Soy-based fillers for thermoset composites

NASA Astrophysics Data System (ADS)

Watt, Paula

Considerable work has been done with bio-based fillers in thermoplastics. Wood dust has been used for decades in wood plastic composites in conjunction with recycled high HDPE and PET. In recent years rapidly renewable fillers derived from dried distillery grains and from wood have been introduced commercially for thermoset polymers. These fillers provide bio-content and weight reduction to thermoset molding compounds but issues with moisture absorption and polymerization inhibition have limited their commercial acceptance. The intent of this research was to develop a bio-based filler suitable for thermoset composites. This filler would provide a low density alternative to mined mineral filler, such as CaCO3 or clay. Composites made with these fillers would be lighter in weight, which is desirable for many markets, particularly transportation. Cost parity to the mineral fillers, on a volume basis, was desirable and the use of green chemistry principles was a key objective of the project. This work provides a basis from which further development of modified soy flours as fillers for thermoset composites will continue. Biomass has been evaluated as fillers for thermoset composites since the early 1980s but failed to gain commercial acceptance due to excessive water absorption and inhibition issues with free radical curing. Biomass, with a large percentage of carbohydrates, are very hydrophilic due to their abundance of hydroxyl groups, while biomass, high in lignin, resulted in inhibition of the free radical cure of the unsaturated styrenated polyester matrix systems. Generally protein use as a filler is not desirable due to its food value. Torrefaction has proved to be a good, cost effective, process to reduce hydrophilicity of high cellulose feedstock. Surprising, however, some levels of torrefaction were found to induce the inhibition effect of the filler. Scientific inquiry into this problem proved that aromatics form during the torrefaction process and can become problematic when threshold levels are reached. Studies to determine suitable levels and appropriate processes provided options for manufacture of suitable fillers.

The Microstructural Evolution of Vacuum Brazed 1Cr18Ni9Ti Using Various Filler Metals

PubMed Central

Chen, Yunxia; Cui, Haichao; Lu, Binfeng; Lu, Fenggui

2017-01-01

The microstructures and weldability of a brazed joint of 1Cr18Ni9Ti austenitic stainless steel with BNi-2, BNi82CrSiBFe and BMn50NiCuCrCo filler metals in vacuum were investigated. It can be observed that an interdiffusion region existed between the filler metal and the base metal for the brazed joint of Ni-based filler metals. The width of the interdiffusion region was about 10 μm, and the microstructure of the brazed joint of BNi-2 filler metal was dense and free of obvious defects. In the case of the brazed joint of BMn50NiCuCrCo filler metal, there were pits, pores and crack defects in the brazing joint due to insufficient wettability of the filler metal. Crack defects can also be observed in the brazed joint of BNi82CrSiBFe filler metal. Compared with BMn50NiCuCrCo and BNi82CrSiBFe filler metals, BNi-2 filler metal is the best material for 1Cr18Ni9Ti austenitic stainless steel vacuum brazing because of its distinct weldability. PMID:28772745

System compliance dictates the effect of composite filler content on polymerization shrinkage stress.

PubMed

Wang, Zhengzhi; Chiang, Martin Y M

2016-04-01

The effect of filler content in dental restorative composites on the polymerization shrinkage stress (PS) is not straightforward and has caused much debate in the literature. Our objective in this study was to clarify the PS/filler content relationship based on analytical and experimental approaches, so that guidelines for materials comparison in terms of PS and clinical selection of dental composites with various filler content can be provided. Analytically, a simplified model based on linear elasticity was utilized to predict PS as a function of filler content under various compliances of the testing system, a cantilever beam-based instrument used in this study. The predictions were validated by measuring PS of composites synthesized using 50/50 mixtures of two common dimethacrylate resins with a variety of filler contents. Both experiments and predictions indicated that the influence of filler content on the PS highly depended on the compliance of the testing system. Within the clinic-relevant range of compliances and for the specific sample configuration tested, the PS increased with increasing filler content at low compliance of instrument, while increasing the compliance caused the effect of filler content on the PS to gradually diminish. Eventually, at high compliance, the PS inverted and decreased with increasing filler content. This compliance-dependent effect of filler content on PS suggests: (1) for materials comparison in terms of PS, the specific compliance at which the comparison being done should always be reported and (2) clinically, composites with relatively lower filler content could be selected for such cavities with relatively lower compliance (e.g. a Class-I cavity with thick tooth walls or the basal part in a cavity) and vice versa in order to reduce the final PS. Published by Elsevier Ltd.

Signature Motifs Identify an Acinetobacter Cif Virulence Factor with Epoxide Hydrolase Activity*

PubMed Central

Bahl, Christopher D.; Hvorecny, Kelli L.; Bridges, Andrew A.; Ballok, Alicia E.; Bomberger, Jennifer M.; Cady, Kyle C.; O'Toole, George A.; Madden, Dean R.

2014-01-01

Endocytic recycling of the cystic fibrosis transmembrane conductance regulator (CFTR) is blocked by the CFTR inhibitory factor (Cif). Originally discovered in Pseudomonas aeruginosa, Cif is a secreted epoxide hydrolase that is transcriptionally regulated by CifR, an epoxide-sensitive repressor. In this report, we investigate a homologous protein found in strains of the emerging nosocomial pathogens Acinetobacter nosocomialis and Acinetobacter baumannii (“aCif”). Like Cif, aCif is an epoxide hydrolase that carries an N-terminal secretion signal and can be purified from culture supernatants. When applied directly to polarized airway epithelial cells, mature aCif triggers a reduction in CFTR abundance at the apical membrane. Biochemical and crystallographic studies reveal a dimeric assembly with a stereochemically conserved active site, confirming our motif-based identification of candidate Cif-like pathogenic EH sequences. Furthermore, cif expression is transcriptionally repressed by a CifR homolog (“aCifR”) and is induced in the presence of epoxides. Overall, this Acinetobacter protein recapitulates the essential attributes of the Pseudomonas Cif system and thus may facilitate airway colonization in nosocomial lung infections. PMID:24474692

Synthesis of Transesterified Palm Olein-Based Polyol and Rigid Polyurethanes from this Polyol.

PubMed

Arniza, Mohd Zan; Hoong, Seng Soi; Idris, Zainab; Yeong, Shoot Kian; Hassan, Hazimah Abu; Din, Ahmad Kushairi; Choo, Yuen May

Transesterification of palm olein with glycerol can increase the functionality by introducing additional hydroxyl groups to the triglyceride structure, an advantage compared to using palm olein directly as feedstock for producing palm-based polyol. The objective of this study was to synthesize transesterified palm olein-based polyol via a three-step reaction: (1) transesterification of palm olein, (2) epoxidation and (3) epoxide ring opening. Transesterification of palm olein yielded approximately 78 % monoglyceride and has an hydroxyl value of approximately 164 mg KOH g -1 . The effect of formic acid and hydrogen peroxide concentrations on the epoxidation reaction was studied. The relationships between epoxide ring-opening reaction time and residual oxirane oxygen content and hydroxyl value were monitored. The synthesized transesterified palm olein-based polyol has hydroxyl value between 300 and 330 mg KOH g -1 and average molecular weight between 1,000 and 1,100 Da. On the basis of the hydroxyl value and average molecular weight of the polyol, the transesterified palm olein-based polyol is suitable for producing rigid polyurethane foam, which can be designed to exhibit desirable properties. Rigid polyurethane foams were synthesized by substituting a portion of petroleum-based polyol with the transesterified palm olein-based polyol. It was observed that by increasing the amount of transesterified palm olein-based polyol, the core density and compressive strength were reduced but at the same time the insulation properties of the rigid polyurethane foam were improved.

Thermal behavior of epoxidized cardanol diethyl phosphate as novel renewable plasticizer for poly(vinyl chloride)

USDA-ARS?s Scientific Manuscript database

A novel plasticizer, epoxidized cardanol diethyl phosphate (ECEP), based on cardanol was synthesized. Chemical structure of ECEP was characterized by fourier transform infrared (FTIR), 1H-nuclear magnetic resonance(1H NMR) and 13C-nuclear magnetic resonance(13C NMR) spectroscopy. Effects of ECEP sub...

Nanobody based immunoassay for human soluble epoxide hydrolase detection using polyHRP for signal enhancement—the rediscovery of polyHRP

USDA-ARS?s Scientific Manuscript database

Soluble epoxide hydrolase (sEH) is a potential pharmacological target for treating hypertension, vascular inflammation, cancer, pain and multiple cardiovascular related diseases. A variable domain of a heavy chain only antibody (termed sdAb, nanobody or VHH) possesses advantages of small size, high ...

The use and correlates of illicit silicone or “fillers” in a population-based sample of transwomen, San Francisco, 2013

PubMed Central

Wilson, Erin; Rapues, Jenna; Jin, Harry; Raymond, H. Fisher

2014-01-01

Introduction There is a dearth of studies to quantify the use of illicit fillers by transwomen. Case studies of illicit filler injections have pointed to an array of serious health complications, including death. Aim The aim of this study was to determine the population prevalence of filler use among transwomen, and to identify correlations with filler use. Methods An analysis of data collected in 2013 with a population-based sample of 234 transwomen recruited using respondent driven sampling (RDS). We used RDS weights to conduct bivariate and multivariate analyses of correlates of filler use. Main Outcome measures Main outcome measures were an RDS-weighted population prevalence of filler use among transwomen and differences in demographic characteristics, transition-related care factors and self-esteem related to appearance. Results Weighted filler prevalence among transwomen was 16.7%. Being a transwomen between 30–49 years of age, owning/renting or living with a partner/family/friend, having had and planning to have surgery in the future and having used non-prescribed hormones were all associated with filler use. HIV was not associated with filler use. Conclusions This study provides the first known estimate to date of the prevalence of filler use in a population-based sample of transwomen in San Francisco. Accessing illicit fillers may be the only choice available for many transwomen due to the cost of legal surgeries and other procedures to change one’s appearance. An important next step in this research is to determine the overall prevalence and long-term consequences of filler use among transwomen, to explore how the use of fillers is protective to the safety and wellbeing of transwomen, and to find safe and affordable alternatives to this method that meets important gender-related appearance needs. PMID:24810672

Welding wire pressure sensor assembly

NASA Technical Reports Server (NTRS)

Morris, Timothy B. (Inventor); Milly, Peter F., Sr. (Inventor); White, J. Kevin (Inventor)

1994-01-01

The present invention relates to a device which is used to monitor the position of a filler wire relative to a base material being welded as the filler wire is added to a welding pool. The device is applicable to automated welding systems wherein nonconsumable electrode arc welding processes are utilized in conjunction with a filler wire which is added to a weld pool created by the electrode arc. The invention senses pressure deviations from a predetermined pressure between the filler wire and the base material, and provides electrical signals responsive to the deviations for actuating control mechanisms in an automatic welding apparatus so as to minimize the pressure deviation and to prevent disengagement of the contact between the filler wire and the base material.

Methods for polymer synthesis

DOEpatents

Allen, Scott D.; Simoneau, Christopher A.; Keefe, William D.; Conuel, Jeff R.

2016-12-06

The present invention provides methods for reducing induction periods in epoxide-CO.sub.2 copolymerizations. In certain embodiments, the methods include the step of contacting an epoxide with CO.sub.2 in the presence of two catalysts: an epoxide hydrolysis catalyst and an epoxide CO.sub.2 copolymerization catalyst. In another aspect, the invention provides catalyst compositions comprising a mixture of an epoxide hydrolysis catalyst and an epoxide CO.sub.2 copolymerization catalyst.

In Silico Prediction of Cytochrome P450-Mediated Biotransformations of Xenobiotics: A Case Study of Epoxidation.

PubMed

Zhang, Jing; Ji, Li; Liu, Weiping

2015-08-17

Predicting the biotransformation of xenobiotics is important in toxicology; however, as more compounds are synthesized than can be investigated experimentally, powerful computational methods are urgently needed to prescreen potentially useful candidates. Cytochrome P450 enzymes (P450s) are the major enzymes involved in xenobiotic metabolism, and many substances are bioactivated by P450s to form active compounds. An example is the conversion of olefinic substrates to epoxides, which are intermediates in the metabolic activation of many known or suspected carcinogens. We have calculated the activation energies for epoxidation by the active species of P450 enzymes (an iron-oxo porphyrin cation radical oxidant, compound I) for a diverse set of 36 olefinic substrates with state-of-the-art density functional theory (DFT) methods. Activation energies can be estimated by the computationally less demanding method of calculating the ionization potentials of the substrates, which provides a useful and simple predictive model based on the reaction mechanism; however, the preclassification of these diverse substrates into weakly polar and strongly polar groups is a prerequisite for the construction of specific predictive models with good predictability for P450 epoxidation. This approach has been supported by both internal and external validations. Furthermore, the relation between the activation energies for the regioselective epoxidation and hydroxylation reactions of P450s and experimental data has been investigated. The results show that the computational method used in this work, single-point energy calculations with the B3LYP functional including zero-point energy and solvation and dispersion corrections based on B3LYP-optimized geometries, performs well in reproducing the experimental trends of the epoxidation and hydroxylation reactions.

Mesoporous Silica Gel-Based Mixed Matrix Membranes for Improving Mass Transfer in Forward Osmosis: Effect of Pore Size of Filler.

PubMed

Lee, Jian-Yuan; Wang, Yining; Tang, Chuyang Y; Huo, Fengwei

2015-11-23

The efficiency of forward osmosis (FO) process is generally limited by the internal concentration polarization (ICP) of solutes inside its porous substrate. In this study, mesoporous silica gel (SG) with nominal pore size ranging from 4-30 nm was used as fillers to prepare SG-based mixed matrix substrates. The resulting mixed matrix membranes had significantly reduced structural parameter and enhanced membrane water permeability as a result of the improved surface porosity of the substrates. An optimal filler pore size of ~9 nm was observed. This is in direct contrast to the case of thin film nanocomposite membranes, where microporous nanoparticle fillers are loaded to the membrane rejection layer and are designed in such a way that these fillers are able to retain solutes while allowing water to permeate through them. In the current study, the mesoporous fillers are designed as channels to both water and solute molecules. FO performance was enhanced at increasing filler pore size up to 9 nm due to the lower hydraulic resistance of the fillers. Nevertheless, further increasing filler pore size to 30 nm was accompanied with reduced FO efficiency, which can be attributed to the intrusion of polymer dope into the filler pores.

Mesoporous Silica Gel–Based Mixed Matrix Membranes for Improving Mass Transfer in Forward Osmosis: Effect of Pore Size of Filler

PubMed Central

Lee, Jian-Yuan; Wang, Yining; Tang, Chuyang Y.; Huo, Fengwei

2015-01-01

The efficiency of forward osmosis (FO) process is generally limited by the internal concentration polarization (ICP) of solutes inside its porous substrate. In this study, mesoporous silica gel (SG) with nominal pore size ranging from 4–30 nm was used as fillers to prepare SG-based mixed matrix substrates. The resulting mixed matrix membranes had significantly reduced structural parameter and enhanced membrane water permeability as a result of the improved surface porosity of the substrates. An optimal filler pore size of ~9 nm was observed. This is in direct contrast to the case of thin film nanocomposite membranes, where microporous nanoparticle fillers are loaded to the membrane rejection layer and are designed in such a way that these fillers are able to retain solutes while allowing water to permeate through them. In the current study, the mesoporous fillers are designed as channels to both water and solute molecules. FO performance was enhanced at increasing filler pore size up to 9 nm due to the lower hydraulic resistance of the fillers. Nevertheless, further increasing filler pore size to 30 nm was accompanied with reduced FO efficiency, which can be attributed to the intrusion of polymer dope into the filler pores. PMID:26592565

Exploiting epoxidized natural rubber latex (ENRL) as a starting raw material for latex-based products

NASA Astrophysics Data System (ADS)

Siti Nor Qamarina, M.; Fatimah Rubaizah, M. R.; Nurul Suhaira, A.; Norhanifah, M. Y.

2017-12-01

Epoxidized natural rubber latex (ENRL) is a chemically modified natural rubber latex produced from epoxidation process that involves usage of organic peracids. Conversion of the ENRL into dry rubber products has been known to exhibit many beneficial properties, however limited published works were found on diversifiying the ENRL latex-based products applications. In this preliminary work, different source of raw materials and neutralization systems were investigated. The objective was to explore possibilities in producing distinctive ENRL. Findings have demonstrated that different source of raw materials and neutralization systems influenced the typical ENRL specifications, stability behavior and particle size distribution. Morphological observations performed on these ENRL systems appeared to agree with the ENRL characteristics achieved. Since experimenting these two main factors resulted in encouraging ENRL findings, detailed work shall be further scrutinized to search for an optimum condition in producing marketable ENRL specifically for latex-based products applications.

Efficient alkene epoxidation catalyzed by molybdenyl acetylacetonate supported on aminated UiO-66 metal-organic framework

NASA Astrophysics Data System (ADS)

Kardanpour, Reihaneh; Tangestaninejad, Shahram; Mirkhani, Valiollah; Moghadam, Majid; Mohammadpoor-Baltork, Iraj; Zadehahmadi, Farnaz

2015-03-01

Metal-organic frameworks (MOFs) containing Mo Schiff base complexes were prepared by post-synthesis method and applied as efficient catalysts in the epoxidation of alkenes with tert-BuOOH. In this manner, UiO-66-NH2 (UiO=University of Oslo) MOF was reacted with salicylaldehyde and thiophene-2-carbaldehyde to produce bidentate Schiff bases. Then, the Schiff base ligands were used for immobilization of molybdenyl acetylacetonate. These new catalysts were characterized by FT-IR, UV-vis spectroscopic techniques, X-ray diffraction (XRD), BET, inductively coupled plasma atomic emission spectroscopy (ICP-AES) and field emission scanning electron microscopy (FE-SEM). These catalytic systems showed excellent activity in the epoxidation of alkenes such as cyclic and linear ones with tert-butyl hydroperoxide (TBHP) in 1,2-dichloroethane, and reused several times without any appreciable loss of their activity.

Improvement of Scratch and Wear Resistance of Polymers by Fillers Including Nanofillers

PubMed Central

Brostow, Witold; Lobland, Haley E. Hagg; Hnatchuk, Nathalie; Perez, Jose M.

2017-01-01

Polymers have lower resistance to scratching and wear than metals. Liquid lubricants work well for metals but not for polymers nor for polymer-based composites (PBCs). We review approaches for improvement of tribological properties of polymers based on inclusion of fillers. The fillers can be metallic or ceramic—with obvious consequences for electrical resistivity of the composites. Distinctions between effectiveness of micro- versus nano-particles are analyzed. For example, aluminum nanoparticles as filler are more effective for property improvement than microparticles at the same overall volumetric concentration. Prevention of local agglomeration of filler particles is discussed along with a technique to verify the prevention. PMID:28336900

Catalytic asymmetric epoxidation of alpha,beta-unsaturated amides: efficient synthesis of beta-aryl alpha-hydroxy amides using a one-pot tandem catalytic asymmetric epoxidation-Pd-catalyzed epoxide opening process.

PubMed

Nemoto, Tetsuhiro; Kakei, Hiroyuki; Gnanadesikan, Vijay; Tosaki, Shin-Ya; Ohshima, Takashi; Shibasaki, Masakatsu

2002-12-11

The catalytic asymmetric epoxidation of alpha,beta-unsaturated amides using Sm-BINOL-Ph3As=O complex was succeeded. Using 5-10 mol % of the asymmetric catalyst, a variety of amides were epoxidized efficiently, yielding the corresponding alpha,beta-epoxy amides in up to 99% yield and in more than 99% ee. Moreover, the novel one-pot tandem process, one-pot tandem catalytic asymmetric epoxidation-Pd-catalyzed epoxide opening process, was developed. This method was successfully utilized for the efficient synthesis of beta-aryl alpha-hydroxy amides, including beta-aryllactyl-leucine methyl esters. Interestingly, it was found that beneficial modifications on the Pd catalyst were achieved by the constituents of the first epoxidation, producing a more suitable catalyst for the Pd-catalyzed epoxide opening reaction in terms of chemoselectivity.

Regio- and enantiofacial selectivity of epoxyeicosatrienoic acid hydration by cytosolic epoxide hydrolase.

PubMed

Zeldin, D C; Kobayashi, J; Falck, J R; Winder, B S; Hammock, B D; Snapper, J R; Capdevila, J H

1993-03-25

The hydration of cis-epoxyeicosatrienoic acids to the corresponding vic-dihydroxyeicosatrienoic acids by cytosolic epoxide hydrolase demonstrates moderate regioselectivity with rates of hydration highest for the 14,15-epoxide and lower for the 11,12- and 8,9-epoxide (4.5, 1.6, and 1.5 mumol of product/mg of protein/min, respectively). Incubations of the 8,9- and 14,15-epoxides with cytosolic epoxide hydrolase show stereoselective formation of diols (7:3 and 4:1 ratio of antipodes, respectively) and concomitant chiral enrichment of the remaining unmetabolized substrate. In contrast, hydration of the 11,12-epoxide is nonenantioselective. The Km value of the enzyme for the 14(R),15(S)-epoxide is 3 microM. Incubations of the enantiomerically pure 8,9- and 14,15-epoxides with lung or liver cytosol, followed by chiral analysis of the resulting diols demonstrate selective cleavage of the oxirane ring at C9 and C15, respectively. On the other hand, cleavage of the 11,12- oxirane ring was less selective. The stereochemical preference of the cytosolic epoxide hydrolase, together with the known chiral composition of the endogenous arachidonate epoxide pools, suggests a functional role for this enzyme in the metabolism of these important compounds.

In-Situ Generated Graphene as the Catalytic Site for Visible-Light Mediated Ethylene Epoxidation on AG Nanocatalysts

NASA Astrophysics Data System (ADS)

Zhang, Xueqiang Alex; Jain, Prashant

2017-06-01

Despite the harsh conditions for chemical conversion, ethylene oxide produced from ethylene epoxidation on Ag-based heterogeneous catalyst constitutes one of the largest volume chemicals in chemical industry. Recently, photocatalytic epoxidation of ethylene over plasmonic Ag nanoparticles enables the chemical conversion under significantly decreased temperature and ambient pressure conditions. Yet a detailed understanding of the photocatalytic process at the reactant/catalyst interface is under debate. Surface enhanced Raman spectroscopy (SERS) is a powerful vibrational spectroscopy technique that enables the localized detection of rare and/or transient chemical species with high sensitivity under in situ and ambient conditions. Using SERS, we are able to monitor at individual sites of an Ag nanocatalyst the visible-light-mediated adsorption and epoxidation of ethylene. From detected intermediates, we find that the primary step in the photoepoxidation is the transient formation of graphene catalyzed by the Ag surface. Density functional theory (DFT) simulations that model the observed SERS spectra suggest that the defective edge sites of the graphene formed on Ag constitute the active site for C2H4 adsorption and epoxidation. Further studies with pre-formed graphene/Ag catalyst composites confirm the indispensable role of graphene in visible-light-mediated ethylene epoxidation. Carbon is often thought to be either an innocent support or a poison for metallic catalysts; however our studies reveal a surprising role for crystalline carbon layers as potential co-catalysts.

Increasing the wear resistance of ultra-high molecular weight polyethylene by adding solid lubricating fillers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Panin, S. V., E-mail: svp@ispms.tsc.ru; Kornienko, L. A.; Poltaranin, M. A.

2014-11-14

In order to compare effectiveness of adding solid lubricating fillers for polymeric composites based on ultra-high molecular weight polyethylene (UHMWPE) with graphite, molybdenum disulfide and polytetrafluoroethylene, their tribotechnical characteristics under dry friction, boundary lubrication and abrasive wearing were investigated. The optimal weight fractions of fillers in terms of improving wear resistance have been determined. The supramolecular structure and topography of wear track surfaces of UHMWPE-based composites with different content of fillers have been studied.

Mechanism of epoxide hydrolysis in microsolvated nucleotide bases adenine, guanine and cytosine: a DFT study.

PubMed

Vijayalakshmi, Kunduchi P; Mohan, Neetha; Ajitha, Manjaly J; Suresh, Cherumuttathu H

2011-07-21

Six water molecules have been used for microsolvation to outline a hydrogen bonded network around complexes of ethylene epoxide with nucleotide bases adenine (EAw), guanine (EGw) and cytosine (ECw). These models have been developed with the MPWB1K-PCM/6-311++G(3df,2p)//MPWB1K/6-31+G(d,p) level of DFT method and calculated S(N)2 type ring opening of the epoxide due to amino group of the nucleotide bases, viz. the N6 position of adenine, N2 position of guanine and N4 position of cytosine. Activation energy (E(act)) for the ring opening was found to be 28.06, 28.64, and 28.37 kcal mol(-1) respectively for EAw, EGw and ECw. If water molecules were not used, the reactions occurred at considerably high value of E(act), viz. 53.51 kcal mol(-1) for EA, 55.76 kcal mol(-1) for EG and 56.93 kcal mol(-1) for EC. The ring opening led to accumulation of negative charge on the developing alkoxide moiety and the water molecules around the charge localized regions showed strong hydrogen bond interactions to provide stability to the intermediate systems EAw-1, EGw-1 and ECw-1. This led to an easy migration of a proton from an activated water molecule to the alkoxide moiety to generate a hydroxide. Almost simultaneously, a proton transfer chain reaction occurred through the hydrogen bonded network of water molecules and resulted in the rupture of one of the N-H bonds of the quaternized amino group. The highest value of E(act) for the proton transfer step of the reaction was 2.17 kcal mol(-1) for EAw, 2.93 kcal mol(-1) for EGw and 0.02 kcal mol(-1) for ECw. Further, the overall reaction was exothermic by 17.99, 22.49 and 13.18 kcal mol(-1) for EAw, EGw and ECw, respectively, suggesting that the reaction is irreversible. Based on geometric features of the epoxide-nucleotide base complexes and the energetics, the highest reactivity is assigned for adenine followed by cytosine and guanine. Epoxide-mediated damage of DNA is reported in the literature and the present results suggest that hydrated DNA bases become highly S(N)2 active on epoxide systems and the occurrence of such reactions can inflict permanent damage to the DNA.

Theoretical study on the mechanism of a ring-opening reaction of oxirane by the active-site aspartic dyad of HIV-1 protease.

PubMed

Kóna, Juraj

2008-01-21

Two possible mechanisms of the irreversible inhibition of HIV-1 protease by epoxide inhibitors are investigated on an enzymatic model using ab initio (MP2) and density functional theory (DFT) methods (B3LYP, MPW1K and M05-2X). The calculations predict the inhibition as a general acid-catalyzed nucleophilic substitution reaction proceeding by a concerted SN2 mechanism with a reaction barrier of ca. 15-21 kcal mol(-1). The irreversible nature of the inhibition is characterized by a large negative reaction energy of ca. -17-(-24) kcal mol(-1). A mechanism with a direct proton transfer from an aspartic acid residue of the active site onto the epoxide ring has been shown to be preferred compared to one with the proton transfer from the acid catalyst facilitated by a bridging catalytic water molecule. Based on the geometry of the transition state, structural data important for the design of irreversible epoxide inhibitors of HIV-1 protease were defined. Here we also briefly discuss differences between the epoxide ring-opening reaction in HIV-1 protease and epoxide hydrolase, and the accuracy of the DFT method used.

Swelling behaviour in n-pentane and mechanical properties of epoxidized natural rubber with different epoxide content

NASA Astrophysics Data System (ADS)

Kinasih, N. A.; Fathurrohman, M. I.; Winarto, D. A.

2017-07-01

Epoxidized natural rubber (ENR) with different level of epoxidation (i.e. 10, 20, 30, 40 and 50 mol% indicated as ENR ENR10, ENR20, ENR30, ENR40 and ENR50, respectively) were prepared. They were then vulcanized by using efficient system vulcanization. The effect of epoxide content on curing characteristic, swelling and mechanical properties in N-pentane was investigated. The Attenuated Resonance Fourier Transform Infrared (ATR-FTIR) and H-Nuclear Magnetic Resonance (H-NMR) were used to determine the epoxidation level. Glass transition (Tg) of ENR samples was determined by using Direct Scanning Calorimetry (DSC). The result revealed that the resistance of ENR in N-pentane increased with increasing epoxidation level, which indicated by decreasing equilibrium mol uptake and diffusion coefficient. The compression set of ENR and aging resistance increased with increasing epoxide content, except ENR50 was due to ENR 50 have two Tg value. However, the value of hardness and tensile strength were not effected by epoxidation level.

Hydrogen-Bonding Catalysis and Inhibition by Simple Solvents in the Stereoselective Kinetic Epoxide-Opening Spirocyclization of Glycal Epoxides to Form Spiroketals

PubMed Central

Wurst, Jacqueline M.; Liu, Guodong; Tan, Derek S.

2011-01-01

Mechanistic investigations of a MeOH-induced kinetic epoxide-opening spirocyclization of glycal epoxides have revealed dramatic, specific roles for simple solvents in hydrogen-bonding catalysis of this reaction to form spiroketal products stereoselectively with inversion of configuration at the anomeric carbon. A series of electronically-tuned C1-aryl glycal epoxides was used to study the mechanism of this reaction based on differential reaction rates and inherent preferences for SN2 versus SN1 reaction manifolds. Hammett analysis of reaction kinetics with these substrates is consistent with an SN2 or SN2-like mechanism (ρ = −1.3 vs. ρ = −5.1 for corresponding SN1 reactions of these substrates). Notably, the spirocyclization reaction is second-order dependent on MeOH and the glycal ring oxygen is required for second-order MeOH catalysis. However, acetone cosolvent is a first-order inhibitor of the reaction. A transition state consistent with the experimental data is proposed in which one equivalent of MeOH activates the epoxide electrophile via a hydrogen bond while a second equivalent of MeOH chelates the sidechain nucleophile and glycal ring oxygen. A paradoxical previous observation that decreased MeOH concentration leads to increased competing intermolecular methyl glycoside formation is resolved by the finding that this side reaction is only first-order dependent on MeOH. This study highlights the unusual abilities of simple solvents to act as hydrogen-bonding catalysts and inhibitors in epoxide-opening reactions, providing both stereoselectivity and discrimination between competing reaction manifolds. This spirocyclization reaction provides efficient, stereocontrolled access to spiroketals that are key structural motifs in natural products. PMID:21539313

[Facial injections of hyaluronic acid-based fillers for malformations. Preliminary study regarding scar tissue improvement and cosmetic betterment].

PubMed

Franchi, G; Neiva-Vaz, C; Picard, A; Vazquez, M-P

2018-06-01

Cross-linked hyaluronic acid-based fillers have gained rapid acceptance for treating facial wrinkles, deep tissue folds and sunken areas due to aging. This study evaluates, in addition to space-filling properties, their effects on softness and elasticity as a secondary effect, following injection of 3 commercially available cross-linked hyaluronic acid-based fillers (15mg/mL, 17,5mg/mL and 20mg/mL) in patients presenting with congenital or acquired facial malformations. We started injecting gels of cross-linked hyaluronic acid-based fillers in those cases in 2013; we performed 46 sessions of injections in 32 patients, aged from 13-32. Clinical assessment was performed by the patient himself and by a plastic surgeon, 15 days after injections and 6-18 months later. Cross-linked hyaluronic acid-based fillers offered very subtle cosmetic results and supplemented surgery with a very high level of satisfaction of the patients. When injected in fibrosis, the first session enhanced softness and elasticity; the second session enhanced the volume. Cross-linked hyaluronic acid-based fillers fill sunken areas and better softness and elasticity of scar tissues. In addition to their well-understood space-filling function, as a secondary effect, the authors demonstrate that cross-linked hyaluronic acid-based fillers improve softness and elasticity of scarring tissues. Many experimental studies support our observations, showing that cross-linked hyaluronic acid stimulates the production of several extra-cellular matrix components, including dermal collagen and elastin. Copyright © 2018 Elsevier Masson SAS. All rights reserved.

Enzyme-catalyzed cationic epoxide rearrangements in quinolone alkaloid biosynthesis.

PubMed

Zou, Yi; Garcia-Borràs, Marc; Tang, Mancheng C; Hirayama, Yuichiro; Li, Dehai H; Li, Li; Watanabe, Kenji; Houk, K N; Tang, Yi

2017-03-01

Epoxides are highly useful synthons and biosynthons for the construction of complex natural products during total synthesis and biosynthesis, respectively. Among enzyme-catalyzed epoxide transformations, a reaction that is notably missing, in regard to the synthetic toolbox, is cationic rearrangement that takes place under strong acid. This is a challenging transformation for enzyme catalysis, as stabilization of the carbocation intermediate upon epoxide cleavage is required. Here, we discovered two Brønsted acid enzymes that can catalyze two unprecedented epoxide transformations in biology. PenF from the penigequinolone pathway catalyzes a cationic epoxide rearrangement under physiological conditions to generate a quaternary carbon center, while AsqO from the aspoquinolone pathway catalyzes a 3-exo-tet cyclization to forge a cyclopropane-tetrahydrofuran ring system. The discovery of these new epoxide-modifying enzymes further highlights the versatility of epoxides in complexity generation during natural product biosynthesis.

Iron-catalyzed olefin epoxidation in the presence of acetic acid: insights into the nature of the metal-based oxidant.

PubMed

Mas-Ballesté, Rubén; Que, Lawrence

2007-12-26

The iron complexes [(BPMEN)Fe(OTf)2] (1) and [(TPA)Fe(OTf)2] (2) [BPMEN = N,N'-bis-(2-pyridylmethyl)-N,N'-dimethyl-1,2-ethylenediamine; TPA = tris-(2-pyridylmethyl)amine] catalyze the oxidation of olefins by H2O2 to yield epoxides and cis-diols. The addition of acetic acid inhibits olefin cis-dihydroxylation and enhances epoxidation for both 1 and 2. Reactions carried out at 0 degrees C with 0.5 mol % catalyst and a 1:1.5 olefin/H2O2 ratio in a 1:2 CH3CN/CH3COOH solvent mixture result in nearly quantitative conversions of cyclooctene to epoxide within 1 min. The nature of the active species formed in the presence of acetic acid has been probed at low temperature. For 2, in the absence of substrate, [(TPA)FeIII(OOH)(CH3COOH)]2+ and [(TPA)FeIVO(NCCH3)]2+ intermediates can be observed. However, neither is the active epoxidizing species. In fact, [(TPA)FeIVO(NCCH3)]2+ is shown to form in competition with substrate oxidation. Consequently, it is proposed that epoxidation is mediated by [(TPA)FeV(O)(OOCCH3)]2+, generated from O-O bond heterolysis of the [(TPA)FeIII(OOH)(CH3COOH)]2+ intermediate, which is promoted by the protonation of the terminal oxygen atom of the hydroperoxide by the coordinated carboxylic acid.

Effect of Filler and Heat Treatment on the Physical and Mechanical Properties of the Brazed Joint between Carbide Tip and Steel

NASA Astrophysics Data System (ADS)

Winardi, Y.; Triyono; Wijayanta, A. T.

2017-02-01

In this study, the effect of filler and heat treatment on the physical and mechanical properties of the brazed joint carbide tip and steel was investigated. Tip carbide YG6 and low carbon steel (SS400) is joining by torch brazing with two filler metals, silver, and copper filler. Heat treatment was performed in induction furnace. Microstructure and shear strength of the brazed joint have been investigated. Many silver filler layer are formed on the surface of the base metal rather then using copper filler. The highest shear strength is achieved using a silver filler metal at temperatur 725°C. The highest shear load is 18.62 kN.

Silicone nanocomposite coatings for fabrics

NASA Technical Reports Server (NTRS)

Lee, Stein S. (Inventor); Ou, Runqing (Inventor); Eberts, Kenneth (Inventor); Singhal, Amit (Inventor)

2011-01-01

A silicone based coating for fabrics utilizing dual nanocomposite fillers providing enhanced mechanical and thermal properties to the silicone base. The first filler includes nanoclusters of polydimethylsiloxane (PDMS) and a metal oxide and a second filler of exfoliated clay nanoparticles. The coating is particularly suitable for inflatable fabrics used in several space, military, and consumer applications, including airbags, parachutes, rafts, boat sails, and inflatable shelters.

Corrosion behavior in high-temperature pressurized water of Zircaloy-4 joints brazed with Zr-Cu-based amorphous filler alloys

NASA Astrophysics Data System (ADS)

Lee, Jung Gu; Lee, Gyoung-Ja; Park, Jin-Ju; Lee, Min-Ku

2017-05-01

The compositional effects of ternary Zr-Cu-X (X: Al, Fe) amorphous filler alloys on galvanic corrosion susceptibility in high-temperature pressurized water were investigated for Zircaloy-4 brazed joints. Through an Al-induced microgalvanic reaction that deteriorated the overall nobility of the joint, application of the Zr-Cu-Al filler alloy caused galvanic coupling to develop readily between the Al-bearing joint and the Al-free base metal, finally leading to massive localized corrosion of the joint. Contrastingly, joints prepared with a Zr-Cu-Fe filler alloy showed excellent corrosion resistance comparable to that of the Zircaloy-4 base metal, since the Cu and Fe elements forming fine intermetallic particles with Zr did not influence the electrochemical stability of the resultant joints. The present results demonstrate that Fe is a more suitable alloying element than Al for brazing filler alloys subjected to high-temperature corrosive environments.

Crystal structures and catalytic performance of three new methoxy substituted salen type nickel(II) Schiff base complexes derived from meso-1,2-diphenyl-1,2-ethylenediamine

NASA Astrophysics Data System (ADS)

Ghaffari, Abolfazl; Behzad, Mahdi; Pooyan, Mahsa; Amiri Rudbari, Hadi; Bruno, Giuseppe

2014-04-01

Three new nickel(II) complexes of a series of methoxy substituted salen type Schiff base ligands were synthesized and characterized by IR, UV-Vis and 1H NMR spectroscopy and elemental analysis. The ligands were synthesized from the condensation of meso-1,2-diphenyl-1,2-ethylenediamine with n-methoxysalicylaldehyde (n = 3, 4 and 5). Crystal structures of these complexes were determined. Electrochemical behavior of the complexes was studied by means of cyclic voltammetry in DMSO solutions. Catalytic performance of the complexes was studied in the epoxidation of cyclooctene using tert-butylhydroperoxide (TBHP) as oxidant under various conditions to find the optimum operating parameters. Low catalytic activity with moderate epoxide selectivity was observed in in-solvent conditions but in the solvent-free conditions, enhanced catalytic activity with high epoxide selectivity was achieved.

Structural insights into human microsomal epoxide hydrolase by combined homology modeling, molecular dynamics simulations, and molecular docking calculations.

PubMed

Saenz-Méndez, Patricia; Katz, Aline; Pérez-Kempner, María Lucía; Ventura, Oscar N; Vázquez, Marta

2017-04-01

A new homology model of human microsomal epoxide hydrolase was derived based on multiple templates. The model obtained was fully evaluated, including MD simulations and ensemble-based docking, showing that the quality of the structure is better than that of only previously known model. Particularly, a catalytic triad was clearly identified, in agreement with the experimental information available. Analysis of intermediates in the enzymatic mechanism led to the identification of key residues for substrate binding, stereoselectivity, and intermediate stabilization during the reaction. In particular, we have confirmed the role of the oxyanion hole and the conserved motif (HGXP) in epoxide hydrolases, in excellent agreement with known experimental and computational data on similar systems. The model obtained is the first one that fully agrees with all the experimental observations on the system. Proteins 2017; 85:720-730. © 2016 Wiley Periodicals, Inc. © 2017 Wiley Periodicals, Inc.

Ionic Liquid Epoxy Resin Monomers

NASA Technical Reports Server (NTRS)

Paley, Mark S. (Inventor)

2013-01-01

Ionic liquid epoxide monomers capable of reacting with cross-linking agents to form polymers with high tensile and adhesive strengths. Ionic liquid epoxide monomers comprising at least one bis(glycidyl) N-substituted nitrogen heterocyclic cation are made from nitrogen heterocycles corresponding to the bis(glycidyl) N-substituted nitrogen heterocyclic cations by a method involving a non-nucleophilic anion, an alkali metal cation, epichlorohydrin, and a strong base.

Directionally solidified article with weld repair

NASA Technical Reports Server (NTRS)

Smashey, Russell W. (Inventor); Snyder, John H. (Inventor); Borne, Bruce L. (Inventor)

2003-01-01

A directionally solidified nickel-base superalloy article has a defect therein extending parallel to the solidification direction. The article is repaired by removing any foreign matter present in the defect, and then heating the article to a repair temperature of from about 60 to about 98 percent of the solidus temperature of the base material in a chamber containing a protective gas that inhibits oxidation of the base material. The defect is filled with a filler metal while maintaining the article at the repair temperature. The filling is accomplished by providing a source of the filler metal of substantially the same composition as the base material of the directionally solidified article, and melting the filler metal into the defect progressively while moving the source of the filler metal relative to the article in a direction parallel to the solidification direction. Optionally, additional artificial heat extraction is accomplished in a heat-flow direction that is within about 45 degrees of the solidification direction, as the filler metal solidifies within the defect. The article may thereafter be heat treated.

Weld repair of directionally solidified articles

NASA Technical Reports Server (NTRS)

Smashey, Russell W. (Inventor); Snyder, John H. (Inventor); Borne, Bruce L. (Inventor)

2002-01-01

A directionally solidified nickel-base superalloy article has a defect therein extending parallel to the solidification direction. The article is repaired by removing any foreign matter present in the defect, and then heating the article to a repair temperature of from about 60 to about 98 percent of the solidus temperature of the base material in a chamber containing a protective gas that inhibits oxidation of the base material. The defect is filled with a filler metal while maintaining the article at the repair temperature. The filling is accomplished by providing a source of the filler metal of substantially the same composition as the base material of the directionally solidified article, and melting the filler metal into the defect progressively while moving the source of the filler metal relative to the article in a direction parallel to the solidification direction. Optionally, additional artificial heat extraction is accomplished in a heat-flow direction that is within about 45 degrees of the solidification direction, as the filler metal solidifies within the defect. The article may thereafter be heat treated.

Aluminum Lithium Alloy 2195 Fusion Welding Improvements with New Filler Wire

NASA Technical Reports Server (NTRS)

Russell, Carolyn; Bjorkman, Gerry; McCool, Carolyn (Technical Monitor)

2000-01-01

A viewgraph presentation outlines NASA Marshall Space Flight Center, Lockheed Martin Michoud Space Systems, and McCook Metals' development an aluminum-copper weld filler wire for fusion welding 2195 aluminum lithium. The aluminum-copper based weld filler wire has been identified as B218, which is the result of six years of weld filler wire development funded by NASA, Lockheed Martin, and McCook Metals. The Super Lightweight External Tank for the NASA Space Shuttle Program consists of 2195 welded with 4043 aluminum-silicon weld filler wire. The B218 filler wire chemistry was developed to produce enhanced 2195 weld and repair weld mechanical properties. An initial characterization of the B218 weld filler wire was performed consisting of initial weld and repair weld evaluation comparing B218 and 4043. The testing involved room temperature and cryogenic tensile testing along with fracture toughness testing. B218 weld filler wire proved to produce enhanced initial and repair weld tensile and fracture properties over 4043. B218 weld filler wire has proved to be a superior weld filler wire for welding 2195 and other aluminum lithium alloys over 4043.

Development and characterization of soy-based epoxy resins and pultruded FRP composites

NASA Astrophysics Data System (ADS)

Zhu, Jiang

This dissertation focuses on the development, manufacture and characterization of novel soy-based epoxy FRP composites. Use of alternative epoxy resin systems derived from a renewable resource holds potential for low cost raw materials for the polymer and composite industries. Epoxidized Allyl Soyate (EAS) and Epoxidized Methyl Soyate (EMS) were developed from soybean oil with two chemical modification procedures: transesterification and epoxidation. This research investigates the curing characteristics and thermal and mechanical properties of the neat soyate resin systems. The derived soyate resins have higher reactivity and superior performance compared to commercially available epoxidized soybean oil. An efficient two-step curing method was developed in order to utilize these soyate resins to their full potential. The epoxy co-resin systems with varied soyate resin content were successfully used to fabricate composite material through pultrusion. The pultrusion resin systems with 30 wt% soyate resins yielded improved, or comparable mechanical properties with neat commercial resins. A finite element analysis of the heat transfer and curing process was performed to study the processing characterization on glass/epoxy composite pultrusion. This model can be used to establish baseline process variables and will benefit subsequent optimization. This research demonstrates that soy-based resins, especially EAS, show considerable promise as an epoxy resin supplement for use in polymer and composite structural applications. The new products derived from soybean oil can provide competitive performance, low cost and environmental advantages.

Polyvinyl alcohol battery separator containing inert filler. [alkaline batteries

NASA Technical Reports Server (NTRS)

Sheibley, D. W.; Hsu, L. C.; Manzo, M. A. (Inventor)

1981-01-01

A cross-linked polyvinyl alcohol battery separator is disclosed. A particulate filler, inert to alkaline electrolyte of an alkaline battery, is incorporated in the separator in an amount of 1-20% by weight, based on the weight of the polyvinyl alcohol, and is dispersed throughout the product. Incorporation of the filler enhances performance and increases cycle life of alkaline batteries when compared with batteries containing a similar separator not containing filler. Suitable fillers include titanates, silicates, zirconates, aluminates, wood floor, lignin, and titania. Particle size is not greater than about 50 microns.

Effect of filler properties in composite resins on light transmittance characteristics and color.

PubMed

Arikawa, Hiroyuki; Kanie, Takahito; Fujii, Koichi; Takahashi, Hideo; Ban, Seiji

2007-01-01

The purpose of this investigation was to examine the effect of filler particle size and shape as well as filler content on light transmittance characteristics and color of experimental composite resins. A mixture of 30 mol% Bis-GMA and 70 mol% TEGDMA was prepared as a base monomer and to which a photoinitiator (camphorquinone) and a co-initiator (N,N-dimethylaminoethyl methacrylate) were added. Four different irregular- and spherical-shaped filler types with an average particle size of 1.9-11.1 microm were added to the mixture in three different filler contents of 20, 30, and 40 vol%. Light transmittance characteristics including light diffusion characteristics of the materials were evaluated. Color values and color differences among filler contents of the materials were also determined. Materials containing smaller and irregular-shaped fillers showed higher light transmittance and diffusion angle distribution with a sharper peak, as compared with those containing larger and spherical-shape fillers. It was also found that there was a significant correlation between the specific surface area of fillers and the color difference of the materials containing the fillers. Our results indicated that the shape of filler particles, as well as particle size and filler content, significantly affected the light transmittance characteristics--including light diffusion characteristics--and color of composite resins.

40 CFR 721.2675 - Perfluoroalkyl epoxide (generic name).

Code of Federal Regulations, 2010 CFR

2010-07-01

... Substances § 721.2675 Perfluoroalkyl epoxide (generic name). (a) Chemical substances and significant new uses subject to reporting. (1) The chemical substance identified generically as perfluoroalkyl epoxide (PMN P... 40 Protection of Environment 30 2010-07-01 2010-07-01 false Perfluoroalkyl epoxide (generic name...

40 CFR 721.2675 - Perfluoroalkyl epoxide (generic name).

Code of Federal Regulations, 2011 CFR

2011-07-01

... Substances § 721.2675 Perfluoroalkyl epoxide (generic name). (a) Chemical substances and significant new uses subject to reporting. (1) The chemical substance identified generically as perfluoroalkyl epoxide (PMN P... 40 Protection of Environment 31 2011-07-01 2011-07-01 false Perfluoroalkyl epoxide (generic name...

40 CFR 721.2675 - Perfluoroalkyl epoxide (generic name).

Code of Federal Regulations, 2013 CFR

2013-07-01

... Substances § 721.2675 Perfluoroalkyl epoxide (generic name). (a) Chemical substances and significant new uses subject to reporting. (1) The chemical substance identified generically as perfluoroalkyl epoxide (PMN P... 40 Protection of Environment 32 2013-07-01 2013-07-01 false Perfluoroalkyl epoxide (generic name...

40 CFR 721.2675 - Perfluoroalkyl epoxide (generic name).

Code of Federal Regulations, 2012 CFR

2012-07-01

... Substances § 721.2675 Perfluoroalkyl epoxide (generic name). (a) Chemical substances and significant new uses subject to reporting. (1) The chemical substance identified generically as perfluoroalkyl epoxide (PMN P... 40 Protection of Environment 32 2012-07-01 2012-07-01 false Perfluoroalkyl epoxide (generic name...

40 CFR 721.2675 - Perfluoroalkyl epoxide (generic name).

Code of Federal Regulations, 2014 CFR

2014-07-01

... Substances § 721.2675 Perfluoroalkyl epoxide (generic name). (a) Chemical substances and significant new uses subject to reporting. (1) The chemical substance identified generically as perfluoroalkyl epoxide (PMN P... 40 Protection of Environment 31 2014-07-01 2014-07-01 false Perfluoroalkyl epoxide (generic name...

Preferential glutathione conjugation of a reverse diol epoxide compared to a bay region diol epoxide of phenanthrene in human hepatocytes: relevance to molecular epidemiology studies of glutathione-s-transferase polymorphisms and cancer.

PubMed

Hecht, Stephen S; Berg, Jeannette Zinggeler; Hochalter, J Bradley

2009-03-16

Bay region diol epoxides are recognized ultimate carcinogens of polycyclic aromatic hydrocarbons (PAH), and in vitro studies have demonstrated that they can be detoxified by conjugation with glutathione, leading to the widely investigated hypothesis that individuals with low activity forms of glutathione-S-transferases are at higher risk of PAH induced cancer, a hypothesis that has found at most weak support in molecular epidemiology studies. A weakness in this hypothesis was that the mercapturic acids resulting from the conjugation of PAH bay region diol epoxides had never been identified in human urine. We recently analyzed smokers' urine for mercapturic acids derived from phenanthrene, the simplest PAH with a bay region. The only phenanthrene diol epoxide-derived mercapturic acid in smokers' urine was produced from the reverse diol epoxide, anti-phenanthrene-3,4-diol-1,2-epoxide (11), not the bay region diol epoxide, anti-phenanthrene-1,2-diol-3,4-epoxide (10), which does not support the hypothesis noted above. In this study, we extended these results by examining the conjugation of phenanthrene metabolites with glutathione in human hepatocytes. We identified the mercapturic acid N-acetyl-S-(r-4,t-2,3-trihydroxy-1,2,3,4-tetrahydro-c-1-phenanthryl)-L-cysteine (14a), (0.33-35.9 pmol/mL at 10 microM 8, 24 h incubation, N = 10) in all incubations with phenanthrene-3,4-diol (8) and the corresponding diol epoxide 11, but no mercapturic acids were detected in incubations with phenanthrene-1,2-diol (7), and only trace amounts were observed in incubations with the corresponding bay region diol epoxide 10. Taken together with our previous results, these studies clearly demonstrate that glutathione conjugation of a reverse diol epoxide of phenanthrene is favored over conjugation of a bay region diol epoxide. Since reverse diol epoxides of PAH are generally weakly or nonmutagenic/carcinogenic, these results, if generalizable to other PAH, do not support the widely held assumption that glutathione-S-transferases are important in the detoxification of PAH in humans.

Piezoresistivity, mechanisms and model of cement-based materials with CNT/NCB composite fillers

NASA Astrophysics Data System (ADS)

Zhang, Liqing; Ding, Siqi; Dong, Sufen; Li, Zhen; Ouyang, Jian; Yu, Xun; Han, Baoguo

2017-12-01

The use of conductive cement-based materials as sensors has attracted intense interest over past decades. In this paper, carbon nanotube (CNT)/nano carbon black (NCB) composite fillers made by electrostatic self-assembly are used to fabricate conductive cement-based materials. Electrical and piezoresistive properties of the fabricated cement-based materials are investigated. Effect of filler content, load amplitudes and rate on piezoresistive property within elastic regime and piezoresistive behaviors during compressive loading to destruction are explored. Finally, a model describing piezoresistive property of cement-based materials with CNT/NCB composite fillers is established based on the effective conductive path and tunneling effect theory. The research results demonstrate that filler content and load amplitudes have obvious effect on piezoresistive property of the composites materials, while load rate has little influence on piezoresistive property. During compressive loading to destruction, the composites also show sensitive piezoresistive property. Therefore, the cement-based composites can be used to monitor the health state of structures during their whole life. The built model can well describe the piezoresistive property of the composites during compressive loading to destruction. The good match between the model and experiment data indicates that tunneling effect actually contributes to piezoresistive phenomenon.

PMMA denture base material enhancement: a review of fiber, filler, and nanofiller addition

PubMed Central

Gad, Mohammed M; Fouda, Shaimaa M; Al-Harbi, Fahad A; Näpänkangas, Ritva; Raustia, Aune

2017-01-01

This paper reviews acrylic denture base resin enhancement during the past few decades. Specific attention is given to the effect of fiber, filler, and nanofiller addition on poly(methyl methacrylate) (PMMA) properties. The review is based on scientific reviews, papers, and abstracts, as well as studies concerning the effect of additives, fibers, fillers, and reinforcement materials on PMMA, published between 1974 and 2016. Many studies have reported improvement of PMMA denture base material with the addition of fillers, fibers, nanofiller, and hybrid reinforcement. However, most of the studies were limited to in vitro investigations without bioactivity and clinical implications. Considering the findings of the review, there is no ideal denture base material, but the properties of PMMA could be improved with some modifications, especially with silanized nanoparticle addition and a hybrid reinforcement system. PMID:28553115

Microstructural Evolution of the Interface Between Pure Titanium and Low Melting Point Zr-Ti-Ni(Cu) Filler Metals

NASA Astrophysics Data System (ADS)

Lee, Dongmyoung; Sun, Juhyun; Kang, Donghan; Shin, Seungyoung; Hong, Juhwa

2014-12-01

Low melting point Zr-based filler metals with melting point depressants (MPDs) such as Cu and Ni elements are used for titanium brazing. However, the phase transition of the filler metals in the titanium joint needs to be explained, since the main element of Zr in the filler metals differs from that of the parent titanium alloys. In addition, since the MPDs easily form brittle intermetallics, that deteriorate joint properties, the phase evolution they cause needs to be studied. Zr-based filler metals having Cu content from 0 to 12 at. pct and Ni content from 12 to 24 at. pct with a melting temperature range of 1062 K to 1082 K (789 °C to 809 °C) were wetting-tested on a titanium plate to investigate the phase transformation and evolution at the interface between the titanium plate and the filler metals. In the interface, the alloys system with Zr, Zr2Ni, and (Ti,Zr)2Ni phases was easily changed to a Ti-based alloy system with Ti, Ti2Ni, and (Ti,Zr)2Ni phases, by the local melting of parent titanium. The dissolution depths of the parent metal were increased with increasing Ni content in the filler metals because Ni has a faster diffusion rate than Cu. Instead, slow diffusion of Cu into titanium substrate leads to the accumulation of Cu at the molten zone of the interface, which could form undesirable Ti x Cu y intermetallics. This study confirmed that Zr-based filler metals are compatible with the parent titanium metal with the minimum content of MPDs.

Formation of furan fatty alkyl esters from their bis-epoxide fatty esters

USDA-ARS?s Scientific Manuscript database

Epoxidation of vegetable oils and consecutive epoxide ring-opening reaction is a widely investigated path for producing biobased lubricants and polymers. The reaction mechanism and products are considered well-studied and known. In the current study, the reactions of epoxidized alkyl soyate with fou...

40 CFR 721.10210 - Soybean oil, epoxidized, reaction products with diethanolamine.

Code of Federal Regulations, 2011 CFR

2011-07-01

... 40 Protection of Environment 31 2011-07-01 2011-07-01 false Soybean oil, epoxidized, reaction... Significant New Uses for Specific Chemical Substances § 721.10210 Soybean oil, epoxidized, reaction products... chemical substance identified as soybean oil, epoxidized, reaction products with diethanolamine (PMN P-09...

Epoxide hydrolases: structure, function, mechanism, and assay.

PubMed

Arand, Michael; Cronin, Annette; Adamska, Magdalena; Oesch, Franz

2005-01-01

Epoxide hydrolases are a class of enzymes important in the detoxification of genotoxic compounds, as well as in the control of physiological signaling molecules. This chapter gives an overview on the function, structure, and enzymatic mechanism of structurally characterized epoxide hydrolases and describes selected assays for the quantification of epoxide hydrolase activity.

Unprecedented Carbonato Intermediates in Cyclic Carbonate Synthesis Catalysed by Bimetallic Aluminium(Salen) Complexes.

PubMed

Castro-Osma, José A; North, Michael; Offermans, Willem K; Leitner, Walter; Müller, Thomas E

2016-04-21

The mechanism by which [Al(salen)]2 O complexes catalyse the synthesis of cyclic carbonates from epoxides and carbon dioxide in the absence of a halide cocatalyst has been investigated. Density functional theory (DFT) studies, mass spectrometry and (1) H NMR, (13) C NMR and infrared spectroscopies provide evidence for the formation of an unprecedented carbonato bridged bimetallic aluminium complex which is shown to be a key intermediate for the halide-free synthesis of cyclic carbonates from epoxides and carbon dioxide. Deuterated and enantiomerically-pure epoxides were used to study the reaction pathway. Based on the experimental and theoretical results, a catalytic cycle is proposed. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Charcoal byproducts as potential styrene-butadiene rubber composte filler

USDA-ARS?s Scientific Manuscript database

Carbon black, a byproduct of the petroleum industry, is the world's most predominant filler for rubber composites. In this study, various renewable charcoals in the form of pyrolyzed agricultural byproducts were evaluted as potential carbon-based filler for rubber composites made with carboxylated s...

Evaluating Waste Charcoal as Potential Rubber Composite Filler

USDA-ARS?s Scientific Manuscript database

Carbon black, a byproduct of the petroleum industry, is the world's most predominant filler for rubber composites. In this study, charcoal in the form of pyrolyzed agricultural products was evaluated as potential carbon-based filler for rubber composites made with carboxylated styrene-butadiene lat...

Facial soft-tissue fillers conference: assessing the state of the science.

PubMed

Rohrich, Rod J; Hanke, C William; Busso, Mariano; Carruthers, Alastair; Carruthers, Jean; Fagien, Steven; Fitzgerald, Rebecca; Glogau, Richard; Greenberger, Phyllis E; Lorenc, Z Paul; Marmur, Ellen S; Monheit, Gary D; Pusic, Andrea; Rubin, Mark G; Rzany, Berthold; Sclafani, Anthony; Taylor, Susan; Weinkle, Susan; McGuire, Michael F; Pariser, David M; Casas, Laurie A; Collishaw, Karen J; Dailey, Roger A; Duffy, Stephen C; Edgar, Elizabeth Jan; Greenan, Barbara L; Haenlein, Kelly; Henrichs, Ronald A; Hume, Keith M; Lum, Flora; Nielsen, David R; Poulsen, Lisle; Shoaf, Lori; Schoaf, Lori; Seward, William; Begolka, Wendy Smith; Stanton, Robert G; Svedman, Katherine J; Thomas, J Regan; Sykes, Jonathan M; Wargo, Carol; Weiss, Robert A

2011-04-01

: The American Society of Plastic Surgeons and the American Academy of Dermatology, with the support of other sister societies, conducted the Facial Soft-Tissue Fillers: Assessing the State of the Science conference in December of 2009. The American Society of Plastic Surgeons and the American Academy of Dermatology established a panel of leading experts in the field of soft-tissue fillers-from researchers to clinicians-and other stakeholders for the conference to examine and discuss issues of patient safety, efficacy, and effectiveness in relation to the approved and off-label use of soft-tissue fillers, and other factors, including the training and level of experience of individuals administering fillers. This report represents the systematic literature review that examines comprehensively the available evidence and gaps in the evidence related to soft-tissue fillers, to inform and support the work of the state-of-the-science conference panel. This evidence-based medicine review will serve as the foundation for future evidence-based medicine reports in this growing field.

New biobased high functionality polyols and their use in polyurethane coatings.

PubMed

Pan, Xiao; Webster, Dean C

2012-02-13

High-functionality polyols for application in polyurethanes (PUs) were prepared by epoxide ring-opening reactions from epoxidized sucrose esters of soybean oil-epoxidized sucrose soyates-in which secondary hydroxyl groups were generated from epoxides on fatty acid chains. Ester polyols were prepared by using a base-catalyzed acid-epoxy reaction with carboxylic acids (e.g., acetic acid); ether polyols were prepared by using an acid-catalyzed alcohol-epoxy reaction with monoalcohols (e.g., methanol). The polyols were characterized by using gel permeation chromatography, FTIR spectroscopy, (1)H NMR spectroscopy, differential scanning calorimetry (DSC), and viscosity measurements. PU thermosets were prepared by using aliphatic polyisocyanates based on isophorone diisocyanate and hexamethylene diisocyanate. The properties of the PUs were studied by performing tensile testing, dynamic mechanical analysis, DSC, and thermogravimetric analysis. The properties of PU coatings on steel substrates were evaluated by using ASTM methods to determine coating hardness, adhesion, solvent resistance, and ductility. Compared to a soy triglyceride polyol, sucrose soyate polyols provide greater hardness and range of cross-link density to PU thermosets because of the unique structure of these macromolecules: well-defined compact structures with a rigid sucrose core coupled with high hydroxyl group functionality. Copyright © 2012 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

One-Pot Conversion of Epoxidized Soybean Oil (ESO) into Soy-Based Polyurethanes by MoCl₂O₂ Catalysis.

PubMed

Pantone, Vincenzo; Annese, Cosimo; Fusco, Caterina; Fini, Paola; Nacci, Angelo; Russo, Antonella; D'Accolti, Lucia

2017-02-21

An innovative and eco-friendly one-pot synthesis of bio-based polyurethanes is proposed via the epoxy-ring opening of epoxidized soybean oil (ESO) with methanol, followed by the reaction of methoxy bio-polyols intermediates with 2,6-tolyl-diisocyanate (TDI). Both synthetic steps, methanolysis and polyurethane linkage formation, are promoted by a unique catalyst, molybdenum(VI) dichloride dioxide (MoCl₂O₂), which makes this procedure an efficient, cost-effective, and environmentally safer method amenable to industrial scale-up.

Passive Cooling Enabled by Polymer Composite Coating: Dependence on Filler, Filler Size and Coating Thickness

NASA Astrophysics Data System (ADS)

Shao, Yue; Shi, Frank G.

2017-07-01

The effective passive radiation cooling that is enabled by silicone-based composites is investigated for its dependence on coating thickness and filler size in the range of nanometers to micrometers. It is established, contrary to prior reports, that the effective passive radiation cooling does not exhibit a filler size dependence, i.e., there is no optimal size at which a maximum cooling would be reached. However, the apparent cooling effect is filler type dependent and among the fillers investigated, Al2O3 exhibits the best apparent cooling effect. In addition, the apparent cooling effect is dependent on coating thickness: the thickness dependence is non-monotonic, and the maximum cooling occurs at an optimal thickness of 70 μm, regardless of filler type. Potential significant implications of the findings are also discussed.

Raman Spectroscopy of Novel UHMW Polyethylene-Based Nanocomposites with Nanographite and Nanoclay

NASA Astrophysics Data System (ADS)

Prokhorov, K. A.; Sagitova, E. A.; Averin, A. A.; Nikolaeva, G. Yu; Baimova, A. V.; Novokshonova, L. A.; Brevnov, P. N.; Pashinin, P. P.

2018-04-01

We analyze the Raman spectra of nanocomposites based on ultrahigh-molecular-weight polyethylene with nanoclay, thermoexpanded graphite, and reduced graphite oxide fillers. We discuss the potential of Raman spectroscopy for quantitative analysis of the nanocomposite structure, the influence of the fillers on the phase and conformation compositions of the polymer matrix, as well as for the monitoring of dispersion of the nanographite fillers in the nanocomposites.

B218 Weld Filler Wire Characterization for Al-Li Alloy 2195

NASA Technical Reports Server (NTRS)

Bjorkman, Gerry; Russell, Carolyn

2000-01-01

NASA Marshall Space Flight Center, Lockheed Martin Space Systems- Michoud Operations, and McCook Metals have developed an aluminum-copper weld filler wire for fusion welding aluminum lithium alloy 2195. The aluminum-copper based weld filler wire has been identified as B218, a McCook Metals designation. B218 is the result of six years of weld filler wire development funded by NASA, Lockheed Martin, and McCook Metals. The filler wire chemistry was developed to produce enhanced 2195 weld and repair weld mechanical properties over the 4043 aluminum-silicon weld filler wire, which is currently used to weld 2195 on the Super Lightweight External Tank for the NASA Space Shuttle Program. An initial characterization was performed consisting of a repair weld evaluation using B218 and 4043 weld filler wires. The testing involved room temperature and cryogenic repair weld tensile testing along with fracture toughness testing. From the testing, B218 weld filler wire produce enhanced repair weld tensile strength, ductility, and fracture properties over 4043. B218 weld filler wire has proved to be a superior weld filler wire for welding aluminum lithium alloy 2195 over 4043.

Cu-catalyzed cross-coupling reactions of epoxides with organoboron compounds.

PubMed

Lu, Xiao-Yu; Yang, Chu-Ting; Liu, Jing-Hui; Zhang, Zheng-Qi; Lu, Xi; Lou, Xin; Xiao, Bin; Fu, Yao

2015-02-11

A copper-catalyzed cross-coupling reaction of epoxides with arylboronates is described. This reaction is not limited to aromatic epoxides, because aliphatic epoxides are also suitable substrates. In addition, N-sulfonyl aziridines can be successfully converted into the products. This reaction provides convenient access to β-phenethyl alcohols, which are valuable synthetic intermediates.

The effect of carbon black filler to the mechanical properties of natural rubber as base isolation system

NASA Astrophysics Data System (ADS)

Ismail, R.; Mahadi, Z. A.; Ishak, I. S.

2018-04-01

This paper presented the study on the effect of carbon black as filler to the mechanical properties of natural rubber for base isolation system. This study used the five formulations with the different amount of carbon black filler for every sample. The samples were tested for tensile, hardness and resilience test. The samples were cured or vulcanized at 1500C for 23 minutes for every formulation. The filler used in this study was the carbon black filler with type N660. The tensile test was done to determine the ability of the sample in term of the elongation with the load at break. The hardness test, it has been done to determine the ability of the sample to resist the load. This hardness was measured in the unit of IRHD. The resilience test was being done to determine the properties of the sample in term of rebound characteristics. The finding of this study showed that, the high the loading of carbon black filler, the high the tensile strength of the sample and the high the hardness of the sample. In term of resilience, it was inversely proportional to the loading of the carbon black filler.

Filler particle size and composite resin classification systems.

PubMed

Lang, B R; Jaarda, M; Wang, R F

1992-11-01

The currently used composite resin classification systems need review if they are to continue to serve as descriptives and quantitative parameters denoting the filler particle content of these materials. Examination of the particles in 12 composite resins using a technique of washing the filler particles from the matrix of the composite resin was presented as yet another method of grouping composites according to filler particle content. Light microscopic examination of the filler particles that remained provided a separation of the 12 materials into four easily distinguished groups based on filler particle sizes. The wear of the 12 composite resins determined in a previous study was examined in relation to the classification of the materials by the currently available systems. The wear values were also examined using the groupings of the materials according to their filler particle sizes as determined by separating the particles from the matrix by the washing technique. Grouping composites on the basis of the filler particle sizes found after washing was easily correlated with wear and supported the suggestion that composites with smaller filler particles wear less.

Orbiter Gap Filler Bending Model for Re-entry

NASA Technical Reports Server (NTRS)

Campbell, Charles H.

2007-01-01

Pressure loads on a protruding gap filler during an Orbiter reentry are investigated to evaluate the likelihood of extraction due to pressure loads, and to ascertain how much bending will be induced by re-entry pressure loads. Oblique shock wave theory is utilized to develop a representation of the pressure loads induced on a gap filler for the ISSHVFW trajectory, representative of a heavy weight ISS return. A free body diagram is utilized to react the forces induced by the pressure forces. Preliminary results developed using these methods demonstrate that pressure loads, alone, are not likely causes of gap filler extraction during reentry. Assessment of the amount a gap filler will bend over is presented. Implications of gap filler bending during re-entry include possible mitigation of early boundary layer transition concerns, uncertainty in ground based measurement of protruding gap fillers from historical Orbiter flight history, and uncertainty in the use of Orbiter gap fillers for boundary layer prediction calibration. Authors will be added to the author list as appropriate.

The effects of metyrapone, chalcone epoxide, benzil, clotrimazole and related compounds on the activity of microsomal epoxide hydrolase in situ, in purified form and in reconstituted systems towards different substrates.

PubMed

Seidegård, J; DePierre, J W; Guenthner, T M; Oesch, F

1986-09-01

The influence of metyrapone, chalcone epoxide, benzil and clotrimazole on the activity of microsomal epoxide hydrolase towards styrene oxide, benzo[a]pyrene 4,5-oxide, estroxide and androstene oxide was investigated. The studies were performed using liver microsomes from rats, rabbits, mice and humans; epoxide hydrolase purified from rat liver microsomes to apparent homogeneity; and the purified enzyme incorporated into liposomes composed of egg-yolk phosphatidylcholine or total rat liver microsomal lipids. All four effectors were found to activate the hydrolysis of styrene oxide by epoxide hydrolase in situ in rat liver microsomal membranes, in agreement with earlier findings. Epoxide hydrolase activity towards styrene oxide in liver microsomes from mouse, rabbit and man was also increased by all four effectors. The most striking effect was a 680% activation by clotrimazole in rat liver microsomes. However, none of the effectors activated microsomal epoxide hydrolase more than 50% when benzo[a]pyrene 4,5-oxide, estroxide or androstene oxide was used as substrate. Indeed, clotrimazole was found to inhibit microsomal epoxide hydrolase activity towards estroxide 30-50% and towards androstene oxide 60-90%. The effects of these four compounds were found to be virtually identical in the preparations from rats, rabbits, mice and humans. The effects of metyrapone, chalcone epoxide, benzil and clotrimazole on purified epoxide hydrolase were qualitatively the same as those on epoxide hydrolase in intact microsomes, but much smaller in magnitude. These effects were increased in magnitude only slightly by incorporation of the purified enzyme into liposomes made from egg-yolk phosphatidylcholine. However, when incorporation into liposomes composed of total microsomal lipids was performed, the effects seen were essentially of the same magnitude as with intact microsomes. When the extent of activation was plotted against effector concentration, three different patterns were found with different effectors. Activation of epoxide hydrolase activity towards styrene oxide by clotrimazole was found to be uncompetitive with the substrate and highly structure specific. On the other hand, inhibition of epoxide hydrolase activity towards androstene oxide by clotrimazole was found to be competitive in microsomes. It is concluded that the marked effects of these four modulators on microsomal epoxide hydrolase activity are due to an interaction with the enzyme protein itself, but that the presence of total microsomal phospholipids allows the maximal expression leading to similar degrees of modulation as those observed in intact microsomes.(ABSTRACT TRUNCATED AT 400 WORDS)

The mechanical properties of nanofilled resin-based composites: characterizing discrete filler particles and agglomerates using a micromanipulation technique.

PubMed

Curtis, Andrew R; Palin, William M; Fleming, Garry J P; Shortall, Adrian C C; Marquis, Peter M

2009-02-01

To assess the mechanical properties of discrete filler particles representative of several inorganic fillers in modern dental resin-based composites (RBCs) and to assess the validity of a novel micromanipulation technique. RBCs with microhybrid (Filtek Z250), 'nanohybrid' (Grandio) and 'nanofilled' (Filtek Supreme), filler particle morphologies were investigated. Filler particles were provided by the manufacturer or separated from the unpolymerized resin using a dissolution technique. Filler particles (n=30) were subjected to compression using a micromanipulation technique between a descending glass probe and a glass slide. The number of distinct fractures particles underwent was determined from force/displacement and stress/deformation curves and the force at fracture and pseudo-modulus of stress was calculated. Agglomerated fillers ('nanoclusters') exhibited up to four distinct fractures, while spheroidal and irregular particles underwent either a single fracture or did not fracture following micromanipulation. Z-tests highlighted failure of nanoclusters to be significant compared with spheroidal and irregular particles (P<0.05). The mean force at first fracture of the nanoclusters was greater (1702+/-909 microN) than spheroidal and irregular particles (1389+/-1342 and 1356+/-1093 microN, respectively). Likewise, the initial pseudo-modulus of stress of nanoclusters (797+/-555 MPa) was also greater than spheroidal (587+/-439 MPa) or irregular (552+/-275 MPa) fillers. The validity of employing the micromanipulation technique to determine the mechanical properties of filler particulates was established. The 'nanoclusters' exhibited a greater tendency to multiple fractures compared with conventional fillers and possessed a comparatively higher variability of pseudo-modulus and load prior to and at fracture, which may modify the damage tolerance of the overall RBC system.

Regiospecific Epoxidation of Carvone: A Discovery-Oriented Experiment for Understanding the Selectivity and Mechanism of Epoxidation Reactions

ERIC Educational Resources Information Center

Mak, Kendrew K. W.; Lai, Y. M.; Siu, Yuk-Hong

2006-01-01

This article describes a discovery-oriented experiment for demonstrating the selectivity of two epoxidation reactions. Peroxy acids and alkaline H[subscript 2]O[subscript 2] are two commonly used reagents for alkene epoxidation. The former react preferentially with electron-rich alkenes while the latter works better with alpha,beta-unsaturated…

Exploration on effects of 15 nm SiO2 filler on miscibility, thermal stability and ionic conductivity of PMMA/ENR 50 electrolytes

NASA Astrophysics Data System (ADS)

Zamri, S. F. M.; Latif, F. A.; Ali, A. M. M.; Ibrahim, R.; Azuan, S. I. H. M.; Kamaluddin, N.; Hadip, F.

2017-02-01

The effects of silicon dioxide (SiO2) (15 nm) filler on miscibility, thermal stability and ionic conductivity of polymethyl methacrylate/50% epoxidized narural rubber (PMMA/ENR 50) electrolytes were successfully explored. Samples were prepared by solvent casting method with tetrahydrofuran (THF) as solvent and doped with lithium tetrafluoroborate (LiBF4). Fourier transform infrared spectroscopy (FTIR) confirmed the present of hydrogen bond between PMMA and ENR 50. However, the hydrogen bond was reduced when SiO2 was added. Differential scanning calorimeter (DSC) analysis shows that PMMA/ENR 50 blends exhibit two glass transition temperatures (Tgs) recorded at -35 and 89 °C corresponding to the Tg of ENR 50 rich phase (Tg1) and PMMA rich phase (Tg2), respectively. However, the two Tgs almost merging and reduced when SiO2 was added. Tg1 was found increases as SiO2 weight percent increased. Thermogravimetric analysis (TGA) revealed that thermal degradation temperatures (Tds) of SiO2 filled PMMA/ENR 50 was similar as PMMA/ENR 50. Interestingly, thermal degradation temperatures of the loss of impurities (Td1) and thermal degradation temperatures of PMMA side chain (Td2) were increased when SiO2 was added. Meanwhile thermal degradation temperatures of main PMMA and ENR 50 main chain (Td3) was decreased as SiO2 was added. There was no significant change in Td1, Td2 and Td3 as SiO2 weight percent was varied. Electrochemical impedence spectroscopy (EIS) analysis shows that room temperature ionic conductivity of SiO2 filled PMMA/ENR 50 electrolytes were higher compaed PMMA/ENR 50 electrolyte with two conductivity maxima.

The Effect of Mo Particles Addition in Ag-Cu-Ti Filler Alloy on Ti(C,N)-Based Cermet/45 Steel-Brazed Joints

NASA Astrophysics Data System (ADS)

He, Hu; Du, Xueming; Huang, Xiaokai; Xu, Weijian; Yao, Zhenhua

2018-05-01

Reliable brazing of Ti(C,N)-based cermet and 45 steel was successfully achieved by using the Mo-particle-reinforced Ag-Cu-Ti composite filler. The effects of Mo content on the interfacial microstructure and mechanical properties of Ti(C,N)-based cermet/45 steel joints were analyzed. The results showed that the joint microstructure was primarily composed of Ni3Ti+Cu3Ti2, Ag(s,s)+Cu(s.s), CuTi+Mo, Ti-based solid solution, and FeTi+Fe2Ti. With the increase in Mo content in filler, the thickness of the Ni3Ti+Cu3Ti2 layer adjacent to the Ti(C,N)-based cermet decreases, while more blocky Ti-Cu intermetallic were observed in the brazing seam. The shear strength of the joint could be significantly improved by adding suitable amounts of Mo into the Ag-Cu-Ti filler, and the peak value of 263 MPa was achieved when the alloys were brazed with Ag-Cu-Ti+8wt.%Mo composite filler at 920 °C for 20 min.

Epoxy thermoset networks derived from vegetable oils and their blends

NASA Astrophysics Data System (ADS)

Ryu, Chang; Ravalli, Matthew

2015-03-01

Epoxidized vegetable oils (EVOs), such as epoxidized soybean oil and linseed oils were prepared by the partial oxidation of the unsaturated double bonds in vegetable oils and used as monomers for preparing epoxy thermoset materials based on the cationic polymerization. These EVOs have been used to prepare epoxy thermosets of different network densities by cationic polymerization using onium salt catalyst. The crosslinked epoxy thermosets provide an ideal platform to study the structure-property-relationships of networked polymers. In particular, rheological studies on the epoxidized vegetable oil thermosets have been performed to measure the molecular weights between crosslinks (Mx) in the epoxy thermosets and to ultimately elucidate the role of functionality of epoxy groups in EVO on the mechanical and thermophysical properties of the epoxy thermoset materials. NSF DMR POLYMERS 1308617.

Copper-catalyzed cross-coupling reactions of epoxides with gem-diborylmethane: access to γ-hydroxyl boronic esters.

PubMed

Ebrahim-Alkhalil, Ahmed; Zhang, Zhen-Qi; Gong, Tian-Jun; Su, Wei; Lu, Xiao-Yu; Xiao, Bin; Fu, Yao

2016-04-07

Herein, we describe a novel copper-catalyzed epoxide opening reaction with gem-diborylmethane. Aliphatic, aromatic epoxides as well as aziridines are converted to the corresponding γ-pinacolboronate alcohols or amines in moderate to excellent yields. This new reaction provides beneficial applications for classic epoxide substrates as well as interesting gem-diborylalkane reagents.

Wetting and spreading behavior of molten brazing filler metallic alloys on metallic substrate

NASA Astrophysics Data System (ADS)

Kogi, Satoshi; Kajiura, Tetsurou; Hanada, Yukiakira; Miyazawa, Yasuyuki

2014-08-01

Wetting and spreading of molten brazing filler material are important factors that influence the brazing ability of a joint to be brazed. Several investigations into the wetting ability of a brazing filler alloy and its surface tension in molten state, in addition to effects of brazing time and temperature on the contact angle, have been carried out. In general, dissimilar-metals brazing technology and high-performance brazed joint are necessities for the manufacturing field in the near future. Therefore, to address this requirement, more such studies on wetting and spreading of filler material are required for a deeper understanding. Generally, surface roughness and surface conditions affect spreading of molten brazing filler material during brazing. Wetting by and interfacial reactions of the molten brazing filler material with the metallic substrate, especially, affect strongly the spreading of the filler material. In this study, the effects of surface roughness and surface conditions on the spreading of molten brazing filler metallic alloys were investigated. Ag-(40-x)Cu-xIn and Ag- (40-x)Cu-xSn (x=5, 10, 15, 20, 25) alloys were used as brazing filler materials. A mild-steel square plate (S45C (JIS); side: 30 mm; thickness: 3mm) was employed as the substrate. A few surfaces with varying roughness were prepared using emery paper. Brazing filler material and metallic base plate were first washed with acetone, and then a flux was applied to them. The filler, 50 mg, was placed on the center of the metallic base with the flux. A spreading test was performed under Ar gas using an electrically heated furnace, after which, the original spreading area, defined as the sessile drop area, and the apparent spreading area, produced by the capillary grooves, were both evaluated. It was observed that the spreading area decreased with increasing In and Sn content.

Quantitative characterization of brazing performance for Sn-plated silver alloy fillers

NASA Astrophysics Data System (ADS)

Wang, Xingxing; Peng, Jin; Cui, Datian

2017-12-01

Two types of AgCuZnSn fillers were prepared based on BAg50CuZn and BAg34CuZnSn alloy through a combinative process of electroplating and thermal diffusion. The models of wetting entropy and joint strength entropy of AgCuZnSn filler metals were established. The wetting entropy of the Sn-plated silver brazing alloys are lower than the traditional fillers, and its joint strength entropy value is slightly higher than the latter. The wetting entropy value of the Sn-plated brazing alloys and traditional filler metal are similar to the change trend of the wetting area. The trend of the joint strength entropy value with those fillers are consisted with the tensile strength of the stainless steel joints with the increase of Sn content.

Evaluating corn starch and corn stover biochar as renewable filler in carboxylated styrene-butadiene rubber composites

USDA-ARS?s Scientific Manuscript database

Corn starch, corn flour, and corn stover biochar were evaluated as potential renewable substitutes for carbon black as filler in rubber composites using carboxylated styrene-butadiene as the rubber matrix. Previous work has shown that starch-based fillers have very good reinforcement properties at t...

Filler Wire Development for 2195 Aluminum-Lithium

NASA Technical Reports Server (NTRS)

Bjorkman, Gerry; Cho, Alex; Russell, Carolyn; Zimmerman, Frank

1998-01-01

The presentation outline summarizes activities supporting the development of filler wire for 215 aluminum-lithium. The specific objective of the research was to identify an Al-Cu based filler wire chemistry which reduces weld susceptibility in 2195 Aluminum-Lithium welds and repairs welds along with providing adequate mechanical properties. This report is in viewgraph form.

Effect of Silver-Emitting Filler on Antimicrobial and Mechanical Properties of Soft Denture Lining Material

PubMed Central

Jabłońska-Stencel, Ewa; Pakieła, Wojciech; Mertas, Anna; Bobela, Elżbieta; Kasperski, Jacek; Chladek, Grzegorz

2018-01-01

Colonization of silicone-based soft lining materials by pathogenic yeast-type fungi is a common problem associated with the use of dentures. In this study, silver sodium hydrogen zirconium phosphate (SSHZP) was introduced into polydimethylsiloxane-based material as an antimicrobial filler at concentrations of 0.25, 0.5, 1, 2, 4, 6, 8, 10, 12, and 14% (w/w). The in vitro antimicrobial efficacy was investigated. Candida albicans was used as a characteristic representative of pathogenic oral microflora. Staphylococcus aureus and Escherichia coli were used as the typical Gram-positive and Gram-negative bacterial strains, respectively. The effect of filler addition on the Shore A hardness, tensile strength, tensile bond strength, sorption, and solubility was investigated. An increase in the filler concentration resulted in an increase in hardness, sorption, and solubility, and for the highest concentration, a decrease in bond strength. The favorable combination of antimicrobial efficacy with other properties was achieved at filler concentrations ranging from 2% to 10%. These composites exhibited mechanical properties similar to the material without the antimicrobial filler and enhanced in vitro antimicrobial efficiency. PMID:29470441

Filler wire for aluminum alloys and method of welding

NASA Technical Reports Server (NTRS)

Bjorkman, Jr., Gerald W. O. (Inventor); Cho, Alex (Inventor); Russell, Carolyn K. (Inventor)

2003-01-01

A weld filler wire chemistry has been developed for fusion welding 2195 aluminum-lithium. The weld filler wire chemistry is an aluminum-copper based alloy containing high additions of titanium and zirconium. The additions of titanium and zirconium reduce the crack susceptibility of aluminum alloy welds while producing good weld mechanical properties. The addition of silver further improves the weld properties of the weld filler wire. The reduced weld crack susceptibility enhances the repair weldability, including when planishing is required.

Versatile Synthesis of Stable, Functional Polypeptides via Reaction with Epoxides.

PubMed

Gharakhanian, Eric G; Deming, Timothy J

2015-06-08

Methodology was developed for efficient alkylation of methionine residues using epoxides as a general strategy to introduce a wide range of functional groups onto polypeptides. Use of a spacer between epoxide and functional groups further allowed addition of sterically demanding functionalities. Contrary to other methods to alkylate methionine residues, epoxide alkylations allow the reactions to be conducted in wet protic media and give sulfonium products that are stable against dealkylation. These functionalizations are notable since they are chemoselective, utilize stable and readily available epoxides, and allow facile incorporation of an unprecedented range of functional groups onto simple polypeptides using stable linkages.

Epoxide hydrolase-lasalocid a structure provides mechanistic insight into polyether natural product biosynthesis.

PubMed

Wong, Fong T; Hotta, Kinya; Chen, Xi; Fang, Minyi; Watanabe, Kenji; Kim, Chu-Young

2015-01-14

Biosynthesis of some polyether natural products involves a kinetically disfavored epoxide-opening cyclic ether formation, a reaction termed anti-Baldwin cyclization. One such example is the biosynthesis of lasalocid A, an ionophore antibiotic polyether. During lasalocid A biosynthesis, an epoxide hydrolase, Lsd19, converts the bisepoxy polyketide intermediate into the tetrahydrofuranyl-tetrahydropyran product. We report the crystal structure of Lsd19 in complex with lasalocid A. The structure unambiguously shows that the C-terminal domain of Lsd19 catalyzes the intriguing anti-Baldwin cyclization. We propose a general mechanism for epoxide selection by ionophore polyether epoxide hydrolases.

Thermal properties of oil palm nano filler/kenaf reinforced epoxy hybrid nanocomposites

NASA Astrophysics Data System (ADS)

Saba, N.; Paridah, M. T.; Abdan, K.; Ibrahim, N. A.

2016-11-01

The aim of this research study was to fabricate nano oil palm empty fruit bunch (OPEFB)/kenaf/epoxy hybrid nanocomposites and to make comparative study on the thermal properties of nano OPEFB/kenaf/epoxy hybrid nanocomposites with the montmorillonite (MMT)/kenaf/epoxy hybrid nanocomposites and organically modified MMT (OMMT)/kenaf/epoxy hybrid nanocomposites. Epoxy based kenaf hybrid nanocomposites was prepared by dispersing the nano filler (nano OPEFB filler, MMT, OMMT) at 3% loading through high speed mechanical stirrer followed by hand lay-up technique. Thermal properties of hybrid nanocomposites were analyzed through thermogravimetry analyzer (TGA), and differential scanning calorimetry (DSC). Obtained results specified that addition of nano OPEFB filler improves the thermal stability and char yield of kenaf/epoxy composites. Furthermore, the increase in decomposition temperature by the nano OPEFB filler was quite comparable to the MMT/kenaf/epoxy but relatively less than OMMT/kenaf/epoxy hybrid nanocomposites. We concluded from overall consequences that the nano OPEFB filler can be used as the promising and innovative alternative of existing expensive nano filler, with relatively lesser impact on the environment having marked pronounced impact on the construction, automotive, aerospace, electronics and semiconducting sectors as future industries based on bio-wastes with satisfactory light weight and thermal stability on other side.

A systematic review of filler agents for aesthetic treatment of HIV facial lipoatrophy (FLA).

PubMed

Jagdeo, Jared; Ho, Derek; Lo, Alex; Carruthers, Alastair

2015-12-01

HIV facial lipoatrophy (FLA) is characterized by facial volume loss. HIV FLA affects the facial contours of the cheeks, temples, and orbits, and is associated with social stigma. Although new highly active antiretroviral therapy medications are associated with less severe FLA, the prevalence of HIV FLA among treated individuals exceeds 50%. The goal of our systematic review is to examine published clinical studies involving the use of filler agents for aesthetic treatment of HIV FLA and to provide evidence-based recommendations based on published efficacy and safety data. A systematic review of the published literature was performed on July 1, 2015, on filler agents for aesthetic treatment of HIV FLA. Based on published studies, poly-L-lactic acid is the only filler agent with grade of recommendation: B. Other reviewed filler agents received grade of recommendation: C or D. Poly-L-lactic acid may be best for treatment over temples and cheeks, whereas calcium hydroxylapatite, with a Food and Drug Administration indication of subdermal implantation, may be best used deeply over bone for focal enhancement. Additional long-term randomized controlled trials are necessary to elucidate the advantages and disadvantages of fillers that have different biophysical properties, in conjunction with cost-effectiveness analysis, for treatment of HIV FLA. Published by Elsevier Inc.

Substrate specificity of the violaxanthin de-epoxidase of the primitive green alga Mantoniella squamata (Prasinophyceae).

PubMed

Goss, Reimund

2003-09-01

The substrate specificity of the enzyme violaxanthin de-epoxidase (VDE) of the primitive green alga Mantoniella squamata (Prasinophyceae) was tested in in vitro enzyme assays employing the following xanthophyll mono-epoxides: antheraxanthin (Ax), diadinoxanthin (Ddx), lutein-epoxide (LE), cryptoxanthin-epoxide (CxE), 9- cis neoxanthin (cNx), all- trans neoxanthin (Nx), and xanthophyll di-epoxides: 9- cis violaxanthin (cVx), all- trans violaxanthin (Vx), cryptoxanthin-di-epoxide (CxDE). The data presented in this study show that the VDE of M. squamata not only exhibits a low affinity for the mono-epoxide Ax, as has been reported by R. Frommolt et al. (2001, Planta 213:446-456), but has a reduced substrate affinity for the mono-epoxides Ddx, LE, CxE, and Nx as well. On the other hand, xanthophylls with a second epoxy-group (Vx, CxDE) can be de-epoxidized with a higher efficiency. Such a preference for xanthophyll di-epoxides cannot be observed for the higher-plant VDE, where, in general, no marked differences in the pigment de-epoxidation rates between xanthophyll mono- and di-epoxides are visible. Despite this substantial difference between the VDEs of M. squamata and S. oleracea there are also features common to both enzymes. Neither VDE is able to convert xanthophylls with a 9- cis configuration in the acyclic polyene chain and both rely on substrates in the all- trans configuration. Both enzymes furthermore exhibit a dependence of enzyme activity on the polarity of the substrate. Highly polar (Nx) or non-polar (CxE) xanthophylls are de-epoxidized with greatly reduced rates in comparison to substrates with an intermediate polarity (Vx, Ax, LE, Ddx). This dependence on substrate polarity becomes more obvious when the higher-plant VDE is examined, as the substrate affinity of the VDE of M. squamata is more strongly influenced by the existence or absence of a second epoxy-group. In summary, the data presented in this study underline the fact that different VDEs, although in general catalyzing the same reaction sequence, are functionally diverse.

Comparative study on thermodynamic characteristics of AgCuZnSn brazing alloys

NASA Astrophysics Data System (ADS)

Wang, Xingxing; Li, Shuai; Peng, Jin

2018-01-01

AgCuZnSn brazing alloys were prepared based on the BAg50CuZn filler metal through electroplating diffusion process, and melting alloying method. The thermodynamics of phase transformations of those fillers were analyzed by non-isothermal differentiation and integration methods of thermal analysis kinetics. In this study, it was demonstrated that as the Sn content increased, the reaction fractional integral curves of AgCuZnSn fillers from solid to liquid became straighter at the endothermic peak. Under the same Sn contents, the reaction fractional integral curve of the Sn-plated filler metal was straighter, and the phase transformation activation energy was higher compared to the traditional silver filler metal. At the 7.2 wt% Sn content, the activation energies and pre-exponential factors of the two fillers reached the maximum, then the phase transformation rate equations of the Sn-plated silver filler and the traditional filler were determined as: k = 1.41 × 1032exp(-5.56 × 105/RT), k = 7.29 × 1020exp(-3.64 × 105/RT), respectively.

Probing Competitive and Co-operative Hydroxyl and Ammonium Hydrogen-Bonding Directed Epoxidations.

PubMed

Brambilla, Marta; Brennan, Méabh B; Csatayová, Kristína; Davies, Stephen G; Fletcher, Ai M; Kennett, Alice M R; Lee, James A; Roberts, Paul M; Russell, Angela J; Thomson, James E

2017-10-06

The diastereoselectivities and rates of epoxidation (upon treatment with Cl 3 CCO 2 H then m-CPBA) of a range of cis- and trans-4-aminocycloalk-2-en-1-ol derivatives (containing five-, six-, and seven-membered rings) have been investigated. In all cases where the two potential directing groups can promote epoxidation on opposite faces of the ring scaffold, evidence of competitive epoxidation pathways, promoted by hydrogen-bonding to either the in situ formed ammonium moiety or the hydroxyl group, was observed. In contrast to the relative directing group abilities already established for the six-membered ring system (NHBn ≫ OH > NBn 2 ), an N,N-dibenzylammonium moiety appeared more proficient than a hydroxyl group at directing the stereochemical course of the epoxidation reaction in a five- or seven-membered system. In the former case, this was rationalized by the drive to minimize torsional strain in the transition state being coupled with assistance from hydrogen-bonding to the ammonium moiety. In the latter case, this was ascribed to the steric bulk of the ammonium moiety disfavoring conformations in which hydrogen-bonding to the hydroxyl group results in direction of the epoxidation to the syn face. In cases where the two potential directing groups can promote epoxidation on the same face of the ring scaffold, an enhancement of epoxidation diastereoselectivity was not observed, while introduction of a second, allylic heteroatom to the substrate results in diminishment of the rate of epoxidation in all cases. Presumably, reduction of the nucleophilicity of the olefin by the second, inductively electron-withdrawing heteroatom is the dominant factor, and any assistance to the epoxidation reaction by the potential to form hydrogen-bonds to two directing groups rather than one is clearly unable to overwhelm it.

Design and preparation of plant oil-based polymers and their applications

NASA Astrophysics Data System (ADS)

Ahn, Byung-Jun Kollbe

Renewable materials are desirable for many applications due to the finite fossil resources and environmental issues. Plant oil is one of the most promising renewable feedstocks. Plant oils and functionalized oleo-chemicals including functionalized soybean oils have become attractive sustainable chemicals for industrial applications. Especially, epoxidized oleo-chemicals such as epoxidized soybean oil (ESO) are one of the most well-known readily available inexpensive functionalized plant oils. In this study, novel polymers and nanocomposites for sustainable materials applications were designed and prepared via ring-opening of epoxide in plant oils, and their chemical and physical properties were characterized. The novel transparent elastomers derived from functionalized plant oils have a great potential as flexible electronic and biological applications with their inherent low toxicity. Especially, their rheological properties showed a potential for pressure sensitive adhesives (PSAs). The dominant thermal stability and transparency were obtained via green processing: one pot, single step, fast reactions in moderate conditions, or solvent-free UV curing conditions. These oleo-based elastomers presented excellent end-use properties for PSAs application comparable to commercial PSA tapes. Based on the principal chemical studies, the roles of the each component have been identified: polymer derived from the ring-opening of epoxides as an elastomer, and dihydroxylated triglycerides as a tackifier. Their interaction was also elucidated with an element label analysis. The mechanical and rheological properties of the oleo-polymer as PSAs were able to be improved with a rosin ester tackifier. In addition, biogreases and bio-thermoplastics were developed via the environmentally benign process, which will contribute to further application on the production of new bio-based materials. Further, this study essays a novel acid functionalized iron/iron oxide nanoparticles catalyst with excellent product yields for epoxide ring opening of oleochemicals for a greener synthetic method of biopolyols, and excellent environmental benefits with life cycle assessment of syntheses. Those functionalized iron/iron oxide core shell nanoparticles catalysts has great potential for biomedical engineering process with the highest magnetization of Fe(0) core among all metals.

A review of chemical-approach and ultramorphological studies on the development of fluoride-releasing dental adhesives comprising new pre-reacted glass ionomer (PRG) fillers.

PubMed

Ikemura, Kunio; Tay, Franklin R; Endo, Takeshi; Pashley, David H

2008-05-01

This paper reviews our recent studies on fluoride-releasing adhesives and the related studies in this field based on information from original research papers, reviews, and patent literatures. A revolutionary PRG (pre-reacted glass ionomer) filler technology--where fillers were prepared by the acid-base reaction of a fluoroaluminosilicate glass with polyalkenoic acid in water, was newly developed, and a new category as "Giomer" was introduced into the market. On fluoride release capability, SIMS examination revealed in vitro fluoride ion uptake by dentin substrate from the PRG fillers in dental adhesive. On bonding durability, it was found that the improved durability of resin-dentin bonds might be achieved not only via the strengthened dentin due to fluoride ion uptake from the PRG-Ca fillers, but also due to retention of relatively insoluble 4-AETCa formed around remnant apatite crystallites within the hybrid layer in 4-AET-containing self-etching adhesives. On ultramorphological study of the resin-dentin interface, TEM images of the PRG-Ca fillers revealed that the dehydrated hydrogel was barely distinguishable from normal glass fillers, if not for the concurrent presence of remnant, incompletely reacted glass cores. In conclusion, it was expected that uptake of fluoride ions with cariostatic effect from PRG-Ca fillers would endow dentin substrates with the benefit of secondary caries prevention, together with an effective and durable adhesion to dentin.

Study on Mg/Al Weld Seam Based on Zn–Mg–Al Ternary Alloy

PubMed Central

Liu, Liming; Liu, Fei; Zhu, Meili

2014-01-01

Based on the idea of alloying welding seams, a series of Zn–xAl filler metals was calculated and designed for joining Mg/Al dissimilar metals by gas tungsten arc (GTA) welding. An infrared thermography system was used to measure the temperature of the welding pool during the welding process to investigate the solidification process. It was found that the mechanical properties of the welded joints were improved with the increasing of the Al content in the Zn–xAl filler metals, and when Zn–30Al was used as the filler metal, the ultimate tensile strength could reach a maximum of 120 MPa. The reason for the average tensile strength of the joint increasing was that the weak zone of the joint using Zn–30Al filler metal was generated primarily by α-Al instead of MgZn2. When Zn–40Al was used as the filler metal, a new transition zone, about 20 μm-wide, appeared in the edge of the fusion zone near the Mg base metal. Due to the transition zones consisting of MgZn2- and Al-based solid solution, the mechanical property of the joints was deteriorated. PMID:28788508

The rabbit liver microsomal biotransformation of 1,1-dialkylethylenes: enantioface selection of epoxidation and enantioselectivity of epoxide hydrolysis.

PubMed

Bellucci, G; Chiappe, C; Cordoni, A; Marioni, F

1994-01-01

The rabbit liver microsomal biotransformation of alpha-methylstyrene (1a), 2-methyl-1-hexene (1b), 2,4,4-trimethyl-1-pentene (1c), and 1,3,3-trimethyl-1-butene (1d) has been investigated with the aim at establishing the enantioface selection of the cytochrome P-450-promoted epoxidation of the double bond and the enantioselectivity of microsomal epoxide hydrolase(mEH)-catalyzed hydrolysis of the resulting epoxides. GLC on a Chiraldex G-TA (ASTEC) column was used to determine the enantiomeric composition of the products. The epoxides 2 first produced in incubations carried out in the presence of an NADPH regenerating system were not detected, being rapidly hydrolyzed by mEH to diols 3. The enantiomeric composition of the latter showed that no enantioface selection occurred in the epoxidation of 1c and 1d, and a very low (8%) ee of the (R)-epoxide was formed from 1b. Incubation of racemic epoxides 2b-d with the microsomal fraction showed that the mEH-catalyzed hydrolysis of 2c and 2d was practically nonenantioselective, while that of 2b exhibited a selectivity E = 4.9 favoring the hydrolysis of the (S)-enantiomer. A comparison of these results with those previously obtained for linear and branched chain alkyl monosubstituted oxiranes shows that the introduction of the second alkyl substituent suppresses the selectivity of the mEH reaction of the latter and reverses that of the former substrates.

Microvascular complications associated with injection of cosmetic facelift dermal fillers

NASA Astrophysics Data System (ADS)

Yousefi, Siavash; Prendes, Mark; Chang, Shu-Hong; Wang, Ruikang K.

2015-02-01

Minimally-invasive cosmetic surgeries such as injection of subdermal fillers have become very popular in the past decade. Although rare, some complications may follow injections such as tissue necrosis and even blindness. There exist two hypothesis regarding source of these complications both of which include microvasculature. The first hypothesis is that fillers in between the tissue structures and compress microvasculature that causes blockage of tissue neutrition and oxygen exchange in the tissue. In another theory, it is hypothesized that fillers move inside major arteries and block the arteries/veins. In this paper, we study these hypotheses using optical coherence tomography and optical microangiography technologies with different hyaluronic-acid fillers in a mouse ear model. Based on our observations, the fillers eventually block arteries/veins if injected directly into them that eventually causes tissue necrosis.

Influence of particle size on water absorption capacity and mechanical properties of polyethylene-wood flour composites

NASA Astrophysics Data System (ADS)

Zykova, A. K.; Pantyukhov, P. V.; Kolesnikova, N. N.; Popov, A. A.; Olkhov, A. A.

2015-10-01

Biocomposites based on low density polyethylene (LDPE) and birch wood flour (WF) were investigated. The mechanical properties and water absorption capacity were examined depending on the particle size of a filler in biocomposites. The aim of the paper is the investigation of composite properties depending on the filler particle size. The filler particle sizes were 0-80 µm, 80-140 µm, 140-200 µm, and 0-200 µm. The tensile strength of composite samples varied within the range 5.7-8.2 MPa. Elongation at break of composites varied within the range 5.1-7.5%. Highest mechanical properties were found in composites with the lowest filler fraction. Highest water absorption was observed in composition with a complex fraction of the filler. The influence of the filler particle size on composite properties was shown. It was found that an increase of the filler particle size decreases mechanical parameters and increases water absorption.

Advanced inorganic separators for alkaline batteries

NASA Technical Reports Server (NTRS)

Sheibley, D. W. (Inventor)

1982-01-01

A flexible, porous battery separator comprising a coating applied to a porous, flexible substrate is described. The coating comprises: (1) a thermoplastic rubber-based resin which is insoluble and unreactive in the alkaline electrolyte; (2) a polar organic plasticizer which is reactive with the alkaline electrolyte to produce a reaction product which contains a hydroxyl group and/or a carboxylic acid group; and (3) a mixture of polar particulate filler materials which are unreactive with the electrolyte, the mixture comprising at least one first filler material having a surface area of greater than 25 meters sq/gram, at least one second filler material having a surface area of 10 to 25 sq meters/gram, wherein the volume of the mixture of filler materials is less than 45% of the total volume of the fillers and the binder, the filler surface area per gram of binder is about 20 to 60 sq meters/gram, and the amount of plasticizer is sufficient to coat each filler particle. A method of forming the battery separator is also described.

Advanced inorganic separators for alkaline batteries and method of making the same

NASA Technical Reports Server (NTRS)

Sheibley, D. W. (Inventor)

1983-01-01

A flexible, porous battery separator includes a coating applied to a porous, flexible substrate. The coating comprises: (1) a thermoplastic rubber-based resin which is insoluble and unreactive in the alkaline electrolyte, (2) a polar organic plasticizer which is reactive with the alkaline electrolyte to produce a reaction product which contains a hydroxyl group and/or a carboxylic acid group, and (3) a mixture of polar particulate filler materials which are unreactive with the electrode. The mixture comprises at least one first filler material having a surface area of greater than 25 sq meters/gram, at last one second filler material having a surface area of 10 to 25 sq meters/gram. The volume of the mixture of filler materials is less than 45% of the total volume of the fillers and the binder. The filler surface area per gram of binder is about 20 to 60 sq meters/gram, and the amount of plasticizer is sufficient to coat each filler particle.

Physicochemical Characterization of Functional Lignin–Silica Hybrid Fillers for Potential Application in Abrasive Tools

PubMed Central

Strzemiecka, Beata; Klapiszewski, Łukasz; Jamrozik, Artur; Szalaty, Tadeusz J.; Matykiewicz, Danuta; Sterzyński, Tomasz; Voelkel, Adam; Jesionowski, Teofil

2016-01-01

Functional lignin–SiO2 hybrid fillers were prepared for potential application in binders for phenolic resins, and their chemical structure was characterized. The properties of these fillers and of composites obtained from them with phenolic resin were compared with those of systems with lignin or silica alone. The chemical structure of the materials was investigated by Fourier transform infrared spectroscopy (FT-IR) and carbon-13 nuclear magnetic resonance spectroscopy (13C CP MAS NMR). The thermal stability of the new functional fillers was examined by thermogravimetric analysis–mass spectrometry (TG-MS). Thermo-mechanical properties of the lignin–silica hybrids and resin systems were investigated by dynamic mechanical thermal analysis (DMTA). The DMTA results showed that abrasive composites with lignin–SiO2 fillers have better thermo-mechanical properties than systems with silica alone. Thus, fillers based on lignin might provide new, promising properties for the abrasive industry, combining the good properties of lignin as a plasticizer and of silica as a filler improving mechanical properties. PMID:28773639

Sequential enzymatic epoxidation involved in polyether lasalocid biosynthesis.

PubMed

Minami, Atsushi; Shimaya, Mayu; Suzuki, Gaku; Migita, Akira; Shinde, Sandip S; Sato, Kyohei; Watanabe, Kenji; Tamura, Tomohiro; Oguri, Hiroki; Oikawa, Hideaki

2012-05-02

Enantioselective epoxidation followed by regioselective epoxide opening reaction are the key processes in construction of the polyether skeleton. Recent genetic analysis of ionophore polyether biosynthetic gene clusters suggested that flavin-containing monooxygenases (FMOs) could be involved in the oxidation steps. In vivo and in vitro analyses of Lsd18, an FMO involved in the biosynthesis of polyether lasalocid, using simple olefin or truncated diene of a putative substrate as substrate mimics demonstrated that enantioselective epoxidation affords natural type mono- or bis-epoxide in a stepwise manner. These findings allow us to figure out enzymatic polyether construction in lasalocid biosynthesis. © 2012 American Chemical Society

Epoxide reduction with hydrazine on graphene: a first principles study.

PubMed

Kim, Min Chan; Hwang, Gyeong S; Ruoff, Rodney S

2009-08-14

Mechanisms for epoxide reduction with hydrazine on a single-layer graphene sheet are examined using quantum mechanical calculations within the framework of gradient-corrected spin-polarized density-functional theory. We find that the reduction reaction is mainly governed by epoxide ring opening which is initiated by H transfer from hydrazine or its derivatives. In addition, our calculations suggest that the epoxide reduction by hydrazine may predominantly follow a direct Eley-Rideal mechanism rather than a Langmuir-Hinshelwood mechanism. We also discuss the generation of various hydrazine derivatives during the reduction of graphene oxide with hydrazine and their potential contribution to lowering the barrier height of epoxide ring opening.

Preparation and characterization of zinc sulphide nanocomposites based on acrylonitrile butadiene rubber

NASA Astrophysics Data System (ADS)

Ramesan, M. T.; Nihmath, A.; Francis, Joseph

2013-06-01

Rubber composite based on acrylonitrile butadiene rubber (NBR) reinforced with nano zinc sulphide (ZnS) have been prepared via vulcanization process and characterized by several techniques. Processing characteristics such as scorch time, optimum cure time decreases with increase in concentration of nano filler in acrylonitrile butadiene rubber. Mechanical properties such as tensile and tear strength increases with increase in concentration of nano filler up to 7 phr of loading thereafter the value decreases, whereas hardness, and flame resistance increases with the dosage of fillers. These enhanced properties are due to the homogenous dispersion of nano fillers in NBR matrix, which is evidenced from the structure that evaluated using X-ray diffraction (XRD) and scanning electron microscopy (SEM).

Catalytic Efficiency of Titanium Dioxide (TiO2) and Zeolite ZSM-5 Catalysts in the in-situ Epoxidation of Palm Olein

NASA Astrophysics Data System (ADS)

Yunus, M. Z. Mohd; Jamaludin, S. K.; Abd. Karim, S. F.; Gani, A. Abd; Sauki, A.

2018-05-01

Titanium dioxide and zeolite ZSM-5 are the commonly used heterogeneous catalysts in many chemical reactions. They have several advantages such as low cost and environmental friendly. In this study, titanium dioxide and zeolite ZSM-5 act as catalyst in the in-situ epoxidation of palm olein. Epoxidation of palm olein was carried out by using in-situ generated performic acid to produce epoxidized palm olein in a semi-batch reactor at different temperatures (45°C and 60°C) and agitation speed of 400 rpm. The effects of both catalysts are studied to compare their efficiency in catalyzing the in-situ epoxidation. Epoxidized palm olein was analyzed by using percent of relative conversion to oxirane (RCO%) and fourier transform infrared spectroscopy (FTIR). Surface area of the catalysts used were then characterized by using BET. The results indicated that titanium dioxide is a better catalyst in the in-situ epoxidation of palm olein since it provides higher RCO% compared to Zeolite ZSM-5 at 45°C.

Epoxidation of Short-Chain Alkenes by Resting-Cell Suspensions of Propane-Grown Bacteria

PubMed Central

Hou, Ching T.; Patel, Ramesh; Laskin, Allen I.; Barnabe, Nancy; Barist, Irene

1983-01-01

Sixteen new cultures of propane-utilizing bacteria were isolated from lake water from Warinanco Park, Linden, N.J. and from lake and soil samples from Bayway Refinery, Linden, N.J. In addition, 19 known cultures obtained from culture collections were also found to be able to grow on propane as the sole carbon and energy source. In addition to their ability to oxidize n-alkanes, resting-cell suspensions of both new cultures and known cultures grown on propane oxidize short-chain alkenes to their corresponding 1,2-epoxides. Among the substrate alkenes, propylene was oxidized at the highest rate. In contrast to the case with methylotrophic bacteria, the product epoxides are further metabolized. Propane and other gaseous n-alkanes inhibit the epoxidation of propylene. The optimum conditions for in vivo epoxidation are described. Results from inhibition studies indicate that a propane monooxygenase system catalyzes both the epoxidation and hydroxylation reactions. Experiments with cell-free extracts show that both hydroxylation and epoxidation activities are located in the soluble fraction obtained after 80,000 × g centrifugation. PMID:16346338

Ultrasound-assisted chemoenzymatic epoxidation of soybean oil by using lipase as biocatalyst.

PubMed

Bhalerao, Machhindra S; Kulkarni, Vaishali M; Patwardhan, Anand V

2018-01-01

The present work reports the use of ultrasonic irradiation for enhancing lipase catalyzed epoxidation of soybean oil. Higher degree of unsaturated fatty acids, present in the soybean oil was converted to epoxidized soybean oil by using an immobilized lipase, Candida antarctica (Novozym 435). The effects of various parameters on the relative percentage conversion of the double bond to oxirane oxygen were investigated and the optimum conditions were established. The parameters studied were temperature, hydrogen peroxide to ethylenic unsaturation mole ratio, stirring speed, solvent ratio, catalyst loading, ultrasound frequency, ultrasound input power and duty cycle. The main objective of this work was to intensify chemoenzymatic epoxidation of the soybean oil by using ultrasound, to reduce the time required for epoxidation. Epoxidation of the soybean oil was achieved under mild reaction conditions by indirect ultrasonic irradiations (using ultrasonic bath). The relative percentage conversion to oxirane oxygen of 91.22% was achieved within 5h. The lipase was remarkably stable under optimized reaction conditions, later was recovered and reused six times to produce epoxidized soybean oil (ESO). Copyright © 2017 Elsevier B.V. All rights reserved.

Epoxide Hydrolase Conformational Heterogeneity for the Resolution of Bulky Pharmacologically Relevant Epoxide Substrates.

PubMed

Serrano-Hervás, Eila; Casadevall, Guillem; Garcia-Borràs, Marc; Feixas, Ferran; Osuna, Sílvia

2018-04-06

The conformational landscape of Bacillus megaterium epoxide hydrolase (BmEH) and how it is altered by mutations that confer the enzyme the ability to accept bulky epoxide substrates has been investigated. Extensive molecular dynamics (MD) simulations coupled to active site volume calculations have unveiled relevant features of the enzyme conformational dynamics and function. Our long-timescale MD simulations identify key conformational states not previously observed by means of X-ray crystallography and short MD simulations that present the loop containing one of the catalytic residues, Asp239, in a wide-open conformation, which is likely involved in the binding of the epoxide substrate. Introduction of mutations M145S and F128A dramatically alters the conformational landscape of the enzyme. These singly mutated variants can accept bulky epoxide substrates due to the disorder induced by mutation in the α-helix containing the catalytic Tyr144 and some parts of the lid domain. These changes impact the enzyme active site, which is substantially wider and more complementary to the bulky pharmacologically relevant epoxide substrates. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Inactive Mineral Filler as a Stiffness Modulus Regulator in Foamed Bitumen-Modified Recycled Base Layers

NASA Astrophysics Data System (ADS)

Buczyński, Przemyslaw; Iwański, Marek

2017-10-01

The article presents the results of a cold recycled mix test with a foam bitumen including the addition of the inactive mineral filler as a dust of basalt. Basalt dust was derived from dedusting system by extraction of aggregates in the mine. Assessment of the impact of a basalt dust on the properties of a recycled base layer was carried out in terms of the amount of mineral filler (basalt) in the composition of the mineral mixture. This experiment involved a dosing of mineral filler in range from 5 to 20% with steps of 7.5% in the mineral mixture composition. The foamed bitumen was performed at optimum foaming process settings (ie. bitumen temperature, air pressure) and at 2.5% of the water content. The amount of a hydraulic binder as a Portland cement was 2.0%. The evaluation of rheological properties allowed to determine whether the addition of inactive mineral fillers can act as a stiffness modulus controller in the recycled base layer. The analysis of the rheological properties of a recycled base layer in terms of the amount of inactive fillers was performed in accordance with given standard EN 12697-26 Annex D. The study was carried out according to the direct tension-compression test methodology on cylindrical samples. The sample was subjected to the oscillatory sinusoidal strain ε0 < 25με. Studies carried out at a specific temperature set-points: - 7°C, 5°C, 13°C, 25°C and 40°C and at the frequency 0.1 Hz, 0.3 Hz, 1 Hz, 3 Hz, 10 Hz and 20 Hz. The obtained results allow to conclude that the use of an inactive filler can reduce the stiffness of an appropriate designed mixes of the cold recycled foundation. In addition, the analysis of the relation E‧-E″ showed a similar behaviour of a recycled base, regardless of the amount of inactive fillers in the mix composition, at high temperatures/high frequency of induced load.

Arabidopsis thaliana EPOXIDE HYDROLASE1 (AtEH1) is a cytosolic epoxide hydrolase involved in the synthesis of poly-hydroxylated cutin monomers.

PubMed

Pineau, Emmanuelle; Xu, Lin; Renault, Hugues; Trolet, Adrien; Navrot, Nicolas; Ullmann, Pascaline; Légeret, Bertrand; Verdier, Gaëtan; Beisson, Fred; Pinot, Franck

2017-07-01

Epoxide hydrolases (EHs) are present in all living organisms. They have been extensively characterized in mammals; however, their biological functions in plants have not been demonstrated. Based on in silico analysis, we identified AtEH1 (At3g05600), a putative Arabidopsis thaliana epoxide hydrolase possibly involved in cutin monomer synthesis. We expressed AtEH1 in yeast and studied its localization in vivo. We also analyzed the composition of cutin from A. thaliana lines in which this gene was knocked out. Incubation of recombinant AtEH1 with epoxy fatty acids confirmed its capacity to hydrolyze epoxides of C18 fatty acids into vicinal diols. Transfection of Nicotiana benthamiana leaves with constructs expressing AtEH1 fused to enhanced green fluorescent protein (EGFP) indicated that AtEH1 is localized in the cytosol. Analysis of cutin monomers in loss-of-function Ateh1-1 and Ateh1-2 mutants showed an accumulation of 18-hydroxy-9,10-epoxyoctadecenoic acid and a concomitant decrease in corresponding vicinal diols in leaf and seed cutin. Compared with wild-type seeds, Ateh1 seeds showed delayed germination under osmotic stress conditions and increased seed coat permeability to tetrazolium red. This work reports a physiological role for a plant EH and identifies AtEH1 as a new member of the complex machinery involved in cutin synthesis. © 2017 CNRS New Phytologist © 2017 New Phytologist Trust.

The stability of the three transmembrane and the four transmembrane human vitamin K epoxide reductase models

NASA Astrophysics Data System (ADS)

Wu, Sangwook

2016-04-01

The three transmembrane and the four transmembrane helix models are suggested for human vitamin K epoxide reductase (VKOR). In this study, we investigate the stability of the human three transmembrane/four transmembrane VKOR models by employing a coarse-grained normal mode analysis and molecular dynamics simulation. Based on the analysis of the mobility of each transmembrane domain, we suggest that the three transmembrane human VKOR model is more stable than the four transmembrane human VKOR model.

Stereoselective construction of the 5-hydroxy diazabicyclo[4.3.1]decane-2-one scaffold, a privileged motif for FK506-binding proteins.

PubMed

Bischoff, Matthias; Sippel, Claudia; Bracher, Andreas; Hausch, Felix

2014-10-17

A stereoselective synthesis of a derivatized bicyclic [4.3.1]decane scaffold based on an acyclic precursor is described. The key steps involve a Pd-catalyzed sp(3)-sp(2) Negishi-coupling, an asymmetric Shi epoxidation, and an intramolecular epoxide opening. Representative derivatives of this novel scaffold were synthesized and found to be potent inhibitors of the psychiatric risk factor FKBP51, which bound to FKBP51 with the intended molecular binding mode.

Direct Epoxidation of Propylene over Stabilized Cu + Surface Sites on Ti Modified Cu 2O

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yang, X.; Kattel, S.; Xiong, K.

2015-07-17

Direct propylene epoxidation by O 2 is a challenging reaction because of the strong tendency for complete combustion. Results from the current study demonstrate the feasibility to tune the epoxidation selectivity by generating highly dispersed and stabilized Cu + active sites in a TiCuO x mixed oxide. The TiCuO x surface anchors the key surface intermediate, oxametallacycle, leading to higher selectivity for epoxidation of propylene.

Vibration anesthesia for the reduction of pain with facial dermal filler injections.

PubMed

Mally, Pooja; Czyz, Craig N; Chan, Norman J; Wulc, Allan E

2014-04-01

Vibration anesthesia is an effective pain-reduction technique for facial cosmetic injections. The analgesic effect of this method was tested in this study during facial dermal filler injections. The study aimed to evaluate the safety and efficacy of vibration anesthesia for these facial injections. This prospective study analyzed 41 patients who received dermal filler injections to the nasolabial folds, tear troughs, cheeks, and other facial sites. The injections were administered in a randomly assigned split-face design. One side of the patient's face received vibration together with dermal filler injections, whereas the other side received dermal filler injections alone. The patients completed a posttreatment questionnaire pertaining to injection pain, adverse effects, and preference for vibration with future dermal filler injections. The patients experienced both clinically and statistically significant pain reduction when a vibration stimulus was co-administered with the dermal filler injections. No adverse events were reported. The majority of the patients (95 %) reported a preference for vibration anesthesia with subsequent dermal filler injections. Vibration is a safe and effective method of achieving anesthesia during facial dermal filler injections. This journal requires that authors assign a level of evidence to each article. For a full description of these Evidence-Based Medicine ratings, please refer to the Table of Contents or the online Instructions to Authors www.springer.com/00266 .

Peroxotantalate-Based Ionic Liquid Catalyzed Epoxidation of Allylic Alcohols with Hydrogen Peroxide.

PubMed

Ma, Wenbao; Chen, Chen; Kong, Kang; Dong, Qifeng; Li, Kun; Yuan, Mingming; Li, Difan; Hou, Zhenshan

2017-05-29

The efficient and environmentally benign epoxidation of allylic alcohols has been attained by using new kinds of monomeric peroxotantalate anion-functionalized ionic liquids (ILs=[P 4,4,4,n ] 3 [Ta(O) 3 (η-O 2 )], P 4,4,4,n =quaternary phosphonium cation, n=4, 8, and 14), which have been developed and their structures determined accordingly. This work revealed the parent anions of the ILs underwent structural transformation in the presence of H 2 O 2 . The formed active species exhibited excellent catalytic activity, with a turnover frequency for [P 4,4,4,4 ] 3 [Ta(O) 3 (η-O 2 )] of up to 285 h -1 , and satisfactory recyclability in the epoxidation of various allylic alcohols under very mild conditions by using only one equivalent of hydrogen peroxide as an oxidant. NMR studies showed the reaction was facilitated through a hydrogen-bonding mechanism, in which the peroxo group (O-O) of the peroxotantalate anion served as the hydrogen-bond acceptor and hydroxyl group in the allylic alcohols served as the hydrogen-bond donor. This work demonstrates that simple monomeric peroxotantalates can catalyze epoxidation of allylic alcohols efficiently. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Morphology and phase control of iron oxide polymorph nanoparticles

NASA Astrophysics Data System (ADS)

Cui, Hongtao; Wang, Li; Shi, Min; Li, Yanhong

2017-04-01

In this work, lepidocrocite (γ-FeOOH) nanobundles were prepared by a facile NH4F assisted epoxide precipitation route. The reactions between epoxide and [Fe(H2O)6]2+ promoted the hydrolysis and condensation of [Fe(H2O)6]2+, resulting in the formation of iron oxyhydroxide. After calcination of γ-FeOOH nanobundles at 400 °C, the produced α-Fe2O3 still kept the bundle morphology. Due to the unique chemistry of epoxide, the morphology and phase of iron oxide polymorph nanoparticles (goethite, akaganeite, lepidocrocite, magnetite) were well-controlled through controlling reaction conditions such as Fe2+ concentration, NH4F additive and reaction temperature. It is particularly interesting that NH4F working as phase controlling agent is able to control the phase development of iron oxyhydroxides. This phase control effect of NH4F is attributed to the promoted reaction rate of epoxide originating from the higher electronegativity of fluoride ions than chloride ions. Based on the results in this work and our other preliminary works, it is considered that this route can be used as a general strategy for controlling the morphology and phase of transition element compounds.

Microstructure and Mechanical Properties of Stainless Steel/Brass Joints Brazed by Sn-Electroplated Ag Brazing Filler Metals

NASA Astrophysics Data System (ADS)

Wang, Xingxing; Peng, Jin; Cui, Datian

2018-05-01

To develop a high-Sn-content AgCuZnSn brazing filler metal, the BAg50CuZn was used as the base filler metal and a Sn layer was electroplated upon it. Then, the 304 stainless steel and the H62 brass were induction-brazed with the Sn-plated brazing filler metals. The microstructures of the joints were examined with an optical microscope, a scanning electron microscope and an x-ray diffractometer. The corresponding mechanical properties were obtained with a universal tensile testing machine. The results indicated that the induction brazed joints consisted of the Ag phase, the Cu phase and the CuZn phase. When the content of Sn in the Sn-plated Ag brazing filler metal was 6.0 or 7.2 wt.%, the Cu5Zn8, the Cu41Sn11 and the Ag3Sn phases appeared in the brazed joint. The tensile strength of the joints brazed with the Sn-plated filler metal was higher compared to the joints with the base filler metal. When the content of Sn was 6.0 wt.%, the highest tensile strength of the joint reached to 395 MPa. The joint fractures presented a brittle mode, mixed with a low amount of ductile fracture, when the content of Sn exceeded 6.0 wt.%.

The disfluent discourse: Effects of filled pauses on recall

PubMed Central

Fraundorf, Scott H.; Watson, Duane G.

2011-01-01

We investigated the mechanisms by which fillers, such as uh and um, affect memory for discourse. Participants listened to and attempted to recall recorded passages adapted from Alice’s Adventures in Wonderland. The type and location of interruptions were manipulated through digital splicing. In Experiment 1, we tested a processing time account of fillers’ effects. While fillers facilitated recall, coughs matched in duration to the fillers impaired recall, suggesting that fillers’ benefits cannot be attributed to adding processing time. In Experiment 2, fillers’ locations were manipulated based on norming data to be either predictive or non-predictive of upcoming material. Fillers facilitated recall in both cases, inconsistent with an account in which listeners predict upcoming material using past experience with the distribution of fillers. Instead, these results suggest an attentional orienting account in which fillers direct attention to the speech stream but do not always result in specific predictions about upcoming material. PMID:21765590

An unexpected epoxidation of benzil derivatives in their reaction with a germene.

PubMed

El Kettani, Sakina Ech-Cherif; Lazraq, Mohamed; Ouhsaine, Fatima; Gornitzka, Heinz; Ranaivonjatovo, Henri; Escudié, Jean

2008-11-07

The germene Mes(2)Ge=CR(2) (Mes = 2,4,6-trimethylphenyl, CR(2) = fluorenylidene) reacts with various benzil derivatives to lead to germanium-containing bicyclic epoxides by an unexpected new type of epoxidation reaction.

Di-epoxides of the three isomeric dicyclopenta-fused pyrenes: ultimate mutagenic active agents.

PubMed

Otero-Lobato, María José; Kaats-Richters, Veronica E M; Havenith, Remco W A; Jenneskens, Leonardus W; Seinen, Willem

2004-11-14

To rationalize the high bacterial mutagenic response recently found for the (di-) cyclopenta-fused pyrene congeners, viz. cyclopenta[cd]-(1), dicyclopenta[cd,mn]-(2), dicyclopenta[cd,fg]-(3) and dicyclopenta[cd,jk]pyrene (4), in the presence of a metabolic activation mixture (S9-mix), their (di-)epoxides at the externally fused unsaturated five-membered rings were previously proposed as the ultimate mutagenic active forms. In this study, cyclopenta[cd]pyrene-3,4-epoxide (5) and the novel dicyclopenta[cd,mn]pyrene-1,2,4,5-di-epoxide (6), dicyclopenta[cd,fg]pyrene-5,6,7,8-di-epoxide (7) and dicyclopenta[cd,jk]pyrene-1,2,6,7-di-epoxide (8) were synthesised from 1 to 4, respectively, and subsequently assayed for bacterial mutagenicity in the standard microsomal/histidine reverse mutation assay (Ames-assay with Salmonella typhimurium strain TA98). The di-epoxides 6-8 are present as a mixture of their cis- and trans-stereo-isomers in a close to 1:1 ratio ((1)H NMR spectroscopy and ab initio IGLO/III//RHF/6-31G** calculations). The direct-acting mutagenic activity and the strong cytotoxicity exerted by 5-8 both in the absence or presence of an exogenous metabolic activation system (+/-S9-mix) demonstrate that the ultimate mutagenic active forms are the proposed (di-)epoxides of 1-4.

Construction and photophysical properties of organic-inorganic nanonetworks based on oligo(phenylenevinylene) and functionalized gold nanoparticles.

PubMed

Yang, Jien; Liu, Xiaofeng; Huang, Changshui; Zhou, Chunjie; Li, Yuliang; Zhu, Daoben

2010-02-22

Novel organic-inorganic nanonetworks of oligo(phenylenevinylene) (OPV) and gold nanoparticles (GNPs) have been synthesized by the amine-based epoxide ring-opening reaction. The resulting OPV-GNPs nanocomposites exhibit homogeneous and well-defined interfaces between the organic ligands and the inorganic nanoparticles, thereby promoting efficient electronic interfacial interaction between the two constituents. The functionalized gold nanoparticles serve as chemical reagents for the construction of nanohybrids, while the epoxide-terminated OPV acts as linkage between gold nanoparticles. The new architecture provides a facile methodology for fabrication of novel organic-inorganic nanohybrids under relatively mild conditions, which facilitates further applications of hybrid materials.

Complex Cure Kinetics of the Tertiary Amine activated Reaction in DGEBA Epoxy Hardened with Diethanolamine

NASA Astrophysics Data System (ADS)

Ancipink, Windy; McCoy, John; Clarkson, Caitlyn; Kropka, Jamie; Celina, Mathias; Giron, Nicholas; Hailesilassie, Lebelo; Fredj, Narjes

The curing of a diglycidyl ether of bisphenol-A (DGEBA) epoxy with diethanolamine (DEA) involves a well understood fast amine-epoxide reaction followed by a more complicated slower hydroxyl-epoxide reaction. The time scale of these two reactions are well separated and can be studied independently from one another. The initial amine-epoxide reaction results in a tertiary amine adduct which is a product of the direct reaction of a secondary amine from the DEA reacting with a single DGEBA epoxide. The second hydroxyl-epoxide reaction results in a highly crosslinked glassy epoxy resin. The deviation in the mechanisms between high and low temperatures are discerned through the use of differential scanning calorimetry (DSC), infrared spectroscopy (IR), and isothermal microcalorimetry (IMC) data. Observations of reaction rates at temperatures ranging from 30° C to 110° C have led to the determination that the hydroxyl-epoxide reaction is temperature sensitive. The hydroxyl-epoxide reaction occurs through two different mechanisms: at low temperatures, the reaction is catalyzed by the tertiary amine adduct; at higher temperatures, the reaction does not appear to be catalyzed. Sandia National Laboratories, Albuquerque, NM.

Crosslinked hyaluronic acid dermal fillers: a comparison of rheological properties.

PubMed

Falcone, Samuel J; Berg, Richard A

2008-10-01

Temporary dermal fillers composed of crosslinked hyaluronic acid (XLHA) are space filling gels that are readily available in the United States and Europe. Several families of dermal fillers based on XLHA are now available and here we compare the physical and rheological properties of these fillers to the clinical effectiveness. The XLHA fillers are prepared with different crosslinkers, using HA isolated from different sources, have different particle sizes, and differ substantially in rheological properties. For these fillers, the magnitude of the complex viscosity, |eta*|, varies by a factor of 20, the magnitude of the complex rigidity modulus, |G*|, and the magnitude of the complex compliance, |J*| vary by a factor of 10, the percent elasticity varies from 58% to 89.9%, and the tan delta varies from 0.11 to 0.70. The available clinical data cannot be correlated with either the oscillatory dynamic or steady flow rotational rheological properties of the various fillers. However, the clinical data appear to correlate strongly with the total concentration of XLHA in the products and to a lesser extent with percent elasticity. Hence, our data suggest the following correlation: dermal filler persistence = [polymer] x [% elasticity] and the clinical persistence of a dermal filler composed of XLHA is dominated by the mass and elasticity of the material implanted. This work predicts that the development of future XLHA dermal filler formulations should focus on increasing the polymer concentration and elasticity to improve the clinical persistence.

Effect of mechanical properties of fillers on the grindability of composite resin adhesives.

PubMed

Iijima, Masahiro; Muguruma, Takeshi; Brantley, William A; Yuasa, Toshihiro; Uechi, Jun; Mizoguchi, Itaru

2010-10-01

The purpose of this study was to investigate the effect of filler properties on the grindability of composite resin adhesives. Six composite resin products were selected: Transbond XT (3M Unitek, Monrovia, Calif), Transbond Plus (3M Unitek), Enlight (Ormco, Glendora, Calif), Kurasper F (Kuraray Medical, Tokyo, Japan), Beauty Ortho Bond (Shofu, Kyoto, Japan), and Beauty Ortho Bond Salivatect (Shofu). Compositions and weight fractions of fillers were determined by x-ray fluorescence analysis and ash test, respectively. The polished surface of each resin specimen was examined with a scanning electron microscope. Vickers hardness of plate specimens (15 × 10 × 3 mm) was measured, and nano-indentation was performed on large filler particles (>10 μm). Grindability for a low-speed tungsten-carbide bur was estimated. Data were compared with anlaysis of variance (ANOVA) and the Tukey multiple range test. Relationships among grindability, filler content, filler nano-indentation hardness (nano-hardness), filler elastic modulus, and Vickers hardness of the composite resins were investigated with the Pearson correlation coefficient test. Morphology and filler size of these adhesives showed great variations. The products could be divided into 2 groups, based on composition, which affected grindability. Vickers hardness of the adhesives did not correlate (r = 0.140) with filler nano-hardness, which showed a significant negative correlation (r = -0.664) with grindability. Filler nano-hardness greatly influences the grindability of composite resin adhesives. Copyright © 2010 American Association of Orthodontists. Published by Mosby, Inc. All rights reserved.

Irreversible covalent modification of type I dehydroquinase with a stable Schiff base.

PubMed

Tizón, Lorena; Maneiro, María; Peón, Antonio; Otero, José M; Lence, Emilio; Poza, Sergio; van Raaij, Mark J; Thompson, Paul; Hawkins, Alastair R; González-Bello, Concepción

2015-01-21

The irreversible inhibition of type I dehydroquinase (DHQ1), the third enzyme of the shikimic acid pathway, is investigated by structural, biochemical and computational studies. Two epoxides, which are mimetics of the natural substrate, were designed as irreversible inhibitors of the DHQ1 enzyme and to study the binding requirements of the linkage to the enzyme. The epoxide with the S configuration caused the covalent modification of the protein whereas no reaction was obtained with its epimer. The first crystal structure of DHQ1 from Salmonella typhi covalently modified by the S epoxide, which is reported at 1.4 Å, revealed that the modified ligand is surprisingly covalently attached to the essential Lys170 by the formation of a stable Schiff base. The experimental and molecular dynamics simulation studies reported here highlight the huge importance of the conformation of the C3 carbon of the ligand for covalent linkage to this type of aldolase I enzyme, revealed the key role played by the essential His143 as a Lewis acid in this process and show the need for a neatly closed active site for catalysis.

Epoxidation of Alpha-Methylstyrene and its Lewis Acid Rearrangement to 2-Phenylpropanal

NASA Astrophysics Data System (ADS)

Garin, David L.; Gamber, Melissa; Rowe, Bradley J.

1996-06-01

This undergraduate organic lab experiment includes procedures for the peracid epoxidation of an olefin and the Lewis acid rearrangement of an epoxide to a carbonyl compound. Product mixtures and transformations can be readily analyzed by several spectroscopic techniques.

Mechanism of olefin epoxidation in the presence of a titanium-containing zeolite

NASA Astrophysics Data System (ADS)

Danov, S. M.; Krasnov, V. L.; Sulimov, A. V.; Ovcharova, A. V.

2013-11-01

The effect of the nature of a solvent on the liquid-phase epoxidation of olefins with an aqueous solution of hydrogen peroxide over a titanium-containing zeolite is studied. Butanol-1, butanol-2, propanol-1, isopropanol, methanol, ethanol, water, acetone, methyl ethyl ketone, isobutanol, and tert-butanol are examined as solvents. A mechanism of olefin epoxidation with hydrogen peroxide in an alcohol medium over a titanium-containing zeolite is proposed. Epoxidation reactions involving hydrogen peroxide and different olefins are studied experimentally.

Na@SiO2-Mediated Addition of Organohalides to Carbonyl Compounds for the Formation of Alcohols and Epoxides

NASA Astrophysics Data System (ADS)

Kapoor, Mohit; Hwu, Jih Ru

2016-11-01

Alcohols and epoxides were generated by the addition of organohalides to carbonyl compounds in the presence of sodium metal impregnated with silica gel (Na@SiO2) in THF at 25 °C through a radical pathway. Under the same conditions, Schiff bases were also successfully converted to the corresponding amines. Furthermore, the reaction of aldehydes with α-haloesters or 4-(chloromethyl)-coumarin with the aid of Na@SiO2 generated trans epoxides. An unprecedented mechanism is proposed for their formation. The advantages associated with these new reactions include: (1) products are obtained in good-to-excellent yields, (2) reactions are completed at room temperatures in a short period of time (<2.0 h), (3) it is unnecessary to perform the reactions under anhydrous conditions, and (4) the entire process requires only simple manipulations.

Exciton characteristics in graphene epoxide.

PubMed

Zhu, Xi; Su, Haibin

2014-02-25

Exciton characteristics in graphene epoxide (GE) are investigated by density functional theory with quasi-particle corrections and many-body interactions. The nature of the exciton is influenced by epoxide content and detailed geometric configurations. Two kinds of excitons are identified in GE: Frenkel-like exciton originated from the sp(2) carbon cluster and charge-transfer exciton formed by localized states involving both oxygen and carbon atoms. The unusual blue shift associated with the Frenkel-like exciton leaking is highlighted. One scaling relationship is proposed to address the power-law dependence of Frenkel-like exciton binding strength on its size. The charge-transfer exciton appears in GE samples with the high oxygen coverage. Particularly, the exciton in GE structures exhibits long lifetime by analyzing both radiative and nonradiative decay processes. This study sheds light on the potential applications of GE-based structures with attractive high quantum yield in light emission and optoelectronic technology.

Simulation of Zr content in TiZrCuNi brazing filler metal for Ti6Al4V alloy

NASA Astrophysics Data System (ADS)

Yue, Xishan; Xie, Zonghong; Jing, Yongjuan

2017-07-01

To optimize the Zr content in Ti-based filler metal, the covalent electron on the nearest atoms bond in unit cell ( n A u-v ) with Ti-based BCC structure was calculated, in which the brazing temperature was considered due to its influence on the lattice parameter. Based on EET theory (The Empirical Electron Theory for solid and molecules), n_{{A}}^{{u - v}} represents the strength of the unit cell with defined element composition and structure, which reflects the effect from solid solution strengthening on the strength of the unit cell. For Ti-Zr-15Cu-10Ni wt% filler metal, it kept constant as 0.3476 with Zr as 37.5˜45 wt% and decreased to 0.333 with Zr decreasing from 37.5 to 25 wt%. Finally, it increased up to 0.3406 with Zr as 2˜10 wt%. Thus, Ti-based filler metal with Zr content being 2˜10 wt% is suggested based on the simulation results. Moreover, the calculated covalent electron of n A u-v showed good agreement with the hardness of the joint by filler 37.5Zr and 10Zr. The composition of Ti-10Zr-15Cu-10Ni wt% was verified in this study with higher tensile strength of the brazing joint and uniform microstructure of the interface.

Vibrational Excitations and Low Energy Electronic Structure of Epoxide-decorated Graphene.

PubMed

Mattson, E C; Johns, J E; Pande, K; Bosch, R A; Cui, S; Gajdardziska-Josifovska, M; Weinert, M; Chen, J H; Hersam, M C; Hirschmugl, C J

2014-01-02

We report infrared studies of adsorbed atomic oxygen (epoxide functional groups) on graphene. Two different systems are used as a platform to explore these interactions, namely, epitaxial graphene/SiC(0001) functionalized with atomic oxygen (graphene epoxide, GE) and chemically reduced graphene oxide (RGO). In the case of the model GE system, IR reflectivity measurements show that epoxide groups distort the graphene π bands around the K-point, imparting a finite effective mass and contributing to a band gap. In the case of RGO, epoxide groups are found to be present following the reduction treatment by a combination of polarized IR reflectance and transmittance measurements. Similar to the GE system, a band gap in the RGO sample is observed as well.

Vibrational Excitations and Low Energy Electronic Structure of Epoxide-decorated Graphene

PubMed Central

Mattson, E.C.; Johns, J.E.; Pande, K.; Bosch, R.A.; Cui, S.; Gajdardziska-Josifovska, M.; Weinert, M.; Chen, J.H.; Hersam, M.C.; Hirschmugl, C.J.

2014-01-01

We report infrared studies of adsorbed atomic oxygen (epoxide functional groups) on graphene. Two different systems are used as a platform to explore these interactions, namely, epitaxial graphene/SiC(0001) functionalized with atomic oxygen (graphene epoxide, GE) and chemically reduced graphene oxide (RGO). In the case of the model GE system, IR reflectivity measurements show that epoxide groups distort the graphene π bands around the K-point, imparting a finite effective mass and contributing to a band gap. In the case of RGO, epoxide groups are found to be present following the reduction treatment by a combination of polarized IR reflectance and transmittance measurements. Similar to the GE system, a band gap in the RGO sample is observed as well. PMID:24563725

Enantioselective epoxidation with chiral MN(III)(salen) catalysts: kinetic resolution of aryl-substituted allylic alcohols.

PubMed

Adam, W; Humpf, H U; Roschmann, K J; Saha-Möller, C R

2001-08-24

A set of aryl-substituted allylic alcohols rac-2 has been epoxidized by chiral Mn(salen*) complexes 1 as the catalyst and iodosyl benzene (PhIO) as the oxygen source. Whereas one enantiomer of the allylic alcohol 2 is preferentially epoxidized to give the threo- or cis-epoxy alcohol 3 (up to 80% ee) as the main product (dr up to >95:5), the other enantiomer of 2 is enriched (up to 53% ee). In the case of 1,1-dimethyl-1,2-dihydronaphthalen-2-ol (2c), the CH oxidation to the enone 4c proceeds enantioselectively and competes with the epoxidation. The absolute configurations of the allylic alcohols 2 and their epoxides 3 have been determined by chemical correlation or CD spectroscopy. The observed diastereo- and enantioselectivities in the epoxidation reactions are rationalized in terms of a beneficial interplay between the hydroxy-directing effect and the attack along the Katsuki trajectory.

Thermoset coatings from epoxidized sucrose soyate and blocked, bio-based dicarboxylic acids.

PubMed

Kovash, Curtiss S; Pavlacky, Erin; Selvakumar, Sermadurai; Sibi, Mukund P; Webster, Dean C

2014-08-01

A new 100% bio-based thermosetting coating system was developed from epoxidized sucrose soyate crosslinked with blocked bio-based dicarboxylic acids. A solvent-free, green method was used to block the carboxylic acid groups and render the acids miscible with the epoxy resin. The thermal reversibility of this blocking allowed for the formulation of epoxy-acid thermoset coatings that are 100% bio-based. This was possible due to the volatility of the vinyl ethers under curing conditions. These systems have good adhesion to metal substrates and perform well under chemical and physical stress. Additionally, the hardness of the coating system is dependent on the chain length of the diacid used, making it tunable. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Polyisoprenoid epoxides stimulate the biosynthesis of coenzyme Q and inhibit cholesterol synthesis.

PubMed

Bentinger, Magnus; Tekle, Michael; Brismar, Kerstin; Chojnacki, Tadeusz; Swiezewska, Ewa; Dallner, Gustav

2008-05-23

In our search for compounds that up-regulate the biosynthesis of coenzyme Q (CoQ), we discovered that irradiation of CoQ with ultraviolet light results in the formation of a number of compounds that influence the synthesis of mevalonate pathway lipids by HepG2 cells. Among the compounds that potently stimulated CoQ synthesis while inhibiting cholesterol synthesis, derivatives of CoQ containing 1-4 epoxide moieties in their polyisoprenoid side chains were identified. Subsequently, chemical epoxidation of all-trans-polyprenols of different lengths revealed that the shorter farnesol and geranylgeraniol derivatives were without effect, whereas the longer derivatives of solanesol enhanced CoQ and markedly reduced cholesterol biosynthesis. In contrast, none of the modified trans-trans-poly-cis-polyprenols exerted noticeable effects. Tocotrienol epoxides were especially potent in our system; those with one epoxide moiety in the side-chain generally up-regulated CoQ biosynthesis by 200-300%, whereas those with two such moieties also decreased cholesterol synthesis by 50-90%. Prolonged treatment of HepG2 cells with tocotrienol epoxides for 26 days elevated their content of CoQ by 30%. In addition, the levels of mRNA encoding enzymes involved in CoQ biosynthesis were also elevated by the tocotrienol epoxides. The site of inhibition of cholesterol synthesis was shown to be oxidosqualene cyclase. In conclusion, epoxide derivatives of certain all-trans-polyisoprenoids cause pronounced stimulation of CoQ synthesis and, in some cases, simultaneous reduction of cholesterol biosynthesis by HepG2 cells.

Cellulose whisker/epoxy resin nanocomposites.

PubMed

Tang, Liming; Weder, Christoph

2010-04-01

New nanocomposites composed of cellulose nanofibers or "whiskers" and an epoxy resin were prepared. Cellulose whiskers with aspect ratios of approximately 10 and approximately 84 were isolated from cotton and sea animals called tunicates, respectively. Suspensions of these whiskers in dimethylformamide were combined with an oligomeric difunctional diglycidyl ether of bisphenol A with an epoxide equivalent weight of 185-192 and a diethyl toluenediamine-based curing agent. Thin films were produced by casting these mixtures and subsequent curing. The whisker content was systematically varied between 4 and 24% v/v. Electron microscopy studies suggest that the whiskers are evenly dispersed within the epoxy matrix. Dynamic mechanical thermoanalysis revealed that the glass transition temperature (T(g)) of the materials was not significantly influenced by the incorporation of the cellulose filler. Between room temperature and 150 degrees C, i.e., below T(g), the tensile storage moduli (E') of the nanocomposites increased modestly, for example from 1.6 GPa for the neat polymer to 4.9 and 3.6 GPa for nanocomposites comprising 16% v/v tunicate or cotton whiskers. The relative reinforcement was more significant at 185 degrees C (i.e., above T(g)), where E' was increased from approximately 16 MPa (neat polymer) to approximately 1.6 GPa (tunicate) or approximately 215 MPa (cotton). The mechanical properties of the new materials are well-described by the percolation model and are the result of the formation of a percolating whisker network in which stress transfer is facilitated by strong interactions between the whiskers.

Organocatalyzed enantioselective desymmetrization of aziridines and epoxides

PubMed Central

2013-01-01

Summary Enantioselective desymmetrization of meso-aziridines and meso-epoxides with various nucleophiles by organocatalysis has emerged as a cutting-edge approach in recent years. This review summarizes the origin and recent developments of enantioselective desymmetrization of meso-aziridines and meso-epoxides in the presence of organocatalysts. PMID:24062828

A Sensitive Gel-based Method Combining Distinct Cyclophellitol-based Probes for the Identification of Acid/Base Residues in Human Retaining β-Glucosidases*

PubMed Central

Kallemeijn, Wouter W.; Witte, Martin D.; Voorn-Brouwer, Tineke M.; Walvoort, Marthe T. C.; Li, Kah-Yee; Codée, Jeroen D. C.; van der Marel, Gijsbert A.; Boot, Rolf G.; Overkleeft, Herman S.; Aerts, Johannes M. F. G.

2014-01-01

Retaining β-exoglucosidases operate by a mechanism in which the key amino acids driving the glycosidic bond hydrolysis act as catalytic acid/base and nucleophile. Recently we designed two distinct classes of fluorescent cyclophellitol-type activity-based probes (ABPs) that exploit this mechanism to covalently modify the nucleophile of retaining β-glucosidases. Whereas β-epoxide ABPs require a protonated acid/base for irreversible inhibition of retaining β-glucosidases, β-aziridine ABPs do not. Here we describe a novel sensitive method to identify both catalytic residues of retaining β-glucosidases by the combined use of cyclophellitol β-epoxide- and β-aziridine ABPs. In this approach putative catalytic residues are first substituted to noncarboxylic amino acids such as glycine or glutamine through site-directed mutagenesis. Next, the acid/base and nucleophile can be identified via classical sodium azide-mediated rescue of mutants thereof. Selective labeling with fluorescent β-aziridine but not β-epoxide ABPs identifies the acid/base residue in mutagenized enzyme, as only the β-aziridine ABP can bind in its absence. The Absence of the nucleophile abolishes any ABP labeling. We validated the method by using the retaining β-glucosidase GBA (CAZy glycosylhydrolase family GH30) and then applied it to non-homologous (putative) retaining β-glucosidases categorized in GH1 and GH116: GBA2, GBA3, and LPH. The described method is highly sensitive, requiring only femtomoles (nanograms) of ABP-labeled enzymes. PMID:25344605

Use of Almond Shells and Rice Husk as Fillers of Poly(Methyl Methacrylate) (PMMA) Composites.

PubMed

Sabbatini, Alessandra; Lanari, Silvia; Santulli, Carlo; Pettinari, Claudio

2017-07-28

In recent years, wood fibres have often been applied as the reinforcement of thermoplastic materials, such as polypropylene, whereas their use in combination with thermosetting resin has been less widespread. This study concerns the production of PMMA-based composites by partly replacing alumina trihydrate (ATH) with wood waste fillers, namely rice husks and almond shells, which would otherwise be disposed by incineration. The amount of filler introduced was limited to 10% as regards rice husks and 10 or 15% almond shells, since indications provided by reactivity tests and viscosity measurements did not suggest the feasibility of total replacement of ATH. As a matter of fact, the introduction of these contents of wood waste filler in PMMA-based composite did not result in any significant deterioration of its mechanical properties (Charpy impact, Rockwell M hardness and flexural performance). Some reduction of these properties was only observed in the case of introduction of 15% almond shells. A further issue concerned the yellowing of the organic filler under exposure to UV light. On the other hand, a very limited amount of water was absorbed, never exceeding values around 0.6%, despite the significant porosity revealed by the filler's microscopic evaluation. These results are particularly interesting in view of the application envisaged for these composites, i.e., wood replacement boards.

Study of piezoelectric filler on the properties of PZT-PVDF composites

NASA Astrophysics Data System (ADS)

Matei, Alina; Å¢ucureanu, Vasilica; Vlǎzan, Paulina; Cernica, Ileana; Popescu, Marian; RomaniÅ£an, Cosmin

2017-12-01

The ability to obtain composites with desired functionalities is based on advanced knowledge of the processes synthesis and of the structure of piezoceramic materials, as well the incorporation of different fillers in selected polymer matrix. Polyvinylidene fluoride (PVDF) is a fluorinated polymer with excellent mechanical and electric properties, which it was chosen as matrix due to their applications in a wide range of industrial fields [1-4]. The present paper focuses on the development of composites based on PZT particles as filler obtained by conventional methods and PVDF as polymer matrix. The synthesis of PVDF-PZT composites was obtained by dispersing the ceramic powders in a solution of PVDF in N-methyl-pyrrolidone (NMP) under mechanical mixing and ultrasonication, until a homogenous mixture is obtained. The properties of the piezoceramic fillers before and after embedding into the polymeric matrix were investigated by Fourier transform infrared spectrometry, field emission scanning electron microscopy and X-ray diffraction. In the FTIR spectra, appear a large number of absorption bands which are exclusive of the phases from PVDF matrix confirming the total embedding of PZT filler into matrix. Also, the XRD pattern of the composites has confirmed the presence of crystalline phases of PVDF and the ceramic phase of PZT. The SEM results showed a good distribution of fillers in the matrix.

Composite Solid Electrolyte Containing Li+- Conducting Fibers

NASA Technical Reports Server (NTRS)

Appleby, A. John; Wang, Chunsheng; Zhang, Xiangwu

2006-01-01

Improved composite solid polymer electrolytes (CSPEs) are being developed for use in lithium-ion power cells. The matrix components of these composites, like those of some prior CSPEs, are high-molecular-weight dielectric polymers [generally based on polyethylene oxide (PEO)]. The filler components of these composites are continuous, highly-Li(+)-conductive, inorganic fibers. PEO-based polymers alone would be suitable for use as solid electrolytes, were it not for the fact that their room-temperature Li(+)-ion conductivities lie in the range between 10(exp -6) and 10(exp -8) S/cm, too low for practical applications. In a prior approach to formulating a CSPE, one utilizes nonconductive nanoscale inorganic filler particles to increase the interfacial stability of the conductive phase. The filler particles also trap some electrolyte impurities. The achievable increase in conductivity is limited by the nonconductive nature of the filler particles.

The improvement of the mechanical properties of PMMA denture base by Al2O3 particles with nitrile rubber

NASA Astrophysics Data System (ADS)

Alhareb, Ahmed Omran; Akil, Hazizan Md; Ahmad, Zainal Arifin

2017-07-01

Poly methyl methacrylate (PMMA) is mostly used for fabrication of denture base by heat-curing technique. Therefore, the purpose of this study is to investigate the effect of Al2O3 filler as toughening particles together with nitrile butadiene rubber (NBR) particles as impact modifier were used to reinforce PMMA denture base materials on the impact strength (IS) and fracture toughness (KIC). PMMA powder was mixed with liquid methyl methacrylate (MMA) and ethylene glycol dimethacrylate (EGDMA) as crosslinking agent. The powder components are PMMA, benzoyl peroxide, NBR (5, 7.5 and 10 wt%), and Al2O3 filler (5 wt%) treated by silane. The liquid components are 90% of methyl methacrylate and 10 % ethylene glycol dimethacryate. FTIR analyses confirmed that the Al2O3 filler was successfully treated with silane as coupling agent. The morphology of fracture surfaces was characterized using field emission scanning electron microscopy (FESEM). The results shown that IS and KIC improved significantly when using treated the Al2O3 filler. IS has increased to 56% (8.26 KJ/m2) and 73% (2.77 MPa.m1/2) for KIC when treated Al2O3 filler compared to unreinforced PMMA matrix. Statistical analyses of data results were significantly improved (P<0.05) when using 7.5 wt% NBR with treated Al2O3 filler compared to other the compositions.

Filler characteristics of modern dental resin composites and their influence on physico-mechanical properties.

PubMed

Randolph, Luc D; Palin, William M; Leloup, Gaëtane; Leprince, Julian G

2016-12-01

The mechanical properties of dental resin-based composites (RBCs) are highly dependent on filler characteristics (size, content, geometry, composition). Most current commercial materials are marketed as "nanohybrids" (i.e. filler size <1μm). In the present study, filler characteristics of a selection of RBCs were described, aiming at identifying correlations with physico-mechanical properties and testing the relevance of the current classification. Micron/sub-micron particles (> or <500nm) were isolated from 17 commercial RBCs and analyzed by laser diffractrometry and/or electron microscopy. Filler and silane content were evaluated by thermogravimetric analysis and a sedimentation technique. The flexural modulus (E flex ) and strength (σ flex ) and micro-hardness were determined by three-point bending or with a Vickers indenter, respectively. Sorption was also determined. All experiments were carried out after one week of incubation in water or 75/25 ethanol/water. Average size for micron-sized fillers was almost always higher than 1μm. Ranges for mechanical properties were: 3.775wt%) were associated with the highest mechanical properties (E flex and σ flex >12GPa and 130MPa, respectively) and lowest solvent sorption (∼0.3%). Mechanical properties and filler characteristics significantly vary among modern RBCs and the current classification does not accurately illustrate either. Further, the chemical stability of RBCs differed, highlighting differences in resin and silane composition. Since E flex and sorption were well correlated to the filler content, a simple and unambiguous classification based on such characteristic is suggested, with three levels (ultra-low fill, low-fill and compact resin composites). Copyright © 2016 The Academy of Dental Materials. All rights reserved.

Degradation kinetics of ethylene-octene copolymer/wood flour biocomposites in dependence to filler content

NASA Astrophysics Data System (ADS)

Zykova, A. K.; Pantyukhov, P. V.; Monakhova, T. V.; Popov, A. A.

2017-06-01

This article is focused on thermal oxidative degradation and biodegradation in soil of biocomposites based on ethylene-octene copolymer (EOC), filled by wood flour (from 30 to 70% wt.), in dependence to the filler content. The study of oxidative degradation of composites was carried out at two temperatures (80 and 130°C respectively). The induction period and the rates of oxidation were determined. It was concluded that as filler content raises, the induction period increases. It can be explained by the higher specific area of composites in comparison with pure EOC. However, high filled composites (60 and 70 % of the filler) are oxidized with a huge induction period because polyphenols in the filler inhibit the oxidation process. Biodegradation test under laboratory conditions was carried out to investigate the biodegradability of the material. Composites with lower filler content have lower weight loss rate. Small particles are capsulated by polymer and are isolated from moisture and microorganisms. On the other hand, at a high filling of the composite small particles stick together and act as large ones. Such filler agglomerates are connected with each other and allow microorganisms to penetrate into the composite. It was concluded as filler content raises the mass loss increases.

Hybrid networks based on epoxidized camelina oil

PubMed Central

Balanuca, Brindusa; Stan, Raluca; Lungu, Adriana; Vasile, Eugeniu; Iovu, Horia

2017-01-01

Abstract Lately, renewable resources received great attention in the macromolecular compounds area, regarding the design of the monomers and polymers with different applications. In this study the capacity of several modified vegetable oil-based monomers to build competitive hybrid networks was investigate, taking into account thermal and mechanical behavior of the designed materials. In order to synthesize such competitive nanocomposites, the selected renewable raw material, camelina oil, was employed due to the non-toxicity and biodegradability behavior. General properties of epoxidized camelina oil-based materials were improved by loading of different types of organic-inorganic hybrid compounds – polyhedral oligomeric silsesquioxane (POSS) bearing one (POSS1Ep) or eight (POSS8Ep) epoxy rings on the cages. In order to identify the chemical changes occurring after the thermal curing reactions, FT-IR spectrometry was employed. The new synthesized nanocomposites based on epoxidized camelina oil (ECO) were characterized by dynamic mechanical analyze and thermogravimetric analyze. The morphology of the ECO-based materials was investigate by scanning electron microscopy and supplementary information regarding the presence of the POSS compounds were establish by energy dispersive X-ray analysis and X-ray photoelectron spectroscopy. The smooth materials without any separation phase indicates a well dispersion of the Si–O–Si cages within the organic matrix and the incorporation of this hybrid compounds into the ECO network demonstrates to be a well strategy to improve the thermal and mechanical properties, simultaneously. PMID:29491775

Ring opening of epoxides with C-nucleophiles.

PubMed

Faiz, Sadia; Zahoor, Ameer Fawad

2016-11-01

Ring opening of epoxides has been an area of interest for organic chemists, owing to their reactivity toward nucleophiles. Such reactions yield important products depending on the type of nucleophiles used. This review article covers the synthetic approaches (1991-2015) used for the ring opening of epoxides via carbon nucleophiles.

Cross-linguistic evidence for memory storage costs in filler-gap dependencies with wh-adjuncts

PubMed Central

Stepanov, Arthur; Stateva, Penka

2015-01-01

This study investigates processing of interrogative filler-gap dependencies in which the filler integration site or gap is not directly subcategorized by the verb. This is the case when the wh-filler is a structural adjunct such as how or when rather than subject or object. Two self-paced reading experiments in English and Slovenian provide converging cross-linguistic evidence that wh-adjuncts elicit a kind of memory storage cost similar to that previously shown in the literature for wh-arguments. Experiment 1 investigates the storage costs elicited by the adjunct when in Slovenian, and Experiment 2 the storage costs elicited by how quickly and why in English. The results support the class of theories of storage costs based on the metric in terms of incomplete phrase structure rules or incomplete syntactic head predictions. We also demonstrate that the endpoint of the storage cost for a wh-adjunct filler provides valuable processing evidence for its base structural position, the identification of which remains a rather murky issue in current grammatical research. PMID:26388806

Epoxidation catalyst and process

DOEpatents

Linic, Suljo; Christopher, Phillip

2010-10-26

Disclosed herein is a catalytic method of converting alkenes to epoxides. This method generally includes reacting alkenes with oxygen in the presence of a specific silver catalyst under conditions suitable to produce a yield of the epoxides. The specific silver catalyst is a silver nanocrystal having a plurality of surface planes, a substantial portion of which is defined by Miller indices of (100). The reaction is performed by charging a suitable reactor with this silver catalyst and then feeding the reactants to the reactor under conditions to carry out the reaction. The reaction may be performed in batch, or as a continuous process that employs a recycle of any unreacted alkenes. The specific silver catalyst has unexpectedly high selectivity for epoxide products. Consequently, this general method (and its various embodiments) will result in extraordinarily high epoxide yields heretofore unattainable.

Enzymatic catalysis of anti-Baldwin ring closure in polyether biosynthesis.

PubMed

Hotta, Kinya; Chen, Xi; Paton, Robert S; Minami, Atsushi; Li, Hao; Swaminathan, Kunchithapadam; Mathews, Irimpan I; Watanabe, Kenji; Oikawa, Hideaki; Houk, Kendall N; Kim, Chu-Young

2012-03-04

Polycyclic polyether natural products have fascinated chemists and biologists alike owing to their useful biological activity, highly complex structure and intriguing biosynthetic mechanisms. Following the original proposal for the polyepoxide origin of lasalocid and isolasalocid and the experimental determination of the origins of the oxygen and carbon atoms of both lasalocid and monensin, a unified stereochemical model for the biosynthesis of polyether ionophore antibiotics was proposed. The model was based on a cascade of nucleophilic ring closures of postulated polyepoxide substrates generated by stereospecific oxidation of all-trans polyene polyketide intermediates. Shortly thereafter, a related model was proposed for the biogenesis of marine ladder toxins, involving a series of nominally disfavoured anti-Baldwin, endo-tet epoxide-ring-opening reactions. Recently, we identified Lsd19 from the Streptomyces lasaliensis gene cluster as the epoxide hydrolase responsible for the epoxide-opening cyclization of bisepoxyprelasalocid A to form lasalocid A. Here we report the X-ray crystal structure of Lsd19 in complex with its substrate and product analogue to provide the first atomic structure-to our knowledge-of a natural enzyme capable of catalysing the disfavoured epoxide-opening cyclic ether formation. On the basis of our structural and computational studies, we propose a general mechanism for the enzymatic catalysis of polyether natural product biosynthesis. © 2012 Macmillan Publishers Limited. All rights reserved

Industrially relevant epoxy-acrylate hybrid resin photopolymerizations

NASA Astrophysics Data System (ADS)

Ajiboye, Gbenga I.

Photopolymerization of epoxy-acrylate hybrid resins takes advantages of inherent properties present in the free-radical and cationic reactions to reduce oxygen inhibition problems that plague free-radical reactions. Similarly, the combined reaction mechanisms reduce moisture sensitivity of the cationic reactions. Despite the advantages of epoxy-acrylate hybrid resins, problems persist that need to be addressed. For example, low conversion and polymerization rate of the epoxides are a problem, because the fast acrylate conversion prevents the epoxide from reaching high conversion. Controlling phase separation is challenging, since two moieties with different properties are reacting. The physical properties of the polymer will be impacted by the availability of different moieties. High shrinkage stress results from the acrylate moiety, causing buckling and cracking in film and coating applications. The overall goal of this study is to use the fundamental knowledge of epoxy-acrylate hybrid resins to formulate industrially viable polymers. In order to achieve this goal, the study focuses on the following objectives: (I) determine the apparent activation energy of the hybrid monomer METHB, (II) increase epoxide conversion and polymerization rate of hybrid formulations, and (III) control physical properties in epoxy-acrylate hybrid resins. In order to increase the epoxide conversion and rate of polymerization, the sensitivity of epoxides to alcohol is used to facilitate the activated monomer (AM) mechanism and induce a covalent bond between the epoxide and acrylate polymers through the hydroxyl group. It is hypothesized that if the AM mechanism is facilitated, epoxide conversion will increase. As a result, the resins can be tailored to control phase separation and physical properties, and shrinkage stress can be reduced. In pursuit of these objectives, the hybrid monomer METHB was polymerized at temperatures ranging from 30°C to 70°C to obtain apparent activation energy of 23.49 kJ/mol for acrylate and 57 kJ/mol for epoxide moeities. Then, hybrid systems pairing hydroxyl-containing acrylates with epoxides were formulated to promote the faster AM mechanism. Monomer composition was changed in the presence of hydroxyl-containing acrylate, and initiators were carefully selected in order to control phase separation. The conversion of acrylate and epoxide was monitored in real time by Raman spectroscopy. The physical and mechanical properties were monitored using dynamic mechanical analysis. Epoxide conversion and rate of polymerization in epoxide-acrylate hybrid monomer systems were shown to increase through the introduction of a hydroxyl group on the meth/acrylate monomer, taking advantage of the faster AM mechanism. In addition, this covalent bond linking the epoxide network to the meth/acrylate polymer chains resulted in little or no phase separation and a reduction of the Tg for the hybrid polymer compared to the neat epoxide. Fundamental knowledge gained from this research will enable the use of epoxy-acrylate hybrid resins in variety of applications. For instance, shrinkage may be reduced in dental fillings, noise and vibration problems in aircraft and other machinery may be controlled, and photopolymerization cost could be reduced in thin film applications.

Characterization of electron-beam-modified surface coated clay fillers and their influence on physical properties of rubbers

NASA Astrophysics Data System (ADS)

Ray, Sudip; Bhowmick, Anil K.; Sarma, K. S. S.; Majali, A. B.; Tikku, V. K.

2002-12-01

A novel process of surface modification of clay filler has been developed by coating this with an acrylate monomer, trimethylol propane triacrylate (TMPTA) or a silane coupling agent, triethoxy vinyl silane (TEVS) followed by electron beam irradiation. Characterization of these surface modified fillers has been carried out by Fourier-transform infrared analysis (FTIR), electron spectroscopy for chemical analysis (ESCA), wettability by dynamic wicking method measuring the rise of a liquid through a filler-packed capillary tube and water flotation test, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), thermogravimetric analysis (TGA), and X-ray diffraction (XRD). Presence of the acrylate and the silane coupling agent on the modified fillers has been confirmed from FTIR, ESCA, and EDX studies, which has also been supported by TGA studies. The contact angle measurement by dynamic wicking method suggests improvement in hydrophobicity of the treated fillers, which is supported by water flotation test especially in the case of silanized clay. However, XRD studies demonstrate that the entire modification process does not affect the bulk properties of the fillers. Finally, both unmodified and modified clay fillers have been incorporated in styrene butadiene rubber (SBR) and nitrile rubber (NBR). Rheometric and mechanical properties reveal that there is a definite improvement using these modified fillers specially in the case of silanized clay compared to the control sample, probably due to successful enhancement in interaction between the treated clay and the base polymer.

Dielectric properties of inorganic fillers filled epoxy thin film

NASA Astrophysics Data System (ADS)

Norshamira, A.; Mariatti, M.

2015-07-01

The demand on the small size and high performance electronics has driven changes in the electronic packaging requirements from discrete capacitor to embedded capacitor. Embedded capacitor can improve electrical performance compared with discrete capacitor. This study aimed to achieve high dielectric of epoxy thin film composite that were targeted for application as embedded capacitor. In this study, inorganic fillers such as Calcium Copper Titanate (CCTO), Iron(III) Oxide (Fe2O3) and Titanium Dioxide (TiO2) were loaded in epoxy system at 5 and 20vol%. Morphology and dielectric properties were investigated to identify the effect of fillers loading and types of fillers on the properties of epoxy thin film composite. Based on the study, CCTO with 20vol% loading was found to have good dielectric properties compared to other type of fillers.

Physio-pharmacological Investigations About the Anti-inflammatory and Antinociceptive Efficacy of (+)-Limonene Epoxide.

PubMed

de Almeida, Antonia Amanda Cardoso; Silva, Renan Oliveira; Nicolau, Lucas Antonio Duarte; de Brito, Tarcísio Vieira; de Sousa, Damião Pergentino; Barbosa, André Luiz Dos Reis; de Freitas, Rivelilson Mendes; Lopes, Luciano da Silva; Medeiros, Jand-Venes Rolim; Ferreira, Paulo Michel Pinheiro

2017-04-01

D-limonene epoxidation generates (+)-limonene epoxide, an understudied compound in the pharmacologically point of view. Herein, we investigated the anti-inflammatory and antinociceptive potentialities of (+)-limonene epoxide and suggested a mechanism of action. The anti-inflammatory potential was analyzed using agents to induce paw edema, permeability, and myeloperoxidase (MPO) activity. Pro-inflammatory cytokines and cell migration of peritoneal cells were also assessed. Antinociceptive effects were evaluated by writhing test induced by acetic acid, formalin, and hot plate assays and contribution of opioid pathways. Pretreated animals with (+)-limonene epoxide showed reduced carrageenan-induced paw edema in all doses (25, 50, and 75 mg/kg) (P < 0.05). At 75 mg/kg, it suppressed edema provoked by compound 48/80, histamine, prostaglandin E 2 , and serotonin and reduced permeability determined by Evans blue and MPO activity. It also reduced leukocytes, neutrophils, and IL-1β levels in the peritoneal cavity in comparison with carrageenan group (P < 0.05). (+)-Limonene epoxide diminished abdominal contortions induced by acetic acid (78.9%) and paw licking times in both 1 (41.8%) and 2 (51.5%) phases and a pretreatment with naloxone (3 mg/kg) reverted the antinociceptive action in morphine- and (+)-limonene epoxide-treated groups (P < 0.05). Additionally, it enlarged response times to the thermal stimulus after 60 and 90 min. In conclusion, (+)-limonene epoxide inhibited release/activity of inflammatory mediators, vascular permeability, migration of neutrophils and displayed systemic and peripheral analgesic-dependent effects of the opioid system.

Epoxide-mediated differential packaging of Cif and other virulence factors into outer membrane vesicles.

PubMed

Ballok, Alicia E; Filkins, Laura M; Bomberger, Jennifer M; Stanton, Bruce A; O'Toole, George A

2014-10-01

Pseudomonas aeruginosa produces outer membrane vesicles (OMVs) that contain a number of secreted bacterial proteins, including phospholipases, alkaline phosphatase, and the CFTR inhibitory factor (Cif). Previously, Cif, an epoxide hydrolase, was shown to be regulated at the transcriptional level by epoxides, which serve as ligands of the repressor, CifR. Here, we tested whether epoxides have an effect on Cif levels in OMVs. We showed that growth of P. aeruginosa in the presence of specific epoxides but not a hydrolysis product increased Cif packaging into OMVs in a CifR-independent fashion. The outer membrane protein, OprF, was also increased under these conditions, but alkaline phosphatase activity was not significantly altered. Additionally, we demonstrated that OMV shape and density were affected by epoxide treatment, with two distinct vesicle fractions present when cells were treated with epibromohydrin (EBH), a model epoxide. Vesicles isolated from the two density fractions exhibited different protein profiles in Western blotting and silver staining. We have shown that a variety of clinically or host-relevant treatments, including antibiotics, also alter the proteins packaged in OMVs. Proteomic analysis of purified OMVs followed by an analysis of transposon mutant OMVs yielded mutants with altered vesicle packaging. Finally, epithelial cell cytotoxicity was reduced in the vesicles formed in the presence of EBH, suggesting that this epoxide alters the function of the OMVs. Our data support a model whereby clinically or host-relevant signals mediate differential packaging of virulence factors in OMVs, which results in functional consequences for host-pathogen interactions. Copyright © 2014, American Society for Microbiology. All Rights Reserved.

Three-body-wear resistance of the experimental composites containing filler treated with hydrophobic silane coupling agents.

PubMed

Nihei, Tomotaro; Dabanoglu, Alp; Teranaka, Toshio; Kurata, Shigeaki; Ohashi, Katsura; Kondo, Yukishige; Yoshino, Norio; Hickel, Reinhard; Kunzelmann, Karl-Heinz

2008-06-01

This paper evaluated the wear resistance of resin composite materials with fillers which were modified with a novel hydrophobic silane coupling agent. The novel silane coupling agent containing hydrophobic phenyl group 3-(3-methoxy-4-methacryloyloxyphenyl)propyltrimethoxysilane (p-MBS) was synthesized. The experimental light-cure hybrid composites containing 85wt% of filler modified with this silane were formulated. Twelve specimens were prepared for the three-body-wear test with the ACTA machine and the collected data were analyzed statistically using a one-way ANOVA and Tukey's multiple comparison test as the post hoc test. The wear of the composites containing fillers treated with p-MBS was significantly lower compared with the composite materials containing fillers pretreated with 3-methacryloyloxypropyltrimethoxysilane or the commercially composites (AP-X and ELS extra low shrinkage) after a wear test for 200,000 cycles (p<0.05). It is suggested that the resin composites containing fillers modified with the novel hydrophobic silane has high wear resistant, because of the coupling layers treated with this silane had an excellent affinity with the base resin and formed a highly hydrophobic layer on the filler surface.

Methyltrioxorhenium-catalyzed epoxidation of homoallylic alcohols with hydrogen peroxide.

PubMed

Yamazaki, Shigekazu

2012-11-02

Homoallylic alcohols were efficiently converted to the corresponding 3,4-epoxy alcohols in excellent yields by methyltrioxorhenium (MTO)-catalyzed epoxidation with aqueous hydrogen peroxide as the terminal oxidant and 3-methylpyrazole (10 mol %) as an additive. The epoxidations of homoallylic alcohols proceeded under organic solvent-free conditions faster than those in dichloromethane.

COMPARATIVE STUDIES OF THE EFFECT OF POLYCYCLIC AROMATIC HYDROCARBON GEOMETRY ON THE HYDROLYSIS OF DIOL EPOXIDES

EPA Science Inventory

Comparative studies of the effect of polycyclic aromatic hydrocarbon geometry on the hydrolysis of diol epoxides

The interaction of the diol epoxides (DEs) of both planar and non-planar PAHs with water have been examined using quantum mechanical and molecular dynamics. Th...

Recent trends in ring opening of epoxides with sulfur nucleophiles.

PubMed

Ahmad, Sajjad; Zahoor, Ameer Fawad; Naqvi, Syed Ali Raza; Akash, Muhammad

2018-02-01

Thiolysis of epoxides offers an efficient and simple synthetic approach to access [Formula: see text]-hydroxy sulfides which are valuable scaffold in the synthesis of various important molecules in medicinal chemistry. This review article presents a recent compilation of the synthetic approaches developed after 2000 for the thiolysis of epoxides.

Exploring the origins of selectivity in soluble epoxide hydrolase from Bacillus megaterium† †Electronic supplementary information (ESI) available. See DOI: 10.1039/c7ob01847a

PubMed Central

Serrano-Hervás, Eila

2017-01-01

Epoxide hydrolase (EH) enzymes catalyze the hydration of racemic epoxides to yield their corresponding vicinal diols. These enzymes present different enantio- and regioselectivity depending upon either the substrate structure or the substitution pattern of the epoxide ring. In this study, we computationally investigate the Bacillus megaterium epoxide hydrolase (BmEH)-mediated hydrolysis of racemic styrene oxide (rac-SO) and its para-nitro styrene oxide (rac-p-NSO) derivative using density functional theory (DFT) and an active site cluster model consisting of 195 and 197 atoms, respectively. Full reaction mechanisms for epoxide ring opening were evaluated considering the attack at both oxirane carbons and considering two possible orientations of the substrate at the BmEH active site. Our results indicate that for both SO and p-NSO substrates the BmEH enantio- and regioselectivity is opposite to the inherent (R)-BmEH selectivity, the attack at the benzylic position (C1) of the (S)-enantiomer being the most favoured chemical outcome. PMID:29026902

Oxidation catalysis of Nb(salan) complexes: asymmetric epoxidation of allylic alcohols using aqueous hydrogen peroxide as an oxidant.

PubMed

Egami, Hiromichi; Oguma, Takuya; Katsuki, Tsutomu

2010-04-28

Several optically active Nb(salan) complexes were synthesized, and their oxidation catalysis was examined. A dimeric mu-oxo Nb(salan) complex that was prepared from Nb(OiPr)(5) and a salan ligand was found to catalyze the asymmetric epoxidation of allylic alcohols using a urea-hydrogen peroxide adduct as an oxidant with good enantioselectivity. However, subsequent studies of the time course of this epoxidation and of the relationship between the ee of the ligand and the ee of the product indicated that the mu-oxo dimer dissociates into a monomeric species prior to epoxidation. Moreover, monomeric Nb(salan) complexes prepared in situ from Nb(OiPr)(5) and salan ligands followed by water treatment were found to catalyze the epoxidation of allylic alcohols better using aqueous hydrogen peroxide in CHCl(3)/brine or toluene/brine solution with high enantioselectivity ranging from 83 to 95% ee, except for the reaction of cinnamyl alcohol that showed a moderate ee of 74%. This is the first example of the highly enantioselective epoxidation of allylic alcohols using aqueous hydrogen peroxide as an oxidant.

Secondary Organic Aerosol Formation from 2-Methyl-3-Buten-2-ol Photooxidation: Evidence of Acid-Catalyzed Reactive Uptake of Epoxides

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Haofei; Zhang, Zhenfa; Cui, Tianqu

2014-04-08

Secondary organic aerosol (SOA) formation from 2-methyl-3-buten-2-ol (MBO) photooxidation has recently been observed in both field and laboratory studies. Similar to isoprene, MBO-derived SOA increases with elevated aerosol acidity in the absence of nitric oxide; therefore, an epoxide intermediate, (3,3-dimethyloxiran-2-yl)methanol (MBO epoxide) was synthesized and tentatively proposed here to explain this enhancement. In the present study, the potential of the synthetic MBO epoxide to form SOA via reactive uptake was systematically examined. SOA was observed only in the presence of acidic aerosols. Major SOA constituents, 2,3-dihydroxyisopentanol (DHIP) and MBO-derived organosulfate isomers, were chemically characterized in both laboratory-generated SOA and inmore » ambient fine aerosols collected from the BEACHON-RoMBAS field campaign during summer 2011, where MBO emissions are substantial. Our results support epoxides as potential products of MBO photooxidation leading to formation of atmospheric SOA and suggest that reactive uptake of epoxides may generally explain acid enhancement of SOA observed from other biogenic hydrocarbons.« less

Influence of matrix and filler fraction on biofilm formation on the surface of experimental resin-based composites.

PubMed

Ionescu, Andrei; Brambilla, Eugenio; Wastl, Daniel S; Giessibl, Franz J; Cazzaniga, Gloria; Schneider-Feyrer, Sibylle; Hahnel, Sebastian

2015-01-01

The aim of this study was to investigate the impact of resin matrix chemistry and filler fraction on biofilm formation on the surface of experimental resin-based composites (RBCs). Specimens were prepared from eight experimental RBC formulations differing in resin matrix blend (BisGMA/TEGDMA in a 7:3 wt% ratio or UDMA/aliphatic dimethacrylate in a 1:1 wt% ratio) and filler fraction (no fillers; 65 wt% dental glass with an average diameter of 7 or 0.7 µm or 65 wt% SiO2 with an average diameter of 20 nm). Surface roughness, surface free energy, and chemical surface composition were determined; surface topography was visualized using atomic force microscopy. Biofilm formation was simulated under continuous flow conditions for a 48 h period using a monospecies Streptococcus mutans and a multispecies biofilm model. In the monospecies biofilm model, the impact of the filler fraction overruled the influence of the resin matrix, indicating lowest biofilm formation on RBCs with nano-scaled filler particles and those manufactured from the neat resin blends. The multispecies model suggested a more pronounced effect of the resin matrix blend, as significantly higher biofilm formation was identified on RBCs with a UDMA/dimethacrylate matrix blend than on those including a BisGMA/TEGDMA matrix blend but analogous filler fractions. Although significant differences in surface properties between the various materials were identified, correlations between the surface properties and biofilm formation were poor, which highlights the relevance of surface topography and chemistry. These results may help to tailor novel RBC formulations which feature reduced biofilm formation on their surface.

Capsanthone 3,6-epoxide, a new carotenoid from the fruits of the red paprika Capsicum annuum L.

PubMed

Maoka, T; Fujiwara, Y; Hashimoto, K; Akimoto, N

2001-08-01

The structure of a new carotenoid, isolated from the fruits of the red tomato-shaped paprika Capsicum annuum L., was elucidated to be (3S,5R,6S,5'R)-3,6-epoxy-5,6-dihydro-5-hydroxy-beta,kappa-carotene-3',6'-dione by spectroscopic analyses, including fast atom bombardment collision-induced dissociation-mass spectrometry/mass spectrometry (FAB CID-MS/MS) and was designated capsanthone 3,6-epoxide. Capsanthone 3,6-epoxide is assumed to be an oxidative metabolite of capsanthin 3,6-epoxide in paprika.

Epoxidation of Geraniol: An Advanced Organic Experiment that Illustrates Asymmetric Synthesis

NASA Astrophysics Data System (ADS)

Bradley, Lynn M.; Springer, Joseph W.; Delate, Gregory M.; Goodman, Andrew

1997-11-01

The Sharpless epoxidation reaction is considered one of the most powerful advances in asymmetric organic synthesis (1). It is a classic example of the use of an asymmetric catalyst to provide an enantiomerically enriched mixture of epoxy alcohols. The procedure typically uses titanium(IV) tetraisopropoxide (Ti(OiPr)4) as a catalyst, a peroxide, and dialkyl tartrates to induce asymmetry in the epoxidation reaction of allylic alcohols. The experiment described in this paper illustrates the principle of asymmetric epoxidation and enables students to determine enantiomeric product ratios using chiral shift reagents and NMR spectroscopy.

Enantioselective synthesis of 2,2-disubstituted terminal epoxides via catalytic asymmetric Corey-Chaykovsky epoxidation of ketones.

PubMed

Sone, Toshihiko; Yamaguchi, Akitake; Matsunaga, Shigeki; Shibasaki, Masakatsu

2012-02-07

Catalytic asymmetric Corey-Chaykovsky epoxidation of various ketones with dimethyloxosulfonium methylide using a heterobimetallic La-Li(3)-BINOL complex (LLB) is described. The reaction proceeded smoothly at room temperature in the presence of achiral phosphine oxide additives, and 2,2-disubstituted terminal epoxides were obtained in high enantioselectivity (97%-91% ee) and yield ( > 99%-88%) from a broad range of methyl ketones with 1-5 mol% catalyst loading. Enantioselectivity was strongly dependent on the steric hindrance, and other ketones, such as ethyl ketones and propyl ketones resulted in slightly lower enantioselectivity (88%-67% ee).

Investigation on localized corrosion of 304 stainless steel joints brazed using Sn-plated Ag alloy filler in NaCl aqueous solution

NASA Astrophysics Data System (ADS)

Wang, Xingxing; Li, Shuai; Peng, Jin

2018-03-01

Novel AgCuZnSn filler metal with high Sn contents was prepared from BAg50CuZn filler metal by a process of electroplating and thermal diffusion, and the prepared filler metal was applied to induction brazing of 304 stainless steel. The corrosion behavior of the brazed joints was evaluated based on localized corrosion analysis, the morphology of the joints were analyzed by SEM after immersion in a 3.5 vol% NaCl aqueous solution. The results indicated that corrosion groove occurred near the interface between the stainless steel base metal and the brazing seam. A wide range of defects such as holes and cracks appeared on the surface of the base metal, while the brazing seam zone almost no corrosion defects occur. With the increase of corrosion time, the corrosion rates of both the brazing seam and the base metal first exhibited an increasing trend, followed by a decreasing trend, and the corrosion rate of the base metal was slightly greater than that of the brazing seam. The corrosion potential of the brazing seam and 304 stainless steel were -0.7758 V and -0.7863 V, respectively.

A pseudo-thermodynamic description of dispersion for nanocomposites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jin, Yan; Beaucage, Gregory; Vogtt, Karsten

Dispersion in polymer nanocomposites is determined by the kinetics of mixing and chemical affinity. Compounds like reinforcing filler/elastomer blends display some similarity to colloidal solutions in that the filler particles are close to randomly dispersed through processing. It is attractive to apply a pseudo-thermodynamic approach taking advantage of this analogy between the kinetics of mixing for polymer compounds and thermally driven dispersion for colloids. In order to demonstrate this pseudo-thermodynamic approach, two polybutadienes and one polyisoprene were milled with three carbon blacks and two silicas. These samples were examined using small-angle x-ray scattering as a function of filler concentration tomore » determine a pseudo-second order virial coefficient, A2, which is used as an indicator for compatibility of the filler and polymer. It is found that A2 follows the expected behavior with lower values for smaller primary particles indicating that smaller particles are less compatible and more difficult to mix. The measured values of A2 can be used to specify repulsive interaction potentials for coarse grain DPD simulations of filler/elastomer systems. In addition, new methods to quantify the filler percolation threshold and filler mesh size as a function of filler concentration are obtained. Moreover, the results represent a new approach to understanding and predicting compatibility in polymer nanocomposites based on a pseudo-thermodynamic approach.« less

A pseudo-thermodynamic description of dispersion for nanocomposites

DOE PAGES

Jin, Yan; Beaucage, Gregory; Vogtt, Karsten; ...

2017-09-18

Dispersion in polymer nanocomposites is determined by the kinetics of mixing and chemical affinity. Compounds like reinforcing filler/elastomer blends display some similarity to colloidal solutions in that the filler particles are close to randomly dispersed through processing. It is attractive to apply a pseudo-thermodynamic approach taking advantage of this analogy between the kinetics of mixing for polymer compounds and thermally driven dispersion for colloids. In order to demonstrate this pseudo-thermodynamic approach, two polybutadienes and one polyisoprene were milled with three carbon blacks and two silicas. These samples were examined using small-angle x-ray scattering as a function of filler concentration tomore » determine a pseudo-second order virial coefficient, A2, which is used as an indicator for compatibility of the filler and polymer. It is found that A2 follows the expected behavior with lower values for smaller primary particles indicating that smaller particles are less compatible and more difficult to mix. The measured values of A2 can be used to specify repulsive interaction potentials for coarse grain DPD simulations of filler/elastomer systems. In addition, new methods to quantify the filler percolation threshold and filler mesh size as a function of filler concentration are obtained. Moreover, the results represent a new approach to understanding and predicting compatibility in polymer nanocomposites based on a pseudo-thermodynamic approach.« less

40 CFR 63.1427 - Process vent requirements for processes using extended cookout as an epoxide emission reduction...

Code of Federal Regulations, 2012 CFR

2012-07-01

... reactor liquid at the beginning of the time period, weight percent. k = Reaction rate constant, 1/hr. t = Time, hours. Note: This equation assumes a first order reaction with respect to epoxide concentration... measuring the concentration of the unreacted epoxide, or by using process knowledge, reaction kinetics, and...

Polyurethane foam with multi walled carbon nanotubes/magnesium hybrid filler

NASA Astrophysics Data System (ADS)

Adnan, Sinar Arzuria; Zainuddin, Firuz; Zaidi, Nur Hidayah Ahmad; Akil, Hazizan Md.; Ahmad, Sahrim

2016-07-01

The purpose of this paper is to investigate the effect of multiwalled carbon nanotubes (MWCNTs)/magnesium (Mg) hybrid filler in polyurethane (PU) foams with different weight percentages (0.5 wt.% to 3.0 wt.%). The PU/MWCNTs/Mg foam composites were formed by reaction of based palm oil polyol (POP) with methylene diphenyl diisocyanate (MDI) with ratio 1:1.1 by weight. The foam properties were evaluated in density, morphology and compressive strength. The addition of 2.5 wt.% hybrid filler showed the higher density in 59.72 kg/m3 and thus contribute to the highest compressive strength at 1.76 MPa. The morphology show cell in closed structure and addition hybrid filler showed uneven structure.

Nanostructured Materials Utilized in Biopolymer-based Plastics for Food Packaging Applications.

PubMed

Ghanbarzadeh, Babak; Oleyaei, Seyed Amir; Almasi, Hadi

2015-01-01

Most materials currently used for food packaging are nondegradable, generating environmental problems. Several biopolymers have been exploited to develop materials for ecofriendly food packaging. However, the use of biopolymers has been limited because of their usually poor mechanical and barrier properties, which may be improved by adding reinforcing compounds (fillers), forming composites. Most reinforced materials present poor matrix-filler interactions, which tend to improve with decreasing filler dimensions. The use of fillers with at least one nanoscale dimension (nanoparticles) produces nanocomposites. Nanoparticles have proportionally larger surface area than their microscale counterparts, which favors the filler-matrix interactions and the performance of the resulting material. Besides nanoreinforcements, nanoparticles can have other functions when added to a polymer, such as antimicrobial activity, etc. in this review paper, the structure and properties of main kinds of nanostructured materials which have been studied to use as nanofiller in biopolymer matrices are overviewed, as well as their effects and applications.

Reasons and remedies for the agglomeration of multilayered graphene and carbon nanotubes in polymers

PubMed Central

Atif, Rasheed

2016-01-01

Summary One of the main issues in the production of polymer nanocomposites is the dispersion state of filler as multilayered graphene (MLG) and carbon nanotubes (CNTs) tend to agglomerate due to van der Waals forces. The agglomeration can be avoided by using organic solvents, selecting suitable dispersion and production methods, and functionalizing the fillers. Another proposed method is the use of hybrid fillers as synergistic effects can cause an improvement in the dispersion state of the fillers. In this review article, various aspects of each process that can help avoid filler agglomeration and improve dispersion state are discussed in detail. This review article would be helpful for both current and prospective researchers in the field of MLG- and CNT-based polymer nanocomposites to achieve maximum enhancement in mechanical, thermal, and electrical properties of produced polymer nanocomposites. PMID:27826492

Dielectric properties of inorganic fillers filled epoxy thin film

DOE Office of Scientific and Technical Information (OSTI.GOV)

Norshamira, A., E-mail: myra.arshad@gmail.com; Mariatti, M., E-mail: mariatti@usm.my

2015-07-22

The demand on the small size and high performance electronics has driven changes in the electronic packaging requirements from discrete capacitor to embedded capacitor. Embedded capacitor can improve electrical performance compared with discrete capacitor. This study aimed to achieve high dielectric of epoxy thin film composite that were targeted for application as embedded capacitor. In this study, inorganic fillers such as Calcium Copper Titanate (CCTO), Iron(III) Oxide (Fe{sub 2}O{sub 3}) and Titanium Dioxide (TiO{sub 2}) were loaded in epoxy system at 5 and 20vol%. Morphology and dielectric properties were investigated to identify the effect of fillers loading and types ofmore » fillers on the properties of epoxy thin film composite. Based on the study, CCTO with 20vol% loading was found to have good dielectric properties compared to other type of fillers.« less

Patulin biosynthesis: Epoxidation of toluquinol and gentisyl alcohol by particulate preparations from Penicillium patulum

DOE Office of Scientific and Technical Information (OSTI.GOV)

Priest, J.W.; Light, R.J.

1989-11-14

A crude extract that catalyzes the epoxidation of toluquinol and gentisyl alcohol was isolated from cultures of Penicillium patulum. About 60% of the activity sedimented from crude extract upon centrifugation at 105000g for 2 h, and at 30000g for 30 min after precipitation with 30% ammonium sulfate and resuspension in buffer. The quinone epoxide phyllostine, a product of gentisyl alcohol epoxidation, has previously been shown to be an intermediate in the biosynthesis of patulin and was shown to be further converted to neopatulin by the extract. The epoxide product of toluquinol, desoxyphyllostine (2-methyl-5,6-epoxy-1,4-benzoquinone), has not been reported previously from fungalmore » cultures. Its structure was confirmed by GC-mass spectrometry and proton and {sup 13}C NMR. Its CD spectrum showed the same shape and signs as that of phyllostine, indicating that it too is an enzymatic product with a similar absolute configuration. Whereas chemical epoxidation of toluquinone and gentisly quinone occurs with hydrogen peroxide, the enzymatic epoxidation utilized oxygen and the hydroquinone. The epoxidation was inhibited by 1,10-phenanthroline, EDTA, and {rho}-(chloromercuri)benzenesulfonic acid and by degassing with nitrogen, but no inhibition was observed with KCN, catalase, or CO. The apparent K{sub m}'s were similar for the two substrates with both substrates showing inhibition at 1.0 mM. The rate of desoxyphyllostine formation was more than 10 times that of phyllostine formation at equivalent substrate concentrations. Gentisaldehyde was not a substrate for the enzyme. The epoxidase was induced in late fermentor cultures of P. patulum with the same kinetics as m-hydroxybenzyl alcohol dehydrogenase, another enzyme associated with the induction of patulin biosynthesis.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Askari, Ara A.; Thomson, Scott; Edin, Matthew L.

Highlights: • We examined epoxygenase product formation and regulation in endothelial cells. • The epoxygenase CYP2J2 is an LPS (TLR-4) inducible enzyme in endothelial cells. • The endothelial cell line EA.Hy926 synthesises epoxygenase products. • Inhibition of endothelial epoxygenases increases TNFα secretion. • Soluble epoxide hydrolase inhibitors reduce inflammation-induced TNFα and NFκB. - Abstract: The roles of CYP lipid-metabolizing pathways in endothelial cells are poorly understood. Human endothelial cells expressed CYP2J2 and soluble epoxide hydrolase (sEH) mRNA and protein. The TLR-4 agonist LPS (1 μg/ml; 24 h) induced CYP2J2 but not sEH mRNA and protein. LC–MS/MS analysis of the stablemore » commonly used human endothelial cell line EA.Hy926 showed active epoxygenase and epoxide hydrolase activity: with arachidonic acid (stable epoxide products 5,6-DHET, and 14,15-DHET), linoleic acid (9,10-EPOME and 12,13-EPOME and their stable epoxide hydrolase products 9,10-DHOME and 12,13-DHOME), docosahexaenoic acid (stable epoxide hydrolase product 19,20-DiHDPA) and eicosapentaenoic acid (stable epoxide hydrolase product 17,18-DHET) being formed. Inhibition of epoxygenases using either SKF525A or MS-PPOH induced TNFα release, but did not affect LPS, IL-1β, or phorbol-12-myristate-13-acetate (PMA)-induced TNFα release. In contrast, inhibition of soluble epoxide hydrolase by AUDA or TPPU inhibited basal, LPS, IL-1β and PMA induced TNFα release, and LPS-induced NFκB p65 nuclear translocation. In conclusion, human endothelial cells contain a TLR-4 regulated epoxygenase CYP2J2 and metabolize linoleic acid > eicosapentaenoic acid > arachidonic acid > docosahexaenoic acid to products with anti-inflammatory activity.« less

The de-epoxidase and epoxidase reactions of Mantoniella squamata (Prasinophyceae) exhibit different substrate-specific reaction kinetics compared to spinach.

PubMed

Frommolt, R; Goss, R; Wilhelm, C

2001-07-01

In vivo the prasinophyceaen alga Mantoniella squamata Manton et Parke uses an incomplete violaxanthin (Vx) cycle, leading to a strong accumulation of antheraxanthin (Ax) under conditions of high light. Here, we show that this zeaxanthin (Zx)-depleted Vx/Ax cycle is caused by an extremely slow second de-epoxidation step from Ax to Zx, and a fast epoxidation from Ax back to Vx in the light. The rate constant of Ax epoxidation is 5 to 6 times higher than the rate constant of Zx formation, implying that Ax is efficiently converted back to Vx before it can be de-epoxidated to Zx. It is, however, only half the rate constant of the first de-epoxidation step from Vx to Ax, thus explaining the observed net accumulation of Ax during periods of strong illumination. When comparing the rate constant of the second de-epoxidation step in M. squamata with Zx formation in spinach (Spinacia oleracea L.) thylakoids, we find a 20-fold reduction in the reaction kinetics of the former. This extremely slow Ax de-epoxidation, which is also exhibited by the isolated Mantoniella violaxanthin de-epoxidase (VDE), is due to a reduced substrate affinity of M. squamata VDE for Ax compared with the VDE of higher plants. Mantoniella VDE, which has a similar Km value for Vx, shows a substantially increased Km for the substrate Ax in comparison with spinach VDE. Our results furthermore explain why Zx formation in Mantoniella cells can only be found at low pH values that represent the pH optimum of VDE. A pH of 5 blocks the epoxidation reaction and, consequently, leads to a slow but appreciable accumulation of Zx.

Stable and solubilized active Au atom clusters for selective epoxidation of cis-cyclooctene with molecular oxygen

DOE PAGES

Qian, Linping; Wang, Zhen; Beletskiy, Evgeny V.; ...

2017-03-28

Here, the ability of Au catalysts to effect the challenging task of utilizing molecular oxygen for the selective epoxidation of cyclooctene is fascinating. Although supported nanometre-size Au particles are poorly active, here we show that solubilized atomic Au clusters, present in ng ml –1 concentrations and stabilized by ligands derived from the oxidized hydrocarbon products, are active. They can be formed from various Au sources. They generate initiators and propagators to trigger the onset of the auto-oxidation reaction with an apparent turnover frequency of 440 s –1, and continue to generate additional initiators throughout the auto-oxidation cycle without direct participationmore » in the cycle. Spectroscopic characterization suggests that 7–8 atom clusters are effective catalytically. Extension of work based on these understandings leads to the demonstration that these Au clusters are also effective in selective oxidation of cyclohexene, and that solubilized Pt clusters are also capable of generating initiators for cyclooctene epoxidation.« less

Stable and solubilized active Au atom clusters for selective epoxidation of cis-cyclooctene with molecular oxygen

DOE Office of Scientific and Technical Information (OSTI.GOV)

Qian, Linping; Wang, Zhen; Beletskiy, Evgeny V.

Here, the ability of Au catalysts to effect the challenging task of utilizing molecular oxygen for the selective epoxidation of cyclooctene is fascinating. Although supported nanometre-size Au particles are poorly active, here we show that solubilized atomic Au clusters, present in ng ml –1 concentrations and stabilized by ligands derived from the oxidized hydrocarbon products, are active. They can be formed from various Au sources. They generate initiators and propagators to trigger the onset of the auto-oxidation reaction with an apparent turnover frequency of 440 s –1, and continue to generate additional initiators throughout the auto-oxidation cycle without direct participationmore » in the cycle. Spectroscopic characterization suggests that 7–8 atom clusters are effective catalytically. Extension of work based on these understandings leads to the demonstration that these Au clusters are also effective in selective oxidation of cyclohexene, and that solubilized Pt clusters are also capable of generating initiators for cyclooctene epoxidation.« less

Pesticide contamination of endangered gray bats and their food base in Boone County, Missouri, 1982

USGS Publications Warehouse

Clawson, R.L.; Clark, D.R.

1989-01-01

Gray bat guano from Devil's Icebox and Hunters Caves contained dieldrin at levels previously associated with gray bat mortality. Two of four gray bats found dead in Holton Cave had lethal brain concentrations of dieldrin. Twenty-five of 28 (86%) insect samples from bat foraging areas contained measurable dieldrin, heptachlor epoxide or both. Beetle samples were most heavily contaminated containing up to 2.2 ppm and 1.1 ppm heptachlor epoxide. The addition of Holton Cave brings to five the number of Missouri caves where gray bats have died of food chain pesticide poisoning.

N-Methylpyrrolidone Hydroperoxide/Cs2 CO3 as an Excellent Reagent System for the Hydroxy-Directed Diastereoselective Epoxidation of Electron-Deficient Olefins.

PubMed

Victor, Napoleon John; Gana, Janardhanan; Muraleedharan, Kannoth Manheri

2015-10-12

This report introduces N-methylpyrrolidone hydroperoxide (NMPOOH)/base as an excellent reagent system for hydroxy-directed syn selective epoxidation of electron-deficient olefins, characterized by high diastereoselectivity, short reaction times and remarkable chemoselectivity, especially in presence of oxidatively labile nitrogen or sulfur atoms. NMPOOH also proves efficient in the oxidation of electron-deficient aromatic aldehydes, in the removal of oxazolidinone chiral auxiliary, and in the functionalization of alkenes and alkynes, showing wide application potential. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Calcium oxide supported gold nanoparticles as catalysts for the selective epoxidation of styrene by t-butyl hydroperoxide.

PubMed

Dumbre, Deepa K; Choudhary, Vasant R; Patil, Nilesh S; Uphade, Balu S; Bhargava, Suresh K

2014-02-01

Gold nanoparticles are deposited on basic CaO supports as catalysts for the selective conversion of styrene into styrene oxide. Synthetic methods, gold loading and calcination temperatures are varied to permit an understanding of their influence on gold nanoparticle size, the presence of cationic gold species and the nature of interaction between the gold nanoparticles and the CaO support. Based on these studies, optimal conditions are designed to make the Au/CaO catalyst efficient for the selective epoxidation of styrene. Copyright © 2013 Elsevier Inc. All rights reserved.

Studies toward brevisulcenal F via convergent strategies for marine ladder polyether synthesis.

PubMed

Katcher, Matthew; Jamison, Timothy F

2018-03-15

Shortly after the initial isolation of marine ladder polyether natural products, biomimetic epoxide-opening cascade reactions were proposed as an efficient strategy for the synthesis of these compounds. However, difficulties in assembling the cascade precursors have limited the realization of these cascades. In this report, we describe strategies that provide convergent access to cascade precursors via regioselective allylation and efficient fragment coupling. We then investigate epoxide-opening cascades promoted by strong bases for the formation of fused tetrahydropyrans. These strategies are evaluated in the context of the synthesis of rings CDEFG of brevisulcenal F.

Titanium-based zeolitic imidazolate framework for chemical fixation of carbon dioxide

EPA Science Inventory

A titanium-based zeolitic imidazolate framework (Ti-ZIF) with high surface area and porous morphology was synthesized and itsefficacy was demonstrated in the synthesis of cyclic carbonates from epoxides and carbon dioxide.

Increasing Ti-6Al-4V brazed joint strength equal to the base metal by Ti and Zr amorphous filler alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ganjeh, E., E-mail: navidganjehie@sina.kntu.ac.ir; Sarkhosh, H.; Bajgholi, M.E.

Microstructural features developed along with mechanical properties in furnace brazing of Ti-6Al-4V alloy using STEMET 1228 (Ti-26.8Zr-13Ni-13.9Cu, wt.%) and STEMET 1406 (Zr-9.7Ti-12.4Ni-11.2Cu, wt.%) amorphous filler alloys. Brazing temperatures employed were 900-950 Degree-Sign C for the titanium-based filler and 900-990 Degree-Sign C for the zirconium-based filler alloys, respectively. The brazing time durations were 600, 1200 and 1800 s. The brazed joints were evaluated by ultrasonic test, and their microstructures and phase constitutions analyzed by metallography, scanning electron microscopy and X-ray diffraction analysis. Since microstructural evolution across the furnace brazed joints primarily depends on their alloying elements such as Cu, Ni andmore » Zr along the joint. Accordingly, existence of Zr{sub 2}Cu, Ti{sub 2}Cu and (Ti,Zr){sub 2}Ni intermetallic compounds was identified in the brazed joints. The chemical composition of segregation region in the center of brazed joints was identical to virgin filler alloy content which greatly deteriorated the shear strength of the joints. Adequate brazing time (1800 s) and/or temperature (950 Degree-Sign C for Ti-based and 990 Degree-Sign C for Zr-based) resulted in an acicular Widmanstaetten microstructure throughout the entire joint section due to eutectoid reaction. This microstructure increased the shear strength of the brazed joints up to the Ti-6Al-4V tensile strength level. Consequently, Ti-6Al-4V can be furnace brazed by Ti and Zr base foils produced excellent joint strengths. - Highlights: Black-Right-Pointing-Pointer Temperature or time was the main factors of controlling braze joint strength. Black-Right-Pointing-Pointer Developing a Widmanstaetten microstructure generates equal strength to base metal. Black-Right-Pointing-Pointer Brittle intermetallic compounds like (Ti,Zr){sub 2}Ni/Cu deteriorate shear strength. Black-Right-Pointing-Pointer Ti and Zr base filler alloys were the best choice for brazing Ti-6Al-4V.« less

Filler features and their effects on wear and degree of conversion of particulate dental resin composites.

PubMed

Turssi, C P; Ferracane, J L; Vogel, K

2005-08-01

Based on the incomplete understanding on how filler features influence the wear resistance and monomer conversion of resin composites, this study sought to evaluate whether materials containing different shapes and combinations of size of filler particles would perform similarly in terms of three-body abrasion and degree of conversion. Twelve experimental monomodal, bimodal or trimodal composites containing either spherical or irregular shaped fillers ranging from 100 to 1500 nm were examined. Wear testings were conducted in the OHSU wear machine (n = 6) and quantified after 10(5) cycles using a profilometer. Degree of conversion (DC) was measured by FTIR spectrometry at the surface of the composites (n = 6). Data sets were analyzed using one-way Anova and Tukey's test at a significance level of 0.05. Filler size and geometry was found to have a significant effect on wear resistance and DC of composites. At specific sizes and combinations, the presence of small filler particles, either spherical or irregular, may aid in enhancing the wear resistance of composites, without compromising the percentage of reacted carbon double bonds.

Corrosion protection and adhesion properties of the epoxy coating applied on the steel substrate pre-treated by a sol-gel based silane coating filled with amino and isocyanate silane functionalized graphene oxide nanosheets

NASA Astrophysics Data System (ADS)

Parhizkar, Nafise; Ramezanzadeh, Bahram; Shahrabi, Taghi

2018-05-01

This research has focused on the effect of graphene oxide (GO) nano-fillers embedded in the sol-gel based silane coating on the corrosion protection and adhesion properties of the epoxy coating applied on the steel substrate pre-treated by silane coatings. For this purpose, a mixture of Methyltriethoxysilane (MTES) and Tetraethylorthosilicate (TEOS) silane precursors was used for preparation of composite matrix and the GO nanosheets, which are covalently functionalized with 3-(Triethoxysilyl)propyl isocyanate (TEPI, IGO nano-fillers) and 3-aminopropyltriethoxysilane (APTES, AGO nano-fillers), were used as filler. The GO, AGO and IGO nanosheets were characterized by Fourier Transform Infrared Spectroscopy (FT-IR), UV-Visible analysis and field emission-scanning electron microscopy techniques. The performance of the silane/epoxy coatings was investigated by pull-off adhesion, cathodic delamination, salt spray and electrochemical impedance spectroscopy (EIS) tests. Results revealed that AGO and IGO nano-fillers significantly improved the corrosion resistance and adhesion properties of the top epoxy coating due to better compatibility with silane matrix, excellent barrier properties and the formation of covalent bonds with the top epoxy coating.

Lignin and holocellulose from pecan nutshell as reinforcing fillers in poly (lactic acid) biocomposites.

PubMed

Agustin-Salazar, Sarai; Cerruti, Pierfrancesco; Medina-Juárez, Luis Ángel; Scarinzi, Gennaro; Malinconico, Mario; Soto-Valdez, Herlinda; Gamez-Meza, Nohemi

2018-04-24

Lignocellulose from agro-food biowaste represents a valuable source of cost-effective structural fillers for wholly renewable polymer composites. In this work, pecan (Carya illinoinensis) nutshell (NS) fiber and its structural components, holocellulose (HC) and acid insoluble lignin (AIL), were isolated, characterized and used as reinforcing fillers to manufacture poly(lactic acid) (PLA) based biocomposites. Thermal, morphological and mechanical properties of the prepared materials were analyzed. NS and HC acted as heterogeneous nucleating agents, potentially able to control PLA physical aging. Moreover, they significantly enhanced the viscoelastic response of PLA, mainly restricting the melt molecular mobility due to hydrodynamic effects and the formation of a three-dimensional particulate network. Flexural tests demonstrated that HC induced a 25% increase in modulus compared to the plain polymer. AIL, conversely, conferred higher ductility to the PLA matrix producing an increase in stress and strain at break of 55% and 65%, respectively. Finally, all the biocomposites showed lower resilience with respect to plain PLA due to the lack of chemical adhesion between filler and matrix. These results emphasize the potential of NS as a source of reinforcing filler in polymer-based biocomposites. Copyright © 2018. Published by Elsevier B.V.

Influence of brazing conditions on the strength of brazed joints of alumina dispersion-strengthened copper to 316 stainless steel

NASA Astrophysics Data System (ADS)

Nishi, H.; Kikuchi, K.

1998-10-01

Brazing of alumina dispersion-strengthened copper (DS Cu) to 316 stainless steel were conducted in order to investigate the influence of filler metals and brazing conditions on the joint strength. The brazing were performed with a silver-base (BAg-8) and three kinds of gold-base (BAu-2,4,11) filler metals with varying brazing joint clearance and brazing time. The filler metal had a greater effect on the joint strength than the brazing joint clearance and brazing time. The joint with BAu-2 was superior to the joint with other filler metals. The tensile strength of the joint with BAu-2 was as large as that of DS Cu, however, the Charpy and low cycle fatigue strength were lower than those of DS Cu. The DS Cu melted near the brazed zone, consequently recrystallization and agglomeration of alumina occurred in the diffusion layer for all filler metals. The grain size after the recrystallization was small in order of BAu-2, BAu-4 and BAu-11, that was in accordance with the order of the brazing temperature. The excellent fracture strength for the joint with BAu-2 was attributed to the smallest grain size.

Nanostructured conductive polymeric materials

NASA Astrophysics Data System (ADS)

Al-Saleh, Mohammed H.

Conductive polymer composites (CPCs) are a suitable alternative to metals in many applications due to their light-weight, corrosion resistance, low cost, ease of processing and design flexibility. CPCs have been formulated using different types of conductive fillers. In this PhD thesis, the focus is on CPCs for electrostatic discharge (ESD) protection and electromagnetic interference (EMI) attenuation. Despite the versatility of conductive fillers, carbon black (CB) has been the dominant filler to make CPCs for ESD protection applications because CB/polymer composites have a cost advantage over all other CPCs. For EMI shielding, stainless steel fibres and metal coated fibers are the preferred fillers, however CPCs made of those fibers are not the dominant EMI shielding materials. Metal coated and polymer plated polymers are the most widely used EMI shielding options. The limited use of CPCs in the EMI shielding market is because the high filler loading required to formulate a composite with an adequate level of shielding remarkably increases the composite price. In order to increase the competitiveness of CPCs, percolation threshold should be minimized as much as possible and composites with high EMI shielding capabilities at low filler loading should be formulated because all conductive fillers are expensive compared to polymers. In this thesis, two different methodologies to reduce percolation threshold in CPCs have been successfully developed and a CPC with exceptional EMI shielding capability has been formulated using copper nanowires as conductive filler. The first percolation threshold reduction technique is based on the selective localization of CB at the interface of immiscible polymer blend. The technique requires adding a copolymer that prefers the blend's interface and for which CB nanoparticles has the highest affinity. The second method is based on producing a CPC powder and then using this powder as a conductive filler to produce composite by dry mixing with pure polymer powder followed by compression molding. The EMI shielding material was developed using copper nanowires. CuNW/Polystyrene composites exhibit EMI shielding effectiveness exceeding that of metal microfillers and carbon nanotube/polymer composites and approaching that of coating techniques have been formulated by solution processing and dry mixing.

Asymmetric Epoxidation: A Twinned Laboratory and Molecular Modeling Experiment for Upper-Level Organic Chemistry Students

ERIC Educational Resources Information Center

Hii, King Kuok; Rzepa, Henry S.; Smith, Edward H.

2015-01-01

The coupling of a student experiment involving the preparation and use of a catalyst for the asymmetric epoxidation of an alkene with computational simulations of various properties of the resulting epoxide is set out in the form of a software toolbox from which students select appropriate components. At the core of these are the computational…

Synthesis of water-soluble multidentate aminoalcohol β-cyclodextrin derivatives via epoxide opening.

PubMed

Martina, K; Caporaso, M; Tagliapietra, S; Heropoulos, G; Rosati, O; Cravotto, G

2011-12-13

New highly soluble β-aminoalcohol β-cyclodextrin (β-CD) derivatives have been synthesized via nucleophilic epoxide opening reactions with mono-6-amino mono-6-deoxy-permethyl-β-CD and mono-6-amino mono-6-deoxy-β-CD. The binding properties of the β-CD were enhanced by linking aminoalcohol subunits which caused its solubility to improve markedly. The reaction conditions were optimised using microwave irradiation giving moderate-to-good yields with a series of epoxides. A regioselective epoxide opening reaction was observed in the reaction with styrene oxide while the stereoselectivity was strictly dependent on substrate structure. Copyright © 2011 Elsevier Ltd. All rights reserved.

Methods of producing epoxides from alkenes using a two-component catalyst system

DOEpatents

Kung, Mayfair C.; Kung, Harold H.; Jiang, Jian

2013-07-09

Methods for the epoxidation of alkenes are provided. The methods include the steps of exposing the alkene to a two-component catalyst system in an aqueous solution in the presence of carbon monoxide and molecular oxygen under conditions in which the alkene is epoxidized. The two-component catalyst system comprises a first catalyst that generates peroxides or peroxy intermediates during oxidation of CO with molecular oxygen and a second catalyst that catalyzes the epoxidation of the alkene using the peroxides or peroxy intermediates. A catalyst system composed of particles of suspended gold and titanium silicalite is one example of a suitable two-component catalyst system.

Effect of epoxidation level on thermal properties and ionic conductivity of epoxidized natural rubber solid polymer nanocomposite electrolytes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Harun, Fatin; Chan, Chin Han; Winie, Tan

Effect of epoxide content on the thermal and conductivity properties of epoxidized natural rubber (ENR) solid polymer nanocomposite electrolytes was investigated. Commercial available epoxidized natural rubber having 25 (ENR25) and 50 mole% (ENR50) epoxide, respectively were incorporated with lithium perchlorate (LiClO{sub 4}) salt and titanium dioxide (TiO{sub 2}) nanofiller via solution casting method. The solid polymer nanocomposite electrolytes were characterized by differential scanning calorimetry (DSC) and impedance spectroscopy (IS) for their thermal properties and conductivity, respectively. It was evident that introduction of LiClO{sub 4} causes a greater increase in glass transition temperature (T{sub g}) and ionic conductivity of ENR50 asmore » compared to ENR25. Upon addition of TiO{sub 2} in ENR/LiClO{sub 4} system, a remarkable T{sub g} elevation was observed for both ENRs where ENR50 reveals a more pronounced changes. It is interesting to note that they exhibit different phenomenon in ionic conductivity with TiO{sub 2} loading where ENR25 shows enhancement of conductivity while ENR50 shows declination.« less

Occurrence of neoxanthin and lutein epoxide cycle in parasitic Cuscuta species.

PubMed

Kruk, Jerzy; Szymańska, Renata

2008-01-01

In the present study, xanthophyll composition of eight parasitic Cuscuta species under different light conditions was investigated. Neoxanthin was not detected in four of the eight species examined, while in others it occurred at the level of several percent of total xanthophylls. In C. gronovii and C. lupuliformis it was additionally found that the neoxanthin content was considerably stimulated by strong light. In dark-adapted plants, lutein epoxide level amounted to 10-22% of total xanthophylls in only three species, the highest being for C. lupuliformis, while in others it was below 3%, indicating that the lutein epoxide cycle is limited to only certain Cuscuta species. The obtained data also indicate that the presence of the lutein epoxide cycle and of neoxanthin is independent and variable among the Cuscuta species. The xanthophyll cycle carotenoids violaxanthin, antheraxanthin and zeaxanthin were identified in all the examined species and occurred at the level found in other higher plants. The xanthophyll and lutein epoxide cycle pigments showed typical response to high light stress. The obtained results also suggest that the ability of higher plants to synthesize lutein epoxide probably does not depend on the substrate specificity of zeaxanthin epoxidase but on the availability of lutein for the enzyme.

Covalent Heterogenization of a Discrete Mn(II) Bis-Phen Complex by a Metal-Template/Metal-Exchange Method: An Epoxidation Catalyst with Enhanced Reactivity

PubMed Central

Terry, Tracy J.; Stack, T. Daniel P.

2009-01-01

Considerable attention has been devoted to the immobilization of discrete epoxidation catalysts onto solid supports due to the possible benefits of site isolation such as increased catalyst stability, catalyst recycling, and product separation. A synthetic metal-template/metal-exchange method to imprint a covalently attached bis-1,10-phenanthroline coordination environment onto high-surface area, mesoporous SBA-15 silica is reported herein along with the epoxidation reactivity once reloaded with manganese. Comparisons of this imprinted material with material synthesized by random grafting of the ligand show that the template method creates more reproducible, solution-like bis-1,10-phenanthroline coordination at a variety of ligand loadings. Olefin epoxidation with peracetic acid shows the imprinted manganese catalysts have improved product selectivity for epoxides, greater substrate scope, more efficient use of oxidant, and higher reactivity than their homogeneous or grafted analogues independent of ligand loading. The randomly grafted manganese catalysts, however, show reactivity that varies with ligand loading while the homogeneous analogue degrades trisubstituted olefins and produces trans-epoxide products from cis-olefins. Efficient recycling behavior of the templated catalysts is also possible. PMID:18351763

Förster resonance energy transfer competitive displacement assay for human soluble epoxide hydrolase

PubMed Central

Lee, Kin Sing Stephen; Morisseau, Christophe; Yang, Jun; Wang, Peng; Hwang, Sung Hee; Hammock, Bruce D.

2013-01-01

The soluble epoxide hydrolase (sEH), responsible for the hydrolysis of various fatty acid epoxides to their corresponding 1,2-diols, is becoming an attractive pharmaceutical target. These fatty acid epoxides, particularly epoxyeicosatrienoic acids (EETs), play an important role in human homeostatic and inflammation processes. Therefore, inhibition of human sEH, which stabilizes EETs in vivo, brings several beneficial effects to human health. Although there are several catalytic assays available to determine the potency of sEH inhibitors, measuring the in vitro inhibition constant (Ki) for these inhibitors using catalytic assay is laborious. In addition, koff, which has been recently suggested to correlate better with the in vivo potency of inhibitors, has never been measured for sEH inhibitors. To better measure the potency of sEH inhibitors, a reporting ligand, 1-(adamantan-1-yl)-3-(1-(2-(7-hydroxy-2-oxo-2H-chromen-4-yl)acetyl) piperidin-4-yl)urea (ACPU), was designed and synthesized. With ACPU, we have developed a Förster resonance energy transfer (FRET)-based competitive displacement assay using intrinsic tryptophan fluorescence from sEH. In addition, the resulting assay allows us to measure the Ki values of very potent compounds to the picomolar level and to obtain relative koff values of the inhibitors. This assay provides additional data to evaluate the potency of sEH inhibitors. PMID:23219719

Enzymatic catalysis of anti-Baldwin ring closure in polyether biosynthesis

PubMed Central

Hotta, Kinya; Chen, Xi; Paton, Robert S.; Minami, Atsushi; Li, Hao; Swaminathan, Kunchithapadam; Mathews, Irimpan I.; Watanabe, Kenji; Oikawa, Hideaki; Houk, Kendall N.; Kim, Chu-Young

2012-01-01

Polycyclic polyether natural products have fascinated chemists and biologists alike owing to their useful biological activity, highly complex structure and intriguing biosynthetic mechanisms. Following the original proposal for the polyepoxide origin of lasalocid and isolasalocid1 and the experimental determination of the origins of the oxygen and carbon atoms of both lasalocid and monensin, a unified stereochemical model for the biosynthesis of polyether ionophore antibiotics was proposed2. The model was based on a cascade of nucleophilic ring closures of postulated polyepoxide substrates generated by stereospecific oxidation of all-trans polyene polyketide intermediates2. Shortly thereafter, a related model was proposed for the biogenesis of marine ladder toxins, involving a series of nominally disfavoured anti-Baldwin, endo-tet epoxide-ring-opening reactions3–5. Recently, we identified Lsd19 from the Streptomyces lasaliensis gene cluster as the epoxide hydrolase responsible for the epoxide-opening cyclization of bisepoxyprelasalocid A6 to form lasalocid A7,8. Here we report the X-ray crystal structure of Lsd19 in complex with its substrate and product analogue9 to provide the first atomic structure—to our knowledge—of a natural enzyme capable of catalysing the disfavoured epoxide-opening cyclic ether formation. On the basis of our structural and computational studies, we propose a general mechanism for the enzymatic catalysis of polyether natural product biosynthesis. PMID:22388816

Brazilian Consensus Recommendation on the Use of Polymethylmethacrylate Filler in Facial and Corporal Aesthetics.

PubMed

Blanco Souza, Túlio Armanini; Colomé, Letícia Marques; Bender, Eduardo André; Lemperle, Gottfriede

2018-06-05

Considering that aesthetic benefits can be obtained with the use of permanent filling materials, this work focuses on the development of a consensus regarding the facial and corporal use of polymethylmethacrylate (PMMA) filler in Brazil. A questionnaire regarding PMMA treatment, which included items on the main indication, application site, volume of product applied, criteria for selection of the material, complications, contraindications, and individual professional experience, was distributed to the Expert Group members. In addition, the responses were summarized, constituting the starting point for the debate regarding the use of PMMA-based fillers on The First Brazilian PMMA Symposium to create a guideline to be followed in PMMA facial and corporal treatments. This survey involved 87,371 cases. PMMA treatment is recommended for restorative and aesthetic purposes in facial and corporal cases, particularly for facial balance. PMMA 30% filler is recommended in specific facial sites (nose, mentum, mandible angle, zygomatic arc, and malar). PMMA filler is contraindicated in other sites (lips) regardless of concentration. With regard to facial treatment, the juxtaperiostal is the application plane most recommended. For PMMA corporal application, intramuscular is the application plane most indicated, while intradermal and justadermal planes are contraindicated. The submuscular plane application is relative to PMMA filler concentration. The experts also inquired regarding the amount of PMMA recommended in each corporal site (50 mL in the calf, 100-150 mL in the gluteal region). These recommendations provide a guideline for physicians, supporting them to perform safe and efficacious treatment with PMMA fillers. This journal requires that authors assign a level of evidence to each article. For a full description of these Evidence-Based Medicine ratings, please refer to Table of Contents or the online Instructions to Authors www.springer.com/00266 .

Anti-inflammatory Effects of Omega-3 Polyunsaturated Fatty Acids and Soluble Epoxide Hydrolase Inhibitors in Angiotensin-II Dependent Hypertension

PubMed Central

Ulu, Arzu; Harris, Todd R; Morisseau, Christophe; Miyabe, Christina; Inoue, Hiromi; Schuster, Gertrud; Dong, Hua; Iosif, Ana-Maria; Liu, Jun-Yan; Weiss, Robert H; Chiamvimonvat, Nipavan; Imig, John D; Hammock, Bruce D

2013-01-01

The mechanisms underlying the anti-inflammatory and anti-hypertensive effects of long chain ω-3 polyunsaturated fatty acids (PUFAs) are still unclear. The epoxides of an ω-6 fatty acid, arachidonic acid (epoxyeicosatrienoic acids; EETs) also exhibit anti-hypertensive and anti-inflammatory effects. Thus, we hypothesized that the major ω-3 PUFAs including eicosapentaenoic acid (EPA) and docosahexaenoic acid (DHA) may lower blood pressure and attenuate renal markers of inflammation through their epoxide metabolites. Here, we supplemented mice with an ω-3 rich diet for three weeks in a murine model of angiotensin-II dependent hypertension. Also, since EPA and DHA epoxides are metabolized by soluble epoxide hydrolase (sEH), we tested the combination of a sEH inhibitor and the ω-3 rich diet. Our results show that ω-3 rich diet in combination with the sEH inhibitor lowered Ang-II increased blood pressure, further increased renal levels of EPA and DHA epoxides, reduced renal markers of inflammation (i.e. prostaglandins and MCP-1), down-regulated an epithelial sodium channel and up-regulated Angiotensin converting enzyme-2 message (ACE-2) and significantly modulated cyclooxygenase and lipoxygenase metabolic pathways. Overall, our findings suggest that epoxides of the ω-3 PUFAs contribute to lowering SBP and attenuating inflammation in part by reduced prostaglandins and MCP-1 and by up-regulation of ACE-2 in angiotensin-II dependent hypertension. PMID:23676336

The oxidation of copper catalysts during ethylene epoxidation.

PubMed

Greiner, M T; Jones, T E; Johnson, B E; Rocha, T C R; Wang, Z J; Armbrüster, M; Willinger, M; Knop-Gericke, A; Schlögl, R

2015-10-14

The oxidation of copper catalysts during ethylene epoxidation was characterized using in situ photoemission spectroscopy and electron microscopy. Gas chromatography, proton-transfer reaction mass spectrometry and electron-ionization mass spectrometry were used to characterize the catalytic properties of the oxidized copper. We find that copper corrodes during epoxidation in a 1 : 1 mixture of oxygen and ethylene. The catalyst corrosion passes through several stages, beginning with the formation of an O-terminated surface, followed by the formation of Cu2O scale and eventually a CuO scale. The oxidized catalyst exhibits measurable activity for ethylene epoxidation, but with a low selectivity of <3%. Tests on pure Cu2O and CuO powders confirm that the oxides intrinsically exhibit partial-oxidation activity. Cu2O was found to form acetaldehyde and ethylene epoxide in roughly equal amounts (1.0% and 1.2% respectively), while CuO was found to form much less ethyl aldehyde than ethylene epoxide (0.1% and 1.0%, respectively). Metallic copper catalysts were examined in extreme dilute-O2 epoxidation conditions to try and keep the catalyst from oxidizing during the reaction. It was found that in feed of 1 part O2 to 2500 parts C2H4 (PO2 = 1.2 × 10(-4) mbar) the copper surface becomes O-terminated. The O-terminated surface was found to exhibit partial-oxidation selectivity similar to that of Cu2O. With increasing O2 concentration (>8/2500) Cu2O forms and eventually covers the surface.

Exploring the synthesis and characterization of nanoenergetic materials from sol-gel chemistry

NASA Astrophysics Data System (ADS)

Walker, Jeremy D.

Nanoenergetic composite materials have been synthesized by a sol-gel chemical process where the addition of a weak base molecule induces the gelation of a hydrated metal salt solution. A proposed 'proton scavenging' mechanism, where a weak base molecule extracts a proton from the coordination sphere of the hydrated iron (III) complex in the gelation process to form iron (III) oxide/hydroxide, FeIIIxOyHz, has been confirmed for the weak base propylene oxide (PO), a 1,2 epoxide, as well as for the weak bases tetrahydrofuran (THF), a 1,4 epoxide, and pyridine, a heterocyclic nitrogen-containing compound. Gelation mechanisms for the formation of FeIIIxOyHz from THF and pyridine have been presented and confirmed through pH, XPS, and IR studies. THF follows a similar mechanism as PO, where the epoxide extracts a proton from the coordination sphere of the hydrated iron complex forming a protonated epoxide, which then undergoes irreversible ring-opening after reaction with a nucleophile in solution. Pyridine also extracts a proton from the hydrated metal complex, however, the stable six-membered molecule has low associated ring strain and does not endure ring-opening. Energetic properties for the Fe2O3/Al and RuO 2/Al sol-gel synthesized systems are also presented. Sol-gel chemistry synthesizes x-ray amorphous oxide matrices which contain substantial quantities of residual water and organic species. The iron (III) matrix, formed from the addition of a weak base epoxide molecule to a hydrated iron (III) nitrate solution, consists of stoichiometric Fe2O3, FeO(OH), and Fe(OH)3 and can only definitely be described as of Fe IIIxOyHz. XPS characterization of the metal oxide matrix synthesized from the addition of the weak base propylene oxide to a hydrated ruthenium (III) chloride solution corresponds to that of hydrous ruthenium (IV) oxide. Fe2O3/Al energetic systems were synthesized from the epoxides PO, trimethylene oxide (TMO) and 3,3 dimethyl oxetane (DMO). Energetic systems formed from each epoxide were each synthesized with different components, including: varying concentrations of nano-scale Al, micron Al, and carbon nanotubes. Surface area analysis of the synthesized matrices shows a direct correlation between the surface area of the iron (III) oxide matrix and the quantified exothermic heat of reaction of the energetic material due to the magnitude of the interfacial surface area contact between the iron (III) oxide matrix and the aluminum particles. The Fe2O3(PO)/Al systems possess the highest heat of reaction values due to the oxide surface area available for contact with the aluminum particles. Also, within systems, 1:1 Fe:nano Al samples possess the highest heat of reaction. Samples with nano-scale Al particles start reaction at 430°C, before the melting point of Al, whereas samples containing micron-Al do not react until ˜800°C, after the melting point of Al. The RuO2/Al energetic systems behave differently dependent on the atmosphere the sample is heated. Heating the RuO2/Al samples in an inert atmosphere results in the complete reduction of the ruthenium oxide matrix to Ru(0) before reaction with the aluminum particles. This results in the exothermic formation of RuxAly intermetallics, with the stoichiometry dependent on the initial Ru:Al concentration. However, heating the samples in an oxygen-rich atmosphere results in an exothermic reaction between RuO2 and Al. Post-reaction analysis of these samples reveals the sole existence of ruthenium (IV) oxide as the exothermic reaction vaporizes the aluminum particles.

Tailoring of physical properties in highly filled experimental nanohybrid resin composites.

PubMed

Pick, Bárbara; Pelka, Matthias; Belli, Renan; Braga, Roberto R; Lohbauer, Ulrich

2011-07-01

To assess the elastic modulus (EM), volumetric shrinkage (VS), and polymerization shrinkage stress (PSS) of experimental highly filled nanohybrid composites as a function of matrix composition, filler distribution, and density. One regular viscosity nanohybrid composite (Grandio, VOCO, Germany) and one flowable nanohybrid composite (Grandio Flow, VOCO) were tested as references along with six highly filled experimental nanohybrid composites (four Bis-GMA-based, one UDMA-based, and one Ormocer®-based). The experimental composites varied in filler size and density. EM values were obtained from the "three-point bending" load-displacement curve. VS was calculated with Archimedes' buoyancy principle. PSS was determined in 1-mm thick specimens placed between two (poly)methyl methacrylate rods (Ø=6mm) attached to an universal testing machine. Data were analyzed using oneway ANOVA, Tukey's test (α=0.05), and linear regression analyses. The flowable composite exhibited the highest VS and PSS but lowest EM. The PSS was significantly lower with Ormocer. The EM was significantly higher among experimental composites with highest filler levels. No significant differences were found between all other experimental composites regarding VS and PSS. Filler density and size did not influence EM, VS, or PSS. Neither the filler configuration nor matrix composition in the investigated materials significantly influenced composite shrinkage and mechanical properties. The highest filled experimental composite seemed to increase EM by keeping VS and PSS low; however, matrix composition seemed to be the determinant factor for shrinkage and stress development. The Ormocer, with reduced PSS, deserves further investigation. Filler size and density did not influence the tested parameters. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Structure-Composition-Property Relationships in Polymeric Amorphous Calcium Phosphate-Based Dental Composites †

PubMed Central

O’Donnell, Justin N.R.; Schumacher, Gary E.; Antonucci, Joseph M.; Skrtic, Drago

2009-01-01

Our studies of amorphous calcium phosphate (ACP)-based materials over the last decade have yielded bioactive polymeric composites capable of protecting teeth from demineralization or even regenerating lost tooth mineral. The anti-cariogenic/re-mineralizing potential of these ACP composites originates from their propensity, when exposed to the oral environment, to release in a sustained manner sufficient levels of mineral-forming calcium and phosphate ions to promote formation of stable apatitic tooth mineral. However, the less than optimal ACP filler/resin matrix cohesion, excessive polymerization shrinkage and water sorption of these experimental materials can adversely affect their physicochemical and mechanical properties, and, ultimately, limit their lifespan. This study demonstrates the effects of chemical structure and composition of the methacrylate monomers used to form the matrix phase of composites on degree of vinyl conversion (DVC) and water sorption of both copolymers and composites and the release of mineral ions from the composites. Modification of ACP surface via introducing cations and/or polymers ab initio during filler synthesis failed to yield mechanically improved composites. However, moderate improvement in composite’s mechanical stability without compromising its remineralization potential was achieved by silanization and/or milling of ACP filler. Using ethoxylated bisphenol A dimethacrylate or urethane dimethacrylate as base monomers and adding moderate amounts of hydrophilic 2-hydroxyethyl methacrylate or its isomer ethyl-α-hydroxymethacrylate appears to be a promising route to maximize the remineralizing ability of the filler while maintaining high DVC. Exploration of the structure/composition/property relationships of ACP fillers and polymer matrices is complex but essential for achieving a better understanding of the fundamental mechanisms that govern dissolution/re-precipitation of bioactive ACP fillers, and, ultimately, the suitability of the composites for clinical evaluation. PMID:21966588

Development of brazing process for W-EUROFER joints using Cu-based fillers

NASA Astrophysics Data System (ADS)

de Prado, J.; Sánchez, M.; Ureña, A.

2016-02-01

A successful joint between W and EUROFER using high temperature brazing technique has been achieved for structural application in future fusion power plants. Cu-based powder alloy mixed with a polymeric binder has been used as filler. Microstructural analysis of the joints revealed that the joint consisted mainly of primary phases and acicular structures in a Cu matrix. Interaction between EUROFER and filler took place at the interface giving rise to several Cu-Ti-Fe rich layers. A loss of hardness at the EUROFER substrate close to the joint due to a diffusion phenomenon during brazing cycle was measured; however, the joints had an adequate shear strength value.

40 CFR 63.1427 - Process vent requirements for processes using extended cookout as an epoxide emission reduction...

Code of Federal Regulations, 2011 CFR

2011-07-01

... epoxides, and that are using ECO as a control technique to reduce epoxide emissions in order to comply with... provisions of this section. The owner or operator that is using ECO in order to comply with the emission... used to further reduce the HAP emissions from a process vent already controlled by ECO, then the owner...

40 CFR 63.1427 - Process vent requirements for processes using extended cookout as an epoxide emission reduction...

Code of Federal Regulations, 2010 CFR

2010-07-01

... obtaining the liquid sample, along with the test method used to determine the epoxide concentration. This... pressures, the owner or operator shall determine the time when the pressure has fallen to half its total pressure by using Equation 13: ER08MY00.008 Where: Phalf1 = Half the total pressure of the epoxide for...

Fracture Toughness and Elastic Modulus of Epoxy-Based Nanocomposites with Dopamine-Modified Nano-Fillers

PubMed Central

Koh, Kwang Liang; Ji, Xianbai; Lu, Xuehong; Lau, Soo Khim; Chen, Zhong

2017-01-01

This paper examines the effect of surface treatment and filler shape factor on the fracture toughness and elastic modulus of epoxy-based nanocomposite. Two forms of nanofillers, polydopamine-coated montmorillonite clay (D-clay) and polydopamine-coated carbon nanofibres (D-CNF) were investigated. It was found that Young’s modulus increases with increasing D-clay and D-CNF loading. However, the fracture toughness decreases with increased D-clay loading but increases with increased D-CNF loading. Explanations have been provided with the aid of fractographic analysis using electron microscope observations of the crack-filler interactions. Fractographic analysis suggests that although polydopamine provides a strong adhesion between the fillers and the matrix, leading to enhanced elastic stiffness, the enhancement prohibits energy release via secondary cracking, resulting in a decrease in fracture toughness. In contrast, 1D fibre is effective in increasing the energy dissipation during fracture through crack deflection, fibre debonding, fibre break, and pull-out. PMID:28773136

Heterogeneous epoxide carbonylation by cooperative ion-pair catalysis in Co(CO) 4 –-incorporated Cr-MIL-101

DOE Office of Scientific and Technical Information (OSTI.GOV)

Park, Hoyoung D.; Dinca, Mircea; Roman-Leshkov, Yuriy

Here, despite the commercial desirability of epoxide carbonylation to β-lactones, the reliance of this process on homogeneous catalysts makes its industrial application challenging. Here we report the preparation and use of a Co(CO) 4 –-incorporated Cr-MIL-101 (Co(CO) 4cCr-MIL-101, Cr-MIL-101 = Cr 3O(BDC) 3F, H2BDC = 1,4-benzenedicarboxylic acid) heterogeneous catalyst for the ring-expansion carbonylation of epoxides, whose activity, selectivity, and substrate scope are on par with those of the reported homogeneous catalysts. We ascribe the observed performance to the unique cooperativity between the postsynthetically introduced Co(CO) 4 – and the site-isolated Lewis acidic Cr(III) centers in the metal–organic framework (MOF). Themore » heterogeneous nature of Co(CO) 4cCr-MIL-101 allows the first demonstration of gas-phase continuous-flow production of β-lactones from epoxides, attesting to the potential applicability of the heterogeneous epoxide carbonylation strategy.« less

Heterogeneous epoxide carbonylation by cooperative ion-pair catalysis in Co(CO) 4 –-incorporated Cr-MIL-101

DOE PAGES

Park, Hoyoung D.; Dinca, Mircea; Roman-Leshkov, Yuriy

2017-03-21

Here, despite the commercial desirability of epoxide carbonylation to β-lactones, the reliance of this process on homogeneous catalysts makes its industrial application challenging. Here we report the preparation and use of a Co(CO) 4 –-incorporated Cr-MIL-101 (Co(CO) 4cCr-MIL-101, Cr-MIL-101 = Cr 3O(BDC) 3F, H2BDC = 1,4-benzenedicarboxylic acid) heterogeneous catalyst for the ring-expansion carbonylation of epoxides, whose activity, selectivity, and substrate scope are on par with those of the reported homogeneous catalysts. We ascribe the observed performance to the unique cooperativity between the postsynthetically introduced Co(CO) 4 – and the site-isolated Lewis acidic Cr(III) centers in the metal–organic framework (MOF). Themore » heterogeneous nature of Co(CO) 4cCr-MIL-101 allows the first demonstration of gas-phase continuous-flow production of β-lactones from epoxides, attesting to the potential applicability of the heterogeneous epoxide carbonylation strategy.« less

Mechanistic Basis for High Reactivity of (salen)Co–OTs in the Hydrolytic Kinetic Resolution of Terminal Epoxides

PubMed Central

Nielsen, Lars P. C.; Zuend, Stephan J.; Ford, David D.; Jacobsen, Eric N.

2012-01-01

The (salen)Co(III)-catalyzed hydrolytic kinetic resolution (HKR) of terminal epoxides is a bimetallic process with a rate controlled by partitioning between a nucleophilic (salen)Co–OH catalyst and a Lewis acidic (salen)Co–X catalyst. The commonly used (salen)Co–OAc and (salen)Co–Cl precatalysts undergo complete and irreversible counterion addition to epoxide during the course of the epoxide hydrolysis reaction, resulting in quantitative formation of weakly Lewis acidic (salen)Co–OH, and severely diminished reaction rates in the late stages of HKR reactions. In contrast, (salen)Co–OTs maintains high reactivity over the entire course of HKR reactions. We describe here an investigation of catalyst partitioning with different (salen)Co–X precatalysts, and demonstrate that counterion addition to epoxide is reversible in the case of the (salen)Co–OTs. This reversible counterion addition results in stable partitioning between nucleophilic and Lewis acidic catalyst species, allowing highly efficient catalysis throughout the course of the HKR reaction. PMID:22292515

Mechanistic basis for high reactivity of (salen)Co-OTs in the hydrolytic kinetic resolution of terminal epoxides.

PubMed

Nielsen, Lars P C; Zuend, Stephan J; Ford, David D; Jacobsen, Eric N

2012-03-02

The (salen)Co(III)-catalyzed hydrolytic kinetic resolution (HKR) of terminal epoxides is a bimetallic process with a rate controlled by partitioning between a nucleophilic (salen)Co-OH catalyst and a Lewis acidic (salen)Co-X catalyst. The commonly used (salen)Co-OAc and (salen)Co-Cl precatalysts undergo complete and irreversible counterion addition to epoxide during the course of the epoxide hydrolysis reaction, resulting in quantitative formation of weakly Lewis acidic (salen)Co-OH and severely diminished reaction rates in the late stages of HKR reactions. In contrast, (salen)Co-OTs maintains high reactivity over the entire course of HKR reactions. We describe here an investigation of catalyst partitioning with different (salen)Co-X precatalysts and demonstrate that counterion addition to epoxide is reversible in the case of the (salen)Co-OTs. This reversible counterion addition results in stable partitioning between nucleophilic and Lewis acidic catalyst species, allowing highly efficient catalysis throughout the course of the HKR reaction.

Succinic anhydrides from epoxides

DOEpatents

Coates, Geoffrey W.; Rowley, John M.

2013-07-09

Catalysts and methods for the double carbonylation of epoxides are disclosed. Each epoxide molecule reacts with two molecules of carbon monoxide to produce a succinic anhydride. The reaction is facilitated by catalysts combining a Lewis acidic species with a transition metal carbonyl complex. The double carbonylation is achieved in single process by using reaction conditions under which both carbonylation reactions occur without the necessity of isolating or purifying the product of the first carbonylation.

Succinic anhydrides from epoxides

DOE Office of Scientific and Technical Information (OSTI.GOV)

Coates, Geoffrey W.; Rowley, John M.

2016-06-28

Catalysts and methods for the double carbonylation of epoxides are disclosed. Each epoxide molecule reacts with two molecules of carbon monoxide to produce a succinic anhydride. The reaction is facilitated by catalysts combining a Lewis acidic species with a transition metal carbonyl complex. The double carbonylation is achieved in single process by using reaction conditions under which both carbonylation reactions occur without the necessity of isolating or purifying the product of the first carbonylation.

cis-Stilbene and (1 alpha,2 beta,3 alpha)-(2-ethenyl-3-methoxycyclopropyl)benzene as mechanistic probes in the Mn(III)(salen)-catalyzed epoxidation: influence of the oxygen source and the counterion on the diastereoselectivity of the competitive concerted and radical-type oxygen transfer.

PubMed

Adam, Waldemar; Roschmann, Konrad J; Saha-Möller, Chantu R; Seebach, Dieter

2002-05-08

cis-Stilbene (1) has been epoxidized by a set of diverse oxygen donors [OxD], catalyzed by the Mn(III)(salen)X complexes 3 (X = Cl, PF(6)), to afford a mixture of cis- and trans-epoxides 2. The cis/trans ratios range from 29:71 (extensive isomerization) to 92:8, which depends both on the oxygen source [OxD] and on the counterion X of the catalyst. When (1 alpha,2 beta,3 alpha)-(2-ethenyl-3-methoxycyclopropyl)-benzene (4) is used as substrate, a mechanistic probe which differentiates between radical and cationic intermediates, no cationic ring-opening products are found in this epoxidation reaction; thus, isomerized epoxide product arises from intermediary radicals. The dependence of the diastereoselectivity on the oxygen source is rationalized in terms of a bifurcation step in the catalytic cycle, in which concerted Lewis-acid-activated oxygen transfer competes with stepwise epoxidation by the established Mn(V)(oxo) species. The experimental counterion effect is attributed to the computationally assessed ligand-dependent reaction profiles and stereoselectivities of the singlet, triplet, and quintet spin states available to the manganese species.

Anti-Leishmania and cytotoxic activities of perillaldehyde epoxide synthetic positional isomers.

PubMed

Keesen, Tatjana Souza Lima; da Silva, Larisse Virgolino; da Câmara Rocha, Juliana; Andrade, Luciana Nalone; Lima, Tamires Cardoso; de Sousa, Damião Pergentino

2018-03-13

Leishmaniasis belongs to a complex of zoonotic disease caused by protozoa of the genus Leishmania and is considered a major public health problem. Several essential oil chemical components have inhibitory effect against protozoa, including Leishmania donovani. Thus, the aim of this study was to evaluate for the first time the anti-Leishmania activity of two p-menthane monoterpene isomers (EPER-1: perillaldehyde 1,2-epoxide and EPER-2: perillaldehyde 8,9-epoxide) against L. donovani promastigotes as well as evaluating cytotoxic effect on mononuclear peripheral blood cells. Results of anti-Leishmania assay revealed that EPER-2 (IC 50  = 3.8 μg.mL -1 ) was 16-fold more potent than its isomer EPER-1 (IC 50  = 64.6 μg.mL -1 ). In contrast to PBMC cells, EPER-2 was not cytotoxic (IC 50  > 400 μg.mL -1 ) when compared to positive control. These data suggest that the disposition of epoxide group into the p-menthane skeleton affects the anti-Leishmania activity, being that the presence of the exocyclic epoxide group considerably increased potency. Thus, it was possible to observe that the location of the epoxide group into the p-menthane skeleton resulted in different potencies.

Characteristics comparison of weld metal zones welded to cast and forged steels for piston crown material

NASA Astrophysics Data System (ADS)

Moon, Kyung-Man; Kim, Yun-Hae; Lee, Myeong-Hoon; Baek, Tae-Sil

2015-03-01

An optimum repair welding for the piston crown which is one of the engine parts exposed to the combustion chamber is considered to be very important to prolong the engine lifetime from an economical point of view. In this study, two types of filler metals such as 1.25Cr-0.5Mo, 0.5Mo were welded with SMAW method and the other two types of filler metals such as Inconel 625 and 718 were welded with GTAW method, respectively, and the used base metals were the cast and forged steels of the piston crown material. The weld metal zones welded with Inconel 625 and 718 filler metals exhibited higher corrosion resistance compared to 1.25Cr-0.5Mo and 0.5Mo filler metals. In particular, the weld metal zone welded with Inconel 718 and 0.5Mo, filler metals indicated the best and worst corrosion resistance, respectively. Consequently, it is suggested that the corrosion resistance of the weld metal zone surely depends on the chemical components of each filler metal and welding method irrespective of the types of piston crown material.

Stilbene epoxidation and detoxification in a Photorhabdus luminescens-nematode symbiosis

PubMed Central

Park, Hyun Bong; Sampathkumar, Parthasarathy; Perez, Corey E.; Lee, Joon Ha; Tran, Jeannie; Bonanno, Jeffrey B.; Hallem, Elissa A.; Almo, Steven C.; Crawford, Jason M.

2017-01-01

Members of the gammaproteobacterial Photorhabdus genus share mutualistic relationships with Heterorhabditis nematodes, and the pairs infect a wide swath of insect larvae. Photorhabdus species produce a family of stilbenes, with two major components being 3,5-dihydroxy-4-isopropyl-trans-stilbene (compound 1) and its stilbene epoxide (compound 2). This family of molecules harbors antimicrobial and immunosuppressive activities, and its pathway is responsible for producing a nematode “food signal” involved in nematode development. However, stilbene epoxidation biosynthesis and its biological roles remain unknown. Here, we identified an orphan protein (Plu2236) from Photorhabdus luminescens that catalyzes stilbene epoxidation. Structural, mutational, and biochemical analyses confirmed the enzyme adopts a fold common to FAD-dependent monooxygenases, contains a tightly bound FAD prosthetic group, and is required for the stereoselective epoxidation of compounds 1 and 2. The epoxidase gene was dispensable in a nematode-infective juvenile recovery assay, indicating the oxidized compound is not required for the food signal. The epoxide exhibited reduced cytotoxicity toward its producer, suggesting this may be a natural route for intracellular detoxification. In an insect infection model, we also observed two stilbene-derived metabolites that were dependent on the epoxidase. NMR, computational, and chemical degradation studies established their structures as new stilbene-l-proline conjugates, prolbenes A (compound 3) and B (compound 4). The prolbenes lacked immunosuppressive and antimicrobial activities compared with their stilbene substrates, suggesting a metabolite attenuation mechanism in the animal model. Collectively, our studies provide a structural view for stereoselective stilbene epoxidation and functionalization in an invertebrate animal infection model and provide new insights into stilbene cellular detoxification. PMID:28246174

Tumor initiating activities of various derivatives of benz(a)anthracene and 7, 12-dimethyl-benz(a)anthracene in mouse skin

DOE Office of Scientific and Technical Information (OSTI.GOV)

Slaga, T.J.; Gleason, G.L.; DiGiovanni, J.

Current information indicates that polycyclic aromatic hydrocarbons (PAH) exert their toxic, mutagenic, and carcinogenic activities after they have been metabolically activated by target cells to reactive epoxides. The results obtained from IN VIVO and IN VITRO binding, mutagenicity, metabolism, and carcinogenicity studies have led to the conclusion that BP-7, 8-diol is a proximate carcinogenic metabolite of BP, and the BP-diol-epoxide is an ultimate carcinogenic metabolite of BP. Recent results concerning the strong carcinogenicity of BP-7..beta.., 8..cap alpha..-diol-9..cap alpha..,10..cap alpha..-epoxide in newborn mice and in mouse skin strongly indicate that it is the ultimate carcinogenic metabolite of BP. Since diol-epoxides maymore » be responsible for the carcinogenicity of PAH other than BP, diols and diol-epoxides as well as other derivatives of PAH were tested for skin tumor-initiation in a two-stage system of tumorigenesis. In addition, since activation of methylated PAH may involve the side-chain methyl group, the skin tumor-initiating activity of various side-chain derivatives of methylated PA were determined. In this report, the skin tumor initiation of various derivatives of a nonmethylated PAH, BA as well as a methylated PAH, DMBA are compared. The data suggest that bay region diol-epoxides may be important in BA and DMBA carcinogenicity in mice which is supportive of the theory proposed by Jerina and co-workers which predicts that diol-epoxides in the bay region are the major determinants of PAH carcinogenicity.« less

Zeaxanthin epoxidation - an in vitro approach.

PubMed

Kuczyńska, Paulina; Latowski, Dariusz; Niczyporuk, Sylvia; Olchawa-Pajor, Monika; Jahns, Peter; Gruszecki, Wiesław I; Strzałka, Kazimierz

2012-01-01

Zeaxanthin epoxidase (ZE) is an enzyme operating in the violaxanthin cycle, which is involved in photoprotective mechanisms. In this work model systems to study zeaxanthin (Zx) epoxidation were developed. Two assay systems are presented in which epoxidation of Zx was observed. In these assays two mutants of Arabidopsis thaliana which have active only one of the two xanthophyll cycle enzymes were used. The npq1 mutant possesses an active ZE and is thus able to convert Zx to violaxanthin (Vx) but the violaxanthin de-epoxidase (VDE) is inactive, so that Vx cannot be converted to Zx. The other mutant, npq2, possesses an active VDE and can convert exogenous Vx to Zx under strong light conditions but reverse reaction is not possible. The first assay containing thylakoids from npq1 and npq2 mutants of A. thaliana gave positive results and high efficiency of epoxidation reaction was observed. The amount of Zx was reduced by 25%. To optimize high efficiency of epoxidation reaction additional factors facilitating both fusion of the two types of thylakoids and incorporation of Zx to their membranes were also studied. The second kind of assay contained npq1 mutant thylakoids of A. thaliana supplemented with exogenous Zx and monogalactosyldiacylglycerol (MGDG). Experiments with different proportions of Zx and MGDG showed that their optimal ratio is 1:60. In such system, due to epoxidation, the amount of Zx was reduced by 38% of its initial level. The in vitro systems of Zx epoxidation described in this paper enable analysis some properties of the ZE without necessity of its isolation.

Application of waste bulk moulded composite (BMC) as a filler for isotactic polypropylene composites.

PubMed

Barczewski, Mateusz; Matykiewicz, Danuta; Andrzejewski, Jacek; Skórczewska, Katarzyna

2016-05-01

The aim of this study was to produce isotactic polypropylene based composites filled with waste thermosetting bulk moulded composite (BMC). The influence of BMC waste addition (5, 10, 20 wt%) on composites structure and properties was investigated. Moreover, additional studies of chemical treatment of the filler were prepared. Modification of BMC waste by calcium stearate (CaSt) powder allows to assess the possibility of the production of composites with better dispersion of the filler and more uniform properties. The mechanical, processing, and thermal properties, as well as structural investigations were examined by means of static tensile test, Dynstat impact strength test, differential scanning calorimetry (DSC), wide angle X-ray scattering (WAXS), melt flow index (MFI) and scanning electron microscopy (SEM). Developed composites with different amounts of non-reactive filler exhibited satisfactory thermal and mechanical properties. Moreover, application of the low cost modifier (CaSt) allows to obtain composites with better dispersion of the filler and improved processability.

Application of waste bulk moulded composite (BMC) as a filler for isotactic polypropylene composites

PubMed Central

Barczewski, Mateusz; Matykiewicz, Danuta; Andrzejewski, Jacek; Skórczewska, Katarzyna

2016-01-01

The aim of this study was to produce isotactic polypropylene based composites filled with waste thermosetting bulk moulded composite (BMC). The influence of BMC waste addition (5, 10, 20 wt%) on composites structure and properties was investigated. Moreover, additional studies of chemical treatment of the filler were prepared. Modification of BMC waste by calcium stearate (CaSt) powder allows to assess the possibility of the production of composites with better dispersion of the filler and more uniform properties. The mechanical, processing, and thermal properties, as well as structural investigations were examined by means of static tensile test, Dynstat impact strength test, differential scanning calorimetry (DSC), wide angle X-ray scattering (WAXS), melt flow index (MFI) and scanning electron microscopy (SEM). Developed composites with different amounts of non-reactive filler exhibited satisfactory thermal and mechanical properties. Moreover, application of the low cost modifier (CaSt) allows to obtain composites with better dispersion of the filler and improved processability. PMID:27222742

Sustainable epoxy and oxetane thermosets from photo-initiated cationic polymerization

NASA Astrophysics Data System (ADS)

Ryu, Chang

A group of sustainable materials are proposed and produced from multifunctional epoxides and oxetanes obtained from renewable sources. Monomers are photopolymerized using diaryliodonium salts designed and synthesized by our group as initiator. A detailed investigation of the network formation of epoxidized linseed oil revealed that crosslinks is markedly dependent to the thickness and viscosity of substrate. Copolymerization studies of difunctional oxetane showed that limonene dioxide was effective in increasing the reaction rates and shorten the inherent induction period, also known as kick-starting effect. Such oxetane thermoset can achieve desirable curing rates and Tg compared to petroleum based epoxy used in applications such as large scale surface coatings.

A prospective study of non-surgical primary rhinoplasty using a polymethylmethacrylate injectable implant.

PubMed

Rivkin, Alexander

2014-03-01

Nonsurgical rhinoplasty involves the use of injectable fillers to improve the contours of the nose. It has become a widely practiced procedure since this author first popularized it in 2003. The use of permanent fillers in nonsurgical rhinoplasty has not been well documented, especially in this country. To demonstrate the safety and effectiveness of a polymethylmethacrylate (PMMA)-based filler for nonsurgical rhinoplasty. Eligible subjects underwent up to three injection sessions with a commercially available PMMA product and were followed for 1 year. Efficacy was assessed according to evaluator grading of subjects and digital image analysis of standardized photographs. Nineteen subjects were enrolled and followed to conclusion. Average improvement in global score was more than one point observed on day 90 and lasting through 1 year. Eight of 10 subjects showed improvement according to digital image analysis at 1 year. Subject satisfaction was high throughout the study. Adverse events were minimal and well tolerated. Filler rhinoplasty using a PMMA-based injectable filler is safe and effective. This is the first study documenting the use of PMMA for this indication. Longer-term follow-up is needed to demonstrate persistence of improvement. © 2013 by the American Society for Dermatologic Surgery, Inc. Published by Wiley Periodicals, Inc.

A compound scaffold with uniform longitudinally oriented guidance cues and a porous sheath promotes peripheral nerve regeneration in vivo.

PubMed

Huang, Liangliang; Zhu, Lei; Shi, Xiaowei; Xia, Bing; Liu, Zhongyang; Zhu, Shu; Yang, Yafeng; Ma, Teng; Cheng, Pengzhen; Luo, Kai; Huang, Jinghui; Luo, Zhuojing

2018-03-01

Scaffolds with inner fillers that convey directional guidance cues represent promising candidates for nerve repair. However, incorrect positioning or non-uniform distribution of intraluminal fillers might result in regeneration failure. In addition, proper porosity (to enhance nutrient and oxygen exchange but prevent fibroblast infiltration) and mechanical properties (to ensure fixation and to protect regenerating axons from compression) of the outer sheath are also highly important for constructing advanced nerve scaffolds. In this study, we constructed a compound scaffold using a stage-wise strategy, including directionally freezing orientated collagen-chitosan (O-CCH) filler, electrospinning poly(ε-caprolactone) (PCL) sheaths and assembling O-CCH/PCL scaffolds. Based on scanning electron microscopy (SEM) and mechanical tests, a blend of collagen/chitosan (1:1) was selected for filler fabrication, and a wall thickness of 400 μm was selected for PCL sheath production. SEM and three-dimensional (3D) reconstruction further revealed that the O-CCH filler exhibited a uniform, longitudinally oriented microstructure (over 85% of pores were 20-50 μm in diameter). The electrospun PCL porous sheath with pore sizes of 6.5 ± 3.3 μm prevented fibroblast invasion. The PCL sheath exhibited comparable mechanical properties to commercially available nerve conduits, and the O-CCH filler showed a physiologically relevant substrate stiffness of 2.0 ± 0.4 kPa. The differential degradation time of the filler and sheath allows the O-CCH/PCL scaffold to protect regenerating axons from compression stress while providing enough space for regenerating nerves. In vitro and in vivo studies indicated that the O-CCH/PCL scaffolds could promote axonal regeneration and Schwann cell migration. More importantly, functional results indicated that the CCH/PCL compound scaffold induced comparable functional recovery to that of the autograft group at the end of the study. Our findings demonstrated that the O-CCH/PCL scaffold with uniform longitudinal guidance filler and a porous sheath exhibits favorable properties for clinical use and promotes nerve regeneration and functional recovery. The O-CCH/PCL scaffold provides a promising new path for developing an optimal therapeutic alternative for peripheral nerve reconstruction. Scaffolds with inner fillers displaying directional guidance cues represent a promising candidate for nerve repair. However, further clinical translation should pay attention to the problem of non-uniform distribution of inner fillers, the porosity and mechanical properties of the outer sheath and the morphological design facilitating operation. In this study, a stage-wise fabrication strategy was used, which made it possible to develop an O-CCH/PCL compound scaffold with a uniform longitudinally oriented inner filler and a porous outer sheath. The uniform distribution of the pores in the O-CCH/PCL scaffold provides a solution to resolve the problem of non-uniform distribution of inner fillers, which impede the clinical translation of scaffolds with longitudinal microstructured fillers, especially for aligned-fiber-based scaffolds. In vitro and in vivo studies indicated that the O-CCH/PCL scaffolds could provide topographical cues for axonal regeneration and SC migration, which were not found for random scaffolds (with random microstructure resemble sponge-based scaffolds). The electrospun porous PCL sheath of the O-CCH/PCL scaffold not only prevented fibroblast infiltration, but also satisfied the mechanical requirements for clinical use, paving the way for clinical translation. The differential degradation time of the O-CCH filler and the PCL sheath makes O-CCH/PCL scaffold able to provide long protection for regenerating axons from compression stress, but enough space for regenerating nerve. These findings highlight the possibility of developing an optimal therapeutic alternative for nerve defects using the O-CCH/PCL scaffold. Copyright © 2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Tensile properties of chrome tanned leather waste short fibre filled unsaturated polyester composite

NASA Astrophysics Data System (ADS)

Talib, Satariah; Romli, Ahmad Zafir; Saad, Siti Zaleha

2017-12-01

Waste leather from industries was commonly disposed via land filling or incineration where the oxidation of Cr III to Cr VI by oxidants (such as peroxides and hypohalide) can easily occur. Cr VI is well known as carcinogenic and mutagenic element where the excessive exposure to this element can be very harmful. As an alternative way, the leather waste from footwear industry was utilised as filler in unsaturated polyester composite (UPC). The leather waste was ground using 0.25 mm mesh size and used without any chemical treatment. The sample was fabricated via castingtechnique and the study was carried out at 1 wt%, 2 wt% and 3 wt% filler loading. The leather waste filled composites showed lower tensile strength and Young's modulus than the unfilled composite. The increasing loading amount of leather waste led to the decreased in tensile strength and Young's modulus. The tensile results was supported by the decreasing pattern of density result which indicates the increasing of void content as the filler loading increased. The results of glass transition temperature are also parallel to the tensile properties where the increasing filler loading had decreased the glass transition temperature. Based on the morphological observation on the fractured tensile sample, much severe filler agglomerations and higher amount of voids was observed at higher filler loading compared to the lower filler loading.

A DFT-Based Computational-Experimental Methodology for Synthetic Chemistry: Example of Application to the Catalytic Opening of Epoxides by Titanocene.

PubMed

Jaraíz, Martín; Enríquez, Lourdes; Pinacho, Ruth; Rubio, José E; Lesarri, Alberto; López-Pérez, José L

2017-04-07

A novel DFT-based Reaction Kinetics (DFT-RK) simulation approach, employed in combination with real-time data from reaction monitoring instrumentation (like UV-vis, FTIR, Raman, and 2D NMR benchtop spectrometers), is shown to provide a detailed methodology for the analysis and design of complex synthetic chemistry schemes. As an example, it is applied to the opening of epoxides by titanocene in THF, a catalytic system with abundant experimental data available. Through a DFT-RK analysis of real-time IR data, we have developed a comprehensive mechanistic model that opens new perspectives to understand previous experiments. Although derived specifically from the opening of epoxides, the prediction capabilities of the model, built on elementary reactions, together with its practical side (reaction kinetics simulations of real experimental conditions) make it a useful simulation tool for the design of new experiments, as well as for the conception and development of improved versions of the reagents. From the perspective of the methodology employed, because both the computational (DFT-RK) and the experimental (spectroscopic data) components can follow the time evolution of several species simultaneously, it is expected to provide a helpful tool for the study of complex systems in synthetic chemistry.

Influence of different fillers on the properties of an experimental vinyl polysiloxane.

PubMed

Meincke, Débora Könzgen; Ogliari, Aline de Oliveira; Ogliari, Fabrício Aulo

2016-01-01

The aim of the study was to evaluate the effect of the incorporation of different fillers on an experimental vinyl polysiloxane (VPS) at two different concentrations, 20% and 40%. Different fillers were added to an experimental VPS. The study was developed in two stages: (i) incorporation of fillers in different concentrations: (a) 20 wt% fillers, and (b) 40 wt%. The fillers were added to experimental VPS and mixed with a speed mixer; (ii) characterization of experimental VPS; after the base paste and catalyst paste were mixed, the experimental VPS was used to make specimens specifically for each test, which were stored at 23°C for 24 hours. The tests were designed according to the specific standardization for the analysis of tensile strength, detail reproduction, Shore A hardness, and elastic recovery. For analysis of filler size pattern, scanning electron microscopy at 1500× magnification was used. The aerosil OX-50 40% (AE), and pure aluminum hydroxide 40% (PAH) groups presented the highest tensile strength and Shore A hardness values. However, those were the only groups that did not present continuous detail reproduction of an intersection of 20 μm line. The elastic recovery was not statistically significant. The undesirable characteristics of VPS (lowest Shore A hardness and tensile strength) were observed when it was added to the composition of acrylic polymer (AP) and fiberglass (FG) in both concentrations, 20% and 40%. In groups AE and PAH, agglomerates of nanofillers were shown in SEM micrography, while the other groups presented different shapes and fillers sizes.

Mesoporous silica fillers and resin composition effect on dental composites cytocompatibility.

PubMed

Attik, Nina; Hallay, Franck; Bois, Laurence; Brioude, Arnaud; Grosgogeat, Brigitte; Colon, Pierre

2017-02-01

Many new dental composites containing mesoporous silica fillers have been developed to improve rheological properties and enhance the resin-filler interface. To investigate the correlation between the cytocompatibility of several dental composites and their composition; two aspects have been considered: presence of bisphenol A (BPA)-glycidyl methacrylate (Bis-GMA) or triethyleneglycol-dimethacrylate (TEGDMA) among the resin monomers and presence of porous particles among the filler blends. Five commercial composites with different resin matrices and mineral fillers were compared to four experimental composites designed without any BPA-based monomers or TEGDMA. Porous fillers, with or without silanation, were added in some of the experimental composites. Two reference resin matrices were also selected. Cytocompatibility with cultured primary human gingival fibroblasts was assessed by confocal laser scanning microscopy with time-lapse imaging. Fourier transform infrared spectroscopy was used to control monomer conversion rate. Conversion rates of the experimental composites ranged from 57% to 71%, a comparable ratio for dental composites. Experimental samples were better tolerated than tested commercial samples not containing TEGDMA and significantly better than those containing TEGDMA. Experimental composites with porous fillers exhibited good cytocompatibility, especially when surfaces were silanated. Cytotoxicity was associated with resin amount and especially resin nature. Composites containing porous fillers might behave as if the resin trapped into pores has no effect on toxicity. The cytotoxicity of composites with and without BPA derivatives was mainly attributed to the release of residual TEGDMA rather than the BPA derivatives. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

High temperature insulation for ceramic matrix composites

DOEpatents

Merrill, Gary B.; Morrison, Jay Alan

2001-01-01

A ceramic composition is provided to insulate ceramic matrix composites under high temperature, high heat flux environments. The composition comprises a plurality of hollow oxide-based spheres of various dimensions, a phosphate binder, and at least one oxide filler powder, whereby the phosphate binder partially fills gaps between the spheres and the filler powders. The spheres are situated in the phosphate binder and the filler powders such that each sphere is in contact with at least one other sphere. The spheres may be any combination of Mullite spheres, Alumina spheres, or stabilized Zirconia spheres. The filler powder may be any combination of Alumina, Mullite, Ceria, or Hafnia. Preferably, the phosphate binder is Aluminum Ortho-Phosphate. A method of manufacturing the ceramic insulating composition and its application to CMC substrates are also provided.

High temperature insulation for ceramic matrix composites

DOEpatents

Merrill, Gary B.; Morrison, Jay Alan

2000-01-01

A ceramic composition is provided to insulate ceramic matrix composites under high temperature, high heat flux environments. The composite comprises a plurality of hollow oxide-based spheres of varios dimentions, a phosphate binder, and at least one oxide filler powder, whereby the phosphate binder partially fills gaps between the spheres and the filler powders. The spheres are situated in the phosphate binder and the filler powders such that each sphere is in contact with at least one other sphere. The spheres may be any combination of Mullite spheres, Alumina spheres, or stabilized Zirconia spheres. The filler powder may be any combination of Alumina, Mullite, Ceria, or Hafnia. Preferably, the phosphate binder is Aluminum Ortho-Phosphate. A method of manufacturing the ceramic insulating composition and its application to CMC substates are also provided.

High temperature insulation for ceramic matrix composites

DOEpatents

Merrill, Gary B.; Morrison, Jay Alan

2004-01-13

A ceramic composition is provided to insulate ceramic matrix composites under high temperature, high heat flux environments. The composition comprises a plurality of hollow oxide-based spheres of various dimensions, a phosphate binder, and at least one oxide filler powder, whereby the phosphate binder partially fills gaps between the spheres and the filler powders. The spheres are situated in the phosphate binder and the filler powders such that each sphere is in contact with at least one other sphere. The spheres may be any combination of Mullite spheres, Alumina spheres, or stabilized Zirconia spheres. The filler powder may be any combination of Alumina, Mullite, Ceria, or Hafnia. Preferably, the phosphate binder is Aluminum Ortho-Phosphate. A method of manufacturing the ceramic insulating composition and its application to CMC substrates are also provided.

Update on botulinum toxin and dermal fillers.

PubMed

Berbos, Zachary J; Lipham, William J

2010-09-01

The art and science of facial rejuvenation is an ever-evolving field of medicine, as evidenced by the continual development of new surgical and nonsurgical treatment modalities. Over the past 10 years, the use of botulinum toxin and dermal fillers for aesthetic purposes has risen sharply. Herein, we discuss properties of several commonly used injectable products and provide basic instruction for their use toward the goal of achieving facial rejuvenation. The demand for nonsurgical injection-based facial rejuvenation products has risen enormously in recent years. Used independently or concurrently, botulinum toxin and dermal filler agents offer an affordable, minimally invasive approach to facial rejuvenation. Botulinum toxin and dermal fillers can be used to diminish facial rhytides, restore facial volume, and sculpt facial contours, thereby achieving an aesthetically pleasing, youthful facial appearance.

Chitosan nanocomposites based on distinct inorganic fillers for biomedical applications

PubMed Central

Moura, Duarte; Mano, João F.; Paiva, Maria C.; Alves, Natália M.

2016-01-01

Abstract Chitosan (CHI), a biocompatible and biodegradable polysaccharide with the ability to provide a non-protein matrix for tissue growth, is considered to be an ideal material in the biomedical field. However, the lack of good mechanical properties limits its applications. In order to overcome this drawback, CHI has been combined with different polymers and fillers, leading to a variety of chitosan-based nanocomposites. The extensive research on CHI nanocomposites as well as their main biomedical applications are reviewed in this paper. An overview of the different fillers and assembly techniques available to produce CHI nanocomposites is presented. Finally, the properties of such nanocomposites are discussed with particular focus on bone regeneration, drug delivery, wound healing and biosensing applications. PMID:27877909

Evaluation of cotton byproducts as fillers for poly(lactic acid) and low density polyethylene

USDA-ARS?s Scientific Manuscript database

Polymeric composites based on cotton burr and cottonseed bull have been prepared by melt blending and extrusion. For poly(lactic acid) (PLA) and low-density polyethylene (LDPE), addition of the fillers only slightly changed the composite’s thermal properties and significantly decreased the composite...

Hybrid composite based on poly(vinyl alcohol) and fillers from renewable resources

USDA-ARS?s Scientific Manuscript database

Hybrid composite laminates consisting of polyvinyl alcohol (PVA) as continuous phase (33% by weight) and lignocellulosic fillers, derived from sugarcane bagasse, apple and orange waste (22% by weight) were molded in a carver press in the presence of water and glycerol such as platicizers agents. Cor...

Direct synthesis of ESBO derivatives-¹⁸O labelled with dioxirane.

PubMed

La Tegola, Stefano; Annese, Cosimo; Suman, Michele; Tommasi, Immacolata; Fusco, Caterina; D'Accolti, Lucia

2013-01-01

This work addresses a new approach developed in our laboratory, consisting in the application of isolated dimethyldioxirane (DDO, 1a) labelled with ¹⁸O for synthesis of epoxidized glyceryl linoleate (Gly-LLL, 2). We expect that this work could contribute in improving analytical methods for the determination of epoxidized soybean oil (ESBO) in complex food matrices by adopting an ¹⁸O-labelled-epoxidized triacylglycerol as an internal standard.

A Bimetallic Aluminium(Salphen) Complex for the Synthesis of Cyclic Carbonates from Epoxides and Carbon Dioxide.

PubMed

Wu, Xiao; North, Michael

2017-01-10

A bimetallic aluminium(salphen) complex is reported as a sustainable, efficient and inexpensive catalyst for the synthesis of cyclic carbonates from epoxides and carbon dioxide. In the presence of this complex and tetrabutylammonium bromide, terminal and internal epoxides reacted at 50 °C and 10 bar carbon dioxide pressure to afford their corresponding cyclic carbonates in yields of 50-94 % and 30-71 % for terminal and internal cyclic carbonates, respectively. Mechanistic studies using deuterated epoxides and an analogous monometallic aluminium(salphen) chloride complex support a mechanism for catalysis by the bimetallic complex, which involves intramolecular cooperative catalysis between the two aluminium centres. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

First-principles chemical kinetic modeling of methyl trans-3-hexenoate epoxidation by HO 2

DOE PAGES

Cagnina, S.; Nicolle, Andre; de Bruin, T.; ...

2017-02-16

The design of innovative combustion processes relies on a comprehensive understanding of biodiesel oxidation kinetics. The present study aims at unraveling the reaction mechanism involved in the epoxidation of a realistic biodiesel surrogate, methyl trans-3-hexenoate, by hydroperoxy radicals using a bottom-up theoretical kinetics methodology. The obtained rate constants are in good agreement with experimental data for alkene epoxidation by HO 2. The impact of temperature and pressure on epoxidation pathways involving H-bonded and non-H-bonded conformers was assessed. As a result, the obtained rate constant was finally implemented into a state-of-the-art detailed combustion mechanism, resulting in fairly good agreement with enginemore » experiments.« less

A One-Step Route to CO2 -Based Block Copolymers by Simultaneous ROCOP of CO2 /Epoxides and RAFT Polymerization of Vinyl Monomers.

PubMed

Wang, Yong; Zhao, Yajun; Ye, Yunsheng; Peng, Haiyan; Zhou, Xingping; Xie, Xiaolin; Wang, Xianhong; Wang, Fosong

2018-03-26

The one-step synthesis of well-defined CO 2 -based diblock copolymers was achieved by simultaneous ring-opening copolymerization (ROCOP) of CO 2 /epoxides and RAFT polymerization of vinyl monomers using a trithiocarbonate compound bearing a carboxylic group (TTC-COOH) as the bifunctional chain transfer agent (CTA). The double chain-transfer effect allows for independent and precise control over the molecular weight of the two blocks and ensures narrow polydispersities of the resultant block copolymers (1.09-1.14). Notably, an unusual axial group exchange reaction between the aluminum porphyrin catalyst and TTC-COOH impedes the formation of homopolycarbonates. By taking advantage of the RAFT technique, it is able to meet the stringent demand for functionality control to well expand the application scopes of CO 2 -based polycarbonates. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Discovery of potent inhibitors of soluble epoxide hydrolase by combinatorial library design and structure-based virtual screening.

PubMed

Xing, Li; McDonald, Joseph J; Kolodziej, Steve A; Kurumbail, Ravi G; Williams, Jennifer M; Warren, Chad J; O'Neal, Janet M; Skepner, Jill E; Roberds, Steven L

2011-03-10

Structure-based virtual screening was applied to design combinatorial libraries to discover novel and potent soluble epoxide hydrolase (sEH) inhibitors. X-ray crystal structures revealed unique interactions for a benzoxazole template in addition to the conserved hydrogen bonds with the catalytic machinery of sEH. By exploitation of the favorable binding elements, two iterations of library design based on amide coupling were employed, guided principally by the docking results of the enumerated virtual products. Biological screening of the libraries demonstrated as high as 90% hit rate, of which over two dozen compounds were single digit nanomolar sEH inhibitors by IC(50) determination. In total the library design and synthesis produced more than 300 submicromolar sEH inhibitors. In cellular systems consistent activities were demonstrated with biochemical measurements. The SAR understanding of the benzoxazole template provides valuable insights into discovery of novel sEH inhibitors as therapeutic agents.

Laser Brazing Characteristics of Al to Brass with Zn-Based Filler

NASA Astrophysics Data System (ADS)

Tan, Caiwang; Liu, Fuyun; Sun, Yiming; Chen, Bo; Song, Xiaoguo; Li, Liqun; Zhao, Hongyun; Feng, Jicai

2018-05-01

Laser brazing of Al to brass in lap configuration with Zn-based filler was performed in this work. The process parameters including laser power, defocused distance were found to have a significant influence on appearance, microstructure and mechanical properties. The process parameters were optimized to be laser power of 2700 W and defocusing distance of + 40 mm from brass surface. In addition, preheating exerted great influence on wetting and spreading ability of Zn filler on brass surface. The microstructure observation showed the thickness of reaction layer (CuZn phase) at the interface of the brass side would grow with the increase in laser power and the decrease in the laser defocusing distance. Moreover, preheating could increase the spreading area of the filler metal and induced the growth of the reaction layer. The highest tensile-shear load of the joint could reach 2100 N, which was 80% of that of Al alloy base metal. All the joints fractured along the CuZn reaction layer and brass interface. The fracture morphology displayed the characteristics of the cleavage fracture when without preheating before welding, while it displayed the characteristics of the quasi-cleavage fracture with preheating before welding.

Global Aesthetics Consensus: Hyaluronic Acid Fillers and Botulinum Toxin Type A—Recommendations for Combined Treatment and Optimizing Outcomes in Diverse Patient Populations

PubMed Central

Liew, Steven; Signorini, Massimo; Vieira Braz, André; Fagien, Steven; Swift, Arthur; De Boulle, Koenraad L.; Raspaldo, Hervé; Trindade de Almeida, Ada R.; Monheit, Gary

2016-01-01

Background: Combination of fillers and botulinum toxin for aesthetic applications is increasingly popular. Patient demographics continue to diversify, and include an expanding population receiving maintenance treatments over decades. Methods: A multinational panel of plastic surgeons and dermatologists convened the Global Aesthetics Consensus Group to develop updated guidelines with a worldwide perspective for hyaluronic acid fillers and botulinum toxin. This publication considers strategies for combined treatments, and how patient diversity influences treatment planning and outcomes. Results: Global Aesthetics Consensus Group recommendations reflect increased use of combined treatments in the lower and upper face, and some midface regions. A fully patient-tailored approach considers physiologic and chronologic age, ethnically associated facial morphotypes, and aesthetic ideals based on sex and culture. Lower toxin dosing, to modulate rather than paralyze muscles, is indicated where volume deficits influence muscular activity. Combination of toxin with fillers is appropriate for several indications addressed previously with toxin alone. New scientific data regarding hyaluronic acid fillers foster an evidence-based approach to selection of products and injection techniques. Focus on aesthetic units, rather than isolated rhytides, optimizes results from toxin and fillers. It also informs longitudinal treatment planning, and analysis of toxin nonresponders. Conclusions: The emerging objective of injectable treatment is facial harmonization rather than rejuvenation. Combined treatment is now a standard of care. Its use will increase further as we refine the concept that aspects of aging are intimately related, and that successful treatment entails identifying and addressing the primary causes of each. CLINICAL QUESTION/LEVEL OF EVIDENCE: Therapeutic, V. PMID:27119917

Studies on the structural changes during curing of epoxy and its blend with CTBN

NASA Astrophysics Data System (ADS)

Srivastava, Kavita; Rathore, Ashwani Kumar; Srivastava, Deepak

2018-01-01

Cashew nut shell liquid (CNSL), an agricultural renewable resource material, produces natural phenolic distillates such as cardanol. Cardanol condenses with formaldehyde at the ortho- and para-position of the phenolic ring under acidic or alkaline condition to yield a series of polymers of novolac- or resol-type phenolic resins. These phenolic resins may further be modified by epoxidation with epichlorohydrin to duplicate the performance of such phenolic-type novolacs (CFN). The structural changes during curing of blend samples of epoxy and carboxyl terminated poly (butadiene-co-acrylonitrile) (CTBN) were studies by Fourier-transform infrared (FTIR) spectrophotometer. The epoxy samples were synthesized by biomass material, cardanol. Blend sample was prepared by physical mixing of CTBN ranging between 0 and 20 weight percent CTBN liquid rubber into cardanol-based epoxidized novolac (CEN) resin. The FTIR spectrum of uncured blend sample clearly indicated that there appeared a band in the region of 3200-3500 cm- 1 which might be due to the presence of phenolic hydroxyl group and sbnd OH group of the opened epoxide. Pure epoxy resin showed peaks near 856 cm- 1 which might be due to oxirane functionality of the epoxidized novolac resin. Both epoxy and its blend sample was cured with polyamine. The cure temperature of CEN resin was found to be decreased by the incorporation of CTBN. The decomposition behavior was also studied by thermogravimetric analyzer (TGA). Two-step decomposition behavior was observed in both epoxy and its blend samples.

Studies on the structural changes during curing of epoxy and its blend with CTBN.

PubMed

Srivastava, Kavita; Rathore, Ashwani Kumar; Srivastava, Deepak

2018-01-05

Cashew nut shell liquid (CNSL), an agricultural renewable resource material, produces natural phenolic distillates such as cardanol. Cardanol condenses with formaldehyde at the ortho- and para-position of the phenolic ring under acidic or alkaline condition to yield a series of polymers of novolac- or resol-type phenolic resins. These phenolic resins may further be modified by epoxidation with epichlorohydrin to duplicate the performance of such phenolic-type novolacs (CFN). The structural changes during curing of blend samples of epoxy and carboxyl terminated poly (butadiene-co-acrylonitrile) (CTBN) were studies by Fourier-transform infrared (FTIR) spectrophotometer. The epoxy samples were synthesized by biomass material, cardanol. Blend sample was prepared by physical mixing of CTBN ranging between 0 and 20weightpercent CTBN liquid rubber into cardanol-based epoxidized novolac (CEN) resin. The FTIR spectrum of uncured blend sample clearly indicated that there appeared a band in the region of 3200-3500cm -1 which might be due to the presence of phenolic hydroxyl group and OH group of the opened epoxide. Pure epoxy resin showed peaks near 856cm -1 which might be due to oxirane functionality of the epoxidized novolac resin. Both epoxy and its blend sample was cured with polyamine. The cure temperature of CEN resin was found to be decreased by the incorporation of CTBN. The decomposition behavior was also studied by thermogravimetric analyzer (TGA). Two-step decomposition behavior was observed in both epoxy and its blend samples. Copyright © 2017 Elsevier B.V. All rights reserved.

A PLS-based extractive spectrophotometric method for simultaneous determination of carbamazepine and carbamazepine-10,11-epoxide in plasma and comparison with HPLC

NASA Astrophysics Data System (ADS)

Hemmateenejad, Bahram; Rezaei, Zahra; Khabnadideh, Soghra; Saffari, Maryam

2007-11-01

Carbamazepine (CBZ) undergoes enzyme biotransformation through epoxidation with the formation of its metabolite, carbamazepine-10,11-epoxide (CBZE). A simple chemometrics-assisted spectrophotometric method has been proposed for simultaneous determination of CBZ and CBZE in plasma. A liquid extraction procedure was operated to separate the analytes from plasma, and the UV absorbance spectra of the resultant solutions were subjected to partial least squares (PLS) regression. The optimum number of PLS latent variables was selected according to the PRESS values of leave-one-out cross-validation. A HPLC method was also employed for comparison. The respective mean recoveries for analysis of CBZ and CBZE in synthetic mixtures were 102.57 (±0.25)% and 103.00 (±0.09)% for PLS and 99.40 (±0.15)% and 102.20 (±0.02)%. The concentrations of CBZ and CBZE were also determined in five patients using the PLS and HPLC methods. The results showed that the data obtained by PLS were comparable with those obtained by HPLC method.

Synthesis and properties of a novel bio-based polymer from modified soybean oil

NASA Astrophysics Data System (ADS)

Li, Y. T.; Yang, L. T.; Zhang, H.; Tang, Z. J.

2017-02-01

Maleated acrylated epoxidized soybean oil (MAESO) was prepared by acrylated epoxidized soybean oil (AESO) and maleic anhydride. AESO were obtained by the reaction of epoxidized soybean oil (ESO) with acrylic acid as the ring-opening reagent. The polymer was prepared by MAESO react with styrene. The structures of the products were studied by Fourier transformation infrared spectrometer (FT-IR), and were consistent with the theoretical structures. Swelling experiment indicated that the crosslinking degree increased with increasing epoxy value of ESO. Thermal properties was tested by thermo-gravimetric analysis (TG) and differential scanning calorimetry analysis (DSC), indicating that glass transition temperature (Tg) of the polymer increased with increasing epoxy value of ESO, and thermal stability of polymer have a good correlation with the crosslinking degree. Mechanical properties analysis presented that tensile strength and impact strength affected by epoxy value of ESO. With the increase of epoxy value, the tensile strength increase, while the impact strength decrease. The property of the polymer ranged from elastomer to plastic character depended on the functionality of the ESO.

4D printing smart biomedical scaffolds with novel soybean oil epoxidized acrylate

PubMed Central

Miao, Shida; Zhu, Wei; Castro, Nathan J.; Nowicki, Margaret; Zhou, Xuan; Cui, Haitao; Fisher, John P.; Zhang, Lijie Grace

2016-01-01

Photocurable, biocompatible liquid resins are highly desired for 3D stereolithography based bioprinting. Here we solidified a novel renewable soybean oil epoxidized acrylate, using a 3D laser printing technique, into smart and highly biocompatible scaffolds capable of supporting growth of multipotent human bone marrow mesenchymal stem cells (hMSCs). Porous scaffolds were readily fabricated by simply adjusting the printer infill density; superficial structures of the polymerized soybean oil epoxidized acrylate were significantly affected by laser frequency and printing speed. Shape memory tests confirmed that the scaffold fixed a temporary shape at −18 °C and fully recovered its original shape at human body temperature (37 °C), which indicated the great potential for 4D printing applications. Cytotoxicity analysis proved that the printed scaffolds had significant higher hMSC adhesion and proliferation than traditional polyethylene glycol diacrylate (PEGDA), and had no statistical difference from poly lactic acid (PLA) and polycaprolactone (PCL). This research is believed to significantly advance the development of biomedical scaffolds with renewable plant oils and advanced 3D fabrication techniques. PMID:27251982

Cholesterol-5,6-epoxides: chemistry, biochemistry, metabolic fate and cancer.

PubMed

Poirot, Marc; Silvente-Poirot, Sandrine

2013-03-01

In the nineteen sixties it was proposed that cholesterol might be involved in the etiology of cancers and cholesterol oxidation products were suspected of being causative agents. Researchers had focused their attention on cholesterol-5,6-epoxides (5,6-ECs) based on several lines of evidence: 1) 5,6-ECs contained an oxirane group that was supposed to confer alkylating properties such as those observed for aliphatic and aromatic epoxides. 2) cholesterol-5,6-epoxide hydrolase (ChEH) was induced in pre-neoplastic lesions of skin from rats exposed to ultraviolet irradiations and ChEH was proposed to be involved in detoxification processes like other epoxide hydrolases. However, 5,6-ECs failed to induce carcinogenicity in rodents which ruled out a potent carcinogenic potential for 5,6-ECs. Meanwhile, clinical studies revealed an anomalous increase in the concentrations of 5,6β-EC in the nipple fluids of patients with pre-neoplastic breast lesions and in the blood of patients with endometrious cancers, suggesting that 5,6-ECs metabolism could be linked with cancer. Paradoxically, ChEH has been recently shown to be totally inhibited by therapeutic concentrations of tamoxifen (Tam), which is one of the main drugs used in the hormonotherapy and the chemoprevention of breast cancers. These data would suggest that the accumulation of 5,6-ECs could represent a risk factor, but we found that 5,6-ECs were involved in the induction of breast cancer cell differentiation and death induced by Tam suggesting a positive role of 5,6-ECs. These observations meant that the biochemistry and the metabolism of 5,6-ECs needed to be extensively studied. We will review the current knowledge and the future direction of 5,6-ECs chemistry, biochemistry, metabolism, and relationship with cancer. Copyright © 2012 Elsevier Masson SAS. All rights reserved.

Reactive Nanoparticles Compatibilized Immiscible Polymer Blends: Synthesis of Reactive SiO2 with Long Poly(methyl methacrylate) Chains and the in Situ Formation of Janus SiO2 Nanoparticles Anchored Exclusively at the Interface.

PubMed

Wang, Hengti; Fu, Zhiang; Zhao, Xuewen; Li, Yongjin; Li, Jingye

2017-04-26

The exclusive location of compatibilizers at the interface of immiscible binary polymer blends to bridge the neighboring phases is the most important issue for fabricating desirable materials with synergistic properties. However, the positional stability of the compatibilizers at the interface remains a challenge in both scientific and technical points of view due to the intrinsic flexibility of compatibilizer molecules against aggressive processing conditions. Herein, taking the typical immiscible poly vinylidene fluoride (PVDF)/polylactic acid (PLLA) blend as an example, we demonstrate a novel approach, termed as the interfacial nanoparticle compatibilization (IPC) mechanism, to overcome the challenges by packing nanoparticles thermodynamically at the interface through melt reactive blending. Specifically, we have first synthesized nanosilica with both reactive epoxide groups and long poly(methyl methacrylate) (PMMA) tails, called reactive PMMA-graft-SiO 2 (Epoxy-MSiO 2 ), and then incorporated the Epoxy-MSiO 2 into the PVDF/PLLA (50/50, w/w) blends by melt blending. PLLA was in situ grafted onto SiO 2 by the reaction of the carboxylic acid groups with epoxide groups on the surface of SiO 2 . Therefore, the reacted SiO 2 particles were exclusively located at the interface by the formation of the Janus-faced silica hybrid nanoparticles (JSNp) with pregrafted PMMA tails entangled with PVDF molecular chains in the PVDF phase and the in situ grafted PLLA chains embedded in the PLLA phase. Such JSNp with a distinct hemisphere, functioning as compatibilizer, can not only suppress coalescence of PVDF domains by its steric repulsion but also enhance interfacial adhesion via the selective interactions with the corresponding miscible phase. The interfacial location of JSNp is very stable even under the severe shear field and annealing in the melt. This IPC mechanism paves a new possibility to use the various types of nanoparticles as both effective compatibilizers and functional fillers for immiscible polymer blends.

The effect of filler loading and morphology on the mechanical properties of contemporary composites.

PubMed

Kim, Kyo-Han; Ong, Joo L; Okuno, Osamu

2002-06-01

Little information exists regarding the filler morphology and loading of composites with respect to their effects on selected mechanical properties and fracture toughness. The objectives of this study were to: (1) classify commercial composites according to filler morphology, (2) evaluate the influence of filler morphology on filler loading, and (3) evaluate the effect of filler morphology and loading on the hardness, flexural strength, flexural modulus, and fracture toughness of contemporary composites. Field emission scanning electron microscopy/energy dispersive spectroscopy was used to classify 3 specimens from each of 14 commercial composites into 4 groups according to filler morphology. The specimens (each 5 x 2.5 x 15 mm) were derived from the fractured remnants after the fracture toughness test. Filler weight content was determined by the standard ash method, and the volume content was calculated using the weight percentage and density of the filler and matrix components. Microhardness was measured with a Vickers hardness tester, and flexural strength and modulus were measured with a universal testing machine. A 3-point bending test (ASTM E-399) was used to determine the fracture toughness of each composite. Data were compared with analysis of variance followed by Duncan's multiple range test, both at the P<.05 level of significance. The composites were classified into 4 categories according to filler morphology: prepolymerized, irregular-shaped, both prepolymerized and irregular-shaped, and round particles. Filler loading was influenced by filler morphology. Composites containing prepolymerized filler particles had the lowest filler content (25% to 51% of filler volume), whereas composites containing round particles had the highest filler content (59% to 60% of filler volume). The mechanical properties of the composites were related to their filler content. Composites with the highest filler by volume exhibited the highest flexural strength (120 to 129 MPa), flexural modulus (12 to 15 GPa), and hardness (101 to 117 VHN). Fracture toughness was also affected by filler volume, but maximum toughness was found at a threshold level of approximately 55% filler volume. Within the limitations of this study, the commercial composites tested could be classified by their filler morphology. This property influenced filler loading. Both filler morphology and filler loading influenced flexural strength, flexural modulus, hardness, and fracture toughness.

Towards the Synthesis of Dihydrooxepino[4,3-b]pyrrole-Containing Natural Products via Cope Rearrangement of Vinyl Pyrrole Epoxides.

PubMed

Cameron, Alex; Fisher, Brendan; Fisk, Nicholas; Hummel, Jessica; White, Jonathan M; Krenske, Elizabeth H; Rizzacasa, Mark A

2015-12-18

An approach to the dihydrooxepino[4,3-b]pyrrole core of diketopiperazine natural products which utilizes a vinyl pyrrole epoxide Cope rearrangement was investigated. It was found that an ester substituent on the epoxide was essential for the [3,3]-rearrangement to occur. Density functional calculations with M06-2X provided explanations for the effects of the pyrrole and ester groups on these rearrangements.

Selective and metal-free epoxidation of terminal alkenes by heterogeneous polydioxirane in mild conditions

NASA Astrophysics Data System (ADS)

Kazemnejadi, M.; Shakeri, A.; Nikookar, M.; Shademani, R.; Mohammadi, M.

2018-05-01

Polydioxirane (PDOX) was prepared by the treatment of polysalicylaldehyde with Oxone and was found as a selective, highly efficient and heterogeneous reagent for epoxidation of alkenes which can be successfully isolated. This work also introduced a simpler, safer and milder way for epoxidation of alkenes with dioxirane groups than before. PDOX can be simply recovered from the reaction mixture by plain filtration and reused for eight runs without significant reactivity loss.

Autonomic self-healing in epoxidized natural rubber.

PubMed

Rahman, Arifur; Sartore, Luciana; Bignotti, Fabio; Di Landro, Luca

2013-02-01

The development of polymers that can repair damage autonomously would be useful to improve the lifetime of polymeric materials. To date, limited attention has been dedicated to developing elastomers with autonomic self-healing ability, which can recover damages without need for an external or internal source of healing agents. This work investigates the self-healing behavior of epoxidized natural rubber (ENR) with two different epoxidation levels (25 and 50 mol % epoxidation) and of the corresponding unfunctionalized rubber, cis-1,4-polyisoprene (PISP). A self-adhesion assisted self-healing behavior was revealed by T-peel tests on slightly vulcanized rubbers. A higher epoxidation level was found to enhance self-healing. Self-healing of rubbers following ballistic damages was also investigated. A pressurized air flow test setup was used to evaluate the self-healing of ballistic damages in rubbers. Microscope (OM, SEM, and TEM) analyses were carried out to provide further evidence of healing in the impact zones. Self-healing of ballistic damages was observed only in ENR with 50 mol % epoxidation and it was found to be influenced significantly by the cross-link density. Finally, self-healing of ballistic damages was also observed in ENR50/PISP blends only when the content of the healing component (i.e., ENR50) was at least 25 wt %. From an analysis of the results, it was concluded that a synergistic effect between interdiffusion and interaction among polar groups leads to self-healing in ENR.

Changes in antioxidant capacity and colour associated with the formation of β-carotene epoxides and oxidative cleavage derivatives.

PubMed

Gurak, Poliana D; Mercadante, Adriana Z; González-Miret, M L; Heredia, Francisco J; Meléndez-Martínez, Antonio J

2014-03-15

In this study HPLC-DAD-MS/MS was applied for the identification of compounds derived from (all-E)-β-carotene following epoxidation and oxidative cleavage. The consequences on the CIELAB colour parameters and antioxidant capacity (AC) were also evaluated. Five apocarotenoids, three secocarotenoids, seven Z isomers and two epoxides were detected as a result of the oxidative cleavage. Four epoxides and three Z isomers were detected as a consequence of the epoxidation reaction. Some compounds were detected for the first time as a result of oxidation reactions. Both treatments led to a marked decrease in b(∗) and Cab(∗) values, indicating that these colour parameters can be used for the rapid assessment of β-carotene oxidation. The oxidative cleavage of β-carotene resulted in increased capacity to both scavenge ABTS(+) and quench singlet oxygen. These results suggest that the study of the AC of these oxidative derivatives and their possible usefulness as food ingredients deserves further attention. Copyright © 2013 Elsevier Ltd. All rights reserved.

Rate and Selectivity Control in Thioether and Alkene Oxidation with H 2 O 2 over Phosphonate-Modified Niobium(V)-Silica Catalysts

DOE Office of Scientific and Technical Information (OSTI.GOV)

Thornburg, Nicholas E.; Notestein, Justin M.

Supported metal oxide catalysts are versatile materials for liquid-phase oxidations, including alkene epoxidation and thioether sulfoxidation with H2O2. Periodic trends in H2O2 activation was recently demonstrated for alkene epoxidation, highlighting Nb-SiO2 as a more active and selective catalyst than Ti-SiO2. Three representative catalysts are studied consisting of NbV, TiIV, and ZrIV on silica, each made through a molecular precursor approach that yields highly dispersed oxide sites, for thioanisole oxidation by H2O2. Initial rates trend Nb>Ti>>Zr, as for epoxidation, and Nb outperforms Ti for a number of other thioethers. In contrast, selectivity to sulfoxide vs. sulfone trends Ti>Nb>>Zr at all conversions.more » Modifying the Nb-SiO2 catalyst with phenylphosphonic acid does not completely remove sulfoxidation reactivity, as it did for photooxidation and epoxidation, and results in an unusual material active for sulfoxidation but neither epoxidation nor overoxidation to the sulfone.« less

Brazing Inconel 625 Using Two Ni/(Fe)-Based Amorphous Filler Foils

NASA Astrophysics Data System (ADS)

Chen, Wen-Shiang; Shiue, Ren-Kae

2012-07-01

For MBF-51 filler, the brazed joint consists of interfacial grain boundary borides, coarse Nb6Ni16Si7, and Ni/Cr-rich matrix. In contrast, the VZ-2106 brazed joint is composed of interfacial Nb6Ni16Si7 precipitates as well as grain boundary borides, coarse Nb6Ni16Si7, and Ni/Cr/Fe-rich matrix. The maximum tensile strength of 443 MPa is obtained from the MBF-51 brazed specimen. The tensile strengths of VZ-2106 brazed joints are approximately 300 MPa. Both amorphous filler foils demonstrate potential in brazing IN-625 substrate.

Industrial waste utilization for foam concrete

NASA Astrophysics Data System (ADS)

Krishnan, Gokul; Anand, K. B.

2018-02-01

Foam concrete is an emerging and useful construction material - basically a cement based slurry with at least 10% of mix volume as foam. The mix usually containing cement, filler (usually sand) and foam, have fresh densities ranging from 400kg/m3 to 1600kg/m3. One of the main drawbacks of foam concrete is the large consumption of fine sand as filler material. Usage of different solid industrial wastes as fillers in foam concrete can reduce the usage of fine river sand significantly and make the work economic and eco-friendly. This paper aims to investigate to what extent industrial wastes such as bottom ash and quarry dust can be utilized for making foam concrete. Foam generated using protein based agent was used for preparing and optimizing (fresh state properties). Investigation to find the influence of design density and air-void characteristics on the foam concrete strength shows higher strength for bottom ash mixes due to finer air void distribution. Setting characteristics of various mix compositions are also studied and adoption of Class C flyash as filler demonstrated capability of faster setting.

Thermal, Mechanical, and Electrical Properties of Graphene Nanoplatelet/Graphene Oxide/ Polyurethane Hybrid Nanocomposite.

PubMed

Pokharel, Pashupati; Lee, Sang Hyub; Lee, Dai Soo

2015-01-01

Hybrid nanocomposites of polyurethane (PU) were prepared by in-situ polymerization of 4,4'- diphenyl methane diisocyanate (MDI) with mixture of graphene oxide (GO) and graphene nanoplatelet (GNP) dispersed in a poly(tetramethylene ether glycol) (PTMEG). Effects of the fillers, GO and GNP, on the thermal, mechanical, and electrical properties of the nanocomposites of PU were investigated. Sonication of the hybrid of GNP and GO with PTMEG enabled effective dispersion of the fillers in the solution than the sonication of GNP alone. The addition of PTMEG in the solution prevented the GNPs from the restacking during the drying process. It was observed that the electrical conductivity and mechanical property of the nanocomposites based on the hybrid of GO and GNP were superior to the nanocomposite based on GNP alone at the same loading of the filler. At the loading of the 3 wt% hybrid filler in PU, we observed the improvement of Young's modulus -200% and the surface resistivity of 10(9.5) ohm/sq without sacrificing the elongation at break.

Development of a SMA-Based Slat-Cove Filler for Reduction of Aeroacoustic Noise Associated With Transport-Class Aircraft Wings

NASA Technical Reports Server (NTRS)

Turner, Travis L.; Kidd, Reggie T.; Hartl, Darren J.; Scholten, William D.

2013-01-01

Airframe noise is a significant part of the overall noise produced by typical, transport-class aircraft during the approach and landing phases of flight. Leading-edge slat noise is a prominent source of airframe noise. The concept of a slat-cove filler was proposed in previous work as an effective means of mitigating slat noise. Bench-top models were deployed at 75% scale to study the feasibility of producing a functioning slat-cove filler. Initial results from several concepts led to a more-focused effort investigating a deformable structure based upon pseudoelastic SMA materials. The structure stows in the cavity between the slat and main wing during cruise and deploys simultaneously with the slat to guide the aerodynamic flow suitably for low noise. A qualitative parametric study of SMA-enabled, slat-cove filler designs was performed on the bench-top. Computational models were developed and analyses were performed to assess the displacement response under representative aerodynamic load. The bench-top and computational results provide significant insight into design trades and an optimal design.

Global Aesthetics Consensus: Avoidance and Management of Complications from Hyaluronic Acid Fillers—Evidence- and Opinion-Based Review and Consensus Recommendations

PubMed Central

Liew, Steven; Sundaram, Hema; De Boulle, Koenraad L.; Goodman, Greg J.; Monheit, Gary; Wu, Yan; Trindade de Almeida, Ada R.; Swift, Arthur; Vieira Braz, André

2016-01-01

Background: Although the safety profile of hyaluronic acid fillers is favorable, adverse reactions can occur. Clinicians and patients can benefit from ongoing guidance on adverse reactions to hyaluronic acid fillers and their management. Methods: A multinational, multidisciplinary group of experts in cosmetic medicine convened the Global Aesthetics Consensus Group to review the properties and clinical uses of Hylacross and Vycross hyaluronic acid products and develop updated consensus recommendations for early and late complications associated with hyaluronic acid fillers. Results: The consensus panel provided specific recommendations focusing on early and late complications of hyaluronic acid fillers and their management. The impact of patient-, product-, and technique-related factors on such reactions was described. Most of these were noted to be mild and transient. Serious adverse events are rare. Early adverse reactions to hyaluronic acid fillers include vascular infarction and compromise; inflammatory reactions; injection-related events; and inappropriate placement of filler material. Among late reactions are nodules, granulomas, and skin discoloration. Most adverse events can be avoided with proper planning and technique. Detailed understanding of facial anatomy, proper patient and product selection, and appropriate technique can further reduce the risks. Should adverse reactions occur, the clinician must be prepared and have tools available for effective treatment. Conclusions: Adverse reactions with hyaluronic acid fillers are uncommon. Clinicians should take steps to further reduce the risk and be prepared to treat any complications that arise. PMID:27219265

Composite adhesive bonds reinforced with microparticle filler based on egg shell waste

NASA Astrophysics Data System (ADS)

Müller, Miroslav; Valášek, Petr

2018-05-01

A research on composite adhesive bonds reinforced with waste from hen eggs processing, i.e. egg shell waste (ESW) is based on an assumption of the utilization of agricultural/food production waste. The aim of the research is to gain new pieces of knowledge about the material utilization of ESW, i.e. to evaluate possibilities of the use of various concentrations of ESW microparticles smaller than 100 µm based on hen egg shells as the filler in a structural resin used for a creation of adhesive bonds from bearing metal elements. An adhesive bond strength, an elongation at break and a fracture surface were evaluated within the research on adhesive bonds. The experiment results proved the efficiency of ESW filler in the area of composite adhesive bonds. The adhesive bond strength was increased up of more than 17 % by adding 40 wt.% of ESW microparticles.

Treatment of Soft Tissue Filler Complications: Expert Consensus Recommendations.

PubMed

Urdiales-Gálvez, Fernando; Delgado, Nuria Escoda; Figueiredo, Vitor; Lajo-Plaza, José V; Mira, Mar; Moreno, Antonio; Ortíz-Martí, Francisco; Del Rio-Reyes, Rosa; Romero-Álvarez, Nazaret; Del Cueto, Sofía Ruiz; Segurado, María A; Rebenaque, Cristina Villanueva

2018-04-01

Dermal fillers have been increasingly used in minimally invasive facial esthetic procedures. This widespread use has led to a rise in reports of associated complications. The aim of this expert consensus report is to describe potential adverse events associated with dermal fillers and to provide guidance on their treatment and avoidance. A multidisciplinary group of experts in esthetic treatments convened to discuss the management of the complications associated with dermal fillers use. A search was performed for English, French, and Spanish language articles in MEDLINE, the Cochrane Database, and Google Scholar using the search terms "complications" OR "soft filler complications" OR "injectable complications" AND "dermal fillers" AND "Therapy". An initial document was drafted by the Coordinating Committee, and it was reviewed and modified by the experts, until a final text was agreed upon and validated. The panel addressed consensus recommendations about the classification of filler complications according to the time of onset and about the clinical management of different complications including bruising, swelling, edema, infections, lumps and bumps, skin discoloration, and biofilm formation. Special attention was paid to vascular compromise and retinal artery occlusion. Clinicians should be fully aware of the signs and symptoms related to complications and be prepared to confidently treat them. Establishing action protocols for emergencies, with agents readily available in the office, would reduce the severity of adverse outcomes associated with injection of hyaluronic acid fillers in the cosmetic setting. This document seeks to lay down a set of recommendations and to identify key issues that may be useful for clinicians who are starting to use dermal fillers. Additionally, this document provides a better understanding about the diagnoses and management of complications if they do occur. This journal requires that authors assign a level of evidence to each article. For a full description of these Evidence-Based Medicine ratings, please refer to the Table of Contents or the online Instructions to Authors www.springer.com/00266 .

Reactive Diazonium-Modified Silica Fillers for High-Performance Polymers.

PubMed

Sandomierski, Mariusz; Strzemiecka, Beata; Chehimi, Mohamed M; Voelkel, Adam

2016-11-08

We describe a simple way of modification of three silica-based fillers with in situ generated 4-hydroxymethylbenzenediazonium salt ( + N 2 -C 6 H 4 -CH 2 OH). The rationale for using a hydroxyl-functionalized diazonium salt is that it provides surface-functionalized fillers that can react with phenolic resins. The modification of silica by diazonium salts was assessed using Fourier transform infrared (FTIR) spectroscopy and X-ray photoelectron spectroscopy (XPS). FTIR spectroscopy permitted the tracking of benzene ring breathing and C-C. The absence of the characteristic N≡N stretching vibration in the 2200-2300 cm -1 range indicates the loss of the diazonium group. XPS results indicate a higher C/Si atomic ratio after the diazonium modification of fillers and the presence of π-π* C1s satellite peaks characteristic of the surface-tethered aromatic species. Adhesion of aryl layers to the silicas is excellent because they withstand harsh thermal and organic solvent treatments. Phenolic resins (used, for example, as binders in abrasive products) were filled with diazonium-modified silicas at 10-25 wt %. The reactivity of the fillers toward phenolic resins was evaluated by the determination of the flow distance. After annealing at 180 °C, the diazonium-modified silica/phenolic resin composites were mechanically tested using the three-point flexural method. The flexural strength was found to be up to 35% higher than that of the composites prepared without any diazonium salts. Diazonium-modified silica with surface-bound -CH 2 -OH groups is thus ideal reactive filler for phenolic resins. Such filler ensures interfacial chemical reactions with the matrix and imparts robust mechanical properties to the final composites. This specialty diazonium-modified silica will find potential application as fillers in the composites for the abrasive industry. More generally, aryl diazonium salts are a unique new series of compounds for tailoring the surface properties of fillers and tuning the physicochemical and mechanical properties of polymer composites.

Simple Epoxide Formation for the Organic Laboratory Using Oxone

ERIC Educational Resources Information Center

Broshears, Williams C.; Esteb, John J.; Richter, Jeremy; Wilson, Anne M.

2004-01-01

Epoxide chemistry is widely used in organic synthesis and regularly discussed in organic chemistry textbooks. An experiment to generate dimethyldioxirane in situ from acetone using Oxone is explained.

Molecular-Scale Hybrid Membranes Derived from Metal-Organic Polyhedra for Gas Separation.

PubMed

Liu, Xinlei; Wang, Xuerui; Bavykina, Anastasiya V; Chu, Liangyong; Shan, Meixia; Sabetghadam, Anahid; Miro, Hozanna; Kapteijn, Freek; Gascon, Jorge

2018-06-13

The preparation and the performance of mixed matrix membranes based on metal-organic polyhedra (MOPs) are reported. MOP fillers can be dispersed as discrete molecular units (average 9 nm in diameter) when low filler cargos are used. In spite of the low doping amount (1.6 wt %), a large performance enhancement in permeability, aging resistance, and selectivity can be achieved. We rationalize this effect on the basis of the large surface to volume ratio of the filler, which leads to excellent dispersion at low concentrations and thus alters polymer packing. Although membranes based only on the polymer component age quickly with time, the performance of the resulting MOP-containing membranes meets the commercial target for postcombustion CO 2 capture for more than 100 days.

Use of Almond Shells and Rice Husk as Fillers of Poly(Methyl Methacrylate) (PMMA) Composites

PubMed Central

Sabbatini, Alessandra; Lanari, Silvia; Santulli, Carlo

2017-01-01

In recent years, wood fibres have often been applied as the reinforcement of thermoplastic materials, such as polypropylene, whereas their use in combination with thermosetting resin has been less widespread. This study concerns the production of PMMA-based composites by partly replacing alumina trihydrate (ATH) with wood waste fillers, namely rice husks and almond shells, which would otherwise be disposed by incineration. The amount of filler introduced was limited to 10% as regards rice husks and 10 or 15% almond shells, since indications provided by reactivity tests and viscosity measurements did not suggest the feasibility of total replacement of ATH. As a matter of fact, the introduction of these contents of wood waste filler in PMMA-based composite did not result in any significant deterioration of its mechanical properties (Charpy impact, Rockwell M hardness and flexural performance). Some reduction of these properties was only observed in the case of introduction of 15% almond shells. A further issue concerned the yellowing of the organic filler under exposure to UV light. On the other hand, a very limited amount of water was absorbed, never exceeding values around 0.6%, despite the significant porosity revealed by the filler’s microscopic evaluation. These results are particularly interesting in view of the application envisaged for these composites, i.e., wood replacement boards. PMID:28773234

Gold(I)-Catalyzed Cascade Cyclization of Allenyl Epoxides

PubMed Central

Tarselli, Michael A.; Lucas Zuccarello, J

2009-01-01

Cationic gold(I) phosphite catalysts activate allenes for epoxide cascade reactions. The system is tolerant of numerous functional groups (sulfones, esters, ethers, sulfonamides) and proceeds at room temperature in dichloromethane. The cyclization pathway is sensitive to the substitution pattern of the epoxide, and the backbone structure of the A-ring. It is capable of producing medium-ring ethers, fused 6-5 bicyclic, and linked pyran-furan structures. The resulting cycloisomers are reminiscent of structures found in numerous polyether natural products. PMID:19588972

Study of soybean oil-based polymers for controlled release anticancer drugs

USDA-ARS?s Scientific Manuscript database

Soybean oil-based polymers were prepared by the ring-opening polymerization of epoxidized soybean oil with Lewis acid catalyst. The formed polymers (HPESO) could be converted into hydrogels through hydrolysis. Characterization and viscoelastic properties of this soy hydrogel and application in contr...

Influence of fillers on the alkali activated chamotte

NASA Astrophysics Data System (ADS)

Dembovska, L.; Bumanis, G.; Vitola, L.; Bajare, D.

2017-10-01

Alkali-activated materials (AAM) exhibit remarkable high-temperature resistance which makes them perspective materials for high-temperature applications, for instance as fire protecting and insulating materials in industrial furnaces. Series of experiments were carried out to develop optimum mix proportions of AAM based on chamotte with quartz sand (Q), olivine sand (OL) and firebrick sawing residues (K26) as fillers. Aluminium scrap recycling waste was considered as a pore forming agent and 6M NaOH alkali activation solution has been used. Lightweight porous AAM have been obtained with density in range from 600 to 880 kg/m3 and compressive strength from 0.8 to 2.7 MPa. The XRD and high temperature optical microscopy was used to characterize the performance of AAM. The mechanical, physical and structural properties of the AAM were determined after the exposure to elevated temperatures at 800 and 1000°C. The results indicate that most promising results for AAM were with K26 filler where strength increase was observed while Q and OL filler reduced mechanical properties due to structure deterioration caused by expansive nature of selected filler.

Physical Metallurgy, Weldability, and in-Service Performance of Nickel-Chromium Filler Metals Used in Nuclear Power Systems

NASA Astrophysics Data System (ADS)

Young, George A.; Etien, Robert A.; Hackett, Micah J.; Tucker, Julie D.; Capobianco, Thomas E.

Wrought Alloy 690 is well established for corrosion resistant nuclear applications but development continues to improve the weldability of a filler metal that retains the corrosion resistance and phase stability of the base metal. High alloy Ni-Cr filler metals are prone to several types of welding defects and new alloys are emerging for commercial use. This paper uses experimental and computational methods to illustrate key differences among welding consumables. Results show that solidification segregation is critical to understanding the weldability and environmentally-assisted cracking resistance of these alloys. Primary water stress corrosion cracking tests show a marked decrease in crack growth rates near 21 wt. % Cr at the grain boundary. While filler metals with 21-29 wt.% grain boundary Cr show similar PWSCC resistance, the higher alloyed grades are more prone to solidification cracking. Modeling and aging studies indicate that in some filler metals minor phase formation (e.g., Laves and σ) and long range order (LRO) must be assessed to ensure adequate weldability and inservice performance.

Influence of Filler Pore Structure and Polymer on the Performance of MOF-Based Mixed-Matrix Membranes for CO2 Capture.

PubMed

Sabetghadam, Anahid; Liu, Xinlei; Benzaqui, Marvin; Gkaniatsou, Effrosyni; Orsi, Angelica; Lozinska, Magdalena M; Sicard, Clemence; Johnson, Timothy; Steunou, Nathalie; Wright, Paul A; Serre, Christian; Gascon, Jorge; Kapteijn, Freek

2018-06-04

To gain insight into the influence of metal-organic framework (MOF) fillers and polymers on membrane performance, eight different composites were studied by combining four MOFs and two polymers. MOF materials (NH 2 -MIL-53(Al), MIL-69(Al), MIL-96(Al) and ZIF-94) with various chemical functionalities, topologies, and dimensionalities of porosity were employed as fillers, and two typical polymers with different permeability-selectivity properties (6FDA-DAM and Pebax) were selected as matrices. The best-performing MOF-polymer composites were prepared by loading 25 wt % of MIL-96(Al) as filler, which improved the permeability and selectivity of 6FDA-DAM to 32 and 10 %, while for Pebax they were enhanced to 25 and 18 %, respectively. The observed differences in membrane performance in the separation of CO 2 from N 2 are explained on the basis of gas solubility, diffusivity properties, and compatibility between the filler and polymer phases. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Interfacial reaction of intermetallic compounds of ultrasonic-assisted brazed joints between dissimilar alloys of Ti6Al4V and Al4Cu1Mg.

PubMed

Ma, Zhipeng; Zhao, Weiwei; Yan, Jiuchun; Li, Dacheng

2011-09-01

Ultrasonic-assisted brazing of Al4Cu1Mg and Ti6Al4V using Zn-based filler metal (without and with Si) has been investigated. Before brazing, the Ti6Al4V samples were pre-treated by hot-dip aluminizing and ultrasonic dipping in a molten filler metal bath in order to control the formation of intermetallic compounds between the Ti6Al4V samples and the filler metal. The results show that the TiAl(3) phase was formed in the interface between the Ti6Al4V substrate and the aluminized coating. For the Zn-based filler metal without Si, the Ti6Al4V interfacial area of the brazed joint did not change under the effect of the ultrasonic wave, and only consisted of the TiAl(3) phase. For the Zn-based filler metal with Si, the TiAl(3) phase disappeared and a Ti(7)Al(5)Si(12) phase was formed at the interfacial area of the brazed joints under the effect of the ultrasonic wave. Due to the TiAl(3) phase completely changing to a Ti(7)Al(5)Si(12) phase, the morphology of the intermetallic compounds changed from a block-like shape into a lamellar-like structure. The highest shear strength of 138MPa was obtained from the brazed joint free of the block-like TiAl(3) phase. Copyright © 2011 Elsevier B.V. All rights reserved.

Synergistic effect of the inclusion of glass fibers and halloysite nanotubes on the static and dynamic mechanical, thermal and flame retardant properties of polypropylene

NASA Astrophysics Data System (ADS)

Jenifer, A.; Rasana, N.; Jayanarayanan, K.

2018-06-01

Hybrid composites based on polypropylene (PP), glass fiber (GF) and halloysite nanotubes (HNT) were prepared in the presence of a compatibilizer, polypropylene grafted with maleic anhydride (PP-g-MAH), in a twin screw extruder. The properties of the micro composite (PP/GF), nanocomposite (PP/HNT) and hybrid composite (PP/GF/HNT) were studied and compared. The dispersion of the fillers in the base matrix and the effectiveness of the compatibilizer were ascertained by scanning electron microscopy (SEM) and transmission electron microscopy (TEM) and fourier transform infrared spectroscopy (FTIR). The tensile strength and modulus of the hybrid composite prepared in the presence of PP-g-MAH were found to be superior to those of the compatibilized micro and nanocomposites. Differential scanning calorimetry gave insight to the effect of the fillers on modifying the crystallization behavior of the base polymer. The combination of GF and HNT increased the crystallization temperature of PP phase in all the composites. The dynamic mechanical analysis proved that the fillers introduced in the polymer matrix restricted the relaxation of the PP polymer chains as evidenced by the rise in the glass transition temperature (Tg). The thermal stabilities of the hybrid composites were far superior to the neat polymer as the fillers formed an insulating layer delaying the degradation tendency and elevated the activation energy. The flammability of PP could be modified tremendously by the incorporation of the fillers as they reduced the burning rate and raised the limiting oxygen index values.

Magnetic and elastic anisotropy in magnetorheological elastomers using nickel-based nanoparticles and nanochains

DOE Office of Scientific and Technical Information (OSTI.GOV)

Landa, Romina A.; Soledad Antonel, Paula; Ruiz, Mariano M.

2013-12-07

Nickel (Ni) based nanoparticles and nanochains were incorporated as fillers in polydimethylsiloxane (PDMS) elastomers and then these mixtures were thermally cured in the presence of a uniform magnetic field. In this way, macroscopically structured-anisotropic PDMS-Ni based magnetorheological composites were obtained with the formation of pseudo-chains-like structures (referred as needles) oriented in the direction of the applied magnetic field when curing. Nanoparticles were synthesized at room temperature, under air ambient atmosphere (open air, atmospheric pressure) and then calcined at 400 °C (in air atmosphere also). The size distribution was obtained by fitting Small Angle X-ray Scattering (SAXS) experiments with a polydisperse hardmore » spheres model and a Schulz-Zimm distribution, obtaining a size distribution centered at (10.0 ± 0.6) nm with polydispersivity given by σ = (8.0 ± 0.2) nm. The SAXS, X-ray powder diffraction, and Transmission Electron Microscope (TEM) experiments are consistent with single crystal nanoparticles of spherical shape (average particle diameter obtained by TEM: (12 ± 1) nm). Nickel-based nanochains (average diameter: 360 nm; average length: 3 μm, obtained by Scanning Electron Microscopy; aspect ratio = length/diameter ∼ 10) were obtained at 85 °C and ambient atmosphere (open air, atmospheric pressure). The magnetic properties of Ni-based nanoparticles and nanochains at room temperature are compared and discussed in terms of surface and size effects. Both Ni-based nanoparticles and nanochains were used as fillers for obtaining the PDMS structured magnetorheological composites, observing the presence of oriented needles. Magnetization curves, ferromagnetic resonance (FMR) spectra, and strain-stress curves of low filler's loading composites (2% w/w of fillers) were determined as functions of the relative orientation with respect to the needles. The results indicate that even at low loadings it is possible to obtain magnetorheological composites with anisotropic properties, with larger anisotropy when using nanochains. For instance, the magnetic remanence, the FMR field, and the elastic response to compression are higher when measured parallel to the needles (about 30% with nanochains as fillers). Analogously, the elastic response is also anisotropic, with larger anisotropy when using nanochains as fillers. Therefore, all experiments performed confirm the high potential of nickel nanochains to induce anisotropic effects in magnetorheological materials.« less

Evaluation of pitting corrosion resistance of high-alloyed stainless steels welds for FGD plants in Korea

DOE Office of Scientific and Technical Information (OSTI.GOV)

Baek, K.K.; Sung, H.J.; Im, C.S.

1998-12-31

For successful application of high-alloyed stainless steels for Flue Gas Desulfurization (FGD) plants, pitting corrosion resistance of arc welds of N-added 6%Mo austenitic stainless steels (UNS N 08367) and super duplex stainless steels (UNS S 32550) made with various filler metals were evaluated using the Green Death solution. For Gas Tungsten Arc (GTA) and Gas Metal Arc (GMA) welds of N 08367, Critical Pitting Temperature (CPT) of base metal was 65--70 C, whereas weld made by ERNiCrMo-3 filler metal yielded CPT of 50 C. Welds made by ERNiCrMo-10 or ERNiCrMo-4 filler metals showed CPT of 60--65 C and 65--70C, respectively.more » For GTA and GMA welds of S 32550, CPT of welds made by ERNiCrMo-3 was 45--50 C, indicating that the filler metal can provide pitting corrosion resistance matching the S 32550 alloy. Thus, a proper pitting corrosion resistance of weldments of high-alloy stainless steels can be achieved by selecting filler metals having at least +10 higher Pitting Resistance Equivalent Number (PRE{sub N}) value than the base metal regardless of the type of arc welding process. The over-alloyed filler metals would compensate preferential segregation of Cr, MO along the dendrite boundary, which made the dendrite core more susceptible to pitting. Nitrogen addition to the GTA welds of N 08367 made with ERNiCrMo-3 failed to improve pitting corrosion resistance, which was attributed to the precipitation of nitrogen in the weld metal in the form of Nb-nitride.« less

Characteristic Asphalt Concrete Wearing Course (ACWC) Using Variation Lime Filler

NASA Astrophysics Data System (ADS)

Permana, R. A.; Pramesti, F. P.; Setyawan, A.

2018-03-01

This research use of lime filler Sukaraja expected add durability layers of concrete pavement is asphalt damage caused by the weather and load traffic. This study attempts to know how much value characteristic Marshall on a mixture of concrete asphalt using lime filler. This research uses experimental methods that is with a pilot to get results, thus will look filler utilization lime on construction concrete asphalt variation in filler levels 2 %, 3 %, 4 %.The results showed that the use of lime filler will affect characteristic a mixture of concrete asphalt. The more filler chalk used to increase the value of stability. On the cretaceous filler 2 % value of stability is 1067,04 kg. When lime filler levels added to the levels of filler 4 %, the value of stability increased to 1213,92 kg. The flexibility increased the number of filler as levels lime 2 % to 4 % suggests that are conducted more stiff mix.

Epoxidized natural rubber toughened aqueous resole type liquefied EFB resin: Physical and chemical characterization

NASA Astrophysics Data System (ADS)

Amran, Umar Adli; Zakaria, Sarani; Chia, Chin Hua

2013-11-01

A preliminary study on the reaction between aqueous resole type resinified liquefied palm oil empty fruit bunches fibres (RLEFB) with epoxidized natural rubber (ENR). Liquefaction of empty fruit bunches (EFB) is carried out at different ratio of phenol to EFB (P:EFB). Resole type phenolic resin is prepared using sodium hydroxide (NaOH) as the catalyst with the ratio of liquefied EFB (LEFB) to formaldehyde (LEFB:F) of 1:1.8. 50% epoxidation of epoxidized natural rubber (ENR-50) is used to react with resole resin by mixing with ENR with aqueous resole resin. The cured resin is characterized with FT-IR and SEM. Aqueous system have been found to be unsuitable medium in the reaction between resin and ENR. This system produced a highly porous product when RLEFB/ENR resin is cured.

Benzil, a potent activator of microsomal epoxide hydrolase in vitro.

PubMed

Seidegård, J; DePierre, J W

1980-12-01

Benzil was found to be a very potent activator of microsomal epoxide hydrolase activity (measured with styrene oxide as substrate) in vitro. The activating effect was uncompetitive and benzil causes approximately ninefold increases in both the apparent V and the apparent Km of the enzyme(s). The half-maximal effect on activity was obtained as a 0.3 mM concentration of benzil. The activating effect obtained with benzil was found to be very specific, since a variety of structurally related compounds had little or no effect on microsomal epoxide hydrolase activity. In order to obtain indications for the existence of more than one microsomal epoxide hydrolase the effect of benzil on this activity from rats induced with phenobarbital, 3-methylcholanthrene, 2-acetylaminofluorene, trans-stilbene oxide, and benzil was tested. The differences observed were minor.

Synthesis and physicochemical properties of epoxidized Tmp trioleate by in situ method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Samidin, Salma; Salimon, Jumat

2014-09-03

Tmp trioleate was initially synthesized via esterification of trimetilolprapane and oleic acid (90%) using 1.5% of H{sub 2}SO{sub 4} as a catalyst. The production of Tmp trioleate was observed at 98% (w/w). The iodine value of Tmp trioleate was analyzed for further reaction of epoxidation. Epoxide was important reaction as an intermediate for preparation of chemical modified lubricants from vegetable oils. Finding the best way of epoxidation process will give high quality for further modification of oil instead of reduce the cost and time for the preparation process during reaction of epoxidation. In this study, the epoxidation of unsaturation Tmpmore » trioleate with peroxyformic acid generated in-situ from hydrogen peroxide 30% in H{sub 2}O{sub 2} with formic acid was studied. 95% conversion to oxygen oxirane content (OOC) ring was obtained. The derivatization showed an improvement of the compound's oxidative stability evidenced from pressurized differential scanning calorimetry (PDSC) data which are 177°C to 200°C. Physicochemical properties showed increasing of temperature of flash point from 280°C to 300°C and viscosity index (VI) from 146 to 154. However, the pour point showed increasing temperature which was −58.81°C to −17.32°C. From the data obtained, these derivatives have shown better performance of lubricity properties. Overall, the data indicates that these performances are compatible to the commercial lubricants.« less

Development of epoxide compound from kapok oil for enhanced oil recovery

NASA Astrophysics Data System (ADS)

Anam, M. K.; Supranto; Murachman, B.; Purwono, S.

2017-06-01

Epoxide compound is made by reacting Kapok Oil with acetic acid and hydrogen peroxide with in situ method. The epoxidation reaction was varied at temperatures of 60 °C, 70 °C and 80 °C, while the time of reaction time was varied at 15 minutes, 30 minutes, 60 minutes and 90 minutes. The reaction rate coefficient for the epoxide was obtained as {\\boldsymbol{k}}{\\boldsymbol{=}}{{124}}{\\boldsymbol{,}}{{82}} {{\\exp }} {\\boldsymbol{\\bigg(}}\\frac{{\\boldsymbol-}{{24}}{\\boldsymbol{,}}{{14}}}{{\\boldsymbol{R}}{\\boldsymbol{T}}}{\\boldsymbol{\\bigg)}}. The addition of the epoxide compound 0.5 w/w in the formulation of SLS was able to reduce the IFT value up to 9.95 x 10-2 m N/m. The addition of co-surfactant (1-octanol) was varied between 0.1 and 0.4 of the total mass of the main formulation (SLS + epoxide + water formation). The smallest interfacial tension value is obtained on the addition of co-surfactants as much as 0.2 w/w, with the IFT value is 2.43 x 10-3 m N/m. The effectiveness of the chemicals was tested through micro displacement using artificial porous medium. The experimental results show that some chemicals developed in the laboratory can be used as EOR chemicals. The oil displacement experiments show that as much as 20 to 80 of remaining oil can be recovered by flooding it with the chemicals. The results also show that the oil recovery depends on type of chemicals and chemical concentration.

MODULATION BY IONIC STRENGTH AND SUPERHELICITY OF BENZO[a]PYRENE DIOL EPOXIDE INDUCED DNA ALKYLATION AND UNWINDING

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gamper, Howard B.; Straub, Kenneth; Calvin, Melvin

Superhelical and partially relaxed SV40 DNA were reacted in vitro with (+)7{beta}, 8{alpha}-dihydroxy-9{alpha},10{alpha}-epoxy-7,8,9,10-tetrahydrobenzo[a]pyrene (BaP diol epoxide). The modified DNA contained N{sup 2} guanine and N{sup 6} adeninte hydrocarbon adducts in the ratio 86:14. Superhelical SV40 DNA was approximately 6% more susceptible to modification than partially relaxed viral DNA. Counterions inhibited DNA alkylation by up to 90%, Mg{sup 2+} being 50-fold more effective than Na{sup +}. The sensitivity of covalent binding to helix stability is consistent with a reaction complex in which BaP diol epoxide is intercalated. The superhelical density of the modified DNA substrates was determined electrophoretically relative to partiallymore » relaxed standards and an unwinding angle for the hydrocarbon adducts was calculated. The angle was dependent upon the superhelicity of the DNA molecule and ranged from 330{sup o} to 30{sup o}. This data indicates that the modified base pairs are disrupted and, in the presence of torsional strain, act as centers for the further denaturation of up to 8 adjacent base pairs. In the absence of such strain the alkylation sites have an ordered structure with the attached hydrocarbon probably oriented in the minor or major groove of the helix.« less

Properties of styrene-maleic anhydride copolymers containing wood-based fillers

Treesearch

John Simonsen; Rodney Jacobson; Roger Rowell

1998-01-01

Recycled newsprint (ONP) and dry process aspen fiber were combined with styrene maleic anhydride (SMA) copolymers containing either 7 or 14 percent maleic anhydride. The fiber-filled SMA composites were equivalent or superior to unfilled SMA in strength, stiffness, and notched Izod impact strength. ONP performed surprisingly well as a filler. Unnotched Izod impact...

Characterization of novel soybean-oil-based thermosensitive amphiphilic polymers for drug delivery applications

USDA-ARS?s Scientific Manuscript database

Characterization, aggregation behavior, physical properties and drug-polymer interaction of novel soybean oil-based polymers i.e., hydrolyzed polymers of (epoxidized) soybean oil (HPESO), were studied. The surface tension method was used to determine the critical micelle concentration (CMC). CMC w...

RETENTION OF HALOCARBONS ON A HEXAFLUOROPROPYLENE EPOXIDE-MODIFIED GRAPHITIZED CARBON BLACK - IV. PROPANE- BASED COMPOUNDS

EPA Science Inventory

The retention characteristics of 25 propane-based bromofluorocarbon, chlorocarbon, chlorofluorocarbon, and fluorocarbon fluids have been studied as a function of temperature on a stationary phase consisting of a 5% (m/m) coating of a low-molecular-mass polymer of hexafluoropropyl...

The Molecular Structure of Epoxide Hydrolase B From And Its Complex With Urea-Based Inhibitor

DOE Office of Scientific and Technical Information (OSTI.GOV)

Biswal, B.K.; Morisseau, C.; Garen, G.

2009-05-11

Mycobacterium tuberculosis (Mtb), the intracellular pathogen that infects macrophages primarily, is the causative agent of the infectious disease tuberculosis in humans. The Mtb genome encodes at least six epoxide hydrolases (EHs A to F). EHs convert epoxides to trans-dihydrodiols and have roles in drug metabolism as well as in the processing of signaling molecules. Herein, we report the crystal structures of unbound Mtb EHB and Mtb EHB bound to a potent, low-nanomolar (IC(50) approximately 19 nM) urea-based inhibitor at 2.1 and 2.4 A resolution, respectively. The enzyme is a homodimer; each monomer adopts the classical alpha/beta hydrolase fold that composesmore » the catalytic domain; there is a cap domain that regulates access to the active site. The catalytic triad, comprising Asp104, His333 and Asp302, protrudes from the catalytic domain into the substrate binding cavity between the two domains. The urea portion of the inhibitor is bound in the catalytic cavity, mimicking, in part, the substrate binding; the two urea nitrogen atoms donate hydrogen bonds to the nucleophilic carboxylate of Asp104, and the carbonyl oxygen of the urea moiety receives hydrogen bonds from the phenolic oxygen atoms of Tyr164 and Tyr272. The phenolic oxygen groups of these two residues provide electrophilic assistance during the epoxide hydrolytic cleavage. Upon inhibitor binding, the binding-site residues undergo subtle structural rearrangement. In particular, the side chain of Ile137 exhibits a rotation of around 120 degrees about its C(alpha)-C(beta) bond in order to accommodate the inhibitor. These findings have not only shed light on the enzyme mechanism but also have opened a path for the development of potent inhibitors with good pharmacokinetic profiles against all Mtb EHs of the alpha/beta type.« less

INTERACTION OF BENZO(A)PYRENE DIOL EPOXIDE WITH SVAO MINICHROMOSOMES

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gamper, Howard B.; Yokota, Hisao A.; Bartholomew, James C.

SV40 minichromosomes were reacted with (+)7{beta},8{alpha}-dihydroxy-9{alpha},10{alpha}-epoxy- 7,8,9,10-tetrahydrobenzo[a]pyrene (BaP diol epoxide). Low levels of modification (< 5 DNA adducts/minichromosome) did not detectably alter the structure of the minichromosomes but high levels (> 200 DNA adducts/minichromosome) led to extensive fragmentation. Relative to naked SV40 DNA BaP diol epoxide induced alkylation and strand scission of minichromosomal DNA was reduced or enhanced by factors of 1.5 and 2.0, respectively. The reduction in covalent binding was attributed to the presence of histones, which competed with DNA for the hydrocarbon and reduced the probability of BaP diol epoxide intercalation by tightening the helix. The enhancement ofmore » strand scission was probably due to the catalytic effect of histones on the rate of S-elimination at apurinic sites, although an altered adduct profile or the presence of a repair endonuclease were not excluded. Staphylococcal nuclease digestion indicated that BaP dial epoxide randomly alkylated the minichromosomal DNA. This is in contrast to studies with cellular chromatin where internucleosomal DNA was preferentially modified. Differences in the minichromosomal protein complement were responsible for this altered susceptibility.« less

Functionalization of multi-walled carbon nanotubes by epoxide ring-opening polymerization

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jin Fanlong; Rhee, Kyong Yop; Park, Soo-Jin, E-mail: sjpark@inha.ac.kr

2011-12-15

In this study, covalent functionalization of carbon nanotubes (CNTs) was accomplished by surface-initiated epoxide ring-opening polymerization. FT-IR spectra showed that polyether and epoxide group covalently attached to the sidewalls of CNTs. TGA results indicated that the polyether was successfully grown from the CNT surface, with the final products having a polymer weight percentage of ca. 14-74 wt%. The O/C ratio of CNTs increased significantly from 5.1% to 29.8% after surface functionalization of CNTs. SEM and TEM images of functionalized CNTs exhibited that the tubes were enwrapped by polymer chains with thickness of several nanometers, forming core-shell structures with CNTs atmore » the center. - Graphical abstract: Functionalized CNTs were enwrapped by polymer chains with thickness of several nanometers, forming core-shell structures with CNTs at the center. Highlights: Black-Right-Pointing-Pointer CNTs were functionalized by epoxide ring-opening polymerization. Black-Right-Pointing-Pointer Polyether and epoxide group covalently attached to the sidewalls of CNTs. Black-Right-Pointing-Pointer Functionalized CNTs have a polymer weight percentage of ca. 14-74 wt%. Black-Right-Pointing-Pointer Functionalized CNTs were enwrapped by polymer chains with thickness of several nanometers.« less

Morphology and viscoelastic properties of sealing materials based on EPDM rubber.

PubMed

Milić, J; Aroguz, A; Budinski-Simendić, J; Radicević, R; Prendzov, S

2008-12-01

In this applicative study, the ratio of active and inactive filler loadings was the prime factor for determining the dynamic-mechanical behaviour of ethylene-propylene-diene monomer rubbers. Scanning electron microscopy was used to study the structure of reinforced dense and microcellular elastomeric materials. The effects of filler and blowing agent content on the morphology of composites were investigated. Microcellular samples cured in salt bath show smaller cells and uniform cell size compared with samples cured in hot air. Dynamic-mechanical thermal analysis showed appreciable changes in the viscoelastic properties by increasing active filler content, which could enable tailoring the material properties to suit sealing applications.

Modelling and operation strategies of DLR's large scale thermocline test facility (TESIS)

NASA Astrophysics Data System (ADS)

Odenthal, Christian; Breidenbach, Nils; Bauer, Thomas

2017-06-01

In this work an overview of the TESIS:store thermocline test facility and its current construction status will be given. Based on this, the TESIS:store facility using sensible solid filler material is modelled with a fully transient model, implemented in MATLAB®. Results in terms of the impact of filler site and operation strategies will be presented. While low porosity and small particle diameters for the filler material are beneficial, operation strategy is one key element with potential for optimization. It is shown that plant operators have to ponder between utilization and exergetic efficiency. Different durations of the charging and discharging period enable further potential for optimizations.

Thermal and Mechanical Characteristics of Polymer Composites Based on Epoxy Resin, Aluminium Nanopowders and Boric Acid

NASA Astrophysics Data System (ADS)

Nazarenko, O. B.; Melnikova, T. V.; Visakh, P. M.

2016-01-01

The epoxy polymers are characterized by low thermal stability and high flammability. Nanoparticles are considered to be effective fillers of polymer composites for improving their thermal and functional properties. In this work, the epoxy composites were prepared using epoxy resin ED-20, polyethylene polyamine as a hardener, aluminum nanopowder and boric acid fine powder as flame-retardant filler. The thermal characteristics of the obtained samples were studied using thermogravimetric analysis and differential scanning calorimetry. The mechanical characteristics of epoxy composites were also studied. It was found that an addition of all fillers enhances the thermal stability and mechanical characteristics of the epoxy composites. The best thermal stability showed the epoxy composite filled with boric acid. The highest flexural properties showed the epoxy composite based on the combination of boric acid and aluminum nanopowder.

Synthesis and structure-activity relationship of piperidine-derived non-urea soluble epoxide hydrolase inhibitors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pecic, Stevan; Pakhomova, Svetlana; Newcomer, Marcia E.

2013-09-27

A series of potent amide non-urea inhibitors of soluble epoxide hydrolase (sEH) is disclosed. The inhibition of soluble epoxide hydrolase leads to elevated levels of epoxyeicosatrienoic acids (EETs), and thus inhibitors of sEH represent one of a novel approach to the development of vasodilatory and anti-inflammatory drugs. Structure–activities studies guided optimization of a lead compound, identified through high-throughput screening, gave rise to sub-nanomolar inhibitors of human sEH with stability in human liver microsomal assay suitable for preclinical development.

A Polyoxovanadate-Resorcin[4]arene-Based Porous Metal-Organic Framework as an Efficient Multifunctional Catalyst for the Cycloaddition of CO2 with Epoxides and the Selective Oxidation of Sulfides.

PubMed

Lu, Bing-Bing; Yang, Jin; Liu, Ying-Ying; Ma, Jian-Fang

2017-10-02

In this work, we report a new polyoxovanadate-resorcin[4]arene-based metal-organic framework (PMOF), [Co 2 L 0.5 V 4 O 12 ]·3DMF·5H 2 O (1), assembled with a newly functionalized wheel-like resorcin[4]arene ligand (L). 1 features an elegant porous motif and represents a rare example of PMOFs composed of both a resorcin[4]arene ligand and polyoxovanadate. Remarkably, 1 shows open V sites in the channel, which makes 1 an efficient heterogeneous Lewis acid catalyst for the cycloaddition of carbon dioxide to epoxides with high conversion and selectivity. Strikingly, 1 also exhibits high catalytic activity for the heterogeneous oxidative desulfurization of sulfides. Particularly, the heterogeneous catalyst 1 can be easily separated and reused with good catalytic activity.

Synthesis, reactivity and application studies for different biolubricants

PubMed Central

2014-01-01

Vegetable oils have different unique properties owing to their unique chemical structure. Vegetable oils have a greater ability to lubricate and have higher viscosity indices. Therefore, they are being more closely examined as base oil for biolubricants and functional fluids. In spite of their many advantages, vegetable oils suffer from two major drawbacks of inadequate oxidative stability and poor low-temperature properties, which hinder their utilization as biolubricant base oils. Transforming alkene groups in fatty acids to other stable functional groups could improve the oxidative stability, whereas reducing structural uniformity of the oil by attaching alkyl side chains could improve the low-temperature performance. In that light, the epoxidation of unsaturated fatty acids is very interesting as it can provide diverse side chains arising from the mono- or di-epoxidation of the unsaturated fatty acid. Oxirane ring opening by an acid-catalyzed reaction with a suitable reagent provides interesting polyfunctional compounds. PMID:24612780

Direct characterization of cotton fabrics treated with di-epoxide by nuclear magnetic resonance.

PubMed

Xiao, Min; Chéry, Joronia; Keresztes, Ivan; Zax, David B; Frey, Margaret W

2017-10-15

A non-acid-based, di-functional epoxide, neopentyl glycol diglycidyl ether (NPGDGE), was used to modify cotton fabrics. Direct characterization of the modified cotton was conducted by Nuclear Magnetic Resonance (NMR) without grinding the fabric into a fine powder. NaOH and MgBr 2 were compared in catalyzing the reaction between the epoxide groups of NPGDGE and the hydroxyl groups of cellulose. Possible reaction routes were discussed. Scanning electron microscopy (SEM) images showed that while the MgBr 2 -catalyzed reaction resulted in self-polymerization of NPGDGE, the NaOH-catalyzed reaction did not. Fourier transform infrared spectroscopy (FTIR) showed that at high NaOH concentration cellulose restructures from allomorph I to II. NMR studies verified the incorporation of NPGDGE into cotton fabrics with a clear NMR signal, and confirmed that at higher NaOH concentration the efficiency of grafting of NPGDGE was increased. This demonstrates that use of solid state NMR directly on woven fabric samples can simultaneously characterize chemical modification and crystalline polymorph of cotton. No loss of tensile strength was observed for cotton fabrics modified with NPGDGE. Copyright © 2017 Elsevier Ltd. All rights reserved.

Synthesis of a highly dispersed CuO catalyst on CoAl-HT for the epoxidation of styrene.

PubMed

Hu, Rui; Yang, Pengfei; Pan, Yongning; Li, Yunpeng; He, Yufei; Feng, Junting; Li, Dianqing

2017-10-10

A highly dispersed CuO catalyst was prepared by the deposition-precipitation method and evaluated for the catalytic epoxidation of styrene with tert-butyl hydroperoxide (TBHP) as the oxidant under solvent acetonitrile conditions. Compared with MgAl hydrotalcite (MgAl-HT)-, MgO-, TiO 2 -, C-, and MCM-22-supported catalysts, CuO/CoAl-HT exhibited preferable activity and selectivity towards styrene oxide (72% selectivity at 99.5% styrene conversion) due to its high dispersion of CuO and surface area of Cu. The improved dispersion of CuO/CoAl-HT could be ascribed to the nature of HT support, especially the synergistic effect of acidic and basic sites on the surface, which facilitated the formation of highly dispersed CuO species. A structure-performance relationship study indicated that copper(ii) in CuO was the active site for the epoxidation and oxidation of styrene, and that Cu II of rich electronic density favored the improvement of selectivity of styrene oxide. Based on these results, a reaction mechanism was proposed. Moreover, the preferred catalytic performance of CuO/CoAl-HT could be maintained in five reused cycles.

High-performance polymer/layered silicate nanocomposites

NASA Astrophysics Data System (ADS)

Heidecker, Matthew J.

High-performance layered-silicate nanocomposites of Polycarbonate (PC), poly(ethylene terephthalate) (PET), and their blends were produced via conventional melt-blending techniques. The focus of this thesis was on the fundamentals of dispersion, control of thermal stability, maintenance of melt-blending processing conditions, and on optimization of the composites' mechanical properties via the design of controlled and thermodynamically favorable nano-filler dispersions within the polymer matrices. PET and PC require high temperatures for melt-processing, rendering impractical the use of conventional/commercial organically-modified layered-silicates, since the thermal degradation temperatures of their ammonium surfactants lies below the typical processing temperatures. Thus, different surfactant chemistries must be employed in order to develop melt-processable nanocomposites, also accounting for polymer matrix degradation due to water (PET) or amine compounds (PC). Novel high thermal-stability surfactants were developed and employed in montmorillonite nanocomposites of PET, PC, and PC/PET blends, and were compared to the respective nanocomposites based on conventional quaternary-ammonium modified montmorillonites. Favorable dispersion was achieved in all cases, however, the overall material behavior -- i.e., the combination of crystallization, mechanical properties, and thermal degradation -- was better for the nanocomposites based on the thermally-stable surfactant fillers. Studies were also done to trace, and ultimately limit, the matrix degradation of Polycarbonate/montmorillonite nanocomposites, through varying the montmorillonite surfactant chemistry, processing conditions, and processing additives. Molecular weight degradation was, maybe surprisingly, better controlled in the conventional quaternary ammonium based nanocomposites -- even though the thermal stability of the organically modified montmorillonites was in most cases the lowest. Dependence of the resultant nanocomposites' mechanical properties on the preferential alignment of the montmorillonite nano-platelet was also evaluated. Highly aligned filler platelets did not result in an additional enhancement in mechanical properties. PC/PET blends and their respective PC/PET/montmorillonite nanocomposites were synthesized and compared. The dispersion of the organically modified nano-fillers in the PC/PET blends was controlled via thermodynamic considerations, realized through proper surfactant choice: Nanocomposites in which the layered silicate was preferentially sequestered in the PET phase were designed and synthesized. This preferential dispersion of the nano-filler in the PET phase of the PC/PET blend was insensitive to processing conditions, including approaches employing a master-batch (filler concentrate); regardless of the master-batch matrix, both PC and PET were employed, thermodynamics drove the layered silicate to preferentially migrate to the PET phase of the PC/PET blend. In a second approach, the development of a nanocomposite with controlled PC/PET compatibilization near the montmorillonite platelets, in absence of appreciable transesterification reactions, led to the formation of very high performance nanocomposites. These latter systems, point to an exciting new avenue of future considerations for nanocomposite blends with selective nano-filler dispersions, where performance can be tailored via the controlled preferential dispersion of nano-fillers in one phase, or by filler-induced polymer compatibilization.

Heptachlor epoxide

Integrated Risk Information System (IRIS)

Heptachlor epoxide ; CASRN 1024 - 57 - 3 Human health assessment information on a chemical substance is included in the IRIS database only after a comprehensive review of toxicity data , as outlined in the IRIS assessment development process . Sections I ( Health Hazard Assessments for Noncarcinogen

21 CFR 177.1650 - Polysulfide polymer-polyepoxy resins.

Code of Federal Regulations, 2011 CFR

2011-04-01

...(2-chloroethyl) formal Bis(dichloropropyl) formal Cross-linking agent. Butyl alcohol Solvent. Carbon black (channel process) Chlorinated paraffins Cross-linking agent. Epoxidized linseed oil Epoxidized... monobutyl ether Solvent. Magnesium chloride Methyl isobutyl ketone Solvent. Naphthalene sulfonic acid...

Epoxy resin

DOEpatents

Wilson, Glenn R.; Salyer, Ival O.; Ball, III, George L.

1976-07-13

By mixing one part of a prepolymer containing a polyamine partially polymerized with an organic epoxide and subsequently reacted with a fatty acid containing from 8 to 32 carbon atoms, and then reacting this prepolymer mixture with 3 parts of an organic epoxide, a composition was obtained which made a gas frothable, shear-stable, room temperature curing, low density foam. A particularly advantageous prepolymer was prepared using a polyamine selected from the group consisting of diethylenetriamine, triethylenetetramine, and tetraethylenepentamine, partially polymerized with an organic epoxide having an average molecular weight of about 350 and having an epoxide equivalent of 185 to 192, and reacted with 2-10 weight percent linoleic acid. When one part of this prepolymer was reacted with about three parts of epoxy, and frothed by whipping in air or nitrogen an epoxy foam was produced which could be troweled onto surfaces and into corners or crevices, and subsequently cured, at near ambient temperature, to a strong dimensionally stable foam product.

Persistence and changes in bioavailability of dieldrin, DDE and heptachlor epoxide in earthworms over 45 years

USGS Publications Warehouse

Beyer, W. Nelson; Gale, Robert W.

2013-01-01

The finding of dieldrin (88 ng/g), DDE (52 ng/g), and heptachlor epoxide (19 ng/g) in earthworms from experimental plots after a single moderate application (9 kg/ha) 45 years earlier attests to the remarkable persistence of these compounds in soil and their continued uptake by soil organisms. Half-lives (with 95 % confidence intervals) in earthworms, estimated from exponential decay equations, were as follows: dieldrin 4.9 (4.3-5.7) years, DDE 5.3 (4.7-6.1) years, and heptachlor epoxide 4.3 (3.8-4.9) years. These half-lives were not significantly different from those estimated after 20 years. Concentration factors (dry weight earthworm tissue/dry weight soil) were initially high and decreased mainly during the first 11 years after application. By the end of the study, average concentration factors were 1.5 (dieldrin), 4.0 (DDE), and 1.8 (heptachlor epoxide), respectively.

Multifunctional Graphene-Silicone Elastomer Nanocomposite, Method of Making the Same, and Uses Thereof

NASA Technical Reports Server (NTRS)

Prud'Homme, Robert K. (Inventor); Pan, Shuyang (Inventor); Aksay, Ilhan A. (Inventor)

2018-01-01

A nanocomposite composition having a silicone elastomer matrix having therein a filler loading of greater than 0.05 wt %, based on total nanocomposite weight, wherein the filler is functional graphene sheets (FGS) having a surface area of from 300 sq m/g to 2630 sq m2/g; and a method for producing the nanocomposite and uses thereof.

A screening method based on UV-Visible spectroscopy and multivariate analysis to assess addition of filler juices and water to pomegranate juices.

PubMed

Boggia, Raffaella; Casolino, Maria Chiara; Hysenaj, Vilma; Oliveri, Paolo; Zunin, Paola

2013-10-15

Consumer demand for pomegranate juice has considerably grown, during the last years, for its potential health benefits. Since it is an expensive functional food, cheaper fruit juices addition (i.e., grape and apple juices) or its simple dilution, or polyphenols subtraction are deceptively used. At present, time-consuming analyses are used to control the quality of this product. Furthermore these analyses are expensive and require well-trained analysts. Thus, the purpose of this study was to propose a high-speed and easy-to-use shortcut. Based on UV-VIS spectroscopy and chemometrics, a screening method is proposed to quickly screening some common fillers of pomegranate juice that could decrease the antiradical scavenging capacity of pure products. The analytical method was applied to laboratory prepared juices, to commercial juices and to representative experimental mixtures at different levels of water and filler juices. The outcomes were evaluated by means of multivariate exploratory analysis. The results indicate that the proposed strategy can be a useful screening tool to assess addition of filler juices and water to pomegranate juices. Copyright © 2012 Elsevier Ltd. All rights reserved.

Two approaches for introduction of wheat straw lignin into rigid polyurethane foams

NASA Astrophysics Data System (ADS)

Arshanitsa, A.; Paberza, A.; Vevere, L.; Cabulis, U.; Telysheva, G.

2014-05-01

In present work the BIOLIGNIN{trade mark, serif} obtained in the result of wheat straw organosolv processing in CIMV pilot plant (France) was investigated as a component of rigid polyurethanes (PUR) foam systems. Different separate approaches of lignin introduction into PUR foam system were studied: as filler without chemical preprocessing and as liquid lignopolyol obtained by lignin oxypropylation in alkali conditions. The incorporation of increasing amount of lignin as filler into reference PUR foam systems on the basis of mixture of commercial polyethers Lupranol 3300 and Lupranol 3422 steadily decreased the compression characteristics of foams, their dimensional stability and hydrophobicity. The complete substitution of Lupranol 3300 by lignopolyol increases its cell structure uniformity and dimensional stability and does not reduce the physical-mechanical properties of foam. In both cases the incorporation of lignin into PUR foam leads to the decreasing of maximum values of thermodegradation rates. The lignin filler can be introduced into lignopolyol based PUR foam in higher quantity than in the reference Lupranol based PUR without reduction of compression characteristics of material. In this work the optimal lignin content in the end product - PUR foam as both polyol and filler is 16%.

Abradable dual-density ceramic turbine seal system

NASA Technical Reports Server (NTRS)

Clingman, D. L.; Schechter, B.; Cross, K. R.; Cavanagh, J. R.

1981-01-01

A plasma sprayed dual density ceramic abradable seal system for direct application to the HPT seal shroud of small gas turbine engines. The system concept is based on the thermal barrier coating and depends upon an additional layer of modified density ceramic material adjacent to the gas flow path to provide the desired abradability. This is achieved by codeposition of inert fillers with yttria stabilized zirconia (YSZ) to interrupt the continuity of the zirconia struture. The investigation of a variety of candidate fillers, with hardness values as low as 2 on Moh's scale, led to the conclusion that solid filler materials in combination with a YSZ matrix, regardless of their hardness values, have a propensity for compacting rather than shearing as originally expected. The observed compaction is accompanied by high energy dissipation in the rub interaction, usually resulting in the adhesive transfer of blade material to the stationary seal member. Two YSZ based coating systems which incorported hollow alumino silicate spheres as density reducing agents were surveyed over the entire range of compositions from 100 percent filler to 100 percent YSZ. Abradability and erosion characteristics were determined, hardness and permeability characterized, and engine experience acquired with several system configurations.

Study of gas tungsten arc welding procedures for tantalum alloy T-111 (Ta-8 W-2Hf) plate

NASA Technical Reports Server (NTRS)

Gold, R. E.; Kesterson, R. L.

1973-01-01

Methods of eliminating or reducing underbread cracking in multipass GTA welds in thick T-111 plate were studied. Single V butt welds prepared using experimental filler metal compositions and standard weld procedures resulted in only moderate success in reducing underbread cracking. Subsequent procedural changes incorporating manual welding, slower weld speeds, and three or fewer fill passes resulted in crack-free single V welds only when the filler metal was free of hafnium. The double V joint design with successive fill passes on opposite sides of the joint produced excellent welds. The quality of each weld was determined metallographically since the cracking, when present, was very slight and undetectable using standard NDT techniques. Tensile and bend tests were performed on selected weldments. The inherent filler metal strength and the joint geometry determined the strength of the weldment. Hardness and electron beam microprobe traverses were made on selected specimens with the result that significant filler metal-base metal dilution as well as hafnium segregation was detected. A tentative explanation of T-111 plate underbread cracking is presented based on the intrinsic effects of hafnium in the weldment.

The Effect of Task Duration on Event-Based Prospective Memory: A Multinomial Modeling Approach

PubMed Central

Zhang, Hongxia; Tang, Weihai; Liu, Xiping

2017-01-01

Remembering to perform an action when a specific event occurs is referred to as Event-Based Prospective Memory (EBPM). This study investigated how EBPM performance is affected by task duration by having university students (n = 223) perform an EBPM task that was embedded within an ongoing computer-based color-matching task. For this experiment, we separated the overall task’s duration into the filler task duration and the ongoing task duration. The filler task duration is the length of time between the intention and the beginning of the ongoing task, and the ongoing task duration is the length of time between the beginning of the ongoing task and the appearance of the first Prospective Memory (PM) cue. The filler task duration and ongoing task duration were further divided into three levels: 3, 6, and 9 min. Two factors were then orthogonally manipulated between-subjects using a multinomial processing tree model to separate the effects of different task durations on the two EBPM components. A mediation model was then created to verify whether task duration influences EBPM via self-reminding or discrimination. The results reveal three points. (1) Lengthening the duration of ongoing tasks had a negative effect on EBPM performance while lengthening the duration of the filler task had no significant effect on it. (2) As the filler task was lengthened, both the prospective and retrospective components show a decreasing and then increasing trend. Also, when the ongoing task duration was lengthened, the prospective component decreased while the retrospective component significantly increased. (3) The mediating effect of discrimination between the task duration and EBPM performance was significant. We concluded that different task durations influence EBPM performance through different components with discrimination being the mediator between task duration and EBPM performance. PMID:29163277

The duration of hyaluronidase and optimal timing of hyaluronic acid (HA) filler reinjection after hyaluronidase injection.

PubMed

Kim, H J; Kwon, S B; Whang, K U; Lee, J S; Park, Y L; Lee, S Y

2018-02-01

Hyaluronidase injection is a commonly performed treatment for overcorrection or misplacement of hyaluronic acid (HA) filler. Many patients often wants the HA filler reinjection after the use of hyaluronidase, though the optimal timing of reinjection of HA filler still remains unknown. To provide the optimal time interval between hyaluronidase injections and HA filler reinjections. 6 Sprague-Dawley rats were injected with single monophasic HA filler. 1 week after injection, the injected sites were treated with hyaluronidase. Then, HA fillers were reinjected sequentially with differing time intervals from 30 minutes to 14 days. 1 hour after the reinjection of the last HA filler, all injection sites were excised for histologic evaluation. 3 hours after reinjection of HA filler, the appearance of filler material became evident again, retaining its shape and volume. 6 hours after reinjection, the filler materials restored almost its original volume and there were no significant differences from the positive control. Our data suggest that the hyaluronidase loses its effect in dermis and subcutaneous tissue within 3-6 hours after the injection and successful engraftment of reinjected HA filler can be accomplished 6 hours after the injection.

Chlordane in birds: A study of lethal residues and loss rates

USGS Publications Warehouse

Stickel, L.F.; Stickel, W.H.; McArthur, R.D.; Hughes, D.L.

1979-01-01

Lethal residues of heptachlor epoxide in brains of birds fed heptachlor ranged from 9 to 27 ppm wet weight; residues of oxychlordane in birds fed oxychlordane ranged from 6 to 16 ppm; both were diagnostically distinct from those in equally exposed survivors. In birds fed chlordane, brains of those that died contained less than 30% of these amounts but also contained trans-nonachlor, compound C, and compound E, suggesting additivity or synergism. In birds fed chlordane followed by untreated feed, oxychlordane was most persistent; trans-nonachlor, heptachlor epoxide, and compounds C and E followed, in that order. Loss rates were best expressed on a wet weight basis because lipid-based rates were distorted by seasonal weight gains.

A new approach to the side chain formation of 24-alkyl-22-hydroxy steroids: application to the preparation of early brassinolide biosynthetic precursors.

PubMed

Hurski, Alaksiej L; Zhabinskii, Vladimir N; Khripach, Vladimir A

2012-06-01

A new synthetic route to 22S-hydroxy-24R-methyl steroids has been developed and applied for the preparation of cathasterone, (22S)-hydroxycampesterol, and 6-deoxocathasterone, which are precursors in the early stages of the biosynthesis of brassinolide. The construction of the steroid side chain with the correct stereochemistry at C-24 is based on the use of Claisen rearrangement. The introduction of the 22-hydroxyl group has been achieved by epoxidation of the Δ(22)-double bond, nucleophilic opening of the intermediate mesyl epoxide with sodium sulfide, and desulfurization of the formed tetrahydrothiophenes with Raney nickel. Copyright © 2012 Elsevier Inc. All rights reserved.

Effect of precipitated calcium carbonate--Cellulose nanofibrils composite filler on paper properties.

PubMed

He, Ming; Cho, Byoung-Uk; Won, Jong Myoung

2016-01-20

A new concept of composite filler was developed by using cellulose nanofibrils (CNF), precipitated calcium carbonate (PCC) and cationic starch (C-starch). In this study, cellulose nanofibrils were utilized in two different ways: a PCC-CNF composite filler and a papermaking additive in sheet forming. The aim was to elucidate their effects on flocculation, filler retention and the strength and optical properties of handsheets. The highest filler retention was obtained by using the PCC-CNF composite filler in paper sheets. The paper filled with the composite fillers had much higher bursting and tensile strengths than conventional PCC loading. It was also found that the paper prepared with PCC-CNF composite fillers became denser with increasing the filler content of paper. Copyright © 2015 Elsevier Ltd. All rights reserved.

Rheological properties of cross-linked hyaluronic acid dermal fillers.

PubMed

Santoro, Stefano; Russo, Luisa; Argenzio, Vincenzo; Borzacchiello, Assunta

2011-01-01

Ha based dermal fillers in recent years aroused big interest in the area of cosmetic surgery for the rejuvenation of the dermis. There is not a ideal dermal filler (DF) for all applications and in commerce there are many types of DF that differ for their chemical-physical properties. So the aim of this paper is to correlate the rheological and physical properties of different DF to their clinical effectiveness. In this frame the samples have been subjected to oscillation dynamic rheological and steady shear measurements. Our results demonstrate that the viscoelastic properties of different DF varie strongly also considering fillers of the same family. Furthermore it was found that the materials physical properties influence significantly the performance of dermal filler. In particular the clinical data appear to correlate with the concentration of the polymer and with the product between the concentration and the percent elasticity, so these should be crucial parameters for the clinical performance of DF. So rheological data can be a tool to have an indication on the efficacy and longevity of DF but it has to be considered that production technology, in-vivo-conditions, injector skills and experience influence them also significantly.

Enhanced lithium battery with polyethylene oxide-based electrolyte containing silane-Al2 O3 ceramic filler.

PubMed

Zewde, Berhanu W; Admassie, Shimelis; Zimmermann, Jutta; Isfort, Christian Schulze; Scrosati, Bruno; Hassoun, Jusef

2013-08-01

A solid polymer electrolyte prepared by using a solvent-free, scalable technique is reported. The membrane is formed by low-energy ball milling followed by hot-pressing of dry powdered polyethylene oxide polymer, LiCF3 SO3 salt, and silane-treated Al2 O3 (Al2 O3 -ST) ceramic filler. The effects of the ceramic fillers on the properties of the ionically conducting solid electrolyte membrane are characterized by using electrochemical impedance spectroscopy, XRD, differential scanning calorimeter, SEM, and galvanostatic cycling in lithium cells with a LiFePO4 cathode. We demonstrate that the membrane containing Al2 O3 -ST ceramic filler performs well in terms of ionic conductivity, thermal properties, and lithium transference number. Furthermore, we show that the lithium cells, which use the new electrolyte together with the LiFePO4 electrode, operate within 65 and 90 °C with high efficiency and long cycle life. Hence, the Al2 O3 -ST ceramic can be efficiently used as a ceramic filler to enhance the performance of solid polymer electrolytes in lithium batteries. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Mechanical and optical characterization of bio-nanocomposite from pineapple leaf fiber material for food packaging

NASA Astrophysics Data System (ADS)

Nikmatin, Siti; Rudwiyanti, Jerry R.; Prasetyo, Kurnia W.; Yedi, Dwi A.

2015-01-01

The utilization of Bio-nanocomposite material that was derived from pineapple leaf fiber as filler and tapioca starch with plasticizer glycerol as a matrix for food packaging can reduce the use of plastic that usually was made from petroleum materials. It is important to develop and producethis environmental friendly plastic because of limited availability of petroleum nowadays. The process of synthesize and characterization tapioca starch with the plasticizer glycerol bionanocomposites using print method had been conducted. There were 3 samples with different filler concentration variation; 3%, 4% and 5%.The results of mechanical test from each sample showed that bio-nanocomposite with 5% filler concentration was the optimum sample with 4.6320 MPa for tensile strength test and 24.87% for the elongation test. Based on the result of optical test for each sample was gained that along with the increasing of concentration filler would make the absorbance value of the sample became decreased, bio-nanocomposite with 5% filler concentration had several peaks with low absorbance values. The first peak was in 253 nm of wavelength regionwith absorbance of 0.131%, and the second peak was in 343 nmwavelength region and absorbance was 0.087%.

Rethinking the Role of Nitroglycerin Ointment in Ischemic Vascular Filler Complications: An Animal Model With ICG Imaging.

PubMed

Hwang, Catherine J; Morgan, Payam V; Pimentel, Aline; Sayre, James W; Goldberg, Robert A; Duckwiler, Gary

2016-01-01

Soft tissue dermal fillers, both temporary and permanent, are used frequently in facial rejuvenation. As the use of fillers increases, ischemic complications including skin necrosis are becoming more prevalent. In the literature, topical nitroglycerin paste has been recommended in the early treatment of patients presenting with ischemia. The purpose of this study was to evaluate the vascular perfusion effects of topical nitroglycerin paste in an animal model using indocyanine green (ICG) imaging. After Animal Research Committee approval, a rabbit ear model was used to create filler-associated skin ischemia. Ischemia was confirmed to occur after intra-arterial occlusion. Four commonly used soft tissue fillers were injected intra-arterially: Radiesse (Merz USA, Greensboro NC), Restylane (Galderma, Ft. Worth, TX), Juvederm Ultra (Allergan, Irvine CA), Belotero (Merz USA, Greensboro NC) (0.1 ml). A total of 15 ears were used, 1 control and 4 experimental per product. Thirty minutes after occlusion, nitroglycerin ointment USP, 2%(Nitro-Bid) was applied topically to the experimental ears. Vascular perfusion was evaluated with the SPY System (Novadaq Inc.) using ICG imaging. Perfusion images were obtained at baseline, immediately after, and 30 minutes after intra-arterial filler injection, and at 30, 60, 90, and 120 minutes after application of topical nitroglycerin ointment. In this rabbit ear model, no statistically significant improvement in perfusion was noted after topical application of nitroglycerin paste with ICG imaging. In addition, the skin of the rabbit ear post-nitroglycerin ointment appeared to have more of a congested appearance than the controls. Ischemic filler complications are becoming increasingly prevalent. Practitioners often treat these complications with topical nitroglycerin paste based on the knowledge that topical nitroglycerin causes vasodilation. In filler-induced tissue ischemia, however, filler product is present within arterioles. Theoretically, applying nitroglycerin paste, at least early, may not improve perfusion and could worsen ischemia with dilation of vessels and further propagation of product into the smaller arterioles and capillaries. In addition, nitroglycerin paste has systemic effects, including hypotension and dizziness, which may not be tolerated by some patients. Therefore, the authors caution the use of topical nitroglycerin paste in patients presenting with filler-associated ischemia. Further studies in the best treatment algorithms for patients presenting with ischemic complications need to be performed.

Stereoselective Epoxidation of 4-Deoxypentenosides: A Polarized-πModel

PubMed Central

Cheng, Gang; Boulineau, Fabien P.; Liew, Siong-Tern; Shi, Qicun; Wenthold, Paul G.; Wei, Alexander

2008-01-01

The high facioselectivity in the epoxidation of 4-deoxypentenosides (4-DPs) by dimethyldioxirane (DMDO) correlates with a stereoelectronic bias in the 4-DPs’ ground-state conformations, as elucidated by polarized-π frontier molecular orbital (PPFMO) analysis. PMID:16986946

RETENTION OF HALOCARBONS ON A HEXAFLUOROPROPYLENE-EPOXIDE MODIFIED GRAPHITIZED CARBON BLACK, PART 5: HEAVIER ETHANE- AND ETHENE-BASED COMPOUNDS

EPA Science Inventory

The paper gives results of a study of the retention characteristics of 13 heavier ethane-based and 8 ethene-based halocarbon fluids related to alternative refrigerant research as a function of temperature on a stationary phase consisting of a 5% (by mass) coating of a low molecul...

Preparation of hybrid nano biocomposite κ-carrageenan/cellulose nanocrystal/nanoclay

NASA Astrophysics Data System (ADS)

Zakuwan, Siti Zarina; Ahmad, Ishak; Ramli, Nazaruddin

2013-11-01

Biodegradable composites film based on κ-carrageenan and nano particles as filler was prepared to study the mechanical strength of carrageenan composites. Solution casting technique was used to prepare_this biocomposite. Preparation of composite film and nano filler involve two stages, preparation of cellulose nanocrystals (CNC) from kenaf with alkali treatment, bleaching, and hydrolysis followed by the preparation of two types of nano composite. Tensile test was carried on the composite film based on κ-carrageenan with the variation percentage of CNC and nano clay to obtain the optimum CNC and nano clay loading. After that hybrid nano-biocomposite film based on κ-carrageenan with the variation percentage of CNC/nano clay (OMMT) according to optimum value of composite carrageenan/CNC and composite carrageenan/nano clay film was prepared. The effect of nano filler on the mechanical properties of carrageenan films was examined. κ-carrageenan biocomposite increased with the optimum at 4% CNC and nano clay composition. Additional improvement of tensile strength with hybridization of CNC and nanoclay indicated better mechanical properties.

Characteristics of low polymerization shrinkage flowable resin composites in newly-developed cavity base materials for bulk filling technique.

PubMed

Nitta, Keiko; Nomoto, Rie; Tsubota, Yuji; Tsuchikawa, Masuji; Hayakawa, Tohru

2017-11-29

The purpose of this study was to evaluate polymerization shrinkage and other physical properties of newly-developed cavity base materials for bulk filling technique, with the brand name BULK BASE (BBS). Polymerization shrinkage was measured according to ISO/FDIS 17304. BBS showed the significantly lowest polymerization shrinkage and significantly higher depth of cure than conventional flowable resin composites (p<0.05). The Knoop hardness, flexural strength and elastic modulus of that were significantly lower than conventional flowable resin composites (p<0.05). BBS had the significantly greatest filler content (p<0.05). SEM images of the surface showed failure of fillers. The lowest polymerization shrinkage was due to the incorporation of a new type of low shrinkage monomer, which has urethane moieties. There were no clear correlations between inorganic filler contents and polymerization shrinkage, flexural strength and elastic modulus. In conclusion, the low polymerization shrinkage of BBS will be useful for cavity treatment in dental clinics.

Welding of nickel-base superalloys having a nil-ductility range

NASA Technical Reports Server (NTRS)

Smashey, Russell W. (Inventor); Kelly, Thomas J. (Inventor); Snyder, John H. (Inventor); Sheranko, Ronald L. (Inventor)

1999-01-01

An article made of a nickel-base superalloy having a nil-ductility range from the solidus temperature of the alloy to about 600.degree. F. below the solidus temperature is welded, as for example in the weld repair of surface cracks, by removing foreign matter from the area to be welded, first stress relieving the article, adjusting the temperature of the article to a welding temperature of from about 1800.degree. F. to about 2100.degree. F., welding a preselected area in an inert atmosphere at the welding temperature, and second stress relieving the article. Welding is preferably accomplished by striking an arc in the preselected area so as to locally melt the alloy in the preselected area, providing a filler metal having the same composition as the nickel-based superalloy of the article, and feeding the filler metal into the arc so that the filler metal is melted and fused with the article to form a weldment upon solidification.

Reuse of EAF Slag as Reinforcing Filler for Polypropylene Matrix Composites

NASA Astrophysics Data System (ADS)

Cornacchia, G.; Agnelli, S.; Gelfi, M.; Ramorino, G.; Roberti, R.

2015-06-01

Electric-arc furnace (EAF) slag, the by-product of steel fabricated at the EAF, is in most cases still sent to dumps, with serious environmental consequences. This work shows an innovative, economically convenient application for EAF slag: its use as reinforcing filler for polypropylene. Composites based on polypropylene containing 10-40 wt.% of EAF slag particles were prepared by melt compounding followed by injection molding. A physical-chemical analysis of the EAF slag was performed to determine microstructural features and main component phases. Leaching tests demonstrated that, although EAF slag can release small amounts of toxic elements, such as heavy metals, incorporating such material into the polymeric matrix immobilizes the heavy metals inside that matrix. The mechanical characterization of the polymer-based composites was performed. Incorporating EAF slag particles raises the Young's modulus and the tensile strength at yield, whereas elongation at break and the impact strength of the polymer-based composite are significantly reduced only when large amounts of filler are added, i.e., 30% or more.

Preventing the Complications Associated with the Use of Dermal Fillers in Facial Aesthetic Procedures: An Expert Group Consensus Report.

PubMed

Urdiales-Gálvez, Fernando; Delgado, Nuria Escoda; Figueiredo, Vitor; Lajo-Plaza, José V; Mira, Mar; Ortíz-Martí, Francisco; Del Rio-Reyes, Rosa; Romero-Álvarez, Nazaret; Del Cueto, Sofía Ruiz; Segurado, María A; Rebenaque, Cristina Villanueva

2017-06-01

The use of dermal fillers in minimally invasive facial aesthetic procedures has become increasingly popular of late, yet as the indications and the number of procedures performed increase, the number of complications is also likely to increase. Paying special attention to specific patient characteristics and to the technique used can do much to avoid these complications. Indeed, a well-trained physician can also minimize the impact of such problems when they do occur. A multidisciplinary group of experts in aesthetic treatments reviewed the main factors associated with the complications that arise when using dermal fillers. A search of English, French and Spanish language articles in PubMed was performed using the terms "complications" OR "soft filler complications" OR "injectable complications" AND "dermal fillers". An initial document was drafted that reflected the complications identified and recommendations as to how they should be handled. This document was then reviewed and modified by the expert panel, until a final text was agreed upon and validated. The panel addressed consensus recommendations about the preparation, the procedure and the post-procedural care. The panel considered it crucial to obtain an accurate medical history to prevent potential complications. An additional clinical assessment, including standardized photography, is also crucial to evaluate the outcomes and prevent potential complications. Furthermore, the state of the operating theatre, the patient's health status and the preparation of the skin are critical to prevent superficial soft tissue infections. Finally, selecting the appropriate technique, based on the physician's experience, as well as the characteristics of the patient and filler, helps to ensure successful outcomes and limits the complications. This consensus document provides key elements to help clinicians who are starting to use dermal fillers to employ standard procedures and to understand how best to prevent potential complications of the treatment. This journal requires that authors assign a level of evidence to each article. For a full description of these Evidence-Based Medicine ratings, please refer to the Table of Contents or the online Instructions to Authors www.springer.com/00266 .

Numerical Investigation of T-joints with 3D Four Directional Braided Composite Fillers Under Tensile Loading

NASA Astrophysics Data System (ADS)

Li, Xiao-kang; Liu, Zhen-guo; Hu, Long; Wang, Yi-bo; Lei, Bing; Huang, Xiang

2017-02-01

Numerical studied on T-joints with three-dimensional four directional (3D4D) braided composite fillers was presented in this article. Compared with conventional unidirectional prepreg fillers, the 3D braided composite fillers have excellent ability to prevent crack from penetrating trigone fillers, which constantly occurred in the conventional fillers. Meanwhile, the 3D braided composite fillers had higher fiber volume fraction and eliminated the fiber folding problem in unidirectional prepreg fillers. The braiding technology and mechanical performance of 3D4D braided fillers were studied. The numerical model of carbon fiber T-joints with 3D4D braided composite fillers was built by finite element analysis software. The damage formation, extension and failing process of T-joints with 3D4D braided fillers under tensile load were investigated. Further investigation was extended to the effect of 3D4D braided fillers with different braiding angles on mechanical behavior of the T-joints. The study results revealed that the filling area was the weakest part of the T-joints where the damage first appeared and the crack then rapidly spread to the glue film around the filling area and the interface between over-laminate and soleplate. The 3D4D braided fillers were undamaged and the braiding angle change induced a little effect on the bearing capacity of T-joints.

Dermal Filler Injection: A Novel Approach for Limiting Infarct Expansion

PubMed Central

Ryan, Liam P.; Matsuzaki, Kanji; Noma, Mio; Jackson, Benjamin M.; Eperjesi, Thomas J.; Plappert, Theodore J.; St. John-Sutton, Martin G.; Gorman, Joseph H.; Gorman, Robert C.

2011-01-01

Background Early infarct expansion after coronary occlusion compromises contractile function in perfused myocardial regions and promotes adverse long-term left ventricular (LV) remodeling. We hypothesized that injection of a tissue-expanding dermal filler material into a myocardial infarction (MI) would attenuate infarct expansion and limit LV remodeling. Methods Fifteen sheep were subjected to an anteroapical MI involving approximately 20% of the LV followed by the injection of 1.3 mL of a calcium hydroxyapatite–based dermal filler into the infarct. Real-time three-dimensional echocardiography was performed at baseline, 30 minutes after MI, and 15 minutes after injection to assess infarct expansion. Sixteen additional sheep were subjected to the same infarction and followed echocardiographically and hemodynamically for 4 weeks after MI to assess chronic remodeling. Eight animals had injection with dermal filler as described above immediately after MI, and 8 animals were injected with an equal amount of saline solution. Results All animals exhibited infarct expansion soon after coronary occlusion. The regional ejection fraction of the apex became negative after infarction, consistent with systolic dyskinesia. Injection of the dermal filler converted the apical wall motion from dyskinetic to akinetic and resulted immediately in significant decreases in global, regional, and segmental LV volumes. Chronically, relative to saline control, dermal filler injection significantly reduced LV end-systolic volume (62.2 ± 3.6 mL versus 44.5 ± 3.9 mL; p < 0.05) and improved global ejection fraction (0.295 ± 0.016 versus 0.373 ± 0.017; p < 0.05) at 4 weeks after infarction. Conclusions Injection of an acellular dermal filler into an MI immediately after coronary occlusion reduces early infarct expansion and limits chronic LV remodeling. PMID:19101288

Efficacy and Safety of a Hyaluronic Acid Filler to Correct Aesthetically Detracting or Deficient Features of the Asian Nose: A Prospective, Open-Label, Long-Term Study

PubMed Central

Liew, Steven; Scamp, Terrence; de Maio, Mauricio; Halstead, Michael; Johnston, Nicole; Silberberg, Michael; Rogers, John D.

2016-01-01

Background There is increasing interest among patients and plastic surgeons for alternatives to rhinoplasty, a common surgical procedure performed in Asia. Objectives To evaluate the safety, efficacy, and longevity of a hyaluronic acid filler in the correction of aesthetically detracting or deficient features of the Asian nose. Methods Twenty-nine carefully screened Asian patients had their noses corrected with the study filler (Juvéderm VOLUMA [Allergan plc, Dublin, Ireland] with lidocaine injectable gel), reflecting individualized treatment goals and utilizing a standardized injection procedure, and were followed for over 12 months. Results A clinically meaningful correction (≥1 grade improvement on the Assessment of Aesthetic Improvement Scale) was achieved in 27 (93.1%) patients at the first follow-up visit. This was maintained in 28 (96.6%) patients at the final visit, based on the independent assessments of a central non-injecting physician and the patients. At this final visit, 23 (79.3%) patients were satisfied or very satisfied with the study filler and 25 (86.2%) would recommend it to others. In this small series of patients, there were no serious adverse events (AEs), with all treatment-related AEs being mild to moderate, transient injection site reactions, unrelated to the study filler. Conclusions Using specific eligibility criteria, individualized treatment goals, and a standardized injection procedure, the study filler corrected aesthetically detracting or deficient features of the Asian nose, with the therapeutic effects lasting for over 12 months, consistent with a high degree of patient satisfaction. This study supports the safety and efficacy of this HA filler for specific nose augmentation procedures in selected Asian patients. Level of Evidence: 3 Therapeutic PMID:27301371

Thermal Conductivity of Epoxy Resin Composites Filled with Combustion Synthesized h-BN Particles.

PubMed

Chung, Shyan-Lung; Lin, Jeng-Shung

2016-05-20

The thermal conductivity of epoxy resin composites filled with combustion-synthesized hexagonal boron nitride (h-BN) particles was investigated. The mixing of the composite constituents was carried out by either a dry method (involving no use of solvent) for low filler loadings or a solvent method (using acetone as solvent) for higher filler loadings. It was found that surface treatment of the h-BN particles using the silane 3-glycidoxypropyltrimethoxysilane (GPTMS) increases the thermal conductivity of the resultant composites in a lesser amount compared to the values reported by other studies. This was explained by the fact that the combustion synthesized h-BN particles contain less -OH or active sites on the surface, thus adsorbing less amounts of GPTMS. However, the thermal conductivity of the composites filled with the combustion synthesized h-BN was found to be comparable to that with commercially available h-BN reported in other studies. The thermal conductivity of the composites was found to be higher when larger h-BN particles were used. The thermal conductivity was also found to increase with increasing filler content to a maximum and then begin to decrease with further increases in this content. In addition to the effect of higher porosity at higher filler contents, more horizontally oriented h-BN particles formed at higher filler loadings (perhaps due to pressing during formation of the composites) were suggested to be a factor causing this decrease of the thermal conductivity. The measured thermal conductivities were compared to theoretical predictions based on the Nielsen and Lewis theory. The theoretical predictions were found to be lower than the experimental values at low filler contents (< 60 vol %) and became increasing higher than the experimental values at high filler contents (> 60 vol %).

Properties, sustainability and elevated temperature behavior of concrete containing Portland limestone cement

NASA Astrophysics Data System (ADS)

El-Hawary, Moetaz; Ahmed, Mahmoud

2017-09-01

The utilization of some type of cheap filler as partial cement replacement is an effective way of improving concrete sustainability. With the recent trends to reduce water to cement ratio and improve compaction, there is no enough space or water for complete hydration of cement. This means that actually, a portion of mixed cement acts as expensive filler. Replacing this portion with cheaper filler that requires less energy to produce is, therefore, beneficial. Crushed limestone is the most promising filler. This work is to investigate the effect of the amount of limestone fillers on the sustainability and the fresh and mechanical properties of the resulting concrete. A rich mix is designed with a low water/cement ratio of 0.4. Lime is introduced as a replacement percentage of cement. Ratios of 0, 10, 20 and 30% were used. Slump, compressive strength, specific gravity and water absorption are evaluated for every mix. In addition, the effect of the amount of lime on the residual strength of concrete subjected to elevated temperatures is also investigated. Samples are subjected to six different temperature stations of 20, 100, 200, 300, 500 and 700°C for six hours before being cooled and subsequently tested for compressive strength and specific gravity. Sustainability of the tested mixes is evaluated through reductions in the emitted carbon dioxide, energy and reduction in cost. Based on the annual use of concrete in Kuwait, the sustainability benefits resulting from the use of limestone filler in Kuwait are evaluated and assessed. The paper is concluded with the recommendation of the use of 15% limestone filler as partial cement replacement where the properties and the behavior under high temperature of the resulting concrete are almost the same as those of conventional concrete with considerable cost and sustainability benefits.

Water absorption and biodegradation kinetics of highly filled EOC-FS biocomposites

NASA Astrophysics Data System (ADS)

Zykova, A. K.; Pantyukhov, P. V.; Platov, Yu. T.; Bobojonova, G. A.; Ramos, C. Chaverri; Popov, A. A.

2017-12-01

The paper analyzes the water absorption and biodegradation kinetics in highly filled biocomposites based on ethylene-octene copolymer (EOC) and oil flax straw (FS). It is shown that adding the filler to EOC increases the water absorption from 0 to 22%. The tendency can be explained both by the low interfacial adhesion of EOC to FS and by the hydrophilic nature of the filler. According to biodegradation tests (10 months), the mass of pure EOC remains unchanged, suggesting that it fails to biodegrade in the environment. Increasing the filler content increases the weight loss of the composites and the degree of microbiological contamination (fungi filaments, bacteria) as evidenced by optical microscopy.

Teaching Green Chemistry with Epoxidized Soybean Oil

ERIC Educational Resources Information Center

Barcena, Homar; Tuachi, Abraham; Zhang, Yuanzhuo

2017-01-01

The synthesis of epoxidized soybean oil (ESO) provides students a vantage point on the application of green chemistry principles in a series of experiments. Qualitative tests review the reactions of alkenes, whereas spectroscopic analyses provide insight in monitoring functional group transformations.

40 CFR 721.2685 - Polyisobutene epoxide (generic).

Code of Federal Regulations, 2010 CFR

2010-07-01

....2685 Section 721.2685 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) TOXIC SUBSTANCES CONTROL ACT SIGNIFICANT NEW USES OF CHEMICAL SUBSTANCES Significant New Uses for Specific Chemical Substances § 721.2685 Polyisobutene epoxide (generic). (a) Chemical substances and significant new uses...

Ring-Opening Copolymerization of Epoxides and Cyclic Anhydrides with Discrete Metal Complexes: Structure-Property Relationships.

PubMed

Longo, Julie M; Sanford, Maria J; Coates, Geoffrey W

2016-12-28

Polyesters synthesized through the alternating copolymerization of epoxides and cyclic anhydrides compose a growing class of polymers that exhibit an impressive array of chemical and physical properties. Because they are synthesized through the chain-growth polymerization of two variable monomers, their syntheses can be controlled by discrete metal complexes, and the resulting materials vary widely in their functionality and physical properties. This polymer-focused review gives a perspective on the current state of the field of epoxide/anhydride copolymerization mediated by discrete catalysts and the relationships between the structures and properties of these polyesters.

Biosynthetic machinery of ionophore polyether lasalocid: enzymatic construction of polyether skeleton.

PubMed

Minami, Atsushi; Oguri, Hiroki; Watanabe, Kenji; Oikawa, Hideaki

2013-08-01

Diversity of natural polycyclic polyethers originated from very simple yet versatile strategy consisting of epoxidation of linear polyene followed by epoxide opening cascade. To understand two-step enzymatic transformations at molecular basis, a flavin containing monooxygenase (EPX) Lsd18 and an epoxide hydrolase (EH) Lsd19 were selected as model enzymes for extensive investigation on substrate specificity, catalytic mechanism, cofactor requirement and crystal structure. This pioneering study on prototypical lasalocid EPX and EH provides insight into detailed mechanism of ionophore polyether assembly machinery and clarified remaining issues for polyether biosynthesis. Copyright © 2013 Elsevier Ltd. All rights reserved.

Evaluation of in vitro anticancer activity of Ocimum basilicum, Alhagi maurorum, Calendula officinalis and their parasite Cuscuta campestris.

PubMed

Behbahani, Mandana

2014-01-01

The present investigation was carried out to study the relationship between presence of cytotoxic compounds in Ocimum basilicum, Alhagi maurorum, Calendula officinalis and their parasite Cuscuta campestris. The cytotoxic activity of the pure compounds was performed by MTT assay against breast cancer cell lines (MCF-7 and MDA-MB-231) and normal breast cell line (MCF 10A). The induction of apoptosis was measured by the expression levels of p53, bcl-2, bax and caspase-3 genes using quantitative Real Time PCR. Three active fractions were detected by nuclear magnetic resonance as lutein, lupeol and eugenol, respectively, in C. officinalis, A. maurorum and O. basilicum. These compounds and their epoxidized forms were also detected in their parasite C. campestris. The cytotoxic activity of lutein epoxide, lupeol epoxide and eugenol epoxide was significantly more than lutein, lupeol and eugenol. The mRNA expression level of p53, caspase-3 and bax genes were increased in both cancer cells treated with all pure compounds. However, bcl-2 gene expression decreased in treated breast cancer cells. In conclusion, all the data indicated that the epoxide forms of lupeol, lutein and eugenol are potential drug candidates for inducing apoptosis in human breast cancer cells.

Evaluation of In Vitro Anticancer Activity of Ocimum Basilicum, Alhagi Maurorum, Calendula Officinalis and Their Parasite Cuscuta Campestris

PubMed Central

Behbahani, Mandana

2014-01-01

The present investigation was carried out to study the relationship between presence of cytotoxic compounds in Ocimum basilicum, Alhagi maurorum, Calendula officinalis and their parasite Cuscuta campestris. The cytotoxic activity of the pure compounds was performed by MTT assay against breast cancer cell lines (MCF-7 and MDA-MB-231) and normal breast cell line (MCF 10A). The induction of apoptosis was measured by the expression levels of p53, bcl-2, bax and caspase-3 genes using quantitative Real Time PCR. Three active fractions were detected by nuclear magnetic resonance as lutein, lupeol and eugenol, respectively, in C. officinalis, A. maurorum and O. basilicum. These compounds and their epoxidized forms were also detected in their parasite C. campestris. The cytotoxic activity of lutein epoxide, lupeol epoxide and eugenol epoxide was significantly more than lutein, lupeol and eugenol. The mRNA expression level of p53, caspase-3 and bax genes were increased in both cancer cells treated with all pure compounds. However, bcl-2 gene expression decreased in treated breast cancer cells. In conclusion, all the data indicated that the epoxide forms of lupeol, lutein and eugenol are potential drug candidates for inducing apoptosis in human breast cancer cells. PMID:25548920

Interaction of water, alkyl hydroperoxide, and allylic alcohol with a single-site homogeneous Ti-Si epoxidation catalyst: A spectroscopic and computational study.

PubMed

Urakawa, Atsushi; Bürgi, Thomas; Skrabal, Peter; Bangerter, Felix; Baiker, Alfons

2005-02-17

Tetrakis(trimethylsiloxy)titanium (TTMST, Ti(OSiMe3)4) possesses an isolated Ti center and is a highly active homogeneous catalyst in epoxidation of various olefins. The structure of TTMST resembles that of the active sites in some heterogeneous Ti-Si epoxidation catalysts, especially silylated titania-silica mixed oxides. Water cleaves the Ti-O-Si bond and deactivates the catalyst. An alkyl hydroperoxide, TBHP (tert-butyl hydroperoxide), does not cleave the Ti-O-Si bond, but interacts via weak hydrogen-bonding as supported by NMR, DOSY, IR, and computational studies. ATR-IR spectroscopy combined with computational investigations shows that more than one, that is, up to four, TBHP can undergo hydrogen-bonding with TTMST, leading to the activation of the O-O bond of TBHP. The greater the number of TBHP molecules that form hydrogen bonds to TTMST, the more electrophilic the O-O bond becomes, and the more active the complex is for epoxidation. An allylic alcohol, 2-cyclohexen-1-ol, does not interact strongly with TTMST, but the interaction is prominent when it interacts with the TTMST-TBHP complex. On the basis of the experimental and theoretical findings, a hydrogen-bond-assisted epoxidation mechanism of TTMST is suggested.

Can the epoxides of cinnamyl alcohol and cinnamal show new cases of contact allergy?

PubMed

Hagvall, Lina; Niklasson, Ida B; Luthman, Kristina; Karlberg, Ann-Therese

2018-06-01

Cinnamyl alcohol is considered to be a prohapten and prehapten with cinnamal as the main metabolite. However, many individuals who are allergic to cinnamyl alcohol do not react to cinnamal. Sensitizing epoxides of cinnamyl alcohol and cinnamal have been identified as metabolites and autoxidation products of cinnamyl alcohol. To investigate the clinical relevance of contact allergy to epoxycinnamyl alcohol and epoxycinnamal. Irritative effects of the epoxides were investigated in 12 dermatitis patients. Epoxycinnamyl alcohol and epoxycinnamal were patch tested in 393 and 390 consecutive patients, respectively. In parallel, cinnamyl alcohol and cinnamal were patch tested in 607 and 616 patients, respectively. Both epoxides were irritants, but no more positive reactions were detected than when testing was performed with cinnamyl alcohol and cinnamal. Late allergic reactions to epoxycinnamyl alcohol were observed. In general, patients with late reactions showed doubtful or positive reactions to cinnamal and fragrance mix I at regular patch testing. The investigated epoxides are not important haptens in contact allergy to cinnamon fragrance. The high frequency of fragrance allergy among patients included in the irritancy study showed the difficulty of suspecting fragrance allergy on the basis of history; patch testing broadly with fragrance compounds is therefore important. © 2018 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

Effect of Storage in Distilled Water for Three Months on the Antimicrobial Properties of Poly(methyl methacrylate) Denture Base Material Doped with Inorganic Filler

PubMed Central

Chladek, Grzegorz; Basa, Katarzyna; Mertas, Anna; Pakieła, Wojciech; Żmudzki, Jarosław; Bobela, Elżbieta; Król, Wojciech

2016-01-01

The colonization of poly(methyl methacrylate) (PMMA) denture base materials by pathogenic microorganisms is a major problem associated with the use of prostheses, and the incorporation of antimicrobial fillers is a method of improving the antimicrobial properties of these materials. Numerous studies have demonstrated the initial in vitro antimicrobial effectiveness of this type of material; however, reports demonstrating the stability of these fillers over longer periods are not available. In this study, silver sodium hydrogen zirconium phosphate was introduced into the powder component of a PMMA denture base material at concentrations of 0.25%, 0.5%, 1%, 2%, 4%, and 8% (w/w). The survival rates of the gram-positive bacterium Staphylococcus aureus, gram-negative bacterium Escherichia coli and yeast-type fungus Candida albicans were established after fungal or bacterial suspensions were incubated with samples that had been previously stored in distilled water. Storage over a three-month period led to the progressive reduction of the initial antimicrobial properties. The results of this study suggest that additional microbiological tests should be conducted for materials that are treated with antimicrobial fillers and intended for long-term use. Future long-term studies of the migration of silver ions from the polymer matrix and the influence of different media on this ion emission are required. PMID:28773451

Multifunctional Graphene-Silicone Elastomer Nanocomposite, Method of Making the Same, and Uses Thereof

NASA Technical Reports Server (NTRS)

Aksay, Ilhan A. (Inventor); Pan, Shuyang (Inventor); Prud'Homme, Robert K. (Inventor)

2016-01-01

A nanocomposite composition having a silicone elastomer matrix having therein a filler loading of greater than 0.05 weight percentage, based on total nanocomposite weight, wherein the filler is functional graphene sheets (FGS) having a surface area of from 300 square meters per gram to 2630 square meters per gram; and a method for producing the nanocomposite and uses thereof.

Determination of mineral oil aromatic hydrocarbons in edible oils and fats by online liquid chromatography-gas chromatography-flame ionization detection - Evaluation of automated removal strategies for biogenic olefins.

PubMed

Nestola, Marco; Schmidt, Torsten C

2017-07-07

The determination of mineral oil aromatic hydrocarbons (MOAH) in foodstuffs gained in importance over the last years as carcinogenicity cannot be excluded for certain MOAH. The existence of olefins in foodstuffs, such as edible oils and fats, can be problematic for the determination of MOAH by LC-GC-FID. Removal of these interfering substances by HPLC based on polarity differences is not possible. During gas chromatographic separation heavily overloaded peaks are observed rendering the detection of small mineral oil contaminations almost impossible. Therefore, removal of these olefins is necessary before subjection of the sample to LC-GC-FID. Epoxidation of olefins to increase their polarity proved to be a valuable tool in the past. Precision and trueness of the results as shown in a collaborative trial, however, are relying on exact reaction conditions. Additionally, it is known that certain MOAH are oxidized during epoxidation and therefore get lost. In the scope of this work, hydroboration, bromohydrin reaction, and epoxidation were examined for their potential for derivatization of unsaturated hydrocarbons with increased robustness and higher recovery of MOAH. Epoxidation by meta-chloroperoxybenzoic acid (mCPBA) delivered the best removal of olefins. Factors influencing this reaction were enlightened. Adaption of the reaction conditions and time-controlled automation increased the recovery of polycyclic MOAH. Good precision (RSD r <1.5%) and recovery (95-102%) for MOAH were also observed for sunflower and olive oils spiked with a lubricating mineral oil (at 24.5mg/kg of MOAH). The trueness of the method was verified by analyzing collaborative trial samples. Copyright © 2017 Elsevier B.V. All rights reserved.

Reduced sensitizing capacity of epoxy resin systems: a structure-activity relationship study.

PubMed

Niklasson, Ida B; Broo, Kerstin; Jonsson, Charlotte; Luthman, Kristina; Karlberg, Ann-Therese

2009-11-01

Epoxy resins can be prepared from numerous chemical compositions. Until recently, alternatives to epoxy resins based on diglycidyl ethers of bisphenol A (DGEBA) or bisphenol F (DGEBF) monomers have not received commercial interest, but are presently doing so, as epoxy resins with various properties are desired. Epoxy resin systems are known to cause allergic contact dermatitis because of contents of uncured monomers, reactive diluents, and hardeners. Reactive diluents, for example, glycidyl ethers, which also contain epoxide moieties, are added to reduce viscosity and improve polymerization. We have investigated the contact allergenic properties of a series of six analogues to phenyl glycidyl ether (PGE), all with similar basic structures but with varying carbon chain lengths and degrees of saturation. The chemical reactivity of the compounds in the test series toward the hexapeptide H-Pro-His-Cys-Lys-Arg-Met-OH was investigated. All epoxides were shown to bind covalently to both cysteine and proline residues. The percent depletion of nonreacted peptide was also studied resulting in 88% depletion when using PGE and 46% when using butyl glycidyl ether (5) at the same time point, thus revealing a large difference between the fastest and the slowest reacting epoxide. The skin sensitization potencies of the epoxides using the murine local lymph node assay (LLNA) were evaluated in relation to the observed physicochemical and reactivity properties. To enable determination of statistical significance between structurally closely related compounds, a nonpooled LLNA was performed. It was found that the compounds investigated ranged from strong to weak sensitizers, congruent with the reactivity data, indicating that even small changes in chemical structure result in significant differences in sensitizing capacity.

Impact of a heteroatom in a structure-activity relationship study on analogues of phenyl glycidyl ether (PGE) from epoxy resin systems.

PubMed

Niklasson, Ida B; Delaine, Tamara; Luthman, Kristina; Karlberg, Ann-Therese

2011-04-18

Epoxy resins are among the most common causes of occupational contact dermatitis. They are normally used in so-called epoxy resin systems (ERS). These commercial products are combinations of epoxy resins, curing agents, modifiers, and reactive diluents. The most frequently used resins are diglycidyl ethers based on bisphenol A (DGEBA) and bisphenol F (DGEBF). In this study, we have investigated the contact allergenic properties of a series of analogues to the reactive diluent phenyl glycidyl ether (PGE), all with similar basic structures but with varying heteroatoms or with no heteroatom present. The chemical reactivity of the compounds in the test series toward the hexapeptide H-Pro-His-Cys-Lys-Arg-Met-OH was investigated. All epoxides were shown to bind covalently to both cysteine and proline residues. The percent depletion of nonreacted peptide was also studied resulting in ca. 60% depletion when using either PGE, phenyl 2,3-epoxypropyl sulfide (2), or N-(2,3-epoxypropyl)aniline (3), and only 15% when using 1,2-epoxy-4-phenylbutane (4) at the same time point. The skin sensitization potencies of the epoxides using the murine local lymph node assay (LLNA) were evaluated in relation to the observed physicochemical and reactivity properties. To enable determination of statistical significance between structurally closely related compounds, a nonpooled LLNA was performed. It was found that all investigated compounds containing a heteroatom in the α-position to the epoxide were strong sensitizers, congruent with the reactivity data, indicating that the impact of a heteroatom is crucial for the sensitizing capacity for this type of epoxides.

Tandem Reactions for Streamlining Synthesis

PubMed Central

HUSSAIN, MAHMUD M.; WALSH, PATRICK J.

2009-01-01

CONSPECTUS In 1980 Sharpless and Katsuki introduced the asymmetric epoxidation of prochiral allylic alcohols (the Sharpless-Katsuki Asymmetric Epoxidation), which enabled the rapid synthesis of highly enantioenriched epoxy alcohols. This reaction was a milestone in the development of asymmetric catalysis because it was the first highly enantioselective oxidation reaction. Furthermore, it provided access to enantioenriched allylic alcohols that are now standard starting materials in natural product synthesis. In 1981 Sharpless and coworkers made another seminal contribution by describing the kinetic resolution (KR) of racemic allylic alcohols. This work demonstrated that small-molecule catalysts could compete with enzymatic catalysts in KRs. For these pioneering works, Sharpless was awarded the 2001 Nobel Prize with Knowles and Noyori. Despite these achievements, the Sharpless KR is not an efficient method to prepare epoxy alcohols with high enantiomeric excess (ee). First, the racemic allylic alcohol must be prepared and purified. KR of the racemic allylic alcohol must be stopped at low conversion, because the ee of the product epoxy alcohol decreases as the KR progresses. Thus, better methods to prepare epoxy alcohols containing stereogenic carbinol carbons are needed. This Account summarizes our efforts to develop one-pot methods for the synthesis of various epoxy alcohols and allylic epoxy alcohols with high enantio-, diastereo-, and chemoselectivity. Our laboratory developed titanium-based catalysts for use in the synthesis of epoxy alcohols with tertiary carbinols. The catalysts are involved in the first step, which is an asymmetric alkyl or allyl addition to enones. The resulting intermediates are then subjected to a titanium-directed diastereoselective epoxidation to provide tertiary epoxy alcohols. Similarly, the synthesis of acyclic epoxy alcohols begins with asymmetric additions to enals and subsequent epoxidation. The methods described here enable the synthesis of skeletally diverse epoxy alcohols. PMID:18710197

Glass transition temperature of polymer nano-composites with polymer and filler interactions

NASA Astrophysics Data System (ADS)

Hagita, Katsumi; Takano, Hiroshi; Doi, Masao; Morita, Hiroshi

2012-02-01

We systematically studied versatile coarse-grained model (bead spring model) to describe filled polymer nano-composites for coarse-grained (Kremer-Grest model) molecular dynamics simulations. This model consists of long polymers, crosslink, and fillers. We used the hollow structure as the filler to describe rigid spherical fillers with small computing costs. Our filler model consists of surface particles of icosahedra fullerene structure C320 and a repulsive force from the center of the filler is applied to the surface particles in order to make a sphere and rigid. The filler's diameter is 12 times of beads of the polymers. As the first test of our model, we study temperature dependence of volumes of periodic boundary conditions under constant pressures through NPT constant Andersen algorithm. It is found that Glass transition temperature (Tg) decrease with increasing filler's volume fraction for the case of repulsive interaction between polymer and fillers and Tg weakly increase for attractive interaction.

Effect of biobased fillers nature on biodeterioration of hybrid polyethylene composites by mold fungi

NASA Astrophysics Data System (ADS)

Mastalygina, E. E.; Popov, A. A.; Pantyukhov, P. V.

2017-06-01

The paper is devoted to investigation of deterioration of natural fillers and polyethylene composites on their basis (polyethylene/filler=70/30) due to the action of mold fungi. The fillers chemical composition, dimensional parameters and biodegradability have been analyzed as factors exert a considerable impact on composite materials biodeterioration. It has been found that the principal factor determining the biodeterioration of polyethylene/filler composites by mold fungi is chemical composition of a filler and, in turn, its biodegradability. The excess of holocellulose content over lignin content and high protein content in a filler are able to induce biofouling of the polymeric composite materials. The presence of soluble and easy hydrolysed fraction in a filler increases its availability in a polymeric matrix. According to the study results, most effective natural fillers as additives stimulating polyethylene composites biodegradability are milled straw of seed flax and hydrolyzed keratin of bird’s feather.

IOMIDAZOLIUM-BASED INDIUM(III) TETRAHIDES: RECYCLABLE CATALYSTS FOR EFFICIENT COUPLING OF CARBON DIOXIDE WITH EXPOXIDES TO FORM CYCLIC CARBONATES

EPA Science Inventory

The transformation of CO2 an abundant greenhouse gas, into cyclic carbonates by coupling reaction with epoxides is receiving well-deserved attention. A series of imidazolium-based indium tetrahalides, prepared efficiently via microwave assisted reaction of InX3 with [1-R-3-metht...

Selective Clay Placement Within a Silicate-Clay Epoxy Blend Nanocomposite

NASA Technical Reports Server (NTRS)

Miller, Sandi G (Inventor)

2013-01-01

A clay-epoxy nanocomposite may be prepared by dispersing a layered clay in an alkoxy epoxy, such as a polypropylene oxide based epoxide before combining the mixture with an aromatic epoxy to improve the nanocomposite's thermal and mechanical properties.

A Computational Study of Acid Catalyzed Aerosol Reactions of Atmospherically Relevant Epoxides

EPA Science Inventory

Epoxides are important intermediates of atmospheric isoprene oxidation. Their subsequent reactions in the particle phase lead to the production of organic compounds detected in ambient aerosols. We apply density functional theory to determine the important kinetic factors that ...

Ring-opening Polymerization of Epoxidized Soybean Oil

USDA-ARS?s Scientific Manuscript database

Ring opening polymerization of epoxidized soybean oil (ESO) initiated by boron trifluoride diethyl etherate, (BF3•OEt2), in methylene chloride was conducted in an effort to develop useful biodegradable polymers. The resulting polymers (PESO) were characterized using Infrared (IR), differential scan...

Biobased composites from thermoplastic polyurethane elastomer and cross-linked acrylated-epoxidized soybean oil

USDA-ARS?s Scientific Manuscript database

Soybean oil is an important sustainable material. Crosslinked acrylated epoxidized soybean oil (AESO) is brittle without flexibility and the incorporation of thermoplastic polyurethane improves its toughness for industrial applications. The hydrophilic functional groups from both oil and polyurethan...

ULTRASOUND-ASSISTED ORGANIC SYNTHESIS: ALCOHOL OXIDATION AND OLEFIN EPOXIDATION

EPA Science Inventory

Ultrasound-assisted Organic Synthesis: Alcohol Oxidation and Olefin Epoxidation

Unnikrishnan R Pillai, Endalkachew Sahle-Demessie , Vasudevan Namboodiri, Quiming Zhao, Juluis Enriquez
U.S. EPA , 26 W. Martin Luther King Dr. , Cincinnati, OH 45268
Phone: 513-569-773...

Manufacture of a ceramic paper for art applications

NASA Astrophysics Data System (ADS)

Dölle, K.; Honig, A.; Piatkowski, J.; Kuempel, C.

2018-01-01

Ceramic paper products are mostly used as high temperature ceramic insulation products. They offer an effective solution for most demanding heat management and insulation applications. The objective for this research project was to create a ceramic paper like product that combines the advantages of paper fibers, ceramic filler, and a clay product into one product, which can be produced on a continuous base with a paper machine. The produced ceramic paper product had a ceramic filler level between 59.68% and 78.8% with a basis weight between 322.9 g/m² and 693.7 g/m², and a final moisture content of 58.6% to 44.7% respectively. The wooden fiber served as a support medium for the ceramic filler material during production on the paper machine and during the conversion process into art pieces. During firing in a kiln, the fiber material combusted and the ceramic filler material mixture acts as common pottery clay, holding the desired shape of the art pieces produced.

Fatigue Crack Growth Behavior of Gas Metal Arc Welded AISI 409 Grade Ferritic Stainless Steel Joints

NASA Astrophysics Data System (ADS)

Lakshminarayanan, A. K.; Shanmugam, K.; Balasubramanian, V.

2009-10-01

The effect of filler metals such as austenitic stainless steel, ferritic stainless steel, and duplex stainless steel on fatigue crack growth behavior of the gas metal arc welded ferritic stainless steel joints was investigated. Rolled plates of 4 mm thickness were used as the base material for preparing single ‘V’ butt welded joints. Center cracked tensile specimens were prepared to evaluate fatigue crack growth behavior. Servo hydraulic controlled fatigue testing machine with a capacity of 100 kN was used to evaluate the fatigue crack growth behavior of the welded joints. From this investigation, it was found that the joints fabricated by duplex stainless steel filler metal showed superior fatigue crack growth resistance compared to the joints fabricated by austenitic and ferritic stainless steel filler metals. Higher yield strength and relatively higher toughness may be the reasons for superior fatigue performance of the joints fabricated by duplex stainless steel filler metal.

Microstructure and Properties of Lap Joint Between Aluminum Alloy and Galvanized Steel by CMT

NASA Astrophysics Data System (ADS)

Niu, Song; Chen, Su; Dong, Honggang; Zhao, Dongsheng; Zhang, Xiaosheng; Guo, Xin; Wang, Guoqiang

2016-05-01

Lap joining of 1-mm-thick Novelist AC 170 PX aluminum alloy to 1.2-mm-thick ST06 Z galvanized steel sheets for automotive applications was conducted by cold metal transfer advanced welding process with ER4043 and ER4047 filler wires. Under the optimized welding parameters with ER4043 filler wire, the tensile shear strength of joint was 189 MPa, reaching 89% of the aluminum alloy base metal. Microstructure and elemental distribution were characterized by optical metalloscope and electron probe microanalysis. The lap joints with ER4043 filler wire had smaller wetting angle and longer bonded line length with better wettability than with ER4047 filler wire during welding with same parameters. The needle-like Al-Fe-Si intermetallic compounds (IMCs) were spalled into the weld and brought negative effect to the tensile strength of joints. With increasing welding current, the needle-like IMCs grew longer and spread further into the weld, which would deteriorate the tensile shear strength.

Optical coherence tomography for image-guided dermal filler injection and biomechanical evaluation

NASA Astrophysics Data System (ADS)

Singh, Manmohan; Wang, Shang; Yee, Richard W.; Han, Zhaolong; Aglyamov, Salavat R.; Larin, Kirill V.

2017-02-01

Dermal fillers are a very popular anti-ag ing treatment with estimated sales in the billions of dollars and millions of procedures performed. As the aging population continues to grow, these figures are only e xpected to increase. Dermal fillers have various compositions depending on their intended applicati on. Reactions to dermal fillers can be severe, such as ischemic events and filler migration to the eyes. Howe ver, these adverse reactions are rare. Nevertheless, the capability to perform imag e-guided filler injections would minimize th e risk of such reacti ons. In addition, the biomechanical properties of various fillers have been evalua ted, but there has been no investigation on the effects of filler on the biomechanical properties of skin. In this work, we utilize optical cohe rence tomography (OCT) for visualizing dermal filler injections with micrometer-scale sp atial resolution. In addition, we utilize noncontact optical coherence elastography (OCE) to quantify the changes in the biomechan ical properties of pig skin after the dermal filler injections. OCT was successfully able to visualize the dermal filler injecti on process, and OCE showed that the viscoelasticity of the pig skin was increased locally at the filler injection sites. OCT may be able to provide real-time image guidance in 3D, and when combined with functional OCT techniques such as optical microangiography, could be used to avoid blood vessels during the injection.

A regression analysis of filler particle content to predict composite wear.

PubMed

Jaarda, M J; Wang, R F; Lang, B R

1997-01-01

It has been hypothesized that composite wear is correlated to filler particle content. There is a paucity of research to substantiate this theory despite numerous projects evaluating the correlation. The purpose of this study was to determine whether a linear relationship existed between composite wear and filler particle content of 12 composites. In vivo wear data had been previously collected for the 12 composites and served as basis for this study. Scanning electron microscopy and backscatter electron imaging were combined with digital imaging analysis to develop "profile maps" of the filler particle composition of the composites. These profile maps included eight parameters: (1) total number of filler particles/28742.6 microns2, (2) percent of area occupied by all of the filler particles, (3) mean filler particle size, (4) percent of area occupied by the matrix, (5) percent of area occupied by filler particles, r (radius) 1.0 < or = micron, (6) percent of area occupied by filler particles, r = 1.0 < or = 4.5 microns, (7) percent of area occupied by filler particles, r = 4.5 < or = 10 microns, and (8) percent of area occupied by filler particles, r > 10 microns. Forward stepwise regression analyses were used with composite wear as the dependent variable and the eight parameters as independent variables. The results revealed a linear relationship between composite wear and the filler particle content. A mathematical formula was developed to predict composite wear.

Hardness of model dental composites - the effect of filler volume fraction and silanation.

PubMed

McCabe, J F; Wassell, R W

1999-05-01

The relationship between structure and mechanical properties for dental composites has often proved difficult to determine due to the use of commercially available materials having a number of differences in composition i.e. different type of resin, different type of filler, etc. This makes a scientific study of any one variable such as filler content difficult if not impossible. In the current study it was the aim to test the hypothesis that hardness measurements of dental composites could be used to monitor the status of the resin-filler interface and to determine the efficacy of any particle silanation process. Ten model composites formulated from a single batch of resin and containing a common type of glass filler were formulated to contain varying amounts of filler. Some materials contained silanated filler, others contained unsilanated filler. Specimens were prepared and stored in water and hardness (Vickers') was determined at 24 h using loads of 50, 100, 200 and 300 g. Composites containing silanated fillers were significantly harder than materials containing unsilanated fillers. For unsilanated products hardness was independent of applied load and in this respect they behaved like homogeneous materials. For composites containing silanated fillers there was a marked increase in measured hardness as applied load was increased. This suggests that the hardness-load profile could be used to monitor the status of the resin-filler interface. Copyright 1999 Kluwer Academic Publishers

Toughening mechanism in elastomer-modified epoxy resins, part 2

NASA Technical Reports Server (NTRS)

Yee, A. F.; Pearson, R. A.

1984-01-01

The role of matrix ductility on the toughenability and toughening mechanism of elastomer-modified DGEBRA epoxies was investigated. Matrix ductility was varied by using epoxide resins of varying epoxide monomer molecular weights. These epoxide resins were cured using 4,4' diaminodiphenyl sulfone (DDS) and, in some cases, modified with 10% HYCAR(r)CTBN 1300X8. Fracture roughness values for the neat epoxies were found to be almost independent on the monomer molecular weight of the epoxide resin used. However, it was found that the fracture toughness of the elastomer-modified epoxies was very dependent upon the epoxide monomer molecular weight. Tensile dilatometry indicated that the toughening mechanism, when present, is similar to the mechanisms found for the piperidine cured epoxies in Part 1. SEM and OM corroborate this finding. Dynamic mechanical studies were conducted to shed light on the toughenability of the epoxies. The time-dependent small strain behavior of these epoxies were separated into their bulk and shear components. The bulk component is related to brittle fracture, whereas the shear component is related to yielding. It can be shown that the rates of shear and bulk strain energy buildup for a given stress are uniquely determined by the values of Poisson's ratio, nu. It was found that nu increases as the monomer molecular weight of the epoxide resin used increases. This increase in nu can be associated with the low temperature beta relaxation. The effect of increasing cross-link density is to shift the beta relaxation to higher temperatures and to decrease the magnitude of the beta relaxation. Thus, increasing cross-link density decreases nu and increases the tendency towards brittle fracture.

Microsomal oxidation of tribromoethylene and reactions of tribromoethylene oxide.

PubMed

Yoshioka, Tadao; Krauser, Joel A; Guengerich, F Peter

2002-11-01

Halogenated olefins are of interest because of their widespread use in industry and their potential toxicity to humans. Epoxides are among the enzymatic oxidation products and have been studied in regard to their toxicity. Most of the attention has been given to chlorinated epoxides, and we have previously studied the reactions of the mono-, di-, tri-, and tetrachloroethylene oxides. To further test some hypotheses concerning the reactivity of these compounds, we prepared tribromoethylene (TBE) oxide and compared it to trichloroethylene (TCE) oxide and other chlorinated epoxides. TBE oxide reacted with H(2)O about 3 times faster than did TCE oxide. Several hydrolysis products of TBE oxide were the same as formed from TCE oxide, i.e., glyoxylic acid, CO, and HCO(2)H. Br(2)CHCO(2)H was formed from TBE oxide; the yield was higher than for Cl(2)CHCO(2)H formed in the hydrolysis of TCE oxide. The yield of tribromoacetaldehyde was < 0.4% in aqueous buffer (pH 7.4). In rat liver microsomal incubations containing TBE and NADPH, Br(2)CHCO(2)H was a major product, and tribromoacetaldehyde was a minor product. These results are consistent with schemes previously developed for halogenated epoxides, with migration of bromine being more favorable than for chlorine. Reaction of TBE oxide with lysine yielded relatively more N-dihaloacetyllysine and less N-formyllysine than in the case of TCE oxide. This same pattern was observed in the products of the reaction of TBE oxide with the lysine residues in bovine serum albumin. We conclude that the proposed scheme of hydrolysis of halogenated epoxides follows the expected halide order and that this can be used to rationalize patterns of hydrolysis and reactivity of other halogenated epoxides.

Species differences in the hydrolysis of 2-cyanoethylene oxide, the epoxide metabolite of acrylonitrile.

PubMed

Kedderis, G L; Batra, R

1993-04-01

The carcinogenic effects of acrylonitrile in rats are believed to be mediated by its DNA-reactive epoxide metabolite, 2-cyanoethylene oxide (CEO). Previous studies have shown that conjugation with glutathione is the major detoxication pathway for both acrylonitrile and CEO. This study investigated the role of epoxide hydrolase in the hydrolysis of CEO by HPLC analysis of the products from [2,3-14C]CEO. CEO is a relatively stable epoxide with a half-life of 99 min at 37 degrees C in sodium phosphate buffer (0.1 M), pH 7.3. Incubation with hepatic microsomes or cytosols from male F-344 rats or B6C3F1 mice did not enhance the rate of hydrolysis of CEO (0.69 nmol/min). Human hepatic microsomes significantly increased the rate of hydrolysis of CEO, whereas human hepatic cytosols did not. Human hepatic microsomal hydrolysis activity was heat-sensitive and potently inhibited by 1,1,1-trichloropropene oxide (IC50 of 23 microM), indicating that epoxide hydrolase was the catalyst. The hydrolysis of CEO catalyzed by hepatic microsomes from six individuals exhibited normal saturation kinetics with KM ranging from 0.6 to 3.2 mM and Vmax from 8.3 to 18.8 nmol hydrolysis products/min/mg protein. Pretreatment of rodents with phenobarbital or acetone induced hepatic microsomal hydrolysis activity toward CEO, whereas treatment with beta-naphthoflavone, dexamethasone or acrylonitrile itself was without effect. These data show that humans possess an additional detoxication pathway for CEO that is not active in rodents (but is inducible). The presence of an active epoxide hydrolase hydrolysis activity toward CEO in humans should be considered in assessments of cancer risk from acrylonitrile exposure.

Experimental etch-and-rinse adhesives doped with bioactive calcium silicate-based micro-fillers to generate therapeutic resin-dentin interfaces.

PubMed

Profeta, A C; Mannocci, F; Foxton, R; Watson, T F; Feitosa, V P; De Carlo, B; Mongiorgi, R; Valdré, G; Sauro, S

2013-07-01

This study aimed at evaluating the therapeutic bioactive effects on the bond strength of three experimental bonding agents containing modified Portland cement-based micro-fillers applied to acid-etched dentin and submitted to aging in simulated body fluid solution (SBS). Confocal laser (CLSM) and scanning electron microscopy (SEM) were also performed. A type-I ordinary Portland cement was tailored using different compounds such as sodium-calcium-aluminum-magnesium silicate hydroxide (HOPC), aluminum-magnesium-carbonate hydroxide hydrates (HCPMM) and titanium oxide (HPCTO) to create three bioactive micro-fillers. A resin blend mainly constituted by Bis-GMA, PMDM and HEMA was used as control (RES-Ctr) or mixed with each micro-filler to create three experimental bonding agents: (i) Res-HOPC, (ii) Res-HCPMM and (iii) Res-HPCTO. The bonding agents were applied onto 37% H3PO4-etched dentin and light-cured for 30s. After build-ups, they were prepared for micro-tensile bond strength (μTBS) and tested after 24h or 6 months of SBS storage. SEM analysis was performed after de-bonding, while CLSM was used to evaluate the ultra-morphology/nanoleakage and the mineral deposition at the resin-dentin interface. High μTBS values were achieved in all groups after 24h. Only Res-HOPC and Res-HCPMM showed stable μTBS after SBS storage (6 months). All the resin-dentin interfaces created using the bonding agents containing the bioactive micro-fillers tested in this study showed an evident reduction of nanoleakage and mineral deposition after SBS storage. Resin bonding systems containing specifically tailored Portland cement micro-fillers may promote a therapeutic mineral deposition within the hybrid layer and increase the durability of the resin-dentin bond. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

21 CFR 888.3045 - Resorbable calcium salt bone void filler device.

Code of Federal Regulations, 2012 CFR

2012-04-01

... 21 Food and Drugs 8 2012-04-01 2012-04-01 false Resorbable calcium salt bone void filler device... salt bone void filler device. (a) Identification. A resorbable calcium salt bone void filler device is... entitled “Class II Special Controls Guidance: Resorbable Calcium Salt Bone Void Filler Device; Guidance for...

21 CFR 888.3045 - Resorbable calcium salt bone void filler device.

Code of Federal Regulations, 2014 CFR

2014-04-01

... 21 Food and Drugs 8 2014-04-01 2014-04-01 false Resorbable calcium salt bone void filler device... salt bone void filler device. (a) Identification. A resorbable calcium salt bone void filler device is... entitled “Class II Special Controls Guidance: Resorbable Calcium Salt Bone Void Filler Device; Guidance for...

21 CFR 888.3045 - Resorbable calcium salt bone void filler device.

Code of Federal Regulations, 2011 CFR

2011-04-01

... 21 Food and Drugs 8 2011-04-01 2011-04-01 false Resorbable calcium salt bone void filler device... salt bone void filler device. (a) Identification. A resorbable calcium salt bone void filler device is... entitled “Class II Special Controls Guidance: Resorbable Calcium Salt Bone Void Filler Device; Guidance for...

21 CFR 888.3045 - Resorbable calcium salt bone void filler device.

Code of Federal Regulations, 2010 CFR

2010-04-01

... 21 Food and Drugs 8 2010-04-01 2010-04-01 false Resorbable calcium salt bone void filler device... salt bone void filler device. (a) Identification. A resorbable calcium salt bone void filler device is... entitled “Class II Special Controls Guidance: Resorbable Calcium Salt Bone Void Filler Device; Guidance for...

21 CFR 888.3045 - Resorbable calcium salt bone void filler device.

Code of Federal Regulations, 2013 CFR

2013-04-01

... 21 Food and Drugs 8 2013-04-01 2013-04-01 false Resorbable calcium salt bone void filler device... salt bone void filler device. (a) Identification. A resorbable calcium salt bone void filler device is... entitled “Class II Special Controls Guidance: Resorbable Calcium Salt Bone Void Filler Device; Guidance for...

Microstructure-based modelling of arbitrary deformation histories of filler-reinforced elastomers

NASA Astrophysics Data System (ADS)

Lorenz, H.; Klüppel, M.

2012-11-01

A physically motivated theory of rubber reinforcement based on filler cluster mechanics is presented considering the mechanical behaviour of quasi-statically loaded elastomeric materials subjected to arbitrary deformation histories. This represents an extension of a previously introduced model describing filler induced stress softening and hysteresis of highly strained elastomers. These effects are referred to the hydrodynamic reinforcement of rubber elasticity due to strain amplification by stiff filler clusters and cyclic breakdown and re-aggregation (healing) of softer, already damaged filler clusters. The theory is first developed for the special case of outer stress-strain cycles with successively increasing maximum strain. In this more simple case, all soft clusters are broken at the turning points of the cycle and the mechanical energy stored in the strained clusters is completely dissipated, i.e. only irreversible stress contributions result. Nevertheless, the description of outer cycles involves already all material parameters of the theory and hence they can be used for a fitting procedure. In the general case of an arbitrary deformation history, the cluster mechanics of the material is complicated due to the fact that not all soft clusters are broken at the turning points of a cycle. For that reason additional reversible stress contributions considering the relaxation of clusters upon retraction have to be taken into account for the description of inner cycles. A special recursive algorithm is developed constituting a frame of the mechanical response of encapsulated inner cycles. Simulation and measurement are found to be in fair agreement for CB and silica filled SBR/BR and EPDM samples, loaded in compression and tension along various deformation histories.

Transverse-Weld Tensile Properties of a New Al-4Cu-2Si Alloy as Filler Metal

NASA Astrophysics Data System (ADS)

Sampath, K.

2009-12-01

AA2195, an Al-Cu-Li alloy in the T8P4 age-hardened condition, is a candidate aluminum armor for future combat vehicles, as this material offers higher static strength and ballistic protection than current aluminum armor alloys. However, certification of AA2195 alloy for armor applications requires initial qualification based on the ballistic performance of welded panels in the as-welded condition. Currently, combat vehicle manufacturers primarily use gas metal arc welding (GMAW) process to meet their fabrication needs. Unfortunately, a matching GMAW consumable electrode is currently not commercially available to allow effective joining of AA2195 alloy. This initial effort focused on an innovative, low-cost, low-risk approach to identify an alloy composition suitable for effective joining of AA2195 alloy, and evaluated transverse-weld tensile properties of groove butt joints produced using the identified alloy. Selected commercial off-the-shelf (COTS) aluminum alloy filler wires were twisted to form candidate twisted filler rods. Representative test weldments were produced using AA2195 alloy, candidate twisted filler rods and gas tungsten arc welding (GTAW) process. Selected GTA weldments produced using Al-4wt.%Cu-2wt.%Si alloy as filler metal consistently provided transverse-weld tensile properties in excess of 275 MPa (40 ksi) UTS and 8% El (over 25 mm gage length), thereby showing potential for acceptable ballistic performance of as-welded panels. Further developmental work is required to evaluate in detail GMAW consumable wire electrodes based on the Al-Cu-Si system containing 4.2-5.0 wt.% Cu and 1.6-2.0 wt.% Si.

Autonomous Slat-Cove-Filler Device for Reduction of Aeroacoustic Noise Associated with Aircraft Systems

NASA Technical Reports Server (NTRS)

Turner, Travis L. (Inventor); Kidd, Reggie T. (Inventor); Lockard, David P (Inventor); Khorrami, Mehdi R. (Inventor); Streett, Craig L. (Inventor); Weber, Douglas Leo (Inventor)

2016-01-01

A slat cove filler is utilized to reduce airframe noise resulting from deployment of a leading edge slat of an aircraft wing. The slat cove filler is preferably made of a super elastic shape memory alloy, and the slat cove filler shifts between stowed and deployed shapes as the slat is deployed. The slat cove filler may be configured such that a separate powered actuator is not required to change the shape of the slat cove filler from its deployed shape to its stowed shape and vice-versa. The outer contour of the slat cove filler preferably follows a profile designed to maintain accelerating flow in the gap between the slat cove filler and wing leading edge to provide for noise reduction.

Rheological properties of isotropic magnetorheological elastomers featuring an epoxidized natural rubber

NASA Astrophysics Data System (ADS)

Azhani Yunus, Nurul; Amri Mazlan, Saiful; Ubaidillah; Choi, Seung-Bok; Imaduddin, Fitrian; Aziz, Siti Aishah Abdul; Khairi, Muntaz Hana Ahmad

2016-10-01

This study presents principal field-dependent rheological properties of magnetorheological elastomers (MREs) in which an epoxidized natural rubber (ENR) is adopted as a matrix (in short, we call it ENR-based MREs). The isotropic ENR-based MRE samples are fabricated by mixing the ENR compound with carbonyl iron particles (CIPs) with different weight percentages. The morphological properties of the samples are firstly analysed using the microstructure assessment. The influences of the magnetic field on the viscoelastic properties of ENR-based MREs are then examined through the dynamic test under various excitation frequencies. The microstructure of MRE samples exhibits a homogeneous distribution of CIPs in the ENR matrix. The dramatic increment of storage modulus, loss modulus and loss tangent of the ENR-based MREs are also observed from the field-dependent rheological test. This directly demonstrates that the stiffness and damping properties of the samples can be adjusted by the magnetic field. It is also seen that the CIP content, exciting frequency and the magnetic field essentially influence the dynamic properties of the ENR-based MREs. The strong correlation between the magnetization and the magneto-induced storage modulus could be used as a useful guidance in synthesizing the ENR-based MREs for certain applications.

Does filler database size influence identification accuracy?

PubMed

Bergold, Amanda N; Heaton, Paul

2018-06-01

Police departments increasingly use large photo databases to select lineup fillers using facial recognition software, but this technological shift's implications have been largely unexplored in eyewitness research. Database use, particularly if coupled with facial matching software, could enable lineup constructors to increase filler-suspect similarity and thus enhance eyewitness accuracy (Fitzgerald, Oriet, Price, & Charman, 2013). However, with a large pool of potential fillers, such technologies might theoretically produce lineup fillers too similar to the suspect (Fitzgerald, Oriet, & Price, 2015; Luus & Wells, 1991; Wells, Rydell, & Seelau, 1993). This research proposes a new factor-filler database size-as a lineup feature affecting eyewitness accuracy. In a facial recognition experiment, we select lineup fillers in a legally realistic manner using facial matching software applied to filler databases of 5,000, 25,000, and 125,000 photos, and find that larger databases are associated with a higher objective similarity rating between suspects and fillers and lower overall identification accuracy. In target present lineups, witnesses viewing lineups created from the larger databases were less likely to make correct identifications and more likely to select known innocent fillers. When the target was absent, database size was associated with a lower rate of correct rejections and a higher rate of filler identifications. Higher algorithmic similarity ratings were also associated with decreases in eyewitness identification accuracy. The results suggest that using facial matching software to select fillers from large photograph databases may reduce identification accuracy, and provides support for filler database size as a meaningful system variable. (PsycINFO Database Record (c) 2018 APA, all rights reserved).

Synthesis of Vitamin K Expoxide: An Undergraduate Biochemistry Experiment.

ERIC Educational Resources Information Center

Thierry-Palmer, M.

1984-01-01

Provides procedures for synthesizing and purifying a vitamin K metabolite (2,3-epoxide) to introduce many of the techniques used in lipid biochemistry. Includes typical results obtained as well as an optional experiment designed to test the purity of the epoxide obtained. (JM)

A new efficient iron catalyst for olefin epoxidation with hydrogen peroxide.

PubMed

Mikhalyova, Elena A; Makhlynets, Olga V; Palluccio, Taryn D; Filatov, Alexander S; Rybak-Akimova, Elena V

2012-01-18

A new aminopyridine ligand derived from bipiperidine (the product of full reduction of bipyridine, bipy) coordinates to iron(II) in a cis-α fashion, yielding a new selective catalyst for olefin epoxidation with H(2)O(2) under limiting substrate conditions.

Enhanced metal loading in SBA-15-type catalysts facilitated by salt addition. Synthesis, characterization and catalytic epoxide alcoholysis activity of molybdenum incorporated porous silica

DOE Office of Scientific and Technical Information (OSTI.GOV)

Budhi, Sridhar; Peeraphatdit, Chorthip; Pylypenko, Svitlana

2014-02-07

We report a novel method to increase the metal loading in SBA-15 silica matrix via direct synthesis. It was demonstrated through the synthesis and characterization of a series of molybdenum containing SBA-15 mesoporous silica catalysts prepared with and without diammonium hydrogen phosphate (DHP) as an additive. Catalysts prepared with DHP show a 2–3 times increase in incorporation of molybdenum in the silica matrix and pore size enlargement. The synthesized catalysts were characterized using nitrogen sorption, X-ray diffraction (XRD), Raman spectroscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS) and inductively coupled plasma–optical emission spectroscopy (ICP–OES). Themore » catalytic activity of catalysts prepared with DHP for alcoholysis of epoxides was superior than the catalyst prepared without DHP. Alcoholysis of epoxides was demonstrated for a range of alcohols and epoxides under ambient conditions in as little as 30 min with high selectivity.« less

Alphatic 3,4-epoxyalcohols. Metabolism by epoxide hydrase and mutagenic activity.

PubMed

Ortiz de Montellano, P R; Boparai, A S

1978-12-18

Rabbit hepatic microsomal epoxide hydrase catalyzes the rapid hydrolysis of 1,2-epoxy-4-heptanol to 1,2,4-heptanetriol. Both diastereomers of the substrate are hydrolyzed, and both product diastereomers are formed. Similarly both cis- and trans-3,4-epoxy-1-hexanol are hydrolyzed, albeit more slowly, to give 1,3,4-hexanetriol. The trans isomer gives exclusively one diastereomer (erythro) of the triol, while the cis isomer gives the other diastereomer (threo). The product expected if a primary cationic intermediate were to be formed and trapped intramolecularly during the hydrolysis of 1,2-epoxy-4-heptanol, 2-propyl-4-tetrahydrofuranol, was not observed. A comparison of the mutagenic activity in the Ames test of 1-heptane, 1-hepten-4-ol, 1,2-epoxyheptane, and 1,2-epoxy-4-heptanol revealed that only the latter is a detectable mutagen. A vicinal hydroxyl therefore does not interfere significantly with enzymatic epoxide hydrolysis, but it does enhance the bioalkylating potential of even an aliphatic epoxide.

Characterization of an epoxide hydrolase from the Florida red tide dinoflagellate, Karenia brevis.

PubMed

Sun, Pengfei; Leeson, Cristian; Zhi, Xiaoduo; Leng, Fenfei; Pierce, Richard H; Henry, Michael S; Rein, Kathleen S

2016-02-01

Epoxide hydrolases (EH, EC 3.3.2.3) have been proposed to be key enzymes in the biosynthesis of polyether (PE) ladder compounds such as the brevetoxins which are produced by the dinoflagellate Karenia brevis. These enzymes have the potential to catalyze kinetically disfavored endo-tet cyclization reactions. Data mining of K. brevis transcriptome libraries revealed two classes of epoxide hydrolases: microsomal and leukotriene A4 (LTA4) hydrolases. A microsomal EH was cloned and expressed for characterization. The enzyme is a monomeric protein with molecular weight 44kDa. Kinetic parameters were evaluated using a variety of epoxide substrates to assess substrate selectivity and enantioselectivity, as well as its potential to catalyze the critical endo-tet cyclization of epoxy alcohols. Monitoring of EH activity in high and low toxin producing cultures of K. brevis over a three week period showed consistently higher activity in the high toxin producing culture implicating the involvement of one or more EH in brevetoxin biosynthesis. Copyright © 2015 Elsevier Ltd. All rights reserved.

Enantioconvergent biohydrolysis of racemic styrene oxide to R-phenyl-1, 2-ethanediol by a newly isolated filamentous fungus Aspergillus tubingensis TF1.

PubMed

Duarah, Aparajita; Goswami, Amrit; Bora, Tarun C; Talukdar, Madhumita; Gogoi, Binod K

2013-08-01

An effort was made to isolate biocatalysts hydrolyzing epoxides from various ecological niches of northeast India, a biodiversity hot spot zone of the world and screened for epoxide hydrolase activity to convert different racemic epoxides to the corresponding 1, 2-vicinal diols. Screening of a total of 450 microorganisms isolated was carried out using NBP colorimetric assay. One of the strains TF1, after internal transcribed spacer sequence analysis, identified as Aspergillus tubingensis, showed promising enantioconvergent epoxide hydrolase activity. The hydrolysis of unsubstituted styrene oxide (1) occurred to give 97 % ee of R-(-)-1-phenylethane-1, 2-diol (6) with more than 99 % conversion within 45 min incubation. It is shown to be a cheap and practical biocatalyst for one step asymmetric synthesis of chiral R-diol. The other representative substrates (2-5), although underwent hydrolysis with more than 99 % conversion beyond 15 h, exhibited poor enantioselectivity.

Epoxidation of cottonseed oil by aqueous hydrogen peroxide catalysed by liquid inorganic acids.

PubMed

Dinda, Srikanta; Patwardhan, Anand V; Goud, Vaibhav V; Pradhan, Narayan C

2008-06-01

The kinetics of epoxidation of cottonseed oil by peroxyacetic acid generated in situ from hydrogen peroxide and glacial acetic acid in the presence of liquid inorganic acid catalysts were studied. It was possible to obtain up to 78% relative conversion to oxirane with very less oxirane cleavage by in situ technique. The rate constants for sulphuric acid catalysed epoxidation of cottonseed oil were in the range 0.39-5.4 x 10(-6)L mol(-1)s(-1) and the activation energy was found to be 11.7 kcal mol(-1). Some thermodynamic parameters such as enthalpy, entropy, and free energy of activation were determined to be of 11.0 kcal mol(-1), -51.4 cal mol(-1)K(-1) and 28.1 kcal mol(-1), respectively. The order of effectiveness of catalysts was found to be sulphuric acid>phosphoric acid>nitric acid>hydrochloric acid. Acetic acid was found to be superior to formic acid for the in situ cottonseed oil epoxidation.

Fillers in dermatology: from past to present.

PubMed

Chacon, Anna H

2015-11-01

Injectable fillers were introduced in dermatology as a method for reconstructing facial deformities and restoring the aging face. Although fillers have become a popular option among cosmetic patients, clinical experience has shown that fillers must be used with caution, as complications can occur. This article provides a brief review of the history of filler agents currently available for soft tissue augmentation. Although no single filler is ideal for all patients, indications, and situations, residents should be aware of the properties and characteristics that make each product unique.

Effect of epoxidation on 30% poly(methyl methacrylate)-grafted natural rubber polymer electrolytes

NASA Astrophysics Data System (ADS)

Nazir, Khuzaimah; Aziz, Ahmad Fairoz; Adam, Nurul Ilham; Yahya, Muhd Zu Azhan; Ali, Ab Malik Marwan

2015-08-01

Epoxidized 30% poly(methyl methacrylate)-grafted natural rubber (EMG 30) as a polymer host in solid polymer electrolytes (SPEs) has been investigated. EMG30 was synthesized via performicepoxidation method onto 30% poly(methyl methacrylate)-grafted natural rubber (MG30) and the formations of epoxy group were discussed. The EMG30 were characterized by proton nuclear magnetic resonance (1HNMR) to investigate their chemical structure and differential scanning calorimeter to determine their crystallinity. A new peak in 1HNMR spectra (2.71 ppm) confirmed the appearance of epoxy group. SPE based on EMG30 doped with 40 wt% LiCF3SO3 show the highest conductivity. The complexation between EMG30 and LiCF3SO3 were confirmed by attenuated total reflection Fourier transform infrared (ATR-FTIR).

The impact of fillers on lineup performance.

PubMed

Wetmore, Stacy A; McAdoo, Ryan M; Gronlund, Scott D; Neuschatz, Jeffrey S

2017-01-01

Filler siphoning theory posits that the presence of fillers (known innocents) in a lineup protects an innocent suspect from being chosen by siphoning choices away from that innocent suspect. This mechanism has been proposed as an explanation for why simultaneous lineups (viewing all lineup members at once) induces better performance than showups (one-person identification procedures). We implemented filler siphoning in a computational model (WITNESS, Clark, Applied Cognitive Psychology 17:629-654, 2003), and explored the impact of the number of fillers (lineup size) and filler quality on simultaneous and sequential lineups (viewing lineups members in sequence), and compared both to showups. In limited situations, we found that filler siphoning can produce a simultaneous lineup performance advantage, but one that is insufficient in magnitude to explain empirical data. However, the magnitude of the empirical simultaneous lineup advantage can be approximated once criterial variability is added to the model. But this modification works by negatively impacting showups rather than promoting more filler siphoning. In sequential lineups, fillers were found to harm performance. Filler siphoning fails to clarify the relationship between simultaneous lineups and sequential lineups or showups. By incorporating constructs like filler siphoning and criterial variability into a computational model, and trying to approximate empirical data, we can sort through explanations of eyewitness decision-making, a prerequisite for policy recommendations.

Caries-preventive effect of fissure sealant containing surface reaction-type pre-reacted glass ionomer filler and bonded by self-etching primer.

PubMed

Shimazu, Kisaki; Ogata, Kiyokazu; Karibe, Hiroyuki

2012-01-01

We aimed to evaluate the caries-preventive effect of a fissure sealant containing surface reaction-type pre-reacted glass ionomer (S-PRG) filler and bonded by self-etching primer versus those of 2 conventional resin-based sealants bonded by acid etching in terms of its impact on enamel demineralization and remineralization, enamel bond strength, and integrity of debonded enamel surfaces. Demineralization, remineralization, and bond strength on untreated enamel and enamel subsurface lesions of bovine incisors were assessed among the sealants by polarizing microscopy and microradiography; debonded enamel surfaces were examined by scanning electron microscopy. The conventional resin-based sealants bonded by acid etching caused surface defects on the enamel subsurface lesions and significantly increased the lesion depth (p = 0.014), indicative of enamel demineralization. However the S-PRG filler-containing sealant bonded by self-etching primer maintained the enamel surface integrity and inhibited enamel demineralization. No difference in bond strength on both untreated enamel and enamel subsurface lesions was noted among the sealants. An S-PRG filler-containing fissure sealant bonded by self-etching primer can prevent enamel demineralization, microleakage, and gaps without the tags created by acid etching regardless of the enamel condition. Such sealants are suitable for protecting the pits and fissures of immature permanent teeth.

Recreational Reuse of Waste Disposal Sites: Chanute Air Force Base, Illinois.

DTIC Science & Technology

1983-11-01

Nickel Endrin Lead Heptachlor Zinc Heptachlor epoxide Mercury Lindane Silver MethoxychIor Barium Toxaphene Parathion Lagoon and Monitoring Well Water...Gleditisa T. I. Imperial Imperial Honey Locust Platanus acerifolia Bloodgood London Planetree Ulmus parvifolia True Chinese Elm (Populus alba) White

Flame Retardant Effect of Nano Fillers on Polydimethylsiloxane Composites.

PubMed

Jagdale, Pravin; Salimpour, Samera; Islam, Md Hujjatul; Cuttica, Fabio; Hernandez, Francisco C Robles; Tagliaferro, Alberto; Frache, Alberto

2018-02-01

Polydimethylsiloxane has exceptional fire retardancy characteristics, which make it a popular polymer in flame retardancy applications. Flame retardancy of polydimethylsiloxane with different nano fillers was studied. Polydimethylsiloxane composite fire property varies because of the shape, size, density, and chemical nature of nano fillers. In house made carbon and bismuth oxide nano fillers were used in polydimethylsiloxane composite. Carbon from biochar (carbonised bamboo) and a carbon by-product (carbon soot) were selected. For comparative study of nano fillers, standard commercial multiwall carbon nano tubes (functionalised, graphitised and pristine) as nano fillers were selected. Nano fillers in polydimethylsiloxane positively affects their fire retardant properties such as total smoke release, peak heat release rate, and time to ignition. Charring and surface ceramization are the main reasons for such improvement. Nano fillers in polydimethylsiloxane may affect the thermal mobility of polymer chains, which can directly affect the time to ignition. The study concludes that the addition of pristine multiwall carbon nano tubes and bismuth oxide nano particles as filler in polydimethylsiloxane composite improves the fire retardant property.

Dual-Component Gelatinous Peptide/Reactive Oligomer Formulations as Conduit Material and Luminal Filler for Peripheral Nerve Regeneration

PubMed Central

Kohn-Polster, Caroline; Bhatnagar, Divya; Woloszyn, Derek J.; Richtmyer, Matthew; Starke, Annett; Springwald, Alexandra H.; Franz, Sandra; Schulz-Siegmund, Michaela; Kaplan, Hilton M.; Kohn, Joachim; Hacker, Michael C.

2017-01-01

Toward the next generation of nerve guidance conduits (NGCs), novel biomaterials and functionalization concepts are required to address clinical demands in peripheral nerve regeneration (PNR). As a biological polymer with bioactive motifs, gelatinous peptides are promising building blocks. In combination with an anhydride-containing oligomer, a dual-component hydrogel system (cGEL) was established. First, hollow cGEL tubes were fabricated by a continuous dosing and templating process. Conduits were characterized concerning their mechanical strength, in vitro and in vivo degradation and biocompatibility. Second, cGEL was reformulated as injectable shear thinning filler for established NGCs, here tyrosine-derived polycarbonate-based braided conduits. Thereby, the formulation contained the small molecule LM11A-31. The biofunctionalized cGEL filler was assessed regarding building block integration, mechanical properties, in vitro cytotoxicity, and growth permissive effects on human adipose tissue-derived stem cells. A positive in vitro evaluation motivated further application of the filler material in a sciatic nerve defect. Compared to the empty conduit and pristine cGEL, the functionalization performed superior, though the autologous nerve graft remains the gold standard. In conclusion, LM11A-31 functionalized cGEL filler with extracellular matrix (ECM)-like characteristics and specific biochemical cues holds great potential to support PNR. PMID:28531139

Novel Organically Modified Core-Shell Clay for Epoxy Composites-"SOBM Filler 1".

PubMed

Iheaturu, Nnamdi Chibuike; Madufor, Innocent Chimezie

2014-01-01

Preparation of a novel organically modified clay from spent oil base drilling mud (SOBM) that could serve as core-shell clay filler for polymers is herein reported. Due to the hydrophilic nature of clay, its compatibility with polymer matrix was made possible through modification of the surface of the core clay sample with 3-aminopropyltriethoxysilane (3-APTES) compound prior to its use. Fourier transform infrared (FT-IR) spectroscopy was used to characterize clay surface modification. Electron dispersive X-ray diffraction (EDX) and scanning electron microscopy (SEM) were used to expose filler chemical composition and morphology, while electrophoresis measurement was used to examine level of filler dispersion. Results show an agglomerated core clay powder after high temperature treatment, while EDX analysis shows that the organically modified clay is composed of chemical inhomogeneities, wherein elemental compositions in weight percent vary from one point to the other in a probe of two points. Micrographs of the 3-APTES coupled SOBM core-shell clay filler clearly show cloudy appearance, while FT-IR indicates 25% and 5% increases in fundamental vibrations band at 1014 cm(-1) and 1435 cm(-1), respectively. Furthermore, 3-APTES coupled core-shell clay was used to prepare epoxy composites and tested for mechanical properties.

Study on mechanical and physical properties of composite materials with recycled PET as fillers for paving block application

NASA Astrophysics Data System (ADS)

Wicaksono, Sigit Tri; Ardhyananta, Hosta; Rasyida, Amaliya

2018-04-01

Base on Sidoarjo's goverment data, there was more than 4000 metric ton perday of waste that has been accumulated during 2016. More than 10 percent from overall waste is plastics. In accordance with the Indonesia government regulation, "Indonesia clean from waste" by 2020 through 3R (Reduce, Reuse and Recycle) program, we have been focusing research on how to reduce the accumulation of the plastics waste in Sidoarjo by processing it become a new product. In this research, we have made the plastic waste of PET bottle as additional fillers or agregates of composite material for construction application as a paving block. The composition of PET plastic used as fillers is vary from 0, 10, 20, 30, 40 and 50% from total volume of agregates. The ratio of cement binder to sands agregate is 1:3. The specimens were characterized its mechanical and physical properties by using flexural testing, compressive testing, density and water absorbance measurement. The results show that the mechanical (flexural and compressive) properties of composite materials is increased significantly by increasing PET fillers up to 20%, however it was decreased when PET content more than 20%. But, both the density and water absobance of specimens are decreased by increasing of PET fillers.

Novel Organically Modified Core-Shell Clay for Epoxy Composites—“SOBM Filler 1”

PubMed Central

Iheaturu, Nnamdi Chibuike; Madufor, Innocent Chimezie

2014-01-01

Preparation of a novel organically modified clay from spent oil base drilling mud (SOBM) that could serve as core-shell clay filler for polymers is herein reported. Due to the hydrophilic nature of clay, its compatibility with polymer matrix was made possible through modification of the surface of the core clay sample with 3-aminopropyltriethoxysilane (3-APTES) compound prior to its use. Fourier transform infrared (FT-IR) spectroscopy was used to characterize clay surface modification. Electron dispersive X-ray diffraction (EDX) and scanning electron microscopy (SEM) were used to expose filler chemical composition and morphology, while electrophoresis measurement was used to examine level of filler dispersion. Results show an agglomerated core clay powder after high temperature treatment, while EDX analysis shows that the organically modified clay is composed of chemical inhomogeneities, wherein elemental compositions in weight percent vary from one point to the other in a probe of two points. Micrographs of the 3-APTES coupled SOBM core-shell clay filler clearly show cloudy appearance, while FT-IR indicates 25% and 5% increases in fundamental vibrations band at 1014 cm−1 and 1435 cm−1, respectively. Furthermore, 3-APTES coupled core-shell clay was used to prepare epoxy composites and tested for mechanical properties. PMID:27355022

Dual-Component Gelatinous Peptide/Reactive Oligomer Formulations as Conduit Material and Luminal Filler for Peripheral Nerve Regeneration.

PubMed

Kohn-Polster, Caroline; Bhatnagar, Divya; Woloszyn, Derek J; Richtmyer, Matthew; Starke, Annett; Springwald, Alexandra H; Franz, Sandra; Schulz-Siegmund, Michaela; Kaplan, Hilton M; Kohn, Joachim; Hacker, Michael C

2017-05-21

Toward the next generation of nerve guidance conduits (NGCs), novel biomaterials and functionalization concepts are required to address clinical demands in peripheral nerve regeneration (PNR). As a biological polymer with bioactive motifs, gelatinous peptides are promising building blocks. In combination with an anhydride-containing oligomer, a dual-component hydrogel system (cGEL) was established. First, hollow cGEL tubes were fabricated by a continuous dosing and templating process. Conduits were characterized concerning their mechanical strength, in vitro and in vivo degradation and biocompatibility. Second, cGEL was reformulated as injectable shear thinning filler for established NGCs, here tyrosine-derived polycarbonate-based braided conduits. Thereby, the formulation contained the small molecule LM11A-31. The biofunctionalized cGEL filler was assessed regarding building block integration, mechanical properties, in vitro cytotoxicity, and growth permissive effects on human adipose tissue-derived stem cells. A positive in vitro evaluation motivated further application of the filler material in a sciatic nerve defect. Compared to the empty conduit and pristine cGEL, the functionalization performed superior, though the autologous nerve graft remains the gold standard. In conclusion, LM11A-31 functionalized cGEL filler with extracellular matrix (ECM)-like characteristics and specific biochemical cues holds great potential to support PNR.

Metabolism of halogenated ethylenes.

PubMed Central

Leibman, K C; Ortiz, E

1977-01-01

The metabolism of the chlorinated ethylenes may be explained by the formation of chloroethylene epoxides as the first intermediate products. The evidence indicates that these epoxides rearrange with migration of chlorine to form chloroacetaldehydes and chloroacetyl chlorides. Thus, monochloroacetic acid, chloral hydrate, and trichloroacetic acid have been found in reaction mixtures of 1,1-dichloroethylene, trichloroethylene, and tetrachloroethylene, respectively, with rat liver microsomal systems. Rearrangements of the chloroethylene, and glycols formed from the epoxides by hydration may also take place, but would appear, at least in the case of 1,1-dichloroethylene, to be quantitatively less important. The literature on the metabolism of chlorinated ethylenes and its relationship to their toxicity is reviewed. PMID:612463

Practical synthesis of Shi's diester fructose derivative for catalytic asymmetric epoxidation of alkenes.

PubMed

Nieto, N; Molas, P; Benet-Buchholz, J; Vidal-Ferran, A

2005-11-25

[reaction: see text] A practical synthesis of Shi's diester 3 for catalytic asymmetric epoxidations has been developed. The catalyst has been prepared in multigram quantities from D-fructose in four steps with a 66% overall yield. Efficiency, cost, and selectivity aspects of the reagents involved for its preparation have been taken care of during its preparation. The workup procedures have been simplified to the bare minimum, rendering a very practical preparation method. The well-known high efficiency of this catalyst 3 in the epoxidation of alpha,beta-unsaturated carbonyl compounds has also proved to be high in unfunctionalized alkenes.

Diastereoselective Synthesis of a Strawberry Flavoring Agent by Epoxidation of Ethyl trans-b-Methylcinnamate

NASA Astrophysics Data System (ADS)

Pageau, Gayle J.; Mabaera, Rodwell; Kosuda, Kathryn M.; Sebelius, Tamara A.; Ghaffari, Ali H.; Kearns, Kenneth A.; McIntyre, Jean P.; Beachy, Tina M.; Thamattoor, Dasan M.

2002-01-01

The diastereoselective synthesis of ethyl (E)-3-methyl-3-phenylglycidate, a strawberry flavoring agent, is carried out by epoxidizing ethyl trans-b-methylcinnamate with m-chloroperbenzoic acid. This epoxidation is appropriate for the introductory organic laboratory and augments the small number of such experiments currently available for undergraduate education. In the course of performing this exercise, students are exposed to many important facets of organic chemistry such as synthesis, reaction mechanism, stereochemistry, chromatography, quantitative analysis, spectroscopy, and computational chemistry. The 1H NMR spectrum of this compound is especially interesting and presents instructive examples of diastereotopic protons and shielding effects of the aromatic ring current.

Oxidative Reactions with Nonaqueous Enzymes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jonathan S. Dordick; Douglas Clark; Brian H Davison

2001-12-30

The objective of this work is to demonstrate a proof-of-concept of enzymatic oxidative processing in nonaqueous media using alkene epoxidation and phenolic polymerization as relevant targets. This project will provide both the fundamental and applied investigations necessary to initiate the implementation of oxidative biocatalysts as commercially relevant alternatives to chemical processing in general, and to phenolic polymerizations and alkene epoxidation specifically. Thus, this work will address the Bioprocessing Solicitation Area to: (1) makes major improvements to phenolic polymerization and alkene epoxidation technologies; (2) is expected to be cost competitive with competing conventional processes; and (3) produces higher yields with lessmore » waste.« less

Residential Segregation, Housing Status, and Prostate Cancer in African American and White Men

DTIC Science & Technology

2008-04-01

and Leu432Val, microsomal epoxide hydrolase (mEH) Tyr113His and His139Arg, CYP3A4 A(−392)G] and conjugation [glutathione S-transferase (GST) M1 null...CYP1B1, or CYP3A4 (16) can then transform the dihydrodiol to a highly reactive diol-epoxide [benzo(a)pyrene-7,8-dihydrodiol-9,10-epoxide, BPDE] that can...Although mEH (18) and CYP1B1 (19) are expressed in the prostate, CYP1A1 may only be induced under androgen dependency (20) and CYP3A4 may require

Effect of blue and violet light on polymerization shrinkage vectors of a CQ/TPO-containing composite.

PubMed

Sampaio, Camila S; Atria, Pablo J; Rueggeberg, Frederick A; Yamaguchi, Satoshi; Giannini, Marcelo; Coelho, Paulo G; Hirata, Ronaldo; Puppin-Rontani, Regina M

2017-07-01

To evaluate the effect of light-curing wavelengths on composite filler particle displacement, and thus to visualize localized polymerization shrinkage in a resin-based composite (RBC) containing camphorquinone (CQ) and Lucirin TPO (TPO). Three light-curing units (LCUs) were used to light-cure a RBC containing CQ and TPO: a violet-only, a blue-only, and a dual-wavelength, conventional (Polywave ® , emitting violet and blue wavelengths simultaneously). Zirconia fillers were added to the RBC to act as filler particle displacement tracers. LCUs were characterized for total emitted power (mW) and spectral irradiant output (mW/cm 2 /nm). 2-mm high, 7-mm diameter silanized glass cylindrical specimens were filled in a single increment with the RBC, and micro-computed tomography (μ-CT) scans were obtained before and after light-curing, according to each LCU (n=6). Filler particle movement identified polymerization shrinkage vectors, traced using software, at five depths (from 0 up to 2mm): top, top-middle, middle, middle-bottom and bottom. Considering different RBC depths within the same LCU, use of violet-only and conventional LCUs showed filler particle movement decreased with increased depth. Blue-only LCU showed homogeneous filler particle movement along the depths. Considering the effect of different LCUs within the same depth, filler particle movement within LCUs was not statistically different until the middle of the samples (P>.05). However, at the middle-bottom and bottom depths (1.5 and 2mm, respectively), blue-only LCU compared to violet-only LCU showed higher magnitude of displacement vector values (P<.05). Use of the conventional LCU showed filler displacement magnitudes that were not significantly different than blue-only and violet-only LCUs at any depth (P>.05). With respect to the direction of particle movement vectors, use of violet-only LCU showed a greater displacement when close to the incident violet LED; blue-only LCU showed equally distributed particle displacement values within entire depth among the samples; and the conventional LCU showed greater filler displacement closer to the blue LED locations. Filler particle displacement in a RBC as a result of light-curing is related to localized application of light wavelength and total emitted power of the light emitted on the top surface of the RBC. When the violet LED is present (violet-only and conventional LCUs), filler particle displacement magnitude decreased with increased depth, while results using the blue-only LED show a more consistent pattern of displacement. Clinically, these results correlate to production of different characteristics of curing within a RBC restoration mass, depending on localized wavelengths applied to the irradiated surface. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Identification of geometrical isomers and comparison of different isomeric samples of astaxanthin.

PubMed

Qiu, Dan; Wu, Yue-Chan; Zhu, Wen-Li; Yin, Hong; Yi, Long-Tao

2012-09-01

A high-performance liquid chromatographic (HPLC) analysis system for isomeric astaxanthin was developed. The separation system consisted of a C(30) column and an elution system of methanol/MTBE/water/dichloromethane (77:13:8:2, v/v/v/v). Using the combination of HPLC diode array detector and HPLC atmospheric pressure chemical ionization mass spectrometry, 11 geometrical isomers and 4 epoxides of astaxanthin were successfully identified. Referred to crystal, only isomerization with different degrees was found for solvent dissolving and iodine catalysis, while melting of astaxanthin caused isomerization, slight oxidation, and more noticeable polymerization confirmed by gel permeation chromatography. Chemical changes in isomeric samples all caused a decrease in UV content. The vibrational spectra (infrared and Raman) showed that epoxide was the only new functional group generated for melting. Changes of several key bands and formations of new bands were found in iodine catalysis and melting samples because of isomerization. Practical Application:  Eleven geometrical isomers and 4 epoxides, which were normally generated for solvent dissolving, iodine catalysis, and melting of astaxanthin, have been identified by C(30) -HPLC-MS technology. Furthermore, different samples were measured by gel permeation chromatography, UV, infrared, and Raman, based on the analysis of messages, the effect of each processing was well understood. © 2012 Institute of Food Technologists®

Development of an HTS assay for EPHX2 phosphatase activity and screening of nontargeted libraries.

PubMed

Morisseau, Christophe; Sahdeo, Sunil; Cortopassi, Gino; Hammock, Bruce D

2013-03-01

The EPXH2 gene encodes soluble epoxide hydrolase (sEH), which has two distinct enzyme activities: epoxide hydrolase (Cterm-EH) and phosphatase (Nterm-phos). The Cterm-EH is involved in the metabolism of arachidonic acid epoxides that play important roles in blood pressure, cell growth, inflammation, and pain. While recent findings suggested complementary biological roles for Nterm-phos, research is limited by the lack of potent bioavailable inhibitors of this phosphatase activity. Also, a potent bioavailable inhibitor of this activity could be important in the development of therapy for cardiovascular diseases. We report herein the development of an HTS enzyme-based assay for Nterm-phos (Z'>0.9) using AttoPhos as the substrate. This assay was used to screen a wide variety of chemical entities, including a library of known drugs that have reached through clinical evaluation (Pharmakon 1600), as well as a library of pesticides and environmental toxins. We discovered that ebselen inhibits sEH phosphatase activity. Ebselen binds to the N-terminal domain of sEH (K(I)=550 nM) and chemically reacts with the enzyme to quickly and irreversibly inhibit Nterm-phos, and subsequently Cterm-EH, and thus represents a new class of sEH inhibitor. Copyright © 2012 Elsevier Inc. All rights reserved.

Study of austenitic stainless steel welded with low alloy steel filler metal. [tensile and impact strength tests

NASA Technical Reports Server (NTRS)

Burns, F. A.; Dyke, R. A., Jr.

1979-01-01

The tensile and impact strength properties of 316L stainless steel plate welded with low alloy steel filler metal were determined. Tests were conducted at room temperature and -100 F on standard test specimens machined from as-welded panels of various chemical compositions. No significant differences were found as the result of variations in percentage chemical composition on the impact and tensile test results. The weldments containing lower chromium and nickel as the result of dilution of parent metal from the use of the low alloy steel filler metal corroded more severely in a marine environment. The use of a protective finish, i.e., a nitrile-based paint containing aluminum powder, prevented the corrosive attack.

Significantly enhanced high-frequency permeability for composites with amorphous-membrane-fillers prepared using an infiltration method

NASA Astrophysics Data System (ADS)

Li, Z. W.; Yang, Z. H.

2016-03-01

Amorphous-membrane-filler composites have been fabricated using an infiltration method. The composites are able to significantly increase the permeability by 200%, as compared to general amorphous flake composites. SEM and magnetic measurement show that the amorphous flakes in membrane are in-plane arrangement. A model, which considers the effect of flake arrangement on demagnetizing factor Nd and permeability, is proposed. The effect of the arrangement of flakes is equivalent to an effective Nd, which is equal to 1/3 and zero for random and complete in-plane arrangements, respectively. Due to in-plane arrangement of amorphous flakes, the decreased Nd leads to significantly enhanced permeability for the amorphous-membrane-filler composites, based on the Maxwell-Garret mixing law.

Synthesis and characterization of estolides containing epoxy and cyclic carbonate groups

USDA-ARS?s Scientific Manuscript database

The unsaturated sites in 2-ethylhexyl estolides were converted into 5-membered cyclic carbonate groups utilizing a two-step process. First, epoxidation of the alkene bonds was accomplished using formic acid and hydrogen peroxide. The epoxidized estolide material was then reacted with supercritical c...

Polymercaptanized soybean oil – properties and tribological characterization

USDA-ARS?s Scientific Manuscript database

Polymercaptanized vegetable oils are produced in industrial scale by the addition of hydrogen sulfide across double bonds or epoxides of vegetable oils, in the presence of UV-light. To date, soybean oil, epoxidized soybean oil, and castor oil has been mercaptanized using such a procedure. Depending ...

Epoxide pathways improve model predictions of isoprene markers and reveal key role of acidity in aerosol formation

EPA Science Inventory

Isoprene significantly contributes to organic aerosol in the southeastern United States where biogenic hydrocarbons mix with anthropogenic emissions. In this work, the Community Multiscale Air Quality model is updated to predict isoprene aerosol from epoxides produced under both ...

Lipid Sulfates and Sulfonates Are Allosteric Competitive Inhibitors of the N-Terminal Phosphatase Activity of the Mammalian Soluble Epoxide Hydrolase†

PubMed Central

Tran, Katherine L.; Aronov, Pavel A.; Tanaka, Hiromasa; Newman, John W.; Hammock, Bruce D.; Morisseau, Christophe

2006-01-01

The EPXH2 gene encodes for the soluble epoxide hydrolase (sEH), a homodimeric enzyme with each monomer containing two domains with distinct activities. The C-terminal domain, containing the epoxide hydrolase activity (Cterm-EH), is involved in the metabolism of arachidonic acid epoxides, endogenous chemical mediators that play important roles in blood pressure regulation, cell growth, and inflammation. We recently demonstrated that the N-terminal domain contains a Mg2+-dependent lipid phosphate phosphatase activity (Nterm-phos). However, the biological role of this activity is unknown. The inability of known phosphatase inhibitors to inhibit the Nterm-phos constitutes a significant barrier to the elucidation of its function. We describe herein sulfate, sulfonate, and phosphonate lipids as novel potent inhibitors of Nterm-phos. These compounds are allosteric competitive inhibitors with KI in the hundred nanomolar range. These inhibitors may provide a valuable tool to investigate the biological role of the Nterm-phos. We found that polyisoprenyl phosphates are substrates of Nterm-phos, suggesting a possible role in sterol synthesis or inflammation. Furthermore, some of these compounds inhibit the C-terminal sEH activity through a noncompetitive inhibition mechanism involving a new binding site on the C-terminal domain. This novel site may play a role in the natural in vivo regulation of epoxide hydrolysis by sEH. PMID:16142916

Significance of the lipid phase in the dynamics and functions of the xanthophyll cycle as revealed by PsbS overexpression in tobacco and in-vitro de-epoxidation in monogalactosyldiacylglycerol micelles.

PubMed

Hieber, A David; Kawabata, Osamu; Yamamoto, Harry Y

2004-01-01

The dynamics of the xanthophyll cycle relative to non-photochemical quenching (NPQ) were examined in tobacco plants overexpressing violaxanthin de-epoxidase (VDE), PsbS and PsbS+VDE for effects on NPQ and violaxanthin (V) de-epoxidation over a range of light intensities. Induction of de-epoxidation and NPQ increased in overexpressed VDE and PsbS plants, respectively. Surprisingly, under low light, overexpressing PsbS enhanced de-epoxidation in addition to NPQ. The effect was hypothesized as due to PsbS binding zeaxanthin (Z) or inducing the binding of Z within the quenching complex, thus shifting the equilibrium toward higher de-epoxidation states. Studies in model systems show that Z can stereospecifically inhibit VDE activity against violaxanthin. This effect, observed under conditions of limiting lipid concentration, was interpreted as product feedback inhibition. These results support the hypothesis that the capacity of the thylakoid lipid phase for xanthophylls is limited and modulates xanthophyll-cycle activity, in conjunction with the release of V and binding of Z by pigment-binding proteins. These modulating factors are incorporated into a lipid-matrix model that has elements of a signal transduction system wherein the light-generated protons are the signal, VDE the signal receptor, Z the secondary messenger, the lipid phase the transduction network, and Z-binding proteins the targets.

46 CFR 56.75-5 - Filler metal.

Code of Federal Regulations, 2010 CFR

2010-10-01

... 46 Shipping 2 2010-10-01 2010-10-01 false Filler metal. 56.75-5 Section 56.75-5 Shipping COAST... Brazing § 56.75-5 Filler metal. (a) The filler metal used in brazing must be a nonferrous metal or alloy having a melting point above 1,000 °F. and below that of the metal being joined. The filler metal must...

46 CFR 56.75-5 - Filler metal.

Code of Federal Regulations, 2011 CFR

2011-10-01

... 46 Shipping 2 2011-10-01 2011-10-01 false Filler metal. 56.75-5 Section 56.75-5 Shipping COAST... Brazing § 56.75-5 Filler metal. (a) The filler metal used in brazing must be a nonferrous metal or alloy having a melting point above 1,000 °F. and below that of the metal being joined. The filler metal must...

High-frequency sonography of temporary and permanent dermal fillers.

PubMed

Grippaudo, Francesca Romana; Mattei, Mauro

2010-08-01

Dermal fillers are used widely; some have a permanent effect, whereas others are temporary. The aim of this study is to describe the ultrasonographic features of permanent and temporary fillers injected into patients for cosmetic purposes. Between December 2006 and April 2009, 36 subjects, aged 25-45, who had received lips or nasolabial fold filler augmentation, were enrolled for a high-frequency sonographic examination by a blinded investigator. The criteria for exclusion were a history of autoimmunity, infection, neoplastic diseases or episodes of local reactions to the injected filler. Twenty patients underwent a sonographic exam after the injection of a temporary filler (collagen or hyaluronic acid) by FRG; the rest were enrolled among patients seeking a consultation for further cosmetic reasons, but had been treated with an identifiable filler before. It was always possible to identify the filler at the site of injection. Seldom was it possible to discover a silent inflammatory reaction, otherwise unsuspected. The sonographic images differed according to the temporary or the permanent nature of the filler. Ultrasonography has proved to be a useful, non-invasive tool for the identification of the presence and type of the filler injected.

The Study of the Interaction between Silica Filler and Silicone Rubber

NASA Astrophysics Data System (ADS)

Liu, Jiesheng; Gong, Xiaoqiang; Zhang, Rongtang

2018-01-01

The interaction between silica filler and silicone rubber was studied by swelling ratio, Kraus curve and crosslinking density test. The results showed that lower values of Vro/Vrf and swelling ratio in modified filler system suggests good filler-matrix interactions. The composites with silane coupling agents show higher crosslink-density compared that of untreated ones. In the light of the above statement, it can be concluded that modification of filler is the crucial factor in creating a good interaction between the filler and silicone rubber.

Joint Workplan on Filler Investigations for DPCs.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hardin, Ernest; Brady, Patrick Vane

2017-12-01

This workplan addresses filler attributes (i.e., possible requirements), assumptions needed for analysis, selection of filler materials, testing needs, and a long-range perspective on R&D activities leading to filler demonstration and a safety basis for implementation.

3-D QSAR ANALYSIS OF INHIBITION OF MURINE SOLUBLE EPOXIDE HYDROLASE (MSEH) BY BENZOYLUREAS, ARYLUREAS, AND THEIR ANALOGUES. (R825433)

EPA Science Inventory

Two hundred and seventy-one compounds including benzoylureas, arylureas and related compounds were assayed using recombinant murine soluble epoxide hydrolase (MsEH) produced from a baculovirus expression system. Among all the insect growth regulators assayed, 18 benzoylphenylu...

40 CFR 63.1431 - Process vent annual epoxides emission factor plan requirements.

Code of Federal Regulations, 2010 CFR

2010-07-01

..., recovery, or recapture device, along with the expected percent efficiency. (iii) Annual emissions after the... section, kg/yr. R = Expected control efficiency of the combustion, recovery, or recapture device, percent....1426(c) to determine the epoxide control efficiency of the combustion, recovery, or recapture device...

40 CFR 63.1431 - Process vent annual epoxides emission factor plan requirements.

Code of Federal Regulations, 2011 CFR

2011-07-01

..., recovery, or recapture device, along with the expected percent efficiency. (iii) Annual emissions after the... section, kg/yr. R = Expected control efficiency of the combustion, recovery, or recapture device, percent....1426(c) to determine the epoxide control efficiency of the combustion, recovery, or recapture device...

40 CFR 721.10145 - Modified reaction products of alkyl alcohol, halogenated alkane, substituted epoxide, and amino...

Code of Federal Regulations, 2011 CFR

2011-07-01

... 40 Protection of Environment 31 2011-07-01 2011-07-01 false Modified reaction products of alkyl... Modified reaction products of alkyl alcohol, halogenated alkane, substituted epoxide, and amino compound... identified generically as modified reaction products of alkyl alcohol, halogenated alkane, substituted...

40 CFR 721.10145 - Modified reaction products of alkyl alcohol, halogenated alkane, substituted epoxide, and amino...

Code of Federal Regulations, 2010 CFR

2010-07-01

... 40 Protection of Environment 30 2010-07-01 2010-07-01 false Modified reaction products of alkyl... Modified reaction products of alkyl alcohol, halogenated alkane, substituted epoxide, and amino compound... identified generically as modified reaction products of alkyl alcohol, halogenated alkane, substituted...

40 CFR 63.1425 - Process vent control requirements.

Code of Federal Regulations, 2010 CFR

2010-07-01

... Standards for Hazardous Air Pollutant Emissions for Polyether Polyols Production § 63.1425 Process vent... operators of all affected sources using epoxides in the production of polyether polyols are subject to the... (c) of this section only if epoxides are used in the production of polyether polyols and nonepoxide...

Synthesis of epoxidized cardanol and its antioxidative properties for vegetable oils and biodiesel

USDA-ARS?s Scientific Manuscript database

A novel antioxidant epoxidized cardanol (ECD), derived from cardanol, was synthesized and characterized by FT-IR, 1H-NMR and 13C-NMR. Oxidative stability of ECD used in vegetable oils and biodiesel was evaluated by pressurized differential scanning calorimetry (PDSC) and the Rancimat method, respect...

Catalytic epoxidation activity of keplerate polyoxomolybdate nanoball toward aqueous suspension of olefins under mild aerobic conditions.

PubMed

Rezaeifard, Abdolreza; Haddad, Reza; Jafarpour, Maasoumeh; Hakimi, Mohammad

2013-07-10

Catalytic efficiency of a sphere-shaped nanosized polyoxomolybdate {Mo132} in the aerobic epoxidation of olefins in water at ambient temperature and pressure in the absence of reducing agent is exploited which resulted good-to-high yields and desired selectivity.

EXPOXIDATION OF OLEFINS AND α,β-UNSATURATED KEYTONES OVER SONOCHEMICALLY PREPARED HYDROXYAPATITES USING HYDROGEN PEROXIDE

EPA Science Inventory

An effective and environmentally friendly protocol for the epoxidation of olefins and α,β-unsaturated ketones in the presence of hydroxyapatite as catalyst using hydrogen peroxide is described. The catalyst is active and reusable for the selective epoxidation of a variety...

ULTRASOUND-ASSISTED EPOXIDATION OF OLEFINS AND A,B-UNSATURATED KETONES OVER HYDROTALCITES USING HYDROGEN PEROXIDE

EPA Science Inventory

An efficient ultrasound-assisted epoxidation of olefins and a,B-unsaturated ketones over hydrotacite catalysts in the presence of hydrogen peroxide and acetonitrile is described. This general and selective protocol is relatively fast and is applicable to a wide variety of substra...

Formation of furan fatty alkyl esters from their bis-epoxide fatty esters

USDA-ARS?s Scientific Manuscript database

Reactions of epoxidized alkyl soyate with four different alcohols: ethanol, isopropyl alcohol, 2-ethylhexanol, and benzyl alcohol were investigated in the presence of Bronsted acid catalyst. Products not reported in prior studies of similar reactions were found. These were furan fatty acid alkyl est...

Formation of furan fatty alkyl esters from their bis-epoxide fatty esters

USDA-ARS?s Scientific Manuscript database

Reactions of epoxidized alkyl soyate with four different alcohols: ethanol, isopropyl alcohol, 2-ethylhexanol, benzyl alcohol, in the presence of Bronsted acid catalyst, were investigated. Products that were not reported in prior studies of similar reactions were found. These were furan fatty acid a...

21 CFR 172.723 - Epoxidized soybean oil.

Code of Federal Regulations, 2011 CFR

2011-04-01

... 21 Food and Drugs 3 2011-04-01 2011-04-01 false Epoxidized soybean oil. 172.723 Section 172.723 Food and Drugs FOOD AND DRUG ADMINISTRATION, DEPARTMENT OF HEALTH AND HUMAN SERVICES (CONTINUED) FOOD FOR HUMAN CONSUMPTION (CONTINUED) FOOD ADDITIVES PERMITTED FOR DIRECT ADDITION TO FOOD FOR HUMAN...

21 CFR 172.723 - Epoxidized soybean oil.

Code of Federal Regulations, 2010 CFR

2010-04-01

... 21 Food and Drugs 3 2010-04-01 2009-04-01 true Epoxidized soybean oil. 172.723 Section 172.723 Food and Drugs FOOD AND DRUG ADMINISTRATION, DEPARTMENT OF HEALTH AND HUMAN SERVICES (CONTINUED) FOOD FOR HUMAN CONSUMPTION (CONTINUED) FOOD ADDITIVES PERMITTED FOR DIRECT ADDITION TO FOOD FOR HUMAN...

Alternate nozzle ablative materials program

NASA Technical Reports Server (NTRS)

Kimmel, N. A.

1984-01-01

Four subscale solid rocket motor tests were conducted successfully to evaluate alternate nozzle liner, insulation, and exit cone structural overwrap components for possible application to the Space Shuttle Solid Rocket Motor (SRM) nozzle asasembly. The 10,000 lb propellant motor tests were simulated, as close as practical, the configuration and operational environment of the full scale SRM. Fifteen PAN based and three pitch based materials had no filler in the phenolic resin, four PAN based materials had carbon microballoons in the resin, and the rest of the materials had carbon powder in the resin. Three nozzle insulation materials were evaluated; an aluminum oxide silicon oxide ceramic fiber mat phenolic material with no resin filler and two E-glass fiber mat phenolic materials with no resin filler. It was concluded by MTI/WD (the fabricator and evaluator of the test nozzles) and NASA-MSFC that it was possible to design an alternate material full scale SRM nozzle assembly, which could provide an estimated 360 lb increased payload capability for Space Shuttle launches over that obtainable with the current qualified SRM design.

Atmospheric pressure cold plasma treatment of cellulose based fillers for wood plastic composites

NASA Astrophysics Data System (ADS)

Lekobou, William; Englund, Karl; Pedrow, Patrick; Scudiero, Louis

2011-10-01

The main challenge of wood plastic composites (WPC) resides in the low interfacial adhesion due to incompatibility between the cellulose based filler that has a polar surface and most common matrixes, polyolefins which are non-polar. Plasma treatment is a promising technique for surface modification and its implementation into the processing of WPC would provide this industry with a versatile and nearly environmentally benign manufacturing tool. Our investigation aims at designing a cold atmospheric pressure plasma reactor for coating fillers with a hydrophobic material prior to compounding with the matrix. Deposition was achieved with our reactor that includes an array of high voltage needles, a grounded metal mesh, Ar as carrier gas and C2H2 as the precursor molecule. Parameters studied have included gas feed rates and applied voltage; FTIR, ESCA, AFM and SEM imaging were used for film diagnostics. We will also report on deposition rate and its dependence on radial and axial position as well as the effects of plasma-polymerized acetylene on the surface free energy of cellulose based substrates.

Adaptation of pharmaceutical excipients to FDM 3D printing for the fabrication of patient-tailored immediate release tablets.

PubMed

Sadia, Muzna; Sośnicka, Agata; Arafat, Basel; Isreb, Abdullah; Ahmed, Waqar; Kelarakis, Antonios; Alhnan, Mohamed A

2016-11-20

This work aims to employ fused deposition modelling 3D printing to fabricate immediate release pharmaceutical tablets with several model drugs. It investigates the addition of non-melting filler to methacrylic matrix to facilitate FDM 3D printing and explore the impact of (i) the nature of filler, (ii) compatibility with the gears of the 3D printer and iii) polymer: filler ratio on the 3D printing process. Amongst the investigated fillers in this work, directly compressible lactose, spray-dried lactose and microcrystalline cellulose showed a level of degradation at 135°C whilst talc and TCP allowed consistent flow of the filament and a successful 3D printing of the tablet. A specially developed universal filament based on pharmaceutically approved methacrylic polymer (Eudragit EPO) and thermally stable filler, TCP (tribasic calcium phosphate) was optimised. Four model drugs with different physicochemical properties were included into ready-to-use mechanically stable tablets with immediate release properties. Following the two thermal processes (hot melt extrusion (HME) and fused deposition modelling (FDM) 3D printing), drug contents were 94.22%, 88.53%, 96.51% and 93.04% for 5-ASA, captopril, theophylline and prednisolone respectively. XRPD indicated that a fraction of 5-ASA, theophylline and prednisolone remained crystalline whilst captopril was in amorphous form. By combining the advantages of thermally stable pharmaceutically approved polymers and fillers, this unique approach provides a low cost production method for on demand manufacturing of individualised dosage forms. Copyright © 2016 Elsevier B.V. All rights reserved.

Successful Management of Infected Facial Filler with Brucella.

PubMed

Alshaer, Zahra; Alsaadi, Yazeed; Mrad, Mohamed Amir

2018-06-11

The widespread desire to maintain youth and beauty with minimally invasive procedures made the use of soft tissue fillers an attractive option to correct numerous aesthetic problems. However, many complications have emerged recently especially with the use of non-FDA-approved permanent materials. In this case report, we are demonstrating the effective management of a patient with Brucella isolated from a facial abscess at the site of prior permanent filler injection done 17 years ago. A 56-year-old woman presented complaining of painful swelling of the right cheek after a failed trial of filler evacuation and intralesional corticosteroid injection. The patient was interviewed carefully, and physical examination was performed, followed by culture and imaging. The patient had a facial abscess that was complicated by parotid infiltration by Brucella. Eventually she was managed successfully by anti-Brucella antibiotics for 6 months with no further complaints. A review of causative organisms in the literature along with recommendations for management is discussed. Permanent fillers have shown many complications that can occur even years after injection. Therefore, physicians should be careful when using permanent fillers and should restrict their use to certain situations. Moreover, rare infections must be kept in mind and careful history, including travel history and animal contact, needs to be considered particularly in the unusual scenarios. This journal requires that authors assign a level of evidence to each article. For a full description of these Evidence-Based Medicine ratings, please refer to the Table of Contents or the online Instructions to Authors www.springer.com/00266 .

The asymmetric synthesis of terminal aziridines by methylene transfer from sulfonium ylides to imines.

PubMed

Kavanagh, Sarah A; Piccinini, Alessandro; Connon, Stephen J

2013-06-07

A new ylide-based protocol for the asymmetric aziridination of imines via methylene transfer has been developed involving the use of a simple chiral sulfonium salt and an organic strong base. A systematic study identified triisopropylphenyl sulfonylimines as optimal substrates for the process. Unexpectedly, hindered C2-symmetric sulfonyl salts incorporating bulky ethers at C-2 and C-5--which had previously been useful in the corresponding epoxidation chemistry--decomposed in these aziridination reactions via competing elimination pathways. Under optimised conditions it was found that a simple salt derived from (2R,5R)-2,5-diisopropyl thiolane could mediate asymmetric methylene transfer to a range of imines with uniformly excellent yields with 19-30% ee. Since this is a similar level of enantiomeric excess to that obtained using these same salts in epoxidation chemistry, it was concluded that if more bulky sulfonium salts could be devised which were resistant to decomposition under the reaction conditions, that highly enantioselective aziridine formation by methylene transfer would be possible.

Synthesis, spectroscopic characterization, thermal studies, catalytic epoxidation and biological activity of chromium and molybdenum hexacarbonyl bound to a novel N 2O 2 Schiff base

NASA Astrophysics Data System (ADS)

Abdel Aziz, Ayman A.

2010-08-01

Complexes of M(CO) 6 (M = Cr and Mo) with novel Schiff base N,N'-bis(salicylidene)4,5-dichloro-1,2-phenylenediamine (H 2L) were prepared in benzene in two different conditions: (i) under reduced pressure resulting the dicarbonyl precursors [Cr(CO) 2(H 2L)] and [Mo(CO) 2(L)] and (ii) in air resulting the oxo complex [Cr(O)(L)] and the dioxo complex [Mo(O) 2(L)]. The complexes were characterized by elemental analysis, IR, 1H NMR, mass spectrometry, and magnetic measurement. Thermal behaviors of the complexes were also studied by using thermogravimetric analysis (TGA). The catalytic activity of the novel complexes in the epoxidation of cyclooctene, cyclohexene, 1-octene and 1-hexene with tert-butyl-hydroperoxide (TBHP) in methylene chloride was investigated. The antimicrobial activities of the ligand and their complexes have been screened against various strains of bacteria and fungi and the results have been compared with some known antibiotics.

Subclass-specific labeling of protein-reactive natural products with customized nucleophilic probes.

PubMed

Rudolf, Georg C; Koch, Maximilian F; Mandl, Franziska A M; Sieber, Stephan A

2015-02-23

Natural products represent a rich source of bioactive compounds that constitute a large fraction of approved drugs. Among those are molecules with electrophilic scaffolds, such as Michael acceptors, β-lactams, and epoxides that irreversibly inhibit essential enzymes based on their catalytic mechanism. In the search for novel bioactive molecules, current methods are challenged by the frequent rediscovery of known chemical entities. Herein small nucleophilic probes that attack electrophilic natural products and enhance their detection by HPLC-UV and HPLC-MS are introduced. A screen of diverse probe designs revealed one compound with a desired selectivity for epoxide- and maleimide-based antibiotics. Correspondingly, the natural products showdomycin and phosphomycin could be selectively targeted in extracts of their natural producing organism, in which the probe-modified molecules exhibited superior retention and MS detection relative to their unmodified counterparts. This method may thus help to discover small, electrophilic molecules that might otherwise easily elude detection in complex samples. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Safety and effectiveness of hyaluronic acid fillers in skin of color.

PubMed

Grimes, Pearl E; Thomas, Jane A; Murphy, Diane K

2009-09-01

To assess the safety and effectiveness of hyaluronic acid (HA) fillers in skin of color. Two prospective studies followed up subjects with Fitzpatrick skin phototypes of IV, V, or VI for 24 weeks after dermal filler injections. In a double-blind, randomized study, subjects were injected with one of three high concentration (24 mg/mL) HA fillers (Juvéderm Ultra, Ultra Plus, and 30) in one nasolabial fold and Zyplast collagen in the other. In an open-label, randomized study, subjects received one of three low concentration (5.5 mg/mL) HA fillers (Hylaform, Hylaform Plus, and Captique) in both nasolabial folds. A total of 160 subjects (a subset of 439 study subjects) were randomized and treated with one of the three high concentration fillers, and 119 subjects were randomized and treated with one of the three low concentration fillers. For subjects treated with the high concentration fillers there were no occurrences of hypersensitivity or hypertrophic scarring, and no increased incidence of hyperpigmentation or hypopigmentation in non-Caucasian vs. Caucasian subjects. For subjects treated with the low concentration fillers there were no occurrences of keloid formation, hypertrophic scarring, hypopigmentation, hypersensitivity, and three instances of mild hyperpigmentation. For all of the fillers the majority of subjects maintained >/=1 point improvement in nasolabial fold severity scores through 24 weeks. All of the HA fillers were well tolerated in individuals with skin of color and demonstrated effectiveness throughout the 24 week period. Furthermore, the fillers provided smooth, natural-looking wrinkle correction in darker skin types.

Bio-Based Nano Composites from Plant Oil and Nano Clay

NASA Astrophysics Data System (ADS)

Lu, Jue; Hong, Chang K.; Wool, Richard P.

2003-03-01

We explored the combination of nanoclay with new chemically functionalized, amphiphilic, plant oil resins to form bio-based nanocomposites with improved physical and mechanical properties. These can be used in many new applications, including the development of self-healing nanocomposites through controlled reversible exfoliation/intercalation, and self-assembled nano-structures. Several chemically modified triglyceride monomers of varying polarity, combined with styrene (ca 30include acrylated epoxidized soybean oil (AESO), maleated acrylated epoxidized soybean oil (MAESO) and soybean oil pentaerythritol glyceride maleates (SOPERMA), containing either hydroxyl group or acid functionality or both. The clay used is a natural montmorillonite modified with methyl tallow bis-2-hydroxyethyl quaternary ammonium chloride, which has hydroxyl groups. Both XRD and TEM showed a completely exfoliated structure at 3 wtwhen the clay content is above 5 wtconsidered a mix of intercalated and partially exfoliated structure. The controlled polarity of the monomer has a major effect on the reversible dispersion of clay in the polymer matrix. The bio-based nanocomposites showed a significant increase in flexural modulus and strength. Supported by EPA and DoE

Rheological properties of styrene-butadiene rubber filled with electron beam modified surface treated dual phase fillers

NASA Astrophysics Data System (ADS)

Shanmugharaj, A. M.; Bhowmick, Anil K.

2004-01-01

The rheological properties of styrene-butadiene rubber (SBR) loaded with dual phase filler were measured using Monsanto Processability Tester (MPT) at three different temperatures (100°C, 110°C and 130°C) and four different shear rates (61.3, 306.3, 613, and 1004.5 s -1). The effect of electron beam modification of dual phase filler in absence and presence of trimethylol propane triacrylate (TMPTA) or triethoxysilylpropyltetrasulphide (Si-69) on melt flow properties of SBR was also studied. The viscosity of all the systems decreases with shear rate indicating their pseudoplastic or shear thinning nature. The higher shear viscosity for the SBR loaded with the electron beam modified filler is explained in terms of variation in structure of the filler upon electron beam irradiation. Die swell of the modified filler loaded SBR is slightly higher than that of the unmodified filler loaded rubber, which is explained by calculating normal stress difference for the systems. Activation energy of the modified filler loaded SBR systems is also slightly higher than that of the control filler loaded SBR system.

Developing the multiple stress-strain creep recovery (MS-SCR) test

NASA Astrophysics Data System (ADS)

Elnasri, Mahmoud; Airey, Gordon; Thom, Nick

2018-04-01

While most published work from Europe has been concerned with evaluating binders' resistance to rutting based on their stiffness (deformation resistance), work originating in the US has mainly been concerned with ranking binders based on their recoverability in a multiple stress form. This paper details the design of a new modified multiple stress-strain creep recovery (MS-SCR) test. The test is designed to evaluate binders' rutting resistance based on two rutting resistance mechanisms: stiffness and recoverability. A preliminary investigation is presented in this paper followed by details of the design of the new modified test. A 40/60 penetration grade bitumen and bitumen-filler mastics prepared with three filler concentrations (35%, 50%, and 65% filler content by mass of mastic) were tested. In addition, two polymer modified bitumens (PMBs) using the same base bitumen type were examined for validation. Two parameters are introduced to characterise the short and long recovery in the new test. In terms of stiffness, the test allows the behaviour of binders at different stress levels and loading cycles to be studied and produces a new parameter that can quantify the degree of modification. Finally, a relationship between nonlinearity and normal force in the test was investigated.

Enhanced Thermo-Optical Switching of Paraffin-Wax Composite Spots under Laser Heating

PubMed Central

Said, Asmaa; Salah, Abeer; Abdel Fattah, Gamal

2017-01-01

Thermo-optical switches are of particular significance in communications networks where increasingly high switching speeds are required. Phase change materials (PCMs), in particular those based on paraffin wax, provide wealth of exciting applications with unusual thermally-induced switching properties, only limited by paraffin’s rather low thermal conductivity. In this paper, the use of different carbon fillers as thermal conductivity enhancers for paraffin has been investigated, and a novel structure based on spot of paraffin wax as a thermo-optic switch is presented. Thermo-optical switching parameters are enhanced with the addition of graphite and graphene, due to the extreme thermal conductivity of the carbon fillers. Differential Scanning Calorimetry (DSC) and Scanning electron microscope (SEM) are performed on paraffin wax composites, and specific heat capacities are calculated based on DSC measurements. Thermo-optical switching based on transmission is measured as a function of the host concentration under conventional electric heating and laser heating of paraffin-carbon fillers composites. Further enhancements in thermo-optical switching parameters are studied under Nd:YAG laser heating. This novel structure can be used in future networks with huge bandwidth requirements and electric noise free remote aerial laser switching applications. PMID:28772884

Enhanced Thermo-Optical Switching of Paraffin-Wax Composite Spots under Laser Heating.

PubMed

Said, Asmaa; Salah, Abeer; Fattah, Gamal Abdel

2017-05-12

Thermo-optical switches are of particular significance in communications networks where increasingly high switching speeds are required. Phase change materials (PCMs), in particular those based on paraffin wax, provide wealth of exciting applications with unusual thermally-induced switching properties, only limited by paraffin's rather low thermal conductivity. In this paper, the use of different carbon fillers as thermal conductivity enhancers for paraffin has been investigated, and a novel structure based on spot of paraffin wax as a thermo-optic switch is presented. Thermo-optical switching parameters are enhanced with the addition of graphite and graphene, due to the extreme thermal conductivity of the carbon fillers. Differential Scanning Calorimetry (DSC) and Scanning electron microscope (SEM) are performed on paraffin wax composites, and specific heat capacities are calculated based on DSC measurements. Thermo-optical switching based on transmission is measured as a function of the host concentration under conventional electric heating and laser heating of paraffin-carbon fillers composites. Further enhancements in thermo-optical switching parameters are studied under Nd:YAG laser heating. This novel structure can be used in future networks with huge bandwidth requirements and electric noise free remote aerial laser switching applications.

Basic principles of creating a new generation of high- temperature brazing filler alloys

NASA Astrophysics Data System (ADS)

Kalin, B. A.; Suchkov, A. N.

2016-04-01

The development of new materials is based on the formation of a structural-phase state providing the desired properties by selecting the base and the complex of alloying elements. The development of amorphous filler alloys for a high-temperature brazing has its own features that are due to the limited life cycle and the production method of brazing filler alloys. The work presents a cycle of analytical and experimental materials science investigations including justification of the composition of a new amorphous filler alloy for brazing the products from zirconium alloys at the temperature of no more than 800 °C and at the unbrazing temperature of permanent joints of more than 1200 °C. The experimental alloys have been used for manufacture of amorphous ribbons by rapid quenching, of which the certification has been made by X-ray investigations and a differential-thermal analysis. These ribbons were used to obtain permanent joints from the spacer grid cells (made from the alloy Zr-1% Nb) of fuel assemblies of the thermal nuclear reactor VVER-440. The brazed samples in the form of a pair of cells have been exposed to corrosion tests in autoclaves in superheated water at a temperature of 350 °C, a pressure of 160 MPa and duration of up to 6,000 h. They have been also exposed to destructive tests using a tensile machine. The experimental results obtained have made it possible to propose and patent a brazing filler alloy of the following composition: Zr-5.5Fe-(2.5-3.5)Be-1Nb-(5-8)Cu-2Sn-0.4Cr-(0.5-1.0)Ge. Its melting point is 780 °C and the recommended brazing temperature is 800°C.

Evaluation of Microstructure and Mechanical Properties in Dissimilar Austenitic/Super Duplex Stainless Steel Joint

NASA Astrophysics Data System (ADS)

Rahmani, Mehdi; Eghlimi, Abbas; Shamanian, Morteza

2014-10-01

To study the effect of chemical composition on microstructural features and mechanical properties of dissimilar joints between super duplex and austenitic stainless steels, welding was attempted by gas tungsten arc welding process with a super duplex (ER2594) and an austenitic (ER309LMo) stainless steel filler metal. While the austenitic weld metal had vermicular delta ferrite within austenitic matrix, super duplex stainless steel was mainly comprised of allotriomorphic grain boundary and Widmanstätten side plate austenite morphologies in the ferrite matrix. Also the heat-affected zone of austenitic base metal comprised of large austenite grains with little amounts of ferrite, whereas a coarse-grained ferritic region was observed in the heat-affected zone of super duplex base metal. Although both welded joints showed acceptable mechanical properties, the hardness and impact strength of the weld metal produced using super duplex filler metal were found to be better than that obtained by austenitic filler metal.

Reduction of liquid metal embrittlement in copper-brazed stainless steel joints

NASA Astrophysics Data System (ADS)

Uhlig, T.; Fedorov, V.; Elßner, M.; Wagner, G.; Weis, S.

2017-03-01

Due to its very good formability and the low raw material cost, pure copper in form of foils is commonly used to braze plate heat exchangers made of stainless steel. The difference in the electrochemical potentials of brazing filler and base material leads to corrosion effects in contact with electrolytes. This may lead to leakages, which decrease the reliability of the heat exchanger during service in potable water. The dissolution of the emerging corrosion products of brazing filler and base material induces the migration of heavy metal ions, such as Cu2+ and Ni2+, into the potable water. The so-called liquid metal embrittlement, which takes place during the brazing process, may intensify the corrosion. The brazing filler infiltrates the stainless steel along the grain boundaries and causes an embrittlement. This paper deals with the determination of the grain boundary erosion dependent on the degree of deformation and heat treatment of the stainless steel AISI 316L.

On dissimilar metal welding of AISI4140 and AISI410 by GTAW

NASA Astrophysics Data System (ADS)

Velu, M.; Dixit, Shantanu; Choure, Shubham

2017-11-01

This paper presents the results of metallurgical and mechanical examinations of Gas Tungsten Arc Welding of dissimilar steels AISI4140 and AISI410. Two different filler materials viz., ERNiCr3 and SS410 were used. The various properties of the weldments made using the fillers were compared to select the most appropriate one to get the sound joint. The ultimate tensile and yield strengths of the weldments of SS410 were greater than those of ERNiCr3. The fracture occurred at the weld in weldments made with ERNiCr3, whereas, in the base metal of AISI410 for weldments made with SS410. Microstructure of fusion zone of ERNiCr3 was fully austenitic. Microhardness values in the weld of SS410 were higher and fluctuating compared to those in the weld of ERNiCr3. From this research work, it shall be concluded that SS410 is the best filler material to weld these base materials.

Epoxidation of 1-Octene with hydrogen peroxide aqueous catalyzed by titania supported sulfonated coal

NASA Astrophysics Data System (ADS)

Nurhadi, Mukhamad

2017-02-01

Titania supported sulfonated coal was created as heterogeneous catalyst for epoxidation of 1-octene with aqueous hydrogen peroxide as oxidant at room temperature. The catalysts were prepared from coal that was sulfonated with H2SO4 (97%) and impregnated 7.2%wt with titanium(IV) isopropoxide (Ti(PrO)4). All catalysts coal (C), CS, Ti(7.2)-CS and Ti(7.2)-CSC were characterized by FTIR. The catalytic performance was tested for epoxidation of 1-octene with H2O2 aqueous as oxidant. It is found that Ti(7.2)-CS possessed the best catalytic performance and it gave the highest 1,2 epoxyoctene 322 µmol.

Ladder Polyether Synthesis via Epoxide-Opening Cascades Directed by a Disappearing Trimethylsilyl Group

PubMed Central

Heffron, Timothy P.; Simpson, Graham L.; Merino, Estibaliz; Jamison, Timothy F.

2010-01-01

Epoxide-opening cascades offer the potential to construct complex polyether natural products expeditiously and in a manner that emulates the biogenesis proposed for these compounds. Herein we provide a full account of our development of a strategy that addresses several important challenges of such cascades. The centerpiece of the method is a trimethylsilyl (SiMe3) group that serves several purposes and leaves no trace of itself by the time the cascade has come to an end. The main function of the SiMe3 group is to dictate the regioselectivity of epoxide opening. This strategy is the only general method of effecting endo-selective cascades under basic conditions. PMID:20302314

Layered transition metal carboxylates: efficient reusable heterogeneous catalyst for epoxidation of olefins.

PubMed

Sen, Rupam; Bhunia, Susmita; Mal, Dasarath; Koner, Subratanath; Miyashita, Yoshitaro; Okamoto, Ken-Ichi

2009-12-01

Layered metal carboxylates [M(malonato)(H(2)O)(2)](n) (M = Ni(II) and Mn(II)) that have a claylike structure have been synthesized hydrothermally and characterized. The interlayer separation in these layered carboxylates is comparable to that of the intercalation distance of the naturally occurring clay materials or layered double hydroxides (LDHs). In this study, we have demonstrated that, instead of intercalating the metal complex into layers of the clay or LDH, layered transition metal carboxylates, [M(malonato)(H(2)O)(2)](n), as such can be used as a recyclable heterogeneous catalyst in olefin epoxidation reaction. Metal carboxylates [M(malonato)(H(2)O)(2)](n) exhibit excellent catalytic performance in olefin epoxidation reaction.

Measurement of the degree of cure in epoxies with ultrasonic velocity

NASA Technical Reports Server (NTRS)

Winfree, W. P.; Parker, F. R.

1986-01-01

The use of ultrasonic longitudinal velocity values to measure the degree of cure (defined for an epoxide system as the concentration of epoxide/amine bonds divided by the initial epoxide concentration) in epoxy resins is investigated. The experimental setup used to measure the changes in longitudinal velocity with time is described, together with the technique used to calculate the degree of cure from the acoustic data, using the principle of additive module. Measurements were done with diglycidyl ether of bisphenol A epoxy resin cured with an amine adduct agent. Good qualitative agreement was shown between the time dependence of the acoustically measured degree of cure and the predicted rate of reaction.

Thermochemical Studies of Epoxides and Related Compounds

PubMed Central

Morgan, Kathleen M.; Ellis, Jamie A.; Lee, Joseph; Fulton, Ashley; Wilson, Shavonda L.; Dupart, Patrick S.; Dastoori, Rosanna

2013-01-01

Gas phase heats of formation for the our butene oxide isomers are reported. They were obtained by measuring the condensed-phase heat of reduction to the corresponding alcohol using reaction calorimetry. Heats of vaporization were determined, and allow gas-phase heats of formation to be obtained. The experimental measurements are compared to calculations obtained using a variety of computational methods. Overall, the G3 and CBS-APNO methods agree quite well with the experimental data. The influence of alkyl substituents on epoxide stability is discussed. Comparisons to alkenes, cyclopropanes, aziridines, thiiranes and phosphiranes are also made. Isodesmic-type reactions were used to determine strain energies of the epoxides and related compounds with various substituents. PMID:23551240

The effect of filler on the protein content and interferences in rubber latices

NASA Astrophysics Data System (ADS)

Ruhida, A. R.; Hassan, Aziz

2017-12-01

It is well known that the application of commercial fillers like calcium carbonate has widely been used in natural rubber latex (NRL) gloves as well as other dipped products such as balloons, condom and catheters. The main reason of adding the fillers into the rubber compound was as cheapening aid and to improve the end-product properties. Due to its functional benefit, many studies have been conducted on the application and beneficial usage of fillers in natural rubber (NR) compounds and natural rubber latex (NRL) dipped goods namely gloves. However most of the studies were basically emphasizing on the effect of fillers on the physical properties and surface morphology of rubber. Not many studies have been conducted to investigate the effect of filler on the protein content in NRL products. Earlier work by other workers has only been concentrating on the effect of nano-sized calcium carbonate fillers in NR latex gloves. Because of the concern on the issue of latex protein allergy; it is thus important to study the effect of filler on protein content and its interferences in the rubber lattices. This paper will seek to elaborate on the effect of filler content on the total protein and extractable protein (EP) content of NR latex films at various filler loadings before and after ageing. The effect of interferences by filler that was mixed into the NR latex on the total nitrogen and EP content were also measured and shown.

A systematic review of dermal fillers for age-related lines and wrinkles.

PubMed

Sturm, Lana P; Cooter, Rodney D; Mutimer, Keith L; Graham, John C; Maddern, Guy J

2011-01-01

Dermal fillers are gaining popularity for rapid aesthetic improvement. Long-term efficacy and safety have not been well documented. The aim of this systematic review was to assess the safety and efficacy of injectable dermal fillers compared with other facial augmentation techniques for the management of age-related lines and wrinkles. Studies including patients receiving injectable semi-permanent or permanent dermal fillers for age-related lines and wrinkles were included in this review. Efficacy outcomes (including changes in skin thickness and patient satisfaction) and safety outcomes (including mortality, lumps and infections) were examined. Three randomized control trials and six case series were included. Permanent and semi-permanent dermal fillers improved subjective ratings of appearance and resulted in higher patient satisfaction than temporary fillers. Long-term efficacy appeared good in the few studies that reported it. Short-term safety appeared favourable. Lumps were reported in all but one study but received little follow-up. Long-term safety data were limited. The treatment of age-related lines and wrinkles with permanent and semi-permanent dermal fillers is more efficacious compared with temporary fillers in those studies that compared them. Case series evidence suggests that these fillers achieve their objective, which is to decrease the visible effects of age-related changes. These fillers appear at least as safe as temporary fillers in the short term in those studies that compared them. Long-term safety could not be determined. © 2010 The Authors. ANZ Journal of Surgery © 2010 Royal Australasian College of Surgeons.

Microscopic and ultrastructural evidences in human skin following calcium hydroxylapatite filler treatment.

PubMed

Zerbinati, Nicola; D'Este, Edoardo; Parodi, Pier Camillo; Calligaro, Alberto

2017-07-01

This study uses light and electron microscopes to gain a better knowledge of the interactions of calcium hydroxylapatite filler with the connective tissue of the skin and the modifications of the human deep dermis, after 2 months of treatment. Some morphological evidences of this observational study of filler treated tissue support-specific mechanism involved in the structural modifications of both filler microspherules and cells of the connective tissue. They demonstrate the absence of any immunological reaction and show that the used filler is modified very slowly over time by the action of cells of the connective tissue closely related to the filler without any activity of phagocytosis. Furthermore, associated with the modifications of the filler, evidences of stimulatory effects on dermal fibroblasts are reported.

Reinforcement of natural rubber hybrid composites based on marble sludge/Silica and marble sludge/rice husk derived silica

PubMed Central

Ahmed, Khalil; Nizami, Shaikh Sirajuddin; Riza, Nudrat Zahid

2013-01-01

A research has been carried out to develop natural rubber (NR) hybrid composites reinforced with marble sludge (MS)/Silica and MS/rice husk derived silica (RHS). The primary aim of this development is to scrutinize the cure characteristics, mechanical and swelling properties of such hybrid composite. The use of both industrial and agricultural waste such as marble sludge and rice husk derived silica has the primary advantage of being eco-friendly, low cost and easily available as compared to other expensive fillers. The results from this study showed that the performance of NR hybrid composites with MS/Silica and MS/RHS as fillers is extremely better in mechanical and swelling properties as compared with the case where MS used as single filler. The study suggests that the use of recently developed silica and marble sludge as industrial and agricultural waste is accomplished to provide a probable cost effective, industrially prospective, and attractive replacement to the in general purpose used fillers like china clay, calcium carbonate, and talc. PMID:25685484

Evaluation of mechanically alloyed Cu-based powders as filler alloy for brazing tungsten to a reduced activation ferritic-martensitic steel

NASA Astrophysics Data System (ADS)

de Prado, J.; Sánchez, M.; Ureña, A.

2017-07-01

80Cu-20Ti powders were evaluated for their use as filler alloy for high temperature brazing of tungsten to a reduced activation ferritic/martensitic steel (Eurofer), and its application for the first wall of the DEMO fusion reactor. The use of alloyed powders has not been widely considered for brazing purposes and could improve the operational brazeability of the studied system due to its narrower melting range, determined by DTA analysis, which enhances the spreading capabilities of the filler. Ti contained in the filler composition acts as an activator element, reacting and forming several interfacial layers at the Eurofer-braze, which enhances the wettability properties and chemical interaction at the brazing interface. Brazing thermal cycle also activated the diffusion phenomena, which mainly affected to the Eurofer alloying elements causing in it a softening band of approximately 400 μm of thickness. However, this softening effect did not degrade the shear strength of the brazed joints (94 ± 23 MPa), because failure during testing was always located at the tungsten-braze interface.

Identifying overarching excipient properties towards an in-depth understanding of process and product performance for continuous twin-screw wet granulation.

PubMed

Willecke, N; Szepes, A; Wunderlich, M; Remon, J P; Vervaet, C; De Beer, T

2017-04-30

The overall objective of this work is to understand how excipient characteristics influence the process and product performance for a continuous twin-screw wet granulation process. The knowledge gained through this study is intended to be used for a Quality by Design (QbD)-based formulation design approach and formulation optimization. A total of 9 preferred fillers and 9 preferred binders were selected for this study. The selected fillers and binders were extensively characterized regarding their physico-chemical and solid state properties using 21 material characterization techniques. Subsequently, principal component analysis (PCA) was performed on the data sets of filler and binder characteristics in order to reduce the variety of single characteristics to a limited number of overarching properties. Four principal components (PC) explained 98.4% of the overall variability in the fillers data set, while three principal components explained 93.4% of the overall variability in the data set of binders. Both PCA models allowed in-depth evaluation of similarities and differences in the excipient properties. Copyright © 2017. Published by Elsevier B.V.

Electrically insulating thermal nano-oils using 2D fillers.

PubMed

Taha-Tijerina, Jaime; Narayanan, Tharangattu N; Gao, Guanhui; Rohde, Matthew; Tsentalovich, Dmitri A; Pasquali, Matteo; Ajayan, Pulickel M

2012-02-28

Different nanoscale fillers have been used to create composite fluids for applications such as thermal management. The ever increasing thermal loads in applications now require advanced operational fluids, for example, high thermal conductivity dielectric oils in transformers. These oils require excellent filler dispersion, high thermal conduction, but also electrical insulation. Such thermal oils that conform to this thermal/electrical requirement, and yet remain in highly suspended stable state, have not yet been synthesized. We report here the synthesis and characterization of stable high thermal conductivity Newtonian nanofluids using exfoliated layers of hexagonal boron nitride in oil without compromising its electrically insulating property. Two-dimensional nanosheets of hexagonal boron nitride are liquid exfoliated in isopropyl alcohol and redispersed in mineral oil, used as standard transformer oil, forming stable nanosuspensions with high shelf life. A high electrical resistivity, even higher than that of the base oil, is maintained for the nano-oil containing small weight fraction of the filler (0.01 wt %), whereas the thermal conductivity was enhanced. The low dissipation factor and high pour point for this nano-oil suggests several applications in thermal management.

Effect of monopolar radiofrequency treatment over soft-tissue fillers in an animal model: part 2.

PubMed

Shumaker, Peter R; England, Laura J; Dover, Jeffrey S; Ross, E Victor; Harford, Robert; Derienzo, Damian; Bogle, Melissa; Uebelhoer, Nathan; Jacoby, Mark; Pope, Karl

2006-03-01

Monopolar radiofrequency (RF) treatment is used by physicians to heat skin and promote tissue tightening and contouring. Cosmetic fillers are used to soften deep facial lines and wrinkles. Patients who have had dermal fillers implanted may also benefit from or are candidates for monopolar RF skin tightening. This study examined the effect of RF treatment on various dermal filler substances. This is the second part of a two-part study. A juvenile farm pig was injected with dermal fillers including cross-linked human collagen (Cosmoplast), polylactic acid (PLA) (Sculptra), liquid injectable silicone (Silikon 1000), calcium hydroxylapatite (CaHA) (Radiesse), and hyaluronic acid (Restylane). Skin injected with dermal fillers was RF-treated using a 1.5-cm2 treatment tip and treatment levels typically used in the clinical setting. Fillers were examined histologically 5 days, 2 weeks, or 1 month after treatment. Histological specimens were scored for inflammatory response, foreign body response, and fibrosis in order to assess the effect of treatment on early filler processes, such as inflammation and encapsulation. Each filler substance produced a characteristic inflammatory response. No immediate thermal effect of RF treatment was observed histologically. RF treatment resulted in statistically significant increases in the inflammatory, foreign body, and fibrotic responses associated with the filler substances. Monopolar RF treatment levels that are typically used in the clinical setting were employed in this animal study. RF treatment resulted in measurable and statistically significant histological changes associated with the various filler materials. Additional clinical and histological studies are required to determine the optimal timing of monopolar RF treatment and filler placement for maximal potential aesthetic outcome. 2006 Wiley-Liss, Inc.

Evaluation of Different Mineral Filler Aggregates for Asphalt Mixtures

NASA Astrophysics Data System (ADS)

Wasilewska, Marta; Małaszkiewicz, Dorota; Ignatiuk, Natalia

2017-10-01

Mineral filler aggregates play an important role in asphalt mixtures because they fill voids in paving mix and improve the cohesion of asphalt binder. Limestone powder containing over 90% of CaCO3 is the most frequently used type of filler. Waste material from the production of coarse aggregate can be successfully used as a mineral filler aggregate for hot asphalt concrete mixtures as the limestone powder replacement. This paper presents the experimental results of selected properties of filler aggregates which were obtained from rocks with different mineral composition and origin. Five types of rocks were used as a source of the mineral filler aggregate: granite, gabbro, trachybasalt, quartz sandstone and rocks from postglacial deposits. Limestone filler was used in this study as the reference material. The following tests were performed: grading (air jet sieving), quality of fines according to methylene blue test, water content by drying in a ventilated oven, particle density using pyknometer method, Delta ring and ball test, Bitumen Number, fineness determined as Blaine specific surface area. Mineral filler aggregates showed significant differences when they were mixed with bitumen and stiffening effect in Delta ring and ball test was evaluated. The highest values were achieved when gabbro and granite fillers were used. Additionally, Scanning Electron Microscopy (SEM) analysis of grain shape and size was carried out. Significant differences in grain size and shape were observed. The highest non-homogeneity in size was determined for quartz sandstone, gabbro and granite filler. Their Blaine specific surface area was lower than 2800 cm2/g, while for limestone and postglacial fillers with regular and round grains it exceeded 3000 cm2/g. All examined mineral filler aggregates met requirements of Polish National Specification WT-1: 2014 and could be used in asphalt mixtures.

Epoxy Resin Composite Based on Functional Hybrid Fillers

PubMed Central

Oleksy, Mariusz; Szwarc-Rzepka, Karolina; Heneczkowski, Maciej; Oliwa, Rafał; Jesionowski, Teofil

2014-01-01

A study was carried out involving the filling of epoxy resin (EP) with bentonites and silica modified with polyhedral oligomeric silsesquioxane (POSS). The method of homogenization and the type of filler affect the functional and canceling properties of the composites was determined. The filler content ranged from 1.5% to 4.5% by mass. The basic mechanical properties of the hybrid composites were found to improve, and, in particular, there was an increase in tensile strength by 44%, and in Charpy impact strength by 93%. The developed hybrid composites had characteristics typical of polymer nanocomposites modified by clays, with a fine plate morphology of brittle fractures observed by SEM, absence of a plate separation peak in Wide Angles X-ray Scattering (WAXS) curves, and an exfoliated structure observed by TEM. PMID:28788177

Thermal Conductivity of Polyimide/Carbon Nanofiller Blends

NASA Technical Reports Server (NTRS)

Ghose, S.; Watson, K. A.; Delozier, D. M.; Working, D. C.; Connell, J. W.; Smith, J. G.; Sun, Y. P.; Lin, Y.

2007-01-01

In efforts to improve the thermal conductivity (TC) of Ultem(TM) 1000, it was compounded with three carbon based nano-fillers. Multiwalled carbon nanotubes (MWCNT), vapor grown carbon nanofibers (CNF) and expanded graphite (EG) were investigated. Ribbons were extruded to form samples in which the nano-fillers were aligned. Samples were also fabricated by compression molding in which the nano-fillers were randomly oriented. The thermal properties were evaluated by DSC and TGA, and the mechanical properties of the aligned samples were determined by tensile testing. The degree of dispersion and alignment of the nanoparticles were investigated with high-resolution scanning electron microscopy. The thermal conductivity of the samples was measured in both the direction of alignment as well as perpendicular to that direction using the Nanoflash technique. The results of this study will be presented.

Thermal Conductivity of Polyimide/Nanofiller Blends

NASA Technical Reports Server (NTRS)

Ghose, S.; Watson, K. A.; Delozier, D. M.; Working, D. c.; Connell, J. W.; Smith, J. G.; Sun, Y. P.; Lin, Y.

2006-01-01

In efforts to improve the thermal conductivity of Ultem(TM) 1000, it was compounded with three carbon based nano-fillers. Multiwalled carbon nanotubes (MWCNT), vapor grown carbon nanofibers (CNF) and expanded graphite (EG) were investigated. Ribbons were extruded to form samples in which the nano-fillers were aligned. Samples were also fabricated by compression molding in which the nano-fillers were randomly oriented. The thermal properties were evaluated by DSC and TGA, and the mechanical properties of the aligned samples were determined by tensile testing. The degree of dispersion and alignment of the nanoparticles were investigated with high-resolution scanning electron microscopy. The thermal conductivity of the samples was measured in both the direction of alignment as well as perpendicular to that direction using the Nanoflash technique. The results of this study will be presented.

Aluminum U-groove weld enhancement based on experimental stress analyses

NASA Technical Reports Server (NTRS)

Verderaime, V.; Vaughan, R.

1995-01-01

Though butt-welds are among the most preferred joining methods in aerostructures because of their sealing and assembly integrity and general elastic performance; their inelastic mechanics are generally the least understood. This study investigated experimental strain distributions across a thick aluminum U-grooved weld and identified two weld process considerations for improving the multipass weld strength. The extreme thermal expansion and contraction gradient of the fusion heat input across the tab thickness between the grooves produce severe peaking, which induces bending moment under uniaxial loading. The filler strain hardening decreased with increasing filler pass sequence. These combined effects reduce the weld strength, and a depeaking index model was developed to select filler pass thicknesses, pass numbers, and sequences to improve the welding process results over the current normal weld schedule.

Bismuth(III) trifluoromethanesulfonate catalyzed ring opening reaction of mono epoxy oleochemicals to form keto and diketo derivatives

USDA-ARS?s Scientific Manuscript database

Using a catalytic system, methyl oleate is transformed into long chain keto and diketo derivatives via an epoxide route. Methyl 9(10)-oxooctadecanoate and methyl 9,10-dioxooctadecanoate were made by a ring opening reaction of epoxidized methyl oleate using bismuth triflate catalyst. Lower reaction t...

Synthesis of an Epoxide Carbonylation Catalyst: Exploration of Contemporary Chemistry for Advanced Undergraduates

ERIC Educational Resources Information Center

Getzler, Yutan D. Y. L.; Schmidt, Joseph A. R.; Coates, Geoffrey W.

2005-01-01

A class of highly active, well-defined compounds for the catalytic carbonylation of epoxides and aziridines to beta-lactones and beta-lactams are introduced. The synthesis of one of the catalysts involves a simple imine condensation to form the ligand followed by air-sensitive metalation and salt metathesis steps.

EXPRESSION AND CHARACTERIZATION OF THE RECOMBINANT JUVENILE HORMONE EPOXIDE HYDROLASE (JHEH) FROM MANDUCA SEXTA. (R825433)

EPA Science Inventory

The cDNA of the microsomal Juvenile Hormone Epoxide Hydrolase (JHEH) from Manduca sexta was expressed in vitro in the baculovirus system. In insect cell culture, the recombinant enzyme (Ms-JHEH) was produced at a high level (100 fold over background EH catalytic activit...

Tungsten-catalyzed asymmetric epoxidation of allylic and homoallylic alcohols with hydrogen peroxide.

PubMed

Wang, Chuan; Yamamoto, Hisashi

2014-01-29

A simple, efficient, and environmentally friendly asymmetric epoxidation of primary, secondary, tertiary allylic, and homoallylic alcohols has been accomplished. This process was promoted by a tungsten-bishydroxamic acid complex at room temperature with the use of aqueous 30% H2O2 as oxidant, yielding the products in 84-98% ee.

Epoxidation with Possibilities: Discovering Stereochemistry in Organic Chemistry via Coupling Constants

ERIC Educational Resources Information Center

Treadwell, Edward M.; Yan, Zhiqing; Xiao, Xiao

2017-01-01

A one-day laboratory epoxidation experiment, requiring no purification, is described, wherein the students are given an "unknown" stereoisomer of 3-hexen-1-ol, and use [superscript 1]H NMR coupling constants to determine the stereochemistry of their product. From this they work backward to determine the stereochemistry of their starting…

Lipase catalyzed epoxidation of fatty acid methyl esters derived from unsaturated vegetable oils in absence of carboxylic acid.

PubMed

Sustaita-Rodríguez, Alejandro; Ramos-Sánchez, Víctor H; Camacho-Dávila, Alejandro A; Zaragoza-Galán, Gerardo; Espinoza-Hicks, José C; Chávez-Flores, David

2018-04-11

Nowadays the industrial chemistry reactions rely on green technologies. Enzymes as lipases are increasing its use in diverse chemical processes. Epoxidized fatty acid methyl esters obtained from transesterification of vegetable oils have recently found applications as polymer plasticizer, agrochemical, cosmetics, pharmaceuticals and food additives. In this research article, grapeseed, avocado and olive oils naturally containing high percents of mono and poly unsaturations were used as starting materials for the production of unsaturated fatty acid methyl esters. The effect of lauric acid as an active oxygen carrier was studied on epoxidation reactions where unsaturated fatty acid methyl esters were converted to epoxy fatty acid methyl esters using immobilized Candida antarctica Lipase type B as catalyst and hydrogen peroxide as oxygen donor at mild temperature and pressure conditions. After this study it was confirmed by 1 H NMR, 13 C NMR and GC-MS that the addition of lauric acid to the enzymatic reaction is unnecessary to transform the alkenes in to epoxides. It was found that quantitative conversions were possible in despite of a carboxylic acid absence.

Chemo-Enzymatic Synthesis of Chiral Epoxides Ethyl and Methyl (S)-3-(Oxiran-2-yl)propanoates from Renewable Levoglucosenone: An Access to Enantiopure (S)-Dairy Lactone.

PubMed

Peru, Aurélien A M; Flourat, Amandine L; Gunawan, Christian; Raverty, Warwick; Jevric, Martyn; Greatrex, Ben W; Allais, Florent

2016-07-29

Chiral epoxides-such as ethyl and methyl (S)-3-(oxiran-2-yl)propanoates ((S)-1a/1b)-are valuable precursors in many chemical syntheses. Until recently, these compounds were synthesized from glutamic acid in four steps (deamination, reduction, tosylation and epoxide formation) in low to moderate overall yield (20%-50%). Moreover, this procedure requires some harmful reagents such as sodium nitrite ((eco)toxic) and borane (carcinogen). Herein, starting from levoglucosenone (LGO), a biobased chiral compound obtained through the flash pyrolysis of acidified cellulose, we propose a safer and more sustainable chemo-enzymatic synthetic pathway involving lipase-mediated Baeyer-Villiger oxidation, palladium-catalyzed hydrogenation, tosylation and treatment with sodium ethoxide/methoxide as key steps. This route afforded ethyl and methyl (S)-3-(oxiran-2-yl)propanoates in 57% overall yield, respectively. To demonstrate the potentiality of this new synthetic pathway from LGO, the synthesis of high value-added (S)-dairy lactone was undertaken from these epoxides and provided the target in 37% overall yield from LGO.

Efficient epoxidation of a terminal alkene containing allylic hydrogen atoms: trans-methylstyrene on Cu{111}.

PubMed

Cropley, Rachael L; Williams, Federico J; Urquhart, Andrew J; Vaughan, Owain P H; Tikhov, Mintcho S; Lambert, Richard M

2005-04-27

The selective oxidation of trans-methylstyrene, a phenyl-substituted propene that contains labile allylic hydrogen atoms, has been studied on Cu{111}. Mass spectrometry and synchrotron fast XPS were used to detect, respectively, desorbing gaseous products and the evolution of surface species as a function of temperature and time. Efficient partial oxidation occurs yielding principally the epoxide, and the behavior of the system is sensitive to the order in which reactants are adsorbed. The latter is understandable in terms of differences in the spatial distribution of oxygen adatoms; isolated adatoms lead to epoxidation, while islands of "oxidic" oxygen do not. NEXAFS data taken over a range of coverages and in the presence and absence of coadsorbed oxygen indicate that the adsorbed alkene lies essentially flat with the allylic hydrogen atoms close to the surface. The photoemission results and comparison with the corresponding behavior of styrene on Cu{111} strongly suggest that allylic hydrogen abstraction is indeed a critical factor that limits epoxidation selectivity. An overall mechanism consistent with the structural and reactive properties is proposed.

A Lewis acid β-diiminato-zinc-complex as all-rounder for co- and terpolymerisation of various epoxides with carbon dioxide.

PubMed

Reiter, M; Vagin, S; Kronast, A; Jandl, C; Rieger, B

2017-03-01

A β-diiminato-zinc-N(SiMe 3 ) 2 complex ( 1 ) was synthesised and fully characterised, including an X-ray diffraction study. The activity of catalyst 1 towards the coupling reaction of CO 2 and various epoxides, including propylene oxide (PO), cyclohexene oxide (CHO), styrene oxide (SO), limonene oxide (LO), octene oxide (OO) and epichlorohydrin (ECH), was investigated. Terpolymerisation of CO 2 , PO and LO, as well as CO 2 , CHO and PO, was successfully realised, resulting in polymers with adjustable glass transition temperatures and transparencies. Reaction conditions such as temperature, pressure and catalyst concentration were varied to find the optimal reaction values, especially regarding LO/CO 2 . In situ IR experiments hinted that at 60 °C and a critical LO concentration, polymerisation and depolymerisation are in an equilibrium (ceiling effect). Pressurising catalyst 1 with carbon dioxide resulted in a dimeric catalyst ( 2 ) with a OSiMe 3 group as a new initiator. Homopolymerisation of different epoxides was carried out in order to explain the reactivity concerning copolymerisation reaction of CO 2 and epoxides.

Effect of molecular weight of hyaluronic acid (HA) on viscoelasticity and particle texturing feel of HA dermal biphasic fillers.

PubMed

Chun, Cheolbyong; Lee, Deuk Yong; Kim, Jin-Tae; Kwon, Mi-Kyung; Kim, Young-Zu; Kim, Seok-Soon

2016-01-01

Hyaluronic acid (HA) dermal biphasic fillers are synthesized for their efficacy in correcting aesthetic defects such as wrinkles, scars and facial contouring defects. The fillers consist of crosslinked HA microspheres suspended in a noncrosslinked HA. To extend the duration of HAs within the dermis and obtain the particle texturing feel, HAs are crosslinked to obtain the suitable mechanical properties. Hyaluronic acid (HA) dermal biphasic fillers are prepared by mixing the crosslinked HA microspheres and the noncrosslinked HAs. The elastic modulus of the fillers increased with raising the volume fraction of the microspheres. The mechanical properties and the particle texturing feel of the fillers made from crosslinked HA (1058 kDa) microspheres suspended in noncrosslinked HA (1368 kDa) are successfully achieved, which are adequate for the fillers. Dermal biphasic HA fillers made from 1058 kDa exhibit suitable elastic moduli (211 to 420 Pa) and particle texturing feel (scale 7 ~ 9).

Efficacy and durability of hyaluronic acid fillers for malar enhancement: A prospective, randomized, split-face clinical controlled trial.

PubMed

Jeong, Ki Heon; Gwak, Min Jae; Moon, Sung Kyung; Lee, Sang Jun; Shin, Min Kyung

2018-06-01

Various hyaluronic acid fillers can be used for facial attenuation and rejuvenation. The efficacy and durability of hyaluronic acid fillers are of major concern to dermatologists and patients. This study aimed to evaluate three-dimensional morphology, tissue distribution, and changes in volume after injection of two different hyaluronic acid fillers. Ten Korean women were enrolled in this study. Each subject was injected with monophasic hyaluronic acid filler in one malar area and biphasic filler in the other. Clinical outcome was measured before and after injection, and after 2, 4, 6, 8, 12, and 24 weeks, using the Global Aesthetic Improvement Scale, photographs and Moire's topography. Facial magnetic resonance imaging (MRI) was performed twice over six months. Both products showed good results after injection and demonstrated good durability over time. MRI was a useful modality for assessing tissue distribution and volume changes. The effects and durability after injection of monophasic hyaluronic acid filler and biphasic hyaluronic acid filler are generally comparable.

Caracterisation d'un enrobe bitumineux haute performance et evaluation de son utilisation en couche de base en remplacement d'une grave bitume

NASA Astrophysics Data System (ADS)

Diakite, Ibrahim Soumaila

The annual production of grave-bitume (GB) in the province of Quebec, of 682 757 tons represents 17% of the total production, just behind ESG-10 with 49,9%. Used as base layer, the grave-bitume can withstand easily the stresses from traffic. The mix design of GB requires two different aggregates stockpile. Also, the amount of binder needed is rather high, which makes those mixes expensive. The annual production of grave-bitume (GB) in the province of Quebec, of 682 757 tons represents 17% of the total production, just behind ESG-10 with 49,9%. Used as base layer, the grave-bitume can withstand easily the stresses from traffic. The mix design of GB requires two different aggregates stockpile. Also, the amount of binder needed is rather high, which makes those mixes expensive. In order to achieve this, different mixes with different filler content, from 9,5% to 15% were designed with a PG 64-28 bitumen. Those mixes were designed following the aggregates packing optimization used for the SMA-Cpack developed at ETS. Only two mixes were characterized, the EBHP-20_11% with 11% filler and the EBHP-20_15% with 15% filler. They were selected to study the influence of the amount of filler on the thermo-mechanical characteristics. The results have shown that the EBHP-20_11% can replace the GB-20 as a base layer mix in a flexible pavement because rutting resistance results from both mixes are similar, same goes for the thermal cracking. For the complex modulus, the value of the norm of the complex modulus at 10°C and 10 Hz are a bit higher for the EBHP compared to the GB-20. However, for fatigue resistance, the EBHP-20_11% has shown a fatigue resistance lower than the GB- 20. The EBHP-20_15% did however have better fatigue resistance than the GB-20, which if probably due to the higher amount of filler in the mix.

Assignment of the relative and absolute stereochemistry of two novel epoxides using NMR and DFT-GIAO calculations

NASA Astrophysics Data System (ADS)

Moraes, F. C.; Alvarenga, E. S.; Demuner, A. J.; Viana, V. M.

2018-07-01

Considering the potential biological application of isobenzofuranones, especially as agrochemical defensives, two novel epoxides, (1aR,2R,2aR,5S,5aS,6S,6aS)-5-(hydroxymethyl)hexahydro-2,6-methanooxireno[2,3-f]isobenzofuran-3(1aH)-one (9), and (1aS,2S,2aR,5S,5aS,6R,6aR)-5-(hydroxymethyl)hexahydro-2,6-methanooxireno[2,3-f]isobenzofuran-3(1aH)-one (10), were synthesized from the readily available D-mannitol in six steps. The multiplicities of the hydrogens located at the bridge of the bicycle are distinct for epoxides 9 and 10 due to W coupling, and this feature was employed to confirm the assignment of these nuclei. Besides analyses of the 2D NMR spectra, the assignments of the nuclei at the epoxide ring were also inferred from information obtained by theoretical calculations. The calculated 1H and 13C NMR chemical shifts for eight candidate structures were compared with the experimental chemical shifts of 9 and 10 by measuring the mean absolute errors (MAE) and by the DP4 statistical analysis. The structures and relative configurations of 9, and 10 were determined via NMR spectroscopy assisted with theoretical calculations. As consequence of the enantioselective syntheses starting from a natural polyol, the absolute configurations of the epoxides 9 and 10 were also defined.

An efficient hybrid, nanostructured, epoxidation catalyst: titanium silsesquioxane-polystyrene copolymer supported on SBA-15.

PubMed

Zhang, Lei; Abbenhuis, Hendrikus C L; Gerritsen, Gijsbert; Bhriain, Nollaig Ní; Magusin, Pieter C M M; Mezari, Brahim; Han, Wei; van Santen, Rutger A; Yang, Qihua; Li, Can

2007-01-01

A novel interfacial hybrid epoxidation catalyst was designed with a new immobilization method for homogeneous catalysts by coating an inorganic support with an organic polymer film containing active sites. The titanium silsesquioxane (TiPOSS) complex, which contains a single-site titanium active center, was immobilized successfully by in-situ copolymerization on a mesoporous SBA-15-supported polystyrene polymer. The resulting hybrid materials exhibit attractive textural properties (highly ordered mesostructure, large specific surface area (>380 m2 g-1) and pore volume (>or==0.46 cm3 g-1)), and high activity in the epoxidation of alkenes. In the epoxidation of cyclooctene with tert-butyl hydrogen peroxide (TBHP), the hybrid catalysts have rate constants comparable with that of their homogeneous counterpart, and can be recycled at least seven times. They can also catalyze the epoxidation of cyclooctene with aqueous H2O2 as the oxidant. In two-phase reaction media, the catalysts show much higher activity than their homogeneous counterpart due to the hydrophobic environment around the active centers. They behave as interfacial catalysts due to their multifunctionality, that is, the hydrophobicity of polystyrene and the polyhedral oligomeric silsesquioxanes (POSS), and the hydrophilicity of the silica and the mesoporous structure. Combination of the immobilization of homogeneous catalysts on two conventional supports, inorganic solid and organic polymer, is demonstrated to achieve novel heterogeneous catalytic ensembles with the merits of attractive textural properties, tunable surface properties, and optimized environments around the active sites.

Clinical Application of Earlobe Augmentation with Hyaluronic Acid Filler in the Chinese Population.

PubMed

Qian, Wei; Zhang, Yan-Kun; Cao, Qian; Hou, Ying; Lv, Wei; Fan, Ju-Feng

2017-02-01

Larger earlobes, which are a symbol of "richness" in traditional Chinese culture, are favored by Chinese patients. The objective of this paper is to investigate the application of earlobe augmentation with hyaluronic acid (HA) filler injection and its clinical effects in the Chinese population. A total of 19 patients (38 ears) who received earlobe augmentation with HA filler injections between March 2013 and March 2015 were included. The clinical effects, duration, and complications of these cases were investigated. All patients who received earlobe HA injections showed immediate postoperative effects with obvious morphological improvement of their earlobes. The volume of HA filler injected into each ear was 0.3-0.5 ml. The duration of the effect was 6-9 months. Two of the 19 cases (3 ears) demonstrated mild bruising at the injection site, but the bruising completely disappeared within 7 days after the injection. No vascular embolism, infection, nodule, or granuloma complications were observed in the studied group. The application of earlobe augmentation with HA filler injection is a safe, effective, simple procedure for earlobe shaping. It has an easy clinical application with good clinical prospects. This journal requires that authors assign a level of evidence to each article. For a full description of these Evidence-Based Medicine ratings, please refer to the Table of Contents or the online Instructions to Authors www.springer.com/00266 .

Characteristics of nitrogen removal and microbial community in biofilm system via combination of pretreated lignocellulosic carriers and various conventional fillers.

PubMed

Zhao, Jing; Feng, Lijuan; Dai, Jincheng; Yang, Guangfeng; Mu, Jun

2017-12-01

Each kind of conventional plastic filler (polyurethane filler, SPR-1 suspension filler, TA-II elastic filler and sphere filler) coupled with alkaline pretreated corncob (A.H.corncob) was applied in each bioreactor system for treating polluted water with nitrate and organics. Results demonstrated that addition of A.H.corncob could achieve simultaneous removal of nitrogen and organics, and coupling of SPR-1 suspension filler with A.H.corncob (R 2 ) had the best performance. In coupling system of R 2 , the total nitrogen (TN) removal rate improved from below 10% to 55.92 ± 18.27% with effluent COD Mn concentration maintaining at a low level of 2.67 ± 0.44 mg L -1 . Microbial analysis of combined filler system demonstrated that conventional plastic filler mainly accumulated non-solid-phase denitrifiers for both nitrate and organics removal including genera Salipiger, Enterobacteriaceae etc. while A.H.corncob carrier was stronghold of solid-phase denitrifiers (Runella, etc.) directly using lignocellulosic materials as carbon source and fermentative bacteria (Coprococcus, etc.) for supplementing available carbon sources for denitrifiers in the system, which were integrated to achieve simultaneous removal of nitrate and organics.

Measurement of composite resin filler particles by using scanning electron microscopy and digital imaging.

PubMed

Jaarda, M J; Lang, B R; Wang, R F; Edwards, C A

1993-04-01

Composite resins are routinely classified on the basis of filler particle size for purposes of research, clinical applications, and communications. The size and characterizations of filler particles have also been considered a significant factor in the rate of wear of composites. Making valid correlations between the filler particles within a composite and wear requires accuracy of filler particle size and characterization. This study was initiated to examine two methods that would (1) qualify the filler particle content of a composite resin and (2) quantify the number, size, and the area occupied by the filler particles in composite resins. Three composite resins, BIS-FIL I, Visio-Fil, and Ful-Fil, were selected as the materials to be examined, on the basis of their published composite classification type as fine particle. The findings demonstrated that scientific methods are available to examine qualitatively and measure quantitatively the composite resin filler particles in terms of their numbers, sizes, and area occupied by use of a scanning electron microscope and digital imaging. Significant differences in the filler particle numbers, sizes, and the area occupied were found for the three composite resins in this study that were classified as fine particle.

Influence of filler loading on the two-body wear of a dental composite.

PubMed

Hu, X; Marquis, P M; Shortall, A C

2003-07-01

The purpose of the study was to explore the fundamental wear behaviour of a dental composite with different filler loadings under two-body wear conditions. The parent resin and filler components were mixed according to different weight ratios to produce experimental composites with filler loadings ranging from 20 to 87.5% by weight. A two-body wear test was conducted on the experimental composites using a wear-testing machine. The machine was designed to simulate the impact of the direct cyclic masticatory loading that occurs in the occlusal contact area in vivo. The results showed that there was little increase in the rate of wear with filler loadings below 60 wt%, but a sharp increase between 80 and 87.5 wt% in filler loading. Wide striations and bulk loss of material were apparent on the wear surfaces at higher filler loadings. Coefficients of friction increased with filler loading and followed the increase in rate of wear loss closely. It was concluded that, under two-body wear conditions, addition of high levels of filler particles into the resin matrix could reduce the wear resistance of dental composites. This finding may help when designing future dental composites for use in particular clinical settings.

Mechanical Properties of Epoxy Resin Mortar with Sand Washing Waste as Filler.

PubMed

Yemam, Dinberu Molla; Kim, Baek-Joong; Moon, Ji-Yeon; Yi, Chongku

2017-02-28

The objective of this study was to investigate the potential use of sand washing waste as filler for epoxy resin mortar. The mechanical properties of four series of mortars containing epoxy binder at 10, 15, 20, and 25 wt. % mixed with sand blended with sand washing waste filler in the range of 0-20 wt. % were examined. The compressive and flexural strength increased with the increase in epoxy and filler content; however, above epoxy 20 wt. %, slight change was seen in strength due to increase in epoxy and filler content. Modulus of elasticity also linearly increased with the increase in filler content, but the use of epoxy content beyond 20 wt. % decreased the modulus of elasticity of the mortar. For epoxy content at 10 wt. %, poor bond strength lower than 0.8 MPa was observed, and adding filler at 20 wt. % adversely affected the bond strength, in contrast to the mortars containing epoxy at 15, 20, 25 wt. %. The results indicate that the sand washing waste can be used as potential filler for epoxy resin mortar to obtain better mechanical properties by adding the optimum level of sand washing waste filler.

Mechanical Properties of Epoxy Resin Mortar with Sand Washing Waste as Filler

PubMed Central

Yemam, Dinberu Molla; Kim, Baek-Joong; Moon, Ji-Yeon; Yi, Chongku

2017-01-01

The objective of this study was to investigate the potential use of sand washing waste as filler for epoxy resin mortar. The mechanical properties of four series of mortars containing epoxy binder at 10, 15, 20, and 25 wt. % mixed with sand blended with sand washing waste filler in the range of 0–20 wt. % were examined. The compressive and flexural strength increased with the increase in epoxy and filler content; however, above epoxy 20 wt. %, slight change was seen in strength due to increase in epoxy and filler content. Modulus of elasticity also linearly increased with the increase in filler content, but the use of epoxy content beyond 20 wt. % decreased the modulus of elasticity of the mortar. For epoxy content at 10 wt. %, poor bond strength lower than 0.8 MPa was observed, and adding filler at 20 wt. % adversely affected the bond strength, in contrast to the mortars containing epoxy at 15, 20, 25 wt. %. The results indicate that the sand washing waste can be used as potential filler for epoxy resin mortar to obtain better mechanical properties by adding the optimum level of sand washing waste filler. PMID:28772603

The Effect of Ultrasonic Additive Manufacturing on Integrated Printed Electronic Conductors

NASA Astrophysics Data System (ADS)

Bournias-Varotsis, Alkaios; Wang, Shanda; Hutt, David; Engstrøm, Daniel S.

2018-07-01

Ultrasonic additive manufacturing (UAM) is a low temperature manufacturing method capable of embedding printed electronics in metal components. The effect of UAM processing on the resistivity of conductive tracks printed with five different conductive pastes based on silver, copper or carbon flakes/particles in either a thermoplastic or thermoset filler binder are investigated. For all but the carbon-based paste, the resistivity changed linearly with the UAM energy input. After UAM processing, a resistivity increase of more than 150 times was recorded for the copper based thermoset paste. The silver based pastes showed a resistivity increase of between 1.1 and 50 times from their initial values. The carbon-based paste showed no change in resistivity after UAM processing. Focussed ion beam microstructure analysis of the printed conductive tracks before and after UAM processing showed that the silver particles and flakes in at least one of the pastes partly dislodged from their thermoset filler creating voids, thereby increasing the resistivity, whereas the silver flakes in a thermoplastic filler did not dislodge due to material flow of the polymer binder. The lowest resistivity (8 × 10-5 Ω cm) after UAM processing was achieved for a thermoplastic paste with silver flakes at low UAM processing energy.

The Effect of Ultrasonic Additive Manufacturing on Integrated Printed Electronic Conductors

NASA Astrophysics Data System (ADS)

Bournias-Varotsis, Alkaios; Wang, Shanda; Hutt, David; Engstrøm, Daniel S.

2018-03-01

Ultrasonic additive manufacturing (UAM) is a low temperature manufacturing method capable of embedding printed electronics in metal components. The effect of UAM processing on the resistivity of conductive tracks printed with five different conductive pastes based on silver, copper or carbon flakes/particles in either a thermoplastic or thermoset filler binder are investigated. For all but the carbon-based paste, the resistivity changed linearly with the UAM energy input. After UAM processing, a resistivity increase of more than 150 times was recorded for the copper based thermoset paste. The silver based pastes showed a resistivity increase of between 1.1 and 50 times from their initial values. The carbon-based paste showed no change in resistivity after UAM processing. Focussed ion beam microstructure analysis of the printed conductive tracks before and after UAM processing showed that the silver particles and flakes in at least one of the pastes partly dislodged from their thermoset filler creating voids, thereby increasing the resistivity, whereas the silver flakes in a thermoplastic filler did not dislodge due to material flow of the polymer binder. The lowest resistivity (8 × 10-5 Ω cm) after UAM processing was achieved for a thermoplastic paste with silver flakes at low UAM processing energy.

The interaction of reaction-bonded silicon carbide and inconel 600 with a nickel-based brazing alloy

NASA Astrophysics Data System (ADS)

McDermid, J. R.; Pugh, M. D.; Drew, R. A. L.

1989-09-01

The objective of the present research was to join reaction-bonded silicon carbide (RBSC) to INCONEL 600 (a nickel-based superalloy) for use in advanced heat engine applications using either direct brazing or composite interlayer joining. Direct brazing experiments employed American Welding Society (AWS) BNi-5, a commercial nickel-based brazing alloy, as a filler material; composite interlayers consisted of intimate mixtures of α-SiC and BNi-5 powders. Both methods resulted in the liquid filler metal forming a Ni-Si liquid with the free Si in the RBSC, which, in turn, reacted vigorously with the SiC component of the RBSC to form low melting point constituents in both starting materials and Cr carbides at the metal-ceramic interface. Using solution thermodynamics, it was shown that a Ni-Si liquid of greater than 60 at. pct Ni will decompose a-SiC at the experimental brazing temperature of 1200 ‡C; these calculations are consistent with the experimentally observed composition profiles and reaction morphology within the ceramic. It was concluded that the joining of RBSC to INCONEL 600 using a nickel-based brazing alloy is not feasible due to the inevitability of the filler metal reacting with the ceramic, degrading the high-temperature properties of the base materials.

Kinetics and mechanism of styrene epoxidation by chlorite: role of chlorine dioxide.

PubMed

Leigh, Jessica K; Rajput, Jonathan; Richardson, David E

2014-07-07

An investigation of the kinetics and mechanism for epoxidation of styrene and para-substituted styrenes by chlorite at 25 °C in the pH range of 5-6 is described. The proposed mechanism in water and water/acetonitrile includes seven oxidation states of chlorine (-I, 0, I, II, III, IV, and V) to account for the observed kinetics and product distributions. The model provides an unusually detailed quantitative mechanism for the complex reactions that occur in mixtures of chlorine species and organic substrates, particularly when the strong oxidant chlorite is employed. Kinetic control of the reaction is achieved by the addition of chlorine dioxide to the reaction mixture, thereby eliminating a substantial induction period observed when chlorite is used alone. The epoxidation agent is identified as chlorine dioxide, which is continually formed by the reaction of chlorite with hypochlorous acid that results from ClO produced by the epoxidation reaction. The overall stoichiometry is the result of two competing chain reactions in which the reactive intermediate ClO reacts with either chlorine dioxide or chlorite ion to produce hypochlorous acid and chlorate or chloride, respectively. At high chlorite ion concentrations, HOCl is rapidly eliminated by reaction with chlorite, minimizing side reactions between HOCl and Cl2 with the starting material. Epoxide selectivity (>90% under optimal conditions) is accurately predicted by the kinetic model. The model rate constant for direct reaction of styrene with ClO2(aq) to produce epoxide is (1.16 ± 0.07) × 10(-2) M(-1) s(-1) for 60:40 water/acetonitrile with 0.20 M acetate buffer. Rate constants for para substituted styrenes (R = -SO3(-), -OMe, -Me, -Cl, -H, and -NO2) with ClO2 were determined. The results support the radical addition/elimination mechanism originally proposed by Kolar and Lindgren to account for the formation of styrene oxide in the reaction of styrene with chlorine dioxide.

Reaction Mechanism for Direct Propylene Epoxidation by Alumina-Supported Silver Aggregates. The Role of the Particle / Support Interface

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cheng, Lei; Yin, Chunrong; Mehmood, Faisal

2013-11-21

Sub-nanometer Ag aggregates on alumina supports have been found to be active toward direct propylene epoxidation to propylene oxide by molecular oxygen at low temperatures, with a negligible amount of carbon dioxide formation (Science 328, p. 224, 2010). In this work, we computationally and experimentally investigate the origin of the high reactivity of the sub-nanometer Ag aggregates. Computationally, we study O 2 dissociation and propylene epoxidation on unsupported Ag 19 and Ag 20 clusters, as well as alumina-supported Ag 19. The O 2 dissociation and propylene epoxidation apparent barriers at the interface between the Ag aggregate and the alumina supportmore » are calculated to be 0.2 and 0.2~0.4 eV, respectively. These barriers are somewhat lower than those on sites away from the interface. The mechanism at the interface is similar to what was previously found for the silver trimer on alumina and can account for the high activity observed for the direct oxidation of propylene on the Ag aggregates. The barriers for oxygen dissociation on these model systems both at the interface and on the surfaces are small compared to crystalline surfaces, indicating that availability of oxygen will not be a rate limiting step for the aggregates, as in the case of the crystalline surfaces. Experimentally, we investigate Ultrananocrystalline Diamond (UNCD)-supported silver aggregates under reactive conditions of propylene partial oxidation. The UNCD-supported Ag clusters are found to be not measurably active toward propylene oxidation, in contrast to the alumina supported Ag clusters. This suggests that the lack of metal-oxide interfacial sites of the Ag-UNCD catalyst, limits the epoxidation catalytic activity. This combined computational and experimental study shows the importance of the metal-oxide interface as well as the non-crystalline nature of the alumina-supported sub-nanometer Ag aggregate catalysts for propylene epoxidation.« less

An integrated computational approach of molecular dynamics simulations, receptor binding studies and pharmacophore mapping analysis in search of potent inhibitors against tuberculosis.

PubMed

Agarwal, Shivangi; Verma, Ekta; Kumar, Vivek; Lall, Namrita; Sau, Samaresh; Iyer, Arun K; Kashaw, Sushil K

2018-05-03

Tuberculosis is an infectious chronic disease caused by obligate pathogen Mycobacterium tuberculosis that affects millions of people worldwide. Although many first and second line drugs are available for its treatment, but their irrational use has adversely lead to the emerging cases of multiple drug resistant and extensively drug-resistant tuberculosis. Therefore, there is an intense need to develop novel potent analogues for its treatment. This has prompted us to develop potent analogues against TB. The Mycobacterium tuberculosis genome provides us with number of validated targets to combat against TB. Study of Mtb genome disclosed six epoxide hydrolases (A to F) which convert harmful epoxide into diols and act as a potential drug target for rational drug design. Our current strategy is to develop such analogues which inhibits epoxide hydrolase enzyme present in Mtb genome. To achieve this, we adopted an integrated computational approach involving QSAR, pharmacophore mapping, molecular docking and molecular dynamics simulation studies. The approach envisaged vital information about the role of molecular descriptors, essential pharmacophoric features and binding energy for compounds to bind into the active site of epoxide hydrolase. Molecular docking analysis revealed that analogues exhibited significant binding to Mtb epoxide hydrolase. Further, three docked complexes 2s, 37s and 15s with high, moderate and low docking scores respectively were selected for molecular dynamics simulation studies. RMSD analysis revealed that all complexes are stable with average RMSD below 2 Å throughout the 10 ns simulations. The B-factor analysis showed that the active site residues of epoxide hydrolase are flexible enough to interact with inhibitor. Moreover, to confirm the binding of these urea derivatives, MM-GBSA binding energy analysis were performed. The calculations showed that 37s has more binding affinity (ΔGtotal = -52.24 kcal/mol) towards epoxide hydrolase compared to 2s (ΔGtotal = -51.70 kcal/mol) and 15s (ΔGtotal = -49.97 kcal/mol). The structural features inferred in our study may provide the future directions to the scientists towards the discovery of new chemical entity exhibiting anti-TB property. Copyright © 2018 Elsevier Inc. All rights reserved.

Production, characterization, and modeling of mineral filled polypropylene filaments

NASA Astrophysics Data System (ADS)

George, Brian Robert

1999-11-01

This research produced mineral filled polypropylene filaments using a variety of fillers, characterized these filaments, and attempted to model their mechanical properties with current composite models. Also, these filaments were compared with bone to determine if they are suitable for modeling the mechanical properties of bone. Fillers used consist of wollastonite, talc, calcium carbonate, titanium dioxide, and hydroxyapatite. Fillers and polypropylene chips were combined and extruded into rods with the use of a mixer. The rods were chipped up and then formed into filaments through melt extrusion utilizing a piston extruder. Filaments with volume fractions of filler of 0.05, 0.10, 0.15, and 0.20 were produced. Additionally, some methods of trying to improve the properties of these filaments were attempted, but did not result in any significant property improvements. The fillers and filaments were visually characterized with a scanning electron microscope. Cross-sections, filament outer surfaces, fracture surfaces, and longitudinal cut open surfaces were viewed in this manner. Those filaments with anisotropic filler had some oriented filler particles, while all filaments suffered from poor adhesion between the polypropylene and the filler as well as agglomerations of filler particles. Twenty specimens of each filament were tensile tested and the average tenacity, strain, and modulus were calculated. Filaments containing talc, talc and wollastonite, titanium dioxide, or hydroxyapatite suffered from a drastic transition from ductile to brittle with the addition of 0.05 volume fraction of filler. This is evidenced by the sharp decrease in strain at this volume fraction of filler when compared to the strain of the unfilled polypropylene filament. Additionally, these same filaments suffered a sharp decrease in tenacity at the same volume fraction. These instant decreases are attributed to the agglomerations of filler in the filament. Generally, the modulus of the filaments increased with the increase in concentration of filler. The tensile tenacity, strain, and modulus were modeled with current composite models for particulate filled composites. The tenacity and strain models did not accurately predict the properties of the filaments, while the modulus models were more accurate, perhaps because the agglomerations of filler did not affect the modulus as much as it affected the tenacity and strain of the filaments. Production, characterization, and modeling of these filaments indicates that there are many areas for improvements, such as improved mixing of the filler and polypropylene, increased adhesion between matrix and filler, and decreased agglomerations of filler. Mechanically, these filaments can not match the properties of bone. However, they do have many structural similarities at the micro-mechanical level, so with some improvements in properties these filaments may be suitable models for modeling bone behavior.

Ultrasound detection and identification of cosmetic fillers in the skin.

PubMed

Wortsman, X; Wortsman, J; Orlandi, C; Cardenas, G; Sazunic, I; Jemec, G B E

2012-03-01

While the incidence of cosmetic filler injections is rising world-wide, neither exact details of the procedure nor the agent used are always reported or remembered by the patients. Thus, although complications are reportedly rare, availability of a precise diagnostic tool to detect cutaneous filler deposits could help clarify the association between the procedure and the underlying pathology. The aim of this study was to evaluate cutaneous sonography in the detection and identification of cosmetic fillers deposits and, describe dermatological abnormalities found associated with the presence of those agents. We used ultrasound in a porcine skin model to determine the sonographic characteristics of commonly available filler agents, and subsequently applied the analysis to detect and identify cosmetic fillers among patients referred for skin disorders. Fillers are recognizable on ultrasound and generate different patterns of echogenicity and posterior acoustic artefacts. Cosmetic fillers were identified in 118 dermatological patients; most commonly hyaluronic acid among degradable agents and silicone oil among non-degradable. Fillers deposits were loosely scattered throughout the subcutaneous tissue, with occasional infiltration of local muscles and loco-regional lymph nodes. Accompanying dermatopathies were represented by highly localized inflammatory processes unresponsive to conventional treatment, morphea-like reactions, necrosis of fatty tissue and epidermal cysts; in the case of non-degradable agents, the associated dermatopathies were transient, resolving upon disappearance of the filler. Cosmetic filler agents may be detected and identified during routine ultrasound of dermatological lesions; the latter appear to be pathologically related to the cosmetic procedure. © 2011 The Authors. Journal of the European Academy of Dermatology and Venereology © 2011 European Academy of Dermatology and Venereology.

Elastic and Sorption Characteristics of an Epoxy Binder in a Composite During Its Moistening

NASA Astrophysics Data System (ADS)

Aniskevich, K.; Glaskova, T.; Jansons, J.

2005-07-01

Results of an experimental investigation into the elastic and sorption characteristics of a model composite material (CM) — epoxy resin filled with LiF crystals — during its moistening are presented. Properties of the binder in the CM with different filler contents ( v f = 0, 0.05, 0.11, 0.23, 0.28, 0.33, 0.38, and 0.46) were evaluated indirectly by using known micromechanical models of CMs. It was revealed that, for the CM in a conditionally initial state, the elastic modulus of the binder in it and the filler microstrain (change in the interplanar distance in the crystals, measured by the X-ray method) as functions of filler content had the same character. The elastic modulus of the binder in the CM with a low filler content was equal to that for the binder in a block; the elastic modulus of the binder in the CM decreased with increasing filler content. The maximum (corresponding to water saturation of the CM) stresses in the binder and the filler microstresses as functions of filler content were of the same character. Moreover, the absolute values of maximum stresses in the binder and of filler microstresses coincided for high and low contents of the filler. At v f = 0.2-0. 3, the filler microstrains exceeded the stresses in the binder. The effect of moisture on the epoxy binder in the CM with a high filler content was not entirely reversible: the elastic characteristics of the binder increased, the diffusivity decreased, and the ultimate water content increased after a moistening-drying cycle.

A novel cardanol-based antioxidant and its application in vegetable oils and biodiesel

USDA-ARS?s Scientific Manuscript database

A novel antioxidant, epoxidized cardanol (ECD), derived from cardanol has been synthesized and characterized by FT-IR, 1H-NMR and 13C-NMR. Oxidative stability of ECD in vegetable oils and biodiesel was evaluated by the pressurized differential scanning calorimetry and Rancimat methods, respectively....

Improved fiber retention by the use of fillers in graphite fiber/resin matrix composites

NASA Technical Reports Server (NTRS)

Gluyas, R. E.; Bowles, K. J.

1980-01-01

A variety of matrix fillers were tested for their ability to prevent loss of fiber from graphite fiber/PMR polyimide and graphite fiber/epoxy composites in a fire. The fillers tested included powders of boron, boron carbide lime glass, lead glass, and aluminum. Boron was the most effective and prevented any loss of graphite fiber during burning. Mechanical properties of composites containing boron filler were measured and compared to those of composites containing no filler.

40 CFR 63.1427 - Process vent requirements for processes using extended cookout as an epoxide emission reduction...

Code of Federal Regulations, 2014 CFR

2014-07-01

... = Concentration of epoxide in the reactor liquid at the beginning of the time period, weight percent. k = Reaction rate constant, 1/hr. t = Time, hours. Note: This equation assumes a first order reaction with respect... process knowledge, reaction kinetics, and engineering knowledge, in accordance with paragraph (a)(2)(i) of...