Influence of cobalt on structural and magnetic properties of nickel ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Ati, Ali A.; Othaman, Zulkafli; Samavati, Alireza

2013-11-01

Improving the magnetic response of nanocrystalline nickel ferrites is the key issue in high density recording media. A series of cobalt substituted nickel ferrite nanoparticles with composition Ni(1-x)CoxFe2O4, where 0.0 ⩽ x ⩽ 1.0, are synthesized using co-precipitation method. The XRD spectra revealed the single phase spinel structure and the average sizes of nanoparticles are estimated to be 16-19 nm. These sizes are small enough to achieve the suitable signal to noise ratio in the high density recording media. The lattice parameter and coercivity shows monotonic increment with the increase of Co contents ascribed to the larger ionic radii of the cobalt ion. The specific saturation magnetization (Ms), remanent magnetization (Mr) and the coercivity (Hc) of the spinel ferrites are further improved by the substitutions of Co+2 ions. The values of Ms for NiFe2O4 and CoFe2O4 are found to be 43.92 and 78.59 emu/g, respectively and Hc are in the range of 51-778 Oe. The FTIR spectra of the spinel phase calcinated at 600 °C exhibit two prominent fundamental absorption bands in the range of 350-600 cm-1 assigned to the intrinsic stretching vibrations of the metal at the tetrahedral and octahedral sites. The role played by the Co ions in improving the structural and magnetic properties are analyzed and understood. Our simple, economic and environmental friendly preparation method may contribute towards the controlled growth of high quality ferrite nanopowders, potential candidates for recording.

Modification of Co/Cu nanoferrites properties via Gd3+/Er3+doping

NASA Astrophysics Data System (ADS)

Ateia, Ebtesam E.; Soliman, Fatma S.

2017-05-01

Pure nanoparticles of the rare earth-substituted cobalt and copper ferrites with general formula Me Gd0.025 Er0.05 Fe1.925 O4 (Me = Co, Cu) were prepared by the chemical citrate method. X-ray diffraction, field emission scanning electron microscopy, BET analysis are utilized to study the effect of rare earth substitution and its impact on the physical properties of the investigated samples. Rare earth-doped cobalt shows type IV isotherm suggesting mesopore structure with its hysteresis loop. The estimated crystallite sizes are found in the range of 21.49 and 36.11 nm for the doped Co and Cu samples, respectively. The magnetic properties of rare earth-substituted cobalt and copper ferrites showed a definite hysteresis loop at room temperature. An increase in coercivity and a decrease in saturation magnetization were detected. This can be explained in view of weaker nature of the Re3+-Fe3+ interaction compared to Fe3+-Fe3+ interaction. Greater than 1.13-fold increase in coercivity (Hc = 2184 Oe) was observed in doped cobalt nanoferrite samples compared to copper (Hc = 1936 Oe). It was found that the decreasing in temperature leads to great improvement in the magnetic properties of the investigated samples. As the magnetic recording performance of the magnetic samples is improved for well-crystallized samples with nano-structural, the effect of rare earth substitution seems to be particularly valuable in this regard.

High-Temperature Thermoelectric and Microstructural Characteristics of Cobalt-Based Oxides with Ga Substituted on the Co-Site

NASA Astrophysics Data System (ADS)

Nong, N. V.; Yanagiya, S.; Monica, S.; Pryds, N.; Ohtaki, M.

2011-05-01

The effects of Ga substitution on the Co-site on the high-temperature thermoelectric properties and microstructure are investigated for the misfitlayered Ca3Co4O9 and the complex perovskite-related Sr3RECo4O10.5 (RE = rare earth) cobalt-based oxides. For both systems, substitution of Ga for Co results in a simultaneous increase in the Seebeck coefficient ( S) and the electrical conductivity ( σ), and the influence is more significant in the high temperature region. The power factor ( S 2 σ) is thereby remarkably improved by Ga substitution, particularly at high temperatures. Texture factor calculations using x-ray diffraction pattern data for pressed and powder samples reveal that the Ga-doped samples are highly textured. Microstructure observed by scanning electron microscopy shows very well-crystallized grains for the samples with Ga substitution for Co. Among the Ga-doped samples, Ca3Co3.95Ga0.05O9 shows the best ZT value of 0.45 at 1200 K, which is about 87.5% higher than the nondoped one, a considerable improvement.

Lanthanum ion substituted cobalt ferrite nanoparticles and their hyperthermia efficiency

NASA Astrophysics Data System (ADS)

Demirci, Ç. E.; Manna, P. K.; Wroczynskyj, Y.; Aktürk, S.; van Lierop, J.

2018-07-01

We investigated the structural, compositional, and magnetic properties as well as the AC magnetic hyperthermic response of CoFe2-xLaxO4 (x = 0.0, 0.2, 0.5) nanoparticles. We found that the La3+ ions substituted into the Fe3+ ion sites, and resulted in an increased magnetocrystalline anisotropy with x, and altered the time-dependent magnetism. To provide a better understanding of the AC magnetic hyperthermia response, a series of temperature versus time measurements were done by varying the magnetic field amplitude, the carrier medium viscosity and the concentration of the nanoparticles as parameters that governed the heating efficiency. A decrease of specific loss power was observed with an increase of the viscosity of the carrier medium for x = 0 and x = 0.25 substituted Co-ferrite nanoparticles, while a small increase was observed with the x = 0.1 La3+ substituted Co-ferrite nanoparticles (due to their higher intrinsic magnetocrystalline anisotropy).

Progression in structural, magnetic and electrical properties of La-doped group IV elements

NASA Astrophysics Data System (ADS)

Deepapriya, S.; Annie Vinosha, P.; Rodney, John D.; Jerome Das, S.

2018-04-01

Progression of group IV elements such as zinc ferrite (ZnFe2O4), cobalt ferrite (CoFe2O4) was synthesized by doping lanthanum (La), via adopting a facile co-precipitation method. Doping hefty rare earth ion in spinel structure can amend to the physical properties of the lattice, which can be used in the enhancement of magnetic and electrical properties of the as-synthesized nanomaterial, it is vital to metamorphose and optimize its micro structural and magnetic features. The structural properties of the samples was analysed by powder X-ray diffraction (XRD), Fourier transform infrared (FTIR), Transmission electron microscopy (TEM) and UV-visible spectral analysis (UV-vis) reveals the optical property and optical band gap. The magnetic properties were evaluated using a vibrating sample magnetometer (VSM), the presence of functional group was confirmed by FTIR. XRD analyses elucidates that the synthesized samples zinc and cobalt had a spinel structure. From TEM analyses the morphology and diameter of the particle was observed. The substituted rare earth ions in Zinc ferrite inhibit the grain growth of the materials in an efficient manner compared with that of the Cobalt ferrite.

Investigation of structural, magnetic and dielectric properties of Cr3+ substituted Cu0.75Co0.25Fe2-xO4 ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Reddi, M. Sushma; Ramesh, M.; Sreenivasu, T.; Rao, G. S. N.; Samatha, K.

2018-05-01

Chromium doped Copper-Cobalt ferrite Nanoparticles were obtained by sol-gel auto-combustion method using citric acid as a fuel. The metal nitrates to citric acid ratio was taken as 1:1. The prepared powder of Cr3+ doped copper-cobalt ferrite nanoparticles is annealed at 600°C for 5 hrs and the same powder was used for characterization and investigations of structural properties. The phase composition, micro-structural, micro morphological and elemental analysis studies were carried out by X-ray diffraction (XRD), scanning electron microscope (SEM) technique and energy dispersive spectroscopy (EDS). The FTIR spectra of these samples are recorded to ensure the presence of the metallic compounds. The average crystallite size obtained by Scherrer's formula is of the order of 19.28 nm to 32.92 nm. The dielectric properties are investigated as a function of frequency at room temperature using LCR-Q meter. The saturation magnetization (Ms) of the Cr3+ substituted Cu-Co ferrite sintered at 1100°C lies in the range of 5.4136-28.9943 emu/g, the coercivity (Hc) dropped desperately from about 2091.3-778.53Oe as Cr3+ composition increases from 0.0 to 0.25.

Controlled cobalt doping in biogenic magnetite nanoparticles.

PubMed

Byrne, J M; Coker, V S; Moise, S; Wincott, P L; Vaughan, D J; Tuna, F; Arenholz, E; van der Laan, G; Pattrick, R A D; Lloyd, J R; Telling, N D

2013-06-06

Cobalt-doped magnetite (CoxFe3 -xO4) nanoparticles have been produced through the microbial reduction of cobalt-iron oxyhydroxide by the bacterium Geobacter sulfurreducens. The materials produced, as measured by superconducting quantum interference device magnetometry, X-ray magnetic circular dichroism, Mössbauer spectroscopy, etc., show dramatic increases in coercivity with increasing cobalt content without a major decrease in overall saturation magnetization. Structural and magnetization analyses reveal a reduction in particle size to less than 4 nm at the highest Co content, combined with an increase in the effective anisotropy of the magnetic nanoparticles. The potential use of these biogenic nanoparticles in aqueous suspensions for magnetic hyperthermia applications is demonstrated. Further analysis of the distribution of cations within the ferrite spinel indicates that the cobalt is predominantly incorporated in octahedral coordination, achieved by the substitution of Fe(2+) site with Co(2+), with up to 17 per cent Co substituted into tetrahedral sites.

Effect of cobalt doping level of ferrites in enhancing sensitivity of analytical performances of carbon paste electrode for simultaneous determination of catechol and hydroquinone.

PubMed

Lakić, Mladen; Vukadinović, Aleksandar; Kalcher, Kurt; Nikolić, Aleksandar S; Stanković, Dalibor M

2016-12-01

This work presents the simultaneous determination of catechol (CC) and hydroquinone (HQ), employing a modified carbon paste electrode (CPE) with ferrite nanomaterial. Ferrite nanomaterial was doped with different amount of cobalt and this was investigated toward simultaneous oxidation of CC and HQ. It was shown that this modification strongly increases electrochemical characteristics of the CPE. Also, electrocatalytic activity of such materials strongly depends on the level of substituted Co in the ferrite nanoparticles. The modified electrodes, labeled as CoFerrite/CPE, showed two pairs of well-defined redox peaks for the electrochemical processes of catechol and hydroquinone. Involving of ferrite material in the structure of CPE, cause increase in the potentials differences between redox couples of the investigated compounds, accompanied with increases in peaks currents. Several important parameters were optimized and calibration curves, with limits of detection (LOD) of 0.15 and 0.3µM for catechol and hydroquinone, respectively, were constructed by employing amperometric detection. Effect of possible interfering compounds was also studied, and proposed method was successfully applied for CC and HQ quantification in real samples. Copyright © 2016 Elsevier B.V. All rights reserved.

Effect of cobalt substitution on magnetic properties of Ba4Ni2-xCoxFe36O60 hexaferrite

NASA Astrophysics Data System (ADS)

Jiang, Xiaona; Li, Songze; Yu, Zhong; Harris, Vincent G.; Su, Zhijuan; Sun, Ke; Wu, Chuanjian; Guo, Rongdi; Lan, Zhongwen

2018-05-01

Co-substituted U-type hexagonal ferrite bulks, with composition of Ba4Ni2-xCoxFe36O60 (x=0.2, 0.4, 0.6, 0.8), were prepared by a conventional ceramic method. Saturation magnetization (4πMs), coercivity (Hc), and Curie temperature (Tc) were investigated. Anisotropy constant (K1) was calculated by fitting the magnetization curve (M-H) according to the law of approach to saturation, and anisotropy field (Ha) was calculated accordingly. The results reveal that all the samples possess the U-type hexagonal crystallographic structure. With increasing cobalt substitution content (x), the lattice parameters (a and c) almost remain the same owing to the similar radii of Ni2+ (0.72 Å) Co2+ (0.74 Å) ions. 4πMs goes up, while Hc Hc shows an opposite trend. K1 and Ha monotonously decrease resulting from that cobalt substitution weakens the c-axis orientation. Additionally, Tc increases from 467 °C to 484 °C.

Study of structural phase transformation and hysteresis behavior of inverse-spinel α-ferrite nanoparticles synthesized by co-precipitation method

NASA Astrophysics Data System (ADS)

Dabagh, Shadab; Chaudhary, Kashif; Haider, Zuhaib; Ali, Jalil

2018-03-01

Substitution of cobalt (Co2+) ions in cobalt ferrite (CoFe2O4) with copper (Cu2+) and aluminum (Al3+) ions allows variations in their electric and magnetic properties which can be optimized for specific applications. In this article, synthesis of inverse-spinel Co1-xCuxFe2-xAlxO4 (0.0 ≤ x ≤ 0.8) nanoparticles by substituting Cu2+ and Al3+ ions in CoFe2O4 via co-precipitation method is reported. By controlling copper and aluminum (Cu-Al) substituent ratio, the magnetic moment and coercivity of synthesized cobalt ferrite nanoparticles is optimized. The role of substituents on the structure, particle size, morphology, and magnetic properties of nano-crystalline ferrite is investigated. The Co1-xCuxFe2-xAlxO4 (0.0 ≤ x≤ 0.8) nanoparticles with crystallite size in the range of 23.1-26.5 nm are observed, 26.5 nm for x = 0.0-23.1 nm for x = 0.8. The inverse-spinel structure of synthesized Co1-xCuxFe2-xAlxO4 (0.0 ≤ x ≤ 0.8) nano-particles is confirmed by characteristic vibrational bands at tetrahedral and octahedral sites using Fourier transform infrared spectroscopy. A decreases in coercive field and magnetic moment is observed as Cu-Al contents are increased (x = 0.0-0.8). The positive anisotropy of synthesized particles Co1-xCuxFe2-xAlxO4 (0.0 ≤ x ≤ 0.8) is obtained in the range 1.96 × 105 J/m3 for x = 0.0 to 0.29 × 105 J/m3 for x = 0.8.

Controlled cobalt doping in biogenic magnetite nanoparticles

PubMed Central

Byrne, J. M.; Coker, V. S.; Moise, S.; Wincott, P. L.; Vaughan, D. J.; Tuna, F.; Arenholz, E.; van der Laan, G.; Pattrick, R. A. D.; Lloyd, J. R.; Telling, N. D.

2013-01-01

Cobalt-doped magnetite (CoxFe3 −xO4) nanoparticles have been produced through the microbial reduction of cobalt–iron oxyhydroxide by the bacterium Geobacter sulfurreducens. The materials produced, as measured by superconducting quantum interference device magnetometry, X-ray magnetic circular dichroism, Mössbauer spectroscopy, etc., show dramatic increases in coercivity with increasing cobalt content without a major decrease in overall saturation magnetization. Structural and magnetization analyses reveal a reduction in particle size to less than 4 nm at the highest Co content, combined with an increase in the effective anisotropy of the magnetic nanoparticles. The potential use of these biogenic nanoparticles in aqueous suspensions for magnetic hyperthermia applications is demonstrated. Further analysis of the distribution of cations within the ferrite spinel indicates that the cobalt is predominantly incorporated in octahedral coordination, achieved by the substitution of Fe2+ site with Co2+, with up to 17 per cent Co substituted into tetrahedral sites. PMID:23594814

Investigation on the structures and magnetic properties of carbon or nitrogen doped cobalt ferrite nanoparticles.

PubMed

Cao, Derang; Pan, Lining; Li, Jianan; Cheng, Xiaohong; Zhao, Zhong; Xu, Jie; Li, Qiang; Wang, Xia; Li, Shandong; Wang, Jianbo; Liu, Qingfang

2018-05-21

Carbon or nitrogen doped cobalt ferrite nanoparticles were synthesized in the air by a facile calcination process. X-ray diffraction, mapping, X-ray photoelectron spectroscopy, and mössbauer spectra results indicate that the nonmetal elements as the interstitial one are doped into cobalt ferrite nanoparticles. The morphologies of doped cobalt ferrite nanoparticles change from near-spherical to irregular cubelike shapes gradually with the increased carbon or nitrogen concentration, and their particles sizes also increase more than 200 nm. Furthermore, the saturation magnetization of carbon doped cobalt ferrite is improved. Although the saturation magnetization of N-doped cobalt ferrite is not enhanced obviously due to the involved hematite, they also do not drop drastically. The results reveal an approach to synthesize large scale ferrite nanoparticles, and improve the magnetic properties of ferrite nanoparticles, and also provide the potential candidates to synthesis co-doped functional magnetic materials.

Synthesis and Characterization of Zirconium Substituted Cobalt Ferrite Nanopowders

DOE PAGES

Rus, S. F.; Vlazan, P.; Herklotz, A.

2016-01-01

Nanocrystalline ferrites; CoFe 2O 4 (CFO) and CoFe 1.9Zr 0.1O 4 (CFZO) have been synthesized through chemical coprecipitation method. Moreover, the role played by the zirconium ions in improving the magnetic and structural properties is analyzed. X-ray diffraction revealed a single-phase cubic spinel structure for both materials, where the crystallite size increases and the lattice parameter decreases with substitution of Zr. The average sizes of the nanoparticles are estimated to be 16-19 nm. These sizes are small enough to achieve the suitable signal to noise ratio in the high density recording media. An increase in the saturation magnetization with themore » substitution of Zr suggests the preferential occupation of Zr 4+ ions in the tetrahedral sites. A decrease in the coercivity values indicates the reduction of magneto-crystalline anisotropy. We investigated spinel ferrites can be used also in recoding media due to the large value of coercivity 1000 Oe which is comparable to those of hard magnetic materials.« less

Temperature dependent viscosity of cobalt ferrite / ethylene glycol ferrofluids

NASA Astrophysics Data System (ADS)

Kharat, Prashant B.; Somvanshi, Sandeep B.; Kounsalye, Jitendra S.; Deshmukh, Suraj S.; Khirade, Pankaj P.; Jadhav, K. M.

2018-04-01

In the present work, cobalt ferrite / ethylene glycol ferrofluid is prepared in 0 to 1 (in the step of 0.2) volume fraction of cobalt ferrite nanoparticles synthesized by co-precipitation method. The XRD results confirmed the formation of single phase spinel structure. The Raman spectra have been deconvoluted into individual Lorentzian peaks. Cobalt ferrite has cubic spinel structure with Fd3m space group. FT-IR spectra consist of two major absorption bands, first at about 586 cm-1 (υ1) and second at about 392 cm-1 (υ2). These absorption bands confirm the formation of spinel-structured cobalt ferrite. Brookfield DV-III viscometer and programmable temperature-controlled bath was used to study the relationship between viscosity and temperature. Viscosity behavior with respect to temperature has been studied and it is revealed that the viscosity of cobalt ferrite / ethylene glycol ferrofluids increases with an increase in volume fraction of cobalt ferrite. The viscosity of the present ferrofluid was found to decrease with increase in temperature.

Effect of annealing on particle size, microstructure and gas sensing properties of Mn substituted CoFe2O4 nanoparticles

NASA Astrophysics Data System (ADS)

Kumar, E. Ranjith; Kamzin, A. S.; Janani, K.

2016-11-01

Microstructure, morphological and gas sensor studies of Mn substituted cobalt ferrite nanoparticles synthesized by a simple evaporation method and auto- combustion method. The influence of heat treatment on phase and particle size of spinel ferrite nanoparticles were determined by X-ray diffraction and Mossbauer spectroscopy. The XRD study reveals that the lattice constant and crystallite size of the samples increases with the increase of annealing temperature. Last one was confirmed by Mossbauer data. The lowest size of particles of MnCoFe2O4 (~3 nm) is obtained by auto combustion method. The spherical shaped nanoparticles are recorded by TEM. Furthermore, conductance response of Mn-Co ferrite nanomaterial was measured by exposing the material to reducing gas like liquefied petroleum gas (LPG) which showed a sensor response of ~0.19 at an optimum operating temperature of 250 °C.

Synthesis, structural and magnetic behavior studies of Zn-Al substituted cobalt ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Zare, Samad; Ati, Ali A.; Dabagh, Shadab; Rosnan, R. M.; Othaman, Zulkafli

2015-06-01

A series of nano-sized Zn-Al substituted cobalt ferrite Co(1-x)Zn(x)Fe2-xAlxO4 with 0.0 ⩽ x ⩽ 1.0 have been synthesized by chemical co-precipitation technique. The XRD spectra revealed the single phase spinel structure of Co(1-x)Zn(x)Fe2-xAlxO4 with average size of nanoparticles are estimated to be 17-30 nm. These are small enough to achieve the suitable signal to noise ratio, which is important in the high-density recording media. The FTIR spectra show the characteristic of two strong absorption bands at 560-600 cm-1 corresponds to the intrinsic stretching vibrations of the metal at the tetrahedral site and lowest band is observed at 370-410 cm-1 corresponds to octahedral site. The crystalline structures of nanoparticles composite were characterized by Field Emission Scanning Electron Microscopy (FE-SEM). The magnetic properties such as saturation magnetization, remanence magnetization, and coercivity were calculated from the hysteresis loops. Saturation magnetization were found to increase up to x = 0.4 while remanence magnetization and coercivity continuously decrease with increasing Zn-Al concentration. The stability in coercivity while increase in saturation magnetization confirms that the Co0.6Zn0.4Fe1.6Al0.4O4 ferrite sample is suitable for applications in high-density recording media.

Synthesis and properties of precipitated cobalt ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Ristic, Mira; Krehula, Stjepko; Reissner, Michael; Jean, Malick; Hannoyer, Beatrice; Musić, Svetozar

2017-07-01

The formation and properties of cobalt ferrite were investigated with XRD, FT-IR, FE-SEM, Mössbauer and magnetometry. Cobalt ferrite samples were prepared (a) by combining coprecipitation Co(OH)2/2Fe(OH)3, using NaOH between pH 5.2 and 11.4 and autoclaving, and (b) by autoclaving the Co(OH)2/2Fe(OH)3 coprecipitate in a very strong alkaline medium. XRD and FE SEM showed that both CoFe2O4 crystallites and particles were in the nanosize range. The FT-IR spectra were typical of spinel ferrites. Cobalt ferrite precipitated at pH 7.2 and at 11.4 contained a small fraction of α-Fe2O3, whereas in the sample precipitated at pH 11.4 a very small amount (traces) of α-FeOOH were detected by FT-IR, additionally. Parameters obtained by Mössbauer spectroscopy suggested a structural migration of cobalt and iron ions in prepared cobalt ferrite spinels with the prolonged time of autoclaving. Magnetic measurements showed the magnetic behaviour typical of spinel ferrite nanoparticles.

Impedance spectroscopy studies in cobalt ferrite-reduced graphene oxide nanocomposite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Supriya, Sweety, E-mail: sweety@iitp.ac.in; Kumar, Sunil, E-mail: sunil.pph13@iitp.ac.in; Kar, Manoranjan, E-mail: mano@iitp.ac.in

2016-05-06

(1-x)Cobalt ferrite-(x)reduced graphene oxidenanocomposites with x=0, 0.1, 0.2 and 0.3 were prepared by the ultrasonic method. The crystal symmetry modification due to reduced graphene oxide and cobalt ferrite interaction has been studied by employing the X-ray diffraction technique. Morphology of the samples was studied by the Field emission scanning electron microscopy (FE-SEM). Study on electrical properties of the cobalt ferrite-reduced graphene oxide nanocomposites explores the possible application of these composites as anode material. Impedance decreases with an increase in frequency as well as temperature, which supports an increase in ac electrical conductivity. The modified Debye relaxation model can explain themore » behavior of impedance in cobalt ferrite-reduced graphene oxide nanocomposites.« less

Effect of Er doping on the structural and magnetic properties of cobalt-ferrite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Prathapani, Sateesh; Vinitha, M.; Das, D., E-mail: ddse@uohyd.ernet.in

2014-05-07

Nanocrystalline particulates of Er doped cobalt-ferrites CoFe{sub (2−x)}Er{sub x}O{sub 4} (0 ≤ x ≤ 0.04), were synthesized, using sol-gel assisted autocombustion method. Co-, Fe-, and Er- nitrates were the oxidizers, and malic acid served as a fuel and chelating agent. Calcination (400–600 °C for 4 h) of the precursor powders was followed by sintering (1000 °C for 4 h) and structural and magnetic characterization. X-ray diffraction confirmed the formation of single phase of spinel for the compositions x = 0, 0.01, and 0.02; and for higher compositions an additional orthoferrite phase formed along with the spinel phase. Lattice parameter of the doped cobalt-ferrites was higher than that of pure cobalt-ferrite.more » The observed red shift in the doped cobalt-ferrites indicates the presence of induced strain in the cobalt-ferrite matrix due to large size of the Er{sup +3} compared to Fe{sup +3}. Greater than two-fold increase in coercivity (∼66 kA/m for x = 0.02) was observed in doped cobalt-ferrites compared to CoFe{sub 2}O{sub 4} (∼29 kA/m)« less

Effect of doping rare earths on magnetostriction characteristics of CoFe2O4 prepared from spent Li-ion batteries

NASA Astrophysics Data System (ADS)

Xi, Guoxi; Zhao, Tingting; Wang, Lu; Dun, Changwei; Zhang, Ye

2018-04-01

Recovering spent Li-ion batteries is beneficial to the economy and environment. Therefore, this study synthesized nanoparticles of cobalt ferrite doped with different rare earth ions (Nd, Ce, and Pr) by a sol-gel auto-combustion method using spent Li-ion batteries. The effect of the different doping elements on grain sizes, structure, magnetic and magnetostrictive properties, and strain derivative were confirmed by X-ray diffraction, scanning election microscopy, vibrating sample magnetometer, and a magnetostrictive coefficient measuring system. Substitution of a small amount of Fe3+ with RE3+ in CoRExFe2-xO4 (x = 0.025, 0.05, and 0.1) had a large effect on magnetostrictive properties and strain derivative, which was improved compared with pure cobalt ferrite at low magnetic field. The maximum strain derivative (dλ/dH = -1.49 × 10-9 A-1 m at 18 kA m-1) was obtained for Nd, x = 0.05. Changes in the magnetostriction coefficients and strain derivatives were correlated with changes in cation distribution, microstructure, and magnetic anisotropy, which depended strongly on RE3+ substitution and distribution in the spinel structure.

Micro structural analysis and magnetic characteristics of rare earth substituted cobalt ferrite

NASA Astrophysics Data System (ADS)

Tapdiya, Swati; Singh, Sarika; Kulshrestha, Shobha; Shrivastava, A. K.

2018-05-01

A series of ultrafine nanoparticles of Gd3+ doped Co-ferrites CoGdxFe2-xO4 (x=0.0, 0.05 and 0.10) were prepared by wet chemical co-precipitation method using nitrates of respective metal ions. Structural and morphology studies were performed using XRD, SEM and EDAX. Indexed XRD patterns confirm the formation of cubic spinel phase. Average crystallite sizes found to be decreases with trivalent rare earth ion substitution. Lattice constant (a) and lattice strain increases with increase in Gd3+ concentration due to large ionic radii (0.94nm) of Gd3+ replacing Fe3+ (0.64nm). SEM images show the spherical morphology and uniform growth of nanoparticles. Magnetic studies show that magnetization (Ms), decreases with increase in Gd3+ concentration from 50.16 emu/gm to 31.26 emu/gm.

Magneto-Optic Devices Based on Organic Polymer Materials

DTIC Science & Technology

2012-09-10

cobalt  ferrite  particles...to   cobalt  ferrite  particles.     The   rings   in   the  SAED  pattern  also   indicate  averaging  of   the... cobalt  ferrite  nanoparticles  (A),  a  high   resolution  image  of  a  single  nanoparticle  showing  the

Structural and magnetic characteristics of PVA/CoFe{sub 2}O{sub 4} nano-composites prepared via mechanical alloying method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rashidi, S.; Ataie, A., E-mail: aataie@ut.ac.ir

Highlights: • Single phase CoFe{sub 2}O{sub 4} nano-particles synthesized in one step by mechanical alloying. • PVA/CoFe{sub 2}O{sub 4} magnetic nano-composites were fabricated via mechanical milling. • FTIR confirmed the interaction between PVA and magnetic CoFe{sub 2}O{sub 4} particles. • Increasing in milling time and PVA amount led to well dispersion of CoFe{sub 2}O{sub 4}. - Abstract: In this research, polyvinyl alcohol/cobalt ferrite nano-composites were successfully synthesized employing a two-step procedure: the spherical single-phase cobalt ferrite of 20 ± 4 nm mean particle size was synthesized via mechanical alloying method and then embedded into polymer matrix by intensive milling. Themore » results revealed that increase in polyvinyl alcohol content and milling time causes cobalt ferrite particles disperse more homogeneously in polymer matrix, while the mean particle size and shape of cobalt ferrite have not been significantly affected. Transmission electron microscope images indicated that polyvinyl alcohol chains have surrounded the cobalt ferrite nano-particles; also, the interaction between polymer and cobalt ferrite particles in nano-composite samples was confirmed. Magnetic properties evaluation showed that saturation magnetization, coercivity and anisotropy constant values decreased in nano-composite samples compared to pure cobalt ferrite. However, the coercivity values of related nano-composite samples enhanced by increasing PVA amount due to domain wall mechanism.« less

Study of x CNFO + (1-x) PLZT magnetoelectric composites

NASA Astrophysics Data System (ADS)

Dipti, Singh, Sangeeta; Juneja, J. K.; Pant, R. P.; Raina, K. K.; Prakash, Chandra

2014-04-01

In the present paper, we are reporting the studies on structural, dielectric, ferroelectric and magnetic properties of Lanthanum (La) substituted Lead Zirconate Titanate (PZT) and Cobalt Nickel ferrite (CNFO) composites with compositional formula x(Co0.80Ni0.20Fe2O4)+(1-x)(Pb1.01625La0.0025Zr0.55Ti0.45O3) (x = 0.00,0.10). The materials were synthesized by solid state reaction route. XRD analysis confirms the presence of both ferrite and ferroelectric phases. Dielectric properties were studied as a function of frequency and temperature. Ferroelectric P-E and Magnetic M-H hysteresis loops were measured at room temperature.

Microwave combustion synthesis of Co1-xZnxFe2O4 (0⩽x⩽0.5): Structural, magnetic, optical and vibrational spectroscopic studies.

PubMed

Sundararajan, M; Kennedy, L John; Vijaya, J Judith; Aruldoss, Udaya

2015-04-05

Nanostructured pure and zinc doped cobalt ferrites (Co1-xZnxFe2O4 where x fraction ranging from 0 to 0.5) were prepared by microwave combustion method employing urea as a fuel. The nanostructured samples were characterized by using various instrumental techniques such as X-ray powder diffractometry, high resolution scanning electron microscopy, energy dispersive X-ray analysis, UV-visible diffuse reflectance spectroscopy, photoluminescence spectroscopy and Fourier transformed infrared (FT-IR) spectroscopy. Vibrating sample magnetometry at room temperature was recorded to study the magnetic behavior of the samples. X-ray analysis and the FT-IR spectroscopy revealed the formation of cobalt ferrite cubic spinel-type structure. The average crystallite sizes for the samples were in the range of 3.07-11.30 nm. The direct band gap (Eg) was estimated using Kubelka-Munk method and is obtained from the UV-vis spectra. The band gap value decreased with an increase in zinc fraction (2.56-2.17 eV). The violet and green emission observed in the photoluminescence spectra revealed that cobalt ferrites are governed by defect controlled processes. The elemental analysis of zinc doped cobalt ferrites were obtained from energy dispersive X-ray (EDX) analysis. From the magnetic measurements, it is observed that cobalt ferrite and zinc doped cobalt ferrite systems fall under the soft ferrite category. The saturation magnetization (Ms) value of undoped cobalt ferrite is 14.26 emu/g, and it has reached a maximum of 29.61 emu/g for Co0.7Zn0.3Fe2O4. Copyright © 2014 Elsevier B.V. All rights reserved.

Microstructural and optical properties of Ca and Cr doped cobalt ferrite nanoparticles synthesized by auto combustion

NASA Astrophysics Data System (ADS)

Agrawal, Shraddha; Parveen, Azra; Azam, Ameer

2018-05-01

The Ca and Cr doped cobalt ferrite nanoparticles (Co0.8Ca0.2) (Fe0.8 Cr0.2)2O4 were synthesized by auto combustion method. Microstructural studies were carried out by X-ray diffraction (XRD). The crystalline size of synthesized nanoparticles as determined by the XRD was found to be 17.6 nm. These structural studies suggest that the crystal system remains spinal even with the doping of calcium and chromium. Optical properties of Ca and Cr doped cobalt ferrite were studied by UV-visible technique in the range of 200-800 nm. The energy band gap was calculated with the help of Tauc relationship. Ca and Cr doped cobalt ferrite annealed at 600°C exhibit significant dispersion in complex permeability. The dielectric constant and dielectric loss of cobalt ferrite were studied as a function of frequency and were explained on the basis of Koop's theory based on Maxwell Wagner two layer models and electron hopping.

The effect of Y3+ substitution on the structural, optical band-gap, and magnetic properties of cobalt ferrite nanoparticles.

PubMed

Alves, T E P; Pessoni, H V S; Franco, A

2017-06-28

In this study we investigated the structural, optical band-gap, and magnetic properties of CoY x Fe 2-x O 4 (0 ≤ x ≤ 0.04) nanoparticles (NPs) synthesized using a combustion reaction method without the need for subsequent heat treatment or the calcing process. The particle size measured from X-ray diffraction (XRD) patterns and transmission electron microscope (TEM) images confirms the nanostructural character in the range of 16-36 nm. The optical band-gap (E g ) values increase with the Y 3+ ion (x) concentration being 3.30 and 3.58 eV for x = 0 and x = 0.04, respectively. The presence of yttrium in the cobalt ferrite (Y-doped cobalt ferrite) structure affects the magnetic properties. For instance, the saturation magnetization, M s and remanent magnetization, M r , decrease from 69 emu g -1 to 33 and 28 to 12 emu g -1 for x = 0 and x = 0.04, respectively. On the other hand the coercivity, H c , increases from 1100 to 1900 Oe for x = 0 and x = 0.04 at room temperature. Also we found that M s , M r , and H c decreased with increasing temperature up to 773 K. The cubic magnetocrystalline constant, K 1 , determined by using the "law of approach" (LA) to saturation decreases with Y 3+ ion concentration and temperature. K 1 values for x = 0 (x = 0.04) were 3.3 × 10 6 erg cm -3 (2.0 × 10 6 erg cm -3 ) and 0.4 × 10 6 erg cm -3 (0.3 × 10 6 erg cm -3 ) at 300 K and 773 K, respectively. The results were discussed in terms of inter-particle interactions induced by thermal fluctuations, and Co 2+ ion distribution over tetrahedral A-sites and octahedral B-sites of the spinel structure due to Y 3+ ion substitution.

Electronic Materials Based on Co0.5Zn0.5Fe2O4/Pb(Zr0.52Ti0.48)O3 Nanocomposites

NASA Astrophysics Data System (ADS)

Mandal, Avinandan; Das, Chapal Kumar

2013-01-01

The reduction of the radar cross-sectional area achieved in stealth technology has been a major challenge since the Second World War, being accomplished by covering the metallic surfaces of aircraft, ships, tanks, etc. with radar-absorbing materials. Nowadays, the development of lightweight microwave-absorbing materials with reduced thickness has a greater impact due to their excellent microwave-absorbing properties. In this study, the microwave-absorbing properties of nanocomposites based on Zn-substituted cobalt ferrite and lead zirconium titanate have been investigated in the X-band (8.2 GHz to 12.4 GHz) region. Zn-substituted cobalt ferrite (CZF) and lead zirconium titanate (PZT) nanoparticles were prepared by the coprecipitation and homogeneous precipitation method, respectively. Nanocomposites were developed by dispersing these nanoparticles with different compositions into an epoxy resin matrix. All the composite materials showed more than 90% microwave absorption in the X-band region. The nanocomposite containing CZF/PZT (3:1) with 2 mm thickness displayed maximum return loss of -47.87 dB at 12.23 GHz. The microwave absorbers based on epoxy resin polymeric matrix exhibited better absorbing properties when the dielectric contribution matched the magnetic contribution, and the loss mechanisms were mainly due to the dielectric loss.

Structural, morphological and magnetic properties of Eu-doped CoFe2O4 nano-ferrites

NASA Astrophysics Data System (ADS)

Zubair, Aiman; Ahmad, Zahoor; Mahmood, Azhar; Cheong, Weng-Chon; Ali, Irshad; Khan, Muhammad Azhar; Chughtai, Adeel Hussain; Ashiq, Muhammad Naeem

Europium (Eu) doped spinel cobalt ferrites having composition CoEuxFe2-xO4 where x = 0.00, 0.03, 0.06, 0.09, 0.12 were fabricated by co-precipitation route. In order to observe the phase development of the ferrite samples, thermo-gravimetric analysis was carried out. The synthesized samples were subjected to X-ray diffraction analysis for structural investigation. All the samples were found to constitute face centered cubic (FCC) spinel structure belonging to Fd3m space group. Scanning electron microscopy revealed the formation of nanocrystalline grains with spherical shape. Energy dispersive X-ray spectra confirmed the presence of Co, Eu, Fe and O elements with no existence of any impurity. The magnetic hysteresis curves measured at room temperature exhibited ferrimagnetic behavior with maximum saturation magnetization (Ms) of 65 emu/g and coercivity (Hc) of 966 Oe. The origin of ferrimagnetism in Eu doped cobalt ferrites was discussed in detail with reverence to the allocation of Co2+ and Fe3+ ions within the spinel lattice. The overall coercivity was increased (944-966 Oe) and magnetization was decreased (65-46 emu/g) with the substitution of Eu3+. The enhancement of former is ascribed to the transition from multi domain to single domain state and reduction in lateral is attributed to the incorporation of nonmagnetic Eu ions for Fe, resulting in weak superexchange interactions.

Variation in band gap energy and electrical analysis of double doped cobalt ferrite

NASA Astrophysics Data System (ADS)

Parveen, Azra; Agrawal, Shraddha; Azam, Ameer

2018-05-01

The Ca and Cr doped cobalt ferrite nanoparticles (Co0.9Ca0.1) (Fe0.8 Cr0.2)2O4 were synthesized by microwave gel combustion method. Microstructural studies were carried out by XRD and SEM. Structural studies suggest that the crystal system remains spinal even with the doping of calcium and chromium. The SEM image shows the spherical morphology of surface of the sample. Optical properties of Ca and Cr doped cobalt ferrite were studied by UV-visible technique in the range of 400-600 nm. The electrical conductivity of pure and doped cobalt ferrite were studied as a function of frequency and were explained on the basis of electron hopping.

Magnetic properties of cobalt ferrite synthesized by mechanical alloying

NASA Astrophysics Data System (ADS)

Dedi, Idayanti, Novrita; Kristiantoro, Tony; Alam, Ginanjar Fajar Nur; Sudrajat, Nanang

2018-05-01

Cobalt ferrite (CoFe2O4) is a well-known hard magnetic material with high coercivity and moderate magnetization. These properties, along with their great physical and chemical stability, make CoFe2O4 suitable for many applications such as generator, audio, video-tape etc. In this study, the magnetic properties of cobalt ferrite synthesized via the mechanical alloying using α-Fe2O3 of Hot Strip Mill (HSM) waste and cobalt carbonate as the precursors have been investigated. Structural and magnetic properties were systematically investigated. The X-ray diffraction (XRD) pattern exhibited the single phase of cobalt ferrite when the sintering temperature was 1000 °C. Permagraph measurements of the sintered sample revealed a saturation magnetization (Ms) of 77-83 emu/g and coercivity (Hc) of 575 Oe which closely to the magnetic properties of references; Ms = 47.2-56.7 emu/g and Hc =233-2002 Oe.

Ultrasound assisted extraction of Maxilon Red GRL dye from water samples using cobalt ferrite nanoparticles loaded on activated carbon as sorbent: Optimization and modeling.

PubMed

Mehrabi, Fatemeh; Vafaei, Azam; Ghaedi, Mehrorang; Ghaedi, Abdol Mohammad; Alipanahpour Dil, Ebrahim; Asfaram, Arash

2017-09-01

In this research, a selective, simple and rapid ultrasound assisted dispersive solid-phase micro-microextraction (UA-DSPME) was developed using cobalt ferrite nanoparticles loaded on activated carbon (CoFe 2 O 4 -NPs-AC) as an efficient sorbent for the preconcentration and determination of Maxilon Red GRL (MR-GRL) dye. The properties of sorbent are characterized by X-ray diffraction (XRD), Transmission Electron Microscopy (TEM), Vibrating sample magnetometers (VSM), Fourier transform infrared spectroscopy (FTIR), Particle size distribution (PSD) and Scanning Electron Microscope (SEM) techniques. The factors affecting on the determination of MR-GRL dye were investigated and optimized by central composite design (CCD) and artificial neural networks based on genetic algorithm (ANN-GA). CCD and ANN-GA were used for optimization. Using ANN-GA, optimum conditions were set at 6.70, 1.2mg, 5.5min and 174μL for pH, sorbent amount, sonication time and volume of eluent, respectively. Under the optimized conditions obtained from ANN-GA, the method exhibited a linear dynamic range of 30-3000ngmL -1 with a detection limit of 5.70ngmL -1 . The preconcentration factor and enrichment factor were 57.47 and 93.54, respectively with relative standard deviations (RSDs) less than 4.0% (N=6). The interference effect of some ions and dyes was also investigated and the results show a good selectivity for this method. Finally, the method was successfully applied to the preconcentration and determination of Maxilon Red GRL in water and wastewater samples. Copyright © 2016 Elsevier B.V. All rights reserved.

Carbonate fuel cell anodes

DOEpatents

Donado, R.A.; Hrdina, K.E.; Remick, R.J.

1993-04-27

A molten alkali metal carbonates fuel cell porous anode of lithium ferrite and a metal or metal alloy of nickel, cobalt, nickel/iron, cobalt/iron, nickel/iron/aluminum, cobalt/iron/aluminum and mixtures thereof wherein the total iron content including ferrite and iron of the composite is about 25 to about 80 percent, based upon the total anode, provided aluminum when present is less than about 5 weight percent of the anode. A process is described for production of the lithium ferrite containing anode by slipcasting.

Carbonate fuel cell anodes

DOEpatents

Donado, Rafael A.; Hrdina, Kenneth E.; Remick, Robert J.

1993-01-01

A molten alkali metal carbonates fuel cell porous anode of lithium ferrite and a metal or metal alloy of nickel, cobalt, nickel/iron, cobalt/iron, nickel/iron/aluminum, cobalt/iron/aluminum and mixtures thereof wherein the total iron content including ferrite and iron of the composite is about 25 to about 80 percent, based upon the total anode, provided aluminum when present is less than about 5 weight percent of the anode. A process for production of the lithium ferrite containing anode by slipcasting.

An experimental study of the local electronic structure of B-site gallium doped bismuth ferrite powders

NASA Astrophysics Data System (ADS)

Gholam, Turghunjan; Ablat, Abduleziz; Mamat, Mamatrishat; Wu, Rong; Aimidula, Aimierding; Bake, Muhammad Ali; Zheng, Lirong; Wang, Jiaou; Qian, Haijie; Wu, Rui; Ibrahim, Kurash

2017-08-01

The un-doped and gallium (Ga) doped multiferroic bismuth ferrite (BiFeO3) compounds were successfully synthesized by the hydrothermal technique. This is then followed by a series of detailed investigations into the influence of Ga doping on the structural, morphological, optical and magnetic properties of BiFe1 - xGaxO3 (0 ≤ x ≤ 0.15). X-ray diffraction (XRD) analyses reveal that B-site doping of Ga may lead to the transformation of its crystal structure from a rhombohedral with a space group of R3c to an orthorhombic with a space group of Pbnm phase. The scanning electron microscope (SEM) images show that doping with Ga causes a significant reduction in particle size, when compared to un-doped BiFeO3. X-ray absorption near-edge structure (XANES) spectra have also shown that as the substitution of Ga increases, the Fe K and Bi LIII-edge absorption spectra shift towards higher energy site. It also implies that doping of Ga affects the local structures of both Bi and Fe atoms. Distinct transmission band fluctuations, as shown by Fourier transform infrared (FT-IR) spectra, can provide significant evidence for a transformation in crystal structure, following the increase of Ga concentration. The magnetization hysteresis measurements show that the magnetization decreases when Ga content is x ≥ 0.05. Such a phenomenon mainly stems from the substitution of Fe for an excessive amount of Ga, resulting in reduction of both valence fluctuations and the magnetization in the BiFe1 - xGaxO3 system.

Physiological Remediation of Cobalt Ferrite Nanoparticles by Ferritin

NASA Astrophysics Data System (ADS)

Volatron, Jeanne; Kolosnjaj-Tabi, Jelena; Javed, Yasir; Vuong, Quoc Lam; Gossuin, Yves; Neveu, Sophie; Luciani, Nathalie; Hémadi, Miryana; Carn, Florent; Alloyeau, Damien; Gazeau, Florence

2017-01-01

Metallic nanoparticles have been increasingly suggested as prospective therapeutic nanoplatforms, yet their long-term fate and cellular processing in the body is poorly understood. Here we examined the role of an endogenous iron storage protein - namely the ferritin - in the remediation of biodegradable cobalt ferrite magnetic nanoparticles. Structural and elemental analysis of ferritins close to exogenous nanoparticles within spleens and livers of mice injected in vivo with cobalt ferrite nanoparticles, suggests the intracellular transfer of degradation-derived cobalt and iron, entrapped within endogenous protein cages. In addition, the capacity of ferritin cages to accommodate and store the degradation products of cobalt ferrite nanoparticles was investigated in vitro in the acidic environment mimicking the physiological conditions that are present within the lysosomes. The magnetic, colloidal and structural follow-up of nanoparticles and proteins in the lysosome-like medium confirmed the efficient remediation of nanoparticle-released cobalt and iron ions by ferritins in solution. Metal transfer into ferritins could represent a quintessential process in which biomolecules and homeostasis regulate the local degradation of nanoparticles and recycle their by-products.

Structural and magnetic properties of cobalt-doped iron oxide nanoparticles prepared by solution combustion method for biomedical applications.

PubMed

Venkatesan, Kaliyamoorthy; Rajan Babu, Dhanakotti; Kavya Bai, Mane Prabhu; Supriya, Ravi; Vidya, Radhakrishnan; Madeswaran, Saminathan; Anandan, Pandurangan; Arivanandhan, Mukannan; Hayakawa, Yasuhiro

2015-01-01

Cobalt-doped iron oxide nanoparticles were prepared by solution combustion technique. The structural and magnetic properties of the prepared samples were also investigated. The average crystallite size of cobalt ferrite (CoFe2O4) magnetic nanoparticle was calculated using Scherrer equation, and it was found to be 16±5 nm. The particle size was measured by transmission electron microscope. This value was found to match with the crystallite size calculated by Scherrer equation corresponding to the prominent intensity peak (311) of X-ray diffraction. The high-resolution transmission electron microscope image shows clear lattice fringes and high crystallinity of cobalt ferrite magnetic nanoparticles. The synthesized magnetic nanoparticles exhibited the saturation magnetization value of 47 emu/g and coercivity of 947 Oe. The anti-microbial activity of cobalt ferrite nanoparticles showed better results as an anti-bacterial agent. The affinity constant was determined for the nanoparticles, and the cytotoxicity studies were conducted for the cobalt ferrite nanoparticles at different concentrations and the results are discussed.

Structural and magnetic properties of cobalt-doped iron oxide nanoparticles prepared by solution combustion method for biomedical applications

PubMed Central

Venkatesan, Kaliyamoorthy; Rajan Babu, Dhanakotti; Kavya Bai, Mane Prabhu; Supriya, Ravi; Vidya, Radhakrishnan; Madeswaran, Saminathan; Anandan, Pandurangan; Arivanandhan, Mukannan; Hayakawa, Yasuhiro

2015-01-01

Cobalt-doped iron oxide nanoparticles were prepared by solution combustion technique. The structural and magnetic properties of the prepared samples were also investigated. The average crystallite size of cobalt ferrite (CoFe2O4) magnetic nanoparticle was calculated using Scherrer equation, and it was found to be 16±5 nm. The particle size was measured by transmission electron microscope. This value was found to match with the crystallite size calculated by Scherrer equation corresponding to the prominent intensity peak (311) of X-ray diffraction. The high-resolution transmission electron microscope image shows clear lattice fringes and high crystallinity of cobalt ferrite magnetic nanoparticles. The synthesized magnetic nanoparticles exhibited the saturation magnetization value of 47 emu/g and coercivity of 947 Oe. The anti-microbial activity of cobalt ferrite nanoparticles showed better results as an anti-bacterial agent. The affinity constant was determined for the nanoparticles, and the cytotoxicity studies were conducted for the cobalt ferrite nanoparticles at different concentrations and the results are discussed. PMID:26491320

Physiological Remediation of Cobalt Ferrite Nanoparticles by Ferritin

PubMed Central

Volatron, Jeanne; Kolosnjaj-Tabi, Jelena; Javed, Yasir; Vuong, Quoc Lam; Gossuin, Yves; Neveu, Sophie; Luciani, Nathalie; Hémadi, Miryana; Carn, Florent; Alloyeau, Damien; Gazeau, Florence

2017-01-01

Metallic nanoparticles have been increasingly suggested as prospective therapeutic nanoplatforms, yet their long-term fate and cellular processing in the body is poorly understood. Here we examined the role of an endogenous iron storage protein – namely the ferritin – in the remediation of biodegradable cobalt ferrite magnetic nanoparticles. Structural and elemental analysis of ferritins close to exogenous nanoparticles within spleens and livers of mice injected in vivo with cobalt ferrite nanoparticles, suggests the intracellular transfer of degradation-derived cobalt and iron, entrapped within endogenous protein cages. In addition, the capacity of ferritin cages to accommodate and store the degradation products of cobalt ferrite nanoparticles was investigated in vitro in the acidic environment mimicking the physiological conditions that are present within the lysosomes. The magnetic, colloidal and structural follow-up of nanoparticles and proteins in the lysosome-like medium confirmed the efficient remediation of nanoparticle-released cobalt and iron ions by ferritins in solution. Metal transfer into ferritins could represent a quintessential process in which biomolecules and homeostasis regulate the local degradation of nanoparticles and recycle their by-products. PMID:28067263

Design, Fabrication, Characterization and Modeling of Integrated Functional Materials

DTIC Science & Technology

2009-10-01

cobalt ferrite (CoFe2O4) nanoparticles dispersed in a low-loss commercial polymer matrix obtained from Rogers Corporation. 2 mmol of Cobalt (II...oleylamine and 20 ml benzyl ether were added to the Iron (III) acetylacetonate and Cobalt (II) acetylacetonate mixture. The mixture was stirred...microwave applications Multiferroic bilayers of Cobalt Ferrite and PZT: The objective of this project is to fabricate bilayers of ferroelectric

Facile synthesis of cobalt ferrite nanotubes using bacterial nanocellulose as template.

PubMed

Menchaca-Nal, S; Londoño-Calderón, C L; Cerrutti, P; Foresti, M L; Pampillo, L; Bilovol, V; Candal, R; Martínez-García, R

2016-02-10

A facile method for the preparation of cobalt ferrite nanotubes by use of bacterial cellulose nanoribbons as a template is described. The proposed method relays on a simple coprecipitation operation, which is a technique extensively used for the synthesis of nanoparticles (either isolated or as aggregates) but not for the synthesis of nanotubes. The precursors employed in the synthesis are chlorides, and the procedure is carried out at low temperature (90 °C). By the method proposed a homogeneous distribution of cobalt ferrite nanotubes with an average diameter of 217 nm in the bacterial nanocellulose (BC) aerogel (3%) was obtained. The obtained nanotubes are formed by 26-102 nm cobalt ferrite clusters of cobalt ferrite nanoparticles with diameters in the 9-13 nm interval. The nanoparticles that form the nanotubes showed to have a certain crystalline disorder, which could be attributed in a greater extent to the small crystallite size, and, in a lesser extent, to microstrains existing in the crystalline lattice. The BC-templated-CoFe2O4 nanotubes exhibited magnetic behavior at room temperature. The magnetic properties showed to be influenced by a fraction of nanoparticles in superparamagnetic state. Copyright © 2015 Elsevier Ltd. All rights reserved.

Microwave and millimeter wave dielectric permittivity and magnetic permeability of epsilon-gallium-iron-oxide nano-powders

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chao, Liu, E-mail: liu.chao@tufts.edu; Afsar, Mohammed N.; Ohkoshi, Shin-ichi

2015-05-07

In millimeter wave frequency range, hexagonal ferrites with high uniaxial anisotropic magnetic fields are used as absorbers. These ferrites include M-type barium ferrite (BaFe{sub 12}O{sub 19}) and strontium ferrite (SrFe{sub 12}O{sub 19}), which have natural ferromagnetic resonant frequency range from 40 GHz to 60 GHz. However, the higher frequency range lacks suitable materials that support the higher frequency ferromagnetic resonance. A series of gallium-substituted ε-iron oxides (ε-Ga{sub x}Fe{sub 2−x}O{sub 3}) are synthesized, which have ferromagnetic resonant frequencies appearing over the frequency range of 30 GHz to 150 GHz. The ε-Ga{sub x}Fe{sub 2−x}O{sub 3} is synthesized by the sol-gel method. The particlemore » sizes are observed to be smaller than 100 nm. In this paper, in-waveguide transmission and reflection method and the free space magneto-optical approach have been employed to study these newly developed ε-Ga{sub x}Fe{sub 2−x}O{sub 3} particles in millimeter waves. These techniques enable to obtain precise transmission spectra to determine the dielectric and magnetic properties of both isotropic and anisotropic ferrites in the microwave and millimeter wave frequency range from single set of direct measurements. The complex dielectric permittivity and magnetic permeability spectra of ε-Ga{sub x}Fe{sub 2−x}O{sub 3} are shown in this paper. Strong ferromagnetic resonances at different frequencies determined by the x parameter are found.« less

Structural, Magnetic and Microwave Properties of Nanocrystalline Ni-Co-Gd Ferrites

NASA Astrophysics Data System (ADS)

Nikzad, Alireza; Parvizi, Roghaieh; Rezaei, Ghasem; Vaseghi, Behrooz; Khordad, Reza

2018-02-01

A series of Co- and Gd-substituted NiFe2O4 ferrite nanoparticles with the formula Ni1- x Co x Fe2- y Gd y O4 (where x = 0.0-1.0 and y = 0.0-0.1) have been successfully synthesized using a hydrothermal method. X-ray diffraction and field emission scanning electron microscopy results indicated that a highly crystallized spherical ferrite nanoparticle structure was obtained along with an increase in the lattice parameters. Compositional analysis of the prepared nanoferrite powders has been carried out using energy-dispersive x-ray (EDX) spectra. The EDX analysis reveals the presence of Ni, Co, Gd and Fe elements in the specimens. Magnetization and the coercive field improved dramatically with an increase in the amount of cobalt and gadolinium added, attributed to the redistribution of cations in the spinel nanoferrite structure. Saturation magnetization and coercivity values up to 99 emu/g and 918 Oe, respectively, were measured using a vibration sample magnetometer at room temperature. Comparative microwave absorption experiments demonstrated that the reflection loss (RL) properties enhanced with increasing substitution of cations in the Ni-ferrite spinel structure for an absorber thickness of 1.8 mm. A maximum RL of - 26.7 dB was obtained for substituted Ni-Co-Gd nanoferrite with x = 1.0 and y = 0.1 at a frequency of 9.4 GHz with a bandwidth of 3.6 GHz (RL ≤ - 10 dB). Experimental results revealed that the synthesized nanoparticles possessed great potential in microwave absorption applications.

Investigation of Cr substitution in Co ferrite (CoCrxFe2-xO4) using Mossbauer spectroscopy

NASA Astrophysics Data System (ADS)

Krieble, K.; Lo, C. C. H.; Melikhov, Y.; Snyder, J. E.

2006-04-01

Substitution of other metals for Fe in cobalt ferrite has been proposed as a method to tailor the magnetic and magnetoelastic properties for sensor and actuator applications [H. Zheng et al., Science 303, 661 (2004)]. However, to understand the effect of Cr substitution, one needs atomic-level information on the local environments and interactions of the transition-metal ions. In this study, Mossbauer spectroscopy was used to investigate the local environments of the Fe atoms in these materials. A series of five powder samples with compositions CoCrxFe2-xO4 (x=0.0 to 0.8) was investigated using transmission geometry. Results show two distinct six-line hyperfine patterns, indicating Fe in A and B spinel sites. Increasing Cr concentration is seen to decrease the hyperfine field strength for both A and B sites, as well as increasing the width of those distributions. Results for Cr substitution show generally similar behavior to a prior study using Mn; however, Cr substitution has more pronounced effects: the hyperfine fields decrease and distribution widths increase at greater rates for Cr substitution, and the differences between A and B site behavior are more pronounced. Results are consistent with a model in which Cr has an even stronger B-site preference than Mn, and displaces more of the Co from the B to the A sites.

Isolation of genomic DNA using magnetic cobalt ferrite and silica particles.

PubMed

Prodelalová, Jana; Rittich, Bohuslav; Spanová, Alena; Petrová, Katerina; Benes, Milan J

2004-11-12

Adsorption separation techniques as an alternative to laborious traditional methods (e.g., based on phenol extraction procedure) have been applied for DNA purification. In this work we used two types of particles: silica and cobalt ferrite (unmodified or modified with a reagent containing weakly basic aminoethyl groups, aminophenyl groups, or alginic acid). DNA from chicken erythrocytes and DNA isolated from bacteria Lactococcus lactis were used for testing of adsorption/desorption properties of particles. The cobalt ferrite particles modified with different reagents were used for isolation of PCR-ready bacterial DNA from different dairy products.

Synthesis and characterization of graphene quantum dots/cobalt ferrite nanocomposite

NASA Astrophysics Data System (ADS)

Ramachandran, Shilpa; Sathishkumar, M.; Kothurkar, Nikhil K.; Senthilkumar, R.

2018-02-01

A facile method has been developed for the synthesis of a graphene quantum dots/cobalt ferrite nanocomposite. Graphene quantum dots (GQDs) were synthesized by a simple bottom-up method using citric acid, followed by the co-precipitation of cobalt ferrite nanoparticles on the graphene quantum dots. The morphology, structural analysis, optical properties, magnetic properties were investigated using transmission electron microscopy (TEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), UV-vis absorption spectroscopy, fluorescence spectroscopy, vibrating sample magnetometry (VSM) measurements. The synthesized nanocomposite showed good fluorescence and superparamagnetic properties, which are important for biomedical applications.

Controlling the size and magnetic properties of nano CoFe2O4 by microwave assisted co-precipitation method

NASA Astrophysics Data System (ADS)

Prabhakaran, T.; Mangalaraja, R. V.; Denardin, Juliano C.

2018-02-01

In this report, cobalt ferrite nanoparticles synthesized using microwave assisted co-precipitation method was reported. Efforts have been made to control the particles size, distribution, morphology and magnetic properties of cobalt ferrite nanoparticles by varying the concentration of NaOH solution and microwave irradiation time. It was observed that the rate of nucleation and crystal growth was influenced by the tuning parameters. In that way, the average crystallite size of single phase cobalt ferrite nanoparticles was controlled within 9-11 and 10-12 nm with an increase of base concentration and microwave irradiation time, respectively. A narrow size distribution of nearly spherical nanoparticles was achieved through the present procedure. A soft ferromagnetism at room temperature with the considerable saturation magnetization of 58.4 emu g-1 and coercivity of 262.7 Oe was obtained for the cobalt ferrites synthesized with 2.25 M of NaOH solution for 3 and 7 min of microwave irradiation time, respectively. The cobalt ferrite nanoparticles synthesized with a shorter reaction time of 3-7 min was found to be advantageous over other methods that involved conventional heating procedures and longer reaction time to achieve the better magnetic properties for the technological applications.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kakade, S. G., E-mail: sundipkakade@gmail.com, E-mail: ydk@physics.unipune.ac.in; Department of Physics, Sir Parashurambhau College, Pune-411 030; Kambale, R. C.

Cobalt ferrite (CoFe{sub 2}O{sub 4}) shown to be promising candidate for applications such as high-density magnetic recording, enhanced memory storage, magnetic fluids and catalysts. Utility of ferrite nanoparticles depends on its size, dispersibility in solutions, and magnetic properties. We have investigated the structural properties of synthesized cobalt ferrite nanoparticles synthesized by sol gel auto combustion for uncontrolled, acidic, neutral and basic pH values. X-ray diffraction (XRD) study confirms the cubic spinel phase formation with lattice constant 8.38 Å. In this study, we have optimized the pH value to synthesize homogenous cobalt ferrite nanoparticles with enhanced magnetic behavior. The surface morphologymore » has been investigated by employing SEM images and the confirmation of spinel ferrite was also supported by using IR spectroscopy. Magnetic measurements for CoFe{sub 2}O{sub 4} compositions (with pH <1, pH = 3, 7, 10) were investigated using VSM measurements.« less

Microstructural development of cobalt ferrite ceramics and its influence on magnetic properties

NASA Astrophysics Data System (ADS)

Kim, Gi-Yeop; Jeon, Jae-Ho; Kim, Myong-Ho; Suvorov, Danilo; Choi, Si-Young

2013-11-01

The microstructural evolution and its influence on magnetic properties in cobalt ferrite were investigated. The cobalt ferrite powders were prepared via a solid-state reaction route and then sintered at 1200 °C for 1, 2, and 16 h in air. The microstructures from sintered samples represented a bimodal distribution of grain size, which is associated with abnormal grain growth behavior. And thus, with increasing sintering time, the number and size of abnormal grains accordingly increased but the matrix grains were frozen with stagnant grain growth. In the sample sintered for 16 h, all of the matrix grains were consumed and the abnormal grains consequently impinged on each other. With the appearance of abnormal grains, the magnetic coercivity significantly decreased from 586.3 Oe (1 h sintered sample) to 168.3 Oe (16 h sintered sample). This is due to the magnetization in abnormal grains being easily flipped. In order to achieve high magnetic coercivity of cobalt ferrite, it is thus imperative to fabricate the fine and homogeneous microstructure.

Low laser power micro-Raman study of Co{sub (1−x)}Mn{sub (x)}Fe{sub 2}O{sub 4} prepared by flash combustion method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Baraliya, J. D.

2016-05-23

Manganese substituted Cobalt ferrites of composition with nominal formula Co{sub (1−x)}Mn{sub (x)}Fe{sub 2}O{sub 4} (x = 0.0, 0.2, 0.4, 0.6, 0.8, 1.0) prepared by the Flash Combustion Method(FCM). The single phase spinel formation of nano ferrites was confirmed by X-ray diffraction techniques and micro - Raman spectroscopy. The particle size calculated from the Scherrer formula varied within 13 to 17 nm. Lattice parameter, nano particle size, and cation distribution were quantified as a function of the Mn-content in the range x = 0.0 to 1.0. Micro-Raman spectroscopic studies yielded convincing evidence for a transformation of the structure.

Cation distributions on rapidly solidified cobalt ferrite

NASA Technical Reports Server (NTRS)

De Guire, Mark R.; Kalonji, Gretchen; O'Handley, Robert C.

1990-01-01

The cation distributions in two rapidly solidified cobalt ferrites have been determined using Moessbauer spectroscopy at 4.2 K in an 8-T magnetic field. The samples were obtained by gas atomization of a Co0-Fe2O3-P2O5 melt. The degree of cation disorder in both cases was greater than is obtainable by cooling unmelted cobalt ferrite. The more rapidly cooled sample exhibited a smaller departure from the equilibrium cation distribution than did the more slowly cooled sample. This result is explained on the basis of two competing effects of rapid solidification: high cooling rate of the solid, and large undercooling.

Comprehensive analysis of structure and temperature, frequency and concentration-dependent dielectric properties of lithium-substituted cobalt ferrites (Li x Co1- x Fe2O4)

NASA Astrophysics Data System (ADS)

Anjum, Safia; Nisa, Mehru; Sabah, Aneeqa; Rafique, M. S.; Zia, Rehana

2017-08-01

This paper has been dedicated to the synthesis and characterization of a series of lithium-substituted cobalt ferrites Li x Co1- x Fe2O4 ( x = 0, 0.2, 0.4, 0.6, 0.8, 1). These samples have been prepared using simple ball milling machine through powder metallurgy route. The structural analysis is carried out using X-ray diffractometer and their 3D vitalization is simulated using diamond software. The frequency and temperature-dependent dielectric properties of prepared samples have been measured using inductor capacitor resistor (LCR) meter. The structural analysis confirms that all the prepared samples have inverse cubic spinel structure. It is also revealed that the crystallite size and lattice parameter decrease with the increasing concentration of lithium (Li+1) ions, it is due to the smaller ionic radii of lithium ions. The comprehensive analysis of frequency, concentration and temperature-dependent dielectric properties of prepared samples is described in this paper. It is observed that the dielectric constant and tangent loss have decreased and conductivity increased as the frequency increases. It is also revealed that the dielectric constant, tangent loss and AC conductivity increase as the concentration of lithium increases due to its lower electronegativity value. Temperature plays a vital role in enhancing the dielectric constant, tangent loss and AC conductivity because the mobility of ions increases as the temperature increases.

General control of transition-metal-doped GaN nanowire growth: toward understanding the mechanism of dopant incorporation.

PubMed

Stamplecoskie, Kevin G; Ju, Ling; Farvid, Shokouh S; Radovanovic, Pavle V

2008-09-01

We report the first synthesis and characterization of cobalt- and chromium-doped GaN nanowires (NWs), and compare them to manganese-doped GaN NWs. Samples were synthesized by chemical vapor deposition method, using cobalt(II) chloride and chromium(III) chloride as dopant precursors. For all three impurity dopants hexagonal, triangular, and rectangular NWs were observed. The fraction of NWs having a particular morphology depends on the initial concentration of the dopant precursors. While all three dopant ions have the identical effect on GaN NW growth and faceting, Co and Cr are incorporated at much lower concentrations than Mn. These findings suggest that the doping mechanism involves binding of the transition-metal intermediates to specific NW facets, inhibiting their growth and causing a change in the NW morphology. We discuss the doping concentrations of Mn, Co, and Cr in terms of differences in their crystal-field stabilization energies (DeltaCFSE) in their gas-phase intermediates and in substitutionally doped GaN NWs. Using iron(III) chloride and cobalt(II) acetate as dopant precursors we show that the doping concentration dependence on DeltaCFSE allows for the prediction of achievable doping concentrations for different dopant ions in GaN NWs, and for a rational choice of a suitable dopant-ion precursor. This work further demonstrates a general and rational control of GaN NW growth using transition-metal impurities.

Nanophase cobalt, nickel and zinc ferrites: synchrotron XAS study on the crystallite size dependence of metal distribution.

PubMed

Nordhei, Camilla; Ramstad, Astrid Lund; Nicholson, David G

2008-02-21

Nanophase cobalt, nickel and zinc ferrites, in which the crystallites are in the size range 4-25 nm, were synthesised by coprecipitation and subsequent annealing. X-Ray absorption spectroscopy using synchrotron radiation (supported by X-ray powder diffraction) was used to study the effects of particle size on the distributions of the metal atoms over the tetrahedral and octahedral sites of the spinel structure. Deviations from the bulk structure were found which are attributed to the significant influence of the surface on very small particles. Like the bulk material, nickel ferrite is an inverse spinel in the nanoregime, although the population of metals on the octahedral sites increases with decreasing particle size. Cobalt ferrite and zinc ferrite take the inverse and normal forms of the spinel structure respectively, but within the nanoregime both systems show similar trends in being partially inverted. Further, in zinc ferrite, unlike the normal bulk structure, the nanophase system involves mixed coordinations of zinc(ii) and iron(iii) consistent with increasing partial inversion with size.

Low temperature synthesis and enhanced electrical properties by substitution of Al3+ and Cr3+ in Co-Ni nanoferrites

NASA Astrophysics Data System (ADS)

Pervaiz, Erum; Gul, I. H.

2013-10-01

Aluminum and chromium substituted Co-Ni spinel nanoferrites were prepared by sol-gel auto combustion method. Structural parameters along with electrical and magnetic properties have been investigated in the present work. Crystallite sizes of nano ferrite estimated from the peak (311) lies in the range of 13-21 nm ±2 nm and compared with crystallite sizes calculated from Williamsons-Hall plots. DC electrical resistivity variations due to the concentration of aluminum and chromium in the host ferrite have been measured from 368 K to 573 K. Increase in the room temperature DC electrical resistivity was observed up to a concentration x=0.2 and then decreases for x >0.2. Dielectric parameters (real and imaginary part of complex permittivity, dielectric loss tangent) were studied as a function of frequency (20 Hz-5 MHz) and a decrease in the dielectric parameters was observed due to substitution of nickel, aluminum and chromium ions in cobalt nanoferrites. AC conductivity, complex impedance and complex electrical modulus were studied as a function of frequency for the conduction and relaxation mechanisms in the present ferrite system. Saturation magnetization, coercivity, canting angles and magneto crystalline anisotropy variations with composition were observed and presented for the present ferrites under an applied magnetic field of 10 kOe at room temperature. It was found that both magnetization and coercivity decreases with increase in the concentration of aluminum and chromium along with a decrease in the anisotropy parameters. High DC resistivity with low dielectric parameters of the present nanoferrites make them suitable for high frequency and electromagnetic wave absorbing devices. High purity mixed Co-Ni-Al-Cr nanoferrites have been prepared by sol-gel auto combustion method. DC electrical resistivity increases due to substitution of Al3+ and Cr3+. Complex permittivity decrease for Co-Ni-Al-Cr nanoferrites. Detailed AC response analysis has been presented for mixed Co-Ni-Al-Cr nanoferrites. Magnetization and coercively reduces for Al3+ and Cr3+ doped Co-Ni ferrite nanoparticles showing that material is becoming soft magnetic.

Comparison of effects of overload on parameters and performance of samarium-cobalt and strontium-ferrite radially oriented permanent magnet brushless DC motors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Demerdash, N.A.; Nehl, T.W.; Nyamusa, T.A.

1985-08-01

Effects of high momentary overloads on the samarium-cobalt and strontium-ferrite permanent magnets and the magnetic field in electronically commutated brushless dc machines, as well as their impact on the associated machine parameters were studied. The effect of overload on the machine parameters, and subsequently on the machine system performance was also investigated. This was accomplished through the combined use of finite element analysis of the magnetic field in such machines, perturbation of the magnetic energies to determine machine inductances, and dynamic simulation of the performance of brushless dc machines, when energized from voltage source inverters. These effects were investigated throughmore » application of the above methods to two equivalent 15 hp brushless dc motors, one of which was built with samarium-cobalt magnets, while the other was built with strontium- ferrite magnets. For momentary overloads as high as 4.5 p.u. magnet flux reductions of 29% and 42% of the no load flux were obtained in the samarium-cobalt and strontiumferrite machines, respectively. Corresponding reductions in the line to line armature inductances of 52% and 46% of the no load values were reported for the samarium-cobalt and strontium-ferrite cases, respectively. The overload affected the profiles and magnitudes of armature induced back emfs. Subsequently, the effects of overload on machine parameters were found to have significant impact on the performance of the machine systems, where findings indicate that the samarium-cobalt unit is more suited for higher overload duties than the strontium-ferrite machine.« less

Evidence for reentrant spin glass behavior in transition metal substituted Co-Ga alloys near critical concentration

NASA Astrophysics Data System (ADS)

Yasin, Sk. Mohammad; Srinivas, V.; Kasiviswanathan, S.; Vagadia, Megha; Nigam, A. K.

2018-04-01

In the present study magnetic and electrical transport properties of transition metal substituted Co-Ga alloys (near critical cobalt concentration) have been investigated. Analysis of temperature and field dependence of dc magnetization and ac susceptibility (ACS) data suggests an evidence of reentrant spin glass (RSG) phase in Co55.5TM3Ga41.5 (TM = Co, Cr, Fe, Cu). The magnetic transition temperatures (TC and Tf) are found to depend on the nature of TM element substitution with the exchange coupling strength Co-Fe > Co-Co > Co-Cu > Co-Cr. From magnetization dynamics precise transition temperatures for the glassy phases are estimated. It is found that characteristic relaxation times are higher than that of spin glasses with minimal spin-cluster formation. The RSG behavior has been further supported by the temperature dependence of magnetotransport studies. From the magnetic field and substitution effects it has been established that the magnetic and electrical transport properties are correlated in this system.

Optimization of the behavior of CTAB coated cobalt ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Kumari, Mukesh; Bhatnagar, Mukesh Chander

2018-05-01

In this work, we have synthesized cetyltrimethyl ammonium bromide (CTAB) mixed cobalt ferrite (CoFe2O4) nanoparticles (NPs) using sol-gel auto-combustion method taking a different weight percent ratio of CTAB i.e., 0%, 1%, 2%, 3% and 4% with respect to metal nitrates. The morphological, structural and magnetic properties of these NPs are characterized by high resolution transmitted electron microscopy (HRTEM), X-ray diffraction (XRD), Raman spectrometer and physical property measurement system (PPMS). It has been found that saturation magnetization of cobalt ferrite increases with increase in crystalline size of the NPs. Saturation magnetization and crystallite size both were found to be lowest in the case of sample containing 2% CTAB.

Modulation in magnetic exchange interaction, core shell structure and Hopkinson's peak with chromium substitution into Ni0.75Co0.25Fe2O4 nano particles

NASA Astrophysics Data System (ADS)

Uday Bhasker, S.; Choudary, G. S. V. R. K.; Reddy, M. V. Ramana

2018-05-01

The ever growing applications and ever evolving challenges of magnetic nano particles has been motivating the researchers from various disciplines towards this area of magnetic nano particles. Cation substitutional effect on the magnetic structure of the nanoparticles forms a crucial aspect in their applications. Here the environmentally benign auto combustion method was employed to synthesize chromium substituted nickel cobalt ferrite (Ni0.75Co0.25Fe2-xCrxO4; x = 0, 0.10, 0.15) nano particles, from aqueous metal nitrate solutions. Chromium substitution has shown its effect on the structural, magnetic and electrical properties of Ni0.75Co0.25Fe2O4. Structural and phase analysis of the prepared samples show increased phase purity of ferrite sample with increasing Cr substitution. The TEM (Transmission Electron Microscope) image confirms the nano size of the particles, EDS (Energy dispersive X-ray Spectroscopy) has supported the stoichiometry of the prepared samples and FTIR (Fourier-transform infrared spectroscopic) analysis confirms the spinel structure and also suggests cation redistributions with chromium substitution. VSM (Vibrational Sample Magnetometer) is used to study the magnetic properties through magnetic hysteresis (M-H) loop and magnetic Hopkinson effect. All samples show hysteresis and show reduction in magnetic properties with increase in chromium content. The thermo magnetic study shows Hopkinson peak(s) in the magnetization vs. temperature (M-T) graph and also shows variation in the nature of Hopkinson peak with chromium substitution. Possible reasons for the changes in the nature of the peak are discussed.

Effect of the adsorption of lithium and borate species on the zeta potential of particles of cobalt ferrite, nickel ferrite, and magnetite.

PubMed

Barale, M; Lefèvre, G; Carrette, F; Catalette, H; Fédoroff, M; Cote, G

2008-12-01

Zetametric measurements on suspensions of oxide particles (cobalt ferrite, nickel ferrite, and magnetite) representative of corrosion products from primary circuits of pressurized water reactors were performed at 25 and 70 degrees C in the presence of lithium and borate species. No effect of lithium ions was observed. Borate species cause a decrease of the isoelectric point (IEP), attributed to the sorption of borate as a negative complex MOB(OH)3(-). A predictive model based on thermodynamic calculations (2-pK and diffuse layer models) of the surface acidity constants from the data of acid-base titrations combined with an empirical relationship between the surface potential Psi 0 and the zeta potential determined by zetametry was developed. A whole set of parameters valid at 25 degrees C, in a range of ionic strength between 10(-4) and 10(-2) molL(-1) and in a range of pH between 4 and 8, was determined for this model. Increase of temperature to 70 degrees C in the presence of borate results in a decrease of IEP for cobalt ferrite and an increase of the IEP for nickel ferrite.

Synthesis and characterization of CoFe2O4/polyaniline nanocomposites for electromagnetic interference applications.

PubMed

Praveena, K; Srinath, S

2014-06-01

The Cobalt ferrite (CoFe2O4) powders were synthesized by Co-precipitation method. The as prepared ferrite powders were incorporated into a polyaniline matrix at various volumetric ratios. The as prepared composites of ferrite and polyaniline powders were characterized using X-ray diffraction (XRD), transmission electron microscope (TEM). The particle size of CoFe2O4 is found to be 20 nm. The saturation magnetization (M(s)) of all the composites was found to be decreasing with decrease of ferrite content, while coercivity (H(c)) remained at the value corresponding to pure cobalt ferrite nanopowders. The complex permittivity (epsilon' and epsilon") and permeability (mu' and mu") of composite samples were measured in the range of 1 MHz to 1.1 GHz. The value of epsilon' and mu' found to be increased with ferrite volume concentration.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Coker, Eric Nicholas; Rodriguez, Mark A.; Ambrosini, Andrea

Hydrogen and carbon monoxide may be produced using solar-thermal energy in two-stage reactions of water and carbon dioxide, respectively, over certain metal oxide materials. The most active materials observed experimentally for these processes are complex mixtures of ferrite and zirconia based solids, and it is not clear how far the ferrites, the zirconia, or a solid solution between the two participate in the change of oxidation state during the cycling. Identification of the key phases in the redox material that enable splitting is of paramount importance to developing a working model of the materials. A three-pronged approach was adopted here:more » computer modeling to determine thermodynamically favorable materials compositions, bench reactor testing to evaluate materials’ performance, and in-situ characterization of reactive materials to follow phase changes and identify the phases active for splitting. For the characterization and performance evaluation thrusts, cobalt ferrites were prepared by co-precipitation followed by annealing at 1400 °C. An in-situ X-ray diffraction capability was developed and tested, allowing phase monitoring in real time during thermochemical redox cycling. Key observations made for an un-supported cobalt ferrite include: 1) ferrite phases partially reduce to wustite upon heating to 1400 °C in helium; 2) exposing the material to air at 1100 °C causes immediate re-oxidation; 3) the re-oxidized material may be thermally reduced at 1400 °C under inert; 4) exposure of a reduced material to CO 2 results in gradual re-oxidation at 1100 °C, but minimization of background O 2-levels is essential; 5) even after several redox cycles, the lattice parameters of the ferrites remain constant, indicating that irreversible phase separation does not occur, at least over the first five cycles; 6) substituting chemical (hydrogen) reduction for thermal reduction resulted in formation of a CoFe metallic alloy. Materials were also evaluated for their CO 2-splitting performance in bench reactor systems utilizing chemical reduction in place of thermal reduction. These tests lead to the following general conclusions: 1) despite over-reduction of the cobalt ferrite phase to CoFe alloy on chemical reduction, splitting of CO 2 still occurs; 2) the kinetics of chemical reduction follow the sequence: un-supported < ZrO 2-supported < yttria-stabilized ZrO 2 (YSZ)-supported ferrite; 3) ferrite/YSZ re-oxidizes faster than ferrite/ZrO 2 under CO 2 in the range 400 – 700 °C. The temperature and pressure regimes in which the thermal reduction and water-splitting steps are thermodynamically favorable in terms of the enthalpy and entropy of oxide reduction, were determined. These metrics represent a useful design goal for any proposed water-splitting cycle. Applying this theoretical framework to available thermodynamic data, it was shown that none of the 105 binary oxide redox couples that were screened possess both energetically favorable reduction and oxidation steps. However, several driving forces, including low pressure and a large positive solid-state entropy of reduction of the oxide, have the potential to enable thermodynamically-favored two-step cycles.« less

Cation distribution correlated with magnetic properties of cobalt ferrite nanoparticles defective by vanadium doping

NASA Astrophysics Data System (ADS)

Heiba, Zein K.; Mohamed, Mohamed Bakr; Ahmed, S. I.

2017-11-01

Nanoparticles cobalt ferrite, vacancies defective through vanadium substitution for iron, were synthesized by a sol-gel method. Two systems CoFe2-xVxO4 (0.0 ≤ x ≤ 0.25) and CoFe2-1.67xVxO4 (x = 0.1, 0.2) were prepared. The crystal structure, microstructure and magnetic properties were investigated using XRD, SEM and VSM magnetometer. The occupancy of tetrahedral and octahedral sites by different cations was determined by Rietveld analysis and correlated with magnetic measurements. Vanadium resides at octahedral sites up to x = 0.10, while for higher values it resides mainly at octahedral sites with a lesser amount at the tetrahedrons. Upon increasing the vanadium content, the cell parameter decreases and the bond lengths of the tetrahedral and octahedral sites change opposite to each other. The change in the coercivity and saturation magnetization is correlated with cation distribution. For the same amount of doping x, the iron deficient samples CoFe2-1.67xVxO4 have saturation magnetization obviously reduced than the corresponding samples in CoFe2-xVxO4. The spin canting between cations in A- and B- sites was discussed in details based on Yafet-Kittel triangular arrangement model.

Nickel(0) nanoparticles supported on bare or coated cobalt ferrite as highly active, magnetically isolable and reusable catalyst for hydrolytic dehydrogenation of ammonia borane.

PubMed

Manna, Joydev; Akbayrak, Serdar; Özkar, Saim

2017-12-15

Nickel(0) nanoparticles supported on cobalt ferrite (Ni 0 /CoFe 2 O 4 ), polydopamine coated cobalt ferrite (Ni 0 /PDA-CoFe 2 O 4 ) or silica coated cobalt ferrite (Ni 0 /SiO 2 -CoFe 2 O 4 ) are prepared and used as catalysts in hydrogen generation from the hydrolysis of ammonia borane at room temperature. Ni 0 /CoFe 2 O 4 (4.0% wt. Ni) shows the highest catalytic activity with a TOF value of 38.3min -1 in hydrogen generation from the hydrolysis of ammonia borane at 25.0±0.1°C. However, the initial catalytic activity of Ni 0 /CoFe 2 O 4 catalyst is not preserved in subsequent runs of hydrolysis. Coating the surface of cobalt ferrite support with polydopamine or silica leads to a significant improvement in the stability of catalysts. The TOF values of Ni 0 /PDA-CoFe 2 O 4 and Ni 0 /SiO 2 -CoFe 2 O 4 are found to be 7.6 and 5.3min -1 , respectively, at 25.0±0.1°C. Ni 0 /PDA-CoFe 2 O 4 catalyst shows high reusability as compared to the Ni 0 /CoFe 2 O 4 and Ni 0 /SiO 2 -CoFe 2 O 4 catalysts in hydrolytic dehydrogenation of ammonia borane at room temperature. All the catalysts are characterized by using a combination of various advanced analytical techniques. The results reveal that nickel nanoparticles with an average size of 12.3±0.7nm are well dispersed on the surface of PDA-CoFe 2 O 4 . . Copyright © 2017 Elsevier Inc. All rights reserved.

Refinement of atomic and magnetic structures using neutron diffraction for synthesized bulk and nano-nickel zinc gallate ferrite

NASA Astrophysics Data System (ADS)

Ata-Allah, S. S.; Balagurov, A. M.; Hashhash, A.; Bobrikov, I. A.; Hamdy, Sh.

2016-01-01

The parent NiFe2O4 and Zn/Ga substituted spinel ferrite powders have been prepared by solid state reaction technique. As a typical example, the Ni0.7Zn0.3Fe1.5Ga0.5O4 sample has been prepared by sol-gel auto combustion method with the nano-scale crystallites size. X-ray and Mössbauer studies were carried out for the prepared samples. Structure and microstructure properties were investigated using the time-of-flight HRFD instrument at the IBR-2 pulsed reactor, at a temperatures range 15-473 K. The Rietveld refinement of the neutron diffraction data revealed that all samples possess cubic symmetry corresponding to the space group Fd3m. Cations distribution show that Ni2+ is a complete inverse spinel ion, while Ga3+ equally distributed between the two A and B-sublattices. The level of microstrains in bulk samples was estimated as very small while the size of coherently scattered domains is quite large. For nano-structured sample the domain size is around 120 Å.

Magnetic and absorbing properties of M-type substituted hexaferrites BaFe{sub 12–x}Ga{sub x}O{sub 19} (0.1 < x < 1.2)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Trukhanov, S. V., E-mail: trukhanov@ifttp.bas-net.by; Trukhanov, A. V.; Kostishin, V. G.

2016-09-15

X-ray powder diffraction is used to determine the unit cell parameters and to refine the crystal structure of the solid solutions of M-type hexagonal barium ferrite BaFe{sub 12–x}Ga{sub x}O{sub 19} (x = 0.1–1.2) with isostructural diamagnetic cation Ga{sup 3+} substitution at T = 300 K. As the level of substitution increases, the unit cell parameters are shown to decrease monotonically. The temperature (300 K ≤ T ≤ 750 K, H = 8.6 kOe) and field (T = 300 K,–20 kOe ≤ H ≤ 20 kOe) dependences of the saturation magnetization of these solid solutions are studied with a vibrating-sample magnetometer.more » The concentration dependences of the Curie temperature T{sub C}, the specific spontaneous magnetization, and the coercive force are plotted. The magnetic parameters are found to decrease with increasing substitution. The microwave properties of the solid solutions are analyzed in an external magnetic field (0 ≤ H ≤ 4 kOe). As the cation Ga{sup 3+} concentration increases from x = 0.1 to 0.6, the natural ferromagnetic resonance (NFMR) frequency decreases; as the concentration increases further to x = 1.2, this frequency again increases. As the cation Ga{sup 3+} concentration increases, the NFMR line width increases, which indicates a widening of the frequency range where electromagnetic radiation is intensely absorbed. Here, the resonance curve peak amplitude changes insignificantly. The shift of the NFMR frequency in an applied magnetic field is more pronounced for samples with low cation Ga{sup 3+} concentrations. The role of diamagnetic substitution is revealed, and the prospects and advantages of Ga-substituted beryllium hexaferrite as the material absorbing high-frequency electromagnetic radiation are demonstrated.« less

U.S. Navy Halon 1211 Replacement Program: Assessment of Aircraft Collateral Damage From Dry Chemical Fire Extinguishing Agents.

DTIC Science & Technology

1999-11-15

copper and steels are used in the " low " temperature applications. Stainless steel , titanium, nickel and cobalt alloys are used...The ferritic stainless steels are also named for the analogous ferrite phase , relatively pure iron, of carbon steels . As the martensitic stainless... steels , stainless steels , copper alloys , nickel alloys and cobalt alloys . A major discriminator in the use of these

Synthesis of Novel Ferrite Based Recyclable Catalyst Used to Clean Dye and Emerging Contaminates from Water

EPA Science Inventory

Herein, we describe synthesis of novel palladium, copper, cobalt and vanadium ferrites. The ferrites were synthesized by combustion method using polyvinyl alcohol. The particles phases were confirmed using X-ray diffraction and sizes were determined using particle size analyzer. ...

Enhancement in surface area and magnetization of CoFe2O4 nanoparticles for targeted drug delivery application

NASA Astrophysics Data System (ADS)

Kale, Swati B.; Somvanshi, Sandeep B.; Sarnaik, M. N.; More, S. D.; Shukla, S. J.; Jadhav, K. M.

2018-05-01

This paper reports facile synthesis, characterizations by X-ray diffraction and scanning electron microscopy and magnetic behaviour of cobalt ferrite nanoparticles. Cobalt ferrite nanoparticles were prepared by sol-gel auto combustion technique using glycine as a fuel. Phase purity and nanocrystalline nature of the prepared sample was confirmed through X-ray diffraction technique. No extra peak other than cubic spinel structure was observed in the XRD pattern. The crystallite size calculated by using Scherrer's formula is of the order of 21.6 nm indicating the nanocrystalline nature of the prepared cobalt ferrite sample. The surface morphological studies were carried out using scanning electron microscope (SEM). SEM image shows homogeneous, agglomerated particles with sponge-like form. The saturation magnetization, coercivity and remenance magnetization obtained by hysteresis curve clearly gives the evidence of excellent and enhanced magnetic behaviour.

Correlation between structural, magnetic, and dielectric properties of manganese substituted cobalt ferrite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ramana, C. V., E-mail: rvchintalapalle@utep.edu; Kolekar, Y. D.; Kamala Bharathi, K.

2013-11-14

Manganese (Mn) substituted cobalt ferrites (CoFe{sub 2−x}Mn{sub x}O{sub 4}, referred to CFMO) were synthesized and their structural, magnetic, and dielectric properties were evaluated. X-ray diffraction measurements coupled with Rietveld refinement indicate that the CFMO materials crystallize in the inverse cubic spinel phase. Temperature (T = 300 K and 10 K) dependent magnetization (M(H)) measurements indicate the long range ferromagnetic ordering in CoFe{sub 2−x}Mn{sub x}O{sub 4} (x = 0.00–0.15) ferrites. The cubic anisotropy constant (K{sub 1}(T)) and saturation magnetization (M{sub s}(T)) were derived by using the “law of approach” to saturation that describes the field dependence of M(H) for magnetic fields much higher than the coercive fieldmore » (H{sub c}). Saturation magnetization (M{sub s}), obtained from the model, decreases with increasing temperature. For CoFe{sub 2}O{sub 4}, M{sub s} decreases from 3.63 μ{sub B} per formula unit (f.u.) to 3.47 μ{sub B}/f.u. with increasing temperature from 10 to 300 K. CFMO (0.00–0.15) exhibit the similar trend while the magnitude of M{sub s} is dependent on Mn-concentration. M{sub s}-T functional relationship obeys the Bloch's law. The lattice parameter and magnetic moment calculated for CFMO reveals that Mn ions occupying the Fe and Co position at the octahedral site in the inverse cubic spinel phase. The structure and magnetism in CFMO are further corroborated by bond length and bond angle calculations. The dielectric constant dispersion of CFMO in the frequency range of 20 Hz–1 MHz fits to the modified Debye's function with more than one ion contributing to the relaxation. The relaxation time and spread factor derived from modeling the experimental data are ∼10{sup −4} s and ∼0.35(±0.05), respectively.« less

Influence of La3+ Substitution on Structure, Morphology and Magnetic Properties of Nanocrystalline Ni-Zn Ferrite

PubMed Central

Dasan, Y. K.; Guan, B. H.; Zahari, M. H.; Chuan, L. K.

2017-01-01

Lanthanum substituted Ni-Zn ferrite nanoparticles (Ni0.5Zn0.5LaxFe1-xO4; 0.00 ≤x≤ 1.00) synthesized by sol-gel method were presented. X-ray diffraction patterns reveal the typical single phase spinel cubic ferrite structure, with the traces of secondary phase for lanthanum substituted nanocrystals. In addition, the structural analysis also demonstrates that the average crystallite size varied in the range of 21–25 nm. FTIR spectra present the two prominent absorption bands in the range of 400 to 600 cm-1 which are the fingerprint region of all ferrites. Surface morphology of both substituted and unsubstituted Ni-Zn ferrite nanoparticle samples was studied using FESEM technique and it indicates a significant increase in the size of spherical shaped particles with La3+ substitution. Magnetic properties of all samples were analyzed using vibrating sample magnetometer (VSM). The results revealed that saturation magnetization (Ms) and coercivity (Hc) of La3+ substituted samples has decreased as compared to the Ni-Zn ferrite samples. Hence, the observed results affirm that the lanthanum ion substitution has greatly influenced the structural, morphology and magnetic properties of Ni-Zn ferrite nanoparticles. PMID:28081257

Influence of La3+ Substitution on Structure, Morphology and Magnetic Properties of Nanocrystalline Ni-Zn Ferrite.

PubMed

Dasan, Y K; Guan, B H; Zahari, M H; Chuan, L K

2017-01-01

Lanthanum substituted Ni-Zn ferrite nanoparticles (Ni0.5Zn0.5LaxFe1-xO4; 0.00 ≤x≤ 1.00) synthesized by sol-gel method were presented. X-ray diffraction patterns reveal the typical single phase spinel cubic ferrite structure, with the traces of secondary phase for lanthanum substituted nanocrystals. In addition, the structural analysis also demonstrates that the average crystallite size varied in the range of 21-25 nm. FTIR spectra present the two prominent absorption bands in the range of 400 to 600 cm-1 which are the fingerprint region of all ferrites. Surface morphology of both substituted and unsubstituted Ni-Zn ferrite nanoparticle samples was studied using FESEM technique and it indicates a significant increase in the size of spherical shaped particles with La3+ substitution. Magnetic properties of all samples were analyzed using vibrating sample magnetometer (VSM). The results revealed that saturation magnetization (Ms) and coercivity (Hc) of La3+ substituted samples has decreased as compared to the Ni-Zn ferrite samples. Hence, the observed results affirm that the lanthanum ion substitution has greatly influenced the structural, morphology and magnetic properties of Ni-Zn ferrite nanoparticles.

Giant magneto-optical Kerr rotation, quality factor and figure of merit in cobalt-ferrite magnetic nanoparticles doped in silica matrix as the only defect layer embedded in magnetophotonic crystals

NASA Astrophysics Data System (ADS)

Zamani, Mehdi; Hocini, Abdesselam

2018-03-01

In this work, we report on the theoretical study of one-dimensional magnetophotonic crystals (MPC) comprising of periodic dielectric structure Si/SiO and of silica matrix doped with cobalt-ferrite (CoFe2O4) magnetic nanoparticles as the only magnetic defect layer. Such structure can be prepared by sol-gel dip coating method that controls the thickness of each layer with nanometer level, hence, can overcome the problem of integration of the magneto-optical (MO) devices. We have studied the influence of the volume fraction (concentration of magnetic nanoparticles VF%) on the optical (reflectance, transmittance and absorption) and MO (Kerr rotation) responses in reflection-type one-dimensional MPCs. During investigation of the influence of magnetic nanoparticle's concentration, we found that giant Kerr rotations (even ≈135° for VF = 39%) can be obtained accompanied by large reflectance and low amounts for transmittance and absorption. We report on the demonstration of large MO quality factor and figure of merit in cobalt-ferrite magnetic nanoparticles in the infrared regime. Given the large Kerr rotation, high reflectance accompanied by low absorption and nearly zero transmittance of the 1D MPC containing cobalt-ferrite magnetic nanoparticles, large MO Q factor and figure of merit are obtained.

Characterization and Applications of Micro- and Nano- Ferrites at Microwave and Millimeter Waves

NASA Astrophysics Data System (ADS)

Chao, Liu

Ferrite materials are one of the most widely used magnetic materials in microwave and millimeter wave applications such as radar, wireless communication. They provide unique properties for microwave and millimeter wave devices especially non-reciprocal devices. Some ferrite materials with strong magnetocrystalline anisotropy fields can extend these applications to tens of GHz range while reducing the size, weight and cost. This thesis focuses on characterization of such ferrite materials as micro- and nano-powder and the fabrication of the devices. The ferrite materials with strong magnetocrystalline anisotropy field are metal/non-metal substituted iron oxides oriented in low crystal symmetry. The ferrite materials characterized in this thesis include M-type hexagonal ferrites such as barium ferrite (BaFe12O19), strontium ferrite (SrFe12O19), epsilon phase iron oxide (epsilon-Fe 2O3), substituted epsilon phase iron oxide (epsilon-Ga xFe2-xO3, epsilon-AlxFe2-xO 3). These ferrites exhibit great anisotropic magnetic fields. A transmission-reflection based in-waveguide technique that employs a vector network analyzer was used to determine the scattering parameters for each sample in the microwave bands (8.2--40 GHz). From the S-parameters, complex dielectric permittivity and complex magnetic permeability are evaluated by an improved algorithm. The millimeter wave measurement is based on a free space quasi-optical spectrometer. Initially precise transmittance spectra over a broad millimeter wave frequency range from 40 GHz to 120 GHz are acquired. Later the transmittance spectra are converted into complex permittivity and permeability spectra. These ferrite powder materials are further characterized by x-ray diffraction (XRD) to understand the crystalline structure relating to the strength and the shift of the ferromagnetic resonance affected by the particle size. A Y-junction circulator working in the 60 GHz frequency band is designed based on characterized M-type barium micro- and nano-ferrite. A new fabrication process using ferrite composite is proposed to integrate the Y-junction circulator into the semiconductor substrate. Theoretical design of a high gain Traveling Wave Tube (TWT) amplifier using a metamaterial (MTM) structure and cold-test of the MTM structure are also included in this dissertation. An SWS working around 6 GHz below the X-band waveguide TE10 cutoff frequency is fabricated.

Structural analysis of emerging ferrite: Doped nickel zinc ferrite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kumar, Rajinder; Kumar, Hitanshu; Singh, Ragini Raj

2015-08-28

Ni{sub 0.6-x}Zn{sub 0.4}Co{sub x}Fe{sub 2}O{sub 4} (x = 0, 0.033, 0.264) nanoparticles were synthesized by sol-gel method and annealed at 900°C. Structural properties of all prepared samples were examined with X-ray diffraction (XRD). The partial formation of hematite (α-Fe{sub 2}O{sub 3}) secondary phase with spinel phase cubic structure of undoped and cobalt doped nickel zinc ferrite was found by XRD peaks. The variation in crystallite size and other structural parameters with cobalt doping has been calculated for most prominent peak (113) of XRD and has been explained on the basis of cations ionic radii difference.

Size dependence of magnetorheological properties of cobalt ferrite ferrofluid

DOE Office of Scientific and Technical Information (OSTI.GOV)

Radhika, B.; Sahoo, Rasmita; Srinath, S., E-mail: srinath@uohyd.ac.in

2015-06-24

Cobalt Ferrite nanoparticles were synthesized using co-precipitation method at reaction temperatures of 40°C and 80°C. X-Ray diffraction studies confirm cubic phase formation. The average crystallite sizes were found to be ∼30nm and ∼48nm for 40°C sample and 80°C sample respectively. Magnetic properties measured using vibrating sample magnetometer show higher coercivety and magnetization for sample prepared at 80°C. Magnetorheological properties of CoFe2O4 ferrofluids were measured and studied.

Structural and DC electrical resistivity, magnetic properties of Co0.5M0.5Fe2O4 (M= Ni, Zn, and Mg) ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Ramakrishna, A.; Murali, N.; Mammo, Tulu Wegayehu; Samatha, K.; Veeraiah, V.

2018-04-01

Inverse spinel structured nanoparticles of cobalt ferrite partially substituted by divalent cations of Ni, Zn, and Mg have been synthesized through sol-gel auto combustion route. Structural parameters are studied by powder X-ray diffraction at the diffraction angle range of 10-80°; and FT-IR spectroscopy in the wavenumber range of 1600-400 cm-1. Lattice parameters were calculated from the (hkl) values of the diffraction planes and interplanar spacing and found to be in the range of 8.3659-8.4197 Å. The surface morphology and crystalline nature are studied using scanning electron microscopy and also using HRTEM. The magnetic properties are analyzed through vibrating sample magnetometer. High saturation magnetization of 90.12 emu/g has been achieved from Co-Zn sample whereas high coercive force of 883.45 Oe is achieved in Co-Ni sample. A two-probe DC resistivity was measured in temperature ranges of 300-450 K.

Phase equilibria in the iron oxide-cobalt oxide-phosphorus oxide system

NASA Technical Reports Server (NTRS)

De Guire, Mark R.; Prasanna, T. R. S.; Kalonji, Gretchen; O'Handley, Robert C.

1987-01-01

Two novel ternary compounds are noted in the present study of 1000 C solid-state equilibria in the Fe-Co-P-O system's Fe2O3-FePO4-Co3(Po4)2-CoO region: CoFe(PO4)O, which undergoes incongruent melting at 1130 C, and Co3Fe4(PO4)6, whose incongruent melting occurs at 1080 C. The liquidus behavior-related consequences of rapidly solidified cobalt ferrite formation from cobalt ferrite-phosphate melts are discussed with a view to spinel formation. It is suggested that quenching from within the spinel-plus-liquid region may furnish an alternative to quenching a homogeneous melt.

Optical emission spectroscopy as a tool for the biodistribution investigation of cobalt-ferrite nanoparticles in mice

NASA Astrophysics Data System (ADS)

Kückelhaus, S.; Tedesco, A. C.; Oliveira, D. M.; Morais, P. C.; Boaventura, G. R.; Lacava, Z. G. M.

2005-05-01

This study reports on the biodistribution investigation of two magnetic samples both based on cobalt-ferrite nanoparticles, a magnetic fluid sample (CoMF) and a stealth magnetoliposome polyethylene glycol-monolaurate (PEG-ML). Morphology observations and iron and cobalt concentrations were evaluated after treatment of mice upon intravenous injection. Both magnetic samples had an extended distribution throughout all investigated organs. CoMF was quickly eliminated mainly by the fecal via whereas PEG-ML was retained longer in the circulation and slowly eliminated. These differences are probably due to the presence of polyethylene glycol on the PEG-ML surface, recognized to be responsible for the internalization delay of nanoparticles.

Mössbauer and magnetic properties of coherently mixed magnetite-cobalt ferrite grown by infrared pulsed-laser deposition

DOE PAGES

de la Figuera, Juan; Quesada, Adrian; Martín-García, Laura; ...

2016-01-13

We have studied the magnetic properties and the composition of cobalt ferrite single crystal films on SrTiO 3: Nb grown by infrared pulsed-laser deposition. Mössbauer spectra have been recorded from both the target used to grow the films and the films themselves. The Mössbauer spectra of the target taken at low temperatures show a strong dependence of the recoil free fraction of the octahedral sites with temperature. The films composition, with a coexistence of Co-enriched cobalt ferrite and magnetite, has been estimated assuming a similar ratio of the recoil free fractions of the films. X-ray absorption and x-ray magnetic circularmore » dichroism measurements confirm the valence composition of the film and show ferromagnetic Fe-Co coupling in the films with a coercive field around 0.5 T at room temperature. The combination of these characterization techniques allows establishin g the coherent structural and magnetic properties of this biphase system.« less

Applications of cobalt ferrite nanoparticles in biomedical nanotechnology.

PubMed

Srinivasan, Sumithra Y; Paknikar, Kishore M; Bodas, Dhananjay; Gajbhiye, Virendra

2018-05-01

Magnetic nanoparticles (MNPs) are very attractive especially for biomedical applications, among which, iron oxide nanoparticles have received substantial attention in the past decade due to the elemental composition that makes them biocompatible and degradable. However recently, other magnetic nanomaterials such as spinel ferrites that can provide improved magnetic properties such as coercivity and anisotropy without compromising on inherent advantages of iron oxide nanoparticles are being researched for better applicability of MNPs. Among various spinel ferrites, cobalt ferrite (CoFe 2 O 4 ) nanoparticles (NPs) are one of the most explored MNPs. Therefore, the intention of this article is to provide a comprehensive review of CoFe 2 O 4 NPs and their inherent properties that make them exceptional candidates, different synthesis methods that influence their properties, and applications of CoFe 2 O 4 NPs and their relevant applications that have been considered in biotechnology and bioengineering.

Microwave absorbance properties of zirconium–manganese substituted cobalt nanoferrite as electromagnetic (EM) wave absorbers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Khan, Kishwar, E-mail: kknano@hotmail.com; Rehman, Sarish

2014-02-01

Highlights: • Good candidates for EM materials with low reflectivity. • Good candidates for broad bandwidth at microwave frequency. • Microwave absorbing bandwidth was modulated simply by manipulating the Zr–Mn. • Higher the Zr–Mn content, the higher absorption rates for the electromagnetic radiation. • The predicted reflection loss shows that this can be used for thin ferrite absorber. - Abstract: Nanocrystalline Zr–Mn (x) substituted Co ferrite having chemical formula CoFe{sub 2−2x}Zr{sub x}Mn{sub x}O{sub 4} (x = 0.1–0.4) was prepared by co-precipitation technique. Combining properties such as structural, electrical, magnetic and reflection loss characteristics. Crystal structure and surface morphology of themore » calcined samples were characterized by X-ray diffraction analysis (XRD) and scanning electron microscopy (SEM). By using two point probe homemade resistivity apparatus to find resistivity of the sample. Electromagnetic (EM) properties are measured through RF impedance/materials analyzer over 1 MHz–3 GHz. The room-temperature dielectric measurements show dispersion behavior with increasing frequency from 100 Hz to 3 MHz. Magnetic properties confirmed relatively strong dependence of saturation magnetization on Zr–Mn composition. Curie temperature is also found to decrease linearly with addition of Zr–Mn. Furthermore, comprehensive analysis of microwave reflection loss (RL) is carried out as a function of substitution, frequency, and thickness. Composition accompanying maximum microwave absorption is suggested.« less

Synthesis of Trimagnetic Multishell MnFe2 O4 @CoFe2 O4 @NiFe2 O4 Nanoparticles.

PubMed

Gavrilov-Isaac, Véronica; Neveu, Sophie; Dupuis, Vincent; Taverna, Dario; Gloter, Alexandre; Cabuil, Valérie

2015-06-10

The synthesis and characterization of original ferrite multishell magnetic nanoparticles made of a soft core (manganese ferrite) covered with two successive shells, a hard one (cobalt ferrite) and then a soft one (nickel ferrite), are described. The results demonstrate the modulation of the coercivity when new magnetic shells are added. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Microstructural, dielectric and magnetic properties of multiferroic composite system barium strontium titanate – nickel cobalt ferrite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pahuja, Poonam, E-mail: poonampahuja123@gmail.com; Tandon, R. P., E-mail: ram-tandon@hotmail.com

2015-05-15

Multiferroic composites (1-x) Ba{sub 0.95}Sr{sub 0.05}TiO{sub 3} + (x) Ni{sub 0.8}Co{sub 0.2}Fe{sub 2}O{sub 4} (where x = 0.1, 0.2, 0.3, 0.4) has been prepared by solid state reaction method. X-ray diffraction analysis of the composite samples confirmed the presence of both barium strontium titanate (BST) and nickel cobalt ferrite (NCF) phases. FESEM images indicated the well dispersion of NCF grains among BST grains. Dielectric constant and loss of the composite samples decreases with increase in frequency following Maxwell-Wagner relaxation mechanism. Composite sample with highest ferrite content possesses highest values of remanent and saturation magnetization.

Exchange spring behaviour in SrFe{sub 12}O{sub 19}-CoFe{sub 2}O{sub 4} nanocomposites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Roy, Debangsu, E-mail: debangsu.phy@gmail.com; Anil Kumar, P. S.

2015-07-15

Nanocomposites of hard (SrFe{sub 12}O{sub 19}) and soft ferrite (CoFe{sub 2}O{sub 4}) are prepared by mixing individual ferrite components at appropriate weight ratio and subsequent heat treatment. The magnetization of the composites showed hysteresis loop that is characteristic of the exchange spring system. The variation of J{sub r}/J{sub r}(∞) vs. J{sub d}/ J{sub r}(∞) for these nanocomposites are investigated to understand the presence of both the interacting field and the disorder in the system. This is further corroborated with the First Order Reversal Curve analysis (FORC) on the nanocomposites of 1:4 (Cobalt Ferrite: Strontium Ferrite) and 1:16 (Cobalt Ferrite: Strontiummore » Ferrite). The FORC distribution reveals that the pinning mechanism is stronger in the nanocomposite of 1:4 compared to 1:16. However, the nanocomposite of 1:16 exhibit superior exchange coupling strength in contrast to 1:4. The asymmetric nature of the FORC distribution at H{sub c} = 0 Oe for both the nanocomposites validates the intercoupling between the reversible and irreversible magnetization.« less

Preparation, characterization and catalytic application of CoFe2O4 nanoparticles in the synthesis of benzimidazoles

NASA Astrophysics Data System (ADS)

Borade, Ravikumar M.; Shinde, Pavan R.; Kale, Swati B.; Pawar, Rajendra P.

2018-05-01

A highly efficient magnetically recoverable cobalt ferrite nano-catalyst was prepared by sol-gel autocombustion method using glycine as green fuel. The prepared material has been characterized by X-ray powder diffraction and scanning. An investigation of its catalytic activity showed it to be a heterogeneous Lewis acid catalyst for the synthesis of substituted benzimidazoles. The aqueous ethanol used as green solvent for the reaction. The nm size range of these particles facilitates the catalysis process, as an increased surface area available for the reaction. The easy separation of the catalyst by an external magnet and their recovery and reuse in next cycle reaction are additional benefits.

Investigation of Microwave Monolithic Integrated Circuit (MMIC) Non-Reciprocal Millimeterwave Components

DTIC Science & Technology

1991-09-01

nickel zinc ferrite films and (2) sputtering of barium hexaferrites with C-axis oriented normally to the film plane. The SSP tech- nique potential for...M-Wave, Components, Ferrites, Films , Yig, Nickel, Zinc , Hexagonal, R96E Measurements, Frequency, Magnetic, Barium Ferrite 17. SECURITY CLASSIFICATION...techniques to integrate millimeter-wave ferrite devices with GaAs VI&Cs. APPROACH Our approach was to deposit ferrite thin films on GaAs sub- strates in a

Structural, dielectric and gas sensing behavior of Mn substituted spinel MFe2O4 (M=Zn, Cu, Ni, and Co) ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Ranjith Kumar, E.; Siva Prasada Reddy, P.; Sarala Devi, G.; Sathiyaraj, S.

2016-01-01

Spinel ferrite (MnZnFe2O4, MnCuFe2O4, MnNiFe2O4 and MnCoFe2O4) nanoparticles have been prepared by evaporation method. The annealing temperature plays an important role on changing particle size of the spinel ferrite nanoparticles was found out by X-ray diffraction and transmission electron microscopy. The role of manganese substitution in the spinel ferrite nanoparticles were also analyzed for different annealing temperature. The substitution of Mn also creates a vital change in dielectric properties have been measured in the frequency range of 100 kHz to 5 MHz. These spinel ferrites are decomposed to α-Fe2O3 after annealing above 550 °C in air. Through the characterization of the prepared powder, the effect of annealing temperature, chemical composition and preparation technique on the microstructure, particle size and dielectric properties of the Mn substituted spinel ferrite nanoparticles are discussed. Furthermore, Conductance response of Mn substituted MFe2O4 ferrite nanoparticles were measured by exposing the materials to reducing gas like liquefied petroleum gas (LPG).

Nickel hydroxide/cobalt-ferrite magnetic nanocatalyst for alcohol oxidation.

PubMed

Bhat, Pooja B; Inam, Fawad; Bhat, Badekai Ramachandra

2014-08-11

A magnetically separable, active nickel hydroxide (Brønsted base) coated nanocobalt ferrite catalyst has been developed for oxidation of alcohols. High surface area was achieved by tuning the particle size with surfactant. The surface area of 120.94 m2 g(-1) has been achieved for the coated nanocobalt ferrite. Improved catalytic activity and selectivity were obtained by synergistic effect of transition metal hydroxide (basic hydroxide) on nanocobalt ferrite. The nanocatalyst oxidizes primary and secondary alcohols efficiently (87%) to corresponding carbonyls in good yields.

Epitaxial integration of CoFe2O4 thin films on Si (001) surfaces using TiN buffer layers

NASA Astrophysics Data System (ADS)

Prieto, Pilar; Marco, José F.; Prieto, José E.; Ruiz-Gomez, Sandra; Perez, Lucas; del Real, Rafael P.; Vázquez, Manuel; de la Figuera, Juan

2018-04-01

Epitaxial cobalt ferrite thin films with strong in-plane magnetic anisotropy have been grown on Si (001) substrates using a TiN buffer layer. The epitaxial films have been grown by ion beam sputtering using either metallic, CoFe2, or ceramic, CoFe2O4, targets. X-ray diffraction (XRD) and Rutherford spectrometry (RBS) in random and channeling configuration have been used to determine the epitaxial relationship CoFe2O4 [100]/TiN [100]/Si [100]. Mössbauer spectroscopy, in combination with XRD and RBS, has been used to determine the composition and structure of the cobalt ferrite thin films. The TiN buffer layer induces a compressive strain in the cobalt ferrite thin films giving rise to an in-plane magnetic anisotropy. The degree of in-plane anisotropy depends on the lattice mismatch between CoFe2O4 and TiN, which is larger for CoFe2O4 thin films grown on the reactive sputtering process with ceramic targets.

Synthesis and study of structural, microstructural and dielectric properties of Ce3+ doped Co-Ni ferrites for automotive applications

NASA Astrophysics Data System (ADS)

Srinivasamurthy, K. M.; Angadi, V. Jagadeesha; Kumar, P. Mohan; Nagaraj, B. S.; Deepthy, P. R.; Pasha, U. Mahaboob; Rudraswamy, B.

2018-05-01

Nano crystalline spinel ferrites of Co0.5Ni0.5CexFe2-xO4 (x=0.01, 0.015, 0.02, 0.025 and 0.03) was prepared by modified solution combustion method using a mixture of fuels for the first time. The influence of rare earth Ce3+ substitution at the Fe3+ site on the structural, microstructural and dielectric properties of Co0.5Ni0.5CexFe2-xO4 was investigated. The X-ray diffraction (XRD) studies confirmed the formation of monophasic nano crystalline samples without any secondary phases. The crystallite size decreases and density increases with the increases of Ce3+ contents. Surface morphology was studied through Scanning Electron Microscopy (SEM). Dielectric properties of these ferrites have been studied at room temperature using impedance analyzer in the frequency range up to 20 MHz. The effect of frequency and composition on dielectric constant (ɛ'), dielectric loss (tanδ) and ac conductivity (σac) have been discussed in terms of hopping of charge carriers (Fe2+↔Fe3+). The decrease in dielectric loss with frequency follows Debye's relaxation phenomena. Both the variation in tan loss and dielectric loss with frequency shows a similar. AC conductivity increases with the increases of frequency which directly proportional to concentration of Ce3+ ions follows Jonscher law. These Cerium doped Cobalt-nickel ferrites are very helpful for automotive applications.

Investigation on gas sensing properties of Ag doped BiFeO3

NASA Astrophysics Data System (ADS)

Bagwaiya, Toshi; Khade, Poonam; Reshi, Hilal Ahmad; Bhattacharya, Shovit; Shelke, Vilas; Kaur, Manmeet; Debnath, A. K.; Muthe, K. P.; Gadkari, S. C.

2018-04-01

Bismuth ferrite (BFO) and Ag substituted Bismuth ferrite with perovskite structure have been synthesized using sol-gel method and investigated for their gas sensing properties. Single phase and rhombohedral crystal structure of the samples were confirmed from XRD pattern. Oxidation state of the elements is confirmed using X-Ray Photoelectron Spectroscopy (XPS). Since Ag substituted Bismuth ferrite exhibited pronounced response to H2S gas as compared to other gases, H2S gas sensing properties of Bismuth ferrite (BFO) and Ag substituted Bismuth ferrite were investigated in detail. Bi0.9Ag0.1FeO3 (BAFO) exhibits enhanced sensitivity, quick response and selectivity towards H2S as compared to BFO.

Evaluation of structural, morphological and magnetic properties of CuZnNi (CuxZn0.5-xNi0.5Fe2O4) nanocrystalline ferrites for core, switching and MLCI's applications

NASA Astrophysics Data System (ADS)

Akhtar, Majid Niaz; Khan, Muhammad Azhar; Ahmad, Mukhtar; Nazir, M. S.; Imran, M.; Ali, A.; Sattar, A.; Murtaza, G.

2017-01-01

The influence of Cu substitution on the structural and morphological characteristics of Ni-Zn nanocrystalline ferrites have been discussed in this work. The detailed and systematic magnetic characterizations were also done for Cu substituted Ni-Zn nanoferrites. The nanocrystalline ferrites of Cu substituted CuxZn0.5-xNi0.5Fe2O4 ferrites (x=0, 0.1, 0.2, 0.3, 0.4 and 0.5) were synthesized using sol gel self-combustion hybrid method. X-ray diffraction (XRD), Field emission scanning electron microscopy (FESEM), Transmission electron microscope (TEM) and Vibrating sample magnetometer (VSM) were used to investigate the properties of Cu substituted nanocrystalline ferrites. Single phase structure of Cu substituted in Ni-Zn nanocrystalline ferrites were investigated for all the samples. Crystallite size, lattice constant and volume of the cell were found to increase by increasing Cu contents in spinel structure. The better morphology with well-organized nanocrystals of Cu-Zn-Ni ferrites at x=0 and 0.5 were observed from both FESEM and TEM analysis. The average grain size was 35-46 nm for all prepared nanocrystalline samples. Magnetic properties such as coercivity, saturation, remanence, magnetic squareness, magneto crystalline anisotropy constant (K) and Bohr magneton were measured from the recorded M-H loops. The magnetic saturation and remanence were increased by the incorporation of Cu contents. However, coercivity follow the Stoner-Wolforth model except for x=0.3 which may be due to the site occupancy and replacement of Cu contents from octahedral site. The squareness ratio confirmed the super paramgnetic behaviour of the Cu substituted in Ni-Zn nanocrystalline ferrites. Furthermore, Cu substituted Ni-Zn nanocrystalline ferrites may be suitable for many industrial and domestic applications such as components of transformers, core, switching, and MLCI's due to variety of the soft magnetic characteristics.

Grain size effect on activation energy in spinel CoFe{sub 2}O{sub 4} ceramic

DOE Office of Scientific and Technical Information (OSTI.GOV)

Supriya, Sweety, E-mail: sweety@iitp.ac.in; Kumar, Sunil; Kar, Manoranjan

2016-05-23

Cobalt ferrite of different average crystallites (from nanocrystallite to micro crystallites) has been prepared by the Sol-Gel Method. The X-ray diffraction (XRD) analysis confirms the cubic spinel phase with no trace of impurity phases. The effect of annealing temperature on micro structure and electric transport properties as a function of frequency and temperature has been studied. It is observed that the electric impedance and conductivity are strongly dependent on grain size. The impedance spectroscopic study is employed to understand the electrical transport properties of cobalt ferrite.

Structural analysis of aluminium substituted nickel ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Singh, H. S.; Sangwa, Neha

2018-05-01

Aluminium substituted nickel ferrite nanoparticles were synthesized by High Energy Ball milling (HEBM) of the mixture of α-NiO, α-Al2O3 and α-Fe2O3 followed by annealing at 1000˚C. X-ray diffraction (XRD) and Energy dispersive spectroscopy analysis (EDS) characterization was done for Aluminium substituted nickel ferrite. The structural analysis reveals the formation of the single phase compound. The average grain size was estimated by X-ray diffraction technique ranges from 30 to 10 nm with the increasing concentration of Aluminium. EDS spectra conforms the homogeneous mixing and purity of ferrite.

Synthesis of surfactant-coated cobalt ferrite nanoparticles for adsorptive removal of acid blue 45 dye

NASA Astrophysics Data System (ADS)

Waheed Mushtaq, Muhammad; Kanwal, Farah; Imran, Muhammad; Ameen, Naila; Batool, Madeeha; Batool, Aisha; Bashir, Shahid; Mustansar Abbas, Syed; Rehman, Ata ur; Riaz, Saira; Naseem, Shahzad; Ullah, Zaka

2018-03-01

Cobalt ferrite (CoFe2O4) nanoparticles (NPs) are synthesized by wet chemical coprecipitation method using metal chlorides as precursors and potassium hydroxide (KOH) as a precipitant. The tergitol-1x (T-1x) and didecyldimethyl ammonium bromide (DDAB) are used as capping agents and their effect is investigated on particle size, size distribution and morphology of cobalt ferrite nanoparticles (CFNPs). The Fourier transform infrared spectroscopy confirms the synthesis of CFNPs and formation of metal-oxygen (M-O) bond. The spinel phase structure, morphology, polydispersity and magnetic properties of ferrite nanoparticles are investigated by x-ray diffraction, scanning electron microscopy, dynamic light scattering and vibrating sample magnetometry analyses, respectively. The addition of capping agents effects the secondary growth of CFNPs and reduces their particle size, as is investigated by dynamic light scattering and atomic force microscopy. The results evidence that the DDAB is more promising surfactant to control the particle size (∼13 nm), polydispersity and aggregation of CFNPs. The synthesized CFNPs, CFNPs/T-1x and CFNPs/DDAB are used to study their adsorption potential for removal of acid blue 45 dye, and a maximum adsorptive removal of 92.25% is recorded by 0.1 g of CFNPs/DDAB at pH 2.5 and temperature 20 ± 1 °C. The results show that the dye is physically adsorbed by magnetic NPs and follows the Langmuir isotherm model.

Enhanced magneto-optical and photo-catalytic properties of transition metal cobalt (Co2+ ions) doped spinel MgFe2O4 ferrite nanocomposites

NASA Astrophysics Data System (ADS)

Abraham, A. Godlyn; Manikandan, A.; Manikandan, E.; Vadivel, S.; Jaganathan, S. K.; Baykal, A.; Renganathan, P. Sri

2018-04-01

In this study, spinel magnesium cobalt ferrite (CoxMg1-xFe2O4: x = 0.0, 0.2, 0.4, 0.6, 0.8 and 1.0) nanocomposites were synthesized successfully by modified sol-gel combustion method. Magnesium nitrate, cobalt nitrate and iron nitrate were used as the source of divalent (Mg2+ and Co2+) and trivalent (Fe3+) cations, respectively and urea were used as the reducing (fuel) agent. The effects of cobalt ions on morphology, structural, optical, magnetic and photo-catalytic properties of spinel CoxMg1-xFe2O4 nanocomposites were investigated. Various characterization methods, including X-ray powder diffraction (XRD), high resolution scanning electron microscope (HR-SEM), transmission electron microscopy (HR-TEM), energy-dispersive X-ray spectroscopy (EDX), Fourier transforms infrared (FT-IR) spectroscopy, vibrating sample magnetometer (VSM) and photo-catalytic degradation (PCD) activity were used to study the phase purity, microstructure, particle size, elemental composition, functional group determination, band gap calculation, magnetic properties and degradation efficiency of nanoparticles, respectively. The observed results showed that the final products consists cubic spinel phase with sphere-like nanoparticles morphologies. Furthermore, spinel Co0.6Mg0.4Fe2O4 nanocomposite showed highest PCD efficiency (98.55%) than other composition of ferrite nanoparticles.

Synthesis of cobalt ferrite nanoparticles from thermolysis of prospective metal-nitrosonaphthol complexes and their photochemical application in removing methylene blue

NASA Astrophysics Data System (ADS)

Tavana, Jalal; Edrisi, Mohammad

2016-03-01

In this study, cobalt ferrite (CoFe2O4) nanoparticles were synthesized by two novel methods. The first method is based on the thermolysis of metal-NN complexes. In the second method, a template free sonochemical treatment of mixed cobalt and iron chelates of α-nitroso-β-naphthol (NN) was applied. Products prepared through method 1 were spherical, with high specific surface area (54.39 m2 g-1) and small average crystalline size of 13 nm. However, CoFe2O4 nanoparticles prepared by method 2 were in random shapes, a broad range of crystalline sizes and a low specific surface area of 25.46 m2 g-1 though highly pure. A Taguchi experimental design was implemented in method 1 to determine and obtain the optimum catalyst. The structural and morphological properties of products were investigated by x-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy, Fourier transform infrared, Brunauer-Emmett-Teller and dynamic laser light scattering. The crystalline size calculations were performed using Williamson-Hall method on XRD spectrum. The photocatalytic activity of the optimum nanocrystalline cobalt ferrite was investigated for degradation of a representative pollutant, methylene blue (MB), and visible light as energy source. The results showed that some 92% degradation of MB could be achieved for 7 h of visible light irradiation.

The role of annealing temperature and bio template (egg white) on the structural, morphological and magnetic properties of manganese substituted MFe2O4 (M=Zn, Cu, Ni, Co) nanoparticles

NASA Astrophysics Data System (ADS)

Ranjith Kumar, E.; Jayaprakash, R.; Kumar, Sanjay

2014-02-01

Manganese substituted ferrites (ZnFe2O4, CuFe2O4, NiFe2O4 and CoFe2O4) have been prepared in the bio template medium by using a simple evaporation method. The annealing temperature plays an important position on changing particle size and morphology of the mixed ferrite nanoparticles were found out by X-ray diffraction, transmission electron microscopy and scanning electron microscopy methods. The role of manganese substitution in the mixed ferrite nanoparticles were also analyzed for different annealing temperature. The substitution of Mn also creates a vital change in magnetic properties which is studied by using vibrating sample magnetometer (VSM). These spinel ferrites are decomposed to α-Fe2O3 after annealing above 550 °C in air. However, α-Fe2O3 phase was slowly vanished after ferrites annealing above 900 °C. The effect of this secondary phase on the structural change and magnetic properties of the mixed ferrite nanoparticles is discussed.

Ga and In modified ceria as supports for cobalt-catalyzed Fischer-Tropsch synthesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gnanamani, Muthu Kumaran; Jacobs, Gary; Shafer, Wilson D.

Ga- and In-modified ceria (Ce 0.8Ga 0.2O 2, Ce 0.8In 0.2O 2) materials were used as supports for cobalt-catalyzed Fischer-Tropsch synthesis (FTS). The addition of Ga to ceria was found to improve CO conversion for cobalt-catalyzed FTS, while the addition of In tended to decrease it. A similar trend was observed with the Ag-promoted cobalt/ceria catalysts. Doping of ceria with Ga or In decreased methane and increased the selectivity to olefins and alcohols for Ag-promoted cobalt/ceria. The sum of the products of olefins and alcohols for various catalysts exhibited a decreasing trend as follows: Ag-Co/Ce-Ga > Ag-Co/Ce-In > Ag-Co/Ce. Resultsmore » of H 2-TPR-XANES showed that adding of Ga or In to ceria increases the fraction of Ce 3+ in the surface shell for both unpromoted and Ag-promoted catalysts in the range of temperature typical of catalyst activation. In conclusion, this partially reduced ceria plays an important role in controlling the product selectivity of cobalt-catalyzed FT synthesis.« less

Ga and In modified ceria as supports for cobalt-catalyzed Fischer-Tropsch synthesis

DOE PAGES

Gnanamani, Muthu Kumaran; Jacobs, Gary; Shafer, Wilson D.; ...

2017-08-24

Ga- and In-modified ceria (Ce 0.8Ga 0.2O 2, Ce 0.8In 0.2O 2) materials were used as supports for cobalt-catalyzed Fischer-Tropsch synthesis (FTS). The addition of Ga to ceria was found to improve CO conversion for cobalt-catalyzed FTS, while the addition of In tended to decrease it. A similar trend was observed with the Ag-promoted cobalt/ceria catalysts. Doping of ceria with Ga or In decreased methane and increased the selectivity to olefins and alcohols for Ag-promoted cobalt/ceria. The sum of the products of olefins and alcohols for various catalysts exhibited a decreasing trend as follows: Ag-Co/Ce-Ga > Ag-Co/Ce-In > Ag-Co/Ce. Resultsmore » of H 2-TPR-XANES showed that adding of Ga or In to ceria increases the fraction of Ce 3+ in the surface shell for both unpromoted and Ag-promoted catalysts in the range of temperature typical of catalyst activation. In conclusion, this partially reduced ceria plays an important role in controlling the product selectivity of cobalt-catalyzed FT synthesis.« less

The influence of Ga doping on structural magnetic and dielectric properties of NiCr0.2Fe1.8O4 spinel ferrite

NASA Astrophysics Data System (ADS)

Ajmal, Muhammad; Islam, M. U.; Ashraf, Ghulam Abbas; Nazir, Muhammad Aamir; Ghouri, M. I.

2017-12-01

A series of spinel ferrites NiCr0.2GaxFe1.8-xO4 (x=0.00, 0.002, 0.04, 0.06, 0.08) was prepared by co precipitation technique. The influence of rare earth element Ga ions the structural dielectric and magnetic properties of NiCr0.2Fe1.8O4 ferrites was investigated. The X-ray diffraction confirmed the phase precipitated out was pure spinel phase with few traces of secondary phases. The crystallite size decreases and density increases with the increases of Ga contents. The magnetic moment, saturation magnetization and remanent magnetization increased with addition of Ga ions in spinel ferrite. The dielectric constant is described that it decreases more suddenly at low frequencies as compare at higher frequencies. The decrease in dielectric loss with frequency follows Deby's relaxation phenomena. Both the variation in tan loss and dielectric loss with frequency shows a similar. AC conductivity increases with the increases of frequency which inversely proportional to concentration of Ga3+ ions follows Jonscher law. These Gallium Chromium doped nickel ferrites are very helpful for high frequency switching devices.

Synthesis of cobalt doped BiFeO3 multiferroic thin films on p-Si substrate by sol-gel method

NASA Astrophysics Data System (ADS)

Prasannakumara, R.; Shrisha, B. V.; Naik, K. Gopalakrishna

2018-05-01

Bismuth ferrite (BiFeO3) and cobalt doped BiFeO3 (BiFe1-xCoxO3) nanostructure thin films were grown on p-silicon substrates by sol-gel spin coating method with a sequence of coating and annealing process. The post-annealing of the grown films was carried out under high pure argon atmosphere. The grown nanostructure thin films were characterized using XRD, FESEM, and AFM for the structural, morphological and topological studies, respectively. The elemental compositions of the samples were studied by EDX spectra. The PL spectra of the grown sample shows a narrow emission peak around 559 nm which corresponds to the energy band gap of BFO thin films. The XRD peaks of the BiFeO3 nanostructure thin film reveals the rhombohedral structure and transformed from rhombohedral to orthorhombic or tetragonal structure in Co doped BiFeO3 thin films. The Co substitution in BiFeO3 helped to obtain higher dense nanostructure thin films with smaller grain size than the BiFeO3 thin films.

Deposition of Lanthanum Strontium Cobalt Ferrite (LSCF) Using Suspension Plasma Spraying for Oxygen Transport Membrane Applications

NASA Astrophysics Data System (ADS)

Fan, E. S. C.; Kesler, O.

2015-08-01

Suspension plasma spray deposition was utilized to fabricate dense lanthanum strontium cobalt ferrite oxygen separation membranes (OSMs) on porous metal substrates for mechanical support. The as-sprayed membranes had negligible and/or reversible material decomposition. At the longer stand-off distance (80 mm), smooth and dense membranes could be manufactured using a plasma with power below approximately 81 kW. Moreover, a membrane of 55 μm was observed to have very low gas leakage rates desirable for OSM applications. This thickness could potentially be decreased further to improve oxygen diffusion by using metal substrates with finer surface pores.

Structural and Mössbauer analysis of pure and Ce-Dy doped cobalt ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Hashim, Mohd.; Meena, Sher Singh; Kumar, Shalendra; Ahmed, Ateeq; Bhatt, Pramod

2018-05-01

Ce and Dy doped Cobalt ferrites with the chemical composition CoCexDyxFe2-2xO4 (x = 0.00 and 0.04) were synthesized via the chemical route using citrate-gel auto-combustion method. The structural analysis has been carried out with the help of x-ray diffraction (XRD). Formation of spinel cubic structure of the ferrites was confirmed by XRD analysis. Mössbauer spectra were recorded for both samples at room temperature. Presence of the well resolved sextet spectra corresponding to A and B sub-lattice clearly shows that both the samples have ferrimagnetic ordering at room temperature. Isomer shift observed from fitting of the Mössbauer spectra infers that Fe3+ ions are in high valence state. The decrease in the hyperfine field due to the doping of Ce and Dy clearly showed that magnetic interactions diluted due to the doping of Ce and Dy ions.

Comparison of drug delivery potentials of surface functionalized cobalt and zinc ferrite nanohybrids for curcumin in to MCF-7 breast cancer cells

NASA Astrophysics Data System (ADS)

Sawant, V. J.; Bamane, S. R.; Shejwal, R. V.; Patil, S. B.

2016-11-01

The functionalization and surface engineering of CoFe2O4 and ZnFe2O4 nanoparticles were performed by coating with PEG and Chitosan respectively using simple wet co-precipitation. Then multiactive therapeutic drug curcumin was loaded to form drug delivery nanohybrids by precipitation. These nanohybrids were characterized separately using UV-vis, FTIR, PL spectroscopy, XRD, VSM, SEM and TEM analysis. The moderate antibacterial activities of the nanohybrids were elaborated by in vitro antibacterial screening on Escherichia coli and Staphylococcus aureus. The anticancer potentials, apoptotic effects and enhanced drug delivery properties of these nanohybrids were confirmed and compared on MCF-7 cells by in vitro MTT assay. The drug delivery activities for hydrophobic drug and anticancer effects of chitosan coated zinc ferrite functionalized nanoparticles were higher than PEG coated cobalt ferrite nanohybrids.

Synthesis, electrical and magnetic properties of sodium borosilicate glasses containing Co-ferrites nanoparticles

NASA Astrophysics Data System (ADS)

Othman, H. A.; Eltabey, M. M.; Ibrahim, Samia. E.; El-Deen, L. M. Sharaf; Elkholy, M. M.

2017-02-01

Co-ferrites nanoparticles that have been prepared by the co-precipitation method were added to sodium borosilicate (Na2O-B2O3-SiO2) glass matrix by the solid solution method and they were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), Fourier transform infrared (FTIR) and magnetization measurements. (XRD) revealed the formation of the Co-ferrite magnetic crystalline phase embedded in an amorphous matrix in all the samples. The investigated samples by (TEM) showed the formation of the cobalt ferrite nanoparticles with a spherical shape and highly monodispersed with an average size about 13 nm. IR data revealed that the BO3 and BO4 are the main structural units of these samples network. IR spectra of the investigated samples showed the characteristic vibration bands of Co-ferrite. Composition and frequency dependent dielectric properties of the prepared samples were measured at room temperature in the frequency range 100-100 kHz. The conductivity was found to increase with increasing cobalt ferrite content. The variations of conductivity and dielectric properties with frequency and composition were discussed. Magnetic hysteresis loops were traced at room temperature using VSM and values of saturation magnetization MS and coercive field HC were determined. The obtained results revealed that a ferrimagnetic behavior were observed and as Co-ferrite concentration increases the values of MS and HC increase from 2.84 to 8.79 (emu/g) and from 88.4 to 736.3 Oe, respectively.

Study of gamma ray energy absorption and exposure buildup factors for ferrites by geometric progression fitting method

NASA Astrophysics Data System (ADS)

Raut, S. D.; Awasarmol, V. V.; Shaikh, S. F.; Ghule, B. G.; Ekar, S. U.; Mane, R. S.; Pawar, P. P.

2018-04-01

The gamma ray energy absorption and exposure buildup factors (EABF and EBF) were calculated for ferrites such as cobalt ferrite (CoFe2O4), zinc ferrite (ZnFe2O4), nickel ferrite (NiFe2O4) and magnesium ferrite (MgFe2O4) using five parametric geometric progression (G-P fitting) formula in the energy range 0.015-15.00 MeV up to the penetration depth 40 mean free path (mfp). The obtained data of absorption and exposure buildup factors have been studied as a function of incident photon energy and penetration depth. The obtained EABF and EBF data are useful for radiation dosimetry and radiation therapy.

Magneto-optical waveguides made of cobalt ferrite nanoparticles embedded in silica/zirconia organic-inorganic matrix

NASA Astrophysics Data System (ADS)

Choueikani, Fadi; Royer, François; Jamon, Damien; Siblini, Ali; Rousseau, Jean Jacques; Neveu, Sophie; Charara, Jamal

2009-02-01

This paper describes a way to develop magneto-optical waveguides via sol-gel process. They are made of cobalt ferrite nanoparticles embedded in a silica/zirconia matrix. Thin films are coated on glass substrate using the dip-coating technique. Annealing and UV treatment are applied to finalize sample preparation. Therefore, planar waveguides combining magneto-optical properties with a low refractive index (≈1,5) are obtained. M-lines and free space ellipsometry measurements show a specific Faraday rotation of 250°/cm and a modal birefringence of 1×10-4 at 820 nm. Thus, the mode conversion efficiency can reach a maximum value around 56%.

Design and synthesis of ternary cobalt ferrite/graphene/polyaniline hierarchical nanocomposites for high-performance supercapacitors

NASA Astrophysics Data System (ADS)

Xiong, Pan; Huang, Huajie; Wang, Xin

2014-01-01

A ternary cobalt ferrite/graphene/polyaniline nanocomposite (CGP) is designed and fabricated via a facile two-step approach: cobalt ferrite nanoparticles dispersed on graphene sheets are achieved by a hydrothermal method, followed by coating with polyaniline (PANI) through in situ polymerization process. Electrochemical measurements demonstrate that the specific capacitance of the resulting ternary hybrid (CGP) is up to 1133.3 F g-1 at a scan rate of 1 mV s-1 and 767.7 F g-1 at a current density of 0.1 A g-1 using a three-electrode system, while 716.4 F g-1 at a scan rate of 1 mV s-1 and 392.3 F g-1 at a current density of 0.1 A g-1 using a two-electrode system, which are significantly higher than those of pure CoFe2O4, graphene and PANI, or binary CoFe2O4/graphene, CoFe2O4/PANI and graphene/PANI hybrids. In addition, over 96% of the initial capacitance can be retained after repeating test for 5000 cycles, demonstrating a high cycling stability. The extraordinary electrochemical performance of the ternary CGP nanocomposite can be attributed to its well-designed nanostructure and the synergistic effects of the individual components.

Bizarre dielectric anomalies in magnetoelectric composites of CoFe2O4 and BaTi0.9Zr0.1O3

NASA Astrophysics Data System (ADS)

Mathur, Shubhra; Srivastava, Subodh; Surve, Sachin; Wadhwani, Kiran; Singh Rajaura, Rajveer; Dolia, S. N.

2017-12-01

The magnetoelectric (ME) composites containing cobalt ferrite as the magnetic phase and Zr substituted (10 atomic % occupancy) barium titanate as the ferroelectric counterpart having the general formula (x) CoFe2O4  +  (1  -  x) BaTi0.9Zr0.1O3 (where x  =  0, 0.25, 0.50, 0.75 and 1) have been synthesised by the conventional solid state diffusion route. Powder x-ray diffraction of thus prepared materials confirms the presence of ferrite and ferroelectric phases and their concurrent existence in all three composites without showing traces of any superfluous phase. Dielectric measurements have been recorded as a function of frequency (ranging from 100 Hz to 1 MHz) at room temperature and temperature (from 325 K up to a maximum of 825 K). In composites, relative permittivity and loss tangent curves with variable temperature show upsurge of bizarre anomalies which can be associated to the defect modes existing in the form of oxygen ion vacancies rather than ascribing it to the benchmark ferro to paraeletric transition.

Tailoring the magnetic properties and magnetorheological behavior of spinel nanocrystalline cobalt ferrite by varying annealing temperature.

PubMed

Sedlacik, Michal; Pavlinek, Vladimir; Peer, Petra; Filip, Petr

2014-05-14

Magnetic nanoparticles of spinel nanocrystalline cobalt ferrite were synthesized via the sol-gel method and subsequent annealing. The influence of the annealing temperature on the structure, magnetic properties, and magnetorheological effect was investigated. The finite crystallite size of the particles, determined by X-ray diffraction and the particle size observed via transmission electron microscopy, increased with the annealing temperature. The magnetic properties observed via a vibrating sample magnetometer showed that an increase in the annealing temperature leads to the increase in the magnetization saturation and, in contrast, a decrease in the coercivity. The effect of annealing on the magnetic properties of ferrite particles has been explained by the recrystallization process at high temperatures. This resulted in grain size growth and a decrease in an imposed stress relating to defects in the crystal lattice structure of the nanoparticles. The magnetorheological characteristics of suspensions of ferrite particles in silicone oil were measured using a rotational rheometer equipped with a magnetic field generator in both steady shear and small-strain oscillatory regimes. The magnetorheological performance expressed as a relative increase in the magnetoviscosity appeared to be significantly higher for suspensions of particles annealed at 1000 °C.

Observation of longitudinal spin-Seebeck effect in cobalt-ferrite epitaxial thin films

NASA Astrophysics Data System (ADS)

Niizeki, Tomohiko; Kikkawa, Takashi; Uchida, Ken-ichi; Oka, Mineto; Suzuki, Kazuya Z.; Yanagihara, Hideto; Kita, Eiji; Saitoh, Eiji

2015-05-01

The longitudinal spin-Seebeck effect (LSSE) has been investigated in cobalt ferrite (CFO), an exceptionally hard magnetic spinel ferrite. A bilayer of a polycrystalline Pt and an epitaxially-strained CFO(110) exhibiting an in-plane uniaxial anisotropy was prepared by reactive rf sputtering technique. Thermally generated spin voltage in the CFO layer was measured via the inverse spin-Hall effect in the Pt layer. External-magnetic-field (H) dependence of the LSSE voltage (VLSSE) in the Pt/CFO(110) sample with H ∥ [001] was found to exhibit a hysteresis loop with a high squareness ratio and high coercivity, while that with H ∥ [ 1 1 ¯ 0 ] shows a nearly closed loop, reflecting the different anisotropies induced by the epitaxial strain. The magnitude of VLSSE has a linear relationship with the temperature difference (ΔT), giving the relatively large VLSSE /ΔT of about 3 μV/K for CFO(110) which was kept even at zero external field.

Influence of Bi(3+)-doping on the magnetic and Mössbauer properties of spinel cobalt ferrite.

PubMed

Gore, Shyam K; Mane, Rajaram S; Naushad, Mu; Jadhav, Santosh S; Zate, Manohar K; Alothman, Z A; Hui, Biz K N

2015-04-14

The influence of Bi(3+)-doping on the magnetic and Mössbauer properties of cobalt ferrite (CoFe2O4), wherein the Fe(3+) ions are replaced by the Bi(3+) ions to form CoBixFe2-xO4 ferrites, where x = 0.0, 0.05, 0.1, 0.15 or 0.2, has been investigated. The structural and morphological properties of undoped and doped ferrites, synthesized chemically through a self-igniting sol-gel method, are initially screened using X-ray diffraction, scanning electron microscopy and Fourier transform infrared spectroscopy measurements. The changes in magnetic moment of ions, their coupling with neighboring ions and cation exchange interactions are confirmed from the Mössbauer spectroscopy analysis. The effect of Bi(3+)-doping on the magnetic properties of CoFe2O4 ferrite is examined from the vibrating sample magnetometry spectra. Saturation magnetization and coercivity values are increased initially and then decreased, as result of Bi(3+)-doping. The obtained results with improved saturation magnetization (from 26.36 to 44.96 emu g(-1)), coercivity (from 1457 to 1863 Oe) and remanence magnetization (from 14.48 to 24.63 emu g(-1)) on 0.1-0.15 mol Bi(3+)-doping of CoBixFe2-xO4 demonstrate the usefulness for magnetic recording and memory devices.

Study of structural and magnetic properties of cobalt ferrite nanoparticles sintered at different temperature

NASA Astrophysics Data System (ADS)

Kumari, Mukesh; Bhatnagar, Mukesh Chander

2018-05-01

Cobalt ferrite (CFO) has been synthesized in the form of nanoparticles (NPs) through sol-gel auto-combustion method. The prepared NPs of CFO were sintered for four hours at various temperatures from 300°C to 900°C. The physical properties of the sintered samples have been optimized using X-ray diffraction (XRD), Raman spectroscopy and physical properties measurement system (PPMS). The XRD and Raman studies have confirmed the cubic spinel phase formation of CFO NPs. XRD results showed that as we increase the sintering temperature the crystallite size of particles increases. Whereas the magnetic studies revealed that the saturation magnetization (MS) increases while the coercivity (HC) of nanoparticles decreases with increase of sintering temperature.

Preparation and microwave absorbing properties of carbon/cobalt ferromagnetic composites.

PubMed

Li, Wangchang; Qiao, Xiaojing; Zhao, Hui; Wang, Shuman; Ren, Qingguo

2013-02-01

Carbon/cobalt ferromagnetic light composites with high performance of microwave absorbing properties were prepared by hydrothermal method using starch and hollow cobalt ferrites. It was concluded that after carbonization the spinel structure ferrites changed to Co3Fe7 alloys and the temperature of graphitization was significantly decreased for the catalytic of CoFe2O4/Co3Fe7. The increase of carbon content, and exist of CoFe2O4/Co3Fe7 heightened the microwave absorbing properties. Electromagnetic parameters were tested with 40% of the titled materials and 60% of paraffin wax composites by using HP8722ES vector network analyzer. The reflection was also simulated through transmission line theory. The microwave absorbers exhibited a maximum reflection loss -43 dB and the electromagnetic wave absorption less than -10 dB was found to exceed 3.0 GHz between 11.6 GHz and 15 GHz for an absorber thickness of 2 mm.

Exploring Reaction Conditions to Improve the Magnetic Response of Cobalt-Doped Ferrite Nanoparticles

PubMed Central

Galarreta, Itziar; Gil de Muro, Izaskun; Lezama, Luis

2018-01-01

With the aim of studying the influence of synthesis parameters in structural and magnetic properties of cobalt-doped magnetite nanoparticles, Fe3−xCoxO4 (0 < x < 0.15) samples were synthetized by thermal decomposition method at different reaction times (30–120 min). The Co ferrite nanoparticles are monodisperse with diameters between 6 and 11 nm and morphologies depending on reaction times, varying from spheric, cuboctahedral, to cubic. Chemical analysis and X-ray diffraction were used to confirm the composition, high crystallinity, and pure-phase structure. The investigation of the magnetic properties, both magnetization and electronic magnetic resonance, has led the conditions to improve the magnetic response of doped nanoparticles. Magnetization values of 86 emu·g−1 at room temperature (R.T.) have been obtained for the sample with the highest Co content and the highest reflux time. Magnetic characterization also displays a dependence of the magnetic anisotropy constant with the varying cobalt content. PMID:29370104

Properties of Ferrite Garnet (Bi, Lu, Y)3(Fe, Ga)5O12 Thin Film Materials Prepared by RF Magnetron Sputtering

PubMed Central

Nur-E-Alam, Mohammad; Belotelov, Vladimir; Alameh, Kamal

2018-01-01

This work is devoted to physical vapor deposition synthesis, and characterisation of bismuth and lutetium-substituted ferrite-garnet thin-film materials for magneto-optic (MO) applications. The properties of garnet thin films sputtered using a target of nominal composition type Bi0.9Lu1.85Y0.25Fe4.0Ga1O12 are studied. By measuring the optical transmission spectra at room temperature, the optical constants and the accurate film thicknesses can be evaluated using Swanepoel’s envelope method. The refractive index data are found to be matching very closely to these derived from Cauchy’s dispersion formula for the entire spectral range between 300 and 2500 nm. The optical absorption coefficient and the extinction coefficient data are studied for both the as-deposited and annealed garnet thin-film samples. A new approach is applied to accurately derive the optical constants data simultaneously with the physical layer thickness, using a combination approach employing custom-built spectrum-fitting software in conjunction with Swanepoel’s envelope method. MO properties, such as specific Faraday rotation, MO figure of merit and MO swing factor are also investigated for several annealed garnet-phase films. PMID:29789463

Dopant driven tunability of dielectric relaxation in MxCo(1-x)Fe2O4 (M: Zn2+, Mn2+, Ni2+) nano-ferrites

NASA Astrophysics Data System (ADS)

Datt, Gopal; Abhyankar, A. C.

2017-07-01

Nano-ferrites with tunable dielectric and magnetic properties are highly desirable in modern electronics industries. This work reports the effect of ferromagnetic (Ni), anti-ferromagnetic (Mn), and non-magnetic (Zn) substitution on cobalt-ferrites' dielectric and magnetic properties. The Rietveld analysis of XRD data and the Raman spectroscopic study reveals that all the samples are crystallized in the Fd-3m space group. The T2g Raman mode was observed to split into branches, which is due to the presence of different cations (with different vibrational frequencies) at crystallographic A and B-sites. The magnetization study shows that the MnCoFe2O4 sample has the highest saturation magnetization of 87 emu/g, which is attributed to the presence of Mn2+ cations at the B-site with a magnetic moment of 5 μB. The dielectric permittivity of these nanoparticles (NPs) obeys the modified Debye model, which is further supported by Cole-Cole plots. The dielectric constant of MnCoFe2O4 ferrite is found to be one order higher than that of the other two ferrites. The increased bond length of the Mn2+-O2- bond along with the enhanced d-d electron transition between Mn 2 +/Co 2 +⇋Fe 3 + cations at the B-site are found to be the main contributing factors for the enhanced dielectric constant of MnCoFe2O4 ferrite. We find evidence of variable-range hopping of localized polarons in these ferrite NPs. The activation energy, hopping range, and density of states N (" separators="|EF ), of these polarons were calculated using Motts' 1/4th law. The estimated activation energies of these polarons at 300 K were found to be 288 meV, 426 meV, and 410 meV, respectively, for the MnCoFe2O4, NiCoFe2O4, and ZnCoFe2O4 ferrite NPs, while the hopping range of these polarons were found to be 27.14 Å, 11.66 Å, and 8.17 Å, respectively. Observation of a low dielectric loss of ˜0.04, in the frequency range of 0.1-1 MHz, in these NPs makes them potential candidates for energy harvesting devices in the modern electronics industry.

Spindly cobalt ferrite nanocrystals: preparation, characterization and magnetic properties.

PubMed

Cao, Xuebo; Gu, Li

2005-02-01

In this paper we describe the preparation of homogeneously needle-shaped cobalt ferrite (CoFe(2)O(4)) nanocrystals on a large scale through the smooth decomposition of urea and the resulting co-precipitation of Co(2+) and Fe(3+) in oleic acid micelles. Furthermore, we found that other ferrite nanocrystals with a needle-like shape, such as zinc ferrite (ZnFe(2)O(4)) and nickel ferrite (NiFe(2)O(4)), can be prepared by the same process. Needle-shaped CoFe(2)O(4) nanocrystals dispersed in an aqueous solution containing oleic acid exhibit excellent stability and the formed colloid does not produce any precipitations after two months, which is of prime importance if these materials are applied in magnetic fluids. X-ray diffraction (XRD) measurements were used to characterize the phase and component of the co-precipitation products, and demonstrate that they are spinel ferrite with a cubic symmetry. Transmission electron microscopy (TEM) observation showed that all the nanocrystals present a needle-like shape with a 22 nm short axis and an aspect ratio of around 6. Varying the concentration of oleic acid did not bring about any obvious influence on the size distribution and shapes of CoFe(2)O(4). The magnetic properties of the needle-shaped CoFe(2)O(4) nanocrystals were evaluated by using a vibrating sample magnetometer (VSM), electron paramagnetic resonance (EPR), and a Mössbauer spectrometer, and the results all demonstrated that CoFe(2)O(4) nanocrystals were superparamagnetic at room temperature.

Preparation and Application of Hollow Silica/magnetic Nanocomposite Particle

NASA Astrophysics Data System (ADS)

Wang, Cheng-Chien; Lin, Jing-Mo; Lin, Chun-Rong; Wang, Sheng-Chang

The hollow silica/cobalt ferrite (CoFe2O4) magnetic microsphere with amino-groups were successfully prepared via several steps, including preparing the chelating copolymer microparticles as template by soap-free emulsion polymerization, manufacturing the hollow cobalt ferrite magnetic microsphere by in-situ chemical co-precipitation following calcinations, and surface modifying of the hollow magnetic microsphere by 3-aminopropyltrime- thoxysilane via the sol-gel method. The average diameter of polymer microspheres was ca. 200 nm from transmission electron microscope (TEM) measurement. The structure of the hollow magnetic microsphere was characterized by using TEM and scanning electron microscope (SEM). The spinel-type lattice of CoFe2O4 shell layer was identified by using XRD measurement. The diameter of CoFe2O4 crystalline grains ranged from 54.1 nm to 8.5 nm which was estimated by Scherrer's equation. Additionally, the hollow silica/cobalt ferrite microsphere possesses superparamagnetic property after VSM measurement. The result of BET measurement reveals the hollow magnetic microsphere which has large surface areas (123.4m2/g). After glutaraldehyde modified, the maximum value of BSA immobilization capacity of the hollow magnetic microsphere was 33.8 mg/g at pH 5.0 buffer solution. For microwave absorption, when the hollow magnetic microsphere was compounded within epoxy resin, the maximum reflection loss of epoxy resins could reach -35dB at 5.4 GHz with 1.9 mm thickness.

Magnetic Cobalt Ferrite Nanocrystals For an Energy Storage Concentration Cell.

PubMed

Dai, Qilin; Patel, Ketan; Donatelli, Greg; Ren, Shenqiang

2016-08-22

Energy-storage concentration cells are based on the concentration gradient of redox-active reactants; the increased entropy is transformed into electric energy as the concentration gradient reaches equilibrium between two half cells. A recyclable and flow-controlled magnetic electrolyte concentration cell is now presented. The hybrid inorganic-organic nanocrystal-based electrolyte, consisting of molecular redox-active ligands adsorbed on the surface of magnetic nanocrystals, leads to a magnetic-field-driven concentration gradient of redox molecules. The energy storage performance of concentration cells is dictated by magnetic characteristics of cobalt ferrite nanocrystal carriers. The enhanced conductivity and kinetics of redox-active electrolytes could further induce a sharp concentration gradient to improve the energy density and voltage switching of magnetic electrolyte concentration cells. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Impedance spectroscopy and electric modulus behavior of Molybdenum doped Cobalt-Zinc ferrite

NASA Astrophysics Data System (ADS)

Pradhan, A. K.; Nath, T. K.; Saha, S.

2017-07-01

The complex impedance spectroscopy and the electric modulus of Mo doped Cobalt-Zinc inverse spinel ferrite has been investigated in detail. The conventional ceramic technique has been used to prepare the CZMO. The HRXRD technique has been used to study the structural analysis which confirms the inverse spinel structure of the material and also suggest the material have Fd3m space group. The complex impedance spectroscopic data and the electric modulus formalism have been used to understand the dielectric relaxation and conduction process. The contribution of grain and grain boundary in the electrical conduction process of CZMO has been confirmed from the Cole-Cole plot. The activation energy is calculated from both the IS (Impedance Spectroscopy) and electric modulus formalism and found to be nearly same for the materials.

Annealing pressure induced ions transfer in Cobalt-Ferrite thin films on amorphous SiO2/Si substrates

NASA Astrophysics Data System (ADS)

Huang, Shun-Yu; Chong, Cheong-Wei; Chen, Pin-Hui; Li, Hong-Lin; Li, Min-Kai; Huang, J. C. Andrew

2017-11-01

In this work, Cobalt-Ferrite (CFO) films were grown on silicon substrates with 300 nm amorphous silicon dioxide by Pulsed Laser Deposition (PLD) with different annealing conditions. The results of structural analysis prove that the CFO films have high crystalline quality with (1 1 1) preferred orientation. The Raman spectra and X-ray absorption spectra (XAS) indicate that the Co ions can transfer from tetrahedral sites to octahedral sites with increasing the annealing pressure. The site exchange of Co and Fe ions leads to the change of saturation magnetization in the CFO films. Our experiments provide not only a way to control the magnetism of CFO films, but also a suitable magnetic layer to develop silicon and semiconductor based spintronic devices.

Lead palladium titanate: A room-temperature multiferroic

NASA Astrophysics Data System (ADS)

Gradauskaite, Elzbieta; Gardner, Jonathan; Smith, Rebecca M.; Morrison, Finlay D.; Lee, Stephen L.; Katiyar, Ram S.; Scott, James F.

2017-09-01

There have been a large number of papers on bismuth ferrite (BiFe O3 ) over the past few years, trying to exploit its room-temperature magnetoelectric multiferroic properties. Although these are attractive, BiFe O3 is not the ideal multiferroic due to weak magnetization and the difficulty in limiting leakage currents. Thus there is an ongoing search for alternatives, including such materials as gallium ferrite (GaFe O3 ). In the present work we report a comprehensive study of the perovskite PbT i1 -xP dxO3 with 0

Co2+Ti4+ substituted Z-type barium ferrite with enhanced imaginary permeability and resonance frequency

NASA Astrophysics Data System (ADS)

Li, Z. W.; Guoqing, Lin; Chen, Linfeng; Yuping, Wu; Ong, C. K.

2006-03-01

Co2+Ti4+ substitution for Fe3+ in Co2Z (Ba3Co2Fe24O41) has been prepared. The crystal structure and static and high-frequency magnetic properties have been studied for Ba3Co2+xTixFe24-2xO41 and the corresponding ferrite/polymer composites. As compared to the general Co2Z ferrite/polymer composite, the CoTi substituted ferrite/polymer composite with x=1.0 has a high natural resonance frequency (4.5 GHz), due to its large out-of-plane anisotropy fields Hθ. Furthermore, the maximum imaginary permeability μmax'' is increased by about 50%. The increase is attributed to a decreased damping coefficient, based on the curve-fitted results to the complex permeability spectra. The composites are good electromagnetic attenuation materials with low reflectivity and broad bandwidth at microwave frequencies.

Effect of Cu2+ substitution on the magnetic properties of co-precipitated Ni-Cu-Zn ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Ramakrishna, K. S.; Srinivas, Ch.; Tirupanyam, B. V.; Ramesh, P. N.; Meena, S. S.; Potukuchi, D. M.; Sastry, D. L.

2017-05-01

Spinel ferrite nanoparticles with chemical equation NixCu0.1Zn0.9-xFe2O4 (x = 0.5, 0.6, 0.7) have been synthsized using co-precipitation method followed by heat treatment at a temperature of 200 °C for 2h. The results of XRD, FE-SEM and VSM studies are reported. XRD patterns confirm the formation of cubic spinel phase of ferrite samples along with small amount of a secondary phase of α-Fe2O3 whose concentration decreases as Ni2+ concentration increases. The crystallite sizes (in the range of 7.5-13.9 nm) increase and the lattice parameter decreases with increase in Ni2+ ion concentration. These values are comparable to those of NiZn ferrite without Cu substitution. It has been observed that there is a considerable reduction in saturation magnetisation (Ms). This and differences in other magnetic parameters are attributed to considerable changes in cation distribution or core shell interactions of NiZn ferrite with 10 mole% Cu substitution in the place of Zn.

Structural, morphological and electrical properties of Sn-substituted Ni-Zn ferrites synthesized by double sintering technique

NASA Astrophysics Data System (ADS)

Ali, M. A.; Uddin, M. M.; Khan, M. N. I.; Chowdhury, F.-U.-Z.; Haque, S. M.

2017-02-01

The Sn-substituted Ni-Zn ferrites, (0.0≤x≤0.30), have been synthesized by the standard double sintering technique from the oxide nanopowders of Ni, Zn, Fe and Sn. The structural and electrical properties have been investigated by the X-ray diffraction (XRD), scanning electron microscopy (SEM), DC resistivity and dielectric measurements. From XRD data, the single cubic spinel phase has been confirmed for x≤0.1, whereas for x>0.1 an extra intermediate phase has been detected along with the cubic spinel phase of Ni-Zn ferrite. The grain size is increased due to Sn substitution in Ni-Zn ferrites. DC resistivity as a function of temperature has been measured by two probe method. The semiconducting nature has been found operative in the samples. The DC resistivity was found to decrease whilst the dielectric constant increased with increasing Sn content in Ni-Zn ferrites. The unusual behavior of the dielectric loss factor of the ferrites was explained by the Rezlescu model. The electrical relaxation of the ferrites has been studied in terms of electric modulus formalism and the time for dielectric relaxation was calculated. The contribution of grain resistance has been studied from the Cole-Cole plot. The suitability to use the as prepared samples in the miniaturized memory devices based capacitive components or energy storage principles are confirmed from the values of dielectric constant.

Magnetic and dielectric properties of Co doped nano crystalline Li ferrites by auto combustion method

NASA Astrophysics Data System (ADS)

Aravind, G.; Raghasudha, M.; Ravinder, D.; Kumar, R. Vijaya

2016-05-01

The ultra fine particles of the cobalt substituted lithium ferrites with the formula [Li0.5Fe0.5]1-xCoxFe2O4 (0.0≤x≤1.0) were synthesized by low temperature citrate-gel auto combustion method. Structural characterization of the samples was carried out using XRD studies and FESEM (Field Emission Scanning Electron Microscopy) analysis. XRD studies confirms the formation of single phased spinel structure with crystallite size in the range of 36-43 nm. The M-H loops have been traced using Vibrating Sample Magnetometer (VSM) for all the compositions at room temperature and hysteresis parameters were evaluated. The hysteresis loops of the prepared samples show clear saturation at an applied field of ±20 k Oe and the loops were highly symmetric in nature. The dielectric parameters such as dielectric constant (ε'), dielectric loss tangent (tan δ) of the samples were studied as a function of frequency in the range of 20 Hz to 2 MHz at room temperature using LCR Meter. The dielectric constant and loss tangent of the samples show a normal dielectric behavior with frequency which reveals that the dispersion is due to the Maxwell-Wagner type interfacial polarization and hopping of electrons between the Fe2+ and Fe3+ ions.

Structural and magnetic properties of the products of the transformation of ferrihydrite: Effect of cobalt dications

NASA Astrophysics Data System (ADS)

Camacho, K. I.; Pariona, N.; Martinez, A. I.; Baggio-Saitovitch, E.; Herrera-Trejo, M.; Perry, Dale L.

2017-05-01

The effect of cobalt dications on the transformation of 2-line ferrihydrite (2LF) has been studied. The products of the transformation reaction were characterized by X-ray diffraction, Mössbauer spectroscopy (MS), transmission electron microscopy (TEM), magnetometry, and first-order reversal curve (FORC) diagrams. It was found that the concentration of cobalt dications plays an important role on the structural and magnetic properties of the products; i.e., for low cobalt concentrations, cobalt-substituted hematite is formed, while higher concentrations promote the formation of cobalt-substituted magnetite. Structural results revealed that formation of other iron oxide polymorphs is avoided and residual 2LF is always present in the final products. In this way, hematite/2LF and magnetite/2LF nanocomposites were formed. For all the samples, magnetic measurements yielded non-saturated hysteresis loops at a maximum field of 12 kOe. For cobalt-substituted hematite/2LF samples, FORC diagrams revealed the presence of multiple single-domain (SD) components which generate interaction coupling between SD with low and high coercivity. Moreover, for cobalt-substituted magnetite/2LF samples, the FORC diagrams revealed the components of wasp-waist hysteresis loops which consist of mixtures of SD and superparamagnetic particles. One of the goals of the present study is the rigorous, experimental documentation of ferrihydrite/hematite mixtures as a function of reaction conditions for use as analytical standards research.

Synthesis and Magnetic Properties of Nearly Monodisperse CoFe2O4Nanoparticles Through a Simple Hydrothermal Condition

PubMed Central

2010-01-01

Nearly monodisperse cobalt ferrite (CoFe2O4) nanoparticles without any size-selection process have been prepared through an alluring method in an oleylamine/ethanol/water system. Well-defined nanospheres with an average size of 5.5 nm have been synthesized using metal chloride as the law materials and oleic amine as the capping agent, through a general liquid–solid-solution (LSS) process. Magnetic measurement indicates that the particles exhibit a very high coercivity at 10 K and perform superparamagnetism at room temperature which is further illuminated by ZFC/FC curves. These superparamagnetic cobalt ferrite nanomaterials are considered to have potential application in the fields of biomedicine. The synthesis method is possible to be a general approach for the preparation of other pure binary and ternary compounds. PMID:20672131

Size-dependent antimicrobial properties of the cobalt ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Žalnėravičius, Rokas; Paškevičius, Algimantas; Kurtinaitiene, Marija; Jagminas, Arūnas

2016-10-01

The growing resistance of bacteria to conventional antibiotics elicited considerable interest to non-typical drugs. In this study, antimicrobial investigations were performed on low-size dispersion cobalt ferrite nanoparticles (Nps) fabricated by co-precipitation approach in several average sizes, in particular, 15.0, 5.0, and 1.65 nm. A variety of experimental tests demonstrated that the size of these Nps is determinant for antimicrobial efficiency against S. cerevisiae and several Candida species, in particular, C. parapsilosis, C. krusei, and C. albicans. The small and ultra-small fractions of CoFe2O4 Nps possess especially strong antimicrobial activity against all tested microorganisms. The possible reasons are discussed. Nps were characterized by means of transmission and high-resolution transmission electron microscopy, X-ray diffraction, energy dispersive X-ray spectroscopy and atomic force microscopy, chemical analysis and magnetic measurements.

Modified solvothermal synthesis of cobalt ferrite (CoFe2O4) magnetic nanoparticles photocatalysts for degradation of methylene blue with H2O2/visible light

NASA Astrophysics Data System (ADS)

Kalam, Abul; Al-Sehemi, Abdullah G.; Assiri, Mohammed; Du, Gaohui; Ahmad, Tokeer; Ahmad, Irfan; Pannipara, M.

2018-03-01

Different grads of magnetic nano-scaled cobalt ferrites (CoFe2O4) photocatalysts were synthesized by modified Solvothermal (MST) process with and without polysaccharide. The indigenously synthesized photocatalysts were characterized by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), thermo gravimetric analysis (TGA), Fourier transform infrared (FT-IR), UV-visible (UV-vis) spectroscopy and N2 adsorption-desorption isotherm method. The Fourier transform infrared spectroscopy study showed the Fe-O stretching vibration 590-619 cm-1, confirming the formation of metal oxide. The crystallite size of the synthesized photocatalysts was found in the range between 20.0 and 30.0 nm. The surface area of obtained magnetic nanoparticles is found to be reasonably high in the range of 63.0-76.0 m2/g. The results shown that only MST-2 is the most active catalyst for photo-Fenton like scheme for fast photodegradation action of methylene blue dye, this is possible due to optical band gap estimated of 2.65 eV. Captivatingly the percentage of degradation efficiency increases up to 80% after 140 min by using MST-2 photocatalyst. Photocatalytic degradation of methylene blue (MB) dye under visible light irradiation with cobalt ferrite magnetic nanoparticles followed first order kinetic constant and rate constant of MST-2 is almost 2.0 times greater than MST-1 photocatalyst.

Impact of grain size and structural changes on magnetic, dielectric, electrical, impedance and modulus spectroscopic characteristics of CoFe2O4 nanoparticles synthesized by honey mediated sol-gel combustion method

NASA Astrophysics Data System (ADS)

Singh Yadav, Raghvendra; Kuřitka, Ivo; Vilcakova, Jarmila; Havlica, Jaromir; Masilko, Jiri; Kalina, Lukas; Tkacz, Jakub; Švec, Jiří; Enev, Vojtěch; Hajdúchová, Miroslava

2017-12-01

In this work CoFe2O4 spinel ferrite nanoparticles were synthesized by honey mediated sol-gel combustion method and further annealed at higher temperature 500 °C, 700 °C, 900 °C and 1100 °C. The synthesized spinel ferrite nanoparticles is investigated by x-ray diffraction, Raman spectroscopy, Fourier transform infrared (FTIR) spectroscopy, thermogravimetric analysis/differential scanning calorimetry (TGA/DSC), field emission scanning electron microscopy, x-ray photoelectron spectroscopy and vibrating sample magnetometer. The x-ray diffraction study reveals face-centered cubic spinel cobalt ferrite crystal phase formation. The crystallite size and lattice parameter are increased with annealing temperature. Raman and Fourier transform infrared spectra also confirm spinel ferrite crystal structure of synthesized nanoparticles. The existence of cation at octahedral and tetrahedral site in cobalt ferrite nanoparticles is confirmed by x-ray photoelectron spectroscopy. Magnetic measurement shows increased saturation magnetization 74.4 emu g-1 at higher annealing temperature 1100 °C, high coercivity 1347.3 Oe at lower annealing temperature 500 °C, and high remanent magnetization 32.3 emu g-1 at 900 °C annealing temperature. The magnetic properties of synthesized ferrite nanoparticles can be tuned by adjusting sizes through annealing temperature. Furthermore, the dielectric constant and ac conductivity shows variation with frequency (1-107 Hz), grain size and cation redistribution. The modulus spectroscopy study reveals the role of bulk grain and grain boundary towards the resistance and capacitance. The cole-cole plots in modulus formalism also well support the electrical response of nanoparticles originated from both grain and grain boundaries. The dielectric, electrical, magnetic, impedance and modulus spectroscopic characteristics of synthesized CoFe2O4 spinel ferrite nanoparticles demonstrate the applicability of these nanoparticles for magnetic recording, memory devices and for microwave applications.

Nickel-doped cobalt ferrite nanoparticles: efficient catalysts for the reduction of nitroaromatic compounds and photo-oxidative degradation of toxic dyes.

PubMed

Singh, Charanjit; Goyal, Ankita; Singhal, Sonal

2014-07-21

This study deals with the exploration of NixCo₁-xFe₂O₄ (x = 0.0, 0.2, 0.4, 0.6, 0.8, 1.0) ferrite nanoparticles as catalysts for reduction of 4-nitrophenol and photo-oxidative degradation of Rhodamine B. The ferrite samples with uniform size distribution were synthesized using the reverse micelle technique. The structural investigation was performed using powder X-ray diffraction, high-resolution transmission electron microscopy, energy dispersive X-ray and scanning tunneling microscopy. The spherical particles with ordered cubic spinel structure were found to have the crystallite size of 4-6 nm. Diffused UV-visible reflectance spectroscopy was employed to investigate the optical properties of the synthesized ferrite nanoparticles. The surface area calculated using BET method was found to be highest for Co₀.₄Ni₀.₆Fe₂O₄ (154.02 m(2) g(-1)). Co₀.₄Ni₀.₆Fe₂O₄ showed the best catalytic activity for reduction of 4-nitrophenol to 4-aminophenol in the presence of NaBH4 as reducing agent, whereas CoFe₂O₄ was found to be catalytically inactive. The reduction reaction followed pseudo-first order kinetics. The effect of varying the concentration of catalyst and NaBH₄ on the reaction rates was also scrutinized. The photo-oxidative degradation of Rhodamine B, enhanced oxidation efficacy was observed with the introduction of Ni(2+) in to the cobalt ferrite lattice due to octahedral site preference of Ni(2+). Almost 99% degradation was achieved in 20 min using NiFe₂O₄ nanoparticles as catalyst.

Performance of a Wideband Cadmium Ferrite Microstrip Patch Antenna in the X-Band Region

NASA Astrophysics Data System (ADS)

Bhongale, S. R.; Ingavale, H. R.; Shinde, T. J.; Vasambekar, P. N.

2018-01-01

Magnesium-substituted cadmium ferrites with the chemical composition Mg x Cd1- x Fe2O4 ( x = 0, 0.4 and 0.8) were prepared by an oxalate co-precipitation method under microwave sintering technique. The structural properties of ferrites were studied by x-ray diffraction, Fourier transform infrared spectroscopy and field emission scanning electron microscope techniques. The scattering parameters such as reflection coefficient ( S 11) and transmission coefficient ( S 21) at microwave frequencies of palletized ferrites were measured by using a vector network analyzer. The software module 85071E followed by scattering parameters was used to determine the electromagnetic properties of the ferrites. The values determined for electromagnetic parameters such as the real part of permittivity ( ɛ'), permeability ( μ'), dielectric loss tangent (tan δ e) and magnetic loss tangent (tan δ m) of synthesized ferrites were used to design rectangular microstrip patch antennas. The performance of magnesium-substituted Cd ferrites as substrate for microstrip patch antennas was investigated. The antenna parameters such as return loss, bandwidth, voltage standing wave ratio, Smith chart and radiation pattern were studied. It is found that the Cd ferrite has applicability as a substrate for wideband antennas in the X-band region.

Effect of the deposition of cobalt on the optoelectronic properties of quantum-confined In(Ga)As/GaAs heteronanostructures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Volkova, N. S., E-mail: volkovans88@mail.ru; Gorshkov, A. P.; Zdoroveyshchev, A. V.

2015-12-15

The systematic features of the inf luence of defect formation during the deposition of a cobalt contact on the optoelectronic characteristics of structures containing InAs/GaAs quantum dots and In{sub x}Ga{sub 1–x}As/GaAs quantum wells are studied. From analysis of the temperature dependences of the photosensitivity of the InAs/GaAs quantum-dot structures, the values of the resultant recombination lifetime of photoexcited charge carriers in quantum dots at different conditions of Co deposition and at different structural parameters are determined.

Gadolinium substitution effect on the thermomagnetic properties of Ni ferrite ferrofluids

NASA Astrophysics Data System (ADS)

Jacobo, Silvia E.; Arana, Mercedes; Bercoff, Paula G.

2016-10-01

This work is focused on the structural and magnetic characterization of Gd-doped Ni ferrite nanoparticles and the preparation of a ferrofluid for applications in heat-transfer devices. For this purpose, spinel ferrites NiFe2O4, and NiFe1.88Gd0.12O4 were prepared by the self-combustion method. The substituted sample was obtained with a small amount of Gd inclusion and the excess appeared as GdFeO3. The smallest nanoparticles of both samples were properly coated and dispersed in kerosene. Thermal conductivities of the produced ferrofluids were measured at 25 °C under an applied magnetic field. There is a significant enhancement in the thermal conductivity of the ferrofluid prepared with NiGd ferrite with respect to the one with Ni ferrite, in presence of a magnetic field. This effect is directly related to the well-known magnetocaloric effect of Gd.

Growth mechanism and elemental distribution of beta-Ga2O3 crystalline nanowires synthesized by cobalt-assisted chemical vapor deposition.

PubMed

Wang, Hui; Lan, Yucheng; Zhang, Jiaming; Crimp, Martin A; Ren, Zhifeng

2012-04-01

Long beta-Ga2O3 crystalline nanowires are synthesized on patterned silicon substrates using chemical vapor deposition technique. Advanced electron microscopy indicates that the as-grown beta-Ga2O3 nanowires are consisted of poly-crystalline (Co, Ga)O tips and straight crystalline beta-Ga2O3 stems. The catalytic cobalt not only locates at the nanowire tips but diffuses into beta-Ga2O3 nanowire stems several ten nanometers. A solid diffusion growth mechanism is proposed based on the spatial elemental distribution along the beta-Ga2O3 nanowires at nanoscale.

Effect of cobalt on Escherichia coli metabolism and metalloporphyrin formation

PubMed Central

Majtan, Tomas; Frerman, Frank E.

2011-01-01

Toxicity in Escherichia coli resulting from high concentrations of cobalt has been explained by competition of cobalt with iron in various metabolic processes including Fe–S cluster assembly, sulfur assimilation, production of free radicals and reduction of free thiol pool. Here we present another aspect of increased cobalt concentrations in the culture medium resulting in the production of cobalt protoporphyrin IX (CoPPIX), which was incorporated into heme proteins including membrane-bound cytochromes and an expressed human cystathionine beta-synthase (CBS). The presence of CoPPIX in cytochromes inhibited their electron transport capacity and resulted in a substantially decreased respiration. Bacterial cells adapted to the increased cobalt concentration by inducing a modified mixed acid fermentative pathway under aerobiosis. We capitalized on the ability of E. coli to insert cobalt into PPIX to carry out an expression of CoPPIX-substituted heme proteins. The level of CoPPIX-substitution increased with the number of passages of cells in a cobalt-containing medium. This approach is an inexpensive method to prepare cobalt-substituted heme proteins compared to in vitro enzyme reconstitution or in vivo replacement using metalloporphyrin heme analogs and seems to be especially suitable for complex heme proteins with an additional coenzyme, such as human CBS. PMID:21184140

Small Scale Burner Review

DTIC Science & Technology

2009-07-01

dopants in the semiconductor components of the devices (5). Venkatasubramanian (46) reviewed some state- of-the-art TE materials such as quantum-dot...conversion efficiency of a GaSb micro TPV system incorporating broadband silicon carbide (SiC) and selective emitted materials ( cobalt [Co]/nickel...carbon CFD computational fluid dynamics Co cobalt CO carbon monoxide CO2 carbon dioxide Cu copper GaSb gallium antimonide InGaAs indium gallium

Structural and Magnetic Response in Bimetallic Core/Shell Magnetic Nanoparticles

PubMed Central

Nairan, Adeela; Khan, Usman; Iqbal, Munawar; Khan, Maaz; Javed, Khalid; Riaz, Saira; Naseem, Shahzad; Han, Xiufeng

2016-01-01

Bimagnetic monodisperse CoFe2O4/Fe3O4 core/shell nanoparticles have been prepared by solution evaporation route. To demonstrate preferential coating of iron oxide onto the surface of ferrite nanoparticles X-ray diffraction (XRD), High resolution transmission electron microscope (HR-TEM) and Raman spectroscopy have been performed. XRD analysis using Rietveld refinement technique confirms single phase nanoparticles with average seed size of about 18 nm and thickness of shell is 3 nm, which corroborates with transmission electron microscopy (TEM) analysis. Low temperature magnetic hysteresis loops showed interesting behavior. We have observed large coercivity 15.8 kOe at T = 5 K, whereas maximum saturation magnetization (125 emu/g) is attained at T = 100 K for CoFe2O4/Fe3O4 core/shell nanoparticles. Saturation magnetization decreases due to structural distortions at the surface of shell below 100 K. Zero field cooled (ZFC) and Field cooled (FC) plots show that synthesized nanoparticles are ferromagnetic till room temperature and it has been noticed that core/shell sample possess high blocking temperature than Cobalt Ferrite. Results indicate that presence of iron oxide shell significantly increases magnetic parameters as compared to the simple cobalt ferrite. PMID:28335200

Frequency-Dependent Magnetic Susceptibility of Magnetite and Cobalt Ferrite Nanoparticles Embedded in PAA Hydrogel

PubMed Central

van Berkum, Susanne; Dee, Joris T.; Philipse, Albert P.; Erné, Ben H.

2013-01-01

Chemically responsive hydrogels with embedded magnetic nanoparticles are of interest for biosensors that magnetically detect chemical changes. A crucial point is the irreversible linkage of nanoparticles to the hydrogel network, preventing loss of nanoparticles upon repeated swelling and shrinking of the gel. Here, acrylic acid monomers are adsorbed onto ferrite nanoparticles, which subsequently participate in polymerization during synthesis of poly(acrylic acid)-based hydrogels (PAA). To demonstrate the fixation of the nanoparticles to the polymer, our original approach is to measure low-field AC magnetic susceptibility spectra in the 0.1 Hz to 1 MHz range. In the hydrogel, the magnetization dynamics of small iron oxide nanoparticles are comparable to those of the particles dispersed in a liquid, due to fast Néel relaxation inside the particles; this renders the ferrogel useful for chemical sensing at frequencies of several kHz. However, ferrogels holding thermally blocked iron oxide or cobalt ferrite nanoparticles show significant decrease of the magnetic susceptibility resulting from a frozen magnetic structure. This confirms that the nanoparticles are unable to rotate thermally inside the hydrogel, in agreement with their irreversible fixation to the polymer network. PMID:23673482

Experimental demonstration of all-optical weak magnetic field detection using beam-deflection of single-mode fiber coated with cobalt-doped nickel ferrite nanoparticles.

PubMed

Pradhan, Somarpita; Chaudhuri, Partha Roy

2015-07-10

We experimentally demonstrate single-mode optical-fiber-beam-deflection configuration for weak magnetic-field-detection using an optimized (low coercive-field) composition of cobalt-doped nickel ferrite nanoparticles. Devising a fiber-double-slit type experiment, we measure the surrounding magnetic field through precisely measuring interference-fringe yielding a minimum detectable field ∼100  mT and we procure magnetization data of the sample that fairly predicts SQUID measurement. To improve sensitivity, we incorporate etched single-mode fiber in double-slit arrangement and recorded a minimum detectable field, ∼30  mT. To further improve, we redefine the experiment as modulating fiber-to-fiber light-transmission and demonstrate the minimum field as 2.0 mT. The device will be uniquely suited for electrical or otherwise hazardous environments.

Cobalt ferrite nanocrystals: out-performing magnetotactic bacteria.

PubMed

Prozorov, Tanya; Palo, Pierre; Wang, Lijun; Nilsen-Hamilton, Marit; Jones, DeAnna; Orr, Daniel; Mallapragada, Surya K; Narasimhan, Balaji; Canfield, Paul C; Prozorov, Ruslan

2007-10-01

Magnetotactic bacteria produce exquisitely ordered chains of uniform magnetite (Fe(3)O(4)) nanocrystals, and the use of the bacterial mms6 protein allows for the shape-selective synthesis of Fe(3)O(4) nanocrystals. Cobalt ferrite (CoFe(2)O(4)) nanoparticles, on the other hand, are not known to occur in living organisms. Here we report on the use of the recombinant mms6 protein in a templated synthesis of CoFe(2)O(4) nanocrystals in vitro. We have covalently attached the full-length mms6 protein and a synthetic C-terminal domain of mms6 protein to self-assembling polymers in order to template hierarchical CoFe(2)O(4) nanostructures. This new synthesis pathway enables facile room-temperature shape-specific synthesis of complex magnetic crystalline nanomaterials with particle sizes in the range of 40-100 nm that are difficult to produce using conventional techniques.

Synthesis and characterization of structural and magnetic properties of polyaniline-cobalt ferrite (PA-CoFe) nanocomposites

NASA Astrophysics Data System (ADS)

Thakur, Sonika; Kaur, Parminder; Singh, Lakhwant

2018-05-01

The growing interest in the investigation of the properties of modified conducting polymers stems from their potential applications in various fields such as in sensing and catalytic devices. The present work reports the modification of conducting polymer polyaniline with cobalt ferrite (CoFe) nanoparticles, where CoFe nanoparticles are added in different successive weight percents. The composite samples were synthesized by in-situ chemical oxidative polymerization technique. The density of the samples has been found to increase with an increase in the CoFe content. Structural analysis of the synthesized sample has been done using X-ray diffraction studies. Perusal of the hysteresis curves of the prepared samples depicts that the introduction of CoFe into the polymer matrix leads to enhancement in the ferromagnetic behavior of the synthesized samples, suggesting that these nanocomposites have excellent microwave absorbing capacity.

Magnetic and High-Frequency Dielectric Parameters of Divalent Ion-Substituted W-Type Hexagonal Ferrites

NASA Astrophysics Data System (ADS)

Ali, Akbar; Grössinger, R.; Imran, Muhammad; Khan, M. Ajmal; Elahi, Asmat; Akhtar, Majid Niaz; Mustafa, Ghulam; Khan, Muhammad Azhar; Ullah, Hafeez; Murtaza, Ghulam; Ahmad, Mukhtar

2017-02-01

Polycrystalline W-type hexagonal ferrites with chemical formulae Ba0.5Sr0.5 Co2- x Me x Fe16O27 ( x = 0, 0.5, Me = Mn, Mg, Zn, Ni) have been prepared using sol-gel autocombustion. It has been reported in our earlier published work that all the samples exhibit a single-phase W-type hexagonal structure which was confirmed by x-ray diffraction (XRD) analysis. The values of bulk density lie in the range of 4.64-4.78 g/cm3 for all the samples which are quite high as compared to those for other types of hexaferrites. It was also observed that Zn-substituted ferrite reflects the highest (14.7 × 107 Ω-cm) whereas Mn-substituted ferrite has the lowest (11.3 × 107 Ω-cm) values of direct current (DC) electrical resistivity. The observed values of saturation magnetization ( M s) are found to be in the range of 62.01-68.7 emu/g depending upon the type of cation substitution into the hexagonal lattice. All the samples exhibit a typical soft magnetic character with low values of coercivity ( H c) that are in the range of 26-85 Oe. These ferrites may be promising materials for microwave absorbers due to their higher saturation magnetization and low coercivities. Both the dielectric constant and tangent loss decrease with increasing frequency in the lower frequency region and become constant in the higher frequency region. The much lower dielectric constant obtained in this study makes the investigated ferrites very useful for high-frequency applications, i.e. dielectric resonators and for camouflaging military targets such as ships, tanks and aircrafts, etc.

Cobalt ferrite nano-composite coated on glass by Doctor Blade method for photo-catalytic degradation of an azo textile dye Reactive Red 4: XRD, FESEM and DRS investigations.

PubMed

Habibi, Mohammad Hossein; Parhizkar, Janan

2015-11-05

Cobalt ferrite nano-composite was prepared by hydrothermal route using cobalt nitrate, iron nitrate and ethylene glycol as chelating agent. The nano-composite was coated on glass by Doctor Blade method and annealed at 300 °C. The structural, optical, and photocatalytic properties have been studied by powder X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM) and UV-visible spectroscopy (UV-Vis DRS). Powder XRD analysis confirmed formation of CoFe2O4 spinel phase. The estimated particle size from FESEM data was 50 nm. The calculated energy band gaps, obtained by Tauc relation from UV-Vis absorption spectra was 1.3 eV. Photocatalytic degradation of Reactive Red 4 as an azo textile was investigated in aqueous solution under irradiation showed 68.0% degradation of the dye within 100 min. The experimental enhanced activity compare to pure Fe2O3 can be ascribed to the formation of composite, which was mainly attributable to the transfer of electron and hole to the surface of composite and hinder the electron hole recombination. Copyright © 2015 Elsevier B.V. All rights reserved.

Effect of powder compaction on radiation-thermal synthesis of lithium-titanium ferrites

NASA Astrophysics Data System (ADS)

Surzhikov, A. P.; Lysenko, E. N.; Vlasov, V. A.; Malyshev, A. V.; Korobeynikov, M. V.; Mikhailenko, M. A.

2017-01-01

Effect of powder compaction on the efficiency of thermal and radiation-thermal synthesis of lithium-substituted ferrites was investigated by X-Ray diffraction and specific magnetization analysis. It was shown that the radiation-thermal heating of compacted powder reagents mixture leads to an increase in efficiency of lithium-titanium ferrites synthesis.

Structural and magnetic properties of Ni1-xZnxFe2O4 synthesized through the sol-gel method

NASA Astrophysics Data System (ADS)

Guan, Beh Hoe; Zahari, Muhammad Hanif; Chuan, Lee Kean

2016-11-01

Modification of crystal structure by means of substitution would result in the modification of the overall physical properties of crystallite materials especially in ferrites. This study aims to investigate the effect of non-magnetic Zn substitution in spinel NiFe2O4 and its direct effect towards its microstructural and magnetic properties. Magnetic nanoparticles of Nickel-Zinc ferrite with the chemical formula, Ni1-xZnxFe2O4 (x=0.00, 0.25, 0.50, 0.75) were synthesized through the sol-gel route. Phase formation and structural properties of the synthesized ferrite were identified through X-ray diffraction (XRD) analysis and transmission electron microscopy (TEM). Magnetic properties such as the magnetic saturation, coercivity and remanence were measured by a vibrating sample magnetometer (VSM). XRD measurements reveals successful synthesis of single-phased Nickel ferrite and Nickel—Zinc ferrite. Both crystallite and grain size shows fluctuation with increasing Zn content. The ferrites were found to be ferrimagnetic in nature and show differing values with different x values.

Nickel-doped cobalt ferrite nanoparticles: efficient catalysts for the reduction of nitroaromatic compounds and photo-oxidative degradation of toxic dyes

NASA Astrophysics Data System (ADS)

Singh, Charanjit; Goyal, Ankita; Singhal, Sonal

2014-06-01

This study deals with the exploration of NixCo1-xFe2O4 (x = 0.0, 0.2, 0.4, 0.6, 0.8, 1.0) ferrite nanoparticles as catalysts for reduction of 4-nitrophenol and photo-oxidative degradation of Rhodamine B. The ferrite samples with uniform size distribution were synthesized using the reverse micelle technique. The structural investigation was performed using powder X-ray diffraction, high-resolution transmission electron microscopy, energy dispersive X-ray and scanning tunneling microscopy. The spherical particles with ordered cubic spinel structure were found to have the crystallite size of 4-6 nm. Diffused UV-visible reflectance spectroscopy was employed to investigate the optical properties of the synthesized ferrite nanoparticles. The surface area calculated using BET method was found to be highest for Co0.4Ni0.6Fe2O4 (154.02 m2 g-1). Co0.4Ni0.6Fe2O4 showed the best catalytic activity for reduction of 4-nitrophenol to 4-aminophenol in the presence of NaBH4 as reducing agent, whereas CoFe2O4 was found to be catalytically inactive. The reduction reaction followed pseudo-first order kinetics. The effect of varying the concentration of catalyst and NaBH4 on the reaction rates was also scrutinized. The photo-oxidative degradation of Rhodamine B, enhanced oxidation efficacy was observed with the introduction of Ni2+ in to the cobalt ferrite lattice due to octahedral site preference of Ni2+. Almost 99% degradation was achieved in 20 min using NiFe2O4 nanoparticles as catalyst.

Dielectric and impedance study of praseodymium substituted Mg-based spinel ferrites

NASA Astrophysics Data System (ADS)

Farid, Hafiz Muhammad Tahir; Ahmad, Ishtiaq; Ali, Irshad; Ramay, Shahid M.; Mahmood, Asif; Murtaza, G.

2017-07-01

Spinel ferrites with nominal composition MgPryFe2-yO4 (y = 0.00, 0.025, 0.05, 0.075, 0.10) were prepared by sol-gel method. Temperature dependent DC electrical conductivity and drift mobility were found in good agreement with each other, reflecting semiconducting behavior. The dielectric properties of all the samples as a function of frequency (1 MHz-3 GHz) were measured at room temperature. The dielectric constant and complex dielectric constant of these samples decreased with the increase of praseodymium concentration. In the present spinel ferrite, Cole-Cole plots were used to separate the grain and grain boundary's effects. The substitution of praseodymium ions in Mg-based spinel ferrites leads to a remarkable rise of grain boundary's resistance as compared to the grain's resistance. As both AC conductivity and Cole-Cole plots are the functions of concentration, they reveal the dominant contribution of grain boundaries in the conduction mechanism. AC activation energy was lower than dc activation energy. Temperature dependence normalized AC susceptibility of spinel ferrites reveals that MgFe2O4 exhibits multi domain (MD) structure with high Curie temperature while on substitution of praseodymium, MD to SD transitions occurs. The low values of conductivity and low dielectric loss make these materials best candidate for high frequency application.

Effect on the structural, DC resistivity and magnetic properties of Zr and Cu co-SubstitutedNi0.5Zn0.5Fe2O4using sol-gel auto-combustion method

NASA Astrophysics Data System (ADS)

Jalaiah, K.; Vijaya Babu, K.; Chandra mouli, K.; Subba Rao, P. S. V.

2018-04-01

The Zr and Cu co-substituted Ni0.5Zn0.5Fe2O4 ferrite nanoparticles have been synthesized by the sol-gel auto combustion method. The XRD patterns confirmed single phase cubic spinel structure for present ferrite systems. The substitution of co-dopants in the spinel structure initially decreases the lattice parameter from x = 0.00 to 0.08 and thereafter increases and the same tendency reflecting in cell volume. The DC resistivity was initially increased later followed the decreasing trend; however the drift mobility of all ferrite samples appears to be in opposite phenomenon to DC resistivity. The saturation magnetization and net magnetic moments of all ferrite samples are decreasing with increasing dopant concentration. The coercive field and Y-K angles are increased with dopant concentration. The initial permeability of all samples is decreased with increasing dopant concentration. The Q-Factor for all samples shows the narrow frequency band with increasing frequency.

Significant reduction of saturation magnetization and microwave-reflection loss in barium-natural ferrite via Nd3+ substitution

NASA Astrophysics Data System (ADS)

Widanarto, W.; Ardenti, E.; Ghoshal, S. K.; Kurniawan, C.; Effendi, M.; Cahyanto, W. T.

2018-06-01

To minimize the signal degradation, many electronic devices require efficient microwave absorbers with very low reflection-losses within the X-band. We prepared a series of trivalent neodymium-ion (Nd3+) substituted barium-natural ferrite using a modified solid-state reaction method. The effect of the Nd3+-ion content on the structure, surface morphology, magnetic properties, and microwave reflection loss was studied. The composites were characterized using X-ray diffraction, a vibrating sample magnetometer, scanning electron microscopy, and a vector network analyzer. The XRD patterns of the sample without Nd3+ reveal the presence of BaFe12O19 (hexagonal) and BaFe2O4 (rhombohedral) phases. Furthermore, a new hexagonal crystal phase of Ba6Nd2Fe4O15 appeared after substituting Nd3+. The average size of the prepared barium-natural ferrite particles was estimated to be between 0.4 and 0.8 μm. Both saturation magnetization and microwave reflection losses of these barium-ferrites were significantly reduced by increasing the Nd3+ content.

Improved photocatalytic activities of CuxCo0.5-xNi0.5Fe2O4 nanoparticles through co-precipitation method in degrading methylene blue

NASA Astrophysics Data System (ADS)

Lassoued, Abdelmajid; Lassoued, Mohamed Saber; Dkhil, Brahim; Ammar, Salah; Gadri, Abdellatif

2018-07-01

We report the synthesis of CuxCo0.5-xNi0.5Fe2O4 with x = (0.1, 0.2, 0.3, 0.4) nanoparticles using the co-precipitation method in the presence of oleic acid as a surfactant and coating material. The X-ray diffraction analysis with Rietveld refinement technique confirmed the formation of cubic phase with Fd-3m space group of all the prepared nano-ferrites. The average crystallite size varies in the range of 21-38 nm with varying concentration of copper. The lattice parameter was found to decrease with increase in copper substitution. This may be attributed to larger ionic radius of cobalt as compared to that of copper. TEM and SEM analysis showed the monodispersion and cubic-like nanostructure. Two prominent stretching bands were observed in FT-IR spectra around 400-600 cm-1. These two bands confirmed the spinel structure of the prepared nanoparticles. Raman spectroscopy is used to verify that we have synthesized ferrite spinels and determines their phonon modes. The thermal decomposition of CuxCo0.5-xNi0.5Fe2O4 was investigated by TGA∖DTA. The optical study UV-visible is used to calculate the optical band gap energies. The products exhibited the attractive magnetic properties with high saturation magnetization, which were examined by a vibrating sample magnetometer (VSM). On the other part, the photocatalytic activity of our compounds was studied using methylene blue (MB) as model organic pollutants, where the results showed that an appropriate amount of copper (Cu2+) could greatly increase the amount of hydroxyl radicals generated by the ferrite nanoparticles, which were responsible for the obvious increase in the photocatalytic activity.

Oleate Coated Magnetic Cores Based on Magnetite, Zn Ferrite and Co Ferrite Nanoparticles - Preparation, Physical Characterization and Biological Impact on Helianthus Annuus Photosynthesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ursache-Oprisan, Manuela; Foca-nici, Ecaterina; Cirlescu, Aurelian

2010-12-02

Sodium oleate was used as coating shell for magnetite, Zn ferrite and Co ferrite powders to stabilize them in the form of aqueous magnetic suspensions. The physical characterization was carried out by applying X-ray diffraction and magnetization measurements. Both crystallite size and magnetic core diameter ranged between 7 and 11 nm. The influence of magnetic nanoparticle suspensions (corresponding to magnetic nanoparticle levels of 10{sup -14}-10{sup -15}/cm{sup 3}) on sunflower seedlings was studied considering the changes in the photosynthesis pigment levels. Similar responses were obtained for magnetite and cobalt ferrite nanoparticle treatment consisting in the apparent inhibition of chlorophyll biosynthesis whilemore » for zinc ferrite nanoparticles some concentrations seemed to have stimulatory effects on the chlorophylls as well as on the carotene levels. But the chlorophyll ratio was diminished in the case of all three types of magnetic nanoparticles meaning their slight negative effect on the light harvesting complex II (LHC II) from the chloroplast membranes and consequently on the photosynthesis efficiency.« less

Oleate Coated Magnetic Cores Based on Magnetite, Zn Ferrite and Co Ferrite Nanoparticles—Preparation, Physical Characterization and Biological Impact on Helianthus Annuus Photosynthesis

NASA Astrophysics Data System (ADS)

Ursache-Oprisan, Manuela; Foca-nici, Ecaterina; Cirlescu, Aurelian; Caltun, Ovidiu; Creanga, Dorina

2010-12-01

Sodium oleate was used as coating shell for magnetite, Zn ferrite and Co ferrite powders to stabilize them in the form of aqueous magnetic suspensions. The physical characterization was carried out by applying X-ray diffraction and magnetization measurements. Both crystallite size and magnetic core diameter ranged between 7 and 11 nm. The influence of magnetic nanoparticle suspensions (corresponding to magnetic nanoparticle levels of 10-14-10-15/cm3) on sunflower seedlings was studied considering the changes in the photosynthesis pigment levels. Similar responses were obtained for magnetite and cobalt ferrite nanoparticle treatment consisting in the apparent inhibition of chlorophyll biosynthesis while for zinc ferrite nanoparticles some concentrations seemed to have stimulatory effects on the chlorophylls as well as on the carotene levels. But the chlorophyll ratio was diminished in the case of all three types of magnetic nanoparticles meaning their slight negative effect on the light harvesting complex II (LHC II) from the chloroplast membranes and consequently on the photosynthesis efficiency.

The Influence of Al+++ Substitution for Fe+++ in M-Type Ba Ferrite Powder on the Intrinsic Coercivity HcJ

NASA Astrophysics Data System (ADS)

Zheng, Zong-Yu; Feng, Jie; Mei, Xue-Ming; Guo, Bi-Jun; Zhang,

1990-05-01

The influence of Al+++ Substitution for Fe+++ in M-type Ba ferrite on the magnetocrystalline anisotropy field HA and the critical single-domain radius Rc has been studied by Haneda and Kojima. It is difficult to obtain HcJ values agreeing with theoretical results for the reason that the HcJ is very sensitive to the preparation method. We have been developing a new method called “coprecipitation combined with high-temperature melting.” It offers a suitable condition for studying the rule of HcJ of Ba Fe12-xAlxO19. Our results conformed to the effects calculated by Haneda and Kojima. The highest level of HcJ in our experiment reached 16000 Oe. We have fabricated plastic sheet magnets from the superhigh HcJ ferrite powder and padded the soft ferrite core with this sheet magnet to adjust the bias magnetic field. This ferrite core can be improved and the weight and size of the device can be reduced.

Structural and magnetic properties of ytterbium substituted spinel ferrites

NASA Astrophysics Data System (ADS)

Alonizan, Norah H.; Qindeel, Rabia

2018-06-01

Chemical co-precipitation route adopted to synthesize the magnetic materials. In the present work, iron is replaced by ytterbium ion in manganese-based spinel ferrites. The yield chemically represented by MnYb x Fe2- x O4 ( x = 0.00, 0.025, 0.05, 0.075, 0.10) and its structural, magnetic and electrical properties were observed. The cubic structure of spinel ferrites was confirmed by X-ray diffraction analysis. Spherically shaped grains were perceived in SEM pictures and size lessened with the growth of ytterbium concentration. SEM profile also shows little irregularity in spherical particles. The substitution of ytterbium (Yb) results in the enhancement of electrical resistivity. The resistivity was reduced with the gradual increase in temperature from 303 to 693 K. The trend of activation energy was found to be similar to that of room temperature resistivity. The coercivity of samples was raised with Yb-ion substitution while saturation magnetization and remanence reduced.

Chemical Synthesis of Next Generation High Energy Product Hybrid SmCo Permanent Magnets for High Temperature Applications

DTIC Science & Technology

2010-08-01

among CoxC, AINiCo and Ba / Sr ferrite magnets. AINiCo is shown to exhibit high (BH)max, 35 kJmŗ, but a low intrinsic coercivity, mostly ə kOe...whereas Ba / Sr ferrite features high intrinsic coercivity, 3-4.5 kOe, but typical values of (BH)max below 25 kJm-3. However, the multiple...coercivity of cobalt carbide nanoparticles is compared with free powders of AINiCo and ceramic magnets of the Ba / Sr hexaferrite type. Curie temperatures near

Magnetic and structural properties of CoFe 2O 4 thin films synthesized via a sol-gel process

NASA Astrophysics Data System (ADS)

dos S. Duque, J. G.; Macêdo, M. A.; Moreno, N. O.; Lopez, J. L.; Pfanes, H.-D.

2001-05-01

Using a sol-gel process having the coconut water as a precursor of organic chain, we synthesized thin films of cobalt ferrite. The films were characterized by using a SQUID magnetometer, an X-ray diffractometer, an X-ray spectrophotometer, Mössbauer spectroscopy and atomic force microscope. Co ferrite films annealed at 500°C for 2 h show grain sizes between 10 and 20 nm, grown as single-phase spinel structure and exhibit high coercivity and a moderate saturation magnetization (above 30 kOe).

Magnetic cobalt ferrite composite as an efficient catalyst for photocatalytic oxidation of carbamazepine.

PubMed

He, Yongzhen; Dai, Chaomeng; Zhou, Xuefei

2017-01-01

A magnetic spinel cobalt ferrite nanoparticle composite (CFO) was prepared via an ultrasonication-assisted co-precipitation method. The morphological structure and surface composition of CFO before and after reaction were investigated by using X-ray diffraction, scanning electron microscopy, transmission electron microscopy, energy dispersive X-ray, and Fourier transform infrared spectroscopy, indicating the consumption of iron oxide during photodegradation. X-ray photoelectron spectroscopy and vibrating sample magnetometry confirm the preparation of the ferrite nanoparticle composite and its magnetic properties. The prepared CFO was then used for the photocatalytic degradation of carbamazepine (CBZ) as an example of pharmaceuticals and personal care products (PPCPs) from aqueous solution. The effects of the nanocomposite dosage, contact time, and solution pH on the photodegradation process were investigated. More than 96% of the CBZ was degraded within 100 min at 0.2 g·L -1 CFO in the presence of UV light. The reactive species for CBZ degradation in the CFO/UV system was identified as hydroxyl radicals by the methanol scavenging method. Combined with the detection of leached iron ions during the process, the CBZ degradation mechanism can be presumed to be heterogeneous and homogeneous photocatalytic degradation in the CFO/UV system. Furthermore, iminostilbene and acridine were detected as intermediate products by GC-MS.

Magnetic and magneto elastic properties of cobalt ferrite ceramic compacted through cold isostatic pressing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Indla, Srinivas; Das, Dibakar, E-mail: ddse@uohyd.ernet.in; Chelvane, Arout

2016-05-06

Nano crystalline CoFe{sub 2}O{sub 4} powder was prepared by combustion synthesis method. As synthesized powder was calcined at an appropriate condition to remove the impurities and to promote phase formation. Phase pure CoFe{sub 2}O{sub 4} powder was pressed into cylindrical rod at an applied pressure of 200 MPa using a cold isostatic pressing. Sintering of the green compact at 1350°c for 12 hrs resulted in sintered cylindrical rod with ~85% of the theoretical density. Single phase cubic spinel structure was observed in the powder x-ray diffraction pattern of the sintered pellet. Scanning electron micrographs (SEM) of the as sintered pelletmore » revealed the microstructure to be composed of ferrite grains of average size ~4 µm. Saturation magnetization of 72 emu/g and coercivity of 355 Oe were observed for cobalt ferrite sample. The magnetostriction was measured on a circular disc (12 mm diameter and 12 mm length) with the strain gauge (350 Ω) mounted on the flat surface of the circular disc. Magnetostriciton of 180 ppm and strain derivative of 1 × 10{sup −9} m/A were observed for the sintered CoFe{sub 2}O{sub 4} sample.« less

Two-stage preparation of magnetic sorbent based on exfoliated graphite with ferrite phases for sorption of oil and liquid hydrocarbons from the water surface

NASA Astrophysics Data System (ADS)

Pavlova, Julia A.; Ivanov, Andrei V.; Maksimova, Natalia V.; Pokholok, Konstantin V.; Vasiliev, Alexander V.; Malakho, Artem P.; Avdeev, Victor V.

2018-05-01

Due to the macropore structure and the hydrophobic properties, exfoliated graphite (EG) is considered as a perspective sorbent for oil and liquid hydrocarbons from the water surface. However, there is the problem of EG collection from the water surface. One of the solutions is the modification of EG by a magnetic compound and the collection of EG with sorbed oil using the magnetic field. In this work, the method of the two-stage preparation of exfoliated graphite with ferrite phases is proposed. This method includes the impregnation of expandable graphite in the mixed solution of iron (III) chloride and cobalt (II) or nickel (II) nitrate in the first stage and the thermal exfoliation of impregnated expandable graphite with the formation of exfoliated graphite containing cobalt and nickel ferrites in the second stage. Such two-stage method makes it possible to obtain the sorbent based on EG modified by ferrimagnetic phases with high sorption capacity toward oil (up to 45-51 g/g) and high saturation magnetization (up to 42 emu/g). On the other hand, this method allows to produce the magnetic sorbent in a short period of time (up to 10 s) during which the thermal exfoliation is carried out in the air atmosphere.

Polyethylene glycol coated CoFe{sub 2}O{sub 4} nanoparticles: A potential spinel ferrite for biomedical applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Humbe, Ashok V.; Birajdar, Shankar D.; Jadhav, K. M., E-mail: drjadhavkm@gmail.com

2015-06-24

The structural and magnetic properties of the polyethylene glycol (PEG) coated cobalt spinel ferrite (CoFe{sub 2}O{sub 4}) nanoparticles have been reported in the present study. CoFe{sub 2}O{sub 4} nanoparticles were prepared by sol-gel auto-combustion method using citric acid + ethylene glycol as a fuel. The prepared powder of cobalt ferrite nanoparticles was annealed at 600°C for 6h and used for further study. The structural characterization of CoFe{sub 2}O{sub 4} nanoparticles were carried out by X-ray diffraction technique. The X-ray analysis confirmed the formation of single phase cubic spinel structure. The crystallite size, Lattice constant and X-ray density of the PEGmore » coated CoFe{sub 2}O{sub 4} nanoparticles were calculated by using XRD data. The presence of PEG on CoFe{sub 2}O{sub 4} nanoparticles and reduced agglomeration in the CoFe{sub 2}O{sub 4} nanoparticles were revealed by SEM studies. The magnetic properties were studied by pulse field hysteresis loop tracer technique at a room temperature. The magnetic parameters such as saturation magnetization, remanence magnetization, coercivity etc have been obtained. These magnetic parameters were get decreased by PEG coating.« less

Studies on gallium nitride doped ferrite-polypyrrole nanocomposites

NASA Astrophysics Data System (ADS)

Indrakanti, Rajani; Brahmaji Rao, V.; Udaya Kiran, C.

2018-06-01

This communication reports the synthesis and characterisation of two novel Intrinsic conducting polymer nano composites (ICPN s) with the formulae Ga (2x+2) N Fe 2(49-x) O3—PPY synthesized using Impregnation technique. The Gallium nitride ferrite nano particles were synthesized for x = 1 and x = 5 using the above stichiometric equation earlier by Sol—Gel route. The chemical composition in the assembly of the ICPNs were Ga4NFe96O3-3%,10%,30% Polypyrrole, Ga12NFe88O3-3%,10%,30% Polypyrrole by weight. The Sci-Finder software failed to trace any earlier articles or reviews related to these ICNPs synthesised by us in the literature. X-ray Diffractometric (Structural), Morphological, EDAX SAED, IR spectroscopic characterizations were done on the synthesized nanocomposites. Structural studies reveal the semi-crystalline nature of composites. The average crystallite size of nano composites is decreased when compared with nano ferrites. SEM findings reveal that the shape for higher percentage of PPY is nano rods; for lower percentage it is globular. TEM reveals good dispersion and average particle size from histograms are calculated. The FT- IR bands of PPY and GaNFe2O3 are observed which show strong interaction between PPY- GaNFe2O3. Also there is a shift of bands in GaNFe2O3-PPY nano composites when compared to the bands of PPY.

Synthesis and Characterization of Mononuclear, Pseudotetrahedral Cobalt(III) Compounds

PubMed Central

2015-01-01

The preparation and characterization of two mononuclear cobalt(III) tropocoronand complexes, [Co(TC-5,5)](BF4) and [Co(TC-6,6)](BPh4), are reported. The cobalt(III) centers exist in rare pseudotetrahedral conformations, with twist angles of 65° and 74° for the [Co(TC-5,5]+ and [Co(TC-6,6)]+ species, respectively. Structural and electrochemical characteristics are compared with those of newly synthesized [Ga(TC-5,5)](GaCl4) and [Ga(TC-6,6)](GaCl4) analogues. The spin state of the pseudotetrahedral [Co(TC-6,6)](BPh4) compound was determined to be S = 2, a change in spin state from the value of S = 1 that occurs in the square-planar and distorted square-planar complexes, [Co(TC-3,3)](X) (X = BPh4, BAr′4) and [Co(TC-4,4)](BPh4), respectively. PMID:25531129

Dynamic Magnetostriction of CoFe2 O4 and Its Role in Magnetoelectric Composites

NASA Astrophysics Data System (ADS)

Aubert, A.; Loyau, V.; Pascal, Y.; Mazaleyrat, F.; LoBue, M.

2018-04-01

Applications of magnetostrictive materials commonly involve the use of the dynamic deformation, i.e., the piezomagnetic effect. Usually, this effect is described by the strain derivative ∂λ /∂H , which is deduced from the quasistatic magnetostrictive curve. However, the strain derivative might not be accurate to describe dynamic deformation in semihard materials as cobalt ferrite (CFO). To highlight this issue, dynamic magnetostriction measurements of cobalt ferrite are performed and compared with the strain derivative. The experiment shows that measured piezomagnetic coefficients are much lower than the strain derivative. To point out the direct application of this effect, low-frequency magnetoelectric (ME) measurements are also conducted on bilayers CFO /Pb (Zr ,Ti )O3 . The experimental data are compared with calculated magnetoelectric coefficients which include a measured dynamic coefficient and result in very low relative error (<5 %), highlighting the relevance of using a piezomagnetic coefficient derived from dynamic magnetostriction instead of a strain derivative coefficient to model ME composites. The magnetoelectric effect is then measured for several amplitudes of the alternating field Hac, and a nonlinear response is revealed. Based on these results, a trilayer CFO/Pb (Zr ,Ti )O3 /CFO is made exhibiting a high magnetoelectric coefficient of 578 mV /A (approximately 460 mV /cm Oe ) in an ac field of 38.2 kA /m (about 48 mT) at low frequency, which is 3 times higher than the measured value at 0.8 kA /m (approximately 1 mT). We discuss the viability of using semihard materials like cobalt ferrite for dynamic magnetostrictive applications such as the magnetoelectric effect.

La0.8Sr0.2Fe0.8Cu0.2O3-δ as “cobalt-free” cathode for La0.8Sr0.2Ga0.8Mg0.2O3-δ electrolyte

NASA Astrophysics Data System (ADS)

Zurlo, Francesca; Di Bartolomeo, Elisabetta; D'Epifanio, Alessandra; Felice, Valeria; Natali Sora, Isabella; Tortora, Luca; Licoccia, Silvia

2014-12-01

A "cobalt-free" cathode material with stoichiometric composition La0.8Sr0.2Fe0.8Cu0.2O3-δ (LSFCu) was specifically developed for use with La0.8Sr0.2Ga0.8Mg0.2O3-δ (LSGM) electrolyte in intermediate temperature solid oxide fuel cell (IT-SOFC) systems. The chemical stability of LSFCu in contact with LSGM electrolyte was investigated by structural and morphological analysis. The electrochemical properties of LSFCu dense pellets were investigated in the temperature range 600-750 °C by electrochemical impedance spectroscopy (EIS). LSFCu|LSGM|LSFCu symmetrical cells were prepared and area specific resistance (ASR) values, directly depending on the rate limiting step of the oxygen reduction reaction, were evaluated. Fuel cells were prepared using LSFCu as cathode material on a LSGM pellet and electrochemical tests were performed in the 700-800 °C temperature range and compared to similar fuel cells prepared by using commercial La0.6Sr0.4Fe0.8Co0.2O3-δ (LSFCo) as a cathode. The maximum current density and power density recorded for LSFCu and LSFCo were similar. This fact demonstrates that Cu can be used as Co substitute in perovskite cathode materials.

Structural and magnetic characterization of Ti doped cobalt ferrite (CoFe2O4)

NASA Astrophysics Data System (ADS)

Pal, Jaswinder; Kumar, Sunil; Kaur, Randeep; Agrawal, P.; Singh, Mandeep; Singh, Anupinder

2018-05-01

Synthesis of Co1-xTixFe2O4 solid solutions for 0.1≤x≤0.4 using the solid-state-reaction rate has been done. The prepared samples were characterized by using XRD (X-ray diffraction) and SEM (Scanning Electron Microscopy). Magnetic studies have been done using Vibrating Sample Magnetometer (VSM). XRD confirmed that Cobalt Ferrite spinel cubic structure in all prepared samples. The lattice parameter `a' increases with increase in the concentration of Ti. SEM micrograph shows good grain growth in all samples. Magnetic Study reveals that the M-H curves of all the prepared samples taken at room temperature are very well saturated. The maximum value of remnant magnetization (Mr ˜13.9 emu/g) and saturation magnetization (Ms ˜74.4 emu/g) has been observed for x =0.2 sample. Coercivity does not show any regular variation with increase in the molar concentration of Ti in CoFe2O4 at A-site.

Magnetic behaviour studies on nanocrystalline cobalt ferrite by employing the Arrott plot

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kumar, Rajnish, E-mail: rajnishiitr15@gmail.com; Kar, Manoranjan, E-mail: mano@iitp.ac.in

Vibrating Sample Magnetometer (VSM) has been used to analyze the magnetic behavior of ferrimagnetic material (CoFe{sub 2}O{sub 4}) synthesized by the citric acid modified sol-gel method. X-ray diffraction (XRD) pattern confirms the phase purity of the sample. Its magnetic measurement has been carried out at room temperature in the field range ±1.5T. The magnetocrystalline anisotropy and saturation magnetization of CoFe{sub 2}O{sub 4} are two important parameters which need to be studied for exploring its technological applications like memory device, magnetic sensors etc. Law of Approach (LA) to saturation and the Arrott plot analysis have been carried out to obtain themore » saturation magnetization. The difference in the saturation magnetization obtained from the two methods gives the qualitative understanding of magnetocrystalline anisotropy and lattice strain present in the sample. The present study explores a new way of analyzing magnetic hysteresis loop of nanocrystalline cobalt ferrite.« less

Evidence of exchange-coupled behavior in chromium-cobalt ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Tanbir, Kamar; Sharma, Lalit Kumar; Aakash; Singh, Rakesh Kumar; Choubey, Ravi Kant; Mukherjee, Samrat

2018-06-01

Cr doped cobalt ferrite nanoparticles were synthesized with the generic formula Co1-xCrxFe2O4 (x = 0, 0.05, 0.15, 0.25) through standard chemical co-precipitation method. XRD studies confirmed the pure spinel cubic structure belonging to Fd 3 bar m space group. From the Williamson-Hall plots, crystallite sizes were found to lie within the range (42 ± 1) nm for the different doped samples. The lattice parameter was found to decrease linearly with increase in the concentration of Cr3+ ion. The magnetic behavior of the samples was determined by M-H studies at 300 K, field cooled (5 T) at 5 K and temperature dependent studies. The M-H at 300 K show soft magnetic behavior whereas the M-H plots at 5 K predict the existence of in-homogeneity of the exchange interactions due to strong exchange coupling between the spins at the core and the surface of the nanoparticles.

Influence of Cobalt Substitution on the Magnetic Properties of Fe5PB2.

PubMed

Cedervall, Johan; Nonnet, Elise; Hedlund, Daniel; Häggström, Lennart; Ericsson, Tore; Werwiński, Mirosław; Edström, Alexander; Rusz, Ján; Svedlindh, Peter; Gunnarsson, Klas; Sahlberg, Martin

2018-01-16

The substitutional effects of cobalt in (Fe 1-x Co x ) 5 PB 2 have been studied with respect to crystalline structure and chemical order with X-ray diffraction and Mössbauer spectroscopy. The magnetic properties have been determined from magnetic measurements, and density functional theory calculations have been performed for the magnetic properties of both the end compounds, as well as the chemically disordered intermediate compounds. The crystal structure of (Fe 1-x Co x ) 5 PB 2 is tetragonal (space group I4/mcm) with two different metal sites, with a preference for cobalt atoms in the M(2) position (4c) at higher cobalt contents. The substitution also affects the magnetic properties with a decrease of the Curie temperature (T C ) with increasing cobalt content, from 622 to 152 K for Fe 5 PB 2 and (Fe 0.3 Co 0.7 ) 5 PB 2 , respectively. Thus, the Curie temperature is dependent on composition, and it is possible to tune T C to a temperature near room temperature, which is one prerequisite for magnetic cooling materials.

Glassy behavior of diluted Cu-Zn ferrites

NASA Astrophysics Data System (ADS)

Akhter, Shahida; Hakim, M. A.; Hoque, S. M.; Mathieu, R.; Nordblad, P.

2018-04-01

The magnetic behavior of Zn substituted Cu-Zn spinel ferrites having chemical formula Cu1-xZnxFe2O4 (x = 0.7, 0.8, 0.9 and 1.0) has been studied by SQUID magnetometry, by means of magnetic hysteresis, field-cooled (FC) and zero-field-cooled (ZFC) magnetization, memory effect and low field ac susceptibility measurements. These measurements suggest that the ferrimagnetic phase of the x ≤ 0.8 samples is gradually turned into a spin glass (x ≥ 0.9). The compound with x = 0.9 exhibits the typical dynamical behavior of spin glasses, with indication of aging, rejuvenation and memory effects. The evolution of the magnetic properties of Cu-Zn spinel ferrites with substitution of Zn for Cu is discussed.

Design and installation of a ferromagnetic wall in tokamak geometry

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hughes, P. E., E-mail: peh2109@columbia.edu; Levesque, J. P.; Rivera, N.

Low-activation ferritic steels are leading material candidates for use in next-generation fusion development experiments such as a prospective component test facility and DEMO power reactor. Understanding the interaction of plasmas with a ferromagnetic wall will provide crucial physics for these facilities. In order to study ferromagnetic effects in toroidal geometry, a ferritic wall upgrade was designed and installed in the High Beta Tokamak–Extended Pulse (HBT-EP). Several material options were investigated based on conductivity, magnetic permeability, vacuum compatibility, and other criteria, and the material of choice (high-cobalt steel) is characterized. Installation was accomplished quickly, with minimal impact on existing diagnostics andmore » overall machine performance, and initial results demonstrate the effects of the ferritic wall on plasma stability.« less

Tunable microwave absorbing nano-material for X-band applications

NASA Astrophysics Data System (ADS)

Sadiq, Imran; Naseem, Shahzad; Ashiq, Muhammad Naeem; Khan, M. A.; Niaz, Shanawer; Rana, M. U.

2016-03-01

The effect of rare earth elements substitution in Sr1.96RE0.04Co2Fe27.80Mn0.2O46 (RE=Ce, Gd, Nd, La and Sm) X-type hexagonal ferrites prepared by using sol gel autocombustion method was studied. The XRD and FTIR analysis show the single phase of the prepared material. The lattice constants a (Å) and c (Å) varies with the additives. The particle size measured by Scherer formula for all the samples varies in the range of 54-100 nm and confirmed by the TEM analysis. The average grain size measured by SEM analysis lies in the range of 0.672-1.01 μm for all the samples. The Gd-substituted ferrite has higher value of coercivity (526.06 G) among all the samples which could be a good material for longitudinal recording media. The results also indicate that the Gd-substituted sample has maximum reflection loss of -25.2 dB at 11.878 GHz, can exhibit the best microwave absorption properties among all the substituted samples. Furthermore, the minimum value of reflection loss shifts towards the lower and higher frequencies with the substitution of rare earth elements which confirms that the microwave absorption properties can be tuned with the substitution of rare earth elements in pure ferrites. The peak value of attenuation constant at higher frequency agrees well the reflection loss data.

High temperature dissolution of chromium substituted nickel ferrite in nitrilotriacetic acid medium

NASA Astrophysics Data System (ADS)

Sathyaseelan, V. S.; Chandramohan, P.; Velmurugan, S.

2016-12-01

High temperature (HT) dissolution of chromium substituted nickel ferrite was carried out with relevance to the decontamination of nuclear reactors by way of chemical dissolution of contaminated corrosion product oxides present on stainless steel coolant circuit surfaces. Chromium substituted nickel ferrites of composition, NiFe(2-x)CrxO4 (x ≤ 1), was synthetically prepared and characterized. HT dissolution of these oxides was carried out in nitrilotriacetic acid medium at 160 °C. Dissolution was remarkably increased at 160 °C when compared to at 85 °C in a reducing decontamination formulation. Complete dissolution could be achieved for the oxides with chromium content 0 and 0.2. Increasing the chromium content brought about a marked reduction in the dissolution rate. About 40 fold decrease in rate of dissolution was observed when chromium was increased from 0 to 1. The rate of dissolution was not very significantly reduced in the presence of N2H4. Dissolution of oxide was found to be stoichiometric.

Influence of reagents mixture density on the radiation-thermal synthesis of lithium-zinc ferrites

NASA Astrophysics Data System (ADS)

Surzhikov, A. P.; Lysenko, E. N.; Vlasov, V. A.; Malyshev, A. V.; Korobeynikov, M. V.; Mikhailenko, M. A.

2017-01-01

Influence of Li2CO3-ZnO-Fe2O3 powder reagents mixture density on the synthesis efficiency of lithium-zinc ferrites in the conditions of thermal heating or pulsed electron beam heating was studied by X-Ray diffraction and magnetization analysis. The results showed that the including a compaction of powder reagents mixture in ferrite synthesis leads to an increase in concentration of the spinel phase and decrease in initial components content in lithium-substituted ferrites synthesized by thermal or radiation-thermal heating.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kantor, M. M., E-mail: Kantor@imet.ac.ru; Vorkachev, K. G., E-mail: KGV@imet.ac.ru

The efficiency of different techniques application for the investigation of orientation inhomogeneities in polycrystalline materials was studied using FEG SEM-FIB dual beam station equipped with EBSD. It is shown that for the visualization of pearlitic ferrite fragments it is more appropriate to acquire the images in secondary electrons induced by Ga ions. At the same time for the visualization of nano-sized particles it is more prospective to use images in forward scatter electrons in combination with IQ maps. It is established that pearlitic ferrite fragments are not flat. Complicated spatial configuration of orientation inhomogeneities in pearlitic ferrite is shown bymore » means of 3-d reconstruction. The features of ferrites aggregation are revealed depending on pearlitic ferrite fragmentation criterion. The existence of long-range misorientations in the aggregation area of proeutectoid and pearlitic ferrites is shown.« less

The substitution of nickel for cobalt in hot isostatically pressed powder metallurgy UDIMET 700 alloys

NASA Technical Reports Server (NTRS)

Harf, F. H.

1985-01-01

Nickel was substituted in various proportions for cobalt in a series of five hot-isostatically-pressed powder metallurgy alloys based on the UDIMET 700 composition. These alloys were given 5-step heat treatments appropriate for use in turbine engine disks. The resultant microstructures displayed three distinct sizes of gamma-prime particles in a gamma matrix. The higher cobalt-content alloys contained larger amounts of the finest gamma-prime particles, and had the lowest gamma-gamma-prime lattice mismatch. While all alloys had approximately the same tensile properties at 25 and 650 gamma C, the rupture lives at 650 and 760 C peaked in the alloys with cobalt contents between 12.7 and 4.3 pct. Minimum creep rates increased as cobalt contents were lowered, suggesting their correlation with the gamma-prime particle size distribution and the gamma-gamma-prime mismatch. It was also found that, on overaging at temperatures higher than suitable for turbine disk use, the high cobalt-content alloys were prone to sigma phase formation.

Comparative study of synthesis, structural and magnetic properties of Cu2+ substituted Co-Ni, Co-Zn and Co-Mg nano ferrites

NASA Astrophysics Data System (ADS)

Ramakrishna, A.; Murali, N.; Margarette, S. J.; Samatha, K.; Veeraiah, V.

2018-02-01

Mixed ferrites of the form Co0.5M0.1Cu0.4Fe2O4 (M = Ni, Zn and Mg) have been synthesized using the sol-gel auto combustion technique. Structural analyses are carried out using powder X-ray diffraction to idntify pure ferrite phases. SEM analysis revealed clear crystal morphology with relatively uniform grain sizes with polygonal structures. The FT-IR studies also confirm the bond formation and cation vibrations at low (365-392 cm-1) and high (579-587 cm-1) bands that correspond to the tetrahedral and octahedral sites, respectively. The magnetic properties studied through vibrating sample magnetometer showed that the Ni substituted sample has more magnetic character by exhibiting the highest saturation magnetization.

Influence of Sn4+ on Structural and DC Electrical Resistivity of Ni-Zn Ferrite Thick Films

NASA Astrophysics Data System (ADS)

Dalawai, S. P.; Shinde, T. J.; Gadkari, A. B.; Tarwal, N. L.; Jang, J. H.; Vasambekar, P. N.

2017-03-01

Among the soft ferrites, Ni-Zn ferrite is one of the most versatile ceramic materials because of their important electrical and magnetic properties. These properties were improved by substituting Sn4+ in Ni-Zn ferrites with chemical composition of Ni x Zn1+ y- x Fe2-2 y Sn y O4 ( x = 0, 0.2, 0.4, 0.6, 0.8, 1.0; y = 0.1, 0.2). To achieve homogenous ferrite powder at lower sintering temperature and smaller duration in nano-size form, the oxalate co-precipitation method was preferred as compared to other physical and chemical methods. Using this powder, ferrite thick films (FTFs) were prepared by the screen printing technique because of its low cost and easy use. To study structural behavior, the FTFs were characterized by different techniques. The x-ray diffraction and thermo-gravimetric and differential thermal analysis studies show the formation of cubic spinel structure and ferrite phase formation, respectively. There is no remarkable trend observed in lattice constants for the Sn4+ ( y = 0.1)- and Sn4+ ( y = 0.2)-substituted Ni-Zn ferrites. The bond lengths as well as ionic radii on the A-site of Ni-Zn-Sn ferrites were found to decrease with increasing nickel content. The bond length and ionic radii on the B-sites remained almost constant for Sn4+ ( y = 0.1, 0.2)-substituted Ni-Zn ferrites. The energy dispersive x-ray analysis confirms the elemental analysis of FTFs. The Fourier transform infrared spectra show two major absorption bands near 400 cm-1 and 600 cm-1 corresponding to octahedral and tetrahedral sites, respectively, which also confirms the formation of the ferrites. The field emission scanning electron microscopy images shows that the particles are highly porous in nature and located in loosely packed agglomerates. The average particle size of the FTFs lies in the range 20-60 nm. Direct current (DC) resistivity of Ni-Zn-Sn FTFs shows the semiconductor nature. The DC resistivity of Ni-Zn-Sn0.2FTFs is lower than Ni-Zn-Sn0.1 FTFs. The DC resistivity is found to decrease with the increase in Ni2+ content up to x = 0.6. It increases thereafter for a further increase in Ni2+ content up to x = 1.0, and a similar trend is observed for the variations of activation energy with Ni2+ content.

Bulk Single Crystal-Like Structural and Magnetic Characteristics of Epitaxial Spinel Ferrite Thin Films with Elimination of Antiphase Boundaries.

PubMed

Singh, Amit V; Khodadadi, Behrouz; Mohammadi, Jamileh Beik; Keshavarz, Sahar; Mewes, Tim; Negi, Devendra Singh; Datta, Ranjan; Galazka, Zbigniew; Uecker, Reinhard; Gupta, Arunava

2017-08-01

Spinel ferrite NiFe 2 O 4 thin films have been grown on three isostructural substrates, MgAl 2 O 4 , MgGa 2 O 4 , and CoGa 2 O 4 using pulsed laser deposition. These substrates have lattice mismatches of 3.1%, 0.8%, and 0.2%, respectively, with NiFe 2 O 4 . As expected, the films grown on MgAl 2 O 4 substrate show the presence of the antiphase boundary defects. However, no antiphase boundaries (APBs) are observed for films grown on near-lattice-matched substrates MgGa 2 O 4 and CoGa 2 O 4 . This demonstrates that by using isostructural and lattice-matched substrates, the formation of APBs can be avoided in NiFe 2 O 4 thin films. Consequently, static and dynamic magnetic properties comparable with the bulk can be realized. Initial results indicate similar improvements in film quality and magnetic properties due to the elimination of APBs in other members of the spinel ferrite family, such as Fe 3 O 4 and CoFe 2 O 4 , which have similar crystallographic structure and lattice constants as NiFe 2 O 4 . © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Further Charpy impact test results of low activation ferritic alloys, irradiated at 430{degrees}C to 67 dpa

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schubert, L.E.; Hamilton, M.L.; Gelles, D.S.

1997-04-01

Miniature CVN specimens of four ferritic alloys, GA3X, F82H, GA4X and HT9, have been impact tested following irradiation at 430{degrees}C to 67 dpa. Comparison of the results with those of the previously tested lower dose irradiation condition indicates that the GA3X and F82H alloys, two primary candidate low activation alloys, exhibit virtually identical behavior following irradiation at 430{degrees}C to {approximately}67 dpa and at 370{degrees}C to {approximately}15 dpa. Very little shift is observed in either DBTT or USE relative to the unirradiated condition. The shifts in DBTT and USE observed in both GA4X and HT9 were smaller after irradiation at 430{degrees}Cmore » to {approximately}67 dpa than after irradiation at 370{degrees}C to {approximately}15 dpa.« less

Effect of lanthanum substitution on structural and magnetic properties of nickel zinc ferrites

NASA Astrophysics Data System (ADS)

Šoka, Martin; Ušáková, Mariana; Dosoudil, Rastislav; Ušák, Elemír; Lokaj, Ján

2018-04-01

The purpose of the presented research is to investigate the effect of La3+ ions substitution for Fe3+ ions in Ni0.42Zn0.58LaxFe2-xO4 (x = 0, 0.02, 0.04, 0.06, 0.08, 0.10) ferrite compositions prepared by the innovated glycine-nitrate process based on auto-combustion method. Structural and magnetic properties of examined samples were estimated by the analysis of X-ray spectra, EDAX spectrum, SEM micrographs, thermomagnetic characteristics, magnetic hysteresis loops and complex permeability spectra.

Dielectric and magnetic behavior of nanocrystalline Cu{sub 0.4}Co{sub 0.6}Fe{sub 2}O{sub 4} ferrite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jadoun, Priya, E-mail: priya4jadoun@gmail.com; Sharma, Jyoti; Prashant, B. L.

2016-05-23

The mixed copper cobalt ferrite nanoparticles (Cu{sub 0.4}Co{sub 0.6}Fe{sub 2}O{sub 4}) have been synthesized by sol-gel auto combustion route with aqueous metal nitrates and citric acid as the precursor. The crystal structure has been analyzed by X-Ray diffraction (XRD) method. XRD reveals the formation of single phase cubic spinel structure. The Scanning Electron Microscopy (SEM) is used for morphological studies. The dielectric measurements at room temperature show the decrease in dielectric constant with increasing frequency which is attributed to Maxwell Wagner model and conduction mechanism in ferrites.The magnetic measurements show ferromagnetic behavior at room temperature and large coercivity is observedmore » on cooling down the temperature to 20 K.« less

A facile microwave synthetic route for ferrite nanoparticles with direct impact in magnetic particle hyperthermia.

PubMed

Makridis, A; Chatzitheodorou, I; Topouridou, K; Yavropoulou, M P; Angelakeris, M; Dendrinou-Samara, C

2016-06-01

The application of ferrite magnetic nanoparticles (MNPs) in medicine finds its rapidly developing emphasis on heating mediators for magnetic hyperthermia, the ever-promising "fourth leg" of cancer treatment. Usage of MNPs depends largely on the preparation processes to select optimal conditions and effective routes to finely tailor MNPs. Microwave heating, instead of conventional heating offers nanocrystals at significantly enhanced rate and yield. In this work, a facile mass-production microwave hydrothermal synthetic approach was used to synthesize stable ferromagnetic manganese and cobalt ferrite nanoparticles with sizes smaller than 14 nm from metal acetylacetonates in the presence of octadecylamine. Prolonging the reaction time from 15 to 60 min, led to ferrites with improved crystallinity while the sizes are slight increased. The high crystallinity magnetic nanoparticles showed exceptional magnetic heating parameters. In vitro application was performed using the human osteosarcoma cell line Saos-2 incubated with manganese ferrite nanoparticles. Hyperthermia applied in a two cycle process, while AC magnetic field remained on until the upper limit of 45 °C was achieved. The comparative results of the AC hyperthermia efficiency of ferrite nanoparticles in combination with the in vitro study coincide with the magnetic features and their tunability may be further exploited for AC magnetic hyperthermia driven applications. Copyright © 2016 Elsevier B.V. All rights reserved.

Effects of the synthesis temperature on the crystalline structure and the magnetic properties of cobalt ferrite nanoparticles prepared via coprecipitation

NASA Astrophysics Data System (ADS)

Hutamaningtyas, Evangelin; Utari; Suharyana; Purnama, Budi; Wijayanta, Agung Tri

2016-08-01

The effects of the synthesis temperature on the crystalline structure and the magnetic properties of cobalt ferrite (CoFe2O4) nanoparticles prepared via coprecipitation are discussed. The synthesis was conducted at temperatures of 75 °C, 85 °C and 95 °C. Fourier transform infrared spectroscopy characterization related to a stretching vibration at a wavenumber of 590 cm-1 indicated the formation of a CoFe2O4 metal oxide. In addition, powder X ray diffraction (XRD) characterization proved that the metal oxide was CoFe2O4. Crystallite sizes calculated using the Scherer formula at the strongest peak of the XRD spectra of the samples synthesized at 75 °C, 85 °C and 95 °C were 32 nm, 43 nm and 50.4 nm, respectively. Finally, the results of the vibrating sample magnetometer characterization showed that the saturation magnetization decreased with increasing synthesis temperature, which is related to the dominant preference of Co2+ over Fe3+ cations at the octahedral sites.

Stabilization of scandium rich spinel ferrite CoFe{sub 2−x}Sc{sub x}O{sub 4} (x≤1) in thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lefevre, Christophe, E-mail: christophe.lefevre@ipcms.unistra.fr; Roulland, François; Thomasson, Alexandre

2015-12-15

Scandium rich cobalt ferrites Co{sub y}Fe{sub 3−x−y}Sc{sub x}O{sub 4} with y~1 never obtained in bulk could be stabilized in pulsed laser deposited thin films. Scandium contents of up to x=1 are reached. The cell parameter increases versus x as awaited when considering the size of scandium. It is equal to 0.8620 nm for x=1, significantly higher than that of CoFe{sub 2}O{sub 4} (0.8396 nm). The lattice mismatch between the MgO (100) substrate and the scandium-containing spinel leads to an increased roughness. Cobalt is displaced from the octahedral site by Sc and mainly occupies the tetrahedral sites for high x values.more » - Graphical abstract: Magnification of the XRD patterns recorded on thin films of CoFe{sub 2-x}Sc{sub x}O{sub 4} for x=0, 0.45, 1 and 1.2, the arrows denote the (004) and (008) diffraction lines of the spinel phase.« less

The Influence of Fe Substitution in Lanthanum Calcium Cobalt Oxide on the Oxygen Evolution Reaction in Alkaline Media

DOE PAGES

Abreu-Sepulveda, Maria A.; Dhital, Chetan; Huq, Ashfia; ...

2016-07-30

The effect due to systematic substitution of cobalt by iron in La 0.6Ca 0.4Co 1-xFe xO 3 towards the oxygen evolution reaction(OER) in alkaline media has been investigated. We synthesized these compounds by a facile glycine-nitrate synthesis and the phase formation was confirmed by X-ray diffraction and Neutron Diffraction elemental analysis. The apparent OER activity was evaluated by quasi steady state current measurements in alkaline media using a traditional three-electrode cell. X-ray photoelectron spectroscopy shows iron substitution causes an increase in the surface concentration of various cobalt oxidation states. Tafel slope in the vicinity of 60 mV/decade and electrochemical reactionmore » order towards OH- near unity were achieved for the unsubstituted La 0.6Ca 0.4CoO 3. Moreover, a decrease in the Tafel slope to 49 mV/decade was observed when iron is substituted in high amounts in the perovskite structure. The area specific current density showed dependence on the Fe fraction, however the relationship of specific current density with Fe fraction is not linear. High Fe substitutions, La 0.6Ca 0.4Co 0.2Fe 0.8O 3 and La 0.6Ca 0.4Co 0.1Fe 0.9O 3 showed higher area specific activity towards OER than La 0.6Ca 0.4CoO 3 or La 0.6Ca 0.4FeO 3. Finally, we believe iron inclusion in the cobalt sites of the perovskite helps decrease the electron transfer barrier and facilitates the formation of cobalt-hydroxide at the surface. Possible OER mechanisms based on the observed kinetic parameters will be discussed.« less

Modulation of magnetic interaction in Bismuth ferrite through strain and spin cycloid engineering

NASA Astrophysics Data System (ADS)

Yadav, Rama Shanker; Reshi, Hilal Ahmad; Pillai, Shreeja; Rana, D. S.; Shelke, Vilas

2016-12-01

Bismuth ferrite, a widely studied room temperature multiferroic, provides new horizons of multifunctional behavior in phase transited bulk and thin film forms. Bismuth ferrite thin films were deposited on lattice mismatched LaAlO3 substrate using pulsed laser deposition technique. X-ray diffraction confirmed nearly tetragonal (T-type) phase of thin film involving role of substrate induced strain. The film thickness of 56 nm was determined by X-ray reflectivity measurement. The perfect coherence and epitaxial nature of T- type film was observed through reciprocal space mapping. The room temperature Raman measurement of T-type bismuth ferrite thin film also verified phase transition with appearance of only few modes. In parallel, concomitant La and Al substituted Bi1-xLaxFe0.95Al0.05O3 (x = 0.1, 0.2, 0.3) bulk samples were synthesized using solid state reaction method. A structural phase transition into orthorhombic (Pnma) phase at x = 0.3 was observed. The structural distortion at x = 0.1, 0.2 and phase transition at x = 0.3 substituted samples were also confirmed by changes in Raman active modes. The remnant magnetization moment of 0.199 emu/gm and 0.28 emu/gm were observed for x = 0.2 and 0.3 bulk sample respectively. The T-type bismuth ferrite thin film also showed high remnant magnetization of around 20emu/cc. The parallelism in magnetic behavior between T-type thin film and concomitant La and Al substituted bulk samples is indication of modulation, frustration and break in continuity of spiral spin cycloid.

Spinel Ferrite Core–Shell Nanostructures by a Versatile Solvothermal Seed-Mediated Growth Approach and Study of Their Nanointerfaces

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sanna Angotzi, Marco; Musinu, Anna; Mameli, Valentina

An easy, low-cost, repeatable seed-mediated growth approach in solvothermal condition has been proposed to synthesize bimagnetic spinel ferrite core–shell heterostructures in the 10–20 nm particle size range. Cobalt ferrite and manganese ferrite nanoparticles (CoFe 2O 4 and MnFe 2O 4) have been coated with isostructural spinel ferrites like maghemite/magnetite, MnFe 2O 4, and CoFe 2O 4 with similar cell parameters to create different heterostructures. The conventional study of the structure, morphology, and composition has been combined with advanced techniques in order to achieve details on the interface at the nanoscale level. Clear evidence of the heterostructure formation have been obtainedmore » (i) indirectly by comparing the 57Fe Mössbauer spectra of the core–shell samples and an ad hoc mechanical mixture and (ii) directly by mapping the nanoparticles’ chemical composition by electron energy loss spectroscopy (EELS) and energy-dispersive X-ray spectroscopy (EDX) in the scanning transmission electron microscopy mode (STEM). Additionally, chemical-sensitive electron tomography in STEM-EDX mode has been applied in order to obtain detailed 3D images with a sub-nanometer spatial resolution.« less

Spinel Ferrite Core–Shell Nanostructures by a Versatile Solvothermal Seed-Mediated Growth Approach and Study of Their Nanointerfaces

DOE PAGES

Sanna Angotzi, Marco; Musinu, Anna; Mameli, Valentina; ...

2017-07-23

An easy, low-cost, repeatable seed-mediated growth approach in solvothermal condition has been proposed to synthesize bimagnetic spinel ferrite core–shell heterostructures in the 10–20 nm particle size range. Cobalt ferrite and manganese ferrite nanoparticles (CoFe 2O 4 and MnFe 2O 4) have been coated with isostructural spinel ferrites like maghemite/magnetite, MnFe 2O 4, and CoFe 2O 4 with similar cell parameters to create different heterostructures. The conventional study of the structure, morphology, and composition has been combined with advanced techniques in order to achieve details on the interface at the nanoscale level. Clear evidence of the heterostructure formation have been obtainedmore » (i) indirectly by comparing the 57Fe Mössbauer spectra of the core–shell samples and an ad hoc mechanical mixture and (ii) directly by mapping the nanoparticles’ chemical composition by electron energy loss spectroscopy (EELS) and energy-dispersive X-ray spectroscopy (EDX) in the scanning transmission electron microscopy mode (STEM). Additionally, chemical-sensitive electron tomography in STEM-EDX mode has been applied in order to obtain detailed 3D images with a sub-nanometer spatial resolution.« less

Magneto-structural studies of sol-gel synthesized nanocrystalline manganese substituted nickel ferrites

NASA Astrophysics Data System (ADS)

Pandav, R. S.; Patil, R. P.; Chavan, S. S.; Mulla, I. S.; Hankare, P. P.

2016-11-01

Nanocrystalline NiFe2-xMnxO4 (2≥x≥0) ferrites were prepared by sol-gel method. X-ray diffraction patterns reveal that synthesized compounds are in single phase cubic spinel lattice for all the composition. The surface morphology of all the samples were studied by scanning electron microscopy. The particle size measured from transmission electron microscopy and X-ray diffraction patterns confirms the nanosized dimension of the as-prepared powder. The elemental analysis was carried out by energy dispersive X-ray analysis technique. Magnetic properties such as saturation magnetization, coercivity and remanence are studied as a function of increasing Mn concentration at room temperature. The saturation magnetization shows a decreasing trend with increase in Mn content. The substitution of manganese in the nickel ferrite affects the structural and magnetic properties of cubic spinels.

Influence of Cu-Cr substitution on structural, morphological, electrical and magnetic properties of magnesium ferrite

NASA Astrophysics Data System (ADS)

Yonatan Mulushoa, S.; Murali, N.; Tulu Wegayehu, M.; Margarette, S. J.; Samatha, K.

2018-03-01

Cu-Cr substituted magnesium ferrite materials (Mg1 - xCuxCrxFe21 - xO4 with x = 0.0-0.7) have been synthesized by the solid state reaction method. XRD analysis revealed the prepared samples are cubic spinel with single phase face centered cubic. A significant decrease of ∼41.15 nm in particle size is noted in response to the increase in Cu-Cr substitution level. The room temperature resistivity increases gradually from 0.553 × 105 Ω cm (x = 0.0) to 0.105 × 108 Ω cm (x = 0.7). Temperature dependent DC-electrical resistivity of all the samples, exhibits semiconductor like behavior. Cu-Cr doped materials can be suitable to limit the eddy current losses. VSM result shows pure and doped magnesium ferrite particles show soft ferrimagnetic nature at room temperature. The saturation magnetization of the samples decreases initially from 34.5214 emu/g for x = 0.0 to 18.98 emu/g (x = 0.7). Saturation magnetization, remanence and coercivity are decreased with doping, which may be due to the increase in grain size.

Co0.6Zn0.4Cu0.2CdxFe1.8-xO4 (0.2 ⩽ x ⩽ 0.8) magnetic ferrite nano-particle: Synthesis, characterization and photo-catalytic degradation of methyl orange

NASA Astrophysics Data System (ADS)

Bhukal, Santosh; Bansal, S.; Singhal, Sonal

2014-02-01

Cd2+ ion substituted nano-crystalline cobalt-zinc ferrites having chemical formula Co0.6Zn0.4Cu0.2CdxFe1.8-xO4 (x = 0.2, 0.4, 0.6 and 0.8) have been prepared using sol-gel auto-combustion method. The X-ray diffraction analysis confirmed the crystalline structure and phase purity of all the prepared nano-ferrites. The lattice constant was found to vary linearly from 8.360 Å to 8.390 Å for cadmium ion concentration from 0.2 to 0.8 in accordance with Vegard's law. Ionic radii of tetrahedral site (rA) and octahedral site (rB) was found to increase with increase in the cadmium ion concentration because of larger size of Cd2+ ion (0.97 Å) as compared to that of Fe3+ ion (0.67 Å). Vibrating sample magnetometer (VSM) results revealed that the saturation magnetization, coercivity and anisotropy constant decrease with increase in the cadmium concentration. The distribution of cations among A and B sites of the lattice was estimated by the magnetic moments which were calculated from the magnetic data. Moreover resistivity was found to be decrease with increase in the cadmium concentration. There was increase in drift mobility with increase in temperature because of the enhanced mobility of charge carriers due to thermal activation. Co0.6Zn0.4Cu0.2CdxFe1.8-xO4 showed good catalytic activity towards methyl orange and easily recovered by magnetic separation after the reaction. The photo-catalytic degradation was enhanced as the concentration of cadmium ion increased from 0.2 to 0.8 may be due to decrease in band gap with increase in Cd2+ ion concentration.

Improvement of the Coercivity of Cobalt Ferrites Induced by Substitution of Sr2+ Ions for Co2+ Ions

NASA Astrophysics Data System (ADS)

Zhou, Kaiwen; Chen, Wen; Wu, Xuehang; Wu, Wenwei; Lin, Cuiwu; Wu, Juan

2017-07-01

Spinel Co1- x Sr x Fe2O4 ( x = 0.0, 0.1, 0.2, and 0.3) ferrites have been successfully synthesized by calcining a mixture of oxalates in air. X-ray diffraction study shows that the sample with the concentration of x = 0 has a single spinel phase CoFe2O4 structure and the samples with concentrations of x = 0.1-0.3 have a small amount of foreign phase SrFe12O19 and/or Sr7Fe10O22 along the spinel phase. The lattice parameter of the ferrites at first increases with increasing Sr2+ content, then decreases to x = 0.3 due to the large ionic radius of Sr2+ (0.144 nm) as compared to Co2+ (0.072 nm); for higher doping levels, part of the Sr2+ ions could not enter the tetrahedral (A) and/or octahedral (B) sites but forms a second phase Sr7Fe10O22. The addition of Sr2+ ions decreases the average crystallite size of Co1- x Sr x Fe2O4, which is attributed to the foreign phase Sr7Fe10O22 and/or SrFe12O19 restraining the growth of the Co1- x Sr x Fe2O4 crystallite. The trend of specific saturation magnetization ( Ms), remanence ( Mr), and anisotropy constant ( K eff) decreases with the increase in Sr2+ content, whereas that of coercivity is increased. In this study, Co0.8Sr0.2Fe2O4 obtained at 800°C exhibits the highest coercivity (1699.25 ± 40.78 Oe), and Co0.7Sr0.3Fe2O4 obtained at 900°C exhibits the highest squareness (0.470 ± 0.008).

Structural and physical property study of sol-gel synthesized CoFe2-xHoxO4 nano ferrites

NASA Astrophysics Data System (ADS)

Patankar, K. K.; Ghone, D. M.; Mathe, V. L.; Kaushik, S. D.

2018-05-01

CoFe2-xHoxO4 (x = 0.00, 0.05, 0.10, 0.15, 0.20) ferrites were prepared by the suitably modified Sol-Gel technique. X-ray diffraction (XRD) analysis revealed that the substituted samples show phase pure formation till 10% substitution, which is far higher phase pure than the earlier reports. Upon further substitution an inevitable secondary phase of HoFeO3 along with the spinel phase despite regulating synthesis parameters in the sol-gel reaction route. These results are further corroborated more convincingly by room temperature neutron diffraction. Morphological features of the ferrites were studied by Scanning Electron Microscopy (SEM). The magnetic parameters viz. the saturation magnetization (Ms), coercivity (Hc) and remanence (Mr) were determined from room temperature isothermal magnetization. These parameters were found to decrease with increase in Ho substitution. The decrease in magnetization is analyzed in the light of exchange interactions between rare earth and transition metal ions. Magnetostriction measurements revealed interesting results and the presence of a secondary phase was found to be responsible for decreased measu-red magnetostriction values. The solubility limit of Ho in CoFe2O4 lattice is also reflected from the X-ray and neutron diffraction analysis and magnetostriction studies.

Influence of cobalt doping on structural and magnetic properties of BiFeO3 nanoparticles

NASA Astrophysics Data System (ADS)

Khan, U.; Adeela, N.; Javed, K.; Riaz, S.; Ali, H.; Iqbal, M.; Han, X. F.; Naseem, S.

2015-11-01

Nanocrystalline cobalt-doped bismuth ferrites with general formula of BiFe1- δ Co δ O3 (0 ≤ δ ≤ 0.1) have been synthesized using solution evaporation method. Structure and phase identification was performed with X-ray diffraction (XRD) technique. The results confirm the formation of rhombohedral-distorted Perovskite structure with R3c symmetry. A decrease in lattice parameters and an increase in X-ray density have been observed with increasing cobalt concentration in BiFeO3. Particle size determined by transmission electron microscope was in good agreement with XRD, i.e., 39 nm. Room-temperature coercivity and saturation magnetization of nanoparticles were increased up to 7.5 % of cobalt doping. Low-temperature magnetic measurements of selected sample showed increasing behavior in saturation magnetization, coercivity, effective magnetic moments, and anisotropy constant. An increase in coercivity with decrease in temperature followed theoretical model of Kneller's law, while modified Bloch's model was employed for saturation magnetization in temperature range of 5-300 K.

Structural and electrical properties of nickel substituted cadmium ferrite

NASA Astrophysics Data System (ADS)

Chethan, B.; Raj Prakash, H. G.; Vijayakumari, S. C.; Ravikiran, Y. T.

2018-05-01

Spinal nano-sized Cadmium ferrite (CD) and Nickel substituted cadmium ferrite (NSCF) were fabricated by sol-gel auto combustion method. The formation of spinal structure of ferrite materials was confirmed by X-ray diffraction (XRD) analysis. The crystallites size of CF and NSCF as determined by Scherrer's formula were found to be 24.73 nm and 17.70 nm respectively. comparative study of Fourier transform infrared spectroscopy (FTIR) of CF and NSCF revealed tetrahedral absorption bands shifted slightly towards higher frequency where as octahedral bands shifted towards lower frequency side confirming interfacial interaction between Ni and CF. The AC conductivity (σ), loss tangent (tan δ) and complex plane impedance plots for both CF and NSCF are determined at various frequencies ranging from 50 kHz to 5 MHz and comparatively analyzed. The increase in AC conductivity of the NSCF nano particles as compared to CF was explained in the light of hopping model. The impedance measurement of NSCF show presence of a semi-circle corresponding to the grain boundary resistance and hence shows that the conductivity takes place largely through grain boundaries.

Electrical Properties and Dipole Relaxation Behavior of Zinc-Substituted Cobalt Ferrite

NASA Astrophysics Data System (ADS)

Supriya, Sweety; Kumar, Sunil; Kar, Manoranjan

2017-12-01

Co1- x Zn x Fe2O4 ceramics with x = 0.00, 0.05, 0.10, 0.15 and 0.20 were synthesized by a modified citric acid sol-gel method. The crystalline phase of the samples was characterized by the powder x-ray diffraction technique (XRD) and the Rietveld analysis of the XRD patterns. The morphology and particle size were studied using field emission scanning electron microscopy. Fourier transform infrared spectroscopy studies were consistent with the XRD results. The impedance measurements were carried out from 100 Hz to 10 MHz at different temperatures from 40°C to 300°C. The frequency dispersion of dielectric was analyzed with a modified Debye equation. The activation energy derived from the dielectric constant and the impedance follows the Arrhenius law and are comparable with each other. The dielectric relaxation and impedance relaxation are correlated in terms of activation energy, show a good temperature stability of the dielectrics and are useful for their applications in microelectronic devices such as filters, capacitors, resonators, etc.

Effect of Mn2+ doping on structural, electrical transport and dielectric properties of CoFe2O4 nanoparticles

NASA Astrophysics Data System (ADS)

Ansari, Mohd Mohsin Nizam; Khan, Shakeel; Bhargava, Richa; Ahmad, Naseem

2018-05-01

Manganese substituted cobalt ferrites, Co1-xMnxFe2O4 (0.0, 0.1, 0.2, 0.3 and 0.4) were successfully synthesized by sol-gel method. XRD analysis confirmed the formation of a single-phase cubic spinel structures having Fd-3m space group and crystallite size is found to be in the range of 12.9 - 15.5 nm. The lattice parameter increased from 8.4109 Å to 8.4531 Å with increasing Mn2+ ion doping. Dielectric constant (ɛ'), dielectric loss (tanδ) and ac conductivity (σac) were analyzed at room temperature as a function of frequency (42 Hz to 5 MHz) and the behavior is explained on the basis of Maxwell-Wagner interfacial polarization. DC electrical resistivity measurements were carried out by two-probe method. DC electrical resistivity decreases with increase in temperature confirms the semiconducting nature of the samples. Impedance spectroscopy method has been used to understand the conduction mechanism and the effect of grains and grain boundary on the electrical properties of the materials.

Electrocatalytic behaviour of surface confined pentanethio cobalt (II) binuclear phthalocyanines towards the oxidation of 4-chlorophenol

NASA Astrophysics Data System (ADS)

Makinde, Zainab O.; Louzada, Marcel; Mashazi, Philani; Nyokong, Tebello; Khene, Samson

2017-12-01

Cobalt binuclear phthalocyanine (CoBiPc) bearing pentanethio substituents at the peripheral positions were synthesized. The immobilization of the synthesized cobalt phthalocyanines on gold electrode was achieved using self-assembled monolayer method (SAM). X-ray photoelectron spectroscopy (XPS) and Kelvin Probe (KP) techniques were used to characterise the formation of monomeric and binuclear phthalocyanine SAMs on the gold surface. The phthalocyanine SAMs on gold electrodes were investigated for electrocatalytic oxidation of 4-chlorophenol. The electrocatalytic properties of tetra- and octa- pentanethio substituted cobalt binuclear phthalocyanine (CoBiPc) are compared with their tetra- and octa-pentanethio substituted phthalocyanine (CoPc). The SAMs modified gold electrode surfaces showed a peak current enhancement and stability and reduction in electrocatalytic potentials compared to the bare or unmodified electrodes towards the detection of the 4-chlorophenol. The SAMs of cobalt binuclear phthalocyanines exhibited more enhanced electrocatalytic properties in terms of stability, detection peak current and reduction of the electrocatalytic over potential.

Preparation of Magnesium, Cobalt and Nickel Ferrite Nanoparticles from Metal Oxides using Deep Eutectic Solvents.

PubMed

Söldner, Anika; Zach, Julia; Iwanow, Melanie; Gärtner, Tobias; Schlosser, Marc; Pfitzner, Arno; König, Burkhard

2016-09-05

Natural deep eutectic solvents (DESs) dissolve simple metal oxides and are used as a reaction medium to synthesize spinel-type ferrite nanoparticles MFe2 O4 (M=Mg, Zn, Co, Ni). The best results for phase-pure spinel ferrites are obtained with the DES consisting of choline chloride (ChCl) and maleic acid. By employing DESs, the reactions proceed at much lower temperatures than usual for the respective solid-phase reactions of the metal oxides and at the same temperatures as synthesis with comparable calcination processes using metal salts. The method therefore reduces the overall required energy for the nanoparticle synthesis. Thermogravimetric analysis shows that the thermolysis process of the eutectic melts in air occurs in one major step. The phase-pure spinel-type ferrite particles are thoroughly characterized by X-ray diffraction, diffuse-reflectance UV/Vis spectroscopy, and scanning electron microscopy. The properties of the obtained nanoparticles are shown to be comparable to those obtained by other methods, illustrating the potential of natural DESs for processing metal oxides. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Understanding the roles of the strategic element cobalt in nickel base superalloys

NASA Technical Reports Server (NTRS)

Stephens, J. R.; Dreshfield, R. L.

1983-01-01

The United States imports over 90% of its cobalt, chromium, columbium, and tantalum, all key elements in high temperature nickel base superalloys for aircraft gas turbine disks and airfoils. Research progress in understanding the roles of cobalt and some possible substitutes effects on microstructure, mechanical properties, and environmental resistance of turbine alloys is discussed.

Effect of native defects and Co doping on ferromagnetism in HfO2: first-principles calculations.

PubMed

Han, Chong; Yan, Shi-Shen; Lin, Xue-Ling; Hu, Shu-Jun; Zhao, Ming-Wen; Yao, Xin-Xin; Chen, Yan-Xue; Liu, Guo-Lei; Mei, Liang-Mo

2011-05-01

First-principles calculations of undoped HfO(2) and cobalt-doped HfO(2) have been carried out to study the magnetic properties of the dielectric material. In contrast to previous reports, it was found that the native defects in HfO(2) could not induce strong ferromagnetism. However, the cobalt substituting hafnium is the most stable defect under oxidation condition, and the ferromagnetic (FM) coupling between the cobalt substitutions is favorable in various configurations. We found that the FM coupling is mediated by the threefold-coordinated oxygen atoms in monoclinic HfO(2) and could be further enhanced in electron-rich condition. Copyright © 2010 Wiley Periodicals, Inc.

Adhesion and friction of transition metals in contact with nonmetallic hard materials

NASA Technical Reports Server (NTRS)

Miyoshi, K.; Buckley, D. H.

1981-01-01

Sliding friction experiments were conducted with the metals yttrium, titanium, tantalum, zirconium, vanadium, neodymium, iron, cobalt, nickel, tungsten, platinum, rhenium, ruthenium, and rhodium in sliding contact with single crystal diamond, silicon carbide, pyrolytic boron nitride, and ferrite. Auger electron spectroscopy analysis was conducted with the metals and nonmetals to determine the surface chemistry and the degree of surface cleanliness. The results of the investigation indicate the adhesion and friction of the transition metals in contact with diamond, silicon carbide, boron nitride, and ferrite are related to the relative chemical activity of the metals. The more chemically active the metal, the higher the coefficient of friction and the greater amount of transfer to the nonmetals.

Characterization of SrCo1.5Ti1.5Fe9O19 hexagonal ferrite synthesized by sol-gel combustion and solid state route

NASA Astrophysics Data System (ADS)

Vinaykumar, R.; Mazumder, R.; Bera, J.

2017-05-01

Co-Ti co-substituted SrM hexagonal ferrite (SrCo1.5Ti1.5Fe9O19) was synthesized by sol-gel combustion and solid state route. The effects of sources of TiO2 raw materials; titanium tetra-isopropoxide (TTIP) and titanyl nitrate (TN) on the phase formation behavior and properties of the ferrite were studied. The thermal decomposition behavior of the gel was studied using TG-DSC. The phase formation behavior of the ferrite was studied by using X-ray powder diffraction and FTIR analysis. Phase formation was comparatively easier in the TN-based sol-gel process. The morphology of powder and sintered ferrite was investigated using scanning electron microscope. Magnetic properties like magnetization, coercivity, permeability, tan δμ and dielectric properties were investigated. The ferrite synthesized by sol-gel based chemical route showed higher saturation magnetization, permeability and permittivity compared to the ferrite synthesized by solid state route.

Microwave magnetic properties of spinel ferrite films deposited by one-step electrochemical method

NASA Astrophysics Data System (ADS)

Zhang, Yao; Yuan, Lixin; Zhang, Xiaozhi; Zhang, Jie; Yue, Zhenxing; Li, Longtu

2017-07-01

Spinel ferrites have been widely used in microwave devices due to their excellent electromagnetic properties. In this study, two kinds of spinel ferrite films, Fe3O4 and Co xFe3-xO4, were grown on Pt(111)/Ti/SiO2/Si substrates by one-step electrochemical deposition method. The XRD and SEM characterizations demonstrated that the orientation of the ferrite films changed from (111) to (100) with the increase of depositing time. The cobalt content within Co xFe3-xO4 films was studied in detail by EDS analysis. The ferromagnetic resonance (FMR) responses of the ferrite films were measured by the flip-chip method using a vector network analyzer (VNA). It showed that the FMR frequency of Fe3O4 films reached to 10.5 GHz under an out-plane magnetic field of 5 kOe, while it reached to 27 GHz under an in-plane magnetic field of 5 kOe for Co xFe3-xO4 films. Meanwhile, whether the magnetic field was applied parallelly or perpendicularly, the resonant peaks were increased linearly with increasing the magnetic field, indicating that the films are promising candidates for applications in tunable wave-absorbing materials or other tunable frequency devices.

Influence of nickel substitution on crystal structure and magnetic properties of strontium ferrite preparation via sol-gel auto-combustion route

NASA Astrophysics Data System (ADS)

Roohani, Ebrahim; Arabi, Hadi; Sarhaddi, Reza

2018-01-01

In this research, SrFe12-xNixO19 (x = 0 - 1) hexagonal ferrites were prepared by sol-gel auto-combustion method. Effect of Ni substitution on structural, morphological and magnetic properties of nanoparticles was investigated by X-ray diffraction (XRD), Fourier transform infrared (FT-IR), Transmission electron microscopy (TEM) and vibrating sample magnetometer (VSM), respectively. The XRD results confirmed that all samples with x ≤ 0.5 have single phase M-type strontium ferrite structure, whereas for the SrFe12-xNixO19 samples with x > 0.5, the spinel NiFe2O4 phase has also appeared. The lattice parameters and crystallite sizes of the powders were concluded from the XRD data and Williamson-Hall method. Magnetic analyses showed that the coercivity of powders decreased from 5672 Oe to 639 Oe while the saturation magnetization increased from 74 emu/g to 81 emu/g with nickel substitution. The results of this study suggest that the strontium hexaferrites doped with Ni are suitable for applications in high density magnetic recording media as well as microwave devices because of their promising magnetic properties.

Effect of Cu2+ substitution on the structural, optical and magnetic behaviour ofchemically derived manganese ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Vasuki, G.; Balu, T.

2018-06-01

Mixed spinel copper manganese ferrite (CuXMn1‑XFe2O4, X = 0, 0.25, 0.5, 0.75, 1) nanoparticles were synthesized by chemical co-precipitation technique. From the powder x-ray diffraction analysis the lattice constant, volume of unit cell, x-ray density, hopping lengths, crystallite size, surface area, dislocation density and microstrain were calculated. The substitution of Cu2+ ions shows a considerable reduction in the crystallite size of manganese ferrite from 34 nm to 22 nm. Further a linear fit of Williamson-Hall plot has been drawn to determine the microstrain and crystallite size. The crystallite size and morphology were further observed through high resolution transmission electron microscope and scanning electron microscope. The diffraction rings observed from selected area electron diffraction pattern exhibits the crystalline nature of all the samples. The energy dispersive x-ray analysis shows the composition of all the elements incorporated in the synthesized nanomaterials. FTIR studies reveal the absorption peaks that correspond to the metal-oxygen vibrations in the tetrahedral and octahedral sites. From the UV–vis absorption spectra the band gap energy, refractive index and optical dielectric constant were determined. Magnetic studies carried out using vibrating sample magnetometer shows interesting behaviour in the variation of magnetisation and coercivity. Peculiar magnetic behaviour is observed when Cu2+ ions are substituted in manganese ferrites. All the synthesized materials have very low value of squareness ratio which attributes to the superparamagnetic behaviour.

Synthesis and characterization of carbon-coated cobalt ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Bakhshi, Hamed; Shokuhfar, Ali; Vahdati, Nima

2016-09-01

Cobalt ferrite nanoparticles (CFNPs) were prepared via a reverse micelle method. The CFNPs were subsequently coated with carbon shells by means of thermal chemical vapor deposition (TCVD). In this process, acetylene gas (C2H2) was used as a carbon source and the coating was carried out for 1, 2, or 3 h at 750°C. The Ar/C2H2 ratio was 10:1. Heating during the TCVD process resulted in a NP core size that approached 30 nm; the thickness of the shell was less than 10 nm. The composition, structure, and morphology of the fabricated composites were characterized using X-ray diffraction, simultaneous thermal analysis, transmission electron microscopy, high-resolution transmission electron microscopy, and selected-area diffraction. A vibrating sample magnetometer was used to survey the samples' magnetic properties. The deposited carbon shell substantially affected the growth and magnetic properties of the CFNPs. Micro-Raman spectroscopy was used to study the carbon coating and revealed that the deposited carbon comprised graphite, multiwalled carbon nanotubes, and diamond- like carbon. With an increase in coating time, the intensity ratio between the amorphous and ordered peaks in the Raman spectra decreased, which indicated an increase in crystallite size.

Oil/water nano-emulsion loaded with cobalt ferrite oxide nanocubes for photo-acoustic and magnetic resonance dual imaging in cancer: in vitro and preclinical studies.

PubMed

Vecchione, Raffaele; Quagliariello, Vincenzo; Giustetto, Pierangela; Calabria, Dominic; Sathya, Ayyappan; Marotta, Roberto; Profeta, Martina; Nitti, Simone; Silvestri, Niccolò; Pellegrino, Teresa; Iaffaioli, Rosario V; Netti, Paolo Antonio

2017-01-01

Dual imaging dramatically improves detection and early diagnosis of cancer. In this work we present an oil in water (O/W) nano-emulsion stabilized with lecithin and loaded with cobalt ferrite oxide (Co 0.5 Fe 2.5 O 4 ) nanocubes for photo-acoustic and magnetic resonance dual imaging. The nanocarrier is responsive in in vitro photo-acoustic and magnetic resonance imaging (MRI) tests. A clear and significant time-dependent accumulation in tumor tissue is shown in in vivo photo-acoustic studies on a murine melanoma xenograft model. The proposed O/W nano-emulsion exhibits also high values of r 2 /r 1 (ranging from 45 to 85, depending on the magnetic field) suggesting a possible use as T 2 weighted image contrast agents. In addition, viability and cellular uptake studies show no significant cytotoxicity on the fibroblast cell line. We also tested the O/W nano-emulsion loaded with curcumin against melanoma cancer cells demonstrating a significant cytotoxicity and thus showing possible therapeutic effects in addition to the in vivo imaging. Copyright © 2016 Elsevier Inc. All rights reserved.

Morphological, structural and thermal studies of gallium nitride ferrite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Indrakanti, Rajani; Rao, V. Brahmaji; Kiran, C. Udaya

2016-05-06

We report the synthesis and Characterization of III-V doped Nano ferrite Ga{sub (2x+2)}N Fe{sub 2(49-x)}O{sub 3} for x=1 and x=5 by Sol-Gel method. The Morphological, structural and Thermal characterisation studies are done by using Transmission Electron Microscopy, Energy Dispersive X-ray Analysis, Selected Area Electron Diffraction, Thermo-Gravimetric Analysis and Differential Thermal Analysis. Using the Sci-Finder software we could not trace any reports related to GaNFe{sub 2}O{sub 3} in the literature. It has been observed from our studies that the particles are in the Cylindrical and the Globular structure. The particle diameter values from the Histograms are in good agreement with themore » XRD values that were communicated by us earlier. The SAED and the EDAX studies reveal the confirmation of the composition and also that the synthesized Ferrite exhibits crystalline nature. The TG-DTA results show that the compound indicates constant sample weight.« less

Low activation ferritic alloys

DOEpatents

Gelles, David S.; Ghoniem, Nasr M.; Powell, Roger W.

1986-01-01

Low activation ferritic alloys, specifically bainitic and martensitic stainless steels, are described for use in the production of structural components for nuclear fusion reactors. They are designed specifically to achieve low activation characteristics suitable for efficient waste disposal. The alloys essentially exclude molybdenum, nickel, nitrogen and niobium. Strength is achieved by substituting vanadium, tungsten, and/or tantalum in place of the usual molybdenum content in such alloys.

Low activation ferritic alloys

DOEpatents

Gelles, D.S.; Ghoniem, N.M.; Powell, R.W.

1985-02-07

Low activation ferritic alloys, specifically bainitic and martensitic stainless steels, are described for use in the production of structural components for nuclear fusion reactors. They are designed specifically to achieve low activation characteristics suitable for efficient waste disposal. The alloys essentially exclude molybdenum, nickel, nitrogen and niobium. Strength is achieved by substituting vanadium, tungsten, and/or tantalum in place of the usual molybdenum content in such alloys.

Coastal sources, sinks and strong organic complexation of dissolved cobalt within the US North Atlantic GEOTRACES transect GA03

NASA Astrophysics Data System (ADS)

Noble, Abigail E.; Ohnemus, Daniel C.; Hawco, Nicholas J.; Lam, Phoebe J.; Saito, Mak A.

2017-06-01

Cobalt is the scarcest of metallic micronutrients and displays a complex biogeochemical cycle. This study examines the distribution, chemical speciation, and biogeochemistry of dissolved cobalt during the US North Atlantic GEOTRACES transect expeditions (GA03/3_e), which took place in the fall of 2010 and 2011. Two major subsurface sources of cobalt to the North Atlantic were identified. The more prominent of the two was a large plume of cobalt emanating from the African coast off the eastern tropical North Atlantic coincident with the oxygen minimum zone (OMZ) likely due to reductive dissolution, biouptake and remineralization, and aeolian dust deposition. The occurrence of this plume in an OMZ with oxygen above suboxic levels implies a high threshold for persistence of dissolved cobalt plumes. The other major subsurface source came from Upper Labrador Seawater, which may carry high cobalt concentrations due to the interaction of this water mass with resuspended sediment at the western margin or from transport further upstream. Minor sources of cobalt came from dust, coastal surface waters and hydrothermal systems along the Mid-Atlantic Ridge. The full depth section of cobalt chemical speciation revealed near-complete complexation in surface waters, even within regions of high dust deposition. However, labile cobalt observed below the euphotic zone demonstrated that strong cobalt-binding ligands were not present in excess of the total cobalt concentration there, implying that mesopelagic labile cobalt was sourced from the remineralization of sinking organic matter. In the upper water column, correlations were observed between total cobalt and phosphate, and between labile cobalt and phosphate, demonstrating a strong biological influence on cobalt cycling. Along the western margin off the North American coast, this correlation with phosphate was no longer observed and instead a relationship between cobalt and salinity was observed, reflecting the importance of coastal input processes on cobalt distributions. In deep waters, both total and labile cobalt concentrations were lower than in intermediate depth waters, demonstrating that scavenging may remove labile cobalt from the water column. Total and labile cobalt distributions were also compared to a previously published South Atlantic GEOTRACES-compliant zonal transect (CoFeMUG, GAc01) to discern regional biogeochemical differences. Together, these Atlantic sectional studies highlight the dynamic ecological stoichiometry of total and labile cobalt. As increasing anthropogenic use and subsequent release of cobalt poses the potential to overpower natural cobalt signals in the oceans, it is more important than ever to establish a baseline understanding of cobalt distributions in the ocean.

Self-assembled mesoporous Co and Ni-ferrite spherical clusters consisting of spinel nanocrystals prepared using a template-free approach.

PubMed

Yu, Byong Yong; Kwak, Seung-Yeop

2011-10-21

Based on a self-assembly strategy, spherical mesoporous cobalt and nickel ferrite nanocrystal clusters with a large surface area and narrow size distribution were successfully synthesized for the first time via a template-free solvothermal process in ethylene glycol and subsequent heat treatment. In this work, the mesopores in the ferrite clusters were derived mainly from interior voids between aggregated primary nanoparticles (with crystallite size of less than 7 nm) and disordered particle packing domains. The concentration of sodium acetate is shown herein to play a crucial role in the formation of mesoporous ferrite spherical clusters. These ferrite clusters were characterized in detail using wide-angle X-ray diffraction, thermogravimetric-differential thermal analysis, (57)Fe Mössbauer spectroscopy, X-ray photoelectron spectroscopy, field-emission scanning electron microscopy, standard and high-resolution transmission electron microscopy, and other techniques. The results confirmed the formation of both pure-phase ferrite clusters with highly crystalline spinel structure, uniform size (about 160 nm) and spherical morphology, and worm-like mesopore structures. The BET specific surface areas and mean pore sizes of the mesoporous Co and Ni-ferrite clusters were as high as 160 m(2) g(-1) and 182 m(2) g(-1), and 7.91 nm and 6.87 nm, respectively. A model for the formation of the spherical clusters in our system is proposed on the basis of the results. The magnetic properties of both samples were investigated at 300 K, and it was found that these materials are superparamagnetic. This journal is © The Royal Society of Chemistry 2011

A study on magneto-optic properties of CoxMg1-xFe2O4 nanoferrofluids

NASA Astrophysics Data System (ADS)

Karthick, R.; Ramachandran, K.; Srinivasan, R.

2018-04-01

Nanoparticles of CoxMg1-xFe2O4 (x = 0.1, 0.5, 0.9) were synthesized using chemical co-precipitation method. Characterization by X-ray diffraction technique confirmed the formation of cubic crystalline structure and the crystallite size of the samples obtained using Debye-Scherrer approximation were found to increase with increasing cobalt substitution. Surface morphology and the Chemical composition of the samples were visualized using scanning electron microscope (SEM) with energy dispersive analysis of X-rays (EDAX). Room temperature magnetic parameters of the nanoparticles by vibrating sample magnetometer (VSM) revealed the magnetic properties such as Saturation magnetization (Ms), Remanent magnetization (Mr) and Coercive field (Hc) found to increase with increasing cobalt substitution. Faraday rotation measurements on CoxMg1-xFe2O4 ferrofluids exhibited increase in rotation with cobalt substitution. Further, there is an increase in Faraday rotation with increasing magnetic field for all the samples.

In Vitro Evaluation of Nanoscale Hydroxyapatite-Based Bone Reconstructive Materials with Antimicrobial Properties.

PubMed

Ajduković, Zorica R; Mihajilov-Krstev, Tatjana M; Ignjatović, Nenad L; Stojanović, Zoran; Mladenović-Antić, Snezana B; Kocić, Branislava D; Najman, Stevo; Petrović, Nenad D; Uskoković, Dragan P

2016-02-01

In the field of oral implantology the loss of bone tissue prevents adequate patient care, and calls for the use of synthetic biomaterials with properties that resemble natural bone. Special attention is paid to the risk of infection after the implantation of these materials. Studies have suggested that some nanocontructs containing metal ions have antimicrobial properties. The aim of this study was to examine the antimicrobial and hemolytic activity of cobalt-substituted hydroxyapatite nanoparticles, compared to hydroxyapatite and hydroxyapatite/poly-lactide-co-glycolide. The antibacterial effects of these powders were tested against two pathogenic bacterial strains: Escherichia coi (ATCC 25922) and Staphylococcus aureus (ATCC 25923), using the disc diffusion method and the quantitative antimicrobial test in a liquid medium. The quantitative antimicrobial test showed that all of the tested biomaterials have some antibacterial properties. The effects of both tests were more prominent in case of S. aureus than in E coli. A higher percentage of cobalt in the crystal structure of cobalt-substituted hydroxyapatite nanoparticles led to an increased antimicrobial activity. All of the presented biomaterial samples were found to be non-hemolytic. Having in mind that the tested of cobalt-substituted hydroxyapatite (Ca/Co-HAp) material in given concentrations shows good hemocompatibility and antimicrobial effects, along with its previously studied biological properties, the conclusion can be reached that it is a potential candidate that could substitute calcium hydroxyapatite as the material of choice for use in bone tissue engineering and clinical practices in orthopedic, oral and maxillofacial surgery.

Magnetization and anisotropy of cobalt ferrite thin films

NASA Astrophysics Data System (ADS)

Eskandari, F.; Porter, S. B.; Venkatesan, M.; Kameli, P.; Rode, K.; Coey, J. M. D.

2017-12-01

The magnetization of thin films of cobalt ferrite frequently falls far below the bulk value of 455 kA m-1 , which corresponds to an inverse cation distribution in the spinel structure with a significant orbital moment of about 0.6 μB that is associated with the octahedrally coordinated Co2+ ions. The orbital moment is responsible for the magnetostriction and magnetocrystalline anisotropy and its sensitivity to imposed strain. We have systematically investigated the structure and magnetism of films produced by pulsed-laser deposition on different substrates (Ti O2 , MgO, MgA l2O4 , SrTi O3 , LSAT, LaAl O3 ) and as a function of temperature (500 -700 °C) and oxygen pressure (10-4-10 Pa ) . Magnetization at room-temperature ranges from 60 to 440 kA m-1 , and uniaxial substrate-induced anisotropy ranges from +220 kJ m-3 for films on deposited on MgO (100) to -2100 kJ m-3 for films deposited on MgA l2O4 (100), where the room-temperature anisotropy field reaches 14 T. No rearrangement of high-spin Fe3+ and Co2+ cations on tetrahedral and octahedral sites can reduce the magnetization below the bulk value, but a switch from Fe3+ and Co2+ to Fe2+ and low-spin Co3+ on octahedral sites will reduce the low-temperature magnetization to 120 kA m-1 , and a consequent reduction of Curie temperature can bring the room-temperature value to near zero. Possible reasons for the appearance of low-spin cobalt in the thin films are discussed.

Heavy-metal detectors based on modified ferrite nanoparticles

PubMed Central

Klekotka, Urszula; Wińska, Ewelina; Zambrzycka-Szelewa, Elżbieta; Satuła, Dariusz

2018-01-01

In this work, we analyze artificial heavy-metal solutions with ferrite nanoparticles. Measurements of adsorption effectiveness of different kinds of particles, pure magnetite or magnetite doped with calcium, cobalt, manganese, or nickel ions, were carried out. A dependence of the adsorption efficiency on the composition of the inorganic core has been observed. Ferrites surfaces were modified by phthalic anhydride (PA), succinic anhydride (SA), acetic anhydride (AA), 3-phosphonopropionic acid (3-PPA), or 16-phosphohexadecanoic acid (16-PHDA) to compare the adsorption capability of the heavy metals Cd, Cu and Pb. The obtained nanoparticles were structurally characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and Mössbauer spectroscopy. The amounts of Cd, Cu and Pb were measured out by atomic absorption spectroscopy (AAS) and energy dispersive X-ray (EDX) as comparative techniques. The performed study shows that SA linker appears to be the most effective in the adsorption of heavy metals. Moreover, regarding the influence of the composition of the inorganic core on the detection ability, the most effective ferrite Mn0.5Fe2.5O4 was selected for discussion. The highest heavy-metal adsorption capability and universality was observed for SA as a surface modifier. PMID:29600137

Heavy-metal detectors based on modified ferrite nanoparticles.

PubMed

Klekotka, Urszula; Wińska, Ewelina; Zambrzycka-Szelewa, Elżbieta; Satuła, Dariusz; Kalska-Szostko, Beata

2018-01-01

In this work, we analyze artificial heavy-metal solutions with ferrite nanoparticles. Measurements of adsorption effectiveness of different kinds of particles, pure magnetite or magnetite doped with calcium, cobalt, manganese, or nickel ions, were carried out. A dependence of the adsorption efficiency on the composition of the inorganic core has been observed. Ferrites surfaces were modified by phthalic anhydride (PA), succinic anhydride (SA), acetic anhydride (AA), 3-phosphonopropionic acid (3-PPA), or 16-phosphohexadecanoic acid (16-PHDA) to compare the adsorption capability of the heavy metals Cd, Cu and Pb. The obtained nanoparticles were structurally characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and Mössbauer spectroscopy. The amounts of Cd, Cu and Pb were measured out by atomic absorption spectroscopy (AAS) and energy dispersive X-ray (EDX) as comparative techniques. The performed study shows that SA linker appears to be the most effective in the adsorption of heavy metals. Moreover, regarding the influence of the composition of the inorganic core on the detection ability, the most effective ferrite Mn 0.5 Fe 2.5 O 4 was selected for discussion. The highest heavy-metal adsorption capability and universality was observed for SA as a surface modifier.

Amperometric ascorbic acid sensor based on doped ferrites nanoparticles modified glassy carbon paste electrode.

PubMed

Dimitrijević, Teodora; Vulić, Predrag; Manojlović, Dragan; Nikolić, Aleksandar S; Stanković, Dalibor M

2016-07-01

In this study, a novel electrochemical sensor for quantification of ascorbic acid with amperometric detection in physiological conditions was constructed. For this purpose, cobalt and nickel ferrites were synthesized using microwave and ultrasound assistance, characterized by scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectroscopy, and X-ray powder diffraction (XRPD), and used for modification of glassy carbon paste electrode (GCPE). It was shown that introducing these nanoparticles to the structure of GCPE led to increasing analytical performance. Co ferrite modified GCPE (CoFeGCPE) showed better characteristics toward ascorbic acid sensing. The limit of detection (LOD) obtained by sensor was calculated to be 0.0270 mg/L, with linear range from 0.1758 to 2.6010 mg/L. This sensor was successfully applied for practical analysis, and the obtained results demonstrated that the proposed procedure could be a promising replacement for the conventional electrode materials and time-consuming and expensive separation methods. Copyright © 2016 Elsevier Inc. All rights reserved.

Phase composition and magnetism of sol-gel synthesized Ga-Fe-O nanograins

NASA Astrophysics Data System (ADS)

Rećko, K.; Waliszewski, J.; Klekotka, U.; Soloviov, D.; Ostapczuk, G.; Satuła, D.; Biernacka, M.; Balasoiu, M.; Basa, A.; Kalska-Szostko, B.; Szymański, K.

2018-02-01

We have succeeded in synthesizing orthorhombic Ga(1-x)Fe(1+x)O3 (-0.05? x?0.5), hexagonal GayFe(2-y)O3 (0?y?1.8) and cubic Ga(1+z)Fe(2-z)O4 (-0.1?z?0.8) nanograins of gallium ferrites using conventional precursors and an organic environment of Pechini scenario under atmospheric-pressure conditions (SG method). Phase composition and homogeneity were analyzed using X-ray diffraction. Small angle neutron scattering disclosed ellipsoidal particle shapes of gallium iron oxides (GFO) crystallizing in orthorhombic (o-GFO) and hexagonal (h-GFO) symmetry and parallelepiped shapes of Ga(1+y)Fe(2-y)O4 (c-GFO) grains. Despite local agglomeration among the magnetic grains, the scanning electron microscopy and transmission electron microscopy images point to faced-elliptical shapes. The Mössbauer spectroscopy with magnetization measurements was carried out in the temperature range of 5-295 K. The analysis of gallium ferrites magnetism demonstrates that iron atoms locate with various probabilities in crystallographic positions and the spontaneous magnetization preserves up to room temperature (RT).

Cation distribution of Ni-Zn-Mn ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Parvatheeswara Rao, B.; Dhanalakshmi, B.; Ramesh, S.; Subba Rao, P. S. V.

2018-06-01

Mn substituted Ni-Zn ferrite nanoparticles, Ni0.4Zn0.6-xMnxFe2O4 (x = 0.00-0.25 in steps of 0.05), using metal nitrates were prepared by sol-gel autocombustion in citric acid matrix. The samples were examined by X-ray diffraction and vibrating sample magnetometer techniques. Rietveld structural refinements using the XRD data were performed on the samples to consolidate various structural parameters like phase (spinel), crystallite size (24.86-37.43 nm), lattice constant (8.3764-8.4089 Å) etc and also to determine cation distributions based on profile matching and integrated intensity ratios. Saturation magnetization values (37.18-68.40 emu/g) were extracted from the measured M-H loops of these nanoparticles to estimate their magnetic moments. Experimental and calculated magnetic moments and lattice constants were used to confirm the derived cation distributions from Rietveld analysis. The results of these ferrite nanoparticles are discussed in terms of the compositional modifications, particle sizes and the corresponding cation distributions as a result of Mn substitutions.

Nanoparticles of cobalt-substituted hydroxyapatite in regeneration of mandibular osteoporotic bones.

PubMed

Ignjatović, Nenad; Ajduković, Zorica; Savić, Vojin; Najman, Stevo; Mihailović, Dragan; Vasiljević, Perica; Stojanović, Zoran; Uskoković, Vuk; Uskoković, Dragan

2013-02-01

Indications exist that paramagnetic calcium phosphates may be able to promote regeneration of bone faster than their regular, diamagnetic counterparts. In this study, analyzed was the influence of paramagnetic cobalt-substituted hydroxyapatite nanoparticles on osteoporotic alveolar bone regeneration in rats. Simultaneously, biocompatibility of the material was tested in vitro, on osteoblastic MC3T3-E1 and epithelial Caco-2 cells in culture. The material was shown to be biocompatible and nontoxic when added to epithelial monolayers in vitro, while it caused a substantial decrease in the cell viability as well as deformation of the cytoskeleton and cell morphology when incubated with the osteoblastic cells. In the course of 6 months after the implantation of the material containing different amounts of cobalt, ranging from 5 to 12 wt%, in the osteoporotic alveolar bone of the lower jaw, the following parameters were investigated: histopathological parameters, alkaline phosphatase and alveolar bone density. The best result in terms of osteoporotic bone tissue regeneration was observed for hydroxyapatite nanoparticles with the largest content of cobalt ions. The histological analysis showed a high level of reparatory ability of the nanoparticulate material implanted in the bone defect, paralleled by a corresponding increase in the alveolar bone density. The combined effect of growth factors from autologous plasma admixed to cobalt-substituted hydroxyapatite was furthermore shown to have a crucial effect on the augmented osteoporotic bone regeneration upon the implantation of the biomaterial investigated in this study.

Nanoparticles of cobalt-substituted hydroxyapatite in regeneration of mandibular osteoporotic bones

PubMed Central

Ignjatović, Nenad; Ajduković, Zorica; Savić, Vojin; Najman, Stevo; Mihailović, Dragan; Vasiljević, Perica; Stojanović, Zoran; Uskoković, Vuk; Uskoković, Dragan

2012-01-01

Indications exist that paramagnetic calcium phosphates may be able to promote regeneration of bone faster than their regular, diamagnetic counterparts. In this study, analyzed was the influence of paramagnetic cobalt-substituted hydroxyapatite nanoparticles on osteoporotic alveolar bone regeneration in rats. Simultaneously, biocompatibility of the material was tested in vitro, on osteoblastic MC3T3-E1 and epithelial Caco-2 cells in culture. The material was shown to be biocompatible and nontoxic when added to epithelial monolayers in vitro, while it caused a substantial decrease in the cell viability as well as deformation of the cytoskeleton and cell morphology when incubated with the osteoblastic cells. In the course of six months after the implantation of the material containing different amounts of cobalt, ranging from 5 – 12 wt%, in the osteoporotic alveolar bone of the lower jaw, the following parameters were investigated: histopathological parameters, alkaline phosphatase and alveolar bone density. The best result in terms of osteoporotic bone tissue regeneration was observed for hydroxyapatite nanoparticles with the largest content of cobalt ions. The histological analysis showed a high level of reparatory ability of the nanoparticulate material implanted in the bone defect, paralleled by a corresponding increase in the alveolar bone density. The combined effect of growth factors from autologous plasma admixed to cobalt-substituted hydroxyapatite was furthermore shown to have a crucial effect on the augmented osteoporotic bone regeneration upon the implantation of the biomaterial investigated in this study. PMID:23090835

Small-angle neutron scattering investigations of Co-doped iron oxide nanoparticles. Preliminary results

NASA Astrophysics Data System (ADS)

Creanga, Dorina; Balasoiu, Maria; Soloviov, Dmitro; Balasoiu-Gaina, Alexandra-Maria; Puscasu, Emil; Lupu, Nicoleta; Stan, Cristina

2018-03-01

Preliminary small-angle neutron scattering investigations on aqueous suspensions of several cobalt doped ferrites (CoxFe3-xO4, x=0; 0.5; 1) nanoparticles prepared by chemical co-precipitation method, are reported. The measurements were accomplished at the YuMO instrument in function at the IBR-2 reactor. Results of intermediary data treatment are presented and discussed.

Effect of Molybdenum Incorporation on the Structure and Magnetic Properties of Cobalt Ferrite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Orozco, C.; Melendez, A.; Manadhar, S.

Here, we report on the effect of molybdenum (Mo) incorporation on the crystal structure, surface morphology, Mo chemical valence state, and magnetic properties of cobalt ferrite (CoFe 2O 4, referred to CFO). Molybdenum incorporated cobalt ferrite (CoFe 2–xMo xO 4, referred to CFMO) ceramics were prepared by the conventional solid-state reaction method by varying the Mo concentration in the range of x = 0.0–0.3. X-ray diffraction studies indicate that the CFMO materials crystallize in inverse spinel cubic phase. Molybdenum incorporation induced lattice parameter increase from 8.322 to 8.343 Å coupled with a significant increase in density from 5.4 to 5.7more » g/cm 3 was evident in structural analyses. Scanning electron microscopy imaging analyses indicate that the Mo incorporation induces agglomeration of particles leading to larger particle size with increasing x(Mo) values. Detailed X-ray photoelectron spectroscopic (XPS) analyses indicate the increasing Mo content with increasing x from 0.0 to 0.3. XPS confirms that the chemistry of Mo is complex in these CFMO compounds; Mo ions exist in the lower oxidation state (Mo 4+) for higher x while in a mixed chemical valence state (Mo 4+, Mo 5+, Mo 6+) for lower x values. From the temperature-dependent magnetization, the samples show ferrimagnetic behavior including the pristine CFO. From the isothermal magnetization measurements, we find almost 2-fold decrease in coercive field ( H c) from 2143 to 1145 Oe with the increase in Mo doping up to 30%. This doping-dependent H c is consistently observed at all the temperatures measured (4, 100, 200, and 300 K). Furthermore, the saturation magnetization estimated at 4 K and at 1.5 T (from M–H loops) goes through a peak at 92 emu/g (at 15% Mo doping) from 81 emu/g (pristine CFO), and starts decreasing to 79 emu/g (at 30% Mo doping). The results demonstrate that the crystal structure, microstructure, and magnetic properties can be tuned by controlling the Mo-content in the CFMO materials.« less

Effect of Molybdenum Incorporation on the Structure and Magnetic Properties of Cobalt Ferrite

DOE PAGES

Orozco, C.; Melendez, A.; Manadhar, S.; ...

2017-09-26

Here, we report on the effect of molybdenum (Mo) incorporation on the crystal structure, surface morphology, Mo chemical valence state, and magnetic properties of cobalt ferrite (CoFe 2O 4, referred to CFO). Molybdenum incorporated cobalt ferrite (CoFe 2–xMo xO 4, referred to CFMO) ceramics were prepared by the conventional solid-state reaction method by varying the Mo concentration in the range of x = 0.0–0.3. X-ray diffraction studies indicate that the CFMO materials crystallize in inverse spinel cubic phase. Molybdenum incorporation induced lattice parameter increase from 8.322 to 8.343 Å coupled with a significant increase in density from 5.4 to 5.7more » g/cm 3 was evident in structural analyses. Scanning electron microscopy imaging analyses indicate that the Mo incorporation induces agglomeration of particles leading to larger particle size with increasing x(Mo) values. Detailed X-ray photoelectron spectroscopic (XPS) analyses indicate the increasing Mo content with increasing x from 0.0 to 0.3. XPS confirms that the chemistry of Mo is complex in these CFMO compounds; Mo ions exist in the lower oxidation state (Mo 4+) for higher x while in a mixed chemical valence state (Mo 4+, Mo 5+, Mo 6+) for lower x values. From the temperature-dependent magnetization, the samples show ferrimagnetic behavior including the pristine CFO. From the isothermal magnetization measurements, we find almost 2-fold decrease in coercive field ( H c) from 2143 to 1145 Oe with the increase in Mo doping up to 30%. This doping-dependent H c is consistently observed at all the temperatures measured (4, 100, 200, and 300 K). Furthermore, the saturation magnetization estimated at 4 K and at 1.5 T (from M–H loops) goes through a peak at 92 emu/g (at 15% Mo doping) from 81 emu/g (pristine CFO), and starts decreasing to 79 emu/g (at 30% Mo doping). The results demonstrate that the crystal structure, microstructure, and magnetic properties can be tuned by controlling the Mo-content in the CFMO materials.« less

Development of europium doped core-shell silica cobalt ferrite functionalized nanoparticles for magnetic resonance imaging.

PubMed

Kevadiya, Bhavesh D; Bade, Aditya N; Woldstad, Christopher; Edagwa, Benson J; McMillan, JoEllyn M; Sajja, Balasrinivasa R; Boska, Michael D; Gendelman, Howard E

2017-02-01

The size, shape and chemical composition of europium (Eu 3+ ) cobalt ferrite (CFEu) nanoparticles were optimized for use as a "multimodal imaging nanoprobe" for combined fluorescence and magnetic resonance bioimaging. Doping Eu 3+ ions into a CF structure imparts unique bioimaging and magnetic properties to the nanostructure that can be used for real-time screening of targeted nanoformulations for tissue biodistribution assessment. The CFEu nanoparticles (size ∼7.2nm) were prepared by solvothermal techniques and encapsulated into poloxamer 407-coated mesoporous silica (Si-P407) to form superparamagnetic monodisperse Si-CFEu nanoparticles with a size of ∼140nm. Folic acid (FA) nanoparticle decoration (FA-Si-CFEu, size ∼140nm) facilitated monocyte-derived macrophage (MDM) targeting. FA-Si-CFEu MDM uptake and retention was higher than seen with Si-CFEu nanoparticles. The transverse relaxivity of both Si-CFEu and FA-Si-CFEu particles were r 2 =433.42mM -1 s -1 and r 2 =419.52mM -1 s -1 (in saline) and r 2 =736.57mM -1 s -1 and r 2 =814.41mM -1 s -1 (in MDM), respectively. The results were greater than a log order-of-magnitude than what was observed at replicate iron concentrations for ultrasmall superparamagnetic iron oxide (USPIO) particles (r 2 =31.15mM -1 s -1 in saline) and paralleled data sets obtained for T 2 magnetic resonance imaging. We now provide a developmental opportunity to employ these novel particles for theranostic drug distribution and efficacy evaluations. A novel europium (Eu 3+ ) doped cobalt ferrite (Si-CFEu) nanoparticle was produced for use as a bioimaging probe. Its notable multifunctional, fluorescence and imaging properties, allows rapid screening of future drug biodistribution. Decoration of the Si-CFEu particles with folic acid increased its sensitivity and specificity for magnetic resonance imaging over a more conventional ultrasmall superparamagnetic iron oxide particles. The future use of these particles in theranostic tests will serve as a platform for designing improved drug delivery strategies to combat inflammatory and infectious diseases. Copyright © 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Epitaxial Garnets and Hexagonal Ferrites.

DTIC Science & Technology

1982-04-20

goenv.o -,y la)ers were YIG (yttrium iron garnet ) films grown by liquid phase epitaxy w:* ( LPE ) on gadolinium gallium garnet (GGG) substrates. Magnetic...containing three epitaxial layers. In addition to the MSW work oil garnets , LPE of lithium ferrite and hexagonal fertites was studied. A substituted lead...of a stripline. The other layers are epitaxial films , generally YIG (yttrium iron garnet ) with magnetic properties adjusted by suitable modifications

Electrical conductivity of cobalt doped La 0.8Sr 0.2Ga 0.8Mg 0.2O 3- δ

NASA Astrophysics Data System (ADS)

Wang, Shizhong; Wu, Lingli; Liang, Ying

La 0.8Sr 0.2Ga 0.8Mg 0.2O 3- δ (LSGM8282), La 0.8Sr 0.2Ga 0.8Mg 0.15Co 0.05O 3- δ (LSGMC5) and La 0.8Sr 0.2Ga 0.8Mg 0.115Co 0.085O 3- δ (LSGMC8.5) were prepared using a conventional solid-state reaction. Electrical conductivities and electronic conductivities of the samples were measured using four-probe impedance spectrometry, four-probe dc polarization and Hebb-Wagner polarization within the temperature range of 973-1173 K. The electrical conductivities in LSGMC5 and LSGMC8.5 increased with decreasing oxygen partial pressures especially in the high (>10 -5 atm) and low oxygen partial pressure regions (<10 -15 atm). However, the electrical conductivity in LSGM8282 had no dependency on the oxygen partial pressure. At temperatures higher than 1073 K, PO2 dependencies of the free electron conductivities in LSGM8282, LSGMC5 and LSGMC8.5 were about -1/4, and PO2 dependencies of the electron hole conductivities were about 0.25, 0.12 and 0.07, respectively. Oxygen ion conductivities in LSGMC5 and LSGMC8.5 increased with decreasing oxygen partial pressures especially in the high and low oxygen partial pressure regions, which was due to the increase in the concentration of oxygen vacancies. The change in the concentration of oxygen vacancies and the valence of cobalt with oxygen partial pressure were determined using a thermo-gravimetric technique. Both the electronic conductivity and oxygen ion conductivity in cobalt doped lanthanum gallate samples increased with increasing concentration of cobalt, suggesting that the concentration of cobalt should be optimized carefully to maintain a high electrical conductivity and close to 1 oxygen ion transference number.

Magnetic and magnetoresistance properties of La0.7Sr0.3(Mn,Сo)O3

NASA Astrophysics Data System (ADS)

Troyanchuk, I. O.; Karpinsky, D. V.; Bushinsky, M. V.; Sikolenko, V. V.; Gavrilov, S. A.; Silibin, M. V.

2017-11-01

Magnetic and magnetotransport properties of La0.7Sr0.3Mn1-xCoxO3 ceramics have been investigated by neutron powder diffraction, magnetization and electrical measurements. It is shown that substitution by cobalt ions leads to a decrease of magnetic transition temperature down to 140 K for the compound with x = 0.33. The compounds with cobalt content 0.4 < x < 0.6 are characterized by a presence of small ferromagnetic component due to exchange interactions between cobalt and manganese ions with maximal transition temperature of about 190 K observed for x = 0.5. Further increase of the dopant concentration diminishes ferromagnetic interactions. An evolution of electronic configuration of manganese and cobalt ions upon chemical substitution as well as related changes in the exchange interactions which determine the type of the magnetic state are discussed. Based on the neutron diffraction results and magnetometry data the preliminary magnetic phase diagram has been constructed.

Magnetic moment directions and distributions of cations in Cr (Co) substituted spinel ferrites Ni0.7Fe2.3O4

NASA Astrophysics Data System (ADS)

Xue, L. C.; Lang, L. L.; Xu, J.; Li, Z. Z.; Qi, W. H.; Tang, G. D.; Wu, L. Q.

2015-09-01

Powder samples of the spinel ferrites MxNi0.7-xFe2.3O4 (M = Cr, Co and 0.0 ≤ x ≤ 0.3) and CrxNi0.7Fe2.3-xO4 (0.0 ≤ x ≤ 0.3) were synthesized using the chemical co-precipitation method. The XRD spectra confirmed that the samples had a single-phase cubic spinel structure. Magnetic measurements showed that the magnetic moments (μexp) per formula both at 10 K and 300 K increased with Co substitution, while the values of μexp decreased with Cr substitution. Applying the assumption that the magnetic moments of Cr2+ and Cr3+ lie antiparallel to those of the divalent and trivalent Fe, Co, and Ni cations in the same sublattice of spinel ferrites, these interesting behaviors could be easily interpreted. The cation distributions of the three series of samples were estimated successfully by fitting the dependences of μexp, measured at 10 K, on the doping level x, using a quantum-mechanical potential barrier model earlier proposed by our group. The results obtained for the Cr cation distributions at the (A) and [B] sites are very close to those obtained elsewhere using neutron diffraction.

Thermal Condensation of Glycine and Alanine on Metal Ferrite Surface: Primitive Peptide Bond Formation Scenario.

PubMed

Iqubal, Md Asif; Sharma, Rachana; Jheeta, Sohan; Kamaluddin

2017-03-27

The amino acid condensation reaction on a heterogeneous mineral surface has been regarded as one of the important pathways for peptide bond formation. Keeping this in view, we have studied the oligomerization of the simple amino acids, glycine and alanine, on nickel ferrite (NiFe₂O₄), cobalt ferrite (CoFe₂O₄), copper ferrite (CuFe₂O₄), zinc ferrite (ZnFe₂O₄), and manganese ferrite (MnFe₂O₄) nanoparticles surfaces, in the temperature range from 50-120 °C for 1-35 days, without applying any wetting/drying cycles. Among the metal ferrites tested for their catalytic activity, NiFe₂O₄ produced the highest yield of products by oligomerizing glycine to the trimer level and alanine to the dimer level, whereas MnFe₂O₄ was the least efficient catalyst, producing the lowest yield of products, as well as shorter oligomers of amino acids under the same set of experimental conditions. It produced primarily diketopiperazine (Ala) with a trace amount of alanine dimer from alanine condensation, while glycine was oligomerized to the dimer level. The trend in product formation is in accordance with the surface area of the minerals used. A temperature as low as 50 °C can even favor peptide bond formation in the present study, which is important in the sense that the condensation process is highly feasible without any sort of localized heat that may originate from volcanoes or hydrothermal vents. However, at a high temperature of 120 °C, anhydrides of glycine and alanine formation are favored, while the optimum temperature for the highest yield of product formation was found to be 90 °C.

Thermal Condensation of Glycine and Alanine on Metal Ferrite Surface: Primitive Peptide Bond Formation Scenario

PubMed Central

Iqubal, Md. Asif; Sharma, Rachana; Jheeta, Sohan; Kamaluddin

2017-01-01

The amino acid condensation reaction on a heterogeneous mineral surface has been regarded as one of the important pathways for peptide bond formation. Keeping this in view, we have studied the oligomerization of the simple amino acids, glycine and alanine, on nickel ferrite (NiFe2O4), cobalt ferrite (CoFe2O4), copper ferrite (CuFe2O4), zinc ferrite (ZnFe2O4), and manganese ferrite (MnFe2O4) nanoparticles surfaces, in the temperature range from 50–120 °C for 1–35 days, without applying any wetting/drying cycles. Among the metal ferrites tested for their catalytic activity, NiFe2O4 produced the highest yield of products by oligomerizing glycine to the trimer level and alanine to the dimer level, whereas MnFe2O4 was the least efficient catalyst, producing the lowest yield of products, as well as shorter oligomers of amino acids under the same set of experimental conditions. It produced primarily diketopiperazine (Ala) with a trace amount of alanine dimer from alanine condensation, while glycine was oligomerized to the dimer level. The trend in product formation is in accordance with the surface area of the minerals used. A temperature as low as 50 °C can even favor peptide bond formation in the present study, which is important in the sense that the condensation process is highly feasible without any sort of localized heat that may originate from volcanoes or hydrothermal vents. However, at a high temperature of 120 °C, anhydrides of glycine and alanine formation are favored, while the optimum temperature for the highest yield of product formation was found to be 90 °C. PMID:28346388

Zr doping dependence of structural and magnetic properties of cobalt ferrite synthesized by sol-gel based Pechini method

NASA Astrophysics Data System (ADS)

Motavallian, Pourya; Abasht, Behzad; Abdollah-Pour, Hassan

2018-04-01

Nanocrystalline CoZrxFe2-xO4 (0 ≤ x ≤ 0.3 in a step of 0.05) powders were synthesized by Pechini sol-gel method. The dry gel was grinded and calcined at 700 °C in a static air atmosphere for 1 h. Some tests such as thermo gravimetric analysis (TGA) combined with differential analysis (DTA), fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM) and vibrating sample magnetometer (VSM) were carried out to investigate the thermal behaviour, structural bonds identification, crystallographic properties, morphology and magnetic properties of the obtained powders. X-ray diffraction revealed a single-phase cubic spinel structure for all samples, where the crystallite size decreases; the lattice parameter simultaneously increases with substitution of Zr. The results of FE-SEM showed that the particle size is in the 20-70 nm range. The magnetic properties such as saturation magnetization (Ms), remanent magnetization (Mr) and coercivity (Hc) were measured from the hysteresis loops. The greatest amount of saturation magnetization for CoZr0.05Fe1.95O4 sample was 67.9 emu·g-1.

Physical and magnetic properties of (Ba/Sr) substituted magnesium nano ferrites

NASA Astrophysics Data System (ADS)

Ateia, Ebtesam E.; Takla, E.; Mohamed, Amira T.

2017-10-01

In the presented paper, strontium (Sr) and barium (Ba) nano ferrites were synthesized by citrate auto combustion method. The investigated samples are characterized by X-ray diffraction technique (XRD), field emission scanning electron microscopy, high resolution transmission electron microscopy and energy dispersive X-ray spectroscopy. The structural properties of the obtained samples were examined by XRD analysis showing that the synthesized nanoparticles are in cubic spinel structure. The average crystallite sizes are in the range of 22.66 and 21.95 nm for Mg0.7Ba0.3Fe2O4 and Mg0.7 Sr0.3Fe2O4 respectively. The VSM analysis confirms the existence of ferromagnetic nature of Sr2+/Ba2+ substituted magnesium nano particles. Exchange interaction between hard (Sr/Ba) and soft (Mg) magnetic phases improves the structural and magnetic properties of nano ferrite particles. Rigidity modulus, longitudinal and shear wave velocities are predicted theoretically from Raman spectroscopy and structural data of the investigated spinel ferrite. The magnetic and structural properties of magnesium are enhanced by doping with barium and strontium nano particles. The saturation magnetization, remanent magnetization and coercivity reported on vibrating sample magnetometer curve illustrate the promising industrial and magnetic recording applications of the prepared samples.

Effects of site disorder, off-stoichiometry and epitaxial strain on the optical properties of magnetoelectric gallium ferrite.

PubMed

Roy, Amritendu; Mukherjee, Somdutta; Sarkar, Surajit; Auluck, Sushil; Prasad, Rajendra; Gupta, Rajeev; Garg, Ashish

2012-10-31

We present a combined experimental-theoretical study demonstrating the role of site disorder, off-stoichiometry and strain on the optical properties of magnetoelectric gallium ferrite. Optical properties (bandgap, refractive indices and dielectric constants) were experimentally obtained by performing ellipsometric studies over the energy range 0.8-4.2 eV on pulsed laser deposited epitaxial thin films of stoichiometric gallium ferrite with b-axis orientation and the data were compared with theoretical results. Calculations on the ground state structure show that the optical activity in GaFeO(3) arises primarily from O 2p-Fe 3d transitions. Further, inclusion of site disorder and epitaxial strain in the ground state structure significantly improves the agreement between the theory and the room temperature experimental data substantiating the presence of site disorder in the experimentally derived strained GaFeO(3) films at room temperature. We attribute the modification of the ground state optical behavior upon inclusion of site disorder to the corresponding changes in the electronic band structure, especially in Fe 3d states leading to a lowered bandgap of the material.

Particle-size distribution modified effective medium theory and validation by magneto-dielectric Co-Ti substituted BaM ferrite composites

NASA Astrophysics Data System (ADS)

Li, Qifan; Chen, Yajie; Harris, Vincent G.

2018-05-01

This letter reports an extended effective medium theory (EMT) including particle-size distribution functions to maximize the magnetic properties of magneto-dielectric composites. It is experimentally verified by Co-Ti substituted barium ferrite (BaCoxTixFe12-2xO19)/wax composites with specifically designed particle-size distributions. In the form of an integral equation, the extended EMT formula essentially takes the size-dependent parameters of magnetic particle fillers into account. It predicts the effective permeability of magneto-dielectric composites with various particle-size distributions, indicating an optimal distribution for a population of magnetic particles. The improvement of the optimized effective permeability is significant concerning magnetic particles whose properties are strongly size dependent.

Halogenation of cobalt dicarbollide

DOEpatents

Hurlburt, P.K.; Abney, K.D.; Kinkead, S.A.

1997-05-20

A method for selectively adding chlorine, bromine, or iodine to cobalt dicarbollide anions by means of electrophilic substitution reactions. Halogens are added only to the B10 and B10{prime} positions of the anion. The process involves use of hypohalous acid or N-halosuccinimide or gaseous chlorine in the presence of iron. 1 fig.

Halogenation of cobalt dicarbollide

DOEpatents

Hurlburt, Paul K.; Abney, Kent D.; Kinkead, Scott A.

1997-01-01

A method for selectively adding chlorine, bromine, or iodine to cobalt dicarbollide anions by means of electrophilic substitution reactions. Halogens are added only to the B10 and B10' positions of the anion. The process involves use of hypohalous acid or N-halosuccinimide or gaseous chlorine in the presence of iron.

Could binary mixture of Nd-Ni ions control the electrical behavior of strontium-barium M-type hexaferrite nanoparticles?

DOE Office of Scientific and Technical Information (OSTI.GOV)

Iqbal, Muhammad Javed, E-mail: mjiqauchem@yahoo.com; Farooq, Saima

2011-05-15

Research highlights: {yields} Strontium-barium hexaferrites (Sr{sub 0.5}Ba{sub 0.5}Fe{sub 12}O{sub 19}) in single magnetoplumbite phase solid structure are synthesized by the co-precipitation method. {yields} Structural and electrical properties of Nd-Ni substituted ferrites are investigated. {yields} These ferrite materials possess high electrical resistivity (108 {Omega} cm) that is essential to curb the eddy current loss, which is pre-requisite for surface mount devices. -- Abstract: Cationic substitution in M-type hexaferrites is considered to be an important tool for modification of their electrical properties. This work is part of our comprehensive study on the synthesis and characterization of Nd-Ni doped strontium-barium hexaferrite nanomaterials ofmore » nominal composition Sr{sub 0.5}Ba{sub 0.5-x}Nd{sub x}Fe{sub 12-y}Ni{sub y}O{sub 19} (x = 0.00-0.10; y = 0.00-1.00). Doping with this binary mixture modulates the physical and electrical properties of strontium-barium hexaferrite nanoparticles. Structural and electrical properties of the co-precipitated ferrites are investigated using state-of-the-art techniques. The results of X-ray diffraction analysis reveal that the lattice parameters and cell volume are inversely related to the dopant content. Temperature dependent DC-electrical resistivity measurements infer that resistivity of strontium-barium hexaferrites decreases from 1.8 x 10{sup 10} to 2.0 x 10{sup 8} {Omega} cm whereas the drift mobility, dielectric constant and dielectric loss tangent are directly related to the Nd-Ni content. The results of the study demonstrate a relationship between the modulation of electrical properties of substituted ferrites and nature of cations and their lattice site occupancy.« less

Structural and magnetic properties of yttrium and lanthanum-doped Ni-Co and Ni-Co-Zn spinel ferrites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Stergiou, Charalampos, E-mail: stergiou@cperi.certh.gr; Litsardakis, George, E-mail: lits@eng.auth.gr

2014-11-05

Rare earth doping of Co-rich spinel ferrites is investigated through the preparation of two groups of polycrystalline Ni-Co and Ni-Co-Zn ferrites, where Fe is partly substituted by Y and La. The characterization of the sintered ferrites by means of X-ray powder diffraction and Rietveld profile analysis, indicates the subtle expansion of the spinel unit cell and the cation redistribution in the doped ferrites in order to accommodate the incorporation of Y and La in the lattice. The impurity traces, detected only in the Ni-Co-Zn group, is ascribed to the Zn population in the tetrahedral A-sites impeding the cation transfer. Moreover,more » the examined microstructure of the doped Ni-Co samples comprises enlarged and more homogeneous grains, whereas grain growth is moderated in the doped Ni-Co-Zn ferrites. The discussed characteristics of the crystal and magnetic structure along with the morphological aspects define the impact of Y and La doping on the static magnetic properties of Ni-Co and Ni-Co-Zn ferrites, saturation magnetization MS and coercivity HC, which were extracted from the respective hysteresis loops.« less

Effects on structural, optical, and magnetic properties of pure and Sr-substituted MgFe2O4 nanoparticles at different calcination temperatures

NASA Astrophysics Data System (ADS)

Loganathan, A.; Kumar, K.

2016-06-01

In the present work, pure and Sr2+ ions substituted Mg ferrite nanoparticles (NPs) had been prepared by co-precipitation method and their structural, optical, and magnetic properties at different calcination temperatures were studied. On this purpose, thermo gravimetric and differential thermal analysis (TG-DTA), Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), scanning electron microscopy, UV-Visible diffused reflectance spectroscopy, impedance spectroscopy, and vibrating sample magnetometer were carried out. The exo- and endothermic processes of synthesized precursors were investigated by TG-DTA measurements. The structural properties of the obtained products were examined by XRD analysis and show that the synthesized NPs are in the cubic spinel structure. The existence of two bands around 578-583 and 430-436 cm-1 in FT-IR spectrum also confirmed the formation of spinel-structured ferrite NPs. The lattice constants and particle size are estimated using XRD data and found to be strongly dependent on calcination temperatures. The optical, electrical, and magnetic properties of ferrite compositions also investigated and found to be strongly dependant on calcination temperatures.

Continuous cooling transformations and microstructures in a low-carbon, high-strength low-alloy plate steel

NASA Astrophysics Data System (ADS)

Thompson, S. W.; Vin, D. J., Col; Krauss, G.

1990-06-01

A continuous-cooling-transformation (CCT) diagram was determined for a high-strength low-alloy plate steel containing (in weight percent) 0.06 C, 1.45 Mn, 1.25 Cu, 0.97 Ni, 0.72 Cr, and 0.42 Mo. Dilatometric measurements were supplemented by microhardness testing, light microscopy, and transmission electron microscopy. The CCT diagram showed significant suppression of polygonal ferrite formation and a prominent transformation region, normally attributed to bainite formation, at temperatures intermediate to those of polygonal ferrite and martensite formation. In the intermediate region, ferrite formation in groups of similarly oriented crystals about 1 μm in size and containing a high density of dislocations dominated the transformation of austenite during continuous cooling. The ferrite grains assumed two morphologies, elongated or acicular and equiaxed or granular, leading to the terms “acicular ferrite” and “granular ferrite,” respectively, to describe these structures. Austenite regions, some transformed to martensite, were enriched in carbon and retained at interfaces between ferrite grains. Coarse interfacial ledges and the nonacicular morphology of the granular ferrite grains provided evidence for a phase transformation mechanism involving reconstructive diffusion of substitutional atoms. At slow cooling rates, polygonal ferrite and Widmanstätten ferrite formed. These latter structures contained low dislocation densities and e-copper precipitates formed by an interphase transformation mechanism.

Enhanced electronic and magnetic properties by functionalization of monolayer GaS via substitutional doping and adsorption.

PubMed

Ur Rahman, Altaf; Rahman, Gul; Kratzer, Peter

2018-05-16

The structural, electronic, and magnetic properties of two-dimensional (2D) GaS are investigated using density functional theory (DFT). After confirming that the pristine 2D GaS is a non-magnetic, indirect band gap semiconductor, we consider N and F as substitutional dopants or adsorbed atoms. Except for N substituting for Ga (N Ga ), all considered cases are found to possess a magnetic moment. Fluorine, both in its atomic and molecular form, undergoes a highly exothermic reaction with GaS. Its site preference (F S or F Ga ) as substitutional dopant depends on Ga-rich or S-rich conditions. Both for F Ga and F adsorption at the Ga site, a strong F-Ga bond is formed, resulting in broken bonds within the GaS monolayer. As a result, F Ga induces p-type conductivity in GaS, whereas F S induces a dispersive, partly occupied impurity band about 0.5 e below the conduction band edge of GaS. Substitutional doping with N at both the S and the Ga site is exothermic when using N atoms, whereas only the more favourable site under the prevailing conditions can be accessed by the less reactive N 2 molecules. While N Ga induces a deep level occupied by one electron at 0.5 eV above the valence band, non-magnetic N S impurities in sufficiently high concentrations modify the band structure such that a direct transition between N-induced states becomes possible. This effect can be exploited to render monolayer GaS a direct-band gap semiconductor for optoelectronic applications. Moreover, functionalization by N or F adsorption on GaS leads to in-gap states with characteristic transition energies that can be used to tune light absorption and emission. These results suggest that GaS is a good candidate for design and construction of 2D optoelectronic and spintronics devices.

Impact of Gd3+/graphene substitution on the physical properties of magnesium ferrite nanocomposites

NASA Astrophysics Data System (ADS)

Ateia, Ebtesam E.; Mohamed, Amira T.; Elsayed, Kareem

2018-04-01

Magnesium nano ferrite with composition MgFe2O4, MgGd0.05Fe1.95O4 and MgFe2O4 - 5 wt% GO was synthesized using a citrate auto-combustion method. The crystal structure, morphology, and magnetic properties of the investigated samples were studied. High Resolution Transmission Electron Microscopy (HRTEM) images show that the substitution of small amounts of Gd3+/GO causes a considerable reduction of the grain size. Studies on the magnetic properties demonstrate that the coercivity of GO-substituted magnesium nano ferrites is enhanced from 72 Oe to 203 Oe and the magnetocrystalline anisotropy constant increases from 1171 to 3425 emu Oe/gm at 300 K. The direct effects of graphene on morphology, crystal structure as well as the magnetic properties reveal that the studied sample are suitable for turbidity color and removal. The magnetic entropy change is estimated from magnetization data using Maxwell relation. The calculated Curie temperature from the Curie-Weiss law and the maximum entropy change are in good agreement with each other. Based on UV diffuse reflectance spectroscopy studies, the optical band gaps are in the range of 1.4-2.15 eV. In addition, the combination of small particle size and good magnetic properties makes the investigated samples act as a potential candidates for superior catalysts, adsorbents, and electromagnetic wave absorbers.

Mesoscopic monodisperse ferromagnetic colloids enable magnetically controlled photonic crystals.

PubMed

Xu, Xiangling; Majetich, Sara A; Asher, Sanford A

2002-11-20

We report here the first synthesis of mesoscopic, monodisperse particles which contain nanoscopic inclusions of ferromagnetic cobalt ferrites. These monodisperse ferromagnetic composite particles readily self-assemble into magnetically responsive photonic crystals that efficiently Bragg diffract incident light. Magnetic fields can be used to control the photonic crystal orientation and, thus, the diffracted wavelength. We demonstrate the use of these ferromagnetic particles to fabricate magneto-optical diffracting fluids and magnetically switchable diffracting mirrors.

Effect of Fe and Co substitution on the martensitic stability and the elastic, electronic, and magnetic properties of Mn2NiGa : Insights from ab initio calculations

NASA Astrophysics Data System (ADS)

Kundu, Ashis; Ghosh, Sheuly; Ghosh, Subhradip

2017-11-01

We investigate the effects of Fe and Co substitutions on the phase stability of the martensitic phase and mechanical, electronic, and magnetic properties of the magnetic shape memory system Mn2NiGa by first-principles density functional theory calculations. The evolution of these aspects upon substitution of Fe and Co at different crystallographic sites is investigated by computing the electronic structure, mechanical properties (tetragonal shear constant, Pugh ratio, and Cauchy pressure), and magnetic exchange parameters. We find that the austenite phase of Mn2NiGa gradually stabilizes with increase in concentration of Fe/Co due to the weakening of the minority spin hybridization of Ni and Mn atoms occupying crystallographically equivalent sites. The interplay between relative structural stability and the compositional changes is understood from the variations in the elastic moduli and electronic structures. We find that like in the Ni2MnGa -based systems, the elastic shear modulus C' can be considered as a predictor of composition dependence of martensitic transformation temperature Tm in substituted Mn2NiGa , thus singling it out as the universally acceptable predictor for martensitic transformation in Ni-Mn-Ga compounds over a wide composition range. The magnetic properties of Mn2NiGa are found to be greatly improved by the substitutions due to stronger ferromagnetic interactions in the compounds. The gradually weaker (stronger) Jahn-Teller distortion (covalent bonding) in the minority spin densities of states due to substitutions leads to a half-metallic-like gap in these compounds resulting in materials with high spin polarization when the substitutions are complete. The substitutions at the Ga site result in the two compounds Mn2NiFe and Mn2NiCo with very high magnetic moments and Curie temperatures. Thus, our work indicates that although the substitutions destroy the martensitic transformation and thus the possibility of realization of shape memory properties in Mn2NiGa , magnetic materials with very good magnetic parameters that are potentially useful for novel magnetic applications can be obtained. This can trigger interest in the experimental community in further research on substituted Mn2NiGa .

Amphoteric Be in GaN: Experimental Evidence for Switching between Substitutional and Interstitial Lattice Sites.

PubMed

Tuomisto, Filip; Prozheeva, Vera; Makkonen, Ilja; Myers, Thomas H; Bockowski, Michal; Teisseyre, Henryk

2017-11-10

We show that Be exhibits amphoteric behavior in GaN, involving switching between substitutional and interstitial positions in the lattice. This behavior is observed through the dominance of Be_{Ga} in the positron annihilation signals in Be-doped GaN, while the emergence of V_{Ga} at high temperatures is a consequence of the Be impurities being driven to interstitial positions. The similarity of this behavior to that found for Na and Li in ZnO suggests that this could be a universal property of light dopants substituting for heavy cations in compound semiconductors.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Abreu-Sepulveda, Maria A.; Dhital, Chetan; Huq, Ashfia

The effect due to systematic substitution of cobalt by iron in La 0.6Ca 0.4Co 1-xFe xO 3 towards the oxygen evolution reaction(OER) in alkaline media has been investigated. We synthesized these compounds by a facile glycine-nitrate synthesis and the phase formation was confirmed by X-ray diffraction and Neutron Diffraction elemental analysis. The apparent OER activity was evaluated by quasi steady state current measurements in alkaline media using a traditional three-electrode cell. X-ray photoelectron spectroscopy shows iron substitution causes an increase in the surface concentration of various cobalt oxidation states. Tafel slope in the vicinity of 60 mV/decade and electrochemical reactionmore » order towards OH- near unity were achieved for the unsubstituted La 0.6Ca 0.4CoO 3. Moreover, a decrease in the Tafel slope to 49 mV/decade was observed when iron is substituted in high amounts in the perovskite structure. The area specific current density showed dependence on the Fe fraction, however the relationship of specific current density with Fe fraction is not linear. High Fe substitutions, La 0.6Ca 0.4Co 0.2Fe 0.8O 3 and La 0.6Ca 0.4Co 0.1Fe 0.9O 3 showed higher area specific activity towards OER than La 0.6Ca 0.4CoO 3 or La 0.6Ca 0.4FeO 3. Finally, we believe iron inclusion in the cobalt sites of the perovskite helps decrease the electron transfer barrier and facilitates the formation of cobalt-hydroxide at the surface. Possible OER mechanisms based on the observed kinetic parameters will be discussed.« less

Interdependence between electrical and magnetic properties of polycrystalline cobalt-substituted tungsten bronze multiferroic ceramics

NASA Astrophysics Data System (ADS)

Jindal, Shilpi; Devi, Sheela; Vasishth, Ajay; Batoo, Khalid Mujasam; Kumar, Gagan

Polycrystalline cobalt-substituted tungsten bronze ferroelectric ceramics with chemical composition Ba5CaTi2-xCoXNb8O30 (x=0.00, 0.02, 0.04 and 0.08) were synthesized by solid state reaction technique. X-ray diffraction (XRD) technique was used to confirm the phase formation and it revealed the formation of single phase tetragonal structure with space group P4bm. The surface morphology of the samples was studied by using the scanning electron microscopy (SEM) technique. The dielectric properties such as dielectric constant and dielectric loss have been investigated as a function of temperature and frequency. The P-E and M-H studies confirmed the coexistent of ferroelectricity and magnetism at room temperature. The P-E loop study indicated an increase in the coercive field while the M-H study depicted a decrease in the magnetization with the incorporation of cobalt ions.

A molecular approach to self-supported cobalt-substituted ZnO materials as remarkably stable electrocatalysts for water oxidation.

PubMed

Pfrommer, Johannes; Lublow, Michael; Azarpira, Anahita; Göbel, Caren; Lücke, Marcel; Steigert, Alexander; Pogrzeba, Martin; Menezes, Prashanth W; Fischer, Anna; Schedel-Niedrig, Thomas; Driess, Matthias

2014-05-12

In regard to earth-abundant cobalt water oxidation catalysts, very recent findings show the reorganization of the materials to amorphous active phases under catalytic conditions. To further understand this concept, a unique cobalt-substituted crystalline zinc oxide (Co:ZnO) precatalyst has been synthesized by low-temperature solvolysis of molecular heterobimetallic Co(4-x)Zn(x) O4 (x = 1-3) precursors in benzylamine. Its electrophoretic deposition onto fluorinated tin oxide electrodes leads after oxidative conditioning to an amorphous self-supported water-oxidation electrocatalyst, which was observed by HR-TEM on FIB lamellas of the EPD layers. The Co-rich hydroxide-oxidic electrocatalyst performs at very low overpotentials (512 mV at pH 7; 330 mV at pH 12), while chronoamperometry shows a stable catalytic current over several hours. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Effects of Gd-Substitutions on the Microstructure, Electrical and Electromagnetic Behavior of M-Type Hexagonal Ferrites

NASA Astrophysics Data System (ADS)

Ahmad, Ishtiaq; Ahmad, Mahmood; Ali, Ihsan; Kanwal, M.; Awan, M. S.; Mustafa, Ghulam; Ahmad, Mukhtar

2015-07-01

A series of Gd-substituted Ba-Co-based (M-type) hexaferrites having the chemical compositions of Ba0.5Co0.5Gd x Fe12- x O19 ( x = 0.0, 0.2, 0.4, 0.6, 0.8, 1.0) were prepared by co-precipitation method. The pellets formed by co-precipitated powder were calcined at a temperature of 1200°C for 20 h. Final sintering was done at 1320°C for 4 h. From the x-ray diffraction analysis, it was revealed that all the samples showed M-type hexagonal structure as a major phase. The scanning electron microscope was used to examine the morphology of the sintered ferrites. The average grain size estimated by the line intercept method was found to be in the range of 2.8-1.0 μm. The room temperature DC resistivity increases with increasing Gd-contents to make these ferrites useful for high frequency applications and microwave devices. Lower values of coercivity ( H c) and higher saturation magnetization ( M s) may be suitable to enhance the permeability of these ferrites, which is favorable for impedance matching in microwave absorption. In addition, reflection coefficients for a sample was also measured from a frequency of 1 MHz to 3 GHz and a reflection peak was observed at about 2.2 GHz.

Exploratory screening tests of several alloys and coatings for automobile thermal reactors

NASA Technical Reports Server (NTRS)

Oldrieve, R. E.

1971-01-01

A total of 23 materials (including uncoated ferritic and austenitic iron-base alloys, uncoated nickel and cobalt-base superalloys, and several different coatings on AISI 304 stainless steel) were screened as test coupons on a rack in an automobile thermal reactor. Test exposures were generally 51 hours including 142 thermal cycles of 10 minutes at 1010 + or - 30 C test coupon temperature and 7-minutes cool-down to about 510 C. Materials that exhibited corrosion resistance better than that of Hastelloy X include: a ferritic iron alloy with 6 weight percent aluminum; three nickel-base superalloys; two diffused-aluminum coatings on AISI 304; and a Ni-Cr slurry-sprayed coating on AISI 304. Preliminary comparison is made on the performance of the directly impinged coupons and a reactor core of the same material.

Novel catalysts and photoelectrochemical system for solar fuel production

NASA Astrophysics Data System (ADS)

Zhang, Yan

Solar fuel production from abundant raw chemicals such as CO2 and water is highly desired as a clean renewable energy solution for the future. Developing photoelectrochemical cells is viewed as a promising approach to realize this energy conversion and storage process. Efficient and robust oxygen evolution catalyst made from non-precious materials remains a major challenge for such a system. This thesis basically consists of three parts of work, including studies on enhancing the photocatalytic oxygen evolution activity of cobalt-based spinel nanoparticles by manganese3+ substitution, in situ formation of cobalt oxide nanocubanes as highly active catalyst for photocatalytic oxygen evolution reaction, and development of a photoanode-driven photoelectrochemical cell for CO2 reduction with water. The first part of this thesis work devotes efforts in the development and study on cobalt and other transition metal oxide based oxygen evolution catalyst. Photocatalytic oxygen evolution is a critical step for solar fuel production from abundant sources. It poses a significant challenge because it requires an efficient catalyst to bridge the one-electron photon capture process with the four-electron oxygen reaction. Among all the metal oxides, Co3O4 spinel exhibits a high activity as an oxygen evolution catalyst. The results of this work demonstrate that the photocatalytic oxygen evolution activity of Co3O4 spinel can be further enhanced by substituting Co with Mn in the spinel structure. Using a facile hydrothermal approach, Co3O4 spinel nanoparticles as well as Mn-substituted and Ni-substituted Co3O4 spinel nanoparticles with a typical particle size of 5-7 nm were successfully synthesized. The morphology and crystal structures of the as-synthesized nanoparticle catalysts have been carefully examined using various structural characterization techniques, including powder x-ray diffraction (PXRD), transmission electron microscope (TEM), gas adsorption, and x-ray absorption spectroscopy (XAS). The photocatalytic activities of as-made nanoparticles were investigated using a well-studied visible light driven [Ru(bpy)3]2+-persulfate system. In both Clark electrode and reactor/gas chromatography (GC) systems, Mn-substituted Co3O 4 nanoparticles exhibited the highest turnover frequency (TOF) among all the three kinds of catalysts. The data presented in this paper suggest that the photocatalytic oxygen evolution activity of Co3O 4 spinel catalyst can be further enhanced by Mn3+ substitution at the octahedral sites. The second part of this piece of work was carried out to further investigate cobalt oxide based photocatalytic oxygen evolution catalyst. A new strategy was developed to synthesize nonsupported cobalt oxide nanocubanes through an in situ phase transformation mechanism using a layered Co(OH)(OCH3) precursor. Under sonication, the precursor was exfoliated and transformed into cobalt oxide nanocubanes in the presence of NaHCO 3-Na2SiF6 buffer solution. The resulting cobalt catalyst with an average particle size less than 2 nm exhibited a turnover frequency of 0.0023 per second per cobalt in photocatalytic oxygen evolution reaction. X-ray absorption results suggested that a unique nanocubane structure, where 13 cobalt atoms fully coordinated with oxygen atoms and hydroxide groups in an octahedral arrangement to form 8 Co4O4 cubanes, may be responsible for the exceptionally high oxygen evolution catalysis activity. This thesis work is completed with the development of a photoanode-driven photoelectrochemical cell for CO2 reduction. A NiOx decorated Si photoanode and nanoporous Ag cathode were employed. With an external bias of 2.0 V, a current density at cathode of 10 mA/cm2 and Faradaic efficiency of 70% for CO2 to CO was achieved. Compared to a normal electrochemical cell, the photoelectrochemical cell saves 0.4 V electrical energy by absorbing photo-energy. In addition, post-test photoanodes were carefully characterized by SEM, XAS, and XPS analysis.

Nano-crystalline Magnesium Substituted Cadmium Ferrites as X-band Microwave Absorbers

NASA Astrophysics Data System (ADS)

Bhongale, S. R.; Ingawale, H. R.; Shinde, T. J.; Pubby, Kunal; Bindra Narang, Sukhleen; Vasambekar, P. N.

2017-11-01

The magnetic and electromagnetic properties of nanocrystalline spinel ferrites with chemical formula MgxCd1-xFe2O4 (x = 0, 0.2, 0.4, 0.6, 0.8 and 1.0) prepared by oxalate co-precipitation method under microwave sintering technique were studied. The magnetic and dielectric parameters of ferrites were determined by using vibrating sample magnetometer (VSM) and vector network analyzer (VNA) respectively. Magnetic parameters such as saturation magnetizations (Ms), coercive force (Hc), remnant magnetization (Mr), Yafet-Kittel (Y-K) angle of ferrites were determined from hysteresis loops. The variation of real permittivity (ε‧), dielectric loss tangent (tanδe), real permeability (μ‧) and magnetic loss tangent (tanδm) with frequency and Mg2+content were studied in X-band frequency range. The values of ε‧, tanδe, μ‧ and tanδm of ferrites were observed to be in range of 4.2 - 6.12, 2.9 × 10-1 - 6 × 10-2, 0.6 - 1.12 and 4.5 × 10-1 - 2 × 10-3 respectively for the prepared compositions. The study of variation of reflection loss with frequency of all ferrites shows that ferrite with magnesium content x = 0.4 can be potential candidate for microwave applications in X-band.

Protective effects of kolaviron and gallic acid against cobalt-chloride-induced cardiorenal dysfunction via suppression of oxidative stress and activation of the ERK signaling pathway.

PubMed

Akinrinde, Akinleye Stephen; Omobowale, Olutayo; Oyagbemi, Ademola; Asenuga, Ebunoluwa; Ajibade, Temitayo

2016-12-01

Cobalt (Co) toxicity is a potential public health problem due to recent renewed use of Co in orthopedic implants, dietary supplements, and blood doping in athletes and horses. We investigated the protective roles of kolaviron (KV), a bi-flavonoid of Garcinia kola, and gallic acid (GA) on cobalt chloride (CoCl 2 )-induced cardiorenal damage in rats. CoCl 2 caused significant increases (p < 0.05) in serum creatine kinase-myocardial band (CK-MB), lactate dehydrogenase (LDH), aspartate transaminase (AST), xanthine oxidase (XO), urea, creatinine, malondialdehyde, H 2 O 2 , nitric oxide, as well as C-reactive protein expression, along with significant (p < 0.05) reduction in cardiac and renal expression of extracellular signal regulated kinase (ERK) and the activities of superoxide dismutase, catalase, and glutathione S-transferase. KV and GA prevented the toxic effects of CoCl 2 by stimulating ERK expression and reversing Co-induced biochemical changes. Administration of CoCl 2 alone did not significantly alter ECG patterns in the rats, although co-treatment with KV (200 mg/kg) produced QT-segment prolongation and also appeared to potentiate Co hypotension. Histopathology of the heart and kidneys of rats treated with KV and GA confirmed the biochemical data. KV and GA thus protected against cardiac and renal damage in Co intoxication via antioxidant and (or) cell survival mechanisms, possibly involving ERK activation.

CSMP (Continuous System Modeling Program) Modeling of Brushless DC Motors.

DTIC Science & Technology

1984-09-01

Characteristics of Fifteen HP Samarium Cobalt and Ferrite Based brushless DC Ictcrs j. Operated by the Same Power Conditioner ," IEEE Transactions on Pcwer stenM...paratus and Systeis, v. P -Ii-- -ry Demerdash, N.A. and Nehl.T.W., Dynamic Modeling cf Brushless DC Motor-Power Conditioner U if-- fo -- Iec tro me...III _J- _ o 0 NAVAL POSTGRADUATE SCHOOL Monterey, California •S THETIS CSMP MODEL{ING OF BRUSHLESS DC MOTORS by DTIC

Improved transistor-controlled and commutated brushless DC motors for electric vehicle propulsion

NASA Technical Reports Server (NTRS)

Demerdash, N. A.; Miller, R. H.; Nehl, T. W.; Nyamusa, T. A.

1983-01-01

The development, design, construction, and testing processes of two electronically (transistor) controlled and commutated permanent magnet brushless dc machine systems, for propulsion of electric vehicles are detailed. One machine system was designed and constructed using samarium cobalt for permanent magnets, which supply the rotor (field) excitation. Meanwhile, the other machine system was designed and constructed with strontium ferrite permanent magnets as the source of rotor (field) excitation. These machine systems were designed for continuous rated power output of 15 hp (11.2 kw), and a peak one minute rated power output of 35 hp (26.1 kw). Both power ratings are for a rated voltage of 115 volts dc, assuming a voltage drop in the source (battery) of about 5 volts. That is, an internal source voltage of 120 volts dc. Machine-power conditioner system computer-aided simulations were used extensively in the design process. These simulations relied heavily on the magnetic field analysis in these machines using the method of finite elements, as well as methods of modeling of the machine power conditioner system dynamic interaction. These simulation processes are detailed. Testing revealed that typical machine system efficiencies at 15 hp (11.2 kw) were about 88% and 84% for the samarium cobalt and strontium ferrite based machine systems, respectively. Both systems met the peak one minute rating of 35 hp.

Preparation of silica coated cobalt ferrite magnetic nanoparticles for the purification of histidine-tagged proteins

NASA Astrophysics Data System (ADS)

Aygar, Gülfem; Kaya, Murat; Özkan, Necati; Kocabıyık, Semra; Volkan, Mürvet

2015-12-01

Surface modified cobalt ferrite (CoFe2O4) nanoparticles containing Ni-NTA affinity group were synthesized and used for the separation of histidine tag proteins from the complex matrices through the use of imidazole side chains of histidine molecules. Firstly, CoFe2O4 nanoparticles with a narrow size distribution were prepared in an aqueous solution using the controlled co-precipitation method. In order to obtain small CoFe2O4 agglomerates, oleic acid and sodium chloride were used as dispersants. The CoFe2O4 particles were coated with silica and subsequently the surface of these silica coated particles (SiO2-CoFe2O4) was modified by amine (NH2) groups in order to add further functional groups on the silica shell. Then, carboxyl (-COOH) functional groups were added to the SiO2-CoFe2O4 magnetic nanoparticles through the NH2 groups. After that Nα,Nα-Bis(carboxymethyl)-L-lysine hydrate (NTA) was attached to carboxyl ends of the structure. Finally, the surface modified nanoparticles were labeled with nickel (Ni) (II) ions. Furthermore, the modified SiO2-CoFe2O4 magnetic nanoparticles were utilized as a new system that allows purification of the N-terminal His-tagged recombinant small heat shock protein, Tpv-sHSP 14.3.

Investigations on microstructure, electrical and magnetic properties of copper spinel ferrite with WO3 addition for applications in the humidity sensors

NASA Astrophysics Data System (ADS)

Tudorache, Florin

2018-04-01

In the present study we report the structural, electrical, magnetic and humidity characteristics of copper ferrite with different percent on tungsten trioxide addition. The aim of this study was to obtain more stable and sensitive active materials for humidity sensors. In order to highlight the influence of tungsten on the structural, electrical and magnetic properties, the ferrite samples were fabricated via sol-gel self-combustion method and sintered for 30 min at 1000 °C with percent between 0 and 20% tungsten trioxide additions. The X-ray diffraction investigations showed the copper ferrite phase composition. The scanning electron microscopy revealed the influence of the substitution on characteristics of the crystallites and the profilometry showed the surface topography of samples. The investigation was focused on the variation of permittivity and electrical conductivity, in relation with tungsten trioxide addition, frequency and humidity. We have also, investigated the relevant magnetic characteristics of the copper ferrite material by highlighting the influence of tungsten trioxide addition on to Curie temperature and the permeability frequency characteristics. The data suggests that the copper ferrite with tungsten trioxide addition can be used as active material for humidity sensors.

Enhanced electronic and magnetic properties by functionalization of monolayer GaS via substitutional doping and adsorption

NASA Astrophysics Data System (ADS)

Rahman, Altaf Ur; Rahman, Gul; Kratzer, Peter

2018-05-01

The structural, electronic, and magnetic properties of two-dimensional (2D) GaS are investigated using density functional theory (DFT). After confirming that the pristine 2D GaS is a non-magnetic, indirect band gap semiconductor, we consider N and F as substitutional dopants or adsorbed atoms. Except for N substituting for Ga (NGa), all considered cases are found to possess a magnetic moment. Fluorine, both in its atomic and molecular form, undergoes a highly exothermic reaction with GaS. Its site preference (FS or FGa) as substitutional dopant depends on Ga-rich or S-rich conditions. Both for FGa and F adsorption at the Ga site, a strong F–Ga bond is formed, resulting in broken bonds within the GaS monolayer. As a result, FGa induces p-type conductivity in GaS, whereas FS induces a dispersive, partly occupied impurity band about 0.5 e below the conduction band edge of GaS. Substitutional doping with N at both the S and the Ga site is exothermic when using N atoms, whereas only the more favourable site under the prevailing conditions can be accessed by the less reactive N2 molecules. While NGa induces a deep level occupied by one electron at 0.5 eV above the valence band, non-magnetic NS impurities in sufficiently high concentrations modify the band structure such that a direct transition between N-induced states becomes possible. This effect can be exploited to render monolayer GaS a direct-band gap semiconductor for optoelectronic applications. Moreover, functionalization by N or F adsorption on GaS leads to in-gap states with characteristic transition energies that can be used to tune light absorption and emission. These results suggest that GaS is a good candidate for design and construction of 2D optoelectronic and spintronics devices.

[Spectroscopic studies on transition metal ions in colored diamonds].

PubMed

Meng, Yu-Fei; Peng, Ming-Sheng

2004-07-01

Transition metals like nickel, cobalt and iron have been often used as solvent catalysts in high pressure high temperature (HPHT) synthesis of diamond, and nickel and cobalt ions have been found in diamond lattice. Available studies indicated that nickel and cobalt ions could enter the lattice as interstitial or substitutional impurities and form complexes with nitrogen. Polarized microscopy, SEM-EDS, EPR, PL and FTIR have been used in this study to investigate six fancy color natural and synthetic diamonds in order to determine the spectroscopic characteristics and the existing forms of transition metal ions in colored diamond lattice. Cobalt-related optical centers were first found in natural chameleon diamonds, and some new nickel and cobalt-related optical and EPR centers have also been detected in these diamond samples.

Effects of cobalt on the microstructure of Udimet 700. M.S. Thesis Final Report

NASA Technical Reports Server (NTRS)

Engel, M. A.

1982-01-01

Cobalt, a critical and "strategic" alloying element in many superalloys, was systematically substituted by nickel in experimental alloys Udimet 700 containing 0.1, 4.3, 8.6, 12.8 and the standard 17.0 wt.% cobalt. Electrolytic and chemical extraction techniques, X-ray diffraction, scanning electron and optical microscopy were used for the microstructural studies. The total weight fraction of gamma' was not significantly affected by the cobalt content, although a difference in the size and quantities of the primary and secondary gamma' phases was apparent. The lattice parameters of the gamma' were found to increase with increasing cobalt content while the lattice mismatch between the gamma matrix and gamma' phases decreased. Other significant effects of cobalt on the weight fraction, distribution and formation of the carbide and boride phases as well as the relative stability of the experimental alloys during long-time aging are also discussed.

The substitution of aluminum for cobalt in nanostructured bainitic steels

NASA Astrophysics Data System (ADS)

Yang, Jing; Qiu, Hui; Xu, Pudong; Yu, Hui; Wang, Yuchen

2018-06-01

Two kinds of new steels are designed, in which the only difference is the use of the alloy element aluminum instead of cobalt. The effect of cobalt and aluminum addition on the microstructure and mechanical properties of high-carbon nanostructured bainitic steels was studied. The microstructure and mechanical properties achieved by a low temperature au tempering treatment were investigated by optical microscopy, X-ray diffraction, scanning and transmission electron microscopy and hardness, tension, impact tests. The experimental results show that better mechanical properties were achieved in the high-carbon Al-contained steel.

Effect of Gallium and Indium Co-Substituting on Upconversion Properties of Er/Yb:Yttrium Aluminum Garnet Powders Prepared by the Co-Precipitation Method.

PubMed

Zhang, Wei; Liang, Yun-Ling; Hu, Zheng-Fa; Feng, Zu-Yong; Lun, Ma; Zhang, Xiu-ping; Sheng, Xia; Liu, Qian; Luo, Jie

2016-04-01

Gallium and Indium co-substituted Yb, Er:YAG was fabricated through the chemical co-precipitation method. The formation process and structure of the Ga3+ and In3+ substituted phosphor powders were characterized by the X-ray diffraction, thermo-gravimetry analyzer, infrared spectra, and X-ray photoelectron spectroscopy, and the effects of Ga3+ and In3+ concentration on the luminescence properties were investigated by spectrum. The results showed that the blue shift occurred after the substitution of Ga3+ and In3+ for Al3+ in matrix, and the intensity of emission spectrum was affected by the concentration of Ga3+ and In3+.

Structural, dielectric and impedance spectroscopic studies of Ni0.5Zn0.5-xLixFe2O4 nanocrystalline ferrites

NASA Astrophysics Data System (ADS)

Venkatesh, Davuluri; Ramesh, K. V.

2017-09-01

Nanocrystalline lithium substituted Ni-Zn ferrites with composition Ni0.5Zn0.5-xLixFe2O4 (x = 0.00-0.25 in steps of 0.05) were synthesized by the citrate gel auto-combustion method and were sintered at 1000∘C for 4 h in air atmosphere. The structural, dielectric, impedance spectroscopic and magnetic properties were studied by using X-ray diffraction, impedance analyzer and vibrating sample magnetometer respectively. The X-ray diffraction patterns confirm that all samples exhibit a single phase cubic spinel structure. Suitable cation distribution for all compositions has been proposed by using the X-ray diffraction line intensity calculations and the theoretical lattice parameter for each composition was observed in close agreement with the experimental ones and thereby supporting the proposed distribution. An increase in the saturation magnetization was observed up to x = 0.10 level of Li+ substitution and thereafter magnetization reduced for higher concentrations to the highest level of Li+ substitution. The dielectric constant and the DC resistivity of Ni-Zn-Li ferrites were noticed to decrease with increase in the Li+ ion concentration. The impedance spectroscopic studies by using the Cole-Cole plots were studied in order to obtain the relaxation time, grain resistance and grain capacitance. AC conductivity initially remained almost independent of frequency for lower frequencies and thereafter for higher frequencies the AC conductivity increased with increase of Lithium concentration.

Magnetic moment directions and distributions of cations in Cr (Co) substituted spinel ferrites Ni{sub 0.7}Fe{sub 2.3}O{sub 4}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xue, L. C.; Lang, L. L.; Li, Z. Z.

2015-09-15

Powder samples of the spinel ferrites M{sub x}Ni{sub 0.7−x}Fe{sub 2.3}O{sub 4} (M = Cr, Co and 0.0 ≤ x ≤ 0.3) and Cr{sub x}Ni{sub 0.7}Fe{sub 2.3−x}O{sub 4} (0.0 ≤ x ≤ 0.3) were synthesized using the chemical co-precipitation method. The XRD spectra confirmed that the samples had a single-phase cubic spinel structure. Magnetic measurements showed that the magnetic moments (μ{sub exp}) per formula both at 10 K and 300 K increased with Co substitution, while the values of μ{sub exp} decreased with Cr substitution. Applying the assumption that the magnetic moments of Cr{sup 2+} and Cr{sup 3+} lie antiparallel tomore » those of the divalent and trivalent Fe, Co, and Ni cations in the same sublattice of spinel ferrites, these interesting behaviors could be easily interpreted. The cation distributions of the three series of samples were estimated successfully by fitting the dependences of μ{sub exp}, measured at 10 K, on the doping level x, using a quantum-mechanical potential barrier model earlier proposed by our group. The results obtained for the Cr cation distributions at the (A) and [B] sites are very close to those obtained elsewhere using neutron diffraction.« less

Influence of Co content on the biocompatibility and bio-corrosion of super ferritic stainless steels

NASA Astrophysics Data System (ADS)

Yoo, Y. R.; Jang, S. G.; Nam, H. S.; Shim, G. T.; Cho, H. H.; Kim, J. G.; Kim, Y. S.

2008-12-01

Bio-metals require high corrosion resistance, because their biocompatibility is closely related to this parameter. Bio-metals release metal ions into the human body, leading to deleterious effects. Allergies, dermatitis, and asthma are the predominant systemic effects resulting in the human body. In particular, Ni is one of the most common causes of allergic contact dermatitis. In the present work, we designed new ferritic stainless steels wherein Ni is replaced with Co under consideration of allergic respondes and microstructural stability. This work focuses on the effect of Co content on the biocompatibility and corrosion resistance of high PRE super ferritic stainless steels in bio-solution and acidic chloride solution. In the case of the acidic chloride solution, with increasing Co content in the ferritic stainless steels, passive current density increased and critical pitting temperature (CPT) decreased. Also, in the passive state, AC impedance and repassivation rate were reduced. These results are attributed to the thermodynamic stability of cobalt ions, as indicated in the EpH diagram for a Co-H2O system. However, in the case of bio-solutions, with increasing Co content of the alloys, the passive current density decreased. AC impedance and repassivation rate meanwhile increased in the passive state. This is due to the increased ratios of Cr2O3/Cr(OH)3 and [Metal Oxide]/Metal + Metal Oxide] of the passive film formed in bio-solution.

XMCD and XMCD-PEEM Studies on Magnetic-Field-Assisted Self-Assembled 1D Nanochains of Spherical Ferrite Particles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Wen; Wong, Ping Kwan Johnny; Zhang, Dong

Quasi-1D nanochains of spherical magnetic ferrite particles with a homogeneous particle size of ≈200 nm and a micrometer-sized chain length are fabricated in this paper via a self-assembly method under an external magnetic field. This assisting magnetic field (H assist), applied during synthesis, significantly modifies the distribution of the Fe 2+O h, Fe 3+T d, and Fe 3+O h cations in the chains, as demonstrated by X-ray magnetic circular dichroism (XMCD) combined with theoretical analysis. This provides direct evidence of the nontrivial role of external synthetic conditions for defining the crystal chemistry of nanoscale ferrites and in turn their magneticmore » properties, providing an extra degree of freedom for intentional control over the performances of 1D magnetic nanodevices for various applications. Magnetic imaging, performed via XMCD in photoemission electron microscopy, further shows the possibility of creating and trapping a series of adjacent magnetic domain walls in a single chain, suggesting that there is great application potential for these nanochains in 1D magnetic nanodevices, as determined by field- or current-driven domain wall motions. Finally, practical control over the magnetic properties of the nanochains is also achieved by extrinsic dopants of cobalt and zinc, which are observed to occupy the ferrite ionic sites in a selective manner.« less

XMCD and XMCD-PEEM Studies on Magnetic-Field-Assisted Self-Assembled 1D Nanochains of Spherical Ferrite Particles

DOE PAGES

Zhang, Wen; Wong, Ping Kwan Johnny; Zhang, Dong; ...

2017-05-30

Quasi-1D nanochains of spherical magnetic ferrite particles with a homogeneous particle size of ≈200 nm and a micrometer-sized chain length are fabricated in this paper via a self-assembly method under an external magnetic field. This assisting magnetic field (H assist), applied during synthesis, significantly modifies the distribution of the Fe 2+O h, Fe 3+T d, and Fe 3+O h cations in the chains, as demonstrated by X-ray magnetic circular dichroism (XMCD) combined with theoretical analysis. This provides direct evidence of the nontrivial role of external synthetic conditions for defining the crystal chemistry of nanoscale ferrites and in turn their magneticmore » properties, providing an extra degree of freedom for intentional control over the performances of 1D magnetic nanodevices for various applications. Magnetic imaging, performed via XMCD in photoemission electron microscopy, further shows the possibility of creating and trapping a series of adjacent magnetic domain walls in a single chain, suggesting that there is great application potential for these nanochains in 1D magnetic nanodevices, as determined by field- or current-driven domain wall motions. Finally, practical control over the magnetic properties of the nanochains is also achieved by extrinsic dopants of cobalt and zinc, which are observed to occupy the ferrite ionic sites in a selective manner.« less

Study of cation magnetic moment directions in Cr (Co) doped nickel ferrites

NASA Astrophysics Data System (ADS)

Lang, L. L.; Xu, J.; Qi, W. H.; Li, Z. Z.; Tang, G. D.; Shang, Z. F.; Zhang, X. Y.; Wu, L. Q.; Xue, L. C.

2014-09-01

Powder samples of the ferrites MxNi1-xFe2O4 (M = Cr, Co and 0.0 ≤ x ≤ 0.3) were prepared using a chemical co-precipitation method. X-ray diffraction analysis showed that the two series of samples had a single-phase cubic spinel structure. It was found that the magnetic moments (μexp) per formula of samples measured at 10 K decreased when Cr substituted for Ni, but increased when Co substituted for Ni, in spite of the fact that the magnetic moments of Cr2+ (4 μB) and Co2+ (3 μB) are higher than that of Ni2+ (2 μB). With the assumption that the magnetic moments of Cr2+ and Cr3+ lie antiparallel to those of the Fe, Co, and Ni cations in the same sublattices of spinel ferrites, the dependences on the Cr (Co) doping level of the sample magnetic moments at 10 K were fitted successfully, using the quantum-mechanical potential barrier model earlier proposed by our group. For the two series of samples, the fitted magnetic moments are close to the experimental results.

Increasing the formability of ferritic stainless steel tube by granular medium-based hot forming

NASA Astrophysics Data System (ADS)

Chen, H.; Staupendahl, D.; Hiegemann, L.; Tekkaya, A. E.

2017-09-01

Ferritic stainless steel without the alloy constituent nickel is an economical substitution for austenitic stainless steel in the automotive industry. Its lower formability, however, oftentimes prevents the direct material substitution in forming processes such as hydroforming, necessitating new forming strategies. To extend the forming capacity of ferritic stainless steel tube, the approach of forming at elevated temperatures is proposed. Utilizing granular material as forming medium, high forming temperatures up to 900°C are realized. The forming process works by moving punches axially into the granular medium, thereby, compressing it and causing axial as well as radial pressure. In experimental and numerical investigations it is shown that interfacial friction between the granular medium and the tube inherently causes tube feed, resulting in stain states in the tension-compression region of the FLD. Formability data for this region are gained by notched tensile tests, which are performed at room temperature as well as at elevated temperatures. The measured data show that the formability is improved at forming temperatures higher than 700°C. This observed formability increase is experimentally validated using a demonstrator geometry, which reaches expansion ratios that show fracture in specimens formed at room temperature.

Characterization of Sr-substituted W-type hexagonal ferrites synthesized by sol-gel autocombustion method

NASA Astrophysics Data System (ADS)

Ahmad, Mukhtar; Grössinger, R.; Kriegisch, M.; Kubel, F.; Rana, M. U.

2013-04-01

The magnetic and microwave characterization of single phase hexaferrites of entirely new composition Ba1-xSrxCo2AlFe15O27 (x=0.2-1.0) for application in a microwave absorber, have been reported. The samples synthesized by sol-gel method were investigated by differential thermal analyzer, Fourier transform infrared spectroscope, X-ray diffractometer, field emission gun scanning electron microscope, vibrating sample magnetometer and vector network analyzer. Platelet grains exhibit well defined hexagonal shape which is a better shape for microwave absorption. M-H loops for a selected sample were measured for a temperature range of 4.2-400 K. Moreover M-H loops for all Sr-substituted samples were also measured at room temperature up to a maximum applied field of 9 T. Saturation magnetization values were calculated by the law of approach to saturation. The room temperature coercivity for all the samples is found to be a few hundred oersteds which is necessary for electromagnetic materials and makes these ferrites ideal for microwave devices, security, switching and sensing applications. The complex permittivity, permeability and reflection losses of a selected ferrite-epoxy composite were also investigated over a frequency range of 0.5-13 GHz.

Synthesis and magnetic properties of cobalt-iron/cobalt-ferrite soft/hard magnetic core/shell nanowires

NASA Astrophysics Data System (ADS)

Leandro Londoño-Calderón, César; Moscoso-Londoño, Oscar; Muraca, Diego; Arzuza, Luis; Carvalho, Peterson; Pirota, Kleber Roberto; Knobel, Marcelo; Pampillo, Laura Gabriela; Martínez-García, Ricardo

2017-06-01

A straightforward method for the synthesis of CoFe2.7/CoFe2O4 core/shell nanowires is described. The proposed method starts with a conventional pulsed electrodeposition procedure on alumina nanoporous template. The obtained CoFe2.7 nanowires are released from the template and allowed to oxidize at room conditions over several weeks. The effects of partial oxidation on the structural and magnetic properties were studied by x-ray spectrometry, magnetometry, and scanning and transmission electron microscopy. The results indicate that the final nanowires are composed of 5 nm iron-cobalt alloy nanoparticles. Releasing the nanowires at room conditions promoted surface oxidation of the nanoparticles and created a CoFe2O4 shell spinel-like structure. The shell avoids internal oxidation and promotes the formation of bi-magnetic soft/hard magnetic core/shell nanowires. The magnetic properties of both the initial single-phase CoFe2.7 nanowires and the final core/shell nanowires, reveal that the changes in the properties from the array are due to the oxidation more than effects associated with released processes (disorder and agglomeration).

Synthesis and magnetic properties of cobalt-iron/cobalt-ferrite soft/hard magnetic core/shell nanowires.

PubMed

Londoño-Calderón, César Leandro; Moscoso-Londoño, Oscar; Muraca, Diego; Arzuza, Luis; Carvalho, Peterson; Pirota, Kleber Roberto; Knobel, Marcelo; Pampillo, Laura Gabriela; Martínez-García, Ricardo

2017-06-16

A straightforward method for the synthesis of CoFe 2.7 /CoFe 2 O 4 core/shell nanowires is described. The proposed method starts with a conventional pulsed electrodeposition procedure on alumina nanoporous template. The obtained CoFe 2.7 nanowires are released from the template and allowed to oxidize at room conditions over several weeks. The effects of partial oxidation on the structural and magnetic properties were studied by x-ray spectrometry, magnetometry, and scanning and transmission electron microscopy. The results indicate that the final nanowires are composed of 5 nm iron-cobalt alloy nanoparticles. Releasing the nanowires at room conditions promoted surface oxidation of the nanoparticles and created a CoFe 2 O 4 shell spinel-like structure. The shell avoids internal oxidation and promotes the formation of bi-magnetic soft/hard magnetic core/shell nanowires. The magnetic properties of both the initial single-phase CoFe 2.7 nanowires and the final core/shell nanowires, reveal that the changes in the properties from the array are due to the oxidation more than effects associated with released processes (disorder and agglomeration).

Magnetic and dielectric behavior of chromium substituted Co-Mg ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Jadoun, Priya; Jyoti, Prashant, B. L.; Dolia, S. N.; Bhatnagar, D.; Saxena, V. K.

2016-05-01

The chromium doped Co-Mg ferrite with composition Co0.5Mg0.5Cr0.2Fe1.8O4 has been synthesized using sol-gel auto combustion method. The crystal structure has been analyzed by X-ray diffraction (XRD) technique. XRD pattern reveals the formation of single phase cubic spinel structure. The magnetic measurements show ferromagnetic behavior at room temperature and large coercivity is observed on cooling down the temperature to 20 K. Dielectric constant (ɛ') and dielectric loss tangent (tan δ) have been determined at room temperature as a function of frequency in the frequency range 75 kHz to 80 MHz. The decrease in dielectric constant with increasing frequency attributes to Maxwell Wagner model and conduction mechanism in ferrites.

Amphoteric Be in GaN: Experimental Evidence for Switching between Substitutional and Interstitial Lattice Sites

NASA Astrophysics Data System (ADS)

Tuomisto, Filip; Prozheeva, Vera; Makkonen, Ilja; Myers, Thomas H.; Bockowski, Michal; Teisseyre, Henryk

2017-11-01

We show that Be exhibits amphoteric behavior in GaN, involving switching between substitutional and interstitial positions in the lattice. This behavior is observed through the dominance of BeGa in the positron annihilation signals in Be-doped GaN, while the emergence of VGa at high temperatures is a consequence of the Be impurities being driven to interstitial positions. The similarity of this behavior to that found for Na and Li in ZnO suggests that this could be a universal property of light dopants substituting for heavy cations in compound semiconductors.

Studies on conducting nanocomposite with gallium nitride-doped ferrite, part - III wasp-waist formation

NASA Astrophysics Data System (ADS)

Indrakanti, Rajani; Rao, V. Brahmaji; Kiran, C. Udaya

2018-05-01

We report the maiden experimental observation of the formation of Wasp-waists in the Hysteresis loop, of PPY Nanocomposite with GaN doped Ferrite. Earlier this phenomenon was reported in paleo magnetic and environmental magnetic studies. It is probably the very first time we report it in our Synthesized Nanocomposites. Details supported by data are presented. Parameters like Exchange Anisotropy, Multi Domain formation, Variations in Coercivity are suspected to be prominent causes for this occurrence. Systematic analysis of our data provides substantial evidence for the existence of the phenomenon.

Investigation of Barium Ferrite, Searching for Soft Magnetic Materials in High Frequency Applications

NASA Astrophysics Data System (ADS)

Wu, Shuang; Kanada, Isao; Mewes, Tim; Mewes, Claudia; Mankey, Gary; Ariake, Yusuke; Suzuki, Takao

Soft ferrites have been extensively and intensively applied for high frequency device applications. Among them, Ba-ferrites substituted by Mn and Ti are particularly attractive as future soft magnetic material candidates for advanced high frequency device applications. However, very little has been known as to the intrinsic magnetic properties, such as damping parameter, which is crucial to develop high frequency devices. In the present study, much effort has been focused on fabrication of single crystal Ba-ferrites and measurements of damping parameter by FMR. Ba-ferrite samples consisted of many grains with various sizes have been prepared. The saturation magnetization and the magnetic anisotropy field of the sample are in reasonable agreement with the values in literature. The resonances positions in the FMR spectra over a wide frequency range also comply with theoretical predictions. However, the complex resonance shapes observed makes it difficult to extract dynamic magnetic property. Possible reasons are the demagnetization field originating from irregular sample shape or existence of multiple grains in the samples. S.W. acknowledges the support under the TDK Scholar Program.

Thermal-fatigue and oxidation resistance of cobalt-modified Udimet 700 alloy

NASA Technical Reports Server (NTRS)

Bizon, P. T.; Barrow, B. J.

1986-01-01

Comparative thermal-fatigue and oxidation resistances of cobalt-modified wrought Udimet 700 alloy (obtained by reducing the cobalt level by direct substitution of nickel) were determined from fluidized-bed tests. Bed temperatures were 1010 and 288 C (1850 and 550 C) for the first 5500 symmetrical 6-min cycles. From cycle 5501 to the 14000-cycle limit of testing, the heating bed temperature was increased to 1050 C (1922 F). Cobalt levels between 0 and 17 wt% were studied in both the bare and NiCrAlY overlay coated conditions. A cobalt level of about 8 wt% gave the best thermal-fatigue life. The conventional alloy specification is for 18.5% cobalt, and hence, a factor of 2 in savings of cobalt could be achieved by using the modified alloy. After 13500 cycles, all bare cobalt-modified alloys lost 10 to 13 percent of their initial weight. Application of the NiCrAlY overlay coating resulted in weight losses of 1/20 to 1/100 of that of the corresponding bare alloy.

Slip effects on MHD flow and heat transfer of ferrofluids over a moving flat plate

NASA Astrophysics Data System (ADS)

Ramli, Norshafira; Ahmad, Syakila; Pop, Ioan

2017-08-01

In this study, the problem of MHD flow and heat transfer of ferrofluids over a moving flat plate with slip effect and uniform heat flux is considered. The governing ordinary differential equations are solved via shooting method. The effect of slip parameter on the dimensionless velocity, temperature, skin friction and Nusselt numbers are numerically studied for the three selected ferroparticles; magnetite (Fe3O4), cobalt ferrite (CoFe2O4) and Mn-Zn ferrite (Mn-ZnFe2O4) with water-based fluid. The results indicate that dual solutions exist for a plate moving towards the origin. It is found that the slip process delays the boundary layer separation. Moreover, the velocity and thermal boundary-layer thicknesses decrease in the first solution while increase with the increase of the value of slip parameters in second solution.

Synthesis of Co/MFe(2)O(4) (M = Fe, Mn) Core/Shell Nanocomposite Particles.

PubMed

Peng, Sheng; Xie, Jin; Sun, Shouheng

2008-01-01

Monodispersed cobalt nanoparticles (NPs) with controllable size (8-14 nm) have been synthesized using thermal decomposition of dicobaltoctacarbonyl in organic solvent. The as-synthesized high magnetic moment (125 emu/g) Co NPs are dispersible in various organic solvents, and can be easily transferred into aqueous phase by surface modification using phospholipids. However, the modified hydrophilic Co NPs are not stable as they are quickly oxidized, agglomerated in buffer. Co NPs are stabilized by coating the MFe(2)O(4) (M = Fe, Mn) ferrite shell. Core/shell structured bimagnetic Co/MFe(2)O(4) nanocomposites are prepared with tunable shell thickness (1-5 nm). The Co/MFe(2)O(4) nanocomposites retain the high magnetic moment density from the Co core, while gaining chemical and magnetic stability from the ferrite shell. Comparing to Co NPs, the nanocomposites show much enhanced stability in buffer solution at elevated temperatures, making them promising for biomedical applications.

Electronic regioselectivity of diarylalkynes in cobalt-mediated Pauson-Khand reaction: an experimental and computational study with para- and meta-substituted diarylalkynes and norbornene.

PubMed

Fager-Jokela, Erika; Muuronen, Mikko; Patzschke, Michael; Helaja, Juho

2012-10-19

Both steric and electronic factors of substituted alkynes are known to guide α/β-cyclopentenone regioselectivity in the cobalt-mediated Pauson-Khand reaction (PKR). In synthetic applications of the PKR, the steric factors can often override or render possible electronic effects. This study examined alkyne-dependent electronic regioselectivity of cyclopentenone formation in PKR with norbornene and sterically equivalent, but electronically unsymmetrical, meta- and para-substituted diarylethynyls to unveil the role of electronic effects alone. In agreement with the literature reports, EDG para-substituted aryls, to some extent, favored the cyclopentenone α-regioisomer, while the EWG-substituted aryls correspondingly preferred the β-regioisomer. The cooperation of EGW and EDG in diaryl-substituted alkynes did not lead to any increased regioselectivities that could be expected by a "push-pull" effect. Both EWG and EDG meta-substituted aryls preferred the β-regioisomer, which was demonstrated by 3,5-dimethoxy- and 3,5-bis(trifluoromethyl)-1-phenylethynyls that yielded 1/1.6 and 1/2.0 α/β-regioselectivities, respectively. Theoretically, inspection of Hammett values of α-alkyne carbons gave qualitatively satisfactory prediction for para-substituted aryls but correlated only weakly with meta-substituted effects. Computational investigations at the DFT level revealed a correlation between NBO charges and the regioselectivity. Overall, the results suggest that the polarity of an alkyne, also designated by the relative polarization of aryl α-carbons, dictates the regioselectivity in the absence of steric effects.

Magnetic micro scavengers: highly porous Ni1‑x Co x Fe2O4 microcubes for efficient disintegration of nitrophenol

NASA Astrophysics Data System (ADS)

Pervaiz, Erum; Syam Azhar Virk, Muhammad; Tareen, Ayesha Khan; Zhang, Bingxue; Zhao, Qiuyan; Wang, Zhenzhen; Yang, Minghui

2018-05-01

The fabrication of functional materials in patterned morphology is focused to obtain remarkable physiognomies of the materials for certain applications. Instead of randomly distributed agglomerated nanoparticles, it is highly desirable to arrange them in a motif, as this directed formation of nanomaterials can have a substantial influence on their performance and activity in various applications. With this perspective, MOF derived hollow cubes of nickel cobalt ferrites have been synthesized via a facile process using sacrificial templates at 600 °C. Microcubes, composed of tiny grains in a size range from 10 nm ± 2 nm were obtained in pure form as a polycrystalline material. The high specific surface area (1185 m2 g‑1) and mesoporous nature of hollow cubic ferrites were found to be excellent adsorbents for nitrophenol at room temperature. The equilibrium quantity of adsorbed nitrophenol was calculated as 47 mg g‑1 ferrite, accomplished in 7 min. Their large surface area, mesopores and hollow nature, in combination with controlled size distribution of grains, have enabled this remarkable utilization of nanoferrites for removal of nitrophenol from water.

Magnetic micro scavengers: highly porous Ni1-x Co x Fe2O4 microcubes for efficient disintegration of nitrophenol.

PubMed

Pervaiz, Erum; Virk, Muhammad Syam Azhar; Tareen, Ayesha Khan; Zhang, Bingxue; Zhao, Qiuyan; Wang, Zhenzhen; Yang, Minghui

2018-05-25

The fabrication of functional materials in patterned morphology is focused to obtain remarkable physiognomies of the materials for certain applications. Instead of randomly distributed agglomerated nanoparticles, it is highly desirable to arrange them in a motif, as this directed formation of nanomaterials can have a substantial influence on their performance and activity in various applications. With this perspective, MOF derived hollow cubes of nickel cobalt ferrites have been synthesized via a facile process using sacrificial templates at 600 °C. Microcubes, composed of tiny grains in a size range from 10 nm ± 2 nm were obtained in pure form as a polycrystalline material. The high specific surface area (1185 m 2 g -1 ) and mesoporous nature of hollow cubic ferrites were found to be excellent adsorbents for nitrophenol at room temperature. The equilibrium quantity of adsorbed nitrophenol was calculated as 47 mg g -1 ferrite, accomplished in 7 min. Their large surface area, mesopores and hollow nature, in combination with controlled size distribution of grains, have enabled this remarkable utilization of nanoferrites for removal of nitrophenol from water.

Phonon structures of GaN-based random semiconductor alloys

NASA Astrophysics Data System (ADS)

Zhou, Mei; Chen, Xiaobin; Li, Gang; Zheng, Fawei; Zhang, Ping

2017-12-01

Accurate modeling of thermal properties is strikingly important for developing next-generation electronics with high performance. Many thermal properties are closely related to phonon dispersions, such as sound velocity. However, random substituted semiconductor alloys AxB1-x usually lack translational symmetry, and simulation with periodic boundary conditions often requires large supercells, which makes phonon dispersion highly folded and hardly comparable with experimental results. Here, we adopt a large supercell with randomly distributed A and B atoms to investigate substitution effect on the phonon dispersions of semiconductor alloys systematically by using phonon unfolding method [F. Zheng, P. Zhang, Comput. Mater. Sci. 125, 218 (2016)]. The results reveal the extent to which phonon band characteristics in (In,Ga)N and Ga(N,P) are preserved or lost at different compositions and q points. Generally, most characteristics of phonon dispersions can be preserved with indium substitution of gallium in GaN, while substitution of nitrogen with phosphorus strongly perturbs the phonon dispersion of GaN, showing a rapid disintegration of the Bloch characteristics of optical modes and introducing localized impurity modes. In addition, the sound velocities of both (In,Ga)N and Ga(N,P) display a nearly linear behavior as a function of substitution compositions. Supplementary material in the form of one pdf file available from the Journal web page at http://https://doi.org/10.1140/epjb/e2017-80481-0.

Site preference and magnetic properties of Ga/In-substituted strontium hexaferrite: An ab initio study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dixit, Vivek; Nandadasa, Chandani N.; Kim, Seong-Gon, E-mail: kimsg@ccs.msstate.edu

2015-11-28

The first-principles density functional theory has been used to study Ga/In-substituted strontium hexaferrite (SrFe{sub 12}O{sub 19}). Based on the calculation of the substitution energy of Ga and In in SrFe{sub 12}O{sub 19} and the formation probability analysis, we conclude that in SrFe{sub 12−x}Ga{sub x}O{sub 19} the substituted Ga atoms prefer to occupy the 12k, 2a, and 4f{sub 1} sites, while In atoms in SrFe{sub 12−x}In{sub x}O{sub 19} occupy the 12k, 4f{sub 2}, and 4f{sub 1} sites. We used the site occupation probabilities to calculate the magnetic properties of the substituted SrFe{sub 12}O{sub 19}. It was found that as the fractionmore » of Ga atoms in SrFe{sub 12−x}Ga{sub x}O{sub 19} increases, the saturation magnetization (M{sub s}) as well as magnetic anisotropy energy (MAE) decrease, while the anisotropy field (H{sub a}) increases. In the case of SrFe{sub 12−x}In{sub x}O{sub 19}, M{sub s}, MAE, and H{sub a} decrease with an increase of the concentration of In atoms.« less

Enantioselective Cobalt-Catalyzed Sequential Nazarov Cyclization/Electrophilic Fluorination: Access to Chiral α-Fluorocyclopentenones.

PubMed

Zhang, Heyi; Cheng, Biao; Lu, Zhan

2018-06-20

A newly designed thiazoline iminopyridine ligand for enantioselective cobalt-catalyzed sequential Nazarov cyclization/electrophilic fluorination was developed. Various chiral α-fluorocyclopentenones were prepared with good yields and diastereo- and enantioselectivities. Further derivatizations could be easily carried out to provide chiral cyclopentenols with three contiguous stereocenters. Furthermore, a direct deesterification of fluorinated products could afford chiral α-single fluorine-substituted cyclopentenones.

A Molecular Cobalt Catalyst Architected and TiO2 Modified p-GaInP2 Photoelectrode for Hydrogen Production

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gu, Jing; Yan, Yong; Young, James

2017-05-01

We demonstrate that by employing a hybrid molecular/semiconductor interface with atomic layer deposited (ALD) TiO2 as an intermediate layer, a robust and corrosion resistant GaInP2-TiO2-cobaltoxime-TiO2 photocathode can be operated in alkaline media (pH =13).

A Brillouin Light Scattering Study of Magnetic Excitations.

DTIC Science & Technology

1986-01-30

collaborative project with CNR-Rome, with materials emphasis on substi- tuted LPE garnet thin films . "Localized Canting Models for Substituted Magnetic Oxides...thermal magnons in FeBO 3, exchange in substituted ferrites, parametric spin-waves in epitaxial yttrium iron garnet (YIG. films , surface magnon angle...and surface magnons in thin films . Central to the research was the develooment of a hiqh contrast, high resolu- tion multipassltandem Fabry; Perot

The Formation of Martensitic Austenite During Nitridation of Martensitic and Duplex Stainless Steels

NASA Astrophysics Data System (ADS)

Zangiabadi, Amirali; Dalton, John C.; Wang, Danqi; Ernst, Frank; Heuer, Arthur H.

2017-01-01

Isothermal martensite/ferrite-to-austenite phase transformations have been observed after low-temperature nitridation in the martensite and δ-ferrite phases in 15-5 PH (precipitation hardening), 17-7 PH, and 2205 (duplex) stainless steels. These transformations, in the region with nitrogen concentrations of 8 to 16 at. pct, are consistent with the notion that nitrogen is a strong austenite stabilizer and substitutional diffusion is effectively frozen at the paraequilibrium temperatures of our experiments. Our microstructural and diffraction analyses provide conclusive evidence for the martensitic nature of these phase transformations.

Sol-gel auto-combustion synthesis and properties of Co2Z-type hexagonal ferrite ultrafine powders

NASA Astrophysics Data System (ADS)

Liu, Junliang; Yang, Min; Wang, Shengyun; Lv, Jingqing; Li, Yuqing; Zhang, Ming

2018-05-01

Z-type hexagonal ferrite ultrafine powders with chemical formulations of (BaxSr1-x)3Co2Fe24O41 (x varied from 0.0 to 1.0) have been synthesized by a sol-gel auto-combustion technique. The average particle sizes of the synthesized powders ranged from 2 to 5 μm. The partial substitution of Ba2+ by Sr2+ led to the shrinkage of the crystal lattices and resulted in changes in the magnetic sub-lattices, which tailored the static and dynamic magnetic properties of the as-synthesized powders. As the substitution ratio of Ba2+ by Sr2+, the saturation magnetization of the synthesized powders almost consistently increased from 43.3 to 56.1 emu/g, while the real part of permeability approached to a relatively high value about 2.2 owing to the balance of the saturation magnetization and magnetic anisotropy field.

Room Temperature Gas Sensing Properties of Sn-Substituted Nickel Ferrite (NiFe2O4) Thin Film Sensors Prepared by Chemical Co-Precipitation Method

NASA Astrophysics Data System (ADS)

Manikandan, V.; Li, Xiaogan; Mane, R. S.; Chandrasekaran, J.

2018-04-01

Tin (Sn) substituted nickel ferrite (NiFe2O4) thin film sensors were prepared by a simple chemical co-precipitation method, which initially characterized their structure and surface morphology with the help of x-ray diffraction and scanning electron microscopy. Surface morphology of the sensing films reveals particles stick together with nearer particles and this formation leads to a large specific area as a large specific area is very useful for easy adsorption of gas molecules. Transmission electron microscopy and selected area electron diffraction pattern images confirm particle size and nanocrystallnity as due to formation of circular rings. Fourier transform infrared analysis has supported the presence of functional groups. The 3.69 eV optical band gap of the film was found which enabled better gas sensing. Gas sensors demonstrate better response and recovery characteristics, and the maximum response was 68.43%.

Preparation and characterization of cobalt-substituted anthrax lethal factor

DOE Office of Scientific and Technical Information (OSTI.GOV)

Saebel, Crystal E.; Carbone, Ryan; Dabous, John R.

2011-12-09

Highlights: Black-Right-Pointing-Pointer Cobalt-substituted anthrax lethal factor (CoLF) is highly active. Black-Right-Pointing-Pointer CoLF can be prepared by bio-assimilation and direct exchange. Black-Right-Pointing-Pointer Lethal factor binds cobalt tightly. Black-Right-Pointing-Pointer The electronic spectrum of CoLF reveals penta-coordination. Black-Right-Pointing-Pointer Interaction of CoLF with thioglycolic acid follows a 2-step mechanism. -- Abstract: Anthrax lethal factor (LF) is a zinc-dependent endopeptidase involved in the cleavage of mitogen-activated protein kinase kinases near their N-termini. The current report concerns the preparation of cobalt-substituted LF (CoLF) and its characterization by electronic spectroscopy. Two strategies to produce CoLF were explored, including (i) a bio-assimilation approach involving the cultivation of LF-expressingmore » Bacillus megaterium cells in the presence of CoCl{sub 2}, and (ii) direct exchange by treatment of zinc-LF with CoCl{sub 2}. Independent of the method employed, the protein was found to contain one Co{sup 2+} per LF molecule, and was shown to be twice as active as its native zinc counterpart. The electronic spectrum of CoLF suggests the Co{sup 2+} ion to be five-coordinate, an observation similar to that reported for other Co{sup 2+}-substituted gluzincins, but distinct from that documented for the crystal structure of native LF. Furthermore, spectroscopic studies following the exposure of CoLF to thioglycolic acid (TGA) revealed a sequential mechanism of metal removal from LF, which likely involves the formation of an enzyme: Co{sup 2+}:TGA ternary complex prior to demetallation of the active site. CoLF reported herein constitutes the first spectroscopic probe of LF's active site, which may be utilized in future studies to gain further insight into the enzyme's mechanism and inhibitor interactions.« less

The role of proline-containing peptide triads in β-sheet formation: A kinetic study.

PubMed

Takor, Gaius A; Higashiya, Seiichiro; Sikirzhytski, Vitali K; Seeley, Jason P; Lednev, Igor K; Welch, John T

2015-06-01

The design of biomimetic materials through molecular self-assembly is a growing area of modern nanotechnology. With problems of protein folding, self-assembly, and sequence-structure relationships as essential in nanotechnology as in biology, the effect of the nucleation of β-hairpin formation by proline on the folding process has been investigated in model studies. Previously such studies were limited to investigations of the influence of proline on the formation of turns in short peptide sequences. The effect of proline-based triads on the folding of an 11-kDa amyloidogenic peptide GH6[(GA)3GY(GA)3GE]8 GAH6 (YE8) was investigated by selective substitution of the proline-substituted triads at the γ-turn sites. The folding and fibrillation of the singly proline-substituted polypeptides, e.g., GH6-[(GA)3GY(GA)3GE]7(GA)3GY(GA)3PD-GAH6 (8PD), and doubly proline-substituted polypeptides, e.g., GH6-[(GA)3GY(GA)3GE]3(GA)3GY(GA)3PD[(GA)3GY(GA)3GE]3(GA)3GY(GA)3PD-GAH6 (4,8PD), were directly monitored by circular dichroism and deep UV resonance Raman and fluorescence spectroscopies. These findings were used to identify the essential folding domains, i.e., the minimum number of β-strands necessary for stable folding. These experimental findings may be especially useful in the design and construction of peptidic materials for a wide range of applications as well as in understanding the mechanisms of folding critical to fibril formation. © 2015 Wiley Periodicals, Inc.

The response of cobalt-free Udimet 700 type alloy to modified heat treatments

NASA Technical Reports Server (NTRS)

Harf, F. H.

1986-01-01

A superalloy based on Udimet 700, in which all of the cobalt was replaced by nickel, was prepared from hot isostatically pressed prealloyed powders. This material was given various heat treatments consisting of partial solutioning and aging in a sequence of four different temperatures. Comparisons were made of microstructures and mechanical properties. Best results were obtained by partially solutioning at 1145 deg C and aging through a sequence of 870, 1030, 650 and 760 deg C. This heat treatment also provided significantly improved properties for wrought material of the same composition. The results suggest that cobalt free Udimet 700 should be considered as a substitute for Udimet 700 with the standard 17 percent cobalt content.

The response of cobalt-free Udimet 700 type alloy to modified heat treatments

NASA Technical Reports Server (NTRS)

Harf, F. H.

1985-01-01

A superalloy based on Udimet 700, in which all of the cobalt was replaced by nickel, was prepared from hot isostatically pressed prealloyed powders. This material was given various heat treatments consisting of partial solutioning and aging in a sequence of four different temperatures. Comparisons were made of microstructures and mechanical properties. Best results were obtained by partially solutioning at 1145 deg C and aging through a sequence of 870, 1030, 650 and 760 deg C. This heat treatment also provided significantly improved properties for wrought material of the same composition. The results suggest that cobalt free Udimet 700 should be considered as a substitute for Udimet 700 with the standard 17 percent cobalt content.

Enhanced magnetostrictive properties of nanocrystalline Dy3+ substituted Fe-rich Co0.8Fe2.2O4 for sensor applications

NASA Astrophysics Data System (ADS)

Kharat, Shahaji P.; Swadipta, Roy; Kambale, R. C.; Kolekar, Y. D.; Ramana, C. V.

2017-10-01

We report on the enhanced magnetostrictive properties of nanocrystalline Dysprosium (Dy3+) substituted iron-rich cobalt ferrites (Co0.8Fe(2.2-x)DyxO4, referred to as CFDO). The CFDO samples with a variable Dy concentration (x = 0.000-0.075) were synthesized by the sol-gel auto-combustion method. The phase purity and crystal structure were confirmed from X-ray diffraction analyses coupled with Rietveld refinement. Surface morphology analysis using scanning electron microscopy imaging indicates the agglomerated magnetic particles with a non-uniform particle size distribution, which is desirable to transfer the strain. The magnetostriction coefficient (λ11) measurements indicate that the CFDO with Dy concentration x = 0.025 exhibits the highest strain sensitivity, (dλ/dH) ˜1.432 nm/A (for H ≤ 1000 Oe). On the other hand, the magnetostriction coefficient (λ12) measurements indicate that the Dy concentration x = 0.075 exhibits the larger (dλ/dH) ˜ 0.615 nm/A (for H ≤ 1000 Oe). The maximum λ11value of 166 ppm (at H = 3300 Oe) was observed for a compound with Dy concentration x = 0.050. Magnetization measurements indicate that the saturation magnetization and coercivity of CFDO samples are dependent on the Dy3+content; the highest value of squareness ratio of 0.424 was observed for x = 0.050. The interplay between strain sensitivity (dλ/dH) and instantaneous susceptibility (dM/dH), as derived from magnetostriction and magnetization results, demonstrates that these CFDO materials may be useful for developing torque/stress sensors, as a constituent magnetostrictive phase for making the magnetoelectric composite materials and thus suitable for magnetoelectric sensor applications.

Dielectric, magnetic, ferroelectric, and Mossbauer properties of bismuth substituted nanosized cobalt ferrites through glycine nitrate synthesis method

NASA Astrophysics Data System (ADS)

Routray, Krutika L.; Sanyal, Dirtha; Behera, Dhrubananda

2017-12-01

CoFe2-xBixO4 nanoferrites with x = 0, 0.05, 0.1, 0.5, and 1.0 have been synthesized by the glycine nitrate process. The present study investigates the effect of Bi3+ substitution on the microstructural, dielectric, ferroelectric, magnetic, and Mossbauer properties of CoFe2O4 nanoparticles. The X-ray diffraction technique was used to confirm the phase purity and estimate the crystallite size which revealed the formation of a secondary phase when Bi3+ concentration exceeds x = 0.5. Transmission electron microscopy indicated the formation of grains by aggregation of small crystallites with a reduction in grain size to 20 nm with an increase in Bi3+ content and also divulged the lattice parameter value to be 8.378 Å, confirming the crystalline nature of the synthesised sample. Dielectric properties performed in the frequency range of 100 Hz to 1 MHz determined that the dielectric behavior is attributed to the Maxwell-Wagner polarization and the activation energy of the specimens is calculated from the dielectric measurements. The hysteresis curve indicated the ferrimagnetic nature of the samples. The samples also exhibited a well saturated P-E loop with gradual lowering in remenant polarization, coercive field, and saturation polarization with an increase in bismuth concentration. Mössbauer spectroscopy analysis confirmed the changes in magnetic moment of ions, their coupling with neighbouring ions, and cation exchange interactions. Owing to the high physical, thermal, and chemical stabilities, these magnetic ceramics, CoFe2-xBixO4, possesses tremendous potential in major understanding of magnetism and in magnetic recording applications for high density information storage.

Enhanced magnetic properties in Mn0.6Zn0.4-xNixFe2O4 (x=0-0.4) nanoparticles

NASA Astrophysics Data System (ADS)

Mallesh, S.; Mandal, P.; Srinivas, V.

2018-04-01

Ni substituted MnZn ferrite fine particles were synthesized through sol-gel method. The structure, stability and magnetic properties have been investigated. Thermal stability of as-prepared (AP) particles is improved compared to that of Mn0.6Zn0.4Fe2O4 (MZF) ferrite particles. The as-prepared and samples annealed at 1200 °C exhibit pure spinel ferrite phase, while samples at intermediate temperatures (600 - 1000 °C) exhibit secondary phase of α-Fe2O3 along with ferrite phase. The Mn0.6Zn0.1Ni0.3Fe2O4 (Ni-MZF) sample shows significantly lower volume fraction of secondary phase compared to that of MZF. The observed magnetization of Ni-MZF is twice of that MZF samples. Present results suggest that a small amount (x=0.3) of Ni in place of nonmagnetic Zn in MZF significantly decreases the secondary phase fraction and improves the magnetic properties.

[Lead adsorption and arsenite oxidation by cobalt doped birnessite].

PubMed

Yin, Hui; Feng, Xiong-Han; Qiu, Guo-Hong; Tan, Wen-Feng; Liu, Fan

2011-07-01

In order to study the effects of transition metal ions on the physic-chemical properties of manganese dioxides as environmental friendly materials, three-dimensional nano-microsphere cobalt-doped birnessite was synthesized by reduction of potassium permanganate by mixtures of concentrated hydrochloride and cobalt (II) chloride. Powder X-ray diffraction, chemical analysis, N2 physical adsorption, field emission scanning electron microscopy (FE-SEM) and X-ray photoelectron spectra (XPS) were used to characterize the crystal structure, chemical composition and micro-morphologies of products. In the range of molar ratios from 0.05 to 0.20, birnessite was fabricated exclusively. It was observed that cobalt incorporated into the layers of birnessite and had little effect on the crystal structure and micromorpholgy, but crystallinity decreased after cobalt doping. Both chemical analysis and XPS results showed that manganese average oxidation state decreased after cobalt doping, and the percentage of Mn3+ increased. Co(III) OOH existed mainly in the structure. With the increase of cobalt, hydroxide oxygen percentage in molar increased from 12.79% for undoped birnessite to 13.05%, 17.69% and 17.79% for doped samples respectively. Adsorption capacity for lead and oxidation of arsenite of birnessite were enhanced by cobalt doping. The maximum capacity of Pb2+ adsorption increased in the order HB (2 538 mmol/kg) < CoB5 (2798 mmol/kg) < CoB10 (2932 mmol/kg) < CoB20 (3 146 mmol/kg). Oxidation percentage of arsenite in simulated waste water by undoped birnessite was 76.5%, those of doped ones increased by 2.0%, 12.8% and 18.9% respectively. Partial of Co3+ substitution for Mn4+ results in the increase of negative charge of the layer and the content of hydroxyl group, which could account for the improved adsorption capacity of Pb2+. After substitution of manganese by cobalt, oxidation capacity of arsenite by birnessite increases likely due to the higher standard redox potential of Co3+/Co2+ than those of Mn4+/Mn3+/Mn2+. Therefore, Co-doped birnessite is more applicable for the remediation of water polluted with heavy metal ions, implying new methods of modification of manganese dioxides in practice.

Formation of III–V ternary solid solutions on GaAs and GaSb plates via solid-phase substitution reactions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vasil’ev, V. I.; Gagis, G. S., E-mail: galina.gagis@gmail.com; Kuchinskii, V. I.

2015-07-15

Processes are considered in which ultrathin layers of III–V ternary solid solutions are formed via the delivery of Group-V element vapors to GaAs and GaSb semiconductor plates, with solid-phase substitution reactions occurring in the surface layers of these plates. This method can form defect-free GaAs{sup 1–x}P{sup x}, GaAs{sup x}Sb{sup 1–x}, and GaP{sup x}Sb{sup 1–x} layers with thicknesses of 10–20 nm and a content x of the embedded components of up to 0.04.

Stacking fault effects in Mg-doped GaN

NASA Astrophysics Data System (ADS)

Schmidt, T. M.; Miwa, R. H.; Orellana, W.; Chacham, H.

2002-01-01

First-principles total energy calculations are performed to investigate the interaction of a stacking fault with a p-type impurity in both zinc-blende and wurtzite GaN. For both structures we find that, in the presence of a stacking fault, the impurity level is a more localized state in the band gap. In zinc-blende GaN, the minimum energy position of the substitutional Mg atom is at the plane of the stacking fault. In contrast, in wurtzite GaN the substitutional Mg atom at the plane of the stacking fault is a local minimum and the global minimum is the substitutional Mg far from the fault. This behavior can be understood as a packing effect which induces a distinct strain relief process, since the local structure of the stacking fault in zinc-blende GaN is similar to fault-free wurtzite GaN and vice-versa.

Impedance spectroscopy of the oxide films formed during high temperature oxidation of a cobalt-plated ferritic alloy

NASA Astrophysics Data System (ADS)

Velraj, S.; Zhu, J. H.; Painter, A. S.; Du, S. W.; Li, Y. T.

2014-02-01

Impedance spectroscopy was used to evaluate the oxide films formed on cobalt-coated Crofer 22 APU ferritic stainless steel after thermal oxidation at 800 °C in air for different times (i.e. 2, 50, 100 and 500 h). Impedance spectra of the oxide films exhibited two or three semicircles depending on the oxidation time, which correspond to the presence of two or three individual oxide layers. Coupled with scanning electron microscopy/energy-dispersive spectroscopy (SEM/EDS) and X-ray diffraction (XRD), the individual oxide layer corresponding to each semicircle was determined unambiguously. Impedance spectrum analysis of the oxide films formed on the sample after thermal exposure at 800 °C in air for 2 h led to the identification of the low-frequency and high-frequency semicircles as being from Cr2O3 and Co3O4, respectively. SEM/EDS and XRD analysis of the 500-h sample clearly revealed the presence of three oxide layers, analyzed to be Co3-xCrxO4, CoCr2O4, and Cr2O3. Although the SEM images of the 50-h and 100-h samples did not clearly show the CoCr2O4 layer, impedance plots implied their presence. The oxide scales were assigned to their respective semicircles and the electrical properties of Co3-xCrxO4, CoCr2O4 and Cr2O3 were determined from the impedance data.

Stress-dependent crystal structure of lanthanum strontium cobalt ferrite by in situ synchrotron X-ray diffraction

NASA Astrophysics Data System (ADS)

Geiger, Philipp T.; Khansur, Neamul H.; Riess, Kevin; Martin, Alexander; Hinterstein, Manuel; Webber, Kyle G.

2018-02-01

Lanthanum strontium cobalt ferrite La1-xSrxCo1-yFeyO3-δ (LSCF) is one of the most studied mixed ionic-electronic conductor materials due to electrical and transport properties, which are attractive for intermediate temperature solid oxide fuel cells (SOFCs), oxygen permeation membranes, and catalysis. The integration of such materials, however, depends on the thermal as well as mechanical behavior. LSCF exhibits nonlinear hysteresis during compressive stress-strain measurements, marked by a remanent strain and coercive stress, i.e., ferroelasticity. However, the origin of ferroelastic behavior has not been investigated under high compressive stress. This study, therefore, investigates the microscopic origin of stress-induced mechanical behavior in polycrystalline (La0.6Sr0.4)0.95Co0.2Fe0.8O3-δ using in situ synchrotron x-ray diffraction. The data presented here reveals that the strain response originates from the intrinsic lattice strain as well as the extrinsic domain switching strain without any apparent change in crystallographic symmetry. A comparison of the calculated microscopic strain contribution with that of a macroscopic measurement indicates a significant change in the relative contributions of intrinsic and extrinsic strain depending on the applied stress state, i.e., under maximum stress and after unloading. Direct evidence of the microscopic origin of stress-strain response outlined in this paper may assist in guiding materials design with the improved mechanical reliability of SOFCs.

Investigate the ultrasound energy assisted adsorption mechanism of nickel(II) ions onto modified magnetic cobalt ferrite nanoparticles: Multivariate optimization.

PubMed

Mehrabi, Fatemeh; Alipanahpour Dil, Ebrahim

2017-07-01

In present study, magnetic cobalt ferrite nanoparticles modified with (E)-N-(2-nitrobenzylidene)-2-(2-(2-nitrophenyl)imidazolidine-1-yl) ethaneamine (CoFe 2 O 4 -NPs-NBNPIEA) was synthesized and applied as novel adsorbent for ultrasound energy assisted adsorption of nickel(II) ions (Ni 2+ ) from aqueous solution. The prepared adsorbent characterized by Fourier transforms infrared spectroscopy (FT-IR), transmission electron microscope (TEM), vibrating sample magnetometer (VSM) and X-ray diffraction (XRD). The dependency of adsorption percentage to variables such as pH, initial Ni 2+ ions concentration, adsorbent mass and ultrasound time were studied with response surface methodology (RSM) by considering the desirable functions. The quadratic model between the dependent and independent variables was built. The proposed method showed good agreement between the experimental data and predictive value, and it has been successfully employed to adsorption of Ni 2+ ions from aqueous solution. Subsequently, the experimental equilibrium data at different concentration of Ni 2+ ions and 10mg amount of adsorbent mass was fitted to conventional isotherm models like Langmuir, Freundlich, Tempkin, Dubinin-Radushkevich and it was revealed that the Langmuir is best model for explanation of behavior of experimental data. In addition, conventional kinetic models such as pseudo-first and second-order, Elovich and intraparticle diffusion were applied and it was seen that pseudo-second-order equation is suitable to fit the experimental data. Copyright © 2016 Elsevier B.V. All rights reserved.

Ultradispersed Cobalt Ferrite Nanoparticles Assembled in Graphene Aerogel for Continuous Photo-Fenton Reaction and Enhanced Lithium Storage Performance

NASA Astrophysics Data System (ADS)

Qiu, Bocheng; Deng, Yuanxin; Du, Mengmeng; Xing, Mingyang; Zhang, Jinlong

2016-07-01

The Photo-Fenton reaction is an advanced technology to eliminate organic pollutants in environmental chemistry. Moreover, the conversion rate of Fe3+/Fe2+ and utilization rate of H2O2 are significant factors in Photo-Fenton reaction. In this work, we reported three dimensional (3D) hierarchical cobalt ferrite/graphene aerogels (CoFe2O4/GAs) composites by the in situ growing CoFe2O4 crystal seeds on the graphene oxide (GO) followed by the hydrothermal process. The resulting CoFe2O4/GAs composites demonstrated 3D hierarchical pore structure with mesopores (14~18 nm), macropores (50~125 nm), and a remarkable surface area (177.8 m2 g-1). These properties endowed this hybrid with the high and recyclable Photo-Fenton activity for methyl orange pollutant degradation. More importantly, the CoFe2O4/GAs composites can keep high Photo-Fenton activity in a wide pH. Besides, the CoFe2O4/GAs composites also exhibited excellent cyclic performance and good rate capability. The 3D framework can not only effectively prevent the volume expansion and aggregation of CoFe2O4 nanoparticles during the charge/discharge processes for Lithium-ion batteries (LIBs), but also shorten lithium ions and electron diffusion length in 3D pathways. These results indicated a broaden application prospect of 3D-graphene based hybrids in wastewater treatment and energy storage.

Ultradispersed Cobalt Ferrite Nanoparticles Assembled in Graphene Aerogel for Continuous Photo-Fenton Reaction and Enhanced Lithium Storage Performance.

PubMed

Qiu, Bocheng; Deng, Yuanxin; Du, Mengmeng; Xing, Mingyang; Zhang, Jinlong

2016-07-04

The Photo-Fenton reaction is an advanced technology to eliminate organic pollutants in environmental chemistry. Moreover, the conversion rate of Fe(3+)/Fe(2+) and utilization rate of H2O2 are significant factors in Photo-Fenton reaction. In this work, we reported three dimensional (3D) hierarchical cobalt ferrite/graphene aerogels (CoFe2O4/GAs) composites by the in situ growing CoFe2O4 crystal seeds on the graphene oxide (GO) followed by the hydrothermal process. The resulting CoFe2O4/GAs composites demonstrated 3D hierarchical pore structure with mesopores (14~18 nm), macropores (50~125 nm), and a remarkable surface area (177.8 m(2 )g(-1)). These properties endowed this hybrid with the high and recyclable Photo-Fenton activity for methyl orange pollutant degradation. More importantly, the CoFe2O4/GAs composites can keep high Photo-Fenton activity in a wide pH. Besides, the CoFe2O4/GAs composites also exhibited excellent cyclic performance and good rate capability. The 3D framework can not only effectively prevent the volume expansion and aggregation of CoFe2O4 nanoparticles during the charge/discharge processes for Lithium-ion batteries (LIBs), but also shorten lithium ions and electron diffusion length in 3D pathways. These results indicated a broaden application prospect of 3D-graphene based hybrids in wastewater treatment and energy storage.

High-Performance Flexible Organic Nano-Floating Gate Memory Devices Functionalized with Cobalt Ferrite Nanoparticles.

PubMed

Jung, Ji Hyung; Kim, Sunghwan; Kim, Hyeonjung; Park, Jongnam; Oh, Joon Hak

2015-10-07

Nano-floating gate memory (NFGM) devices are transistor-type memory devices that use nanostructured materials as charge trap sites. They have recently attracted a great deal of attention due to their excellent performance, capability for multilevel programming, and suitability as platforms for integrated circuits. Herein, novel NFGM devices have been fabricated using semiconducting cobalt ferrite (CoFe2O4) nanoparticles (NPs) as charge trap sites and pentacene as a p-type semiconductor. Monodisperse CoFe2O4 NPs with different diameters have been synthesized by thermal decomposition and embedded in NFGM devices. The particle size effects on the memory performance have been investigated in terms of energy levels and particle-particle interactions. CoFe2O4 NP-based memory devices exhibit a large memory window (≈73.84 V), a high read current on/off ratio (read I(on)/I(off)) of ≈2.98 × 10(3), and excellent data retention. Fast switching behaviors are observed due to the exceptional charge trapping/release capability of CoFe2O4 NPs surrounded by the oleate layer, which acts as an alternative tunneling dielectric layer and simplifies the device fabrication process. Furthermore, the NFGM devices show excellent thermal stability, and flexible memory devices fabricated on plastic substrates exhibit remarkable mechanical and electrical stability. This study demonstrates a viable means of fabricating highly flexible, high-performance organic memory devices. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Ultradispersed Cobalt Ferrite Nanoparticles Assembled in Graphene Aerogel for Continuous Photo-Fenton Reaction and Enhanced Lithium Storage Performance

PubMed Central

Qiu, Bocheng; Deng, Yuanxin; Du, Mengmeng; Xing, Mingyang; Zhang, Jinlong

2016-01-01

The Photo-Fenton reaction is an advanced technology to eliminate organic pollutants in environmental chemistry. Moreover, the conversion rate of Fe3+/Fe2+ and utilization rate of H2O2 are significant factors in Photo-Fenton reaction. In this work, we reported three dimensional (3D) hierarchical cobalt ferrite/graphene aerogels (CoFe2O4/GAs) composites by the in situ growing CoFe2O4 crystal seeds on the graphene oxide (GO) followed by the hydrothermal process. The resulting CoFe2O4/GAs composites demonstrated 3D hierarchical pore structure with mesopores (14~18 nm), macropores (50~125 nm), and a remarkable surface area (177.8 m2 g−1). These properties endowed this hybrid with the high and recyclable Photo-Fenton activity for methyl orange pollutant degradation. More importantly, the CoFe2O4/GAs composites can keep high Photo-Fenton activity in a wide pH. Besides, the CoFe2O4/GAs composites also exhibited excellent cyclic performance and good rate capability. The 3D framework can not only effectively prevent the volume expansion and aggregation of CoFe2O4 nanoparticles during the charge/discharge processes for Lithium-ion batteries (LIBs), but also shorten lithium ions and electron diffusion length in 3D pathways. These results indicated a broaden application prospect of 3D-graphene based hybrids in wastewater treatment and energy storage. PMID:27373343

Structural, magnetic and spectral properties of Gd and Dy co-doped dielectrically modified Co-Ni (Ni0.4Co0.6Fe2O4) ferrites

NASA Astrophysics Data System (ADS)

Ditta, Allah; Khan, Muhammad Azhar; Junaid, Muhammad; Khalil, R. M. Arif; Warsi, Muhammad Farooq

2017-02-01

Gadolinium (Gd) and Dysprosium (Dy) co-doped Ni-Co (Ni0.4Co0.6Fe2O4) ferrites were prepared by micro-emulsion route. X-ray diffraction (XRD) analysis indicated the development of cubic spinel structure. The lattice parameter and X-ray density were found to increase from 8.24 to 8.31 Å and 5.57 to 5.91 (gm/cm3) respectively as the Gd-Dy contents increased in nickel-cobalt ferrites. The crystallite size calculated from the Scherrer's formula exhibited the formation of nanocrystalline ferrites (13-26 nm). Two foremost absorption bands observed in FTIR spectra within 400 cm-1 (υ2) to 600 cm-1 (υ1) which correspond to stretching vibrations of tetrahedral and octahedral complexes respectively. The dielectric constant (ε) and dielectric loss (tanδ) were decreased by the optimization of frequency and abrupt decrease in the low frequency region and higher values in the high frequency region were observed. The dielectric dispersion was due to rapid decrease of dielectric constant in the low frequency region. This variation of dielectric dispersion was explicated in the light of space charge polarization model of Maxwell-Wagner. The dielectric loss occurs in these ferrites due to electron hopping and defects in the dipoles. The electron hopping was possible at low frequency range but at higher frequency the dielectric loss was decreased with the decrease of electron hopping. Magnetic properties were observed by measuring M-H loops. Due to low dielectric loss and dielectric constant these materials were appropriate in the fabrication of switching and memory storage devices.

Acrylate intercalation and in situ polymerization in iron-, cobalt-, or manganese-substituted nickel hydroxides.

PubMed

Vaysse, C; Guerlou-Demourgues, L; Duguet, E; Delmas, C

2003-07-28

A chimie douce route based on successive redox and exchange reactions has allowed us to prepare new hybrid organic-inorganic materials, composed of polyacrylate macromolecules intercalated into layered double hydroxides (LDHs), deriving from Ni(OH)(2). Monomer intercalation and in situ polymerization mechanisms have appeared to be strongly dependent upon the nature of the substituting cation in the slabs. In the case of iron-based LDHs, a phase containing acrylate monomeric intercalates has been isolated and identified by X-ray diffraction and infrared spectroscopy. Second, interslab free-radical polymerization of acrylate anions has been successfully initiated using potassium persulfate. In cobalt- or manganese-based LDHs, one-step polymerization has been observed, leading directly to a material containing polyacrylate intercalate.

Evolution of the mössbauer spectra of ludwigite Co3 - x Fe x O2BO3 with substitution of iron for cobalt

NASA Astrophysics Data System (ADS)

Knyazev, Yu. V.; Ivanova, N. B.; Bayukov, O. A.; Kazak, N. V.; Bezmaternykh, L. N.; Vasiliev, A. D.

2013-06-01

A concentration series of single crystals of iron-cobalt ludwigites Co3 - x Fe x O2BO3 ( x = 0.0125, 0.025, 0.050, 0.10, 1.0) has been synthesized. The structure has been studied using X-ray diffraction and Mössbauer effect. A preferred occupation of nonequivalent crystallographic positions by iron in the ludwigite structure has been revealed. It has been found that the valence of substituting iron ions is three. It has been revealed that the structure of the γ-resonance spectrum of Co2FeO2BO3 is complicated due to a composition disorder in the system.

The Effect of Radiation on the Electrical Properties of Aluminum Gallium Nitride/Gallium Nitride Heterostructures

DTIC Science & Technology

2008-06-01

dopant compensation in both the AlGaN and GaN are the primary factors in the depopulation of the 2DEG. 33 Figure 10. Normalized mobility and...measured by activation analysis. Gold, copper and cobalt wires were irradiated at the position where the devices were to be attached on the fin in the

Synthesis, structural and magnetic properties of Mg0.6Zn0.4CrxFe2-xO4 (0.0 ≤ x ≤ 2.0) nano ferrite

NASA Astrophysics Data System (ADS)

Verma, R.; Kane, S. N.; Raghuvanshi, S.; Satalkar, M.; Modak, S. S.; Mazaleyrat, F.

2018-05-01

Present study reports, effect on structural, magnetic properties of Cr doped Mg-Zn nano-ferrite: Mg0.6Zn0.4CrxFe2-xO4 (0.0≤ x≤2.0), synthesized by sol-gel auto combustion method. X-ray diffraction (XRD), vibrating sample magnetometer (VSM), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) techniques were utilized to monitor the effect of Cr substitution on structural, magnetic properties, and correlation between them. XRD confirms the formation of single phase spinel nano ferrite with particle size ranging between 3.9 - 40.5 nm, whereas EDS confirms the formation of the estimated ferrite composition. Distribution of Mg, Zn, Cr, Fe cations on tetrahedral (A), octahedral (B) site show mixed spinel structure. Increase of Cr content leads to increase of specific surface area (4.35 - 28.28 m2/g), decrease of experimental saturation magnetization at 300 K (varies between 0.57 - 40.95 Am2/kg), and theoretical magnetization at 0 K (range between 13.37 - 56.77 Am2/kg). Observed changes in coercivity values reflect soft magnetic nature of the studied ferrites.

Mechanical and thermomechanical properties of radiation modified poly(ethylene-octene)/Ni-Zn ferrite nanocomposites

NASA Astrophysics Data System (ADS)

Reinholds, I.; Kalkis, V.; Zicans, J.; Merijs Meri, R.; Bockovs, I.; Grigalovica, A.; Muizzemnieks, G.

2013-12-01

Poly(ethylene-1-octene) copolymer (POE) composites filled with nickel-zinc ferrite nanoparticles have been modified by exposure to an electron beam at doses up to 500 kGy. The influence of radiation dose and ferrite content on mechanical properties has been investigated. Thermomechanical properties - thermorelaxation stresses formed in thermal heating and thermo residual stresses resulting in the process of full setting and cooling of materials have been investigated for radiation cross-linked oriented (extended up to 100%) composite samples. Increase of concentration of ferrite particles and increase of radiation dose affects a notable increase of elastic modulus and reduces the deformability in comparison to entire elastomer. Improvement of thermomechanical properties especially at low irradiation doses (100-150 kGy) have been detected for composites with increase of ferrite filler content up to 5 wt. %. It was found that gel content of POE increased up to 85% for pristine POE material with increase of irradiation dose up to 500 kGy due to the formation of cross-linked structure, increase of filler concentration up to 5 wt. % affect reduction in gel fraction due to uniform dispersion in amorphous (ethylene and substituted with hexyl branches) POE phases.

Complex doping of group 13 elements In and Ga in caged skutterudite CoSb 3

DOE PAGES

Xi, Lili; Qiu, Yting; Zheng, Shang; ...

2014-12-12

The complex doping behavior of Ga and In in CoSb 3 has been investigated using ab initio total-energy calculations and thermodynamics. The formation energies of void filling, Sb substitution and complex dual-site occupancy defects with different charge states, and their dependence on chemical potentials of species, were studied. Results show that Ga predominantly forms dual-site 2Ga VF–Ga Sb defects and substitutes for Sb only at very high Fermi levels or electron concentrations. In, on the other hand, can play multiple roles in skutterudites, including filling in the crystalline voids, substituting for Sb atoms or forming dual-site occupancy, among which themore » fully charge-compensated dual-site defects (2In VF–In Sb and 4In VF–2In Sb) are dominant. The equilibrium concentration ratio of impurities at void-filling sites to those at Sb-substitution sites for Ga-doped CoSb 3 is very close to be 2:1, while this value markedly deviates from 2:1 for In-doped CoSb 3. Furthermore, the 2:1 ratio of Ga doping in CoSb 3 leads to low electron concentration (~2 × 10 19 cm –3) and makes the doped system a semiconductor.« less

Synthesis and controllable oxidation of monodisperse cobalt-doped wüstite nanoparticles and their core-shell stability and exchange-bias stabilization.

PubMed

Chen, Chih-Jung; Chiang, Ray-Kuang; Kamali, Saeed; Wang, Sue-Lein

2015-09-14

Cobalt-doped wüstite (CWT), Co0.33Fe0.67O, nanoparticles were prepared via the thermal decomposition of CoFe2-oleate complexes in organic solvents. A controllable oxidation process was then performed to obtain Co0.33Fe0.67O/CoFe2O4 core-shell structures with different core-to-shell volume ratios and exchange bias properties. The oxidized core-shell samples with a ∼4 nm CoFe2O4 shell showed good resistance to oxygen transmission. Thus, it is inferred that the cobalt ferrite shell provides a better oxidation barrier performance than magnetite in the un-doped case. The hysteresis loops of the oxidized 19 nm samples exhibited a high exchange bias field (H(E)), an enhanced coercivity field (H(C)), and a pronounced vertical shift, thus indicating the presence of a strong exchange bias coupling effect. More importantly, the onset temperature of H(E) was found to be higher than 200 K, which suggests that cobalt doping increases the Néel temperature (T(N)) of the CWT core. In general, the results show that the homogeneous dispersion of Co in iron precursors improves the stability of the final CWT nanoparticles. Moreover, the CoFe2O4 shells formed following oxidation increase the oxidation resistance of the CWT cores and enhance their anisotropy energy.

Microstructure, magnetic and microwave absorptive behavior of doped W-type hexaferrite nanoparticles prepared by co-precipitation method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gordani, Gholam Reza, E-mail: gordani@gmail.com; Mohseni, Marzieh; Ghasemi, Ali

2016-04-15

Highlights: • High frequency properties of substituted W-type Sr-hexaferrite. • Saturation magnetization of samples is decreased with increasing of dopants content. • The ferrite sample covers about 6 GHz of bandwidth in K{sub u} band. • The optimum substituted samples can be used as a potential magnetic loss material. • Sample contain x = 0.4 of dopants have shown greater than 90% of reflection loss. - Abstract: Substituted W-type hexaferrite nanoparticles of SrZn{sub 2−x}Co{sub x/2}Ni{sub x/2}Fe{sub 16}O{sub 27} were synthesized by a chemical co-precipitation method. The X-ray diffraction results confirmed that W-type ferrite was identified as the main phase inmore » whole samples in the range of x = 0–0.4. According to magnetic hysteresis loops, with increasing of substituted cations, saturation of magnetization increased and coercivity decreased due to crystalline site occupation of Zn with Ni and Co cations. The microwave reflection loss analysis results in the K{sub u} band (12–18 GHz) show that the highest value of reflection loss of samples was −29.11 dB at frequency of 14.57 GHz with an absorption bandwidth of more than 6 GHz by choosing reflection loss value of −10 dB as a reference. The results indicate that, the sample with appropriate amount of substituted cations hold great promise for microwave device applications.« less

Improving p-type doping efficiency in Al0.83Ga0.17N alloy substituted by nanoscale (AlN)5/(GaN)1 superlattice with MgGa-ON δ-codoping: Role of O-atom in GaN monolayer

NASA Astrophysics Data System (ADS)

Zhong, Hong-xia; Shi, Jun-jie; Zhang, Min; Jiang, Xin-he; Huang, Pu; Ding, Yi-min

2015-01-01

We calculate Mg-acceptor activation energy EA and investigate the influence of O-atom, occupied the Mg nearest-neighbor, on EA in nanoscale (AlN)5/(GaN)1 superlattice (SL), a substitution for Al0.83Ga0.17N disorder alloy, using first-principles calculations. We find that the N-atom bonded with Ga-atom is more easily substituted by O-atom and nMgGa-ON (n = 1-3) complexes are favorable and stable in the SL. The O-atom plays a dominant role in reducing EA. The shorter the Mg-O bond is, the smaller the EA is. The Mg-acceptor activation energy can be reduced significantly by nMgGa-ON δ-codoping. Our calculated EA for 2MgGa-ON is 0.21 eV, and can be further reduced to 0.13 eV for 3MgGa-ON, which results in a high hole concentration in the order of 1020 cm-3 at room temperature in (AlN)5/(GaN)1 SL. Our results prove that nMgGa-ON (n = 2,3) δ-codoping in AlN/GaN SL with ultrathin GaN-layer is an effective way to improve p-type doping efficiency in Al-rich AlGaN.

Structural and optical studies of nitrogen incorporation into GaSb-based GaInSb quantum wells

NASA Astrophysics Data System (ADS)

Nair, Hari P.; Crook, Adam M.; Yu, Kin M.; Bank, Seth R.

2012-01-01

We investigate the incorporation of nitrogen into (Ga,In)Sb grown on GaSb and report room temperature photoluminescence from GaInSb(N) quantum wells. X-ray diffraction and channeling nuclear reaction analysis, together with Rutherford backscattering, were employed to identify the optimal molecular beam epitaxial growth conditions that minimized the incorporation of non-substitutional nitrogen into GaNSb. Consistent with this hypothesis, GaInSb(N) quantum wells grown under the conditions that minimized non-substitutional nitrogen exhibited room temperature photoluminescence, indicative of significantly improved radiative efficiency. Further development of this material system could enable type-I laser diodes emitting throughout the (3-5 μm) wavelength range.

[Synthesis and spectral characteristic of Ga-Fe3O4 at room temperature].

PubMed

Wang, Jing; Deng, Tong; Yang, Cai-Qin; Lin, Yu-Long; Wang, Wei; Wu, Hai-Yan

2008-03-01

Gallium bearing ferrites with different gallium content were synthesized by oxidation of ferrous and gallium ions under alkaline condition and room temperature. The samples were subjected to IR, XRD, Mossbauer spectral analysis and magnetization characterization. The results indicated that the green-rust intermediate phase would be produced during the procedure of Ga-Fe3O4 formation, and the green-rust intermediate phase was converted to ferrites with spinel structure during the drying under hot-N2 atmosphere. With the introduction of gallium into the spinel structure, the interplanar crystal spacing of the spinel structure decreased, as indicated from XRD spectra, and the lattice vibration of M(T)-O-M(o) moved to the high-frequency resulting from IR spectra. A small amount gallium introduction entered the tetrahedral sites preferentially rather than the octahedral sites, and increasing gallium introduction would enhance the occupation of octahedral sites. Furthermore, a small content of gallium in the initial solution could prevent the formation of non-magnetic Fe2O3.

Structural and optical properties of cobalt doped multiferroics BiFeO3 nanostructure thin films

NASA Astrophysics Data System (ADS)

Prasannakumara, R.; Naik, K. Gopalakrishna

2018-05-01

Bismuth ferrite (BiFeO3) and Cobalt doped BiFeO3 (BiFe1-XCoXO3) nanostructure thin films were deposited on glass substrates by the sol-gel spin coating method. The X-ray diffraction patterns (XRD) of the grown BiFeO3 and BiFe1-XCoXO3 nanostructure thin films showed distorted rhombohedral structure. The shifting of peaks to higher angles was observed in cobalt doped BiFeO3. The surface morphology of the BiFeO3 and BiFe1-XCoXO3 nanostructure thin films were studied using FESEM, an increase in grain size was observed as Co concentration increases. The thickness of the nanostructure thin films was examined using FESEM cross-section. The EDX studies confirmed the elemental composition of the grown BiFeO3 and BiFe1-XCoXO3 nanostructure thin films. The optical characterizations of the grown nanostructure thin films were carried out using FTIR, it confirms the existence of Fe-O and Bi-O bands and UV-Visible spectroscopy shows the increase in optical band gap of the BiFeO3 nanostructure thin films with Co doping by ploting Tauc plot.

Cobalt(II) complexes with azole-pyridine type ligands for non-aqueous redox-flow batteries: Tunable electrochemistry via structural modification

NASA Astrophysics Data System (ADS)

Armstrong, Craig G.; Toghill, Kathryn E.

2017-05-01

A single species redox flow battery employing a new class of cobalt(II) complexes with 'tunable' tridentate azole-pyridine type ligands is reported. Four structures were synthesised and their electrochemical, physical and battery characteristics were investigated as a function of successive substitution of the ligand terminal pyridyl donors. The Co(II/I) and Co(III/II) couples are stable and quasi-reversible on gold and glassy carbon electrodes, however redox potentials are tunable allowing the cobalt potential difference to be preferentially increased from 1.07 to 1.91 V via pyridine substitution with weaker σ-donating/π-accepting 3,5-dimethylpyrazole groups. The charge-discharge properties of the system were evaluated using an H-type glass cell and graphite rod electrodes. The complexes delivered high Coulombic efficiencies of 89.7-99.8% and very good voltaic efficiencies of 70.3-81.0%. Consequently, energy efficiencies are high at 63.1-80.8%, marking an improvement on other similar non-aqueous systems. Modification of the ligands also improved solubility from 0.18 M to 0.50 M via pyridyl substitution with 3,5-dimethylpyrazole, though the low solubility of the complexes limits the overall energy capacity to between 2.58 and 12.80 W h L-1. Preliminary flow cell studies in a prototype flow cell are also demonstrated.

Magnetic and dielectric behavior of chromium substituted Co-Mg ferrite nanoparticles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jadoun, Priya, E-mail: priya4jadoun@gmail.com; Jyoti,; Prashant, B. L.

The chromium doped Co-Mg ferrite with composition Co{sub 0.5}Mg{sub 0.5}Cr{sub 0.2}Fe{sub 1.8}O{sub 4} has been synthesized using sol-gel auto combustion method. The crystal structure has been analyzed by X-ray diffraction (XRD) technique. XRD pattern reveals the formation of single phase cubic spinel structure. The magnetic measurements show ferromagnetic behavior at room temperature and large coercivity is observed on cooling down the temperature to 20 K. Dielectric constant (ε’) and dielectric loss tangent (tan δ) have been determined at room temperature as a function of frequency in the frequency range 75 kHz to 80 MHz. The decrease in dielectric constant with increasing frequency attributesmore » to Maxwell Wagner model and conduction mechanism in ferrites.« less

Substitutional and interstitial oxygen in wurtzite GaN

NASA Astrophysics Data System (ADS)

Wright, A. F.

2005-11-01

Density-functional theory was used to compute energy-minimum configurations and formation energies of substitutional and interstitial oxygen (O) in wurtzite GaN. The results indicate that O substituted at a N site (ON) acts as a single donor with the ionized state (ON+1) being the most stable O state in p-type GaN. In n-type GaN, interstitial O (OI) is predicted to be a double acceptor and O substituted at a Ga site (OGa) is predicted to be a triple acceptor. The formation energies of these two species are comparable to that of ON in n-type GaN and, as such, they should form and compensate the ON donors. The extent of compensation was estimated for both Ga-rich and N-rich conditions with a total O concentration of 1017cm-3. Ga-rich conditions yielded negligible compensation and an ON concentration in excess of 9.9×1016cm-3. N-rich conditions yielded a 25% lower ON concentration, due to the increased stability of OI and OGa relative to ON, and moderate compensation. These findings are consistent with experimental results indicating that O acts as a donor in GaN(O). Complexes of ON with the Mg acceptor and OI with the Si donor were examined. Binding energies for charge-conserving reactions were ⩾0.5eV, indicating that these complexes can exist in equilibrium at room temperature. Complexes of ON with the Ga vacancy in n-type GaN were also examined and their binding energies were 1.2 and 1.4eV, indicating that appreciable concentrations can exist in equilibrium even at elevated temperatures.

Electric modulation of conduction in multiferroic Ni-doped GaFeO3 ceramics

NASA Astrophysics Data System (ADS)

Ghani, Awais; Yang, Sen; Rajput, S. S.; Ahmed, S.; Murtaza, Adil; Zhou, Chao; Yu, Zhonghai; Zhang, Yin; Song, Xiaoping; Ren, Xiaobing

2018-06-01

In this work, the effects of Ni substitution on the electrical leakage and multiferroic properties of GaFeO3 were examined. Structural analysis of grown ceramics using x-ray diffraction and Raman shows that all ceramics have pure phases with an orthorhombic structure and space group. Ni substitutions slightly modify lattice parameters and induce lattice distortion within the same crystalline structure. It is observed that with increasing Ni-content up to 0.10, the magnetic transition temperature () increases from 196 K to 407 K. Ni-doped samples showed better ferroelectric properties and a drastic reduction in leakage current (~three orders of magnitude) at room temperature. Enhanced characteristics behavior is observed for 10% Ni substitution (GaFe0.9Ni0.1O3) and higher substitution leads to deterioration of properties with a larger leakage current. It is proposed that the role of Ni substitution can reduce hopping between Fe+3 and Fe+2 as well as suppressing the oxygen vacancies. This work would open new possibilities for integrating polycrystalline GaFeO3 at room temperature for magnetoelectric applications.

The Research Laboratory of Electronics Progress Report Number 133, January 1-December 1990

DTIC Science & Technology

1990-12-31

4 6 Chapter 7 High-Frequency InAlAs/InGaAs Metal -Insulator-Doped Semiconductor...Epitaxy of Compound Semiconductors Chapter 7 High-Frequency InAlAs/InGaAs Metal -Insulator- Doped Semiconductor Field-Effect Transistors (MIDFETs) for...aligned silicided NMOS posed of refractory metals to allow a subsequentdevice fabrication. We have used cobalt deposi- high temperature anneal. This

Band-gap modulation via gallium substitution in cerium doped gadolinium aluminum garnet using a mixed fuel combustion approach

NASA Astrophysics Data System (ADS)

Tyagi, Mohit; Pitale, Shreyas S.; Ghosh, Manoranjan; Shinde, Seema

2014-04-01

Cerium doped Gadolinium garnets (Gd3AlxGa5-xO12 where 0≤x≤5) are synthesized via combustion synthesis using mixture of urea and glycine fuels. A 4h Post annealing at 1400 oC is found to be necessary for pure phase formation. Lattice spacing variation as a result of partial or total Ga substitution at Al site was mapped by X-ray diffraction. Photoluminescence emission of Ce shifts as a consequence of Ga substitution and therefore suggests a local re-adjustment of crystal field around activator site.

The Influence of Different Metal Ions on the Absorption Properties of Nano-Nickel Zinc Ferrite

PubMed Central

Ma, Zhijun; Mang, Changye; Weng, Xingyuan; Si, Liwei; Zhao, Haitao

2018-01-01

The hydrothermal method was used to dope different amounts of Co2+, Mn2+, and Cu2+ in nano-nickel zinc ferrite powder. X-ray diffraction (XRD), a scanning electron microscopy (TEM), and a vector network analyzer (VNA) were used to explore the influence of doping on particle size, morphology, and electromagnetic wave absorption performance. Pure nanometer cobalt nickel zinc ferrite phase was prepared using the hydrothermal method with an increasing Co2+ content. Results showed that the grain type structure changed from a spherical structure to an irregular quadrilateral structure with the average particle size increasing from 35 nm to 60 nm. The lattice constant increased from 0.8352 to 0.8404 nm with Co2+ doping. The increasing Co2+ can change the position of the absorption peak, increase the bandwidth of the absorber, and improve the performance of the materials in GHz low frequency. The doping ratio of Mn2+ can affect the size of the lattice constant, but nanocrystals are easy to reunite without improving the electromagnetic loss. However, the absorbance performance decreases. For the doping of Cu2+, there is an agglomeration phenomenon. When the doping quantity is 0.15, the absorbing wave performance becomes better. PMID:29641477

The Influence of Different Metal Ions on the Absorption Properties of Nano-Nickel Zinc Ferrite.

PubMed

Ma, Zhijun; Mang, Changye; Weng, Xingyuan; Zhang, Qi; Si, Liwei; Zhao, Haitao

2018-04-11

The hydrothermal method was used to dope different amounts of Co 2+ , Mn 2+ , and Cu 2+ in nano-nickel zinc ferrite powder. X-ray diffraction (XRD), a scanning electron microscopy (TEM), and a vector network analyzer (VNA) were used to explore the influence of doping on particle size, morphology, and electromagnetic wave absorption performance. Pure nanometer cobalt nickel zinc ferrite phase was prepared using the hydrothermal method with an increasing Co 2+ content. Results showed that the grain type structure changed from a spherical structure to an irregular quadrilateral structure with the average particle size increasing from 35 nm to 60 nm. The lattice constant increased from 0.8352 to 0.8404 nm with Co 2+ doping. The increasing Co 2+ can change the position of the absorption peak, increase the bandwidth of the absorber, and improve the performance of the materials in GHz low frequency. The doping ratio of Mn 2+ can affect the size of the lattice constant, but nanocrystals are easy to reunite without improving the electromagnetic loss. However, the absorbance performance decreases. For the doping of Cu 2+ , there is an agglomeration phenomenon. When the doping quantity is 0.15, the absorbing wave performance becomes better.

Nano-domain states of strontium ferrites SrFe{sub 1−y}M{sub y}O{sub 2.5+x} (M=V, Mo; y≤0.1; x≤0.2)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ancharova, Uliana V., E-mail: ancharova@gmail.com; Cherepanova, Svetlana V., E-mail: svch@catalysis.ru; Novosibirsk State University, Pirogova st., 2, Novosibirsk 630090

Series of the oxygen-deficient strontium ferrites SrFe{sub 1−y}M{sub y}O{sub 2.5+x} (M=V, Mo, y<0.1; x<0.2) substituted with high-charged cations have been investigated by HRTEM and synchrotron radiation XRD. For artificial lowering of x, all the compounds were treated and quenched in vacuum from 950 °C, which led to the formation of the vacancy-ordered brownmillerite phase at local order. Depending on y, the substituted strontium ferrites have three differently disordered nano-domain states. At y≤0.03 there are twinned lamellar 1D nano-domain structures. At 0.04≤y≤0.05 and 0.06≤y≤0.08 the intergrown 3D nano-domain structures with two different types of disorder are formed. The higher the y,more » the lower the domain size. Disordering phenomena of the 3D nano-domain states were examined with local structure simulations followed by the Debye calculation of XRD patterns. - Graphical abstract: Evolution of nano-domain structure with an increase in the substitution degree y in strontium ferrites SrFe{sub 1−y}M{sub y}O{sub 2.5+x} (M=V, Mo; y≤0.1; x≤0.2): an increase in y decreases the average size of domains and increases the degree of disorder, thus producing the lamellar (1D) or 3D nano-domains. - Highlights: • Two major nanodomain states were found for SrFe{sub 1−y}M{sub y}O{sub 2.5+x} (M=V, Mo, y<0.1; x<0.2). • Both contain vacancy-ordered orthorhombic domains intergrown with cubic matrix. • First (y≤0.03) shows orthorhombic and second (0.04≤y≤0.08) – cubic XRD patterns. • First contains 1D twinned lamellar domains with low-angle boundaries and deformations. • Second contains intergrown isotropic in 3D domains perpendicular oriented in matrix.« less

Evaluation of candidate Stirling engine heater tube alloys after 3500 hours exposure to high pressure doped hydrogen or helium

NASA Technical Reports Server (NTRS)

Misencik, J. A.; Titran, R. H.

1984-01-01

The heater head tubes of current prototype automotive Stirling engines are fabricated from alloy N-155, an alloy which contains 20 percent cobalt. Because the United States imports over 90 percent of the cobalt used in this country and resource supplies could not meet the demand imposed by automotive applications of cobalt in the heater head (tubes plus cylinders and regenerator housings), it is imperative that substitute alloys free of cobalt be identified. The research described herein focused on the heater head tubes. Sixteen alloys (15 potential substitutes plus the 20 percent Co N-155 alloy) were evaluated in the form of thin wall tubing in the NASA Lewis Research Center Stirling simulator materials diesel fuel fired test rigs. Tubes filled with either hydrogen doped with 1 percent CO2 or with helium at a gas pressure of 15 MPa and a temperature of 820 C were cyclic endurance tested for times up to 3500 hr. Results showed that two iron-nickel base superalloys, CG-27 and Pyromet 901 survived the 3500 hr endurance test. The remaining alloys failed by creep-rupture at times less than 3000 hr, however, several other alloys had superior lives to N-155. Results further showed that doping the hydrogen working fluid with 1 vol % CO2 is an effective means of reducing hydrogen permeability through all the alloy tubes investigated.

Paramagnetic resonance studies of bistrispyrazolylborate cobalt(II) and related derivatives

NASA Astrophysics Data System (ADS)

Myers, William K.

Herein, a systematic frozen solution electron-nuclear double resonance (ENDOR) study of high-spin Co(II) complexes is reported to demonstrate the efficacy of methyl substitutions as a means of separating dipolar and contact coupling, and further, to increase the utility of high-spin Co(II) as a spectroscopic probe for the ubiquitous, but spectroscopically-silent Zn(II) metalloenzymes. High-spin (hs) Co(II) has been subject of paramagnetic resonance studies for over 50 years and has been used as a spectroscopic probe for Zn metalloenzymes for over 35 years. However, as will be seen, the inherent complexity of the electronic properties of the cobaltous ion remains to be exploited to offer a wealth of information on Zn(II) enzymatic environments. Specifically, ENDOR measurements on bistrispyrazolylborate cobalt(II) confirm the utility of the novel method of methyl substitution to differentiate dipolar and Fermi contact couplings. An extensive set of electron paramagnetic resonance (EPR) simulations were performed. Software was developed to implement an ENDOR control interface. Finally, proton relaxation measurements were made in the range of 12-42 MHz, which were accounted for with the large g-value anisotropy of the Co(II) compounds. Taken as a whole, these studies point to the rich complexity of the electronic structure of high-spin cobalt(II) and, when sufficiently well-characterized, the great utility it has as a surrogate of biological Zn(II).

Effects of Mg substitution on the structural and magnetic properties of Co0.5Ni0.5-x Mg x Fe2O4 nanoparticle ferrites

NASA Astrophysics Data System (ADS)

R, M. Rosnan; Z, Othaman; R, Hussin; Ali, A. Ati; Alireza, Samavati; Shadab, Dabagh; Samad, Zare

2016-04-01

In this study, nanocrystalline Co-Ni-Mg ferrite powders with composition Co0.5Ni0.5-x Mg x Fe2O4 are successfully synthesized by the co-precipitation method. A systematic investigation on the structural, morphological and magnetic properties of un-doped and Mg-doped Co-Ni ferrite nanoparticles is carried out. The prepared samples are characterized using x-ray diffraction (XRD) analysis, Fourier transform infrared spectroscopy (FTIR), field emission scanning electron microscopy (FESEM), and vibrating sample magnetometry (VSM). The XRD analyses of the synthesized samples confirm the formation of single-phase cubic spinel structures with crystallite sizes in a range of ˜ 32 nm to ˜ 36 nm. The lattice constant increases with increasing Mg content. FESEM images show that the synthesized samples are homogeneous with a uniformly distributed grain. The results of IR spectroscopy analysis indicate the formation of functional groups of spinel ferrite in the co-precipitation process. By increasing Mg2+ substitution, room temperature magnetic measurement shows that maximum magnetization and coercivity increase from ˜ 57.35 emu/g to ˜ 61.49 emu/g and ˜ 603.26 Oe to ˜ 684.11 Oe (1 Oe = 79.5775 A·m-1), respectively. The higher values of magnetization M s and M r suggest that the optimum composition is Co0.5Ni0.4Mg0.1Fe2O4 that can be applied to high-density recording media and microwave devices. Project supported by the Ibnu Sina Institute for Scientific and Industrial Research, Physics Department of Universiti Teknologi Malaysia and the Ministry of Education Malaysia (Grant Nos. Q.J130000.2526.04H65).

Effect Of Neodymium Substitution In Structural Characteristics Of Magnesium Ferrite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Thankachan, Smitha; Binu, P. J.; Xavier, Sheena

2011-10-20

The effect of Nd{sup 3+} substitution on the structural properties of Magnesium ferrite was studied in the series MgNd{sub x}Fe{sub 2-x}O{sub 4}, where x = 0 to 0.3 in steps of 0.05. The series was prepared by sol-gel technique which is one of the novel technique to prepare nanosized samples. Structural characterization was done using X-ray diffractometer and Fourier Transform Infrared Spectrometer. XRD analysis reveals the prepared samples are single phasic till x = 0.2. From x0 = .25, a secondary phase of iron neodymium oxide appears along with the spinel phase. Particle size calculation shows the prepared samples aremore » in the 9nm to 11 nm regime. Lattice parameter was found to increase with concentration of Nd. XRD and FTIR analysis confirmed spinel structure of the prepared samples. XRF result shows the expected composition of prepared samples. The frequency dependence of the dielectric constant in the range 100 Hz--120MHz was also studied« less

Structural characterization of Mg substituted on A/B sites in NiFe_2O_4 nanoparticles using autocombustion method

NASA Astrophysics Data System (ADS)

De, Manojit; Tewari, H. S.

2017-07-01

In the present paper, we are reporting the synthesis of pure nickel and magnesium ferrite [NiFe_2O_4, MgFe_2O_4] and magnesium-substituted nickel ferrite (Ni_{1-x}Mg_{x/y}Fe_{2-y}O_4; x=y=0.60) on A/B sites with particles size in nanometer range using autocombustion technique. In this study, it has been observed that with increase in sintering temperature, the estimated bulk density of the materials increases. The XRD patterns of the samples show the formation of single-phase materials and the lattice parameters are estimated from XRD patterns. From Raman spectra, the Raman shift of pure NiFe_2O_4 and MgFe_2O_4 are comparable with the experimental values reported in literature. The Raman spectra give five Raman active modes (A_{{1g}} + Eg + 3F_{2g}) which are expected in the spinel structure.

Studies on Electrical and Magnetic Properties of Mg-Substituted Nickel Ferrites

NASA Astrophysics Data System (ADS)

Chavan, Pradeep; Naik, L. R.; Belavi, P. B.; Chavan, Geeta; Ramesha, C. K.; Kotnala, R. K.

2017-01-01

The semiconducting polycrystalline ferrite materials with the general formula Ni1- x Mg x Fe2O4 were synthesized by using the solid state reaction method. X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectrographs, and atomic force microscopy techniques were utilized to study the structural parameters. XRD confirms the formation of single phase cubic spinel structure of the ferrites. The crystallite sizes of ferrites determined using the Debye-Scherer formula ranges from 0.963 μm to 1.069 μm. The cation distribution of ferrite shows that Mg2+ ions occupy a tetrahedral site ( A-site) and the Ni2+ ion occupy an octahedral site ( B-site) whereas Fe3+ ions occupies an octahedral as well as a tetrahedral site. The study of elastic parameters such as the longitudinal modulus, rigidity modulus, Young's modulus, bulk modulus, and Debye temperature were estimated using the FTIR technique. The decrease of direct current (DC) resistivity with increase in temperature indicates the semiconducting nature of ferrites. The dielectric constant as well as loss tangent decreases with increase in frequency, and at still higher frequencies, they are almost constant. This shows usual dielectric dispersion behavior attributed to the Maxwell-Wagner type of interfacial polarization and is in accordance with Koop's phenomenological theory. The linear increase of alternating current conductivity with increase of frequency shows the small polaron hopping type of conduction mechanism in all the ferrites. The magnetic properties such as saturation magnetization ( M s ), magnetic moment, coercivity, remnant magnetization ( M r ), and the ratio of M r /M s was estimated using the M-H loop.

Structural and magnetic properties of cobalt ferrite nanoparticles synthesized by co-precipitation at increasing temperatures

NASA Astrophysics Data System (ADS)

Stein, C. R.; Bezerra, M. T. S.; Holanda, G. H. A.; André-Filho, J.; Morais, P. C.

2018-05-01

This study reports on the synthesis and characterization of cobalt ferrite (CoFe2O4) nanoparticles (NPs) synthesized by chemical co-precipitation in alkaline medium at increasing temperatures in the range of 27 °C to 100 °C. High-quality samples in the size range of 5 to 10 nm were produced using very low stirring speed (250 rpm) and moderate alkaline aqueous solution concentration (4.8 mol/L). Three samples were synthesized and characterized by x-ray diffraction (XRD) and room-temperature (RT) magnetization measurements. All samples present superparamagnetic (SPM) behavior at RT and Rietveld refinements confirm the inverse cubic spinel structure (space group Fd-3m (227)) with minor detectable impurity phase. As the synthesis temperature increases, structural parameters such as lattice constant and grain size change monotonically from 8.385 to 8.383 Å and from 5.8 to 7.4 nm, respectively. Likewise, as the synthesis temperature increases the NPs' magnetic moment and saturation magnetization increases monotonically from 2.6 ×103 to 16×103 μB and from 37 to 66 emu/g, respectively. The RT magnetization (M) versus applied field (H) curves were analyzed by the first-order Langevin function averaged out by a lognormal distribution function of magnetic moments. The excellent curve-fitting of the M versus H data is credited to a reduced particle-particle interaction due to both the SPM behavior and the existence of a surface amorphous shell layer (dead layer), the latter reducing systematically as the synthesis temperature increases.

Cell type-specific response to high intracellular loading of polyacrylic acid-coated magnetic nanoparticles

PubMed Central

Lojk, Jasna; Bregar, Vladimir B; Rajh, Maruša; Miš, Katarina; Kreft, Mateja Erdani; Pirkmajer, Sergej; Veranič, Peter; Pavlin, Mojca

2015-01-01

Magnetic nanoparticles (NPs) are a special type of NP with a ferromagnetic, electron-dense core that enables several applications such as cell tracking, hyperthermia, and magnetic separation, as well as multimodality. So far, superparamagnetic iron oxide NPs (SPIONs) are the only clinically approved type of metal oxide NPs, but cobalt ferrite NPs have properties suitable for biomedical applications as well. In this study, we analyzed the cellular responses to magnetic cobalt ferrite NPs coated with polyacrylic acid (PAA) in three cell types: Chinese Hamster Ovary (CHO), mouse melanoma (B16) cell line, and primary human myoblasts (MYO). We compared the internalization pathway, intracellular trafficking, and intracellular fate of our NPs using fluorescence and transmission electron microscopy (TEM) as well as quantified NP uptake and analyzed uptake dynamics. We determined cell viability after 24 or 96 hours’ exposure to increasing concentrations of NPs, and quantified the generation of reactive oxygen species (ROS) upon 24 and 48 hours’ exposure. Our NPs have been shown to readily enter and accumulate in cells in high quantities using the same two endocytic pathways; mostly by macropinocytosis and partially by clathrin-mediated endocytosis. The cell types differed in their uptake rate, the dynamics of intracellular trafficking, and the uptake capacity, as well as in their response to higher concentrations of internalized NPs. The observed differences in cell responses stress the importance of evaluation of NP–cell interactions on several different cell types for better prediction of possible toxic effects on different cell and tissue types in vivo. PMID:25733835

Copper-substituted perovskite compositions for solid oxide fuel cell cathodes and oxygen reduction electrodes in other electrochemical devices

DOEpatents

Rieke, Peter C [Pasco, WA; Coffey, Gregory W [Richland, WA; Pederson, Larry R [Kennewick, WA; Marina, Olga A [Richland, WA; Hardy, John S [Richland, WA; Singh, Prabhaker [Richland, WA; Thomsen, Edwin C [Richland, WA

2010-07-20

The present invention provides novel compositions that find advantageous use in making electrodes for electrochemical cells. Also provided are electrochemical devices that include active oxygen reduction electrodes, such as solid oxide fuel cells, sensors, pumps and the like. The compositions comprises a copper-substituted ferrite perovskite material. The invention also provides novel methods for making and using the electrode compositions and solid oxide fuel cells and solid oxide fuel cell assemblies having cathodes comprising the compositions.

Band-gap modulation via gallium substitution in cerium doped gadolinium aluminum garnet using a mixed fuel combustion approach

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tyagi, Mohit; Pitale, Shreyas S.; Ghosh, Manoranjan

2014-04-24

Cerium doped Gadolinium garnets (Gd{sub 3}Al{sub x}Ga{sub 5−x}O{sub 12} where 0≤x≤5) are synthesized via combustion synthesis using mixture of urea and glycine fuels. A 4h Post annealing at 1400 oC is found to be necessary for pure phase formation. Lattice spacing variation as a result of partial or total Ga substitution at Al site was mapped by X-ray diffraction. Photoluminescence emission of Ce shifts as a consequence of Ga substitution and therefore suggests a local re-adjustment of crystal field around activator site.

Improvement of the magnetic moment of NiZn ferrites induced by substitution of Nd3+ ions for Fe3+ ions

NASA Astrophysics Data System (ADS)

Wu, Xuehang; Chen, Wen; Wu, Wenwei; Wu, Juan; Wang, Qing

2018-05-01

Four types of Ni-Zn based ferrites materials having the general formula Ni0.5Zn0.5NdxFe2-xO4 (0.0 ≤ x ≤ 0.12) have been successfully synthesized by calcining oxalates in air and the influence of Nd content on the structure and magnetic properties of Ni0.5Zn0.5NdxFe2-xO4 is studied. X-ray diffraction examination confirms that a high-crystallized Ni0.5Zn0.5NdxFe2-xO4 with cubic spinel structure is obtained when the precursor is calcined at 1000 °C in air for 2 h. The substitutions of Nd3+ ions for partial Fe3+ ions do not change the spinel crystalline structure of MFe2O4. The incorporation of Nd3+ ions in place of Fe3+ ions in Ni-Zn ferrites increases the average crystallite size. Specific saturation magnetization decreases with increase in Nd content. This is because Nd3+ ions with smaller magnetic moment preferentially fill the octahedral sites. In addition, antiferromagnetic FeNdO3 increases with increase in Nd content. In this study, Ni0.5Zn0.5Nd0.08Fe1.92O4, calcined at 1000 °C, exhibits the highest magnetic moment (4.2954 μB) and the lowest coercivity (28.82 Oe).

Structural and electromagnetic characterization of Co-Mn doped Ni-Sn ferrites fabricated via micro-emulsion route

NASA Astrophysics Data System (ADS)

Ali, Rajjab; Azhar Khan, Muhammad; Manzoor, Alina; Shahid, Muhammad; Farooq Warsi, Muhammad

2017-11-01

Ni0.5Sn0.5CoxMnxFe2-2xO4 ferrites with x = 0.0-0.8 have been prepared by the micro-emulsion method, using CTAB as a surfactant material. X-ray diffraction (XRD), Fourier transformed infrared spectroscopy (FTIR) and vibrational sample magnetometer (VSM) were used to investigate the effects of Co and Mn substitutions on cationic distribution, crystallite size, lattice constant, spectral, magnetic and dielectric properties. Lattice constant and crystallite size were found to increase from 7.4 to 9.25 Å and from 11.8 to 19.7 nm respectively with increasing substitution of Co and Mn ions. Saturation magnetization (MS) gradually increased from 20.5 to 47.6 emu/g with increase in the value of x. However, Coercivity increased from 152.7 to 462.4 Oe up to x = 0.4 and then it decreased thereafter. The dielectric constant, complex dielectric constant and tan loss (tanδ) were observed to decrease with increase in frequency, depicting the semiconductor behavior of the ferrites. Dc resistivity was observed to decrease considerably upon addition of Co and Mn content. The outcome for the tunable magnetic properties and achieved modification of the synthesized nanocrystallites may be chosen for tremendous applications; such as miniaturized memory devices that are based on the energy storage principles and capacitive components.

Prussian blue analogue derived magnetic carbon/cobalt/iron nanocomposite as an efficient and recyclable catalyst for activation of peroxymonosulfate.

PubMed

Lin, Kun-Yi Andrew; Chen, Bo-Jau

2017-01-01

A Prussian blue analogue, cobalt hexacyanoferrate Co 3 [Fe(CN) 6 ] 2 , was used for the first time to prepare a magnetic carbon/cobalt/iron (MCCI) nanocomposite via one-step carbonization of Co 3 [Fe(CN) 6 ] 2 . The resulting MCCI consisted of evenly-distributed cobalt and cobalt ferrite in a porous carbonaceous matrix, making it an attractive magnetic heterogeneous catalyst for activating peroxymonosulfate (PMS). As Rhodamine B (RhB) degradation was adopted as a model test for evaluating activation capability of MCCI, factors influencing RhB degradation were thoroughly examined, including MCCI and PMS dosages, temperature, pH, salt and radical scavengers. A higher MCCI dosage noticeably facilitated the degradation kinetics, whereas insufficient PMS dosage led to ineffective degradation. RhB degradation by MCCI-activated PMS was much more favorable at high temperatures and under neutral conditions. The presence of high concentration of salt slightly interfered with RhB degradation by MCCI-activated PMS. Through examining effects of radical scavengers, RhB degradation by MCCI-activated PMS can be primarily attributed to sulfate radicals instead of a combination of sulfate and hydroxyl radicals. Compared to Co 3 O 4 , a typical catalyst for PMS activation, MCCI also exhibited a higher catalytic activity for activating PMS. In addition, MCCI was proven as a durable and recyclable catalyst for activating PMS over multiple cycles without efficiency loss and significant changes of chemical characteristics. These features demonstrate that MCCI, simply prepared from a one-step carbonization of Co 3 [Fe(CN) 6 ] 2 is a promising heterogeneous catalyst for activating PMS to degrade organic pollutants. Copyright © 2016. Published by Elsevier Ltd.

Improving p-type doping efficiency in Al{sub 0.83}Ga{sub 0.17}N alloy substituted by nanoscale (AlN){sub 5}/(GaN){sub 1} superlattice with Mg{sub Ga}-O{sub N} δ-codoping: Role of O-atom in GaN monolayer

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhong, Hong-xia; Shi, Jun-jie, E-mail: jjshi@pku.edu.cn; Jiang, Xin-he

2015-01-15

We calculate Mg-acceptor activation energy E{sub A} and investigate the influence of O-atom, occupied the Mg nearest-neighbor, on E{sub A} in nanoscale (AlN){sub 5}/(GaN){sub 1} superlattice (SL), a substitution for Al{sub 0.83}Ga{sub 0.17}N disorder alloy, using first-principles calculations. We find that the N-atom bonded with Ga-atom is more easily substituted by O-atom and nMg{sub Ga}-O{sub N} (n = 1-3) complexes are favorable and stable in the SL. The O-atom plays a dominant role in reducing E{sub A}. The shorter the Mg-O bond is, the smaller the E{sub A} is. The Mg-acceptor activation energy can be reduced significantly by nMg{sub Ga}-O{submore » N} δ-codoping. Our calculated E{sub A} for 2Mg{sub Ga}-O{sub N} is 0.21 eV, and can be further reduced to 0.13 eV for 3Mg{sub Ga}-O{sub N}, which results in a high hole concentration in the order of 10{sup 20} cm{sup −3} at room temperature in (AlN){sub 5}/(GaN){sub 1} SL. Our results prove that nMg{sub Ga}-O{sub N} (n = 2,3) δ-codoping in AlN/GaN SL with ultrathin GaN-layer is an effective way to improve p-type doping efficiency in Al-rich AlGaN.« less

Reactions of glycidyl derivatives with ambident nucleophiles; part 2: amino acid derivatives

PubMed Central

Dyker, Gerald; Thöne, Andreas; Henkel, Gerald

2007-01-01

A three-step procedure for the synthesis of multifunctionalized heterocycles from a pyroglutamic acid derivative, glycidyl components and anilines by nucleophilic substitution and cobalt catalysis is presented. PMID:17900352

Synthesis, characterization and investigation of electrochemical and spectroelectrochemical properties of peripherally tetra 4-phenylthiazole-2-thiol substituted metal-free, zinc(II), copper(II) and cobalt(II) phthalocyanines

NASA Astrophysics Data System (ADS)

Demirbaş, Ümit; Akçay, Hakkı Türker; Koca, Atıf; Kantekin, Halit

2017-08-01

In this study novel peripherally tetra 4-phenylthiazole-2-thiol substituted metal-free phthalocyanine (4) and its zinc(II) (5), copper(II) (6) and cobalt(II) (7) derivatives were synthesized and characterized by a combination of various spectroscopic techniques such as FT-IR, 1H-NMR, UV-vis and MALDI-TOF mass. Electrochemical characterizations of metallo-phthalocyanine complexes were conducted by voltammetric and in situ spectroelectrochemical measurements. CoIIPc went [CoIIPc-2]/[CoIPc-2]1-, [CoIPc-2]1-/[CoIPc-3]2-, [CoIPc-3]2-/[CoIPc-4]3- and [CoIIPc-2]/[CoIIPc-2]1+ reduction and oxidation processes respectively. Differently ZnIIPc only showed four ligand-based reductions and two ligand based oxidation processes.

Novel Co(II) phthalocyanines of extended periphery and their water-soluble derivatives. Synthesis, spectral properties and catalytic activity

NASA Astrophysics Data System (ADS)

Filippova, Anna; Vashurin, Artur; Znoyko, Serafima; Kuzmin, Ilya; Razumov, Mikhail; Chernova, Alena; Shaposhnikov, Gennady; Koifman, Oscar

2017-12-01

Novel complexes of cobalt and copper with substituted phthalocyanines were synthesized and characterized. Their water-soluble derivatives were obtained by sulfonation under mild conditions and structurally proved. Aggregation equilibrium in water mediums was shown and influence of geometrical and electron parameters of macroheterocycle peripheral substituents on these processes was established. Catalytic activity upon liquid-phase oxidation of N,N-diethylcarbamodithiolate to thiuram E was studied. Kinetic parameters of substrate oxidation in presence of cobalt phthalocyanines were considered.

Asymmetric intermolecular Pauson-Khand reaction of symmetrically substituted alkynes.

PubMed

Ji, Yining; Riera, Antoni; Verdaguer, Xavier

2009-10-01

The asymmetric intermolecular Pauson-Khand reaction of symmetric alkynes has been accomplished for the first time. N-Phosphino-p-tolylsulfinamide (PNSO) ligands have been identified as efficient ligands in this process. The chirality of the cobalt S-bonded sulfinyl moiety was found to direct olefin insertion into one of the two possible cobalt-carbon bonds in the alkyne complex. Reaction of symmetric alkynes allows for a simplified experimental protocol since there is no need for separation of diastereomeric complexes.

Influence of the manganese and cobalt content on the electrochemical performance of P2-Na0.67MnxCo1-xO2 cathodes for sodium-ion batteries.

PubMed

Hemalatha, K; Jayakumar, M; Prakash, A S

2018-01-23

The resurgence of sodium-ion batteries in recent years is due to their potential ability to form intercalation compounds possessing a high specific capacity and energy density comparable to existing lithium systems. To comprehend the role of cobalt substitution in the structure and electrochemical performance of Na 0.67 MnO 2 , the solid solutions of P2-Na 0.67 Mn x Co 1-x O 2 (x = 0.25, 0.5, 0.75) are synthesized and characterized. The XRD-Rietveld analysis revealed that the Co-substitution in Na 0.67 MnO 2 decreases lattice parameters 'a' and 'c' resulting in the contraction of MO 6 octahedra and the enlargement of inter-layer 'd' spacing. XPS indicates that the isovalent cobalt substitution in Na 0.67 MnO 2 results in the partial/complete replacement of Jahn-Teller active trivalent manganese to form low-spin complexes of better structural stability. The Na-ion diffusion coefficient, D Na + , derived from cyclic voltammetry and impedance spectroscopy, confirmed the enhanced mass transport in Co-rich phases compared to Mn-rich phases. Furthermore, higher diffusion coefficient values are observed for Co 3+ /Co 4+ than for their Mn 3+ /Mn 4+ redox processes. In addition, Co-rich phases exhibit a high structural stability and superior capacity retention, whereas Mn-rich phases discharge higher capacities.

Zn-site Substitution Effect in YbCo2Zn20

NASA Astrophysics Data System (ADS)

Kobayashi, Riki; Takamura, Haruki; Higa, Yasuyuki; Ikeda, Yoichi; Matsubayashi, Kazuyuki; Uwatoko, Yoshiya; Yoshizawa, Hideki; Aso, Naofumi

2017-04-01

We have investigated the substitution effect of YbCo2(Zn1-xTx)20 (T = Cu, Ga, and Cd) systems by using the experiments of X-ray powder diffraction (XRPD), specific heat, magnetic susceptibility, magnetization, and electrical resistivity in order to find out a material that approaches a quantum critical point by chemical pressure. The XRPD and electrical resistivity measurements clarify that the Cu-substitution makes the lattice constants shrink and keeps the magnetic electrical resistivity high, while the Ga- and the Cd-substitution show opposite relation of the Cu-substitution. However, we could not detect clear substitution effect in the specific heat, magnetic susceptibility, and magnetization measurements of Cu-substitution system within our experiments. It is necessary that to study the Cu-substitution samples that have higher x value at lower temperature.

Magnetic properties of Mn-doped GaN with defects: ab-initio calculations

NASA Astrophysics Data System (ADS)

Salmani, E.; Benyoussef, A.; Ez-Zahraouy, H.; H. Saidi, E.

2011-08-01

According to first-principles density functional calculations, we have investigated the magnetic properties of Mn-doped GaN with defects, Ga1-x-yVGxMny N1-z-tVNzOt with Mn substituted at Ga sites, nitrogen vacancies VN, gallium vacancies VG and oxygen substituted at nitrogen sites. The magnetic interaction in Mn-doped GaN favours the ferromagnetic coupling via the double exchange mechanism. The ground state is found to be well described by a model based on a Mn3+-d5 in a high spin state coupled via a double exchange to a partially delocalized hole accommodated in the 2p states of neighbouring nitrogen ions. The effect of defects on ferromagnetic coupling is investigated. It is found that in the presence of donor defects, such as oxygen substituted at nitrogen sites, nitrogen vacancy antiferromagnetic interactions appear, while in the case of Ga vacancies, the interactions remain ferromagnetic; in the case of acceptor defects like Mg and Zn codoping, ferromagnetism is stabilized. The formation energies of these defects are computed. Furthermore, the half-metallic behaviours appear in some studied compounds.

Influence of iron substitution by selected rare-earth ions on the properties of NiZn ferrite fillers and PVC magneto-polymer composites

NASA Astrophysics Data System (ADS)

Ušák, Elemír; Ušáková, Mariana; Dosoudil, Rastislav; Šoka, Martin; Dobročka, Edmund

2018-04-01

Nickel-zinc ferrites are very important soft magnetic materials from the point of view of diverse technical applications (such as, e.g., various electronic devices and components) for their high magnetic permeability and permittivity, low core loss, high resistivity, high Curie temperature as well as mechanical strength and chemical stability. Due to their good absorbing properties, they can be used as microwave absorbing and shielding materials with the aim of decreasing the environmental pollution caused by non-ionizing microwave radiation. The ferrite material incorporated into the polymer matrix creates qualitatively new magneto-polymer composite material taking benefits from both components. The properties typical for polymers (elasticity, mouldability, etc.) are combined with good high-frequency magnetic parameters, thus allowing to utilize these materials, e.g., in high-frequency applications where especially flexibility of composite materials plays a key role. Small amounts of selected rare-earth (RE) ions, in particular Y3+, La3+, Eu3+ and Gd3+ have been embedded into the nickel-zinc ferrite that has been used as the magnetic filler in magnetic polymer composites with polyvinylchloride (PVC) acting as the polymeric matrix. The effect of various types of rare-earth ions on the structural as well as quasi-static and dynamic (electro)magnetic properties of the ferrite fillers as well as ferrite/PVC composites, in particular the frequency dispersion of the complex permeability, has been studied.

A Rice gid1 Suppressor Mutant Reveals That Gibberellin Is Not Always Required for Interaction between Its Receptor, GID1, and DELLA Proteins[W][OA

PubMed Central

Yamamoto, Yuko; Hirai, Takaaki; Yamamoto, Eiji; Kawamura, Mayuko; Sato, Tomomi; Kitano, Hidemi; Matsuoka, Makoto; Ueguchi-Tanaka, Miyako

2010-01-01

To investigate gibberellin (GA) signaling using the rice (Oryza sativa) GA receptor GIBBERELLIN-INSENSITIVE DWARF1 (GID1) mutant gid1-8, we isolated a suppressor mutant, Suppressor of gid1-1 (Sgd-1). Sgd-1 is an intragenic mutant containing the original gid1-8 mutation (L45F) and an additional amino acid substitution (P99S) in the loop region. GID1P99S interacts with the rice DELLA protein SLENDER RICE1 (SLR1), even in the absence of GA. Substitution of the 99th Pro with other amino acids revealed that substitution with Ala (P99A) caused the highest level of GA-independent interaction. Physicochemical analysis using surface plasmon resonance revealed that GID1P99A has smaller Ka (association) and Kd (dissociation) values for GA4 than does wild-type GID1. This suggests that the GID1P99A lid is at least partially closed, resulting in both GA-independent and GA-hypersensitive interactions with SLR1. One of the three Arabidopsis thaliana GID1s, At GID1b, can also interact with DELLA proteins in the absence of GA, so we investigated whether GA-independent interaction of At GID1b depends on a mechanism similar to that of rice GID1P99A. Substitution of the loop region or a few amino acids of At GID1b with those of At GID1a diminished its GA-independent interaction with GAI while maintaining the GA-dependent interaction. Soybean (Glycine max) and Brassica napus also have GID1s similar to At GID1b, indicating that these unique GID1s occur in various dicots and may have important functions in these plants. PMID:21098733

A rice gid1 suppressor mutant reveals that gibberellin is not always required for interaction between its receptor, GID1, and DELLA proteins.

PubMed

Yamamoto, Yuko; Hirai, Takaaki; Yamamoto, Eiji; Kawamura, Mayuko; Sato, Tomomi; Kitano, Hidemi; Matsuoka, Makoto; Ueguchi-Tanaka, Miyako

2010-11-01

To investigate gibberellin (GA) signaling using the rice (Oryza sativa) GA receptor GIBBERELLIN-INSENSITIVE DWARF1 (GID1) mutant gid1-8, we isolated a suppressor mutant, Suppressor of gid1-1 (Sgd-1). Sgd-1 is an intragenic mutant containing the original gid1-8 mutation (L45F) and an additional amino acid substitution (P99S) in the loop region. GID1(P99S) interacts with the rice DELLA protein SLENDER RICE1 (SLR1), even in the absence of GA. Substitution of the 99th Pro with other amino acids revealed that substitution with Ala (P99A) caused the highest level of GA-independent interaction. Physicochemical analysis using surface plasmon resonance revealed that GID1(P99A) has smaller K(a) (association) and K(d) (dissociation) values for GA(4) than does wild-type GID1. This suggests that the GID1(P99A) lid is at least partially closed, resulting in both GA-independent and GA-hypersensitive interactions with SLR1. One of the three Arabidopsis thaliana GID1s, At GID1b, can also interact with DELLA proteins in the absence of GA, so we investigated whether GA-independent interaction of At GID1b depends on a mechanism similar to that of rice GID1(P99A). Substitution of the loop region or a few amino acids of At GID1b with those of At GID1a diminished its GA-independent interaction with GAI while maintaining the GA-dependent interaction. Soybean (Glycine max) and Brassica napus also have GID1s similar to At GID1b, indicating that these unique GID1s occur in various dicots and may have important functions in these plants.

Influence of samarium substitution on the structural and magnetic properties of M-type hexagonal ferrites

NASA Astrophysics Data System (ADS)

Yasmin, Nazia; Mirza, Misbah; Muhammad, Safdar; Zahid, Maria; Ahmad, Mukhtar; Awan, M. S.; Muhammad, Altaf

2018-01-01

The M-type hexagonal ferrites with chemical formula SrFe12-xSmxO19 (x = 0, 0.01, 0.02, 0.03) were synthesized via sol-gel method. We studied the effects of substitution of rare earth on the structural and magnetic temperament of M-type hexaferrites. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) strategies are employed for the systematical examination of micrographs and structures of the samples. The magnetic particularities are studied by the use of vibrating sample magnetometery. The M-H loops are used to investigate the hard magnetic behavior of all the samples. The substantial value of coercivity (>1 kOe) for all the samples shows that the particular sample is permanent magnet and reveals the hard magnetic action. It is observed that values of saturation magnetization (Mr) and remanence (Ms) decline with increasing the rare earth ions substitution. This decrease may follow spin canting and the magnetic dilution, which results in dislocation of superexchange interactions. The improvement in Hc may be because of large anisotropy of magnetocrystalline, where ion anisotropy of Fe2+ ion on the 2a site probably overriding in all hexaferrites series. The synthesized composites were useful for applications in magnetic microwave absorbing materials.

The Structure and Properties of Plasma Sprayed Iron Oxide Doped Manganese Cobalt Oxide Spinel Coatings for SOFC Metallic Interconnectors

NASA Astrophysics Data System (ADS)

Puranen, Jouni; Lagerbom, Juha; Hyvärinen, Leo; Kylmälahti, Mikko; Himanen, Olli; Pihlatie, Mikko; Kiviaho, Jari; Vuoristo, Petri

2011-01-01

Manganese cobalt oxide spinel doped with Fe2O3 was studied as a protective coating on ferritic stainless steel interconnects. Chromium alloying causes problems at high operation temperatures in such oxidizing conditions where chromium compounds evaporate and poison the cathode active area, causing the degradation of the solid oxide fuel cell. In order to prevent chromium evaporation, these interconnectors need a protective coating to block the chromium evaporation and to maintain an adequate electrical conductivity. Thermal spraying is regarded as a promising way to produce dense and protective layers. In the present work, the ceramic Mn-Co-Fe oxide spinel coatings were produced by using the atmospheric plasma spray process. Coatings with low thickness and low amount of porosity were produced by optimizing deposition conditions. The original spinel structure decomposed because of the fast transformation of solid-liquid-solid states but was partially restored by using post-annealing treatment.

Synthesis, characterization, and growth mechanism of motifs of ultrathin cobalt-substituted NaFeSi 2O 6 nanowires

DOE PAGES

Lewis, Crystal S.; Moronta, Dominic; Terban, Maxwell W.; ...

2017-12-12

In this report, we have synthesized and structurally characterized nanowire bundles of cobalt-substituted pyroxenes, similar to the crystal structure of aegirine (i.e. Co-substituted XYSi 2O 6 with X and Y referring to metallic elements such as but not limited to Co, Na, and Fe), using a readily scalable hydrothermal technique. We then propose a growth mechanism for these bundles, based on detailed time and temperature dependent studies as well as complementary control experiments, particularly reactions in the absence of either 3-aminopropyltriethoxysilane (APTES) or sodium hydroxide (NaOH), via a transmission electron microscopy visualization study. Moreover, these nanowire bundles were probed formore » their magnetic properties and chemical composition using superconducting quantum interference device (SQUID) measurements, X-ray diffraction, and pair distribution function analysis, respectively. Specifically, SQUID measurement observations highlighted that these bundles evince (i) unique and interesting super-paramagnetic properties at 5 K that are consistent with that of our previously published ~2 nm ultra-small nanoparticles as well as (ii) paramagnetic behavior at 300 K.« less

Synthesis, characterization, and growth mechanism of motifs of ultrathin cobalt-substituted NaFeSi 2O 6 nanowires

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lewis, Crystal S.; Moronta, Dominic; Terban, Maxwell W.

In this report, we have synthesized and structurally characterized nanowire bundles of cobalt-substituted pyroxenes, similar to the crystal structure of aegirine (i.e. Co-substituted XYSi 2O 6 with X and Y referring to metallic elements such as but not limited to Co, Na, and Fe), using a readily scalable hydrothermal technique. We then propose a growth mechanism for these bundles, based on detailed time and temperature dependent studies as well as complementary control experiments, particularly reactions in the absence of either 3-aminopropyltriethoxysilane (APTES) or sodium hydroxide (NaOH), via a transmission electron microscopy visualization study. Moreover, these nanowire bundles were probed formore » their magnetic properties and chemical composition using superconducting quantum interference device (SQUID) measurements, X-ray diffraction, and pair distribution function analysis, respectively. Specifically, SQUID measurement observations highlighted that these bundles evince (i) unique and interesting super-paramagnetic properties at 5 K that are consistent with that of our previously published ~2 nm ultra-small nanoparticles as well as (ii) paramagnetic behavior at 300 K.« less

Influence of composition on phase occurrence during charge process of AB 5+x Ni-MH negative electrode materials

NASA Astrophysics Data System (ADS)

Vivet, S.; Latroche, M.; Chabre, Y.; Joubert, J.-M.; Knosp, B.; Percheron-Guégan, A.

2005-05-01

Multi-substituted LaNi 5-type alloys (AB 5+x) are widely used as negative electrode materials in commercial Ni-MH batteries. Cobalt substitution on Ni sites allows to enhance battery cycle life by reducing alloy pulverization induced by hydrogen cycling. This improvement is attributed to the occurrence of a three-phase process (α, β and γ) during electrochemical hydrogen loading. In order to better understand the effect of the composition on the phase occurrence and to reduce the rate of costly cobalt, an in situ neutron diffraction study has been performed at room temperature during electrochemical charge of two different electrode materials MmNi 4.07Mn 0.63Al 0.2M 0.4 with M=Fe and Mn and B/A=5.3. These cobalt free compounds show cycle life comparable to that of commercial materials. The results show that three phases are also observed for these samples. The γ-phase content depends on M and is higher for M=Fe than for M=Mn. These results are related to the improved cycle lives and to the alloy pulverization process.

Cobalt doping of the MOF-5 framework and its effect on gas-adsorption properties.

PubMed

Botas, Juan A; Calleja, Guillermo; Sánchez-Sánchez, Manuel; Orcajo, M Gisela

2010-04-20

Partial isomorphic substitution of Zn in IRMOF metal clusters by cobalt ions is described for the first time. Specifically, different numbers of Co(2+) ions have been incorporated during solvothermal crystallization into the Zn-based MOF-5 (IRMOF-1) framework, which is one of the most studied MOF materials. The amount of Zn that can be substituted seems to be limited, being no more than 25% of total metal content, that is, no more than one Co atom inside every metal cluster formed by four transition-metal ions, on average. Several characterization techniques, including X-ray diffraction, DR UV-visible spectroscopy, N(2) adsorption isotherms, and thermogravimetrical analysis, strongly support the effective incorporation of Co into the material framework. As-synthesized CoMOF-5 has cobalt ions in octahedral coordination, changing to tetrahedral by simple evacuation, presumably by the removal of two diethylformamide molecules per Co ion. Moreover, the H(2), CH(4), and CO(2) uptake of MOF-5 materials systematically increases with the Co content, particularly at high pressure. Such an increase is moderate anyway, considering that Co is incorporated into unexposed metal sites that are less accessible to gas molecules.

Magnesium doping of efficient GaAs and Ga(0.75)In(0.25)As solar cells grown by metalorganic chemical vapor deposition

NASA Technical Reports Server (NTRS)

Lewis, C. R.; Ford, C. W.; Werthen, J. G.

1984-01-01

Magnesium has been substituted for zinc in GaAs and Ga(0.75)In(0.25)As solar cells grown by metalorganic chemical vapor deposition (MOCVD). Bis(cyclopentadienyl)magnesium (Cp2Mg) is used as the MOCVD transport agent for Mg. Full retention of excellent material quality and efficient cell performance results. The substitution of Mg for Zn would enhance the abruptness and reproducibility of doping profiles, and facilitate high temperature processing and operation, due to the much lower diffusion coefficient of Mg, relative to Zn, in these materials.

Nanoscale-driven crystal growth of hexaferrite heterostructures for magnetoelectric tuning of microwave semiconductor integrated devices.

PubMed

Hu, Bolin; Chen, Zhaohui; Su, Zhijuan; Wang, Xian; Daigle, Andrew; Andalib, Parisa; Wolf, Jason; McHenry, Michael E; Chen, Yajie; Harris, Vincent G

2014-11-25

A nanoscale-driven crystal growth of magnetic hexaferrites was successfully demonstrated at low growth temperatures (25-40% lower than the temperatures required often for crystal growth). This outcome exhibits thermodynamic processes of crystal growth, allowing ease in fabrication of advanced multifunctional materials. Most importantly, the crystal growth technique is considered theoretically and experimentally to be universal and suitable for the growth of a wide range of diverse crystals. In the present experiment, the conical spin structure of Co2Y ferrite crystals was found to give rise to an intrinsic magnetoelectric effect. Our experiment reveals a remarkable increase in the conical phase transition temperature by ∼150 K for Co2Y ferrite, compared to 5-10 K of Zn2Y ferrites recently reported. The high quality Co2Y ferrite crystals, having low microwave loss and magnetoelectricity, were successfully grown on a wide bandgap semiconductor GaN. The demonstration of the nanostructure materials-based "system on a wafer" architecture is a critical milestone to next generation microwave integrated systems. It is also practical that future microwave integrated systems and their magnetic performances could be tuned by an electric field because of the magnetoelectricity of hexaferrites.

Metallographic study of metallic fragment of lunar surface material

NASA Technical Reports Server (NTRS)

Mints, R. I.; Petukhova, T. M.; Ivanov, A. V.

1974-01-01

A high precision investigation of a metallic fragment from the lunar material returned by the Soviet Luna 16 automatic station revealed three characteristic temperature intervals with different kinetics of solid solution decomposition. The following were found in the structure of the iron-nickel-cobalt alloy: (1) delta-phase and alpha-ferrite of diffusional, displacement origin in the grain boundary and acicular forms; and (2) martensite of isothermal and athermal nature, acicular, lamellar, massive, and dendritic. The diversity of the shapes of structural constituents is associated with the effect on their formation of elastic distortions and various mechanisms of deformation relaxation processes.

Comparing highly ordered monolayers of nanoparticles fabricated using electrophoretic deposition: Cobalt ferrite nanoparticles versus iron oxide nanoparticles

DOE PAGES

Dickerson, James H.; Krejci, Alex J.; Garcia, Adriana -Mendoza; ...

2015-08-01

Ordered assemblies of nanoparticles remain challenging to fabricate, yet could open the door to many potential applications of nanomaterials. Here, we demonstrate that locally ordered arrays of nanoparticles, using electrophoretic deposition, can be extended to produce long-range order among the constituents. Voronoi tessellations along with multiple statistical analyses show dramatic increases in order compared with previously reported assemblies formed through electric field-assisted assembly. As a result, based on subsequent physical measurements of the nanoparticles and the deposition system, the underlying mechanisms that generate increased order are inferred.

Structure analysis of aqueous ferrofluids at interface with silicon: neutron reflectometry data

NASA Astrophysics Data System (ADS)

Gapon, I. V.; Petrenko, V. I.; Bulavin, L. A.; Balasoiu, M.; Kubovcikova, M.; Zavisova, V.; Koneracka, M.; Kopcansky, P.; Chiriac, H.; Avdeev, M. V.

2017-05-01

Adsorption of nanoparticles from aqueous ferrofluids (FFs) on solid surface (crystalline silicon) was studied by neutron reflectometry (NR). Two kinds of FFs were considered. First kind was heavy water-based ferrofluids with magnetite nanoparticles coated by double layer of sodium oleate. Second one FF was cobalt ferrite nanoparticles stabilized by lauric acid/sodium n-dodecylsulphate layer and dispersed in water. It was obtained only a single adsorption layer for two types of ferrofluids. The impact of the magnetic nanoparticles concentration and geometry was considered in frame of the adsorption characteristic of FFs.

Electronic Structure of p- and n-Type Doping Impurities in Cubic Gallium Nitride

NASA Astrophysics Data System (ADS)

Pentaleri, E. A.; Gubanov, V. A.; Fong, C. Y.; Klein, B. M.

1996-03-01

LMTO-TB calculations were performed to investigate the electronic structure of C, Be, Mg, Si, Zn, and Cd substitutional impurities in cubic GaN (c-GaN). The calculations used 128-site supercells consisting of 64-atoms. Empty spheres of two types occupied the remaining sites. Semi-core Ga 3d states were treated explicitly as valence states. Both amphoteric substitutions were considered for C and Si impurities, while only cation-site substitutions were considered for Be, Mg, Zn, and Cd. All metal impurities formed partially occupied impurity states at the VB edge, which may result in p-type conductivity. C and Si impurities substituted at anion sites form sharp resonances in the gap, and are inactive in creating either p- or n-type carriers. Likewise, cation-site C substitutions introduce to the middle of the band gap strongly localized states that are inactive in carrier formation. Cation-site Si substitutions form an impurity sub-band at the CB edge, leading to n-type conductivity. The DOS at the Fermi level for each impurity-doped c-GaN crystal is used to estimate the most effective p-type doping impurities. The wave-function composition, space, and energy localization is analyzed for different impurities via projections onto the orbital basis and atomic coordinational spheres, and by examining calculated charge-density distributions.

Doping process of p-type GaN nanowires: A first principle study

NASA Astrophysics Data System (ADS)

Xia, Sihao; Liu, Lei; Diao, Yu; Feng, Shu

2017-10-01

The process of p-type doping for GaN nanowires is investigated using calculations starting from first principles. The influence of different doping elements, sites, types, and concentrations is discussed. Results suggest that Mg is an optimal dopant when compared to Be and Zn due to its stronger stability, whereas Be atoms are more inclined to exist in the interspace of a nanowire. Interstitially-doped GaN nanowires show notable n-type conductivity, and thus, Be is not a suitable dopant, which is to be expected since systems with inner substitutional dopants are more favorable than those with surface substitutions. Both interstitial and substitutional doping affect the atomic structure near dopants and induce charge transfer between the dopants and adjacent atoms. By altering doping sites and concentrations, nanowire atomic structures remain nearly constant. Substitutional doping models show p-type conductivity, and Mg-doped nanowires with doping concentrations of 4% showing the strongest p-type conductivity. All doping configurations are direct bandgap semiconductors. This study is expected to direct the preparation of high-quality GaN nanowires.

A unique substituted Co(II)-formate coordination framework exhibits weak ferromagnetic single-chain-magnet like behavior.

PubMed

Zhao, Jiong-Peng; Yang, Qian; Liu, Zhong-Yi; Zhao, Ran; Hu, Bo-Wen; Du, Miao; Chang, Ze; Bu, Xian-He

2012-07-04

A magnetic isolated chain-based substituted cobalt-formate framework was obtained with isonicotine as a spacer. In the chain, canted antiferromagnetic interactions exist in between the Co(II) ions, and slow magnetic relaxation is detected at low temperature. For the block effects of the isonicotine ligands, the complex could be considered as a peculiar example of a weak ferromagnetic single-chain-magnet.

Effect of dilution in the cobalt subsystem on phase transitions in rare-earth cobaltites RBaCo4- x M x O7 (R = Dy-Er, Yb, Y; M = Al, Zn)

NASA Astrophysics Data System (ADS)

Kazei, Z. A.; Snegirev, V. V.; Kozeeva, L. P.; Kameneva, M. Yu.

2016-01-01

We have experimentally studied the structural and elastic characteristics of rare-earth cobaltites RBaCo4- x M x O7 (R = Dy-Er, Yb, Y), in which cobalt ions are partly substituted by diamagnetic Al or Zn ions. It was found that small substitution of Co3+ ions by Al3+ ions in the YbRBaCo4- x M x O7 system ( x = 0.1, 0.2, 0.5) leads to a rapid decrease and smearing of Δ E( T) /E 0 anomalies of the Young's modulus in the region of the structural phase transition, which is accompanied by increasing hysteresis. Pure rare-earth cobaltites RBaCo4O7 (R = Dy-Er, Y) exhibit a correlation between the room-temperature structure distortion and hysteresis on the Δ E( T)/ E 0 curve in a temperature interval of 80-280 K. In Zn-substituted cobaltites RBaCoZn3O7, both the hysteresis and Δ E( T)/ E 0 anomalies disappear, as do low-temperature sound absorption maxima. This behavior is evidence of the suppression of structural and magnetic phase transitions and the retention of only short-range correlations of the order parameter in Zn-substituted samples.

Transformation of cooperative free energies between ligation systems of hemoglobin: resolution of the carbon monoxide binding intermediates.

PubMed

Huang, Y; Ackers, G K

1996-01-23

A strategy has been developed for quantitatively "translating" the distributions of cooperative free energy between different oxygenation analogs of hemoglobin (Hb). The method was used to resolve the cooperative free energies of all eight carbon monoxide binding intermediates. These parameters of the FeCOHb system were determined by thermodynamic transformation of corresponding free energies obtained previously for all species of the Co/FeCO system, i.e., where cobalt-substituted hemes comprise the unligated sites [Speros, P. C., et al. (1991) Biochemistry 30, 7254-7262]. Using hybridized combinations of normal and cobalt-substituted Hb, ligation analog systems Co/FeX (X = CO, CN) were constructed and experimentally quantified. Energetics of cobalt-induced structural perturbation were determined for all species of both the "mixed metal" Co/Fe system and also the ligated Co/FeCN system. It was found that major energetic perturbations of the Co/Fe hybrid species originate from a pure cobalt substitution effect on the alpha subunits. These perturbations are transduced to the beta subunit within the same dimeric half-tetramer, resulting in alteration of the free energies for binding at the nonsubstituted (Fe) sites. Using the linkage strategy developed in this study along with the determined energetics of these couplings, the experimental assembly free energies for the Co/FeCO species were transformed into cooperative free energies of the 10 Fe/FeCO species. The resulting values were found to distribute according to predictions of a symmetry rule mechanism proposed previously [Ackers, G. K., et al. (1992) Science 255, 54-63]. Their distribution is consistent with accurate CO binding data of normal Hb [Perrella, M., et al. (1990b) Biophys. Chem. 37, 211-223] and also with accurate O2 binding data obtained under the same conditions [Chu, A. H., et al. (1984) Biochemistry 23, 604-617].

Photodynamic Effect of some Phthalocyanines on Enveloped and Naked Viruses.

PubMed

Nikolaeva-Glomb, L; Mukova, L; Nikolova, N; Kussovski, V; Doumanova, L; Mantareva, V; Angelov, I; Wöhrle, D; Galabov, A S

Activity of three photosensitizing phthalocyanine derivatives was tested for photodynamic inactivation towards two coated and two non-enveloped viruses - bovine viral diarrhea virus (BVDV), influenza virus A(H3N2), poliovirus type 1 (PV-1) and human adenovirus type 5 (HAdV5). In the case of coated viruses, a combination of virucidal and irradiation effects was registered by octa-methylpyridyloxy-substituted Ga phthalocyanine (Ga8) toward BVDV, whereas tetra-methylpyridyloxy-substituted Ga phthalocyanine (Ga4) revealed a marked photoinactivation only. No such effect was observed towards influenza A virus. In contrast, the photoinactivating potential of Ga4 and Ga8 marked very high values on naked viruses, especially on HAdV5, at which both the virucidal as well as the irradiation effects became combined.

Conservation of Strategic Aerospace Materials (COSAM)

NASA Technical Reports Server (NTRS)

Stephens, J. R.

1981-01-01

Research efforts to reduce the dependence of the aerospace industry on strategic metals, such as cobalt (Co), columbium (Cb), tantalum (Ta), and chromium (Cr), by providing the materials technology needed to minimize the strategic metal content of critical aerospace components for gas turbine engines are addressed. Thrusts in three technology areas are identified: near term activities in the area of strategic element substitution; intermediate-range activities in the area of materials processing; and long term, high risk activities in the area of 'new classes' of high temprature metallic materials. Specifically, the role of cobalt in nickel-base and cobalt-base superalloys vital to the aerospace industry is examined along with the mechanical and physical properties of intermetallics that will contain a minimum of the stragetic metals.

Transport and {Tc} anomalies around x = 0.22 in La{sub 2{minus}x}Sr{sub x}Cu{sub 1{minus}y}M{sub y}O{sub 4} (M = Zn, Ga, Ni): Possibility of charge and/or spin ordering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Koike, Y.; Kakinuma, N.; Aoyama, M.

1999-12-01

Transport and {Tc} anomalies around x = 0.22 in La{sub 2{minus}x}Sr{sub x}CuO{sub 4} have been studied through the partial substitution of Zn, Ga and Ni for Cu. It has been found that the value of x where the anomalies occur shifts to lower x values through the Zn substitution, while it shifts to larger x values through the Ga substitution, and it disappears through the Ni substitution. There is a possibility that an order of holes and/or spins, such as the so-called stripe order, is formed or fluctuates around x = 0.22 in La{sub 2{minus}x}Sr{sub x}CuO{sub 4}.

Preparation of Scandium-Doped, Textured, M-Type Barium Ferrite via a Wet Magnetizing Orientation Process

NASA Astrophysics Data System (ADS)

Wang, Yu; Liu, Yingli; Zhang, Huaiwu; Li, Jie; Gao, Liwen; Chen, Daming; Chen, Yong

2018-02-01

In this paper, a wet magnetizing orientation process was applied to synthesize c-axis-textured, M-type barium ferrite (BaFe12O19 or BaM), which is widely used to produce hard magnetic materials. To modify the magnetic properties of the BaM ferrite and make it suitable for certain operating frequencies, Sc3+ was substituted into Fe3+ sites of the BaM crystal structure. A BaSc x Fe12- x O19 ferrite with a typical relative density of ˜ 75% was successfully obtained. We used x-ray diffraction, scanning electronic microscopy, and a vibrating sample magnetometer to obtain phase information, detail of the microstructure, and magnetic properties of the BaSc x Fe12- x O19, respectively. The composition BaSc x Fe12- x O19 ( x = 0.1) featured a superior squareness ratio of ˜ 67% and a saturation magnetization ( M S) of ˜ 5300 Gauss in magnetic hysteresis loop measurements. These features match well with requirements for self-biased passive devices. Moreover, the site preference of Sc3+ in the hexagonal crystal structure was investigated.

NASA's activities in the conservation of strategic aerospace materials

NASA Technical Reports Server (NTRS)

Stephens, J. R.

1980-01-01

The United States imports 50-100 percent of certain metals critical to the aerospace industry, namely, cobalt, columbium, chromium, and tantalum. In an effort to reduce this dependence on foreign sources, NASA is planning a program called Conservation of Strategic Aerospace Materials (COSAM), which will provide technology minimizing strategic metal content in the components of aerospace structures such as aircraft engines. With a proposed starting date of October 1981, the program will consist of strategic element substitution, process technology development, and alternate materials research. NASA's two-fold pre-COSAM studies center on, first, substitution research involving nickel-base and cobalt-base superalloys (Waspaloy, Udimet-700, MAE-M247, Rene 150, HA-188) used in turbine disks, low-pressure blades, turbine blades, and combustors; and, second, alternate materials research devoted initially to investigating possible structural applications of the intermetallic alloys nickel aluminide and iron aluminide.

Microwave and millimeter wave dielectric permittivity and magnetic permeability of epsilon-gallium-iron-oxide nano-powders

NASA Astrophysics Data System (ADS)

Chao, Liu; Afsar, Mohammed N.; Ohkoshi, Shin-ichi

2015-05-01

In millimeter wave frequency range, hexagonal ferrites with high uniaxial anisotropic magnetic fields are used as absorbers. These ferrites include M-type barium ferrite (BaFe12O19) and strontium ferrite (SrFe12O19), which have natural ferromagnetic resonant frequency range from 40 GHz to 60 GHz. However, the higher frequency range lacks suitable materials that support the higher frequency ferromagnetic resonance. A series of gallium-substituted ɛ-iron oxides (ɛ-GaxFe2-xO3) are synthesized, which have ferromagnetic resonant frequencies appearing over the frequency range of 30 GHz to 150 GHz. The ɛ-GaxFe2-xO3 is synthesized by the sol-gel method. The particle sizes are observed to be smaller than 100 nm. In this paper, in-waveguide transmission and reflection method and the free space magneto-optical approach have been employed to study these newly developed ɛ-GaxFe2-xO3 particles in millimeter waves. These techniques enable to obtain precise transmission spectra to determine the dielectric and magnetic properties of both isotropic and anisotropic ferrites in the microwave and millimeter wave frequency range from single set of direct measurements. The complex dielectric permittivity and magnetic permeability spectra of ɛ-GaxFe2-xO3 are shown in this paper. Strong ferromagnetic resonances at different frequencies determined by the x parameter are found.

Magnetic properties of Sn-substituted Ni-Zn ferrites synthesized from nano-sized powders of NiO, ZnO, Fe2O3, and SnO2

NASA Astrophysics Data System (ADS)

Ali, MA; Uddin, MM; Khan, MNI; Chowdhury, FUZ; Hoque, SM; Liba, SI

2017-06-01

A series of Ni0.6-x/2Zn0.4-x/2Sn x Fe2O4 (x = 0.0, 0.05, 0.1, 0.15, 0.2, and 0.3) (NZSFO) ferrite composities have been synthesized from nano powders using a standard solid state reaction technique. The spinel cubic structure of the investigated samples has been confirmed by x-ray diffraction (XRD). The magnetic properties such as saturation magnetization ({M}{{s}}), remanent magnetization ({M}{{r}}), coercive field ({H}{{c}}), and Bohr magneton (μ) are calculated from the hysteresis loops. The value of {M}{{s}} is found to decrease with increasing Sn content in the samples. This change is successfully explained by the variation of A-B interaction strength due to Sn substitution in different sites. The compositional stability and quality of the prepared ferrite composites have also been endorsed by the fairly constant initial permeability ({μ }^{\\prime }) over a wide range of frequency. The decreasing trend of {μ }^{\\prime } with increasing Sn content has been observed. Curie temperature {T}{{C}} has been found to increase with the increase in Sn content. A wide spread frequency utility zone indicates that the NZSFO can be considered as a good candidate for use in broadband pulse transformers and wide band read-write heads for video recording. The composition of x = 0.05 shows unusual results and the possible reason is also mentioned with the established formalism.

Influence of Al3+ substitution on the electrical resistivity and dielectric behavior of Ni0.25Cu0.20Zn0.55AlxFe2-xO4 ferrites synthesized by solid state reaction technique

NASA Astrophysics Data System (ADS)

Rahman, K. R.; Chowdhury, F.-U.-Z.; Khan, M. N. I.

2017-12-01

In this paper, the effect of Al3+ substitution on the electrical and dielectric properties of Ni0.25Cu0.20Zn0.55AlxFe2-xO4 ferrites with x = 0.0, 0.05. 0.10, 0.15 and 0.20, synthesized by solid state reaction has been reported. Using two probe method, the DC resistivity has been investigated in the temperature range from 30 °C to 300 °C. Activation energy was calculated from the Arrhenius plot. The electrical conduction is explained on the basis of the hopping mechanism. The frequency dependent dielectric properties of these spinel ferrites have been studied at room temperature by measuring AC resistivity, conductivity (σac), dielectric constant and dielectric loss tangent (tan δ) in the frequency range between 1 kHz and 120 MHz. The study of dielectric properties showed that the dielectric constant and dielectric loss increased with increasing non-magnetic Al ions. The dependence of dielectric constant with frequency has been explained by Maxwell-Wagner interfacial polarization. Cole-Cole plots show semicircular arc(s) for the samples, and equivalent RC circuits have been proposed to clarify the phenomena involved therein. The analysis of complex impedance spectroscopy has been used to distinguish between the grain and grain boundary contribution to the total resistance.

Cobalt Ferrite Bearing Nitrogen-Doped Reduced Graphene Oxide Layers Spatially Separated with Microporous Carbon as Efficient Oxygen Reduction Electrocatalyst.

PubMed

Kashyap, Varchaswal; Singh, Santosh K; Kurungot, Sreekumar

2016-08-17

The present work discloses how high-quality dispersion of fine particles of cobalt ferrite (CF) could be attained on nitrogen-doped reduced graphene oxide (CF/N-rGO) and how this material in association with a microporous carbon phase could deliver significantly enhanced activity toward electrochemical oxygen reduction reaction (ORR). Our study indicates that the microporous carbon phase plays a critical role in spatially separating the layers of CF/N-rGO and in creating a favorable atmosphere to ensure the seamless distribution of the reactants to the active sites located on CF/N-rGO. In terms of the ORR current density, the heat-treated hybrid catalyst at 150 °C (CF/N-rGO-150) is found to be clearly outperforming (7.4 ± 0.5 mA/cm(2)) the state-of-the-art 20 wt % Pt-supported carbon catalyst (PtC) (5.4 ± 0.5 mA/cm(2)). The mass activity and stability of CF-N-rGO-150 are distinctly superior to PtC even after 5000 electrochemical cycles. As a realistic system level exploration of the catalyst, testing of a primary zinc-air battery could be demonstrated using CF/N-rGO-150 as the cathode catalyst. The battery is giving a galvanostatic discharge time of 15 h at a discharge current density of 20 mA/cm(2) and a specific capacity of ∼630 mAh g(-1) in 6 M KOH by using a Zn foil as the anode. Distinctly, the battery performance of this system is found to be superior to that of PtC in less concentrated KOH solution as the electrolyte.

Evaluation of humidity sensing properties of TMBHPET thin film embedded with spinel cobalt ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Zafar, Qayyum; Azmer, Mohamad Izzat; Al-Sehemi, Abdullah G.; Al-Assiri, Mohammad S.; Kalam, Abul; Sulaiman, Khaulah

2016-07-01

In this study, we report the enhanced sensing parameters of previously reported TMBHPET-based humidity sensor. Significant improved sensing performance has been demonstrated by coupling of TMBHPET moisture sensing thin film with cobalt ferrite nanoparticles (synthesized by eco-benign ultrasonic method). The mean size of CoFe2O4 nanoparticles has been estimated to be 6.5 nm. It is assumed that the thin film of organic-ceramic hybrid matrix (TMBHPET:CoFe2O4) is a potential candidate for humidity sensing utility by virtue of its high specific surface area and porous surface morphology (as evident from TEM, FESEM, and AFM images). The hybrid suspension has been drop-cast onto the glass substrate with preliminary deposited coplanar aluminum electrodes separated by 40 µm distance. The influence of humidity on the capacitance of the hybrid humidity sensor (Al/TMBHPET:CoFe2O4/Al) has been investigated at three different frequencies of the AC applied voltage ( V rms 1 V): 100 Hz, 1 kHz, and 10 kHz. It has been observed that at 100 Hz, under a humidity of 99 % RH, the capacitance of the sensor increased by 2.61 times, with respect to 30 % RH condition. The proposed sensor exhibits significantly improved sensitivity 560 fF/ % RH at 100 Hz, which is nearly 7.5 times as high as that of pristine TMBHPET-based humidity sensor. Further, the capacitive sensor exhibits improved dynamic range (30-99 % RH), small hysteresis ( 2.3 %), and relatively quicker response and recovery times ( 12 s, 14 s, respectively). It is assumed that the humidity response of the sensor is associated with the diffusion kinetics of water vapors and doping of the semiconductor nanocomposite by water molecules.

Crystal field splitting and spin states of Co ions in cobalt ferrite with composition Co1.5Fe1.5O4 using magnetization and X-ray absorption spectroscopy measurements

NASA Astrophysics Data System (ADS)

Sinha, A. K.; Singh, M. N.; Achary, S. N.; Sagdeo, A.; Shukla, D. K.; Phase, D. M.

2017-08-01

Structural, magnetic and electronic properties of partially inverted Cobalt Ferrite with composition Co1.5Fe1.5O4 is discussed in the present work. Single phase (SG: Fd3m) sample is synthesized by co-precipitation technique and subsequent air annealing. The values of saturation magnetization obtained from careful analysis of approach to saturation in initial M(H) curves are used to determine spin states of Co ions in tetrahedral (TH) and octahedral (OH) sites. Spin states of Co3+ ions in TH sites, which has not been reported in literature, were found to be in high spin state. Temperature variation of magnetic parameters has been studied. The sample shows magneto-crystalline anisotropy with two clearly distinct pinning centers. Oxygen K-edge and Fe as well as Co L2,3-edge X-ray absorption (XAS) spectra have been used as complementary measurements to study crystal field splitting and core hole effects on transition metal (TM) 3d orbitals. The ratio of intensities of t2g and eg absorption bands in O-K edge XAS spectrum is used to estimate the spin states of Co ions at OH and TH sites. The results are in agreement with those obtained from magnetization data, and favors Co3+ ions in TH sites in high spin states. Normalized areas of the satellite peaks in TM L2,3-edge XAS spectra have been used to estimate 3dn+1L contribution in ground state wave function and the contributions were found to be significant.

Synthesis and structural characterization of magnetic cadmium sulfide-cobalt ferrite nanocomposite, and study of its activity for dyes degradation under ultrasound

NASA Astrophysics Data System (ADS)

Farhadi, Saeed; Siadatnasab, Firouzeh

2016-11-01

Cadmium sulfide-cobalt ferrite (CdS/CFO) nanocomposite was easily synthesized by one-step hydrothermal decomposition of cadmium diethyldithiocarbamate complex on the CoFe2O4 nanoparticles at 200 °C. Spectroscopic techniques of powder X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FT-IR), UV-visible spectroscopy, field emission scanning electron microscopy (FESEM), energy-dispersive X-ray spectroscopy (EDX), Brunauer-Emmett-Teller (BET), and magnetic measurements were applied for characterizing the structure and morphology of the product. The results of FT-IR, XRD and EDX indicated that the CdS/CFO was highly pure. SEM and TEM results revealed that the CdS/CFO nanocomposite was formed from nearly uniform and sphere-like nanoparticles with the size of approximately 20 nm. The UV-vis absorption spectrum of the CdS/CFO nanocomposite showed the band gap of 2.21 eV, which made it suitable for sono-/photo catalytic purposes. By using the obtained CdS/CFO nanocomposite, an ultrasound-assisted advanced oxidation process (AOP) has been developed for catalytic degradation of methylene blue (MB), Rhodamine B (RhB), and methyl orange (MO)) in the presence of H2O2 as a green oxidant. CdS/CFO nanocomposite exhibited excellent sonocatalytic activity, so that, dyes were completely degraded in less than 10 min. The influences of crucial factors such as the H2O2 amount and catalyst dosage on the degradation efficiency were evaluated. The as-prepared CdS/CFO nanocomposite exhibited higher catalytic activity than pure CdS nanoparticles. Moreover, the magnetic property of CoFe2O4 made the nanocomposite recyclable.

Electromagnetic interference shielding and microwave absorption properties of cobalt ferrite CoFe2O4/polyaniline composite

NASA Astrophysics Data System (ADS)

Ismail, Mukhils M.; Rafeeq, Sewench N.; Sulaiman, Jameel M. A.; Mandal, Avinandan

2018-05-01

Improvement of microwave-absorbing materials (MAMs) is the most important research area in various applications, such as in communication, radiation medical exposure, electronic warfare, air defense, and different civilian applications. Conducting polymer, polyaniline doped with para toluene sulphonic acid (PANI-PTSA) as well as cobalt ferrite (CoFe2O4) is synthesized by sol-gel method and intensely blends in different ratios. The characterization of the composite materials, CoFe2O4/PANI-PTSA (CFP1, CFP2, CFP3 and CFP4), was performed by X-ray diffraction (XRD), atomic force microscopy (AFM) and vibrating sample magnetometry (VSM). The microwave-absorbing properties' reflection loss (dB) and important parameters, such as complex relative permittivity ( ɛ r '- jɛ r ″) and complex relative permeability ( µ r '- jµ r ″) were measured in different microwave frequencies in the X-band (8.2-12.4 GHz) region. The composite material CFP3 showed a wider absorption frequency range and maximum reflection loss of - 28.4 dB (99.8% power absorption) at 8.1 GHz and - 9.6 dB (> 90% power absorption) at 11.2 GHz, and so the composite can be used as a microwave absorber; however, it can be more suitable for application in daily life for making cell phones above 9 GHz. Also the results showed that the thicker composites like CFP3 (4 mm) exhibit obviously better EMI SE as compared with the thinner ones (0.19, 0.19, 0.3 mm); this may be related to the low transmission of the EM wave from the composites.

Applications of magnetic hybrid adsorbent derived from waste biomass for the removal of metal ions and reduction of 4-nitrophenol.

PubMed

Cunha, Graziele da C; Dos Santos, Bruna Thaysa; Alves, Jôse Raymara; Alves Silva, Iris Amanda; de Souza Cruz, Daiane Requião; Romão, Luciane P C

2018-05-01

The use of industrial waste to synthesize materials of technological interest is a rational way to minimize or solve environmental pollution problems. This work investigates the adsorption of cadmium and lead ions by magnetic hybrid adsorbents synthesized using the in natura biomasses coconut mesocarp (CCFe), sawdust (SAFe), and termite nest (TEFe) for the organic phases and magnetic cobalt ferrite as the inorganic phase. The formation of a cobalt ferrite phase was confirmed by XRD. The use of XRD and FTIR analyses revealed the presence of organic matter in the structure of the material. Removal assays performed at different pH values (2.0-8.0) showed the effectiveness of the adsorbent for the removal of Pb 2+ at pH 3.0 and Cd 2+ at pH 4.0. The adsorption processes showed fast kinetics, with removal of 79-86% of Pb 2+ and 49% of Cd 2+ within only 5 min, and removal of 92-96% of the metal species at equilibrium. In the case of cadmium, the hybrid sorbents (CCFe, SAFe, and TEFe) showed high removal capacity after three reuse cycles, while the removal of lead decreased from 99% to 40%. The adsorbent matrices saturated with the recovered cadmium and lead ions showed excellent catalytic performance in the reduction of 4-nitrophenol, with 99.9% conversion within 43-56 s. The materials showed high capacities for reuse in three successive reduction cycles. The findings highlight the effectiveness of an industrial symbiosis approach to the development of new technologically important materials. Copyright © 2018 Elsevier Ltd. All rights reserved.

Effects of magnetic cobalt ferrite nanoparticles on biological and artificial lipid membranes

PubMed Central

Drašler, Barbara; Drobne, Damjana; Novak, Sara; Valant, Janez; Boljte, Sabina; Otrin, Lado; Rappolt, Michael; Sartori, Barbara; Iglič, Aleš; Kralj-Iglič, Veronika; Šuštar, Vid; Makovec, Darko; Gyergyek, Sašo; Hočevar, Matej; Godec, Matjaž; Zupanc, Jernej

2014-01-01

Background The purpose of this work is to provide experimental evidence on the interactions of suspended nanoparticles with artificial or biological membranes and to assess the possibility of suspended nanoparticles interacting with the lipid component of biological membranes. Methods 1-Palmitoyl-2-oleoyl-sn-glycero-3-phosphocholine (POPC) lipid vesicles and human red blood cells were incubated in suspensions of magnetic bare cobalt ferrite (CoFe2O4) or citric acid (CA)-adsorbed CoFe2O4 nanoparticles dispersed in phosphate-buffered saline and glucose solution. The stability of POPC giant unilamellar vesicles after incubation in the tested nanoparticle suspensions was assessed by phase-contrast light microscopy and analyzed with computer-aided imaging. Structural changes in the POPC multilamellar vesicles were assessed by small angle X-ray scattering, and the shape transformation of red blood cells after incubation in tested suspensions of nanoparticles was observed using scanning electron microscopy and sedimentation, agglutination, and hemolysis assays. Results Artificial lipid membranes were disturbed more by CA-adsorbed CoFe2O4 nanoparticle suspensions than by bare CoFe2O4 nanoparticle suspensions. CA-adsorbed CoFe2O4-CA nanoparticles caused more significant shape transformation in red blood cells than bare CoFe2O4 nanoparticles. Conclusion Consistent with their smaller sized agglomerates, CA-adsorbed CoFe2O4 nanoparticles demonstrate more pronounced effects on artificial and biological membranes. Larger agglomerates of nanoparticles were confirmed to be reactive against lipid membranes and thus not acceptable for use with red blood cells. This finding is significant with respect to the efficient and safe application of nanoparticles as medicinal agents. PMID:24741305

Effect of size and shape dependent anisotropy on superparamagnetic property of CoFe2O4 nanoparticles and nanoplatelets

NASA Astrophysics Data System (ADS)

Chandekar, Kamlesh V.; Kant, K. Mohan

2017-09-01

Superparamagnetic cobalt ferrite (CoFe2O4) spherical nanoparticles and rhomboidal nanoplatelets were synthesized by co-precipitation at 80 °C (S1) and hydrothermal route at 150 °C (S2). X-ray diffraction (XRD) pattern confirms formation of cubic inverse spinel structure of as prepared cobalt ferrite samples (S1 and S2) with average crystallite size of 13 nm and 18.7 nm for S1 and S2 respectively. Transmission electron microscopy (TEM) reveals spherical and rhomboidal shaped with average particle size 16.7 nm (S1) and 19.8 nm (S2). The zero field cooled magnetization MZFCvs. T exhibit a broad maxima at 400 K and 510 K for S1 and S2 respectively. The blocking temperature TB is obtained as 310 K and 341 K for S1 and S2 respectively, by fitting coercive field at different temperatures to T 1 / 2 law. The morphology of S1 and S2 corresponds to shape dependence of continuum approach. The effective demagnetization factors estimated as ΔN1 = 0 and ΔN2 = 0 . 749 for S1 and S2 samples respectively. The uniaxial anisotropy and shape anisotropy observed to be dominant in spherical shaped and rhomboidal shaped CoFe2O4 nanoparticles respectively. The uniaxial anisotropy constant of S1 sample is estimated as 56 (kJ/m3) at TB = 310 K whereas the effective anisotropy constant for S2 sample is 627 (kJ/m3) at TB = 341 K , in which shape anisotropy constant 605 (kJ/m3) dominates over contribution from uniaxial anisotropy constant 22 (kJ/m3) in S2 sample.

High temperature dielectric studies of indium-substituted NiCuZn nanoferrites

NASA Astrophysics Data System (ADS)

Hashim, Mohd.; Raghasudha, M.; Shah, Jyoti; Shirsath, Sagar E.; Ravinder, D.; Kumar, Shalendra; Meena, Sher Singh; Bhatt, Pramod; Alimuddin; Kumar, Ravi; Kotnala, R. K.

2018-01-01

In this study, indium (In3+)-substituted NiCuZn nanostructured ceramic ferrites with a chemical composition of Ni0.5Cu0.25Zn0.25Fe2-xInxO4 (0.0 ≤ x ≤ 0.5) were prepared by chemical synthesis involving sol-gel chemistry. Single phased cubic spinel structure materials were prepared successfully according to X-ray diffraction and transmission electron microscopy analyses. The dielectric properties of the prepared ferrites were measured using an LCR HiTester at temperatures ranging from room temperature to 300 °C at different frequencies from 102 Hz to 5 × 106 Hz. The variations in the dielectric parameters ε‧ and (tanδ) with temperature demonstrated the frequency- and temperature-dependent characteristics due to electron hopping between the ions. The materials had low dielectric loss values in the high frequency range at all temperatures, which makes them suitable for high frequency microwave applications. A qualitative explanation is provided for the dependences of the dielectric constant and dielectric loss tangent on the frequency, temperature, and composition. Mӧssbauer spectroscopy was employed at room temperature to characterize the magnetic behavior.

Optimized alumina coagulants for water treatment

DOEpatents

Nyman, May D [Albuquerque, NM; Stewart, Thomas A [Albuquerque, NM

2012-02-21

Substitution of a single Ga-atom or single Ge-atom (GaAl.sub.12 and GeAl.sub.12 respectively) into the center of an aluminum Keggin polycation (Al.sub.13) produces an optimal water-treatment product for neutralization and coagulation of anionic contaminants in water. GaAl.sub.12 consistently shows .about.1 order of magnitude increase in pathogen reduction, compared to Al.sub.13. At a concentration of 2 ppm, GaAl.sub.12 performs equivalently to 40 ppm alum, removing .about.90% of the dissolved organic material. The substituted GaAl.sub.12 product also offers extended shelf-life and consistent performance. We also synthesized a related polyaluminum chloride compound made of pre-hydrolyzed dissolved alumina clusters of [GaO.sub.4Al.sub.12(OH).sub.24(H.sub.2O).sub.12].sup.7+.

Effect of Ga3+ and Gd3+ ions substitution on the structural and optical properties of Ce3+ -doped yttrium aluminium garnet phosphor nanopowders.

PubMed

Wako, A H; Dejene, F B; Swart, H C

2016-11-01

The structural and optical properties of commercially obtained Y 3 Al 5 O 12 :Ce 3 + phosphor were investigated by replacing Al 3 + with Ga 3 + and Y 3 + with Gd 3 + in the Y 3 Al 5 O 12 :Ce 3 + structure to form Y 3 (Al,Ga) 5 O 12 :Ce 3 + and (Y,Gd) 3 Al 5 O 12 :Ce 3 + . X-Ray diffraction (XRD) results showed slight 2-theta peak shifts to lower angles when Ga 3 + was used and to higher angles when Gd 3 + was used, with respect to peaks from Y 3 Al 5 O 12 :Ce 3 + and JCPDS card no. 73-1370. This could be attributed to induced crystal-field effects due to the different ionic sizes of Ga 3 + and Gd 3 + compared with Al 3 + and Y 3 + . The photoluminescence (PL) spectra showed broad excitation from 350 to 550 nm with a maximum at 472 nm, and broad emission bands from 500 to 650 nm, centred at 578 nm for Y 3 Al 5 O 12 :Ce 3 + arising from the 5d → 4f transition of Ce 3 + . PL revealed a blue shift for Ga 3 + substitution and a red shift for Gd 3 + substitution. UV-Vis showed two absorption peaks at 357 and 457 nm for Y 3 Al 5 O 12 :Ce 3 + , with peaks shifting to 432 nm for Ga 3 + and 460 nm for Gd 3 + substitutions. Changes in the trap levels or in the depth and number of traps due to Ce 3 + were analysed using thermoluminescence (TL) spectroscopy. This revealed the existence of shallow and deep traps. It was observed that Ga 3 + substitution contributes to the shallowest traps at 74 °C and fewer deep traps at 163 °C, followed by Gd 3 + with shallow traps at 87 °C and deep traps at 146 °C. Copyright © 2016 John Wiley & Sons, Ltd. Copyright © 2016 John Wiley & Sons, Ltd.

Regulation of the forming process and the set voltage distribution of unipolar resistance switching in spin-coated CoFe2O4 thin films.

PubMed

Mustaqima, Millaty; Yoo, Pilsun; Huang, Wei; Lee, Bo Wha; Liu, Chunli

2015-01-01

We report the preparation of (111) preferentially oriented CoFe2O4 thin films on Pt(111)/TiO2/SiO2/Si substrates using a spin-coating process. The post-annealing conditions and film thickness were varied for cobalt ferrite (CFO) thin films, and Pt/CFO/Pt structures were prepared to investigate the resistance switching behaviors. Our results showed that resistance switching without a forming process is preferred to obtain less fluctuation in the set voltage, which can be regulated directly from the preparation conditions of the CFO thin films. Therefore, instead of thicker film, CFO thin films deposited by two times spin-coating with a thickness about 100 nm gave stable resistance switching with the most stable set voltage. Since the forming process and the large variation in set voltage have been considered as serious obstacles for the practical application of resistance switching for non-volatile memory devices, our results could provide meaningful insights in improving the performance of ferrite material-based resistance switching memory devices.

Investigation of structural, morphological and electromagnetic properties of Mg0.25Mn0.25Zn0.5-xSrxFe2O4 ferrites

NASA Astrophysics Data System (ADS)

Rahaman, Md. D.; Nusrat, Tania; Maleque, Rumana; Hossain, A. K. M. Akther

2018-04-01

Polycrystalline Mg0.25Mn0.25Zn0.5-xSrxFe2O4 (0 ≤ x ≤ 0.20) ferrites were synthesized using the solid state reaction sintering at 1373 K and 1473 K for 4 h. The XRD patterns revealed the formation of single phase cubic spinel with Sr2FeO4 and SrFe12O19 as impurity phases. The decrement in the lattice parameter for Sr2+ substituted samples is attributed to the difference in ionic radii of cations. The crystallite size decreases with increase in Sr2+ content. Low frequency dielectric dispersion is attributed due to the Maxwell-Wagner interfacial polarization. The appearance of the peak in dielectric loss spectrum for x = 0.15 and 0.20 at 1373 K and x = 0.20 at 1473 K suggests the presence of relaxing dipoles. The loss peak shifts towards lower frequency side with Sr2+ content at 1373 K which is due to the strengthening of dipole-dipole interactions. The complex impedance spectra clearly revealed that the both grain and grain boundary effects on the electrical properties. A complex electric modulus spectrum indicates that a non-Debye type of conductivity relaxation exists. The saturation magnetization and remanence gradually decreases with Sr2+ substitution which may be due to the existence of non-magnetic phase in the space between the magnetic particles and the substitution of Zn2+ cation in Mg0.25Mn0.25Zn0.5Fe2O4 ferrite lattice by Sr2+ content. The permeability decreases significantly while the cut-off frequency increases with the Sr2+ content at 1373 K and decreases at 1473 K, obeying the Snoek's law. The decrease in permeability with Sr2+ content is attributed due to the decrease in magnetization because non-magnetic ions weaken the inter-site exchange interaction.

Gallium hole traps in irradiated KTiOPO{sub 4}:Ga crystals

DOE Office of Scientific and Technical Information (OSTI.GOV)

Grachev, V.; Meyer, M.; Malovichko, G.

2014-12-07

Nominally pure and gallium doped single crystals of potassium titanyl phosphate (KTiOPO{sub 4}) have been studied by Electron Paramagnetic Resonance at low temperatures before and after irradiation. Irradiation with 20 MeV electrons performed at room temperature and liquid nitrogen temperature caused an appearance of electrons and holes. Gallium impurities act as hole traps in KTiOPO{sub 4} creating Ga{sup 4+} centers. Two different Ga{sup 4+} centers were observed, Ga1 and Ga2. The Ga1 centers are dominant in Ga-doped samples. For the Ga1 center, a superhyperfine structure with one nucleus with nuclear spin ½ was registered and attributed to the interaction of galliummore » electrons with a phosphorus nucleus or proton in its surrounding. In both Ga1 and Ga2 centers, Ga{sup 4+} ions substitute for Ti{sup 4+} ions, but with a preference to one of two electrically distinct crystallographic positions (site selective substitution). The Ga doping eliminates one of the shortcomings of KTP crystals—ionic conductivity of bulk crystals. However, this does not improve significantly the resistance of the crystals to electron and γ-radiation.« less

The acceleration of dissolved cobalt's ecological stoichiometry due to biological uptake, remineralization, and scavenging in the Atlantic Ocean

NASA Astrophysics Data System (ADS)

Saito, Mak A.; Noble, Abigail E.; Hawco, Nicholas; Twining, Benjamin S.; Ohnemus, Daniel C.; John, Seth G.; Lam, Phoebe; Conway, Tim M.; Johnson, Rod; Moran, Dawn; McIlvin, Matthew

2017-10-01

The stoichiometry of biological components and their influence on dissolved distributions have long been of interest in the study of the oceans. Cobalt has the smallest oceanic inventory of inorganic micronutrients and hence is particularly vulnerable to influence by internal oceanic processes including euphotic zone uptake, remineralization, and scavenging. Here we observe not only large variations in dCo : P stoichiometry but also the acceleration of those dCo : P ratios in the upper water column in response to several environmental processes. The ecological stoichiometry of total dissolved cobalt (dCo) was examined using data from a US North Atlantic GEOTRACES transect and from a zonal South Atlantic GEOTRACES-compliant transect (GA03/3e and GAc01) by Redfieldian analysis of its statistical relationships with the macronutrient phosphate. Trends in the dissolved cobalt to phosphate (dCo : P) stoichiometric relationships were evident in the basin-scale vertical structure of cobalt, with positive dCo : P slopes in the euphotic zone and negative slopes found in the ocean interior and in coastal environments. The euphotic positive slopes were often found to accelerate towards the surface and this was interpreted as being due to the combined influence of depleted phosphate, phosphorus-sparing (conserving) mechanisms, increased alkaline phosphatase metalloenzyme production (a zinc or perhaps cobalt enzyme), and biochemical substitution of Co for depleted Zn. Consistent with this, dissolved Zn (dZn) was found to be drawn down to only 2-fold more than dCo, despite being more than 18-fold more abundant in the ocean interior. Particulate cobalt concentrations increased in abundance from the base of the euphotic zone to become ˜ 10 % of the overall cobalt inventory in the upper euphotic zone with high stoichiometric values of ˜ 400 µmol Co mol-1 P. Metaproteomic results from the Bermuda Atlantic Time-series Study (BATS) station found cyanobacterial isoforms of the alkaline phosphatase enzyme to be prevalent in the upper water column, as well as a sulfolipid biosynthesis protein indicative of P sparing. The negative dCo : P relationships in the ocean interior became increasingly vertical with depth, and were consistent with the sum of scavenging and remineralization processes (as shown by their dCo : P vector sums). Attenuation of the remineralization with depth resulted in the increasingly vertical dCo : P relationships. Analysis of particulate Co with particulate Mn and particulate phosphate also showed positive linear relationships below the euphotic zone, consistent with the presence and increased relative influence of Mn oxide particles involved in scavenging. Visualization of dCo : P slopes across an ocean section revealed hotspots of scavenging and remineralization, such as at the hydrothermal vents and below the oxygen minimum zone (OMZ) region, respectively, while that of an estimate of Co* illustrated stoichiometrically depleted values in the mesopelagic and deep ocean due to scavenging. This study provides insights into the coupling between the dissolved and particulate phase that ultimately creates Redfield stoichiometric ratios, demonstrating that the coupling is not an instantaneous process and is influenced by the element inventory and rate of exchange between phases. Cobalt's small water column inventory and the influence of external factors on its biotic stoichiometry can erode its limited inertia and result in an acceleration of the dissolved stoichiometry towards that of the particulate phase in the upper euphotic zone. As human use of cobalt grows exponentially with widespread adoption of lithium ion batteries, there is a potential to affect the limited biogeochemical inertia of cobalt and its resultant ecology in the oceanic euphotic zone.

Nitrated metalloporphyrins as catalysts for alkane oxidation

DOEpatents

Ellis, P.E. Jr.; Lyons, J.E.

1994-01-18

Compositions of matter comprising nitro-substituted metal complexes of porphyrins are catalysts for the oxidation of alkanes. The metal is iron, chromium, manganese, ruthenium, copper or cobalt. The porphyrin ring has nitro groups attached thereto in meso and/or [beta]-pyrrolic positions.

Nitrated metalloporphyrins as catalysts for alkane oxidation

DOEpatents

Ellis, Jr., Paul E.; Lyons, James E.

1994-01-01

Compositions of matter comprising nitro-substituted metal complexes of porphyrins are catalysts for the oxidation of alkanes. The metal is iron, chromium, manganese, ruthenium, copper or cobalt. The porphyrin ring has nitro groups attached thereto in meso and/or .beta.-pyrrolic positions.

Superposition model analysis of zero field splitting for Mn2+ in some host single crystals

NASA Astrophysics Data System (ADS)

Bansal, R. S.; Ahlawat, P.; Bharti, M.; Hooda, S. S.

2013-07-01

The Newman superposition model has been used to investigate the substitution of Mn2+ for Zn2+ site in ammonium tetra flurozincate dihydrate and for Co2+ site in cobalt ammonium phosphate hexahydrate and cobalt potassium phosphate hexahydrate single crystals. The calculated values of zero field splitting parameter b 2 0 at room temperature fit the experimental data with average intrinsic parameters overline{b}2 (F) = -0.0531 cm-1 for fluorine and overline{b}2 (O) = -0.0280 cm-1 for oxygen, taken t 2 = 7 for Mn2+ doped in ammonium tetra fluorozincate dihydrate single crystals. The values of overline{b}2 determined for Mn2+ doped in cobalt ammonium phosphate hexahydrate are -0.049 cm-1 for site I and -0.045 cm-1 for site II and in cobalt pottasium phosphate hexahydrate single crystals it is found to be overline{b}2 = -0.086 cm-1. We find close agreement between theoretical and experimental values of b 2 0.

Characterization of Magnetic Nanostructures Using Off-Axis Electron Holography

NASA Astrophysics Data System (ADS)

Zhang, Desai

This dissertation research has involved microscopic characterization of magnetic nanostructures using off-axis electron holography and Lorentz microscopy. The nanostructures investigated have included Co nanoparticles (NPs), Au/Fe/GaAs shell/core nanowires (NWs), carbon spirals with magnetic cores, magnetic nanopillars, Ni-Zn-Co spinel ferrite and CoFe/Pd multilayers. The studies have confirmed the capability of holography to describe the behavior of magnetic structures at the nanoscale. The phase changes caused by the fringing fields of chains consisting of Co NPs were measured and calculated. The difference between chains with different numbers of Co NPs followed the trend indicated by calculations. Holography studies of Au/Fe/GaAs NWs grown on (110) GaAs substrates with rotationally non-uniform coating confirmed that Fe was present in the shell and that the shell behaved as a bar magnet. No fringing field was observed from NWs with cylindrical coating grown on (111)B GaAs substrates. The most likely explanation is that magnetic fields are confined within the shells and form closed loops. The multiple-magnetic-domain structure of iron carbide cores in carbon spirals was imaged using phase maps of the fringing fields. The strength and range of this fringing field was insufficient for manipulating the carbon spirals with an external applied magnetic field. No magnetism was revealed for CoPd/Fe/CoPd magnetic nanopillars. Degaussing and MFM scans ruled out the possibility that saturated magnetization and sample preparation had degraded the anisotropy, and the magnetism, respectively. The results suggested that these nanopillars were not suitable as candidates for prototypical bit information storage devices. Observations of Ni-Zn-Co spinel ferrite thin films in plan-view geometry indicated a multigrain magnetic domain structure and the magnetic fields were oriented in-plane only with no preferred magnetization distribution. This domain structure helps explain this ferrite's high permeability at high resonance frequency, which is an unusual character. Perpendicular magnetic anisotropy (PMA) of CoFe/Pd multilayers was revealed using holography. Detailed microscopic characterization showed structural factors such as layer waviness and interdiffusion that could contribute to degradation of the PMA. However, these factors are overwhelmed by the dominant effect of the CoFe layer thickness, and can be ignored when considering magnetic domain structure.

Crystalline and magnetooptical characteristics of (Tb,Bi)3(Fe,Ga)5O12 deposited on (Y,Nd)3Al5O12

NASA Astrophysics Data System (ADS)

Morimoto, Ryohei; Goto, Taichi; Nakamura, Yuichi; Boey Lim, Pang; Uchida, Hironaga; Inoue, Mitsuteru

2018-06-01

We prepared Bi- and Ga-substituted Tb3Fe5O12 (BiGa:TIG) films on a Nd-substituted Y3Al5O12 (Nd:YAG) single crystal substrate by pulsed laser deposition, and investigated their magnetic, optical, and magnetooptical properties. A BiGa:TIG film deposited with a substrate temperature of 700 °C shows the easy axis of magnetization along the out-of-plane direction of the film and the Faraday rotation angle of 900°/cm at a wavelength of 1064 nm. The epitaxial growth of the film is confirmed by X-ray diffraction analysis.

Photoemission Studies of Kondo Lattice Compounds YbNi3(Ga1-xAlx)9

NASA Astrophysics Data System (ADS)

Utsumi, Yuki; Sato, Hitoshi; Nagata, Heisuke; Kodama, Junichi; Ohara, Shigeo; Yamashita, Tetsuro; Mimura, Kojiro; Motonami, Satoru; Arita, Masashi; Ueda, Shigenori; Shimada, Kenya; Namatame, Hirofumi; Taniguchi, Masaki

We have investigated the electronic structure of YbNi3 (Ga1-xAlx)9 (x = 0, 0.05, 0.10, 0.15) by means of hard x-ray (hν ˜ 6 keV) and low energy (hν ˜ 7 eV) photoemission spectroscopies (HAXPES and LEPES). Both Yb2+ and Yb3+ components are observed in the Yb 3d HAXPES spectra, which is an evidence of the valence fluctuation in YbNi3(Ga1-xAlx)9. A substitution of an Al ion for a Ga ion in YbNi3Ga9 changes the Yb ion into a trivalent state. The LEPES spectra of YbNi3Ga9 clearly exhibit the Kondo peak near the Fermi level (EF) and the Kondo temperature is estimated to be TK ˜ 550 K. With the Al substitution, the Kondo peak is shifted toward EF, indicating the decrease of TK

The effect of electron and hole doping on the thermoelectric properties of shandite-type Co3Sn2S2

NASA Astrophysics Data System (ADS)

Mangelis, Panagiotis; Vaqueiro, Paz; Jumas, Jean-Claude; da Silva, Ivan; Smith, Ronald I.; Powell, Anthony V.

2017-07-01

Electron and hole doping in Co3Sn2S2, through chemical substitution of cobalt by the neighbouring elements, nickel and iron, affects both the structure and thermoelectric properties. Electron doping to form Co3-xNixSn2S2 (0≤x≤3) results in an expansion of the kagome layer and materials become increasingly metallic as cobalt is substituted. Conversely, hole doping in Co3-xFexSn2S2 (0≤x≤0.6) leads to a transition from metallic to n-type semiconducting behaviour at x=0.5. Iron substitution induces a small increase in the separation between the kagome layers and improves the thermoelectric performance. Neutron diffraction data reveal that substitution occurs at the Co 9(d) site in a disordered fashion. Mössbauer spectroscopy reveals two iron environments with very different isomer shifts, which may be indicative of a mixed-valence state, while Sn exhibits an oxidation state close to zero in both series. Co2.6Fe0.4Sn2S2 exhibits a maximum figure-of-merit, ZT=0.2 at 523 K while Co2.4Fe0.6Sn2S2 reaches a power factor of 10.3 μW cm-1 K-2 close to room temperature.

The enhanced spin-polarized transport behaviors through cobalt benzene-porphyrin-benzene molecular junctions: the effect of functional groups

NASA Astrophysics Data System (ADS)

Cheng, Jue-Fei; Zhou, Liping; Wen, Zhongqian; Yan, Qiang; Han, Qin; Gao, Lei

2017-05-01

The modification effects of the groups amino (NH2) and nitro (NO2) on the spin polarized transport properties of the cobalt benzene-porphyrin-benzene (Co-BPB) molecule coupled to gold (Au) nanowire electrodes are investigated by the nonequilibrium Green’s function method combined with the density functional theory. The calculation results show that functional groups can lead to the significant spin-filter effect, enhanced low-bias negative differential resistance (NDR) behavior and novel reverse rectifying effect in Co-BPB molecular junction. The locations and types of functional groups have distinct influences on spin-polarized transport performances. The configuration with NH2 group substituting H atom in central porphyrin ring has larger spin-down current compared to that with NO2 substitution. And Co-BPB molecule junction with NH2 group substituting H atom in side benzene ring shows reverse rectifying effect. Detailed analyses confirm that NH2 and NO2 group substitution change the spin-polarized transferred charge, which makes the highest occupied molecular orbitals (HOMO) of spin-down channel of Co-BPB closer to the Fermi level. And the shift of HOMO strengthens the spin-polarized coupling between the molecular orbitals and the electrodes, leading to the enhanced spin-polarized behavior. Our findings might be useful in the design of multi-functional molecular devices in the future.

First-principles study on alkali-metal effect of Li, Na, and K in CuInSe2 and CuGaSe2

NASA Astrophysics Data System (ADS)

Maeda, Tsuyoshi; Kawabata, Atsuhito; Wada, Takahiro

2015-08-01

The substitution energies and migration energies of the alkali metal atoms of Li, Na, and K in CuInSe2 (CIS) and CuGaSe2 (CGS) were investigated by first-principles calculations. The substitution energies of Li, Na, and K atoms in CIS and CGS were calculated for two different cationic atom positions of Cu and In/Ga in the chalcopyrite unit cell. In CIS and CGS, the substitution energies of NaCu are much lower than those of NaIn and NaGa. The substitution energies of the LiCu atoms in CIS and CGS are lower than those of NaCu, while the substitution energies of KCu atoms in CIS and CGS are much higher than those of NaCu. Therefore, it is difficult to form KCu in CIS and CGS. The migration energies of Li, Na, and K atoms in CIS and CGS are obtained by a combination of the linear and quadratic synchronous transit (LST/QST) methods and the nudged elastic band (NEB) method. The theoretical migration energies of a Na atom at the Cu site to the nearest Cu vacancy (NaCu → VCu) in CIS and CGS are much lower than those of (CuCu → VCu) in CIS and CGS. The mechanism underlying the alkali metal effect of Li, Na, and K in the CIGS film during the post-deposition treatment of LiF, NaF, and KF is discussed on the basis of the calculated substitution and migration energies.

Mixed nickel-gallium tellurides Ni{sub 3−x}GaTe{sub 2} as a matrix for incorporating magnetic cations: A Ni{sub 3−x}Fe{sub x}GaTe{sub 2} series

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kuznetsov, Alexey N., E-mail: alexei@inorg.chem.msu.ru; N.S. Kurnakov Institute of General and Inorganic Chemistry, RAS, Leninsky pr. 31, GSP-1, 119991 Moscow; Stroganova, Ekaterina A.

Using a high-temperature ampoule technique, a series of mixed nickel-iron-gallium metal-rich tellurides with layered structures, Ni{sub 3-x}Fe{sub x}GaTe{sub 2}, were prepared and characterized based on X-ray powder diffraction, energy-dispersive spectroscopy, and {sup 57}Fe Mössbauer spectroscopy data. These compounds may be regarded as a result of partial substitution of nickel by iron in the recently reported ternary Ni{sub 3-x}GaTe{sub 2} series, which are based on NiAs/Ni{sub 2}In type of structure. The compositional boundary for the substitution was found to be at x~1. According to the Mössbauer spectroscopy data, the substitution is not statistical, and iron atoms with the increase in xmore » tend to preferentially occupy those nickel positions that are partially vacant in the initial ternary compound. Magnetic measurements data for the Ni{sub 3-x}Fe{sub x}GaTe{sub 2} series show dramatic change in behavior from temperature-independent paramagnetic properties of the initial matrix to a low-temperature (~75 K) ferromagnetic ordering in the Ni{sub 2}FeGaTe{sub 2}. - Graphical abstract: Ordered substitution of nickel by iron in the Ni{sub 3−x}GaTe{sub 2} series leading to ferromagnetic ordering. - Highlights: • A series of Ni{sub 3−x}Fe{sub x}GaTe{sub 2} compounds were synthesized. • They adopt the NiAs/Ni{sub 2}In type of structure with ordered iron distribution. • The distribution of iron was studied using {sup 57}Fe Mössbauer spectroscopy. • An increase in iron content leads to the strong ferromagnetic coupling.« less

Investigation of structural, optical, magnetic and electrical properties of tungsten doped Nisbnd Zn nano-ferrites

NASA Astrophysics Data System (ADS)

Pathania, Abhilash; Bhardwaj, Sanjay; Thakur, Shyam Singh; Mattei, Jean-Luc; Queffelec, Patrick; Panina, Larissa V.; Thakur, Preeti; Thakur, Atul

2018-02-01

Tungsten substituted nickel-zinc ferrite nanoparticles with chemical composition of Ni0.5Zn0.5WxFe2-xO4 (x = 0.0, 0.2, 0.4, 0.6, 0.8 & 1.0) were successfully synthesized by a chemical co-precipitation method. The prepared ferrites were pre sintered at 850 °C and then annealed at 1000 °C in a muffle furnace for 3 h each. This sintered powder was inspected by X-ray diffraction (XRD), transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FTIR), and vibrating sample magnetometer (VSM) to study the structural, optical, and magnetic properties. XRD measurement revealed the phase purity of all the nanoferrite samples with cubic spinel structure. The estimated crystallite size by X-ray line broadening is found in the range of 49-62 nm. FTIR spectra of all the samples have observed two prominent absorption bands in the range 400-700 cm-1 arising due to tetrahedral and octahedral stretching vibrations. Vibrating sample magnetometer experiments showed that the saturation magnetizations (MS) decreased with an increase in non-magnetic tungsten ion doping. The electrical resistivity of tungsten doped Nisbnd Zn nano ferrites were examined extensively as a function of temperature. With an increase in tungsten composition, resistivity was found to decrease from 2.2 × 105 Ω cm to 1.9 × 105 Ω cm which indicates the semiconducting behavior of the ferrite samples. The activation energy also decreased from 0.0264 to 0.0221 eV at x = 0.0 to x = 1.0. These low coercive field tungsten doped Nisbnd Zn ferrites are suitable for hyperthermia and sensor applications. These observations are explained in detail on the basis of various models and theories.

Synthesis and characterization of BaGa2O4 and Ba3Co2O6(CO3)0.6 compounds in the search of alternative materials for Proton Ceramic Fuel Cell (PCFC)

NASA Astrophysics Data System (ADS)

Acuña, Wilder; Tellez, Jhoan F.; Macías, Mario A.; Roussel, Pascal; Ricote, Sandrine; Gauthier, Gilles H.

2017-09-01

BaGa2O4 and Ba3Co2O6(CO3)0.6 compounds were studied as electrolyte and cathode materials for Proton Ceramic Fuel Cells (PCFC), respectively. Not only BaGa2O4 rapidly reacts with atmospheric H2O and CO2 and leads to a progressive material decomposition, but it does not present real hydration properties in normal conditions of pressure. On the other hand, the basic cobalt oxocarbonate Ba3Co2O6(CO3)0.6 exhibits an interesting tendency for weight uptake and formation of hydrogencarbonate groups in moist heating/cooling conditions. This material was therefore considered for complementary studies in order to confirm its potential use as mixed proton-electron conductor, taking into account the ordered intergrowth of carbonates and face sharing Co-octahedra columns forming a pseudo-one-dimensional structure. Some preliminary results concerning electrochemical properties of the barium cobalt oxocarbonate as a PCFC cathode are also described and show at the moment modest performance, possibly related to a hydrated/carbonated surface layer contribution and/or the lack of electron percolation within the electrode layer.

Bioinspired synthesis of magnetic nanoparticles

DOE Office of Scientific and Technical Information (OSTI.GOV)

David, Anand

2009-01-01

The synthesis of magnetic nanoparticles has long been an area of active research. Magnetic nanoparticles can be used in a wide variety of applications such as magnetic inks, magnetic memory devices, drug delivery, magnetic resonance imaging (MRI) contrast agents, and pathogen detection in foods. In applications such as MRI, particle uniformity is particularly crucial, as is the magnetic response of the particles. Uniform magnetic particles with good magnetic properties are therefore required. One particularly effective technique for synthesizing nanoparticles involves biomineralization, which is a naturally occurring process that can produce highly complex nanostructures. Also, the technique involves mild conditions (ambientmore » temperature and close to neutral pH) that make this approach suitable for a wide variety of materials. The term 'bioinspired' is important because biomineralization research is inspired by the naturally occurring process, which occurs in certain microorganisms called 'magnetotactic bacteria'. Magnetotactic bacteria use biomineralization proteins to produce magnetite crystals having very good uniformity in size and morphology. The bacteria use these magnetic particles to navigate according to external magnetic fields. Because these bacteria synthesize high quality crystals, research has focused on imitating aspects of this biomineralization in vitro. In particular, a biomineralization iron-binding protein found in a certain species of magnetotactic bacteria, magnetospirillum magneticum, AMB-1, has been extracted and used for in vitro magnetite synthesis; Pluronic F127 gel was used to increase the viscosity of the reaction medium to better mimic the conditions in the bacteria. It was shown that the biomineralization protein mms6 was able to facilitate uniform magnetite synthesis. In addition, a similar biomineralization process using mms6 and a shorter version of this protein, C25, has been used to synthesize cobalt ferrite particles. The overall goal of this project is to understand the mechanism of magnetite particle synthesis in the presence of the biomineralization proteins, mms6 and C25. Previous work has hypothesized that the mms6 protein helps to template magnetite and cobalt ferrite particle synthesis and that the C25 protein templates cobalt ferrite formation. However, the effect of parameters such as the protein concentration on the particle formation is still unknown. It is expected that the protein concentration significantly affects the nucleation and growth of magnetite. Since the protein provides iron-binding sites, it is expected that magnetite crystals would nucleate at those sites. In addition, in the previous work, the reaction medium after completion of the reaction was in the solution phase, and magnetic particles had a tendency to fall to the bottom of the medium and aggregate. The research presented in this thesis involves solid Pluronic gel phase reactions, which can be studied readily using small-angle x-ray scattering, which is not possible for the solution phase experiments. In addition, the concentration effect of both of the proteins on magnetite crystal formation was studied.« less

Magnetic properties of Co-ferrite-doped hydroxyapatite nanoparticles having a core/shell structure

NASA Astrophysics Data System (ADS)

Petchsang, N.; Pon-On, W.; Hodak, J. H.; Tang, I. M.

2009-07-01

The magnetic properties of Co-ferrite-doped hydroxyapatite (HAP) nanoparticles of composition Ca 10-3xFe 2xCo x(PO 4) 6(OH) 2 (where x=0, 0.1, 0.2, 0.3, 0.4 and 0.5% mole) are studied. Transmission electron microscope micrograms show that the 90 nm size nanoparticles annealed at 1250 °C have a core/shell structure. Their electron diffraction patterns show that the shell is composed of the hydroxyapatite and the core is composed of the Co-ferrite, CoFe 2O 4. Electron spin resonance measurements indicate that the Co 2+ ions are being substituted into the Ca(1) sites in HAP lattice. X-ray diffraction studies show the formation of impurity phases as higher amounts of the Fe 3+/Co 2+ ions which are substituted into the HAP host matrix. The presence of two sextets (one for the A-site Fe 3+ and the other for the B-site Fe 3+) in the Mössbauer spectrum for all the doped samples clearly indicates that the CoFe 2O 4.cores are in the ferromagnetic state. Evidence of the impurity phases is seen in the appearance of doublet patterns in the Mössbauer spectrums for the heavier-doped ( x=0.4 and 0.5) specimens. The decrease in the saturation magnetizations and other magnetic properties of the nanoparticles at the higher doping levels is consistent with some of the Fe 3+ and Co 2+ which being used to form the CoO and Fe 2O 3 impurity phase seen in the XRD patterns.

Structural studies of the crystallisation of microporous materials

NASA Astrophysics Data System (ADS)

Davies, Andrew Treharne

A range of powerful synchrotron radiation characterisation techniques have been used to study fundamental aspects of the fonnation of microporous solids, specifically alumi nosilicates, heteroatom substituted aluminophosphates and titanosilicates. This work has been performed with the aim of investigating in situ the structural changes occurring during crystallisation and post synthetic treatment. In situ EDXRD was used to follow the crystallisation of these materials under a wide range of synthesis conditions using a hydrothermal cell and a solid-state detector array. A quantitative analysis of the crystallisation kinetics was performed for the large pore aluminosilicate, zeolite A, using a simple mathematical model to calculate the activation energy of formation. The results obtained were found to closely agree with both the experimental results and theoretical models of others. A qualitative study of the effect of altering the synthesis conditions was also investigated for this material. Similar kinetic studies were then performed for a range of microporous aluminophosphates and their cobalt substituted derivatives in order to follow the effects of varying synthesis conditions such as the synthesis temperature, organic template type, and cobalt concentration. Distinct trends were noted in the formation times, stability and nature of the resulting crystalline phases as conditions were varied. The relationship between the cobalt and organic template molecules during crystallisation was considered in some detail with reference to other experimental data and theoretical models. The alumi nophosphate studies were subsequently extended to a range of other heteroatom substituted aluminophosphates, using in situ EDXRD, complimented by EXAFS, which allowed investigation of the local environments around the heteroatoms within the microporous structure. EDXRD and EXAFS studies have been performed on the microporous titanosilicate, ETS-10, while the thermal stability of this material has also been investigated in situ using synchrotron X-ray diffraction in conjunction with a high temperature environmental cell.

Efficient removal of amoxicillin and paracetamol from aqueous solutions using magnetic activated carbon.

PubMed

Saucier, Caroline; Karthickeyan, P; Ranjithkumar, V; Lima, Eder C; Dos Reis, Glaydson S; de Brum, Irineu A S

2017-02-01

Activated carbon (AC)/CoFe 2 O 4 nanocomposites, MAC-1 and MAC-2, were prepared by a simple pyrolytic method using a mixture of iron(III)/cobalt(II) benzoates and iron(III)/cobalt(II) oxalates, respectively, and were used as efficient adsorbents for the removal of amoxicillin (AMX) and paracetamol (PCT) of aqueous effluents. The synthesized nanocomposites were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), vibrating sample magnetometry (VSM), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX) and transmission electron microscopy (TEM). The sizes of cobalt ferrite nanoparticles formed from benzoates of iron(III)/cobalt(II) and oxalates of iron(III)/cobalt(II) precursors were in the ranges of 5-80 and 6-27 nm, respectively. The saturation magnetization (M s ), remanence (M r ) and coercivity (H c ) of the MAC-2 nanocomposites were found to be 3.07 emu g -1 , 1.36 emu g -1 and 762.49 Oe; for MAC-1, they were 0.2989 emu g -1 , 0.0466 emu g -1 and 456.82 Oe. The adsorption kinetics and isotherm studies were investigated, and the results showed that the as-prepared nanocomposites MAC-1 and MAC-2 could be utilized as an efficient, magnetically separable adsorbent for environmental cleanup. The maximum sorption capacities obtained were 280.9 and 444.2 mg g -1 of AMX for MAC-1 and MAC-2, respectively, and 215.1 and 399.9 mg g -1 of PCT using MAC-1 and MAC-2, respectively. Both adsorbents were successfully used for simulated hospital effluents, removing at least 93.00 and 96.77% for MAC-1 and MAC-2, respectively, of a mixture of nine pharmaceuticals with high concentrations of sugars, organic components and saline concentrations.

Axial zero-field splitting in mononuclear Co(ii) 2-N substituted N-confused porphyrin: Co(2-NC3H5-21-Y-CH2C6H4CH3-NCTPP)Cl (Y = o, m, p) and Co(2-NC3H5-21-CH2C6H5-NCTPP)Cl.

PubMed

Lai, Ya-Yuan; Chang, Yu-Chang; Chen, Jyh-Horung; Wang, Shin-Shin; Tung, Jo-Yu

2016-03-21

The inner C-benzyl- and C-o-xylyl (or m-xylyl, p-xylyl)-substituted cobalt(ii) complexes of a 2-N-substituted N-confused porphyrin were synthesized from the reaction of 2-NC3H5NCTPPH (1) and CoCl2·6H2O in toluene (or o-xylene, m-xylene, p-xylene). The crystal structures of diamagnetic chloro(2-aza-2-allyl-5,10,15,20-tetraphenyl-21-hydrogen-21-carbaporphyrinato-N,N',N'')zinc(ii) [Zn(2-NC3H5-21-H-NCTPP)Cl; 3 ] and paramagnetic chloro(2-aza-2-allyl-5,10,15,20-tetraphenyl-21-benzyl-21-carbaporphyrinato-N,N',N'')cobalt(ii) [Co(2-NC3H5-21-CH2C6H5NCTPP)Cl; 7], and chloro(2-aza-2-allyl-5,10,15,20-tetraphenyl-21-Y-xylyl-21-carbaporphyrinato-N,N',N'')cobalt(ii) [Co(2-NC3H5-21-Y-CH2C6H4CH3NCTPP)Cl] [Y = o (8), m (9), p (10)] were determined. The coordination sphere around the Zn(2+) (or Co(2+)) ion in 3 (or 7-10) is a distorted tetrahedron (DT). The free energy of activation at the coalescence temperature Tc for the exchange of phenyl ortho protons o-H (26) with o-H (22) in 3 in a CDCl3 solvent is found to be ΔG = 61.4 kJ mol(-1) through (1)H NMR temperature-dependent measurements. The axial zero-field splitting parameter |D| was found to vary from 35.6 cm(-1) in 7 (or 30.7 cm(-1) in 8) to 42.0 cm(-1) in 9 and 46.9 cm(-1) in 10 through paramagnetic susceptibility measurements. The magnitude of |D| can be related to the coordination sphere at the cobalt sites.

Hypoxia-mimicking bioactive glass regenerative effects on dental stem cells

NASA Astrophysics Data System (ADS)

Noor, Siti Noor Fazliah Mohd; Azevedo, Maria; Mohamad, Hasmaliza; Autefage, Hélène

2016-12-01

Vascularization is an important aspect of tissue regeneration. Hypoxia, low oxygen concentration, is a known stimulus for the release of vascular endothelial growth factors (VEGF) which play important roles in vascularization. The current study aimed to assess the effect of a cobalt-containing bioactive glass (BG) in stimulating hypoxia and promoting vascularization. To incorporate cobalt into BG, 1 mol% of calcium was substituting with cobalt, and this formulation was compared to the one without cobalt. Both BGs were processed via melt-derived method. The BG powders with particle size less than 38 µm were incubated with cell culture medium for 4 hours at 37°C on continuous rolling, and then the medium was filtered using 0.22 µm syringe filters. Prior to use, the BG-conditioned media were supplemented with 10% (v/v) fetal bovine serum and 1% (v/v) antibiotic-antimycotic, and were allowed to equilibrate overnight inside a CO2 incubator. The conditioned media were used on human dental stem cells (stem cells from permanent (DPSC) and deciduous (SHED) teeth) and assessed for their capacity to stimulate the release of angiogenic factors from the cells. The results showed that cobalt ions were released from the cobalt-containing BG, following partial dissolution of the glasses in cell culture medium, and promoted VEGF release from the cells. In conclusion, the incorporation of cobalt in BG may have potential to be used for tissue regeneration by promoting vascularization through the activation of hypoxia pathway and the release of VEGF.

A New Type of Metal-Binding Site in Cobalt- And Zinc-Containing Adenylate Kinases Isolated From Sulfate-Reducers D. Gigas And D. Desulfuricans ATCC 27774

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gavel, O.Y.; Bursakov, S.A.; Rocco, G.Di

2009-05-18

Adenylate kinase (AK) mediates the reversible transfer of phosphate groups between the adenylate nucleotides and contributes to the maintenance of their constant cellular level, necessary for energy metabolism and nucleic acid synthesis. The AK were purified from crude extracts of two sulfate-reducing bacteria (SRB), Desulfovibrio (D.) gigas NCIB 9332 and Desulfovibrio desulfuricans ATCC 27774, and biochemically and spectroscopically characterized in the native and fully cobalt- or zinc-substituted forms. These are the first reported adenylate kinases that bind either zinc or cobalt and are related to the subgroup of metal-containing AK found, in most cases, in Gram-positive bacteria. The electronic absorptionmore » spectrum is consistent with tetrahedral coordinated cobalt, predominantly via sulfur ligands, and is supported by EPR. The involvement of three cysteines in cobalt or zinc coordination was confirmed by chemical methods. Extended X-ray absorption fine structure (EXAFS) indicate that cobalt or zinc are bound by three cysteine residues and one histidine in the metal-binding site of the 'LID' domain. The sequence {sup 129}Cys-X{sub 5}-His-X{sub 15}-Cys-X{sub 2}-Cys of the AK from D. gigas is involved in metal coordination and represents a new type of binding motif that differs from other known zinc-binding sites of AK. Cobalt and zinc play a structural role in stabilizing the LID domain.« less

Cyano- and polycyanometallo-porphyrins as catalysts for alkane oxidation

DOEpatents

Ellis, P.E. Jr.; Lyons, J.E.

1995-01-17

New compositions of matter comprising cyano-substituted metal complexes of porphyrins are catalysts for the oxidation of alkanes. The metal is iron, chromium, manganese, ruthenium, copper or cobalt. The porphyrin ring has cyano groups attached thereto in meso and/or [beta]-pyrrolic positions.

Cyano- and polycyanometallo-porphyrins as catalysts for alkane oxidation

DOEpatents

Ellis, P.E. Jr.; Lyons, J.E.

1993-05-18

New compositions of matter comprising cyano-substituted metal complexes of porphyrins are catalysts for the oxidation of alkanes. The metal is iron, chromium, manganese, ruthenium, copper or cobalt. The porphyrin ring has cyano groups attached thereto in meso- and/or [beta]-pyrrolic positions.

Cyano- and polycyanometallo-porphyrins as catalysts for alkane oxidation

DOEpatents

Ellis, Jr., Paul E.; Lyons, James E.

1993-01-01

New compositions of matter comprising cyano-substituted metal complexes of porphyrins are catalysts for the oxidation of alkanes. The metal is iron, chromium, manganese, ruthenium, copper or cobalt. The porphyrin ring has cyano groups attached thereto in meso and/or .beta.-pyrrolic positions.

Cyano- and polycyanometallo-porphyrins as catalysts for alkane oxidation

DOEpatents

Ellis, Jr., Paul E.; Lyons, James E.

1995-01-01

New compositions of matter comprising cyano-substituted metal complexes of porphyrins are catalysts for the oxidation of alkanes. The metal is iron, chromium, manganese, ruthenium, copper or cobalt. The porphyrin ring has cyano groups attached thereto in meso and/or .beta.-pyrrolic positions.

From an Easily Accessible Pentacarbonylcobalt(I) Salt to Piano-Stool Cations [(arene)Co(CO)2 ].

PubMed

Meier, Stefan C; Holz, Albina; Schmidt, Alexei; Kratzert, Daniel; Himmel, Daniel; Krossing, Ingo

2017-10-17

The facile synthesis of a pentacarbonyl cobalt(I) salt without the need for a superacid as solvent is presented. This salt, [Co(CO) 5 ] + [Al(OR F ) 4 ] - {R F =C(CF 3 ) 3 }, readily accessible on a multigram scale, undergoes substitution reactions with arenes yielding the hitherto unknown class of two-legged cobalt piano-stool complexes [(arene)Co(CO) 2 ] + with four different arene ligands. Such a substitution chemistry would have been impossible in superacid solution, as the arenes used would have been oxidized and/or protonated. Thus, the general approach described herein may have a wide synthetic use. Additionally, the thermochemistry of the piano-stool complexes is shown to be not easy to describe computationally and most of the established DFT methods overestimate the reaction energies. Only CCSD(T) calculations close to the basis set limit gave energies fully agreeing with the experiment. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

United States Air Force Summary, Fifth Edition

DTIC Science & Technology

1979-03-01

t911 COPPER BAUXITE UNITED STATES ZINC CBROIJJI. C!’ NICKEL SOURCE. CIA -HANDBOOK OF ECONOMIC STATISTICS, 19711 IINC it IANSINESE COBALT IRON().pueUI...Wilson, Charles (TX) Boggs, Lindy (Mrs. Hole)(LA) Benjomin, Adam Jr. (IN) Dicks, Norman D. (WAI McHugh "Mafhew F. (NY) Ginn, So (GA) lehman, Williom

Probing the Unique Role of Gallium in Amorphous Oxide Semiconductors through Structure-Property Relationships

DOE Office of Scientific and Technical Information (OSTI.GOV)

Moffitt, Stephanie L.; Zhu, Qimin; Ma, Qing

This study explores the unique role of Ga in amorphous (a-) In[BOND]Ga[BOND]O oxide semiconductors through combined theory and experiment. It reveals substitutional effects that have not previously been attributed to Ga, and that are investigated by examining how Ga influences structure–property relationships in a series of pulsed laser deposited a-In[BOND]Ga[BOND]O thin films. Element-specific structural studies (X-ray absorption and anomalous scattering) show good agreement with the results of ab initio molecular dynamics simulations. This structural knowledge is used to understand the results of air-annealing and Hall effect electrical measurements. The crystallization temperature of a-IO is shown to increase by as muchmore » as 325 °C on substituting Ga for In. This increased thermal stability is understood on the basis of the large changes in local structure that Ga undergoes, as compared to In, during crystallization. Hall measurements reveal an initial sharp drop in both carrier concentration and mobility with increasing Ga incorporation, which moderates at >20 at% Ga content. This decline in both the carrier concentration and mobility with increasing Ga is attributed to dilution of the charge-carrying In[BOND]O matrix and to increased structural disorder. The latter effect saturates at high at% Ga.« less

Symmetry transition via tetravalent impurity and investigations on magnetic properties of Li0.5Fe2.5O4

NASA Astrophysics Data System (ADS)

Kounsalye, Jitendra S.; Kharat, Prashant B.; Chavan, Apparao R.; Humbe, Ashok V.; Borade, R. M.; Jadhav, K. M.

2018-04-01

The present study, deals with the phase symmetry transformation of lithium ferrite after introducing tetravalent (Ti4+) impurity. The sol-gel auto combustion technique was adopted for the synthesis of nanoparticle samples with generic chemical formula Li0.5Fe2.5O4 and Li0.55Ti0.10Fe2.35O4. The synthesized nanoparticles were characterized by X-ray diffraction (XRD) technique for structural analysis. The XRD patterns show the single phase cubic structure without any impurity phase but the P4332 to Fd-3m transformation was observed after introducing Ti4+ impurity. The Nano size of the synthesized particles was confirmed by crystallite size ( 20nm) calculated using Debye-Scherrer's formula. The Fourier transform infrared spectroscopy (FTIR) studies shows shifting of band frequencies which reflect the structural changes after tetravalent substitutional impurities. The magnetic properties were studied through pulse field hysteresis loop (M-H loop) technique at room temperature, the M-H loops showdecrease in magnetic properties afternonmagnetic Ti4+ ion substitution. This is attributed to transition of inverse spinel structure of lithium ferrite to random spinel structure.

Cobalt-Catalyzed C(sp(2))-H Borylation: Mechanistic Insights Inspire Catalyst Design.

PubMed

Obligacion, Jennifer V; Semproni, Scott P; Pappas, Iraklis; Chirik, Paul J

2016-08-24

A comprehensive study into the mechanism of bis(phosphino)pyridine (PNP) cobalt-catalyzed C-H borylation of 2,6-lutidine using B2Pin2 (Pin = pinacolate) has been conducted. The experimentally observed rate law, deuterium kinetic isotope effects, and identification of the catalyst resting state support turnover limiting C-H activation from a fully characterized cobalt(I) boryl intermediate. Monitoring the catalytic reaction as a function of time revealed that borylation of the 4-position of the pincer in the cobalt catalyst was faster than arene borylation. Cyclic voltammetry established the electron withdrawing influence of 4-BPin, which slows the rate of C-H oxidative addition and hence overall catalytic turnover. This mechanistic insight inspired the next generation of 4-substituted PNP cobalt catalysts with electron donating and sterically blocking methyl and pyrrolidinyl substituents that exhibited increased activity for the C-H borylation of unactivated arenes. The rationally designed catalysts promote effective turnover with stoichiometric quantities of arene substrate and B2Pin2. Kinetic studies on the improved catalyst, 4-(H)2BPin, established a change in turnover limiting step from C-H oxidative addition to C-B reductive elimination. The iridium congener of the optimized cobalt catalyst, 6-(H)2BPin, was prepared and crystallographically characterized and proved inactive for C-H borylation, a result of the high kinetic barrier for reductive elimination from octahedral Ir(III) complexes.

The effect of ionic Co presence on the structural, optical and photocatalytic properties of modified cobalt-titanate nanotubes.

PubMed

Barrocas, B; Silvestre, A J; Rolo, A G; Monteiro, O C

2016-07-21

With the aim of producing materials with enhanced optical and photocatalytic properties, titanate nanotubes (TNTs) modified by cobalt doping (Co-TNT) and by Na(+)→ Co ion-exchange (TNT/Co) were successfully prepared by a hydrothermal method. The influence of the doping level and of the cobalt position in the TNT crystalline structure was studied. Although no perceptible influence of the cobalt ion position on the morphology of the prepared titanate nanotubes was observed, the optical behaviour of the cobalt modified samples is clearly dependent on the cobalt ions either substituting the Ti(4+) ions in the TiO6 octahedra building blocks of the TNT structure (doped samples) or replacing the Na(+) ions between the TiO6 interlayers (ion-exchange samples). The catalytic ability of these materials on pollutant photodegradation was investigated. First, the evaluation of hydroxyl radical formation using the terephthalic acid as a probe was performed. Afterwards, phenol, naphthol yellow S and brilliant green were used as model pollutants. Anticipating real world situations, photocatalytic experiments were performed using solutions combining these pollutants. The results show that the Co modified TNT materials (Co-TNT and TNT/Co) are good catalysts, the photocatalytic performance being dependent on the Co/Ti ratio and on the structural metal location. The Co(1%)-TNT doped sample was the best photocatalyst for all the degradation processes studied.

Reducing Mg Acceptor Activation-Energy in Al0.83Ga0.17N Disorder Alloy Substituted by Nanoscale (AlN)5/(GaN)1 Superlattice Using MgGa δ-Doping: Mg Local-Structure Effect

NASA Astrophysics Data System (ADS)

Zhong, Hong-Xia; Shi, Jun-Jie; Zhang, Min; Jiang, Xin-He; Huang, Pu; Ding, Yi-Min

2014-10-01

Improving p-type doping efficiency in Al-rich AlGaN alloys is a worldwide problem for the realization of AlGaN-based deep ultraviolet optoelectronic devices. In order to solve this problem, we calculate Mg acceptor activation energy and investigate its relationship with Mg local structure in nanoscale (AlN)5/(GaN)1 superlattice (SL), a substitution for Al0.83Ga0.17N disorder alloy, using first-principles calculations. A universal picture to reduce acceptor activation energy in wide-gap semiconductors is given for the first time. By reducing the volume of the acceptor local structure slightly, its activation energy can be decreased remarkably. Our results show that Mg acceptor activation energy can be reduced significantly from 0.44 eV in Al0.83Ga0.17N disorder alloy to 0.26 eV, very close to the Mg acceptor activation energy in GaN, and a high hole concentration in the order of 1019 cm-3 can be obtained in (AlN)5/(GaN)1 SL by MgGa δ-doping owing to GaN-monolayer modulation. We thus open up a new way to reduce Mg acceptor activation energy and increase hole concentration in Al-rich AlGaN.

Reducing Mg acceptor activation-energy in Al(0.83)Ga(0.17)N disorder alloy substituted by nanoscale (AlN)₅/(GaN)₁ superlattice using Mg(Ga) δ-doping: Mg local-structure effect.

PubMed

Zhong, Hong-xia; Shi, Jun-jie; Zhang, Min; Jiang, Xin-he; Huang, Pu; Ding, Yi-min

2014-10-23

Improving p-type doping efficiency in Al-rich AlGaN alloys is a worldwide problem for the realization of AlGaN-based deep ultraviolet optoelectronic devices. In order to solve this problem, we calculate Mg acceptor activation energy and investigate its relationship with Mg local structure in nanoscale (AlN)5/(GaN)1 superlattice (SL), a substitution for Al(0.83)Ga(0.17)N disorder alloy, using first-principles calculations. A universal picture to reduce acceptor activation energy in wide-gap semiconductors is given for the first time. By reducing the volume of the acceptor local structure slightly, its activation energy can be decreased remarkably. Our results show that Mg acceptor activation energy can be reduced significantly from 0.44 eV in Al(0.83)Ga(0.17)N disorder alloy to 0.26 eV, very close to the Mg acceptor activation energy in GaN, and a high hole concentration in the order of 10(19) cm(-3) can be obtained in (AlN)5/(GaN)1 SL by Mg(Ga) δ-doping owing to GaN-monolayer modulation. We thus open up a new way to reduce Mg acceptor activation energy and increase hole concentration in Al-rich AlGaN.

Superconductivity of Ba8Si46-xGax clathrates

NASA Astrophysics Data System (ADS)

Li, Yang; Zhang, Ruihong; Chen, Ning; Ma, Xingqiao; Cao, Guohui; Luo, Z. P.; Hu, C. R.; Ross, Joseph H., Jr.

2007-03-01

We have presented a combined experimental and theoretical study of the effect of Gallium substitution on the superconductivity of the type I clathrate Ba8Si46-xGax. In Ga-doped clathrates, the Ga state is found to be strongly hybridized with the cage conduction-band state. Ga substitution results in a shift toward to a lower energy, a decrease of density of states at Fermi level, a lowering of the carrier concentration and a breakage of integrity of the sp3 hybridized networks. These play key roles in the suppression of superconductivity. For Ba8Si40Ga6, the onset of the superconducting transition occurs at Tc=3.3 K. The investigation of the magnetic superconducting state shows that Ba8Si40Ga6 is a type II superconductor. The critical magnetic fields were measured to be Hc1=35 Oe and Hc2=8.5 kOe. Our estimate of the lectron-phonon coupling reveals that Ba8Si40Ga6 is a moderate phonon-mediated BCS superconductor.

Lattice Location of Mg in GaN: A Fresh Look at Doping Limitations.

PubMed

Wahl, U; Amorim, L M; Augustyns, V; Costa, A; David-Bosne, E; Lima, T A L; Lippertz, G; Correia, J G; da Silva, M R; Kappers, M J; Temst, K; Vantomme, A; Pereira, L M C

2017-03-03

Radioactive ^{27}Mg (t_{1/2}=9.5  min) was implanted into GaN of different doping types at CERN's ISOLDE facility and its lattice site determined via β^{-} emission channeling. Following implantations between room temperature and 800 °C, the majority of ^{27}Mg occupies the substitutional Ga sites; however, below 350 °C significant fractions were also found on interstitial positions ∼0.6  Å from ideal octahedral sites. The interstitial fraction of Mg was correlated with the GaN doping character, being highest (up to 31%) in samples doped p type with 2×10^{19}  cm^{-3} stable Mg during epilayer growth, and lowest in Si-doped n-GaN, thus giving direct evidence for the amphoteric character of Mg. Implanting above 350 °C converts interstitial ^{27}Mg to substitutional Ga sites, which allows estimating the activation energy for migration of interstitial Mg as between 1.3 and 2.0 eV.

Lattice Location of Mg in GaN: A Fresh Look at Doping Limitations

NASA Astrophysics Data System (ADS)

Wahl, U.; Amorim, L. M.; Augustyns, V.; Costa, A.; David-Bosne, E.; Lima, T. A. L.; Lippertz, G.; Correia, J. G.; da Silva, M. R.; Kappers, M. J.; Temst, K.; Vantomme, A.; Pereira, L. M. C.

2017-03-01

Radioactive 27Mg (t1 /2=9.5 min ) was implanted into GaN of different doping types at CERN's ISOLDE facility and its lattice site determined via β- emission channeling. Following implantations between room temperature and 800 °C , the majority of 27Mg occupies the substitutional Ga sites; however, below 350 °C significant fractions were also found on interstitial positions ˜0.6 Å from ideal octahedral sites. The interstitial fraction of Mg was correlated with the GaN doping character, being highest (up to 31%) in samples doped p type with 2 ×1019 cm-3 stable Mg during epilayer growth, and lowest in Si-doped n -GaN, thus giving direct evidence for the amphoteric character of Mg. Implanting above 350 °C converts interstitial 27Mg to substitutional Ga sites, which allows estimating the activation energy for migration of interstitial Mg as between 1.3 and 2.0 eV.

Ab-initio study of dilute nitride substitutional and split-interstitial impurities in gallium antimonide (N-GaSb)

NASA Astrophysics Data System (ADS)

Jadaun, Priyamvada; Nair, Hari P.; Bank, Seth R.; Banerjee, Sanjay K.

2012-02-01

We present an ab-initio density functinal theory study of dilute-nitride GaSb. Adding dilute quantities of nitrogen causes rapid reduction in bandgap of GaSb (˜300 meV for 2% N). Due to this rapid reduction in bandgap, dilute-nitrides provide a pathway for extending the emission of GaSb based type-I diode lasers into the mid-infrared wavelength region (3-5 micron). In this study we look at the effect of substitutional N impurity on the electronic properties of our system and compare it with the band-anticrossing model, a phenomenological model, which has been used to explain giant band bowing observed in dilute-nitride alloys. We also study the effect of Sb-N split interstitials which are known to be non-radiative recombination centers. Furthermore we also discuss the stability of the Sb-N split interstitial relative to substitutional nitrogen to determine if the split interstitials can be annihilated using post-growth annealing to improve the radiative lifetime of the material which essential for laser operation.

Influence of Fe-substitution on structural, magnetic and magnetocaloric properties of Nd2Fe17-xCox solid solutions

NASA Astrophysics Data System (ADS)

Bouchaala, N.; Jemmali, M.; Bartoli, T.; Nouri, K.; Hentech, I.; Walha, S.; Bessais, L.; Salah, A. Ben

2018-02-01

Nd2Fe17-xCox (x = 0 , 1 , 2 , 3 , 4) intermetallic compounds, obtained under arc-melting conditions, have been investigated by means of X-ray diffraction analysis (XRD), Mössbauer spectrometry and magnetic measurements. The Rietveld refinement revealed that the sample is a pure compound with rhombohedral Th2Zn17-type structure (R 3 bar m space group) with the following lattice parameters: a = 8.5792 (2) Å, c = 12.4615 (2) Å. Using Mössbauer spectrometry analysis coupled with structural consideration we have unambiguously determined the cobalt atoms preferred inequivalent crystallographic site. Nd2Fe17 show an increase of 3.5 T in their weighted average hyperfine fields upon cobalt substitution. Whatever the cobalt content, the hyperfine field of these compounds follow this sequence Hhf { 6 c } >Hhf { 9 d } >Hhf { 18 f } >Hhf { 18 h }. The magnetic measurements showed that the Curie temperature increases with the Co content. The magnetic entropy change (ΔSM) was estimated from isothermal magnetization curves and it increases from 3.35 J/Kg K for x = 0 to 5.83 J/Kg K for x = 2 at μ0 H = 1.6 T . The relative cooling power (RCP) is in the range of 11.6 J/kg (x = 0) and 16 J/kg (x = 2).

High temperature alloy

NASA Technical Reports Server (NTRS)

Frank, R. G.; Semmel, J. W., Jr.

1968-01-01

Molybdenum is substituted for tungsten on an atomic basis in a cobalt-based alloy, S-1, thus enabling the alloy to be formed into various mill products, such as tubing and steels. The alloy is weldable, has good high temperature strength and is not subject to embrittlement produced by high temperature aging.

Effect of Cu2+ substitution on the structural, magnetic and electrical properties of gadolinium orthoferrite

NASA Astrophysics Data System (ADS)

Sai Vandana, C.; Hemalatha Rudramadevi, B.

2018-04-01

The pure and copper (Cu) substituted Gadolinium orthoferrites, GdFeO3, GdCu0.1Fe0.9O3, GdCu0.2Fe0.8O3 and GdCu0.3Fe0.7O3 were synthesized by conventional solid state method. The structural, morphological, dielectric, magnetic and impedance properties of Cu substituted Gadolinium orthoferrites have been investigated. The crystallographic phase as well as the substitution of Cu2+ ions in the lattice of GdFeO3 is confirmed from the x-ray diffraction patterns. The Fourier transform infrared spectra exhibit two prominent fundamental absorption peaks at ∼417 cm‑1 and 545 cm‑1. These bands are related to inherent stretching vibrations of metals at octahedral and tetrahedral sites respectively. The coercivity (Hc) and saturation magnetization (Ms) of the synthesized samples at different temperatures were determined from the hysteresis plots. Higher coercive values, 598 Oe and 600 Oe were achieved in GdCu0.1Fe0.9O3 ferrites compared to 527 Oe and 360 Oe in pure GdFeO3 at room temperature (300 K) and low temperature (20 k) respectively. Dielectric dispersion has been observed for gadolinium ferrite samples with Maxwell–Wagner type interfacial polarization. The decrease of dielectric constant and dielectric loss tangent with an increase in frequency was observed. The conduction due to charge hopping between localized states was confirmed from AC conductivity measurements. The composition dependent cationic distributions estimated from XRD, magnetic and electrical studies are in good agreement with each other. The achieved results indicate that the substitution of Cu in gadolinium orthoferrite strongly influences the crystal structure, magnetic and electrical properties thereby making them suitable as multiple state memory devices, transducers, electronic field controlled ferromagnetic resonance devices and spintronic devices.

Calcination temperature effect on the microstructure and dielectric properties of M-type strontium hexagonal ferrites

NASA Astrophysics Data System (ADS)

Mohammed, J.; Sharma, Jyoti; Kumar, Sachin; Trudel, T. T. Carol; Srivastava, A. K.

2017-07-01

M-type hexagonal ferrites have found wide application in electronics industry due to the possibility of tuning properties such as dielectric properties. An improved dielectric property is useful in high frequency application. In this paper, we studied the effect of calcination temperature on structural and dielectric properties of Al-Mn substituted M-type strontium hexagonal ferrites with chemical composition Sr1-xAlxFe12-yMnyO19 (x=0.3 and y=0.6) synthesized by sol-gel auto-combustion method. The prepared sample was sintered at four different temperatures (T=750°C, 850°C, 950°C and 1050°C) for 5 hours. Characterisations of the synthesized samples were carried out using X-ray diffraction (XRD), impedance analyser, field emission electron microscope (FE-SEM) and energy dispersive X-ray (EDX) spectroscopy. The dielectric properties were explained on the basis of Koop's phenomenological theory and Maxwell Wagner theory. The sample calcinated at 750°C shows the highest value of dielectric constant and AC conductivity whereas that calcinated at 1050°C exhibit the lowest dielectric losses.

Phase Transformations of an Fe-0.85 C-17.9 Mn-7.1 Al Austenitic Steel After Quenching and Annealing

NASA Astrophysics Data System (ADS)

Cheng, Wei-Chun

2014-09-01

Low-density Mn-Al steels could potentially be substitutes for commercial Ni-Cr stainless steels. However, the development of the Mn-Al stainless steels requires knowledge of the phase transformations that occur during the steel making processes. Phase transformations of an Fe-0.85 C-17.9 Mn-7.1 Al (wt.%) austenitic steel, which include spinodal decomposition, precipitation transformations, and cellular transformations, have been studied after quenching and annealing. The results show that spinodal decomposition occurs prior to the precipitation transformation in the steel after quenching and annealing at temperatures below 1023 K and that coherent fine particles of L12-type carbide precipitate homogeneously in the austenite. The cellular transformation occurs during the transformation of high-temperature austenite into lamellae of austenite, ferrite, and kappa carbide at temperatures below 1048 K. During annealing at temperatures below 923 K, the austenite decomposes into lamellar austenite, ferrite, κ-carbide, and M23C6 carbide grains for another cellular transformation. Last, when annealing at temperatures below 873 K, lamellae of ferrite and κ-carbide appear in the austenite.

Effect of zinc substitution on the structural, electrical and magnetic properties of nano-structured Ni0.5Co0.5Fe2O4 ferrites

NASA Astrophysics Data System (ADS)

Babu, K. Vijaya; Sailaja, B.; Jalaiah, K.; Shibeshi, Paulos Taddesse; Ravi, M.

2018-04-01

A series of Ni0.5Co0.5-xZnxFe2O4 (x = 0, 0.02, 0.04 and 0.06) nanoferrites were synthesized by sol-gel method using citric acid as chelating reagent. The synthesized ferrite systems are characterized by XRD, SEM, FTIR, ESR and dielectric techniques. The formation of cubic spinel phase belonging to space group Fd3m is identified from the X-ray diffraction patterns. SEM showed the particles are in spherical shape with an average grain size 5-10 nm. FTIR spectra portrait the fundamental absorption bands in the range 400-600 cm-1 relating to octahedral and tetrahedral sites. Dielectric properties are investigated over the frequency range of 20 Hz to 1 MHz at room temperature. A difference in dielectric constant (εr) and dissipation factor (tanδ) of the ferrites has been observed. The dielectric constant and dielectric loss tangent decreases exponentially with increase in frequency. The obtained results are good agreeing with the reported values.

Size tuned polyol-made Zn0.9M0.1Fe2O4 (M = Mn, Co, Ni) ferrite nanoparticles as potential heating agents for magnetic hyperthermia: from synthesis control to toxicity survey

NASA Astrophysics Data System (ADS)

Basti, H.; Hanini, A.; Levy, M.; Ben Tahar, L.; Herbst, F.; Smiri, L. S.; Kacem, K.; Gavard, J.; Wilhelm, C.; Gazeau, F.; Chau, F.; Ammar, S.

2014-12-01

Zn-rich substituted Zn0.9M0.1Fe2O4 (M = Mn, Co, Ni) ferrite nanoparticles (NPs) of about 5 and 10 nm were produced by the so-called polyol method. They were engineered for hyperthermia therapy based on their magnetic and morphological properties. Indeed, because of their comparatively low Curie temperature and reasonable magnetization, these probes may turn into useful self-regulated heating agents under suitable conditions. For such a purpose, the structure, the microstructure, the magnetic and magnetocalorimetric properties of the produced NPs as well as their in vitro cytotoxicity were investigated. Our results demonstrate that the magnetic properties of these magnetically diluted spinel ferrite particles can be largely modified by just changing their size. They also show that the about 10 nm sized manganese-based ones exhibit the highest heating power under a 700 kHz ac magnetic field and the lowest cytotoxicity on Immortalized human umbilical vascular endothelial cells (HUVEC).

Effects of the substitution of gallium with boron on the physical and mechanical properties of Ni-Mn-Ga shape memory alloys

NASA Astrophysics Data System (ADS)

Aydogdu, Yildirim; Turabi, Ali Sadi; Kok, Mediha; Aydogdu, Ayse; Tobe, Hirobumi; Karaca, Haluk Ersin

2014-12-01

The effects of the substitution of gallium with boron on the physical, mechanical and magnetic shape memory properties of Ni51Mn28.5Ga20.5- xBx (at.%) ( x = 0, 1, 2, 3) polycrystalline alloys are investigated. It has been found that transformation temperatures are decreasing while hardness is increasing with boron addition. B-doping of NiMnGa alloys results in the formation of a second phase that increases its ductility and strength in compression. Moreover, saturation magnetization of austenite is decreasing, while Curie temperature of austenite is increasing with B-doping.

Structural study of Mg doped cobalt ferrite thin films on ITO coated glass substrate

NASA Astrophysics Data System (ADS)

Suthar, Mahesh; Bapna, Komal; Kumar, Kishor; Ahuja, B. L.

2018-05-01

We have synthesized thin films of Co1-xMgxFe2O4 (x = 0, 0.4, 0.6, 0.8, 1) on transparent conducting indium tin oxide (ITO) coated glass substrate by pulsed laser deposition method. The structural properties of the grown films were analyzed by the X-ray diffraction and Raman spectroscopy, which suggest the single phase growth of these films. Raman spectra revealed the incorporation of Mg ions into CoFe2O4 lattice and suggest that the Mg ions initially go both to the octahedral and tetrahedral sites upto a certain concentration. For higher concentration, Mg ions prefer to occupy the tetrahedral sites.

Synthesis, morphology and electrical properties of Co2+ substituted NiCuZn ferrites for MLCI applications

NASA Astrophysics Data System (ADS)

Kabbur, S. M.; Waghmare, S. D.; Ghodake, U. R.; Suryavanshi, S. S.

2018-04-01

Co2+ is a fast relaxing ion which can enhance microwave properties. This work focuses on the synthesis and analysis of Ni0.25-xCoxCu0.30Zn0.45Fe2O4 (x = 0.00, 0.05, 0.01, 0.15, 0.20 and 0.25) ferrites by auto combustion method using glycine as the chelating agent. From X-ray Diffraction (XRD) spectra, the structural parameters are analysed. The lattice parameter (a) decreases due to smaller ionic radius of Co2+ (0.072 nm) which replaces Ni2+ (0.078 nm). Bulk density and porosity measurements show that there are pores and lattice imperfections. The cation distribution of the ferrites based on Neel's two sublattice model is proposed. Transmission Electron Micrographs (TEM) indicate narrow size distribution of spherical shaped nanoparticles. DC electrical resistivity (ρD.C.) is very important factor of low temperature sintered ferrites for MLCI applications. Electroplating of the devices is much affected by electrical resistivity. Maximum DC resistivity (2.89 × 106 Ω-cm) is observed for the sample with x=0.20. The dielectric parameters (ɛ', ɛ″ and tan δ) decrease as the alternating field increases which is due to space charge distribution and hopping mechanism. AC resistivity (ρAC) decreases with frequency, increased concentration of Fe2+ ions induces electron hopping: Fe3+ ↔ Fe2+ at B sites thereby reducing the resistivity. The low dielectric loss factor of 0.07 for x=0.20 ferrite indicates that the sample can be potential candidate for MLCI applications.

Highly efficient solid state magnetoelectric gyrators

NASA Astrophysics Data System (ADS)

Leung, Chung Ming; Zhuang, Xin; Friedrichs, Daniel; Li, Jiefang; Erickson, Robert W.; Laletin, V.; Popov, M.; Srinivasan, G.; Viehland, D.

2017-09-01

An enhancement in the power-conversion-efficiency (η) of a magneto-electric (ME) gyrator has been found by the use of Mn-substituted nickel zinc ferrite. A trilayer gyrator of Mn-doped Ni0.8Zn0.2Fe2O3 and Pb(Zr,Ti)O3 has η = 85% at low power conditions (˜20 mW/in3) and η ≥ 80% at high power conditions (˜5 W/in3). It works close to fundamental electromechanical resonance in both direct and converse modes. The value of η is by far the highest reported so far, which is due to the high mechanical quality factor (Qm) of the magnetostrictive ferrite. Such highly efficient ME gyrators with a significant power density could become important elements in power electronics, potentially replacing electromagnetic and piezoelectric transformers.

On the dielectric dispersion and absorption in nanosized manganese zinc mixed ferrites.

PubMed

Veena Gopalan, E; Malini, K A; Sakthi Kumar, D; Yoshida, Yasuhiko; Al-Omari, I A; Saravanan, S; Anantharaman, M R

2009-04-08

The temperature and frequency dependence of dielectric permittivity and dielectric loss of nanosized Mn(1-x)Zn(x)Fe(2)O(4) (for x = 0, 0.2, 0.4, 0.6, 0.8, 1) were investigated. The impact of zinc substitution on the dielectric properties of the mixed ferrite is elucidated. Strong dielectric dispersion and broad relaxation were exhibited by Mn(1-x)Zn(x)Fe(2)O(4). The variation of dielectric relaxation time with temperature suggests the involvement of multiple relaxation processes. Cole-Cole plots were employed as an effective tool for studying the observed phenomenon. The activation energies were calculated from relaxation peaks and Cole-Cole plots and found to be consistent with each other and indicative of a polaron conduction.

Moessbauer studies in zinc-manganese ferrites for use in measuring small velocities and accelerations with great precision

NASA Technical Reports Server (NTRS)

Escue, W. T.; Gupta, R. G.; Mendiratta, R. G.

1975-01-01

Mossbauer spectroscopy was used for a systematic study of the magnetic behavior of manganese and zinc in mixed ferrites. It was observed that Zn2+ has preference to substitute Mn2+ at interstitial sites where the metal ions are tetrahedrally coordinated with four oxygen neighbors. The internal magnetic hyperfine field at the tetrahedral iron site is larger than that at the octahedral site. The relaxation effects were observed to play an important role as the zinc contents were increased, while the spin-correlation time and the magnetic field were observed to decrease in strength. It is concluded that Mossbauer effect data on complex materials, when used in conjunction with other data, can provide useful insight into the origin of the microscopic properties of magnetic materials.

On the Processing of Martensitic Steels in Continuous Galvanizing Lines: Part II

NASA Astrophysics Data System (ADS)

Song, Taejin; Kwak, Jaihyun; de Cooman, B. C.

2012-01-01

The conventional continuous hot-dip galvanizing (GI) and galvannealing (GA) processes can be applied to untransformed austenite to produce Zn and Zn-alloy coated low-carbon ultra-high-strength martensitic steel provided specific alloying additions are made. The most suitable austenite decomposition behavior results from the combined addition of boron, Cr, and Mo, which results in a pronounced transformation bay during isothermal transformation. The occurrence of this transformation bay implies a considerable retardation of the austenite decomposition in the temperature range below the bay, which is close to the stages in the continuous galvanizing line (CGL) thermal cycle related to the GI and GA processes. After the GI and GA processes, a small amount of granular bainite, which consists of bainitic ferrite and discrete islands of martensite/austenite (M/A) constituents embedded in martensite matrix, is present in the microstructure. The ultimate tensile strength (UTS) of the steel after the GI and GA cycle was over 1300 MPa, and the stress-strain curve was continuous without any yielding phenomena.

First-principles study of alloying effects on fluorine incorporation in Al x Ga1-x N alloys

NASA Astrophysics Data System (ADS)

Wang, Rong; Tan, Wei; Zhang, Jian; Chen, Feng-Xiang; Wei, Su-Huai

2018-02-01

Incorporation of fluorine (F) into the AlGaN layer is crucial to the fabrication of enhancement-mode (E-mode) AlGaN/GaN high electron mobility transistors (HEMTs). However, the understanding of properties of F doping in AlGaN alloys is rather limited. Using first-principles calculations and the special quasirandom structure (SQS) approach, we investigate the alloying effects on the doping properties of F-incorporated Al x Ga1-x N alloys. We find that substitutional F on N sites (FN) and interstitial F (Fi) are dominant defects for F in Al x Ga1-x N alloys. For these two types of defects, both the global composition x and the local motif surrounding the dopant play important roles. On contrary, the incorporation of substitutional F on Ga sites (FGa) or Al sites (FAl) are affected only by the composition x. We also find that there exists a large asymmetric bowing for the effective formation energies of FN and Fi. These results are explained in terms of local structural distortion and electronic effects. The mechanism discussed in this paper can also be used in understanding doping in other semiconductor alloys.

DEVELOPING AZO AND FORMAZAN DYES BASED ON ENVIRONMENTAL CONSIDERATIONS: SALMONELLA MUTAGENICITY

EPA Science Inventory

Abstract
In previous papers, the synthesis and chemical properties of iron-complexed azo and formazan dyes were reported. In this regard, it was shown that in certain cases iron could be substituted for the traditionally used metals, chromium and cobalt, without having an adve...

Electronic Conductivity of Doped-Lanthanum Gallate Electrolytes

NASA Astrophysics Data System (ADS)

Yamaji, Katsuhiko; Xiong, Yue Ping; Kishimoto, Haruo; Horita, Teruhisa; Sakai, Natsuko; Brito, Manuel E.; Yokokawa, Harumi

Electronic conductivity of doped lanthanum gallate electrolytes were determined by using a Hebb-Wagner type polarization cell. Electronic conductivity of cobalt-doped, La0.8Sr0.2Ga0.8Mg0.15Co0.5O3-δ (LSGMC), and non cobalt-doped, La0.8Sr0.2Ga0.8Mg0.2O2.8 (LSGM8282), were measured as a function of oxygen partial pressures. The electronic conductivity of LSGM8282 showed a linear dependence on p(O2)1/4 in the higher p(O2) region, which is attributed to the electronic hole conductivity. The electronic conductivity of LSGMC showed a linear dependence on p(O2)1/6 in the higher p(O2) region. LSGMC has higher electronic conductivity than LSGM, and the conductivity was not clearly changed with temperatures between 600 and 800 °C. In lower p(O2) region, the electronic conductivity data have poor reproducibility and did not show any dependence on p(O2) because of the degradation of the electrolytes in severe reducing atmospheres.

Synthesis and first-principle calculations of the structural and electronic properties of Ge-substituted type-VIII Ba8Ga16Sn30 clathrate

NASA Astrophysics Data System (ADS)

Shen, Lanxian; Li, Decong; Liu, Hongxia; Liu, Zuming; Deng, Shukang

2016-12-01

In this study, the structural and electronic structural properties of Ba8Ga16Sn30-xGex (0≤x≤30) are determined by the first-principle method on the basis of density functional theory. Consistent with experimental findings, calculated results reveal that Ge atoms preferentially occupy the 2a and 24g sites in these compounds. As the content of Ge in Ge-substituted clathrate is increased, the lattice parameter is decreased, and the structural stability is enhanced. The bandgaps of the compound at 1≤x≤10 are smaller than those of Ba8Ga16Sn30. By contrast, the bandgaps of the compound at x>10 are larger than those of Ba8Ga16Sn30. The substitution of Ge for Sn affects p-type conductivity but not n-type conductivity. As Ge content increases, the whole conduction band moves to the direction of high energy, and the density of states of valence-band top decreases. The calculated potential energy versus displacement of Ba indicates that the vibration energy of this atom increases as cage size decreases. Because Ge substitution also affects clathrate structural symmetry, the distance of Ba atom deviation from the center of the cage initially increases and subsequently decreases as the Ge content increases.

Tunable ferromagnetic resonance in La-Co substituted barium hexaferrites at millimeter wave frequencies

NASA Astrophysics Data System (ADS)

Korolev, Konstantin A.; Wu, Chuanjian; Yu, Zhong; Sun, Ke; Afsar, Mohammed N.; Harris, Vincent G.

2018-05-01

Transmittance measurements have been performed on La-Co substituted barium hexaferrites in millimeter waves. Broadband millimeter-wave measurements have been carried out using the free space quasi-optical spectrometer, equipped with a set of high power backward wave oscillators covering the frequency range of 30 - 120 GHz. Strong absorption zones have been observed in the millimeter-wave transmittance spectra of all La-Co substituted barium hexaferrites due to the ferromagnetic resonance. Linear shift of ferromagnetic resonance frequency as functions of La-Co substitutions have been found. Real and imaginary parts of dielectric permittivity of La-Co substituted barium hexaferrites have been calculated using the analysis of recorded high precision transmittance spectra. Frequency dependences of magnetic permeability of La-Co substituted barium hexaferrites, as well as saturation magnetization and anisotropy field have been determined based on Schlömann's theory for partially magnetized ferrites. La-Co substituted barium hexaferrites have been further investigated by DC magnetization to assess magnetic behavior and compare with millimeter wave data. Consistency of saturation magnetization determined independently by both millimeter wave absorption and DC magnetization have been found for all La-Co substituted barium hexaferrites. These materials seem to be quite promising as tunable millimeter wave absorbers, filters, circulators, based on the adjusting of their substitution parameters.

Characterization of High-Velocity Solution Precursor Flame-Sprayed Manganese Cobalt Oxide Spinel Coatings for Metallic SOFC Interconnectors

NASA Astrophysics Data System (ADS)

Puranen, Jouni; Laakso, Jarmo; Kylmälahti, Mikko; Vuoristo, Petri

2013-06-01

A modified high-velocity oxy-fuel spray (HVOF) thermal spray torch equipped with liquid feeding hardware was used to spray manganese-cobalt solutions on ferritic stainless steel grade Crofer 22 APU substrates. The HVOF torch was modified in such a way that the solution could be fed axially into the combustion chamber through 250- and 300-μm-diameter liquid injector nozzles. The solution used in this study was prepared by diluting nitrates of manganese and cobalt, i.e., Mn(NO3)2·4H2O and Co(NO3)2·6H2O, respectively, in deionized water. The as-sprayed coatings were characterized by X-ray diffraction and field-emission scanning electron microscopy operating in secondary electron mode. Chemical analyses were performed on an energy dispersive spectrometer. Coatings with remarkable density could be prepared by the novel high-velocity solution precursor flame spray (HVSPFS) process. Due to finely sized droplet formation in the HVSPFS process and the use of as delivered Crofer 22 APU substrate material having very low substrate roughness ( R a < 0.5 μm), thin and homogeneous coatings, with thicknesses lower than 10 μm could be prepared. The coatings were found to have a crystalline structure equivalent to MnCo2O4 spinel with addition of Co-oxide phases. Crystallographic structure was restored back to single-phase spinel structure by heat treatment.

Structural and magnetic properties of Ni-Zn and Ni-Zn-Co ferrites

NASA Astrophysics Data System (ADS)

Knyazev, A. V.; Zakharchuk, I.; Lähderanta, E.; Baidakov, K. V.; Knyazeva, S. S.; Ladenkov, I. V.

2017-08-01

Ni-Zn and Ni-Zn-Co ferrite powders with nominal compositions Ni0.5Zn0.5Fe2O4 and Ni0.5Zn0.3Co0.2Fe2O4 were prepared by the solid-state reaction synthesis with periodic regrinding during the calcination at 1073 K. The structure of Ni0.5Zn0.5Fe2O4 and Ni0.5Zn0.3Co0.2Fe2O4 was refined assuming space group F d-3m. Scanning electron microscopy revealed the average sizes of the crystalline ferrite particles are 130-630 nm for Ni0.5Zn0.5Fe2O4 and 140-350 nm for Ni0.5Zn0.3Co0.2Fe2O4. The room temperature saturation magnetizations are 59.7 emu/g for Ni0.5Zn0.5Fe2O4 and 57.1 emu/g for Ni0.5Zn0.3Co0.2Fe2O4. The coercivity of the samples is found to be much larger than that of bulk ferrites and increases with Co introduction. The Curie temperature tends to increase upon Zn substitution by Co, as well. The temperature dependences of magnetization measured using zero-field cooled and field cooled protocols exhibit large spin frustration and spin-glass-like behavior.

Substitution of ceramics for high temperature alloys. [advantages of using silicon carbides and silicon nitrides in gas turbine engines

NASA Technical Reports Server (NTRS)

Probst, H. B.

1978-01-01

The high temperature capability of ceramics such as silicon nitride and silicon carbide can result in turbine engines of improved efficiency. Other advantages when compared to the nickel and cobalt alloys in current use are raw material availability, lower weight, erosion/corrosion resistance, and potentially lower cost. The use of ceramics in three different sizes of gas turbine is considered; these are the large utility turbines, advanced aircraft turbines, and small automotive turbines. Special consideration, unique to each of these applications, arise when one considers substituting ceramics for high temperature alloys. The effects of material substitutions are reviewed in terms of engine performance, operating economy, and secondary effects.

Near total magnetic moment compensation with high Curie temperature in Mn2V0.5Co0.5Z (Z  =  Ga,Al) Heusler alloys

NASA Astrophysics Data System (ADS)

Midhunlal, P. V.; Arout Chelvane, J.; Arjun Krishnan, U. M.; Prabhu, D.; Gopalan, R.; Kumar, N. Harish

2018-02-01

Mn2V1-x Co x Z (Z  =  Ga,Al and x  =  0, 0.25, 0.5, 0.75, 1) Heusler alloys have been synthesized to investigate the effect of Co substitution at the V site on the magnetic moment and Curie temperature of half-metallic ferrimagnets Mn2VGa and Mn2VAl. Near total magnetic moment compensation was achieved with high Curie temperature for x  =  0.5 composition. The Co substituted alloys show a non linear decrease in lattice parameter without altering the crystal structure of the parent alloys. The end members Mn2VGa and Mn2CoGa have the saturation magnetization of 1.80 µ B/f.u. and 2.05 µ B/f.u. respectively whereas for the Mn2V0.5Co0.5Ga alloy, a near total magnetic moment compensation (0.10 µ B/f.u.) was observed due to the ferrimagnetic coupling of Mn with parallelly aligned V and Co. The Co substituted Mn2VAl has also shown a similar trend with compensated magnetic moment value of 0.06 µ B/f.u. for x  =  0.5. The Curie temperatures of the alloys including the x  =  0.5 composition are well above the room temperature (more than 650 K) which is in sharp contrast to the earlier reported values of 171 K for the (MnCo)VGa and 105 K for the (MnCo)VAl (substitution at the Mn site). The observed T C values are highest among the Mn2V based fully compensated ferrimagnets. The magnetic moment compensation without significant reduction in T C indicates that the V site substitution of Co does not weaken the magnetic interaction in Mn2VZ (Z  =  Ga,Al) alloys which is contrary to the earlier experimental reports on Mn site substitution.

Reducing Mg Acceptor Activation-Energy in Al0.83Ga0.17N Disorder Alloy Substituted by Nanoscale (AlN)5/(GaN)1 Superlattice Using MgGa δ-Doping: Mg Local-Structure Effect

PubMed Central

Zhong, Hong-xia; Shi, Jun-jie; Zhang, Min; Jiang, Xin-he; Huang, Pu; Ding, Yi-min

2014-01-01

Improving p-type doping efficiency in Al-rich AlGaN alloys is a worldwide problem for the realization of AlGaN-based deep ultraviolet optoelectronic devices. In order to solve this problem, we calculate Mg acceptor activation energy and investigate its relationship with Mg local structure in nanoscale (AlN)5/(GaN)1 superlattice (SL), a substitution for Al0.83Ga0.17N disorder alloy, using first-principles calculations. A universal picture to reduce acceptor activation energy in wide-gap semiconductors is given for the first time. By reducing the volume of the acceptor local structure slightly, its activation energy can be decreased remarkably. Our results show that Mg acceptor activation energy can be reduced significantly from 0.44 eV in Al0.83Ga0.17N disorder alloy to 0.26 eV, very close to the Mg acceptor activation energy in GaN, and a high hole concentration in the order of 1019 cm−3 can be obtained in (AlN)5/(GaN)1 SL by MgGa δ-doping owing to GaN-monolayer modulation. We thus open up a new way to reduce Mg acceptor activation energy and increase hole concentration in Al-rich AlGaN. PMID:25338639

Molecular design of cage iron(II) and cobalt(II,III) complexes with a second fluorine-enriched superhydrophobic shell.

PubMed

Belov, Alexander S; Zelinskii, Genrikh E; Varzatskii, Oleg A; Belaya, Irina G; Vologzhanina, Anna V; Dolganov, Alexander V; Novikov, Valentin V; Voloshin, Yan Z

2015-02-28

Pentafluorophenylboron-capped iron and cobalt(II) hexachloroclathrochelate precursors were obtained by the one-pot template condensation of dichloroglyoxime with pentafluorophenylboronic acid on iron and cobalt(II) ions under vigorous reaction conditions in trifluoroacetic acid media. These reactive precursors easily undergo nucleophilic substitution with (per)fluoroarylthiolate anions, giving (per)fluoroarylsulfide macrobicyclic complexes with encapsulated iron and cobalt(II) ions; nucleophilic substitution of the cobalt(II) hexachloroclathrochelate precursor with a pentafluorophenylsulfide anion gave the target hexasulfide monoclathrochelate and the mixed-valence Co(III)Co(II)Co(III) bis-clathrochelate as a side product. The complexes obtained were characterized using elemental analysis, MALDI-TOF mass spectrometry, IR, UV-Vis, (57)Fe Mössbauer (for the X-rayed iron complexes), (1)H, (11)B, (13)C and (19)F NMR spectroscopies and by X-ray diffraction; their redox and electrocatalytic behaviors were studied using cyclic voltammetry and gas chromatography. As can be seen from the single-crystal X-ray diffraction data, the second superhydrophobic shell of such caged metal ions is formed by fluorine atoms of both the apical and ribbed (per)fluoroaryl peripheral groups. The main bond distances and chelate N=C-C=N angles in their molecules are similar, but rotational elongation (contraction) along the molecular C3-pseudoaxes, accompanied by changes in the geometry of the corresponding MN6-coordination polyhedra from a trigonal prism to a trigonal antiprism, allowed encapsulating Fe(2+), Co(2+) and Co(3+) ions. The nature of an encapsulated metal ion and its oxidation state affect the M-N bond lengths, and, for cobalt(ii) clathrochelate with an electronic configuration d(7) the Jahn-Teller structural effect is observed as an alternation of the Co-N distances. Pentafluorophenylboron-capped hexachloroclathrochelate precursors, giving stable catalytically active metal(I)-containing intermediates due to the electron-withdrawing effect of their six ribbed chlorine substituents, were found to show moderate electrocatalytic activity in a 2H(+)/H2 hydrogen-forming reaction. In the case of their ribbed-functionalized sulfide derivatives, the strong electron-withdrawing (per)fluoroaryl groups do not stabilize the reduced electrocatalytically active metal(i)-containing species as their mesomeric effect is absent or substantially decreased by steric hindrances between them.

Electrospinning preparation, characterization and magnetic properties of cobalt-nickel ferrite (Co(1-x)Ni(x)Fe2)O4) nanofibers.

PubMed

Xiang, Jun; Chu, Yanqiu; Shen, Xiangqian; Zhou, Guangzhen; Guo, Yintao

2012-06-15

Uniform Co(1-)(x)Ni(x)Fe(2)O(4) (x=0.0, 0.2, 0.4, 0.6, 0.8 and 1.0) nanofibers with average diameter of 110 nm and length up to several millimeters were prepared by calcination of electrospun precursor nanofibers containing polymer and inorganic salts. The as-spun and calcined nanofibers were characterized in detail by TG-DTA, XRD, FE-SEM, TEM, SAED and VSM, respectively. The effect of composition of the nanofibers on the structure and magnetic properties were investigated. The nanofibers are formed through assembling magnetic nanoparticles with poly(vinyl pyrrolidone) as the structure-directing template. The structural characteristics and magnetic properties of the resultant nanofibers vary with chemical composition and can be tuned by adjusting the Co/Ni ratio. Both lattice parameter and particle size decrease gradually with increasing nickel concentration. The saturation magnetization and coercivity lie in the range 29.3-56.4 emu/g and 210-1255 Oe, respectively, and both show a monotonously decreasing behavior with the increase in nickel concentration. Such changes in magnetic properties can mainly be attributed to the lower magnetocrystalline anisotropy and the smaller magnetic moment of Ni(2+) ions compared to Co(2+) ions. Furthermore, the coercivity of Co-Ni ferrite nanofibers is found to be superior to that of the corresponding nanoparticle counterparts, presumably due to their large shape anisotropy. These novel one-dimensional Co-Ni ferrite magnetic nanofibers can potentially be used in micro-/nanoelectronic devices, microwave absorbers and sensing devices. Copyright © 2012 Elsevier Inc. All rights reserved.

Structural, optical and dielectric properties of transition metal (MFe2O4; M = Co, Ni and Zn) nanoferrites

NASA Astrophysics Data System (ADS)

Chand, Prakash; Vaish, Swapnil; Kumar, Praveen

2017-11-01

In the present work, transition metal spinel ferrite (MFe2O4; M = Co, Ni, Zn) nanostructures synthesized by chemical co-precipitation method. XRD analysis confirms the formation of cubic spinel-type structure with space group Fd3m and the average crystallite size calculated by Scherrer's formula found to be in 9-14 nm range. Scanning electron microscopy was used to study surface morphology of the samples. Moreover, Raman and PL spectra also confirm the formation of the cubic structure. The Raman spectra measured on cobalt, nickel and zinc ferrite revealed a larger number of phonon bands than expected for the cubic spinel structure. The calculated optical energy band gaps, obtained by Tauc's relation from UV-Vis absorption spectra are found to be as 2.44, 3.54 and 3.25 eV for CoFe2O4, NiFe2O4&ZnFe2O, respectively. The analysis of the complex impedance spectra of all ferrites samples shows the presence of one semicircular arc at all selected temperatures, signifying a key role of the grain boundary contribution. The dielectric constants (ε ‧) were measured in the frequency range from 10 Hz to 5 MHz at different temperatures and is found to be decreased suddenly with an increase in frequency and maintain a steady state or constant at higher frequencies for all the three samples. The AC conductivity is found to be increased with frequency and temperature of all the three samples which is explained on the basis of Koop's phenomenological theory.

Superconductivity in gallium-substituted Ba8Si46 clathrates

NASA Astrophysics Data System (ADS)

Li, Yang; Zhang, Ruihong; Liu, Yang; Chen, Ning; Luo, Z. P.; Ma, Xingqiao; Cao, Guohui; Feng, Z. S.; Hu, Chia-Ren; Ross, Joseph H., Jr.

2007-02-01

We report a joint experimental and theoretical investigation of superconductivity in Ga-substituted type-I silicon clathrates. We prepared samples of the general formula Ba8Si46-xGax , with different values of x . We show that Ba8Si40Ga6 is a bulk superconductor, with an onset at TC≈3.3K . For x=10 and higher, no superconductivity was observed down to T=1.8K . This represents a strong suppression of superconductivity with increasing Ga content, compared to Ba8Si46 with TC≈8K . Suppression of superconductivity can be attributed primarily to a decrease in the density of states at the Fermi level, caused by a reduced integrity of the sp3 -hybridized networks as well as the lowering of carrier concentration. These results are corroborated by first-principles calculations, which show that Ga substitution results in a large decrease of the electronic density of states at the Fermi level, which explains the decreased superconducting critical temperature within the BCS framework. To further characterize the superconducting state, we carried out magnetic measurements showing Ba8Si40Ga6 to be a type-II superconductor. The critical magnetic fields were measured to be HC1≈35Oe and HC2≈8.5kOe . We deduce the London penetration depth λ≈3700Å and the coherence length ξc≈200Å . Our estimate of the electron-phonon coupling reveals that Ba8Si40Ga6 is a moderate phonon-mediated BCS superconductor.

Assessment of thyroid endocrine system impairment and oxidative stress mediated by cobalt ferrite (CoFe2 O4 ) nanoparticles in zebrafish larvae.

PubMed

Ahmad, Farooq; Liu, Xiaoyi; Zhou, Ying; Yao, Hongzhou; Zhao, Fangfang; Ling, Zhaoxing; Xu, Chao

2016-12-01

Fascinating super paramagnetic uniqueness of iron oxide particles at nano-scale level make them extremely useful in the state of the art therapies, equipments, and techniques. Cobalt ferrite (CoFe 2 O 4 ) magnetic nanoparticles (MNPs) are extensively used in nano-based medicine and electronics, results in extensive discharge and accumulation into the environment. However, very limited information is available for their endocrine disrupting potential in aquatic organisms. In this study, the thyroid endocrine disrupting ability of CoFe 2 O 4 NPs in Zebrafish larvae for 168-h post fertilization (hpf) was evaluated. The results showed the elevated amounts of T4 and T3 hormones by malformation of hypothalamus pituitary axis in zebrafish larvae. These elevated levels of whole body THs leads to delayed hatching, head and eye malformation, arrested development, and alterations in metabolism. The influence of THs disruption on ROS production and change in activities of catalase (CAT), mu-glutathione s-transferase (mu-GST), and acid phosphatase (AP) were also studied. The production of significantly higher amounts of in vivo generation of ROS leads to membrane damage and oxidative stress. Presences of NPs and NPs agglomerates/aggregates were also the contributing factors in mechanical damaging the membranes and physiological structure of thyroid axis. The increased activities of CAT, mu-GST, and AP confirmed the increased oxidative stress, possible DNA, and metabolic alterations, respectively. The excessive production of in vivo ROS leads to severe apoptosis in head, eye, and heart region confirming that malformation leads to malfunctioning of hypothalamus pituitary axis. ROS-induced oxidative DNA damage by formation of 8-OHdG DNA adducts elaborates the genotoxicity potential of CoFe 2 O 4 NPs. This study will help us to better understand the risk and assessment of endocrine disrupting potential of nanoparticles. © 2015 Wiley Periodicals, Inc. Environ Toxicol 31: 2068-2080, 2016. © 2015 Wiley Periodicals, Inc.

Visible light driven photocatalytic degradation of rhodamine B using Mg doped cobalt ferrite spinel nanoparticles synthesized by microwave combustion method

NASA Astrophysics Data System (ADS)

Sundararajan, M.; John Kennedy, L.; Nithya, P.; Judith Vijaya, J.; Bououdina, M.

2017-09-01

Co1-xMgxFe2O4 (0≤x≤0.5) spinel nanoparticles were synthesized by a simple microwave combustion method. The characterization of the samples were performed using X-ray diffraction (XRD) analysis, scanning electron (SEM) microscopy, energy dispersive X-ray (EDX) analysis, UV-visible and diffuse reflectance (DRS) spectroscopy, photoluminescence (PL) spectroscopy, Fourier transformed infrared (FT-IR) spectroscopy and vibrating sample magnetometry (VSM) analysis. The XRD patterns indicate the formation of cubic inverse spinel structure. The calculated average crystallite size using Debye Scherrer's equation is found to be around 46-38 nm. The morphology of spinel nanoparticles was observed from SEM images and the elemental mapping of magnesium doped cobalt ferrite was obtained by using energy dispersive X-ray technique. Optical studies were carried out for the deeper understanding of the conduction band (CB) and valence band (VB) edges of the synthesized nanoparticles. The intrinsic stretching vibrations of Fe3+-O2- in tetrahedral sites leads to the appearance of IR band at around 573 cm-1. The magnetic properties such as remanence magnetization (Mr), coercivity (Hc) and saturation magnetization (Ms) were calculated from the hysteresis curves. The maximum photocatalytic degradation efficiency for Co0.6Mg0.4Fe2O4 is around (99.5%) when compared to that of CoFe2O4 whose efficiency is around (73.0%). The improvement in photocatalytic degradation efficiency is due to the effective separation and prevention of electron-hole pair recombination. The R2 values for the first order rate kinetics are found to be better than R2 values for the second order rate kinetics and this proves that photocatalytic degradation of RhB dye follows first order kinetics. The probable mechanism for the photocatalytic degradation of RhB dye is proposed.

Cobalt ferrite sphere-coated buckhorn-like barium titanate: Fabrication, characterization, its dielectric resonance, and microwave attenuation properties

NASA Astrophysics Data System (ADS)

Ji, Renlong; Cao, Chuanbao

2014-10-01

Barium titanate (BTO) with different morphology is prepared through hydrothermal method using titania spheres as precursor, then calcined at different temperatures and ultimately coated with cobalt ferrite (BTO/CFO). The dielectric dispersion of the composite containing BTO (75 wt. % ratio in paraffin wax) shows evidence of resonance behaviour in the microwave spectrum, rather than the usually observed relaxation mode. The imaginary part of permittivity (ɛ″) displays a strong peak in the 10-13 GHz frequency region, especially for buckhorn-like BTO (hydrothermally synthesized at 110 °C and calcined at 1100 °C). The dielectric response anomaly of BTO in special morphology is due to the emission of plane acoustic waves caused by electrostrictive and converse piezoelectric effects. An accepted model is adopted to simulate the resonance frequency. The minimum reflection loss of cauliflower-like BTO (hydrothermally synthesized at 110 °C, then calcined at 600 °C for 2 h, 75 wt. % ratio) in paraffin wax reaches -30.831 dB at 10.56 GHz with a matching thickness of 2 mm, lower than all the reported values. When the sintering temperature is changed to 1100 °C (buckhorn-like BTO), the minimum reflection loss value is -24.37 dB at 12.56 GHz under the thickness of 3 mm. After combination with CFO, the value reaches -42.677 dB when the thickness is 5.6 mm. The ginger-like BTO (hydrothermally synthesized at 200 °C and calcined at different temperatures) is inferior in microwave reflection reduction. The electromagnetic interference shielding effectiveness of buckhorn-like BTO composite is calculated to be -12.7 dB (94.6% shielding) at resonance frequency (2 mm, 11.52 GHz). This work clearly shows the potential to tune the dielectric property of ferroelectrics through control of morphology, facilitating new comprehension of the ferroelectrics in microwave regime.

Preparation, Structural Characterization and Magnetic Properties of La-SUBSTITUTED co Ferrites via a Modified Citrate Precursor Route

NASA Astrophysics Data System (ADS)

Ai, Lunhong; Jiang, Jing

CoLaxFe2-xO4 (x = 0.00, 0.05 and 0.1) nanoparticles were prepared simply by a modified citrate precursor route. Effects of La-substituting level on the their magnetic properties were investigated on the basis of the structural analysis. The thermal evolution of the precursor, as well as the microstructure of as-prepared products were studied by means of a thermogravimetric analyzer (TGA), X-ray diffractometer (XRD) and Fourier transform infrared (FTIR) spectrometer. The magnetic properties of the as-prepared samples were measured using a vibrating sample magnetometer (VSM). It was found that the magnetic properties were dependent on many factors such as La-substituting level, particle size and microstructure. The observed saturation magnetization decreased with increasing La content, whereas coercivity exhibited reverse behavior.

Novel solution-phase structures of gallium-containing pyrogallol[4]arene scaffolds**

PubMed Central

Kumari, Harshita; Kline, Steven R.; Wycoff, Wei G.; Paul, Rick L.; Mossine, Andrew V.; Deakyne, Carol A.; Atwood, Jerry L.

2012-01-01

The variations in architecture of gallium-seamed (PgC4Ga) and gallium-zinc-seamed (PgC4GaZn) C-butylpyrogallol[4]arene nanoassemblies in solution (SANS/NMR) versus the solid state (XRD) have been investigated. Rearrangement from the solid-state spheroidal to the solution-phase toroidal shape differentiates the gallium-containing pyrogallol[4]arene nanoassemblies from all other PgCnM nanocapsules studied thus far. Different structural arrangements of the metals and arenes of PgC4Ga versus PgC4GaZn have been deduced from the different toroidal dimensions, C–H proton environments and guest encapsulation of the two toroids. PGAA of mixed-metal hexamers reveals a decrease in gallium-to-metal ratio as the second metal varies from cobalt to zinc. Overall, the combined study demonstrates the versatility of gallium in directing the self-assembly of pyrogallol[4]arenes into novel nanoarchitectures. PMID:22511521

Magnetic properties and structural characterization of layered (Cr0.5Mn0.5)2AuC synthesized by thermally induced substitutional reaction in (Cr0.5Mn0.5)2GaC

NASA Astrophysics Data System (ADS)

Lai, Chung-Chuan; Tao, Quanzheng; Fashandi, Hossein; Wiedwald, Ulf; Salikhov, Ruslan; Farle, Michael; Petruhins, Andrejs; Lu, Jun; Hultman, Lars; Eklund, Per; Rosen, Johanna

2018-02-01

The magnetic properties of the new phase (Cr0.5Mn0.5)2AuC are compared to the known MAX-phase (Cr0.5Mn0.5)2GaC, where the former was synthesized by thermally induced substitution reaction of Au for Ga in (Cr0.5Mn0.5)2GaC. The reaction introduced a lattice expansion of ˜3% along the c-axis, an enhancement of the coercive field from 30 mT to 140 mT, and a reduction of the Curie temperature and the saturation magnetization. Still, (Cr0.5Mn0.5)2AuC displays similar features in the magnetic field- and temperature-dependent magnetization curves as previously reported magnetic MAX phases, e.g., (Cr0.5Mn0.5)2GaC and (Mo0.5Mn0.5)2GaC. The work suggests a pathway for tuning the magnetic properties of MAX phases.

Anisotropic polaron localization and spontaneous symmetry breaking: Comparison of cation-site acceptors in GaN and ZnO

NASA Astrophysics Data System (ADS)

Sun, Y. Y.; Abtew, Tesfaye A.; Zhang, Peihong; Zhang, S. B.

2014-10-01

The behavior of cation substitutional hole doping in GaN and ZnO is investigated using hybrid density functional calculations. Our results reveal that Mg substitution for Ga (MgGa) in GaN can assume three different configurations. Two of the configurations are characterized by the formation of defect-bound small polaron (i.e., a large structural distortion accompanied by hole localization on one of the neighboring N atoms). The third one has a relatively small but significant distortion that is characterized by highly anisotropic polaron localization. In this third configuration, MgGa exhibits both effective-mass-like and noneffective-mass-like characters. In contrast, a similar defect in ZnO, LiZn, cannot sustain the anisotropic polaron in the hybrid functional calculation, but undergoes spontaneous breaking of a mirror symmetry through a mechanism driven by the hole localization. Finally, using NaZn in ZnO as an example, we show that the deep acceptor levels of the small-polaron defects could be made shallower by applying compressive strain to the material.

Growth of self-textured Ga3+-substituted Li7La3Zr2O12 ceramics by solid state reaction and their significant enhancement in ionic conductivity

NASA Astrophysics Data System (ADS)

Qin, Shiying; Zhu, Xiaohong; Jiang, Yue; Ling, Ming'en; Hu, Zhiwei; Zhu, Jiliang

2018-03-01

A highly self-textured Ga2O3-substituted Li7La3Zr2O12 (LLZO-Ga) solid electrolyte with a nominal composition of Li6.55Ga0.15La3Zr2O12 is obtained by a simple and low-cost solid-state reaction technique, requiring no seed crystals to achieve grain orientation. The as-prepared self-textured LLZO-Ga shows a strong (420) preferred orientation with a high Lotgering factor of 0.91. Coherently, a terrace-shaped microstructure consisting of many parallel layers, indicating a two-dimensional-like growth mode, is clearly observed in the self-textured sample. As a result, the highly self-textured garnet-type lithium-ion conducting solid electrolyte of LLZO-Ga exhibits an extremely high ionic conductivity, reaching a state-of-the-art level of 2.06 × 10-3 S cm-1 at room temperature (25 °C) and thus shedding light on an important strategy for improving the structure and ionic conductivity of solid electrolytes.

Water reduction by a p-GaInP2 photoelectrode stabilized by an amorphous TiO2 coating and a molecular cobalt catalyst

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gu, Jing; Yan, Yong; Young, James L.

2015-12-21

Producing hydrogen through solar water splitting requires the coverage of large land areas. Abundant metal-based molecular catalysts offer scalability, but only if they match noble metal activities. We report on a highly active p-GaInP2 photocathode protected through a 35-nm TiO2 layer functionalized by a cobaloxime molecular catalyst (GaInP2-TiO2-cobaloxime). This photoelectrode mediates H2 production with a current density of ~9"0mA"0cm-2 at a potential of 0"0V versus RHE under 1-sun illumination at pH"013. The calculated turnover number for the catalyst during a 20-h period is 139,000, with an average turnover frequency of 1.9"0s-1. Bare GaInP2 shows a rapid current decay, whereas themore » GaInP2-TiO2-cobaloxime electrode shows« less

Influence of ferrite phase in alite-calcium sulfoaluminate cements

NASA Astrophysics Data System (ADS)

Duvallet, Tristana Yvonne Francoise

Since the energy crisis in 1970's, research on low energy cements with low CO2- emissions has been increasing. Numerous solutions have been investigated, and the goal of this original research is to create a viable hybrid cement with the components of both Ordinary Portland cement (OPC) and calcium sulfoaluminate cement (CSAC), by forming a material that contains both alite and calcium sulfoaluminate clinker phases. Furthermore, this research focuses on keeping the cost of this material reasonable by reducing aluminum requirements through its substitution with iron. The aim of this work would produce a cement that can use large amounts of red mud, which is a plentiful waste material, in place of bauxite known as an expensive raw material. Modified Bogue equations were established and tested to formulate this novel cement with different amounts of ferrite, from 5% to 45% by weight. This was followed by the production of cement from reagent chemicals, and from industrial by-products as feedstocks (fly ash, red mud and slag). Hydration processes, as well as the mechanical properties, of these clinker compositions were studied, along with the addition of gypsum and the impact of a ferric iron complexing additive triisopropanolamine (TIPA). To summarize this research, the influence of the addition of 5-45% by weight of ferrite phase, was examined with the goal of introducing as much red mud as possible in the process without negatively attenuate the cement properties. Based on this PhD dissertation, the production of high-iron alite-calcium sulfoaluminateferrite cements was proven possible from the two sources of raw materials. The hydration processes and the mechanical properties seemed negatively affected by the addition of ferrite, as this phase was not hydrated entirely, even after 6 months of curing. The usage of TIPA counteracted this decline in strength by improving the ferrite hydration and increasing the optimum amount of gypsum required in each composition. The mechanical data were equivalent to OPC strengths for some compositions with 25% ferrite. This preliminary work constitutes the first research phase of this novel cement and requires additional research for its improvement. Topics for additional research are identified in this dissertation. KEYWORDS: alite, calcium sulfoaluminate, ferrite, low-energy cement, triisopropanolamine.

Oxidation behaviour and electrical properties of cobalt/cerium oxide composite coatings for solid oxide fuel cell interconnects

NASA Astrophysics Data System (ADS)

Harthøj, Anders; Holt, Tobias; Møller, Per

2015-05-01

This work evaluates the performance of cobalt/cerium oxide (Co/CeO2) composite coatings and pure Co coatings to be used for solid oxide fuel cell (SOFC) interconnects. The coatings are electroplated on the ferritic stainless steels Crofer 22 APU and Crofer 22H. Coated and uncoated samples are exposed in air at 800 °C for 3000 h and oxidation rates are measured and oxide scale microstructures are investigated. Area-specific resistances (ASR) in air at 850 °C of coated and uncoated samples are also measured. A dual layered oxide scale formed on all coated samples. The outer layer consisted of Co, Mn, Fe and Cr oxide and the inner layer consisted of Cr oxide. The CeO2 was present as discrete particles in the outer oxide layer after exposure. The Cr oxide layer thicknesses and oxidations rates were significantly reduced for Co/CeO2 coated samples compared to for Co coated and uncoated samples. The ASR of all Crofer 22H samples increased significantly faster than of Crofer 22 APU samples which was likely due to the presence of SiO2 in the oxide/metal interface of Crofer 22H.

A status review of NASA's COSAM (Conservation Of Strategic Aerospace Materials) program

NASA Technical Reports Server (NTRS)

Stephens, J. R.

1982-01-01

The use and supply of strategic elements in nickel base superalloys for gas turbine engines are reviewed. Substitution of strategic elements, advanced processing concepts, and the identification of alternate materials are considered. Cobalt, tantalum, columbium, and chromium, the supplies of which are 91-100% imported, are the materials of major concern.

Dielectric studies of (x) NiFe2O4 + (1 - x) BaTi0.9Zr0.1O3 (where x = 0, 0.25, 0.50, 0.75 and 1)

NASA Astrophysics Data System (ADS)

Wadhwani, Kiran; Srivastava, Subodh; Mathur, Shubhra

2018-05-01

We present the room temperature dielectric studies of the samples in the series (x) NiFe2O4 + (1-x) BaTi0.9Zr0.1O3 (where x = 0, 0.25, 0.50, 0.75 and 1) containing nickel ferrite and Zr substituted barium titanate as the ferroelectric phase and their magnetoelectric (ME) composites in mixed in different molar ratios. Solid state diffusion has been used for the synthesis of samples. Powder X-ray diffraction (XRD) confirms the formation of ferrite and ferroelectric phases and their presence in all three composites with no impurity traces. Room temperature dielectric measurements have been made as a function of frequency (ranging from 100 Hz to 1 MHz).

Growth and Proteome Response of Temperate and Polar Diatoms Thalassiosira pseudonana and Chaetoceros sp. to variations in Cobalt and Zinc: Identification of the High-Affinity Zinc Transporter and Potential for Use as a Biomarker

NASA Astrophysics Data System (ADS)

Kellogg, M. M.; Moran, D. M.; McIlvin, M. R.; Allen, A. E.; Saito, M. A.

2016-02-01

Marine diatoms such as the temperate Thalassiosira pseudonana (Tp) and the polar Chaetoceros sp (Ch) are known to be important contributors to marine primary productivity and the global carbon cycle. The nutritional use of zinc (Zn) in diatoms and the ability to substitute cobalt (Co) for Zn has been previously demonstrated to be of importance in their growth and biochemistry. We conducted physiological experiments with Zn and Co on these diatoms and analyzed their proteomic response. Growth studies involving Tp confirmed previous studies' findings showing Zn/Co substitution, while studies on Ch showed a toxic response to high Zn abundances. Proteome responses of Tp to Zn limitation identified a putative and previously unidentified transporter that was undetectable at high Zn concentration and became highly abundant at two lower Zn concentrations. The distribution of this protein in nature and its potential use as a Zn stress biomarker in diatoms will be discussed.

Diastereoselective Radical‐Type Cyclopropanation of Electron‐Deficient Alkenes Mediated by the Highly Active Cobalt(II) Tetramethyltetraaza[14]annulene Catalyst

PubMed Central

Chirila, Andrei; Gopal Das, Braja; Paul, Nanda D.

2017-01-01

Abstract A new protocol for the catalytic synthesis of cyclopropanes using electron‐deficient alkenes is presented, which is catalysed by a series of affordable, easy to synthesise and highly active substituted cobalt(II) tetraaza[14]annulenes. These catalysts are compatible with the use of sodium tosylhydrazone salts as precursors to diazo compounds in one‐pot catalytic transformations to afford the desired cyclopropanes in almost quantitative yields. The reaction takes advantage of the metalloradical character of the Co complexes to activate the diazo compounds. The reaction is practical and fast, and proceeds from readily available starting materials. It does not require the slow addition of diazo reagents or tosylhydrazone salts or heating and tolerates many solvents, which include protic ones such as MeOH. The CoII complexes derived from the tetramethyltetraaza[14]annulene ligand are easier to prepare than cobalt(II) porphyrins and present a similar catalytic carbene radical reactivity but are more active. The reaction proceeds at 20 °C in a matter of minutes and even at −78 °C in a few hours. The catalytic system is robust and can operate with either the alkene or the diazo reagent as the limiting reagent, which inhibits the dimerisation of diazo compounds totally. The protocol has been applied to synthesise a variety of substituted cyclopropanes. High yields and selectivities were achieved for various substrates with an intrinsic preference for trans cyclopropanes. PMID:28529668

Local crystal/chemical structures at iron sites in amorphous, magnetic, and nanocrystalline materials

NASA Astrophysics Data System (ADS)

Clark, Ted Michael

Order-disorder phenomena have been examined by means of Mossbauer spectroscopy in a variety of materials, including (a) tektites and other silicate glasses, (b) magnetic materials such as natural and synthetic magnetoplumbite, M-type hexagonal ferrites and magnetite, and (c) nanocrystalline zinc ferrite. A methodology has been established for the analysis of the local crystal/chemical structures of iron in tektites and its application has reconfirmed a low ferric/ferrous ratio of approximately 0.10 for tektites. Additionally, a greater degree of submirocscopic heterogeneity has been established for Muong Nong tektites in comparison with splash form tektites. The dynamics of the 2b site in hexagonal ferrites has been studied above and below the Curie temperature for magnetoplumbite and its synthetic analogs, and also for polycrystalline and oriented single-crystals of MeFesb{12}Osb{19} (Me=Ba, Sr, Pb). Cation ordering on this site is shown to be dependent on the thermal history of the material, while the dynamic disorder of the 2b site for the end-member hexagonal ferrites is shown to be influenced by the divalent heavy metal species, Me. The influence of chemical composition on the morphology of magnetite has been shown to depend on the site preference of impurity cations: Substitutional impurities with tetrahedral site preferences are postulated to result in the seldom-observed cubic habit. Based on the cation distributions of bulk and nanocrystalline material it is held that the enhanced magnetic moments and susceptibilities of nanocrystalline zinc ferrite are shown to be consistent with surface phenomena, independent of synthesis methodology, and contrary to claims of special effects resulting from a particular synthesis methodology.

Cation disorder in Ga1212.

PubMed

Greenwood, K B; Ko, D; Vander Griend, D A; Sarjeant, G M; Milgram, J W; Garrity, E S; DeLoach, D I; Poeppelmeier, K R; Salvador, P A; Mason, T O

2000-07-24

Substitution of calcium for strontium in LnSr2-xCaxCu2GaO7 (Ln = La, Pr, Nd, Gd, Ho, Er, Tm, and Yb) materials at ambient pressure and 975 degrees C results in complete substitution of calcium for strontium in the lanthanum and praseodymium systems and partial substitution in the other lanthanide systems. The calcium saturation level depends on the size of the Ln cation, and in all cases, a decrease in the lattice parameters with calcium concentration was observed until a common, lower bound, average A-cation size is reached. Site occupancies from X-ray and neutron diffraction experiments for LnSr2-xCaxCu2GaO7 (x = 0 and x = 2) confirm that the A-cations distribute between the two blocking-layer sites and the active-layer site based on size. A quantitative link between cation distribution and relative site-specific cation enthalpy for calcium, strontium, and lanthanum within the gallate structure is derived. The cation distribution in other similar materials can potentially be modeled.