Comparison of the shear bond strength of self-adhesive resin cements to enamel and dentin with different protocol of application

PubMed Central

Moghaddas, Mohammad Javad; Hossainipour, Zahra; Majidinia, Sara; Ojrati, Najmeh

2017-01-01

Aim The aim of the present study was to determine the shear bond strength of self-adhesive resin cements to enamel and dentin with and without surface treatments, and compare them with conventional resin cement as the control group. Methods In this experimental study, buccal and lingual surface of the thirty sound human premolars were polished in order to obtain a flat surface of enamel (E) in buccal, and dentin (D) in lingual. Sixty feldspathic ceramic blocks (2×3×3 mm) were prepared and randomly divided into six groups (n=10). Each block was cemented to the prepared surface (30 enamel and 30 dentin surface) according to different protocol: E1 and D1; RelyX ARC as control group, E2, D2; RelyX Unicem, E3, D3; acid etching +RelyX Unicem. The specimens were termocycled and subjected to shear forces by a universal testing machine at a cross head speed of 0.5 mm/min. The mode of fracture were evaluated by stereomicroscope. Data were analyzed with descriptive statistical methods using SPSS version 15. One-way ANOVA, and post hoc Tukey tests were used to compare bond strengths between the groups with different adhesives at α=0.05. Results Statistical analysis showed no significant differences within the enamel subgroups, but there were significant differences within the dentinal subgroups, and statistically significant differences were found between the groups D1and D3 (p=0.02). Comparison between similar enamel and dentinal subgroups showed that there was a significant difference just between the subgroups E3 and D3 (p=0.01). Conclusion Elective etching of enamel did not lead to significant increase in the shear bond strength of RelyX Unicem in comparison to RelyX ARC. On the other hand, elective etching of dentin reduces the bond strength of RelyX Unicem with the dentin. PMID:28979732

Comparison of the shear bond strength of self-adhesive resin cements to enamel and dentin with different protocol of application.

PubMed

Moghaddas, Mohammad Javad; Hossainipour, Zahra; Majidinia, Sara; Ojrati, Najmeh

2017-08-01

The aim of the present study was to determine the shear bond strength of self-adhesive resin cements to enamel and dentin with and without surface treatments, and compare them with conventional resin cement as the control group. In this experimental study, buccal and lingual surface of the thirty sound human premolars were polished in order to obtain a flat surface of enamel (E) in buccal, and dentin (D) in lingual. Sixty feldspathic ceramic blocks (2×3×3 mm) were prepared and randomly divided into six groups (n=10). Each block was cemented to the prepared surface (30 enamel and 30 dentin surface) according to different protocol: E1 and D1; RelyX ARC as control group, E2, D2; RelyX Unicem, E3, D3; acid etching +RelyX Unicem. The specimens were termocycled and subjected to shear forces by a universal testing machine at a cross head speed of 0.5 mm/min. The mode of fracture were evaluated by stereomicroscope. Data were analyzed with descriptive statistical methods using SPSS version 15. One-way ANOVA, and post hoc Tukey tests were used to compare bond strengths between the groups with different adhesives at α=0.05. Statistical analysis showed no significant differences within the enamel subgroups, but there were significant differences within the dentinal subgroups, and statistically significant differences were found between the groups D1and D3 (p=0.02). Comparison between similar enamel and dentinal subgroups showed that there was a significant difference just between the subgroups E3 and D3 (p=0.01). Elective etching of enamel did not lead to significant increase in the shear bond strength of RelyX Unicem in comparison to RelyX ARC. On the other hand, elective etching of dentin reduces the bond strength of RelyX Unicem with the dentin.

Smear layer-deproteinizing improves bonding of one-step self-etch adhesives to dentin.

PubMed

Thanatvarakorn, Ornnicha; Prasansuttiporn, Taweesak; Thittaweerat, Suppason; Foxton, Richard M; Ichinose, Shizuko; Tagami, Junji; Hosaka, Keiichi; Nakajima, Masatoshi

2018-03-01

Smear layer deproteinizing was proved to reduce the organic phase of smear layer covered on dentin surface. It was shown to eliminate hybridized smear layer and nanoleakage expression in resin-dentin bonding interface of two-step self-etch adhesive. This study aimed to investigate those effects on various one-step self-etch adhesives. Four different one-step self-etch adhesives were used in this study; SE One (SE), Scotchbond™ Universal (SU), BeautiBond Multi (BB), and Bond Force (BF). Flat human dentin surfaces with standardized smear layer were prepared. Smear layer deproteinizing was carried out by the application of 50ppm hypochlorous acid (HOCl) on dentin surface for 15s followed by Accel ® (p-toluenesulfinic acid salt) for 5s prior to adhesive application. No surface pretreatment was used as control. Microtensile bond strength (μTBS) and nanoleakage under TEM observation were investigated. The data were analyzed by two-way ANOVA and Tukey's post-hoc test and t-test at the significant level of 0.05. Smear layer deproteinizing significantly improved μTBS of SE, SU, and BB (p<0.001). Hybridized smear layer observed in control groups of SE, BB, and BF, and reticular nanoleakage presented throughout the hybridized complex in control groups of BB and BF were eliminated upon the smear layer deproteinizing. Smear layer deproteinizing by HOCl and Accel ® application could enhance the quality of dentin for bonding to one-step self-etch adhesives, resulting in the improving μTBS, eliminating hybridized smear layer and preventing reticular nanoleakage formation in resin-dentin bonding interface. Copyright © 2018 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Polymerization contraction stress in dentin adhesives bonded to dentin and enamel.

PubMed

Hashimoto, Masanori; de Gee, Anton J; Feilzer, Albert J

2008-10-01

In a previous study on of polymerization contraction stress determinations of adhesives bonded to dentin a continuous decline of stress was observed after the adhesives had been light-cured. The decline was ascribed to stress relief caused by diffusion into the adhesive layer of water and/or solvents, left in the impregnated dentin surface after drying and/or evaporation in the application procedure. The purpose of the present study was to test the hypothesis that the contraction stress of adhesives bonded to enamel will not decline after light-curing, based on the assumption that water and/or solvents are more efficiently removed from impregnated enamel surfaces in the drying and/or evaporation step. Contraction stress was determined in a tensilometer for three total-etching adhesives Scotchbond multi-purpose, Single bond and One-step plus and four self-etching adhesives Clearfil SE Bond, Clearfil Protect Bond, AdheSE, and Xeno III. The adhesives were placed in a thin layer between a glass plate and a flat dentin or enamel surface pre-treated with phosphoric acid or self-etching primer and light-cured under constrained conditions. All adhesives bonded to enamel showed a stress decline, but significantly less than for dentin with the exception of two self-etching adhesives. The greatest decline was found for the total-etching adhesive systems bonded to dentin. The presence of hydrophobic monomers in the adhesives had a significant influence on the decline. The experiments indicate that fluids are withdrawn from the resin impregnated tooth structures, which may result in small defects in the tooth-resin interfaces.

Effects of attrition, prior acid-etching, and cyclic loading on the bond strength of a self-etching adhesive system to dentin.

PubMed

Shinkai, Koichi; Ebihara, Takashi; Shirono, Manabu; Seki, Hideaki; Wakaki, Suguru; Suzuki, Masaya; Suzuki, Shiro; Katoh, Yoshiroh

2009-03-01

The purpose of this study was to evaluate the effects of dentin attrition, phosphoric acid etching, and cyclic loading on the microtensile bond strength (microTBS) of a self-etching adhesive system to dentin. Flat dentin surfaces of human molars were assigned to eight experimental groups based on those with or without attrition, prior acid-etching, and cyclic loading. Resin composite paste was placed and polymerized after the bonding procedure according to manufacturer's instructions. The specimens were subjected to microTBS testing at a crosshead speed of 0.5 mm/min. Results showed that the minimum mean value of microTBS was 14.9 MPa in the group without attrition and acid-etching but with loading, while the maximum mean value of microTBS was 40.0 MPa in the group without attrition and loading but with acid etching. Therefore, the value of microTBS to dentin without attrition was significantly decreased by cyclic loading but that to dentin with attrition was not affected.

Effect of handpiece maintenance method on bond strength.

PubMed

Roberts, Howard W; Vandewalle, Kraig S; Charlton, David G; Leonard, Daniel L

2005-01-01

This study evaluated the effect of dental handpiece lubricant on the shear bond strength of three bonding agents to dentin. A lubrication-free handpiece (one that does not require the user to lubricate it) and a handpiece requiring routine lubrication were used in the study. In addition, two different handpiece lubrication methods (automated versus manual application) were also investigated. One hundred and eighty extracted human teeth were ground to expose flat dentin surfaces that were then finished with wet silicon carbide paper. The teeth were randomly divided into 18 groups (n=10). The dentin surface of each specimen was exposed for 30 seconds to water spray from either a lubrication-free handpiece or a lubricated handpiece. Prior to exposure, various lubrication regimens were used on the handpieces that required lubrication. The dentin surfaces were then treated with total-etch, two-step; a self-etch, two-step or a self-etch, one-step bonding agent. Resin composite cylinders were bonded to dentin, the specimens were then thermocycled and tested to failure in shear at seven days. Mean bond strength data were analyzed using Dunnett's multiple comparison test at an 0.05 level of significance. Results indicated that within each of the bonding agents, there were no significant differences in bond strength between the control group and the treatment groups regardless of the type of handpiece or use of routine lubrication.

[Influence of carbodiimide-ethanol solution surface treatment on dentin microtensile bond strength].

PubMed

Zhang, Yi; Liu, Yu-hua; Zhou, Yong-sheng; Chung, Kwok-hung

2015-10-18

To evaluate the microtensile bond strength changes and patterns of fractures of the bonding interface after dentine surface treatment with carbodiimide-ethanol solution. 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide (EDC) dissolved in ethanol was diluted into different concentrations of 2, 1, 0.3, 0.1 and 0.01 mol/L EDC-ethanol solutions. Twenty-eight caries-free extracted human third molars were ground metallurgically to prepare flat occlusal mid-coronal dentin surfaces and etched with 35% (mass fraction) phosphoric acid gel. Then they were treated with EDC-ethanol solution for 60 s before the bonding procedure and randomly divided into five experimental groups corresponding to the tested EDC-ethanol concentrations. The ethanol treated and no pre-treated surfaces were used as controls. Single Bond 2 adhesive was applied and resin composite disk was stacked on the treated dentine surface. The teeth with resin composite disks were stored in water at room temperature for 24 h and then sectioned longitudinally to produce stick specimens for microtensile bond strength test. Fracture patterns were observed with a stereomicroscope. The dentin surfaces pre-treated with 2 mol/L [(22.17±13.31) MPa] and 1 mol/L [(45.31±17.80) MPa] EDC-ethanol solutions resulted in statistically significant lower bond strength value (P<0.05). Increasing numbers of fracture pattern at the resin-dentin interface were also found in this two groups with percentages of 81.2% and 41.3% respectively. No significant difference was observed in the groups with 0.3, 0.1, 0.01 mol/L EDC surface treatment (P>0.05). No significant difference of immediate bond strengths was found in the 0.3, 0.1, 0.01 mol/L groups compared with the control group. EDC-ethanol solution surface treatment with concentrations of 2 mol/L and 1 mol/L resulted in decreasing of the bonding strength.

Effect of indirect composite treatment microtensile bond strength of self-adhesive resin cements

PubMed Central

Escribano, Nuria; Baracco, Bruno; Romero, Martin; Ceballos, Laura

2016-01-01

Background No specific indications about the pre-treatment of indirect composite restorations is provided by the manufacturers of most self-adhesive resin cements. The potential effect of silane treatment to the bond strength of the complete tooth/indirect restoration complex is not available.The aim of this study was to determine the contribution of different surface treatments on microtensile bond strength of composite overlays to dentin using several self-adhesive resin cements and a total-etch one. Material and Methods Composite overlays were fabricated and bonding surfaces were airborne-particle abraded and randomly assigned to two different surface treatments: no treatment or silane application (RelyX Ceramic Primer) followed by an adhesive (Adper Scotchbond 1 XT). Composite overlays were luted to flat dentin surfaces using the following self-adhesive resin cements: RelyX Unicem, G-Cem, Speedcem, Maxcem Elite or Smartcem2, and the total-etch resin cement RelyX ARC. After 24 h, bonded specimens were cut into sticks 1 mm thick and stressed in tension until failure. Two-way ANOVA and SNK tests were applied at α=0.05. Results Bond strength values were significantly influenced by the resin cement used (p<0.001). However, composite surface treatment and the interaction between the resin cement applied and surface treatment did not significantly affect dentin bond strength (p>0.05). All self-adhesive resin cements showed lower bond strength values than the total-etch RelyX ARC. Among self-adhesive resin cements, RelyX Unicem and G-Cem attained statistically higher bond strength values. Smartcem2 and Maxcem Elite exhibited 80-90% of pre-test failures. Conclusions The silane and adhesive application after indirect resin composite sandblasting did not improve the bond strength of dentin-composite overlay complex. Selection of the resin cement seems to be a more relevant factor when bonding indirect composites to dentin than its surface treatment. Key words:Bond strength, self-adhesive cement, silane, dentin, indirect composite. PMID:26855700

Effect of temporary cements on the microtensile bond strength of self-etching and self-adhesive resin cement.

PubMed

Carvalho, Edilausson Moreno; Carvalho, Ceci Nunes; Loguercio, Alessandro Dourado; Lima, Darlon Martins; Bauer, José

2014-11-01

The aim of this study was to evaluate the microtensile bond strength (µTBS) of self-etching and self-adhesive resin cement systems to dentin affected by the presence of remnants of either eugenol-containing or eugenol-free temporary cements. Thirty extracted teeth were obtained and a flat dentin surface was exposed on each tooth. Acrylic blocks were fabricated and cemented either with one of two temporary cements, one zinc oxide eugenol (ZOE) and one eugenol free (ZOE-free), or without cement (control). After cementation, specimens were stored in water at 37°C for 1 week. The restorations and remnants of temporary cements were removed and dentin surfaces were cleaned with pumice. Resin composite blocks were cemented to the bonded dentin surfaces with one of two resin cements, either self-etching (Panavia F 2.0) or self-adhesive (RelyX U-100). After 24 h, the specimens were sectioned to obtain beams for submission to µTBS. The fracture mode was evaluated under a stereoscopic loupe and a scanning electron microscope (SEM). Data from µTBS were submitted to two-way repeated-measure ANOVA and the Tukey test (alpha = 0.05). The cross-product interaction was statistically significant (p < 0.0003). The presence of temporary cements reduced the bond strength to Panavia self-etching resin cements only (p < 0.05). Fracture occurred predominantly at the dentin-adhesive interface. The presence of eugenol-containing temporary cements did not interfere in the bond strength to dentin of self-adhesive resin cements.

Toothbrush abrasivity in a long-term simulation on human dentin depends on brushing mode and bristle arrangement.

PubMed

Bizhang, Mozhgan; Schmidt, Ilka; Chun, Yong-Hee Patricia; Arnold, Wolfgang H; Zimmer, Stefan

2017-01-01

The aim of this study was to evaluate the susceptibility of dentin to brushing abrasion using four different toothbrushes (rotating-oscillating, sonic and two types of manual toothbrushes) with the same brushing forces. Dentin samples (n = 72) were selected from 72 impacted third molars. Half of the surface of dentin samples was covered with an adhesive tape, creating a protected and a freely exposed area in the same specimen. Brushing was performed with either a: sonic (Sonicare PowerUp, Philips GmbH, Hamburg, Germany), b: oscillating-rotating (Oral B Vitality Precisions Clean, Procter & Gamble, Schwalbach am Taunus, Germany) or two different manual toothbrushes c: flat trim brush head toothbrush (Dr. Best: Original, Glaxo-Smith-Kline, Bühl, Germany) and d: rippled-shaped brush head toothbrush (Blend-a-Dent, Complete V-Interdental, Blend-a-med, Schwalbach, Germany) in a custom made automatic brushing machine. The brushing force was set to 2 N and a whitening toothpaste (RDA = 150) was used. The simulation period was performed over a calculated period to mimic a brushing behavior of two times a day brushing for eight years and six months. Dentin loss was quantitatively determined by profilometry and statistically analyzed by Wilcoxon and Mann-Whitney-U Test (p < 0.05). The mean (standard deviation) surface loss was 21.03 (±1.26) μm for the sonic toothbrush, 15.71 (±0.85) μm for the oscillating-rotating toothbrush, 6.13 (±1.24) μm for the manual toothbrush with flat trim brush head and 2.50 (±0.43) μm for the manual toothbrush with rippled-shaped brush head. Differences between all groups were statistically significant at p<0.05. Using the same brushing force and a highly abrasive toothpaste, manual toothbrushes are significantly less abrasive compared to power toothbrushes for an 8.5-year simulation.

Toothbrush abrasivity in a long-term simulation on human dentin depends on brushing mode and bristle arrangement

PubMed Central

2017-01-01

Objective The aim of this study was to evaluate the susceptibility of dentin to brushing abrasion using four different toothbrushes (rotating-oscillating, sonic and two types of manual toothbrushes) with the same brushing forces. Methods Dentin samples (n = 72) were selected from 72 impacted third molars. Half of the surface of dentin samples was covered with an adhesive tape, creating a protected and a freely exposed area in the same specimen. Brushing was performed with either a: sonic (Sonicare PowerUp, Philips GmbH, Hamburg, Germany), b: oscillating-rotating (Oral B Vitality Precisions Clean, Procter & Gamble, Schwalbach am Taunus, Germany) or two different manual toothbrushes c: flat trim brush head toothbrush (Dr. Best: Original, Glaxo-Smith-Kline, Bühl, Germany) and d: rippled-shaped brush head toothbrush (Blend-a-Dent, Complete V-Interdental, Blend-a-med, Schwalbach, Germany) in a custom made automatic brushing machine. The brushing force was set to 2 N and a whitening toothpaste (RDA = 150) was used. The simulation period was performed over a calculated period to mimic a brushing behavior of two times a day brushing for eight years and six months. Dentin loss was quantitatively determined by profilometry and statistically analyzed by Wilcoxon and Mann-Whitney-U Test (p < 0.05). Results The mean (standard deviation) surface loss was 21.03 (±1.26) μm for the sonic toothbrush, 15.71 (±0.85) μm for the oscillating-rotating toothbrush, 6.13 (±1.24) μm for the manual toothbrush with flat trim brush head and 2.50 (±0.43) μm for the manual toothbrush with rippled-shaped brush head. Differences between all groups were statistically significant at p<0.05. Conclusion Using the same brushing force and a highly abrasive toothpaste, manual toothbrushes are significantly less abrasive compared to power toothbrushes for an 8.5—year simulation. PMID:28222156

Effect of air-blowing variables on bond strength of all-in-one adhesives to bovine dentin.

PubMed

Shinkai, Koichi; Suzuki, Shiro; Katoh, Yoshiroh

2006-12-01

This study evaluated the effect of air-blowing variables on the microtensile bond strength (microTBS) of two all-in-one adhesives. A bonding agent was applied to the flat dentin surface of extracted bovine teeth, and the surface left undisturbed for 20 seconds. Gentle or intensive air-blowing was applied for five seconds, and the adhesive photopolymerized for 10 seconds. Resin composite paste was placed and cured after each bonding treatment. Specimens were subjected to microTBS test with a crosshead speed of 1.0 mm/min. Data were statistically analyzed using ANOVA, followed by Bonferroni post hoc test. When Clearfil tri-S Bond was bonded to dentin, the microTBS value of specimens applied with intensive air-blowing was significantly higher than that applied with gentle air-blowing (p<0.01). On the other hand, with Fluoro Bond Shake One, the microTBS value of specimens applied with intensive air-blowing was significantly lower than that applied with gentle air-blowing (p<0.01).

Long-term bonding effectiveness of simplified etch-and-rinse adhesives to dentin after different surface pre-treatments

PubMed Central

Verma, Radhika; Singh, Udai Pratap; Tyagi, Shashi Prabha; Nagpal, Rajni; Manuja, Naveen

2013-01-01

Objective: To evaluate the effect of 2% chlorhexidine (CHX) and 30% proanthocyanidin (PA) application on the immediate and long-term bond strength of simplified etch-and-rinse adhesives to dentin. Materials and Methods: One hundred twenty extracted human molar teeth were ground to expose the flat dentin surface. The teeth were equally divided into six groups according to the adhesives used, either Tetric N Bond or Solobond M and pretreatments given either none, CHX, or PA. Composite cylinder was bonded to each specimen using the respective adhesive technique. Half the samples from each group (n = 10) were then tested immediately. The remaining samples were tested after 6 month storage in distilled water. Results: The mean bond strength of samples was not significantly different upon immediate testing being in the range of 8.4(±0.7) MPa. The bond strength fell dramatically in the control specimens after 6 month storage to around 4.7(±0.33) MPa, while the bond strength was maintained in the samples treated with both CHX and PA. Conclusion: Thirty percent PA was comparable to 2% CHX with respect to preservation of the resin dentin bond over 6 months. PMID:23956543

Effect of sonic application mode on the resin-dentin bond strength and dentin permeability of self-etching systems.

PubMed

Mena-Serrano, Alexandra; Costa, Thays Regina Ferreira da; Patzlaff, Rafael Tiago; Loguercio, Alessandro Dourado; Reis, Alessandra

2014-10-01

To compare manual and sonic adhesive application modes in terms of the permeability and microtensile bond strength of a self-etching adhesive applied in the one-step or two-step protocol. Self-etching All Bond SE (Bisco) was applied as a one- or a two-step adhesive under manual or sonic vibration modes on flat occlusal dentin surfaces of 64 human molars. Half of the teeth were used to measure the hydraulic conductance of dentin at 200 cm H₂O hydrostatic pressure for 5 min immediately after the adhesive application. In the other half, composite buildups (Opallis) were constructed incrementally to create resin-dentin sticks with a cross-sectional area of 0.8 mm² to be tested in tension (0.5 mm/min) immediately after restoration placement. Data were analyzed using a two-way ANOVA and Tukey's test (α = 0.05). The fluid conductance of dentin was significantly reduced by the sonic vibration mode for both adhesives, but no effect on the bond strength values was observed for either adhesive. The sonic application mode at an oscillating frequency of 170 Hz can reduce the fluid conductance of the one- and two-step All Bond SE adhesive when applied on dentin.

Adhesive permeability affects coupling of resin cements that utilise self-etching primers to dentine.

PubMed

Carvalho, R M; Pegoraro, T A; Tay, F R; Pegoraro, L F; Silva, N R F A; Pashley, D H

2004-01-01

To examine the effects of an experimental bonding technique that reduces the permeability of the adhesive layer on the coupling of resin cements to dentine. Extracted human third molars had their mid to deep dentin surface exposed flat by transversally sectioning the crowns. Resin composite overlays were constructed and cemented to the surfaces using either Panavia F (Kuraray) or Bistite II DC (Tokuyama) resin cements mediated by their respective one-step or two-step self-etch adhesives. Experimental groups were prepared in the same way, except that the additional layer of a low-viscosity bonding resin (LVBR, Scotchbond Multi-Purpose Plus, 3M ESPE) was placed on the bonded dentine surface before luting the overlays with the respective resin cements. The bonded assemblies were stored for 24 h in water at 37 degrees C and subsequently prepared for microtensile bond strength testing. Beams of approximately 0.8 mm(2) were tested in tension at 0.5 mm/min in a universal tester. Fractured surfaces were examined under scanning electron microscopy (SEM). Additional specimens were prepared and examined with TEM using a silver nitrate-staining technique. Two-way ANOVA showed significant interactions between materials and bonding protocols (p<0.05). When bonded according to manufacturer's directions, Panavia F produced bond strengths that were significantly lower than Bistite II DC (p<0.05). The placement of an additional layer of a LVBR improved significantly the bond strengths of Panavia F (p<0.05), but not of Bistite II DC (p>0.05). SEM observation of the fractured surfaces in Panavia F showed rosette-like features that were exclusive for specimens bonded according to manufacturer's directions. Such features corresponded well with the ultrastructure of the interfaces that showed more nanoleakage associated with the more permeable adhesive interface. The application of the additional layer of the LVBR reduced the amount of silver impregnation for both adhesives suggesting that reduced permeability of the adhesives resulted in improved coupling of the resin cements to dentin. Placement of an intermediate layer of a LVBR between the bonded dentine surface and the resin cements resulted in improved coupling of Panavia F to dentine.

Zinc oxide eugenol paste jeopardises the adhesive bonding to primary dentine.

PubMed

Pires, C W; Lenzi, T L; Soares, F Z M; Rocha, R O

2018-05-12

This was to evaluate the influence of root canal filling pastes on microshear bond strength (µSBS) of an adhesive system to primary dentine. Human (32) primary molars were randomly assigned into four experimental groups (n = 8): zinc oxide eugenol paste (ZOE); iodoform paste (Guedes-Pinto paste); calcium hydroxide paste thickened with zinc oxide; and no filling paste (control). Flat dentine surfaces were covered with a 1 mm-thick layer of the pastes for 15 min at 37 °C. The pastes were mechanically removed from dentine surfaces, followed by rinsing and drying. After adhesive application (Adper Single Bond 2, 3M ESPE), starch tubes were placed over pre-treated dentine and filled with composite resin (Z250, 3M ESPE). The µSBS test was performed after 24 h of water storage at 37 °C. The failure mode was evaluated using a stereomicroscope. The µSBS values (MPa) were analysed with one-way ANOVA and Tukey post-hoc tests (α = 0.05). The lowest µSBS values were achieved when ZOE was used. No difference was found among other filling pastes compared with control group. All specimens showed adhesive/mixed failures. Zinc oxide eugenol paste negatively influenced the bond strength of adhesive systems to primary dentine. Iodoform-based Guedes-Pinto paste and calcium hydroxide paste thickened with zinc oxide did not influence the microshear bond strength values.

Influence of previous acid etching on bond strength of universal adhesives to enamel and dentin.

PubMed

Torres, Carlos Rocha Gomes; Zanatta, Rayssa Ferreira; Silva, Tatiane Josefa; Huhtala, Maria Filomena Rocha Lima; Borges, Alessandra Bühler

2017-01-01

The objective of this study was to evaluate the effect of acid pretreatment on the bond strength of composite resin bonded to enamel and dentin with 2 different universal self-etching adhesives. The null hypothesis was that the acid treatment performed prior to adhesive application would not significantly change the bond strength to enamel or dentin for either universal adhesive tested. A sample of 112 bovine incisors were selected and embedded in acrylic resin. Half were ground until a flat enamel surface was obtained, and the other half were polished until a 6 × 6-mm area of dentin was exposed, resulting into 2 groups (n = 56). The enamel and dentin groups were divided into 2 subgroups according to the adhesive system applied: Futurabond U or Scotchbond Universal. Each of these subgroups was divided into 2 additional subgroups (n = 14); 1 subgroup received phosphoric acid pretreatment, and 1 subgroup did not. The bond strength was assessed with a microtensile test. Data from enamel and dentin specimens were analyzed separately using 1-way analysis of variance. The acid pretreatment did not significantly change the bond strength of the adhesives tested, either to enamel (P = 0.4161) or to dentin (P = 0.4857). The acid etching pretreatment did not affect the bond strength to dentin and enamel when the tested universal multipurpose adhesive systems were used.

Micro-shear bond strength of resin cement to dentin after application of desensitizing toothpastes.

PubMed

Bavbek, Andac Barkin; Goktas, Baris; Cekic-Nagas, Isil; Egilmez, Ferhan; Ergun, Gulfem; Eskitascioglu, Gurcan

2013-01-01

The aim of the study was to evaluate the effect of three desensitizing toothpastes on bonding of resin cements to dentin. The occlusal surfaces of 72 maxillary third molars were ground to obtain flat dentin surfaces and then divided into three groups according to three desensitizing toothpastes used: Sensodyne Rapid Relief (GlaxoSmithKline, SmithKline Beecham Ltd., Slough, UK), Signal Sensitive Expert (Unilever Sanayi ve Ticaret Türk A.Ş., Ümraniye, İstanbul, Turkey) and Colgate Sensitive Pro-Relief (Colgate Palmolive, New York, NY). Following bonding of the resin cement (Clearfil™ SA Cement, Kuraray Co, Osaka, Japan) to dentin, the specimens were light cured for 40 s with a LED (Elipar S10, 3M Espe, St. Paul, MN). The strength measurements were accomplished with a micro-shear testing machine (Bisco, Schaumburg, IL) at a cross-head speed of 0.5 mm/min until the failure occurs. Failure modes were examined using a stereomicroscope and scanning electron microscope. The data were analyzed with one-way analysis of variance (ANOVA) and Tukey HSD test (α = 0.05). ANOVA revealed that the application of desensitizing toothpastes had significant effects on bond strength of the resin cement tested to dentin (p < 0.05). Mixed failures were observed in all of the groups. The use of a desensitizing toothpaste before cementation might alter the bond strength of adhesively luted restorations.

The effect of double-coating and times on the immediate and 6-month dentin bonding of universal adhesives.

PubMed

Pashaev, Diial; Demirci, Mustafa; Tekçe, Neslihan; Tuncer, Safa; Baydemir, Canan

2017-01-01

The purpose of this study was to evaluate the effect of double-application coats and times on microtensile bond strength (μTBS) and adhesive-dentin interfaces created by dentin adhesive systems after 6 months of storage in water. Two-hundred sixteen extracted non-carious human third molars were selected for the study. Single-Bond Universal (SU) and All-Bond Universal (AU), Adper Easy One (Eo) Self-Etch adhesive and Adper Single-Bond 2 (Sb) etch-and-rinse adhesive were applied to a flat dentin surface using three methods (1): dentin adhesives were applied as recommended by the manufacturers; (2): two consecutive coats of dentin adhesives were applied before photo-polymerization; and (3): a single coat of adhesive was applied but with twice the manufacturers recommended application time. Microtensile bond strength was determined either immediately or after 6 months of water storage. Data were analyzed using one-way analysis of variance and Tukey's post-hoc tests. At 24 h, groups 1, 2, and 3 exhibited statistically similar results for all dentin adhesive systems. For AU-Er, group 3 showed significantly higher bond strength than all group of AU-Se after 6 months. Universal adhesives seemed more stable against water degradation than traditional two-step etch-and-rinse and all-in-one systems within the 6-month period.

Effects of water storage on bond strength and dentin sealing ability promoted by adhesive systems.

PubMed

Cantanhede de Sá, Renata Bacelar; Oliveira Carvalho, Adriana; Puppin-Rontani, Regina Maria; Ambrosano, Glaúcia Maria; Nikaido, Toru; Tagami, Junji; Giannini, Marcelo

2012-12-01

To evaluate the dentin bond strength (BS) and sealing ability (SA) promoted by adhesive systems after 24 h or 6 months of water storage. The tested adhesive systems were: one three-step etch-and-rinse adhesive (Adper Scotchbond Multi-Purpose, SBMP) and three single-step self-etching systems (Adper Easy Bond, Bond Force, and G-Bond Plus). Bovine incisors were used for both evaluations, BS (n = 11) and SA (n = 5). To examine BS, the buccal surface was ground with SiC paper to expose a flat dentin surface. After adhesive application, a block of resin composite was incrementally built up over the bonded surface and sectioned into sticks. These bonded specimens were subjected to microtensile bond strength testing after 24 h and 6 months of water storage using a universal testing machine. For SA analysis, enamel was removed from the buccal surfaces. The teeth were connected to a device to measure the initial SA (10 psi), and the second measurement was taken after treating dentin with EDTA. Afterwards, the adhesive systems were applied to dentin and the SA was re-measured for each adhesive after 24 h and 6 months of water storage. The SA was expressed in terms of percentage of dentinal sealing. BS and SA data were submitted to two-way ANOVA and Tukey's test (α = 0.05). All adhesives showed a reduction of SA after 6 months of water storage. The SA promoted by self-etching adhesives was higher than that of SBMP. No adhesive system showed a reduction of the BS after 6 months. Sealing ability was affected by water storage, while no changes in microtensile bond strength were observed after 6 months of water storage. The single-step self-etching systems showed greater sealing ability than did SBMP, even after 6 months of storage in water.

Enhanced differentiation of dental pulp cells cultured on microtubular polymer scaffolds in vitro.

PubMed

Haeri, Morteza; Sagomonyants, Karen; Mina, Mina; Kuhn, Liisa T; Goldberg, A Jon

2017-06-01

Dental caries (tooth decay) is the most common chronic disease. Dental tissue engineering is a promising alternative approach to alleviate the shortcomings of the currently available restorative materials. Mimicking the natural extracellular matrix (ECM) could enhance the performance of tissue engineering scaffolds. In this study, we developed microtubular (~20 μm diameter) polymethyl methacrylate (PMMA) scaffolds resembling the tubular (~2.5 μm diameter) structure of dentin, the collagen-based mineralized tissue that forms the major portion of teeth, to study the effect of scaffold architecture on differentiation of mouse dental pulp cells in vitro . Flat (control), plasma-treated solid and microtubular PMMA scaffolds with densities of 240±15, 459±51 and 480±116 tubules/mm 2 were first characterized using scanning electron microscopy and contact angle measurements. Dental pulp cells were cultured on the surface of the scaffolds for up to 21 days and examined using various assays. Cell proliferation and mineralization were examined using Alamar Blue and Xylenol Orange (XO) staining assays, respectively. The differentiation of pulp cells into odontoblasts was examined by immunostaining for Nestin and by quantitative PCR analysis for dentin matrix protein 1 ( Dmp1 ), dentin sialophosphoprotein ( Dspp ) and osteocalcin ( Ocn ). Our results showed that the highest tubular density scaffolds significantly (p<0.05) enhanced differentiation of pulp cells into odontoblasts as compared to control flat scaffolds, as evidenced by increased expression of Nestin (5.4x). However, mineralization was suppressed on all surfaces, possibly due to low cell density. These results suggest that the microtubular architecture may be a desirable feature of scaffolds developed for clinical applications. Regenerative engineering of diseased or traumatized tooth structure could avoid the deficiencies of traditional dental restorative (filling) materials. Cells in the dental pulp have the potential to differentiate to dentin-producing odontoblast cells. Furthermore, cell-supporting scaffolds that mimic a natural extracellular matrix (ECM) are known to influence behavior of progenitor cells. Accordingly, we hypothesized that a dentin-like microtubular scaffold would enhance differentiation of dental pulp cells. The hypothesis was proven true and differentiation to odontoblasts increased with increasing density of the microtubules. However, mineralization was suppressed, possibly due to a low density of cells. The results demonstrate the potential benefits of a microtubular scaffold design to promote odontoblast cells for regeneration of dentin.

Effect of time on tensile bond strength of resin cement bonded to dentine and low-viscosity composite.

PubMed

Duarte, Rosângela Marques; de Goes, Mario Fernando; Montes, Marcos Antonio Japiassú Resende

2006-01-01

The purpose of this study was to evaluate the tensile bond strength (TBS) of Panavia F resin cement (PF) applied on dentine pre-treated with ED Primer (ED) and Clearfil Liner Bond 2V (CLB) coated with a layer of low-viscosity composite Protect Liner F (PLF) at 10 min, 24 h and 12 months after curing. The labial surfaces of 60 bovine lower incisors were ground to obtain a flat dentine surface, allowing a demarcation of a 4.0 mm-diameter area with adhesive tape. The teeth were randomly divided in six groups; ED was applied in groups A I, A II and A III and CLB was applied, followed by PLF, in groups B I, B II and B III. A resin composite rod with a wire loop was luted directly to the prepared surface of each group with PF. The specimens of groups A I and B I were submitted to TBS test after 10 min. Groups A II and B II were submitted to TBS test after 24 h storage and groups A III and B III were submitted to TBS test after 12 months storage. Each specimen was inspected by SEM and classified according to the failure mode. Additionally, two representative specimens of each failure mode were sectioned for a composite/dentine interface SEM evaluation. No significant statistical differences were observed among the groups at 10 min and 24 h. Groups A III and B III presented the lowest TBS values (p<0.05) after 12 months storage. PF on resin-coated dentin (PLF) showed the highest TBS values and was statistically different to PF on dentine for all the groups. The fracture pattern was generally cohesive on the adhesive/hybrid layer for groups A I, A II and A III and cohesive on composite resin for B I, B II and B III. The use of a less hydrophilic self-etching system to pre-treat dentine, coating with a low-viscosity composite layer prior luting with resin cement, may provide a protection of the hybridised complex, allowing a dentine seal during the 12 months storage period.

Resin–dentin bonds to EDTA-treated vs. acid-etched dentin using ethanol wet-bonding

PubMed Central

Sauro, Salvatore; Toledano, Manuel; Aguilera, Fatima Sánchez; Mannocci, Francesco; Pashley, David H.; Tay, Franklin R.; Watson, Timothy F.; Osorio, Raquel

2013-01-01

Objective To compare resin–dentin bond strengths and the micropermeability of hydrophobic vs. hydrophilic resins bonded to acid-etched or EDTA-treated dentin, using the ethanol wet-bonding technique. Methods Flat dentin surfaces from extracted human third molars were conditioned before bonding with: 37% H3PO4 (15 s) or 0.1 M EDTA (60 s). Five experimental resin blends of different hydrophilicities and one commercial adhesive (SBMP: Scotchbond Multi-Purpose) were applied to ethanol wet-dentin (1 min) and light-cured (20 s). The solvated resins were used as primers (50% ethanol/50% comonomers) and their respective neat resins were used as the adhesive. The resin-bonded teeth were stored in distilled water (24 h) and sectioned in beams for microtensile bond strength testing. Modes of failure were examined by stereoscopic light microscopy and SEM. Confocal tandem scanning microscopy (TSM) interfacial characterization and micropermeability were also performed after filling the pulp chamber with 1 wt% aqueous rhodamine-B. Results The most hydrophobic resin 1 gave the lowest bond strength values to acid-etched dentin and all beams failed prematurely when the resin was applied to EDTA-treated dentin. Resins 2 and 3 gave intermediate bond strengths to both conditioned substrates. Resin 4, an acidic hydrophilic resin, gave the highest bond strengths to both EDTA-treated and acid-etched dentin. Resin 5 was the only hydrophilic resin showing poor resin infiltration when applied on acid-etched dentin. Significance The ethanol wet-bonding technique may improve the infiltration of most of the adhesives used in this study into dentin, especially when applied to EDTA-treated dentin. The chemical composition of the resin blends was a determining factor influencing the ability of adhesives to bond to EDTA-treated or 37% H3PO4 acid-etched dentin, when using the ethanol wet-bonding technique in a clinically relevant time period. PMID:20074787

The effect of increasing sodium fluoride concentrations on erosion and attrition of enamel and dentine in vitro.

PubMed

Austin, R S; Rodriguez, J M; Dunne, S; Moazzez, R; Bartlett, D W

2010-10-01

To investigate the effect of an aqueous sodium fluoride solution of increasing concentration on erosion and attrition of enamel and dentine in vitro. Enamel and dentine sections from caries-free human third molars were polished flat and taped (exposing a 3 mm x 3 mm area) before being randomly allocated to 1 of 5 groups per substrate (n=10/gp): G1 (distilled water control); G2 (225 ppm NaF); G3 (1450 ppm NaF); G4 (5000 ppm NaF); G5 (19,000 ppm NaF). All specimens were subjected to 5, 10 and 15 cycles of experimental wear [1 cycle=artificial saliva (2h, pH 7.0)+erosion (0.3% citric acid, pH 3.2, 5 min)+fluoride/control (5 min)+attrition (60 linear strokes in artificial saliva from enamel antagonists loaded to 300 g)]. Following tape removal, step height (SH) in mum was measured using optical profilometry. When the number of cycles increased the amount of tooth surface loss increased significantly in enamel and dentine after attrition and erosion and for dentine after attrition. Attrition and erosion resulted in greater surface loss than attrition alone after 15 cycles of experimental wear of enamel. 5000 ppm and 19,000 ppm sodium fluoride solutions had a protective effect on erosive and attritional enamel tooth wear in vitro, however no other groups showed significant differences. The more intensive the fluoride regime the more protection was afforded to enamel from attrition and erosion. However, in this study no such protective effect was demonstrated for dentine. Copyright 2010 Elsevier Ltd. All rights reserved.

Effect of hydrostatic pressure on regional bond strengths of compomers to dentine.

PubMed

Zheng, L; Pereira, P N; Somphone, P; Nikaido, T; Tagami, J

2000-09-01

The aim of this study was to evaluate the effect of hydrostatic pressure on the regional bond strengths of compomers to dentine. Thirty freshly extracted molars were ground flat to expose the dentine and randomly divided into two groups for bonding: no hydrostatic pressure and hydrostatic pressure of 15cm H(2)O. Xeno CF, Dyract AP and F 2000 were applied to dentine surfaces pretreated by the respective bonding systems following the manufactures' instructions, and then restored with Clearfil AP-X. After 24h storage in water, the teeth were sectioned into 0.7-mm thick slabs and visually divided into three regional subgroups: the region communicating with the pulp through dentinal tubules (pulp horn); the region between the pulp horns (center); and the region between the pulp horn and DEJ (periphery). The specimens were trimmed to a cross-sectional area of 1mm(2) and subjected to the micro-tensile bond test. The data were analyzed by one- and three-way ANOVA, and Fisher's PLSD (p<0.05). There were no significant regional differences of bond strengths for all the compomers tested (p>0.05). However, hydrostatic pressure significantly decreased the bond strength of F 2000 to all regions (p<0.05), while the bond strength of Dyract AP significantly decreased only at the pulp horn region (p<0.05). On the other hand, the bond strengths of Xeno CF seemed not to be affected by hydrostatic pressure (p>0.05). For Dyract AP and F 2000, the fracture modes were affected by hydrostatic pressure, while, for Xeno CF, there were no significant differences between the fracture modes with non- or positive hydrostatic pressure. Simulated pulpal pressure of 15cm H(2)O had a greater influence on the bond strengths of compomers to dentine than did dentine regions. Therefore, when measuring the bond strengths of compomers to dentine under the simulated in vivo conditions, the wetness of the dentine surface, as well as the intrinsic properties of each material should be seriously considered.

Enamel and dentin bond strengths of a new self-etch adhesive system.

PubMed

Walter, Ricardo; Swift, Edward J; Boushell, Lee W; Braswell, Krista

2011-12-01

statement of problem:  Self-etch adhesives typically are mildly acidic and therefore less effective than etch-and-rinse adhesives for bonding to enamel.   The purpose of this study was to evaluate the enamel and dentin shear bond strengths of a new two-step self-etch adhesive system, OptiBond XTR (Kerr Corporation, Orange, CA, USA).   The labial surfaces of 80 bovine teeth were ground to create flat, 600-grit enamel or dentin surfaces. Composite was bonded to enamel or dentin using the new two-step self-etch system or a three-step etch-and-rinse (OptiBond FL, Kerr), two-step self-etch (Clearfil SE Bond, Kuraray America, Houston, TX, USA), or one-step self-etch adhesive (Xeno IV, Dentsply Caulk, Milford, DE, USA). Following storage in water for 24 hours, shear bond strengths were determined using a universal testing machine. The enamel and dentin data sets were subjected to separate analysis of variance and Tukey's tests. Scanning electron microscopy was used to evaluate the effects of each system on enamel.   Mean shear bond strengths to enamel ranged from 18.1 MPa for Xeno IV to 41.0 MPa for OptiBond FL. On dentin, the means ranged from 33.3 MPa for OptiBond FL to 47.1 MPa for Clearfil SE Bond. OptiBond XTR performed as well as Clearfil SE Bond on dentin and as well as OptiBond FL on enamel. Field emission scanning electron microscope revealed that OptiBond XTR produced an enamel etch pattern that was less defined than that of OptiBond FL (37.5% phosphoric acid) but more defined than that of Clearfil SE Bond or Xeno IV.   The new two-step self-etch adhesive system formed excellent bonds to enamel and dentin in vitro. OptiBond XTR, a new two-step self-etch adhesive system, is a promising material for bonding to enamel as well as to dentin. © 2011 Wiley Periodicals, Inc.

Influence of drying time and temperature on bond strength of contemporary adhesives to dentine.

PubMed

Garcia, Fernanda C P; Almeida, Júlio C F; Osorio, Raquel; Carvalho, Ricardo M; Toledano, Manuel

2009-04-01

To evaluate the bond strength (microTBS) of self-etching adhesives in different solvent evaporation conditions. Flat dentine surfaces from extracted human third molars were bonded with: (1) 2 two-steps self-etching adhesives (Clearfil SE Bond-CSEB); (Protect Bond-PB) and (2) 2 one-step self-etch systems (Adper Prompt L Pop-ADPLP); (Xeno III-XIII). Bonded dentine surfaces were air-dried for 5s, 20s, 30s or 40s at either 21 degrees C or 38 degrees C. Composite build-ups were constructed incrementally. After storage in water for 24h at 37 degrees C, the specimens were prepared for microtensile bond strength testing. Data were analyzed by two-way ANOVA and Student-Newman-Keuls at alpha=0.05. CSEB and PB performed better at warm temperature with only 20s of air-blowing. The bond strength increased when XIII was performed at warm temperature at 40s air-blowing. Extended air-blowing not affect the performance of ADPLP, except at 30s air-blowing time at warm temperature. The use of a warm air-dry stream seems to be a clinical tool to improve the bond strength to self-etching adhesives.

The influence of temporary cements on dental adhesive systems for luting cementation.

PubMed

Ribeiro, José C V; Coelho, Paulo G; Janal, Malvin N; Silva, Nelson R F A; Monteiro, André J; Fernandes, Carlos A O

2011-03-01

This study tested the hypothesis that bond strength of total- and self-etching adhesive systems to dentine is not affected by the presence of remnants from either eugenol-containing (EC) or eugenol-free (EF) temporary cements after standardized cleaning procedures. Thirty non-carious human third molars were polished flat to expose dentine surfaces. Provisional acrylic plates were fabricated and cemented either with EC, EF or no temporary cements. All specimens were incubated for 7 days in water at 37°C. The restorations were then taken out and the remnants of temporary cements were mechanically removed with a dental instrument. The dentine surfaces were cleaned with pumice and treated with either total-etching (TE) or self-etching (SE) dental adhesive systems. Atomic force microscopy was used to examine the presence of remnants of temporary cements before and after dentine cleaning procedures. Composite resin build-ups were fabricated and cemented to the bonded dentine surfaces with a resin luting cement. The specimens were then sectioned to obtain 0.9mm(2) beams for microtensile bond strength testing. Fractographic analysis was performed by optical and scanning electron microscopy. ANOVA showed lower mean microtensile bond strength in groups of specimens treated with EC temporary cement than in groups treated with either no cement or an EF cement (p<0.05). Mean microtensile bond strength was lower in groups employing the SE rather than the TE adhesive system (p<0.001). SE samples were also more likely to fail during initial processing of the samples. There was no evidence of interaction between cement and adhesive system effects on tensile strength. Fractographic analysis indicated different primary failure modes for SE and TE bonding systems, at the dentine-adhesive interface and at the resin cement-resin composite interface, respectively. The use of eugenol-containing temporary cements prior to indirect bonding restorations reduce, to a statistically similar extent, the bond strength of both total- and self-etching adhesive systems to dentine. Copyright © 2011 Elsevier Ltd. All rights reserved.

Resin-dentin bonds to EDTA-treated vs. acid-etched dentin using ethanol wet-bonding. Part II: Effects of mechanical cycling load on microtensile bond strengths.

PubMed

Sauro, Salvatore; Toledano, Manuel; Aguilera, Fatima Sánchez; Mannocci, Francesco; Pashley, David H; Tay, Franklin R; Watson, Timothy F; Osorio, Raquel

2011-06-01

To compare microtensile bond strengths (MTBS) subsequent to load cycling of resin bonded acid-etched or EDTA-treated dentin using a modified ethanol wet-bonding technique. Flat dentin surfaces were obtained from extracted human molars and conditioned using 37% H(3)PO(4) (PA) (15s) or 0.1M EDTA (60s). Five experimental adhesives and one commercial bonding agent were applied to the dentin and light-cured. Solvated experimental resins (50% ethanol/50% comonomers) were used as primers and their respective neat resins were used as the adhesives. The resin-bonded teeth were stored in distilled water (24h) or submitted to 5000 loading cycles of 90N. The bonded teeth were then sectioned in beams for MTBS. Modes of failure were examined by scanning electron microscopy. The most hydrophobic resin 1 gave the lowest bond strength values to both acid and EDTA-treated dentin. The hydrophobic resin 2 applied to EDTA-treated dentin showed lower bond strengths after cycling load but this did not occur when it was bonded to PA-etched dentin. Resins 3 and 4, which contained hydrophilic monomers, gave higher bond strengths to both EDTA-treated or acid-etched dentin and showed no significant difference after load cycling. The most hydrophilic resin 5 showed no significant difference in bond strengths after cycling loading when bonded to EDTA or phosphoric acid treated dentin but exhibited low bond strengths. The presence of different functional monomers influences the MTBS of the adhesive systems when submitted to cyclic loads. Adhesives containing hydrophilic comonomers are not affected by cycling load challenge especially when applied on EDTA-treated dentin followed by ethanol wet bonding. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of Storage Time on Bond Strength and Nanoleakage Expression of Universal Adhesives Bonded to Dentin and Etched Enamel.

PubMed

Makishi, P; André, C B; Ayres, Apa; Martins, A L; Giannini, M

2016-01-01

To investigate bond strength and nanoleakage expression of universal adhesives (UA) bonded to dentin and etched enamel. Extracted human third molars were sectioned and ground to obtain flat surfaces of dentin (n = 36) and enamel (n = 48). Dentin and etched enamel surfaces were bonded with one of two UAs, All-Bond Universal (ABU) or Scotchbond Universal (SBU); or a two-step self-etching adhesive, Clearfil SE Bond (CSEB). A hydrophobic bonding resin, Adper Scotchbond Multi-Purpose Bond (ASMP Bond) was applied only on etched enamel. Following each bonding procedure, resin composite blocks were built up incrementally. The specimens were sectioned and subjected to microtensile bond strength (MTBS) testing after 24 hours or one year water storage, or immersed into ammoniacal silver nitrate solution after aging with 10,000 thermocycles and observed using scanning electron microscopy. The percentage distribution of silver particles at the adhesive/tooth interface was calculated using digital image-analysis software. The MTBS (CSEB = SBU > ABU, for dentin; and CSEB > ABU = SBU = ASMP Bond, for etched enamel) differed significantly between the adhesives after 24 hours. After one year, MTBS values were reduced significantly within the same adhesive for both substrates (analysis of variance, Bonferroni post hoc, p<0.05), and no significant differences were found among the adhesives for etched enamel. Silver particles could be detected within the adhesive/dentin interface of all specimens tested. Kruskal-Wallis mean ranks for nanoleakage in ABU, SBU, and CSEB were 16.9, 18.5 and 11, respectively (p>0.05). In the short term, MTBS values were material and dental-substrate dependent. After aging, a decrease in bonding effectiveness was observed in all materials, with nanoleakage at the adhesive/dentin interface. The bonding of the UAs was equal or inferior to that of the conventional restorative systems when applied to either substrate and after either storage period.

Tensile bond strength of filled and unfilled adhesives to dentin.

PubMed

Braga, R R; Cesar, P F; Gonzaga, C C

2000-04-01

To determine the tensile bond strength of three filled and two unfilled adhesives applied to bovine dentin. Fragments of the labial dentin of bovine incisors were embedded in PVC cylinders with self-cure acrylic resin, and ground flat using 200 grit and 600 grit sandpaper. The following adhesive systems were tested (n=10): Prime & Bond NT, Prime & Bond NT dual cure, Prime & Bond 2.1, OptiBond Solo and Single Bond. A 3 mm-diameter bonding surface was delimited using a perforated adhesive tape. After etching with 37% phosphoric acid and adhesive application, a resin-based composite truncated cone (TPH, shade A3) was built. Tensile test was performed after 24 hrs storage in distilled water at 37 degrees C. Failure mode was accessed using a x10 magnification stereomicroscope. Weibull statistical analysis revealed significant differences in the characteristic strength between Single Bond and Prime & Bond NT dual cure, and between Single Bond and Prime & Bond 2.1. The Weibull parameter (m) was statistically similar among the five groups. Single Bond and Prime & Bond NT showed areas of dentin cohesive failure in most of the specimens. For OptiBond Solo, Prime & Bond NT dual cure and Prime & Bond 2.1 failure was predominantly adhesive.

Effects of Contamination by Hemostatic Agents and Use of Cleaning Agent on Etch-and-Rinse Dentin Bond Strength.

PubMed

Pucci, César Rogério; Araújo, Rodrigo Maximo de; Lacerda, Ana Julia Farias de; Souza, Mirella Anjos de; Huhtala, Maria Filomena Rocha Lima; Feitosa, Fernanda Alves

2016-01-01

The aim of this study was to evaluate the influence of contamination by hemostatic agents and rinsing with chlorhexidine on bond strength between dentin and resin composite. Ninety-six bovine teeth were sectioned to expose a flat dentin surface area. A standardized cavity with 2.0 mm in thickness, superficial diameter of 4.0 mm and bottom diameter of 3.0 mm was prepared with a diamond bur in each dentin specimen. The teeth were divided into four groups according to the hemostatic employed: G1: control; G2: use of ViscoStat, Ultradent; G3: Hemosthasegel, FGM; and G4: Hemostop, Dentsply. The groups were divided into two subgroups according to the cleaning protocol method (n=12): A: without any further cleaning; and B: cleaning with chlorhexidine at 0.2%. All cavities were filled using a dentin adhesive and a resin composite, following the manufacturer's instructions. After 24 h, the specimens were aged by thermal and mechanical cycling. The bond strength was determined by the push out bond test (MPa), Statistical analysis was performed using two-way ANOVA and Tukey test (p<0.05). Statistically significant differences were detected among all groups treated with hemostatic agents and the control group. The post-hoc test showed that cleaning the cavity with chlorhexidine significantly improves the bond strength between dentin and resin composite. Our results suggested that the use of chlorhexidine can reestablish the bond strength between dentin and resin composite when a hemostatic agent was applied.

Shear bond strengths of composite to dentin using six dental adhesive systems.

PubMed

Triolo, P T; Swift, E J; Barkmeier, W W

1995-01-01

The development of adhesive agents for bonding composite to dentin has rapidly evolved in recent years. It is postulated that dentin bond strengths in the range of 17 MPa are sufficient to resist the polymerization shrinkage of composite resins. The purpose of this study was to evaluate the shear bond strengths of the following dentin adhesive systems: All-Bond 2 (Bisco), Imperva Bond (Shofu), Optibond (Kerr), Permagen (Ultradent), ProBond (Caulk/Dentsply), and Scotchbond Multi-Purpose (3M). Sixty human molars (10 per group) were mounted in phenolic rings, and the occlusal surfaces were flat ground in dentin to 600 grit. The prepared dentin bonding sites were treated according to the directions for each of the systems evaluated. A gelatin capsule technique was used to bond Bis-Fil composite cylinders to the teeth. The specimens were stored in water at 37 degrees C for 24 hours. Mean shear bond strengths were as follows: Scotchbond Multi-Purpose: 23.1 +/- 2.6 MPa, All-Bond 2: 21.4 +/- 7.8 MPa, Imperva Bond: 19.8 +/- 6.1 MPa, Optibond: 19.7 +/- 3.6 MPa, ProBond: 16.3 +/- 4.5 MPa, and Permagen: 16.2 +/- 3.0 MPa. There was not a significant difference (P<0.05) in the bond strengths of Scotchbond Multi-Purpose, All-Bond 2, Imperva Bond, and Optibond. The bond strengths of Scotchbond Multi-Purpose and All-Bond 2 were significantly greater (P<0.05) than ProBond and Permagen. Current-generation dentin adhesive systems have approached or exceeded the theoretical threshold value to resist contraction stresses during polymerization of resin materials.

Effect of conditioning solutions containing ferric chloride on dentin bond strength and collagen degradation.

PubMed

Rodrigues, Raquel Viana; Giannini, Marcelo; Pascon, Fernanda Miori; Panwar, Preety; Brömme, Dieter; Manso, Adriana Pigozzo; Carvalho, Ricardo Marins

2017-10-01

To investigate the effects of conditioning solutions containing ferric chloride (FeCl 3 ) on resin-dentin bond strength; on protection of dentin collagen against enzymatic degradation and on cathepsin-K (CT-K) activity. Conditioning solutions were prepared combining citric acid (CA) and anhydrous ferric chloride (FeCl 3 ) in different concentrations. The solutions were applied to etch flat dentin surfaces followed by bonding with adhesive resin. Phosphoric acid (PA) gel etchant was used as control. The microtensile bond strength (μTBS) was tested after 24h of storage in water and after 9 months of storage in phosphate buffer saline. Dentin slabs were demineralized in 0.5M EDTA, pre-treated or not with FeCl 3 and incubated with CT-K. The collagenase activity on dentin collagen matrix was examined and characterized by SEM. Additional demineralized dentin slabs were treated with the conditioning solutions, and the amount of Fe bound to collagen was determined by EDX. The activity of CT-K in the presence of FeCl 3 was monitored fluorimetrically. Data were analyzed by ANOVA followed by post-hoc tests as required (α=5%). Slightly higher bond strengths were obtained when dentin was conditioned with 5% CA/0.6% FeCl 3 and 5% CA-1.8%FeCl 3 regardless of storage time. Bond strengths reduced significantly for all tested conditioners after 9 months of storage. Treating dentin with 1.8% FeCl 3 was effective to preserve the structure of collagen against CT-K. EDX analysis revealed binding of Fe-ions to dentin collagen after 15s immersion of demineralized dentin slabs into FeCl 3 solutions. FeCl 3 at concentration of 0.08% was able to suppress CT-K activity. This study shows that FeCl 3 binds to collagen and offers protection against Cat-K degradation. Mixed solutions of CA and FeCl 3 may be used as alternative to PA to etch dentin in resin-dentin bonding with the benefits of preventing collagen degradation. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Amalgam shear bond strength to dentin using single-bottle primer/adhesive systems.

PubMed

Cobb, D S; Denehy, G E; Vargas, M A

1999-10-01

To evaluate the in vitro shear bond strengths (SBS) of a spherical amalgam alloy (Tytin) to dentin using several single-bottle primer/adhesive systems both alone: Single Bond (SB), OptiBond Solo (Sol), Prime & Bond 2.1 (PB), One-Step (OS) and in combination with the manufacturer's supplemental amalgam bonding agent: Single Bond w/3M RelyX ARC (SBX) and Prime & Bond 2.1 w/Amalgam Bonding Accessory Kit (PBA). Two, three-component adhesive systems, Scotchbond Multi-Purpose (SBMP) and Scotchbond Multi-Purpose Plus w/light curing (S + V) and w/o light curing (S+) were used for comparison. One hundred eight extracted human third molars were mounted lengthwise in phenolic rings with acrylic resin. The proximal surfaces were ground to expose a flat dentin surface, then polished to 600 grit silicon carbide paper. The teeth were randomly assigned to 9 groups (n = 12), and dentin surfaces in each group were treated with an adhesive system according to the manufacturer's instructions, except for S + V specimens, where the adhesive was light cured for 10 s before placing the amalgam. Specimens were then secured in a split Teflon mold, having a 3 mm diameter opening and amalgam was triturated and condensed onto the treated dentin surfaces. Twenty minutes after condensation, the split mold was separated. Specimens were placed in distilled water for 24 hrs, then thermocycled (300 cycles, between 5 degrees C and 55 degrees C, with 12 s dwell time). All specimens were stored in 37 degrees C distilled water for 7 days, prior to shear strength testing using a Zwick Universal Testing Machine at a cross-head speed of 0.5 mm/min. The highest to the lowest mean dentin shear bond strength values (MPa) for the adhesive systems tested were: S + V (10.3 +/- 2.3), SBX (10.2 +/- 3.5), PBA, (6.4 +/- 3.6), SOL (5.8 +/- 2.5), SBMP (5.7 +/- 1.8), S+ (4.8 +/- 2.3), PB (2.7 +/- 2.6), SB (2.7 +/- 1.1) and OS (2.5 +/- 1.8). One-way ANOVA and Duncan's Multiple Range Test indicated significant differences among groups. SBX and S + V produced significantly higher amalgam to dentin shear bond strengths than all other adhesive systems. Bond strengths of amalgam to dentin for the single-bottle adhesives, SOL and PBA were comparable to the three-component systems, SBMP and S+ and were significantly greater than OS, SB and PB (P < 0.05).

[Adhesion of sealer cements to dentin with and without smear layer].

PubMed

Gettleman, B H; Messer, H H; ElDeeb, M E

1991-01-01

The influence of a smear layer on the adhesion of sealer cements to dentin was assessed in recently extracted human anterior teeth. A total of 120 samples was tested, 40 per sealer; 20 each with and without the smear layer. The teeth were split longitudinally, and the internal surfaces were ground flat. One-half of each tooth was left with the smear layer intact, while the other half had the smear removed by washing for 3 min with 17% EDTA followed by 5.25% NaOCI. Evidence of the ability to remove the smear layer was verified by scanning electron microscopy. Using a specially designed jig, the sealer was placed into a 4-mm wide x 4 mm deep well which was then set onto the tooth.

Influence of preheating the bonding agent of a conventional three-step adhesive system and the light activated resin cement on dentin bond strength

PubMed Central

Holanda, Daniel Brandão Vilela; França, Fabiana Mantovani Gomes; do Amaral, Flávia Lucisano Botelho; Flório, Flávia Martão; Basting, Roberta Tarkany

2013-01-01

Aims: to evaluate the influence of preheating the bonding agent (Scotchbond Multipurpose Adhesive/3M ESPE) and the light-activated resin cement (RelyX Venner/3M ESPE) on dentin microtensile bond strength. Materials and Methods: The exposed flat dentin surface of 40 human third molars were randomly distributed into four groups for cementation (SR Adoro/Ivoclar Vivadent) (n = 10): G1-bond and resin cement, both at room temperature (22°C), G2-bond preheated to 58°C and cement at room temperature (22°C), G3-bond at room temperature (22°C) and the cement preheated to 58°C, G4-bond preheated to 58°C and cement preheated to 58°C. Sticks of dentin/block set measuring approximately 1 mm2 were obtained and used for the microtensile bond strength test. All sticks had their failure mode classified. Statistical analysis used: Factorial analysis of variance was applied, 2 × 2 (bond × cement) (P < 0.05). Results: Preheating the bonding agent (P = 0.8411) or the cement (P = 0.7155), yielded no significant difference. The interaction bond × cement was not significant (P = 0.9389). Conclusions: Preheating the bond and/or the light-activated resin cement did not influence dentin bond strength or fracture failure mode. PMID:24347889

Combined effect of smear layer characteristics and hydrostatic pulpal pressure on dentine bond strength of HEMA-free and HEMA-containing adhesives.

PubMed

Mahdan, Mohd Haidil Akmal; Nakajima, Masatoshi; Foxton, Richard M; Tagami, Junji

2013-10-01

This study evaluated the combined effect of smear layer characteristics with hydrostatic pulpal pressure (PP) on bond strength and nanoleakage expression of HEMA-free and -containing self-etch adhesives. Flat dentine surfaces were obtained from extracted human molars. Smear layers were created by grinding with #180- or #600-SiC paper. Three HEMA-free adhesives (Xeno V, G Bond Plus, Beautibond Multi) and two HEMA-containing adhesives (Bond Force, Tri-S Bond) were applied to the dentine surfaces under hydrostatic PP or none. Dentine bond strengths were determined using the microtensile bond test (μTBS). Data were statistically analyzed using three- and two-way ANOVA with Tukey post hoc comparison test. Nanoleakage evaluation was carried out under a scanning electron microscope (SEM). Coarse smear layer preparation and hydrostatic PP negatively affected the μTBS of HEMA-free and -containing adhesives, but there were no significant differences. The combined experimental condition significantly reduced μTBS of the HEMA-free adhesives, while the HEMA-containing adhesives exhibited no significant differences. Two-way ANOVA indicated that for HEMA-free adhesives, there were significant interactions in μTBS between smear layer characteristics and pulpal pressure, while for HEMA-containing adhesives, there were no significant interactions between them. Nanoleakage formation within the adhesive layers of both adhesive systems distinctly increased in the combined experimental group. The combined effect of coarse smear layer preparation with hydrostatic PP significantly reduced the μTBS of HEMA-free adhesives, while in HEMA-containing adhesives, these effects were not obvious. Smear layer characteristics and hydrostatic PP would additively compromise dentine bonding of self-etch adhesives, especially HEMA-free adhesives. Copyright © 2013 Elsevier Ltd. All rights reserved.

Assessment of post-contamination treatments affecting different bonding stages to dentin

PubMed Central

Elkassas, Dina; Arafa, Abla

2016-01-01

Objectives: To assess the effect of cleansing treatments following saliva and blood contamination at different bonding stages to dentin. Materials and Methods: Labial surfaces of 168 permanent maxillary central incisors were ground flat exposing superficial dentin. Specimens were divided into: uncontaminated control (A), contamination after etching (B), contamination after adhesive application (C), contamination after adhesive polymerization (D). Groups were further subdivided according to cleansing treatments into: rinsing (B1, C1, D1), re-etching (B2, D3), sodium hypochlorite application (B3), ethyl alcohol application (C2), acetone application (C3), rinsing and rebonding (D2), re-etching and rebonding (D4). Composite microcylinders were bonded to treated substrates and shear loaded micro-shear bond strength (μSBS) until failure and treated surfaces were examined with scanning electron microscope. Debonded surfaces were classified as adhesive, cohesive or mixed failure. The data were analyzed using one-way ANOVA and Tukey's post hoc test. Results: The μSBS values were ranked as follow; Group B: A > B3 > B2 > B1 > B, Group C: A > C3 > C2 > C1 > C, Group D: A > D4 > D1 = D2 ≥ D3. Debonded surfaces showed adhesive failure in Group B while cohesive failure in Groups C and D. Conclusions: Cleansing treatments differ according to bonding step; re-etching then rebonding suggested if etched substrate or polymerized adhesive were contaminated while acetone application decontaminated affected unpolymerized adhesive. PMID:27403048

Bond performance of "Touch and Cure" adhesives on resin core systems.

PubMed

Kadowaki, Yoshitaka; Kakuda, Shinichi; Kawano, Shimpei; Katsumata, Aiichiro; Ting, Shihchun; Hoshika, Shuhei; Ikeda, Takatsumi; Tanaka, Toru; Carvalho, Ricardo Marinsde; Sano, Hidehiko

2016-01-01

The purpose of this study was to compare the micro-tensile bond strength (µTBS) of three resin core composites to dentin and to examine the bonded interface of the composites. One experimental TDK-03(TD) and, two commercial, DC core Automix One (DC) and Unifil core EM(UN) were used. Flat dentin surfaces of human molars were exposed using #600 SiC paper and bonded with the respective adhesive of each system. After bonding, the composites were built up on the surfaces and cured under two conditions: "light condition" or "dark condition". µTBSs (MPa) in the light condition were: TD; 60.02±17.08, DC; 38.21±13.70, and UN; 29.50±9.71; in the dark condition: TD; 54.62±17.11, DC; 8.40±4.81, and UN; 9.47±6.56. Dark curing negatively affected the bond strength of the two commercial resin-core materials. The experimental material was not affected by the curing conditions.

Effect of 2% Chlorhexidine Digluconate on the Bond Strength to Normal versus Caries-Affected Dentin

PubMed Central

Komori, Paula C. P.; Pashley, David H.; Tjäderhane, Leo; Breschi, Lorenzo; Mazzoni, Annalisa; de Goes, Mario Fernando; Wang, Linda; Carrilho, Marcela R.

2013-01-01

SUMMARY This study evaluated the effect of 2% chlorhexidine digluconate (CHX) used as a therapeutic primer on the long-term bond strengths of two etch-and-rinse adhesives to normal (ND) and caries-affected (CAD) dentin. Forty extracted human molars with coronal carious lesions, surrounded by normal dentin, were selected for this study. Flat surfaces of two types of dentin (i.e. ND and CAD) were prepared with a water-cooled high speed diamond disc, and then acid-etched, rinsed and air-dried. In control groups, dentin was re-hydrated with distilled water, blot-dried and bonded with a three-step (Scotchbond Multi-Purpose-MP) or a two-step (Single Bond 2-SB) etch-and-rinse adhesive. In experimental groups, dentin was re-hydrated with 2% CHX (60 s), blot-dried and bonded with the same adhesives. Resin composite build-ups were made. Specimens were prepared for microtensile bond testing in accordance with the non-trimming technique and then tested either immediately or after 6-month storage in artificial saliva. Data were analyzed by ANOVA/Bonferroni tests (α = 0.05). CHX did not affect the immediate bond strength to ND or CAD (p>0.05). CHX treatment significantly lowered the loss of bond strength after 6 months seen in control bonds for ND (p<0.05), but it did not alter the bond strength of CAD (p>0.05). Application of MP on CHX-treated ND or CAD produced bonds that did not change over 6 months of storage. PMID:19363971

Effect of 2% chlorhexidine digluconate on the bond strength to normal versus caries-affected dentin.

PubMed

Komori, Paula C P; Pashley, David H; Tjäderhane, Leo; Breschi, Lorenzo; Mazzoni, Annalisa; de Goes, Mario Fernando; Wang, Linda; Carrilho, Marcela R

2009-01-01

This study evaluated the effect of 2% chlorhexidine digluconate (CHX) used as a therapeutic primer on the long-term bond strengths of two etch-and-rinse adhesives to normal (ND) and caries-affected (CAD) dentin. Forty extracted human molars with coronal carious lesions, surrounded by normal dentin, were selected for this study. The flat surfaces of two types of dentin (ND and CAD) were prepared with a water-cooled high-speed diamond disc, then acid-etched, rinsed and air-dried. In the control groups, the dentin was re-hydrated with distilled water, blot-dried and bonded with a three-step (Scotchbond Multi-Purpose-MP) or two-step (Single Bond 2-SB) etch-and-rinse adhesive. In the experimental groups, the dentin was rehydrated with 2% CHX (60 seconds), blot-dried and bonded with the same adhesives. Resin composite build-ups were made. The specimens were prepared for microtensile bond testing in accordance with the non-trimming technique, then tested either immediately or after six-months storage in artificial saliva. The data were analyzed by ANOVA/Bonferroni tests (alpha = 0.05). CHX did not affect the immediate bond strength to ND or CAD (p > 0.05). CHX treatment significantly lowered the loss of bond strength after six months as seen in the control bonds for ND (p < 0.05), but it did not alter the bond strength of CAD (p > 0.05). The application of MP on CHX-treated ND or CAD produced bonds that did not change over six months of storage.

The impact of artificially caries-affected dentin on bond strength of multi-mode adhesives

PubMed Central

Follak, Andressa Cargnelutti; Miotti, Leonardo Lamberti; Lenzi, Tathiane Larissa; Rocha, Rachel de Oliveira; Maxnuck Soares, Fabio Zovico

2018-01-01

Aim: The aim of this study is to evaluate the impact of dentin condition on bond strength of multi-mode adhesive systems (MMAS) to sound and artificially induced caries-affected dentin (CAD). Methods: Flat dentin surfaces of 112 bovine incisors were assigned to 16 subgroups (n = 7) according to the substrate condition (sound and CAD– pH-cycling for 14 days); adhesive systems (Scotchbond Universal, All-Bond Universal, Prime and Bond Elect, Adper Single Bond Plus and Clearfil SE Bond) and etching strategy (etch-and-rinse and self-etch). All systems were applied according to the manufacturer's instructions, and resin composite restorations were built. After 24 h of water storage, specimens were sectioned (0.8 mm2) and submitted to the microtensile test. Statistical Analysis: Data (MPa) were analyzed using three-way analysis of variance and Tukey's test (α = 0.05). Results: MMAS presented similar bond strength values, regardless etching strategy in each substrate condition. Bond strength values were lower when MMAS were applied to CAD in the etch-and-rinse strategy. Conclusion: The etching strategy did not influence the bond strength of MMAS to sound or CAD, considering each substrate separately. However, CAD impact negatively on bond strength of MMAS in etch-and rinse mode. PMID:29674813

Effect of air-blowing duration on the bond strength of current one-step adhesives to dentin.

PubMed

Fu, Jiale; Saikaew, Pipop; Kawano, Shimpei; Carvalho, Ricardo M; Hannig, Matthias; Sano, Hidehiko; Selimovic, Denis

2017-08-01

To evaluate the influence of different air-blowing durations on the micro-tensile bond strength (μTBS) of five current one-step adhesive systems to dentin. One hundred and five caries-free human molars and five current one-step adhesive systems were used: ABU (All Bond Universal, Bisco, Inc.), CUB (CLEARFIL™ Universal Bond, Kuraray), GPB (G-Premio BOND, GC), OBA (OptiBond All-in-one, Kerr) and SBU (Scotchbond Universal, 3M ESPE). The adhesives were applied to 600 SiC paper-flat dentin surfaces according to each manufacturer's instructions and were air-dried with standard, oil-free air pressure of 0.25MPa for either 0s, 5s, 15s or 30s before light-curing. Bond strength to dentin was determined by using μTBS test after 24h of water storage. The fracture pattern on the dentin surface was analyzed by SEM. The resin-dentin interface of untested specimens was visualized by panoramic SEM image. Data from μTBS were analyzed using two-way ANOVA (adhesive vs. air-blowing time), and Games-Howell (a=0.05). Two-way ANOVA revealed a significant effect of materials (p=0.000) and air-blowing time (p=0.000) on bond strength to dentin. The interaction between factors was also significantly different (p=0.000). Maximum bond strength for each system were recorded, OBA/15s (76.34±19.15MPa), SBU/15s (75.18±12.83MPa), CUB/15s (68.23±16.36MPa), GPB/30s (55.82±12.99MPa) and ABU/15s (44.75±8.95MPa). The maximum bond strength of OBA and SUB were significantly higher than that of GPB and ABU (p<0.05). The bond strength of the current one-step adhesive systems is material-dependent (p=0.000), and was influenced by air-blowing duration (p=0.000). For the current one-step adhesive systems, higher bond strengths could be achieved with prolonged air-blowing duration between 15-30s. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Dentin surface treatment using a non-thermal argon plasma brush for interfacial bonding improvement in composite restoration

PubMed Central

Ritts, Andy Charles; Li, Hao; Yu, Qingsong; Xu, Changqi; Yao, Xiaomei; Hong, Liang; Wang, Yong

2010-01-01

The objective of this study is to investigate the treatment effects of non-thermal atmospheric gas plasmas on dentin surfaces for composite restoration. Extracted unerupted human third molars were used by removing the crowns and etching the exposed dentin surfaces with 35% phosphoric acid gel. The dentin surfaces were treated by using a non-thermal atmospheric argon plasma brush for various durations. The molecular changes of the dentin surfaces were analyzed using FTIR/ATR and an increase in carbonyl groups on dentin surfaces was detected with plasma treated dentin. Adper Single Bond Plus adhesive and Filtek Z250 dental composite were applied as directed. To evaluate the dentin/composite interfacial bonding, the teeth thus prepared were sectioned into micro-bars as the specimens for tensile test. Student Newman Keuls tests showed that the bonding strength of the composite restoration to peripheral dentin was significantly increased (by 64%) after 30 s plasma treatment. However, the bonding strength to plasma treated inner dentin did not show any improvement. It was found that plasma treatment of peripheral dentin surface up to 100 s gave an increase in interfacial bonding strength, while a prolong plasma treatment of dentin surfaces, e.g., 5 min treatments, showed a decrease in interfacial bonding strength. PMID:20831586

Influence of laboratory degradation methods and bonding application parameters on microTBS of self-etch adhesives to dentin.

PubMed

Erhardt, Maria Carolina G; Pisani-Proença, Jatyr; Osorio, Estrella; Aguilera, Fátima S; Toledano, Manuel; Osorio, Raquel

2011-04-01

To evaluate the laboratory resistance to degradation and the use of different bonding treatments on resin-dentin bonds formed with three self-etching adhesive systems. Flat, mid-coronal dentin surfaces from extracted human molars were bonded according to manufacturer's directions and submitted to two challenging regimens: (A) chemical degradation with 10% NaOC1 immersion for 5 hours; and (B) fatigue loading at 90 N using 50,000 cycles at 3.0 Hz. Additional dentin surfaces were bonded following four different bonding application protocols: (1) according to manufacturer's directions; (2) acid-etched with 36% phosphoric acid (H3PO4) for 15 seconds; (3) 10% sodium hypochlorite (NaOClaq) treated for 2 minutes, after H3PO4-etching; and (4) doubling the application time of the adhesives. Two one-step self-etch adhesives (an acetone-based: Futurabond/FUT and an ethanol-based: Futurabond NR/FNR) and a two-step self-etch primer system (Clearfil SE Bond/CSE) were examined. Specimens were sectioned into beams and tested for microtensile bond strength (microTBS). Selected debonded specimens were observed under scanning electron microscopy (SEM). Data (MPa) were analyzed by ANOVA and multiple comparisons tests (alpha= 0.05). microTBS significantly decreased after chemical and mechanical challenges (P< 0.05). CSE showed higher microTBS than the other adhesive systems, regardless the bonding protocol. FUT attained the highest microTBS after doubling the application time. H3PO4 and H3PO4 + NaOCl pretreatments significantly decreased bonding efficacy of the adhesives.

Can 1% chlorhexidine diacetate and ethanol stabilize resin-dentin bonds?

PubMed Central

Manso, Adriana Pigozzo; Grande, Rosa Helena Miranda; Bedran-Russo, Ana Karina; Reis, Alessandra; Loguercio, Alessandro D.; Pashley, David Henry; Carvalho, Ricardo Marins

2014-01-01

Objectives To examine the effects of the combined use of chlorhexidine and ethanol on the durability of resin-dentin bonds. Methods Forty-eight flat dentin surfaces were etched (32% phosphoric acid), rinsed (15 s) and kept wet until bonding procedures. Dentin surfaces were blot-dried with absorbent paper and re-wetted with water (Water, control), 1% chlorhexidine diacetate in water (CHD/Water), 100% ethanol (Ethanol), or 1% chlorhexidine diacetate in ethanol (CHD/Ethanol) solutions for 30 s. They were then bonded with All Bond 3 (AB3, Bisco) or Excite (EX, Ivoclar-Vivadent) using a smooth, continuous rubbing application (10 s), followed by 15 s gentle air stream to evaporate solvents. The adhesives were light-cured (20 s) and resin composite build-ups constructed for the microtensile method. Bonded beams were obtained and tested after 24-hours, 6-months and 15-months of water storage at 37°C. Storage water was changed every month. Effects of treatment and testing periods were analyzed (ANOVA, Holm-Sidak, p<0.05) for each adhesive. Results There were no interactions between factors for both etch-and-rinse adhesives. AB3 was significantly affected only by storage (p = 0.003). Excite was significantly affected only by treatments (p = 0.048). AB3 treated either with ethanol or CHD/ethanol resulted in reduced bond strengths after 15 months. The use of CHD/ethanol resulted in higher bond strengths values for Excite. Conclusions Combined use of ethanol/1% chlorhexidine diacetate did not stabilize bond strengths after 15 months. PMID:24815823

Effect of intrinsic wetness and regional difference on dentin bond strength.

PubMed

Pereira, P N; Okuda, M; Sano, H; Yoshikawa, T; Burrow, M F; Tagami, J

1999-01-01

The aim of this investigation was to determine the influence of intrinsic wetness on regional bond strengths of adhesive resins to dentin. Human caries-free third molars were randomly divided into three groups for bonding: Group 1--no pulpal pressure; Group 2--pulpal pressure of 15 cm H2O; and Group 3--dentin dried overnight in a desiccator. Clearfil Liner Bond II (Kuraray) or One Step (Bisco) adhesive resins systems were applied to the flat dentin surfaces and the teeth were restored with APX resin composite (Kuraray). After 24 h in water at 37 degrees C, the specimens were sectioned into 0.7 mm thick slabs and divided into three regional subgroups according to the remaining dentin thickness and visual criteria: pulp horn, center, and periphery. The slabs were then trimmed for the micro-tensile bond test and subjected to a tensile force and crosshead of 1 mm/min. The data were analyzed with ANOVA and Fisher's PLSD test at a confidence level of 95%. The fracture modes were determined under a scanning electron microscope (JXA-840, JEOL, Japan). No significant regional difference was observed for the Group 1 and 2 specimens restored with Clearfil Liner Bond II (p > 0.05). However, bond strengths significantly decreased at the pulp horn region of the Group 1 and 2 specimens restored with One Step (p > 0.01). All bond strengths of Group 3 decreased significantly and regional differences were not evident (p > 0.05). The dentin adhesive system should be chosen according to the substrate and region to be bonded, since bond strengths can vary according to the intrinsic wetness, region, and the adhesive system.

In vivo remineralization of dentin using an agarose hydrogel biomimetic mineralization system

NASA Astrophysics Data System (ADS)

Han, Min; Li, Quan-Li; Cao, Ying; Fang, Hui; Xia, Rong; Zhang, Zhi-Hong

2017-02-01

A novel agarose hydrogel biomimetic mineralization system loaded with calcium and phosphate was used to remineralize dentin and induce the oriented densely parallel packed HA layer on defective dentin surface in vivo in a rabbit model. Firstly, the enamel of the labial surface of rabbits’ incisor was removed and the dentin was exposed to oral environment. Secondly, the hydrogel biomimetic mineralization system was applied to the exposed dentin surface by using a custom tray. Finally, the teeth were extracted and evaluated by scanning electron microscopy, X-ray diffraction, and nanoindentation test after a certain time of mineralization intervals. The regenerated tissue on the dentin surface was composed of highly organised HA crystals. Densely packed along the c axis, these newly precipitated HA crystals were perpendicular to the underlying dental surface with a tight bond. The demineralized dentin was remineralized and dentinal tubules were occluded by the grown HA crystals. The nanohardness and elastic modulus of the regenerated tissue were similar to natural dentin. The results indicated a potential clinical use for repairing dentin-exposed related diseases, such as erosion, wear, and dentin hypersensitivity.

Effect of dimethyl sulfoxide on dentin collagen.

PubMed

Mehtälä, P; Pashley, D H; Tjäderhane, L

2017-08-01

Infiltration of adhesive on dentin matrix depends on interaction of surface and adhesive. Interaction depends on dentin wettability, which can be enhanced either by increasing dentin surface energy or lowering the surface energy of adhesive. The objective was to examine the effect of dimethyl sulfoxide (DMSO) on demineralized dentin wettability and dentin organic matrix expansion. Acid-etched human dentin was used for sessile drop contact angle measurement to test surface wetting on 1-5% DMSO-treated demineralized dentin surface, and linear variable differential transformer (LVDT) to measure expansion/shrinkage of dentinal matrix. DMSO-water binary liquids were examined for surface tension changes through concentrations from 0 to 100% DMSO. Kruskal-Wallis and Mann-Whitney tests were used to test the differences in dentin wettability, expansion and shrinkage, and Spearman test to test the correlation between DMSO concentration and water surface tension. The level of significance was p<0.05. Pretreatment with 1-5% DMSO caused statistically significant concentration-dependent increase in wetting: the immediate contact angles decreased by 11.8% and 46.6% and 60s contact angles by 9.5% and 47.4% with 1% and 5% DMSO, respectively. DMSO-water mixtures concentration-dependently expanded demineralized dentin samples less than pure water, except with high (≥80%) DMSO concentrations which expanded demineralized dentin more than water. Drying times of LVDT samples increased significantly with the use of DMSO. Increased dentin wettability may explain the previously demonstrated increase in adhesive penetration with DMSO-treated dentin, and together with the expansion of collagen matrix after drying may also explain previously observed increase in dentin adhesive bonding. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Relationship between thin-film bond strength as measured by a scratch test, and indentation hardness for bonding agents.

PubMed

Kusakabe, Shusuke; Rawls, H Ralph; Hotta, Masato

2016-03-01

To evaluate thin-film bond strength between a bonding agent and human dentin, using a scratch test, and the characteristics and accuracy of measurement. One-step bonding agents (BeautiBond; Bond Force; Adper Easy Bond; Clearfil tri-S Bond) and two-step bonding agents (Cleafil SE Bond; FL-Bond II) were investigated in this study. Flat dentin surfaces were prepared for extracted human molars. The dentin surfaces were ground and bonding agents were applied and light cured. The thin-film bond strength test of the specimens was evaluated by the critical load at which the coated bonding agent failed and dentin appeared. The scratch mark sections were then observed under a scanning electron microscope. Indentation hardness was evaluated by the variation in depth under an applied load of 10gf. Data were compared by one-way ANOVA with the Scheffé's post hoc multiple comparison test (p<0.05). In addition, thin-film bond strength and indentation hardness were analyzed using analysis of correlation and covariance. The thin-film bond strength of two-step bonding agents were found to be significantly higher than that of one-step bonding agents with small standard deviations. Scratch marks consistently showed adhesive failure in the vicinity of the bonding agent/dentin interface. The indentation hardness showed a trend that two-step bonding agents have greater hardness than one-step bonding agents. A moderately significant correlation (r(2)=0.31) was found between thin-film bond strength and indentation hardness. Thin-film bond strength test is a valid and reliable means of evaluating bond strength in the vicinity of the adhesive interface and is more accurate than other methods currently in use. Further, the thin-film bond strength is influenced by the hardness of the cued bonding agent. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of Phosphoric Acid Pre-etching on Fatigue Limits of Self-etching Adhesives.

PubMed

Takamizawa, T; Barkmeier, W W; Tsujimoto, A; Scheidel, D D; Erickson, R L; Latta, M A; Miyazaki, M

2015-01-01

The purpose of this study was to use shear bond strength (SBS) and shear fatigue limit (SFL) testing to determine the effect of phosphoric acid pre-etching of enamel and dentin prior to application of self-etch adhesives for bonding resin composite to these substrates. Three self-etch adhesives--1) G- ænial Bond (GC Corporation, Tokyo, Japan); 2) OptiBond XTR (Kerr Corp, Orange, CA, USA); and 3) Scotchbond Universal (3M ESPE Dental Products, St Paul, MN, USA)--were used to bond Z100 Restorative resin composite to enamel and dentin surfaces. A stainless-steel metal ring with an inner diameter of 2.4 mm was used to bond the resin composite to flat-ground (4000 grit) tooth surfaces for determination of both SBS and SFL. Fifteen specimens each were used to determine initial SBS to human enamel/dentin, with and without pre-etching with a 35% phosphoric acid (Ultra-Etch, Ultradent Products Inc, South Jordan, UT, USA) for 15 seconds prior to the application of the adhesives. A staircase method of fatigue testing (25 specimens for each test) was then used to determine the SFL of resin composite bonded to enamel/dentin using a frequency of 10 Hz for 50,000 cycles or until failure occurred. A two-way analysis of variance and Tukey post hoc test were used for analysis of SBS data, and a modified t-test with Bonferroni correction was used for the SFL data. Scanning electron microscopy was used to examine the area of the bonded restorative/tooth interface. For all three adhesive systems, phosphoric acid pre-etching of enamel demonstrated significantly higher (p<0.05) SBS and SFL with pre-etching than it did without pre-etching. The SBS and SFL of dentin bonds decreased with phosphoric acid pre-etching. The SBS and SFL of bonds using phosphoric acid prior to application of self-etching adhesives clearly demonstrated different tendencies between enamel and dentin. The effect of using phosphoric acid, prior to the application of the self-etching adhesives, on SBS and SFL was dependent on the adhesive material and tooth substrate and should be carefully considered in clinical situations.

Evaluation Of The Shear Bond Strength Between Dentin And Dental Luting Cement Following Dentin Surface Treatment By 980 Nm Diode Laser And Desensitizing Agent

NASA Astrophysics Data System (ADS)

Ibrahim, T.; Gheith, M.

2011-09-01

Dentin hypersensitivity is described clinically as an exaggerated response to non-noxious sensory stimuli. Current treatment is concentrating on two approaches; to occlude the dentinal tubules or to block neural transmission. This is achieved through using dentin desensitizers and low power lasers. Forty eight freshly extracted human molar teeth were used in this study and divided equally into three groups. Group 1) control group, group 2) laser treated dentin surface group, and group 3) desensitizing agent dentin surface group. Scanning electron microscopic analysis of laser treated group showed melted globules, no carbonization, recrystalization and crystal growth of the apatite in some areas. In diode laser dentin surface treated group showed the highest shear bond strength mean value.

Influence of dimethyl sulfoxide used as a solvent on the physical properties and long-term dentin bonding of hydrophilic resins.

PubMed

Stape, Thiago Henrique Scarabello; Tezvergil-Mutluay, Arzu; Mutluay, Mustafa Murat; Martins, Luís Roberto Marcondes; do Prado, Rosana Leal; Pizi, Eliane Cristina Gava; Tjäderhane, Leo

2016-12-01

To examine the feasibility of dimethyl sulfoxide (DMSO) incorporation into relatively hydrophilic resins as a new potential method to improve the durability of resin-dentin bonds. Six experimental light-curing BisGMA/HEMA resins solvated in ethanol and DMSO with increasing concentrations of DMSO (0, 0.5, 1, 2, 4 and 10wt%) were prepared. The degree of conversion (DC) was evaluated by Fourier Transform Infrared Spectroscopy (n=8); water sorption (Wsp) and water solubility (Wso) were gravimetrically assessed (n=10); and flexural strength (FS) and elastic modulus (E) were determined by a three-point bending flexural test (n=10). Flat dentin surfaces on sound third molars (n=10/group) were bonded with resins containing 0, 2, 4 and 10wt% DMSO used as a two-step etch-and-rinse system. Dentin microtensile bond strength was determined at 24h and after two-year aging in artificial saliva at 37°C. DMSO significantly affected Wsp (p=0.0006), DC, Wso, FS, and E (p<0.0001). In general, the resins' mechanical/physical properties were not affected by 2% or lower DMSO incorporation. Incorporation of 4% or higher DMSO content significantly increased DC, Wsp and Wso, but 2% or higher DMSO concentrations significantly reduced FS and E. No influence on immediate dentin bond strength occurred up to 4% DMSO incorporation. While 4% or higher DMSO concentrations impaired bond strength over time, the resin containing 2% DMSO presented significant higher dentin bond strength compared to the control resin after two year-aging. The use of DMSO as a new solvent in adhesive dentistry improves dentin bonding of relatively hydrophilic resins over time. 2% DMSO incorporation in BisGMA/HEMA resins should be sufficient to reduce bond strength loss without compromising polymer mechanical strength and physical properties. Copyright © 2016 Elsevier Ltd. All rights reserved.

Five-year Effects of Chlorhexidine on the In Vitro Durability of Resin/Dentin Interfaces.

PubMed

Loguercio, Alessandro D; Hass, Viviane; Gutierrez, Mario Felipe; Luque-Martinez, Issis Virginia; Szezs, Anna; Stanislawczuk, Rodrigo; Bandeca, Matheus Coelho; Reis, Alessandra

2016-01-01

To evaluate the effect of an acid containing 2% chlorhexidine (Ac/CHX) or a 2% CHX aqueous solution (Aq/CHX) on the immediate and 5-year bonding properties of resin/dentin interfaces produced by two adhesives. The presence of CHX in these interfaces was also evaluated under micro-Raman spectroscopy. Forty-two molars were ground to expose a flat dentin surface. In the control group, the surfaces were etched with conventional phosphoric acid, and Prime&Bond NT (PB) and Adper Single Bond 2 (SB) were applied. In Ac/CHX, an acid containing 2% CHX was applied after adhesive application. In the Aq/CHX group, an aqueous solution of 2% CHX was applied for 60 s after etching. After placing the restoration, specimens were prepared and tested using the microtensile bond strength test (μTBS, 0.5 mm/min) immediately or after 5 years. For nanoleakage (NL), specimens at each period were immersed in silver nitrate solution and examined by EDX-SEM. In addition, specimens at each period underwent examination for CHX using micro-Raman spectroscopy. Data were submitted to appropriate statistical analysis (a=0.05). After 5 years, NL was more pronounced in the control than in the Ac/CHX or Aq/CHX (p<0.001). Significant reductions in the μTBS were observed for all groups; however, they were more pronounced for the control (p<0.001). CHX was still present in the hybrid layers Ac/CHX or Aq/CHX groups after 5 years. The use of a 2% chlorhexidine-containing acid or the application of an aqueous CHX primer may increase the long-term stability of resin/dentin interfaces.

Tannic acid for smear layer removal: pilot study with scanning electron microscope.

PubMed

Bitter, N C

1989-04-01

The effects of a 25% tannic acid solution applied to the surface of prepared dentin was compared with untreated prepared dentin surfaces. The following results were demonstrated by electron microscope observation: (1) cavity preparations created an amorphous dentinal smear layer, (2) placement of a 25% tannic acid solution for 15 seconds removed the smear layer, (3) the contents of the dentinal tubules were not removed and no enlargement of dentinal tubules was found, and (3) a clean dentinal surface was observed.

Variations in collagen fibrils network structure and surface dehydration of acid demineralized intertubular dentin: effect of dentin depth and air-exposure time.

PubMed

Fawzy, Amr S

2010-01-01

The aim was to characterize the variations in the structure and surface dehydration of acid demineralized intertubular dentin collagen network with the variations in dentin depth and time of air-exposure (3, 6, 9 and 12 min). In addition, to study the effect of these variations on the tensile bond strength (TBS) to dentin. Phosphoric acid demineralized superficial and deep dentin specimens were prepared. The structure of the dentin collagen network was characterized by AFM. The surface dehydration was characterized by probing the nano-scale adhesion force (F(ad)) between AFM tip and intertubular dentin surface as a new experimental approach. The TBS to dentin was evaluated using an alcohol-based dentin self-priming adhesive. AFM images revealed a demineralized open collagen network structure in both of superficial and deep dentin at 3 and 6 min of air-exposure. However, at 9 min, superficial dentin showed more collapsed network structure compared to deep dentin that partially preserved the open network structure. Total collapsed structure was found at 12 min for both of superficial and deep dentin. The value of the F(ad) is decreased with increasing the time of air-exposure and is increased with dentin depth at the same time of air-exposure. The TBS was higher for superficial dentin at 3 and 6 min, however, no difference was found at 9 and 12 min. The ability of the demineralized dentin collagen network to resist air-dehydration and to preserve the integrity of open network structure with the increase in air-exposure time is increased with dentin depth. Although superficial dentin achieves higher bond strength values, the difference in the bond strength is decreased by increasing the time of air-exposure. The AFM probed F(ad) showed to be sensitive approach to characterize surface dehydration, however, further researches are recommended regarding the validity of such approach.

Influence of Er:YAG and Ti:sapphire laser irradiation on the microtensile bond strength of several adhesives to dentin.

PubMed

Portillo, M; Lorenzo, M C; Moreno, P; García, A; Montero, J; Ceballos, L; Fuentes, M V; Albaladejo, A

2015-02-01

The aim of the present study was to evaluate the influence of erbium:yttrium-aluminum-garnet (Er:YAG) and Ti:sapphire laser irradiation on the microtensile bond strength (MTBS) of three different adhesive systems to dentin. Flat dentin surfaces from 27 molars were divided into three groups according to laser irradiation: control, Er:YAG (2,940 nm, 100 μs, 2.7 W, 9 Hz) and Ti:sapphire laser (795 nm, 120 fs, 1 W, 1 kHz). Each group was divided into three subgroups according to the adhesive system used: two-step total-etching adhesive (Adper Scotchbond 1 XT, from now on XT), two-step self-etching adhesive (Clearfil SE Bond, from now on CSE), and all-in-one self-etching adhesive (Optibond All-in-One, from now on OAO). After 24 h of water storage, beams of section at 1 mm(2) were longitudinally cut from the samples. Each beam underwent traction test in an Instron machine. Fifteen polished dentin specimens were used for the surface morphology analysis by scanning electron microscopy (SEM). Failure modes of representative debonded microbars were SEM-assessed. Data were analyzed by ANOVA, chi-square test, and multiple linear regression (p < 0.05). In the control group, XT obtained higher MTBS than that of laser groups that performed equally. CSE showed higher MTBS without laser than that with laser groups, where Er:YAG attained higher MTBS than ultrashort laser. When OAO was used, MTBS values were equal in the three treatments. CSE obtained the highest MTBS regardless of the surface treatment applied. The Er:YAG and ultrashort laser irradiation reduce the bonding effectiveness when a two-step total-etching adhesive or a two-step self-etching adhesive are used and do not affect their effectiveness when an all-in-one self-etching adhesive is applied.

The effect of Er:YAG laser irradiation on the bond stability of self-etch adhesives at different dentin depths.

PubMed

Karadas, Muhammet; Çağlar, İpek

2017-07-01

The aim of this study was to evaluate the effect of Er:YAG laser irradiation on the micro-shear bond strength of self-etch adhesives to the superficial dentin and the deep dentin before and after thermocycling. Superficial dentin and deep dentin surfaces were prepared by flattening of the occlusal surfaces of extracted human third molars. The deep or superficial dentin specimens were randomized into three groups according to the following surface treatments: group I (control group), group II (Er:YAG laser; 1.2 W), and group III (Er:YAG laser; 0.5 W). Clearfil SE Bond or Clearfil S 3 Bond was applied to each group's dentin surfaces. After construction of the composite blocks on the dentin surface, the micro-shear bond testing of each adhesive was performed at 24 h or after 15,000 thermal cycles. The data were analyzed using a univariate analysis of variance and Tukey's test (p < 0.05). Laser irradiation in superficial dentin did not significantly affect bond strength after thermocycling (p > 0.05). However, deep-dentin specimens irradiated with laser showed significantly higher bond strengths than did control specimens after thermocycling (p < 0.05). Thermocycling led to significant deterioration in the bond strengths of all deep-dentin groups. The stable bond strength after thermocycling was measured for all of the superficial-dentin groups. No significant difference was found between the 0.5 and 1.2 W output power settings. In conclusion, the effect of laser irradiation on the bond strength of self-etch adhesives may be altered by the dentin depth. Regardless of the applied surface treatment, deep dentin showed significant bond degradation.

The effects of dentin and intaglio indirect ceramic optimized polymer restoration surface treatment on the shear bond strength of resin cement

NASA Astrophysics Data System (ADS)

Puspitarini, A.; Suprastiwi, E.; Usman, M.

2017-08-01

Ceramic optimized polymer (ceromer) bonds to the tooth substrate through resin cements. The bond strength between dentin, resin cement, and ceromer depends on the applied surface treatment. To analyze the effects of dentin and intaglio ceromer surface treatment on the shear bond strength self-adhesive resin cement. Forty-five dentin premolar and ceromer specimens were bonded with resin cement and divided into three groups as follows: in group 1, no treatment was applied; in group 2, dentin surface treatment was carried out with acid etching and a bonding agent; and in group 3, dentin surface treatment was carried out with acid etching, a bonding agent, and intaglio ceromer surface treatment with etching and silane. All specimens were incubated at 37 °C for 24 hours, and the shear bond strength was measured using a universal testing machine. Group 3 showed the highest shear bond strength, followed by group 2. The surface treatment of dentin and intaglio ceromer showed significantly improved shear bond strength in the group comparison. Dentin and intaglio ceromer surface treatment can improved the shear bond strength self-adhesive resin cement.

ADHESIVES WITH DIFFERENT PHS: EFFECT ON THE MTBS OF CHEMICALLY ACTIVATED AND LIGHT-ACTIVATED COMPOSITES TO HUMAN DENTIN

PubMed Central

Mallmann, André; de Melo, Renata Marques; Estrela, Verbênia; Pelogia, Fernanda; Campos, Laura; Bottino, Marco Antonio; Valandro, Luiz Felipe

2007-01-01

Purpose: To evaluate the bond strength between human dentin and composites, using two light-activated single-bottle total-etch adhesive systems with different pHs combined with chemically activated and light-activated-composites. The tested hypothesis was that the dentin bond strength is not influenced by an adhesive system of low pH, combined with chemically activated or light-activated composites. Material and Method: Flat dentin surfaces of twenty-eight human third molars were allocated in 4 groups (n=7), depending on the adhesive system: (One Step Plus-OS and Prime & Bond NT-PB) and composite (light-activated Filtek Z-100 [Z100] and chemically activated Bisfil 2B [B2B]). Each adhesive system was applied on acid-etched dentin and then one of the composites was added to form a 5 mm-high resin block. The specimens were stored in tap water (37°C/24 h) and sectioned into two axes, x and y. This was done with a diamond disk under coolant irrigation to obtain beams with a cross-section area of approximately 0.8 mm2. Each specimen was then attached to a custom-made device and submitted to the microtensile test (1 mm.min−1). Data were analyzed using two-way ANOVA and Tukey’s tests (p<0.05). Results: The anticipated hypothesis was not confirmed (p<0.0001). The bond strengths (MPa) were not statistically different between the two adhesive systems when light-activated composite was used (OS+Z100 = 24.7±7.1ª; PB+Z100 = 23.8±5.7ª). However, with use of the chemically activated composite (B2B), PB (7.8±3.6b MPa) showed significantly lower dentin bond strengths than OS (32.2±7.6ª). Conclusion: The low pH of the adhesive system can affect the bond of chemically activated composite to dentin. On the other hand, under the present conditions, the low pH did not seem to affect the bond of light-activated composites to dentin significantly. PMID:19089142

Adhesives with different pHs: effect on the MTBS of chemically activated and light-activated composites to human dentin.

PubMed

Mallmann, André; de Melo, Renata Marques; Estrela, Verbênia; Pelogia, Fernanda; Campos, Laura; Bottino, Marco Antonio; Valandro, Luiz Felipe

2007-08-01

To evaluate the bond strength between human dentin and composites, using two light-activated single-bottle total-etch adhesive systems with different pHs combined with chemically activated and light-activated-composites. The tested hypothesis was that the dentin bond strength is not influenced by an adhesive system of low pH, combined with chemically activated or light-activated composites. Flat dentin surfaces of twenty-eight human third molars were allocated in 4 groups (n=7), depending on the adhesive system: (One Step Plus-OS and Prime & Bond NT-PB) and composite (light-activated Filtek Z-100 [Z100] and chemically activated Bisfil 2B [B2B]). Each adhesive system was applied on acid-etched dentin and then one of the composites was added to form a 5 mm-high resin block. The specimens were stored in tap water (37 degrees C/24 h) and sectioned into two axes, x and y. This was done with a diamond disk under coolant irrigation to obtain beams with a cross-section area of approximately 0.8 mm(2). Each specimen was then attached to a custom-made device and submitted to the microtensile test (1 mm*min-1). Data were analyzed using two-way ANOVA and Tukey's tests (p<0.05). The anticipated hypothesis was not confirmed (p<0.0001). The bond strengths (MPa) were not statistically different between the two adhesive systems when light-activated composite was used (OS+Z100 = 24.7+/-7.1 feminine; PB+Z100 = 23.8+/-5.7 feminine). However, with use of the chemically activated composite (B2B), PB (7.8+/-3.6b MPa) showed significantly lower dentin bond strengths than OS (32.2+/-7.6 feminine). The low pH of the adhesive system can affect the bond of chemically activated composite to dentin. On the other hand, under the present conditions, the low pH did not seem to affect the bond of light-activated composites to dentin significantly.

Influences of the cold atmospheric plasma jet treatment on the properties of the demineralized dentin surfaces

NASA Astrophysics Data System (ADS)

Xiaoming, ZHU; Heng, GUO; Jianfeng, ZHOU; Xiaofei, ZHANG; Jian, CHEN; Jing, LI; Heping, LI; Jianguo, TAN

2018-04-01

Improvement of the bonding strength and durability between the dentin surface and the composite resin is a challenging job in dentistry. In this paper, a radio-frequency atmospheric-pressure glow discharge (RF-APGD) plasma jet is employed for the treatment of the acid-etched dentin surfaces used for the composite restoration. The properties of the plasma treated dentin surfaces and the resin-dentin interfaces are analyzed using the x-ray photoemission spectroscopy, contact angle goniometer, scanning electron microscope and microtensile tester. The experimental results show that, due to the abundant chemically reactive species existing in the RF-APGD plasma jet under a stable and low energy input operating mode, the contact angle of the plasma-treated dentin surfaces decreases to a stable level with the increase of the atomic percentage of oxygen in the specimens; the formation of the long resin tags in the scattered clusters and the hybrid layers at the resin-dentin interfaces significantly improve the bonding strength and durability. These results indicate that the RF-APGD plasma jet is an effective tool for modifying the chemical properties of the dentin surfaces, and for improving the immediate bonding strength and the durability of the resin-dentin bonding in dentistry.

[Nanoleakage at the resin-dental interface of four self-etching adhesives].

PubMed

Liao, Zhi-qing; Ouyang, Yong; Yang, Jian-zhen

2011-09-01

To evaluate the nanoleakage and ultramorphology of four self-etching adhesives. Sixteen freshly extracted, caries-free human third molars were selected. A flat dentin surface was exposed by removing occlusal enamel. All teeth were randomly divided into four groups acorrding to four different self-etch adhesive: Adper Prompt (A), iBond (B), Xeno III (C) and SE Bond (D). The dentin were bonded with dentin adhesive system according to manufacturer's directions. Composite layers were built up incrementally. The specimens were sectioned longitudinally across the resin-dentin interface into 4.0 mm×0.9 mm sticks and then traced with ammoniacal silver solution. Epoxy resin-embedded sections were prepared for transmission electron microscope (TEM) to observe nanoleakage. The images were qualitatively compared by NIH software, and data was analyzed by SPSS. Different thickness of hybrid layer and adhesives layer were observed for each adhesive. The hybrid layer of A, C was thicker than that of B, D, and adhesive layer of D was thicker than the others. The extent of nanoleakage varied among different adhesives: A (45.02 ± 9.49), B (43.97 ± 8.55), C (27.02 ± 10.86), D (12.94 ± 2.07). D presented significantly less silver deposition than any of the others did (P < 0.05). The thickness of hybrid layer and adhesive layer vary among the four adhesives. The shape and extent of nanoleakage of each adhesive are also different. Two-step system shows less nanoleakage than one-step systems do.

NaOCl degradation of a HEMA-free all-in-one adhesive bonded to enamel and dentin following two air-blowing techniques.

PubMed

De Munck, Jan; Ermis, R Banu; Koshiro, Kenichi; Inoue, Satoshi; Ikeda, Takatsumi; Sano, Hidehiko; Van Landuyt, Kirsten L; Van Meerbeek, Bart

2007-01-01

Phase-separation within HEMA-free all-in-one dental adhesives may result in the entrapment of droplets within the adhesive resin. Strongly air-blowing prior to polymerization, can remove most of these droplets. The objective of this study was to evaluate the effect these droplets may have on the resistance of the adhesive-tooth interface to NaOCl degradation. The micro-tensile bond strength (microTBS) to enamel and dentin was determined when a HEMA-free all-in-one adhesive was applied either following a mild or strong air-blowing technique. The bonds were also exposed to an aqueous sodium hypochlorite (NaOCl) solution for 1h, following a recently introduced methodology to mimic in vivo bond degradation. This study revealed that strong air-blowing of the adhesive only resulted in a significantly higher micro-tensile bond strength (microTBS) to dentin, but not to enamel. Likewise, NaOCl only reduced the microTBS to dentin for both the mild and strong air-blowing technique, but again not the microTBS to enamel. Failure analysis by SEM clearly revealed that strong air-blowing is less effective in droplet removal when the adhesive was applied in small and narrow class-I cavities, as compared to when it was applied to flat surfaces. NaOCl did preferentially dissolve the hybrid layer at dentin, and more for the mild than for the strong air-blowing technique. A strong air-blowing procedure resulted in a more NaOCl-resistant hybrid layer, so that it can be concluded that a HEMA-free one-step adhesive definitely benefits from a strong air-blowing technique.

Influence of ethanol on dentin roughness, surface free energy, and interaction between AH Plus and root dentin.

PubMed

Pantoja, Carlos Augusto de Morais Souto; Silva, Diogo Henrique da; Soares, Adriana de Jesus; Ferraz, Caio Cezar Randi; Gomes, Brenda Paula Figueiredo de Almeida; Zaia, Alexandre Augusto; Almeida, José Flávio Affonso de

2018-01-01

This study aimed to evaluate the influence of different ethanol concentrations on dentin roughness, surface free energy, and contact angle between AH Plus and the root canal dentin. One hundred human maxillary anterior teeth were split longitudinally and 200 dentin specimens were polished to make the surface flatter and smoother. An acrylic bar was positioned between two dentin specimens and impression material was added to create a block, simulating an instrumented root canal space. Specimens were removed from the mold and cleaned in an ultrasonic bath for 10 min. Thereafter, dentin specimens were divided into four groups (n = 50) according to the drying methods used: a) wet: vacuum only, b) paper points: vacuum + absorbent paper points, c) 70% alcohol: 70% alcohol (1 min) + vacuum + absorbent paper points, and d) 100% alcohol: 100% alcohol (1 min) + vacuum + absorbent paper points. A rugosimeter and a goniometer were used to verify the roughness (Ra) and to measure the surface free energy and the contact angle between the AH Plus sealer and the root canal dentin. ANOVA and Tukey tests (α = 0.05) were used for statistical analysis. The 70% and 100% ethanol groups showed significantly decreased roughness as well as increased surface free energy in the root canal dentin when compared to the wet and paper point groups. In addition, ethanol significantly reduced the contact angle between the AH Plus sealer and the root canal dentin. Ethanol solutions (70% and 100%) provide better wettability of AH Plus sealer on dentin surfaces.

The effect of propolis fluoride on caries dentine activity

NASA Astrophysics Data System (ADS)

Darwita, Risqa Rina; Soekanto, Sri Angky; Finisha, Andanali Rhukul; Wahyuni, Hardiati Nur; Andiani, Salsabila Ghina

2018-02-01

This research was conducted to analyze the effect of propolis fluoride on the occurrence of arrested caries dentine surface. The design of the study was a clinical trial experimental. The respondent were primary school students aged 6-8 years, from primary school in Kukusan, Depok, West Java, Indonesia. They were screened of dental examination and the total number of 296 children with an age range of 6-8 year old were included in the study. All students who had dentin caries were get dental treatment with propolis fluoride topical application in dentin caries surface. After one month, two months and four months all students who were got propolis fluoride topical application in dentin caries surface were controlled. All data were analyzed by Wilcoxon test. The total number of dentinal decay of 296 student was 1740 surfaces indicated to Flolis topical application. After one, two and three months of Flolis application, all arrested of dentinal decay was evaluated, the result of evaluation from the second month to the third month evaluation was found that the arrested dentinal caries surfaces were decreased significantly at 29.36% (p<0.01), while the evaluation of arrested dentinal caries surface from the first month to the third month was decreased significantly at 38.62% (p<0.001). Flolis was proven significantly to be able to arrest the activity of dental caries, and their ability to arrest dental caries was significantly different. Flolis was found to be effective in arresting dentinal caries surface until three months application, and should be repeated after 3 months of Flolis application.

Effect of etching on bonding of a self-etch adhesive to dentine affected by amelogenesis imperfecta.

PubMed

Epasinghe, Don Jeevanie; Yiu, Cynthia Kar Yung

2018-02-01

Dentine affected by amelogenesis imperfecta (AI) is histologically altered due to loss of hypoplastic enamel and becomes hypermineralized. In the present study, we examined the effect of additional acid etching on microtensile bond strength of a self-etch adhesive to AI-affected dentine. Flat coronal dentine obtained from extracted AI-affected and non-carious permanent molars were allocated to two groups: (a) Clearfil SE Bond (control); and (b) Clearfil SE Bond and additional etching with 34% phosphoric acid for 15 seconds. The bonded teeth were sectioned into .8-mm 2 beams for microtensile bond strength testing, and stressed to failure under tension. The bond strength data were analyzed using two-way analysis of variance (dentine type and etching step) and Student-Newman-Keuls multiple comparison test (P<.05). Representative fractured beams from each group were examined under scanning electron microscopy. Both factors, dentine substrate (P<.001) and etching step (P<.05), and their interactions (P<.001), were statistically significant. Additional etching had an adverse effect on the bond strength of Clearfil SE Bond to normal dentine (P<.005), and no significant improvement was found for AI-affected dentine (P=.479). Additional acid etching does not improve the bond strength of a self-etch adhesive to AI-affected dentine. © 2017 John Wiley & Sons Australia, Ltd.

Effect of sonic application mode on the resin-dentin bond strength and nanoleakage of simplified self-etch adhesive.

PubMed

Mena-Serrano, Alexandra; Garcia, Eugenio Jose; Loguercio, Alessandro Dourado; Reis, Alessandra

2014-04-01

This study aims to evaluate the effect of different application modes on the immediate and 6-month resin-dentin bond strength (μTBS) and nanoleakage in the hybrid and adhesive layers. Three 1-step self-etch adhesives (One Coat 7.0 (OC), Clearfil S(3) Bond (CS), and FuturaBond NR (FB)) were applied on a flat superficial dentin surface of 30 human molars under manual mode or sonic vibration at a frequency of 170 Hz (SV). Composite build-ups were constructed incrementally; specimens were sectioned to obtain resin-dentin sticks with cross-sectional area of 0.8 mm(2) and tested in tension (0.5 mm/min) immediately (IM) or after 6 months (6M) of water storage. Two bonded sticks, from each tooth at each storage time, were immersed in a silver nitrate solution, photo-developed, and analyzed under scanning electron microscopy. The amount of nanoleakage was measured using the ImageTool 3.0 software. Data, from each adhesive, were analyzed by two-way ANOVA and Tukey's test (α = 0.05). OC and CS showed higher μTBS and lower nanoleakage in the IM period when applied with SV groups. For FB, no significant difference was observed between the two modes of application. All materials showed lower nanoleakage in the SV groups. Higher nanoleakage was observed after 6M for OC and FB. The sonic application mode at an oscillating frequency of 170 Hz can improve the resin-dentin μTBS, reduce the nanoleakage, and retard the degradation of the resin-dentin μTBS of Clearfil S(3) Bond and One Coat 7.0 adhesives. Sonic application mode at an oscillating frequency of 170 Hz can be helpful and easy to use in dental practice to guaranty long-lasting restorations.

Effect of dimethyl sulfoxide wet-bonding technique on hybrid layer quality and dentin bond strength.

PubMed

Stape, Thiago Henrique Scarabello; Tjäderhane, Leo; Marques, Marcelo Rocha; Aguiar, Flávio Henrique Baggio; Martins, Luís Roberto Marcondes

2015-06-01

This study examined the effect of a dimethyl sulfoxide (DMSO) wet bonding technique on the resin infiltration depths at the bonded interface and dentin bond strength of different adhesive systems. Flat dentin surfaces of 48 human third molars were treated with 50% DMSO (experimental groups) or with distilled water (controls) before bonding using an etch-and-rinse (SBMP: Scotchbond Multi-Purpose, 3M ESPE) or a self-etch (Clearfil: Clearfil SE Bond, Kuraray) adhesive system. The restored crown segments (n=12/group) were stored in distilled water (24h) and sectioned for interfacial analysis of exposed collagen using Masson's Trichrome staining and for microtensile bond strength testing. The extent of exposed collagen was measured using light microscopy and a histometric analysis software. Failure modes were examined by SEM. Data was analyzed by two-way ANOVA followed by Tukey Test (α=0.05). The interaction of bonding protocol and adhesive system had significant effects on the extension of exposed collagen matrix (p<0.0001) and bond strength (p=0.0091). DMSO-wet bonding significantly reduced the extent of exposed collagen matrix for SBMP and Clearfil (p<0.05). Significant increase in dentin bond strength was observed on DMSO-treated specimens bonded with SBMP (p<0.05), while no differences were observed for Clearfil (p>0.05). DMSO-wet bonding was effective to improve the quality of resin-dentin bonds of the tested etch-and-rinse adhesives by reducing the extent of exposed collagen matrix at the base of the resin-dentin biopolymer. The improved penetration of adhesive monomers is reflected as an increase in the immediate bond strength when the DMSO-wet bonding technique is used with a water-based etch-and-rinse adhesive. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Microtensile bond strength of contemporary adhesives to primary enamel and dentin.

PubMed

Marquezan, Marcela; da Silveira, Bruno Lopes; Burnett, Luiz Henrique; Rodrigues, Célia Regina Martins Delgado; Kramer, Paulo Floriani

2008-01-01

The purpose of this study was to assess bond strength of three self-etching and two total-etch adhesive systems bonded to primary tooth enamel and dentin. Forty extracted primary human molars were selected and abraded in order to create flat buccal enamel and occlusal dentin surfaces. Teeth were assigned to one of the adhesive systems: Adper Scotch Bond Multi Purpose, Adper Single Bond 2, Adper Prompt L-Pop, Clearfil SE Bond and AdheSE. Immediately to adhesive application, a composite resin (Filtek Z250) block was built up. After 3 months of water storage, each sample was sequentially sectioned in order to obtain sticks with a square cross-sectional area of about 0.72 mm2. The specimens were fixed lengthways to a microtensile device and tested using a universal testing machine with a 50-N load cell at a crosshead speed of 0.5 mm/min. Microtensile bond strength values were recorded in MPa and compared by Analysis of Variance and the post hoc Tukey test (a = 0.05). In enamel, Clearfil SE Bond presented the highest values, followed by Adper Single Bond 2, AdheSE and Adper Scotch Bond Multi Purpose, without significant difference. The highest values in dentin were obtained with Adper Scotch Bond Multi Purpose and all other adhesives did not present significant different values from that, except Adper Prompt L-Pop that achieved the lowest bond strength in both substrates. Adper Scotch Bond Multi Purpose and Adper Single Bond 2 presented significantly lower values in enamel than in dentin although all other adhesives presented similar results in both substrates. contemporary adhesive systems present similar behaviors when bonded to primary teeth, with the exception of the one-step self-etching system; and self-etching systems can achieve bond strength values as good in enamel as in dentin of primary teeth.

The effect of 25% tannic acid on prepared dentin: a scanning electron microscope-methylene blue dye study.

PubMed

Bitter, N C

1990-07-01

The effect on the permeability of prepared dentin treated with 25% tannic acid and 6% citric acid was compared with the untreated dentinal surface. Methylene blue was applied to the dentin surface after treatment to evaluate penetration into dentinal tubules. The tannic acid solution reduced or prevented dye penetration of the dentinal tubules. Citric acid treatment permitted severe penetration. The 25% tannic acid solution removed the smear layer while inhibiting penetration of the dye.

The durability of phosphoric acid promoted bioglass-dentin interaction layer.

PubMed

Bakry, A S; Takahashi, H; Otsuki, M; Tagami, J

2013-04-01

Phosphoric acid-Bioglass 45S5 paste can create an interaction layer formed of calcium-phosphate crystals on the dentin surface. In this study, the efficiency of decreasing the dentin permeability exerted by the interaction layer formed between bioglass and dentin was compared to a resin-containing oxalate desensitizing agent (MS Coat One) and a resin-free oxalate desensitizing agent (Super Seal). Dentin permeability was measured before/after a brushing abrasion challenge, followed by examining the top and the fractured dentin surfaces with a field emission scanning electron microscope. Moreover, the chemical nature of the compounds formed on top of the dentin surface was examined using the field emission scanning electron microscope (FE-SEM) equipped with an energy-dispersive X-ray spectroscope (EDS), and the crystalline structures of the dentinal surfaces were examined by X-ray diffraction (XRD). The results showed that application of 45S5 bioglass paste to dentin was able to occlude patent dentinal tubule orifices with a layer of calcium-phosphate crystals, while the oxalate containing agents were able to form small crystals which were found in dentinal tubule orifices and scattered along the superficial parts of the dentinal tubule lumen. The brushing-abrasion challenge significantly increased the permeability of dentin treated by Super Seal and MS Coat One, while these challenges had no significant effect on the dentin permeability of specimens treated with 45S5 bioglass paste. The new technique provided better durability than two products available on the market. Moreover, our previous research showed the biocompatibility of using this technique on dental pulp cells, suggesting that this technique can aid in treating dentin hypersensitivity cases. Copyright © 2012 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Microtensile bond strength of three simplified adhesive systems to caries-affected dentin.

PubMed

Scholtanus, J D; Purwanta, Kenny; Dogan, Nilgun; Kleverlaan, Cees J; Feilzer, Albert J

2010-08-01

The purpose of the study was to determine the microtensile bond strength of three different simplified adhesive systems to caries-affected dentin. Fifteen extracted human molars with primary carious lesions were ground flat until dentin was exposed. Soft caries-infected dentin was excavated with the help of caries detector dye. On the remaining hard dentin, a standardized smear layer was created by polishing with 600-grit SiC paper. Teeth were divided into three groups and treated with one of the three tested adhesives: Adper Scotchbond 1 XT (3M ESPE), a 2-step etch-andrinse adhesive, Clearfil S3 Bond (Kuraray), a 1-step self-etching or all-in-one adhesive, and Clearfil SE Bond (Kuraray), a 2-step self-etching adhesive. Five-mm-thick composite buildups (Z-250, 3M ESPE) were built and light cured. After water storage for 24 h at 37ºC, the bonded specimens were sectioned into bars (1.0 x 1.0 mm; n = 20 to 30). Microtensile bond strength of normal dentin specimens and caries-affected dentin specimens was measured in a universal testing machine (crosshead speed = 1 mm/min). Data were analyzed using two-way ANOVA and Tukey's post-hoc test (p < 0.05). No significant differences in bond strength values to normal dentin between the three adhesives were found. Adper Scotchbond 1 XT and Clearfil S3 Bond showed significantly lower bond strength values to caries-affected dentin. For Clearfil SE Bond, bond strength values to normal and caries-affected dentin were not significantly different. All the tested simplified adhesives showed similar bond strength values to normal dentin. For the tested 2-step etch-and-rinse adhesive and the all-in-one adhesive, the bond strength values to caries-affected dentin were lower than to normal dentin.

Qualitative Time-of-Flight Secondary Ion Mass Spectrometry Analysis of Root Dentin Irrigated with Sodium Hypochlorite, EDTA, or Chlorhexidine.

PubMed

Kolosowski, Kamil P; Sodhi, Rana N S; Kishen, Anil; Basrani, Bettina R

2015-10-01

Sodium hypochlorite (NaOCl), chelating agents, and chlorhexidine (CHX), which are commonly used irrigants during endodontic treatment, have the potential to alter the physical and chemical properties of the dentin structure. The aim of this study was to use time-of-flight secondary ion mass spectrometry to qualitatively evaluate the chemical characteristics of dentin surface and compare it with dentin exposed to NaOCl, EDTA, or CHX. Four blocks of dentin from a root of a human maxillary molar were embedded in resin and trimmed with a microtome to expose the dentin. Samples were randomly assigned to 4 treatment groups: (1) no irrigation treatment (sample A), (2) 2.5% NaOCl (sample B), (3) 17% EDTA (sample C), and (4) 2% CHX (sample D). Dentin surfaces were analyzed by time-of-flight secondary ion mass spectrometry, which allowed characterization of dentin surface chemistry by both imaging and mass spectroscopic analysis obtained in high mass and spatial resolution modes. Sample A revealed intense peaks characteristics of hydroxyapatite in addition to Na(+), K(+), CH4N(+), CN(-), CNO(-), Mg(+), F(-), and HCO2(-) peaks. Sample B showed severely decreased CH4N(+) and increased intensity of Cl(-). Sample C lacked Ca(+) and Mg(+) and showed decreased PO2(-) and PO3(-). Sample D exhibited a distinct presence of CHX. The spectral image of sample A displayed even distribution of Na(+) and Ca(+) on a smeared surface. The surfaces of samples B and D had patent dentinal tubules, whereas sample D showed an intense CHX signal. Sample C had some patent dentinal tubules and lacked Ca(+). NaOCl removed protein components from the dentin matrix, EDTA removed calcium and magnesium ions from the dentin, and CHX formed an adsorbed layer on the dentin surface. Copyright © 2015 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

Morphological Analysis of Dentin Surface after Conditioning with Two Different methods: Chemical and Mechanical.

PubMed

Rafael, Caroline Freitas; Quinelato, Valquíria; Morsch, Carolina Schaffer; DeDeus, Gustavo; Reis, Claudia Mendonca

2016-01-01

Alternative pretreatment strategies of dentin and adhesionare constantly being developed and studied with the goal of improving the adhesion of resin restorative materials with this tissue. The objectives of the present study were to evaluate the ability of airborne-particle abrasion (APA) with aluminum oxide on dentin to remove the smear layer and the effects produced on the dentin microstructure. The phosphoric acid (PA) was used for a comparison. For that, 20 human third molars were randomly allocated into two experimental groups, according to the dentin pretreatment method used: G1 (N = 10) - PA, G2 (N = 10) -APA. For dentin surface analyses, an environmental scanning electron microscope (ESEM) was employed to observe dentin surfaces before and after the procedures. Before pretreatment, the specimens of both groups were smear covered. After pretreatment, the G1 images revealed dentin tubule orifices opened, enlarged and some erosive effects. (G2) exposed tubule orifices without enlargement, but crack-like alterations were observed on the surfaces. In this way, APA with aluminum oxide was able to remove the smear layer. The influences of the dentin roughness on adhesion and the consequences on dentin integrity and hardness need further investigations. A good conditioning of the dentin before cementation is necessary in order to obtain a satisfactory rehabilitation in adhesive dentistry. So, it is necessary to know all methods to do it.

Zinc-Containing Restorations Create Amorphous Biogenic Apatite at the Carious Dentin Interface: A X-Ray Diffraction (XRD) Crystal Lattice Analysis.

PubMed

Toledano, Manuel; Aguilera, Fátima S; López-López, Modesto T; Osorio, Estrella; Toledano-Osorio, Manuel; Osorio, Raquel

2016-10-01

The aim of this research was to assess the ability of amalgam restorations to induce amorphous mineral precipitation at the caries-affected dentin substrate. Sound and caries-affected dentin surfaces were subjected to both Zn-free and Zn-containing dental amalgam restorations. Specimens were submitted to thermocycling (100,000 cycles/5°C-55°C, 3 months). Dentin surfaces were studied by atomic force microscopy (nanoroughness), X-ray diffraction, field emission scanning electron microscopy, and energy-dispersive analysis, for physical and morphological surface characterization. Zn-containing amalgam placement reduced crystallinity, crystallite size, and grain size of calcium phosphate crystallites at the dentin surface. Both microstrain and nanoroughness were augmented in caries-affected dentin restored with Zn-containing amalgams. Caries-affected dentin showed the shortest mineral crystallites (11.04 nm), when Zn-containing amalgams were used for restorations, probably leading to a decrease of mechanical properties which might favor crack propagation and deformation. Sound dentin restored with Zn-free amalgams exhibited a substantial increase in length of grain particles (12.44 nm) embedded into dentin crystallites. Zn-containing amalgam placement creates dentin mineralization and the resultant mineral was amorphous in nature. Amorphous calcium phosphate provides a local ion-rich environment, which is considered favorable for in situ generation of prenucleation clusters, promotong further dentin remineralization.

Influence of Nd:YAG laser on the bond strength of self-etching and conventional adhesive systems to dental hard tissues.

PubMed

Marimoto, A K; Cunha, L A; Yui, K C K; Huhtala, M F R L; Barcellos, D C; Prakki, A; Gonçalves, S E P

2013-01-01

The aim of this study was to investigate the influence of Nd:YAG laser on the shear bond strength to enamel and dentin of total and self-etch adhesives when the laser was applied over the adhesives, before they were photopolymerized, in an attempt to create a new bonding layer by dentin-adhesive melting. One-hundred twenty bovine incisors were ground to obtain flat surfaces. Specimens were divided into two substrate groups (n=60): substrate E (enamel) and substrate D (dentin). Each substrate group was subdivided into four groups (n=15), according to the surface treatment accomplished: X (Xeno III self-etching adhesive, control), XL (Xeno III + laser Nd:YAG irradiation at 140 mJ/10 Hz for 60 seconds + photopolymerization, experimental), S (acid etching + Single Bond conventional adhesive, Control), and SL (acid etching + Single Bond + laser Nd:YAG at 140 mJ/10 Hz for 60 seconds + photopolymerization, experimental). The bonding area was delimited with 3-mm-diameter adhesive tape for the bonding procedures. Cylinders of composite were fabricated on the bonding area using a Teflon matrix. The teeth were stored in water at 37°C/48 h and submitted to shear testing at a crosshead speed of 0.5 mm/min in a universal testing machine. Results were analyzed with three-way analysis of variance (ANOVA; substrate, adhesive, and treatment) and Tukey tests (α=0.05). ANOVA revealed significant differences for the substrate, adhesive system, and type of treatment: lased or unlased (p<0.05). The mean shear bond strength values (MPa) for the enamel groups were X=20.2 ± 5.61, XL=23.6 ± 4.92, S=20.8 ± 4.55, SL=22.1 ± 5.14 and for the dentin groups were X=14.1 ± 7.51, XL=22.2 ± 6.45, S=11.2 ± 5.77, SL=15.9 ± 3.61. For dentin, Xeno III self-etch adhesive showed significantly higher shear bond strength compared with Single Bond total-etch adhesive; Nd:YAG laser irradiation showed significantly higher shear bond strength compared with control (unlased). Nd:YAG laser application prior to photopolymerization of adhesive systems significantly increased the bond strength to dentin.

Sealing ability and bond strength of four contemporary adhesives to enamel and to dentine.

PubMed

Atash, R; Vanden Abbeele, A

2005-12-01

To compare the shear bond strength and microleakage of four adhesive systems to the enamel and dentine of primary bovine teeth. 120 bovine primary mandibular incisors were collected and stored in an aqueous 1% chloramine solution at room temperature for no longer than 3 months after extraction (80 for shear bond testing and 40 for microleakage evaluation). The adhesives tested were Clearfil SE bond (SE), Adper Prompt L Pop (LP), Xeno III (XE), and Prime and Bond NT (PB). For shear bond strength testing the specimens were wet ground to 600 grit SiC paper to expose a flat enamel or dentine surface. After bonding and restoration with Dyract AP (DAP), the teeth were subjected to shear stress using a universal testing machine. For microleakage evaluation, facial class V cavities were prepared half in enamel and half in cementum. All cavities were restored with DAP. After thermocycling and immersion in 2% methylene blue, the dye penetration was evaluated under a stereomicroscope. All data were analysed by Chi-square tests or Fisher's tests when adapted in order to determine the significant differences between groups. Results were considered as significant for p < 0.05. Results were analysed with an ANOVA test and a Bonferroni's multiple comparison. The level of significance was p < 0.05. Shear bond strength values (MPa,) ranged from: on enamel 11.06 to 5.34, in decreasing order SE, LP, XE and PB and on dentine 10.47 to 4.74, in decreasing order SE, XE, LP and PB. Differences in bond strengths between the four systems on enamel and dentine were all statistically significant, excepted for XE vs LP (shear bond at dentine). No significant differences were recorded in the microleakage degree between the four adhesive systems on enamel and on dentine (p > 0.0.5). The highest shear bond strength was achieved by Clearfil SE bond and the lowest by Prime and Bond NT. There was no significant difference concerning the sealing ability of the four adhesive systems.

Multiscale characterization of partially demineralized superficial and deep dentin surfaces.

PubMed

Pelin, Irina M; Trunfio-Sfarghiu, Ana-Maria; Farge, Pierre; Piednoir, Agnes; Pirat, Christophe; Ramos, Stella M M

2013-08-01

The objective of this study was to address the following question: 'Which properties are modified in partially demineralized surfaces, compared with non-demineralized dentin surfaces, following orthophosphoric acid-etching as performed in clinical procedures?'. For this purpose, the complementary techniques atomic force microscopy/spectroscopy, scanning electron microscopy, energy-dispersive X-ray spectroscopy, and contact angle measurements were used to provide a multiscale characterization of the dentin substrate undergoing the acidic preconditioning designed to enhance wetting. Special attention was given to the influence of the etching pretreatment on the nanomechanical properties at different levels of dentin surfaces, in both dry and hydrated conditions. The four-sided pyramid model (extended Hertz contact model) proved to be accurate for calculating the apparent Young's modulus, offering new information on the elasticity of dentin. The modulus value notably decreased following etching and surface hydration. This study underlines that after the acid etching pretreatment the contribution of the nanomechanical, morphological, and physicochemical modifications has a strong influence on the dentin adhesion properties and thus plays a significant role in the coupling of the adhesive-resin composite build-up material at the dentin surface. © 2013 Eur J Oral Sci.

Residual interface tensile strength of ceramic bonded to dentin after cyclic loading and aging.

PubMed

Hernandez, Alfredo I; Roongruangphol, Thasanai; Katsube, Noriko; Seghi, Robert R

2008-03-01

To guard against the potential risk of cusp fracture, esthetic onlay restorations have been advocated for teeth with large restorations. The influence of the adhesive resin cement is believed to play a role in strengthening these restorations. The durability of this tooth/adhesive/ceramic interface is critical to ensure clinical longevity. The purpose of this study was to assess the effects of cyclic loading and environmental aging on the residual interface strength of a ceramic bonded to dentin structure. Eighteen simple trilayer specimens were fabricated, consisting of a 1.5-mm-thick ceramic plate (ProCAD) bonded to a flattened human molar tooth with exposed coronal dentin. The ceramic plates were bonded using resin cement (Nexus 2) and manufacturer-recommended bonding techniques. The specimens were divided into 3 equal groups and were stored in water at 37 degrees C for 10 weeks as a control group (CT), 9 months as an aging group (AG), or placed in water at 37 degrees C while being subjected to 10 million vertical loading cycles between 20 N to 200 N, as a fatigue group (FG). After the specimens were subjected to the experimental conditions, they were sectioned perpendicular to the flat ceramic surface into 1 x 1-mm sticks. The mean residual interface microtensile bond (MTB) strength was determined for each specimen using only those sticks which contained ceramic bonded to dentin. The MTB strength data were analyzed using Weibull analysis methods to determine differences between groups. All subsequent failed specimen surfaces were evaluated under a stereomicroscope at x10 magnification to determine the apparent failure modes. Some specimens were selected from each failure mode category for surface evaluation under a scanning electron microscope (SEM). The characteristic Weibull means for the 3 groups were CT, 19.2, FG, 14.7, and AG, 11.7. The bond strength of group CT was significantly greater than both AG (P=.007) and FG (P=.014). Light microscopic categorization of the failure modes suggests that adhesive failure at the ceramic/cement interface was the most common (65%) for all 3 groups. SEM evaluation of failed surfaces of select specimens from each group could not distinguish any interface appearance differences. For indirect adhesive-retained ceramic restorations, both cyclic masticatory loading and hydrolytic degradation may contribute to a weakening of the interface bond. The ceramic/resin interface may be more susceptible to these changes over the time frame of this investigation than the dentin/resin interface.

Influence of temporary cement contamination on the surface free energy and dentine bond strength of self-adhesive cements.

PubMed

Takimoto, Masayuki; Ishii, Ryo; Iino, Masayoshi; Shimizu, Yusuke; Tsujimoto, Akimasa; Takamizawa, Toshiki; Ando, Susumu; Miyazaki, Masashi

2012-02-01

The surface free energy and dentine bond strength of self-adhesive cements were examined after the removal of temporary cements. The labial dentine surfaces of bovine mandibular incisors were wet ground with #600-grit SiC paper. Acrylic resin blocks were luted to the prepared dentine surfaces using HY Bond Temporary Cement Hard (HY), IP Temp Cement (IP), Fuji TEMP (FT) or Freegenol Temporary Cement (TC), and stored for 1 week. After removal of the temporary cements with an ultrasonic tip, the contact angle values of five specimens per test group were determined for the three test liquids, and the surface-energy parameters of the dentine surfaces were calculated. The dentine bond strengths of the self-adhesive cements were measured after removal of the temporary cements in a shear mode at a crosshead speed of 1.0mm/min. The data were subjected to one-way analysis of variance (ANOVA) followed by Tukey's HSD test. For all surfaces, the value of the estimated surface tension component γ(S)(d) (dispersion) was relatively constant at 41.7-43.3 mJm(-2). After removal of the temporary cements, the value of the γ(S)(h) (hydrogen-bonding) component decreased, particularly with FT and TC. The dentine bond strength of the self-adhesive cements was significantly higher for those without temporary cement contamination (8.2-10.6 MPa) than for those with temporary cement contamination (4.3-7.1 MPa). The γ(S) values decreased due to the decrease of γ(S)(h) values for the temporary cement-contaminated dentine. Contamination with temporary cements led to lower dentine bond strength. The presence of temporary cement interferes with the bonding performance of self-adhesive cements to dentine. Care should be taken in the methods of removal of temporary cement when using self-adhesive cements. Copyright © 2011 Elsevier Ltd. All rights reserved.

Effect of simulated pulpal pressure on all-in-one adhesive bond strengths to dentine.

PubMed

Hosaka, Keiichi; Nakajima, Masatoshi; Yamauti, Monica; Aksornmuang, Juthatip; Ikeda, Masaomi; Foxton, Richard M; Pashley, David H; Tagami, Junji

2007-03-01

To evaluate the durability of all-in-one adhesive systems bonded to dentine with and without simulated hydrostatic pulpal pressure (PP). Flat dentine surfaces of extracted human molars were prepared. Two all-in-one adhesive systems, One-Up Bond F (OBF) (Tokuyama Corp., Tokyo, Japan), and Fluoro Bond Shake One (FBS) (Shofu Co., Kyoto, Japan) were applied to the dentine surfaces under either a PP of 0 or 15cm H(2)O. Then, resin composite build-ups were made. The specimens bonded under pressure were stored in 37 degrees C water for 24h, 1 and 3 months under 15cm H(2)O PP. Specimens not bonded under pressure were stored under zero PP. After storage, the specimens were sectioned into slabs that were trimmed to hourglass shapes and subjected to micro-tensile bond testing (muTBS). The data were analysed using two-way ANOVA and Holm-Sidak HSD multiple comparison tests (alpha=0.05). The muTBS of OBF fell significantly (p<0.05) when PP was applied during bonding and storage, regardless of storage time. In contrast, although the muTBS of OBF specimens bonded and stored without hydrostatic pressure storage fell significantly over the 3 months period, the decrease was less than half as much as specimens stored under PP. In FBS bonded specimens, although there was no significant difference between the muTBS with and without hydrostatic pulpal pressure at 24h, by 1 and 3 months of storage under PP, significant reductions were seen compared with the control group without PP. The muTBS of OBF bonded specimens was lowered more by simulated PP than by storage time; specimens bonded with FBS were not sensitive to storage time in the absence of PP, but showed lower bond strengths at 1 and 3 months in the presence of PP.

Shear bond strength of composite to deep dentin after treatment with two different collagen cross-linking agents at varying time intervals.

PubMed

Srinivasulu, S; Vidhya, S; Sujatha, M; Mahalaxmi, S

2012-01-01

This in vitro study evaluated the shear bond strength of composite resin to deep dentin using a total etch adhesive after treatment with two collagen cross-linking agents at varying time intervals. Thirty freshly extracted human maxillary central incisors were sectioned longitudinally into equal mesial and distal halves (n=60). The proximal deep dentin was exposed, maintaining a remaining dentin thickness (RDT) of approximately 1 mm. The specimens were randomly divided into three groups based on the surface treatment of dentin prior to bonding as follows: group I (n=12, control): no prior dentin surface treatment; group II (n=24): dentin surface pretreated with 10% sodium ascorbate; and group III (n=24): dentin surface pretreated with 6.5% proanthocyanidin. Groups II and III were further subdivided into two subgroups of 12 specimens each, based on the pretreatment time of five minutes (subgroup A) and 10 minutes (subgroup B). Shear bond strength of the specimens was tested with a universal testing machine, and the data were statistically analyzed. Significantly higher shear bond strength to deep dentin was observed in teeth treated with 10% sodium ascorbate (group II) and 6.5% proanthocyanidin (group III) compared to the control group (group I). Among the collagen cross-linkers used, specimens treated with proanthocyanidin showed significantly higher shear bond strength values than those treated with sodium ascorbate. No significant difference was observed between the five-minute and 10-minute pretreatment times in groups II and III. It can be concluded that dentin surface pretreatment with both 10% sodium ascorbate and 6.5% proanthocyanidin resulted in significant improvement in bond strength of resin composite to deep dentin.

Effect and Stability of Poly(Amido Amine)-Induced Biomineralization on Dentinal Tubule Occlusion

PubMed Central

Gao, Yuan; Liang, Kunneng; Li, Jianshu; Yuan, He; Liu, Hongling; Duan, Xiaolei; Li, Jiyao

2017-01-01

In recent years, scientists have developed various biomaterials to remineralize human teeth to treat dentine hypersensitivity. Poly(amido amine) (PAMAM) dendrimers have become a research focus in this field. It has been demonstrated that PAMAM is able to create precipitates both on the surface of and within the dentinal tubules, however, there is little information about its effect on reducing dentine permeability in vitro. This study aimed to evaluate the in vitro effectiveness and stability of the fourth generation amine-terminated PAMAM on dentinal tubule occlusion, especially on dentine permeability. Sodium fluoride (NaF), which has been widely used as a desensitizing agent, is regarded as positive control. Demineralized sensitive dentine samples were coated with PAMAM or sodium fluoride solutions and soaked in artificial saliva (AS) at 37 °C for different periods. Four weeks later, samples in each group were then equally split into two subgroups for testing using a brushing challenge and an acid challenge. Dentine permeability of each specimen was measured before and after each challenge using a fluid filtration system. Dentine morphology and surface deposits were characterized by scanning electron microscope (SEM) and analyzed with Image-Pro Plus software. Data were evaluated through multifactorial ANOVA with repeated measures and pair-wise comparisons at a level of 5%. The results showed that PAMAM and NaF significantly reduced dentine permeability to 25.1% and 20.7%. Both of them created precipitates on dentine surfaces after AS immersion for 28 days. PAMAM-induced biomineralization not only on dentine surfaces, but also deeper in dentinal tubules, significantly reduced dentine permeability. Moreover, PAMAM-induced biomineralization elicited excellent stable occlusion effects after acid challenge. In conclusion, PAMAM demonstrated a strong ability to resist acid and showed great potential to be used in the treatment of dentine hypersensitivity in future. PMID:28772744

Water evaporation from substrate tooth surface during dentin treatments.

PubMed

Kusunoki, Mizuho; Itoh, Kazuo; Gokan, Yuka; Nagai, Yoshitaka; Tani, Chihiro; Hisamitsu, Hisashi

2011-01-01

The purpose of this study was to evaluate changes in the quantity of water evaporation from tooth surfaces. The amount of water evaporation was measured using Multi probe adapter MPA5 and Tewameter TM300 (Courage+Khazaka Electric GmbH, Köln, Germany) after acid etching and GM priming of enamel; and after EDTA conditioning and GM priming of dentin. The results indicated that the amount of water evaporation from the enamel surface was significantly less than that from the dentin. Acid etching did not affect the water evaporation from enamel, though GM priming significantly decreased the evaporation (83.48 ± 15.14% of that before priming). The evaporation from dentin was significantly increased by EDTA conditioning (131.38 ± 42.08% of that before conditioning) and significantly reduced by GM priming (80.26 ± 7.43% of that before priming). It was concluded that dentin priming reduced water evaporation from the dentin surface.

Influence of handpiece maintenance sprays on resin bonding to dentin.

PubMed

Sugawara, Toyotarou; Kameyama, Atsushi; Haruyama, Akiko; Oishi, Takumi; Kukidome, Nobuyuki; Takase, Yasuaki; Tsunoda, Masatake

2010-01-01

To investigate the influence of maintenance spray on resin bonding to dentin. The crown of extracted, caries-free human molars was transversally sectioned with a model trimmer to prepare the dentin surfaces from mid-coronal sound dentin, and then uniformly abraded with #600 silicon carbide paper. The dentin surfaces were randomly divided into three groups: oil-free spray group where maintenance cleaner for air bearing handpieces was sprayed onto the dentin surface for 1 s and rinsed with water spray for 30 s; oil-containing spray group where maintenance cleaner for micro motor handpieces was sprayed onto the dentin surface for 1 s and rinsed with water spray for 30 s; and control group where the surface was rinsed with water spray for 30 s and then air-dried. These surfaces were then bonded with Clearfil SE Bond (Kuraray Medical), and resin composite (Clearfil AP-X, Kuraray Medical) build-up crowns were incrementally constructed on the bonded surfaces. After storage for 24 h in 37°C water, the bonded teeth were sectioned into hour-glass shaped slices (0.7-mm thick) perpendicular to the bonded surfaces. The specimens were then subjected to microtensile bond strength (μTBS) testing at a crosshead speed of 1.0 mm/min. Data were analyzed with one-way ANOVA and the Tukey-Kramer test. Maintenance spray-contaminated specimens (oil-free and oil-containing spray groups) showed significantly lower μTBS than control specimens (P < 0.05). However, there was no significant difference between the spray-contaminated groups (P > 0.05). Maintenance spray significantly reduces the bond strength of Clearfil SE Bond to dentin.

Effect of Collagen Matrix Saturation on the Surface Free Energy of Dentin using Different Agents.

PubMed

de Almeida, Leopoldina de Fátima Dantas; Souza, Samilly Evangelista; Sampaio, Aline Araújo; Cavalcanti, Yuri Wanderley; da Silva, Wander José; Del Bel Cur, Altair A; Hebling, Josimeri

2015-07-01

The surface free energy of conditioned-dentin is one of the factors that interfere with monomeric infiltration of the interfibrillar spaces. Saturation of the tooth matrix with different substances may modulate this energy and, consequently, the wettability of the dentin. To evaluate the influence of different substances used to saturate conditioned-dentin on surface free energy (SFE) of this substrate. Dentin blocks (4 × 7 × 1 mm, n = 6/ group), obtained from the roots of bovine incisors, were etched using phosphoric acid for 15 seconds, rinsed and gently dried. The surfaces were treated for 60 seconds with: ultra-purified water (H20-control); ethanol (EtOH), acetone (ACT), chlorhexidine (CHX), ethylenediaminetetraacetic acid (EDTA); or sodium hypochlorite (NaOCl). The tooth surfaces were once again dried with absorbent paper and prepared for SFE evaluation using three standards: water, formamide and bromonaphthalene. Analysis of variance (ANOVA) and Dunnet's tests (a = 0.05) were applied to the data. Ethylenediaminetetraacetic acid was the only substance that caused a change to the contact angle for the standards water and formamide, while only EtOH influenced the angles formed between formamide and the dentin surface. None of the substances exerted a significant effect for bromonaphtha-lene. In comparison to the control, only EDTA and NaOCl altered both polar components of the SFE. Total SFE was increased by saturation of the collagen matrix by EDTA and reduced when NaOCl was used. Saturation of the collagen matrix by EDTA and EtOH changed the surface free energy of the dentin. In addition, the use of NaOCl negatively interfered with the properties evaluated. The increase of surface free energy and wettability of the dentin surface would allow higher penetration of the the adhesive system, which would be of importance to the clinical success of resin-dentin union.

Potential role of surface wettability on the long-term stability of dentin bonds after surface biomodification

PubMed Central

Leme, Ariene A.; Vidal, Cristina M. P.; Hassan, Lina Saleh; Bedran-Russo, Ana K.

2015-01-01

Degradation of the adhesive interface contributes to the failure of resin composite restorations. The hydrophilicity of the dentin matrix during and after bonding procedures may result in an adhesive interface that is more prone to degradation over time. This study assessed the effect of chemical modification of dentin matrix on the wettability and the long-term reduced modulus of elasticity (Er) of the adhesive interfaces. Human molars were divided into groups according to the priming solutions: distilled water (control), 6.5% Proanthocyanidin-rich grape seed extract (PACs), 5.75% 1-ethyl-3-[3-dimethylaminopropyl] carbodiimide hydrochloride/1.4% n-hydroxysuccinimide (EDC/NHS) and 5% Glutaraldehyde (GA). The water-surface contact angle was verified before and after chemical modification of the dentin matrix. The demineralized dentin surface was treated with the priming solutions and restored with One Step Plus (OS) and Single Bond Plus (SB) and resin composite. The Er of the adhesive, hybrid layer and underlying dentin was evaluated after 24 h and 30 months in artificial saliva. The dentin hydrophilicity significantly decreased after application of the priming solutions. Aging significantly decreased the Er in the hybrid layer and underlying dentin of control groups. The Er of GA groups remained stable over time at the hybrid layer and underlying dentin. Significant higher Er was observed for PACs and EDC/NHS groups at the hybrid layer after 24 h. The decreased hydrophilicity of the modified dentin matrix likely influence the immediate mechanical properties of the hybrid layer. Dentin biomodification prevented substantial aging at the hybrid layer and underlying dentin after 30 months storage. PMID:25869721

Surface modification of gutta-percha cones by non-thermal plasma.

PubMed

Prado, Maíra; Menezes, Marilia Santana de Oliveira; Gomes, Brenda Paula Figueiredo de Almeida; Barbosa, Carlos Augusto de Melo; Athias, Leonardo; Simão, Renata Antoun

2016-11-01

This study was designed to evaluate the effects of Oxygen and Argon plasma on gutta-percha surfaces. A total of 185 flat smooth gutta-percha surfaces were used. Samples were divided into groups: control: no plasma treatment; Oxygen: treatment with Oxygen plasma for 1min; Argon: treatment with Argon plasma for 1min. Samples were evaluated topographically by scanning electron microscopy and atomic force microscopy; and chemically by Fourier Transform-infrared Spectroscopy. A goniometer was used to determine the surface free energy and the wettability of the endodontic sealers. Additionally 60 bovine teeth were filled using pellets of gutta-percha (control, oxygen and argon plasma) and the sealers. Teeth were evaluated by push-out and microleakage tests. Data were statistically analyzed using specific tests. Argon plasma did not change the surface topography, while Oxygen plasma led to changes. Both treatments chemically modified the gutta-percha surface. Argon and Oxygen plasma increased the surface free energy and favored the wettability of AH Plus and Pulp Canal Sealer EWT. Regarding bond strength analysis, for AH Plus sealer, both plasma treatments on gutta-percha favored the bond strength to dentin. However, for Pulp Canal Sealer, there is no statistically significant influence. For leakage test, dye penetration occurred between sealer and dentin in all groups. In conclusion, Oxygen plasma led to both topographic and chemical changes in the gutta-percha surface, while Argon plasma caused only chemical changes. Both treatments increased the surface free energy, favoring the wettability of AH Plus and Pulp Canal Sealer EWT sealers and influenced positively in the adhesion and leakage. Copyright © 2016 Elsevier B.V. All rights reserved.

Qualitative analysis of precipitate formation on the surface and in the tubules of dentin irrigated with sodium hypochlorite and a final rinse of chlorhexidine or QMiX.

PubMed

Kolosowski, Kamil P; Sodhi, Rana N S; Kishen, Anil; Basrani, Bettina R

2014-12-01

Interaction of sodium hypochlorite (NaOCl) mixed with chlorhexidine (CHX) produces a brown precipitate containing para-chloroaniline (PCA). When QMiX is mixed with NaOCl, no precipitate forms, but color change occurs. The aim of this study was to qualitatively assess the formation of precipitate and PCA on the surface and in the tubules of dentin irrigated with NaOCl, followed either by EDTA, NaOCl, and CHX or by saline and QMiX by using time-of-flight secondary ion mass spectrometry (TOF-SIMS). Dentin blocks were obtained from human maxillary molars, embedded in resin, and cross-sectioned to expose dentin. Specimens in group 1 were immersed in 2.5% NaOCl, followed by 17% EDTA, 2.5% NaOCl, and 2% CHX. Specimens in group 2 were immersed in 2.5% NaOCl, followed by saline and QMiX. The dentin surfaces were subjected to TOF-SIMS spectra analysis. Longitudinal sections of dentin blocks were then exposed and subjected to TOF-SIMS analysis. All samples and analysis were performed in triplicate for confirmation. TOF-SIMS analysis of group 1 revealed an irregular precipitate, containing PCA and CHX breakdown products, on the dentin surfaces, occluding and extending into the tubules. In TOF-SIMS analysis of group 2, no precipitates, including PCA, were detected on the dentin surface or in the tubules. Within the limitations of this study, precipitate containing PCA was formed in the tubules of dentin irrigated with NaOCl followed by CHX. No precipitates or PCA were detected in the tubules of dentin irrigated with NaOCl followed by saline and QMiX. Copyright © 2014 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

A comparative in vitro study investigating the occlusion and mineralization properties of commercial toothpastes in a four-day dentin disc model.

PubMed

Parkinson, Charles R; Willson, Richard J

2011-01-01

The objective of this study was to evaluate the relative level of dentin tubule occlusion and dentin mineralization conferred by a 5% w/w calcium sodium phosphosilicate (45S5)/1450 ppm fluoride toothpaste in comparison to a range of commercial toothpastes reported to occlude dentin tubules. Two separate experiments were employed to (i) determine the level of dentin tubule occlusion, and (ii) explore the change in dentin mineralization conferred by a number of marketed toothpastes and controls, following twice-daily brushing in a longitudinal, acid challenge-based, dentin disc model. In Study I, 192 bovine dentin discs, polished and etched in citric acid to provide a smooth dentin surface with patent tubules, were divided into eight treatment groups and subjected to brushing with one of seven test toothpastes or deionized water over four days. Prior to and between treatments, the dentin samples were stored in saliva. The test products were fluoridated toothpastes containing: calcium sodium phosphosilicate (45S5); strontium acetate; arginine/calcium carbonate; amine fluoride; calcium sulphate/diphosphate; stannous fluoride; casein stabilized amorphous calcium phosphate toothpaste; and a non-occluding negative control, deionized water. At the end of each treatment day (1 though 4), one group of samples was removed for scanning electron microscopy (SEM) analysis and graded on a categorical visual scale to assess the level of dentin tubule occlusion. A subset of samples from Study I was also cross-sectioned and examined using SEM. For the exploratory mineralization study (Study II), 120 dentin specimens were prepared as previously described and divided into four treatment groups consisting of A, C, F, and a tooth sealant varnish (I), and subjected to the treatment regimen described in Study I. The dentin samples were assessed for changes in surface microhardness using an indenter fitted with a Knoop probe and the level of dentin occlusion. In Study I, the 5% w/w calcium sodium phosphosilicate/1450 ppm fluoride-containing toothpaste (A), the stannous fluoride-containing toothpaste (F), and the strontium acetate-containing toothpaste (B) delivered the highest level of occlusion following four days of twice-daily brushing and a twice-daily acid challenge on days 3 and 4. Surface analysis of a subset of Study I samples, following four days of treatment, indicated that the 5% w/w calcium sodium phosphosilicate/1450 ppm fluoride-containing toothpaste formed a distinct layer at the surface of dentin. For Study II, surface microhardness analysis revealed that the 5% w/w calcium sodium phosphosilicate/1450 ppm fluoride-containing toothpaste (A) delivered significantly more surface hardening then the control or competitor toothpastes on days 2 and 4. Desensitizing toothpastes reported to operate by an occlusion mechanism have been observed to confer varying degrees of dentin tubule occlusion and dentin mineralization over four days in an acid challenge-based in vitro model. A 5% w/w calcium sodium phosphosilicate/1450 ppm fluoride-containing toothpaste was observed to impart a significant level of dentin tubule occlusion and surface hardening, and form durable occlusive deposits following four days of twice-daily brushing in vitro.

The effect of dentine surface preparation and reduced application time of adhesive on bonding strength.

PubMed

Saikaew, Pipop; Chowdhury, A F M Almas; Fukuyama, Mai; Kakuda, Shinichi; Carvalho, Ricardo M; Sano, Hidehiko

2016-04-01

This study evaluated the effects of surface preparation and the application time of adhesives on the resin-dentine bond strengths with universal adhesives. Sixty molars were cut to exposed mid-coronal dentine and divided into 12 groups (n=5) based on three factors; (1) adhesive: G-Premio Bond (GP, GC Corp., Tokyo, Japan), Clearfil Universal Bond (CU, Kuraray Noritake Dental Inc., Okayama, Japan) and Scotchbond Universal Adhesive (SB, 3M ESPE, St. Paul, MN, USA); (2) smear layer preparation: SiC paper ground dentine or bur-cut dentine; (3) application time: shortened time or as manufacturer's instruction. Fifteen resin-dentine sticks per group were processed for microtensile bond strength test (μTBS) according to non-trimming technique (1mm(2)) after storage in distilled water (37 °C) for 24h. Data were analyzed by three-way ANOVA and Dunnett T3 tests (α=0.05). Fractured surfaces were observed under scanning electron microscope (SEM). Another 12 teeth were prepared and cut into slices for SEM examination of bonded interfaces. μTBS were higher when bonded to SiC-ground dentine according to manufacturer's instruction. Bonding to bur-cut dentine resulted in significantly lower μTBS (p<0.000). Shortening the application time resulted in significantly lower bond strength for CU on SiC and GP on bur-cut dentine. SEM of fractured surfaces revealed areas with a large amount of porosities at the adhesive resin interface. This was more pronounced when adhesives were bonded with a reduced application time and on bur cut dentine. The performance of universal adhesives can be compromised on bur cut dentine and when applied with a reduced application time. Copyright © 2016 Elsevier Ltd. All rights reserved.

The effect of prophylaxis method on microtensile bond strength of indirect restorations to dentin.

PubMed

Soares, C J; Pereira, J C; Souza, S J B; Menezes, M S; Armstrong, S R

2012-01-01

The aim of this study was to evaluate the effect of different materials used for dentin prophylaxis on the microtensile bond strengths (μTBS) of adhesively cemented indirect composite restorations. Sixty bovine incisors had the buccal surface ground with wet #600-grit silicon carbide abrasive paper to obtain a flat exposed superficial dentin and were submitted to different prophylaxis protocols, as follows: 3% hydrogen peroxide (HydP); 0.12% chlorhexidine (Chlo); sodium bicarbonate jet (SodB); 50-μm aluminum oxide air abrasion (AirA); pumice paste (PumP), and control group-water spray (Cont). After prophylaxis protocols a resin composite block (3.0 mm × 5.0 mm × 5.0 mm) was adhesively cemented using dual resin cement (Rely X ARC). After 24 hours of water storage, specimens were serially sectioned perpendicular to the bonded interface into 1-mm-thick slices. Each specimen was trimmed with a diamond bur to an hourglass shape with a cross-sectional area of approximately 1.0 mm(2) at the bonded area. Specimens were tested (μTBS) at 0.5 mm/min using a universal testing machine. Scanning electron microscopy was used to examine the effects of prophylaxis techniques on dentin. Bond strength data (MPa) were analyzed by one-way analysis of variance and failure mode by Fisher test (α=0.05). μTBS data, means (SD), were (different superscripted letters indicate statistically significant differences): AirA, 25.2 (7.2)(a); PumP, 24.1 (7.8)(a); Chlo, 21.5 (5.6)(a); Cont, 20.6 (8.1)(a); HydP(,) 15.5 (7.6)(b); and SodB(,) 11.5 (4.4)(c). The use of aluminum oxide air abrasion, pumice paste, and chlorhexidine before acid etching did not significantly affect μTBS to dentin; however, the use of hydrogen peroxide and sodium bicarbonate jet significantly reduced μTBS.

Effect of hyaluronic acid on morphological changes to dentin surfaces and subsequent effect on periodontal ligament cell survival, attachment, and spreading.

PubMed

Mueller, Andrea; Fujioka-Kobayashi, Masako; Mueller, Heinz-Dieter; Lussi, Adrian; Sculean, Anton; Schmidlin, Patrick R; Miron, Richard J

2017-05-01

Hyaluronic acid (HA) is a natural constituent of connective tissues and plays an important role in their development, maintenance, and regeneration. Recently, HA has been shown to improve wound healing. However, no basic in vitro study to date has investigated its mode of action. Therefore, the purpose of this study was to examine morphological changes of dentin surfaces following HA coating and thereafter investigate the influence of periodontal ligament (PDL) cell survival, attachment, and spreading to dentin discs. HA was coated onto dentin discs utilizing either non-cross-linked (HA) or cross-linked (HA cl) delivery systems. Morphological changes to dentin discs were then assessed using scanning electron microscopy (SEM). Thereafter, human PDL cells were seeded under three in vitro conditions including (1) dilution of HA (1:100), (2) dilution of HA (1:10), and (3) HA coated directly to dentin discs. Samples were then investigated for PDL cell survival, attachment, and spreading using a live/dead assay, cell adhesion assay, and SEM imaging, respectively. While control dentin discs demonstrated smooth surfaces both at low and high magnification, the coating of HA altered surface texture of dentin discs by increasing surface roughness. HA cl further revealed greater surface texture/roughness likely due to the cross-linking carrier system. Thereafter, PDL cells were seeded on control and HA coated dentin discs and demonstrated a near 100 % survival rate for all samples demonstrating high biocompatibility of HA at dilutions of both 1:100 and 1:10. Interestingly, non-cross-linked HA significantly increased cell numbers at 8 h, whereas cross-linked HA improved cell spreading as qualitatively assessed by SEM. The results from the present study demonstrate that both carrier systems for HA were extremely biocompatible and demonstrated either improved cell numbers or cell spreading onto dentin discs. Future in vitro and animal research is necessary to further characterize the optimal delivery system of HA for improved clinical use. HA is a highly biocompatible material that may improve PDL cell attachment or spreading on dentin.

Effects of air polishing and an amino acid buffered hypochlorite solution to dentin surfaces and periodontal ligament cell survival, attachment, and spreading.

PubMed

Schmidlin, Patrick R; Fujioka-Kobayashi, Masako; Mueller, Heinz-Dieter; Sculean, Anton; Lussi, Adrian; Miron, Richard J

2017-06-01

The aim of this study is to examine morphological changes of dentin surfaces following air polishing or amino acid buffered hypochlorite solution application and to assess their influence on periodontal ligament (PDL) cell survival, attachment, and spreading to dentin discs in vitro. Bovine dentin discs were treated with either (i) Classic, (ii) Plus, or (iii) Perio powder (EMS). Furthermore, Perisolv® a hypochlorite solution buffered with various amino acids was investigated. Untreated dentin discs served as controls. Morphological changes to dentin discs were assessed using scanning electron microscopy (SEM). Human PDL cells were seeded onto the respectively treated discs, and samples were then investigated for PDL cell survival, attachment, and spreading using a live/dead assay, adhesion assay, and SEM imaging, respectively. Both control and Perisolv®-rinsed dentin discs demonstrated smooth surfaces at low and high magnifications. The Classic powders demonstrated the thickest coating followed by the Powder Plus. The Perio powder demonstrated marked alterations of dentin discs by revealing the potential to open dentinal tubules even before rinsing. Seeding of PDL cells demonstrated an almost 100 % survival rate on all samples demonstrating very high biocompatibility for all materials. Significantly higher PDL cell numbers were observed on samples treated with the Perio powder and the Perisolv® solution (approximately 40 % more cells; p < 0.05). SEM imaging revealed the potential for PDL cells to attach and spread on all surfaces. The results from the present study demonstrate that cell survival and spreading of PDL cells on root surfaces is possible following either air polishing or application with Perisolv®. Future in vitro and animal testing is necessary to further characterize the beneficial effects of either system in a clinical setting. The use of air polishing or application with Perisolv amino acid buffered hypochlorite solution was effective in treating root surfaces and allowed for near 100 % PDL cell survival, attachment, and spreading onto all root surfaces.

Morphological effects of MMPs inhibitors on the dentin bonding

PubMed Central

Li, He; Li, Tianbo; Li, Xiuying; Zhang, Zhimin; Li, Penglian; Li, Zhenling

2015-01-01

Matrix metalloproteinases (MMPs) have been studied extensively, and MMP inhibitors have been used as dental pretreatment agents prior to dentin bonding because they reduce collagen fiber degradation and improve bonding strength. However, morphologic characteristics of the collagen network after etching and of the post-adhesive dentin hybrid layers (DHL) after MMP inhibitors pretreatment have not been evaluated. Thus, we investigated demineralized dentin pretreated with chlorhexidine (CHX) and minocycline (MI) in an etch- and -rinse adhesive system with field emission scanning electron microscopy (FESEM) and immuno-gold labeling markers to observe the collagen network and DHL. FESEM revealed after CHX and MI, a demineralized dentin surface and improved collagen network formation, reduced collagen degradation, and distinct gold-labeling signals. Applying adhesive after either MMP inhibitor created a better dentin interface as evidenced by immuno-gold staining, better adhesive penetration, and higher DHL quality. With microtensile bond strength tests (µTBS) we estimated bonding strength using µTBS data. Immediate µTBS was enhanced with MMP inhibitor application to the bonding surface, and the CHX group was significantly different than non-treated etched surfaces, but no significant change was detected in the MI group. Surface micromorphology of the fractured dentin resin restoration showed that the CHX group had a better resin and dentin tube combination. Both MMP inhibitors created uniform resin coverage. Thus, morphologic results and µTBS data suggest that CHX and MI can inhibit MMP activity, improve immediate bonding strength, and enhance dentin bonding stability with an etch- and -rinse adhesive system. PMID:26379873

The effect of zoledronate-containing primer on dentin bonding of a universal adhesive.

PubMed

Zenobi, Walter; Feitosa, Victor Pinheiro; Moura, Maria Elisa Martins; D'arcangelo, Camillo; Rodrigues, Lidiany Karla de Azevedo; Sauro, Salvatore

2018-01-01

To evaluate the bonding ability and nanoleakage of a universal adhesive applied to dentin pre-treated using a zoledronate-containing primer (zol-primer) before and after mechanical load cycling. Flat dentin surfaces obtained from human molars were assigned to one of the following adhesion procedures (n=6): 1-Single Bond Universal (SBU) applied in etch-and-rinse mode; 2- SBU applied as etch-and-rinse after the application of zol-primer; 3- SBU applied in self-etch strategy; 4- SBU applied as self-etch after the use of zol-primer. Half of the specimens were processed for microtensile bond strength test after 24h, while the other half part was submitted to 200,000 mechanical cycles. Further specimens were silver-impregnated and assessed for interface nanoleakage by SEM. Data were analyzed with two-way ANOVA and Tukey's test (p<0.05). At 24h evaluation, the four groups presented similar bond strengths, whilst both groups bonded with etch-and-rinse technique showed significant bond strength reduction after mechanical load (p<0.05), with the highest drop in bond strength for the specimens pre-treated with the zol-primer. No negative effects were found for self-etch strategy (p>0.05) in microtensile test. Lower nanoleakage expression was observed for etch-and-rinse specimens treated with zol-primer. However, noteworthy reduction of adhesive layer thickness was observed when combining the zol-primer with the self-etch bonding approach. It can be concluded that zol-primer should not be used along with a universal adhesive in etch-and-rinse mode, but its application before self-etch application may provide less degradation of the resin-dentin interface. Copyright © 2017 Elsevier Ltd. All rights reserved.

The use of acetone to enhance the infiltration of HA nanoparticles into a demineralized dentin collagen matrix.

PubMed

Besinis, Alexandros; van Noort, Richard; Martin, Nicolas

2016-03-01

This study investigates the role of acetone, as a carrier for nano-hydroxyapatite (nano-HA) in solution, to enhance the infiltration of fully demineralized dentin with HA nanoparticles (NPs). Dentin specimens were fully demineralized and subsequently infiltrated with two types of water-based nano-HA solutions (one containing acetone and one without). Characterization of the dentin surfaces and nano-HA particles was performed using scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The surface wettability and infiltration capacity of the nano-HA solutions were quantified by means of contact angle measurements and energy dispersive X-ray spectroscopy (EDS), respectively. Contact angle measurements were taken at baseline and repeated at regular intervals to assess the effect of acetone. The P and Ca levels of infiltrated dentin specimens were measured and compared to sound dentin and non-infiltrated controls. The presence of acetone resulted in an eight-fold decrease in the contact angles of the nano-HA solutions recorded on the surface of demineralized dentin compared to nano-HA solutions without acetone (one-way ANOVA, p<0.05). Perfect wetting of the demineralized dentin surface was achieved 5min after the application of the nano-HA solution containing acetone. Infiltration of demineralized dentin with the nano-HA solution containing acetone restored the lost mineral content by 50%, whereas the mean mineralization values for P and Ca in dentin treated with the acetone-free nano-HA solution were less than 6%. Acetone was shown to act as a vehicle to enhance the capacity to infiltrate demineralized dentin with HA NPs. The successful infiltration of dentin collagen with HA NPs provides a suitable scaffold, whereby the infiltrated HA NPs have the potential to act as seeds that may initiate heterogenous mineral growth when exposed to an appropriate mineral-rich environment. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Morphological and chemical characterization of the dentin/resin cement interface produced with a self-etching primer.

PubMed

Walker, Mary P; Wang, Yong; Spencer, Paulette

2002-01-01

The purpose of this study was to analyze a resin cement/dentin interface by comparing the diffusion of a resin cement into dentin surfaces pretreated with a self-etching primer with or without pretreatment by conventional acid etching. Dentin surfaces of 8 unerupted human third molars were treated with a self-etch primer (Panavia 21) with or without conventional phosphoric acid pretreatment. Panavia 21 resin cement was applied according to manufacturer's instructions. Dentin/resin cement interface sections from each tooth were examined with scanning electron microscopy and micro-Raman spectroscopy. When the self-etch primer was used following conventional acid pretreatment, the resin cement did not penetrate to the depth of the zone of demineralized dentin, leaving a substantial area of exposed dentin matrix at the dentin/cement interface. In contrast, there was substantial resin cement diffusion throughout the demineralized dentin when the self-etch primer was used without acid etching pretreatment. The in vitro evaluation of resin cement penetration throughout the zone of demineralized dentin is an important step in identifying sites of exposed dentin matrix that may promote postoperative sensitivity and may leave the dentin/resin cement interface vulnerable to premature degradation under clinical conditions. In this study, the self-etch primer used alone produced substantial resin cement penetration and left no exposed dentin matrix at the dentin/resin cement interface.

The effect of silver fluoride and potassium iodide on the bond strength of auto cure glass ionomer cement to dentine.

PubMed

Knight, G M; McIntyre, J M; Mulyani

2006-03-01

Diamine silver fluoride (Ag(NH3)2F), referred to as AgF, has been shown to reduce the incidence of caries in primary dentitions. The clinical application of this material has been limited by staining associated with both teeth and restorative materials. The application of potassium iodide (KI) after AgF eliminates stain formation. There is a lack of information as to how the addition of AgF followed by KI may affect the bond strength to dentine. The purpose of this study was to compare the bond strengths of auto cure glass ionomer cement to dentine surfaces that had been treated with AgF and KI and without treatment. Ten recently extracted human third molars were embedded into methyl methacrylate resin and sliced to form a square block of exposed dentine surfaces. Each of the four surfaces were treated by one of the following procedures: (a) etching with 37 per cent phosphoric acid; (b) applying GC dentine conditioner; (c) etching, followed by application of AgF/KI then washing off the precipitate and air drying; and (d) etching, applying AgF/KI and air drying the reaction products on the surface. Fuji VII auto cure glass ionomer cement was bonded onto each sample and fracture tested. The dentine samples treated with AgF/KI followed by washing away the precipitate and air drying had bond strengths (2.83 MPa) not significantly different from samples that had been conditioned (2.40 MPa). Samples where the AgF/KI precipitate had been air dried onto the dentine surface had significantly lower bond strengths (1.49 MPa) than the washed samples. Samples that were etched had significantly lower bond strengths (1.91MPa) than the conditioned samples. This study found that the application of AgF/KI to etched dentine samples followed by washing off the precipitate, created bond strengths that were not significantly different to conditioned samples. Leaving the AgF/KI precipitate on the dentine surface significantly reduced the bond strength of auto cured glass ionomer cement to dentine. Washing away the reaction products and air drying is recommended as the clinical protocol for using AgF and KI on dentine surfaces prior to application of an auto cure glass ionomer cement.

Effect of EDTA, sodium hypochlorite, and chlorhexidine gluconate with or without surface modifiers on dentin microhardness.

PubMed

Aslantas, Eda E; Buzoglu, Hatice Dogan; Altundasar, Emre; Serper, Ahmet

2014-06-01

This study aimed to evaluate the effects of root canal irrigants on the microhardness of root canal dentin in the presence and absence of surface-modifying agents. Forty-eight root halves were prepared by longitudinal splitting of the distal roots of 24 freshly extracted mandibular human third molars and embedded in autopolymerizing acrylic resin, leaving the dentin surface exposed. After polishing, the microhardness values of the untreated dentin surfaces were recorded by using Vickers tester at the mid-root level. The root halves were randomly assigned to 6 groups composed of 8 samples each and treated for 5 minutes with one of the following irrigants: 17% EDTA, REDTA, 2% chlorhexidine gluconate (CHX), 2% CHX with surface modifiers (CHX-Plus), 6% NaOCl, or 6% NaOCl with surface modifiers (Chlor-XTRA). After surface treatment, dentin microhardness values were recorded at close proximity to the initial indentation areas. Experimental data were statistically analyzed by using the t test and one-way analysis of variance, followed by Tukey honestly significant difference test at α = 0.05. EDTA, REDTA, NaOCl, and Chlor-XTRA significantly decreased the microhardness of root dentin compared with intact controls (P < .05). The addition of surface modifiers to the irrigants did not affect the microhardness of the samples. Copyright © 2014 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

Resin-dentin interface of Scotchbond Multi-Purpose dentin adhesive.

PubMed

Griffiths, B M; Watson, T F

1995-08-01

To evaluate the interface between dentin, Scotchbond Multi-Purpose (SMP), and resin composite (Z100) using confocal fluorescence microscopy. Novel techniques were employed to view and record at video rate the application of the SMP primer and adhesive onto the dentin surface. The subsurface morphology of the dentin/restorative interface was also studied. To facilitate this study, the components of the adhesive system were labeled with fluorescent dyes. In an ideal situation, the primer and adhesive penetrated the dentin tubules, a distinct hybrid zone was formed and a thin layer of adhesive was observed at the interfacial region. However, the primed dentin surface was sensitive to disruption by the adhesive application brush during its placement, so that parts of the primer layer could be incorporated into the adhesive. This disruption could only be seen using confocal microscopy and a fluorescence labeling technique. Delamination of the primer layer was not observed when the adhesive film was thinned by air blowing. The application of an air stream to the cavity surface increased the penetration of the primer and adhesive along the dentin tubules, but also increased the thickness of the adhesive within irregularities on the cavity surface and at the cavity line angle. The cause of the problems in the handling properties of SMP may be the difference in viscosity between the two components (primer and adhesive) at the adhesive interface.

Surface temperature and thermal penetration depth of Nd:YAG laser applied to enamel and dentin

NASA Astrophysics Data System (ADS)

White, Joel M.; Neev, Joseph; Goodis, Harold E.; Berns, Michael W.

1992-06-01

The determination of the thermal effects of Nd:YAG laser energy on enamel and dentin is critical in understanding the clinical applications of caries removal and surface modification. Recently extracted non-carious third molars were sterilized with gamma irradiation. Calculus and cementum were removed using scaling instruments and 600 grit sand paper. The smear layer produced by sanding was removed with a solution of 0.5 M EDTA (pH 7.4) for two minutes. Enamel and dentin surfaces were exposed to a pulsed Nd:YAG laser with 150 microsecond(s) pulse duration. Laser energy was delivered to the teeth with a 320 micrometers diameter fiberoptic delivery system, for exposure times of 1, 10 and 30 seconds. Laser parameters varied from 0.3 to 3.0 W, 10 to 30 Hz and 30 to 150 mJ/pulse. Other conditions included applications of hot coffee, carbide bur in a dental air-cooled turbine drill and soldering iron. Infrared thermography was used to measure the maximum surface temperature on, and thermal penetration distance into enamel and dentin. Thermographic data were analyzed with a video image processor to determine the diameter of maximum surface temperature and thermal penetration distance of each treatment. Between/within statistical analysis of variance (p

Characterization of Chlorhexidine-Loaded Calcium-Hydroxide Microparticles as a Potential Dental Pulp-Capping Material.

PubMed

Priyadarshini, Balasankar M; Selvan, Subramanian T; Narayanan, Karthikeyan; Fawzy, Amr S

2017-06-22

This study explores the delivery of novel calcium hydroxide [Ca(OH)₂] microparticles loaded with chlorhexidine (CHX) for potential dental therapeutic and preventive applications. Herein, we introduce a new approach for drug-delivery to deep dentin-surfaces in the form of drug-loaded microparticles. Unloaded Ca(OH)₂ [Ca(OH)₂/Blank] and CHX-loaded/Ca(OH)₂ microparticles were fabricated by aqueous chemical-precipitation technique. The synthesized-microparticles were characterized in vitro for determination of surface-morphology, crystalline-features and thermal-properties examined by energy-dispersive X-ray scanning and transmission electron-microscopy (EDX-SEM/TEM), Fourier-transform infrared-spectroscopy (FTIR), X-ray diffraction (XRD), thermogravimetric analysis (TGA) and differential scanning-calorimetry (DSC). Time-related pH changes, initial antibacterial/biofilm-abilities and cytotoxicity of CHX-loaded/Ca(OH)₂ microparticles were evaluated. Microparticles were delivered to dentin-surfaces with subsequent SEM examination of treated dentin-substrates. The in vitro and ex vivo CHX-release profiles were characterized. Ca(OH)₂/Blank were hexagonal-shaped with highest z -average diameter whereas CHX-inclusion evidenced micro-metric spheres with distinguishable surface "rounded deposits" and a negative-shift in diameter. CHX:Ca(OH)₂/50 mg exhibited maximum encapsulation-efficiency with good antibacterial and cytocompatible properties. SEM examination revealed an intact layer of microparticles on exposed dentin-surfaces with retention of spherical shape and smooth texture. Microparticles loaded on dentin-surfaces showed prolonged release of CHX indicating substantial retention on dentin-substrates. This study validated the inherent-applicability of this novel drug-delivery approach to dentin-surfaces using micro-metric CHX-loaded/Ca(OH)₂ microparticles.

Surface properties and bond strength measurements of N-vinylcaprolactam (NVC)-containing glass-ionomer cements.

PubMed

Moshaverinia, Alireza; Chee, Winston W; Brantley, William A; Schricker, Scott R

2011-03-01

N-vinylcaprolactam (NVC)-containing glass ionomers are promising dental restorative materials with improved mechanical properties; however, little information is available on other physical characteristics of these types of modified glass ionomers, especially their surface properties. Understanding the surface characteristics and behavior of glass ionomers is important for understanding their clinical behavior and predictability as dental restorative materials. The purpose of this study was to investigate the effect of NVC-containing terpolymers on the surface properties and bond strength to dentin of GIC (glass-ionomer cement), and to evaluate the effect of NVC-containing terpolymer as a dentin conditioner. The terpolymer of acrylic acid (AA)-itaconic acid (IA)-N-vinylcaprolactam (NVC) with a molar ratio of 8:1:1 (AA:IA:NVC) was synthesized by free radical polymerization and characterized using nuclear magnetic resonance ((1)H-NMR) and Fourier transform infrared spectroscopy (FTIR). The synthesized terpolymer was used in glass-ionomer cement formulations (Fuji IX GP). Ten disc-shaped specimens (12 × 1 mm) were mixed and fabricated at room temperature. Surface properties (wettability) of modified cements were studied by contact angle measurements as a function of time. Work of adhesion values of different surfaces were also determined. The effect of NVC-modified polyacid on the bond strength of glass-ionomer cement to dentin was investigated. The mean data obtained from contact angle and bonding strength measurements were subjected to t test and 2-way ANOVA (α=.05). NVC-modified glass-ionomer cements showed significantly (P<.05) lower contact angles (46 degrees) and higher work of adhesion (W(A)=60.33 erg/cm(2)) in comparison to commercially available Fuji IX GP (57 degrees and W(A)=53.01 erg/cm(2)). The wettability of dentin surfaces conditioned with NVC-containing terpolymer was significantly higher (P<.05) (22 degrees, WA=73.77 erg/cm(2)) than dentin conditioned with GC dentin conditioner (29 degrees, W(A)=70.52 erg/cm(2)). The experimental cement also showed significantly higher values for shear bond strength to dentin (8.7 ±0.15 MPa after 1 month) when compared to the control group (8.4 ±0.13 MPa after 1 month). NVC-containing terpolymers may enhance the surface properties of GICs and increase their bond strength to the dentin. Furthermore, NVC-containing polyelectrolytes are better dentin conditioners than a commercially available dentin conditioner (GC dentin conditioner). Copyright © 2011 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Effect of gamma irradiation on the wear behavior of human tooth dentin.

PubMed

Qing, Ping; Huang, Shengbin; Gao, ShanShan; Qian, LinMao; Yu, HaiYang

2016-12-01

The objective of this study was to evaluate the effect of gamma irradiation on the wear behavior of human tooth dentin in terms of possible alterations in crystallinity, grain size, and composition. Human premolars (n = 19) were collected to obtain the perpendicular or parallel to the direction of the dentin tubule specimens. Each specimen was subjected to 60 Gy of gamma irradiation, in daily increments of 2 Gy. The nanoscratch tests were conducted. The scratch traces were observed via scanning electron microscope (SEM) and surface profilometer. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) were used to investigate the alteration of crystallography and chemical composition of dentin after irradiation. The change of surface microhardness (SMH) was also evaluated. The nanoscratch results showed that the friction coefficient of dentin after irradiation became higher, and the depths and widths of scratch were greater than that of dentin before irradiation. Additionally, irradiation decreased the crystallinity of dentin and induced the formation of bigger crystals. The carbonate/mineral ratio was increased. Furthermore, a significant reduction in microhardness after irradiation was observed. The main damage mechanisms consisted of the formation of delamination and crack in both the specimens cut perpendicular and parallel to tubule dentin after irradiation. Irradiation affected directly the wear behavior of tooth dentin, accompanied by the alterations in crystallography, chemical composition, and surface microhardness of dentin. This would help extend understanding the influence of irradiation on dentin and provide suggestions for selecting more suitable materials for irradiated tooth.

Effect of surface protection on the permeability of eroded dentin

PubMed Central

Martins, Vivian Leite; da Costa Ramos, Rodrigo Vitoria; Pimenta Lima, Max José; Correia de Araújo, Roberto Paulo; Cavalcanti, Andrea Nóbrega

2018-01-01

Context: Eroded dentin might present the opening of dentinal tubules, increasing permeability, and consequently dentinal hypersensitivity. Aims: This study evaluated the permeability of dentin surfaces exposed to different levels of erosion and methods of surface protection. Materials and Methods: Dentine samples (3 mm × 3 mm × 1 mm) were prepared from bovine incisors (n = 90) and divided into three groups according to the method of controlling erosive challenge: Negative control, topical fluoride application, and glass ionomer sealant. Subsequently, they were randomly divided into three subgroups according to the exposure of simulated gastric acid solution (Demineralization – DES) (5% HCl, pH = 2.2), and remineralization (RE); negative control, 9 and 18 cycles DES-RE. The dentin permeability was measured by assessing the hydraulic conductance (μl/min.cmH2O.cm2). Statistical analysis was performed by two-way ANOVA and Tukey's test. Results and Conclusions: Greater permeability was observed after 18 erosive cycles, followed by exposure to 9 cycles and negative control (P < 0.0001). The application of glass ionomer sealant resulted in a major reduction of the hydraulic conductivity, regardless of the erosive challenge. Control groups and topical fluoride application showed similar results. In conclusion, the severity of erosive challenge contributed to the increase of dentin permeability. Besides, the glass ionomer sealant was the only protection agent that promoted significant effects in dentin permeability. PMID:29628641

Potential effects of tooth-brushing on human dentin wear following exposure to acidic soft drinks.

PubMed

Choi, S; Park, K-H; Cheong, Y; Moon, S W; Park, Y-G; Park, H-K

2012-08-01

This study used scanning electron microscopy and atomic force microscopy to examine the short-term potential effects of brushing time and the start-time of tooth-brushing after demineralization on primary dentin wear in vitro. Thirty-six noncarious primary central incisors were assigned to 12 experimental groups. Exposure to cola drinks was used to initiate the demineralization process. Three brushing times (5, 15 and 30 s) and four start-times of brushing (0, 30, 60 and 120 min) after an erosive attack were used for the abrasion process. Tooth-brushing the softened dentin surface led to increases in the open tubular fraction and microstructural changes on the dentin surface. Brushing immediately after exposure to cola resulted in the greatest irreversible dentin loss, whereas brushing 60 or 120 min after pretreatment resulted in the least irreversible dentin loss. However, brushing time had no effect on the irreversible loss of dentin wear. Based on these experimental results, tooth-brushing should be performed at least 60 min after consuming a cola drink to achieve the desired tooth cleaning and avoid the introduction of surface lesions on dentin. © 2012 The Authors Journal of Microscopy © 2012 Wadsworth Center, New York State Department of Health.

Influence of air-powder polishing on bond strength and surface-free energy of universal adhesive systems.

PubMed

Tamura, Yukie; Takamizawa, Toshiki; Shimamura, Yutaka; Akiba, Shunsuke; Yabuki, Chiaki; Imai, Arisa; Tsujimoto, Akimasa; Kurokawa, Hiroyasu; Miyazaki, Masashi

2017-11-29

The influences of air-powder polishing with glycine or sodium bicarbonate powders on shear bond strengths (SBS) and surface-free energies of universal adhesives were examined. Scotchbond Universal Adhesive (SU, 3M ESPE), G-Premio Bond (GP, GC), Adhese Universal (AU, Ivoclar Vivadent), and All-Bond Universal (AB, Bisco) were used in this study. Bovine dentin surfaces were air polished with glycine or sodium bicarbonate powders prior to the bonding procedure, and resin pastes were bonded to the dentin surface using universal adhesives. SBSs were determined after 24-h storage in distilled water at 37°C. Surface-free energy was then determined by measuring contact angles using three test liquids on dentin surfaces. Significantly lower SBSs were observed for dentin that was air-powder polished and surface-free energies were concomitantly lowered. This study indicated that air-powder polishing influences SBSs and surface-free energies. However, glycine powder produced smaller changes in these surface parameters than sodium bicarbonate.

Optothermal transfer simulation in laser-irradiated human dentin.

PubMed

Moriyama, Eduardo H; Zangaro, Renato A; Lobo, Paulo D C; Villaverde, Antonio Balbin; Pacheco, Marcos T; Watanabe, Ii-Sei; Vitkin, Alex

2003-04-01

Laser technology has been studied as a potential replacement to the conventional dental drill. However, to prevent pulpal cell damage, information related to the safety parameters using high-power lasers in oral mineralized tissues is needed. In this study, the heat distribution profiles at the surface and subsurface regions of human dentine samples irradiated with a Nd:YAG laser were simulated using Crank-Nicolson's finite difference method for different laser energies and pulse durations. Heat distribution throughout the dentin layer, from the external dentin surface to the pulp chamber wall, were calculated in each case, to investigate the details of pulsed laser-hard dental tissue interactions. The results showed that the final temperature at the pulp chamber wall and at the dentin surface are strongly dependent on the pulse duration, exposure time, and the energy contained in each pulse.

A 2-year in vitro evaluation of a chlorhexidine-containing acid on the durability of resin-dentin interfaces.

PubMed

Stanislawczuk, Rodrigo; Reis, Alessandra; Loguercio, Alessandro D

2011-01-01

This study evaluated the effect of 2% chlorhexidine-containing acid (Ac/CHX) and 2% chlorhexidine digluconate solution (CHX) on immediate (IM) and 2-year (2Y) resin-dentin bond strength (BS) and silver nitrate uptake (SNU) for two simplified etch-and-rinse adhesives. Forty-two caries-free extracted molars had a flat dentin surface exposed. In the control groups (groups 1), the surfaces were acid etched with conventional phosphoric acid and the adhesives Prime&Bond NT (PB) or Adper Single Bond 2 (SB) was applied after rinsing, drying and rewetting with water. In groups 2, Ac/CHX groups the adhesives were applied in a similar manner; however a 2% CHX-containing acid was previously applied. In groups 3, the adhesives were applied according to the control group; however the rewetting procedure was performed with an aqueous solution of 2% CHX for 60s. Composite build-ups were constructed incrementally and microtensile specimens (0.8mm(2)) were prepared for microtensile bond strength testing in the IM or 2Y periods at 0.5mm/min. For SNU, 2 bonded sticks from each tooth were coated with nail varnish, placed in the silver nitrate, polished down with SiC papers and analysed by EDX-SEM. The data from each adhesive was submitted to a two-way repeated measures ANOVA and Tukey's test (α=0.05). After 2Y, significant reductions of BS were observed for both adhesives in the control group (p<0.05). In Ac/CHX or CHX groups the BS remained stable for both systems. SNU was more evident in the control than in the experimental groups (p<0.05) both in IM and 2Y periods. The use of CHX in an aqueous solution or associated with the acid conditioner was effective to reduce the degradation of dentin bonds over a 2-year period. The addition of CHX digluconate in the acidic conditioner may be an excellent tool to increase the long-term stability of collagens fibrils within the hybrid layer against host-derived metalloproteinases without the need for additional steps for the bonding protocol. Copyright © 2010 Elsevier Ltd. All rights reserved.

Structural modifications induced in dentin by femtosecond laser

NASA Astrophysics Data System (ADS)

Le, Quang-Tri; Bertrand, Caroline; Vilar, Rui

2016-12-01

The structural and chemical modifications induced in dentin by ultrafast laser ablation were studied. The laser experiments were performed with a Yb:KYW chirped-pulse-regenerative amplification laser system (560-fs pulse duration, 1030-nm radiation wavelength), fluences in the range 2 to 14 J/cm2, 1-kHz pulse repetition rate, and 5-mm/s scanning speed. The ablation surfaces were characterized by scanning electron microscopy and Fourier transform infrared spectroscopy. The ablation surfaces produced with 2 J/cm2 presented an irregular morphology with exposed dentinal tubules and no evidence of thermal effects. For 7 and 14 J/cm2, the ablation surfaces were covered by a layer of redeposited ablation debris, consisting mainly of amorphous calcium phosphate. This layer is weakly adherent to the underlying tissue and can be easily removed by ultrasonication, revealing a surface with a morphology similar to the one obtained with 2 J/cm2. The constitution of the dentin ablation surfaces is similar to the constitution of pristine dentin, showing that, within this fluence range, the laser treatment does not significantly modify the structure and constitution of dentin. The results achieved suggest an ablation mechanism where collagen is preferentially decomposed by the laser radiation, reducing the tissue cohesive strength and leading, ultimately, to its ablation.

Characterization of Chlorhexidine-Loaded Calcium-Hydroxide Microparticles as a Potential Dental Pulp-Capping Material

PubMed Central

Priyadarshini, Balasankar M.; Selvan, Subramanian T.; Narayanan, Karthikeyan; Fawzy, Amr S.

2017-01-01

This study explores the delivery of novel calcium hydroxide [Ca(OH)2] microparticles loaded with chlorhexidine (CHX) for potential dental therapeutic and preventive applications. Herein, we introduce a new approach for drug-delivery to deep dentin-surfaces in the form of drug-loaded microparticles. Unloaded Ca(OH)2 [Ca(OH)2/Blank] and CHX-loaded/Ca(OH)2 microparticles were fabricated by aqueous chemical-precipitation technique. The synthesized-microparticles were characterized in vitro for determination of surface-morphology, crystalline-features and thermal-properties examined by energy-dispersive X-ray scanning and transmission electron-microscopy (EDX-SEM/TEM), Fourier-transform infrared-spectroscopy (FTIR), X-ray diffraction (XRD), thermogravimetric analysis (TGA) and differential scanning-calorimetry (DSC). Time-related pH changes, initial antibacterial/biofilm-abilities and cytotoxicity of CHX-loaded/Ca(OH)2 microparticles were evaluated. Microparticles were delivered to dentin-surfaces with subsequent SEM examination of treated dentin-substrates. The in vitro and ex vivo CHX-release profiles were characterized. Ca(OH)2/Blank were hexagonal-shaped with highest z-average diameter whereas CHX-inclusion evidenced micro-metric spheres with distinguishable surface “rounded deposits” and a negative-shift in diameter. CHX:Ca(OH)2/50 mg exhibited maximum encapsulation-efficiency with good antibacterial and cytocompatible properties. SEM examination revealed an intact layer of microparticles on exposed dentin-surfaces with retention of spherical shape and smooth texture. Microparticles loaded on dentin-surfaces showed prolonged release of CHX indicating substantial retention on dentin-substrates. This study validated the inherent-applicability of this novel drug-delivery approach to dentin-surfaces using micro-metric CHX-loaded/Ca(OH)2 microparticles. PMID:28952538

Grinding efficiency of abutment tooth with both dentin and core composite resin on axial plane.

PubMed

Miho, Otoaki; Sato, Toru; Matsukubo, Takashi

2015-01-01

The purpose of this study was to evaluate grinding efficiency in abutment teeth comprising both dentin and core composite resin in the axial plane. Grinding was performed over 5 runs at two loads (0.5 or 0.25 N) and two feed rates (1 or 2 mm/sec). The grinding surface was observed with a 3-D laser microscope. Tomographic images of the grinding surfaces captured perpendicular to the feed direction were also analyzed. Using a non-ground surface as a reference, areas comprising only dentin, both dentin and core composite resin, or only core composite resin were analyzed to determine the angle of the grinding surface. Composite resins were subjected to the Vickers hardness test and scanning electron microscopy. Data were statistically analyzed using a one-way analysis of variance and multiple comparison tests. Multiple regression analysis was performed for load, feed rate, and Vickers hardness of the build-up material depending on number of runs. When grinding was performed at a constant load and feed rate, a greater grinding angle was observed in areas comprising both dentin and composite resin or only composite resin than in areas consisting of dentin alone. A correlation was found between machinability and load or feed rate in areas comprising both dentin and composite resin or composite resin alone, with a particularly high correlation being observed between machinability and load. These results suggest that great caution should be exercised in a clinical setting when the boundary between the dentin and composite resin is to be ground, as the angle of the grinding surface changes when the rotating diamond point begins grinding the composite resin.

Shear bond strength of a new one-bottle dentin adhesive.

PubMed

Swift, E J; Bayne, S C

1997-08-01

To test the shear bond strength of a new adhesive, 3M Single Bond, to dentin surfaces containing different degrees of moisture. Two commercially available one-bottle adhesives (Prime & Bond, One-Step) and a conventional three-step system (Scotchbond Multi-Purpose Plus) were included for comparison. 120 bovine teeth were embedded in acrylic and the labial surfaces were polished to 600 grit to create standardized dentin surfaces for testing. Resin composite was bonded to dentin using a gelatin capsule technique. Four adhesive systems were evaluated with three different degrees of surface moisture (moist, wet, and overwet). Shear bond strengths of adhesives to dentin were determined using a universal testing machine and analyzed by ANOVA and Tukey's post hoc tests. Single Bond had mean shear bond strengths of 19.2, 23.2 and 20.3 MPa to moist, wet, and overwet dentin, respectively. Bond strengths of the three-component system Scotchbond Multi-Purpose Plus ranged from 23.1 to 25.3 MPa, but were not significantly higher than the values for Single Bond. Prime & Bond had bond strengths similar to those of Single Bond, but One-Step had significantly lower bond strengths (P < 0.05) in the wet and overwet conditions.

A safety study in vitro for the effects of an in-office bleaching system on the integrity of enamel and dentine.

PubMed

Sulieman, M; Addy, M; Macdonald, E; Rees, J S

2004-09-01

The aim of this study was to investigate safety concerns with bleaching procedures by studying the effects of a high concentration hydrogen peroxide (HP) in-surgery bleaching product on enamel and dentine. Flat enamel and dentine samples embedded in epoxy resin were prepared from human third molar teeth. Erosion of enamel: groups of enamel samples were treated with 35% HP then citric acid (CA) or brushing with toothpaste or CA alone and water alone. Enamel Loss was measured using a profilometer. Abrasion/erosion of dentine: groups of dentine specimens were treated as follows: Group 1--brushed with water for 30 min. Group 2--brushed with 35% HP for 30 min. Group 3--power bleached for 30 min and then Group 4--brushed with toothpaste for 1 minute. Group 5--water soaked for 30 min followed by brushing with toothpaste for 1 min. Group 6--orange juice soaked for 30 min followed by brushing with toothpaste for 1 min. Treatment effects were measured using a profilometer. Hardness tests: enamel and dentine specimens were hardness tested using a Wallace indenter prior to and post bleaching. Scanning Electron Microscopy: enamel and dentine specimens were taped and the exposed tissue treated with 35% HP and then studied under scanning electronmicroscopy (SEM). Enamel erosion: bleaching enamel samples had no measurable effect on enamel. Pre-bleaching had no significant effect on subsequent CA erosion or brushing. Abrasion/erosion of dentine: no significant differences were found between treatments 1-5 with little change from baseline detected. Orange juice (Group 6) produced considerable and significantly more erosion than other treatments. Hardness tests: there were no significant changes in hardness values for enamel and dentine. SEM: there was no evidence of any topographical changes to either enamel or dentine. Using one of the highest concentrations of HP for tooth bleaching procedures and maximum likely peroxide exposure, there was no evidence of deleterious effects on enamel or dentine. It must be assumed that studies which reported adverse effects on enamel and or dentine of bleaches reflect not the bleach itself but the pH of the formulation used.

Characterization of transparent dentin in attrited teeth using optical coherence tomography.

PubMed

Mandurah, Mona M; Sadr, Alireza; Bakhsh, Turki A; Shimada, Yasushi; Sumi, Yasunori; Tagami, Junji

2015-05-01

Attrition and wear of tooth surface occur with aging and result in loss of enamel, with exposure and histological changes in dentin. Dealing with attrited teeth and restoration of the lost tissue are clinically challenging. The main objective of this study is to characterize the exposed transparent dentin in the occlusal surface of attrited teeth by optical coherence tomography (OCT). Naturally attrited, extracted human teeth with occlusal-transparent dentin were investigated in comparison to sound and carious teeth. The teeth were subjected to OCT imaging and then cross-sectioned and polished. OCT B-scans were compared to light microscopy images of the same cross section. In OCT images, some changes were evident at the transparent dentin in attrited teeth. An OCT attenuation coefficient parameter (μ t) was derived based on the Beer-Lambert law as a function of backscatter signal slope. The mean values of μ t were 1.05 ± 0.3, 2.23 ± 0.4, and 0.61 ± 0.27 mm(-1) for sound, carious, and transparent dentins, respectively. One-way ANOVA with Tukey's post-hoc showed a significant difference between groups (p < 0.05). Physiological changes in transparent dentin that involve deposition of mineral casts in the dentinal tubules lead to lower attenuation of OCT signal. OCT has a potential role to detect transparent dentin on the surface of attrited teeth and can be used in the future as a clinical adjunct tool.

Influence of Er,Cr:YSGG laser treatment on the microtensile bond strength of adhesives to dentin.

PubMed

Cardoso, Marcio Vivan; Coutinho, Edurado; Ermis, R Banu; Poitevin, André; Van Landuyt, Kirsten; De Munck, Jan; Carvalho, Rubens C R; Lambrechts, Paul; Van Meerbeek, Bart

2008-02-01

In light of the concept of minimally invasive dentistry, erbium lasers have been considered as an alternative technique to the use of diamond burs for cavity preparation. The purpose of this study was to assess the bonding effectiveness of adhesives to Er,Cr:YSGG laser-irradiated dentin using irradiation settings specific for cavity preparation. Fifty-four midcoronal dentin surfaces, obtained from sound human molars, were irradiated with an Er,Cr:YSGG laser or prepared with a diamond bur using a high-speed turbine. One etch-and-rinse (Optibond FL/Kerr) and three self-etching adhesives (Adper Prompt L-Pop/3M ESPE, Clearfil SE Bond/Kuraray, and Clearfil S3 Bond/Kuraray) were used to bond the composite to dentin. The microtensile bond strength (microTBS) was determined after 24 h of storage in water at 37 degrees C. The Kruskal-Wallis test was used to determine pairwise statistical differences (p < 0.05). Prepared dentin surfaces, adhesive interfaces, and failure patterns were analyzed using a stereomicroscope and Field-emission gun Scanning Electron Microscopy (Feg-SEM). Significantly lower microTBS was observed to laser-irradiated than to bur-cut dentin (p < 0.05), irrespective of the adhesive employed. Feg-SEM photomicrographs of lased dentin revealed an imbricate patterned substrate and the presence of microcracks at the dentin surface. Morphological alterations produced by Er,Cr:YSGG laser-irradiation adversely influence the bonding effectiveness of adhesives to dentin.

Chemical treatment of the intra-canal dentin surface: a new approach to modify dentin hydrophobicity

PubMed Central

GAITAN-FONSECA, Cesar; COLLART-DUTILLEUL, Pierre-Yves; SEMETEY, Vincent; ROMIEU, Olivier; CRUZ, Roel; FLORES, Hector; CUISINIER, Frédéric; PÉREZ, Elías; POZOS-GUILLEN, Amaury

2013-01-01

Objective: This study evaluated the hydrophobicity of dentin surfaces that were modified through chemical silanization with octadecyltrichlorosilane (OTS). Material and Methods: An in vitro experimental study was performed using 40 human permanent incisors that were divided into the following two groups: non-silanized and silanized. The specimens were pretreated and chemically modified with OTS. After the chemical modification, the dentin hydrophobicity was examined using a water contact angle measurement (WCA). The effectiveness of the modification of hydrophobicity was verified by the fluid permeability test (FPT). Results and Conclusions: Statistically significant differences were found in the values of WCA and FPT between the two groups. After silanization, the hydrophobic intraradicular dentin surface exhibited in vitro properties that limit fluid penetration into the sealed root canal. This chemical treatment is a new approach for improving the sealing of the root canal system. PMID:23559114

An in vitro assessment of the effect of load and pH on wear between opposing enamel and dentine surfaces.

PubMed

Ranjitkar, Sarbin; Kaidonis, John A; Townsend, Grant C; Vu, Anh M; Richards, Lindsay C

2008-11-01

Previous in vitro studies have described the wear characteristics of specimens in which enamel has been opposed to enamel and dentine opposed to dentine. The aim of this study was to assess the characteristics of wear between specimens in which enamel was opposed to dentine at loads simulating attrition and at pH values simulating different erosive environments. It was hypothesized that enamel would wear more slowly than dentine under all conditions. Opposing enamel and dentine specimens from 57 human third molar teeth were worn in electromechanical machines with various loads (32, 62 and 100 N) and lubricants (pH 1.2, 3.0 and 6.1). Tooth wear was quantified by measuring reduction in dentine volume over time using a 3D profilometer. Qualitative assessment was also carried out using scanning electron microscopy. Dentine wear increased with increasing load, and dentine wear was faster at pH 1.2 than at pH 3.0 or 6.1 for all loads tested. Interestingly, enamel wore more rapidly than dentine at pH 1.2 under all loads. At pH values of 3.0 and 6.1, enamel wear rates were not measurably different from zero and they were less than wear rates for opposing dentine specimens at all loads. Micrographic assessment showed extensive surface destruction of dentine wear facets due to erosion at pH 1.2. Dentine wear facets were smoother at pH 3.0 that at pH 6.1. When enamel wears against dentine in an acidic environment enamel will wear more rapidly at very low pH, while under less acid conditions dentine will wear faster than enamel.

Long-Term Bond Strength of Two Benzalkonium Chloride-Modified Adhesive Systems to Eroded Dentin

PubMed Central

Lussi, Adrian; Peutzfeldt, Anne

2017-01-01

This study investigated the effect of benzalkonium chloride (BAC) modification of two adhesive systems on long-term bond strength to normal and artificially eroded dentin. A total of 128 extracted human molars were sectioned and the buccal and oral surfaces of each molar were ground until the dentin. One half was left untreated (normal dentin) while the other half underwent artificial erosion. Resin composite was bonded to the buccal or oral surface following treatment with Adper Scotchbond 1XT or OptiBond FL without or with 1% BAC incorporation. Shear bond strength (SBS) was measured after 24 h (100% humidity, 37°C) or 1 year (tap water, 37°C). SBS results were statistically analyzed (α = 0.05). SBS was significantly lower to artificially eroded dentin than to normal dentin (p < 0.001). Storage for 1 year had no effect on SBS to normal dentin but led to a significant decrease in SBS to artificially eroded dentin (p < 0.001). BAC incorporation decreased the 24 h SBS to normal dentin (p = 0.018), increased the 24 h SBS to eroded dentin (p = 0.001), and had no effect on the 1-year SBS for either substrate. Consequently, BAC incorporation did not improve bond durability. PMID:28875148

Effect of pulsed Nd:YAG on dentin morphological changes

NASA Astrophysics Data System (ADS)

Moriyama, Eduardo H.; Zangaro, Renato A.; Villaverde, Antonio G. J. B.; Watanabe-Sei, Ii; Munin, Egberto; Sasaki, Luis H.; Otsuka, Daniel K.; Lobo, Paulo D. d. C.; Pacheco, Marcos T. T.; Junior, Durval R.

2002-06-01

Infrared lasers have been used for several clinical applications in dentistry, including laser ablation, oral surgeries and dentin hypersensitivity treatment. Despite of dentin low absorption coefficient in the near infrared spectrum, Nd:YAG laser radiation ((lambda) = 1064 nm) is able to melt the human dentin surface resulting in dentin tubules closure that can suppress the symptoms of dentin hypersensitivity pathology. Objectives: This study aims to analyze, through SEM technique, the morphological changes in dentin surface after Nd:YAG laser irradiation using different parameters in energy distribution. Materials and Methods: In this study sixteen human dentin samples were submitted to Nd:YAG laser radiation using a total energy of 900mJ distributed in one, two, three or six laser pulses with energy for each pulse of 900, 450, 300 or 150 mJ respectively. All the samples were irradiated with laser pulse width of 90ms, pulse intervals of 300 ms and spot size area of 0,005 cm2. Results: SEM analysis suggests that differences in energy distribution results in morphological differences even though the same energy is used for all the samples.

Fractography and fracture toughness of human dentin.

PubMed

Yan, J; Taskonak, B; Mecholsky, J J

2009-10-01

Dentin, the mineralized tissue forming the bulk of the tooth, serves as an energy-absorbing cushion for the hard, wear-resistant enamel and protects the inner soft tissues. Several studies used fracture mechanics methods to study the fracture toughness of dentin. However, all of them utilized precracks and cannot be used to estimate the intrinsic critical flaw size of dentin. We applied quantitative fractography to study the fracture pattern and fracture toughness of human dentin. Sixteen specimens were prepared from the coronal dentin and fractured in three-point flexure. Fracture surfaces were examined using a scanning electron microscope and the fracture toughness was calculated using a fracture mechanics equation. It was found that human dentin has a fracture surface similar to those of brittle materials. Twist hackle markings were observed and were used to identify the fracture origins. Average fracture toughness of all specimens was found to be 2.3 MPa m(1/2) and the average critical flaw size was estimated to 120 mum. It is suggested that fractography is a promising technique in analyzing the fracture of dentin under catastrophic failure.

Effect of overglazed and polished surface finishes on the compressive fracture strength of machinable ceramic materials.

PubMed

Asai, Tetsuya; Kazama, Ryunosuke; Fukushima, Masayoshi; Okiji, Takashi

2010-11-01

Controversy prevails over the effect of overglazing on the fracture strength of ceramic materials. Therefore, the effects of different surface finishes on the compressive fracture strength of machinable ceramic materials were investigated in this study. Plates prepared from four commercial brands of ceramic materials were either surface-polished or overglazed (n=10 per ceramic material for each surface finish), and bonded to flat surfaces of human dentin using a resin cement. Loads at failure were determined and statistically analyzed using two-way ANOVA and Bonferroni test. Although no statistical differences in load value were detected between polished and overglazed groups (p>0.05), the fracture load of Vita Mark II was significantly lower than those of ProCAD and IPS Empress CAD, whereas that of IPS e.max CAD was significantly higher than the latter two ceramic materials (p<0.05). It was concluded that overglazed and polished surfaces produced similar compressive fracture strengths irrespective of the machinable ceramic material tested, and that fracture strength was material-dependent.

Influence of multi-wavelength laser irradiation of enamel and dentin surfaces at 0.355, 2.94, and 9.4 μm on surface morphology, permeability, and acid resistance.

PubMed

Chang, Nai-Yuan N; Jew, Jamison M; Simon, Jacob C; Chen, Kenneth H; Lee, Robert C; Fried, William A; Cho, Jinny; Darling, Cynthia L; Fried, Daniel

2017-12-01

Ultraviolet (UV) and infrared (IR) lasers can be used to specifically target protein, water, and mineral, respectively, in dental hard tissues to produce varying changes in surface morphology, permeability, reflectivity, and acid resistance. The purpose of this study was to explore the influence of laser irradiation and topical fluoride application on the surface morphology, permeability, reflectivity, and acid resistance of enamel and dentin to shed light on the mechanism of interaction and develop more effective treatments. Twelve bovine enamel surfaces and twelve bovine dentin surfaces were irradiated with various combinations of lasers operating at 0.355 (Freq.-tripled Nd:YAG (UV) laser), 2.94 (Er:YAG laser), and 9.4 μm (CO 2 laser), and surfaces were exposed to an acidulated phosphate fluoride gel and an acid challenge. Changes in the surface morphology, acid resistance, and permeability were measured using digital microscopy, polarized light microscopy, near-IR reflectance, fluorescence, polarization sensitive-optical coherence tomography (PS-OCT), and surface dehydration rate measurements. Different laser treatments dramatically influenced the surface morphology and permeability of both enamel and dentin. CO 2 laser irradiation melted tooth surfaces. Er:YAG and UV lasers, while not melting tooth surfaces, showed markedly different surface roughness. Er:YAG irradiation led to significantly rougher enamel and dentin surfaces and led to higher permeability. There were significant differences in acid resistance among the various treatment groups. Surface dehydration measurements showed significant changes in permeability after laser treatments, application of fluoride and after exposure to demineralization. CO 2 laser irradiation was most effective in inhibiting demineralization on enamel while topical fluoride was most effective for dentin surfaces. Lasers Surg. Med. 49:913-927, 2017. © 2017 Wiley Periodicals, Inc. © 2017 Wiley Periodicals, Inc.

In vivo effect of a self-etching primer on dentin.

PubMed

Milia, E; Lallai, M R; García-Godoy, F

1999-08-01

To determine the ultrastructural aspects of the dentin collagen area in the cavity preparation floor produced in vivo after phosphoric acid acid-etching or after using Clearfil Liner Bond 2 self-etching primer (LB2 Primer). Twenty-four non-carious third molars scheduled for extraction from young adult patients (16-30 years old) were used. Conventional Class I cavities (+/- 2 mm deep) were prepared on the occlusal surfaces of all teeth using a cylindrical diamond bur on a high-speed handpiece with copious water spray. To avoid dehydration of the dentin, the smear layer-covered dentin was briefly air-dried for 2 seconds. Cavities were assigned at random to the following groups: Group A: Dentin etched for 15 seconds with 34% phosphoric acid, rinsed for 20 seconds and then briefly air-dried for 2 seconds with oil-free compressed air leaving the surfaces slightly moist. Group B: LB2 Primer was applied to the cavity surfaces for 30 seconds and then briefly air-dried to remove the solvent. Group C: The untreated dentin smear layer was used as a control. In all three groups, the cavities were filled incrementally with a resin-based composite (APX), light curing every increment for 40 seconds. After 30 minutes, the teeth were extracted atraumatically and the samples immediately prepared for evaluation with the transmission electron microscope. The use of a self-etching primer did not produce significant morphological changes in the moist dentin substrate. Adverse morphological conditions where observed when there was an excess water on the dentin surface. Phosphoric acid altered the collagen more severely than the self-etching primer.

Influence of light intensity on surface free energy and dentin bond strength of core build-up resins.

PubMed

Shimizu, Y; Tsujimoto, A; Furuichi, T; Suzuki, T; Tsubota, K; Miyazaki, M; Platt, J A

2015-01-01

We examined the influence of light intensity on surface free energy characteristics and dentin bond strength of dual-cure direct core build-up resin systems. Two commercially available dual-cure direct core build-up resin systems, Clearfil DC Core Automix with Clearfil Bond SE One and UniFil Core EM with Self-Etching Bond, were studied. Bovine mandibular incisors were mounted in acrylic resin and the facial dentin surfaces were wet ground on 600-grit silicon carbide paper. Adhesives were applied to dentin surfaces and cured with light intensities of 0 (no irradiation), 200, 400, and 600 mW/cm(2). The surface free energy of the adhesives (five samples per group) was determined by measuring the contact angles of three test liquids placed on the cured adhesives. To determine the strength of the dentin bond, the core build-up resin pastes were condensed into the mold on the adhesive-treated dentin surfaces according to the methods described for the surface free energy measurement. The resin pastes were cured with the same light intensities as those used for the adhesives. Ten specimens per group were stored in water maintained at 37°C for 24 hours, after which they were shear tested at a crosshead speed of 1.0 mm/minute in a universal testing machine. Two-way analysis of variance (ANOVA) and a Tukey-Kramer test were performed, with the significance level set at 0.05. The surface free energies of the adhesive-treated dentin surfaces decreased with an increase in the light intensity of the curing unit. Two-way ANOVA revealed that the type of core build-up system and the light intensity significantly influence the bond strength, although there was no significant interaction between the two factors. The highest bond strengths were achieved when the resin pastes were cured with the strongest light intensity for all the core build-up systems. When polymerized with a light intensity of 200 mW/cm(2) or less, significantly lower bond strengths were observed. CONClUSIONS: The data suggest that the dentin bond strength of core build-up systems are still affected by the light intensity of the curing unit, which is based on the surface free energy of the adhesives. On the basis of the results and limitations of the test conditions used in this study, it appears that a light intensity of >400 mW/cm(2) may be required for achieving the optimal dentin bond strength.

Effects of N-vinylpyrrolidone (NVP) containing polyelectrolytes on surface properties of conventional glass-ionomer cements (GIC).

PubMed

Moshaverinia, Alireza; Roohpour, Nima; Ansari, Sahar; Moshaverinia, Maryam; Schricker, Scott; Darr, Jawwad A; Rehman, Ihtesham U

2009-10-01

It has been found that polyacids containing an N-vinylpyrrolidinone (NVP) comonomer produces a glass inomer cement with improved mechanical and handling properties. The objective of this study was to investigate the effect of NVP modified polyelectrolytes on the surface properties and shear bond strength to dentin of glass ionomer cements. Poly(acrylic acid (AA)-co-itaconic acid (IA)-co-N-vinylpyrrolidone) was synthesized by free radical polymerization. The terpolymer was characterized using (1)H NMR, FTIR spectroscopy and viscometry for solution properties. The synthesized polymers were used in glass ionomer cement formulations (Fuji II commercial GIC). Surface properties (wettability) of modified cements were studied by water contact angle measurements as a function of time. Work of adhesion values of different surfaces was also determined. The effect of NVP modified polyacid, on bond strength of glass-ionomer cement to dentin was also investigated. The mean data obtained from contact angle and bonding strength measurements were subjected to one- and two-way analysis of variance (ANOVA) at alpha=0.05. Results showed that NVP modified glass ionomer cements showed significantly lower contact angles (theta=47 degrees) and higher work of adhesion (WA=59.4 erg/cm(2)) in comparison to commercially available Fuji II GIC (theta=60 degrees and WA=50.3 erg/cm(2), respectively). The wettability of dentin surfaces conditioned with NVP containing terpolymer was higher (theta=21 degrees, WA=74.2 erg/cm(2)) than dentin conditioned with Fuji conditioner (theta=30 degrees, WA=69 erg/cm(2)). The experimental cement also showed higher but not statistically significant values for shear bond strength to dentin (7.8 MPa), when compared to control group (7.3 MPa). It was concluded that NVP containing polyelectrolytes are better dentin conditioners than the commercially available dentin conditioner (Fuji Cavity Conditioner, GC). NVP containing terpolymers can enhance the surface properties of GICs and also increase their bond strength to the dentin.

Effect of nano-hydroxyapatite on bone morphogenetic protein-2-induced hard tissue formation and dentin resorption on a dentin surface

NASA Astrophysics Data System (ADS)

Tamagawa, Hiroki; Tenkumo, Taichi; Sugaya, Tsutomu; Kawanami, Masamitsu

2012-12-01

AimThe purpose of this study was to evaluate the effects of the addition of nano-hydroxyapatite to a collagen membrane-carrier of recombinant human bone morphogenetic protein-2 (rhBMP-2) on hard tissue formation and dentin resorption on dentin surfaces in vivo. Materials and methodsNano-hydroxyapatite collagen composite (nHAC) membranes or collagen (C) membranes were each immersed in either 100 or 400 μg/ml rhBMP-2 and placed on dentin chips that were implanted into rat thigh muscle. The implants were analyzed at 2 or 4 weeks after surgery by histological observation and histomorphometric analysis. ResultsThe percentage of the hard tissue formed by each nHAC group was significantly higher than that formed by any of the C groups, except for that formed by the group loaded with 400 μg/ml rhBMP-2 at 4 weeks after implantation. No significant differences were observed in the percentage of dentin resorption between the nHAC groups and C groups at any stage or at any rhBMP-2 concentration. ConclusionThese findings showed that addition of nano-hydroxyapatite to a collagen membrane accelerated the formation of hard tissue induced by a low dose of rhBMP-2 on dentin surfaces at an early stage after implantation into rat thigh muscle, without increasing dentin resorption.

Mathematical simulation of the thermal diffusion in dentine irradiated with Nd:YAG laser using finite difference method

NASA Astrophysics Data System (ADS)

Moriyama, Eduardo H.; Zangaro, Renato A.; Lobo, Paulo D. d. C.; Villaverde, Antonio G. J. B.; Watanabe-Sei, Ii; Pacheco, Marcos T. T.; Otsuka, Daniel K.

2002-06-01

Thermal damage in dental pulp during Nd:YAG laser irradiation have been studied by several researchers; but due to dentin inhomogeneous structure, laser interaction with dentin in the hypersensitivity treatment are not fully understood. In this work, heat distribution profile on human dentine samples irradiated with Nd:YAG laser was simulated at surface and subjacent layers. Calculations were carried out using the Crank-Nicolson's finite difference method. Sixteen dentin samples with 1,5 mm of thickness were evenly distributed into four groups and irradiated with Nd:YAG laser pulses, according to the following scheme: (I) 1 pulse of 900 mJ, (II) 2 pulses of 450 mJ, (III) 3 pulses of 300 mJ, (IV) 6 pulses of 150 mJ; corresponding to a total laser energy of 900 mJ. The pulse interval was 300ms, the pulse duration of 900 ms and irradiated surface area of 0,005 mm2. Laser induced morphological changes in dentin were observed for all the irradiated samples. The heat distribution throughout the dentin layer, from the external dentin surface to the pulpal chamber wall, was calculated for each case, in order to obtain further information about the pulsed Nd:YAG laser-oral hard tissue interaction. The simulation showed significant differences in the final temperature at the pulpal chamber, depending on the exposition time and the energy contained in the laser pulse.

Dentin hypersensitivity treatment by CO2 laser: the influence of the density of dentin tubules and laser-beam incidence

NASA Astrophysics Data System (ADS)

Colojoara, Carmen; Gabay, Shimon; van der Meulen, Freerk W.; van Gemert, Martin J. C.; Miron, Mariana I.; Mavrantoni, Androniki

1997-12-01

Dentin hypersensitivity is considered to be a consequence of the presence of open dentin tubules on the exposed dentin surface. Various methods and materials used in the treatment of this disease are directed to achieve a tubule's occlusion. The purpose of this study was to evaluate under scanning electron microscopy and clinical method the sealing effects of CO2 laser on dentin tubules of human teeth without any damages of the surrounding tissues. Samples of freshly extracted noncarious 3rd molars were used. The teeth were randomly divided in to two groups A and B. The samples of group A were exposed to laser beam in cervical area, directed parallel to their dentin tubules. The teeth of group B were sectioned through a hypothetical carious lesion and lased perpendicularly or obliquely of the dentin tubules. The CO2 laser, at 10.6 micrometers wavelength, was operated only in pulse mode and provided 6.25 - 350 mJ in a burst of 25 pulses each of 250 microsecond(s) time duration with a 2 ms time interval between successive pulses (repetition rate up to 500 mH). Melting of dentin surface and partial closure of exposed dentin tubules were found for all specimens at 6.25 to 31.25 mJ energy. Our results indicated that using CO2 laser in a parallel orientation of laser beam with dentin tubules, the dentin sensitivity can be reduced without any damages of pulp vitality.

Assessment of dentin remineralization with PS-OCT

NASA Astrophysics Data System (ADS)

Manesh, Saman K.; Darling, Cynthia L.; Fried, Daniel

2009-02-01

Previous studies have demonstrated that polarization sensitive optical coherence tomography (PS-OCT) can be used to image natural root caries lesions, measure non-destructively the severity of dentin demineralization and determine the efficacy of intervention with anti-caries agents including fluoride and lasers. The objective of this study was to determine if PS-OCT could be used to nondestructively measure the formation of a layer of remineralized dentin on the surface of dentin lesions after exposure to a remineralization solution. In this study images of artificial dentin lesions on extracted human teeth were acquired using PS-OCT after exposure to an artificial demineralizing solution at pH 4.9 for six days and after subsequent exposure to a remineralizing solution at pH 7.0 for 20 days. Polarized light microscopy and microradiography were used to examine histological thin sections from the samples for comparison. PS-OCT successfully measured the formation of a layer of increased mineral content near the lesion surface. PLM and TMR corroborated those results. This study demonstrates the potential use of PS-OCT for the nondestructive measurement of the remineralization of dentin surfaces.

Effect of laser activated bleaching on the chemical stability and morphology of intracoronal dentin.

PubMed

Lopes, Fabiane Carneiro; Roperto, Renato; Akkus, Anna; Akkus, Ozan; Palma-Dibb, Regina Guenka; de Sousa-Neto, Manoel Damião

2018-02-01

To evaluate the effect of the bleaching with 35% hydrogen peroxide either activated or not by a 970nm diode laser on the chemical stability and dentin surface morphology of intracoronary dentin. Twenty-seven slabs of intracoronary dentin specimens (3×3mm) were distributed into three groups (n=9), according to surface treatment: HP - 35% hydrogen peroxide (1×4'), DL - 970nm diode laser (1×30"/0,8W/10Hz), HP+DL - 35% HP activated with 970nm diode laser (1×30"/0,8W/10Hz leaving the gel in contact to the surface for 4' after activation). Three Raman spectra from each fragment were obtained to calculate the mean intensity of peaks of inorganic component (a.u.), organic collagen content (a.u.), and the ratio of inorganic/organic content, before and after treatment. Analyses of the samples by confocal laser microscopy were performed to evaluate the surface roughness, percentage of tubules, perimeter and area percentage of tubules, before and after treatment. Data were analyzed by Kruskal-Wallis, Dunn's, and Wilcoxon test (P<0.05). Data analysis showed that HP+DL did not change the inorganic content peaks 8.31 [29.78] or the inorganic/organic ratio 3.37 [14.67] (P>0.05). Similarly, DL did not affect the chemical stability of the dentin surface (P>0.05). However, HP significantly increased inorganic content peaks 10.87 [22.62], as well as the inorganic/organic ratio 6.25 [27.78] (P<0.05). Regarding the morphological alterations, all surface treatments increase tubules exposure; HP treatment significantly increases perimeter and area percentage; and HP+DL increases surface roughness. Bleaching HP combined with DL offers an improvement in terms of intracoronal dentin surface protection, yielding better maintenance of dentin chemical stability and morphology. Copyright © 2017 Elsevier Ltd. All rights reserved.

Effect of different surface treatments on the push-out bond strength of fiber post to root canal dentin.

PubMed

Demiryürek, Ebru Ozsezer; Külünk, Safak; Saraç, Duygu; Yüksel, Gözde; Bulucu, Bilinç

2009-08-01

The purpose of this study was to evaluate the effects of different surface treatments on the bond strength of a fiber post to dentin. Sixty extracted human maxillary incisor teeth were manually shaped with K-files using the step-back technique. ISO size 45 files were used as master apical files. Post spaces were prepared and then the root canals were subjected to one of the following 5 surface treatments: irrigation with 5% sodium hypochlorite (NaOCl); treatment with ethanol, ethyl acetate, and acetone-based cleansing agent (Sikko Tim); irrigation with 17% EDTA; etching with 37% orthophosphoric acid for 15 seconds; and etching with 10% citric acid for 15 seconds. Fiber posts were luted using self-etching/self-priming dual polymerized resin cement. From the coronal part of each root, 3 slides of 0.6-mm thickness were obtained. A push-out bond strength test was performed by a universal testing machine at a crosshead speed of 0.5 mm/min. Dentin surfaces were examined under scanning electron microscopy (SEM) after different surface treatments. Data were analyzed with a one-way analysis of variance (ANOVA) and Tukey HSD test. ANOVA revealed that canal surface treatment affected the bond strength (P < .001). The highest bond strength was obtained in the Sikko Tim group. The results also showed that surface treatment methods increased the bond strength to dentin when compared with the control group. Sikko Tim group was the more effective surface treatment agent compared with EDTA, orthophosphoric acid, citric acid, and control groups; however, it could not remove the smear layer and sealer remnants effectively on radicular dentin surfaces. Removal of the smear layer and opening of dentinal tubules are not recommended when a self-etching/self-priming adhesive system is used.

Microtensile bond strength of etch-and-rinse and self-etching adhesives to intrapulpal dentin after endodontic irrigation and setting of root canal sealer.

PubMed

Wattanawongpitak, Nipaporn; Nakajima, Masatoshi; Ikeda, Masaomi; Foxton, Richard M; Tagami, Junji

2009-02-01

To evaluate the effect of endodontic irrigation regimens and calcium hydroxide root canal sealer (Sealapex) on the microtensile bond strengths (muTBS) of dual-curing resin composite (Clearfil DC Core Automix) to the intrapulpal dentin. Forty standardized coronal-half root canal dentin specimens obtained from human premolars were divided into 4 groups: group A, no treatment (control); group B, Sealapex; group C, NaOCl/Sealapex; group D, EDTA/NaOCl/Sealapex. After 7 days of storage in 100% relative humidity, Sealapex was removed. Dentin surfaces were bonded with adhesives, either etch-and-rinse (Single Bond) or self-etching (Clearfil SE Bond), and built up with resin composite. The bonded specimens were trimmed into an hourglass shape with a 1-mm2 cross-sectional area for microtensile testing (n = 20). The muTBS to intrapulpal dentin was analyzed using two-way ANOVA and Dunnett's TC test. Two teeth of each group were prepared for micromorphological analysis of dentin surface. The root canal sealer with or without endodontic irrigation significantly affected the bond strengths of resin composite to intrapulpal dentin compared with the control group (p < 0.05). There were no significant differences in muTBS of each experimental group between etch-and-rinse and self-etching adhesives (p > 0.05). The dentin surface was covered with a mud-like material after sealer application for 7 days. The root canal sealer reduced the muTBS of dual-curing resin composite with etch-and-rinse and self-etching adhesive systems to intrapulpal dentin. Treatment with EDTA followed by NaOCI prior to obturation caused an additional reduction in muTBS of both adhesive systems to intrapulpal dentin.

Mechanical properties and molecular structure analysis of subsurface dentin after Er:YAG laser irradiation.

PubMed

He, Zhengdi; Chen, Lingling; Hu, Xuejuan; Shimada, Yasushi; Otsuki, Masayuki; Tagami, Junji; Ruan, Shuangchen

2017-10-01

The purpose of this study was to evaluate the chemical and mechanical modifications in subsurface dentin layer after Er: YAG (Erbium-Yttrium Aluminium Garnet) laser irradiation, as the guidance of new dental restorative materials specific for laser irradiated dentin. Dentin disks obtained from extracted human molars were prepared and exposed to a single pulse Er:YAG laser irradiation at 80mJ/pulse. After laser irradiation the mechanical and chemical characteristics of intertubular dentin in subsurface layer were studied using nanoindentation tester and micro-Raman spectromy (μ-RS). The dentin 5-50µm depth beneath the lased surface was determined as testing area. Two-way analysis of variance (ANOVA) were used to compare the mechanical values between lased and untreated subsurface dentin (P = 0.05). A laser affected subsurface dentin layer after Er:YAG laser treatment is present. The laser irradiation is considered to decrease the mechanical properties in the superficial subsurface layer (<15µm deep). There was no significant difference in nanohardness and Young's modulus between lased subsurface dentin and untreated dentin (p > 0.05) under the depth of 15µm. However, the dentin at 5µm and 10µm depth beneath the lased surface exhibited significantly lower (~ 47.8% and ~ 33.6% respectively) hardness (p < 0.05). Er:YAG laser irradiation affected both mineral and organic components in subsurface dentin layer, a higher degree of crystallinity and reduced organic compounds occurred in the lased subsurface dentin. Under the tested laser parameters, Er:YAG laser irradiation causes lower mechanical values and reduction of organic components in subsurface dentin, which has deleterious effects on resin adhesion to this area. Copyright © 2017 The Authors. Published by Elsevier Ltd.. All rights reserved.

The influence of the energy density and other clinical parameters on bond strength of Er:YAG-conditioned dentin compared to conventional dentin adhesion.

PubMed

Gisler, Gottfried; Gutknecht, Norbert

2014-01-01

The aim of this in vitro study was to optimise clinical parameters and the energy density of Er:YAG laser-conditioned dentin for class V fillings. Shear tests in three test series were conducted with 24 freshly extracted human third molars as samples for each series. For every sample, two orofacial and two approximal dentin surfaces were prepared. The study design included different laser energies, a thin vs a thick bond layer, the influence of adhesives as well as one-time- vs two-time treatment. The best results with Er:YAG-conditioned dentin were obtained with fluences just above the ablation threshold (5.3 J/cm(2)) in combination with a self-etch adhesive, a thin bond layer and when bond and composite were two-time cured. Dentin conditioned this way reached an averaged bond strength of 23.32 MPa (SD 5.3) and 24.37 MPa (SD 6.06) for two independent test surfaces while showing no statistical significance to conventional dentin adhesion and two-time treatment with averaged bond strength of 24.93 MPa (SD 11.51). Significant reduction of bond strength with Er:YAG-conditioned dentin was obtained when using either a thick bond layer, twice the laser energy (fluence 10.6 J/cm(2)) or with no dentin adhesive. The discussion showed clearly that in altered (sclerotic) dentin, e.g. for class V fillings of elderly patients, bond strengths in conventional dentin adhesion are constantly reduced due to the change of the responsibles, bond giving dentin structures, whereas for Er:YAG-conditioned dentin, the only way to get an optimal microretentive bond pattern is a laser fluence just above the ablation threshold of sclerotic dentin.

Evaluation of sub-surface penetration and bonding durability of self-etching primer systems to Er:YAG laser treated cervical dentin.

PubMed

He, Zhengdi; Chen, Lingling; Shimada, Yasushi; Tagami, Junji; Ruan, Shuangchen

2017-03-31

This study aimed to investigate self-etching bonding systems penetrating in sub-surface dentin layer after Er:YAG laser irradiation and micro-shear bonding durability over a period of 1 year. Dentin slices obtained from extracted human third molars were prepared. Two self-etching adhesive systems were evaluated: Clearfil SE Bond and Clearfil Tri-S Bond. Specimens were tested for micro-shear bond strength with one of the following treatments: Er:YAG laser irradiation and 600-grit silicon paper polishing at 24 h, 7 days, 6 months and 1 year. The adhesive interfaces between bonding agents and lased cervical dentin were studied. No hybrid layer could be observed for lased dentin. The slim resin tags could be seen penetrating through the lased subsurface layer. Bond strength to lased dentin after 6 months and 1 year were significantly decreased (p<0.05).

Polydopamine-induced tooth remineralization.

PubMed

Zhou, Yun-Zhi; Cao, Ying; Liu, Wei; Chu, Chun Hung; Li, Quan-Li

2012-12-01

Inspired by mussel bioadhesion in nature, dopamine is extensively used for biomaterial surface modification. In this study, we coated dopamine on demineralized enamel and dentin surfaces to evaluate the effect of polydopamine coating on dental remineralization. Dental slices containing enamel and dentin were first etched with 37% phosphoric acid for 2 min, followed by immersion in a 2 mg/mL freshly prepared solution of dopamine (10 mM Tris buffer, pH 8.5) for approximately 24 h at room temperature in the dark to obtain polydopamine coating. Then, the dental slices with and without polydopamine coating were immersed in the supersaturated solution of calcium and phosphate at 37 °C for 2 and 7 days. The supersaturated solution of calcium and phosphate was refreshed each day. The precipitates were characterized by SEM, XRD, FTIR, microhardness, and nanoscratch analyses. No significant difference was observed in the remineralization of enamel whether it was coated with polydopamine or not. However, a significant difference was found in dentin remineralization between dentin with and without polydopamine coating. Polydopamine coating remarkably promoted demineralized dentin remineralization, and all dentin tubules were occluded by densely packed hydroxyapatite crystals. Thus, coating polydopamine on dental tissue surface may be a simple universal technique to induce enamel and dentin remineralization simultaneously.

Effect of smear layer deproteinization on bonding of self-etch adhesives to dentin: a systematic review and meta-analysis

PubMed Central

Alshaikh, Khaldoan H.; Mahmoud, Salah H.

2018-01-01

Objectives The aim of this systematic review was to critically analyze previously published studies of the effects of dentin surface pretreatment with deproteinizing agents on the bonding of self-etch (SE) adhesives to dentin. Additionally, a meta-analysis was conducted to quantify the effects of the above-mentioned surface pretreatment methods on the bonding of SE adhesives to dentin. Materials and Methods An electronic search was performed using the following databases: Scopus, PubMed and ScienceDirect. The online search was performed using the following keywords: ‘dentin’ or ‘hypochlorous acid’ or ‘sodium hypochlorite’ and ‘self-etch adhesive.’ The following categories were excluded during the assessment process: non-English articles, randomized clinical trials, case reports, animal studies, and review articles. The reviewed studies were subjected to meta-analysis to quantify the effect of the application time and concentration of sodium hypochlorite (NaOCl) and hypochlorous acid (HOCl) deproteinizing agents on bonding to dentin. Results Only 9 laboratory studies fit the inclusion criteria of this systematic review. The results of the meta-analysis revealed that the pooled average microtensile bond strength values to dentin pre-treated with deproteinizing agents (15.71 MPa) was significantly lower than those of the non-treated control group (20.94 MPa). Conclusions In light of the currently available scientific evidence, dentin surface pretreatment with deproteinizing agents does not enhance the bonding of SE adhesives to dentin. The HOCl deproteinizing agent exhibited minimal adverse effects on bonding to dentin in comparison with NaOCl solutions. PMID:29765895

In Vitro Ability of a Novel Nanohydroxyapatite Oral Rinse to Occlude Dentine Tubules

PubMed Central

Hill, Robert G.; Chen, Xiaohui; Gillam, David G.

2015-01-01

Objectives. The aim of the study was to investigate the ability of a novel nanohydroxyapatite (nHA) desensitizing oral rinse to occlude dentine tubules compared to selected commercially available desensitizing oral rinses. Methods. 25 caries-free extracted molars were sectioned into 1 mm thick dentine discs. The dentine discs (n = 25) were etched with 6% citric acid for 2 minutes and rinsed with distilled water, prior to a 30-second application of test and control oral rinses. Evaluation was by (1) Scanning Electron Microscopy (SEM) of the dentine surface and (2) fluid flow measurements through a dentine disc. Results. Most of the oral rinses failed to adequately cover the dentine surface apart from the nHa oral rinse. However the hydroxyapatite, 1.4% potassium oxalate, and arginine/PVM/MA copolymer oral rinses, appeared to be relatively more effective than the nHA test and negative control rinses (potassium nitrate) in relation to a reduction in fluid flow measurements. Conclusions. Although the novel nHA oral rinse demonstrated the ability to occlude the dentine tubules and reduce the fluid flow measurements, some of the other oral rinses appeared to demonstrate a statistically significant reduction in fluid flow through the dentine disc, in particular the arginine/PVM/MA copolymer oral rinse. PMID:26161093

The Effect of Energy Densities on the Shear Bond Strength of Self-Adhering Flowable Composite to Er:YAG Pretreated Dentin.

PubMed

Nahas, Paul; Zeinoun, Toni; Majzoub, Zeina; Corbani, Karim; Nammour, Samir

2016-01-01

Objective . To investigate the shear bond strength of self-adhering flowable resin composite, to dentin, after exposing it to Er:YAG laser radiation, at different energy densities. Materials and Methods . Sixty freshly extracted human third molars were randomly divided into five groups ( n = 12). In the control group, dentin was left unirradiated, whereas, in the other four groups, dentin was irradiated with Er:YAG laser in noncontact mode (MSP mode = 100  µ s; 10 Hz; beam diameter: 1.3 mm; speed of 1 mm/second; air 6 mL/min; and water 4 mL/min), and respectively, with the following level of energy (50 mJ, 60 mJ, 80 mJ, and 100 mJ). Then, self-adhering flowable resin composite was bonded to all prepared dentin surfaces. Shear bond strength (SBS) was applied and fractured surfaces were examined using scanning electron microscopy. Results . SBS values showed significant differences in 60 mJ ( P < 0.05) compared to other groups. Morphological evaluation revealed tags or plugs in dentinal tubules, especially when 60 mJ and 80 mJ were used. All four groups tended to leave more residues on the dentin surface, than the control group. Conclusion . Er:YAG dentin irradiation may enhance SBS of the self-adhering flowable resin composite when it is used at the appropriate low level of energy density.

The Effect of Energy Densities on the Shear Bond Strength of Self-Adhering Flowable Composite to Er:YAG Pretreated Dentin

PubMed Central

Corbani, Karim

2016-01-01

Objective. To investigate the shear bond strength of self-adhering flowable resin composite, to dentin, after exposing it to Er:YAG laser radiation, at different energy densities. Materials and Methods. Sixty freshly extracted human third molars were randomly divided into five groups (n = 12). In the control group, dentin was left unirradiated, whereas, in the other four groups, dentin was irradiated with Er:YAG laser in noncontact mode (MSP mode = 100 µs; 10 Hz; beam diameter: 1.3 mm; speed of 1 mm/second; air 6 mL/min; and water 4 mL/min), and respectively, with the following level of energy (50 mJ, 60 mJ, 80 mJ, and 100 mJ). Then, self-adhering flowable resin composite was bonded to all prepared dentin surfaces. Shear bond strength (SBS) was applied and fractured surfaces were examined using scanning electron microscopy. Results. SBS values showed significant differences in 60 mJ (P < 0.05) compared to other groups. Morphological evaluation revealed tags or plugs in dentinal tubules, especially when 60 mJ and 80 mJ were used. All four groups tended to leave more residues on the dentin surface, than the control group. Conclusion. Er:YAG dentin irradiation may enhance SBS of the self-adhering flowable resin composite when it is used at the appropriate low level of energy density. PMID:27830151

Dentinal permeation modeling

NASA Astrophysics Data System (ADS)

Trunina, Natalia; Derbov, Vladimir; Tuchin, Valery; Altshuler, Gregory

2008-06-01

Dentinal permeation is of interest in a wide context of tooth care and treatment, in particular, tooth color improvement using combination of chemical whitening agents and light activation. A simple model of dentinal permeation accounting for the morphology of human tooth dentine and including dentinal tubules, more dense and homogeneous peritubular dentine, and less dense and less homogeneous intertubular dentin is proposed. Calculation of permeability of dentine layer is carried out for H IIO and H IIO II versus the tubule diameter and tubule density taken from the microphotograph analysis. This opens the possibility to calculate the distribution of permeability over the tooth surface taking into account the variations of tubule diameter and density as well as those of the diffusion coefficients and layer thickness

Monitoring Demineralization and Subsequent Remineralization of Human Teeth at the Dentin-Enamel Junction with Atomic Force Microscopy.

PubMed

Lechner, Bob-Dan; Röper, Stephanie; Messerschmidt, Jens; Blume, Alfred; Magerle, Robert

2015-09-02

Using atomic force microscopy, we monitored the nanoscale surface morphology of human teeth at the dentin-enamel junction after performing successive demineralization steps with an acidic soft drink. Subsequently, we studied the remineralization process with a paste containing calcium and phosphate ions. Repeated atomic force microscopy imaging of the same sample areas on the sample allowed us to draw detailed conclusions regarding the specific mechanism of the demineralization process and the subsequent remineralization process. The about 1-μm-deep grooves that are caused by the demineralization process were preferentially filled with deposited nanoparticles, leading to smoother enamel and dentine surfaces after 90 min exposure to the remineralizing agent. The deposited material is found to homogeneously cover the enamel and dentine surfaces in the same manner. The temporal evolution of the surface roughness indicates that the remineralization caused by the repair paste proceeds in two distinct successive phases.

Shear bond strength of porcelain laminate veneers to enamel, dentine and enamel-dentine complex bonded with different adhesive luting systems.

PubMed

Öztürk, Elif; Bolay, Şükran; Hickel, Reinhard; Ilie, Nicoleta

2013-02-01

The aim of this study was to evaluate the shear bond strength of porcelain laminate veneers to 3 different surfaces by means of enamel, dentine, and enamel-dentine complex. One hundred thirty-five extracted human maxillary central teeth were used, and the teeth were randomly divided into 9 groups (n=15). The teeth were prepared with 3 different levels for bonding surfaces of enamel (E), dentine (D), and enamel-dentine complex (E-D). Porcelain discs (IPS e.max Press, Ivoclar Vivadent) of 2mm in thickness and 4mm in diameter were luted to the tooth surfaces by using 2 light-curing (RelyX Veneer [RV], 3M ESPE; Variolink Veneer [VV], Ivoclar Vivadent) and a dual-curing (Variolink II [V2], Ivoclar Vivadent) adhesive systems according to the manufacturers' instructions. Shear bond strength test was performed in a universal testing machine at 0.5mm/min until bonding failure. Failure modes were determined under a stereomicroscope, and fracture surfaces were evaluated with a scanning electron microscope. The data were statistically analysed (SPSS 17.0) (p=0.05). Group RV-D exhibited the lowest bond strength value (5.42±6.6MPa). There was statistically no difference among RV-D, V2-D (13.78±8.8MPa) and VV-D (13.84±6.2MPa) groups (p>0.05). Group VV-E exhibited the highest bond strength value (24.76±8.8MPa). The type of tooth structure affected the shear bond strength of the porcelain laminate veneers to the 3 different types of tooth structures (enamel, dentine, and enamel-dentine complex). When dentine exposure is necessary during preparation, enough sound enamel must be protected as much as possible to maintain a good bonding; to obtain maximum bond strength, preparation margins should be on sound enamel. Copyright © 2012 Elsevier Ltd. All rights reserved.

Separate whitening effects on enamel and dentin after fourteen days.

PubMed

Kugel, Gerard; Petkevis, Jason; Gurgan, Sevil; Doherty, Eileen

2007-01-01

The purpose of this study was to investigate the mechanism of action of a bleaching agent, as it relates to enamel and dentin. Twenty-six extracted human molar teeth were sectioned at the cemento-enamel junction and were randomly assigned to two groups. L*a*b* readings were taken with a spectrophotometer: on buccal surfaces of the crown, at enamel and dentin. The teeth were exposed to carbamide peroxide or placebo gel and L*a*b* scores were again recorded to determine color changes. Treatments were compared using ancova test with baseline color as the covariate. Relative to placebo, buccal surfaces exhibited the greatest Deltab* and DeltaL* color change. On buccal surfaces, the adjusted mean (SE) treatment differences were -7.8 (1.00) for Deltab* and 5.7 (0.97) for DeltaL, with groups differing significantly (p < 0.0001). On enamel surfaces, treatment differences were -3.6 (0.61) for Deltab* and 4.6 (0.80) for DeltaL* (p < 0.0001). Dentin exhibited the least color improvement. Adjusted mean (SE) treatment differences were -1.9 (0.87) for Deltab* and 2.4 (1.10) for DeltaL*, with groups differing significantly (p < 0.02) on dentin color change. The majority of color change seen on the buccal surface of tooth crowns exposed to carbamide peroxide 15% was because of the color change in enamel. As compared to enamel, dentin was less affected after 14 days.

The role of copper nanoparticles in an etch-and-rinse adhesive on antimicrobial activity, mechanical properties and the durability of resin-dentine interfaces.

PubMed

Gutiérrez, Mario F; Malaquias, Pamela; Hass, Viviane; Matos, Thalita P; Lourenço, Lucas; Reis, Alessandra; Loguercio, Alessandro D; Farago, Paulo Vitor

2017-06-01

To evaluate the effect of addition of copper nanoparticles at different concentrations into an etch-and-rinse adhesive (ER) on antimicrobial activity, Knoop microhardness (KHN), in vitro and in situ degree of conversion (DC), as well as the immediate (IM) and 2-year (2Y) resin-dentine bond strength (μTBS) and nanoleakage (NL). Seven experimental ER adhesives were formulated according to the amount of copper nanoparticles incorporated into the adhesives (0 [control], 0.0075 to 1wt.%). We tested the antimicrobial activity of adhesives against Streptococcus mutans using agar diffusion assay after IM and 2Y. The Knoop microhardness and in vitro DC were tested after IM and 2Y. The adhesives were applied to flat occlusal dentine surfaces after acid etching. After resin build-ups, specimens were longitudinally sectioned to obtain beam-like resin-dentine specimens (0.8mm 2 ), which were used for evaluation of μTBS and nanoleakage at the IM and 2Y periods. In situ DC was evaluated at the IM period in these beam-like specimens. Data were submitted to appropriate statistical analyses (α=0.05). The addition of copper nanoparticles provided antimicrobial activity to the adhesives only in the IM evaluation and slightly reduced the KHN, the in vitro and in situ DC (copper concentrations of 1wt.%). However, KHN increase for all concentrations after 2Y. After 2Y, no significant reductions of μTBS (0.06 to 1% wt.%) and increases of nanoleakage were observed for copper containing adhesives compared to the control group. Copper nanoparticles addition up to 0.5wt.% may provide antimicrobial properties to ER adhesives and prevent the degradation of the adhesive interface, without reducing the mechanical properties of the formulations. Copyright © 2017 Elsevier Ltd. All rights reserved.

To What Extent is Primate Second Molar Enamel Occlusal Morphology Shaped by the Enamel-Dentine Junction?

PubMed Central

Gilissen, Emmanuel; Thiery, Ghislain

2015-01-01

The form of two hard tissues of the mammalian tooth, dentine and enamel, is the result of a combination of the phylogenetic inheritance of dental traits and the adaptive selection of these traits during evolution. Recent decades have been significant in unveiling developmental processes controlling tooth morphogenesis, dental variation and the origination of dental novelties. The enamel-dentine junction constitutes a precursor for the morphology of the outer enamel surface through growth of the enamel cap which may go along with the addition of original features. The relative contribution of these two tooth components to morphological variation and their respective response to natural selection is a major issue in paleoanthropology. This study will determine how much enamel morphology relies on the form of the enamel-dentine junction. The outer occlusal enamel surface and the enamel-dentine junction surface of 76 primate second upper molars are represented by polygonal meshes and investigated using tridimensional topometrical analysis. Quantitative criteria (elevation, inclination, orientation, curvature and occlusal patch count) are introduced to show that the enamel-dentine junction significantly constrains the topographical properties of the outer enamel surface. Our results show a significant correlation for elevation, orientation, inclination, curvature and occlusal complexity between the outer enamel surface and the enamel dentine junction for all studied primate taxa with the exception of four modern humans for curvature (p<0.05). Moreover, we show that, for all selected topometrical parameters apart from occlusal patch count, the recorded correlations significantly decrease along with enamel thickening in our sample. While preserving tooth integrity by providing resistance to wear and fractures, the variation of enamel thickness may modify the curvature present at the occlusal enamel surface in relation to enamel-dentine junction, potentially modifying dental functionalities such as blunt versus sharp dental tools. In terms of natural selection, there is a balance between increasing tooth resistance and maintaining efficient dental tools. In this sense the enamel cap acts as a functional buffer for the molar occlusal pattern. In primates, results suggest a primary emergence of dental novelties on the enamel-dentine junction and a secondary transposition of these novelties with no or minor modifications of dental functionalities by the enamel cap. Whereas enamel crenations have been reported by previous studies, our analysis do not support the presence of enamel tubercles without dentine relief nuclei. As is, the enamel cap is, at most, a secondary source of morphological novelty. PMID:26406597

Micro-shear bond strengths of adhesive resins to coronal dentin versus the floor of the pulp chamber.

PubMed

Toba, Shigemitsu; Veerapravati, Weeraporn; Shimada, Yasushi; Nikaido, Toru; Tagami, Junji

2003-09-01

To evaluate the micro-shear bond strengths to superficial coronal dentin and the floor of the pulp chamber using two dentin bonding systems and to compare the ultrastructure of the resin-dentin interface of the two regions. 30 non-carious molars were used to obtain 2 mm thick slabs of coronal dentin and dentin at the pulp chamber. The specimens in each region were divided into three sub-groups to be bonded as follows; Clearfil SE Bond was used according to the manufacturer's instructions, Single Bond was applied to either wet dentin (Blot dry Group) or air-dried dentin (Dry Group) after phosphoric acid etching. A resin composite cylinder 0.5 mm high and 0.75 mm in diameter formed using a vinyl tube was bonded to the dentin. Specimens were stored at 37 degrees C for 24 hours in water and then stressed in shear at a crosshead speed of 1 mm/minute. The data were analyzed with one-way ANOVA and Fisher's PLSD test at the 5% level of significance. In addition, the ultrastructure of cross-sectioned dentin surfaces, the conditioned dentin surface and the resin dentin interfaces were observed by SEM. The bond strengths of Clearfil SE Bond and the Single Bond Blot dry group were approximately 40 MPa in coronal dentin and 30 MPa in the dentin at the floor of the pulp chamber respectively. However, the bond strengths of Single Bond were significantly lower in the Dry condition (MPa) (P < 0.05). SEM observations revealed the thickness of the hybrid layer created by Clearfil SE Bond in coronal dentin and at the floor of the pulp chamber were less than 1.0 microm thick. For Single Bond, a 3-4 microm hybrid layer was created in coronal dentin, while a thinner hybrid layer was observed in the floor of the pulp chamber. Morphological and structural variations in dentin may have influenced the bond strengths of the bonding systems to the floor of the pulp chamber.

Effect of different adhesive strategies on microtensile bond strength of computer aided design/computer aided manufacturing blocks bonded to dentin.

PubMed

Roperto, Renato; Akkus, Anna; Akkus, Ozan; Lang, Lisa; Sousa-Neto, Manoel Damiao; Teich, Sorin; Porto, Thiago Soares

2016-01-01

The aim of this study was to determine the microtensile bond strength (μTBS) of ceramic and composite computer aided design-computer aided manufacturing (CAD-CAM) blocks bonded to dentin using different adhesive strategies. In this in vitro study, 30 crowns of sound freshly extracted human molars were sectioned horizontally 3 mm above the cementoenamel junction to produce flat dentin surfaces. Ceramic and composite CAD/CAM blocks, size 14, were sectioned into slices of 3 mm thick. Before bonding, CAD/CAM block surfaces were treated according to the manufacturer's instructions. Groups were created based on the adhesive strategy used: Group 1 (GI) - conventional resin cement + total-etch adhesive system, Group 2 (GII) - conventional resin cement + self-etch adhesive system, and Group 3 (GIII) - self-adhesive resin cement with no adhesive. Bonded specimens were stored in 100% humidity for 24h at 37΀C, and then sectioned with a slow-speed diamond saw to obtain 1 mm × 1 mm × 6 mm microsticks. Microtensile testing was then conducted using a microtensile tester. μTBS values were expressed in MPa and analyzed by one-way ANOVA with post hoc (Tukey) test at the 5% significance level. Mean values and standard deviations of μTBS (MPa) were 17.68 (±2.71) for GI/ceramic; 17.62 (±3.99) for GI/composite; 13.61 (±6.92) for GII/composite; 12.22 (±4.24) for GII/ceramic; 7.47 (±2.29) for GIII/composite; and 6.48 (±3.10) for GIII/ceramic; ANOVA indicated significant differences among the adhesive modality and block interaction (P < 0.05), and no significant differences among blocks only, except between GI and GII/ceramic. Bond strength of GIII was consistently lower (P < 0.05) than GI and GII groups, regardless the block used. Cementation of CAD/CAM restorations, either composite or ceramic, can be significantly affected by different adhesive strategies used.

Reducing the risk of sensitivity and pulpal complications after the placement of crowns and fixed partial dentures.

PubMed

Brännström, M

1996-10-01

Sensitivity after cementation of a crown with glass-ionomer cement is often attributed to an adverse effect on the pulp by the luting agent. Most permanent restorative materials in common use today do not tend to irritate the pulp; the main cause of pulpal damage is infection, the bacteria originating in the smear layer or deep in the dental tubules, inaccessible to caries-excavating procedures. A poorly fitting provisional crown may expose cut dentin to the oral fluids, and mechanical trauma caused by frictional heat during preparation may also damage the pulp. The following precautions are recommended during precementation procedures to reduce the risk of an inflammatory response in the pulp: (1) The provisional crown should be well fitting, covering cervical dentin but not impinging on the periodontal tissues. The permanent crown should be cemented as soon as possible. (2) The superficial smear layer should be removed and the dentinal surface should be treated with an antibacterial solution before the provisional crown is placed. (3) To decrease dentinal permeability under the provisional crown, the dentinal surface should be covered with a liner that can be easily removed before final cementation. (4) to ensure optimal mircomechanical bonding, the dentinal surface should be thoroughly cleaned, and the dentin should be kept moist until cementation. (5) The occlusion should be carefully checked before cementation of the crown.

Optical analysis of enamel and dentin caries in relation to mineral density using swept-source optical coherence tomography

PubMed Central

Ueno, Tomoka; Shimada, Yasushi; Matin, Khairul; Zhou, Yuan; Wada, Ikumi; Sadr, Alireza; Sumi, Yasunori; Tagami, Junji

2016-01-01

Abstract. The aim of this study was to evaluate the signal intensity and signal attenuation of swept source optical coherence tomography (SS-OCT) for dental caries in relation to the variation of mineral density. SS-OCT observation was performed on the enamel and dentin artificial demineralization and on natural caries. The artificial caries model on enamel and dentin surfaces was created using Streptococcus mutans biofilms incubated in an oral biofilm reactor. The lesions were centrally cross sectioned and SS-OCT scans were obtained in two directions to construct a three-dimensional data set, from the lesion surface (sagittal scan) and parallel to the lesion surface (horizontal scan). The integrated signal up to 200  μm in depth (IS200) and the attenuation coefficient (μ) of the enamel and dentin lesions were calculated from the SS-OCT signal in horizontal scans at five locations of lesion depth. The values were compared with the mineral density obtained from transverse microradiography. Both enamel and dentin demineralization showed significantly higher IS200 and μ than the sound tooth substrate from the sagittal scan. Enamel demineralization showed significantly higher IS200 than sound enamel, even with low levels of demineralization. In demineralized dentin, the μ from the horizontal scan consistently trended downward compared to the sound dentin. PMID:27704033

Effect of different adhesion strategies on bond strength of resin composite to composite-dentin complex.

PubMed

Özcan, M; Pekkan, G

2013-01-01

Service life of discolored and abraded resin composite restorations could be prolonged by repair or relayering actions. Composite-composite adhesion can be achieved successfully using some surface conditioning methods, but the most effective adhesion protocol for relayering is not known when the composite restorations are surrounded with dentin. This study evaluated the effect of three adhesion strategies on the bond strength of resin composite to the composite-dentin complex. Intact maxillary central incisors (N=72, n=8 per subgroup) were collected and the coronal parts of the teeth were embedded in autopolymerized poly(methyl tfr54methacrylate) surrounded by a polyvinyl chloride cylinder. Cylindrical cavities (diameter: 2.6 mm; depth: 2 mm) were opened in the middle of the labial surfaces of the teeth using a standard diamond bur, and the specimens were randomly divided into three groups. Two types of resin composite, namely microhybrid (Quadrant Anterior Shine; AS) and nanohybrid (Grandio; G), were photo-polymerized incrementally in the cavities according to each manufacturer's recommendations. The composite-enamel surfaces were ground finished to 1200-grit silicone carbide paper until the dentin was exposed. The surfaces of the substrate composites and the surrounding dentin were conditioned according to one of the following adhesion protocols: protocol 1: acid-etching (dentin) + silica coating (composite) + silanization (composite) + primer (dentin) + bonding agent (dentin + composite); protocol 2: silica coating (composite) + acid-etching (dentin) + silanization (composite) + primer (dentin) + bonding agent (dentin + composite); and protocol 3: acid-etching (dentin) + primer (dentin) + silanization (composite) + bonding agent (dentin + composite). Applied primer and bonding agents were the corresponding materials of the composite manufacturer. Silica coating (CoJet sand, 30 μm) was achieved using a chairside air-abrasion device (distance: 10 mm; duration: four seconds in circular motion). After conditioning protocols, the repair resin was adhered to the substrate surfaces using transparent polyethylene molds (diameter: 3.6 mm) incrementally and photo-polymerized. The substrate-adherend combinations were as follows: AS-AS, G-G, AS-G. Shear force was applied to the adhesive interface in a Universal Testing Machine (crosshead speed: 1 mm/min). The types of failures were further evaluated and categorized as follows: 1) cohesive in the composite substrate and 2) adhesive at the interface. Bond strength values (MPa) were statistically analyzed using two-way analysis of variance and least significant difference post hoc tests (α=0.05). Significant effects of the adhesion strategy (p=0.006) and the composite type (p=0.000) were found. Interaction terms were not significant (p=0.292). Regardless of the substrate-adherend combination, protocol 1 (17-22 MPa) showed significantly higher results than did protocols 2 (15-17 MPa) and 3 (11-17 MPa) (p=0.028, p=0.002, respectively). The highest results were obtained from the G-G combination after all three protocols (17-22 MPa). The incidence of cohesive failures was more common when the substrate and the adherend were the same composite type (AS-AS: 87.5%, 87.5%, 75%; G-G: 100%, 75%, 50% for protocols 1, 2, and 3, respectively). When substrate and adherend were used interchangeably, adhesive failures were more frequent (25%, 50%, and 100% for protocol 1, 2, and 3, respectively). When the substrate and the adherend are of the same type, greater repair strength could be expected. In the repair of composites next to the dentin, depending on the composite type, conditioning the composite with silica coating and silanization after etching the dentin adds to the repair strength compared to the results obtained with silane application only.

Scanning electron microscopy study of the effect of the brushing time on the human tooth dentin after exposure to acidic softdrinks.

PubMed

Kwoni, Eri; Choi, Samjin; Cheong, Youjin; Park, Ki-Ho; Park, Hun-Kuk

2012-07-01

Scanning electron microscopy (SEM) was used to examine the abrasive and erosive potential of the brushing time on the dentin surface eroded by acidic soft drinks to suggest an optimized toothbrushing start time after the consumption of cola (pH 2.52) in children. Thirty-six non-carious primary central incisors were assigned to 12 experimental groups (n = 3) based on the erosive and abrasive treatment protocols. Cola exposure was used as the erosive treatment. Three brushing durations (5, 15, and 30 sec) and four brushing start times (immediately, 30 min, 60 min, and 120 min) after an erosive pre-treatment were used for the abrasive treatment. Toothbrushing after exposure to acidic soft drinks led to an increase in the open-tubule fraction and microstructural changes. Toothbrushing immediately after the erosive pre-treatment showed the largest abrasive and erosive potential on the dentin whereas that 60 and 120 min after the pre-treatment showed the least abrasive and erosive potential on the dentin. Toothbrushing for both 60 and 120 min after the pre-treatment showed similar erosive and abrasive potentials on the dentin. The brushing duration showed no effect on the erosive and abrasive potential on the dentin. Therefore, to achieve the desired tooth surface cleaning and less surface lesion on the dentin surface, toothbrushing should be performed at least 1 hour after cola consumption. Three-minute brushing after cola consumption is sufficient to prevent dental lesions, and prolonged brushing can irritate the gingival tissues.

Intrapulpal temperatures during pulsed Nd:YAG laser treatment of dentin, in vitro.

PubMed

White, J M; Fagan, M C; Goodis, H E

1994-03-01

Lasers are being used for soft tissue removal, caries removal, and treatment of root surface sensitivity. One concern for laser safety is that the heat produced at the irradiated root surface may diffuse to the pulp causing irreversible pulpal damage. To test this heat diffusion, copper-constantan thermocouples were inserted into the radicular pulp canals of extracted teeth. Simulating direct exposure which might occur during gingival excision, superficial caries removal, and modification of the dentin surface for treatment of root surface sensitivity, a 2 mm2 area of the external root surface was uniformly irradiated with a pulsed Nd:YAG laser using a 320 microns diameter fiber optic contact probe. Power was varied from 0.3 to 3.0 W with frequencies of 10 and 20 Hz. Temperature changes during cavity preparations using a high speed handpiece with air coolant were also recorded. Repeated measures ANOVA (P < or = 0.05) indicated that intrapulpal temperatures increased as a function of power, frequency, and time. Intrapulpal temperatures decreased as remaining dentin thickness (0.2 to 2.0 mm) increased for each laser parameter. Irradiation of dentin using a Nd:YAG pulsed laser, within the treatment times, powers, and frequencies with adequate remaining dentin thickness, as outlined in this paper, should not cause devitalizing intrapulpal temperature rises.

Bond strength of self-etch adhesives after saliva contamination at different application steps.

PubMed

Cobanoglu, N; Unlu, N; Ozer, F F; Blatz, M B

2013-01-01

This study evaluated and compared the effect of saliva contamination and possible decontamination methods on bond strengths of two self-etching adhesive systems (Clearfil SE Bond [CSE], Optibond Solo Plus SE [OSE]). Flat occlusal dentin surfaces were created on 180 extracted human molar teeth. The two bonding systems and corresponding composite resins (Clearfil AP-X, Kerr Point 4) were bonded to the dentin under six surface conditions (n=15/group): group 1 (control): primer/bonding/composite; group 2: saliva/drying/primer/bonding/composite; group 3: primer/saliva/rinsing/drying/primer/bonding/composite; group 4: primer/saliva/rinsing/drying/bonding/composite; group 5: primer/bonding (cured)/saliva/rinsing/drying/primer/bonding/composite; group 6: primer/bonding (cured)/saliva/removing contaminated layer with a bur/rinsing/drying/primer/bonding/composite. Shear bond strength was tested after specimens were stored in distilled water at 37°C for 24 hours. One-way analysis of variance and Tukey post hoc tests were used for statistical analyses. For CSE, groups 2, 3, and 4 and for OSE, groups 6, 2, and 4 showed significantly lower bond strengths than the control group (p<0.05). CSE groups 5 and 6 and OSE groups 3 and 5 revealed bond strengths similar to the control. When saliva contamination occurred after light polymerization of the bonding agent, repeating the bonding procedure recovered the bonding capacity of both self-etch adhesives. However, saliva contamination before or after primer application negatively affected their bond strength.

Shear test of composite bonded to dentin: Er:YAG laser versus dental handpiece preparations

NASA Astrophysics Data System (ADS)

Visuri, Steven R.; Gilbert, Jeremy L.; Walsh, Joseph T., Jr.; Wigdor, Harvey A.

1995-05-01

The erbium:YAG laser coupled with a cooling stream of water appears to be an effective means of removing dental hard tissues. However, before the procedure is deemed clinically viable, there are several important issues of safety and efficacy that need to be explored. In this study we investigated the surface that remains following laser ablation of dentin and compared the results to the use of a dental handpiece. Specifically, we studied the effect the laser radiation had on the bonding of composite to dentin. The crowns of extracted human molars were removed revealing the underlying dentin. An additional thickness of material was removed with either a dental handpiece or an Er:YAG laser by raster scanning the samples under a fixed handpiece or laser. Comparable surface roughnesses were achieved. A cylinder of composite was bonded onto the prepared surfaces following the manufacturer's directions. The dentin-composite bond was then shear stressed to failure on a universal testing apparatus and the maximum load recorded. Preliminary results indicated that laser irradiated samples had improved bond strengths. SEM photographs of the surfaces were also taken to compare the two methods of tooth preparation.

Bond strengths of Scotchbond Multi-Purpose to moist dentin and enamel.

PubMed

Swift, E J; Triolo, P T

1992-12-01

This in vitro study tested the shear bond strengths of the Scotchbond Multi-Purpose adhesive system to moist and dry enamel and dentin. After the tooth was etched, the surface was either dried with compressed air or blotted with tissue paper, leaving the surface visibly moist. Primer and adhesive were applied according to the manufacturer's directions. Resin composite posts were applied, and the specimens were thermocycled. Shear bond strengths were determined using an Instron universal testing machine. For both enamel and dentin, mean shear bond strengths were higher when the surface was left visibly moist after etching. Bond strengths to moist and dry dentin were 21.8 and 17.8 MPa, respectively. Enamel bond strengths were slightly lower, with values of 17.0 and 14.2 MPa to moist and dry enamel, respectively.

Influence of chlorhexidine on dentin adhesive interface micromorphology and nanoleakage expression of resin cements.

PubMed

Stape, Thiago Henrique Scarabello; Menezes, Murilo De Sousa; Barreto, Bruno De Castro Ferreira; Naves, Lucas Zago; Aguiar, Flávio Henrique Baggio; Quagliatto, Paulo Sérgio; Martins, Luís Roberto Marcondes

2013-08-01

This study focused on adhesive interface morphologic characterization and nanoleakage expression of resin cements bonded to human dentin pretreated with 1% chlorhexidine (CHX). Thirty-two non-carious human third molars were ground flat to expose superficial dentin. Resin composite blocks were luted to the exposed dentin using one conventional (RelyX ARC) and one self-adhesive resin cement (RelyX U100), with/without CHX pretreatment. Four groups (n = 8) were obtained: control groups (ARC and U100); experimental groups (ARC/CHX and U100/CHX) were pretreated with 1% CHX prior to the luting process. After storage in water for 24 h, the bonded teeth were sectioned into 0.9 × 0.9 mm(2) sticks producing a minimum of 12 sticks per tooth. Four sticks from each tooth were prepared for hybrid layer evaluation by scanning electron microscope analysis. The remaining sticks were immersed in silver nitrate for 24 h for either nanoleakage evaluation along the bonded interfaces or after rupture. Nanoleakage samples were carbon coated and examined using backscattered electron mode. Well-established hybrid layers were observed in the groups luted with RelyX ARC. Nanoleakage evaluation revealed increase nanoleakage in groups treated with CHX for both resin cements. Group U100/CHX exhibited the most pronouncing nanoleakage expression along with porous zones adjacent to the CHX pretreated dentin. The results suggest a possible incompatibility between CHX and RelyX U100 that raises the concern that the use of CHX with self-adhesive cements may adversely affect resin-dentin bond. Copyright © 2013 Wiley Periodicals, Inc.

Light-attenuating effect of dentin on the polymerization of light-activated restorative resins.

PubMed

Arikawa, Hiroyuki; Kanie, Takahito; Fujii, Koichi; Ban, Seiji; Takahashi, Hideo

2004-12-01

The light-attenuating effect of dentin on the mechanical properties of light-activated composite resins was evaluated using a simple experimental filter. The filter was designed to simulate the light transmittance and light diffusion characteristics of 1.0-mm thick dentin. The depth of cure, surface hardness, and flexural strength for 13 shades of three light-activated restorative resins were examined. These resins were cured either using direct irradiation with a light source, or indirect irradiation through the filter. The attenuation of light intensity by 1.0-mm thick dentin reached 85-90% in the 400-550 nm wavelength region. For all materials, the values of depth of cure, surface hardness on the top and bottom surfaces, and flexural strength of specimens irradiated indirectly through the simulated 1.0-mm thick dentin filter decreased by 37-60%, 16-55%, 50-83%, and 44-82% in comparison with those by direct irradiation, respectively. Recovery from mechanical properties' reduction was achieved when materials were irradiated 1.5-4 times longer than the standard irradiation time.

Pulsed Nd-YAG laser in endodontics

NASA Astrophysics Data System (ADS)

Ragot-Roy, Brigitte; Severin, Claude; Maquin, Michel

1994-12-01

The purpose of this study was to establish an operative method in endodontics. The effect of a pulsed Nd:YAG laser on root canal dentin has been examined with a scanning electron microscope. Our first experimentation was to observe the impacts carried out perpendicularly to root canal surface with a 200 micrometers fiber optic in the presence of dye. Secondarily, the optical fiber was used as an endodontic instrument with black dye. The irradiation was performed after root canal preparation (15/100 file or 40/100 file) or directly into the canal. Adverse effects are observed. The results show that laser irradiation on root canal dentin surfaces induces a nonhomogeneous modified dentin layer, melted and resolidified dentin closed partially dentinal tubules. The removal of debris is not efficient enough. The laser treatment seems to be indicated only for endodontic and periapical spaces sterilization after conventional root canal preparation.

Surface roughness and bacterial adhesion on root dentin treated with diode laser and conventional desensitizing agents.

PubMed

Cury, Maiza S; Silva, Camilla B; Nogueira, Ruchele D; Campos, Michelle G D; Palma-Dibb, Regina G; Geraldo-Martins, Vinicius R

2018-02-01

The treatments for dentin hypersensitivity (DH) may change the surface roughness of the root dentin, which can lead to biofilm accumulation, increasing the risk of root caries. The aim was to compare the surface roughness of root dentin after different treatments of DH and the biofilm formation on those surfaces. After initial surface roughness (Sa) assessment, 50 bovine root fragments received the following treatments (n = 10): G 1-no treatment; G2-5% sodium fluoride varnish; G3-professional application of a desensitizing dentifrice; G4-toothbrushing with a desensitizing dentifrice; and G5-diode laser application (908 nm; 1.5 W, 20 s). The Sa was reevaluated after treatments. Afterward, all samples were incubated in a suspension of Streptococcus mutans at 37 °C for 24 h. The colony-forming units (CFU) were counted using a stereoscope, and the results were expressed in CFU/mL. The one-way ANOVA and the Tukey's tests compared the roughness data and the results obtained on the bacterial adhesion test (α = 5%). G2 (2.3 ± 1.67%) showed similar Sa variation than G1 (0.25 ± 0.41%) and G5 (5.69 ± 0.99%), but different from group G3 (9.05 ± 2.39%). Group 4 showed the highest Sa variation (30.02 ± 3.83%; p < 0.05). Bacterial adhesion was higher in G4 (2208 ± 211.9), suggesting that bacterial growth is greater on rougher surfaces. The diode laser and the conventional treatments for DH may change the surface roughness of the root dentin, but only brushing with desensitizing dentifrice induced a higher bacteria accumulation on root dentin surface.

Fracture Forces of Dentin after Surface Treatment with High Speed Drill Compared to Er:YAG and Er,Cr:YSGG Laser Irradiation

PubMed Central

Franzen, Rene; Kianimanesh, Nasrin; Marx, Rudolf; Ahmed, Asma; Gutknecht, Norbert

2016-01-01

Dental tooth restorative procedures may weaken the structural integrity of the tooth, with the possibility of leading to fracture. In this study we present findings of coronal dentin strength after different techniques of surface modification. The fracture strength of dentin beams after superficial material removal with a fine diamond bur high speed drill hand piece, Er:YAG (2.94 μm, 8 J/cm2), and Er,Cr:YSGG (2.78 μm, 7.8 J/cm2) laser irradiation slightly above the ablation threshold was measured by a four-point bending apparatus. Untreated dentin beams served as a control. A total of 58 dentin beams were manufactured from sterilized human extracted molars using the coronal part of the available dentin. Mean values of fracture strength were calculated as 82.0 ± 27.3 MPa for the control group (n = 10), 104.5 ± 26.3 MPa for high speed drill treatment (n = 10), 96.1 ± 28.1 MPa for Er,Cr:YSGG laser irradiation (n = 20), and 89.1 ± 36.3 MPa for Er:YAG laser irradiation (n = 18). Independent Student's t-tests showed no significant difference between each two groups (p > 0.05). Within the parameter settings and the limits of the experimental setup used in this study, both lasers systems as well as the high speed drill do not significantly weaken coronal dentin after surface treatment. PMID:26962473

Assessment of radicular dentin permeability after irradiation with CO2 laser and endodontic irrigation treatments with thermal imaging

NASA Astrophysics Data System (ADS)

Cho, Heajin; Lee, Robert C.; Chan, Kenneth H.; Fried, Daniel

2017-02-01

Previous studies have demonstrated that the permeability changes due to the surface modification of dentin can be quantified via thermal imaging during dehydration. The CO2 laser has been shown to remove the smear layer and disinfect root canals. Moreover, thermal modification via CO2 laser irradiation can be used to convert dentin into a highly mineralized enamel-like mineral. The purpose of this study is to evaluate the radicular dentin surface modification after CO2 laser irradiation by measuring the permeability with thermal imaging. Human molar specimens (n=12) were sectioned into 4 axial walls of the pulp chamber and treated with either 10% NaClO for 1 minute, 5% EDTA for 1 minute, CO2 laser or none. The CO2 laser was operated at 9.4 μm with a pulse duration of 26 μs, pulse repetition rate of 300 Hz and a fluence of 13 J/cm2. The samples were dehydrated using an air spray for 60 seconds and imaged using a thermal camera. The resulting surface morphological changes were assessed using 3D digital microscopy. The images from digital microscopy confirmed melting of the mineral phase of dentin. The area enclosed by the time-temperature curve during dehydration, ▵Q, measured with thermal imaging increased significantly with treatments with EDTA and the CO2 laser (P<0.05). These results indicate that the surface modification due to CO2 laser treatment increases permeability of radicular dentin.

Effect of different surface treatments on adhesion of In-Ceram Zirconia to enamel and dentin substrates.

PubMed

Saker, Samah; Ibrahim, Fatma; Ozcan, Mutlu

2013-08-01

Resin bonding of In-Ceram Zirconia (ICZ) ceramics is still a challenge, especially for minimally invasive applications. This study evaluated the adhesion of ICZ to enamel and dentin after different surface treatments of the ceramic. ICZ ceramic specimens (diameter: 6 mm; thickness: 2 mm) (N = 100) were fabricated following the manufacturer's instructions and randomly assigned to 5 groups (n = 20), according to the surface treatment methods applied. The groups were as follows: group C: no treatment; group SB: sandblasting; group SCS-S: CoJet+silane; group SCS-P: CoJet+Alloy Primer; group GE-S: glaze+ hydrofluoric acid etching (9.6%) for 60 s+silane. Each group was randomly divided into two subgroups to be bonded to either enamel or dentin (n = 10 per group) using MDP-based resin cement (Panavia F2.0). All the specimens were subjected to thermocycling (5000x, 5°C-55°C). The specimens were mounted in a universal testing machine and tensile force was applied to the ceramic/cement interface until failure occurred (1 mm/min). After evaluating all the debonded specimens under SEM, the failure types were defined as either "adhesive" with no cement left on the ceramic surface (score 0) or "mixed" with less than 1/2 of the cement left adhered to the surface with no cohesive failure of the substrate (score 1). The data were statistically evaluated using 2-way ANOVA and Tukey's tests (α = 0.05). The highest tensile bond strength for the enamel surfaces was obtained in group GE-S (18.1 ± 2 MPa) and the lowest in group SB (7.1 ± 1.4 MPa). Regarding dentin, group CSC-P showed the highest (12 ± 1.3 MPa) and SB the lowest tensile bond strength (5.7 ± 0.4 MPa). Groups SB, CSC-S, CSC-P, and GE-S did not show significant differences between the different surface treatments on either enamel or dentin surfaces (p < 0.05, p < 0.001, respectively). Groups CSC-P and GE-S presented similar bond strength for both the enamel and dentin substrates (p < 0.8 and p < 0.9), respectively. While on enamel substrates, exclusively adhesive failures from ICZ (score 0) were found, on dentin exclusively mixed failures were observed (score 1). Adhesion of ICZ to both enamel and dentin can be improved when ceramics are glazed, etched, and silanized, or sandblasted, primed, and cemented with an MDP-based cement.

Review of methyl methacrylate (MMA)/tributylborane (TBB)-initiated resin adhesive to dentin.

PubMed

Taira, Yohsuke; Imai, Yohji

2014-01-01

This review, focusing mainly on research related to methyl methacrylate/tributylborane (MMA/TBB) resin, presents the early history of dentin bonding and MMA/TBB adhesive resin, followed by characteristics of resin bonding to dentin. Bond strengths of MMA/TBB adhesive resin to different adherends were discussed and compared with other bonding systems. Factors affecting bond strength (such as conditioners, primers, and medicaments used for dental treatment), bonding mechanism, and polymerization characteristics of MMA/TBB resin were also discussed. This review further reveals the unique adhesion features between MMA/TBB resin and dentin: in addition to monomer diffusion into the demineralized dentin surface, graft polymerization of MMA onto dentin collagen and interfacial initiation of polymerization at the resin-dentin interface provide the key bonding mechanisms.

The effect of dentinal stimulation on pulp nerve function and pulp morphology in the dog.

PubMed

Hirvonen, T J; Närhi, M V

1986-11-01

The effect of dentinal stimulation on pulpal nerve responses and pulp morphology has been studied in the dog. Canine tooth (n = 25) dentin was stimulated by drilling, probing, and air-blasting for from two to five hours. Acid-etching was used to open dentinal tubules. All test teeth showed disruption of the odontoblast layer and its separation from the predentin; also, dislocation of odontoblast nuclei into dentinal tubules was found in most cases. Single-fiber (n = 14, conduction velocity = 24.3 +/- 7.4 (SD) m/s) recordings of the responses of canine tooth pulpal nerves to dentinal stimulation were made in ten of the stimulated teeth. No changes in the sensitivity of the nerves to dentinal stimulation could be detected. It is concluded that pulpal nerve function and morphological changes of the pulp are not clearly correlated. The condition of the dentin surface seems to be the important factor.

Evaluation of tartar control dentifrices in in vitro models of dentin sensitivity.

PubMed

Mason, S; Levan, A; Crawford, R; Fisher, S; Gaffar, A

1991-01-01

The effects of anticalculus dentifrices were compared with other commercially available dentifrices in in vitro models of dentin sensitivity. Changes in the hydraulic conductance of dentin discs were measured with and without a smear layer before and after treatment and also after a post-treatment acid etch. The capacity of dentifrices to occlude open dentinal tubules in vitro was also assessed by scanning electron microscopy (SEM). There was good correlation (R = 0.98) between our test and values reported in the literature. Tartar control dentifrices gave reductions in fluid flow rates through the dentin discs comparable to those obtained with Promise, Sensodyne, Thermodent and Denquel. Additionally, tartar control dentifrices did not remove microcrystalline debris (smear layers) from the surfaces of dentin in vitro. These results were confirmed by SEM. Thus, according to the hydrodynamic theory of dentin sensitivity, these in vitro results suggest that pyrophosphate-containing dentifrices should reduce dentinal sensitivity.

In vitro dentin permeability after application of Gluma® desensitizer as aqueous solution or aqueous fumed silica dispersion

PubMed Central

ISHIHATA, Hiroshi; FINGER, Werner J.; KANEHIRA, Masafumi; SHIMAUCHI, Hidetoshi; KOMATSU, Masashi

2011-01-01

Objectives To assess and to compare the effects of Gluma® Desensitizer (GDL) with an experimental glutaraldehyde and HEMA containing fumed silica dispersion (GDG) on dentin permeability using a chemiluminous tracer penetration test. Material and Methods Twenty disc-shaped dentin specimens were dissected from extracted human third molars. The dentin specimens were mounted in a split chamber device for determination of permeability under liquid pressure using a photochemical method. Ten specimens were randomly selected and allocated to the evaluation groups Gluma® Desensitizer as aqueous solution and glutaraldehyde/HEMA as fumed silica dispersion, respectively. Dentin disc permeability was determined at two pressure levels after removal of smear with EDTA, after albumin soaking, and after application of the desensitizing agents. Two desensitizer-treated and rinsed specimens of each group were examined by scanning electron microscopy (SEM) for surface remnants. Results Comparatively large standard deviations of the mean EDTA reference and albumin soaked samples permeability values reflected the differences of the dentin substrates. The mean chemiluminescence values of specimen treated with GDL and GDG, respectively, were significantly reduced after topical application of the desensitizing agents on albumin-soaked dentin. The effects of GDL and GDG on permeability were not significantly different. Treated specimens showed no surface remnants after rinsing. Conclusions The experimental desensitizer gel formulation reduced dentin permeability as effectively as the original Gluma® Desensitizer solution. PMID:21552716

Influence of hydrostatic pulpal pressure on the microtensile bond strength of all-in-one self-etching adhesives.

PubMed

Hosaka, Keiichi; Nakajima, Masatoshi; Monticelli, Francesca; Carrilho, Marcela; Yamauti, Monica; Aksornmuang, Juthatip; Nishitani, Yoshihiro; Tay, Franklin R; Pashley, David H; Tagami, Junji

2007-10-01

To evaluate the microtensile bond strength (microTBS) of two all-in-one self-etching adhesive systems and two self-etching adhesives with and without simulated hydrostatic pulpal pressure (PP). Flat coronal dentin surfaces of extracted human molars were prepared. Two all-in-one self-etching adhesive systems, One-Up Bond F (OBF; Tokuyama) and Clearfil S3 Bond (Tri-S, Kuraray Medical) and two self-etching primer adhesives, Clearfil Protect Bond (PB; Kuraray) and Clearfil SE Bond (SE; Kuraray) were applied to the dentin surfaces according to manufacturers' instructions under either a pulpal pressure (PP) of zero or 15 cm H2O. A hybrid resin composite (Clearfil AP-X, Kuraray) was used for the coronal buildup. Specimens bonded under PP were stored in water at 37 degrees C under 15 cm H2O for 24 h. Specimens not bonded under PP were stored under a PP of zero. After storage, the bonded specimens were sectioned into slabs that were trimmed to hourglass-shaped specimens, and were subjected to microtensile bond testing (microTBS). The bond strength data were statistically analyzed using two-way ANOVA and the Holm-Sidak method for multiple comparison tests (alpha = 0.05). The surface area percentage of different failure modes for each material was also statistically analyzed with three one-way ANOVAs and Tukey's multiple comparison tests. The microTBS of OBF and Tri-S fell significantly under PP. However, in the, PB and SE bonded specimens under PP, there were no significant differences compared with the control groups without PP. The microTBS of the two all-in-one adhesive systems decreased when PP was applied. However, the microTBS of both self-etching primer adhesives did not decrease under PP.

DESENSITIZING BIOACTIVE AGENTS IMPROVES BOND STRENGTH OF INDIRECT RESIN-CEMENTED RESTORATIONS: PRELIMINARY RESULTS

PubMed Central

Pires-De-Souza, Fernanda de Carvalho Panzeri; de Marco, Fabíola Fiorezi; Casemiro, Luciana Assirati; Panzeri, Heitor

2007-01-01

Objective: The aim of this study was to assess the bond strength of indirect composite restorations cemented with a resin-based cement associated with etch-and-rinse and self-etching primer adhesive systems to dentin treated or not with a bioactive material. Materials and Method: Twenty bovine incisor crowns had the buccal enamel removed and the dentin ground flat. The teeth were assigned to 4 groups (n=5): Group I: acid etching + Prime & Bond NT (Dentsply); Group II: application of a bioactive glass (Biosilicato®)+ acid etching + Prime & Bond NT; Group III: One-up Bond F (J Morita); Group IV: Biosilicato® + One-up Bond F. Indirect composite resin (Artglass, Kulzer) cylinders (6x10mm) were fabricated and cemented to the teeth with a dualcure resin-based cement (Enforce, Dentsply). After cementation, the specimens were stored in artificial saliva at 37oC for 30 days and thereafter tested in tensile strength in a universal testing machine (EMIC) with 50 kgf load cell at a crosshead speed of 1 mm/min. Failure modes were assessed under scanning electron microscopy. Data were analyzed statistically by ANOVA and Tukey's test (95% level of confidence). Results: Groups I, II and III had statistically similar results (p>0.05). Group IV had statistically significant higher bond strength means (p<0.05) than the other groups. The analysis of the debonded surfaces showed a predominance of adhesive failure mode for Group III and mixed failure mode for the other groups. Conclusion: The use of desensitizing agent did not affect negatively the bonding of the indirect composite restorations to dentin, independently of the tested adhesive systems. PMID:19089114

Etidronate from Medicine to Endodontics: effects of different irrigation regimes on root dentin roughness

PubMed Central

TARTARI, Talita; DUARTE JUNIOR, Anivaldo Pereira; SILVA JÚNIOR, José Otávio Carrera; KLAUTAU, Eliza Burlamaqui; SILVA E SOUZA JUNIOR, Mario Honorato; SILVA E SOUZA, Patrícia de Almeida Rodrigues

2013-01-01

An increase in dentin roughness, associated with surface composition, contributes to bacterial adherence in recontaminations. Surface roughness is also important for micromechanical interlocking of dental materials to dentin, and understanding the characteristics of the surface is essential to obtain the adhesion of root canal sealers that have different physico-chemical characteristics. Objectives To evaluate the effects of sodium hypochlorite (NaOCl), ethylenediaminetetraacetic (EDTA), etidronic (HEBP), and citric acid (CA) associated with different irrigation regimens on root dentin roughness. Material and Methods Forty-five root halves of anterior teeth were used. The root parts were sectioned in thirds, embedded in acrylic resin and polished to a standard surface roughness. Initially, the samples of each third were randomly assigned into 3 groups and treated as follows: G1 - saline solution (control); G2 - 5% NaOCl+18% HEBP mixed in equal parts; and G3 - 2.5% NaOCl. After initial measuments, the G3 samples were distributed into subgroups G4, G5 and G6, which were subjected to 17% EDTA, 10% CA and 9% HEBP, respectively. Following the new measuments, these groups received a final flush with 2.5% NaOCl, producing G7, G8 and G9. The dentin surface roughness (Ra) was determined before and after treatments using a profilometer. The Wilcoxon test (α<0.05) was used to compare the values before and after treatments, and the Friedman test (α<0.05) to detect any differences among root thirds. Results (i) NaOCl did not affect the surface roughness; (ii) there was a significant increase in roughness after the use of chelating agents (P<0.01); and (iii) only the G3 group showed a difference in surface roughness between apical third and other thirds of the teeth (P<0.0043). Conclusion Only the irrigation regimens that used chelating agents altered the roughness of root dentin. PMID:24212986

Etidronate from medicine to endodontics: effects of different irrigation regimes on root dentin roughness.

PubMed

Tartari, Talita; Duarte Junior, Anivaldo Pereira; Silva Júnior, José Otávio Carrera; Klautau, Eliza Burlamaqui; Silva E Souza Junior, Mario Honorato; Silva E Souza Junior, Patrícia de Almeida Rodrigues

2013-01-01

An increase in dentin roughness, associated with surface composition, contributes to bacterial adherence in recontaminations. Surface roughness is also important for micromechanical interlocking of dental materials to dentin, and understanding the characteristics of the surface is essential to obtain the adhesion of root canal sealers that have different physico-chemical characteristics. To evaluate the effects of sodium hypochlorite (NaOCl), ethylenediaminetetraacetic (EDTA), etidronic (HEBP), and citric acid (CA) associated with different irrigation regimens on root dentin roughness. Forty-five root halves of anterior teeth were used. The root parts were sectioned in thirds, embedded in acrylic resin and polished to a standard surface roughness. Initially, the samples of each third were randomly assigned into 3 groups and treated as follows: G1 - saline solution (control); G2 - 5% NaOCl+18% HEBP mixed in equal parts; and G3 - 2.5% NaOCl. After initial measuments, the G3 samples were distributed into subgroups G4, G5 and G6, which were subjected to 17% EDTA, 10% CA and 9% HEBP, respectively. Following the new measuments, these groups received a final flush with 2.5% NaOCl, producing G7, G8 and G9. The dentin surface roughness (Ra) was determined before and after treatments using a profilometer. The Wilcoxon test (α<0.05) was used to compare the values before and after treatments, and the Friedman test (α<0.05) to detect any differences among root thirds. (i) NaOCl did not affect the surface roughness; (ii) there was a significant increase in roughness after the use of chelating agents (P<0.01); and (iii) only the G3 group showed a difference in surface roughness between apical third and other thirds of the teeth (P<0.0043). Only the irrigation regimens that used chelating agents altered the roughness of root dentin.

Efficacy of different whitening modalities on bovine enamel and dentin.

PubMed

Wiegand, Annette; Vollmer, Doreen; Foitzik, Magdalena; Attin, Rengin; Attin, Thomas

2005-06-01

Previous studies have shown that bleaching treatment may be efficient in both enamel and dentin, but it is still unknown how much the subsurface dentin contributes to the color change of teeth. This in vitro study evaluated the whitening effect of different external bleaching agents on enamel-dentin slabs and subsurface dentin. Ninety bovine teeth were distributed among six groups (A, Opalescence 10%; B, Opalescence PF 15%; C, Opalescence Quick; D, Opalescence Extra Boost; E, Rapid White; F, Whitestrips). Two enamel-dentin specimens were prepared from the labial surface of each teeth. In one of the specimens enamel was removed, resulting in a dentin (CD) disc of 1 mm high. The labial and the pulpal sides of the second specimen were ground until the remaining enamel and dentin layers of the enamel-dentin sample (ED) were 1 mm each. Whitening treatment of the ED specimens was performed according to manufacturers' instructions. Pre- and posttreatment Lab values of ED samples were analyzed using CIE-Lab. Baseline Lab values of dentin were analyzed by evaluation of the CD specimen. Finally, enamel of the ED specimens was removed and color change of the exposed dentin (D) was recorded. For all treatment agents significant color changes (DeltaE) were observed for enamel-dentin samples and subsurface dentin specimens compared to controls. In groups A-D DeltaE was significantly higher in dentin than enamel-dentin. Furthermore, L and b values of bleached enamel-dentin and subsurface dentin samples differed significantly from baseline. Treatment with the tested external whitening bleaching agents resulted in color change of both enamel-dentin and subsurface dentin samples. The results indicate that color change of treated teeth might be highly influenced by color change of the subsurface dentin.

High-speed scanning ablation of dental hard tissues with a λ = 9.3 μm CO2 laser: adhesion, mechanical strength, heat accumulation, and peripheral thermal damage

PubMed Central

Nguyen, Daniel; Chang, Kwang; Hedayatollahnajafi, Saba; Staninec, Michal; Chan, Kenneth; Lee, Robert; Fried, Daniel

2011-01-01

CO2 lasers can be operated at high laser pulse repetition rates for the rapid and precise removal of dental decay. Excessive heat accumulation and peripheral thermal damage is a concern when using high pulse repetition rates. Peripheral thermal damage can adversely impact the mechanical strength of the irradiated tissue, particularly for dentin, and reduce the adhesion characteristics of the modified surfaces. The interpulpal temperature rise was recorded using microthermocouples situated at the roof of the pulp chamber on teeth that were occlusally ablated using a rapidly-scanned CO2 laser operating at 9.3 μm with a pulse duration of 10 to 15 μs and repetition rate of 300 Hz over a 2 min time course. The adhesion strength of laser treated enamel and dentin surfaces was measured for various laser scanning parameters with and without post-ablation acid etching using the single-plane shear test. The mechanical strength of laser-ablated dentin surfaces were determined via the four-point bend test and compared to control samples prepared with 320 grit wet sand paper to simulate conventional preparations. Thermocouple measurements indicated that the temperature remained below ambient temperature if water-cooling was used. There was no discoloration of either dentin or enamel laser treated surfaces, the surfaces were uniformly ablated, and there were no cracks visible. Four-point bend tests yielded mean mechanical strengths of 18.2 N (s.d. = 4.6) for ablated dentin and 18.1 N (s.d. = 2.7) for control (p > 0.05). Shear tests yielded mean bond strengths approaching 30 MPa for both enamel and dentin under certain irradiation conditions. These values were slightly lower than nonirradiated acid-etched control samples. Additional studies are needed to determine if the slightly lower bond strength than the acid-etched control samples is clinically significant. These measurements demonstrate that enamel and dentin surfaces can be rapidly ablated by CO2 lasers with minimal peripheral thermal and mechanical damage and without excessive heat accumulation. PMID:21806256

High-speed scanning ablation of dental hard tissues with a λ = 9.3 μm CO2 laser: adhesion, mechanical strength, heat accumulation, and peripheral thermal damage

NASA Astrophysics Data System (ADS)

Nguyen, Daniel; Chang, Kwang; Hedayatollahnajafi, Saba; Staninec, Michal; Chan, Kenneth; Lee, Robert; Fried, Daniel

2011-07-01

CO2 lasers can be operated at high laser pulse repetition rates for the rapid and precise removal of dental decay. Excessive heat accumulation and peripheral thermal damage is a concern when using high pulse repetition rates. Peripheral thermal damage can adversely impact the mechanical strength of the irradiated tissue, particularly for dentin, and reduce the adhesion characteristics of the modified surfaces. The interpulpal temperature rise was recorded using microthermocouples situated at the roof of the pulp chamber on teeth that were occlusally ablated using a rapidly-scanned CO2 laser operating at 9.3 μm with a pulse duration of 10 to 15 μs and repetition rate of 300 Hz over a 2 min time course. The adhesion strength of laser treated enamel and dentin surfaces was measured for various laser scanning parameters with and without post-ablation acid etching using the single-plane shear test. The mechanical strength of laser-ablated dentin surfaces were determined via the four-point bend test and compared to control samples prepared with 320 grit wet sand paper to simulate conventional preparations. Thermocouple measurements indicated that the temperature remained below ambient temperature if water-cooling was used. There was no discoloration of either dentin or enamel laser treated surfaces, the surfaces were uniformly ablated, and there were no cracks visible. Four-point bend tests yielded mean mechanical strengths of 18.2 N (s.d. = 4.6) for ablated dentin and 18.1 N (s.d. = 2.7) for control (p > 0.05). Shear tests yielded mean bond strengths approaching 30 MPa for both enamel and dentin under certain irradiation conditions. These values were slightly lower than nonirradiated acid-etched control samples. Additional studies are needed to determine if the slightly lower bond strength than the acid-etched control samples is clinically significant. These measurements demonstrate that enamel and dentin surfaces can be rapidly ablated by CO2 lasers with minimal peripheral thermal and mechanical damage and without excessive heat accumulation.

High-speed scanning ablation of dental hard tissues with a λ = 9.3 μm CO2 laser: adhesion, mechanical strength, heat accumulation, and peripheral thermal damage.

PubMed

Nguyen, Daniel; Chang, Kwang; Hedayatollahnajafi, Saba; Staninec, Michal; Chan, Kenneth; Lee, Robert; Fried, Daniel

2011-07-01

CO(2) lasers can be operated at high laser pulse repetition rates for the rapid and precise removal of dental decay. Excessive heat accumulation and peripheral thermal damage is a concern when using high pulse repetition rates. Peripheral thermal damage can adversely impact the mechanical strength of the irradiated tissue, particularly for dentin, and reduce the adhesion characteristics of the modified surfaces. The interpulpal temperature rise was recorded using microthermocouples situated at the roof of the pulp chamber on teeth that were occlusally ablated using a rapidly-scanned CO(2) laser operating at 9.3 μm with a pulse duration of 10 to 15 μs and repetition rate of 300 Hz over a 2 min time course. The adhesion strength of laser treated enamel and dentin surfaces was measured for various laser scanning parameters with and without post-ablation acid etching using the single-plane shear test. The mechanical strength of laser-ablated dentin surfaces were determined via the four-point bend test and compared to control samples prepared with 320 grit wet sand paper to simulate conventional preparations. Thermocouple measurements indicated that the temperature remained below ambient temperature if water-cooling was used. There was no discoloration of either dentin or enamel laser treated surfaces, the surfaces were uniformly ablated, and there were no cracks visible. Four-point bend tests yielded mean mechanical strengths of 18.2 N (s.d. = 4.6) for ablated dentin and 18.1 N (s.d. = 2.7) for control (p > 0.05). Shear tests yielded mean bond strengths approaching 30 MPa for both enamel and dentin under certain irradiation conditions. These values were slightly lower than nonirradiated acid-etched control samples. Additional studies are needed to determine if the slightly lower bond strength than the acid-etched control samples is clinically significant. These measurements demonstrate that enamel and dentin surfaces can be rapidly ablated by CO(2) lasers with minimal peripheral thermal and mechanical damage and without excessive heat accumulation.

Study on the potential inhibition of root dentine wear adjacent to fluoride-containing restorations.

PubMed

Turssi, Cecilia Pedroso; Hara, Anderson Takeo; Domiciano, Silvia Jorge; Serra, Mônica Campos

2008-01-01

The purpose of this in vitro study was to determine whether the vicinity of root dentine that had been restored with fluoride-releasing materials was at reduced risk for erosive/abrasive wear compared to root dentine restored with a non-fluoride-containing material. According to a randomized complete block design, standardized cavities prepared on the surface of 150 bovine root dentine slabs were restored with glass-ionomer cement, resin-modified glass ionomer, polyacid-modified resin composite, fluoride-containing or conventional composite. Specimens were coated with two layers of an acid-resistant nail varnish exposing half of the dentine surface and half of the restoration. Subsequently, specimens were either eroded in an acidic drink or left uneroded, then exposed to artificial saliva and abraded in a toothbrushing machine. Wear depth in the vicinity of restorations was quantified by a stylus profilometer, based on the nonabraded areas surrounding the erosion/abrasion region. Two-way ANOVA did not demonstrate significant interaction between restoratives and eroded-uneroded dentine (p=0.5549) nor significant difference among restorative materials (p=0.8639). Tukey's test ascertained that the wear depth was higher for eroded than for uneroded groups. Fluoride-releasing materials seemed to negligibly inhibit wear in the vicinity of restored root dentine subjected to erosive/abrasive challenges.

Investigation of biomineralization by Raman spectroscopy

NASA Astrophysics Data System (ADS)

Fatscher, Robert William

Biomineralization is a process in which living organism grow composite materials consisting of inorganic and organic materials. This produces a composite material consisting of both inorganic and organic components, with superior mechanical properties. In the human body bone and dentin are both examples of biominerals. In this research Raman spectroscopy was used to characterize dentin from mice and human teeth, to determine composition. In the mouse tooth samples areas of irregular dentin were found, along the inside of the tooth, to be in the process of mineralization. By analyzing the samples along these areas we were able to determine the composition of dentin and track how it changed in these area. By analysis of the mineral to matrix ratio the areas of irregular dentin were determined to have less mineral present. Observations of other organic components and collagen in increased concentrations in this area suggested these area were in the process of biomineralization. The understanding of the structure of dentin and its biomineralization process is of crucial importance when trying reproduce dentin. Scientists and engineers are able to produce dentin minerals in vitro by culturing various dental stem cells. The ability to create dentin mineral from cells could lead to methods of repairing dentin in patients, or even lead to the creation of a completely engineered tooth. While dentin-like materials can be produced in a laboratory environment, analysis and comparison of the composition of these materials must be performed to ensure the mineral produced is consistent with dentin. Mineralized nodules from six different dental stem cell lines were cultured to produce a mineralized deposit. Utilizing Raman spectroscopy, we were able to determine cell source dependent differences in a variety of dental stem cells, and compare the mineral produced to native dentin. Orthopedic implants are implants used to replace damaged bone, examples include knee, hip and dental implants. These implants are designed to osteointegrate with the native healthy tissues in order to create a functionally stable and structural interface. Biomaterials such as hydroxyapatite and titania are known to increase the rate of bone regeneration in vivo.1 By accelerating the early response of bone forming cells to these implants, better fixation is achieved between the implant and the bone, shortening recovery times and increasing the viability of these implants. In the last part of this research an investigation of osteoblasts cultured at 14 days on five different heat-treated titania substrates was investigated by Raman spectroscopy, in order to observe the initial cellular response to the titania substrates. The heat-treatment of titania changes the amount of oxygen on it's surface which in turn effects the surface energy. A change in the surface energy of a material will affect the cellular response, by culturing cells on various heat-treated titania substrates a relationship between the surface energy and cellular response can be investigated. A faster cellular response would lead to an increased rate of bone regeneration shortening healing times and allowing for better fixation of the implant.

Effects of dentin surface treatments on shear bond strength of glass-ionomer cements

PubMed Central

Poggio, Claudio; Beltrami, Riccardo; Scribante, Andrea; Colombo, Marco; Lombardini, Marco

2014-01-01

Summary Aim The aim of this in vitro study was to evaluate the effect of different surface treatments on shear bond strength of a conventional glass-ionomer cement (GIC) and a resin-modified glass-ionomer cement (RMGIC) to dentin. Materials and methods 80 bovine permanent incisors were used. 40 cylindrical specimens of a GIC (Fuji IX GP Extra) and 40 cylindrical specimens of a RMGIC (Fuji II LC) were attached to the dentin. The teeth were then randomly assigned to 8 groups of equal size (n=10), 4 for every type of glass-ionomer cement, corresponding to type of dentin surface treatments. Group 1: GC Cavity Conditioner; Group 2: 37% phosphoric acid gel; Group 3: Clearfil SE Bond; Group 4: no dentin conditioning (control). The specimens were placed in a universal testing machine (Model 3343, Instron Corp., Canton, Mass., USA) and subsequently tested for shear bond strength (MPa). Results ANOVA showed the presence of significant differences among the various groups. Post hoc Tukey test showed different values of shear bond strength for Fuji IX GP Extra and for Fuji II LC. The different conditioners variably influence the adhesion of the glass-ionomer cements tested. Conclusions. RMGIC shear bond to dentin was higher than GIC. The use of a Self-etch adhesive system improved the shear bond strength values of RMGIC and lowered the shear bond strength values of GIC significantly. PMID:24753797

Time of Application of Sodium Ascorbate on Bonding to Bleached Dentin.

PubMed

Jung, Kyoung-Hwa; Seon, Eun-Mi; Choi, An-Na; Kwon, Yong-Hoon; Son, Sung-Ae; Park, Jeong-Kil

2017-01-01

This study examined the effects of different application times of sodium ascorbate (SA) on the bond strength of composite resin to bleached dentin. Specimens with an exposed dentin surface were divided into 3 groups according to the type of bleaching agent used: Group A, mixture of sodium perborate (SP) and distilled water (DW); Group B, mixture of SP and hydrogen peroxide (HP); control group, no bleaching. Each group was classified into 10 subgroups. Subgroups IB and DB underwent immediate bonding and delayed bonding, respectively. 10% SA was applied to 3, 5, 10, and 30 minutes and 1, 24, 48, and 72 hours, respectively. Microtensile bond strength ( μ TBS) was measured after restoration, and the data was analyzed by one-way ANOVA and Scheffé's test. Before restoration, the dentin surfaces were examined by scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). SEM showed that most dentin surfaces were filled with crystals when SA was applied to more than 24 hours. EDS revealed peaks of calcium, carbon, oxygen, and sodium. The application of SA for 5 minutes to 48 hours or for 30 minutes to 24 hours is suggested when a mixture of SP and DW or HP is used, respectively.

Effect of property gradients on enamel fracture in human molar teeth.

PubMed

Barani, Amir; Bush, Mark B; Lawn, Brian R

2012-11-01

A model for the fracture of tooth enamel with graded elastic modulus and toughness is constructed using an extended finite element modeling (XFEM) package. The property gradients are taken from literature data on human molars, with maximum in modulus at the outer enamel surface and in toughness at the inner surface. The tooth is modeled as a brittle shell (enamel) and a compliant interior (dentin), with occlusal loading from a hard, flat contact at the cusp. Longitudinal radial (R) and margin (M) cracks are allowed to extend piecewise along the enamel walls under the action of an incrementally increasing applied load. A simple stratagem is deployed in which fictitious temperature profiles generate the requisite property gradients. The resulting XFEM simulations demonstrate that the crack fronts become more segmented as the property gradients become more pronounced, with enhanced propagation at the outer surface and inhibited propagation at the inner. Whereas the growth history of the cracks is profoundly influenced by the gradients, the ultimate critical loads required to attain full fractures are relatively unaffected. Some implications concerning dentistry are considered. Copyright © 2012 Elsevier Ltd. All rights reserved.

Catechol-Functionalized Synthetic Polymer as a Dental Adhesive to Contaminated Dentin Surface for a Composite Restoration.

PubMed

Lee, Sang-Bae; González-Cabezas, Carlos; Kim, Kwang-Mahn; Kim, Kyoung-Nam; Kuroda, Kenichi

2015-08-10

This study reports a synthetic polymer functionalized with catechol groups as dental adhesives. We hypothesize that a catechol-functionalized polymer functions as a dental adhesive for wet dentin surfaces, potentially eliminating the complications associated with saliva contamination. We prepared a random copolymer containing catechol and methoxyethyl groups in the side chains. The mechanical and adhesive properties of the polymer to dentin surface in the presence of water and salivary components were determined. It was found that the new polymer combined with an Fe(3+) additive improved bond strength of a commercial dental adhesive to artificial saliva contaminated dentin surface as compared to a control sample without the polymer. Histological analysis of the bonding structures showed no leakage pattern, probably due to the formation of Fe-catechol complexes, which reinforce the bonding structures. Cytotoxicity test showed that the polymers did not inhibit human gingival fibroblast cells proliferation. Results from this study suggest a potential to reduce failure of dental restorations due to saliva contamination using catechol-functionalized polymers as dental adhesives.

Catechol-Functionalized Synthetic Polymer as a Dental Adhesive to Contaminated Dentin Surface for a Composite Restoration

PubMed Central

2015-01-01

This study reports a synthetic polymer functionalized with catechol groups as dental adhesives. We hypothesize that a catechol-functionalized polymer functions as a dental adhesive for wet dentin surfaces, potentially eliminating the complications associated with saliva contamination. We prepared a random copolymer containing catechol and methoxyethyl groups in the side chains. The mechanical and adhesive properties of the polymer to dentin surface in the presence of water and salivary components were determined. It was found that the new polymer combined with an Fe3+ additive improved bond strength of a commercial dental adhesive to artificial saliva contaminated dentin surface as compared to a control sample without the polymer. Histological analysis of the bonding structures showed no leakage pattern, probably due to the formation of Fe–catechol complexes, which reinforce the bonding structures. Cytotoxicity test showed that the polymers did not inhibit human gingival fibroblast cells proliferation. Results from this study suggest a potential to reduce failure of dental restorations due to saliva contamination using catechol-functionalized polymers as dental adhesives. PMID:26176305

Bacterial reduction and dentin microhardness after treatment by a pulsed fiber optic delivered Nd:YAG laser

NASA Astrophysics Data System (ADS)

Goodis, Harold E.; White, Joel M.; Marshall, Sally J.; Marshall, Grayson W.

1994-09-01

The purpose of this study was to determine the microhardness and extent of bacterial reduction of contaminated dentin following pulsed fiber optic delivered Nd:YAG laser exposure. Knoop hardness was determined before and after laser exposures from 0.3 to 3.0 W and repetition rates of 10 to 30 Hz. Half the sections were covered with an organic black pigment before laser exposure to evaluate the use of the pigment as an initiator to increase laser absorbance on the surface. Repeated measures design was employed to determine the microhardness of cut and polished dentin sections. Additional dentin sections were sterilized by gamma irradiation and then inoculated with B. subtilis, E. coli or B. stearothermophilus. The contaminated sections were exposed to contact delivered Nd:YAG laser. Cultures were obtained from the dentin surfaces and the colony forming units counted. Increased microhardness was found for all laser treatments above the physical modification. Bacterial reduction was obtained but complete sterilization was not.

The acid-base resistant zone in three dentin bonding systems.

PubMed

Inoue, Go; Nikaido, Toru; Foxton, Richard M; Tagami, Junji

2009-11-01

An acid-base resistant zone has been found to exist after acid-base challenge adjacent to the hybrid layer using SEM. The aim of this study was to examine the acid-base resistant zone using three different bonding systems. Dentin disks were applied with three different bonding systems, and then a resin composite was light-cured to make dentin disk sandwiches. After acid-base challenge, the polished surfaces were observed using SEM. For both one- and two-step self-etching primer systems, an acid-base resistant zone was clearly observed adjacent to the hybrid layer - but with differing appearances. For the wet bonding system, the presence of an acid-base resistant zone was unclear. This was because the self-etching primer systems etched the dentin surface mildly, such that the remaining mineral phase of dentin and the bonding agent yielded clear acid-base resistant zones. In conclusion, the acid-base resistant zone was clearly observed when self-etching primer systems were used, but not so for the wet bonding system.

Treatment of dentinal tubules by Nd:YAG laser

NASA Astrophysics Data System (ADS)

Chmelíčkova, Hana; Zapletalova, Zdeňka; Peřina, Jan, Jr.; Novotný, Radko; Kubínek, Roman; Stranyánek, Martin

2005-08-01

Symptom of cervical dentine hypersensitivity attacks from 10% to 15% of population and causes an uncomfortable pain during contact with any matter. Sealing of open dentinal tubules is one of the methods to reach insensibility. Laser as a source of coherent radiation is used to melt dentine surface layers. Melted dentine turns to hard mass with a smooth, non-porous surface. Simulation of this therapy was made in vitro by means of LASAG Nd:YAG pulsed laser system KLS 246-102. Eighty human extracted teeth were cut horizontally to obtain samples from 2 mm to 3 mm thick. First experiments were done on cross section surfaces to find an optimal range of laser parameters. A wide range of energies from 30 mJ to 210 mJ embedded in 0,3 ms long pulse was tested. Motion in X and Y axes was ensured by a CNC driven table and the pulse frequency 15 Hz was chosen to have a suitable overlap of laser spots. Some color agents were examined with the aim to improve surface absorption. Scanning Electron Microscopy was used to evaluate all samples and provided optimal values of energies around 50 J.cm-2. Next experiments were done with the beam oriented perpendicularly to a root surface, close to the real situation. Optical fibers with the diameter of 0,6 mm and 0,2 mm were used to guide a laser beam to teeth surfaces. Laser processing heads with lens F = 100 mm and F = 50 mm were used. The best samples were investigated by means of the Atomic Force Microscopy.

Microleakage in Class V Composite Restorations after Desensitizing Surface Treatment with Er:YAG and CO2 Lasers.

PubMed

Mozaffari, Hamid Reza; Ehteshami, Alireza; Zallaghi, Farshad; Chiniforush, Nasim; Moradi, Zohreh

2016-12-30

Aims: Glutaraldehyde, CO 2 and Er:YAG lasers can be used for treatment of dentin hypersensitivity. However, their application may have adverse effects on the clinical service of restorations. This study aimed to assess the microleakage in composite restorations following surface treatment with Glutaraldehyde desensitizer, CO 2 and Er:YAG laser irradiation for treatment of dentin hypersensitivity. Materials and methods: This experimental study was conducted on 60 extracted sound human teeth. Class V cavities were prepared measuring 3×3 mm using a diamond bur. Specimens were randomly divided into 4 groups of 15. Group one:no surface treatment, Group two:applying Glutaraldehyde desensitizer, Groups of three and four were irradiated with CO 2 and Er:YAG lasers, respectively. Surfaces were restored with bonding agent (Single Bond 2, 3M, USA) and Z250 composite (3M, USA). Specimens were thermocycled and immersed in 1% methylene blue solution for 24 hours. Microleakage scores were assessed under a stereomicroscope at ×20 magnification. Data were analyzed using SPSS and the Kruskal Wallis test (P=0.05). Results: There was no significant difference between microleakage of groups in enamel margins (P=0.694). The difference in microleakage at the dentin margin was significant between groups (P=0.018). Conclusions: Application of Glutaraldehyde-desensitizer and CO 2 laser irradiation of surfaces prior to composite restoration do not increase microleakage at the enamel or dentin margins but tooth surface treatment with Er:YAG laser significantly increased the microleakage at the dentin margins.

Shear bond strength of resin composite bonded with two adhesives: Influence of Er: YAG laser irradiation distance

PubMed Central

Shirani, Farzaneh; Birang, Reza; Malekipour, Mohammad Reza; Hourmehr, Zahra; Kazemi, Shantia

2014-01-01

Background: Dental surfaces prepared with different Er:YAG laser distance may have different characteristics compared with those prepared with conventional instruments. The aim of this study was to investigate the effect of Er:YAG laser irradiation distance from enamel and dentin surfaces on the shear bond strength of composite with self-etch and etch and rinse bonding systems compared with conventional preparation method. Materials and Methods: Two hundred caries-free human third molars were randomly divided into twenty groups (n = 10). Ten groups were designated for enamel surface (E1-E10) and ten for dentin surface (D1-D10). Er: YAG laser (2940 nm) was used on the E1-E8 (240 mJ, 25 Hz) and D1-D8 (140 mJ, 30 Hz) groups at four different distances of 0.5 (standard), 2, 4 and 11 mm. Control groups (E9, E10, D9 and D10) were ground with medium grit diamond bur. The enamel and dentin specimens were divided into two subgroups that were bonded with either Single Bond or Clearfil SE Bond. Resin composite (Z100) was dispensed on prepared dentin and enamel. The shear bond strengths were tested using a universal testing machine. Data were analyzed by SPSS12 statistical software using three way analysis of variance, Tukey and independent t-test. P < 0.05 was considered as significant. Results: There was a significant difference between enamel and dentin substrates (P < 0.001) and between lased and un-lased groups; the un-lased group had significantly higher bond strength (P < 0.001). Shear bond strength increased significantly with an increase in the laser irradiation distance (P < 0.05) on enamel surfaces (in both bonding agent subgroups) and on dentin surfaces (in the Single Bond subgroup). Conclusion: Laser irradiation decreases shear bond strength. Irradiation distance affects shear bond strength and increasing the distance would decrease the negative effects of laser irradiation. PMID:25540665

Effects of Dentifrice Containing Hydroxyapatite on Dentinal Tubule Occlusion and Aqueous Hexavalent Chromium Cations Sorption: A Preliminary Study

PubMed Central

Liu, Jing; Hou, Yarong; Zhu, Manqun; Huang, Jiansheng; Xu, Pingping

2012-01-01

In order to endow environmental protection features to dentifrice, hydroxyapatite (HA) was added to ordinary dentifrice. The effects on dentinal tubule occlusion and surface mineralization were compared after brushing dentine discs with dentifrice with or without HA. The two types of dentifrice were then added to 100 µg/ml of hexavalent chromium cation (Cr6+) solution in order to evaluate their capacities of adsorbing Cr6+ from water. Our results showed that the dentifrice containing HA was significantly better than the ordinary dentifrice in occluding the dentinal tubules with a plugging rate greater than 90%. Moreover, the effect of the HA dentifrice was persistent and energy-dispersive spectrometer (EDS) revealed that the atomic percentages of calcium and phosphorus on the surface of dentine discs increased significantly. Adding HA to ordinary dentifrice significantly enhanced the ability of dentifrice to adsorb Cr6+ from water with the removal rate up to 52.36%. In addition, the sorption was stable. Our study suggests that HA can be added to ordinary dentifrice to obtain dentifrice that has both relieving dentin hypersensitivity benefits and also helps to control environmental pollution. PMID:23300511

Enamel and Dentin Surface Finishing Influence on the Roughness and Microshear Bond Strength of a Lithium Silicate Glass-Ceramic for Laminate Veneers

PubMed Central

Gonzaga, Carla Castiglia; Bravo, Ruth Peggy; Pavelski, Thiago Vinícius; Garcia, Paula Pontes; Correr, Gisele Maria; Leonardi, Denise Piotto; da Cunha, Leonardo Fernandes; Furuse, Adilson Yoshio

2015-01-01

Objectives. This study evaluated the influence of cavity surface finishing with diamond burs of different grit mounted on high-speed turbine and ultrasound on the roughness and microshear bond strength (MBS) of a lithium silicate glass-ceramic to enamel and dentin. Methods. Enamel and dentin specimens were divided into seven groups, according to the type of surface finishing: 1200-grit sandpaper (control), two different brands of medium-grit and fine-grit diamond burs in a high-speed turbine; medium-grit and fine-grit CVD (chemical vapor deposition) tips in an ultrasonic device. Roughness parameters (n = 5) and MSBS to a glass-ceramic (n = 10) were determined. Data were analyzed using ANOVA and Tukey's test (α = 5%). Results. Control group showed lower mean roughness readings and groups that used medium-grit diamond burs showed the highest mean roughness values. Regarding MSBS, there was no statistical difference when comparing the groups gritted with the same brand of medium- and fine-grit burs and tips. Conclusions. Cavity surface finishing influenced the roughness parameters and MSBS of a glass-ceramic to enamel and dentin. Medium-grit diamond burs in high-speed turbine showed the highest mean roughness values. Fine-grit CVD tips in ultrasound presented the highest MSBS values for both enamel and dentin. PMID:27347507

Enamel and Dentin Surface Finishing Influence on the Roughness and Microshear Bond Strength of a Lithium Silicate Glass-Ceramic for Laminate Veneers.

PubMed

Gonzaga, Carla Castiglia; Bravo, Ruth Peggy; Pavelski, Thiago Vinícius; Garcia, Paula Pontes; Correr, Gisele Maria; Leonardi, Denise Piotto; da Cunha, Leonardo Fernandes; Furuse, Adilson Yoshio

2015-01-01

Objectives. This study evaluated the influence of cavity surface finishing with diamond burs of different grit mounted on high-speed turbine and ultrasound on the roughness and microshear bond strength (MBS) of a lithium silicate glass-ceramic to enamel and dentin. Methods. Enamel and dentin specimens were divided into seven groups, according to the type of surface finishing: 1200-grit sandpaper (control), two different brands of medium-grit and fine-grit diamond burs in a high-speed turbine; medium-grit and fine-grit CVD (chemical vapor deposition) tips in an ultrasonic device. Roughness parameters (n = 5) and MSBS to a glass-ceramic (n = 10) were determined. Data were analyzed using ANOVA and Tukey's test (α = 5%). Results. Control group showed lower mean roughness readings and groups that used medium-grit diamond burs showed the highest mean roughness values. Regarding MSBS, there was no statistical difference when comparing the groups gritted with the same brand of medium- and fine-grit burs and tips. Conclusions. Cavity surface finishing influenced the roughness parameters and MSBS of a glass-ceramic to enamel and dentin. Medium-grit diamond burs in high-speed turbine showed the highest mean roughness values. Fine-grit CVD tips in ultrasound presented the highest MSBS values for both enamel and dentin.

Evaluation of the bond strength of resin cements used to lute ceramics on laser-etched dentin.

PubMed

Giray, Figen Eren; Duzdar, Lale; Oksuz, Mustafa; Tanboga, Ilknur

2014-07-01

The purpose of this study was to investigate the shear bond strength (SBS) of two different adhesive resin cements used to lute ceramics on laser-etched dentin. Erbium, chromium: yttrium, scandium, gallium, garnet (Er,Cr:YSGG) laser irradiation has been claimed to improve the adhesive properties of dentin, but results to date have been controversial, and its compatibility with existing adhesive resin cements has not been conclusively determined. Two adhesive cements, one "etch-and-rinse" [Variolink II (V)] and one "self-etch" [Clearfil Esthetic Cement (C)] luting cement, were used to lute ceramic blocks (Vita Celay Blanks, Vita) onto dentin surfaces. In total, 80 dentin specimens were distributed randomly into eight experimental groups according to the dentin surface-etching technique used Er,Cr:YSGG laser and Er:YAG laser: (1) 37% orthophosphoric acid+V (control group), (2) Er,Cr:YSGG laser+V, (3) Er,Cr:YSGG laser+acid+V, (4) Er:YAG laser+V, (5) Er:YAG laser+acid+V, (6) C, (7) Er,Cr:YSGG laser+C, and (8) Er:YAG laser+C. Following these applications, the ceramic discs were bonded to prepared surfaces and were shear loaded in a universal testing machine until fracture. SBS was recorded for each group in MPa. Shear test values were evaluated statistically using the Mann-Whitney U test. No statistically significant differences were evident between the control group and the other groups (p>0.05). The Er,Cr:YSGG laser+A+V group demonstrated significantly higher SBS than did the Er,Cr:YSGG laser+V group (p=0.034). The Er,Cr:YSGG laser+C and Er:YAG laser+C groups demonstrated significantly lower SBS than did the C group (p<0.05). Dentin surfaces prepared with lasers may provide comparable ceramic bond strengths, depending upon the adhesive cement used.

[Influence of different designs of marginal preparation on stress distribution in the mandibular premolar restored with endocrown].

PubMed

Guo, Jing; Wang, Xiao-Yu; Li, Xue-Sheng; Sun, Hai-Yang; Liu, Lin; Li, Hong-Bo

2016-02-01

To evaluate the effect of different designs of marginal preparation on stress distribution in the mandibular premolar restored with endocrown using three-dimensional finite element method. Four models with different designs of marginal preparation, including the flat margin, 90° shoulder, 135° shoulder and chamfer shoulder, were established to imitate mandibular first premolar restored with endocrown. A load of 100 N was applied to the intersection of the long axis and the occlusal surface, either parallel or with an angle of 45° to the long axis of the tooth. The maximum values of Von Mises stress and the stress distribution around the cervical region of the abutment and the endocrown with different designs of marginal preparation were analyzed. The load parallel to the long axis of the tooth caused obvious stress concentration in the lingual portions of both the cervical region of the tooth tissue and the restoration. The stress distribution characteristics on the cervical region of the models with a flat margin and a 90° shoulder were more uniform than those in the models with a 135° shoulder and chamfer shoulder. Loading at 45° to the long axis caused stress concentration mainly on the buccal portion of the cervical region, and the model with a flat margin showed the most favorable stress distribution patterns with a greater maximum Von Mises stress under this circumstance than that with a parallel loading. Irrespective of the loading direction, the stress value was the lowest in the flat margin model, where the stress value in the cervical region of the endocrown was greater than that in the counterpart of the tooth tissue. The stress level on the enamel was higher than that on the dentin nearby in the flat margin model. From the stress distribution point of view, endocrowns with flat margin followed by a 90° shoulder are recommended.

A study of cavity preparation by Er:YAG laser. Effects on the marginal leakage of composite resin restoration.

PubMed

Shigetani, Yoshimi; Tate, Yasuaki; Okamoto, Akira; Iwaku, Masaaki; Abu-Bakr, Neamat

2002-09-01

The purpose of this study was to evaluate marginal leakage of composite resin restoration from cavities prepared by Er:YAG laser. The observation of the dentin surface after the application of laser irradiation was performed by LSM, the cutting surface showed a rough surface similar to scales, and exposed dentinal tubules were observed without striations or a smeared layer formation that were observed when using a rotary cutting device. Leakage tests revealed no significant differences in the marginal seal for both enamel and dentin between cavities prepared by Er:YAG laser irradiation and when using an air-turbine. In this study, the usefulness of cavity preparation by Er:YAG laser irradiation in composite resin restoration was suggested.

Effect of CO2 laser on Class V cavities of human molar teeth under a scanning electron microscope.

PubMed

Watanabe, I; Lopes, R A; Brugnera, A; Katayama, A Y; Gardini, A E

1996-01-01

The purpose of this study was to evaluate the effects of CO2 laser on dentin of class V cavities of extracted human molar teeth using a scanning electron microscope. SEM showed a smooth area with concentric lines formed by melting with subsequent recrystallization of dentin, areas of granulation, vitrified surface, numerous cracks, and irregular areas of descamative dentin. These data indicate that CO2 laser (4 and 6 watts) produces dentin alterations and limit its clinical applications.

Presence of matrix vesicles in the body of odontoblasts and in the inner third of dentinal tissue: a scanning electron microscopic study.

PubMed

Garcés-Ortíz, Maricela; Ledesma-Montes, Constantino; Reyes-Gasga, José

2013-05-01

The aim of this report is to present the results of a scanning electron microscopic study on the presence of matrix vesicles (MVs) found in human dentine. Dentin tissue from 20 human bicuspids was analyzed by means of scanning electron microscopy. MVs were found as outgrowths of the cellular membrane of the odontoblastic body, the more proximal portion of the odontoblastic process before entering the dentinal tubule and in the odontoblastic process within the inner third of the dentin. Size of MVs varied depending on location. In the inner third of dentin, they were seen in diverse positions; as membranal outgrowths, deriving from the odontoblastic process, lying free in the intratubular space and attached to the dentinal wall. Sometimes, they were seen organized forming groups of different sizes and shapes or as multivesicular chains running from the surface of the odontoblastic process to the tubular wall. MVs were present in places never considered: 1) the body of odontoblasts; 2) the most proximal part of the odontoblastic processes before entering the circumpulpal dentine and also: 3) in the inner third of dentinal tissue. According to our results, MVs not only participate during mantle dentin mineralization during early dentinogenesis, they also contribute during the mineralization process of the inner dentin.

Effect of bioactive glass-containing resin composite on dentin remineralization.

PubMed

Lee, Myoung Geun; Jang, Ji-Hyun; Ferracane, Jack L; Davis, Harry; Bae, Han Eul; Choi, Dongseok; Kim, Duck-Su

2018-05-25

The purpose of this study was to evaluate the effect of bioactive glass (BAG)-containing composite on dentin remineralization. Sixty-six dentin disks with 3 mm thickness were prepared from thirty-three bovine incisors. The following six experimental groups were prepared according to type of composite (control and experimental) and storage solutions (simulated body fluid [SBF] and phosphate-buffered saline [PBS]): 1 (undemineralized); 2 (demineralized); 3 (demineralized with control in SBF); 4 (demineralized with control in PBS); 5 (demineralized with experimental composite in SBF); and 6 (demineralized with experimental composite in PBS). BAG65S (65% Si, 31% Ca, and 4% P) was prepared via the sol-gel method. The control composite was made with a 50:50 Bis-GMA:TEGDMA resin matrix, 57 wt% strontium glass, and 15 wt% aerosol silica. The experimental composite had the same resin and filler, but with 15 wt% BAG65S replacing the aerosol silica. For groups 3-6, composite disks (20 × 10 × 2 mm) were prepared and approximated to the dentin disks and stored in PBS or SBF for 2 weeks. Micro-hardness measurements, attenuated total reflection Fourier-transform infrared spectroscopy (ATR-FTIR) and field-emission scanning electron microscopy (FE-SEM) was investigated. The experimental BAG-containing composite significantly increased the micro-hardness of the adjacent demineralized dentin. ATR-FTIR revealed calcium phosphate peaks on the surface of the groups which used experimental composite. FE-SEM revealed surface deposits partially occluding the dentin surface. No significant difference was found between SBF and PBS storage. BAG-containing composites placed in close proximity can partially remineralize adjacent demineralized dentin. Copyright © 2018. Published by Elsevier Ltd.

An in-vitro evaluation of the effect of 980 nm diode laser irradiation on intra-canal dentin surface and dentinal tubule openings after biomechanical preparation: Scanning electron microscopic study

PubMed Central

Jhingan, Pulkit; Sandhu, Meera; Jindal, Garima; Goel, Deepti; Sachdev, Vinod

2015-01-01

Context: Very recently, diode laser has been used for disinfecting the root canals in endodontic treatment and increasing its success rate and longevity utilizing the thermal effect of laser on surrounding tissues. Aims: The aim of this study is to evaluate the effect of 980 nm laser irradiation on intra-canal dentin surface – scanning electron microscopic (SEM) - in-vitro study. Methods: A total of 40 single-rooted freshly extracted permanent teeth were collected. Teeth were sectioned at the cemento-enamel junction using diamond disc. Root canals of all samples were prepared using hand ProTaper, which were randomly assigned into two groups (n = 20 each). Group 1: Receiving no treatment after biomechanical preparation; Group 2: 980 nm diode laser-treated root canals. Teeth were prepared for SEM analysis to check the size of intra-canal dentinal tubule openings. Statistical Analysis Used: Data were analyzed using SPSS V.16 software and compared using Levene's and independent t-test. Results: On statistical analysis, width of intracanal dentinal tubule openings in Group 1 (control) was significantly higher than those observed in Group 2 (diode laser-treated) (P < 0.001). Conclusion: This study showed that the application of 980 nm diode laser on intra-radicular dentin resulted in ultrastructural alterations resulting in melting of dentin. PMID:26097338

The Effect of Four Commonly Used Root Conditioner Agents in Different Time Periods Applied on Periodontally Diseased and Healthy Teeth

PubMed Central

P, Torkzaban; S, Seyedzadeh Sabounchi

2016-01-01

Statement of Problem: Root surface contamination or infection can potentially change the consequences of regenerative periodontal therapies and therefore the modification and disinfection of the contaminated root surfaces are necessary. Objectives: This study aimed to compare the surface characteristics of the extracted human teeth after exposure to four root conditioners in different time periods. Materials and Methods: The study samples were prepared from 40 freshly extracted teeth including 20 affected teeth with periodontal diseases and 20 healthy teeth. After performing root planning, 240 dentinal block samples were prepared and each affected and healthy sample was randomly allocated to receive one of the following root conditioners; Ethylenediaminetetraaceti acid (EDTA), citric acid, doxycycline, and tetracycline or rinsed with normal saline as the control agent. The prepared specimens were evaluated using scanning electron microscope and the inter-group differences and changes in study indices; dentin (%), tubular spaces (%), and diameter of dentinal tubules (μm²) were compared using one-way ANOVA test. Results: In the control group receiving normal saline, the changes in the indicators of dentin, tubular spaces, and diameter of dentinal tubules remained insignificant in all time periods. EDTA, citric acid, and tetracycline had chelating effects on the study indices; however, doxycycline led to gradual decrease of the tubular space and diameter as well as increase in dentin percentage. Conclusions: In different time intervals and when considering healthy or affected tooth surfaces, the effect of conditioning agents could be different. Amongst the four agents used, EDTA and tetracycline consistently increased the diameter of tubules and percentage of patent tubules in both healthy and diseased teeth. PMID:28959749

Do matrix metalloproteinase inhibitors improve the bond durability of universal dental adhesives?

PubMed

Tekçe, Neslihan; Tuncer, Safa; Demirci, Mustafa; Balci, Sibel

2016-11-01

The aim of this study was to evaluate the effects of matrix metalloproteinases (MMPs) inhibitors on the microtensile bond strength (μTBS) and the adhesive-dentin interface of two universal dentin bonding agents, Single Bond Universal and All Bond Universal, after 12 months of water storage. Seventy extracted, caries-free, human third molars were used in this study. Of these, 50 were used for μTBS testing and 20 were used for scanning electron microscopy. The two bonding agents were applied to flat dentin surfaces in five different ways: self-etch mode, etch-and-rinse mode with 37% phosphoric acid, etch-and-rinse mode with phosphoric acid containing 1% benzalkonium chloride, etch-and-rinse mode with phosphoric acid and 2% chlorhexidine, and etch-and-rinse mode with 0.5 M ethylenediaminetetraacetic acid (EDTA) (n = 5 for each bonding agent in each group; N = 50). Half the specimens were subjected to μTBS tests at 24 h, while half were subjected to the tests after 12 months of water storage. For each bonding agent, inhibition, storage, and their interaction effects were tested by two-way analysis of variance and Bonferroni tests. For Single Bond Universal, the benzalkonium chloride (p = 0.024) and chlorhexidine groups (p = 0.033) exhibited significantly higher μTBS values at 24 h compared with the self-etch group. For All Bond Universal, all groups displayed similar bond strengths at 24 h (p > 0.05). After 12 months of water storage, the μTBS values decreased significantly in the benzalkonium chloride group for Single Bond Universal (p = 0.001) and the self-etch (p = 0.029), chlorhexidine (p = 0.046), and EDTA (p = 0.032) groups for All Bond Universal. These results suggest that the immediate dentin bond strength increases when universal bonding systems are applied in the etch-and-rinse mode, although the durability decreases. The use of chlorhexidine and EDTA can increase the bond durability of mild adhesives such as Single Bond Universal. SCANNING 38:535-544, 2016. © 2016 Wiley Periodicals, Inc. © Wiley Periodicals, Inc.

Effect of tetracalcium phosphate/monetite toothpaste on dentin remineralization and tubule occlusion in vitro.

PubMed

Medvecky, L; Stulajterova, R; Giretova, M; Mincik, J; Vojtko, M; Balko, J; Briancin, J

2018-03-01

To investigate the tubule occlusion and remineralization potential of a novel toothpaste with active tetracalcium phosphate/monetite mixtures under de/remineralization cycling. Dentin de/remineralization cycling protocol consisted of demineralization in 1% citric acid at pH 4.6 with following remineralization with toothpastes and soaking in artificial saliva. Effectiveness of toothpastes to promote remineralization was evaluated by measurement of microhardness recovery, analysis of surface roughness, thickness of coating and scanning electron microscopy. The novel tetracalcium phosphate/monetite dentifrice had comparable remineralization potential as commercial calcium silicate/phosphate (SENSODYNE ® ) and magnesium aluminum silicate (Colgate ® ) toothpastes and significantly higher than control saliva (p<0.02). Surface roughness was significantly lower after treatment with prepared and SENSODYNE ® dentifirice (p<0.05). The coatings on dentin surfaces was significantly thicker after applying toothpastes as compared to negative control (p<0.001). The new fluoride toothpaste formulation with bioactive tetracalcium phosphate/monetite calcium phosphate mixture effectively occluded dentin tubules and showed good dentin remineralization potential under de/remineralization cycling. It could replace professional powder preparation based on this mixture. It was demonstrated that prepared dentifrice had comparable properties with commercial fluoride calcium silicate/phosphate or magnesium aluminum silicate dentifrices. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

12-month color stability of enamel, dentine, and enamel-dentine samples after bleaching.

PubMed

Wiegand, Annette; Drebenstedt, Steffi; Roos, Malgorzata; Magalhães, Ana Carolina; Attin, Thomas

2008-12-01

The study aimed to quantify the color regression of enamel (E), dentine (D), and combined enamel-dentine (ED) of differently bleached ED specimens over a period of 12 months in vitro. Two ED samples were obtained from the labial surfaces of bovine teeth and prepared to a standardized thickness with the enamel and dentine layer each 1 mm. The ED samples were distributed on four groups (each n = 80), in which the different bleaching products were applied on enamel (1, Whitestrips; 2, Illuminé 15%; 3, Opalescence Xtra Boost) or dentine surfaces (4, mixture of sodium perborate/distilled water). Eighty ED samples were not bleached (control). Color (L*a*b*) of ED was assessed at baseline, subsequently after bleaching and at 3, 6, and 12 months of storage after bleaching (each 20 samples/group). E and D samples were prepared by removing the dentine or enamel layer of ED samples to allow for separate color analysis. Bleaching resulted in a significant color change (Delta E) of ED specimens. Within the observation period, Delta L but not Delta b declined to baseline. L* values of E and D samples also declined and were not significantly different from control samples after 12 months, while b* values did not decrease to baseline. Generally, no differences between the bleaching agents could be observed. Color change of enamel, dentine, and combined ED of in vitro bleached tooth samples is not stable over time with regard to lightness. However, yellowness did not return to baseline within 1 year.

Evaluation of tensile retention of Y-TZP crowns after long-term aging: effect of the core substrate and crown surface conditioning.

PubMed

Amaral, R; Rippe, M; Oliveira, B G; Cesar, P F; Bottino, M A; Valandro, L F

2014-01-01

This study evaluated the effect of the core substrate type (dentin and composite resin) on the retention of crowns made of yttrium oxide stabilized tetragonal zirconia polycrystal (Y-TZP), submitted to three inner surface conditionings. For this purpose, 72 freshly extracted molars were embedded in acrylic resin, perpendicular to the long axis, and prepared for full crowns: 36 specimens had crown preparations in dentin; the remaining 36 teeth had the crowns removed, and crown preparations were reconstructed with composite resin plus fiber posts with dimensions identical to the prepared dentin. The preparations were impressed using addition silicone, and 72 Y-TZP copings for the tensile test were produced. Cementation was performed with a dual-cured cement containing phosphate monomers. For cementation, the crown preparation (dentin or resin) was conditioned with the adhesive system, and the ceramic was subjected to one of three surface treatments: isopropyl alcohol, tribochemical silica coating, or thin low-fusing glassy porcelain layer application plus silanization. After 24 hours, all specimens were submitted to thermocycling (6000 cycles) and placed in a special tensile testing device in a universal testing machine to determine failure loads. The failure modes of all samples were analyzed under a stereomicroscope. Two-way analysis of variance showed that the surface treatment and substrate type (α=0.05) affected the tensile retention results. The dentin substrate presented the highest tensile retention values, regardless of the surface treatment. When the substrate was resin, the tribochemical silica coating and low-fusing glaze application plus silanization groups showed the higher retention values.

The effect of retreatment procedure on the pH changes at the surface of root dentin using two different calcium hydroxide pastes

PubMed Central

Kazemipoor, Maryam; Tabrizizadeh, Mehdi; Dastani, Milad; Hakimian, Roqayeh

2012-01-01

Aim: To compare pH changes at the cervical, middle and apical surfaces of root dentin in retreated and non- retreated teeth, after canal obturation with two different calcium hydroxide pastes. Materials and Methods: After instrumentation of 55 extracted teeth, three cavities with 0.75 mm depth and 1.5 mm in diameter were drilled at buccal root surface. The teeth were randomly divided into five groups. Canals in the first two groups were filled with either mixture of calcium hydroxide and saline solution and calcium hydroxide and 2% chlorhexidine (CHX). In the third and fourth groups canals were first obturated with gutta-percha and AH26 sealer, and then materials were removed. After 2 days canals were filled with two different calcium hydroxide pastes similar to the first and the second groups. The pH was measured in the prepared cavities at 1, 3, 7 and 14 days. Results: In the non-retreated groups, pH at the surface of the roots was significantly higher in comparison to the retreated ones (P value < 0.001). pH values were significantly higher in the non-retreated teeth filling with calcium hydroxide and saline solution (P value < 0.001). Conclusion: Regarding to the little pH changes at the surface of dentin in retreated teeth, the hydroxyl ions cannot penetrate into the dentinal tubules. Thus, to achieve higher pH at the root surface in retreated teeth, it is clinically advisable to remove more dentin from the inner walls and to use normal saline as a vehicle for calcium hydroxide rather than acidic pH materials. PMID:23112482

The effect of retreatment procedure on the pH changes at the surface of root dentin using two different calcium hydroxide pastes.

PubMed

Kazemipoor, Maryam; Tabrizizadeh, Mehdi; Dastani, Milad; Hakimian, Roqayeh

2012-10-01

To compare pH changes at the cervical, middle and apical surfaces of root dentin in retreated and non- retreated teeth, after canal obturation with two different calcium hydroxide pastes. After instrumentation of 55 extracted teeth, three cavities with 0.75 mm depth and 1.5 mm in diameter were drilled at buccal root surface. The teeth were randomly divided into five groups. Canals in the first two groups were filled with either mixture of calcium hydroxide and saline solution and calcium hydroxide and 2% chlorhexidine (CHX). In the third and fourth groups canals were first obturated with gutta-percha and AH26 sealer, and then materials were removed. After 2 days canals were filled with two different calcium hydroxide pastes similar to the first and the second groups. The pH was measured in the prepared cavities at 1, 3, 7 and 14 days. In the non-retreated groups, pH at the surface of the roots was significantly higher in comparison to the retreated ones (P value < 0.001). pH values were significantly higher in the non-retreated teeth filling with calcium hydroxide and saline solution (P value < 0.001). Regarding to the little pH changes at the surface of dentin in retreated teeth, the hydroxyl ions cannot penetrate into the dentinal tubules. Thus, to achieve higher pH at the root surface in retreated teeth, it is clinically advisable to remove more dentin from the inner walls and to use normal saline as a vehicle for calcium hydroxide rather than acidic pH materials.

Adhesion of Porphyromonas gingivalis and Tannerella forsythia to dentin and titanium with sandblasted and acid etched surface coated with serum and serum proteins - An in vitro study.

PubMed

Eick, Sigrun; Kindblom, Christian; Mizgalska, Danuta; Magdoń, Anna; Jurczyk, Karolina; Sculean, Anton; Stavropoulos, Andreas

2017-03-01

To evaluate the adhesion of selected bacterial strains incl. expression of important virulence factors at dentin and titanium SLA surfaces coated with layers of serum proteins. Dentin- and moderately rough SLA titanium-discs were coated overnight with human serum, or IgG, or human serum albumin (HSA). Thereafter, Porphyromonas gingivalis, Tannerella forsythia, or a six-species mixture were added for 4h and 24h. The number of adhered bacteria (colony forming units; CFU) was determined. Arg-gingipain activity of P. gingivalis and mRNA expressions of P. gingivalis and T. forsythia proteases and T. forsythia protease inhibitor were measured. Coating specimens never resulted in differences exceeding 1.1 log10 CFU, comparing to controls, irrespective the substrate. Counts of T. forsythia were statistically significantly higher at titanium than dentin, the difference was up to 3.7 log10 CFU after 24h (p=0.002). No statistically significant variation regarding adhesion of the mixed culture was detected between surfaces or among coatings. Arg-gingipain activity of P. gingivalis was associated with log10 CFU but not with the surface or the coating. Titanium negatively influenced mRNA expression of T. forsythia protease inhibitor at 24h (p=0.026 uncoated, p=0.009 with serum). The present findings indicate that: a) single bacterial species (T. forsythia) can adhere more readily to titanium SLA than to dentin, b) low expression of T. forsythia protease inhibitor may influence the virulence of the species on titanium SLA surfaces in comparison with teeth, and c) surface properties (e.g. material and/or protein layers) do not appear to significantly influence multi-species adhesion. Copyright © 2016 Elsevier Ltd. All rights reserved.

Prospective in (Primate) Dental Analysis through Tooth 3D Topographical Quantification

PubMed Central

Guy, Franck; Gouvard, Florent; Boistel, Renaud; Euriat, Adelaïde; Lazzari, Vincent

2013-01-01

The occlusal morphology of the teeth is mostly determined by the enamel-dentine junction morphology; the enamel-dentine junction plays the role of a primer and conditions the formation of the occlusal enamel reliefs. However, the accretion of the enamel cap yields thickness variations that alter the morphology and the topography of the enamel–dentine junction (i.e., the differential deposition of enamel by the ameloblasts create an external surface that does not necessarily perfectly parallel the enamel–dentine junction). This self-reliant influence of the enamel on tooth morphology is poorly understood and still under-investigated. Studies considering the relationship between enamel and dentine morphologies are rare, and none of them tackled this relationship in a quantitative way. Major limitations arose from: (1) the difficulties to characterize the tooth morphology in its comprehensive tridimensional aspect and (2) practical issues in relating enamel and enamel–dentine junction quantitative traits. We present new aspects of form representation based exclusively on 3D analytical tools and procedures. Our method is applied to a set of 21 unworn upper second molars belonging to eight extant anthropoid genera. Using geometrical analysis of polygonal meshes representatives of the tooth form, we propose a 3D dataset that constitutes a detailed characterization of the enamel and of the enamel–dentine junction morphologies. Also, for the first time, to our knowledge, we intend to establish a quantitative method for comparing enamel and enamel–dentine junction surfaces descriptors (elevation, inclination, orientation, etc.). New indices that allow characterizing the occlusal morphology are proposed and discussed. In this note, we present technical aspects of our method with the example of anthropoid molars. First results show notable individual variations and taxonomic heterogeneities for the selected topographic parameters and for the pattern and strength of association between enamel–dentine junction and enamel, the enamel cap altering in different ways the “transcription” of the enamel–dentine junction morphology. PMID:23826088

Initial and long-term bond strengths of one-step self-etch adhesives with silane coupling agent to enamel-dentin-composite in combined situation.

PubMed

Mamanee, Teerapong; Takahashi, Masahiro; Nakajima, Masatoshi; Foxton, Richard M; Tagami, Junji

2015-01-01

This study evaluated the effect of adding silane coupling agent on initial and long-term bond strengths of one-step self-etch adhesives to enamel-dentin-composite in combined situation. Cervical cavities were prepared on extracted molars and filled with Clearfil AP-X. After water-storage for one-week, the filled teeth were sectioned in halves to expose enamel, dentin and composite surfaces and then enamel-dentin-composite surface was totally applied with one of adhesive treatments (Clearfil SE One, Clearfil SE One with Clearfil Porcelain Bond Activator, Beautibond Multi, Beautibond Multi with Beautibond Multi PR Plus and Scotchbond Universal). After designed period, micro-shear bond strengths (µSBSs) to each substrate were determined. For each period of water-storage, additive silane treatments significantly increased µSBS to composite (p<0.001). On the other hand, they significantly decreased µSBS to dentin (p<0.001), although did not have adverse effect on µSBS to enamel (p>0.05). Moreover, the stability of µSBS was depended on materials and substrates used.

Optimization of the etch-and-rinse technique: New perspectives to improve resin-dentin bonding and hybrid layer integrity by reducing residual water using dimethyl sulfoxide pretreatments.

PubMed

Stape, Thiago Henrique Scarabello; Tjäderhane, Leo; Abuna, Gabriel; Sinhoreti, Mário Alexandre Coelho; Martins, Luís Roberto Marcondes; Tezvergil-Mutluay, Arzu

2018-04-13

To determine whether bonding effectiveness and hybrid layer integrity on acid-etched dehydrated dentin would be comparable to the conventional wet-bonding technique through new dentin biomodification approaches using dimethyl sulfoxide (DMSO). Etched dentin surfaces from extracted sound molars were randomly bonded in wet or dry conditions (30s air drying) with DMSO/ethanol or DMSO/H 2 O as pretreatments using a simplified (Scotchbond Universal Adhesive, 3M ESPE: SU) and a multi-step (Adper Scotchbond Multi-Purpose, 3M ESPE: SBMP) etch-and-rinse adhesives. Untreated dentin surfaces served as control. Bonded teeth (n=8) were stored in distilled water for 24h and sectioned into resin-dentin beams (0.8mm 2 ) for microtensile bond strength test and quantitative interfacial nanoleakage analysis (n=8) under SEM. Additional teeth (n=2) were prepared for micropermeability assessment by CFLSM under simulated pulpar pressure (20cm H 2 O) using 5mM fluorescein as a tracer. Microtensile data was analyzed by 3-way ANOVA followed by Tukey Test and nanoleakage by Kruskal-Wallis and Dunn-Bonferroni multiple comparison test (α=0.05). While dry-bonding of SBMP produced significantly lower bond strengths than wet-bonding (p<0.05), DMSO/H 2 O and DMSO/ethanol produced significantly higher bond strengths for SBMP irrespective of dentin condition (p<0.05). SU presented significantly higher nanoleakage levels (p<0.05) and micropermeability than SBMP. Improvement in hybrid layer integrity occurred for SBMP and SU for both pretreatments, albeit most pronouncedly for DMSO/ethanol regardless of dentin moisture. DMSO pretreatments may be used as a new suitable strategy to improve bonding of water-based adhesives to demineralized air-dried dentin beyond conventional wet-bonding. Less porous resin-dentin interfaces with higher bond strengths on air-dried etched dentin were achieved; nonetheless, overall efficiency varied according to DMSO's co-solvent and adhesive type. DMSO pretreatments permit etched dentin to be air-dried before hybridization facilitating residual water removal and thus improving bonding effectiveness. This challenges the current paradigm of wet-bonding requirement for the etch-and-rinse approach creating new possibilities to enhance the clinical longevity of resin-dentin interfaces. Copyright © 2018 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved.

The effect of 10% carbamide peroxide bleaching material on microhardness of sound and demineralized enamel and dentin in situ.

PubMed

Basting, R T; Rodrigues Júnior, A L; Serra, M C

2001-01-01

This in situ study evaluated the microhardness of sound and demineralized enamel and dentin submitted to treatment with 10% carbamide peroxide for three weeks. A 10% carbamide peroxide bleaching agent--Opalescence/Ultradent (OPA)--was evaluated against a placebo agent (PLA). Two hundred and forty dental fragments--60 sound enamel fragments (SE), 60 demineralized enamel fragments (DE), 60 sound dentin fragments (SD) and 60 demineralized dentin fragments (DD)--were randomly fixed on the vestibular surface of the first superior molars and second superior premolars of 30 volunteers. The volunteers were divided into two groups that received bleaching or the placebo agent at different sequences and periods at a double blind 2 x 2 crossover study with a wash-out period of two weeks. Microhardness tests were performed on the enamel and dentin surface. The SE and DE submitted to treatment with OPA showed lower microhardness values than the SE and DE submitted to treatment with PLA. There were no statistical differences in microhardness values for SD and DD submitted to the treatment with OPA and PLA. The results suggest that treatment with 10% carbamide peroxide bleaching material for three weeks alters the enamel microhardness, although it does not seem to alter the dentin microhardness.

Structural analysis of strontium in human teeth treated with surface pre-reacted glass-ionomer filler eluate by using extended X-ray absorption fine structure analysis.

PubMed

Uo, Motohiro; Wada, Takahiro; Asakura, Kiyotaka

2017-03-31

The bioactive effects of strontium released from surface pre-reacted glass-ionomer (S-PRG) fillers may aid in caries prevention. In this study, the local structure of strontium taken up by teeth was estimated by extended X-ray absorption fine structure analysis. Immersing teeth into S-PRG filler eluate increased the strontium content in enamel and dentin by more than 100 times. The local structure of strontium in enamel and dentin stored in distilled water was the same as that in synthetic strontium-containing hydroxyapatite (SrHAP). Moreover, the local structure of strontium in enamel and dentin after immersion in the S-PRG filler eluate was also similar to that of SrHAP. After immersion in the S-PRG filler eluate, strontium was suggested to be incorporated into the hydroxyapatite (HAP) of enamel and dentin at the calcium site in HAP.

Crack propagation in teeth: a comparison of perimortem and postmortem behavior of dental materials and cracks.

PubMed

Hughes, Cris E; White, Crystal A

2009-03-01

This study presents a new method for understanding postmortem heat-induced crack propagation patterns in teeth. The results demonstrate that patterns of postmortem heat-induced crack propagation differ from perimortem and antemortem trauma-induced crack propagation patterns. Dental material of the postmortem tooth undergoes dehydration leading to a shrinking and more brittle dentin material and a weaker dentin-enamel junction. Dentin intertubule tensile stresses are amplified by the presence of the pulp cavity, and initiates crack propagation from the internal dentin, through the dentin-enamel junction and lastly the enamel. In contrast, in vivo perimortem and antemortem trauma-induced crack propagation initiates cracking from the external surface of the enamel toward the dentin-enamel junction where the majority of the energy of the crack is dissipated, eliminating the crack's progress into the dentin. These unique patterns of crack propagation can be used to differentiate postmortem taphonomy-induced damage from antemortem and perimortem trauma in teeth.

Effect of functional monomers in all-in-one adhesive systems on formation of enamel/dentin acid-base resistant zone.

PubMed

Nikaido, Toru; Ichikawa, Chiaki; Li, Na; Takagaki, Tomohiro; Sadr, Alireza; Yoshida, Yasuhiro; Suzuki, Kazuomi; Tagami, Junji

2011-01-01

This study aimed at evaluating the effect of functional monomers in all-in-one adhesive systems on formation of acid-base resistant zone (ABRZ) in enamel and dentin. Experimental adhesive systems containing one of three functional monomers; MDP, 3D-SR and 4-META were applied to enamel or dentin surface and light-cured. A universal resin composite was then placed. The specimens were subjected to a demineralizing solution (pH 4.5) and 5% NaClO for acid-base challenge and then observed by SEM. The ABRZ was clearly observed in both enamel and dentin interfaces. However, enamel ABRZ was thinner than dentin ABRZ in all adhesives. Morphology of the ABRZ was different between enamel and dentin, and also among the adhesives. Funnel-shaped erosion was observed only in the enamel specimen with the 4-META adhesive. The formation of enamel/dentin ABRZ was confirmed in all adhesives, but the morphology was influenced by the functional monomers.

Effect of endodontic irrigating solutions on the microhardness and roughness of root canal dentin: an in vitro study.

PubMed

Patil, Chetan R; Uppin, Veerendra

2011-01-01

To evaluate the effect of widely used endodontic irrigating solutions on root dentin microhardness and surface roughness. One hundred twenty, non-carious extracted human permanent incisor teeth were selected. The crowns of the teeth were sectioned and the roots were separated longitudinally to get 240 specimens. These specimens were then divided into six groups according to the irrigating solutions used. The solutions used were 5% and 2.5% NaOCl solutions, 3% H2 O2 , 17% EDTA solution, 0.2% chlorhexidine gluconate, and distilled water. Then, the specimens were subjected to microhardness and roughness testing. The data were analyzed using ANOVA and Tukey's multiple comparison tests. The results of this study indicated that all irrigation solutions, except 0.2% chlorhexidine gluconate, decreased the microhardness of root dentin, and 3% H2 O2 and 0.2% chlorhexidine gluconate had no effect on surface roughness. Within the limitation of this study, it is concluded that 0.2% chlorhexidine gluconate seems to be an appropriate irrigation solution, because of its harmless effect on the microhardness and surface roughness of root canal dentin.

Characterization of two types of osteoclasts from human peripheral blood monocytes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yuasa, Kimitaka; Mori, Kouki; Ishikawa, Hitoshi

2007-05-04

The two osteoclastogenesis pathways, receptor activator nuclear factor (NF)-{kappa}B ligand (RANKL)-mediated and fusion regulatory protein-1 (FRP-1)-mediated osteoclastogenesis, have recently been reported. There were significant differences in differentiation and activation mechanisms between the two pathways. When monocytes were cultured with FRP-1 without adding M-CSF, essential for the RANKL system, TRAP-positive polykaryocyte formation occurred. FRP-1-mediated osteoclasts formed larger pits on mineralized calcium phosphate plates than RANKL+M-CSF-mediated osteoclasts did. Lacunae on dentin surfaces induced by FRP-1-mediated osteoclasts were inclined to be single and isolated. However, osteoclasts induced by RANKL+M-CSF made many connected pits on dentin surfaces as if they crawled on there. Interestingly,more » FRP-1 osteoclastogenesis was enhanced by M-CSF/IL-1{alpha}, while chemotactic behavior to the dentin slices was not effected. There were differences in pH and concentration of HCO3- at culture endpoint and in adherent feature to dentin surfaces. Our findings indicate there are two types of osteoclasts with distinct properties.« less

The shear bond strength of self-adhesive resin cements to dentin and enamel: an in vitro study.

PubMed

Rodrigues, Raphaela F; Ramos, Carla M; Francisconi, Paulo A S; Borges, Ana Flávia S

2015-03-01

Clinicians continue to search for ways to simplify bonding procedures without compromising clinical efficacy. The purpose of this study was to evaluate the shear strength of self-adhesive cements RelyX U100 and RelyX U200, and conventional resin cement RelyX ARC to enamel and dentin after different surface treatments. The crowns of 120 bovine incisor teeth were separated from the roots and embedded in epoxy resin in polyvinyl chloride tubes. In each tooth, the area to be cemented was delimited with central holed adhesive tape. The teeth were distributed into 12 groups (n=10) according to the substrate; etched or not with 37% phosphoric acid; and cement type of enamel-U100, enamel-phosphoric acid-U100, enamel-U200, enamel-phosphoric acid-U200, enamel-ARC, enamel-phosphoric acid-ARC, dentin-U100, dentin-phosphoric acid-U100, dentin-U200, dentin-phosphoric acid-U200, dentin-ARC, and dentin-phosphoric acid-ARC. After 7 days of storage in artificial saliva, shear strength tests were performed by using a universal testing machine (0.5 mm/min). The data were analyzed with 3-way ANOVA and the Tukey test (α=.05). Fracture analysis was performed with a light microscope. Two specimens from each group were analyzed with a scanning electron microscope. In enamel, ARC (9.96 MPa) had higher shear strength (P=.038) than U100 (5.14 MPa); however, after surface etching, U100 (17.81 MPa) and U200 (17.52 MPa) had higher shear strength (P<.001). With dentin, no significant differences were observed (P=.999), except for dentin-ARC (0.34 MPa) (P=.001). Most fractures were of the adhesive type. U200 self-adhesive cement had similar bond strength to the ARC in enamel, but the combination with phosphoric acid had the best bond strength. For dentin, self-adhesive resin cements are equally effective alternatives to conventional resin cement. Copyright © 2015 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Effect of Er,Cr:YSGG laser on the microtensile bond strength of two different adhesives to the sound and caries-affected dentin.

PubMed

Ergücü, Z; Celik, E U; Unlü, N; Türkün, M; Ozer, F

2009-01-01

This study examined the effect of Er,Cr:YSGG laser irradiation on the microtensile bond strength (microTBS) of a three-step etch-and-rinse and a two-step self-etch adhesive to sound and caries-affected dentin. Sixteen freshly extracted human molars with occlusal dentin caries were used. The caries lesion was removed by one of the following methods: conventional treatment with burs or Er,Cr:YSGG laser (Waterlase MD, Biolase). The adhesive systems (AdheSE, Ivoclar Vivadent and Scotchbond Multi Purpose, 3M ESPE) were applied to the entire tooth surface according to the manufacturers' instructions. Resin composites were applied to the adhesive-treated dentin surfaces and light-cured. Each tooth was sectioned into multiple beams with the "non-trimming" version of the microtensile test. The specimens were subjected to microtensile forces (BISCO Microtensile Tester, BISCO). The data was analyzed by three-way ANOVA and independent t-tests (p=0.05). Er,Cr:YSGG laser irradiation exhibited similar microTBS values compared to that of conventional bur treatment, regardless of the adhesive system and type of treated dentin. The self-etch system revealed lower microTBS values, both with conventional and laser treatment techniques, compared to the etch-and-rinse adhesive in sound and caries-affected dentin (p<0.05). Er,Cr:YSGG laser irradiation did not negatively affect the bonding performance of adhesive systems to sound and caries-affected dentin.

Experimental resin cements containing bioactive fillers reduce matrix metalloproteinase-mediated dentin collagen degradation.

PubMed

Osorio, Raquel; Yamauti, Monica; Sauro, Salvatore; Watson, Thimoty F; Toledano, Manuel

2012-09-01

Collagen dentin matrix may represent a suitable scaffold to be remineralized in the presence of bioactive materials. The purpose of this study was to determine if experimental resin cements containing bioactive fillers may modulate matrix metalloproteinase-mediated collagen degradation of etched dentin. Human dentin beams demineralized using 10% phosphoric acid or 0.5 mol/L EDTA were infiltrated with the following experimental resins: (1) unfilled resin, (2) resin with Bioglass 45S5 particles (Sylc; OSspray Ltd, London, UK), and (3) resin with β-tricalcium phosphate-modified calcium silicate cement (HCAT-β) particles. The filler/resin ratio was 40/60 wt%. The specimens were stored in artificial saliva, and the determination of C-terminal telopeptide (ICTP) was performed by radioimmunoassay after 24 hours, 1 week, and 4 weeks. Scanning electron microscopic analysis of dentin surfaces after 4 weeks of storage was also executed. Collagen degradation was prominent both in phosphoric acid and EDTA-treated dentin. Resin infiltration strongly reduced the MMP activity in demineralized dentin. Resin-containing Bioglass 45S5 particles exerted higher and more stable protection of collagen at all tested dentin states and time points. HCAT-β induced collagen protection from MMPs only in EDTA-treated specimens. Dentin remineralization was achieved when dentin was infiltrated with the resin cements containing bioactive fillers. MMP degradation of dentin collagen is strongly reduced in resin-infiltrated dentin. The inclusion of Bioglass 45S5 particles exerted an additional protection of collagen during dentin remineralization. Copyright © 2012 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

The threshold effects of Nd and Ho: YAG laser-induced surface modification on demineralization of dentin surfaces.

PubMed

Kinney, J H; Haupt, D L; Balooch, M; White, J M; Bell, W L; Marshall, S J; Marshall, G W

1996-06-01

Laser irradiation alters the structure of dentin and produces surface layers that give the appearance of being more enamel-like. The laser-modified surface may be more resistant to demineralization; hence, many investigators are proposing continued development of the laser as a possible preventive treatment for caries. The purpose of this study was to explore the morphological changes that occur in dentin when treated at threshold illuminance with two clinically interesting laser wavelengths, and to evaluate the effectiveness of the laser-treated surface at resisting demineralization in an acid-gel solution. The Nd: YAG laser (wavelength 1060 nm) produced significant recrystallization and grain growth of the apatite, without the formation of second phases such as beta-tricalcium phosphate. This recrystallized surface layer showed resistance to demineralization; however, the layer did not provide protection of the underlying dentin from demineralization because of cracks and macroscopic voids that allowed for penetration of the demineralizing gel. The Ho: YAG laser-treated surface (wavelength 2100 nm) did not show significant evidence of recrystallization and grain growth, and only a trace amount of an acid-resistant layer was observed with demineralization. It is speculated that the Ho:YAG laser is coupling with absorbed water, and that the heat transfer from the water to the mineral phase is inefficient. For the purposes of creating a demineralization-resistant layer, threshold illuminance with both Nd: YAG and Ho: YAG was ineffective.

Effect of Different Protocols in Preconditioning With EDTA in Sclerotic Dentin and Enamel Before Universal Adhesives Applied in Self-etch Mode.

PubMed

Martini, E C; Parreiras, S O; Gutierrez, M F; Loguercio, A D; Reis, A

The aim of this study was to investigate the effect of different protocols of 17% ethylene diamine tetra-acetic acid (EDTA) conditioning on the etching pattern and immediate bond strength of universal adhesives to enamel and sclerotic dentin. Forty bovine teeth with sclerotic dentin and 20 human third molars were randomly divided into eight groups resulting from the combination of the main factors surface treatment (none, two-minute EDTA conditioning manual application, 30-second EDTA manual application, 30-second EDTA sonic application) and adhesives systems (Scotchbond Universal Adhesive [SBU] and Prime & Bond Elect [PBE]). Resin-dentin and enamel-dentin bond specimens were prepared and tested under the microtensile bond strength (μTBS) and microshear bond strength (μSBS) tests, respectively. The etching pattern produced on the unground enamel and the sclerotic dentin surfaces under the different protocols and adhesive systems was evaluated under scanning electron microscopy. For enamel, only the main factor adhesive was significant (p<0.0001), with SBU showing the highest μSBS. In sclerotic dentin, the lowest mean was observed for the group without EDTA application and the highest mean in the group with EDTA application with the sonic device for 30 seconds. Regardless of the EDTA protocol, the highest means of μTBS were observed for SBU (p<0.05). EDTA conditioning improves the bonding performance of universal adhesives in the self-etch mode on sclerotic dentin, mainly when applied for 30 seconds with the aid of a sonic device. EDTA pretreatment also improves the retentive etching pattern of enamel, but it does not result in higher enamel bond strength.

Roles of Heparan Sulfate Sulfation in Dentinogenesis*

PubMed Central

Hayano, Satoru; Kurosaka, Hiroshi; Yanagita, Takeshi; Kalus, Ina; Milz, Fabian; Ishihara, Yoshihito; Islam, Md. Nurul; Kawanabe, Noriaki; Saito, Masahiro; Kamioka, Hiroshi; Adachi, Taiji; Dierks, Thomas; Yamashiro, Takashi

2012-01-01

Cell surface heparan sulfate (HS) is an essential regulator of cell signaling and development. HS traps signaling molecules, like Wnt in the glycosaminoglycan side chains of HS proteoglycans (HSPGs), and regulates their functions. Endosulfatases Sulf1 and Sulf2 are secreted at the cell surface to selectively remove 6-O-sulfate groups from HSPGs, thereby modifying the affinity of cell surface HSPGs for its ligands. This study provides molecular evidence for the functional roles of HSPG sulfation and desulfation in dentinogenesis. We show that odontogenic cells are highly sulfated on the cell surface and become desulfated during their differentiation to odontoblasts, which produce tooth dentin. Sulf1/Sulf2 double null mutant mice exhibit a thin dentin matrix and short roots combined with reduced expression of dentin sialophosphoprotein (Dspp) mRNA, encoding a dentin-specific extracellular matrix precursor protein, whereas single Sulf mutants do not show such defective phenotypes. In odontoblast cell lines, Dspp mRNA expression is potentiated by the activation of the Wnt canonical signaling pathway. In addition, pharmacological interference with HS sulfation promotes Dspp mRNA expression through activation of Wnt signaling. On the contrary, the silencing of Sulf suppresses the Wnt signaling pathway and subsequently Dspp mRNA expression. We also show that Wnt10a protein binds to cell surface HSPGs in odontoblasts, and interference with HS sulfation decreases the binding affinity of Wnt10a for HSPGs, which facilitates the binding of Wnt10a to its receptor and potentiates the Wnt signaling pathway, thereby up-regulating Dspp mRNA expression. These results demonstrate that Sulf-mediated desulfation of cellular HSPGs is an important modification that is critical for the activation of the Wnt signaling in odontoblasts and for production of the dentin matrix. PMID:22351753

Evaluating the shear bond strength of enamel and dentin with or without etching: A comparative study between dimethacrylate-based and silorane-based adhesives

PubMed Central

Hajizadeh, Hila; Nasseh, Atefeh; Rahmanpour, Naim

2015-01-01

Background Silorane-based composites and their specific self-etch adhesive were introduced to conquest the polymerization shrinkage of methacrylate-based composites. It has been shown that additional etching of enamel and dentin can improve the bond strength of self-etch methacrylate-based adhesives but this claim is not apparent about silorane-based adhesives. Our objective was to compare the shear bond strength (SBS) of enamel and dentin between silorane-based adhesive resin and a methacrylate-based resin with or without additional etching. Material and Methods 40 sound human premolars were prepared and divided into two groups: 1- Filtek P60 composite and Clearfil SE Bond adhesive; 2- Filtek P90 composite and Silorane adhesive. Each group divided into two subgroups: with or without additional etching. For additional etching, 37% acid phosphoric was applied before bonding procedure. A cylinder of the composite was bonded to the surface. After 24 hours storage and 500 thermo cycling between 5-55°C, shear bond strength was assessed with the cross head speed of 0.5 mm/min. Then, bonded surfaces were observed under stereomicroscope to determine the failure mode. Data were analyzed with two-way ANOVA and Fischer exact test. Results Shear bond strength of Filtek P60 composite was significantly higher than Filtek P90 composite both in enamel and dentin surfaces (P<0.05). However, additional etching had no significant effect on shear bond strength in enamel or dentin for each of the composites (P>0.05). There was no interaction between composite type and additional etching (P>0.05). Failure pattern was mainly adhesive and no significant correlation was found between failure and composite type or additional etching (P>0.05). Conclusions Shear bond strength of methacrylate-based composite was significantly higher than silorane-based composite both in enamel and dentin surfaces and additional etching had no significant effect on shear bond strength in enamel or dentin for each of the composites. The mode of failure had no meaningful relation to the type of composite and etching factor. Key words:Shear bond strength, adhesive, composite resin, silorane, methacrylate. PMID:26644830

Chlorhexidine diminishes the loss of bond strength over time under simulated pulpal pressure and thermo-mechanical stressing.

PubMed

Campos, Edson Alves; Correr, Gisele Maria; Leonardi, Denise Piotto; Barato-Filho, Flares; Gonzaga, Carla Castiglia; Zielak, João César

2009-02-01

The purpose of this study was to investigate the effects of chlorhexidine (CHX) digluconate at 0.2% and 2% on dentin bonding durability of etch-and-rinse and self-etch adhesive systems. In this study were used 24 extracted non-carious human third-molars. The occlusal surfaces of the molar crowns were removed with a low-speed diamond saw to expose flat dentin surfaces. The tested materials were Single-Bond (SB) (two-step etch-and-rinse adhesive) and Clearfil Tri S Bond (CTSB) (all-in-one self-etch adhesive) used in association or not with CHX at 0.2% and 2%. The bonding systems were applied according to manufacturer's instructions and followed by composite application (Z250). For each condition, half of the specimens was immediately submitted to microtensile test and half of them was submitted to long-term storage of 6 months under simulated pulpal pressure and thermo-mechanical stressing before testing. The data were analyzed using Two-Way ANOVA and Tukey post hoc test (alpha=0.05). Failure patterns of the specimens were observed using scanning electron microscopy. The falling % in bond strength over the 6-month period was: SB control-43.64%; SB/0.2%CHX-23.79%; SB/2%CHX-26.42%; CTSB control-40.94%; CTSB/0.2%CHX-37.07%; CTSB/2%CHX-22.14%. The fracture modes were predominantly adhesive, mainly in the specimens of terminal groups. CXH digluconate at 2% was able to diminish loss of microtensile bond strength over time associated to both etch-and-rinse and self-etch adhesives. Lower concentration of CHX (0.2%) was not able to diminish the loss of bond strength over time when associated to the self-etch adhesive CTSB.

Effect of a novel bioactive glass-ceramic on dentinal tubule occlusion: an in vitro study.

PubMed

Zhong, Y; Liu, J; Li, X; Yin, W; He, T; Hu, D; Liao, Y; Yao, X; Wang, Y

2015-03-01

This in vitro study aimed to assess the ability and efficacy of HX-BGC, a novel bioactive glass-ceramic (SiO2-P2 O5-CaO-Na2 O-SrO), to reduce dentine tubule permeability. Dentine discs from human third molars were etched and randomly allocated into five groups: Group 1--distilled water; Group 2--Sensodyne Repair toothpaste (containing NovaMin®); Group 3--HX-BGC toothpaste (containing 7.5% HX-BGC); Group 4--control toothpaste (without HX-BGC); and Group 5--HX-BGC powder. Specimens were treated daily by brushing with an electric toothbrush for 20 seconds. Between daily treatments (7 days total), specimens were immersed in artificial saliva for 24 hours. Dentine permeability was measured at baseline, after the first treatment, after the first 24-hour immersion in artificial saliva and at the end of day 7. Dentine morphology and surface deposits were observed by scanning electron microscopy after one day and 7 days of treatment, respectively. Sensodyne Repair and bioactive glass-ceramic toothpaste significantly and immediately lowered dentine permeability. The HX-BGC powder group showed the highest reduction in dentine permeability after 7 days of treatment. The novel bioactive glass-ceramic material HX-BGC is effective in reducing dentine permeability by occluding open dentine tubules, indicating that HX-BGC may be a potential treatment for dentine hypersensitivity. © 2015 Australian Dental Association.

Demonstration of a focused ion-beam cross-sectioning technique for ultrastructural examination of resin-dentin interfaces.

PubMed

Van Meerbeek, B; Conn, L J; Duke, E S; Schraub, D; Ghafghaichi, F

1995-03-01

focused ion-beam (FIB) etching, commonly used as a cross-sectioning technique for failure analysis of semiconductor devices, has recently been applied to biological tissues to expose their ultrastructure for examination. It was the aim of this investigation to determine the practical utility of FIB to cross-section resin-dentin interfaces in order to morphologically evaluate the completeness of resin penetration into the exposed collagen scaffold at the resin-dentin bond interface. Two representative commercially available dentin adhesive systems were bonded to mid-coronal dentin. After appropriate fixation and dehydration of the resin-bonded dentin samples, a scanned focused ion-beam of a few tens of nano-meters in diameter was used to cross=section the resin-dentin interface. Examination of the interfacial ultrastructure was accomplished using a field-emission SEM. Results indicate possible artifact production at the cross-sectioned interface, hiding its actual ultrastructure, probably due to a heat-effect with possible recrystallization. Further studies of FIB are needed to optimize its usefulness for resin-dentin interface examinations and other biological tissue applications. Complete resin saturation of the demineralized dentin surface-layer has been claimed to be the key factor for a long-lasting resin-dentin bond. A "clean" artifact-free micro-cross-sectioning technique may provide indisputable ultra-structural information about the depth of resin penetration into the demineralized zone. Such a test would be useful in the development of dentin adhesive systems.

Phosphorus Effects of Mesoporous Bioactive Glass on Occlude Exposed Dentin

PubMed Central

Chen, Wen-Cheng; Chen, Cheng-Hwei; Kung, Jung-Chang; Hsiao, Yu-Cheng; Shih, Chi-Jen; Chien, Chi-Sheng

2013-01-01

In recent studies, sealing of exposed dentinal tubules is generally considered as one of the most effective strategies to treat dentin hypersensitivity. Mesoporous bioactive glass (MBG) is a potential material for treating dentin hypersensitivity due to its highly specific areas for dissolution and re-precipitated reaction for reduction in dentin permeability. The groups of commercial products of PerioGlas®, synthetic MBG and MBG without phosphorus (MBGNP) were compared. The MBG and MBGNP powders were prepared by the sol-gel method and mixed with different calculated ratios of phosphoric acid (PA) and then was brushed onto dentin surfaces. We used X-ray diffractometer (XRD), scanning electronic microscope (SEM), and Fourier transform infrared spectroscopy (FTIR) to investigate the physiochemistry and the occlusion ability of dentinal tubules. The results showed that MBG paste mixed with PA solution has a better ability for occluding dentinal tubules than MBGNP; it has a short reaction time and good operability. The major crystallite phase of MBG agents was monocalcium phosphate monohydrate [Ca(H2PO4)2·H2O] in the early stages of the reactions. MBG pastes that were mixed with 30% and 40% PA had the ability to create excellent penetration depth greater than 80 μm. These agents have the potential to treat dentin hypersensitivity. PMID:28788393

Chlorhexidine stabilizes the adhesive interface: a 2 year in vitro study

PubMed Central

Breschi, Lorenzo; Mazzoni, Annalisa; Nato, Fernando; Carrilho, Marcela; Visintini, Erika; Tjäderhane, Leo; Ruggeri, Alessandra; Tay, Franklin R; De Stefano Dorigo, Elettra; Pashley, David H

2013-01-01

Objectives This study evaluated the role of endogenous dentin MMPs in auto-degradation of collagen fibrils within adhesive-bonded interfaces. The null hypotheses tested were that adhesive blends or chlorhexidine digluconate (CHX) application does not modify dentin MMPs activity and that CHX used as therapeutic primer does not improve the stability of adhesive interfaces over time. Methods Zymograms of protein extracts from human dentin powder incubated with Adper Scotchbond 1XT (SB1XT) on untreated or 0.2–2% CHX treated dentin were obtained to assay dentin MMPs activity. Microtensile bond strength and interfacial nanoleakage expression of SB1XT bonded interfaces (with or without CHX pre-treatment for 30s on the etched surface) were analyzed immediately and after 2 yr of storage in artificial saliva at 37°C. Results Zymograms showed that application of SB1XT to human dentin powder increases MMP-2 activity, while CHX pre-treatment inhibited all dentin gelatinolytic activity, irrespective from the tested concentration. CHX significantly lowered the loss of bond strength and nanoleakage seen in acid-etched resin-bonded dentin artificially aged for 2 yr. Significance The study demonstrates the active role of SB1XT in dentin MMP-2 activation and the efficacy of CHX inhibition of MMPs even if used at low concentration (0.2%). PMID:20045177

Tensile bond strength of indirect composites luted with three new self-adhesive resin cements to dentin.

PubMed

Türkmen, Cafer; Durkan, Meral; Cimilli, Hale; Öksüz, Mustafa

2011-08-01

The aims of this study were to evaluate the tensile bond strengths between indirect composites and dentin of 3 recently developed self-adhesive resin cements and to determine mode of failure by SEM. Exposed dentin surfaces of 70 mandibular third molars were used. Teeth were randomly divided into 7 groups: Group 1 (control group): direct composite resin restoration (Alert) with etch-and-rinse adhesive system (Bond 1 primer/adhesive), Group 2: indirect composite restoration (Estenia) luted with a resin cement (Cement-It) combined with the same etch-and-rinse adhesive, Group 3: direct composite resin restoration with self-etch adhesive system (Nano-Bond), Group 4: indirect composite restoration luted with the resin cement combined with the same self-etch adhesive, Groups 5-7: indirect composite restoration luted with self-adhesive resin cements (RelyX Unicem, Maxcem, and Embrace WetBond, respectively) onto the non-pretreated dentin surfaces. Tensile bond strengths of groups were tested with a universal testing machine at a constant speed of 1 mm/min using a 50 kgf load cell. Results were statistically analyzed by the Student's t-test. The failure modes of all groups were also evaluated. The indirect composite restorations luted with the self-adhesive resin cements (groups 5-7) showed better results compared to the other groups (p<0.05). Group 4 showed the weakest bond strength (p>0.05). The surfaces of all debonded specimens showed evidence of both adhesive and cohesive failure. The new universal self-adhesive resins may be considered an alternative for luting indirect composite restorations onto non-pretreated dentin surfaces.

Efficacy of a new filler-containing root coating material for dentin remineralization.

PubMed

Okuyama, Katsushi; Kadowaki, Yoshitaka; Matsuda, Yasuhiro; Hashimoto, Naoki; Oki, Saiko; Yamamoto, Hiroko; Tamaki, Yukimichi; Sano, Hidehiko

2016-08-01

To evaluate a new root coating material containing surface pre-reacted glass-ionomer (S-PRG) filler for remineralization of demineralized dentin. The dentin was exposed on root surfaces of human third molars and demineralized by immersion in demineralization solution for 4 days. The demineralized dentin surface was divided into three areas. The center area was left untreated. The area on one side of the center area was coated with protective wax. The area on the other side was coated with one of four test materials: fluoride-containing S-PRG filler (PRG Barrier Coat: PR), fluoride-containing bonding agent (Bond Force: BF), fluoride-containing glass-ionomer cement as a positive control (Fuji IX EXTRA: EX), or non-fluoride-containing bonding agent as a negative control (Clearfil MegaBond: MB). The samples were stored in remineralization solution for 7 days, and then cut into two slices. The mineral changes, defined as variation in mineral loss between wax-coated area and the central untreated area, were measured in one slice by transversal microradiography. The fluoride concentration was measured in the other slice by µ-particle-induced gamma/X-ray emission. Seven thin specimens (0.25-mm thickness) of each test material were used to determine fluoride ion release from the materials over 21 days. The mineral changes were greatest for EX, followed by PR, with no difference between BF and MB (P> 0.05). Regarding the fluoride concentrations in dentin, there was no difference between EX and PR (P> 0.05). MB had the lowest value (P< 0.01). Fluoride release from EX was largest, followed by PR, with BF showing low fluoride release (P< 0.05). MB had no fluoride release. A new coating material with S-PRG filler can be applied in a thin layer on root dentin, which could be especially useful for hard-to-access lesions. This material remineralized demineralized root dentin and had fluoride diffusion characteristics similar to those of glass-ionomer cement in vitro.

An experiment on the attrition of acid demineralized dentine in vitro.

PubMed

Li, H; Liu, M C; Deng, M; Moazzez, R; Bartlett, D W

2011-03-01

A laboratory investigation was designed to test the hypothesis that acids increase the rate of wear caused by attrition on dentine. Dentine sections from 10 teeth were polished, cleaned in an ultrasonic bath and divided into 8 equally sized areas. The occlusal tip of a tooth, placed vertically in a wear machine and loaded at 150 N, was moved against each dentine section for 5000 return strokes with artificial saliva acting as a lubricant. Each dentine section was divided into 8 sections and half randomly immersed in a 1% citric acid solution (pH 2.3) for 20 minutes. The wear regime produced 8 wear scars in total per dentine sample. The volume of each wear scar was measured using a contacting digitizing profilometer. A total of 80 wear scars were produced with 40 treated with acid and 40 acting as controls. The mean for wear volume of the dentine scars with acid was 4.84 μm(3) (1.38) and for the non-acid surface 2.95 μm(3) (0.86). This difference was statistically significant (p < 0.05). These results support the hypothesis that acids increase the rate of wear caused by attrition on dentine. © 2011 Australian Dental Association.

Grape seed extracts inhibit dentin matrix degradation by MMP-3

PubMed Central

Khaddam, Mayssam; Salmon, Benjamin; Le Denmat, Dominique; Tjaderhane, Leo; Menashi, Suzanne; Chaussain, Catherine; Rochefort, Gaël Y.; Boukpessi, Tchilalo

2014-01-01

Since Matrix metalloproteinases (MMPs) have been suggested to contribute to dentin caries progression, the hypothesis that MMP inhibition would affect the progression of dentin caries is clinically relevant. Grape seed extracts (GSE) have been previously reported to be natural inhibitors of MMPs. Objective: To evaluate the capacity of a GSE mouthrinse to prevent the degradation of demineralized dentin matrix by MMP-3 (stromelysin-1). Materials and Methods: Standardized blocks of dentin obtained from sound permanent teeth extracted for orthodontic reasons were demineralized with Ethylenediaminetetraacetic acid (EDTA) and pretreated either with (A) GSE (0.2% w/v), (B) amine fluoride (AmF) (20% w/v), (C) a mouthrinse which contains both, (D) placebo, (E) sodium fluoride (0.15 mg.ml−1), (F) PBS, (G) Chlorhexidine digluconate (CHX), or (H) zinc chloride (ZnCl2). The dentin blocks were then incubated with activated recombinant MMP-3. The supernatants were analyzed by Western Blot for several dentin matrix proteins known to be MMP-3 substrate. In parallel, scanning electron microscopy (SEM) was performed on resin replica of the dentin blocks. Results: Western blot analysis of the supernatants revealed that MMP-3 released from the dentin matrix small proteoglycans (decorin and biglycan) and dentin sialoprotein (DSP) in the AmF, sodium fluoride, PBS and placebo pretreated groups, but not in the GSE and mouthrinse pretreated groups. SEM examination of resin replica showed that the mouthrinse and its active components not only had an anti-MMP action but also modified the dentin surface accessibility. Conclusion: This study shows that GSE either alone or combined with AmF as in the evaluated mouthrinse limits dentin matrix degradation. This association may be promising to prevent the progression of caries within dentin. However, the procedure should be adapted to clinically relevant durations. PMID:25400590

Shear bond strength of one-step self-etch adhesives to dentin: Evaluation of NaOCl pretreatment.

PubMed

Colombo, Marco; Beltrami, Riccardo; Chiesa, Marco; Poggio, Claudio; Scribante, Andrea

2018-02-01

The aim of this study was to evaluate the influence of dentin pretreatment with NaOCl on shear bond strength of four one-step self-etch adhesives with different pH values. Bovine permanent incisors were used. Four one-step self-etch adhesives were tested: Adper™ Easy Bond, Futurabond NR, G-aenial Bond, Clearfil S3 Bond. One two-step self-etch adhesive (Clearfil SE Bond) was used as control. Group 1- no pretreatment; group 2- pretratment with 5,25 % NaOCl; group 3- pretreatment with 37 % H3PO4 etching and 5,25 % NaOCl. A hybrid composite resin was inserted into the dentin surface. The specimens were tested in a universal testing machine. The examiners evaluated the fractured surfaces in optical microscope to determine failure modes, quantified with adhesive remnant index (ARI). Dentin pretreatment variably influenced bond strength values of the different adhesive systems. When no dentin pretreatment was applied, no significant differences were found ( P >.05) among four adhesives tested. No significant differences were recorded when comparing NaOCl pretreatment with H3PO4 + NaOCl pretreatment for all adhesive tested ( P >.05) except Clearfil S3 Bond that showed higher shear bond strength values when H3PO4 was applied. Frequencies of ARI scores were calculated. The influence of dentin pretreatment with NaOCl depends on the composition of each adhesive system used. There was no difference in bond strength values among self-etch adhesives with different pH values. Key words: Dentin, pretreatment, self-etch adhesives.

Nondestructive assessment of dentin demineralization using polarization sensitive optical coherence tomography after exposure to fluoride and laser irradiation

PubMed Central

Manesh, Saman K.; Darling, Cynthia L.; Fried, Daniel

2009-01-01

Previous studies have demonstrated that polarization sensitive optical coherence tomography (PS-OCT) can be used to image natural and artificial caries in dentin. The purpose of this study was to measure non-destructively the severity of artificial caries lesions in dentin and determine the efficacy of intervention with anti-caries agents including fluoride and lasers. Although several studies have assessed the utility of PS-OCT to image caries lesions in enamel and to quantify the lesion severity, only a few studies have focused on lesions in dentin. In this study images of artificial dentin lesions on extracted human teeth were acquired with PS-OCT. Before exposure to an artificial demineralizing solution, three incisions were made on the sample surfaces using either Er:YAG, Nd:YAG (λ=355-nm), or TEA CO2 lasers and selected areas were treated with topical fluoride to create six unique treatment areas for each of the three laser conditions investigated. The integrated reflectivity and depth of demineralization were calculated for each of the six areas on each sample using the PS-OCT images. Polarized light microscopy (PLM) and transverse microradiography (TMR) were used to measure lesion severity on histological thin sections for comparison. PS-OCT successfully measured the inhibition of demineralization by topical fluoride. Laser irradiation was not particularly effective in increasing or decreasing the rate of dentin demineralization. PLM and TMR corroborated those results. This study demonstrates that PS-OCT can be used to measure demineralization on dentin surfaces and determine the degree of inhibition of demineralization by anti-caries agents. PMID:19283826

Histologic and SEM evaluation of caries removal and restoration in enamel and dentin using a pulsed fiber optic delivered Nd:YAG laser

NASA Astrophysics Data System (ADS)

White, Joel M.; Goodis, Harold E.; Kudler, Joel J.; Eakle, W. S.; Neev, Joseph

1994-09-01

The pulsed Nd:YAG laser has been proposed as an alternative to the dental handpiece for caries removal in enamel and dentin. The purpose of this study was to systematically evaluate, in vitro, the process of caries removal and restoration in enamel and dentin. The effectiveness of this device was investigated utilizing scanning electron microscopy to determine the behavior of dentin after laser treatment of artificially created carious lesions in dentin. Histologic sections of extracted teeth after laser treatment and restoration demonstrated successful caries removal and restoration using the pulsed fiber optic delivered Nd:YAG laser as compared to both high and low speed rotary instrumentation. The adjacent enamel and dentin were unaffected by the laser irradiation although slight carbonization was seen on the dentin surface. Thermocouples placed in the pulp chamber during caries removal confirmed previous studies that showed laser parameters up to 1 W and 10 Hz being the same as conventional caries removal in the amount of heat generated which reaches the pulp. The addition of air/water coolant decreased pulpal temperature.

Dentin hypersensitivity: from diagnosis to a breakthrough therapy for everyday sensitivity relief.

PubMed

Cummins, Diane

2009-01-01

This paper provides an overview of the current knowledge of diagnosis, epidemiology, etiology, and clinical management of dentin hypersensitivity. It summarizes technical approaches to relieve sensitivity in professional and home-use products, with emphasis on the clinical evidence for the efficacy of desensitizing toothpaste, and introduces a new innovative dentifrice technology containing 8% arginine, calcium carbonate, and 1450 ppm fluoride. Dentin hypersensitivity is characterized by short, sharp pain arising from exposed dentin in response to external stimuli which cannot be ascribed to any other form of dental defect or disease. The hydrodynamic theory proposes that pain-producing stimuli cause a change in dentin fluid flow that activates intra-dental nerve fibers, via a mechanoreceptor response, to cause pain. To be hypersensitive, dentin must be exposed and dentin tubules must be open to external stimuli and patent at the pulp. Gingival recession is the primary cause of dentin exposure, and a major predisposing factor for dentin hypersensitivity. Dentin hypersensitivity is a prevalent condition. It has been reported to afflict 15-20% of the adult population, typically 20 to 50-year-olds, with peak incidence between 30 and 39 years. Some studies have reported higher prevalence levels of up to 57%. The incidence of dentin hypersensitivity is expected to rise with changing diets, and as caries and periodontal disease prevention result in improved oral health status, and retention and functionality of the dentition. Treatments to relieve dentin hypersensitivity are based on interruption of the neural response to pain stimuli or occlusion of open tubules to block the hydrodynamic mechanism. Effective and robust dentin occlusion offers the greatest prospect for instant and lasting relief of dentin hypersensitivity. In particular, materials which can coat exposed dentin surfaces, in addition to plugging and sealing open dentin tubules, offer the intriguing prospect of strengthening dentin and rendering it less susceptible to predisposing factors, while concurrently reducing dentin hypersensitivity. Clinical studies have shown that a new toothpaste containing 8% arginine, calcium carbonate, and 1450 ppm fluoride as sodium monofluorophosphate offers significantly increased efficacy in reducing sensitivity, compared to a market-leading toothpaste containing 2% potassium ion. Mechanism of action studies have shown that this technology physically seals dentin tubules with a plug that contains arginine, calcium carbonate, and phosphate. This plug, which is resistant to normal pulpal pressures and to acid challenge, effectively reduces dentin fluid flow and, thereby, reduces sensitivity.

Effect of surface treatments on the flexural properties and adhesion of glass fiber-reinforced composite post to self-adhesive luting agent and radicular dentin.

PubMed

Elnaghy, Amr M; Elsaka, Shaymaa E

2016-01-01

This study evaluated the effect of different surface treatments on the flexural properties and adhesion of glass fiber post to self-adhesive luting agent and radicular dentin. Seventy-five single-rooted human teeth were prepared to receive a glass fiber post (Reblida). The posts were divided into five groups according to the surface treatment: Gr C (control; no treatment), Gr S (silanization for 60 s), Gr AP (airborne-particle abrasion), Gr HF (etching with 9 % hydrofluoric acid for 1 min), and Gr M10 (etching with CH2Cl2 for 10 min). Dual-cure self-adhesive luting agent (Rely X Unicem) was applied to each group for testing the adhesion using micropush-out test. Failure types were examined with stereomicroscope and surface morphology of the posts was characterized using a scanning electron microscopy (SEM). Flexural properties of posts were assessed using a three-point bending test. Data were analyzed using ANOVA and Tukey's HSD test. Statistical significance was set at the 0.05 probability level. Groups treated with M10 showed significantly higher bond strength than those obtained with other surface treatments (P < 0.05). In general, improvements in bond strength (MPa) were found in the following order: M10 > C > S > AP > HF. Most failure modes were adhesive type of failures between dentin and luting agent (48.2%). SEM analysis revealed that the fiber post surfaces were modified after surface treatments. The surface treatments did not compromise the flexural properties of fiber posts. Application of M10 to the fiber post surfaces enhanced the adhesion to self-adhesive luting agent and radicular dentin.

[Clinical research of EDTA pretreatment on the bonding strength of resin].

PubMed

Li, Ting-ting; Sun, Min-min; Kang, Jun-tang; Sun, Zhe

2015-10-01

This study was to evaluate clinical results of adhesives to sclerotic dentin in non-carious cervical lesions pretreated with ethylene diamine tetraacetic acid (EDTA). Twelve patients who had at least one pair of teeth with typical cervical wedge-shaped defects and class III sclerotic dentin were selected. The teeth were randomly divided into experimental and control groups. In the experimental group, EDTA was used to pretreat dentin surface first and then self-etching resin adhesive; In the control group, only self-etching resin adhesive was used. Modified USPHS rating system was applied in baseline, 6 months and 12 months after treatment. SAS 8.02 software package was used for two-sample rank sum test. At the time point of 6-month and 12-month, the scores in the experimental group were significantly better than the control group (P<0.05). EDTA pretreatment of the sclerotic dentin of cervical wedge-shaped defects could improve the resin bonding strength, marginal discoloration, marginal form and surface quality.

Effects of various final irrigants on the shear bond strength of resin-based sealer to dentin.

PubMed

Kandaswamy, Deivanayagam; Venkateshbabu, Nagendrababu; Arathi, Ganesh; Roohi, Riaz; Anand, Suresh

2011-01-01

This study has been designed to evaluate the effect of strong (MTAD) or soft (1- hydroxyethylidene - 1, 1-bisphosphonate (HEBP) final irrigating solution on the shear bond strength of AH plus sealer to coronal dentin. 17% EDTA was used as the reference. Forty freshly extracted human maxillary first premolars were prepared using different irrigation protocols (n=10). All the test groups had 1.3% NaOCl as initial rinse and followed by specific final rinse for each group: G1 - distilled water(control), G2 - 17% EDTA, G3- 18% HEBP and G4 - MTAD. Sections of polyethylene tubes that are 3mm long were filled with freshly mixed sealer and placed on the dentin surfaces. The bonding between the sealer and dentine surface was evaluated using shear bond testing. The values were statistically evaluated using one-way ANOVA followed by Tukey's test. Significant difference was found among the irrigating regimes. EDTA showed highest bond strength followed by HEBP and MTAD.

A biomimetic approach to ameliorate dental hypersensitivity by amorphous polyphosphate microparticles.

PubMed

Müller, Werner E G; Neufurth, Meik; Tolba, Emad; Wang, Shunfeng; Geurtsen, Werner; Feng, Qingling; Schröder, Heinz C; Wang, Xiaohong

2016-06-01

Dental hypersensitivity has become one of the most common and most costly diseases in the world, even though those maladies are very rarely life threatening. Using amorphous microparticles, fabricated from the natural polymer (polyphosphate), we intend to reseal the dentinal tubules exposed and reduce by that the hypersensitivity. Amorphous microparticles (termed aCa-polyP-MP) were prepared from Na-polyphosphate (polyP) and CaCl2, then incubated with human teeth. The potential of the microparticles to plug the dentinal tubules was determined by microscopic and spectroscopic techniques. We demonstrate that, in contrast to polyP, the aCa-polyP-MP efficiently reseal dentinal tubules exposed at the tooth surface. Scanning electron microscopical (SEM) and energy dispersive X-ray spectroscopic (EDX) studies showed that the tooth cement and dentin surfaces, incubated with aCa-polyP-MP, form a nearly homogenous, approximately 50-μm thick solid polyP layer on the tooth cement and dentin surfaces, while no coating on the tooth surface, incubated with Na-polyP [Ca(2+)], was observed. Determination of the mechanical properties of the polyP coating revealed a Martens hardness of 3.85±0.64GPa and a reduced elastic modulus of 94.72±8.54GPa already after a 3h exposure to the aCa-polyP-MP, which become close to those of the natural enamel (4.33±0.69GPa and 101.61±8.52GPa, respectively) after prolonged incubation periods. In addition, aCa-polyP-MP turned out to display morphogenetic activity. Incubation of precursor odontoblasts cultures in the presence of aCa-polyP-MP resulted in a 7-fold increase of the steady-state-expression level of the gene encoding for the alkaline phosphatase (ALP) during a 7 d incubation period. Ca-polyP microparticles, consisting of the biocompatible natural polymer polyP, provide a potential sealing material for dentinal tubules on the tooth surface. Copyright © 2016 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of the coating material on root dentin remineralization in vitro.

PubMed

Shiiya, Toru; Tomiyama, Kiyoshi; Iizuka, Junko; Hasegawa, Haruhiko; Kuramochi, Erika; Fujino, Fukue; Ohashi, Katsura; Nihei, Tomotaro; Teranaka, Toshio; Mukai, Yoshiharu

2014-10-01

A fluoride-releasing coating material containing surface pre-reacted glass-ionomer (S-PRG) filler has become commercially available. However, there has been no detailed investigation of its remineralization effects at various tooth surface regions. The remineralization effects of S-PRG filler-containing coating material at different sites of demineralized dentin surfaces in vitro were evaluated. Baseline lesions were prepared on bovine root dentin surfaces by immersion in demineralization buffer and divided into four groups: (B)--baseline lesion; (P)--S-PRG filler-containing material; (V)--S-PRG filler-free coating material as negative control; and (X)--resin-modified glass- ionomer as positive control. Material was applied to half the lesion surface, then P, V and X were remineralized in a gel system. Mineral profiles, integrated mineral loss (IML) and lesion depth (LD) at four regions, i.e. 1--exposed dentin surface adjacent to the material; 2--at a distance from the material; 3--beneath the material near to the edge; and 4--at a distance from the edge, were analyzed by transversal microradiography. Data were analyzed using ANOVA and Games-Howell test with α = 0.05. B showed typical artificial demineralized lesion. The IMLs of V, P and X at regions 1 and 2, and P and X at region 3 were significantly lower than that of B, however, those of V at region 3 and the other three groups at region 4 were not significantly different from that of B. At region 1, P and X showed significantly lower IMLs than V. At region 2, the IML of X showed significantly lower IML than V. There was no significant difference between P and X. The LD values of V, P and X at all regions were not significantly different from that of B. Fluoride, strontium and silicate ions released from the S-PRG filler would provide a favorable environment for remineralization of the demineralized dentin in P.

Dentin and pulp sense cold stimulus.

PubMed

Tokuda, Masayuki; Tatsuyama, Shoko; Fujisawa, Mari; Morimoto-Yamashita, Yoko; Kawakami, Yoshiko; Shibukawa, Yoshiyuki; Torii, Mistuso

2015-05-01

Dentin hypersensitivity is a common symptom, and recent convergent evidences have reported transient receptor potential (TRP) channels in odontoblasts act as mechanical and thermal molecular sensor, which detect stimulation applied on the exposed dentin surface, to drive multiple odontoblastic cellular functions, such as sensory transduction and/or dentin formation. In the present study, we confirmed expression of TRP melastatin subfamily member-8 (TRPM8) channels in primary cultured cells derived from human dental pulp cells (HPCs) and mouse odontoblast-lineage cells (OLCs) as well as in dentin matrix protein-1 (DMP-1) and dentin sialoprotein (DSP) positive acutely isolated rat odontoblasts from dental pulp tissue slice culture by immunohistochemical analyses. In addition, we detected TRPM8 channel expression on HPCs and OLCs by RT-PCR and Western blotting analyses. These results indicated that both odontoblasts and dental pulp cells express TRPM8 channels in rat, mouse and human, and therefore we hypothesize they may contribute as cold sensor in tooth. Copyright © 2015 Elsevier Ltd. All rights reserved.

Influence of an arginine-containing toothpaste on bond strength of different adhesive systems to eroded dentin.

PubMed

Bergamin, Ana Cláudia Pietrobom; Bridi, Enrico Coser; Amaral, Flávia Lucisano Botelho; Turssi, Cecília Pedroso; Basting, Roberta Tarkany; Aguiar, Flávio Henrique Baggio; França, Fabiana Mantovani Gomes

2016-01-01

The aim of this study was to evaluate the bond strength of different adhesive systems to eroded dentin following toothbrushing with an arginine-containing toothpaste. Sixty standardized 3 × 3 × 2-mm fragments of root dentin (n = 10) were prepared. After all surfaces except the buccal surfaces were impermeabilized, specimens were subjected to an erosive wear protocol and stored for 24 hours at 37°C. The specimens underwent 1000 toothbrushing cycles with an arginine-containing toothpaste, an arginine-free toothpaste (positive control group), or artificial saliva (negative control group). Following application of a self-etching or an etch-and-rinse adhesive to the buccal surfaces of the specimens, 6-mm-high composite resin blocks were built up in 2-mm increments. After 24 hours' storage in 100% relative humidity, microtensile test specimens with an approximate area of 1 mm² were prepared. The test was performed at a speed of 0.5 mm/min until specimen fracture, and the failure patterns were evaluated using a stereoscopic loupe. Two-way analysis of variance revealed no significant difference between the toothpastes, the adhesive systems, or the interactions between toothpaste and adhesive system in terms of the bond strength to eroded dentin (P > 0.05). The predominant failure pattern was adhesive in all groups. It was concluded that a toothpaste containing arginine did not interfere with the bond between either the self-etching or the etch-and-rinse adhesive system and eroded dentin.

Preventive effect of a high fluoride toothpaste and arginine-carbonate toothpaste on dentinal tubules exposure followed by acid challenge: a dentine permeability evaluation

PubMed Central

2014-01-01

Background Considering the current high use of high fluoride toothpastes, the aim of the study was to quantify alterations in the root dentine permeability submitted to treatment with a high fluoride toothpaste and 8% arginine, calcium carbonate, sodium monofluorophosphate toothpaste as a preventive treatment for dentinal tubules exposure followed by acid challenge. Methods Thirty-third molars were sectioned below the cementoenamel. The root segments were connected to a hydraulic pressure apparatus to measure dentine permeability after the following sequential steps (n = 10 per group): I) Baseline; II) treatment with phosphoric acid for 30 s (maximum permeability); III) Toothbrushing (1 min) according to the experimental groups (G1- control; G2- 5000 ppm fluoride toothpaste; G3- 8% arginine-calcium carbonate toothpaste); IV) acid challenge for 5 min (orange juice). The data were converted into percentage, considering stage II as 100%. Results The results have shown a statistically significant decreasing on dentine permeability after treatment with toothpaste (Friedman test and Dunn’s post hoc test). Comparison among groups demonstrated a high increasing on dentine permeability when acid challenge was performed after toothbrushing with distilled water (control group) (Kruskal-Wallis and Dunn’s post hoc test). Conclusion The toothpaste treatment may provide sufficient resistance on dentine surface, preventing dentinal tubules exposure after acid challenge. PMID:24958423

Effects of different peracetic acid formulations on post space radicular dentin.

PubMed

Belizário, Lauriê Garcia; Kuga, Milton Carlos; Castro-Núñez, Gabriela Mariana; Escalante-Otárola, Wilfredo Gustavo; Só, Marcus Vinicius Reis; Pereira, Jefferson Ricardo

2018-01-05

The optimal irrigating solution with antimicrobial and dentin cleansing properties for post space preparation for fiber posts is unclear. Peracetic acid is one option but is available in various chemical formulations that require evaluation. The purpose of this in vitro study was to evaluate dentin surface cleanliness based on the presence of a smear layer and the number of open dentin tubules. It also investigates the chemical composition of residues after canal irrigation with a 1% peracetic acid solution (PA) at low or high concentration of hydrogen peroxide during the preparation of intracanal fiber posts. After filling the root canals of 40 mandibular incisors, a rotary instrument was used for intracanal preparation to place fiber posts. The teeth were divided into 4 groups (n=10) according to the post space irrigation protocol as follows: CG (control): distilled water; NA (NaOCl): 2.5% sodium hypochlorite; LH: PA with low concentration of hydrogen peroxide; and HH: PA with high concentrations of hydrogen peroxide. After irrigation, the teeth were sectioned, and the intracanal dentin surface was subjected to analysis using energy dispersive spectroscopy to evaluate chemical composition and to scanning electron microscopy (×500) to evaluate the presence of the smear layer. The number of open dentin tubules was measured by scanning electron microscopy analysis (×2000) using photo-editing software. ANOVA and the Tukey test (α=.05) were used to evaluate the data, except for the presence of a smear layer, for which the Kruskal-Wallis and Dunn tests were used (α=.05). The highest concentrations of oxygen in the dentin residues were detected in LH and HH (P<.05); CG and NA showed similar oxygen concentrations (P>.05). NA had a higher concentration of chlorine (P<.05), whereas LH had a lower amount of smear layer and a larger number of open dentin tubules than the other groups (P<.05). These were equivalent to each other (P>.05), except for HH, which also had a larger number of open dentin tubules than CG and NA (P<.05). PA 1% with a low concentration of hydrogen peroxide yielded a lower amount of smear layer and a larger number of open dentin tubules in the dentin of the post space when compared with PA 1% with a high concentration of hydrogen peroxide, despite maintaining a similar oxygen concentration in these dentin residues. Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Remineralization of artificial dentinal caries lesions by biomimetically modified Mineral Trioxide Aggregate

PubMed Central

Qi, Yi-pin; Li, Nan; Niu, Li-na; Primus, Carolyn M.; Ling, Jun-Qi; Pashley, David H.; Tay, Franklin R.

2011-01-01

Fluoride-releasing restorative materials are available for remineralization of enamel and root caries. However, dentin remineralization is more difficult than enamel remineralization due to the paucity of apatite seed crystallites along the lesion surface for heterogeneous crystal growth. Extracellular matrix proteins play critical roles in controlling apatite nucleation/growth in collagenous tissues. This study examined the remineralization efficacy of mineral trioxide aggregate (MTA) in phosphate-containing simulated body fluid (SBF) by incorporating polyacrylic acid and sodium tripolyphosphate as biomimetic analogs of matrix proteins for remineralizing caries-like dentin. Artificial caries-like dentin lesions incubated in SBF were remineralized over a 6-week period using MTA or MTA containing biomimetic analogs in the absence or presence of dentin adhesive application. Lesion depths and integrated mineral loss were monitored with micro-computed tomography. Ultrastructure of baseline and remineralized lesions were examined by transmission electron microscopy. Dentin remineralization was best achieved using MTA containing biomimetic analogs regardless of whether an adhesive was applied; dentinal tubules within the remineralized dentin were occluded by apatite. It is concluded that the MTA version employed in the study may be doped with biomimetic analogs for remineralization of unbonded and bonded artificial caries-like lesions in the presence of SBF. PMID:22085925

Remineralization of artificial dentinal caries lesions by biomimetically modified mineral trioxide aggregate.

PubMed

Qi, Yi-pin; Li, Nan; Niu, Li-na; Primus, Carolyn M; Ling, Jun-Qi; Pashley, David H; Tay, Franklin R

2012-02-01

Fluoride-releasing restorative materials are available for remineralization of enamel and root caries. However, remineralization of dentin is more difficult than remineralization of enamel due to the paucity of apatite seed crystallites along the lesion surface for heterogeneous crystal growth. Extracellular matrix proteins play critical roles in controlling apatite nucleation/growth in collagenous tissues. This study examined the remineralization efficacy of mineral trioxide aggregate (MTA) in phosphate-containing simulated body fluid (SBF) by incorporating polyacrylic acid and sodium tripolyphosphate as biomimetic analogs of matrix proteins for remineralizing caries-like dentin. Artificial caries-like dentin lesions incubated in SBF were remineralized over a 6 week period using MTA alone or MTA containing biomimetic analogs in the absence or presence of dentin adhesive application. Lesion depths and integrated mineral loss were monitored with microcomputed tomography. The ultrastructure of baseline and remineralized lesions was examined by transmission electron microscopy. Dentin remineralization was best achieved using MTA containing biomimetic analogs regardless of whether an adhesive was applied; dentinal tubules within the remineralized dentin were occluded by apatite. It is concluded that the version of MTA employed in this study may be doped with biomimetic analogs for remineralization of unbonded and bonded artificial caries-like lesions in the presence of SBF. Copyright © 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

The Dentin Sialoprotein (DSP) Domain Regulates Dental Mesenchymal Cell Differentiation through a Novel Surface Receptor

PubMed Central

Wan, Chunyan; Yuan, Guohua; Luo, Daoshu; Zhang, Lu; Lin, Heng; Liu, Huan; Chen, Lei; Yang, Guobin; Chen, Shuo; Chen, Zhi

2016-01-01

Dentin sialophosphoprotein (DSPP) is a dentin extracellular matrix protein that is processed into dentin sialoprotein (DSP), dentin glycoprotein (DGP) and dentin phosphoprotein (DPP). DSP is mainly expressed in odontoblasts. We hypothesized that DSP interacts with cell surface receptors and subsequently activates intracellular signaling. Using DSP as bait for screening a protein library, we demonstrate that DSP acts as a ligand and binds to integrin β6. The 36 amino acid residues of DSP are sufficient to bind to integrin β6. This peptide promoted cell attachment, migration, differentiation and mineralization of dental mesenchymal cells. In addition, DSP aa183-219 stimulated phosphorylation of ERK1/2 and P38 kinases. This activation was inhibited by an anti-integrin β6 antibody and siRNA. Furthermore, we demonstrate that this DSP fragment induces SMAD1/5/8 phosphorylation and nuclear translocation via ERK1/2 and P38 signaling. SMAD1/5/8 binds to SMAD binding elements (SBEs) in the DSPP gene promoter. SBE mutations result in a decrease in DSPP transcriptional activity. Endogenous DSPP expression was up-regulated by DSP aa183-219 in dental mesenchymal cells. The data in the current study demonstrate for the first time that this DSP domain acts as a ligand in a RGD-independent manner and is involved in intracellular signaling via interacting with integrin β6. The DSP domain regulates DSPP expression and odontoblast homeostasis via a positive feedback loop. PMID:27430624

The Dentin Sialoprotein (DSP) Domain Regulates Dental Mesenchymal Cell Differentiation through a Novel Surface Receptor.

PubMed

Wan, Chunyan; Yuan, Guohua; Luo, Daoshu; Zhang, Lu; Lin, Heng; Liu, Huan; Chen, Lei; Yang, Guobin; Chen, Shuo; Chen, Zhi

2016-07-19

Dentin sialophosphoprotein (DSPP) is a dentin extracellular matrix protein that is processed into dentin sialoprotein (DSP), dentin glycoprotein (DGP) and dentin phosphoprotein (DPP). DSP is mainly expressed in odontoblasts. We hypothesized that DSP interacts with cell surface receptors and subsequently activates intracellular signaling. Using DSP as bait for screening a protein library, we demonstrate that DSP acts as a ligand and binds to integrin β6. The 36 amino acid residues of DSP are sufficient to bind to integrin β6. This peptide promoted cell attachment, migration, differentiation and mineralization of dental mesenchymal cells. In addition, DSP (aa183-219) stimulated phosphorylation of ERK1/2 and P38 kinases. This activation was inhibited by an anti-integrin β6 antibody and siRNA. Furthermore, we demonstrate that this DSP fragment induces SMAD1/5/8 phosphorylation and nuclear translocation via ERK1/2 and P38 signaling. SMAD1/5/8 binds to SMAD binding elements (SBEs) in the DSPP gene promoter. SBE mutations result in a decrease in DSPP transcriptional activity. Endogenous DSPP expression was up-regulated by DSP (aa183-219) in dental mesenchymal cells. The data in the current study demonstrate for the first time that this DSP domain acts as a ligand in a RGD-independent manner and is involved in intracellular signaling via interacting with integrin β6. The DSP domain regulates DSPP expression and odontoblast homeostasis via a positive feedback loop.

Short communication: pre- and co-curing effect of adhesives on shear bond strengths of composite resins to primary enamel and dentine: an in vitro study.

PubMed

Viswanathan, R; Shashibhushan, K K; Subba Reddy, V V

2011-12-01

To evaluate and compare shear bond strengths of composite resins to primary enamel and dentine when the adhesives are pre-cured (light cured before the application of the resin) or co-cured (adhesive and the resin light cured together). Buccal surfaces of 80 caries-free primary molars were wet ground to create bonding surfaces on enamel and dentine and specimens mounted on acrylic blocks. Two bonding agents (Prime and Bond NT® and Xeno III®) were applied to either enamel or dentine as per manufacturer's instructions. In 40 specimens, the bonding agent was light cured immediately after the application (pre-cured). The other 40 specimens were not light cured until the composite resin application (co-cured). Resin composite cylinders were made incrementally using acrylic moulds over the adhesives and light cured. Specimens were stored in deionised water for 24 hours at room temperature. Shear bond strength was measured using an Instron universal testing machine (in MPa) and was analysed with Student's unpaired t test. Light curing the adhesive separately produced significantly higher bond strengths to primary dentine than co-curing (p<0.001). At the same time light curing the adhesive separately did not produce significantly different bond strengths to primary enamel (p>0.05). Curing sequence had no significant effect on shear bond strength of adhesives on the primary enamel. Pre-curing adhesives before curing composite resins produced greater shear bond strength to primary dentine.

Improved degree of conversion of model self-etching adhesives through their interaction with dentin

PubMed Central

Zhang, Ying; Wang, Yong

2011-01-01

Objective To investigate the correlation of the chemical interaction between model self-etching adhesives and dentin with the degree of conversion (DC) of the adhesives. Methods The model self-etching adhesives contained bis[2-methacryloyloxy)ethyl] phosphate (2MP) and 2-hydroxyethyl methacrylate (HEMA) with a mass ratio of 1/1, and 0-40% water contents, respectively. The adhesives were applied either onto the prepared dentin surface or unreactive substrates (such as glass slides), agitated for 15s, then light-cured for 40s. The DCs of the adhesives were determined using micro-Raman spectral and mapping analysis. Results The DCs of the adhesives cured on the dentin substrate were found to be significantly higher than those on the unreactive glass substrate. Moreover, the DCs of the adhesives displayed a decreasing trend as the distance from the dentin surface became greater. The chemical interaction of the acidic 2MP/HEMA adhesives with the mineral apatite in dentin was proposed to play a significant role for the observations. The chemical interaction could be validated by the spectral comparison in the phosphate regions of 1100 cm−1 and 960 cm−1 in the Raman spectra. The results also revealed a notable influence of water content on the DC of adhesives. The DCs of the adhesive at 10% water content exhibited the highest DC level for both substrates. Conclusions Interaction with dentin dramatically improved the degree of conversion of self-etching adhesives. Our ability to chemically characterize the a/d interface including in situ detection of the DC distribution is very important in understanding self-etching adhesive bonding under in vivo conditions. PMID:22024375

Effect of Er:YAG laser pulse duration on the shear bond strength of bleached dentin

NASA Astrophysics Data System (ADS)

Yu, Ping; Yu, Dandan; Zhao, Peng; Xu, Zhou; Gao, Shanshan

2017-11-01

The influence of different Er:YAG laser pulse durations on the shear bond strength (SBS) of bleached dentin was investigated in this study. In total, 176 crowns of extracted human premolars were cut horizontally, embedded and ground to expose the sound dentin. Of these, 132 specimens were bleached with 12% hydrogen peroxide (HP) and divided into three groups, irradiated by an Er:YAG laser with different pulse lengths of 50 µs super short pulse (SSP), 100 µs moderate short pulse (MSP) and 300 µs short pulse (SP), respectively. The energy density of the three groups was the same at about 15.73 J cm-2 for each. Then, each group was further divided into two subgroups according to whether it had been etched with 37% phosphoric acid or not. The control group (N  =  22) was bleached and etched with acid while the blank group (N  =  22) was just etched with acid. The surface morphology of the dentin was observed using scanning electron microscopy (SEM). The SBS of the composite resin to the conditioned dentin was tested with a universal testing machine. It was found that the SBS of the dentin significantly decreased after bleaching treatment, while it was possible to restore it using Er:YAG laser irradiation. Lasers with various pulse durations led to different surface morphologies but had no effect on the SBS. The SSP laser was more suitable on account of it resulting in less thermal damage, and additional acid etching was not necessary for the irradiated bleached dentin in the clinic because it could not further improve the SBS value.

Improved degree of conversion of model self-etching adhesives through their interaction with dentine.

PubMed

Zhang, Ying; Wang, Yong

2012-01-01

To investigate the correlation of the chemical interaction between model self-etching adhesives and dentine with the degree of conversion (DC) of the adhesives. The model self-etching adhesives contained bis[2-methacryloyloxy)ethyl] phosphate (2MP) and 2-hydroxyethyl methacrylate (HEMA) with a mass ratio of 1/1, and 0-40% water contents, respectively. The adhesives were applied either onto the prepared dentine surface or unreactive substrates (such as glass slides), agitated for 15s, then light-cured for 40s. The DCs of the adhesives were determined using micro-Raman spectral and mapping analysis. The DCs of the adhesives cured on the dentine substrate were found to be significantly higher than those on the unreactive glass substrate. Moreover, the DCs of the adhesives displayed a decreasing trend as the distance from the dentine surface became greater. The chemical interaction of the acidic 2MP/HEMA adhesives with the mineral apatite in dentine was proposed to play a significant role for the observations. The chemical interaction could be validated by the spectral comparison in the phosphate regions of 1100 cm(-1) and 960 cm(-1) in the Raman spectra. The results also revealed a notable influence of water content on the DC of adhesives. The DCs of the adhesive at 10% water content exhibited the highest DC level for both substrates. Interaction with dentine dramatically improved the degree of conversion of self-etching adhesives. Our ability to chemically characterise the a/d interface including in situ detection of the DC distribution is very important in understanding self-etching adhesive bonding under in vivo conditions. Copyright © 2011 Elsevier Ltd. All rights reserved.

Cariotester, a new device for assessment of dentin lesion remineralization in vitro.

PubMed

Utaka, Sachiko; Nakashima, Syozi; Sadr, Alireza; Ikeda, Masaomi; Nikaido, Toru; Shimizu, Akihiko; Tagami, Junji

2013-01-01

This study aimed to evaluate the potential of a new device (Cariotester) for monitoring of incipient carious lesion remineralization in root dentin by topical fluoride in vitro. Demineralized bovine dentin specimens were treated by fluoride solutions (APF or neutral NaF) and remineralized for 4 weeks. Cariotester was used to measure penetration depth (CTR depth) of the indenter into the de- and remineralized specimen surface. The specimens were assessed by transverse microradiography (TMR) to determine lesion parameters (depth: LD, mineral loss: ΔZ). Pearson's correlation analysis showed an overall significant relationship between CTR depth and both TMR parameters. CTR depth appeared to distinguish the positive effect that topical fluoride application had on the remineralization of the outer zone of dentin lesions. Cariotester had the potential to serve as a quantitative tool for monitoring of incipient carious lesion remineralization in root dentin.

Influence of dentin pretreatment on bond strength of universal adhesives.

PubMed

Poggio, Claudio; Beltrami, Riccardo; Colombo, Marco; Chiesa, Marco; Scribante, Andrea

2017-01-01

Objective: The purpose of the present study was to compare bond strength of different universal adhesives under three different testing conditions: when no pretreatment was applied, after 37% phosphoric acid etching and after glycine application. Materials and methods: One hundred and fifty bovine permanent mandibular incisors were used as a substitute for human teeth. Five different universal adhesives were tested: Futurabond M+, Scotchbond Universal, Clearfil Universal Bond, G-Premio BOND, Peak Universal Bond. The adhesive systems were applied following each manufacturer's instructions. The teeth were randomly assigned to three different dentin surface pretreatments: no pretreatment agent (control), 37% phosphoric acid etching, glycine pretreatment. The specimens were placed in a universal testing machine in order to measure and compare bond strength values. Results: The Kruskal-Wallis analysis of variance and the Mann-Whitney test were applied to assess significant differences among the groups. Dentin pretreatments provided different bond strength values for the adhesives tested, while similar values were registered in groups without dentin pretreatment. Conclusions: In the present report, dentin surface pretreatment did not provide significant differences in shear bond strength values of almost all groups. Acid pretreatment lowered bond strength values of Futurabond and Peak Universal Adhesives, whereas glycine pretreatment increased bond strength values of G Praemio Bond adhesive system.

Influence of dentin pretreatment on bond strength of universal adhesives

PubMed Central

Poggio, Claudio; Beltrami, Riccardo; Colombo, Marco; Chiesa, Marco; Scribante, Andrea

2017-01-01

Abstract Objective: The purpose of the present study was to compare bond strength of different universal adhesives under three different testing conditions: when no pretreatment was applied, after 37% phosphoric acid etching and after glycine application. Materials and methods: One hundred and fifty bovine permanent mandibular incisors were used as a substitute for human teeth. Five different universal adhesives were tested: Futurabond M+, Scotchbond Universal, Clearfil Universal Bond, G-Premio BOND, Peak Universal Bond. The adhesive systems were applied following each manufacturer’s instructions. The teeth were randomly assigned to three different dentin surface pretreatments: no pretreatment agent (control), 37% phosphoric acid etching, glycine pretreatment. The specimens were placed in a universal testing machine in order to measure and compare bond strength values. Results: The Kruskal–Wallis analysis of variance and the Mann–Whitney test were applied to assess significant differences among the groups. Dentin pretreatments provided different bond strength values for the adhesives tested, while similar values were registered in groups without dentin pretreatment. Conclusions: In the present report, dentin surface pretreatment did not provide significant differences in shear bond strength values of almost all groups. Acid pretreatment lowered bond strength values of Futurabond and Peak Universal Adhesives, whereas glycine pretreatment increased bond strength values of G Praemio Bond adhesive system. PMID:28642929

Shear Bond Strengths and Morphological Evaluation of Filled and Unfilled Adhesive Interfaces to Enamel and Dentine

PubMed Central

Mortazavi, Vajihesadat; Fathi, Mohammadhosein; Ataei, Ebrahim; Khodaeian, Niloufar; Askari, Navid

2012-01-01

In this laboratory study shear bond strengths of three filled and one unfilled adhesive systems to enamel and dentine were compared. Forty-eight extracted intact noncarious human mandibular molars were randomly assigned to two groups of 24 one for bonding to enamel and the other for bonding to dentine. Buccal and lingual surfaces of each tooth were randomly assigned for application of each one of filled (Prime & Bond NT (PBNT), Optibond Solo Plus (OBSP), and Clearfil SE Bond (CSEB)) and unfilled (Single Bond (SB)) adhesive systems (n = 12). A universal resin composite was placed into the translucent plastic cylinders (3 mm in diameter and 2 mm in length) and seated against the enamel and dentine surfaces and polymerized for 40 seconds. Shear bond strength was determined using a universal testing machine, and the results were statistically analyzed using two-way ANOVA, one-way ANOVA, t-test, and Tukey HSD post hoc test with a 5% level of significance.There were no statistically significant differences in bond strength between the adhesive systems in enamel, but CSEB and SB exhibited significantly higher and lower bond strength to dentine, respectively, than the other tested adhesive systems while there were no statistically significant differences between PBNT and OBSP. PMID:23209471

In Vitro Study of Dentin Hypersensitivity Treated by 980-nm Diode Laser.

PubMed

Liu, Ying; Gao, Jie; Gao, Yan; Xu, Shuaimei; Zhan, Xueling; Wu, Buling

2013-01-01

To investigate the ultrastructural changes of dentin irradiated with 980-nm diode laser under different parameters and to observe the morphological alterations of odontoblasts and pulp tissue to determine the safety parameters of 980-nm diode laser in the treatment of dentin hypersensitivity (DH). Twenty extracted human third molars were selected to prepare dentin discs. Each dentin disc was divided into four areas and was irradiated by 980-nm diode laser under different parameters: Group A: control group, 0 J/cm(2); Group B: 2 W/CW (continuous mode), 166 J/cm(2); Group C: 3W/CW, 250 J/cm(2); and Group D: 4W/CW, 333 J/cm(2). Ten additional extracted human third molars were selected to prepare dentin discs. Each dentin disc was divided into two areas and was irradiated by 980-nm diode laser: Group E: control group, 0 J/cm(2); and Group F: 2.0 W/CW, 166 J/cm(2). The morphological alterations of the dentin surfaces and odontoblasts were examined with scanning electron microscopy (SEM), and the morphological alterations of the dental pulp tissue irradiated by laser were observed with an upright microscope. The study demonstrated that dentinal tubules can be entirely blocked after irradiation by 980-nm diode laser, regardless of the parameter setting. Diode laser with settings of 2.0 W and 980-nm sealed exposed dentin tubules effectively, and no significant morphological alterations of the pulp and odontoblasts were observed after irradiation. Irradiation with 980-nm diode laser could be effective for routine clinical treatment of DH, and 2.0W/CW (166 J/cm(2)) was a suitable energy parameter due to its rapid sealing of the exposed dentin tubules and its safety to the odontoblasts and pulp tissue.

In Vitro Study of Dentin Hypersensitivity Treated by 980-nm Diode Laser

PubMed Central

Liu, Ying; Gao, Jie; Gao, Yan; XU, Shuaimei; Zhan, Xueling; Wu, Buling

2013-01-01

Introduction: To investigate the ultrastructural changes of dentin irradiated with 980-nm diode laser under different parameters and to observe the morphological alterations of odontoblasts and pulp tissue to determine the safety parameters of 980-nm diode laser in the treatment of dentin hypersensitivity (DH). Methods: Twenty extracted human third molars were selected to prepare dentin discs. Each dentin disc was divided into four areas and was irradiated by 980-nm diode laser under different parameters: Group A: control group, 0 J/cm2; Group B: 2 W/CW (continuous mode), 166 J/cm2; Group C: 3W/CW, 250 J/cm2; and Group D: 4W/CW, 333 J/cm2. Ten additional extracted human third molars were selected to prepare dentin discs. Each dentin disc was divided into two areas and was irradiated by 980-nm diode laser: Group E: control group, 0 J/cm2; and Group F: 2.0 W/CW, 166 J/cm2. The morphological alterations of the dentin surfaces and odontoblasts were examined with scanning electron microscopy (SEM), and the morphological alterations of the dental pulp tissue irradiated by laser were observed with an upright microscope. Results: The study demonstrated that dentinal tubules can be entirely blocked after irradiation by 980-nm diode laser, regardless of the parameter setting. Diode laser with settings of 2.0 W and 980-nm sealed exposed dentin tubules effectively, and no significant morphological alterations of the pulp and odontoblasts were observed after irradiation. Conclusions: Irradiation with 980-nm diode laser could be effective for routine clinical treatment of DH, and 2.0W/CW (166 J/cm2) was a suitable energy parameter due to its rapid sealing of the exposed dentin tubules and its safety to the odontoblasts and pulp tissue. PMID:25606318

Release of ICTP and CTX telopeptides from demineralized dentin matrices: Effect of time, mass and surface area.

PubMed

Turco, Gianluca; Cadenaro, Milena; Maravić, Tatjana; Frassetto, Andrea; Marsich, Eleonora; Mazzoni, Annalisa; Di Lenarda, Roberto; Tay, Franklin R; Pashley, David H; Breschi, Lorenzo

2018-03-01

The present study evaluated the influence of time, mass and surface area of demineralized dentin collagen matrices on telopeptides release. The hypotheses tested were that the rates of ICTP and CTX release by matrix bound endogenous proteases are 1) not time-dependent, 2) unrelated to specimen mass, 3) unrelated to specimen surface area. Non-carious human molars (N=24) were collected and randomly assigned to three groups. Dentin slabs with three different thicknesses: 0.37mm, 0.75mm, and 1.50mm were completely demineralized and stored in artificial saliva for one week. Collagen degradation was evaluated by sampling storage media for ICTP and CTX telopeptidases. Activity of MMPs in the aging medium was evaluated using fluorometric activity assay kit. A statistically significant (p<0.05) decrease in the release of both ICTP and CTX fragments over time was observed irrespective of the specimen thickness. When data were normalized by the specimen mass, no significant differences were observed. Releases of ICTP and CTX were significantly related to the aging time as a function of surface area for the first 12h. Total MMP activity, mainly related to MMP-2 and -9, decreased with time (p<0.05). Because the release of collagen fragments was influenced by specimen storage time and surface area, it is likely that cleaved collagen fragments closer to the specimen surface diffuse into the incubation medium; those further away from the exposed surface are still entrapped within the demineralized dentin matrix. Bound MMPs can only degrade the substrate within the limited zone of their molecular mobility. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Adhesive sealing of dentin surfaces in vitro: A review

PubMed Central

Abu-Nawareg, Manar M; Zidan, Ahmed Z; Zhou, Jianfeng; Agee, Kelli; Chiba, Ayaka; Tagami, Jungi; Pashley, David H

2016-01-01

Purpose The purpose of this review is to describe the evolution of the use of dental adhesives to form a tight seal of freshly prepared dentin to protect the pulp from bacterial products, during the time between crown preparation and final cementum of full crowns. The evolution of these “immediate dentin sealants” follows the evolution of dental adhesives, in general. That is, they began with multiple-step, etch-and-rinse adhesives, and then switched to the use of simplified adhesives. Methods Literature was reviewed for evidence that bacteria or bacterial products diffusing across dentin can irritate pulpal tissues before and after smear layer removal. Smear layers can be solubilized by plaque organisms within 7–10 days if they are directly exposed to oral fluids. It is likely that smear layers covered by temporary restorations may last more than one month. As long as smear layers remain in place, they can partially seal dentin. Thus, many in vitro studies evaluating the sealing ability of adhesive resins use smear layer-covered dentin as a reference condition. Surprisingly, many adhesives do not seal dentin as well as do smear layers. Results Both in vitro and in vivo studies show that resin-covered dentin allows dentinal fluid to cross polymerized resins. The use of simplified single bottle adhesives to seal dentin was a step backwards. Currently, most authorities use either 3-step adhesives such as Scotchbond Multi-Purposea or OptiBond FLb or two-step self-etching primer adhesives, such as Clearfil SEc, Unifil Bondd or AdheSEe, respectfully. PMID:26846037

Comparative Evaluation of the Etching Pattern of Er,Cr:YSGG & Acid Etching on Extracted Human Teeth-An ESEM Analysis

PubMed Central

Mazumdar, Dibyendu; Ranjan, Shashi; Krishna, Naveen Kumar; Kole, Ravindra; Singh, Priyankar; Lakiang, Deirimika; Jayam, Chiranjeevi

2016-01-01

Introduction Etching of enamel and dentin surfaces increases the surface area of the substrate for better bonding of the tooth colored restorative materials. Acid etching is the most commonly used method. Recently, hard tissue lasers have been used for this purpose. Aim The aim of the present study was to evaluate and compare the etching pattern of Er,Cr:YSGG and conventional etching on extracted human enamel and dentin specimens. Materials and Methods Total 40 extracted non-diseased teeth were selected, 20 anterior and 20 posterior teeth each for enamel and dentin specimens respectively. The sectioned samples were polished by 400 grit Silicon Carbide (SiC) paper to a thickness of 1.0 ± 0.5 mm. The enamel and dentin specimens were grouped as: GrE1 & GrD1 as control specimens, GrE2 & GrD2 were acid etched and GrE3 & GrD3 were lased. Acid etching was done using Conditioner 36 (37 % phosphoric acid) according to manufacturer instructions. Laser etching was done using Er,Cr:YSGG (Erbium, Chromium : Ytrium Scandium Gallium Garnet) at power settings of 3W, air 70% and water 20%. After surface treatment with assigned agents the specimens were analyzed under ESEM (Environmental Scanning Electron Microscope) at X1000 and X5000 magnification. Results Chi Square and Student “t” statistical analysis was used to compare smear layer removal and etching patterns between GrE2-GrE3. GrD2 and GrD3 were compared for smear layer removal and diameter of dentinal tubule opening using the same statistical analysis. Chi-square test for removal of smear layer in any of the treated surfaces i.e., GrE2-E3 and GrD2-D3 did not differ significantly (p>0.05). While GrE2 showed predominantly type I etching pattern (Chi-square=2.78, 0.05

0.10) and GrE3 showed type III etching (Chi-square=4.50, p<0.05). The tubule diameters were measured using GSA (Gesellschaft fur Softwareentwicklung und Analytik, Germany) image analyzer and the ‘t’ value of student ‘t’ test was 18.10 which was a highly significant result (p<.001). GrD2 had a mean dentinal tubule diameter of 2.78μm and GrD3 of 1.09μm. Conclusion The present study revealed type I etching pattern after acid etching, while type III etching pattern in enamel after laser etching. The lased dentin showed preferential removal of intertubular dentin while acid etching had more effect on the peritubular dentin. No significant differences was observed in removal of smear layer between the acid etched and lased groups. Although diameter of the exposed dentinal tubules was lesser after lased treatment in comparison to acid etching, further long term in vivo studies are needed with different parameters to establish the usage of Er,Cr:YSGG as a sole etching agent. PMID:27437337

Mechanical loading influences the viscoelastic performance of the resin-carious dentin complex.

PubMed

Toledano, Manuel; Osorio, Raquel; López-López, Modesto T; Aguilera, Fátima S; García-Godoy, Franklin; Toledano-Osorio, Manuel; Osorio, Estrella

2017-04-04

The aim of this study was to evaluate the changes in the mechanical behavior and bonding capability of Zn-doped resin-infiltrated caries-affected dentin interfaces. Dentin surfaces were treated with 37% phosphoric acid (PA) followed by application of a dentin adhesive, single bond (SB) (PA+SB) or by 0.5 M ethylenediaminetetraacetic acid (EDTA) followed by SB (EDTA+SB). ZnO microparticles of 10 wt. % or 2 wt. % ZnCl 2 was added into SB, resulting in the following groups: PA+SB, PA+SB-ZnO, PA+SB-ZnCl 2 , EDTA+SB, EDTA+SB-ZnO, EDTA+SB-ZnCl 2 . Bonded interfaces were stored for 24 h, and tested or submitted to mechanical loading. Microtensile bond strength was assessed. Debonded surfaces were evaluated by scanning electron microscopy and elemental analysis. The hybrid layer, bottom of the hybrid layer, and peritubular and intertubular dentin were evaluated using a nanoindenter. The load/displacement responses were used for the nanodynamic mechanical analysis III to estimate complex modulus, tan delta, loss modulus, and storage modulus. The modulus mapping was obtained by imposing a quasistatic force setpoint to which a sinusoidal force was superimposed. Atomic force microscopy imaging was performed. Load cycling decreased the tan delta at the PA+SB-ZnCl 2 and EDTA+SB-ZnO interfaces. Tan delta was also diminished at peritubular dentin when PA+SB-ZnO was used, hindering the dissipation of energy throughout these structures. Tan delta increased at the interface after using EDTA+SB-ZnCl 2 , lowering the energy for recoil or failure. After load cycling, loss moduli at the interface decreased when using ZnCl 2 as doping agent, increasing the risk of fracture; but when using ZnO, loss moduli was dissimilarly affected if dentin was EDTA-treated. The border between intertubular and peritubular dentin attained the highest discrepancy in values of viscoelastic properties, meaning a risk for cracking and breakdown of the resin-dentin interface. PA used on dentin provoked differences in complex and storage modulus values at the intertubular and peritubular structures, and these differences were higher than when EDTA was employed. In these cases, the long-term performance of the restorative interface will be impaired.

Direct Tensile Strength and Characteristics of Dentin Restored with All-Ceramic, Resin-Composite, and Cast Metal Prostheses Cemented with Resin Adhesives

PubMed Central

Piemjai, Morakot; Nakabayashi, Nobuo

2015-01-01

A dentin-cement-prosthesis complex restored with either all-porcelain, cured resin-composite, or cast base metal alloy and cemented with either of the different resin cements was trimmed into a mini-dumbbell shape for tensile testing. The fractured surfaces and characterization of the dentin-cement interface of bonded specimens were investigated using a Scanning Electron Microscope. A significantly higher tensile strength of all-porcelain (12.5 ± 2.2 MPa) than that of cast metal (9.2 ± 3.5 MPa) restorations was revealed with cohesive failure in the cement and failure at the prosthesis-cement interface in Super-Bond C&B group. No significant difference in tensile strength was found among the types of restorations using the other three cements with adhesive failure on the dentin side and cohesive failure in the cured resin. SEM micrographs demonstrated the consistent hybridized dentin in Super-Bond C&B specimens that could resist degradation when immersed in hydrochloric acid followed by NaOCl solutions whereas a detached and degraded interfacial layer was found for the other cements. The results suggest that when complete hybridization of resin into dentin occurs tensile strength at the dentin-cement is higher than at the cement-prosthesis interfaces. The impermeable hybridized dentin can protect the underlying dentin and pulp from acid demineralization, even if detachment of the prosthesis has occurred. PMID:26539520

Thermal effects associated with the Nd/YAG dental laser.

PubMed

von Fraunhofer, J A; Allen, D J

1993-01-01

The heat produced at the dentinal pulpal wall opposite the irradiation site was measured during etching of dental enamel with an Nd:YAG laser in preparation for direct bonding of orthodontic appliances. Forty extracted human teeth were randomly divided into four groups of 10 teeth. Within each group, the buccal surfaces of 5 teeth and the lingual surfaces of the other 5 teeth were laser treated for 12 sec. Irradiation was performed with a commercial Nd:YAG laser at the power settings of 80mJ, 1W, 2W and 3W. Prior to irradiation, an occlusal access preparation was made into the pulp in order to facilitate the placement of a thermocouple for measurement of temperature changes at the dentinal pulpal wall opposite the irradiation site. The thermocouple was held against the dentinal pulpal wall and the resulting temperature changes were recorded. Heating effects at the dentinal pulpal wall on both buccal and lingual surfaces showed an increase in heat as a function of the increase in power output from the laser unit (p < 0.01). The temperatures measured at power levels 1-3W appeared to be of sufficient magnitude to cause at least localized pulpal inflammation and possible irreversible damage to the pulp tissue immediately opposite the site of laser irradiation.

Improving the efficiency of an Er:YAG laser on enamel and dentin.

PubMed

Rizcalla, Nicolas; Bader, Carl; Bortolotto, Tissiana; Krejci, Ivo

2012-02-01

To evaluate the influence of air pressure, water flow rate, and pulse frequency on the removal speed of enamel and dentin as well as on their surface morphology. Twenty-four bovine incisors were horizontally cut in slices. Each sample was mounted on an experimental assembly, allowing precise orientation. Eighteen cavities were prepared, nine in enamel and nine in dentin. Specific parameters for frequency, water flow rate, and air pressure were applied for each experimental group. Three groups were randomly formed according to the air pressure settings. Cavity depth was measured using a digital micrometer gauge, and surface morphology was checked by means of scanning electron microscopy. Data was analyzed with ANOVA and Duncan post hoc test. Irradiation at 25 Hz for enamel and 30 Hz for dentin provided the best ablation rates within this study, but efficiency decreased if the frequency was raised further. Greater tissue ablation was found with water flow rate set to low and dropped with higher values. Air pressure was found to have an interaction with the other settings, since ablation rates varied with different air pressure values. Fine-tuning of all parameters to get a good ablation rate with minimum surface damage seems to be key in achieving optimal efficiency for cavity preparation with an Er:YAG laser.

Shear bond strength of bulk-fill and nano-restorative materials to dentin.

PubMed

Colak, Hakan; Ercan, Ertugrul; Hamidi, Mehmet Mustafa

2016-01-01

Bulk-fill composite materials are being developed for preparation depths of up to 4 mm in an effort to simplify and improve the placement of direct composite posterior restorations. The aim of our study was to compare shear-bond strength of bulk-fill and conventional posterior composite resins. In this study, 60 caries free extracted human molars were used and sectioned parallel to occlusal surface to expose midcoronal dentin. The specimens were randomly divided into four groups. Total-etch dentine bonding system (Adper Scotchbond 1XT, 3M ESPE) was applied to dentin surface in all the groups to reduce variability in results. Then, dentine surfaces covered by following materials. Group I: SonicFill Bulk-Fill, Group II: Tetric EvoCeram (TBF), Group III: Herculite XRV Ultra, and Group IV: TBF Bulk-Fill, 2 mm × 3 mm cylindrical restorations were prepared by using application apparatus. Shear bond testing was measured by using a universal testing machine. Kruskal-Wallis and Mann-Whitney U-tests were performed to evaluate the data. The highest value was observed in Group III (14.42 ± 4.34) and the lowest value was observed in Group IV (11.16 ± 2.76) and there is a statistically significant difference between these groups (P = 0.046). However, there is no statistically significant difference between the values of other groups. In this study, Group III was showed higher strength values. There is a need for future studies about long-term bond strength and clinical success of these adhesive and bulk-fill systems.

Enzyme-catalyzed hydrolysis of dentin adhesives containing a new urethane-based trimethacrylate monomer

PubMed Central

Park, Jong-Gu; Ye, Qiang; Topp, Elizabeth M.; Spencer, Paulette

2009-01-01

A new trimethacrylate monomer with urethane-linked groups, 1,1,1-tri-[4-(methacryloxyethylamino-carbonyloxy)-phenyl]ethane (MPE), was synthesized, characterized, and used as a co-monomer in dentin adhesives. Dentin adhesives containing 2-hydroxyethyl methacrylate (HEMA, 45% w/w) and 2,2-bis[4(2-hydroxy-3-methacryloyloxy-propyloxy)-phenyl] propane (BisGMA, 30% w/w) in addition to MPE (25% w/w) were formulated with H2O at 0 (MPE0), 8 (MPE8) and 16 wt % water (MPE16) to simulate the wet demineralized dentin matrix and compared with controls [HEMA/BisGMA, 45/55 w/w, at 0 (C0), 8 (C8) and 16 wt% water (C16)]. The new adhesive showed a degree of double bond conversion and mechanical properties comparable with control, with good penetration into the dentin surface and a uniform adhesive/dentin interface. On exposure to porcine liver esterase, the net cumulative methacrylic acid (MAA) release from the new adhesives was dramatically (P < 0.05) decreased relative to the control, suggesting that the new monomer improves esterase resistance. PMID:19582843

Construction and in vitro test of a new electrode for dentin resistance measurement.

PubMed

Stein, Steffen; Gente, Michael

2013-10-01

It is necessary to reduce the tooth substance before treating a tooth with a dental crown. The preparation often requires reduction of the dentin. This results in a dentin wound and a thinner substance over the pulp, increases the risk of inflammation, and could result in necrosis of the pulp. To give the dentist information about the amount of dentin over the pulp during preparation, the Prepometer was developed. The function of this device is based on the measurement of the electric resistance of the tooth substance. The measuring behavior of the first-generation Prepometer is characterized by smaller values of electric resistance before reaching full contact of the measuring head to the dentin surface and the actual value RT. This measuring behavior can mislead inexperienced therapists with inaccurate values that suggest thinner dentin than the reality. In this study, a new electrode based on the technology of active guard drive was constructed to overcome this issue. The results show that improvement in the measuring behavior of the new electrode could be achieved, eliminating the earlier disadvantage of the Prepometer.

Microtensile bond strength of indirect resin composite to resin-coated dentin: interaction between diamond bur roughness and coating material.

PubMed

Kameyama, Atsushi; Oishi, Takumi; Sugawara, Toyotarou; Hirai, Yoshito

2009-02-01

This aim of this study was to determine the effect of type of bur and resin-coating material on microtensile bond strength (microTBS) of indirect composite to dentin. Dentin surfaces were first ground with two types of diamond bur and resin-coated using UniFil Bond (UB) or Adper Single Bond (SB), and then bonded to a resin composite disc for indirect restoration with adhesive resin cement. After storage for 24 hr in distilled water at 37 degrees C, microTBS was measured (crosshead speed 1 mm/min). When UB was applied to dentin prepared using the regular-grit diamond bur, microTBS was significantly lower than that in dentin prepared using the superfine-grit bur. In contrast, no significant difference was found between regular-grit and superfine-grit bur with SB. However, more than half of the superfine-grit specimens failed before microTBS testing. These results indicate that selection of bur type is important in improving the bond strength of adhesive resin cement between indirect resin composite and resin-coated dentin.

[Effect of nano-silica coating on bonding strength of zirconia ceramics to dentin].

PubMed

Zhang, Xian-Fang; Zheng, Hu; Han, Dong-Wei

2009-04-01

To investigate the effect of silica coating by sol-gel process on bonding strength of zirconia ceramics to dentin. Blocks of sintered zirconia ceramics were cut and randomly divided into 4 groups,16 slices in each group. Each group was subject to one of the 4 kinds of surface treatment (control group, sandblasting, sandblasting +silicone, sandblasting + silica coating + silicone) and then bonded to dentin with resin cement. After preservation in 37 degrees centigrade distilled water for 24 hours, the shear bonding strength of these specimens was tested and the data was analyzed with SAS6.12 software package for analysis of variance. The surface modality of the ceramics was observed under scanning electron microscopy (SEM). The group of sandblasting+ silica coating + silicone attained the highest shear bonding strength, which was significantly different from the other groups(P=0.000);There was no significant difference between the sandblasting and sandblasting + silicone group (P=0.827), which was significantly different from the control group(P=0.001). Silica coating by sol-gel process, coupled with silicone, can significantly increase the bonding strength of zirconia ceramics to dentin.

Effects of various final irrigants on the shear bond strength of resin-based sealer to dentin

PubMed Central

Kandaswamy, Deivanayagam; Venkateshbabu, Nagendrababu; Arathi, Ganesh; Roohi, Riaz; Anand, Suresh

2011-01-01

Aim: This study has been designed to evaluate the effect of strong (MTAD) or soft (1- hydroxyethylidene – 1, 1-bisphosphonate (HEBP) final irrigating solution on the shear bond strength of AH plus sealer to coronal dentin. 17% EDTA was used as the reference. Materials and Methods: Forty freshly extracted human maxillary first premolars were prepared using different irrigation protocols (n=10). All the test groups had 1.3% NaOCl as initial rinse and followed by specific final rinse for each group: G1 – distilled water(control), G2 – 17% EDTA, G3- 18% HEBP and G4 – MTAD. Sections of polyethylene tubes that are 3mm long were filled with freshly mixed sealer and placed on the dentin surfaces. The bonding between the sealer and dentine surface was evaluated using shear bond testing. The values were statistically evaluated using one-way ANOVA followed by Tukey's test. Result: Significant difference was found among the irrigating regimes. EDTA showed highest bond strength followed by HEBP and MTAD PMID:21691504

Repair dentinogenesis following transplantation into normal and germ-free animals.

PubMed

Inoue, T; Shimono, M

1992-01-01

The purpose of this study was to investigate the dentinogenesis of dental pulp tissue following transplantation and during regeneration in normal and germ free animals, as well as in vitro experiments. (1) Partial and complete exposure of dental pulp in germ free rats by removing the enamel and dentin of molars. (2) The central portion of rat incisor which consisted of pulp and pulp chamber were autografted into various tissues. (3) Explants of rat pulp tissue were cultured on dentin matrix. (4) Resin bonding agent, 4-META/MMA-TBB-O (Superbond), was placed directly on surgically-exposed dental pulp. (1) Dentin bridge formation was recognized at 5 days after operation in germ free rat. (2) The cut surface of the transplant exhibited dentin bridge at 7 days after implantation, and the thickness of the newly formed dentin increased gradually thereafter up to 30 days. (3) Cultured pulp cells had high alkaline phosphatase activity and bone- or dentin-like hard tissue was synthesized on the dentin matrix in vitro. (4) Dentin bridge formation was evident on the surgically-exposed dental pulp even after application of Superbond. From these results, it is suggested that pulp tissue has a high activity of dentinogenesis both in vivo and in vitro and 3 days is enough for pulp cells to express the odontoblast phenotype when inflammatory factors are not present.

Microorganism penetration in dentinal tubules of instrumented and retreated root canal walls. In vitro SEM study.

PubMed

Al-Nazhan, Saad; Al-Sulaiman, Alaa; Al-Rasheed, Fellwa; Alnajjar, Fatimah; Al-Abdulwahab, Bander; Al-Badah, Abdulhakeem

2014-11-01

This in vitro study aimed to investigate the ability of Candida albicans (C. albicans) and Enterococcus faecalis (E. faecalis) to penetrate dentinal tubules of instrumented and retreated root canal surface of split human teeth. Sixty intact extracted human single-rooted teeth were divided into 4 groups, negative control, positive control without canal instrumentation, instrumented, and retreated. Root canals in the instrumented group were enlarged with endodontic instruments, while root canals in the retreated group were enlarged, filled, and then removed the canal filling materials. The teeth were split longitudinally after canal preparation in 3 groups except the negative control group. The teeth were inoculated with both microorganisms separately and in combination. Teeth specimens were examined by scanning electron microscopy (SEM), and the depth of penetration into the dentinal tubules was assessed using the SMILE view software (JEOL Ltd). Penetration of C. albicans and E. faecalis into the dentinal tubules was observed in all 3 groups, although penetration was partially restricted by dentin debris of tubules in the instrumented group and remnants of canal filling materials in the retreated group. In all 3 groups, E. faecalis penetrated deeper into the dentinal tubules by way of cell division than C. albicans which built colonies and penetrated by means of hyphae. Microorganisms can easily penetrate dentinal tubules of root canals with different appearance based on the microorganism size and status of dentinal tubules.

Effect of reducing acid etching time on bond strength to noncarious and caries-affected primary and permanent dentin.

PubMed

Scheffel, Débora Lopes Salles; Ricci, Hérica Adad; de Souza Costa, Carlos Alberto; Pashley, David Henry; Hebling, Josimeri

2013-01-01

The purpose was to evaluate the effect of acid etching time on the bond strength of a simplified etch-and-rinse adhesive system to noncarious and caries-affected dentin of primary and permanent teeth. Twenty-four extracted primary and permanent teeth were divided into three groups, according to the acid etching time. Four teeth from each group were exposed to a microbiological caries-inducing protocol. After caries removal, noncarious and caries-affected dentin surfaces were etched with 37 percent phosphoric acid for five, 10, or 15 seconds prior to the application of Prime & Bond NT adhesive. Crowns were restored with resin composite and prepared for microtensile testing. Data were submitted to Kruskal-Wallis and Mann-Whitney tests (α=0.05). Higher bond strengths were obtained for noncarious dentin vs. caries-affected dentin for both primary and permanent teeth. Reducing the acid etching time from 15 to five seconds did not affect the bond strength to caries-affected or noncarious dentin in primary teeth. For permanent teeth, lower bond strength values were observed when the noncarious dentin was etched for five seconds, while no difference was seen between 10 and 15 seconds. For Prime & Bond NT, the etching of dentin for five seconds could be recommended for primary teeth, while 10 seconds would be the minimum time for permanent teeth.

Changes in deciduous and permanent dentinal tubules diameter after several conditioning protocols: In vitro study.

PubMed

de Los Angeles Moyaho-Bernal, María; Contreras-Bulnes, Rosalía; Rodríguez-Vilchis, Laura Emma; Rubio-Rosas, Efraín

2018-05-08

Innovators conditioning protocols are emerged in permanent dentin, however for deciduous dentin the information is limited; the aim of this study was to evaluate in vitro diameter of deciduous and permanent dentinal tubules after several conditioning protocols. Eighty dentin samples were distributed in sixteen groups (n = 5 p/g) and dentin surface was conditioned as follow: G1D/G1P acid etching; G2D/G2P, self-etch adhesive; G3D/G3P, G4D/G4P, Er: YAG laser irradiation at 200 mJ-25.5 J/cm 2 and 300 mJ-38.2 J/cm 2 , at 10 Hz under water spray respectively; G5D/G5P, G6D/G6P, G7D/G7P, and G8D/G8P were irradiated under the same energy densities followed phosphoric acid or self-etch adhesive conditioning. The sample dentin of deciduous and permanent teeth was analyzed with scanning electron microscopy and tubule diameter was evaluated by Image Tools Scandium program. Data were subjected to one-way analysis ANOVA to compare among groups with a level of significance at p ≤ .05. For deciduous dentin, diameters were from 1.52 ± 0.32 µm in G3D to 3.88 ± 0.37 µm in G1D; narrowest and widest diameter, respectively (p < .000). While permanent dentin tubules exhibited diameters from 1.16 ± 0.16/1.19 ± 0.12 µm in G7P/G8P to 2.76 ± 0.28 µm in G6P; narrowest and widest diameter, respectively (p < .000). All dentin conditioning protocols produced more open dentin tubules (diameter size) in deciduous dentin than permanent, specific conditioning protocols are required for each tissue (deciduous or permanent dentin), since same protocol produced stronger effects on primary dentin, which is important for dental clinical success in children and adolescents. © 2018 Wiley Periodicals, Inc.

Effect of propolis gel on the in vitro reduction of dentin permeability

PubMed Central

SALES-PERES, Silvia Helena de Carvalho; de CARVALHO, Flávia Negreiros; MARSICANO, Juliane Avansini; MATTOS, Maria Cecília; PEREIRA, José Carlos; FORIM, Moacir Rossi; da SILVA, Maria Fatima das Graças Fernandes

2011-01-01

Objective The aim of this study was to evaluate the capacity of potassium oxalate, fluoride gel and two kinds of propolis gel to reduce the hydraulic conductance of dentin, in vitro. Material and Methods The methodology used for the measurement of hydraulic conductance of dentin in the present study was based on a model proposed in literature. Thirty-six 1-mm-thick dentin discs, obtained from extracted human third molars were divided into 4 groups (n=9). The groups corresponded to the following experimental materials: GI-10% propolis gel, pH 4.1; GII-30% propolis gel; GIII-3% potassium oxalate gel, pH 4,1; and GIV-1.23% fluoride gel, pH 4.1, applied to the dentin under the following surface conditions: after 37% phosphoric acid and before 6% citric acid application. The occluding capacity of the dentin tubules was evaluated using scanning electron microscopy (SEM) at ×500, ×1,000 and ×2,000 magnifications. Data were analyzed statistically by two-way ANOVA and Tukey's test at 5% significance level. Results Groups I, II, III, IV did not differ significantly from the others in any conditions by reducing in hydraulic conductance. The active agents reduced dentin permeability; however they produced the smallest reduction in hydraulic conductance when compared to the presence of smear layer (P<0.05). The effectiveness in reducing dentin permeability did not differ significantly from 10% or 30% propolis gels. SEM micrographs revealed that dentin tubules were partially occluded after treatment with propolis. Conclusions Under the conditions of this study, the application of 10% and 30% propolis gels did not seem to reduce the hydraulic conductance of dentin in vitro, but it showed capacity of partially obliterating the dentin tubules. Propolis is used in the treatment of different oral problems without causing significant great collateral effects, and can be a good option in the treatment of patients with dentin sensitivity. PMID:21956588

Penetration pattern of rhodamine dyes into enamel and dentin: confocal laser microscopy observation.

PubMed

Kwon, S R; Wertz, P W; Li, Y; Chan, D C N

2012-02-01

Enamel and dentin are susceptible to extrinsic and intrinsic stains. The purposes of this study were to determine the penetration pattern of Rhodamine B and dextran-conjugated Rhodamine B into the enamel and dentin as observed by confocal laser microscopy and to relate it to the penetration pattern of hydrogen peroxide commonly used as an active ingredient in tooth-whitening agents and high-molecular-weight staining molecules. Eighteen recently extracted human maxillary anterior teeth were used. Teeth were cleaned and painted with nail varnish except for the crown area above the cemento-enamel junction (CEJ). The painted teeth were then immersed in Rhodamine B and dextran-conjugated Rhodamine B (70 000 MW) for 4, 7, 10 and 15 days. Teeth were sliced to 3 mm thickness in transverse plane and mounted on a glass slide just prior to observation with confocal laser microscopy. Rhodamine B and dextran-conjugated Rhodamine B readily penetrated into the enamel and dentin when exposed for 4 and 7 days, respectively. Rhodamine B penetrated along the interprismatic spaces of the enamel into the dentin. The penetration was accentuated in sections with existing crack lines in the enamel. Rhodamine B was readily absorbed into the dentinal tubules at the dentino-enamel junction and continued to penetrate through the dentin via the dentinal tubules into the pre-dentin. Within the limitations of this study, it is concluded that Rhodamine B and dextran-conjugated Rhodamine B when applied to the external surface of the tooth readily penetrate into the enamel and dentin via the interprismatic spaces in the enamel and dentinal tubules in the dentin, suggesting that stain molecules and bleaching agents possibly exhibit similar penetration pathways. © 2011 The Authors. ICS © 2011 Society of Cosmetic Scientists and the Société Française de Cosmétologie.

Nanoindentation hardness of intertubular dentin in sound, demineralized and natural caries-affected dentin.

PubMed

Joves, Gerardo José; Inoue, Go; Sadr, Alireza; Nikaido, Toru; Tagami, Junji

2014-04-01

The purpose of this study was to investigate the mechanical properties of intertubular dentin in sound, natural caries-affected (NCAD) and artificial caries-affected dentin (ACAD) using nanoindentation. Non-caries molars and caries molars with International Caries Detection and Assessment System (ICDAS II) score 5 at the occlusal site were used and caries was excavated using a spoon excavator, a round bur at low speed without water and a dye solution as guidance to detect the infected tissue. Specimens with remaining dentin thickness (RDT) >2mm were selected. ACAD teeth were created from sound teeth over 7 days in a demineralizing solution. Specimens were embedded into plastic rings with acrylic resin and then sagittal mesial-distal sectioned from crown to the long axis of the root under cooling water using a low-speed diamond blade. The surface of interest was fine polished sequentially. Hardness measurement was performed within an axial depth of 1000μm with at least of 320 indentations on each sample. Mann-Whitney U Test was used to compare the hardness as the variable among different dentin types (SOUND, NCAD and ACAD) at each dentin depth level. There was no significant difference in nanohardness between NCAD and ACAD up to a depth of 130μm (p>0.05). NCAD consistently showed lower hardness. ACAD showed no significant difference in hardness with SOUND dentin beyond 190μm (p<0.05). The lesion front in ACAD was considered to be located around the depth of 180μm. Natural and artificial caries-affected dentin tissues were superficially comparable in intertubular nanohardness. There is a certain layer within the natural caries-affected dentin with higher hardness; however the long-term effects of caries beneath the lesion extend deeply through intertubular dentin. Sound dentin at deep areas (close to the pulp chamber) is considered to be soft. Copyright © 2014 Elsevier Ltd. All rights reserved.

Influence of ultrasound and diamond burs treatments on microtensile bond strength.

PubMed

Conde, Alexandre; Mainieri, Vivian; Mota, Eduardo Goncalves; Oshima, Hugo Mitsuo

2012-01-01

To compare surface treatments with CVDentUS ultrasound tips (UT) and KGSorensen diamond burs (DB) on etched (e) and non-etched (n/e) dentin. The microtensile bond strength (μTBS) was measured and fractography was assessed by scanning electron microscope (SEM). Sixteen molars were divided into four groups of four teeth each according to treatment (DB-n/e; DB-e; UT-n/e; UT-e). The teeth were restored, sectioned into samples for μTBS (n=40) and tested on a EMIC DL-2000 universal machine (0.5 mm/min) and analyzed by SEM for fracture classification. For analysis of the data on μTBS, the two-way ANOVA, using treatment and acid etching as fixed factor, and the Tukey test were used (α=0.05). To failures classification in cohesive in dentin (CD); cohesive in composite resin (CC); cohesive interfacial on base or top of hybrid layer (CBT); cohesive in adhesive (CA); mixed (M); interfacial on smear layer (S) the Fisher's exact test (α=0.05) was performed. The mean values of μTBS (in MPa) in the different groups were as follows: UT-e: 45.31 ± 8.16; DB-e: 34.04 ± 9.29; UT-n/e: 15.17 ± 3.71; and DB-n/e: 9.86 ± 3.80. On analysis of the SEM micrographs, the DB-n/e group showed total obstruction of dentinal tubules; the UT-n/e group showed partial desobstruction of dentinal tubules and irregular surface; the DB-e group showed complete desobstruction of dentinal tubules; and the UT-e group showed complete desobstruction of dentinal tubules and irregular surface. The combination of ultrasound treatment and acid etching provides high values of μTBS. An association exists between CA/CC failures and the UT method, CBT failure and the DB method, CBT/CC failures and etching, S failure and non-etching.

Atraumatic Restorative Treatment: Restorative Component.

PubMed

Leal, Soraya; Bonifacio, Clarissa; Raggio, Daniela; Frencken, Jo

2018-01-01

Atraumatic restorative treatment (ART) is a method of managing dental caries based on 2 pillars: sealants for preventing carious lesions in pits and fissures, and restorations for cavitated dentine carious lesions. ART uses only hand instruments for opening/enlarging the cavity and for removing carious tissue. The amount of carious tissue that should be removed depends mainly on the cavity depth. In cavities of shallow and medium depth, carious tissue is removed up to firm dentine. In deep/very deep cavities, in which there is no sign of pulp exposure, pulp inflammation and/or history of spontaneous pain, some soft dentine can be left in the pulpal floor/wall with the aim of avoiding pulp exposure. The ART restorative method is indicated for treating single-surface cavities in primary and permanent teeth, and in multiple-surface cavities in primary teeth. Insufficient information is available to conclude on its use for treating multiple-surface cavities in permanent teeth. © 2018 S. Karger AG, Basel.

Ethanol wet-bonding technique sensitivity assessed by AFM.

PubMed

Osorio, E; Toledano, M; Aguilera, F S; Tay, F R; Osorio, R

2010-11-01

In ethanol wet bonding, water is replaced by ethanol to maintain dehydrated collagen matrices in an extended state to facilitate resin infiltration. Since short ethanol dehydration protocols may be ineffective, this study tested the null hypothesis that there are no differences in ethanol dehydration protocols for maintaining the surface roughness, fibril diameter, and interfibrillar spaces of acid-etched dentin. Polished human dentin surfaces were etched with phosphoric acid and water-rinsed. Tested protocols were: (1) water-rinse (control); (2) 100% ethanol-rinse (1-min); (3) 100% ethanol-rinse (5-min); and (4) progressive ethanol replacement (50-100%). Surface roughness, fibril diameter, and interfibrillar spaces were determined with atomic force microscopy and analyzed by one-way analysis of variance and the Student-Newman-Keuls test (α = 0.05). Dentin roughness and fibril diameter significantly decreased when 100% ethanol (1-5 min) was used for rinsing (p < 0.001). Absolute ethanol produced collapse and shrinkage of collagen fibrils. Ascending ethanol concentrations did not collapse the matrix and shrank the fibrils less than absolute ethanol-rinses.

[Effect of three aging challenges on the bonding stability of resin-dentin interface using an etch-and-rinse adhesive].

PubMed

Xu, Shuai; Zhang, Ling; Li, Fang; Zhou, Wei; Chen, Yujiang; Chen, Jihua

2014-06-01

To systematically investigate the aging effect of thermocycling, water storage and bacteria aggression on the stability of resin-dentin bonds. Forty molars were sectioned perpendicularly to the axis of the teeth to expose the middle-coronal dentin surfaces. The dentin surfaces were then treated with Single Bond 2 and made a core build-up. According to random digits table, the bonding specimens were divided into four groups (n = 10) as follows: immediate control group, aging group with thermocycling for 5 000 times, aging group with artificial saliva storage for 6 months and aging group with bacteria aggression for 14 days. The specimens in each group were then subjected to microtensile bond strengths (µTBS) testing and nanoleakage evaluation respectively. After aging treatments, the three aging groups showed significantly lower µTBS than the immediate control group [(44.24 ± 12.75) MPa, P < 0.05]. The immediate control group also showed the lowest value of nanoleakage. The µTBS of aging group with bacteria aggression [(25.53 ± 7.39) MPa] was significantly lower than those of the other aging groups with artificial saliva storage[(29.72 ± 6.51) MPa] and thermocycling [(31.92 ± 11.87) MPa, P < 0.05]. There were no differences in the nanoleakage values among the three aging groups (P > 0.05). All the aging treatments with artificial saliva storage, thermocycling and bacteria aggression could accelerate the degradation of bonding interfaces between an etch-and-rinse adhesive and dentin. Bacteria aggression showed the most impairing effect on the stability of resin-dentin bonds.

Impact of dentifrice abrasivity and remineralization time on erosive tooth wear in vitro.

PubMed

Buedel, Sarah; Lippert, Frank; Zero, Domenick T; Eckert, George J; Hara, Anderson T

2018-02-01

To investigate the in vitro effects of simulated dentifrice slurry abrasivity (L-low, M-medium and H-high) and remineralization time (0, 30, 60 and 120 minutes) on erosive tooth wear. Enamel and root dentin specimens were prepared from bovine incisors (n= 8) and submitted to a cycling protocol including erosion, remineralization at the test times, and brushing with each of the tested slurries, for 5 days. Dental surface loss (SL) was determined by optical profilometry. Data was analyzed using mixed-model ANOVA and Fisher's PLSD tests (alpha= 0.05). SL generally increased along with the increase in slurry abrasive level, with significance dependent upon the specific substrate and remineralization times. H showed the highest SL on both enamel and dentin; remineralization for 30 minutes reduced SL significantly (P< 0.05), but only for enamel. M showed intermediate SL values, with remineralization benefit clearly seen only after 120 minutes of remineralization (P< 0.05). L caused the least SL for both enamel and dentin, which was further reduced after remineralization for 120 and 30 minutes, respectively (both P< 0.05). Overall, root dentin had significantly higher SL than enamel. Less abrasive dentifrice slurries were able to reduce toothbrushing abrasion on both enamel and root dentin. This protection was enhanced by remineralization for all abrasive levels on enamel, but only for L on root dentin. High-risk erosion patients should avoid highly abrasive toothpastes, as remineralization can only partially compensate for their deleterious effects on eroded dental surfaces. Lower abrasive toothpastes are recommended. Copyright©American Journal of Dentistry.

Modeling micromechanical measurements of depth-varying properties with scanning acoustic microscopy

NASA Astrophysics Data System (ADS)

Marangos, Orestes; Misra, Anil

2018-02-01

Scanning acoustic microscopy (SAM) has been applied to measure the near-surface elastic properties of materials. For many substrates, the near-surface property is not constant but varies with depth. In this paper, we aim to interpret the SAM data from such substrates by modeling the interaction of the focused ultrasonic field with a substrate having a near-surface graded layer. The focused ultrasonic field solutions were represented as spherical harmonic expansions while the substrate solutions were represented as plane wave expansions. The bridging of the two solutions was achieved through the decomposition of the ultrasonic pressure fields in their angular spectra. Parametric studies were performed, which showed that near-surface graded layers exhibit distinctive frequency dependence of their reflectance functions. This behavior is characteristic to the material property gradation profile as well as the extent of the property gradation. The developed model was used to explain the frequency-dependent reflection coefficients measured from an acid-etched dentin substrate. Based on the model calculations, the elastic property variations of the acid-etched dentin near-surface indicate that the topmost part of the etched layer is very soft (3-6 GPa) and transitions to the native dentin through a depth of 27 and 36 microns.

Effects of gamma radiation on hard dental tissues of albino rats using scanning electron microscope - Part 1

NASA Astrophysics Data System (ADS)

El-Faramawy, Nabil; Ameen, Reham; El-Haddad, Khaled; Maghraby, Ahmed; El-Zainy, Medhat

2011-12-01

In the present study, 40 adult male albino rats were used to study the effect of gamma radiation on the hard dental tissues (enamel surface, dentinal tubules and the cementum surface). The rats were irradiated at 0.2, 0.5, 1.0, 2.0, 4.0 and 6.0 Gy gamma doses. The effects of irradiated hard dental tissues samples were investigated using a scanning electron microscope. For doses up to 0.5 Gy, there was no evidence of the existence of cracks on the enamel surface. With 1 Gy irradiation dose, cracks were clearly observed with localized erosive areas. At 2 Gy irradiation dose, the enamel showed morphological alterations as disturbed prismatic and interprismatic areas. An increase in dentinal tubules diameter and a contemporary inter-tubular dentine volume decrease were observed with higher irradiation dose. Concerning cementum, low doses,<0.5 Gy, showed surface irregularities and with increase in the irradiation dose to≥1 Gy, noticeable surface irregularities and erosive areas with decrease in Sharpey's fiber sites were observed. These observations could shed light on the hazardous effects of irradiation fields to the functioning of the human teeth.

Effect of application mode on interfacial morphology and chemistry between dentin and self-etch adhesives

PubMed Central

Zhang, Ying; Wang, Yong

2012-01-01

Objective To investigate the influence of application mode on the interfacial morphology and chemistry between dentin and self-etch adhesives with different aggressiveness. Methods The occlusal one-third of the crown was removed from un-erupted human third molars, followed by abrading with 600 grit SiC under water. Rectangular dentin slabs were prepared by sectioning the tooth specimens perpendicular to the abraded surfaces. The obtained dentin slabs were treated with one of the two one-step self-etch adhesives: Adper Easy Bond (AEB, PH~2.5) and Adper Prompt L-Pop (APLP, PH~0.8) with (15s, active application) or without (15s, inactive application) agitation. The dentin slabs were fractured and the exposed adhesive/dentin (A/D) interfaces were examined with micro-Raman spectroscopy and scanning electron microscopy (SEM). Results The interfacial morphology, degree of dentin demineralization (DD) and degree of conversion (DC) of the strong self-etch adhesive APLP showed more significant dependence on the application mode than the mild AEB. APLP exhibited inferior bonding at the A/D interface if applied without agitation, evidenced by debonding from the dentin substrate. The DDs and DCs of the APLP with agitation were higher than those of without agitation in the interface, in contrast to the comparable DD and DC values of two AEB specimen groups with different application modes. Raman spectral analysis revealed the important role of chemical interaction between acid monomers of self-etch adhesives and dentin in the above observations. Conclusion The chemical interaction with dentin is especially important for improving the DC of the strong self-etching adhesive at the A/D interface. Agitation could benefit polymerization efficacy of the strong self-etch adhesive through enhancing the chemical interaction with tooth substrate. PMID:23153573

Effect of additional etching and ethanol-wet bonding on the dentin bond strength of one-step self-etch adhesives

PubMed Central

Ahn, Joonghee; Jung, Kyoung-Hwa; Son, Sung-Ae; Hur, Bock; Kwon, Yong-Hoon

2015-01-01

Objectives This study examined the effects of additional acid etching on the dentin bond strength of one-step self-etch adhesives with different compositions and pH. The effect of ethanol wetting on etched dentin bond strength of self-etch adhesives was also evaluated. Materials and Methods Forty-two human permanent molars were classified into 21 groups according to the adhesive types (Clearfil SE Bond [SE, control]; G-aenial Bond [GB]; Xeno V [XV]; Beauti Bond [BB]; Adper Easy Bond [AE]; Single Bond Universal [SU]; All Bond Universal [AU]), and the dentin conditioning methods. Composite resins were placed on the dentin surfaces, and the teeth were sectioned. The microtensile bond strength was measured, and the failure mode of the fractured specimens was examined. The data were analyzed statistically using two-way ANOVA and Duncan's post hoc test. Results In GB, XV and SE (pH ≤ 2), the bond strength was decreased significantly when the dentin was etched (p < 0.05). In BB, AE and SU (pH 2.4 - 2.7), additional etching did not affect the bond strength (p > 0.05). In AU (pH = 3.2), additional etching increased the bond strength significantly (p < 0.05). When adhesives were applied to the acid etched dentin with ethanol-wet bonding, the bond strength was significantly higher than that of the no ethanol-wet bonding groups, and the incidence of cohesive failure was increased. Conclusions The effect of additional acid etching on the dentin bond strength was influenced by the pH of one-step self-etch adhesives. Ethanol wetting on etched dentin could create a stronger bonding performance of one-step self-etch adhesives for acid etched dentin. PMID:25671215

Influence of the dentinal wall on the pH of sodium hypochlorite during root canal irrigation.

PubMed

Macedo, Ricardo Gomes; Herrero, Noemi Pascual; Wesselink, Paul; Versluis, Michel; van der Sluis, Luc

2014-07-01

The purpose of this study was to evaluate the influence of dentin on the pH levels of different concentrations of sodium hypochlorite (NaOCl) solutions over time and to evaluate if preconditioning of dentin with 17% EDTA or agitation of the NaOCl solution influences these pH levels. A novel clinically representative model that scales with the ratio of the irrigant volume to the dentin surface area of a human root canal was used. Three standardized bovine dentin bars (2 × 2 × 10 mm) were placed in a plastic test tube. A total of 150 tubes were distributed in 29 groups. In the first experiment, the pH of various NaOCl solutions, with different concentrations (3%, 6%, and 9%) and starting pH levels (5 and 12), was monitored during exposure to dentin between 10 and 300 seconds. In a second experiment, the effect of agitation (45 Hz) and pretreatment of dentin with 17% EDTA on the pH levels of various NaOCl solutions was studied after 30 seconds of exposure to dentin. The short-term chemical stability of the tested solutions was assessed for both the concentration and the pH. The exposure time (P < .001) and concentration of the NaOCl solution (P < .011) significantly influence the pH level after exposure to dentin. However, the change in pH is too small to induce a change in the irrigant antimicrobial/tissue dissolution capacity. Agitation of the irrigant and preconditioning of the dentin did not alter the pH (P > .05). Both the pH 5 and pH 12 solutions were chemically stable for 1 hour. Copyright © 2014 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

Effect of tooth substrate and porcelain thickness on porcelain veneer failure loads in vitro.

PubMed

Ge, Chunling; Green, Chad C; Sederstrom, Dalene A; McLaren, Edward A; Chalfant, James A; White, Shane N

2017-12-19

Bonded porcelain veneers are widely used esthetic restorations. High success and survival rates have been reported, but failures do occur. Fractures are the commonest failure mode. Minimally invasive or thin veneers have gained popularity. Increased enamel and porcelain thickness improve the strength of veneers bonded to enamel, but less is known about dentin or mixed substrates. The purpose of this in vitro study was to measure the influences of tooth substrate type (all-enamel, all-dentin, or half-dentin-half-enamel) and veneer thickness on the loads needed to cause initial and catastrophic porcelain veneer failure. Model discoid porcelain veneer specimens of varying thicknesses were bonded to the flattened facial surfaces of incisors with different enamel and dentin tooth substrates, artificially aged, and loaded to failure with a small sphere. Initial and catastrophic fracture events were identified and analyzed statistically and fractographically. Fracture events included initial Hertzian cracks, intermediate radial cracks, and catastrophic gross failure. All specimens retained some porcelain after catastrophic failure. Cement failure occurred at the cement-porcelain interface not at the cement-tooth interface. Porcelain veneers bonded to enamel were substantially stronger and more damage-tolerant than those bonded to dentin or mixed substrates. Increased porcelain thickness substantially raised the loads to catastrophic failure on enamel substrates but only moderately raised the loads to catastrophic failure on dentin or mixed substrates. The veneers bonded to half-dentin-half-enamel behaved remarkably like those bonded wholly to dentin. Porcelain veneers bonded to enamel were substantially stronger and more damage-tolerant than those bonded to dentin or half-enamel-half dentin. Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Validation of a Cariogenic Biofilm Model to Evaluate the Effect of Fluoride on Enamel and Root Dentine Demineralization.

PubMed

Fernández, Constanza E; Tenuta, Livia M A; Cury, Jaime A

2016-01-01

Due to gingival recession both enamel and root dentine are at risk of developing caries. Both tissues are exposed to a similar environment, however there is not a validated model to evaluate the effect of fluoride on these dental substrates simultaneously. Hence, this study aimed to validate a caries model to evaluate the effect of fluoride to prevent demineralization on enamel and root-dentine. Streptococcus mutans UA159 biofilms were formed on saliva-coated bovine enamel and root dentine slabs (n = 12 per group) mounted in the same well of culture plates. The biofilms were exposed 8×/day to 10% sucrose and treated 2×/day with fluoridated solutions containing 0, 150, 450, or 1,350 ppm F; thus, simulating the use of low to high fluoride concentration toothpastes. The pH values of the culture medium was monitored 2×/day as a biofilm acidogenicity indicator. After 96 h, biofilms were collected for fluoride concentration analysis. The percentage of surface hardness loss (%SHL) was calculated for slabs. The fluoride uptake by the enamel and dentine was also determined. The model showed a dose-response because the biofilm and fluoride uptake increased and %SHL decreased at increasing fluoride concentrations (p < 0.05). Fluoride in the biofilm formed on dentine and fluoride uptake by dentine were higher than those for enamel. With the same fluoride concentration treatment, the percentage of reduction of demineralization was lower for dentine than for enamel. In conclusion, the model was validated in terms of a dose-response effect of fluoride on enamel and root dentine. Furthermore, the findings support the clinical data, suggesting that higher fluoride concentrations are necessary to control caries of root dentine than of enamel.

Effect of Minocycline on the Durability of Dentin Bonding Produced with Etch-and-Rinse Adhesives.

PubMed

Loguercio, A D; Stanislawczuk, R; Malaquias, P; Gutierrez, M F; Bauer, J; Reis, A

2016-01-01

To evaluate the effect of minocycline and chlorhexidine pretreatment of acid-etched dentin on the longevity of resin-dentin bond strength (μTBS) and nanoleakage of two-step etch-and-rinse adhesives. Before application of Prime & Bond NT and Adper Single Bond 2 in occlusal dentin, the dentin surfaces were treated with 37% phosphoric acid, rinsed, air-dried, and rewetted with water (control group), 2% minocycline, or 2% chlorexidine digluconate. Composite buildups were constructed incrementally, and specimens were longitudinally sectioned to obtain bonded sticks (0.8 mm 2 ) to be tested in tension (0.5 mm/min) immediately or after 24 months of water storage. For nanoleakage, two specimens of each tooth/period were immersed in the silver nitrate solution, photo-developed, and polished with SiC paper for analysis under energy-dispersive X-ray spectroscopy/scanning electron microscopy. Reductions of the μTBS and increases in the nanoleakage were observed for both adhesives when the rewetting procedure was performed with water. Stable bonds were observed for the 2% minocycline and 2% chlorexidine digluconate groups after 24 months. The use of 2% minocycline as pretreatment of acid-etched dentin is one alternative to retard the degradation of resin-dentin interfaces over a 24-month period as well as 2% chlorexidine digluconate.

Microtensile bond strength of etch and rinse versus self-etch adhesive systems.

PubMed

Hamouda, Ibrahim M; Samra, Nagia R; Badawi, Manal F

2011-04-01

The aim of this study was to compare the microtensile bond strength of the etch and rinse adhesive versus one-component or two-component self-etch adhesives. Twelve intact human molar teeth were cleaned and the occlusal enamel of the teeth was removed. The exposed dentin surfaces were polished and rinsed, and the adhesives were applied. A microhybride composite resin was applied to form specimens of 4 mm height and 6 mm diameter. The specimens were sectioned perpendicular to the adhesive interface to produce dentin-resin composite sticks, with an adhesive area of approximately 1.4 mm(2). The sticks were subjected to tensile loading until failure occurred. The debonded areas were examined with a scanning electron microscope to determine the site of failure. The results showed that the microtensile bond strength of the etch and rinse adhesive was higher than that of one-component or two-component self-etch adhesives. The scanning electron microscope examination of the dentin surfaces revealed adhesive and mixed modes of failure. The adhesive mode of failure occurred at the adhesive/dentin interface, while the mixed mode of failure occurred partially in the composite and partially at the adhesive/dentin interface. It was concluded that the etch and rinse adhesive had higher microtensile bond strength when compared to that of the self-etch adhesives. Copyright © 2010 Elsevier Ltd. All rights reserved.

Tensile and bending fatigue of the adhesive interface to dentin.

PubMed

Belli, Renan; Baratieri, Luiz Narciso; Braem, Marc; Petschelt, Anselm; Lohbauer, Ulrich

2010-12-01

The aim of this study was to evaluate the fatigue limits of the dentin-composite interfaces established either with an etch-and-rinse or an one-step self-etch adhesive systems under tensile and bending configurations. Flat specimens (1.2 mm×5 mm×35 mm) were prepared using a plexiglass mold where dentin sections from human third molars were bonded to a resin composite, exhibiting the interface centrally located. Syntac Classic and G-Bond were used as adhesives and applied according to the manufacturer's instructions. The fluorochrome Rhodamine B was added to the adhesives to allow for fractographic evaluation. Tensile strength was measured in an universal testing machine and the bending strength (n=15) in a Flex machine (Flex, University of Antwerp, Belgium), respectively. Tensile (TFL) and bending fatigue limits (BFL) (n=25) were determined under wet conditions for 10(4) cycles following a staircase approach. Interface morphology and fracture mechanisms were observed using light, confocal laser scanning and scanning electron microscopy. Statistical analysis was performed using three-way ANOVA (mod LSD test, p<0.05). Tensile and bending characteristic strengths at 63.2% failure probability for Syntac were 23.8 MPa and 71.5 MPa, and 24.7 MPa and 72.3 MPa for G-Bond, respectively. Regarding the applied methods, no significant differences were detected between adhesives. However, fatigue limits for G-Bond (TFL=5.9 MPa; BFL=36.2 MPa) were significantly reduced when compared to Syntac (TFL=12.6 MPa; BFL=49.7 MPa). Fracture modes of Syntac were generally of adhesive nature, between the adhesive resin and dentin, while G-Bond showed fracture planes involving the adhesive-dentin interface and the adhesive resin. Cyclic loading under tensile and bending configurations led to a significant strength degradation, with a more pronounced fatigue limit decrease for G-Bond. The greater decrease in fracture strength was observed in the tensile configuration. Copyright © 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

In Vitro Adhesion of Streptococcus sanguinis to Dentine Root Surface After Treatment with Er:Yag Laser, Ultrasonic System, or Manual Curette

PubMed Central

Martins, Fernanda L.; Giorgetti, Ana Paula O.; de Freitas, Patrícia M.; Duarte, Poliana M.

2009-01-01

Abstract Objective: The purpose of this in vitro study was to evaluate the dentine root surface roughness and the adherence of Streptococcus sanguinis (ATCC 10556) after treatment with an ultrasonic system, Er:YAG laser, or manual curette. Background Data: Bacterial adhesion and formation of dental biofilm after scaling and root planing may be a challenge to the long-term stability of periodontal therapy. Materials and Methods: Forty flattened bovine roots were randomly assigned to one of the following groups: ultrasonic system (n = 10); Er:YAG laser (n = 10); manual curette (n = 10); or control untreated roots (n = 10). The mean surface roughness (Ra, μm) of the specimens before and after exposure to each treatment was determined using a surface profilometer. In addition, S. sanguinis was grown on the treated and untreated specimens and the amounts of retained bacteria on the surfaces were measured by culture method. Results: All treatments increased the Ra; however, the roughest surface was produced by the curettes. In addition, the specimens treated with curettes showed the highest S. sanguinis adhesion. There was a significant positive correlation between roughness values and bacterial cells counts. Conclusion: S. sanguinis adhesion was the highest on the curette-treated dentine root surfaces, which also presented the greatest surface roughness. PMID:19712018

Monitoring of copper nanoparticle penetration into dentin of human tooth in vitro

NASA Astrophysics Data System (ADS)

Selifonov, Alexey A.; Glukhovskoy, Evgeny G.; Skibina, Yulia S.; Zakharevich, Andrey M.; Begletsova, Nadezhda N.; Tuchin, Valery V.

2018-04-01

Study of the penetration depth of synthesized copper nanoparticles into cut samples of human dentin was conducted. The scanning electron microscopy was used to determine the elemental composition of fresh transverse cleavage of the dentin cut for determination of the copper nanoparticles penetration with an effective antiseptic effect. The morphology of the cut surface of the dentin of a human tooth was studied and the lower limit of the diffusion boundary was determined. It was found that copper nanoparticles penetrate into the dentin cut to a depth of 1.8 μm with the diffusion coefficient of 1.8×10-11 cm2/s. Despite the rather small size of the synthesized copper nanoparticles (20-80 nm), a rather small penetration depth can be explained by the high aggregation ability of copper nanoparticles, as well as the ability of a micellar solution of sodium dodecyl sulfate, in which nanoparticles were stabilized, to form conglomerates in micelles of much larger sizes.

Qualitative comparison of sonic or laser energisation of 4% sodium hypochlorite on an Enterococcus faecalis biofilm grown in vitro.

PubMed

Seet, Aaron N; Zilm, Peter S; Gully, Neville J; Cathro, Peter R

2012-12-01

The effectiveness of sonic activation, laser activation and syringe irrigation of 4% sodium hypochlorite in removing an Enterococcus faecalis biofilm was compared. Biofilms were grown in extracted human single rooted teeth using a flow cell apparatus. After 4 weeks' growth, teeth were subjected to each treatment using 4% sodium hypochlorite and radicular dentinal surfaces of the root canals were analysed by scanning electron microscopy. Results showed that sonic activation and syringe irrigation with sodium hypochlorite showed reduced numbers of bacterial cells on the radicular dentine but were not effective in eliminating E. faecalis in the dentinal tubules. Laser activation of sodium hypochlorite resulted in clean dentine walls and undetectable levels of bacteria within dentinal tubules. Qualitatively, sonic or laser activation of 4% NaOCl resulted in greater bacterial reduction compared with syringe irrigation, with laser activation producing the greatest overall reduction. © 2012 The Authors. Australian Endodontic Journal © 2012 Australian Society of Endodontology.

Effect of Er,Cr:YSGG laser on human dentin fluid flow.

PubMed

Al-Omari, Wael M; Palamara, Joseph E

2013-11-01

The aim of the current investigation was to assess the rate and magnitude of dentin fluid flow of dentinal surfaces irradiated with Er,Cr:YSGG laser. Twenty extracted third molars were sectioned, mounted, and irradiated with Er,Cr:YSGG laser at 3.5 and 4.5 W power settings. Specimens were connected to an automated fluid flow measurement apparatus (Flodec). The rate, magnitude, and direction of dentin fluid flow were recorded at baseline and after irradiation. Nonparametric Wilcoxon signed ranks repeated measure t test revealed a statistically significant reduction in fluid flow for all the power settings. The 4.5-W power output reduced the flow significantly more than the 3.5 W. The samples showed a baseline outward flow followed by inward flow due to irradiation then followed by decreased outward flow. It was concluded that Er,Cr:YSGG laser irradiation at 3.5 and 4.5 W significantly reduced dentinal fluid flow rate. The reduction was directly proportional to power output.

Elemental content of enamel and dentin after bleaching of teeth (a comparative study between laser-induced breakdown spectroscopy and x-ray photoelectron spectroscopy)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Imam, H.; Ahmed, Doaa; Eldakrouri, Ashraf

2013-06-21

The elemental content of the superficial and inner enamel as well as that of dentin was analyzed using laser-induced breakdown spectroscopy (LIBS) and x-ray photoelectron spectroscopy (XPS) of bleached and unbleached tooth specimens. It is thus clear from the spectral analysis using both the LIBS and XPS technique that elemental changes (though insignificant within the scopes of this study) of variable intensities do occur on the surface of the enamel and extend deeper to reach dentin. The results of the LIBS revealed a slight reduction in the calcium levels in the bleached compared to the control specimens in all themore » different bleaching groups and in both enamel and dentin. The good correlation found between the LIBS and XPS results demonstrates the possibility of LIBS technique for detection of minor loss in calcium and phosphorus in enamel and dentin.« less

MicroCT analysis of a retrieved root restored with a bonded fiber-reinforced composite dowel: a pilot study.

PubMed

Lorenzoni, Fabio Cesar; Bonfante, Estevam A; Bonfante, Gerson; Martins, Leandro M; Witek, Lukasz; Silva, Nelson R F A

2013-08-01

This evaluation aimed to (1) validate micro-computed tomography (microCT) findings using scanning electron microscopy (SEM) imaging, and (2) quantify the volume of voids and the bonded surface area resulting from fiber-reinforced composite (FRC) dowel cementation technique using microCT scanning technology/3D reconstructing software. A fiberglass dowel was cemented in a condemned maxillary lateral incisor prior to its extraction. A microCT scan was performed of the extracted tooth creating a large volume of data in DICOM format. This set of images was imported to image-processing software to inspect the internal architecture of structures. The outer surface and the spatial relationship of dentin, FRC dowel, cement layer, and voids were reconstructed. Three-dimensional spatial architecture of structures and volumetric analysis revealed that 9.89% of the resin cement was composed of voids and that the bonded area between root dentin and cement was 60.63% larger than that between cement and FRC dowel. SEM imaging demonstrated the presence of voids similarly observed using microCT technology (aim 1). MicroCT technology was able to nondestructively measure the volume of voids within the cement layer and the bonded surface area at the root/cement/FRC interfaces (aim 2). The interfaces at the root dentin/cement/dowel represent a timely and relevant topic where several efforts have been conducted in the past few years to understand their inherent features. MicroCT technology combined with 3D reconstruction allows for not only inspecting the internal arrangement rendered by fiberglass adhesively bonded to root dentin, but also estimating the volume of voids and contacted bond area between the dentin and cement layer. © 2013 by the American College of Prosthodontists.

Two methods to simulate intrapulpal pressure: effects upon bonding performance of self-etch adhesives.

PubMed

Feitosa, V P; Gotti, V B; Grohmann, C V; Abuná, G; Correr-Sobrinho, L; Sinhoreti, M A C; Correr, A B

2014-09-01

To evaluate the effects of two methods to simulate physiological pulpal pressure on the dentine bonding performance of two all-in-one adhesives and a two-step self-etch silorane-based adhesive by means of microtensile bond strength (μTBS) and nanoleakage surveys. The self-etch adhesives [G-Bond Plus (GB), Adper Easy Bond (EB) and silorane adhesive (SIL)] were applied to flat deep dentine surfaces from extracted human molars. The restorations were constructed using resin composites Filtek Silorane or Filtek Z350 (3M ESPE). After 24 h using the two methods of simulated pulpal pressure or no pulpal pressure (control groups), the bonded teeth were cut into specimens and submitted to μTBS and silver uptake examination. Results were analysed with two-way anova and Tukey's test (P < 0.05). Both methods of simulated pulpal pressure led statistically similar μTBS for all adhesives. No difference between control and pulpal pressure groups was found for SIL and GB. EB led significant drop (P = 0.002) in bond strength under pulpal pressure. Silver impregnation was increased after both methods of simulated pulpal pressure for all adhesives, and it was similar between the simulated pulpal pressure methods. The innovative method to simulate pulpal pressure behaved similarly to the classic one and could be used as an alternative. The HEMA-free one-step and the two-step self-etch adhesives had acceptable resistance against pulpal pressure, unlike the HEMA-rich adhesive. © 2013 International Endodontic Journal. Published by John Wiley & Sons Ltd.

Effect of in vitro chewing and bruxism events on remineralization, at the resin-dentin interface.

PubMed

Toledano, Manuel; Cabello, Inmaculada; Aguilera, Fátima S; Osorio, Estrella; Osorio, Raquel

2015-01-02

The purpose of this study was to evaluate if different in vitro functional and parafunctional habits promote mineralization at the resin-dentin interface after bonding with three different adhesive approaches. Dentin surfaces were subjected to distinct treatments: demineralization by (1) 37% phosphoric acid (PA) followed by application of an etch-and-rinse dentin adhesive, Single Bond (SB) (PA+SB); (2) 0.5 M ethylenediaminetetraacetic acid (EDTA) followed by SB (EDTA+SB); (3) application of a self-etch dentin adhesive, Clearfil SE Bond (SEB). Different loading waveforms were applied: No cycling (I), cycled in sine (II) or square (III) waves, sustained loading hold for 24 h (IV) or sustained loading hold for 72 h (V). Remineralization at the bonded interfaces was assessed by AFM imaging/nano-indentation, Raman spectroscopy and Masson's trichrome staining. In general, in vitro chewing and parafunctional habits, promoted an increase of nano-mechanical properties at the resin-dentin interface. Raman spectroscopy through cluster analysis demonstrated an augmentation of the mineral-matrix ratio in loaded specimens. Trichrome staining reflected a narrow demineralized dentin matrix after loading in all groups except in PA+SB and EDTA+SB samples after sustained loading hold for 72 h, which exhibited a strong degree of mineralization. In vitro mechanical loading, produced during chewing and bruxism (square or hold 24 and 72 h waveforms), induced remineralization at the resin-dentin bonded interface. Copyright © 2014 Elsevier Ltd. All rights reserved.

Microorganism penetration in dentinal tubules of instrumented and retreated root canal walls. In vitro SEM study

PubMed Central

Al-Sulaiman, Alaa; Al-Rasheed, Fellwa; Alnajjar, Fatimah; Al-Abdulwahab, Bander; Al-Badah, Abdulhakeem

2014-01-01

Objectives This in vitro study aimed to investigate the ability of Candida albicans (C. albicans) and Enterococcus faecalis (E. faecalis) to penetrate dentinal tubules of instrumented and retreated root canal surface of split human teeth. Materials and Methods Sixty intact extracted human single-rooted teeth were divided into 4 groups, negative control, positive control without canal instrumentation, instrumented, and retreated. Root canals in the instrumented group were enlarged with endodontic instruments, while root canals in the retreated group were enlarged, filled, and then removed the canal filling materials. The teeth were split longitudinally after canal preparation in 3 groups except the negative control group. The teeth were inoculated with both microorganisms separately and in combination. Teeth specimens were examined by scanning electron microscopy (SEM), and the depth of penetration into the dentinal tubules was assessed using the SMILE view software (JEOL Ltd). Results Penetration of C. albicans and E. faecalis into the dentinal tubules was observed in all 3 groups, although penetration was partially restricted by dentin debris of tubules in the instrumented group and remnants of canal filling materials in the retreated group. In all 3 groups, E. faecalis penetrated deeper into the dentinal tubules by way of cell division than C. albicans which built colonies and penetrated by means of hyphae. Conclusions Microorganisms can easily penetrate dentinal tubules of root canals with different appearance based on the microorganism size and status of dentinal tubules. PMID:25383343

Morphological alterations of radicular dentine pretreated with different irrigating solutions and irradiated with 980-nm diode laser.

PubMed

Alfredo, Edson; Souza-Gabriel, Aline E; Silva, Silvio Rocha C; Sousa-Neto, Manoel D; Brugnera-Junior, Aldo; Silva-Sousa, Yara T C

2009-01-01

The topographical features of intraradicular dentine pretreated with sodium hypochlorite (NaOCl) or ethylenediamine tetraacetic acid (EDTA) followed by diode laser irradiation have not yet been determined. To evaluate the alterations of dentine irradiated with 980-nm diode laser at different parameters after the surface treatment with NaOCl and EDTA. Roots of 60 canines were biomechanically prepared and irrigated with NaOCl or EDTA. Groups were divided according to the laser parameters: 1.5 W/CW; 1.5 W/100 Hz; 3.0 W/CW; 3.0 W/100 Hz and no irradiation (control). The roots were splited longitudinally and analyzed by scanning electron microscopy (SEM) in a quali-quatitative way. The scores were submitted to two-way Kruskal-Wallis and Dunn's tests. The statistical analysis demonstrated that the specimens treated only with NaOCl or EDTA (control groups) were statistically different (P < 0.05) from the laser-irradiated specimens, regardless of the parameter setting. The specimens treated with NaOCl showed a laser-modified surface with smear layer, fissures, and no visible tubules. Those treated with EDTA and irradiated by laser presented absence of smear layer, tubules partially exposed and melting areas. The tested parameters of 980-nm diode laser promoted similar alterations on dentine morphology, dependent to the type of surface pretreatment. Copyright 2008 Wiley-Liss, Inc.

Bond strength to dentin with artificial carious lesions: influence of caries detecting dye.

PubMed

Palma, R G; Turbino, M L; Matson, E; Powers, J M

1998-06-01

To evaluate the influence of dyes for caries detection on tensile bond strength of adhesive materials to artificial carious dentin. Buccal and lingual enamel of human molars were removed leaving intact dentin surfaces. The entire surface of each specimen was covered with nail varnish, keeping a window area of 4 x 4 mm. Artificial carious lesions were induced with acidified gel. Three dyes (0.5% basic fuchsin; Caries Finder and Cari-D-Tect) were used according to manufacturers' recommendations. Specimens were etched with 35% phosphoric acid for 20 s, washed and dried, leaving a wet dentin surface. The adhesive system (Prime & Bond 2.0) was applied in two layers and light-cured. Restorative materials (TPH Spectrum, Dyract, Advance) were bonded using a 3-mm diameter inverted-cone mold. Control groups were made without dye. Eight samples were tested for each group. After 24 hrs of storage in distilled water, the samples were debonded using a testing machine at 0.5 mm/min crosshead speed. ANOVA and Tukey-Kramer test showed that TPH Spectrum (0.73 MPa) and Dyract (0.74 MPa) had similar bond strengths, and both were higher than Advance (0.0 MPa), which was statistically different (P < 0.01). The use of the dyes did not cause any changes in tensile bond strength for any tested materials.

The Retentive Strength of Cemented Zirconium Oxide Crowns after Dentin Pretreatment with Desensitizing Paste Containing 8% Arginine and Calcium Carbonate

PubMed Central

Pilo, Raphael; Harel, Noga; Nissan, Joseph; Levartovsky, Shifra

2016-01-01

The effect of dentin pretreatment with Desensitizing Paste containing 8% arginine and calcium carbonate on the retention of zirconium oxide (Y-TZP) crowns was tested. Forty molar teeth were mounted and prepared using a standardized protocol. Y-TZP crowns were produced using computer-aided design and computer-aided manufacturing (CAD-CAM) technology. The 40 prepared teeth were either pretreated with Desensitizing Paste or not pretreated. After two weeks, each group was subdivided into two groups, cemented with either Resin Modified Glass Ionomer Cement (RMGIC) or Self Adhesive Resin Cement (SARC)). Prior to cementation, the surface areas of the prepared teeth were measured. After aging, the cemented crown-tooth assemblies were tested for retentive strength using a universal testing machine. The debonded surfaces of the teeth and crowns were examined microscopically at 10× magnification. Pretreating the dentin surfaces with Desensitizing Paste prior to cementation did not affect the retention of the Y-TZP crowns. The retentive values for RMGIC (3.04 ± 0.77 MPa) were significantly higher than those for SARC (2.28 ± 0.58 MPa). The predominant failure modes for the RMGIC and SARC were adhesive cement-dentin and adhesive cement-crown, respectively. An 8.0% arginine and calcium carbonate in-office desensitizing paste can be safely used to reduce post-cementation sensitivity without reducing the retentive strength of Y-TZP crowns. PMID:27023532

The Retentive Strength of Cemented Zirconium Oxide Crowns after Dentin Pretreatment with Desensitizing Paste Containing 8% Arginine and Calcium Carbonate.

PubMed

Pilo, Raphael; Harel, Noga; Nissan, Joseph; Levartovsky, Shifra

2016-03-25

The effect of dentin pretreatment with Desensitizing Paste containing 8% arginine and calcium carbonate on the retention of zirconium oxide (Y-TZP) crowns was tested. Forty molar teeth were mounted and prepared using a standardized protocol. Y-TZP crowns were produced using computer-aided design and computer-aided manufacturing (CAD-CAM) technology. The 40 prepared teeth were either pretreated with Desensitizing Paste or not pretreated. After two weeks, each group was subdivided into two groups, cemented with either Resin Modified Glass Ionomer Cement (RMGIC) or Self Adhesive Resin Cement (SARC)). Prior to cementation, the surface areas of the prepared teeth were measured. After aging, the cemented crown-tooth assemblies were tested for retentive strength using a universal testing machine. The debonded surfaces of the teeth and crowns were examined microscopically at 10× magnification. Pretreating the dentin surfaces with Desensitizing Paste prior to cementation did not affect the retention of the Y-TZP crowns. The retentive values for RMGIC (3.04 ± 0.77 MPa) were significantly higher than those for SARC (2.28 ± 0.58 MPa). The predominant failure modes for the RMGIC and SARC were adhesive cement-dentin and adhesive cement-crown, respectively. An 8.0% arginine and calcium carbonate in-office desensitizing paste can be safely used to reduce post-cementation sensitivity without reducing the retentive strength of Y-TZP crowns.

Femtosecond laser ablation of dentin and enamel: relationship between laser fluence and ablation efficiency.

PubMed

Chen, Hu; Liu, Jing; Li, Hong; Ge, Wenqi; Sun, Yuchun; Wang, Yong; Lü, Peijun

2015-02-01

The objective was to study the relationship between laser fluence and ablation efficiency of a femtosecond laser with a Gaussian-shaped pulse used to ablate dentin and enamel for prosthodontic tooth preparation. A diode-pumped thin-disk femtosecond laser with wavelength of 1025 nm and pulse width of 400 fs was used for the ablation of dentin and enamel. The laser spot was guided in a line on the dentin and enamel surfaces to form a groove-shaped ablation zone under a series of laser pulse energies. The width and volume of the ablated line were measured under a three-dimensional confocal microscope to calculate the ablation efficiency. Ablation efficiency for dentin reached a maximum value of 0.020 mm3∕J when the laser fluence was set at 6.51 J∕cm2. For enamel, the maximum ablation efficiency was 0.009 mm3∕J at a fluence of 7.59 J∕cm2.Ablation efficiency of the femtosecond laser on dentin and enamel is closely related to the laser fluence and may reach a maximum when the laser fluence is set to an appropriate value. © 2015 Society of Photo-Optical Instrumentation Engineers (SPIE)

Effectiveness of plant-derived proanthocyanidins on demineralization on enamel and dentin under artificial cariogenic challenge

PubMed Central

da SILVA, Ana Paula Pereira; GONÇALVES, Rafael Simões; BORGES, Ana Flávia Sanches; BEDRAN-RUSSO, Ana Karina; SHINOHARA, Mirela Sanae

2015-01-01

Dental caries is considered a disease of high prevalence and a constant problem in public health. Proanthocyanidins (PAs) are substances that have been the target of recent studies aiming to control or treat caries. Objective The aim of this in vitro study was to evaluate the efficacy of a treatment with grape seed extract, under cariogenic challenge, to minimize or even prevent the onset of caries in the enamel and dentin. Material and Methods Blocks of enamel and dentin (6.0x6.0 mm) were obtained from bovine central incisors, polished, and selected by analysis of surface microhardness (SH). The blocks were randomly divided into 3 groups (n=15), according to the following treatments: GC (control), GSE (grape seed extract), GF (fluoride – 1,000 ppm). The blocks were subjected to 6 daily pH cycles for 8 days. Within the daily cycling, the specimens were stored in buffered solution. The blocks were then analyzed for perpendicular and surface hardness and polarized light microscopy. Results The means were subjected to statistical analysis using the ANOVA and Fisher’s PLSD tests (p<0.05). For enamel SH, GF showed the highest hardness values. In the dentin, GF was also the one that showed higher hardness values, followed by GSE. Regarding the cross-sectional hardness values, all groups behaved similarly in both the enamel and dentin. The samples that were treated with GSE and fluoride (GF) showed statistically higher values than the control. Conclusion Based on the data obtained in this in vitro study, it is suggested that grape seed extract inhibits demineralization of artificial carious lesions in both the enamel and dentin, but in a different scale in each structure and in a smaller scale when compared to fluoride. PMID:26221925

Dentine Tubule Occlusion by Novel Bioactive Glass-Based Toothpastes

PubMed Central

Hill, Robert G.; Chen, Xiaojing

2018-01-01

There are numerous over-the-counter (OTC) and professionally applied (in-office) products and techniques currently available for the treatment of dentine hypersensitivity (DH), but more recently, the use of bioactive glasses in toothpaste formulations have been advocated as a possible solution to managing DH. Aim. The aim of the present study, therefore, was to compare several bioactive glass formulations to investigate their effectiveness in an established in vitro model. Materials and Methods. A 45S5 glass was synthesized in the laboratory together with several other glass formulations: (1) a mixed glass (fluoride and chloride), (2) BioMinF, (3) a chloride glass, and (4) an amorphous chloride glass. The glass powders were formulated into five different toothpaste formulations. Dentine discs were sectioned from extracted human teeth and prepared for the investigation by removing the cutting debris (smear layer) following sectioning using a 6% citric acid solution for 2 minutes. Each disc was halved to provide test and control halves for comparison following the brushing of the five toothpaste formulations onto the test halves for each toothpaste group. Following the toothpaste application, the test discs were immersed in either artificial saliva or exposed to an acid challenge. Results. The dentine samples were analyzed using scanning electron microscopy (SEM), and observation of the SEM images indicated that there was good surface coverage following artificial saliva immersion. Furthermore, although the acid challenge removed the hydroxyapatite layer on the dentine surface for most of the samples, except for the amorphous chloride glass, there was evidence of tubular occlusion in the dentine tubules. Conclusions. The conclusions from the study would suggest that the inclusion of bioactive glass into a toothpaste formulation may be an effective approach to treat DH. PMID:29849637

Bonding effectiveness and interfacial characterization of a nano-filled resin-modified glass-ionomer.

PubMed

Coutinho, E; Cardoso, M V; De Munck, J; Neves, A A; Van Landuyt, K L; Poitevin, A; Peumans, M; Lambrechts, P; Van Meerbeek, B

2009-11-01

Glass-ionomers (GIs) exhibit excellent clinical bonding effectiveness, but still have shortcomings such as polishability and general aesthetics. The aims of this study were (1) to determine the micro-tensile bond strength (microTBS) to enamel and dentin of a nano-filled resin-modified GI (nano-RMGI; Ketac N100, 3M-ESPE), and (2) to characterize its interfacial interaction with enamel and dentin using transmission electron microscopy (TEM). The nano-RMGI was used both with and without its primer, while a conventional RMGI restorative material (conv-RMGI; Fuji II LC, GC) and a packable conventional GI cement (conv-GI; Fuji IX GP, GC) were used as controls. After bonding to freshly extracted human third molars, microspecimens of the interfaces were machined into a cylindrical hourglass shape and tested to failure in tension. Non-demineralized TEM sections were prepared and examined from additional teeth. The microTBS to both enamel and dentin of nano-RMGI and conv-GI were not statistically different; the microTBS of non-primed nano-RMGI was significantly lower, while that of conv-RMGI was significantly higher than that of all other groups. TEM of nano-RMGI disclosed a tight interface at enamel and dentin without surface demineralization and hybrid-layer formation. A thin filler-free zone (<1 microm) was formed at dentin. A high filler loading and effective filler distribution were also evident, with localized areas exhibiting nano-filler clustering. The nano-RMGI bonded as effectively to enamel and dentin as conv-GI, but bonded less effectively than conv-RMGI. Its bonding mechanism should be attributed to micro-mechanical interlocking provided by the surface roughness, most likely combined with chemical interaction through its acrylic/itaconic acid copolymers.

Comparative Evaluation of Efficacy of Iontophoresis with 0.33% Sodium Fluoride Gel and Diode Laser Alone on Occlusion of Dentinal Tubules

PubMed Central

Varma, Siddhartha; Suragimath, Girish; Abbayya, Keshava; Zope, Sameer Anil; Kale, Vishwajeet

2017-01-01

Introduction Dentinal Hypersensitivity (DH) is one of the most commonly encountered clinical problems. Literature reveals no specific therapy to satisfactorily eliminate dentinal hypersensitivity. Aim The aim of this study was to assess and compare the efficacy of iontophoresis with 0.33% Sodium Fluoride (NaF) gel and diode laser alone in dentinal tubule occlusion. Materials and Methods This in vitro study included 20 teeth with intact root surfaces unaltered by extraction procedure for specimen preparation. Each tooth was cleaned, air dried and cut into three sections. Total 60 sections were prepared (30 longitudinal and 30 transverse sections), which were acid etched. In control group, no treatment was carried. In iontophoresis treatment group, samples were inserted into a foam tray containing 0.33 % NaF Gel and subjected to 1.5 mA output current for three minutes. In laser treatment group, specimens were lased with 980 nm diode laser at 0.5 W/PW (62.2J /cm2) in a noncontact mode for 30 seconds. Specimens were evaluated under Scanning Electron Microscope (SEM) at 10KV to 20KV under x 2000, x5000 magnification for surface characteristics and patency of dentinal tubules. Total number of tubules visible, open, completely and partially occluded were recorded in each microphotograph and compared. Results On comparison, laser group showed the least number of open tubules i.e., 130 (31.1%) followed by iontophoresis group, 155 (51.32%) and control group 417 (100%). Conclusion Diode laser application provided better results as compared to iontophoresis on occlusion of dentinal tubules. Hence, it can be used to treat the patients with DH. PMID:28969290

Comparative Evaluation of Efficacy of Iontophoresis with 0.33% Sodium Fluoride Gel and Diode Laser Alone on Occlusion of Dentinal Tubules.

PubMed

Patil, Anup Raghunath; Varma, Siddhartha; Suragimath, Girish; Abbayya, Keshava; Zope, Sameer Anil; Kale, Vishwajeet

2017-08-01

Dentinal Hypersensitivity (DH) is one of the most commonly encountered clinical problems. Literature reveals no specific therapy to satisfactorily eliminate dentinal hypersensitivity. The aim of this study was to assess and compare the efficacy of iontophoresis with 0.33% Sodium Fluoride (NaF) gel and diode laser alone in dentinal tubule occlusion. This in vitro study included 20 teeth with intact root surfaces unaltered by extraction procedure for specimen preparation. Each tooth was cleaned, air dried and cut into three sections. Total 60 sections were prepared (30 longitudinal and 30 transverse sections), which were acid etched. In control group, no treatment was carried. In iontophoresis treatment group, samples were inserted into a foam tray containing 0.33 % NaF Gel and subjected to 1.5 mA output current for three minutes. In laser treatment group, specimens were lased with 980 nm diode laser at 0.5 W/PW (62.2J /cm 2 ) in a noncontact mode for 30 seconds. Specimens were evaluated under Scanning Electron Microscope (SEM) at 10KV to 20KV under x 2000, x5000 magnification for surface characteristics and patency of dentinal tubules. Total number of tubules visible, open, completely and partially occluded were recorded in each microphotograph and compared. On comparison, laser group showed the least number of open tubules i.e., 130 (31.1%) followed by iontophoresis group, 155 (51.32%) and control group 417 (100%). Diode laser application provided better results as compared to iontophoresis on occlusion of dentinal tubules. Hence, it can be used to treat the patients with DH.

Inhibitory effect of silver diamine fluoride on dentine demineralisation and collagen degradation.

PubMed

Mei, May L; Ito, L; Cao, Y; Li, Q L; Lo, Edward C M; Chu, C H

2013-09-01

To investigate the inhibitory effects of 38% silver diamine fluoride (SDF) on demineralised dentine. Human dentine blocks were demineralised and allocated to four groups: SF, F, S and W. The blocks in group SF received a topical application of 38% SDF solution (253,900ppm Ag, 44,800ppm F), group F received a 10% sodium fluoride solution (44,800ppm F), group S received a 42% silver nitrate solution (253,900ppm Ag) and group W received deionised water (control). They were subjected to pH cycling using demineralisation solution (pH 5) and remineralisation solution (pH 7) for 8 days. The surface morphology, crystal characteristics, lesion depth and collagen matrix degradation of the specimens were investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD), micro-CT testing and spectrophotometry with a hydroxyproline assay. The surface morphology under SEM showed evident demineralisation with exposed collagen in groups S and W, but not in group SF. Clusters of granular spherical grains were observed in the cross-sections of specimens in groups SF and F. XRD revealed precipitates of silver chloride in groups SF and S. The mean lesion depths (±SD) of groups SF, F, S and W were 182 ± 32μm, 204 ± 26μm, 259 ± 42μm and 265 ± 40μm, respectively (SDF, F

Development of a multifunctional adhesive system for prevention of root caries and secondary caries

PubMed Central

Zhang, Ning; Melo, Mary A. S.; Chen, Chen; Liu, Jason; Weir, Michael D.; Bai, Yuxing; Xu, Hockin H. K.

2015-01-01

Objectives The objectives of this study were to: (1) develop a novel adhesive for prevention of tooth root caries and secondary caries by possessing a combination of protein-repellent, antibacterial, and remineralization capabilities for the first time; and (2) investigate the effects of 2-methacryloyloxyethyl phosphorylcholine (MPC), dimethylaminohexadecyl methacrylate (DMAHDM), and nanoparticles of amorphous calcium phosphate (NACP) on dentine bond strength, protein-repellent properties, and dental plaque microcosm biofilm response. Methods MPC, DMAHDM and NACP were added into Scotchbond Multi-Purpose primer and adhesive. Dentine shear bond strengths were measured. Adhesive coating thickness, surface texture and dentine-adhesive interfacial structure were examined. Protein adsorption onto adhesive resin surface was determined by the micro bicinchoninic acid method. A human saliva microcosm biofilm model was used to investigate biofilm metabolic activity, colony-forming unit (CFU) counts, and lactic acid production. Results The resin with 7.5% MPC + 5% DMAHDM + 30% NACP did not adversely affect dentine shear bond strength (p > 0.1). The resin with 7.5% MPC + 5% DMAHDM + 30% NACP produced a coating on root dentine with a thickness of approximately 70 μm and completely sealed all the dentinal tubules. The resin with 7.5% MPC + 5% DMAHDM + 30% NACP had 95% reduction in protein adsorption, compared to SBMP control (p < 0.05). The resin with 7.5% MPC + 5% DMAHDM + 30% NACP was strongly antibacterial, with biofilm CFU being four orders of magnitude lower than that of SBMP control. Significance The novel multifunctional adhesive with strong protein-repellent, antibacterial and remineralization properties is promising to coat tooth roots to prevent root caries and secondary caries. The combined use of MPC, DMAHDM and NACP may have wide applicability to bonding agents, cements, sealants and composites to inhibit caries. PMID:26187532

Comparison of the Effect of Dentin Bonding, Dentin Sealing Agents on the Microleakage of Provisional Crowns Fabricated with Direct and Indirect Technique-An Invitro Study

PubMed Central

Muthukumar, B; Kumar, M Vasantha

2015-01-01

Background Postoperative sensitivity after temporization is a common complaint in Fixed Partial Denture patients. It is caused by weak and ill fitting temporary restorations which results in microleakage. This can be controlled by providing good temporary restorations and by coating the exposed dentinal tubules of the prepared tooth with dentin bonding agent or dental varnish. Aim The purpose of the study was to determine the effect of dentin-bonding, dentin sealing agents on the microleakage of temporary crowns made by tooth colored auto polymerizing resin fabricated with direct and indirect technique. Materials and Methods Thirty premolar and molar human teeth were collected which were extracted recently was used for the study. The teeth were marked and divided into 3 groups each containing 10 nos. They were individually mounted with self-cure acrylic resin. It was then mounted on a milling machine and crown preparations done. Temporary crowns were fabricated by direct and indirect method with two types of materials. In group A (Control group), the temporary crowns fabricated with both direct and indirect method were cemented directly with temporary luting cement. In group B dentine-bonding agent (solobond M) was applied once to the prepared surface of each tooth specimen before the cementation of temporary crowns where as in case of group C a single layer of dental varnish is applied prior to crown cementation. The entire specimens were immersed in 1% methylene blue and allowed to undergo thermal treatment. It was then sectioned in a hard tissue microtome. Each section was evaluated for dye penetration into the dentin tubules by comparing it with a visual scale. Statistical Analysis SPSS Version 13 software was used for non-parametric data analysis by a qualified statistician. P-values less than 0.05 (p-value<0.05) were considered to be statistically significant. Results Group B (Dentin Bonding Agent) specimens cemented with crowns fabricated in direct technique showed the least amount of microleakage when compared with group A and group C. Group C (Dental Varnish) specimen showed comparatively more amount of microleakage than that of group B. Group A (control group) specimens showed the maximum amount of microleakage. Conclusion The application of a single layer of Dental varnish appears to be of no significant benefit when compared to crowns cemented with the application of Dentin bonding agent on the tooth surface. The application of a single layer of Dentin bonding agent (Solobond M) and temporary crowns fabricated with direct technique may be of some benefit for crown preparations as an interim measure prior to the luting of final crown. PMID:26266219

Tooth surface treatment strategies for adhesive cementation

PubMed Central

2017-01-01

PURPOSE The aim of this study was to evaluate the effect of tooth surface pre-treatment steps on shear bond strength, which is essential for understanding the adhesive cementation process. MATERIALS AND METHODS Shear bond strengths of different cements with various tooth surface treatments (none, etching, priming, or etching and priming) on enamel and dentin of human teeth were measured using the Swiss shear test design. Three adhesives (Permaflo DC, Panavia F 2.0, and Panavia V5) and one self-adhesive cement (Panavia SA plus) were included in this study. The interface of the cement and the tooth surface with the different pre-treatments was analyzed using SEM. pH values of the cements and primers were measured. RESULTS The highest bond strength values for all cements were achieved with etching and primer on enamel (25.6 ± 5.3 - 32.3 ± 10.4 MPa). On dentin, etching and priming produced the highest bond strength values for all cements (8.6 ± 2.9 - 11.7 ± 3.5 MPa) except for Panavia V5, which achieved significantly higher bond strengths when pre-treated with primer only (15.3 ± 4.1 MPa). Shear bond strength values were correlated with the micro-retentive surface topography of enamel and the tag length on dentin except for Panavia V5, which revealed the highest bond strength with primer application only without etching, resulting in short but sturdy tags. CONCLUSION The highest bond strength can be achieved for Panavia F 2.0, Permaflo DC, and Panavia SA plus when the tooth substrate is previously etched and the respective primer is applied. The new cement Panavia V5 displayed low technique-sensitivity and attained significantly higher adhesion of all tested cements to dentin when only primer was applied. PMID:28435616

Non-thermal Atmospheric Plasma Treatment for Deactivation of Oral Bacteria and Improvement of Dental Composite Restoration

NASA Astrophysics Data System (ADS)

Yu, Qing Song; Li, H.; Ritts, A. C.; Yang, B.; Chen, M.; Hong, L.; Xu, C.; Yao, X.; Wang, Y.

This paper reviews our recent research results of using non-thermal ­atmospheric plasmas for oral bacterial deactivation and for composite restoration improvement. Oral bacteria of Streptococcus mutans (S. mutans) and Lactobacillus acidophilus (L. acidophilus) with an initial bacterial population density between 1.0 × 108 and 5.0 × 108 cfu/ml were seeded on various media and their survivability with plasma exposure was examined. The plasma exposure time for a 99.9999% cell reduction was less than 15 s for S. mutans and within 5 min for L. acidophilus. To evaluate the dentin/composite interfacial bonding, extracted unerupted human third molars were used by removing the crowns and etching the exposed dentin surfaces with 35% phosphoric acid gel. After dental composite application and light curing, the teeth were then sectioned into micro-bars as the specimens for microtensile test. Student Newman Keuls (SNK) tests showed that the bonding strength of the composite restoration to peripheral dentin was significantly increased (by 64%) after 30 s plasma treatment of the dentin surfaces. These findings indicated that non-thermal atmospheric plasma technology is very promising for dental clinical applications.

Evaluation of effectiveness of Er,Cr:YSGG laser for root canal disinfection: theoretical simulation of temperature elevations in root dentin.

PubMed

Zhu, L; Tolba, M; Arola, D; Salloum, M; Meza, F

2009-07-01

Erbium, chromium: yttrium, scandium, gallium, garnet (Er,Cr:YSGG) lasers are currently being investigated for disinfecting the root canal system. Prior to using laser therapy, it is important to understand the temperature distribution and to assess thermal damage to the surrounding tissue. In this study, a theoretical simulation using the Pennes bioheat equation is conducted to evaluate how heat spreads from the canal surface using an Er,Cr:YSGG laser. Results of the investigation show that some of the proposed treatment protocols for killing bacteria in the deep dentin are ineffective, even for long heating durations. Based on the simulation, an alternative treatment protocol is identified that has improved effectiveness and is less likely to introduce collateral damage to the surrounding tissue. The alternative protocol uses 350 mW laser power with repeating laser tip movement to achieve bacterial disinfection in the deep dentin (800 microm lateral from the canal surface), while avoiding thermal damage to the surrounding tissue (T<47 degrees C). The alternative treatment protocol has the potential to not only achieve bacterial disinfection of deep dentin but also shorten the treatment time, thereby minimizing potential patient discomfort during laser procedures.

The role of erosion, abrasion and attrition in tooth wear.

PubMed

Barbour, Michele E; Rees, Gareth D

2006-01-01

There is increasing clinical awareness of erosion of enamel and dentine by dietary acids and the consequent increased susceptibility to physical wear. Enamel erosion is characterized by acid-mediated surface softening that, if unchecked, will progress to irreversible loss of surface tissue, potentially exposing the underlying dentine. In comparison, dentine erosion is less well understood as the composition and microstructure are more heterogeneous. Factors which affect the erosive potential of a solution include pH, titratable acidity, common ion concentrations, and frequency and method of exposure. Abrasion and attrition are sources of physical wear and are commonly associated with tooth brushing and tooth-to-tooth contact, respectively. A combination of erosion and abrasion or attrition exacerbates wear; however, further research is required to understand the role of fluoride in protecting mineralized tissues from such processes. Abrasive wear may be seen in a wide range of patients, whereas attritive loss is usually seen in individuals with bruxism. Wear processes are implicated in the development of dentine hypersensitivity. Saliva confers the major protective function against wear due to its role in pellicle formation, buffering, acid clearance, and hard tissue remineralization. This review focuses on the physiochemical factors impacting tooth wear.

Prevention of root caries with dentin adhesives.

PubMed

Grogono, A L; Mayo, J A

1994-04-01

This in vitro investigation determined the feasibility of using dentin adhesives to protect root surfaces against caries. The roots of 22 recently extracted human teeth were all painted with a protective lacquer leaving two unprotected small windows. On each specimen, one window (control) was left untreated and the other window (experimental) was treated using a dentin adhesive (Scotchbond Multi-Purpose). The roots were then immersed in an in vitro acetate/calcium/phosphate demineralization model at pH 4.3. After 70 days, the samples were removed and sectioned through the windows. The undecalcified ground sections were examined under transmitted and polarized light. Lesions characteristic of natural root caries were seen in the untreated control windows. No such lesions were apparent in the experimental windows. The results of this preliminary study suggest that dentin adhesives may provide protection against root caries.

Toothbrushing abrasion susceptibility of enamel and dentin bleached with calcium-supplemented hydrogen peroxide gel.

PubMed

Borges, A B; Santos, L F T F; Augusto, M G; Bonfiette, D; Hara, A T; Torres, C R G

2016-06-01

The objective of this study was to evaluate enamel and dentin susceptibility to toothbrushing abrasion, after bleaching with 7.5% hydrogen peroxide (HP) gel supplemented or not with 0.5% calcium gluconate (Ca). Toothbrushing was performed immediately and 1h after bleaching, with two suspensions (high and low abrasivity). Bovine enamel and dentin specimens were divided into 12 groups (n=10) according to the bleaching gel (with and without Ca), slurry abrasivity (high or low) and elapsed time after bleaching (immediately and after 1h). As control, a group was not bleached, but abraded. The treatment cycle (7 d) consisted of bleaching (1h) and toothbrushing (135 strokes/day) immediatelly or after 1h of artificial saliva exposure. Surface roughness and surface loss (μm) were measured by profilometry and analysed by three-way ANOVA (5%). Surface roughness means were significantly influenced by slurry abrasivity (p<0.0001). For enamel loss, significant triple interaction was observed (p<0.0001). HP-bleached groups and immediately brushed with high-abrasive slurry exhibited increased loss (1.41±0.14) compared to other groups (μm). Control and HP+Ca-bleached groups brushed after 1h with low abrasive slurry presented the lowest loss (0.21±0.03/0.27±0.02). For dentin loss, significant interaction was observed for bleaching and interval factors (p<0.001). 7.5%HP-bleached groups and immediately brushed showed significantly higher loss (8.71±2.45) than the other groups. It was concluded that surface roughness increased when high abrasive was used, independently of bleaching. 7.5%HP increased enamel and dentin loss, mainly with high abrasive slurries. Calcium supplementation of bleaching gel reduced surface loss. Additionally, in order to minimize tooth wear susceptibility, it is recommended to delay brushing after bleaching. After bleaching gel application, postponing toothbrushing is recommended, as well as brushing with low abrasive dentifrices. Additionally, supplementation of hydrogen peroxide gel with calcium-based remineralizing agent potentially reduces tooth loss after abrasion. Copyright © 2016 Elsevier Ltd. All rights reserved.

Ions-modified nanoparticles affect functional remineralization and energy dissipation through the resin-dentin interface.

PubMed

Toledano, Manuel; Osorio, Raquel; Osorio, Estrella; Medina-Castillo, Antonio Luis; Toledano-Osorio, Manuel; Aguilera, Fátima S

2017-04-01

The aim of this study was to evaluate changes in the mechanical and chemical behavior, and bonding ability at dentin interfaces infiltrated with polymeric nanoparticlesstandard deviations and modes of failure are (NPs) prior to resin application. Dentin surfaces were treated with 37% phosphoric acid followed by application of an ethanol suspension of NPs, Zn-NPs or Ca-NPs followed by the application of an adhesive, Single Bond (SB). Bonded interfaces were stored for 24h, submitted to microtensile bond strength test, and evaluated by scanning electron microscopy. After 24h and 21 d of storage, the whole resin-dentin interface adhesive was evaluated using a Nano-DMA. Complex modulus, storage modulus and tan delta (δ) were assessed. AFM imaging and Raman analysis were performed. Bond strength was not affected by NPs infiltration. After 21 d of storage, tan δ generally decreased at Zn-NPs/resin-dentin interface, and augmented when Ca-NPs or non-doped NPs were used. When both Zn-NPs and Ca-NPs were employed, the storage modulus and complex modulus decreased, though both moduli increased at the adhesive and at peritubular dentin after Zn-NPs infiltration. The phosphate and the carbonate peaks, and carbonate substitution, augmented more at interfaces promoted with Ca-NPs than with Zn-NPs after 21 d of storage, but crystallinity did not differ at created interfaces with both ions-doped NPs. Crosslinking of collagen and the secondary structure of collagen improved with Zn-NPs resin-dentin infiltration. Ca-NPs-resin dentin infiltration produced a favorable dissipation of energy with minimal stress concentration trough the crystalline remineralized resin-dentin interface, causing minor damage at this structure. Copyright © 2017 Elsevier Ltd. All rights reserved.

Influence of various bonding techniques on the fracture strength of thin CAD/CAM-fabricated occlusal glass-ceramic veneers.

PubMed

Yazigi, Christine; Kern, Matthias; Chaar, Mohamed Sad

2017-11-01

To evaluate the efficiency of immediate dentin sealing and the effects of different bonding protocols on the fracture strength of CAD/CAM occlusal veneers bonded to exposed dentin. Ninety-six extracted maxillary premolars were initially divided into three main groups with 32 specimens each: without immediate dentin sealing, immediate dentin sealing/total etching and immediate dentin sealing/selective etching. Teeth were identically prepared in the dentin to receive occlusal veneers of 0.8mm thickness, milled from lithium disilicate ceramic blocks (IPS e.max CAD). Each main group was later subdivided, according to the pre-cementation surface etching protocol (total/selective), into two subgroups with 16 specimens each. All restorations were adhesively bonded using a resin cement (Variolink Esthetic). Half of the specimens of each subgroup were subjected to thermo-dynamic loading in a chewing simulator with 1,200,000 cycles at 10kg load. The other half and the surviving specimens were subjected to quasi-static loading until failure. Statistical analysis was performed using three-way ANOVA and Tukey's post-hoc tests. All specimens except one survived the artificial aging. A significantly higher fracture strength of restorations (p ≤ 0.001) was obtained when immediate dentin sealing was followed regardless of the etching method with values ranging from a minimum of 1122 ± 336N to a maximum of 1853 ± 333N. Neither the pre-cementation treatment nor the artificial aging had a statistical significant effect on the fracture strength. Immediate dentin sealing protocol is recommended whenever dentin is exposed during the preparation for thin glass-ceramic occlusal veneers. Copyright © 2017 Elsevier Ltd. All rights reserved.

Imperfect hybrid layers created by an aggressive one-step self-etch adhesive in primary dentin are amendable to biomimetic remineralization in vitro

PubMed Central

Kim, Jongryul; Vaughn, Ryan M.; Gu, Lisha; Rockman, Roy A.; Arola, Dwayne D.; Schafer, Tara E.; Choi, Kyungkyu; Pashley, David H.; Tay, Franklin R.

2009-01-01

Degradation of hybrid layers created in primary dentin occurs as early as 6 months in vivo. Biomimetic remineralization utilizes “bottom-up” nanotechnology principles for interfibrillar and intrafibrillar remineralization of collagen matrices. This study examined whether imperfect hybrid layers created in primary dentin can be remineralized. Coronal dentin surfaces were prepared from extracted primary molars and bonded using Adper Prompt L-Pop and a composite. One millimeter-thick specimen slabs of the resin-dentin interface were immersed in a Portland cement-based remineralization medium that contained two biomimetic analogs to mimic the sequestration and templating functions of dentin noncollagenous proteins. Specimens were retrieved after 1–6 months. Confocal laser scanning microscopy was employed for evaluating the permeability of hybrid layers to Rhodamine B. Transmission electron microscopy was used to examine the status of remineralization within hybrid layers. Remineralization at different locations of the hybrid layers corresponded with quenching of fluorescence within similar locations of those hybrid layers. Remineralization was predominantly intrafibrillar in nature as interfibrillar spaces were filled with adhesive resin. Biomimetic remineralization of imperfect hybrid layers in primary human dentin is a potential means for preserving bond integrity. The success of the current proof-of-concept, laterally-diffusing remineralization protocol warrants development of a clinically-applicable biomimetic remineralization delivery system. PMID:19768792

Evaluation of ex vivo effectiveness of commercial desensitizing dentifrices

PubMed Central

Mockdeci, Hanny; Polonini, Hudson; Granato, Ana-Paula; Raposo, Nádia; Chaves, Maria-das Graças

2017-01-01

Background Dentin hypersensitivity is a short, severe pain with fast onset. Therapy aims to either prevent or decrease neural transmission or physically occlude the dentinal tubules. This study aimed to evaluate the effectiveness of commercial desensitizing dentifrice by means of an ex vivo method. Material and Methods Samples (n=8 lower human premolars for each group) were randomly allocated into: G1- brushing with Colgate®Sensitive Pro-Relief; G2- brushing with Sensodyne®Rapid Relief; G3- brushing with Sensodyne®Repair & Protect; and G4- brushing with Colgate®Maximum Cavity Protection. The test bodies were submitted to simulated toothbrushing and dentifrices were analyzed regarding their hydrodynamic size, polydispersity index (PI) and zeta potential. Specimens were evaluated using: scanning electron microscopy (SEM); spectroscopy energy dispersive X-ray (EDS); and profilometry. A qualitative analysis of the photomicrographs and topographies was performed. Results The dentifrices showed statistical similar physical and chemical characteristics. They also demonstrated obliteration of dentinal tubules when micrographs were observed. Regarding the chemical elements present in the dentin samples, there was a statistically significant difference between the control and experimental surfaces in the four groups. Conclusions Joint data analysis shows that the desensitizing dentifrice showed better results with regards to the obliteration of dentinal tubules compared to positive and negative controls. Key words:Dentin hypersensitivity, dentin desensitizing agents, toothpastes. PMID:28469813

Enamel and dentine demineralization by a combination of starch and sucrose in a biofilm - caries model.

PubMed

Botelho, Juliana Nunes; Villegas-Salinas, Mario; Troncoso-Gajardo, Pía; Giacaman, Rodrigo Andrés; Cury, Jaime Aparecido

2016-05-20

Sucrose is the most cariogenic dietary carbohydrate and starch is considered non-cariogenic for enamel and moderately cariogenic for dentine. However, the cariogenicity of the combination of starch and sucrose remains unclear. The aim of this study was to evaluate the effect of this combination on Streptococcus mutans biofilm composition and enamel and dentine demineralization. Biofilms of S. mutans UA159 were grown on saliva-coated enamel and dentine slabs in culture medium containing 10% saliva. They were exposed (8 times/day) to one of the following treatments: 0.9% NaCl (negative control), 1% starch, 10% sucrose, or 1% starch and 10% sucrose (starch + sucrose). To simulate the effect of human salivary amylase on the starch metabolization, the biofilms were pretreated with saliva before each treatment and saliva was also added to the culture medium. Acidogenicity of the biofilm was estimated by evaluating (2 times/day) the culture medium pH. After 4 (dentine) or 5 (enamel) days of growth, biofilms (n = 9) were individually collected, and the biomass, viable microorganism count, and polysaccharide content were quantified. Dentine and enamel demineralization was assessed by determining the percentage of surface hardness loss. Biofilms exposed to starch + sucrose were more acidogenic and caused higher demineralization (p < 0.0001) on either enamel or dentine than those exposed to each carbohydrate alone. The findings suggest that starch increases the cariogenic potential of sucrose.

Violet and blue light-induced green fluorescence emissions from dental caries.

PubMed

Shakibaie, F; Walsh, L J

2016-12-01

The objective of this laboratory study was to compare violet and visible blue LED light-elicited green fluorescence emissions from enamel and dentine in healthy or carious states. Microscopic digital photography was undertaken using violet and blue LED illumination (405 nm and 455 nm wavelengths) of tooth surfaces, which were photographed through a custom-made stack of green compensating filters which removed the excitation light and allowed green fluorescence emissions to pass. Green channel pixel data were analysed. Dry sound enamel and sound root surfaces showed strong green fluorescence when excited by violet or blue lights. Regions of cavitated dental caries gave lower green fluorescence, and this was similar whether the dentine in the lesions was the same colour as normal dentine or was darkly coloured. The presence of saliva on the surface did not significantly change the green fluorescence, while the presence of blood diluted in saliva depressed green fluorescence. Using violet or blue illumination in combination with green compensating filters could potentially aid in the assessment of areas of mineral loss. © 2016 Australian Dental Association.

Effect of saliva contamination and cleansing solutions on the bond strengths of self-etch adhesives to dentin.

PubMed

Sheikh, Huma; Heymann, Harald O; Swift, Edward J; Ziemiecki, Thomas L; Ritter, André V

2010-12-01

This study determined the effect of saliva contamination and cleansing solutions on microtensile bond strengths of self-etch adhesives to dentin. Seventy-five human molars were ground flat to expose mid-coronal dentin and randomly assigned to five groups (N = 15): no contamination, saliva contamination without cleansing, saliva and cleansing with water, saliva and cleansing with 2% chlorhexidine, and saliva and cleansing with 5% sodium hypochlorite. One-third of the specimens in each group of 15 were bonded with Adper Prompt L-Pop (all-in-one self-etch adhesive; 3M ESPE, St. Paul, MN, USA), one-third with Adper Easy Bond (all-in-one self-etch adhesive; 3M ESPE), and one-third with Clearfil SE Bond (self-etch primer system; Kuraray America, New York, NY, USA). Specimens were restored with composite and processed for microtensile bond strength testing (5-6 rods/tooth). Mean bond strengths ranged from 17.3 MPa for Adper Prompt L-Pop after water cleansing to 69.3 MPa for Clearfil SE Bond after water cleansing. For all three adhesives, there was no statistically significant difference in bond strengths between the saliva contaminated group, the cleansing groups, and the no contamination groups. Neither saliva nor the cleansing solutions adversely affected bond strengths of the self-etch adhesive systems. © 2010, COPYRIGHT THE AUTHORS. JOURNAL COMPILATION © 2010, WILEY PERIODICALS, INC.

Comparative bonding ability to dentin of a universal adhesive system and monomer conversion as functions of extended light curing times and storage.

PubMed

Sampaio, Paula Costa Pinheiro; Kruly, Paula de Castro; Ribeiro, Clara Cabral; Hilgert, Leandro Augusto; Pereira, Patrícia Nóbrega Rodrigues; Scaffa, Polliana Mendes Candia; Di Hipólito, Vinicius; D'Alpino, Paulo Henrique Perlatti; Garcia, Fernanda Cristina Pimentel

2017-11-01

The purpose of this in vitro study was to evaluate the bonding ability and monomer conversion of a universal adhesive system applied to dentin as functions of different curing times and storage. The results were compared among a variety of commercial adhesives. Flat superficial dentin surfaces were exposed on human molars and assigned into one of the following adhesives (n = 15): total-etch Adper Single Bond 2 (SB) and Optibond Solo Plus (OS), self-etch Optibond All in One (OA) and Clearfil SE Bond (CSE), and Scotchbond Universal Adhesive in self-etch mode (SU). The adhesives were applied following the manufacturers' instructions and cured for 10, 20, or 40s. Specimens were processed for the microtensile bond strength (µTBS) test in accordance with the non-trimming technique and tested after 24h and 2 years. The fractured specimens were classified under scanning electron microscopy (SEM). Infrared (IR) spectra were obtained and monomer conversion (%) was calculated by comparing the aliphatic-to-aromatic IR absorption peak ratio before and after polymerization (n=5). Data were analyzed by 2-way ANOVA/Tukey's tests (α = 0.05). At 24-h evaluation, OA and CSE presented similar bond strength means irrespective of the curing time, whereas SB and SU exhibited significantly higher means when cured for 40s as did OS when cured for 20 or 40s (p < 0.05). At 2-year evaluation, only OA exhibited significantly higher bond strength when cured for 20 and 40s (p < 0.05). When the evaluation times were compared, OA also exhibited the same bonding ability when cured for longer periods of time (20 and 40s). All of the adhesives tested exhibited significantly lower monomer conversion when photoactivated according to the manufacturers' instructions (10s). Higher monomer conversions obtained with longer light exposure allow only higher immediate bond strength for most of the adhesives tested. After 2-year storage, only the self-etching adhesive Optibond All-In-One exhibited the same bonding ability when cured for longer periods of time. Copyright © 2017 Elsevier Ltd. All rights reserved.

Effect of preheating of low shrinking resin composite on intrapulpal temperature and microtensile bond strength to dentin

PubMed Central

El-Deeb, Heba A.; Abd El-Aziz, Sara; Mobarak, Enas H.

2014-01-01

The effect of preheating of the silorane-based resin composite on intrapulpal temperature (IPT) and dentin microtensile bond strength (μTBS) was evaluated. For the IPT, teeth (n = 15) were sectioned to obtain discs of 0.5 mm thickness (2 discs/tooth). The discs were divided into three groups (n = 10/group) according to the temperature of the Filtek LS™ silorane-based resin composite during its placement, either at room temperature (23 ± 1 °C) or preheated to 54 °C or 68 °C using a commercial Calset™ device. Discs were subjected to a simulated intrapulpal pressure (IPP) and placed inside a specially constructed incubator adjusted at 37 °C. IPT was measured before, during and after placement and curing of the resin composite using K-type thermocouple. For μTBS testing, flat occlusal middentin surfaces (n = 24) were obtained. P90 System Adhesive was applied according to manufacturer’s instructions then Filtek LS was placed at the tested temperatures (n = 6). Restorative procedures were done while the specimens were connected to IPP simulation. IPP was maintained and the specimens were immersed in artificial saliva at 37 °C for 24 h before testing. Each specimen was sectioned into sticks (0.9 ± 0.01 mm2). The sticks (24/group) were subjected to μTBS test and their modes of failure were determined using scanning electron microscope (SEM). For both preheated groups, IPT increased equally by 1.5–2 °C upon application of the composite. After light curing, IPT increased by 4–5 °C in all tested groups. Nevertheless, the IPT of the preheated groups required a longer time to return to the baseline temperature. One-way ANOVA revealed no significant difference between the μTBS values of all groups. SEM revealed predominately mixed mode of failure. Preheating of silorane-based resin composite increased the IPT but not to the critical level and had no effect on dentin μTBS. PMID:26257945

Bond Strength of a Novel One Bottle Multi-mode Adhesive to Human Dentin After Six Months of Storage

PubMed Central

Manfroi, Fernanda Borguetti; Marcondes, Maurem Leitão; Somacal, Deise Caren; Borges, Gilberto Antonio; Júnior, Luiz Henrique Burnett; Spohr, Ana Maria

2016-01-01

Objective: The aim of the study was to evaluate the microtensile bond strength (µTBS) of Scotchbond Universal to dentin using the etch-and-rinse or the self-etch technique after 24 h and 6 months of storage. Materials and Methods: Flat dentin surfaces were obtained in 24 third molars. The teeth were divided into four groups: G1 – Scotchbond Universal applied in the etch-and-rinse mode; G2 – Scotchbond Universal applied in the self-etch mode; G3 – Scotchbond Multi-Purpose; G4 – Clearfil SE Bond. A block of composite was built on the adhesive area. The tooth/resin sets were cut parallel to the long axis to obtain 40 beams (~0.8 mm2) for each group. Twenty specimens were immediately submitted to the µTBS test, and the remaining 20 were stored in water for 6 months. Failures and the adhesive interface were analyzed by SEM. Results: According to two-way ANOVA, the interaction between adhesive and storage time was significant (p=0.015).The µTBS (MPa) means were the following: 24 h – G1 (39.37±10.82), G2 (31.02±13.76), G3 (35.09±14.03) and G4 (35.84±11.06); 6 months – G1 (36.99±8.78), G2 (40.58±8.07), G3 (32.44±6.07) and G4 (41.75±8.25). Most failures were mixed. Evidence of hybrid layer and numerous resin tags were noted for Scotchbond Universal applied with the etch-and-rinse mode and Scotchbond Multi-Purpose. A thinner hybrid layer and fewer resin tags were noted for Scotchbond Universal applied in the self-etch mode and Clearfil SE Bond. Conclusion: The results indicate that the µTBS for Scotchbond Universal is comparable to the gold-standard adhesives. Scotchbond Universal applied in the self-etch mode and Clearfil SE Bond revealed higher bond stability compared to the etch-and-rinse mode. PMID:27347230

Efficacy of Modified Bioactive Glass for Dentin Remineralization and Obstruction of Dentinal Tubules.

PubMed

Saffarpour, Mahshid; Mohammadi, Maryam; Tahriri, Mohammadreza; Zakerzadeh, Azadeh

2017-07-01

This study assessed the efficacy of modified bioactive glass (MBG) for dentin remineralization and obstruction of dentinal tubules. Thirty-six dentin discs were made from 20 third molars and were stored in 12% lactic acid solution for two weeks to induce demineralization. The samples were divided into three groups (n=12): 1- BG, 2- BG modified with 5% strontium (Sr) and 3- BG modified with 10% Sr. After applying the BG, the samples were stored in artificial saliva for 7, 14 and 21 days. Attenuated Total Reflection-Fourier Transform Infrared Spectroscopy (ATR-FTIR), X-ray Diffraction (XRD) analysis, Scanning Electron Microscopy (SEM), and Energy-Dispersive X-ray (EDX) analysis were used to assess remineralization. Also, 6 dentin discs were divided into three groups of BG, BG modified with 5% Sr and BG modified with 10% Sr, to examine tubular occlusion. The discs were etched using 0.5M of EDTA for two minutes and were stored in artificial saliva for 7 days. Changes in dentin surface morphology were evaluated under SEM. Group 3 showed high rates of remineralization at days 7 and 14, although the rate decreased at day 21. Group 2 exhibited high rates of remineralization at days 7, 14 and 21. Dentinal tubules were partially occluded by BG and BG modified with 5% Sr, while they were almost completely obstructed after the use of BG modified with 10% Sr. Strontium increases remineralization. Addition of 10% Sr to BG enhances apatite formation; however, the apatite dissolves over time. Addition of 5% Sr to BG stabilizes the apatite lattice and increases the remineralization.

Clinical status of ten dentin adhesive systems.

PubMed

Van Meerbeek, B; Peumans, M; Verschueren, M; Gladys, S; Braem, M; Lambrechts, P; Vanherle, G

1994-11-01

Laboratory testing of dentin adhesive systems still requires corroboration by long-term clinical trials for their ultimate clinical effectiveness to be validated. The objective of this clinical investigation was to evaluate, retrospectively, the clinical effectiveness of earlier-investigated dentin adhesive systems (Scotchbond, Gluma, Clearfil New Bond, Scotchbond 2, Tenure, and Tripton), and to compare their clinical results with those obtained with four modern total-etch adhesive systems (Bayer exp. 1 and 2, Clearfil Liner Bond System, and Scotchbond Multi-Purpose). In total, 1177 Class V cervical lesions in the teeth of 346 patients were restored following two cavity designs: In Group A, enamel was neither beveled nor intentionally etched, as per ADA guidelines; in Group B, adjacent enamel was beveled and conditioned. Clinical retention rates definitely indicated the improved clinical efficacy of the newest dentin adhesives over the earlier systems. With regard to adhesion strategy, adhesive systems that removed the smear layer and concurrently demineralized the dentin surface layer performed clinically better than systems that modified the disorderly layer of smear debris without complete removal. Hybridization by resin interdiffusion into the exposed dentinal collagen layer, combined with attachment of resin tags into the opened dentin tubules, appeared to be essential for reliable dentin bonding but might be insufficient by itself. The additional formation of an elastic bonding area as a polymerization shrinkage absorber and the use of a microfine restorative composite apparently guaranteed an efficient clinical result. The perfect one-year retention recorded for Clearfil Liner Bond System and Scotchbond Multi-Purpose must be confirmed at later recalls.

Effects of Dentin Debris on the Antimicrobial Properties of Sodium Hypochlorite and Etidronic Acid.

PubMed

Arias-Moliz, Maria Teresa; Morago, Ana; Ordinola-Zapata, Ronald; Ferrer-Luque, Carmen María; Ruiz-Linares, Matilde; Baca, Pilar

2016-05-01

The purpose of this study was to determine the influence of dentin powder on the concentration, pH, and antimicrobial activity of sodium hypochlorite (NaOCl) alone and combined with etidronic acid (HEBP). Biofilms of Enterococcus faecalis were grown on the surface of dentin blocks for 5 days and then exposed to 1% and 2.5% NaOCl alone or combined with 9% HEBP for 3 minutes in the absence and presence of dentin powder. The biovolumes of the biofilm were measured using confocal microscopy and the live/dead technique. The available chlorine and pH of the solutions were also measured. Nonparametric tests were used to determine statistical differences (P < .05). The presence of dentin powder resulted in a reduction of the free available chlorine and pH in all the irrigating solutions; 1% NaOCl lost its antimicrobial activity completely in the presence of dentin powder. The antimicrobial activity was significantly reduced in the 2.5% NaOCl and 1% NaOCl/HEBP groups, and it was not affected in the 2.5% NaOCl/HEBP group. The presence of dentin powder significantly decreased the available chlorine and antimicrobial activity of 1% NaOCl, 2.5% NaOCl, and 1% NaOCl/HEBP irrigating solutions. The antimicrobial activity of 2.5% NaOCl/HEBP was not affected by the dentin powder after a 3-minute contact time against E. faecalis biofilms. Copyright © 2016 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

In vitro photodynamic antimicrobial chemotherapy in dentine contaminated by cariogenic bacteria

NASA Astrophysics Data System (ADS)

Melo, M. A. S.; de-Paula, D. M.; Lima, J. P. M.; Borges, F. M. C.; Steiner-Oliveira, C.; Nobre-Dos-Santos, M.; Zanin, I. C. J.; Barros, E. B.; Rodrigues, L. K. A.

2010-06-01

The development of a method to ensure bacterial-free substrates without extensive cavity preparation would be highly useful to dentistry, since there is no currently available effective method for killing residual bacteria in dentinal tissue. This randomized in vitro study determined parameters for using toluidine blue O (TBO) with a light-emitting diode (LED) for dentine caries disinfection and monitored intrapulpal/periodontal temperatures during irradiation. Occlusal human dentine slabs were immersed in Streptococcus mutans culture for demineralization induction. Slabs were allocated to 10 groups ( n = 15), which were treated with 0.1 mg ml-1 TBO with 5 min of incubation time or 0.9% NaCl solution for 5, 10 or 15 min, and submitted or not to irradiation for 5, 10 or 15 min (47, 94, and 144 J/cm2). Before and after treatments, dentine samples were analyzed with regard to S. mutans counts. In whole teeth, temperature in pulp and periodontium was measured by thermocouples during irradiation. Kruskal-Wallis/Student-Newman-Keuls, and ANOVA/Tukey test were respectively utilized to compare log reductions and temperature rises between groups. Bacterial reduction was observed when dentine was exposed to both TBO and LED at all irradiation times, as well as to LED alone for 10 and 15 min. Temperature increases lower than 2°C were observed for either pulp or periodontium. Concluding, LED combined with TBO is a safe and effective approach for dentine caries disinfection. Nevertheless, additional studies should be conducted to determine the influence of the irradiation in S. mutans viability in dentinal surface/tubules.

Viscoelasticity and plasticity mechanisms of human dentin

NASA Astrophysics Data System (ADS)

Borodin, E. N.; Seyedkavoosi, S.; Zaitsev, D.; Drach, B.; Mikaelyan, K. N.; Panfilov, P. E.; Gutkin, M. Yu.; Sevostianov, I.

2018-01-01

Theoretical models of viscoelastic behavior and plastic deformation mechanisms of human dentin are considered. Using the linear viscoelasticity theory in which creep and relaxation kernels have the form of fraction-exponential functions, numerical values of instantaneous and long-time Young's moduli and other characteristics of dentin viscoelasticity under uniaxial compression are found. As dentin plastic deformation mechanisms, mutual collagen fiber sliding in the region of contact of their side surfaces, separation of these fibers from each other, and irreversible tension of some collagen fibers, are proposed. It is shown that the second mechanism activation requires a smaller stress than that for activating others. The models of plastic zones at the mode I crack tip, which correspond to these mechanisms, are studied. It is shown that the plastic zone size can increase from a few hundreds of nanometers to hundreds of micrometers with increasing applied stress.

Molecular energy dissipation in nanoscale networks of dentin matrix protein 1 is strongly dependent on ion valence

NASA Astrophysics Data System (ADS)

Adams, J.; Fantner, G. E.; Fisher, L. W.; Hansma, P. K.

2008-09-01

The fracture resistance of biomineralized tissues such as bone, dentin, and abalone is greatly enhanced through the nanoscale interactions of stiff inorganic mineral components with soft organic adhesive components. A proper understanding of the interactions that occur within the organic component, and between the organic and inorganic components, is therefore critical for a complete understanding of the mechanics of these tissues. In this paper, we use atomic force microscope (AFM) force spectroscopy and dynamic force spectroscopy to explore the effect of ionic interactions within a nanoscale system consisting of networks of dentin matrix protein 1 (DMP1) (a component of both bone and dentin organic matrix), a mica surface and an AFM tip. We find that DMP1 is capable of dissipating large amounts of energy through an ion-mediated mechanism, and that the effectiveness increases with increasing ion valence.

Quantification of peroxide ion passage in dentin, enamel, and cementum after internal bleaching with hydrogen peroxide.

PubMed

Palo, R M; Bonetti-Filho, I; Valera, M C; Camargo, C H R; Camargo, Sea; Moura-Netto, C; Pameijer, C

2012-01-01

The aim of this study was to evaluate the amount of peroxide passage from the pulp chamber to the external enamel surface during the internal bleaching technique. Fifty bovine teeth were sectioned transversally 5 mm below the cemento-enamel junction (CEJ), and the remaining part of the root was sealed with a 2-mm layer of glass ionomer cement. The external surface of the samples was coated with nail varnish, with the exception of standardized circular areas (6-mm diameter) located on the enamel, exposed dentin, or cementum surface of the tooth. The teeth were divided into three experimental groups according to exposed areas close to the CEJ and into two control groups (n=10/group), as follows: GE, enamel exposure area; GC, cementum exposed area; GD, dentin exposed area; Negative control, no presence of internal bleaching agent and uncoated surface; and Positive control, pulp chamber filled with bleaching agent and external surface totally coated with nail varnish. The pulp chamber was filled with 35% hydrogen peroxide (Opalescence Endo, Ultradent). Each sample was placed inside of individual flasks with 1000 μL of acetate buffer solution, 2 M (pH 4.5). After seven days, the buffer solution was transferred to a glass tube, in which 100 μL of leuco-crystal violet and 50 μL of horseradish peroxidase were added, producing a blue solution. The optical density of the blue solution was determined by spectrophotometer and converted into microgram equivalents of hydrogen peroxide. Data were submitted to Kruskal-Wallis and Dunn-Bonferroni tests (α=0.05). All experimental groups presented passage of peroxide to the external surface that was statistically different from that observed in the control groups. It was verified that the passage of peroxide was higher in GD than in GE (p<0.01). The GC group presented a significantly lower peroxide passage than did GD and GE (p<0.01). It can be concluded that the hydrogen peroxide placed into the pulp chamber passed through the dental hard tissues, reaching the external surface and the periodontal tissue. The cementum surface was less permeable than were the dentin and enamel surfaces.

Dental Stem Cell Migration on Pulp Ceiling Cavities Filled with MTA, Dentin Chips, or Bio-Oss

PubMed Central

Lymperi, Stefania; Taraslia, Vasiliki; Tsatsoulis, Ioannis N.; Samara, Athina; Agrafioti, Anastasia; Anastasiadou, Ema; Kontakiotis, Evangelos

2015-01-01

MTA, Bio-Oss, and dentin chips have been successfully used in endodontics. The aim of this study was to assess the adhesion and migration of dental stem cells on human pulp ceiling cavities filled with these endodontic materials in an experimental model, which mimics the clinical conditions of regenerative endodontics. Cavities were formed, by a homemade mold, on untouched third molars, filled with endodontic materials, and observed with electron microscopy. Cells were seeded on cavities' surface and their morphology and number were analysed. The phenomenon of tropism was assessed in a migration assay. All three materials demonstrated appropriate microstructures for cell attachment. Cells grew on all reagents, but they showed a differential morphology. Moreover, variations were observed when comparing cells numbers on cavity's filling versus the surrounding dentine disc. The highest number of cells was recorded on dentin chips whereas the opposite was true for Bio-Oss. This was confirmed in the migration assay where a statistically significant lower number of cells migrated towards Bio-Oss as compared to MTA and dentin chips. This study highlights that MTA and dentin chips have a greater potential compared to Bio-Oss regarding the attraction of dental stem cells and are good candidates for bioengineered pulp regeneration. PMID:26146613

Micro energy-dispersive x-ray fluorescence spectrometry study of dentin coating with nanobiomaterials

NASA Astrophysics Data System (ADS)

Soares, Luís. Eduardo Silva; Nahorny, Sídnei; Marciano, Fernanda Roberta; Zanin, Hudson; Lobo, Anderson de Oliveira

2015-06-01

New biomaterials such as multi-walled carbon nanotubes oxide/graphene oxide (MWCNTO/GO), nanohydroxyapatite (nHAp) and combination of them together or not to acidulated phosphate fluoride gel (F) have been tested as protective coating before root dentin erosion. Fourteen bovine teeth were cleaned, polished, divided into two parts (n=28) and assigned to seven groups: (Control) - without previous surface treatment; F treatment; nHAp; MWCNTO/GO; F+nHAp; F+MWCNTO/GO and F+MWCNTO/GO/nHAp composites. Each sample had two sites of pre-treatments: acid etched area and an area without treatment. After the biomaterials application, the samples were submitted to six cycles (demineralization: orange juice, 10 min; remineralization: artificial saliva, 1 h). Micro energy-dispersive X-ray fluorescence spectrometry (μ-EDXRF) mapping area analyses were performed after erosive cycling on both sites (n=84). μ-EDXRF mappings showed that artificial saliva and MWCNTO/GO/nHAp/F composite treatments produced lower dentin demineralization than in the other groups. Exposed dentin tubules allowed better interaction of nanobiomaterials than in smear layer covered dentin. Association of fluoride with other biomaterials had a positive influence on acid etched dentin. MWCNTO/GO/nHAp/F composite treatment resulted in levels of demineralization similar to the control group.

Effect of ethanol-wet bonding with hydrophobic adhesive on caries-affected dentine.

PubMed

Huang, Xueqing; Li, Li; Huang, Cui; Du, Xijin

2011-08-01

Frequently encountered in clinical practice, caries-affected dentine (CAD) is the most challenging bonding substrate. This study evaluated the effect of ethanol-wet bonding with hydrophobic adhesive to sound dentine and to CAD. In the control groups, prepared sound dentine and CAD were bonded with Adper Single Bond 2 using a traditional water-wet bonding technique. In the experimental groups, the specimens were treated as follows: Group 1, rinsed with stepwise ethanol dehydration; Group 2, immersion in 100% ethanol, three times, for 20 s each time; and Group 3, immersion in 100% ethanol for 20 s. Microtensile bond strength (μTBS) testing was used to evaluate the effects of the different protocols on bonding. The microhardness of debonded dentine surfaces was measured to ensure the presence of CAD. Interfacial nanoleakage was evaluated by field-emission scanning electron microscopy. Treatment significantly improved the μTBS in CAD in Groups 1 and 2, but had no effect on Group 3. Conversely, treatment significantly reduced the μTBS in sound dentine in Groups 2 and 3, but had no effect in Group 1. The presence of nanoleakage varied with the ethanol-wet protocol used. In conclusion, ethanol-wet bonding can potentially improve bond efficacy to CAD when an appropriate protocol is used. © 2011 Eur J Oral Sci.

[The effects of the processing technic on dentinal adhesion].

PubMed

Krejci, I; Lutz, F; Perisic, U

1992-01-01

In this in vitro study, the effect of application techniques on marginal adaptation of thermal cycled class V restorations restored with an actual dentinal adhesive were quantitated using SEM and dye penetration. Under optimal application conditions, excellent results were generated: though a simple bulk insertion technique was used, no difference was found between enamel and dentin margins before and after thermal loading. On the other hand, contamination of the bonding agent with saliva before composite resin insertion dramatically decreased the percentage of "excellent margin" in dentin and in enamel. Similar effects were found after protecting the bonding agent with an insulating gel. No improvement in marginal adaptation was found after reapplication of the bonding agent. The class V inlay did not show better results than the direct filling technique. However, postcured inlays performed better than their non-postcured counterparts. Without etching enamel with a phosphoric acid gel, but by priming its surface, approximately 80% of "excellent margin" were found in enamel before thermal cycling. This percentage decreased significantly after thermal loading. Restorations totally confined to dentin had slightly lower percentages of "excellent margin" than the mixed class V fillings. The results of this study indicated, that by using dentinal adhesives, little changes and deviations from the correct procedure result in significant alterations in marginal adaptation.

Evaluation of dentin tubule occlusion after laser irradiation and desensitizing agent application.

PubMed

Kim, Min-Ho; Kim, Ryan Jin-Young; Lee, Woo-Cheol; Lee, In-Bog

2015-10-01

To evaluate the effects of lasers (Nd:YAG and Er:YAG) and of topical desensitizing agents on dentin tubule occlusion by measuring real-time dentin fluid flow (DFF). 32 molars were prepared with V-shape cavity at the cervical area, acid-etched, water rinsed, blotted dry, and treated with (1) Nd:YAG laser; (2) Er:YAG laser; (3) SuperSeal, a desensitizing agent; (4) ClinproXT, a resin-modified glass-ionomer (RMGI) varnish (n = 8 each). A real-time fluid flow measuring instrument (nano-Flow) was used to measure the DFF throughout the procedures. The DFF rates before and after the treatment were compared. Moreover, the surface topography of dentin tubules after each desensitizing method was examined using SEM. DFF varied among the groups. The DFF rate was significantly reduced after laser irradiation/application of the desensitizing agents (P < 0.05). ClinproXT showed the greatest reduction of DFF rate (71.9%), followed by the SuperSeal (34.8%) and laser groups (P< 0.05). However, there was no significant difference between the Nd:YAG (24.1%) and Er:YAG (20.6%) groups (P > 0.05). In SEM images, narrowed dentin tubules were observed in both lased groups and SuperSeal group. In the ClinproXT group, the occluded dentin tubules by the RMGI covering were observed.

Fluoride-dependent formation of mineralized layers in bovine dentin during demineralization in vitro.

PubMed

Damen, J J; Buijs, M J; ten Cate, J M

1998-01-01

Demineralization of dentin in the presence of fluoride produces lesions with a mineralized surface layer which becomes thicker and more mineralized with higher fluoride concentrations whereas the lesion depth is hardly affected. The aim of this study was to investigate the effects of the time of fluoride treatment and the amount of fluoride taken up on the properties of the mineralized layer. Discs of bovine dentin embedded in methylmethacrylate with one surface exposed were demineralized in 50 mM acetic acid, 2.2 mM CaCl2, 2.2 mM KH2PO4, pH 5.0. At the start and/or later during the demineralization period, the specimens were incubated individually for 1 or 2 days in 10 ml of the same demineralization solution supplemented with 0.5, 2.0 or 5.0 ppm fluoride, which was then assessed for changes in calcium and fluoride concentrations. After 2, 5 and 8 days, specimens were sectioned for microradiographic analysis so as to follow development of the lesions and the mineralized layers. The results were the following: While demineralization with fluoride present at the first day led to the formation of a surface layer, fluoride present only at a later day produced a subsurface layer, not at the lesion front but closer to the surface. This layer resulted from (re)precipitation and not from preservation of the original mineral. The 'integrated mineral content' of the surface layer increased linearly with the uptake of fluoride, which resulted in an apparent fluorapatite content of about 20 vol%. The profiles of the surface layers remained unchanged during continued demineralization in the absence of fluoride. It was concluded that in the presence of fluoride mineral loss is reduced as a result of the reprecipitation of dissolved mineral ions as a layer of fluoride-enriched apatite. This layer does not offer protection of underlying dentin against continued demineralization.

Effect of different diode laser wavelengths on root dentin decontamination infected with Enterococcus faecalis.

PubMed

Borges, Caroline Cristina; Estrela, Carlos; Lopes, Fabiane Carneiro; Palma-Dibb, Regina Guenka; Pecora, Jesus Djalma; De Araújo Estrela, Cyntia Rodrigues; Sousa-Neto, Manoel Damião de

2017-11-01

The objective of this study was to evaluate the antibacterial effect and the ultrastructural alterations of diode laser with different wavelengths (808nm and 970nm) and its association with irrigating solutions (2.5% sodium hypochlorite and 2% chlorhexidine) in root dentin contaminated by a five days biofilm. Thirteen uniradicular teeth were sectioned into 100 dentin intraradicular blocks. Initially, the blocks were immersed for 5min in 17% EDTA and washed with distilled water for 5min, then samples were sterilized for 30min at 120°C. The dentin samples were inoculated with 0.1mL of E. faecalis suspension in 5mL BHI (Brain Heart Infusion) and incubated at 37°C for 5days. After contamination, the specimens were distributed into ten groups (n=10) according to surface treatment: GI - 5mL NaOCl 2.5%, GII - 5mL NaOCl 2.5%+808nm diode (0.1W for 20s), GIII - 5mL NaOCl 2.5%+970nm diode (0.5W for 4s), GIV - 808nm diode (0.1W for 20s), GV - 970nm diode (0.5W for 4s), GVI - CHX 2%, GVII - CHX 2%+808nm diode (0.1W for 20s), GVIII - CHX 2%+970nm diode (0.5W for 4s), GIX - positive control and GX - negative control. Bacterial growth was analyzed by turbidity and optical density of the growth medium by spectrophotometry (nm). Then, the specimens were processed for analysis ultrastructural changes of the dentin surface by SEM. The data was subject to the One-way ANOVA test. GI (77.5±12.1), GII (72.5±12.2), GIII (68.7±8.7), GV (68.3±8.7), GVI (62.0±5.5) and GVII (67.5±3.3) were statistically similar and statistically different from GIV (58.8±25.0), GVIII (59.2±4.0) and control groups (p<0.05). SEM analysis showed a modified amorphous organic matrix layer with melted intertubular dentin when dentin samples were irradiated with 970nm diode laser; erosion of the intertubular dentin in blocks submitted to 808nm diode laser irradiation; and an increased erosion of the intertubular dentin when 2.5% NaOCl was associated to the different wavelengths lasers. All the therapeutic protocols were able to reduce the bacterial contingent in dentin blocks, and the association of diode laser and solutions did not significantly improve the reduction of the bacterial contingent. Copyright © 2017 Elsevier B.V. All rights reserved.

EFFECT OF AN ADDITIONAL HYDROPHILIC VERSUS HYDROPHOBIC COAT ON THE QUALITY OF DENTINAL SEALING PROVIDED BY TWO-STEP ETCH-AND-RINSE ADHESIVES

PubMed Central

Silva, Safira Marques de Andrade; Carrilho, Marcela Rocha de Oliveira; Marquezini, Luiz; Garcia, Fernanda Cristina Pimentel; Manso, Adriana Pigozzo; Alves, Marcelo Corrêa; de Carvalho, Ricardo Marins

2009-01-01

Objective: To test the hypothesis that the quality of the dentinal sealing provided by two-step etch-and-rinse adhesives cannot be altered by the addition of an extra layer of the respective adhesive or the application of a more hydrophobic, non-solvated resin. Material and Methods: full-crown preparations were acid-etched with phosphoric acid for 15 s and bonded with Adper Single Bond (3M ESPE), Excite DSC (Ivoclar/Vivadent) or Prime & Bond NT (Dentsply). The adhesives were used according to the manufacturers' instructions (control groups) or after application to dentin they were a) covered with an extra coat of each respective system or b) coated with a non-solvated bonding agent (Adper Scotchbond Multi-Purpose Adhesive, 3M ESPE). Fluid flow rate was measured before and after dentin surfaces were acid-etched and bonded with adhesives. Results: None of the adhesives or experimental treatments was capable to block completely the fluid transudation across the treated dentin. Application of an extra coat of the adhesive did not reduce the fluid flow rate of adhesive-bonded dentin (p>0.05). Conversely, the application of a more hydrophobic non-solvated resin resulted in significant reductions in the fluid flow rate (p<0.05) for all tested adhesives. Conclusions: The quality of the dentinal sealing provided by etch-and-rinse adhesives can be significantly improved by the application of a more hydrophobic, non-solvated bonding agent. PMID:19466248

Influence of five home whitening gels and a remineralizing gel on the enamel and dentin ultrastructure and hardness.

PubMed

Pinheiro, Helena Burlamaqui; Cardoso, Paulo Eduardo Capel

2011-06-01

To investigate the influence of calcium phosphate enhanced home whitening agents on human enamel and dentin surface microhardness and ultramorphology. Five intact molars crowns were used for ultrastructural analysis and five for microhardness test. Each resulting coronal structure was cut in slices. After measuring baseline Knoop Hardness Number (KHN) of the enamel and dentin, the slices were divided into six experimental groups and one control (n= 5). G1= 15% carbamide peroxide (CP); G2= 16% CP; G3= Ca and PO4 (remineralizing agent); G4= 16% CP with Ca and PO4; G5= 7.5% hydrogen peroxide (HP) with Ca and PO4; G6=7.5% HP with Ca. After each daily session of treatment, specimens were stored in distilled water (37 degrees C) until the next session. Products were applied for 2 weeks, according to manufacturers' instructions. Additional KHN weredetermined. Conventional whitening agents (G1; G2) and the gel with Ca (G6), caused KHN decrease (P< 0.05).The remineralizing and whitening agents with Ca and PO4 (G3; G4; G5) did not change KHN. A change of morphology was observed on enamel and dentin surfaces in G1; G2; G5.

Periodontal ligament stem/progenitor cells with protein-releasing scaffolds for cementum formation and integration on dentin surface.

PubMed

Cho, Hankyu; Tarafder, Solaiman; Fogge, Michael; Kao, Kristy; Lee, Chang H

2016-11-01

Purpose/Aim: Cementogenesis is a critical step in periodontal tissue regeneration given the essential role of cementum in anchoring teeth to the alveolar bone. This study is designed to achieve integrated cementum formation on the root surfaces of human teeth using growth factor-releasing scaffolds with periodontal ligament stem/progenitor cells (PDLSCs). Human PDLSCs were sorted by CD146 expression, and characterized using CFU-F assay and induced multi-lineage differentiation. Polycaprolactone scaffolds were fabricated using 3D printing, embedded with poly(lactic-co-glycolic acids) (PLGA) microspheres encapsulating connective tissue growth factor (CTGF), bone morphogenetic protein-2 (BMP-2), or bone morphogenetic protein-7 (BMP-7). After removing cementum on human tooth roots, PDLSC-seeded scaffolds were placed on the exposed dentin surface. After 6-week culture with cementogenic/osteogenic medium, cementum formation and integration were evaluated by histomorphometric analysis, immunofluorescence, and qRT-PCR. Periodontal ligament (PDL) cells sorted by CD146 and single-cell clones show a superior clonogenecity and multipotency as compared with heterogeneous populations. After 6 weeks, all the growth factor-delivered groups showed resurfacing of dentin with a newly formed cementum-like layer as compared with control. BMP-2 and BMP-7 showed de novo formation of tissue layers significantly thicker than all the other groups, whereas CTGF and BMP-7 resulted in significantly improved integration on the dentin surface. The de novo mineralized tissue layer seen in BMP-7-treated samples expressed cementum matrix protein 1 (CEMP1). Consistently, BMP-7 showed a significant increase in CEMP1 mRNA expression. Our findings represent important progress in stem cell-based cementum regeneration as an essential part of periodontium regeneration.

Self-induced vomiting and dental erosion--a clinical study.

PubMed

Uhlen, Marte-Mari; Tveit, Anne Bjørg; Stenhagen, Kjersti Refsholt; Mulic, Aida

2014-07-29

In individuals suffering from eating disorders (ED) characterized by vomiting (e.g. bulimia nervosa), the gastric juice regularly reaches the oral cavity, causing a possible risk of dental erosion. This study aimed to assess the occurrence, distribution and severity of dental erosions in a group of Norwegian patients experiencing self-induced vomiting (SIV). The individuals included in the study were all undergoing treatment at clinics for eating disorders and were referred to a university dental clinic for examinations. One calibrated clinician registered erosions using the Visual Erosion Dental Examination (VEDE) system. Of 72 referred patients, 66 (63 females and three males, mean age 27.7 years) were or had been experiencing SIV (mean duration 10.6 years; range: 3 - 32 years), and were therefore included in the study. Dental erosions were found in 46 individuals (69.7%), 19 had enamel lesions only, while 27 had both enamel and dentine lesions. Ten or more teeth were affected in 26.1% of those with erosions, and 9% had ≥10 teeth with dentine lesions. Of the erosions, 41.6% were found on palatal/lingual surfaces, 36.6% on occlusal surfaces and 21.8% on buccal surfaces. Dentine lesions were most often found on lower first molars, while upper central incisors showed enamel lesions most frequently. The majority of the erosive lesions (48.6%) were found in those with the longest illness period, and 71.7% of the lesions extending into dentine were also found in this group. However, despite suffering from SIV for up to 32 years, 30.3% of the individuals showed no lesions. Dental erosion commonly affects individuals with ED experiencing SIV, and is more often found on the palatal/lingual surfaces than on the buccal in these individuals, confirming a common clinical assumption.

Comparison of shear bond strength of self-etch and self-adhesive cements bonded to lithium disilicate, enamel and dentin.

PubMed

Naranjo, Jennifer; Ali, Mohsin; Belles, Donald

2015-11-01

Comparison of shear bond strength of self-etch and self-adhesive cements bonded to lithium disilicate, enamel and dentin. With several self-adhesive resin cements currently available, there is confusion about which product and technique is optimal for bonding ceramic restorations to teeth. The objective of this study was to compare the shear bond strength of lithium disilicate cemented to enamel and dentin using 5 adhesive cements. 100 lithium disilicate rods were pretreated with 5% hydrofluoric acid, silane, and cemented to 50 enamel and 50 dentin surfaces using five test cements: Variolink II (etch-and-rinse) control group, Clearfil Esthetic (two step self-etch), RelyX Unicem, SpeedCEM, and BifixSE (self-adhesive). All specimens were stored (37 degrees C, 100% humidity) for 24 hours before testing their shear bond strength using a universal testing machine (Instron). Debonded surfaces were observed under a low-power microscope to assess the location and type of failure. The highest bond strength for both enamel and dentin were recorded for Variolink II, 15.1MPa and 20.4MPa respectively, and the lowest were recorded for BifixSE, 0.6MPa and 0.9MPa respectively. Generally, higher bond strengths were found for dentin (7.4MPa) than enamel (5.3MPa). Tukey's post hoc test showed no significant difference between Clearfil Esthetic and SpeedCem (p = 0.059), Unicem and SpeedCem (p = 0.88), and Unicem and BifixSE (p = 0.092). All cements bonded better to lithium disilicate than to enamel or dentin, as all bond failures occurred at the tooth/adhesive interface except for Variolink II. Bond strengths recorded for self-adhesive cements were very low compared to the control "etch and rinse" and self-etch systems. Further improvements are apparently needed in self-adhesive cements for them to replace multistep adhesive systems. The use of conventional etch and rinse cements such as Veriolink II should be preferred for cementing all ceramic restorations over self-adhesive cements until the bond strengths are improved.

Microanalysis of dental caries using laser-scanned fluorescence

NASA Astrophysics Data System (ADS)

Barron, Joseph R.; Paton, Barry E.; Zakariasen, Kenneth L.

1992-06-01

It is well known that enamel and dentin fluoresce when illuminated by short-wavelength optical radiation. Fluorescence emission from carious and non-carious regions of teeth have been studied using a new experimental scanning technique for fluorescence analysis of dental sections. Scanning in 2 dimensions will allow surface maps of dental caries to be created. These surface images are then enhanced using the conventional and newer image processing techniques. Carious regions can be readily identified and contour maps can be used to graphically display the degree of damage on both surfaces and transverse sections. Numerous studies have shown that carious fluorescence is significantly different than non-carious regions. The scanning laser fluorescence spectrometer focuses light from a 25 mW He-Cd laser at 442 nm through an objective lens onto a cross-section area as small as 3 micrometers in diameter. Microtome prepared dental samples 100 micrometers thick are laid flat onto an optical bench perpendicular to the incident beam. The sample is moved under computer control in X & Y with an absolute precision of 0.1 micrometers . The backscattered light is both spatial and wavelength filtered before being measured on a long wavelength sensitized photomultiplier tube. High precision analysis of dental samples allow detailed maps of carious regions to be determined. Successive images allow time studies of caries growth and even the potential for remineralization studies of decalcified regions.

The variation in surface morphology and hardness of human deciduous teeth samples after laser irradiation

NASA Astrophysics Data System (ADS)

Khalid, Arooj; Bashir, Shazia; Akram, Mahreen; Salman Ahmed, Qazi

2017-11-01

The variation in surface morphology and hardness of human deciduous teeth samples has been investigated after laser irradiation at different wavelengths and energies. Nd:YAG was employed as a source of irradiation for IR (1064 nm) and visible (532 nm) radiation, whereas an excimer laser was used as the source of UV (248 nm) radiation. Scanning electron microscope (SEM) analysis was carried out to reveal the surface morphological evolution of teeth samples. Vickers microhardness tester was employed to investigate the modifications in the hardness of the laser-treated samples. It is observed from SEM analysis that IR wavelength is responsible for ablation of collagen matrix and intertubular dentine. For visible radiation, the ablation of collagen along with hydroxypatite is observed. With UV radiation, the ablation of peritubular dentine is dominant and is responsible for the sealing of tubules. The decrease in hardness at lower energy for both wavelengths is due to the evaporation of carbon content. With increasing energy, evaporation of water along with carbon content, and resolidification and re-organization of inorganic content causes the increase in hardness of the treated dentine. SEM as well as microhardness analyses reveal that laser wavelengths and energy of laser radiation significantly influence the surface morphology and hardness of samples.

Adhesion of multimode adhesives to enamel and dentin after one year of water storage.

PubMed

Vermelho, Paulo Moreira; Reis, André Figueiredo; Ambrosano, Glaucia Maria Bovi; Giannini, Marcelo

2017-06-01

This study aimed to evaluate the ultramorphological characteristics of tooth-resin interfaces and the bond strength (BS) of multimode adhesive systems to enamel and dentin. Multimode adhesives (Scotchbond Universal (SBU) and All-Bond Universal) were tested in both self-etch and etch-and-rinse modes and compared to control groups (Optibond FL and Clearfil SE Bond (CSB)). Adhesives were applied to human molars and composite blocks were incrementally built up. Teeth were sectioned to obtain specimens for microtensile BS and TEM analysis. Specimens were tested after storage for either 24 h or 1 year. SEM analyses were performed to classify the failure pattern of beam specimens after BS testing. Etching increased the enamel BS of multimode adhesives; however, BS decreased after storage for 1 year. No significant differences in dentin BS were noted between multimode and control in either evaluation period. Storage for 1 year only reduced the dentin BS for SBU in self-etch mode. TEM analysis identified hybridization and interaction zones in dentin and enamel for all adhesives. Silver impregnation was detected on dentin-resin interfaces after storage of specimens for 1 year only with the SBU and CSB. Storage for 1 year reduced enamel BS when adhesives are applied on etched surface; however, BS of multimode adhesives did not differ from those of the control group. In dentin, no significant difference was noted between the multimode and control group adhesives, regardless of etching mode. In general, multimode adhesives showed similar behavior when compared to traditional adhesive techniques. Multimode adhesives are one-step self-etching adhesives that can also be used after enamel/dentin phosphoric acid etching, but each product may work better in specific conditions.

Efficacy of Modified Bioactive Glass for Dentin Remineralization and Obstruction of Dentinal Tubules

PubMed Central

Saffarpour, Mahshid; Tahriri, Mohammadreza; Zakerzadeh, Azadeh

2017-01-01

Objectives: This study assessed the efficacy of modified bioactive glass (MBG) for dentin remineralization and obstruction of dentinal tubules. Materials and Methods: Thirty-six dentin discs were made from 20 third molars and were stored in 12% lactic acid solution for two weeks to induce demineralization. The samples were divided into three groups (n=12): 1- BG, 2- BG modified with 5% strontium (Sr) and 3- BG modified with 10% Sr. After applying the BG, the samples were stored in artificial saliva for 7, 14 and 21 days. Attenuated Total Reflection-Fourier Transform Infrared Spectroscopy (ATR-FTIR), X-ray Diffraction (XRD) analysis, Scanning Electron Microscopy (SEM), and Energy-Dispersive X-ray (EDX) analysis were used to assess remineralization. Also, 6 dentin discs were divided into three groups of BG, BG modified with 5% Sr and BG modified with 10% Sr, to examine tubular occlusion. The discs were etched using 0.5M of EDTA for two minutes and were stored in artificial saliva for 7 days. Changes in dentin surface morphology were evaluated under SEM. Results: Group 3 showed high rates of remineralization at days 7 and 14, although the rate decreased at day 21. Group 2 exhibited high rates of remineralization at days 7, 14 and 21. Dentinal tubules were partially occluded by BG and BG modified with 5% Sr, while they were almost completely obstructed after the use of BG modified with 10% Sr. Conclusions: Strontium increases remineralization. Addition of 10% Sr to BG enhances apatite formation; however, the apatite dissolves over time. Addition of 5% Sr to BG stabilizes the apatite lattice and increases the remineralization. PMID:29285031

TEM characterization of a silorane composite bonded to enamel/dentin.

PubMed

Mine, Atsushi; De Munck, Jan; Van Ende, Annelies; Cardoso, Marcio Vivan; Kuboki, Takuo; Yoshida, Yasuhiro; Van Meerbeek, Bart

2010-06-01

The low-shrinking composite composed of combined siloxane-oxirane technology (Filtek Silorane, 3M ESPE, Seefeld, Germany) required the development of a specific adhesive (Silorane System Adhesive, 3M ESPE), in particular because of the high hydrophobicity of the silorane composite. The purpose of this study was to characterize the interfacial ultra-structure at enamel and dentin using transmission electron microscopy (TEM). Non-demineralized/demineralized 70-90 nm sections were prepared following common TEM specimen processing procedures. TEM revealed a typical twofold build-up of the adhesive resin, resulting in a total adhesive layer thickness of 10-20 microm. At bur-cut enamel, a tight interface without distinct dissolution of hydroxyapatite was observed. At bur-cut dentin, a relatively thin hybrid layer of maximum a few hundreds of nanometer was formed without clear surface demineralization. No clear resin tags were formed. At fractured dentin, the interaction appeared very superficial (100-200 nm). Distinct resin tags were formed due to the absence of smear plugs. Silver-nitrate infiltration showed a varying pattern of both spot- and cluster-like appearance of nano-leakage. Traces of Ag were typically detected along some part of the enamel-adhesive interface and/or between the two adhesive resin layers. Substantially more Ag-infiltration was observed along the dentin-adhesive interface of bur-cut dentin, as compared to that of fractured dentin. The nano-interaction of Silorane System Adhesive should be attributed to its relatively high pH of 2.7. The obtained tight interface at both enamel and dentin indicates that the two-step self-etch adhesive effectively bridged the hydrophilic tooth substrate with the hydrophobic silorane composite. Copyright (c) 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Does Acid Challenge Affect the Properties and Bond Stability of Restorative Materials on Primary Teeth?

PubMed

Tedesco, Tamara K; Calvo, Ana F B; Yoshioka, Laysa; Fukushima, Karen A; Cesar, Paulo F; Raggio, Daniela P

2018-05-31

To evaluate the effect of acidic challenge (AC) on the properties and bond stability of restorative materials to primary enamel and dentin. One hundred twenty primary molars were assigned to 12 groups according to substrate (enamel or dentin), restorative material (composite, high-viscosity glass ionomer cement [HV-GIC] or resin-modified glass-ionomer cement [RM-GIC]), and immersion after restoration (control [saline solution/7 days] or AC [cola-based drink/5 min/3x per day/7 days]). Twenty-four hours after the restorative procedure, specimens were submitted to one of the proposed challenges. Half of the specimens were immediately subjected to the microshear bond strength test, and the other half after 12 months. To determine flexural strength flexural strength and superficial roughness (SR), 30 specimens were built up. After 24 h, the first measurement of SR from 10 specimens was performed. Specimens were then immersed in one of proposed challenges and SR was measured again. Subsequently, flexural strength testing was performed. Bond strength, surface roughness, and flexural strength data were subjected to ANOVA and Tukey's test. Composite showed the highest bond strengths compared to the others materials on both substrates. The storage period negatively influenced the bond strength only for composite groups in dentin. AC after restoration negatively influenced bond strength when the materials were evaluated in eroded dentin. AC affected the second SR measurement, showing increased SR for all restorative materials. AC did not affect flexural strength. The acidic challenge jeopardizes the surface roughness and bond strength of restorations to eroded dentin.

Anatomical analysis of the resected roots of mandibular first molars after failed non-surgical retreatment

PubMed Central

2018-01-01

Objectives Understanding the reason for an unsuccessful non-surgical endodontic treatment outcome, as well as the complex anatomy of the root canal system, is very important. This study examined the cross-sectional root canal structure of mandibular first molars confirmed to have failed non-surgical root canal treatment using digital images obtained during intentional replantation surgery, as well as the causative factors of the failed conventional endodontic treatments. Materials and Methods This study evaluated 115 mandibular first molars. Digital photographic images of the resected surface were taken at the apical 3 mm level and examined. The discolored dentin area around the root canal was investigated by measuring the total surface area, the treated areas as determined by the endodontic filling material, and the discolored dentin area. Results Forty 2-rooted teeth showed discolored root dentin in both the mesial and distal roots. Compared to the original filled area, significant expansion of root dentin discoloration was observed. Moreover, the mesial roots were significantly more discolored than the distal roots. Of the 115 molars, 92 had 2 roots. Among the mesial roots of the 2-rooted teeth, 95.7% of the roots had 2 canals and 79.4% had partial/complete isthmuses and/or accessory canals. Conclusions Dentin discoloration that was not visible on periapical radiographs and cone-beam computed tomography was frequently found in mandibular first molars that failed endodontic treatment. The complex anatomy of the mesial roots of the mandibular first molars is another reason for the failure of conventional endodontic treatment. PMID:29765897

Effects of increased apical enlargement on the amount of unprepared areas and coronal dentine removal: a micro-computed tomography study.

PubMed

Pérez, A R; Alves, F R F; Marceliano-Alves, M F; Provenzano, J C; Gonçalves, L S; Neves, A A; Siqueira, J F

2018-06-01

To evaluate the effects of progressive apical enlargement on the amount of unprepared root canal surface area and remaining dentine thickness. The root canals of 30 extracted mandibular incisors with Vertucci's type I configuration were instrumented with rotary HyFlex CM instruments (Coltene-Whaledent, Altstätten, Switzerland) up to 4 instruments larger than the first one that bound at the working length (WL). Teeth were scanned in a micro-computed tomography (micro-CT) device before canal preparation and after instrumentation with the 2nd, 3rd and 4th larger instruments. The amount of unprepared surface area in the full canal or in the apical 4 mm as well as the remaining dentine thickness at 10 mm from the WL were calculated and compared. The general linear model for repeated measures adjusted by Bonferroni's post hoc test was used for statistic analysis. There was a significant reduction in the amount of unprepared areas after each increase in preparation size (P < 0.01). This was observed for both the full canal length and the 4-mm apical segment. The amount of remaining dentine was also significantly reduced after each file size (P < 0.01). However, dentine thickness always remained greater than 1 mm, even after using the largest instrument. Apical preparations up to 4 instruments larger than the first one to bind at the WL caused a significant progressive reduction in the unprepared canal area. © 2017 International Endodontic Journal. Published by John Wiley & Sons Ltd.

ADHESION OF AN ENDODONTIC SEALER TO DENTIN AND GUTTA-PERCHA: SHEAR AND PUSH-OUT BOND STRENGTH MEASUREMENTS AND SEM ANALYSIS

PubMed Central

Teixeira, Cleonice Silveira; Alfredo, Edson; Thomé, Luis Henrique de Camargo; Gariba-Silva, Ricardo; Silva-Sousa, Yara T. Correa; Sousa, Manoel Damião

2009-01-01

The use of an adequate method for evaluation of the adhesion of root canal filling materials provides more reliable results to allow comparison of the materials and substantiate their clinical choice. The aims of this study were to compare the shear bond strength (SBS) test and push-out test for evaluation of the adhesion of an epoxy-based endodontic sealer (AH Plus) to dentin and guttapercha, and to assess the failure modes on the debonded surfaces by means of scanning electron microscopy (SEM). Three groups were established (n=7): in group 1, root cylinders obtained from human canines were embedded in acrylic resin and had their canals prepared and filled with sealer; in group 2, longitudinal sections of dentin cylinders were embedded in resin with the canal surface smoothed and turned upwards; in group 3, gutta-percha cylinders were embedded in resin. Polyethylene tubes filled with sealer were positioned on the polished surface of the specimens (groups 2 and 3). The push-out test (group 1) and the SBS test (groups 2 and 3) were performed in an Instron universal testing machine running at crosshead speed of 1 mm/min. Means (±SD) in MPa were: G1 (8.8±1.13), G2 (5.9±1.05) and G3 (3.8±0.55). Statistical analysis by ANOVA and Student's t-test (α=0.05) revealed statistically significant differences (p<0.01) among the groups. SEM analysis showed a predominance of adhesive and mixed failures of AH Plus sealer. The tested surface affected significantly the results with the sealer reaching higher bond strength to dentin than to guttapercha with the SBS test. The comparison of the employed methodologies showed that the SBS test produced significantly lower bond strength values than the push-out test, was skilful in determining the adhesion of AH Plus sealer to dentin and gutta-percha, and required specimens that could be easily prepared for SEM, presenting as a viable alternative for further experiments. PMID:19274399

A scanning electron microscopy study of diseased root surfaces conditioned with EDTA gel plus Cetavlon after scaling and root planing.

PubMed

Martins Júnior, Walter; De Rossi, Andiara; Samih Georges Abi Rached, Ricardo; Rossi, Marcos Antonio

2011-01-01

In the present investigation, a scanning electron microscopy analysis was performed to evaluate the effects of the topical application of ethylenediaminetetraacetic acid (EDTA) gel associated with Cetavlon (EDTAC) in removing the smear layer and exposing collagen fibers following root surface instrumentation. Twenty-eight teeth from adult humans, single rooted and scheduled for extraction due to periodontal reasons, were selected. Each tooth was submitted to manual (scaling and root planing) instrumentation alone or combined with ultrasonic instruments, with or without etching using a 24% EDTAC gel. Following extraction, specimens were processed and examined under a scanning electron microscope. A comparative morphological semi-quantitative analysis was performed; the intensity of the smear layer and the decalcification of cementum and dentinal surfaces were graded in 12 sets using an arbitrary scale ranging from 1 (area covered by a smear layer) to 4 (no smear layer). Root debridement with hand instruments alone or combined with ultrasonic instruments resulted in a similar smear layer covering the root surfaces. The smear layer was successfully removed from the surfaces treated with EDTAC, which exhibited numerous exposed dentinal tubules and collagen fibers. This study supports the hypothesis that manual instrumentation alone or instrumentation combined with ultrasonic instrumentation is unable to remove the smear layer, whereas the subsequent topical application of EDTAC gel effectively removes the smear layer, uncovers dentinal openings and exposes collagen fibers.

TiF(4) and NaF at pH 1.2 but not at pH 3.5 are able to reduce dentin erosion.

PubMed

Wiegand, Annette; Magalhães, Ana Carolina; Sener, Beatrice; Waldheim, Elena; Attin, Thomas

2009-08-01

This study aimed to analyse and compare the protective effect of buffered (pH 3.5) and native (pH 1.2) TiF(4) in comparison to NaF solutions of same pH on dentin erosion. Bovine samples were pretreated with 1.50% TiF(4) or 2.02% NaF (both 0.48M F) solutions, each with a pH of 1.2 and 3.5. The control group received no fluoride pretreatment. Ten samples in each group were eroded with HCl (pH 2.6) for 10x60s. Erosion was analysed by determination of calcium release into the acid. Additionally, the surface and the elemental surface composition were examined by scanning electron microscopy (two samples in each group) and X-ray energy-dispersive spectroscopy in fluoridated but not eroded samples (six samples in each group). Cumulative calcium release (nmol/mm(2)) was statistically analysed by repeated measures ANOVA and one-way ANOVA at t=10min. TiF(4) and NaF at pH 1.2 decreased calcium release significantly, while TiF(4) and NaF at pH 3.5 were not effective. Samples treated with TiF(4) at pH 1.2 showed a significant increase of Ti, while NaF pretreatment increased F concentration significantly. TiF(4) at pH 1.2 led to the formation of globular precipitates occluding dentinal tubules, which could not be observed on samples treated with TiF(4) at pH 3.5. NaF at pH 1.2 but not at pH 3.5 induced the formation of surface precipitates covering dentinal tubules. Dentin erosion can be significantly reduced by TiF(4) and NaF at pH 1.2, but not at pH 3.5.

Stress distribution on dentin-cement-post interface varying root canal and glass fiber post diameters. A three-dimensional finite element analysis based on micro-CT data

PubMed Central

LAZARI, Priscilla Cardoso; de OLIVEIRA, Rodrigo Caldeira Nunes; ANCHIETA, Rodolfo Bruniera; de ALMEIDA, Erika Oliveira; FREITAS JUNIOR, Amilcar Chagas; KINA, Sidney; ROCHA, Eduardo Passos

2013-01-01

Objective The aim of the present study was to analyze the influence of root canal and glass fiber post diameters on the biomechanical behavior of the dentin/cement/post interface of a root-filled tooth using 3D finite element analysis. Material and Methods Six models were built using micro-CT imaging data and SolidWorks 2007 software, varying the root canal (C) and the glass fiber post (P) diameters: C1P1-C=1 mm and P=1 mm; C2P1-C=2 mm and P=1 mm; C2P2-C=2 mm and P=2 mm; C3P1-C=3 mm and P=1 mm; C3P2-C=3 mm and P=2 mm; and C3P3-C=3 mm and P=3 mm. The numerical analysis was conducted with ANSYS Workbench 10.0. An oblique force (180 N at 45º) was applied to the palatal surface of the central incisor. The periodontal ligament surface was constrained on the three axes (x=y=z=0). Maximum principal stress (σmax) values were evaluated for the root dentin, cement layer, and glass fiber post. Results: The most evident stress was observed in the glass fiber post at C3P1 (323 MPa), and the maximum stress in the cement layer occurred at C1P1 (43.2 MPa). The stress on the root dentin was almost constant in all models with a peak in tension at C2P1 (64.5 MPa). Conclusion The greatest discrepancy between root canal and post diameters is favorable for stress concentration at the post surface. The dentin remaining after the various root canal preparations did not increase the stress levels on the root. PMID:24473716

Comparative Analysis of Dentinal Erosion after Passive Ultrasonic Irrigation versus Irrigation with Reciprocating Activation: An Environmental Scanning Electron Study.

PubMed

Simezo, Ana Paula; da Silveira Bueno, Carlos Eduardo; Cunha, Rodrigo Sanches; Pelegrine, Rina Andrea; Rocha, Daniel Guimarães Pedro; de Martin, Alexandre Sigrist; Kato, Augusto Shoji

2017-01-01

The aim of this study was to assess ex vivo the erosive effects of passive ultrasonic irrigation versus irrigation with reciprocating activation on the dentinal surface of the root canal at 3 predetermined levels using environmental scanning electron microscopy. Ten roots of mandibular premolars were prepared using the ProTaper Universal system (Dentsply Maillefer, Ballaigues, Switzerland). The specimens were embedded in flasks cleaved longitudinally, and indentations were made 3.0, 6.0, and 9.0 mm from the apex. The specimens in the control group (n = 10) were cleaned in an ultrasonic bath containing 2.5% sodium hypochlorite and 17% EDTA and then dried. Then, environmental scanning electron microscopic images were obtained at magnification × 800. The specimens were then reassembled in their flasks, and the NaOCl and EDTA solutions were activated according to the conditions established for the experimental groups (ie, the passive ultrasonic irrigation group [n = 5] and the EasyClean (Easy Equipamentos Odontológicos, Belo Horizonte, MG, Brazil) group, irrigation with reciprocating activation with the EasyClean instrument [n = 5]). The specimens of both experimental groups were analyzed in the same manner as in the control group. Analysis of the dentinal surface topography was conducted using the 3D Roughness Reconstruction program (Phenom-World BV, Eindhoven, the Netherlands) as a means for assessing erosion. The data were evaluated by means of the Kruskal-Wallis, Student-Newman-Keuls, and Mann-Whitney tests. In the EasyClean group, the degree of dentinal erosion at 3.0 mm was significantly higher than at 9.0 mm. In the other comparisons, there was no statistically significant difference (P < .05). The final irrigation techniques tested were equivalent in relation to the degree of erosion caused to the dentinal surface. Copyright © 2016 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

Effect of etch-and-rinse and self-etching adhesive systems on hardness uniformity of resin cements after glass fiber post cementation

PubMed Central

Grande da Cruz, Fernanda Zander; Grande, Christiana Zander; Roderjan, Douglas Augusto; Galvão Arrais, César Augusto; Bührer Samra, Adriana Postiglione; Calixto, Abraham Lincoln

2012-01-01

Objective To evaluate the effects of etch-and-rinse and self-etching adhesive systems on Vickers hardness (VHN) uniformity of dual-cured resin cements after fiber post cementation. Methods: Fifty glass fiber posts were cemented into bovine roots using the following cementing systems: Prime&Bond 2.1 Dual Cure and Enforce with light-activation (PBDC-LCEN); Prime&Bond 2.1 and Enforce with light-activation (PB-CLEN); Prime&Bond 2.1 Dual Cure and Enforce without light exposure (PBDC-SCEN); ED Primer and Panavia 21 (ED-SCPN); and Clearfil SE Bond and Panavia 21 (CF-SCPN). The roots were stored in distilled water for 72 h and transversely sectioned into thirds (coronal, medium, and apical). The VHN values of the resin cement layers were measured close to the post and to the dentin wall on the transversely sectioned flat surfaces. The results were analyzed by three-way repeated measures analysis of variance (ANOVA) and Tukey’s post-hoc test (pre-set alpha of 5%). Results: Most resin cements presented higher VHN values near the post than near the dentin wall. The ED-SCPN group showed the highest VHN values regardless of the root third, while the self-cured group PBDC-SCEN exhibited the lowest values. The resin cements from the light-activated groups PBDC-LCEN and PB-LCEN showed lower VHN values at the apical third than at the coronal third. The VHN values were not influenced by the root third in self-cured groups PBDC-SCEN, ED-SCPN, and ED-SCPN. Conclusion: Depending on the product, bonding agents might promote changes in hardness uniformity of resin cements after post cementation. PMID:22904652

The role of phosphorylation in dentin phosphoprotein peptide absorption to hydroxyapatite surfaces: a molecular dynamics study

PubMed Central

Villarreal-Ramirez, Eduardo; Garduño-Juarez, Ramon; Gericke, Arne; Boskey, Adele

2015-01-01

Dentin phosphoprotein (DPP) is a protein expressed mainly in dentin and to a lesser extent in bone. DPP has a disordered structure, rich in glutamic acid, aspartic acid and phosphorylated serine/threonine residues. It has a high capacity for binding to calcium ions and to hydroxyapatite (HA) crystal surfaces. We used molecular dynamics (MD) simulations as a method for virtually screening interactions between DPP motifs and HA. The goal was to determine which motifs are absorbed to HA surfaces. For these simulations, we considered five peptides from the human DPP sequence. All-atom MD simulations were performed using GROMACS, the peptides were oriented parallel to the {100} HA crystal surface, the distance between the HA and the peptide was 3 nm. The system was simulated for 20 ns. Preliminary results show that for the unphosphorylated peptides, the acidic amino acids present an electrostatic attraction where their side chains are oriented towards HA. This attraction, however, is slow to facilitate bulk transport to the crystal surface. On the other hand, the phosphorylated (PP) peptides are rapidly absorbed on the surface of the HA with their centers of mass closer to the HA surface. More importantly, the root mean square fluctuation (RMSF) indicates that the average structures of the phosphorylated peptides are very inflexible and elongate, while that of the unphosphorylated peptides are flexible. Radius of gyration (Rg) analysis showed the compactness of un-phosphorylated peptides is lower than phosphorylated peptides. Phosphorylation of the DPP peptides is necessary for binding to HA surfaces. PMID:25158198

Comparative Morphologic Evaluation and Occluding Effectiveness of Nd: YAG, CO2 and Diode Lasers on Exposed Human Dentinal Tubules: An Invitro SEM Study

PubMed Central

Grover, Harpreet Singh; Choudhary, Pankaj

2016-01-01

Introduction Dentinal hypersensitivity is one of the most common problem, encountered in dental practice but has least predictable treatment outcome. The advent of lasers in dentistry has provided an additional therapeutic option for treating dentinal hypersensitivity. Although various lasers have been tried over a period of time to treat dentinal hypersensitivity, but still the doubt persist as to which laser leads to maximum dentinal tubular occlusion and is most suitable with minimal hazardous effects. Aim To compare the effects of Nd: YAG, CO2 and 810-nm diode lasers on width of exposed dentinal tubule orifices and to evaluate the morphologic changes on dentinal surface of human tooth after laser irradiation by scanning electron microscope (SEM). Materials and Methods Forty root specimens were obtained from ten freshly extracted human premolars, which were randomly divided into four groups of ten each. Group I: control group treated with only saline, Group II: Nd:YAG laser, Group III: CO2 laser and Group IV: 810-nm diode laser. The specimens were examined using SEM. After calculating mean tubular diameter for each group, the values were compared statistically using parametric one-way ANOVA test and Turkey’s post hoc multiple comparison test. Results All the three lased groups showed a highly statistical significant result with p-value of <0.001 as compared to non-lased group. On intergroup comparison within the lased groups, all the three groups showed statistically significant difference in the reduction of dentinal tubular diameter (p-value < 0.001). Conclusion Nd: YAG laser was found to be most effective, followed by the CO2 laser and 810-nm diode laser was found to be least effective. The morphologic changes like craters, cracks and charring effect of the dentine were seen maximum by the use of CO2 laser. PMID:27630957

Comparative Morphologic Evaluation and Occluding Effectiveness of Nd: YAG, CO2 and Diode Lasers on Exposed Human Dentinal Tubules: An Invitro SEM Study.

PubMed

Saluja, Mini; Grover, Harpreet Singh; Choudhary, Pankaj

2016-07-01

Dentinal hypersensitivity is one of the most common problem, encountered in dental practice but has least predictable treatment outcome. The advent of lasers in dentistry has provided an additional therapeutic option for treating dentinal hypersensitivity. Although various lasers have been tried over a period of time to treat dentinal hypersensitivity, but still the doubt persist as to which laser leads to maximum dentinal tubular occlusion and is most suitable with minimal hazardous effects. To compare the effects of Nd: YAG, CO2 and 810-nm diode lasers on width of exposed dentinal tubule orifices and to evaluate the morphologic changes on dentinal surface of human tooth after laser irradiation by scanning electron microscope (SEM). Forty root specimens were obtained from ten freshly extracted human premolars, which were randomly divided into four groups of ten each. Group I: control group treated with only saline, Group II: Nd:YAG laser, Group III: CO2 laser and Group IV: 810-nm diode laser. The specimens were examined using SEM. After calculating mean tubular diameter for each group, the values were compared statistically using parametric one-way ANOVA test and Turkey's post hoc multiple comparison test. All the three lased groups showed a highly statistical significant result with p-value of <0.001 as compared to non-lased group. On intergroup comparison within the lased groups, all the three groups showed statistically significant difference in the reduction of dentinal tubular diameter (p-value < 0.001). Nd: YAG laser was found to be most effective, followed by the CO2 laser and 810-nm diode laser was found to be least effective. The morphologic changes like craters, cracks and charring effect of the dentine were seen maximum by the use of CO2 laser.

The influence of fluoride varnish on the attrition of dentine.

PubMed

Li, H; Watson, T F; Sherriff, M; Curtis, R; Bartlett, D W

2007-01-01

Previous investigations have shown the potential for fluoride to be protective in an abrasion/erosion laboratory model. The aim of this study was to investigate the effect of high concentrations of fluoride delivered in a varnish on attrition of dentine. Fifteen caries-free, intact lower third molar teeth were sectioned and the enamel removed by a water-cooled diamond disc. Polished dentine surfaces were divided into 8 areas, 4 of which were randomly covered with a high-concentration fluoride varnish for 24 h. The samples were subjected to 5,000 cycles of attrition bathed under artificial saliva. Microhardness testing adjacent to the wear scars showed no statistical difference between the fluoride-treated (71.42 KHN, SD 10.52) and control surfaces (72.66 KHN, SD 9.69). The volume of the wear scar was statistically greater for the fluoride-treated surface at 9.6 microm(3) (SD 4.92) and 8.13 microm(3) (SD 5.54) for the control areas (p = 0.029). The low pH of the fluoride varnish appears to have increased the amount of wear from attrition in this laboratory study. Copyright 2007 S. Karger AG, Basel.

[The adhesive properties of two bonding systems to tetracycline stained dentin].

PubMed

Liu, H L; Liang, K N; Cheng, L; Li, J Y; He, L B

2016-01-01

To investigate and compare the bonding properties of Single Bond 2 and SE Bond to tetracycline stained dentin in vitro. Ten extracted tetracycline stained human teeth and ten extracted normal human teeth were collected and the occlusal dentin surfaces of all extracted teeth were exposed. The tetracycline stained teeth and normal teeth were divided into two groups, respectively and randomly, based on the adhesives applied. Total-etch adhesive(Single Bond 2) and self-etch adhesive(SE Bond) were used. After application of the adhesives to the dentin surfaces, composite crowns were built up. After 24 h water storage, the teeth were sectioned longitudinally into sticks(0.9 mm×0.9 mm bonding area) for micro tensile testing or micro Raman spectroscopy detection. Bonding strength(μTBS) and resin conversion rate were analyzed using one-way ANOVA. The tetracycline Single Bond 2 group presented lower bonding strength[(16.17 ± 3.16) MPa] than the tetracycline SE Bond group[(25.82 ± 2.62) MPa], and also demonstrated lower bonding strength than the normal Single Bond 2 group[(29.13 ± 2.44) MPa] and the normal SE Bond group[(24.29±2.83) MPa] (P<0.05) , while there was no statistical differences among the other three groups(P>0.05). The resin conversion rate of tetracycline Single Bond 2 group[(55±6)%] was significantly lower than the tetracycline SE Bond group[(66±3)% ](P<0.05) and also lower than the normal Single Bond 2 group[(64 ± 5)%] and the normal SE Bond group[(65 ± 4)%] (P<0.05). No statistically significant differences were observed among the other three groups(P>0.05). The bonding strength of total-etch adhesive system to the tetracycline stained dentin was significantly lower than that to the normal dentin.

Enamel organic matrix: potential structural role in enamel and relationship to residual basement membrane constituents at the dentin enamel junction

PubMed Central

McGuire, Jacob D.; Walker, Mary P.; Dusevich, Vladimir; Wang, Yong; Gorski, Jeff P.

2015-01-01

Although mature enamel is predominantly composed of mineral, a previously uncharacterized organic matrix layer remains in the post-eruptive tissue that begins at the dentin enamel junction and extends 200–300 µm towards the outer tooth surface. Identification of the composition of this layer has been hampered by its insolubility; however, we have developed a single step method to isolate the organic enamel matrix relatively intact. After dissociative dissolution of the matrix with SDS and urea, initial characterization by Western blotting and gel zymography indicates the presence of type IV and type VII basement membrane collagens and active matrix metalloproteinase-20. When combined with data from transgenic knockout mice and from human mutations, these data suggest that the enamel organic matrix (EOM) and dentin enamel junction may have a structural and functional relationship with basement membranes, e.g. skin. To clarify this relationship, we hypothesize a “foundation” model which proposes that components of the EOM form a support structure that stabilizes the crystalline enamel layer, and bonds it to the underlying dentin along the dentin enamel junction. Since we have also co-localized an active matrix metalloproteinase to this layer, our hypothesis suggests that, under pathologic conditions, MMP-mediated degradation of the EOM could destabilize the enamel–dentin interface. PMID:25158177

Bonding effectiveness of self-etch adhesives to dentin after 24 h water storage.

PubMed

Sarr, Mouhamed; Benoist, Fatou Leye; Bane, Khaly; Aidara, Adjaratou Wakha; Seck, Anta; Toure, Babacar

2018-01-01

This study evaluated the immediate bonding effectiveness of five self-etch adhesive systems bonded to dentin. The microtensile bond strength of five self-etch adhesives systems, including one two-step and four one-step self-etch adhesives to dentin, was measured. Human third molars had their superficial dentin surface exposed, after which a standardized smear layer was produced using a medium-grit diamond bur. The selected adhesives were applied according to their respective manufacturer's instructions for μTBS measurement after storage in water at 37°C for 24 h. The μTBS varied from 11.1 to 44.3 MPa; the highest bond strength was obtained with the two-step self-etch adhesive Clearfil SE Bond and the lowest with the one-step self-etch adhesive Adper Prompt L-Pop. Pretesting failures mainly occurring during sectioning with the slow-speed diamond saw were observed only with the one-step self-etch adhesive Adper Prompt L-Pop (4 out of 18). When bonded to dentin, the self-etch adhesives with simplified application procedures (one-step self-etch adhesives) still underperform as compared to the two-step self-etch adhesive Clearfil SE Bond.

Bonding effectiveness of self-etch adhesives to dentin after 24 h water storage

PubMed Central

Sarr, Mouhamed; Benoist, Fatou Leye; Bane, Khaly; Aidara, Adjaratou Wakha; Seck, Anta; Toure, Babacar

2018-01-01

Purpose: This study evaluated the immediate bonding effectiveness of five self-etch adhesive systems bonded to dentin. Materials and Methods: The microtensile bond strength of five self-etch adhesives systems, including one two-step and four one-step self-etch adhesives to dentin, was measured. Human third molars had their superficial dentin surface exposed, after which a standardized smear layer was produced using a medium-grit diamond bur. The selected adhesives were applied according to their respective manufacturer's instructions for μTBS measurement after storage in water at 37°C for 24 h. Results: The μTBS varied from 11.1 to 44.3 MPa; the highest bond strength was obtained with the two-step self-etch adhesive Clearfil SE Bond and the lowest with the one-step self-etch adhesive Adper Prompt L-Pop. Pretesting failures mainly occurring during sectioning with the slow-speed diamond saw were observed only with the one-step self-etch adhesive Adper Prompt L-Pop (4 out of 18). Conclusions: When bonded to dentin, the self-etch adhesives with simplified application procedures (one-step self-etch adhesives) still underperform as compared to the two-step self-etch adhesive Clearfil SE Bond. PMID:29674814

Dentin bonding performance and interface observation of an MMA-based restorative material.

PubMed

Shinagawa, Junichi; Inoue, Go; Nikaido, Toru; Ikeda, Masaomi; Sadr, Alireza; Tagami, Junji

2016-07-30

The purpose of this study was to evaluate bonding performance and dentin interface acid resistance using a 4-META/MMA-TBB based restorative material (BF) compared to a conventional 4-META/MMA-TBB resin cement (SB), and the effect of sodium fluoride (NaF) addition to the materials. Dentin surfaces were treated with 10% citric acid-3% ferric chloride (10-3) or 4-META containing self-etching primer (TP), followed by application of BF or SB polymer powders with or without NaF, to evaluate microtensile bond strength (µTBS) in six experimental groups; 10-3/SB, 10-3/BF, TP/SB, TP/BF, TP/SB/NaF and TP/BF/NaF. SEM observation of the resin-dentin interface was performed after acid-base challenge to evaluate interfacial dentin resistance to acid attack. TP/BF showed highest µTBS, while NaF polymers decreased µTBS. TP/BF showed funnel-shaped erosion at the interface, however, NaF polymers improved acid resistance of interface. In conclusion, BF demonstrated high µTBSs and low acid-resistance at the interface. NaF addition enhanced acid resistance but decreased µTBS.

Femtosecond laser for cavity preparation in enamel and dentin: ablation efficiency related factors.

PubMed

Chen, H; Li, H; Sun, Yc; Wang, Y; Lü, Pj

2016-02-11

To study the effects of laser fluence (laser energy density), scanning line spacing and ablation depth on the efficiency of a femtosecond laser for three-dimensional ablation of enamel and dentin. A diode-pumped, thin-disk femtosecond laser (wavelength 1025 nm, pulse width 400 fs) was used for the ablation of enamel and dentin. The laser spot was guided in a series of overlapping parallel lines on enamel and dentin surfaces to form a three-dimensional cavity. The depth and volume of the ablated cavity was then measured under a 3D measurement microscope to determine the ablation efficiency. Different values of fluence, scanning line spacing and ablation depth were used to assess the effects of each variable on ablation efficiency. Ablation efficiencies for enamel and dentin were maximized at different laser fluences and number of scanning lines and decreased with increases in laser fluence or with increases in scanning line spacing beyond spot diameter or with increases in ablation depth. Laser fluence, scanning line spacing and ablation depth all significantly affected femtosecond laser ablation efficiency. Use of a reasonable control for each of these parameters will improve future clinical application.

Analysis of root surface properties by fluorescence/Raman intensity ratio.

PubMed

Nakamura, Shino; Ando, Masahiro; Hamaguchi, Hiro-O; Yamamoto, Matsuo

2017-11-01

The aim of this study is to evaluate the existence of residual calculus on root surfaces by determining the fluorescence/Raman intensity ratio. Thirty-two extracted human teeth, partially covered with calculus on the root surface, were evaluated by using a portable Raman spectrophotometer, and a 785-nm, 100-mW laser was applied for fluorescence/Raman excitation. The collected spectra were normalized to the hydroxyapatite Raman band intensity at 960 cm -1 . Raman spectra were recorded from the same point after changing the focal distance of the laser and the target radiating angle. In seven teeth, the condition of calculus, cementum, and dentin were evaluated. In 25 teeth, we determined the fluorescence/Raman intensity ratio following three strokes of debridement. Raman spectra collected from the dentin, cementum, and calculus were different. After normalization, spectra values were constant. The fluorescence/Raman intensity ratio of calculus region showed significant differences compared to the cementum and dentin (p < 0.05). The fluorescence/Raman intensity ratio decreased with calculus debridement. For this analysis, the delta value was defined as the difference between the values before and after three strokes, with the final 2 delta values close to zero, indicating a gradual asymptotic curve and the change in intensity ratio approximating that of individual constants. Fluorescence/Raman intensity ratio was effectively used to cancel the angle- and distance-dependent fluctuations of fluorescence collection efficiency during measurement. Changes in the fluorescence/Raman intensity ratio near zero suggested that cementum or dentin was exposed, and calculus removed.

Enhanced bioactive properties of BiodentineTM modified with bioactive glass nanoparticles.

PubMed

Corral Nuñez, Camila; Covarrubias, Cristian; Fernandez, Eduardo; Oliveira, Osmir Batista de

2017-01-01

To prepare nanocomposite cements based on the incorporation of bioactive glass nanoparticles (nBGs) into BiodentineTM (BD, Septodent, Saint-Maur-des-Fosses Cedex, France) and to assess their bioactive properties. nBGs were synthesised by the sol-gel method. BD nanocomposites (nBG/BD) were prepared with 1 and 2% nBGs by weight; unmodified BD and GC Fuji IX (GIC, GC Corporation, Tokyo, Japan) were used as references. The in vitro ability of the materials to induce apatite formation was assessed in SBF by X-ray diffraction (XRD), attenuated total reflectance with Fourier transform infrared spectroscopy (ATR-FTIR), and scanning electron microscopy (SEM) with energy dispersive X-ray (EDX) analysis. BD and nBG/BD were also applied to dentine discs for seven days; the morphology and elemental composition of the dentine-cement interface were analysed using SEM-EDX. One and two percent nBG/BD composites accelerated apatite formation on the disc surface after short-term immersion in SBF. Apatite was detected on the nBG/BD nanocomposites after three days, compared with seven days for unmodified BD. No apatite formation was detected on the GIC surface. nBG/BD formed a wider interfacial area with dentine than BD, showing blockage of dentine tubules and Si incorporation, suggesting intratubular precipitation. The incorporation of nBGs into BD improves its in vitro bioactivity, accelerating the formation of a crystalline apatite layer on its surface after immersion in SBF. Compared with unmodified BD, nBG/BD showed a wider interfacial area with greater Si incorporation and intratubular precipitation of deposits when immersed in SBF.

Observation of the pulp horn by swept source optical coherence tomography and cone beam computed tomography

NASA Astrophysics Data System (ADS)

Iino, Yoshiko; Yoshioka, Toshihiko; Hanada, Takahiro; Ebihara, Arata; Sunakawa, Mitsuhiro; Sumi, Yasunori; Suda, Hideaki

2015-02-01

Cone-beam computed tomography (CBCT) is one of the most useful diagnostic techniques in dentistry but it involves ionizing radiation, while swept source optical coherence tomography (SS-OCT) has been introduced recently as a nondestructive, real-time, high resolution imaging technique using low-coherence interferometry, which involves no ionizing radiation. The purpose of this study was to evaluate the ability of SS-OCT to detect the pulp horn (PH) in comparison with that of CBCT. Ten extracted human mandibular molars were used. After horizontally removing a half of the tooth crown, the distance from the cut dentin surface to PH was measured using microfocus computed tomography (Micro CT) (SL) as the gold standard, by CBCT (CL) and by SS-OCT (OL). In the SS-OCT images, only when PH was observed beneath the overlying dentin, the distance from the cut dentin surface to PH was recorded. If the pulp was exposed, it was defined as pulp exposure (PE). The results obtained by the above three methods were statistically analyzed by Spearman's rank correlation coefficient at a significance level of p < 0.01. SS-OCT detected the presence of PH when the distance from the cut dentin surface to PH determined by SL was 2.33 mm or less. Strong correlations of the measured values were found between SL and CL (r=0.87), SL and OL (r=0.96), and CL and OL (r=0.86). The results showed that SS-OCT images correlated closely with CBCT images, suggesting that SS-OCT can be a useful tool for the detection of PH.

Evaluation of the effects of the solution used for electrochemical dissolution of nickel-titanium endodontic files on dentine structure, microhardness and cell viability.

PubMed

Amaral, C C F; Ormiga, F; Boldrini, L C; Miranda, P G; Mendonça, T A; Granjeiro, J M; Gomes, J A C P

2018-05-15

To evaluate the effects of the [NaF 12 g/L + NaCl 1 g/L] solution used in the electrochemical dissolution process of fractured endodontic files, as well as its NiTi-containing product, on dentine hardness, topography and human fibroblast viability. Sixty single-rooted human teeth were evaluated for dentine microhardness using the Vickers hardness test and the area and number of dentinal tubules by scanning electron microscopy. The samples were divided according to the dentine surface treatment: distilled water; 17% EDTA; [NaF 12 g/L + NaCl 1 g/L]; and 17% EDTA + [NaF 12 g/L + NaCl 1 g/L]. Thirty-six single-rooted human teeth were divided according to the irrigation protocol: Dulbecco's Modified Eagle's Medium + 10% fetal bovine serum; 5.25% NaOCl; [NaF 12 g/L + NaCl 1 g/L]; and [NaF 12 g/L + NaCl 1 g/L+NiTi]. The extracts in contact with the apical foramen were used in the MTT assay to evaluate human fibroblast viability, with dilutions of 100, 50, 25 and 12.5%. Statistical tests used were paired t-tests, one-way ANOVA, Tukey's test, Kruskal-Wallis test and Dunn's post-test. The [NaF 12 g/L + NaCl 1 g/L] solution did not modify the dentine microhardness or the average dentinal tubule area. However, the EDTA induced changes in the dentine structure and microhardness (p<0.05). The [NaF 12 g/L + NaCl 1 g/L] solution and its NiTi-containing product had lower cytotoxicity than NaOCl at dilutions of 25% and 50% (p<0.01). The [NaF 12 g/L + NaCl 1 g/L] solution did not alter dentine microhardness or damage the dentine structure. It also demonstrated lower cytotoxicity than NaOCl. This article is protected by copyright. All rights reserved. This article is protected by copyright. All rights reserved.

Real-Time Binding Kinetic Analyses of the Interaction of the Dietary Stain Orange II with Dentin Matrix.

PubMed

Alraies, Amr; Cole, David K; S Rees, Jeremy; Glasse, Carl; Young, Nigel; Waddington, Rachel J; Sloan, Alastair J

2018-06-09

Dietary stains can be adsorbed into the dentin of teeth. Using Orange II as a model dietary stain, this study investigated the strength of its interaction with the mineral and protein components of dentin matrix and how hydrogen peroxide (H 2 O 2 ) treatment influences this interaction. Dentin slices were prepared from human teeth and were either deproteinized (5.6% sodium hypochlorite, 12 days), demineralised (0.5 M EDTA, 3 days) or left as intact control samples. Samples were stained with Orange II for 1-168 h, during which staining intensity was quantified by image analysis. Similarly, uptake of stain by deproteinized / demineralized samples treated with 10 or 30% H 2 O 2 was investigated. Using surface plasmon resonance technology, real-time binding kinetics were determined assessing the interaction of orange II with the dentin matrix protein constituents, collagen type I, biglycan, decorin, dentin sialoprotein and osteopontin. Deproteinization of dentin matrix reduced the uptake of the orange II compared to the intact control. Conversely, demineralization of dentin samples increased the uptake of the dye. Treatment of samples for 48 h with H 2 O 2 reduced subsequent uptake of the orange II. Real-time kinetic analysis indicated moderate strength of binding for Orange II with collagen type I, weak binding with decorin and biglycan and negligible binding with dentine sialoprotein and osteopontin. These results indicate a predominant role for collagen type I, which accounts for 90% of the organic protein matrix of teeth, for attracting dietary stains. Binding analyses indicate that the interaction is highly dissociable, and further binding is reduced following H 2 O 2 treatment. This study provides new information regarding adsorption of dietary stains into tooth dentin, suggesting that they are attracted and moderately bound to the collagen type I matrix. This study also contributes valuable information for discussion for considering the effect of H 2 O 2 on bleaching teeth and its influence on subsequent uptake of dietary stains following whitening treatments. Copyright © 2018. Published by Elsevier Ltd.

Cone-beam Computed Tomography Evaluation of Root Canal Preparation using Various Rotary Instruments: An in vitro Study.

PubMed

Ramanathan, Suhashini; Solete, Pradeep

2015-11-01

To evaluate the remaining dentin thickness of teeth after cleaning and shaping the root canal using three rotary instrumentation technique using cone-beam computed tomography (CBCT). This in vitro study is being done with 30 premolar samples with 20' curvature. The study is divided into three groups a CBCT was taken to measure the shortest distance from the root canal outline to the closest adjacent root surface was measured at each level from the cementoenamel junction (CEJ) (1,3, 5 and 7 mm) before and after root canal instrumentation. The purpose of this study was to compare the effects of different instruments used to prepare curved root canals on the remaining cervical dentin thickness and total amount of dentin removed from root canals during instrumentation by using multi-slice CBCT. The remaining dentin thickness is very much necessary for the success rate of root canal treatment. However, this study helps to prove that a conservative preparation with a sound remaining dentin thickness is much more advisable. It was observed that there was a significant difference at 1 and 3 mm (p < 0.05) and at 5 and 7 mm there was no significant difference ( p > 0.05). Mtwo has removed less amount dentin when compared to ProTaper Universal and ProTaper Next system at 1 and 3 mm. Under the conditions of the study, we concluded that ProTaper Universal and ProTaper Next should be used judiciously, as it causes higher thinning of root dentin of the root when compared with Mtwo.

Dentin pretreatment and adhesive temperature as affecting factors on bond strength of a universal adhesive system.

PubMed

Sutil, Bruna Gabrielle da Silva; Susin, Alexandre Henrique

2017-01-01

To evaluate the effects of dentin pretreatment and temperature on the bond strength of a universal adhesive system to dentin. Ninety-six extracted non-carious human third molars were randomly divided into 12 groups (n=8) according to Scotchbond Universal Adhesive (SbU) applied in self-etch (SE) and etch-and-rinse (ER) mode, adhesive temperature (20°C or 37°C) and sodium bicarbonate or aluminum oxide air abrasion. After composite build up, bonded sticks with cross-sectional area of 1 mm2 were obtained to evaluate the microtensile bond strength (μTBS). The specimens were tested at a crosshead speed of 0.5 mm/min on a testing machine until failure. Fractured specimens were analyzed under stereomicroscope to determine the failure patterns in adhesive, cohesive (dentin or resin) and mixed fractures. The microtensile bond strength data was analyzed using two-way ANOVA and Tukey's test (α=5%). Interaction between treatment and temperature was statistically significant for SbU applied in self-etch technique. Both dentin treatments showed higher bond strength for ER mode, regardless of adhesive temperature. When compared to control group, sodium bicarbonate increased bond strength of SbU in SE technique. Adhesive temperature did not significantly affect the μTBS of tested groups. Predominantly, adhesive failure was observed for all groups. Dentin surface treatment with sodium bicarbonate air abrasion improves bond strength of SbU, irrespective of adhesive application mode, which makes this approach an alternative to increase adhesive performance of Scotchbond Universal Adhesive to dentin.

Dentin pretreatment and adhesive temperature as affecting factors on bond strength of a universal adhesive system

PubMed Central

Sutil, Bruna Gabrielle da Silva; Susin, Alexandre Henrique

2017-01-01

Abstract Objectives: To evaluate the effects of dentin pretreatment and temperature on the bond strength of a universal adhesive system to dentin. Material and Methods: Ninety-six extracted non-carious human third molars were randomly divided into 12 groups (n=8) according to Scotchbond Universal Adhesive (SbU) applied in self-etch (SE) and etch-and-rinse (ER) mode, adhesive temperature (20°C or 37°C) and sodium bicarbonate or aluminum oxide air abrasion. After composite build up, bonded sticks with cross-sectional area of 1 mm2 were obtained to evaluate the microtensile bond strength (μTBS). The specimens were tested at a crosshead speed of 0.5 mm/min on a testing machine until failure. Fractured specimens were analyzed under stereomicroscope to determine the failure patterns in adhesive, cohesive (dentin or resin) and mixed fractures. The microtensile bond strength data was analyzed using two-way ANOVA and Tukey's test (α=5%). Results: Interaction between treatment and temperature was statistically significant for SbU applied in self-etch technique. Both dentin treatments showed higher bond strength for ER mode, regardless of adhesive temperature. When compared to control group, sodium bicarbonate increased bond strength of SbU in SE technique. Adhesive temperature did not significantly affect the μTBS of tested groups. Predominantly, adhesive failure was observed for all groups. Conclusions: Dentin surface treatment with sodium bicarbonate air abrasion improves bond strength of SbU, irrespective of adhesive application mode, which makes this approach an alternative to increase adhesive performance of Scotchbond Universal Adhesive to dentin. PMID:29069151

Biomimetic mineralization: long-term observations in patients with dentin sensitivity.

PubMed

Guentsch, Arndt; Seidler, Karin; Nietzsche, Sandor; Hefti, Arthur F; Preshaw, Philip M; Watts, David C; Jandt, Klaus D; Sigusch, Bernd W

2012-04-01

Cervical tooth erosion is increasingly observed among adults and frequently associated with dentin sensitivity (DS). This study evaluated the effectiveness on DS of a biomimetic mineralization system (BIMIN) in comparison to the current standard treatment (Gluma(®) Desensitizer, Gluma). In this single-blind, 2-arm study, 40 patients with confirmed cervical DS were randomized to either the test group or the positive control group. A Visual-Analog-Scale (VAS) was used to assess DS following stimulation of the exposed dentin with a 2-s air blast. Assessments were made at baseline (pre-treatment), 2 days, 4, 8 and 12 weeks, and 12 months after treatment. Two-stage replicas were obtained from the treated teeth and gold sputtered at baseline, and 2 days, 3 and 12 months after treatment. Surface topography of the treated cervical lesions and occlusion of dentinal tubules were investigated using scanning electron microscopy (SEM). Both treatments led to a statistically significant reduction (P<0.0001) in DS that persisted over the entire 12-month observation period. Differences in DS between the treatments were not statistically significant. SEM photomicrographs demonstrated that a mineral layer concealed the dentinal tubules in the test group. In contrast, numerous dentinal tubules remained visible in cervical defects that were treated with Gluma. A biomimetic mineralization kit was successfully used to treat patients exhibiting DS. The effect was similar to using Gluma, and was likely the result of the deposition of an enamel-like layer on the exposed cervical dentin. Copyright © 2012 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

The effect of surface sealants with different filler content on microleakage of Class V resin composite restorations.

PubMed

Hepdeniz, Ozge Kam; Temel, Ugur Burak; Ugurlu, Muhittin; Koskan, Ozgur

2016-01-01

Microleakage is still one of the most cited reasons for failure of resin composite restorations. Alternative methods to prevent microleakage have been investigated increasingly. The aim of this study is to evaluate the microleakage in Class V resin composite restorations with or without application of surface sealants with different filler content. Ninety-six cavities were prepared on the buccal and lingual surfaces with the coronal margins located in enamel and the cervical margins located in dentin. The cavities restored with an adhesive system (Clearfil SE Bond, Kuraray, Tokyo, Japan) and resin composite (Clearfil Majesty ES-2, Kuraray, Tokyo, Japan). Teeth were stored in distilled water for 24 h and separated into four groups according to the surface sealants (Control, Fortify, Fortify Plus, and G-Coat Plus). The teeth were thermocycled (500 cycles, 5-55° C), immersed in basic fuchsine, sectioned, and analyzed for dye penetration using stereomicroscope. The data were submitted to statistical analysis by Kruskal-Wallis and Bonferroni-Dunn test. The results of the study indicated that there was minimum leakage at the enamel margins of all groups. Bonferroni-Dunn tests revealed that Fortify and GC-Coat groups showed significantly less leakage than the Control group and the Fortify Plus group at dentin margins in lingual surfaces (P < 0.05). The all surface sealants used in this study eliminated microleakage at enamel margins. Moreover, unfilled or nanofilled surface sealants were the most effective in decreasing the degree of marginal microleakage at dentin margins. However, viscosity and penetrability of the sealants could be considered for sealing ability besides composition.

Total etch technique and cavity isolation.

PubMed

Fusayama, T

1992-01-01

In the total etch technique for chemically adhesive composite restorations, the phosphoric acid penetrates only 10 microns or less into the vital dentin with the dentinal tubules being filled with the odontoblast processes. The acid is completely removed by subsequent air-water jet spray washing. The tubule apertures are perfectly sealed by the protective bonding agent layer with the resin tags adhering to the tubule walls and the resin-impregnated dentin surface. Isolation of the cavity from moisture contamination is required for only less than a few seconds after drying the etched cavity until the bonding agent coating and after this coating until the composite resin placement. Such a short time for isolation is quite easy even without a rubber dam when a trained assistant is cooperating.

Selective removal of natural caries lesions from dentin and tooth occlusal surfaces using a diode-pumped Er:YAG laser

NASA Astrophysics Data System (ADS)

Jew, Jamison; Chan, Kenneth H.; Darling, Cynthia L.; Fried, Daniel

2017-02-01

Selective removal of caries lesions with high precision is best accomplished using lasers operating at high pulse repetition rates utilizing small spot sizes. Conventional flash-lamp pumped Er:YAG lasers are poorly suited for this purpose, but new diode-pumped solid-state (DPSS) Er:YAG lasers have become available operating at high pulse repetition rates. Microradiography was used to determine the mineral content of the demineralized dentin of 200-μm thick sections with natural caries lesions prior to laser ablation. The purpose of this study was to explore the use of a DPSS Er:YAG laser for the selective removal of demineralized dentin and natural occlusal lesions on extracted teeth.

Fluoride rinse effect on retention of CaF2 formed on enamel/dentine by fluoride application.

PubMed

Falcão, Amanda; Masson, Nadia; Leitão, Tarcísio Jorge; Botelho, Juliana Nunes; Ferreira-Nóbilo, Naiara de Paula; Tabchoury, Cínthia Pereira Machado; Tenuta, Livia Maria Andaló; Cury, Jaime Aparecido

2016-01-01

Calcium fluoride-like materials ("CaF2") formed on dental surfaces after professional fluoride application are unstable in the oral environment but can be retained longer with a daily NaF mouthrinse. We tested the effect of twice daily 0.05% NaF rinses on the retention of "CaF2" formed on enamel and dentine after applying acidulated phosphate fluoride (APF). "CaF2" formed on enamel/dentine by APF application significantly decreased after exposure to artificial saliva and the 0.05% NaF rinse was ineffective to avoid this reduction. These findings suggest that the combination of APF and 0.05% NaF is not clinically relevant, either for caries or dental hypersensitivity.

Cigarette smoke affects bonding to dentin.

PubMed

Almeida e Silva, Junio S; de Araujo, Edson Medeiro; Araujo, Elito

2010-01-01

This in vitro study evaluated the microtensile bond strength (muTBS) of composite resin bonded to dentin that had been contaminated by cigarette smoke. Ten extracted unerupted human third molars were used: Six molars were prepared for muTBS testing, while the other four molars were assigned to pre- and post-etching scanning electronic microscopy (SEM) analysis. The 20 specimens obtained from the 10 coronal portions were distributed into two experimental groups so that each tooth served as its own control. Group 1 underwent a daily toothbrushing simulation and exposure to a smoking simulation chamber, while Group 2 received only a daily simulated toothbrushing. Student's t-test demonstrated that Group 1 samples demonstrated significantly lower bond strength (49.58 MPa) than Group 2 samples (58.48 MPa). Pre and postetching SEM analysis revealed the presence of contaminants on the dentinal surfaces of the Group 1 specimens. It was concluded that contamination by cigarette smoke decreases the bond strength between dentin and composite resin.

Thin and thick layers of resin-based sealer cement bonded to root dentine compared: Adhesive behaviour.

PubMed

Pane, Epita S; Palamara, Joseph E A; Messer, Harold H

2015-12-01

This study aims to evaluate tensile and shear bond strengths of one epoxy (AH) and two methacrylate resin-based sealers (EZ and RS) in thin and thick layers bonded to root dentine. An alignment device was prepared for accurate positioning of 20 root dentine cylinders in a predefined gap of 0.1 or 1 mm. Sealer was placed in the interface. Bond strength tests were conducted. Mode of failures and representative surfaces were evaluated. Data were analysed using anova and post-hoc tests, with P < 0.05. The thick layer of sealer produced higher bond strength, except for the shear bond strength of EZ. Significant differences between thin and thick layers were found only in tensile bond strengths of AH and RS. Mixed type of failure was constantly found with all sealers. Bond strengths of thick layers of resin-based sealers to root dentine tended to be higher than with thin layers. © 2015 Australian Society of Endodontology.

High-energy x-ray scattering quantification of in-situ-loading-related strain gradients spanning the dentinoenamel junction (DEJ) in bovine tooth specimens.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Almer, J. D.; Stock, S. R.; Northeastern Univ.

2010-08-26

High energy X-ray scattering (80.7keV photons) at station 1-ID of the Advanced Photon Source quantified internal strains as a function of applied stress in mature bovine tooth. These strains were mapped from dentin through the dentinoenamel junction (DEJ) into enamel as a function of applied compressive stress in two small parallelepiped specimens. One specimen was loaded perpendicular to the DEJ and the second parallel to the DEJ. Internal strains in enamel and dentin increased and, as expected from the relative values of the Young's modulus, the observed strains were much higher in dentin than in enamel. Large strain gradients weremore » observed across the DEJ, and the data suggest that the mantle dentin-DEJ-aprismatic enamel structure may shield the near-surface volume of the enamel from large strains. In the enamel, drops in internal strain for applied stresses above 40MPa also suggest that this structure had cracked.« less

High-speed scanning ablation of dental hard tissues with a λ=9.3-μm CO2 laser: heat accumulation and peripheral thermal damage

NASA Astrophysics Data System (ADS)

Nguyen, Daniel; Staninec, Michal; Lee, Chulsung; Fried, Daniel

2010-02-01

A mechanically scanned CO2 laser operated at high laser pulse repetition rates can be used to rapidly and precisely remove dental decay. This study aims to determine whether these laser systems can safely ablate enamel and dentin without excessive heat accumulation and peripheral thermal damage. Peripheral thermal damage can adversely impact the mechanical strength of the irradiated tissue, particularly for dentin, and reduce the adhesion characteristics of the modified surfaces. Samples were derived from noncarious extracted molars. Pulpal temperatures were recorded using microthermocouples situated at the pulp chamber roof of samples (n=12), which were occlusally ablated using a rapid-scanning, water-cooled 300 Hz CO2 laser over a two minute time course. The mechanical strength of facially ablated dentin (n=10) was determined via four-point bend test and compared to control samples (n=10) prepared with 320 grit wet sand paper to simulate conventional preparations. Composite-to-enamel bond strength was measured via single-plane shear test for ablated/non-etched (n=10) and ablated/acid-etched (n=8) samples and compared to control samples (n=9) prepared by 320 grit wet sanding. Thermocouple measurements indicated that the temperature remained below ambient temperature at 19.0°C (s.d.=0.9) if water-cooling was used. There was no discoloration of either dentin and enamel, the treated surfaces were uniformly ablated and there were no cracks observable on the laser treated surfaces. Fourpoint bend tests yielded mean mechanical strengths of 18.2 N (s.d.=4.6) for ablated dentin and 18.1 N (s.d.=2.7) for control (p>0.05). Shear tests yielded mean bond strengths of 31.2 MPa (s.d.=2.5, p<0.01) for ablated/acid-etched samples, 5.2 MPa (s.d.=2.4, p<0.001) for ablated/non-etched samples, and 37.0 MPa (s.d.=3.6) for control. The results indicate that a rapid-scanning 300 Hz CO2 laser can effectively ablate dentin and enamel without excessive heat accumulation and with minimal thermal damage. It is not clear whether the small (16%) but statistically significant reduction in the shear bond strength to enamel is clinically significant since the mean shear bond strength exceeded 30 MPa.

Effect of Adhesive Cementation Strategies on the Bonding of Y-TZP to Human Dentin.

PubMed

Alves, Mll; Campos, F; Bergoli, C D; Bottino, M A; Özcan, M; Souza, Roa

2016-01-01

This study evaluated the effects of different adhesive strategies on the adhesion of zirconia to dentin using conventional and self-adhesive cements and their corresponding adhesive resins. The occlusal parts of human molars (N=80) were sectioned, exposing the dentin. The teeth and zirconia cylinders (N=80) (diameter=3.4 mm; height=4 mm) were randomly divided into eight groups according to the factors "surface conditioning" and "cement type" (n=10 per group). One conventional cement (CC: RelyX ARC, 3M ESPE) and one self-adhesive cement (SA: RelyX U200, 3M ESPE) and their corresponding adhesive resin (for CC, Adper Single Bond Plus; for SA, Scotchbond Universal Adhesive-SU) were applied on dentin. Zirconia specimens were conditioned either using chairside (CJ: CoJet, 30 μm, 2.5 bar, four seconds), laboratory silica coating (RC: Rocatec, 110 μm, 2.5 bar, four seconds), or universal primer (Single Bond Universal-UP). Nonconditioned groups for both cements acted as the control (C). Specimens were stored in water (37°C, 30 days) and subjected to shear bond strength (SBS) testing (1 mm/min). Data (MPa) were analyzed using two-way analysis of variance and a Tukey test (α=0.05). While surface conditioning significantly affected the SBS values (p=0.0001) (C

Frequency of Fluoride Dentifrice Use and Caries Lesions Inhibition and Repair.

PubMed

Nóbrega, Diego Figueiredo; Fernández, Constanza Estefany; Del Bel Cury, Altair Antoninha; Tenuta, Livia Maria Andaló; Cury, Jaime Aparecido

2016-01-01

The clinical relevance of the frequency of fluoride dentifrice (FD) use on enamel caries is based on evidence. However, the relative effect of FD on reduction of demineralization or enhancement of remineralization is unknown and the effect of frequency on root dentine caries has not been explored. The aim of this double-blind, crossover, in situ study, which was conducted in 4 phases of 14 days each, was to evaluate the relationship between the frequency of FD use and enamel and root dentine de- and remineralization. Eighteen volunteers wore palatal appliances containing enamel and root dentine slabs, either sound or carious. Biofilm accumulation on the slab surface was allowed, and 20% sucrose solution was dripped 3 or 8 times per day on the carious and sound slabs, respectively. Volunteers used FD (1,100 μg F/g) in the frequencies 0 (fluoride-placebo dentifrice), 1, 2 and 3 times per day. The demineralization and remineralization that occurred in sound or carious slabs was estimated by the percentage of surface hardness loss (%SHL) or recovery (%SHR). Loosely (CaF2) and firmly (FAp) bound fluoride concentrations were also determined. The relationship between the variables was analyzed by linear regression. The %SHL, CaF2 and FAp concentrations were a function of the frequency of FD use for enamel and dentine, but the %SHR was a function of the frequency of FD use only for enamel (p < 0.05). The results suggest that demineralization in enamel and root dentine is reduced in proportion to the frequency of FD use, but for remineralization the effect of the frequency of FD use was relevant only to enamel. © 2016 S. Karger AG, Basel.

The role of grape seed extract in the remineralization of demineralized dentine: micromorphological and physical analyses.

PubMed

Tang, Cheng-fang; Fang, Ming; Liu, Rui-rui; Dou, Qi; Chai, Zhi-guo; Xiao, Yu-hong; Chen, Ji-hua

2013-12-01

Grape seed extract (GSE) is known to have a positive effect on the demineralization and/or remineralization of artificial root caries lesions. The present study aimed to investigate whether biomodification of caries-like acid-etched demineralized dentine, using proanthocyanidins-rich GSE, would promote its remineralization potential. Dentine specimens were acid-etched for 30s, then biomodified using proanthocyanidin-based preconditioners (at different concentrations and pH values) for 2min, followed by a 15-day artificial remineralization regimen. They were subsequently subjected to microhardness measurements, micromorphological evaluation and X-ray diffraction analyses. Stability of the preconditioners was also analyzed, spectrophotometrically. A concentration-dependent increase was observed in the microhardness of the specimens that were biomodified using GSE preconditioners, without pH adjustment. Field emission scanning electron microscopy revealed greater mineral deposition on their surfaces, which was further identified mainly as hydroxylapatite. The absorbances of preconditioner dilutions at pH 7.4 and pH 10.0 decreased at the two typical polyphenol bands. Transient GSE biomodification promoted remineralization on the surface of demineralized dentine, and this process was influenced by the concentration and pH value of the preconditioner. GSE preconditioner at a concentration of 15%, without pH adjustment, presented with the best results, and this may be attributed to its high polyphenolic content. Copyright © 2013 Elsevier Ltd. All rights reserved.

Effects of NaOCl, EDTA and MTAD when applied to dentine on stress distribution in post-restored roots with flared canals.

PubMed

Belli, S; Eraslan, O; Eraslan, O; Eskitascioglu, M; Eskitascioglu, G

2014-12-01

To evaluate the effect of NaOCl, EDTA and MTAD on the stress distribution and levels in roots with flared canals and three different aesthetic post systems using finite element stress analysis (FEA). Three-dimensional (3D) FEA models simulating a maxillary incisor with excessive structural loss and flared root canals were created. The dentine of the first models of each post group was assumed as homogenous, whereas the others were deemed as having their elastic modulus affected up to 100 μm deep as a result of irrigation protocol (5.25 NaOCl, 17% EDTA and MTAD for 2 h). A sound incisor tooth model was used as the control. Restorations were created according to the post system used (pre-fabricated fibre post (PFP)), polyethylene fibre (Ribbond) post and core build-up (RBP), and one-piece milled zirconia post and core (ZP). Ceramic crowns were added to the models. A 300-N static load was applied at the centre of the palatal surface of the models to calculate the stress distributions. The SolidWorks/Cosmosworks structural analysis programmes were used for FEA analysis. Results were presented by considering von Mises criteria. The analysis of the von Mises stresses revealed that RBP created less stress in the remaining root dentine when compared to PFP and ZP. ZP maintained the stresses inside its body and reduced stress on the palatal surface of the root; however, it forwarded more stress towards the apical area. NaOCl-, EDTA- and MTAD-treated dentine increased the stresses within the root structure regardless of the effect of the post system used (11-15.4 MPa for PFP, 9.5-13.02 MPa for RBP and 14.2 MPa for ZP). Amongst the irrigation solutions used, EDTA and MTAD increased the stresses more than NaOCl in all models. All the irrigation solutions showed the same stress levels and distributions in the ZP model. NaOCl-, EDTA- and MTAD- treated dentine and a rigid post with high elastic modulus may increase fracture risk in roots with flared canals by increasing the stresses within root dentine. Therefore, solutions that alter the elastic modulus of dentine less (such as NaOCl) or an individually shaped post-core system constructed with a material that has an elastic modulus close to dentine (polyethylene fibre) should be used in weak roots. © 2014 International Endodontic Journal. Published by John Wiley & Sons Ltd.

Effects of tooth-brushing force with a desensitising dentifrice on dentine tubule patency and surface roughness.

PubMed

Mullan, F; Paraskar, S; Bartlett, D W; Olley, R C

2017-05-01

To investigate the effects of a 5% NovaMin containing dentifrice on dentine tubule patency and surface roughness at 100g and 400g tooth brush abrasion forces. 75 polished human dentine samples were prepared and randomly allocated into one of five groups; control (1), Na 2 PFO 3 100g abrasion force (2), NovaMin 100g (3), Na 2 PFO 3 400g (4) and NovaMin 400g (5). The control group underwent two 2-min cycles of artificial saliva (AS), one 2-min erosion cycle; the rest underwent two toothbrush abrasion cycles in an AS/dentifrice slurry and one 2-min erosion cycle. All samples were imaged at baseline and post intervention using Tandem Scanning Microscopy and Profilometry to analyse tubule patency and roughness. Mean tubule patency increased significantly between baseline and post intervention in groups 1,2 and 4 and decreased significantly post intervention in groups 3 and 5 (p<0.01). Post intervention, there were statistically significant differences in mean patent tubules between NovaMin and the Na 2 PFO 3 and control groups (p<0.001). Surface roughness increased for all groups between baseline and post interventions (P<0.001); mean (SD) roughness increases for groups 1, 2, 3, 4 and 5 were 0.14 (0.05) μm, 0.18 (0.04) μm, 0.16 (0.06) μm, 0.19 (0.07) μm and 0.21 (0.02) μm respectively. Differences between group 1 and 5 were significant (p<0.01). Brushing with NovaMin resulted in significant dentine tubule occlusion at 100g and 400g, but brushing with Na 2 PFO 3 resulted in increased tubule patency. Surface roughness increased significantly at 400g brushing with NovaMin. There was no correlation between tubule patency and surface roughness. A NovaMin desensitising dentifrice resulted in tubule occlusion even at high brushing forces. There was minimal increase in surface roughness at the lower (100g) brushing force. Copyright © 2017 Elsevier Ltd. All rights reserved.

The influence of salivary contamination on shear bond strength of dentin adhesive systems.

PubMed

Park, Jeong-won; Lee, Kyung Chae

2004-01-01

This study evaluated the influence of salivary contamination during dentin bonding procedures on shear bond strength and investigated the effect of contaminant-removing treatments on the recovery of bond strength for two dentin bonding agents. One hundred and ten human molars were embedded in cylindrical molds with self-curing acrylic resin. The occlusal dentin surface was exposed by wet grinding with #800 silicon carbide abrasive paper. The teeth were divided into five groups for One-step (OS) (BISCO, Inc) and six groups for Clearfil SE Bond (SE) (Kuraray Co, Ltd, Osaka, Japan). For One-step, the grinding surface was treated with 32% phosphoric acid; BAC (BISCO Inc) and divided into five groups: OS control group (uncontaminated), OS I (salivary contamination, blot dried), OS II (salivary contamination, completely dried), OS III (salivary contamination, wash and blot dried) and OS IV (salivary contamination, re-etching for 10 seconds, wash and blot dried). For SE bond, the following surface treatments were done: SE control group (primer applied to the fresh dentin surface), SE I (after salivary contamination, primer applied), SE II (primer, salivary contamination, dried), SE III (primer, salivary contamination, wash and dried), SE IV (after procedure of SE II, re-application of primer) and SE V (after procedure of SE III, re-application of primer). Each bonding agent was applied and light cured for 10 seconds. Clearfil AP-X (Kuraray Co, Ltd) composite was packed into the Ultradent mount jig mold and light cured for 40 seconds. The bonded specimens were stored for 24 hours in a 37 degrees C waterbath. The shear bond strengths were measured using an Instron testing machine (Model 4202, Instron Corp). The data for each group were subjected to one-way ANOVA followed by the Newman-Keuls test to make comparisons among the groups. The results were as follows: In the One-step groups, the OS II group showed statistically significant lower shear bond strength than the OS control, I, III and IV (p<0.05). In the Clearfil SE Bond groups, the SE II and SE III groups had decreased shear bond strength compared with the control and SE I, SE IV and SE V groups (p<0.05). In conclusion, when using One-step total etch adhesive and when the etched surface is contaminated by saliva, blotting the surface and applying the primer can recover the bond strength. Complete drying of the salivary contaminated surface should be avoided. In the Clearfil SE Bond groups, the re-priming treatment (SE IV and SE V) resulted in the recovery of shear bond strength in the specimens contaminated after priming.

Ultramorphology of the root surface subsequent to hand-ultrasonic simultaneous instrumentation during non-surgical periodontal treatments. An in vitro study

PubMed Central

D. ASPRIELLO, Simone; PIEMONTESE, Matteo; LEVRINI, Luca; SAURO, Salvatore

2011-01-01

Objective The purpose of this study was to investigate the ultramorphology of the root surfaces induced by mechanical instrumentation performed using conventional curettes or piezoelectric scalers when used single-handedly or with a combined technique. Material and Methods Thirty single-rooted teeth were selected and divided into 3 groups: Group A, instrumentation with curettes; Group B instrumentation with titanium nitride coated periodontal tip mounted in a piezoelectric handpiece; Group C, combined technique with curette/ultrasonic piezoelectric instrumentation. The specimens were processed and analyzed using confocal and scanning electron microscopy. Differences between the different groups of instrumentation were determined using Pearson’s χ 2 with significance predetermined at α=0.001. Results Periodontal scaling and root planing performed with curettes, ultrasonic or combined instrumentation induced several morphological changes on the root surface. The curettes produced a compact and thick multilayered smear layer, while the morphology of the root surfaces after ultrasonic scaler treatment appeared irregular with few grooves and a thin smear layer. The combination of curette/ultrasonic instrumentation showed exposed root dentin tubules with a surface morphology characterized by the presence of very few grooves and slender remnants of smear layer which only partially covered the root dentin. In some cases, it was also possible to observe areas with exposed collagen fibrils. Conclusion The curette-ultrasonic simultaneous instrumentation may combine the beneficial effects of each instrument in a single technique creating a root surface relatively free from the physical barrier of smear layer and dentin tubules orifices partial occlusion. PMID:21437474

Effect of citric acid, tetracycline, and doxycycline on instrumented periodontally involved root surfaces: A SEM study

PubMed Central

Chahal, Gurparkash Singh; Chhina, Kamalpreet; Chhabra, Vipin; Bhatnagar, Rakhi; Chahal, Amna

2014-01-01

Background: A surface smear layer consisting of organic and inorganic material is formed on the root surface following mechanical instrumentation and may inhibit the formation of new connective tissue attachment to the root surface. Modification of the tooth surface by root conditioning has resulted in improved connective tissue attachment and has advanced the goal of reconstructive periodontal treatment. Aim: The aim of this study was to compare the effects of citric acid, tetracycline, and doxycycline on the instrumented periodontally involved root surfaces in vitro using a scanning electron microscope. Settings and Design: A total of 45 dentin samples obtained from 15 extracted, scaled, and root planed teeth were divided into three groups. Materials and Methods: The root conditioning agents were applied with cotton pellets using the Passive burnishing technique for 5 minutes. The samples were then examined by the scanning electron microscope. Statistical Analysis Used: The statistical analysis was carried out using Statistical Package for Social Sciences (SPSS Inc., Chicago, IL, version 15.0 for Windows). For all quantitative variables means and standard deviations were calculated and compared. For more than two groups ANOVA was applied. For multiple comparisons post hoc tests with Bonferroni correction was used. Results: Upon statistical analysis the root conditioning agents used in this study were found to be effective in removing the smear layer, uncovering and widening the dentin tubules and unmasking the dentin collagen matrix. Conclusion: Tetracycline HCl was found to be the best root conditioner among the three agents used. PMID:24744541

Laser ablation of hard tissue: correlation between the laser beam parameters and the post-ablative tissue characteristics

NASA Astrophysics Data System (ADS)

Serafetinides, Alexandros A.; Makropoulou, Mersini I.; Khabbaz, Maruan

2003-11-01

Hard dental tissue laser applications, such as preventive treatment, laser diagnosis of caries, laser etching of enamel, laser decay removal and cavity preparation, and more recently use of the laser light to enlarge the root canal during the endodontic therapy, have been investigated for in vitro and in vivo applications. Post-ablative surface characteristics, e.g. degree of charring, cracks and other surface deformation, can be evaluated using scanning electron microscopy. The experimental data are discussed in relevance with the laser beam characteristics, e.g. pulse duration, beam profile, and the beam delivery systems employed. Techniques based on the laser illumination of the dental tissues and the subsequent evaluation of the scattered fluorescent light will be a valuable tool in early diagnosis of tooth diseases, as carious dentin or enamel. The laser induced autofluorescence signal of healthy dentin is much stronger than that of the carious dentin. However, a better understanding of the transmission patterns of laser light in teeth, for both diagnosis and therapy is needed, before the laser procedures can be used in a clinical environment.

Effect of theobromine-containing toothpaste on dentin tubule occlusion in situ.

PubMed

Amaechi, Bennett T; Mathews, Sapna M; Mensinkai, Poornima K

2015-01-01

Dentin hypersensitivity (DH) is treated by either occlusion of dentin tubules or nerve desensitization. This in situ study compared dentin tubules occlusion by theobromine-containing dentifrices with (Theodent-classic-F®, TCF) and without (Theodent-classic®, TC) fluoride with 1,500 ppm fluoride toothpaste, Colgate®-Regular (Fluoride) and Novamin®-containing toothpaste, Sensodyne®-5000-Nupro (Novamin®). Each subject wore four intraoral appliances bearing dentin blocks while using one of four test dentifrices (n = 20/dentifrice) twice daily for 7 days. The four appliances were removed successively after 1, 2, 3, and 7 days. Treated blocks and their control (untreated) blocks were examined with scanning electron microscopy (SEM). Effects were compared statistically (ANOVA/Tukey's) based on percentage of surface area covered by deposited precipitate layer (%DPL) and percentage of fully open (%FOT), partially occluded (%POT), and completely occluded (%COT) tubules in each block calculated relative to the number of tubules in their control blocks. SEM observation indicated an increased %COT and %DPL over time. After 1 and 2 days, %COT was comparable with TC and TCF, and significantly (p < 0.05) higher compared with Novamin® and Fluoride. Following 3 and 7 days, %COT was comparable among TC, TCF, and Novamin®, but remained significantly lower in Fluoride. At any time, %DPL was significantly (p < 0.05) higher in TC, TCF, and Novamin® compared with Fluoride. Theobromine-containing toothpastes with and without fluoride have equal potential in occluding dentin tubules within a shorter time period than Novamin®-containing toothpaste; however, the three demonstrated equal potential after 1 week, but not the fluoride toothpaste. Theobromine-containing toothpaste promoted dentin tubule occlusion thus shows potential to relief DH.

Incidence of apical root cracks and apical dentinal detachments after canal preparation with hand and rotary files at different instrumentation lengths.

PubMed

Liu, Rui; Kaiwar, Anjali; Shemesh, Hagay; Wesselink, Paul R; Hou, Benxiang; Wu, Min-Kai

2013-01-01

The aim of this study was to compare the incidence of apical root cracks and dentinal detachments after canal preparation with hand and rotary files at different instrumentation lengths. Two hundred forty mandibular incisors were mounted in resin blocks with simulated periodontal ligaments, and the apex was exposed. The root canals were instrumented with rotary and hand files, namely K3, ProTaper, and nickel-titanium Flex K files to the major apical foramen (AF), short AF, or beyond AF. Digital images of the apical surface of every tooth were taken during the apical enlargement at each file change. Development of dentinal defects was determined by comparing these images with the baseline image. Multinomial logistic regression test was performed to identify influencing factors. Apical crack developed in 1 of 80 teeth (1.3%) with hand files and 31 of 160 teeth (19.4%) with rotary files. Apical dentinal detachment developed in 2 of 80 teeth (2.5%) with hand files and 35 of 160 teeth (21.9%) with rotary files. Instrumentation with rotary files terminated 2 mm short of AF and did not cause any cracks. Significantly less cracks and detachments occurred when instrumentation with rotary files was terminated short of AF, as compared with that terminated at or beyond AF (P < .05). The AF deviated from the anatomic apex in 128 of 240 teeth (53%). Significantly more apical dentinal detachments appeared in teeth with a deviated AF (P = .033). Rotary instruments caused more dentinal defects than hand instruments; instrumentation short of AF reduced the risk of dentinal defects. Copyright © 2013 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

Influence of pH cycling on the microtensile bond strength of self-etching adhesives containing MDPB and fluoride to dentin and microhardness of enamel and dentin adjacent to restorations.

PubMed

Pedrosa, Vivianne Oliveira; Flório, Flávia Martão; Turssi, Cecília Pedroso; Amaral, Flávia Lucisano; Basting, Roberta Tarkany; França, Fabiana Mantovani

2012-12-01

To evaluate the influence of pH cycling on microtensile bond strength (µTBS) and fracture pattern of MDPB- and fluoride-containing self-etching adhesive systems to dentin, and on the cross-sectional Knoop microhardness (CSMH) of enamel and dentin adjacent to restorations. The two-step self-etching adhesive Clearfil SE Bond (SE; Kuraray), the two-step MDPBand fluoride-containing adhesive Clearfil Protect Bond (PB; Kuraray), and the one-step fluoride-containing adhesive One-Up Bond F Plus (OU; Tokuyama) were used to bond resin composite to midcoronal dentin surfaces (for µTBS testing) or to Class V cavities (for CSMH testing). µTBS and CSMH tests were performed after a 15-day period of pH cycling or storage in artificial saliva. µTBS to dentin was not affected by pH cycling or storage in artificial saliva; however, µTBS values found for PB were higher than those observed for OU. No difference existed among the µTBS values shown by PB, OU, and SE. The fracture pattern was affected by both pH cycling and adhesive system. In enamel, there was no difference in CSMH values provided by the different adhesive systems and storage media, regardless of the distance and depth from restoration. In dentin, PB and SE showed the highest CSMH values, which differed from those obtained for OU. Significantly higher CSMH values were found 100 µm from the restoration margin for all adhesive systems tested. The bond strength and microhardness in the vicinity of restorations were adhesive dependent, with MDPB and fluoride exerting no effect on the performance of the adhesive systems.

Influence of different etching modes on bond strength and fatigue strength to dentin using universal adhesive systems.

PubMed

Takamizawa, Toshiki; Barkmeier, Wayne W; Tsujimoto, Akimasa; Berry, Thomas P; Watanabe, Hedehiko; Erickson, Robert L; Latta, Mark A; Miyazaki, Masashi

2016-02-01

The purpose of this study was to determine the dentin bonding ability of three new universal adhesive systems under different etching modes using fatigue testing. Prime & Bond elect [PE] (DENTSPLY Caulk), Scotchbond Universal [SU] (3M ESPE), and All Bond Universal [AU] (Bisco) were used in this study. A conventional single-step self-etch adhesive, Clearfil Bond SE ONE [CS] (Kuraray Noritake Dental) was also included as a control. Shear bond strengths (SBS) and shear fatigue strength (SFS) to human dentin were obtained in the total-etch mode and self-etch modes. For each test condition, 15 specimens were prepared for the SBS and 30 specimens for SFS. SEM was used to examine representative de-bonded specimens, treated dentin surfaces and the resin/dentin interface for each test condition. Among the universal adhesives, PE in total-etch mode showed significantly higher SBS and SFS values than in self-etch mode. SU and AU did not show any significant difference in SBS and SFS between the total-etch mode and self-etch mode. However, the single-step self-etch adhesive CS showed significantly lower SBS and SFS values in the etch-and-rinse mode when compared to the self-etch mode. Examining the ratio of SFS/SBS, for PE and AU, the etch-and-rinse mode groups showed higher ratios than the self-etch mode groups. The influence of different etching modes on dentin bond quality of universal adhesives was dependent on the adhesive material. However, for the universal adhesives, using the total-etch mode did not have a negative impact on dentin bond quality. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Mini-interfacial Fracture Toughness of a Multimode Adhesive Bonded to Plasma-treated Dentin.

PubMed

Ayres, Ana Paula Almeida; Pongprueksa, Pong; De Munck, Jan; Gré, Cristina Parise; Nascimento, Fábio Dupart; Giannini, Marcelo; Van Meerbeek, Bart

2017-01-01

To investigate the bonding efficacy of a multimode adhesive to plasma-treated and -untreated (control) dentin using a mini-interfacial fracture toughness (mini-iFT) test. Twenty human molars were used in a split-tooth design (n = 10). The adhesive Scotchbond Universal (SBU; 3M ESPE) was applied in etch-and-rinse (E&R) and self-etch (SE) modes. Mid-coronal dentin was exposed and covered with a standardized smear layer ground to 320 grit. One half of each dentin surface received 15 s of non-thermal atmospheric plasma (NTAP), while the other half was covered with a metallic barrier and kept untreated. Following the E&R mode, dentin was plasma treated immediately after phosphoric acid etching. SBU and a resin-based composite were applied to dentin following the manufacturer's instructions. Six mini-iFT specimens were prepared per tooth (1.5 x 2.0 x 16 to 18 mm), and a single notch was prepared at the adhesive-dentin interface using a 150-μm diamond blade under water cooling. Half of the mini-iFT specimens were immediately loaded until failure in a 4-point bending test, while the other half were first stored in distilled water for 6 months. After testing, the exact dimensions of the notch were measured with a measuring optical microscope, from which ΚIc was determined. Three-way ANOVA revealed higher mini-iFT for SBU applied in E&R than SE mode for both storage times, irrespective of NTAP treatment. Overall, mini-iFT did not decrease for any of the experimental groups upon 6-month aging, while plasma treatment did not show a direct beneficial effect on mini-iFT of SBU applied in either E&R or SE mode.

Arresting simulated dentine caries with adjunctive application of silver nitrate solution and sodium fluoride varnish: an in vitro study.

PubMed

Zhao, Irene Shuping; Mei, May Lei; Li, Quan-Li; Lo, Edward Chin Man; Chu, Chun-Hung

2017-08-01

The aim of this in vitro study was to assess the ability of silver nitrate solution, followed by sodium fluoride varnish, to arrest caries. Dentine slices were prepared and demineralised. Each slice was cut into three specimens for three groups (SF, SDF and W). Specimens of the SF group received topical application of 25% silver nitrate solution followed by 5% sodium fluoride varnish. The SDF group received topical application of 38% silver diamine fluoride solution (positive control). Specimens of the W group received deionised water (negative control). All specimens were subjected to pH cycling for 8 days. Dentine surface morphology, crystal characteristics, carious lesion depth and collagen matrix degradation were evaluated by scanning electron microscopy, X-ray diffraction, X-ray microtomography and spectrophotometry with a hydroxyproline assay. Scanning electron microscopy showed that dentine collagen was exposed in group W, but not in groups SF and SDF, while clusters of granular spherical grains were formed in groups SF and SDF. The mean lesion depths (±standard deviation) of groups SF, SDF and W were 128 ± 19, 135 ± 24 and 258 ± 53 μm, respectively (SF, SDF < W; P < 0.001). The X-ray diffraction analysis indicated that silver chloride was formed in groups SF and SDF. The concentration of hydroxyproline released from the dentine matrix was significantly lower in groups SF and SDF than in group W (P < 0.05). The results of this in vitro study indicate that the use of silver nitrate solution and sodium fluoride varnish is effective in inhibiting dentine demineralisation and dentine collagen degradation. © 2017 FDI World Dental Federation.

The narwhal (Monodon monoceros) cementum-dentin junction: a functionally graded biointerphase.

PubMed

Grandfield, Kathryn; Chattah, Netta Lev-Tov; Djomehri, Sabra; Eidelmann, Naomi; Eichmiller, Frederick C; Webb, Samuel; Schuck, P James; Nweeia, Martin; Ho, Sunita P

2014-08-01

In nature, an interface between dissimilar tissues is often bridged by a graded zone, and provides functional properties at a whole organ level. A perfect example is a "biological interphase" between stratified cementum and dentin of a narwhal tooth. This study highlights the graded structural, mechanical, and chemical natural characteristics of a biological interphase known as the cementum-dentin junction layer and their effect in resisting mechanical loads. From a structural perspective, light and electron microscopy techniques illustrated the layer as a wide 1000-2000 μm graded zone consisting of higher density continuous collagen fiber bundles from the surface of cementum to dentin, that parallels hygroscopic 50-100 μm wide collagenous region in human teeth. The role of collagen fibers was evident under compression testing during which the layer deformed more compared to cementum and dentin. This behavior is reflected through site-specific nanoindentation indicating a lower elastic modulus of 2.2 ± 0.5 GPa for collagen fiber bundle compared to 3 ± 0.4 GPa for mineralized regions in the layer. Similarly, microindentation technique illustrated lower hardness values of 0.36 ± 0.05 GPa, 0.33 ± 0.03 GPa, and 0.3 ± 0.07 GPa for cementum, dentin, and cementum-dentin layer, respectively. Biochemical analyses including Raman spectroscopy and synchrotron-source microprobe X-ray fluorescence demonstrated a graded composition across the interface, including a decrease in mineral-to-matrix and phosphate-to-carbonate ratios, as well as the presence of tidemark-like bands with Zn. Understanding the structure-function relationships of wider tissue interfaces can provide insights into natural tissue and organ function. © IMechE 2014.

A Chemical Phosphorylation-inspired Design for Type I Collagen Biomimetic Remineralization

PubMed Central

Gu, Li-sha; Kim, Jongryul; Kim, Young Kyung; Liu, Yan; Dickens, Sabine H.; Pashley, David H.; Ling, Jun-qi; Tay, Franklin R.

2010-01-01

Objectives Type I collagen alone cannot initiate tissue mineralization. Sodium trimetaphosphate (STMP) is frequently employed as a chemical phosphorylating reagent in the food industry. This study examined the feasibility of using STMP as a functional analog of matrix phosphoproteins for biomimetic remineralization of resin-bonded dentin. Methods Equilibrium adsorption and desorption studies of STMP were performed using demineralized dentin powder (DDP). Interaction between STMP and DDP was examined using Fourier-transform infrared spectroscopy. Based on those results, a bio-inspired mineralization scheme was developed for chemical phosphorylation of acid-etched dentin with STMP, followed by infiltration of the STMP-treated collagen matrix with two etch-and-rinse adhesives. Resin-dentin interfaces were remineralized in a Portland cement-simulated body fluid system, with or without the use of polyacrylic acid (PAA) as a dual biomimetic analog. Remineralized resin-dentin interfaces were examined unstained using transmission electron microscopy. Results Analysis of saturation binding curves revealed the presence of irreversible phosphate group binding sites on the surface of the DDP. FT-IR provided additional evidence of chemical interaction between STMP and DDP, with increased in the peak intensities of the P=O and P–O–C stretching modes. Those peaks returned to their original intensities after alkaline phosphatase treatment. Evidence of intrafibrillar apatite formation could be seen in incompletely resin-infiltrated, STMP-phosphorylated collagen matrices only when PAA was present in the SBF. Significance These results reinforce the importance of PAA for sequestration of amorphous calcium phosphate nanoprecursors in the biomimetic remineralization scheme. They also highlight the role of STMP as a templating analog of dentin matrix phosphoproteins for inducing intrafibrillar remineralization of apatite nanocrystals within the collagen matrix of incompletely resin-infiltrated dentin. PMID:20688381

Effect of different concentrations of fluoride in dentifrices on dentin erosion subjected or not to abrasion in situ/ex vivo.

PubMed

Magalhães, A C; Rios, D; Moino, A L; Wiegand, A; Attin, T; Buzalaf, M A R

2008-01-01

This in situ/ex vivo study assessed the effect of different concentrations of fluoride in dentifrices on dentin subjected to erosion or to erosion plus abrasion. Ten volunteers took part in this crossover and double-blind study performed in 3 phases (7 days). They wore acrylic palatal appliances containing 4 bovine dentin blocks divided in two rows: erosion and erosion plus abrasion. The blocks were subjected to erosion by immersion ex vivo in a cola drink (60 s, pH 2.6) 4 times daily. During this step, the volunteers brushed their teeth with one of three dentifrices D (5,000 ppm F, NaF, silica); C (1,100 ppm F, NaF, silica) and placebo (22 ppm F, silica). Then, the respective dentifrice slurry (1:3) was dripped on dentin surfaces. While no further treatment was performed in one row, the other row was brushed using an electric toothbrush for 30 s ex vivo. The appliances were replaced in the mouth and the volunteers rinsed with water. Dentin loss was determined by profilometry and analyzed by 2-way ANOVA/Bonferroni test (a = 0.05). Dentin loss after erosive-abrasive wear was significantly greater than after erosion alone. Wear was significantly higher for the placebo than for the D and C dentifrices, which were not significantly different from each other. It can be concluded that the presence of fluoride concentrations around 1,100 ppm in dentifrices is important to reduce dentin wear by erosion and erosion + abrasion, but the protective effect does not increase with fluoride concentration. (c) 2008 S. Karger AG, Basel

Effect of salivary contamination and decontamination on bond strength of two one-step self-etching adhesives to dentin of primary and permanent teeth.

PubMed

Santschi, Katharina; Peutzfeldt, Anne; Lussi, Adrian; Flury, Simon

2015-02-01

To evaluate the effects of human saliva contamination and two decontamination procedures at different stages of the bonding procedure on the bond strength of two one-step self-etching adhesives to primary and permanent dentin. Extracted human primary and permanent molars (210 of each) were ground to mid-coronal dentin. The dentin specimens were randomly divided into 7 groups (n = 15/group/molar type) for each adhesive (Xeno V+ and Scotchbond Universal): no saliva contamination (control); saliva contamination before or after light curing of the adhesives followed by air drying, rinsing with water spray/air drying, or by rinsing with water spray/air drying/reapplication of the adhesives. Resin composite (Filtek Z250) was applied on the treated dentin surfaces. The specimens were stored at 37°C and 100% humidity for 24 h. After storage, shear bond strength (SBS) was measured and data analyzed with nonparametric ANOVA followed by exact Wilcoxon rank sum tests. Xeno V+ generated significantly higher SBS than Scotchbond Universal when no saliva contamination occurred. Saliva contamination reduced SBS of Xeno V+, with the reduction being more pronounced when contamination occurred before light curing than after. In both situations, decontamination involving reapplication of the adhesive restored SBS. Saliva contamination had no significant effect on Scotchbond Universal. There were no differences in SBS between primary and permanent teeth. Rinsing with water and air drying followed by reapplication of the adhesive restored bond strength to saliva-contaminated dentin.

Sodium Trimetaphosphate as a Novel Strategy for Matrix Metalloproteinase Inhibition and Dentin Remineralization.

PubMed

Gonçalves, Rafael Simões; Scaffa, Polliana Mendes Candia; Giacomini, Marina Ciccone; Vidal, Cristina de Mattos Pimenta; Honório, Heitor Marques; Wang, Linda

2018-01-01

The effect of sodium trimetaphosphate (STMP) as an antiproteolytic and remineralizing agent on demineralized dentin was evaluated in vitro. The inhibitory potential of STMP at 0.5, 1.5, 3.5, and 5% against recombinant matrix metalloproteinases (MMPs) MMPs-2 and -9 was assessed by zymography. To investigate its remineralization potential, 40 bovine root specimens were obtained and subjected to a demineralization protocol to produce caries-like dentin lesions. After that, dentin surfaces were divided into 3 areas: (1) mineralized (no treatment); (2) demineralized; and (3) demineralized/treated with STMP and submitted to a pH-cycling associated or not with STMP (1.5, 3.5, or 5% STMP, 10 min of treatment). After that, superficial hardness (SH) and cross-sectional hardness (CSH) were determined. Polarized light microscopy (PLM) was used to qualitatively evaluate mineralization within the caries-like lesions. The zymographic analysis showed that STMP solution is a potent inhibitor of the gelatinolytic activity of MMPs-2 and -9 depending on the dose, since the lowest concentration (0.5%) partially inhibited the enzyme activity, while the higher concentrations completely inhibited enzyme activity. Regarding remineralization effect, only 1.5% STMP solution enhanced both the SH and CSH. PLM showed that the area treated with 1.5% STMP presented similar birefringence as mineralized sound dentin. In conclusion, 1.5% STMP solution is effective as an antiproteolytic agent against MMPs and promotes dentin remineralization. © 2018 S. Karger AG, Basel.

Variation on Molecular Structure, Crystallinity, and Optical Properties of Dentin Due to Nd:YAG Laser and Fluoride Aimed at Tooth Erosion Prevention

PubMed Central

Freitas, Anderson Z.; Bachmann, Luciano; Benetti, Carolina; Ana, Patricia A.

2018-01-01

This in vitro study evaluated the compositional, crystalline, and morphological effects promoted by Nd:YAG laser on root dentin, and verified the effects of laser and topical acidulated phosphate fluoride application (APF-gel) on dentin erosion. 180 bovine dentin slabs were randomized into 4 groups (n = 45): G1–untreated, G2–APF-gel (1.23% F−, 4 min), G3–Nd:YAG (1064 nm, 84.9 J/cm2, 10 Hz), and G4–APF-gel application followed by Nd:YAG laser irradiation. The compositional, crystalline, and morphological effects promoted by treatments were investigated on five samples of each experimental group. The other samples were submitted to a 5-day, 10-day, or 15-day erosive and abrasive demineralization and remineralization cycling in order to create erosion lesions. The area and depth of lesions, as well as the optical attenuation coefficient, were assessed, and all data were statistically analysed (p < 0.05). Nd:YAG laser promoted the reduction of carbonate, the formation of tetracalcium phosphate, as well as the melting and recrystallization of the dentin surface. Laser significantly decreased the area and depth of erosion lesions and altered the optical attenuation coefficient when compared to untreated and APF-gel groups, but the association of APF-gel and laser did not promote an additional effect. Nd:YAG laser irradiation can be a promissory treatment to prevent dentin erosion and the abrasion process. PMID:29389868

Regeneration of dental pulp/dentine complex with a three-dimensional and scaffold-free stem-cell sheet-derived pellet.

PubMed

Na, Sijia; Zhang, Hao; Huang, Fang; Wang, Weiqi; Ding, Yin; Li, Dechao; Jin, Yan

2016-03-01

Dental pulp/dentine complex regeneration is indispensable to the construction of biotissue-engineered tooth roots and represents a promising approach to therapy for irreversible pulpitis. We used a tissue-engineering method based on odontogenic stem cells to design a three-dimensional (3D) and scaffold-free stem-cell sheet-derived pellet (CSDP) with the necessary physical and biological properties. Stem cells were isolated and identified and stem cells from root apical papilla (SCAPs)-based CSDPs were then fabricated and examined. Compact cell aggregates containing a high proportion of extracellular matrix (ECM) components were observed, and the CSDP culture time was prolonged. The expression of alkaline phosphatase (ALP), dentine sialoprotein (DSPP), bone sialoprotein (BSP) and runt-related gene 2 (RUNX2) mRNA was higher in CSDPs than in cell sheets (CSs), indicating that CSDPs have greater odonto/osteogenic potential. To further investigate this hypothesis, CSDPs and CSs were inserted into human treated dentine matrix fragments (hTDMFs) and transplanted into the subcutaneous space in the backs of immunodeficient mice, where they were cultured in vivo for 6 weeks. The root space with CSDPs was filled entirely with a dental pulp-like tissue with well-established vascularity, and a continuous layer of dentine-like tissue was deposited onto the existing dentine. A layer of odontoblast-like cells was found to express DSPP, ALP and BSP, and human mitochondria lined the surface of the newly formed dentine-like tissue. These results clearly indicate that SCAP-CSDPs with a mount of endogenous ECM have a strong capacity to form a heterotopic dental pulp/dentine complex in empty root canals; this method can be used in the fabrication of bioengineered dental roots and also provides an alternative treatment approach for pulp disease. Copyright © 2013 John Wiley & Sons, Ltd.

Tooth wear in three ethnic groups in Sabah (northern Borneo).

PubMed

Milosevic, A; Lo, M S

1996-12-01

The prevalence and associated aetiologies of tooth wear were investigated in three ethnic groups in Sabah (Northern Borneo) using the Tooth Wear Index (TWI). The number of surfaces with enamel wear only, dentine exposed for less than a third or dentine exposed for more than a third were categorised into the TW minimal, moderate or severe respectively. A structured questionnaire was used to elicit medical/dental history, oral hygiene practices, satisfaction with body image, diet and other personal habits/details. The sample comprised of a self selected sample of 148 dental hospital attenders; 47 (32 per cent) each of ethnic Chinese and Malay and 54 (36 per cent) of ethnic Kadazan, matched for age and with a similar number of scoreable teeth per subject. Dentine exposure within the total sample was a common finding (95 per cent TW with moderate, 41 per cent TW severe). The Kadazan group had significantly (P < 0.05) more surfaces with severe tooth wear than the Chinese or Malay. Tobacco chewing was positively associated (rho = +0.4, P < 0.05) with both moderate and severe tooth wear, as was the habit of crushing/eating bones. Neither carbonated beverages or fresh fruit intake were associated with tooth wear, but their frequency of consumption was low. The buccal and occlusal surfaces of the posterior teeth were the most severely worn. Generally, wear was greater in the upper anterior sextant compared to the lower anterior sextant, with the exception of the lower incisal edges in the Kadazan group. Tooth wear into dentine was a common occurrence, especially among the Kadazan subjects and least among the Chinese subjects. The aetiological factors associated with this tooth wear are different to those encountered in Western cultures.

Enhanced bioactive properties of BiodentineTM modified with bioactive glass nanoparticles

PubMed Central

CORRAL NUÑEZ, Camila; COVARRUBIAS, Cristian; FERNANDEZ, Eduardo; de OLIVEIRA, Osmir Batista

2017-01-01

Abstract Objective To prepare nanocomposite cements based on the incorporation of bioactive glass nanoparticles (nBGs) into BiodentineTM (BD, Septodent, Saint-Maur-des-Fosses Cedex, France) and to assess their bioactive properties. Material and Methods nBGs were synthesised by the sol-gel method. BD nanocomposites (nBG/BD) were prepared with 1 and 2% nBGs by weight; unmodified BD and GC Fuji IX (GIC, GC Corporation, Tokyo, Japan) were used as references. The in vitro ability of the materials to induce apatite formation was assessed in SBF by X-ray diffraction (XRD), attenuated total reflectance with Fourier transform infrared spectroscopy (ATR-FTIR), and scanning electron microscopy (SEM) with energy dispersive X-ray (EDX) analysis. BD and nBG/BD were also applied to dentine discs for seven days; the morphology and elemental composition of the dentine-cement interface were analysed using SEM-EDX. Results One and two percent nBG/BD composites accelerated apatite formation on the disc surface after short-term immersion in SBF. Apatite was detected on the nBG/BD nanocomposites after three days, compared with seven days for unmodified BD. No apatite formation was detected on the GIC surface. nBG/BD formed a wider interfacial area with dentine than BD, showing blockage of dentine tubules and Si incorporation, suggesting intratubular precipitation. Conclusions The incorporation of nBGs into BD improves its in vitro bioactivity, accelerating the formation of a crystalline apatite layer on its surface after immersion in SBF. Compared with unmodified BD, nBG/BD showed a wider interfacial area with greater Si incorporation and intratubular precipitation of deposits when immersed in SBF. PMID:28403358

Effects of different lasers on organic/inorganic ratio of radicular dentin.

PubMed

Lopes, F C; Roperto, R; Akkus, A; Akkus, O; Souza-Gabriel, A E; Sousa-Neto, M D

2016-04-01

The aim of this study was to evaluate the chemical stability of endodontic-treated root dentin after different laser irradiations through Raman spectroscopy. Fifty maxillary canines were selected and prepared with K3 system. Roots were randomly distributed into five groups (n = 10) according to the surface treatment: GI (water), GII (NaOCl + EDTA), GIII (NaOCl + EDTA + 980 nm Diode laser), GIV (NaOCl + EDTA+ 1064 nm Nd: YAG laser) and GV (NaOCl + EDTA+ 2780 nm Er,Cr: YSGG laser). Lasers were applied for 20 s. Samples were bisected, and the organic and inorganic content of dentin was analyzed by Raman spectroscopy. Data were submitted to ANOVA and Tukey tests (p < 0.05). None of the surface treatments alter the inorganic content (cts) (p = 0.183). Roots irradiated with Er,Cr: YSGG laser had a reduced collagen content (GV-290.7 ± 41.7) compared with the water-treated roots (GI-328.3 ± 63.5) and those treated with NaOCl + EDTA (GII-333.9 ± 55.8). Roots irradiated with Er,Cr: YSGG laser also showed a higher inorganic/organic ratio (GV-9.5 ± 1.1) than roots treated with water (GI-7.7 ± 1.5), NaOCl + EDTA (GII-8.0 ± 1.4) and diode laser (GIII-8.2 ± 1.6). Both organic and inorganic contents increased from cervical to apical thirds in all groups. None of the surface treatments were able to promote changes in the inorganic content of the root dentin; treatment with NaOCl + EDTA combined with Er,Cr: YSGG altered collagen.

Shear bond strengths of tooth coating materials including the experimental materials contained various amounts of multi-ion releasing fillers and their effects for preventing dentin demineralization.

PubMed

Arita, Shoko; Suzuki, Masaya; Kazama-Koide, Miku; Shinkai, Koichi

2017-10-01

We examined shear bond strengths (SBSs) of various tooth-coating-materials including the experimental materials to dentin and demineralization resistance of a fractured adhesive surface after the SBS testing. Three resin-type tooth-coating-materials (BC, PRG Barrier Coat; HC, Hybrid Coat II; and SF, Shield force plus) and two glass-ionomer-type tooth-coating-materials (CV, Clinpro XT Varnish; and FJ, Fuji VII) were selected. The experimental PRG Barrier Coat containing 0, 17, and 33 wt% S-PRG filler (BC0, BC17, and BC33, respectively) were developed. Each tooth-coating-material was applied to flattened dentin surfaces of extracted human teeth for SBS testing. After storing in water for 32 days with 4000 thermal cycling, the specimens were subjected to the SBS test. Specimens after SBS testing were subjected to a pH cycling test, and then, demineralization depths were measured using a polarized-light microscope. ANOVA and Tukey's HSD test were used for statistical analysis. The SBS value of FJ and CV was significantly lower than those of other materials except for BC (p < 0.01). The lesion depth of FJ was significantly shallower than those of other materials (p < 0.01); that of CV was significantly shallower than those of BC, HC, SF, and the control; and those of BC0 and BC17 were significantly shallower than that of the control (p < 0.05). The resin-type tooth-coating-materials demonstrated significantly higher SBS for dentin than the glass-ionomer-type tooth-coating-materials; however, they were inferior to the glass ionomer-type tooth-coating-materials in regards to the acid resistance of the fractured adhesion surface.

Heat propagation in dentin during instrumentation with different sonic scaler tips.

PubMed

Kocher, T; Plagmann, H C

1996-04-01

It is important to know how much heat is generated when a root surface is debrided with sonic scalers and if that heat can be released satisfactorily into the environment. The temperature changes that occurred in dentinal specimens treated with two different sonic scaler tips, used with and without coolant, were studied. Temperature increases of up to 4 degrees C were observed for both tips when a coolant was used. Heat propagation during instrumentation was dependent to a considerable degree on the temperature of the coolant. Sonic scalers should not be used without coolant, because the dentinal temperature may increase up to 35 degrees C, depending on the force of application. A high positive linear correlation was found between increase in temperature and force of application.

Indirect resin composite restorations bonded to dentin using self-adhesive resin cements applied with an electric current-assisted method.

PubMed

Gotti, Valeria Bisinoto; Feitosa, Victor Pinheiro; Sauro, Salvatore; Correr-Sobrinho, Lourenço; Correr, Americo Bortolazzo

2014-10-01

To evaluate the effects of an electric current-assisted application on the bond strength and interfacial morphology of self-adhesive resin cements bonded to dentin. Indirect resin composite build-ups were luted to prepared dentin surfaces using two self-adhesive resin cements (RelyX Unicem and BisCem) and an ElectroBond device under 0, 20, or 40 μA electrical current. All specimens were submitted to microtensile bond strength test and to interfacial SEM analysis. The electric current-assisted application induced no change (P > 0.05) on the overall bond strength, although RelyX Unicem showed significantly higher bond strength (P < 0.05) than BisCem. Similarly, no differences were observed in terms of interfacial integrity when using the electrical current applicator.

Surface modulation of dental hard tissues

NASA Astrophysics Data System (ADS)

Tantbirojn, Daranee

Tooth surfaces play a central role in the equilibrium of dental hard tissues, in which contrasting processes lead to loss or deposition of materials. The central interest of this Thesis was the modulation of tooth surfaces to control such equilibrium. Four specific studies were carried out to investigate different classes of surface modulating agents. These are: (1) Ionic modulation of the enamel surface to enhance stain removal . Dental stain is the most apparent form of tooth surface deposit. The nature of extrinsic stain in terms of spatial chemical composition was studied by using electron probe microanalysis. An ionic surface modulating agent, sodium tripolyphosphate (STPP), was evaluated. Image analysis methodologies were developed and the ability of STPP in stain removal was proved. (2) Thin film modulation with substantive polymeric coating and the effect on in vitro enamel de/re-mineralization . A novel polymeric coating that formed a thin film on the tooth surface was investigated for its inhibitory effect on artificial enamel caries, without interfering with the remineralization process. The preventive effect was distinct, but the mineral redeposition was questionable. (3) Thick film modulation with fluoride containing sealants and the effect on in vitro enamel and root caries development. Fluoride incorporated into resin material is an example of combining different classes of surface modulating agents to achieve an optimal outcome. A proper combination, such as in resin modified glass ionomer, showed in vitro caries inhibitory effect beyond the material boundary in both enamel and dentin. (4) Thick film modulation with dental adhesives and the determination of adhesion to dentin. Dentin adhesives modulate intracoronal tooth surfaces by enhancing adhesion to restorative materials. Conventional nominal bond tests were inadequate to determine the performance of current high strength adhesives. It was shown that interfacial fracture toughness test was more appropriate. In general, this Thesis evaluates diverse tooth surface modulations, for which several experimental methodologies had to be developed. These will be invaluable for the development of succeeding generations of surface modulating agents.

Effects of potassium oxalate on knoop hardness of etch-and-rinse adhesives.

PubMed

Silva, S M A; Malacarne-Zanon, J; Carvalho, R M; Alves, M C; De Goes, M F; Anido-Anido, A; Carrilho, M R

2012-01-01

The objective of this study was to determine whether the hardness of etch-and-rinse adhesives may be affected by the pretreatment of acid-etched dentin with potassium oxalate desensitizer. Unerupted human third molars were cut into crown segments by removing the occlusal enamel and roots. The pulp chamber of these crown segments was connected to a syringe barrel filled with phosphate-buffered saline so that the moisture of dentin was maintained during the bonding procedures. Three etch-and-rinse adhesives-two two-step systems (Adper Single Bond 2 [SB], One-Step [OS]) and one three-step system (Adper Scotchbond Multi-Purpose [MP])-were applied to acid-etched dentin that had been treated (experimental groups) or not (control groups) with potassium oxalate (BisBlock). The Knoop hardness (KHN) of adhesives was taken at different sites of the outer surface of the adhesive-bonded dentin. The KHN of the three tested adhesives applied to acid-etched dentin treated with potassium oxalate was significantly lower than that exhibited by the respective controls (not treated with oxalate; p<0.05). Regardless of the adhesive, the treatment with potassium oxalate reduced the adhesives' KHN (p<0.05), with the OS system exhibiting the lowest KHN compared with the MP and SB systems.

The Effects of CO2 Laser with or without Nanohydroxyapatite Paste in the Occlusion of Dentinal Tubules

PubMed Central

Al-maliky, Mohammed Abbood; Mahmood, Ali Shukur; Al-karadaghi, Tamara Sardar; Kurzmann, Christoph; Laky, Markus; Franz, Alexander; Moritz, Andreas

2014-01-01

The aim of this study was to evaluate a new treatment modality for the occlusion of dentinal tubules (DTs) via the combination of 10.6 µm carbon dioxide (CO2) laser and nanoparticle hydroxyapatite paste (n-HAp). Forty-six sound human molars were used in the current experiment. Ten of the molars were used to assess the temperature elevation during lasing. Thirty were evaluated for dentinal permeability test, subdivided into 3 groups: the control group (C), laser only (L−), and laser plus n-HAp (L+). Six samples, two per group, were used for surface and cross section morphology, evaluated through scanning electron microscope (SEM). The temperature measurement results showed that the maximum temperature increase was 3.2°C. Morphologically groups (L−) and (L+) presented narrower DTs, and almost a complete occlusion of the dentinal tubules for group (L+) was found. The Kruskal-Wallis nonparametric test for permeability test data showed statistical differences between the groups (P < 0.05). For intergroup comparison all groups were statistically different from each other, with group (L+) showing significant less dye penetration than the control group. We concluded that CO2 laser in moderate power density combined with n-HAp seems to be a good treatment modality for reducing the permeability of dentin. PMID:25386616

Nature of light scattering in dental enamel and dentin at visible and near-infrared wavelengths

NASA Astrophysics Data System (ADS)

Fried, Daniel; Glena, Richard E.; Featherstone, John D. B.; Seka, Wolf

1995-03-01

The light-scattering properties of dental enamel and dentin were measured at 543, 632, and 1053 nm. Angularly resolved scattering distributions for these materials were measured from 0 deg to 180 deg using a rotating goniometer. Surface scattering was minimized by immersing the samples in an index-matching bath. The scattering and absorption coefficients and the scattering phase function were deduced by comparing the measured scattering data with angularly resolved Monte Carlo light-scattering simulations. Enamel and dentin were best represented by a linear combination of a highly forward-peaked Henyey-Greenstein (HG) phase function and an isotropic phase function. Enamel weakly scatters light between 543 nm and 1.06 mu m, with the scattering coefficient ( mu s) ranging from mu s = 15 to 105 cm-1. The phase function is a combination of a HG function with g = 0.96 and a 30-60% isotropic phase function. For enamel, absorption is negligible. Dentin scatters strongly in the visible and near IR ( mu s approximately equals 260 cm-1) and absorbs weakly ( mu a approximately equals 4 cm-1). The scattering phase function for dentin is described by a HG function with g = 0.93 and a very weak isotropic scattering component ( approximately 2%).

Composite Replacement of Amalgam Restoration Versus Freshly Cut Dentin: An In Vitro Microleakage Comparison.

PubMed

Redwan, H; Bardwell, D N; Ali, A; Finkelman, M; Khayat, S; Weber, H-P

2016-01-01

The aim of this study was to evaluate the microleakage of the composite restorations when bonded to tooth structure previously restored with amalgam material compared with that of freshly cut dentin. Thirty intact, extracted intact human molars were mounted in autopolymerizing acrylic resin. Class II box preparations were prepared on the occluso-proximal surfaces of each tooth (4-mm bucco-lingual width and 2-mm mesio-distal depth) with the gingival cavosurface margin 1 mm above the CEJ. Each cavity was then restored using high copper amalgam restoration (Disperalloy, Dentsply) and then thermocycled for 10,000 thermal cycles. Twenty-five of the amalgam restorations were then carefully removed and replaced with Filtek Supreme Ultra Universal (3M ESPE); the remaining five were used for scanning electron microscopy and energy dispersive x-ray spectroscopy analysis. A preparation of the same dimensions was performed on the opposite surface of the tooth and restored with composite resin and thermocycled for 5000 thermal cycles. Twenty samples were randomly selected for dye penetration testing using silver nitrate staining to detect the microleakage. The specimens were analyzed with a stereomicroscope at a magnification of 20×. All of the measurements were done in micrometers; two readings were taken for each cavity at the occlusal and proximal margins. Two measurements were taken using a 0-3 scale and the percentage measurements. Corrosion products were not detected in either group (fresh cut dentin and teeth previously restored with amalgam). No statistically significant difference was found between the microleakage of the two groups using a 0-3 scale at the occlusal margins (McNemar test, p=0.727) or proximal margins (Wilcoxon signed-rank test, p=0.174). No significance difference was found between the two groups using the percentage measurements and a Wilcoxon signed-rank test at either the occlusal (p=0.675) or proximal (p=0.513) margins. However, marginal microleakage was statistically significant between the proximal and occlusal margins (p<0.001). Within the limitations of this in vitro study, no significant difference was found between the microleakage of nondiscolored dentin in teeth that were previously restored with amalgam compared with freshly cut dentin. However, marginal microleakage in the proximal surface was higher than that in the occlusal surface.

Bonding resin thixotropy and viscosity influence on dentine bond strength.

PubMed

Niem, Thomas; Schmidt, Alexander; Wöstmann, Bernd

2016-08-01

To investigate the influence of bonding resin thixotropy and viscosity on dentine tubule penetration, blister formation and consequently on dentine bond strength as a function of air-blowing pressure (air-bp) intensity. Two HEMA-free, acetone-based, one-bottle self-etch adhesives with similar composition except disparate silica filler contents and different bonding resin viscosities were investigated. The high-filler-containing adhesive (G-Bond) featured a lower viscous bonding resin with inherent thixotropic resin (TR) properties compared to the low-filler-containing adhesive (iBond) exhibiting a higher viscous bonding resin with non-thixotropic resin (NTR) properties. Shear bond strength tests for each adhesive with low (1.5bar; 0.15MPa; n=16) and high (3.0bar; 0.30MPa; n=16) air-bp application were performed after specimen storage in distilled water (24h; 37.0±1.0°C). Results were analysed using a Student's t-test to identify statistically significant differences (p<0.05). Fracture surfaces of TR adhesive specimens were morphologically characterised by SEM. Statistically significant bond strength differences were obtained for the thixotropic resin adhesive (high-pressure: 24.6MPa, low-pressure: 9.6MPa). While high air-bp specimens provided SEM images revealing resin-plugged dentine tubules, resin tags and only marginally blister structures, low air-bp left copious droplets and open dentine tubules. In contrast, the non-thixotropic resin adhesive showed no significant bond strength differences (high-pressure: 9.3MPa, low-pressure: 7.6MPa). A pressure-dependent distinct influence of bonding resin thixotropy and viscosity on dentine bond strength has been demonstrated. Stronger adhesion with high air-bp application is explained by improved resin fluidity and facilitated resin penetration into dentine tubules. Filler particles used in adhesive systems may induce thixotropic effects in bonding resin layers, accounting for improved free-flowing resin properties. In combination with high air-bp this effect allows an easy plugging of dentine tubules and elimination of blister structures, both resulting in superior dentine bond strength. Copyright © 2016 Elsevier Ltd. All rights reserved.

The effect of surface sealants with different filler content on microleakage of Class V resin composite restorations

PubMed Central

Hepdeniz, Ozge Kam; Temel, Ugur Burak; Ugurlu, Muhittin; Koskan, Ozgur

2016-01-01

Objective: Microleakage is still one of the most cited reasons for failure of resin composite restorations. Alternative methods to prevent microleakage have been investigated increasingly. The aim of this study is to evaluate the microleakage in Class V resin composite restorations with or without application of surface sealants with different filler content. Materials and Methods: Ninety-six cavities were prepared on the buccal and lingual surfaces with the coronal margins located in enamel and the cervical margins located in dentin. The cavities restored with an adhesive system (Clearfil SE Bond, Kuraray, Tokyo, Japan) and resin composite (Clearfil Majesty ES-2, Kuraray, Tokyo, Japan). Teeth were stored in distilled water for 24 h and separated into four groups according to the surface sealants (Control, Fortify, Fortify Plus, and G-Coat Plus). The teeth were thermocycled (500 cycles, 5–55° C), immersed in basic fuchsine, sectioned, and analyzed for dye penetration using stereomicroscope. The data were submitted to statistical analysis by Kruskal–Wallis and Bonferroni–Dunn test. Results: The results of the study indicated that there was minimum leakage at the enamel margins of all groups. Bonferroni–Dunn tests revealed that Fortify and GC-Coat groups showed significantly less leakage than the Control group and the Fortify Plus group at dentin margins in lingual surfaces (P < 0.05). Conclusion: The all surface sealants used in this study eliminated microleakage at enamel margins. Moreover, unfilled or nanofilled surface sealants were the most effective in decreasing the degree of marginal microleakage at dentin margins. However, viscosity and penetrability of the sealants could be considered for sealing ability besides composition. PMID:27095890

Self-induced vomiting and dental erosion – a clinical study

PubMed Central

2014-01-01

Background In individuals suffering from eating disorders (ED) characterized by vomiting (e.g. bulimia nervosa), the gastric juice regularly reaches the oral cavity, causing a possible risk of dental erosion. This study aimed to assess the occurrence, distribution and severity of dental erosions in a group of Norwegian patients experiencing self-induced vomiting (SIV). Methods The individuals included in the study were all undergoing treatment at clinics for eating disorders and were referred to a university dental clinic for examinations. One calibrated clinician registered erosions using the Visual Erosion Dental Examination (VEDE) system. Results Of 72 referred patients, 66 (63 females and three males, mean age 27.7 years) were or had been experiencing SIV (mean duration 10.6 years; range: 3 – 32 years), and were therefore included in the study. Dental erosions were found in 46 individuals (69.7%), 19 had enamel lesions only, while 27 had both enamel and dentine lesions. Ten or more teeth were affected in 26.1% of those with erosions, and 9% had ≥10 teeth with dentine lesions. Of the erosions, 41.6% were found on palatal/lingual surfaces, 36.6% on occlusal surfaces and 21.8% on buccal surfaces. Dentine lesions were most often found on lower first molars, while upper central incisors showed enamel lesions most frequently. The majority of the erosive lesions (48.6%) were found in those with the longest illness period, and 71.7% of the lesions extending into dentine were also found in this group. However, despite suffering from SIV for up to 32 years, 30.3% of the individuals showed no lesions. Conclusions Dental erosion commonly affects individuals with ED experiencing SIV, and is more often found on the palatal/lingual surfaces than on the buccal in these individuals, confirming a common clinical assumption. PMID:25069878

Assessment of remineralized dentin lesions with thermal and near-infrared reflectance imaging

NASA Astrophysics Data System (ADS)

Lee, Robert C.; Darling, Cynthia L.; Fried, Daniel

2016-02-01

Accurate detection and measurement of the highly mineralized surface layer that forms on caries lesions is important for the diagnosis of lesion activity. Previous studies have demonstrated that optical imaging methods can be used to measure the degree of remineralization on enamel lesions. The purpose of this study was to determine if thermal and near-IR reflectance imaging could be used to assess the remineralization process in simulated dentin lesions. Artificial bovine (n=15) dentin lesions were prepared by immersion in a demineralization solution for 24 hours and they were subsequently placed in an acidic remineralization solution for up to 12 days. The samples were dehydrated using an air spray for 30 seconds and imaged using thermal and InGaAs cameras. The area enclosed by the time-temperature curve, ΔQ, from thermal imaging decreased significantly with longer periods of remineralization. However, near-IR reflectance intensity differences, ΔI, before and after dehydration failed to show any significant relationship with the degree of remineralization. This study shows that thermal imaging can be used for the assessment of the remineralization of dentin lesions.

FT-Raman spectroscopy, µ-EDXRF spectrometry, and microhardness analysis of the dentin of primary and permanent teeth.

PubMed

Torres, Carolina Paes; Miranda Gomes-Silva, Jaciara; Menezes-Oliveira, Maria Angélica Hueb; Silva Soares, Luís Eduardo; Palma-Dibb, Regina Guenka; Borsatto, Maria Cristina

2018-05-01

The chemical compositions (organic and inorganic contents) and mechanical behaviors of the dentin of permanent and deciduous teeth were analyzed and compared using X-ray fluorescence spectrometry (µ-EDXRF) Fourier transform Raman spectroscopy (FT-Raman) and a microhardness test (HD). Healthy fresh human primary and permanent molars (n = 10) were selected, The buccal surfaces facing upwards were stabilized in an acrylic plate, flattened, polished, and submitted to the µ-EDXRF, FT-Raman, and HD analysis. The results of the analysis were subjected to ANOVAs and Mann-Whitney U/Student's t multiple comparisons tests. The data showed similar values for the dentin of the primary and permanent teeth in P content, organic content (amide I peak), inorganic content ( PO43- - 430 and 590), and microhardness, Nevertheless, Ca content and Ca/P weight ratio were higher, and the CO32- peak was lower in the dentin of the permanent teeth compared to primary teeth. It be concluded that despite permanent teeth showed more Ca element, both substrates showed similar behavior of chemical and physical properties. © 2018 Wiley Periodicals, Inc.

Ultrastructural analysis of root canal dentine irradiated with 980-nm diode laser energy at different parameters.

PubMed

Marchesan, Melissa Andréia; Brugnera-Junior, Aldo; Souza-Gabriel, Aline Evangelista; Correa-Silva, Silvio Rocha; Sousa-Neto, Manoel D

2008-06-01

The purpose of this in vitro study was to investigate using the scanning electron microscope (SEM) the ultrastructural morphological changes of the radicular dentine surface after irradiation with 980-nm diode laser energy at different parameters and angles of incidence. There have been limited reports on the effects of diode laser irradiation at 980 nm on radicular dentin morphology. Seventy-two maxillary canines were sectioned and roots were biomechanically prepared using K3 rotary instruments. The teeth were irrigated with 2 mL of distilled water between files and final irrigation was performed with 10 mL of distilled water. The teeth were then randomly divided into five groups (n = 8 each) according to their diode laser parameters: Group 1: no irradiation (control); group 2: 1.5 W/continuous wave (CW) emission (the manufacturer's parameters); group 3: 1.5 W/100 Hz; group 4: 3 W/CW; and group 5: 3 W/100 Hz. Laser energy was applied with helicoid movements (parallel to the canal walls) for 20 sec. Eight additional teeth for each group were endodontically prepared and split longitudinally and irradiation was applied perpendicularly to the root surface. Statistical analysis showed no difference between the root canal thirds irradiated with the 980-nm diode laser, and similar results between the parameters 1.5 W/CW and 3 W/100 Hz (p > 0.05). When considering different output powers and delivery modes our results showed that changes varied from smear layer removal to dentine fusion.

Concept and clinical application of the resin-coating technique for indirect restorations.

PubMed

Nikaido, Toru; Tagami, Junji; Yatani, Hirofumi; Ohkubo, Chikahiro; Nihei, Tomotaro; Koizumi, Hiroyasu; Maseki, Toshio; Nishiyama, Yuichiro; Takigawa, Tomoyoshi; Tsubota, Yuji

2018-03-30

The resin-coating technique is one of the successful bonding techniques used for the indirect restorations. The dentin surfaces exposed after cavity preparation are coated with a thin film of a coating material or a dentin bonding system combined with a flowable composite resin. Resin coating can minimize pulp irritation and improve the bond strength between a resin cement and tooth structures. The technique can also be applied to endodontically treated teeth, resulting in prevention of coronal leakage of the restorations. Application of a resin coating to root surface provides the additional benefit of preventing root caries in elderly patients. Therefore, the coating materials have the potential to reinforce sound tooth ("Super Tooth" formation), leading to preservation of maximum tooth structures.

Evaluation of Blood Cell Attachment on Er:Yag Laser Applied Root Surface Using Scanning Electron Microscopy

PubMed Central

CEKICI, Ali; MADEN, Ilay; YILDIZ, Sercan; SAN, Tangul; ISIK, Gulden

2013-01-01

Background: Periodontal regeneration is dependent on the uninterrupted adhesion, maturation and absorption of fibrin clots to a periodontally compromised root surface. The modification of the root surface with different agents has been used for better fibrin clot formation and blood cell attachment. It is known that Er:YAG laser application on dentin removes the smear layer succesfully. Aim: The aim of this study is to observe blood cell attachment and fibrin network formation following ER:YAG laser irradiation on periodontally compromised root surfaces in comparison to chemical root conditioning techniques in vitro. Materials and methods: 40 dentin blocks prepared from freshly extracted periodontally compromised hopeless teeth. Specimens were divided in 5 groups; those applied with PBS, EDTA, Citric acid and Er:YAG. They were further divided into two groups: those which had received these applications, and the control group. The specimens were evaluated with scanning electron microscope and micrographs were taken. Smear layer and blood cell attachment scoring was performed. Results: In the Er:YAG laser applied group, smear layer were totally removed. In the blood applied specimens, better fibrin clot formation and blood cell attachment were observed in the Er:YAG group. In the group that had been applied with citric acid, the smear layer was also removed. The smear layer could not be fully removed in the EDTA group. Conclusion: Er:YAG laser application on the root dentin seems to form a suitable surface for fibrin clot formation and blood cell attachment. Further clinical studies to support these results are necessitated. PMID:23533017

The efficacy of techniques for the disinfection of artificial sub-surface dentinal caries lesions and their effect on demineralization and remineralization in vitro.

PubMed

Preston, K P; Higham, S M; Smith, P W

2007-06-01

The efficacy of three techniques for the disinfection of artificial sub-surface root caries lesions and their response to subsequent episodes of de- and remineralization was investigated quantitatively in vitro. Sub-surface dentinal lesions (n=20), cut into four experimental blocks and deliberately contaminated with Streptococcus mutans, were subject to either steam autoclaving (121 degrees C, 5min), gamma irradiation (4100Gy), immersion in 0.1% (w/v) thymol-distilled water solution (24h) or reserved as a control. Next, the lesions were incubated aerobically in sterile nutrient broth for 24h at 37 degrees C and resultant cultures plated onto blood agar and neutralisation agar. Ten blocks from each experimental group were then immersed in an acidic buffer solution or exposed to artificial saliva for 5 days. Baseline changes in the mineral content and distribution of the lesions were assessed by transverse microradiography (TMR). Micro-organisms were recovered from each control block and one block treated by gamma irradiation. Steam autoclaving and immersion in a thymol solution significantly decreased (p<0.05) the amount of mineral lost from the body of lesions subject to a further acid challenge. Mineral ion uptake by lesions exposed to artificial saliva was significantly increased (p<0.05) through disinfection by steam autoclaving. Gamma irradiation proved the most acceptable method for the disinfection of sub-surface root dentine lesions having the least adverse effect on demineralization and remineralization.

Bonding of contemporary glass ionomer cements to dentin.

PubMed

Yip, H K; Tay, F R; Ngo, H C; Smales, R J; Pashley, D H

2001-09-01

The objective of this study was to investigate the microtensile bond strength (microTBS) of contemporary glass ionomer cements (GIC) to sound coronal dentin. Three specimen teeth were prepared for each material tested: Fuji IX GP (GC), ChemFlex (Dentsply) and Ketac-Molar Aplicap (ESPE). GIC buildups were made according to the manufacturers' instructions. After being stored at 37 degrees C, 100% humidity for 24h, the teeth were vertically sectioned into 1x1mm beams for microTBS evaluation. Representative fractured beams were prepared for scanning (SEM) and transmission electron microscopic (TEM) examination. Results of the microTBS test were: Fuji IX GP (12.4+/-8.6MPa), ChemFlex (15.0+/-9.3MPa) and Ketac-Molar Aplicap (11.4+/-7.7MPa). One-way ANOVA and a multiple comparison test showed that ChemFlex had a statistically higher microTBS (p<0.05). SEM fractographic analysis showed that the predominant failure modes were interfacial and mixed failures. The GIC side of the fractured beams revealed dehydration cracks, a high level of porosity, and voids with an eggshell-like crust. TEM analysis of the demineralized dentin sides of the fractured beams revealed the presence of an intermediate layer along the GIC-dentin interface. This zone was present on the fractured dentin surface in the case of interfacial failure, and beneath GIC remnants in specimens that exhibited a mixed failure mode. The findings suggest that the bonding of GIC to dentin is not weak and that the microTBS values probably represent the weak yield strengths of GICs under tension.

Dentine sialoprotein and collagen I expression after experimental pulp capping in humans using emdogain gel.

PubMed

Fransson, H; Petersson, K; Davies, J R

2011-03-01

To characterize the hard tissue formed in human teeth experimentally pulp capped either with calcium hydroxide or with Emdogain Gel (Biora AB, Malmö, Sweden) - a derivative of enamel matrix (EMD), using two markers for dentine; dentine sialoprotein (DSP) and type 1 collagen (Col I). Affinity-purified rabbit anti-Col I and anti-DSP polyclonal antibodies were used to stain histological sections from nine pairs of contra-lateral premolars that had been experimentally pulp amputated and randomly capped with EMDgel or calcium hydroxide. Twelve weeks after the teeth had been pulp capped, they were extracted, fixed, demineralized and serially sectioned prior to immunohistochemical staining. In the calcium hydroxide treated teeth DSP was seen in the new hard tissue which formed a bridge. DSP was also seen in the newly formed hard tissue in the EMDgel-treated teeth. Proliferated pulp tissue partly filled the space initially occupied by EMDgel and DSP-stained hard tissue was observed alongside exposed dentine surfaces as well as in isolated masses within the proliferated pulp tissue, although the new hard tissue did not cover the pulp exposure. DSP staining was also seen in the cells lining the hard tissue in both groups. Col I staining was seen in the newly formed hard tissue in both groups. The new hard tissue formed after pulp capping with EMDgel or calcium hydroxide contained DSP and Col I, considered to be markers for dentine. Thus, the newly formed hard tissue can be characterized as dentine rather than unspecific hard tissue. © 2010 International Endodontic Journal.

Mechanisms of silver diamine fluoride on arresting caries: a literature review.

PubMed

Zhao, Irene Shuping; Gao, Sherry Shiqian; Hiraishi, Noriko; Burrow, Michael Francis; Duangthip, Duangporn; Mei, May Lei; Lo, Edward Chin-Man; Chu, Chun-Hung

2018-04-01

To review the evidence regarding the mechanisms of silver diamine fluoride (SDF) for arresting caries. A literature search was conducted using the keywords silver diamine fluoride, and its alternative names, in seven databases: PubMed, Embase and Scopus (English); China National Knowledge Infrastructure (Chinese); Bilioteca Virtual em Saude (Portuguese); Biblioteca Virtual en Salud Espana (Spanish); and Ichushi-Web (Japanese). The titles and abstracts were screened. Full texts were retrieved for publications that studied mechanisms of actions of SDF, including its effects on remineralisation of carious lesions and on cariogenic bacteria. A total of 1,123 publications were identified. Twenty-nine articles were included and they investigated the effect of SDF on cariogenic bacteria and dental hard tissues. Eleven studies investigated the antibacterial properties of SDF. They found that SDF was bactericidal to cariogenic bacteria, mainly Streptococcus mutans. It inhibited the growth of cariogenic biofilms on teeth. Twenty studies reported the remineralisation of demineralised enamel or dentine by SDF. They found that mineral loss of demineralised enamel and dentine was reduced after SDF treatment. A highly mineralised surface rich in calcium and phosphate was formed on arrested carious lesions. Four studies examined the effect of SDF on dentine collagen. They found that SDF inhibited collagenases (matrix metalloproteinases and cysteine cathepsins) and protected dentine collagen from destruction. SDF is a bactericidal agent and reduces the growth of cariogenic bacteria. It inhibits demineralisation and promotes the remineralisation of demineralised enamel and dentine. It also hampers degradation of the dentine collagen. © 2017 FDI World Dental Federation.

Effect of the calcium silicate-based sealer removal protocols and time-point of acid etching on the dentin adhesive interface.

PubMed

Morais, Jéssika Mayhara Pereira; Victorino, Keli Regina; Escalante-Otárola, Wilfredo Gustavo; Jordão-Basso, Keren Cristina Fagundes; Palma-Dibb, Regina Guenka; Kuga, Milton Carlos

2018-06-15

The aim of the study was to evaluate the effects when acid etching on the dentin surface was immediately performed (I) or 7 days (D) after calcium silicate-based sealer (MTA Fillapex) removal, using 95% ethanol (E) or xylol (X). First study, 60 bovine incisor dentin specimens were impregnated with sealer and divided into six groups (n = 10): (EI), E + I; (XI), X + I; (ED), E + D; (XD), X + D, (UN), untreated and (MR), mechanical removal of sealer. Scanning electron microscopy (SEM) images (500×) were obtained from each specimen and scores assessed the sealer residues persistence. Second study, 60 specimens were similarly treated; however, the specimens were restored with composite resin after the removal protocols. Hybrid layer formation was evaluated using confocal laser microscopy (1,024×). Third study, 60 specimens were similarly obtained and subjected to micro-shear test to evaluate the effects of removal protocols on the bond strength of etch-and- rinse adhesive system to dentin. XI showed the highest persistence of sealer residues (p < .05), similar to MR (p > .05). EI showed the greatest hybrid layer extension, except in relation to UN (p < .05). XI and MR presented the lowest bond strength adhesive system to dentin (p < .05). Acid etching immediately after calcium silicate-based endodontic sealer removal using xylol presented the highest residues persistence and negatively affected the adhesive interface between dentin and etch-and-rinse adhesive system. © 2018 Wiley Periodicals, Inc.

Enamel and dentin bond strength following gaseous ozone application.

PubMed

Cadenaro, Milena; Delise, Chiara; Antoniollo, Francesca; Navarra, Ottavia Chiara; Di Lenarda, Roberto; Breschi, Lorenzo

2009-08-01

To evaluate the effects of gaseous ozone application on enamel and dentin bond strength produced by two self-etching adhesive systems. The shear bond strength test was conducted to assess adhesion on enamel (protocol 1), while the microtensile bond strength test was performed on dentin (protocol 2). Protocol 1: 96 bovine incisors were randomly divided into 4 groups, and enamel surfaces were bonded in accordance with the following treatments: (1E) ozone + Clearfil Protect Bond; (2E) Clearfil Protect Bond (control); (3E) ozone + Xeno III; (4E) Xeno III (control). Ozone gas was applied for 80 s. Shear bond strength was measured with a universal testing machine. Protocol 2: 40 noncarious human molars were selected. Middle/deep dentin was exposed and bonded in accordance with the following treatments: (1D) ozone+Clearfil Protect Bond; (2D) Clearfil Protect Bond (control); (3D) ozone+Xeno III (4D) Xeno III (control). Four-mm-thick buildups were built on the adhesives, then specimens were sectioned in accordance with the nontrimming technique. Specimens were stressed until failure occurred, and failure modes were analyzed. Shear bond and microtensile bond strength data were analyzed using two-way ANOVA and Tukey's post-hoc test. No statistical differences were found between ozone treated specimens and controls, neither on enamel nor on dentin irrespective of the tested adhesive. Clearfil Protect Bond showed higher bond strength to enamel than Xeno III, irrespective of the ozone treatment (p < 0.05). The use of ozone gas to disinfect the cavity before placing a restoration had no influence on immediate enamel and dentin bond strength.

Dentinal tubule occluding capability of nano-hydroxyapatite; The in-vitro evaluation.

PubMed

Baglar, Serdar; Erdem, Umit; Dogan, Mustafa; Turkoz, Mustafa

2018-04-29

In this in-vitro study, the effectiveness of experimental pure nano-hydroxyapatite (nHAP) and 1%, 2%, and 3% F¯ doped nano-HAp on dentine tubule occlusion was investigated. And also, the cytotoxicity of materials used in the experiment was evaluated. Nano-HAp types were synthesized by the precipitation method. Forty dentin specimens were randomly divided into five groups of; 1-no treatment (control), 2-specimens treated with 10% pure nano-HAp and 3, 4, 5 specimens treated with 1%, 2%, and 3% F - doped 10% nano-HAp, respectively. To evaluate the effectiveness of the materials used; pH, FTIR, and scanning electron microscopy evaluations were performed before and after degredation in simulated body fluid. To determine cytotoxicity of the materials, MTT assay was performed. Statistical evaluations were performed with F and t tests. All of the nano-HAp materials used in this study built up an effective covering layer on the dentin surfaces even with plugs in tubules. It was found that this layer had also a resistance to degradation. None of the evaluated nano-HAp types were have toxicity. Fluoride doping showed a positive effect on physical and chemical stability until a critical value of 1% F - . The all evaluated nano-HAp types may be effectively used in dentin hypersensitivity treatment. The formed nano-HAp layers were seem to resistant to hydrolic deletion. The pure and 1% F - doped nano-HAp showed the highest biocompatibility thus it was assessed that pure and 1% F - doped materials may be used as an active ingredient in dentin hypersensitivity agents. © 2018 Wiley Periodicals, Inc.

Long-term durability of one-step adhesive-composite systems to enamel and dentin.

PubMed

Foxton, Richard M; Melo, Luciana; Stone, David G; Pilecki, Peter; Sherriff, Martin; Watson, Timothy F

2008-01-01

This study evaluated the long-term durability of three one-step adhesive-composite systems to ground enamel and dentin. Twenty-seven teeth were randomly divided into three groups of nine. The first group had its crowns sectioned to expose superficial dentin, which was then ground with 600 grit SiC paper. One of three one-step adhesives: a trial bonding agent, OBF-2; i Bond or Adper Prompt L-Pop was applied to the dentin of three teeth and built-up with the corresponding resin composite (Estelite sigma, Venus or Filtek Supreme). The second group of nine teeth had their enamel approximal surfaces ground with wet 600-grit SiC paper, then one of the three one-step adhesives was applied and built-up with resin composite. The bonded specimens were sliced into 0.7 mm-thick slabs. After 24 hours and one year of water storage at 37 degrees C, the slabs were sectioned into beams for the microtensile bond strength test. Failure modes were observed using optical and electron scanning microscopy. The third group of nine teeth had approximal wedge-shaped cavities prepared above the CEJ into dentin. Two-to-three grains of rhodamine B were added to each of the three adhesives prior to restoring the cavities with resin composite. After 24 hours storage, the teeth were sectioned and their interfaces examined with a laser scanning confocal microscope. The bond strengths of the three adhesive-composite systems to both enamel and dentin significantly lessened after one year of water storage, however, there was no significant difference between the materials.

Study of surface topography, roughness, and microleakage after dental preparation with different instrumentation.

PubMed

Solá-Ruiz, Ma Fernanda; Faus-Matoses, Ignacio; Del Rio Highsmith, Jamie; Fons-Font, Antonio

2014-01-01

The purpose of this study was to compare the differences in surface characteristics and roughness of teeth finished for porcelain veneer laminates using different instrumentation and to assess their influence on microleakage. Fifty-six extracted human maxillary central incisors were divided randomly into two groups: Group HsR teeth were finished with a high-speed handpiece with diamond burs; group SO teeth were finished with a sonic oscillating diamond instrument. Porcelain veneers were bonded to 24 teeth in each group. Microleakage was measured in the cervical area. Four remaining teeth in each group were examined using confocal laser-scanning microscopy and scanning electron microscopy. Oscillating instruments produced a rougher dentinal surface (Ra values; P = .029) than those finished with high-speed rotary technology. There is less microleakage when bonded restoration edges are situated over dentin that has been finished with sonic oscillating instrumentation (P = .006).

Solvent composition of one-step self-etch adhesives and dentine wettability.

PubMed

Grégoire, Geneviève; Dabsie, Firas; Dieng-Sarr, Farimata; Akon, Bernadette; Sharrock, Patrick

2011-01-01

Our aim was to determine the wettability of dentine by four commercial self-etch adhesives and evaluate their spreading rate on the dentine surface. Any correlation with chemical composition was sought, particularly with the amount of solvent or HEMA present in the adhesive. The adhesives used were AdheSE One, Optibond All.In.One, Adper Easy Bond and XenoV. Chemical compositions were determined by proton nuclear magnetic resonance (NMR) spectroscopy of the adhesives dissolved in dimethylsulfoxide. Apparent contact angles for sessile drops of adhesives were measured on dentine slices as a function of time for up to 180s. The water contact angles were determined for fully polymerised adhesives. All adhesives were water-based with total solvent contents ranging from 27% to 73% for HEMA-free adhesives, and averaging 45% for HEMA containing adhesives. The contents in hydrophobic groups decreased as water contents increased. No differences were found in the adhesive contact angles after 180s even though the spreading rates were different for the products tested. Water contact angles differed significantly but were not correlated with HEMA or solvent presence. Manufacturers use different approaches to stabilise acid co-monomer ingredients in self-etch adhesives. Co-solvents, HEMA, or acrylamides without co-solvents are used to simultaneously etch and infiltrate dentine. A large proportion of water is necessary for decalcification action. Copyright © 2010 Elsevier Ltd. All rights reserved.

A Stereomicroscopic Evaluation of Dentinal Cracks at Different Instrumentation Lengths by Using Different Rotary Files (ProTaper Universal, ProTaper Next, and HyFlex CM): An Ex Vivo Study

PubMed Central

Shankarappa, Pushpa; Misra, Abhinav; Sawhney, Asheesh; Sridevi, Nandamuri; Singh, Anu

2016-01-01

Introduction. The aim of the present study was to evaluate the dentinal cracks after root canal preparation with rotary files: Gates Glidden, ProTaper Universal, ProTaper Next, and HyFlex CM at different instrumentation lengths. Methodology. Sixty-five mandibular premolars were mounted in the acrylic tube with simulated periodontal ligaments and the apex was exposed. The root canals were instrumented with different rotary files, namely, ProTaper Universal, ProTaper Next, and HyFlex CM, to the major apical foramen (AF), short AF, and beyond AF. The root apex was stained with 1% methylene blue dye and digital images of apical surface of every tooth were taken and development of dentinal defects was determined by using stereomicroscope. Multinomial logistic regression test was performed to identify influencing factors. Results. Instrumentation with rotary files terminated 2 mm short AF and did not cause any cracks. Significantly less cracks were seen when instrumentation with rotary files terminated 1 mm short apical foramen when compared with the instrumentation terminated at or beyond apical foramen (p < 0.05). Conclusion. ProTaper Universal rotary files caused more dentinal cracks than ProTaper Next and HyFlex CM. Instrumentation short AF reduced the risk of dentinal defects. PMID:27446636

Fiber optic backscatter spectroscopic sensor to monitor enamel demineralization and remineralization in vitro

PubMed Central

Kishen, Anil; Shrestha, Annie; Rafique, Adeela

2008-01-01

In this study, a Fiber Optic Backscatter Spectroscopic Sensor (FOBSS) is used to monitor demineralization and remineralization induced changes in the enamel. A bifurcated fiber optic backscatter probe connected to a visible light source and a high resolution spectrophotometer was used to acquire the backscatter light spectrum from the tooth surface. The experiments were conducted in two parts. In Part 1, experiments were carried out using fiber optic backscatter spectroscopy on (1) sound enamel and dentine sections and (2) sound tooth specimens subjected to demineralization and remineralization. In Part 2, polarization microscopy was conducted to examine the depth of demineralization in tooth specimens. The enamel and dentine specimens from the Part-1 experiments showed distinct backscatter spectra. The spectrum obtained from the enamel-dentine combination and the spectrum generated from the average of the enamel and dentine spectral values were closely similar and showed characteristics of dentine. The experiments in Part 2 showed that demineralization and remineralization processes induced a linear decrease and linear increase in the backscatter light intensity respectively. A negative correlation between the decrease in the backscatter light intensity during demineralization and the depth of demineralization determined using the polarization microscopy was calculated to be p = -0.994. This in vitro experiment highlights the potential benefit of using FOBSS to detect demineralization and remineralization of enamel. PMID:20142887

Influence of chlorhexidine digluconate concentration and application time on resin-dentin bond strength durability.

PubMed

Loguercio, Alessandro D; Stanislawczuk, Rodrigo; Polli, Luceli G; Costa, Jully A; Michel, Milton D; Reis, Alessandra

2009-10-01

Although it is known that chlorhexidine application may preserve resin-dentin bonds from degradation, the lowest optimal concentration and application time have yet to be established. This study evaluated the effects of different concentrations of chlorhexidine digluconate and different application times on the preservation of resin-dentin bonds formed using two etch-and-rinse adhesives. In experiment 1, after acid etching, the occlusal demineralized dentin was rewetted either with water or with 0.002, 0.02, 0.2, 2, or 4% chlorhexidine for 60 s. In experiment 2, the surfaces were rewetted with water, or with 0.002% or 2% chlorhexidine for 15 or 60 s. After this, both adhesives and composite resin were applied and light-cured. Bonded sticks (0.8 mm(2)) were tested under tension (0.5 mm min(-1)) immediately or after 6 months of storage in water. Two bonded sticks from each tooth were immersed in silver nitrate and analyzed quantitatively using scanning electron microscopy. Reductions in microtensile bond strengths and higher silver nitrate uptake were observed for both adhesives when the rewetting procedure was performed with water. Stable bonds were maintained for up to 6 months under all chlorhexidine conditions tested, irrespective of the chlorhexidine concentration and application time. The use of 0.002% chlorhexidine for 15 s seems to be sufficient to preserve resin-dentin interfaces over a 6-month period.

Saliva with reduced calcium and phosphorous concentrations: Effect on erosion dental lesions.

PubMed

Denucci, Giovanna Corrêa; Mantilla, Taís Fonseca; Amaral, Flávia Lucisano Botelho; Basting, Roberta Tarkany; França, Fabiana Mantovani Gomes; Turssi, Cecilia Pedroso

2018-02-08

To investigate whether saliva formulations with reduced calcium (Ca) and inorganic phosphorous (Pi) concentration would affect dental erosion caused by hydrochloric acid (HCl). Enamel and root dentine bovine slabs were embedded, polished and measured for surface Knoop microhardness (SMH). After reference areas were created, specimens were exposed to HCl solution (0.01M; pH 2; 120s) and immersed in artificial salivas (6h) containing three different Ca/Pi concentrations (n=15), which simulate serum conditions of normo-, mild- or severe hypocalcaemia. The control group was immersed in Ca/Pi-free saliva. The study protocol was carried out 2x/day for 5 days. Surface loss of enamel and root dentine was assessed using an optical profilometer and SMH was remeasured for enamel. ANOVA (p<0.001) and Tukey's test showed that enamel loss in groups subjected to artificial salivas that simulated mild- or severe hypocalcaemia did not differ from that resembling normocalcemia. %SMH was lower when saliva was mildly- and normally-concentrated in Ca/Pi (p<0.001). Root dentine loss was higher in saliva simulating severe hypocalcaemia than in those referring to mild, hypo- and normocalcemia. Depending on the dental substrate, salivary formulations resembling serum hypocalcaemia affected surface loss due to erosion and rehardening thereof. This article is protected by copyright. All rights reserved. This article is protected by copyright. All rights reserved.

Interaction between Octenidine-based Solution and Sodium Hypochlorite: A Mass Spectroscopy, Proton Nuclear Magnetic Resonance, and Scanning Electron Microscopy-based Observational Study.

PubMed

Thaha, Khaleel Ahamed; Varma, R Luxmi; Nair, Mali G; Sam Joseph, V G; Krishnan, Unni

2017-01-01

Octenisept (OCT; Schülke & Mayr, Nordersdedt, Germany), an antimicrobial, antibiofilm agent and a promising root canal irrigant, can be potentially combined with sodium hypochlorite (NaOCl) during endodontic treatment. The aim of this study was first to identify the precipitate formed on the interaction between OCT and NaOCl and secondly to compare its effect on dentinal tubules with that of precipitate formed on combining chlorhexidine (CHX) and NaOCl. This observational study was conducted in 3 stages. Initially, the color changes and precipitate formation were assessed when the test solution 0.1% OCT and 5.2% NaOCl were mixed. Color changes were compared with those observed when 2% CHX was mixed with 5.2% NaOCl. The residue obtained on combining OCT and NaOCl was subjected to proton nuclear magnetic resonance ( 1 H NMR) and mass spectrometric (MS) analysis. In the final stage, dentinal surfaces irrigated alternatively with OCT and NaOCl were compared using scanning electron microscopy (SEM) with the dentinal surface irrigated with CHX and NaOCl. The OCT-NaOCl mixture changed in color from initial milky white to transparent over time, whereas the CHX-NaOCl mixture showed an immediate peach-brown discoloration. 1 H NMR and MS analysis established that the whitish precipitate obtained on combining OCT and NaOCl solutions correlated with the structure of phenoxyethanol (PE). SEM revealed dense precipitate occluding the dentinal tubules with the CHX and NaOCl group, whereas the precipitate was sparse and partially occluded in the OCT and NaOCl group. The whitish precipitate formed with the OCT-NaOCl mixture was identified as PE, a compound already present in OCT, and it partly occluded the dentinal tubules. Copyright © 2016 American Association of Endodontists. All rights reserved.

Effect of 5,000 ppm Fluoride Dentifrice or 1,100 ppm Fluoride Dentifrice Combined with Acidulated Phosphate Fluoride on Caries Lesion Inhibition and Repair.

PubMed

Fernández, Constanza E; Tenuta, Livia Maria Andaló; Del Bel Cury, Altair Antoninha; Nóbrega, Diego Figueiredo; Cury, Jaime Aparecido

2017-01-01

High fluoride dentifrice (FD; 5,000 ppm F) has been recommended to arrest root dentine lesions and to control enamel caries in high-risk patients. Also, standard FD (1,100 ppm F) in combination with professional fluoride application has been recommended to control dentine caries, but the effect of this combination on enamel has been considered modest. Considering the lack of evaluation comparing the use of 5,000 ppm FD (5,000-FD) versus acidulated phosphate fluoride (APF) application combined with 1,100 ppm FD (1,100-FD) on the inhibition and repair of caries lesions in both enamel and dentine, we conducted this in situ, double-blind, crossover study of 3 phases of 14 days. In each phase, 18 volunteers wore palatal appliances containing enamel and root dentine specimens, either sound or carious, to evaluate the effect of the treatments on the inhibition or repair of caries lesions, respectively. The treatments were non-FD (negative control), 5,000-FD, or 1 APF gel application on dental specimens combined with 1,100-FD used twice per day (APF + 1,100-FD). The reduction of demineralization and enhancement of remineralization were assessed by surface and cross-sectional hardness. Fluoride concentration was determined on dental specimens and on the formed biofilm. For enamel, APF + 1,100-FD and 5,000-FD did not differ regarding the inhibition of demineralization and repair of caries lesions. However, for dentine the difference between these treatments was inconclusive because while APF + 1,100-FD was more effective than 5,000-FD in caries lesion reduction and repair, 5,000-FD was more effective than APF + 1,100-FD in the reduction of surface demineralization. Therefore, the findings show that the combination of APF + 1,100-FD is as effective as 5,000-FD in enamel inhibition of demineralization and enhancement of remineralization. © 2017 S. Karger AG, Basel.

Edge chipping and flexural resistance of monolithic ceramics☆

PubMed Central

Zhang, Yu; Lee, James J.-W.; Srikanth, Ramanathan; Lawn, Brian R.

2014-01-01

Objective Test the hypothesis that monolithic ceramics can be developed with combined esthetics and superior fracture resistance to circumvent processing and performance drawbacks of traditional all-ceramic crowns and fixed-dental-prostheses consisting of a hard and strong core with an esthetic porcelain veneer. Specifically, to demonstrate that monolithic prostheses can be produced with a much reduced susceptibility to fracture. Methods Protocols were applied for quantifying resistance to chipping as well as resistance to flexural failure in two classes of dental ceramic, microstructurally-modified zirconias and lithium disilicate glass–ceramics. A sharp indenter was used to induce chips near the edges of flat-layer specimens, and the results compared with predictions from a critical load equation. The critical loads required to produce cementation surface failure in monolithic specimens bonded to dentin were computed from established flexural strength relations and the predictions validated with experimental data. Results Monolithic zirconias have superior chipping and flexural fracture resistance relative to their veneered counterparts. While they have superior esthetics, glass–ceramics exhibit lower strength but higher chip fracture resistance relative to porcelain-veneered zirconias. Significance The study suggests a promising future for new and improved monolithic ceramic restorations, with combined durability and acceptable esthetics. PMID:24139756

Primum non nocere - The effects of sodium hypochlorite on dentin as used in endodontics.

PubMed

Gu, Li-Sha; Huang, Xue-Qing; Griffin, Brandon; Bergeron, Brian R; Pashley, David H; Niu, Li-Na; Tay, Franklin R

2017-10-01

The medical literature is replete with the maxim 'primum non nocere', cautioning health care providers to avoid doing any harm to human subjects in their delivery of medical care. Sodium hypochlorite (NaOCl) is a well-established irrigant for root canal treatment because of its antimicrobial and organic tissue remnant dissolution capability. However, little is known about the deleterious effect of this strong oxidizing agent on the integrity of human mineralized dentin. Iatrogenically-induced loss of dentin integrity may precipitate post-treatment root fracture and has potential medico-legal complications. In the present work, transmission electron microscopy provided evidence for collagen destruction in the surface/subsurface of dentin treated with high NaOCl concentrations and long contact times. Size exclusion chromatography showed that the hypochlorite anion, because of its small size, penetrated the water compartments of apatite-encapsulated collagen fibrils, degraded the collagen molecules and produced a 25-35µm thick, non-uniform "ghost mineral layer" with enlarged, coalesced dentinal tubules and their lateral branches. Fourier transform-infrared spectroscopy identified increases in apatite/collagen ratio in NaOCl-treated dentin. The apatite-rich, collagen-sparse dentin matrix that remained after NaOCl treatment is more brittle, as shown by the reductions in flexural strength. Understanding the deleterious effects of NaOCl on mineralized dentin enables one to balance the risks and benefits in using high NaOCl concentrations for lengthy periods in root canal debridement. Delineating the mechanism responsible for such a phenomenon enables high molecular weight, polymeric antimicrobial and tissue dissolution irrigants to be designed that abides by the maxim of 'primum non nocere' in contemporary medical practices. The antimicrobial and tissue-dissolution capacities of NaOCl render it a well-accepted agent for root canal debridement. These highly desirable properties, however, appear to be intertwined with the untoward effect of collagen matrix degradation within mineralized dentin. Because of its small size, the hypochlorite anion is capable of infiltrating mineralized collagen and destroying the collagen fibrils, producing a mineral-rich, collagen sparse ghost mineral matrix with reduced flexural strength. Findings from the present work challenge the biosafety of NaOCl when it is used in high concentrations and for lengthy time periods during root canal treatment, and laid the background work for future biomaterials design in debridement of the canal space. Published by Elsevier Ltd.

Mechanical properties of components of the bonding interface in different regions of radicular dentin surfaces.

PubMed

Suzuki, Thaís Yumi Umeda; Gomes-Filho, João Eduardo; Gallego, Juno; Pavan, Sabrina; Dos Santos, Paulo Henrique; Fraga Briso, André Luiz

2015-01-01

The mechanical properties of the adhesive materials used in intraradicular treatments could vary according to the interaction between the restorative material and dentin substrate. An evaluation of these properties is essential to determine the success of the luting procedures performed on glass-fiber posts. The purpose of this study was to evaluate the mechanical properties of dentin adhesives, resin cements, and the dentin that underlies the bonding interface in different thirds of intraradicular dentin. Forty extracted, single-rooted human teeth were used in this study. After the endodontic treatment of the post spaces, the teeth were divided into 5 groups (n=8): Adper Single Bond 2 + RelyX ARC, Excite DSC + RelyX ARC, Adper SE Plus + RelyX ARC, RelyX Unicem, and Set. The hardness and elastic modulus values were measured at the adhesive interface in different thirds of the radicular dentin by using an ultramicrohardness tester. The data were subjected to 2-way ANOVA and the Fisher protected least significant difference test (α=.05). In the underlying dentin, the highest Martens hardness values were found in the apical region for all groups; the exceptions were the groups with the self-etching adhesive. In the adhesive layer, the highest Martens hardness values were obtained for the Adper SE Plus + RelyX ARC group; further, no statistical differences were found among the different regions for this group. RelyX ARC had the lowest Martens hardness and elastic modulus values in the apical regions when used with Adper Single Bond 2 and Adper SE Plus. No differences were found in the Martens hardness and elastic modulus values for the self-adhesive resin cement in the regions investigated. The mechanical properties of adhesive materials and the underlying dentin are influenced by the interaction between the two as well as by the depth of the analyzed intraradicular area. Copyright © 2015 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Remineralization of root caries monitored using cross polarization optical coherence tomography

NASA Astrophysics Data System (ADS)

Darling, Cynthia L.; Staninec, Michal; Chan, Kenneth H.; Kang, Hobin; Fried, Daniel

2012-01-01

Previous studies have demonstrated that polarization sensitive optical coherence tomography (PS-OCT) can be used to image caries lesions in dentin, measure nondestructively the severity of dentin demineralization, and determine the efficacy of intervention with anticaries agents including fluoride and lasers. However, those studies were limited to artificial lesions on dentin and roots surfaces. The objective of this study is to determine if a cross polarization OCT system (CP-OCT) can be used to nondestructively measure a reduction in the reflectivity of natural root caries lesions after exposure to a remineralization solution. CPOCT images of 11 teeth with existing root lesions were acquired before and after exposure to a remineralizing solution for 20 days. The integrated reflectivity was calculated after integrating to a fixed depth of 200-μm. There was a significant decrease in the integrated reflectivity after exposure to the remineralizing solution.

[Evaluation of pH variation and cervical dentin permeability in teeth submitted to bleaching treatment].

PubMed

Dezotti, Mariela S G; Souza, Mário Honorato Silva e; Nishiyama, Celso Kenji

2002-01-01

External cervical root resorption is one of the disadvantages of the bleaching procedure. There are several mechanisms that may be responsible for causing resorption, such as the chemical and physical action of the utilized materials and the morphology of the cementoenamel junction. The purpose of this study was to investigate the presence of a communication between the pulp chamber and the external root surface. The investigation was carried out by means of pH tests and measurement of dye infiltration into cervical dentin after the bleaching procedure. Thirty-four human permanent incisors were submitted to endodontic treatment. The teeth were assigned to three experimental groups, according to the level at which the filling was cut, and to the sealing of the root canal entrance with glass ionomer cement. Sodium perborate and 30% hydrogen peroxide were utilized for bleaching. pH readings were carried out after 30 minutes, 24 h, 48 h and 72 h from the beginning of the procedure. The teeth were immersed in 0.5% basic fuchsin for 24 h in order to determine possible differences in the permeability of cervical dentin. The results revealed that pH tended to change when the root filling was cut at the entrance of the canal, when 2 mm of the filling were removed, and when the canal entrance was sealed with glass ionomer. Dentinal permeability increased in the three experimental groups, in comparison with the control group. These slight differences may suggest a communication between the pulp chamber and the external root surface.

Comparing two quantitative methods for studying remineralization of artificial caries.

PubMed

Lo, E C M; Zhi, Q H; Itthagarun, A

2010-04-01

To compare the detection of changes before and after remineralization of artificial enamel and dentin caries by microCT scanning, polarized light microscopy (PLM) and transverse microradiography (TMR). Fourteen extracted premolars were cut into tooth blocks and painted with an acid-resistant varnish leaving one enamel and one dentin surface exposed. The tooth blocks were immersed into demineralizing solution for 4 days to produce artificial caries-like lesions and scanned by microCT. Then the 14 tooth blocks were randomly allocated into two groups. Seven tooth blocks in Group I were cut longitudinally through the exposed surface into 100-150 microm thick sections and microradiographs were taken. The other seven tooth blocks in Group II were left intact. All the tooth blocks and sections were then immersed into remineralizing solution for 5 days. PLM and TMR of the tooth sections in Group I were taken again. Depth of the lesion on the TMR was measured. Tooth blocks in Group II were scanned by microCT. Mean lesion depth in Group I reduced by 13.0% and 8.2% after remineralization for enamel and dentin, respectively (paired t-test, P<0.001). In Group II, linear attenuation coefficient (LAC) of the region of interest (ROI) increased by 11.1% and 23.8% after remineralization for enamel and dentin lesions, respectively (paired t-test, P<0.001). Both microCT and microradiography are able to detect a change of similar magnitude in the artificial caries lesions after remineralization. MicroCT may be used to substitute TMR and PLM in in vitro studies about caries. Copyright 2010 Elsevier Ltd. All rights reserved.

Effect of silica coating on fracture strength of glass-infiltrated alumina ceramic cemented to dentin.

PubMed

Xie, Haifeng; Zhu, Ye; Chen, Chen; Gu, Ning; Zhang, Feimin

2011-10-01

To examine the availability of sol-gel processed silica coating for alumina-based ceramic bonding, and determine which silica sol concentration was appropriate for silica coating. Sixty disks of In-Ceram alumina ceramic were fabricated and randomly divided into 5 main groups. The disks received 5 different surface conditioning treatments: Group Al, sandblasted; Group AlC, sandblasted + silane coupling agent applied; Groups Al20C, Al30C, and Al40C, sandblasted, silica coating via sol-gel process prepared using 20 wt%, 30 wt%, and 40 wt% silica sols, and then silane coupling agent applied. Before bonding, one-step adhesives were applied on pre-prepared ceramic surfaces of all groups. Then, 60 dentin specimens were prepared and conditioned with phosphoric acid and one-step adhesive. Ceramic disks of all groups were cemented to dentin specimens with dual-curing resin cements. Fracture strength was determined at 24 h and after 20 days of storage in water. Groups Al20C, Al30C, and Al40C revealed significantly higher fracture strength than groups Al and AlC. No statistically significant difference in fracture strength was found between groups Al and AlC, or among groups Al20C, Al30C, and Al40C. Fracture strength values of all the groups did not change after 20 days of water storage. Sol-gel processed silica coating can enhance fracture strength of In-Ceram alumina ceramic after bonding to dentin, and different silica sol concentrations produced the same effects. Twenty days of water storage did not decrease the fracture strength.

Effect of smear layer thickness and pH of self-adhesive resin cements on the shear bond strength to dentin.

PubMed

Ebrahimi Chaharom, Mohammad Esmaeel; Ajami, Amir Ahmad; Bahari, Mahmoud; Rezazadeh, Haleh

2017-01-01

There are concerns in relation to the bonding efficacy of self-adhesive resin cements to dentin covered with the smear layer. This study aims to evaluate the effect of smear layer thickness and different pH values of self-adhesive resin cements on the shear bond strength to dentin. The dentin on the buccal and lingual surfaces of 48 sound human premolars were abraded with 60- and 600-grit silicon carbide papers to achieve thick and thin smear layers, respectively. The samples were divided into three groups (n = 16) based on the cement pH: Rely-X Unicem (RXU) (pH < 2); Clearfil SA Luting (CSL) (pH = 3); and Speed CEM (SPC) (pH = 4.5). In each group, composite resin blocks were bonded to the buccal and lingual surfaces. After 24 h, the shear bond strength values were measured in MPa, and the failure modes were evaluated under a stereomicroscope. Data were analyzed with two-way ANOVA and post hoc least significant difference tests (P < 0.05). Cement pH had a significant effect on the shear bond strength (P = 0.02); however, the smear layer thickness had no significant effect on the shear bond strength (P > 0.05). The cumulative effect of these variables was not significant, either (P = 0.11). The shear bond strengths of SPC and CSL self-adhesive resin cements were similar and significantly lower than that of RXU. The smear layer thickness was not a determining factor for the shear bond strength value of self-adhesive resin cements.

Long-Term Effect of Erythritol on Dental Caries Development during Childhood: A Posttreatment Survival Analysis.

PubMed

Falony, Gwen; Honkala, Sisko; Runnel, Riina; Olak, Jana; Nõmmela, Rita; Russak, Silvia; Saag, Mare; Mäkinen, Pirkko-Liisa; Mäkinen, Kauko; Vahlberg, Tero; Honkala, Eino

2016-01-01

To assess the effect of daily consumption of erythritol, xylitol, and sorbitol candies on caries development in mixed dentition during a 3-year intervention and 3 years after the intervention. 485 Estonian first- and second-grade primary school children participated. Children were randomly allocated to an erythritol, xylitol, or sorbitol (control) group. Polyol-containing candies were administered on school days with a daily polyol consumption of 3 × 2.5 g. Yearly, caries development was assessed by calibrated dentists using the ICDAS criteria. Six years after initiation of the study and 3 years after cessation of daily polyol consumption, 420 participants were re-examined to identify potential long-term effects of polyol consumption. Survival curves were generated at the end of the intervention period and 3 years after intervention. The model included age of the subjects, schools, tooth surface ages and years of surface exposure to intervention. ICDAS scoring system-based events included enamel/dentin caries development, dentin caries development, increase in caries score, and dentist intervention. At the end of the intervention, time to enamel/dentin caries development, dentin caries development, increase in caries score, and dentist intervention were significantly longer in the erythritol group as compared to the sorbitol group. Except for increase in caries score, all effects persisted 3 years after cessation of daily polyol consumption. A caries-preventive effect of 3-year erythritol consumption as compared to sorbitol was established in children with mixed dentition. The effect persisted up to 3 years after the end of the intervention. © 2016 S. Karger AG, Basel.

Temperature changes across CO2-lased dentin during multiple exposures

NASA Astrophysics Data System (ADS)

Zakariasen, Kenneth L.; Barron, Joseph R.; Boran, Thomas L.

1990-06-01

The literature increasingly indicates that lasers will have a multitude of applications for dental hard tissue procedures, e.g. preventive therapy, caries removal, laser etching and endodontic therapy. However, it is critical that such laser therapies avoid the production of heat levels which will be damaging to the surrounding vital tissues, such as the dental pulp and periodontal tissues. Our preliminary research on temperature changes across C02 lased dentin indicated that for single preventive therapeutic exposures (1.2 W., 0. 1 sec., 1.0 mm focal spot) the mean temperature rise across 350 j.tm of dentin was 0.57 0C while across 1000 .tm of dentin the mean rise was only 0.18 °C. Further research utilizing multiple preventive therapeutic exposures (1.2 W., 0. 1 sec., 1.0 mm focal spot, 3 x 1.0 sec. intervals) showed mean temperature elevations of 1.56 0C across 350 m of dentin and 0.66 O across 1000 xm of dentin. While these temperature elevations, which would be associated with preventive therapy, are very low and would be biologically acceptable, it must be noted that exposures of higher intensities are required to fuse enamel and porcelain, or remove decay. This current research investigates temperature elevations which occuT during C02 lasing utilizing the following exposure parameters: 8.0 W., 1.0 mm focal spot, 0.1 sec. exposures, 2 or 4 exposures per site pulsed 1.0 sec. apart. Three dentin thicknesses were utilized, i.e. 1000 jim, 1500 p.tm and 2000 .tm. Four sections of each thickness were utilized with four exposure sites per specimen (2 with 2 exposures, 2 with 4 exposures). All dentin sections were prepared from non-carious third molars using a hard tissue microtome. A thermistor was placed on the dentin surface opposite each lased site and temperature changes were recorded for approximately 50 sec. following lasing. Mean temperature elevations ranged from a high of 3.07 C for the 1000 xm section utilizing four exposures to a low of 0.37 0C for the 2000 m section utilizing two exposures. Analysis of Variance (p < .0001) and Duncan's Multiple Range Test (p =.05) indicated significant differences existed among the mean temperature elevations observed. While significant differences in temperature elevation can be observed both by numbers of exposures and by dentin thickness, it would appear that, under the conditions of this study, the temperature changes across CO2 lased dentin are all relatively low. It should be reiterated that the lasing parameters used in this study are far in excess of those necessary for preventive applications and are, in fact, in the range of exposures which will fuse enamel and dental porcelain, or remove dental caries. The modest temperature elevations observed, combined with the relatively severe exposure parameters utilized on thin sections of dentin, demonstrate the effective protective barrier which dentin provides for the dental pulp relative to heat damage from C02 lasing.

Restorative Treatment Thresholds for Occlusal Primary Caries by Dentists in “The Dental Practice-Based Research Network”

PubMed Central

Gordan, Valeria V; Bader, James D; Garvan, Cynthia W; Richman, Joshua S; Qvist, Vibeke; Fellows, Jeffrey L; Rindal, D. Brad; Gilbert, Gregg H

2010-01-01

Objectives (1) Quantify at which carious lesion depths dentists intervene surgically for cases of varying caries penetration and caries risk; (2) Identify characteristics that are associated with surgical intervention. Methods Dentists in a practice-based research network who reported doing at least some restorative dentistry were surveyed. Dentists were asked to indicate whether they would surgically intervene in a series of cases depicting occlusal caries. Each case included a photograph of an occlusal surface displaying typical characteristics of caries penetration, and a written description of a patient at a specific level of caries risk. Using logistic regression, we analyzed associations of surgical treatment with dentist and practice characteristics, and patient caries risk levels. Results 519 DPBRN practitioner-investigators responded, of whom 63% indicated that they would surgically restore lesions located on inner enamel surfaces, and 90% of lesions located in outer dentin surfaces in a low caries risk individual. Regarding individuals at high caries risk, 77% reported that they would surgically restore inner enamel lesions and 94% reported restoring lesions located on the outer dentin surface. Dentists who did not assess caries risk were more likely to intervene on dentin lesions (p=.004). Practitioner-investigators who were in private practice were significantly more likely to intervene surgically on enamel lesions, compared to dentists from large group practices (p<.001). Conclusion Most dentists chose to provide some treatment to lesions that were within the enamel surface. Decisions to intervene surgically in the caries process differ by caries lesion depth, patient caries risk, assessment of caries risk, type of practice model, and percent of patients who self-pay. PMID:20123876

Structural changes in the irradiated dentin with Nd:YAG and Er:YAG lasers for cervical hypersensitivity treatment and their influence on the microtensile resistance in resin-dentin interface

NASA Astrophysics Data System (ADS)

Mota, Cláudia C. B. O.; Sena, Tatiane V. N. S.; Castro, Roseane F.; Araújo, Ana C. S.; Gomes, Anderson S. L.

2016-02-01

This study aimed to evaluate, in vitro, the structural changes in dentin surfaces irradiated with Er:YAG (2940 nm, 90 mJ, 2 Hz, 300 μs, spot diameter 0.9 mm, 60 s/cm2, using the handpiece at 6 cm of distance to surface) and Nd:YAG (1064 nm, 1 W, 10 Hz, 300 μs, optical fiber diameter 300 μm, 60 s/cm2, using the handpiece at 2 mm of distance to surface) lasers to the treatment of cervical hypersensitivity and the respective bond strength compromising of resin composite restorations over these surfaces. 45 bovine teeth were selected, and removed the enamel portion of the buccal surface for laser irradiation and restorative procedure. Samples were divided into three groups: G1: control, only fluoride therapy; G2: irradiated with Er:YAG laser; G3: irradiated with Nd:YAG laser. Samples were submitted to optical coherence tomography analysis and subsequently they were restored with resin composite and sectioned into sticks for microtensile tests of achievement. ANOVA analysis of variance for the maximum force (N) and strength (MPa), with a significance level of 5% was performed. It was observed that G3 presented lower performance of maximum force (38,8 +/- 11,3 N) and resistance (26,0 +/- 9,3 MPa), and the G2 presented better results (51,0 +/- 13,5 N and 36,5 +/- 10,1 MPa), but still lower than those one obtained for G1 (56,0 +/- 12,3 N and 43,5 +/- 8,6 MPa). Although both lasers are effective in the cervical hypersensitivity treatment, when the aesthetic factor is the priority, the use of Er:YAG is preferable.

Evaluation of bond strength of self-etching adhesives having different pH on primary and permanent teeth dentin.

PubMed

Ozmen, Bilal; Koyuturk, Alp Erdin; Tokay, Ugur; Cortcu, Murat; Sari, Mustafa Erhan

2015-10-16

The purpose of this in vitro study was to evaluate the dentin shear bond strength of 4 self-etching adhesives having a different pH on primary and permanent teeth dentin. The occlusal enamel was removed from 60 freshly extracted third molar and 60 primary second molar human teeth, which were randomly separated into 4 groups (n = 15). Four adhesive systems were applied: G-Bond (GC Corporation, Tokyo, Japan, pH: 1.5), Futura Bond M (Voco, Cuxhaver, Germany, pH: 1.4), Adper Prompt L-Pop (3M/ESPE, St Paul, MN, USA, pH: 0.8), and Clearfil S(3) Bond (Kuraray Medical, Tokyo, Japan, pH: 2.7) according to the manufacturer's instructions. After the application of dentin bonding agents, a composite resin material (Z250 Restorative A2, 3M ESPE, St. Paul, MN, USA) for permanent teeth and a compomer resin material (Dyract Extra A2, Dentsply, Konstanz, Germany) for primary teeth was applied onto the prepared dentin surfaces. The data were obtained by using a universal test machine at a crosshead speed of 1 mm/min. The mean values were compared using Tukey's multiple comparison test. Although there was no difference between adhesives on the permanent teeth, Clearfil S3 adhesive showed higher bond (18.07 ± 0.58 MPa) (P>0.05). Lower bond strength values were obtained from primary teeth and especially G-Bond adhesive (9.36 ± 0.48 MPa) (P<0.05). Self-etching adhesives with different pH and solvent types can be used successfully for permanent teeth dentin but adhesives with low pH did not provide greater shear bond strength values.

Fracture toughness of dentin/resin-composite adhesive interfaces.

PubMed

Tam, L E; Pilliar, R M

1993-05-01

The reliability and validity of tensile and shear bond strength determinations of dentin-bonded interfaces have been questioned. The fracture toughness value (KIC) reflects the ability of a material to resist crack initiation and unstable propagation. When applied to an adhesive interface, it should account for both interfacial bond strength and inherent defects at or near the interface, and should therefore be more appropriate for characterization of interface fracture resistance. This study introduced a fracture toughness test for the assessment of dentin/resin-composite bonded interfaces. The miniature short-rod specimen geometry was used for fracture toughness testing. Each specimen contained a tooth slice, sectioned from a bovine incisor, to form the bonded interface. The fracture toughness of an enamel-bonded interface was assessed in addition to the dentin-bonded interfaces. Tensile bond strength specimens were also prepared from the dentin surfaces of the cut bovine incisors. A minimum of ten specimens was fabricated for each group of materials tested. After the specimens were aged for 24 h in distilled water at 37 degrees C, the specimens were loaded to failure in an Instron universal testing machine. There were significant differences (p < 0.05) between the dental adhesives tested. Generally, both the fracture toughness and tensile bond strength measurements were highest for AllBond 2, intermediate for 3M MultiPurpose, and lowest for Scotchbond 2. Scanning electron microscopy of the fractured specimen halves confirmed that crack propagation occurred along the bond interface during the fracture toughness test. It was therefore concluded that the mini-short-rod fracture toughness test provided a valid method for characterization of the fracture resistance of the dentin-resin composite interface.

Potential relationship between design of nickel-titanium rotary instruments and vertical root fracture.

PubMed

Kim, Hyeon-Cheol; Lee, Min-Ho; Yum, Jiwan; Versluis, Antheunis; Lee, Chan-Joo; Kim, Byung-Min

2010-07-01

Nickel-titanium (NiTi) rotary files can produce cleanly tapered canal shapes with low tendency of transporting the canal lumen. Because NiTi instruments are generally perceived to have high fracture risk during use, new designs have been marketed to lower fracture risks. However, these design variations may also alter the forces on a root during instrumentation and increase dentinal defects that predispose a root to fracture. This study compared the stress conditions during rotary instrumentation in a curved root for three NiTi file designs. Stresses were calculated using finite element (FE) analysis. FE models of ProFile (Dentsply Maillefer, Ballaigues, Switzerland; U-shaped cross-section and constant 6% tapered shaft), ProTaper Universal (Dentsply; convex triangular cross-section with notch and progressive taper shaft), and LightSpeed LSX (Lightspeed Technology, Inc, San Antonio, TX; noncutting round shaft) were rotated within a curved root canal. The stress and strain conditions resulting from the simulated shaping action were evaluated in the apical root dentin. ProTaper Universal induced the highest von Mises stress concentration in the root dentin and had the highest tensile and compressive principal strain components at the external root surface. The calculated stress values from ProTaper Universal, which had the biggest taper shaft, approached the strength properties of dentin. LightSpeed generated the lowest stresses. The stiffer file designs generated higher stress concentrations in the apical root dentin during shaping of the curved canal, which raises the risk of dentinal defects that may lead to apical root cracking. Thus, stress levels during shaping and fracture susceptibility after shaping vary with instrument design. Copyright 2010 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

Molecular and morphological surface analysis: effect of filling pastes and cleaning agents on root dentin

PubMed Central

DAINEZI, Vanessa Benetello; IWAMOTO, Alexsandra Shizue; MARTIN, Airton Abrahão; SOARES, Luís Eduardo Silva; HOSOYA, Yumiko; PASCON, Fernanda Miori; PUPPIN-RONTANI, Regina Maria

2017-01-01

Abstract The quality of the dentin root is the most important factor for restoration resin sealing and drives the outcome of endodontic treatment. Objective This study evaluated the effect of different filling pastes and cleaning agents on the root dentin of primary teeth using Fourier-transformed Raman spectroscopy (FT-Raman), micro energy-dispersive X-ray fluorescence (µ-EDXRF) and scanning electron microscopic (SEM) analysis. Material and Methods Eighty roots of primary teeth were endodontically prepared and distributed into 4 groups and filled according to the following filling pastes: Control-no filling (CP), Calen®+zinc oxide (CZ), Calcipex II® (CII), Vitapex® (V). After seven days, filling paste groups were distributed to 4 subgroups according to cleaning agents (n=5): Control-no cleaning (C), Ethanol (E), Tergenform® (T), 35% Phosphoric acid (PA). Then, the roots were sectioned and the dentin root sections were internally evaluated by FT-Raman, µ-EDXRF and SEM. Data was submitted to two-way ANOVA and Tukey tests (α=0.05). Results Regarding filling pastes, there was no significant difference in organic content. CP provided the lowest calcium values and, calcium/phosphoric ratio (Ca/P), and the highest phosphoric values. For cleaning agents there was no difference in organic content when compared to the C; however, T showed significantly higher calcium and Ca/P than PA. All groups showed similar results for phosphorus. The dentin smear layer was present after use of the cleaning agents, except PA. Conclusion The filling pastes changed the inorganic content, however they did not change the organic content. Cleaning agents did not alter the inorganic and organic content. PA cleaned and opened dentin tubules. PMID:28198982

Influence of Smear Layer on the Antimicrobial Activity of a Sodium Hypochlorite/Etidronic Acid Irrigating Solution in Infected Dentin.

PubMed

Morago, Ana; Ordinola-Zapata, Ronald; Ferrer-Luque, Carmen María; Baca, Pilar; Ruiz-Linares, Matilde; Arias-Moliz, María Teresa

2016-11-01

The aim of this study was to evaluate the influence of the smear layer on the antimicrobial activity of a 2.5% sodium hypochlorite (NaOCl)/9% etidronic acid (HEBP) irrigating solution against bacteria growing inside dentin tubules. Dentin tubules were infected with Enterococcus faecalis by centrifugation. After 5 days of incubation, the smear layer had formed in half of the samples, which were then treated with 2.5% NaOCl either alone or combined with 9% HEBP for 3 minutes. The percentage of dead cells in infected dentinal tubules was measured using confocal laser scanning microscopy and the live/dead technique. The smear layer on the surface of the root canal wall was also observed by scanning electron microscopy. Results of the percentage of dead cells were compared using parametric tests after subjecting data to the normalized Anscombe transformation. The level of significance was P < .05. In the absence of the smear layer, 2.5% NaOCl alone and combined with 9% HEBP showed high antimicrobial activity without significant differences between the 2. The smear layer reduced the antimicrobial activity of 2.5% NaOCl significantly, whereas the solution with HEBP was not affected. No dentin tubules free of the smear layer were obtained in the 2.5% NaOCl group. In the case of 2.5% NaOCl/9% HEBP, 95.40% ± 3.63% of dentin tubules were cleaned. The presence of the smear layer reduced the antimicrobial activity of 2.5% NaOCl. The combination of 2.5% NaOCl/9% HEBP exerted antimicrobial activity that was not reduced by the smear layer. Copyright © 2016 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

Effect of a single application of TiF(4) and NaF varnishes and solutions on dentin erosion in vitro.

PubMed

Magalhães, Ana Carolina; Levy, Flávia Mauad; Rios, Daniela; Buzalaf, Marília Afonso Rabelo

2010-02-01

This in vitro study aimed to analyse the effect of a single application of TiF(4) and NaF varnishes and solutions to protect against dentin erosion. Bovine root dentin samples were pre-treated with NaF-Duraphat varnish (2.26%F, pH 4.5), NaF/CaF(2)-Duofluorid varnish (5.63%F, pH 8.0), NaF-experimental varnish (2.45%F, pH 4.5), TiF(4)-experimental varnish (2.45%F, pH 1.2), NaF solution (2.26%F, pH 4.5), TiF(4) solution (2.45%F, pH 1.2) and placebo varnish (pH 5.0, no-F varnish control). Controls remained untreated. Ten samples in each group were then subjected to an erosive demineralisation (Sprite Zero, 4x 90s/day) and remineralisation (artificial saliva, between the erosive cycles) cycling for 5 days. Dentin loss was measured profilometrically after pre-treatment and after 1, 3 and 5 days of de-remineralisation cycling. The data were statistically analysed by two-way ANOVA and Bonferroni's post hoc test (p<0.05). After pre-treatment, TiF(4) solution significantly induced surface loss (1.08+/-0.53 microm). Only Duraphat reduced the dentin loss overtime, but it did not significantly differ from placebo varnish (at 3rd and 5th days) and TiF(4) varnish (at 3rd day). Duraphat varnish seems to be the best option to partially reduce dentin erosion. However, the maintenance of the effects of this treatment after successive erosive challenges is limited. Copyright 2009 Elsevier Ltd. All rights reserved.

Effect of Nd:YAG Laser Irradiation on the Number of Open Dentinal Tubules and Their Diameter with and without Smear of Graphite: An in Vitro Study

PubMed Central

Maleki-pour, Mohammad Reza; Birang, Reza; Khoshayand, Maryam; Naghsh, Narges

2015-01-01

Introduction: Dentin hypersensitivity (DH) is characterized by tooth pain arising from exposure of dental roots. In this study the efficiency of neodymium yttrium-aluminum-garnet (Nd:YAG) laser in association with graphite on dentinal surface changes as the alternative to the treatment of DH was evaluated. Methods: Sixteen noncarious human third molars were collected and sectioned into 5 parts from cementoenamel junction (CEJ) to the furcation area. The prepared samples were randomly assigned into five groups (Gs) of each 16: Control (G1), treated by Nd:YAG laser at 0.5 W (G2), irradiation of Nd:YAG with a 0.25 W output power(G3), smeared with graphite and then using Nd:YAG laser at output powers of 0.5 W (G4) and 0.25 W (G5). For all groups the parameters were 15 Hz, 60 s, at two stages and with a right angle irradiation. The number and diameter of dentinal tubules (DT) were compared and analyzed by SPSS software, One way ANOVA and Post hoc LSD tests. Results:The number of open dentinal tubules varied significantly between all groups except among G1 with G3 and G2 with G5. Multiple comparison tests also exhibited significant differences regarding the diameter of tubules between the groups two by two except among G2 with G5. Conclusion: Nd:YAG laser used at 0.25 W and 0.5 W with application of graphite smear was able to reduce the number and diameter of dentinal tubules. PMID:25699166

Starch Combined with Sucrose Provokes Greater Root Dentine Demineralization than Sucrose Alone.

PubMed

Souza, Samilly Evangelista; Sampaio, Aline Araújo; Del Bel Cury, Altair Antoninha; Cavalcanti, Yuri Wanderley; Ricomini Filho, Antônio Pedro; Cury, Jaime Aparecido

2018-02-14

Since there is no consensus about whether starch increases the cariogenic potential of sucrose, we used a validated 3-species biofilm model to evaluate if starch combined with sucrose provokes higher root dentine demineralization than sucrose alone. Biofilms (n = 18) composed by Streptococcus mutans (the most cariogenic bacteria), Actinomces naeslundii (which has amylolytic activity), and Streptococcus gordonii (which binds salivary amylase) were formed on root dentine slabs under exposure 8 ×/day to one of the following treatments: 0.9% NaCl, 1% starch, 10% sucrose, or a combination of 1% starch and 10% sucrose. Before each treatment, biofilms were pretreated with human whole saliva for 1 min. The pH of the culture medium was measured daily as an indicator of biofilm acidogenicity. After 96 h of growth, the biofilms were collected, and the biomass, bacteria viability, and polysaccharides were analyzed. Dentine demineralization was assessed by surface hardness loss (% SHL). Biofilm bioarchitecture was analyzed using confocal laser scanning microscopy. Treatment with a starch and sucrose combination provoked higher (p = 0.01) dentine demineralization than sucrose alone (% SHL = 53.2 ± 7.0 vs. 43.2 ± 8.7). This was supported by lower pH values (p = 0.007) of the culture medium after daily exposure to the starch and sucrose combination compared with sucrose (4.89 ± 0.29 vs. 5.19 ± 0.32). Microbiological and biochemical findings did not differ between biofilms treated with the combination of starch and sucrose and sucrose alone (p > 0.05). Our findings give support to the hypothesis that a starch and sucrose combination is more cariogenic for root dentine than sucrose alone. © 2018 S. Karger AG, Basel.

Effect of high energy X-ray irradiation on the nano-mechanical properties of human enamel and dentine.

PubMed

Liang, Xue; Zhang, Jing Yang; Cheng, Iek Ka; Li, Ji Yao

2016-01-01

Radiotherapy for malignancies in the head and neck can cause common complications that can result in tooth damage that are also known as radiation caries. The aim of this study was to examine damage to the surface topography and calculate changes in friction behavior and the nano-mechanical properties (elastic modulus, nanohardness and friction coefficient) of enamel and dentine from extracted human third molars caused by exposure to radiation. Enamel and dentine samples from 50 human third molars were randomly assigned to four test groups or a control group. The test groups were exposed to high energy X-rays at 2 Gy/day, 5 days/week for 5 days (10 Gy group), 15 days (30 Gy group), 25 days (50 Gy group), 35 days (70 Gy group); the control group was not exposed. The nanohardness, elastic modulus, and friction coefficient were analyzed using a Hysitron Triboindenter. The nano-mechanical properties of both enamel and dentine showed significant dose-response relationships. The nanohardness and elastic modulus were most variable between 30-50 Gy, while the friction coefficient was most variable between 0-10 Gy for dentine and 30-50 Gy for enamel. After exposure to X-rays, the fracture resistance of the teeth clearly decreased (rapidly increasing friction coefficient with increasing doses under the same load), and they were more fragile. These nano-mechanical changes in dental hard tissue may increase the susceptibility to caries. Radiotherapy caused nano-mechanical changes in dentine and enamel that were dose related. The key doses were 30-50 Gy and the key time points occurred during the 15th-25th days of treatment, which is when application of measures to prevent radiation caries should be considered.

The Effect of Chemically Modified Tetracycline-3 on the Progression of Dental Caries in Rats.

PubMed

Xu, Jun; Miao, Congcong; Tian, Zhenchuan; Li, Jinlu; Zhang, Chunmei; Yang, Dongmei

2018-02-07

Matrix metalloproteinases (MMPs) exist in human saliva and dentin and play an important role in the degradation of organic matrix in teeth. Chemically modified tetracycline-3 (CMT-3) is an inhibitor of MMPs. CMT-3 has been used experimentally to treat caries since 1999, but no distinction between dental caries prevalence and dentin caries prevalence has been described. A total of 65 Sprague-Dawley rats were randomly divided into three groups. The positive control group (25 rats) was inoculated with Streptococcus mutans (ATCC700610) and fed the cariogenic feed of improved Keyes Diet 2000. The CMT-3 group (25 rats) was also inoculated with S. mutans and fed the cariogenic feed of improved Keyes Diet 2000; the surfaces of rats' molars were daily treated with 0.02% CMT-3. The negative control group (15 rats) was only fed the standard rodent chow. At the end of the 10th week, the dental caries prevalence and dentin caries prevalence of each group were calculated, and the regions of caries were assessed. No caries was found in the negative control group. The dental caries prevalence of the CMT-3 and the positive control group was 75.0 and 83.3%, respectively (p > 0.05, Table 2). The dentin caries prevalence of the CMT-3 and the positive control group was 33.3 and 70.8%, respectively (p < 0.05, Table 2). The Keyes scoring of dentin caries in the CMT-3 group was significantly lower than that in the positive control group (p < 0.05, Table 3). CMT-3 had no effect on the prevalence of dental caries, but could lower the prevalence and slow down the progression of dentin caries. © 2018 S. Karger AG, Basel.

Ozone Gas Effect on Mineral Content of Dentin exposed to Streptococcus mutans Biofilm: An Energy-dispersive X-ray Evaluation.

PubMed

Chaves, Rafaella M; Estrela, Carlos; Cardoso, Paula C; de Je Barata, Terezinha; de Souza, João B; de Torres, Érica M; Estrela, Cyntia Ra; Magalhães, Ana Pr; Lopes, Lawrence G

2017-04-01

This study aims to assess the effect of ozone gas on dentin exposed to Streptococcus mutans biofilm by evaluation of mineral content [log calcium-to-phosphorus (Ca/P)] using energy-dispersive X-ray (EDX) spectroscopy. Five human third molars were sectioned into four slices of dentin and distributed in four groups: I - control (no treatment); II - ozone therapy; III - biofilm development; IV - ozone therapy followed by biofilm development. Mineral content (log Ca/P) was evaluated by EDX. Data were analyzed by analysis of variance and Tukey's test (p < 0.05). Results showed that the mineral content of control group (I) was similar to ozone group (II), and was statistically higher than biofilm (III) and ozone + biofilm (IV). The lowest log Ca/P was determined in biofilm group (III). It can be concluded that ozone gas did not grant preventive effects of demineralization by S. mutans biofilm on dentin surface. Ozone gas therapy may be an alternative noninvasive treatment aiming to reduce the levels of caries-associated microorganisms. This therapy may, thereby, be an alternative and/or complementary treatment strategy in preventive dentistry.

[Effects of different surface modifications on micro-structure and adhesion of zirconia ceramic: an in vitro study].

PubMed

Siwen, Li; Shishi, Li; Yanhong, Wang; Hongmei, Ma

2017-02-01

This study evaluated the effect of different mechanical-chemical surface treatments on the characteristics, microstructure, and composition of zirconia ceramics and on the zirconia-dentin adhesion. The sintered commercial zirconia blocks (IPS e.max ZirCAD) were sectioned into 126 beams (6 mm×6 mm×5 mm) and randomly assigned to seven experimental groups (n=18). The zirconia block specimens were further treated as follows: (A) untreated, as control; (B) sandblasted with 50 μm Al2O3; (C) sandblasted with 50 μm Al2O3+30 μm silica powder; (D) sandblasted with 50 μm Al2O3+30% silica-sol coating; (E) sandblasted with 110 μm Al2O3; (F) sandblasted with 110 μm Al2O3+30 μm silica powder; and (G) sandblasted with 110 μm Al2O3+30% silica-sol coating. The surface roughness (Ra) of zirconia ceramics using X-ray diffraction (XRD), field emission scanning electron microscopy (SEM), and energy dispersive X-ray spectroscopy (EDX) after seven surface treatments was analyzed. Seventy specimens of dentin surfaces were prepared. A dual-cure resin cement was applied into zirconia surfaces with its corresponding adhesive components to dentin. Shear bond strength (SBS) of each sample was measured using a universal testing machine. The data were analyzed by ANOVA using SPSS 17.0 software. Ra of zirconia were significantly different compared with the control group (P<0.05). The crystalline transformation from tetragonal phase to monoclinic phase was observed after surface modification. Monoclinic volume content of the heat-treated group was highest than that in other groups. The content of element Si in the heat-treated group was higher than that in other treatment groups accompanied by a decrease in elements Zr, Y, and Hf after being treated by two silica-coating methods. Air abrasion significantly increased the micro-cracks in the ceramic surface and caused the grain boundaries to disappear. A serious shrinkage of the thin silica film can be observed after sintering procedure. This process induced cracks and the film to strip away slightly from the surfaces of Y-TZP substrate. The SBS values from large to small were F and G groups, C and D groups, B and E groups (P<0.05), and control group (P<0.05). Alumina sandblasting, silica powder abrasion, and silica-sol coating affect the surface morphology, structure, and composition of the tooth. This effect can also achieve the improved micro-mechanical interlocking or chemical bonding and finally increase the bond strength between zirconia and tooth. Alumina sandblasting followed by silica coating is an effective technique to increase the bonding strength between the zirconia ceramic and dentin.
.

Water interaction and bond strength to dentin of dye-labelled adhesive as a function of the addition of rhodamine B.

PubMed

Wang, Linda; Bim, Odair; Lopes, Adolfo Coelho de Oliveira; Francisconi-Dos-Rios, Luciana Fávaro; Maenosono, Rafael Massunari; D'Alpino, Paulo Henrique Perlatti; Honório, Heitor Marques; Atta, Maria Teresa

2016-01-01

This study investigated the effect of the fluorescent dye rhodamine B (RB) for interfacial micromorphology analysis of dental composite restorations on water sorption/solubility (WS/WSL) and microtensile bond strength to dentin (µTBS) of a 3-step total etch and a 2-step self-etch adhesive system. The adhesives Adper Scotchbond Multi-Purpose (MP) and Clearfil SE Bond (SE) were mixed with 0.1 mg/mL of RB. For the WS/WSL tests, cured resin disks (5.0 mm in diameter x 0.8 mm thick) were prepared and assigned into four groups (n=10): MP, MP-RB, SE, and SE-RB. For µTBS assessment, extracted human third molars (n=40) had the flat occlusal dentin prepared and assigned into the same experimental groups (n=10). After the bonding and restoration procedures, specimens were sectioned in rectangular beams, stored in water and tested after seven days or after 12 months. The failure mode of fractured specimens was qualitatively evaluated under optical microscope (x40). Data from WS/WSL and µTBS were assessed by one-way and three-way ANOVA, respectively, and Tukey's test (α=5%). RB increased the WSL of MP and SE. On the other hand, WS of both MP and SE was not affected by the addition of RB. No significance in µTBS between MP and MP-RB for seven days or one year was observed, whereas for SE a decrease in the µTBS means occurred in both storage times. RB should be incorporated into non-simplified DBSs with caution, as it can interfere with their physical-mechanical properties, leading to a possible misinterpretation of bonded interface.

Water interaction and bond strength to dentin of dye-labelled adhesive as a function of the addition of rhodamine B

PubMed Central

WANG, Linda; BIM, Odair; LOPES, Adolfo Coelho de Oliveira; FRANCISCONI-DOS-RIOS, Luciana Fávaro; MAENOSONO, Rafael Massunari; D’ALPINO, Paulo Henrique Perlatti; HONÓRIO, Heitor Marques; ATTA, Maria Teresa

2016-01-01

ABSTRACT Objective This study investigated the effect of the fluorescent dye rhodamine B (RB) for interfacial micromorphology analysis of dental composite restorations on water sorption/solubility (WS/WSL) and microtensile bond strength to dentin (µTBS) of a 3-step total etch and a 2-step self-etch adhesive system. Material and Methods The adhesives Adper Scotchbond Multi-Purpose (MP) and Clearfil SE Bond (SE) were mixed with 0.1 mg/mL of RB. For the WS/WSL tests, cured resin disks (5.0 mm in diameter x 0.8 mm thick) were prepared and assigned into four groups (n=10): MP, MP-RB, SE, and SE-RB. For µTBS assessment, extracted human third molars (n=40) had the flat occlusal dentin prepared and assigned into the same experimental groups (n=10). After the bonding and restoration procedures, specimens were sectioned in rectangular beams, stored in water and tested after seven days or after 12 months. The failure mode of fractured specimens was qualitatively evaluated under optical microscope (x40). Data from WS/WSL and µTBS were assessed by one-way and three-way ANOVA, respectively, and Tukey’s test (α=5%). Results RB increased the WSL of MP and SE. On the other hand, WS of both MP and SE was not affected by the addition of RB. No significance in µTBS between MP and MP-RB for seven days or one year was observed, whereas for SE a decrease in the µTBS means occurred in both storage times. Conclusions RB should be incorporated into non-simplified DBSs with caution, as it can interfere with their physical-mechanical properties, leading to a possible misinterpretation of bonded interface. PMID:27556201

Curing mode affects bond strength of adhesively luted composite CAD/CAM restorations to dentin.

PubMed

Lührs, Anne-Katrin; Pongprueksa, Pong; De Munck, Jan; Geurtsen, Werner; Van Meerbeek, Bart

2014-03-01

To determine the effect of curing mode and restoration-surface pre-treatment on the micro-tensile bond strength (μTBS) to dentin. Sandblasted CAD/CAM composite blocks (LAVA Ultimate, 3M ESPE) were cemented to bur-cut dentin using either the etch & rinse composite cement Nexus 3 ('NX3', Kerr) with Optibond XTR ('XTR', Kerr), or the self-etch composite cement RelyX Ultimate ('RXU', 3M ESPE) with Scotchbond Universal ('SBU', 3M ESPE). All experimental groups included different 'curing modes' (light-curing of adhesive and cement ('LL'), light-curing of adhesive and auto-cure of cement ('LA'), co-cure of adhesive through light-curing of cement ('AL'), or complete auto-cure ('AA')) and different 'restoration-surface pre-treatments' of the composite block (NX3: either a silane primer (Kerr), or the XTR adhesive; RXU: either silane primer (RelyX Ceramic Primer, 3M ESPE) and SBU, or solely SBU). After water-storage (7 days, 37°C), the μTBS was measured. Additionally, the degree of conversion (DC) of both cements was measured after 10min and after 1 week, either auto-cured (21°C/37°C) or light-cured (directly/through 3-mm CAD/CAM composite). The linear mixed-effects model (α=0.05) revealed a significant influence of the factors 'curing mode' and 'composite cement', and a less significant effect of the factor 'restoration-surface pre-treatment'. Light-curing 'LL' revealed the highest μTBS, which decreased significantly for all other curing modes. For curing modes 'AA' and 'AL', the lowest μTBS and a high percentage of pre-testing failures were reported. Overall, DC increased with light-curing and incubation time. The curing mode is decisive for the bonding effectiveness of adhesively luted composite CAD/CAM restorations to dentin. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Microtensile bond strength analysis of adhesive systems to Er:YAG and Er,Cr:YSGG laser-treated dentin.

PubMed

Ramos, Thaysa Monteiro; Ramos-Oliveira, Thayanne Monteiro; Moretto, Simone Gonçalves; de Freitas, Patricia Moreira; Esteves-Oliveira, Marcella; de Paula Eduardo, Carlos

2014-03-01

The aim of this in vitro study was to evaluate the effect of different surface treatments (control, diamond bur, erbium-doped yttrium aluminum garnet (Er:YAG) laser, and erbium, chromium:yttrium-scandium-gallium-garnet (Er,Cr:YSGG) laser) on sound dentin surface morphology and on microtensile bond strength (μTBS). Sixteen dentin fragments were randomly divided into four groups (n = 4), and different surface treatments were analyzed by scanning electron microscopy. Ninety-six third molars were randomly divided into eight groups (n = 12) according to type of surface treatment and adhesive system: G1 = Control + Clearfil SE Bond (SE); G2 = Control + Single Bond (SB); G3 = diamond bur (DB) + SE; G4 = DB + SB, G5 = Er:YAG laser (2.94 μm, 60 mJ, 2 Hz, 0.12 W, 19.3 J/cm(2)) + SE; G6 = Er:YAG + SB, G7 = Er,Cr:YSGG laser (2.78 μm, 50 mJ, 30 Hz, 1.5 W, 4.5 J/cm(2)) + SE; and G8 = Er,Cr:YSGG + SB. Composite blocks were bonded to the samples, and after 24-h storage in distilled/deionized water (37 °C), stick-shaped samples were obtained and submitted to μTBS test. Bond strength values (in megapascal) were analyzed by two-way ANOVA and Tukey tests (α = 0.05). G1 (54.69 ± 7.8 MPa) showed the highest mean, which was statistically significantly higher than all the other groups (p < 0.05). For all treatments, SE showed higher bond strength than SB, except only for Er,Cr:YSGG treatment, in which the systems did not differ statistically from each other. Based on the irradiation parameters considered in this study, it can be concluded that Er:YAG and Er,Cr:YSGG irradiation presented lower values than the control group; however, their association with self-etching adhesive does not have a significantly negative effect on sound dentin (μTBS values of >20 MPa).

Effects of blood contamination on microtensile bond strength to dentin of three self-etch adhesives.

PubMed

Chang, Seok Woo; Cho, Byeong Hoon; Lim, Ran Yeob; Kyung, Seung Hyun; Park, Dong Sung; Oh, Tae Seok; Yoo, Hyun Mi

2010-01-01

This study evaluated the effects of blood contamination and decontamination methods during different steps of bonding procedures on the microtensile bond strength of two-step self-etch adhesives to dentin. Sixty extracted human molars were ground flat to expose occlusal dentin. The 60 molars were randomly assigned to three groups, each treated with a different two-step self-etch adhesive: Clearfil SE Bond, AdheSE and Tyrian SPE. In turn, these groups were subdivided into five subgroups (n = 20), each treated using different experimental conditions as follows: control group-no contamination; contamination group 1-CG1: primer application/ contamination/primer re-application; contamination group 2-CG2: primer application/contamination/wash/dry/primer re-application; contamination group 3-CG3: primer application/adhesive application/light curing/contamination/ adhesive re-application/light curing; contamina- tion group 4-CG4: primer application/adhesive application/light curing/contamination/wash/ dry/adhesive re-application/light curing. Composite buildup was performed using Z250. After 24 hours of storage in distilled water at 37 degrees C, the bonded specimens were trimmed to an hourglass shape and serially sectioned into slabs with 0.6 mm2 cross-sectional areas. Microtensile bond strengths (MTBS) were assessed for each specimen using a universal testing machine. The data were analyzed by two-way ANOVA followed by a post hoc LSD test. SEM evaluations of the fracture modes were also performed. The contaminated specimens showed lower bond strengths than specimens in the control group (p < 0.05), with the exception of CG1 in the Clearfil SE group and CG2 and CG3 in the Tyrian SPE group. Among the three self-etch adhesives, the Tyrian SPE group exhibited a significantly lower average MTBS compared to the Clearfil SE Bond and AdheSE (p < 0.05) groups. Based on the results of the current study, it was found that blood contamination reduced the MTBS of all three self-etch adhesives to dentin, and water-rinsing was unable to overcome the effects of blood contamination.