Diffusion of Oxygen Isotopes in Thermally Evolving Planetesimals and Size Ranges of Presolar Silicate Grains

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wakita, Shigeru; Nozawa, Takaya; Hasegawa, Yasuhiro, E-mail: shigeru@cfca.jp

Presolar grains are small particles found in meteorites through their isotopic compositions, which are considerably different from those of materials in the solar system. If some isotopes in presolar grains diffused out beyond their grain sizes when they were embedded in parent bodies of meteorites, their isotopic compositions could be washed out, and hence the grains could no longer be identified as presolar grains. We explore this possibility for the first time by self-consistently simulating the thermal evolution of planetesimals and the diffusion length of {sup 18}O in presolar silicate grains. Our results show that presolar silicate grains smaller thanmore » ∼0.03 μ m cannot keep their original isotopic compositions even if the host planetesimals experienced a maximum temperature as low as 600 °C. Since this temperature corresponds to that experienced by petrologic type 3 chondrites, isotopic diffusion can constrain the size of presolar silicate grains discovered in such chondrites to be larger than ∼0.03 μ m. We also find that the diffusion length of {sup 18}O reaches ∼0.3–2 μ m in planetesimals that were heated up to 700–800°C. This indicates that, if the original size of presolar grains spans a range from ∼0.001 μ m to ∼0.3 μ m like that in the interstellar medium, then the isotopic records of the presolar grains may be almost completely lost in such highly thermalized parent bodies. We propose that isotopic diffusion could be a key process to control the size distribution and abundance of presolar grains in some types of chondrites.« less

The effect of grain size and surface area on organic matter, lignin and carbohydrate concentration, and molecular compositions in Peru Margin sediments

USGS Publications Warehouse

Bergamaschi, B.A.; Tsamakis, E.; Keil, R.G.; Eglinton, T.I.; Montlucon, D.B.; Hedges, J.I.

1997-01-01

A C-rich sediment sample from the Peru Margin was sorted into nine hydrodynamically-determined grain size fractions to explore the effect of grain size distribution and sediment surface area on organic matter content and composition. The neutral monomeric carbohydrate composition, lignin oxidation product yields, total organic carbon, and total nitrogen contents were determined independently for each size fraction, in addition to sediment surface area and abundance of biogenic opal. The percent organic carbon and percent total nitrogen were strongly related to surface area in these sediments. In turn, the distribution of surface area closely followed mass distribution among the textural size classes, suggesting hydrodynamic controls on grain size also control organic carbon content. Nevertheless, organic compositional distinctions were observed between textural size classes. Total neutral carbohydrate yields in the Peru Margin sediments were found to closely parallel trends in total organic carbon, increasing in abundance among grain size fractions in proportion to sediment surface area. Coincident with the increases in absolute abundance, rhamnose and mannose increased as a fraction of the total carbohydrate yield in concert with surface area, indicating these monomers were preferentially represented in carbohydrates associated with surfaces. Lignin oxidation product yields varied with surface area when normalized to organic carbon, suggesting that the terrestrially-derived component may be diluted by sorption of marine derived material. Lignin-based parameters suggest a separate source for terrestrially derived material associated with sand-size material as opposed to that associated with silts and clays. Copyright ?? 1997 Elsevier Science Ltd.

The effect of grain size and surface area on organic matter, lignin and carbohydrate concentration, and molecular compositions in Peru Margin sediments

NASA Astrophysics Data System (ADS)

Bergamaschi, Brian A.; Tsamakis, Elizabeth; Keil, Richard G.; Eglinton, Timothy I.; Montluçon, Daniel B.; Hedges, John I.

1997-03-01

A C-rich sediment sample from the Peru Margin was sorted into nine hydrodynamically-determined grain size fractions to explore the effect of grain size distribution and sediment surface area on organic matter content and composition. The neutral monomeric carbohydrate composition, lignin oxidation product yields, total organic carbon, and total nitrogen contents were determined independently for each size fraction, in addition to sediment surface area and abundance of biogenic opal. The percent organic carbon and percent total nitrogen were strongly related to surface area in these sediments. In turn, the distribution of surface area closely followed mass distribution among the textural size classes, suggesting hydrodynamic controls on grain size also control organic carbon content. Nevertheless, organic compositional distinctions were observed between textural size classes. Total neutral carbohydrate yields in the Peru Margin sediments were found to closely parallel trends in total organic carbon, increasing in abundance among grain size fractions in proportion to sediment surface area. Coincident with the increases in absolute abundance, rhamnose and mannose increased as a fraction of the total carbohydrate yield in concert with surface area, indicating these monomers were preferentially represented in carbohydrates associated with surfaces. Lignin oxidation product yields varied with surface area when normalized to organic carbon, suggesting that the terrestrially-derived component may be diluted by sorption of marine derived material. Lignin-based parameters suggest a separate source for terrestrially derived material associated with sand-size material as opposed to that associated with silts and clays.

Investigating the Magneto Electric Coupling of [90 wt%Na0.5Bi0.5TiO3 (NBT)-10 wt% BaFe12O19 (BaM)] novel multiferroiccomposite system by increasing of BaM grain size

NASA Astrophysics Data System (ADS)

Pattanayak, Ranjit; Raut, Subhajit; Kuila, Sourav; Chandrasekhar, Mallam; Panigrahi, Simanchala

2017-02-01

Polycrystalline three novel [90 wt%Na0.5Bi0.5TiO3 (NBT)-10 wt% BaFe12O19 (BaM)] magnetoelctricmultiferroic composite systems were fabricated by considering the variation (increasing) of BaM grain size. The desired formation of composites was confirmed by X-ray diffraction study. The FESEM and SEM study were verified the variation of grain size and 0-3 type connectivity of composite systems. To predict the room temperature multiferroicbehaviour of theses composite systems we were taken PE and MH loop. For investigating the extrinsic and intrinsic magnetoelctric effect magneto impedance spectroscopy was considered for theses composite systems. The variation of intrinsic magnetoelctric coupling was predicted by proposing a simple mechanical model.

Retrieving optical constants of glasses with variable iron abundance

NASA Astrophysics Data System (ADS)

Carli, C.; Roush, T. L.; Capaccioni, F.; Baraldi, A.

2013-12-01

Visible and Near Infrared (VNIR, ~0.4-2.5 μm) spectroscopy is an important tool to explore the surface composition of objects in our Solar System. Using this technique different minerals have been recognized on the surfaces of solar system bodies. One of the principal products of extrusive volcanism and impact cratering is a glassy component, that can be abundant and thus significantly influence the spectral signature of the region investigated. Different types of glasses have been proposed and identified on the lunar surface and in star forming regions near young stellar objects. Here we report an initial effort of retrieving the optical constants of volcanic glasses formed in oxidizing terrestrial-like conditions. We also investigated how those calculations are affected by the grain size distribution. Bidirectional reflectance spectra, obtained with incidence and emission angles of 30° and 0°, respectively, were measured on powders of different grain sizes for four different glassy compositions in the VNIR. Hapke's model of the interaction of light with particulate surfaces was used to determine the imaginary index, k, at each wavelength by iteratively minimizing the difference between measured and calculated reflectance The basic approach to retrieving the optical constants was to use multiple grain sizes of the same sample and assume all grain sizes are compositionally equivalent. Unless independently known as a function of wavelength, an additional assumption must be made regarding the real index of refraction, n. The median size for each particle size separate was adopted for initially estimating k. Then, iterating the Hapke analysis results with a subtractive Kramers-Kronig analysis we were able to determine the wavelength dependence of n. For each composition we used the k-values estimated for all the grain sizes to calculate a mean k-value representing that composition. These values were then used to fit the original spectra by only varying the grain sizes. As a separate estimate of the k-values, we will use transmission measurements in the VNIR. Two slabs, with different thicknesses, will be measured for each composition. These data will be used to determine a k value and a comparison between k values obtained from the two different techniques will be discussed.

Sediment Grain Size Measurements: Is There a Differenc Between Digested and Un-digested Samples? And Does the Organic Carbon of the Sample Play a Role

EPA Science Inventory

Grain size is a physical measurement commonly made in the analysis of many benthic systems. Grain size influences benthic community composition, can influence contaminant loading and can indicate the energy regime of a system. We have recently investigated the relationship betw...

Chemical aspects of agglutinate formation - Relationships between agglutinate composition and the composition of the bulk soil. [lunar surface composition

NASA Technical Reports Server (NTRS)

Via, W. N.; Taylor, L. A.

1976-01-01

Attention is centered on the nature and intensity of geochemical fractionation accompanying agglutination of several size fractions of the immature Apollo-16 soil sample 67460, from North Ray Crater. The soil features coarse mean grain size about 150 microns, low (20 wt.%) magnetic agglutinate content, and a bimodal grain size distribution. The magnetic fraction included both agglutinates and magnetic non-agglutinates (glass-free microbreccias with 30-60 micron native FeNi grains hosted in a matrix of pyroxene, ilmenite, and olivine). The separation process residue contained nonmagnetic agglutinates with compositions near pure plagioclase. The magnetic agglutinate fraction appears selectively enriched in ferromagnesian elements to the partial exclusion of plagioclase elements. Agglutinate glass chemistry based solely on magnetic separation is deprecated on the basis of the results.

Effects of grain size and humidity on fretting wear in fine-grained alumina, Al{sub 2}O{sub 3}/TiC, and zirconia

DOE Office of Scientific and Technical Information (OSTI.GOV)

Krell, A.; Klaffke, D.

Friction and wear of sintered alumina with grain sizes between 0.4 and 3 {micro}m were measured in comparison with Al{sub 2}O{sub 3}/TiC composites and with tetragonal ZrO{sub 2} (3 mol% Y{sub 2}O{sub 3}). The dependence on the grain boundary toughness and residual microstresses is investigated, and a hierarchical order of influencing parameters is observed. In air, reduced alumina grain sizes improve the micromechanical stability of the grain boundaries and the hardness, and reduced wear is governed by microplastic deformation, with few pullout events. Humidity and water slightly reduce the friction of all of the investigated ceramics. In water, this effectmore » reduces the wear of coarser alumina microstructures. The wear of aluminas and of the Al{sub 2}O{sub 3}/TiC composite is similar; it is lower than observed in zirconia, where extended surface cracking occurs at grain sizes as small as 0.3 {micro}m.« less

Application of composite flow laws to grain size distributions derived from polar ice cores

NASA Astrophysics Data System (ADS)

Binder, Tobias; de Bresser, Hans; Jansen, Daniela; Weikusat, Ilka; Garbe, Christoph; Kipfstuhl, Sepp

2014-05-01

Apart from evaluating the crystallographic orientation, focus of microstructural analysis of natural ice during the last decades has been to create depth-profiles of mean grain size. Several ice flow models incorporated mean grain size as a variable. Although such a mean value may coincide well with the size of a large proportion of the grains, smaller/larger grains are effectively ignored. These smaller/larger grains, however, may affect the ice flow modeling. Variability in grain size is observed on centimeter, meter and kilometer scale along deep polar ice cores. Composite flow laws allow considering the effect of this variability on rheology, by weighing the contribution of grain-size-sensitive (GSS, diffusion/grain boundary sliding) and grain-size-insensitive (GSI, dislocation) creep mechanisms taking the full grain size distribution into account [1]. Extraction of hundreds of grain size distributions for different depths along an ice core has become relatively easy by automatic image processing techniques [2]. The shallow ice approximation is widely adopted in ice sheet modeling and approaches the full-Stokes solution for small ratios of vertical to horizontal characteristic dimensions. In this approximation shear stress in the vertical plain dominates the strain. This assumption is not applicable at ice divides or dome structures, where most deep ice core drilling sites are located. Within the upper two thirds of the ice column longitudinal stresses are not negligible and ice deformation is dominated by vertical strain. The Dansgaard-Johnsen model [3] predicts a dominating, constant vertical strain rate for the upper two thirds of the ice sheet, whereas in the lower ice column vertical shear becomes the main driver for ice deformation. We derived vertical strain rates from the upper NEEM ice core (North-West Greenland) and compared them to classical estimates of strain rates at the NEEM site. Assuming intervals of constant accumulation rates, we found a variation of vertical strain rates by a factor 2-3 in the upper ice column. We discuss the current applicability of composite flow laws to grain size distributions extracted from ice cores drilled at sites where the flow direction rotates by 90 degrees with depth (i.e. ice divide). An interesting finding is that a transition to a glacial period in future would be associated with a decrease in vertical strain rate (due to a reduced accumulation rate) and an increase of the frequency of small grains (due to an enhanced impurity content). Composite flow laws assign an enhanced contribution of GSS creep to this transition. It is currently unclear which factor would have a greater influence. [1] Herwegh et al., 2005, J. Struct. Geol., 27, 503-521 [2] T. Binder et al., 2013, J. Microsc., 250, 130-141 [3] W. Dansgaard & S.J. Johnsen, 1969, J. Glaciol., 8, 215-223

On the thermal stability of physical vapor deposited oxide-hardened nanocrystalline gold thin films

DOE PAGES

Argibay, Nicolas; Mogonye, J. E.; Michael, Joseph R.; ...

2015-04-08

We describe a correlation between electrical resistivity and grain size for PVD synthesized polycrystalline oxide-hardened metal-matrix thin films in oxide-dilute (<5 vol. % oxide phase) compositions. The correlation is based on the Mayadas-Shatzkes (M-S) electron scattering model, predictive of grain size evolution as a function of composition in the oxide-dilute regime for 2 μm thick Au-ZnO films. We describe a technique to investigate grain boundary (GB) mobility and the thermal stability of GBs based on in situelectrical resistivity measurements during annealing experiments, interpreted using a combination of the M-S model and the Michels et al. model describing solute drag stabilizedmore » grain growth kinetics. Using this technique, activation energy and pre-exponential Arrhenius parameter values of E a = 21.6 kJ/mol and A o = 2.3 × 10 -17 m 2/s for Au-1 vol. % ZnO and E a =12.7 kJ/mol and A o = 3.1 × 10 -18 m 2/s for Au-2 vol.% ZnO were determined. In the oxide-dilute regime, the grain size reduction of the Au matrix yielded a maximum hardness of 2.6 GPa for 5 vol. % ZnO. A combined model including percolation behavior and grain refinement is presented that accurately describes the composition dependent change in electrical resistivity throughout the entire composition range for Au-ZnO thin films. As a result, the proposed correlations are supported by microstructural characterization using transmission electron microscopy and electron diffraction mapping for grain size determination.« less

Microstructures and Grain Refinement of Additive-Manufactured Ti- xW Alloys

NASA Astrophysics Data System (ADS)

Mendoza, Michael Y.; Samimi, Peyman; Brice, David A.; Martin, Brian W.; Rolchigo, Matt R.; LeSar, Richard; Collins, Peter C.

2017-07-01

It is necessary to better understand the composition-processing-microstructure relationships that exist for materials produced by additive manufacturing. To this end, Laser Engineered Net Shaping (LENS™), a type of additive manufacturing, was used to produce a compositionally graded titanium binary model alloy system (Ti- xW specimen (0 ≤ x ≤ 30 wt pct), so that relationships could be made between composition, processing, and the prior beta grain size. Importantly, the thermophysical properties of the Ti- xW, specifically its supercooling parameter ( P) and growth restriction factor ( Q), are such that grain refinement is expected and was observed. The systematic, combinatorial study of this binary system provides an opportunity to assess the mechanisms by which grain refinement occurs in Ti-based alloys in general, and for additive manufacturing in particular. The operating mechanisms that govern the relationship between composition and grain size are interpreted using a model originally developed for aluminum and magnesium alloys and subsequently applied for titanium alloys. The prior beta grain factor observed and the interpretations of their correlations indicate that tungsten is a good grain refiner and such models are valid to explain the grain-refinement process. By extension, other binary elements or higher order alloy systems with similar thermophysical properties should exhibit similar grain refinement.

The Effect of Film Composition on the Texture and Grain Size of CuInS2 Prepared by Spray Pyrolysis

NASA Technical Reports Server (NTRS)

Jin, Michael H.; Banger, Kulinder K.; Harris, Jerry D.; Hepp, Aloysius F.

2003-01-01

Ternary single-source precursors were used to deposit CuInS2 thin films using chemical spray pyrolysis. We investigated the effect of the film composition on texture, secondary phase formation, and grain size. As-grown films were most often In-rich. They became more (204/220)-oriented as indium concentration increased, and always contained a yet unidentified secondary phase. The (112)-prefened orientation became more pronounced as the film composition became more Cu-rich. The secondary phase was determined to be an In-rich compound based on composition analysis and Raman spectroscopy. In addition, as-grown Cu-rich (112)-oriented films did not exhibit the In-rich compound. Depositing a thin Cu layer prior to the growth of CuInS2 increased the maximum grain size from - 0.5 micron to - 1 micron, and prevented the formation of the In-rich secondary phase.

A Model of Thermal Conductivity for Planetary Soils: 1. Theory for Unconsolidated Soils

NASA Technical Reports Server (NTRS)

Piqueux, S.; Christensen, P. R.

2009-01-01

We present a model of heat conduction for mono-sized spherical particulate media under stagnant gases based on the kinetic theory of gases, numerical modeling of Fourier s law of heat conduction, theoretical constraints on the gas thermal conductivity at various Knudsen regimes, and laboratory measurements. Incorporating the effect of the temperature allows for the derivation of the pore-filling gas conductivity and bulk thermal conductivity of samples using additional parameters (pressure, gas composition, grain size, and porosity). The radiative and solid-to-solid conductivities are also accounted for. Our thermal model reproduces the well-established bulk thermal conductivity dependency of a sample with the grain size and pressure and also confirms laboratory measurements finding that higher porosities generally lead to lower conductivities. It predicts the existence of the plateau conductivity at high pressure, where the bulk conductivity does not depend on the grain size. The good agreement between the model predictions and published laboratory measurements under a variety of pressures, temperatures, gas compositions, and grain sizes provides additional confidence in our results. On Venus, Earth, and Titan, the pressure and temperature combinations are too high to observe a soil thermal conductivity dependency on the grain size, but each planet has a unique thermal inertia due to their different surface temperatures. On Mars, the temperature and pressure combination is ideal to observe the soil thermal conductivity dependency on the average grain size. Thermal conductivity models that do not take the temperature and the pore-filling gas composition into account may yield significant errors.

Austenite Grain Size Control in Upstream Processing of Niobium Microalloyed Steels by Nano-Scale Precipitate Engineering of TiN-NbC Composite

NASA Astrophysics Data System (ADS)

Subramanian, S. V.; Ma, Xiaoping; Rehman, Kashif

There is a growing demand for thicker gage pipes particularly for off-shore projects. Austenite grain size control in upstream processing before pancaking is essential to obtain excellent DBTT and DWTT properties in thicker gage product. This paper examines the basic science aspects of austenite grain size control by nano-scale precipitate engineering.

Experimental Study of Dust Grain Charging

NASA Technical Reports Server (NTRS)

Spann, James F; Venturini, Catherine C.; Comfort, Richard H.; Mian, Abbas M.

1999-01-01

The results of an experimental study of the charging mechanisms of micron size dust grains are presented. Individual dust grains are electrodynamically suspended and exposed to an electron beam of known energy and flux, and to far ultraviolet radiation of known wavelength and intensity. Changes in the charge-to-mass ratio of the grain are directly measured as a function of incident beam (electron and/or photon), grain size and composition. Comparisons of our results to theoretical models that predict the grain response are presented.

Geochemical evidence for the provenance of aeolian deposits in the Qaidam Basin, Tibetan Plateau

NASA Astrophysics Data System (ADS)

Du, Shisong; Wu, Yongqiu; Tan, Lihua

2018-06-01

The main purpose of this study is to analyse the material source of different grain-size components of dune sand in the Qaidam Basin. We determined the trace and rare earth element (REE) compositions and Sr-Nd isotopic compositions of the coarse (75-500 μm) and fine (<75 μm) fractions of surface sediment samples. The comparison of the immobile trace element and REE compositions, Sr-Nd isotopic compositions and multidimensional scaling (MDS) results of the dune sands with those of different types of sediments in potential source areas revealed the following information. (1) The fine- and coarse-grained fractions of dune sands in the Qaidam Basin exhibit distinctly different elemental concentrations, elemental patterns and characteristic parameters of REE. Moreover, Sr-Nd isotopic differences also exist between different grain-size fractions of aeolian sand, which means that different grain-size fractions of these dune sands have different source areas. (2) The geochemical characteristics of the coarse particles of dune sand exhibit obvious regional heterogeneity and generally record a local origin derived from local fluvial sediments and alluvial/proluvial sediments. The coarse- and fine-grained dune sand in the southern Qaidam Basin mainly came from Kunlun Mountains, whereas the coarse- and fine-grained dune sand in the northeastern Qaidam Basin mainly came from Qilian Mountains. (3) The fine-grained fractions of sediments throughout the entire Qaidam Basin may have been affected by the input of foreign materials from the Tarim Basin.

Recrystallization and grain growth phenomena in a particle-reinforced aluminum composite

NASA Astrophysics Data System (ADS)

van Aken, D. C.; Krajewski, P. E.; Vyletel, G. M.; Allison, J. E.; Jones, J. W.

1995-06-01

Recrystallization and grain growth in a 2219/TiC/15p composite were investigated as functions of the amount of deformation and deformation temperature. Both cold and hot deformed samples were annealed at the normal solution treatment temperature of 535 °C. It was shown that large recrystallized grain diameters, relative to the interparticle spacing, could be produced in a narrow range of deformation for samples cold-worked and those hot-worked below 450 °C. For cold-worked samples, between 4 to 6 pct deformation, the recrystallized grain diameters varied from 530 to 66 μm as the amount of deformation increased. Subsequent grain growth was not observed in these recrystallized materials and noncompact grain shapes were observed. For deformations greater than 15 pct, recrystallized grain diameters less than the interparticle spacing were observed and subsequent grain growth produced a pinned grain diameter of 27 μm. The pinned grain diameter agreed well with an empirical model based on three dimensional (3-D) Monte Carlo simulations of grain growth and particle pinning in a two-phase material. Tensile properties were determined as a function of grain size, and it was shown that grain size had a weak influence on yield strength. A maximum in the yield strength was observed at a grain size larger than the normal grain growth and particle-pinned diameter.

Fingerprints of carbon, nitrogen, and silicon isotopes in small interstellar SiC grains from the Murchison meteorite

NASA Technical Reports Server (NTRS)

Hoppe, Peter; Geiss, Johannes; Buehler, Fritz; Neuenschwander, Juerg; Amari, Sachiko; Lewis, Roy S.

1993-01-01

We report ion microprobe determinations of the carbon, nitrogen, and silicon isotopic compositions of small SiC grains from the Murchison CM2 chondrite. Analyses were made on samples containing variable numbers of grains and on 14 individual grains. In some cases the multiple-grain sample compositions were probably dominated by only one or two grains. Total ranges observed are given. Only a few grains show values near the range limits. Both the total ranges of carbon and nitrogen isotopic compositions, and even the narrower ranges typical for the majority of the grains, are similar to those observed for larger SiC grains. Two rare components appear to be present in the smaller-size fraction, one characterized by C-12/C-13 about 12-16 and the other by very heavy nitrogen. The carbon and nitrogen isotopic compositions qualitatively may reflect hydrostatic H-burning via the CNO cycle and He-burning in red giants, as well as explosive H-burning in novae. The silicon isotopic compositions of most grains qualitatively show what is the signature of He-burning. The silicon isotopic composition of one grain, however, suggests a different process.

From Aeolis Palus to the Bagnold Dunes field: Overview of martian soil analyses performed by ChemCam in Gale Crater

NASA Astrophysics Data System (ADS)

Cousin, A.; Meslin, P. Y.; Dehouck, E.; David, G.; Rapin, W.; Schröder, S.; Forni, O.; Gasnault, O.; Williams, A. J.; Lasue, J.; Stein, N.; Ehlmann, B. L.; Payre, V.; Anderson, R. B.; Blaney, D. L.; Bridges, N. T.; Clark, B. C.; Frydenvang, J.; Gasda, P. J.; Johnson, J. R.; Lanza, N.; l'Haridon, J.; Mangold, N.; Maurice, S.; Newsom, H. E.; Ollila, A.; Pinet, P. C.; Sautter, V.; Thomas, N. H.; Wiens, R. C.

2017-12-01

In situ analysis of the chemical and mineralogical composition of the martian soil, and the determination of its volatile inventory, can provide important constraints on the bulk composition of the martian crust, on its igneous diversity, but also on the physical and chemical weathering processes that have altered its primary igneous constituents. Transport processes that have occurred over long geological time scales, however, make this analysis quite complex, as constituents from different unknown sources are mixed together, and may have been sorted according to grain size or density. A meteoritic contribution is also present. Disentangling the influence of each of these processes requires the use of different analytical techniques, at different spatial scales, and at different locations over the planet. We will present an overview of the soil analyses obtained over the past 5 years by the ChemCam instrument on board MSL/Curiosity. Their specificity lies in their small spatial scale ( 300 μm), close to the average grains' size. At this scale, chemical trends are observed, resulting from the mixing of different end-members with different grain sizes: coarse felsic grains of likely local origin, fine grains with a basaltic composition close to soil compositions observed at other landing sites, but distinct from local rocks, and a fine-grained, Si-poor, volatile-rich component probably associated with the XRD-amorphous component detected by the CheMin instrument. The thin ablation depth associated with each laser shot ( 1 μm) enables us to analyse the surface of the grains, which is characterized by a strong, but variable hydrogen signal. These analyses provide constraints on the composition of a possible alteration rind or coating present at their surface. An extensive, multi-instrument investigation of active dunes (barchan and linear dunes) has also been carried out, revealing slight chemical differences with surrounding soils, and a more homogeneous composition, although chemical variations as a function of grain size are observed, with coarser grains enriched in mafic minerals. These results illustrate the still ongoing influence of aeolian transport on the physical sorting of loose, unconsolidated sediments. These results also provide ground truth for orbital IR observations of aeolian bedforms.

Uses and misuses of compositional data in sedimentology

NASA Astrophysics Data System (ADS)

Tolosana-Delgado, Raimon

2012-12-01

This paper serves two goals. The first part shows how mass evolution processes of different nature become undistinguishable once we take a size-limited, noisy sample of its compositional fingerprint: processes of exponential decay, mass mixture and complementary accumulation are simulated, and then samples contaminated with noise are extracted. The aim of this exercise is to illustrate the limitations of typical graphical representations and statistical methods when dealing with compositional data, i.e. data in percentages, concentrations or proportions. The second part presents a series of concepts, tools and methods to represent and statistically treat a compositional data set attending to these limitations. The aim of this second part is to offer a state-of-the-art Compositional Data Analysis. This includes: descriptive statistics and graphics (the biplot); ternary diagrams with confidence regions for the mean; regression and ANalysis-Of-VAriance models to explain compositional variability; and the use of compositional information to predict environmental covariables or discriminate between groups. All these tools share a four-step algorithm: (1) transform compositions with an invertible log-ratio transformation; (2) apply a statistical method to the transformed scores; (3) back-transform the results to compositions; and (4) interpret results in relative terms. Using these techniques, a data set of sand petrographic composition has been analyzed, highlighting that: finer sands are richer in single-crystal grains in relation to polycrystalline grains, and that grain-size accounts for almost all compositional variability; a stronger water flow (river discharge) favors mica grains against quartz or rock fragment grains, possibly due to hydrodynamic sorting effects; a higher relief ratio implies shorter residence times, which may favor survival of micas and rock fragments, relatively more labile grains.

Temperature-dependency of Magnetic Susceptibility U Advantages and Limits For Magneto-mineralogical Studies

NASA Astrophysics Data System (ADS)

Kontny, A.

Low-field magnetic susceptibility measurements in the temperature range U192 to 700 C (k(T)) are a widely applied method used for the identification of magnetic phases and characteristic magnetic phase transitions. One of the advantages of this method is the precise determination of titanomagnetite composition independently from grain size. However, the interpretations of k(T)-curves often are discussed controversially because other effects like grain size or the occurrence of more than one magnetic phase complicate the courses. Case studies from the titanomagnetite and titanohe- matite solid solution series including pure magnetite and hematite will be presented and variations in chemical composition, alteration and grain size will be discussed in relation to their geological significance. (1) In subaerially extruded basaltic lava differences in the low-temperature legs of the k(T) curves indicate variations in the degree of high-temperature (deuteric) oxidation of titanomagnetite. This alteration to magnetite-rich titanomagnetite is accompanied by a grain size reduction, which can be correlated with the development of a susceptibility peak at about U160 C. Fur- ther oxidation transforms the titanomagnetite into titanohematite which again results in a characteristic k(T) behavior at low temperatures with a decrease in k with in- creasing temperature (2) Hydrothermal alteration from magnetite to hematite creates a hematite phase that cannot be seen in k(T)-curves. However, hematite that is grown in sediments, can be identified by its Tc. Therefore it is assumed that crystallinity of magnetic phases seems to play a significant role to explain a different behaviour. (3) Submarine basalts rapidly quenched from high temperatures often show wide anti- clines in the k(T)-curves which can be correlated with a range of chemical composition and grain sizes, including small amounts of pure magnetite. This feature is commonly attributed to low-temperature alteration of single domain grains of titanomagnetite and is described for ocean floor basalts. An alternative interpretation is given by composi- tional and grain size variations due to small scale fractionation of melt related to the cooling of the lava. Generally, the high-temperature leg of k(T) curves mostly indi- cates the chemical composition (Tc) and degree of alteration, the low-temperature leg seems to be more sensible for grain size variations.

Impact of grain size and rock composition on simulated rock weathering

NASA Astrophysics Data System (ADS)

Israeli, Yoni; Emmanuel, Simon

2018-05-01

Both chemical and mechanical processes act together to control the weathering rate of rocks. In rocks with micrometer size grains, enhanced dissolution at grain boundaries has been observed to cause the mechanical detachment of particles. However, it remains unclear how important this effect is in rocks with larger grains, and how the overall weathering rate is influenced by the proportion of high- and low-reactivity mineral phases. Here, we use a numerical model to assess the effect of grain size on chemical weathering and chemo-mechanical grain detachment. Our model shows that as grain size increases, the weathering rate initially decreases; however, beyond a critical size no significant decrease in the rate is observed. This transition occurs when the density of reactive boundaries is less than ˜ 20 % of the entire domain. In addition, we examined the weathering rates of rocks containing different proportions of high- and low-reactivity minerals. We found that as the proportion of low-reactivity minerals increases, the weathering rate decreases nonlinearly. These simulations indicate that for all compositions, grain detachment contributes more than 36 % to the overall weathering rate, with a maximum of ˜ 50 % when high- and low-reactivity minerals are equally abundant in the rock. This occurs because selective dissolution of the high-reactivity minerals creates large clusters of low-reactivity minerals, which then become detached. Our results demonstrate that the balance between chemical and mechanical processes can create complex and nonlinear relationships between the weathering rate and lithology.

An Informatics Based Approach to Reduce the Grain Size of Cast Hadfield Steel

NASA Astrophysics Data System (ADS)

Dey, Swati; Pathak, Shankha; Sheoran, Sumit; Kela, Damodar H.; Datta, Shubhabrata

2016-04-01

Materials Informatics concept using computational intelligence based approaches are employed to bring out the significant alloying additions to achieve grain refinement in cast Hadfield steel. Castings of Hadfield steels used for railway crossings, requires fine grained austenitic structure. Maintaining proper grain size of this component is very crucial in order to achieve the desired properties and service life. This work studies the important variables affecting the grain size of such steels which includes the compositional and processing variables. The computational findings and prior knowledge is used to design the alloy, which is subjected to a few trials to validate the findings.

Evaluating the importance of grain size sensitive creep in terrestrial ice sheet rheology

NASA Astrophysics Data System (ADS)

Maaijwee, C. N. P. J.; de Bresser, J. H. P.

2009-04-01

The rheology of ice in terrestrial ice sheets is generally considered to be independent of the size of the grains (crystals), and appears well described by Glen's flow law. In recent years, however, new laboratory deformation experiments on ice as well as analysis of in situ measurements of deformation at glaciers suggested that grain size and variations therein should not be discarded as important parameters in the deformation of ice in nature. Ice, just like crystalline rock materials, exhibits distributed grain sizes. Taking now that not only grain size insensitive (GSI; dislocation) mechanisms, but also grain size sensitive (GSS; diffusion and/or grain boundary sliding) mechanisms may be operative in ice, variations in the shape of the distribution (e.g. the width) can be expected to affect the rheological behaviour. To evaluate this effect, we have derived a composite GSI+GSS flow law and combined this with full grain size distributions. The constitutive flow equations for end-member GSI and GSS creep of ice were taken from the work of Goldsby and Kohlstedt (2001, J.Geophys.Res., vol. 106). We used their description of grain boundary sliding controlled creep as representative of GSS creep. The grain size data largely came from published measurements from the top 800-1000 m of two Greenland ice cores (NorthGRIP and GRIP) and one Antarctic ice core (Epica, Dome Concordia). Temperature profiles were available for both core settings. The grain size data show a close to lognormal distribution in all three settings, with the median grain size increasing with depth. We constructed a synthetic grain size profile up to a depth of 3100 m (cf. GRIP) by allowing the median grain size and standard deviation of the distribution to linearly increase with depth. The percentage GSS creep contributing to the total strain rate has been calculated for a range of strain rates that were assumed constant along the ice core axes. The results of our calculations show that at realistic strain rates in the order of 10-11 to 10-12 s-1, GSS mechanisms can be expected to dominate creep in the parts of the ice sheets investigated (i.e. the top ~1000 m). In the synthetic core, the GSS contribution decreases if going to greater depth (~2500 m), but increases again close to the contact with the bedrock (at 3100 m). Although many assumptions have been made in our approach, the results confirm the important role that grain size might play in ice sheet rheology. The application of full grain size distributions in composite flow equations helps to come to reliable extrapolation of lab data to nature.

The Effect of Film Composition on the Texture and Grain Size of CuInS2 Prepared by Spray Pyrolysis

NASA Technical Reports Server (NTRS)

Jin, Michael H.-C.; Banger, Kulbinder K.; Harris, Jerry D.; Hepp, Aloysius F.

2003-01-01

CuInS2 was deposited by spray pyrolysis using single-source precursors synthesized in-house. Films with either (112) or (204/220) preferred orientation always showed Cu-rich and In-rich composition respectively. The In-rich (204/220)-oriented films always contained a secondary phase evaluated as an In-rich compound, and the hindrance of (112)-oriented grain growth was confirmed by glancing angle X-ray diffraction. In conclusion, only the Cu-rich (112)-oriented films with dense columnar grains can be prepared without the secondary In-rich compound. The effect of extra Cu on the grain size and the solar cell results will be also presented.

Room-Temperature and High-Temperature Tensile Mechanical Properties of TA15 Titanium Alloy and TiB Whisker-Reinforced TA15 Matrix Composites Fabricated by Vacuum Hot-Pressing Sintering

PubMed Central

Feng, Yangju; Zhang, Wencong; Zeng, Li; Cui, Guorong; Chen, Wenzhen

2017-01-01

In this paper, the microstructure, the room-temperature and high-temperature tensile mechanical properties of monolithic TA15 alloy and TiB whisker-reinforced TA15 titanium matrix composites (TiBw/TA15) fabricated by vacuum hot-pressing sintering were investigated. The microstructure results showed that there were no obvious differences in the microstructure between monolithic TA15 alloy and TiBw/TA15 composites, except whether or not the grain boundaries contained TiBw. After sintering, the matrix microstructure presented a typical Widmanstätten structure and the size of primary β grain was consistent with the size of spherical TA15 titanium metallic powders. This result demonstrated that TiBw was not the only factor limiting grain coarsening of the primary β grain. Moreover, the grain coarsening of α colonies was obvious, and high-angle grain boundaries (HAGBs) were distributed within the primary β grain. In addition, TiBw played an important role in the microstructure evolution. In the composites, TiBw were randomly distributed in the matrix and surrounded by a large number of low-angle grain boundaries (LAGBs). Globularization of α phase occurred prior, near the TiBw region, because TiBw provided the nucleation site for the equiaxed α phase. The room-temperature and high-temperature tensile results showed that TiBw distributed at the primary β grain boundaries can strengthen the grain boundary, but reduce the connectivity of the matrix. Therefore, compared to the monolithic TA15 alloy fabricated by the same process, the tensile strength of the composites increased, and the tensile elongation decreased. Moreover, with the addition of TiBw, the fracture mechanism was changed to a mixture of brittle fracture and ductile failure (composites) from ductile failure (monolithic TA15 alloy). The fracture surfaces of TiBw/TA15 composites were the grain boundaries of the primary β grain where the majority of TiB whiskers distributed, i.e., the surfaces of the spherical TA15 titanium metallic powders. PMID:28772786

Room-Temperature and High-Temperature Tensile Mechanical Properties of TA15 Titanium Alloy and TiB Whisker-Reinforced TA15 Matrix Composites Fabricated by Vacuum Hot-Pressing Sintering.

PubMed

Feng, Yangju; Zhang, Wencong; Zeng, Li; Cui, Guorong; Chen, Wenzhen

2017-04-18

In this paper, the microstructure, the room-temperature and high-temperature tensile mechanical properties of monolithic TA15 alloy and TiB whisker-reinforced TA15 titanium matrix composites (TiBw/TA15) fabricated by vacuum hot-pressing sintering were investigated. The microstructure results showed that there were no obvious differences in the microstructure between monolithic TA15 alloy and TiBw/TA15 composites, except whether or not the grain boundaries contained TiBw. After sintering, the matrix microstructure presented a typical Widmanstätten structure and the size of primary β grain was consistent with the size of spherical TA15 titanium metallic powders. This result demonstrated that TiBw was not the only factor limiting grain coarsening of the primary β grain. Moreover, the grain coarsening of α colonies was obvious, and high-angle grain boundaries (HAGBs) were distributed within the primary β grain. In addition, TiBw played an important role in the microstructure evolution. In the composites, TiBw were randomly distributed in the matrix and surrounded by a large number of low-angle grain boundaries (LAGBs). Globularization of α phase occurred prior, near the TiBw region, because TiBw provided the nucleation site for the equiaxed α phase. The room-temperature and high-temperature tensile results showed that TiBw distributed at the primary β grain boundaries can strengthen the grain boundary, but reduce the connectivity of the matrix. Therefore, compared to the monolithic TA15 alloy fabricated by the same process, the tensile strength of the composites increased, and the tensile elongation decreased. Moreover, with the addition of TiBw, the fracture mechanism was changed to a mixture of brittle fracture and ductile failure (composites) from ductile failure (monolithic TA15 alloy). The fracture surfaces of TiBw/TA15 composites were the grain boundaries of the primary β grain where the majority of TiB whiskers distributed, i.e., the surfaces of the spherical TA15 titanium metallic powders.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pauly, Tyler; Garrod, Robin T., E-mail: tap74@cornell.edu

Computational models of interstellar gas-grain chemistry have historically adopted a single dust-grain size of 0.1 micron, assumed to be representative of the size distribution present in the interstellar medium. Here, we investigate the effects of a broad grain-size distribution on the chemistry of dust-grain surfaces and the subsequent build-up of molecular ices on the grains, using a three-phase gas-grain chemical model of a quiescent dark cloud. We include an explicit treatment of the grain temperatures, governed both by the visual extinction of the cloud and the size of each individual grain-size population. We find that the temperature difference plays amore » significant role in determining the total bulk ice composition across the grain-size distribution, while the effects of geometrical differences between size populations appear marginal. We also consider collapse from a diffuse to a dark cloud, allowing dust temperatures to fall. Under the initial diffuse conditions, small grains are too warm to promote grain-mantle build-up, with most ices forming on the mid-sized grains. As collapse proceeds, the more abundant, smallest grains cool and become the dominant ice carriers; the large population of small grains means that this ice is distributed across many grains, with perhaps no more than 40 monolayers of ice each (versus several hundred assuming a single grain size). This effect may be important for the subsequent processing and desorption of the ice during the hot-core phase of star formation, exposing a significant proportion of the ice to the gas phase, increasing the importance of ice-surface chemistry and surface–gas interactions.« less

In Situ Sampling of Relative Dust Devil Particle Loads and Their Vertical Grain Size Distributions.

PubMed

Raack, Jan; Reiss, Dennis; Balme, Matthew R; Taj-Eddine, Kamal; Ori, Gian Gabriele

2017-04-19

During a field campaign in the Sahara Desert in southern Morocco, spring 2012, we sampled the vertical grain size distribution of two active dust devils that exhibited different dimensions and intensities. With these in situ samples of grains in the vortices, it was possible to derive detailed vertical grain size distributions and measurements of the lifted relative particle load. Measurements of the two dust devils show that the majority of all lifted particles were only lifted within the first meter (∼46.5% and ∼61% of all particles; ∼76.5 wt % and ∼89 wt % of the relative particle load). Furthermore, ∼69% and ∼82% of all lifted sand grains occurred in the first meter of the dust devils, indicating the occurrence of "sand skirts." Both sampled dust devils were relatively small (∼15 m and ∼4-5 m in diameter) compared to dust devils in surrounding regions; nevertheless, measurements show that ∼58.5% to 73.5% of all lifted particles were small enough to go into suspension (<31 μm, depending on the used grain size classification). This relatively high amount represents only ∼0.05 to 0.15 wt % of the lifted particle load. Larger dust devils probably entrain larger amounts of fine-grained material into the atmosphere, which can have an influence on the climate. Furthermore, our results indicate that the composition of the surface, on which the dust devils evolved, also had an influence on the particle load composition of the dust devil vortices. The internal particle load structure of both sampled dust devils was comparable related to their vertical grain size distribution and relative particle load, although both dust devils differed in their dimensions and intensities. A general trend of decreasing grain sizes with height was also detected. Key Words: Mars-Dust devils-Planetary science-Desert soils-Atmosphere-Grain sizes. Astrobiology 17, xxx-xxx.

The Effects of Grain Size and Temperature Distributions on the Formation of Interstellar Ice Mantles

NASA Astrophysics Data System (ADS)

Pauly, Tyler; Garrod, Robin T.

2016-02-01

Computational models of interstellar gas-grain chemistry have historically adopted a single dust-grain size of 0.1 micron, assumed to be representative of the size distribution present in the interstellar medium. Here, we investigate the effects of a broad grain-size distribution on the chemistry of dust-grain surfaces and the subsequent build-up of molecular ices on the grains, using a three-phase gas-grain chemical model of a quiescent dark cloud. We include an explicit treatment of the grain temperatures, governed both by the visual extinction of the cloud and the size of each individual grain-size population. We find that the temperature difference plays a significant role in determining the total bulk ice composition across the grain-size distribution, while the effects of geometrical differences between size populations appear marginal. We also consider collapse from a diffuse to a dark cloud, allowing dust temperatures to fall. Under the initial diffuse conditions, small grains are too warm to promote grain-mantle build-up, with most ices forming on the mid-sized grains. As collapse proceeds, the more abundant, smallest grains cool and become the dominant ice carriers; the large population of small grains means that this ice is distributed across many grains, with perhaps no more than 40 monolayers of ice each (versus several hundred assuming a single grain size). This effect may be important for the subsequent processing and desorption of the ice during the hot-core phase of star formation, exposing a significant proportion of the ice to the gas phase, increasing the importance of ice-surface chemistry and surface-gas interactions.

Grain-size dynamics beneath mid-ocean ridges: Implications for permeability and melt extraction.

PubMed

Turner, Andrew J; Katz, Richard F; Behn, Mark D

2015-03-01

Grain size is an important control on mantle viscosity and permeability, but is difficult or impossible to measure in situ. We construct a two-dimensional, single phase model for the steady state mean grain size beneath a mid-ocean ridge. The mantle rheology is modeled as a composite of diffusion creep, dislocation creep, dislocation accommodated grain boundary sliding, and a plastic stress limiter. The mean grain size is calculated by the paleowattmeter relationship of Austin and Evans (2007). We investigate the sensitivity of our model to global variations in grain growth exponent, potential temperature, spreading-rate, and mantle hydration. We interpret the mean grain-size field in terms of its permeability to melt transport. The permeability structure due to mean grain size may be approximated as a high permeability region beneath a low permeability region. The transition between high and low permeability regions occurs across a boundary that is steeply inclined toward the ridge axis. We hypothesize that such a permeability structure generated from the variability of the mean grain size may focus melt toward the ridge axis, analogous to Sparks and Parmentier (1991)-type focusing. This focusing may, in turn, constrain the region where significant melt fractions are observed by seismic or magnetotelluric surveys. This interpretation of melt focusing via the grain-size permeability structure is consistent with MT observation of the asthenosphere beneath the East Pacific Rise. The grain-size field beneath MORs can vary over orders of magnitude The grain-size field affects the rheology and permeability of the asthenosphere The grain-size field may focus melt toward the ridge axis.

Settling equivalence of detrital minerals and grain-size dependence of sediment composition

NASA Astrophysics Data System (ADS)

Garzanti, Eduardo; Andò, Sergio; Vezzoli, Giovanni

2008-08-01

This study discusses the laws which govern sediment deposition, and consequently determine size-dependent compositional variability. A theoretical approach is substantiated by robust datasets on major Alpine, Himalayan, and African sedimentary systems. Integrated (bulk-petrography, heavy-mineral, X-ray powder diffraction) multiple-window analyses at 0.25ϕ to 0.50ϕ sieve interval of eighty-five fluvial, beach, and eolian-dune samples, ranging from very fine silt to coarse sand, document homologous intrasample compositional trends, revealed by systematic concentration of denser grains in finer-grained fractions (“size-density sorting”). These trends are explained by the settling-equivalence principle, stating that detrital minerals are deposited together if their settling velocity is the same. Settling of silt is chiefly resisted by fluid viscosity, and Stokes' law predicts that size differences between detrital minerals in ϕ units (“size shifts”) are half the difference between the logarithms of their submerged densities. Settling of pebbles is chiefly resisted by turbulence effects, and the Impact law predicts double size shifts than Stokes' law. Settling of sand is resisted by both viscosity and turbulence, the settling-equivalence formula is complex, and size shifts increase - with increasing settling velocity and grain size - from those predicted by Stokes' law to those predicted by the Impact law. In wind-laid sands, size shifts match those predicted by the Impact law; size-density sorting is thus greater than in water-laid fine sands. New analytical, graphical, and statistical techniques for rigorous settling-equivalence analysis of terrigenous sediments are illustrated. Deviations associated with non-spherical shape, density anomalies, inheritance from source rocks, or mixing of detrital species with contrasting provenance and different size distribution are also tentatively assessed. Such integrated theoretical and experimental approach allows us to mathematically predict intrasample compositional variability of water-laid and wind-laid sediments, once the density of detrital components is known.

Observation of grain size effect on multiferroism and magnetoelectric coupling of Na0.5Bi0.5TiO3 - BaFe12O19 novel composite system

NASA Astrophysics Data System (ADS)

Pattanayak, Ranjit; Kuila, Sourav; Raut, Subhajit; Ghosh, Surya Prakash; Dhal, Satyanarayan; Panigrahi, Simanchalo

2017-12-01

Four novel polycrystalline magnetoelectric composite systems: S1, S2, S3 and S4 having composition [90 wt% Na0.5Bi0.5TiO3 (NBT) - 10 wt% BaFe12O19 (BaM)] considering the variation of grain size of both the phases [NBT(Lg)-BaM(Lg)-[S1], NBT(Lg)-BaM(Sg)-[S2], NBT(Sg)-BaM(Lg)-[S3] and NBT(Sg)-BaM(Sg)-[S4

Luna 24 regolith breccias: A possible source of the fine size material of the Luna 24 regolith

NASA Technical Reports Server (NTRS)

Rode, O. D.; Lindstrom, M. M.

1994-01-01

The regolith breccias from the Luna 24 core were analyzed. The Luna 24 regolith is a mixture of fine and coarse grain materials. The comparable analysis of the grain size distributions, the modal and chemical compositions of the breccias, and the regolith from the same levels show that the friable slightly litificated breccia with a friable fine grain matrix may be a source of fine grain material of the Luna 24 present day regolith.

Structure and phase composition of ultrafine-grained TiNb alloy after high-temperature annealings

NASA Astrophysics Data System (ADS)

Eroshenko, Anna Yu.; Glukhov, Ivan A.; Mairambekova, Aikol; Tolmachev, Alexey I.; Sharkeev, Yurii P.

2017-12-01

The paper presents the experimental data observed in the microstructure and phase composition of ultrafine-grained Ti-40 mass % Nb (Ti40Nb) alloy after high-temperature annealings. The ultrafine-grained Ti40Nb alloy is produced by severe plastic deformation (SPD). This method includes multiple abc-pressing and multi-pass rolling followed by further pre-recrystallizing annealing which, in its turn, enhances the formation of ultrafine-grained structures with mean size of 0.28 µm involving stable β- and α-phase and metastable nanosized ω-phase in the alloy. It is shown that annealing at 500°C preserves the ultrafine-grained structure and phase composition. In cases of annealing at 800°C the ultrafine-grained state transforms into the coarse-grained state. The stable β-phase and the nanosized metastable ω-phase have been identified in the coarse-grained structure.

Grain-Size Based Additivity Models for Scaling Multi-rate Uranyl Surface Complexation in Subsurface Sediments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Xiaoying; Liu, Chongxuan; Hu, Bill X.

This study statistically analyzed a grain-size based additivity model that has been proposed to scale reaction rates and parameters from laboratory to field. The additivity model assumed that reaction properties in a sediment including surface area, reactive site concentration, reaction rate, and extent can be predicted from field-scale grain size distribution by linearly adding reaction properties for individual grain size fractions. This study focused on the statistical analysis of the additivity model with respect to reaction rate constants using multi-rate uranyl (U(VI)) surface complexation reactions in a contaminated sediment as an example. Experimental data of rate-limited U(VI) desorption in amore » stirred flow-cell reactor were used to estimate the statistical properties of multi-rate parameters for individual grain size fractions. The statistical properties of the rate constants for the individual grain size fractions were then used to analyze the statistical properties of the additivity model to predict rate-limited U(VI) desorption in the composite sediment, and to evaluate the relative importance of individual grain size fractions to the overall U(VI) desorption. The result indicated that the additivity model provided a good prediction of the U(VI) desorption in the composite sediment. However, the rate constants were not directly scalable using the additivity model, and U(VI) desorption in individual grain size fractions have to be simulated in order to apply the additivity model. An approximate additivity model for directly scaling rate constants was subsequently proposed and evaluated. The result found that the approximate model provided a good prediction of the experimental results within statistical uncertainty. This study also found that a gravel size fraction (2-8mm), which is often ignored in modeling U(VI) sorption and desorption, is statistically significant to the U(VI) desorption in the sediment.« less

Microstructural Evaluations of Baseline HSR/EPM Disk Alloys

NASA Technical Reports Server (NTRS)

Gabb, Timothy P.; Garg, Anita; Ellis, David L.

2004-01-01

Six alloys representing two classes of powder metallurgy nickel-based superalloys were examined by transmission electron microscopy (TEM) and phase extraction. Alloys KM4, CH98, IN-100 and 456 are based on a Ni-18Co-12Cr composition while alloys Rene' 88 DT and SR 3 have lower Al and Co and higher Cr contents. The lambda size distributions were determined from quantitative image analysis of the TEM images. The volume fraction of lambda and carbides and the composition of the phases were determined by a combination of phase extraction and TEM. The results showed many similarities in lambda size distributions, grain boundary serrations, and grain boundary carbide frequencies between alloys KM4, CH98, 456, Rene' 88 DT and SR 3 when heat treated to give an approximate grain size of ASTM 6. The density of grain boundary carbides in KM4 was shown to substantially increase as the grain size increased. IN-100 and 456 subjected to a serration cooling heat treatment had much more complex lambda size distributions with very large intergranular and intragranular secondary lambda as well as finer than average cooling and aging lambda. The grain boundary carbides in IN-100 were similar to the other alloys, but 456 given the serration cooling heat treatment had a more variable density of grain boundary carbides. Examination of the phases extracted from the matrix showed that there were significant differences in the phase chemistries and elemental partitioning ratios between the various alloys.

Effects of debris-flow composition on runout and erosion

NASA Astrophysics Data System (ADS)

Haas, T. D.; Kleinhans, M. G.

2016-12-01

Predicting debris-flow runout is of major importance for hazard mitigation. Apart from topography and volume, runout depends on debris-flow composition (i.e., particle-size distribution and water content), but how is poorly understood. Moreover, debris flows can grow greatly in size by entrainment of bed material, enhancing their volume and thereby runout and hazardous impact. Debris-flow erosion rates also depend on debris-flow composition, but the relation between the two is largely unexplored. Composition thus strongly affects the dynamics of debris flows. We experimentally investigate the effects of composition on debris-flow runout and erosion. We find a clear optimum in the relations of runout with coarse-material fraction and clay fraction. Increasing coarse material concentration leads to larger runout. However, excess coarse material results in a large accumulation of coarse debris at the flow front and enhances diffusivity, increasing frontal friction and decreasing runout. Increasing clay content initially enhances runout, but too much clay leads to very viscous flows, reducing runout. We further find that debris-flow runout depends at least as much on composition as on topography. In general, erosion depth increases with basal shear stress in our experiments, while there is no correlation with grain collisional stress. There are substantial differences in the scour caused by different types of debris flows. Mean and maximum erosion depths generally become larger with increasing water fraction and grain size and decrease with increasing clay content. However, the erodibility of the very coarse-grained experimental debris flows is unrelated to basal shear stress. This relates to the relatively large influence of grain-collisional stress to the total bed stress in these flows (30-50%). The relative effect of grain-collisional stress is low in the other experimental debris flows (<5%) causing erosion to be largely controlled by basal shear stress. These results show that the erosive behaviour of debris flows may change from basal-shear stress dominated to grain-collisional stress dominated in increasingly coarse-grained debris flows. In short, this study improves our understanding of the effects of debris-flow composition on runout and erosion.

Magnetic hysteresis in small-grained CoxPd1-x nanowire arrays

NASA Astrophysics Data System (ADS)

Viqueira, M. S.; Pozo-López, G.; Urreta, S. E.; Condó, A. M.; Cornejo, D. R.; Fabietti, L. M.

2015-11-01

Co-Pd nanowires with small grain size are fabricated by AC electrodeposition into hexagonally ordered alumina pores, 20-35 nm in diameter and about 1 μm long. The effects of the alloy composition, the nanowire diameter and the grain size on the hysteresis properties are considered. X-ray diffraction indicates that the nanowires are single phase, a fcc Co-Pd solid solution; electron microscopy results show that they are polycrystalline, with randomly oriented grains (7-12 nm), smaller than the wire diameter. Nanowire arrays are ferromagnetic, with an easy magnetization axis parallel to the nanowire long axis. Both, the coercive field and the loop squareness monotonously increase with the Co content and with the grain size, but no clear correlation with the wire diameter is found. The Co and Co-rich nanowire arrays exhibit coercive fields and reduced remanence values quite insensitive to temperature in the range 4 K-300 K; on the contrary, in Pd-rich nanowires both magnitudes are smaller and they largely increase during cooling below 100 K. These behaviors are systematized by considering the strong dependences displayed by the magneto-crystalline anisotropy and the saturation magnetostriction on composition and temperature. At low temperatures the effective anisotropy value and the domain-wall width to grain size ratio drastically change, promoting less cooperative and harder nucleation modes.

Performance analysis of SA-3 missile second stage

NASA Technical Reports Server (NTRS)

Helmy, A. M.

1981-01-01

One SA-3 missile was disassembled. The constituents of the second stage were thoroughly investigated for geometrical details. The second stage slotted composite propellant grain was subjected to mechanical properties testing, physiochemical analyses, and burning rate measurements at different conditions. To determine the propellant performance parameters, the slotted composite propellant grain was machined into a set of small-size tubular grains. These grains were fired in a small size rocket motor with a set of interchangeable nozzles with different throat diameters. The firings were carried out at three different conditions. The data from test motor firings, physiochemical properties of the propellant, burning rate measurement results and geometrical details of the second stage motor, were used as input data in a computer program to compute the internal ballistic characteristics of the second stage.

The influence of grain size and composition on 1000 to 1400 K slow plastic flow properties of NiAl

NASA Technical Reports Server (NTRS)

Whittenberger, J. Daniel

1988-01-01

The compressive slow plastic flow behavior of several B2 crystal structure NiAl intermetallics has been studied in air between 1000 and 1400 K. Small grain-sized Ni-48.25 at. pct Al (of about 10 microns) was found to be stronger than the previously studied 17 microns diameter material. While grain refinement improved the strength at all test temperatures, the exact mechanism is not clear. Experiments at lower temperature revealed that composition as well as grain size can be an important factor, since Ni-49.2Al was weaker than Ni-48.25Al. Pronounced yield points were found during slow strain-rate testing at 1000 K; however, continued deformation appears to take place by the same mechanism(s) as found at high temperatures. Small changes in thermomechanical processing (TMP) schedules to fabricate Ni-49.2Al indicated that basic deformation characteristics (stress exponent and activation energy) are not affected; however, the preexponential term could be modified if TMP alters the grain structure.

Search for Large Presolar Silicate Grains in the QUE 99177 CR Chondrite

NASA Technical Reports Server (NTRS)

Nguyen, A. N.; Messenger, S.

2012-01-01

Silicates are among the most abundant pre-solar grain type, and their diverse chemical and isotopic compos-tions preserve detailed constraints on their stellar origins, condensation conditions, and nucleosynthetic and interstellar processes. Yet, owing to their small sizes, relatively few grains have been measured for isotopic compositions besides O and Si, and their mineralogy is poorly characterized. The average grain size (approx 270 nm) limits the number of analyses that can be conducted on a given grain, and their identification among solar system silicates introduces contaminating signal. These difficulties can be overcome by identifying large presolar silicate grains. However, such grains are very rare and only two approx 1 micron grains have been discovered. We are conducting a dedicated search for large presolar silicates in size-separated QUE 99177 matrix material. This primitive meteorite has among the highest abundance of presolar silicates

PROGRESS ON THE STUDY OF BETA TREATMENT OF URANIUM, AUGUST 1, 1961-NOVEMBER 30, 1961

DOE Office of Scientific and Technical Information (OSTI.GOV)

Russell, R.B.; Wolff, A.K.

Variables affecting the texture and grain size of uranium during beta treatment are summarized. The effects of composition (ingot versus dingot), prior delta condition, prior texture, pre-quenching air delay, rod or tube size, quenching medium and applied stress on grain size, distontion, and G/sub 3/ gradients in the final beta-treated shapes are described. (N.W.R.)

Prediction of as-cast grain size of inoculated aluminum alloys melt solidified under non-isothermal conditions

NASA Astrophysics Data System (ADS)

Du, Qiang; Li, Yanjun

2015-06-01

In this paper, a multi-scale as-cast grain size prediction model is proposed to predict as-cast grain size of inoculated aluminum alloys melt solidified under non-isothermal condition, i.e., the existence of temperature gradient. Given melt composition, inoculation and heat extraction boundary conditions, the model is able to predict maximum nucleation undercooling, cooling curve, primary phase solidification path and final as-cast grain size of binary alloys. The proposed model has been applied to two Al-Mg alloys, and comparison with laboratory and industrial solidification experimental results have been carried out. The preliminary conclusion is that the proposed model is a promising suitable microscopic model used within the multi-scale casting simulation modelling framework.

Grain-size-yield stress relationship: Analysis and computation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Meyers, M.A.; Benson, D.J.; Fu, H.H.

1999-07-01

The seminal contributions of Julia Weertman to the understanding of the mechanical properties of nanocrystalline materials will be briefly outlined. A constitutive equation predicting the effect of grain size on the yield stress of metals, based on the model proposed by M.A. Meyers and E. Ashworth, is discussed and extended to the nanocrystalline regime. At large grain sizes, it has the Hall-Petch form, and in the nanocrystalline domain the slope gradually decreases until it asymptotically approaches the flow stress of the grain boundaries. The material is envisaged as a composite, comprised of the grain interior, with flow stress {sigma}{sub fB},more » and grain boundary work-hardened layer, with flow stress {sigma}{sub fGB}. Three principal factors contribute to the grain-boundary hardening: (1) the grain boundaries act as barriers to plastic flow; (2) the grain boundaries act as dislocation sources; and (3) elastic anisotropy causes additional stresses in grain-boundary surroundings. The predictions of this model are compared with experimental measurements over the mono, micro, and nanocrystalline domains. Computational predictions are made of plastic flow as a function of grain size incorporating elastic and plastic anisotropy as well as differences of dislocation accumulation rate in grain boundary regions and grain interiors. This is the first plasticity calculation that accounts for grain size effects in a physically-based manner. 58 refs., 7 figs., 1 tab.« less

Sputter deposited titanium disilicide at high substrate temperatures

NASA Astrophysics Data System (ADS)

Tanielian, M.; Blackstone, S.; Lajos, R.

1984-08-01

Titanium disilicide films were sputter deposited from a composite TiSi2.1 target on <111> bare silicon wafers both at room temperature and at 600 °C. The room temperature as-deposited films require a 900 °C sintering step to reduce their resistivity. On the other hand, the as-deposited 600 °C films are fully reacted, polycrystalline, have no oxygen contamination, large grain sizes, and are oxidation resistant. Further annealing of these films at 900 °C produces no changes in their crystal structure, composition, resistivity, or grain size.

Physical processes dominate in shaping invertebrate assemblages in reef-associated sediments of an exposed Hawaiian coast

USGS Publications Warehouse

DeFelice, R.C.; Parrish, J.D.

2001-01-01

The invertebrate assemblages in sediments bordering exposed fringing reefs at Hanalei Bay, Kauai, Hawaii, were examined during July to September 1994. Densities of invertebrate animals larger than 0.5 mm in sediments of the bay ranged from counts of 10 260 m-2 in the fine carbonate sands of the central bay to 870 m-2 in the habitat dominated by terrigenous silt near the reef edge close to the Hanalei river mouth. Similar sediment types supported broadly similar infaunal communities. Within the primarily carbonate sediments, mean grain size and wave exposure appear to have an important influence on the community. Taxonomic richness, number of individuals, and diversity showed significant negative relationships with exposure to wave energy (as estimated by sand ripple wavelength). The number of individuals was also significantly correlated with mean grain size. Overall, polychaetes and small crustaceans were numerically dominant among the major taxonomic groups investigated. Macrophagous and microphagous polychaetes had significant, but opposite, associations with grain size. In addition, microphagous polychaetes were significantly negatively correlated with wave exposure. No habitat variable measured could explain the variation in percent composition of crustaceans or echinoderms in the sedimentary habitats. The percentage of gastropods in the community was significantly negatively correlated with grain size, grain-size standard deviation and exposure, and positively with percent organic carbon. Bivalves were significantly positively associated with depth and grain size. These strong relationships imply that, in Hanalei Bay, physical processes are especially important in influencing assemblage structure, and that community structure and composition vary continuously along environmental gradients.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tiegs, T.N.

The Cooperative Research and Development Agreement (CRADA) was to develop composites of TiC-Ni{sub 3}Al with refined grain microstructures for application in diesel engine fuel injection devices. Grain refinement is important for improved wear resistance and high strength for the applications of interest. Attrition milling effectively reduces the initial particle size and leads to a reduction of the final grain size. However, an increase in the oxygen content occurs concomitantly with the grinding operation and decreased densification of the compacts occurs during sintering.

Electrical conductivity enhancement in heterogeneously doped scandia-stabilized zirconia

NASA Astrophysics Data System (ADS)

Varanasi, Chakrapani; Juneja, Chetan; Chen, Christina; Kumar, Binod

Composites of 6 mol% scandia-stabilized zirconia materials (6ScSZ) and nanosize Al 2O 3 powder (0-30 wt.%) were prepared and characterized for electrical conductivity by the ac impedance method at various temperatures ranging from 300 to 950 °C. All the composites characterized showed improved conductivity at higher temperatures compared to the undoped ScSZ. An average conductivity of 0.12 S cm -1 was measured at 850 °C for 6ScSZ + 30 wt.% Al 2O 3 composite samples, an increase in conductivity up to 20% compared to the undoped 6ScSZ specimen at this temperature. Microstructural evaluation using scanning electron microscopy revealed that the ScSZ grain size was relatively unchanged up to 10 wt.% of Al 2O 3 additions. However, the grain size was reduced in samples with higher (20 and 30 wt.%) additions of Al 2O 3. Small grain size, reduced quantity of the 6ScSZ material (only 70%), and improved conductivity makes these ScSZ + 30 wt.% Al 2O 3 composites very attractive as electrolyte materials in view of their collective mechanical and electrical properties and cost requirements. The observed increase in conductivity values with the additions of an insulating Al 2O 3 phase is explained in light of the space charge regions at the 6ScSZ-Al 2O 3 grain boundaries.

Influence of fibre distribution and grain size on the mechanical behaviour of friction stir processed Mg–C composites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mertens, A., E-mail: anne.mertens@ulg.ac.be; Simar, A.; Adrien, J.

Short C fibres–Mg matrix composites have been produced by friction stir processing sandwiches made of a layer of C fabric stacked between two sheets of Mg alloy AZ31B or AZ91D. This novel processing technique can allow the easy production of large-scale metal matrix composites. The paper investigates the microstructure of FSPed C fibre–Mg composites in relation with the fragmentation of the C fibres during FSP and their influence on the tensile properties. 3D X-ray tomography reveals that the fibres orient like onion rings and are more or less fragmented depending on the local shear stress during the process. The fibremore » volume fraction can be increased from 2.3% to 7.1% by reducing the nugget volume, i.e. by using a higher advancing speed in AZ31B alloy or a stronger matrix alloy, like AZ91D alloy. A higher fibre volume fraction leads to a smaller grain size which brings about an increase of the composite yield strength by 15 to 25%. However, a higher fibre volume fraction also leads to a lower fracture strain. Fracture surface observations reveal that damage occurs by fibre/matrix decohesion along fibres oriented perpendicularly to the loading direction. - Graphical abstract: Display Omitted - Highlights: • C–Mg MMCs were produced by FSP sandwiches made of a C fabric between Mg sheets. • Fibre fragmentation and erosion is larger when the temperature reached during FSP is lower. • A lower advancing speed brings a lower fibre volume fraction and a lower grain size. • X-ray tomography reveals that fibres orient along the FSP material flow. • The fibres and grain size reduction increase the yield strength by 15 to 25%.« less

Gas-Grain Chemical Models: Inclusion of a Grain Size Distribution and a Study Of Young Stellar Objects in the Magellanic Clouds

NASA Astrophysics Data System (ADS)

Pauly, Tyler Andrew

2017-06-01

Computational models of interstellar gas-grain chemistry have aided in our understanding of star-forming regions. Chemical kinetics models rely on a network of chemical reactions and a set of physical conditions in which atomic and molecular species are allowed to form and react. We replace the canonical single grain-size in our chemical model MAGICKAL with a grain size distribution and analyze the effects on the chemical composition of the gas and grain surface in quiescent and collapsing dark cloud models. We find that a grain size distribution coupled with a temperature distribution across grain sizes can significantly affect the bulk ice composition when dust temperatures fall near critical values related to the surface binding energies of common interstellar chemical species. We then apply the updated model to a study of ice formation in the cold envelopes surrounding massive young stellar objects in the Magellanic Clouds. The Magellanic Clouds are local satellite galaxies of the Milky Way, and they provide nearby environments to study star formation at low metallicity. We expand the model calculation of dust temperature to include a treatment for increased interstellar radiation field intensity; we vary the radiation field to model the elevated dust temperatures observed in the Magellanic Clouds. We also adjust the initial elemental abundances used in the model, guided by observations of Magellanic Cloud HII regions. We are able to reproduce the relative ice fractions observed, indicating that metal depletion and elevated grain temperature are important drivers of the envelope ice composition. The observed shortfall in CO in Small Magellanic Cloud sources can be explained by a combination of reduced carbon abundance and increased grain temperatures. The models indicate that a large variation in radiation field strength is required to match the range of observed LMC abundances. CH 3OH abundance is found to be enhanced (relative to total carbon abundance) in low-metallicity models, providing seed material for complex organic molecule formation. We conclude with a preliminary study of the recently discovered hot core in the Large Magellanic Cloud; we create a grid of models to simulate hot core formation in Magellanic Cloud environments, comparing them to models and observations of well-characterized galactic counterparts.

Characterisation of a garnet population from the Sikkim Himalaya: implications for the mechanisms and rates of porphyroblast crystallisation

NASA Astrophysics Data System (ADS)

George, Freya; Gaidies, Fred

2016-04-01

Analysis of porphyroblast distribution in metamorphic rocks yields insight into the processes controlling metamorphic reaction rates. By coupling this textural record with microprobe analysis and phase-equilibria and diffusion modelling, a detailed view of the nucleation and growth history of metamorphic minerals can be obtained. In this study, we comprehensively characterise the 3D distribution and compositional variation of a garnet population in a garnet-grade pelitic schist of the Lesser Himalayan Sequence (Sikkim), in order to investigate both the rates and kinetic controls of porphyroblastic crystallisation. Quantification of the size, shape and spatial distribution of garnet using high-resolution μ-computed X-ray tomography and statistical analysis reveals a log-normal crystal size distribution, systematic variation of aspect ratio with crystal size, and a significantly clustered garnet texture in the study sample. The latter is indicative of interface-controlled nucleation and growth, with nucleation sites controlled principally by a heterogeneous precursor assemblage. At length-scales less than 0.7 mm, there is evidence for adjacent grains that are on average smaller than the mean size of the population; this minor ordering is attributed to secondary redistribution of porphyroblast centers and reduction of crystal sizes due to syn-kinematic growth and resorption, respectively. Geochemical traverses through centrally sectioned garnet crystals of variable size highlight several features: (1) core compositions of even the smallest crystals preserve primary prograde growth zonation, with little evidence for diffusional modification in any crystal size; (2) rim compositions are within error between grains, suggestive of sample-scale equilibration of the growth medium at the time of cessation of crystallisation; (3) different grains of equal radii display equivalent compositional zoning; and (4) gradients of compositional profiles display a steepening trend in progressively smaller grain sizes, converse to anticipated trends based on classic kinetic crystallisation theory. The observed systematic behaviour is interpreted to reflect interface-controlled rates of crystallisation, with a decrease in the rate of crystal growth of newly nucleated grains as the crystallisation interval proceeds. Numerical simulations of garnet growth successfully reproduce observed core and rim compositions, and simulations of intracrystalline diffusion yield rapid heating/cooling rates along the P-T path, in excess of 100 °C/Ma. Radial garnet crystallisation is correspondingly rapid, with minimum growth rates of 1.5 mm/Ma in the smallest crystals. Simulations suggest progressive nucleation of new generations of garnet occurred with an exponentially decreasing frequency along the prograde path; however, measured gradients indicate that core compositions developed more slowly than predicted by the model, potentially resulting in a more evenly distributed pattern of nucleation.

Grain-Size Dynamics Beneath Mid-Ocean Ridges: Implications for Permeability and Melt Extraction

NASA Astrophysics Data System (ADS)

Turner, A. J.; Katz, R. F.; Behn, M. D.

2014-12-01

The permeability structure of the sub-ridge mantle plays an important role in how melt is focused and extracted at mid-ocean ridges. Permeability is controlled by porosity and the grain size of the solid mantle matrix, which is in turn controlled by the deformation conditions. To date, models of grain size evolution and mantle deformation have not been coupled to determine the influence of spatial variations in grain-size on the permeability structure at mid-ocean ridges. Rather, current models typically assume a constant grain size for the whole domain [1]. Here, we use 2-D numerical models to evaluate the influence of grain-size variability on the permeability structure beneath a mid-ocean ridge and use these results to speculate on the consequences for melt focusing and extraction. We construct a two-dimensional, single phase model for the steady-state grain size beneath a mid-ocean ridge. The model employs a composite rheology of diffusion creep, dislocation creep, dislocation accommodated grain boundary sliding, and a brittle stress limiter. Grain size is calculated using the "wattmeter" model of Austin and Evans [2]. We investigate the sensitivity of the model to global variations in grain growth exponent, potential temperature, spreading-rate, and grain boundary sliding parameters [3,4]. Our model predicts that permeability varies by two orders of magnitude due to the spatial variability of grain size within the expected melt region of a mid-ocean ridge. The predicted permeability structure suggests grain size may promote focusing of melt towards the ridge axis. Furthermore, the calculated grain size structure should focus melt from a greater depth than models that exclude grain-size variability. Future work will involve evaluating this hypothesis by implementing grain-size dynamics within a two-phase mid-ocean ridge model. The developments of such a model will be discussed. References: [1] R. F. Katz, Journal of Petrology, volume 49, issue 12, page 2099, 2008. [2] N. J. Austin and B. Evans, Geology, 35:354, 2007. [3] G. Hirth and D. Kohlstedt, In Inside the Subduction Factory, volume 138 of AGU Geophysical Monograph, 2003. [4] L. N. Hansen et al., JGR (Solid Earth), 116:B08201, 2011.

Fluid Percolation Within AN Ocean-Continent Transition

NASA Astrophysics Data System (ADS)

Kaczmarek, M.; Reddy, S. M.

2013-12-01

Divergent plate boundaries, such as ocean-continent transitions (OCT) are the perfect target to study mechanisms activated during extension leading to localisation of deformation. The Platta-Totalp massifs in the Eastern Central Alps (Grison, Switzerland) represent a type example of a zone of exhumed continental mantle and offer a complete stratigraphic sequence of an OCT. A detailed study of the geochemistry and microstructures is undertaken to characterise the deformation in such setting. The mantle rocks are spinel lherzolites and harzburgites, into which gabbros and basaltic dykes were intruded, and are partially covered by ophicarbonates. Previous work across the Platta reveals that mantle rocks close to the continent may represent spinel peridotite mixed with (garnet)-pyroxenite layers while the ultramafic rocks at some distance from the continent are pyroxenite-poor peridotites that equilibrated in the plagioclase stability field (Muntener et al. 2004). Fieldwork across the mantle sequence shows localization of deformation with metric or centimetric shear-zones. Peridotites in shear-zones close to the continent have an ultra-mylonitic texture, and contain amphibole testifying fluid percolation. In a centimetric shear-zone amphibole is observed within a matrix made up of a mixture of pyroxenes, olivine, amphibole and spinel with a grain size from 1 to 8 μm, and as round grains (grain size from 30 to 50μm) embedded in the fine-grained matrix. The host peridotite, which is also deformed, contains larger grains of amphibole with a grain size up to 400 μm. The chemical composition of the amphibole changes from large to small grains, increasing in K2O and decreasing in TiO2 (wt%) indicating an evolution of the percolating fluid during the localisation of deformation. Another ultra-mylonite (grain size ~ 5μm) from the same mantle sequence displays unmixed areas of clinopyroxene-amphibole and olivine-orthopyroxene, which are folded together. The chemical composition of the amphibole has a lower TiO2 and K2O content than in the other sample. From the continent to the ocean, the clinopyroxene shows a decrease in Na2O for a similar Cr2O3 (wt%) content. However, clinopyroxene compositions indicate a decrease in Al2O3, Na2O, and Cr2O3 (wt%) and homogenisation of the compositions in the fine-grained matrix in the entire sequence suggesting a concordant decrease in temperature. A detailed study of the peridotite textures and geochemistry is combined with analysis of the crystallographic preferred orientation using the EBSD method to determine the deformation mechanisms activated during extension. Mapping of individual porphyroclastic clinopyroxenes and large grains of amphiboles within the host (deformed) peridotite display cumulative misorientation angles up to 35 degrees. Moreover, the patterns of dispersion indicate intra-grain composite deformation leading to a grain size reduction. Our preliminary results indicate fluid percolation and chemical variation during localisation of deformation. This study will constrain the localisation of the deformation related to decreasing temperatures and fluid percolation within extensional setting such as OCT. Ref: Muntener et al. 2004, EPSL, 221, 293-308

Spectral Profiler Probe for In Situ Snow Grain Size and Composition Stratigraphy

NASA Technical Reports Server (NTRS)

Berisford, Daniel F.; Molotch, Noah P.; Painter, Thomas

2012-01-01

An ultimate goal of the climate change, snow science, and hydrology communities is to measure snow water equivalent (SWE) from satellite measurements. Seasonal SWE is highly sensitive to climate change and provides fresh water for much of the world population. Snowmelt from mountainous regions represents the dominant water source for 60 million people in the United States and over one billion people globally. Determination of snow grain sizes comprising mountain snowpack is critical for predicting snow meltwater runoff, understanding physical properties and radiation balance, and providing necessary input for interpreting satellite measurements. Both microwave emission and radar backscatter from the snow are dominated by the snow grain size stratigraphy. As a result, retrieval algorithms for measuring snow water equivalents from orbiting satellites is largely hindered by inadequate knowledge of grain size.

Comet C2012 S1 (ISON)s Carbon-rich and Micron-size-dominated Coma Dust

NASA Technical Reports Server (NTRS)

Wooden, D.; De Buizer, J.; Kelley, M.; Sitko, M.; Woodward, C.; Harker, D.; Reach, W.; Russell, R.; Kim, D.; Yanamadra-Fisher, P.;

Relation between grain size and modal composition in deep-sea gravity-flow deposits. Example from the Voirons Flysch (Gurnigel nappe, Chablais Prealps, France)

NASA Astrophysics Data System (ADS)

Ragusa, Jérémy; Kindler, Pascal

2016-04-01

A coupled analysis of modal composition, grain size and sedimentary features of gravity-flow deposits in the Gurnigel nappe shows that the transition from coarse proximal to fine distal deposits is accompanied by a change in composition from siliciclastic to calcareous. Such compositional variation should be taken into account when interpretating deep-sea deposits if sampling is restricted to a single part of the fan. The Chablais Prealps (Haute-Savoie, France) represent a well-preserved accretionary wedge in the Western Alps. They comprise a stack of northward-thrusted sedimentary cover nappes originating from the Ultrahelvetic realm (distal part of the European margin) to the southern part of the Piemont Ocean. The present study focuses on the Voirons Flysch, belonging to the Gurnigel nappe, which includes four formations consisting of gravity-flow deposits (from bottom to top): (1) the Voirons Sandstone Fm., composed of channel to lobe deposits; (2) the Vouan Conglomerate Fm., represented by the proximal part of a channel system; (3) the Boëge Marls Fm., constituted by distal lobe deposits; finally, (4) the Bruant Sandstone Fm., which consists in channel to lobe deposits. Recent biostratigraphic results using planktonic foraminifers attributed a Middle to Late Eocene age to the Voirons Flysch, which was formerly believed to range from the Paleocene to the Middle Eocene (based on calcareous nannofossils). A total of 270 thin sections with stained feldspars were prepared, representing the four formations of the Voirons Flysch. Circa 300 extrabasinal grains were counted per thin section using the classic Indiana method. In addition, the quantity of intrabasinal grains (i.e. bioclasts, glauconite), cement and porosity was analysed. Cement was stained with alizarine and potassium ferrocyanide. 200 grain-size measurements on ca. 100 samples were performed using 3D conversion and statistical moment analysis. Sedimentary observations for each sampled bed were categorized following Mutti's turbiditic facies scheme. Cluster analysis on the composition of major grains discriminated 10 clusters which are merged into seven petrofacies (P1 - P7) following optical observations under the microscope: P1: poorly cemented porous arenite; P2: all porosity are filled by calcitic cement; P3: well-cemented volcano-clastic arenite; P4: red algae-rich highly cemented arenite to calcarenite; P5: highly cemented arenite; P6: globigerina-rich laminated calcarenite and P7: glauconitic quartzarenite. Grain-size distribution is grouped following the petrofacies. They provide a homogeneous distribution within each petrofacies with a gradual fining and progressively increasing sorting from P1 to P7. Moreover, Mutti's facies distribution indicates a progressive change towards more distal environments: from channel facies (F2 to F5) in P1-P3 to lobe facies (F8 to F9) in P4-P6. The washed composition of the P7 petrofacies is interpreted as distal turbidites that were reworked by bottom currents. The results presented here reveal a link between sand composition, grain size and gravity-flow facies. They highlight that composition of gravity flows is modified during their basinward transport. Consequently, coarse proximal deposits are more siliciclastic with limited filling of voids due to low carbonate contents. On the contrary, carbonate content increases significantly in the fine-grained calcarenites of the distal petrofacies. In distal settings, the segregation of light and porous foraminifera from the heavier siliciclastic fraction occurs under the increasing importance of traction currents.

Origin and diversity of testate amoebae shell composition: Example of Bullinularia indica living in Sphagnum capillifolium.

PubMed

Delaine, Maxence; Bernard, Nadine; Gilbert, Daniel; Recourt, Philippe; Armynot du Châtelet, Eric

2017-06-01

Testate amoebae are free-living shelled protists that build a wide range of shells with various sizes, shapes, and compositions. Recent studies showed that xenosomic testate amoebae shells could be indicators of atmospheric particulate matter (PM) deposition. However, no study has yet been conducted to assess the intra-specific mineral, organic, and biologic grain diversity of a single xenosomic species in a natural undisturbed environment. This study aims at providing new information about grain selection to develop the potential use of xenosomic testate amoebae shells as bioindicators of the multiple-origin mineral/organic diversity of their proximal environment. To fulfil these objectives, we analysed the shell content of 38 Bullinularia indica individuals, a single xenosomic testate amoeba species living in Sphagnum capillifolium, by scanning electron microscope (SEM) coupled with X-ray spectroscopy. The shells exhibited high diversities of mineral, organic, and biomineral grains, which confirms their capability to recycle xenosomes. Mineral grain diversity and size of B. indica matched those of the atmospheric natural mineral PM deposited in the peatbog. Calculation of grain size sorting revealed a discrete selection of grains agglutinated by B. indica. These results are a first step towards understanding the mechanisms of particle selection by xenosomic testate amoebae in natural conditions. Copyright © 2017 Elsevier GmbH. All rights reserved.

Effect of different thickness h-BN coatings on interface shear strength of quartz fiber reinforced Sisbnd Osbnd Csbnd N composite

NASA Astrophysics Data System (ADS)

Wang, Shubin; Zheng, Yu

2014-02-01

Hexagonal boron nitride (h-BN) coatings with different thickness were prepared on quartz fibers to improve mechanical properties of quartz fiber reinforced Sisbnd Osbnd Csbnd N composite. Scanning electron microscopy (SEM), push-out test and single edge notched beam (SENB) in three point bending test were employed to study morphology, interface shear strength and fracture toughness of the composite. The results showed that h-BN coatings changed the crack growth direction and weaken the interface shear strength efficiently. When the h-BN coating was 308.2 nm, the interface shear strength was about 5.2 MPa, which was about one-quarter of that of the sample without h-BN coatings. After the heating process for obtaining composite, the h-BN nanometer-sized grains would grow up to micron-sized hexagonal grains. Different thickness h-BN coatings had different structure. When the coatings were relatively thin, the hexagonal grains were single layer structure, and when the coatings were thicker, the hexagonal grains were multiple layer structure. This multiple layer interface phase would consume more power of cracks, thus interface shear strength of the composite decreased steadily with the increasing of h-BN coatings thickness. When the coating thickness was 238.8 nm, KIC reaches the peak value 3.8 MPa m1/2, which was more than two times of that of composites without h-BN coatings.

Metamorphic reactions, grain size reduction and deformation of mafic lower crustal rocks

NASA Astrophysics Data System (ADS)

Degli Alessandrini, Giulia; Menegon, Luca; Beltrando, Marco; Dijkstra, Arjan; Anderson, Mark

2016-04-01

This study investigates grain-scale deformation mechanisms associated with strain localization in the mafic continental lower crust, with particular focus on the role of syn-kinematic metamorphic reactions and their product - symplectites - in promoting grain size reduction and phase mixing. The investigated shear zone is hosted in the Finero mafic-ultramafic complex in the Italian Southern Alps. Shearing occurred at T ≥ 650° C and P ≥ 0.4-0.6 GPa. The shear zone reworks both mafic and ultramafic lithologies and displays anastomosing patterns of (ultra)mylonitic high strain zones wrapping less foliated, weakly deformed low strain domains. Field and microstructural observations indicate that different compositional layers of the shear zone responded differently to deformation, resulting in strain partitioning. Four distinct microstructural domains have been identified: (1) an ultramylonitic domain characterized by an amph + pl matrix (grain size < 30μm) with large amphibole porphyroclasts (grain size between 200μm and 5000μm) and rare garnets; (2) a domain rich in garnet porphyroclasts embedded in a matrix of monomineralic plagioclase displaying a core and mantle structure (average grain size 45μm) (3) a metagabbroic domain with porphyroclasts of clinopyroxene, orthopyroxene and garnets (200μm average grain size) wrapped by monomineralic ribbons of recrystallized plagioclase and (4) a garnet-free ultramylonitic domain composed of an intermixed amph + cpx + opx + pl matrix (6μm average grain size). In these domains, each porphyroclastic mineral responds differently to deformation: amphibole readily breaks down to symplectitic intergrowths of amph + pl or opx + pl. Garnet undergoes fracturing (in domain 2) or reacts to give symplectites of pl + opx (in domain 3). Plagioclase dynamically recrystallizes in mono-phase aggregates, whereas clinopyroxene undergoes fracturing and orthopyroxene undergoes plastic deformation. The behaviour of the different phases and their relative abundance in the layers are believed to influence the deformation of the layers themselves. In symplectite-rich layers (domains 1, 4) deformation is localised, grain-size is below 30μm and phases are well mixed. On the other hand, in pyroxene or plagioclase-rich layers, deformation is less localised, the phases are less mixed and the grain size is larger (domain 2, 3). These preliminary results suggest that syn-kinematic metamorphic reactions forming symplectites played an essential role in grain size reduction, phase mixing and strain localization. We speculate that the compositional domains with symplectites localized deformation more efficiently, by activation of grain size sensitive creep, most likely because those domains were originally more hydrated than the others. On the contrary, domains without symplectites accommodated deformation less efficiently, either through fracturing (clinopyroxene, garnet) or dislocation creep + recrystallization (orthopyroxene, plagioclase).

Charging of Individual Micron-Size Interstellar/Planetary Dust Grains by Secondary Electron Emissions

NASA Technical Reports Server (NTRS)

Tankosic, D.; Abbas, M. M.

2012-01-01

Dust grains in various astrophysical environments are generally charged electrostatically by photoelectric emissions with UV/X-ray radiation, as well as by electron/ion impact. Knowledge of physical and optical properties of individual dust grains is required for understanding of the physical and dynamical processes in space environments and the role of dust in formation of stellar and planetary systems. In this paper, we discuss experimental results on dust charging by electron impact, where low energy electrons are scattered or stick to the dust grains, thereby charging the dust grains negatively, and at sufficiently high energies the incident electrons penetrate the grain leading to excitation and emission of electrons referred to as secondary electron emission (SEE). Currently, very limited experimental data are available for charging of individual micron-size dust grains, particularly by low energy electron impact. Available theoretical models based on the Sternglass equation (Sternglass, 1954) are applicable for neutral, planar, and bulk surfaces only. However, charging properties of individual micron-size dust grains are expected to be different from the values measured on bulk materials. Our recent experimental results on individual, positively charged, micron-size lunar dust grains levitated in an electrodynamic balance facility (at NASA-MSFC) indicate that the SEE by electron impact is a complex process. The electron impact may lead to charging or discharging of dust grains depending upon the grain size, surface potential, electron energy, electron flux, grain composition, and configuration (e.g. Abbas et al, 2010). Here we discuss the complex nature of SEE charging properties of individual micron-size lunar dust grains and silica microspheres.

Refining Mechanism of 7075 Al Alloy by In-Situ TiB₂ Particles.

PubMed

Gan, Guisheng; Yang, Bin; Zhang, Bo; Jiang, Xin; Shi, Yunlong; Wu, Yiping

2017-02-04

The nucleation undercooling of TiB₂/7075 Al matrix composites, the microstructure observed after solidification at different cooling rate, and the size and distribution of TiB₂ particles were investigated. The experimental results have shown that the grain sizes of TiB₂/7075 Al matrix composites firstly decreased, then increased, and finally decreased again with the increase of TiB₂ content. The nucleation undercooling of TiB₂/7075 Al matrix composites first increased, then decreased, and finally increased again with the increase of TiB₂ content when the cooling rates was 5 and 10 °C/min respectively, but kept decreasing with the increase of TiB₂ content at a cooling rate of 20 °C/min. The melting and solidification process showed no significant change with the decrease of cooling rate in 9.0% TiB₂/7075 Al matrix composites. Most small particles can act as heterogeneous nucleus, which induced grain growth and were captured into the grain by the solid/liquid interface. At the same time, most of the larger particles and a minority of the small TiB₂ particles are pushed into the grain boundary; locating in the grain boundary can hinder the Al atoms from diffusing during the solidification process and restrain α-Al phase growth. The influence of particles shifted from dominating by locating to dominating by nucleation as the quantity of TiB₂ particles increased.

Effect of Cold Forging on Microstructure and MechanicalProperties of Al/SiC Composites

NASA Astrophysics Data System (ADS)

Hanamantraygouda, M. B.; Shivakumar, B. P., Dr; Siddappa, P. N.; Sampathkumar, L.; Prashanth, L.

2018-02-01

The objective of this work was to investigate the effect of cold forging on mechanical properties and microstructural study of Al MMCs, at different wt% of SiC and forging cycle. The Al-SiC composite material was fabricated by stir casting method at different weight percentage of SiC such as 2.5, 5, 7.5 and 10%. Further, the deformation characteristics during open-die forging of Al-SiC composite at cold conditions was investigated. Cast and forged composite material was subjected to hardness test, tensile test and impact test. The grain size, microstructure behaviour was investigated using optical microscope. The results show that hardness and strength of Al-SiC composite increases and ductility decreases as compared to Al alloy in both as-cast and forged conditions. Optical microscope images showed that the distribution of SiC in Al matrix was more homogeneous in a forged composite as compared to cast one and reduction of porosity was found. Further, it showed that due to forging cycle the grain size was reduced by 30% to 35% from initial size.

Effect of preparation conditions on the characteristics and photocatalytic activity of TiO2/purified diatomite composite photocatalysts

NASA Astrophysics Data System (ADS)

Sun, Zhiming; Hu, Zhibo; Yan, Yang; Zheng, Shuilin

2014-09-01

TiO2/purified diatomite composite materials were prepared through a modified hydrolysis-deposition method under low temperature using titanium tetrachloride as precursor combined with a calcination crystallization process. The microstructure and crystalline phases of the obtained composites prepared under different preparation conditions were characterized by high resolution scanning electron microscope (SEM) and X-ray diffraction (XRD), respectively. The photocatalytic performance of TiO2/purified diatomite composites was evaluated by Rhodamine B as the target pollutant under UV irradiation, and the optimum preparation conditions of composites were obtained. The TiO2 crystal form in composites prepared under optimum conditions was anatase, the grain size of which was 34.12 nm. The relationships between structure and property of composite materials were analyzed and discussed. It is indicated that the TiO2 nanoparticles uniformly dispersed on the surface of diatoms, and the photocatalytic performance of the composite materials was mainly determined by the dispersity and grain size of loaded TiO2 nanoparticles.

Grain optical properties

NASA Technical Reports Server (NTRS)

Hanner, Martha

1988-01-01

The optical properties of small grains provide the link between the infrared observations presented in Chapter 1 and the dust composition described in Chapter 3. In this session, the optical properties were discussed from the viewpoint of modeling the emission from the dust coma and the scattering in order to draw inference about the dust size distribution and composition. The optical properties are applied to the analysis of the infrared data in several ways, and these different uses should be kept in mind when judging the validity of the methods for applying optical constants to real grains.

Laboratory Reflectance Spectra in the Middle-infrared: Effects of Grain Size on Spectral Features

NASA Astrophysics Data System (ADS)

Le Bras, A.; Erard, S.; Fulchignoni, M.

2000-10-01

Since spectral mineral features are sensitive to surface parameters, interpretation of remote-sensing asteroids spectra in terms of mineral composition is not easy nor unique, and laboratory spectra are needed in order to understand the influence of each parameter. We developped an experimental program at IAS, using the 2.5-120 microns interferometer spectrometer, to study the influence of surface parameters on mineral features. We present here the results obtained variing the grain size. We studied grain size effects with two types of terrestrial rocks: anorthosite (bright) and basalte (dark) in the 2-40 microns range. We observed variations of the spectral contrast with grain size, shifts in wavelengths and variations of the intensity of some characteristic spectral features, and appearence of transparency features at wavelengths longer than 8 microns.

Bonanza: An extremely large dust grain from a supernova

NASA Astrophysics Data System (ADS)

Gyngard, Frank; Jadhav, Manavi; Nittler, Larry R.; Stroud, Rhonda M.; Zinner, Ernst

2018-01-01

We report the morphology, microstructure, and isotopic composition of the largest SiC stardust grain known to have condensed from a supernova. The 25-μm diameter grain, termed Bonanza, was found in an acid-resistant residue of the Murchison meteorite. Grains of such large size have neither been observed around supernovae nor predicted to form in stellar environments. The large size of Bonanza has allowed the measurement of the isotopic composition of more elements in it than any other previous presolar grain, including: Li, B, C, N, Mg, Al, Si, S, Ca, Ti, Fe, and Ni. Bonanza exhibits large isotopic anomalies in the elements C, N, Mg, Si, Ca, Ti, Fe, and Ni typical of an astrophysical origin in ejecta of a Type II core-collapse supernova and comparable to those previously observed for other presolar SiC grains of type X. Additionally, we extracted multiple focused ion beam lift-out sections from different regions of the grain. Our transmission electron microscopy demonstrates that the crystalline order varies at the micrometer scale, and includes rare, higher order polytype domains (e.g., 15 R). Analyses with STEM-EDS show Bonanza contains a heterogeneous distribution of subgrains with sizes ranging from <10 nm to >100 nm of Ti(N, C); Fe, Ni-rich grains with variable Fe:Ni; and (Al, Mg)N. Bonanza also has the highest ever inferred initial 26Al/27Al ratio, consistent with its supernova origin. This unique grain affords us the largest expanse of data, both microstructurally and isotopically, to compare with detailed calculations of nucleosynthesis and dust condensation in supernovae.

Experimental study of the effect of grain sizes in a bimodal mixture on bed slope, bed texture, and the transition to washload

NASA Astrophysics Data System (ADS)

Hill, Kimberly M.; Gaffney, John; Baumgardner, Sarah; Wilcock, Peter; Paola, Chris

2017-01-01

When fine sediment is added to a coarse-grained system, the mobility and composition of the bed can change dramatically. We conducted a series of flume experiments to determine how the size of fine particles introduced to an active gravel bed influences the mobility and composition of the bed. We initiated our experiments using a constant water discharge and feed rate of gravel. After the system reached steady state, we doubled the feed rate by supplying a second sediment of equal or lesser size, creating size ratios from 1:1 to 1:150. As we decreased the relative size of the fine particles, the system transitioned among three regimes: (1) For particle size ratios close to one, the bed slope increased to transport the additional load of similar-sized particles. The bed surface remained planar and unchanged. (2) For intermediate particle size ratios, the bed slope decreased with the additional fines. The bed surface became patchy with regions of fine and coarse grains. (3) For the largest particle size ratios (the smallest fines), the bed slope remained relatively unchanged. The subsurface became clogged with fine sediment, but fine particles were not present in the surface layer. This third regime constitutes washload, defined by those fractions that do not affect bed-material transport conditions. Our results indicate washload should be defined in terms of three conditions: small grain size relative to that of the bed material, full suspension based on the Rouse number, and a small rate of fine sediment supply relative to transport capacity.

Only pick the right grains: Modelling the bias due to subjective grain-size interval selection for chronometric and fingerprinting approaches.

NASA Astrophysics Data System (ADS)

Dietze, Michael; Fuchs, Margret; Kreutzer, Sebastian

2016-04-01

Many modern approaches of radiometric dating or geochemical fingerprinting rely on sampling sedimentary deposits. A key assumption of most concepts is that the extracted grain-size fraction of the sampled sediment adequately represents the actual process to be dated or the source area to be fingerprinted. However, these assumptions are not always well constrained. Rather, they have to align with arbitrary, method-determined size intervals, such as "coarse grain" or "fine grain" with partly even different definitions. Such arbitrary intervals violate principal process-based concepts of sediment transport and can thus introduce significant bias to the analysis outcome (i.e., a deviation of the measured from the true value). We present a flexible numerical framework (numOlum) for the statistical programming language R that allows quantifying the bias due to any given analysis size interval for different types of sediment deposits. This framework is applied to synthetic samples from the realms of luminescence dating and geochemical fingerprinting, i.e. a virtual reworked loess section. We show independent validation data from artificially dosed and subsequently mixed grain-size proportions and we present a statistical approach (end-member modelling analysis, EMMA) that allows accounting for the effect of measuring the compound dosimetric history or geochemical composition of a sample. EMMA separates polymodal grain-size distributions into the underlying transport process-related distributions and their contribution to each sample. These underlying distributions can then be used to adjust grain-size preparation intervals to minimise the incorporation of "undesired" grain-size fractions.

Grain size dependent phase stabilities and presence of a monoclinic (Pm) phase in the morphotropic phase boundary region of (1-x)Bi(Mg1/2Ti1/2)O3-xPbTiO3 piezoceramics

NASA Astrophysics Data System (ADS)

Upadhyay, Ashutosh; Singh, Akhilesh Kumar

2015-04-01

Results of the room temperature structural studies on (1-x)Bi(Mg1/2Ti1/2)O3-xPbTiO3 ceramics using Rietveld analysis of the powder x-ray diffraction data in the composition range 0.28 ≤ x ≤ 0.45 are presented. The morphotropic phase boundary region exhibits coexistence of monoclinic (space group Pm) and tetragonal (space group P4 mm) phases in the composition range 0.33 ≤ x ≤ 0.40. The structure is nearly single phase monoclinic (space group Pm) in the composition range 0.28 ≤ x ≤ 0.32. The structure for the compositions with x ≥ 0.45 is found to be predominantly tetragonal with space group P4 mm. Rietveld refinement of the structure rules out the coexistence of rhombohedral and tetragonal phases in the morphotropic phase boundary region reported by earlier authors. The Rietveld structure analysis for the sample x = .35 calcined at various temperatures reveals that phase fraction of the coexisting phases in the morphotropic phase boundary region varies with grain size. The structural parameters of the two coexisting phases also change slightly with changing grain size.

Effects of Co contents on the microstructures and properties of the electrodeposited NiCo–Zr composite coatings

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cai, Fei; Jiang, Chuanhai, E-mail: chuanhaijiang1963@163.com; Zhao, Yuantao

2015-05-15

Highlights: • The novel NiCo–Zr coatings were prepared by electro-deposition. • Surface morphology, crystal structure, grain size and microstrain were examined. • Texture, residual stress and corrosion resistance were investigated. • Addition of Co increased the hardness and corrosion resistance of the coatings. - Abstract: In this study, the NiCo–Zr composite coatings were prepared from the electrolytes with different Co{sup 2+} concentrations by electrodeposition method. The effects of Co contents on the crystal structure, surface morphology, grain size, microstrain and residual stress were examined by X-ray diffractometer (XRD), field emission scanning electron microscopy (FESEM), Energy dispersive X-ray spectroscopy (EDX) andmore » atomic force microscope (AFM). The corrosion resistance of the composite coatings was also examined by the potentiodynamic polarization and electrochemical impedance (EIS) measurements. The results revealed that the crystal structures of the coatings were dependent on the Co contents and addition of Co content of 58 wt% resulted in the formation of hexagonal (hcp) Co. The increasing Co contents in the NiCo–Zr composite coatings resulted in the smoother and more compact surface, decreased the grain size and increased the microstrain. The micro-hardness and residual stress also increased with increasing Co contents. The addition of Co increased the corrosion resistance of the NiCo–Zr composite coatings compared with the Ni–Zr coating while the corrosion resistance of the NiCo–Zr composite coatings decreased as the Co contents increased.« less

Deposition of Nanostructured Thin Film from Size-Classified Nanoparticles

NASA Technical Reports Server (NTRS)

Camata, Renato P.; Cunningham, Nicholas C.; Seol, Kwang Soo; Okada, Yoshiki; Takeuchi, Kazuo

2003-01-01

Materials comprising nanometer-sized grains (approximately 1_50 nm) exhibit properties dramatically different from those of their homogeneous and uniform counterparts. These properties vary with size, shape, and composition of nanoscale grains. Thus, nanoparticles may be used as building blocks to engineer tailor-made artificial materials with desired properties, such as non-linear optical absorption, tunable light emission, charge-storage behavior, selective catalytic activity, and countless other characteristics. This bottom-up engineering approach requires exquisite control over nanoparticle size, shape, and composition. We describe the design and characterization of an aerosol system conceived for the deposition of size classified nanoparticles whose performance is consistent with these strict demands. A nanoparticle aerosol is generated by laser ablation and sorted according to size using a differential mobility analyzer. Nanoparticles within a chosen window of sizes (e.g., (8.0 plus or minus 0.6) nm) are deposited electrostatically on a surface forming a film of the desired material. The system allows the assembly and engineering of thin films using size-classified nanoparticles as building blocks.

Electron backscatter diffraction analysis of Nb3Al multifilamentary strands prepared by rapid heating, quenching and transformation annealing

NASA Astrophysics Data System (ADS)

Takeuchi, T.; Tsuchiya, K.; Saeda, M.; Banno, N.; Kikuchi, A.; Iijima, Y.

2010-12-01

To enhance the non-Cu critical current density Jc at 15 T and 4.2 K (1000 A mm - 2 at present) we have endeavoured to refine the grain size of rapid heating, quenching and transformation (RHQT)-processed Nb3Al. In the present study, the grain boundary structures of RHQT-processed Nb3Al were examined by electron backscatter diffraction (EBSD) because transgranular fracture prevents the observation of fractured cross sections of Nb3Al to statistically determine the grain size. The grain size distributions of body-centred-cubic supersaturated-solid-solution Nb(Al)ss and A15 Nb3Al filaments were measured for grains misoriented by more than 2°, 5° and 15°. A mixed grain structure, which consists of a few large grains (>25 µm) and many small grains (<1 µm), was observed for an Nb3Al filament that had been transformed from non-deformed Nb(Al)ss. Plastic deformation that had been made between the rapid heating and quenching steps and the transformation step apparently homogenized the grain size distribution and then reduced the average grain size. The misorientation angle distributions of Nb(Al)ss and Nb3Al were also measured and compared with each other. A clear relationship between the Jc and the inverse grain size was not confirmed for the RHQT Nb3Al conductors examined in the present study, which indicates the importance of making a filament compositionally homogeneous to obtain a high Jc.

Effects of plastic deformation on microstructure and superplasticity of the in situ Al3Ti/2024Al composites

NASA Astrophysics Data System (ADS)

Jiao, Lei; Yang, Yonggang; Li, Hui; Zhao, Yutao; Wang, Xiaolu

2018-05-01

In this study, the in situ Al3Ti/2024Al composites were successfully fabricated by direct melt reaction method and subjected to forging and friction stir processing (FSP) to achieve superplasticity. Then, the microstructure and superplastic tensile behavior of the composites were investigated. The results show that the reinforcement particles are broken and grains are fine after plastic processing. Particularly, the size of reinforcement particles ranges from 0.2 μm to 5 μm and the average size of fine equiaxed grains is 5 μm after FSP processing. And the superplasticity of the composites was improved apparently. The maximum elongation of 642% was obtained at 0.15 s‑1 and 510 °C for the FSP specimen, with a strain rate sensitive parameter (m) of 0.58, indicating the FSP specimen has obtained excellent high strain rate superplasticity. The strain rate sensitivity parameter, m, ranges from 0.23 to 0.58, and the activation energy was calculated to be 135.24 kJ mol‑1. All results indicated that the main superplastic deformation mechanism was grain boundary sliding (GBS) for the FSP Al3Ti/2024Al composites.

Soil grain analyses at Meridiani Planum, Mars

USGS Publications Warehouse

Weitz, C.M.; Anderson, R.C.; Bell, J.F.; Farrand, W. H.; Herkenhoff, K. E.; Johnson, J. R.; Jolliff, B.L.; Morris, R.V.; Squyres, S. W.; Sullivan, R.J.

2006-01-01

Grain-size analyses of the soils at Meridiani Planum have been used to identify rock souces for the grains and provide information about depositional processes under past and current conditions. Basaltic sand, dust, millimeter-size hematite-rich spherules interpreted as concretions, spherule fragments, coated partially buried spherules, basalt fragments, sedimentary outcrop fragments, and centimeter-size cobbles are concentrated on the upper surfaces of the soils as a lag deposit, while finer basaltic sands and dust dominate the underlying soils. There is a bimodal distribution of soil grain sizes with one population representing grains <125 ??m and the other falling between 1-4.5 mm. Soils within craters like Eagle and Endurance show a much greater diversity of grain morphologies compared to the plains. The spherules found in the plains soils are approximately 1-2 mm smaller in size than those seen embedded in the outcrop rocks of Eagle and Endurance craters. The average major axis for all unfractured spherules measured in the soils and outcrop rocks is 2.87 ?? 1.18 mm, with a trend toward decreasing spherule sizes in both the soils and outcrop rocks as the rover drove southward. Wind ripples seen across the plains of Meridiani are dominated by similar size (1.3-1.7 mm) hematite-rich grains, and they match in size the larger grains on plains ripples at Gusev Crater. Larger clasts and centimeter-size cobbles that are scattered on the soils have several spectral and compositional types, reflecting multiple origins. The cobbles tend to concentrate within ripple troughs along the plains and in association with outcrop exposures. Copyright 2006 by the American Geophysical Union.

VERY LARGE INTERSTELLAR GRAINS AS EVIDENCED BY THE MID-INFRARED EXTINCTION

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Shu; Jiang, B. W.; Li, Aigen, E-mail: shuwang@mail.bnu.edu.cn, E-mail: bjiang@bnu.edu.cn, E-mail: wanshu@missouri.edu, E-mail: lia@missouri.edu

The sizes of interstellar grains are widely distributed, ranging from a few angstroms to a few micrometers. The ultraviolet (UV) and optical extinction constrains the dust in the size range of a couple hundredths of micrometers to several submicrometers. The near and mid infrared (IR) emission constrains the nanometer-sized grains and angstrom-sized very large molecules. However, the quantity and size distribution of micrometer-sized grains remain unknown because they are gray in the UV/optical extinction and they are too cold and emit too little in the IR to be detected by IRAS, Spitzer, or Herschel. In this work, we employ themore » ∼3–8 μm mid-IR extinction, which is flat in both diffuse and dense regions to constrain the quantity, size, and composition of the μm-sized grain component. We find that, together with nano- and submicron-sized silicate and graphite (as well as polycyclic aromatic hydrocarbons), μm-sized graphite grains with C/H ≈ 137 ppm and a mean size of ∼1.2 μm closely fit the observed interstellar extinction of the Galactic diffuse interstellar medium from the far-UV to the mid-IR, as well as the near-IR to millimeter thermal emission obtained by COBE/DIRBE, COBE/FIRAS, and Planck up to λ ≲ 1000 μm. The μm-sized graphite component accounts for ∼14.6% of the total dust mass and ∼2.5% of the total IR emission.« less

Effect of diffusion annealing regimes on the structure of Nb3Sn layers in ITER-type bronze-processed wires

NASA Astrophysics Data System (ADS)

Valova-Zaharevskaya, E. G.; Popova, E. N.; Deryagina, I. L.; Abdyukhanov, I. M.; Tsapleva, A. S.

2018-03-01

The goal of the present study is to characterize the growth kinetics and structural parameters of the Nb3Sn layers formed under various regimes of the diffusion annealing of bronze-processed Nb/Cu-Sn composites. The structure of the superconducting layers is characterized by their thickness, average size of equiaxed grains and by the ratio of fractions of columnar and equiaxed grains. It was found that at higher diffusion annealing temperatures (above 650°C) thicker superconducting layers are obtained, but the average sizes of equiaxed Nb3Sn grains even under short exposures (10 h) are much larger than after the long low-temperature annealing. At the low-temperature (575 °C) annealing the relative fraction of columnar grains increases with increasing annealing time. Based on the data obtained, optimal regimes of the diffusion annealing can be chosen, which would on the one hand ensure complete transformation of Nb into Nb3Sn of close to the stoichiometric composition, and on the other hand prevent the formation of coarse and columnar grains.

Mineral Fractionation during Sediment Comminution and Transport in Fluvio-Deltaic and Lacustrine Rocks of the Bradbury Group, Gale Crater, Mars

NASA Astrophysics Data System (ADS)

Siebach, K. L.; Baker, M. B.; Grotzinger, J. P.; McLennan, S. M.; Gellert, R.; Thompson, L. M.; Hurowitz, J.

2017-12-01

Mineral distribution patterns in sediments of the Bradbury group in Gale crater, interpreted from observations by the Mars Science Laboratory rover Curiosity, show the importance of transport mechanics in source-to-sink processes on Mars. The Bradbury group is comprised of basalt-derived mudstones to conglomerates exposed along the modern floor of Gale crater and analyzed along a 9-km traverse of the Curiosity rover. Over 110 bulk chemistry analyses of the rocks were acquired, along with two XRD mineralogical analyses of the mudstone. These rocks are uniquely suited for analysis of source-to-sink processes because they exhibit a wide range of compositions, but (based on multiple chemical weathering proxies) they appear to have experienced negligible cation-loss during weathering and erosion. Chemical variations between analyses correlate with sediment grain sizes, with coarser-grained rocks enriched in plagioclase components SiO2, Al2O3, and Na2O, and finer-grained rocks enriched in components of mafic minerals, consistent with grain-size sorting of mineral fractions during sediment transport. Further geochemical and mineralogical modeling supports the importance of mineral fractionation: even though the limited XRD data suggests that some fraction (if not all) of the rocks contain clays and an amorphous component, models show that 90% of the compositions measured are consistent with sorting of primary igneous minerals from a plagioclase-phyric subalkaline basalt (i.e., no corrections for cation-loss are required). The distribution of K2O, modeled as a potassium feldspar component, is an exception to the major-element trends because it does not correlate with grain size, but has an elevation-dependent signal likely correlated with the introduction of a second source material. However, the dominant compositional trends within the Bradbury group sedimentary rocks are correlated with grain size and consistent with mineral fractionation of minimally-weathered plagioclase-phyric basalts; the plagioclase phenocrysts settle into coarser deposits and the finer deposits are dominated by mafic minerals.

Laboratory Studies of Charging Properties of Dust Grains in Astrophysical/Planetary Environments

NASA Technical Reports Server (NTRS)

Tankosic, D.; Abbas, M. M.

2012-01-01

Dust grains in various astrophysical environments are generally charged electrostatically by photoelectric emissions with UV/X-ray radiation, as well as by electron/ion impact. Knowledge of physical and optical properties of individual dust grains is required for understanding of the physical and dynamical processes in space environments and the role of dust in formation of stellar and planetary systems. In this paper we focus on charging of individual micron/submicron dust grains by processes that include: (a) UV photoelectric emissions involving incident photon energies higher than the work function of the material and b) electron impact, where low energy electrons are scattered or stick to the dust grains, thereby charging the dust grains negatively, and at sufficiently high energies the incident electrons penetrate the grain leading to excitation and emission of electrons referred to as secondary electron emission (SEE). It is well accepted that the charging properties of individual micron/submicron size dust grains are expected to be substantially different from the bulk materials. However, no viable models for calculation of the charging properties of individual micron size dust grains are available at the present time. Therefore, the photoelectric yields, and secondary electron emission yields of micron-size dust grains have to be obtained by experimental methods. Currently, very limited experimental data are available for charging of individual micron-size dust grains. Our experimental results, obtained on individual, micron-size dust grains levitated in an electrodynamic balance facility (at NASA-MSFC), show that: (1) The measured photoelectric yields are substantially higher than the bulk values given in the literature and indicate a particle size dependence with larger particles having order-of-magnitude higher values than for submicron-size grains; (2) dust charging by low energy electron impact is a complex process. Also, our measurements indicate that the electron impact may lead to charging or discharging of dust grains depending upon the grain size, surface potential, electron energy, electron flux, grain composition, and configuration (e.g. Abbas et al, 2010). Laboratory measurements on charging of analogs of the interstellar dust as well as Apollo 11 dust grains conducted at the NASA-MSFC Dusty Plasma Lab. are presented here

Effect of substrate temperature and gas flow ratio on the nanocomposite TiAlBN coating

NASA Astrophysics Data System (ADS)

Rosli, Z. M.; Kwan, W. L.; Juoi, J. M.

2016-07-01

Nanocomposite TiAlBN (nc-TiAlBN) coatings were successfully deposited via RF magnetron sputtering by varying the nitrogen-to-total gas flow ratio (RN), and substrate temperature (TS). All coatings were deposited on AISI 316 substrates using single Ti-Al-BN hot-pressed disc as a target. The grain size, phases, and chemical composition of the coatings were evaluated using glancing angle X-ray diffraction analysis (GAXRD) and X-ray photoelectron spectroscopy (XPS). Results showed that the grains size of the deposited nc-TiAlBN coatings were in the range of 3.5 to 5.7 nm and reached a nitride saturation state as early as 15 % RN. As the nitrogen concentration decreases, boron concentration increased from 9 at.% to 16.17 at.%. and thus, increase the TiB2 phase within the coatings. The TS, however, showed no significant effect either on the crystallographic structure, grain size, or in the chemical composition of the deposited nc-TiAlBN coating.

Grain-Size Based Additivity Models for Scaling Multi-rate Uranyl Surface Complexation in Subsurface Sediments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Xiaoying; Liu, Chongxuan; Hu, Bill X.

The additivity model assumed that field-scale reaction properties in a sediment including surface area, reactive site concentration, and reaction rate can be predicted from field-scale grain-size distribution by linearly adding reaction properties estimated in laboratory for individual grain-size fractions. This study evaluated the additivity model in scaling mass transfer-limited, multi-rate uranyl (U(VI)) surface complexation reactions in a contaminated sediment. Experimental data of rate-limited U(VI) desorption in a stirred flow-cell reactor were used to estimate the statistical properties of the rate constants for individual grain-size fractions, which were then used to predict rate-limited U(VI) desorption in the composite sediment. The resultmore » indicated that the additivity model with respect to the rate of U(VI) desorption provided a good prediction of U(VI) desorption in the composite sediment. However, the rate constants were not directly scalable using the additivity model. An approximate additivity model for directly scaling rate constants was subsequently proposed and evaluated. The result found that the approximate model provided a good prediction of the experimental results within statistical uncertainty. This study also found that a gravel-size fraction (2 to 8 mm), which is often ignored in modeling U(VI) sorption and desorption, is statistically significant to the U(VI) desorption in the sediment.« less

Refining Mechanism of 7075 Al Alloy by In-Situ TiB2 Particles

PubMed Central

Gan, Guisheng; Yang, Bin; Zhang, Bo; Jiang, Xin; Shi, Yunlong; Wu, Yiping

2017-01-01

The nucleation undercooling of TiB2/7075 Al matrix composites, the microstructure observed after solidification at different cooling rate, and the size and distribution of TiB2 particles were investigated. The experimental results have shown that the grain sizes of TiB2/7075 Al matrix composites firstly decreased, then increased, and finally decreased again with the increase of TiB2 content. The nucleation undercooling of TiB2/7075 Al matrix composites first increased, then decreased, and finally increased again with the increase of TiB2 content when the cooling rates was 5 and 10 °C/min respectively, but kept decreasing with the increase of TiB2 content at a cooling rate of 20 °C/min. The melting and solidification process showed no significant change with the decrease of cooling rate in 9.0% TiB2/7075 Al matrix composites. Most small particles can act as heterogeneous nucleus, which induced grain growth and were captured into the grain by the solid/liquid interface. At the same time, most of the larger particles and a minority of the small TiB2 particles are pushed into the grain boundary; locating in the grain boundary can hinder the Al atoms from diffusing during the solidification process and restrain α-Al phase growth. The influence of particles shifted from dominating by locating to dominating by nucleation as the quantity of TiB2 particles increased. PMID:28772492

Predictive modelling of grain-size distributions from marine electromagnetic profiling data using end-member analysis and a radial basis function network

NASA Astrophysics Data System (ADS)

Baasch, B.; Müller, H.; von Dobeneck, T.

2018-07-01

In this work, we present a new methodology to predict grain-size distributions from geophysical data. Specifically, electric conductivity and magnetic susceptibility of seafloor sediments recovered from electromagnetic profiling data are used to predict grain-size distributions along shelf-wide survey lines. Field data from the NW Iberian shelf are investigated and reveal a strong relation between the electromagnetic properties and grain-size distribution. The here presented workflow combines unsupervised and supervised machine-learning techniques. Non-negative matrix factorization is used to determine grain-size end-members from sediment surface samples. Four end-members were found, which well represent the variety of sediments in the study area. A radial basis function network modified for prediction of compositional data is then used to estimate the abundances of these end-members from the electromagnetic properties. The end-members together with their predicted abundances are finally back transformed to grain-size distributions. A minimum spatial variation constraint is implemented in the training of the network to avoid overfitting and to respect the spatial distribution of sediment patterns. The predicted models are tested via leave-one-out cross-validation revealing high prediction accuracy with coefficients of determination (R2) between 0.76 and 0.89. The predicted grain-size distributions represent the well-known sediment facies and patterns on the NW Iberian shelf and provide new insights into their distribution, transition and dynamics. This study suggests that electromagnetic benthic profiling in combination with machine learning techniques is a powerful tool to estimate grain-size distribution of marine sediments.

Predictive modelling of grain size distributions from marine electromagnetic profiling data using end-member analysis and a radial basis function network

NASA Astrophysics Data System (ADS)

Baasch, B.; M"uller, H.; von Dobeneck, T.

2018-04-01

In this work we present a new methodology to predict grain-size distributions from geophysical data. Specifically, electric conductivity and magnetic susceptibility of seafloor sediments recovered from electromagnetic profiling data are used to predict grain-size distributions along shelf-wide survey lines. Field data from the NW Iberian shelf are investigated and reveal a strong relation between the electromagnetic properties and grain-size distribution. The here presented workflow combines unsupervised and supervised machine learning techniques. Nonnegative matrix factorisation is used to determine grain-size end-members from sediment surface samples. Four end-members were found which well represent the variety of sediments in the study area. A radial-basis function network modified for prediction of compositional data is then used to estimate the abundances of these end-members from the electromagnetic properties. The end-members together with their predicted abundances are finally back transformed to grain-size distributions. A minimum spatial variation constraint is implemented in the training of the network to avoid overfitting and to respect the spatial distribution of sediment patterns. The predicted models are tested via leave-one-out cross-validation revealing high prediction accuracy with coefficients of determination (R2) between 0.76 and 0.89. The predicted grain-size distributions represent the well-known sediment facies and patterns on the NW Iberian shelf and provide new insights into their distribution, transition and dynamics. This study suggests that electromagnetic benthic profiling in combination with machine learning techniques is a powerful tool to estimate grain-size distribution of marine sediments.

The Anatomy of AP1000 Mono-Block Low Pressure Rotor Forging

NASA Astrophysics Data System (ADS)

Jin, Jia-yu; Rui, Shou-tai; Wang, Qun

AP1000 mono-block low pressure (LP) rotor forgings for nuclear power station have maximum ingot weight, maximum diameter and the highest technical requirements. It confronts many technical problems during manufacturing process such as composition segregation and control of inclusion in the large ingot, core compaction during forging, control of grain size and mechanical performance. The rotor forging were anatomized to evaluate the manufacturing level of CFHI. This article introduces the anatomical results of this forging. The contents include chemical composition, mechanical properties, inclusions and grain size and other aspects from the full-length and full cross-section of this forging. The fluctuation of mechanical properties, uniformity of microstructure and purity of chemical composition were emphasized. The results show that the overall performance of this rotor forging is particularly satisfying.

Model Fe-Al Steel with Exceptional Resistance to High Temperature Coarsening. Part II: Experimental Validation and Applications

NASA Astrophysics Data System (ADS)

Zhou, Tihe; Zhang, Peng; O'Malley, Ronald J.; Zurob, Hatem S.; Subramanian, Mani

2015-01-01

In order to achieve a fine uniform grain-size distribution using the process of thin slab casting and directing rolling (TSCDR), it is necessary to control the grain-size prior to the onset of thermomechanical processing. In the companion paper, Model Fe- Al Steel with Exceptional Resistance to High Temperature Coarsening. Part I: Coarsening Mechanism and Particle Pinning Effects, a new steel composition which uses a small volume fraction of austenite particles to pin the growth of delta-ferrite grains at high temperature was proposed and grain growth was studied in reheated samples. This paper will focus on the development of a simple laboratory-scale setup to simulate thin-slab casting of the newly developed steel and demonstrate the potential for grain size control under industrial conditions. Steel bars with different diameters are briefly dipped into the molten steel to create a shell of solidified material. These are then cooled down to room temperature at different cooling rates. During cooling, the austenite particles nucleate along the delta-ferrite grain boundaries and greatly retard grain growth. With decreasing temperature, more austenite particles precipitate, and grain growth can be completely arrested in the holding furnace. Additional applications of the model alloy are discussed including grain-size control in the heat affected zone in welds and grain-growth resistance at high temperature.

ZrB2-CNTs Nanocomposites Fabricated by Spark Plasma Sintering

PubMed Central

Jin, Hua; Meng, Songhe; Xie, Weihua; Xu, Chenghai; Niu, Jiahong

2016-01-01

ZrB2-based nanocomposites with and without carbon nanotubes (CNTs) as reinforcement were prepared at 1600 °C by spark plasma sintering. The effects of CNTs on the microstructure and mechanical properties of nano-ZrB2 matrix composites were studied. The results indicated that adding CNTs can inhibit the abnormal grain growth of ZrB2 grains and improve the fracture toughness of the composites. The toughness mechanisms were crack deflection, crack bridging, debonding, and pull-out of CNTs. The experimental results of the nanograined ZrB2-CNTs composites were compared with those of the micro-grained ZrB2-CNTs composites. Due to the small size and surface effects, the nanograined ZrB2-CNTs composites exhibited stronger mechanical properties: the hardness, flexural strength and fracture toughness were 18.7 ± 0.2 GPa, 1016 ± 75 MPa, and 8.5 ± 0.4 MPa·m1/2, respectively. PMID:28774087

ZrB₂-CNTs Nanocomposites Fabricated by Spark Plasma Sintering.

PubMed

Jin, Hua; Meng, Songhe; Xie, Weihua; Xu, Chenghai; Niu, Jiahong

2016-11-29

ZrB₂-based nanocomposites with and without carbon nanotubes (CNTs) as reinforcement were prepared at 1600 °C by spark plasma sintering. The effects of CNTs on the microstructure and mechanical properties of nano-ZrB₂ matrix composites were studied. The results indicated that adding CNTs can inhibit the abnormal grain growth of ZrB₂ grains and improve the fracture toughness of the composites. The toughness mechanisms were crack deflection, crack bridging, debonding, and pull-out of CNTs. The experimental results of the nanograined ZrB₂-CNTs composites were compared with those of the micro-grained ZrB₂-CNTs composites. Due to the small size and surface effects, the nanograined ZrB₂-CNTs composites exhibited stronger mechanical properties: the hardness, flexural strength and fracture toughness were 18.7 ± 0.2 GPa, 1016 ± 75 MPa, and 8.5 ± 0.4 MPa·m 1/2 , respectively.

Mechanical, Dielectric, and Spectroscopic Characteristics of "Micro/Nanocellulose + Oxide" Composites.

PubMed

Nedielko, Maksym; Hamamda, Smail; Alekseev, Olexander; Chornii, Vitalii; Dashevskii, Mykola; Lazarenko, Maksym; Kovalov, Kostiantyn; Nedilko, Sergii G; Tkachov, Sergii; Revo, Sergiy; Scherbatskyi, Vasyl

2017-12-01

The set of composite materials that consist of micro/nanocellulose and complex K 2 Eu(MoO 4 )(PO 4 ) luminescent oxide particles was prepared. The composites were studied by means of scanning electron microscopy, XRD analysis, dilatometry, differential scanning calorimetry and thermogravimetric analysis, and dielectric and luminescence spectroscopy.Dependencies of density, crystallinity, relative extension, thermal extension coefficient, dielectric relaxation parameters, intensity and shape of photoluminescence bands on temperature, and content of oxide component were studied. The structure of the composite without oxide is formed by grains of nearly 5-50 μm in size (crystallinity is about ~56%). Structure of the micro/nanocellulose samples which contain oxide particles is similar, but the cellulose grains are deformed by oxide particles. Dependencies of the abovementioned properties on temperature and oxide content were analyzed together with data on the size distribution of oxide particles for the samples for various oxide and molecules of water concentrations.

TOPICAL REVIEW: Progress in engineering high strain lead-free piezoelectric ceramics

NASA Astrophysics Data System (ADS)

Leontsev, Serhiy O.; Eitel, Richard E.

2010-08-01

Environmental concerns are strongly driving the need to replace the lead-based piezoelectric materials currently employed as multilayer actuators. The current review describes both compositional and structural engineering approaches to achieve enhanced piezoelectric properties in lead-free materials. The review of the compositional engineering approach focuses on compositional tuning of the properties and phase behavior in three promising families of lead-free perovskite ferroelectrics: the titanate, alkaline niobate and bismuth perovskites and their solid solutions. The 'structural engineering' approaches focus instead on optimization of microstructural features including grain size, grain orientation or texture, ferroelectric domain size and electrical bias field as potential paths to induce large piezoelectric properties in lead-free piezoceramics. It is suggested that a combination of both compositional and novel structural engineering approaches will be required in order to realize viable lead-free alternatives to current lead-based materials for piezoelectric actuator applications.

Progress in engineering high strain lead-free piezoelectric ceramics

PubMed Central

Leontsev, Serhiy O; Eitel, Richard E

2010-01-01

Environmental concerns are strongly driving the need to replace the lead-based piezoelectric materials currently employed as multilayer actuators. The current review describes both compositional and structural engineering approaches to achieve enhanced piezoelectric properties in lead-free materials. The review of the compositional engineering approach focuses on compositional tuning of the properties and phase behavior in three promising families of lead-free perovskite ferroelectrics: the titanate, alkaline niobate and bismuth perovskites and their solid solutions. The ‘structural engineering’ approaches focus instead on optimization of microstructural features including grain size, grain orientation or texture, ferroelectric domain size and electrical bias field as potential paths to induce large piezoelectric properties in lead-free piezoceramics. It is suggested that a combination of both compositional and novel structural engineering approaches will be required in order to realize viable lead-free alternatives to current lead-based materials for piezoelectric actuator applications. PMID:27877343

Effects of road dust on the growth characteristics of Sophora japonica L. seedlings.

PubMed

Bao, Le; Qu, Laiye; Ma, Keming; Lin, Lin

2016-08-01

Road dust is one of the most common pollutants and causes a series of negative effects on plant physiology. Dust's impacts on plants can be regarded as a combination of load, composition and grain size impacts on plants; however, there is a lack of integrated dust effect studies involving these three aspects. In our study, Sophora japonica seedlings were artificially dusted with road dust collected from the road surface of Beijing so that we could study the impacts of this dust on nitrogen/carbon allocation, biomass allocation and photosynthetic pigments from the three aspects of composition, load and grain size. The results showed that the growth characteristics of S. japonica seedlings were mostly influenced by dust composition and load. Leaf N, root-shoot ratio and chlorophyll a/b were significantly affected by dust composition and load; leaf C/N, shoot biomass, total chlorophyll and carotenoid were significantly affected by dust load; stem N and stem C/N were significantly affected by dust composition; while the dust grain size alone did not affect any of the growth characteristics. Road dust did influence the growth characteristics more extensively than loam. Therefore, a higher dust load could increase the differences between road dust and loam treatments. The elements in dust are well correlated to the shoot N, shoot C/N, and root-shoot ratio of S. japonica seedlings. This knowledge could benefit the management of urban green spaces. Copyright © 2016. Published by Elsevier B.V.

Comet C/2012 S1 (ISON)'s carbon-rich and micron-size-dominated coma dust

NASA Astrophysics Data System (ADS)

Wooden, D.; De Buizer, J.; Kelley, M.; Sitko, M.; Woodward, C.; Harker, D.; Reach, W.; Russell, R.; Kim, D.; Yanamadra-Fisher, P.; Lisse, C.; de Pater, I.; Gehrz, R.; Kolokolova, L.

2014-07-01

Comet C/2012 S1 (ISON) was unique in that it was a dynamically new comet derived from the Nearly Isotropic Oort cloud reservoir of comets with a sun-grazing orbit. We present thermal models for comet ISON (r_h ˜ 1.15 au, 2013-Oct-25 11:30 UT) that reveal comet ISON's dust was carbon-rich and dominated by a steep (and therefor narrow) grain size distribution (GSD) dominated by ˜ micron-sized grains. We constrained the models by our SOFIA FORCAST photometry at 11.1, 19.7 and 31.5 μ m and by a silicate feature strength of ˜1.1 and an 8-13 μ m continuum greybody color temperature of ˜275-280 K (using T_{bb}∝ {r}_h^{-0.5} and T_{bb}˜260-265 K from Subaru+COMICS, 2013-Oct-19 UT) [1,2]. Spectra of comet ISON with IRTF+BASS (2013-Nov-11-12 UT) also show a silicate feature strength of ˜1.1 as well as an 11.2 μ m forsterite peak [3]. Our thermal models [6], which employ 0.1-1000 μ m grains, yield constraints for the dust composition as well as GSD parameters of slope, peak grain size, porosity: ISON's dust has a low silicate-to-amorphous carbon ratio (˜1:9), the GSD has a steep slope (N≃4.5), a peak grain radius of ˜0.7 μ m, and moderately porous grains. Specifically, the 8-13 μ m continuum color temperature implies submicron- to micron-size grains and the steep fall off of the SOFIA far-IR photometry requires the GSD to have fewer relative numbers of larger and cooler grains compared to smaller and hotter grains. A IR proxy for the dust production rate is ɛ f ρ ˜ 1500 cm [4], which is akin to but larger than Afρ in scattered light (2013-Oct-20 UT, Afρ=796 cm(±5 %) in V-band from Swift) [5]. Also, ISON had a moderate-to-low dust-to-gas ratio [6]. Comet ISON's dust composition and GSD properties are distinct from the few well-studied long-period Nearly Isotropic Comets (NICs) that all had 'typical' GSD slopes (3.4≤N≤3.7) and silicate-to-amorphous carbon ratios ≫1 as well as the following properties: C/1995 O1 (Hale-Bopp)[7,8,9,10] and C/2001 Q4 (NEAT)[11] had smaller and highly porous grains, whereas C/2007 N4 (Lulin)[12] and C/2006 P1 (McNaught)[13] had larger and compact porous grains. Radial transport to comet-forming disk distances (≥ 20 au) is easier for smaller grains than for larger grains (≤ 1 μ m vs.˜20 μ m-like Stardust terminal particles) [14]. Perhaps Comet ISON formed either earlier in disk evolution whereby larger grains did not have the time to be transported to distances beyond Neptune, or the comet formed so far out in the disk that larger grains did not traverse such large radial distances. The high carbon-content of ISON's refractory dust appears to be complimented by the presence of limited-lifetime organic (CHON-like) grain materials: preliminary analyses of near-IR and high-resolution optical spectra indicate that gas-phase daughter molecules C_2, CN, and CH were more abundant than their parent molecules (HCN, C_2H_2, C_2H_6, measured in the near-IR) [15]. Dust composition as well as grain size distribution parameters (slope, peak grain size, and porosity) give clues to comet origins [16,17].

Zirconia-alumina-nanodiamond composites with gemological properties

NASA Astrophysics Data System (ADS)

Díaz, Luis A.; Montes-Morán, Miguel A.; Peretyagin, Pavel Y.; Vladimirov, Yuriy G.; Okunkova, Anna; Moya, José S.; Torrecillas, Ramón

2014-02-01

Nanodiamonds have excellent mechanical and optical properties with a wide range of potential applications as a filler material for nanocomposites. Here, we present a new family of zirconia-alumina-nanodiamond composites using two main processing routes: (1) a colloidal method, and (2) power mixing homogenization. Composites with detonation nanodiamonds quantities ranging within 0.3-5 vol.% followed by a pulsed electrical current sintering at a temperature range from 1,200 to 1,500 °C have been analyzed, and a significant enhancement in mechanical properties, i.e., indentation hardness (16.17 GPa), fracture toughness (15.5 MPa m1/2), and bending strength (1,600 MPa), could be observed. To support these excellent properties, TEM, color, reflectivity, and Raman spectroscopy measurements were also carried out. The microstructure of the composites is very homogeneous with average grain sizes between 200 and 500 nm depending on the processing temperature. Two morphologies are present: (a) intergranular dispersion of alumina grains and nanodiamonds distributed along the grain boundaries of the ZrO2 matrix, and (b) intragranular nano-dispersion of ZrO2 particles with sizes 20-80 nm located inside the alumina grains. In the present article, we show, for the first time in the scientific literature, a continuous palette of gray color gradation of new ceramic materials of metalized colors (white index L* 98-40) for gemological applications.

Grain growth kinetics of ringwoodite and majorite garnet mixtures and implications for the rheology of the transition zone

NASA Astrophysics Data System (ADS)

Ezad, I.; Dobson, D. P.; Brodholt, J. P.; Thomson, A.; Hunt, S.

2017-12-01

The grain size of the transition zone is a poorly known but important geophysical parameter. Among others, the grain size may control the rheology, seismic attenuation and radiative thermal conductivity of the mantle. However, the grain size of the transition zone minerals ringwoodite (Mg,Fe)2SiO4 and majorite garnet MgSiO3 under appropriate zone conditions is currently unknown and there are very few experiments with which to constrain it. In order to determine the grain size of the transition zone, the grain growth kinetics must be determined for a range of mantle compositions. We have, therefore, experimentally determined the grain growth kinetics of the lowermost transition zone minerals through multi anvil experiments at University College London (UCL). This is achieved through a comprehensive set of time series experiments at pressures of 21 GPa and temperatures relevant to the transition zone. We have also determined the effect of varying water content, oxygen fugacity, iron content and aluminium content also discussed by Dobson and Mariani., (2014). Our initial grain growth experiments conducted at 1200°C and 1400°C at 18 GPa show extremely slow grain growth kinetics; time series experiments extended to 105.8 seconds are unable to produce grains larger than 100 nm. This suggests that fine-grained material at the base of the transition zone will persist on geological timescales. Such small grains size suggests that diffusion creep might be the dominant deformation mechanism in this region. Reference: Dobson, D.P., Mariani, E., 2014. The kinetics of the reaction of majorite plus ferropericlase to ringwoodite: Implications for mantle upwellings crossing the 660 km discontinuity. Earth Planet. Sci. Lett. 408, 110-118. doi:10.1016/j.epsl.2014.10.009

Corrosion resistance of nanostructured titanium.

PubMed

Garbacz, H; Pisarek, M; Kurzydłowski, K J

2007-11-01

The present work reports results of studies of corrosion resistance of pure nano-Ti-Grade 2 after hydrostatic extrusion. The grain size of the examined samples was below 90 nm. Surface analytical technique including AES combined with Ar(+) ion sputtering, were used to investigate the chemical composition and thicknesses of the oxides formed on nano-Ti. It has been found that the grain size of the titanium substrate did not influence the thickness of oxide formed on the titanium. The thickness of the oxide observed on the titanium samples before and after hydrostatic extrusion was about 6 nm. Tests carried out in a NaCl solution revealed a slightly lower corrosion resistance of nano-Ti in comparison with the titanium with micrometric grain size.

Static Grain Growth in Contact Metamorphic Calcite: A Cathodoluminescence Study.

NASA Astrophysics Data System (ADS)

Vogt, B.; Heilbronner, R.; Herwegh, M.; Ramseyer, K.

2009-04-01

In the Adamello contact aureole, monomineralic mesozoic limestones were investigated in terms of grain size evolution and compared to results on numerical modeling performed by Elle. The sampled area shows no deformation and therefore represents an appropriate natural laboratory for the study of static grain growth (Herwegh & Berger, 2003). For this purpose, samples were collected at different distances to the contact to the pluton, covering a temperature range between 270 to 630°C. In these marbles, the grain sizes increase with temperature from 5 µm to about 1 cm as one approaches the contact (Herwegh & Berger, 2003). In some samples, photomicrographs show domains of variable cathodoluminescence (CL) intensities, which are interpreted to represent growth zonations. Microstructures show grains that contain cores and in some samples even several growth stages. The cores are usually not centered and the zones not concentric. They may be in touch with grain boundaries. These zonation patterns are consistent within a given aggregate but differ among the samples even if they come from the same location. Relative CL intensities depend on the Mn/Fe ratio. We assume that changes in trace amounts of Mn/Fe must have occurred during the grain size evolution, preserving local geochemical trends and their variations with time. Changes in Mn/Fe ratios can either be explained by (a) locally derived fluids (e.g. hydration reactions of sheet silicate rich marbles in the vicinity) or (b) by the infiltration of the calcite aggregates by externally derived (magmatic?) fluids. At the present stage, we prefer a regional change in fluid composition (b) because the growth zonations only occur at distances of 750-1250 m from the pluton contact (350-450°C). Closer to the contact, neither zonations nor cores were found. At larger distances, CL intensities differ from grain to grain, revealing diagenetic CL patterns that were incompletely recrystallized by grain growth. The role of infiltration of magmatic fluids is also manifest in the vicinity of dikes, where intense zonation patterns are prominent in the marbles. The software Elle was developed to simulate microstructural evolution in rocks. The numerical model with the title "Grain boundary sweeping" was performed by M. Jessell and was found on http://www.materialsknowledge.org/elle. It displays the grain size evolution and the development of growth zonations during grain boundary migration of a 2D foam structure. This simulation was chosen because the driving force is the minimization of isotropic surface energies. It will be compared to the natural microstructures. At the last stage of the simulation the average grain and core sizes have increased. All, even the smallest grains, show growth zonations. Grains can be divided into two groups: (a) initially larger grains, increasing their grain size and maintaining their core size and (b) initially smaller grains with decreasing grain and decreasing core size. Group (a) grains show large areas swept by grain boundaries into the direction of small grains. Grain boundaries between large grains move more slowly. Their cores do not touch any grain boundaries. Cores of group (b) grains are in contact with the grain boundary network and are on the way to be consumed. In the numerical model and in the natural example similar features can be observed: The cores are not necessarily centered, the zonations are not necessarily concentric and some of the cores touch the grain boundary network. In the simulation, grain boundary migration velocity between large grains is smaller than between a large and a small grain. From this we would predict that - given enough time - a well sorted grain size distribution of increased grain size could be generated. But since many small grains occur we infer that this equilibrium has not been obtained. Analytical results of some natural samples that could be analyzed up to now indicate a relatively well sorted grain size distribution suggesting a more mature state of static grain growth. In comparison to the simulation, grain and core boundaries in the marbles are not always straight. For lobate grain boundaries the surface area has not been minimized in respect to the grain size. An explanation for this might be grain boundary pinning or a local dynamic overprint. Some cores and growth zones in the investigated calcites show a continuous change in luminescence. This is interpreted to be an effect of late diffusion within the grain and/or a continuous change of fluid composition and supply. The absence of zonation in samples close to the contact might be explained by fast grain growth due to high temperatures and/or fast fluid transport. Possibly, this is combined with an enhanced component of volume diffusion. Thus concentration variations of Mn/Fe are diminished and not visible in form of a growth zonation. Herwegh M, Berger A (2003) Differences in grain growth of calcite: a field-based modeling approach. Contr. Min. Pet. 145: 600-611

Compositional variations in sands of the Bagnold Dunes, Gale Crater, Mars, from visible-shortwave infrared spectroscopy and comparison with ground truth from the Curiosity Rover

USGS Publications Warehouse

Lapotre, Mathieu G.A.; Ehlmann, B. L.; Minson, Sarah E.; Arvidson, R. E.; Ayoub, F.; Fraeman, A. A.; Ewing, R. C.; Bridges, N. T.

2017-01-01

During its ascent up Mount Sharp, the Mars Science Laboratory Curiosity rover traversed the Bagnold Dune Field. We model sand modal mineralogy and grain size at four locations near the rover traverse, using orbital shortwave infrared single scattering albedo spectra and a Markov-Chain Monte Carlo implementation of Hapke's radiative transfer theory to fully constrain uncertainties and permitted solutions. These predictions, evaluated against in situ measurements at one site from the Curiosity rover, show that XRD-measured mineralogy of the basaltic sands is within the 95% confidence interval of model predictions. However, predictions are relatively insensitive to grain size and are non-unique, especially when modeling the composition of minerals with solid solutions. We find an overall basaltic mineralogy and show subtle spatial variations in composition in and around the Bagnold dunes, consistent with a mafic enrichment of sands with cumulative transport distance by sorting of olivine, pyroxene, and plagioclase grains during aeolian saltation. Furthermore, the large variations in Fe and Mg abundances (~20 wt%) at the Bagnold Dunes suggest that compositional variability induced by wind sorting may be enhanced by local mixing with proximal sand sources. Our estimates demonstrate a method for orbital quantification of composition with rigorous uncertainty determination and provide key constraints for interpreting in situ measurements of compositional variability within martian aeolian sandstones.

H2O grain size and the amount of dust in Mars' residual north polar cap

NASA Technical Reports Server (NTRS)

Kieffer, Hugh H.

1990-01-01

In Mars' north polar cap, the probable composition of material residual from the annual condensation cycle is a mixture of fine dust and H2O grains of comparable size and abundance. However, metamorphism of such material will gradually lower its albedo by increasing the size of the H2O grains only. If the cap is undergoing net annual sublimation (as inferred from water vapor observations), late summer observations should be of old ice with H2O grain sizes of 100 microns or more. Ice of this granularity containing 30 percent fine dust has a reflectivity similar to that of dust alone; the observed albedo and computed ice grain size imply dust concentrations of 1 part per 1000 or less. The brightness of the icy areas conflicts with what would be expected for a residual cap deposited by an annual cycle similar to that observed by Viking and aged for thousands of years. The residual cap surface cannot be 'old dirty' ice. It could be old, coarse, and clean; or it could be young, fine, and dirty. This brings into question both the source of the late summer water vapor and the formation rate of laminated terrain.

H2O grain size and the amount of dust in Mars' residual North polar cap

USGS Publications Warehouse

Kieffer, H.H.

1990-01-01

In Mars' north polar cap the probable composition of material residual from the annual condensation cycle is a mixture of fine dust and H2O grains of comparable size and abundance. However, metamorphism of such material will gradually lower its albedo by increasing the size of the H2O grains only. If the cap is undergoing net annual sublimation (as inferred from water vapor observations), late summer observations should be of old ice with H2O grain sizes of 100 ??m or more. Ice of this granularity containing 30% fine dust has a reflectivity similar to that of dust alone; the observed albedo and computed ice grain size imply dust concentrations of 1 part per 1000 or less. The brightness of the icy areas conflicts with what would be expected for a residual cap deposited by an annual cycle similar to that observed by Viking and aged for thousands of years. The residual cap surface cannot be "old dirty' ice. It could be old, coarse, and clean; or it could be young, fine, and dirty. This brings into question both the source of the late summer water vapor and the formation rate of laminated terrain. -Author

Effect of Nb Addition to Ti-Bearing Super Martensitic Stainless Steel on Control of Austenite Grain Size and Strengthening

NASA Astrophysics Data System (ADS)

Ma, Xiaoping; Langelier, Brian; Gault, Baptiste; Subramanian, Sundaresa

2017-05-01

The role of Nb in normalized and tempered Ti-bearing 13Cr5Ni2Mo super martensitic stainless steel is investigated through in-depth characterization of the bimodal chemistry and size of Nb-rich precipitates/atomic clusters and Nb in solid solution. Transmission electron microscopy and atom probe tomography are used to analyze the samples and clarify precipitates/atom cluster interactions with dislocations and austenite grain boundaries. The effect of 0.1 wt pct Nb addition on the promotion of (Ti, Nb)N-Nb(C,N) composite precipitates, as well as the retention of Nb in solution after cooling to room temperature, are analyzed quantitatively. (Ti, Nb)N-Nb(C,N) composite precipitates with average diameters of approximately 24 ± 8 nm resulting from epitaxial growth of Nb(C,N) on pre-existing (Ti,Nb)N particles, with inter-particle spacing on the order of 205 ± 68 nm, are found to be associated with mean austenite grain size of 28 ± 10 µm in the sample normalized at 1323 K (1050 °C). The calculated Zener limiting austenite grain size of 38 ± 13 µm is in agreement with the experimentally observed austenite grain size distribution. 0.08 wt pct Nb is retained in the as-normalized condition, which is able to promote Nb(C, N) atomic clusters at dislocations during tempering at 873 K (600 °C) for 2 hours, and increases the yield strength by 160 MPa, which is predicted to be close to maximum increase in strengthening effect. Retention of solute Nb before tempering also leads to it preferentially combing with C and N to form Nb(C, N) atom clusters, which suppresses the occurrence of Cr- and Mo-rich carbides during tempering.

VNIR reflectance spectroscopy of natural carbonate rocks: implication for remote sensing identification of fault damage zones

NASA Astrophysics Data System (ADS)

Traforti, Anna; Mari, Giovanna; Carli, Cristian; Demurtas, Matteo; Massironi, Matteo; Di Toro, Giulio

2017-04-01

Reflectance spectroscopy in the visible and near-infrared (VNIR) is a common technique used to study the mineral composition of Solar System bodies from remote sensed and in-situ robotic exploration. In the VNIR spectral range, both crystal field and vibrational overtone absorptions can be present with spectral characteristics (i.e. albedo, slopes, absorption band with different positions and depths) that vary depending on composition and texture (e.g. grain size, roughness) of the sensed materials. The characterization of the spectral variability related to the rock texture, especially in terms of grain size (i.e., both the size of rock components and the size of particulates), commonly allows to obtain a wide range of information about the different geological processes modifying the planetary surfaces. This work is aimed at characterizing how the grain size reduction associated to fault zone development produces reflectance variations in rock and mineral spectral signatures. To achieve this goal we present VNIR reflectance analysis of a set of fifteen rock samples collected at increasing distances from the fault core of the Vado di Corno fault zone (Campo Imperatore Fault System - Italian Central Apennines). The selected samples had similar content of calcite and dolomite but different grain size (X-Ray Powder Diffraction, optical and scanning electron microscopes analysis). Consequently, differences in the spectral signature of the fault rocks should not be ascribed to mineralogical composition. For each sample, bidirectional reflectance spectra were acquired with a Field-Pro Spectrometer mounted on a goniometer, on crushed rock slabs reduced to grain size <800, <200, <63, <10 μm and on intact fault zone rock slabs. The spectra were acquired on dry samples, at room temperature and normal atmospheric pressure. The source used was a Tungsten Halogen lamp with an illuminated spot area of ca. 0.5 cm2and incidence and emission angles of 30˚ and 0˚ respectively. The spectral analysis of the crushed and intact rock slabs in the VNIR spectral range revealed that in both cases, with increasing grain size: (i) the reflectance decreases (ii) VNIR spectrum slopes (i.e. calculated between wavelengths of 0.425 - 0.605 μm and 2.205 - 2.33 μm, respectively) and (iii) carbonate main absorption band depth (i.e. vibrational absorption band at wavelength of ˜2.3 μm) increase. In conclusion, grain size variations resulting from the fault zone evolution (e.g., cumulated slip or development of thick damage zones) produce reflectance variations in rocks and mineral spectral signatures. The remote sensing analysis in the VNIR spectral range can be applied to identify the spatial distribution and extent of fault core and damage zone domains for industrial and seismic hazard applications. Moreover, the spectral characterization of carbonate-built rocks can be of great interest for the surface investigation of inner planets (e.g. Earth and Mars) and outer bodies (e.g. Galilean icy satellites). On these surfaces, carbonate minerals at different grain sizes are common and usually related to water and carbon distribution, with direct implications for potential life outside Earth (e.g. Mars).

Isolating magnetic moments from individual grains within a magnetic assemblage

NASA Astrophysics Data System (ADS)

Béguin, A.; Fabian, K.; Jansen, C.; Lascu, I.; Harrison, R.; Barnhoorn, A.; de Groot, L. V.

2017-12-01

Methods to derive paleodirections or paleointensities from rocks currently rely on measurements of bulk samples (typically 10 cc). The process of recording and storing magnetizations as function of temperature, however, differs for grains of various sizes and chemical compositions. Most rocks, by their mere nature, consist of assemblages of grains varying in size, shape, and chemistry. Unraveling the behavior of individual grains is a holy grail in fundamental rock magnetism. Recently, we showed that it is possible to obtain plausible magnetic moments for individual grains in a synthetic sample by a micromagnetic tomography (MMT) technique. We use a least-squares inversion to obtain these magnetic moments based on the physical locations and dimensions of the grains obtained from a MicroCT scanner and a magnetic flux density map of the surface of the sample. The sample used for this proof of concept, however, was optimized for success: it had a low dispersion of the grains, and the grains were large enough so they were easily detected by the MicroCT scanner. Natural lavas are much more complex than the synthetic sample analyzed so far: the dispersion of the magnetic markers is one order of magnitude higher, the grains differ more in composition and size, and many small (submicron) magnetic markers may be present that go undetected by the MicroCT scanner. Here we present the first results derived from a natural volcanic sample from the 1907-flow at Hawaii. To analyze the magnetic flux at the surface of the sample at room temperature, we used the Magnetic Tunneling Junction (MTJ) technique. We were able to successfully obtain MicroCT and MTJ scans from the sample and isolate plausible magnetic moments for individual grains in the top 70 µm of the sample. We discuss the potential of the MMT technique applied to natural samples and compare the MTJ and SSM methods in terms of work flow and quality of the results.

Major factors influencing the elemental composition of surface estuarine sediments: the case of 15 estuaries in Portugal.

PubMed

Mil-Homens, M; Vale, C; Raimundo, J; Pereira, P; Brito, P; Caetano, M

2014-07-15

Upper sediments (0-5 cm) were sampled in 94 sites of water bodies of the fifteen Portuguese estuaries characterized by distinct settings of climate, topography and lithology, and marked by diverse anthropogenic pressures. Confined areas recognized as highly anthropogenic impacted, as well as areas dominated by erosion or frequently dredged were not sampled. Grain size, organic carbon (Corg), Al and trace elements (As, Cd, Co, Cr, Cu, Hg, Ni, Pb and Zn) were determined. Normalisation of trace element concentrations to Al and Corg, correlations between elements and Principal Component Analysis (PCA) allowed identifying elemental associations and the relevance of grain-size, lithology and anthropogenic inputs on sediment chemical composition. Whereas grain-size is the dominant effect for the majority of the studied estuaries, the southern estuaries Mira, Arade and Guadiana are dominated by specific lithologies of their river basins, and anthropogenic effects are identified in Ave, Leça, Tagus and Sado. This study emphasizes how baseline values of trace elements in sediments may vary within and among estuarine systems. Copyright © 2014 Elsevier Ltd. All rights reserved.

Nano and micro U1-xThxO2 solid solutions: From powders to pellets

NASA Astrophysics Data System (ADS)

Balice, Luca; Bouëxière, Daniel; Cologna, Marco; Cambriani, Andrea; Vigier, Jean-François; De Bona, Emanuele; Sorarù, Gian Domenico; Kübel, Christian; Walter, Olaf; Popa, Karin

2018-01-01

Nuclear fuels production, structural materials, separation techniques, and waste management, all may benefit from an extensive knowledge in the nano-nuclear technology. In this line, we present here the production of U1-xThxO2 (x = 0 to 1) mixed oxides nanocrystals (NC's) through the hydrothermal decomposition of the oxalates in hot compressed water at 250 °C. Particles of spherical shape and size of about 5.5-6 nm are obtained during the hydrothermal decomposition process. The powdery nanocrystalline products were consolidated by spark plasma sintering into homogeneous mixed oxides pellets with grain sizes in the 0.4 to 5.5 μm range. Grain growth and mechanical properties were studied as a function of composition and size. No grain size effect was observed on the hardness or elastic modulus.

Ferrite Formation Dynamics and Microstructure Due to Inclusion Engineering in Low-Alloy Steels by Ti2O3 and TiN Addition

NASA Astrophysics Data System (ADS)

Mu, Wangzhong; Shibata, Hiroyuki; Hedström, Peter; Jönsson, Pär Göran; Nakajima, Keiji

2016-08-01

The dynamics of intragranular ferrite (IGF) formation in inclusion engineered steels with either Ti2O3 or TiN addition were investigated using in situ high temperature confocal laser scanning microscopy. Furthermore, the chemical composition of the inclusions and the final microstructure after continuous cooling transformation was investigated using electron probe microanalysis and electron backscatter diffraction, respectively. It was found that there is a significant effect of the chemical composition of the inclusions, the cooling rate, and the prior austenite grain size on the phase fractions and the starting temperatures of IGF and grain boundary ferrite (GBF). The fraction of IGF is larger in the steel with Ti2O3 addition compared to the steel with TiN addition after the same thermal cycle has been imposed. The reason for this difference is the higher potency of the TiO x phase as nucleation sites for IGF formation compared to the TiN phase, which was supported by calculations using classical nucleation theory. The IGF fraction increases with increasing prior austenite grain size, while the fraction of IGF in both steels was the highest for the intermediate cooling rate of 70 °C/min, since competing phase transformations were avoided, the structure of the IGF was though refined with increasing cooling rate. Finally, regarding the starting temperatures of IGF and GBF, they decrease with increasing cooling rate and the starting temperature of GBF decreases with increasing grain size, while the starting temperature of IGF remains constant irrespective of grain size.

Experimental Investigation of Charging Properties of Interstellar Type Silica Dust Grains by Secondary Electron Emissions

NASA Technical Reports Server (NTRS)

Tankosic, D.; Abbas, M. M.

2013-01-01

The dust charging by electron impact is an important dust charging processes in astrophysical and planetary environments. Incident low energy electrons are reflected or stick to the grains charging the dust grains negatively. At sufficiently high energies electrons penetrate the grains, leading to excitation and emission of electrons referred to as secondary electron emission (SEE). Available classical theoretical models for calculations of SEE yields are generally applicable for neutral, planar, or bulk surfaces. These models, however, are not valid for calculations of the electron impact charging properties of electrostatically charged micron/submicron-size dust grains in astrophysical environments. Rigorous quantum mechanical models are not yet available, and the SEE yields have to be determined experimentally for development of more accurate models for charging of individual dust grains. At the present time, very limited experimental data are available for charging of individual micron-size dust grains, particularly for low energy electron impact. The experimental results on individual, positively charged, micron-size lunar dust grains levitated carried out by us in a unique facility at NASA-MSFC, based on an electrodynamic balance, indicate that the SEE by electron impact is a complex process. The electron impact may lead to charging or discharging of dust grains depending upon the grain size, surface potential, electron energy, electron flux, grain composition, and configuration (Abbas et al, 2010, 2012). In this paper, we discuss SEE charging properties of individual micron-size silica microspheres that are believed to be analogs of a class of interstellar dust grains. The measurements indicate charging of the 0.2m silica particles when exposed to 25 eV electron beams and discharging when exposed to higher energy electron beams. Relatively large size silica particles (5.2-6.82m) generally discharge to lower equilibrium potentials at both electron energies. These measurements conducted on silica microspheres are qualitatively similar in nature to our previous SEE measurements on lunar Apollo missions dust samples.

The Microstructural Design of Trimodal Aluminum Composites

NASA Astrophysics Data System (ADS)

Jiang, Lin; Ma, Kaka; Yang, Hanry; Li, Meijuan; Lavernia, Enrique J.; Schoenung, Julie M.

2014-06-01

Trimodal composites, consisting of nanocrystalline or ultrafine grains (UFGs), coarse grains (CGs), and ceramic particles, were originally formulated to achieve combinations of physical and mechanical properties that are unattainable with the individual phases, such as strength, ductility, and high-strain-rate deformation. The concept of a trimodal structure is both scientifically novel as well as technologically promising because it provides multiple controllable degrees of freedom that allow for extensive microstructure design. The UFGs provide efficient obstacles for dislocation movement, such as grain boundaries and other crystalline defects. The size, distribution, and spatial arrangement of the CGs can be controlled to provide plasticity during deformation. The size, morphology, and distribution of the reinforcement particles can be tailored to attain various engineering and physical properties. Moreover, the interfaces that form among the various phases also help determine the overall behavior of the trimodal composites. In this article, a review is provided to discuss the selection and design of each component in trimodal Al composites. The toughening and strengthening mechanisms in the trimodal composite structure are discussed, paying particular attention to strategies that can be implemented to tailor microstructures for optimal mechanical behavior. Recent results obtained with high-performance trimodal Al composites that contain nanometric reinforcements are also discussed to highlight the ability to control particle-matrix interface characteristics. Finally, a perspective is provided on potential approaches that can be explored to develop the next generation of trimodal composites, and interesting scientific paradigms that evolve from the proposed design strategies are discussed.

Effects of Grain Orientation on Cu6Sn5 Growth Behavior in Cu6Sn5-Reinforced Composite Solder Joints During Electromigration

NASA Astrophysics Data System (ADS)

Han, Jing; Wang, Yan; Tan, Shihai; Guo, Fu

2018-02-01

Electromigration is a major reliability problem in composite solder joints. Due to the anisotropy of the β-Sn crystal structure, the Sn grain orientations present in the solder matrix dominate the principal failure mechanism in solder joints under electric current stressing. In this work, the Cu6Sn5 growth behavior in Cu6Sn5-reinforced composite solder joints with three different Sn grain orientations was investigated at current density of 104 A/cm2 at room temperature. Micron-sized Cu particles were added to Sn-3.5Ag solder at 2% volume fraction using an in situ method. After current stressing for 528 h, the polarity effect in the composite solder joint was greatest for an angle ( θ) between the c-axis and electron flow direction of 30°, resulting in higher growth rate of Cu6Sn5 in the solder matrix compared with composite solder joints with θ of 60° or 90°. There were no noticeable changes in the composite solder joint with θ of 90°. The growth behavior of Cu6Sn5, Cu atomic motion, and Cu diffusivity in the composite solder joints with different Sn grain orientations were analyzed in detail.

Physical characteristics of cometary dust from optical studies

NASA Technical Reports Server (NTRS)

Hanner, M. S.

1980-01-01

Observations of the sunlight scattered and thermal emission from cometary dust, which may be used to infer the physical properties of the dust grains, are reviewed. Consideration is given to the observed wavelength dependence of the scattered light from cometary coma and tails, the average scattering function of the dust grains, the average grain Bond albedo, the polarization of the scattered light, and grain temperatures deduced from thermal infrared emission. The thermal properties of dust grains are illustrated for models based on magnetite or olivine grain materials, with consideration given to the variation of thermal properties with particle radius and heliocentric distance. Comparison of the models with observations indicates that a disordered or amorphous olivine composition can give a reasonable fit to the data for appropriate grain sizes and temperatures. The observations acquired are noted to indicate an optically important particle size of 1 micron, with silicate particles not larger than a few microns usually present although pure silicate grains can not be responsible for the thermal emission, and the cometary dust grains are most likely not spherical. Further observations needed in the infrared are indicated.

Grain size dependent phase stabilities and presence of a monoclinic (Pm) phase in the morphotropic phase boundary region of (1−x)Bi(Mg{sub 1/2}Ti{sub 1/2})O{sub 3}-xPbTiO{sub 3} piezoceramics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Upadhyay, Ashutosh; Singh, Akhilesh Kumar, E-mail: akhilesh-bhu@yahoo.com, E-mail: aksingh.mst@itbhu.ac.in

2015-04-14

Results of the room temperature structural studies on (1−x)Bi(Mg{sub 1/2}Ti{sub 1/2})O{sub 3}-xPbTiO{sub 3} ceramics using Rietveld analysis of the powder x-ray diffraction data in the composition range 0.28 ≤ x ≤ 0.45 are presented. The morphotropic phase boundary region exhibits coexistence of monoclinic (space group Pm) and tetragonal (space group P4 mm) phases in the composition range 0.33 ≤ x ≤ 0.40. The structure is nearly single phase monoclinic (space group Pm) in the composition range 0.28 ≤ x ≤ 0.32. The structure for the compositions with x ≥ 0.45 is found to be predominantly tetragonal with space group P4 mm. Rietveld refinement of the structure rules out the coexistence of rhombohedral and tetragonal phases inmore » the morphotropic phase boundary region reported by earlier authors. The Rietveld structure analysis for the sample x = .35 calcined at various temperatures reveals that phase fraction of the coexisting phases in the morphotropic phase boundary region varies with grain size. The structural parameters of the two coexisting phases also change slightly with changing grain size.« less

A TEM Investigation of the Fine-Grained Matrix of the Martian Basaltic Breccia NWA 7034

NASA Technical Reports Server (NTRS)

Muttik, N.; Keller, L. P.; Agee, C. B.; McCubbin, F. M.; Santos, A. R.; Rahman, Z.

2014-01-01

The martian basaltic breccia NWA 7034 is characterized by fine-grained groundmass containing several different types of mineral grains and lithologic clasts. The matrix composition closely resembles Martian crustal rock and soil composition measured by recent rover and orbiter missions. The first results of NWA 7034 suggest that the brecciation of this martian meteorite may have formed due to eruptive volcanic processes; however, impact related brecciation processes have been proposed for paired meteorites NWA 7533 and NWA 7475]. Due to the very fine grain size of matrix, its textural details are difficult to resolve by optical and microprobe observations. In order to examine the potential nature of brecciation, transmission electron microscopy (TEM) studies combined with focused ion-beam technique (FIB) has been undertaken. Here we present the preliminary observations of fine-grained groundmass of NWA 7034 from different matrix areas by describing its textural and mineralogical variations and micro-structural characteristics.

A conceptual review of regional-scale controls on the composition of clastic sediment and the co-evolution of continental blocks and their sedimentary cover.

PubMed

Cox, R; Lowe, D R

1995-01-02

Both sediment recycling and first-cycle input influence the composition of clastic material in sedimentary systems. This paper examines conceptually the roles played by these processes in governing the composition of clastic sediment on a regional scale by outlining the expected effects on sediment composition of protracted sediment recycling and of continuous first-cycle input on a maturing continental block. Generally speaking, long-term recycling tends to enrich sediments in the most chemically and mechanically stable components: quartz in the sand and silt size fractions, and illite among the clay minerals. Sandstones trend towards pure quartz arenites, and mudrocks become more potassic and aluminous. The average grain size of clastic sediment decreases by a combination of progressive attrition of sand grains and ongoing breakdown of primary silicate minerals to finer-grained clay minerals and oxides. Sandstones derived by continuous first-cycle input from an evolving continental crustal source also become increasingly rich in quartz, but in addition become more feldspathic as the proportion of granitic material in the upper continental crust increases during crustal stabilization. Associated mudrocks also become richer in potassium and aluminum, but will have higher K2O/Al2O3 ratios than recycled muds. The average grain size of the sediment may increase with time as the proportion of sand-prone granitic source rocks increases at the expense of more mud-prone volcanic sources. In general, except in instances where chemical weathering is extreme, first-cycle sediments lack the compositional maturity of recycled detritus, and are characterized by the presence of a variety of primary silicate minerals. Sedimentary systems are not usually completely dominated by either recycling or first-cycle detritus. Generally, however, sedimentary systems associated with the earliest phases of formation and accretion of continental crust are characterized by first-cycle input from igneous and metamorphic rocks, whereas those associated with more mature cratons tend to be dominated by recycled sedimentary material.

C, N, and O Isotopic Heterogeneities in Low-density Supernova Graphite Grains from Orgueil

NASA Astrophysics Data System (ADS)

Groopman, Evan; Bernatowicz, Thomas; Zinner, Ernst

2012-07-01

We report on the results of NanoSIMS isotope imaging of low-density supernova graphite grains from the Orgueil meteorite. 70 nm thick microtomed sections of three supernova graphite grains were deposited on Si wafers and isotopically imaged in the NanoSIMS. These sections contain hotspots of excesses in 18O and 15N, which are spatially well correlated, and are likely carried by internal TiC subgrains. These hotspots are considerably more enriched in 18O and 15N than the host graphite grain. Correlations between 18O and 15N excesses indicate that the grains incorporated material from the He/C supernova zone. Isotope images of the surfaces of some grains show heterogeneities in their N and O isotope compositions, with extreme excesses in 15N and 18O. In the microtome sections, we also observe two types of heterogeneities in the grains' C isotopic compositions: smooth, radial gradients in 12C/13C, with this ratio trending toward solar with increasing radius; and highly anomalous pockets up to 2 μm in size with 12C/13C Gt solar that are located near the centers of the grain sections. Partial isotopic equilibration does not likely explain the C isotopic heterogeneities. These grains and their constituent parts probably formed in a stellar environment with changing isotopic composition.

Terrigenous sediment supply along the Chilean continental margin: modern regional patterns of texture and composition

NASA Astrophysics Data System (ADS)

Lamy, F.; Hebbeln, D.; Wefer, G.

The regional patterns of texture and composition of modern continental slope and pelagic sediments off Chile between 25°S and 43°S reflect the latitudinal segmentation of geological, morphological, and climatic features of the continental hinterland. Grain-size characteristics are controlled by the grain-size of source rocks, the weathering regime, and mode of sediment input (eolian off northern Chile vs fluvial further south). Bulk-mineral assemblages reveal a low grade of maturity. Regional variations are governed by the source-rock composition of the different geological terranes and the relative source-rock contribution of the Coastal Range and Andes, as controlled by the continental hydrology. The relative abundance of clay minerals is also predominantly influenced by the source-rock composition and partly by continental smectite neoformation. Latitudinal variations of illite crystallinities along the Chilean continental slope (and west of the Peru-Chile trench) clearly reflect modifications of the weathering regime which correspond to the strong climatic zonation of Chile.

Grain Size Distribution in Mudstones: A Question of Nature vs. Nurture

NASA Astrophysics Data System (ADS)

Schieber, J.

2011-12-01

Grain size distribution in mudstones is affected by the composition of the source material, the processes of transport and deposition, and post-depositional diagenetic modification. With regard to source, it does make a difference whether for example a slate belt is eroded vs a stable craton. The former setting tends to provide a broad range of detrital quartz in the sub 62 micron size range in addition to clays and greenschist grade rock fragments, whereas the latter may be biased towards coarser quartz silt (30-60 microns), in addition to clays and mica flakes. In flume experiments, when fine grained materials are transported in turbulent flows at velocities that allow floccules to transfer to bedload, a systematic shift of grain size distribution towards an increasingly finer grained suspended load is observed as velocity is lowered. This implies that the bedload floccules are initially constructed of only the coarsest clay particles at high velocities, and that finer clay particles become incorporated into floccules as velocity is lowered. Implications for the rock record are that clay beds deposited from decelerating flows should show subtle internal grading of coarser clay particles; and that clay beds deposited from continuous fast flows should show a uniform distribution of coarse clays. Still water settled clays should show a well developed lower (coarser) and upper (finer) subdivision. A final complication arises when diagenetic processes, such as the dissolution of biogenic silica, give rise to diagenetic quartz grains in the silt to sand size range. This diagenetic silica precipitates in fossil cavities and pore spaces of uncompacted muds, and on casual inspection can be mistaken for detrital quartz. In distal mudstone successions close to 100 % of "apparent" quartz silt can be of that origin, and reworking by bottom currents can further enhance a detrital perception by producing rippled and laminated silt beds. Although understanding how size distributions in mudstones evolve is considered central to problems in hillslope, fluvial, aeolian, coastal, and submarine systems, one can not simply measure distributions and hope to arrive at an answer. The complex origins of mudstones are reflected in their very broad compositional range, and multiple overprinted processes have to be considered in order to make sense out of observed grain size distributions.

Carbon, nitrogen, magnesium, silicon, and titanium isotopic compositions of single interstellar silicon carbide grains from the Murchison carbonaceous chondrite

NASA Technical Reports Server (NTRS)

Hoppe, Peter; Amari, Sachiko; Zinner, Ernst; Ireland, Trevor; Lewis, Roy S.

1994-01-01

Seven hundred and twenty SiC grains from the Murchison CM2 chondrite, ranging in size from 1 to 10 micrometers, were analyzed by ion microprobe mass spectrometry for their C-isotopic compositions. Subsets of the grains were also analyzed for N (450 grains), Si (183 grains), Mg (179 grains), and Ti (28 grains) isotopes. These results are compared with previous measurements on 41 larger SiC grains (up to 15 x 26 micrometers) from a different sample of Murchison analyzed by Virag et al. (1992) and Ireland, Zinner, & Amari (1991a). All grains of the present study are isotopically anomalous with C-12/C-13 ratios ranging from 0.022 to 28.4 x solar, N-14/N-15 ratios from 0.046 to 30 x solar, Si-29/Si-28 from 0.54 to 1.20 x solar, Si-30/Si-28 from 0.42 to 1.14 x solar, Ti-49/Ti-48 from 0.96 to 1.95 x solar, and Ti-50/Ti-48 from 0.94 to 1.39 x solar. Many grains have large Mg-26 excesses from the decay of Al-26 with inferred Al-26/Al-27 ratios ranging up to 0.61, or 12,200 x the ratio of 5 x 10(exp -5) inferred for the early solar system. Several groups can be distinguished among the SiC grains. Most of the grains have C-13 and N-14 excesses, and their Si isotopic compositions (mostly excesses in Si-29 and Si-30) plot close to a slope 1.34 line on a Delta Si-29/Si-28 versus Delta Si-30/Si-28 three-isotope plot. Grains with small C-12/C-13 ratios (less than 10) tend to have smaller or no N-14 excesses and high Al-26/Al-27 ratios (up to 0.01). Grains with C-12/C-13 greater than 150 fall into two groups: grains X have N-15 excesses and Si-29 and Si-30 deficits and the highest (0.1 to 0.6) Al-26/Al-27 ratios; grains Y have N-14 excesses and plot on a slope 0.35 line on a Si three-isotope plot. In addition, large SiC grains of the Virag et al. (1992) study fall into three-distinct clusters according to their C-, Si-, and Ti-isotopic compositions. The isotopic diversity of the grains and the clustering of their isotopic compositions imply distinct and multiple stellar sources. The C- and N-isotopic compositions of most grains are consistent with H-burning in the CNO cycle. These and s-process Kr, Xe, Ba, and Nd suggest asymptotic giant branch (AGB) or Wolf-Rayet stars as likely sources for the grains, but existing models of nucleosynthesis in these stellar sites fail to account in detail for all the observed isotopic compositions. Special problems are posed by grains with C-12/C-13 less than 10 and almost normal and heavy N-isotopic compositions. Also the Si- and Ti-isotopic compositions, with excesses in Si-29 and Si-30 relative to Si-28 and excesses in all Ti isotopes relative to Ti-48, do not precisely conform with the compositions predicted for slow neutron capture. Additional theoretical efforts are needed to achieve an understanding of the isotopic composition of the SiC grains and their stellar sources.

Processing, microstructure evolution and properties of nanoscale aluminum alloys

NASA Astrophysics Data System (ADS)

Han, Jixiong

In this project, phase transformations and precipitation behavior in age-hardenable nanoscale materials systems, using Al-Cu alloys as model materials, were first studied. The Al-Cu nanoparticles were synthesized by a Plasma Ablation process and found to contain a 2˜5 nm thick adherent aluminum oxide scale, which prevented further oxidation. On aging of the particles, a precipitation sequence consisting of, nearly pure Cu precipitates to the metastable theta' to equilibrium theta was observed, with all three forming along the oxide-particle interface. The structure of theta' and its interface with the Al matrix has been characterized in detail. Ultrafine Al-Cu nanoparticles (5˜25 nm) were also synthesized by inert gas condensation (IGC) and their aging behavior was studied. These particles were found to be quite stable against precipitation. Secondly, pure Al nanoparticles were prepared by the Exploding Wire process and their sintering and consolidation behavior were studied. It was found that nanopowders of Al could be processed to bulk structures with high hardness and density. Sintering temperature was found to have a dominant effect on density, hardness and microstructure. Sintering at temperatures >600°C led to breakup of the oxide scale, leading to an interesting nanocomposite composed of 100˜200 nm Al oxide dispersed in a bimodal nanometer-micrometer size Al matrix grains. Although there was some grain growth, the randomly dispersed oxide fragments were quite effective in pinning the Al grain boundaries, preventing excessive grain growth and retaining high hardness. Cold rolling and hot rolling were effective methods for attaining full densification and high hardness. Thirdly, the microstructure evolution and mechanical behavior of Al-Al 2O3 nanocomposites were studied. The composites can retain high strength at elevated temperature and thermal soaking has practically no detrimental effect on strength. Although the ductility of the composite remains quite low, there was substantial evidence for high localized plasticity. The strengthening mechanisms of the composite include: Orowan strengthening, grain size strengthening and Forest strengthening. Finally, the microstructure evolution and mechanical behavior of 2024Al-Al 2O3 nanocomposites were studied. This 2024Al-Al2O 3 composite exhibits similar thermal stability and high strength at elevated temperature as Al-Al2O3. On aging, the matrix of 2024Al-Al2O3 composites revealed a precipitation sequence of: alphaAl → GP/GPB → theta'/S' → theta/S. The strengthening mechanisms of the 2024Al-Al2O3 composites include precipitation strengthening, Orowan strengthening, grain size strengthening and Forest strengthening.

Capacitance scaling of grain boundaries with colossal permittivity of CaCu3Ti4O12-based materials

NASA Astrophysics Data System (ADS)

De Almeida-Didry, Sonia; Autret, Cécile; Honstettre, Christophe; Lucas, Anthony; Pacreau, François; Gervais, François

2015-04-01

Samples of copper-deficient CaCu3Ti4O12 (CCTO) compared to the nominal composition, all synthesized via organic gel-assisted citrate process, show huge change of grain boundaries capacitance as deduced from a fit of an RC element model to the impedance spectroscopic data. The grain boundary capacitance is found to scale with the permittivity measured at 1 kHz weighted by the size of the grains. This result is found consistent with the internal barrier layer capacitance (IBLC) model.

Quantification of the effects of secondary matrix on the analysis of sandstone composition, and a petrographic-chemical technique for retrieving original framework grain modes of altered sandstones.

PubMed

Cox, R; Lowe, D R

1996-05-01

Most studies of sandstone provenance involve modal analysis of framework grains using techniques that exclude the fine-grained breakdown products of labile mineral grains and rock fragments, usually termed secondary matrix or pseudomatrix. However, the data presented here demonstrate that, when the proportion of pseudomatrix in a sandstone exceeds 10%, standard petrographic analysis can lead to incorrect provenance interpretation. Petrographic schemes for provenance analysis such as QFL and QFR should not therefore be applied to sandstones containing more than 10% secondary matrix. Pseudomatrix is commonly abundant in sandstones, and this is therefore a problem for provenance analysis. The difficulty can be alleviated by the use of whole-rock chemistry in addition to petrographic analysis. Combination of chemical and point-count data permits the construction of normative compositions that approximate original framework grain compositions. Provenance analysis is also complicated in many cases by fundamental compositional alteration during weathering and transport. Many sandstones, particularly shallow marine deposits, have undergone vigorous reworking, which may destroy unstable mineral grains and rock fragments. In such cases it may not be possible to retrieve provenance information by either petrographic or chemical means. Because of this, pseudomatrix-rich sandstones should be routinely included in chemical-petrological provenance analysis. Because of the many factors, both pre- and post-depositional, that operate to increase the compositional maturity of sandstones, petrologic studies must include a complete inventory of matrix proportions, grain size and sorting parameters, and an assessment of depositional setting.

The electrodeposition of silver composites using deep eutectic solvents.

PubMed

Abbott, Andrew P; El Ttaib, Khalid; Frisch, Gero; Ryder, Karl S; Weston, David

2012-02-21

Silver is an important metal for electronic connectors, however, it is extremely soft and wear can be a significant issue. This paper describes how improved wear resistant silver coatings can be obtained from the electrolytic deposition of silver from a solution of AgCl in an ethylene glycol/choline chloride based Deep Eutectic Solvent. An up to 10-fold decrease in the wear volume is observed by the incorporation of SiC or Al(2)O(3) particles. The work also addresses the fundamental aspect of speciation of silver chloride in solution using EXAFS to probe solution structure. The size but not the nature of the composite particles is seen to change the morphology and grain size of the silver deposit. Grain sizes are shown to be consistent with previous nucleation studies. The addition of LiF is found to significantly affect the deposit morphology and improve wear resistance.

Characteristics and origin of coarse gold in Late Pleistocene sediments of the Cariboo placer mining district, British Columbia, Canada

NASA Astrophysics Data System (ADS)

Eyles, N.

1995-02-01

The Cariboo placer mining district (1000 km 2) sited in the Interior Plateau of central British Columbia, Canada, is the premier placer gold mining district of the Province. Gold is recovered from three Late Pleistocene sedimentary facies: postglacial fluvial gravels (< 10 Ka), Late Wisconsin till (ca. 25-10 Ka), and "older" fluvial gravels (>25 Ka). This study reports the morphology (size, roundness, sphericity) of 1636 gold grains, ranging in size from 0.25 to 17 mm, recovered from 19 placer mines. Older gravels contain the smallest gold grains (mean grani size 1.53 mm), grains of intermediate size occur in till (2.23 mm) and the coarsest gold occurs in postglacial gravels (2.34 mm) with a mean of 1.93 mm for the mining district as a whole. The most common grain shapes are sub-rounded, discoidal (14.73% of the grain population), sub-angular, discoidal (10.88%), and sub-rounded, sub-discoidal (9.59%); the most angular grains occur in postglacial gravels. In-situ growth of coarse, angular grains is indicated by a "composite" grain structure, consisting of aggregates of gold particles welded together by high-grade (Ag = < 2%) filamentous gold; in-situ coarsening may be reliant on organic complexing agents produced below a dense forest cover. An evolutionary sequence of grain form, from angular aggregates to rounded "pumpkin seed" grains, is suggested. Rounded grains commonly show a crystalline structure which may result from the cold hammering of gold during transport; fracturing along crystal boundaries is common. Gold grains may undergo cycles of coarsening, rounding, diagenesis and breakup in response to repeated recycling through Pleistocene sedimentary environments.

Experimental Investigations of the Physical and Optical Properties of Individual Micron/Submicron-Size Dust Grains in Astrophysical Environments

NASA Technical Reports Server (NTRS)

Abbas, M. M.; Tankosic, D.; LeClair, A.

2014-01-01

Dust grains constitute a significant component of matter in the universe, and play an important and crucial role in the formation and evolution of the stellar/planetary systems in interstellar dust clouds. Knowledge of physical and optical properties of dust grains is required for understanding of a variety of processes in astrophysical and planetary environments. The currently available and generally employed data on the properties of dust grains is based on bulk materials, with analytical models employed to deduce the corresponding values for individual small micron/submicron-size dust grains. However, it has been well-recognized over a long period, that the properties of individual smallsize dust grains may be very different from those deduced from bulk materials. This has been validated by a series of experimental investigations carried out over the last few years, on a laboratory facility based on an Electrodynamic Balance at NASA, which permits levitation of single small-size dust grains of desired composition and size, in vacuum, in simulated space environments. In this paper, we present a brief review of the results of a series of selected investigations carried out on the analogs of interstellar and planetary dust grains, as well as dust grains obtained by Apollo-l1-17 lunar missions. The selected investigations, with analytical results and discussions, include: (a) Direct measurements of radiation on individual dust grains (b) Rotation and alignments of dust grains by radiative torque (c) Charging properties of dust grains by: (i) UV Photo-electric emissions (ii) Electron Impact. The results from these experiments are examined in the light of the current theories of the processes involved.

The molecular composition of dense interstellar clouds

NASA Technical Reports Server (NTRS)

Allen, M.; Robinson, G. W.

1977-01-01

Presented in this paper is an ab initio chemical model for dense interstellar clouds that incorporates 598 grain surface reactions, with small grains providing the reaction area. Gas-phase molecules are depleted through collisions with grains. The abundances of 372 chemical species are calculated as a function of time and are found to be of sufficient magnitude to explain most observations. Peak abundances are achieved on time scales of the order of 100,000 to 1 million years, depending on cloud density and kinetic temperature. The reaction rates for ion-molecule chemistry are approximately the same, indicating that surface and gas-phase chemistry may be coupled in certain regions. The composition of grain mantles is shown to be a function of grain radius. In certain grain-size ranges, large molecules containing two or more heavy atoms are more predominant than lighter 'ices' - H2O, NH3, and CH4. It is possible that absorption due to these large molecules in the mantle may contribute to the observed 3-micron band in astronomical spectra.

Size effects on magnetic actuation in Ni-Mn-Ga shape-memory alloys.

PubMed

Dunand, David C; Müllner, Peter

2011-01-11

The off-stoichiometric Ni(2)MnGa Heusler alloy is a magnetic shape-memory alloy capable of reversible magnetic-field-induced strains (MFIS). These are generated by twin boundaries moving under the influence of an internal stress produced by a magnetic field through the magnetocrystalline anisotropy. While MFIS are very large (up to 10%) for monocrystalline Ni-Mn-Ga, they are near zero (<0.01%) in fine-grained polycrystals due to incompatibilities during twinning of neighboring grains and the resulting internal geometrical constraints. By growing the grains and/or shrinking the sample, the grain size becomes comparable to one or more characteristic sample sizes (film thickness, wire or strut diameter, ribbon width, particle diameter, etc), and the grains become surrounded by free space. This reduces the incompatibilities between neighboring grains and can favor twinning and thus increase the MFIS. This approach was validated recently with very large MFIS (0.2-8%) measured in Ni-Mn-Ga fibers and foams with bamboo grains with dimensions similar to the fiber or strut diameters and in thin plates where grain diameters are comparable to plate thickness. Here, we review processing, micro- and macrostructure, and magneto-mechanical properties of (i) Ni-Mn-Ga powders, fibers, ribbons and films with one or more small dimension, which are amenable to the growth of bamboo grains leading to large MFIS, and (ii) "constructs" from these structural elements (e.g., mats, laminates, textiles, foams and composites). Various strategies are proposed to accentuate this geometric effect which enables large MFIS in polycrystalline Ni-Mn-Ga by matching grain and sample sizes.

Relict grains in chondrules: Evidence for chondrule recycling

NASA Technical Reports Server (NTRS)

Jones, R. H.

1994-01-01

The presence of relict grains in chondrules, which offers some insight into the degree to which chondrule material was recycled in the chondrule-forming region, is discussed in this report. Relics are grains that clearly did not crystallize in situ in the host chondrule. They represent coarse-grained precursor material that did not melt during chondrule formation, and provide the only tangible record of chondrule precursor grains. Relics are commonly identified by a large difference in size, textural differences, and/or significant compositional differences compared with normal grains in the host chondrule. Two important types of relics are: (1) 'dusty,' metal-bearing grains of olivine and pyroxene; and (2) forsterite (Mg-rich olivine) grains present in FeO-rich chondrules.

Relation between the microstructure and the electromagnetic properties of BaTiO3/Ni0.5Zn0.5Fe2O4 ceramic composite

NASA Astrophysics Data System (ADS)

Xiao, Bin; Tang, Yu; Ma, Guodong; Ma, Ning; Du, Piyi

2015-06-01

The microstructure-property relation in ferroelectric/ferromagnetic composite is investigated in detail, exemplified by typical sol-gel-derived 0.3BTO/0.7NZFO ceramic composite. The effect of microstructural factors including intergrain connectivity, grain size and interfaces on the dielectric and magnetic properties of the composite prepared by conventional ceramic method and three-step sintering method is discussed both experimentally and theoretically. It reveals that the dielectric behavior of the composite is controlled by a hybrid dielectric process that combines the contribution of Debye-like dipoles and Maxwell-Wagner (M-W or interfacial) polarization. Enhanced dielectric, magnetic and conductive behaviors appear in the composite with better intergrain connectivity and larger grain size derived by sol-gel route and three-step sintering method. The effective permittivity contributed by Debye-like dipoles exhibits a value of ~130,000 in three-step sintered composite, which is almost the same as that in conventionally sintered one, but that contributed by M-W response is much smaller in the former. Compared with conventionally prepared samples, the relaxation time ( τ) is 3.476 × 10-6 s, about one order of magnitude smaller, and the dc electrical conductivity is 3.890 × 10-3 S/m, one order of magnitude higher in three-step sintered composite. The minimum dielectric loss reveals almost the same (~0.2) for all samples, but shows distinguishable difference in low-frequency region. Meanwhile, an initial permeability of 84, twice as large as that of conventionally prepared composite and 56 % the value of single-phased NZFO ferrite (~150), and a saturation magnetization of 63.5 emu/g, 32 % higher than that of conventional one and approximately 84 % the value of single-phased NZFO ferrite (~76 emu/g), appear simultaneously in three-step sintered composite with larger grain size and better intergrain connectivity. It is clear that the discovery is helpful for establishing a more explicit view on the physics of multi-functional composite materials, while the composite with optimized microstructure is beneficial to be used as a high-performance material.

Magma Mixing: Magmatic Enclaves in Morne Micotrin, Dominica

NASA Astrophysics Data System (ADS)

Hickernell, S.; Frey, H. M.; Manon, M. R. F.; Waters, L. E.

2017-12-01

Magmatic enclaves in volcanic rocks provide direct evidence of magma mingling/mixing within a magma reservoir and may reinvigorate the system and trigger eruption, as documented at the Soufriere Hills in Montserrat. Lava domes on the neighboring island of Dominica also contain multiple enclave populations and may be evidence for similar magma chamber processes. The central dome of Micotrin is at the head of the Roseau Valley, which was filled with 3 km3 of pyroclastic deposits from eruptions spanning 65 - 25 ka. There appear to be two distinct types of enclaves in the crystal-rich Micotrin andesites (60 wt% SiO2), fine-grained and coarse-grained. Fine-grained mafic enclaves (52 wt% SiO2) vary in size from 1 to 15 cm in diameter, whereas the coarse-grained enclaves are generally larger and range from 3-20 cm. Fine-grained enclaves are saturated in plag (35%) + opx (35%) + cpx (20%) + oxides (10%). Average pyroxenes are 0.01 to 0.02 cm in size, whereas plagioclase averages 0.05 cm and up to 0.1 cm. The texture of the fine-grained enclaves is cumulate-like, devoid of microlites and matrix glass. Coarse-grained enclaves lack cpx and have different modal abundances and textures: plag (75%) + opx (10%) + oxides (5%) + plag microlites (10%). Plagioclase are 0.1 cm in size and orthopyroxenes average 0.05 cm. The coarse-grained enclaves are highly vesicular, a notable difference from the host as well as the fine-grained enclaves. The boundaries of both the fine- and coarse-grained enclaves are quite sharp and distinct and there do not appear to be enclave minerals disaggregated in the host rock. Temperatures were determined by two oxides. The fine-grained enclaves had two populations of magnetite, yielding 847 + 21° and 920 + 17°C. The coarse-grained enclave was 890 + 42 °C, but the oxides were extensively exsolved. Plagioclase composition in both coarse and fine-grained samples was comparable, ranging from An50 to An80. Despite compositional similarity the textures of the plagioclase are distinctive. Fine-grained enclave plagioclase has patchy, uneven zoning, whereas coarse-grained enclave plagioclase has oscillatory zoning. The presence of these enclaves indicates that there may be several different magma inputs contributing to the system that is feeding Micotrin, and the injection of these unique magmas may be eruption triggers.

Optical and dielectric properties of poly(vinyl-alcohol) - Cobalt oxide nanocomposite film

NASA Astrophysics Data System (ADS)

Das, Amit Kumar; Tripathi, Himadri Sekhar; Meikap, Ajit Kumar

2018-04-01

Highly crystalline cobalt oxide (Co3O4) have been synthesized via calcination method. The crystallite size of the nanoparticles is 28.5 nm. Two direct band gap of Co3O4 is observed. The temperature dependent dielectric spectroscopy of PVA-Co3O4 composite film shows ferroelectric behavior. The dielectric constant of the composite film is almost 2.5 times compare to pure PVA at a 1kHz frequency and room temperature. From the Nyquist plot grain and grain boundary effects are identified.

Frequency Dependent Susceptibility Analysis of Magnetic Carriers: Application to Fe-Oxides on Mars surface

NASA Astrophysics Data System (ADS)

Adachi, T.; Kletetschka, G.; Mikula, V.

2007-12-01

On Mars, Fe-oxides mineral phases (inferred/detected) are mainly magnetite, pyrrhotite, and hematite. Kletetschka et al., 2005 suggested that the grain size dependent potential may contribute to the Mars surface magnetic anomaly. Grain size of Fe-oxides may play a role for the magnetic signature and anomaly on Mars. According to Kletetschka et al., 2005, the larger the grain size, the larger the magnetization (in this case hematite's TRM). Weather they are magnetite, pyrrhotite or hematite, nano-phase or superparamagnetic grains may contribute to the absence of remanent magnetization on the surface of Mars. In this contribution we tackle how to resolve grain size variations by frequency dependent susceptibility measured on terrestrial hematite samples such as hemo-ilmenite from Allard Lake, Canada, Mars analogue concretions from Utah and Czech Republic, and hematite aggregates from Hawaii. The magnetic characteristics of hematite-goethite mineralogies of Utah and Czech concretions suggested (Adachi et al., 2007) that they contain super paramagnetic (SP) to single domain (SD) magnetic states. Coercivity spectra analysis from acquisition of isothermal remanent magnetization (IRM) data showed the distinct behaviors of hematite, goethite, and mixed composition of both. The estimated magnetic states are analyzed with the frequency-dependent susceptibility instrument (500-250,000 Hertz). The frequency- and size-dependent susceptibility for hematite, goethite, and magnetite are calibrated using the known size powdered (commercial) samples.

Development of SiC Nanoparticles and Second Phases Synergistically Reinforced Mg-Based Composites Processed by Multi-Pass Forging with Varying Temperatures

PubMed Central

Nie, Kaibo; Guo, Yachao; Deng, Kunkun; Wang, Xiaojun; Wu, Kun

2018-01-01

In this study, SiC nanoparticles were added into matrix alloy through a combination of semisolid stirring and ultrasonic vibration while dynamic precipitation of second phases was obtained through multi-pass forging with varying temperatures. During single-pass forging of the present composite, as the deformation temperature increased, the extent of recrystallization increased, and grains were refined due to the inhibition effect of the increasing amount of dispersed SiC nanoparticles. A small amount of twins within the SiC nanoparticle dense zone could be found while the precipitated phases of Mg17Al12 in long strips and deformation bands with high density dislocations were formed in the particle sparse zone after single-pass forging at 350 °C. This indicated that the particle sparse zone was mainly deformed by dislocation slip while the nanoparticle dense zone may have been deformed by twinning. The yield strength and ultimate tensile strength of the composites were gradually enhanced through increasing the single-pass forging temperature from 300 °C to 400 °C, which demonstrated that initial high forging temperature contributed to the improvement of the mechanical properties. During multi-pass forging with varying temperatures, the grain size of the composite was gradually decreased while the grain size distribution tended to be uniform with reducing the deformation temperature and extending the forging passes. In addition, the amount of precipitated second phases was significantly increased compared with that after multi-pass forging under a constant temperature. The improvement in the yield strength of the developed composite was related to grain refinement strengthening and Orowan strengthening resulting from synergistical effect of the externally applied SiC nanoparticles and internally precipitated second phases. PMID:29342883

Development of SiC Nanoparticles and Second Phases Synergistically Reinforced Mg-Based Composites Processed by Multi-Pass Forging with Varying Temperatures.

PubMed

Nie, Kaibo; Guo, Yachao; Deng, Kunkun; Wang, Xiaojun; Wu, Kun

2018-01-13

In this study, SiC nanoparticles were added into matrix alloy through a combination of semisolid stirring and ultrasonic vibration while dynamic precipitation of second phases was obtained through multi-pass forging with varying temperatures. During single-pass forging of the present composite, as the deformation temperature increased, the extent of recrystallization increased, and grains were refined due to the inhibition effect of the increasing amount of dispersed SiC nanoparticles. A small amount of twins within the SiC nanoparticle dense zone could be found while the precipitated phases of Mg 17 Al 12 in long strips and deformation bands with high density dislocations were formed in the particle sparse zone after single-pass forging at 350 °C. This indicated that the particle sparse zone was mainly deformed by dislocation slip while the nanoparticle dense zone may have been deformed by twinning. The yield strength and ultimate tensile strength of the composites were gradually enhanced through increasing the single-pass forging temperature from 300 °C to 400 °C, which demonstrated that initial high forging temperature contributed to the improvement of the mechanical properties. During multi-pass forging with varying temperatures, the grain size of the composite was gradually decreased while the grain size distribution tended to be uniform with reducing the deformation temperature and extending the forging passes. In addition, the amount of precipitated second phases was significantly increased compared with that after multi-pass forging under a constant temperature. The improvement in the yield strength of the developed composite was related to grain refinement strengthening and Orowan strengthening resulting from synergistical effect of the externally applied SiC nanoparticles and internally precipitated second phases.

Toward unraveling a secret of the lower mantle: Detecting and characterizing piles using a grain size-dependent, composite rheology

NASA Astrophysics Data System (ADS)

Schierjott, Jana; Rozel, Antoine; Tackley, Paul

2017-04-01

Seismic studies show two antipodal regions of low shear velocity at the core-mantle boundary (CMB), one beneath the Pacific and one beneath Africa. These regions, called Large Low Shear Velocity Provinces (LLSVPs), are thought to be thermally and chemically distinct and thus have a different density and viscosity. Whereas there is some general consensus about the density of the LLSVPs, their viscosity is still debated. So far, in numerical studies the viscosity is treated as either depth- and/or temperature- dependent but the potential grain size-dependence of the viscosity is neglected most of the time. In this study we use a self-consistent convection model which includes a grain size- dependent rheology based on the approach by Rozel et al. (2011). Further, we consider a basal primordial layer and a time-dependent basalt production to dynamically form the present-day chemical heterogeneities, similar to earlier studies, e.g by Nakagawa & Tackley (2014). Our study comprises three main parts: 1) We perform a parameter study which includes different densities and viscosities of the imposed primordial layer. 2) We detect possible piles and compute their average effective viscosity, density, rheology and grain size. 3) We test the influence of grain size evolution on the development and morphology of piles and compare it to non-grain size models. Our preliminary results show that a higher density and/or viscosity of the piles is needed to keep them at the core-mantle boundary (CMB). Relatively to the ambient mantle grain size is high in the piles but due to the temperature at the CMB the viscosity is not remarkably different than the one of ordinary plumes. We observe that grain size is lower if the density of the imposed primordial material is lower than basalt. In that case the average temperature of the pile is also reduced. Interestingly, changing the reference viscosity is responsible for a change in the average viscosity of the pile but not for a different average grain size.

Morphology and composition of gold in a lateritic profile, Fazenda Pison “Garimpo”, Amazon, Brazil

NASA Astrophysics Data System (ADS)

Larizzatti, J. H.; Oliveira, S. M. B.; Butt, C. R. M.

2008-05-01

This study describes the morphological evolution of gold grains in a lateritic weathering profile in an equatorial rainforest climate. Primary sources of gold are quartz veins associated with shallow granophyric intrusion. Gold grains were found in fresh ore, saprolite, transition zones, ferruginous duricrust, red latosol, and yellow latosol. Irregularly shaped grains predominate, with smaller proportions of dendritic and prismatic forms. Gold grains are weathered in the uppermost 10 m of the regolith. Mean gold grain size is maximum in the duricrust (>125 μm) and decreases progressively upward into the yellow latosol (<90 μm). Voids and corrosion pits appear on grain surfaces, and progressive rounding is observed from the bottom of the profile to the top. Gold grains can be classified as either homogeneous or zoned with respect to their chemical composition. Homogeneous grains contain 2-15% Ag (mean 8.3%). Zoned grains have more variable Ag contents; grain cores have means of approximately 10% or 23% Ag, with Ag-poor zones of approximately 3.7% Ag along internal discontinuities and/or outer rims. Formation of Ag-poor rims is due to preferential depletion of silver. Processes responsible for duricrust formation may preserve some grains as large aggregates, but subsequent transformation into latosol further modifies them.

Enhanced thermal conductivity of uranium dioxide-silicon carbide composite fuel pellets prepared by Spark Plasma Sintering (SPS)

NASA Astrophysics Data System (ADS)

Yeo, S.; Mckenna, E.; Baney, R.; Subhash, G.; Tulenko, J.

2013-02-01

Uranium dioxide (UO2)-10 vol% silicon carbide (SiC) composite fuel pellets were produced by oxidative sintering and Spark Plasma Sintering (SPS) at a range of temperatures from 1400 to 1600 °C. Both SiC whiskers and SiC powder particles were utilized. Oxidative sintering was employed over 4 h and the SPS sintering was employed only for 5 min at the highest hold temperature. It was noted that composite pellets sintered by SPS process revealed smaller grain size, reduced formation of chemical products, higher density, and enhanced interfacial contact compared to the pellets made by oxidative sintering. For given volume of SiC, the pellets with powder particles yielded a smaller grain size than pellets with SiC whiskers. Finally thermal conductivity measurements at 100 °C, 500 °C, and 900 °C revealed that SPS sintered UO2-SiC composites exhibited an increase of up to 62% in thermal conductivity compared to UO2 pellets, while the oxidative sintered composite pellets revealed significantly inferior thermal conductivity values. The current study points to the improved processing capabilities of SPS compared to oxidative sintering of UO2-SiC composites.

Tailored Net-Shape Powder Composites by Spark Plasma Sintering

NASA Astrophysics Data System (ADS)

Khaleghi, Evan Aryan

This dissertation investigates the ability to produce net-shape and tailored composites in spark plasma sintering (SPS), with an analysis of how grain growth, densification, and mechanical properties are affected. Using alumina and four progressively anisotropic dies, we studied the impact of specimen shape on densification. We found specimen shape had an impact on overall densification, but no impact on localized properties. We expected areas of the specimen to densify differently, or have higher grain growth, based on current anisotropy in the specimen during sintering, and preliminary results indicated this, but further investigation showed this did not occur. Overall average grain size and porosity decreased as shape complexity increased. In Fe-V-C steel, we mechanical alloyed two rapidly solidified powders, and used spark sintering to retain the properties imparted during the rapid solidification. We noticed VC grains being produced during densification, which improved the final properties. We conducted spark plasma extrusion (SPE) of aluminum to understand the effect on microstructure. We found, through an analysis of the grain structure, that SPE did have a grain deformation potential, and grain size was severely decreased compared to conventional sintering. Dynamic recrystallization did not occur, due to the reduced temperatures we were able to extrude with SPS. Finally, we examined whether there were particular sintering conditions for SPS that reduced the complexity of the grain growth and porosity relationship to one similar to conventional sintering, of the form G = k G0 ε -1/. We found that although a reasonable case could be made for free sintering, as found in the literature, for hot-pressing and SPS the conditions required go against the common knowledge in grain growth and densification kinetics. We were able to fit our data very well to the model, but the correlated results do not make physical sense.

Laboratory Studies of the Optical Properties and Condensation Processes of Cosmic Dust Grains

NASA Technical Reports Server (NTRS)

Abbas, M. M.; Craven, P. D.; Spann, J. F.; Tankosic, D.; LeClair, A.; West, E.; Sheldon, R.; Witherow, W. K.; Gallagher, D. L.; Adrian, M. L.

2002-01-01

A laboratory facility for conducting a variety of experiments on single isolated dust particles of astrophysical interest levitated in an electrodynamics balance has been developed at NASA/Marshall Space Flight Center. The objective of the research is to employ this experimental technique for studies of the physical and optical properties of individual cosmic dust grains of 0.1-100 micron size in controlled pressure/temperatures environments simulating astrophysical conditions. The physical and optical properties of the analogs of interstellar and interplanetary dust grains of known composition and size distribution will be investigated by this facility. In particular, we will carry out three classes of experiments to study the micro-physics of cosmic dust grains. (1) Charge characteristics of micron size single dust grains to determine the photoelectric efficiencies, yields, and equilibrium potentials when exposed to UV radiation. (2) Infrared optical properties of dust particles (extinction coefficients and scattering phase functions) in the 1-30 micron region using infrared diode lasers and measuring the scattered radiation. (3) Condensation experiments to investigate the condensation of volatile gases on colder nucleated particles in dense interstellar clouds and lower planetary atmospheres. The condensation experiments will involve levitated nucleus dust grains of known composition and initial mass (or m/q ratio), cooled to a temperature and pressure (or scaled pressure) simulating the astrophysical conditions, and injection of a volatile gas at a higher temperature from a controlled port. The increase in the mass due to condensation on the particle will be monitored as a function of the dust particle temperature and the partial pressure of the injected volatile gas. The measured data will permit determination of the sticking coefficients of volatile gases and growth rates of dust particles of astrophysical interest. Some preliminary results based on measurements of photoelectric emission and radiation pressure on single isolated 0.2 to 6.6 micron size silica particles exposed to UV radiation at 120-200 nm and green laser light at 532 nm are presented.

Nd Isotope and U-Th-Pb Age Mapping of Single Monazite Grains by Laser Ablation Split Stream Analysis

NASA Astrophysics Data System (ADS)

Fisher, C. M.; Hanchar, J. M.; Miller, C. F.; Phillips, S.; Vervoort, J. D.; Martin, W.

2015-12-01

Monazite is a common accessory mineral that occurs in medium to high grade metamorphic and Ca-poor felsic igneous rocks, and often controls the LREE budget (including Sm and Nd) of the host rock in which it crystallizes. Moreover, it contains appreciable U and Th, making it an ideal mineral for determining U-Th-Pb ages and Sm-Nd isotopic compositions, both of which are readily determined using in situ techniques with very high spatial resolution like LA-MC-ICPMS. Here, we present the results of laser ablation split stream analyses (LASS), which allows for simultaneous determination of the age and initial Nd isotopic composition in a single analysis. Analyses were done using a 20mm laser spot that allowed for detailed Nd isotope mapping of monazite grains (~30 analyses per ~250mm sized grain). Combined with LREE ratios (e.g., Sm/Nd, Ce/Gd, and Eu anomalies) these results yield important petrogenetic constraints on the evolution of peraluminous granites from the Old Woman-Piute batholith in southeastern California. Our findings also allow an improved understanding of the causes of isotope heterogeneity in granitic rocks. U-Th-Pb age mapping across the crystals reveals a single Cretaceous age for all grains with precision and accuracy typical of laser ablation analyses (~2%). In contrast, the concurrent Nd isotope mapping yields homogeneous initial Nd isotope compositions for some grains and large initial intra-grain variations of up to 8 epsilon units in others. The grains that yield homogeneous Nd isotope compositions have REE ratios suggesting that they crystallized in a fractionally crystallizing magma. Conversely, other grains, which also record fractional crystallization of both feldspar and LREE rich minerals, demonstrate a change in the Nd isotope composition of the magma during crystallization of monazite. Comparison of inter- and intra-grain Nd isotope compositions reveals further details on the potential mechanisms responsible for isotope heterogeneity present in single rock samples. This method highlights the potential of single grain isotope mapping of LREE phases such as monazite, allanite, and titanite for understanding both igneous and metamorphic petrogenesis.

Geochemistry of sediments in the Northern and Central Adriatic Sea

NASA Astrophysics Data System (ADS)

De Lazzari, A.; Rampazzo, G.; Pavoni, B.

2004-03-01

Major, minor and trace elements, loss of ignition, specific surface area, quantities of calcite and dolomite, qualitative mineralogical composition, grain-size distribution and organic micropollutants (PAH, PCB, DDT) were determined on surficial marine sediments sampled during the 1990 ASCOP (Adriatic Scientific Cooperative Program) cruise. Mineralogical composition and carbonate content of the samples were found to be comparable with data previously reported in the literature, whereas geochemical composition and distribution of major, minor and trace elements for samples in international waters and in the central basin have never been reported before. The large amount of information contained in the variables of different origin has been processed by means of a comprehensive approach which establishes the relations among the components through the mathematical-statistical calculation of principal components (factors). These account for the major part of data variance loosing only marginal parts of information and are independent from the units of measure. The sample descriptors concerning natural components and contamination load are discussed by means of a statistical model based on an R-mode Factor analysis calculating four significant factors which explain 86.8% of the total variance, and represent important relationships between grain size, mineralogy, geochemistry and organic micropollutants. A description and an interpretation of factor composition is discussed on the basis of pollution inputs, basin geology and hydrodynamics. The areal distribution of the factors showed that it is the fine grain-size fraction, with oxides and hydroxides of colloidal origin, which are the main means of transport and thus the principal link between chemical, physical and granulometric elements in the Adriatic.

Effect of natural fibers on mechanical properties of green cement mortar

NASA Astrophysics Data System (ADS)

AL-Zubaidi, Aseel B.

2018-05-01

Natural fibers of banana, reed, palm and coconut were used to reinforce cement composite. Optical microscopy showed that the prepared fibers are different in size and morphology. Nearly equiaxed, ribbon-like and nearly cylindrical morphologies were observed. Each of the utilized natural fibers was incorporated in the cement matrix at 0, 0.25, 0.5, 0.75 and 1.0 wt% and cured for 28 days. The scanning electron micrographs for the 1.0 wt% -reinforced composite showed differences in porosity, grain size and shape. Each of the utilized fibers has different effect on the microstructure of the cement composite that depends on the fiber size and morphology. Water absorption, thermal conductivity, bending strength, hardness and compression strengths were measured for the reinforced cement composite. It is found that the final physical and mechanical properties of the set cement composite depend on the fiber content and fiber type through the differences in their sizes and morphologies.

Microstructural Evolution of Al2O3-ZrO2 (Y2O3) Composites and its Correlation with Toughness

NASA Astrophysics Data System (ADS)

Kim, Hee Seung; Seo, Mi Young; Kim, Ik Jin

2008-02-01

The microstructure of zirconia (ZrO2) toughened alumina (Al2O3) ceramics was carefully controlled so as to obtain dense and fine-grained ceramics, thereby improving the properties and reliability of the ceramics for capillary applications in semiconductor bonding technology. Al2O3-ZrO2(Y2O3) composite was produced via Ceramic Injection Molding (CIM) technology, followed by Sinter-HIP process. Room temperature strength, hardness, Young's modulus, thermal expansion coefficient and toughness were determined, as well as surface strengthening induced by the fine grained homogenous microstructure and the thermal treatment. The changes in alumina/zirconia grain size, sintering condition and HIP treatment were found to be correlated.

Atomistic simulation of Al-graphene thin film growth on polycrystalline Al substrate

NASA Astrophysics Data System (ADS)

Zhang, Lan; Zhu, Yongchao; Li, Na; Rong, Yan; Xia, Huimin; Ma, Huizhong

2018-03-01

The growth of Al-Graphene composite coatings on polycrystalline Al substrate was investigated by using classical molecular dynamics (MD) simulations. Unlike the diffusion behaviors on single crystal surface, most of adatoms were easily bound by the steps on polycrystalline Al surface, owing to the local accelerated energy. Both Ehrlich-Schwoebel (ES) barriers and the steering effect backed up the volmer-weber growth mode, which was consistent with the dynamic growth process observed in the deposit. The morphology of composite coatings was significantly affected by graphene flakes. Enrichment of graphene flakes gave rise to an increase of the local thickness, and graphene flakes only existed in Al grain boundaries. The size of Al grains in the composite coating visibly decreased when compared with that in the pure Al coating. This grain refinement and the mechanical property can be reinforced by the increase of graphene flakes.

Behavior of grain boundary chemistry and precipitates upon thermal treatment of controlled purity alloy 690

NASA Astrophysics Data System (ADS)

Angeliu, Thomas M.; Was, Gary S.

1990-08-01

Grain boundary composition and carbide composition and structure were characterized for various microstructures of controlled purity alloy 690. Heat treatments produced varying degrees of grain boundary chromium depletion and precipitate distributions which were characterized via scanning transmission electron microscopy (STEM). Convergent beam electron diffraction revealed that the dominant carbide is M23C6, and energy dispersive X-ray analysis (EDAX) determined that the metallic content was about 90 at. pct chromium. A discontinuous precipitation reaction was observed and is attributed to a high degree of carbon supersaturation. Grain boundary composition measurements confirm that chromium depletion is controlled by volume diffusion of chromium to chromium-rich grain boundary carbides in the temperature range of 873 to 1073 K. Grain boundary chromium levels as low as 18.8 at. pct were obtained by thermal treatment at 873 K for 250 hours and 973 K for 1 hour. A thermodynamic and kinetic model developed for alloy 600 was modified to describe the development of the chromium depletion profile in alloy 690 during thermal treatment. Experimentally measured chromium profiles agree well with the model results for the dependence of the chromium depletion zone width and depth on various input parameters. The establishment of the model for alloy 690 allows the chromium depletion zone width and depth to be computed as a function of alloy composition, grain size, and temperature. The chromium depletion profiles and the precipitate structure and composition of controlled purity 690 are compared to those of controlled purity 600. A thermodynamic analysis of the carbide stability indicates that other factors, such as favorable orientation relationships, play an important role in controlling the precipitation of Cr23C6 in nickel-base alloys.

Study of the Effects of the Electric Field on Charging Measurements on Individual Micron-size Dust Grains by Secondary Electron Emissions

NASA Technical Reports Server (NTRS)

Tankosic, D.; Abbas, M. M.

2013-01-01

The dust charging by electron impact is an important dust charging process in Astrophysical, Planetary, and the Lunar environments. Low energy electrons are reflected or stick to the grains charging the dust grains negatively. At sufficiently high energies electrons penetrate the grain leading to excitation and emission of electrons referred to as secondary electron emission (SEE). Available theoretical models for the calculation of SEE yield applicable for neutral, planar or bulk surfaces are generally based on Sternglass Equation. However, viable models for charging of individual dust grains do not exist at the present time. Therefore, the SEE yields have to be obtained by some experimental methods at the present time. We have conducted experimental studies on charging of individual micron size dust grains in simulated space environments using an electrodynamic balance (EDB) facility at NASA-MSFC. The results of our extensive laboratory study of charging of individual micron-size dust grains by low energy electron impact indicate that the SEE by electron impact is a very complex process expected to be substantially different from the bulk materials. It was found that the incident electrons may lead to positive or negative charging of dust grains depending upon the grain size, surface potential, electron energy, electron flux, grain composition, and configuration. In this paper we give a more elaborate discussion about the possible effects of the AC field in the EDB on dust charging measurements by comparing the secondary electron emission time-period (tau (sub em) (s/e)) with the time-period (tau (sub ac) (ms)) of the AC field cycle in the EDB that we have briefly addressed in our previous publication.

Beta-Tin Grain Formation in Aluminum-Modified Lead-Free Solder Alloys

NASA Astrophysics Data System (ADS)

Reeve, Kathlene N.; Handwerker, Carol A.

2018-01-01

The limited number of independent β-Sn grain orientations that typically form during solidification of Sn-based solders and the resulting large β-Sn grain size have major effects on overall solder performance and reliability. This study analyzes whether additions of Al to Sn-Cu and Sn-Cu-Ag alloys can be used to change the grain size, morphology, and twinning structures of atomized (as-solidified) and re-melted (reflowed) β-Sn dendrites as determined using scanning electron microscopy and electron backscatter diffraction for as-solidified and reflow cycled (20-250°C, 1-5 cycles) Sn-Cu-Al and Sn-Ag-Cu-Al drip atomized spheres (260 μm diameter). The resulting microstructures were compared to as-solidified and reflow cycled Sn-Ag-Cu spheres (450 μm diameter) as well as as-solidified Sn-Ag-Cu, Sn-Cu, and Sn-Ag microstructures from the literature. Previous literature observations reporting reductions in undercooling and β-Sn grain size with Al micro-alloying additions could not be correlated to the presence of the Cu9Al4 phase or Al solute. The as-solidified spheres displayed no change in β-Sn dendrite structure or grain size when compared to non-Al-modified alloys, and the reflow cycled spheres produced high undercoolings (22-64°C), indicating a lack of potent nucleation sites. The current findings highlighted the role of Ag in the formation of the interlaced twinning structure and demonstrated that with deliberate compositional choices, formation of the alloy's β-Sn grain structure (cyclical twinning versus interlaced twinning) could be influenced, in both the as-solidified and reflow cycled states, though still not producing the fine-grain sizes and multiple orientations desired for improved thermomechanical properties.

The retention of dust in protoplanetary disks: Evidence from agglomeratic olivine chondrules from the outer Solar System

NASA Astrophysics Data System (ADS)

Schrader, Devin L.; Nagashima, Kazuhide; Waitukaitis, Scott R.; Davidson, Jemma; McCoy, Timothy J.; Connolly, Harold C.; Lauretta, Dante S.

2018-02-01

By investigating the in situ chemical and O-isotope compositions of olivine in lightly sintered dust agglomerates from the early Solar System, we constrain their origins and the retention of dust in the protoplanetary disk. The grain sizes of silicates in these agglomeratic olivine (AO) chondrules indicate that the grain sizes of chondrule precursors in the Renazzo-like carbonaceous (CR) chondrites ranged from <1 to 80 μm. We infer this grain size range to be equivalent to the size range for dust in the early Solar System. AO chondrules may contain, but are not solely composed of, recycled fragments of earlier formed chondrules. They also contain 16O-rich olivine related to amoeboid olivine aggregates and represent the best record of chondrule-precursor materials. AO chondrules contain one or more large grains, sometimes similar to FeO-poor (type I) and/or FeO-rich (type II) chondrules, while others contain a type II chondrule core. These morphologies are consistent with particle agglomeration by electrostatic charging of grains during collision, a process that may explain solid agglomeration in the protoplanetary disk in the micrometer size regime. The petrographic, isotopic, and chemical compositions of AO chondrules are consistent with chondrule formation by large-scale shocks, bow shocks, and current sheets. The petrographic, isotopic, and chemical similarities between AO chondrules in CR chondrites and chondrule-like objects from comet 81P/Wild 2 indicate that comets contain AO chondrules. We infer that these AO chondrules likely formed in the inner Solar System and migrated to the comet forming region at least 3 Ma after the formation of the first Solar System solids. Observations made in this study imply that the protoplanetary disk retained a dusty disk at least ∼3.7 Ma after the formation of the first Solar System solids, longer than half of the dusty accretion disks observed around other stars.

Effect of grain growth of [beta]-silicon nitride on strength, Weibull modulus, and fracture toughness

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hirosaki, Naota; Akimune, Yoshio; Mitomo, Mamoru

1993-07-01

[beta]-Si[sub 3]N[sub 4] powder containing 1 mol% of equimolar Y[sub 2]O[sub 3]-Nd[sub 2]O[sub 3] was gas-pressure sintered at 2,000C for 2 h (SN2), 4 h (SN4), and 8 h (SN8) in 30-MPa nitrogen gas. These materials had a microstructure of in-situ composites'' as a result of exaggerated grain growth of some [beta]-Si[sub 3]N[sub 4] grains during firing. Growth of elongated grains was controlled by the sintering time, so that the desired microstructures were obtained. SN2 had a Weibull modulus as high as 53 because of the uniform size and spatial distribution of its large grains. SN4 had a fracture toughnessmore » of 10.3 MPa[center dot]m[sup 1/2] because of toughening provided by the bridging of elongated grains, whereas SN8 showed a lower fracture toughness, possibly caused by extensive microcracking resulting from excessively large grains. Gas-pressure sintering of [beta]-Si[sub 3]N[sub 4] powder was shown to be effective in fostering selective grain growth for obtaining the desired composite microstructure.« less

Standardizing texture and facies codes for a process-based classification of clastic sediment and rock

USGS Publications Warehouse

Farrell, K.M.; Harris, W.B.; Mallinson, D.J.; Culver, S.J.; Riggs, S.R.; Pierson, J.; ,; Lautier, J.C.

2012-01-01

Proposed here is a universally applicable, texturally based classification of clastic sediment that is independent from composition, cementation, and geologic environment, is closely allied to process sedimentology, and applies to all compartments in the source-to-sink system. The classification is contingent on defining the term "clastic" so that it is independent from composition or origin and includes any particles or grains that are subject to erosion, transportation, and deposition. Modifications to Folk's (1980) texturally based classification that include applying new assumptions and defining a broader array of textural fields are proposed to accommodate this. The revised ternary diagrams include additional textural fields that better define poorly sorted and coarse-grained deposits, so that all end members (gravel, sand, and mud size fractions) are included in textural codes. Revised textural fields, or classes, are based on a strict adherence to volumetric estimates of percentages of gravel, sand, and mud size grain populations, which by definition must sum to 100%. The new classification ensures that descriptors are applied consistently to all end members in the ternary diagram (gravel, sand, and mud) according to several rules, and that none of the end members are ignored. These modifications provide bases for standardizing vertical displays of texture in graphic logs, lithofacies codes, and their derivatives- hydrofacies. Hydrofacies codes are nondirectional permeability indicators that predict aquifer or reservoir potential. Folk's (1980) ternary diagram for fine-grained clastic sediments (sand, silt, and clay size fractions) is also revised to preserve consistency with the revised diagram for gravel, sand, and mud. Standardizing texture ensures that the principles of process sedimentology are consistently applied to compositionally variable rock sequences, such as mixed carbonate-siliciclastic ramp settings, and the extreme ends of depositional systems.

Structure and magnetic properties of Ni-poly(p-xylylene) nanocomposites synthesized by vapor deposition polymerization

NASA Astrophysics Data System (ADS)

Ozerin, Sergei A.; Vdovichenko, Artem Yu.; Streltsov, Dmitry R.; Davydov, Alexander B.; Orekhov, Anton S.; Vasiliev, Alexander L.; Zubavichus, Yan V.; Grigoriev, Evgenii I.; Zavyalov, Sergei A.; Oveshnikov, Leonid N.; Aronzon, Boris A.; Chvalun, Sergei N.

2017-12-01

The relationship between structure, electrical and magnetic properties of thin poly(p-xylylene) - nickel nanocomposite films with Ni concentrations from 5 to 30 vol% was studied. It was found that metal concentration strongly affects size and oxidation state of the nanoparticles and composites morphology. At nickel concentration below 5 vol% the nanoparticles are oxidized to NiO and homogeneously distributed within fine-grained polymer matrix. An increase of Ni concentration up to 10 vol% results in the development of coarse-grained morphology with preferable localization of the nanoparticles at the boundaries of polymeric grains. And finally, in the composite films with nickel concentration above 20 vol%, the fine-grained morphology is observed again, but the nanoparticles are mainly metallic. Effect of the filler content on electrical and magnetic properties of the nanocomposites was elucidated showing that they are determined by percolation phenomenon with the threshold value of about 10 vol%. The well-pronounced magnetic hysteresis as well as ferromagnetic ordering were observed at Ni content above the percolation threshold. The diagrams of magnetic properties of these composites as a function of composition and temperature were elaborated. It was demonstrated that film annealing can be used to control magnetic properties of the composites and strongly enhance magnetoresistance.

Grain Surface Chemistry and the Composition of Interstellar Ices

NASA Technical Reports Server (NTRS)

Tielens, A. G. G. M.

2006-01-01

Submicron sized dust grains are an important component of the interstellar medium. In particular they provide surface where active chemistry can take place. At the low temperatures (-10 K) of the interstellar medium, colliding gas phase species will stick, diffuse, react, and form an icy mantle on these dust grains. This talk will review the principles of grain surface chemistry and delineate important grain surface routes, focusing on reactions involving H, D, and O among each other and with molecules such as CO. Interstellar ice mantles can be studied through the fundamental vibrations of molecular species in the mid-infrared spectra of sources embedded in or located behind dense molecular clouds. Analysis of this type of data has provided a complex view of the composition of these ices and the processes involved. Specifically, besides grain surface chemistry, the composition of interstellar ices is also affected by thermal processing due to nearby newly formed stars. This leads to segregation between different ice components as well as outgassing. The latter results in the formation of a so-called Hot Core region with a gas phase composition dominated by evaporated mantle species. Studies of such regions provide thus a different view on the ice composition and the chemical processes involved. Interstellar ices can also be processed by FUV photons and high energy cosmic ray ions. Cosmic ray processing likely dominates the return of accreted species to the gas phase where further gas phase reactions can take place. These different chemical routes towards molecular complexity in molecular clouds and particularly regions of star formation will be discussed.

Distribution and grain-size partitioning of metals in bovfom sediments of an experimentally acidified Wisconsin lake

USGS Publications Warehouse

Elder, John F.

2007-01-01

A study of concentrations and distribution of major and trace elements in surficial bottom sediments of Little Rock Lake in northern Wisconsin included examination of spatial variation and grain-size effects. No significant differences with respect to metal distribution in sediments were observed between the two basins of the lake, despite the experimental acidification of one of the basins from pH 6.1 to 4.6. The concentrations of most elements in the lake sediments were generally similar to soil concentrations in the area and were well below sediment quality criteria. Two exceptions were lead and zinc, whose concentrations in July 1990 exceeded the criteria of 50 μg/g and 100 μg/g, respectively, in both littoral and pelagic sediments. Concentrations of some elements, particularly Cu, Pb, and Zn, increased along transects from nearshore to midlake, following a similar gradient of sedimentary organic carbon. In contrast, Mn, Fe, and alkali/alkaline-earth elements were at maximum concentrations in nearshore sediments. These elements are less likely to partition to organic particles, and their distribution is more dependent on mineralogical composition, grain size, and other factors. Element concentrations varied among different sediment grain-size fractions, although a simple inverse relation to grain size was not observed. Fe, Mn, Pb, and Zn were more concentrated in a grain-size range 20–60 tm than in either the very fine or the coarse fractions, possibly because of the aggregation of smaller particles cemented together by organic and Fe/Mn hydrous-oxide coatings.

Compositional changes of minerals associated with dynamic recrystallizatin

NASA Astrophysics Data System (ADS)

Yund, Richard A.; Tullis, Jan

1991-09-01

The rate of compositional and isotopic exchange between minerals may be enhanced significantly if the rock is deformed simultaneously. The enhanced exchange rate may result from a reduction in grain size (shorter distance for volume diffusion), dissolution and growth of grains by diffusion creep (pressure solution), or the movement of high-angle grain boundaries through strained grains during recrystallization in the dislocation creep regime. The migration of high-angle grain boundaries provides high diffusivity paths for the rapid exchange of components during recrystallization. The operation of the latter process has been demonstrated by deforming aggregates consisting of two plagioclases (An1 and An79) at 900°C, 1 GPa confining pressure, and a strain rate of ˜2x10-6s-1. The polygonal, recrystallized grains were analyzed using an analytical transmission electron microscope and have a variable but often intermediate composition. At the conditions of these experiments, the volume interdiffusion rate of NaSi/CaAl is too slow to produce any observable chemical change, and microstructural-chemical relations indicate that the contribution from diffusion creep was insignificant except for initially fine-grained (2 10 μm) aggregates. These results indicate that strain-induced recrystallization can be an effective mechanism for enhancing the kinetics of metamorphic reactions and for resetting the isotope systematics of minerals such as feldspars, pyroxenes, and amphiboles.

Supernova Dust at Sub-micrometer Scales

NASA Astrophysics Data System (ADS)

Nittler, Larry; Stroud, R. M.

2006-06-01

Meteorites contain nanometer to micrometer stardust grains, which formed in pre-solar generations of stars and exhibit large isotopic anomalies that reflect the nuclear processes that occurred in their individual parent stars [1]. Supernovae of Type II have been identified as the sources of much of the stardust, including grains of SiC, Si3N4, graphite and Mg2SiO4. Although, the isotopic compositions of many elements in these grains point unambiguously to supernova nucleosynthesis processes [2], the data require extensive and heterogeneous mixing of disparate nuclear burning zones. A recent study found that individual 200 nm TiC sub-grains within a 12 micron supernova graphite grain have uniform Ti isotopic composition but a range of O isotopic ratios [3]. New microanalysis techniques allow us to correlate the physical microstructures of supernova grains with isotopic composition, e.g., SiC and Si3N4, providing a sub-micron view of condensation processes in supernova ejecta. Results on two SiC grains indicate that micron-sized SiC grains from supernovae consist of assemblages of smaller crystallites with some evidence of radiation and/or shock processing. This is in strong contrast to SiC grains from AGB stars, which are typically single euhedral crystals [4]. The Si, C and N isotopic compositions of the grains are highly uniform, in contrast to the model of [5], which predicts strong isotopic gradients in supernova-derived SiC grains.This work is supported by NASA.[1] Clayton D. D. and Nittler L. R. (2004) ARAA, 42, 39-78.[2] Nittler L. R., et al. (1996) ApJ, 462, L31-34.[3] Stadermann F. J., et al. (2005) GCA, 69, 177-188.[4] Daulton T. L., et al. (2002) Science, 296, 1852-1855.[5] Deneault E. A.-N., et al. (2003) ApJ, 594, 312-325.

C/O atomic ratios in micrometer-size crushed grains from Antarctic micrometeorites and two carbonaceous meteorites

NASA Technical Reports Server (NTRS)

Perreau, M.; Engrand, C.; Maurette, Michel; Kurat, G.; Presper, TH.

1993-01-01

Antarctic micrometeorites (AMM's) have similarities (but also differences) with primitive meteorites, such as unequilibrated mineral assemblages. To further assess such similarities, we have measured the carbon content of micrometeorites and meteorites (Orgueil and Murchison), as determined in a random selection of micrometer-size crushed grain, with an analytical transmission electron microscope. Such analyses yield the C/O atomic ratio, the major and minor elements contents, and the textural features of the grains on a scale of approx. equal to 100 nanometers. An important proportion of micrometeorites from both the 100-400 micron and the 50-100 micron size fractions contains much more carbon than CI chondrite Orgueil. The average C-content of all micrometeorites in these two size fractions amount to approximately 1.8 x CI, and approximately 0.8 x CI, respectively (CI refers to the bulk C-content of Orgueil, of about 3.5 percent by weight). Carbon is usually not homogeneously distributed in the micrometeorite but is concentrated in C-rich grains. So far, most of these grains are amorphous, and seem to be associated with an oxidized Fe-rich phase (possibly a variety of 'dirty' magnetite). About 5 percent of them have the composition of 'COPS', a phase additionally enriched in O, P, and S.

Nanocrystalline Al7075 + 1 wt % Zr Alloy Prepared Using Mechanical Milling and Spark Plasma Sintering

PubMed Central

Málek, Přemysl; Minárik, Peter; Chráska, Tomáš; Novák, Pavel; Průša, Filip

2017-01-01

The microstructure, phase composition, and microhardness of both gas-atomized and mechanically milled powders of the Al7075 + 1 wt % Zr alloy were investigated. The gas-atomized powder exhibited a cellular microstructure (grain size of a few µm) with layers of intermetallic phases along the cell boundaries. Mechanical milling (400 revolutions per minute (RPM)/8 h) resulted in a grain size reduction to the nanocrystalline range (20 to 100 nm) along with the dissolution of the intermetallic phases. Milling led to an increase in the powder’s microhardness from 97 to 343 HV. Compacts prepared by spark plasma sintering (SPS) exhibited negligible porosity. The grain size of the originally gas-atomized material was retained, but the continuous layers of intermetallic phases were replaced by individual particles. Recrystallization led to a grain size increase to 365 nm in the SPS compact prepared from the originally milled powder. Small precipitates of the Al3Zr phase were observed in the SPS compacts, and they are believed to be responsible for the retainment of the sub-microcrystalline microstructure during SPS. A more intensive precipitation in this SPS compact can be attributed to a faster diffusion due to a high density of dislocations and grain boundaries in the milled powder. PMID:28930192

A new method to generate dust with astrophysical properties

NASA Astrophysics Data System (ADS)

Hansen, J. F.; van Breugel, W.; Bringa, E. M.; Eberly, B.; Graham, G. A.; Remington, B. A.; Taylor, E. A.; Tielens, A. G. G. M.

2011-05-01

To model the size distribution and composition of interstellar and interplanetary dust grains, and their effect on a wide range of phenomena, it is vital to understand the mechanism of dust-shock interaction. We demonstrate a new laser experiment that subjects dust grains to pressure spikes similar to those of colliding astrophysical dust, and that accelerates the grains to astrophysical velocities. This new method generates much larger data sets than earlier methods; we show how large quantities (thousands) of grains are accelerated at once, rather than accelerating individual grains, as is the case of earlier methods using electric fields. We also measure the in-flight velocity ( ~ 4.5km/s) of hundreds of grains simultaneously by use of a particle image velocimetry (PIV) technique.

Tensile Properties and Fracture Characteristics of Nanostructured Copper and Cu-SiC Nanocomposite Produced by Mechanical Milling and Spark Plasma Sintering Process

NASA Astrophysics Data System (ADS)

Akbarpour, M. R.

2018-03-01

The presence of large grains within nanometric and ultrafine grain matrix is an effective method in order to enhance strength while keeping the high ductility of metals. For this purpose, in this research, spark plasma sintering (SPS) was used to consolidate milled Cu and Cu-SiC powders. In SPS process, local sparks with high temperature between particles take place and locally lead to intense grain growth, and therefore, this method has the ability to produce bimodal grain structures in copper and copper-based composites. Microstructural and mechanical studies showed ≈ 185 and ≈ 437 nm matrix grain sizes, high tensile yield strength values of ≈ 188.4 and ≈ 296.9 MPa, and fracture strain values of 15.1 and 6.7% for sintered Cu and Cu-4 vol.% SiC nanocomposite materials, respectively. The presence of nanoparticles promoted the occurrence of static recrystallization and decreased the fraction of coarse grains in microstructure. The high tensile properties of the produced materials are attributed to fine grain size, homogenous dispersion of nanoparticles and retarded grain boundary migration during sintering.

The Effect of Zeolite Composition and Grain Size on Gas Sensing Properties of SnO₂/Zeolite Sensor.

PubMed

Sun, Yanhui; Wang, Jing; Li, Xiaogan; Du, Haiying; Huang, Qingpan; Wang, Xiaofeng

2018-01-29

In order to improve the sensing properties of tin dioxide gas sensor, four kinds of different SiO₂/Al₂O₃ ratio, different particle size of MFI type zeolites (ZSM-5) were coated on the SnO₂ to prepared zeolite modified gas sensors, and the gas sensing properties were tested. The measurement results showed that the response values of ZSM-5 zeolite (SiO₂/Al₂O₃ = 70, grain size 300 nm) coated SnO₂ gas sensors to formaldehyde vapor were increased, and the response to acetone decreased compared with that of SnO₂ gas sensor, indicating an improved selectivity property. The other three ZSM-5 zeolites with SiO₂/Al₂O₃ 70, 150 and 470, respectively, and grain sizes all around 1 μm coated SnO₂ sensors did not show much difference with SnO₂ sensor for the response properties to both formaldehyde and acetone. The sensing mechanism of ZSM-5 modified sensors was briefly analyzed.

Response of 9Cr-ODS Steel to Proton Irradiation at 400 °C

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jianchao He; Farong Wan; Kumar Sridharan

2014-09-01

The stability of Y–Ti–O nanoclusters, dislocation structure, and grain boundary segregation in 9Cr-ODS steels has been investigated following proton irradiation at 400 °C with damage levels up to 3.7 dpa. A slight coarsening and a decrease in number density of nanoclusters were observed as a result of irradiation. The composition of nanoclusters was also observed to change with a slight increase of Y and Cr concentration in the nanoclusters following irradiation. Size, density, and composition of the nanoclusters were investigated as a function of nanocluster size, specifically classified to three groups. In addition to the changes in nanoclusters, dislocation loopsmore » were observed after irradiation. Finally, radiation-induced enrichment of Cr and depletion of W were observed at grain boundaries after irradiation.« less

Accurate Modeling of X-ray Extinction by Interstellar Grains

NASA Astrophysics Data System (ADS)

Hoffman, John; Draine, B. T.

2016-02-01

Interstellar abundance determinations from fits to X-ray absorption edges often rely on the incorrect assumption that scattering is insignificant and can be ignored. We show instead that scattering contributes significantly to the attenuation of X-rays for realistic dust grain size distributions and substantially modifies the spectrum near absorption edges of elements present in grains. The dust attenuation modules used in major X-ray spectral fitting programs do not take this into account. We show that the consequences of neglecting scattering on the determination of interstellar elemental abundances are modest; however, scattering (along with uncertainties in the grain size distribution) must be taken into account when near-edge extinction fine structure is used to infer dust mineralogy. We advertise the benefits and accuracy of anomalous diffraction theory for both X-ray halo analysis and near edge absorption studies. We present an open source Fortran suite, General Geometry Anomalous Diffraction Theory (GGADT), that calculates X-ray absorption, scattering, and differential scattering cross sections for grains of arbitrary geometry and composition.

High Temperature Deformation of Twin-Roll Cast Al-Mn-Based Alloys after Equal Channel Angular Pressing.

PubMed

Málek, Přemysl; Šlapáková Poková, Michaela; Cieslar, Miroslav

2015-11-12

Twin roll cast Al-Mn- and Al-Mn-Zr-based alloys were subjected to four passes of equal channel angular pressing. The resulting grain size of 400 nm contributes to a significant strengthening at room temperature. This microstructure is not fully stable at elevated temperatures and recrystallization and vast grain growth occur at temperatures between 350 and 450 °C. The onset of these microstructure changes depends on chemical and phase composition. Better stability is observed in the Al-Mn-Zr-based alloy. High temperature tensile tests reveal that equal channel angular pressing results in a softening of all studied materials at high temperatures. This can be explained by an active role of grain boundaries in the deformation process. The maximum values of ductility and strain rate sensitivity parameter m found in the Al-Mn-Zr-based alloy are below the bottom limit of superplasticity (155%, m = 0.25). However, some features typical for superplastic behavior were observed-the strain rate dependence of the parameter m , the strengthening with increasing grain size, and the fracture by diffuse necking. Grain boundary sliding is believed to contribute partially to the overall strain in specimens where the grain size remained in the microcrystalline range.

High Temperature Deformation of Twin-Roll Cast Al-Mn-Based Alloys after Equal Channel Angular Pressing

PubMed Central

Málek, Přemysl; Šlapáková Poková, Michaela; Cieslar, Miroslav

2015-01-01

Twin roll cast Al-Mn- and Al-Mn-Zr-based alloys were subjected to four passes of equal channel angular pressing. The resulting grain size of 400 nm contributes to a significant strengthening at room temperature. This microstructure is not fully stable at elevated temperatures and recrystallization and vast grain growth occur at temperatures between 350 and 450 °C. The onset of these microstructure changes depends on chemical and phase composition. Better stability is observed in the Al-Mn-Zr-based alloy. High temperature tensile tests reveal that equal channel angular pressing results in a softening of all studied materials at high temperatures. This can be explained by an active role of grain boundaries in the deformation process. The maximum values of ductility and strain rate sensitivity parameter m found in the Al-Mn-Zr-based alloy are below the bottom limit of superplasticity (155%, m = 0.25). However, some features typical for superplastic behavior were observed—the strain rate dependence of the parameter m, the strengthening with increasing grain size, and the fracture by diffuse necking. Grain boundary sliding is believed to contribute partially to the overall strain in specimens where the grain size remained in the microcrystalline range. PMID:28793667

Effect of sample inhomogeneity in KAr dating

USGS Publications Warehouse

Engels, J.C.; Ingamells, C.O.

1970-01-01

Error in K-Ar ages is often due more to deficiencies in the splitting process, whereby portions of the sample are taken for potassium and for argon determination, than to imprecision in the analytical methods. The effect of the grain size of a sample and of the composition of a contaminating mineral can be evaluated, and this provides a useful guide in attempts to minimize error. Rocks and minerals should be prepared for age determination with the effects of contaminants and grain size in mind. The magnitude of such effects can be much larger than intuitive estimates might indicate. ?? 1970.

Flow and fracture of ices, with application to icy satellites (Invited)

NASA Astrophysics Data System (ADS)

Durham, W. B.; Stern, L. A.; Pathare, A.; Golding, N.

2013-12-01

Exploration of the outer planets and their satellites by spacecraft over the past 4 decades has revealed that the prevailing low temperatures in the outer solar system have not produced "dead" cryoworlds of generic appearance. Rather, there is an extraordinary diversity in average densities, presence/absence and compositions of atmospheres and planetary rings, average albedos and their seasonal changes, near-surface compositions, and surface records of impact cratering and endogenic tectonic and igneous processes. One reason for this diversity is that the icy minerals present in abundance on many of these worlds are now or once were at significant fractions of their melting temperatures. Hence, a host of thermally activated processes related to endogenic activity (such as crystal defect migration, mass diffusion, surface transport, solid-solid changes of state, and partial melting) may occur that can enable inelastic flow on the surfaces and in the interiors of these bodies. Planetary manifestations include viscous crater relaxation in ice-rich terrain, cryovolcanism, the presence of a stable subsurface ocean, and the effects of solid-ice convection in deep interiors. We make the connection between theoretical mechanisms of deformation and planetary geology through laboratory experiment. Specifically, we develop quantitative constitutive flow laws (strain rate vs. stress) that describe the effects of relevant environmental variables (hydrostatic pressure, temperature, phase composition, chemical impurities). Our findings speak to topics including (1) the behavior of an outer ice I layer, its thickness, the depth to which a stagnant lid might extend, and possibility of wholesale overturn; (2) softening effects of dissolved species such as ammonia and perchlorate; (3) hardening effects of enclathration and of rock dust; and (4) effects of grain size on strength and factors affecting grain size. Other applications of lab data include dynamics of the deep interiors of large icy moons; flow of very low melting temperature, weakly bonded solids such as N2, CH4, and CO2; and the behavior of ice-rich, large exoplanets. We will review recent results on the rheological behavior of water ice I in the regime of combined flow by grain size sensitive and grain size insensitive mechanisms of deformation, and in particular the possibility that grain size is not a free variable when ice I deforms over large strains for long periods of time, but rather is defined by stress and temperature. Existing rheological laws suggest that viscosity of an ice-I-rich outer layer on a large icy moon, including a moon as small as Enceladus, may be strongly grain size dependent. We will also review developments in two-phase flow, with implications for geysers on Enceladus and methane in Titan's atmosphere.

Major and trace element chemistry of Luna 24 samples from Mare Crisium

NASA Technical Reports Server (NTRS)

Blanchard, D. P.; Brannon, J. C.; Aaboe, E.; Budahn, J. R.

1978-01-01

Atomic absorption spectrometry and instrumental neutron activation analysis were employed to analyze six Luna 24 soils for major and trace elements. The analysis revealed well-mixed soils, though size fractions of each of the soils showed quite dissimilar compositions. Thus the regolith apparently has not been extensively reworked. Noritic breccia admixed preferentially to the finest size fractions and differential comminution of one or more other soil components accounted for the observed elemental distributions as a function of grain size. The ferrobasalt composition and one or more components with higher MgO contents have been identified in the samples.

Effect of Cooling Rate on Microstructure of Two Kinds of High Nb Containing Tial Alloys

NASA Astrophysics Data System (ADS)

Chai, L. H.; Feng, Z. Y.; Xiang, Z. L.; Cui, Y. S.; Zhou, F.; Chen, Z. Y.

2017-09-01

In this paper, high Nb-TiAl alloys with Cr and W additions were prepared by Vacuum induction melting method, and then were heat treated under three different cooling rates of slow cooling, furnace cooling and air cooling. The phase composition of the alloy was analyzed by X ray diffraction, and the microstructure of the alloy was observed by optical microscope (OM), scanning electron microscope (SEM) and energy dispersive analyzer. The results show that the microstructure of Ti45Al8Nb0.2Cr and Ti45Al8Nb0.2W are fully lamellar structure with the main phase composition of α+γ after 3 different heat treatment conditions. The grain size of the two alloys decreases with decreasing of cooling rate, and the grain size of the alloyed with Cr alloy is smaller than that of the alloyed with W alloy. Most of the original massive β phase at grain boundaries and lamellar interfaces dissolved after heat treatment, and the transformation of β phase is easier for Ti45Al8Nb0.2Cr.

FIB-TEM Investigations of Fe-NI-Sulfides in the CI Chondrites Alais and Orgueil

NASA Technical Reports Server (NTRS)

Berger, Eve L.; Lauretta, D. S.; Zega, T. J.; Keller, L. P.

2013-01-01

The CI chondrites are primitive meteorites with bulk compositions matching the solar photosphere for all but the lightest elements. They have been extensively aqueously altered, and are composed primarily of fine-grained phyllosilicate matrix material which is host to carbonates, sulfates, sulfides, and minor amounts of olivine and pyroxene. The alteration, while extensive, is heterogeneous. For example, CI-chondrite cubanite and carbonate grains differ on mm to sub-mm scales, demonstrating multiple aqueous episodes. CI-chondrite variability is also evidenced by degree of brecciation, abundance and size of coarse-grained phyllosilicates, olivine and pyroxene abundance, as well as Ni-content and size of sulfide grains. Our previous work revealed Orgueil sulfide grains with variable Ni-contents, metal:S ratios, crystal structures and textures. We continue to explore the variability of CI-chondrite pyrrhotite (Po, (FeNi)1-xS) and pentlandite (Pn, (Fe,Ni)9S8) grains. We investigate the microstructure of sulfides within and among CI-chondrite meteorites in order to place constraints on the conditions under which they formed.

Influence of Hydrodynamic Sorting on the Composition and Age of Yellow River Suspended Particulate Organic Matter

NASA Astrophysics Data System (ADS)

Yu, M.; Eglinton, T. I.; Haghipour, N.; Montluçon, D. B.; Wacker, L.; Hou, P.; Zhao, M.

2016-12-01

The transport of organic carbon (OC) by rivers to coastal oceans is an important component of the global carbon cycle. The Yellow River (YR), the second largest river in China, transports large amounts of particulate organic carbon (POC) to the Chinese marginal seas, with fossil and pre-aged (ca, 1600 yr) OC comprising the dominant components. However, the influence of hydrodynamic processes on the origin, composition and age of POC exported by the YR remains poorly understood, yet these processes likely ultimately play an important role in determining OC fate in the Chinese marginal seas. We address this question through bulk, biomarker and carbon isotopic (δ13C and Δ14C) characterization of organic matter associated with different grain size fractions of total suspended particles (TSP) in the YR. Surface TSP samples were collected in the spring, summer, fall and during the Water-Sediment Regulation period (WSR, July) of 2015. TSP samples were separated into five grain-size fractions (<8μm, 8-16μm, 16-32μm, 32-63μm and >63μm) for organic geochemical and isotope analysis. Generally, the 16-32 and 32-63μm fractions contributed most of the TSP mass and the majority of OC resided in 16-32μm fraction. TOC% decreased with increasing grain size and 14C ages exhibited significant variability, ranging from 3,335 yr (<8μm fraction in summer) to 11,120 yr (>63μm fraction in autumn), but did not show any systematic trend among grain size fractions or across sampling times. In contrast, compound-specific 14C analysis of long-chain n-fatty acids (C26-30 FAs) revealed two clear patterns: first, C26-30 FAs age decreased with increasing grain size for all sampling times; second, the C26-30 FAs age difference was the largest among the different size fractions during the WSR period, and smallest after the WSR. These findings have important implications for our understanding of riverine POC transport mechanisms and their influence on the dispersal and burial efficiency of terrestrial OC in coastal oceans.

An attempt to reproduce high burn-up structure by ion irradiation of SIMFUEL

NASA Astrophysics Data System (ADS)

Baranov, V. G.; Lunev, A. V.; Reutov, V. F.; Tenishev, A. V.; Isaenkova, M. G.; Khlunov, A. V.

2014-09-01

Experiments in IC-100 and U-400 cyclotrons were conducted with SIMFUEL pellets (11.47 wt.% of fission products simulators) to reproduce some aspects of the long-term irradiation conditions in epithermal reactors. Pellets were irradiated with Xe16+, Xe24+ and He+ at energies ranging from 20 keV (He+) to 320 keV (Xe16+) and 1-90 MeV (Xe24+). Some samples were subsequently annealed to obtain larger grain sizes and to study defects recovery. The major microstructural changes consisted in grain sub-division observed on SEM and AFM images and change in composition registered by EPMA (pellets irradiated with 1-90 MeV Xe24+ ions at fluence of 5 × 1015 cm-2). Lattice distortion and increase in dislocation density is also noted according to X-ray data. At low energies and high fluences formation of bubbles (20 keV He+ at 5.5 × 1017 cm-2) was observed. Grain sub-division exhibits full coverage of the grain body and preservation of former grain boundaries. The size of sub-grains depends on local dislocation density and changes from 200 nm to 400 nm along the irradiated surface. Beneath it the size ranges from 150 to 600 nm. Sub-grains are not observed in samples irradiated by low-energy ions even at high dislocation densities.

Computational study of energy filtering effects in one-dimensional composite nano-structures

NASA Astrophysics Data System (ADS)

Kim, Raseong; Lundstrom, Mark S.

2012-01-01

Possibilities to improve the Seebeck coefficient S versus electrical conductance G trade-off of diffusive composite nano-structures are explored using an electro-thermal simulation framework based on the non-equilibrium Green's function method for quantum electron transport and the lattice heat diffusion equation. We examine the role of the grain size d, potential barrier height ΦB, grain doping, and the lattice thermal conductivity κL using a one-dimensional model structure. For a uniform κL, simulation results show that the power factor of a composite structure may be improved over bulk with the optimum ΦB being about kBT, where kB and T are the Boltzmann constant and the temperature, respectively. An optimum ΦB occurs because the current flow near the Fermi level is not obstructed too much while S still improves due to barriers. The optimum grain size dopt is significantly longer than the momentum relaxation length λp so that G is not seriously degraded due to the barriers, and dopt is comparable to or somewhat larger than the energy relaxation length λE so that the carrier energy is not fully relaxed within the grain and |S| remains high. Simulation results also show that if κL in the barrier region is smaller than in the grain, S and power factor are further improved. In such cases, the optimum ΦB and dopt increase, and the power factor may improve even for ΦB (d) significantly higher (longer) than kBT (λE). We find that the results from this quantum mechanical approach are readily understood using a simple, semi-classical model.

Magnetic fingerprint of the sediment load in a meander bend section of the Seine River (France)

NASA Astrophysics Data System (ADS)

Kayvantash, D.; Cojan, I.; Kissel, C.; Franke, C.

2017-06-01

This study aims to evaluate the potential of magnetic methods to determine the composition of the sediment load in a cross section of an unmanaged meander in the upstream stretch of the Seine River (Marnay-sur-Seine). Suspended particulate matter (SPM) was collected based on a regular sampling scheme along a cross section of the river, at two different depth levels: during a low-water stage (May 2014) and a high-water stage (February 2015). Riverbed sediments (RBS) were collected during the low-water stage and supplementary samples were taken from the outer and inner banks. Magnetic properties of the dry bulk SPM and sieved RBS and bank sediments were analysed. After characterizing the main magnetic carrier as magnetite, hysteresis parameters were measured, giving access to the grain size and the concentration of these magnetite particles. The results combined with sedimentary grain size data were compared to the three-dimensional velocity profile of the river flow. In the RBS where the magnetic grain size is rather uniform, the concentration of magnetite is inversely proportional to the mean grain size of the total sediment indicating that magnetite is strongly associated with the fine sedimentary fraction. The same pattern is observed in the samples from the outer and inner banks. During the low-water stage, the uniformly fine SPM grain size distribution characterizes the wash load. The magnetic fraction is also relatively fine (within the pseudo single domain range) with concentration similar to that of the fine RBS fraction. During the high-water stage, SPM samples correspond to mixtures of wash load and resuspended sediment from the bedload and riverbanks. Here, the grain size distribution is heterogeneous across the section showing coarser particles compared to those in the low-water stage and more varying magnetite concentrations while the magnetic grain size is like that of the low-water stage. The magnetite concentration in the high-water SPM can be modelled based on a mixing of the magnetite concentrations of the different grain size fractions, thus quantifying the impact of resuspension in the cross section.

Volatiles in interplanetary dust particles: A comparison with CI and CM chondrites

NASA Technical Reports Server (NTRS)

Bustin, Roberta

1992-01-01

In an effort to classify and determine the origin of interplanetary dust particles (IDPs), 14 of these particles were studied using a laser microprobe/mass spectrometer. The mass spectra for these particles varied dramatically. Some particles released hydroxide or water which probably originated in hydroxide-bearing minerals or hydrates. Others produced spectra which included a number of hydrocarbons and resembled meteorite spectra. However, none of the individual IDPs gave spectra which could be matched identically with a particular meteorite type such as a CI or CM carbonaceous chondrite. We believe this was due to the fact that 10-20 micron size IDPs are too small to be representative of the parent body. To verify that the diversity was due primarily to the small particle sizes, small grains of approximately the same size range as the IDPs were obtained from two primitive meteorites, Murchison and Orgueil, and these small meteorite particles were treated exactly like the IDPs. Considerable diversity was observed among individual grains, but a composite spectrum of all the grains from one meteorite closely resembled the spectrum obtained from a much larger sample of that meteorite. A composite spectrum of the 14 IDPs also resembled the spectra of the CM and CI meteorites, pointing to a possible link between IDPs and carbonaceous chondrites. This also illustrates that despite the inherent diversity in particles as small as 10-20 micron, conclusions can be drawn about the possible origin and overall composition of such particles by looking not only at results from individual particles but also by including many particles in a study and basing conclusions on some kind of composite data.

Novel superconducting phases of Tl-based compounds

NASA Technical Reports Server (NTRS)

Kostadinov, I. Z.; Mateev, M.; Michov, M.; Skumriev, V.; Tsakin, E.

1991-01-01

Researchers report the measurements of the I(sub c)(T) of the 102 K phase. They also discuss briefly the composition of the lattice parameters and the ac susceptibility relation to the grain size and microstructure.

Effect of aggregate graining compositions on skid resistance of Exposed Aggregate Concrete pavement

NASA Astrophysics Data System (ADS)

Wasilewska, Marta; Gardziejczyk, Wladysław; Gierasimiuk, Pawel

2018-05-01

The paper presents the evaluation of skid resistance of EAC (Exposed Aggregate Concrete) pavements which differ in aggregate graining compositions. The tests were carried out on concrete mixes with a maximum aggregate size of 8 mm. Three types of coarse aggregates were selected depending on their resistance to polishing which was determined on the basis of the PSV (Polished Stone Value). Basalt (PSV 48), gabbro (PSV 50) and trachybasalt (PSV 52) aggregates were chosen. For each type of aggregate three graining compositions were designed, which differed in the content of coarse aggregate > 4mm. Their content for each series was as follows: A - 38%, B - 50% and C - 68%. Evaluation of the skid resistance has been performed using the FAP (Friction After Polishing) test equipment also known as the Wehner/Schulze machine. Laboratory method enables to compare the skid resistance of different types of wearing course under specified conditions simulating polishing processes. In addition, macrotexture measurements were made on the surface of each specimen using the Elatexure laser profile. Analysis of variance showed that at significance level α = 0.05, aggregate graining compositions as well as the PSV have a significant influence on the obtained values of the friction coefficient μm of the tested EAC pavements. The highest values of the μm have been obtained for EAC with the lowest amount of coarse aggregates (compositions A). In these cases the resistance to polishing of the aggregate does not significantly affect the friction coefficients. This is related to the large areas of cement mortar between the exposed coarse grains. Based on the analysis of microscope images, it was observed that the coarse aggregates were not sufficiently exposed. It has been proved that PSV significantly affected the coefficient of friction in the case of compositions B and C. This is caused by large areas of exposed coarse aggregate. The best parameters were achieved for the EAC pavements with graining composition B and C and trachybasalt aggregate.

Mammalian Cell Interactions with Nanophase Materials

DTIC Science & Technology

2005-01-01

alumina , titania and hydroxylapatite) as well as on composites of these ceramics with either poly(L-lactic) acid or poly(methyl) methacrylate. Most...osteoblasts on flat, nanophase (versus microphase/conventional) ceramics ( alumina , titania and hydroxylapatite) as a function of decreasing ceramic grain size...acid (PLA) and nanophase (but not on polymer/conventional) ceramics ( alumina , titania and hydroxylapatite) composites [4]. Specifically, osteoblast

Microstructure Evolution and Composition Control during the Processing of Thin-gage Metallic Foil (Preprint)

DTIC Science & Technology

2012-02-01

the presence of somewhat randomly-distributed carbides and borides (white particles in BSE images), this grain size was comparable to that observed...pinned by carbide/ boride particles (imaging white in Figure 8c). The very fine gamma-prime precipitates likely produced during magnetron sputtering...sputtered material. First, the carbide/ boride particles were nucleated and hence located preferentially at the grain boundaries in the sputtered

Analysis of soft magnetic materials by electron backscatter diffraction as a powerful tool

NASA Astrophysics Data System (ADS)

Schuller, David; Hohs, Dominic; Loeffler, Ralf; Bernthaler, Timo; Goll, Dagmar; Schneider, Gerhard

2018-04-01

The current work demonstrates that electron backscatter diffraction (EBSD) is a powerful and versatile characterization technique for investigating soft magnetic materials. The properties of soft magnets, e.g., magnetic losses strongly depend on the materials chemical composition and microstructure, including grain size and shape, texture, degree of plastic deformation and elastic strain. In electrical sheet stacks for e-motor applications, the quality of the machined edges/surfaces of each individual sheet is of special interest. Using EBSD, the influence of the punching process on the microstructure at the cutting edge is quantitatively assessed by evaluating the crystallographic misorientation distribution of the deformed grains. Using an industrial punching process, the maximum affected deformation depth is determined to be 200 - 300 μm. In the case of laser cutting, the affected deformation depth is determined to be approximately zero. Reliability and detection limits of the developed EBSD approach are evaluated on non-affected sample regions and model samples containing different indentation test bodies. A second application case is the investigation of the recrystallization process during the annealing step of soft magnetic composites (SMC) toroids produced by powder metallurgy as a function of compaction pressure, annealing parameters and powder particle size. With increasing pressure and temperature, the recrystallized area fraction (e.g., grains with crystallographic misorientations < 3°) increases from 71 % (200 MPa, 800°C) to 90% (800 MPa, 800°C). Recrystallization of the compacted powder material starts at the particle boundaries or areas with existing plastic deformation. The progress of recrystallization is visualized as a function of time and of different particle to grain size distributions. Here, large particles with coarse internal grain structures show a favorable recrystallization behavior which results in large bulk permeability of up to 600 - 700 and lower amount of residual misorientations (>3°).

USE OF COMBUSTION SYNTHESIS IN PREPARING CERAMIC-MATRIX AND METAL-MATRIX COMPOSITE POWDERS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Weil, K. Scott; Hardy, John S.

A standard combustion-based approach typically used to synthesize nanosize oxide powders has been modified to prepare composite oxide-metal powders for subsequent densification via sintering or hot-pressing into ceramic- or metal-matrix composites. Copper and cerium nitrate salts were dissolved in the appropriate ratio in water and combined with glycine, then heated to cause autoignition. The ratio of glycine-to-total nitrate concentration was found to have the largest effect on the composition, agglomerate size, crystallite size, and dispersivity of phases in the powder product. After consolidation and sintering under reducing conditions, the resulting composite compact consists of a well-dispersed mixture of sub-micron sizemore » reinforcement particles in a fine-grained matrix.« less

Tensile and Compressive Responses of Ceramic and Metallic Nanoparticle Reinforced Mg Composites

PubMed Central

Tun, Khin Sandar; Wong, Wai Leong Eugene; Nguyen, Quy Bau; Gupta, Manoj

2013-01-01

In the present study, room temperature mechanical properties of pure magnesium, Mg/ZrO2 and Mg/(ZrO2 + Cu) composites with various compositions are investigated. Results revealed that the use of hybrid (ZrO2 + Cu) reinforcements in Mg led to enhanced mechanical properties when compared to that of single reinforcement (ZrO2). Marginal reduction in mechanical properties of Mg/ZrO2 composites were observed mainly due to clustering of ZrO2 particles in Mg matrix and lack of matrix grain refinement. Addition of hybrid reinforcements led to grain size reduction and uniform distribution of hybrid reinforcements, globally and locally, in the hybrid composites. Macro- and micro- hardness, tensile strengths and compressive strengths were all significantly increased in the hybrid composites. With respect to unreinforced magnesium, failure strain was almost unchanged under tensile loading while it was reduced under compressive loading for both Mg/ZrO2 and Mg/(ZrO2 + Cu) composites. PMID:28809245

Photoelectric Emission Measurements on the Analogs of Individual Cosmic Dust Grains

NASA Technical Reports Server (NTRS)

Abbas, M. M.; Tankosic, D.; Craven, P. D.; Spann, J. F.; LeClair, A.; West, E. A.; Weingartner, J. C.; Tielens, A. G. G. M.; Nuth, J. a.; Camata, R. P.

2006-01-01

The photoelectric emission process is considered to be the dominant mechanism for charging of cosmic dust grains in many astrophysical environments. The grain charge and equilibrium potentials play an important role in the dynamical and physical processes that include heating of the neutral gas in the interstellar medium, coagulation processes in the dust clouds, and levitation and dynamical processes in the interplanetary medium and planetary surfaces and rings. An accurate evaluation of photoelectric emission processes requires knowledge of the photoelectric yields of individual dust grains of astrophysical composition as opposed to the values obtained from measurements on flat surfaces of bulk materials, as it is generally assumed on theoretical considerations that the yields for the small grains are much different from the bulk values. We present laboratory measurements of the photoelectric yields of individual dust grains of silica, olivine, and graphite of approx. 0.09-5 micrometer radii levitated in an electrodynamic balance and illuminated with ultraviolet radiation at 120-160 nm wavelengths. The measured yields are found to be substantially higher than the bulk values given in the literature and indicate a size dependence with larger particles having order-of-magnitude higher values than for submicron-size grains.

Ion transport studies on Pb(NO3)2:Al2O3 composite solid electrolytes: Effect of dispersoid particle size

NASA Astrophysics Data System (ADS)

Reddy, Y. Govinda; Sekhar, M. Chandra; Sadananda Chary, A.; Narender Reddy, S.

2018-02-01

Composites of Alumina dispersed Lead Nitrate of different particles sizes (0.3µm, 36.9µm) were prepared through mechanical mixing process. These composites have been characterized by using XRD and SEM. Transport properties of these systems have been studied by means of impedance spectroscopy in the frequency range 100Hz to 4MHz in the temperature range from room temperature to 300°C. Temperature dependent conductivity spectra for composites with different mole percentages of alumina and with different particle sizes (0.3µm, 36.9µm) studied. The contact surface area between host and dispersoid increases with the decrease in particle size. These studies indicate that the conductivity in these systems is mainly due to the contribution enhanced concentration of mobile ions at the interfacial regions of host and dispersoid materials and increased mobility of charge carriers along the grain boundaries. It is believed that mechanism of conductivity through anti-Frenkel disorder (NO3 - ions) in these composites.

Microhardness and microstructure evolution of TiB2 reinforced Inconel 625/TiB2 composite produced by selective laser melting

NASA Astrophysics Data System (ADS)

Zhang, Baicheng; Bi, Guijun; Nai, Sharon; Sun, Chen-nan; Wei, Jun

2016-06-01

In this study, micron-size TiB2 particles were utilized to reinforce Inconel 625 produced by selective laser melting. Exceptional microhardness 600-700 HV0.3 of the composite was obtained. In further investigation, the microstructure and mechanical properties of Inconel 625/TiB2 composite can be significantly influenced by addition of TiB2 particles during SLM. It was found that the long directional columnar grains observed from SLM-processed Inconel 625 were totally changed to fine dendritic matrix due to the addition of TiB2 particles. Moreover, with laser energy density (LED) of 1200 J/m, a Ti, Mo rich interface around TiB2 particles with fine thickness can be observed by FESEM and EDS. The microstructure evolution can be determined by different laser energy density (LED): under 1200 J/m, γ phase in dendrite grains; under 600 J/m, γ phase in combination of dendritic and acicular grains; under 400 J/m, γ phase acicular grains. Under optimized LED 1200 J/m, the dynamic nanohardness (8.62 GPa) and elastic modulus (167 GPa) of SLM-processed Inconel 625/TiB2 composite are higher compared with those of SLM-processed Inconel 625 (3.97 GPa and 135 GPa, respectively).

Carbide/nitride grain refined rare earth-iron-boron permanent magnet and method of making

DOEpatents

McCallum, R.W.; Branagan, D.J.

1996-01-23

A method of making a permanent magnet is disclosed wherein (1) a melt is formed having a base alloy composition comprising RE, Fe and/or Co, and B (where RE is one or more rare earth elements) and (2) TR (where TR is a transition metal selected from at least one of Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, and Al) and at least one of C and N are provided in the base alloy composition melt in substantially stoichiometric amounts to form a thermodynamically stable compound (e.g. TR carbide, nitride or carbonitride). The melt is rapidly solidified in a manner to form particulates having a substantially amorphous (metallic glass) structure and a dispersion of primary TRC, TRN and/or TRC/N precipitates. The amorphous particulates are heated above the crystallization temperature of the base alloy composition to nucleate and grow a hard magnetic phase to an optimum grain size and to form secondary TRC, TRN and/or TRC/N precipitates dispersed at grain boundaries. The crystallized particulates are consolidated at an elevated temperature to form a shape. During elevated temperature consolidation, the primary and secondary precipitates act to pin the grain boundaries and minimize deleterious grain growth that is harmful to magnetic properties. 33 figs.

Carbide/nitride grain refined rare earth-iron-boron permanent magnet and method of making

DOEpatents

McCallum, R. William; Branagan, Daniel J.

1996-01-23

A method of making a permanent magnet wherein 1) a melt is formed having a base alloy composition comprising RE, Fe and/or Co, and B (where RE is one or more rare earth elements) and 2) TR (where TR is a transition metal selected from at least one of Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, and Al) and at least one of C and N are provided in the base alloy composition melt in substantially stoichiometric amounts to form a thermodynamically stable compound (e.g. TR carbide, nitride or carbonitride). The melt is rapidly solidified in a manner to form particulates having a substantially amorphous (metallic glass) structure and a dispersion of primary TRC, TRN and/or TRC/N precipitates. The amorphous particulates are heated above the crystallization temperature of the base alloy composition to nucleate and grow a hard magnetic phase to an optimum grain size and to form secondary TRC, TRN and/or TRC/N precipitates dispersed at grain boundaries. The crystallized particulates are consolidated at an elevated temperature to form a shape. During elevated temperature consolidation, the primary and secondary precipitates act to pin the grain boundaries and minimize deleterious grain growth that is harmful to magnetic properties.

The Influence of Grain Structure on Intermetallic Compound Layer Growth Rates in Fe-Al Dissimilar Welds

NASA Astrophysics Data System (ADS)

Xu, Lei; Robson, Joseph D.; Wang, Li; Prangnell, Philip B.

2018-02-01

The thickness of the intermetallic compound (IMC) layer that forms when aluminum is welded to steel is critical in determining the properties of the dissimilar joints. The IMC reaction layer typically consists of two phases ( η and θ) and many attempts have been made to determine the apparent activation energy for its growth, an essential parameter in developing any predictive model for layer thickness. However, even with alloys of similar composition, there is no agreement of the correct value of this activation energy. In the present work, the IMC layer growth has been characterized in detail for AA6111 aluminum to DC04 steel couples under isothermal annealing conditions. The samples were initially lightly ultrasonically welded to produce a metallic bond, and the structure and thickness of the layer were then characterized in detail, including tracking the evolution of composition and grain size in the IMC phases. A model developed previously for Al-Mg dissimilar welds was adapted to predict the coupled growth of the two phases in the layer, whilst accounting explicitly for grain boundary and lattice diffusion, and considering the influence of grain growth. It has been shown that the intermetallic layer has a submicron grain size, and grain boundary diffusion as well as grain growth plays a critical role in determining the thickening rate for both phases. The model was used to demonstrate how this explains the wide scatter in the apparent activation energies previously reported. From this, process maps were developed that show the relative importance of each diffusion path to layer growth as a function of temperature and time.

Soils from Mare Crisium - Agglutinitic glass chemistry and soil development

NASA Technical Reports Server (NTRS)

Hu, H.-N.; Taylor, L. A.

1978-01-01

Agglutinates were studied in 29 polished thin sections of grain mounts from various size fractions of six Luna 24 soil horizons. Three populations of agglutinitic glass compositions were found: a high-MgO, high-FeO group identified as a coarse-grained basaltic component; a low-MgO, low-FeO group from a highland source; and a low-MgO, high-FeO group probably from the subophitic basalt component. The presence of a significant amount of admixed highland component probably accounts for an enrichment in plagioclase and a depletion in ferromagnesian elements displayed by the agglutinitic glass compositions relative to the bulk soil.

Properties and rapid sintering of a nanostructured tetragonal zirconia composites

NASA Astrophysics Data System (ADS)

Shon, In-Jin; Yoon, Jin-Kook; Hong, Kyung-Tae

2017-09-01

4YSZ is generally used as oxygen sensors, fuel cells, thermal barrier and hip and knee joint replacements as a result of these excellent properties with its high biocompatibility, low density, good resistance against corrosion, high ionic conductivity, hard phase and melting point. However, 4YTZ with coarse grain has low resistance to wear and abrasion because of low hardness and low fracture toughness at room temperature. The fracture toughness and hardness of a 4YTZ can be improved by forming nanostructured composites and addition of a second hard phase. In this study, nanostuctured 4YTZ-graphene composites with nearly full density were achieved using high-frequency induction heated sintering for one min at a pressure of 80 MPa. The rapid consolidation and addition of graphene to 4YTZ retained the nano-scale structure of the ceramic by inhibiting grain growth. The grain size of 4YTZ was reduced remarkably by the addition of graphene and the addition of graphene to 4YTZ greatly improved the fracture toughness without decrease of hardness.

Doped zinc oxide microspheres

DOEpatents

Arnold, Jr., Wesley D.; Bond, Walter D.; Lauf, Robert J.

1993-01-01

A new composition and method of making same for a doped zinc oxide microsphere and articles made therefrom for use in an electrical surge arrestor which has increased solid content, uniform grain size and is in the form of a gel.

Preparation of TbCu7-type Sm-Fe powders by low-temperature HDDR treatment

NASA Astrophysics Data System (ADS)

Takagi, Kenta; Jinno, Miho; Ozaki, Kimihiro

2018-05-01

Low-temperature hydrogen-disproportionation-desorption-recombination (HDDR) treatment of Sm-Fe alloy powder was conducted to prepare a metastable TbCu7 type Sm-Fe alloy powder with a grain size of more than a few hundreds of nanometers. While a treatment temperature above 700 °C produced the familiar Th2Zn17 type alloy, one below 600 °C resulted in successful synthesis of the TbCu7 type Sm-Fe alloy with submicron-size grains. This TbCu7 type alloy powder, however, showed no significant improvement in magnetic properties compared to the Th2Zn17 type, as its composition was estimated to be near SmFe8.5 and thus did not achieve the expected Fe-rich composition. Therefore, cross-sectional transmission electron microscope observation of the unfinished TbCu7 type alloy powder was conducted in order to explore means of forming the Fe-rich phase.

Morphological and functional effects of graphene on the synthesis of uranium carbide for isotopes production targets.

PubMed

Biasetto, L; Corradetti, S; Carturan, S; Eloirdi, R; Amador-Celdran, P; Staicu, D; Blanco, O Dieste; Andrighetto, A

2018-05-29

The development of tailored targets for the production of radioactive isotopes represents an active field in nuclear research. Radioactive beams find applications in nuclear medicine, in astrophysics, matter physics and materials science. In this work, we study the use of graphene both as carbon source for UO 2 carbothermal reduction to produce UC x targets, and also as functional properties booster. At fixed composition, the UC x target grain size, porosity and thermal conductivity represent the three main points that affect the target production efficiency. UC x was synthesized using both graphite and graphene as the source of carbon and the target properties in terms of composition, grain size, porosity, thermal diffusivity and thermal conductivity were studied. The main output of this work is related to the remarkable enhancement achieved in thermal conductivity, which can profitably improve thermal dissipation during operational stages of UC x targets.

Influence of surface morphology and UFG on damping and mechanical properties of composite reinforced with spinel MgAl{sub 2}O{sub 4}-SiC core-shell microcomposites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Singh, Subhash; Pal, Kaushik, E-mail: pl_kshk@yaho

Interface between ceramic particulate and matrix is known to control the response of the materials and functionality of the composite. Among numerous physical properties, grain structure of the materials has also played a significant role in defining the behaviour of metal matrix composites. Usually, silicon carbide (SiC) particles show poor interfacial wettability in aluminium melt. Herein, we were successfully synthesized magnesium oxide (MgO) and nanocrystalline magnesium aluminate (MgAl{sub 2}O{sub 4}) spinel coated silicon carbide (SiC) core-shell micro-composites through sol-gel technique to improve the wettability of dispersoids. Core-shell structures of submicron size were thoroughly investigated by various characterization techniques. Further, aluminiummore » matrix composites incorporated with pristine SiC, MgO grafted SiC and MgAl{sub 2}O{sub 4} grafted SiC particles were fabricated by stir casting technique, respectively. Additionally, as-cast composites were processed via friction stir processing (FSP) technique to observe the influence of grain refinement on mechanical and damping properties. Electron back scattered diffraction (EBSD), Field emission scanning electron microscopy (FE-SEM) and X-ray energy dispersion spectroscopy (EDX) analysis were conducted for investigating grain size refinement, adequate dispersion, stability and de-agglomeration of encapsulated SiC particles in aluminium matrix. The mechanical as well as thermal cyclic (from − 100 to 400 °C) damping performance of the as-cast and friction stir processed composites were studied, respectively. Finally, the enhanced properties were attributable to reduced agglomeration, stabilization and proper dispersion of the tailored SiC particles Al matrix. - Highlights: •Synthesizing a novel coating layer of MgO and MgAl{sub 2}O{sub 4} spinel onto SiC particles •Significant improvement in UTS and hardness by reinforcing tailored SiC in Al •Significant grain refinements were obtained through FSP •SiC/MgAl{sub 2}O{sub 4}/Al exhibits ~ 61% higher storage modulus as compare to pure Al after FSP.« less

On Organic Material in E Ring Ice Grains

NASA Astrophysics Data System (ADS)

Postberg, F.; Khawaja, N.; Reviol, R.; Nölle, L.; Klenner, F.; Hsu, H. W.; Horanyi, M.

2015-12-01

Pure water ice dominates the composition of the micron and sub-micron sized dust particles in Saturn's E-ring, a ring constantly replenished by active ice jets of the moon Enceladus [1]. Details about the composition of this tenuous, optically thin ring can only be constrained by in situ measurements. The Cosmic Dust Analyzer (CDA) onboard Cassini investigates the composition of these grains by cationic time-of-flight mass spectra of individual ice grains hitting the instruments target surface. From these spectra three compositional types of E ring ice grains have been identified previously [2,3]: Type-1: Almost pure water, Type-2: Enriched in organics, and Type-3: Enriched in salt. Unlike Type-1 and 3, organic-enriched Type-2 spectra have not yet been investigated in depth. Here we report the first detailed compositional analysis of this type. The spectra analysis is supported by a large-scale laboratory ground campaign yielding a library of analogue spectra for organic material embedded in a water ice matrix. In contrast to Type 1 and 3, Type-2 spectra display a great compositional diversity, which indicates varying contributions of several organic species. So far we have identified characteristic fragment patterns of at least three classes of organic compounds: aromatic species, amines, and carbonyl group species. Work is in progress to quantify concentrations of the identified species and to assign yet un-specified organic mass lines in Type 2 spectra. Due to the dynamical evolution of the orbital elements of E ring grains a large fraction collides with the icy moons embedded in the E ring. Therefore, the organic components identified by CDA can accumulate on the surfaces of these bodies over time. Ref: :[1]Kempf et al., Icarus-206, 2010. [2]Postberg et al., Nature-459, 2009. [3]Postberg et al., Icarus-193, 2008.

Seeing the Soils of Meridiani Planum Through the Eyes of Pancam and Microscopic Imager

NASA Technical Reports Server (NTRS)

Weitz, C. M.; Anderson, R. C.; Bell, J. F., III; Cabrol, N. A.; Calvin, W. M.; Ehlmann, B. L.; Farrand, W. H.; Greeley, R.; Herkenhoff, K. E.; Johnson, J. R.

2005-01-01

We are using data from the Pancam and Microscopic Imager (MI) on the Opportunity rover to characterize the soil grains at Meridiani Planum. We have traced individual grains in all MI images of the soils using the software application ImageJ distributed by NIH, and subsequently derived size and shape properties about the grains. The resolution of the MI is 31 microns per pixel [1] so we limit our measurements to those grains larger than about 0.3 mm in size. In cases where the grain is partially or substantially buried by other grains or finer soil particles, we do not make a measurement. False-color composites from Pancam images that cover the same location imaged by MI are made from the Left 2,5,6 (753, 535, 482 nm) filters or Right 2,7,1 (753, 1009, 430 nm) filters [2] in the Red, Green, and Blue channels, respectively. These color images are then merged with the MI images to illustrate color properties of particular grains. Pancam spectra are also extracted from grains when there is sufficient spatial coverage. in diameter. Figure 2 illustrates the dominance of these small grains at this particular location, which happens to be on the southern wall of Eagle crater. The Pancam color merge with this MI image suggests that the small spherules are more consistent with the basalt grains than the blueberries (spherulitic concretions derived from outcrop rocks [7]). The resolution of Pancam images of this location is on the order of 0.5 mm so the grains are only barely resolved. A Mossbauer measurement taken on an adjacent soil (Sol 53 Vanilla) that is composed solely of these smaller spherules (Fig 1) is consistent with a basaltic composition for the grains. Their concentration at this particular location in a brighter, elongate patch along the southeastern wall compared to elsewhere inside Eagle crater suggests wind activity favored their transport and subsequent deposition here. Their spherical shape is also possibly the result of wind action rounding them during transport, though water action cannot be ruled out.

Apollo 17 Soil Characterization for Reflectance Spectroscopy

NASA Technical Reports Server (NTRS)

Taylor, L. A.; Pieters, C.; Patchen, A.; Morris, R. V.; Keller, L. P.; Wentworth, S.; McKay, D. S.

1999-01-01

It is the fine fractions that dominate the observed spectral signatures of bulk lunar soil, and the next to the smallest size fractions are the most similar to the overall properties of the bulk soil. Thus, our Lunar Soil Characterization Consortium has concentrated on understanding the inter-relations of compositional, mineralogical, and optical properties of the <45-micron size fraction and its component sizes (20-44 micron, 10-20 micron, and <10 micron size fractions). To be able to generalize our results beyond the particular sample set studied, it is necessary to quantitatively identify the observed effects of space weathering and evaluate the processes involved. For this, it is necessary to know the chemistry of each size fraction, modal abundances of each phase, average compositions of the minerals and glasses, I(sub s)/FeO values, reflectance spectra, and the physical makeup of the individual particles and their patinas. This characterization includes the important dissection of the pyroxene minerals into four separate populations, with data on both modes and average chemical compositions. Armed with such data, it should be possible to effectively isolate spectral effects of space weathering from spectral properties related to mineral and glass chemistry. Four mare soils from the Apollo 17 site were selected for characterization based upon similarities in bulk composition and their contrasting maturities, ranging from immature to submature to mature. The methodology of our characterization has been discussed previously. Results of the Apollo 17 mare soils, outlined herein, are being prepared for publication in MAPS. As shown, with decreasing grain size, the agglutinitic (impact) glass content profoundly increases. This is the most impressive change for the mare soils. In several soils we have examined, there is an over two-fold increase in the agglutinitic glass contents between the 90-150- micron and the 10-20-micron size fractions. Accompanying this increase in agglutinitic glass is a definite decrease in pyroxenes and to lesser extents, the oxides (ilmenite), volcanic glass, and olivine. Unexpectedly, however, the absolute plagioclase abundances stay relatively constant throughout the different grain sizes, although the abundance of plagioclase relative to the mafic minerals increases with decreasing particle size. These soils were chosen for study based upon their similarities in FeO and Ti02 content, allowing for direct comparisons between evolutions of chemistry between size fractions and among different maturities of soils. The bulk chemistry of these fractions was determined by EMP analyses of fused glass beads. In contrast to the systematic variations in bulk chemistry discussed below, the relatively uniform composition of agglutinitic glass with grain size and soil maturity is illustrated. The composition of the bulk fraction of each size fraction becomes more feldspathic with increasing maturity, with the effect being most pronounced for the finest fractions. The composition of the agglutinitic glass, however, is relatively invariant and more feldspathic (i.e., rich in Al2O3) than even the <10-micron fraction. This relation not only strengthens the "fusion of the finest fraction" (F(sup 3)) hypothesis, but also highlights the important role of plagioclase in the formation of agglutinitic glass. With decreasing grain size, FeO, MgO, and TiO2 contents decrease, whereas CaO, Na2O, and Al2O3 (plag components) increase for all soils. These chemical variations would appear to be coupled with the significant increase in agglutinitic glass and decrease in oxide (ilmenite),pyroxene, and volcanic glass. These changes in chemistry do not appear to be due to distinct changes in the compositions of individual phases but to their abundances. Values of I(sub s)/FeO increase with decreasing grain size, even though the bulk FeO contents decrease. That is, the percentage of the total Fe that is present as nanophase Fe(sup O) has increased substantially in the smaller size fraction. Note that the increase in nanophase FeO in smaller size fractions is significantly greater than the increase in agglutinitic glass content, with its single-domain FeO component. This would seem to indicate that at least some of the FeO is surface correlated. To illustrate this effect, if it is assumed that the nanophase FeO is entirely surface correlated, then equal masses of 15-micron and 6-micron spheres should have about 3x as much FeO in the finer fraction. The recent findings of Kelleret al. of the major role of vapor-deposited, nanophase FeO-containing patinas on most soil particles is a major breakthrough in our understanding of the distribution of FeO within agglutinitic glass and upon grain surfaces. Bidirectional reflectance spectra for a representative Apollo 17 soil (70181) are shown. The size separates all have similar albedo in the blue and follow a regular sequence in which the continuum slope increases, ferrous bands weaken, and albedo, increases with decreasing particle size. The bulk <45-micron soil is typically close to the 10-20 micron spectrum. It is important to note that although the finest fraction (<10 micron) is close in composition to the abundant agglutinitic glass in each size fraction, this size fraction is relatively featureless and does not dominate the spectrum of the bulk <45-micron soil. It has long been suspected that agglutinitic glass, to a large extent, is the product of melting of the finest fraction of the soils, with a dominance of plagioclase. Given the low abundance of pyroxene in the finest fractions of each soil the source of the FeO in these Apollo 17 agglutinitic glasses is not fully identified. We suspect the abundant volcanic glass in these samples may be a significant contributor and this hypothesis will be tested with the suite under study from other Apollo sites.

Phobos MRO/CRISM visible and near-infrared (0.5-2.5 μm) spectral modeling

NASA Astrophysics Data System (ADS)

Pajola, Maurizio; Roush, Ted; Dalle Ore, Cristina; Marzo, Giuseppe A.; Simioni, Emanuele

2018-05-01

This paper focuses on the spectral modeling of the surface of Phobos in the wavelength range between 0.5 and 2.5 μm. We exploit the Phobos Mars Reconnaissance Orbiter/Compact Reconnaissance Imaging Spectrometer for Mars (MRO/CRISM) dataset and extend the study area presented by Fraeman et al. (2012) including spectra from nearly the entire surface observed. Without a priori selection of surface locations we use the unsupervised K-means partitioning algorithm developed by Marzo et al. (2006) to investigate the spectral variability across Phobos surface. The statistical partitioning identifies seven clusters. We investigate the compositional information contained within the average spectra of four clusters using the radiative transfer model of Shkuratov et al. (1999). We use optical constants of Tagish Lake meteorite (TL), from Roush (2003), and pyroxene glass (PM80), from Jaeger et al. (1994) and Dorschner et al. (1995), as previously suggested by Pajola et al. (2013) as inputs for the calculations. The model results show good agreement in slope when compared to the averages of the CRISM spectral clusters. In particular, the best fitting model of the cluster with the steepest spectral slope yields relative abundances that are equal to those of Pajola et al. (2013), i.e. 20% PM80 and 80% TL, but grain sizes that are 12 μm smaller for PM80 and 4 μm smaller for TL (the grain sizes are 11 μm for PM80 and 20 μm for TL in Pajola et al. (2013), respectively). This modest discrepancy may arise from the fact that the areas observed by CRISM and those analyzed in Pajola et al. (2013) are on opposite locations on Phobos and are characterized by different morphological and weathering settings. Instead, as the clusters spectral slopes decrease, the best fits obtained show trends related to both relative abundance and grain size that is not observed for the cluster with the steepest spectral slope. With a decrease in slope there is general increase of relative percentage of PM80 from 12% to 18% and the associated decrease of TL from 88% to 82%. Simultaneously the PM80 grain sizes decrease from 9 to 5 μm and TL grain sizes increase from 13 to 16 μm. The best fitting models show relative abundances and grain sizes that partially overlap. This supports the hypothesis that from a compositional perspective the transition between the highest and lowest slopes on Phobos is subtle, and it is characterized by a smooth change of relative abundances and grain sizes, instead of a distinct dichotomy between the areas.

Manufacturing techniques for titanium aluminide based alloys and metal matrix composites

NASA Astrophysics Data System (ADS)

Kothari, Kunal B.

Dual phase titanium aluminides composed vastly of gamma phase (TiAl) with moderate amount of alpha2 phase (Ti3Al) have been considered for several high temperature aerospace and automobile applications. High specific strength coupled with good high temperature performance in the areas of creep and oxidation resistance makes titanium aluminides "materials of choice" for next generation propulsion systems. Titanium alumnides are primarily being considered as potential replacements for Ni-based superalloys in gas turbine engine components with aim of developing more efficient and leaner engines exhibiting high thrust-to-weight ratio. Thermo-mechanical treatments have shown to enhance the mechanical performance of titanium aluminides. Additionally, small additions of interstitial elements have shown further and significant improvement in the mechanical performance of titanium alumnide alloys. However, titanium aluminides lack considerably in room temperature ductility and as a result manufacturing processes of these aluminides have greatly suffered. Traditional ingot metallurgy and investment casting based methods to produce titanium aluminide parts in addition to being expensive, have also been unsuccessful in producing titanium aluminides with the desired mechanical properties. Hence, the manufacturing costs associated with these methods have completely outweighed the benefits offered by titanium aluminides. Over the last two decades, several powder metallurgy based manufacturing techniques have been studied to produce titanium aluminide parts. These techniques have been successful in producing titanium aluminide parts with a homogeneous and refined microstructure. These powder metallurgy techniques also hold the potential of significant cost reduction depending on the wide market acceptance of titanium aluminides. In the present study, a powder metallurgy based rapid consolidation technique has been used to produce near-net shape parts of titanium aluminides. Micron-sized titanium aluminide powders were rapidly consolidated to form near-net shape titanium aluminide parts in form of small discs and tiles. The rapidly consolidated titanium aluminide parts were found to be fully dense. The microstructure morphology was found to vary with consolidation conditions. The mechanical properties were found to be significantly dependent on microstructure morphology and grain size. Due to rapid consolidation, grain growth during consolidation was limited, which in turn led to enhanced mechanical properties. The high temperature mechanical properties for the consolidated titanium aluminide samples were characterized and were found to retain good mechanical performance up to 700°C. Micron-sized titanium aluminide powders with slightly less Aluminum and small Nb, and Cr additions were rapidly consolidated into near-net shape parts. The consolidated parts were found to exhibit enhanced mechanical performance in terms of ductility and yield strength. The negative effect of Oxygen on the flexural strength at high temperatures was found to be reduced with the addition of Nb. In an effort to further reduce the grain size of the consolidated titanium aluminide samples, the as-received titanium aluminide powders were milled in an attrition mill. The average powder particle size of the powders was reduced by 60% after milling. The milled powders were then rapidly consolidated. The grain size of the consolidated parts was found to be in the sub-micrometer range. The mechanical properties were found to be significantly enhanced due to reduction of grain size in the sub-micrometer range. In order to develop a metal matrix composite based on titanium aluminide matrix reinforced with titanium boride, an experiment to study the effect of rapid consolidation on titanium diboride powders was conducted. Micron-sized titanium diboride powders were consolidated and were found to be 93% dense and exhibited minimal grain growth. The low density of the consolidated part was attributed to low consolidation temperature. Titanium aluminide and titanium diboride powders were blended together in an attrition mill and rapidly consolidated. A metal matrix composite with titanium aluminide matrix reinforced with titanium monoboride plates was formed. The titanium diboride in the powder form was found to be transformed to titanium monoboroide plates during consolidation due to the thermodynamic equilibrium between titanium and titanium monoboride. The metal matrix composite was found to be 90% dense. The low density was due to particle size mismatch between the matrix and reinforcement powders and low consolidation temperature. An increase in the volume of titanium monoboride plates in the metal matrix composite was accompanied by an increase in the elastic modulus of the metal matrix composite.

High temperature compounds for turbine vanes. [of SiC, Si3N4, and Si composites

NASA Technical Reports Server (NTRS)

Rhodes, W. H.; Cannon, R. M., Jr.

1974-01-01

Fabrication and microstructure control studies were conducted on SiC, Si3N and composites based on Si3N. Charpy mode impact testing to 2400 F established that Si3N4/Mo composites have excellent potential. Attempts to fabricate composites of Si3N4 with superalloys, both by hot pressing and infiltration were largely unsuccessful in comparison to using Mo, Re, and Ta which are less reactive. Modest improvements in impact strength were realized for monolithic Si3N4; however, SiC strengths increased by a factor of six and now equal values achieved for Si3N4. Correlations of impact strength with material properties are discussed. Reduced MgO densification aid additions to Si3N4 were found to decrease densification kinetics, increase final porosity, decrease room temperature bend strength, increase high temperature bend strength, and decrease bend stress rupture properties. The decrease in bend strength at high temperature for fine grain size SiC suggested that a slightly larger grain size material with a nearly constant strength-temperature relation may prove desirable in the creep and stress rupture mode.

Structure of Cu/Ni Nanowires Obtained by Matrix Synthesis

NASA Astrophysics Data System (ADS)

Zhigalina, O. M.; Doludenko, I. M.; Khmelenin, D. N.; Zagorskiy, D. L.; Bedin, S. A.; Ivanov, I. M.

2018-05-01

The structure of layered Cu/Ni nanowires obtained by template synthesis in 100-nm channels of track membranes has been investigated by transmission and scanning electron microscopy. The phase composition and main structural features of individual nanowires are determined. It is shown that nanowires consist of alternating Ni ( Fm3m) and Cu ( Fm3m) layers with grains up to 100 nm in size. It is found that nanowires contain also copper oxide crystallites up to 20 nm in size. The elemental composition of individual layers and their mutual arrangement are determined.

Grain Size Distribution and Health Risk Assessment of Metals in Outdoor Dust in Chengdu, Southwestern China.

PubMed

Chen, Mengqin; Pi, Lu; Luo, Yan; Geng, Meng; Hu, Wenli; Li, Zhi; Su, Shijun; Gan, Zhiwei; Ding, Sanglan

2016-04-01

A total of 27 outdoor dust samples from roads, parks, and high spots were collected and analyzed to investigate the contamination of 11 metals (Cr, Mn, Co, Ni, Cu, Zn, As, Sr, Cd, Sb, and Pb) in Chengdu, China. The results showed that the samples from the high spots exhibited the highest heavy metal level compared with those from the roads and the parks, except for Ni, Cu, and Pb. The dust was classified into five grain size fractions. The mean loads of each grain size fraction of 11 determined metals displayed similar distribution, and the contribution of median size (63-125, 125-250, 250-500 μm) fractions accounted for more than 70% of overall heavy metal loads. The health risk posed by the determined metals to human via dust ingestion, dermal contact, and inhalation was investigated. Oral and respiratory bioaccessible parts of the metals in dust were extracted using simulated stomach solution and composite lung serum. The mean bioaccessibilities of 11 investigated metals in the gastric solution were much higher than those in the composite lung serum, especially Zn, Cd, and Pb. Ingestion was the most important exposure pathway with percentage greater than 70% for both children and adults. Risk evaluation results illustrated that children in Chengdu might suffer noncarcinogenic risk when exposed to outdoor dust. Given that the cancer risk values of Pb and Cr larger than 1 × 10(-4), potential carcinogenic risk might occur for Chengdu residents through outdoor dust intake.

High Strength and Thermally Stable Nanostructured Magnesium Alloys and Nanocomposites

NASA Astrophysics Data System (ADS)

Chang, Yuan-Wei

Magnesium and its alloys are currently in the spotlight of global research because of the need to limit energy consumption and reduce the environmental impact. In particular, their low densities compared to other structural metals make them a very attractive alternative in the automobile and aerospace industries. However, their low strength compared to other structural materials (e.g. Al and steels) has limited their widespread application. This dissertation presents the results of developing and investigation of a high strength nanostructured magnesium-aluminum alloy and composite. The nanostructured magnesium alloy is prepared by cryomilling and consolidated by spark-plasma-sintering. Focused ion beam is used to prepare micropillars with different diameters ranging from 1.5 to 8 mum and micro-compression test is conducted by nanoindenter in order to evaluate the mechanical properties. The yield strength obtained in the present study is around three times higher than conventional magnesium alloys (120 MPa vs. 370 MPa). The yield strength of the nanostructured magnesium alloy is further improved through hot extrusion, resulting in a yield strength of 550 MPa and an ultimate strength of 580 MPa. The nanostructured magnesium alloy exhibits a strong size-dependence, and a significant improvement in strength is observed when the pillar diameter is reduced to below 3.5 mum. The deformation mechanisms of the compressed pillars were characterized using transmission electron microscopy. The size-induced strengthening is attributed to a less number of dislocation sources along with a higher activity of non-basal deformation mechanisms. We have also developed a high strength and thermally stable nanostructured magnesium composite by adding diamantane. A yield strength of 500 MPa is achieved, moreover, excellent thermal stability is demonstrated in the magnesium alloy containing diamantanes. The strength and grain size are thermally stable after annealing at 400°C for 100 hours. In contrast, the yield strength of the alloy without diamantanes decreases significantly after annealing due to severe grain growth. These results suggest that diamantanes are pinning the grain boundaries and inhibiting grain growth at elevated temperatures. Finally, molecular dynamics simulations and finite element analysis are used to explore the deformation mechanisms of magnesium with different grain sizes at atomic resolutions and correct tapering effect on micro-compression test, respectively. The results in the dissertation show that nanostructured Mg-Al alloy and Mg-Al-Diamantane composite are promising materials for aerospace and automobile industries.

Doped zinc oxide microspheres

DOEpatents

Arnold, W.D. Jr.; Bond, W.D.; Lauf, R.J.

1993-12-14

A new composition and method of making same for a doped zinc oxide microsphere and articles made therefrom for use in an electrical surge arrestor which has increased solid content, uniform grain size and is in the form of a gel. 4 figures.

The influence of rheological weakening and yield stress on the interaction of slabs with the 670 km discontinuity

NASA Astrophysics Data System (ADS)

Čížková, Hana; van Hunen, Jeroen; van den Berg, Arie P.; Vlaar, Nico J.

2002-06-01

Results of high resolution seismic tomography showing subducting slabs deflected in the transition zone and thickened in the lower mantle seem to call for slab material weaker than inferred from mineral physics deformation mechanisms. A possible mechanism suggested by several authors could be the weakening due to grain size reduction, which should occur in the cold portion of fast slabs after an exothermic phase transition at a depth of 400 km. Since the amount of weakening as well as the rate of subsequent strengthening due to the grain growth are not precisely known, we present here a parametric study of slab behavior in the transition zone and upper part of the lower mantle. We simulate a subducting slab in a two-dimensional (2-D) Cartesian box in the numerical model with composite rheology including diffusion creep, dislocation creep and a general stress limiting rheology approximating Peierl's creep. We concentrate on two rheologic effects: the dynamic effect of slab weakening due to grain size reduction at the phase boundary and the effect of yield stress of stress limiting rheology. The effect of trench migration on slab deformation is also included in our study. Results show that the slab ability to penetrate into the lower mantle is not significantly affected by a trench retreat in the absence of grain size weakening. However, in case of a 4 cm/yr trench retreat, grain size weakening provides a viable mechanism to deflect the slab in the transition zone, provided that stress limiting deformation mechanism would limit the effective viscosity outside the areas of grain size weakening to about 1024 Pa s.

A new route for the synthesis of submicron-sized LaB{sub 6}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lihong, Bao; Wurentuya,; Wei, Wei

Submicron crystalline LaB{sub 6} has been successfully synthesized by a solid-state reaction of La{sub 2}O{sub 3} with NaBH{sub 4} at 1200 °C. The effects of reaction temperature on the crystal structure, grain size and morphology were investigated by X-ray diffraction, scanning electron microscope and transmission electron microscope. It is found that when the reaction temperature is in the range of 1000–1100 °C, there are ultrafine nanoparticles and nanocrystals that coexist. When the reaction temperature elevated to 1200 °C, the grain morphology transformed from ultrafine nanoparticle to submicron crystals completely. High resolution transmission electron microscope images fully confirm the formation ofmore » LaB{sub 6} cubic structure. - Highlights: • Single-phased LaB{sub 6} have been synthesized by a solid-state reaction in a continuous evacuating process. • The reaction temperature has a important effect on the phase composition. • The grain size increase from nano-size to submicron with increasing reaction temperature.« less

Structure and mechanical properties of foils made of nanocrystalline beryllium

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhigalina, O. M., E-mail: zhigal@ns.crys.ras.ru; Semenov, A. A.; Zabrodin, A. V.

2016-07-15

The phase composition and structural features of (45–90)-μm-thick foils obtained from nanocrystalline beryllium during multistep thermomechanical treatment have been established using electron microscopy, electron diffraction, electron backscattering diffraction, and energy-dispersive analysis. This treatment is shown to lead to the formation of a structure with micrometer- and submicrometer-sized grains. The minimum average size of beryllium grains is 352 nm. The inclusions of beryllium oxide (BeO) of different modifications with tetragonal (sp. gr. P4{sub 2}/mnm) and hexagonal (sp. gr. P6{sub 3}/mmc) lattices are partly ground during deformation to a size smaller than 100 nm and are located along beryllium grain boundaries inmore » their volume, significantly hindering migration during treatment. The revealed structural features of foils with submicrometer-sized crystallites provide the thermal stability of their structural state. Beryllium with this structure is a promising material for X-ray instrument engineering and for the production of ultrathin (less than 10 μm) vacuum-dense foils with very high physicomechanical characteristics.« less

Study of corrosion behavior on the addition of sodium citrate in nickel electroplating on SPCC steel using EIS

NASA Astrophysics Data System (ADS)

Riastuti, R.; Ramadini, C.; Siallagan, S. T.; Rifki, A.; Herdino, F.

2018-04-01

The addition of sodium citrate to nickel electroplating process as additive is useful for refining the grain size of nickel deposit. The refining of grain size in nickel deposit as coating layer can improve surface performance, one of which corrosion resistance. This paper aims to investigate the effect of sodium citrate addition as grain refiner to promote corrosion resistance on SPCC steel. This experiment used Watt’s Bath solution of NiSO4 300 g/L, NiCl4 45 g/L, H3BO3 60 g/L, wetting agent 0.2 cc/L. Sodium citrate was added in composition of 45g/L and 60g/L. Nickel were deposited by direct current using current density on 6 A/dm2 at the acidity level of 5 for 30 minutes by keeping the operating temperature stable at 50°C. The grain size of nickel deposit was observed through Optical Microscope and Atomic Force Microscope (AFM). The corrosion behavior of SPCC was observed by linear polarization and Electrochemical Impedance Spectroscopy (EIS) methods using 3% NaCl solution. Based on the research, the addition of sodium citrate as grain refiner will increasing corrosion resistance on SPCC steel from 0.35 to 0.05 mm/year.

Bulk critical state and fundamental length scales of superconducting nanocrystalline Nb3Al in Nb-Al matrix

NASA Astrophysics Data System (ADS)

Mondal, Puspen; Manekar, Meghmalhar; Srivastava, A. K.; Roy, S. B.

2009-07-01

We present the results of magnetization measurements on an as-cast nanocrystalline Nb3Al superconductor embedded in Nb-Al matrix. The typical grain size of Nb3Al ranges from about 2-8 nm with the maximum number of grains at around 3.5 nm, as visualized using transmission electron microscopy. The isothermal magnetization hysteresis loops in the superconducting state can be reasonably fitted within the well-known Kim-Anderson critical-state model. By using the same fitting parameters, we calculate the variation in field with respect to distance inside the sample and show the existence of a critical state over length scales much larger than the typical size of the superconducting grains. Our results indicate that a bulk critical current is possible in a system comprising of nanoparticles. The nonsuperconducting Nb-Al matrix thus appears to play a major role in the bulk current flow through the sample. The superconducting coherence length ξ is estimated to be around 3 nm, which is comparable to the typical grain size. The penetration depth λ is estimated to be about 94 nm, which is much larger than the largest of the superconducting grains. Our results could be useful for tuning the current carrying capability of conductors made out of composite materials which involve superconducting nanoparticles.

ACCURATE MODELING OF X-RAY EXTINCTION BY INTERSTELLAR GRAINS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hoffman, John; Draine, B. T., E-mail: jah5@astro.princeton.edu, E-mail: draine@astro.princeton.edu

Interstellar abundance determinations from fits to X-ray absorption edges often rely on the incorrect assumption that scattering is insignificant and can be ignored. We show instead that scattering contributes significantly to the attenuation of X-rays for realistic dust grain size distributions and substantially modifies the spectrum near absorption edges of elements present in grains. The dust attenuation modules used in major X-ray spectral fitting programs do not take this into account. We show that the consequences of neglecting scattering on the determination of interstellar elemental abundances are modest; however, scattering (along with uncertainties in the grain size distribution) must bemore » taken into account when near-edge extinction fine structure is used to infer dust mineralogy. We advertise the benefits and accuracy of anomalous diffraction theory for both X-ray halo analysis and near edge absorption studies. We present an open source Fortran suite, General Geometry Anomalous Diffraction Theory (GGADT), that calculates X-ray absorption, scattering, and differential scattering cross sections for grains of arbitrary geometry and composition.« less

Stardust from Supernovae and Its Isotopes

NASA Astrophysics Data System (ADS)

Hoppe, Peter

Primitive solar system materials, namely, meteorites, interplanetary dust particles, and cometary matter contain small quantities of nanometer- to micrometer-sized refractory dust grains that exhibit large isotopic abundance anomalies. These grains are older than our solar system and have been named "presolar grains." They formed in the winds of red giant and asymptotic giant stars and in the ejecta of stellar explosions, i.e., represent a sample of stardust that can be analyzed in terrestrial laboratories for isotopic compositions and other properties. The inventory of presolar grains is dominated by grains from red giant and asymptotic giant branch stars. Presolar grains from supernovae form a minor but important subpopulation. Supernova (SN) minerals identified to date include silicon carbide, graphite, silicon nitride, oxides, and silicates. Isotopic studies of major, minor, and trace elements in these dust grains have provided detailed insights into nucleosynthetic and mixing processes in supernovae and how dust forms in these violent environments.

What does it take to turn a rock into a badlands material?

NASA Astrophysics Data System (ADS)

Kasanin-Grubin, Milica; Nadal Romero, Estela; Della Seta, Marta; Martinez-Murillo, Juan F.

2016-04-01

Badlands can develop under different climatic conditions ranging from arid to humid on materials that have a complex combination of physico-chemical properties. The aim of this study is to determine the critical material properties for badland development based on current knowledge and new data. For that purpose we analyzed, both using the existing and new data, the importance of the distribution of grain size, mineralogical composition, and physico-chemical properties. Generally, the badland materials are most commonly described as "fine - grained" however, the size of the dominant grain fractions is not the solely important parameter. We argue that there is a critical amount of each size fraction (sand, silt and clay) that makes these materials susceptible to erosion. Furthermore, sorting of the material is an important factor in material susceptibility to erosion. The well-sorted fine sediments are generally considered as materials prone to disintegration and piping, while sediments with a large range of sizes and higher degree of packing are more resistant. However, poorly sorted sediments can also be very erodible and are found in badlands. Besides quartz, feldspar and carbonates, clay minerals are always present in badland materials and these minerals are crucial for badland development.The dominant clay mineral determines the behaviour of badland material, regarding swelling/shrinking, dispersion and crust development. Previous studies have shown that pH, SAR (sodium adsorption ratio), TDS (total dissolved salts), PS (percentage of sodium) and ESP (exchangeable sodium percentage) are distinctive parameters for both eroded and non-eroded slopes in badlands. Furthermore, our findings prove that content of organic carbon (Corg) is also a very important parameter and that materials with high SAR are less dispersive if the Corg is above 3%. In conclusion, this study shows that there are a number of thresholds regarding grain size, mineralogical composition and physico-chemical parameters that have to be met to make sediment a badland material.

Electrical and Thermal Transport in Coplanar Polycrystalline Graphene-hBN Heterostructures.

PubMed

Barrios-Vargas, José Eduardo; Mortazavi, Bohayra; Cummings, Aron W; Martinez-Gordillo, Rafael; Pruneda, Miguel; Colombo, Luciano; Rabczuk, Timon; Roche, Stephan

2017-03-08

We present a theoretical study of electronic and thermal transport in polycrystalline heterostructures combining graphene (G) and hexagonal boron nitride (hBN) grains of varying size and distribution. By increasing the hBN grain density from a few percent to 100%, the system evolves from a good conductor to an insulator, with the mobility dropping by orders of magnitude and the sheet resistance reaching the MΩ regime. The Seebeck coefficient is suppressed above 40% mixing, while the thermal conductivity of polycrystalline hBN is found to be on the order of 30-120 Wm -1 K -1 . These results, agreeing with available experimental data, provide guidelines for tuning G-hBN properties in the context of two-dimensional materials engineering. In particular, while we proved that both electrical and thermal properties are largely affected by morphological features (e.g., by the grain size and composition), we find in all cases that nanometer-sized polycrystalline G-hBN heterostructures are not good thermoelectric materials.

[Biological activity evaluation of porous HA ceramics using NH4 HCO3/PVA as pore-creating agents].

PubMed

Wang, Songquan; Zhang, Dekun

2010-12-01

Porous HA ceramics were prepared by using NH4 HCO3/PVA as pore-formed material along with biological glass as intensifier, and these ceramics were immersed in Locke's Physiological Saline and Simulate Body Fluid (SBF). The changes of phase composition, grain size and crystallinity of porous HA ceramics before and after immersion were investigated by X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM). The biological activity was evaluated. The porous HA ceramics showed various degrees of decomposition after immersion in the two solution systems, but there was no evident change in respect to crystallinity. Besides, the impact of different degrees of solution systems on the change of grain size and planar preferred orientation was observed. The TCP phase of the ceramics immersed in Locke's Physiological Saline decomposed and there was no crystal growth on the surface of ceramics; however, the grain size of ceramics immersed in SBF became refined in certain degree and the surface of ceramics took on the new crystal growth.

Mapping South San Francisco Bay's seabed diversity for use in wetland restoration planning

USGS Publications Warehouse

Fregoso, Theresa A.; Jaffe, B.; Rathwell, G.; Collins, W.; Rhynas, K.; Tomlin, V.; Sullivan, S.

2006-01-01

Data for an acoustic seabed classification were collected as a part of a California Coastal Conservancy funded bathymetric survey of South Bay in early 2005.  A QTC VIEW seabed classification system recorded echoes from a sungle bean 50 kHz echosounder.  Approximately 450,000 seabed classification records were generated from an are of of about 30 sq. miles.  Ten district acoustic classes were identified through an unsupervised classification system using principle component and cluster analyses.  One hundred and sixty-one grab samples and forty-five benthic community composition data samples collected in the study area shortly before and after the seabed classification survey, further refined the ten classes into groups based on grain size.  A preliminary map of surficial grain size of South Bay was developed from the combination of the seabed classification and the grab and benthic samples.  The initial seabed classification map, the grain size map, and locations of sediment samples will be displayed along with the methods of acousitc seabed classification.

Effect of deformation induced nucleation and phase mixing, a two phase model for the ductile deformation of rocks.

NASA Astrophysics Data System (ADS)

Bevillard, Benoit; Richard, Guillaume; Raimbourg, Hugues

2017-04-01

Rocks are complex materials and particularly their rheological behavior under geological stresses remains a long-standing question in geodynamics. To test large scale lithosphere dynamics numerical modeling is the main tool but encounter substantial difficulties to account for this complexity. One major unknown is the origin and development of the localization of deformation. This localization is observed within a large range of scales and is commonly characterized by sharp grain size reduction. These considerations argues for a control of the microscopical scale over the largest ones through one predominant variable: the mean grain-size. However, the presence of second phase and broad grain-size distribution may also have a important impact on this phenomenon. To address this question, we built a model for ductile rocks deformation based on the two-phase damage theory of Bercovici & Ricard 2012. We aim to investigate the role of grain-size reduction but also phase mixing on strain localization. Instead of considering a Zener-pining effect on damage evolution, we propose to take into account the effect of the grain-boundary sliding (GBS)-induced nucleation mechanism which is better supported by experimental or natural observations (Precigout et al 2016). This continuum theory allows to represent a two mineral phases aggregate with explicit log-normal grain-size distribution as a reasonable approximation for polymineralic rocks. Quantifying microscopical variables using a statistical approach may allow for calibration at small (experimental) scale. The general set of evolutions equations remains up-scalable provided some conditions on the homogenization scale. Using the interface density as a measure of mixture quality, we assume unlike Bercovici & Ricard 2012 that it may depend for some part on grain-size . The grain-size independent part of it is being represented by a "contact fraction" variable, whose evolution may be constrained by the dominant deformation mechanism. To derive the related evolution equations and account for the interdependence of thermodynamic state variables, we use Onsager's thermodynamic extremum principle. Eventually, we solve for our set of equations using an Anorthite/Pyroxene gabbroic composition. The results are used to discuss the interaction between grain-size reduction and phase mixing on strain localization on several simple cases. Bercovici D, Ricard Y (2012) Mechanisms for the generation of plate tectonics by two phase grain damage and pinning. Physics of the Earth and Planetary Interiors 202-203:27-55 Precigout J, Stunitz H (2016) Evidence of phase nucleation during olivine diffusion creep: A new perspective for mantle strain localisation. Earth and Planetary Science Letters 405:94-105

In-situ High Temperature Phase Transformations in Ceramics

DTIC Science & Technology

2009-07-28

microscopy - SEM and transmission electron microscopy - TEM), have identified important microstructural considerations, such as the critical ...particularly with judicial design of the critical particle size and microstructure.12, 47, 48 Likewise, preliminary work indicates the possibility of high...toughening of fiber reinforced, fibrous monolithic or laminated ceramic matrix composites.49, 50 enstatite was above a 7 μm critical grain size

Oxygen Isotopic Compositions of Solar Corundum Grains

NASA Astrophysics Data System (ADS)

Makide, Kentaro; Nagashima, Kazuhide; Krot, Alexander N.; Huss, Gary R.

2009-11-01

Oxygen is one of the major rock-forming elements in the solar system and the third most abundant element of the Sun. Oxygen isotopic composition of the Sun, however, is not known due to a poor resolution of astronomical spectroscopic measurements. Several Δ17O values have been proposed for the composition of the Sun based on (1) the oxygen isotopic measurements of the solar wind implanted into metallic particles in lunar soil (< -20‰ by Hashizume & Chaussidon and ~ +26‰ by Ireland et al.), (2) the solar wind returned by the Genesis spacecraft (-27‰ ± 6‰ by McKeegan et al.), and (3) the mineralogically pristine calcium-aluminum-rich inclusions (CAIs) (-23.3‰ ± 1.9‰ by Makide et al. and -35‰ by Gounelle et al.). CAIs are the oldest solar system solids, and are believed to have formed by evaporation, condensation, and melting processes in hot nebular region(s) when the Sun was infalling (Class 0) or evolved (Class 1) protostar. Corundum (Al2O3) is thermodynamically the first condensate from a cooling gas of solar composition. Corundum-bearing CAIs, however, are exceptionally rare, suggesting either continuous reaction of the corundum condensates with a cooling nebular gas and their replacement by hibonite (CaAl12O19) or their destruction by melting together with less refractory condensates during formation of igneous CAIs. In contrast to the corundum-bearing CAIs, isolated micrometer-sized corundum grains are common in the acid-resistant residues from unmetamorphosed chondrites. These grains could have avoided multistage reprocessing during CAI formation and, therefore, can potentially provide constraints on the initial oxygen isotopic composition of the solar nebula, and, hence, of the Sun. Here we report oxygen isotopic compositions of ~60 micrometer-sized corundum grains in the acid-resistant residues from unequilibrated ordinary chondrites (Semarkona (LL3.0), Bishunpur (LL3.1), Roosevelt County 075 (H3.2)) and unmetamorphosed carbonaceous chondrites (Orgueil (CI1), Murray (CM2), and Alan Hills A77307 (CO3.0)) measured with a Cameca ims-1280 ion microprobe. All corundum grains, except two, are 16O-rich (Δ17O = -22.7‰ ± 8.5‰, 2σ), and compositionally similar to the mineralogically pristine CAIs from the CR carbonaceous chondrites (-23.3‰ ± 1.9‰, 2σ), and solar wind returned by the Genesis spacecraft (-27‰ ± 6‰, 2σ). One corundum grain is highly 17O-enriched (δ17O ~ +60‰, δ18O ~ -40‰) and is probably of the presolar origin; the origin of another 17O-rich grain (δ17O ~ -15‰, δ18O ~ -35‰) is unclear. We conclude that the 16O-rich corundum grains in the acid-resistant residues from unequilibrated ordinary and unmetamorphosed carbonaceous chondrites recorded initial oxygen isotopic composition of the solar nebula, and, hence, of the Sun. Our inferred oxygen isotopic composition of the Sun is inconsistent with the more extreme 16O-rich value (Δ17O ~ -35‰) proposed by Gounelle et al. on the basis of two extremely 16O-rich CAIs from the CH/CB-like chondrite Isheyevo and with the 16O-poor value observed as a component of the solar wind implanted into the metallic particles in lunar soil (Ireland et al.).

A field method for making a quantitative estimate of altered tuff in sandstone

USGS Publications Warehouse

Cadigan, R.A.

1954-01-01

The use of benzidine to identify altered tuff in sandstone is practical for field or field laboratory studies associated with stratigraphic correlations, mineral deposit investigations, or paleogeographic interpretations. The method is based on the ability of saturated benzidine (C12H12N2) solution to produce a blue stain on montmorillonite-bearing tuff grains. The method is substantiated by the results of microscopic, X-ray spectrometer, and spectrographic tests which lead to the conclusion that: (1) the benzidine stain test differentiates grains of different composition, (2) the white or gray grains which are stained a uniform blue color are fragments of altered tuff, and (3) white or gray grains which stain in a few small spots are probably silicified tuff. The amount of sand grains taken from a hand specimen or an outcrop which will be held by a penny is spread out on a nonabsorbent white surface and soaked with benzidine for 5 minutes. The approximate number blue grains and the average grain size are used in a chart to determine a reference number which measures relative order of abundance. The chart, based on a volume relationship, corrects for the variation in the number of grains in the sample as the grain size varies. Practical use of the method depends on a knowledge of several precautionary measures as well as an understanding of the limitations of benzidine staining tests.

A generalized self-consistent polycrystal model for the yield strength of nanocrystalline materials

NASA Astrophysics Data System (ADS)

Jiang, B.; Weng, G. J.

2004-05-01

Inspired by recent molecular dynamic simulations of nanocrystalline solids, a generalized self-consistent polycrystal model is proposed to study the transition of yield strength of polycrystalline metals as the grain size decreases from the traditional coarse grain to the nanometer scale. These atomic simulations revealed that a significant portion of atoms resides in the grain boundaries and the plastic flow of the grain-boundary region is responsible for the unique characteristics displayed by such materials. The proposed model takes each oriented grain and its immediate grain boundary to form a pair, which in turn is embedded in the infinite effective medium with a property representing the orientational average of all these pairs. We make use of the linear comparison composite to determine the nonlinear behavior of the nanocrystalline polycrystal through the concept of secant moduli. To this end an auxiliary problem of Christensen and Lo (J. Mech. Phys. Solids 27 (1979) 315) superimposed on the eigenstrain field of Luo and Weng (Mech. Mater. 6 (1987) 347) is first considered, and then the nonlinear elastoplastic polycrystal problem is addressed. The plastic flow of each grain is calculated from its crystallographic slips, but the plastic behavior of the grain-boundary phase is modeled as that of an amorphous material. The calculated yield stress for Cu is found to follow the classic Hall-Petch relation initially, but as the gain size decreases it begins to depart from it. The yield strength eventually attains a maximum at a critical grain size and then the Hall-Petch slope turns negative in the nano-range. It is also found that, when the Hall-Petch relation is observed, the plastic behavior of the polycrystal is governed by crystallographic slips in the grains, but when the slope is negative it is governed by the grain boundaries. During the transition both grains and grain boundaries contribute competitively.

Properties and rapid low-temperature consolidation of nanocrystalline Fe-ZrO2 composite by pulsed current activated sintering

NASA Astrophysics Data System (ADS)

Kang, Hyun-Su; Ko, In-Yong; Yoon, Jin-Kook; Doh, Jung-Mann; Hong, Kyung-Tae; Shon, In-Jin

2011-02-01

Nanopowders of Fe and ZrO2 were synthesized from Fe2O3 and Zr by high-energy ball milling. The powder sizes of Fe and ZrO2 were 70 nm and 12 nm, respectively. Highly dense nanostructured 4/3Fe-ZrO2 composite was consolidated by a pulsed current activated sintering method within 1 minute from the mechanically synthesized powders (Fe-ZrO2) and horizontal milled Fe2O3+Zr powders under the 1 GPa pressure. The grain sizes of Fe and ZrO2 in the composite were calculated. The average hardness and fracture toughness values of nanostuctured 4/3Fe-ZrO2 composite were investigated.

Corrosion resistant surface for vanadium nitride and hafnium nitride layers as function of grain size

NASA Astrophysics Data System (ADS)

Escobar, C. A.; Caicedo, J. C.; Aperador, W.

2014-01-01

In this research it was studied vanadium nitride (VN) and hafnium nitride (HfN) film, which were deposited onto silicon (Si (100)) and AISI 4140 steel substrates via r.f. magnetron sputtering technique in Ar/N2 atmosphere with purity at 99.99% for both V and Hf metallic targets. Both films were approximately 1.2±0.1 μm thick. The crystallography structures that were evaluated via X-ray diffraction analysis (XRD) showed preferential orientations in the Bragg planes VN (200) and HfN (111). The chemical compositions for both films were characterized by EDX. Atomic Force Microscopy (AFM) was used to study the morphology; the results reveal grain sizes of 78±2 nm for VN and 58±2 nm for HfN and roughness values of 4.2±0.1 nm for VN and 1.5±0.1 nm for HfN films. The electrochemical performance in VN and HfN films deposited onto steel 4140 were studied by Tafel polarization curves and impedance spectroscopy methods (EIS) under contact with sodium chloride at 3.5 wt% solution, therefore, it was found that the corrosion rate decreased about 95% in VN and 99% for HfN films in relation to uncoated 4140 steel, thus demonstrating, the protecting effect of VN and HfN films under a corrosive environment as function of morphological characteristics (grain size). VN(grain size)=78±2.0 nm, VN(roughness)=4.2±0.1 nm, VN(corrosion rate)=40.87 μmy. HfN(grain size)=58±2.0 nm, HfN(roughness)=1.5±0.1 nm, HfN(corrosion rate)=0.205 μmy. It was possible to analyze that films with larger grain size, can be observed smaller grain boundary thus generating a higher corrosion rate, therefore, in this work it was found that the HfN layer has better corrosion resistance (low corrosion rate) in relation to VN film which presents a larger grain size, indicating that the low grain boundary in (VN films) does not restrict movement of the Cl- ion and in this way the corrosion rate increases dramatically.

Pore structure characterization of Chang-7 tight sandstone using MICP combined with N2GA techniques and its geological control factors

NASA Astrophysics Data System (ADS)

Cao, Zhe; Liu, Guangdi; Zhan, Hongbin; Li, Chaozheng; You, Yuan; Yang, Chengyu; Jiang, Hang

2016-11-01

Understanding the pore networks of unconventional tight reservoirs such as tight sandstones and shales is crucial for extracting oil/gas from such reservoirs. Mercury injection capillary pressure (MICP) and N2 gas adsorption (N2GA) are performed to evaluate pore structure of Chang-7 tight sandstone. Thin section observation, scanning electron microscope, grain size analysis, mineral composition analysis, and porosity measurement are applied to investigate geological control factors of pore structure. Grain size is positively correlated with detrital mineral content and grain size standard deviation while negatively related to clay content. Detrital mineral content and grain size are positively correlated with porosity, pore throat radius and withdrawal efficiency and negatively related to capillary pressure and pore-to-throat size ratio; while interstitial material is negatively correlated with above mentioned factors. Well sorted sediments with high debris usually possess strong compaction resistance to preserve original pores. Although many inter-crystalline pores are produced in clay minerals, this type of pores is not the most important contributor to porosity. Besides this, pore shape determined by N2GA hysteresis loop is consistent with SEM observation on clay inter-crystalline pores while BJH pore volume is positively related with clay content, suggesting N2GA is suitable for describing clay inter-crystalline pores in tight sandstones.

Pore structure characterization of Chang-7 tight sandstone using MICP combined with N2GA techniques and its geological control factors

PubMed Central

Cao, Zhe; Liu, Guangdi; Zhan, Hongbin; Li, Chaozheng; You, Yuan; Yang, Chengyu; Jiang, Hang

2016-01-01

Understanding the pore networks of unconventional tight reservoirs such as tight sandstones and shales is crucial for extracting oil/gas from such reservoirs. Mercury injection capillary pressure (MICP) and N2 gas adsorption (N2GA) are performed to evaluate pore structure of Chang-7 tight sandstone. Thin section observation, scanning electron microscope, grain size analysis, mineral composition analysis, and porosity measurement are applied to investigate geological control factors of pore structure. Grain size is positively correlated with detrital mineral content and grain size standard deviation while negatively related to clay content. Detrital mineral content and grain size are positively correlated with porosity, pore throat radius and withdrawal efficiency and negatively related to capillary pressure and pore-to-throat size ratio; while interstitial material is negatively correlated with above mentioned factors. Well sorted sediments with high debris usually possess strong compaction resistance to preserve original pores. Although many inter-crystalline pores are produced in clay minerals, this type of pores is not the most important contributor to porosity. Besides this, pore shape determined by N2GA hysteresis loop is consistent with SEM observation on clay inter-crystalline pores while BJH pore volume is positively related with clay content, suggesting N2GA is suitable for describing clay inter-crystalline pores in tight sandstones. PMID:27830731

On the superposition of strengthening mechanisms in dispersion strengthened alloys and metal-matrix nanocomposites: Considerations of stress and energy

NASA Astrophysics Data System (ADS)

Ferguson, J. B.; Schultz, Benjamin F.; Venugopalan, Dev; Lopez, Hugo F.; Rohatgi, Pradeep K.; Cho, Kyu; Kim, Chang-Soo

2014-03-01

Yield strength improvement in dispersion strengthened alloys and nano particle-reinforced composites by well-known strengthening mechanisms such as solid solution, grain refinement, coherent and incoherent dispersed particles, and increased dislocation density resulting from work-hardening can all be described individually. However, there is no agreed upon description of how these mechanisms combine to determine the yield strength. In this work, we propose an analytical yield strength prediction model combining arithmetic and quadratic addition approaches based on the consideration of two types of yielding mechanisms; stress-activated and energy-activated. Using data available in the literature for materials of differing grain sizes, we consider the cases of solid solutions and coherent precipitates to show that they follow stress-activated behavior. Then, we applied our model with some empirical parameters to precipitationhardenable materials of various grain sizes in both coherent and incoherent precipitate conditions, which demonstrated that grain boundary and Orowan-strengthening can be treated as energy-activated mechanisms.

Rock magnetic properties estimated from coercivity - blocking temperature diagram: application to recent volcanic rocks

NASA Astrophysics Data System (ADS)

Terada, T.; Sato, M.; Mochizuki, N.; Yamamoto, Y.; Tsunakawa, H.

2013-12-01

Magnetic properties of ferromagnetic minerals generally depend on their chemical composition, crystal structure, size, and shape. In the usual paleomagnetic study, we use a bulk sample which is the assemblage of magnetic minerals showing broad distributions of various magnetic properties. Microscopic and Curie-point observations of the bulk sample enable us to identify the constituent magnetic minerals, while other measurements, for example, stepwise thermal and/or alternating field demagnetizations (ThD, AFD) make it possible to estimate size, shape and domain state of the constituent magnetic grains. However, estimation based on stepwise demagnetizations has a limitation that magnetic grains with the same coercivity Hc (or blocking temperature Tb) can be identified as the single population even though they could have different size and shape. Dunlop and West (1969) carried out mapping of grain size and coercivity (Hc) using pTRM. However, it is considered that their mapping method is basically applicable to natural rocks containing only SD grains, since the grain sizes are estimated on the basis of the single domain theory (Neel, 1949). In addition, it is impossible to check thermal alteration due to laboratory heating in their experiment. In the present study we propose a new experimental method which makes it possible to estimate distribution of size and shape of magnetic minerals in a bulk sample. The present method is composed of simple procedures: (1) imparting ARM to a bulk sample, (2) ThD at a certain temperature, (3) stepwise AFD on the remaining ARM, (4) repeating the steps (1) ~ (3) with ThD at elevating temperatures up to the Curie temperature of the sample. After completion of the whole procedures, ARM spectra are calculated and mapped on the HC-Tb plane (hereafter called HC-Tb diagram). We analyze the Hc-Tb diagrams as follows: (1) For uniaxial SD populations, theoretical curve for a certain grain size (or shape anisotropy) is drawn on the Hc-Tb diagram. The curves are calculated using the single domain theory, since coercivity and blocking temperature of uniaxial SD grains can be expressed as a function of size and shape. (2) Boundary between SD and MD grains are calculated and drawn on the Hc-Tb diagram according to the theory by Butler and Banerjee (1975). (3) Theoretical predictions by (1) and (2) are compared with the obtained ARM spectra to estimate quantitive distribution of size, shape and domain state of magnetic grains in the sample. This mapping method has been applied to three samples: Hawaiian basaltic lava extruded in 1995, Ueno basaltic lava formed during Matsuyama chron, and Oshima basaltic lava extruded in 1986. We will discuss physical states of magnetic grains (size, shape, domain state, etc.) and their possible origins.

Grain Structure Control of Additively Manufactured Metallic Materials

PubMed Central

Faierson, Eric J.

2017-01-01

Grain structure control is challenging for metal additive manufacturing (AM). Grain structure optimization requires the control of grain morphology with grain size refinement, which can improve the mechanical properties of additive manufactured components. This work summarizes methods to promote fine equiaxed grains in both the additive manufacturing process and subsequent heat treatment. Influences of temperature gradient, solidification velocity and alloy composition on grain morphology are discussed. Equiaxed solidification is greatly promoted by introducing a high density of heterogeneous nucleation sites via powder rate control in the direct energy deposition (DED) technique or powder surface treatment for powder-bed techniques. Grain growth/coarsening during post-processing heat treatment can be restricted by presence of nano-scale oxide particles formed in-situ during AM. Grain refinement of martensitic steels can also be achieved by cyclic austenitizing in post-processing heat treatment. Evidently, new alloy powder design is another sustainable method enhancing the capability of AM for high-performance components with desirable microstructures.

High efficiency, low cost, thin film silicon solar cell design and method for making

DOEpatents

Sopori, Bhushan L.

2001-01-01

A semiconductor device having a substrate, a conductive intermediate layer deposited onto said substrate, wherein the intermediate layer serves as a back electrode, an optical reflector, and an interface for impurity gettering, and a semiconductor layer deposited onto said intermediate layer, wherein the semiconductor layer has a grain size at least as large as the layer thickness, and preferably about ten times the layer thickness. The device is formed by depositing a metal layer on a substrate, depositing a semiconductive material on the metal-coated substrate to produce a composite structure, and then optically processing the composite structure by illuminating it with infrared electromagnetic radiation according to a unique time-energy profile that first produces pits in the backside surface of the semiconductor material, then produces a thin, highly reflective, low resistivity alloy layer over the entire area of the interface between the semiconductor material and the metal layer, and finally produces a grain-enhanced semiconductor layer. The time-energy profile includes increasing the energy to a first energy level to initiate pit formation and create the desired pit size and density, then ramping up to a second energy level in which the entire device is heated to produce an interfacial melt, and finally reducing the energy to a third energy level and holding for a period of time to allow enhancement in the grain size of the semiconductor layer.

High efficiency low cost thin film silicon solar cell design and method for making

DOEpatents

Sopori, Bhushan L.

1999-01-01

A semiconductor device having a substrate, a conductive intermediate layer deposited onto said substrate, wherein the intermediate layer serves as a back electrode, an optical reflector, and an interface for impurity gettering, and a semiconductor layer deposited onto said intermediate layer, wherein the semiconductor layer has a grain size at least as large as the layer thickness, and preferably about ten times the layer thickness. The device is formed by depositing a metal layer on a substrate, depositing a semiconductive material on the metal-coated substrate to produce a composite structure, and then optically processing the composite structure by illuminating it with infrared electromagnetic radiation according to a unique time-energy profile that first produces pits in the backside surface of the semiconductor material, then produces a thin, highly reflective, low resistivity alloy layer over the entire area of the interface between the semiconductor material and the metal layer, and finally produces a grain-enhanced semiconductor layer. The time-energy profile includes increasing the energy to a first energy level to initiate pit formation and create the desired pit size and density, then ramping up to a second energy level in which the entire device is heated to produce an interfacial melt, and finally reducing the energy to a third energy level and holding for a period of time to allow enhancement in the grain size of the semiconductor layer.

Ba isotopic compositions in stardust SiC grains from the Murchison meteorite: Insights into the stellar origins of large SiC grains

NASA Astrophysics Data System (ADS)

Ávila, Janaína N.; Ireland, Trevor R.; Gyngard, Frank; Zinner, Ernst; Mallmann, Guilherme; Lugaro, Maria; Holden, Peter; Amari, Sachiko

2013-11-01

We report barium isotopic measurements in 12 large (7-58 μm) stardust silicon carbide grains recovered from the Murchison carbonaceous chondrite. The C-, N-, and Si-isotopic compositions indicate that all 12 grains belong to the mainstream population and, as such, are interpreted to have condensed in the outflows of low-mass carbon-rich asymptotic giant branch (AGB) stars with close-to-solar metallicity. Barium isotopic analyses were carried out on the Sensitive High Resolution Ion Microprobe - Reverse Geometry (SHRIMP-RG) with combined high mass resolution and energy filtering to eliminate isobaric interferences from molecular ions. Contrary to previous measurements in small (<5 μm) mainstream grains, the analyzed large SiC grains do not show the classical s-process enrichment, having near solar Ba isotopic compositions. While contamination with solar material is a common explanation for the lack of large isotopic anomalies in stardust SiC grains, particularly for these large grains which have low trace element abundances, our results are consistent with previous observations that Ba isotopic ratios are dependent on grain size. We have compared the SiC data with theoretical predictions of the evolution of Ba isotopic ratios in the envelopes of low-mass AGB stars with a range of stellar masses and metallicities. The Ba isotopic measurements obtained for large SiC grains from the LS + LU fractions are consistent with grain condensation in the envelope of very low-mass AGB stars (1.25 M⊙) with close-to-solar metallicity, which suggests that conditions for growth of large SiC might be more favorable in very low-mass AGB stars during the early C-rich stages of AGB evolution or in stable structures around AGB stars whose evolution was cut short due to binary interaction, before the AGB envelope had already been largely enriched with the products of s-process nucleosynthesis.

Process for fabricating doped zinc oxide microsphere gel

DOEpatents

Arnold, Jr., Wesley D.; Bond, Walter D.; Lauf, Robert J.

1991-01-01

A new composition and method of making same for a doped zinc oxide microsphere and articles made therefrom for use in an electrical surge arrestor which has increased solid content, uniform grain size and is in the form of a gel.

THE COMPOSITION OF INTERSTELLAR GRAINS TOWARD ζ OPHIUCHI: CONSTRAINING THE ELEMENTAL BUDGET NEAR THE DIFFUSE-DENSE CLOUD TRANSITION

DOE Office of Scientific and Technical Information (OSTI.GOV)

Poteet, Charles A.; Whittet, Douglas C. B.; Draine, Bruce T., E-mail: charles.poteet@gmail.com

2015-03-10

We investigate the composition of interstellar grains along the line of sight toward ζ Ophiuchi, a well-studied environment near the diffuse-dense cloud transition. A spectral decomposition analysis of the solid-state absorbers is performed using archival spectroscopic observations from the Spitzer Space Telescope and Infrared Space Observatory. We find strong evidence for the presence of sub-micron-sized amorphous silicate grains, principally comprised of olivine-like composition, with no convincing evidence of H{sub 2}O ice mantles. However, tentative evidence for thick H{sub 2}O ice mantles on large (a ≈ 2.8 μm) grains is presented. Solid-state abundances of elemental Mg, Si, Fe, and O aremore » inferred from our analysis and compared to standard reference abundances. We find that nearly all of the Mg and Si atoms along the line of sight reside in amorphous silicate grains, while a substantial fraction of the elemental Fe resides in compounds other than silicates. Moreover, we find that the total abundance of elemental O is largely inconsistent with the adopted reference abundances, indicating that as much as ∼156 ppm of interstellar O is missing along the line of sight. After taking into account additional limits on the abundance of elemental O in other O-bearing solids, we conclude that any missing reservoir of elemental O must reside on large grains that are nearly opaque to infrared radiation.« less

Geochemistry of the Bagnold dune field as observed by ChemCam and comparison with other aeolian deposits at Gale Crater

DOE Office of Scientific and Technical Information (OSTI.GOV)

Agnes, Cousin; Dehouck, Erwin; Meslin, Pierre-Yves

The Curiosity rover conducted the first field investigation of an active extraterrestrial dune. Our study of the Bagnold dunes focuses on the ChemCam chemical results and also presents findings on the grain size distributions based on the ChemCam RMI and MAHLI images. These active dunes are composed of grains that are mostly <250 μm. Their composition is overall similar to that of the aeolian deposits analyzed all along the traverse (“Aeolis Palus soils”). Nevertheless, the dunes contain less volatiles (Cl, H, S) than the Aeolis Palus soils, which appears to be due to a lower content of volatile-rich fine-grained particlesmore » (<100 μm), or a lower content of volatile-rich amorphous component, possibly as a result of: 1) a lower level of chemical alteration; 2) the removal of an alteration rind at the surface of the grains during transport; 3) a lower degree of interaction with volcanic gases/aerosols; or 4) physical sorting that removed the smallest and most altered grains. Analyses of the >150 μm grain-size dump piles have shown that coarser grains (150-250 μm) are enriched in the mafic elements Fe and Mn, suggesting a larger content in olivine compared to smaller grains (<150 μm) of the Bagnold dunes. Furthermore, the chemistry of soils analyzed in the vicinity of the dunes indicates that they are similar to the dune material. Altogether these observations suggest that the olivine content determined by X-ray diffraction of the <150 μm grain-size sample should be considered as a lower limit for the Bagnold dunes.« less

Geochemistry of the Bagnold dune field as observed by ChemCam and comparison with other aeolian deposits at Gale Crater

DOE PAGES

Agnes, Cousin; Dehouck, Erwin; Meslin, Pierre-Yves; ...

2017-06-27

The Curiosity rover conducted the first field investigation of an active extraterrestrial dune. Our study of the Bagnold dunes focuses on the ChemCam chemical results and also presents findings on the grain size distributions based on the ChemCam RMI and MAHLI images. These active dunes are composed of grains that are mostly <250 μm. Their composition is overall similar to that of the aeolian deposits analyzed all along the traverse (“Aeolis Palus soils”). Nevertheless, the dunes contain less volatiles (Cl, H, S) than the Aeolis Palus soils, which appears to be due to a lower content of volatile-rich fine-grained particlesmore » (<100 μm), or a lower content of volatile-rich amorphous component, possibly as a result of: 1) a lower level of chemical alteration; 2) the removal of an alteration rind at the surface of the grains during transport; 3) a lower degree of interaction with volcanic gases/aerosols; or 4) physical sorting that removed the smallest and most altered grains. Analyses of the >150 μm grain-size dump piles have shown that coarser grains (150-250 μm) are enriched in the mafic elements Fe and Mn, suggesting a larger content in olivine compared to smaller grains (<150 μm) of the Bagnold dunes. Furthermore, the chemistry of soils analyzed in the vicinity of the dunes indicates that they are similar to the dune material. Altogether these observations suggest that the olivine content determined by X-ray diffraction of the <150 μm grain-size sample should be considered as a lower limit for the Bagnold dunes.« less

Thermal Stabilization and Mechanical Properties of Nanocrystalline Iron-Nickel-Zirconium Alloys

NASA Astrophysics Data System (ADS)

Kotan, Hasan

Ultrafine grained and nanostructured materials are promising for structural applications because of the high strength compared to coarse grained counterparts. However, their widespread application is limited by an inherently high driving force for thermally induced grain growth, even at low temperatures. Accordingly, the understanding of and control over grain growth in nanoscale materials is of great technological and scientific importance as many physical properties (i.e. mechanical properties) are functions of the average grain size and the grain size distribution within the microstructure. Here, we investigate the microstructural evolution and grain growth in Fe-Ni alloys with Zr addition and differentiate the stabilization mechanisms acting on grain boundaries. Fe-Ni alloys are chosen for stability investigations since they are important for understanding the behavior of many steels and other ferrous alloys. Zirconium is proven to be an effective grain size stabilizer in pure Fe and Fe-base systems. In this study, nanocrystalline alloys were prepared by high energy ball milling. In situ and ex situ experiments were utilized to directly follow grain growth and microstructural evolution as a function of temperature and composition. The information obtained from these experiments enables the real time observation of microstructural evolution and phase transformation and provides a unique view of dynamic reactions as they occur. The knowledge of the thermal stability will exploit the potential high temperature applications and the consolidation conditions (i.e. temperature and pressure) to obtain high dense materials for advanced mechanical tests. Our investigations reveal that the grain growth of Fe-Ni alloys is not affected by Ni content but strongly inhibited by the addition of 1 at% Zr up to about 700 °C. The microstructural stability is lost due to the bcc-to-fcc transformation (occurring at 700°C) by the sudden appearance of abnormally grown fcc grains. However it was determined grain growth can be suppressed kinetically at higher temperatures for high Zr containing alloys by precipitation of intermetallic compounds. Eventually at high enough temperatures the retention of nanocrystallinity was lost, leaving behind fine micron grains filled with nanoscale intermetallic precipitates. Despite the loss of stability the in-situ formed precipitates were found to induce an Orowan hardening affect. The results from the mechanical tests show that Orowan particle strengthening can be as significant as Hall Petch hardening is at the smallest grain sizes.

Statistical electric field and switching time distributions in PZT 1Nb2Sr ceramics: Crystal- and microstructure effects

NASA Astrophysics Data System (ADS)

Zhukov, Sergey; Kungl, Hans; Genenko, Yuri A.; von Seggern, Heinz

2014-01-01

Dispersive polarization response of ferroelectric PZT ceramics is analyzed assuming the inhomogeneous field mechanism of polarization switching. In terms of this model, the local polarization switching proceeds according to the Kolmogorov-Avrami-Ishibashi scenario with the switching time determined by the local electric field. As a result, the total polarization reversal is dominated by the statistical distribution of the local field magnitudes. Microscopic parameters of this model (the high-field switching time and the activation field) as well as the statistical field and consequent switching time distributions due to disorder at a mesoscopic scale can be directly determined from a set of experiments measuring the time dependence of the total polarization switching, when applying electric fields of different magnitudes. PZT 1Nb2Sr ceramics with Zr/Ti ratios 51.5/48.5, 52.25/47.75, and 60/40 with four different grain sizes each were analyzed following this approach. Pronounced differences of field and switching time distributions were found depending on the Zr/Ti ratios. Varying grain size also affects polarization reversal parameters, but in another way. The field distributions remain almost constant with grain size whereas switching times and activation field tend to decrease with increasing grain size. The quantitative changes of the latter parameters with grain size are very different depending on composition. The origin of the effects on the field and switching time distributions are related to differences in structural and microstructural characteristics of the materials and are discussed with respect to the hysteresis loops observed under bipolar electrical cycling.

High Temperature, Slow Strain Rate Forging of Advanced Disk Alloy ME3

NASA Technical Reports Server (NTRS)

Gabb, Timothy P.; OConnor, Kenneth

2001-01-01

The advanced disk alloy ME3 was designed in the HSR/EPM disk program to have extended durability at 1150 to 1250 F in large disks. This was achieved by designing a disk alloy and process producing balanced monotonic, cyclic, and time-dependent mechanical properties. combined with robust processing and manufacturing characteristics. The resulting baseline alloy, processing, and supersolvus heat treatment produces a uniform, relatively fine mean grain size of about ASTM 7, with as-large-as (ALA) grain size of about ASTM 3. There is a long term need for disks with higher rim temperature capabilities than 1250 F. This would allow higher compressor exit (T3) temperatures and allow the full utilization of advanced combustor and airfoil concepts under development. Several approaches are being studied that modify the processing and chemistry of ME3, to possibly improve high temperature properties. Promising approaches would be applied to subscale material, for screening the resulting mechanical properties at these high temperatures. n obvious path traditionally employed to improve the high temperature and time-dependent capabilities of disk alloys is to coarsen the grain size. A coarser grain size than ASTM 7 could potentially be achieved by varying the forging conditions and supersolvus heat treatment. The objective of this study was to perform forging and heat treatment experiments ("thermomechanical processing experiments") on small compression test specimens of the baseline ME3 composition, to identify a viable forging process allowing significantly coarser grain size targeted at ASTM 3-5, than that of the baseline, ASTM 7.

Textural analysis of marine sediments at the USGS Woods Hole Science Center; methodology and data on DVD

USGS Publications Warehouse

Poppe, Lawrence J.; Williams, S. Jeffress; Paskevich, Valerie F.

2006-01-01

Marine sediments off the eastern United States vary markedly in texture (i.e., the size, shape, composition, and arrangement of their grains) due to a complex geologic history. For descriptive purposes, however, it is typically most useful to classify these sediments according to their grain-size distributions. In 1962, the U.S. Geological Survey began a program to study the marine geology of the continental margin off the Atlantic coast of the United States. As part of this program and numerous subsequent projects, thousands of sediment grab samples and cores were collected and analyzed for grain size at the Woods Hole Science Center. USGS Open-File Report 2005-1001 (Poppe et al., 2005), available on DVD and online, describes the field methods used to collect marine sediment samples as well as the laboratory methods used to determine and characterize grain-size distributions, and presents these data in several formats that can be readily employed by interested parties. The report is divided into three sections. The first section discusses procedures and contains pictures of the equipment, analytical flow diagrams, video clips with voice commentary, classification schemes, useful forms and compiled and uncompiled versions of the data-acquisition and data-processing software with documentation. The second section contains the grain-size data for more than 23,000 analyses in two “flat-file” formats, a data dictionary, and color-coded browse maps. The third section provides a GIS data catalog of the available point, interpretive, and baseline data layers, with FGDC-compliant metadata to help users visualize the textural information in a geographic context.

Compaction of Chromite Cumulates applying a Centrifuging Piston-Cylinder

NASA Astrophysics Data System (ADS)

Manoochehri, S.; Schmidt, M. W.

2012-12-01

Stratiform accumulations of chromite cumulates, such as the UG2 chromitite layer in the Bushveld Complex, is a common feature in most of the large layered mafic intrusions. The time scales and mechanics of gravitationally driven crystal settling and compaction and the feasibility of these processes for the formation of such cumulate layers is investigated through a series of high temperature (1280-1300 °C) centrifuge-assisted experiments at 100-2000 g, 0.4-0.6 GPa. A mixture of natural chromite, with defined grain sizes (means of 5 μm, 13 μm, and 52 μm), and a melt with a composition thought to represent the parental magma of the Bushveld Complex, was first chemically and texturally equilibrated at static conditions and then centrifuged. Centrifugation leads to a single cumulate layer formed at the gravitational bottom of the capsule. This layer was analysed for porosity, mean grain size, size distribution and also travelling distance of chromite crystals. The experimentally observed mechanical settling velocity of chromite grains in a suspension with ~ 24 vol% crystals is calculated to be about half (~ 0.53) of the Stokes settling velocity, consistent with a sedimentation exponent n of 2.35±0.3. The settling leads to a porosity of about 52 % in the chromite layer. Formation times of chromite orthocumulates with initial crystal content in the melt of 1 % and grain sizes of 2 mm are thus around 0.6 m/day. To achieve more compacted chromite piles, centrifugation times and acceleration were increased. Within each experiment the crystal content of the cumulate layer increases downward almost linearly at least in the lower 2/3 of the cumulate pile. Although porosity in the lowermost segment of the chromite layer decreases with increasing effective stress integrated over time, the absolute decrease is smaller than for experiments with olivine (from a previous study). Formation times of a ½ meter single chromite layer with 70 vol% chromite, is calculated to be around 20 years whereas this value is around 0.4 years for olivine cumulates. When considering a natural outcrop of a layered intrusion with multiple layers of about 50 meters height, adcumulate formation time decreases to a few months. With increasing the effective stress integrated over time, applied during centrifugation, crystal size distribution histograms move slightly toward larger grain sizes, but looking at mean grain sizes, a narrow range of changes can be observed. Classic crystal size distribution profiles corrected for real 3D sizes (CSDCorrectin program) of the chromite grains in different experiments illustrate a collection of parallel log-linear trends at larger grain sizes with a very slight overturn at small grain sizes. This is in close agreement with the idealized CSD plots of adcumulus growth.

Microstructure characterization of Al matrix composite reinforced with Ti-6Al-4V meshes after compression by scanning electron microscope and transmission electron microscope.

PubMed

Guo, Q; Sun, D L; Han, X L; Cheng, S R; Chen, G Q; Jiang, L T; Wu, G H

2012-02-01

Compressive properties of Al matrix composite reinforced with Ti-6Al-4V meshes (TC4(m)/5A06 Al composite) under the strain rates of 10(-3)S(-1) and 1S(-1) at different temperature were measured and microstructure of composites after compression was characterized by scanning electron microscope (SEM) and transmission electron microscope (TEM). Compressive strength decreased with the test temperature increased and the strain-rate sensitivity (R) of composite increased with the increasing temperature. SEM observations showed that grains of Al matrix were elongated severely along 45° direction (angle between axis direction and fracture surface) and TC4 fibres were sheared into several parts in composite compressed under the strain rate of 10(-3)S(-1) at 25°C and 250°C. Besides, amounts of cracks were produced at the interfacial layer between TC4 fibre and Al matrix and in (Fe, Mn)Al(6) phases. With the compressive temperature increasing to 400°C, there was no damage at the interfacial layer between TC4 fibre and Al matrix and in (Fe, Mn)Al(6) phases, while equiaxed recrystal grains with sizes about 10 μm at the original grain boundaries of Al matrix were observed. However, interface separation of TC4 fibres and Al matrix occurred in composite compressed under the strain rate of 1S(-1) at 250°C and 400°C. With the compressive temperature increasing from 25°C to 100°C under the strain rate of 10(-3) S(-1), TEM microstructure in Al matrix exhibited high density dislocations and slipping bands (25°C), polygonized dislocations and dynamic recovery (100°C), equiaxed recrystals with sizes below 500 μm (250°C) and growth of equiaxed recrystals (400°C), respectively. Copyright © 2011 Elsevier Ltd. All rights reserved.

Particle size distribution of distillers dried grains with solubles (DDGS) and relationships to compositional and color properties.

PubMed

Liu, Keshun

2008-11-01

Eleven distillers dried grains with solubles (DDGS), processed from yellow corn, were collected from different ethanol processing plants in the US Midwest area. Particle size distribution (PSD) by mass of each sample was determined using a series of six selected US standard sieves: Nos. 8, 12, 18, 35, 60, and 100, and a pan. The original sample and sieve sized fractions were measured for surface color and contents of moisture, protein, oil, ash, and starch. Total carbohydrate (CHO) and total non-starch CHO were also calculated. Results show that there was a great variation in composition and color among DDGS from different plants. Surprisingly, a few DDGS samples contained unusually high amounts of residual starch (11.1-17.6%, dry matter basis, vs. about 5% of the rest), presumably resulting from modified processing methods. Particle size of DDGS varied greatly within a sample and PSD varied greatly among samples. The 11 samples had a mean value of 0.660mm for the geometric mean diameter (dgw) of particles and a mean value of 0.440mm for the geometric standard deviation (Sgw) of particle diameters by mass. The majority had a unimodal PSD, with a mode in the size class between 0.5 and 1.0mm. Although PSD and color parameters had little correlation with composition of whole DDGS samples, distribution of nutrients as well as color attributes correlated well with PSD. In sieved fractions, protein content, L and a color values negatively while contents of oil and total CHO positively correlated with particle size. It is highly feasible to fractionate DDGS for compositional enrichment based on particle size, while the extent of PSD can serve as an index for potential of DDGS fractionation. The above information should be a vital addition to quality and baseline data of DDGS.

Rate & Microstructure Influence on Fracture of WC-Co/Ni Composites

NASA Astrophysics Data System (ADS)

Lamberson, Leslie

2017-06-01

Tungsten carbide metal matrix composites contain ceramic grains of tungsten carbide within a binder of cobalt (Co) or nickel (Ni), allowing the material to have advantageous properties of both metals and ceramics including higher resistance to fracture than most structural ceramics, and higher resistance to permanent deformation than most engineering metals. Due to these performance advantages, WC composites are of interest in drilling, manufacturing tools, and defense penetrator applications, to name a few. Under quasi-static conditions, these hardmetals have been shown to generally exhibit an increase in fracture toughness with an increase in mean free path in the binder phase, and an increase in hardness and wear resistance with a decrease in WC grain size; yet relatively little is known in regards to their dynamic response. Here we present the fracture behavior of WC metal matrix composites under three extreme loading conditions: (1) a single-strike acceleration loading to characterize classical dynamic crack tip energetics via stress intensity factors (SIFs) (2) the impact fatigue, or sub-catastrophic repetitive strikes to failure, and (3) the dynamic crack interactions with normal impact over 1 km/s using an in-house combustionless two-stage light-gas gun. All investigations are conducted using ultra high-speed imaging with full-field measurements from digital image correlation (DIC), and post-mortem scanning electron microscopy. Preliminary results for (1) show that the dynamic fracture toughness increases by a factor of 1.22 to 1.65 over quasi-static, regardless of the binder or grain size investigated. Supported by the American Chemical Society Petroleum Research Fund No. 55860-ND10.

A New Electrochemical Approach for the Synthesis of Copper-Graphene Nanocomposite Foils with High Hardness

PubMed Central

Pavithra, Chokkakula L. P.; Sarada, Bulusu V.; Rajulapati, Koteswararao V.; Rao, Tata N.; Sundararajan, G.

2014-01-01

Graphene has proved its significant role as a reinforcement material in improving the strength of polymers as well as metal matrix composites due to its excellent mechanical properties. In addition, graphene is also shown to block dislocation motion in a nanolayered metal-graphene composites resulting in ultra high strength. In the present paper, we demonstrate the synthesis of very hard Cu-Graphene composite foils by a simple, scalable and economical pulse reverse electrodeposition method with a well designed pulse profile. Optimization of pulse parameters and current density resulted in composite foils with well dispersed graphene, exhibiting a high hardness of ~2.5 GPa and an increased elastic modulus of ~137 GPa while exhibiting an electrical conductivity comparable to that of pure Cu. The pulse parameters are designed in such a way to have finer grain size of Cu matrix as well as uniform dispersion of graphene throughout the matrix, contributing to high hardness and modulus. Annealing of these nanocomposite foils at 300°C, neither causes grain growth of the Cu matrix nor deteriorates the mechanical properties, indicating the role of graphene as an excellent reinforcement material as well as a grain growth inhibitor. PMID:24514043

Plasma etching a ceramic composite. [evaluating microstructure

NASA Technical Reports Server (NTRS)

Hull, David R.; Leonhardt, Todd A.; Sanders, William A.

1992-01-01

Plasma etching is found to be a superior metallographic technique for evaluating the microstructure of a ceramic matrix composite. The ceramic composite studied is composed of silicon carbide whiskers (SiC(sub W)) in a matrix of silicon nitride (Si3N4), glass, and pores. All four constituents are important in evaluating the microstructure of the composite. Conventionally prepared samples, both as-polished or polished and etched with molten salt, do not allow all four constituents to be observed in one specimen. As-polished specimens allow examination of the glass phase and porosity, while molten salt etching reveals the Si3N4 grain size by removing the glass phase. However, the latter obscures the porosity. Neither technique allows the SiC(sub W) to be distinguished from the Si3N4. Plasma etching with CF4 + 4 percent O2 selectively attacks the Si3N4 grains, leaving SiC(sub W) and glass in relief, while not disturbing the pores. An artifact of the plasma etching reaction is the deposition of a thin layer of carbon on Si3N4, allowing Si3N4 grains to be distinguished from SiC(sub W) by back scattered electron imaging.

Enhancing the Scientific Return from HST Imaging of Debris Disks

NASA Astrophysics Data System (ADS)

Weinberger, Alycia

2016-10-01

We propose realistic modeling of scattering of light by small aggregate dust grains that will enable us to interpret visible to near-infrared imaging of debris disks. We will determine if disk colors, phase functions, and polarizations place unique constraints on the composition of debris dust. Ongoing collisions of planetesimals generate dust; therefore, the dust provides unique information on compositions of the parent bodies. These exosolar analogs of asteroids and comets can bear clues to the history of a planetary system including migration and thermal processing. Because directly imaged debris disks are cold, they have no solid state emission features. Grain scattering properties as a function of wavelength are our only tool to reveal their compositions. Solar system interplanetary dust particles are fluffy aggregates, but most previous work on debris disk composition relied on Mie theory, i.e. assumed compact spherical grains. Mie calculations do not reproduce the observed colors and phase functions observed from debris disks. The few more complex calculations that exist do not explore the range of compositions and sizes relevant to debris disk dust. In particular, we expect porosity to help distinguish between cometary-like parent bodies, which are fluffy due to high volatile content and low collisional velocities, and asteroidal-like parent bodies that are compacted.

Microstructural and petrophysical characterization of a "structurally oversimplified" fault zone in poorly lithified sands: evidence for a coseismic rupture?

NASA Astrophysics Data System (ADS)

Balsamo, Fabrizio; Storti, Fabrizio

2010-05-01

We studied an extensional fault zone developed in poorly lithified, quartz-rich high porosity sandy sediments of the seismically active Crotone basin (southern Italy). The fault zone cuts across interlayered fine- to coarse-grained sands and consists of a cm-thick, discrete fault core embedded in virtually undeformed wall sediments. Consequently, it can be described as "structurally oversimplified" due to the lack of footwall and hanging wall damage zones. We acquired microstructural, grain size, grain shape, porosity, mineralogical and permeability data to investigate the influence of initial sedimentological characteristics of sands on the final faulted granular products and related hydrologic properties. Faulting evolves by a general grain size and porosity reduction with a combination of intragranular fracturing, spalling, and flaking of grain edges, irrespective of grain mineralogy. The dominance of cataclasis, also confirmed by fractal dimensions >2.6, is generally not expected at a deformation depth <1 km. Coarse-grained sand shows a much higher comminution intensity, grain shape variations and permeability drop than fine-grained sands. This is because coarser aggregates have (i) fewer grain-to-grain contacts for a given area, which results in higher stress concentration at contact points, and (ii) a higher probability of pre-existing intragranular microstructural defects that result in a lower grain strength. The peculiar structural architecture, the dominance of cataclasis over non-destructive particulate flow, and the compositional variations of clay minerals in the fault core, strongly suggest that the studied fault zone developed by a coseismic rupture.

A new method for reporting and interpreting textural composition of spawning gravel.

Treesearch

Fredrick B. Lotspeich; Fred H. Everest

1981-01-01

A new method has been developed for collecting, sorting, and interpreting gravel quality. Samples are collected with a tri-tube freeze-core device and dry-sorted by using sieves based on the Wentworth scale. An index to the quality of gravel is obtained by dividing geometric mean particle size by the sorting coefficient (a measure of the distribution of grain sizes) of...

Central role of TiO2 anatase grain boundaries on resistivity of CaCu3Ti4O12-based materials probed by Raman spectroscopy

NASA Astrophysics Data System (ADS)

De Almeida-Didry, Sonia; Autret, Cécile; Honstettre, Christophe; Lucas, Anthony; Zaghrioui, Mustapha; Pacreau, François; Gervais, François

2016-11-01

This study focuses on characterization and control of grain boundaries to enhance the properties of CaCu3Ti4O12 (CCTO) ceramics capacitors for industrial applications. A novel factor deals with TiO2 anatase revealed by Raman scattering in grain boundaries, found as a dominant parameter of largest sample resistivity, consistent with higher grain boundary resistivity and higher breakdown voltage. Four selected samples of CCTO-based compositions showing very different properties in terms of permittivity ranging from 1000 to 684 000 measured at 1 kHz, capacitance of grain boundaries ranging from 8 10-10 to 4.5 10-7 F cm-1, grain boundary resistivity ranging from 193 to 30,000,000 Ω cm and sample resistivity extending from 450 to 1011 Ω cm. The relationship between permittivity weighted by grain size and capacitance of grain boundaries confirms the internal barrier layer capacitance model over 5 orders of magnitude.

Ion implantation effects in 'cosmic' dust grains

NASA Technical Reports Server (NTRS)

Bibring, J. P.; Langevin, Y.; Maurette, M.; Meunier, R.; Jouffrey, B.; Jouret, C.

1974-01-01

Cosmic dust grains, whatever their origin may be, have probably suffered a complex sequence of events including exposure to high doses of low-energy nuclear particles and cycles of turbulent motions. High-voltage electron microscope observations of micron-sized grains either naturally exposed to space environmental parameters on the lunar surface or artificially subjected to space simulated conditions strongly suggest that such events could drastically modify the mineralogical composition of the grains and considerably ease their aggregation during collisions at low speeds. Furthermore, combined mass spectrometer and ionic analyzer studies show that small carbon compounds can be both synthesized during the implantation of a mixture of low-energy D, C, N ions in various solids and released in space by ion sputtering.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Morales, F. Y.; Bryden, G.; Werner, M. W.

We present dual-band Herschel /PACS imaging for 59 main-sequence stars with known warm dust ( T {sub warm} ∼ 200 K), characterized by Spitzer . Of 57 debris disks detected at Herschel wavelengths (70 and/or 100 and 160 μ m), about half have spectral energy distributions (SEDs) that suggest two-ring disk architectures mirroring that of the asteroid–Kuiper Belt geometry; the rest are consistent with single belts of warm, asteroidal material. Herschel observations spatially resolve the outer/cold dust component around 14 A-type and 4 solar-type stars with two-belt systems, 15 of which for the first time. Resolved disks are typically observedmore » with radii >100 AU, larger than expected from a simple blackbody fit. Despite the absence of narrow spectral features for ice, we find that the shape of the continuum, combined with resolved outer/cold dust locations, can help constrain the grain size distribution and hint at the dust’s composition for each resolved system. Based on the combined Spitzer /IRS+Multiband Imaging Photometer (5-to-70 μ m) and Herschel /PACS (70-to-160 μ m) data set, and under the assumption of idealized spherical grains, we find that over half of resolved outer/cold belts are best fit with a mixed ice/rock composition. Minimum grain sizes are most often equal to the expected radiative blowout limit, regardless of composition. Three of four resolved systems around the solar-type stars, however, tend to have larger minimum grains compared to expectation from blowout ( f {sub MB} = a {sub min}/ a {sub BOS} ∼ 5). We also probe the disk architecture of 39 Herschel -unresolved systems by modeling their SEDs uniformly, and find them to be consistent with 31 single- and 8 two-belt debris systems.« less

Formation of Glass with Embedded Metal and Sulfides from Shock-accelerated Crystalline Dust in Superbubbles

NASA Astrophysics Data System (ADS)

Westphal, A. J.; Bradley, J. P.

2004-12-01

Interplanetary dust particles (IDPs) contain enigmatic submicron components called GEMS (glass with embedded metal and sulfides). The compositions and structures of GEMS indicate that they have been processed by exposure to ionizing radiation, but details of the actual irradiation environment(s) have remained elusive. Here we propose a mechanism and astrophysical site for GEMS formation that explains for the first time the following key properties of GEMS: they are stoichiometrically enriched in oxygen and systematically depleted in S, Mg, Ca, and Fe (relative to solar abundances); most have normal (solar) oxygen isotopic compositions; they exhibit a strikingly narrow size distribution (0.1-0.5 μm diameter); and some of them contain ``relict'' crystals within their silicate glass matrices. We show that the compositions, size distribution, and survival of relict crystals are inconsistent with amorphization by particles accelerated by diffusive shock acceleration. Instead, we propose that GEMS are formed from crystalline grains that condense in stellar outflows from massive stars in OB associations, are accelerated in encounters with frequent supernova shocks inside the associated superbubble (SB), and are implanted with atoms from the hot gas in the SB interior. We thus reverse the usual roles of target and projectile. Rather than being bombarded at rest by energetic ions, grains are accelerated and bombarded by a nearly monovelocity beam of atoms as viewed in their rest frame. Meyer, Drury, and Ellison have proposed that Galactic cosmic rays (GCRs) originate from ions sputtered from such accelerated dust grains. We suggest that GEMS are surviving members of a population of fast grains that constitute the long-sought source material for GCRs. Thus, representatives of the GCR source material may have been awaiting discovery in cosmic dust labs for the last 30 yr.

An analysis of Apollo lunar soil samples 12070,889, 12030,187, and 12070,891: Basaltic diversity at the Apollo 12 landing site and implications for classification of small-sized lunar samples

NASA Astrophysics Data System (ADS)

Alexander, Louise; Snape, Joshua F.; Joy, Katherine H.; Downes, Hilary; Crawford, Ian A.

2016-09-01

Lunar mare basalts provide insights into the compositional diversity of the Moon's interior. Basalt fragments from the lunar regolith can potentially sample lava flows from regions of the Moon not previously visited, thus, increasing our understanding of lunar geological evolution. As part of a study of basaltic diversity at the Apollo 12 landing site, detailed petrological and geochemical data are provided here for 13 basaltic chips. In addition to bulk chemistry, we have analyzed the major, minor, and trace element chemistry of mineral phases which highlight differences between basalt groups. Where samples contain olivine, the equilibrium parent melt magnesium number (Mg#; atomic Mg/[Mg + Fe]) can be calculated to estimate parent melt composition. Ilmenite and plagioclase chemistry can also determine differences between basalt groups. We conclude that samples of approximately 1-2 mm in size can be categorized provided that appropriate mineral phases (olivine, plagioclase, and ilmenite) are present. Where samples are fine-grained (grain size <0.3 mm), a "paired samples t-test" can provide a statistical comparison between a particular sample and known lunar basalts. Of the fragments analyzed here, three are found to belong to each of the previously identified olivine and ilmenite basalt suites, four to the pigeonite basalt suite, one is an olivine cumulate, and two could not be categorized because of their coarse grain sizes and lack of appropriate mineral phases. Our approach introduces methods that can be used to investigate small sample sizes (i.e., fines) from future sample return missions to investigate lava flow diversity and petrological significance.

Heat transfer through particulated media in stagnant gases model and laboratory measurements: Application to Mars

NASA Astrophysics Data System (ADS)

Piqueux, Sylvain Loic Lucien

The physical characterization of the upper few centimeters to meters of the Martian surface has greatly benefited from remote temperature measurements. Typical grain sizes, rock abundances, subsurface layering, soil cementation, bedrock exposures, and ice compositions have been derived and mapped using temperature data in conjunction with subsurface models of heat conduction. Yet, these models of heat conduction are simplistic, precluding significant advances in the characterization of the physical nature of the Martian surface. A new model of heat conduction for homogeneous particulated media accounting for the grain size, porosity, gas pressure and composition, temperature, and the effect of any cementing phase is presented. The incorporation of the temperature effect on the bulk conductivity results in a distortion of the predicted diurnal and seasonal temperatures when compared to temperatures predicted with a temperature-independent conductivity model. Such distortions have been observed and interpreted to result from subsurface heterogeneities, but they may simply be explained by a temperature-dependency of the thermal inertia, with additional implications on the derived grain sizes. Cements are shown to significantly increase the bulk conductivity of a particulated medium and bond fractions <5% per volume are consistent with Martian thermal inertia data previously hypothesized to correspond to a global duricrust. A laboratory setup has been designed, built, calibrated and used to measure the thermal conductivity of particulated samples in order to test and refine the models mentioned above. Preliminary results confirm the influence of the temperature on the bulk conductivity, as well as the effect of changing the gas composition. Cemented samples are shown to conduct heat more efficiently than their uncemented counterparts.

Mineralogy of the Almahata Sitta Ureilite

NASA Technical Reports Server (NTRS)

Zolensky, Michael E.; Herrin, J.; Friedrich, J. M.; Rumble, D.; Steele, A.; Jenniskens, P.; Shaddad, M. H.; Le, L.; Robinson, G. A.

2009-01-01

Mineralogy & Petrography: Almahata Sitta, deriving from the asteroid 2008 TC3, is a coarse-grained- to porous, fine-grained, fragmental breccia with subrounded mineral fragments and olivine aggregates embedded in a cataclastic matrix of ureilitic material. Mineral fragments include polycrystalline olivine, low-calcium, pigeonite, and augite. Abundant carbonaceous aggregates containing graphite, microdiamonds and aliphatics. Kamacite, Cr-rich troilite, silica and schreibersite are abundant. The compositional range of the silicates is characteristic of the ureilites as a group, but unusually broad for an individual ureilite. The dense lithology is typical for ureilites, but the porous lithology is anomalous. In the porous lithology pore walls are largely coated by crystals of olivine. Classification: Almahata Sitta is an anomalous, polymict eucrite. Anomalous features include large compositional range of silicates, high abundance and large size of pores, crystalline pore wall linings, and fine-grained texture. Tomography reveals that the pores define thin, discontinuous "sheets" connected in three dimensions, suggesting that they outline grains that have been incompletely welded together. The crystals lining the pore walls are probably vapor phase deposits. Therefore Almahata Sitta may represent an agglomeration of coarse- to fine-grained, incompletely reduced pellets formed during impact, and subsequently welded together at high temperature.

Processing and Properties of Airframe Materials.

DTIC Science & Technology

1987-06-01

size to develop a composite with 61% fine grains mixed with 39% coarse grains by volume. The stack was placed inside a stainless steel vacuum bag and...alloys, considerable interest exists for superplastic forming of the alloys. However, the first order priority is to consolidate a void- free and...1o- 0 1 5 " 20 25 Oelto K. bPa (sqrt(m)) Fig. 3.3-38 Secondary cracking vs AK, forged material, as-forged, heat treatment No. 2, including load shed

Impact Damage and Erosion of Ceramics and Composites.

DTIC Science & Technology

1980-12-31

local fracture toughness, Keff’ with crack length, a, was used to determine the fracture criticality. Specifically, the fracture toughness was chosen...A complete description of strength behaviors thus requires an experimental determination of the local toughness, One of us (A. V. Virkar) is currently...34Simulated Strength - Grain Size Study Using Glass- Glass Ceramic Composite System," submitted to Journal of Materials Science, (1979). -~_ 6 I ~ -_- 0

DOE Office of Scientific and Technical Information (OSTI.GOV)

Luňáček, J., E-mail: jiri.lunacek@vsb.cz

The present paper is devoted to detailed study of the magnetically separable sorbents based on a cerium dioxide/iron oxide composite annealed at temperatures T{sub a} = 773 K, 873 K, and 973 K. The X-ray diffraction and high resolution transmission electron microscopy are used to determine the phase composition and microstructure morphology. Mössbauer spectroscopy at room (300 K) and low (5 K) temperatures has contributed to more exact identification of iron oxides and their transformations Fe{sub 3}O{sub 4} → γ-Fe{sub 2}O{sub 3} (ε-Fe{sub 2}O{sub 3}) → α-Fe{sub 2}O{sub 3} in dependence on calcination temperature. Different iron oxide phase compositions andmore » grain size distributions influence the magnetic characteristics determined from the room- and low-temperature hysteresis loop measurements. The results are supported by zero-field-cooled and field-cooled magnetization measurements allowing a quantitative estimation of the grain size distribution and its effect on the iron oxide transformations. - Highlights: •Magnetically separable sorbents based on a CeO{sub 2}/Fe{sub 2}O{sub 3} composite were investigated. •Microstructure of sorbents was determined by XRD, TEM and Mössbauer spectroscopy. •Magnetic properties were studied by hysteresis loops at room- and low-temperatures. •Phase transitions of iron oxides with increasing annealing temperature are observed.« less

Mechanical and In Vitro Biological Performance of Graphene Nanoplatelets Reinforced Calcium Silicate Composite

PubMed Central

Mehrali, Mehdi; Moghaddam, Ehsan; Seyed Shirazi, Seyed Farid; Baradaran, Saeid; Mehrali, Mohammad; Latibari, Sara Tahan; Metselaar, Hendrik Simon Cornelis; Kadri, Nahrizul Adib; Zandi, Keivan; Osman, Noor Azuan Abu

2014-01-01

Calcium silicate (CaSiO3, CS) ceramic composites reinforced with graphene nanoplatelets (GNP) were prepared using hot isostatic pressing (HIP) at 1150°C. Quantitative microstructural analysis suggests that GNP play a role in grain size and is responsible for the improved densification. Raman spectroscopy and scanning electron microscopy showed that GNP survived the harsh processing conditions of the selected HIP processing parameters. The uniform distribution of 1 wt.% GNP in the CS matrix, high densification and fine CS grain size help to improve the fracture toughness by ∼130%, hardness by ∼30% and brittleness index by ∼40% as compared to the CS matrix without GNP. The toughening mechanisms, such as crack bridging, pull-out, branching and deflection induced by GNP are observed and discussed. The GNP/CS composites exhibit good apatite-forming ability in the simulated body fluid (SBF). Our results indicate that the addition of GNP decreased pH value in SBF. Effect of addition of GNP on early adhesion and proliferation of human osteoblast cells (hFOB) was measured in vitro. The GNP/CS composites showed good biocompatibility and promoted cell viability and cell proliferation. The results indicated that the cell viability and proliferation are affected by time and concentration of GNP in the CS matrix. PMID:25229540

Structural, chemical, and isotopic microanalytical investigations of graphite from supernovae

NASA Astrophysics Data System (ADS)

Croat, T. Kevin; Bernatowicz, Thomas; Amari, Sachiko; Messenger, Scott; Stadermann, Frank J.

2003-12-01

We report the results of coordinated ion microprobe and transmission electron microscope (TEM) studies of presolar graphites from the KE3 separate (1.65-1.72 g/cm 3) of the Murchison CM2 meteorite. Isotopic analysis of individual graphites (1-12 μm) with the ion microprobe shows many to have large 18O excesses combined with large silicon isotopic anomalies, indicative of a supernova (SN) origin. Transmission electron microscopy (TEM) of ultramicrotome slices of these SN graphites revealed a high abundance (25-2400 ppm) of internal titanium carbides (TiCs), with a single graphite in some cases containing hundreds of TiCs. Isotopic compositions of individual TiCs by nanoscale resolution secondary ion mass spectrometry (NanoSIMS) confirmed their presolar origin. In addition to TiCs, composite TiC/Fe grains (TiCs with attached iron-nickel subgrains) and solitary kamacite internal grains were found. In the composite grains, the attached iron phase (kamacite [0-24 at. % Ni] or taenite [up to 60 at. % Ni]) was epitaxially grown onto one or more TiC faces. In contrast to the denser Murchison KFC1 graphites, no Zr-Ti-Mo carbides were observed. The average TiC diameters were quite variable among the SN graphites, from 30 to 232 nm, and were generally independent of the host graphite size. TiC grain morphologies ranged from euhedral to anhedral, with the grain surfaces exhibiting variable degrees of corrosion, and sometimes partially amorphous rims (3 to 15 nm thick). Partially amorphous rims of similar thickness were also observed on some solitary kamacite grains. We speculate that the rims on the internal grains are most plausibly the result of atom bombardment caused by drift of grains with respect to the ambient gas, requiring relative outflow speeds ˜100 km/s (i.e., a few percent of the SN mass outflow speed). Energy dispersive X-ray spectrometry (EDXS) of TiCs revealed significant V in solid solution, with an average V/Ti ratio over all TiCs of ˜83% of the solar value of 0.122. Significant variations about the mean V/Ti ratio were also seen among TiCs in the same graphite, likely indicating chemical equilibration with the surrounding gas over a range of temperatures. In general, the diversity in internal TiC properties suggests that TiCs formed first and had substantially diverse histories before incorporation into the graphite, implying some degree of turbulent mixing in the SN outflows. In most graphites, there is a decrease in the number density of TiCs as a function of increasing radial dis- tance, caused by either preferential depletion of TiCs from the gas or an acceleration of graphite growth with decreasing ambient temperature. In several graphites, TiCs showed a trend of larger V/Ti ratios with increasing distance from the graphite center, an indication of progressive equilibration with the surrounding gas before they were sequestered in the graphites. In all but one graphite, no trend was seen in the TiC size vs. distance from the graphite center, implying that appreciable TiC growth had effectively stopped before the graphites formed, or else that graphite growth was rapid compared to TiC growth. Taken together, the chemical variations among internal grains as well as the presence of partially amorphous rims and epitaxial Fe phases on some TiCs clearly indicate that the phase condensation sequence was TiC, followed by the iron phases (only found in some graphites) and finally graphite. Since graphite typically condenses at a higher temperature than iron at low pressures (<10 -3 bars) in a gas with C > O and otherwise solar composition, the observed condensation sequence implies a relative iron enrichment in the gas or greater supersaturation of graphite relative to iron. The TEM observations allow inferences to be made about the physical conditions in the gas from which the grains condensed. Given the TiC sizes and abundances, the gas was evidently quite dusty. From the observed TiC size range of ˜20 nm to ˜500 nm (assuming ˜1 yr growth time and T ˜ 1800°K), we infer minimum Ti number densities in the gas to be ˜7 × 10 4 to ˜2 × 10 6 atoms/cc, respectively. Although the gas composition is clearly not solar, for scale, these number densities would correspond to a pressure range of ˜0.2 μbar to ˜5.0 μbar in a gas of solar composition. They also correspond to minimum TiC grain number densities of ˜3 × 10 -4 to ˜0.2 grains/cc, assuming complete condensation of Ti in TiC. We estimate the maximum ratio of mean TiC grain separation distance in the gas to grain diameter from the Ti number densities as ˜3 × 10 5 to ˜1 × 10 6.

Effects of water deficit on breadmaking quality and storage protein compositions in bread wheat (Triticum aestivum L.).

PubMed

Zhou, Jiaxing; Liu, Dongmiao; Deng, Xiong; Zhen, Shoumin; Wang, Zhimin; Yan, Yueming

2018-03-12

Water deficiency affects grain proteome dynamics and storage protein compositions, resulting in changes in gluten viscoelasticity. In this study, the effects of field water deficit on wheat breadmaking quality and grain storage proteins were investigated. Water deficiency produced a shorter grain-filling period, a decrease in grain number, grain weight and grain yield, a reduced starch granule size and increased protein content and glutenin macropolymer contents, resulting in superior dough properties and breadmaking quality. Reverse phase ultra-performance liquid chromatography analysis showed that the total gliadin and glutenin content and the accumulation of individual components were significantly increased by water deficiency. Two-dimensional gel electrophoresis detected 144 individual storage protein spots with significant accumulation changes in developing grains under water deficit. Comparative proteomic analysis revealed that water deficiency resulted in significant upregulation of 12 gliadins, 12 high-molecular-weight glutenin subunits and 46 low-molecular-weight glutenin subunits. Quantitative real-time polymerase chain reaction analysis revealed that the expression of storage protein biosynthesis-related transcription factors Dof and Spa was upregulated by water deficiency. The present results illustrated that water deficiency leads to increased accumulation of storage protein components and upregulated expression of Dof and Spa, resulting in an improvement in glutenin strength and breadmaking quality. © 2018 Society of Chemical Industry. © 2018 Society of Chemical Industry.

Process for fabricating doped zinc oxide microsphere gel

DOEpatents

Arnold, W.D. Jr.; Bond, W.D.; Lauf, R.J.

1991-11-05

Disclosed are a new composition and method of making same for a doped zinc oxide microsphere and articles made therefrom for use in an electrical surge arrestor which has increased solid content, uniform grain size and is in the form of a gel. 4 figures.

Morphology, composition and electrical properties of SnO{sub 2}:Cl thin films grown by atomic layer deposition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cheng, Hsyi-En, E-mail: sean@mail.stust.edu.tw; Wen, Chia-Hui; Hsu, Ching-Ming

2016-01-15

Chlorine doped SnO{sub 2} thin films were prepared using atomic layer deposition at temperatures between 300 and 450 °C using SnCl{sub 4} and H{sub 2}O as the reactants. Composition, structure, surface morphology, and electrical properties of the as-deposited films were examined. Results showed that the as-deposited SnO{sub 2} films all exhibited rutile structure with [O]/[Sn] ratios between 1.35 and 1.40. The electrical conductivity was found independent on [O]/[Sn] ratio but dependent on chlorine doping concentration, grain size, and surface morphology. The 300 °C-deposited film performed a higher electrical conductivity of 315 S/cm due to its higher chlorine doping level, larger grain size, andmore » smoother film surface. The existence of Sn{sup 2+} oxidation state was demonstrated to minimize the effects of chlorine on raising the electrical conductivity of films.« less

Bonding of TRIP-Steel/Al2O3-(3Y)-TZP Composites and (3Y)-TZP Ceramic by a Spark Plasma Sintering (SPS) Apparatus

PubMed Central

Miriyev, Aslan; Grützner, Steffen; Krüger, Lutz; Kalabukhov, Sergey; Frage, Nachum

2016-01-01

A combination of the high damage tolerance of TRIP-steel and the extremely low thermal conductivity of partially stabilized zirconia (PSZ) can provide controlled thermal-mechanical properties to sandwich-shaped composite specimens comprising these materials. Sintering the (TRIP-steel-PSZ)/PSZ sandwich in a single step is very difficult due to differences in the sintering temperature and densification kinetics of the composite and the ceramic powders. In the present study, we successfully applied a two-step approach involving separate SPS consolidation of pure (3Y)-TZP and composites containing 20 vol % TRIP-steel, 40 vol % Al2O3 and 40 vol % (3Y)-TZP ceramic phase, and subsequent diffusion joining of both sintered components in an SPS apparatus. The microstructure and properties of the sintered and bonded specimens were characterized. No defects at the interface between the TZP and the composite after joining in the 1050–1150 °C temperature range were observed. Only limited grain growth occurred during joining, while crystallite size, hardness, shear strength and the fraction of the monoclinic phase in the TZP ceramic virtually did not change. The slight increase of the TZP layer’s fracture toughness with the joining temperature was attributed to the effect of grain size on transformation toughening. PMID:28773680

Detailed Study of BSA Adsorption on Micro- and Nanocrystalline Diamond/β-SiC Composite Gradient Films by Time-Resolved Fluorescence Microscopy.

PubMed

Handschuh-Wang, Stephan; Wang, Tao; Druzhinin, Sergey I; Wesner, Daniel; Jiang, Xin; Schönherr, Holger

2017-01-24

The adsorption of bovine serum albumin (BSA) on micro- and nanocrystalline diamond/β-SiC composite films synthesized using the hot filament chemical vapor deposition (HFCVD) technique has been investigated by confocal fluorescence lifetime imaging microscopy. BSA labeled with fluorescein isothiocyanate (FITC) was employed as a probe. The BSA FITC conjugate was found to preferentially adsorb on both O-/OH-terminated microcrystalline and nanocrystalline diamond compared to the OH-terminated β-SiC, resulting in an increasing amount of BSA adsorbed to the gradient surfaces with an increasing diamond/β-SiC ratio. The different strength of adsorption (>30 times for diamond with a grain size of 570 nm) coincides with different surface energy parameters and differing conformational changes upon adsorption. Fluorescence data of the adsorbed BSA FITC on the gradient film with different diamond coverage show a four-exponential decay with decay times of 3.71, 2.54, 0.66, and 0.13 ns for a grain size of 570 nm. The different decay times are attributed to the fluorescence of thiourea fluorescein residuals of linked FITC distributed in BSA with different dye-dye and dye-surface distances. The longest decay time was found to correlate linearly with the diamond grain size. The fluorescence of BSA FITC undergoes external dynamic fluorescence quenching on the diamond surface by H- and/or sp 2 -defects and/or by amorphous carbon or graphite phases. An acceleration of the internal fluorescence concentration quenching in BSA FITC because of structural changes of albumin due to adsorption, is concluded to be a secondary contributor. These results suggest that the micro- and nanocrystalline diamond/β-SiC composite gradient films can be utilized to spatially control protein adsorption and diamond crystallite size, which facilitates systematic studies at these interesting (bio)interfaces.

ChemCam Compositional Results from the Shaler Outcrop in Gale Crater, Mars (Invited)

NASA Astrophysics Data System (ADS)

Anderson, R. B.; Leveille, R. J.; Vaniman, D.; Williams, J.; Clegg, S. M.; Le Mouelic, S.; Wiens, R. C.; Edgar, L. A.; Newsom, H. E.; Clark, B. C.; Ollila, A.; Lewis, K. W.; Gupta, S.; Team, M.

2013-12-01

The Curiosity rover first visited the outcrop known as 'Shaler' on Sol 121 of the mission. The ~1 m thick outcrop is the 'type section' for the Shaler member, which forms the uppermost part of the Yellowknife Bay formation. The Shaler outcrop exhibits multiple well-exposed cross-bedded facies with typical grain sizes of 1-2 mm, most consistent with fluvial deposition. Initial results from the two Sol 121 observations of Shaler by the ChemCam instrument showed similar composition, with a mix of mafic silicates and feldspar grains. A strong correlation between iron and titanium indicates the possible presence of titanomagnetite or ilmenite. CaO shows an anticorrelation with the total of the measured major elements, suggesting that it may be related to a non-silicate phase such as a salt. The rover returned to the outcrop on Sols 309-324. Because of the rugged nature of the outcrop, much of the exposed rock was not reachable by the rover's robotic arm. However, the ChemCam instrument can collect elemental compositional information out to a range of ~7 m using laser-induced breakdown spectroscopy (LIBS), and can acquire high-resolution images at even greater range. ChemCam analyzed 29 locations using LIBS to determine chemical composition, and four additional locations were imaged with the Remote Micro Imager. The targets analyzed included both fine- and coarse-grained facies, as well as a distinct upper unit which appears darker and less red than other Shaler units in Mastcam images, and lacks the striking alternating resistant and recessive cross-bedding observed in lower Shaler. This upper unit occurs at an elevation similar to the rocks at 'Rocknest', and similar-looking rocks appear across the cratered surface to the south and east of Shaler. Several blocks apparently derived from this upper unit were analyzed by ChemCam to test the hypothesis that the unit is related to rocks observed at Rocknest. Work is ongoing to interpret the results of the ChemCam campaign at Shaler. This work includes localization of individual laser analysis points to relate fine-scaled texture and grain size to chemical compositions, analysis of detectable minor and trace elements, identification of compositional trends related to facies type, comparison with compositions of other stratigraphic units in Gale crater, and chemical classification based on terrestrial sedimentary geochemistry.

Holocene water mass history off NE Greenland - A first high-resolution sediment record from the western Fram Strait

NASA Astrophysics Data System (ADS)

Zehnich, Marc; Palme, Tina; Spielhagen, Robert F.; Hass, H. Christian; Bauch, Henning A.

2017-04-01

While the Holocene history of the eastern Fram Strait seems well investigated, no high-resolution paleoenvironmental records were available from the western Fram Strait so far. A new sedimentary record, obtained during expedition PS93.1 (2015) of RV Polarstern on the outermost NE Greenland shelf, allows for the first time to reconstruct Holocene changes in near-surface salinities, temperature, stratification and water masses (polar waters vs. Atlantic Water), potentially related to variations of the freshwater and sea ice export from the Arctic Ocean. The 260 cm long sedimentary record from site PS93/025 (80.5°N, 8.5°W) was investigated for sediment composition, foraminifer contents, grain size variations (sortable silt) and the isotopic composition of planktic foraminifers. Radiocarbon datings reveal an age of 10.2 cal-ka for the core base and continuous sedimentation throughout most of the Holocene. The sediments are generally very fine-grained (<2% sand). The grain size record reveals a fining-upwards trend and sediments from <6.5 cal-ka consist of <0.5% coarse fraction. A comparison of foraminifer and coarse fraction abundances shows strong similarities. Apparently the contribution of coarse terrestrial material from iceberg transport was extremely low throughout the last 10.2 cal-ka. Foraminifer abundances (both planktic and benthic) are high in Early Holocene sediments until ca. 7 cal-ka and decrease rapidly thereafter. This is interpreted to reflect a relatively strong advection of Atlantic Water to the NW Fram Strait, which correlates well with similar findings on the eastern side of the Arctic Gateway. Sortable silt grain sizes are high (27-32 µm) in the older part of the record and gradually decrease between 7 cal-ka and 4 cal-ka. After ca. 4 cal-ka, sortable silt shows values of 20-22 µm and little variation. Considering also the grain-size distribution curves, we propose a decline of bottom current velocities on the outer NE Greenland shelf after 7 cal-ka, related to a decrease of Atlantic Water advection. These preliminary results reveal a strong coupling of Holocene environments on both sides of the Fram Strait.

Tailoring Magnetic Properties in Bulk Nanostructured Solids

NASA Astrophysics Data System (ADS)

Morales, Jason Rolando

Important magnetic properties and behaviors such as coercivity, remanence, susceptibility, energy product, and exchange coupling can be tailored by controlling the grain size, composition, and density of bulk magnetic materials. At nanometric length scales the grain size plays an increasingly important role since magnetic domain behavior and grain boundary concentration determine bulk magnetic behavior. This has spurred a significant amount of work devoted to developing magnetic materials with nanometric features (thickness, grain/crystallite size, inclusions or shells) in 0D (powder), 1D (wires), and 2D (thin films) materials. Large 3D nanocrystalline materials are more suitable for many applications such as permanent magnets, magneto-optical Faraday isolators etc. Yet there are relatively few successful demonstrations of 3D magnetic materials with nanoscale influenced properties available in the literature. Making dense 3D bulk materials with magnetic nanocrystalline microstructures is a challenge because many traditional densification techniques (HIP, pressureless sintering, etc.) move the microstructure out of the "nano" regime during densification. This dissertation shows that the Current Activated Pressure Assisted Densification (CAPAD) method, also known as spark plasma sintering, can be used to create dense, bulk, magnetic, nanocrystalline solids with varied compositions suited to fit many applications. The results of my research will first show important implications for the use of CAPAD for the production of exchange-coupled nanocomposite magnets. Decreases in grain size were shown to have a significant role in increasing the magnitude of exchange bias. Second, preferentially ordered bulk magnetic materials were produced with highly anisotropic material properties. The ordered microstructure resulted in changing magnetic property magnitudes (ex. change in coercivity by almost 10x) depending on the relative orientation (0° vs. 90°) of an externally applied magnetic field to the sample. Third, a dense magneto-optical material (rare earth oxide) was produced that rotates transmitted polarized light under an externally applied magnetic field, called the Faraday Effect. The magnitude of the rare earth oxide Faraday Effect surpasses that of the current market leader (terbium gallium garnet) in Faraday isolators by ˜2.24x.

Oxygen and Magnesium Isotopic Compositions of Asteroidal Materials Returned from Itokawa by the Hayabusa Mission

NASA Technical Reports Server (NTRS)

Yurimoto, H; Abe, M.; Ebihara, M.; Fujimura, A.; Hashizume, K.; Ireland, T. R.; Itoh, S.; Kawaguchi, K.; Kitajima, F.; Mukai, T.;

Patterned solid state growth of barium titanate crystals

NASA Astrophysics Data System (ADS)

Ugorek, Michael Stephen

An understanding of microstructure evolution in ceramic materials, including single crystal development and abnormal/enhanced grain growth should enable more controlled final ceramic element structures. In this study, two different approaches were used to control single crystal development in a patterned array. These two methods are: (1) patterned solid state growth in BaTiO 3 ceramics, and (2) metal-mediated single crystal growth in BaTiO 3. With the patterned solid state growth technique, optical photolithography was used to pattern dopants as well as [001] and [110] BaTiO3 single crystal template arrays with a 1000 microm line pattern array with 1000 microm spacings. These patterns were subsequently used to control the matrix grain growth evolution and single crystal development in BaTiO3. It was shown that the growth kinetics can be controlled by a small initial grain size, atmosphere conditions, and the introduction of a dopant at selective areas/interfaces. By using a PO2 of 1x10-5 atm during high temperature heat treatment, the matrix coarsening has been limited (to roughly 2 times the initial grain size), while retaining single crystal boundary motion up to 0.5 mm during growth for dwell times up to 9 h at 1300°C. The longitudinal and lateral growth rates were optimized at 10--15 microm/h at 1300°C in a PO2 of 1x10 -5 atm for single crystal growth with limited matrix coarsening. Using these conditions, a patterned microstructure in BaTiO3 was obtained. With the metal-mediated single crystal growth technique, a novel approach for fabricating 2-2 single crystal/polymer composites with a kerf < 5 microns was demonstrated. Surface templated grain growth was used to propagate a single crystal interface into a polycrystalline BaTiO3 or Ba(Zr0.05 Ti0.95)O3 matrix with lamellar nickel layers. The grain growth evolution and texture development were studied using both [001] and [110] BaTiO3 single crystals templates. By using a PO 2 of 1x10-11 atm during high temperature heat treatment, matrix coarsening was limited while enabling single crystal boundary motion up to 0.35 mm during growth between 1250°C and 1300°C with growth rates ˜ 3--4 microm/h for both single crystal orientations. By removing the inner electrodes, 2-2 single crystal (or ceramic) composites were prepared. The piezoelectric and dielectric properties of the composites of the two compositions were measured. The d33 and d31 of the composites were similar to the polycrystalline ceramic of the same composition.

Lake Sediment Particle Size Analysis for Holocene Paleoenvironmental Study of Steens Mountain, Eastern Oregon

NASA Astrophysics Data System (ADS)

Morris, J.; Stoner, J. S.; Reilly, B. T.; Hatfield, R. G.; Konyndyk, D.; Abbott, M. B.; Finkenbinder, M. S.; Hillman, A. L.

2016-12-01

In order to better understand climate trends in the late Pleistocene and Holocene in southeast Oregon, we present a sedimentological analysis of Fish Lake, Harney County, Oregon. Fish Lake (42° 44' 15" N, 118° 38' 57" W, 2,246.7 m) sits on the west slope of Steens Mountain, a fault-block mountain of Miocene basalt, adjacent to a glacial moraine. The present environment is high desert with sub alpine steppe vegetation, receiving approximately 12" of precipitation annually. The lake was cored in August 2013 with a series of overlapping drives, correlated by six distinct tephra and magnetic susceptibility. The composite section provides a 7.5 m continuous record of at least the last 13 ka, constrained by an age model built with 13 terrestrial macrofossil 14C dates. The recovered sediments, consisting of fine terrigenous and biogenous material in varying proportions, were analyzed with computed tomography (CT) scans, x-ray fluorescence (XRF) scans, magnetic measurements, loss on ignition (LOI), and sediment grain-size. CT and LOI data reveal a low density, high organic interval in the early Holocene ( 8.5-11 ka) with relatively coarse and well-sorted grain-size, suggesting an extended period of low lake level and low precipitation. Sediment grain-sizes are variable through the middle and late Holocene with high amplitude longer period features from 3 ka to the present. We investigate these grain-size fluctuations in the context of regional Holocene records.

Size and density sorting of dust grains in SPH simulations of protoplanetary discs

NASA Astrophysics Data System (ADS)

Pignatale, F. C.; Gonzalez, J.-F.; Cuello, Nicolas; Bourdon, Bernard; Fitoussi, Caroline

2017-07-01

The size and density of dust grains determine their response to gas drag in protoplanetary discs. Aerodynamical (size × density) sorting is one of the proposed mechanisms to explain the grain properties and chemical fractionation of chondrites. However, the efficiency of aerodynamical sorting and the location in the disc in which it could occur are still unknown. Although the effects of grain sizes and growth in discs have been widely studied, a simultaneous analysis including dust composition is missing. In this work, we present the dynamical evolution and growth of multicomponent dust in a protoplanetary disc using a 3D, two-fluid (gas+dust) smoothed particle hydrodynamics code. We find that the dust vertical settling is characterized by two phases: a density-driven phase that leads to a vertical chemical sorting of dust and a size-driven phase that enhances the amount of lighter material in the mid-plane. We also see an efficient radial chemical sorting of the dust at large scales. We find that dust particles are aerodynamically sorted in the inner disc. The disc becomes sub-solar in its Fe/Si ratio on the surface since the early stage of evolution but sub-solar Fe/Si can be also found in the outer disc-mid-plane at late stages. Aggregates in the disc mimic the physical and chemical properties of chondrites, suggesting that aerodynamical sorting played an important role in determining their final structure.

Deformation of olivine during phase transformation to wadsleyite

NASA Astrophysics Data System (ADS)

Mohiuddin, A.; Girard, J.; Karato, S. I.

2017-12-01

The strength of subducting slabs in the transition zone is critical in controlling the style of mantle convection. However, rheological properties of a subducted slab are elusive: low temperatures of a slab would make slabs strong, but in many regions there is evidence of intense deformation of slabs in the transition zone. One potential cause of intense deformation of subducting slabs is grain size reduction and accompanied microstructural changes during phase transformation of olivine to its higher-pressure polymorphs. There have been no experimental studies to quantify the influence of grain-size evolution. In addition to grain size reduction, distribution of small grains during phase transformation governs the degree of weakening during phase transformation (for e.g. load bearing framework vs. inter-connected layered framework). We conducted laboratory studies on the size and spatial distribution of new grains of wadsleyite after the transformation from olivine. Our results under static conditions show that an interconnected microstructure develops during the initial stage of phase transformation and that the grain size of the interconnected phase (wadsleyite) depends on the temperature at which the phase transformation occurs (smaller grains at lower temperatures). Development of an interconnected microstructure may lead to strain localization in the weaker phase, i.e. the fine-grained interconnected network accommodates most of the strain and therefore weakening of the entire composite. We will test this model through a series of two synchrotron in-situ deformation experiments: (i) Olivine aggregate will be deformed during slow pressure increase from deep upper mantle pressure ( 10 GPa) to transition zone pressure ( 15 GPa) at a given temperature simulating the deformation of a slab penetrating into the transition zone (ii) olivine is partially transformed to wadsleyite in a multi anvil apparatus at Yale and will be deformed within the stability field where olivine and wadsleyite coexist. We will use the Rotational Drickamer Apparatus (RDA) at a synchrotron facility (Argonne National Lab, 6-BM-B beamline, white beam and x-ray radiography) and characterize the stresses acting on olivine and wadsleyite during such simulations. We plan to present our preliminary results.

Size Matters: FTIR Spectral Analysis of Apollo Regolith Samples Exhibits Grain Size Dependence.

NASA Astrophysics Data System (ADS)

Martin, Dayl; Joy, Katherine; Pernet-Fisher, John; Wogelius, Roy; Morlok, Andreas; Hiesinger, Harald

2017-04-01

The Mercury Thermal Infrared Spectrometer (MERTIS) on the upcoming BepiColombo mission is designed to analyse the surface of Mercury in thermal infrared wavelengths (7-14 μm) to investigate the physical properties of the surface materials [1]. Laboratory analyses of analogue materials are useful for investigating how various sample properties alter the resulting infrared spectrum. Laboratory FTIR analysis of Apollo fine (<1mm) soil samples 14259,672, 15401,147, and 67481,96 have provided an insight into how grain size, composition, maturity (i.e., exposure to space weathering processes), and proportion of glassy material affect their average infrared spectra. Each of these samples was analysed as a bulk sample and five size fractions: <25, 25-63, 63-125, 125-250, and <250 μm. Sample 14259,672 is a highly mature highlands regolith with a large proportion of agglutinates [2]. The high agglutinate content (>60%) causes a 'flattening' of the spectrum, with reduced reflectance in the Reststrahlen Band region (RB) as much as 30% in comparison to samples that are dominated by a high proportion of crystalline material. Apollo 15401,147 is an immature regolith with a high proportion of volcanic glass pyroclastic beads [2]. The high mafic mineral content results in a systematic shift in the Christiansen Feature (CF - the point of lowest reflectance) to longer wavelength: 8.6 μm. The glass beads dominate the spectrum, displaying a broad peak around the main Si-O stretch band (at 10.8 μm). As such, individual mineral components of this sample cannot be resolved from the average spectrum alone. Apollo 67481,96 is a sub-mature regolith composed dominantly of anorthite plagioclase [2]. The CF position of the average spectrum is shifted to shorter wavelengths (8.2 μm) due to the higher proportion of felsic minerals. Its average spectrum is dominated by anorthite reflectance bands at 8.7, 9.1, 9.8, and 10.8 μm. The average reflectance is greater than the other samples due to a lower proportion of glassy material. In each soil, the smallest fractions (0-25 and 25-63 μm) have CF positions 0.1-0.4 μm higher than the larger grain sizes. Also, the bulk-sample spectra mostly closely resemble the 0-25 μm sieved size fraction spectrum, indicating that this size fraction of each sample dominates the bulk spectrum regardless of other physical properties. This has implications for surface analyses of other Solar System bodies where some mineral phases or components could be concentrated in a particular size fraction. For example, the anorthite grains in 67481,96 are dominantly >25 μm in size and therefore may not contribute proportionally to the bulk average spectrum (compared to the <25 μm fraction). The resulting bulk spectrum of 67481,96 has a CF position 0.2 μm higher than all size fractions >25 microns and therefore does not represent a true average composition of the sample. Further investigation of how grain size and composition alters the average spectrum is required to fully understand infrared spectra of planetary surfaces. [1] - Hiesinger H., Helbert J., and MERTIS Co-I Team. (2010). The Mercury Radiometer and Thermal Infrared Spectrometer (MERTIS) for the BepiColombo Mission. Planetary and Space Science. 58, 144-165. [2] - NASA Lunar Sample Compendium. https://curator.jsc.nasa.gov/lunar/lsc/

Muddled or mixed? Inferring palaeoclimate from size distributions of deep-sea clastics

NASA Astrophysics Data System (ADS)

Weltje, G. J.; Prins, M. A.

2003-04-01

One of the outstanding problems of palaeoclimate reconstruction from physico-chemical properties of terrigenous deep-sea sediments is the fact that most basin fills are mixtures of sediment populations derived from different sources and transported to the site of deposition by different mechanisms. Conventional approaches to palaeoclimate reconstruction from deep-sea sediments, which ignore this common fact, often fail to recognise the true significance of variations in sediment properties. We formulate a set of requirements that each proposed palaeoenvironmental indicator should fulfil, and focus on the intrinsic coupling between grain size and chemical composition. A critical review of past achievements in grain-size analysis is given to provide a starting point for a conceptual model of spatio-temporal grain-size variation in terms of dynamic populations. Each dynamic population results from a characteristic combination of production and transport mechanisms that corresponds to a distinct subpopulation in the data analysed. The mathematical-statistical equivalent of the conceptual model may be solved by means of the end-member modelling algorithm EMMA. Applications of the model to several ocean basins are discussed, as well as methods to examine the validity of the palaeoclimate reconstructions.

Investigation of the recycling of tires to elastomeric requirements by techniques of thermal compression

NASA Astrophysics Data System (ADS)

Nadal Gisbert, Antonio V.

In this work is investigated the recycling of tires to elastomeric requirements by thermal compression. The production of recycled products is carried out starting from the powder, of elastomeric nature, coming from the grinding of used tires denominated GTR (Ground Tire Rubber) of different grain size, although the fundamental objective is the recycling of powder of 0,2mm grain size. The process of forming used for obtaining the recycled product is thermal compression, due to its simplicity and low cost. The composition of the powder has been analyzed and also the influence, on the elastomeric characteristics of the recycled product, of different parameters: Grain size, compact pressure, temperature, time, thickness of the recycled product and combination of sizes. At last we give an hypothesis that justifies the mechanism that gives cohesion to the powder GTR and allows their recycling. We also have carried out an analysis of the investigation lines, at the present, on the recycling of tires in general and an economic study of the viability of the recycled product in front of present products in the market, agglomerated with polyurethane, that have their application in using it in different types of floors.

Methods for providing ceramic matrix composite components with increased thermal capacity

NASA Technical Reports Server (NTRS)

Steibel, James Dale (Inventor); Utah, David Alan (Inventor)

2001-01-01

A method for enhancing the cooling capability of a turbine component made from a ceramic matrix composite. The method improves the thermal performance of the component by producing a surface having increased cooling capacity, thereby allowing the component to operate at a higher temperature. The method tailors the available surface area on the cooling surface of the composite component by depositing a particulate layer of coarse grained ceramic powders of preselected size onto the surface of the ceramic matrix composite component. The size of the particulate is selectively tailored to match the desired surface finish or surface roughness of the article. The article may be designed to have different surface finishes for different locations, so that the application of different sized powders can provide different cooling capabilities at different locations, if desired. The compositions of the particulates are chemically compatible with the ceramic material comprising the outer surface or portion of the ceramic matrix composite. The particulates are applied using a slurry and incorporated into the article by heating to an elevated temperature without melting the matrix, the particulates or the fiber reinforcement.

Mineralogical and chemical properties of the lunar regolith

NASA Astrophysics Data System (ADS)

McKay, D. S.; Ming, D. W.

The composition of lunar regolith and its attendant properties are discussed. Tables are provided listing lunar minerals, the abundance of plagioclase feldspar, pyroxene, olivine, and ilmenite in lunar materials, typical compositions of common lunar minerals, and cumulative grain-size distribution for a large number of lunar soils. Also provided are charts on the chemistry of breccias, the chemistry of lunar glass, and the comparative chemistry of surface soils for the Apollo sites. Lunar agglutinates, constructional particles made of lithic, mineral, and glass fragments welded together by a glassy matrix containing extremely fine-grained metallic iron and formed by micrometeoric impacts at the lunar surface, are discussed. Crystalline, igneous rock fragments, breccias, and lunar glass are examined. Volatiles implanted in lunar materials and regolith maturity are also addressed.

Mineralogical and chemical properties of the lunar regolith

NASA Technical Reports Server (NTRS)

Mckay, David S.; Ming, Douglas W.

1989-01-01

The composition of lunar regolith and its attendant properties are discussed. Tables are provided listing lunar minerals, the abundance of plagioclase feldspar, pyroxene, olivine, and ilmenite in lunar materials, typical compositions of common lunar minerals, and cumulative grain-size distribution for a large number of lunar soils. Also provided are charts on the chemistry of breccias, the chemistry of lunar glass, and the comparative chemistry of surface soils for the Apollo sites. Lunar agglutinates, constructional particles made of lithic, mineral, and glass fragments welded together by a glassy matrix containing extremely fine-grained metallic iron and formed by micrometeoric impacts at the lunar surface, are discussed. Crystalline, igneous rock fragments, breccias, and lunar glass are examined. Volatiles implanted in lunar materials and regolith maturity are also addressed.

Nitrogen Isotopic Anomalies in a Hydrous Interplanetary Dust Particle

NASA Technical Reports Server (NTRS)

Smith, J. B.; Dai, Z. R.; Weber, P. K.; Graham, G. A.; Hutcheon, I. D.; Bajt, S.; Ishii, H.; Bradley, J. P.

2005-01-01

Interplanetary dust particles (IDPs) collected in the stratosphere are the fine-grained end member (5 - 50 microns in size) of the meteoritic material available for investigation in the laboratory. IDPs are derived from either cometary or asteroidal sources. Some IDPs contain cosmically primitive materials with isotopic signatures reflecting presolar origins. Recent detailed studies using the NanoSIMS have shown there is a wide variation of isotopic signatures within individual IDPs; grains with a presolar signature have been observed surrounded by material with a solar isotopic composition. The majority of IDPs studied have been anhydrous. We report here results from integrated NanoSIMS/FIB/TEM/Synchrotron IR studies of a hydrous IDP, focused on understanding the correlations between the isotopic, mineralogical and chemical compositions of IDPs.

Using ICP and micro-PIXE to investigate possible differences in the mineral composition of genetically modified versus wild-type sorghum grain

NASA Astrophysics Data System (ADS)

Ndimba, R.; Cloete, K.; Mehlo, L.; Kossmann, J.; Mtshali, C.; Pineda-Vargas, C.

2017-08-01

In the present study, possible differences in the mineral composition of transgenic versus non-transgenic sorghum grains were investigated using inductively coupled atomic emission spectroscopy (ICP-AES); and, in-tissue elemental mapping by micro Proton-Induced X-ray Emission (micro-PIXE) analysis. ICP AES was used to analyse the bulk mineral content of the wholegrain flour derived from each genotype; whilst micro-PIXE was used to interrogate localised differences in mineral composition specific to certain areas of the grain, such as the bran layer and the central endosperm tissue. According to the results obtained, no significant difference in the average Fe, Zn or Ca content was found to differentiate the transgenic from the wild-type grain using ICP-AES. However, using micro-PIXE, a significant reduction in zinc could be detected in the bran layer of the transgenic grains relative to wild-type. Although it is difficult to draw firm conclusions, as a result of the small sample size used in this study, micro-PIXE has nonetheless proven itself as a useful technique for highlighting the possibility that there may be reduced levels of zinc accumulation in the bran layer of the transgenic grains. Given that the genetic modification targets proteins that are highly concentrated in certain parts of the bran tissue, it seems plausible that the reduced levels of zinc may be an unintended consequence of the silencing of kafirin proteins. Although no immediate health or nutritional concerns emerge from this preliminary finding, it is noted that zinc plays an important biological role within this part of the grain as a structural stabiliser and antioxidant factor. Further study is therefore needed to assess more definitively the extent of the apparent localised reduction in zinc in the transgenic grains and how this may affect other important grain quality characteristics.

Floral display size, conspecific density and florivory affect fruit set in natural populations of Phlox hirsuta, an endangered species

PubMed Central

Ruane, Lauren G.; Rotzin, Andrew T.; Congleton, Philip H.

2014-01-01

Background and Aims Natural variation in fruit and seed set may be explained by factors that affect the composition of pollen grains on stigmas. Self-incompatible species require compatible outcross pollen grains to produce seeds. The siring success of outcross pollen grains, however, can be hindered if self (or other incompatible) pollen grains co-occur on stigmas. This study identifies factors that determine fruit set in Phlox hirsuta, a self-sterile endangered species that is prone to self-pollination, and its associated fitness costs. Methods Multiple linear regressions were used to identify factors that explain variation in percentage fruit set within three of the five known populations of this endangered species. Florivorous beetle density, petal colour, floral display size, local conspecific density and pre-dispersal seed predation were quantified and their effects on the ability of flowers to produce fruits were assessed. Key Results In all three populations, percentage fruit set decreased as florivorous beetle density increased and as floral display size increased. The effect of floral display size on fruit set, however, often depended on the density of nearby conspecific plants. High local conspecific densities offset – even reversed – the negative effects of floral display size on percentage fruit set. Seed predation by mammals decreased fruit set in one population. Conclusions The results indicate that seed production in P. hirsuta can be maximized by selectively augmenting populations in areas containing isolated large plants, by reducing the population sizes of florivorous beetles and by excluding mammals that consume unripe fruits. PMID:24557879

High efficiency low cost thin film silicon solar cell design and method for making

DOEpatents

Sopori, B.L.

1999-04-27

A semiconductor device is described having a substrate, a conductive intermediate layer deposited onto said substrate, wherein the intermediate layer serves as a back electrode, an optical reflector, and an interface for impurity gettering, and a semiconductor layer deposited onto said intermediate layer, wherein the semiconductor layer has a grain size at least as large as the layer thickness, and preferably about ten times the layer thickness. The device is formed by depositing a metal layer on a substrate, depositing a semiconductive material on the metal-coated substrate to produce a composite structure, and then optically processing the composite structure by illuminating it with infrared electromagnetic radiation according to a unique time-energy profile that first produces pits in the backside surface of the semiconductor material, then produces a thin, highly reflective, low resistivity alloy layer over the entire area of the interface between the semiconductor material and the metal layer, and finally produces a grain-enhanced semiconductor layer. The time-energy profile includes increasing the energy to a first energy level to initiate pit formation and create the desired pit size and density, then ramping up to a second energy level in which the entire device is heated to produce an interfacial melt, and finally reducing the energy to a third energy level and holding for a period of time to allow enhancement in the grain size of the semiconductor layer. 9 figs.

Pb2+ and Zn2+ adsorption by a natural aluminum- and iron-bearing surface coating on an aquifer sand

USGS Publications Warehouse

Coston, J.A.; Fuller, C.C.; Davis, J.A.

1995-01-01

Pb2+ and Zn2+ adsorption was studied in batch experiments with material collected from a shallow, unconfined aquifer of glacial outwash sand and gravel in Falmouth, Massachusetts, USA. The aquifer solids contain primarily quartz with minor amounts of alkali feldspars and ferromagnetic minerals. Pb2+ and Zn2+ adsorption experiments with various grain size and mineral fractions of the aquifer solids showed that: 1) Zn2+ adsorption was independent of grain size, but Pb2+ was preferentially adsorbed by the <64 ??m size fraction and 2) Pb2+ adsorption decreased after removal of the paramagnetic, Fe-bearing mineral fraction, but Zn2+ adsorption was unaffected. Pb2+ and Zn2+ adsorption on mineral separates from the aquifer material compared with metal adsorption on a purified quartz powder indicated that adsorption of both metal ions was dominated by coatings on the quartz fraction of the sediment. Characterization of the coatings by AES, SEM-EDS, and TOF-SIMS demonstrated that the natural quartz grains were extensively coated with Al- and Fe-bearing minerals of variable composition. -from Authors

Development of Bulk Nanocrystalline Tungsten Alloys for Fusion Reactor Structures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fang, Zhigang Zak

This project developed a technology for manufacturing bulk ultrafine tungsten materials that are at or near full density for fusion reactor structural applications, aiming to improve ductility and toughness of tungsten before and after irradiation. The project involved the development of fabrication processes for making bulk ultrafine grained W, the development of new alloys of ultrafine grained W and evaluations of properties of these specific materials. The goal of this fabrication process is to produce fully dense bulk W with ultrafine grain sizes, with uniform distributions of grain size and additives. To date there is no known process that couldmore » be used to make ultrafine grained tungsten in a fully dense state and in a cost-acceptable fashion. The specific technology described in this proposal for making ultrafine grained tungsten involves a suite of nano-particle processing and sintering techniques. The program also developed new alloys of ultrafine grained W, e.g. W-(Ta,V,Ti)-TiC alloys to improve ductility and toughness before and after irradiation. By completing this project, we achieved the following objectives: • Demonstrated experimentally the feasibility of producing bulk ultrafine grained tungsten alloys (at or near 100% dense, <1000 nm grain size) using the proposed process • Demonstrated the proposed ultrafine grained W alloys, namely, W-(Ta, V, Ti)-TiC, can indeed be made using the proposed process • Demonstrated that the properties of nano tungsten alloys meet the requirements for fusion reactor applications. The overall goal was to harness the potential of ultrafine grained W produced using the proposed processes as the core structural materials for future fusion reactors. The project was very successful overall, meeting all milestones and surpassing project goals in terms of process development and material’s blistering resistance properties. A novel process similar to the conventional press-and-sinter powder metallurgy method was developed for producing ultrafine grain tungsten from nanosize tungsten powders. Grain growth was significantly controlled during sintering by certain alloy compositions, particularly Ti, and most compositions sintered to maximum densification. To optimize this process, the effect of processing parameters on the densification and grain growth of nano-W powders was investigated. Near-fully densified tungsten was obtained at sintering temperatures between 1100 and 1300 °C, and both Ar and H2 sintering atmospheres were investigated. The Ar sintering atmosphere was determined to more favorably promote densification and minimize grain growth. The nanosized tungsten powder compacts were subjected to reduction in H2 as a part of the sintering cycle. The reduction temperature was found to have significant effects on the sintering of nano-W powder, primarily as a result of grain coarsening, which was seen at temperatures as low as 700 °C. In an effort to inhibit grain growth, the effect of Ti-based additives on the densification and grain growth of nano-W powders was investigated in this project. The addition of 1 wt.% Ti into tungsten led to more than a 63% decrease in average grain size of sintered samples at comparable density levels. Compared to conventional high temperature sintering, a lower temperature sintering cycle for a longer hold time resulted in both near-full density and fine grain size. The roles of the Ti additives include not only the inhibition of grain growth, but also the potential absorption of oxygen from W particles. The project has resulted in the publication; thus far, of six peer reviewed journal articles and seven conference presentations, as well as a master’s thesis. Two additional journal articles are currently in preparation. Presentations and articles were a particular focus of the second half of the project, once significant experimentation had been performed and analyzed. As part of our efforts to disseminate information of our results, the W research teams with Prof. Fang had a strong presence at multiple international conferences during 2015 and 2016. Several research groups in the US are now performing experiments using the ultrafine grained W materials.« less

Dispersal of Volcanic Ash on Mars: Ash Grain Shape Analysis

NASA Astrophysics Data System (ADS)

Langdalen, Z.; Fagents, S. A.; Fitch, E. P.

2017-12-01

Many ash dispersal models use spheres as ash-grain analogs in drag calculations. These simplifications introduce inaccuracies in the treatment of drag coefficients, leading to inaccurate settling velocities and dispersal predictions. Therefore, we are investigating the use of a range of shape parameters, calculated using grain dimensions, to derive a better representation of grain shape and effective grain cross-sectional area. Specifically, our goal is to apply our results to the modeling of ash deposition to investigate the proposed volcanic origin of certain fine-grained deposits on Mars. Therefore, we are documenting the dimensions and shapes of ash grains from terrestrial subplinian to plinian deposits, in eight size divisions from 2 mm to 16 μm, employing a high resolution optical microscope. The optical image capture protocol provides an accurate ash grain outline by taking multiple images at different focus heights prior to combining them into a composite image. Image composite mosaics are then processed through ImageJ, a robust scientific measurement software package, to calculate a range of dimensionless shape parameters. Since ash grains rotate as they fall, drag forces act on a changing cross-sectional area. Therefore, we capture images and calculate shape parameters of each grain positioned in three orthogonal orientations. We find that the difference between maximum and minimum aspect ratios of the three orientations of a given grain best quantifies the degree of elongation of that grain. However, the average aspect ratio calculated for each grain provides a good representation of relative differences among grains. We also find that convexity provides the best representation of surface irregularity. For both shape parameters, natural ash grains display notably different shape parameter values than sphere analogs. Therefore, Mars ash dispersal modeling that incorporates shape parameters will provide more realistic predictions of deposit extents because volcanic ash-grain morphologies differ substantially from simplified geometric shapes.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Valiev, R.Z.; Islamgaliev, R.K.; Kuzmina, N.F.

Intense plastic straining techniques such as torsion straining and equal channel angular (ECA) pressing are processing procedures which may be used to make beneficial changes in the properties of materials through a substantial refinement in the microstructure. Although intense plastic straining procedures have been used for grain refinement in numerous experiments reported over the last decade, there appears to have been no investigations in which these procedures were used with metal matrix composites. The present paper describes a series of experiments in which torsion straining and ECA pressing were applied to an Al-6061 metal matrix composite reinforced with 10 volumemore » % of Al{sub 2}O{sub 3} particulates. As will be demonstrated, intense plastic straining has the potential for both reducing the grain size of the composite to the submicrometer level and increasing the strength at room temperature by a factor in the range of {approximately}2 to {approximately}3.« less

Microhardness variation and related microstructure in Al-Cu alloys prepared by HF induction melting and RF sputtering

NASA Astrophysics Data System (ADS)

Boukhris, N.; Lallouche, S.; Debili, M. Y.; Draissia, M.

2009-03-01

The materials under consideration are binary aluminium-copper alloys (10 at% to 90.3 at%Cu) produced by HF melting and RF magnetron sputtering. The resulting micro structures have been observed by standard metallographic techniques, X-ray powder diffraction, scanning electron microscopy and transmission electron microscopy. Vickers microhardness of bulk Al-Cu alloys reaches a maximum of 1800 MPa at 70.16 at%Cu. An unexpected metastable θ ' phase has been observed within aluminium grain in Al-37 at%Cu. The mechanical properties of a family of homogeneous Al{1-x}Cu{x} (0 < x < 0.92) thin films made by radiofrequency (13.56 MHz) cathodic magnetron sputtering from composite Al-Cu targets have been investigated. The as-deposited microstructures for all film compositions consisted of a mixture of the two expected face-centred-cubic (fcc) Al solid solution and tetragonal θ (Al{2}Cu) phases. The microhardness regularly increases and the grain size decreases both with copper concentration. This phenomenon of significant mechanical strengthening of aluminium by means of copper is essentially due to a combination between solid solution effects and grain size refinement. This paper reports some structural features of different Al-Cu alloys prepared by HF melting and RF magnetron on glass substrate sputtering.

Fabrication and luminescent properties of (Y0.99Eu0.01)2O3 transparent nanostructured ceramics

NASA Astrophysics Data System (ADS)

Yavetskiy, R. P.; Dobrotvorskaya, M. V.; Doroshenko, A. G.; Tolmachev, A. V.; Petrusha, I. A.; Turkevich, V. Z.; Tomala, R.; Hreniak, D.; Strek, W.; Baumer, V. N.

2018-04-01

(Y0.99Eu0.01)2O3 nanoceramics have been produced by sintering of stable cubic nanopowders under 8 GPa at temperature in the range of 25-500 °C with the use of Low Temperature High Pressure (LTHP) technique. During consolidation step irreversible phase transition from cubic to monoclinic yttria occurs resulting in two-phase nanoceramics with a grain size in the 10-40 nm range. It has been demonstrated that composite nanoceramics possess a high transmittance in the visible and mid IR ranges due to small light scattering on the nanoscale pores and low birefringence due to extremely small grain size. It has been shown that Eu3+ ions act as a luminescent probe in composite (Y0.99Eu0.01)2O3 nanoceramics since their 4f-4f luminescence strongly depends on the crystallographic environment. The luminescence spectra excited in the charge transfer band (CTB) are presented by superposition of emission from europium ions in cubic and monoclinic yttria. A new wide emission band of (Y0.99Eu0.01)2O3 ceramics in the λ = 500-650 nm wavelengths range (λex. = 307 nm) were attributed to luminescence of Eu3+ ions located in perturbed sites at grain boundaries or interfaces.

Infrared Spectroscopy of the Dust in Comets and Relationships to Interstellar Dust

NASA Technical Reports Server (NTRS)

Hanner, Martha S.

2003-01-01

Infrared spectroscopy of the dust in comets reveals a complex mix of silicate materials, including both crystalline and non-crystalline components of both olivine (forsterite) and pyroxene composition. These various components do not necessarily share a common origin. Since comets formed in cold regions of the solar nebula, pre-solar grains in the nebula could have been accreted into comets with little alteration. Some of the cometary silicates may be of circumstellar (formed in circumstellar outflows of evolved stars) or interstellar (formed in dense region of the interstellar medium) origin. Spectral similarities to both circumstellar and interstellar silicates are seen in comet spectra. the short-period Kuiper Belt comets) show weak or no spectral features. The lack of features is generally explained as a particle size effect: the small silicate grains are embedded in larger, optically thick particles. However, compositional differences cannot be ruled out. For example, no unambiguous signature of forsterite has yet been seen in the spectrum of a short-period comet. Thus, the Stardust sample from short-period comet P/Wild 2 will be extremely valuable. Not only grain by grain composition and isotopic ratios but also grain morphology, irradiation history, and evidence of organic refractory mantles are important for understanding their origin. The relative abundance and distinguishing characteristics of the various crystalline and non-crystalline silicate components needs to be established. While some comets, such as Hale-Bopp, display a rich infrared spectrum, others (particularly

Polarimetric Imaging Of Protoplanetary Disks From The Optical To Sub-Mm

NASA Astrophysics Data System (ADS)

De Boer, Jos; Ménard, F.; Pinte, C.; van der Plas, G.; Snik, F.

2017-10-01

To learn how planets form from the smallest building blocks within protoplanetary disks, we first need to know how dust grains grow from micron to mm sizes. Polarimetry across the spectrum has proven to be sensitive to grain properties like dust size distribution and composition and thus can be used to characterize the scattering grains. However, polarization measured with radio interferometric arrays is rarely studied in concert with optical polarimetry. Our team has successfully calibrated the NIR polarimetric imaging mode of VLT/SPHERE, hence upgrading the instrument from a high-contrast imager to a robust tool for quantitative characterization. In this presentation, we will discuss which lessons can be learned by comparing polarimetry in the optical and sub-mm and explore for which science cases both techniques can complement each other. When we combine the polarimetric capabilities of the most advanced optical high-contrast imagers (e.g., Gemini GPI or VLT SPHERE) with that of ALMA we will be able to study the spatial distribution of an extensive range of different grains, which allows us to take an essential step towards a deeper understanding of planet formation.

Cooperative nucleation modes in polycrystalline CoxPd1-x nanowires

NASA Astrophysics Data System (ADS)

Viqueira, M. S.; Pozo-López, G.; Urreta, S. E.; Condó, A. M.; Cornejo, D. R.; Fabietti, L. M.

2015-05-01

Polycrystalline CoxPd1-x (x = 1, 0.60, 0.45, 0.23, and 0.11) cylindrical nanowires (ø = 18-35 nm, about 1 μm length) are produced by AC electrodeposition into hexagonally ordered alumina pores. Single-phase nanowires of an fcc Co-Pd solid solution, with randomly oriented equiaxed grains (7-12 nm) are obtained; in all the cases, the grain size is smaller than the wire diameter. The coercive field and the reduced remanence of Co-rich nanowire arrays are hardly sensitive to temperature within the range varying from 4 K to 300 K. On the other hand, in Pd-rich nanowires both magnitudes are smaller and they largely increase when cooling below 100 K. This behavior also depends on the mean grain size. These facts are systematized considering two main aspects: the non-trivial temperature and composition dependence of the crystalline anisotropy and the saturation magnetostriction in Co-Pd alloys; and a random anisotropy effect, which defines a nucleation localization length that may involve more than a single grain, and thus promotes more cooperative nucleation modes.

The Electric Environment of Martian Dust Devils

NASA Astrophysics Data System (ADS)

Barth, E. L.; Farrell, W. M.; Rafkin, S. C.

2017-12-01

While Martian dust devils have been monitored through decades of observations, we have yet to study their possible electrical effects from in situ instrumentation. However, evidence for the existence of active electrodynamic processes on Mars is provided by laboratory studies of analog material and field campaigns of dust devils on Earth. We have enabled our Mars regional scale atmospheric model (MRAMS) to estimate an upper limit on electric fields generated through dust devil circulations by including charged particles as defined from the Macroscopic Triboelectric Simulation (MTS) code. MRAMS is used to investigate the complex physics of regional, mesoscale, and microscale atmospheric phenomena on Mars; it is a 3-D, nonhydrostatic model, which permits the simulation of atmospheric flows with large vertical accelerations, such as dust devils. MTS is a 3-D particle code which quantifies charging associated with swirling, mixing dust grains; grains of pre-defined sizes and compositions are placed in a simulation box and allowed to move under the influence of winds and gravity. Our MRAMS grid cell size makes our results most applicable to dust devils of a few hundred meters in diameter. We have run a number of simulations to understand the sensitivity of the electric field strength to the particle size and abundance and the amount of charge on each dust grain. We find that Efields can indeed develop in Martian dust convective features via dust grain filtration effects. The overall value of these E-fields is strongly dependent upon dust grain size, dust load, and lifting efficiency, and field strengths can range from 100s of mV/m to 10s of kV/m.

Developing precipitation hardenable high entropy alloys

NASA Astrophysics Data System (ADS)

Gwalani, Bharat

High entropy alloys (HEAs) is a concept wherein alloys are constructed with five or more elements mixed in equal proportions; these are also known as multi-principle elements (MPEs) or complex concentrated alloys (CCAs). This PhD thesis dissertation presents research conducted to develop precipitation-hardenable high entropy alloys using a much-studied fcc-based equi-atomic quaternary alloy (CoCrFeNi). Minor additions of aluminium make the alloy amenable for precipitating ordered intermetallic phases in an fcc matrix. Aluminum also affects grain growth kinetics and Hall-Petch hardenability. The use of a combinatorial approach for assessing composition-microstructure-property relationships in high entropy alloys, or more broadly in complex concentrated alloys; using laser deposited compositionally graded AlxCrCuFeNi 2 (0 < x < 1.5) complex concentrated alloys as a candidate system. The composition gradient has been achieved from CrCuFeNi2 to Al 1.5CrCuFeNi2 over a length of ˜25 mm, deposited using the laser engineered net shaping process from a blend of elemental powders. With increasing Al content, there was a gradual change from an fcc-based microstructure (including the ordered L12 phase) to a bcc-based microstructure (including the ordered B2 phase), accompanied with a progressive increase in microhardness. Based on this combinatorial assessment, two promising fcc-based precipitation strengthened systems have been identified; Al0.3CuCrFeNi2 and Al0.3CoCrFeNi, and both compositions were subsequently thermo-mechanically processed via conventional techniques. The phase stability and mechanical properties of these alloys have been investigated and will be presented. Additionally, the activation energy for grain growth as a function of Al content in these complex alloys has also been investigated. Change in fcc grain growth kinetic was studied as a function of aluminum; the apparent activation energy for grain growth increases by about three times going from Al0.1CoCrFeNi (3% Al (at%)) to Al0.3CoCrFeNi. (7% Al (at%)). Furthermore, Al addition leads to the precipitation of highly refined ordered L12 (gamma') and B2 precipitates in Al0.3CoCrFeNi. A detailed investigation of precipitation of the ordered phases in Al0.3CoCrFeNi and their thermal stability is done using atom probe tomography (APT), transmission electron microscopy (TEM) and Synchrotron X-ray in situ and ex situ analyses. The alloy strengthened via grain boundary strengthening following the Hall-Petch relationship offers a large increment of strength with small variation in grain size. Tensile strength of the Al0.3CoFeNi is increased by 50% on precipitation fine-scale gamma' precipitates. Furthermore, precipitation of bcc based ordered phase B2 in Al0.3CoCrFeNi can further strengthen the alloy. Fine-tuning the microstructure by thermo-mechanical treatments achieved a wide range of mechanical properties in the same alloy. The Al0.3CoCrFeNi HEA exhibited ultimate tensile strength (UTS) of ˜250 MPa and ductility of ˜65%; a UTS of ˜1100 MPa and ductility of ˜30%; and a UTS of 1850 MPa and a ductility of 5% after various thermo-mechanical treatments. Grain sizes, precipitates type and size scales manipulated in the alloy result in different strength ductility combinations. Henceforth, the alloy presents a fertile ground for development by grain boundary strengthening and precipitation strengthening, and offers very high activation energy of grain growth aptly suitable for high-temperature applications.

Synthesis and structural analysis of Fe doped TiO2 nanoparticles using Williamson Hall and Scherer Model

NASA Astrophysics Data System (ADS)

Patle, L. B.; Labhane, P. K.; Huse, V. R.; Gaikwad, K. D.; Chaudhari, A. L.

2018-05-01

The nanoparticles of Pure and doped Ti1-xFexO were synthesized by modified co-precipitation method successfully with nominal composite of x=0.0, 0.01, 0.03 and 0.05 at room temperature. The precursors were further calcined at 500°C for 6hrs in muffle furnace which results in the formation of different TiO2 phase compositions. The structural analysis carried out by XRD (Bruker D8 Cu-Kα1). X-ray peak broadening analysis was used to evaluate the crystalline sizes, the lattice parameters, atomic packing fraction, c/a ratio, X-ray density and Volume of unit cell. The Williamson Hall analysis is used to find grain size and Strain of prepared TiO2 nano particles. Crystalline TiO2 with a Tetragonal Anatase phase is confirmed by XRD results. The grain size of pure and Fe doped samples were found in the range of 10nm to 18nm. All the physical parameters of anatase tetragonal TiO2 nanoparticles were calculated more precisely using modified W-H plot a uniform deformation model (UDM). The results calculated from both the techniques were approximately similar.

Identification of an Extremely 180-Rich Presolar Silicate Grain in Acfer 094

NASA Technical Reports Server (NTRS)

Nguyen, A. N.; Messenger, S.

2009-01-01

Presolar silicate grains have been abundantly identified since their first discovery less than a decade ago [1,2,3]. The O isotopic compositions of both silicate and oxide stardust indicate the vast majority (>90%) condensed around Orich asymptotic giant branch (AGB) stars. Though both presolar phases have average sizes of 300 nm, grains larger than 1 m are extremely uncommon for presolar silicates. Thus, while numerous isotopic systems have been measured in presolar oxide grains [4], very few isotopic analyses for presolar silicates exist outside of O and Si [2,5]. And still, these measurements suffer from isotopic dilution with surrounding matrix material [6]. We conduct a search for presolar silicates in the primitive carbonaceous chondrite Acfer 094 and in some cases obtain high spatial resolution, high precision isotopic ratios.

Finite Element Modeling of Fragment Penetration of Thin Structural Composite Laminates

DTIC Science & Technology

1991-12-01

his direction and assistance provided during the program. The following are registered trade names: Kevlar-29, 3M Co., Scotchply, Owens Corning Fiberglass...grains, are used. Composite laminates such as Owens Corning Fiberglass (R) panels, 3M Scotchply 1002 (R) panels and Kevlar-29 (R) reinforced plastic...results [2]: 1. Owens Corning Fiberglass (OCF) Structural Panels. Woven S-2 glass and a typical resin type, contert, sizing, and cure cycle at 220

Dynamics of sediments along with their core properties in the Monastir-Bekalta coastline (Tunisia, Central Mediterranean)

NASA Astrophysics Data System (ADS)

Khiari, Nouha; Atoui, Abdelfattah; Khalil, Nadia; Charef, Abdelkrim; Aleya, Lotfi

2017-10-01

The authors report on two campaigns of high-resolution samplings along the shores of Monastir Bay in Tunisia: the first being a study of sediment dynamics, grain size and mineral composition in surface sediment, and the second, eight months later, using four sediment cores to study grain-size distribution in bottom sediments. Particle size analysis of superficial sediment shows that the sand in shallow depths is characterized by S-shaped curves, indicating a certain degree of agitation, possible transport by rip currents near the bottom and hyperbolic curves illustrating heterogeneity of sand stock. The sediments settle in a relatively calm environment. Along the bay shore (from 0 to 2 m depth), the bottom is covered by medium sand. Sediment transport is noted along the coast; from north to south and from south to north, caused by longshore drift and a rip current in the middle of the bay. These two currents are generated by wind and swell, especially by north to northeast waves which transport the finest sediment. Particle size analysis of bottom sediment indicates a mean grain size ranging from coarse to very fine sands while vertical distribution of grain size tends to decrease from surface to depth. The increase in particle size of sediment cores may be due to the coexistence of terrigenous inputs along with the sedimentary transit parallel to the coast due to the effect of longshore drift. Mineralogical analysis shows that Monastir's coastal sands and bottom sediment are composed of quartz, calcite, magnesium calcite, aragonite and hematite. The existence of a low energy zone with potential to accumulate pollutants indicates that managerial action is necessary to help preserve Monastir Bay.

Ongoing hydrothermal activities within Enceladus

NASA Astrophysics Data System (ADS)

Hsu, Hsiang-Wen; Postberg, Frank; Sekine, Yasuhito; Shibuya, Takazo; Kempf, Sascha; Horányi, Mihály; Juhász, Antal; Altobelli, Nicolas; Suzuki, Katsuhiko; Masaki, Yuka; Kuwatani, Tatsu; Tachibana, Shogo; Sirono, Sin-Iti; Moragas-Klostermeyer, Georg; Srama, Ralf

2015-03-01

Detection of sodium-salt-rich ice grains emitted from the plume of the Saturnian moon Enceladus suggests that the grains formed as frozen droplets from a liquid water reservoir that is, or has been, in contact with rock. Gravitational field measurements suggest a regional south polar subsurface ocean of about 10 kilometres thickness located beneath an ice crust 30 to 40 kilometres thick. These findings imply rock-water interactions in regions surrounding the core of Enceladus. The resulting chemical `footprints' are expected to be preserved in the liquid and subsequently transported upwards to the near-surface plume sources, where they eventually would be ejected and could be measured by a spacecraft. Here we report an analysis of silicon-rich, nanometre-sized dust particles (so-called stream particles) that stand out from the water-ice-dominated objects characteristic of Saturn. We interpret these grains as nanometre-sized SiO2 (silica) particles, initially embedded in icy grains emitted from Enceladus' subsurface waters and released by sputter erosion in Saturn's E ring. The composition and the limited size range (2 to 8 nanometres in radius) of stream particles indicate ongoing high-temperature (>90 °C) hydrothermal reactions associated with global-scale geothermal activity that quickly transports hydrothermal products from the ocean floor at a depth of at least 40 kilometres up to the plume of Enceladus.

PROGRESS ON THE STUDY OF BETA TREATMENT OF URANIUM, DECEMBER 1, 1962 TO MARCH 31, 1962

DOE Office of Scientific and Technical Information (OSTI.GOV)

Russell, R.B.; Wolff, A.K.

The effects of composition (ingot vs dingot), prior delta condition, geometry, heat treatment, and applied stress on cooling rate, grain size, and texture are described for U rods and tubes. Investigations were also made on the effect of stress and free surfaces on the texture distribution. Cooling rates were obtained for the quenching of 3- and 1.5-in. OD tubes with a 0.5-in. ID in different media, including a comparison of the rates between room temperature Houghto K and Poco No. 2 oils. The quenching rate in Houghto K was slightly greater. A study of 1.5-in. OD by 0.5-in. ID as-extrudedmore » dingot tube quenched from the beta phase into different media showed that the FEDC grain size of water- quenched tube varied between A-6 and A-7, that oil quenching produced grains between C-4 and C-5, and that the air-cooled tube had B-2 to B-3 grain size. Both ingot and dingot were similar in exhibiting severe radial texture penetration after water quenches. In general, both ingot and dingot have the same range of radial G/sub 3/ values, but with different G/sub 3/ distributions. (P.C.H.)« less

Compositional modes in the ash fraction of some modern pyroclastic deposits: their determination and significance

NASA Astrophysics Data System (ADS)

De Rosa, R.

This paper illustrates some problems involved in the quantitative compositional study of pyroclastic deposits and proposes criteria for selecting the main petrographic and textural classes for modal analysis. The relative proportions of the different classes are obtained using a point-counting procedure applied to medium-coarse ash samples that reduces the dependence of the modal composition on grain size and avoids tedious counting of different grain-size fractions. The major purposes of a quantified measure of component distributions are to: (a) document the nature of the fragmenting magma; (b) define the eruptive dynamics of the eruptions on a detailed scale; and (c) ensure accuracy in classifying pyroclastic deposits. Compositional modes of the ash fraction of pyroclastic deposits vary systematically, and their graphical representation defines the compositional and textural characteristics of pyroclastic fragments associated with different eruptive styles. Textural features of the glass component can be very helpful for inferring aspects of eruptive dynamics. Four major parameters can be used to represent the component composition of pyroclastic ash deposits: (a) juvenile index (JI); (b) crystallinity index (CrI); (c) juvenile vesicularity index (JVI); and (d) free crystal index (FCrI). The FCrI is defined as the ratio between single and total crystal fragments in the juvenile component (single crystals+crystals in juvenile glass). This parameter may provide an effective estimate of the mechanical energy of eruptions. Variations in FCrI vs JVI discriminate among pyroclastic deposits of different origin and define compositional fields that represent ash derived from different fragmentation styles.

Eolian features in the Western Desert of Egypt and some applications to Mars.

USGS Publications Warehouse

El-Baz, F.; Breed, C.S.; Grolier, M.J.; McCauley, J.F.

1979-01-01

Relations of landform types to wind regimes, bedrock composition, sediment supply, and topography are shown by field studies and satellite photographs of the Western Desert. This desert provides analogs of Martian wind-formed features and sand dunes, alternating light and dark streaks, knob 'shadows' and yardangs. Surface particles have been segregated by wind into dunes, sand sheets, and light streaks, that can be differentiated by their grain size distributions, surface shapes, and colors. Throughgoing sand of mostly fine to medium grain size is migrating S in longitudinal dune belts and barchan chains whose long axes lie parallel to the prevailing W winds, but topographic variations such as scarps and depressions strongly influence the zones of deposition and dune morphology. -from Authors

Computational study of textured ferroelectric polycrystals: Dielectric and piezoelectric properties of template-matrix composites

NASA Astrophysics Data System (ADS)

Zhou, Jie E.; Yan, Yongke; Priya, Shashank; Wang, Yu U.

2017-01-01

Quantitative relationships between processing, microstructure, and properties in textured ferroelectric polycrystals and the underlying responsible mechanisms are investigated by phase field modeling and computer simulation. This study focuses on three important aspects of textured ferroelectric ceramics: (i) grain microstructure evolution during templated grain growth processing, (ii) crystallographic texture development as a function of volume fraction and seed size of the templates, and (iii) dielectric and piezoelectric properties of the obtained template-matrix composites of textured polycrystals. Findings on the third aspect are presented here, while an accompanying paper of this work reports findings on the first two aspects. In this paper, the competing effects of crystallographic texture and template seed volume fraction on the dielectric and piezoelectric properties of ferroelectric polycrystals are investigated. The phase field model of ferroelectric composites consisting of template seeds embedded in matrix grains is developed to simulate domain evolution, polarization-electric field (P-E), and strain-electric field (ɛ-E) hysteresis loops. The coercive field, remnant polarization, dielectric permittivity, piezoelectric coefficient, and dissipation factor are studied as a function of grain texture and template seed volume fraction. It is found that, while crystallographic texture significantly improves the polycrystal properties towards those of single crystals, a higher volume fraction of template seeds tends to decrease the electromechanical properties, thus canceling the advantage of ferroelectric polycrystals textured by templated grain growth processing. This competing detrimental effect is shown to arise from the composite effect, where the template phase possesses material properties inferior to the matrix phase, causing mechanical clamping and charge accumulation at inter-phase interfaces between matrix and template inclusions. The computational results are compared with complementary experiments, where good agreement is obtained.

A multi-scale homogenization model for fine-grained porous viscoplastic polycrystals: I - Finite-strain theory

NASA Astrophysics Data System (ADS)

Song, Dawei; Ponte Castañeda, P.

2018-06-01

We make use of the recently developed iterated second-order homogenization method to obtain finite-strain constitutive models for the macroscopic response of porous polycrystals consisting of large pores randomly distributed in a fine-grained polycrystalline matrix. The porous polycrystal is modeled as a three-scale composite, where the grains are described by single-crystal viscoplasticity and the pores are assumed to be large compared to the grain size. The method makes use of a linear comparison composite (LCC) with the same substructure as the actual nonlinear composite, but whose local properties are chosen optimally via a suitably designed variational statement. In turn, the effective properties of the resulting three-scale LCC are determined by means of a sequential homogenization procedure, utilizing the self-consistent estimates for the effective behavior of the polycrystalline matrix, and the Willis estimates for the effective behavior of the porous composite. The iterated homogenization procedure allows for a more accurate characterization of the properties of the matrix by means of a finer "discretization" of the properties of the LCC to obtain improved estimates, especially at low porosities, high nonlinearties and high triaxialities. In addition, consistent homogenization estimates for the average strain rate and spin fields in the pores and grains are used to develop evolution laws for the substructural variables, including the porosity, pore shape and orientation, as well as the "crystallographic" and "morphological" textures of the underlying matrix. In Part II of this work has appeared in Song and Ponte Castañeda (2018b), the model will be used to generate estimates for both the instantaneous effective response and the evolution of the microstructure for porous FCC and HCP polycrystals under various loading conditions.

Microstructure Characterization Of Lead-Free Solders Depending On Alloy Composition

NASA Astrophysics Data System (ADS)

Panchenko, Iuliana; Mueller, Maik; Wolter, Klaus-Juergen

2010-11-01

Fatigue and crack nucleation in solder joints is basically associated with changes in the microstructure. Therefore the microstructure evolution of SnAgCu solder joints during solidification and subsequent application is an important subject for reliability investigations and physics of failure analysis. The scope of this study is a systematic overview of the as-cast microstructures in small sized lead-free SnAgCu solder spheres after solidification. A total of 32 alloy compositions have been investigated with varying Ag content from 0 to 5 wt.% and varying Cu content from 0 to 1.2 wt.%. The solder spheres had a diameter of approx. 270 μm and were all manufactured under the similar conditions. Subsequent cross-sectioning was carried out in order to analyze the microstructure by optical and electron microscopy as well as Electron Backscatter Diffraction and Energy Dispersive X-ray Spectroscopy. The results allow a comprehensive overview of the dependence of the as-cast microstructure on the solder composition. It is shown that strong changes in microstructure can be caused by small changes in solder composition. In addition, a solidification phenomenon known as cyclic twinning has been found in the samples. Three different microstructures related to that phenomenon will be presented and detailed characterizations of these structures are given in this study. These microstructures differ in their appearance by solidification morphology, phase distribution as well as grain structure and can be described as follows: 1. large dentritic areas of different grain orientations which are characterized by approx. 60° twin boundaries; 2. areas of small β-Sn cells with approx. 60° twin relation and larger intermetallic precipitates; 3. large grains consisting of a β-Sn matrix with very fine intermetallic precipitates and high angle grain boundaries between adjacent grains.

Using complimentary microscopy methods to examine Ni-Mn-Si-precipitates in highly-irradiated reactor pressure vessel steels

DOE PAGES

Edmondson, P. D.; Parish, C. M.; Nanstad, R. K.

2017-05-29

Nano-scale Ni-Mn-Si-rich precipitates formed in a reactor pressure vessel steel under high neutron fluence have been characterized using highly complimentary atom probe tomography (APT) and scanning transmission electron microscopy with energy dispersive spectroscopy (STEM-EDS) combined with STEM-EDS modeling. Using these techniques in a synergistic manner to overcome the well-known trajectory aberrations in APT data, the average upper limit Fe concentration within the precipitates was found to be ~6 at.%. Using this knowledge, accurate compositions of the precipitates was determined and it was found that the spread of precipitate compositions was large, but mostly centered around the Γ2-and G-phases. The usemore » of STEM-EDS also allowed for larger areas to be examined, and segregation of minor solutes was observed to occur on grain boundaries, along with Ni-Mn-Si-rich precipitates that were smaller in size than those in the matrix. Solute segregation at the grain boundaries is proposed to occur through a radiation induced segregation or radiation enhanced diffusion mechanism due to the presence of a denuded zone about the grain boundary. It is also proposed that the reduced precipitate size at the grain boundaries is due to the structure of the grain boundary. The lack of Ni-Mn-Si precipitates observed in larger Mo-rich precipitates is also discussed, and the absence of the minor solutes required to form the Ni-Mn-Si precipitates results in the lack of nucleation. This is in contrast to cementite phases in which Ni-Mn-Si precipitates have been seen to be formed. It was also determined through this work that the exclusion of all the Fe ions during atom probe analysis is a reasonable approximation.« less

Automated Coastal Engineering System: Technical Reference

DTIC Science & Technology

1992-09-01

of Contents ACES Technical Reference Wave Transmission Through Permeable Structures ..................................... 5-4 Littoral Processes...A-2 Table A-4: Grain-Size Scales ( Soil Classification) ..................................... A-3 Table A-5: Major Tidal Constituents... Permeable Structures Lonphore Sediment Tranaport Littoral Numerical Si~ulation of Time-Dependent Beach and Dune Erosion Processes Calculation of Composite

The dust scattering halo of Cygnus X-3

NASA Astrophysics Data System (ADS)

Corrales, L. R.; Paerels, F.

2015-10-01

Dust grains scatter X-ray light through small angles, producing a diffuse halo image around bright X-ray point sources situated behind a large amount of interstellar material. We present analytic solutions to the integral for the dust scattering intensity, which allow for a Bayesian analysis of the scattering halo around Cygnus X-3. Fitting the optically thin 4-6 keV halo surface brightness profile yields the dust grain size and spatial distribution. We assume a power-law distribution of grain sizes (n ∝ a-p) and fit for p, the grain radius cut-off amax, and dust mass column. We find that a p ≈ 3.5 dust grain size distribution with amax ≈ 0.2 μm fits the halo profile relatively well, whether the dust is distributed uniformly along the line of sight or in clumps. We find that a model consisting of two dust screens, representative of foreground spiral arms, requires the foreground Perseus arm to contain 80 per cent of the total dust mass. The remaining 20 per cent of the dust, which may be associated with the outer spiral arm of the Milky Way, is located within 1 kpc of Cyg X-3. Regardless of which model was used, we found τ_sca ˜ 2 E_keV^{-2}. We examine the energy resolved haloes of Cyg X-3 from 1 to 6 keV and find that there is a sharp drop in scattering halo intensity when E < 2-3 keV, which cannot be explained with multiple scattering effects. We hypothesize that this may be caused by large dust grains or material with unique dielectric properties, causing the scattering cross-section to depart from the Rayleigh-Gans approximation that is used most often in X-ray scattering studies. The foreground Cyg OB2 association, which contains several evolved stars with large extinction values, is a likely culprit for grains of unique size or composition.

Post-processing of metal matrix composites by friction stir processing

NASA Astrophysics Data System (ADS)

Sharma, Vipin; Singla, Yogesh; Gupta, Yashpal; Raghuwanshi, Jitendra

2018-05-01

In metal matrix composites non-uniform distribution of reinforcement particles resulted in adverse affect on the mechanical properties. It is of great interest to explore post-processing techniques that can eliminate particle distribution heterogeneity. Friction stir processing is a relatively newer technique used for post-processing of metal matrix composites to improve homogeneity in particles distribution. In friction stir processing, synergistic effect of stirring, extrusion and forging resulted in refinement of grains, reduction of reinforcement particles size, uniformity in particles distribution, reduction in microstructural heterogeneity and elimination of defects.

Size effects on magnetoelectric response of multiferroic composite with inhomogeneities

NASA Astrophysics Data System (ADS)

Yue, Y. M.; Xu, K. Y.; Chen, T.; Aifantis, E. C.

2015-12-01

This paper investigates the influence of size effects on the magnetoelectric performance of multiferroic composite with inhomogeneities. Based on a simple model of gradient elasticity for multiferroic materials, the governing equations and boundary conditions are obtained from an energy variational principle. The general formulation is applied to consider an anti-plane problem of multiferroic composites with inhomogeneities. This problem is solved analytically and the effective magnetoelectric coefficient is obtained. The influence of the internal length (grain size or particle size) on the effective magnetoelectric coefficients of piezoelectric/piezomagnetic nanoscale fibrous composite is numerically evaluated and analyzed. The results suggest that with the increase of the internal length of piezoelectric matrix (PZT and BaTiO3), the magnetoelectric coefficient increases, but the rate of increase is ratcheting downwards. If the internal length of piezoelectric matrix remains unchanged, the magnetoelectric coefficient will decrease with the increase of internal length scale of piezomagnetic nonfiber (CoFe2O3). In a composite consisiting of a piezomagnetic matrix (CoFe2O3) reinforced with piezoelectric nanofibers (BaTiO3), an increase of the internal length in the piezomagnetic matrix, results to a decrease of the magnetoelectric coefficient, with the rate of decrease diminishing.

Single-phase ceramics with La 1- xSr xGa 1- yMg yO 3- δ composition from precursors obtained by mechanosynthesis

NASA Astrophysics Data System (ADS)

Moure, A.; Castro, A.; Tartaj, J.; Moure, C.

Dense ceramics with La 0.80Sr 0.20Ga 0.85Mg 0.15O 2.825 and La 0.80Sr 0.15Ga 0.85Mg 0.20O 2.825 compositions have been prepared by sintering of mechanosynthesized precursors. The perovskite is synthesized after 85 h of milling in a planetary mill. Single phases have been obtained at conditions that are not possible if traditional solid-state reaction (SSR) method is used. The influence of milling time and composition in the reactivity of the precursors is studied. Highest purity is obtained in Sr = 0.15 and Mg = 0.20 composition, with relative density higher than 97%. The total elimination of typical secondary phases for these compositions, as SrLaGaO 4 and SrLaGa 3O 7, allows the total conductivity of the ceramics to be improved. The influence of the grain size and the nature of the grain boundaries on the electrical characteristic of the ceramics are also discussed.

Modelling of the sublimation of icy grains in the coma of comet 67P/Churyumov-Gerasimenko

NASA Astrophysics Data System (ADS)

Gicquel, A.; Vincent, J.-B.; Shi, X.; Sierks, H.; Rose, M.; Güttler, C.; Tubiana, C.

2015-10-01

The ESA (European Space Agency) Rosetta spacecraft was launched on 2 March 2004, to reach comet 67P/Churyumov-Gerasimenko in August 2014. Since March 2014, images of the nucleus and the coma (gas and dust) of the comet have been acquired by the OSIRIS (Optical, Spectroscopic, and Infrared Remote Imaging System) camera system [1] using both, the wide angle camera (WAC) and the narrow angle camera (NAC). The orbiter will be maintained in the vicinity of the comet until perihelion (Rh=1.3 AU) or even until Rh=1.8 AU post-perihelion (December 2015). Nineteen months of uninterrupted, close-up observations of the gas and dust coma will be obtained and will help to characterize the evolution of comet gas and dust activity during its approach to the Sun. Indeed, for the first time, we will follow the development of a comet's coma from a close distance. Also the study of the dust-gas interaction in the coma will highlight the sublimation of icy grains. Even if the sublimation of icy grains is known, it is not yet integrated in a complete dust-gas model. We are using the Direct Simulation Monte Carlo (DSMC) method to study the gas flow close to the nucleus. The code called PI-DSMC (www.pidsmc. com) can simulate millions of molecules for multiple species.When the gas flow is simulated, we inject the dust particle with a zero velocity and we take into account the 3 forces acting on the grains in a cometary environment (drag force, gravity and radiative pressure). We used the DLL (Dynamic Link Library) model to integrate the sublimation of icy grains in the gas flowand allow studying the effect of the additional gas on the dust particle trajectories. For a quantitative analysis of the sublimation of icy, outflowing grains we will consider an ensemble of grains of various radii with different compositions [2] The evolution of the grains, once they are ejected into the coma, depends on their initial size, their composition and the heliocentric distance (because the temperature of the grain is higher close to the Sun). The grain temperatures will be derived by assuming equilibrium between the energy absorbed from the Sun, the energy re-radiated in the infrared, and the cooling by sublimation. We will use Mie theory [3, 4] to compute the scattering properties of an assumed grain (grain size, shape and composition, including mineralogy and porosity). We follow the evolution of grains until the icy layer sublimates completely. Once ejected in the gas flow, the generated molecules have no preferred direction. First results highlighted that the sublimation has a significant influence on the dust trajectories and generates a gas cloud that moves with the velocity of the icy grains. Our model can produce artificial images for a wide range of parameters, including outgassing rate, surface temperature, dust properties and sublimation of icy grains. The results of this model will be compared to the images obtained with OSIRIS camera and to the published data from other instruments.

Investigation of Carbide Precipitation Process and Chromium Depletion during Thermal Treatment of Alloy 690

NASA Astrophysics Data System (ADS)

Jiao, S. Y.; Zhang, M. C.; Zheng, L.; Dong, J. X.

2010-01-01

For the purpose of studying the effect of heat treatment on carbide morphology and chromium concentration distribution, which are critical to the resistance of alloy 690 to stress corrosion cracking (SCC), a series of thermal treatments was performed. A model taking into account the intercorrelated dynamic process between the carbide precipitation and chemical diffusion of the chromium atom from matrix to grain boundary (GB) was constructed on the basis of classical nucleation theory, Kolmogorov-Johnson-Mehl-Avrami law, and diffusion theory. The validity of this model was evaluated by comparing the simulated results of the carbide average size and chromium concentration near the GB with the corresponding measured results. A discontinuous factor was introduced based on the relation linking the interdistance between the carbides and the carbide average size; thus, the carbide morphology and chromium concentration could be predicted by this model. According to the results of the experiments and simulations, a carbide discontinuous factor smaller than 2.2 together with the chromium concentration at the GB higher than a critical value (21 wt pct) were essential for the corrosion resistance ability of the alloy, and then some proper heat-treatment conditions were obtained through predicting the value of the two variables. In addition, the effects of the grain size and composition variation on the carbide discontinuous factor and chromium concentration profile were simulated. The results indicated that an intermediate grain size of approximately 31.8 to ~63.5 μm was beneficial for effectively improving the resistance of the alloy to SCC. Simultaneously, the carbon content should be adjusted near 0.02 pct, and the chromium content should be the highest possible in its chemical composition scale.

Chemical composition and microstructure of Bauhinia grains.

PubMed

Amonsou, Eric O; Siwela, Muthulisi; Dlamini, Nomusa

2014-09-01

Bauhinia is a leguminous plant species found in almost every part of the world, including southern Africa. In this study, grain composition and protein body microstructure of two indigenous southern African Bauhinia species, B. galpinii and B. petersiana were determined. Protein (38 g/100 g) and fat (23 g/100 g) were the major constituents of Bauhinia. Bauhinia grains also contained substantial amounts of zinc (6 mg/100 g) and iron (3 mg/100 g) when compared to FAO/WHO standards. The parenchyma cells of Bauhinia showed spherical protein bodies with globoids inclusions and these were surrounded by lipids. However, the protein bodies of B. petersiana were smaller in size (7 ± 3 μm) than those of B. galpinii (13 ± 4 μm). The microstructure of protein bodies in Bauhinia is very similar to that of soya, suggesting that the processing technology developed for soya protein may be adopted for Bauhinia.

Physical characteristics and magnetic properties of BaFe{sub 12}O{sub 19}/SrTiO{sub 3} based composites derived from mechanical alloying

DOE Office of Scientific and Technical Information (OSTI.GOV)

Widodo, Rahmat Doni, E-mail: rahmat-doni@yahoo.com; Manaf, Azwar

2016-04-19

A composite system BaFe{sub 12}O{sub 19}/SrTiO{sub 3} with ferrimagnetic BaFe{sub 12}O{sub 19} phase (BHF) and ferroelectric SrTiO{sub 3} phase (STO) have been prepared by mechanical alloying and subsequent heat treatment. The composite powders were studied by Particle Size Analyze, X-ray diffraction and magnetic measurement. It was found that the particle size of composite powders initially increased due to laminated layers formation of a composite and then decreased to an asymptotic value of ∼8 µm as the milling time extended even to a relatively longer time. However, based on results of line broadening analysis the mean grain size of the particles wasmore » found in the nanometer scale. We thus believed that mechanical blending and milling of mixture components for the composite materials has promoted heterogeneous nucleation and only after successive sintering at 1100°C the milled powder transformed into particles of nanograin. In this report, microstructure as well as magnetic properties for the composite is also briefly discussed.« less

Simulation of Particle Size Effect on Dynamic Properties and Fracture of PTFE-W-Al Composites

NASA Astrophysics Data System (ADS)

Herbold, Eric; Cai, Jing; Benson, David; Nesterenko, Vitali

2007-06-01

Recent investigations of the dynamic compressive strength of cold isostatically pressed (CIP) composites of polytetrafluoroethylene (PTFE), tungsten and aluminum powders show significant differences depending on the size of metallic particles. PTFE and aluminum mixtures are known to be energetic under dynamic and thermal loading. The addition of tungsten increases density and overall strength of the sample. Multi-material Eulerian and arbitrary Lagrangian-Eulerian methods were used for the investigation due to the complexity of the microstructure, relatively large deformations and the ability to handle the formation of free surfaces in a natural manner. The calculations indicate that the observed dependence of sample strength on particle size is due to the formation of force chains under dynamic loading in samples with small particle sizes even at larger porosity in comparison with samples with large grain size and larger density.

The Mineralogy of Circumstellar Silicates Preserved in Cometary Dust

NASA Technical Reports Server (NTRS)

Keller, L. P.; Messenger, S.

2010-01-01

Interplanetary dust particles (IDPs) contain a record of the building blocks of the solar system including presolar grains, molecular cloud material, and materials formed in the early solar nebula. Cometary IDPs have remained relatively unaltered since their accretion because of the lack of parent body thermal and aqueous alteration. We are using coordinated transmission electron microscope (TEM) and ion microprobe studies to establish the origins of the various components within cometary IDPs. Of particular interest is the nature and abundance of presolar silicates in these particles because astronomical observations suggest that crystalline and amorphous silicates are the dominant grain types produced in young main sequence stars and evolved O-rich stars. Five circumstellar grains have been identified including three amorphous silicate grains and two polycrystalline aggregates. All of these grains are between 0.2 and 0.5 micrometers in size. The isotopic compositions of all five presolar silicate grains fall within the range of presolar oxides and silicates, having large (17)O-enrichments and normal (18)O/(16)O ratios (Group 1 grains from AGB and RG stars). The amorphous silicates are chemically heterogeneous and contain nanophase FeNi metal and FeS grains in a Mg-silicate matrix. Two of the amorphous silicate grains are aggregates with subgrains showing variable Mg/Si ratios in chemical maps. The polycrystalline grains show annealed textures (equilibrium grains boundaries, uniform Mg/Fe ratios), and consist of 50-100 nm enstatite and pyrrhotite grains with lesser forsterite. One of the polycrystalline aggregates contains a subgrain of diopside. The polycrystalline aggregates form by subsolidus annealing of amorphous precursors. The bulk compositions of the five grains span a wide range in Mg/Si ratios from 0.4 to 1.2 (avg. 0.86). The average Fe/Si (0.40) and S/Si (0.21) ratios show a much narrower range of values and are approximately 50% of their solar abundances. The latter observation may indicate a decoupling of the silicate and sulfide components in grains that condense in stellar outflows. The amorphous silicate grains described here were not extensively affected by irradiation, sputtering, or thermal processing and may represent relatively pristine circumstellar grains. They are strong candidates for the "dirty silicates" in astronomical observations of circumstellar dust shells. The polycrystalline grains were originally amorphous silicate grains that were likely annealed in the early solar nebula but the processing was not sufficient to erase their anomalous oxygen isotopic compositions.

Synthesis and characterization of LiFePO4/C cathode materials by sol-gel method.

PubMed

Liu, Shuxin; Yin, Hengbo; Wang, Haibin; Wang, Hong

2014-09-01

The carbon coated LiFePO4 cathode materials (LiFePO4/C) were successfully synthesized by sol-gel method with glucose, citric acid and PEG-4000 as dispersant and carbon source, respectively. The microstructure and grain size of LiFePO4/C composite were characterized by X-ray diffraction, Raman spectroscopy, transmission electron microscopy. The results showed that the carbon source and calcination temperature had important effect on the graphitization degree of carbon; the carbon decomposed by citric acid had higher graphitization degree; with calcination temperature rising, the graphitization degree of carbon increased and the particles size increased. The graphitization degree and grain size were very important for improving the electrochemical performance of LiFePO4 cathode materials, according to the experimental results, the sample LFP-700 (LFP-C) which was synthesized with citric acid as dispersant at 700 degree C had lower polarization and larger discharge capacity.

Towards the determination of deformation rates - pinch-and-swell structures as a natural and simulated paleo-strain rate gage

NASA Astrophysics Data System (ADS)

Peters, Max; Poulet, Thomas; Karrech, Ali; Regenauer-Lieb, Klaus; Herwegh, Marco

2014-05-01

Layered rocks deformed under viscous deformation conditions frequently show boudinage, a phenomenon that results from differences in effective viscosity between the involved layers. In the case of continuous necking of a mechanically stiffer layer embedded in a weaker matrix, symmetric boudins are interpreted as the result of dominant visco-plastic deformation (Goscombe et al., 2004). However, information on the physical conditions, material properties and deformation processes are yet unknown. Natural samples deformed under low-grade (T<350°C) metamorphic conditions were studied in detail in the Dent de Morcles and Doldenhorn nappes of the Helvetic Alps in order to accurately simulate their deformation styles by numerical models. In these samples, monomineralic calcite (Cc) veins were repeatedly boudinaged on cm- to µm-scale. Remnants of incompletely recrystallized original vein Cc grains in the swells indicate a sequence of deformation twinning, followed by progressive dynamic recrystallization along former twin planes up to complete recrystallization in the pinches (Schmalholz and Maeder, 2012). This sequence suggests dislocation creep to be active as important deformation mechanism. In contrast to the pinch-and-swell structures, the grain size of the Cc in the surrounding matrix is much finer-grained due to pinning by secondary particles, forcing the matrix to deform under viscous granular creep, i.e. by diffusion accommodated grain boundary sliding. The deformation processes observed in the natural samples were incorporated into a numerical model in order to evaluate the rheology of both layer and matrix, using an extension to a user material subroutine (Karrech et al., 2011a) for the finite element solver ABAQUS. We implemented thermo-mechanical coupling allowing elastic, viscous and plastic deformation of Cc (Herwegh et al., in press). We simulate a pure-shear box using finite elements, each representing a grain size distribution, which undergo layer-parallel extension. The box is built up by 3 layers, consisting of a central layer of coarse-grained populations, surrounded by finer-grained populations on bottom and top. The rheology evolves from transient stages (elasticity and strain hardening) to composite viscous flow (GSI & GSS) with increasing shear strain. The small grain sizes in top and bottom layers are strain-invariant and limited in their growth (comparable to Zener pinning) forcing the matrix to deform by exclusively by GSS creep. In contrast, the initially coarse grain sizes of the central layer are allowed to adapt to the physical deformation conditions by either grain growth or grain size reduction following the Paleowattmeter of Austin and Evans (2007) combined with the thermodynamic approach of Regenauer-Lieb and Yuen (2004). Depending on the dissipated energy, grain sizes in these domains vary substantially in space and time. While low strain rates (low stresses) in the swells favor grain growth and GSI dominated deformation, high strain rates in the pinches provoke dramatic grain size reduction with an increasing contribution of GSS as a function of decreasing grain size. The development of symmetric necks observed in nature thus seems to coincide with the transition from dislocation to diffusion creep dominated flow with continuous grain size reduction and growth from swell to neck at relatively high extensional strains. REFERENCES Austin, N. and Evans, B. (2007). Paleowattmeters: A scaling relation for dynamically recrystallized grain size. Geology, 35. Goscombe, B.D., Passchier, C.W. and Hand, M. (2004). Boudinage classification: End-member boudin types and modified boudin structures, Journal of Structural Geology, 26. Herwegh, M., Poulet, T., Karrech, A. and Regenauer-Lieb, K. (in press). From transient to steady state deformation and grain size: A thermodynamic approach using elasto-visco-plastic numerical modeling. Journal of Geophysical Research. Karrech, A., Regenauer-Lieb, K. and Poulet, T. (2011a). A Damaged visco-plasticity model for pressure and temperature sensitive geomaterials. Journal of Engineering Science 49. Regenauer-Lieb, K. and Yuen, D. (2004). Positive feedback of interacting ductile faults from coupling of equation of state, rheology and thermal-mechanics. Physics of the Earth and Planetary Interiors, 142. Schmalholz, S.M. and Maeder, X. (2012). Pinch-and-swell structure and shear zones in viscoplastic layers. Journal of Structural Geology, 34.

Microstructure, Mechanical, and Fatigue Strength of Ti-54M Processed by Rotary Swaging

NASA Astrophysics Data System (ADS)

Al-Khazraji, Hasan; El-Danaf, Ehab; Wollmann, Manfred; Wagner, Lothar

2015-05-01

TIMETAL 54M is a newly developed (α + β) titanium alloy with nominal composition Ti-5Al-4V-0.6Mo-0.4Fe. The alloy can provide a cost benefit over Ti-6Al-4V due to improved machinability and formability. In the present work, evolution of mechanical properties in terms of tensile and hardness values is investigated as a function of deformation degrees imposed via rotary swaging (RS). Microstructure, mechanical properties, and fatigue performance of Ti-54M are investigated after severe plastic deformation by RS conducted at 850 °C and after being subjected to two different post-swaging annealing conditions. Optical microscopy and scanning electron microscopy using electron back scatter diffraction were utilized to document the evolution of the microstructure. Tensile tests were conducted to characterize mechanical properties. RS, to a true strain of 3.0, is found to lead to a marked ultrafine-grained structure of about 1 μm grain size with low content of high angle grain boundaries (HAGBs). Post-swaging heat treatment at 800 °C followed by air cooling did not change the grain size but exhibited high content of HAGBs. Post-swaging heat treatment at 940 °C followed by furnace cooling resulted in a grain size of about 5 μm and enhanced work-hardening capability and ductility, which resulted in less fatigue notch sensitivity, but at the same time lower fatigue strength at 107 cycles.

Characterization and Evaluation of TiB2-AlN Composites for Armor Applications

DTIC Science & Technology

2013-09-01

identified structural defects and studied the fracture mechanisms (15, 16). 2 2. Experimental One TiB2 powder was used for this study. The TiB2...on phase formation and grain size effects compounded with residual stress on the fracture mechanisms . However, it was determined that the composite...Temperature. Annu. Book ASTM Stand. 2002, Vol. 15.01. 18. ASTM C 1421-10. Standard Test Methods for Determination of Fracture Toughness of

High temperature compounds for turbine vanes

NASA Technical Reports Server (NTRS)

Rhodes, W. H.; Cannon, R. M., Jr.

1972-01-01

Fabrication and microstructure control studies were conducted on SiC, Si3N4, and composites based on these compounds. Charpy mode impact testing to 2400 F established that beta-spodumene, lithium aluminum silicate, coated Si3N4, Si3N4 derived from alpha-Si3N4 powder, and SiC containing 5-25 v/o chopped C fibers had the most promising strengths. Several other composite systems had excellent microstructures and could prove interesting materials in the future. Stress-rupture testing on Si3N4 established that increasing 2000 F - 100 hour strengths were obtained for increasing grain size to at least 5 micrometers, increasing density and possibly increasing phase purity. These parameters became less important at 2400 F where it is thought a grain boundary phase controls strength.

Implications of Grain Size Evolution for the Effective Stress Exponent in Ice

NASA Astrophysics Data System (ADS)

Behn, M. D.; Goldsby, D. L.; Hirth, G.

2016-12-01

Viscous flow in ice has typically been described by the Glen law—a non-Newtonian, power-law relationship between stress and strain-rate with a stress exponent n 3. The Glen law is attributed to grain-size-insensitive dislocation creep; however, laboratory and field studies demonstrate that deformation in ice is strongly dependent on grain size. This has led to the hypothesis that at sufficiently low stresses, ice flow is controlled by grain boundary sliding [1], which explicitly incorporates the grain-size dependence of ice rheology. Yet, neither dislocation creep (n 4), nor grain boundary sliding (n 1.8), have stress exponents that match the value of n 3 for the Glen law. Thus, although the Glen law provides an approximate description of ice flow in glaciers and ice sheets, its functional form cannot be explained by a single deformation mechanism. Here we seek to understand the origin of the n 3 dependence of the Glen law through a new model for grain-size evolution in ice. In our model, grain size evolves in response to the balance between dynamic recrystallization and grain growth. To simulate these processes we adapt the "wattmeter" [2], originally developed within the solid-Earth community to quantify grain size in crustal and mantle rocks. The wattmeter posits that grain size is controlled by a balance between the mechanical work required for grain growth and dynamic grain size reduction. The evolution of grain size in turn controls the relative contributions of dislocation creep and grain boundary sliding, and thus the effective stress exponent for ice flow. Using this approach, we first benchmark our grain size evolution model on experimental data and then calculate grain size in two end-member scenarios: (1) as a function of depth within an ice-sheet, and (2) across an ice-stream margin. We show that the calculated grain sizes match ice core observations for the interior of ice sheets. Furthermore, owing to the influence of grain size on strain rate, the variation in grain size with deformation conditions results in an effective stress exponent intermediate between grain boundary sliding and dislocation creep. [1] Goldsby & Kohlstedt, JGR, 2001; [2] Austin & Evans, Geology, 1997

A refractory inclusion returned by Stardust from comet 81P/Wild 2

NASA Astrophysics Data System (ADS)

Simon, S. B.; Joswiak, D. J.; Ishii, H. A.; Bradley, J. P.; Chi, M.; Grossman, L.; AlÉOn, J.; Brownlee, D. E.; Fallon, S.; Hutcheon, I. D.; Matrajt, G.; McKeegan, K. D.

2008-11-01

Among the samples returned from comet 81P/Wild 2 by the Stardust spacecraft is a suite of particles from one impact track (Track 25) that are Ca-, Al-rich and FeO-free. We studied three particles from this track that range in size from 5.3 × 3.2 μ to 15 × 10 μ. Scanning and transmission electron microscopy show that they consist of very fine-grained (typically from ˜0.5 to ˜2 μ) Al-rich, Ti-bearing and Ti-free clinopyroxene, Mg-Al spinel and anorthite, with trace amounts of fine perovskite, FeNi metal and osbornite (TiN) grains. In addition to these phases, the terminal particle, named "Inti", also contains melilite. All of these phases, with the exception of osbornite, are common in refractory inclusions and are predicted to condense at high temperature from a gas of solar composition. Osbornite, though very rare, has also been found in meteoritic refractory inclusions, and could have formed in a region of the nebula where carbon became enriched relative to oxygen compared to solar composition. Compositions of Ti-pyroxene in Inti are similar, but not identical, to those of fassaite from Allende inclusions. Electron energy loss spectroscopy shows that Ti-rich pyroxene in Inti has Ti3+/Ti4+within the range of typical meteoritic fassaite, consistent with formation under reducing conditions comparable to those of a system of solar composition. Inti is 16O-rich, with δ18O?δ17O?-40%0, like unaltered phases in refractory inclusions and refractory IDPs. With grain sizes, mineralogy, mineral chemistry, and an oxygen isotopic composition like those of refractory inclusions, we conclude that Inti is a refractory inclusion that formed in the inner solar nebula. Identification of a particle that formed in the inner solar system among the comet samples demonstrates that there was transport of materials from the inner to the outer nebula, probably either in a bipolar outflow or by turbulence.

3D Observation of GEMS by Electron Tomography

NASA Technical Reports Server (NTRS)

Matsuno, Junya; Miyake, Akira; Tsuchiyama, Akira; Nakamura-Messenger, Keiko; Messenger, Scott

2014-01-01

Amorphous silicates in chondritic porous interplanetary dust particles (CP-IDPs) coming from comets are dominated by glass with embedded metal and sulfides (GEMS). GEMS grains are submicron-sized rounded objects (typically 100-500) nm in diameter) with anaometer-sized (10-50 nm) Fe-Ni metal and sulfide grains embedded in an amorphous silicate matrix. Several formation processes for GEMS grains have been proposed so far, but these models are still being debated [2-5]. Bradley et al. proposed that GEMS grains are interstellar silicate dust that survived various metamorphism or alteration processes in the protoplanetary disk and that they are amorphiation products of crystalline silicates in the interstellar medium by sputter-deposition of cosmic ray irradiation, similar to space weathering [2,4]. This consideration is based on the observation of nano-sized crystals (approximately 10 nm) called relict grains in GEMS grains and their shapes are pseudomorphs to the host GEMS grains. On the other hand, Keller and Messenger proposed that most GEMS formed in the protoplanetary disk as condensates from high temperature gas [3,5]. This model is based on the fact that most GEMS grains have solar isotopic compositions and have extremely heterogeneous and non-solar elemental compositions. Keller and Messenger (2011) also reported that amorphous silicates in GEMS grains are surrounded by sulfide grains, which formed as sulfidization of metallic iron grains located on the GEMS surface. The previous studies were performed with 2D observation by using transmission electron microscopy (TEM) or scanning TEM (STEM). In order to understand the structure of GEMS grains described above more clearly, we observed 3D structure of GEMS grains by electron tomography using a TEM/STEM (JEM-2100F, JEOL) at Kyoto University. Electron tomography gives not only 3D structures but also gives higher spatial resolution (approximately a few nm) than that in conventional 2D image, which is restricted by sample thickness ) approx. or greater than 50 nm). Three cluster IDPs (L2036AA5 cluster4, L2009L8 cluster 13 and W726A2) were used for the observations. ID W726A2 was collected without silicon oil, which is ordinary used to collect IDPs, so this sample has no possibility of contaminations caused by silicon oil or solvent to rinse it [6]. The samples were embedded in epoxy risin and sliced into ultrathin sections (50-300 nm) using an ultramicotome. The sections were observed by BF-TEM and HAADF-STEM (high angle annular dark field-scanning TEM) modes. Images were obtained by rotating the sample tilt angle over a range of +/- 65 deg in 1 deg steps. The obtained images were reconstructed to slice images. Mineral phases in the slice images were estimated by comparing with a 2D elemental map obtained by an EDS (energy dispersive X-ray spectroscopy) system equipped in the TEM/STEM. Careful examination of the slice images confirmed that iron grains are embedded in the amorphous silicate matrix of the GEMS grains, but sulfide grains were mainly present on the surface of the amorphous silicate. These results are consistent with the model that GEMS grains formed as condensates [3,5], although more data are needed to conclude the origin of GEMS grains. The present study is the first successful example adapting the electron tomography to the IDPs. This type of analysis will be important for planetary material sciences in the future.

Metal/ceramic interface structures and segregation behavior in aluminum-based composites

DOE PAGES

Zhang, Xinming; Hu, Tao; Rufner, Jorgen F.; ...

2015-06-14

Trimodal Al alloy (AA) matrix composites consisting of ultrafine-­grained (UFG) and coarse-­ grained (CG) Al phases and micron-­sized B 4C ceramic reinforcement particles exhibit combinations of strength and ductility that render them useful for potential applications in the aerospace, defense and automotive industries. Tailoring of microstructures with specific mechanical properties requires a detailed understanding of interfacial structures to enable strong interface bonding between ceramic reinforcement and metal matrix, and thereby allow for effective load transfer. Trimodal AA metal matrix composites typically show three characteristics that are noteworthy: nanocrystalline grains in the vicinity of the B4C reinforcement particles; Mg segregation atmore » AA/B 4C interfaces; and the presence of amorphous interfacial layers separating nanocrystalline grains from B 4C particles. Interestingly, however, fundamental information related to the mechanisms responsible for these characteristics as well as information on local compositions and phases are absent in the current literature. Here in this study, we use high-­resolution transmission electron microscopy, energy-­dispersive X-­ray spectroscopy, electron energy-­loss spectroscopy, and precession assisted electron diffraction to gain fundamental insight into the mechanisms that affect the characteristics of AA/B 4C interfaces. Specifically, we determined interfacial structures, local composition and spatial distribution of the interfacial constituents. Near atomic resolution characterization revealed amorphous multilayers and a nanocrystalline region between Al phase and B 4C reinforcement particles. The amorphous multilayers consist of nonstoichiometric Al xO y, while the nanocrystalline region is comprised of MgO nanograins. The experimental results are discussed in terms of the possible underlying mechanisms at AA/B 4C interfaces.« less

Effects of Degassing on the Microstructure, Chemistry, and Estimated Mechanical Properties of a Cryomilled Al-Mg Alloy

NASA Astrophysics Data System (ADS)

Hofmeister, Clara; Zhou, Le; Kellogg, Frank; Giri, Anit; Cho, Kyu; Sohn, Yongho

2018-04-01

Nanostructured aluminum alloys produced through cryomilling have generated interest due to their potential to create consolidated parts with high strength and low density. Degassing prior to consolidation minimizes adsorbed and absorbed volatiles, but is accompanied by microstructural changes such as grain growth, dislocation annihilation, and formation of dispersoids. These changes can influence the mechanical behavior of consolidated components. Cryomilled AA5083 was degassed at temperatures from 473 K to 773 K (200 °C to 500 °C) with a vacuum at or below 2.7 × 10-3 Pa. Grain size in the as-cryomilled powder (ranging from 21 to 34 nm) increased with higher degassing temperature and reached a maximum size of up to 70 to 80 nm. The dislocation density of 1.11 × 1015 m-2 in as-cryomilled powder decreased to 1.56 × 1014 m-2 for powder degassed at 773 K (500 °C). The Al6(MnFeCr) dispersoid formed when powders were degassed at or above 573 K (300 °C). Oxygen and nitrogen concentrations were unaffected by degassing; however, hydrogen concentration decreased with increasing degassing temperature to a minimum of 45 ± 3.16 ppm. Evolutions in composition and microstructure in cryomilled AA5083 were correlated to the strengthening mechanisms of grain size reduction (i.e., Hall-Petch), dislocation forest, and Orowan. However, strengthening by grain size reduction was the dominant strengthening mechanism.

Nanoblast synthesis and consolidation of (La0.8Sr0.2)(Ga0.9Mg0.1)O(3-delta) under Spark plasma sintering conditions.

PubMed

Vasylkiv, Oleg; Borodianska, Hanna; Badica, Petre; Zhen, Yongda; Tok, Alfred

2009-01-01

Four-cation nanograined strontium and magnesium doped lanthanum gallate (La0.8Sr0.2) (Ga0.9Mg0.1)O(3-delta) (LSGM) and its composite with 2 wt% of ceria (LSGM-Ce) were prepared. Morphologically homogeneous nanoreactors, i.e., complex intermediate metastable aggregates of desired composition were assembled by spray atomization technique, and subsequently loaded with nanoparticles of highly energetic C3H6N6O6. Rapid nanoblast calcination technique was applied and the final composition was synthesized within the preliminary localized volumes of each single nanoreactor on the first step of spark plasma treatment. Subsequent SPS consolidations of nanostructured extremely active LSGM and LSGM-Ce powders were achieved by rapid treatment under pressures of 90-110 MPa. This technique provided the heredity of the final structure of nanosize multimetal oxide, allowed the prevention of the uncontrolled agglomeration during multicomponent aggregates assembling, subsequent nanoblast calcination, and final ultra-rapid low-temperature SPS consolidation of nanostructured ceramics. LaSrGaMgCeO(3-delta) nanocrystalline powder consisting of approximately 11 nm crystallites was consolidated to LSGM-Ce nanoceramic with average grain size of approximately 14 nm by low-temperature SPS at 1250 degrees C. Our preliminary results indicate that nanostructured samples of (La0.8Sr0.2)(Ga0.9Mg0.1)O(3-delta) with 2 wt% of ceria composed of approximataley 14 nm grains can exhibit giant magnetoresistive effect in contrast to the usual paramagnetic properties measured on the samples with larger grain size.

The nature of cometary dust as determined from infrared observations

NASA Technical Reports Server (NTRS)

Swamy, K. S. Krishna; Sandford, Scott A.; Allamandola, Louis J.; Witteborn, Fred C.; Bregman, Jesse D.

1989-01-01

The infrared measurements of comets, the compositional information available from interplanetary dust particles (IDPs), and the recent results of flybys to Comet Halley can help in restricting the nature and composition of cometary dust models (c.f., Proceedings of the 20th ESLAB Symposium on Exploration of Halley's Comet, 1986). Researchers tried to incorporate some of these results into a coherent model to account for the observed cometary infrared emission. The presence of 10 and 3.4 micron features in Comet Halley (c.f. Bregman et al. 1987; Wickramasinghe and Allen 1986) indicated the presence of at least two components in the grain material, namely silicates and some form of amorphous carbon. These two components could reside in separate grains or may be parts of composite particles. Both these cases have been considered (see Krishna Swamy el a. 1988a, 1988b). In the absence of refractive index data for cometary analogs, the authors used the optical constants of olivine-rich lunar material 12009.48 (Perry et al. 1972) for the infrared region and that of alpha:C-H film for amorphous carbon (angus et al. 1986). For the visible region, a value of m = 1.38-0.39i was used for the silicates, and values published by Arakawa et al. (1985) were used for the amorphous carbon. These materials should give a representative behavior of the expected results. The model results were compared to observational data. The strength of the 3.4 micron and 10 micron features relative to the adjacent continuum, as well as the slope of the continuum between 2500 and 1250 cm(exp -1) (4 to 8 microns), were used as criteria for comparison. Model calculations with alpha approx. equals -3.5, and also the size distribution function inferred for Comet Halley, with a mass fraction (X) of silicate to amorphous carbon grains of about 40 to 1 can fit the data. A good match is obtained for the infrared spectra of Comets Halley and West from a 40 to 1 mixture of silicate and amorphous carbon grains with a a(exp -3.5) size distribution function. The results are consistent with compositional constraints provided by interplanetary dust particles (IPDs) and Halley flyby data. The variation of grain temperature with heliocentric distance appears to account for the major changes observed in cometary spectra.

The Hardness and Strength Properties of WC-Co Composites

PubMed Central

Armstrong, Ronald W.

2011-01-01

The industrially-important WC-Co composite materials provide a useful, albeit complicated materials system for understanding the combined influences on hardness and strength properties of the constituent WC particle strengths, the particle sizes, their contiguities, and of Co binder hardness and mean free paths, and in total, the volume fraction of constituents. A connection is made here between the composite material properties, especially including the material fracture toughness, and the several materials-type considerations of: (1) related hardness stress-strain behaviors; (2) dislocation (viscoplastic) thermal activation characterizations; (3) Hall-Petch type reciprocal square root of particle or grain size dependencies; and (4) indentation and conventional fracture mechanics results. Related behaviors of MgO and Al2O3 crystal and polycrystal materials are also described for the purpose of making comparisons. PMID:28824143

The Effect of Friction Stir Processing on Microstructure and Tensile Behavior of Thixomolded AZ91 Magnesium Alloy

NASA Astrophysics Data System (ADS)

Mansoor, B.; Decker, R. F.; Kulkarni, S.; LeBeau, S. E.; Khraisheh, M. K.

Friction Stir Processing (FSP) to partial sheet thickness can be utilized to engineer unique microstructures in metallic alloys. These composite microstructures consist of three distinct layers associated with stirred, transition and core micro structural regions. The stirred region is of particular interest where severe plastic deformation imparted by the rotating and translating FSP tool under frictional heat leads to grain refinement down to 1 urn grain size. In this work, partial depth penetration into thixomolded AZ91 Mg plate from the top and bottom surfaces by friction stir processing is explored. Furthermore, low temperature aging treatments are applied to the processed material. The present results with AZ91 Mg show that FSP processed material exhibits higher strength (> 300 MPa), and improvement in ductility (> 7 % tensile elongation). It is found that in addition to Hall-Petch strengthening produced by 1 um grain size in the stirred region, the enhanced strength levels and ductility are strongly influenced by dispersoids of the intermetallic precipitates found in this alloy.

X-ray absorption fine structure and x-ray diffraction studies of crystallographic grains in nanocrystalline FePd:Cu thin films

NASA Astrophysics Data System (ADS)

Krupinski, M.; Perzanowski, M.; Polit, A.; Zabila, Y.; Zarzycki, A.; Dobrowolska, A.; Marszalek, M.

2011-03-01

FePd alloys have recently attracted considerable attention as candidates for ultrahigh density magnetic storage media. In this paper we investigate FePd thin alloy film with a copper admixture composed of nanometer-sized grains. [Fe(0.9 nm)/Pd(1.1 nm)/Cu(d nm)]×5 multilayers were prepared by thermal deposition at room temperature in UHV conditions on Si(100) substrates covered by 100 nm SiO2. The thickness of the copper layer has been changed from 0 to 0.4 nm. After deposition, the multilayers were rapidly annealed at 600 °C in a nitrogen atmosphere, which resulted in the creation of the FePd:Cu alloy. The structure of alloy films obtained this way was determined by x-ray diffraction (XRD), glancing angle x-ray diffraction, and x-ray absorption fine structure (EXAFS). The measurements clearly showed that the L10 FePd:Cu nanocrystalline phase has been formed during the annealing process for all investigated copper compositions. This paper concentrates on the crystallographic grain features of FePd:Cu alloys and illustrates that the EXAFS technique, supported by XRD measurements, can help to extend the information about grain size and grain shape of poorly crystallized materials. We show that, using an appropriate model of the FePd:Cu grains, the comparison of EXAFS and XRD results gives a reasonable agreement.

Lasting Impact of a Tsunami Event on Sediment-Organism Interactions in the Ocean

NASA Astrophysics Data System (ADS)

Seike, Koji; Sassa, Shinji; Shirai, Kotaro; Kubota, Kaoru

2018-02-01

Although tsunami sedimentation is a short-term phenomenon, it may control the long-term benthic environment by altering seafloor surface characteristics such as topography and grain-size composition. By analyzing sediment cores, we investigated the long-term effect of the 2011 tsunami generated by the Tohoku Earthquake off the Pacific coast of Japan on sediment mixing (bioturbation) by an important ecosystem engineer, the heart urchin Echinocardium cordatum. Recent tsunami deposits allow accurate estimation of the depth of current bioturbation by E. cordatum, because there are no preexisting burrows in the sediments. The in situ hardness of the substrate decreased significantly with increasing abundance of E. cordatum, suggesting that echinoid bioturbation softens the seafloor sediment. Sediment-core analysis revealed that this echinoid rarely burrows into the coarser-grained (medium-grained to coarse-grained) sandy layer deposited by the 2011 tsunami; thus, the vertical grain-size distribution resulting from tsunami sedimentation controls the depth of E. cordatum bioturbation. As sandy tsunami layers are preserved in the seafloor substrate, their restriction on bioturbation continues for an extended period. The results demonstrate that understanding the effects on seafloor processes of extreme natural events that occur on geological timescales, including tsunami events, is important in revealing continuing interactions between seafloor sediments and marine benthic invertebrates.

Development of cataclastic foliation in deformation bands in feldspar-rich conglomerates of the Rio do Peixe Basin, NE Brazil

NASA Astrophysics Data System (ADS)

Nicchio, Matheus A.; Nogueira, Francisco C. C.; Balsamo, Fabrizio; Souza, Jorge A. B.; Carvalho, Bruno R. B. M.; Bezerra, Francisco H. R.

2018-02-01

In this work we describe the deformation mechanisms and processes that occurred during the evolution of cataclastic deformation bands developed in the feldspar-rich conglomerates of the Rio do Peixe Basin, NE Brazil. We studied bands with different deformation intensities, ranging from single cm-thick tabular bands to more evolved clustering zones. The chemical identification of cataclastic material within deformation bands was performed using compositional mapping in SEM images, EDX and XRD analyses. Deformation processes were identified by microstructural analysis and by the quantification of comminution intensity, performed using digital image processing. The deformation bands are internally non homogeneous and developed during five evolutionary stages: (1) moderate grain size reduction, grain rotation and grain border comminution; (2) intense grain size reduction with preferential feldspar fragmentation; (3) formation of subparallel C-type slip zones; (4) formation of S-type structures, generating S-C-like fabric; and (5) formation of C‧-type slip zones, generating well-developed foliation that resembles S-C-C‧-type structures in a ductile environment. Such deformation fabric is mostly imparted by the preferential alignment of intensely comminuted feldspar fragments along thin slip zones developed within deformation bands. These processes were purely mechanical (i.e., grain crushing and reorientation). No clays or fluids were involved in such processes.

Using Antifreeze Proteins to understand ice microstructure evolution

NASA Astrophysics Data System (ADS)

Bayer-Giraldi, Maddalena; Azuma, Nobuhiko; Takata, Morimasa; Weikusat, Christian; Kondo, Hidemasa; Kipfstuhl, Sepp

2017-04-01

Polar ice sheets are considered a unique climate archive. The chemical analysis of its impurities and the development of its microstructure with depth give insight in past climate conditions as well as in the development of the ice sheet with time and deformation. Microstructural patterns like small grain size observed in specific depths are thought to be linked to the retarding effect of impurities on ice grain growth. Clear evidence of size or chemical composition of the impurities causing this effect is missing, but in this context a major role of nanoparticles has been suggested. In order to shed light on different mechanisms by which nanoparticles can control microstructure development we used antifreeze proteins (AFPs) as proxies for particles in ice. These proteins are small nanoparticles, approx. 5 nm in size, with the special characteristics of firmly binding to ice through several hydrogen bonds. We used AFPs from the sea-ice microalgae Fragilariopsis cylindrus (fcAFPs) in bubble-free, small-grained polycrystalline ice obtained by the phase-transition size refinement method. We explain how fcAFP bind to ice by presenting the 3-D-protein structure model inferred by X-ray structure analysis, and show the importance of the chemical interaction between particles and ice in controlling normal grain growth, comparing fcAFPs to other protein nanoparticles. We used modifications of fcAFPs for particle localization through fluorescence spectroscopy. Furthermore, the effect of fcAFPs on the driving factors for ice deformation during creep, i.e. on internal dislocations due to incorporation within the lattice and on the mobility of grain boundaries due to pinning, makes these proteins particularly interesting in studying the process of ice deformation.

Temporal pattern and memory in sediment transport in an experimental step-pool channel

NASA Astrophysics Data System (ADS)

Saletti, Matteo; Molnar, Peter; Zimmermann, André; Hassan, Marwan A.; Church, Michael; Burlando, Paolo

2015-04-01

In this work we study the complex dynamics of sediment transport and bed morphology in steep streams, using a dataset of experiments performed in a steep flume with natural sediment. High-resolution (1 sec) time series of sediment transport were measured for individual size classes at the outlet of the flume for different combinations of sediment input rates, discharges, and flume slopes. The data show that the relation between instantaneous discharge and sediment transport exhibits large variability on different levels. After dividing the time series into segments of constant water discharge, we quantify the statistical properties of transport rates by fitting the data with a Generalized Extreme Value distribution, whose 3 parameters are related to the average sediment flux. We analyze separately extreme events of transport rate in terms of their fractional composition; if only events of high magnitude are considered, coarse grains become the predominant component of the total sediment yield. We quantify the memory in grain size dependent sediment transport with variance scaling and autocorrelation analyses; more specifically, we study how the variance changes with different aggregation scales and how the autocorrelation coefficient changes with different time lags. Our results show that there is a tendency to an infinite memory regime in transport rate signals, which is limited by the intermittency of the largest fractions. Moreover, the structure of memory is both grain size-dependent and magnitude-dependent: temporal autocorrelation is stronger for small grain size fractions and when the average sediment transport rate is large. The short-term memory in coarse grain transport increases with temporal aggregation and this reveals the importance of the sampling frequency of bedload transport rates in natural streams, especially for large fractions.

Soil texture and granulometry at the surface of Mars

NASA Technical Reports Server (NTRS)

Dollfus, A.; Deschamps, M.; Zimbelman, J.

1992-01-01

The microtexture of the near-surface Martian soil was sensed with three diagnostic parameters: (1) the albedo A at normal incidence and phase angle 5 degrees, which relates to the composition of the top surface exposed layer; (2) the polarization parameter b characterizes the texture of the top surface layer in terms of grain size; and (3) the thermal inertia parameter I which refers to the soil compaction through the first few decimeters below the top surface sensed by polarimetry, in terms of size for the pieces making a granular regolith. Parameter b was derived from instrument VPM on board the Soviet spacecraft MARS-5, inertial I is from IRTM on the American Viking, and albedo A from both. The polarimetric scans racked strips covering two contrasted regions, the dark hued Mare Erythraeum, and the adjacent bright orange Thaumasia. Erythraem is characterized everywhere by a same type of terrain, despite the large geomorphological diversity of the surface. There is an ubiquitous coating or mantling with small dark grains, of both albedo 12.7 percent and particle size 10 to 20 microns, above a subsurface dislocation in pieces around 300 to 600 microns. A simple model is with sand-size particles completely coated with 15 micron dark grains.

Structure and thermomechanical behavior of NiTiPt shape memory alloy wires.

PubMed

Lin, Brian; Gall, Ken; Maier, Hans J; Waldron, Robbie

2009-01-01

The objective of this work is to understand the structure-property relationships in polycrystalline NiTiPt (Ti 42.7 at.% Ni 7.5 at %Pt) with a composition showing pseudoelasticity at ambient temperatures. Structural characterization of the alloy includes grain size determination and texture analysis while the thermomechanical properties are explored using tensile testing. Variation in heat treatment is used as a vehicle to modify microstructure. The results are compared to experiments on Ni-rich NiTi alloy wires (Ti-51.0 at.% Ni), which are in commercial use in various biomedical applications. With regards to microstructure, both alloys exhibit a <111> fiber texture along the wire drawing axis; however, the NiTiPt alloy grain size is smaller than that of the Ni-rich NiTi wires, while the latter materials contain second-phase precipitates. Given the nanometer-scale grain size in NiTiPt and the dispersed, nanometer-scale precipitate size in NiTi, the overall strength and ductility of the alloys are essentially identical when given appropriate heat treatments. Property differences include a much smaller stress hysteresis and smaller temperature dependence of the transformation stress for NiTiPt alloys compared to NiTi alloys. Potential benefits and implications for use in vascular stent applications are discussed.

New research on the origin of mottled clay in Quaternary basins in the coastal area of south China

NASA Astrophysics Data System (ADS)

Wang, Jing; Chen, Zhen; Gao, Quanzhou; Chen, Guoneng

2018-06-01

Last Glacial Maximum (LGM) mottled clay occurs widely in Late Quaternary basins in south China coastal areas. Current research attributes its origin to exposure weathering of Late Pleistocene marine/fluvial deposits during the LGM. However, field data suggest that this is not the case as there is no gradual transition in lithology, grain size, structure and material composition among these layers. Instead, the mottled clay possesses sedimentary characteristics of exotic dust. In this study, three typical drill cores in the Pearl River Delta were studied using grain size analysis, diffuse reflection spectroscopy (DRS) and geochemical analysis to ascertain the clay's sedimentary characteristics and origin. Grain size distribution patterns and parameters of the mottled clay were similar to those of a typical loess, indicating aeolian origin. In DRS curves, the peak height of hematite > goethite, indicating that the mottled clay had not experienced strong hydration and constitutes a continental product. This conforms to a typical loess but differs from the underlying marine/fluvial deposits. The chemical composition of the mottled clay was homogeneous in the vertical and planar directions. Upper continental crust (UCC) normalized curves of major and trace elements of the mottled clay were close to the average UCC and were consistent with typical aeolian deposits. The spatial and temporal distribution characteristics and relationship with the underlying layer suggest that the mottled clay was a loess-like deposit during the LGM and its mottled structure originated from strong modification of oxidation during the postglacial period after homogeneous dust had accumulated.

U.S.-MEXICO BORDER PROGRAM ARIZONA BORDER STUDY--STANDARD OPERATING PROCEDURE FOR SOIL CHARACTERIZATION (UA-L-11.1)

EPA Science Inventory

The purpose of this SOP is to describe the procedures to be followed in splitting and determining the grain size characteristics, electrical conductivity, and pH of the "Composite Soil" and "Foundation Soil" samples. This procedure applies to the general characterization of sedi...

Krypton and xenon in lunar fines

NASA Technical Reports Server (NTRS)

Basford, J. R.; Dragon, J. C.; Pepin, R. O.; Coscio, M. R., Jr.; Murthy, V. R.

1973-01-01

Data from grain-size separates, stepwise-heated fractions, and bulk analyses of 20 samples of fines and breccias from five lunar sites are used to define three-isotope and ordinate intercept correlations in an attempt to resolve the lunar heavy rare gas system in a statistically valid approach. Tables of concentrations and isotope compositions are given.

Glued structural members

Treesearch

Russell C. Moody; Jen Y. Liu

1999-01-01

Glued structural members are manufactured in a variety of configurations. Structural composite lumber (SCL) products consist of small pieces of wood glued together into sizes common for solid-sawn lumber. Glued-laminated timber (glulam) is an engineered stress-rated product that consists of two or more layers of lumber in which the grain of all layers is oriented...

An Integrative Framework for the Analysis of Multiple and Multimodal Representations for Meaning-Making in Science Education

ERIC Educational Resources Information Center

Tang, Kok-Sing; Delgado, Cesar; Moje, Elizabeth Birr

2014-01-01

This paper presents an integrative framework for analyzing science meaning-making with representations. It integrates the research on multiple representations and multimodal representations by identifying and leveraging the differences in their units of analysis in two dimensions: timescale and compositional grain size. Timescale considers the…

Hot-cracking studies of Inconel 718 weld- heat-affected zones

NASA Technical Reports Server (NTRS)

Thompson, E. G.

1969-01-01

Hot ductility tests, gas-tungsten-arc fillerless fusion tests, and circle patch-weld-restraint tests were conducted on Inconel 718 to better understand and correlate the weldability /resistance to hot cracking/ of the alloy. A correlation of the test results with composition, heat-treat condition, grain size, and microstructure was made.

A Phase Field Study of the Effect of Microstructure Grain Size Heterogeneity on Grain Growth

NASA Astrophysics Data System (ADS)

Crist, David J. D.

Recent studies conducted with sharp-interface models suggest a link between the spatial distribution of grain size variance and average grain growth rate. This relationship and its effect on grain growth rate was examined using the diffuse-interface Phase Field Method on a series of microstructures with different degrees of grain size gradation. Results from this work indicate that the average grain growth rate has a positive correlation with the average grain size dispersion for phase field simulations, confirming previous observations. It is also shown that the grain growth rate in microstructures with skewed grain size distributions is better measured through the change in the volume-weighted average grain size than statistical mean grain size. This material is based upon work supported by the National Science Foundation under Grant No. 1334283. The NSF project title is "DMREF: Real Time Control of Grain Growth in Metals" and was awarded by the Civil, Mechanical and Manufacturing Innovation division under the Designing Materials to Revolutionize and Engineer our Future (DMREF) program.

New Experiences in Dike Construction with Soil-Ash Composites and Fine-Grained Dredged Materials

NASA Astrophysics Data System (ADS)

Duszyński, Remigiusz; Duszyńska, Angelika; Cantré, Stefan

2017-12-01

The supporting structure inside a coastal dike is often made of dredged non-uniform sand with good compaction properties. Due to the shortage of natural construction material for both coastal and river dikes and the surplus of different processed materials, new experiments were made with sand-ash mixtures and fine-grained dredged materials to replace both dike core and dike cover materials resulting in economical, environmentally friendly and sustainable dikes. Ash from EC Gdańsk and dredged sand from the Vistula river were mixed to form an engineering material used for dike construction. The optimum sand-ash composites were applied at a field test site to build a large-scale research dike. Fine-grained dredged materials from Germany were chosen to be applied in a second full-scale research dike in Rostock. All materials were investigated according to the standards for soil mechanical analysis. This includes basic soil properties, mechanical characteristics, such as grain-size distribution, compaction parameters, compressibility, shear strength, and water permeability. In the field, the infiltration of water into the dike body as well as the erosion resistance of the cover material against overflowing water was determined. Results of both laboratory and field testing are discussed in this paper. In conclusion, the mixing of bottom ash with mineral soil, such as relatively uniform dredged sand, fairly improves the geotechnical parameters of the composite, compared to the constituents. Depending on the composite, the materials may be suitable to build a dike core or an erosion-resistant dike cover.

Parking simulation of three-dimensional multi-sized star-shaped particles

NASA Astrophysics Data System (ADS)

Zhu, Zhigang; Chen, Huisu; Xu, Wenxiang; Liu, Lin

2014-04-01

The shape and size of particles may have a great impact on the microstructure as well as the physico-properties of particulate composites. However, it is challenging to configure a parking system of particles to a geometrical shape that is close to realistic grains in particulate composites. In this work, with the assistance of x-ray tomography and a spherical harmonic series, we present a star-shaped particle that is close to realistic arbitrary-shaped grains. To realize such a hard particle parking structure, an inter-particle overlapping detection algorithm is introduced. A serial sectioning approach is employed to visualize the particle parking structure for the purpose of justifying the reliability of the overlapping detection algorithm. Furthermore, the validity of the area and perimeter of solids in any arbitrary section of a plane calculated using a numerical method is verified by comparison with those obtained using an image analysis approach. This contribution is helpful to further understand the dependence of the micro-structure and physico-properties of star-shaped particles on the realistic geometrical shape.

Space-Weathering on Mercury: Inferences Based on Comparison of MESSENGER Spectral Data and Experimental Space Weathering Data

NASA Astrophysics Data System (ADS)

Gillis-Davis, J. J.; Blewett, D. T.; Lawrence, D. J.; Izenberg, N. R.; McClintock, W. E.; Holsclaw, G. M.; Domingue, D. L.

2009-12-01

Production and accumulation of submicroscopic metallic iron (SMFe) is a principal mechanism by which surfaces of airless silicate bodies in the Solar System, exposed to the space weathering environment, experience spectral modification. Micrometeorite impact vaporization and solar-wind sputtering produce coatings of vapor-deposited SMFe. Both processes can be more intense on Mercury and, as a result, more efficient at creating melt and vapor. In addition, Ostwald ripening may cause SMFe particles to grow larger due to the high surface temperatures on Mercury (as great as 450°C). Spectral effects on the ultraviolet-visible-near-infrared continuum change with the amount and size of SMFe present. Thus, the physical properties and abundance of iron in Mercury’s regolith can be understood by comparing spectral data from controlled space-weathering experiments with spectra from MESSENGER’s Mercury Atmospheric and Surface Composition Spectrometer (MASCS). Knowledge of SMFe size and abundance may provide information on the space weathering conditions under which it was produced or subsequently modified. Reflectance spectra of laboratory-produced samples with varying SMFe grain sizes (average grain sizes of 8, 15, 35, and 40 nm) and iron compositions (from 0.005 to 3.8 wt% Fe as SMFe) are compared with MASCS disk-integrated reflectance from the first flyby of Mercury and will be compared with observations of spectral end members targeted for the third flyby. We compare spectra from 300 nm to 1400 nm wavelength, scaled to 1 at 700 nm, from the laboratory and MASCS. This comparison between laboratory and remote-sensing spectra reveals an excellent match with observations of Mercury for samples with an average iron metal grain size of 8 nm and 1.65 wt% FeO and 15 nm and 0.13 wt% Fe. These average grain sizes of the SMFe component are larger than the average grain size determined for lunar soil samples using transmission electron microscopy (3 nm in rims and 10-15 nm in agglutinates) but are smaller than values obtained from lunar spectra with the methods used here (15-25 nm). We can also infer that silicates in Mercury's high reflectance plains are potentially iron poor, precluding thick vapor deposits coating - both spectral data sets lack a 1-μm absorption and the experimental iron particles are suspended in an iron-free silica gel. Thus, our conclusion on the basis of spectral comparison is that SMFe on Mercury is potentially smaller than on the Moon and that Ostwald ripening is not a major influence on the surface of Mercury. The absence of pronounced darkening of the equatorial regions of Mercury in images from Mariner 10 and MESSENGER's Mercury Dual Imaging System supports also suggest an apparent lack of Ostwald ripening.

MID-INFRARED SPECTROPHOTOMETRIC OBSERVATIONS OF FRAGMENTS B AND C OF COMET 73P/SCHWASSMANN-WACHMANN 3

DOE Office of Scientific and Technical Information (OSTI.GOV)

Harker, David E.; Woodward, Charles E.; Kelley, Michael S.

2011-01-15

We present mid-infrared spectra and images from the Gemini-N (+ Michelle) observations of fragments SW3-[B] and SW3-[C] of the ecliptic (Jupiter family) comet 73P/Schwassmann-Wachmann 3 pre-perihelion. We observed fragment B soon after an outburst event (between 2006 April 16-26 UT) and detected crystalline silicates. The mineralogy of both fragments was dominated by amorphous carbon and amorphous pyroxene. The grain size distribution (assuming a Hanner-modified power law) for fragment SW3-[B] has a peak grain radius of a{sub p} {approx} 0.5 {mu}m, and for fragment SW3-[C], a{sub p} {approx} 0.3 {mu}m; both values are larger than the peak grain radius of themore » size distribution for the dust ejected from ecliptic comet 9P/Tempel 1 during the Deep Impact event (a{sub p} = 0.2 {mu}m). The silicate-to-carbon ratio and the silicate crystalline mass fraction for the submicron to micron-sized portion of the grain size distribution on the nucleus of fragment SW3-[B] were 1.341{sup +0.250}{sub -0.253} and 0.335{sup +0.089}{sub -0.112}, respectively, while on the nucleus of fragment SW3-[C] they were 0.671{sup +0.076}{sub -0.076} and 0.257{sup +0.039}{sub -0.043}, respectively. The similarity in mineralogy and grain properties between the two fragments implies that 73P/Schwassmann-Wachmann 3 is homogeneous in composition. The slight differences in grain size distribution and silicate-to-carbon ratio between the two fragments likely arise because SW3-[B] was actively fragmenting throughout its passage while the activity in SW3-[C] was primarily driven by jets. The lack of diverse mineralogy in the fragments SW3-[B] and SW3-[C] of 73P/Schwassmann-Wachmann 3 along with the relatively larger peak in the coma grain size distribution suggests that the parent body of this comet may have formed in a region of the solar nebula with different environmental properties than the natal sites where comet C/1995 O1 (Hale-Bopp) and 9P/Tempel 1 nuclei aggregated.« less

Pollination ecology of Silene acutifolia (Caryophyllaceae): floral traits variation and pollinator attraction.

PubMed

Buide, María Luisa

2006-02-01

The floral display influences the composition of pollinators interacting with a plant species. Geographic and temporal variation in pollinator composition complicates the understanding of the evolutionary consequences of floral display variation. This paper analyses the relationships between Silene acutifolia, a hermaphroditic perennial herb, and its pollinators, based on field studies in the north-west of Spain. Studies were conducted over three years (1997-1999). Firstly, the main pollinators of this species were determined for two years in one population. Secondly, pollen limitation in fruit and seed production was analysed by supplementary hand pollinations, and counting the pollen grains and tubes growing in styles for two different-sized populations. Finally, the effect of flower size and number on the rate of visitation and total seed number was examined for 15 marked plants. The primary pollinators were long-tongued insects, including Hymenoptera, Lepidoptera and Diptera, but the composition and visitation frequencies differed between years. Pollen limitation occurred in one of the years of study. There was between-population variation in the number of pollen grains and pollen tubes found in styles, suggesting pollen limitation in one population. Overall, pollinators visited plants with more open flowers more frequently, and pollinated more flowers within these plants. Conversely, petal and calyx sizes had no effect on insect visitation. Plants with higher rates of visits produced higher number of seeds, suggesting that pollinator-mediated limitation of seed and fruit production may be important in some years.

Impact of grain size evolution on necking and pinch-and-swell formation in calcite layers

NASA Astrophysics Data System (ADS)

Schmalholz, Stefan Markus; Duretz, Thibault

2017-04-01

The formation of necking zones and the associated formation of pinch-and-swell structure is one form of strain localization in extending, competent layers. Natural pinch-and-swell structure in centimetre-thick calcite layers typically shows a reduction of grain size from swell towards pinch. However, the impact of grain size evolution on necking and pinch-and-swell formation is incompletely understood. We perform zero-dimensional (0D) and 2D thermo-mechanical numerical simulations to quantify the impact of grain size evolution on necking for extension rates between 10-12s^-1and10^-14 s-1 and temperatures around 350°C. For a combination of diffusion and dislocation creep we calculate grain size evolution according to the paleowattmeter (grain size is proportional to mechanical work rate) or the paleopiezometer (grain size is proportional to stress). Numerical results fit two observations: (i) grain size reduction from swells towards pinches, and (ii) dislocation creep dominated deformation in swells and significant contribution of diffusion creep in pinches. Modelled grain size in pinches (10 to 60 μm) and swells (70 to 800 μm) is close to observed grain size in pinches (15 to 27 μm) and in swells (250 to 1500 μm). Grain size evolution has only a minor impact on necking suggesting that grain size evolution is a consequence, and not the cause of necking. Viscous shear heating and grain size evolution had a negligible thermal impact in the simulations.

Composition of bands in Argadnel Regio, Europa: Implications for Volcanic Resurfacing.

NASA Astrophysics Data System (ADS)

Prockter, L. M.; Shirley, J. H.; Dalton, J. B.; Kamp, L. W.

2012-04-01

Bands on Europa are dark or grey features which formed as a result of the pulling apart of cracks in Europa's surface, allowing new cryovolcanic material to be emplaced into the newly formed gaps. Bands have been shown to be sites of extensive resurfacing, and appear to have brightened over time, although the exact cause is not known. Thus the relative albedo of a band can be used as a proxy for age, as has been observed on Europa's surface, where the darkest bands crosscut, and are therefore younger than, lighter, or "grey" bands. We here combine Galileo Near-Infrared Mapping Spectrometer (NIMS) and Solid State Imager (SSI) data, using the methods of Shirley et al., [2010], to determine the surface compositions and water ice grain sizes of dark and grey bands in Europa's anti-Jovian Argadnel Regio, and to understand their relative histories. Preliminary results show that the total amount of hydrated salts modeled in the grey bands tends to be less than that seen in the dark bands (from ~19 to ~38% and ~38 to 47% respectively). One dark band contains hydrated sulfuric acid which is >5% lower than that of the surrounding ridged plains, as well as only 9% water ice of small grain size. These observations are interpreted as evidence that this band has been less processed by radiolysis, and so is relatively young or has been recently resurfaced. Relatively larger ice grain sizes are observed in the grey bands, as might be expected if they are older than the dark bands, and all the bands contain less large-grained ice than the surrounding ridged plains, thought to be the oldest unit on Europa's surface. We also find a wedge-shaped band that exhibits a different composition across its northern part, and appears to have undergone resurfacing as the result of the formation of a large, shallow trough that cuts diagonally across the band. We speculate that this resurfacing could be due to processes such as (1) the removal of frost due to surface shaking during the tectonic event, resulting in lower albedo material being revealed; (2) the emplacement of fine-grained plume or similar material due to a cryovolcanic eruption on the wedge floor; or (3) because the fault forming the southwestern wall of the depression intersected a near-surface briny reservoir, such as has been suggested to exist on Europa, enabling low-albedo material to be emplaced onto the floor of the depression, thereby darkening the wedge and modifying its surface composition. Reference: [1] Shirley J.H. et al. (2010) Icarus, 210, 358-384.

A continuum theory of grain size evolution and damage

NASA Astrophysics Data System (ADS)

Ricard, Y.; Bercovici, D.

2009-01-01

Lithospheric shear localization, as occurs in the formation of tectonic plate boundaries, is often associated with diminished grain size (e.g., mylonites). Grain size reduction is typically attributed to dynamic recrystallization; however, theoretical models of shear localization arising from this hypothesis are problematic because (1) they require the simultaneous action of two creep mechanisms (diffusion and dislocation creep) that occur in different deformation regimes (i.e., in grain size stress space) and (2) the grain growth ("healing") laws employed by these models are derived from normal grain growth or coarsening theory, which are valid in the absence of deformation, although the shear localization setting itself requires deformation. Here we present a new first principles grained-continuum theory, which accounts for both coarsening and damage-induced grain size reduction in a monomineralic assemblage undergoing irrecoverable deformation. Damage per se is the generic process for generation of microcracks, defects, dislocations (including recrystallization), subgrains, nuclei, and cataclastic breakdown of grains. The theory contains coupled macroscopic continuum mechanical and grain-scale statistical components. The continuum level of the theory considers standard mass, momentum, and energy conservation, as well as entropy production, on a statistically averaged grained continuum. The grain-scale element of the theory describes both the evolution of the grain size distribution and mechanisms for both continuous grain growth and discontinuous grain fracture and coalescence. The continuous and discontinuous processes of grain size variation are prescribed by nonequilibrium thermodynamics (in particular, the treatment of entropy production provides the phenomenological laws for grain growth and reduction); grain size evolution thus incorporates the free energy differences between grains, including both grain boundary surface energy (which controls coarsening) and the contribution of deformational work to these free energies (which controls damage). In the absence of deformation, only two mechanisms that increase the average grain size are allowed by the second law of thermodynamics. One mechanism, involving continuous diffusive mass transport from small to large grains, captures the essential components of normal grain growth theories of Lifshitz-Slyosov and Hillert. The second mechanism involves the aggregation of grains and is described using a Smoluchovski formalism. With the inclusion of deformational work and damage, the theory predicts two mechanisms for which the thermodynamic requirement of entropy positivity always forces large grains to shrink and small ones to grow. The first such damage-driven mechanism involving continuous mass transfer from large to small grains tends to homogenize the distribution of grain size toward its initial mean grain size. The second damage mechanism favors the creation of small grains by discontinuous division of larger grains and reduces the mean grain size with time. When considered separately, most of these mechanisms allow for self-similar grain size distributions whose scales (i.e., statistical moments such as the mean, variance, and skewness) can all be described by a single grain scale, such as the mean or maximum. However, the combination of mechanisms, e.g., one that captures the competition between continuous coarsening and mean grain size reduction by breakage, does not generally permit a self-similar solution for the grain size distribution, which contradicts the classic assumption that grain growth laws allowing for both coarsening and recrystallization can be treated with a single grain scale such as the mean size.

Complete grain boundaries from incomplete EBSD maps: the influence of segmentation on grain size determinations

NASA Astrophysics Data System (ADS)

Heilbronner, Renée; Kilian, Ruediger

2017-04-01

Grain size analyses are carried out for a number of reasons, for example, the dynamically recrystallized grain size of quartz is used to assess the flow stresses during deformation. Typically a thin section or polished surface is used. If the expected grain size is large enough (10 µm or larger), the images can be obtained on a light microscope, if the grain size is smaller, the SEM is used. The grain boundaries are traced (the process is called segmentation and can be done manually or via image processing) and the size of the cross sectional areas (segments) is determined. From the resulting size distributions, 'the grain size' or 'average grain size', usually a mean diameter or similar, is derived. When carrying out such grain size analyses, a number of aspects are critical for the reproducibility of the result: the resolution of the imaging equipment (light microscope or SEM), the type of images that are used for segmentation (cross polarized, partial or full orientation images, CIP versus EBSD), the segmentation procedure (algorithm) itself, the quality of the segmentation and the mathematical definition and calculation of 'the average grain size'. The quality of the segmentation depends very strongly on the criteria that are used for identifying grain boundaries (for example, angles of misorientation versus shape considerations), on pre- and post-processing (filtering) and on the quality of the recorded images (most notably on the indexing ratio). In this contribution, we consider experimentally deformed Black Hills quartzite with dynamically re-crystallized grain sizes in the range of 2 - 15 µm. We compare two basic methods of segmentations of EBSD maps (orientation based versus shape based) and explore how the choice of methods influences the result of the grain size analysis. We also compare different measures for grain size (mean versus mode versus RMS, and 2D versus 3D) in order to determine which of the definitions of 'average grain size yields the most stable results.

Grain size constraints on twin expansion in hexagonal close packed crystals

DOE PAGES

Kumar, Mariyappan Arul; Beyerlein, Irene Jane; Tome, Carlos N.

2016-10-20

Deformation twins are stress-induced transformed domains of lamellar shape that form when polycrystalline hexagonal close packed metals, like Mg, are strained. Several studies have reported that the propensity of deformation twinning reduces as grain size decreases. Here, we use a 3D crystal plasticity based micromechanics model to calculate the effect of grain size on the driving forces responsible for expanding twin lamellae. The calculations reveal that constraints from the neighboring grain where the grain boundary and twin lamella meet induce a stress reversal in the twin lamella. A pronounced grain size effect arises as reductions in grain size cause thesemore » stress-reversal fields from twin/grain boundary junctions to affect twin growth. We further show that the severity of this neighboring grain constraint depends on the crystallographic orientation and plastic response of the neighboring grain. We show that these stress-reversal fields from twin/grain boundary junctions will affect twin growth, below a critical parent grain size. Finally, these results reveal an unconventional yet influential role that grain size and grain neighbors can play on deformation twinning.« less

Mafic and felsic igneous rocks at Gale crater

NASA Astrophysics Data System (ADS)

Sautter, Violaine; Cousin, Agnès; Mangold, Nicolas; Toplis, Michael; Fabre, Cécile; Forni, Olivier; Payré, Valérie; Gasnault, Olivier; Ollila, Anne; Rapin, William; Fisk, Martin; Meslin, Pierre-Yves; Wiens, Roger; Maurice, Sylvestre; Lasue, Jérémie; Newsom, Horton; Lanza, Nina

2015-04-01

The Curiosity rover landed at Gale, an early Hesperian age crater formed within Noachian terrains on Mars. The rover encountered a great variety of igneous rocks to the west of the Yellow Knife Bay sedimentary unit (from sol 13 to 800) which are float rocks or clasts in conglomerates. Textural and compositional analyses using MastCam and ChemCam Remote micro Imager (RMI) and Laser Induced Breakdown Spectroscopy (LIBS) with a ˜300-500 µm laser spot lead to the recognition of 53 massive (non layered) igneous targets, both intrusive and effusive, ranging from mafic rocks where feldspars form less than 50% of the rock to felsic samples where feldspar is the dominant mineral. From morphology, color, grain size, patina and chemistry, at least 5 different groups of rocks have been identified: (1) a basaltic class with shiny aspect, conchoidal frature, no visible grains (less than 0.2mm) in a dark matrix with a few mm sized light-toned crystals (21 targets) (2) a porphyritic trachyandesite class with light-toned, bladed and polygonal crystals 1-20 mm in length set in a dark gray mesostasis (11 targets); (3) light toned trachytes with no visible grains sometimes vesiculated or forming flat targets (6 targets); (4) microgabbro-norite (grain size < 1mm) and gabbro-norite (grain size >1 mm) showing dark and light toned crystals in similar proportion ( 8 targets); (5) light-toned diorite/granodiorite showing coarse granular (>4 mm) texture either pristine or blocky, strongly weathered rocks (9 rock targets). Overall, these rocks comprise 2 distinct geochemical series: (i) an alkali-suite: basanite, gabbro trachy-andesite and trachyte) including porphyritic and aphyric members; (ii) quartz-normative intrusives close to granodioritic composition. The former looks like felsic clasts recently described in two SNC meteorites (NWA 7034 and 7533), the first Noachian breccia sampling the martian regolith. It is geochemically consistent with differentiation of liquids produced by low degrees of partial melting of the primitive martian mantle. The latter rock-type is unlike anything proposed in the literature for Mars but resembles Archean TTG's encountered on Earth related to the building of continental crust. This work thus provides the first in-situ detection of low density leucocratic igneous rocks on Mars in the southern highlands.

Thermal Infrared Spectra of a Suite of Forsterite Samples and Ab-initio Modelling of theirs Spectra

NASA Astrophysics Data System (ADS)

Maturilli, A.; Stangarone, C.; Helbert, J.; Tribaudino, M.; Prencipe, M.

2017-12-01

Forsterite is the dominating component in olivine, a major constituent in ultrafemic rocks, as well as planetary bodies. Messenger X-ray spectrometer has shown that Mg-rich silicate minerals, such as enstatite and forsterite, dominate Mercury's surface (Weider et al 2012). A careful and detailed acquaintance with the forsterite spectral features and their dependence wrt environmental conditions on Mercury is needed to interpret the remote sensing data from previous and forthcoming missions. We propose an experimental vs calculation approach to reproduce and describe the spectral features of forsterite. TIR emissivity measurements are performed by the Planetary Spectroscopy Laboratory (PSL) of DLR. PSL offers the unique capability to measure the emissivity of samples at temperature up to 1000K under vacuum conditions. TIR emissivity and reflectance measurements are performed on 11 olivine samples having a different composition within the forsterite-fayalite series. When available, the sample has been measured in 2 different grain sizes (<25µm and 125-250µm ranges). Emissivity measurements are taken for temperatures from 300K to 900K step 100K in the 1-100µm spectral range. Modelling is based on ab initio calculation techniques, which allow reproducing properties of crystals, at any P/T condition, with the least possible amount of a priori empirical information. Spectra are calculated evaluating vibrational frequencies at different volume cell, here 0K, 300K and 1000K (extreme situations), taking into account zero point effects. The aim of this work is to study experimentally the effects of temperature, composition and grain sizes on emissivity band minima shifts. The outcomes will benefit the modelling of emissivity spectra with ab initio methods, already successfully enabling to foresee the bands shift due to temperature and composition, but not taking into account band shape due to grain size variations. Considering the chameleon-like effects of Mercury surface already observed (Helbert et al. 2013), this study wants to point out the main spectral features due to the composition and temperature. Our results are used to create a theoretical background to interpret the high temperature infrared emissivity spectra from MERTIS onboard the ESA BepiColombo mission to Mercury (Helbert et al. 2010).

Magnetic properties of atmospheric PMx in a small settlement during heating and non-heating season

NASA Astrophysics Data System (ADS)

Petrovsky, E.; Kotlik, B.; Zboril, R.; Kapicka, A.; Grison, H.

2012-04-01

Magnetic properties of environmental samples can serve as fast and relatively cheap proxy method to investigate occurrence of iron oxides. These methods are very sensitive in detecting strongly magnetic compounds such as magnetite and maghemite and can reveal concentration and assess grain-size distribution of these minerals. This information can be significant in estimating e.g. the source of pollutants, monitoring pollution load, or investigating seasonal and climatic effects. We studied magnetic properties of PM1, PM2.5 and PM10, collected over 32-48 hours in a small settlement in south Bohemia during heating and non-heating season. The site is rather remote, with negligible traffic and industrial contributions to air pollution. Thus, the suggested seasonal effect should be dominantly due to local (domestic) heating, burning wood or coal. In our contribution we show typical differences in PMx concentration, which is much higher in the winter (heating) sample, accompanied by SEM analyses and magnetic data oriented on concentration and grain-size distribution of magnetite/maghemite particles. While concentration of Fe-oxides does not vary that much, significant seasonal differences were observed in composition and grain-size distribution, reflecting different sources of the dust particles.

Magnetic Force Microscopy Investigation of Magnetic Domains in Nd2Fe14B

NASA Astrophysics Data System (ADS)

Talari, Mahesh Kumar; Markandeyulu, G.; Rao, K. Prasad

2010-07-01

Remenance and coercivity in Nd2Fe14B materials are strongly dependent on the microstructural aspects like phases morphology and grain size. The coercivity (Hc) of a magnetic material varies inversely with the grain size (D) and there is a critical size below which Hc∝D6. Domain wall pinning by grain boundaries and foreign phases is the important mechanism in explaining the improvement in coercivity and remenance. Nd2Fe14B intermetallic compound with stochiometric composition was prepared from pure elements (Nd -99.5%, Fe—99.95%, B -99.99%) by arc melting in argon atmosphere. Magnetic Force Microscope (MFM) gives high-resolution magnetic domain structural information of ferromagnetic samples. DI-3100 Scanning Probe Microscope with MESP probes was used For MFM characterization of the samples. Magnetic domains observed in cast ingots were very long (up to 40 μm were observed) and approximately 1-5 μm wide due to high anisotropy of the compounds. Magnetic domains have displayed different image contrast and morphologies at different locations of the samples. The domain morphologies and image contrast obtained in this analysis were explained in this paper.

Microstructural Evolution of Nanocrystalline ZrO2 in a Fe Matrix During High-Temperature Exposure

NASA Astrophysics Data System (ADS)

Raghavendra, K. G.; Dasgupta, Arup; Athreya, C. N.; Jayasankar, K.; Saroja, S.; Subramanya Sarma, V.

2018-06-01

The current study examines the evolution of nanocrystallites of ZrO2 with time and temperature in a Fe-ZrO2 composite. The crystallite sizes were determined through X-ray peak broadening analysis by the Williamson-Hall method together with dark field transmission electron microscopy. The ZrO2 crystallites were found to be stable and retained their sizes at 973 K and 1073 K for hold durations up to 600 minutes. On the other hand, the crystallites were seen to grow at 1173 K and reached up to 200 nm for a hold time of 600 minutes. The Ostwald ripening model was adopted to understand crystallite growth while a dislocation-driven pipe diffusion was adopted for understanding the kinetics of grain growth. The activation energy of grain growth was calculated as 379 kJ mol-1. The modeled and experimentally calculated size evolutions with time and temperature were shown to be in good agreement with each other. A detailed discussion on the kinetics and activation energy of grain growth of ZrO2 crystallites in a Fe matrix is presented in this manuscript.

Noble gas isotopic composition, cosmic ray exposure history, and terrestrial age of the meteorite Allan Hills A81005 from the moon

NASA Astrophysics Data System (ADS)

Eugster, O.; Geiss, J.; Kraehenbuehl, U.; Niedermann, S.

1986-06-01

A comprehensive study of the elemental and isotopic abundances of the noble gases He, Ne, Ar, Kr, and Xe in the meteorite Allan Hills A81005 from the moon is presented. In addition to a bulk sample, five grain-size fractions were analyzed. Chemical abundances relevant to the interpretation of the cosmic-ray-produced noble gases were determined and indicate that the grain size fractions are chemically uniform. Except for the fact that the trapped noble gas concentrations appear to be grain size correlated, the isotopic and elemental pattern of the trapped solar wind noble gases in A81005 are very similar to those observed in lunar soils and breccias. The A81005 material resided during (580 + or - 180) Myr in the nuclear active zone of the lunar regolith at an average shielding depth of about 40 g/sq cm. From literature data, it is concluded that the moon-earth transit time lasted less than a few million years. Finally, A81005 was captured by the earth more than 140,000 years ago, as indicated by the abundance of cosmic-ray-produced Kr-81.

WIDE AND THICK GRAIN 1, which encodes an otubain-like protease with deubiquitination activity, influences grain size and shape in rice.

PubMed

Huang, Ke; Wang, Dekai; Duan, Penggen; Zhang, Baolan; Xu, Ran; Li, Na; Li, Yunhai

2017-09-01

Grain size and shape are two crucial traits that influence grain yield and grain appearance in rice. Although several factors that affect grain size have been described in rice, the molecular mechanisms underlying the determination of grain size and shape are still elusive. In this study we report that WIDE AND THICK GRAIN 1 (WTG1) functions as an important factor determining grain size and shape in rice. The wtg1-1 mutant exhibits wide, thick, short and heavy grains and also shows an increased number of grains per panicle. WTG1 determines grain size and shape mainly by influencing cell expansion. WTG1 encodes an otubain-like protease, which shares similarity with human OTUB1. Biochemical analyses indicate that WTG1 is a functional deubiquitinating enzyme, and the mutant protein (wtg1-1) loses this deubiquitinating activity. WTG1 is expressed in developing grains and panicles, and the GFP-WTG1 fusion protein is present in the nucleus and cytoplasm. Overexpression of WTG1 results in narrow, thin, long grains due to narrow and long cells, further supporting the role of WTG1 in determining grain size and shape. Thus, our findings identify the otubain-like protease WTG1 to be an important factor that determines grain size and shape, suggesting that WTG1 has the potential to improve grain size and shape in rice. © 2017 The Authors The Plant Journal © 2017 John Wiley & Sons Ltd.

Effect of the Angle Between Sn Grain c-Axis and Electron Flow Direction on Cu-Reinforced Composite Solder Joints Under Current Stressing

NASA Astrophysics Data System (ADS)

Wang, Yan; Han, Jing; Wang, Yishu; Ma, Limin; Guo, Fu

2018-01-01

With a body-centered tetragonal crystal structure, Sn grains were demonstrated to have highly anisotropic behaviors in various properties. The electromigration behavior of lead-free solder was impacted by the grain orientations. In this paper, the angle between the c-axis and the electron flow direction in composite solder joints (angle θ) was proven to be an important factor during electromigration. The effects of angle θ on the electromigration of composite solder joints were investigated in this paper. Cu particle-reinforced Sn3.5Ag solder joints were stressed under a current density of 104 A/cm2 at room temperature. After 336 h current stressing time, different electromigration phenomena occurred at the two sides of the grain boundary in the composite solder joint which contained two Sn grains with different angle θ. The Sn grains with the larger angle θ had a smaller growth rate of Cu6Sn5. In addition, a composite solder joint with a single Sn grain was set as the contrast and its angle θ was smaller than that of the composite solder joint with two Sn grains. The growth rate of Cu6Sn5 in the composite solder joint with a single grain was faster than that of the composite solder joint with two Sn grains.

SCR and GCR exposure ages of plagioclase grains from lunar soil

NASA Technical Reports Server (NTRS)

Etique, P.; Baur, H.; Signer, P.; Wieler, R.

1986-01-01

The concentrations of solar wind implanted Ar-36 in mineral grains extracted from lunar soils show that they were exposed to the solar wind on the lunar surface for an integrated time of 10E4 to 10E5 years. From the bulk soil 61501 plagioclase separates of 8 grain size ranges was prepared. The depletion of the implanted gases was achieved by etching aliquot samples of 4 grain sizes to various degrees. The experimental results pertinent to the present discussion are: The spallogenic Ne is, as in most plagioclases from lunar soils, affected by diffusive losses and of no use. The Ar-36 of solar wind origin amounts to (2030 + or - 100) x 10E-8 ccSTP/g in the 150 to 200 mm size fraction and shows that these grains were exposed to the solar wind for at least 10,000 years. The Ne-21/Ne-22 ratio of the spallogenic Ne is 0.75 + or - 0.01 and in very good agreement with the value of this ratio in a plagioclase separate from rock 76535. This rock has had a simple exposure history and its plagioclases have a chemical composition quite similar to those studied. In addition to the noble gases, the heavy particle tracks in an aliquot of the 150 to 200 mm plagioclase separate were investigated and found 92% of the grains to contain more than 10E8 tracks/sq cm. This corresponds to a mean track density of (5 + or - 1) x 10E8 tracks/sq cm. The exploration of the exposure history of the plagioclase separates from the soil 61501 do not contradict the model for the regolith dynamics but also fail to prove it.

Effect of Sn Content in a CuSnZn Metal Precursor on Formation of MoSe2 Film during Selenization in Se+SnSe Vapor

PubMed Central

Yao, Liyong; Ao, Jianping; Jeng, Ming-Jer; Bi, Jinlian; Gao, Shoushuai; Sun, Guozhong; He, Qing; Zhou, Zhiqiang; Sun, Yun; Chang, Liann-Be

2016-01-01

The preparation of Cu2ZnSnSe4 (CZTSe) thin films by the selenization of an electrodeposited copper–tin–zinc (CuSnZn) precursor with various Sn contents in low-pressure Se+SnSex vapor was studied. Scanning electron microscope (SEM) and energy dispersive spectroscopy (EDS) measurements revealed that the Sn content of the precursor that is used in selenization in a low-pressure Se+SnSex vapor atmosphere only slightly affects the elemental composition of the formed CZTSe films. However, the Sn content of the precursor significantly affects the grain size and surface morphology of CZTSe films. A metal precursor with a very Sn-poor composition produces CZTSe films with large grains and a rough surface, while a metal precursor with a very Sn-rich composition procures CZTSe films with small grains and a compact surface. X-ray diffraction (XRD) and SEM revealed that the metal precursor with a Sn-rich composition can grow a thicker MoSe2 thin film at CZTSe/Mo interface than one with a Sn-poor composition, possibly because excess Sn in the precursor may catalyze the formation of MoSe2 thin film. A CZTSe solar cell with an efficiency of 7.94%was realized by using an electrodeposited metal precursor with a Sn/Cu ratio of 0.5 in selenization in a low-pressure Se+SnSex vapor. PMID:28773366

Igneous fractionation and subsolidus equilibration of diogenite meteorites

NASA Technical Reports Server (NTRS)

Mittlefehldt, David W.

1993-01-01

Diogenites are coarse-grained orthopyroxenite breccias of remarkably uniform major element composition. Most diogenites contain homogeneous pyroxene fragments up to 5 cm across of Wo2En74Fs24 composition. Common minor constituents are chromite, olivine, trolite and metal, while silica, plagioclase, merrillite and diopside are trace phases. Diogenites are generally believed to be cumulates from the eucrite parent body, although their relationship with eucrites remains obscure. It has been suggested that some diogenites are residues after partial melting. I have performed EMPA and INAA for major, minor and trace elements on most diogenites, concentrating on coarse-grained mineral and lithic clasts in order to elucidate their igneous formation and subsequent metamorphic history. Major element compositions of diogenites are decoupled from minor and trace element compositions; the latter record an igneous fractionation sequence that is not preserved in the former. Low equilibration temperatures indicate that major element diffusion continued long after crystallization. Diffusion coefficients for trivalent and tetravalent elements in pyroxene are lower than those of divalent elements. Therefore, major element compositions of diogenites may represent means of unknown portions of a cumulate homogenized by diffusion, while minor and trace elements still yield information on their igneous history. The scale of major element equilibration is unknown, but is likely to be on the order of a few cm. Therefore, the diogenite precursors may have consisted largely of cm-sized, igneously zoned orthopyroxene grains, which were subsequently annealed during slow cooling, obliterating major element zoning but preserving minor and trace incompatible element zoning.

Microstructure and mechanical properties of AZ91 magnesium alloy subject to deep cryogenic treatments

NASA Astrophysics Data System (ADS)

Li, Gui-rong; Wang, Hong-ming; Cai, Yun; Zhao, Yu-tao; Wang, Jun-jie; Gill, Simon P. A.

2013-09-01

AZ91 magnesium alloy was subjected to a deep cryogenic treatment. X-ray diffraction (XRD), scanning electronic microscopy (SEM), and transmission electronic microscopy (TEM) methods were utilized to characterize the composition and microstructure of the treated samples. The results show that after two cryogenic treatments, the quantity of the precipitate hardening β phase increases, and the sizes of the precipitates are refined from 8-10 μm to 2-4 μm. This is expected to be due to the decreased solubility of aluminum in the matrix at low temperature and the significant plastic deformation owing to internal differences in thermal contraction between phases and grains. The polycrystalline matrix is also noticeably refined, with the sizes of the subsequent nanocrystalline grains in the range of 50-100 nm. High density dislocations are observed to pile up at the grain boundaries, inducing the dynamic recrystallization of the microstructure, leading to the generation of a nanocrystalline grain structure. After two deep cryogenic treatments, the tensile strength and elongation are found to be substantially increased, rising from 243 MPa and 4.4% of as-cast state to 299 MPa and 5.1%.

Development of low-Cr ODS FeCrAl alloys for accident-tolerant fuel cladding

NASA Astrophysics Data System (ADS)

Dryepondt, Sebastien; Unocic, Kinga A.; Hoelzer, David T.; Massey, Caleb P.; Pint, Bruce A.

2018-04-01

Low-Cr oxide dispersion strengthened (ODS) FeCrAl alloys were developed as accident tolerant fuel cladding because of their excellent oxidation resistance at very high temperature, high strength and improved radiation tolerance. Fe-12Cr-5Al wt.% gas atomized powder was ball milled with Y2O3+FeO, Y2O3+ZrO2 or Y2O3+TiO2, and the resulting powders were extruded at 950 °C. The resulting fine grain structure, particularly for the Ti and Zr containing alloys, led to very high strength but limited ductility. Comparison with variants of commercial PM2000 (Fe-20Cr-5Al) highlighted the significant impact of the powder consolidation step on the alloy grain size and, therefore, on the alloy mechanical properties at T < 500 °C. These low-Cr compositions exhibited good oxidation resistance at 1400 °C in air and steam for 4 h but could not form a protective alumina scale at 1450 °C, similar to observations for fine grained PM2000 alloys. The effect of alloy grain size, Zr and Ti additions, and impurities on the alloy mechanical and oxidation behaviors are discussed.

The effect of grain size and cement content on index properties of weakly solidified artificial sandstones

NASA Astrophysics Data System (ADS)

Atapour, Hadi; Mortazavi, Ali

2018-04-01

The effects of textural characteristics, especially grain size, on index properties of weakly solidified artificial sandstones are studied. For this purpose, a relatively large number of laboratory tests were carried out on artificial sandstones that were produced in the laboratory. The prepared samples represent fifteen sandstone types consisting of five different median grain sizes and three different cement contents. Indices rock properties including effective porosity, bulk density, point load strength index, and Schmidt hammer values (SHVs) were determined. Experimental results showed that the grain size has significant effects on index properties of weakly solidified sandstones. The porosity of samples is inversely related to the grain size and decreases linearly as grain size increases. While a direct relationship was observed between grain size and dry bulk density, as bulk density increased with increasing median grain size. Furthermore, it was observed that the point load strength index and SHV of samples increased as a result of grain size increase. These observations are indirectly related to the porosity decrease as a function of median grain size.

A brittle to ductile transition in NiAl of a critical grain size

NASA Technical Reports Server (NTRS)

Schulson, E. M.; Barker, D. R.

1983-01-01

Tensile tests have been carried out on the strongly ordered B2 aluminide NiAl at 400 C to investigate the effect of the grain size on the ductility of the material. It is found that the ductility is very low and essentially independent of the grain size for aggregates of grains larger than about 20 microns; for finer-grained aggregates, the ductility increases sharply with decreasing grain size. Thus, NiAl exhibits a critical grain size below which polycrystalline aggregates are ductile in tension. For all grain sizes, fracture occurs in a brittle manner through a combination of intergranular decohesion and transgranular cleavage.

Elemental Analysis of Beryllium Samples Using a Microzond-EGP-10 Unit

NASA Astrophysics Data System (ADS)

Buzoverya, M. E.; Karpov, I. A.; Gorodnov, A. A.; Shishpor, I. V.; Kireycheva, V. I.

2017-12-01

Results concerning the structural and elemental analysis of beryllium samples obtained via different technologies using a Microzond-EGP-10 unit with the help of the PIXE and RBS methods are presented. As a result, the overall chemical composition and the nature of inclusions were determined. The mapping method made it possible to reveal the structural features of beryllium samples: to select the grains of the main substance having different size and chemical composition, to visualize the interfaces between the regions of different composition, and to describe the features of the distribution of impurities in the samples.

Monochromatic, Rosseland mean, and Planck mean opacity routine

NASA Astrophysics Data System (ADS)

Semenov, D.

2006-11-01

Several FORTRAN77 codes were developed to compute frequency-dependent, Rosseland and Planck mean opacities of gas and dust in protoplanetary disks. The opacities can be computed for an ensemble of dust grains having various compositions (ices, silicates, organics, etc), sizes, topologies (homogeneous/composite aggregates, homogeneous/layered/composite spheres, etc.), porosities, and dust-to-gas ratio. Several examples are available. In addition, a very fast opacity routine to be used in modeling of the radiative transfer in hydro simulations of disks is available upon request (10^8 routine calls require about 30s on Pentium 4 3.0GHz).

Uppermost impact fallback layer in the Bosumtwi crater (Ghana): Mineralogy, geochemistry, and comparison with Ivory Coast tektites

NASA Astrophysics Data System (ADS)

Koeberl, Christian; Brandstätter, Franz; Glass, Billy P.; Hecht, Lutz; Mader, Dieter; Reimold, Wolf Uwe

In 2004, an International Continental Scientific Drilling Program (ICDP) drilling project at the Bosumtwi impact crater, Ghana (10.5 km in diameter, 1.07 Myr old), was performed to study the sediments that fill the lake as well as the underlying impactites. In one (LB-05) of 16 cores drilled into the lake sediments, the zone between the impact breccias and the post-impact sediments was penetrated, preserving the final, fine-grained impact fallback layer. This ~30 cm thick layer contains in the top 10 cm “accretionary” lapilli, microtektite-like glass spherules, and shocked quartz grains. Glass particles -- mostly of splash form less than 1 mm size -- make up the bulk of the grains (~70-78% by number) in the coarser size fraction (>125 μm) of the top of the fallback layer. About one-third of all quartz grains in the uppermost part of the layer are shocked, with planar deformation features (PDFs); almost half of these grains are highly shocked, with 3 or more sets of PDFs. K-feldspar grains also occur and some show shock deformation. The abundance of shocked quartz grains and the average shock level as indicated by the number of sets of PDFs, for both quartz and K-feldspar, decrease with depth into the layer. The well-preserved glass spherules and fragments are chemically rather homogeneous within each particle, and also show relatively small variations between the various particles. On average, the composition of the fallback spherules from core LB-5B is very similar to the composition of Ivory Coast tektites and microtektites, with the exception of CaO contents, which are about 1.5 to 2 times higher in the fallback spherules. This is a rare case in which the uppermost fallback layer and the transition to the post-impact sediments has been preserved in an impact structure; its presence indicates that the impactite sequence at Bosumtwi is complete and that Bosumtwi is a very well-preserved impact crater.

Microstructural Evaluation of Forging Parameters for Superalloy Disks

NASA Technical Reports Server (NTRS)

Falsey, John R.

2004-01-01

Forgings of nickel base superalloy were formed under several different strain rates and forging temperatures. Samples were taken from each forging condition to find the ASTM grain size, and the as large as grain (ALA). The specimens were mounted in bakelite, polished, etched and then optical microscopy was used to determine grain size. The specimens ASTM grain sizes from each forging condition were plotted against strain rate, forging temperature, and presoak time. Grain sizes increased with increasing forging temperature. Grain sizes also increased with decreasing strain rates and increasing forging presoak time. The ALA had been determined from each forging condition using the ASTM standard method. Each ALA was compared with the ASTM grain size of each forging condition to determine if the grain sizes were uniform or not. The forging condition of a strain rate of .03/sec and supersolvus heat treatment produced non uniform grains indicated by critical grain growth. Other anomalies are noted as well.

Composite grain size sensitive and grain size insensitive creep of bischofite, carnallite and mixed bischofite-carnallite-halite salt rock

NASA Astrophysics Data System (ADS)

Muhammad, Nawaz; de Bresser, Hans; Peach, Colin; Spiers, Chris

2016-04-01

Deformation experiments have been conducted on rock samples of the valuable magnesium and potassium salts bischofite and carnallite, and on mixed bischofite-carnallite-halite rocks. The samples have been machined from a natural core from the northern part of the Netherlands. Main aim was to produce constitutive flow laws that can be applied at the in situ conditions that hold in the undissolved wall rock of caverns resulting from solution mining. The experiments were triaxial compression tests carried out at true in situ conditions of 70° C temperature and 40 MPa confining pressure. A typical experiment consisted of a few steps at constant strain rate, in the range 10-5 to 10-8 s-1, interrupted by periods of stress relaxation. During the constant strain rate part of the test, the sample was deformed until a steady (or near steady) state of stress was reached. This usually required about 2-4% of shortening. Then the piston was arrested and the stress on the sample was allowed to relax until the diminishing force on the sample reached the limits of the load cell resolution, usually at a strain rate in the order of 10-9 s-1. The duration of each relaxation step was a few days. Carnallite was found to be 4-5 times stronger than bischofite. The bischofite-carnallite-halite mixtures, at their turn, were stronger than carnallite, and hence substantially stronger than pure bischofite. For bischofite as well as carnallite, we observed that during stress relaxation, the stress exponent nof a conventional power law changed from ˜5 at strain rate 10-5 s-1 to ˜1 at 10-9 s-1. The absolute strength of both materials remained higher if relaxation started at a higher stress, i.e. at a faster strain rate. We interpret this as indicating a difference in microstructure at the initiation of the relaxation, notably a smaller grain size related to dynamical recrystallization during the constant strain rate step. The data thus suggest that there is a gradual change in deformation mechanism with decreasing strain rate for both bischofite and carnallite, from grain size insensitive (GSI) dislocation creep at the higher strain rates to grain size sensitive (GSS, i.e. pressure solution) creep at slow strain rate. We can speculate about the composite GSI-GSS nature of the constitutive laws describing the creep of the salt materials.

An experimental and modeling study of grain-scale uranium desorption from field-contaminated sediments and the potential influence of microporosity on mass-transfer

NASA Astrophysics Data System (ADS)

Stoliker, D.; Liu, C.; Kent, D. B.; Zachara, J. M.

2012-12-01

The aquifer below the 300-Area of the Hanford site (Richland, WA, USA) is plagued by a persistent plume of dissolved uranium (U(VI)) in excess of the Environmental Protection Agency drinking water maximum contamination level even after the removal of highly contaminated sediments. The aquifer sediments in the seasonally saturated lower vadose zone act as both a source and sink for uranium during stage changes in the nearby Columbia River. Diffusion limitation of uranium mass-transfer within these sediments has been cited as a potential cause of the plume's persistence. Equilibrium U(VI) sorption is a strong function of variable chemical conditions, especially carbonate, hydrogen, and uranyl ion activities. Field-contaminated sediments from the site require up to 1,000 hours to reach equilibrium in static batch reactors. Increases in U(VI) concentrations over longer time-scales result from changes in chemical conditions, which drive reactions with sediments that favor U(VI) desorption. Grain-scale U(VI) sorption/desorption rates are slow, likely owing to diffusion of U(VI) and other solutes through intra-granular pore domains. In order to improve understanding of the impact of intra-granular diffusion and chemical reactions controlling grain-scale U(VI) release, experiments were conducted on individual particle size fractions of a <8 mm composite of field-contaminated, lower vadose zone sediments. For each size fraction, equilibrium U(VI) sorption/desorption in static batch reactors was well-described by surface complexation models over a range of chemical conditions applicable to the field site. Desorption rates from individual size fractions in flow-through batch reactors, examined under a single set of constant chemical conditions with multiple stop-flow events, were similar for all size fractions <2 mm. Kinetic U(VI) desorption in flow-through batch reactors was modeled using a multi-rate surface complexation approach, where sorption/desorption rates were assumed to be proportional to the displacement from equilibrium and multiple diffusion domains were described with a two-parameter lognormal distribution of mass-transfer rate coefficients. Parameters describing mass transfer were the same for all size fractions <2 mm but differed for the largest (2-8 mm) size fraction. The evolution of pH, along with dissolved cation and carbonate concentrations, was modeled using equilibrium cation exchange, rate-limited calcite dissolution, aerobic respiration, and silica dissolution. Desorption and chemical reaction models calibrated with individual size fractions predicted U(VI) and chemical composition as a function of time for the bulk sediment sample. Volumes of pores less than 2.4 nm, quantified using nitrogen adsorption-desorption isotherms, were the same for all size fractions < 2 mm, nearly double that of the 2-8 mm size fraction. Similarity in the observed pore volumes and multi-rate mass-transfer parameters across all size fractions <2 mm suggest the importance of pores in this size class in controlling slow grain-scale U(VI) desorption rates. Models like these provide a means for testing the influence of grain-scale mass-transfer on the persistence of U(VI) plume at the site.

Spectrophotometry of Dust in Comet Hale-Bopp

NASA Technical Reports Server (NTRS)

Witteborn, Fred C. (Technical Monitor)

1997-01-01

Comets, such as Hale-Bopp (C/1995 O1), are frozen reservoirs of primitive solar nebula dust grains and ices. Analysis of the composition of cometary dust grains from infrared spectroscopic techniques permits an estimation of the types of organic and inorganic materials that constituted the early primitive solar nebula. In addition, the cometary bombardment of the Earth (approximately 3.5 Gy ago) supplied the water for the oceans and brought organic materials to Earth which may have been biogenic. Spectroscopic observations of comet Hale-Bopp suggest the possible presence of organic hydrocarbon species, silicate and olivine dust grains, and water ice. Spectroscopy near 3 microns obtained in Nov 1996 r=2.393 AU, delta=3.034 AU) shows a feature which we attribute to PAH emission. The spatial morphology of the 3.28 microns PAH feature is also presented. Optical and infrared spectrophotometric observations of comets convey valuable information about the spatial distribution and properties of dust and gas within the inner coma. In the optical and NIR shortward of 2 microns, the observed light is primarily scattered sunlight from the dust grains. At longer wavelengths, particularly in the 10 gm window, thermal emission from these grains dominates the radiation allowing an accurate estimate of grain sizes and chemical composition. Here we present an initial analysis of spectra taken with the NASA HIFOGS at 7-14 microns as part of a multiwavelength temporal study of the "comet of the century".

MAHLI at the Rocknest sand shadow: Science and science-enabling activities

NASA Astrophysics Data System (ADS)

Minitti, M. E.; Kah, L. C.; Yingst, R. A.; Edgett, K. S.; Anderson, R. C.; Beegle, L. W.; Carsten, J. L.; Deen, R. G.; Goetz, W.; Hardgrove, C.; Harker, D. E.; Herkenhoff, K. E.; Hurowitz, J. A.; Jandura, L.; Kennedy, M. R.; Kocurek, G.; Krezoski, G. M.; Kuhn, S. R.; Limonadi, D.; Lipkaman, L.; Madsen, M. B.; Olson, T. S.; Robinson, M. L.; Rowland, S. K.; Rubin, D. M.; Seybold, C.; Schieber, J.; Schmidt, M.; Sumner, D. Y.; Tompkins, V. V.; Van Beek, J. K.; Van Beek, T.

2013-11-01

Martian solar days 57-100, the Mars Science Laboratory Curiosity rover acquired and processed a solid (sediment) sample and analyzed its mineralogy and geochemistry with the Chemistry and Mineralogy and Sample Analysis at Mars instruments. An aeolian deposit—herein referred to as the Rocknest sand shadow—was inferred to represent a global average soil composition and selected for study to facilitate integration of analytical results with observations from earlier missions. During first-time activities, the Mars Hand Lens Imager (MAHLI) was used to support both science and engineering activities related to sample assessment, collection, and delivery. Here we report on MAHLI activities that directly supported sample analysis and provide MAHLI observations regarding the grain-scale characteristics of the Rocknest sand shadow. MAHLI imaging confirms that the Rocknest sand shadow is one of a family of bimodal aeolian accumulations on Mars—similar to the coarse-grained ripples interrogated by the Mars Exploration Rovers Spirit and Opportunity—in which a surface veneer of coarse-grained sediment stabilizes predominantly fine-grained sediment of the deposit interior. The similarity in grain size distribution of these geographically disparate deposits support the widespread occurrence of bimodal aeolian transport on Mars. We suggest that preservation of bimodal aeolian deposits may be characteristic of regions of active deflation, where winnowing of the fine-sediment fraction results in a relatively low sediment load and a preferential increase in the coarse-grained fraction of the sediment load. The compositional similarity of Martian aeolian deposits supports the potential for global redistribution of fine-grained components, combined with potential local contributions.

Effects of ultrasonic vibration on microstructure and mechanical properties of nano-sized SiC particles reinforced Al-5Cu composites.

PubMed

Li, Jianyu; Lü, Shulin; Wu, Shusen; Gao, Qi

2018-04-01

Ultrasonic vibration (UV) treatment has been successfully applied to improve the particles distribution of nano-sized SiC particles (SiC p ) reinforced Al-5Cu alloy matrix composites which were prepared by combined processes of dry high energy ball milling and squeeze casting. When UV treatment is applied, the distribution of nano-sized SiC p has been greatly improved. After UV for 1 min, large particles aggregates are broken up into small aggregates due to effects of cavitation and the acoustic streaming. After UV for 5 min, all the particles aggregates are dispersed and the particles are uniformly distributed in the composites. Compared with the Al-5Cu matrix alloy, the ultimate tensile strength, yield strength and elongation of the 1 wt% nano-sized SiC p /Al-5Cu composites treated by UV for 5 min are 270 MPa, 173 MPa and 13.3%, which are increased by 7.6%, 6.8% and 29%, respectively. The improvements of mechanical properties after UV are attributed to the uniform distribution of nano particles, grain refinement of aluminum matrix alloy and reduction of porosity in the composites. Copyright © 2017 Elsevier B.V. All rights reserved.

Electrochemical Synthesis of Core-Shell-Structured NbC-Fe Composite Powder for Enforcement in Low-Carbon Steel.

PubMed

Li, Hongmei; Song, Qiushi; Xu, Qian; Chen, Ying; Xu, Liang; Man, Tiannan

2017-11-01

An NbC-Fe composite powder was synthesized from an Nb₂O₅/Fe/C mixture by electrochemical reduction and subsequent carbonization in molten CaCl₂-NaCl. The composite has a core-shell structure, in which NbC acts as the cores distributing in the Fe matrix. A strong bonding between NbC and Fe is benefit from the core-shell structure. The sintering and electrochemical reduction processes were investigated to probe the mechanism for the reactions. The results show that NbC particles about several nanometers were embraced by the Fe shell to form a composite about 100 nm in size. This featured structure can feasibly improve the wettability and sinterability of NbC as well as the uniform distribution of the carbide in the cast steel. By adding the composite into steel in the casting process, the grain size of the casted steel was markedly deceased from 1 mm to 500 μm on average, favoring the hardening of the casted steel.

Compositional and Microtextural Analysis of Basaltic Feedstock Materials Used for the 2010 ISRU Field Tests, Mauna Kea, Hawaii

NASA Astrophysics Data System (ADS)

Marin, N.; Farmer, J. D.; Zacny, K.; Sellar, R. G.; Nunez, J.

2011-12-01

This study seeks to understand variations in composition and texture of basaltic pyroclastic materials used in the 2010 International Lunar Surface Operation-In-Situ Resource Utilization Analogue Test (ILSO-ISRU) held on the slopes of Mauna Kea Volcano, Hawaii (1). The quantity and quality of resources delivered by ISRU depends upon the nature of the materials processed (2). We obtained a one-meter deep auger cuttings sample of a basaltic regolith at the primary site for feed stock materials being mined for the ISRU field test. The auger sample was subdivided into six, ~16 cm depth increments and each interval was sampled and characterized in the field using the Multispectral Microscopic Imager (MMI; 3) and a portable X-ray Diffractometer (Terra, InXitu Instruments, Inc.). Splits from each sampled interval were returned to the lab and analyzed using more definitive methods, including high resolution Powder X-ray Diffraction and Thermal Infrared (TIR) spectroscopy. The mineralogy and microtexture (grain size, sorting, roundness and sphericity) of the auger samples were determined using petrographic point count measurements obtained from grain-mount thin sections. NIH Image J (http://rsb.info.nih.gov/ij/) was applied to digital images of thin sections to document changes in particle size with depth. Results from TIR showed a general predominance of volcanic glass, along with plagioclase, olivine, and clinopyroxene. In addition, thin section and XRPD analyses showed a down core increase in the abundance of hydrated iron oxides (as in situ weathering products). Quantitative point count analyses confirmed the abundance of volcanic glass in samples, but also revealed olivine and pyroxene to be minor components, that decreased in abundance with depth. Furthermore, point count and XRD analyses showed a decrease in magnetite and ilmenite with depth, accompanied by an increase in Fe3+phases, including hematite and ferrihydrite. Image J particle analysis showed that the average grain size decreased down the depth profile. This decrease in average grain size and increase in hydrated iron oxides down hole suggests that the most favorable ISRU feedstock materials were sampled in the lower half-meter of the mine section sampled.

10 years of Cassini/VIMS observations at Titan

NASA Astrophysics Data System (ADS)

Sotin, C.; Brown, R. H.; Baines, K. H.; Barnes, J.; Buratti, B. J.; Clark, R. N.; Jaumann, R.; LeMouelic, S.; Nicholson, P. D.; Rodriguez, S.; Soderblom, J.; Soderblom, L.; Stephan, K.

2014-04-01

The interplanetary space probe Cassini/Huygens reached Saturn in July 2004 after seven years of cruise phase. Today, the German-lead Cosmic Dust Analyser (CDA) is operated continuously for 10 years in orbit around Saturn. During the cruise phase CDA measured the interstellar dust flux at one AU distance from the Sun, the charge and composition of interplanetary dust grains and the composition of the Jovian nanodust streams. The first discovery of CDA related to Saturn was the measurement of nanometer sized dust particles ejected by its magnetosphere to interplanetary space with speeds higher than 100 km/s. Their origin and composition was analysed and an their dynamical studies showed a strong link to the conditions of the solar wind plasma flow. A recent surprising result was, that stream particles stem from the interior of Enceladus. Since 2004 CDA measured millions of dust impacts characterizing the dust environment of Saturn. The instrument showed strong evidence for ice geysers located at the south pole of Saturn's moon Enceladus in 2005. Later, a detailed compositional analysis of the salt-rich water ice grains in Saturn's E ring system lead to the discovery of liquid water below the icy crust connected to an ocean at depth feeding the icy jets. CDA was even capable to derive a spatially resolved compositional profile of the plume during close Enceladus flybys. A determination of the dust-magnetosphere interaction and the discovery of the extended E ring allowed the definition of a dynamical dust model of Saturn's E ring describing the observed properties. The measured dust density profiles in the dense E ring revealed geometric asymmetries. Cassini performed shadow crossings in the ring plane and dust grain charges were measured in shadow regions delivering important data for dust-plasma interaction studies. In the last years, dedicated measurement campaigns were executed by CDA to monitor the flux of interplanetary and interstellar dust particles reaching Saturn. Currently, the composition of interstellar grains and the meteoroid flux into the Saturnian system are in analysis.

Discrete dipole approximation models of chrystalline forsterite: Applications to cometary crystalline silicates

NASA Astrophysics Data System (ADS)

Lindsay, Sean Stephen

The shape, size, and composition of crystalline silicates observed in comet comae and external proto-planetary disks are indicative of the formation and evolution of the dust grains during the processes of planetary formation. In this dissertation, I present the 3 -- 40 mum absorption efficiencies( Qabs) of irregularly shaped forsterite crystals computed with the discrete dipole approximation (DDA) code DDSCAT developed by Draine and Flatau and run on the NASA Advanced Supercomputing facility Pleiades. An investigation of grain shapes ranging from spheroidal to irregular indicate that the strong spectral features from forsterite are sensitive to grain shape and are potentially degenerate with the effects of crystal solid state composition (Mg-content). The 10, 11, 18, 23, and 33.5 mum features are found to be the most crystal shape sensitive and should be avoided in determining Mg-content. The distinct spectral features for the three shape classes are connected with crystal formation environment using a condensation experiment by (Kobatake et al., 2008). The condensation experiment demonstrates that condensed forsterite crystal shapes are dependent on the condensation environmental temperature. I generate DDSCAT target analog shapes to the condensed crystal shapes. These analog shapes are represented by the three shape classes: 1) equant, 2) a, c-columns, and 3) b-shortened platelets. Each of these shape classes exhibit distinct spectral features that can be used to interpret grain shape characteristics from 8 --- 40 mum spectroscopy of astronomical objects containing crystalline silicates. Synthetic spectral energy distributions (SEDs) of the coma of Hale-Bopp at rh = 2.8 AU are generated by thermally modeling the flux contributions of 5 mineral species present in comets. The synthetic SEDs are constrained using a chi2- minimization technique. The mineral species are amorphous carbon, amorphous pyroxene, amorphous olivine, crystalline enstatite, and crystalline forsterite. Using the DDSCAT computed absorption efficiencies for a large variety of forsterite crystal shapes, which are computed for 66 grain sizes between 0.1 -- 5.0 mum, the flux contribution of irregularly shaped forsterite is computed. The forsterite flux contribution is then summed with the amorphous and crystalline enstatite contributions to generate the total synthetic SED. The DDSCAT forsterite grain shape synthetic SEDs reveal that the crystalline silicates in the coma of Hale-Bopp are irregular in shape with two distinct shape characteristics related to specific formation mechanisms: 1) equant grains with sharp ( ≲ 90°) angles between the faces, edges, and vertices that formed as high temperature condensates in the inner 1 -- 3 AU radial region of the Solar System's protoplanetary disk; and 2) c-shortened platelet shapes that likely formed from collisional processing of the crystals. The 8 -- 40 mum silicate spectral features of Hale-Bopp's coma are compared to the silicate spectral features of the comae of 17P/Holmes during 2007 outburst and 9P/Tempel 1 during the Deep Impact experiment to show that the silicate features with crystalline resonances are remarkably similar. The similarity in silicate spectral features suggests that the grain populations in the comae of these comets are similar in shape, size, and compositon. However, Hale-Bopp is a nearly isotropic comet (NIC) that dynamically came from the Oort cloud, and 17P and 9P are ecliptic comets (ECs) that dynamically came from the Scattered Disk. The different dynamical source regions yet similar silicate (amorphous and crystalline) grain populations suggest that ECs and NICs innately have similar grains and that the typically weaker silicate features of ECs are an effect of the surface grains becoming compacted with numerous perihelion passages. Hence, the differences in silicate between ECs and NICs are the result of grain structure and not grain composition. (Abstract shortened by UMI.)

Meteoritical Society Annual Meeting, 57th, Prague, Czech Republic, July 25-29, 1994. [Abstracts only

NASA Technical Reports Server (NTRS)

1994-01-01

Ranging in size from mere grains and palm-size stones to boulders and many-mile- wide hunks of rock, meteorites hold many secrets of our solar system, and indeed of our universe. The 57th Annual Meeting of the Meteoritical Society discussed many aspects of this fascinating 'chunk' of the evolution of the Solar System. Topics covered included: chemical composition, meteorite types, meteorite age determination, meteorite origins, and find locations, as well as a multitude of other important subjects.

The microstructure and properties of rapidly solidified, dispersion-strengthened NiAl

NASA Technical Reports Server (NTRS)

Jha, S. C.; Ray, R.

1990-01-01

An advanced rapid solidification technology for processing reactive and refractory alloys, utilized to produce large quantities of melt-spun filaments of NiAl, is presented. The melt-spun filaments are pulverized to fine particle sizes, and subsequently consolidated by hot extrusion or hot isostatic pressing. Rapid solidification process gives rise to very fine-grained microstructures. However, exposure to elevated temperature during hot consolidation leads to grain growth. Alloying agents such as borides, carbides, and tungsten can pin the grain boundaries and retard the grain growth. Various alloy compositions are investigated. The eventual goal is to utilize the hot-extruded and forged stock to grow single-crystal NiAl blades for advanced gas-turbine engine applications. Single-crystal NiAl, containing a uniform dispersion of carbide strengthening precipitates, is expected to lead to highly creep-resistant turbine blades, and is of considerable interest to the aerospace propulsion industry.

Nanoscale phase transition behavior of shape memory alloys — closed form solution of 1D effective modelling

NASA Astrophysics Data System (ADS)

Li, M. P.; Sun, Q. P.

2018-01-01

We investigate the roles of grain size (lg) and grain boundary thickness (lb) on the stress-induced phase transition (PT) behaviors of nanocrystalline shape memory alloys (SMAs) by using a Core-shell type "crystallite-amorphous composite" model. A non-dimensionalized length scale lbarg(=lg /lb) is identified as the governing parameter which is indicative of the energy competition between the crystallite and the grain boundary. Closed form analytical solutions of a reduced effective 1D model with embedded microstructure length scales of lg and lb are presented in this paper. It is shown that, with lbarg reduction, the energy of the elastic non-transformable grain boundary will gradually become dominant in the phase transition process, and eventually bring fundamental changes of the deformation behaviors: breakdown of two-phase coexistence and vanishing of superelastic hysteresis. The predictions are supported by experimental data of nanocrystalline NiTi SMAs.

SALT-RESPONSIVE ERF1 is a negative regulator of grain filling and gibberellin-mediated seedling establishment in rice.

PubMed

Schmidt, Romy; Schippers, Jos H M; Mieulet, Delphine; Watanabe, Mutsumi; Hoefgen, Rainer; Guiderdoni, Emmanuel; Mueller-Roeber, Bernd

2014-02-01

Grain quality is an important agricultural trait that is mainly determined by grain size and composition. Here, we characterize the role of the rice transcription factor (TF) SALT-RESPONSIVE ERF1 (SERF1) during grain development. Through genome-wide expression profiling and chromatin immunoprecipitation, we found that SERF1 directly regulates RICE PROLAMIN-BOX BINDING FACTOR (RPBF), a TF that functions as a positive regulator of grain filling. Loss of SERF1 enhances RPBF expression resulting in larger grains with increased starch content, while SERF1 overexpression represses RPBF resulting in smaller grains. Consistently, during grain filling, starch biosynthesis genes such as GRANULE-BOUND STARCH SYNTHASEI (GBSSI), STARCH SYNTHASEI (SSI), SSIIIa, and ADP-GLUCOSE PYROPHOSPHORYLASE LARGE SUBUNIT2 (AGPL2) are up-regulated in SERF1 knockout grains. Moreover, SERF1 is a direct upstream regulator of GBSSI. In addition, SERF1 negatively regulates germination by controlling RPBF expression, which mediates the gibberellic acid (GA)-induced expression of RICE AMYLASE1A (RAmy1A). Loss of SERF1 results in more rapid seedling establishment, while SERF1 overexpression has the opposite effect. Our study reveals that SERF1 represents a negative regulator of grain filling and seedling establishment by timing the expression of RPBF.

The theory of granular packings for coarse soils

NASA Astrophysics Data System (ADS)

Yanqui, Calixtro

2013-06-01

Coarse soils are substances made of grains of different shape, size and orientation. In this paper, new massive-measurable grain indexes are defined to develop a simple and systematic theory for the ideal packing of grains. First, a linear relationship between an assemblage of monodisperse spheres and an assemblage of polydisperse grains is deduced. Then, a general formula for the porosity of linearly ordered packings of spheres in contact is settled down by the appropriated choosing of eight neighboring spheres located at the vertices of the unit parallelepiped. The porosity of axisymmetric packings of grains, related to sand piles and axisymmetric compression tests, is proposed to be determined averaging the respective linear parameters. Since they can be tested experimentally, porosities of the densest state and the loosest state of a granular soil can be used to verify the accuracy of the present theory. Diagrams for these extreme quantities show a good agreement between the theoretical lines and the experimental data, no matter the dependency on the protocols and mineral composition.

Experimental Observations on Dynamic Response of Selected Transparent Armor Materials

DTIC Science & Technology

2014-07-01

that is transmitted through the specimen. A cu- boidal calibration specimen made from Ti – 6Al – 4V alloy was used for this purpose. References 9 and...average (Fig. 9). The density is typically 3.67 g/ cm3, but will vary slightly depending on the composition and porosity . The range of grain sizes for

Creation of a Data Base on Energetic Materials

DTIC Science & Technology

1987-08-10

Examples of booster explosives are Tetryl, RDX , and HMX . Examples of bursting explosives are Amatols, TNT, Compositions A, B, & C, and Picatrol. Within...Test Thermal Shock Resistance Glass Transition Temperature Toxicity Grain Size Viscosity Hardness Volatility Heat Capacity Water Resistance Heat of...Tensile Strength Flammability Thermal Conductivity Flexural Strength Thermal Expansion Coefficient Gap Test Thermal Shock Resistance Glass Transition

Impact of petroleum products on soil composition and physical-chemical properties

NASA Astrophysics Data System (ADS)

Brakorenko, N. N.; Korotchenko, T. V.

2016-03-01

The article describes the grain-size distribution, physical and mechanical properties, swelling and specific electrical resistivity of soils before and after the contact with petroleum products. The changes in mechanical properties of soils contaminated with petroleum products have been stated. It leads to the increase in compressibility values, decline in internal friction angle and cohesion.

Magnetic properties and microstructure of gas atomized MRE2(Fe, Co)14B powder with ZrC addition (MRE=Nd + Y + Dy)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tang, W.; Wu, Y. Q.; Dennis, K.

2009-05-12

Gas atomization powder with Zr substitutions for the MRE and ZrC additions were systematically studied. The results show that the partial substitutions of Zr and the ZrC additions effectively improved glass formability in the alloys. Scanning electron microscopy (SEM) revealed that the as-atomized powder with a particle size of less than 32 {micro}m is predominately uniform equiaxed grains with an average grain size of 1.5 {micro}m. X-ray diffraction and differential thermal analysis measurements detected very tiny amounts of amorphous phase. After annealing at 700 C for 15 min, the SEM grain microstructure exhibits a minor change, but magnetic properties aremore » substantially improved. M versus T measurements reveal that the phase composition evolved from 2:14:1 plus a small amount of 2:17 phases to a single 2:14:1 phase during the annealing process. The sieve analysis of the powders showed a particle size distribution with 90 wt % of the powder less than 45 {micro}m. The magnetic properties of the annealed powder varied with particle size. (BH){sub max} first increases with increasing particle size from 5 {micro}m, reaches the peak value in the size range of 20-25 {micro}m, and then decreases with increasing particle size. For the 20-25 {micro}m powder sample annealed at 700 C for 15 min, the (BH){sub max} of 9.6 MG Oe at room temperature and 5.6 MG Oe at 200 C were obtained, respectively.« less

Densification behavior and mechanical properties of nanocrystalline TiC reinforced 316L stainless steel composite parts fabricated by selective laser melting

NASA Astrophysics Data System (ADS)

Zhao, Shuming; Shen, Xianfeng; Yang, Jialin; Teng, Wenhua; Wang, Yingying

2018-07-01

Metal matrix composite parts produced using selective laser melting have superior mechanical properties to those produced using traditional powder metallurgy. In this study, nanocrystalline TiC reinforced 316L stainless steel composite parts were fabricated using selective laser melting, and the effects of the TiC mass fraction, particle size, and processing parameters on the relative density, microhardness, and mechanical properties of the TiC/316L composites were investigated. The results show that the relative density of the fabricated parts is related to the laser power and exposure time, and increases when these parameters are increased. The greater the mass fraction of nano-TiC added, the more severe the degree of spheroidization and the lower the density of the resulting material. The microhardness of the 316L stainless steel parts is enhanced by the nano-TiC particles, and increases with increasing nano-TiC mass fraction. The tensile strength is improved with longer exposure time and with the addition of 2 wt% nano-TiC particles. Compared with pure 316L, the microhardness of the TiC/316L composite parts fabricated with 2 wt% 40 nm TiC enhanced from HV0.3 = 219.1 to 277.6, and the ultimate tensile strength significantly increased from 627.5 to 748.6 MPa. The strengthening mechanism of TiC particles is the refinement of the grain size of the 316L matrix, and the greater amount of TiC particles added, the better the grain refinement of 316L.

Morphology and microstructure evolution of Ti-50 at.% Al cathodes during cathodic arc deposition of Ti-Al-N coatings

NASA Astrophysics Data System (ADS)

Syed, Bilal; Zhu, Jianqiang; Polcik, Peter; Kolozsvari, Szilard; Hâkansson, Greger; Johnson, Lars; Ahlgren, Mats; Jöesaar, Mats; Odén, Magnus

2017-06-01

Today's research on the cathodic arc deposition technique and coatings therefrom primarily focuses on the effects of, e.g., nitrogen partial pressure, growth temperature, and substrate bias. Detailed studies on the morphology and structure of the starting material—the cathode—during film growth and its influence on coating properties at different process conditions are rare. This work aims to study the evolution of the converted layer, its morphology, and microstructure, as a function of the cathode material grain size during deposition of Ti-Al-N coatings. The coatings were reactively grown in pure N2 discharges from powder metallurgically manufactured Ti-50 at.% Al cathodes with grain size distribution averages close to 1800, 100, 50, and 10 μm, respectively, and characterized with respect to microstructure, composition, and mechanical properties. The results indicate that for the cathode of 1800 μm grain size the disparity in the work function among parent phases plays a dominant role in the pronounced erosion of Al, which yields the coatings rich in macro-particles and of high Al content. We further observed that a reduction in the grain size of Ti-50 at.% Al cathodes to 10 μm provides favorable conditions for self-sustaining reactions between Ti and Al phases upon arcing to form γ phase. The combination of self-sustaining reaction and the arc process not only result in the formation of hole-like and sub-hole features on the converted layer but also generate coatings of high Al content and laden with macro-particles.

Tungsten Carbide Grain Size Computation for WC-Co Dissimilar Welds

NASA Astrophysics Data System (ADS)

Zhou, Dongran; Cui, Haichao; Xu, Peiquan; Lu, Fenggui

2016-06-01

A "two-step" image processing method based on electron backscatter diffraction in scanning electron microscopy was used to compute the tungsten carbide (WC) grain size distribution for tungsten inert gas (TIG) welds and laser welds. Twenty-four images were collected on randomly set fields per sample located at the top, middle, and bottom of a cross-sectional micrograph. Each field contained 500 to 1500 WC grains. The images were recognized through clustering-based image segmentation and WC grain growth recognition. According to the WC grain size computation and experiments, a simple WC-WC interaction model was developed to explain the WC dissolution, grain growth, and aggregation in welded joints. The WC-WC interaction and blunt corners were characterized using scanning and transmission electron microscopy. The WC grain size distribution and the effects of heat input E on grain size distribution for the laser samples were discussed. The results indicate that (1) the grain size distribution follows a Gaussian distribution. Grain sizes at the top of the weld were larger than those near the middle and weld root because of power attenuation. (2) Significant WC grain growth occurred during welding as observed in the as-welded micrographs. The average grain size was 11.47 μm in the TIG samples, which was much larger than that in base metal 1 (BM1 2.13 μm). The grain size distribution curves for the TIG samples revealed a broad particle size distribution without fine grains. The average grain size (1.59 μm) in laser samples was larger than that in base metal 2 (BM2 1.01 μm). (3) WC-WC interaction exhibited complex plane, edge, and blunt corner characteristics during grain growth. A WC ( { 1 {bar{{1}}}00} ) to WC ( {0 1 1 {bar{{0}}}} ) edge disappeared and became a blunt plane WC ( { 10 1 {bar{{0}}}} ) , several grains with two- or three-sided planes and edges disappeared into a multi-edge, and a WC-WC merged.

The grain-size lineup: A test of a novel eyewitness identification procedure.

PubMed

Horry, Ruth; Brewer, Neil; Weber, Nathan

2016-04-01

When making a memorial judgment, respondents can regulate their accuracy by adjusting the precision, or grain size, of their responses. In many circumstances, coarse-grained responses are less informative, but more likely to be accurate, than fine-grained responses. This study describes a novel eyewitness identification procedure, the grain-size lineup, in which participants eliminated any number of individuals from the lineup, creating a choice set of variable size. A decision was considered to be fine-grained if no more than 1 individual was left in the choice set or coarse-grained if more than 1 individual was left in the choice set. Participants (N = 384) watched 2 high-quality or low-quality videotaped mock crimes and then completed 4 standard simultaneous lineups or 4 grain-size lineups (2 target-present and 2 target-absent). There was some evidence of strategic regulation of grain size, as the most difficult lineup was associated with a greater proportion of coarse-grained responses than the other lineups. However, the grain-size lineup did not outperform the standard simultaneous lineup. Fine-grained suspect identifications were no more diagnostic than suspect identifications from standard lineups, whereas coarse-grained suspect identifications carried little probative value. Participants were generally reluctant to provide coarse-grained responses, which may have hampered the utility of the procedure. For a grain-size approach to be useful, participants may need to be trained or instructed to use the coarse-grained option effectively. (c) 2016 APA, all rights reserved).

Origins of GEMS Grains

NASA Technical Reports Server (NTRS)

Messenger, S.; Walker, R. M.

2012-01-01

Interplanetary dust particles (IDPs) collected in the Earth s stratosphere contain high abundances of submicrometer amorphous silicates known as GEMS grains. From their birth as condensates in the outflows of oxygen-rich evolved stars, processing in interstellar space, and incorporation into disks around new stars, amorphous silicates predominate in most astrophysical environments. Amorphous silicates were a major building block of our Solar System and are prominent in infrared spectra of comets. Anhydrous interplanetary dust particles (IDPs) thought to derive from comets contain abundant amorphous silicates known as GEMS (glass with embedded metal and sulfides) grains. GEMS grains have been proposed to be isotopically and chemically homogenized interstellar amorphous silicate dust. We evaluated this hypothesis through coordinated chemical and isotopic analyses of GEMS grains in a suite of IDPs to constrain their origins. GEMS grains show order of magnitude variations in Mg, Fe, Ca, and S abundances. GEMS grains do not match the average element abundances inferred for ISM dust containing on average, too little Mg, Fe, and Ca, and too much S. GEMS grains have complementary compositions to the crystalline components in IDPs suggesting that they formed from the same reservoir. We did not observe any unequivocal microstructural or chemical evidence that GEMS grains experienced prolonged exposure to radiation. We identified four GEMS grains having O isotopic compositions that point to origins in red giant branch or asymptotic giant branch stars and supernovae. Based on their O isotopic compositions, we estimate that 1-6% of GEMS grains are surviving circumstellar grains. The remaining 94-99% of GEMS grains have O isotopic compositions that are indistinguishable from terrestrial materials and carbonaceous chondrites. These isotopically solar GEMS grains either formed in the Solar System or were completely homogenized in the interstellar medium (ISM). However, the chemical compositions of GEMS grains are extremely heterogeneous and seem to rule out this possibility. Based on their solar isotopic compositions and their non-solar elemental compositions we propose that most GEMS grains formed in the nebula as late-stage non-equilibrium condensates.

Phase transformations in 40-60-GPa shocked gneisses from the Haughton Crater (Canada): An Analytical Transmission Electron Microscopy (ATEM) study

NASA Technical Reports Server (NTRS)

Martinez, I.; Guyot, F.; Schaerer, U.

1992-01-01

In order to better understand phase transformations, chemical migration, and isotopic disequilibrium in highly shocked rocks, we have performed a microprobe and an ATEM study on gneisses shocked up to 60 GPa from the Haughton Crater. This study reveals the following chemical and structural characteristics: (1) SiO2 dominant areas are formed by a mixture of pure SiO2 polycrystalline quartz identified by electron diffraction pattern and chemical analysis and a silica-rich amorphous phase containing minor amounts of aluminium, potassium, and iron; (2) Areas with biotitelike composition are formed by less than 200-nm grains of iron-rich spinels embedded in a silica-rich amorphous phase that is very similar to the one described above; (3) Layers with feldsparlike composition are constituted by 100-200-nm-sized alumina-rich grains (the indexation of the crystalline structure is under progress) and the silica-rich amorphous phase; (4) Zones characterized by the unusual Al/Si ratio close to 1 are formed by spinel grains (200-nm-sized) embedded in the same silica-rich amorphous phase; and (5) The fracturated sillimanites contain domains with a lamellar structure, defined by the intercalation of 100-nm-wide lamellae of mullite crystals and of a silica-rich amorphous phase. These mullite crystals preserved the crystallographical orientation of the preshock sillimanite. All compositional domains, identified at the microprobe scale, can thus be explained by a mixture in different proportion between the following phases: (1) a silica-rich amorphous phase, with minor Al and K; (2) quartz crystals; (3) spinel crystals and alumina-rich crystals; (4) sillimanite; and (5) mullite. Such mixtures of amorphous phases and crystals in different proportions explain disturbed isotope systems in these rocks and chemical heterogeneities observed on the microprobe.

Current and sea-level signals in periplatform ooze (Neogene, Maldives, Indian Ocean)

NASA Astrophysics Data System (ADS)

Betzler, Christian; Lüdmann, Thomas; Hübscher, Christian; Fürstenau, Jörn

2013-05-01

Periplatform ooze is an admixture of pelagic carbonate and sediment derived from neritic carbonate platforms. Compositional variations of periplatform ooze allow the reconstruction of past sea-level changes. Periplatform ooze formed during sea-level highstands is finer grained and richer in aragonite through the elevated input of material from the flooded platform compared to periplatform ooze formed during the episodes of lowered sea level. In many cases, however, the sea floor around carbonate platforms is subjected to bottom currents which are expected to affect sediment composition, i.e. through winnowing of the fine fraction. The interaction of sea-level driven highstand shedding and current impact on the formation of periplatform ooze has hitherto not been analyzed. To test if a sea-level driven input signal in periplatform ooze is influenced or even distorted by changing current activity, an integrated study using seismic, hydroacoustic and sedimentological data has been performed on periplatform ooze deposited in the Inner Sea of the Maldives. The Miocene to Pleistocene succession of drift deposits is subdivided into nine units; limits of seismostratigraphic units correspond to changes or turnarounds in grain size trends in cores recovered at ODP Site 716 and NEOMA Site 1143. For the Pleistocene it can be shown how changes in grain size occur in concert with sea-level changes and changes of the monsoonal system, which is thought to be a major driver of bottom currents in the Maldives. A clear highstand shedding pattern only appears in the data at a time of relaxation of monsoonal strength during the last 315 ky. Results imply (1) that drift sediments provide a potential target for analyzing past changes in oceanic currents and (2) that the ooze composition bears a mixed signal of input and physical winnowing at the sea floor.

A Critical Examination of Relative Concentrations of Volume-correlated and Surface-correlated Submicron Globules of Pure Fe-0 in Lunar Soils

NASA Technical Reports Server (NTRS)

Basu, A.; McKay, D. S.; Wentworth, S. J.

2003-01-01

Impacts on lunar soils produce melt and vapor in an approximate proportion of 7:1. The melt scavenges soil grains of diverse size, quenches and forms agglutinates, thereby converting surface correlated components of soil grains as volume correlated components; simultaneously, parts of the vapor may condense or escape. Cumulative small impacts increase the maturity of the soils, increase the abundance of agglutinates, and increase the concentration of vapor condensated material. Since the discovery of vapor deposited crystalline Fe-0 in vugs of regolith breccias and the theoretical anticipation of amorphous vapor deposits of diverse composition coating lunar soils grains, empirical evidence is gathering in support of such deposits, now commonly called vapor deposited patina (VDP). In addition, submicron globules of Fe-0 are seen to be ubiquitous in VDP. The amorphous VDP lowers the albedo of lunar soils, affects magnetic properties of soils, changes the slopes of uv-vis-ir reflectance spectra, and potentially also alters the gamma and x-ray spectra of lunar soils, compromising compositional inferences from remote sensing.

[Characterization of puroindolines in the control of endosperm texture in common wheat lines with substitutions of homeologous group-5 chromosomes].

PubMed

Obukhova, L V; Efremova, T T; Shumnyĭ, V K

2013-03-01

The genetic control of grain hardness and its association with the specific friabilin content on starch granules of common wheat cultivars and lines with intervarietal substitutions of homeologous group-5 chromosomes were studied. A significant correlation was revealed between the technological parameters of grain hardness (mean size of flour particles) and the specific content of puroindolines on the starch surface estimated in terms of starch doses. The results obtained allowed the method of starch doses to be used to identify soft and hard wheat cultivars and lines based on an analysis of a single grain. The biochemical analysis confirmed the previously obtained estimates of flour-grinding properties of wheat cultivars and substitution lines, which allowed specific genotypes to be characterized according to the composition of puroindolines. The influence of chromosomes 5D and 5A of donor wheat cultivars on the activity of the Ha loci of recipient cultivars was revealed and found to be associated with the composition of PIN products and with the expression of the Pina-D1 and Pinb-D1 genes.

Cool Bottom Processing on the AGB and Presolar Grain Compositions

NASA Technical Reports Server (NTRS)

Nollett, Kenneth M.; Busso, M.; Wasserburg, G. J.

2002-01-01

We describe results from a model of cool bottom processing (CBP) in AGB (asymptotic giant branch) stars. We predict O, Al, C and N isotopic compositions of circumstellar grains. Measured compositions of mainstream SiC grains and many oxide grains are consistent with CBP. Additional information is contained in the original extended abstract.

Constructing nanoporous carbon nanotubes/Bi2Te3 composite for synchronous regulation of the electrical and thermal performances

NASA Astrophysics Data System (ADS)

Zhang, Qihao; Xu, Leilei; Zhou, Zhenxing; Wang, Lianjun; Jiang, Wan; Chen, Lidong

2017-02-01

Porous nanograined thermoelectric materials exhibit low thermal conductivity due to scattering of phonons by pores, which are favorable for thermoelectric applications. However, the benefit is not large enough to overcome the deficiency in the electrical performance. Herein, an approach is presented to reduce the thermal conductivity and synchronously enhance the electrical conductivity through constructing a nanoporous thermoelectric composite. Carbon nanotubes (CNTs) are truncated and homogeneously dispersed within the Bi2Te3 matrix by a cryogenic grinding (CG) technique for the first time, which efficiently suppress the Bi2Te3 grain growth and create nanopores with the size ranging from dozens to hundreds of nanometers. The lattice thermal conductivity is substantially decreased by broad wavelength phonon scattering resulting from nanopores, increased grain boundaries, and newly formed interfaces. Meanwhile, the electrical conductivity is improved due to the enhanced carrier mobility, which may originate from the bridging effect between the Bi2Te3 grains and CNTs. The maximum ZT is improved by almost a factor of 2 due to the simultaneous optimization of electrical and thermal performances. Our study demonstrates the superiority of constructing a bulk thermoelectric composite with nanopores by the uniform dispersion of CNTs through a CG technique for enhanced thermoelectric properties, which provides a wider approach to thermoelectric nanostructure engineering.

Effects of grain size on the properties of bulk nanocrystalline Co-Ni alloys

NASA Astrophysics Data System (ADS)

Qiao, Gui-Ying; Xiao, Fu-Ren

2017-08-01

Bulk nanocrystalline Co78Ni22 alloys with grain size ranging from 5 nm to 35 nm were prepared by high-speed jet electrodeposition (HSJED) and annealing. Microhardness and magnetic properties of these alloys were investigated by microhardness tester and vibrating sample magnetometer. Effects of grain size on these characteristics were also discussed. Results show that the microhardness of nanocrystalline Co78Ni22 alloys increases following a d -1/2-power law with decreasing grain size d. This phenomenon fits the Hall-Petch law when the grain size ranges from 5 nm to 35 nm. However, coercivity H c increases following a 1/d-power law with increasing grain size when the grain size ranges from 5 nm to 15.9 nm. Coercivity H c decreases again for grain sizes above 16.6 nm according to the d 6-power law.

Simple approach to sediment provenance tracing using element analysis and fundamental principles

NASA Astrophysics Data System (ADS)

Matys Grygar, Tomas; Elznicova, Jitka; Popelka, Jan

2016-04-01

Common sediment fingerprinting techniques use either (1) extensive analytical datasets, sometimes nearly complete with respect to accessible characterization techniques; they are processed by multidimensional statistics based on certain statistical assumptions on distribution functions of analytical results and conservativeness/additivity of some components, or (2) analytically demanding characteristics such as isotope ratios assumed to be unequivocal "labels" on the parent material unaltered by any catchment process. The inherent problem of the approach ad (1) is that interpretation of statistical components ("sources") is done ex post and remains purely formal. The problem of the approach ad (2) is that catchment processes (weathering, transport, deposition) can modify most geochemical parameters of soils and sediments, in other words, that the idea that some geochemistry parameters are "conservative" may be idealistic. Grain-size effects and sediment provenance have a joint influence on chemical composition of fluvial sediments that is indeed not easy to distinguish. Attempts to separate those two main components using only statistics seem risky and equivocal, because grain-size dependence of element composition is nearly individual for each element and reflects sediment maturity and catchment-specific formation transport processes. We suppose that the use of less extensive datasets of analytical results and their interpretation respecting fundamental principles should be more robust than only statistic tools applied to overwhelming datasets. We examined sediment composition, both published by other researchers and gathered by us, and we found some general principles, which are in our opinion relevant for fingerprinting: (1) Concentrations of all elements are grain-size sensitive, i.e. there are no "conservative" elements in conventional sense of provenance- or transport-pathways tracing, (2) fractionation by catchment processes and fluvial transport changes slightly but systematically element ratios in solids, (3) the geochemistry and fates of the finest particles, neoformed by weathering and reactive during transport and storage in fluvial system, are different than those of the parent material and its less mature coarse weathering products, and (4) most inter-element ratios and some grain-size effects are non-linear that endanger assumption on additivity of properties in components mixing. We are aware we offer only a conceptual model and not a novel algorithm for quantification of sediment sources, which could be tested in practical studies. On the other hand, we consider element fractionation by exogenic processes fascinating as they are poorly described but relevant not only for provenance tracing but also for general environmental geochemistry.

The effect of rock fabric on P-wave velocity distribution in amphibolites

NASA Astrophysics Data System (ADS)

Vajdová, V.; Přikryl, R.; Pros, Z.; Klíma, K.

1999-07-01

This study presents contribution to the laboratory investigation of elastic properties and rock fabric of amphibolites. P-wave velocity was determined on four spherical samples prepared from a shallow borehole core. The measurement was conducted in 132 directions under various conditions of hydrostatic pressure (up to 400 MPa). The rock fabric was investigated by image analysis of thin sections that enabled precise determination of grain size, modal composition and shape parameters of rock-forming minerals. Laboratory measurement of P-waves revealed pseudoorthorhombic symmetry of rock fabric in amphibolites studied. This symmetry reflects rocks' macro- and microfabric. Maximum P-wave velocity corresponds to the macroscopically visible stretching lineation. Minimum P-wave velocity is oriented perpendicular to the foliation plane. The average grain size is the main microstructural factor controlling mean P-wave velocity.

Grain-scale imaging and compositional characterization of cryo-preserved India NGHP 01 gas-hydrate-bearing cores

USGS Publications Warehouse

Stern, Laura A.; Lorenson, T.D.

2014-01-01

We report on grain-scale characteristics and gas analyses of gas-hydrate-bearing samples retrieved by NGHP Expedition 01 as part of a large-scale effort to study gas hydrate occurrences off the eastern-Indian Peninsula and along the Andaman convergent margin. Using cryogenic scanning electron microscopy, X-ray spectroscopy, and gas chromatography, we investigated gas hydrate grain morphology and distribution within sediments, gas hydrate composition, and methane isotopic composition of samples from Krishna–Godavari (KG) basin and Andaman back-arc basin borehole sites from depths ranging 26 to 525 mbsf. Gas hydrate in KG-basin samples commonly occurs as nodules or coarse veins with typical hydrate grain size of 30–80 μm, as small pods or thin veins 50 to several hundred microns in width, or disseminated in sediment. Nodules contain abundant and commonly isolated macropores, in some places suggesting the original presence of a free gas phase. Gas hydrate also occurs as faceted crystals lining the interiors of cavities. While these vug-like structures constitute a relatively minor mode of gas hydrate occurrence, they were observed in near-seafloor KG-basin samples as well as in those of deeper origin (>100 mbsf) and may be original formation features. Other samples exhibit gas hydrate grains rimmed by NaCl-bearing material, presumably produced by salt exclusion during original hydrate formation. Well-preserved microfossil and other biogenic detritus are also found within several samples, most abundantly in Andaman core material where gas hydrate fills microfossil crevices. The range of gas hydrate modes of occurrence observed in the full suite of samples suggests a range of formation processes were involved, as influenced by local in situconditions. The hydrate-forming gas is predominantly methane with trace quantities of higher molecular weight hydrocarbons of primarily microbial origin. The composition indicates the gas hydrate is Structure I.

Effect of Excess Lead and Bismuth Content on the Electrical Properties of High-Temperature Bismuth Scandium Lead Titanate Ceramics

NASA Technical Reports Server (NTRS)

Sehirlioglu, Alp; Sayir, Ali

2008-01-01

Aeronautic and aerospace applications require piezoelectric materials that can operate at high temperatures. The air-breathing aeronautic engines can use piezoelectric actuators for active combustion control for fuel modulation to mitigate thermo-acoustic instabilities and/or gas flow control to improve efficiency. The principal challenge for the insertion of piezoelectric materials is their limitation for upper use temperature and this limitation is due low Curie temperature and increasing conductivity. We investigated processing, microstructure and property relationship of (1-x)BiScO3-(x)PbTiO3 (BS-PT) composition as a promising high temperature piezoelectric. The effect of excess Pb and Bi and their partitioning in grain boundaries were studied using impedance spectroscopy, ferroelectric, and piezoelectric measurement techniques. Excess Pb addition increased the grain boundary conduction and the grain boundary area (average grain size was 24.8 m, and 1.3 m for compositions with 0at.% and 5at.% excess Pb, respectively) resulting in ceramics with higher AC conductivity (tan d= 0.9 and 1.7 for 0at.% and 5at.% excess Pb at 350 C and at 10kHz) that were not resistive enough to pole. Excess Bi addition increased the resistivity (rho= 4.1x10(exp 10) Omega cm and 19.6 x10(exp 10) Omega.cm for compositions with 0at.% and 5at.% excess Bi, respectively), improved poling, and increased the piezoelectric coefficient from 137 to 197 pC/N for 5at.% excess Bi addition. In addition, loss tangent decreased more than one order of magnitude at elevated temperatures (greater than 300 C). For all compositions the activation energy of the conducting species was similar (approximately equal to 0.35-0.40 eV) and indicated electronic conduction.

Interstellar and Cometary Dust

NASA Technical Reports Server (NTRS)

Mathis, John S.

1997-01-01

'Interstellar dust' forms a continuum of materials with differing properties which I divide into three classes on the basis of observations: (a) diffuse dust, in the low-density interstellar medium; (b) outer-cloud dust, observed in stars close enough to the outer edges of molecular clouds to be observed in the optical and ultraviolet regions of the spectrum, and (c) inner-cloud dust, deep within the cores of molecular clouds, and observed only in the infrared by means of absorption bands of C-H, C=O, 0-H, C(triple bond)N, etc. There is a surprising regularity of the extinction laws between diffuse- and outer-cloud dust. The entire mean extinction law from infrared through the observable ultraviolet spectrum can be characterized by a single parameter. There are real deviations from this mean law, larger than observational uncertainties, but they are much smaller than differences of the mean laws in diffuse- and outer-cloud dust. This fact shows that there are processes which operate over the entire distribution of grain sizes, and which change size distributions extremely efficiently. There is no evidence for mantles on grains in local diffuse and outer-cloud dust. The only published spectra of the star VI Cyg 12, the best candidate for showing mantles, does not show the 3.4 micro-m band which appreciable mantles would produce. Grains are larger in outer-cloud dust than diffuse dust because of coagulation, not accretion of extensive mantles. Core-mantle grains favored by J. M. Greenberg and collaborators, and composite grains of Mathis and Whiffen (1989), are discussed more extensively (naturally, I prefer the latter). The composite grains are fluffy and consist of silicates, amorphous carbon, and some graphite in the same grain. Grains deep within molecular clouds but before any processing within the solar system are presumably formed from the accretion of icy mantles on and within the coagulated outer-cloud grains. They should contain a mineral/carbonaceous matrix, without organic refractory mantles, in between the ices. Unfortunately, they may be significantly processed by chemical processes accompanying the warming (over the 10 K of the dark cloud cores) which occurs in the outer solar system. Evidence of this processing is the chemical anomalies present in interplanetary dust particles collected in the stratosphere, which may be the most primitive materials we have obtained to date. The comet return mission would greatly clarify the situation, and probably provide samples of genuine interstellar grains.

Magnesium-Aluminum-Zirconium Oxide Amorphous Ternary Composite: A Dense and Stable Optical Coating

NASA Technical Reports Server (NTRS)

Sahoo, N. K.; Shapiro, A. P.

1998-01-01

In the present work, the process parameter dependent optical and structural properties of MgO-Al(2)O(3)-ZrO(2) ternary mixed-composite material have been investigated. Optical properties were derived from spectrophotometric measurements. The surface morphology, grain size distributions, crystallographic phases and process dependent material composition of films have been investigated through the use of Atomic Force Microscopy (AFM), X-ray diffraction analysis and Energy Dispersive X- ray (EDX) analysis. EDX analysis made evident the correlation between the optical constants and the process dependent compositions in the films. It is possible to achieve environmentally stable amorphous films with high packing density under certain optimized process conditions.

MgO-Al2O3-ZrO2 Amorphous Ternary Composite: A Dense and Stable Optical Coating

NASA Technical Reports Server (NTRS)

Shaoo, Naba K.; Shapiro, Alan P.

1998-01-01

The process-parameter-dependent optical and structural properties of MgO-Al2O3-ZrO2 ternary mixed-composite material were investigated. Optical properties were derived from spectrophotometric measurements. The surface morphology, grain size distributions, crystallographic phases, and process- dependent material composition of films were investigated through the use of atomic force microscopy, x-ray diffraction analysis, and energy-dispersive x-ray analysis. Energy-dispersive x-ray analysis made evident the correlation between the optical constants and the process-dependent compositions in the films. It is possible to achieve environmentally stable amorphous films with high packing density under certain optimized process conditions.

Interrelationships among Grain Size, Surface Composition, Air Stability, and Interfacial Resistance of Al-Substituted Li7La3Zr2O12 Solid Electrolytes.

PubMed

Cheng, Lei; Wu, Cheng Hao; Jarry, Angelique; Chen, Wei; Ye, Yifan; Zhu, Junfa; Kostecki, Robert; Persson, Kristin; Guo, Jinghua; Salmeron, Miquel; Chen, Guoying; Doeff, Marca

2015-08-19

The interfacial resistances of symmetrical lithium cells containing Al-substituted Li7La3Zr2O12 (LLZO) solid electrolytes are sensitive to their microstructures and histories of exposure to air. Air exposure of LLZO samples with large grain sizes (∼150 μm) results in dramatically increased interfacial impedances in cells containing them, compared to those with pristine large-grained samples. In contrast, a much smaller difference is seen between cells with small-grained (∼20 μm) pristine and air-exposed LLZO samples. A combination of soft X-ray absorption (sXAS) and Raman spectroscopy, with probing depths ranging from nanometer to micrometer scales, revealed that the small-grained LLZO pellets are more air-stable than large-grained ones, forming far less surface Li2CO3 under both short- and long-term exposure conditions. Surface sensitive X-ray photoelectron spectroscopy (XPS) indicates that the better chemical stability of the small-grained LLZO is related to differences in the distribution of Al and Li at sample surfaces. Density functional theory calculations show that LLZO can react via two different pathways to form Li2CO3. The first, more rapid, pathway involves a reaction with moisture in air to form LiOH, which subsequently absorbs CO2 to form Li2CO3. The second, slower, pathway involves direct reaction with CO2 and is favored when surface lithium contents are lower, as with the small-grained samples. These observations have important implications for the operation of solid-state lithium batteries containing LLZO because the results suggest that the interfacial impedances of these devices is critically dependent upon specific characteristics of the solid electrolyte and how it is prepared.

Characterization of SiC Fiber (SCS-6) Reinforced-Reaction-Formed Silicon Carbide Matrix Composites

NASA Technical Reports Server (NTRS)

Singh, M.; Dickerson, R. M.

1996-01-01

Silicon carbide fiber (SCS-6) reinforced-reaction-formed silicon carbide matrix composites were fabricated using a reaction-forming process. Silicon-2 at.% niobium alloy was used as an infiltrant instead of pure silicon to reduce the amount of free silicon in the matrix after reaction forming. The matrix primarily consists of silicon carbide with a bimodal grain size distribution. Minority phases dispersed within the matrix are niobium disilicide (NbSi2), carbon, and silicon. Fiber pushout tests on these composites determined a debond stress of approximately 67 MPa and a frictional stress of approximately 60 MPa. A typical four-point flexural strength of the composite is 297 MPa (43.1 KSi). This composite shows tough behavior through fiber pullout.

Chemistry, Mineralogy, and Grain Properties at Namib and High Dunes, Bagnold Dune Field, Gale Crater, Mars: A Synthesis of Curiosity Rover Observations: Bagnold Dune Sands Composition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ehlmann, B. L.; Edgett, K. S.; Sutter, B.

The Mars Science Laboratory Curiosity rover performed coordinated measurements to examine the textures and compositions of aeolian sands in the active Bagnold dune field. The Bagnold sands are rounded to subrounded, very fine- to medium- sized (~45-500 µm) with ≥6 distinct grain colors. In contrast to sands examined by Curiosity in a dust-covered, inactive bedform called Rocknest and soils at other landing sites, Bagnold sands are darker, less red, better sorted, have fewer silt-sized or smaller grains, and show no evidence for cohesion. Nonetheless, Bagnold mineralogy and Rocknest mineralogy are similar with plagioclase, olivine, and pyroxenes in similar proportions comprisingmore » >90% of crystalline phases, along with a substantial amorphous component (35% ± 15%). Yet, Bagnold and Rocknest bulk chemistry differ. Bagnold sands are Si-enriched relative to other soils at Gale crater, and H 2O, S, and Cl are lower relative to all previously measured martian soils and most Gale crater rocks. Mg, Ni, Fe, and Mn are enriched in the coarse-sieved fraction of Bagnold sands, corroborated by VNIR spectra that suggest enrichment of olivine. Together, patterns in major element chemistry and volatile release data indicate two distinctive volatile reservoirs in martian soils: (1) amorphous components in the sand-sized fraction (represented by Bagnold) that are Si-enriched, hydroxylated alteration products and/or impact or volcanic glasses; and (2) amorphous components in the fine fraction (<40 µm; represented by Rocknest and other bright soils) that are Fe-, S-, and Cl-enriched with low Si and adsorbed and structural H 2O.« less

Chemistry, Mineralogy, and Grain Properties at Namib and High Dunes, Bagnold Dune Field, Gale Crater, Mars: A Synthesis of Curiosity Rover Observations: Bagnold Dune Sands Composition

DOE PAGES

Ehlmann, B. L.; Edgett, K. S.; Sutter, B.; ...

2017-06-12

The Mars Science Laboratory Curiosity rover performed coordinated measurements to examine the textures and compositions of aeolian sands in the active Bagnold dune field. The Bagnold sands are rounded to subrounded, very fine- to medium- sized (~45-500 µm) with ≥6 distinct grain colors. In contrast to sands examined by Curiosity in a dust-covered, inactive bedform called Rocknest and soils at other landing sites, Bagnold sands are darker, less red, better sorted, have fewer silt-sized or smaller grains, and show no evidence for cohesion. Nonetheless, Bagnold mineralogy and Rocknest mineralogy are similar with plagioclase, olivine, and pyroxenes in similar proportions comprisingmore » >90% of crystalline phases, along with a substantial amorphous component (35% ± 15%). Yet, Bagnold and Rocknest bulk chemistry differ. Bagnold sands are Si-enriched relative to other soils at Gale crater, and H 2O, S, and Cl are lower relative to all previously measured martian soils and most Gale crater rocks. Mg, Ni, Fe, and Mn are enriched in the coarse-sieved fraction of Bagnold sands, corroborated by VNIR spectra that suggest enrichment of olivine. Together, patterns in major element chemistry and volatile release data indicate two distinctive volatile reservoirs in martian soils: (1) amorphous components in the sand-sized fraction (represented by Bagnold) that are Si-enriched, hydroxylated alteration products and/or impact or volcanic glasses; and (2) amorphous components in the fine fraction (<40 µm; represented by Rocknest and other bright soils) that are Fe-, S-, and Cl-enriched with low Si and adsorbed and structural H 2O.« less

Grain size evolution and convection regimes of the terrestrial planets

NASA Astrophysics Data System (ADS)

Rozel, A.; Golabek, G. J.; Boutonnet, E.

2011-12-01

A new model of grain size evolution has recently been proposed in Rozel et al. 2010. This new approach stipulates that the grain size dynamics is governed by two additive and simultaneous processes: grain growth and dynamic recrystallization. We use the usual normal grain growth laws for the growth part. For dynamic recrystallization, reducing the mean grain size increases the total area of grain boundaries. Grain boundaries carry some surface tension, so some energy is required to decrease the mean grain size. We consider that this energy is available during mechanical work. It is usually considered to produce some heat via viscous dissipation. A partitioning parameter f is then required to know what amount of energy is dissipated and what part is converted in surface tension. This study gives a new calibration of the partitioning parameter on major Earth materials involved in the dynamic of the terrestrial planets. Our calibration is in adequation with the published piezometric relations available in the literature (equilibrium grain size versus shear stress). We test this new model of grain size evolution in a set of numerical computations of the dynamics of the Earth using stagYY. We show that the grain size evolution has a major effect on the convection regimes of terrestrial planets.

Micro- and nano-hydroxyapatite as active reinforcement for soft biocomposites.

PubMed

Munarin, F; Petrini, P; Gentilini, R; Pillai, R S; Dirè, S; Tanzi, M C; Sglavo, V M

2015-01-01

Pectin-based biocomposite hydrogels were produced by internal gelation, using different hydroxyapatite (HA) powders from commercial source or synthesized by the wet chemical method. HA possesses the double functionality of cross-linking agent and inorganic reinforcement. The mineralogical composition, grain size, specific surface area and microstructure of the hydroxyapatite powders are shown to strongly influence the properties of the biocomposites. Specifically, the grain size and specific surface area of the HA powders are strictly correlated to the gelling time and rheological properties of the hydrogels at room temperature. Pectin pH is also significant for the formation of ionic cross-links and therefore for the hydrogels stability at higher temperatures. The obtained results point out that micrometric-size hydroxyapatite can be proposed for applications which require rapid gelling kinetics and improved mechanical properties; conversely the nanometric hydroxyapatite synthesized in the present work seems the best choice to obtain homogeneous hydrogels with more easily controlled gelling kinetics. Copyright © 2014 Elsevier B.V. All rights reserved.

Determination of sendust intrinsic permeability from microwave constitutive parameters of composites with sendust spheres and flakes

NASA Astrophysics Data System (ADS)

Starostenko, Sergey N.; Rozanov, Konstantin N.; Shiryaev, Artem O.; Shalygin, Alexander N.; Lagarkov, Andrey N.

2017-06-01

Intrinsic permeability of sendust alloys is determined from the measured microwave permittivity and permeability of composites filled with either spherical or flaky sendust powders. The permittivity and permeability measurements are performed applying the coaxial reflection-transmission technique in the 0.05 to 18 GHz frequency range. The effects of the filling factor, inclusion shape, and size on composite constitutive parameters are discussed. The permeability of metal inclusion is retrieved from the measured permeability of composites using a generalized Maxwell Garnett equation that accounts for the percolation threshold. The equation parameters are found by fitting the measured dependence of composite permittivity and permeability on frequency and filling. The inclusion dimensions calculated from the found parameters agree with the results of grain-size analyses. The alloy intrinsic permeability is retrieved from inclusion permeability with the account for skinning. The fitted frequency and damping factor of ferromagnetic resonance depend on the inclusion shape. The calculated reflectivity map of the flake-filled composite shows that sendust powders are promising fillers for interference suppressors and microwave absorbers at frequencies close to 1 GHz.

Gabbroic and Peridotitic Enclaves from the 2008 Kasatochi Eruption, Aleutian Islands, Alaska

NASA Astrophysics Data System (ADS)

Kentner, A.; Nadin, E. S.; Izbekov, P. E.; Nye, C. J.; Neill, O. K.

2012-12-01

Kasatochi volcano of the Andreanof Islands in the western Aleutian Arc violently erupted over a two day period from August 7-8, 2008. The eruption involved multiple explosive events generating pyroclastic flows, which included abundant mafic and ultramafic enclaves that have since weathered out and accumulated in talus along the coast. These and other mafic enclaves sampled by modern island arc lavas provide insight into subduction magmatism because they emerge from a section of the subduction system that is less likely than shallower zones to be modified by magmatic processes such as mixing, assimilation, or fractionation. We present new whole rock, clinopyroxene, amphibole, plagioclase, and melt compositions from Kasatochi enclaves of the 2008 eruption. The highly crystalline (~40 vol. % phenocryst content), medium-K basaltic andesite host rock contains ~52-55 wt. % SiO2 and 0.6-0.9 wt. % K2O, and is composed of plagioclase, ortho- and clinopyroxene, amphibole, and Ti-magnetite in a microlite-rich groundmass. Upon eruption, this magma sampled two distinct enclave populations: gabbro and peridotite. The gabbro has abundant amphibole (mostly magnesio-hastingsite) and plagioclase with minor clinopyroxene, olivine, and magnetite, while the peridotite is composed of olivine with minor amounts of clinopyroxene and orthopyroxene. There is little textural variation amongst the peridotitic samples collected, but the gabbroic samples vary from layered to massive and cover a range in grain size from fine-grained to pegmatitic. The layered gabbros display centimeter-scale bands of alternating plagioclase- and amphibole-rich layers, with a strong preferential alignment of the amphibole grains. The coarser-grained samples are very friable, with ~10% pore space; disaggregation of these upon host-magma ascent likely formed the amphibole and plagioclase xenocrysts in the andesitic host. Based on the textural and compositional differences, we divide the enclaves into four groups, (1) fine-grained gabbro, (2) medium- to coarse-grained gabbro, (3) pegmatitic gabbro with crystals up to 11 cm long, and (4) medium-grained peridotite. Bulk analyses of the gabbros using LA-ICP-MS show strong light rare-earth element depletion typical of primitive melts and arc volcanics such as the South Sandwich Arc. Our data suggest that the enclaves are primitive, with plagioclase compositions of An92-96 and crystallization temperatures of 900-1100 deg. C. Initial thermobarometric analyses from compositions of amphibole in the gabbroic samples suggest different temperature-pressure conditions for crystallization of fine-grained and very coarse-grained gabbros. We interpret these rocks as hydrous cumulate-melt mixtures with primitive geochemistry that is similar to Aleutian xenoliths of Kanaga Island.

Macroscopic character of composite high-temperature superconducting wires

NASA Astrophysics Data System (ADS)

Kivelson, S. A.; Spivak, B.

2015-11-01

The "d -wave" symmetry of the superconducting order in the cuprate high temperature superconductors is a well established fact [J. Tsuei and J. R. Kirtley, Rev. Mod. Phys. 72, 969 (2000), 10.1103/RevModPhys.72.969 and D. J. Vanharlingen, Rev. Mod. Phys. 67, 515 (1995), 10.1103/RevModPhys.67.515], and one which identifies them as "unconventional." However, in macroscopic contexts—including many potential applications (i.e., superconducting "wires")—the material is a composite of randomly oriented superconducting grains in a metallic matrix, in which Josephson coupling between grains mediates the onset of long-range phase coherence. [See, e.g., D. C. Larbalestier et al., Nat. Mater. 13, 375 (2014), 10.1038/nmat3887, A. P. Malozemoff, MRS Bull. 36, 601 (2011), 10.1557/mrs.2011.160, and K. Heine et al., Appl. Phys. Lett. 55, 2441 (1989), 10.1063/1.102295] Here we analyze the physics at length scales that are large compared to the size of such grains, and in particular the macroscopic character of the long-range order that emerges. While X Y -superconducting glass order and macroscopic d -wave superconductivity may be possible, we show that under many circumstances—especially when the d -wave superconducting grains are embedded in a metallic matrix—the most likely order has global s -wave symmetry.

Combining Hard with Soft Materials in Nanoscale Under High-Pressure High-Temperature Conditions

NASA Technical Reports Server (NTRS)

Palosz, B.; Gierlotka, S.; Swiderska-Sroda, A.; Fietkiewicz, K.; Kalisz, G.; Grzanka, E.; Stel'makh, S.; Palosz, W.

2004-01-01

Nano-composites with a primary nanocrystalline ceramic matrix and a secondary nanocrystalline material (metal or semiconductor) were synthesized by infiltration of an appropriate liquid into ceramic compacts under pressures of up to 8 GPa and temperatures of up to 2000 K. The purpose of our work is to obtain nanocomposites which constitute homoger?ous mixtures of two phases, both forming nano- grains of about 10 nm in size. The high pressure is used to bring the porosity of the compacted powders down to the nano-scale and force a given liquid into the nano-sized pores. The advantage of the infiltration technique is that, in a single, continuous process, we start with a nanocrystalline powder, compress it to form the matrix of the composite, and crystallize and/or synthesize a second nanomaterial in the matrix pores. The key limitation of this technology is, that the pores in the matrix need to stay open during the entire process of infiltration. Thus the initial powder should form a rigid skeleton, otherwise the so-called self-stop process can limit cr block a further flow of the liquid phase and hinder the process of the composite formation. Therefore powders of only very hard ceramic materials like diamond, Sic, or Alz03, which can withstand a substantial external load without undesired deformation, can be used as the primary phase. With this technique, using diamond and S i c ceramic powders infiltrated by liquid metals (AI, Zn, Sn, Ag, Au) and semiconductors (Si, Ge, GaAs, CdTe), we obtained nano-composites with the grain size in the range of 10 - 30 nm. Our work addresses the key problem in manufacturing bulk nanocrystalline materials, i.e. preservation of nano-scale during the fabrication process. In this paper we discuss basic technical and methodological problems associated with nano-infiltration based on the results obtained for Zn-Sic composites.

The silicon isotopic composition of fine-grained river sediments and its relation to climate and lithology

NASA Astrophysics Data System (ADS)

Bayon, G.; Delvigne, C.; Ponzevera, E.; Borges, A. V.; Darchambeau, F.; De Deckker, P.; Lambert, T.; Monin, L.; Toucanne, S.; André, L.

2018-05-01

The δ30Si stable isotopic composition of silicon in soils and fine-grained sediments can provide insights into weathering processes on continents, with important implications on the Si budget of modern and past oceans. To further constrain the factors controlling the distribution of Si isotopes in sediments, we have analysed a large number (n = 50) of separate size-fractions of sediments and suspended particulate materials collected near the mouth of rivers worldwide. This includes some of the world's largest rivers (e.g. Amazon, Congo, Mackenzie, Mississippi, Murray-Darling, Nile, Yangtze) and rivers from the case study areas of the Congo River Basin and Northern Ireland. Silt-size fractions exhibit a mean Si isotopic composition (δ30Si = -0.21 ± 0.19‰; 2 s.d.) similar to that previously inferred for the upper continental crust. In contrast, clay-size fractions display a much larger range of δ30Si values from -0.11‰ to -2.16‰, which yield a global δ30Siclay of -0.57 ± 0.60‰ (2 s.d.) representative of the mean composition of the average weathered continental crust. Overall, these new data show that the Si isotopic signature transported by river clays is controlled by the degree of chemical weathering, as inferred from strong relationships with Al/Si ratios. At a global scale, the clay-bound Si isotopic composition of the world's largest river systems demonstrates a link with climate, defining a general correlation with mean annual temperature (MAT) in corresponding drainage basins. While the distribution of Si isotopes in river sediments also appears to be influenced by the tectonic setting, lithological effects and sediment recycling from former sedimentary cycles, our results pave the way for their use as paleo-weathering and paleo-climate proxies in the sedimentary record.

Relict chondrules in primitive achondrites: Remnants from their precursor parent bodies

NASA Astrophysics Data System (ADS)

Schrader, Devin L.; McCoy, Timothy J.; Gardner-Vandy, Kathryn

2017-05-01

We studied the petrography, analyzed the chemical compositions, constrained the closure temperatures (via geothermometry), and determined the oxidation states of relict chondrules in Campo del Cielo (IAB iron meteorite), Graves Nunataks (GRA) 98028 (acapulcoite), and Netschaëvo (IIE iron meteorite) to constrain their formation conditions and investigate links to known meteorite groups. Despite having been thermally metamorphosed, mineral phases within relict chondrules retain information about their precursor compositions. The sizes and textures of relict chondrules, and silicate and chromite compositions indicate that Campo del Cielo, GRA 98028, and Netschaëvo had distinct parent bodies that were similar to, but different from, known chondrite groups. To determine the utility of relict chondrule sizes in thermally metamorphosed meteorites, we determined the chondrule size distributions in the LL chondrites Semarkona (LL3.00), Soko-Banja (LL4), Siena (LL5), and Saint-Séverin (LL6), and the H chondrites Clovis (No. 1) (H3.6), Kesen (H4), Arbol Solo (H5), and Estacado (H6). As expected, mean chondrule diameters increase with degree of thermal metamorphism. We find that Campo del Cielo and GRA 98028 were reduced during thermal metamorphism, consistent with previous studies, indicating that their precursors were initially more FeO-rich than their current compositions. In contrast to previous studies, we find no evidence for reduction of silicates in Netschaëvo. Normal zoning of olivine in Netschaëvo is consistent with crystallization and suggests its silicates are near their primary FeO-contents. The presence of elongated chromite grains along olivine grain boundaries in Netschaëvo indicates formation during thermal metamorphism under oxidizing conditions. Due to the absence of reduction and the composition of chromite being distinct from that of metamorphosed H chondrites, we conclude that Netschaëvo, and by extension the IIE iron meteorites, are not from the H chondrite parent body.

Liquid-feed flame spray pyrolysis synthesis of oxide nanopowders for the processing of ceramic composites

NASA Astrophysics Data System (ADS)

Taylor, Nathan John

In the liquid-feed flame spray pyrolysis (LF-FSP) process, alcohol solutions of metalloorganic precursors are aerosolized by O2 and combusted. The metal oxide combustion products are rapidly quenched (< 10 ms) from flame temperatures of 1500°C to temperatures < 400° C, limiting particle growth. The resulting nanopowders are typically agglomerated but unaggregated. Here, we demonstrate two processing approaches to dense materials: nanopowders with the exact composition, and mixed single metal oxide nanopowders. The effect of the initial degree of phase separation on the final microstructures was determined by sintering studies. Our first studies included the production of yttrium aluminum garnet, Y3Al5O12 (YAG), tubes which we extruded from a thermoplastic/ceramic blend. At equivalent final densities, we found finer grain sizes in the from the mixed Y2O3 and Al2 O3 nanopowders, which was attributed to densification occurring before full transformation to the YAG phase. The enhanced densification in production of pure YAG from the reactive sintering process led us to produce composites in the YAG/alpha-Al 2O3 system. Finally, a third Y2O3 stabilized ZrO2 (YSZ) phase was added to further refine grain sizes using the same two processing approaches. In a separate study, single-phase metastable Al2O3 rich spinels with the composition MO•3Al 2O3 where M = Mg, Ni, and Co were sintered to produce dense MAl2O4/alpha-Al2O3 composites. All of these studies provide a test of the bottom-up approach; that is, how the initial length scale of mixing affects the final composite microstructure. Overall, the length scale of mixing is highly dependent upon the specific oxide composites studied. This work provides a processing framework to be adopted by other researchers to further refine microstructural size. LF-FSP flame temperatures were mapped using different alcohols with different heats of combustion: methanol, ethanol, 1-propanol, and n-butanol. The effect of different alcohols on particle size and phase was determined through studies on Al2O3, Y2O3 and TiO2 nanopowders. The final studies describe the morphology of composite nanopowders produced in the WO3-TiO2 and CuO-TiO2 systems. The composite nanopowders have novel morphology, and may offer novel electronic, optical, or catalytic properties.

Unfolding grain size effects in barium titanate ferroelectric ceramics

PubMed Central

Tan, Yongqiang; Zhang, Jialiang; Wu, Yanqing; Wang, Chunlei; Koval, Vladimir; Shi, Baogui; Ye, Haitao; McKinnon, Ruth; Viola, Giuseppe; Yan, Haixue

2015-01-01

Grain size effects on the physical properties of polycrystalline ferroelectrics have been extensively studied for decades; however there are still major controversies regarding the dependence of the piezoelectric and ferroelectric properties on the grain size. Dense BaTiO3 ceramics with different grain sizes were fabricated by either conventional sintering or spark plasma sintering using micro- and nano-sized powders. The results show that the grain size effect on the dielectric permittivity is nearly independent of the sintering method and starting powder used. A peak in the permittivity is observed in all the ceramics with a grain size near 1 μm and can be attributed to a maximum domain wall density and mobility. The piezoelectric coefficient d33 and remnant polarization Pr show diverse grain size effects depending on the particle size of the starting powder and sintering temperature. This suggests that besides domain wall density, other factors such as back fields and point defects, which influence the domain wall mobility, could be responsible for the different grain size dependence observed in the dielectric and piezoelectric/ferroelectric properties. In cases where point defects are not the dominant contributor, the piezoelectric constant d33 and the remnant polarization Pr increase with increasing grain size. PMID:25951408

Space Weathering in the Fine Size Fractions of Lunar Soils: Soil Maturity Effects

NASA Technical Reports Server (NTRS)

Keller, L. P.; Wentworth, S. J.; McKay, D. S.; Taylor, L. A.; Pieters, C.; Morris, R. V.

1999-01-01

The effects of space weathering on the optical properties of lunar materials have been well documented. These effects include a reddened continuum slope, lowered albedo, and attenuated absorption features in reflectance spectra of lunar soils as compared to finely comminuted rocks from the same Apollo sites. However, the regolith processes that cause these effects are not well known, nor is the petrographic setting of the products of these processes fully understood. A Lunar Soil Characterization Consortium has been formed with the purpose of systematically integrating chemical and mineralogical data with the optical properties of lunar soils. Understanding space-weathering effects is critical in order to fully integrate the lunar sample collection with remotely-sensed data from recent robotic missions (e.g., Lunar Prospector, Clementine, and Galileo) We have shown that depositional processes (condensation of impact-derived vapors, sputter deposits, accreted impact material, e.g., splash glass, spherules, etc.) are a major factor in the modification of the optical surfaces of lunar regolith materials. In mature soils, it is the size and distribution of the nanophase metal in the soil grains that has the major effect on optical properties. In this report, we compare and contrast the space-weathering effects in an immature and a mature soil with similar elemental compositions. For this study, we analyzed <10 micron sieve fractions of two Apollo 17 soils, 79221 (mature, Is/FeO = 81) and 71061 (immature, Is/FeO = 14). Details of the sieving procedures and allocation scheme are given else where. The results of other detailed chemical, mineralogical, and spectroscopic analyses of these soil samples are reported elsewhere. A representative sample of each soil was embedded in low-viscosity epoxy, and thin sections (about 70nm thick) were obtained through ultra microtomy. The thin sections used for these analyses typically contained cross sections of up to 500 individual grains. The thin sections were studied using a JEOL 2010 transmission electron microscope (TEM) equipped with a thin window energy-dispersive X-ray (EDX) spectrometer. An individual thin section was selected from each soil, and for each grain in the section we determined (1) the elemental composition by EDX; (2) whether the grain was crystalline or glassy using electron diffraction and darkfield imaging; (3) the presence or absence of rims and accreted material; and (4) the distribution of nanophase Fe where present. Most of the categories are self-evident; however, we divide the agglutinate derived material into agglutinitic glass (glass with approximately the same composition as the bulk soil that contains nanophase Fe with or without vesicles) and agglutinate fragments, which are composed of crystalline grains and agglutinitic glass. Lithic fragments are defined as polymineralic grains with no glass. Pyroxene grains have been divided into high- and low-Ca groups. As expected, there are a number of differences in the petrography of the <10-microns fractions of 79221 and 71061 given the great difference in their respective maturities, but we focus here on two major distinctions: agglutinate content and the number of grains with micropatina. Slightly over 50% of the particles in 79221 consist of agglutinitic glass and agglutinate fragments, while the remainder are predominantly crystalline mineral grains. The agglutinic glass particles contain abundant nanophase Fe and vesicles. Angular particles are rare, with most showing smooth, rounded exteriors, Of the mineral grains analyzed thus far, over 90% of the grains have amorphous rims that contain nanophase Fe (these rims are believed to have formed by vapor deposition and irradiation effects). The nanophase Fe in these rims probably accounts for a significant fraction of the increase in Is/FeO measured in these size fractions. In addition to the rims, the majority of particles also show abundant accreted material in the form of glass splashes and spherules that also contain nanophase Fe. In stark contrast, the surfaces of the mineral grains in the 71061 sample are relatively prisitine, as only about 14% of the mineral grains in the sample exhibited amorphous rims. Furthermore, the mineral particles are more angular and show greater surface roughness than in the mature sample. Accreted material on particle surfaces is rare. Agglutinitic material is a major component of the 71061 sample; however, nanophase Fe and vesicles are not as well developed as in the 79221 sample. It is now recognized that nanophase Fe is probably the main agent in modifying the optical properties of lunar soil grains. The most important result of this study is the observation that in the fine size fractions of mature soils, nearly every grain has nanophase Fe within 100 run of the particle surface. (Additional Information contained in original)

A simple autocorrelation algorithm for determining grain size from digital images of sediment

USGS Publications Warehouse

Rubin, D.M.

2004-01-01

Autocorrelation between pixels in digital images of sediment can be used to measure average grain size of sediment on the bed, grain-size distribution of bed sediment, and vertical profiles in grain size in a cross-sectional image through a bed. The technique is less sensitive than traditional laboratory analyses to tails of a grain-size distribution, but it offers substantial other advantages: it is 100 times as fast; it is ideal for sampling surficial sediment (the part that interacts with a flow); it can determine vertical profiles in grain size on a scale finer than can be sampled physically; and it can be used in the field to provide almost real-time grain-size analysis. The technique can be applied to digital images obtained using any source with sufficient resolution, including digital cameras, digital video, or underwater digital microscopes (for real-time grain-size mapping of the bed). ?? 2004, SEPM (Society for Sedimentary Geology).

FIM/atom probe analysis of a heat treated 7150 aluminum alloy

NASA Astrophysics Data System (ADS)

Brenner, S. S.; Kowalik, J.; Hua Ming-Jian

1991-04-01

The stress corrosion cracking resistance of high strength aluminum alloys can be substantially altered by heat treatment. In addition to microstructural changes, the alloys may also undergo chemical changes as a result of the heat treatment which may affect the stress corrosion properties. The FIM/atom probe has been used to detect such changes. The compositions of the matrix, matrix precipitates, precipitate-free zone (PFZ) and grain boundary precipitates in a heat-treated 7150 Al alloy tempered to peak strength have been quantitatively measured. A substantial increase in the concentrations of Mg, Zn and Cu were found in the PFZ. The average compositions of the precipitates in the matrix and at the sub-boundaries were shown not to differ significantly. The coarser precipitates at high-angle boundaries, which may have a more important effect on stress corrosion, were difficult to analyze because of their low number density and the large grain size of the material.

Transmission Electron Microscopy of Cometary Residues from Micron-Sized Craters in the Stardust Al-Foils

NASA Technical Reports Server (NTRS)

Leroux, Hugues; Stroud, Rhonda M.; Dai, Zu Rong; Graham, Giles A.; Troadec, David; Bradley, John P.; Teslich, Nick; Borg, Janet; Kearsley, Anton T.; Horz, Friedrich

2008-01-01

We report Transmission Electron Microscopy (TEM) investigations of micro-craters that originated from hypervelocity impacts of comet 81P/Wild 2 dust particles on the aluminium foil of the Stardust collector. The craters were selected by Scanning Electron Microscopy (SEM) and then prepared by Focused Ion Beam (FIB) milling techniques in order to provide electron transparent cross-sections for TEM studies. The crater residues contain both amorphous and crystalline materials in varying proportions and compositions. The amorphous component is interpreted as resulting from shock melting during the impact and the crystalline phases as relict minerals. The latter show evidence for shock metamorphism. Based on the residue morphology and the compositional variation, the impacting particles are inferred to have been dominated by mixtures of submicron olivine, pyroxene and Fe-sulfide grains, in agreement with prior results of relatively coarse-grained mineral assemblages in the aerogel collector.

Interlinking backscatter, grain size and benthic community structure

NASA Astrophysics Data System (ADS)

McGonigle, Chris; Collier, Jenny S.

2014-06-01

The relationship between acoustic backscatter, sediment grain size and benthic community structure is examined using three different quantitative methods, covering image- and angular response-based approaches. Multibeam time-series backscatter (300 kHz) data acquired in 2008 off the coast of East Anglia (UK) are compared with grain size properties, macrofaunal abundance and biomass from 130 Hamon and 16 Clamshell grab samples. Three predictive methods are used: 1) image-based (mean backscatter intensity); 2) angular response-based (predicted mean grain size), and 3) image-based (1st principal component and classification) from Quester Tangent Corporation Multiview software. Relationships between grain size and backscatter are explored using linear regression. Differences in grain size and benthic community structure between acoustically defined groups are examined using ANOVA and PERMANOVA+. Results for the Hamon grab stations indicate significant correlations between measured mean grain size and mean backscatter intensity, angular response predicted mean grain size, and 1st principal component of QTC analysis (all p < 0.001). Results for the Clamshell grab for two of the methods have stronger positive correlations; mean backscatter intensity (r2 = 0.619; p < 0.001) and angular response predicted mean grain size (r2 = 0.692; p < 0.001). ANOVA reveals significant differences in mean grain size (Hamon) within acoustic groups for all methods: mean backscatter (p < 0.001), angular response predicted grain size (p < 0.001), and QTC class (p = 0.009). Mean grain size (Clamshell) shows a significant difference between groups for mean backscatter (p = 0.001); other methods were not significant. PERMANOVA for the Hamon abundance shows benthic community structure was significantly different between acoustic groups for all methods (p ≤ 0.001). Overall these results show considerable promise in that more than 60% of the variance in the mean grain size of the Clamshell grab samples can be explained by mean backscatter or acoustically-predicted grain size. These results show that there is significant predictive capacity for sediment characteristics from multibeam backscatter and that these acoustic classifications can have ecological validity.

Spatial and vertical distribution of soil physico-chemical properties and the content of heavy metals in the pedosphere in Poland

Treesearch

Marek Degorski

1998-01-01

The lithological and petrographical characteristics of soil pedogenesis was determined, and the spatial and vertical distribution of some soil physico-chemical properties (including heavy metal content) were studied along two transects in Poland. The genetic horizon for 22 soil profiles were described for particle size and petrographic composition, quartz grain...

Numerical study of electrical transport in co-percolative metal nanowire-graphene thin-films

NASA Astrophysics Data System (ADS)

Gupta, Man Prakash; Kumar, Satish

2016-11-01

Nanowires-dispersed polycrystalline graphene has been recently explored as a transparent conducting material for applications such as solar cells, displays, and touch-screens. Metal nanowires and polycrystalline graphene play synergetic roles during the charge transport in the material by compensating for each other's limitations. In the present work, we develop and employ an extensive computational framework to study the essential characteristics of the charge transport not only on an aggregate basis but also on individual constituents' levels in these types of composite thin-films. The method allows the detailed visualization of the percolative current pathways in the material and provides the direct evidence of current crowding in the 1-D nanowires and 2-D polygraphene sheet. The framework is used to study the effects of several important governing parameters such as length, density and orientation of the nanowires, grain density in polygraphene, grain boundary resistance, and the contact resistance between nanowires and graphene. We also present and validate an effective medium theory based generalized analytical model for the composite. The analytical model is in agreement with the simulations, and it successfully predicts the overall conductance as a function of several parameters including the nanowire network density and orientation and graphene grain boundaries. Our findings suggest that the longer nanowires (compared to grain size) with low angle orientation (<40°) with respect to the main carrier transport direction provide significant advantages in enhancing the conductance of the polygraphene sheet. We also find that above a certain value of grain boundary resistance (>60 × intra-grain resistance), the overall conductance becomes nearly independent of grain boundary resistance due to nanowires. The developed model can be applied to study other emerging transparent conducting materials such as nanowires, nanotubes, polygraphene, graphene oxide, and their hybrid nanostructures.

Microstructural Indicators Of Convection In Sills And Dykes

NASA Astrophysics Data System (ADS)

Holness, M. B.; Neufeld, J. A.; Gilbert, A. J.; Macdonald, R.

2016-12-01

The question of whether or not convection occurs in crustal magma chambers is a vexed one, with some advocating vigorous convection while others argue that convection is weak and short-lived. We argue that microstructural analysis is key to determining whether crystallization took place in solidification fronts or whether crystals grew suspended in a convecting magma before settling. The 168m, composite, Shiant Isles Main Sill is dominated by a 140m unit, of which the lower 45m contains olivine phenocrysts. The phenocrysts first fine upwards, then coarsen upwards. The coarsening-upwards sequence contains clustered olivines. Both the extent of sintering and average cluster size increase upwards. The coarsening-upwards sequence is mirrored at the roof. The fining-upwards sequence formed by rapid settling of incoming cargo crystals, while the coarsening-upwards sequence represents post-emplacement growth and clustering of grains suspended in a convecting magma. Convection is also recorded by plagioclase grain shape. Well-facetted and compact plagioclase grains are platy in rapidly-cooled rocks and blocky in slowly-cooled rocks. Plagioclase grain shape varies smoothly across mafic sills, consistent with growth in solidification fronts. In contrast, grain shape is invariant across mafic dykes, consistent with growth as individual grains and clusters suspended in a convecting magma. Convection in sills occurs when the critical Rayleigh number is exceeded, but cooling at vertical walls always results in convective instabilities. That the Shiant Isles Main Sill records prolonged and vigorous convection, while other sills of comparable thickness record grain growth predominantly in solidification fronts, is most likely due to the composite nature of the Shiant. The 140m unit is underlain by 23m of picrite which intruded shortly before - the strongly asymmetric cooling and absence of a cold, stagnant basal thermal boundary layer make convection throughout the sill more likely.

Experimental Investigation of Space Radiation Processing in Lunar Soil Ilmenite: Combining Perspectives from Surface Science and Transmission Electron Microscopy

NASA Technical Reports Server (NTRS)

Christoffersen, R.; Keller, L. P.; Rahman, Z.; Baragiola, R.

2010-01-01

Energetic ions mostly from the solar wind play a major role in lunar space weathering because they contribute structural and chemical changes to the space-exposed surfaces of lunar regolith grains. In mature mare soils, ilmenite (FeTiO3) grains in the finest size fraction have been shown in transmission electron microscope (TEM) studies to exhibit key differences in their response to space radiation processing relative to silicates [1,2,3]. In ilmenite, solar ion radiation alters host grain outer margins to produce 10-100 nm thick layers that are microstructurally complex, but dominantly crystalline compared to the amorphous radiation-processed rims on silicates [1,2,3]. Spatially well-resolved analytical TEM measurements also show nm-scale compositional and chemical state changes in these layers [1,3]. These include shifts in Fe/Ti ratio from strong surface Fe-enrichment (Fe/Ti >> 1), to Fe depletion (Fe/Ti < 1) at 40-50 nm below the grain surface [1,3]. These compositional changes are not observed in the radiation-processed rims on silicates [4]. Several mechanism(s) to explain the overall relations in the ilmenite grain rims by radiation processing and/or additional space weathering processes were proposed by [1], and remain under current consideration [3]. A key issue has concerned the ability of ion radiation processing alone to produce some of the deeper- penetrating compositional changes. In order to provide some experimental constraints on these questions, we have performed a combined X-ray photoelectron spectroscopy (XPS) and field-emission scanning transmission electron (FE-STEM) study of experimentally ion-irradiated ilmenite. A key feature of this work is the combination of analytical techniques sensitive to changes in the irradiated samples at depth scales going from the immediate surface (approx.5 nm; XPS), to deeper in the grain interior (5-100 nm; FE-STEM).

Structural and Optical Properties of Cd 1- x Se x Thin Films Deposited by Electron Beam Evaporation Technique

NASA Astrophysics Data System (ADS)

Tripathi, Ravishankar Nath; Verma, Aneet Kumar; Rahul, Vishwakarma, S. R.

2011-10-01

Cadmium selenide (CdSe) thin films deposited by means of electron beam evaporation technique under high vacuum ˜10 -5 torr on ultrasonically cleaned glass substrate. Using stating materials of various compositions of cadmium and selenium using formula Cd 1- x Se x where x is orbitory constant having value 0.20≤ x ≤0.40 here we take less value of x for the creation of anion vacancy in thin films. In present work the structural properties have been studies using XRD technique and found that starting materials and thin films both are polycrystalline in nature having hexagonal structure. Here we study the effect of composition ratio Cd/Se in starting material and its prepared thin films on its grain size and lattice parameter. From the analysis of X-Ray diffractogram found that lattice parameter and grain size both are decreases with increasing Cd/Se ratio in thin films as well as in starting material the preferred orientation in thin films along (100) plane. The surface morphology was studied using SEM characterization and found that films are smooth and homogeneous. The films have been analysed for optical band gap and absorbed a direct band gap.

A-site compositional effects in Ga-doped hollandite materials of the form BaxCsyGa2x+yTi8−2x−yO16: implications for Cs immobilization in crystalline ceramic waste forms

PubMed Central

Xu, Yun; Wen, Yi; Grote, Rob; Amoroso, Jake; Shuller Nickles, Lindsay; Brinkman, Kyle S.

2016-01-01

The hollandite structure is a promising crystalline host for Cs immobilization. A series of Ga-doped hollandite BaxCsyGa2x+yTi8−2x−yO16 (x = 0, 0.667, 1.04, 1.33; y = 1.33, 0.667, 0.24, 0) was synthesized through a solid oxide reaction method resulting in a tetragonal hollandite structure (space group I4/m). The lattice parameter associated with the tunnel dimension was found to increases as Cs substitution in the tunnel increased. A direct investigation of cation mobility in tunnels using electrochemical impedance spectroscopy was conducted to evaluate the ability of the hollandite structure to immobilize cations over a wide compositional range. Hollandite with the largest tunnel size and highest aspect ratio grain morphology resulting in rod-like microstructural features exhibited the highest ionic conductivity. The results indicate that grain size and optimized Cs stoichiometry control cation motion and by extension, the propensity for Cs release from hollandite. PMID:27273791

Structural Ceramic Nanocomposites: A Review of Properties and Powders’ Synthesis Methods

PubMed Central

Palmero, Paola

2015-01-01

Ceramic nanocomposites are attracting growing interest, thanks to new processing methods enabling these materials to go from the research laboratory scale to the commercial level. Today, many different types of nanocomposite structures are proposed in the literature; however, to fully exploit their exceptional properties, a deep understanding of the materials’ behavior across length scales is necessary. In fact, knowing how the nanoscale structure influences the bulk properties enables the design of increasingly performing composite materials. A further key point is the ability of tailoring the desired nanostructured features in the sintered composites, a challenging issue requiring a careful control of all stages of manufacturing, from powder synthesis to sintering. This review is divided into four parts. In the first, classification and general issues of nanostructured ceramics are reported. The second provides basic structure–property relations, highlighting the grain-size dependence of the materials properties. The third describes the role of nanocrystalline second-phases on the mechanical properties of ordinary grain sized ceramics. Finally, the fourth part revises the mainly used synthesis routes to produce nanocomposite ceramic powders, underlining when possible the critical role of the synthesis method on the control of microstructure and properties of the sintered ceramics. PMID:28347029

Porous silicon nanocrystals in a silica aerogel matrix

PubMed Central

2012-01-01

Silicon nanoparticles of three types (oxide-terminated silicon nanospheres, micron-sized hydrogen-terminated porous silicon grains and micron-size oxide-terminated porous silicon grains) were incorporated into silica aerogels at the gel preparation stage. Samples with a wide range of concentrations were prepared, resulting in aerogels that were translucent (but weakly coloured) through to completely opaque for visible light over sample thicknesses of several millimetres. The photoluminescence of these composite materials and of silica aerogel without silicon inclusions was studied in vacuum and in the presence of molecular oxygen in order to determine whether there is any evidence for non-radiative energy transfer from the silicon triplet exciton state to molecular oxygen adsorbed at the silicon surface. No sensitivity to oxygen was observed from the nanoparticles which had partially H-terminated surfaces before incorporation, and so we conclude that the silicon surface has become substantially oxidised. Finally, the FTIR and Raman scattering spectra of the composites were studied in order to establish the presence of crystalline silicon; by taking the ratio of intensities of the silicon and aerogel Raman bands, we were able to obtain a quantitative measure of the silicon nanoparticle concentration independent of the degree of optical attenuation. PMID:22805684

Porous silicon nanocrystals in a silica aerogel matrix.

PubMed

Amonkosolpan, Jamaree; Wolverson, Daniel; Goller, Bernhard; Polisski, Sergej; Kovalev, Dmitry; Rollings, Matthew; Grogan, Michael D W; Birks, Timothy A

2012-07-17

Silicon nanoparticles of three types (oxide-terminated silicon nanospheres, micron-sized hydrogen-terminated porous silicon grains and micron-size oxide-terminated porous silicon grains) were incorporated into silica aerogels at the gel preparation stage. Samples with a wide range of concentrations were prepared, resulting in aerogels that were translucent (but weakly coloured) through to completely opaque for visible light over sample thicknesses of several millimetres. The photoluminescence of these composite materials and of silica aerogel without silicon inclusions was studied in vacuum and in the presence of molecular oxygen in order to determine whether there is any evidence for non-radiative energy transfer from the silicon triplet exciton state to molecular oxygen adsorbed at the silicon surface. No sensitivity to oxygen was observed from the nanoparticles which had partially H-terminated surfaces before incorporation, and so we conclude that the silicon surface has become substantially oxidised. Finally, the FTIR and Raman scattering spectra of the composites were studied in order to establish the presence of crystalline silicon; by taking the ratio of intensities of the silicon and aerogel Raman bands, we were able to obtain a quantitative measure of the silicon nanoparticle concentration independent of the degree of optical attenuation.

The aggregation efficiency of very fine volcanic ash

NASA Astrophysics Data System (ADS)

Del Bello, E.; Taddeucci, J.; Scarlato, P.

2013-12-01

Explosive volcanic eruptions can discharge large amounts of very small sized pyroclasts (under 0.090 mm) into the atmosphere that may cause problems to people, infrastructures and environment. The transport and deposition of fine ash are ruled by aggregation that causes premature settling of fine ash and, as consequence, significantly reduces the concentration of airborne material over long distances. Parameterizing the aggregation potential of fine ash is then needed to provide accurate modelling of ash transport and deposition from volcanic plumes. Here we present the first results of laboratory experiments investigating the aggregation efficiency of very fine volcanic particles. Previous laboratory experiments have shown that collision kinetic and relative humidity provide the strongest effect on aggregation behaviour but were only limited to particles with size > 0.125 mm. In our work, we focus on natural volcanic ash at ambient humidity with particles size < 0.090 mm, by taking into account the effect of grain size distribution on aggregation potential. Two types of ash were used in our experiments: fresh ash, collected during fall-out from a recent plume-forming eruption at Sakurajima (Japan -July 2013) and old ash, collected from fall-out tephra deposits at Campi Flegrei (Italy, ca. 10 ka), to account for the different chemical composition and morphoscopic effects of altered ash on aggregation efficiency. Total samples were hand sieved to obtain three classes with unimodal grain size distributions (<0.090 mm, <0.063 mm, <0.032 mm). Bimodal grain size distributions were also obtained by mixing the three classes in different proportions. During each experiments, particles were sieved from the top of a transparent tank where a fan, placed at the bottom, allows turbulent dispersion of particles. Collision and sticking of particles on a vertical glass slide were filmed with a high speed cameras at 6000 fps. Our lenses arrangement provide high image resolution allowing to capture particles down to 0.005 mm in diameter. Video sequences of particles motion and collision were then processed with image analysis and particle tracking tools to determine i) the particle number density and ii) the grain size distribution of particles in the turbulent dispersion, and iii) the number of adhered particles as a function of time. Optical laser granulometry provided constrains on grain size distribution of ash particles effectively adhered to the glass slide at the end of each run. Results obtained from our data-set allowed to provide a relationship for determining aggregation rate as a function of particle number density across a range of particle size distributions. This empirical model can be used to determine the aggregation fraction starting from a given total grain size distribution, thus providing fundamental parameters to incorporate aggregation into numerical models of ash dispersal and deposition.

Understanding bias in provenance studies

NASA Astrophysics Data System (ADS)

Garzanti, Eduardo; Andò, Sergio; Malusà, Marco; Vezzoli, Giovanni

2010-05-01

Innumerable pieces of information are stored in the sedimentary archive. Each single sediment layer contains billions of detrital grains, and every grain preserves imprints of its geological story. If we learn to read, compare, and combine these messages properly, through a deeper understanding of physical and chemical processes that modify sediment composition during the sedimentary cycle, provenance analysis may eventually enable us to reconstruct more accurately the geological processes that shaped the Earth's crust in the past. Interpreting detrital modes is not straightforward because provenance signals issued from source rocks become progressively blurred by multiple noises in the sedimentary environment ("environmental bias"; Komar, 2007), and finally during post-depositional history ("diagenetic bias"; Morton and Hallsworth, 2007). During transport and deposition, detrital minerals are segregated in different size fractions and environments according to their size, density and shape (Rubey, 1933; Garzanti et al., 2008). Heavy-mineral concentration can increase by an order of magnitude due to selective-entrainment effects, with potentially overwhelming impact on chemical composition and provenance estimates based on detrital-geochronology data (Garzanti et al., 2009). Conversely, heavy-mineral concentration is typically reduced by an order of magnitude in Alpine and Himalayan foreland-basin deposits older than the Pleistocene (Garzanti and Andò, 2007). Extensive chemical dissolution can occur even prior to deposition during weathering in hot humid climates (Velbel, 2007). Primary provenance signals can be isolated and assessed by studying first modern sediments in hyperarid settings (i.e., free from diagenetic and weathering bias). Next, weathering, hydraulic-sorting, and diagenetic effects can be singled out by analysing sediments of similar provenance produced in contrasting climatic conditions, sediments transported in diverse modes and deposited in different subenvironments within a same system, and sediments of approximately constant provenance and progressively older age. Detangling the various interacting factors controlling mineralogical and chemical compositional variability is a fundamental pre-requisite to improve decisively not only on our ability to unravel provenance, but also to understand much about climatic, hydraulic, and diagenetic processes. Garzanti E., Andò S., 2007, Heavy-mineral concentration in modern sands: implications for provenance interpretation. In: Mange, M.A., Wright, D.T., (Eds.), Heavy Minerals in Use, Elsevier, Amsterdam, Developments in Sedimentology Series 58, 517-545. Garzanti, E., Andò, S., Vezzoli, G., 2008. Settling-equivalence of detrital minerals and grain-size dependence of sediment composition. Earth Planet. Sci. Lett. 273, 138-151. Garzanti E., Ando' S., Vezzoli G., 2009, Grain-size dependence of sediment composition and environmental bias in provenance studies, Earth Planet. Sci. Lett., 277, 422-432. Komar, P.D., 2007. The entrainment, transport and sorting of heavy minerals by waves and currents In: Mange, M.A., Wright, D.T., (Eds.), Heavy Minerals in Use, Elsevier, Amsterdam, Developments in Sedimentology Series 58, 3-48. Morton A.C., Hallsworth, C., 2007. Stability of detrital heavy minerals during burial diagenesis. In: Mange, M.A., Wright, D.T., (Eds.), Heavy Minerals in Use, Elsevier, Amsterdam, Developments in Sedimentology Series 58, 215-245. Rubey, W.W., 1933. The size-distribution of heavy minerals within a water-laid sandstone. J. Sedim. Petrol. 3, 3-29. Velbel, M.A., 2007. Surface textures and dissolution processes of heavy minerals in the sedimentary cycle: examples from pyroxenes and amphiboles. In: Mange, M.A., Wright, D.T., (Eds.), Heavy Minerals in Use, Elsevier, Amsterdam, Developments in Sedimentology Series 58, 113-150.

On the role of the grain size in the magnetic behavior of sintered permanent magnets

NASA Astrophysics Data System (ADS)

Efthimiadis, K. G.; Ntallis, N.

2018-02-01

In this work the finite elements method is used to simulate, by micromagnetic modeling, the magnetic behavior of sintered anisotropic magnets. Hysteresis loops were simulated for different grain sizes in an oriented multigrain sample. By keeping out other parameters that contribute to the magnetic microstructure, such as the sample size, the grain morphology and the grain boundaries mismatch, it has been found that the grain size affects the magnetic properties only if the grains are exchange-decoupled. In this case, as the grain size decreases, a decrease in the nucleation field of a reverse magnetic domain is observed and an increase in the coercive field due to the pinning of the magnetic domain walls at the grain boundaries.

Grain-size variations on a longitudinal dune and a barchan dune

NASA Astrophysics Data System (ADS)

Watson, Andrew

1986-01-01

The grain-size characteristics of the sand upon two dunes—a 40 m high longitudinal dune in the central Namib Desert and a 6.0 m high barchan in the Jafurah sand sea of Saudi Arabia—vary with position on the dunes. On the longitudinal dune, median grain size decreases, sorting improves and the grain-size distributions are less skewed and more normalized toward the crest. Though sand at the windward toe is distinct, elsewhere on the dune the changes in grain-size characteristics are gradual. An abrupt change in grain size and sorting near the crest—as described by Bagnold (1941, pp. 226-229)—is not well represented on this dune. Coarse grains remain as a lag on concave slope units and small particles are winnowed from the sand on the steepest windward slopes near the crest. Avalanching down slipfaces at the crest acts only as a supplementary grading mechanism. On the barchan dune median grain size also decreases near the crest, but sorting becomes poorer, though the grain-size distributions are more symmetric and more normalized. The dune profile is a Gaussian curve with a broad convex zone at the apex upon which topset beds had accreted prior to sampling. Grain size increases and sorting improves down the dune's slipface. However, this grading mechanism does not influence sand on the whole dune because variations in wind regime bring about different modes of dune accretion. On both dunes, height and morphology appear to influence significantly the grain-size characteristics.

Supernova graphite in the NanoSIMS: Carbon, oxygen and titanium isotopic compositions of a spherule and its TiC sub-components

NASA Astrophysics Data System (ADS)

Stadermann, F. J.; Croat, T. K.; Bernatowicz, T. J.; Amari, S.; Messenger, S.; Walker, R. M.; Zinner, E.

2005-01-01

Presolar graphite spherules from the Murchison low-density separate KE3 contain a large number of internal TiC crystals that range in size from 15 to 500 nm. We have studied one such graphite grain in great detail by successive analyses with SEM, ims3f SIMS, TEM and NanoSIMS. Isotopic measurements of the 'bulk' particle in the ims3f indicate a supernova origin for this graphite spherule. The NanoSIMS measurements of C, N, O and Ti isotopes were performed directly on TEM ultramicrotome sections of the spherule, allowing correlated studies of the isotopic and mineralogical properties of the graphite grain and its internal crystals. We found isotopic gradients in 12C/ 13C and 16O/ 18O from the core of the graphite spherule to its perimeter, with the most anomalous compositions being present in the center. These gradients may be the result of isotopic exchange with isotopically normal material, either in the laboratory or during the particle's history. No similar isotopic gradients were found in the 16O/ 17O and 14N/ 15N ratios, which are normal within analytical uncertainty throughout the graphite spherule. Due to an unusually high O signal, internal TiC crystals were easily located during NanoSIMS imaging measurements. It was thus possible to determine isotopic compositions of several internal TiC grains independent of the surrounding graphite matrix. These TiC crystals are significantly more anomalous in their O isotopes than the graphite, with 16O/ 18O ratios ranging from 14 to 250 (compared to a terrestrial value of 499). Even the most centrally located TiC grains show significant variations in their O isotopic compositions from crystal to crystal. Measurement of the Ti isotopes in three TiC grains found no variations among them and no large differences between the compositions of the different crystals and the 'bulk' graphite spherule. However, the same three TiC crystals vary by a factor of 3 in their 16O/ 18O ratios. It is not clear in what form the O is associated with the TiC grains and whether it is cogenetic or the result of surface reactions on the TiC grains before they accreted onto the growing graphite spherule. The presence of 44Ca from short-lived 44Ti (t 1/2 = 60y) in one of the TiC subgrains confirms the identification of this graphite spherule as a supernova condensate.

Dust grains in the coma of 67P/Churyumov-Gerasimenko - link with surface properties and cometary activity

NASA Astrophysics Data System (ADS)

Capria, M. T.; Ivanovski, S.; Zakharov, W.; Capaccioni, F.; Filacchione, G.; De Sanctis, M. C.; Rotundi, A.; Della Corte, V.; Longobardo, A.; Palomba, E.; Colangeli, L.; Bockelee-Morvan, D.; Erard, S.; Leyrat, C.

2016-11-01

The imaging spectrometer VIRTIS and the dust analyzer GIADA, onboard Rosetta, made an extensive observation of the dust particles in the coma of the comet 67P/Churyumov-Gerasimenko. From the analysis of GIADA data, two different kind of particles have been revealed, compact and fluffy with different compositions and dynamical properties. Compact particles are characterized by densities of about 10E3 kg/m3, while fluffy particles have an almost fractal nature, with densities less than 1 kg/m3. In this work we present the initial results of a model linking the dust flux distribution, as obtained from a theoretical thermal nucleus model, with a model describing the dynamics of aspherical grains in the coma. The results are discussed in the context of the latest observations from VIRTIS and GIADA instruments. The 2D nucleus thermal model, when applied to the real shape of the comet, provides the size distribution and physical properties of the emitted grains at different times and location on the surface. The thermal model can simulate grains of various size distribution, composition and physical properties. This information is used as an input for the dust dynamical model that follows the emitted particles in the coma. The main source of heating is the solar illumination. In the dust dynamical model, the grain trajectory of emitted particles remains in a plane perpendicular to the rotational axis and the direction of illumination is taken to be in the same plane (i.e. does not cause transversal forces). The dust particles are assumed to be isothermal convex bodies and temperature changes only induce modest changes in the aerodynamic force (twice higher temperature changes aerodynamic force less than 30%). This study reviews the theoretical values at which temperature difference starts to play a role on the dynamics. We discuss to what extent the particle's temperature affects the terminal velocities of the dust grains in the 67P coma in dependence on their mass and temperature constrained by the observations.

Dust grains in the coma of 67P/Churyumov-Gerasimenko - link with surface properties and cometary activity

NASA Astrophysics Data System (ADS)

Capria, Maria Teresa; Ivanovski, Stavro; Zakharov, Vladimir; Capaccioni, Fabrizio; Filacchione, Gianrico; De Sanctis, Maria Cristina; rotundi, alessandra; della corte, vincenzo; Longobardo, Andrea; Palomba, Ernesto; colangeli, luigi; Bockelee-Morvan, Dominique; Érard, Stéphane; Leyrat, Cedric; VIRTIS, GIADA

2016-10-01

The imaging spectrometer VIRTIS and the dust analyzer GIADA, onboard Rosetta, made an extensive observation of the dust particles in the coma of the comet 67P/Churyumov-Gerasimenko. From the analysis of GIADA data, two different kind of particles have been revealed, compact and fluffy with different compositions and dynamical properties. Compact particles are characterized by densities of about 103 kg/m3, while fluffy particles have an almost fractal nature, with densities less than 1 kg/m3.In this work we present the initial results of a model linking the dust flux distribution, as obtained from a theoretical thermal nucleus model, with a model describing the dynamics of aspherical grains in the coma. The results are discussed in the context of the latest observations from VIRTIS and GIADA instruments.The 2D nucleus thermal model, when applied to the real shape of the comet, provides the size distribution and physical properties of the emitted grains at different times and location on the surface. The thermal model can simulate grains of various size distribution, composition and physical properties. This information is used as an input for the dust dynamical model that follows the emitted particles in the coma. The main source of heating is the solar illumination. In the dust dynamical model, the grain trajectory of emitted particles remains in a plane perpendicular to the rotational axis and the direction of illumination is taken to be in the same plane (i.e. does not cause transversal forces). The dust particles are assumed to be isothermal convex bodies and temperature changes only induce modest changes in the aerodynamic force (twice higher temperature changes aerodynamic force less than ~30%). This study reviews the theoretical values at which temperature difference starts to play a role on the dynamics. We discuss to what extent the particle's temperature affects the terminal velocities of the dust grains in the 67P coma in dependence on their mass and temperature constrained by the observations.

The Femtosecond Laser Ablation on Ultrafine-Grained Copper

NASA Astrophysics Data System (ADS)

Lu, Jianxun; Wu, Xiaoyu; Ruan, Shuangchen; Guo, Dengji; Du, Chenlin; Liang, Xiong; Wu, Zhaozhi

2018-07-01

To investigate the effects of femtosecond laser ablation on the surface morphology and microstructure of ultrafine-grained copper, point, single-line scanning, and area scanning ablation of ultrafine-grained and coarse-grained copper were performed at room temperature. The ablation threshold gradually increased and materials processing became more difficult with decreasing grain size. In addition, the ablation depth and width of the channels formed by single-line scanning ablation gradually increased with increasing grain size for the same laser pulse energy. The microhardness of the ablated specimens was also evaluated as a function of laser pulse energy using area scanning ablation. The microhardness difference before and after ablation increased with decreasing grain size for the same laser pulse energy. In addition, the microhardness after ablation gradually decreased with increasing laser pulse energy for the ultrafine-grained specimens. However, for the coarse-grained copper specimens, no clear changes of the microhardness were observed after ablation with varying laser pulse energies. The grain sizes of the ultrafine-grained specimens were also surveyed as a function of laser pulse energy using electron backscattered diffraction (EBSD). The heat generated by laser ablation caused recrystallization and grain growth of the ultrafine-grained copper; moreover, the grain size gradually increased with increasing pulse energy. In contrast, no obvious changes in grain size were observed for the coarse-grained copper specimens with increasing pulse energy.

The Femtosecond Laser Ablation on Ultrafine-Grained Copper

NASA Astrophysics Data System (ADS)

Lu, Jianxun; Wu, Xiaoyu; Ruan, Shuangchen; Guo, Dengji; Du, Chenlin; Liang, Xiong; Wu, Zhaozhi

2018-05-01

To investigate the effects of femtosecond laser ablation on the surface morphology and microstructure of ultrafine-grained copper, point, single-line scanning, and area scanning ablation of ultrafine-grained and coarse-grained copper were performed at room temperature. The ablation threshold gradually increased and materials processing became more difficult with decreasing grain size. In addition, the ablation depth and width of the channels formed by single-line scanning ablation gradually increased with increasing grain size for the same laser pulse energy. The microhardness of the ablated specimens was also evaluated as a function of laser pulse energy using area scanning ablation. The microhardness difference before and after ablation increased with decreasing grain size for the same laser pulse energy. In addition, the microhardness after ablation gradually decreased with increasing laser pulse energy for the ultrafine-grained specimens. However, for the coarse-grained copper specimens, no clear changes of the microhardness were observed after ablation with varying laser pulse energies. The grain sizes of the ultrafine-grained specimens were also surveyed as a function of laser pulse energy using electron backscattered diffraction (EBSD). The heat generated by laser ablation caused recrystallization and grain growth of the ultrafine-grained copper; moreover, the grain size gradually increased with increasing pulse energy. In contrast, no obvious changes in grain size were observed for the coarse-grained copper specimens with increasing pulse energy.

A novel route for processing cobalt–chromium–molybdenum orthopaedic alloys

PubMed Central

Patel, Bhairav; Inam, Fawad; Reece, Mike; Edirisinghe, Mohan; Bonfield, William; Huang, Jie; Angadji, Arash

2010-01-01

Spark plasma sintering has been used for the first time to prepare the ASTM F75 cobalt–chromium–molybdenum (Co–Cr–Mo) orthopaedic alloy composition using nanopowders. In the preliminary work presented in this report, the effect of processing variables on the structural features of the alloy (phases present, grain size and microstructure) has been investigated. Specimens of greater than 99.5 per cent theoretical density were obtained. Carbide phases were not detected in the microstructure but oxides were present. However, harder materials with finer grains were produced, compared with the commonly used cast/wrought processing methods, probably because of the presence of oxides in the microstructure. PMID:20200035

DOE Office of Scientific and Technical Information (OSTI.GOV)

Palomba, M., E-mail: mariano.palomba@cnr.it; Carotenuto, G.; Binetti, S.

Owing to the very brittle nature of the tellurium powder, nanoscopic grains with average size of 4.8 nm were produced by dry vibration milling technique using a Mixer mill apparatus. A novel material was obtained by binding the nanosized tellurium grains with poly(methyl methacrylate) (PMMA). The morphology, elemental composition, and structural properties of Te/PMMA films were investigated. The prepared material was composed of hexagonal tellurium and α-phase of tellurium oxide. The electrical properties of the films were studied in dark condition and under white light illumination varying the optical power density from 10 to 170 mW/cm{sup 2} and turning onmore » and off the light cyclically.« less

SULFUR ISOTOPIC COMPOSITIONS OF SUBMICROMETER SiC GRAINS FROM THE MURCHISON METEORITE

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xu, Yuchen; Zinner, Ernst; Gallino, Roberto

2015-02-01

We report C, Si, N, S, Mg-Al, and Ca-Ti isotopic compositions of presolar silicon carbide (SiC) grains from the SiC-rich KJE size fraction (0.5-0.8 μm) of the Murchison meteorite. One thousand one hundred thirteen SiC grains were identified based on their C and Si isotopic ratios. Mainstream, AB, C, X, Y, and Z subtypes of SiC, and X-type silicon nitride (Si{sub 3}N{sub 4}) account for 81.4%, 5.7%, 0.1%, 1.5%, 5.8%, 4.9%, and 0.4%, respectively. Twenty-five grains with unusual Si isotopic ratios, including one C grain, 16 X grains, 1 Y grain, 5 Z grains, and 2 X-type Si{sub 3}N{sub 4} grainsmore » were selected for N, S, Mg-Al, and Ca-Ti isotopic analysis. The C grain is highly enriched in {sup 29}Si and {sup 30}Si (δ{sup 29}Si = 1345‰ ± 19‰, δ{sup 30}Si = 1272‰ ± 19‰). It has a huge {sup 32}S excess, larger than any seen before, and larger than that predicted for the Si/S supernova (SN) zone, providing evidence against the elemental fractionation model by Hoppe et al. Two SN models investigated here present a more satisfying explanation in terms of a radiogenic origin of {sup 32}S from the decay of short-lived {sup 32}Si (τ{sub 1/2} = 153 yr). Silicon-32 as well as {sup 29}Si and {sup 30}Si can be produced in SNe by short neutron bursts; evidence for initial {sup 44}Ti (τ{sub 1/2} = 60 yr) in the C grain is additional evidence for an SN origin. The X grains have marginal {sup 32}S excesses, much smaller than expected from their large {sup 28}Si excesses. Similarly, the Y and Z grains do not show the S-isotopic anomalies expected from their large Si isotopic anomalies. Low intrinsic S contents and contamination with isotopically normal S are the most likely explanations.« less

Determination of grain-size characteristics from electromagnetic seabed mapping data: A NW Iberian shelf study

NASA Astrophysics Data System (ADS)

Baasch, Benjamin; Müller, Hendrik; von Dobeneck, Tilo; Oberle, Ferdinand K. J.

2017-05-01

The electric conductivity and magnetic susceptibility of sediments are fundamental parameters in environmental geophysics. Both can be derived from marine electromagnetic profiling, a novel, fast and non-invasive seafloor mapping technique. Here we present statistical evidence that electric conductivity and magnetic susceptibility can help to determine physical grain-size characteristics (size, sorting and mud content) of marine surficial sediments. Electromagnetic data acquired with the bottom-towed electromagnetic profiler MARUM NERIDIS III were analysed and compared with grain size data from 33 samples across the NW Iberian continental shelf. A negative correlation between mean grain size and conductivity (R=-0.79) as well as mean grain size and susceptibility (R=-0.78) was found. Simple and multiple linear regression analyses were carried out to predict mean grain size, mud content and the standard deviation of the grain-size distribution from conductivity and susceptibility. The comparison of both methods showed that multiple linear regression models predict the grain-size distribution characteristics better than the simple models. This exemplary study demonstrates that electromagnetic benthic profiling is capable to estimate mean grain size, sorting and mud content of marine surficial sediments at a very high significance level. Transfer functions can be calibrated using grains-size data from a few reference samples and extrapolated along shelf-wide survey lines. This study suggests that electromagnetic benthic profiling should play a larger role for coastal zone management, seafloor contamination and sediment provenance studies in worldwide continental shelf systems.

Orientation influence on grain size-effects in ultrafine-grained magnesium

DOE PAGES

Fan, Haidong; Aubry, Sylvie; Arsenlis, A.; ...

2014-11-08

The mechanical behavior of ultrafine-grained magnesium was studied by discrete dislocation dynamics (DDD) simulations. Our results show basal slip yields a strong size effect, while prismatic and pyramidal slips produce a weak one. We developed a new size-strength model that considers dislocation transmission across grain boundaries. Good agreement between this model, current DDD simulations and previous experiments is observed. These results reveal that the grain size effect depends on 3 factors: Peierls stress, dislocation source strength and grain boundary strength.

40Ar/39Ar mica ages from marble mylonites: a cautionary tale

NASA Astrophysics Data System (ADS)

Rogowitz, Anna; Huet, Benjamin; Schneider, David; Grasemann, Bernhard

2014-05-01

40Ar/39Ar geochronology on white mica is a popular method to date deformation under moderate (brittle-ductile) temperatures. In particular, deformation events preserved in greenschist facies shear zones have been successfully dated with this method. A consequence of strain localization in many tectonic settings that bear calcitic marbles is the formation of marble mylonites and ultramylonites. Little is known, however, about the behaviour of the K/Ar systems and the influence of deformation on the ages in such rocks. We studied an extremely localized shear zone (2 cm thick) in marble from Syros (Cyclades, Greece) and performed microstructural, chemical and isotopic analysis on samples from the host rock and the shear zone. The host rock is composed of coarse-grained (300 µm) calcite with only minor undulatory extinction and slightly curved grain boundaries. This initial large grain size is likely to have formed during the Eocene high-pressure - low-temperature event that is well documented in the Cyclades. In contrast, the marble within the shear zone shows evidence of strong intracrystalline deformation and recrystallization resulting in grain size reduction and the formation of an ultramylonite. Both microstructures and kinematics are consistent with the low grade evolution described on Syros. White mica (100's microns in size) are preferentially orientated parallel to the foliation. In both samples there is no clear evidence for crystal plastic deformation of the mica grains. Bigger grains behave brittle resulting in grain size reduction. A deformation mechanism map for calcite at 300 °C indicates that the host rock deformed at strain rates of around 10-12.5 s-1 whereas within the shear zone strain rates of up to 10-9.5 s-1 are attained. We performed laser-heating 40Ar/39Ar analysis on white mica located in the host rock and the shear zone. The low-strain host rock yielded a ca. 40 Ma age, and the shear zone recorded a ca. 37 Ma age; both ages are statistically indistinguishable when errors are considered. These dates correspond to the regional Eocene high-pressure - low-temperature event and not the later low grade deformation event that is responsible for the formation of the studied shear zone. Although the marble within the shear zone was deformed at extremely fast strain rates, we observe no resetting in the isotopic system. Moreover, mineral chemistry demonstrates that (1) white mica is homogeneous and (2) there is no compositional difference between the host rock and the shear zone. This is in agreement with thermodynamical modelling, which indicates that the observed assemblage (calcite + dolomite + quartz + white mica) is stable without any composition change along the pressure-temperature path followed by the metamorphic rocks of Syros. Our case study emphasizes it is not the amount of strain the rock suffered but the degree of mica recrystallization that is important for resetting of the K/Ar system at low temperatures.

Constraints on Grain Formation Around Carbon Stars from Laboratory Studies of Presolar Graphite

NASA Technical Reports Server (NTRS)

Bernatowicz, T. J.; Akande, O. W.; Croat, T. K.; Cowsik, R.

2005-01-01

We report the results of an investigation into the physical conditions in the mass outflows of asymptotic giant branch (AGB) carbon stars that are required for the formation of micron-sized presolar graphite grains, either with or without internal crystals of titanium carbide (TiC). In addition to providing detailed information about stellar nucleosynthesis, the structure and composition of presolar grains give unique information about the conditions of grain formation. In the present work we use laboratory observations of presolar graphite to gain insight into the physical conditions in circumstellar outflows from carbon AGB stars. The periodic pulsation of AGB stars enhances the gas density through shocks in the stellar atmosphere above the photosphere, promoting the condensation of dust grains. Copious mass outflow occurs largely because grains are coupled to the radiation field of the star, which accelerates them by radiation pressure; momentum is in turn transferred to gas molecules by collisions with grains. The dust/gas mixture is effectively a two-component fluid whose motion depends on atmospheric structure and which, in turn, influences that structure. In particular, the radiation pressure on the grains determines the velocity field of the outflow and thus the density distribution, while the density distribution itself determines the conditions of radiative transfer within the outflow and thus the effective radiation pressure.

Effects of grain size on the corrosion resistance of pure magnesium by cooling rate-controlled solidification

NASA Astrophysics Data System (ADS)

Liu, Yichi; Liu, Debao; You, Chen; Chen, Minfang

2015-09-01

The aim of this study was to investigate the effect of grain size on the corrosion resistance of pure magnesium developed for biomedical applications. High-purity magnesium samples with different grain size were prepared by the cooling rate-controlled solidification. Electrochemical and immersion tests were employed to measure the corrosion resistance of pure magnesium with different grain size. The electrochemical polarization curves indicated that the corrosion susceptibility increased as the grain size decrease. However, the electrochemical impedance spectroscopy (EIS) and immersion tests indicated that the corrosion resistance of pure magnesium is improved as the grain size decreases. The improvement in the corrosion resistance is attributed to refine grain can produce more uniform and density film on the surface of sample.

Dunes Around Khnifiss Lagoon (Tarfaya, SW of Morocco): Composition, Itinerary In Dune Fields, Effects on Dunes' Colours and Morphodynamic

NASA Astrophysics Data System (ADS)

Adnani, M.; Azzaoui, M. A.; Elbelrhiti, H.; Ahmamou, M.; Masmoudi, L.

2015-12-01

Dunes around Khnifiss lagoon (28° 3'N, 12°13'W) show different colors ranging from black at the beach, whitish yellow in transverse dunes near the beach to reddish at the mega barchans situated few kilometers in the SW. The scientific question is about the abundance of different dunes in the same environmental conditions. The present work aims to investigate the factors that influence dunes color change, and then at which degree these factors could control dunes stability. To highlight the difference in color observed at the dune fields then to characterize dunes mineralogy, Landsat TM images were used in addition to mineralogical analysis that was carried out for the black grains samples originated from megabarchans. Optic Microscope and SEM- EDS data was adopted, in addition to physico-chemical analysis provided by Electronic Microprobe. Grain size and shape analysis were conducted to characterize the different types of grains of sand. 3/1 Landsat image band ratio allowed iron oxide distinction, the results revealed the importance of iron oxide concentration. Furthermore, mineralogical and physico-chemical analysis revealed (i) a high grade of oxides (Rutile, Ilmenite, Magnetite, Ulvöspinel) in samples, (ii) silicates (Quartz, Clinopyroxene, feldspar, Zircon), (iii) phosphate (apatite) and (iv) carbonate (calcite). The grain size analysis of the sand originated from the megabarchans reveals that there are three populations of sand. Black grains with a diameter less than 100μm and dominated by the magnetite, red ones composed mainly by the quartz with diameter between 100 and 180 μm and grains with diameter more than 180 μm are white and composed by carbonates. The threshold of motion of these different grains was calculated. It shows that these different grains have the same threshold of motion, which means that the grain size compensates the density. This explains the abundance of different populations of sand in the same environment. The dominance of iron oxides justified the color black in sand. However, the whitish yellow and reddish color observed in dunes could be attributed to iron oxide clay coating, produced under weathering conditions, covering the grains of quartz. Key words: black sand, Landsat, Iron Oxide, Khnifiss beach, megadunes, Tarfaya, Morocco

AFM Studies of Lunar Soils and Application to the Mars 2001 Mission

NASA Technical Reports Server (NTRS)

Weitz, C. M.; Anderson, M. S.; Marshall, J.

1999-01-01

The upcoming Mars 01 mission will carry an Atomic Force Microscope (AFM) as part of the Mars Environmental Compatibility Assessment (MECA) instrument. By operating in a tapping mode, the AFM is capable of sub-nanometer resolution in three dimensions and can distinguish between substances of different compositions by employing phase contrast imaging. To prepare for the Mars 01 mission, we are testing the AFM on a lunar soil to determine its ability to define particle shapes and sizes and grain-surface textures. The test materials are from the Apollo 17 soil 79221, which is a mixture of agglutinates, impact and volcanic beads, and mare and highland rock and mineral fragments. The majority of the lunar soil particles are less than 100 microns in size, comparable to the sizes estimated for martian dust. We have used the AFM to examine several different soil particles at various resolutions. The instrument has demonstrated the ability to identify parallel ridges characteristic of twinning on a 150 micron plagioclase feldspar particle. Extremely small (10-100 nanometer) adhering particles are visible on the surface of the feldspar grain, and they appear elongate with smooth surfaces. Phase contrast imaging of the nanometer particles shows several compositions to be present. When the AFM was applied to a 100 micron glass spherule, it was possible to define an extremely smooth surface; this is in clear contrast to results from a basalt fragment which exhibited a rough surface texture. Also visible on the surface of the glass spherule were chains of 100 nanometer and smaller impact melt droplets. For the '01 Mars mission, the AFM is intended to define the size and shape distributions of soil particles, in combination with the NMCA optical microscope system and images from the Robot Arm Camera (RAC). These three data sets will provide a means of assessing potentially hazardous soil and dust properties. The study that we have conducted on the lunar soils now suggests that the NMCA experiment will be able to define grain transport and weathering processes. For example, it should be possible to determine if Martian grains have been subjected to aeolian or water transport, volcanic activity, impact melting processes, in-situ weathering, and a host of other processes. Additionally, textural maturity could be assessed (via freshness and form of fracture patterns and grain shapes). Thus, the AFM has the potential to shed new light on Martian surface processes by adding the submicroscopic dimension to planetary investigations.

Magnetospheric ion sputtering and water ice grain size at Europa

NASA Astrophysics Data System (ADS)

Cassidy, T. A.; Paranicas, C. P.; Shirley, J. H.; Dalton, J. B., III; Teolis, B. D.; Johnson, R. E.; Kamp, L.; Hendrix, A. R.

2013-03-01

We present the first calculation of Europa's sputtering (ion erosion) rate as a function of position on Europa's surface. We find a global sputtering rate of 2×1027 H2O s-1, some of which leaves the surface in the form of O2 and H2. The calculated O2 production rate is 1×1026 O2 s-1, H2 production is twice that value. The total sputtering rate (including all species) peaks at the trailing hemisphere apex and decreases to about 1/3rd of the peak value at the leading hemisphere apex. O2 and H2 sputtering, by contrast, is confined almost entirely to the trailing hemisphere. Most sputtering is done by energetic sulfur ions (100s of keV to MeV), but most of the O2 and H2 production is done by cold oxygen ions (temperature ∼ 100 eV, total energy ∼ 500 eV). As a part of the sputtering rate calculation we compared experimental sputtering yields with analytic estimates. We found that the experimental data are well approximated by the expressions of Famá et al. for ions with energies less than 100 keV (Famá, M., Shi, J., Baragiola, R.A., 2008. Sputtering of ice by low-energy ions. Surf. Sci. 602, 156-161), while the expressions from Johnson et al. fit the data best at higher energies (Johnson, R.E., Burger, M.H., Cassidy, T.A., Leblanc, F., Marconi, M., Smyth, W.H., 2009. Composition and Detection of Europa's Sputter-Induced Atmosphere, in: Pappalardo, R.T., McKinnon, W.B., Khurana, K.K. (Eds.), Europa. University of Arizona Press, Tucson.). We compare the calculated sputtering rate with estimates of water ice regolith grain size as estimated from Galileo Near-Infrared Mapping Spectrometer (NIMS) data, and find that they are strongly correlated as previously suggested by Clark et al. (Clark, R.N., Fanale, F.P., Zent, A.P., 1983. Frost grain size metamorphism: Implications for remote sensing of planetary surfaces. Icarus 56, 233-245.). The mechanism responsible for the sputtering rate/grain size link is uncertain. We also report a surface composition estimate using NIMS data from an area on the trailing hemisphere apex. We find a high abundance of sulfuric acid hydrate and radiation-resistant hydrated salts along with large water ice regolith grains, all of which are consistent with the high levels of magnetospheric bombardment at the trailing apex.

Microscopy of Analogs for Martian Dust and Soil

NASA Technical Reports Server (NTRS)

Anderson, M. A.; Pike, W. T.; Weitz, C. M.

1999-01-01

The upcoming Mars 2001 lander will carry an atomic force microscope (AFM) as part of the Mars Environmental Compatibility Assessment (MECA) payload. By operating in a tapping mode, the AFM is capable of sub-nanometer resolution in three dimensions and can distinguish between substances of different compositions by employing phase-contrast imaging. Phase imaging is an extension of tapping-mode AFM that provides nanometer-scale information about surface composition not revealed in the topography. Phase imaging maps the phase of the cantilever oscillation during the tapping mode scan, hence detecting variations in composition, adhesion, friction, and viscoelasticity. Because phase imaging highlights edges and is not affected by large-scale height differences, it provides for clearer observation of fine features, such as grain edges, which can be obscured by rough topography. To prepare for the Mars 01 mission, we are testing the AFM on a lunar soil and terrestrial basaltic glasses to determine the AFMOs ability to define particle shapes and sizes and grain-surface textures. The test materials include the Apollo 17 soil 79221, which is a mixture of agglutinates, impact and volcanic beads, and mare and highland rock and mineral fragments. The majority of the lunar soil particles are less than 100 microns in size, comparable to the sizes estimated for Martian dust. The terrestrial samples are millimeter size basaltic glasses collected on Black Pointe at Mono Lake, just north of the Long Valley caldera in California. The basaltic glass formed by a phreatomagmatic eruption 13,000 years ago beneath a glacier that covered the Mono Lake region. Because basaltic glass formed by reworking of pyroclastic deposits may represent a likely source for Martian dunes, these basaltic glass samples represent plausible analogs to the types of particles that may be studied in sand dunes by the 01 lander and rover. We have used the AFM to examine several different soil particles at various resolutions. The instrument has demonstrated the ability to identify parallel ridges characteristic of twinning on a 150-micron plagioclase feldspar particle. Extremely small (10-100 nanometer) adhering particles are visible on the surface of the feldspar grain, and appear elongate with smooth surfaces. Phase contrast imaging of the nanometer particles shows several compositions to be present. When the AFM was applied to a 100-micron glass spherule, it was possible to define an extremely smooth surface.E Also visible on the surface of the glass spherule were chains of 100-nanometer- and-smaller impact melt droplets. Additional information is contained in the original extended abstract.

Non-Destructive Evaluation of Grain Structure Using Air-Coupled Ultrasonics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Belvin, A. D.; Burrell, R. K.; Cole, E.G.

2009-08-01

Cast material has a grain structure that is relatively non-uniform. There is a desire to evaluate the grain structure of this material non-destructively. Traditionally, grain size measurement is a destructive process involving the sectioning and metallographic imaging of the material. Generally, this is performed on a representative sample on a periodic basis. Sampling is inefficient and costly. Furthermore, the resulting data may not provide an accurate description of the entire part's average grain size or grain size variation. This project is designed to develop a non-destructive acoustic scanning technique, using Chirp waveforms, to quantify average grain size and grain sizemore » variation across the surface of a cast material. A Chirp is a signal in which the frequency increases or decreases over time (frequency modulation). As a Chirp passes through a material, the material's grains reduce the signal (attenuation) by absorbing the signal energy. Geophysics research has shown a direct correlation with Chirp wave attenuation and mean grain size in geological structures. The goal of this project is to demonstrate that Chirp waveform attenuation can be used to measure grain size and grain variation in cast metals (uranium and other materials of interest). An off-axis ultrasonic inspection technique using air-coupled ultrasonics has been developed to determine grain size in cast materials. The technique gives a uniform response across the volume of the component. This technique has been demonstrated to provide generalized trends of grain variation over the samples investigated.« less

The spatial distribution of major and trace elements in the surface sediments from the northeastern Beibu Gulf, South China Sea

NASA Astrophysics Data System (ADS)

Ge, Q.; Xue, Z. G.

2017-12-01

Major and trace elements contents and grain size were analyzed for surface sediments retrieved from the northeastern Beibu (Tonkin) Gulf. The study area was divided into four zones: Zone I locates in the northeastern coastal area of the gulf, which received large amount of the fluvial materials from local rivers; Zone II locates in the center of the study area, where surface sediments is from multiple sources; Zone III locates in the Qiongzhou Strait, which is dominated by material from the Pearl River and Hainan Island; Zone IV locates in the southwest of the study area, and the sediments mainly originated from the Red River. Statistical analyses of sediment geochemical characteristics reveal that grain size is the leading factor for elementary distribution, which is also influenced by hydrodynamics, mineral composition of terrigenous sediments, anthropogenic activity, and authigenic components.

Holocene variations in mineral and grain-size composition along the East Greenland glaciated margin (ca 67°–70°N): local versus long-distance sediment transport

USGS Publications Warehouse

Andrews, John T.; Jennings, Anne E.; Coleman, George C.; Eberl, Dennis D.

2010-01-01

Quantitative X-Ray Diffraction (qXRD) analysis of the <2 mm sediment fraction from surface (sea floor) samples, and marine sediment cores that span the last 10-12 cal ka BP, are used to describe spatial and temporal variations in non-clay mineral compositions for an area between Kangerlussuaq Trough and Scoresby Sund (???67??-70??N), East Greenland. Bedrock consists primarily of an early Tertiary alkaline complex with high weight% of pyroxene and plagioclase. Farther inland and to the north, the bedrock is dominantly felsic with a high fraction of quartz and potassium feldspars. Principal Component (PC) analysis of the non-clay sediment compositions indicates the importance of quartz and pyroxene as compositional end members, with an abrupt shift from quartz and k-feldspar dominated sediments north of Scoresby Sund to sediments rich in pyroxene and plagioclase feldspars offshore from the early Tertiary basaltic outcrop. Coarse (<2 mm or <1 mm) ice-rafted sediments are largely absent from the trough sediments between ???8 and 5 cal ka BP, but then increase in the last 4 cal ka BP. Compositional unmixing of the sediments in Grivel Basin and Kangerlussuaq Trough indicate the dominance of local over long distance sediment sources, with pulses of sediment from tidewater glaciers in Kangerlussuaq and Nansen fjords reaching the inner shelf during the Neoglaciation. The change in IRD is more dramatic in the sediment grain-size proxies than in the quartz wt%. Forty to seventy percent of the variance in the quartz records from either side of Denmark Strait is explained by low frequency trends, but the data from the Grivel Basin, East Greenland, are distinctly different, with an approximate 2500 yr periodicity. ?? 2010 Elsevier Ltd.

Multidisciplinary studies of the dust storm that affected Sydney in September 2009

NASA Astrophysics Data System (ADS)

De Deckker, P.

2012-04-01

A major dust storm transgressed over southeastern Australia in September 2009 and continued as far as northern Queensland [to the north], New Zealand and New Caledonia [to the east] . We analysed samples of the dust for organic compounds, its microbiological composition, pollen, trace and rare earth elements as well as Sr and Nd isotopes. Grain size analysis was also performed on some of the samples. We also obtained information on the meteorological conditions that led to the large dust plume and its pathway. Our geochemical fingerprinting allowed us to determine the origin of the dust, and this was confirmed by meteorological observations and satellite imagery. As the pathway of the dust plume went over the city of Canberra, located to the southwest of Sydney, we were able to collect samples of dust that fell with rain, and the surprise was that the geochemical composition of the dust varied with time [and dust fall], identifying that as the dust plume transgressed over the landscape, it picked up additional material that was compositionally different from its point of origin. We also compared our data with those obtained from another major dust event that affected Canberra in October 2002, and a number of important differences are noted, particularly with respect of the microbiological composition of the dust, and its chemical composition. Collaborators on this project are: Chris Munday and Gwen Allison [microbiology]: Research School of Biology, ANU; Jochen Brocks and Janet Hope [organic chemistry] and Marc Norman [inorganic geochemistry]: Research School of Earth Sciences, ANU; Tadhg O'Loingsigh and Nigel Tapper [meteorology, satellite imagery] and Sander van der Kaars [palynology]: Geography and Environmental Science, Monash University; and J.-B. Stuut [grain size analysis], NIOZ.

Calculating permittivity of semi-conductor fillers in composites based on simplified effective medium approximation models

NASA Astrophysics Data System (ADS)

Feng, Yefeng; Wu, Qin; Hu, Jianbing; Xu, Zhichao; Peng, Cheng; Xia, Zexu

2018-03-01

Interface induced polarization has a significant impact on permittivity of 0–3 type polymer composites with Si based semi-conducting fillers. Polarity of Si based filler, polarity of polymer matrix and grain size of filler are closely connected with induced polarization and permittivity of composites. However, unlike 2–2 type composites, the real permittivity of Si based fillers in 0–3 type composites could be not directly measured. Therefore, achieving the theoretical permittivity of fillers in 0–3 composites through effective medium approximation (EMA) models should be very necessary. In this work, the real permittivity results of Si based semi-conducting fillers in ten different 0–3 polymer composite systems were calculated by linear fitting of simplified EMA models, based on particularity of reported parameters in those composites. The results further confirmed the proposed interface induced polarization. The results further verified significant influences of filler polarity, polymer polarity and filler size on induced polarization and permittivity of composites as well. High self-consistency was gained between present modelling and prior measuring. This work might offer a facile and effective route to achieve the difficultly measured dielectric performances of discrete filler phase in some special polymer based composite systems.

Magnetic properties in an ash flow tuff with continuous grain size variation: a natural reference for magnetic particle granulometry

USGS Publications Warehouse

Till, J.L.; Jackson, M.J.; Rosenbaum, J.G.; Solheid, P.

2011-01-01

The Tiva Canyon Tuff contains dispersed nanoscale Fe-Ti-oxide grains with a narrow magnetic grain size distribution, making it an ideal material in which to identify and study grain-size-sensitive magnetic behavior in rocks. A detailed magnetic characterization was performed on samples from the basal 5 m of the tuff. The magnetic materials in this basal section consist primarily of (low-impurity) magnetite in the form of elongated submicron grains exsolved from volcanic glass. Magnetic properties studied include bulk magnetic susceptibility, frequency-dependent and temperature-dependent magnetic susceptibility, anhysteretic remanence acquisition, and hysteresis properties. The combined data constitute a distinct magnetic signature at each stratigraphic level in the section corresponding to different grain size distributions. The inferred magnetic domain state changes progressively upward from superparamagnetic grains near the base to particles with pseudo-single-domain or metastable single-domain characteristics near the top of the sampled section. Direct observations of magnetic grain size confirm that distinct transitions in room temperature magnetic susceptibility and remanence probably denote the limits of stable single-domain behavior in the section. These results provide a unique example of grain-size-dependent magnetic properties in noninteracting particle assemblages over three decades of grain size, including close approximations of ideal Stoner-Wohlfarth assemblages, and may be considered a useful reference for future rock magnetic studies involving grain-size-sensitive properties.

Characterization of SiC (SCS-6) Fiber Reinforced Reaction-Formed Silicon Carbide Matrix Composites

NASA Technical Reports Server (NTRS)

Singh, Mrityunjay; Dickerson, Robert M.

1995-01-01

Silicon carbide (SCS-6) fiber reinforced-reaction formed silicon carbide matrix composites were fabricated using NASA's reaction forming process. Silicon-2 at a percent of niobium alloy was used as an infiltrant instead of pure silicon to reduce the amount of free silicon in the matrix after reaction forming. The matrix primarily consists of silicon carbide with a bi-modal grain size distribution. Minority phases dispersed within the matrix are niobium disilicide (NbSi2), carbon and silicon. Fiber push-out tests on these composites determined a debond stress of approx. 67 MPa and a frictional stress of approx. 60 MPa. A typical four point flexural strength of the composite is 297 MPa (43.1 KSi). This composite shows tough behavior through fiber pull out.

Strengthening and Improving Yield Asymmetry of Magnesium Alloys by Second Phase Particle Refinement Under the Guidance of Integrated Computational Materials Engineering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Dongsheng; Lavender, Curt

2015-05-08

Improving yield strength and asymmetry is critical to expand applications of magnesium alloys in industry for higher fuel efficiency and lower CO 2 production. Grain refinement is an efficient method for strengthening low symmetry magnesium alloys, achievable by precipitate refinement. This study provides guidance on how precipitate engineering will improve mechanical properties through grain refinement. Precipitate refinement for improving yield strengths and asymmetry is simulated quantitatively by coupling a stochastic second phase grain refinement model and a modified polycrystalline crystal viscoplasticity φ-model. Using the stochastic second phase grain refinement model, grain size is quantitatively determined from the precipitate size andmore » volume fraction. Yield strengths, yield asymmetry, and deformation behavior are calculated from the modified φ-model. If the precipitate shape and size remain constant, grain size decreases with increasing precipitate volume fraction. If the precipitate volume fraction is kept constant, grain size decreases with decreasing precipitate size during precipitate refinement. Yield strengths increase and asymmetry approves to one with decreasing grain size, contributed by increasing precipitate volume fraction or decreasing precipitate size.« less

Size effect on the deformation mechanisms of nanocrystalline platinum thin films.

PubMed

Shu, Xinyu; Kong, Deli; Lu, Yan; Long, Haibo; Sun, Shiduo; Sha, Xuechao; Zhou, Hao; Chen, Yanhui; Mao, Shengcheng; Liu, Yinong

2017-10-16

This paper reports a study of time-resolved deformation process at the atomic scale of a nanocrystalline Pt thin film captured in situ under a transmission electron microscope. The main mechanism of plastic deformation was found to evolve from full dislocation activity-enabled plasticity in large grains (with grain size d > 10 nm), to partial dislocation plasticity in smaller grains (with grain size 10 nm < d < 6 nm), and grain boundary-mediated plasticity in the matrix with grain sizes d < 6 nm. The critical grain size for the transition from full dislocation activity to partial dislocation activity was estimated based on consideration of stacking fault energy. For grain boundary-mediated plasticity, the possible contributions to strain rate of grain creep, grain sliding and grain rotation to plastic deformation were estimated using established models. The contribution of grain creep is found to be negligible, the contribution of grain rotation is effective but limited in magnitude, and grain sliding is suggested to be the dominant deformation mechanism in nanocrystalline Pt thin films. This study provided the direct evidence of these deformation processes at the atomic scale.

Species distribution model transferability and model grain size - finer may not always be better.

PubMed

Manzoor, Syed Amir; Griffiths, Geoffrey; Lukac, Martin

2018-05-08

Species distribution models have been used to predict the distribution of invasive species for conservation planning. Understanding spatial transferability of niche predictions is critical to promote species-habitat conservation and forecasting areas vulnerable to invasion. Grain size of predictor variables is an important factor affecting the accuracy and transferability of species distribution models. Choice of grain size is often dependent on the type of predictor variables used and the selection of predictors sometimes rely on data availability. This study employed the MAXENT species distribution model to investigate the effect of the grain size on model transferability for an invasive plant species. We modelled the distribution of Rhododendron ponticum in Wales, U.K. and tested model performance and transferability by varying grain size (50 m, 300 m, and 1 km). MAXENT-based models are sensitive to grain size and selection of variables. We found that over-reliance on the commonly used bioclimatic variables may lead to less accurate models as it often compromises the finer grain size of biophysical variables which may be more important determinants of species distribution at small spatial scales. Model accuracy is likely to increase with decreasing grain size. However, successful model transferability may require optimization of model grain size.

Effects of MgO modified β-TCP nanoparticles on the microstructure and properties of β-TCP/Mg-Zn-Zr composites.

PubMed

Zheng, H R; Li, Z; You, C; Liu, D B; Chen, M F

2017-03-01

The mechanical properties and corrosion resistance of magnesium alloy composites were improved by the addition of MgO surface modified tricalcium phosphate ceramic nanoparticles (m-β-TCP). Mg-3Zn-0.8Zr composites with unmodified (MZZT) and modified (MZZMT) nanoparticles were produced by high shear mixing technology. Effects of MgO m-β-TCP nanoparticles on the microstructure, mechanical properties, electrochemical corrosion properties and cytocompatibility of Mg-Zn-Zr/β-TCP composites were investigated. After hot extrusion deformation and dynamic recrystallization, the grain size of MZZMT was the half size of MZZT and the distribution of m-β-TCP particles in the matrix was more uniform than β-TCP particles. The yield tensile strength (YTS), ultimate tensile strength (UTS), and corrosion potential (Ecorr) of MZZMT were higher than MZZT; the corrosion current density (I corr ) of MZZMT was lower than MZZT. Cell proliferation of co-cultured MZZMT and MZZT composite samples were roughly the same and the cell number at each time point is higher for MZZMT than for MZZT samples.

Electrochemical Synthesis of Core–Shell-Structured NbC–Fe Composite Powder for Enforcement in Low-Carbon Steel

PubMed Central

Song, Qiushi; Xu, Qian; Chen, Ying; Xu, Liang; Man, Tiannan

2017-01-01

An NbC–Fe composite powder was synthesized from an Nb2O5/Fe/C mixture by electrochemical reduction and subsequent carbonization in molten CaCl2–NaCl. The composite has a core–shell structure, in which NbC acts as the cores distributing in the Fe matrix. A strong bonding between NbC and Fe is benefit from the core–shell structure. The sintering and electrochemical reduction processes were investigated to probe the mechanism for the reactions. The results show that NbC particles about several nanometers were embraced by the Fe shell to form a composite about 100 nm in size. This featured structure can feasibly improve the wettability and sinterability of NbC as well as the uniform distribution of the carbide in the cast steel. By adding the composite into steel in the casting process, the grain size of the casted steel was markedly deceased from 1 mm to 500 μm on average, favoring the hardening of the casted steel. PMID:29104266

Production and Characterization of WC-Reinforced Co-Based Superalloy Matrix Composites

NASA Astrophysics Data System (ADS)

Özgün, Özgür; Dinler, İlyas

2018-05-01

Cobalt-based superalloy matrix composite materials were produced through the powder metallurgy technique using element powders at high purity and nano-sized wolfram carbide (WC) reinforcement in this study. An alloy that had the same chemical composition as the Stellite 6 alloy but not containing carbon was selected as the matrix alloy. The powder mixtures obtained as a result of mixing WC reinforcing member and element powders at the determined ratio were shaped by applying 300 MPa of pressure. The green components were sintered under argon atmosphere at 1240 °C for 120 minutes. The densities of the sintered components were determined by the Archimedes' principle. Microstructural characterization was performed via X-ray diffraction analysis, scanning electron microscope examinations, and energy-dispersive spectrometry. Hardness measurements and tensile tests were performed for determining mechanical characteristics. The relative density values of the sintered components increased by increasing the WC reinforcement ratio and they could almost reach the theoretical density. It was determined from the microstructural examinations that the composite materials consisted of fine and equiaxed grains and coarse carbides demonstrating a homogeneous dispersion along the microstructure at the grain boundaries. As it was the case in the density values, the hardness and strength values of the composites increased by increasing the WC ratio.

Production and Characterization of WC-Reinforced Co-Based Superalloy Matrix Composites

NASA Astrophysics Data System (ADS)

Özgün, Özgür; Dinler, İlyas

2018-07-01

Cobalt-based superalloy matrix composite materials were produced through the powder metallurgy technique using element powders at high purity and nano-sized wolfram carbide (WC) reinforcement in this study. An alloy that had the same chemical composition as the Stellite 6 alloy but not containing carbon was selected as the matrix alloy. The powder mixtures obtained as a result of mixing WC reinforcing member and element powders at the determined ratio were shaped by applying 300 MPa of pressure. The green components were sintered under argon atmosphere at 1240 °C for 120 minutes. The densities of the sintered components were determined by the Archimedes' principle. Microstructural characterization was performed via X-ray diffraction analysis, scanning electron microscope examinations, and energy-dispersive spectrometry. Hardness measurements and tensile tests were performed for determining mechanical characteristics. The relative density values of the sintered components increased by increasing the WC reinforcement ratio and they could almost reach the theoretical density. It was determined from the microstructural examinations that the composite materials consisted of fine and equiaxed grains and coarse carbides demonstrating a homogeneous dispersion along the microstructure at the grain boundaries. As it was the case in the density values, the hardness and strength values of the composites increased by increasing the WC ratio.

Fractionation of distillers dried grains with solubles (DDGS) by sieving and winnowing.

PubMed

Liu, KeShun

2009-12-01

Four commercial samples of distillers dried grains with solubles (DDGS) were sieved. All sieved fractions except for the pan fraction, constituting about 90% of original mass, were then winnowed with an air blast seed cleaner. Sieving was effective in producing fractions with varying composition. As the particle size decreased, protein and ash contents increased, and total carbohydrate (CHO) decreased. Winnowing sieved fractions was also effective in shifting composition, particularly for larger particle classes. Heavy sub-fractions were enriched in protein, oil and ash, while light sub-fractions were enriched for CHO. For protein, the combination of the two procedures resulted in a maximum 56.4% reduction in a fraction and maximum 60.2% increase in another fraction. As airflow velocity increased, light sub-fraction mass increased, while the compositional difference between the heavy and light sub-fractions decreased. Winnowing three times at a lower velocity was as effective as winnowing one time at a medium velocity. Winnowing the whole DDGS was much less effective than winnowing sieved fractions in changing composition, but sieving winnowed fractions was more effective than sieving whole DDGS. The two combination sequences gave comparable overall effects but sieving followed by winnowing is recommended because it requires less time. Regardless of combinational sequence, the second procedure was more effective in shifting composition than the first procedure.

Effect of freeze-thaw cycling on grain size of biochar.

PubMed

Liu, Zuolin; Dugan, Brandon; Masiello, Caroline A; Wahab, Leila M; Gonnermann, Helge M; Nittrouer, Jeffrey A

2018-01-01

Biochar may improve soil hydrology by altering soil porosity, density, hydraulic conductivity, and water-holding capacity. These properties are associated with the grain size distributions of both soil and biochar, and therefore may change as biochar weathers. Here we report how freeze-thaw (F-T) cycling impacts the grain size of pine, mesquite, miscanthus, and sewage waste biochars under two drainage conditions: undrained (all biochars) and a gravity-drained experiment (mesquite biochar only). In the undrained experiment plant biochars showed a decrease in median grain size and a change in grain-size distribution consistent with the flaking off of thin layers from the biochar surface. Biochar grain size distribution changed from unimodal to bimodal, with lower peaks and wider distributions. For plant biochars the median grain size decreased by up to 45.8% and the grain aspect ratio increased by up to 22.4% after 20 F-T cycles. F-T cycling did not change the grain size or aspect ratio of sewage waste biochar. We also observed changes in the skeletal density of biochars (maximum increase of 1.3%), envelope density (maximum decrease of 12.2%), and intraporosity (porosity inside particles, maximum increase of 3.2%). In the drained experiment, mesquite biochar exhibited a decrease of median grain size (up to 4.2%) and no change of aspect ratio after 10 F-T cycles. We also document a positive relationship between grain size decrease and initial water content, suggesting that, biochar properties that increase water content, like high intraporosity and pore connectivity large intrapores, and hydrophilicity, combined with undrained conditions and frequent F-T cycles may increase biochar breakdown. The observed changes in biochar particle size and shape can be expected to alter hydrologic properties, and thus may impact both plant growth and the hydrologic cycle.

Grain Size as a Control for Melt Focusing Beneath Mid-Ocean Ridges

NASA Astrophysics Data System (ADS)

Turner, A.; Katz, R. F.; Behn, M. D.

2015-12-01

Grain size is a fundamental control on both the rheology and permeability of the mantle. These properties, in turn, affect the transport of melt beneath mid-ocean ridges. Previous models of grain size beneath ridges have considered only the single-phase problem of dynamic recrystallisation and the resultant pattern of grain-size variation [1,2]. These models have not coupled the spatially variable grain-size field to two-phase (partially molten) mechanics to investigate the implications of spatially variable grain size on melt transport. Here, we present new results from numerical models that investigate the consequences of this coupling. In our two-dimensional, two-phase model the grain-size is coupled to both the permeability and rheology. The rheology is strain-rate and grain-size dependent. For simplicity, however, the grain-size field is not computed dynamically — rather, it is imposed from a single-phase, steady-state model [1] that is based on the "wattmeter" theory [3]. Our calculations predicts that a spatially variable grain size field can promote focusing of melt towards the ridge axis. This focusing is distinct from the commonly discussed, sub-lithospheric decompaction channel [4]. Furthermore, our model predicts that the shape of the partially molten region is sensitive to rheological parameters associated with grain size. The comparison of this shape with observations [5] may help to constrain the rheology of the upper mantle beneath mid-ocean ridges. References: [1] Turner et al., Geochem. Geophys. Geosyst., 16, 925-946, 2015. [2] Behn et al., EPSL, 282, 178-189, 2009. [3] Austin and Evans, Geology, 35:343-346, 2007. [4] Sparks and Parmentier, EPSL, 105, 368-377, 1991. [5] Key et al., Nature, 495, 499-502, 2013.

Effect of freeze-thaw cycling on grain size of biochar

PubMed Central

Dugan, Brandon; Masiello, Caroline A.; Wahab, Leila M.; Gonnermann, Helge M.; Nittrouer, Jeffrey A.

2018-01-01

Biochar may improve soil hydrology by altering soil porosity, density, hydraulic conductivity, and water-holding capacity. These properties are associated with the grain size distributions of both soil and biochar, and therefore may change as biochar weathers. Here we report how freeze-thaw (F-T) cycling impacts the grain size of pine, mesquite, miscanthus, and sewage waste biochars under two drainage conditions: undrained (all biochars) and a gravity-drained experiment (mesquite biochar only). In the undrained experiment plant biochars showed a decrease in median grain size and a change in grain-size distribution consistent with the flaking off of thin layers from the biochar surface. Biochar grain size distribution changed from unimodal to bimodal, with lower peaks and wider distributions. For plant biochars the median grain size decreased by up to 45.8% and the grain aspect ratio increased by up to 22.4% after 20 F-T cycles. F-T cycling did not change the grain size or aspect ratio of sewage waste biochar. We also observed changes in the skeletal density of biochars (maximum increase of 1.3%), envelope density (maximum decrease of 12.2%), and intraporosity (porosity inside particles, maximum increase of 3.2%). In the drained experiment, mesquite biochar exhibited a decrease of median grain size (up to 4.2%) and no change of aspect ratio after 10 F-T cycles. We also document a positive relationship between grain size decrease and initial water content, suggesting that, biochar properties that increase water content, like high intraporosity and pore connectivity large intrapores, and hydrophilicity, combined with undrained conditions and frequent F-T cycles may increase biochar breakdown. The observed changes in biochar particle size and shape can be expected to alter hydrologic properties, and thus may impact both plant growth and the hydrologic cycle. PMID:29329343

The relevance of grain dissection for grain size reduction in polar ice: insights from numerical models and ice core microstructure analysis

NASA Astrophysics Data System (ADS)

Steinbach, Florian; Kuiper, Ernst-Jan N.; Eichler, Jan; Bons, Paul D.; Drury, Martyn R.; Griera, Albert; Pennock, Gill M.; Weikusat, Ilka

2017-09-01

The flow of ice depends on the properties of the aggregate of individual ice crystals, such as grain size or lattice orientation distributions. Therefore, an understanding of the processes controlling ice micro-dynamics is needed to ultimately develop a physically based macroscopic ice flow law. We investigated the relevance of the process of grain dissection as a grain-size-modifying process in natural ice. For that purpose, we performed numerical multi-process microstructure modelling and analysed microstructure and crystallographic orientation maps from natural deep ice-core samples from the North Greenland Eemian Ice Drilling (NEEM) project. Full crystallographic orientations measured by electron backscatter diffraction (EBSD) have been used together with c-axis orientations using an optical technique (Fabric Analyser). Grain dissection is a feature of strain-induced grain boundary migration. During grain dissection, grain boundaries bulge into a neighbouring grain in an area of high dislocation energy and merge with the opposite grain boundary. This splits the high dislocation-energy grain into two parts, effectively decreasing the local grain size. Currently, grain size reduction in ice is thought to be achieved by either the progressive transformation from dislocation walls into new high-angle grain boundaries, called subgrain rotation or polygonisation, or bulging nucleation that is assisted by subgrain rotation. Both our time-resolved numerical modelling and NEEM ice core samples show that grain dissection is a common mechanism during ice deformation and can provide an efficient process to reduce grain sizes and counter-act dynamic grain-growth in addition to polygonisation or bulging nucleation. Thus, our results show that solely strain-induced boundary migration, in absence of subgrain rotation, can reduce grain sizes in polar ice, in particular if strain energy gradients are high. We describe the microstructural characteristics that can be used to identify grain dissection in natural microstructures.

Processing - microstructure relationships of chemically vapor deposited zirconia fiber coating for environmentally durable silicon carbide/silicon carbide composites

NASA Astrophysics Data System (ADS)

Lee, Jinil

In SiC/SiC ceramic matrix composites, toughness is obtained by adding a fiber coating which provides a weak interface for crack deflection and debonding between the fiber and the matrix. However, the most commonly used fiber coatings, carbon and boron nitride, are unstable in oxidative environments. In the present study, the feasibility of using a chemically vapor deposited zirconia (CVD-ZrO 2) fiber coating as an oxidation-resistant interphase for SiC/SiC composites was investigated. The feasibility of the CVD-ZrO2 coating as a useful interphase for SiC/SiC composites was investigated with emphasis on developing critical processing-microstructure relationships. A study of morphological evolution in the CVD-ZrO2 coating suggested that a size-controlled displacive phase transformation from tetragonal ZrO2 (t-ZrO2) to monoclinic ZrO2 (m-ZrO2) was the key mechanism responsible for the weak interface behavior exhibited by the ZrO2 coating. The pre-delamination occurred as a result of (i) continuous formation of t-ZrO2 nuclei on the deposition surface; (ii) martensitic transformation of the tetragonal phase to a monoclinic phase upon reaching a critical grain size; and (iii) development of significant compressive hoop stresses due to the volume dilation associated with the transformation. We also discovered that low oxygen partial pressure in the CVD reactor was required for the nucleation of t-ZrO2 and was ultimately responsible for the delamination behavior. The effects of oxygen partial pressure on the nucleation behavior of the CVD-ZrO2 coating was systematically studied by intentionally adding the controlled amount of O2 into the CVD chamber. Characterization results suggested that the number density of t-ZrO2 nuclei apparently decreased with increasing the oxygen partial pressure from 0.004 to 1.6 Pa. Also, the coating layer became more columnar and contained larger m-ZrO2 grains. The observed relationships between the oxygen partial pressure and the morphological characteristics of the ZrO 2 coating were explained in the context of the grain size and oxygen deficiency effects which have been previously reported to cause the stabilization of the t-ZrO2 phase in bulk ZrO2 specimens.

Dependence of diffusive radiative transfer on grain-size, temperature, and Fe-content: Implications for mantle processes

NASA Astrophysics Data System (ADS)

Hofmeister, A. M.

2005-08-01

Locally diffusive, radiative heat transport inside the earth is represented by an effective thermal conductivity ( krad,dif), calculated from spectra. Previous geophysical models assumed that emissivity ( ξ) equals unity, which violates local radiative equilibrium in an internally heated, grainy medium. Our new formulation accounts for ξ depending on frequency, physical scattering depending on grain-size ( d), and for light lost through back-reflections at interfaces. Mantle values of krad,dif are estimated from recent visible spectra of olivine combined with new IR data. The following trends hold for krad,dif calculated from olivine spectra, and should be equally valid for pyroxene and spinel: (1) pressure is unimportant, (2) radiative thermal conductivity depends non-linearly on d, temperature ( T), and Fe 2+ content ( X), (3) maxima occur in krad,dif( d) when the grains are large enough to emit substantially, but not so large that light is strongly attenuated within a single-grain, (4) the dependence of krad,dif on Fe 2+ content parallels that with d because absorption is controlled by the product dX (Beer's law), and (5) a local minimum occurs in krad,dif near 2000 K for d > 2 mm because at that temperature the peak position of the blackbody curve coincides with that of the strongly absorbing Fe 2+ peak in the visible. Larger krad,dif exists at lower and higher temperatures because mean free paths are long in the transmitting near-IR and UV spectral regions. As integration smooths over spectral details, the above representation based on olivine becomes increasingly accurate for other phases as grain-size decreases. For conditions expected in the transition zone, ∂ krad,dif/∂ T is negative, which is destabilizing [Dubuffet, F., Yuen, D.A., Rainey, E.S.G., 2002. Controlling thermal chaos in the mantle by positive feedback from radiative thermal conductivity. Nonlinear Proc. Geophys. 9, 1-13]. In the lower mantle, photon transport dominates phonon, promoting stable, weak convection. That radiative transfer is linked to chemical composition and grain-size suggests that this process impacts planetary evolution through the non-linear feedback with rheology.

Straight from the source's mouth; a quantitative study of grain-size export for an entire active rift, the Corinth Rift, central Greece

NASA Astrophysics Data System (ADS)

Watkins, Stephen E.; Whittaker, Alexander C.; Bell, Rebecca E.; Brooke, Sam A. S.; McNeill, Lisa C.; Gawthorpe, Robert L.

2017-04-01

The volumes, grain sizes and characteristics of sediment supplied from source catchments fundamentally controls basin stratigraphy. However, to date, few studies have constrained sediment budgets, including grain size, released into an active rift basin at a regional scale. The Gulf of Corinth, central Greece, is one of the most rapidly extending rifts in the world, with geodetic measurements of 5 mm/yr in the East to 15 mm/yr in the West. It has well-constrained climatic and tectonic boundary conditions and bedrock lithologies are well-characterised. It is therefore an ideal natural laboratory to study the grain-size export for a rift. In the field, we visited the river mouths of 49 catchments draining into the Corinth Gulf, which in total drain 83% of the rift. At each site, hydraulic geometries, surface grain-size of channel bars and full-weighted grain-size distributions of river sediment were obtained. The surface grain-size was measured using the Wolman point count method and the full-weighted grain-size distribution of the bedload by in-situ sieving. In total, approximately 17,000 point counts and 3 tonnes of sediment were processed. The grain-size distributions show an overall increase from East to West on the southern coast of the gulf, with largest grain-sizes exported from the Western rift catchments. D84 ranges from 20 to 110 mm, however 50% of D84 grain-sizes are less than 40 mm. Subsequently, we derived the full Holocene sediment budget for the Corinth Gulf by combining our grain size data with catchment sediment fluxes, constrained using the BQART model and calibrated to known Holocene sediment volumes in the basin from seismic data (c.f. Watkins et al., in review). This is the first time such a budget has been derived for the Corinth Rift. Finally, our estimates of sediment budgets and grain sizes were compared to regional uplift constraints, fault distributions, slip rates and lithology to identify the relative importance of these controls on sediment supply to the basin.

Microstructural indicators of convection: insights from the Little Minch Sill Complex, Scotland

NASA Astrophysics Data System (ADS)

Nicoli, Gautier; Holness, Marian; Neufeld, Jerome; Farr, Robert

2017-04-01

The fluid dynamic behaviour of crystal-bearing magmas is a key parameter to understand the formation of magmatic bodies. There are two opposite views on the subject: Some argue that solidification in intrusive bodies is affected by convection whereas others claim solidification happens in a static environment. A consensus on the question may be reached by carefully studying the grain size distribution in the settled accumulations of cargo crystals. In the absence of significant crystal growth or particle coarsening by agglomeration, settling of a polydisperse crystal load will always result in a fining-upwards sequence in static magmas as well as in convecting environments. If we assume the particle concentration is always sufficiently low to prevent hindered settling, gravitational settling in a static magma leads to the settling of individual crystals at a constant rate determined by their Stokes' velocity. Each size class is deposited at a constant rate, until all the grains of that size class have fallen out of suspension, leading to a well-stratified sequence and the complete disappearance of progressively smaller size classes upwards in the accumulation. In contrast, in a vigorously convecting magma crystals settle when they enter the stagnant basal boundary layer. In a system containing a polydisperse crystal population most of the bigger particles are removed rapidly from the bulk magma, leading to the creation of a fining-upwards sequence on the floor. However, in detail the structure of this fining-upwards sequence is critically different from that created by settling from a stagnant magma, with the gradual phasing out of each size class instead of the abrupt termination of size classes seen in static systems. This provides us with the opportunity to distinguish between settling from static or convecting magma using the spatial variation of grain size in settled accumulations. We focus on the Little Minch Sill Complex in Scotland, which formed from olivine-phyric magma and is characterised by both composite and single-injection bodies with significant accumulation of olivine on their lower margins. Comparison of the fining-upwards sequences in the picrodolerite/crinanite unit of the composite Shiant Isles Main Sill,and related single-injection sills on the Trotternish Peninsula, Skye, illustrate the ability of this method to distinguish between convecting and non-convecting magma bodies.

Strengthening and toughening mechanisms in low-c microalloyed martensitic steel as influenced by austenite conditioning

NASA Astrophysics Data System (ADS)

Kennett, Shane C.

Three low-carbon ASTM A514 microalloyed steels were used to assess the effects of austenite conditioning on the microstructure and mechanical properties of martensite. A range of prior austenite grain sizes with and without thermomechanical processing were produced in a Gleeble RTM 3500 and direct-quenched. Samples in the as-quenched, low temperature tempered, and high temperature tempered conditions were studied. The microstructure was characterized with scanning electron microscopy, electron backscattered diffraction, transmission electron microscopy, and x-ray diffraction. The uniaxial tensile properties and Charpy V-notch properties were measured and compared with the microstructural features (prior austenite grain size, packet size, block size, lath boundaries, and dislocation density). For the equiaxed prior austenite grain conditions, prior austenite grain size refinement decreases the packet size, decreases the block size, and increases the dislocation density of as-quenched martensite. However, after high temperature tempering the dislocation density decreases with prior austenite grain size refinement. Thermomechanical processing increases the low angle substructure, increases the dislocation density, and decreases the block size of as-quenched martensite. The dislocation density increase and block size refinement is sensitive to the austenite grain size before ausforming. The larger prior austenite grain size conditions have a larger increase in dislocation density, but the small prior austenite grain size conditions have the largest refinement in block size. Additionally, for the large prior austenite grain size conditions, the packet size increases with thermomechanical processing. The strength of martensite is often related to an effective grain size or carbon concentration. For the current work, it was concluded that the strength of martensite is primarily controlled by the dislocation density and dislocation substructure; which is related to a grain size and carbon concentration. In the microyielding regime, the strength and work hardening is related to the motion of unpinned dislocation segments. However, with tensile strain, a dislocation cell structure is developed and the flow strength (greater than 1% offset) is controlled by the dislocation density following a Taylor hardening model, thereby ruling out any grain size effects on the flow strength. Additionally, it is proposed that lath boundaries contribute to strength. It is shown that the strength differences associated with thermomechanically processed steels can be fully accounted for by dislocation density differences and the effect of lath boundaries. The low temperature ductile to brittle transition of martensite is controlled by the martensite block size, packet size, and prior austenite grain size. However, the effect of block size is likely small in comparison. The ductile to brittle transition temperature is best correlated to the inverse square root of the martensite packet size because large crack deflections are typical at packet boundaries.