Surface Characteristics and Catalytic Activity of Copper Deposited Porous Silicon Powder

PubMed Central

Abdul Halim, Muhammad Yusri; Tan, Wei Leng; Abu Bakar, Noor Hana Hanif; Abu Bakar, Mohamad

2014-01-01

Porous structured silicon or porous silicon (PS) powder was prepared by chemical etching of silicon powder in an etchant solution of HF: HNO3: H2O (1:3:5 v/v). An immersion time of 4 min was sufficient for depositing Cu metal from an aqueous solution of CuSO4 in the presence of HF. Scanning electron microscopy (SEM) analysis revealed that the Cu particles aggregated upon an increase in metal content from 3.3 wt% to 9.8 wt%. H2-temperature programmed reduction (H2-TPR) profiles reveal that re-oxidation of the Cu particles occurs after deposition. Furthermore, the profiles denote the existence of various sizes of Cu metal on the PS. The Cu-PS powders show excellent catalytic reduction on the p-nitrophenol regardless of the Cu loadings. PMID:28788272

Synthesis of octahedral like Cu-BTC derivatives derived from MOF calcined under different atmosphere for application in CO oxidation

NASA Astrophysics Data System (ADS)

Yang, Yiqiong; Dong, Han; Wang, Yin; He, Chi; Wang, Yuxin; Zhang, Xiaodong

2018-02-01

A series of octahedral structure Cu-BTC derivatives were successfully achieved through direct calcination of copper based metal organic framework Cu-BTC under different atmosphere (CO reaction gas, oxidizing gas O2, reducing gas H2, inert gas Ar). The Cu-BTC derivatives were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), laser Raman spectroscopy (LRS), N2 adsorption-desorption isotherm, element analysis, H2-temperature program reduction (H2-TPR) and X-ray photoelectron spectroscopic (XPS). It is found that Cu-BTC derivative derived from MOF calcined under reaction gas/O2 (Cu-BTC-CO/Cu-BTC-O) only retain Cu2O and CuO species. In addition, a weak Cu-BTC structure and Cu particles were observed on Cu-BTC derivative derived from MOF calcined under H2 (Cu-BTC-H). Obviously differently, Cu-BTC derivative derived from MOF calcined under Ar (Cu-BTC-Ar) still retains good MOF structure. The catalytic performance for CO oxidation over Cu-BTC derivatives was studied. It was found that Cu-BTC-CO showed a smaller specific surface area (8.0 m2/g), but presented an excellent catalytic performance, long-term stability and cycling stability with a complete CO conversion temperature (T100) of 140 °C, which was ascribed to the higher Cu2O/CuO ratio, good low temperature reduction behavior and a high quantity of surface active oxygen species.

Reduction of metal oxides through mechanochemical processing

DOEpatents

Froes, Francis H.; Eranezhuth, Baburaj G.; Senkov, Oleg N.

2000-01-01

The low temperature reduction of a metal oxide using mechanochemical processing techniques. The reduction reactions are induced mechanically by milling the reactants. In one embodiment of the invention, titanium oxide TiO.sub.2 is milled with CaH.sub.2 to produce TiH.sub.2. Low temperature heat treating, in the range of 400.degree. C. to 700.degree. C., can be used to remove the hydrogen in the titanium hydride.

Synthesis and Hydrodeoxygenation Properties of Ruthenium Phosphide Catalysts

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bowker, Richard H.; Smith, Mica C.; Pease, Melissa

2011-07-01

Ru2P/SiO2 and RuP/SiO2 catalysts were prepared by the temperature-programmed reduction (TPR) of uncalcined precursors containing hypophosphite ion (H2PO2-) as the phosphorus source. The Ru2P/SiO2 and RuP/SiO2 catalysts had small average particle sizes (~4 nm) and high CO chemisorption capacities (90-110 umol/g). The Ru phosphide catalysts exhibited similar or higher furan (C4H4O) hydrodeoxygenation (HDO) activities than did a Ru/SiO2 catalyst, and the phosphide catalysts favored C4 hydrocarbon products while the Ru metal catalyst produced primarily C3 hydrocarbons.

Large Reduction of Hot Spot Temperature in Graphene Electronic Devices with Heat-Spreading Hexagonal Boron Nitride.

PubMed

Choi, David; Poudel, Nirakar; Park, Saungeun; Akinwande, Deji; Cronin, Stephen B; Watanabe, Kenji; Taniguchi, Takashi; Yao, Zhen; Shi, Li

2018-04-04

Scanning thermal microscopy measurements reveal a significant thermal benefit of including a high thermal conductivity hexagonal boron nitride (h-BN) heat-spreading layer between graphene and either a SiO 2 /Si substrate or a 100 μm thick Corning flexible Willow glass (WG) substrate. At the same power density, an 80 nm thick h-BN layer on the silicon substrate can yield a factor of 2.2 reduction of the hot spot temperature, whereas a 35 nm thick h-BN layer on the WG substrate is sufficient to obtain a factor of 4.1 reduction. The larger effect of the h-BN heat spreader on WG than on SiO 2 /Si is attributed to a smaller effective heat transfer coefficient per unit area for three-dimensional heat conduction into the thick, low-thermal conductivity WG substrate than for one-dimensional heat conduction through the thin oxide layer on silicon. Consequently, the h-BN lateral heat-spreading length is much larger on WG than on SiO 2 /Si, resulting in a larger degree of temperature reduction.

Effect of pH, temperature, humic acid and coexisting anions on reduction of Cr(Ⅵ) in the soil leachate by nZVI/Ni bimetal material.

PubMed

Zhu, Fang; Li, Luwei; Ren, Wentao; Deng, Xiaoqiang; Liu, Tao

2017-08-01

Nano zero valent iron/Ni bimetal materials (nZVI/Ni) were prepared by borohydride reduction method to remediate toxic Cr(Ⅵ) contaminated in soil leachate. nZVI/Ni was characterized using scanning electron microscopy (SEM), X-ray diffraction (XRD) and X-ray Photoelectron Spectroscopy (XPS). Different factors including pH value of soil leachate, reaction time, temperature, humic acid and coexisting anions (SO 4 2- , NO 3 - , HCO 3 - , CO 3 2- ) were studied to analyze the reduction rate. Results showed that the reduction rate of Cr(Ⅵ) could reach 99.84% under the condition of pH of 5 and temperature of 303 K. pH values and temperature of soil leachate had a significant effect on the reduction efficiency, while humic acid had inhibition effect for the reduction reaction. SO 4 2- , HCO 3 - and CO 3 2- had inhibition effect for reduction rate, while NO 3 - barely influenced the reduction process of nZVI/Ni. Moreover, Langumir-Hinshelwood first order kinetic model was studied and could describe the reduction process well. The thermodynamic studies indicated that the reaction process was endothermic and spontaneous. Activation energy was 143.80 kJ mol -1 , showing that the reaction occurred easily. Therefore, the study provides an idea for nZVI/Ni further research and practical application of nZVI/Ni in soil remediation. Copyright © 2017 Elsevier Ltd. All rights reserved.

Laser Raman diagnostics in subsonic and supersonic turbulent jet diffusion flames

NASA Technical Reports Server (NTRS)

Cheng, T. S.; Wehrmeyer, J. A.; Pitz, R. W.

1991-01-01

Ultraviolet (UV) spontaneous vibrational Raman scattering combined with laser-induced predissociative fluorescence (LIPF) is developed for temperature and multi-species concentration measurements. Simultaneous measurements of temperature, major species (H2, O2, N2, H2O), and minor species (OH) concentrations are made with a 'single' narrow band KrF excimer laser in subsonic and supersonic lifted turbulent hydrogen-air diffusion flames. The UV Raman system is calibrated with a flat-flame diffusion burner operated at several known equivalence ratios from fuel-lean to fuel-rich. Temperature measurements made by the ratio of Stokes/anti-Stokes signal and by the ideal gas law are compared. The single shot measurement precision for concentration and temperature measurement is 5 to 10 pct. Calibration constants and bandwidth factors are determined from the flat burner measurements and used in a data reduction program to arrive at temperature and species concentration measurements. These simultaneous measurements of temperature and multi-species concentrations allow a better understanding of the complex turbulence-chemistry interactions and provide information for the input and validation of CFD models.

Rational design of template-free MnOx-CeO2 hollow nanotube as de-NOx catalyst at low temperature

NASA Astrophysics Data System (ADS)

Li, Chenlu; Tang, Xiaolong; Yi, Honghong; Wang, Lifeng; Cui, Xiaoxu; Chu, Chao; Li, Jingying; Zhang, Runcao; Yu, Qingjun

2018-01-01

MnOx-CeO2 hollow nanotube was synthesized for the low temperature selective catalytic reduction (SCR) of NOx with NH3. The nanotube was fabricated firstly through the interfacial oxidation-reduction reaction by dealing the Ce(OH)CO3 intermediate with KMnO4 aqueous solution, then followed by selective wash with HNO3. The catalysts were systematically examined by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, elemental mapping, X-ray photoelectron spectroscopy, NH3 temperature-programmed desorption measurements and catalytic activity test. It was found that the as-prepared MnOx-CeO2-B nanotube exhibited best NOx removal efficiency among the catalysts investigated, where 96% NOx conversion at 100 °C at a space velocity of 30000 h-1 was obtained. Meanwhile, superior resistance to H2O and SO2 was achieved as well as high thermal stability. On the basis of various analysis results, the remarkable de-NOx performance of the MnOx-CeO2-B nanobube could be attributed to the uniform distribution of active species, abundant content of Mn4+ and Oα species, and especially the hollow porous architectures provided huge specific surface area and sufficient acidic sites.

Composite material application for liquid rocket engines

NASA Technical Reports Server (NTRS)

Heubner, S. W.

1982-01-01

With increasing emphasis on improving engine thrust-to-weight ratios to provide improved payload capabilities, weight reductions achievable by the use of composites have become attractive. Of primary significance is the weight reduction offered by composites, although high temperature properties and cost reduction were also considered. The potential for application of composites to components of Earth-to-orbit hydrocarbon engines and orbit-to-orbit LOX/H2 engines was assessed. The components most likely to benefit from the application of composites were identified, as were the critical technology areas where developed would be required. Recommendations were made and a program outlined for the design, fabrication, and demonstration of specific engine components.

Inhaled hydrogen sulfide: a rapidly reversible inhibitor of cardiac and metabolic function in the mouse.

PubMed

Volpato, Gian Paolo; Searles, Robert; Yu, Binglan; Scherrer-Crosbie, Marielle; Bloch, Kenneth D; Ichinose, Fumito; Zapol, Warren M

2008-04-01

Breathing hydrogen sulfide (H2S) has been reported to induce a suspended animation-like state with hypothermia and a concomitant metabolic reduction in rodents. However, the impact of H2S breathing on cardiovascular function remains incompletely understood. In this study, the authors investigated the cardiovascular and metabolic effects of inhaled H2S in a murine model. The impact of breathing H2S on cardiovascular function was examined using telemetry and echocardiography in awake mice. The effects of breathing H2S on carbon dioxide production and oxygen consumption were measured at room temperature and in a warmed environment. Breathing H2S at 80 parts per million by volume at 27 degrees C ambient temperature for 6 h markedly reduced heart rate, core body temperature, respiratory rate, and physical activity, whereas blood pressure remained unchanged. Echocardiography demonstrated that H2S exposure decreased both heart rate and cardiac output but preserved stroke volume. Breathing H2S for 6 h at 35 degrees C ambient temperature (to prevent hypothermia) decreased heart rate, physical activity, respiratory rate, and cardiac output without altering stroke volume or body temperature. H2S breathing seems to induce bradycardia by depressing sinus node activity. Breathing H2S for 30 min decreased whole body oxygen consumption and carbon dioxide production at either 27 degrees or 35 degrees C ambient temperature. Both parameters returned to baseline levels within 10 min after the cessation of H2S breathing. Inhalation of H2S at either 27 degrees or 35 degrees C reversibly depresses cardiovascular function without changing blood pressure in mice. Breathing H2S also induces a rapidly reversible reduction of metabolic rate at either body temperature.

Inhaled Hydrogen Sulfide

PubMed Central

Volpato, Gian Paolo; Searles, Robert; Yu, Binglan; Scherrer-Crosbie, Marielle; Bloch, Kenneth D.; Ichinose, Fumito; Zapol, Warren M.

2010-01-01

Background Breathing hydrogen sulfide (H2S) has been reported to induce a suspended animation–like state with hypothermia and a concomitant metabolic reduction in rodents. However, the impact of H2S breathing on cardiovascular function remains incompletely understood. In this study, the authors investigated the cardiovascular and metabolic effects of inhaled H2S in a murine model. Methods The impact of breathing H2S on cardiovascular function was examined using telemetry and echocardiography in awake mice. The effects of breathing H2S on carbon dioxide production and oxygen consumption were measured at room temperature and in a warmed environment. Results Breathing H2S at 80 parts per million by volume at 27°C ambient temperature for 6 h markedly reduced heart rate, core body temperature, respiratory rate, and physical activity, whereas blood pressure remained unchanged. Echocardiography demonstrated that H2S exposure decreased both heart rate and cardiac output but preserved stroke volume. Breathing H2S for 6 h at 35°C ambient temperature (to prevent hypothermia) decreased heart rate, physical activity, respiratory rate, and cardiac output without altering stroke volume or body temperature. H2S breathing seems to induce bradycardia by depressing sinus node activity. Breathing H2S for 30 min decreased whole body oxygen consumption and carbon dioxide production at either 27° or 35°C ambient temperature. Both parameters returned to baseline levels within 10 min after the cessation of H2S breathing. Conclusions Inhalation of H2S at either 27° or 35°C reversibly depresses cardiovascular function without changing blood pressure in mice. Breathing H2S also induces a rapidly reversible reduction of metabolic rate at either body temperature. PMID:18362598

Hydrodeoxygenation of Guaiacol over Ceria-Zirconia Catalysts.

PubMed

Schimming, Sarah M; LaMont, Onaje D; König, Michael; Rogers, Allyson K; D'Amico, Andrew D; Yung, Matthew M; Sievers, Carsten

2015-06-22

The hydrodeoxygenation of guaiacol is investigated over bulk ceria and ceria-zirconia catalysts with different elemental compositions. The reactions are performed in a flow reactor at 1 atm and 275-400 °C. The primary products are phenol and catechol, whereas cresol and benzene are formed as secondary products. No products with hydrogenated rings are formed. The highest conversion of guaiacol is achieved over a catalyst containing 60 mol % CeO2 and 40 mol % ZrO2 . Pseudo-first-order activation energies of 97-114 kJ mol(-1) are observed over the mixed metal oxide catalysts. None of the catalysts show significant deactivation during 72 h on stream. The important physicochemical properties of the catalysts are characterized by X-ray diffraction (XRD), temperature-programmed reduction, titration of oxygen vacancies, and temperature-programmed desorption of ammonia. On the basis of these experimental results, the reasons for the observed reactivity trends are identified. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Modified Ni-Cu catalysts for ethanol steam reforming

NASA Astrophysics Data System (ADS)

Dan, M.; Mihet, M.; Almasan, V.; Borodi, G.; Katona, G.; Muresan, L.; Lazar, M. D.

2013-11-01

Three Ni-Cu catalysts, having different Cu content, supported on γ-alumina were synthesized by wet co-impregnation method, characterized and tested in the ethanol steam reforming (ESR) reaction. The catalysts were characterized for determination of: total surface area and porosity (N2 adsorption - desorption using BET and Dollimer Heal methods), Ni surface area (hydrogen chemisorption), crystallinity and Ni crystallites size (X-Ray Diffraction), type of catalytic active centers (Hydrogen Temperature Programmed Reduction). Total surface area and Ni crystallites size are not significantly influenced by the addition of Cu, while Ni surface area is drastically diminished by increasing of Cu concentration. Steam reforming experiments were performed at atmospheric pressure, temperature range 150-350°C, and ethanol - water molar ration of 1 at 30, using Ar as carrier gas. Ethanol conversion and hydrogen production increase by the addition of Cu. At 350°C there is a direct connection between hydrogen production and Cu concentration. Catalysts deactivation in 24h time on stream was studied by Transmission Electron Microscopy (TEM) and temperature-programmed reduction (TPR) on used catalysts. Coke deposition was observed at all studied temperatures; at 150°C amorphous carbon was evidenced, while at 350°C crystalline, filamentous carbon is formed.

Drastic reduction of adsorption of CO and H2 on (111)-type Pd layers

NASA Technical Reports Server (NTRS)

Poppa, H.; Soria, F.

1983-01-01

Clean surfaces of (111)-type Pd layers, grown from the vapor phase on Mo(110) at room temperature, were used to study the adsorption of CO and H2 by temperature-programmed desorption, Auger electron spectroscopy, and low-energy electron diffraction. Mild annealing of the as-grown layers during a single desorption cycle (to about 600 K) drastically reduces the adsorption for both adsorbates. Low-dose argon-ion bombardment introduces surface imperfections which restore a high adsorption probability. The results are interpreted in terms of particular (111)-type surface structures that persist tp layer thicknesses of about four monolayers; the results raise questions with respect to the surface structure of supported thin epitaxial islands and particles of Pd and possibly also with respect to conventional methods of preparing bulk surfaces of Pd for adsorption studies.

Experimental characterization of enhanced SNCR process with carbonaceous gas additives.

PubMed

Yao, Ting; Duan, Yufeng; Yang, Zhizhong; Li, Yuan; Wang, Linwei; Zhu, Chun; Zhou, Qiang; Zhang, Jun; She, Min; Liu, Meng

2017-06-01

Carbonaceous gases such as CO and alkanes are commonly used as additives to enhance the selective non-catalytic reduction (SNCR) performance due to their high reducibility. This study compared the effect of CO and CH 4 on NO reduction in a tubular reactor with simulated flue gas. The enhancement of C 3 H 8 on SNCR process was tested at extremely low temperature, i.e. 650 °C. Experimental results suggested that reactions between NH 3 and SO 2 were favored at low temperatures and the competition for NH 3 between SO 2 and NO was influenced by gas additives. A maximum downward shift of 25 °C and 100 °C in temperature window for 50% NO reduction efficiency was obtained with the addition of CO and CH 4 , respectively. Considerable CO emission was observed with addition of CH 4 . The addition of CH 4 contributed to the formation of a self-accelerating reaction route within NO/O 2 /NH 3 SNCR reaction system. NO 2 produced from NO accelerates the oxidation of CH 4 to CO, while the oxidation of CH 4 returns to enhance the NO reduction globally. Optimal NO reduction of 44% was achieved with addition of C 3 H 8 at 650 °C. Substantial portion of C 3 H 8 was partially oxidized to CO and the remaining was converted into C 2 H 4 and C 3 H 6 during the SNCR process. Oxidative dehydrogenation of C 3 H 8 was involved. High reactivity of C 3 H 6 and C 2 H 4 favored the further oxidation and cracking to produce CO. These differences in oxidation behavior significantly influence the promotion capacities of CO, CH 4 and C 3 H 8 for NO reduction. Copyright © 2017 Elsevier Ltd. All rights reserved.

Efficient generation of H2 by splitting water with an isothermal redox cycle.

PubMed

Muhich, Christopher L; Evanko, Brian W; Weston, Kayla C; Lichty, Paul; Liang, Xinhua; Martinek, Janna; Musgrave, Charles B; Weimer, Alan W

2013-08-02

Solar thermal water-splitting (STWS) cycles have long been recognized as a desirable means of generating hydrogen gas (H2) from water and sunlight. Two-step, metal oxide-based STWS cycles generate H2 by sequential high-temperature reduction and water reoxidation of a metal oxide. The temperature swings between reduction and oxidation steps long thought necessary for STWS have stifled STWS's overall efficiency because of thermal and time losses that occur during the frequent heating and cooling of the metal oxide. We show that these temperature swings are unnecessary and that isothermal water splitting (ITWS) at 1350°C using the "hercynite cycle" exhibits H2 production capacity >3 and >12 times that of hercynite and ceria, respectively, per mass of active material when reduced at 1350°C and reoxidized at 1000°C.

Template-Mediated Ni(II) Dispersion in Mesoporous SiO2 for Preparation of Highly Dispersed Ni Catalysts: Influence of Template Type.

PubMed

Ning, Xin; Lu, Yiyuan; Fu, Heyun; Wan, Haiqin; Xu, Zhaoyi; Zheng, Shourong

2017-06-07

Supported Ni catalysts on three mesoporous SiO 2 supports (i.e., SBA-15, MCM-41, and HMS) were prepared using a solid-state reaction between Ni(NO 3 ) 2 and organic template-occluded mesoporous SiO 2 . For comparison, supported Ni catalysts on mesoporous SiO 2 synthesized by the conventional impregnation method were also included. The catalysts were characterized by scanning electron microscopy, X-ray diffraction, UV-vis diffuse reflectance spectroscopy, N 2 adsorption, X-ray photoelectron spectroscopy, H 2 temperature-programmed reduction, transmission electron microscopy, and transmission electron microscopy-energy-dispersive X-ray. The catalytic properties of the catalysts were evaluated using gas-phase catalytic hydrodechlorination of 1,2-dichloroethane. The results showed that upon grinding Ni(NO 3 ) 2 with template-occluded mesoporous SiO 2 , strong coordination between Ni 2+ and dodecylamine was identified in the Ni(NO 3 ) 2 -HMS system. Additionally, the results of H 2 temperature-programmed reduction revealed that NiO in calcined NiO/HMS was reduced at higher temperature than those in calcined NiO/SBA-15 and NiO/MCM-41, reflecting the presence of a strong interaction between NiO and mesoporous SiO 2 in NiO/HMS. Consistently, the average particle sizes of metallic Ni were found to be 2.7, 3.4, and 9.6 nm in H 2 -reduced Ni/HMS, Ni/SBA-15, and Ni/MCM-41, respectively, indicative of a much higher Ni dispersion in Ni/HMS. For the catalytic hydrodechlorination of 1,2-dichloroethane, Ni/MCM-41 synthesized by the solid-state reaction method exhibited a catalytic activity similar to that prepared by the impregnation method, while higher catalytic activities were observed on Ni/HMS and Ni/SBA-15 than on their counterparts prepared by the impregnation method. Furthermore, a higher conversion was identified on Ni/HMS than on Ni/SBA-15 and Ni/MCM-41, highlighting the importance of template type for the preparation of highly dispersed metal catalysts on mesoporous SiO 2 .

Sulfation of K-based Lean NOx Trap while Cycling Between Lean and Rich Conditions: I. Microreactor Study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Toops, Todd J; Pihl, Josh A

2008-01-01

Exposure of Pt/K/Al{sub 2}O{sub 3} to 15 ppm SO{sub 2} reduces the NOx activity at 200, 300, and 400 C at significantly different rates--1.5, 8.5, and 18.0 {micro}mol NOx/(h g{sub cat}), respectively. During the initial sulfation, NOx conversion is directly linked to lean phase storage capacity, and sulfation does not impact the reduction kinetics since the amount of unconverted NOx was constant or decreased with increasing sulfation time. A portion of sulfur stored at 200 C desorbs upon mild heating to 400 C while cycling between lean and rich conditions. This apparently is a result of sulfur being released frommore » Al{sub 2}O{sub 3}; however, performance is not significantly recovered as much of the sulfur is re-adsorbed on the K-phase. This is apparent from analysis of the NOx storage and release profiles. Additional analysis of these profiles suggests that SO{sub 2} initially adsorbs near Pt before interacting with other sites further away from Pt at 300 C. At 400 C, it appears that SO{sub 2} either preferentially adsorbs near Pt and then quickly diffuses along the surface to other less proximal sites, or it directly adsorbs on sites further away from Pt. De-sulfurization up to 800 C using a temperature programmed reduction (TPR) procedure and rich conditions with both CO{sub 2} and H{sub 2}O restored 73=94% of the LNT performance at 300 and 400 C. However, the recovered performance measured at 200 C was only 34-49% of the original NOx reduction activity. H{sub 2}S and SO{sub 2} were the primary de-sulfurization products with H{sub 2}S having a maximum release between 690 and 755 C, while SO{sub 2} had a peak release between 770 and 785 C. The sulfation temperature does not have a significant impact on the recovered performance, the de-sulfurization products or the sulfur release temperature.« less

Optimization of heat and relative humidity conditions to reduce Escherichia coli O157:H7 contamination and maximize the germination of radish seeds.

PubMed

Song, M K; Kim, H W; Rhee, M S

2016-06-01

We previously reported that a combination of heat and relative humidity (RH) had a marked bactericidal effect on Escherichia coli O157:H7 on radish seeds. Here, response surface methodology with a Box-Behnken design was used to build a model to predict reductions in E. coli O157:H7 populations based on three independent variables: heating temperature (55 °C, 60 °C, or 65 °C), RH (40%, 60%, and 80%), and holding time (8, 15, or 22 h). Optimum treatment conditions were selected using a desirability function. The predictive model for microbial reduction had a high regression coefficient (R(2) = 0.97), and the accuracy of the model was verified using validation data (R(2) = 0.95). Among the three variables examined, heating temperature (P < 0.0001) and RH (P = 0.004) were the most significant in terms of bacterial reduction and seed germination, respectively. The optimum conditions for microbial reduction (6.6 log reduction) determined by ridge analysis were as follows: 64.5 °C and 63.2% RH for 17.7 h. However, when both microbial reduction and germination rate were taken into consideration, the desirability function yielded optimal conditions of 65 °C and 40% RH for 8 h (6.6 log reduction in the bacterial population; 94.4% of seeds germinated). This study provides comprehensive data that improve our understanding of the effects of heating temperature, RH, and holding time on the E. coli O157:H7 population on radish seeds. Radish seeds can be exposed to these conditions before sprouting, which greatly increases the microbiological safety of the products. Copyright © 2015 Elsevier Ltd. All rights reserved.

Role of CeO2 promoter in NiO/α-Al2O3 catalyst for dry reforming of methane

NASA Astrophysics Data System (ADS)

Loc, Luu Cam; Phuong, Phan Hong; Tri, Nguyen

2017-09-01

A series of Ni/α-Al2O3 (NiAl) catalysts promoted by CeO2 was prepared by co-impregnation methods with content of (NiO+CeO2) being in the range of 10-30 wt%. The NiO:CeO2 weight ratio was fluctuated at 1:1, 1:2 and 1:3. Several techniques, including X-ray powder diffraction (XRD), Hydrogen temperature-programmed reduction (H2-TPR), and transmission electron microscopy (TEM) were used to investigate catalysts' physico-chemical properties. The activity of these catalysts in dry reforming of CH4 was investigated at temperature range of 550-800 °C. The results revealed that the most suitable CeO2 promoted Ni catalyst contained 20 wt% of (NiO+CeO2) and NiO:CeO2 weight ratio of 1:2. The best catalytic performance of catalyst [20(1Ni2Ce)Al] due to a better reducibility resulted in a higher amount of free small particle NiO. At 700 °C and CH4:CO2 molar ratio of 1:1, the conversion of CH4 and CO2 on the most suitable CeO2 promoted Ni catalyst reached 86% and 67%, respectively; H2 and CO selectivity of 90% and H2:CO molar ratio of 1.15 were obtained. Being similar to MgO [1], promoter CeO2 could improve catalytic activity of Ni/α-Al2O3 catalyst at a lower range of temperature. Besides, both MgO and CeO2 had a great impact on improving coke resistance of Ni catalysts. At higher temperature, the role of CeO2 as well as MgO in preventing coke formation on catalyst was clarified by temperature-programmed oxidation (TPO) technique. Coke amount formed after 30-h TOS on 20(1Ni2Ce) catalyst was found to be 22.18 mgC/gcat, being less than on non-promoted catalyst (36.75 mgC/gcat), but more than on 20(1Ni2Mg)Al one (5.25 mgC/gcat).

Chemistry, isotopic composition, and origin of a methane-hydrogen sulfide hydrate at the Cascadia subduction zone

USGS Publications Warehouse

Kastner, M.; Kvenvolden, K.A.; Lorenson, T.D.

1998-01-01

Although the presence of extensive gas hydrate on the Cascadia margin, offshore from the western U.S. and Canada, has been inferred from marine seismic records and pore water chemistry, solid gas hydrate has only been found at one location. At Ocean Drilling Program (ODP) Site 892, offshore from central Oregon, gas hydrate was recovered close to the sediment - water interface at 2-19 m below the seafloor, (mbsf) at 670 m water depth. The gas hydrate occurs as elongated platy crystals or crystal aggregates, mostly disseminated irregularly, with higher concentrations occurring in discrete zones, thin layers, and/or veinlets parallel or oblique to the bedding. A 2-to 3-cm thick massive gas hydrate layer, parallel to bedding, was recovered at ???17 mbsf. Gas from a sample of this layer was composed of both CH4 and H2S. This sample is the first mixed-gas hydrate of CH4-H2S documented in ODP; it also contains ethane and minor amounts of CO2. Measured temperature of the recovered core ranged from 2 to - 18??C and are 6 to 8 degrees lower than in-situ temperatures. These temperature anomalies were caused by the partial dissociation of the CH4-H2S hydrate during recovery without a pressure core sampler. During this dissociation, toxic levels of H2S (??34S, +27.4???) were released. The ??13C values of the CH4 in the gas hydrate, -64.5 to -67.5???(PDB), together with ??D values of - 197 to - 199???(SMOW) indicate a primarily microbial source for the CH4. The ??18O value of the hydrate H2O is +2.9???(SMOW), comparable with the experimental fractionation factor for sea-ice. The unusual composition (CH4-H2S) and depth distribution (2-19 mbsf) of this gas hydrate indicate mixing between a methane-rich fluid with a pore fluid enriched in sulfide; at this site the former is advecting along an inclined fault into the active sulfate reduction zone. The facts that the CH4-H2S hydrate is primarily confined to the present day active sulfate reduction zone (2-19 mbsf), and that from here down to the BSR depth (19-68 mbsf) the gas hydrate inferred to exist is a ???99% CH4 hydrate, suggest that the mixing of CH4 and H2S is a geologically young process. Because the existence of a mixed CH4-H2S hydrate is indicative of moderate to intense advection of a methane-rich fluid into a near surface active sulfate reduction zone, technically active (faulted) margins with organic-rich sediments and moderate to high sedimentation rates are the most likely regions of occurrence. The extension of such a mixed hydrate below the sulfate reduction zone should reflect the time-span of methane advection into the sulfate reduction zone. ?? 1998 Elsevier Science B.V. All rights reserved.

Continuous flow reduction of artemisinic acid utilizing multi-injection strategies-closing the gap towards a fully continuous synthesis of antimalarial drugs.

PubMed

Pieber, Bartholomäus; Glasnov, Toma; Kappe, C Oliver

2015-03-09

One of the rare alternative reagents for the reduction of carbon-carbon double bonds is diimide (HN=NH), which can be generated in situ from hydrazine hydrate (N2H4⋅H2O) and O2. Although this selective method is extremely clean and powerful, it is rarely used, as the rate-determining oxidation of hydrazine in the absence of a catalyst is relatively slow using conventional batch protocols. A continuous high-temperature/high-pressure methodology dramatically enhances the initial oxidation step, at the same time allowing for a safe and scalable processing of the hazardous reaction mixture. Simple alkenes can be selectively reduced within 10-20 min at 100-120 °C and 20 bar O2 pressure. The development of a multi-injection reactor platform for the periodic addition of N2H4⋅H2O enables the reduction of less reactive olefins even at lower reaction temperatures. This concept was utilized for the highly selective reduction of artemisinic acid to dihydroartemisinic acid, the precursor molecule for the semisynthesis of the antimalarial drug artemisinin. The industrially relevant reduction was achieved by using four consecutive liquid feeds (of N2H4⋅H2O) and residence time units resulting in a highly selective reduction within approximately 40 min at 60 °C and 20 bar O2 pressure, providing dihydroartemisinic acid in ≥93% yield and ≥95% selectivity. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Effect of high-temperature on the swellable organically-modified silica (SOMS) and its application to gas-phase hydrodechlorination of trichloroethylene

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sohn, Hyuntae; Celik, Gokhan; Gunduz, Seval

Pd catalysts supported on swellable organically-modified silica (SOMS) and high-temperature-treated swellable organically-modified silica (H-SOMS) were characterized and tested for gas-phase hydrodechlorination (HDC) of trichloroethylene (TCE) conditions. The high-temperature treatment on SOMS resulted in an increase in surface area and pore diameter as well as significant improvement of Pd dispersion on H-SOMS with smaller Pd particle sizes compared to the Pd/SOMS catalyst. Although the high-temperature treatment led to some alteration of the SOMS polysiloxane network, the hydrophobicity and organic vapor adsorption characteristics of SOMS were preserved. The reduction and oxidation characteristics of Pd on SOMS and HSOMS were investigated in situmore » using XANES technique. It was found that the Pd sites in the pores of SOMS was accessible to small molecules such as H 2, facilitating the reduction of PdO x, whereas oxidation of metallic Pd was limited even at higher temperatures when O 2 was used. This effect was only observed over Pd/SOMS catalyst. For Pd/H-SOMS, because the pores were more widely open than Pd/SOMS, both reduction and oxidation of Pd were observed. Finally, the catalytic activity of Pd/H-SOMS for gas-phase HDC of TCE was significantly better than Pd/SOMS. When water was added to the reactant stream (TCE + H 2O), both Pd/SOMS and Pd/H-SOMS maintained its catalytic performances due to hydrophobic property of the supports.« less

Porous Ni-Mn oxide nanosheets in situ formed on nickel foam as 3D hierarchical monolith de-NOx catalysts

NASA Astrophysics Data System (ADS)

Cai, Sixiang; Zhang, Dengsong; Shi, Liyi; Xu, Jing; Zhang, Lei; Huang, Lei; Li, Hongrui; Zhang, Jianping

2014-06-01

In this work, we successfully in situ decorated nickel foam with porous Ni-Mn oxide nanosheets (3DH-NM/NF) as 3D hierarchical monolith de-NOx catalysts via a simple hydrothermal reaction and calcination process. The catalysts were carefully examined by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, elemental mapping, X-ray photoelectron spectroscopy, H2 temperature-programmed reduction and NH3 temperature-programmed desorption measurements. The results indicated that the nanosheets are composed of a Ni6Mn1O8 spinel and the metal species are uniformly dispersed in bi-metal oxides. As a result, the strong synergistic effects between the Mn and Ni species have been observed. The active oxygen species, reducible species and acidity are enhanced by the in situ formation of the nanosheets on the surface of nickel foam. These desirable features of 3DH-NM/NF catalysts bring about the excellent de-NOx performance. Moreover, the 3DH-NM/NF catalysts also present good stability and H2O resistance. Based on these favorable properties, 3DH-NM/NF could be considered as a promising candidate for the monolith de-NOx catalysts.In this work, we successfully in situ decorated nickel foam with porous Ni-Mn oxide nanosheets (3DH-NM/NF) as 3D hierarchical monolith de-NOx catalysts via a simple hydrothermal reaction and calcination process. The catalysts were carefully examined by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, elemental mapping, X-ray photoelectron spectroscopy, H2 temperature-programmed reduction and NH3 temperature-programmed desorption measurements. The results indicated that the nanosheets are composed of a Ni6Mn1O8 spinel and the metal species are uniformly dispersed in bi-metal oxides. As a result, the strong synergistic effects between the Mn and Ni species have been observed. The active oxygen species, reducible species and acidity are enhanced by the in situ formation of the nanosheets on the surface of nickel foam. These desirable features of 3DH-NM/NF catalysts bring about the excellent de-NOx performance. Moreover, the 3DH-NM/NF catalysts also present good stability and H2O resistance. Based on these favorable properties, 3DH-NM/NF could be considered as a promising candidate for the monolith de-NOx catalysts. Electronic supplementary information (ESI) available: Experimental details and catalytic performance of the NM/cordierite catalysts, SEM image and EDX analysis of the NF and 3DH-N/NF catalysts, N2 selectivity and catalytic performance under different gas hourly space velocities of the 3DH-NM/NF catalysts. See DOI: 10.1039/c4nr00475b

Study of Pt-Rh/CeO2-ZrO2-MxOy (M = Y, La)/Al2O3 three-way catalysts

NASA Astrophysics Data System (ADS)

Jiaxiu, Guo; Zhonghua, Shi; Dongdong, Wu; Huaqiang, Yin; Maochu, Gong; Yaoqiang, Chen

2013-05-01

CeO2-ZrO2-MxOy (M = Y; La) mixed oxides, prepared by co-precipitation method and characterized by Brunauer-Emmett-Teller (BET), X-ray diffraction (XRD), Raman spectra (RM) and oxygen pulse reaction, were comparatively investigated to elucidate the combinational effects of Y and/or La oxide promoters on the catalytic activity and anti-aging performance of monolithic cordierite honeycomb catalysts with low Pt and Rh content. The catalytic activities, water-gas shift (WGS) and steam reforming reaction (SR) were studied under a simulated gas mixture. The catalysts were also characterized by H2-temperature-programmed reduction (H2-TPR) and O2-temperature-programmed desorption (O2-TPD). The results showed that the prepared CeO2-ZrO2-MxOy oxides have a face-centered cubic fluorite structure and are nanosize. La3+ ions can significantly improve thermal stability and efficiently retard CeO2-ZrO2 crystal sintering and growth. Doped CeO2-ZrO2 with Y3+ and La3+ has 105 and 60 m2/g surface area and 460 and 390 μmol/g OSC before and after aging. The T50 of fresh Pt-Rh/CZYL/LA is 170 °C for CO, 222 °C for C3H8 and 189 °C for NO, and shift to 205, 262 and 228 °C after hydrothermal aging, which are better than those of Pt-Rh/CZY/LA or Pt-Rh/CZL/LA. WGS and SR are relate to the OSC of oxygen storage materials and absorbed oxygen species on the catalyst surface and affect the three-way catalytic activities of catalysts. The reductive property of noble metals and the dissociatively adsorbed O2 on the surface of catalysts are closely related to the catalytic activities.

Thermodynamic changes in mechanochemically synthesized magnesium hydride nanoparticles.

PubMed

Paskevicius, Mark; Sheppard, Drew A; Buckley, Craig E

2010-04-14

The thermodynamic properties of magnesium hydride nanoparticles have been investigated by hydrogen decomposition pressure measurements using the Sieverts technique. A mechanochemical method was used to synthesize MgH(2) nanoparticles (down to approximately 7 nm in size) embedded in a LiCl salt matrix. In comparison to bulk MgH(2), the mechanochemically produced MgH(2) with the smallest particle size showed a small but measurable decrease in the decomposition reaction enthalpy (DeltaH decrease of 2.84 kJ/mol H(2) from DeltaH(bulk) = 74.06 +/- 0.42 kJ/mol H(2) to DeltaH(nano) = 71.22 +/- 0.49 kJ/mol H(2)). The reduction in DeltaH matches theoretical predictions and was also coupled with a similar reduction in reaction entropy (DeltaS decrease of 3.8 J/mol H(2)/K from DeltaS(bulk) = 133.4 +/- 0.7 J/mol H(2)/K to DeltaS(nano) = 129.6 +/- 0.8 J/mol H(2)/K). The thermodynamic changes in the MgH(2) nanoparticle system correspond to a drop in the 1 bar hydrogen equilibrium temperature (T(1 bar)) by approximately 6 degrees C to 276.2 +/- 2.4 degrees C in contrast to the bulk MgH(2) system at 281.8 +/- 2.2 degrees C. The reduction in the desorption temperature is less than that expected from theoretical studies due to the decrease in DeltaS that acts to partially counteract the effect from the change in DeltaH.

Nitrous oxide causes a regulated hypothermia: rats select a cooler ambient temperature while becoming hypothermic.

PubMed

Ramsay, Douglas S; Seaman, Jana; Kaiyala, Karl J

2011-04-18

An initial administration of 60% nitrous oxide (N(2)O) evokes hypothermia in rats and if the administration continues for more than 1-2h, acute tolerance typically develops such that the initial reduction in core temperature (Tc) reverses and Tc recovers toward control values. Calorimeter studies at normal ambient temperature indicate that hypothermia results from a transient reduction in heat production (HP) combined with an elevation in heat loss. Acute tolerance develops primarily due to progressive increases in HP. Our aim was to determine whether rats provided a choice of ambient temperatures would behaviorally facilitate or oppose N(2)O-induced hypothermia. A gas-tight thermally-graded alleyway (range, 6.7-37.0°C) enabled male Long-Evans rats (n=12) to select a preferred ambient temperature during a 5-hour steady-state administration of 60% N(2)O and a separate paired control gas exposure (order counterbalanced). Tc was measured telemetrically from a sensor surgically implanted into the peritoneal cavity >7days before testing. Internal LED lighting maintained the accustomed day:night cycle (light cycle 0700-1900h) during sessions lasting 45.5h. Rats entered the temperature gradient at 1100h, and the 5-h N(2)O or control gas period did not start until 23h later to provide a long habituation/training period. Food and water were provided ad libitum at the center of the alleyway. The maximum decrease of mean Tc during N(2)O administration occurred at 0.9h and was -2.05±0.25°C; this differed significantly (p<0.0001) from the corresponding Tc change at 0.9h during control gas administration (0.01±0.14°C). The maximum decrease of the mean selected ambient temperature during N(2)O administration occurred at 0.7h and was -13.58±1.61°C; this differed significantly (p<0.0001) from the corresponding mean change in the selected ambient temperature at 0.7h during control gas administration (0.30±1.49°C). N(2)O appears to induce a regulated hypothermia because the selection of a cool ambient temperature facilitates the reduction in Tc. The recovery of Tc during N(2)O administration (i.e., acute tolerance development) could have been facilitated by selection of ambient temperatures that were warmer than those chosen during control administrations, but interestingly, this did not occur. Copyright © 2011 Elsevier Inc. All rights reserved.

Enhanced room-temperature catalytic decomposition of formaldehyde on magnesium-aluminum hydrotalcite/boehmite supported platinum nanoparticles catalyst.

PubMed

Yan, Zhaoxiong; Yang, Zhihua; Xu, Zhihua; An, Liang; Xie, Fang; Liu, Jiyan

2018-08-15

Magnesium-aluminum hydrotalcite (Mg-Al HT)/boehmite (AlOOH) composite supported Pt catalysts were obtained via one-pot microemulsion synthesis of Mg-Al HT/AlOOH composite and NaBH 4 -reduction of Pt precursor processes. The catalytic performances of the catalysts were evaluated for formaldehyde (HCHO) removal at room temperature. The performance tests showed that the catalyst obtained by immobilizing Pt nanoparticles (NPs) on Mg-Al HT/AlOOH support with Al/Mg molar ratio equivalent to 9:1 (Pt/Al 9 Mg 1 ) displayed a superior catalytic activity and stability for HCHO removal. In order to find out the causes of its higher activity, X-ray diffraction, transmission electron microscopy, N 2 adsorption/desorption, X-ray photoelectron spectroscopy, temperature programmed desorption of CO 2 and reduction of H 2 were used to analyze the physicochemical properties of Pt/Al 9 Mg 1 and Pt/AlOOH. The remarkable catalytic performance of Pt/Al 9 Mg 1 is mainly attributed to the relatively larger amount of surface oxygen species, and more reactive oxygen species led by the interaction of Mg-Al HT and AlOOH/Pt, and relatively larger number of weak base sites caused by Mg-Al HT. The formate species are the main reaction intermediate over Pt/Al 9 Mg 1 during HCHO oxidation at room temperature, which could be further oxidized into CO 2 and H 2 O in the presence of O 2 . This study might shed some light on further improving the catalytic performance of the catalyst for indoor air purification at room temperature. Copyright © 2018 Elsevier Inc. All rights reserved.

First Detection of Near-infrared Line Emission from Organics in Young Circumstellar Disks

NASA Astrophysics Data System (ADS)

Mandell, Avi M.; Bast, Jeanette; van Dishoeck, Ewine F.; Blake, Geoffrey A.; Salyk, Colette; Mumma, Michael J.; Villanueva, Geronimo

2012-03-01

We present an analysis of high-resolution spectroscopy of several bright T Tauri stars using the CRIRES spectrograph on the Very Large Telescope and NIRSPEC spectrograph on the Keck Telescope, revealing the first detections of emission from HCN and C2H2 in circumstellar disks at near-infrared wavelengths. Using advanced data reduction techniques, we achieve a dynamic range with respect to the disk continuum of ~500 at 3 μm, revealing multiple emission features of H2O, OH, HCN, and C2H2. We also present stringent upper limits for two other molecules thought to be abundant in the inner disk, CH4 and NH3. Line profiles for the different detected molecules are broad but centrally peaked in most cases, even for disks with previously determined inclinations of greater than 20°, suggesting that the emission has both a Keplerian and non-Keplerian component as observed previously for CO emission. We apply two different modeling strategies to constrain the molecular abundances and temperatures: we use a simplified single-temperature local thermal equilibrium (LTE) slab model with a Gaussian line profile to make line identifications and determine a best-fit temperature and initial abundance ratios, and we compare these values with constraints derived from a detailed disk radiative transfer model assuming LTE excitation but utilizing a realistic temperature and density structure. Abundance ratios from both sets of models are consistent with each other and consistent with expected values from theoretical chemical models, and analysis of the line shapes suggests that the molecular emission originates from within a narrow region in the inner disk (R < 1 AU). Based partially on observations collected at the European Southern Observatory Very Large Telescope under program ID 179.C-0151, program ID 283.C-5016, and program ID 082.C-0432 (P.I.: Pontopiddan).

The reduction of chromium (VI) by iron (II) in aqueous solutions

NASA Astrophysics Data System (ADS)

Pettine, Maurizio; D'Ottone, Luca; Campanella, Luigi; Millero, Frank J.; Passino, Roberto

1998-05-01

The rates of the reduction of Cr(VI) with Fe(II) were measured in NaCl, NaClO 4, and natural seawater as a function of pH (1.5-8.7), temperature (5-40°C) and ionic strength (I = 0.01-2 M). The pseudo first-order rate constant (log k 1) showed a parabolic dependence on pH decreasing from 1.5 to 4.5 and increasing from 5.5 to 8.7. The kinetics of the reaction in these two regions of pH also showed different influences of temperature, ionic strength, and reductant concentration. The rate of Cr(VI) reduction is described by the general expression -d[Cr(VI)]/dt = k [Cr(VI)] [Fe(II)] where k (M -1 min -1) can be determined from the log k=6.74-1.01 pH-188.5/T for the pH range 1.5-4.5 (σ = 0.2) and log k=11.93+0.95 pH-4260.1/T-1.06 I 0.5 for the pH range 5-8.7 (σ = 0.2) from 5 to 40°C and 0.01 to 2 M ionic strength. The effect of pH, temperature, and ionic strength on the reaction indicates that the reactions at low pH are due to H2CrO4+ Fe2+limit→k H2 A-Feproducts While the reactions at high pH are due to HCrO4-+ FeOH+limit→k HA-FeOHproductsHCrO4-+ Fe(OH)2limit→k HA-Fe(OH)2 products The overall rate expression over the entire pH range can be determined from (H 2A = H 2CrO 4) k=k H2 A-Feα( H2A)α( Fe2+)+k HA-FeOHα( HA-)α( FeOH+)+k HA-Fe(OH)2 α( HA-)α( Fe(OH)2) where k H2A-Fe = 5 x 10 6, k HA-FeOH = 1 x 10 6, k HA-Fe (OH)2= 5 x 10 11. In oxic aqueous systems Cr(VI) competes with O 2 in the oxidation of Fe(II) and an extension of the rate law for Cr(VI) reduction with Fe(II) in oxygenated solutions is proposed. The application of this extended rate law to environmental conditions suggests that this reaction influences the distribution of oxidized and reduced species of chromium in oxic and anoxic waters.

Electrochemical Reduction of N2 under Ambient Conditions for Artificial N2 Fixation and Renewable Energy Storage Using N2 /NH3 Cycle.

PubMed

Bao, Di; Zhang, Qi; Meng, Fan-Lu; Zhong, Hai-Xia; Shi, Miao-Miao; Zhang, Yu; Yan, Jun-Min; Jiang, Qing; Zhang, Xin-Bo

2017-01-01

Using tetrahexahedral gold nanorods as a heterogeneous electrocatalyst, an electrocatalytic N 2 reduction reaction is shown to be possible at room temperature and atmospheric pressure, with a high Faradic efficiency up to 4.02% at -0.2 V vs reversible hydrogen electrode (1.648 µg h -1 cm -2 and 0.102 µg h -1 cm -2 for NH 3 and N 2 H 4 ·H 2 O, respectively). © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Performance characterization of CNTs and γ-Al2O3 supported cobalt catalysts in Fischer-Tropsch reaction

NASA Astrophysics Data System (ADS)

Ali, Sardar; Zabidi, Noor Asmawati Mohd; Subbarao, Duvvuri

2014-10-01

Catalysts were prepared via a wet impregnation method. Different physicochemical properties of the samples were revealed by transmission electron microscope (TEM), temperature programmed reduction (H2-TPR) and carbon dioxide desorption (CO2-desorption). Fischer-Tropsch reaction (FTS) was carried out in a fixed-bed microreactor at 220°C and 1 atm, with H2/ CO = 2v / v and space velocity, SV of 12L/g.h for 5 h. Various characterization techniques revealed that there was a stronger interaction between Co and Al2O3 support compared to that of CNTs support. CNTs support increased the reducibility and decreased Co particle size. A significant increase in % CO conversion and FTS reaction rate was observed over CNTs support compared to that of Co / Al2O3. Co/CNTs resulted in higher C5+ hydrocarbons selectivity compared to that of Co / Al2O3 catalyst. CNTs are a better support for Co compared to Al2O3.

Time-resolved in situ XAS study of the preparation of supported gold clusters.

PubMed

Bus, Eveline; Prins, Roel; van Bokhoven, Jeroen A

2007-07-07

Incipient-wetness impregnation of gamma-Al(2)O(3) with HAuCl(4) and subsequent removal of chlorine with NaOH, and deposition-precipitation of HAuCl(4) on TiO(2) at pH 7 resulted in supported Au(3+) species. Time-resolved in situ XAS at the Au L(3) edge showed that the Al(2)O(3)-supported oxidic or hydroxidic species were reduced in hydrogen at 440 K to yield small metallic gold clusters. The Au(3+) precursor decomposed to metallic gold in inert atmosphere at 573 K and in oxidizing atmosphere above 623 K. In all atmospheres, initially small clusters were formed that gradually grew with increasing temperature. The TiO(2)-supported species were considerably less stable. In hydrogen and carbon monoxide, Au(0) clusters of 1 to 1.5 nm were formed at room temperature, which was the lowest temperature studied. In inert and oxidizing atmosphere, the Au(3+) precursor decomposed fully to metallic gold at 530 K, as shown by XAS and temperature-programmed experiments. Large clusters were obtained already in the initial stage of reduction. Residual chlorine inhibited the reduction and led to sintering of the gold clusters. Exposure of the TiO(2)-supported catalyst precursor to light or the X-ray beam led to partial reduction, and STEM showed that storage of the reduced gold clusters under ambient conditions led to agglomeration and bimodal cluster-size distributions.

Low-temperature thermal reduction of graphene oxide: In situ correlative structural, thermal desorption, and electrical transport measurements

NASA Astrophysics Data System (ADS)

Lipatov, Alexey; Guinel, Maxime J.-F.; Muratov, Dmitry S.; Vanyushin, Vladislav O.; Wilson, Peter M.; Kolmakov, Andrei; Sinitskii, Alexander

2018-01-01

Elucidation of the structural transformations in graphene oxide (GO) upon reduction remains an active and important area of research. We report the results of in situ heating experiments, during which electrical, mass spectrometry, X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, and transmission electron microscopy (TEM) measurements were carried out correlatively. The simultaneous electrical and temperature programmed desorption measurements allowed us to correlate the onset of the increase in the electrical conductivity of GO by five orders of magnitude at about 150 °C with the maxima of the rates of desorption of H2O, CO, and CO2. Interestingly, this large conductivity change happens at an intermediate level of the reduction of GO, which likely corresponds to the point when the graphitic domains become large enough to enable percolative electronic transport. We demonstrate that the gas desorption is intimately related to (i) the changes in the chemical structure of GO detected by XPS and Raman spectroscopy and (ii) the formation of nanoscopic holes in GO sheets revealed by TEM. These in situ observations provide a better understanding of the mechanism of the GO thermal reduction.

Probing the Active Surface Sites for CO Reduction on Oxide-Derived Copper Electrocatalysts

DOE PAGES

Verdaguer-Casadevall, Arnau; Li, Christina W.; Johansson, Tobias P.; ...

2015-07-30

CO electroreduction activity on oxide-derived Cu (OD-Cu) was found to correlate with metastable surface features that bind CO strongly. OD-Cu electrodes prepared by H 2 reduction of Cu 2O precursors reduce CO to acetate and ethanol with nearly 50% Faradaic efficiency at moderate overpotential. Temperature-programmed desorption of CO on OD-Cu revealed the presence of surface sites with strong CO binding that are distinct from the terraces and stepped sites found on polycrystalline Cu foil. After annealing at 350 °C, the surface-area corrected current density for CO reduction is 44-fold lower and the Faradaic efficiency is less than 5%. These changesmore » are accompanied by a reduction in the proportion of strong CO binding sites. Here, we propose that the active sites for CO reduction on OD-Cu surfaces are strong CO binding sites that are supported by grain boundaries. Uncovering these sites is a first step toward understanding the surface chemistry necessary for efficient CO electroreduction.« less

Low-temperature solvothermal approach to the synthesis of La4Ni3O8 by topotactic oxygen deintercalation.

PubMed

Blakely, Colin K; Bruno, Shaun R; Poltavets, Viktor V

2011-07-18

A chimie douce solvothermal reduction method is proposed for topotactic oxygen deintercalation of complex metal oxides. Four different reduction techniques were employed to qualitatively identify the relative reduction activity of each including reduction with H(2) and NaH, solution-based reduction using metal hydrides at ambient pressure, and reduction under solvothermal conditions. The reduction of the Ruddlesden-Popper nickelate La(4)Ni(3)O(10) was used as a test case to prove the validity of the method. The completely reduced phase La(4)Ni(3)O(8) was produced via the solvothermal technique at 150 °C--a lower temperature than by other more conventional solid state oxygen deintercalation methods.

Evaluation and characterization of the methane-carbon dioxide decomposition reaction

NASA Technical Reports Server (NTRS)

Davenport, R. J.; Schubert, F. H.; Shumar, J. W.; Steenson, T. S.

1975-01-01

A program was conducted to evaluate and characterize the carbon dioxide-methane (CO2-CH4) decomposition reaction, i.e., CO2 + CH4 = 2C + 2H2O. The primary objective was to determine the feasibility of applying this reaction at low temperatures as a technique for recovering the oxygen (O2) remaining in the CO2 which exits mixed with CH4 from a Sabatier CO2 reduction subsystem (as part of an air revitalization system of a manned spacecraft). A test unit was designed, fabricated, and assembled for characterizing the performance of various catalysts for the reaction and ultraviolet activation of the CH4 and CO2. The reactor included in the test unit was designed to have sufficient capacity to evaluate catalyst charges of up to 76 g (0.17 lb). The test stand contained the necessary instrumentation and controls to obtain the data required to characterize the performance of the catalysts and sensitizers tested: flow control and measurement, temperature control and measurement, product and inlet gas analysis, and pressure measurement. A product assurance program was performed implementing the concepts of quality control and safety into the program effort.

The electrocatalytic reduction of nitrate in water on Pd/Sn-modified activated carbon fiber electrode.

PubMed

Wang, Ying; Qu, Jiuhui; Wu, Rongcheng; Lei, Pengju

2006-03-01

The Pd/Sn-modified activated carbon fiber (ACF) electrodes were successfully prepared by the impregnation of Pd2+ and Sn2+ ions onto ACF, and their electrocatalytic reduction capacity for nitrate ions in water was evaluated in a batch experiment. The electrode was characterized by scanning electron microscope (SEM), transmission electron microscope (TEM), X-ray diffraction (XRD), X-ray photoelectron spectrum (XPS) and temperature programmed reduction (TPR). The capacity for nitrate reduction depending on Sn content on the electrode and the pH of electrolyte was discussed at length. The results showed that at an applied current density of 1.11 mA cm(-2), nitrate ions in water (solution volume: 400 mL) were reduced from 110 to 3.4 mg L(-1) after 240 min with consecutive change of intermediate nitrite. Ammonium ions and nitrogen were formed as the main final products. The amount of other possible gaseous products (including NO and N2O) was trace. With the increase of Sn content on the Pd/Sn-modified ACF electrode, the activity for nitrate reduction went up to reach a maximum (at Pd/Sn = 4) and then decreased, while the selectivity to N2 was depressed. Higher pH value of electrolyte exhibited more suppression effect on the reduction of nitrite than that of nitrate. However, no significant influence on the final ammonia formation was observed. Additionally, Cu ion in water was found to cover the active sites of the electrode to make the electrode deactivated.

Low temperature chemical reduction of fusional sodium metasilicate nonahydrate into a honeycomb porous silicon nanostructure.

PubMed

Liang, Jianwen; Wei, Denghu; Lin, Ning; Zhu, Youngchun; Li, Xiaona; Zhang, Jingjing; Fan, Long; Qian, Yitai

2014-07-04

Honeycomb porous silicon (hp-Si) has been synthesized by a low temperature (200 °C) magnesiothermic reduction of Na2SiO3·9H2O. This process can be regarded as a general synthesis method for other silicide materials. Significantly, hp-Si features excellent electrochemical properties after graphene coating.

Fracture toughness and Charpy impact properties of several RAFMS before and after irradiation in HFIR

NASA Astrophysics Data System (ADS)

Sokolov, M. A.; Tanigawa, H.; Odette, G. R.; Shiba, K.; Klueh, R. L.

2007-08-01

As part of the development of candidate reduced-activation ferritic steels for fusion applications, several steels, namely F82H, 9Cr-2WVTa steels and F82H weld metal, are being investigated in the joint DOE-JAEA collaboration program. Within this program, three capsules containing a variety of specimen designs were irradiated at two design temperatures in the ORNL High Flux Isotope Reactor (HFIR). Two capsules, RB-11J and RB-12J, were irradiated in the HFIR removable beryllium positions with europium oxide (Eu 2O 3) thermal neutron shields in place. Specimens were irradiated up to 5 dpa. Capsule JP25 was irradiated in the HFIR target position to 20 dpa. The design temperatures were 300 °C and 500 °C. Precracked third-sized V-notch Charpy (3.3 × 3.3 × 25.4 mm) and 0.18 T DC(T) specimens were tested to determine transition and ductile shelf fracture toughness before and after irradiation. The master curve methodology was applied to evaluate the fracture toughness transition temperature, T0. Irradiation induced shifts of T0 and reductions of JQ were compared with Charpy V-notch impact properties. Fracture toughness and Charpy shifts were also compared to hardening results.

Disproportionation and thermochemical sulfate reduction reactions in S-H20-Ch4 and S-D2O-CH4 systems from 200 to 340 °C at elevated pressures

USGS Publications Warehouse

Yuan, Shunda; Chou, I-Ming; Burruss, Robert A.

2013-01-01

Elemental sulfur, as a transient intermediate compound, by-product, or catalyst, plays significant roles in thermochemical sulfate reduction (TSR) reactions. However, the mechanisms of the reactions in S-H2O-hydrocarbons systems are not clear. To improve our understanding of reaction mechanisms, we conducted a series of experiments between 200 and 340 °C for S-H2O-CH4, S-D2O-CH4, and S-CH4-1m ZnBr2 systems in fused silica capillary capsules (FSCC). After a heating period ranging from 24 to 2160 hours (hrs), the quenched samples were analyzed by Raman spectroscopy. Combined with the in situ Raman spectra collected at high temperatures and pressures in the S-H2O and S-H2O-CH4 systems, our results showed that (1) the disproportionation of sulfur in the S-H2O-CH4 system occurred at temperatures above 200 °C and produced H2S, SO42-, and possibly trace amount of HSO4-; (2) sulfate (and bisulfate), in the presence of sulfur, can be reduced by methane between 250 and 340 °C to produce CO2 and H2S, and these TSR temperatures are much closer to those of the natural system (2O-CH4 system may take place simultaneously, with TSR being favored at higher temperatures; and (4) in the system S-D2O-CH4, both TSR and the competitive disproportionation reactions occurred simultaneously at temperatures above 300 °C, but these reactions were very slow at lower temperatures. Our observation of methane reaction at 250 °C in a laboratory time scale suggests that, in a geologic time scale, methane may be destroyed by TSR reactions at temperatures > 200 °C that can be reached by deep drilling for hydrocarbon resources.

Regeneration and sulfur poisoning behavior of In/H-BEA catalyst for NOx reduction by CH4

NASA Astrophysics Data System (ADS)

Pan, Hua; Jian, Yanfei; Yu, Yanke; He, Chi; Shen, Zhenxing; Liu, Hongxia

2017-04-01

Sulfur poisoning and regeneration behavior of In/H-BEA catalyst were carried out in NOx reduction by CH4. In/H-BEA catalyst exhibited a poor resistance to sulfur dioxide after addition of 200 ppm SO2 and 10 vol.% H2O into NO reduction with CH4 at 450 °C for 45 h. Sulfur poisoning of In/H-BEA was attributed to the inhibition of NOx adsorption on Brønsted acid sites, suppression of reaction intermediates generation on the active sites, and the formation of surface sulfate species. The formation of surface sulfate reduced the availability of surface active sites, blocked the pore structure and decreased the surface area of catalyst. These changes in chemical and textural properties resulted in a severe loss in the activity of sulfated In/H-BEA catalyst for NO reduction with CH4. H2 reduction is a promising technology for regeneration of In/H-BEA deactivated by SO2 for removing NOx from lean-burn and diesel exhausts. Indium sulfate could be reduced by H2 to InO+ with In2O3 and In(OH)2+ as the intermediates. The optimal parameters of H2 reduction was regeneration temperature of 400 °C and regeneration time of 60 min which completely recovered the catalytic activity of In/H-BEA.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jadeja, K.A.; Patel, K.M.; Tanna, R.L., E-mail: kumarpal@ipr.res.in

Low temperature glow discharge wall conditioning (GDC) using H{sub 2} gas is effective in reduction of oxygen and carbon (low-Z) contain impurities on near surface region of vessel wall. The high retention of hydrogen in vessel wall/components due to long operation of H{sub 2} GDC increases hydrogen out-gassing during tokamak operation and affects the production of high temperature plasma. The hydrogen retention can be reduced using inert gas GDC by sputter cleaning for short duration. But in that case the out-gassing rate of inert gas increases, that again impairs the plasma performance. To overcome above problems, the GDC with hydrogen-inertmore » gas mixture can be used for better removal of C and O surface contaminants and low hydrogen retention in surface. In ADITYA tokamak, H{sub 2}-GDC is carried out regularly after plasma operation, while the GDC with argon-hydrogen (Ar-H{sub 2}) mixture has been experimentally tested to observe the reduction of oxygen and carbon impurities along with low hydrogen retention. In Ar-H{sub 2} GDC, the reason being the formation of ArH{sup +} hydride ions, which has quite long life and more energy compared to H{sub 2}{sup +} ions formed in H{sub 2} GDC for breaking the bond of wall molecules. A systematic comparative study of H{sub 2} GDC and Ar-H{sub 2} Mixture GDC by changing the mixture ratio has been carried out in ADITYA tokamak. The relative levels of oxygen and carbon contain impurities have been measured using residual gas analyzer in both GDC's. We have observed a substantial reduction in oxygen and carbon impurities with a significant improvement in wall condition with Ar-H{sub 2} GDC compared to the H{sub 2} GDC. The effect of wall conditioning by Ar-H{sub 2} GDC on the performance of high temperature plasma operation will be presented in this paper. (author)« less

Iridium clusters in KLTL zeolite: Structure and catalytic selectivity for n-hexane aromatization

DOE Office of Scientific and Technical Information (OSTI.GOV)

Triantafillou, N.D.; Miller, J.T.; Gates, B.C.

Catalysts consisting of Ir clusters in zeolite KLTL were prepared by reduction of [Ir(NH{sub 3}){sub 5}Cl]Cl{sub 2} in the zeolite with H{sub 2} at temperatures 300 or 500{degrees}C. The catalysts were tested for reactions of n-hexane and H{sub 2} at 400, 440 and 480{degrees}C and were characterized by temperature-programmed reduction, hydrogen chemisorption, transmission electron microscopy, infrared spectroscopy of adsorbed CO, and extended X-ray absorption fine structure spectroscopy. The clusters consist of 4 to 6 Ir atoms on average and are sufficiently small to reside within the pores of the zeolite. The infrared spectra characteristic of terminal CO suggest that themore » support environment is slightly basic and that the Ir clusters are electron rich relative to the bulk metal. Notwithstanding the small cluster size, the support basicity, and the confining geometry of the LTL zeolite pore structure, the catalytic performance is similar to those of other Ir catalysts, with a poor selectivity for aromatization and a high selectivity for hydrogenolysis. These results are consistent with the inference that the principal requirements for selective naphtha aromatization catalysts are both a nonacidic support and a metal with a low hydrogenolsis activity, i.e., Pt. 47 refs., 6 figs., 3 tabs.« less

Hydrogen storage and evolution catalysed by metal hydride complexes.

PubMed

Fukuzumi, Shunichi; Suenobu, Tomoyoshi

2013-01-07

The storage and evolution of hydrogen are catalysed by appropriate metal hydride complexes. Hydrogenation of carbon dioxide by hydrogen is catalysed by a [C,N] cyclometalated organoiridium complex, [Ir(III)(Cp*)(4-(1H-pyrazol-1-yl-κN(2))benzoic acid-κC(3))(OH(2))](2)SO(4) [Ir-OH(2)](2)SO(4), under atmospheric pressure of H(2) and CO(2) in weakly basic water (pH 7.5) at room temperature. The reverse reaction, i.e., hydrogen evolution from formate, is also catalysed by [Ir-OH(2)](+) in acidic water (pH 2.8) at room temperature. Thus, interconversion between hydrogen and formic acid in water at ambient temperature and pressure has been achieved by using [Ir-OH(2)](+) as an efficient catalyst in both directions depending on pH. The Ir complex [Ir-OH(2)](+) also catalyses regioselective hydrogenation of the oxidised form of β-nicotinamide adenine dinucleotide (NAD(+)) to produce the 1,4-reduced form (NADH) under atmospheric pressure of H(2) at room temperature in weakly basic water. In weakly acidic water, the complex [Ir-OH(2)](+) also catalyses the reverse reaction, i.e., hydrogen evolution from NADH to produce NAD(+) at room temperature. Thus, interconversion between NADH (and H(+)) and NAD(+) (and H(2)) has also been achieved by using [Ir-OH(2)](+) as an efficient catalyst and by changing pH. The iridium hydride complex formed by the reduction of [Ir-OH(2)](+) by H(2) and NADH is responsible for the hydrogen evolution. Photoirradiation (λ > 330 nm) of an aqueous solution of the Ir-hydride complex produced by the reduction of [Ir-OH(2)](+) with alcohols resulted in the quantitative conversion to a unique [C,C] cyclometalated Ir-hydride complex, which can catalyse hydrogen evolution from alcohols in a basic aqueous solution (pH 11.9). The catalytic mechanisms of the hydrogen storage and evolution are discussed by focusing on the reactivity of Ir-hydride complexes.

In Situ UV-Visible Assessment of Iron-Based High-Temperature Water-Gas Shift Catalysts Promoted with Lanthana: An Extent of Reduction Study

DOE PAGES

Hallac, Basseem B.; Brown, Jared C.; Stavitski, Eli; ...

2018-02-04

Here, the extent of reduction of unsupported iron-based high-temperature water-gas shift catalysts with small (<5 wt %) lanthana contents was studied using UV-visible spectroscopy. Temperature- programmed reduction measurements showed that lanthana content higher than 0.5 wt % increased the extent of reduction to metallic Fe, while 0.5 wt % of lanthana facilitated the reduction to Fe 3O 4. In situ measurements on the iron oxide catalysts using mass and UV-visible spectroscopies permitted the quantification of the extent of reduction under temperature-programmed reduction and high-temperature water-gas shift conditions. The oxidation states were successfully calibrated against normalized absorbance spectra of visible lightmore » using the Kubelka-Munk theory. The normalized absorbance relative to the fully oxidized Fe 2O 3 increased as the extent of reduction increased. XANES suggested that the average bulk iron oxidation state during the water-gas shift reaction was Fe +2.57 for the catalyst with no lanthana and Fe +2.54 for the catalysts with 1 wt % lanthana. However, the UV-vis spectra suggest that the surface oxidation state of iron would be Fe +2.31 for the catalyst with 1 wt % lanthana if the oxidation state of iron in the catalyst with 0 wt % lanthana were Fe +2.57. The findings of this paper emphasize the importance of surface sensitive UV-visible spectroscopy for determining the extent of catalyst reduction during operation. Furthermore, the paper highlights the potential to use bench-scale UV-visible spectroscopy to study the surface chemistry of catalysts instead of less-available synchrotron X-ray radiation facilities.« less

In Situ UV-Visible Assessment of Iron-Based High-Temperature Water-Gas Shift Catalysts Promoted with Lanthana: An Extent of Reduction Study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hallac, Basseem B.; Brown, Jared C.; Stavitski, Eli

Here, the extent of reduction of unsupported iron-based high-temperature water-gas shift catalysts with small (<5 wt %) lanthana contents was studied using UV-visible spectroscopy. Temperature- programmed reduction measurements showed that lanthana content higher than 0.5 wt % increased the extent of reduction to metallic Fe, while 0.5 wt % of lanthana facilitated the reduction to Fe 3O 4. In situ measurements on the iron oxide catalysts using mass and UV-visible spectroscopies permitted the quantification of the extent of reduction under temperature-programmed reduction and high-temperature water-gas shift conditions. The oxidation states were successfully calibrated against normalized absorbance spectra of visible lightmore » using the Kubelka-Munk theory. The normalized absorbance relative to the fully oxidized Fe 2O 3 increased as the extent of reduction increased. XANES suggested that the average bulk iron oxidation state during the water-gas shift reaction was Fe +2.57 for the catalyst with no lanthana and Fe +2.54 for the catalysts with 1 wt % lanthana. However, the UV-vis spectra suggest that the surface oxidation state of iron would be Fe +2.31 for the catalyst with 1 wt % lanthana if the oxidation state of iron in the catalyst with 0 wt % lanthana were Fe +2.57. The findings of this paper emphasize the importance of surface sensitive UV-visible spectroscopy for determining the extent of catalyst reduction during operation. Furthermore, the paper highlights the potential to use bench-scale UV-visible spectroscopy to study the surface chemistry of catalysts instead of less-available synchrotron X-ray radiation facilities.« less

Energy for biologic sulfate reduction in a hydrothermally formed ocean on Europa

NASA Astrophysics Data System (ADS)

Zolotov, Mikhail Y.; Shock, Everett L.

2003-04-01

Formation of a sulfate-bearing ocean on Jupiter's satellite Europa by quenched hydrothermal fluids provides a source of metabolic energy for low-temperature sulfate-reducing organisms that use dissolved H2 as an electron donor. Inhibition of thermodynamically favorable sulfate reduction in cooled hydrothermal fluids creates the potential for biologic reduction. Both high temperature and reduced conditions of ocean-forming hydrothermal solutions favor sulfate reduction in quenched fluids. The maximum amount of energy available to support autotrophic sulfate reduction is on the order of a few kilojoules per kilogram of water and is limited by the low abundances of either H2 or sulfate in ocean-forming fluids. Although this irreplaceable energy source might have supported early life on Europa, maintenance of biologic sulfate reduction throughout the ocean's history would require a supply of organic compounds from endogenic sources or from the satellite's surface.

The Effect of Temperature and Hydrogen Limited Growth on the Fractionation of Sulfur Isotopes by Thermodesulfatator indicus, a Deep-sea Hydrothermal Vent Sulfate-Reducing Bacterium

NASA Astrophysics Data System (ADS)

Hoek, J.; Reysenbach, A.; Habicht, K.; Canfield, D. E.

2004-12-01

Sulfate-reducing bacteria fractionate sulfur isotopes during dissimilatory sulfate reduction, producing sulfide depleted in 34S. Although isotope fractionation during sulfate reduction of pure cultures has been extensively studied, most of the research to date has focused on mesophilic sulfate reducers, particularly for the species Desulfovibrio desulfuricans. Results from these studies show that: 1) fractionations range from 3-46‰ with an average around 18‰ , 2) when organic electron donors are utilized, the extent of fractionation is dependent on the rate of sulfate reduction, with decreasing fractionations observed with higher specific rates, 3) fractionations are suppressed with low sulfate concentrations, and when hydrogen is used as the electron donor. High specific sulfate-reduction rates are encountered when sulfate-reducing bacteria metabolize at their optimal temperature and under non-limiting substrate conditions. Changes in both temperature and substrate availability could shift fractionations from those expressed under optimal growth conditions. Sulfate reducers may frequently experience substrate limitation and sub-optimal growth temperatures in the environment. Therefore it is important to understand how sulfate-reducing bacteria fractionate sulfur isotopes under conditions that more closely resemble the restrictions imposed by the environment. In this study the fractionation of sulfur isotopes by Thermodesulfatator indicus was explored during sulfate reduction under a wide range of temperatures and with both hydrogen-saturating and hydrogen-limited conditions. T. indicus is a thermophilic (temperature optimum = 70° C) chemolithotrophic sulfate-reducing bacterium, which was recently isolated from a deep-sea hydrothermal vent on the Central Indian Ridge. This bacterium represents the type species of a new genus and to date is the most deeply branching sulfate-reducing bacterium known. T. indicus was grown in carbonate-buffered salt-water medium with H2 as the sole electron donor, and CO2 as primary carbon source. The fractionation of sulfur isotopes was measured in batch cultures and in a thermal gradient block over the full temperature range of growth (40-80° C). For experiments in the gradient block, cell-specific rates of sulfate reduction increased with increasing temperatures to 70° C after which sulfate-reduction rates rapidly decreased. The range of fractionations (1.5-10‰ ) was typical for growth with hydrogen as the electron donor. Fractionations decreased with increasing temperature from 40--60° C, and increased with increasing temperatures from 60-80° C. Growth under H2-limited conditions in a fed-batch culture revealed high fractionations of 24-37‰ . This is the first report of sulfur isotope fractionation under H2 limited growth and indicates that large fractionations are produced when H2 is supplied as a limiting substrate. Our results suggest that fractionation is controlled by the competition of forward and reverse enzymatic reaction rates during sulfate reduction and by sulfate transport into the cell.

Passive Biobarrier for Treating Co-mingled Perchlorate and RDX in Groundwater at an Active Range

DTIC Science & Technology

2016-05-12

and Groundwater Temperature ............................. 102 6.1.2 Dissolved Oxygen (DO) and Oxidation Reduction Potential (ORP...22 or equivalent). Parameters, including temperature , conductivity, dissolved oxygen , oxidation-reduction potential (ORP), turbidity, and pH were...3% for temperature and specific conductivity, and ᝺% for dissolved oxygen , ORP, and turbidity. When parameters were stable according to the above

The primary solar-type atmosphere surrounding the accreting Earth: H2O-induced high surface temperature.

NASA Astrophysics Data System (ADS)

Sasaki, S.

In the solar nebula, a growing planet attracts ambient gas to form a solar-type atmosphere. The structure of this H2-He atmosphere is calculated assuming the Earth was formed in the nebula. The blanketing effect of the atmosphere renders the planetary surface molten when the planetary mass exceeds 0.2 ME (ME being the present Earth's mass). Reduction of the surface melt by atmospheric H2 should add a large amount of H2O to the atmosphere: under the quartz-iron-fayalite oxygen buffer, partial pressure ratio P(H2O)/P(H2) becomes higher than 0.1. Enhancing opacity and gas mean molecular weight, the excess H2O raises the temperature and renders the atmosphere in convective equilibrium, while the dissociation of H2 suppresses the adiabatic temperature gradient. The surface temperature of the proto-Earth can be as high as 4700K when its mass is 1 ME. Such a high temperature may accelerate the evaporation of surface materials. A deep totally-molten magma ocean should exist in the accretion Earth.

Selective hydrodeoxygenation of cyclic vicinal diols to cyclic alcohols over tungsten oxide-palladium catalysts.

PubMed

Amada, Yasushi; Ota, Nobuhiko; Tamura, Masazumi; Nakagawa, Yoshinao; Tomishige, Keiichi

2014-08-01

Hydrodeoxygenation of cyclic vicinal diols such as 1,4-anhydroerythritol was conducted over catalysts containing both a noble metal and a group 5-7 transition-metal oxide. The combination of Pd and WOx allowed the removal of one of the two OH groups selectively. 3-Hydroxytetrahydrofuran was obtained from 1,4-anhydroerythritol in 72 and 74% yield over WOx -Pd/C and WOx -Pd/ZrO2 , respectively. The WOx -Pd/ZrO2 catalyst was reusable without significant loss of activity if the catalyst was calcined as a method of regeneration. Characterization of WOx -Pd/C with temperature-programmed reduction, X-ray diffraction, and transmission electron microscopy/energy-dispersive X-ray spectroscopy suggested that Pd metal particles approximately 9 nm in size were formed on amorphous tungsten oxide particles. A reaction mechanism was proposed on the basis of kinetics, reaction results with tungsten oxides under an atmosphere of Ar, and density functional theory calculations. A tetravalent tungsten center (W(IV) ) was formed by reduction of WO3 with the Pd catalyst and H2 , and this center served as the reductant for partial hydrodeoxygenation. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Nitrous Oxide Causes a Regulated Hypothermia: Rats Select a Cooler Ambient Temperature While Becoming Hypothermic

PubMed Central

Ramsay, Douglas S.; Seaman, Jana; Kaiyala, Karl J.

2011-01-01

An initial administration of 60% nitrous oxide (N2O) evokes hypothermia in rats and if the administration continues for more than 1 – 2 hours, acute tolerance typically develops such that the initial reduction in core temperature (Tc) reverses and Tc recovers toward control values. Calorimeter studies at normal ambient temperature indicate that hypothermia results from a transient reduction in heat production (HP) combined with an elevation in heat loss. Acute tolerance develops primarily due to progressive increases in HP. Our aim was to determine whether rats provided a choice of ambient temperatures would behaviorally facilitate or oppose N2O -induced hypothermia. A gas-tight thermally-graded alleyway (range, 6.7 – 37.0°C) enabled male Long-Evans rats (n=12) to select a preferred ambient temperature during a 5-hour steady-state administration of 60% N2O and a separate paired control gas exposure (order counterbalanced). Tc was measured telemetrically from a sensor surgically implanted into the peritoneal cavity > 7 days before testing. Internal LED lighting maintained the accustomed day:night cycle (light cycle 0700 – 1900 h) during sessions lasting 45.5 hours. Rats entered the temperature gradient at 1100 h, and the 5-h N2O or control gas period did not start until 23 hours later to provide a long habituation / training period. Food and water were provided ad libitum at the center of the alleyway. The maximum decrease of mean Tc during N2O administration occurred at 0.9 h and was −2.05 ± 0.25°C; this differed significantly (p<0.0001) from the corresponding Tc change at 0.9 h during control gas administration (0.01 ± 0.14°C). The maximum decrease of mean selected ambient temperature during N2O administration occurred at 0.7 h and was −13.58 ± 1.61°C; this differed significantly (p < 0.0001) from the corresponding mean change in selected ambient temperature at 0.7 h during control gas administration (0.30 ± 1.49°C). N2O appears to induce a regulated hypothermia because the selection of a cool ambient temperature facilitates the reduction in Tc. The recovery of Tc during N2O administration (i.e., acute tolerance development) could have been facilitated by selection of ambient temperatures that were warmer than those chosen during control administrations, but interestingly, this did not occur. PMID:21184766

Magnetic studies of nickel hydride nanoparticles embedded in chitosan matrix

NASA Astrophysics Data System (ADS)

Araújo-Barbosa, S.; Morales, M. A.

2017-11-01

In this work we present a method to produce NiH (β-NiH phase) nanoparticles from Ni-Cu solid solution. The reduction of Ni2+ and Cu2+ occurred at high temperatures and in presence of glutaraldehyde, citric acid and chitosan biopolymer. The samples are mainly composed of Ni and NiH phases with particles sizes ranging from 9 to 27 nm. DC magnetization studies reveal the presence of hydrogen-poor nickel hydride phase (α-NiH phase) which enhances the saturation magnetization at temperatures below 50 K. Stability of samples stored in air after 8 months was verified, and thermal treatment at 350 oC in presence of air transformed the samples to Ni and Cu oxides. Furthermore, we present a discussion regarding the mechanism of Ni2+ and Cu2+ chemical reduction.

High latitude hydrological changes during the Eocene Thermal Maximum 2

NASA Astrophysics Data System (ADS)

Krishnan, Srinath; Pagani, Mark; Huber, Matthew; Sluijs, Appy

2014-10-01

The Eocene hyperthermals, including the Paleocene-Eocene Thermal Maximum (PETM) and Eocene Thermal Maximum 2 (ETM2), represent extreme global warming events ∼56 and 54 million years ago associated with rapid increases in atmospheric greenhouse gas concentrations. An initial study on PETM characteristics in the Arctic region argued for intensification of the hydrological cycle and a substantial increase in poleward moisture transport during global warming based on compound-specific carbon and hydrogen isotopic (2H/1H) records from sedimentary leaf-wax lipids. In this study, we apply this isotopic and hydrological approach on sediments deposited during ETM2 from the Lomonosov Ridge (Integrated Ocean Drilling Program Expedition 302). Our results show similar 2H/1H changes during ETM2 as during the PETM, with a period of 2H-enrichment (∼ 20 ‰) relative to ;pre-event; values just prior to the negative carbon isotope shift (CIE) that is often taken as the onset of the hyperthermal, and more negative lipid δ2H values (∼ - 15 ‰) during peak warming. Notably, lipid 2H-enrichment at the base of the event is coeval with colder TEX86H temperatures. If 2H/1H values of leaf waxes primarily reflect the hydrogen isotopic composition of precipitation, the observed local relationship between temperature and 2H/1H values for the body of ETM2 is precisely the opposite of what would be predicted using a simple Rayleigh isotope distillation model, assuming a meridional vapor trajectory and a reduction in equator-pole temperature gradients. Overall, a negative correlation exists between the average chain length of n-alkanes and 2H/1H suggesting that local changes in ecology could have impacted the hydrogen isotopic compositions of leaf waxes. The negative correlation falls across three separate intervals - the base of the event, the initial CIE, and during the H2 hyperthermal (of which the assignment is not fully certain). Three possible mechanisms potentially explain 2H-enriched signals at the base of the event, including (1) intense local drying and cooling leading to evaporative 2H-enrichment; (2) changes in frequency/intensity of storm events and its impact on high latitude amount effects; and (3) changes in low-latitude temperatures. Evidence for hydrological shifts at the base of both hyperthermals suggests that hydrological change or the factors promoting hydrological change played a role in triggering the release of greenhouse gases. Generation of similar high-resolution isotopic- and temperature records at other latitudes is crucial for understanding the causal links between temperature and hydrological changes and may help constrain the source and mechanism of carbon release that triggered the early Eocene hyperthermals.

Comparison of preparation methods for ceria catalyst and the effect of surface and bulk sulfates on its activity toward NH3-SCR.

PubMed

Chang, Huazhen; Ma, Lei; Yang, Shijian; Li, Junhua; Chen, Liang; Wang, Wei; Hao, Jiming

2013-11-15

A series of CeO2 catalysts prepared with sulfate (S) and nitrate (N) precursors by hydrothermal (H) and precipitation (P) methods were investigated in selective catalytic reduction of NOx by NH3 (NH3-SCR). The catalytic activity of CeO2 was significantly affected by the preparation methods and the precursor type. CeO2-SH, which was prepared by hydrothermal method with cerium (IV) sulfate as a precursor, showed excellent SCR activity and high N2 selectivity in the temperature range of 230-450 °C. Based on the results obtained by temperature-programmed reduction (H2-TPR), transmission infrared spectra (IR) and thermal gravimetric analysis (TGA), the excellent performance of CeO2-SH was correlated with the surface sulfate species formed in the hydrothermal reaction. These results indicated that sulfate species bind with Ce(4+) on the CeO2-SH catalyst, and the specific sulfate species, such as Ce(SO4)2 or CeOSO4, were formed. The adsorption of NH3 was promoted by these sulfate species, and the probability of immediate oxidation of NH3 to N2O on Ce(4+) was reduced. Accordingly, the selective oxidation of NH3 was enhanced, which contributed to the high N2 selectivity in the SCR reaction. However, the location of sulfate on the CeO2-SP catalyst was different. Plenty of sulfate species were likely deposited on CeO2-SP surface, covering the active sites for NO oxidation, which resulted in poor SCR activity in the test temperature range. Moreover, the resistance to alkali metals, such as Na and K, was improved over the CeO2-SH catalyst. Copyright © 2013 Elsevier B.V. All rights reserved.

Reduction of hexavalent chromium in water samples acidified for preservation

USGS Publications Warehouse

Stollenwerk, K.G.; Grove, D.B.

1985-01-01

Reduction of hexavalent chromium, Cr(VI), in water samples, preserved by standard techniques, was investigated. The standard preservation technique for water samples that are to be analyzed for Cr(VI) consists of filtration through a 0.45-??m membrane, acidification to a pH < 2, and storage in plastic bottles. Batch experiments were conducted to evaluate the effect of H+ concentration, NO2, temperature, and dissolved organic carbon (DOC) on the reduction of Cr(VI) to Cr(III). The rate of reduction of Cr(VI) to Cr(III) increased with increasing NO2, DOC, H+, and temperature. Reduction of Cr(VI) by organic matter occurred in some samples even though the samples were unacidified. Reduction of Cr(VI) is inhibited to an extent by storing the sample at 4??C. Stability of Cr(VI) in water is variable and depends on the other constituents present in the sample. Water samples collected for the determination of Cr(VI) should be filtered (0.45-??m membrane), refrigerated, and analyzed as quickly as possible. Water samples should not be acidified. Measurement of total Cr in addition to Cr(VI) can serve as a check for Cr(VI) reduction. If total Cr is greater than Cr(VI), the possibility that Cr(VI) reduction has occurred needs to be considered.The rate of reduction of Cr(VI) to Cr(III) increased with increasing NO//2, DOC, H** plus , and temperature. Reduction of Cr(VI) by organic matter occurred in some samples even though the samples were unacidified. Reduction of Cr(VI) is inhibited to an extent by storing the sample at 4 degree C. Stability of Cr(VI) in water is variable and depends on the other constituents present in the sample. Water samples collected for the determination of Cr(VI) should be filtered (0. 45- mu m membrane), refrigerated, and analyzed as quickly as possible. Water samples should not be acidified. Measurement of total Cr in addition to Cr(VI) can serve as a check for Cr(VI) reduction. If total Cr is greater than Cr(VI), the possibility that Cr(VI) reduction has occurred needs to be considered.

On the temperature-programmed reduction of Pt-Ir/. gamma. -Al/sub 2/O/sub 3/ catalysts

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wagstaff, N.; Prins, R.

1979-10-15

Temperature-programed reduction of a catalyst containing 0.37% Pt and 0.37% Ir on chlorided alumina and treated as previously described for a Pt-Re bimetallic catalyst showed a single reduction peak at 105/sup 0/C, almost exactly at the midpoint between the reduction peaks of the pure platimun and pure iridium peaks treated identically. This peak remained unaltered after fairly severe oxidation treatment (350/sup 0/C). The results indicated that the catalyst formed bimetallic clusters in the reduced state which were more stable than the Pt-Re clusters and did not segregate on oxidation.

Thermal treatment for pathogen inactivation as a risk mitigation strategy for safe recycling of organic waste in agriculture.

PubMed

Elving, Josefine; Vinnerås, Björn; Albihn, Ann; Ottoson, Jakob R

2014-01-01

Thermal treatment at temperatures between 46.0°C and 55.0°C was evaluated as a method for sanitization of organic waste, a temperature interval less commonly investigated but important in connection with biological treatment processes. Samples of dairy cow feces inoculated with Salmonella Senftenberg W775, Enterococcus faecalis, bacteriophage ϕX174, and porcine parvovirus (PPV) were thermally treated using block thermostats at set temperatures in order to determine time-temperature regimes to achieve sufficient bacterial and viral reduction, and to model the inactivation rate. Pasteurization at 70°C in saline solution was used as a comparison in terms of bacterial and viral reduction and was proven to be effective in rapidly reducing all organisms with the exception of PPV (decimal reduction time of 1.2 h). The results presented here can be used to construct time-temperature regimes in terms of bacterial inactivation, with D-values ranging from 0.37 h at 55°C to 22.5 h at 46.0°C and 0.45 h at 55.0°C to 14.5 h at 47.5°C for Salmonella Senftenberg W775 and Enterococcus faecalis, respectively and for relevant enteric viruses based on the ϕX174 phage with decimal reduction times ranging from 1.5 h at 55°C to 16.5 h at 46°C. Hence, the study implies that considerably lower treatment temperatures than 70°C can be used to reach a sufficient inactivation of bacterial pathogens and potential process indicator organisms such as the ϕX174 phage and raises the question whether PPV is a valuable process indicator organism considering its extreme thermotolerance.

Hepatitis A Virus Disinfection in Water by Solar Photo-Fenton Systems.

PubMed

Polo, David; García-Fernández, Irene; Fernández-Ibañez, Pilar; Romalde, Jesús L

2018-06-01

This study evaluates and compares the effectiveness of solar photo-Fenton systems for the inactivation of hepatitis A virus (HAV) in water. The effect of solar irradiance, dark- Fenton reaction and three different reactant concentrations (2.5/5, 5/10 and 10/20 mg/L of Fe 2+ /H 2 O 2 ) on the photo-Fenton process were tested in glass bottle reactors (200 mL) during 6 h under natural sunlight. Disinfection kinetics were determined both by RT-qPCR and infectivity assays. Mean water temperatures ranged from 25 to 27.3 °C, with a maximum local noon UV irradiances of 22.36 W/m 2 . Photo-Fenton systems yielded increased viral reduction rates in comparison with the isolated effect under the Fenton reaction in darkness (negligible viral reduction) or the solar radiation (0.25 Log of RNA reduction). With the highest concentration employed (10-20 mg/L Fe 2+ -H 2 O 2 ), an average RNA reduction rate of ~ 1.8 Log (initial concentration of 10 5 pfu/mL) and a reduction of 80% in the infectivity capacity were reached. Results showed a strong synergistic effect between Fe 2+ /H 2 O 2 and sunlight, demonstrating that significant disinfection rates of HAV under photo-Fenton systems may occur with relatively higher efficiency at middle environmental temperatures and without the need for an energy-intensive light source.

On the genesis of molybdenum carbide phases during reduction-carburization reactions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Guil-Lopez, R., E-mail: rut.guil@icp.csic.es; Nieto, E.; Departamento de Tecnologia Quimica y Energetica, ESCET, Universidad Rey Juan Carlos, C/Tulipan s/n, 28933-Mostoles

2012-06-15

Molybdenum carbide has been prepared according to the carbothermal reduction method. Carbon black substrate was used as C-source whereas a H{sub 2}-flow was the reducing agent. Two different H{sub 2} consumption steps were identified during the carburization treatment. The low temperature step is related to the reduction of Mo{sup 6+}-to-Mo{sup 4+}, the higher temperature process accounts for the deep reduction of Mo{sup 4+}-to-metal Mo{sup 0} and its subsequent reaction with C to form the Mo-carbide. The influences of the maximum carburization temperature, carburization time, gas hourly space velocity regarding Mo-loading, heating rate and temperature of Ar pre-treatment were analyzed. Allmore » these conditions are interrelated to each other. Thus, the carburization process ends at 700 Degree-Sign C when Mo-loading is 10 wt%, however Mo-loading higher than 10 wt% requires higher temperatures. Carburization temperatures up to 800 Degree-Sign C are needed to fulfill Mo-carbide formation with samples containing 50 wt% Mo. Nevertheless, Ar pre-treatment at 550 Degree-Sign C and slow heating rates favor the carburization, thus requiring lower carburization temperatures to reach the same carburization level. - Graphical Abstract: H{sub 2}-consumption profile (TPR) during the molybdenum carburization process, XRD patterns of the reduced Mo-samples after carburization and TEM-micrographs with two different enlargement of the samples with 5, 20 and 50 wt% Mo. Highlights: Black-Right-Pointing-Pointer Control of carburization variables: tailor the reduced/carbide Mo-phases (single/mixture). Black-Right-Pointing-Pointer Mo carburization in two stages: (1) Mo{sup 6+}-Mo{sup 4+}; (2) Mo{sup 4+}-Mo{sup 0} and, at once, MoC. Black-Right-Pointing-Pointer The carburization process is faster than Mo{sup 4+} reduction. Black-Right-Pointing-Pointer XPS probed: reduced Mo particles show core-shell structure. Black-Right-Pointing-Pointer Core: reduced Mo (Mo{sub 2}C, MoO{sub 2} and/or Mo{sup 0}); Shell: 2-3 nm of MoO{sub 3}.« less

Performance characterization of CNTs and γ-Al{sub 2}O{sub 3} supported cobalt catalysts in Fischer-Tropsch reaction

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ali, Sardar, E-mail: alikhan-635@yahoo.com; Zabidi, Noor Asmawati Mohd, E-mail: noorasmawati-mzabidi@petronas.com.my; Subbarao, Duvvuri, E-mail: duvvuri-subbarao@petronas.com.my

2014-10-24

Catalysts were prepared via a wet impregnation method. Different physicochemical properties of the samples were revealed by transmission electron microscope (TEM), temperature programmed reduction (H{sub 2}-TPR) and carbon dioxide desorption (CO{sub 2}-desorption). Fischer-Tropsch reaction (FTS) was carried out in a fixed-bed microreactor at 220°C and 1 atm, with H{sub 2}/CO = 2v/v and space velocity, SV of 12L/g.h for 5 h. Various characterization techniques revealed that there was a stronger interaction between Co and Al{sub 2}O{sub 3} support compared to that of CNTs support. CNTs support increased the reducibility and decreased Co particle size. A significant increase in % CO conversion andmore » FTS reaction rate was observed over CNTs support compared to that of Co/Al{sub 2}O{sub 3}. Co/CNTs resulted in higher C{sub 5+} hydrocarbons selectivity compared to that of Co/Al{sub 2}O{sub 3} catalyst. CNTs are a better support for Co compared to Al{sub 2}O{sub 3}.« less

Stabilization of Co{sup 2+} in layered double hydroxides (LDHs) by microwave-assisted ageing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Herrero, M.; Benito, P.; Labajos, F.M.

2007-03-15

Co-containing layered double hydroxides at different pH have been prepared, and aged following different routes. The solids prepared have been characterized by element chemical analysis, powder X-ray diffraction, thermogravimetric and differential thermal analyses (both in nitrogen and in oxygen), FT-IR and Vis-UV spectroscopies, temperature-programmed reduction and surface area assessment by nitrogen adsorption at -196 deg. C. The best conditions found to preserve the cobalt species in the divalent oxidation state are preparing the samples at controlled pH, and then submit them to ageing under microwave irradiation. - Graphical abstract: The use of microwave-hydrothermal treatment, controlling both temperature and ageing time,more » permits to synthesize well-crystallized nanomaterials with controlled surface properties. An enhancement in the crystallinity degree and an increase in the particle size are observed when the irradiation time is prolonged.« less

Influence of moisture content and temperature on degree of carbonation and the effect on Cu and Cr leaching from incineration bottom ash.

PubMed

Lin, Wenlin Yvonne; Heng, Kim Soon; Sun, Xiaolong; Wang, Jing-Yuan

2015-09-01

This study investigated the influence of moisture content and temperature on the degree of carbonation of municipal solid waste (MSW) incineration bottom ash (IBA) from two different incineration plants in Singapore. The initial rate of carbonation was affected by the nominal moisture content used. Carbonation temperature seemed to play a part in changing the actual moisture content of IBA during carbonation, which in turn affected the degree of carbonation. Results showed that 2h of carbonation was sufficient for the samples to reach a relatively high degree of carbonation that was close to the degree of carbonation observed after 1week of carbonation. Both Cu and Cr leaching also showed significant reduction after only 2h of carbonation. Therefore, the optimum moisture content and temperature were selected based on 2h of carbonation. The optimum moisture content was 15% for both incineration plants while the optimum temperature was different for the two incineration plants, at 35°C and 50°C. The effect on Cu and Cr leaching from IBA after accelerated carbonation was evaluated as a function of carbonation time. Correlation coefficient, Pearson's R, was used to determine the dominant leaching mechanism. The reduction in Cu leaching was found to be contributed by both formation of carbonate mineral and reduction of DOC leaching. On the other hand, Cr leaching seemed to be dominantly controlled by pH. Copyright © 2015 Elsevier Ltd. All rights reserved.

Hard templating ultrathin polycrystalline hematite nanosheets: effect of nano-dimension on CO2 to CO conversion via the reverse water-gas shift reaction.

PubMed

Fishman, Zachary S; He, Yulian; Yang, Ke R; Lounsbury, Amanda W; Zhu, Junqing; Tran, Thanh Minh; Zimmerman, Julie B; Batista, Victor S; Pfefferle, Lisa D

2017-09-14

Understanding how nano-dimensionality impacts iron oxide based catalysis is central to a wide range of applications. Here, we focus on hematite nanosheets, nanowires and nanoparticles as applied to catalyze the reverse water gas shift (RWGS) probe reaction. We introduce a novel approach to synthesize ultrathin (4-7 nm) hematite nanosheets using copper oxide nanosheets as a hard template and propose a reaction mechanism based on density functional theory (DFT) calculations. Hematite nanowires and nanoparticles were also synthesized and characterized. H 2 temperature programmed reduction (H 2 -TPR) and RWGS reactions were performed to glean insights into the mechanism of CO 2 conversion to CO over the iron oxide nanomaterials and were compared to H 2 binding energy calculations based on density functional theory. While the nanosheets did exhibit high CO 2 conversion, 28% at 510 °C, we found that the iron oxide nanowires had the highest CO 2 conversion, reaching 50% at 750 °C under atmospheric pressure. No products besides CO and H 2 O were detected.

(18)O(2) label mechanism of sulfur generation and characterization in properties over mesoporous Sm-based sorbents for hot coal gas desulfurization.

PubMed

Liu, B S; Wan, Z Y; Wang, F; Zhan, Y P; Tian, M; Cheung, A S C

2014-02-28

Using a sol-gel method, SmMeOx/MCM-41 or SBA-15 (Me=Fe, Co and Zn) and corresponding unsupported sorbents were prepared. The desulfurization performance of these sorbents was evaluated over a fixed-bed reactor and the effects of reaction temperature, feed and sorbent composition on desulfurization performance were studied. Samarium-based sorbents used to remove H2S from hot coal gas were reported for the first time. The results of successive sulfidation/regeneration cycles revealed that SmFeO3/SBA-15 sorbent was suitable for desulfurization of hot coal gas in the chemical industry. The formation of elemental sulfur during both sulfidation and regeneration processes depended strongly on the catalytic action of Sm2O2S species, which was confirmed for the first time via high sensitive time of flight mass spectrometer (TOF-MS) using 6%vol(18)O2/Ar regeneration gas and can reduce markedly procedural complexity. The sorbents were characterized using N2-adsorption, high-resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD), temperature-programmed reduction of H2 (H2-TPR), thermogravimetry (TG) and time-of-flight mass spectrometry (TOF-MS) techniques. Copyright © 2014 Elsevier B.V. All rights reserved.

Extremely low-outgassing material: 0.2% beryllium copper alloy

NASA Astrophysics Data System (ADS)

Watanabe, Fumio

2004-01-01

Exploration for low-outgassing materials for use in ultrahigh vacuum and extreme high-vacuum systems is one of the most important topics of a vacuum researcher. We have found that a copper alloy containing 0.2% beryllium (0.2% BeCu) can attain an extremely low hydrogen outgassing rate of 10-14 Pa (H2) m/s order. Almost the entire surface of 0.2% BeCu is dominated by a BeO layer, after a 400 °C×72 h prebakeout treatment in an ultrahigh vacuum. This layer functions as a barrier to the processes of oxidization and permeation of hydrogen. In addition, this layer resists carbon contamination. Temperature-programmed desorption spectra show only a single peak for water at 150 °C and small quantities of any other desorption gases. Therefore, an in situ bakeout process in which the temperature simply ramps up to 150 °C and immediately ramps back down is enough for degassing; it does not require an ordinary sustained-temperature bakeout. Using an outgassing sample consisting of 0.2% BeCu disks housed in a 0.2% BeCu nipple chamber, a lowest outgassing rate of the 5.6×10-14 Pa (H2) m/s was measured by the pressure-rise method after pump cutoff. The pressure-rise versus time curve was completely nonlinear. It rises over time to a constant slope of 1/2 in a log-log plot, due to hydrogen diffusion from the bulk, but this requires over a week at room temperature. The hydrogen outgassing from the 0.2% BeCu bulk is completely dominated by a diffusion-limited mechanism. This article will describe why we obtain such low-outgassing rates with 0.2% BeCu. It is based on the observed surface changes with prebakeout treatment seen by x-ray photoelectron spectroscopy, and the improvement of hydrogen outgassing measurements by the pressure-rise method. A comparison is made to ordinary stainless steel. In addition, the concept of an outgassing reduction method will be discussed from a review of the published ultralow-outgassing data and reduction methods. .

Catalytic N 2O decomposition and reduction by NH 3 over Fe/Beta and Fe/SSZ-13 catalysts

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Aiyong; Wang, Yilin; Walter, Eric D.

Fe/zeolites are important N 2O abatement catalysts, efficient in direct N 2O decomposition and (selective) catalytic N 2O reduction. In this study, Fe/Beta and Fe/SSZ-13 were synthesized via solution ion-exchange and used to catalyze these two reactions. Nature of the Fe species was probed with UV-vis, Mössbauer and EPR spectroscopies and H2-TPR. The characterizations collectively indicate that isolated and dinuclear Fe sites dominate in Fe/SSZ-13, whereas Fe/Beta contains higher concentrations of oligomeric Fe xO y species. H 2-TPR results suggest that Fe-O interactions are weaker in Fe/SSZ-13, as evidenced by the lower reduction temperatures and higher extents of autoreduction duringmore » high-temperature pretreatments in inert gas. Kinetic measurements show that Fe/SSZ-13 has higher activity in catalytic N 2O decomposition, thus demonstrating a positive correlation between activity and Fe-O binding, consistent with O 2 desorption being rate-limiting for this reaction. However, Fe/Beta was found to be more active in catalyzing N 2O reduction by NH 3. This indicates that larger active ensembles (i.e., oligomers) are more active for this reaction, consistent with the fact that both N 2O and NH 3 need to be activated in this case. The authors from PNNL gratefully acknowledge the US Department of Energy (DOE), Energy Efficiency and Renewable Energy, Vehicle Technologies Office for the support of this work. The research described in this paper was performed in the Environmental Molecular Sciences Laboratory (EMSL), a national scientific user facility sponsored by the DOE’s Office of Biological and Environmental Research and located at Pacific Northwest National Laboratory (PNNL). PNNL is operated for the US DOE by Battelle. Aiyong Wang gratefully acknowledges the China Scholarship Council for the Joint-Training Scholarship Program with the Pacific Northwest National Laboratory (PNNL). The authors from East China University of Science and Technology acknowledge National Basic Research Program of China (2013CB933200), National Natural Science Foundation of China (21577035, 21577034), Commission of Science and Technology of Shanghai Municipality (15DZ1205305) and 111 Project (B08021) for supports.« less

Rate Controlling Step in the Reduction of Iron Oxides; Kinetics and Mechanism of Wüstite-Iron Step in H2, CO and H2/CO Gas Mixtures

NASA Astrophysics Data System (ADS)

El-Geassy, Abdel-Hady A.

2017-09-01

Wüstite (W1 and W2) micropellets (150-50 μm) were prepared from the reduction of pure Fe2O3 and 2.1% SiO2-doped Fe2O3 in 40%CO/CO2 gas mixture at 1000°C which were then isothermally reduced in H2, CO and H2/CO gas mixtures at 900-1100°C. The reduction reactions was followed by Thermogravimetric Analysis (TG) technique. The effect of gas composition, gas pressure and temperature on the rate of reduction was investigated. The different phases formed during the reduction were chemically and physically characterized. In SiO2-doped wüstite, fayalite (Fe2SiO3) was identified. At the initial reduction stages, the highest rate was obtained in H2 and the lowest was in CO gas. In H2/CO gas mixtures, the measured rate did not follow a simple additive equation. The addition of 5% H2 to CO led to a measurable increase in the rate of reduction compared with that in pure CO. Incubation periods were observed at the early reduction stages of W1 in CO at lower gas pressure (<0.25 atm). In SiO2-doped wüstite, reaction rate minimum was detected in H2 and H2-rich gas mixtures at 925-950°C. The influence of addition of H2 to CO or CO to H2 on the reduction reactions, nucleation and grain growth of iron was intensively studied. Unlike in pure wüstite, the presence of fayalite enhances the reduction reactions with CO and CO-rich gas mixtures. The chemical reaction equations of pure wüstite with CO are given showing the formation of carbonyl-like compound [Fem(CO2)n]*. The apparent activation energy values, at the initial stages, ranged from 53.75 to 133.97 kJ/mole indicating different reaction mechanism although the reduction was designed to proceed by the interfacial chemical reaction.

Shape-Dependent Activity of Ceria for Hydrogen Electro-Oxidation in Reduced-Temperature Solid Oxide Fuel Cells.

PubMed

Tong, Xiaofeng; Luo, Ting; Meng, Xie; Wu, Hao; Li, Junliang; Liu, Xuejiao; Ji, Xiaona; Wang, Jianqiang; Chen, Chusheng; Zhan, Zhongliang

2015-11-04

Single crystalline ceria nanooctahedra, nanocubes, and nanorods are hydrothermally synthesized, colloidally impregnated into the porous La0.9Sr0.1Ga0.8Mg0.2O3-δ (LSGM) scaffolds, and electrochemically evaluated as the anode catalysts for reduced temperature solid oxide fuel cells (SOFCs). Well-defined surface terminations are confirmed by the high-resolution transmission electron microscopy--(111) for nanooctahedra, (100) for nanocubes, and both (110) and (100) for nanorods. Temperature-programmed reduction in H2 shows the highest reducibility for nanorods, followed sequentially by nanocubes and nanooctahedra. Measurements of the anode polarization resistances and the fuel cell power densities reveal different orders of activity of ceria nanocrystals at high and low temperatures for hydrogen electro-oxidation, i.e., nanorods > nanocubes > nanooctahedra at T ≤ 450 °C and nanooctahedra > nanorods > nanocubes at T ≥ 500 °C. Such shape-dependent activities of these ceria nanocrystals have been correlated to their difference in the local structure distortions and thus in the reducibility. These findings will open up a new strategy for design of advanced catalysts for reduced-temperature SOFCs by elaborately engineering the shape of nanocrystals and thus selectively exposing the crystal facets. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

NH3-SCR denitration catalyst performance over vanadium-titanium with the addition of Ce and Sb.

PubMed

Xu, Chi; Liu, Jian; Zhao, Zhen; Yu, Fei; Cheng, Kai; Wei, Yuechang; Duan, Aijun; Jiang, Guiyuan

2015-05-01

Selective catalytic reduction technology using NH3 as a reducing agent (NH3-SCR) is an effective control method to remove nitrogen oxides. TiO2-supported vanadium oxide catalysts with different levels of Ce and Sb modification were prepared by an impregnation method and were characterized by X-ray diffractometer (XRD), Brunauer-Emmett-Teller (BET), Transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FT-IR), UV-Vis diffuse reflectance spectroscopy (UV-Vis DRS), Raman and Hydrogen temperature-programmed reduction (H2-TPR). The catalytic activities of V5CexSby/TiO2 catalysts for denitration were investigated in a fixed bed flow microreactor. The results showed that cerium, vanadium and antimony oxide as the active components were well dispersed on TiO2, and the catalysts exhibited a large number of d-d electronic transitions, which were helpful to strengthen SCR reactivity. The V5CexSby/TiO2 catalysts exhibited a good low temperature NH3-SCR catalytic activity. In the temperature range of 210 to 400°C, the V5CexSby/TiO2 catalysts gave NO conversion rates above 90%. For the best V5Ce35Sb2/TiO2 catalyst, at a reaction temperature of 210°C, the NO conversion rate had already reached 90%. The catalysts had different catalytic activity with different Ce loadings. With the increase of Ce loading, the NO conversion rate also increased. Copyright © 2015. Published by Elsevier B.V.

The vanadium nitrogenase of Azotobacter chroococcum. Reduction of acetylene and ethylene to ethane.

PubMed Central

Dilworth, M J; Eady, R R; Eldridge, M E

1988-01-01

1. The vanadium (V-) nitrogenase of Azobacter chroococcum transfers up to 7.4% of the electrons used in acetylene (C2H2) reduction for the formation of ethane (C2H6). The apparent Km for C2H2 (6 kPa) is the same for either ethylene (C2H4) or ethane (C2H6) formation and much higher than the reported Km values for C2H2 reduction to C2H4 by molybdenum (Mo-) nitrogenases. Reduction of C2H2 in 2H2O yields predominantly [cis-2H2]ethylene. 2. The ratio of electron flux yielding C2H6 to that yielding C2H4 (the C2H6/C2H4 ratio) is increased by raising the ratio of Fe protein to VFe protein and by increasing the assay temperature up to at least 40 degrees C. pH values above 7.5 decrease the C2H6/C2H4 ratio. 3. C2H4 and C2H6 formation from C2H2 by V-nitrogenase are not inhibited by H2. CO inhibits both processes much less strongly than it inhibits C2H4 formation from C2H2 with Mo-nitrogenase. 4. Although V-nitrogenase also catalyses the slow CO-sensitive reduction of C2H4 to C2H6, free C2H4 is not an intermediate in C2H6 formation from C2H2. 5. Propyne (CH3C identical to CH) is not reduced by the V-nitrogenase. 6. Some implications of these results for the mechanism of C2H6 formation by the V-nitrogenase are discussed. PMID:3162672

Influence of temperature and organic load on chemical disinfection of Geobacillus steareothermophilus spores, a surrogate for Bacillus anthracis

PubMed Central

Guan, Jiewen; Chan, Maria; Brooks, Brian W.; Rohonczy, Liz

2013-01-01

This study evaluated the influence of temperature and organic load on the effectiveness of domestic bleach (DB), Surface Decontamination Foam (SDF), and Virkon in inactivating Geobacillus stearothermophilus spores, which are a surrogate for Bacillus anthracis spores. The spores were suspended in light or heavy organic preparations and the suspension was applied to stainless steel carrier disks. The dried spore inoculum was covered with the disinfectants and the disks were then incubated at various temperatures. At −20°C, the 3 disinfectants caused less than a 2.0 log10 reduction of spores in both organic preparations during a 24-h test period. At 4°C, the DB caused a 4.4 log10 reduction of spores in light organic preparations within 2 h, which was about 3 log10 higher than what was achieved with SDF or Virkon. In heavy organic preparations, after 24 h at 4°C the SDF had reduced the spore count by 4.5 log10, which was about 2 log10 higher than for DB or Virkon. In general, the disinfectants were most effective at 23°C but a 24-h contact time was required for SDF and Virkon to reduce spore counts in both organic preparations by at least 5.5 log10. Comparable disinfecting activity with DB only occurred with the light organic load. In summary, at temperatures as low as 4°C, DB was the most effective disinfectant, inactivating spores within 2 h on surfaces with a light organic load, whereas SDF produced the greatest reduction of spores within 24 h on surfaces with a heavy organic load. PMID:24082400

Temperature Independent Catalytic Two-Electron Reduction of Dioxygen by Ferrocenes with a Tris[2-(2-pyridyl)ethyl]amine-Copper(II) Catalyst in the Presence of Perchloric Acid

PubMed Central

Das, Dipanwita; Lee, Yong-Min; Ohkubo, Kei; Nam, Wonwoo; Karlin, Kenneth D.; Fukuzumi, Shunichi

2013-01-01

Selective two-electron plus two-proton (2e−/2H+) reduction of O2 to hydrogen peroxide by ferrocene (Fc) or 1,1′-dimethylferrocene (Me2Fc) in the presence of perchloric acid is catalyzed efficiently by a mononuclear copper(II) complex, [CuII(tepa)]2+ {tepa = tris[2-(2-pyridyl)ethyl]amine} (1) in acetone. The E1/2 value for [CuII(tepa)]2+ as measured by cyclic voltammetry is 0.07 V vs Fc/Fc+ in acetone, being significantly positive, which makes it possible to use relatively weak one-electron reductants such as Fc and Me2Fc for the overall two-electron reduction of O2. Fast electron transfer from Fc or Me2Fc to 1 affords the corresponding CuI complex, [CuI(tepa)]+ (2), which reacts at low temperature (193 K) with O2, however only in presence of HClO4 to afford the hydroperoxo complex, [CuII(tepa)(OOH)]2+ (3). The detailed kinetic study on the homogeneous catalytic system reveals the rate-determining step to be the O2-binding process in the presence of HClO4 at lower temperature as well as at room temperature. The O2-binding kinetics in the presence of HClO4 were studied, demonstrating that the rate of formation of the hydroperoxo complex (3) as well as the overall catalytic reaction remained virtually the same with changing temperature. The apparent lack of an activation energy for the catalytic two-electron reduction of O2 is shown to result from the existence of a pre-equilibrium between 2 and O2 prior to the formation of the hydroperoxo complex 3. No further reduction of [CuII(tepa)(OOH)]2+ (3) by Fc or Me2Fc occurred, and instead 3 is protonated by HClO4 to yield H2O2 accompanied by regeneration of 1, thus completing the catalytic cycle for the two-electron reduction of O2 by Fc or Me2Fc. PMID:23394287

Catalyst evaluation for high-purity H2 production by sorption-enhanced steam-methane reforming coupled to a Ca/Cu process

NASA Astrophysics Data System (ADS)

Navarro, M. V.; López, J. M.; García, T.; Grasa, G.; Murillo, R.

2017-09-01

The operational limits of a commercial nickel-based catalyst under the conditions of a sorption-enhanced steam-methane reforming process coupled to a Ca/Cu chemical loop are investigated for high-purity H2 production in a cyclic operation. The performance of the reforming catalyst is tested by means of a high number of oxidation-reduction-reforming cycles. After 100 oxidation-reduction cycles, this catalyst retains its exceptional reforming activity. The methane conversion values are close to the thermodynamic equilibrium under very demanding conditions: temperature between 500 °C - 700 °C and mass hourly space velocity of 8.8 kgCH4 h-1 kgcat-1. After 200 cycles, the sample shows reduction in its reforming activity in line with a lower dispersion of the Ni species. Sintering of Ni nanocrystals is evidenced during the oxidation-reduction multi-cycles. The performance of the catalyst after 200 oxidation-reduction cycles mixed with a CaO-based CO2 sorbent is studied under optimal conditions calculated for the sorption-enhanced reforming process coupled to a Ca/Cu cycle (temperature of 650 °C, steam/methane ratio of 4, sorbent/catalyst ratio of 4 and space velocity of 0.75 kgCH4 h-1 kgcat-1). Remarkably, an equilibrium value over 92 vol.% H2 concentration is achieved, highlighting this catalyst as a promising candidate for the next steps of the process development.

Effects of sulfation level on the desulfation behavior of pre-sulfated Pt BaO/Al2O3 lean NOx trap catalysts: a combined H2 Temperature-Programmed Reaction, in-situ sulfur K-edge X-ray Absorption Near-Edge Spectroscopy, X-ray Photoelectron Spectroscopy, and Time-Resolved X-ray Diffraction Study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Do Heui; Szanyi, Janos; Kwak, Ja Hun

2009-04-03

Desulfation by hydrogen of pre-sulfated Pt(2wt%) BaO(20wt%)/Al2O3 with various sulfur loading (S/Ba = 0.12, 0.31 and 0.62) were investigated by combining H2 temperature programmed reaction (TPRX), x-ray photoelectron spectroscopy (XPS), in-situ sulfur K-edge x-ray absorption near-edge spectroscopy (XANES), and synchrotron time-resolved x-ray diffraction (TR-XRD) techniques. We find that the amount of H2S desorbed during the desulfation in the H2 TPRX experiments is not proportional to the amount of initial sulfur loading. The results of both in-situ sulfur K-edge XANES and TR-XRD show that at low sulfur loadings, sulfates were transformed to a BaS phase and remained in the catalyst, rathermore » than being removed as H2S. On the other hand, when the deposited sulfur level exceeded a certain threshold (at least S/Ba = 0.31) sulfates were reduced to form H2S, and the relative amount of the residual sulfide species in the catalyst was much less than at low sulfur loading. Unlike samples with high sulfur loading (e.g., S/Ba = 0.62), H2O did not promote the desulfation for the sample with S/Ba of 0.12, implying that the formed BaS species originating from the reduction of sulfates at low sulfur loading are more stable to hydrolysis. The results of this combined spectroscopy investigation provide clear evidence to show that sulfates at low sulfur loadings are less likely to be removed as H2S and have a greater tendency to be transformed to BaS on the material, leading to the conclusion that desulfation behavior of Pt BaO/Al2O3 lean NOx trap catalysts is markedly dependent on the sulfation levels.« less

Effects of Sulfation Level on the Desulfation Behavior of Presulfated Pt-BaO/Al2O3 Lean NOx Trap Catalysts: A Combined H2 Temperature-Programmed Reaction, in Situ Sulfur K-Edge X-ray Absorption Near-Edge Spectroscopy, X-ray Photoelectron Spectroscopy, and Time-Resolved X-ray Diffraction Study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, D.H.; Hanson, J.; Szanyi, J.

2009-04-30

Desulfation by hydrogen of presulfated Pt (2 wt %)-BaO(20 wt %)/Al{sub 2}O{sub 3} with various sulfur loading (S/Ba = 0.12, 0.31, and 0.62) were investigated by combining H{sub 2} temperature programmed reaction (TPRX), X-ray photoelectron spectroscopy (XPS), in situ sulfur K-edge X-ray absorption near-edge spectroscopy (XANES), and synchrotron time-resolved X-ray diffraction (TR-XRD) techniques. We find that the amount of H{sub 2}S desorbed during the desulfation in the H{sub 2} TPRX experiments is not proportional to the amount of initial sulfur loading. The results of both in situ sulfur K-edge XANES and TR-XRD show that at low sulfur loadings, sulfates weremore » transformed to a BaS phase and remained in the catalyst rather than being removed as H{sub 2}S. On the other hand, when the deposited sulfur level exceeded a certain threshold (at least S/Ba = 0.31) sulfates were reduced to form H{sub 2}S, and the relative amount of the residual sulfide species in the catalyst was much less than at low sulfur loading. Unlike samples with high sulfur loading (e.g., S/Ba = 0.62), H{sub 2}O did not promote the desulfation for the sample with S/Ba of 0.12, implying that the formed BaS species originating from the reduction of sulfates at low sulfur loading are more stable to hydrolysis. The results of this combined spectroscopy investigation provide clear evidence to show that sulfates at low sulfur loadings are less likely to be removed as H{sub 2}S and have a greater tendency to be transformed to BaS on the material, leading to the conclusion that desulfation behavior of Pt-BaO/Al{sub 2}O{sub 3} lean NO{sub x} trap catalysts is markedly dependent on the sulfation levels.« less

Alloy formation and metal oxide segregation on Pt-Re/. gamma. -Al/sub 2/O/sub 3/ catalysts as investigated by temperature-programmed reduction

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wagstaff, N.; Prins, R.

1979-10-15

Catalysts resembling reforming catalysts were prepared to contain finely dispersed 0.75% Pt, 0.7% Re, or 0.35% Pt plus 0.1-2% Re on chlorided ..gamma..-alumina. The catalysts were dried in an oxidizing atmosphere and studied by temperature-programed reduction. Up to a Re/Pt ratio of 0.6:1 the metals were completely reduced in hydrogen below 255/sup 0/C, i.e., the platinum catalyzed rhenium reduction. A small amount of added water (< 50 ppm) also promoted rhenium reduction. Segregation of the metals occurred in oxygen above 200/sup 0/C, but at 100/sup 0/C, the rate of segregation was slow. These results suggested that under reforming conditions, Pt-Remore » catalysts are completely reduced bimetallic clusters. The mechanisms of reduction, cluster formation, and oxidative segregation are discussed.« less

The influence of metal-support interactions on the accurate determination of Ru dispersion for Ru/TiO{sub 2}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Komaya, Takashi; Bell, A.T.; Weng-Sieh, Zara

1994-09-01

Titania-supported Ru catalysts have been characterized by TEM, {sup 1}H NMR, and H{sub 2} chemisorption to determine the metal particle size, the fraction of the metal surface available for H{sub 2} chemisorption, and the H{sub 2} adsorption capacity of the catalyst, as functions of the reduction temperature. TEM micrographs show that as the reduction temperature rises from 573 to 773K, the average particle size of Ru remains the same but the surface of the particles is covered to an increasing extent by an amorphous layer of titania. Quantitative estimates of the fraction of the Ru particle surface available for H{submore » 2} chemisorption were obtained by {sup 1}H NMR. The NMR spectra also show that a fraction of the adsorbed H{sub 2} spills over onto the support and that as a consequence measurements of total H{sub 2} chemisorption overestimate the number of Ru sites available for H{sub 2} adsorption. The implications of these results for the correct calculation of Ru dispersion and the determination of turnover frequencies for reactions carried out over Ru/TiO{sub 2} are discussed. 16 refs., 5 figs., 1 tab.« less

Ammonia Formation by the Reduction of Nitrite/Nitrate by FeS: Ammonia Formation Under Acidic Conditions

NASA Technical Reports Server (NTRS)

Summers, David P.; DeVincenzi, Donald (Technical Monitor)

2000-01-01

FeS reduces nitrite to, ammonia at pHs lower than the corresponding reduction by aqueous Fe+2. The reduction follows a reasonable first order decay, in nitrite concentration, with a half life of about 150 min (room temperature, CO2, pH 6.25). The highest ammonia product yield measured was 53%. Under CO2, the product yield decreases from pH 5.0 to pH 6.9. The increasing concentration of bicarbonate at higher pH interferes with the reaction. Bicarbonate interference is shown by comparing runs under N2 and CO2. The reaction proceeds well in the presence of such species as chloride, sulfate, and phosphate though the yield drops significantly with phosphate. FeS also reduces nitrate and, unlike with Fe+2, the reduction shows more reproducibility. Again, the product yield decreases with increasing pH, from 7% at pH 4.7 to 0% at pH 6.9. It appears as if nitrate is much more sensitive to the presence of added species, perhaps not competing as well for binding sites on the FeS surface. This may be the cause of the lack of reproducibility of nitrate reduction by Fe+2 (which also can be sensitive to binding by certain species).

In-Vessel Composting of Simulated Long-Term Missions Space-Related Solid Wastes

NASA Technical Reports Server (NTRS)

Rodriguez-Carias, Abner A.; Sager, John; Krumins, Valdis; Strayer, Richard; Hummerick, Mary; Roberts, Michael S.

2002-01-01

Reduction and stabilization of solid wastes generated during space missions is a major concern for the Advanced Life Support - Resource Recovery program at the NASA, Kennedy Space Center. Solid wastes provide substrates for pathogen proliferation, produce strong odor, and increase storage requirements during space missions. A five periods experiment was conducted to evaluate the Space Operation Bioconverter (SOB), an in vessel composting system, as a biological processing technology to reduce and stabilize simulated long-term missions space related solid-wastes (SRSW). For all periods, SRSW were sorted into components with fast (FBD) and slow (SBD) biodegradability. Uneaten food and plastic were used as a major FBD and SBD components, respectively. Compost temperature (C), CO2 production (%), mass reduction (%), and final pH were utilized as criteria to determine compost quality. In period 1, SOB was loaded with a 55% FBD: 45% SBD mixture and was allowed to compost for 7 days. An eleven day second composting period was conducted loading the SOB with 45% pre-composted SRSW and 55% FBD. Period 3 and 4 evaluated the use of styrofoam as a bulking agent and the substitution of regular by degradable plastic on the composting characteristics of SRSW, respectively. The use of ceramic as a bulking agent and the relationship between initial FBD mass and heat production was investigated in period 5. Composting SRSW resulted in an acidic fermentation with a minor increase in compost temperature, low CO2 production, and slightly mass reduction. Addition of styrofoam as a bulking agent and substitution of regular by biodegradable plastic improved the composting characteristics of SRSW, as evidenced by higher pH, CO2 production, compost temperature and mass reduction. Ceramic as a bulking agent and increase the initial FBD mass (4.4 kg) did not improve the composting process. In summary, the SOB is a potential biological technology for reduction and stabilization of mission space-related solid wastes. However, the success of the composting process may depend of the physical characteristics (particle size, porosity, structure, texture) of the SBD components which would require pre-processing of solid wastes before placing them in the SOB.

Alloy formation and metal oxide segregation in Pt-Re/. gamma. -Al/sub 2/O/sub 3/ catalysts as investigated by temperature-programmed reduction

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wagstaff, N.; Prins, R.

1979-10-15

Temperature-programmed reduction has been used to characterize the finely dispersed metal compounds in a series of Pt-Re/..gamma..-Al/sub 2/O/sub 3/ catalysts. Strong evidence has been obtained that zerovalent Pt and Re atoms are in intimate contact with each other after catalyst reduction. The formation of bimetallic clusters supports the alloy explanation for the improved performance of this type of bimetallic reforming catalyst. Treatment of the reduced catalysts with oxygen above about 200/sup 0/C causes segregation of platinum and rhenium oxides. Adsorption of oxygen at temperatures up to 100/sup 0/C leaves the bimetallic clusters largely intact, but subsequent high-temperature treatment in themore » absence of extra oxygen leads to segregation of Pt and Re species. This suggests that in the presence of adsorbed oxygen the Pt-Re clusters are thermodynamically unstable, but that under mild conditions the rate of segregation is slow. 10 figures, 4 tables.« less

Effect of phage and host concentration on the inactivation of Escherichia coli O157:H7 on cooked and raw beef.

PubMed

Hudson, J A; Billington, C; Wilson, T; On, S L W

2015-03-01

A previously described phage infecting Escherichia coli O157:H7 was added to raw and cooked beef pieces at concentrations ranging from 10(1)-10(8) plaque forming units/cm(2) to either low (<100 CFU/cm(2)) or high (10(4) CFU/cm(2)) concentrations of host bacterial cells. Incubation for up to 24 h was performed at 5 ℃ and 24 ℃ to simulate refrigerated and room temperature storage/temperature abuse. Surviving bacteria were enumerated during the incubation period, with phages being counted at the first and last sampling times. Significant reductions of E. coli O157:H7 of the order of >4 log10 CFU/cm(2) at both temperatures could be achieved compared to phage-free controls. There was a trend for greater inactivation to occur with increasing phage concentration. While re-growth of surviving cells occurred in nearly all samples incubated for 24 h at 24 ℃, these conditions are not typical of those experienced by perishable foods. It was concluded that phages can be used to reduce the concentration of a bacterial pathogen on meat, but the concentration of phages needs to be high (>4-5 log10 plaque forming units/cm(2)) for reductions to occur. A concentration of the order 8 log10 plaque forming units/cm(2) was needed to achieve a 4 log10 CFU/cm(2) reduction. © The Author(s) 2013 Reprints and permissions: sagepub.co.uk/journalsPermissions.nav.

Bimetallic iron and cobalt incorporated MFI/MCM-41 composite and its catalytic properties

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Baoshan, E-mail: bsli@mail.buct.edu.cn; Xu, Junqing; Li, Xiao

2012-05-15

Graphical abstract: The formation of FeCo-MFI/MCM-41 composite is based on two steps, the first step of synthesizing the MFI-type proto-zeolite unites under hydrothermal conditions. The second step of assembling these zeolite fragment together new silica and heteroatom source on the CTAB surfactant micelle to synthesize the mesoporous product with hexagonal structure. Highlights: Black-Right-Pointing-Pointer Bimetallic iron and cobalt incorporated MFI/MCM-41 composite was prepared using templating method. Black-Right-Pointing-Pointer FeCo-MFI/MCM-41 composite simultaneously possessed two kinds of meso- and micro-porous structures. Black-Right-Pointing-Pointer Iron and cobalt ions incorporated into the silica framework with tetrahedral coordination. -- Abstract: The MFI/MCM-41 composite material with bimetallic Fe andmore » Co incorporation was prepared using templating method via a two-step hydrothermal crystallization procedure. The obtained products were characterized by a series of techniques including powder X-ray diffraction, N{sub 2} sorption, transmission electron microscopy, scanning electron microscope, H{sub 2} temperature programmed reduction, thermal analyses, and X-ray absorption fine structure spectroscopy of the Fe and Co K-edge. The catalytic properties of the products were investigated by residual oil hydrocracking reactions. Characterization results showed that the FeCo-MFI/MCM-41 composite simultaneously possessed two kinds of stable meso- and micro-porous structures. Iron and cobalt ions were incorporated into the silicon framework, which was confirmed by H{sub 2} temperature programmed reduction and X-ray absorption fine structure spectroscopy. This composite presented excellent activities in hydrocracking of residual oil, which was superior to the pure materials of silicate-1/MCM-41.« less

Catalytic Silylation of N2 and Synthesis of NH3 and N2H4 by Net Hydrogen Atom Transfer Reactions Using a Chromium P4 Macrocycle.

PubMed

Kendall, Alexander J; Johnson, Samantha I; Bullock, R Morris; Mock, Michael T

2018-02-21

We report the first discrete molecular Cr-based catalysts for the reduction of N 2 . This study is focused on the reactivity of the Cr-N 2 complex, trans-[Cr(N 2 ) 2 (P Ph 4 N Bn 4 )] (P 4 Cr(N 2 ) 2 ), bearing a 16-membered tetraphosphine macrocycle. The architecture of the [16]-P Ph 4 N Bn 4 ligand is critical to preserve the structural integrity of the catalyst. P 4 Cr(N 2 ) 2 was found to mediate the reduction of N 2 at room temperature and 1 atm pressure by three complementary reaction pathways: (1) Cr-catalyzed reduction of N 2 to N(SiMe 3 ) 3 by Na and Me 3 SiCl, affording up to 34 equiv N(SiMe 3 ) 3 ; (2) stoichiometric reduction of N 2 by protons and electrons (for example, the reaction of cobaltocene and collidinium triflate at room temperature afforded 1.9 equiv of NH 3 , or at -78 °C afforded a mixture of NH 3 and N 2 H 4 ); and (3) the first example of NH 3 formation from the reaction of a terminally bound N 2 ligand with a traditional H atom source, TEMPOH (2,2,6,6-tetramethylpiperidine-1-ol). We found that trans-[Cr( 15 N 2 ) 2 (P Ph 4 N Bn 4 )] reacts with excess TEMPOH to afford 1.4 equiv of 15 NH 3 . Isotopic labeling studies using TEMPOD afforded ND 3 as the product of N 2 reduction, confirming that the H atoms are provided by TEMPOH.

Enhancing the stability of copper chromite catalysts for the selective hydrogenation of furfural using ALD overcoating

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Hongbo; Lei, Yu; Kropf, A. Jeremy

2014-08-01

The stability of a gas-phase furfural hydrogenation catalyst (CuCr2O4 center dot CuO) was enhanced by depositing a thin Al2O3 layer using atomic layer deposition (ALD). Based on temperature-programed reduction (TPR) measurements, the reduction temperature of Cu was raised significantly, and the activation energy for furfural reduction was decreased following the ALD treatment. Thinner ALD layers yielded higher furfural hydrogenation activities. X-ray absorption fine structure (XAFS) spectroscopy studies indicated that Cu1+/Cu-0 are the active species for furfural reduction.

Structural and surface changes of cobalt modified manganese oxide during activation and ethanol steam reforming reaction

NASA Astrophysics Data System (ADS)

Gac, Wojciech; Greluk, Magdalena; Słowik, Grzegorz; Turczyniak-Surdacka, Sylwia

2018-05-01

Surface and structural changes of unmodified manganese and cobalt-manganese oxide during activation and ethanol steam reforming reaction conditions (ESR) were studied by means of X-ray diffraction, X-ray photoelectron spectroscopy, temperature-programmed reduction/oxidation (TPR/TPO) and transmission electron microscopy. It was shown that synthesis of cobalt manganese oxide by the redox precipitation method led to the formation of strongly dispersed cobalt ionic species within cryptomelane-based manganese oxide structure. Development of large cube-like MnO nanoparticles with spherical cobalt metallic crystallites decorated by manganese oxide on the high oxidation state and potassium species was observed during reduction. Cobalt manganese catalyst showed high initial activity and selectivity to H2 and CO2 in ethanol stem reforming reaction in the range of 390-480 °C. The drop of ethanol conversion and changes of selectivity with the time-on-stream were observed. An increase of reaction temperature led to intensification of deactivation phenomena. TEM studies evidenced coexistence of Co and CoOx nanoparticles formed under ethanol steam reforming conditions, partially covered by filamentous and encapsulating carbonaceous deposits.

In-situ X-ray diffraction activation study on an Fe/TiO2 pre-catalyst.

PubMed

Rayner, Matthew K; Billing, David G; Coville, Neil J

2014-06-01

This study focuses on the use of in situ powder X-ray diffraction (PXRD) and quantitative phase analysis using the Rietveld method to monitor the structural properties of a titania-supported iron (10% Fe/TiO2) pre-catalyst during calcination (oxidation) and activation (reduction) in the temperature range 25-900°C. The TiO2 oxidation study revealed an increase in anatase particle size before the anatase to rutile phase transformation, lending credibility to the bridging mechanism proposed by Kim et al. [(2007), Mater. Sci. Forum, 534-536, 65-68]. Pre-catalyst oxidation experiments allowed for the determination of a suitable calcination temperature (450°C) of the pre-catalyst in terms of maximum hematite concentration and appropriate particle size. These experiments also confirmed that the anatase to rutile phase transformation occurred at higher temperatures after Fe addition and that anatase was the sole donor of Ti(4+) ions, which are known to migrate into hematite (Gennari et al., 1998), during the formation of pseudobrookite (Fe2TiO5) at temperatures above 690°C. Using the results from the oxidation experiments, two pre-catalyst samples were calcined at different temperatures; one to represent the preferred case and one to represent a case where the pre-catalyst had been excessively heated. Samples of the excessively heated catalysts were exposed to different reducing gas atmospheres (5, 10 and 100% H2/N2) and heated in the in situ PXRD reactor, so that diffraction data could be collected during the activation process. The results show that reduction with gases containing low concentrations of H2 (5 and 10%) led to the formation of ilmenite (FeTiO3) and we were able to show that both anatase and rutile are consumed in the reaction. Higher concentrations of H2 led to the formation of magnetite (Fe3O4) and metallic iron (Fe(0)). We also noted a decrease in the anatase to rutile transformation temperature under reducing atmospheres when compared with the pre-catalyst heat-treatment experiment. A reduced calcination temperature prior to reduction allowed more facile Fe reduction.

Redox thermodynamics of the native and alkaline forms of eukaryotic and bacterial class I cytochromes c.

PubMed

Battistuzzi, G; Borsari, M; Sola, M; Francia, F

1997-12-23

The reduction potentials of beef heart cytochrome c and cytochromes c2 from Rhodopseudomonas palustris, Rhodobacter sphaeroides, and Rhodobacter capsulatus were measured through direct electrochemistry at a surface-modified gold electrode as a function of temperature in nonisothermal experiments carried out at neutral and alkaline pH values. The thermodynamic parameters for protein reduction (DeltaS degrees rc and DeltaH degrees rc) were determined for the native and alkaline conformers. Enthalpy and entropy terms underlying species-dependent differences in E degrees and pH- and temperature-induced E degrees changes for a given cytochrome were analyzed. The difference of about +0.1 V in E degrees between cytochromes c2 and the eukaryotic species can be separated into an enthalpic term (-DeltaDeltaH degrees rc/F) of +0.130 V and an entropic term (TDeltaDeltaS degrees rc/F) of -0.040 V. Hence, the higher potential of the bacterial species appears to be determined entirely by a greater enthalpic stabilization of the reduced state. Analogously, the much lower potential of the alkaline conformer(s) as compared to the native species is by far enthalpic in origin for both protein families, and is largely determined by the substitution of Met for Lys in axial heme ligation. Instead, the biphasic E degrees /temperature profile for the native cytochromes is due to a difference in reduction entropy between the conformers at low and high temperatures. Temperature-dependent 1H NMR experiments suggest that the temperature-induced transition also involves a change in orientation of the axial methionine ligand with respect to the heme plane.

Modifying surface properties of KIT-6 zeolite with Ni and V for enhancing catalytic CO methanation

NASA Astrophysics Data System (ADS)

Cao, Hong-Xia; Zhang, Jun; Guo, Cheng-Long; Chen, Jingguang G.; Ren, Xiang-Kun

2017-12-01

The surface of the KIT-6 zeolite was modified with different amounts of Ni and V to promote the catalytic properties for CO methanation. A series of xNi-yV/KIT-6 with various Ni and V contents were prepared by the incipient-wetness impregnation method. The modified surfaces were characterized using N2 adsorption-desorption, Brunauer-Emmett-Teller (BET), X-ray diffraction (XRD), hydrogen temperature-programmed reduction (H2-TPR), Fourier transformed infrared spectroscopy (FT-IR), Raman, X-ray photoelectron spectroscopy (XPS), transmission electron microscope (TEM), and energy-dispersive X-ray spectroscopy (EDX), respectively. The characterization results illustrated that the modification of V species was able to significantly promote low-temperature catalytic performance below 350 °C compared to that of unmodified Ni/KIT-6, which was likely due to an increase in the H2 uptake accompanied by enhanced CO dissociation derived from stronger electron transfer from V species to Ni0. Correspondingly, the xNi-yV/KIT-6 catalysts exhibited a distinct enhancement in CO conversion, CH4 selectivity and CH4 yield over unmodified Ni/KIT-6. Among all catalysts, 20Ni-2V/KIT-6 showed the best catalytic performance, corresponding to nearly 100% CO conversion and 85% CH4 yield at a low temperature of 300 °C. Furthermore, 20Ni-2V/KIT-6 presented enhanced coking-resistant and anti-sintering properties during a 60h-lifetime test at 500 °C and 1 atm with a high weight hourly space velocity (WHSV) of 60000 ml/g/h.

Catalysts for selective hydrogenation of furfural derived from the double complex salt [Pd(NH 3 ) 4 ](ReO 4 ) 2 on γ-Al 2 O 3

DOE Office of Scientific and Technical Information (OSTI.GOV)

Thompson, Simon T.; Lamb, H. Henry

The double complex salt [Pd(NH3)4](ReO4)2 was employed as precursor of supported bimetallic catalysts for selective hydrogenation of furfural. Direct reduction of [Pd(NH3)4](ReO4)2 on γ-Al2O3 in flowing H2 at 400 °C yields bimetallic nanoparticles 1–2 nm in size that exhibit significant interaction between the metals, as evidenced by temperature-programmed hydride decomposition (complete suppression of β-PdHx formation), extended X-ray absorption fine structure spectroscopy at the Pd K and Re LIII edges (PdRe distance = 2.72 Å), and scanning transmission electron microscopy with energy dispersive X-ray analysis. In contrast, calcination of [Pd(NH3)4](ReO4)2 on γ-Al2O3 at 350 °C in air and subsequent reduction inmore » H2 at 400 °C results in metal segregation and formation of large (>50 nm) supported Pd particles; Re species cover the Pd particles and γ-Al2O3 support. A PdRe 1:2 catalyst prepared by sequential impregnation and calcination using HReO4 and [Pd(NH3)4](NO3)2 has a similar morphology. The catalyst derived by direct reduction of [Pd(NH3)4](ReO4)2 on γ-Al2O3 exhibits remarkably high activity for selective hydrogenation of furfural to furfuryl alcohol (FAL) at 150 °C and 1 atm. Suppression of H2 chemisorption via elimination of Pd threefold sites, as evidenced by CO diffuse-reflectance infrared Fourier transform spectroscopy, correlates with increased FAL selectivity.« less

Carbon and Mo transformations during the synthesis of mesoporous Mo2C/carbon catalysts by carbothermal hydrogen reduction

NASA Astrophysics Data System (ADS)

Wang, Haiyan; Liu, Shida; Liu, Bing; Montes, Vicente; Hill, Josephine M.; Smith, Kevin J.

2018-02-01

The synthesis of mesoporous Mo2C/carbon catalysts by carbothermal hydrogen reduction is reported. Petroleum coke (petcoke) was activated with KOH at 800 °C to obtain high surface area microporous activated petcoke (APC; 2000 m2/g). The APC was wet impregnated with ammonium heptamolybdate (AHM: 10 wt% Mo), dried and reduced in H2 at temperatures from 400 to 800 °C, to yield Mo2C/APC catalysts. Increased reduction temperature increased the Mo2C yield and the mesoporous volume of the Mo2C/APC. At a reduction temperature of 750 °C the mesopore volume of the catalyst doubled compared to the APC support and accounted for 37% of the total pore volume. Maintaining the final CHR temperature for 90 min further increased the Mo2C yield and mesoporosity of the catalyst. The role of Mo2C in the catalytic hydrogenation of the APC and mesopore generation is demonstrated. The activity of the Mo2C/carbon catalysts in the hydrodeoxygenation of 4-methyl phenol increased with increased CHR temperature and catalyst mesoporosity.

Synthesis of C60H2 by rhodium-catalyzed hydrogenation of C60

NASA Technical Reports Server (NTRS)

Becker, L.; Evans, T. P.; Bada, J. L.; Miller, S. L. (Principal Investigator)

1993-01-01

Reduction of C60 with rhodium(0) on alumina and hydrogen in deuterated benzene (C6D6) at ambient temperature and pressure yields a mixture of hydrogenated compounds; C60H2 has been characterized as the major product in 14% yield based on 1H NMR.

A prospective, observational clinical trial of fever reduction to reduce systemic oxygen consumption in the setting of acute brain injury.

PubMed

Hata, J Steven; Shelsky, Constance R; Hindman, Bradley J; Smith, Thomas C; Simmons, Jonathan S; Todd, Michael M

2008-01-01

Fever after acute brain injury appears to be a detrimental factor, associated with impaired neurological outcomes. This study assessed physiological changes in systemic oxygen consumption (VO2) during cutaneous cooling after severe brain injury. This prospective, observational, clinical study evaluated ten, critically ill, brain-injured patients requiring mechanical ventilation with a core body temperature of greater or equal to 38 degrees C. Febrile patients failing to defervesce after acetaminophen underwent indirect calorimetry for a 1-hour baseline period followed by a 4 h cooling period. The Arctic Sun(R) Temperature Management System (Medivance) directed core temperature to a goal of 36 degrees C. The patients had a mean age of 32 years (95% CI 23, 40), Glasgow Coma Scale of 6 (95% CI 5,7), and APACHE 2 score of 19 (95% CI 15, 22), with 8 of 10 patients suffering traumatic brain injuries. The baseline 1-h core temperature was significantly reduced from 38.6 degrees +/- 0.9 to 36.3 degrees +/- 1.2 degrees C (P < 0.0001) over 4 h. Two cohorts were identified based upon the presence or absence of shivering. Within the non-shivering cohort, systemic VO2 was significantly reduced from 415 +/- 123 to 308 +/- 115 ml/min (-27 +/- 18%) (P < 0.05). In contrast, those with shivering showed no significant reduction in VO2, despite significantly decreasing core temperature. The overall percentage change of VCO2 correlated with VO2 (r (2) = 0.91). Fever reduction in acute brain injury appears to significantly reduce systemic VO2, but is highly dependent on shivering control.

Column temperature programming in enantioseparation of dihydropyrimidinone compounds using derivatized cellulose and amylose chiral stationary phases.

PubMed

Wang, Fang; Yeung, David; Han, Jun; Semin, David; McElvain, James S; Cheetham, Janet

2008-03-01

We report the application of column temperature programs as a tool to examine unusual temperature-induced behaviors of polysaccharide chiral stationary phases (CSPs). Using dihydropyrimidinone (DHP) compounds as probes we observed the heating (10-50 degrees C) and cooling (50-10 degrees C) van't Hoff plots of retention factors and/or selectivities of DHP compounds were not superimposable on AD, IA, and AS-H columns solvated with ethanol (EtOH)/n-hexane (n-Hex) mobile phases. The plots were not superimposable on AD, IB, and AS-H columns solvated with 2-propanol (2-PrOH)/n-Hex mobile phases. The thermally induced path-dependant behaviors were caused by slow equilibration as evidenced by the disappearance of the hysteresis in the second heating to cooling cycle and in a cooling to heating cycle. From the step-temperature program (10-50-10 degrees C), only EtOH solvated AD and AS-H phases showed the change of retention factors and/or selectivities with time while only 2-PrOH solvated AS-H phase showed similar behaviors.

Promoting Ethylene Selectivity from CO2 Electroreduction on CuO Supported onto CO2 Capture Materials.

PubMed

Yang, Hui-Juan; Yang, Hong; Hong, Yu-Hao; Zhang, Peng-Yang; Wang, Tao; Chen, Li-Na; Zhang, Feng-Yang; Wu, Qi-Hui; Tian, Na; Zhou, Zhi-You; Sun, Shi-Gang

2018-03-09

Cu is a unique catalyst for CO 2 electroreduction, since it can catalyze CO 2 reduction to a series of hydrocarbons, alcohols, and carboxylic acids. Nevertheless, such Cu catalysts suffer from poor selectivity. High pressure of CO 2 is considered to facilitate the activity and selectivity of CO 2 reduction. Herein, a new strategy is presented for CO 2 reduction with improved C 2 H 4 selectivity on a Cu catalyst by using CO 2 capture materials as the support at ambient pressure. N-doped carbon (N x C) was synthesized through high-temperature carbonization of melamine and l-lysine. We observed that the CO 2 uptake capacity of N x C depends on both the microporous area and the content of pyridinic N species, which can be controlled by the carbonization temperature (600-800 °C). The as-prepared CuO/N x C catalysts exhibit a considerably higher C 2 H 4 faradaic efficiency (36 %) than CuO supported on XC-72 carbon black (19 %), or unsupported CuO (20 %). Moreover, there is a good linear relationship between the C 2 H 4 faradaic efficiency and CO 2 uptake capacity of the supports for CuO. The local high CO 2 concentration near Cu catalysts, created by CO 2 capture materials, was proposed to increase the coverage of CO intermediate, which is favorable for the coupling of two CO units in the formation of C 2 H 4 . This study demonstrates that pairing Cu catalysts with CO 2 capture supports is a promising approach for designing highly effective CO 2 reduction electrocatalysts. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Reduction of verotoxigenic Escherichia coli by process and recipe optimisation in dry-fermented sausages.

PubMed

Heir, E; Holck, A L; Omer, M K; Alvseike, O; Høy, M; Måge, I; Axelsson, L

2010-07-15

Outbreaks of verotoxigenic Escherichia coli (VTEC) linked to dry-fermented sausages (DFSs) have emphasized the need for DFS manufacturers to introduce measures to obtain enhanced safety and still maintain the sensory qualities of their products. To our knowledge no data have yet been reported on non-O157:H7 VTEC survival in DFS. Here, the importance of recipe and process variables on VTEC (O157:H7 and O103:H25) reductions in two types of DFS, morr and salami, was determined through three statistically designed experiments. Linear regression and ANOVA analyses showed that no single variable had a dominant effect on VTEC reductions. High levels of NaCl, NaNO(2), glucose (low pH) and fermentation temperature gave enhanced VTEC reduction, while high fat and large casing diameter (a(w)) gave the opposite effect. Interaction effects were small. The process and recipe variables showed similar effects in morr and salami. In general, recipes combining high batter levels of salt (NaCl and NaNO(2)) and glucose along with high fermentation temperature that gave DFS with low final pH and a(w), provided approximately 3 log(10) reductions compared to approximately 1.5 log(10) reductions obtained for standard recipe DFS. Storage at 4 degrees C for 2 months provided log(10) 0.33-0.95 additional VTEC reductions and were only marginally affected by recipe type. Sensory tests revealed only small differences between the various recipes of morr and salami. By optimisation of recipe and process parameters, it is possible to obtain increased microbial safety of DFS while maintaining the sensory qualities of the sausages. 2010 Elsevier B.V. All rights reserved.

Strong Temperature Dependence in the Reactivity of H 2 on RuO 2 (110)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Henderson, Michael A.; Dahal, Arjun; Dohnálek, Zdenek

2016-08-04

The ability of hydrogen to facilitate many types of heterogeneous catalysis starts with its adsorption. As such, understanding the temperature-dependence sticking of H2 is critical toward controlling and optimizing catalytic conditions in those cases where adsorption is rate-limiting. In this work, we examine the temperature-dependent sticking of H2/D2 to the clean RuO2(110) surface using the King & Wells molecular beam approach, temperature programmed desorption (TPD) and scanning tunneling microscopy (STM). We show that the sticking probability (molecular or dissociative) of H2/D2 on this surface is highly temperature-dependent, decreasing from ~0.4-0.5 below 25 K to effectively zero above 200 K. Bothmore » STM and TPD reveal that OH/OD formation is severely limited for adsorption temperatures above ~150 K. Previous literature reports of extensive surface hydroxylation from H2/D2 exposures at room temperature were most likely the result of inadvertent contamination brought about from dosing by chamber backfilling.« less

Electron-stimulated reactions in layered CO/H2O films: Hydrogen atom diffusion and the sequential hydrogenation of CO to methanol

DOE Office of Scientific and Technical Information (OSTI.GOV)

Petrik, Nikolay G.; Monckton, Rhiannon J.; Koehler, Sven

Low-energy (100 eV) electron-stimulated reactions in layered H2O/CO/H2O ices are investigated. For CO trapped within approximately 50 ML of the vacuum interface in the amorphous solid water (ASW) films, both oxidation and reduction reactions are observed. However for CO buried more deeply in the film, only the reduction of CO to methanol is observed. Experiments with layered films of H2O and D2O show that the hydrogen atoms participating in the reduction of the buried CO originate in region from ~10 – 40 ML below the surface of the ASW films and subsequently diffuse through the film. For deeply buried COmore » layers, the CO reduction reactions quickly increase with temperature above ~60 K. We present a simple chemical kinetic model that treats the diffusion of hydrogen atoms in the ASW and sequential hydrogenation of the CO to methanol that accounts for the observations.« less

In-Situ Anode Heating and Its Effects on Atomic Constituents in the A-K Gap in Self-Magnetic Pinch (SMP) Experiments

NASA Astrophysics Data System (ADS)

Simpson, Sean; Renk, Timothy; Johnston, Mark; Mazarakis, Mike; Patel, Sonal

2015-11-01

The RITS-6 inductive voltage adder (IVA) accelerator (3.5-8.5 MeV) at Sandia National Laboratories produces high-power (TW) focused electron beams (<3mm diameter) for flash x-ray radiography applications. The Self-Magnetic Pinch (SMP) diode utilizes a hollowed metal cathode to produce a pinched focus onto a high-Z metal anode converter. There is not a clear understanding as to the effects various contaminants such as C, CO, H, H2O, HmCn, O2, and N2, on the anode surface or in the bulk may have on impedance dynamics, beam stability, beam spot size, and reproducibility. Heating pure Ta anodes with and without a thin Al coating have been investigated using temperatures ranging from 400 °C to 1000 °C. Initial experiments indicate a significant reduction in H and C as seen in high-speed spectral analysis of plasmas at the converter and a reduction in the back-streaming proton current. Experiments are ongoing, and latest results will be reported. Sandia National Laboratories is a multi-program laboratory managed and operated by Sandia Corporation, a wholly owned subsidiary of Lockheed Martin Corporation, for the U.S. Department of Energy's National Nuclear Security Administration under contract DE-AC04-94AL85000.

In situ X-ray diffraction study of reduction processes of Fe{sub 3}O{sub 4}- and Fe{sub 1-x}O-based ammonia-synthesis catalysts

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zheng Yifan, E-mail: zhengyifan@zjut.edu.c; Catalysis Institute, Zhejiang University of Technology, Hangzhou 310014; Liu Huazhang

2009-09-15

The temperature-programmed reduction process of two types of industrial ammonia-synthesis catalysts, A110 and ZA-5, which are, respectively, based on Fe{sub 3}O{sub 4} and Fe{sub 1-x}O precursors, were studied by in situ X-ray power diffraction (XRD). It has been found that the ZA-5 has lower reduction temperature and faster reduction rate, and its active phase alpha-Fe possesses a higher value of lattice microstrain than A110. The simulation based on Rietveld refinement has also shown that the shape of alpha-Fe grain of ZA-5 has a mixed shape of cube and sphere with more exposing (111) and (211) planes, while that of A110more » looks like a concave cube with more exposing (110) planes. Based on the results obtained, a growth model of alpha-Fe during the reduction of Fe{sub 3}O{sub 4}- and Fe{sub 1-x}O-based ammonia-synthesis catalysts is proposed, and the origins for the activity difference has been also discussed. - Graphical Abstract: A proposed growth model of active phase alpha-Fe during reduction. Due to H{sub 2} diffusing easily into the pores, reduction starts on outside and inside surface simultaneously to form 'microcrystalline film', and the particles shrink during reduction which results in breaking of the aggregated oxide particle.« less

Characterization of copper oxides, iron oxides, and zinc copper ferrite desulfurization sorbents by X-ray photoelectron spectroscopy and scanning electron microscopy

NASA Astrophysics Data System (ADS)

Siriwardane, Ranjani V.; Poston, James A.

1993-05-01

Characterization of copper oxides, iron oxides, and zinc copper ferrite desulfurization sorbents was performed by X-ray photoelectron spectroscopy and scanning electron microscopy/energy-dispersive spectroscopy at temperatures of 298 to 823 K. Analysis of copper oxides indicated that the satellite structure of the Cu22p region was absent in the Cu(I) state but was present in the Cu(II) state. Reduction of CuO at room temperature was observed when the ion gauge was placed close to the sample. The satellite structure was absent in all the copper oxides at 823 K in vacuum. Differentiation of the oxidation state of copper utilizing both Cu(L 3M 4,5M 4,5) X-ray-induced Auger lines and Cu2p satellite structure, indicated that the copper in zinc copper ferrite was in the + 1 oxidation state at 823 K. This + 1 state of copper was not significantly changed after exposure to H 2, CO, and H 2O. There was an increase in Cu/Zn ratio and a decrease in Fe/Zn ratio on the surface of zinc copper ferrite at 823 K compared to that at room temperature. These conditions of copper offered the best sulfidation equilibrium for the zinc copper ferrite desulfurization sorbent. Analysis of iron oxides indicated that there was some reduction of both Fe 2O 3 and FeO at 823K. The iron in zinc copper ferrite was similar to that of Fe 2O 3 at room temperature but there was some reduction of this Fe(III) state to Fe(II) at 823 K. This reduction was more enhanced in the presence of H 2 and CO. Reduction to Fe(II) may not be desirable for the lifetime of the sorbent.

Hierarchically porous LaFeO3 perovskite prepared from the pomelo peel bio-template for catalytic oxidation of NO

NASA Astrophysics Data System (ADS)

Zhao, Shaojun; Wang, Li; Wang, Ying; Li, Xing

2018-05-01

In this paper, pomelo peel was used as biological template to obtain hierarchically porous LaFeO3 perovskite for the catalytic oxidation of NO to NO2. In addition, X-ray diffraction (XRD), scanning electron microscopy (SEM), N2 adsorption-desorption analyses, X-ray photoelectron spectra (XPS), NO temperature-programmed desorption (NO-TPD), oxygen temperature-programmed desorption (O2-TPD) and hydrogen temperature-programmed reduction (H2-TPR) were used to investigate the micro-structure and the redox properties of the hierarchically porous LaFeO3 perovskite prepared from pomelo peel biological template and the LaFeO3 perovskite without the biological template. The results indicated that the hierarchically porous LaFeO3 perovskite successfully replicated the porous structure of pomelo peel with high specific surface area. Compared to the LaFeO3 perovskite prepared without the pomelo peel template, the hierarchically porous LaFeO3 perovskite showed better catalytic oxidization of NO to NO2 under the same conditions. The maximum NO conversions for LaFeO3 prepared with and without template were 90% at 305 °C and 76% at 313 °C, respectively. This is mainly attributed to the higher ratio of Fe4+/Fe3+, the hierarchically porous structure with more adsorbed oxygen species and higher surface area for the hierarchically porous LaFeO3 perovskite compared with the sample prepared without the pomelo peel template.

Visible light plasmonic heating of Au-ZnO for the catalytic reduction of CO 2

DOE PAGES

Wang, Congjun; Ranasingha, Oshadha; Natesakhawat, Sittichai; ...

2013-01-01

Plasmonic excitation of Au nanoparticles attached to the surface of ZnO catalysts using low power 532 nm laser illumination leads to significant heating of the catalyst and the conversion of CO 2 and H 2 reactants to CH 4 and CO products. Temperature-calibrated Raman spectra of ZnO phonons show that intensity-dependent plasmonic excitation can controllably heat Au–ZnO from 30 to ~600 °C and simultaneously tune the CH 4 : CO product ratio. The laser induced heating and resulting CH 4 : CO product distribution agrees well with predictions from thermodynamic models and temperature-programmed reaction experiments indicating that the reaction ismore » a thermally driven process resulting from the plasmonic heating of the Au-ZnO. The apparent quantum yield for CO 2 conversion under continuous wave (cw) 532 nm laser illumination is 0.030%. The Au-ZnO catalysts are robust and remain active after repeated laser exposure and cycling. The light intensity required to initiate CO 2 reduction is low ( ~2.5 x 10 5 W m -2) and achievable with solar concentrators. Our results illustrate the viability of plasmonic heating approaches for CO 2 utilization and other practical thermal catalytic applications.« less

Optimizing Phosphoric Acid plus Hydrogen Peroxide (PHP) Pretreatment on Wheat Straw by Response Surface Method for Enzymatic Saccharification.

PubMed

Qiu, Jingwen; Wang, Qing; Shen, Fei; Yang, Gang; Zhang, Yanzong; Deng, Shihuai; Zhang, Jing; Zeng, Yongmei; Song, Chun

2017-03-01

Wheat straw was pretreated by phosphoric acid plus hydrogen peroxide (PHP), in which temperature, time, and H 3 PO 4 proportion for pretreatment were investigated by using response surface method. Results indicated that hemicellulose and lignin removal positively responded to the increase of pretreatment temperature, H 3 PO 4 proportion, and time. H 3 PO 4 proportion was the most important variable to control cellulose recovery, followed by pretreatment temperature and time. Moreover, these three variables all negatively related to cellulose recovery. Increasing H 3 PO 4 proportion can improve enzymatic hydrolysis; however, reduction on cellulose recovery results in decrease of glucose yield. Extra high temperature or long time for pretreatment was not beneficial to enzymatic hydrolysis and glucose yield. Based on the criterion for minimizing H 3 PO 4 usage and maximizing glucose yield, the optimized pretreatment conditions was 40 °C, 2.0 h, and H 3 PO 4 proportion of 70.2 % (H 2 O 2 proportion of 5.2 %), by which glucose yielded 299 mg/g wheat straw (946.2 mg/g cellulose) after 72-h enzymatic hydrolysis.

Enhancing hydrogen storage performances of MgH2 by Ni nano-particles over mesoporous carbon CMK-3

NASA Astrophysics Data System (ADS)

Chen, Gang; Zhang, Yao; Chen, Jian; Guo, Xinli; Zhu, Yunfeng; Li, Liquan

2018-06-01

Nano-dispersed Ni particles over mesoporous carbon material CMK-3 (Ni/CMK-3) was fabricated by means of impregnation-reduction strategy using precursor NiCl2 · 6H2O, which is beneficial to improving the de/rehydrogenation performances of MgH2. The dehydrogenation onset temperature of MgH2–Ni/CMK-3 is significantly lowered by 170 K from that of pristine MgH2 (around 603 K). Totally 5.9 wt% of hydrogen absorption capacity is liberated within 1 h at a temperature of 423 K under a pressure of 3 MPa. This composite can absorb 3.9 wt% hydrogen even at a temperature of 328 K under 3 MPa H2. Activation energy values of both dehydrogenation (43.4 kJ mol‑1) and rehydrogenation (37.4 kJ mol‑1) for MgH2–Ni/CMK-3 are greatly enhanced from those of as-milled MgH2. Ni/CMK-3 also slightly destabilizes the dehydrogenation of MgH2 by 1.5 kJ mol {{{{H}}}2}-1. The enhanced performances can be attributed to the synergistic effects of both destabilization and activation from nano-dispersed Ni particles.

Biogeochemical modeling of CO2 and CH4 production in anoxic Arctic soil microcosms

NASA Astrophysics Data System (ADS)

Tang, Guoping; Zheng, Jianqiu; Xu, Xiaofeng; Yang, Ziming; Graham, David E.; Gu, Baohua; Painter, Scott L.; Thornton, Peter E.

2016-09-01

Soil organic carbon turnover to CO2 and CH4 is sensitive to soil redox potential and pH conditions. However, land surface models do not consider redox and pH in the aqueous phase explicitly, thereby limiting their use for making predictions in anoxic environments. Using recent data from incubations of Arctic soils, we extend the Community Land Model with coupled carbon and nitrogen (CLM-CN) decomposition cascade to include simple organic substrate turnover, fermentation, Fe(III) reduction, and methanogenesis reactions, and assess the efficacy of various temperature and pH response functions. Incorporating the Windermere Humic Aqueous Model (WHAM) enables us to approximately describe the observed pH evolution without additional parameterization. Although Fe(III) reduction is normally assumed to compete with methanogenesis, the model predicts that Fe(III) reduction raises the pH from acidic to neutral, thereby reducing environmental stress to methanogens and accelerating methane production when substrates are not limiting. The equilibrium speciation predicts a substantial increase in CO2 solubility as pH increases, and taking into account CO2 adsorption to surface sites of metal oxides further decreases the predicted headspace gas-phase fraction at low pH. Without adequate representation of these speciation reactions, as well as the impacts of pH, temperature, and pressure, the CO2 production from closed microcosms can be substantially underestimated based on headspace CO2 measurements only. Our results demonstrate the efficacy of geochemical models for simulating soil biogeochemistry and provide predictive understanding and mechanistic representations that can be incorporated into land surface models to improve climate predictions.

MOF-74 as an Efficient Catalyst for the Low-Temperature Selective Catalytic Reduction of NOx with NH3.

PubMed

Jiang, Haoxi; Wang, Qianyun; Wang, Huiqin; Chen, Yifei; Zhang, Minhua

2016-10-12

In this work, Mn-MOF-74 with hollow spherical structure and Co-MOF-74 with petal-like shape have been prepared successfully via the hydrothermal method. The catalysts were characterized using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), thermogravimetry-mass spectrum analysis (TG-MS), N 2 adsorption/desorption, scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS). It is found that MOF-74(Mn, Co) exhibits the capability for selective catalytic reduction (SCR) of NO x at low temperatures. Both experimental (temperature-programmed desorption, TPD) and computational methods have shown that Co-MOF-74 and Mn-MOF-74 owned high adsorption and activation abilities for NO and NH 3 . The catalytic activities of Mn-MOF-74 and Co-MOF-74 for low-temperature denitrification (deNO x ) in the presence of NH 3 were 99% at 220 °C and 70% at 210 °C, respectively. It is found that the coordinatively unsaturated metal sites (CUSs) in M-MOF-74 (M = Mn and Co) played important roles in SCR reaction. M-MOF-74 (M = Mn and Co), especially Mn-MOF-74, showed excellent catalytic performance for low-temperature SCR. In addition, in the reaction process, NO conversion on Mn-MOF-74 decreased with the introduction of H 2 O and SO 2 and almost recovered when gas was cut off. However, for Co-MOF-74, SO 2 almost has no effect on the catalytic activity. This work showed that MOF-74 could be used prospectively as deNO x catalyst.

Effect of ultrasonic treatment of palygorskite on the catalytic performance of Pd-Cu/palygorskite catalyst for room temperature CO oxidation in humid circumstances.

PubMed

Wang, Yongzhao; Wang, Yongning; Li, Xiao; Liu, Zhaotie; Zhao, Yongxiang

2018-03-01

Pd-Cu/palygorskite catalysts were prepared by a wet impregnation method using palygorskite (PC/N-Pal) and ultrasonic-treated palygorskite (PC/U-Pal) as the support. Their catalytic activities toward CO oxidation at room temperature and in humid circumstances were investigated. PC/U-Pal exhibits much higher catalytic activity and stability than PC/N-Pal under the conditions of 1.0 vol.% CO and 3.3 vol.% H 2 O in the feed gas. The X-ray diffraction results indicate that quartz impurities were eliminated from the Pal after the ultrasonic treatment, and more copper species exist in the form of Cu 2 Cl(OH) 3 in PC/U-Pal. The temperature-programmed reduction results suggest that there is an enhanced reducibility of PC/U-Pal after ultrasonic treatment. Furthermore, the ultrasonic treatment can properly decrease the hydrophilicity of the support and catalyst, which may also contribute to the excellent catalytic performance.

Survival of Salmonella typhimurium and Escherichia coli O157:H7 in poultry manure and manure slurry at sublethal temperatures.

PubMed

Himathongkham, S; Riemann, H; Bahari, S; Nuanualsuwan, S; Kass, P; Cliver, D O

2000-01-01

Exponential inactivation was observed for Salmonella typhimurium and Escherichia coli O157:H7 in poultry manure with decimal reduction times ranging from half a day at 37 C to 1-2 wk at 4 C. There was no material difference in inactivation rates between S. typhimurium and E. coli O157:H7. Inactivation was slower in slurries made by mixing two parts of water with one part of manure; decimal reduction times (time required for 90% destruction) ranged from 1-2 days at 37 C to 6-22 wk at 4 C. Escherichia coli O157:H7 consistently exhibited slightly slower inactivation than S. typhimurium. Log decimal reduction time for both strains was a linear function of storage temperature for manure and slurries. Chemical analysis indicated that accumulation of free ammonia in poultry manure was an important factor in inactivation of the pathogens. This finding was experimentally confirmed for S. typhimurium by adding ammonia directly to peptone water or to bovine manure, which was naturally low in ammonia, and adjusting pH to achieve predetermined levels of free ammonia.

[Enhanced remediation of 4-chloronitrobenzene contaminated groundwater with nanoscale zero-valence iron (nZVI) catalyzed hydrogen peroxide (H2O2)].

PubMed

Fu, Rong-Bing

2014-04-01

Chemical oxidation-reduction technology is an important way to quickly remedy contaminated groundwater. Nanoscale zero-valent iron (nZVI) was produced by liquid-phase reduction using FeSO4 and NaBH4, and characterized by SEM and XRD. The remediation of 4-chloronitrobezene (4-CINB) contaminated groundwater at ambient temperature and pressure was conducted with the nZVI catalytic H2O2 process, and the affecting factors and degradation mechanisms were investigated. The results indicated that under initial pH 3.0 at the temperature of 30 degrees C, after 30 mins of reaction, 4-ClNB in groundwater was completely degraded when the concentrations of nZVI and H2O2 were 268.8 mg x L(-1) and 4.90 mmol x L(-1), respectively. 4-chloronitrosobenzene, 4-chlorophenylhydroxylamine, 4-chloroazoxybenzene, 4-chloroaniline, 4-chloroazobenzene, 4-benzoquinone, acetic acid, formic acid, oxalic acid and chlorine ion were identified as the major intermediates of 4-ClNB degradation after the process. A tentative pathway for the degradation of 4-ClNB was proposed.

Fast hydrogen sorption from MgH2-VO2(B) composite materials

NASA Astrophysics Data System (ADS)

Milošević, Sanja; Kurko, Sandra; Pasquini, Luca; Matović, Ljiljana; Vujasin, Radojka; Novaković, Nikola; Novaković, Jasmina Grbović

2016-03-01

The hydrogen sorption kinetics of MgH2‒VO2(B) composites synthesised by mechanical milling have been studied. The microstructural properties of composites were characterized by means of X-ray diffraction (XRD), Raman spectroscopy, Scanning electron microscopy (SEM), Particle size analysis (PSD), while sorption behaviour was followed by differential scanning calorimetry (DSC) and Sievert measurements. Results have shown that although desorption temperature reduction is moderate; there is a substantial improvement in hydrogen sorption kinetics. The complete desorption of pure MgH2 at elevated temperature takes place in more than 30 min while the composite fully desorbs in less than 2 min even at lower temperatures. It has been shown that the metastable γ-MgH2 phase and the point defects have a decisive role in desorption process only in the first sorption cycle, while the second and the subsequent sorption cycles are affected by microstructural and morphological characteristics of the composite.

Optimization of palm oil physical refining process for reduction of 3-monochloropropane-1,2-diol (3-MCPD) ester formation.

PubMed

Zulkurnain, Musfirah; Lai, Oi Ming; Tan, Soo Choon; Abdul Latip, Razam; Tan, Chin Ping

2013-04-03

The reduction of 3-monochloropropane-1,2-diol (3-MCPD) ester formation in refined palm oil was achieved by incorporation of additional processing steps in the physical refining process to remove chloroester precursors prior to the deodorization step. The modified refining process was optimized for the least 3-MCPD ester formation and acceptable refined palm oil quality using response surface methodology (RSM) with five processing parameters: water dosage, phosphoric acid dosage, degumming temperature, activated clay dosage, and deodorization temperature. The removal of chloroester precursors was largely accomplished by increasing the water dosage, while the reduction of 3-MCPD esters was a compromise in oxidative stability and color of the refined palm oil because some factors such as acid dosage, degumming temperature, and deodorization temperature showed contradictory effects. The optimization resulted in 87.2% reduction of 3-MCPD esters from 2.9 mg/kg in the conventional refining process to 0.4 mg/kg, with color and oil stability index values of 2.4 R and 14.3 h, respectively.

Enhancing hydrogen storage performances of MgH2 by Ni nano-particles over mesoporous carbon CMK-3.

PubMed

Chen, Gang; Zhang, Yao; Chen, Jian; Guo, Xinli; Zhu, Yunfeng; Li, Liquan

2018-06-29

Nano-dispersed Ni particles over mesoporous carbon material CMK-3 (Ni/CMK-3) was fabricated by means of impregnation-reduction strategy using precursor NiCl 2  · 6H 2 O, which is beneficial to improving the de/rehydrogenation performances of MgH 2 . The dehydrogenation onset temperature of MgH 2 -Ni/CMK-3 is significantly lowered by 170 K from that of pristine MgH 2 (around 603 K). Totally 5.9 wt% of hydrogen absorption capacity is liberated within 1 h at a temperature of 423 K under a pressure of 3 MPa. This composite can absorb 3.9 wt% hydrogen even at a temperature of 328 K under 3 MPa H 2 . Activation energy values of both dehydrogenation (43.4 kJ mol -1 ) and rehydrogenation (37.4 kJ mol -1 ) for MgH 2 -Ni/CMK-3 are greatly enhanced from those of as-milled MgH 2 . Ni/CMK-3 also slightly destabilizes the dehydrogenation of MgH 2 by 1.5 kJ mol [Formula: see text] The enhanced performances can be attributed to the synergistic effects of both destabilization and activation from nano-dispersed Ni particles.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yung, Matthew M.; Starace, Anne K.; Mukarakate, Calvin

Here in this work, Ni/ZSM-5 catalysts with varied nickel loadings were evaluated for their ability to produce aromatic hydrocarbons by upgrading of pine pyrolysis vapors. The effect of catalyst pretreatment by hydrogen reduction was also investigated. Results indicate that the addition of nickel increases the yield of aromatic hydrocarbons while simultaneously increasing the conversion of oxygenates, relative to ZSM-5, and these effects are more pronounced with increasing nickel loading. Additionally, while initial activity differences were observed between the oxidized and reduced forms of nickel on ZSM-5 (i.e., NiO/ZSM-5 versus Ni/ZSM-5), the activity of both catalysts converges with increasing time onmore » stream. These reaction results coupled with characterization of pristine and spent catalysts suggest that the catalysts reach similar active states during catalytic pyrolysis, regardless of pretreatment, as NiO undergoes in situ reduction to Ni by biomass pyrolysis vapors. This reduction of NiO to Ni was confirmed by reaction results and characterization by NH 3 temperature-programmed desorption, temperature-programmed reduction, and X-ray diffraction. This finding is significant in that the ability to reduce or eliminate the need for a pre-reaction H 2 reduction of Ni-modified zeolite catalysts could reduce process complexity and operating costs in a biorefinery-based vapor-phase upgrading process to produce biomass-derived fuels and chemicals. The ability to monitor catalyst activity in real time with a molecular beam mass spectrometer used to measure uncondensed, hot pyrolysis vapors allows for an improved understanding of the mechanism for improved activity with Ni addition to ZSM-5, which is attributed to the ability to prevent deactivation by deposition of coke and capping of zeolite micropores.« less

Biomass Catalytic Pyrolysis on Ni/ZSM-5: Effects of Nickel Pretreatment and Loading

DOE PAGES

Yung, Matthew M.; Starace, Anne K.; Mukarakate, Calvin; ...

2016-04-25

Here in this work, Ni/ZSM-5 catalysts with varied nickel loadings were evaluated for their ability to produce aromatic hydrocarbons by upgrading of pine pyrolysis vapors. The effect of catalyst pretreatment by hydrogen reduction was also investigated. Results indicate that the addition of nickel increases the yield of aromatic hydrocarbons while simultaneously increasing the conversion of oxygenates, relative to ZSM-5, and these effects are more pronounced with increasing nickel loading. Additionally, while initial activity differences were observed between the oxidized and reduced forms of nickel on ZSM-5 (i.e., NiO/ZSM-5 versus Ni/ZSM-5), the activity of both catalysts converges with increasing time onmore » stream. These reaction results coupled with characterization of pristine and spent catalysts suggest that the catalysts reach similar active states during catalytic pyrolysis, regardless of pretreatment, as NiO undergoes in situ reduction to Ni by biomass pyrolysis vapors. This reduction of NiO to Ni was confirmed by reaction results and characterization by NH 3 temperature-programmed desorption, temperature-programmed reduction, and X-ray diffraction. This finding is significant in that the ability to reduce or eliminate the need for a pre-reaction H 2 reduction of Ni-modified zeolite catalysts could reduce process complexity and operating costs in a biorefinery-based vapor-phase upgrading process to produce biomass-derived fuels and chemicals. The ability to monitor catalyst activity in real time with a molecular beam mass spectrometer used to measure uncondensed, hot pyrolysis vapors allows for an improved understanding of the mechanism for improved activity with Ni addition to ZSM-5, which is attributed to the ability to prevent deactivation by deposition of coke and capping of zeolite micropores.« less

n-Hexane hydro-isomerization over promoted Pd/HZSM-5 catalysts

NASA Astrophysics Data System (ADS)

Thoa Dao, Thi Kim; Loc Luu, Cam

2015-09-01

A series of Pd/HZSM-5 catalysts modified by various metallic species, including Co, Ni, Fe, Re, and Cu, was prepared by sequential impregnation. Contents of Pd and second metals in modified catalysts were 0.8 and 1.0 wt%, respectively. Physico-chemical characteristics of catalysts were investigated by nitrogen physi-sorption (BET), x-ray diffraction (XRD), transmission electron microscopy (TEM), ammonia temperature programmed desorption (NH3-TPD), temperature programmed reduction (TPR) and hydrogen pulse chemisorption (HPC). Coke formation was studied by the method of thermogravimetric analysis (TGA). The activities of catalysts in n-hexane isomerization were studied in a micro-flow reactor under atmospheric pressure at 250 °C, and molar ratio of H2: n-hexane of 5.92. It was found that Co, Ni, Fe, and Re additives exhibited geometric and electronic effects toward Pd/HZSM-5 catalyst, leading to an enhancement of its activity and stability. On the contrary, Cu additive caused Pd/HZSM-5 to become poorer in activity and stability.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tang, Guoping; Zheng, Jianqiu; Xu, Xiaofeng

Soil organic carbon turnover to CO 2 and CH 4 is sensitive to soil redox potential and pH conditions. But, land surface models do not consider redox and pH in the aqueous phase explicitly, thereby limiting their use for making predictions in anoxic environments. Using recent data from incubations of Arctic soils, we extend the Community Land Model with coupled carbon and nitrogen (CLM-CN) decomposition cascade to include simple organic substrate turnover, fermentation, Fe(III) reduction, and methanogenesis reactions, and assess the efficacy of various temperature and pH response functions. Incorporating the Windermere Humic Aqueous Model (WHAM) enables us to approximatelymore » describe the observed pH evolution without additional parameterization. Though Fe(III) reduction is normally assumed to compete with methanogenesis, the model predicts that Fe(III) reduction raises the pH from acidic to neutral, thereby reducing environmental stress to methanogens and accelerating methane production when substrates are not limiting. Furthermore, the equilibrium speciation predicts a substantial increase in CO 2 solubility as pH increases, and taking into account CO 2 adsorption to surface sites of metal oxides further decreases the predicted headspace gas-phase fraction at low pH. Without adequate representation of these speciation reactions, as well as the impacts of pH, temperature, and pressure, the CO 2 production from closed microcosms can be substantially underestimated based on headspace CO 2 measurements only. Our results demonstrate the efficacy of geochemical models for simulating soil biogeochemistry and provide predictive understanding and mechanistic representations that can be incorporated into land surface models to improve climate predictions.« less

Innovative techniques for the production of energetic radicals for lunar processing including cold plasma processing of local planetary ores

NASA Technical Reports Server (NTRS)

Bullard, D.; Lynch, D. C.

1992-01-01

Hydrogen reduction of ilmenite has been studied by a number of investigators as a potential means for recovery of oxygen from lunar soil. Interest in this process has always rested with the simplicity of the flow diagram and the utilization of established technology. Effective utilization of hydrogen in the reduction process at temperatures of 1200 C and below has always been disappointing and, as such, has led other investigators to focus attention on other systems. Effective utilization of hydrogen in the reduction of ilmenite can be significantly enhanced in the presence of a non-equilibrium hydrogen plasma. Ilmenite at solid specimen temperatures of 600 C to 970 C were reacted in a hydrogen plasma. Those experiments revealed that hydrogen utilization can be significantly enhanced. At a specimen temperature of 850 C the fraction of H2 reacted was 24 percent compared to the 7 percent theoretical limit calculated with thermodynamic theory for the same temperature. An added advantage for a hydrogen plasma involves further reduction of TiO2. Reduction of the iron oxide in ilmenite yields TiO2 and metallic iron as by products. Titanium forms a number of oxides including TiO, Ti2O3, Ti3O5 and the Magneli oxides (Ti4O7 to Ti50O99). In conventional processing of ilmenite with hydrogen it is possible to reduce TiO2 to Ti7O13 within approximately an hour, but with poor utilization of hydrogen on the order of one mole of H2 per thousand. In the cold or non-equilibrium plasma TiO2 can be rapidly reduced to Ti2O3 with hydrogen utilization exceeding 10 percent. Based on design considerations of the plasma reactor greater utilization of the hydrogen in the reduction of TiO2 is possible.

Collision-induced Absorption in the Infrared: A Data Base for Modelling Planetary and Stellar Atmospheres

NASA Technical Reports Server (NTRS)

Borysow, Aleksandra

1998-01-01

Accurate knowledge of certain collision-induced absorption continua of molecular pairs such as H2-H2, H2-He, H2-CH4, CO2-CO2, etc., is a prerequisite for most spectral analyses and modelling attempts of atmospheres of planets and cold stars. We collect and regularly update simple, state of the art computer programs for the calculation of the absorption coefficient of such molecular pairs over a broad range of temperatures and frequencies, for the various rotovibrational bands. The computational results are in agreement with the existing laboratory measurements of such absorption continua, recorded with a spectral resolution of a few wavenumbers, but reliable computational results may be expected even in the far wings, and at temperatures for which laboratory measurements do not exist. Detailed information is given concerning the systems thus studied, the temperature and frequency ranges considered, the rotovibrational bands thus modelled, and how one may obtain copies of the FORTRAN77 computer programs by e-mail.

Effect of the Mn oxidation state and lattice oxygen in Mn-based TiO2 catalysts on the low-temperature selective catalytic reduction of NO by NH3.

PubMed

Lee, Sang Moon; Park, Kwang Hee; Kim, Sung Su; Kwon, Dong Wook; Hong, Sung Chang

2012-09-01

TiO2-supported manganese oxide catalysts formed using different calcination temperatures were prepared by using the wet-impregnation method and were investigated for their activity in the low-temperature selective catalytic reduction (SCR) of NO by NH3 with respect to the Mn valence and lattice oxygen behavior. The surface and bulk properties of these catalysts were examined using Brunauer-Emmett-Teller (BET) surface area, X-ray diffraction (XRD), temperature-programmed reduction (TPR), and temperature-programmed desorption (TPD). Catalysts prepared using lower calcination temperatures, which contained Mn4+ displayed high SCR activity at low temperatures and possessed several acid sites and active oxygen. The TPD analysis determined that the Brönsted and Lewis acid sites in the Mn/TiO2 catalysts were important for the low-temperature SCR at 80-160 and 200-350 degrees C, respectively. In addition, the available lattice oxygen was important for attaining high NO to NO2 oxidation at low temperatures. Recently, various Mn catalysts have been evaluated as SCR catalysts. However, there have been no studies on the relationship of adsorption and desorption properties and behavior of lattice oxygen according to the valence state for manganese oxides (MnO(x)). Therefore, in this study, the catalysts were prepared by the wet-impregnation method at different calcination temperatures in order to show the difference of manganese oxidation state. These catalysts were then characterized using various physicochemical techniques, including BET, XRD, TPR, and TPD, to understand the structure, oxidation state, redox properties, and adsorption and desorption properties of the Mn/TiO2 catalysts.

Nb-H system at high pressures and temperatures

NASA Astrophysics Data System (ADS)

Liu, Guangtao; Besedin, Stanislav; Irodova, Alla; Liu, Hanyu; Gao, Guoying; Eremets, Mikhail; Wang, Xin; Ma, Yanming

2017-03-01

We studied the Nb-H system over extended pressure and temperature ranges to establish the highest level of hydrogen abundance we could achieve from the resulting alloy. We probed the Nb-H system with laser heating and x-ray diffraction complemented by numerical density functional theory-based simulations. New quenched double hexagonal close-packed (hcp) Nb H2.5 appears under 46 GPa, and above 56 GPa cubic Nb H3 is formed as theoretically predicted. Nb atoms are arranged in close-packed lattices which are martensitically transformed in the sequence: face-centered cubic (fcc) → hcp → double hcp (dhcp) → distorted body-centered cubic (bcc) as pressure increases. The appearance of fcc Nb H2.5 -3 and dhcp Nb H2.5 cannot be understood in terms of enthalpic stability, but can be rationalized when finite temperatures are taken into account. The structural and compressional behavior of Nb Hx >2 is similar to that of NbH. Nevertheless, a direct H-H interaction emerges with hydrogen concentration increases, which manifests itself via a reduction in the lattice expansion induced by hydrogen dissolution.

Uranium oxide catalysts: environmental applications for treatment of chlorinated organic waste from nuclear industry.

PubMed

Lazareva, Svetlana; Ismagilov, Zinfer; Kuznetsov, Vadim; Shikina, Nadezhda; Kerzhentsev, Mikhail

2018-02-05

Huge amounts of nuclear waste, including depleted uranium, significantly contribute to the adverse environmental situation throughout the world. An approach to the effective use of uranium oxides in catalysts for the deep oxidation of chlorine-containing hydrocarbons is suggested. Investigation of the catalytic activity of the synthesized supported uranium oxide catalysts doped with Cr, Mn and Co transition metals in the chlorobenzene oxidation showed that these catalysts are comparable with conventional commercial ones. Physicochemical properties of the catalysts were studied by X-ray diffraction, temperature-programmed reduction with hydrogen (H 2 -TPR), and Fourier transform infrared spectroscopy. The higher activity of Mn- and Co-containing uranium oxide catalysts in the H 2 -TPR and oxidation of chlorobenzene in comparison with non-uranium catalysts may be related to the formation of a new disperse phase represented by uranates. The study of chlorobenzene adsorption revealed that the surface oxygen is involved in the catalytic process.

Temperature-dependent field-effect carrier mobility in organic thin-film transistors with a gate SiO2 dielectric modified by H2O2 treatment

NASA Astrophysics Data System (ADS)

Lin, Yow-Jon; Hung, Cheng-Chun

2018-02-01

The effect of the modification of a gate SiO2 dielectric using an H2O2 solution on the temperature-dependent behavior of carrier transport for pentacene-based organic thin-film transistors (OTFTs) is studied. H2O2 treatment leads to the formation of Si(-OH) x (i.e., the formation of a hydroxylated layer) on the SiO2 surface that serves to reduce the SiO2 capacitance and weaken the pentacene-SiO2 interaction, thus increasing the field-effect carrier mobility ( µ) in OTFTs. The temperature-dependent behavior of carrier transport is dominated by the multiple trapping model. Note that H2O2 treatment leads to a reduction in the activation energy. The increased value of µ is also attributed to the weakening of the interactions of the charge carriers with the SiO2 dielectric that serves to reduce the activation energy.

Changes in the morphology of interstellar ice analogues after hydrogen atom exposure.

PubMed

Accolla, Mario; Congiu, Emanuele; Dulieu, François; Manicò, Giulio; Chaabouni, Henda; Matar, Elie; Mokrane, Hakima; Lemaire, Jean Louis; Pirronello, Valerio

2011-05-07

The morphology of water ice in the interstellar medium is still an open question. Although accretion of gaseous water could not be the only possible origin of the observed icy mantles covering dust grains in cold molecular clouds, it is well known that water accreted from the gas phase on surfaces kept at 10 K forms ice films that exhibit a very high porosity. It is also known that in the dark clouds H(2) formation occurs on the icy surface of dust grains and that part of the energy (4.48 eV) released when adsorbed atoms react to form H(2) is deposited in the ice. The experimental study described in the present work focuses on how relevant changes of the ice morphology result from atomic hydrogen exposure and subsequent recombination. Using the temperature-programmed desorption (TPD) technique and a method of inversion analysis of TPD spectra, we show that there is an exponential decrease in the porosity of the amorphous water ice sample following D-atom irradiation. This decrease is inversely proportional to the thickness of the ice and has a value of ϕ(0) = 2 × 10(16) D-atoms cm(-2) per layer of H(2)O. We also use a model which confirms that the binding sites on the porous ice are destroyed regardless of their energy depth, and that the reduction of the porosity corresponds in fact to a reduction of the effective area. This reduction appears to be compatible with the fraction of D(2) formation energy transferred to the porous ice network. Under interstellar conditions, this effect is likely to be efficient and, together with other compaction processes, provides a good argument to believe that interstellar ice is amorphous and non-porous. This journal is © the Owner Societies 2011

Hydrogen production by tailoring the brookite and Cu2O ratio of sol-gel Cu-TiO2 photocatalysts.

PubMed

Hinojosa-Reyes, Mariana; Camposeco-Solís, Roberto; Zanella, Rodolfo; Rodríguez González, Vicente

2017-10-01

Cu-TiO 2 photocatalysts were prepared by the sol-gel method. Copper loadings from, 1.0 to 5.0 wt % were used. The materials were annealed at different temperatures (from 400 to 600 °C) to study the formation of brookite and copper ionic species. The photocatalysts were characterized by X-ray diffraction, UV-vis, Raman and XPS spectroscopies, H 2 -temperature programmed reduction (TPR), N 2 physisorption, and SEM-EDS to quantify the actual copper loadings and characterize morphology. The photocatalysts were evaluated during the hydrogen photocatalytic production using an ethanolic solution (50% v/v) under UV and visible radiation. The best hydrogen production was performed by Ti-Cu 1.0 with an overall hydrogen production that was five times higher than that obtained with photolysis. This sample had an optimal thermal treatment at 500 °C, and at this temperature, the Cu 2 O and brookite/anatase ratio boosted the photocatalytic production of hydrogen. In addition, a deactivation test was carried out for the most active sample (TiO 2 -Cu 1.0), showing unchanged H 2 production for three cycles with negligible Cu lixiviation. The activity of hydrogen-through-copper production reported in this research work is comparable with the one featured by noble metals and that reported in the literature for doped TiO 2 materials. Copyright © 2017 Elsevier Ltd. All rights reserved.

Enzymatic and spectroscopic properties of a thermostable [NiFe]‑hydrogenase performing H2-driven NAD+-reduction in the presence of O2.

PubMed

Preissler, Janina; Wahlefeld, Stefan; Lorent, Christian; Teutloff, Christian; Horch, Marius; Lauterbach, Lars; Cramer, Stephen P; Zebger, Ingo; Lenz, Oliver

2018-01-01

Biocatalysts that mediate the H 2 -dependent reduction of NAD + to NADH are attractive from both a fundamental and applied perspective. Here we present the first biochemical and spectroscopic characterization of an NAD + -reducing [NiFe]‑hydrogenase that sustains catalytic activity at high temperatures and in the presence of O 2 , which usually acts as an inhibitor. We isolated and sequenced the four structural genes, hoxFUYH, encoding the soluble NAD + -reducing [NiFe]‑hydrogenase (SH) from the thermophilic betaproteobacterium, Hydrogenophilus thermoluteolus TH-1 T (Ht). The HtSH was recombinantly overproduced in a hydrogenase-free mutant of the well-studied, H 2 -oxidizing betaproteobacterium Ralstonia eutropha H16 (Re). The enzyme was purified and characterized with various biochemical and spectroscopic techniques. Highest H 2 -mediated NAD + reduction activity was observed at 80°C and pH6.5, and catalytic activity was found to be sustained at low O 2 concentrations. Infrared spectroscopic analyses revealed a spectral pattern for as-isolated HtSH that is remarkably different from those of the closely related ReSH and other [NiFe]‑hydrogenases. This indicates an unusual configuration of the oxidized catalytic center in HtSH. Complementary electron paramagnetic resonance spectroscopic analyses revealed spectral signatures similar to related NAD + -reducing [NiFe]‑hydrogenases. This study lays the groundwork for structural and functional analyses of the HtSH as well as application of this enzyme for H 2 -driven cofactor recycling under oxic conditions at elevated temperatures. Copyright © 2017 Elsevier B.V. All rights reserved.

SNCR De-NOx within a moderate temperature range using urea-spiked hydrazine hydrate as reductant.

PubMed

Chen, H; Chen, D Z; Fan, S; Hong, L; Wang, D

2016-10-01

In this research, urea-spiked hydrazine hydrate solutions are used as reductants for the Selective Non-Catalytic Reduction (SNCR) De-NOx process below 650 °C. The urea concentration in the urea/hydrazine hydrate solutions is chosen through experimental and theoretical studies. To determine the mechanism of the De-NOx process, thermogravimetric analysis (TGA) of the urea/hydrazine hydrate solutions and their thermal decomposition in air and nitrogen atmospheres were studied to understand their decomposition behaviours and redox characteristics. Then a plug flow reactor (PFR) model was adopted to simulate the De-NOx processes in a pilot scale tubular reactor, and the calculated De-NOx efficiency vs. temperature profiles were compared with experimental results to support the mechanism and choose the proper reductant and its reaction temperature. Both the experimental and calculated results show that when the urea is spiked into hydrazine hydrate solution to make the urea-N content approximately 16.7%-25% of the total N content in the solution, better De-NOx efficiencies can be obtained in the temperature range of 550-650 °C, under which NH3 is inactive in reducing NOx. And it is also proved that for these urea-spiked hydrazine hydrate solutions, the hydrazine decomposition through the pathway N2H4 + M = N2H3 + H + M is enhanced to provide radical H, which is active to reduce NO. Finally, the reaction routes for SNCR De-NOx process based on urea-spiked hydrazine hydrate at the proper temperature are proposed. Copyright © 2016 Elsevier Ltd. All rights reserved.

Biogeochemical modeling of CO 2 and CH 4 production in anoxic Arctic soil microcosms

DOE PAGES

Tang, Guoping; Zheng, Jianqiu; Xu, Xiaofeng; ...

2016-09-12

Soil organic carbon turnover to CO 2 and CH 4 is sensitive to soil redox potential and pH conditions. But, land surface models do not consider redox and pH in the aqueous phase explicitly, thereby limiting their use for making predictions in anoxic environments. Using recent data from incubations of Arctic soils, we extend the Community Land Model with coupled carbon and nitrogen (CLM-CN) decomposition cascade to include simple organic substrate turnover, fermentation, Fe(III) reduction, and methanogenesis reactions, and assess the efficacy of various temperature and pH response functions. Incorporating the Windermere Humic Aqueous Model (WHAM) enables us to approximatelymore » describe the observed pH evolution without additional parameterization. Though Fe(III) reduction is normally assumed to compete with methanogenesis, the model predicts that Fe(III) reduction raises the pH from acidic to neutral, thereby reducing environmental stress to methanogens and accelerating methane production when substrates are not limiting. Furthermore, the equilibrium speciation predicts a substantial increase in CO 2 solubility as pH increases, and taking into account CO 2 adsorption to surface sites of metal oxides further decreases the predicted headspace gas-phase fraction at low pH. Without adequate representation of these speciation reactions, as well as the impacts of pH, temperature, and pressure, the CO 2 production from closed microcosms can be substantially underestimated based on headspace CO 2 measurements only. Our results demonstrate the efficacy of geochemical models for simulating soil biogeochemistry and provide predictive understanding and mechanistic representations that can be incorporated into land surface models to improve climate predictions.« less

Effects of Temperature and pH on Reduction of Bacteria in a Point-of-Use Drinking Water Treatment Product for Emergency Relief

PubMed Central

Marois-Fiset, Jean-Thomas; Carabin, Anne; Lavoie, Audrey

2013-01-01

The effects of temperature and pH on the water treatment performance of a point-of-use (POU) coagulant/disinfectant product were evaluated. Cold temperatures (∼5°C) reduced the bactericidal efficiency of the product with regard to Escherichia coli and total coliform log10 reductions. PMID:23335762

2001 NASA Seal/secondary Air System Workshop, Volume 1. Volume 1

NASA Technical Reports Server (NTRS)

Steinetz, Bruce M. (Editor); Hendricks, Robert C. (Editor)

2002-01-01

The 2001 NASA Seal/Secondary Air System Workshop covered the following topics: (i) overview of NASA's Vision for 21st Century Aircraft; (ii) overview of NASA-sponsored Ultra-Efficient Engine Technology (UEET); (iii) reviews of sealing concepts, test results, experimental facilities, and numerical predictions; and (iv) reviews of material development programs relevant to advanced seals development. The NASA UEET overview illustrates for the reader the importance of advanced technologies, including seals, in meeting future turbine engine system efficiency and emission goals. The NASA UEET program goals include an 8-to 15-percent reduction in fuel burn, a 15-percent reduction in CO2, a 70-percent reduction in NOx, CO, and unburned hydrocarbons, and a 30-dB noise reduction relative to program baselines. The workshop also covered several programs NASA is funding to investigate advanced reusable space vehicle technologies (X-38) and advanced space ram/scramjet propulsion systems. Seal challenges posed by these advanced systems include high-temperature operation, resiliency at the operating temperature to accommodate sidewall flexing, and durability to last many missions.

First-Principles Studies on Deoxidizing Mechanism of V2O5 via Hydrogen

NASA Astrophysics Data System (ADS)

Zhang, Yanning; Jin, Mengting

With its high melting point, good plasticity and good corrosion resistance at low temperatures, vanadium has been widely used in the industries of iron and steel, aviation, energy storage, etc. However, the traditional manufacturing technologies of pure vanadium are usually connected with complex manufacturing processes, high costs and serious environment pollution, which more or less hindered its further applications. Recently, hydrogen gas has been considered as a promising reducing agent of V2O5, but experimental studies of deoxidization process of V2O5 single crystal surfaces were found to be extremely difficult. In this work, we perform extensive ab initio studies on the structural and electronic properties of different V2O5 surfaces, as well as the adsorption sites, diffusion and desorption processes of H on these surfaces as a dependence of depth. We found that H atoms adsorb at oxygen site to form surface hydroxyl (OH-) and further to form H2O on V2O5(010) surfaces, and the latter is easier to be desorbed compared with the former. But the desorption of H2O causes significant surface reconstructions, which makes the further deoxidization of V2O5 difficult, particularly on the V2O5 single-layer. Our theoretical results are instructive for understandings of the reduction mechanism of V2O5 by using a green agent of H2, and furthermore for the design of new experiments. Work was supported by the startup fund of China Thousand Young Talents, and National Basic Research Program of China (973 program, No: 2013CB934700). The calculations were supported by Tianhe2-JK in Beijing Computational Science Research Center.

Pure-rotational H2 thermometry by ultrabroadband coherent anti-Stokes Raman spectroscopy.

PubMed

Courtney, Trevor L; Bohlin, Alexis; Patterson, Brian D; Kliewer, Christopher J

2017-06-14

Coherent anti-Stokes Raman spectroscopy (CARS) is a sensitive technique for probing highly luminous flames in combustion applications to determine temperatures and species concentrations. CARS thermometry has been demonstrated for the vibrational Q-branch and pure-rotational S-branch of several small molecules. Practical advantages of pure-rotational CARS, such as multi-species detection, reduction of coherent line mixing and collisional narrowing even at high pressures, and the potential for more precise thermometry, have motivated experimental and theoretical advances in S-branch CARS of nitrogen (N 2 ), for example, which is a dominant species in air-fed combustion processes. Although hydrogen (H 2 ) is of interest given its prevalence as a reactant and product in many gas-phase reactions, laser bandwidth limitations have precluded the extension of CARS thermometry to the H 2 S-branch. We demonstrate H 2 thermometry using hybrid femtosecond/picosecond pure-rotational CARS, in which a broadband pump/Stokes pulse enables simultaneous excitation of the set of H 2 S-branch transitions populated at flame temperatures over the spectral region of 0-2200 cm -1 . We present a pure-rotational H 2 CARS spectral model for data fitting and compare extracted temperatures to those from simultaneously collected N 2 spectra in two systems of study: a heated flow and a diffusion flame on a Wolfhard-Parker slot burner. From 300 to 650 K in the heated flow, the H 2 and N 2 CARS extracted temperatures are, on average, within 2% of the set temperature. For flame measurements, the fitted H 2 and N 2 temperatures are, on average, within 5% of each other from 300 to 1600 K. Our results confirm the viability of pure-rotational H 2 CARS thermometry for probing combustion reactions.

Pure-rotational H2 thermometry by ultrabroadband coherent anti-Stokes Raman spectroscopy

NASA Astrophysics Data System (ADS)

Courtney, Trevor L.; Bohlin, Alexis; Patterson, Brian D.; Kliewer, Christopher J.

2017-06-01

Coherent anti-Stokes Raman spectroscopy (CARS) is a sensitive technique for probing highly luminous flames in combustion applications to determine temperatures and species concentrations. CARS thermometry has been demonstrated for the vibrational Q-branch and pure-rotational S-branch of several small molecules. Practical advantages of pure-rotational CARS, such as multi-species detection, reduction of coherent line mixing and collisional narrowing even at high pressures, and the potential for more precise thermometry, have motivated experimental and theoretical advances in S-branch CARS of nitrogen (N2), for example, which is a dominant species in air-fed combustion processes. Although hydrogen (H2) is of interest given its prevalence as a reactant and product in many gas-phase reactions, laser bandwidth limitations have precluded the extension of CARS thermometry to the H2 S-branch. We demonstrate H2 thermometry using hybrid femtosecond/picosecond pure-rotational CARS, in which a broadband pump/Stokes pulse enables simultaneous excitation of the set of H2 S-branch transitions populated at flame temperatures over the spectral region of 0-2200 cm-1. We present a pure-rotational H2 CARS spectral model for data fitting and compare extracted temperatures to those from simultaneously collected N2 spectra in two systems of study: a heated flow and a diffusion flame on a Wolfhard-Parker slot burner. From 300 to 650 K in the heated flow, the H2 and N2 CARS extracted temperatures are, on average, within 2% of the set temperature. For flame measurements, the fitted H2 and N2 temperatures are, on average, within 5% of each other from 300 to 1600 K. Our results confirm the viability of pure-rotational H2 CARS thermometry for probing combustion reactions.

Formic acid acting as an efficient oxygen scavenger in four-electron reduction of oxygen catalyzed by a heterodinuclear iridium-ruthenium complex in water.

PubMed

Fukuzumi, Shunichi; Kobayashi, Takeshi; Suenobu, Tomoyoshi

2010-09-01

A heterodinuclear iridium-ruthenium complex [Ir(III)(Cp*)(H(2)O)(bpm)Ru(II)(bpy)(2)](SO(4))(2) (Cp* = eta(5)-pentamethyl-cyclopentadienyl, bpm = 2,2'-bipyrimidine, bpy = 2,2'-bipyridine) acts as an effective catalyst for removal of dissolved O(2) by the four-electron reduction of O(2) with formic acid in water at an ambient temperature.

2002 NASA Seal/Secondary Air System Workshop. Volume 1

NASA Technical Reports Server (NTRS)

Steinetz, Bruce M. (Editor); Hendricks, Robert C. (Editor)

2003-01-01

The 2002 NASA Seal/Secondary Air System Workshop covered the following topics: (i) Overview of NASA s perspective of aeronautics and space technology for the 21st century; (ii) Overview of the NASA-sponsored Ultra-Efficient Engine Technology (UEET), Turbine-Based Combined-Cycle (TBCC), and Revolutionary Turbine Accelator (RTA) programs; (iii) Overview of NASA Glenn's seal program aimed at developing advanced seals for NASA's turbomachinery, space propulsion, and reentry vehicle needs; (iv) Reviews of sealing concepts, test results, experimental facilities, and numerical predictions; and (v) Reviews of material development programs relevant to advanced seals development. The NASA UEET and TBCC/RTA program overviews illustrated for the reader the importance of advanced technologies, including seals, in meeting future turbine engine system efficiency and emission goals. For example, the NASA UEET program goals include an 8- to 15-percent reduction in fuel burn, a 15-percent reduction in CO2, a 70-percent reduction in NOx, CO, and unburned hydrocarbons, and a 30-dB noise reduction relative to program baselines. The workshop also covered several programs NASA is funding to investigate advanced reusable space vehicle technologies (X-38) and advanced space ram/scramjet propulsion systems. Seal challenges posed by these advanced systems include high-temperature operation, resiliency at the operating temperature to accommodate sidewall flexing, and durability to last many missions.

Alternative Antimicrobial Commercial Egg Washing Procedures.

PubMed

Hudson, Lauren K; Harrison, Mark A; Berrang, Mark E; Jones, Deana R

2016-07-01

Commercial table eggs are washed prior to packaging. Standard wash procedures use an alkaline pH and warm water. If a cool water method could be developed that would still provide a microbiologically safe egg, the industry may save energy costs associated with water heating. Four wash procedures were evaluated for Salmonella reduction: pH 11 at 48.9°C (industry standard), pH 11 at ambient temperature (∼20°C), pH 6 at 48.9°C, and pH 6 at ambient temperature. Alkaline washes contained potassium hydroxide-based detergent, while pH 6 washes contained approximately 200 ppm of chlorine and a proprietary chlorine stabilizer (T-128). When eggs were inoculated by immersion in a cell suspension of Salmonella Enteritidis and Salmonella Typhimurium, all treatments resulted in a slight and similar reduction of Salmonella numbers (approximately 0.77 log CFU/ml of shell emulsion reduction). When eggs were inoculated by droplet on the shell surface, Salmonella counts were reduced by approximately 5 log CFU when washed with chlorine plus the chlorine stabilizer at both temperatures and with the alkaline wash at the high temperature. The reductions in Salmonella by these treatments were not significantly (P > 0.05) different from each other but were significantly (P < 0.05) more than the reduction observed for the 20°C alkaline treatment and 20°C control water treatments. Ambient temperature acidic washes reduced Salmonella contamination to the same degree as the standard pH 11 warm water wash and may be a viable option to reduce cost, increase shelf life, and slow pathogen growth in and on shell eggs.

Photoinduced Reductive Elimination of H2 from the Nitrogenase Dihydride (Janus) State Involves a FeMo-cofactor-H2 Intermediate.

PubMed

Lukoyanov, Dmitriy; Khadka, Nimesh; Dean, Dennis R; Raugei, Simone; Seefeldt, Lance C; Hoffman, Brian M

2017-02-20

N 2 reduction by nitrogenase involves the accumulation of four reducing equivalents at the active site FeMo-cofactor to form a state with two [Fe-H-Fe] bridging hydrides (denoted E 4 (4H), the Janus intermediate), and we recently demonstrated that the enzyme is activated to cleave the N≡N triple bond by the reductive elimination (re) of H 2 from this state. We are exploring a photochemical approach to obtaining atomic-level details of the re activation process. We have shown that, when E 4 (4H) at cryogenic temperatures is subjected to 450 nm irradiation in an EPR cavity, it cleanly undergoes photoinduced re of H 2 to give a reactive doubly reduced intermediate, denoted E 4 (2H)*, which corresponds to the intermediate that would form if thermal dissociative re loss of H 2 preceded N 2 binding. Experiments reported here establish that photoinduced re primarily occurs in two steps. Photolysis of E 4 (4H) generates an intermediate state that undergoes subsequent photoinduced conversion to [E 4 (2H)* + H 2 ]. The experiments, supported by DFT calculations, indicate that the trapped intermediate is an H 2 complex on the ground adiabatic potential energy suface that connects E 4 (4H) with [E 4 (2H)* + H 2 ]. We suggest that this complex, denoted E 4 (H 2 ; 2H), is a thermally populated intermediate in the catalytically central re of H 2 by E 4 (4H) and that N 2 reacts with this complex to complete the activated conversion of [E 4 (4H) + N 2 ] into [E 4 (2N2H) + H 2 ].

Photoinduced Reductive Elimination of H 2 from the Nitrogenase Dihydride (Janus) State Involves a FeMo-cofactor-H 2 Intermediate

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lukoyanov, Dmitriy; Khadka, Nimesh; Dean, Dennis R.

N2 reduction by nitrogenase involves the accumulation of four reducing equivalents at the active site FeMo-cofactor to form a state with two [Fe-H-Fe] bridging hydrides (denoted E4(4H), the Janus intermediate), and we recently demonstrated that the enzyme is activated to cleave the N≡N triple bond by the reductive elimination (re) of H2 from this state. We are exploring a photochemical approach to obtaining atomic-level details of the re activation process. We have shown that when E4(4H) at cryogenic temperatures is subjected to 450 nm irradiation in an EPR cavity, it cleanly undergoes photoinduced re of H2 to give a reactivemore » doubly-reduced intermediate, denoted E4(2H)*, which corresponds to the intermediate that would form if thermal dissociative re loss of H2 preceded N2 binding. Experiments reported here establish that photoinduced re occurs in two steps. Photolysis of E4(4H) generates an intermediate state that undergoes subsequent photoinduced conversion to [E4(2H)* + H2]. The experiments, supported by DFT calculation, indicate that the trapped intermediate is an H2 complex on the ground adiabatic potential energy suface that connects E4(4H) with [E4(2H)* + H2]. We suggest this complex, denoted E4(H2; 2H), is a thermally populated intermediate in the catalytically central re of H2 by E4(4H), and that N2 reacts with this complex to complete the activated conversion of [E4(4H) + N2] into [E4(2N2H) + H2].« less

Microchannel Reactor System Design & Demonstration For On-Site H2O2 Production by Controlled H2/O2 Reaction

DOE Office of Scientific and Technical Information (OSTI.GOV)

Adeniyi Lawal

We successfully demonstrated an innovative hydrogen peroxide (H2O2) production concept which involved the development of flame- and explosion-resistant microchannel reactor system for energy efficient, cost-saving, on-site H2O2 production. We designed, fabricated, evaluated, and optimized a laboratory-scale microchannel reactor system for controlled direct combination of H2 and O2 in all proportions including explosive regime, at a low pressure and a low temperature to produce about 1.5 wt% H2O2 as proposed. In the second phase of the program, as a prelude to full-scale commercialization, we demonstrated our H2O2 production approach by ‘numbering up’ the channels in a multi-channel microreactor-based pilot plant tomore » produce 1 kg/h of H2O2 at 1.5 wt% as demanded by end-users of the developed technology. To our knowledge, we are the first group to accomplish this significant milestone. We identified the reaction pathways that comprise the process, and implemented rigorous mechanistic kinetic studies to obtain the kinetics of the three main dominant reactions. We are not aware of any such comprehensive kinetic studies for the direct combination process, either in a microreactor or any other reactor system. We showed that the mass transfer parameter in our microreactor system is several orders of magnitude higher than what obtains in the macroreactor, attesting to the superior performance of microreactor. A one-dimensional reactor model incorporating the kinetics information enabled us to clarify certain important aspects of the chemistry of the direct combination process as detailed in section 5 of this report. Also, through mathematical modeling and simulation using sophisticated and robust commercial software packages, we were able to elucidate the hydrodynamics of the complex multiphase flows that take place in the microchannel. In conjunction with the kinetics information, we were able to validate the experimental data. If fully implemented across the whole industry as a result of our technology demonstration, our production concept is expected to save >5 trillion Btu/year of steam usage and >3 trillion Btu/year in electric power consumption. Our analysis also indicates >50 % reduction in waste disposal cost and ~10% reduction in feedstock energy. These savings translate to ~30% reduction in overall production and transportation costs for the $1B annual H2O2 market.« less

Ni-H2 cell characterization for INTELSAT programs

NASA Technical Reports Server (NTRS)

Dunnet, Andrew F.; Earl, Martin W.

1994-01-01

Various Ni/H2 cell designs manufactured for INTELSAT Programs during the past decade have been characterized electrically as a function of temperature. The resulting data for these INTELSAT V, VI, VII and VIIA cells are assembled in a manner which allows ready comparison of performance. Also included is a detailed description of each design.

Thermochemical Properties of the Lattice Oxygen in W,Mn-Containing Mixed Oxide Catalysts for the Oxidative Coupling of Methane

NASA Astrophysics Data System (ADS)

Lomonosov, V. I.; Gordienko, Yu. A.; Sinev, M. Yu.; Rogov, V. A.; Sadykov, V. A.

2018-03-01

Mixed NaWMn/SiO2 oxide, samples containing individual components (Na, W, Mn) and their double combinations (Na-W, Na-Mn, W-Mn) supported on silica were studied by temperature programmed reduction (TPR) and desorption (TPD), and heat flow calorimetry during their reoxidation with molecular oxygen in pulse mode. The NaWMn/SiO2 mixed oxide was shown to contain two different types of reactive lattice oxygen. The weakly-bonded oxygen can be reversibly released from the oxide in a flow of inert gas in the temperature range of 575‒900°C, while the strongly-bonded oxygen can be removed during the reduction of the sample with hydrogen at 700-900°C. The measured thermal effect of oxygen consumption for these two oxygen forms are 185 and 350 kJ/mol, respectively. The amount of oxygen removed at reduction ( 443 μmol/g) considerably exceeded the amount desorbed in an inert gas flow ( 56 μmol/g). The obtained results suggest that the reversible oxygen desorption is due to the redox process in which manganese ions are involved, while during the temperature programmed reduction, mainly oxygen bonded with tungsten is removed.

Zr/ZrO2 sensors for in situ measurement of pH in high-temperature and -pressure aqueous solutions.

PubMed

Zhang, R H; Zhang, X T; Hu, S M

2008-04-15

The aim of this study is to develop new pH sensors that can be used to test and monitor hydrogen ion activity in hydrothermal conditions. A Zr/ZrO2 oxidation electrode is fabricated for in situ pH measurement of high-temperature aqueous solutions. This sensor responds rapidly and precisely to pH over a wide range of temperature and pressure. The Zr/ZrO2 electrode was made by oxidizing zirconium metal wire with Na2CO3 melt, which produced a thin film of ZrO2 on its surface. Thus, an oxidation-reduction electrode was produced. The Zr/ZrO2 electrode has a good electrochemical stability over a wide range of pH in high-temperature aqueous solutions when used with a Ag/AgCl reference electrode. Measurements of the Zr/ZrO2 sensor potential against a Ag/AgCl reference electrode is shown to vary linearly with pH between temperatures 20 and 200 degrees C. The slope of the potential versus pH at high temperature is slightly below the theoretical value indicated by the Nernst equation; such deviation is attributed to the fact that the sensor is not strictly at equilibrium with the solution to be tested in a short period of time. The Zr/ZrO2 sensor can be calibrated over the conditions that exist in the natural deep-seawater. Our studies showed that the Zr/ZrO2 electrode is a suitable pH sensor for the hydrothermal systems at midocean ridge or other geothermal systems with the high-temperature environment. Yttria-stabilized zirconia sensors have also been used to investigate the pH of hydrothermal fluids in hot springs vents at midocean ridge. These sensors, however, are not sensitive below 200 degrees C. Zr/ZrO2 sensors have wider temperature range and can be severed as good alternative sensors for measuring the pH of hydrothermal fluids.

Sensitivity of surface temperature and atmospheric temperature to perturbations in the stratospheric concentration of ozone and nitrogen dioxide

NASA Technical Reports Server (NTRS)

Ramanathan, V.; Callis, L. B.; Boughner, R. E.

1976-01-01

A radiative-convective model is proposed for estimating the sensitivity of the atmospheric radiative heating rates and atmospheric and surface temperatures to perturbations in the concentration of O3 and NO2 in the stratosphere. Contribution to radiative energy transfer within the atmosphere from H2O, CO2, O3, and NO2 is considered. It is found that the net solar radiation absorbed by the earth-atmosphere system decreases with a reduction in O3; if the reduction of O3 is accompanied by an increase in NO2, there is a compensating effect due to solar absorption by NO2. The surface temperature and atmospheric temperature decrease with decreasing stratospheric O3. Another major conclusion is the strong sensitivity of surface temperature to the vertical distribution of O3 within the atmosphere. The results should be considered as reflecting the sensitivity of the proposed model rather than the sensitivity of the actual earth-atmosphere system.

Facile synthesis of high surface area molybdenum nitride and carbide

DOE Office of Scientific and Technical Information (OSTI.GOV)

Roy, Aaron; Serov, Alexey; Artyushkova, Kateryna

2015-08-15

The synthesis of high surface area γ-Mo{sub 2}N and α-Mo{sub 2}C is reported (116 and 120 m{sup 2}/g) without the temperature programmed reduction of MoO{sub 3}. γ-Mo{sub 2}N was prepared in an NH{sub 3}-free synthesis using forming gas (7 at% H{sub 2}, N{sub 2}-balance) as the reactive atmosphere. Three precursors were studied ((NH{sub 4}){sub 6}Mo{sub 7}O{sub 24}·4H{sub 2}O, (NH{sub 4}){sub 2} Mg(MoO{sub 4}){sub 2}, and MgMoO{sub 4}) along with the sacrificial support method (SSM) as a means of reducing the particle size of Mo{sub 2}N and Mo{sub 2}C. In situ X-ray diffraction (XRD) studies were carried out to identify reactionmore » intermediates, the temperature at which various intermediates form, and the average domain size of the Mo{sub 2}N products. Materials were synthesized in bulk and further characterized by XRD, HRTEM, XPS, and BET. - Highlights: • Facile synthesis of γ-Mo2N and α-Mo2C with surface area exceeding 100 m{sup 2}/g. • Sacrificial support method was used to achieve these high surface areas. • Materials can serve as catalysts or supports in (electro)chemical processes.« less

Temperature and pH effect on reduction of graphene oxides in aqueous solution

NASA Astrophysics Data System (ADS)

Tai, Guoan; Zeng, Tian; Li, Hongxiang; Liu, Jinsong; Kong, Jizhou; Lv, Fuyong

2014-09-01

Reduced graphene oxides (RGOs) have usually been obtained by hydrazine reduction, but hydrazine-related compounds are corrosive, highly flammable and very hazardous, and the obtained RGOs heavily aggregated. Here we investigated extensively the effect of temperature and pH value on the structure of RGOs in hydrothermal environments without any reducing agents. The attenuated total reflectance Fourier transform infrared (ATR-FTIR) spectra showed that reduction rate of GOs remarkably increased with the temperature from 100 to 180 °C and with pH value from 3 to 10. Field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM) exhibited the structural transition of the RGOs. Energy-dispersive x-ray analysis (EDX) showed the reduction degree of the RGO samples quantitatively. The results demonstrate that the GOs can be reduced controllably by a hydrothermal reduction process at pH value of 10 at 140 °C, and the large-scale RGOs are cut into small nanosheets with size from several to a few tens of nanometers with increasing temperature and duration. This study provides a feasible approach to controllably reduce GO with different nanostructures such as porous structures and quantum dots for applications in optoelectronics and biomedicals.

Kinetics and mechanisms of iron sulfide reductions in hydrogen and in carbon monoxide

USGS Publications Warehouse

Wiltowski, T.; Hinckley, C.C.; Smith, Gerard V.; Nishizawa, T.; Saporoschenko, Mykola; Shiley, R.H.; Webster, J.R.

1987-01-01

The reduction of iron sulfides by hydrogen and by carbon monoxide has been studied using plug flow and thermogravimetric methods. The reactions were studied in the 523-723??K temperature range and were found to be first-order processes. Plug flow studies were used to correlate reaction rates between pyrite and the gases as a function of the surface area of the pyrite. The rate of H2S formation increases with the surface area of the pyrite sample. The results of thermogravimetric experiments indicate that the reactions consist of several steps. Rate constants for the pyrite reduction by H2 and by CO were obtained. The activation energies increased with degree of reduction. Values of Ea were 113.2 (step I) and 122.5 kJ/mole (step II) for pyrite reduction with CO and 99.4 (step I), 122.4 (step II), 125.2 (step III), and 142.6 kJ/mole (step IV) for pyrite reduction with hydrogen. ?? 1987.

Radiative cooling to deep sub-freezing temperatures through a 24-h day-night cycle

NASA Astrophysics Data System (ADS)

Chen, Zhen; Zhu, Linxiao; Raman, Aaswath; Fan, Shanhui

2016-12-01

Radiative cooling technology utilizes the atmospheric transparency window (8-13 μm) to passively dissipate heat from Earth into outer space (3 K). This technology has attracted broad interests from both fundamental sciences and real world applications, ranging from passive building cooling, renewable energy harvesting and passive refrigeration in arid regions. However, the temperature reduction experimentally demonstrated, thus far, has been relatively modest. Here we theoretically show that ultra-large temperature reduction for as much as 60 °C from ambient is achievable by using a selective thermal emitter and by eliminating parasitic thermal load, and experimentally demonstrate a temperature reduction that far exceeds previous works. In a populous area at sea level, we have achieved an average temperature reduction of 37 °C from the ambient air temperature through a 24-h day-night cycle, with a maximal reduction of 42 °C that occurs when the experimental set-up enclosing the emitter is exposed to peak solar irradiance.

Sustained Low Temperature NOx Reduction

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zha, Yuhui

Increasing regulatory, environmental, and customer pressure in recent years led to substantial improvements in the fuel efficiency of diesel engines, including the remarkable breakthroughs demonstrated through the Super Truck program supported by the U.S. Department of Energy (DOE). On the other hand, these improvements have translated into a reduction of exhaust gas temperatures, thus further complicating the task of controlling NOx emissions, especially in low power duty cycles. The need for improved NOx conversion over these low temperature duty cycles is also observed as requirements tighten with in-use emissions testing. Sustained NOx reduction at low temperatures, especially in the 150-200oCmore » range, shares some similarities with the more commonly discussed cold-start challenge, however poses a number of additional and distinct technical problems. In this project we set a bold target of achieving and maintaining a 90% NOx conversion at the SCR catalyst inlet temperature of 150oC. The project is intended to push the boundaries of the existing technologies, while staying within the realm of realistic future practical implementation. In order to meet the resulting challenges at the levels of catalyst fundamentals, system components, and system integration, Cummins has partnered with the DOE, Johnson Matthey, and Pacific Northwest National Lab and initiated the Sustained Low-Temperature NOx Reduction program at the beginning of 2015. Through this collaboration, we are exploring catalyst formulations and catalyst architectures with enhanced catalytic activity at 150°C; opportunities to approach the desirable ratio of NO and NO2 in the SCR feed gas; options for robust low-temperature reductant delivery; and the requirements for overall system integration. The program is expected to deliver an on-engine demonstration of the technical solution and an assessment of its commercial potential. In the SAE meeting, we will share the initial performance data on engine to highlight the path to achieve 90% NOx conversion at the SCR inlet temperature of 150oC.« less

The preparation and activity of Cu-Fe-Zr-Ce based catalysts for water gas shift

NASA Astrophysics Data System (ADS)

Wu, H. D.; Liu, T. S.; Liu, H. Z.

2018-01-01

CeO2-ZrO2 composite oxide was synthesized with precipitation method as support and CuaFeb(ZrCe4)8Ox catalysts were prepared by impregnation; X-ray diffraction, H2 temperature program reduction, and scanning electron microscope techniques were jointly used to characterize the crystal phases and reduction properties of catalysts. Then the activity of catalysts in water gas shift was studied, thus investigated how catalyst composition impacted the water gas shift. Conclusions drew from the results can be briefly stated. CuaFeb(ZrCe4)8Ox was provided with stable cubic crystalline framework and Cu and Fe, as the active components, was highly dispersed on the surface of supports in the form of CuO and Fe2O3 respectively. The strong interactions between copper and iron component enhanced the reducing capacity of CuO and Fe2O3. CuaFeb(ZrCe4)8Ox catalysts exhibited high catalytic activity and selectivity while the main active components were Cu and Fe3O4. The CO conversion rate reached 96% when Cu7Fe3(ZrCe4)8Ox catalysts was used in water gas shift at 623K and the only products were H2 and CO2. The activity was still desirable even the catalysts was applied at 723K.

Fabrication of porous silicon nanowires by MACE method in HF/H2O2/AgNO3 system at room temperature

PubMed Central

2014-01-01

In this paper, the moderately and lightly doped porous silicon nanowires (PSiNWs) were fabricated by the ‘one-pot procedure’ metal-assisted chemical etching (MACE) method in the HF/H2O2/AgNO3 system at room temperature. The effects of H2O2 concentration on the nanostructure of silicon nanowires (SiNWs) were investigated. The experimental results indicate that porous structure can be introduced by the addition of H2O2 and the pore structure could be controlled by adjusting the concentration of H2O2. The H2O2 species replaces Ag+ as the oxidant and the Ag nanoparticles work as catalyst during the etching. And the concentration of H2O2 influences the nucleation and motility of Ag particles, which leads to formation of different porous structure within the nanowires. A mechanism based on the lateral etching which is catalyzed by Ag particles under the motivation by H2O2 reduction is proposed to explain the PSiNWs formation. PMID:24910568

H2 enrichment from synthesis gas by Desulfotomaculum carboxydivorans for potential applications in synthesis gas purification and biodesulfurization.

PubMed

Sipma, Jan; Osuna, M Begoña; Parshina, Sofiya N; Lettinga, Gatze; Stams, Alfons J M; Lens, Piet N L

2007-08-01

Desulfotomaculum carboxydivorans, recently isolated from a full-scale anaerobic wastewater treatment facility, is a sulfate reducer capable of hydrogenogenic growth on carbon monoxide (CO). In the presence of sulfate, the hydrogen formed is used for sulfate reduction. The organism grows rapidly at 200 kPa CO, pH 7.0, and 55 degrees C, with a generation time of 100 min, producing nearly equimolar amounts of H(2) and CO(2) from CO and H(2)O. The high specific CO conversion rates, exceeding 0.8 mol CO (g protein)(-1) h(-1), makes this bacterium an interesting candidate for a biological alternative of the currently employed chemical catalytic water-gas shift reaction to purify synthesis gas (contains mainly H(2), CO, and CO(2)). Furthermore, as D. carboxydivorans is capable of hydrogenotrophic sulfate reduction at partial CO pressures exceeding 100 kPa, it is also a good candidate for biodesulfurization processes using synthesis gas as electron donor at elevated temperatures, e.g., in biological flue gas desulfurization. Although high maximal specific sulfate reduction rates (32 mmol (g protein)(-1) h(-1)) can be obtained, its sulfide tolerance is rather low and pH dependent, i.e., maximally 9 and 5 mM sulfide at pH 7.2 and pH 6.5, respectively.

Mesoporous Hollow Ge Microspheres Prepared via Molten-Salt Metallothermic Reaction for High-Performance Li-Storage Anode.

PubMed

Lin, Ning; Li, Tieqiang; Han, Ying; Zhang, Qianliang; Xu, Tianjun; Qian, Yitai

2018-03-14

Generally, Ge-based anodes are prepared by metallothermic reduction of GeO 2 with Mg at 650 °C. Herein, a molten-salt system is developed a low-temperature metallothermic reduction of GeO 2 to prepare nanostructured Ge based anode materials. Typically, mesoporous hollow Ge microspheres are prepared by reduction of GeO 2 with metallic Mg in molten ZnCl 2 (mp 292) at 350 °C. Monodispersed Ge particles are synthesized through reduction of GeO 2 with Mg in molten AlCl 3 (mp 192 °C) at 250 °C. The meso-porous Ge anode delivers the reversible capacity of 1291 mA h g -1 at 0.2 C after 150 cycles with a retention of 97.3%, 1217 mA h g -1 at 0.8 C after 400 cycles with a retention of 91.9%, and superior rate capability with a capacity of 673 mA h g -1 even at 10 C. Then, the reaction mechanism and full-cell performance of as-prepared Ge anodes are studied systemically.

The structure and stability of aqueous rare-earth elements in hydrothermal fluids: New results on neodymium(III) aqua and chloroaqua complexes in aqueous solutions to 500 °C and 520 MPa

USGS Publications Warehouse

Mayanovic, Robert A.; Anderson, Alan J.; Bassett, William A.; Chou, I.-Ming

2009-01-01

X-ray absorption spectroscopy (XAS) measurements were made at the Nd L3-edge on neodymium(III) aqua and chloroaqua complexes in low pH aqueous solutions from 25 to 500????C and up to 520??MPa. Analysis of the extended X-ray absorption fine structure of the XAS spectra measured from a 0.07??m Nd/0.16??m HNO3 aqueous solution reveals a contraction of the Nd-O distance of the Nd3+ aqua ion at a uniform rate of ~ 0.013????/100????C and a uniform reduction of the number of coordinated H2O molecules from 10.0 ?? 0.9 to 7.4 ?? 0.9 over the range from 25 to 500????C and up to 370??MPa. The rate of reduction of the first-shell water molecules with temperature for Nd3+ (26%) is intermediate between the rate for the Gd3+ aqua ion (22% from 25 to 500????C) and the rates for the Eu3+ (29% from 25 to 400????C) and the Yb3+ aqua ions (42% from 25 to 500????C) indicating an intermediate stability of the Nd3+ aqua ion consistent with the tetrad effect. Nd L3-edge XAS measurements of 0.05??m NdCl3 aqueous solution at 25 to 500????C and up to 520??MPa show that stepwise inner-sphere complexes most likely of the type Nd(H2O)?? - nCln+3 - n occur in the solution at elevated temperatures, where ?? ??? 9 at 150????C decreasing to ~ 6 at 500????C and the number of chloride ions (n) of the chloroaqua complexes increases uniformly with temperature from 1.2 ?? 0.2 to 2.0 ?? 0.2 in the solution upon increase of temperature from 150 to 500????C. Conversely, the number of H2O ligands of Nd(H2O)?? - nCln+3 - n complexes is uniformly reduced with temperature from 7.5 ?? 0.8 to 3.7 ?? 0.3 in the aqueous solution, in the same temperature range. These data show greater stability of neodymium(III) than gadolinium(III) and ytterbium(III) chloride complexes in low pH aqueous solutions at elevated temperatures. Our data suggest a greater stability of aqueous light REE than that of heavy REE chloride complexes in low pH fluids at elevated temperatures consistent with REE analysis of fluids from deep-sea hydrothermal vents. ?? 2008 Elsevier B.V.

Effect of Ce/Zr molar ratio on the performance of Cu–Ce{sub x}–Zr{sub 1−x}/TiO{sub 2} catalyst for selective catalytic reduction of NO{sub x} with NH{sub 3} in diesel exhaust

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sun, Xiaoliang; Gong, Cairong, E-mail: gcr@tju.edu.cn; Lv, Gang

2014-12-15

Graphical abstract: The Cu–Ce{sub 0.25}–Zr{sub 0.75}/TiO{sub 2} catalyst exhibited excellent SCR activity at 165–450 °C within the range of exhaust temperatures of diesel engines. - Highlights: • Cu–Ce{sub x}–Zr{sub 1−x}/TiO{sub 2} catalysts were prepared by a wet impregnation method. • The property for NH{sub 3}-selective catalytic reduction of NO{sub x} were investigated. • The Ce/Zr molar ratio had effects on the performance of Cu–Ce–Zr/TiO{sub 2} catalysts. • The Cu–Ce{sub 0.25}–Zr{sub 0.75}/TiO{sub 2} sample exhibited 100% NO{sub x} conversion between 165 °C and 450 °C. • The factors that govern the activity enhancement were extensively investigated. - Abstract: Copper–cerium–zirconium catalysts loadedmore » on TiO{sub 2} prepared by a wet impregnation method were investigated for NH{sub 3}-selective catalytic reduction of NO{sub x}, aiming to study the effects of the Ce/Zr molar ratio on the performance of Cu–Ce–Zr/TiO{sub 2} catalysts. The Cu–Ce{sub 0.25}–Zr{sub 0.75}/TiO{sub 2} sample exhibited nearly 100% NO{sub x} conversion over a wide temperature range (165–450 °C), which is strikingly superior to that of Cu/TiO{sub 2} (210–389 °C) within the range of exhaust temperatures of diesel engines. The factors that govern the activity enhancement were extensively investigated by using a series of characterization techniques, namely X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS) and temperature-programmed reduction by hydrogen (H{sub 2}-TPR). The results showed that the addition of zirconium and/or cerium refined the copper dispersion, prevented copper crystallization and partially incorporated the copper ions into the zirconia (ceira) lattice, which led to enhance the redox abilities of Cu–Ce–Zr/TiO{sub 2} catalysts.« less

A metabolic hypothesis for the evolution of temperature effects on the arterial PCO2  and pH of vertebrate ectotherms.

PubMed

Hillman, Stanley S; Hedrick, Michael S

2018-01-04

Body temperature increases in ectothermic vertebrates characteristically lead to both increases in arterial P CO 2  ( P a CO 2 ) and declines in resting arterial pH (pHa) of about 0.017 pH units per 1°C increase in temperature. This 'alphastat' pH pattern has previously been interpreted as being evolutionarily driven by the maintenance of a constant protonation state on the imidazole moiety of histidine protein residues, hence stabilizing protein structure-function. Analysis of the existing data for interclass responses of ectothermic vertebrates shows different degrees of P a CO 2  increases and pH declines with temperature between the classes, with reptiles>amphibians>fish. The P a CO 2  at the temperature where maximal aerobic metabolism ( V̇ O 2 ,max ) is achieved is significantly and positively correlated with temperature for all vertebrate classes. For ectotherms, the P a CO 2  where V̇ O 2 ,max is greatest is also correlated with V̇ O 2 ,max , indicating there is an increased driving force for CO 2 efflux that is lowest in fish, intermediate in amphibians and highest in reptiles. The pattern of increased P a CO 2  and the resultant reduction of pHa in response to increased body temperature would serve to increase CO 2 efflux, O 2 delivery and blood buffering capacity and maintain ventilatory scope. This represents a new hypothesis for the selective advantage of arterial pH regulation from a systems physiology perspective in addition to the advantages of maintenance of protein structure-function. © 2018. Published by The Company of Biologists Ltd.

Low-temperature, high yield synthesis, and convenient isolation of the high-electron-density cluster compound Ta6Br14.8H2O for use in biomacromolecular crystallographic phase determination.

PubMed

Hay, Daniel N T; Messerle, Louis

2002-09-01

Reduction of TaBr(5) with Ga in the presence of KBr in a sealed borosilicate ampule at 400 degrees, followed by aqueous Soxhlet extraction and addition of stannous bromide and hydrobromic acid to the extract, yielded Ta(6)Br(14).8H(2)O in 80-84% yield. The new procedure provides a convenient, low temperature, high yield route to the synthesis of the title compound from inexpensive precursors.

Effects of low-Z and high-Z impurities on divertor detachment and plasma confinement

DOE PAGES

Wang, H. Q.; Guo, Houyang Y.; Petrie, Thomas W.; ...

2017-03-18

The impurity-seeded detached divertor is essential for heat exhaust in ITER and other reactor-relevant devices. Dedicated experiments with injection of N 2, Ne and Ar have been performed in DIII-D to assess the impact of the different impurities on divertor detachment and confinement. Seeding with N 2, Ne and Ar all promote divertor detachment, greatly reducing heat flux near the strike point. The upstream plasma density at the onset of detachment decreases with increasing impurity-puffing flow rates. For all injected impurity species, the confinement and pedestal pressure are correlated with the impurity content and the ratio of separatrix loss powermore » to the L-H transition threshold power. As the divertor plasma approaches detachment, the high-Z impurity seeding tends to degrade the core confinement owing to the increased core radiation. In particular, Ar injection leads to an increase in core radiation, up to 50% of the injected power, and a reduction in pedestal temperature over 60%, thus significantly degrading the confinement, i.e., with H 98 reducing from 1.1 to below 0.7. As for Ne seeding, H 98 near 0.8 can be maintained during the detachment phase with the pedestal temperature being reduced by about 50%. In contrast, in the N 2 seeded plasmas, radiation is predominately confined in the boundary plasma, with up to 50% of heating power being radiated in the divertor region and less than 25% in the core at the onset of detachment. In the case of strong N 2 gas puffing, the confinement recovers during the detachment, from ~20% reduction at the onset of the detachment to greater than that before the seeding. The core and pedestal temperatures feature a reduction of 30% from the initial attached phase and remain nearly constant during the detachment phase. The improvement in confinement appears to arise from the increase in pedestal and core density despite the temperature reduction.« less

Observations of the temperature dependent response of ozone to NOx reductions in the Sacramento, CA urban plume

NASA Astrophysics Data System (ADS)

Lafranchi, B. W.; Goldstein, A. H.; Cohen, R. C.

2011-07-01

Observations of NOx in the Sacramento, CA region show that mixing ratios decreased by 30 % between 2001 and 2008. Here we use an observation-based method to quantify net ozone (O3) production rates in the outflow from the Sacramento metropolitan region and examine the O3 decrease resulting from reductions in NOx emissions. This observational method does not rely on assumptions about detailed chemistry of ozone production, rather it is an independent means to verify and test these assumptions. We use an instantaneous steady-state model as well as a detailed 1-D plume model to aid in interpretation of the ozone production inferred from observations. In agreement with the models, the observations show that early in the plume, the NOx dependence for Ox (Ox = O3 + NO2) production is strongly coupled with temperature, suggesting that temperature-dependent biogenic VOC emissions and other temperature-related effects can drive Ox production between NOx-limited and NOx-suppressed regimes. As a result, NOx reductions were found to be most effective at higher temperatures over the 7 year period. We show that violations of the California 1-h O3 standard (90 ppb) in the region have been decreasing linearly with decreases in NOx (at a given temperature) and predict that reductions of NOx concentrations (and presumably emissions) by an additional 30 % (relative to 2007 levels) will eliminate violations of the state 1 h standard in the region. If current trends continue, a 30 % decrease in NOx is expected by 2012, and an end to violations of the 1 h standard in the Sacramento region appears to be imminent.

The survivability of Bacillus anthracis (Sterne strain) in processed liquid eggs.

PubMed

Khan, Saeed A; Sung, Kidon; Nawaz, Mohamed S; Cerniglia, Carl E; Tamplin, Mark L; Phillips, Robert W; Kelley, Lynda Collins

2009-04-01

In this study, we investigated the survival and inactivation kinetics of a surrogate strain of Bacillus anthracis (Sterne strain) in whole egg (WE), egg white (EW), sugared egg yolk (YSU), and salted egg yolk (YSA) at low (-20, 0, and 5 degrees C), moderate (15, 20, 25, 30, 35, and 40 degrees C), and high storage temperatures (45, 50, 55, and 60 degrees C). Outgrowth of the spores was measured as lag phase duration (LPD). Replication of vegetative cells was measured in terms of growth rate (GR) and maximum population density (MPD). Spore inactivation was recorded as inactivation rate and percent reduction in viable count. In general, spore viability decreased at low and high temperatures and increased at moderate temperatures. At 0 and 5 degrees C, a 60-100% reduction in spore viability was seen within 2-3 weeks in WE and YSU, 0-30% in YSA, and 50-100% in EW. At -20 degrees C, however, no drop in spore titer was observed in YSU and EW but a 20% drop in titer was seen in YSA and 50% in WE within 2-3 weeks. At high temperatures, WE, EW, and YSA produced a 20-50% drop in the spore titer within 1-4h whereas YSU showed 100% inactivation within 0.75 h. At moderate storage temperatures, as the temperature increased from 15 to 40 degrees C, LPD decreased from 13.5 to 0.75 h and MPD reached 0.27-2.2 x1 0(9) CFU/ml in YSU and WE, respectively. Markedly lower growth was observed in YSA (LPD=24-270 h, MPD=9 x 10(5) CFU/ml) and spores were inactivated completely within 1-6h in EW. The survivability and inactivation data of B. anthracis in liquid egg products reported in this investigation will be helpful in developing risk assessment models on food biosecurity.

2004 NASA Seal/Secondary Air System Workshop, Volume 1

NASA Technical Reports Server (NTRS)

2005-01-01

The 2004 NASA Seal/Secondary Air System workshop covered the following topics: (1) Overview of NASA s new Exploration Initiative program aimed at exploring the Moon, Mars, and beyond; (2) Overview of the NASA-sponsored Ultra-Efficient Engine Technology (UEET) program; (3) Overview of NASA Glenn s seal program aimed at developing advanced seals for NASA s turbomachinery, space, and reentry vehicle needs; (4) Reviews of NASA prime contractor and university advanced sealing concepts including tip clearance control, test results, experimental facilities, and numerical predictions; and (5) Reviews of material development programs relevant to advanced seals development. The NASA UEET overview illustrated for the reader the importance of advanced technologies, including seals, in meeting future turbine engine system efficiency and emission goals. For example, the NASA UEET program goals include an 8- to 15-percent reduction in fuel burn, a 15-percent reduction in CO2, a 70-percent reduction in NOx, CO, and unburned hydrocarbons, and a 30-dB noise reduction relative to program baselines. The workshop also covered several programs NASA is funding to develop technologies for the Exploration Initiative and advanced reusable space vehicle technologies. NASA plans on developing an advanced docking and berthing system that would permit any vehicle to dock to any on-orbit station or vehicle, as part of NASA s new Exploration Initiative. Plans to develop the necessary mechanism and androgynous seal technologies were reviewed. Seal challenges posed by reusable re-entry space vehicles include high-temperature operation, resiliency at temperature to accommodate gap changes during operation, and durability to meet mission requirements.

Progress in high-temperature oven development for 28 GHz electron cyclotron resonance ion source

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ohnishi, J., E-mail: ohnishi@riken.jp; Higurashi, Y.; Nakagawa, T.

2016-02-15

We have been developing a high-temperature oven using UO{sub 2} in the 28 GHz superconducting electron cyclotron resonance ion source at RIKEN since 2013. A total of eleven on-line tests were performed. The longest operation time in a single test was 411 h, and the consumption rate of UO{sub 2} was approximately 2.4 mg/h. In these tests, we experienced several problems: the ejection hole of a crucible was blocked with UO{sub 2} and a crucible was damaged because of the reduction of tungsten strength at high temperature. In order to solve these problems, improvements to the crucible shape were mademore » by simulations using ANSYS.« less

Reversible Silylene Insertion Reactions into Si-H and P-H σ-Bonds at Room Temperature.

PubMed

Rodriguez, Ricardo; Contie, Yohan; Nougué, Raphael; Baceiredo, Antoine; Saffon-Merceron, Nathalie; Sotiropoulos, Jean-Marc; Kato, Tsuyoshi

2016-11-07

Phosphine-stabilized silylenes react with silanes and a phosphine by silylene insertion into E-H σ-bonds (E=Si,P) at room temperature to give the corresponding silanes. Of special interest, the process occurs reversibly at room temperature. These results demonstrate that both the oxidative addition (typical reaction for transient silylenes) and the reductive elimination processes can proceed at the silicon center under mild reaction conditions. DFT calculations provide insight into the importance of the coordination of the silicon center to achieve the reductive elimination step. © 2016 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Ocean Warming, More than Acidification, Reduces Shell Strength in a Commercial Shellfish Species during Food Limitation

PubMed Central

Mackenzie, Clara L.; Ormondroyd, Graham A.; Curling, Simon F.; Ball, Richard J.; Whiteley, Nia M.; Malham, Shelagh K.

2014-01-01

Ocean surface pH levels are predicted to fall by 0.3–0.4 pH units by the end of the century and are likely to coincide with an increase in sea surface temperature of 2–4°C. The combined effect of ocean acidification and warming on the functional properties of bivalve shells is largely unknown and of growing concern as the shell provides protection from mechanical and environmental challenges. We examined the effects of near-future pH (ambient pH –0.4 pH units) and warming (ambient temperature +4°C) on the shells of the commercially important bivalve, Mytilus edulis when fed for a limited period (4–6 h day−1). After six months exposure, warming, but not acidification, significantly reduced shell strength determined as reductions in the maximum load endured by the shells. However, acidification resulted in a reduction in shell flex before failure. Reductions in shell strength with warming could not be explained by alterations in morphology, or shell composition but were accompanied by reductions in shell surface area, and by a fall in whole-body condition index. It appears that warming has an indirect effect on shell strength by re-allocating energy from shell formation to support temperature-related increases in maintenance costs, especially as food supply was limited and the mussels were probably relying on internal energy reserves. The maintenance of shell strength despite seawater acidification suggests that biomineralisation processes are unaffected by the associated changes in CaCO3 saturation levels. We conclude that under near-future climate change conditions, ocean warming will pose a greater risk to shell integrity in M. edulis than ocean acidification when food availability is limited. PMID:24489785

Ocean warming, more than acidification, reduces shell strength in a commercial shellfish species during food limitation.

PubMed

Mackenzie, Clara L; Ormondroyd, Graham A; Curling, Simon F; Ball, Richard J; Whiteley, Nia M; Malham, Shelagh K

2014-01-01

Ocean surface pH levels are predicted to fall by 0.3-0.4 pH units by the end of the century and are likely to coincide with an increase in sea surface temperature of 2-4 °C. The combined effect of ocean acidification and warming on the functional properties of bivalve shells is largely unknown and of growing concern as the shell provides protection from mechanical and environmental challenges. We examined the effects of near-future pH (ambient pH -0.4 pH units) and warming (ambient temperature +4 °C) on the shells of the commercially important bivalve, Mytilus edulis when fed for a limited period (4-6 h day(-1)). After six months exposure, warming, but not acidification, significantly reduced shell strength determined as reductions in the maximum load endured by the shells. However, acidification resulted in a reduction in shell flex before failure. Reductions in shell strength with warming could not be explained by alterations in morphology, or shell composition but were accompanied by reductions in shell surface area, and by a fall in whole-body condition index. It appears that warming has an indirect effect on shell strength by re-allocating energy from shell formation to support temperature-related increases in maintenance costs, especially as food supply was limited and the mussels were probably relying on internal energy reserves. The maintenance of shell strength despite seawater acidification suggests that biomineralisation processes are unaffected by the associated changes in CaCO3 saturation levels. We conclude that under near-future climate change conditions, ocean warming will pose a greater risk to shell integrity in M. edulis than ocean acidification when food availability is limited.

Ammonia formation by the reduction of nitrite/nitrate by FeS: ammonia formation under acidic conditions.

PubMed

Summers, David P

2005-08-01

One issue for the origin of life under a non-reducing atmosphere is the availability of the reduced nitrogen necessary for amino acids, nucleic acids, etc. One possible source of this nitrogen is the formation of ammonia from the reduction of nitrates and nitrites produced by the shock heating of the atmosphere and subsequent chemistry. Ferrous ions will reduce these species to ammonium, but not under acidic conditions. We wish to report results on the reduction of nitrite and nitrate by another source of iron (II), ferrous sulfide, FeS. FeS reduces nitrite to ammonia at lower pHs than the corresponding reduction by aqueous Fe+ 2. The reduction follows a first order decay, in nitrite concentration, with a half-life of about 150 min (room temperature, CO2, pH 6.25). The highest product yield of ammonia measured was 53%. Under CO2, the product yield decreases from pH 5.0 to pH 6.9. The increasing concentration of bicarbonate, at higher pH, interferes with the reaction. Comparing experiments under N2 CO2 shows the interference of bicarbonate. The reaction proceeds well in the presence of such species as chloride, sulfate, and phosphate, though the yield drops significantly with phosphate. FeS also reduces nitrate and, unlike with Fe+ 2, the reduction shows more reproducibility. Again, the product yield decreases with increasing pH, from 7% at pH 4.7 to 0% at pH 6.9. It appears that nitrate is much more sensitive to the presence of added species, perhaps not competing as well for binding sites on the FeS surface. This may be the cause of the lack of reproducibility of nitrate reduction by Fe+ 2 (which also can be sensitive to binding by certain species).

Ammonia Formation By The Reduction Of Nitrite/Nitrate By Fes: Ammonia Formation Under Acidic Conditions

NASA Astrophysics Data System (ADS)

Summers, David P.

2005-08-01

One issue for the origin of life under a non-reducing atmosphere is the availability of the reduced nitrogen necessary for amino acids, nucleic acids, etc. One possible source of this nitrogen is the formation of ammonia from the reduction of nitrates and nitrites produced by the shock heating of the atmosphere and subsequent chemistry. Ferrous ions will reduce these species to ammonium, but not under acidic conditions. We wish to report results on the reduction of nitrite and nitrate by another source of iron (II), ferrous sulfide, FeS. FeS reduces nitrite to ammonia at lower pHs than the corresponding reduction by aqueous Fe+ 2. The reduction follows a first order decay, in nitrite concentration, with a half-life of about 150 min (room temperature, CO2, pH 6.25). The highest product yield of ammonia measured was 53%. Under CO2, the product yield decreases from pH 5.0 to pH 6.9. The increasing concentration of bicarbonate, at higher pH, interferes with the reaction. Comparing experiments under N2 CO2 shows the interference of bicarbonate. The reaction proceeds well in the presence of such species as chloride, sulfate, and phosphate, though the yield drops significantly with phosphate. FeS also reduces nitrate and, unlike with Fe+ 2, the reduction shows more reproducibility. Again, the product yield decreases with increasing pH, from 7% at pH 4.7 to 0% at pH 6.9. It appears that nitrate is much more sensitive to the presence of added species, perhaps not competing as well for binding sites on the FeS surface. This may be the cause of the lack of reproducibility of nitrate reduction by Fe+ 2 (which also can be sensitive to binding by certain species)

Direct Electrodeposition of UO2 from Uranyl Bis(trifluoromethanesulfonyl)imide Dissolved in 1-Ethyl-3-methylimidazolium Bis(trifluoromethanesulfonyl)imide Room Temperature Ionic Liquid System

DOE PAGES

Freiderich, John W.; Wanigasekara, Eranda P.; Sun, Xiao-Guang; ...

2013-11-11

Our study demonstrates a direct electrodeposition of UO 2 at a Pt cathode from a solution of uranyl bis(trifluoromethanesulfonyl)imide [UO 2(NTf 2) 2)] in a bulk room-temperature ionic liquid (RTIL), 1-ethyl-3-methylimidazolium bis(trifluoromethanesulfonyl)imide (EMIM +NTf 2 –). Cyclic voltammetry (CV) studies revealed two reduction waves corresponding to the conversion of uranium(VI) to uranium(IV), and a mechanism for the overall electroreduction is proposed. A controlled-potential experiment was performed, holding the reduction potential at–1.0 V for 24 h to obtain a brown-black deposit of UO 2 on the Pt cathode. The Faradaic efficiency of the reduction process was determined to be >80%. Themore » UO 2deposit was characterized by powder X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS).« less

VizieR Online Data Catalog: IR absorbance spectra of CH4, C2H6, C3H8 & C4H10 (Turner+, 2018)

NASA Astrophysics Data System (ADS)

Turner, A. M.; Abplanalp, M. J.; Blair, T. J.; Dayuha, R.; Kaiser, R. I.

2018-03-01

In situ infrared data were collected by a Nicolet 6700 Fourier Transform Infrared Spectrometer at 4cm-1 resolution throughout the irradiation and temperature programmed desorption (TPD). (2 data files).

Biogas biodesulfurization in an anoxic biotrickling filter packed with open-pore polyurethane foam.

PubMed

Fernández, Maikel; Ramírez, Martín; Gómez, José Manuel; Cantero, Domingo

2014-01-15

Biogas biodesulfurization by an anoxic biotrickling filter packed with open pore polyurethane foam at the laboratory scale (packed volume 2.4L) has been studied. The biotrickling system was operated for 620 days with biogas supplied continuously and two nitrate feeding regimes were tested (manual and programmed). Biomass immobilization was carried out under the manual nitrate feeding regime and a study was then carried out on the effects on removal efficiency of the following parameters: nitrate source, H2S inlet load, nitrate concentration, sulfate accumulation, temperature, pH and trickling liquid velocity. The effect of increased H2S inlet load was studied under the programmed nitrate feeding regime. The results show that a removal efficiency of 99% can be obtained when working under the following conditions: inlet loads below 130gSm(-3)h(-1), a programmed nitrate feeding system, temperature of 30°C, sulfate concentration below 33gL(-1), a pH between 7.3 and 7.5, and a trickling liquid velocity higher than 4.6mh(-1). Copyright © 2013 Elsevier B.V. All rights reserved.

Effects of H2 Atmospheres on Sintering of Low Alloy Steels Containing Oxygen-Sensitive Masteralloys

NASA Astrophysics Data System (ADS)

de Oro Calderon, Raquel; Jaliliziyaeian, Maryam; Gierl-Mayer, Christian; Danninger, Herbert

2017-04-01

Processing of novel sintered steels with compositions including oxygen-sensitive elements requires deep understanding of the chemistry of sintering. The use of H2 atmospheres alleviates the oxygen transference from the base powder to the oxygen-sensitive particles. However, in H2, methane formation at 700-1200°C causes dramatic homogeneous decarburization of the part that affects both mechanical behavior and dimensional stability. The intensity and the critical temperatures of this effect depend strongly on the alloying elements, being significantly enhanced in presence of Si. When combining the alloying elements as Fe-Mn-Si masteralloys, methane formation is enhanced around 760°C due to the high Mn content (40 wt.%) in the masteralloys. Nevertheless, the benefits of H2 towards oxide reduction can still be advantageously used if diluting it in the form of N2-H2 atmospheres, or if limiting the use of H2 to temperatures below 500°C. Thus, decarburization due to methane formation can be successfully controlled.

Effect of temperature (cooking and freezing) on the concentration of oxytetracycline residue in experimentally induced birds

PubMed Central

Vivienne, Ezenduka Ekene; Josephine, Okorie-kanu Onyinye; Anaelom, Nwanta John

2018-01-01

Aim: The objective of this study was to determine the effect of varying temperatures (different cooking methods and freezing) on the concentration of oxytetracycline (OTC) residues in tissues of broiler birds. Materials and Methods: Fifty, 5-week-old birds were purchased and acclimatized for 3 weeks while being fed antibiotic-free feed and water. Four birds were then tested for residue and in the absence; the remaining birds were injected intramuscularly with oxytetracycline at its therapeutic dose. Muscle and liver samples of the treated birds were harvested and checked for OTC residues before subjecting them to boiling, microwaving, and roasting. The three plate test was used for the residue detection. Result: OTC was detected at both pH 6.0 and pH 7.2 but not detected at pH 8.0. Roasting and boiling significantly reduced the concentration of oxytetracycline in muscle by 53.6% and 69.6%, respectively, at pH 6.0, microwaving reduced the concentration by 49.1% but was not statistically significant. The same pattern was followed at pH 7.2 with reduction of 34.3%, 53.2%, and 67.7% for microwaved, roasted, and boiled. For the liver tissues, there was a significant reduction in the concentration for both pH: 6.0 (57.75%, 79.75%, and 89%; pH 7.2 (48.06%, 79.6%, and 88.79%) for boiled, microwaved, and roasted samples. Boiling had a greater reduction effect for muscle samples while roasting had a greater reduction in liver samples at both pHs. Freezing at −10°C had no effect on the concentration of OTC even after 9 days. Conclusion: The significant reduction of OTC concentration by cooking indicates that consumers may not be at risk of the effects of OTC residues in meat, but microwaving meat may not reduce the concentration below the maximum residue limit if the initial concentration is very high. Therefore, routine monitoring of drug residues in farms and abattoirs is still advocated. PMID:29657398

Thermal response, catalytic activity, and color change of the first hybrid vanadate containing Bpe guest molecules.

PubMed

Fernández de Luis, Roberto; Urtiaga, M Karmele; Mesa, José L; Larrea, Edurne S; Iglesias, Marta; Rojo, Teófilo; Arriortua, María I

2013-03-04

Four isomorphic compounds with formula [{Co2(H2O)2(Bpe)2}(V4O12)]·4H2O·Bpe, CoBpe 1; [{CoNi(H2O)2(Bpe)2}(V4O12)]·4H2O·Bpe, CoNiBpe 2; [{Co0.6Ni1.4(H2O)2(Bpe)2}(V4O12)]·4H2O·Bpe, NiCoBpe 3; and [{Ni2(H2O)2(Bpe)2}(V4O12)]·4H2O·Bpe, NiBpe 4, have been obtained by hydrothermal synthesis. The crystal structures of CoBpe 1 and NiBpe 4 were determined by single-crystal X-ray diffraction (XRD). The Rietveld refinement of CoNiBpe 2 and NiCoBpe 3 XRD patterns confirms that those are isomorphic. The compounds crystallize in the P1̅ space group, exhibiting a crystal structure constructed from inorganic layers pillared by Bpe ligands. The crystal structure contains intralayer and interlayer channels, in which the crystallization water molecules and Bpe guest molecules, respectively, are located. The solvent molecules establish a hydrogen bonding network with the coordinated water molecules. Thermodiffractometric and thermogravimetric studies showed that the loss of crystallization and coordinated water molecules takes place at different temperatures, giving rise to crystal structure transformations that involve important reduction of the interlayer distance, and strong reduction of crystallinity. The IR, Raman, and UV-vis spectra of the as-synthesized and heated compounds confirm that the structural building blocks and octahedral coordination environment of the metal centers are maintained after the structural transformations. The color change and reversibility of the water molecules uptake/removal were tested showing that the initial color is not completely recovered when the compounds are heated at temperatures higher than 200 °C. The thermal evolution of the magnetic susceptibility indicates one-dimensional antiferromagnetic coupling of the metal centers at high temperatures. For NiCoBpe 3 and NiBpe 4 compounds magnetic ordering is established at low temperatures, as can be judged by the maxima observed in the magnetic susceptibilities. CoNiBpe 2 was proved as catalyst being active for cyanosilylation reactions of aldehydes.

DOE Office of Scientific and Technical Information (OSTI.GOV)

King, Sean W., E-mail: sean.king@intel.com; Davis, Robert F.; Carter, Richard J.

The desorption kinetics of molecular hydrogen (H{sub 2}) from silicon (001) surfaces exposed to aqueous hydrogen fluoride and remote hydrogen plasmas were examined using temperature programmed desorption. Multiple H{sub 2} desorption states were observed and attributed to surface monohydride (SiH), di/trihydride (SiH{sub 2/3}), and hydroxide (SiOH) species, subsurface hydrogen trapped at defects, and hydrogen evolved during the desorption of surface oxides. The observed surface hydride species were dependent on the surface temperature during hydrogen plasma exposure with mono, di, and trihydride species being observed after low temperature exposure (150 °C), while predominantly monohydride species were observed after higher temperature exposure (450 °C).more » The ratio of surface versus subsurface H{sub 2} desorption was also found to be dependent on the substrate temperature with 150 °C remote hydrogen plasma exposure generally leading to more H{sub 2} evolved from subsurface states and 450 °C exposure leading to more H{sub 2} desorption from surface SiH{sub x} species. Additional surface desorption states were observed, which were attributed to H{sub 2} desorption from Si (111) facets formed as a result of surface etching by the remote hydrogen plasma or aqueous hydrogen fluoride treatment. The kinetics of surface H{sub 2} desorption were found to be in excellent agreement with prior investigations of silicon surfaces exposed to thermally generated atomic hydrogen.« less

Determination of Ni Release in NiTi SMA with Surface Modification by Nitrogen Plasma Immersion Ion Implantation

NASA Astrophysics Data System (ADS)

de Camargo, Eliene Nogueira; Oliveira Lobo, Anderson; Silva, Maria Margareth Da; Ueda, Mario; Garcia, Edivaldo Egea; Pichon, Luc; Reuther, Helfried; Otubo, Jorge

2011-07-01

NiTi SMA is a promising material in the biomedical area due to its mechanical properties and biocompatibility. However, the nickel in the alloy may cause allergic and toxic reactions and thus limiting its applications. It was evaluated the influence of surface modification in NiTi SMA by nitrogen plasma immersion ion implantation (varying temperatures, and exposure time as follows: <250 °C/2 h, 290 °C/2 h, and 560 °C/1 h) in the amount of nickel released using immersion test in simulated body fluid. The depth of the nitrogen implanted layer increased as the implantation temperature increased resulting in the decrease of nickel release. The sample implanted in high implantation temperature presented 35% of nickel release reduction compared to reference sample.

Nitrogen fixation activity in biological soil crusts dominated by cyanobacteria in the Subpolar Urals (European North-East Russia).

PubMed

Patova, Elena; Sivkov, Michail; Patova, Anna

2016-09-01

The nitrogen fixation by biological soil crusts with a dominance of cyanobacteria was studied using the acetylene reduction assay in the territory of the Subpolar Urals (65°11' N, 60°18' E), Russia. The field measurements of nitrogen fixation activity were conducted in situ for two different types of soil crusts dominated by Stigonema (V1 type) and Nostoc with Scytonema (V2 type). The nitrogen fixation process had similar dynamics in both crusts but nitrogen fixation rates were different. The crusts of the V2 type showed a significantly higher acetylene reduction activity, with ethylene production rate of 1.76 ± 0.49 g C2H4 m(-2) h(-1) at 15°C, compared with V1-type soil crusts, with a rate of 0.53 ± 0.21 mg C2H4 m(-2) h(-1) at 15°C. The daily value of acetylene reduction activity in V2-type soil crusts was 32.7 ± 6.2 mg C2H4 m(-2) d(-1) and in V1-type crusts, 12.3 ± 1.8 mg C2H4 m(-2) d(-1) After recalculation for N, the daily values of nitrogen fixation were in the range 3.3-22.3 mg N m(-2) d(-1), which is a few times higher than the values of N input from the precipitation to the soil in the studied regions. The dependence of nitrogen-fixation activity on temperature and light intensity of biological soil crusts was investigated. On the basis of temperature models obtained from the dependence, the nitrogen balance was calculated for the growing season (approximately 120 days). The crusts dominated by Stigonema species were fixing 0.3 g N m(-2) (ethylene production rate, 1.10 g C2H4 m(-2)) and crusts dominated by Nostoc and Scytonema were fixing 1.3 g N m(-2) (4.10 g C2H4 m(-2)). © FEMS 2016. All rights reserved. For permissions, please e-mail: journals.permissions@oup.com.

Reductive dehalogenation of 3,5-dibromo-4-hydroxybenzoate by an aerobic strain of Delftia sp. EOB-17.

PubMed

Chen, Kai; Jian, Shanshan; Huang, Linglong; Ruan, Zhepu; Li, Shunpeng; Jiang, Jiandong

2015-12-01

To confirm the reductive dehalogenation ability of the aerobic strain of Delftia sp. EOB-17, finding more evidences to support the hypothesis that reductive dehalogenation may occur extensively in aerobic bacteria. Delftia sp. EOB-17, isolated from terrestrial soil contaminated with halogenated aromatic compounds, completely degraded 0.2 mM DBHB in 28 h and released two equivalents of bromides under aerobic conditions in the presence of sodium succinate. LC-MS analysis revealed that DBHB was transformed to 4-hydroxybenzoate via 3-bromo-4-hydroxybenzoate by successive reductive dehalogenation. Highly conserved DBHB-degrading genes, including reductive dehalogenase gene (bhbA3) and the extra-cytoplasmic binding receptor gene (bhbB3), were also found in strain EOB-17 by genome sequencing. The optimal temperature and pH for DBHB reductive dehalogenation activity are 30 °C and 8, respectively, and 0.1 mM Cd(2+), Cu(2+), Hg(2+) and Zn(2+) strongly inhibited dehalogenation activity. The aerobic strain of Delftia sp. EOB-17 was confirmed to reductively dehalogenate DBHB under aerobic conditions, providing another evidence to support the hypothesis that reductive dehalogenation occurs extensively in aerobic bacteria.

Experimental investigation on thermochemical sulfate reduction in the presence of 1-pentanethiol at 200 and 250 °C: Implications for in situ TSR processes occurring in some MVT deposits

USGS Publications Warehouse

Yuan, Shunda; Ellis, Geoffrey S.; Chou, I-Ming; Burruss, Robert

2017-01-01

Organic sulfur compounds are ubiquitous in natural oil and gas fields and moderate-low temperature sulfide ore deposits. Previous studies have shown that organic sulfur compounds are important in enhancing the rates of thermochemical sulfate reduction (TSR) reactions, but the details of these reaction mechanisms remain unclear. In order to assess the extent of sulfate reduction in the presence of labile sulfur species at temperature conditions near to those where TSR occurs in nature, we conducted a series of experiments using the fused silica capillary capsule (FCSS) method. The tested systems containing labile sulfur species are MgSO4 + 1-pentanethiol (C5H11SH) + 1-octene (C8H16), MgSO4 + 1-octene (C8H16), MgSO4 + 1-pentanethiol (C5H11SH), 1-pentanethiol (C5H11SH)+H2O, and MgSO4 + 1-pentanethiol (C5H11SH) + ZnBr2 systems. Our results show that: (1) intermediate oxidized carbon species (ethanol and acetic acid) are formed during TSR simulation experiments when 1-pentanethiol is present; (2) in the presence of ZnBr2, 1-pentanethiol can be oxidized by sulfate to CO2 at 200 °C, which is within the temperature range observed in natural TSR; and (3) the precipitation of sulfide minerals may significantly promote the rate of TSR, indicating that the rates of in situ TSR reactions in ore deposits could be much faster than previously thought. This may be important for understanding the possibility of in situ TSR as a mechanism for the precipitation of metal sulfides in some ore deposits. These findings provide important experimental evidence for understanding the role of organic sulfur compounds in TSR reactions and the pathway of TSR reactions initiated by organic sulfur compounds under natural conditions.

Effects of Si/Al Ratio on Cu/SSZ-13 NH3-SCR Catalysts: Implications for the active Cu species and the Roles of Brønsted Acidity

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gao, Feng; Washton, Nancy M.; Wang, Yilin

2015-09-03

Cu/SSZ-13 catalysts with three Si/Al ratios of 6, 12 and 35 were synthesized with Cu incorporation via solution ion exchange. The implications of varying Si/Al ratios on the nature of the multiple Cu species that can be present in the SSZ-13 zeolite are a major focus of this work, as highlighted by the results of a variety of catalyst characterization and reaction kinetics measurements. Specifically, catalysts were characterized with surface area/pore volume measurements, temperature programmed reduction by H2 (H2-TPR), NH3 temperature programmed desorption (NH3-TPD), and DRIFTS and solid-state nuclear magnetic resonance (NMR) spectroscopies. Catalytic properties were examined using NO oxidation,more » ammonia oxidation, and standard ammonia selective catalytic reduction (NH3-SCR) reactions on selected catalysts under differential conditions. Besides indicating possible variably active multiple Cu species for these reactions, the measurements are also used to untangle some of the complexities caused by the interplay between redox of Cu ion centers and Brønsted acidity. All three reactions appear to follow a redox reaction mechanism, yet the roles of Brønsted acidity are quite different. For NO oxidation, increasing Si/Al ratio lowers Cu redox barriers, thus enhancing reaction rates. Brønsted acidity appears to play essentially no role for this reaction. For standard NH3-SCR, residual Brønsted acidity plays a significant beneficial role at both low- and high-temperature regimes. For NH3 oxidation, no clear trend is observed suggesting both Cu ion center redox and Brønsted acidity play important and perhaps competing roles. The authors gratefully acknowledge the US Department of Energy (DOE), Energy Efficiency and Renewable Energy, Vehicle Technologies Office for the support of this work. The research described in this paper was performed in the Environmental Molecular Sciences Laboratory (EMSL), a national scientific user facility sponsored by the DOE’s Office of Biological and Environmental Research and located at Pacific Northwest National Laboratory (PNNL). PNNL is operated for the US DOE by Battelle.« less

Catalysts based on PdO_ZrO2 in the hydrodechlorination reaction of chlorobenzene

NASA Astrophysics Data System (ADS)

Otroshchenko, T. P.; Turakulova, A. O.; Lokteva, E. S.; Golubina, E. V.; Lunin, V. V.

2015-07-01

The possibility of using mixed oxides of palladium and zirconium obtained with biotemplates (cellulose and wood pulp) as the precursor of catalysts for the hydrodechlorination of chlorobenzene is analyzed. The properties of the samples are studied by means of scanning electron microscopy (SEM), transmission electron microscopy (TEM), the Brunauer-Emmet-Teller (BET) method, and temperature-programmed reduction (TPR). They are then compared to the properties of a supported analogue. The biomorphic precursors are characterized by high porosity and include micropores, mesopores, and macropores; the results from TPR reveal the presence in the precursors of several forms of PdO that differ by reduction temperature. It is shown that the distribution of palladium in the catalysts obtained by reducing the precursors with hydrogen depends on the method used in synthesizing the precursor. It is shown that the studied catalysts ensure 100% conversion of chlorobenzene at temperatures of 100 to 250°C. It is established that cyclohexane is the principal product in the presence of the supported catalyst across the range of temperatures, while cyclohexane and benzene are detected among the products in the presence of biomorphous samples at temperatures above 130°C. The effect the presence of an admixture of alkaline and alkaline-earth metals in the catalyst has on the selectivity of the process is noted. It is established that the catalysts operate in a stable manner for at least 27 h of use under experimental conditions.

Selective autocatalytic reduction of NO from sintering flue gas by the hot sintered ore in the presence of NH3.

PubMed

Chen, Wangsheng; Luo, Jing; Qin, Linbo; Han, Jun

2015-12-01

In this paper, the selective autocatalytic reduction of NO by NH3 combined with multi-metal oxides in the hot sintered ore was studied, and the catalytic activity of the hot sintered ore was investigated as a function of temperature, NH3/NO ratio, O2 content, H2O and SO2. The experimental results indicated that the hot sintered ore, when combined with NH3, had a maximum denitration efficiency of 37.67% at 450 °C, 3000 h(-1) gas hourly space velocity (GHSV) and a NH3/NO ratio of 0.4/1. Additionally, it was found that O2 played an important role in removing NOx. However, high O2 content had a negative effect on NO reduction. H2O was found to promote the denitration efficiency in the absence of SO2, while SO2 inhibited the catalytic activity of the sintered ore. In the presence of H2O and SO2, the catalytic activity of the sintered ore was dramatically suppressed. Copyright © 2015 Elsevier Ltd. All rights reserved.

Specific features of spin-variable properties of [Fe(acen)pic2]BPh4 · nH2O

NASA Astrophysics Data System (ADS)

Ivanova, T. A.; Ovchinnikov, I. V.; Gil'mutdinov, I. F.; Mingalieva, L. V.; Turanova, O. A.; Ivanova, G. I.

2016-02-01

The [Fe(acen)pic2]BPh4 · nH2O compound has been synthesized and studied in the temperature interval of 5-300 K by the methods of EPR and magnetic susceptibility. The existence of ferromagnetic interactions between Fe(III) complexes in this compound has been revealed, in contrast to unhydrated [Fe(acen)pic2]BPh4. The reduction in the integrated intensity of the magnetic resonance signal as the temperature decreases below 80 K has been explained by the transition of high-spin ions to the low-spin state. It has been shown that the phase transition temperature in the presence of intermolecular (ferromagnetic) interactions is lower than that in the case of noninteracting centers.

Effect of temperature on reduction of CaSO{sub 4} oxygen carrier in chemical-looping combustion of simulated coal gas in a fluidized bed reactor

DOE Office of Scientific and Technical Information (OSTI.GOV)

Song, Q.L.; Xiao, R.; Deng, Z.Y.

2008-12-15

Chemical-looping combustion (CLC) is a promising combustion technology for gaseous and solid fuel with efficient use of energy and inherent separation of CO{sub 2}. The concept of a coal-fueled CLC system using, calcium sulfate (CaSO{sub 4}) as oxygen carrier is proposed in this study. Reduction tests of CaSO{sub 4} oxygen carrier with simulated coal gas were performed in a laboratory-scale fluidized bed reactor in the temperature range of 890-950{degree}C. A high concentration of CO{sub 2} was obtained at the initial reduction period. CaSO{sub 4} oxygen carrier exhibited high reactivity initially and decreased gradually at the late period of reduction. Themore » sulfur release during the reduction of CaSO{sub 4} as oxygen carrier was also observed and analyzed. H{sub 2} and CO{sub 2} conversions were greatly influenced by reduction temperature. The oxygen carrier conversion and mass-based reaction rates during the reduction at typical temperatures were compared. Higher temperatures would enhance reaction rates and result in high conversion of oxygen carrier. An XRD patterns study indicated that CaS was the dominant product of reduction and the variation of relative intensity with temperature is in agreement with the solid conversion. ESEM analysis indicated that the surface structure of oxygen carrier particles changed significantly from impervious to porous after reduction. EDS analysis also demonstrated the transfer of oxygen from the oxygen carrier to the fuel gas and a certain amount of sulfur loss and CaO formation on the surface at higher temperatures. The reduction kinetics of CaSO{sub 4} oxygen carrier was explored with the shrinking unreacted-core model. The apparent kinetic parameters were obtained, and the kinetic equation well predicted the experimental data. Finally, some basic considerations on the use of CaSO{sub 4} oxygen carrier in a CLC system for solid fuels were discussed.« less

Kinetics of uncatalyzed thermochemical sulfate reduction by sulfur-free paraffin

USGS Publications Warehouse

Zhang, Tongwei; Ellis, Geoffrey S.; Ma, Qisheng; Amrani, Alon; Tang, Yongchun

2012-01-01

To determine kinetic parameters of sulfate reduction by hydrocarbons (HC) without the initial presence of low valence sulfur, we carried out a series of isothermal gold-tube hydrous-pyrolysis experiments at 320, 340, and 360 °C under a constant confined pressure of 24.1 MPa. The reactants used consisted of saturated HC (sulfur-free) and CaSO4 in an aqueous solution buffered to three different pH conditions without the addition of elemental sulfur (S8) or H2S as initiators. H2S produced in the course of reaction was proportional to the extent of the reduction of CaSO4 that was initially the only sulfur-containing reactant. Our results show that the in situ pH of the aqueous solution (herein, in situ pH refers to the calculated pH value of the aqueous solution at certain experimental conditions) can significantly affect the rate of the thermochemical sulfate reduction (TSR) reaction. A substantial increase in the TSR reaction rate was observed with a decrease in the in situ pH. Our experimental results show that uncatalyzed TSR is a first-order reaction. The temperature dependence of experimentally measured H2S yields from sulfate reduction was fit with the Arrhenius equation. The determined activation energy for HC (sulfur-free) reacting with View the MathML sourceHSO4− in our experiments is 246.6 kJ/mol at pH values ranging from 3.0 to 3.5, which is slightly higher than the theoretical value of 227.0 kJ/mol using ab initio quantum chemical calculations on a similar reaction. Although the availability of reactive sulfate significantly affects the rate of reaction, a consistent rate constant was determined by accounting for the HSO4− ion concentration. Our experimental and theoretical approach to the determination of the kinetics of TSR is further validated by a reevaluation of several published experimental TSR datasets without the initial presence of native sulfur or H2S. When the effect of reactive sulfate concentration is appropriately accounted for, the published experimental TSR data yield kinetic parameters that are consistent with our values. Assuming MgSO4 contact-ion-pair ([MgSO4]CIP) as the reactive form of sulfate in petroleum reservoir formation waters, a simple extrapolation of our experimentally derived HSO4− reduction kinetics as a proxy for [MgSO4]CIP to geologically reasonable conditions predicts onset temperatures (130–140 °C) that are comparable to those observed in nature.

The O2 reduction at the IFC modified O2 fuel cell electrode

NASA Technical Reports Server (NTRS)

Fielder, William L.; Singer, Joseph; Baldwin, Richard S.; Johnson, Richard E.

1992-01-01

The International Fuel Corporation (IFC) state of the art (SOA) O2 electrode (Au-10 percent Pt electrocatalyst by weight) is currently being used in the alkaline H2-O2 fuel cell in the NASA Space Shuttle. Recently, IFC modified O2 electrode, as a possible replacement for the SOA electrode. In the present study, O2 reduction data were obtained for the modified electrode at temperatures between 23.3 and 91.7 C. BET measurements gave an electrode BET surface area of about 2070 sq. cm/sq. cm of geometric surface area. The Tafel data could be fitted to two straight line regions. The slope for the lower region, designated as the 0.04 V/decade region, was temperature dependent, and the transfer coefficient was about 1.5. The 'apparent' energy of activation for this region was about 19 kcal/mol. An O2 reduction mechanism for this 0.04 region is presented. In the upper region, designated as the 0.08 V/decade region, diffusion may be the controlling process. Tafel data are presented to illustrate the increase in performance with increasing temperature.

Dual-catalyst system to broaden the window of operability in the reduction of NO/sub chi/ with ammonia

DOE Office of Scientific and Technical Information (OSTI.GOV)

Medros, F.G.; Eldridge, J.W.; Kittrell, J.R.

1989-08-01

The objective of the research discussed in this paper was to determine if a dual-catalyst system for NO reduction with NH/sub 3/ can achieve a given percent NO reduction over a wider range of temperatures and space velocities than either catalyst used alone in the same total reactor volume. Hydrogen mordenite (20/32 mesh) and copper-ion-exchanged hydrogen mordenite (2.2% Cu) were used in series at temperatures from 200 to 600 {sup 0}C and space velocities from 1000000 to 450000 h/sup -1/ (STP). The superiority of the dual-catalyst system was demonstrated experimentally, and a model was developed which predicted its performance verymore » well from data on the individual catalysts. A technique was then developed for predicting quantitatively the dual-catalyst enhancement of the space velocity versus temperature window for achieving a given percent NO conversion.« less

Potential effects of ultraviolet radiation reduction on tundra nitrous oxide and methane fluxes in maritime Antarctica.

PubMed

Bao, Tao; Zhu, Renbin; Wang, Pei; Ye, Wenjuan; Ma, Dawei; Xu, Hua

2018-02-27

Stratospheric ozone has begun to recover in Antarctica since the implementation of the Montreal Protocol. However, the effects of ultraviolet (UV) radiation on tundra greenhouse gas fluxes are rarely reported for Polar Regions. In the present study, tundra N 2 O and CH 4 fluxes were measured under the simulated reduction of UV radiation in maritime Antarctica over the last three-year summers. Significantly enhanced N 2 O and CH 4 emissions occurred at tundra sites under the simulated reduction of UV radiation. Compared with the ambient normal UV level, a 20% reduction in UV radiation increased tundra emissions by an average of 8 μg N 2 O m -2 h -1 and 93 μg CH 4 m -2 h -1 , whereas a 50% reduction in UV radiation increased their emissions by an average of 17 μg N 2 O m -2 h -1 and 128 μg CH 4 m -2 h -1 . No statistically significant correlation (P > 0.05) was found between N 2 O and CH 4 fluxes and soil temperature, soil moisture, total carbon, total nitrogen, NO 3 - -N and NH 4 + -N contents. Our results confirmed that UV radiation intensity is an important factor affecting tundra N 2 O and CH 4 fluxes in maritime Antarctica. Exclusion of the effects of reduced UV radiation might underestimate their budgets in Polar Regions with the recovery of stratospheric ozone.

Reduction of iron-bearing lunar minerals for the production of oxygen

NASA Technical Reports Server (NTRS)

Massieon, Charles; Cutler, Andrew; Shadman, Farhang

1992-01-01

The kinetics and mechanism of the reduction of simulants of the iron-bearing lunar minerals olivine ((Fe,Mg)2SiO4), pyroxene ((Fe,Mg,Ca)SiO3), and ilmenite (FeTiO3) are investigated, extending previous work with ilmenite. Fayalite is reduced by H2 at 1070 K to 1480 K. A layer of mixed silica glass and iron forms around an unreacted core. Reaction kinetics are influenced by permeation of hydrogen through this layer and a reaction step involving dissociated hydrogen. Reaction mechanisms are independent of Mg content. Augite, hypersthene, and hedenbergite are reduced in H2 at the same temperatures. The products are iron metal and lower iron silicates mixed throughout the mineral. Activation energy rises with calcium content. Ilmenite and fayalite are reduced with carbon deposited on partially reduced minerals via the CO disproportionation reaction. Reduction with carbon is rapid, showing the carbothermal reduction of lunar minerals is possible.

An Inner-Sphere Mechanism for Molecular Oxygen Reduction Catalyzed by Copper Amine Oxidases

PubMed Central

Mukherjee, Arnab; Smirnov, Valeriy V.; Lanci, Michael P.; Brown, Doreen E.; Shepard, Eric M.; Dooley, David M.; Roth, Justine P.

2008-01-01

Copper and topaquinone (TPQ) containing amine oxidases utilize O2 for the metabolism of biogenic amines while concomitantly generating H2O2 for use by the cell. The mechanism of O2 reduction has been the subject of long-standing debate due to the obscuring influence of a proton-coupled electron transfer between the tyrosine-derived TPQ and copper, a rapidly established equilibrium precluding assignment of the enzyme in its reactive form. Here we show that substrate-reduced pea seedling amine oxidase (PSAO) exists predominantly in the CuI, TPQ semiquinone state. A new mechanistic proposal for O2 reduction is advanced on the basis of thermodynamic considerations together with kinetic studies (at varying pH, temperature and viscosity), the identification of steady-state intermediates and the analysis of competitive oxygen kinetic isotope effects: 18O KIEs, [kcat/KM(16,16O2)]/[kcat/KM(16,18O2)]. The 18O KIE = 1.0136 ± 0.0013 at pH 7.2 is independent of temperature from 5 to 47°C and insignificantly changed to 1.0122 ± 0.0020 upon raising the pH to 9, thus indicating the absence of kinetic complexity. Using density functional methods, the effect is found to be precisely in the range expected for reversible O2 binding to CuI to afford a superoxide, [CuII(η1-O2)−I]+, intermediate. Electron transfer from the TPQ semiquinone follows in the first irreversible step to form a peroxide, CuII(η1-O2)−II, intermediate driving the reduction of O2. The similar 18O KIEs reported for copper amine oxidases from other sources raise the possibility that all enzymes react by related inner-sphere mechanisms although additional experiments are needed to test this proposal. PMID:18582059

Hydrogen retention in lithium and lithium oxide films

NASA Astrophysics Data System (ADS)

Buzi, L.; Yang, Y.; Domínguez-Gutiérrez, F. J.; Nelson, A. O.; Hofman, M.; Krstić, P. S.; Kaita, R.; Koel, B. E.

2018-04-01

Pure lithium (Li) surfaces are difficult to maintain in fusion devices due to rapid oxide formation, therefore, parameterizing and understanding the mechanisms of hydrogen (H, D) retention in lithium oxide (Li2O) in addition to pure Li is crucial for Li plasma-facing material applications. To compare H retention in Li and Li2O films, measurements were made as a function of surface temperature (90-520 K) under ultrahigh vacuum (UHV) conditions using temperature programmed desorption (TPD). In both cases, the total retention dropped with surface temperature, from 95% at 90 K to 35% at 520 K Li2O films retained H in similar amounts as pure Li. Molecular Dynamics (MD) modeling was used to elucidate the mechanisms of H retention, and results were consistent with experiments in terms of both retention fraction and the drop of retention with temperature.

Synthesis of nanocomposites comprising iron and barium hexaferrites

NASA Astrophysics Data System (ADS)

Pal, M.; Bid, S.; Pradhan, S. K.; Nath, B. K.; Das, D.; Chakravorty, D.

2004-02-01

Composites of nanometre-sized α-iron and barium hexaferrite phases, respectively, have been synthesized by the ceramic processing route. Pure barium hexaferrite (BaO·6Fe 2O 3) was first of all prepared by calcinations of the precursor oxides at a maximum temperature of 1200°C for 4 h. By subjecting the resulting powder having particle size of the order of 1 μm to a reduction treatment in the temperature range 500-650°C for a period varying from 10 to 15 min it was possible to obtain a composite consisting of nanosized barium hexaferrite and α-Fe. At reduction temperature of 650°C for a period greater than 15 min all the ferrite phase was converted to α-Fe and Ba—the particle sizes being 59.4 and 43.6 nm, respectively. These conclusions are based on X-ray diffraction and Mossbauer studies of different samples. During reduction H + ions are introduced into the hexaferrite crystallite. It is believed that due to a tensile stress the crystals are broken up into smaller dimensions and the reduction brings about the growth of nanosized α-Fe and barium, respectively, around the hexaferrite particles. Magnetic measurements show coercivity values for the reduced samples in the range 120-440 Oe and saturation magnetization varying from 158 to 53.7 emu/g. These values have been ascribed to the formation and growth of α-Fe particles as the reduction treatment is increased. By heating the nanocomposites at a temperature of 1000°C for 1 h in ordinary atmosphere it was found that they were reconverted to the barium hexaferrite phase with a particle size ˜182.3 nm. The reaction described in this study is thus reversible.

Catalytic reduction of dinitrogen to ammonia at a single molybdenum center.

PubMed

Yandulov, Dmitry V; Schrock, Richard R

2003-07-04

Dinitrogen (N2) was reduced to ammonia at room temperature and 1 atmosphere with molybdenum catalysts that contain tetradentate [HIPTN3N]3- triamidoamine ligands (such as [HIPTN3N]Mo(N2), where [HIPTN3N]3- is [(3,5-(2,4,6-i-Pr3C6H2)2C6H3NCH2CH2)3N]3-) in heptane. Slow addition of the proton source [(2,6-lutidinium)(BAr'4), where Ar' is 3,5-(CF3)2C6H3]and reductant (decamethyl chromocene) was critical for achieving high efficiency ( approximately 66% in four turnovers). Numerous x-ray studies, along with isolation and characterization of six proposed intermediates in the catalytic reaction under noncatalytic conditions, suggest that N2 was reduced at a sterically protected, single molybdenum center that cycled from Mo(III) through Mo(VI) states.

Adsorption, desorption, and displacement kinetics of H2O and CO2 on TiO2(110).

PubMed

Smith, R Scott; Li, Zhenjun; Chen, Long; Dohnálek, Zdenek; Kay, Bruce D

2014-07-17

The adsorption, desorption, and displacement kinetics of H2O and CO2 on TiO2(110) are investigated using temperature programmed desorption (TPD) and molecular beam techniques. The TPD spectra for both H2O and CO2 have well-resolved peaks corresponding to desorption from bridge-bonded oxygen (Ob), Ti5c, and defect sites in order of increasing peak temperature. Analysis of the saturated surface spectrum for both species reveals that the corresponding adsorption energies on all sites are greater for H2O than for CO2. Sequential dosing of H2O and CO2 reveals that, independent of the dose order, H2O molecules will displace CO2 in order to occupy the highest energy binding sites available. Isothermal experiments show that the displacement of CO2 by H2O occurs between 75 and 80 K.

[Effects of different irrigation treatments during heading and flowering stage on cold resis-tance, yield and physiological characteristics of late rice].

PubMed

Cao, Na; Chen, Xiao Rong; He, Hao Hua; Zhu, Chang Lan; Cai, Shuo; Xu, Tao; Xie, Heng Wang; Liu, Fang Ping

2017-12-01

Taking super hybrid rice variety 'Wufengyou T025' as test material, the effects of different irrigation methods and water layer depth on physiological characteristics and yield in double-season late rice under low temperature conditions during heading and flowering stage were investigated. Three treatments were set, i.e., draining during day and containing 4-5 cm water layer during night (H 1 ), draining during day and containing 8-10 cm water layer during night (H 2 ), and containing 8-10 cm water layer day and night (H 3 ), with the 0-1 cm water layer day and night was as the control (CK). The results showed that rice leaf temperature, soil layer temperature and canopy temperature under the different irrigation treatments were higher than that of CK, and the warming effect of treatment H 2 was the best during the low temperature period. Leaf chlorophyll content, net photosynthetic rate, transpiration rate, leaf stomatal conductance and intercellular CO 2 concentration of rice plants decreased gradually under the low temperature, while the smallest reduction occurred in H 2 . The increase ranges of malondialdehyde and proline content in H 2 were lower, while its soluble protein content was the highest compared with other irrigation treatments. The increase ranges for the activities of superoxide dismutase and peroxidase in H 2 were lower, while its decrease range for the activity of catalase was the lowest. Irrigation for heat preservation could increase the yield, and H 2 performed best. Yield of H 2 at the second sowing date in 2014 and 2015 encountering low temperature increased by 12.9% and 13.5% respectively compared to CK. The yield components including the effective panicle numbers per plant, panicle length, seed setting rate and 1000-grain mass were improved in all irrigation treatments compared to CK. Draining during day and containing 8-10 cm water layer during night (H 2 ) was the most effective agronomic measure to enhance the tolerance to low temperature during heading and flowering stage for double-season hybrid late rice.

IF-WS{sub 2} nanoparticles size design and synthesis via chemical reduction

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ghoreishi, S.M., E-mail: ghoreshi@cc.iut.ac.ir; Meshkat, S.S.; Dadkhah, A.A.

2010-05-15

An innovative synthesis of inorganic fullerene-like disulfide tungsten (IF-WS{sub 2}) nanoparticles was developed using a chemical reduction reaction in a horizontal quartz reactor. In this process, first tungsten trisulfide (WS{sub 3}) was formed via a chemical reaction of tetra thiotungstate ammonium ((NH{sub 4}){sub 2}WS{sub 4}), polyethylene glycol (PEG), and hydrochloric acid (HCl) at ambient temperature and pressure. Subsequently, WS{sub 3} was reacted with hydrogen (H{sub 2}) at high temperature (1173-1373 K) in a quartz tube. The produced WS{sub 2} nanoparticles were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray (EDAX), and transmission electron microscopy (TEM). Themore » characterization results indicated that the high-purity (100%) IF-WS{sub 2} nanoparticles were produced. Moreover, addition of surfactant (PEG) and higher operating temperature (1173-1373 K) decreased the particles agglomeration, and consequently led to the reduction of average diameter of WS{sub 2} particles in the range of 50-78 nm. The developed method is simple, environmentally compatible, and cost-effective in contrast to the conventional techniques.« less

Analytical results and sample locality map of heavy-mineral-concentrate and rock samples from the Castle Peaks Wilderness Study Area (CDCA- 266), San Bernardino County, California

USGS Publications Warehouse

Adrian, B.M.; Frisken, J.G.; Malcolm, M.J.; Crock, J.G.

1986-01-01

The report presents water-quality and geohydrologic information for 106 public water-supply wells in Illinois. These wells were sampled during April to December 1984 as part of a pilot program to develop a ground-water observation network in the State. The pilot program was designed to sample single-aquifer wells from three major aquifer systems--(1) sand and gravel, both confined and unconfined; (2) Silurian dolomite; and (3) the Ironton-Galesville deep sandstone. Data are tabulated for water temperature, pH, specific conductance, oxidation-reduction potential, ammonia nitrogen, nitrate + nitrite nitrogen, phosphorus, silica, arsenic, lead, mercury, fluoride, chloride, sulfate, cyanide, phenols, selenium, residue on evaporation at 180 degrees Celsius, alkalinity, calcium, magnesium, sodium, potassium, barium, boron, beryllium, cadmium, chormium, copper, cobalt, iron, aluminum, manganese, nickel, silver, strontium, vanadium, zinc, and selected geohydrologic information.

Metal Al produced by H2 plasma reduction of AlCl3: a thermodynamic and kinetic study on the plasma chemistry.

PubMed

Zheng, Jie; Sun, Bo; Yang, Rong; Song, Xubo; Li, Xingguo; Pu, Yikang

2008-10-09

In this paper we reported that low temperature plasma may reverse the direction of a chemical reaction. The thermodynamically forbidden reaction between H 2 and AlCl 3 was able to take place with the assistance of low temperature plasma, yielding metal Al. The plasma chemistry of the reaction was investigated by optical emission spectroscopy, which suggested that the dissociation of H 2 and AlCl 3 molecules by plasma led the reaction to a thermodynamically favorable one by creating reaction channels with low Gibbs free energy change. The addition of Ar promoted the reaction kinetics dramatically, which was attributed to the enhanced dissociation of AlCl 3 molecules by excited Ar species.

DoD Force & Infrastructure Categories: A FYDP-Based Conceptual Model of Department of Defense Programs and Resources

DTIC Science & Technology

2002-09-01

Support 0605160D Counterproliferation Support (H) 0901502A Service Support to DTSA 0901502F Service Support to DTSA 0901502N Service Support to DTSA ...Base Operations Support 0901502A Service Support to DTSA (1F2C) Int’l Engagement & Threat Reduction 0901502F Service Support to DTSA (1F2C...Int’l Engagement & Threat Reduction 0901502N Service Support to DTSA (1F2C) Int’l Engagement & Threat Reduction 0901503A Service Support to OSD

Effect of reductive treatments on Pt behavior and NOx storage in lean NOx trap catalysts

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Xianqin; Kim, Do Heui; Kwak, Ja Hun

2011-10-01

Lean NOx trap (LNT) catalysts represent a promising approach to meet increasingly stringent NOx emission regulations on diesel and other lean-burn engines. Pt material properties, including dispersion and particle size, are known to be important factors in determining NOx uptake performance, since Pt provides active sites for NO oxidation to NO2 necessary for storing NOx as nitrates, and for the reduction of nitrates to N2. In this work, the physicochemical properties of Pt in Pt-BaO/Al2O3 LNT catalysts, such as the Pt accessible surface area and particle size, were investigated by using various tools, such as irreversible volumetric H2 chemisorption, highmore » resolution transmission electron microscopy (HRTEM), and X-ray diffraction (XRD), following successive reductive treatments at elevated temperatures. NOx uptake activities were also measured to establish a relationship between the properties of Pt and NOx storage following identical high-temperature reductive treatments. We find that the reductive treatments of Pt-BaO/Al2O3 lean NOx trap catalysts at temperatures up to 500 ºC promote a significant increase in NOx uptake explained, in part, by an induced close interaction between Pt and BaO phases in the catalyst, thus enabling facilitation of the NOx storage process.« less

H2/O2 three-body rates at high temperatures

NASA Technical Reports Server (NTRS)

Marinelli, William J.; Kessler, William J.; Piper, Lawrence G.; Rawlins, W. Terry

1990-01-01

The extraction of thrust from air breathing hypersonic propulsion systems is critically dependent on the degree to which chemical equilibrium is reached in the combustion process. In the combustion of H2/Air mixtures, slow three-body chemical reactions involving H-atoms, O-atoms, and the OH radical play an important role in energy extraction. A first-generation high temperature and pressure flash-photolysis/laser-induced fluorescence reactor was designed and constructed to measure these important three-body rates. The system employs a high power excimer laser to produce these radicals via the photolysis of stable precursors. A novel two-photon laser-induced fluorescence technique is employed to detect H-atoms without optical thickness or O2 absorption problems. To demonstrate the feasibility of the technique the apparatus in the program is designed to perform preliminary measurements on the H + O2 + M reaction at temperatures from 300 to 835 K.

Gold nanoclusters confined in a supercage of Y zeolite for aerobic oxidation of HMF under mild conditions.

PubMed

Cai, Jiaying; Ma, Hong; Zhang, Junjie; Song, Qi; Du, Zhongtian; Huang, Yizheng; Xu, Jie

2013-10-11

Au nanoclusters with an average size of approximately 1 nm size supported on HY zeolite exhibit a superior catalytic performance for the selective oxidation of 5-hydroxymethyl-2-furfural (HMF) into 2,5-furandicarboxylic acid (FDCA). It achieved >99 % yield of 2,5-furandicarboxylic acid in water under mild conditions (60 °C, 0.3 MPa oxygen), which is much higher than that of Au supported on metal oxides/hydroxide (TiO2 , CeO2 , and Mg(OH)2 ) and channel-type zeolites (ZSM-5 and H-MOR). Detailed characterizations, such as X-ray diffraction, transmission electron microscopy, N2 -physisorption, and H2 -temperature-programmed reduction (TPR), revealed that the Au nanoclusters are well encapsulated in the HY zeolite supercage, which is considered to restrict and avoid further growing of the Au nanoclusters into large particles. The acidic hydroxyl groups of the supercage were proven to be responsible for the formation and stabilization of the gold nanoclusters. Moreover, the interaction between the hydroxyl groups in the supercage and the Au nanoclusters leads to electronic modification of the Au nanoparticles, which is supposed to contribute to the high efficiency in the catalytic oxidation of HMF to FDCA. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Microwave Plasma Hydrogen Recovery System

NASA Technical Reports Server (NTRS)

Atwater, James; Wheeler, Richard, Jr.; Dahl, Roger; Hadley, Neal

2010-01-01

A microwave plasma reactor was developed for the recovery of hydrogen contained within waste methane produced by Carbon Dioxide Reduction Assembly (CRA), which reclaims oxygen from CO2. Since half of the H2 reductant used by the CRA is lost as CH4, the ability to reclaim this valuable resource will simplify supply logistics for longterm manned missions. Microwave plasmas provide an extreme thermal environment within a very small and precisely controlled region of space, resulting in very high energy densities at low overall power, and thus can drive high-temperature reactions using equipment that is smaller, lighter, and less power-consuming than traditional fixed-bed and fluidized-bed catalytic reactors. The high energy density provides an economical means to conduct endothermic reactions that become thermodynamically favorable only at very high temperatures. Microwave plasma methods were developed for the effective recovery of H2 using two primary reaction schemes: (1) methane pyrolysis to H2 and solid-phase carbon, and (2) methane oligomerization to H2 and acetylene. While the carbon problem is substantially reduced using plasma methods, it is not completely eliminated. For this reason, advanced methods were developed to promote CH4 oligomerization, which recovers a maximum of 75 percent of the H2 content of methane in a single reactor pass, and virtually eliminates the carbon problem. These methods were embodied in a prototype H2 recovery system capable of sustained high-efficiency operation. NASA can incorporate the innovation into flight hardware systems for deployment in support of future long-duration exploration objectives such as a Space Station retrofit, Lunar outpost, Mars transit, or Mars base. The primary application will be for the recovery of hydrogen lost in the Sabatier process for CO2 reduction to produce water in Exploration Life Support systems. Secondarily, this process may also be used in conjunction with a Sabatier reactor employed to stockpile life-support oxygen as well as propellant and fuel production from Martian atmospheric CO2

Magnetic study of the low temperature anomalies in the underdoped PrBCO compound

NASA Astrophysics Data System (ADS)

Lahoubi, Mahieddine

2018-05-01

The low temperature anomalous magnetic properties of a non-superconducting PrBCO6+x compound in an underdoped oxygen state of concentration (x = 0.44) are characterized by paraprocess magnetic susceptibility χH(T) measurements carried out as a function of temperature T under different values of a DC magnetic field H up to 110 kOe. The derivatives dχH(T)/dT curves reveal a significant reduction with increasing H in the Néel temperature TN = 9 K of the Pr antiferromagnetic (AFM) ordering for which the transition subsists at 100 kOe. The small anomaly at T2 = 6-7 K is confirmed at 20 kOe and the previous spin reorientation attributed to this transition temperature seems to be suppressed above 60 kOe. The well defined anomaly in the vicinity of the low-critical point Tcr = 4-5 K which occurs simultaneously, is still present when the strength of H is increased up to 100 kOe. Weak field induced phase transitions are observed between T2 and TN at a low transition-field (Ht<11 kOe) in the differential magnetic susceptibility dMT(H)/dH as a function of H deduced from the isothermal magnetizations MT(H) with H up to 21 kOe, whereas a weak ferromagnetic behavior of the Pr sublattice appears below Tcr. The magnetic field effects give rise to more evidence for the Pr-Cu(2) coupling with 'exchange-frustrated AFM' interactions and ascertain the main role of the Pr sublattice whereas the Cu(2) sublattice seems to be less efficient.

Stability and accuracy of total and free PSA values in samples stored at room temperature.

PubMed

Forde, J C; Blake, O; Crowley, V E; Lynch, T H

2016-11-01

In 2010, an estimated 476,076 total PSA tests were performed in Ireland, at a cost of €3.6 million with the majority ordered by general practitioners. We aimed to replicate storage conditions at room temperature and see if prolonged storage affected total and free PSA values. Blood samples were taken from 20 male patients in four VACUETTE ® Serum Separator tubes (Greiner-Bio-One, Austria) and stored at room temperature (22 °C) for different time intervals (4, 8, 24, 48 h) before being centrifuged and analyzed. Total PSA (tPSA) and free PSA (fPSA) values were determined using the Tosoh AIA 1800 assay (Tokyo, Japan). Mean tPSA values were measured at 4, 8, 24 and 48 h with values of 7.9, 8.1, 7.8 and 8.0 μg/L, respectively. Values ranged from -1.26 to +2.53 % compared to the initial 4 h interval reading, indicating tPSA remained consistent at room temperature. The tPSA showed no significance between groups (ANOVA, p = 0.283). Mean fPSA values at 4, 8, 24 and 48 h were 2.05, 2.04, 1.83, 1.82 μg/L, respectively. At 24 and 48 h there was 10.73 and 11.22 % reduction, respectively, in fPSA compared to the 4-h time interval, indicating prolonged storage resulted in reduced fPSA values. After 24 h, there was an 8.8 % reduction in the free/total PSA %. The fPSA showed significant differences between groups (ANOVA, p = 0.024). Our recommendation is that samples that have been stored for prolonged amounts of time (greater than 24 h) should not be used for free PSA testing.

Reduction of hexavalent chromium by the thermophilic methanogen Methanothermobacter thermautotrophicus

NASA Astrophysics Data System (ADS)

Singh, Rajesh; Dong, Hailiang; Liu, Deng; Zhao, Linduo; Marts, Amy R.; Farquhar, Erik; Tierney, David L.; Almquist, Catherine B.; Briggs, Brandon R.

2015-01-01

Despite significant progress on iron reduction by thermophilic microorganisms, studies on their ability to reduce toxic metals are still limited, despite their common co-existence in high temperature environments (up to 70 °C). In this study, Methanothermobacter thermautotrophicus, an obligate thermophilic methanogen, was used to reduce hexavalent chromium. Experiments were conducted in a growth medium with H2/CO2 as substrate with various Cr6+ concentrations (0.2, 0.4, 1, 3, and 5 mM) in the form of potassium dichromate (K2Cr2O7). Time-course measurements of aqueous Cr6+ concentrations using 1,5-diphenylcarbazide colorimetric method showed complete reduction of the 0.2 and 0.4 mM Cr6+ solutions by this methanogen. However, much lower reduction extents of 43.6%, 13.0%, and 3.7% were observed at higher Cr6+ concentrations of 1, 3 and 5 mM, respectively. These lower extents of bioreduction suggest a toxic effect of aqueous Cr6+ to cells at this concentration range. At these higher Cr6+ concentrations, methanogenesis was inhibited and cell growth was impaired as evidenced by decreased total cellular protein production and live/dead cell ratio. Likewise, Cr6+ bioreduction rates decreased with increased initial concentrations of Cr6+ from 13.3 to 1.9 μM h-1. X-ray absorption near-edge structure (XANES) spectroscopy revealed a progressive reduction of soluble Cr6+ to insoluble Cr3+ precipitates, which was confirmed as amorphous chromium hydroxide by selected area electron diffraction pattern. However, a small fraction of reduced Cr occurred as aqueous Cr3+. Scanning and transmission electron microscope observations of M. thermautotrophicus cells after Cr6+ exposure suggest both extra- and intracellular chromium reduction mechanisms. Results of this study demonstrate the ability of M. thermautotrophicus cells to reduce toxic Cr6+ to less toxic Cr3+ and its potential application in metal bioremediation, especially at high temperature subsurface radioactive waste disposal sites, where the temperature may reach ∼70 °C.

Temperature-dependent infrared optical properties of 3C-, 4H- and 6H-SiC

NASA Astrophysics Data System (ADS)

Tong, Zhen; Liu, Linhua; Li, Liangsheng; Bao, Hua

2018-05-01

The temperature-dependent optical properties of cubic (3C) and hexagonal (4H and 6H) silicon carbide are investigated in the infrared range of 2-16 μm both by experimental measurements and numerical simulations. The temperature in experimental measurement is up to 593 K, while the numerical method can predict the optical properties at elevated temperatures. To investigate the temperature effect, the temperature-dependent damping parameter in the Lorentz model is calculated based on anharmonic lattice dynamics method, in which the harmonic and anharmonic interatomic force constants are determined from first-principles calculations. The infrared phonon modes of silicon carbide are determined from first-principles calculations. Based on first-principles calculations, the Lorentz model is parameterized without any experimental fitting data and the temperature effect is considered. In our investigations, we find that the increasing temperature induces a small reduction of the reflectivity in the range of 10-13 μm. More importantly, it also shows that our first-principles calculations can predict the infrared optical properties at high-temperature effectively which is not easy to be obtained through experimental measurements.

Chemical catalysis of nitrate reduction by iron (II)

NASA Astrophysics Data System (ADS)

Ottley, C. J.; Davison, W.; Edmunds, W. M.

1997-05-01

Experiments have been conducted to investigate the chemical reduction of nitrate under conditions relevant to the often low organic carbon environment of groundwaters. At pH 8 and 20 ± 2°C, in the presence of Cu(II), NO 3- was chemically reduced by Fe(II) to NH 4+ with an average stoichiometric liberation of 8 protons. The rate of the reaction systematically increased with pH in the range pH 7-8.5. The half-life for nitrate reduction, t 1/2, was inversely related to the total molar copper concentration, [Cu T], by the equation log t 1/2 = -1.35 log [Cu T] -2.616, for all measured values of t 1/2 from 23 min to 15 days. At the Cu(II) concentrations used of 7 × 10 -6 -10 -3 M, Cu was present mainly as a solid phase, either adsorbed to the surfaces of precipitated iron oxides or as a saturated solid. It is this solid phase copper rather than CU 2+ in solution which is catalytically active. Neither magnetite, which was formed as a product of the reaction, nor freshly prepared lepidocrocite catalysed the reaction, but goethite did. Although traces of oxygen accelerated the reaction, at higher partial pressures (>0.01 atm) the reduction of nitrate was inhibited, probably due to competition between NO 3- and O 2 for Fe(II). Appreciable catalytic effects were also observed for solid phase forms of Ag(I), Cd(H), Ni(H), Hg(II), and Pb(II). Mn(II) enhanced the rate slightly, and there was evidence for slow abiotic reduction in the absence of any added metal catalysts. These results suggest that the chemical reduction of nitrate at catalytic concentrations and temperatures appropriate to groundwater conditions is feasible on a timescale of months to years.

The reaction of selenium (IV) with ascorbic acid: its relevance in aqueous and soil systems.

PubMed

Pettine, Maurizio; Gennari, Francesca; Campanella, Luigi

2013-01-01

Abiotic processes able to reduce oxidized Se species may have a strong influence on the environmental behavior of selenium since Se toxicity, bioavailability and mobility follow the order Se(-II)0.3), while does not affect significantly the reduction of Se(IV) by H(2)A at low ratios (<0.1). Fe(III) also catalyzes the oxidation of H(2)A but in this case the possible diminution of the reduction rates of Se(IV) by H(2)A are masked by additional processes of adsorption on and coprecipitation by ferric oxyhydroxides, which lower the concentrations of Se(IV). Copyright © 2012 Elsevier Ltd. All rights reserved.

Reduction of PCDDs/PCDFs in MSWI fly ash using microwave peroxide oxidation in H2SO4/HNO3 solution.

PubMed

Chang, Yu-Min; Dai, Wen-Chien; Tsai, Kao-Shen; Chen, Shiao-Shing; Chen, Jyh-Herng; Kao, Jimmy C M

2013-05-01

Microwave peroxide oxidation (MPO) is an energy-efficient and low GHG emission technology to destroy the hazardous organic compounds in solid waste. The objective of this paper is to explore the reduction feasibility of PCDDs/Fs in MSWI fly ash using the MPO in H2SO4/HNO3 solution. Nearly all PCDDs/Fs, 99% in the original fly ash, can be reduced in 120min at the temperature of 150°C using the MPO treatment. It was also found that a change occurred in the content distribution profiles of 17 major PCDD/F congeners before and after MPO treatment. This provides the potential to reduce the actual PCDDs/Fs content more than I-TEQ contents of PCDDs/Fs. The percentile distribution profile has a tendency of higher chlorinated PCDDs/Fs moving to the lower ones. It concludes that a significant reduction efficiency of I-TEQ toxicity was achieved and showed sufficient reduction of toxic level to lower than 1.0ngI-TEQ(gdw)(-1). The treatment temperature would be a critical factor facilitating the dissolution because higher temperature leads more inorganic salt (parts of fly ash) dissolution. Some problems caused by the MPO method are also delineated in this paper. Copyright © 2013 Elsevier Ltd. All rights reserved.

Fabrication of CuO-doped catalytic material containing zeolite synthesized from red mud and rice husk ash for CO oxidation

NASA Astrophysics Data System (ADS)

Hieu Do Thi, Minh; Thinh Tran, Quoc; Nguyen, Tri; Van Nguyen Thi, Thuy; Huynh, Ky Phuong Ha

2018-06-01

In this study a series of the CuO-doped materials containing zeolite with varying CuO contents were synthesized from red mud (RM) and rice husk ash (RHA). The rice husk ash/red mud with the molar ratio of , and being 1.8, 2.5 and 60, respectively, were maintained during the synthetic process of materials. The characteristic structure samples were analyzed by x-ray diffraction (XRD), Fourier transformed infrared spectroscopy (FTIR), scanning electron microscopy (SEM), transmission electron microscope (TEM), Brunauer–Emmett–Teller (BET) surface area and H2 temperature program reduction (H2-TPR). The catalytic activity of samples was evaluated in CO oxidation reaction in a microflow reactor at temperature range 200 °C–350 °C. The obtained results showed that all synthetic samples there exist the A-type zeolites with the average crystal size of 15–20 nm, the specific surface area of , and pore volume of . The material synthesized from RM and RHA with the zeolite structure (ZRM, undoped CuO) could also oxidize CO completely at 350 °C, and its activity was increase significantly when doped with CuO. CuO-doped materials with the zeolite structure exhibited excellent catalytic activity in CO oxidation. The ZRM sample loading 5 wt% CuO with particle nanosize about 10–30 nm was the best one for CO oxidation with complete conversion temperature at 275 °C.

Solar kerosene from H2O and CO2

NASA Astrophysics Data System (ADS)

Furler, P.; Marxer, D.; Scheffe, J.; Reinalda, D.; Geerlings, H.; Falter, C.; Batteiger, V.; Sizmann, A.; Steinfeld, A.

2017-06-01

The entire production chain for renewable kerosene obtained directly from sunlight, H2O, and CO2 is experimentally demonstrated. The key component of the production process is a high-temperature solar reactor containing a reticulated porous ceramic (RPC) structure made of ceria, which enables the splitting of H2O and CO2 via a 2-step thermochemical redox cycle. In the 1st reduction step, ceria is endo-thermally reduced using concentrated solar radiation as the energy source of process heat. In the 2nd oxidation step, nonstoichiometric ceria reacts with H2O and CO2 to form H2 and CO - syngas - which is finally converted into kerosene by the Fischer-Tropsch process. The RPC featured dual-scale porosity for enhanced heat and mass transfer: mm-size pores for volumetric radiation absorption during the reduction step and μm-size pores within its struts for fast kinetics during the oxidation step. We report on the engineering design of the solar reactor and the experimental demonstration of over 290 consecutive redox cycles for producing high-quality syngas suitable for the processing of liquid hydrocarbon fuels.

Comparative study on the effect of H2 pre-adsorption on CO oxidation in O2-poor atmosphere over Au/TiO2 and TiO2: Temperature programmed surface reaction by a multiplexed mass spectrometer testing

NASA Astrophysics Data System (ADS)

Si, Ruiru; Liu, Junfeng; Zhang, Yujuan; Chen, Xun; Dai, Wenxin; Fu, Xianzhi

2016-11-01

The behaviors of H2 pre-adsorption on CO oxidation in an O2-poor stream containing a trace H2O over Au/TiO2 and TiO2 have been investigated by a temperature programmed surface reaction testing, respectively. It was found that the H2 pre-adsorption could keep CO oxidation without H2O consumption over Au/TiO2, but suppress CO oxidation over TiO2. The chemisorption testing showed that the H2 adsorption at Au/TiO2 could benefit to the formation of Ti-bonded hydroxyl species (Ti4+-OH), while the H2 adsorption at TiO2 would consume the Ti-bonded hydroxyl species and form the bridge hydroxyl species (Ti4+-OH-Ti4+). These results show that only the Ti-bonded hydroxyl species (not all kinds of hydroxyl species) could act as the active species of oxidizing CO. Furthermore, it is suggested that the dissociative hydrogen adsorbed at Au sites could activate the lattice oxygen of TiO2 to form the active Ti-bonded hydroxyl species (hydrogen spillover from Au to TiO2), which exhibit a strong reducibility than the H directly adsorbed at TiO2.

Low-Temperature Molten-Salt Production of Silicon Nanowires by the Electrochemical Reduction of CaSiO3.

PubMed

Dong, Yifan; Slade, Tyler; Stolt, Matthew J; Li, Linsen; Girard, Steven N; Mai, Liqiang; Jin, Song

2017-11-13

Silicon is an extremely important technological material, but its current industrial production by the carbothermic reduction of SiO 2 is energy intensive and generates CO 2 emissions. Herein, we developed a more sustainable method to produce silicon nanowires (Si NWs) in bulk quantities through the direct electrochemical reduction of CaSiO 3 , an abundant and inexpensive Si source soluble in molten salts, at a low temperature of 650 °C by using low-melting-point ternary molten salts CaCl 2 -MgCl 2 -NaCl, which still retains high CaSiO 3 solubility, and a supporting electrolyte of CaO, which facilitates the transport of O 2- anions, drastically improves the reaction kinetics, and enables the electrolysis at low temperatures. The Si nanowire product can be used as high-capacity Li-ion battery anode materials with excellent cycling performance. This environmentally friendly strategy for the practical production of Si at lower temperatures can be applied to other molten salt systems and is also promising for waste glass and coal ash recycling. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

A program for calculation of intrapulmonary shunts, blood-gas and acid-base values with a programmable calculator.

PubMed

Ruiz, B C; Tucker, W K; Kirby, R R

1975-01-01

With a desk-top, programmable calculator, it is now possible to do complex, previously time-consuming computations in the blood-gas laboratory. The authors have developed a program with the necessary algorithms for temperature correction of blood gases and calculation of acid-base variables and intrapulmonary shunt. It was necessary to develop formulas for the Po2 temperature-correction coefficient, the oxyhemoglobin-dissociation curve for adults (withe necessary adjustments for fetal blood), and changes in water vapor pressure due to variation in body temperature. Using this program in conjuction with a Monroe 1860-21 statistical programmable calculator, it is possible to temperature-correct pH,Pco2, and Po2. The machine will compute alveolar-arterial oxygen tension gradient, oxygen saturation (So2), oxygen content (Co2), actual HCO minus 3 and a modified base excess. If arterial blood and mixed venous blood are obtained, the calculator will print out intrapulmonary shunt data (Qs/Qt) and arteriovenous oxygen differences (a minus vDo2). There also is a formula to compute P50 if pH,Pco2,Po2, and measured So2 from two samples of tonometered blood (one above 50 per cent and one below 50 per cent saturation) are put into the calculator.

Effects of K and Pt promoters on the performance of cobalt catalyst supported on CNTs

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zabidi, Noor Asmawati Mohd, E-mail: noorasmawati-mzabidi@petronas.com.my; Ali, Sardar, E-mail: alikhan-635@yahoo.com; Subbarao, Duvvuri, E-mail: duvvuri-subbarao@petronas.com.my

2014-10-24

This paper presents a comparative study on the effects of incorporation of potassium (K) and platinum (Pt) as promoters on the physicochemical properties of cobalt catalyst. The catalyst was prepared by a wet impregnation method on a CNTs support. Samples were characterized using transmission electron microscopy (TEM), H{sub 2}-temperature-programmed reduction (TPR) and X-ray photoelectron spectroscopy (XPS) techniques. Fischer-Tropsch Synthesis (FTS) was carried out in a fixed-bed microreactor at 543 K and 1 atm, with H{sub 2}/CO = 2v/v and space velocity, SV of 12 L/g.h for 5 hours. The K-promoted and Pt-promoted Co catalysts have different physicochemical properties and catalytic performances comparedmore » to that of the un-promoted Co catalyst. XPS analysis revealed that K and Pt promoters induced electronic modifications as exhibited by the shifts in the Co binding energies. Incorporation of 0.06 wt% K and 0.06 wt% Pt in Co/CNTs catalyst resulted in an increase in the CO conversion and C{sub 5+} selectivity and a decrease in methane selectivity. Potassium was found to be a better promoter for Co/CNTs catalyst compared to platinum.« less

Effects of K and Pt promoters on the performance of cobalt catalyst supported on CNTs

NASA Astrophysics Data System (ADS)

Zabidi, Noor Asmawati Mohd; Ali, Sardar; Subbarao, Duvvuri

2014-10-01

This paper presents a comparative study on the effects of incorporation of potassium (K) and platinum (Pt) as promoters on the physicochemical properties of cobalt catalyst. The catalyst was prepared by a wet impregnation method on a CNTs support. Samples were characterized using transmission electron microscopy (TEM), H2-temperature-programmed reduction (TPR) and X-ray photoelectron spectroscopy (XPS) techniques. Fischer-Tropsch Synthesis (FTS) was carried out in a fixed-bed microreactor at 543 K and 1 atm, with H2/ CO = 2v / v and space velocity, SV of 12 L/g.h for 5 hours. The K-promoted and Pt-promoted Co catalysts have different physicochemical properties and catalytic performances compared to that of the un-promoted Co catalyst. XPS analysis revealed that K and Pt promoters induced electronic modifications as exhibited by the shifts in the Co binding energies. Incorporation of 0.06 wt% K and 0.06 wt% Pt in Co/CNTs catalyst resulted in an increase in the CO conversion and C5+ selectivity and a decrease in methane selectivity. Potassium was found to be a better promoter for Co/CNTs catalyst compared to platinum.

Cold plasma inactivates Salmonella Stanley and Escherichia coli O157:H7 inoculated on golden delicious apples.

PubMed

Niemira, Brendan A; Sites, Joseph

2008-07-01

Cold plasma generated in a gliding arc was applied to outbreak strains of Escherichia coli O157:H7 and Salmonella Stanley on agar plates and inoculated onto the surfaces of Golden Delicious apples. This novel sanitizing technology inactivated both pathogens on agar plates, with higher flow rate (40 liters/min) observed to be more efficacious than were lower flow rates (20 liters/min), irrespective of treatment time (1 or 2 min). Golden Delicious apples were treated with various flow rates (10, 20, 30, or 40 liters/min) of cold plasma for various times (1, 2, or 3 min), applied to dried spot inoculations. All treatments resulted in significant (P < 0.05) reductions from the untreated control, with 40 liters/min more effective than were lower flow rates. Inactivation of Salmonella Stanley followed a time-dependent reduction for all flow rates. Reductions after 3 min ranged from 2.9 to 3.7 log CFU/ml, close to the limit of detection. For E. coli O157:H7, 40 liters/min gave similar reductions for all treatment times, 3.4 to 3.6 log CFU/ml. At lower flow rates, inactivation was related to exposure time, with 3 min resulting in reductions of 2.6 to 3 log CFU/ml. Temperature increase of the treated apples was related to exposure time for all flow rates. The maximum temperature of any plasma-treated apple was 50.8 degrees C (28 degrees C above ambient), after 20 liters/min for 3 min, indicating that antimicrobial effects were not the result of heat. These results indicate that cold plasma is a nonthermal process that can effectively reduce human pathogens inoculated onto fresh produce.

Photogeneration of H2O2 in Water-Swollen SPEEK/PVA Polymer Films.

PubMed

Lockhart, PaviElle; Little, Brian K; Slaten, B L; Mills, G

2016-06-09

Efficient reduction of O2 took place via illumination with 350 nm photons of cross-linked films containing a blend of sulfonated poly(ether etherketone) and poly(vinyl alcohol) in contact with air-saturated aqueous solutions. Swelling of the solid macromolecular matrices in H2O enabled O2 diffusion into the films and also continuous extraction of the photogenerated H2O2, which was the basis for a method that allowed quantification of the product. Peroxide formed with similar efficiencies in films containing sulfonated polyketones prepared from different precursors and the initial photochemical process was found to be the rate-determining step. Generation of H2O2 was most proficient in the range of 4.9 ≤ pH ≤ 8 with a quantum yield of 0.2, which was 10 times higher than the efficiencies determined for solutions of the polymer blend. Increases in temperature as well as [O2] in solution were factors that enhanced the H2O2 generation. H2O2 quantum yields as high as 0.6 were achieved in H2O/CH3CN mixtures with low water concentrations, but peroxide no longer formed when film swelling was suppressed. A mechanism involving reduction of O2 by photogenerated α-hydroxy radicals from the polyketone in competition with second-order radical decay processes explains the kinetic features. Higher yields result from the films because cross-links present in them hinder diffusion of the radicals, limiting their decay and enhancing the oxygen reduction pathway.

Catalytic Silylation of N 2 and Synthesis of NH 3 and N 2H 4 by Net Hydrogen Atom Transfer Reactions Using a Chromium P 4 Macrocycle

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kendall, Alexander J.; Johnson, Samantha I.; Bullock, R. Morris

We report the first discrete molecular Cr-based catalysts for the reduction of N2. This study is focused on the reactivity of the Cr-N2 complex, trans-[Cr(N2)2(PPh4NBn4)] P4Cr(N2)2, bearing a 16-membered tetraphosphine macrocycle. The architecture of the [16]-PPh4NBn4 ligand is critical to preserve the structural integrity of the catalyst. P4Cr(N2)2 was found to mediate the reduction of N2 by three complementary reaction pathways: (1) Cr-catalyzed reduction of N2 to N(SiMe3)3 by Na and Me3SiCl affording up to 34 equiv N(SiMe3)3; (2) stoichiometric reduction of N2 by protons and electrons. For example, the reaction of cobaltocene (CoCp2) and collidinium triflate (ColH[OTf]) at roommore » temperature to afforded 1.9 equiv of NH3, or at -78 °C to afforded a mixture of NH3 and N2H4; (3) the first example of NH3 formation from the reaction of a terminally bound N2 ligand with a traditional H atom source, TEMPOH, (2,2,6,6-tetramethylpiperidine-1-ol). We found that trans-[Cr(15N2)2(PPh4NBn4)] reacts with excess TEMPOH to afford a 1.4 equiv of 15NH3.« less

Heterogeneous Reactions of ClONO2, HCl, and HOCl on Liquid Sulfuric Acid Surfaces

NASA Technical Reports Server (NTRS)

Zhang, Renyi; Leu, Ming-Taun; Keyser, Leon F.

1994-01-01

The heterogeneous reactions of ClONO2 + H2O yields HNO3 + HOCl (1), ClONO2 + HCl yields C12 + HNO3 (2), and HOCl + HCl yields Cl2 + H2O (3) on liquid sulfuric acid surfaces have been studied using a fast flow reactor coupled to a quadrupole mass spectrometer. The main objectives of the study are to investigate: (a) the temperature dependence of these reactions at a fixed H2O partial pressure typical of the lower stratosphere (that is, by changing temperature at a constant water partial pressure, the H2SO4 content of the surfaces is also changed), (b) the relative importance or competition between reactions 1 and 2, and (c) the effect of HNO3 on the reaction probabilities due to the formation of a H2SO4/HNO3/H2O ternary system. The measurements show that all the reactions depend markedly on temperature at a fixed H2O partial pressure: they proceed efficiently at temperatures near 200 K and much slower at temperatures near 220 K. The reaction probability (gamma(sub 1)) for ClONO2 hydrolysis approaches 0.01 at temperatures below 200 K, whereas the values for gamma(sub 2) and gamma(sub 3) are on the order of a few tenths at 200 K. Although detailed mechanisms for these reactions are still unknown, the present data indicate that the competition between ClONO2 hydrolysis and ClONO2 reaction with HCl may depend on temperature (or H2SO4 Wt %): in the presence of gaseous HCl at stratospheric concentrations, reaction 2 is dominant at lower temperatures (less than 200 K), but reaction 1 becomes important at temperatures above 210 K. Furthermore, reaction probability measurements performed on the H2SO4/HNO3/ H2O ternary solutions do not exhibit noticeable deviation from those performed on the H2SO4/H2O binary system, suggesting little effect of HNO3 in sulfate aerosols on the ClONO2 and HOCl reactions with HCl. The results reveal that significant reductions in the chlorine-containing reservoir species (such as ClONO2 and HCl) can take place on stratospheric sulfate aerosols at high latitudes in winter and early spring, even at temperatures too warm for Polar Stratospheric Clouds (PSCs) to form or in regions where nucleation of PSCs is sparse. This is particularly true under elevated sulfuric acid loading, such as that after the eruption of Mt. Pinatubo. Comparisons between our results and those presently available have also been made.

Application of bacteriophages specific to hydrogen sulfide-producing bacteria in raw poultry by-products.

PubMed

Gong, Chao; Liu, Xiaohua; Jiang, Xiuping

2014-03-01

Hydrogen sulfide-producing bacteria (SPB) can spoil raw animal materials and release harmful hydrogen sulfide (H2S) gas. The objective of this study was to apply a SPB-specific bacteriophage cocktail to control H2S production by SPB in different raw poultry by-products in the laboratory (20, 30, and 37°C) and greenhouse (average temperature 29 to 31°C, humidity 34.8 to 59.8%, and light intensity 604.8 Wm(2)) by simulating transportation and a rendering facility. The amount of H2S production was determined using either test strips impregnated with lead acetate or a H2S monitor. In the laboratory, phage treatment applied to fresh chicken meat inoculated with SPB, spoiled chicken meat, chicken guts, and chicken feathers reduced H2S production by approximately 25 to 69% at temperatures from 20 to 37°C. In the greenhouse, phage treatment achieved approximately a 30 to 85% reduction of H2S yield in chicken offal and feathers. Among all phage treatments, multiplicity of infection (MOI) of 100 exhibited the highest inhibitory activities against SPB on H2S production. Several factors such as initial SPB level, temperature, and MOI affect lytic activities of bacteriophages. Our study demonstrated that the phage cocktail is effective to reduce the production of H2S by SPB significantly in raw animal materials. This biological control method can control SPB in raw poultry by-products at ambient temperatures, leading to a safer working environment and high quality product with less nutrient degradation for the rendering industry.

Gas-liquid interface-mediated room-temperature synthesis of "clean" PdNiP alloy nanoparticle networks with high catalytic activity for ethanol oxidation.

PubMed

Wang, Rongfang; Ma, Yuanyuan; Wang, Hui; Key, Julian; Ji, Shan

2014-11-04

PdNiP alloy nanoparticle networks (PdNiP NN) were prepared by simultaneous reduction of PdCl2, NiCl2 and NaH2PO2 with NaBH4via a gas-liquid interface reaction at room temperature using N2 bubbles. PdNiP NN had markedly higher activity and durability for ethanol oxidation than PdNi nanoparticle networks and PdNiP grain aggregates.

Effects of salicylic acid on thermotolerance and cardenolide accumulation under high temperature stress in Digitalis trojana Ivanina.

PubMed

Cingoz, Gunce Sahin; Gurel, Ekrem

2016-08-01

Long periods of high temperature or transitory increased temperature, a widespread agricultural problem, may lead to a drastic reduction in economic yield, affecting plant growth and development in many areas of the world. Heat stress causes many anatomical and physiological changes in plants. Its unfavorable effects can be alleviated by thermotolerance induced by exogenous application of plant growth regulators and osmoprotectants or by gradual application of temperature stress. Digitalis trojana Ivanina is an important medicinal plant species well known mainly for its cardenolides. The production of cardenolides via traditional agriculture is commercially inadequate. In this study, elicitation strategies were employed for improving crop thermotolerance and accumulation of cardenolides. For these purposes, the effects of salicylic acid (SA) and/or high temperature treatments in inducing cardenolide accumulation and thermotolerance were tested in callus cultures of D. trojana. Considerable increases in the production of cardenolides (up to 472.28 μg.g(-1) dry weight, dw) and induction of thermotolerance capacity were observed when callus cultures were exposed to high temperature for 2 h after pretreating with SA. High temperature treatments (2 h and 4 h) caused a marked reduction in superoxide dismutase (SOD; EC 1.15.1.1) and catalase (CAT; EC 1.11.1.6) activities, while SA pretreatment increased their activities. High temperature and/or SA appeared to increase the levels of proline, total phenolic, and flavonoid content. Elevated phenolic accumulation could be associated with increased stress protection. These results indicated that SA treatments induced synthesis of antioxidants and cardenolides, which may play a significant role in resistance to high temperature stress. Copyright © 2016 Elsevier Masson SAS. All rights reserved.

Synthesis and Evaluation of Cu/SAPO-34 Catalysts for NH3-SCR 2: Solid-state Ion Exchange and One-pot Synthesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gao, Feng; Walter, Eric D.; Washton, Nancy M.

2015-01-01

Cu-SAPO-34 catalysts are synthesized using two methods: solid-state ion exchange (SSIE) and one-pot synthesis. SSIE is conducted by calcining SAPO-34/CuO mixtures at elevated temperatures. For the one-pot synthesis method, Cu-containing chemicals (CuO and CuSO4) are added during gel preparation. A high-temperature calcination step is also needed for this method. Catalysts are characterized with surface area/pore volume measurements, temperature programmed reduction (TPR), electron paramagnetic resonance (EPR) and nuclear magnetic resonance (NMR) spectroscopies, and scanning electron microscopy (SEM). Catalytic properties are examined using standard ammonia selective catalytic reduction (NH3-SCR) and ammonia oxidation reactions. In Cu-SAPO-34 samples formed using SSIE, Cu presents bothmore » as isolated Cu2+ ions and unreacted CuO. The former is highly active and selective in NH3-SCR, while the latter catalyzes a side reaction; notably, the non-selective oxidation of NH3 above 350 ºC. Using the one-pot method followed by a high-temperature aging treatment, it is possible to form Cu SAPO-34 samples with predominately isolated Cu2+ ions at low Cu loadings. However at much higher Cu loadings, isolated Cu2+ ions that bind weakly with the CHA framework and CuO clusters also form. These Cu moieties are very active in catalyzing non-selective NH3 oxidation above 350 ºC. Low-temperature reaction kinetics indicate that Cu-SAPO-34 samples formed using SSIE have core-shell structures where Cu is enriched in the shell layers; while Cu is more evenly distributed within the one-pot samples. Reaction kinetics also suggest that at low temperatures, the local environment next to Cu2+ ion centers plays little role on the overall catalytic properties. The authors gratefully acknowledge the US Department of Energy (DOE), Energy Efficiency and Renewable Energy, Vehicle Technologies Office for the support of this work. The research described in this paper was performed at the Environmental Molecular Sciences Laboratory (EMSL), a national scientific user facility sponsored by the DOE’s Office of Biological and Environmental Research and located at Pacific Northwest National Laboratory (PNNL). PNNL is operated for the US DOE by Battelle under contract number DE-AC05-76RL01830. The authors also thank Shari Li (PNNL) for surface area/pore volume measurements, and Bruce W. Arey (PNNL) for SEM measurements. Discussions with Drs. A. Yezerets, K. Kamasamudram, J.H. Li, N. Currier and J.Y. Luo from Cummins, Inc. and H.Y. Chen and H. Hess from Johnson-Matthey are greatly appreciated.« less

Cloning, expression and characterization of glycerol dehydrogenase involved in 2,3-butanediol formation in Serratia marcescens H30.

PubMed

Zhang, Liaoyuan; Xu, Quanming; Peng, Xiaoqian; Xu, Boheng; Wu, Yuehao; Yang, Yulong; Sun, Shujing; Hu, Kaihui; Shen, Yaling

2014-09-01

The meso-2,3-butanediol dehydrogenase (meso-BDH) from S. marcescens H30 is responsible for converting acetoin into 2,3-butanediol during sugar fermentation. Inactivation of the meso-BDH encoded by budC gene does not completely abolish 2,3-butanediol production, which suggests that another similar enzyme involved in 2,3-butanediol formation exists in S. marcescens H30. In the present study, a glycerol dehydrogenase (GDH) encoded by gldA gene from S. marcescens H30 was expressed in Escherichia coli BL21(DE3), purified and characterized for its properties. In vitro conversion indicated that the purified GDH could catalyze the interconversion of (3S)-acetoin/meso-2,3-butanediol and (3R)-acetoin/(2R,3R)-2,3-butanediol. (2S,3S)-2,3-Butanediol was not a substrate for the GDH at all. Kinetic parameters of the GDH enzyme showed lower K m value and higher catalytic efficiency for (3S/3R)-acetoin in comparison to those for (2R,3R)-2,3-butanediol and meso-2,3-butanediol, implying its physiological role in favor of 2,3-butanediol formation. Maximum activity for reduction of (3S/3R)-acetoin and oxidations of meso-2,3-butanediol and glycerol was observed at pH 8.0, while it was pH 7.0 for diacetyl reduction. The enzyme exhibited relative high thermotolerance with optimum temperature of 60 °C in the oxidation-reduction reactions. Over 60 % of maximum activity was retained at 70 °C. Additionally, the GDH activity was significantly enhanced for meso-2,3-BD oxidation in the presence of Fe(2+) and for (3S/3R)-acetoin reduction in the presence of Mn(2+), while several cations inhibited its activity, particularly Fe(2+) and Fe(3+) for (3S/3R)-acetoin reduction. The properties provided potential application for single configuration production of acetoin and 2,3-butanediol .

The effect of temporary reductions in incubation temperature on growth characteristics and lipid utilisation in the chick embryo

PubMed Central

FEAST, M.; NOBLE, R. C.; SPEAKE, B. K.; FERGUSON, M. W. J.

1998-01-01

The effect(s) of finite exposure(s) to 22.0 °C on embryo weight gain, 3rd tarsus length, transfer of lipid from the yolk and uptake of specific lipid components by the liver, were measured in the chick embryo. Embryo growth was completely suspended over the period of temperature reduction, but resumed unimpaired when the optimum temperature of 37.5 °C was restored. Two successive periods of embryonic exposure to 22.0 °C (36 h at d 3 followed by 24 at d 10) were additive in their effect on growth retardation. Embryos subjected to temperature reductions on d 3 of incubation displayed significant changes in lipid concentrations and polyunsaturated fatty acid profiles within the liver when measured at d 18 of incubation. Yolk lipid uptake was significantly reduced but not suspended by embryonic exposure to 22.0 °C. It is suggested that the observed suspension of embryonic development was the result of a temperature dependent reduction in metabolism according to a Q10∼2, which is typical of an ectothermic organism. PMID:9877293

High-Temperature Reactions of Metal Triangles: The Influence of Counterion, Ligand, and Metal on the Structure Observed

NASA Astrophysics Data System (ADS)

Coxall, Robert A.; Parkin, Andrew; Parsons, Simon; Smith, Andrew A.; Timco, Grigore A.; Winpenny, Richard E. P.

2001-07-01

A series of oxo-centered metal carboxylate triangles have been heated to 200-400°C under a stream of N2. The products of this treatment depend on the metal, carboxylate, and counterion present. Heating [Cr3O(O2CC6H4Cl)6(H2O)3][NO3]to 200°C gives a compound that crystallizes as [Cr(OH)(O2CC6H4Cl)2]8 [Cr3O(O2CC6H4Cl)6]2[O2CC6H4Cl], indicating incomplete dehydration of [Cr3O(O2CC6H4Cl)6(H2O)3][NO3] at this temperature. For [Cr3O(O2CCMe3)6][O2CCMe3] heating to 400°C gives a new salt containing the hexanuclear cages [Cr6O2(OH)2(O2CCMe3)11] [Cr6O4(O2CCMe3)11]. For [Mn3O(O2CPh)6(NC5H5)2(H2O)] a reduction of the metal occurs and a polymeric complex [Mn4(O2CPh)8(EtOH)6]n can be crystallized from EtOH.

Ni0 encapsulated in N-doped carbon nanotubes for catalytic reduction of highly toxic hexavalent chromium

NASA Astrophysics Data System (ADS)

Yao, Yunjin; Zhang, Jie; Chen, Hao; Yu, Maojing; Gao, Mengxue; Hu, Yi; Wang, Shaobin

2018-05-01

N-doped carbon nanotubes encapsulating Ni0 nanoparticles (Ni@N-C) were fabricated via thermal reduction of dicyandiamide and NiCl2·6H2O, and used to remove CrVI in polluted water. The resultant products present an excellent catalytic activity for CrVI reduction using formic acid under relatively mild conditions. The CrVI reduction efficiency of Ni@N-C was significantly affected by the preparation conditions including the mass of nickel salt and synthesis temperatures. The impacts of several reaction parameters, such as initial concentrations of CrVI and formic acid, solution pH and temperatures, as well as inorganic anions in solution on CrVI reduction efficiency were also evaluated in view of scalable industrial applications. Owing to the synergistic effects amongst tubes-coated Ni0, doped nitrogen, oxygen containing groups, and the configuration of carbon nanotubes, Ni@N-C catalysts exhibit excellent catalytic activity and recyclable capability for CrVI reduction. Carbon shell can efficiently protect inner Ni0 core and N species from corrosion and subsequent leaching, while Ni0 endows the Ni@N-C catalysts with ferromagnetism, so that the composites can be easily separated via a permanent magnet. This study opens up an avenue for design of N-doped carbon nanotubes encapsulating Ni0 nanoparticles with high CrVI removal efficiency and magnetic recyclability as low-cost catalysts for industrial applications.

Thermoelectric properties of Sr0.61Ba0.39Nb2O6-δ ceramics in different oxygen-reduction conditions

NASA Astrophysics Data System (ADS)

Li, Yi; Liu, Jian; Wang, Chun-Lei; Su, Wen-Bin; Zhu, Yuan-Hu; Li, Ji-Chao; Mei, Liang-Mo

2015-04-01

The thermoelectric properties of Sr0.61Ba0.39Nb2O6-δ ceramics, reduced in different conditions, are investigated in the temperature range from 323 K to 1073 K. The electrical transport behaviors of the samples are dominated by the thermal-activated polaron hopping in the low temperature range, the Fermi glass behavior in the middle temperature range, and the Anderson localized behavior in the high temperature range. The thermal conductivity presents a plateau at high-temperatures, indicating a glass-like thermal conduction behavior. Both the thermoelectric power factor and the thermal conductivity increase with the increase of the degree of oxygen-reduction. Taking these two factors into account, the oxygen-reduction can still contribute to promoting the thermoelectric figure of merit. The highest ZT value is obtained to be ˜0.19 at 1073 K in the heaviest oxygen reduced sample. Project supported by the National Basic Research Program of China (Grant No. 2013CB632506) and the National Natural Science Foundation of China (Grant Nos. 51202132 and 51002087).

Temperature, soluble solids and pH effect on Alicyclobacillus acidoterrestris viability in lemon juice concentrate.

PubMed

Maldonado, María C; Belfiore, Carolina; Navarro, Antonio R

2008-02-01

Alicyclobacillus acidoterrestris is a thermoacidophilic, non-pathogenic, spore-forming bacterium detected in spoiled commercial pasteurized fruit juice. Apple, white grape and tomato are particularly susceptible. A. acidoterrestris spores are resistant to lemon juice pasteurization (2 min at 82 degrees C), and they can germinate and grow causing spoilage. This contamination is characterized by a medicinal or disinfectant smell attributed to guaiacol (o-dihydroxybenzene) production and other taint chemicals. The aim of this work was to study the influence of temperature (82, 86, 92 and 95 degrees C), total soluble solids (SS) (6.20, 9.8, 50 and 68 degrees Brix) and pH (2.28, 2.45, 2.80, 3.25, 3.5) on decimal reduction time (D) of the A. acidoterrestris in clarified and non-clarified concentrated lemon juice. Once D-value was determined, the resistance of A. acidoterrestris at the assayed temperatures was confirmed. SS and pH influence spore viability, because spore resistance increases with higher SS (50 degrees Brix 22 min 82 degrees C-68 degrees Brix 28 min 82 degrees C) and pH values (pH 2.28, 17 min-pH 4.00, 22 min). Bacterial growth was lower in clarified lemon juice, 26 min at 82 degrees C, than in non-clarified lemon juice, 51 min at 82 degrees C. Temperature was the parameter that had the greatest influence on the D value.

Electron Excess Doping and Effective Schottky Barrier Reduction on the MoS2/h-BN Heterostructure.

PubMed

Joo, Min-Kyu; Moon, Byoung Hee; Ji, Hyunjin; Han, Gang Hee; Kim, Hyun; Lee, Gwanmu; Lim, Seong Chu; Suh, Dongseok; Lee, Young Hee

2016-10-12

Layered hexagonal boron nitride (h-BN) thin film is a dielectric that surpasses carrier mobility by reducing charge scattering with silicon oxide in diverse electronics formed with graphene and transition metal dichalcogenides. However, the h-BN effect on electron doping concentration and Schottky barrier is little known. Here, we report that use of h-BN thin film as a substrate for monolayer MoS 2 can induce ∼6.5 × 10 11 cm -2 electron doping at room temperature which was determined using theoretical flat band model and interface trap density. The saturated excess electron concentration of MoS 2 on h-BN was found to be ∼5 × 10 13 cm -2 at high temperature and was significantly reduced at low temperature. Further, the inserted h-BN enables us to reduce the Coulombic charge scattering in MoS 2 /h-BN and lower the effective Schottky barrier height by a factor of 3, which gives rise to four times enhanced the field-effect carrier mobility and an emergence of metal-insulator transition at a much lower charge density of ∼1.0 × 10 12 cm -2 (T = 25 K). The reduced effective Schottky barrier height in MoS 2 /h-BN is attributed to the decreased effective work function of MoS 2 arisen from h-BN induced n-doping and the reduced effective metal work function due to dipole moments originated from fixed charges in SiO 2 .

The effect of cool water ingestion on gastrointestinal pill temperature.

PubMed

Wilkinson, David M; Carter, James M; Richmond, Victoria L; Blacker, Sam D; Rayson, Mark P

2008-03-01

Telemetric gastrointestinal (GI) temperature pills are now commonly used to measure core body temperature and could minimize the risk of heat illness while maximizing operational effectiveness in workers subject to high levels of thermal strain. To quantify the effect of repeated cool water ingestion on the accuracy of GI pill temperature. Ten operational firefighters ingested a pill to measure GI temperature (T1int) before overnight sleep. Two hours following breakfast and 11.5 h after ingesting T1int, the firefighters ingested a second pill (T2int) before performing 8.5 h of intermittent activity (repetitive cycles of 30 min of seated rest followed by 30 min of general firefighter duties). During the first 2 min of each 30-min rest period, the firefighters consumed 250 mL of chilled water (5-8 degrees C). Water ingestion had a highly variable effect both within and between subjects in transiently (32 +/- 10 min) reducing the temperature of T2int in comparison with T1int. In general, this transient reduction in T2int became progressively smaller as time following ingestion increased. In some firefighters, the difference between T1int and T2int became negligible (+/- 0.1 degrees C) after 3 h, whereas in two others, large differences (peaking at 2.0 degrees C and 6.3 degrees C) were still observed when water was consumed 8 h after pill ingestion. These results show that a GI pill ingested immediately prior to physical activity cannot be used to measure core body temperature accurately in all individuals during the following 8 h when cool fluids are regularly ingested. This makes GI temperature measurement unsuitable for workers who respond to emergency deployments when regular fluid consumption is recommended operational practice.

Dual gas-diffusion membrane- and mediatorless dihydrogen/air-breathing biofuel cell operating at room temperature

NASA Astrophysics Data System (ADS)

Xia, Hong-qi; So, Keisei; Kitazumi, Yuki; Shirai, Osamu; Nishikawa, Koji; Higuchi, Yoshiki; Kano, Kenji

2016-12-01

A membraneless direct electron transfer (DET)-type dihydrogen (H2)/air-breathing biofuel cell without any mediator was constructed wherein bilirubin oxidase from Myrothecium verrucaria (BOD) and membrane-bound [NiFe] hydrogenase from Desulfovibrio vulgaris Miyazaki F (MBH) were used as biocatalysts for the cathode and the anode, respectively, and Ketjen black-modified water proof carbon paper (KB/WPCC) was used as an electrode material. The KB/WPCC surface was modified with 2-aminobenzoic acid and p-phenylenediamine, respectively, to face the positively charged electron-accepting site of BOD and the negatively charged electron-donating site of MBH to the electrode surface. A gas-diffusion system was employed for the electrodes to realize high-speed substrate supply. As result, great improvement in the current density of O2 reduction with BOD and H2 reduction with MBH were realized at negatively and postively charged surfaces, respectively. Gas diffusion system also suppressed the oxidative inactivation of MBH at high electrode potentials. Finally, based on the improved bioanode and biocathode, a dual gas-diffusion membrane- and mediatorless H2/air-breathing biofuel cell was constructed. The maximum power density reached 6.1 mW cm-2 (at 0.72 V), and the open circuit voltage was 1.12 V using 1 atm of H2 gas as a fuel at room temperature and under passive and quiescent conditions.

Observation of reduced 1/f noise in graphene field effect transistors on boron nitride substrates

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kayyalha, Morteza; School of Electrical and Computer Engineering, Purdue University, West Lafayette, Indiana 47907; Chen, Yong P., E-mail: yongchen@purdue.edu

2015-09-14

We have investigated the low frequency (f) flicker (also called 1/f) noise of single-layer graphene devices on h-BN (placed on SiO{sub 2}/Si) along with those on SiO{sub 2}/Si. We observe that the devices fabricated on h-BN have on average one order of magnitude lower noise amplitude compared with devices fabricated on SiO{sub 2}/Si despite having comparable mobilities at room temperature. We associate this noise reduction to the lower densities of impurities and trap sites in h-BN than in SiO{sub 2}. Furthermore, the gate voltage dependent noise amplitude shows a broad maximum at Dirac point for devices on h-BN, in contrastmore » to the M-shaped behavior showing a minimum at Dirac point for devices on SiO{sub 2}, consistent with the reduced charge inhomogeneity (puddles) for graphene on h-BN. This study demonstrates that the use of h-BN as a substrate or dielectric can be a simple and efficient noise reduction technique valuable for electronic applications of graphene and other nanomaterials.« less

Performance evaluation of Iranian cooling vest on the physiological indices in hot climatic chamber

PubMed Central

Dehghan, Habibollah; Gharehbaei, Somayeh; Mahaki, Behzad

2016-01-01

Background: Heat stress is a threat to those who work in high temperatures. The purpose in this study was an examination of the cooling ability of Iranian phase change material (PCM) cold vest in hot and dry conditions in a climatic chamber. Materials and Methods: This experimental study was implemented on 12 male students (age 23.7 ± 2.8 years, weight 66.1 ± 11.4 kg, and VO2 max 2.53 L/min) in 2013. The heat strain score index (HSSI), skin temperature and oral temperature, and heartbeat in two phases with and without cooling vest was measured during 30 min in a climatic chamber (temperature 38.8 ± 1.3°C humidity ratio 32.9 ± 2.3%) and in two activity intensity of 2.4 and 4.8 km/h speed on the treadmill, and the data differences between groups “with” and “without” vest were tested by t-test and repeated measurement. The level of significance was considered as 0.05. Results: The change in heartbeat at two activities, the oral temperature and heat strain score at 4.8 km/h, did not differ significantly between groups (with and without vest), as expected (P > 0.05). However, the change in skin temperature at two activities, oral temperature and heat strain score at 2.4 km/h, was significant between groups, as expected (P < 0.05). The average of skin temperature at 15th and 30th min during the experiment at two activities of 2.4 and 4.8 km/h was significant. Conclusion: The findings of the study indicated that using the Iranian PCM cold vest in hot and dry climate can affect the reduction of skin temperature, oral temperature, and HSSI in light activities. PMID:27500168

Performance evaluation of Iranian cooling vest on the physiological indices in hot climatic chamber.

PubMed

Dehghan, Habibollah; Gharehbaei, Somayeh; Mahaki, Behzad

2016-01-01

Heat stress is a threat to those who work in high temperatures. The purpose in this study was an examination of the cooling ability of Iranian phase change material (PCM) cold vest in hot and dry conditions in a climatic chamber. This experimental study was implemented on 12 male students (age 23.7 ± 2.8 years, weight 66.1 ± 11.4 kg, and VO2 max 2.53 L/min) in 2013. The heat strain score index (HSSI), skin temperature and oral temperature, and heartbeat in two phases with and without cooling vest was measured during 30 min in a climatic chamber (temperature 38.8 ± 1.3°C humidity ratio 32.9 ± 2.3%) and in two activity intensity of 2.4 and 4.8 km/h speed on the treadmill, and the data differences between groups "with" and "without" vest were tested by t-test and repeated measurement. The level of significance was considered as 0.05. The change in heartbeat at two activities, the oral temperature and heat strain score at 4.8 km/h, did not differ significantly between groups (with and without vest), as expected (P > 0.05). However, the change in skin temperature at two activities, oral temperature and heat strain score at 2.4 km/h, was significant between groups, as expected (P < 0.05). The average of skin temperature at 15(th) and 30(th) min during the experiment at two activities of 2.4 and 4.8 km/h was significant. The findings of the study indicated that using the Iranian PCM cold vest in hot and dry climate can affect the reduction of skin temperature, oral temperature, and HSSI in light activities.

New Ni-based quaternary disk-shaped catalysts for low-temperature CO2 methanation: Fabrication, characterization, and performance.

PubMed

Moon, Dea Hyun; Lee, Sang Moon; Ahn, Jeong Yoon; Nguyen, Dinh Duc; Kim, Sung Su; Chang, Soon Woong

2018-07-15

Ni-based quaternary disk catalysts were manufactured for low-temperature CO 2 methanation reactions, and the reaction activity was examined with respect to the thermal treatment conditions. By applying varying reduction and combustion treatments, the same catalysts were compared, and the Ni oxidation conditions and physical features were confirmed through X-Ray diffraction, scanning electron microscopy, and energy dispersive X-ray analyses. In addition, oxygen adsorption/desorption changes were measured by temperature-programmed reduction after pre-treating with oxygen and hydrogen. The reduction treatment catalyst showed a conversion of 20% at 280 °C, and the 70% calcined catalyst did not form a NiO crystalloid. The activation of the catalyst increased because of NiO movement on the catalyst surface, which enabled easy transformation to metallic Ni. The prepared catalyst is a highly reactive, yet stable, candidate for practical catalytic CO 2 methanation. Copyright © 2018 Elsevier Ltd. All rights reserved.

Investigation of Dynamics in BMIM TFSA Ionic Liquid through Variable Temperature and Pressure NMR Relaxometry and Diffusometry

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pilar, Kartik; Rua, Armando; Suarez, Sophia N.

A comprehensive variable temperature, pressure and frequency multinuclear ( 1H, 2H, and 19F) magnetic resonance study was undertaken on selectively deuterated 1-butyl-3-methylimidazolium bis(trifluoromethylsulfonyl)amide (BMIM TFSA) ionic liquid isotopologues. This study builds on our earlier investigation of the effects of increasing alkyl chain length on diffusion and dynamics in imidazolium-based TFSA ionic liquids. Fast field cycling 1H T 1 data revealed multiple modes of motion. Through calculation of diffusion coefficient (D) values and activation energies, the low- and high-field regimes were assigned to the translational and reorientation dynamics respectively. Variable-pressure 2H T 1 measurements reveal site-dependent interactions in the cation withmore » strengths in the order MD 3 > CD 3 > CD 2, indicating dissimilarities in the electric field gradients along the alkyl chain, with the CD 2 sites having the largest gradient. Additionally, the α saturation effect in T 1 vs. P was observed for all three sites, suggesting significant reduction of the short-range rapid reorientational dynamics. This reduction was also deduced from the variable pressure 1H T 1 data, which showed an approach to saturation for both the methyl and butyl group terminal methyl sites. Pressure-dependent D measurements show independent motions for both cations and anions, with the cations having greater D values over the entire pressure range.« less

Investigation of Dynamics in BMIM TFSA Ionic Liquid through Variable Temperature and Pressure NMR Relaxometry and Diffusometry

DOE PAGES

Pilar, Kartik; Rua, Armando; Suarez, Sophia N.; ...

2017-05-11

A comprehensive variable temperature, pressure and frequency multinuclear ( 1H, 2H, and 19F) magnetic resonance study was undertaken on selectively deuterated 1-butyl-3-methylimidazolium bis(trifluoromethylsulfonyl)amide (BMIM TFSA) ionic liquid isotopologues. This study builds on our earlier investigation of the effects of increasing alkyl chain length on diffusion and dynamics in imidazolium-based TFSA ionic liquids. Fast field cycling 1H T 1 data revealed multiple modes of motion. Through calculation of diffusion coefficient (D) values and activation energies, the low- and high-field regimes were assigned to the translational and reorientation dynamics respectively. Variable-pressure 2H T 1 measurements reveal site-dependent interactions in the cation withmore » strengths in the order MD 3 > CD 3 > CD 2, indicating dissimilarities in the electric field gradients along the alkyl chain, with the CD 2 sites having the largest gradient. Additionally, the α saturation effect in T 1 vs. P was observed for all three sites, suggesting significant reduction of the short-range rapid reorientational dynamics. This reduction was also deduced from the variable pressure 1H T 1 data, which showed an approach to saturation for both the methyl and butyl group terminal methyl sites. Pressure-dependent D measurements show independent motions for both cations and anions, with the cations having greater D values over the entire pressure range.« less

Honduran-U.S. Relations

DTIC Science & Technology

2010-02-01

government resources to finance poverty-reduction programs. Nonetheless, Honduras continues to face a poverty rate of nearly 70%, in addition to widespread...d’état” in Honduras (H.Res. 630, Delahunt) and calling upon the Micheletti government to end its “illegal seizure of power”(H.Res. 620, Serrano...2 Micheletti Government

Efficient and Selective Electrochemical and Photoelectrochemical Reduction of 5-Hydroxymethylfurfural to 2,5-Bis(hydroxymethyl)furan using Water as the Hydrogen Source

DOE PAGES

Roylance, John J.; Kim, Tae Woo; Choi, Kyoung-Shin

2016-02-17

Reductive biomass conversion has been conventionally conducted using H 2 gas under high-temperature and-pressure conditions. Here, efficient electrochemical reduction of 5-hydroxymethylfurfural (HMF), a key intermediate for biomass conversion, to 2,5-bis(hydroxymethyl)furan (BHMF), an important monomer for industrial processes, was demonstrated using Ag catalytic electrodes. This process uses water as the hydrogen source under ambient conditions and eliminates the need to generate and consume H 2 for hydrogenation, providing a practical and efficient route for BHMF production. By systematic investigation of HMF reduction on the Ag electrode surface, BHMF production was achieved with the Faradaic efficiency and selectivity nearing 100%, and plausiblemore » reduction mechanisms were also elucidated. Furthermore, construction of a photoelectrochemical cell (PEC) composed of an n-type BiVO 4 semiconductor anode, which uses photogenerated holes for water oxidation, and a catalytic Ag cathode, which uses photoexcited electrons from BiVO 4 for the reduction of HMF to BHMF, was demonstrated to utilize solar energy to significantly decrease the external voltage necessary for HMF reduction. This shows the possibility of coupling electrochemical HMF reduction and solar energy conversion, which can provide more efficient and environmentally benign routes for reductive biomass conversion.« less

Low Temperature Studies of the Removal Reactions of 1CH2 with Relevance to the Atmosphere of Titan

NASA Astrophysics Data System (ADS)

Douglas, Kevin; Slater, Eloise; Feng, Wuhu; Blitz, Mark; Plane, John; Heard, Dwayne; Seakins, Paul

2017-04-01

The photolysis of methane by UV photons is the primary source of hydrocarbon radicals in the atmosphere of Titan and the giant planets. Although there is still significant uncertainty in the branching ratios of products, the production of the first singlet excited state of methylene, 1CH2, is thought to be a significant channel. Reactions of 1CH2 with methane (R1a) and hydrogen (R2a) are a significant source of methyl radicals, the recombination of which is the primary route to ethane on Titan (R3). The reaction of 1CH2 with acetylene is also a source of propargyl, C3H3, the recombination of which is the primary route to benzene on Titan. However, in addition to these reactions of 1CH2 leading to chemical products, there is also competition between inelastic electronic relaxation to form ground triplet state methylene, 3CH2 (R1b and R2b). Triplet methylene is much less reactive, and cannot undergo the complex insertion elimination reactions of singlet methylene. The main reaction of 3CH2 occurs with other radical species such as H (R4). 1CH2 + CH4 → CH3 + H2 (R1a) 1CH2 + CH4 → 3CH2 + CH4 (R1b) 1CH2 + H2 → CH3 + H (R2a) 1CH2 + H2 → 3CH2 + H2 (R2a) CH3 + CH3 (+M) → C2H6 (R3) 3CH2 + H → CH + H2 (R4) Using pulsed laser photolysis laser-induced fluorescence, we have studied the reaction kinetics for the removal of 1CH2 with N2, H2, CH4, C2H6, C2H4, C2H6, and O2 as a function of temperature. Low temperatures between 43 and 135 K were obtained using a pulsed Laval nozzle apparatus, while data at 160 K was obtained using a low flow reaction cell with cryogenic cooling. In addition to measuring total removal rates, the fraction of 1CH2 removed via electronic relaxation versus chemical reaction to products has also been investigated for H2 and CH4 at 160 and 73 K. Results show that that removal of 1CH2 by electronic relaxation increases with decreasing temperature. These experimental results indicate that the majority of 1CH2 formed in Titan's atmosphere will be rapidly relaxed to its ground state via collisions with both reactive and non-reactive species, and thus is likely to play a less significant role in the formation of larger hydrocarbons than previously thought. However, for a full understanding of the implications of these results, the new measurements have been included in a 1D model of Titan's atmosphere. The model results show a significant reduction in ethane concentrations (10 - 50 %), due to reduction in CH3 production via reactions R1a and R1b. In addition we also observe an increase in ethylene concentrations, the result of increased amounts of 3CH2 reacting with H radicals to form CH (R4), which primarily react with methane to form ethylene. Additional work is also underway to determine branching ratios between reaction and relaxation of 1CH2 with ethane, ethylene, and acetylene. Model results have shown that if a similar trend to reactions with H2 and CH4 is observed, there would be significant reductions in benzene production on Titan.

Effect of incubation temperature and pH on the recovery of Bacillus weihenstephanensis spores after exposure to a peracetic acid-based disinfectant or to pulsed light.

PubMed

Trunet, C; Mtimet, N; Mathot, A-G; Postollec, F; Leguérinel, I; Couvert, O; Carlin, F; Coroller, L

2018-04-12

The recovery at a range of incubation temperatures and pH of spores of Bacillus weihenstephanensis KBAB4 exposed to a peracetic acid-based disinfectant (PABD) or to pulsed light was estimated. Spores of B. weihenstephanensis were produced at 30 °C and pH 7.00, at 30 °C and pH 5.50, or at 12 °C and pH 7.00. The spores were treated with a commercial peracetic acid-based disinfectant at 80 mg·mL -1 for 0 to 200 min at 18 °C or by pulsed light at fluences ranging between 0.4 and 2.3 J·cm -2 for pulsed light treatment. After each treatment, the spores were incubated on nutrient agar at 12 °C, 30 °C or 37 °C, or at pH 5.10, 6.00 or 7.40. Incubation temperature during recovery had a significant impact only near the recovery limits, beyond which surviving spores previously exposed to a PABD or to pulsed light were not able to form colonies. In contrast, a decrease in pH of the recovery nutrient agar had a progressive impact on the ability of spores to form colonies. The time to first log reduction after PABD treatment was 29.5 ± 0.7 min with recovery at pH 7.40, and was tremendously shortened 5.1 ± 0.2 min with recovery at pH 5.10. Concerning the fluence necessary for the first log reduction, it was 1.5 times higher when the spores were recovered at pH 6.00 compared to a recovery at pH 5.10. The impact of recovery temperature and pH can be described with a mathematical model using cardinal temperature and pH as parameters. These effects of temperature and pH on recovery of Bacillus weihenstephanensis spores exposed to a disinfectant combining peracetic acid and hydrogen peroxide, or pulsed light are similar, although these treatments are of different natures. Sporulation temperature or pH did not impact resistance to the peracetic acid-based disinfectant or pulsed light. Copyright © 2018 Elsevier B.V. All rights reserved.

Optimizing anti-coking abilities of zeolites by ethylene diamine tetraacetie acid modification on catalytic fast pyrolysis of corn stalk

NASA Astrophysics Data System (ADS)

Zhang, Bo; Zhong, Zhaoping; Song, Zuwei; Ding, Kuan; Chen, Paul; Ruan, Roger

2015-12-01

In order to minimize coke yield during biomass catalytic fast pyrolysis (CFP) process, ethylene diamine tetraacetie acid (EDTA) chemical modification method is carried out to selectively remove the external framework aluminum of HZSM-5 catalyst. X-ray diffraction (XRD), nitrogen (N2)-adsorption and ammonia-temperature programmed desorption (NH3-TPD) techniques are employed to investigate the porosity and acidity characteristics of original and modified HZSM-5 samples. Py-GC/MS and thermo-gravimetric analyzer (TGA) experiments are further conducted to explore the catalytic effect of modified HZSM-5 samples on biomass CFP and to verify the positive effect on coke reduction. Results show that EDTA treatment does not damage the crystal structure of HZSM-5 zeolites, but leads to a slight increase of pore volume and pore size. Meanwhile, the elimination of the strong acid peak indicates the dealumination of outer surface of HZSM-5 zeolites. Treatment time of 2 h (labeled EDTA-2H) is optimal for acid removal and hydrocarbon formation. Among all modified catalysts, EDTA-2H performs the best for deacidification and can obviously increase the yields of positive chemical compositions in pyrolysis products. Besides, EDTA modification can improve the anti-coking properties of HZSM-5 zeolites, and EDTA-2H gives rise to the lowest coke yield.

Modeling the survival of Escherichia coli O157:H7, Listeria monocytogenes, and Salmonella Typhimurium during fermentation, drying, and storage of soudjouk-style fermented sausage.

PubMed

Hwang, Cheng-An; Porto-Fett, Anna C S; Juneja, Vijay K; Ingham, Steven C; Ingham, Barbara H; Luchansky, John B

2009-02-28

This study quantified and modeled the survival of Escherichia coli O157:H7, Listeria monocytogenes and Salmonella Typhimurium in soudjouk-style fermented sausage during fermentation, drying, and storage. Batter prepared from ground beef (20% fat), seasonings, starter culture, and dextrose was separately inoculated with a multi-strain mixture of each pathogen to an initial inoculum of ca. 6.5 log(10) CFU/g in the batter. The sausages were subsequently fermented at 24 degrees C with a relative humidity (RH) of 90% to 95% for 3 to 5 days to ca. pH 5.2, pH 4.9 or pH 4.6, then dried at 22 degrees C to a(w) 0.92, a(w) 0.89, or a(w) 0.86, respectively, and then stored at 4, 21, or 30 degrees C for up to 60 days. Lethality of the three pathogens was modeled as a function of pH, a(w) and/or storage temperature. During fermentation to pH 5.2 to pH 4.6, cell reductions ranged from 0 to 0.9 log(10) CFU/g for E. coli O157:H7, 0.1 to 0.5 log(10) CFU/g for L. monocytogenes, and 0 to 2.2 log(10) CFU/g for S. Typhimurium. Subsequent drying of sausages of pH 5.2 to pH 4.6 at 22 degrees C with 80% to 85% RH for 3 to 7 days to a(w) of 0.92 to a(w) 0.86 resulted in additional reductions that ranged from 0 to 3.5 log(10) CFU/g for E. coli O157:H7, 0 to 0.4 log(10) CFU/g for L. monocytogenes, and 0.3 to 2.4 log(10) CFU/g for S. Typhimurium. During storage at 4, 21, or 30 degrees C the reduction rates of the three pathogens were generally higher (p<0.05) in sausages with lower pH and lower a(w) that were stored at higher temperatures. Polynomial equations were developed to describe the inactivation of the three pathogens during fermentation, drying, and storage. The applicability of the resulting models for fermented sausage was evaluated by comparing model predictions with published data. Pathogen reductions estimated by the models for E. coli O157:H7 and S. Typhimurium were comparable to 67% and 73% of published data, respectively. Due to limited published data for L. monocytogenes, the models for L. monocytogenes would need additional validations. Results of pathogen reductions from this study may be used as a reference to assist manufacturers of soudjouk-style sausages to adopt manufacturing processes that meet the regulatory requirements. The resulting models may also be used for estimating the survival of E. coli O157:H7 and S. Typhimurium in other similar fermented sausage during fermentation and storage.

Experimental investigation on thermochemical sulfate reduction by H2S initiation

USGS Publications Warehouse

Zhang, T.; Amrani, A.; Ellis, G.S.; Ma, Q.; Tang, Y.

2008-01-01

Hydrogen sulfide (H2S) is known to catalyze thermochemical sulfate reduction (TSR) by hydrocarbons (HC), but the reaction mechanism remains unclear. To understand the mechanism of this catalytic reaction, a series of isothermal gold-tube hydrous pyrolysis experiments were conducted at 330 ??C for 24 h under a constant confining pressure of 24.1 MPa. The reactants used were saturated HC (sulfur-free) and CaSO4 in the presence of variable H2S partial pressures at three different pH conditions. The experimental results showed that the in-situ pH of the aqueous solution (herein, in-situ pH refers to the calculated pH of aqueous solution under the experimental conditions) can significantly affect the rate of the TSR reaction. A substantial increase in the TSR reaction rate was recorded with a decrease in the in-situ pH value of the aqueous solution involved. A positive correlation between the rate of TSR and the initial partial pressure of H2S occurred under acidic conditions (at pH ???3-3.5). However, sulfate reduction at pH ???5.0 was undetectable even at high initial H2S concentrations. To investigate whether the reaction of H2S(aq) and HSO4- occurs at pH ???3, an additional series of isothermal hydrous pyrolysis experiments was conducted with CaSO4 and variable H2S partial pressures in the absence of HC at the same experimental temperature and pressure conditions. CaSO4 reduction was not measurable in the absence of paraffin even with high H2S pressure and acidic conditions. These experimental observations indicate that the formation of organosulfur intermediates from H2S reacting with hydrocarbons may play a significant role in sulfate reduction under our experimental conditions rather than the formation of elemental sulfur from H2S reacting with sulfate as has been suggested previously (Toland W. G. (1960) Oxidation of organic compounds with aqueous sulphate. J. Am. Chem. Soc. 82, 1911-1916). Quantification of labile organosulfur compounds (LSC), such as thiols and sulfides, was performed on the products of the reaction of H2S and HC from a series of gold-tube non-isothermal hydrous pyrolysis experiments conducted at about pH 3 from 300 to 370 ??C and a 0.1-??C/h heating rate. Incorporation of sulfur into HC resulted in an appreciable amount of thiol and sulfide formation. The rate of LSC formation positively correlated with the initial H2S pressure. Thus, we propose that the LSC produced from H2S reaction with HC are most likely the reactive intermediates for H2S initiation of sulfate reduction. We further propose a three-step reaction scheme of sulfate reduction by HC under reservoir conditions, and discuss the geological implications of our experimental findings with regard to the effect of formation water and oil chemistry, in particular LSC content. ?? 2008 Elsevier Ltd. All rights reserved.

Treatment of pulp and paper industry bleaching effluent by electrocoagulant process.

PubMed

Sridhar, R; Sivakumar, V; Prince Immanuel, V; Prakash Maran, J

2011-02-28

The experiments were carried out in an electrocoagulation reactor with aluminum as sacrificial electrodes. The influence of electrolysis time, current density, pH, NaCl concentration, rotational speed of the stirrer and electrode distance on reduction of color, COD and BOD were studied in detail. From the experimental results, 15 mA/cm(2) current density, pH of 7, 1 g/l NaCl, 100 rpm, 28°C temperature and 3 cm electrode distance were found to be optimum for maximum reduction of color, COD and BOD. The reduction of color, COD and BOD under the optimum condition were found to be 94%, 90% and 87% respectively. The electrode energy consumption was calculated and found to be varied from 10.1 to 12.9 kWh/m(3) depending on the operating conditions. Under optimal operating condition such as 15 mA/cm(2) current density, pH of 7, 1 g/l NaCl, 100 rpm, 28°C temperature and 3 cm electrode distance, the operating cost was found to be 1.56 US $/m(3). The experimental results proved that the electrocoagulation is a suitable method for treating bleaching plant effluents for reuse. Copyright © 2010 Elsevier B.V. All rights reserved.

Highly Loaded Fe-MCM-41 Materials: Synthesis and Reducibility Studies

PubMed Central

Mokhonoana, Malose P.; Coville, Neil J.

2009-01-01

Fe-MCM-41 materials were prepared by different methods. The Fe was both incorporated into the structure and formed crystallites attached to the silica. High Fe content MCM-41 (~16 wt%) with retention of mesoporosity and long-range order was achieved by a range of new synthetic methodologies: (i) by delaying the addition of Fe3+(aq) to the stirred synthesis gel by 2 h, (ii) by addition of Fe3+ precursor as a freshly-precipitated aqueous slurry, (iii) by exploiting a secondary synthesis with Si-MCM-41 as SiO2 source. For comparative purposes the MCM-41 was also prepared by incipient wetness impregnation (IWI). Although all these synthesis methods preserved mesoporosity and long-range order of the SiO2 matrix, the hydrothermally-fabricated Fe materials prepared via the secondary synthesis route has the most useful properties for exploitation as a catalyst, in terms of hydrothermal stability of the resulting support. Temperature-programmed reduction (TPR) studies revealed a three-peak reduction pattern for this material instead of the commonly observed two-peak reduction pattern. The three peaks showed variable intensity that related to the presence of two components: crystalline Fe2O3 and Fe embedded in the SiO2 matrix (on the basis of ESR studies). The role of secondary synthesis of Si-MCM-41 on the iron reducibility was also demonstrated in IWI of sec-Si-MCM-41.

H2O absorption tomography in a diesel aftertreatment system using a polymer film for optical access

NASA Astrophysics Data System (ADS)

Wang, Ze; Sanders, Scott T.; Backhaus, Jacob A.; Munnannur, Achuth; Schmidt, Niklas M.

2017-12-01

Film-optical-access H2O absorption tomography is, for the first time, applied to a practical diesel aftertreatment system. A single rotation stage and a single translation stage are used to move a single laser beam to obtain each of the 3480 line-of-sight measurements used in the tomographic reconstruction. It takes 1 h to acquire one image in a 60-view-angle measurement. H2O images are acquired in a 292.4-mm-diameter selective catalytic reduction (SCR) can with a 5-mm spatial resolution at temperatures in the 158-185 °C range. When no liquid H2O is injected into the gas, the L1 norm-based uniformity index is 0.994, and the average mole fraction error is - 6% based on a separate FTIR measurement. When liquid water is injected through the reductant dosing system designed to inject diesel exhaust fluid, nonuniformity is observed, as evidenced by measured uniformity indices for H2O in the 0.977-0.986 range. A mixing plate installed into the system is able to improve the uniformity of the H2O mole fraction.

Advanced Power Electronics Components

NASA Technical Reports Server (NTRS)

Schwarze, Gene E.

2004-01-01

This paper will give a description and status of the Advanced Power Electronics Materials and Components Technology program being conducted by the NASA Glenn Research Center for future aerospace power applications. The focus of this research program is on the following: 1) New and/or significantly improved dielectric materials for the development of power capacitors with increased volumetric efficiency, energy density, and operating temperature. Materials being investigated include nanocrystalline and composite ceramic dielectrics and diamond-like carbon films; 2) New and/or significantly improved high frequency, high temperature, low loss soft magnetic materials for the development of transformers/inductors with increased power/energy density, electrical efficiency, and operating temperature. Materials being investigated include nanocrystalline and nanocomposite soft magnetic materials; 3) Packaged high temperature, high power density, high voltage, and low loss SiC diodes and switches. Development of high quality 4H- and 6H- SiC atomically smooth substrates to significantly improve device performance is a major emphasis of the SiC materials program; 4) Demonstration of high temperature (> 200 C) circuits using the components developed above.

Computer Program for Calculation of a Gas Temperature Profile by Infrared Emission: Absorption Spectroscopy

NASA Technical Reports Server (NTRS)

Buchele, D. R.

1977-01-01

A computer program to calculate the temperature profile of a flame or hot gas was presented in detail. Emphasis was on profiles found in jet engine or rocket engine exhaust streams containing H2O or CO2 radiating gases. The temperature profile was assumed axisymmetric with an assumed functional form controlled by two variable parameters. The parameters were calculated using measurements of gas radiation at two wavelengths in the infrared. The program also gave some information on the pressure profile. A method of selection of wavelengths was given that is likely to lead to an accurate determination of the parameters. The program is written in FORTRAN IV language and runs in less than 60 seconds on a Univac 1100 computer.

Vanadium Flow Battery Electrolyte Synthesis via Chemical Reduction of V2O5 in Aqueous HCl and H2SO4.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Small, Leo J.; Pratt, Harry; Staiger, Chad

We report a simple method to synthesize V 4+ (VO 2+ ) electrolytes as feedstock for all- vanadium redox flow batteries (RFB). By dissolving V 2 O 5 in aqueous HCl and H 2 SO 4 , subsequently adding glycerol as a reducing agent, we have demonstrated an inexpensive route for electrolyte synthesis to concentrations >2.5 M V 4+ (VO 2+ ). Electrochemical analysis and testing of laboratory scale RFB demonstrate improved thermal stability across a wider temperature range (-10-65 degC) for V 4+ (VO 2+ ) electrolytes in HCl compared to in H 2 SO 4 electrolytes.

Inhibition of Mild Steel Corrosion in Sulfuric Acid Solution by New Schiff Base

PubMed Central

Al-Amiery, Ahmed A.; Kadhum, Abdul Amir H.; Kadihum, Abdulhadi; Mohamad, Abu Bakar; How, Chong K.; Junaedi, Sutiana

2014-01-01

The efficiency of Schiff base derived from 4-aminoantipyrine, namely 2-(1,5-dimethyl-4-(2-methylbenzylidene)amino)-2-phenyl-1H-pyrazol-3(2H)-ylidene) hydrazinecarbothioamide as a corrosion inhibitor on mild steel in 1.0 M H2SO4 was investigated using electrochemical impedance spectroscopy (EIS), potentiodynamic polarization (PD) and electrochemical frequently modulation (EFM) in addition to the adsorption isotherm, corrosion kinetic parameters and scanning electron microscopy (SEM). The results showed that this inhibitor behaved as a good corrosion inhibitor, even at low concentration, with a mean efficiency of 93% and, also, a reduction of the inhibition efficiency as the solution temperature increases. A polarization technique and EIS were tested for different concentrations and different temperatures to reveal that this compound is adsorbed on the mild steel, therefore blocking the active sites, and the adsorption follows the Langmuir adsorption isotherm model. The excellent inhibition effectiveness of 2-(1,5-dimethyl-4-(2-methylbenzylidene)amino)-2-phenyl-1H-pyrazol-3(2H)-ylidene)hydrazinecarbothioamide was also verified by scanning electron microscope (SEM). PMID:28788488

Inhibition of Mild Steel Corrosion in Sulfuric Acid Solution by New Schiff Base.

PubMed

Al-Amiery, Ahmed A; Kadhum, Abdul Amir H; Kadihum, Abdulhadi; Mohamad, Abu Bakar; How, Chong K; Junaedi, Sutiana

2014-01-28

The efficiency of Schiff base derived from 4-aminoantipyrine, namely 2-(1,5-dimethyl-4-(2-methylbenzylidene)amino)-2-phenyl-1H-pyrazol-3(2H)-ylidene) hydrazinecarbothioamide as a corrosion inhibitor on mild steel in 1.0 M H2SO4 was investigated using electrochemical impedance spectroscopy (EIS), potentiodynamic polarization (PD) and electrochemical frequently modulation (EFM) in addition to the adsorption isotherm, corrosion kinetic parameters and scanning electron microscopy (SEM). The results showed that this inhibitor behaved as a good corrosion inhibitor, even at low concentration, with a mean efficiency of 93% and, also, a reduction of the inhibition efficiency as the solution temperature increases. A polarization technique and EIS were tested for different concentrations and different temperatures to reveal that this compound is adsorbed on the mild steel, therefore blocking the active sites, and the adsorption follows the Langmuir adsorption isotherm model. The excellent inhibition effectiveness of 2-(1,5-dimethyl-4-(2-methylbenzylidene)amino)-2-phenyl-1H-pyrazol-3(2H)-ylidene)hydrazinecarbothioamide was also verified by scanning electron microscope (SEM).

Syngas Production from CO2 Reforming and CO2-steam Reforming of Methane over Ni/Ce-SBA-15 Catalyst

NASA Astrophysics Data System (ADS)

Tan, J. S.; Danh, H. T.; Singh, S.; Truong, Q. D.; Setiabudi, H. D.; Vo, D.-V. N.

2017-06-01

This study compares the catalytic performance of mesoporous 10 Ni/Ce-SBA-15 catalyst for CO2 reforming and CO2-steam reforming of methane reactions in syngas production. The catalytic performance of 10 Ni/Ce-SBA-15 catalyst for CO2 reforming and CO2-steam reforming of methane was evaluated in a temperature-controlled tubular fixed-bed reactor at stoichiometric feed composition, 1023 K and atmospheric pressure for 12 h on-stream with gas hourly space velocity (GHSV) of 36 L gcat -1 h-1. The 10 Ni/Ce-SBA-15 catalyst possessed a high specific BET surface area and average pore volume of 595.04 m2 g-1. The XRD measurement revealed the presence of NiO phase with crystallite dimension of about 13.60 nm whilst H2-TPR result indicates that NiO phase was completely reduced to metallic Ni0 phase at temperature beyond 800 K and the reduction temperature relied on different degrees of metal-support interaction associated with the location and size of NiO particles. The catalytic reactivity was significantly enhanced with increasing H2O/CO2 feed ratio. Interestingly, the H2/CO ratio for CO2-steam reforming of methane varied between 1 and 3 indicated the occurrence of parallel reactions, i.e., CH4 steam reforming giving a H2/CO of 3 whilst reverse water-gas shift (RWGS) reaction consuming H2 to produce CO gaseous product.

Nanocrystalline CeO2-δ coated β-MnO2 nanorods with enhanced oxygen transfer property

NASA Astrophysics Data System (ADS)

Huang, Xiubing; Zhao, Guixia; Chang, Yueqi; Wang, Ge; Irvine, John T. S.

2018-05-01

In this research, β-MnO2 nanorods were synthesized by a hydrothermal method, followed by a facile precipitation method to obtain nanocrystalline CeO2-δ coated β-MnO2 nanorods. The as-prepared samples were characterized by XRD, HRTEM, FESEM, XPS and in-situ high-temperature XRD. The HRTEM results show that well dispersed CeO2-δ nanocrystals sized about 5 nm were coated on the surface of β-MnO2 nanorods. The oxygen storage and transfer property of as-synthesized materials were evaluated using TGA under various atmospheres (air, pure N2, and 5%H2/95%Ar). The TGA results indicate that CeO2-δ modification could favour the reduction of Mn4+ to Mn3+ and/or Mn2+ at lower temperature as compared with pure β-MnO2 nanorods and the physically mixed CeO2-δ-β-MnO2 under low oxygen partial pressure conditions (i.e., pure N2, 5%H2/95%Ar). Specifically, CeO2-δ@β-MnO2 sample can exhibit 7.5 wt% weight loss between 100 and 400 °C under flowing N2 and 11.4 wt% weight loss between 100 and 350 °C under flowing 5%H2/95%Ar. During the reduction process under pure N2 or 5%H2/95%Ar condition, the oxygen ions in β-MnO2 nanorods are expected to be released to the surroundings in the form of O2 or H2O with the coated CeO2-δ nanocrystals acting as mediator as inferred from the synergistic effect between the well-interacted CeO2-δ nanocrystals and β-MnO2 nanorods.

Laser Raman Diagnostics in Subsonic and Supersonic Turbulent Jet Diffusion Flames.

NASA Astrophysics Data System (ADS)

Cheng, Tsarng-Sheng

1991-02-01

UV spontaneous vibrational Raman scattering combined with laser-induced predissociative fluorescence (LIPF) is developed for temperature and multi-species concentration measurements. For the first time, simultaneous measurements of temperature, major species (H_2, O_2, N_2, H_2O), and minor species (OH) concentrations are made with a "single" narrowband KrF excimer laser in subsonic and supersonic lifted turbulent hydrogen-air diffusion flames. The UV Raman system is calibrated with a flat -flame diffusion burner operated at several known equivalence ratios from fuel-lean to fuel-rich. Temperature measurements made by the ratio of Stokes/anti-Stokes signal and by the ideal gas law are compared. Single-shot uncertainties for temperature and concentration measurements are analyzed with photon statistics. Calibration constants and bandwidth factors are used in the data reduction program to arrive at temperature and species concentration measurements. UV Raman measurements in the subsonic lifted turbulent diffusion flame indicate that fuel and oxidizer are in rich, premixed, and unignited conditions in the center core of the lifted flame base. The unignited mixtures are due to rapid turbulent mixing that affects chemical reaction. Combustion occurs in an intermittent annular turbulent flame brush with strong finite-rate chemistry effects. The OH radical exists in sub-equilibrium and super-equilibrium concentrations. Major species and temperature are found with non-equilibrium values. Further downstream the super-equilibrium OH radicals decay toward equilibrium through slow three-body recombination reactions. In the supersonic lifted flame, a little reaction occurs upstream of the flame base, due to shock wave interactions and mixing with hot vitiated air. The strong turbulent mixing and total enthalpy fluctuations lead to temperature, major, and minor species concentrations with non-equilibrium values. Combustion occurs farther downstream of the lifted region. Slow three-body recombination reactions result in super-equilibrium OH concentrations that depress temperature below the equilibrium values. Near the equilibrium region, ambient air entrainment contaminates flame properties. These simultaneous measurements of temperature and multi-species concentrations allow a better understanding of the complex turbulence-chemistry interactions and provide information for the input and validation of CFD models.

A robust one-compartment fuel cell with a polynuclear cyanide complex as a cathode for utilizing H2O2 as a sustainable fuel at ambient conditions.

PubMed

Yamada, Yusuke; Yoneda, Masaki; Fukuzumi, Shunichi

2013-08-26

A robust one-compartment H2O2 fuel cell, which operates without membranes at room temperature, has been constructed by using a series of polynuclear cyanide complexes that contain Fe, Co, Mn, and Cr as cathodes, in sharp contrast to conventional H2 and MeOH fuel cells, which require membranes and high temperatures. A high open-circuit potential of 0.68 V was achieved by using Fe3[{Co(III)(CN)6}2] on a carbon cloth as the cathode and a Ni mesh as the anode of a H2O2 fuel cell by using an aqueous solution of H2O2 (0.30  M, pH 3) with a maximum power density of 0.45 mW cm(-2). The open-circuit potential and maximum power density of the H2O2 fuel cell were further increased to 0.78 V and 1.2 mW cm(-2), respectively, by operation under these conditions at pH 1. No catalytic activity of Co3[{Co(III)(CN)6}2] and Co3[{Fe(III)(CN)6}2] towards H2O2 reduction suggests that the N-bound Fe ions are active species for H2O2 reduction. H2O2 fuel cells that used Fe3[{Mn(III)(CN)6}2] and Fe3[{Cr(III)(CN)6}2] as the cathode exhibited lower performance compared with that using Fe3[{Co(III)(CN)6}2] as a cathode, because ligand isomerization of Fe3[{M(III)(CN)6}2] into (FeM2)[{Fe(II)(CN)6}2] (M = Cr or Mn) occurred to form inactive Fe-C bonds under ambient conditions, whereas no ligand isomerization of Fe3[{Co(III)(CN)6}2] occurred under the same reaction conditions. The importance of stable Fe(2+)-N bonds was further indicated by the high performance of the H2O2 fuel cells with Fe3[{Ir(III)(CN)6}2] and Fe3[{Rh(III)(CN)6}2], which also contained stable Fe(2+)-N bonds. The stable Fe(2+)-N bonds in Fe3[{Co(III)(CN)6}2], which lead to high activity for the electrocatalytic reduction of H2O2, allow Fe3[{Co(III)(CN)6}2] to act as a superior cathode in one-compartment H2O2 fuel cells. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Differences between young adults and elderly in thermal comfort, productivity, and thermal physiology in response to a moderate temperature drift and a steady-state condition.

PubMed

Schellen, L; van Marken Lichtenbelt, W D; Loomans, M G L C; Toftum, J; de Wit, M H

2010-08-01

Results from naturally ventilated buildings show that allowing the indoor temperature to drift does not necessarily result in thermal discomfort and may allow for a reduction in energy use. However, for stationary conditions, several studies indicate that the thermal neutral temperature and optimum thermal condition differ between young adults and elderly. There is a lack of studies that describe the effect of aging on thermal comfort and productivity during a moderate temperature drift. In this study, the effect of a moderate temperature drift on physiological responses, thermal comfort, and productivity of eight young adults (age 22-25 year) and eight older subjects (age 67-73 year) was investigated. They were exposed to two different conditions: S1-a control condition; constant temperature of 21.5 degrees C; duration: 8 h; and S2-a transient condition; temperature range: 17-25 degrees C, duration: 8 h, temperature drift: first 4 h: +2 K/h, last 4 h: -2 K/h. The results indicate that thermal sensation of the elderly was, in general, 0.5 scale units lower in comparison with their younger counterparts. Furthermore, the elderly showed more distal vasoconstriction during both conditions. Nevertheless, TS of the elderly was related to air temperature only, while TS of the younger adults also was related to skin temperature. During the constant temperature session, the elderly preferred a higher temperature in comparison with the young adults. Because the stock of fossil fuels is limited, energy savings play an important role. Thermal comfort is one of the most important performance indicators to successfully apply measures to reduce the energy need in buildings. Allowing drifts in indoor temperature is one of the options to reduce the energy demand. This study contributes to the knowledge concerning the effects of a moderate temperature drift and the age of the inhabitants on their thermal comfort.

Factors promoting in vitro excystation of Giardia muris cysts.

PubMed

Schaefer, F W; Rice, E W; Hoff, J C

1984-01-01

Giardia muris cysts, isolated from mouse faeces, excysted routinely at levels greater than 90%, when induced in 1X Hanks' supplemented with 17 mM glutathione, 29 mM L-cysteine-HCl, and 50 mM NaHCO3 for 30 minutes at 35 degrees C, followed by washing and suspension in trypsin-Tyrode's solution at pH 8.0. Although trypsin was not required in this final step, it enhanced the escape of the trophozoites from their cysts. G. muris excystation was dependent upon the length of the induction period, pH, oxidation-reduction potential and temperature. Optimal induction conditions for excystation were: an induction period of 5 to 30 min; pH of 2; 120 mV oxidation-reduction potential; and a temperature around 35 degrees C. A gradual decline in excystation occurred as pH and oxidation-reduction potential were changed to 7 and 57 mV, respectively. There was a pronounced increase in excystation percentages with increasing temperatures between 0 and 37 degrees C. At 40 degrees C and above, the G. muris cysts showed signs of inactivation. The thermal death point of G. muris cysts was determined to be about 54 degrees C. G. muris cysts showed no polarity; however, the tail or posterior trophozoite portion always emerged through one end of the cyst first. Cytokinensis began within the first hour after excystation. This method always produced extremely active, normal-looking G. muris trophozoites.

Enhanced Photoelectrochemical Behavior of H-TiO2 Nanorods Hydrogenated by Controlled and Local Rapid Thermal Annealing

NASA Astrophysics Data System (ADS)

Wang, Xiaodan; Estradé, Sonia; Lin, Yuanjing; Yu, Feng; Lopez-Conesa, Lluis; Zhou, Hao; Gurram, Sanjeev Kumar; Peiró, Francesca; Fan, Zhiyong; Shen, Hao; Schaefer, Lothar; Braeuer, Guenter; Waag, Andreas

2017-05-01

Recently, colored H-doped TiO2 (H-TiO2) has demonstrated enhanced photoelectrochemical (PEC) performance due to its unique crystalline core—disordered shell nanostructures and consequent enhanced conduction behaviors between the core-shell homo-interfaces. Although various hydrogenation approaches to obtain H-TiO2 have been developed, such as high temperature hydrogen furnace tube annealing, high pressure hydrogen annealing, hydrogen-plasma assisted reaction, aluminum reduction and electrochemical reduction etc., there is still a lack of a hydrogenation approach in a controlled manner where all processing parameters (temperature, time and hydrogen flux) were precisely controlled in order to improve the PEC performance of H-TiO2 and understand the physical insight of enhanced PEC performance. Here, we report for the first time a controlled and local rapid thermal annealing (RTA) approach to prepare hydrogenated core-shell H-TiO2 nanorods grown on F:SnO2 (FTO) substrate in order to address the degradation issue of FTO in the typical TiO2 nanorods/FTO system observed in the conventional non-RTA treated approaches. Without the FTO degradation in the RTA approach, we systematically studied the intrinsic relationship between the annealing temperature, structural, optical, and photoelectrochemical properties in order to understand the role of the disordered shell on the improved photoelectrochemical behavior of H-TiO2 nanorods. Our investigation shows that the improvement of PEC performance could be attributed to (i) band gap narrowing from 3.0 to 2.9 eV; (ii) improved optical absorption in the visible range induced by the three-dimensional (3D) morphology and rough surface of the disordered shell; (iii) increased proper donor density; (iv) enhanced electron-hole separation and injection efficiency due to the formation of disordered shell after hydrogenation. The RTA approach developed here can be used as a suitable hydrogenation process for TiO2 nanorods/FTO system for important applications such as photocatalysis, hydrogen generation from water splitting and solar energy conversion.

Enhanced Photoelectrochemical Behavior of H-TiO2 Nanorods Hydrogenated by Controlled and Local Rapid Thermal Annealing.

PubMed

Wang, Xiaodan; Estradé, Sonia; Lin, Yuanjing; Yu, Feng; Lopez-Conesa, Lluis; Zhou, Hao; Gurram, Sanjeev Kumar; Peiró, Francesca; Fan, Zhiyong; Shen, Hao; Schaefer, Lothar; Braeuer, Guenter; Waag, Andreas

2017-12-01

Recently, colored H-doped TiO 2 (H-TiO 2 ) has demonstrated enhanced photoelectrochemical (PEC) performance due to its unique crystalline core-disordered shell nanostructures and consequent enhanced conduction behaviors between the core-shell homo-interfaces. Although various hydrogenation approaches to obtain H-TiO 2 have been developed, such as high temperature hydrogen furnace tube annealing, high pressure hydrogen annealing, hydrogen-plasma assisted reaction, aluminum reduction and electrochemical reduction etc., there is still a lack of a hydrogenation approach in a controlled manner where all processing parameters (temperature, time and hydrogen flux) were precisely controlled in order to improve the PEC performance of H-TiO 2 and understand the physical insight of enhanced PEC performance. Here, we report for the first time a controlled and local rapid thermal annealing (RTA) approach to prepare hydrogenated core-shell H-TiO 2 nanorods grown on F:SnO 2 (FTO) substrate in order to address the degradation issue of FTO in the typical TiO 2 nanorods/FTO system observed in the conventional non-RTA treated approaches. Without the FTO degradation in the RTA approach, we systematically studied the intrinsic relationship between the annealing temperature, structural, optical, and photoelectrochemical properties in order to understand the role of the disordered shell on the improved photoelectrochemical behavior of H-TiO 2 nanorods. Our investigation shows that the improvement of PEC performance could be attributed to (i) band gap narrowing from 3.0 to 2.9 eV; (ii) improved optical absorption in the visible range induced by the three-dimensional (3D) morphology and rough surface of the disordered shell; (iii) increased proper donor density; (iv) enhanced electron-hole separation and injection efficiency due to the formation of disordered shell after hydrogenation. The RTA approach developed here can be used as a suitable hydrogenation process for TiO 2 nanorods/FTO system for important applications such as photocatalysis, hydrogen generation from water splitting and solar energy conversion.

Defining treatment conditions for pulsed electric field pasteurization of apple juice.

PubMed

Saldaña, G; Puértolas, E; Monfort, S; Raso, J; Alvarez, I

2011-11-15

The influence of temperature and the presence of N(α)-lauroyl ethylester (ethyl lauroyl arginate, LAE) on the inactivation caused by continuous pulsed electric field treatments (PEF) in Escherichia coli O157:H7 suspended in apple juice have been investigated to define treatment conditions applicable at industrial scale that promote an equivalent safety level when compared with thermal processing. In the range of experimental conditions investigated (outlet temperature: 20-40 °C, electric field strength: 20-30 kV, treatment time: 5-125 μs) at outlet temperatures equal or lower than 55±1 °C, the inactivation of E. coli O157:H7 treated in apple juice ranged from 0.4 to 3.6 Log₁₀ cycles reduction and treated in apple juice supplemented with LAE (50 ppm) ranged from 0.9 to 6.7 Log₁₀ cycles reduction. An empirical mathematical model was developed to estimate the treatment time and total specific energy input to obtain 5 Log₁₀ cycles reduction in the population of E. coli O157:H7 suspended in apple juice supplemented with 50 ppm of LAE at different electric field strengths and inlet temperatures. Treatment conditions established for E. coli O157:H7 were validated with other PEF resistant Gram-positive (Listeria monocytogenes, and Staphylococcus aureus) and Gram-negative (Salmonella enterica serovar Typhimurium) strains. When the treatment was applied to the apple juice, a treatment of 25 kV/cm for 63 μs corresponding with an outlet temperature of 65 °C and input energy of 125 kJ/kg was required to achieve more than 5 Log₁₀ cycles in the four strains investigated. The addition of LAE reduced the treatment time required to obtain an equivalent inactivation (>5 Log₁₀ cycles) in the four microorganisms to 38.4 μs, the outlet temperature to 55 °C, and the input energy to 83.2 kJ/kg. Copyright © 2011 Elsevier B.V. All rights reserved.

Inactivation of food spoilage microorganisms by hydrodynamic cavitation to achieve pasteurization and sterilization of fluid foods.

PubMed

Milly, P J; Toledo, R T; Harrison, M A; Armstead, D

2007-11-01

Hydrodynamic cavitation is the formation of gas bubbles in a fluid due to pressure fluctuations induced by mechanical means. Various high-acid (pH < [corrected]/= 4.6) fluid foods were processed in a hydrodynamic cavitation reactor to determine if commercial sterility can be achieved at reduced processing temperatures. Sporicidal properties of the process were also tested on a low-acid (pH > [corrected] 4.6) fluid food. Fluid foods were pumped under pressure into a hydrodynamic cavitation reactor and subjected to 2 rotor speeds and flow rates to achieve 2 designated exit temperatures. Thermal inactivation kinetics were used to determine heat-induced lethality for all organisms. Calcium-fortified apple juice processed at 3000 and 3600 rpm rotor speeds on the reactor went through a transient temperature change from 20 to 65.6 or 76.7 degrees C and the total process lethality exceeded 5-log reduction of Lactobacillus plantarum and Lactobacillus sakei cells, and Zygosaccharomyces bailii cells and ascospores. Tomato juice inoculated with Bacillus coagulans spores and processed at 3000 and 3600 rpm rotor speeds endured a transient temperature from 37.8 to 93.3 or 104.4 degrees C with viable CFU reductions of 0.88 and 3.10 log cycles, respectively. Skim milk inoculated with Clostridium sporogenes putrefactive anaerobe 3679 spores and processed at 3000 or 3600 rpm rotor speeds endured a transient temperature from 48.9 to 104.4 or 115.6 degrees C with CFU reductions of 0.69 and 2.84 log cycles, respectively. Utilizing hydrodynamic cavitation to obtain minimally processed pasteurized low-acid and commercially sterilized high-acid fluid foods is possible with appropriate process considerations for different products.

Gas phase recovery of hydrogen sulfide contaminated polymer electrolyte membrane fuel cells

NASA Astrophysics Data System (ADS)

Kakati, Biraj Kumar; Kucernak, Anthony R. J.

2014-04-01

The effect of hydrogen sulfide (H2S) on the anode of a polymer electrolyte membrane fuel cell (PEMFC) and the gas phase recovery of the contaminated PEMFC using ozone (O3) were studied. Experiments were performed on fuel cell electrodes both in an aqueous electrolyte and within an operating fuel cell. The ex-situ analyses of a fresh electrode; a H2S contaminated electrode (23 μmolH2S cm-2); and the contaminated electrode cleaned with O3 shows that all sulfide can be removed within 900 s at room temperature. Online gas analysis of the recovery process confirms the recovery time required as around 720 s. Similarly, performance studies of an H2S contaminated PEMFC shows that complete rejuvenation occurs following 600-900 s O3 treatment at room temperature. The cleaning process involves both electrochemical oxidation (facilitated by the high equilibrium potential of the O3 reduction process) and direct chemical oxidation of the contaminant. The O3 cleaning process is more efficient than the external polarization of the single cell at 1.6 V. Application of O3 at room temperature limits the amount of carbon corrosion. Room temperature O3 treatment of poisoned fuel cell stacks may offer an efficient and quick remediation method to recover otherwise inoperable systems.

Process for the preparation of benozotriazoles and their polymers, and 2(2-hydroxy-5-isopropenylphenyl)2H-benzotriazole produced thereby

DOEpatents

Vogl, Otto; Nir, Zohar

1989-03-14

The compound 2(2-hydroxy-5-isopropenylphenyl)2H-benzotriazole (2H5P) is produced by azo coupling of o-nitrophenyl diazonium chloride with p-hydroxyacetophenone, subjecting the resulting isolated azo compound to reductive cyclization with zinc in the presence of sodium hydroxide at a temperature of about 50.degree.-70.degree. C., acidifying the resulting mixture so as to produce (2(2-hydroxy-5-acetylphenyl)2H-benzotriazole (2H5A), acetylating the isolated 2(2-hydroxy-5-acetylphenyl)2H-benzotriazole (2H5A), so as to produce 2(2-acetoxy-5-acetylphenyl)2H-benzotriazole (2A5A), methylating the isolated 2(2-acetoxy-5-acetylphenyl(2H-benzotriazole (2A5A) with a methyl Grignard reagent and dehydrating the isolated reaction product with potassium hydrogen sulfate so as to produce 2(2-hydroxy-5-isopropenylphenyl)2H-benzotriazole (2H5P). The compound is used as a polymerizable ultra violet light stabilizer.

Laboratory and in-situ reductions of soluble phosphorus in swine waste slurries.

PubMed

Burns, R T; Moody, L B; Walker, F R; Raman

2001-11-01

Laboratory and field experiments were conducted using magnesium chloride (MgCl2) to force the precipitation of struvite (MgNH4PO4 x 6H2O) and reduce the concentration of soluble phosphorus (SP) in swine waste. In laboratory experiments, reductions of SP of 76% (572 to 135 mg P l(-1)) were observed in raw swine manure after addition of magnesium chloride (MgCl2) at a rate calculated to provide a 1.6:1 molar ratio of magnesium (Mg) to total phosphorus. Adjusting the pH of the treated manure to pH 9.0 with sodium hydroxide (NaOH) increased SP reduction to 91% (572 to 50 mg P l(-1)). X-ray diffraction of the precipitate recovered from swine waste slurry treated only with MgCl2 confirmed the presence ofstruvite. The molar N:P:Mg ratio of the recovered precipitate was 1:1.95:0.24, suggesting that compounds in addition to struvite were formed. In a field experiment conducted in a swine manure holding pond, a 90% reduction in SP concentration was observed in approximately 140,000 l of swine manure slurry treated before land application with 2,000 l MgCl2 (64% solution) at ambient slurry temperatures ranging from 5 to 10 degrees C.

Properties of immobile hydrogen confined in microporous carbon

DOE PAGES

Bahadur, Jitendra; Bhabha Atomic Research Centre; Contescu, Cristian I.; ...

2017-03-06

The mobility of H2 confined in microporous carbon was studied as a function of temperature and pressure using inelastic neutron scattering, and the translational and rotational motion of H2 molecules has been probed. At low loading, rotation of H2 molecules adsorbed in the smallest carbon pores (~6 ) is severely hindered, suggesting that the interaction between H2 and the host matrix is anisotropic. At higher loading, H2 molecules behave as nearly free rotor, implying lower anisotropic interactions with adsorption sites. At supercritical temperatures where bulk H2 is a gas, the inelastic spectrum of confined H2 provides evidence of a significantmore » fraction of immobile, solid-like hydrogen. The onset temperature for molecular mobility depends strongly on the loaded amount. The fraction of immobile molecules increases with pressure and attains a plateau at high pressures. Surprisingly, immobile H2 is present even at temperatures as high as ~110 K. This research at ORNL s Spallation Neutron Source was sponsored by the Scientific User Facilities Division, Office of Basic Energy Sciences, U. S. Department of Energy. This research was supported in part by the ORNL Postdoctoral Research Associates Program, administered jointly by the ORNL and the Oak Ridge Institute for Science and Education. CIC and NCG acknowledge support from the Materials Science and Engineering Division, Office of Basic Energy Sciences, U.S. Department of Energy.« less

Synthesis of Supported Pd 0 Nanoparticles from a Single-Site Pd 2+ Surface Complex by Alkene Reduction

DOE PAGES

Mouat, Aidan R.; Whitford, Cassandra L.; Chen, Bor-Rong; ...

2018-02-02

Here, a surface metal–organic complex, (-AlO x)Pd(acac) (acac = acetylacetonate), is prepared by chemically grafting the precursor Pd(acac) 2 onto γ-Al 2O 3 in toluene at 25 °C. The resulting surface complex is characterized by inductively coupled plasma atomic emission spectroscopy (ICP-AES), X-ray photoelectron spectroscopy (XPS), X-ray absorption spectroscopy (XAS), and dynamic nuclear polarization surface-enhanced solid-state nuclear magnetic resonance spectroscopy (DNP SENS). This surface complex is a precursor in the direct synthesis of size-controlled Pd nanoparticles under mild reductive conditions and in the absence of additional stabilizers or pretreatments. Indeed, upon exposure to gaseous ethylene or liquid 1-octene at 25more » °C, the Pd 2+ species is reduced to form Pd 0 nanoparticles with a mean diameter of 4.3 ± 0.6 nm, as determined by scanning transmission electron microscopy (STEM). These nanoparticles are catalytically relevant using the aerobic 1-phenylethanol oxidation as a probe reaction, with rates comparable to a conventional Pd/Al 2O 3 catalyst but without an induction period. Diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) and temperature-programmed reaction mass spectrometry (TPR-MS) reveal that the surface complex reduction with ethylene coproduces H 2, acetylene, and 1,3-butadiene. This process reasonably proceeds via an olefin activation/coordination/insertion pathway, followed by β-hydride elimination to generate free Pd 0. Lastly, the well-defined nature of the single-site supported Pd 2+ precursor provides direct mechanistic insights into this unusual and likely general reductive process.« less

Synthesis of Supported Pd 0 Nanoparticles from a Single-Site Pd 2+ Surface Complex by Alkene Reduction

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mouat, Aidan R.; Whitford, Cassandra L.; Chen, Bor-Rong

Here, a surface metal–organic complex, (-AlO x)Pd(acac) (acac = acetylacetonate), is prepared by chemically grafting the precursor Pd(acac) 2 onto γ-Al 2O 3 in toluene at 25 °C. The resulting surface complex is characterized by inductively coupled plasma atomic emission spectroscopy (ICP-AES), X-ray photoelectron spectroscopy (XPS), X-ray absorption spectroscopy (XAS), and dynamic nuclear polarization surface-enhanced solid-state nuclear magnetic resonance spectroscopy (DNP SENS). This surface complex is a precursor in the direct synthesis of size-controlled Pd nanoparticles under mild reductive conditions and in the absence of additional stabilizers or pretreatments. Indeed, upon exposure to gaseous ethylene or liquid 1-octene at 25more » °C, the Pd 2+ species is reduced to form Pd 0 nanoparticles with a mean diameter of 4.3 ± 0.6 nm, as determined by scanning transmission electron microscopy (STEM). These nanoparticles are catalytically relevant using the aerobic 1-phenylethanol oxidation as a probe reaction, with rates comparable to a conventional Pd/Al 2O 3 catalyst but without an induction period. Diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) and temperature-programmed reaction mass spectrometry (TPR-MS) reveal that the surface complex reduction with ethylene coproduces H 2, acetylene, and 1,3-butadiene. This process reasonably proceeds via an olefin activation/coordination/insertion pathway, followed by β-hydride elimination to generate free Pd 0. Lastly, the well-defined nature of the single-site supported Pd 2+ precursor provides direct mechanistic insights into this unusual and likely general reductive process.« less

Reduction of mixed Mn-Zr oxides: in situ XPS and XRD studies.

PubMed

Bulavchenko, O A; Vinokurov, Z S; Afonasenko, T N; Tsyrul'nikov, P G; Tsybulya, S V; Saraev, A A; Kaichev, V V

2015-09-21

A series of mixed Mn-Zr oxides with different molar ratios Mn/Zr (0.1-9) have been prepared by coprecipitation of manganese and zirconium nitrates and characterized by X-ray diffraction (XRD) and BET methods. It has been found that at concentrations of Mn below 30 at%, the samples are single-phase solid solutions (MnxZr1-xO2-δ) based on a ZrO2 structure. X-ray photoelectron spectroscopy (XPS) measurements showed that manganese in these solutions exists mainly in the Mn(4+) state on the surface. An increase in Mn content mostly leads to an increase in the number of Mn cations in the structure of solid solutions; however, a part of the manganese cations form Mn2O3 and Mn3O4 in the crystalline and amorphous states. The reduction of these oxides with hydrogen was studied by a temperature-programmed reduction technique, in situ XRD, and near ambient pressure XPS in the temperature range from 100 to 650 °C. It was shown that the reduction of the solid solutions MnxZr1-xO2-δ proceeds via two stages. During the first stage, at temperatures between 100 and 500 °C, the Mn cations incorporated into the solid solutions MnxZr1-xO2-δ undergo partial reduction. During the second stage, at temperatures between 500 and 700 °C, Mn cations segregate on the surface of the solid solution. In the samples with more than 30 at% Mn, the reduction of manganese oxides was observed: Mn2O3 → Mn3O4 → MnO.

The reactions of thiophene on Mo(110) and Mo(110)-p(2×2)-S

NASA Astrophysics Data System (ADS)

Roberts, Jeffrey T.; Friend, C. M.

1987-07-01

The reactions of thiophene and 2,5-dideuterothiophene on Mo(110) and Mo(110)-p(2×2)-S have been investigated under ultrahigh vacuum conditions using temperature programmed reaction spectroscopy and Auger electron spectroscopy. Thiophene chemisorbed on Mo(110) decomposes during temperature programmed reaction to yield only gaseous dihydrogen, surface carbon, and surface sulfur. At low thiophene exposures, dihydrogen evolves from Mo(110) in a symmetric peak at 440 K. At saturation exposures, three dihydrogen peaks are detected at 360 K, at 420 K and at 565 K. Multilayers of thiophene desorb at 180 K. Temperature programmed reaction of 2,5-dideuterothiophene demonstrates that at high thiophene coverages, one of the α-C-H bonds (those nearest sulfur) breaks first. No bond breaking selectivity is observed at low thiophene exposures. The Mo(110)-p(2×2)-S surface is less active for thiophene decomposition. Thiophene adsorbed on Mo(110)-p(2×2)-S to low coverages decomposes to surface carbon surface sulfur, and hydrogen at 430 K. At reaction saturation, dihydrogen production is observed at 375 and 570 K. In addition, at moderate and high exposures, chemisorbed thiophene desorbs from Mo(110)-p(2×2)-S. At saturation the desorption temperature of the reversibly chemisorbed state is 215 K. Experiments with 2,5-dideuterothiophene demonstrate no surface selectivity for α-C-H bond breaking reactions on Mo(110)-p(2×2)-S. The decomposition mechanism and energetics of thiophene decomposition are proposed to be dependent on the coverage of thiophene. At low thiophene exposures, the ring is proposed to bond parallel to the surface. All C-H bonds in the parallel geometry are sterically available for activation by the surface, accounting for the lack of selectivity in C-H bond breaking. High thiophene coverages are suggested to result in perpendicularly bound thiophene which undergoes selective α-dehydrogenation to an α)-thiophenyl intermediate. The presence of sulfur leads to a high energy pathway for cleavage of C-H bonds in a thiophene derived intermediate. Carbon-hydrogen bonds survive on the surface up to temperatures of 650 K. Comparison of this study with work on Mo(100) demonstrates that the reaction of thiophene on molybdenum is relatively insensitive to the surface geometric structure.

Cobalt–iron nano catalysts supported on TiO{sub 2}–SiO{sub 2}: Characterization and catalytic performance in Fischer–Tropsch synthesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Feyzi, Mostafa, E-mail: Dalahoo2011@yahoo.com; Yaghobi, Nakisa; Eslamimanesh, Vahid

2015-12-15

Graphical abstract: The Co–Fe/TiO{sub 2}–SiO{sub 2} catalysts were prepared. The prepared catalysts were tested for light olefins and C{sub 5}–C{sub 12} production. The best operational conditions are 250 °C, H{sub 2}/CO = 1/1 under 5 bar pressure. - Highlights: • The TiO{sub 2}–SiO{sub 2} supported cobalt–iron catalysts were prepared via sol–gel method. • The best operational conditions were 250 °C, GHSV = 2000 h{sup −1}, H{sub 2}/CO = 1/1 and 5 bar. • The (Co/Fe)/TiO{sub 2}–SiO{sub 2} is efficient catalyst for light olefins and C{sub 5}–C{sub 12} production. - Abstract: A series of Co–Fe catalysts supported on TiO{sub 2}–SiO{sub 2}more » were prepared by the sol–gel method. This research investigated the effects of (Co/Fe) wt.%, the solution pH, different Co/Fe molar ratio, calcination conditions and different promoters on the catalytic performance of cobalt–iron catalysts for the Fisher–Tropsch synthesis (FTS). It was found that the catalyst containing 35 wt.% (Co–Fe)/TiO{sub 2}–SiO{sub 2} (Co/Fe molar ratio is 80/20) promoted with 1.5 wt.% Cu and calcined in air atmosphere at 600 °C for 7 h with a heating rate of 3 °C min{sup −1} is an optimal nano catalyst for converting synthesis gas to light olefins and C{sub 5}–C{sub 12} hydrocarbons. The effects of operational conditions such as the H{sub 2}/CO ratio, gas hourly space velocity (GHSV), different reaction temperature, and reaction pressure were investigated. The results showed that the best operational conditions for optimal nano catalyst are 250 °C, GHSV = 2000 h{sup −1}, H{sub 2}/CO molar ratio 1/1 under 5 bar total pressure. Catalysts and precursors were characterized by, X-ray diffraction (XRD), scanning electron microcopy (SEM), thermal gravimetric analysis (TGA), differential scanning calorimetry (DSC), temperature program reduction (TPR) and N{sub 2} adsorption–desorption measurements.« less

Toxic hexavalent chromium reduction by Bacillus pumilis, Cellulosimicrobium cellulans and Exiguobacterium

NASA Astrophysics Data System (ADS)

Rehman, Fatima; Faisal, Muhammad

2015-05-01

Three bacterial strains Bacillus pumilis, Cellulosimicrobium cellulans and Exiguobacterium were investigated when grown in Luria-Bertani (LB) medium at 500 μg/mL Cr(VI). The hexavalent chromium reduction was measured by growing the strains in DeLeo and Ehrlich (1994) medium at 200 and 400 μg/mL K2CrO4. The optimal Cr (VI) reduction by strains B. pumilis, Exigubacterium and C. cellulans was 51%, 39%, and 41%, respectively, at an initial K2CrO4 concentration of 200 μg/mL at pH 3 and temperature 37°C. At an initial chromate concentration of 400 μg/mL, the Cr(VI) reduction by strains B. pumilis, Exigubacterium and C. cellulans was 24%, 19%, and 18%, respectively at pH 3 at 37°C after 24 h. These strains have ability to reduce toxic hexavalent chromium to the less mobile trivalent chromium at a wide range of different environmental conditions and can be useful for the treatment of contaminated wastewater and soils.

Preparation of Si3N4 Form Diatomite via a Carbothermal Reduction-Nitridation Process

NASA Astrophysics Data System (ADS)

Ma, Bin; Huang, Zhaohui; Mei, Lefu; Fang, Minghao; Liu, Yangai; Wu, Xiaowen; Hu, Xiaozhi

2016-05-01

Si3N4 was produced using diatomite and sucrose as silicon and carbon sources, respectively. The effect of the C/SiO2 molar ratio, heating temperature and soaking time on the morphology and phase compositions of the final products was investigated by scanning electron microscopy, x-ray diffraction analysis and energy dispersive spectroscopy. The phase equilibrium relationships of the system at different heating temperatures were also investigated based on the thermodynamic analysis. The results indicate that the phase compositions depended on the C/SiO2 molar ratio, heating temperature and soaking time. Fabrication of Si3N4 from the precursor via carbothermal reduction nitridation was achieved at 1550°C for 1-8 h using a C/SiO2 molar ratio of 3.0. The as-prepared Si3N4 contained a low amount of Fe3Si (<1 wt.%).

Direct Observation by Rapid-Scan FT-IR Spectroscopy of Two-Electron-Reduced Intermediate of Tetraaza Catalyst [Co IIN 4H(MeCN)] 2+ Converting CO 2 to CO

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sheng, Hua; Frei, Heinz

In the search for the two-electron-reduced intermediate of the tetraaza catalyst [Co IIN 4H(MeCN)] 2+ (N 4H = 2,12-dimethyl-3,7,11,17-tetraazabicyclo[11.3.1]heptadeca-1(17),2,11,13,15-pentaene) for CO 2 reduction and elementary steps that result in the formation of CO product, rapid-scan FT-IR spectroscopy of the visible-light-sensitized catalysis, using Ir(ppy) 3 in wet acetonitrile (CD 3CN) solution, led to the observation of two sequential intermediates. The initially formed one-electron-reduced [Co IN 4H] +--CO 2 adduct was converted by the second electron to a transient [Co IN 4H] +--CO 2 - complex that spontaneously converted CO 2 to CO in a rate-limiting step on the second time scalemore » in the dark under regeneration of the catalyst (room temperature). The macrocycle IR spectra of the [Co IN 4H] +--CO 2 - complex and the preceding one-electron [Co IN 4H] +--CO 2 intermediate show close similarity but distinct differences in the carboxylate modes, indicating that the second electron resides mainly on the CO 2 ligand. Vibrational assignments are corroborated by 13C isotopic labeling. The structure and stability of the two-electron-reduced intermediate derived from the time-resolved IR study are in good agreement with recent predictions by DFT electronic structure calculations. This is the first observation of an intermediate of a molecular catalyst for CO 2 reduction during the bond-breaking step producing CO. The reaction pathway for the Co tetraaza catalyst uncovered here suggests that the competition between CO 2 reduction and proton reduction of a macrocyclic multi-electron catalyst is steered toward CO 2 activation if the second electron is directly captured by an adduct of CO 2 and the one-electron-reduced catalyst intermediate.« less

Interactive effects of near-future temperature increase and ocean acidification on physiology and gonad development in adult Pacific sea urchin, Echinometra sp . A

NASA Astrophysics Data System (ADS)

Uthicke, S.; Liddy, M.; Nguyen, H. D.; Byrne, M.

2014-09-01

Increased atmospheric CO2 will have a twofold impact on future marine ecosystems, increasing global sea surface temperatures and uptake of CO2 (Ocean Acidification). Many experiments focus on the investigation of one of these stressors, but under realistic future climate predictions, these stressors may have interactive effects on individuals. Here, we investigate the effect of warming and acidification in combination. We test for interactive effects of potential near-future (2100) temperature (+2 to 3 °C) and pCO2 (~860-940 μAtm) levels on the physiology of the tropical echinoid Echinometra sp . A. The greatest reduction in growth was under simultaneous temperature and pH/ pCO2 stress (marginally significant temperature × pH/ pCO2 interaction). This was mirrored by the physiological data, with highest metabolic activity (measured as respiration and ammonium excretion) occurring at the increased temperature and pCO2 treatment, although this was not significant for excretion. The perivisceral coelomic fluid pH was ~7.5-7.6, as typical for echinoids, and showed no significant changes between treatments. Indicative of active calcification, internal magnesium and calcium concentrations were reduced compared to the external medium, but were not different between treatments. Gonad weight was lower at the higher temperature, and this difference was more distinct and statistically significant for males. The condition of the gonads assessed by histology declined in increased temperature and low pH treatments. The Echinometra grew in all treatments indicating active calcification of their magnesium calcite tests even as carbonate mineral saturation decreased. Our results indicate that the interactive temperature and pH effects are more important for adult echinoids than individual stressors. Although adult specimens grow and survive in near-future conditions, higher energy demands may influence gonad development and thus population maintenance.

Platinum-mordenite catalysts for n-Hexane isomerization: Characterization by X-ray absorption spectroscopy and chemical probes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Otten, M.M.; Clayton, M.J.; Lamb, H.H.

Platinum-mordenite (Pt-MOR) catalysts were prepared from NH{sub 4}-MOR by ion exchange with (Pt{sup II}(NH{sub 3}){sub 4})(OH){sub 2}, calcination in O{sub 2} at 350{degrees}C, and reduction in H{sub 2} at 350{degrees}C. The resultant Pt-H-MOR was active for n-hexane isomerization and hydrocracking via bifunctional catalysis at 240-300{degrees}C and 1 atm. The observed activation energies for C{sub 6} branched-isomer formation are unusually low, suggesting that the isomerization rates were controlled by pore diffusion. A Pt-KH-MOR catalyst was prepared by ion exchange with aqueous KNO{sub 3} and re-reduction at 350{degrees}C; elemental analysis evidenced 90% exchange of protons for K{sup +} ions. The product distributionmore » and observed activation energies for C{sub 6} branched-isomer formation over Pt-KH-MOR are consistent with n-hexane isomerization via bifunctional catalysis. Hydrocracking was strongly suppressed, and light hydrocarbons were formed primarily by Pt-catalyzed hydrogenolysis. From in-situ extended X-ray absorption fine structure spectroscopy and H{sub 2} temperature-programmed desorption, we conclude that the Pt-MOR catalysts consist of small Pt clusters hosted within the mordenite crystals. The PtL{sub III}X-ray absorption near-edge structure (XANES) spectra of Pt-H-MOR and Pt-KH-MOR are closely similar, suggesting that the electronic structure of the Pt clusters is unaffected by mordenite acid-base chemistry. The infrared spectrum of CO adsorbed on Pt-H-MOR contains an intense band at 2084 cm{sup -1}, which is assigned to linear CO moieties on Pt clusters. The infrared spectrum of CO adsorbed on Pt-KH-MOR evidences a red shift of the linear CO band, which the authors suggest is due to electrostatic interactions between carbonyl O atoms and nearby K{sup +} ions. 45 refs., 9 figs., 6 tabs.« less

Optimization study of ethanolic fermentation from oil palm trunk, rubberwood and mixed hardwood hydrolysates using Saccharomyces cerevisiae.

PubMed

Chin, K L; H'ng, P S; Wong, L J; Tey, B T; Paridah, M T

2010-05-01

Ethanolic fermentation using Saccharomyces cerevisiae was carried out on three types of hydrolysates produced from lignocelulosic biomass which are commonly found in Malaysia such as oil palm trunk, rubberwood and mixed hardwood. The effect of fermentation temperature and pH of hydrolysate was evaluated to optimize the fermentation efficiency which defined as maximum ethanol yield in minimum fermentation time. The fermentation process using different temperature of 25 degrees Celsius, 30 degrees Celsius and 40 degrees Celsius were performed on the prepared fermentation medium adjusted to pH 4, pH 6 and pH 7, respectively. Results showed that the fermentation time was significantly reduced with the increase of temperature but an adverse reduction in ethanol yield was observed using temperature of 40 degrees Celsius. As the pH of hydrolysate became more acidic, the ethanol yield increased. Optimum fermentation efficiency for ethanolic fermentation of lignocellulosic hydrolysates using S. cerevisiae can be obtained using 33.2 degrees Celsius and pH 5.3. Copyright 2009 Elsevier Ltd. All rights reserved.

Regeneration of aluminum hydride

DOEpatents

Graetz, Jason Allan; Reilly, James J.

2009-04-21

The present invention provides methods and materials for the formation of hydrogen storage alanes, AlH.sub.x, where x is greater than 0 and less than or equal to 6 at reduced H.sub.2 pressures and temperatures. The methods rely upon reduction of the change in free energy of the reaction between aluminum and molecular H.sub.2. The change in free energy is reduced by lowering the entropy change during the reaction by providing aluminum in a state of high entropy, by increasing the magnitude of the change in enthalpy of the reaction or combinations thereof.

Assessment of tomato and wine processing solid wastes as soil amendments for biosolarization.

PubMed

Achmon, Yigal; Harrold, Duff R; Claypool, Joshua T; Stapleton, James J; VanderGheynst, Jean S; Simmons, Christopher W

2016-02-01

Pomaces from tomato paste and wine production are the most abundant fruit processing residues in California. These residues were examined as soil amendments for solarization to promote conditions conducive to soil disinfestation (biosolarization). Simulated biosolarization studies were performed in both aerobic and anaerobic soil environments and soil temperature elevation, pH, and evolution of CO2, H2 and CH4 gases were measured as metrics of soil microbial activity. Tomato pomace amendment induced conditions associated with soil pest inactivation, including elevation of soil temperature by up to 2°C for a duration of 4days under aerobic conditions and a reduction of soil pH from 6.5 to 4.68 under anaerobic conditions. White wine grape pomace amendment showed similar trends but to a lesser extent. Red wine grape pomace was generally less suitable for biosolarization due to significantly lower soil temperature elevations, reduced acidification relative to the other pomaces and induction of methanogenesis in the soil. Copyright © 2015 Elsevier Ltd. All rights reserved.

Reactive impinging-flow technique for polymer-electrolyte-fuel-cell electrode-defect detection

DOE PAGES

Zenyuk, Iryna V.; Englund, Nicholas; Bender, Guido; ...

2016-09-29

Reactive impinging flow (RIF) is a novel quality-control method for defect detection (i.e., reduction in Pt catalyst loading) in gas-diffusion electrodes (GDEs) on weblines. The technique uses infrared thermography to detect temperature of a nonflammable (<4% H 2) reactive mixture of H 2/O 2 in N 2 impinging and reacting on a Pt catalytic surface. In this article, different GDE size defects (with catalyst-loading reductions of 25, 50, and 100%) are detected at various webline speeds (3.048 and 9.144 m min -1) and gas flowrates (32.5 or 50 standard L min -1). Furthermore, a model is developed and validated formore » the technique, and it is subsequently used to optimize operating conditions and explore the applicability of the technique to a range of defects. The model suggests that increased detection can be achieved by recting more of the impinging H 2, which can be accomplished by placing blocking substrates on the top, bottom, or both of the GDE; placing a substrate on both results in a factor of four increase in the temperature differential, which is needed for smaller defect detection. Lastly, overall, the RIF technique is shown to be a promising route for in-line, high-speed, large-area detection of GDE defects on moving weblines.« less

Reactive impinging-flow technique for polymer-electrolyte-fuel-cell electrode-defect detection

NASA Astrophysics Data System (ADS)

Zenyuk, Iryna V.; Englund, Nicholas; Bender, Guido; Weber, Adam Z.; Ulsh, Michael

2016-11-01

Reactive impinging flow (RIF) is a novel quality-control method for defect detection (i.e., reduction in Pt catalyst loading) in gas-diffusion electrodes (GDEs) on weblines. The technique uses infrared thermography to detect temperature of a nonflammable (<4% H2) reactive mixture of H2/O2 in N2 impinging and reacting on a Pt catalytic surface. In this paper, different GDE size defects (with catalyst-loading reductions of 25, 50, and 100%) are detected at various webline speeds (3.048 and 9.144 m min-1) and gas flowrates (32.5 or 50 standard L min-1). Furthermore, a model is developed and validated for the technique, and it is subsequently used to optimize operating conditions and explore the applicability of the technique to a range of defects. The model suggests that increased detection can be achieved by recting more of the impinging H2, which can be accomplished by placing blocking substrates on the top, bottom, or both of the GDE; placing a substrate on both results in a factor of four increase in the temperature differential, which is needed for smaller defect detection. Overall, the RIF technique is shown to be a promising route for in-line, high-speed, large-area detection of GDE defects on moving weblines.

Observations of the temperature dependent response of ozone to NOx reductions in the Sacramento, CA urban plume

NASA Astrophysics Data System (ADS)

Lafranchi, B. W.; Goldstein, A. H.; Cohen, R. C.

2011-02-01

Observations of NOx in the Sacramento, CA region show that mixing ratios decreased by 30% between 2001 and 2008. Here we use an observation-based method to quantify net ozone production rates in the outflow from the Sacramento metropolitan region and examine the O3 decrease resulting from reductions in NOx emissions. This observational method does not rely on assumptions about detailed chemistry of ozone production, rather it is an independent means to verify and test these assumptions. We use an instantaneous steady-state model as well as a detailed 1-D plume model to aid in interpretation of the ozone production inferred from observations. In agreement with the models, the observations show that early in the plume, the NOx dependence for Ox (Ox = O3 + NO2) production is strongly coupled with temperature, suggesting that temperature-dependent biogenic VOC emissions can drive Ox production between NOx-limited and NOx-suppressed regimes. As a result, NOx reductions were found to be most effective at higher temperatures over the 7 year period. We show that violations of the California 1-hour O3 standard (90 ppb) in the region have been decreasing linearly with decreases in NOx (at a given temperature) and predict that reductions of NOx concentrations (and presumably emissions) by an additional 30% (relative to 2007 levels) will eliminate violations of the state 1 h standard in the region. If current trends continue, a 30% decrease in NOx is expected by 2012, and an end to violations of the 1 h standard in the Sacramento region appears to be imminent.

EQUILGAS: Program to estimate temperatures and in situ two-phase conditions in geothermal reservoirs using three combined FT-HSH gas equilibria models

NASA Astrophysics Data System (ADS)

Barragán, Rosa María; Núñez, José; Arellano, Víctor Manuel; Nieva, David

2016-03-01

Exploration and exploitation of geothermal resources require the estimation of important physical characteristics of reservoirs including temperatures, pressures and in situ two-phase conditions, in order to evaluate possible uses and/or investigate changes due to exploitation. As at relatively high temperatures (>150 °C) reservoir fluids usually attain chemical equilibrium in contact with hot rocks, different models based on the chemistry of fluids have been developed that allow deep conditions to be estimated. Currently either in water-dominated or steam-dominated reservoirs the chemistry of steam has been useful for working out reservoir conditions. In this context, three methods based on the Fischer-Tropsch (FT) and combined H2S-H2 (HSH) mineral-gas reactions have been developed for estimating temperatures and the quality of the in situ two-phase mixture prevailing in the reservoir. For these methods the mineral buffers considered to be controlling H2S-H2 composition of fluids are as follows. The pyrite-magnetite buffer (FT-HSH1); the pyrite-hematite buffer (FT-HSH2) and the pyrite-pyrrhotite buffer (FT-HSH3). Currently from such models the estimations of both, temperature and steam fraction in the two-phase fluid are obtained graphically by using a blank diagram with a background theoretical solution as reference. Thus large errors are involved since the isotherms are highly nonlinear functions while reservoir steam fractions are taken from a logarithmic scale. In order to facilitate the use of the three FT-HSH methods and minimize visual interpolation errors, the EQUILGAS program that numerically solves the equations of the FT-HSH methods was developed. In this work the FT-HSH methods and the EQUILGAS program are described. Illustrative examples for Mexican fields are also given in order to help the users in deciding which method could be more suitable for every specific data set.

Effect of active zinc oxide dispersion on reduced graphite oxide for hydrogen sulfide adsorption at mid-temperature

NASA Astrophysics Data System (ADS)

Song, Hoon Sub; Park, Moon Gyu; Croiset, Eric; Chen, Zhongwei; Nam, Sung Chan; Ryu, Ho-Jung; Yi, Kwang Bok

2013-09-01

Composites of Zinc oxide (ZnO) with reduced graphite oxide (rGO) were synthesized and used as adsorbents for hydrogen sulfide (H2S) at 300 °C. Various characterization methods (TGA, XRD, FT-IR, TEM and XPS) were performed in order to link their H2S adsorption performance to the properties of the adsorbent's surface. Microwave-assisted reduction process of graphite oxide (GO) provided mild reduction environment, allowing oxygen-containing functional groups to remain on the rGO surface. It was confirmed that for the ZnO/rGO synthesize using the microwave-assisted reduction method, the ZnO particle size and the degree of ZnO dispersion remained stable over time at 300 °C, which was not the case for only the ZnO particles themselves. This stable highly dispersed feature allows for sustained high surface area over time. This was confirmed through breakthrough experiments for H2S adsorption where it was found that the ZnO/rGO composite showed almost four times higher ZnO utilization efficiency than ZnO itself. The effect of the H2 and CO2 on H2S adsorption was also investigated. The presence of hydrogen in the H2S stream had a positive effect on the removal of H2S since it allows a reducing environment for Znsbnd O and Znsbnd S bonds, leading to more active sites (Zn2+) to sulfur molecules. On the other hand, the presence of carbon dioxide (CO2) showed the opposite trend, likely due to the oxidation environment and also due to possible competitive adsorption between H2S and CO2.

Kinetic and catalytic analysis of mesoporous metal oxides on the oxidation of Rhodamine B

NASA Astrophysics Data System (ADS)

Xaba, Morena S.; Noh, Ji-Hyang; Mokgadi, Keabetswe; Meijboom, Reinout

2018-05-01

In this study, we demonstrate the synthesis and catalytic activity of different mesoporous transition metal oxides, silica (SiO2), copper oxide (CuO), chromium oxide (Cr2O3), iron oxide (Fe2O3) cobalt oxide (Co3O4), cerium oxide (CeO2) and nickel oxide (NiO), on the oxidation of a pollutant dye, Rhodamine B (RhB). These metal oxides were synthesized by inverse micelle formation method and characterized by transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray diffraction (XRD), adsorption-desorption isotherms (BET) and H2-temperature programmed reduction (TPR). UV-vis spectrophotometry was used to monitor the time-resolved absorbance of RhB at λmax = 554 nm. Mesoporous copper oxide was calcined at different final heating temperatures of 250, 350, 450 and 550 °C, and each mesoporous copper oxide catalyst showed unique physical properties and catalytic behavior. Mesoporous CuO-550 with the smallest characteristic path length δ, proved to be the catalyst of choice for the oxidation of RhB in aqueous media. We observed that the oxidation of RhB in aqueous media is dependent on the crystallite size and characteristic path length of the mesoporous metal oxide. The Langmuir-Hinshelwood model was used to fit the experimental data and to prove that the reaction occurs on the surface of the mesoporous CuO. The thermodynamic parameters, EA, ΔH#, ΔS# and ΔG# were calculated and catalyst recycling and reusability were demonstrated.

Influence of physicochemical treatments on iron-based spent catalyst for catalytic oxidation of toluene.

PubMed

Kim, Sang Chai; Shim, Wang Geun

2008-06-15

The catalytic oxidation of toluene was studied over an iron-based spent and regenerated catalysts. Air, hydrogen, or four different acid solutions (oxalic acid (C2H2O4), citric acid (C6H8O7), acetic acid (CH3COOH), and nitric acid (HNO3)) were employed to regenerate the spent catalyst. The properties of pretreated spent catalyst were characterized by the Brunauer Emmett Teller (BET), inductively coupled plasma (ICP), temperature programmed reduction (TPR), and X-ray diffraction (XRD) analyses. The air pretreatment significantly enhanced the catalytic activity of the spent catalyst in the pretreatment temperature range of 200-400 degrees C, but its catalytic activity diminished at the pretreatment temperature of 600 degrees C. The catalytic activity sequence with respect to the air pretreatment temperatures was 400 degrees C>200 degrees C>parent>600 degrees C. The TPR results indicated that the catalytic activity was correlated with both the oxygen mobility and the amount of available oxygen on the catalyst. In contrast, the hydrogen pretreatment had a negative effect on the catalytic activity, and toluene conversion decreased with increasing pretreatment temperatures (200-600 degrees C). The XRD and TPR results confirmed the formation of metallic iron which had a negative effect on the catalytic activity with increasing pretreatment temperature. The acid pretreatment improved the catalytic activity of the spent catalyst. The catalytic activity sequence with respect to different acids pretreatment was found to be oxalic acid>citric acid>acetic acid>or=nitric acid>parent. The TPR results of acid pretreated samples showed an increased amount of available oxygen which gave a positive effect on the catalytic activity. Accordingly, air or acid pretreatments were more promising methods of regenerating the iron-based spent catalyst. In particular, the oxalic acid pretreatment was found to be most effective in the formation of FeC2O4 species which contributed highly to the catalytic combustion of toluene.

Adsorption, Desorption, and Displacement Kinetics of H2O and CO2 on TiO2(110)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Smith, R. Scott; Li, Zhenjun; Chen, Long

The adsorption, desorption, and displacement kinetics of H2O and CO2 on TiO2(110) are investigated using temperature programmed desorption (TPD) and molecular beam techniques. The TPD spectra for both H2O and CO2 have well-resolved peaks corresponding to desorption from bridge-bonded oxygen (BBO), Ti, and oxygen vacancies (VO) sites in order of increasing peak temperature. Analysis of the saturated monolayer peak for both species reveals that the corresponding adsorption energies on all sites are greater for H2O and for CO2. Sequential dosing of H2O and CO2 reveals that, independent of the dose order, H2O molecules will displace CO2 in order to occupymore » the highest energy binding sites available. Isothermal experiments show that the displacement of CO2 by H2O occurs between 75 and 80 K. Further analysis shows that a ratio of 4 H2O to 3 CO2 molecules is needed to displace CO2 from the TiO2(110) surface.« less

Resonant tunneling modulation in quasi-2D Cu(2)O/SnO(2) p-n horizontal-multi-layer heterostructure for room temperature H(2)S sensor application.

PubMed

Cui, Guangliang; Zhang, Mingzhe; Zou, Guangtian

2013-01-01

Heterostructure material that acts as resonant tunneling system is a major scientific challenge in applied physics. Herein, we report a resonant tunneling system, quasi-2D Cu(2)O/SnO(2) p-n heterostructure multi-layer film, prepared by electrochemical deposition in a quasi-2D ultra-thin liquid layer. By applying a special half-sine deposition potential across the electrodes, Cu(2)O and SnO(2) selectively and periodically deposited according to their reduction potentials. The as-prepared heterostructure film displays excellent sensitivity to H(2)S at room temperature due to the resonant tunneling modulation. Furthermore, it is found that the laser illumination could enhance the gas response, and the mechanism with laser illumination is discussed. It is the first report on gas sensing application of resonant tunneling modulation. Hence, heterostructure material act as resonant tunneling system is believed to be an ideal candidate for further improvement of room temperature gas sensing.

Cascade Reductive Etherification of Bioderived Aldehydes over Zr-Based Catalysts.

PubMed

Shinde, Suhas; Rode, Chandrashekhar

2017-10-23

An efficient one-pot catalytic cascade sequence has been developed for the production of value-added ethers from bioderived aldehydes. Etherification of 5-(hydroxymethyl)furfural with different aliphatic alcohols over acidic Zr-montmorillonite (Zr-Mont) catalyst produced a mixture of 5-(alkoxymethyl)furfural and 2-(dialkoxymethyl)-5-(alkoxymethyl)furan. The latter was selectively converted back into 5-(alkoxymethyl)furfural by treating it with water over the same catalyst. The synthesis of 2,5-bis(alkoxymethyl)furan was achieved through a cascade sequence involving etherification, transfer hydrogenation, and re-etherification over a combination of acidic Zr-Mont and the charge-transfer hydrogenation catalyst [ZrO(OH) 2 ]. This catalyst combination was further explored for the cascade conversion of 2-furfuraldehyde into 2-(alkoxymethyl)furan. The scope of this strategy was then extended for the reductive etherification of lignin-derived arylaldehydes to obtain the respective benzyl ethers in >80 % yield. Additionally, the mixture of Zr-Mont and ZrO(OH) 2 does not undergo mutual destruction, which was proved by recycling experiments and XRD analysis. Both the catalysts were thoroughly characterized using BET, temperature-programmed desorption of NH 3 and CO 2 , pyridine-FTIR, XRD, inductively coupled plasma optical emission spectroscopy, and X-ray photoelectron spectroscopy techniques. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Below-Room-Temperature C–H Bond Breaking on an Inexpensive Metal Oxide: Methanol to Formaldehyde on CeO 2(111)

DOE PAGES

Sutton, Jonathan E.; Danielson, Thomas; Beste, Ariana; ...

2017-11-14

C-H bond breaking is important for industrial commodity and specialty chemical transformations, including the upgrading of alcohols. Small primary alcohols – methanol and ethanol – are used industrially as precursors for the corresponding aldehydes at industrial scales. However, upgrading these primary alcohols involves C-H bond breaking and the processes are run at elevated temperatures (> 200 °C). In this work, new understanding from temperature programmed reaction (TPR) studies with methanol over a CeO 2(111) surface show the C-H bond breaking and the subsequent desorption of formaldehyde, even below room temperature. This is of particular interests because CeO 2 is amore » naturally abundant, inexpensive metal oxide. We combine density functional theory (DFT) and kinetic Monte Carlo (KMC) to simulate the TPR of methanol on CeO2. Our simulations show that the low temperature C H bond breaking occurs via disproportionation of adjacent methoxy species to form methanol and formaldehyde which each then desorb. We further show from DFT calculations that the same transition state with comparably low activation energies should be possible for other sustainable primary alcohols, with ethanol, 1-propanol, and 1-butanol having been explicitly calculated. In conclusion, these findings point out a new class of transition states to search for in seeking low temperature C-H bond breaking over inexpensive metal oxides.« less

Below-Room-Temperature C–H Bond Breaking on an Inexpensive Metal Oxide: Methanol to Formaldehyde on CeO 2(111)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sutton, Jonathan E.; Danielson, Thomas; Beste, Ariana

C-H bond breaking is important for industrial commodity and specialty chemical transformations, including the upgrading of alcohols. Small primary alcohols – methanol and ethanol – are used industrially as precursors for the corresponding aldehydes at industrial scales. However, upgrading these primary alcohols involves C-H bond breaking and the processes are run at elevated temperatures (> 200 °C). In this work, new understanding from temperature programmed reaction (TPR) studies with methanol over a CeO 2(111) surface show the C-H bond breaking and the subsequent desorption of formaldehyde, even below room temperature. This is of particular interests because CeO 2 is amore » naturally abundant, inexpensive metal oxide. We combine density functional theory (DFT) and kinetic Monte Carlo (KMC) to simulate the TPR of methanol on CeO2. Our simulations show that the low temperature C H bond breaking occurs via disproportionation of adjacent methoxy species to form methanol and formaldehyde which each then desorb. We further show from DFT calculations that the same transition state with comparably low activation energies should be possible for other sustainable primary alcohols, with ethanol, 1-propanol, and 1-butanol having been explicitly calculated. In conclusion, these findings point out a new class of transition states to search for in seeking low temperature C-H bond breaking over inexpensive metal oxides.« less

Reduction of hexavalent chromium by the thermophilic methanogen Methanothermobacter thermautotrophicus

DOE PAGES

Singh, Rajesh; Dong, Hailiang; Liu, Deng; ...

2014-10-22

Despite the significant progress on iron reduction by thermophilic microorganisms, studies on their ability to reduce toxic metals are still limited, despite their common co-existence in high temperature environments (up to 70°C). In this study, Methanothermobacter thermautotrophicus, an obligate thermophilic methanogen, was used to reduce hexavalent chromium. Experiments were conducted in a growth medium with H 2/CO 2 as substrate with various Cr 6+ concentrations (0.2, 0.4, 1, 3, and 5 mM) in the form of potassium dichromate (K 2Cr 2O 7). Time-course measurements of aqueous Cr 6+ concentrations with the 1, 5-diphenylcarbazide colorimetric method showed complete reduction of themore » 0.2 and 0.4 mM Cr 6+ solutions by this methanogen. However, much lower reduction extents of 43.6%, 13.0%, and 3.7% were observed at higher Cr 6+ concentrations of 1, 3 and 5 mM, respectively. These lower extents of bioreduction suggest a toxic effect of aqueous Cr 6+ to cells at this concentration range. At these higher Cr 6+ concentrations, methanogenesis was inhibited and cell growth was impaired as evidenced by decreased total cellular protein production and live/dead cell ratio. Likewise, Cr 6+ bioreduction rates decreased with increased initial concentrations of Cr 6+ from 13.3 to1.9 μM h ₋1. X-ray absorption near-edge structure (XANES) spectroscopy revealed a progressive reduction of soluble Cr 6+ to insoluble Cr 3+ precipitates, which was confirmed as amorphous chromium hydroxide by X-ray diffraction and selected area electron diffraction pattern. However, a small fraction of reduced Cr occurred as aqueous Cr 3+. Scanning and transmission electron microscope observations of M. thermautotrophicus cells after Cr 6+ exposure suggest both extra- and intracellular chromium reduction mechanisms. Results of this study demonstrate the ability of M. thermautotrophicus cells to reduce toxic Cr 6+ to less toxic Cr 3+ and its potential application in metal bioremediation, especially at high temperature subsurface radioactive waste disposal sites, where the temperature may reach ~70°C.« less

Combined effects of cadmium, temperature and hypoxia-reoxygenation on mitochondrial function in rainbow trout (Oncorhynchus mykiss).

PubMed

Onukwufor, John O; Stevens, Don; Kamunde, Collins

2017-01-01

Although aquatic organisms face multiple environmental stressors that may interact to alter adverse outcomes, our knowledge of stressor-stressor interaction on cellular function is limited. We investigated the combined effects of cadmium (Cd), hypoxia-reoxygenation (H-R) and temperature on mitochondrial function. Liver mitochondria from juvenile rainbow trout were exposed to Cd (0-20μM) and H-R (0 and 5min) at 5, 13 and 25°C followed by measurements of mitochondrial Cd load, volume, complex І active (A)↔deactive (D) transition, membrane potential, ROS release and ultrastructural changes. At high temperature Cd exacerbated H-R-imposed reduction of maximal complex I (CI) respiration whereas at low temperature 5 and 10μM stimulated maximal CI respiration post H-R. The basal respiration showed a biphasic response at high temperatures with low Cd concentrations reducing the stimulatory effect of H-R and high concentrations enhancing this effect. At low temperature Cd monotonically enhanced H-R-induced stimulation of basal respiration. Cd and H-R reduced both the P/O ratio and the RCR at all 3 temperatures. Temperature rise alone increased mitochondrial Cd load and toxicity, but combined H-R and temperature exposure reduced mitochondrial Cd load but surprisingly exacerbated the mitochondrial dysfunction. Mitochondrial dysfunction induced by H-R was associated with swelling of the organelle and blocking of conversion of CІ D to A form. However, low amounts of Cd protected against H-R induced swelling and prevented the inhibition of H-R-induced CI D to A transition. Both H-R and Cd dissipated mitochondrial membrane potential Δψ m and damaged mitochondrial structure. We observed increased reactive oxygen species (H 2 O 2 ) release that together with the protection afforded by EGTA, vitamin E and N-acetylcysteine against the Δψ m dissipation suggested direct involvement of Cd and oxidative stress. Overall, our findings indicate that mitochondrial sensitivity to Cd toxicity was enhanced by the effects of H-R and temperature, and changes in mitochondrial Cd load did not always explain this effect. Copyright © 2016 Elsevier B.V. All rights reserved.

Observation of internal transport barrier in ELMy H-mode plasmas on the EAST tokamak

NASA Astrophysics Data System (ADS)

Yang, Y.; Gao, X.; Liu, H. Q.; Li, G. Q.; Zhang, T.; Zeng, L.; Liu, Y. K.; Wu, M. Q.; Kong, D. F.; Ming, T. F.; Han, X.; Wang, Y. M.; Zang, Q.; Lyu, B.; Li, Y. Y.; Duan, Y. M.; Zhong, F. B.; Li, K.; Xu, L. Q.; Gong, X. Z.; Sun, Y. W.; Qian, J. P.; Ding, B. J.; Liu, Z. X.; Liu, F. K.; Hu, C. D.; Xiang, N.; Liang, Y. F.; Zhang, X. D.; Wan, B. N.; Li, J. G.; Wan, Y. X.; EAST Team

2017-08-01

The internal transport barrier (ITB) has been obtained in ELMy H-mode plasmas by neutron beam injection and lower hybrid wave heating on the Experimental Advanced Superconducting Tokamak (EAST). The ITB structure has been observed in profiles of ion temperature, electron temperature, and electron density within ρ < 0.5. It was also observed that the ITB formation is stepwise. Due to the ITB formation, the confinement quality H 98y2 increases from 1 to 1.1 and the normalized beta, β N, increases from 1.5 to near 2. The fishbone activity observed during the ITB phase suggests the central safety factor q(0) ˜ 1. Transport coefficients are calculated by particle balance and power balance analysis, showing an obvious reduction after the ITB formation.

Hydrogen retention in lithium and lithium oxide films

DOE PAGES

Buzi, L.; Yang, Y.; Dominguez-Gutierrez, F. J.; ...

2018-02-09

Pure lithium (Li) surfaces are difficult to maintain in fusion devices due to rapid oxide formation, therefore, parameterizing and understanding the mechanisms of hydrogen (H, D) retention in lithium oxide (Li 2O) in addition to pure Li is crucial for Li plasma-facing material applications. To compare H retention in Li and Li 2O films, measurements were made as a function of surface temperature (90–520 K) under ultrahigh vacuum (UHV) conditions using temperature programmed desorption (TPD). In both cases, the total retention dropped with surface temperature, from 95% at 90 K to 35% at 520 K Li 2O films retained Hmore » in similar amounts as pure Li. Finally, Molecular Dynamics (MD) modeling was used to elucidate the mechanisms of H retention, and results were consistent with experiments in terms of both retention fraction and the drop of retention with temperature.« less

Hydrogen retention in lithium and lithium oxide films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Buzi, L.; Yang, Y.; Dominguez-Gutierrez, F. J.

Pure lithium (Li) surfaces are difficult to maintain in fusion devices due to rapid oxide formation, therefore, parameterizing and understanding the mechanisms of hydrogen (H, D) retention in lithium oxide (Li 2O) in addition to pure Li is crucial for Li plasma-facing material applications. To compare H retention in Li and Li 2O films, measurements were made as a function of surface temperature (90–520 K) under ultrahigh vacuum (UHV) conditions using temperature programmed desorption (TPD). In both cases, the total retention dropped with surface temperature, from 95% at 90 K to 35% at 520 K Li 2O films retained Hmore » in similar amounts as pure Li. Finally, Molecular Dynamics (MD) modeling was used to elucidate the mechanisms of H retention, and results were consistent with experiments in terms of both retention fraction and the drop of retention with temperature.« less

A Meteorological Rocket Data Reduction Program with Automated Temperature Processing.

DTIC Science & Technology

1982-01-01

WRD3 CPI 003Q WORD3 (ZERO) 005A C2 61 00 1490 JNZ WRD4 005D AF 1500 ZERO XRA A 005E C3 C8 00 1510 JMP XMIT 0061 FE 04 1520 WRD4 CPI 004Q WORD4 (HD, TD ...is made by typing (tl, is th, v,.’tii unI ilt o’r ’(:A)I) 8300l:. 0KI . CONTROL MI’H tO ie SVSten rsponds with ’>’, the file PRINT. can t’ examined...hy pro( tss rig the radar ficId tapc DR friIitt td tap s ,ire. aiss i ’d ti ( Fo1rt ran Iop.i I unit I. fhese tjes ire hi r i 1111 ( , )It Int i [Io

Understanding Automotive Exhaust Catalysts Using a Surface Science Approach: Model NOx Storage Materials

DOE Office of Scientific and Technical Information (OSTI.GOV)

Szanyi, Janos; Yi, Cheol-Woo W.; Mudiyanselage, Kumudu K.

2013-11-01

The structure-reactivity relationships of model BaO-based NOx storage/reduction catalysts were investigated under well controlled experimental conditions using surface science analysis techniques. The reactivity of BaO toward NO2, CO2, and H2O was studied as a function of BaO layer thickness [0\\hBaO\\30 monolayer (ML)], sample temperature, reactant partial pressure, and the nature of the substrate the NOx storage material was deposited onto. Most of the efforts focused on understanding the mechanism of NO2 storage either on pure BaO, or on BaO exposed to CO2 or H2O prior to NO2 exposure. The interaction of NO2 with a pure BaO film results in themore » initial formation of nitrite/nitrate ion pairs by a cooperative adsorption mechanism predicted by prior theoretical calculations. The nitrites are then further oxidized to nitrates to produce a fully nitrated surface. The mechanism of NO2 uptake on thin BaO films (\\4 ML), BaO clusters (\\1 ML) and mixed BaO/Al2O3 layers are fundamentally different: in these systems initially nitrites are formed only, and then converted to nitrates at longer NO2 exposure times. These results clarify the contradicting mechanisms presented in prior studies in the literature. After the formation of a nitrate layer the further conversion of the underlying BaO is slow, and strongly depends on both the sample temperature and the NO2 partial pressure. At 300 K sample temperature amorphous Ba(NO3)2 forms that then can be converted to crystalline nitrates at elevated temperatures. The reaction between BaO and H2O is facile, a series of Ba(OH)2 phases form under the temperature and H2O partial pressure regimes studied. Both amorphous and crystalline Ba(OH)2 phases react with NO2, and initially form nitrites only that can be converted to nitrates. The NO2 adsorption capacities of BaO and Ba(OH)2 are identical, i.e., both of these phases can completely be converted to Ba(NO3)2. In contrast, the interaction of CO2 with pure BaO results in the formation of a BaCO3 layer that prevents to complete carbonation of the entire BaO film under the experimental conditions applied in these studies. However, these ‘‘carbonated’’ BaO layers readily react with NO2, and at elevated sample temperature even the carbonate layer is converted to nitrates. The importance of the metal oxide/metal interface in the chemistry on NOx storage-reduction catalysts was studied on BaO(\\1 ML)/Pt(111) reverse model catalysts. In comparison to the clean Pt(111), new oxygen adsorption phases were identified on the BaO/Pt(111) surface that can be associated with oxygen atoms strongly adsorbed on Pt atoms at the peripheries of BaO particles. A simple kinetic model developed helped explain the observed thermal desorption results. The role of the oxide/metal interface in the reduction of Ba(NO3)2 was also substantiated in experiments where Ba(NO3)2/O/Pt(111) samples were exposed to CO at elevated sample temperature. The catalytic decomposition of the nitrate phase occurred as soon as metal sites opened up by the removal of interfacial oxygen via CO oxidation from the O/Pt(111) surface. The temperature for catalytic nitrate reduction was found to be significantly lower than the onset temperature of thermal nitrate decomposition. We gratefully acknowledge the US Department of Energy (DOE), Office of Science, Division of Chemical Sciences, Geosciences, and Biosciences for the support of this work. The research described in this paper was performed at the Environmental Molecular Sciences Laboratory (EMSL), a national user facility sponsored by the DOE Office of Biological and Environmental Research and located at the Pacific Northwest National Laboratory (PNNL). PNNL is operated for the US DOE by Battelle under contract number DE-AC05-76RL01830.« less

Influence of H2O on Liquidus Temperatures of Primitive Basalts and Olivine-Liquid Thermometry.

NASA Astrophysics Data System (ADS)

Medard, E.; Grove, T. L.

2005-12-01

We have undertaken a systematic experimental study aimed at understanding the effect of water on olivine liquidus temperatures of primitive basalts. Experiments have been performed on a primitive tholeiitic basalt from Medicine Lake Volcano, California (sample 82-72f, Bartels et al. 1991). The dry liquidus has been characterized from 0.1 MPa to 1.2 GPa. The wet liquidus has been constrained to within 15 °C using water-saturated experiments performed in a MHC externally heated pressure vessel. Preliminary results show that the olivine-liquidus depression (i.e., the difference between dry and water-bearing liquidus) is essentially a linear function of the water content of the melt: ΔT = 560  X(HO0.5), where X(HO0.5) is the mole fraction of water, calculated on a single-cation oxide basis. For 82-72f, this roughly translates into a 30 °C / wt% H2O depression. Simple systems (e.g., diopside/H2O, albite/H2O) suggest that melt structure / composition may have an influence on H2O liquidus depression, and this potential influence is currently under investigation. Experimental phase equilibria and thermobarometry of primitive basalts provide the primary evidence for estimating melting conditions and thermal structures in the Earth's mantle. Assessing the influence of H2O is critical, because it is the dominant volatile component involved in igneous processes, and it has been shown to cause a significant reduction in liquidus temperatures. However, recent model parameterizations vary from very large effects at low H2O contents (about 75 °C at 1 wt% H2O, Falloon and Danyushevsky 2000) to linear effect of H2O vs liquidus temperature (about 25 °C at 1 wt% H2O, Sugawara 2000). Our experimental determination more closely approximates the latter model. A key consequence is that the presence of small amounts of water in MORB magmas (< 1wt%) will only have a very small effect (< 30 °C) on liquidus temperature determination for mid-ocean-ridges. For magmas that are more water-rich, as observed in subduction zones, ocean island and continental magmatism, this parameterization of H2O liquidus depression can be included in existing thermodynamic models to retrieve magmatic temperatures from petrology of primitive basalts.

YKL071W from Saccharomyces cerevisiae encodes a novel aldehyde reductase for detoxification of glycolaldehyde and furfural derived from lignocellulose.

PubMed

Wang, Hanyu; Ouyang, Yidan; Zhou, Chang; Xiao, Difan; Guo, Yaping; Wu, Lan; Li, Xi; Gu, Yunfu; Xiang, Quanju; Zhao, Ke; Yu, Xiumei; Zou, Likou; Ma, Menggen

2017-12-01

Aldehydes generated as by-products during the pretreatment of lignocellulose are the key inhibitors to Saccharomyces cerevisiae, which is considered as the most promising microorganism for industrial production of biofuel, xylitol as well as other special chemicals from lignocellulose. S. cerevisiae has the inherent ability to in situ detoxify aldehydes to corresponding alcohols by multiple aldehyde reductases. Herein, we report that an uncharacterized open reading frame YKL071W from S. cerevisiae encodes a novel "classical" short-chain dehydrogenase/reductase (SDR) protein with NADH-dependent enzymatic activities for reduction of furfural (FF), glycolaldehyde (GA), formaldehyde (FA), and benzaldehyde (BZA). This enzyme showed much better specific activities for reduction of GA and FF than FA and BZA, and displayed much higher Km and Kcat/Km but lower Vmax and Kcat for reduction of GA than FF. For this enzyme, the optimum pH was 5.5 and 6.0 for reduction of GA and FF, and the optimum temperature was 30 °C for reduction of GA and FF. Both pH and temperature affected stability of this enzyme in a similar trend for reduction of GA and FF. Cu 2+ , Zn 2+ , Ni 2+ , and Fe 3+ had severe inhibition effects on enzyme activities of Ykl071wp for reduction of GA and FF. Transcription of YKL071W in S. cerevisiae was significantly upregulated under GA and FF stress conditions, and its transcription is most probably regulated by transcription factor genes of YAP1, CAD1, PDR3, and STB5. This research provides guidelines to identify more uncharacterized genes with reductase activities for detoxification of aldehydes derived from lignocellulose in S. cerevisiae.

Studies on the stripping of cerium from the loaded tbp-kerosene solution

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rizk, S.E.; Abdel Rahman, N.; Daoud, J.A.

2008-07-01

The reductive stripping of Ce(IV) from the loaded organic phase (30% TBP in kerosene) was investigated, using two stripping agents, EDTA and H{sub 2}O{sub 2}, in nitric acid. The results are compared to determine the optimum conditions for the reduction of Ce(IV) in the organic phase to Ce(III) in the aqueous phase. For each of the two stripping agents, the effect of different parameters affecting the reduction process was investigated: stripping-agent concentration, nitric acid concentration, phase ratio, shaking time, and temperature. The results are compared and discussed in terms of the conditions required for maximum reductive stripping of Ce(IV). (authors)

The effect of a comprehensive injury audit program on injury incidence in ballet: a 3-year prospective study.

PubMed

Allen, Nick; Nevill, Alan M; Brooks, John H M; Koutedakis, Yiannis; Wyon, Matthew A

2013-09-01

The aim of this study was to determine whether an intervention with individualized conditioning program based on injury history and functional movement screening would be effective in reducing ballet injury incidence. Prospective 3-year epidemiological study. Professional ballet company and its in-house medical facility. Dancers from a professional ballet company over the 3-year study period. Participant numbers ranged from 52 to 58 (year 1: 52; year 2: 58; year 3: 53). The intervention consisted of individual conditioning programs developed using injury history and functional movement screening. Analysis was undertaken of the all dancers who were present in the company during the study period. The significance of change in injuries over a 3-year period was determined using a Poisson distribution model. To determine whether individual conditioning programs resulted in a decrease in injury incidence over the study period. The injury count reduced significantly in years 2 and 3 (P < 0.001). Injury incidence for male dancers declined from year 1 (in year/1000 h) (4.76/1000 h) to year 2 (2.40/1000 h) and year 3 (2.22/1000 h). For women, a reduction in the injury incidence was observed from year 1 (4.14/1000 h) to year 2 (1.71/1000 h) and year 3 (1.81/1000 h). Through prospective injury surveillance, we were able to demonstrate the benefit of individualized conditioning programs based on injury history and functional movement screening in reducing injuries in ballet. The implementation of well-structured injury surveillance programs can impact on injury incidence through its influence on intervention programs.

Reductive atmospheric acid leaching of spent alkaline batteries in H2SO4/Na2SO3 solutions

NASA Astrophysics Data System (ADS)

Morcali, Mehmet Hakan

2015-07-01

This work studies the optimum reductive leaching process for manganese and zinc recovery from spent alkaline battery paste. The effects of reducing agents, acid concentration, pulp density, reaction temperature, and leaching time on the dissolution of manganese and zinc were investigated in detail. Manganese dissolution by reductive acidic media is an intermediate-controlled process with an activation energy of 12.28 kJ·mol-1. After being leached, manganese and zinc were selectively precipitated with sodium hydroxide. The zinc was entirely converted into zincate (Zn(OH){4/2-}) ions and thus did not co-precipitate with manganese hydroxide during this treatment (2.0 M NaOH, 90 min, 200 r/min, pH > 13). After the manganese was removed from the solution, the Zn(OH){4/2-} was precipitated as zinc sulfate in the presence of sulfuric acid. The results indicated that this process could be effective in recovering manganese and zinc from alkaline batteries.

Bactericidal active ingredient in cryopreserved plasma-treated water with the reduced-pH method for plasma disinfection

NASA Astrophysics Data System (ADS)

Kitano, Katsuhisa; Ikawa, Satoshi; Nakashima, Yoichi; Tani, Atsushi; Yokoyama, Takashi; Ohshima, Tomoko

2016-09-01

For the plasma disinfection of human body, plasma sterilization in liquid is crucial. We found that the plasma-treated water (PTW) has strong bactericidal activity under low pH condition. Physicochemical properties of PTW is discussed based on chemical kinetics. Lower temperature brings longer half-life and the bactericidal activity of PTW can be kept by cryopreservation. High performance PTW, corresponding to the disinfection power of 22 log reduction (B. subtilis spore), can be obtained by special plasma system equipped with cooling device. This is equivalent to 65% H2O2, 14% sodium hypochlorite and 0.33% peracetic acid, which are deadly poison for human. But, it is deactivated soon at higher temperature (4 sec. at body temperature), and toxicity to human body seems low. For dental application, PTW was effective on infected models of human extracted tooth. Although PTW has many chemical components, respective chemical components in PTW were isolated by ion chromatography. In addition to peaks of H2O2, NO2- and NO3-, a specific peak was detected. and only this fraction had bactericidal activity. Purified active ingredient of PTW is the precursor of HOO, and further details will be discussed in the presentation. MEXT (15H03583, 23340176, 25108505). NCCE (23-A-15).

Recombination reduction at the c-Si/RCA oxide interface through Ar-H2 plasma treatment

NASA Astrophysics Data System (ADS)

Landheer, Kees; Bronsveld, Paula C. P.; Poulios, Ioannis; Tichelaar, Frans D.; Kaiser, Monja; Schropp, Ruud E. I.; Rath, Jatin K.

2017-02-01

An Ar-H2 plasma treatment was applied on an ultrathin RCA oxide to create well-passivated silicon wafers with symmetric c-Si/SiOx:H/a-Si:H passivation layer stacks. The effective lifetime of these samples increased from 10 μs to 4 ms after annealing at 200 °C through Ar-H2 plasma treatment of the oxide. The results indicate that the plasma treatment can modify the RCA oxide and this enables atomic hydrogen diffusion at low annealing temperature, leading to a well passivated c-Si/SiOx:H interface. This might provide new possibilities to use wet chemical oxides in c-Si solar cells, for example as tunnel contacts.

Oscillations and patterns in a model of simultaneous CO and C2H2 oxidation and NO(x) reduction in a cross-flow reactor.

PubMed

Hadač, Otto; Kohout, Martin; Havlica, Jaromír; Schreiber, Igor

2015-03-07

A model describing simultaneous catalytic oxidation of CO and C2H2 and reduction of NOx in a cross-flow tubular reactor is explored with the aim of relating spatiotemporal patterns to specific pathways in the mechanism. For that purpose, a detailed mechanism proposed for three-way catalytic converters is split into two subsystems, (i) simultaneous oxidation of CO and C2H2, and (ii) oxidation of CO combined with NOx reduction. The ability of these two subsystems to display mechanism-specific dynamical effects is studied initially by neglecting transport phenomena and applying stoichiometric network and bifurcation analyses. We obtain inlet temperature - inlet oxygen concentration bifurcation diagrams, where each region possessing specific dynamics - oscillatory, bistable and excitable - is associated with a dominant reaction pathway. Next, the spatiotemporal behaviour due to reaction kinetics combined with transport processes is studied. The observed spatiotemporal patterns include phase waves, travelling fronts, pulse waves and spatiotemporal chaos. Although these types of pattern occur generally when the kinetic scheme possesses autocatalysis, we find that some of their properties depend on the underlying dominant reaction pathway. The relation of patterns to specific reaction pathways is discussed.

Polycyclic Aromatic Hydrocarbon Ionization Energy Lowering in Water Ices

NASA Technical Reports Server (NTRS)

Gudipati, Murthy S.; Allamandola, Louis J.

2004-01-01

In studying various interstellar and solar system ice analogs, we have recently found that upon vacuum ultraviolet photolysis, polycyclic aromatic hydrocarbons (PAHs) frozen in water ice at low temperatures are easily ionized and indefinitely stabilized as trapped ions (Gudipati; Gudipati & Allamandola). Here we report the first experimental study that shows that PAH ionization energy is significantly lowered in PAH/H2O ices, in agreement with recent theoretical work (Woon & Park). The ionization energy (IE) of the PAH studied here, quaterrylene (C40H20, IE = 6.11 eV), is lowered by up to 2.11 eV in water ice. PAH ionization energy reduction in low-temperature water ice substantially expands the astronomical regions in which trapped ions and electrons may be important. This reduction in ionization energy should also hold for other types of trapped species in waterrich interstellar, circumstellar, and solar system ices. Subject headings: ISM: clouds - methods: laboratory - molecular processes - radiation mechanisms: nonthermal -ultraviolet: ISM - ultraviolet: solar system

Effects of Ti-Based Additives on the Hydrogen Storage Properties of a L i B H 4 / C a H 2 Destabilized System

DOE PAGES

Yang, Hongwei; Ibikunle, Adeola; Goudy, Andrew J.

2010-01-01

Tmore » he hydrogen storage properties of a destabilized LiBH 4 / CaH 2 system ball-milled with iCl 3 , iF 3 , and iO 2 additives have been investigated. It is found that the system with iCl 3 additive has a lower dehydrogenation temperature than the ones with other additives. Further study shows that a higher amount of iCl 3 is more effective in reducing the desorption temperature of the LiBH 4 / CaH 2 system, since it leads to a lower activation energy of dehydrogenation. he activations energies for mixtures containing 4, 10, and 25 mol% of iCl 3 are 141, 126, and 110 kJ/mol, respectively. However, the benefits of higher amounts of iCl 3 are offset by a larger reduction in hydrogen capacity of the mixtures.« less

Temperature and pH effects on feeding and growth of Antarctic krill

NASA Astrophysics Data System (ADS)

Saba, G.; Bockus, A.; Fantasia, R. L.; Shaw, C.; Sugla, M.; Seibel, B.

2016-02-01

Rapid warming in the Western Antarctic Peninsula (WAP) region is occurring, and is associated with an overall decline in primary, secondary, and higher trophic levels, including Antarctic krill (Euphausia superba), a key species in Antarctic food webs. Additionally, there are predictions that by the end of this century the Southern Ocean will be one of the first regions to be affected by seawater chemistry changes associated with enhanced CO2. Ocean acidification and warming may act synergistically to impair animal performance, which may negatively impact Antarctic krill. We assessed the effects of temperature (ambient temperature, ambient +3 degrees C) and pH (Experiment 1 = 8.0, 7.7; Experiment 2 = 8.0, 7.5, 7.1) on juvenile Antarctic krill feeding and growth (growth increment and intermolt period) during incubation experiments at Palmer Station, Antarctica. Food intake was lower in krill exposed to reduced pH. Krill intermolt period (IMP) was significantly lower in the elevated temperature treatments (16.9 days) compared to those at 0 degrees (22.8 days). Within the elevated temperature treatment, minor increases in IMP occurred in krill exposed reduced pH. Growth increment (GI) was lower with decreased pH at the first molt, and this was exacerbated at elevated temperature. However, differences in GI were eliminated between the first and second molts suggesting potential ability of Antarctic krill to acclimate to changes in temperature and pH. Reductions in juvenile krill growth and feeding under elevated temperature and reduced pH are likely caused by higher demands for internal acid-base regulation or a metabolic suppression. However, the subtlety of these feeding and growth responses leaves an open question as to how krill populations will tolerate prolonged future climate change in the Antarctic.

CO-Bridged H-Cluster Intermediates in the Catalytic Mechanism of [FeFe]-Hydrogenase CaI.

PubMed

Ratzloff, Michael W; Artz, Jacob H; Mulder, David W; Collins, Reuben T; Furtak, Thomas E; King, Paul W

2018-06-20

The [FeFe]-hydrogenases ([FeFe] H 2 ases) catalyze reversible H 2 activation at the H-cluster, which is composed of a [4Fe-4S] H subsite linked by a cysteine thiolate to a bridged, organometallic [2Fe-2S] ([2Fe] H ) subsite. Profoundly different geometric models of the H-cluster redox states that orchestrate the electron/proton transfer steps of H 2 bond activation have been proposed. We have examined this question in the [FeFe] H 2 ase I from Clostridium acetobutylicum (CaI) by Fourier-transform infrared (FTIR) spectroscopy with temperature annealing and H/D isotope exchange to identify the relevant redox states and define catalytic transitions. One-electron reduction of H ox led to formation of H red H + ([4Fe-4S] H 2+ -Fe I -Fe I ) and H red ' ([4Fe-4S] H 1+ -Fe II -Fe I ), with both states characterized by low frequency μ-CO IR modes consistent with a fully bridged [2Fe] H . Similar μ-CO IR modes were also identified for H red H + of the [FeFe] H 2 ase from Chlamydomonas reinhardtii (CrHydA1). The CaI proton-transfer variant C298S showed enrichment of an H/D isotope-sensitive μ-CO mode, a component of the hydride bound H-cluster IR signal, H hyd . Equilibrating CaI with increasing amounts of NaDT, and probed at cryogenic temperatures, showed H red H + was converted to H hyd . Over an increasing temperature range from 10 to 260 K catalytic turnover led to loss of H hyd and appearance of H ox , consistent with enzymatic turnover and H 2 formation. The results show for CaI that the μ-CO of [2Fe] H remains bridging for all of the "H red " states and that H red H + is on pathway to H hyd and H 2 evolution in the catalytic mechanism. These results provide a blueprint for designing small molecule catalytic analogs.

Hydrogen retention in Li and Li-C-O films

NASA Astrophysics Data System (ADS)

Buzi, Luxherta; Nelson, Andrew O.; Yang, Yuxin; Kaita, Robert; Koel, Bruce E.

2017-10-01

The efficiency of Li in binding H isotopes has led to reduced recycling in magnetic fusion devices and improved plasma performance. Since elemental Li surfaces are challenging to maintain in fusion devices due to the presence of impurities, parameterizing and understanding the mechanisms for H retention in various Li compounds (Li-C-O), in addition to pure Li, is crucial for Li plasma-facing material applications. To determine H retention in Li and Li-C-O films, measurements were done under ultrahigh vacuum conditions using temperature programmed desorption (TPD). Thin Li films (20 monolayers) were deposited on a nickel single crystal substrate and irradiated with 500 eV H2+ions at surface temperatures from 90K to 520K. Initial measurements on Li and Li-O films showed that the retention was comparable and dropped exponentially with surface temperature, from 95% at 90 K to 35% at 520 K. Auger electron spectroscopy and TPD showed that H was retained as lithium hydride (LiH) in pure Li and as lithium hydroxide (LiOH) in Li2O, which decomposed to H2O and Li2O at temperatures higher than 470K. H retention in Li-C and Li-C-O films will be determined over a similar temperature range, and the sputtering rate of these layers with H ions will also be reported. This material is based upon work supported by the U.S. Department of Energy, Office of Science/Fusion Energy Sciences under Award Number DE-SC0012890.

Low-temperature electronic transport in single K(0.27)MnO(2)·0.5H(2)O nanowires: enhanced electron-electron interaction.

PubMed

Long, Y Z; Yin, Z H; Chen, Z J; Jin, A Z; Gu, C Z; Zhang, H T; Chen, X H

2008-05-28

The current-voltage (I-V) characteristics and electrical resistivity of isolated potassium manganese oxide (K(0.27)MnO(2)·0.5H(2)O) nanowires prepared by a simple hydrothermal method were investigated over a wide temperature range from 300 to 4 K. With lowering temperature, a transition from linear to nonlinear I-V curves was observed around 50 K, and a clear zero bias anomaly (i.e., Coulomb gap-like structure) appeared on the differential conductance (dI/dV) curves, possibly due to enhanced electron-electron interaction at low temperatures. The temperature dependence of resistivity, [Formula: see text], follows the Efros-Shklovskii (ES) law, as expected in the presence of a Coulomb gap. Here we note that both the ES law and Coulomb blockade can in principle lead to a reduced zero bias conductance at low temperatures; in this study we cannot exclude the possibility of Coulomb-blockade transport in the measured nanowires, especially in the low-temperature range. It is still an open question how to pin down the origin of the observed reduction to a Coulomb gap (ES law) or Coulomb blockade.

CO-Bridged H-Cluster Intermediates in the Catalytic Mechanism of [FeFe]-Hydrogenase CaI

DOE PAGES

Ratzloff, Michael W.; Artz, Jacob H.; Mulder, David W.; ...

2018-05-23

The [FeFe]-hydrogenases ([FeFe] H 2ases) catalyze reversible H 2 activation at the H-cluster, which is composed of a [4Fe-4S] H subsite linked by a cysteine thiolate to a bridged, organometallic [2Fe-2S] ([2Fe] H) subsite. Profoundly different geometric models of the H-cluster redox states that orchestrate the electron/proton transfer steps of H 2 bond activation have been proposed. We have examined this question in the [FeFe] H 2ase I from Clostridium acetobutylicum (CaI) by Fourier-transform infrared (FTIR) spectroscopy with temperature annealing and H/D isotope exchange to identify the relevant redox states and define catalytic transitions. One-electron reduction of H ox ledmore » to formation of H redH + ([4Fe-4S] H 2+-Fe I-Fe I) and H red' ([4Fe-4S] H 1+-Fe II-Fe I), with both states characterized by low frequency μ-CO IR modes consistent with a fully bridged [2Fe] H. Similar μ-CO IR modes were also identified for H redH + of the [FeFe] H 2ase from Chlamydomonas reinhardtii (CrHydA1). The CaI proton-transfer variant C298S showed enrichment of an H/D isotope-sensitive μ-CO mode, a component of the hydride bound H-cluster IR signal, H hyd. Equilibrating CaI with increasing amounts of NaDT, and probed at cryogenic temperatures, showed H redH + was converted to H hyd. Over an increasing temperature range from 10 to 260 K catalytic turnover led to loss of Hhyd and appearance of H ox, consistent with enzymatic turnover and H 2 formation. The results show for CaI that the μ-CO of [2Fe] H remains bridging for all of the 'H red' states and that H redH + is on pathway to H hyd and H 2 evolution in the catalytic mechanism. Here, this provides a blueprint for designing small molecule catalytic analogs« less

CO-Bridged H-Cluster Intermediates in the Catalytic Mechanism of [FeFe]-Hydrogenase CaI

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ratzloff, Michael W.; Artz, Jacob H.; Mulder, David W.

The [FeFe]-hydrogenases ([FeFe] H 2ases) catalyze reversible H 2 activation at the H-cluster, which is composed of a [4Fe-4S] H subsite linked by a cysteine thiolate to a bridged, organometallic [2Fe-2S] ([2Fe] H) subsite. Profoundly different geometric models of the H-cluster redox states that orchestrate the electron/proton transfer steps of H 2 bond activation have been proposed. We have examined this question in the [FeFe] H 2ase I from Clostridium acetobutylicum (CaI) by Fourier-transform infrared (FTIR) spectroscopy with temperature annealing and H/D isotope exchange to identify the relevant redox states and define catalytic transitions. One-electron reduction of H ox ledmore » to formation of H redH + ([4Fe-4S] H 2+-Fe I-Fe I) and H red' ([4Fe-4S] H 1+-Fe II-Fe I), with both states characterized by low frequency μ-CO IR modes consistent with a fully bridged [2Fe] H. Similar μ-CO IR modes were also identified for H redH + of the [FeFe] H 2ase from Chlamydomonas reinhardtii (CrHydA1). The CaI proton-transfer variant C298S showed enrichment of an H/D isotope-sensitive μ-CO mode, a component of the hydride bound H-cluster IR signal, H hyd. Equilibrating CaI with increasing amounts of NaDT, and probed at cryogenic temperatures, showed H redH + was converted to H hyd. Over an increasing temperature range from 10 to 260 K catalytic turnover led to loss of Hhyd and appearance of H ox, consistent with enzymatic turnover and H 2 formation. The results show for CaI that the μ-CO of [2Fe] H remains bridging for all of the 'H red' states and that H redH + is on pathway to H hyd and H 2 evolution in the catalytic mechanism. Here, this provides a blueprint for designing small molecule catalytic analogs« less

Facile Reductive Silylation of UO22+ to Uranium(IV) Chloride.

PubMed

Kiernicki, John J; Zeller, Matthias; Bart, Suzanne C

2017-01-19

General reductive silylation of the UO 2 2+ cation occurs readily in a one-pot, two-step stoichiometric reaction at room temperature to form uranium(IV) siloxides. Addition of two equivalents of an alkylating reagent to UO 2 X 2 (L) 2 (X=Cl, Br, I, OTf; L=triphenylphosphine oxide, 2,2'-bipyridyl) followed by two equivalents of a silyl (pseudo)halide, R 3 Si-X (R=aryl, alkyl, H; X=Cl, Br, I, OTf, SPh), cleanly affords (R 3 SiO) 2 UX 2 (L) 2 in high yields. Support is included for the key step in the process, reduction of U VI to U V . This procedure is applicable to a wide range of commercially available uranyl salts, silyl halides, and alkylating reagents. Under this protocol, one equivalent of SiCl 4 or two equivalents of Me 2 SiCl 2 results in direct conversion of the uranyl to uranium(IV) tetrachloride. Full spectroscopic and structural characterization of the siloxide products is reported. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

SO2-tolerant and H2O-promoting Pt/C catalysts for efficient NO removal via fixed-bed H2-SCR.

PubMed

Tu, Baosheng; Shi, Nian; Sun, Wei; Cao, Limei; Yang, Ji

2017-01-01

In this paper, Pt supports on carbon black powder (Vulcan XC-72) were synthesized via a hydrothermal method for selective catalytic reduction (SCR) of NO with H 2 in the presence of 2 vol% O 2 over a wide temperature of 20-300 °C. The results showed that the 3 and 5 wt% Pt/C catalysts resulted in high NO conversion (>90 %) over a temperature range of 120 to 300 °C, and the maximum NO conversion of 98.6 % was achieved over 5 wt% Pt/C at 120 °C. Meanwhile, the influence of SO 2 and H 2 O on the catalyst performance of 3 wt% Pt/C was investigated. The catalysts exhibited good SO 2 poisoning resistance when the SO 2 concentration was lower than 260 ppm. Moreover, a positive effect on NO conversion was detected with the addition of 3 and 5 vol% H 2 O in the feed gas stream. Graphical abstract TEM image and good NO conversion performance of the Pt/C catalysts.

Highly-basic large-pore zeolite catalysts for NOx reduction at low temperatures

DOEpatents

Penetrante, Bernardino M.; Brusasco, Raymond M.; Merritt, Bernard T.; Vogtlin, George E.

2004-02-03

A high-surface-area (greater than 600 m2/g), large-pore (pore size diameter greater than 6.5 angstroms), basic zeolite having a structure such as an alkali metal cation-exchanged Y-zeolite is employed to convert NO.sub.x contained in an oxygen-rich engine exhaust to N.sub.2 and O.sub.2. Preferably, the invention relates to a two-stage method and apparatus for NO.sub.x reduction in an oxygen-rich engine exhaust such as diesel engine exhaust that includes a plasma oxidative stage and a selective reduction stage. The first stage employs a non-thermal plasma treatment of NO.sub.x gases in an oxygen-rich exhaust and is intended to convert NO to NO.sub.2 in the presence of O.sub.2 and added hydrocarbons. The second stage employs a lean-NO.sub.x catalyst including the basic zeolite at relatively low temperatures to convert such NO.sub.2 to environmentally benign gases that include N.sub.2, CO.sub.2, and H.sub.2 O.

Study on the reduction of atmospheric mercury emissions from mine waste enriched soils through native grass cover in the Mt. Amiata region of Italy.

PubMed

Fantozzi, L; Ferrara, R; Dini, F; Tamburello, L; Pirrone, N; Sprovieri, F

2013-08-01

Atmospheric mercury emissions from mine-waste enriched soils were measured in order to compare the mercury fluxes of bare soils with those from other soils covered by native grasses. Our research was conducted near Mt. Amiata in central Italy, an area that was one of the largest and most productive mining centers in Europe up into the 1980s. To determine in situ mercury emissions, we used a Plexiglas flux chamber connected to a portable mercury analyzer (Lumex RA-915+). This allowed us to detect, in real time, the mercury vapor in the air, and to correlate this with the meteorological parameters that we examined (solar radiation, soil temperature, and humidity). The highest mercury flux values (8000ngm(-2)h(-1)) were observed on bare soils during the hours of maximum insulation, while lower values (250ngm(-2)h(-1)) were observed on soils covered by native grasses. Our results indicate that two main environmental variables affect mercury emission: solar radiation intensity and soil temperature. The presence of native vegetation, which can shield soil surfaces from incident light, reduced mercury emissions, a result that we attribute to a drop in the efficiency of mercury photoreduction processes rather than to decreases in soil temperature. This finding is consistent with decreases in mercury flux values down to 3500ngm(-2)h(-1), which occurred under cloudy conditions despite high soil temperatures. Moreover, when the soil temperature was 28°C and the vegetation was removed from the experimental site, mercury emissions increased almost four-fold. This increase occurred almost immediately after the grasses were cut, and was approximately eight-fold after 20h. Thus, this study demonstrates that enhancing wild vegetation cover could be an inexpensive and effective approach in fostering a natural, self-renewing reduction of mercury emissions from mercury-contaminated soils. Copyright © 2013 Elsevier Inc. All rights reserved.

Partitioning Effects during Terminal Carbon and Electron Flow in Sediments of a Low-Salinity Meltwater Pond near Bratina Island, McMurdo Ice Shelf, Antarctica

PubMed Central

Mountfort, Douglas O.; Kaspar, Heinrich F.; Downes, Malcolm; Asher, Rodney A.

1999-01-01

A study of anaerobic sediments below cyanobacterial mats of a low-salinity meltwater pond called Orange Pond on the McMurdo Ice Shelf at temperatures simulating those in the summer season (<5°C) revealed that both sulfate reduction and methane production were important terminal anaerobic processes. Addition of [2-14C]acetate to sediment samples resulted in the passage of label mainly to CO2. Acetate addition (0 to 27 mM) had little effect on methanogenesis (a 1.1-fold increase), and while the rate of acetate dissimilation was greater than the rate of methane production (6.4 nmol cm−3 h−1 compared to 2.5 to 6 nmol cm−3 h−1), the portion of methane production attributed to acetate cleavage was <2%. Substantial increases in the methane production rate were observed with H2 (2.4-fold), and H2 uptake was totally accounted for by methane production under physiological conditions. Formate also stimulated methane production (twofold), presumably through H2 release mediated through hydrogen lyase. Addition of sulfate up to 50-fold the natural levels in the sediment (interstitial concentration, ∼0.3 mM) did not substantially inhibit methanogenesis, but the process was inhibited by 50-fold chloride (36 mM). No net rate of methane oxidation was observed when sediments were incubated anaerobically, and denitrification rates were substantially lower than rates for sulfate reduction and methanogenesis. The results indicate that carbon flow from acetate is coupled mainly to sulfate reduction and that methane is largely generated from H2 and CO2 where chloride, but not sulfate, has a modulating role. Rates of methanogenesis at in situ temperatures were four- to fivefold less than maximal rates found at 20°C. PMID:10584008

Preparation of metal/zeolite catalysts: Formation of palladium aquocomplexes in the precursor of palladium-mordenite catalysts

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

1993-09-01

Previous research has revealed that the catalytic performance of metal/zeolite catalysts can be significantly modified by exposing the catalyst precursor to H[sub 2]O vapor during the period after calcination, but before reduction. For bimetallic PdCo/NaY catalysts used for CO hydrogenation, the selectivity was changed from predominant production of oxygenates to predominant production of higher hydrocarbons. For Pt/H-mordenite catalysts, this water treatment has been reported to improve the alkane isomerization activity. Although it is certain that Lewis sites are transformed to Bronsted sites by reaction with H[sub 2]O, the activity of the catalyst is affected most when the water is addedmore » after calcination, when the noble metal is present as ligand-free ions. This observation led to the hypothesis that complexation of transition metal ions with water might be instrumental for the observed effects. In zeolites containing cages, such as Y, the formation of metal-ligand complex ions appears to incite their migration from small to large cages. In cageless zeolites such as mordenite, however, it is not clear, a priori, whether hydration of transition metal ions will increase or decrease their reducibility and whether it will ultimately result in higher or lower metal dispersion. The authors have therefore undertaken research to clarify these issues. Palladium supported in H-mordenite (Pd/HMor) or Na-mordenite (Pd/Na-Mor) has been tested using methylcyclopentane as a probe reaction; temperature-programmed reduction (TPR), desorption (TPD), and extended X-ray absorption fine structure (EXAFS) spectroscopy have been used to characterize the effects of water treatment on the samples.« less

Experimentally Determined Binding Energies of Astrophysically Relevant Hydrocarbons in Pure and H2O-Layered Ices

NASA Astrophysics Data System (ADS)

Behmard, Aida; Graninger, Dawn; Fayolle, Edith; Oberg, Karin I.

2017-01-01

Small hydrocarbons represent an important organic reservoir in a variety of interstellar environments. Constraints on desorption temperatures and binding energies of hydrocarbons are thus necessary for accurate predictions of where and in which phase these molecules exist. Through a series of temperature programmed desorption experiments, we determined binding energies of 1, 2, and 3-carbon interstellar hydrocarbons (CH4, C2H2, C2H4, C2H6, C3H4, C3H6, and C3H8) in pure ices and in relation to water ice, the dominant ice constituent during star and planet formation. These empirically determined values can be used to inform observations and models of the molecular spatial distribution in protoplanetary disks, thus providing insight into planetesimal composition. In addition, knowledge of hydrocarbon binding energies will refine simulations of grain surface chemistry, allowing for better predictions of the chemical conditions that lead to the production of complex organic molecules vital for life.

Red soil as a regenerable sorbent for high temperature removal of hydrogen sulfide from coal gas.

PubMed

Ko, Tzu-Hsing; Chu, Hsin; Lin, Hsiao-Ping; Peng, Ching-Yu

2006-08-25

In this study, hydrogen sulfide (H(2)S) was removed from coal gas by red soil under high temperature in a fixed-bed reactor. Red soil powders were collected from the northern, center and southern of Taiwan. They were characterized by XRPD, porosity analysis and DCB chemical analysis. Results show that the greater sulfur content of LP red soils is attributed to the higher free iron oxides and suitable sulfidation temperature is around 773K. High temperature has a negative effect for use red soil as a desulfurization sorbent due to thermodynamic limitation in a reduction atmosphere. During 10 cycles of regeneration, after the first cycle the red soil remained stable with a breakthrough time between 31 and 36 min. Hydrogen adversely affects sulfidation reaction, whereas CO exhibits a positive effect due to a water-shift reaction. COS was formed during the sulfidation stage and this was attributed to the reaction of H(2)S and CO. Results of XRPD indicated that, hematite is the dominant active species in fresh red soil and iron sulfide (FeS) is a product of the reaction between hematite and hydrogen sulfide in red soils. The spinel phase FeAl(2)O(4) was found during regeneration, moreover, the amount of free iron oxides decreased after regeneration indicating the some of the free iron oxide formed a spinel phase, further reducting the overall desulfurization efficiency.

Efficacy of a Community-Based Physical Activity Program KM2H2 for Stroke and Heart Attack Prevention among Senior Hypertensive Patients: A Cluster Randomized Controlled Phase-II Trial.

PubMed

Gong, Jie; Chen, Xinguang; Li, Sijian

2015-01-01

To evaluate the efficacy of the program Keep Moving toward Healthy Heart and Healthy Brain (KM2H2) in encouraging physical activities for the prevention of heart attack and stroke among hypertensive patients enrolled in the Community-Based Hypertension Control Program (CBHCP). Cluster randomized controlled trial with three waves of longitudinal assessments at baseline, 3 and 6 months post intervention. Community-based and patient-centered self-care for behavioral intervention in urban settings of China. A total of 450 participants diagnosed with hypertension from 12 community health centers in Wuhan, China were recruited, and were randomly assigned by center to receive either KM2H2 plus standard CBHCP care (6 centers and 232 patients) or the standard care only (6 centers and 218 patients). KM2H2 is a behavioral intervention guided by the Transtheoretical Model, the Model of Personalized Medicine and Social Capital Theory. It consists of six intervention sessions and two booster sessions engineered in a progressive manner. The purpose is to motivate and maintain physical activities for the prevention of heart attack and stroke. Heart attack and stroke (clinically diagnosed, primary outcome), blood pressure (measured, secondary outcome), and physical activity (self-report, tertiary outcome) were assessed at the individual level during the baseline, 3- and 6-month post-intervention. Relative to the standard care, receiving KM2H2 was associated with significant reductions in the incidence of heart attack (3.60% vs. 7.03%, p < .05) and stroke (5.11% vs. 9.90%, p<0.05), and moderate reduction in blood pressure (-3.72 mmHg in DBP and -2.92 mmHg in DBP) at 6-month post-intervention; and significant increases in physical activity at 3- (d = 0.53, 95% CI: 0.21, 0.85) and 6-month (d = 0.45, 95% CI: 0.04, 0.85) post-intervention, respectively. The program KM2H2 is efficacious to reduce the risk of heart attack and stroke among senior patients who are on anti-hypertensive medication. Findings of this study provide solid data supporting a formal phase-III trial to establish the effectiveness of KM2H2 for use in community settings for prevention. ISRCTN Register ISRCTN12608966.

Hollow ZSM-5 encapsulated Pt nanoparticles for selective catalytic reduction of NO by hydrogen

NASA Astrophysics Data System (ADS)

Hong, Zhe; Wang, Zhong; Chen, Dan; Sun, Qiang; Li, Xuebing

2018-05-01

Pt nanoparticles were successfully encapsulated in hollow ZSM-5 single crystals by tetrapropylammonium hydroxide (TPAOH) hydrothermal treatment with an "dissolution-recrystallization" process. The prepared Pt/hollow ZSM-5 (Pt/h-ZSM-5re) sample exhibited the best activity and a maximum NO conversion of 84% can be achieved at 90 °C with N2 selectivity of 92% (GHSV = 50,000 h-1). Meanwhile, Pt/h-ZSM-5re catalyst exhibited excellent SO2, H2O resistance and durability, which was related to the stabilization of Pt active sites by hollow structure during H2-SCR. It was found that the increase of NO2 concentration in the feed gas mixture led to an activity decline. In addition, the H2-SCR reaction routes over Pt/hollow ZSM-5 catalyst at different temperature were investigated.

Effect of H2O on the NO emission characteristics of pulverized coal during oxy-fuel combustion.

PubMed

Lei, Ming; Sun, Cen; Zou, Chan; Mi, Hang; Wang, Chunbo

2018-04-01

The NO emission characteristics of Datong bituminous coal and Yangquan anthracite in O 2 /H 2 O/CO 2 atmospheres were investigated by using a fixed-bed reactor system, and the emission characteristics were compared with the experimental results from O 2 /N 2 and O 2 /CO 2 atmospheres, especially at low O 2 concentrations and high temperatures. The results showed that NO emissions of pulverized coal in O 2 /CO 2 environments were less than those in the O 2 /N 2 environments, regardless of the O 2 concentration and the furnace temperature. Adding H 2 O decreased the possibility of reactions between the reductive groups (NH) and the oxygen radical during devolatilization, which led to a decrease in NO emissions at 1000 °C. However, as the furnace temperature increased, "additional" nitrogen precursors (HCN and NH 3 ) generated by enhanced char-H 2 O gasification were quickly oxidized to generate a large amount of NO during char oxidation that exceeded the amount of NO reduced by NH during devolatilization. Thus, the NO emissions in O 2 /CO 2 /H 2 O atmosphere were higher than those in O 2 /CO 2 atmosphere at a low O 2 concentration. However, as the O 2 concentration increased, the NO emissions in O 2 /CO 2 /H 2 O atmosphere became lower than those in O 2 /CO 2 atmosphere because the effect of H 2 O gasification became weaker. The NO emissions of Yangquan anthracite (YQ) were higher than those of DT, but the changing trend of YQ was similar to that of DT.

Numerical Study of Pressure Influence on Methane-Oxygen Laminar Counterflow Diffusion Flames

NASA Astrophysics Data System (ADS)

Iino, Kimio; Akamatsu, Fumiteru; Katsuki, Masashi

We carried out numerical studies on methane/oxygen diffusion flames of counter-flow configuration to elucidate the influence of pressure on flame structure, heat release rate and reaction mechanisms. The chemistry in gas-phase was based on GRI-Mech 3.0 database. The thickness of diffusion flame became thinner with increasing strain rate a , with its characteristic flame thickness varying inversely with √a, especially its relation became significant with increasing pressure. Flame temperature increased with increasing pressure. Enhanced H2O production reactions, especially chain terminal reactions for H2O production, were found to be important in determining the flame temperature at high pressures. The small reduction in the flame temperature with increasing strain rate at high pressures, compared to the atmospheric pressure, is caused by the capacitor effect of product dissociation. From QRPDs, the third body dependent reactions were enhanced in high pressure conditions, hence C2 pathway was enhanced.

One-step gas-solid reaction synthesis of W@WS2 nanorattles and their novel catalytic activity.

PubMed

Wen, Yan; Zhang, Haijun; Zhang, Shaowei

2014-11-07

W@WS2 nanorattles were synthesised by heating a mixture of WO3 nanoparticles and S at a relatively low temperature between 750 and 950 °C in H2/Ar. In addition to the temperature, the competition between the H2 reduction and the S sulphidation sub-reactions dominated the reaction mechanisms and the morphologies of final products. Based on this, several types of nanostructures, including WS2 nanoflakes, inorganic fullerene-like nanoparticles and W@WS2 nanorattles (with desirable core size and shell thickness), could be selectively prepared by simply tailoring the processing parameters. Moreover, it was found for the first time that as-prepared W@WS2 nanorattles exhibited excellent catalytic activities which were close to or even better than their much more costive Au-based counterparts.

One-step gas-solid reaction synthesis of W@WS2 nanorattles and their novel catalytic activity

NASA Astrophysics Data System (ADS)

Wen, Yan; Zhang, Haijun; Zhang, Shaowei

2014-10-01

W@WS2 nanorattles were synthesised by heating a mixture of WO3 nanoparticles and S at a relatively low temperature between 750 and 950 °C in H2/Ar. In addition to the temperature, the competition between the H2 reduction and the S sulphidation sub-reactions dominated the reaction mechanisms and the morphologies of final products. Based on this, several types of nanostructures, including WS2 nanoflakes, inorganic fullerene-like nanoparticles and W@WS2 nanorattles (with desirable core size and shell thickness), could be selectively prepared by simply tailoring the processing parameters. Moreover, it was found for the first time that as-prepared W@WS2 nanorattles exhibited excellent catalytic activities which were close to or even better than their much more costive Au-based counterparts.

Raman Spectroscopy and Microphysics of Single PSC Precursor Particles Suspended in a Quadrupole Trap

NASA Astrophysics Data System (ADS)

Sonnenfroh, D. M.; Hunter, A. J.; Rawlins, W. T.

2001-12-01

Polar stratospheric clouds (PSCs) consist primarily of solid nitric acid trihydrate (NAT) particles, which are thought to nucleate via HNO3 uptake on background sulfuric acid particles at temperatures below 195 K. The mechanism for this process is uncertain, and depends on whether the sulfuric acid particles are solid or liquid at these temperatures. Previous results from laboratory and field measurements are mixed; our previous single-particle laboratory experiments showed that binary H2SO4/H2O particles at stratospheric compositions are essentially metastable in the liquid phase when cooled to PSC temperatures. Currently, we are investigating the detailed microphysics of binary (H2SO4/H2O) and ternary (HNO3/H2SO4/H2O) single particles suspended in an electrodynamic levitator, using optical elastic scattering and Raman spectroscopy to observe changes in phase and composition. Single-particle Raman spectra for supercooled binary particles exhibit spectral distributions which alter markedly with decreasing temperature down to 190 K. The variations signify increasing dissociation of HSO4(-) to SO4(-2) with decreasing temperature, consistent with measurements for bulk solutions. Upon gradual warming of supercooled liquid binary particles, some of them freeze briefly in a narrow "window" of the phase diagram, near 210 K and 60 weight per cent H2SO4. We will discuss the Raman spectroscopy and microphysical behavior of the liquid and frozen particles for both the binary and ternary systems. This research was supported by the NASA Atmospheric Effects of Aviation Program.

Sulfur and oxygen isotope insights into sulfur cycling in shallow-sea hydrothermal vents, Milos, Greece

PubMed Central

2014-01-01

Shallow-sea (5 m depth) hydrothermal venting off Milos Island provides an ideal opportunity to target transitions between igneous abiogenic sulfide inputs and biogenic sulfide production during microbial sulfate reduction. Seafloor vent features include large (>1 m2) white patches containing hydrothermal minerals (elemental sulfur and orange/yellow patches of arsenic-sulfides) and cells of sulfur oxidizing and reducing microorganisms. Sulfide-sensitive film deployed in the vent and non-vent sediments captured strong geochemical spatial patterns that varied from advective to diffusive sulfide transport from the subsurface. Despite clear visual evidence for the close association of vent organisms and hydrothermalism, the sulfur and oxygen isotope composition of pore fluids did not permit delineation of a biotic signal separate from an abiotic signal. Hydrogen sulfide (H2S) in the free gas had uniform δ34S values (2.5 ± 0.28‰, n = 4) that were nearly identical to pore water H2S (2.7 ± 0.36‰, n = 21). In pore water sulfate, there were no paired increases in δ34SSO4 and δ18OSO4 as expected of microbial sulfate reduction. Instead, pore water δ34SSO4 values decreased (from approximately 21‰ to 17‰) as temperature increased (up to 97.4°C) across each hydrothermal feature. We interpret the inverse relationship between temperature and δ34SSO4 as a mixing process between oxic seawater and 34S-depleted hydrothermal inputs that are oxidized during seawater entrainment. An isotope mass balance model suggests secondary sulfate from sulfide oxidation provides at least 15% of the bulk sulfate pool. Coincident with this trend in δ34SSO4, the oxygen isotope composition of sulfate tended to be 18O-enriched in low pH (<5), high temperature (>75°C) pore waters. The shift toward high δ18OSO4 is consistent with equilibrium isotope exchange under acidic and high temperature conditions. The source of H2S contained in hydrothermal fluids could not be determined with the present dataset; however, the end-member δ34S value of H2S discharged to the seafloor is consistent with equilibrium isotope exchange with subsurface anhydrite veins at a temperature of ~300°C. Any biological sulfur cycling within these hydrothermal systems is masked by abiotic chemical reactions driven by mixing between low-sulfate, H2S-rich hydrothermal fluids and oxic, sulfate-rich seawater. PMID:25183951

Ammonia on the prebiotic Earth: Iron(II) reduction of nitrite. [Abstract only

NASA Technical Reports Server (NTRS)

Summers, David P.; Chang, Sherwood

1994-01-01

Theories for the origin of life require the availability of reduced nitrogen. In the non-reducing atmosphere suggested by geochemical evidence, production in the atmosphere and survival of NH3 against photochemical destruction are problematic. Electric discharges and impact shocks would produce NO rather than HCN or NH3. Conversion of NO to nitrous and nitric acid (by way of HNO) and precipitation in acid rain would provide a source of fixed nitrogen to the early ocean. One solution to the NH3 problem may have been the reduction of nitrite/nitrate in the ocean with aqueous ferrous iron, Fe(2+): 6Fe(+2) + 7 H2O + NO2(-) yields 3Fe2O3 + 11 H(+) + NH3. We have measured the kinetics of this reaction as a function of temperature, pH, and concentrations of salts, Fe(+2), and NO2(-). Cations (Na(+), Mg(2+), K(+)) and anions (Cl(-), Br(-), SO4(2-)) increase the rate by factors of 4 to 8. Although a competing pathway yields N2, the efficiency of the conversion of nitrite to ammonia ranges from 25% to 85%. Nitrate reduction was not consistently reproducible; however, when it was observed, its rate was slower by at least 8X than that of nitrite reduction. If the prebiotic atmosphere contained 0.2 to 10 atmospheres CO2 as suggested by Walker (1985), the Fe(+2) concentration and the rate would have been limited by siderite (FeCO3) solubility.

A detailed study of Au-Ni bimetal synthesized by the phase separation mechanism for the cathode of low-temperature solid oxide fuel cells

NASA Astrophysics Data System (ADS)

Yang, Tao; Rodrigues de Almeida, Carlos Manuel; Ramasamy, Devaraj; Almeida Loureiro, Francisco José

2014-12-01

A facile co-reduction and annealing synthesis route of nanospheric particles of Au-Ni bimetal with adjustable composition was developed. In a typical synthesis, a direct co-reduction of HAuCl4.4H2O and NiCl2 in aqueous solution was performed with the assistance of reductive NaBH4 and an anionic surfactant sodium dodecyl sulfate (SDS) functioned as the structure-directing agent. Ultrasonic mixing was used at the same time to control the size of the particles. The morphology, microstructure and the state of the surface atoms were analyzed in detail. These nanospheres showed enhanced electrocatalytic activity towards oxygen reduction reaction than that of pure Au nanoparticles, demonstrated in the low temperature SOFC as cathode. The maximum power density generated is 810 mW cm-2 at 550 °C. This is a promising route of taking advantages the Phase Separation Mechanism to greatly reduce the use of noble metals in the ORR field without sacrificing the electrocatalytic activity.

H2S induced hypometabolism in mice is missing in sedated sheep.

PubMed

Haouzi, Philippe; Notet, Véronique; Chenuel, Bruno; Chalon, Bernard; Sponne, Isabelle; Ogier, Virginie; Bihain, Bernard

2008-01-01

On the basis of studies performed in mice that showed H(2)S inhalation decreasing dramatically the metabolic rate, H(2)S was proposed as a means of protecting vital organs from traumatic or ischemic episodes in humans. Hypoxia has in fact also long been shown to induce hypometabolism. However, this effect is observed solely in small-sized animals with high VO2 kg(-1), and not in large mammals. Thus, extrapolating the hypometabolic effect of H(2)S to large mammals is questionable and could be potentially dangerous. We measured metabolism in conscious mice (24 g) exposed to H(2)S (60 ppm) at an ambient temperature of 23-24 degrees C. H(2)S caused a rapid and large (50%) drop in gas exchange rate, which occurred independently of the change in body temperature. The metabolic response occurred within less than 3 min. In contrast, sheep, sedated with ketamine and weighing 74 kg did not exhibit any decrease in metabolic rate during a similar challenge at an ambient temperature of 22 degrees C. While a part of H(2)S induced hypometabolism in the mice is related to the reduction in activity, we speculate that the difference between sheep and mice may rely on the nature and the characteristics of the relationship between basal metabolic rate and body weight thus on the different mechanisms controlling resting metabolic rate according to body mass. Therefore, the proposed use of H(2)S administration as a way of protecting vital organs should be reconsidered in view of the lack of hypometabolic effect in a large sedated mammal and of H(2)S established toxicity.

Kinetic and catalytic analysis of mesoporous Co3O4 on the oxidation of morin

NASA Astrophysics Data System (ADS)

Xaba, Morena. S.; Meijboom, Reinout

2017-11-01

Herein we report on the synthesis, characterization and catalytic evaluation of mesoporous cobalt oxides on the oxidation of morin. These mesoporous cobalt oxides were synthesized using an inverse surfactant micelle method, they are connected, well-defined with intra-particle voids. These materials were calcined to different final heating temperatures of 150, 250, 350, 450 and 550 °C, and each mesoporous cobalt oxide catalyst showed unique physical properties and catalytic behavior. Morin oxidation was used as a model reaction in the presence of hydrogen peroxide to evaluate the kinetic and catalytic activity of calcined mesoporous cobalt oxides. The adsorption-desorption equilibrium rate constants of morin and hydrogen peroxide were found to be inversely proportional to the crystallite size of the mesoporous cobalt oxide, and the characteristic path length in which the mass transfer takes place was found to be directly proportional to the crystallite size. The materials were characterized using powder X-Ray Diffraction (p-XRD), N2-sorption isotherms (BET), hydrogen temperature programmed reduction (H2-TPR) and High Resolution-Transmission Electron Microscopy (HR-TEM). UV-vis spectrophotometry was used to monitor the time-resolved absorbance of morin at λmax = 410 nm. The surface reaction in this system is described in terms of the well-established Langmuir-Hinshelwood model. The thermodynamic parameters, EA, ΔH#, ΔS# and ΔG# were calculated and catalyst recycling and reusability is demonstrated.

Missing magnetism in Sr 4Ru 3O 10: Indication for Antisymmetric Exchange Interaction

DOE PAGES

Weickert, Franziska; Civale, Leonardo; Maiorov, Boris; ...

2017-06-20

Metamagnetism occuring inside a ferromagnetic phase is peculiar. Therefore, Sr 4Ru 3O 10, a T C = 105 K ferromagnet, has attracted much attention in recent years, because it develops a pronounced metamagnetic anomaly below T C for magnetic fields applied in the crystallographic ab-plane. The metamagnetic transition moves to higher fields for lower temperatures and splits into a double anomaly at critical fields H c1 = 2.3 T and H c2 = 2.8 T, respectively. Here, we report a detailed study of the different components of the magnetization vector as a function of temperature, applied magnetic field, and varyingmore » angle in Sr 4Ru 3O 10. We discover for the first time a reduction of the magnetic moment in the plane of rotation at the metamagnetic transition. The anomaly shifts to higher fields by rotating the field from H ⊥ c to H || c. We compare our experimental findings with numerical simulations based on spin reorientation models taking into account magnetocrystalline anisotropy, Zeeman effect and antisymmetric exchange interactions. While Magnetocrystalline anisotropy combined with a Zeeman term are sufficient to explain a metamagnetic transition in Sr 4Ru 3O 10, a Dzyaloshinskii-Moriya term is crucial to account for the reduction of the magnetic moment as observed in the experiments.« less

Missing magnetism in Sr 4Ru 3O 10: Indication for Antisymmetric Exchange Interaction

DOE Office of Scientific and Technical Information (OSTI.GOV)

Weickert, Franziska; Civale, Leonardo; Maiorov, Boris

Metamagnetism occuring inside a ferromagnetic phase is peculiar. Therefore, Sr 4Ru 3O 10, a T C = 105 K ferromagnet, has attracted much attention in recent years, because it develops a pronounced metamagnetic anomaly below T C for magnetic fields applied in the crystallographic ab-plane. The metamagnetic transition moves to higher fields for lower temperatures and splits into a double anomaly at critical fields H c1 = 2.3 T and H c2 = 2.8 T, respectively. Here, we report a detailed study of the different components of the magnetization vector as a function of temperature, applied magnetic field, and varyingmore » angle in Sr 4Ru 3O 10. We discover for the first time a reduction of the magnetic moment in the plane of rotation at the metamagnetic transition. The anomaly shifts to higher fields by rotating the field from H ⊥ c to H || c. We compare our experimental findings with numerical simulations based on spin reorientation models taking into account magnetocrystalline anisotropy, Zeeman effect and antisymmetric exchange interactions. While Magnetocrystalline anisotropy combined with a Zeeman term are sufficient to explain a metamagnetic transition in Sr 4Ru 3O 10, a Dzyaloshinskii-Moriya term is crucial to account for the reduction of the magnetic moment as observed in the experiments.« less

Electrodeposition of nanostructured Sn-Zn coatings

NASA Astrophysics Data System (ADS)

Salhi, Y.; Cherrouf, S.; Cherkaoui, M.; Abdelouahdi, K.

2016-03-01

The electrodeposition of Sn-Zn coating at ambient temperature was investigated. The bath consists of metal salts SnCl2·2H2O and ZnSO4·7H2O and sodium citrate (NaC6H5Na3O7·2H2O) as complexing agent. To prevent precipitation, the pH is fixed at 5. Reducing tin and zinc through Sncit2- and ZnHcit- complex respectively is confirmed by the presence of two cathodic peaks on the voltammogram. The kinetic of tin (II) reduction process is limited by the SnCit2- dissociation. The SEM and TEM observations have showed that the coating consists of a uniform Sn-Zn layer composed of fine grains on which tin aggregates grow up. XRD revealed peaks corresponding to the hexagonal Zn phase and the tetragonal β-Sn phase.

Catalytically Enhanced Hydrogen Sorption in Mg-MgH2 by Coupling Vanadium-Based Catalyst and Carbon Nanotubes

PubMed Central

Kadri, Atikah; Jia, Yi; Chen, Zhigang; Yao, Xiangdong

2015-01-01

Mg (MgH2)-based composites, using carbon nanotubes (CNTs) and pre-synthesized vanadium-based complex (VCat) as the catalysts, were prepared by high-energy ball milling technique. The synergistic effect of coupling CNTs and VCat in MgH2 was observed for an ultra-fast absorption rate of 6.50 wt. % of hydrogen per minute and 6.50 wt. % of hydrogen release in 10 min at 200 °C and 300 °C, respectively. The temperature programmed desorption (TPD) results reveal that coupling VCat and CNTs reduces both peak and onset temperatures by more than 60 °C and 114 °C, respectively. In addition, the presence of both VCat and CNTs reduces the enthalpy and entropy of desorption of about 7 kJ/mol H2 and 11 J/mol H2·K, respectively, as compared to those of the commercial MgH2, which ascribe to the decrease of desorption temperature. From the study of the effect of CNTs milling time, it is shown that partially destroyed CNTs (shorter milling time) are better to enhance the hydrogen sorption performance.

In situ formation of a 3D core-shell and triple-conducting oxygen reduction reaction electrode for proton-conducting SOFCs

NASA Astrophysics Data System (ADS)

Zhang, Zhenbao; Wang, Jian; Chen, Yubo; Tan, Shaozao; Shao, Zongping; Chen, Dengjie

2018-05-01

BaZrxCeyY1-x-yO3-δ are recognized proton-conducting electrolyte materials for proton-conducting solid oxide fuel cells (H+-SOFCs) below 650 °C. Here Co cations are incorporated into the BaZr0.4Ce0.4Y0.2O3-δ (BZCY) scaffold to generate a 3D core-shell and triple-conducting (H+/O2-/e-) electrode in situ via infiltrating and reactive sintering. The core is the bulk BZCY scaffold, while the shell is composed of the cubic Ba(Zr0.4Ce0.4Y0.2)1-xCoxO3-δ, cubic spinel Co3O4 and cubic fluorite (Ce, Zr, Y)O2. The obtained electrode exhibits an excellent compatibility with the BZCY electrolyte, and performs well in yielding a low and stable polarization resistance for oxygen reduction reaction for intermediate-temperature H+-SOFCs. In particular, it achieves polarization resistances as low as 0.094 and 0.198 Ω cm2 at 650 and 600 °C in wet air (3% H2O) when the sintering temperature for the electrode is 900 °C. In addition, a symmetrical cell also exhibits operation stability of 70 h at 650 °C. Furthermore, a fuel cell assembled with the 3D core-shell and triple-conducting electrode delivers a peak power density of ∼330 mW cm-2 at 650 °C. The substantially improved electrochemical performance and high stability are ascribed to the unique core-shell structure and the formation of Ba(Zr0.4Ce0.4Y0.2)1-xCoxO3-δ in the shell.

Enhanced activity and stability of copper oxide/γ-alumina catalyst in catalytic wet-air oxidation: Critical roles of cerium incorporation

NASA Astrophysics Data System (ADS)

Zhang, Yongli; Zhou, Yanbo; Peng, Chao; Shi, Junjun; Wang, Qingyu; He, Lingfeng; Shi, Liang

2018-04-01

By successive impregnation method, the Ce-modified Cu-O/γ-Al2O3 catalyst was prepared and characterized using nitrogen adsorption-desorption, scanning electron microscopy energy dispersive X-ray analysis (SEM-EDS), high-resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Raman, and H2-Temperature programming reduction (H2-TPR). In catalytic wet-air oxidation (CWAO) process for the printing and dyeing wastewater (PDW), the effects of Ce addition on performance, mechanism and kinetics of the catalyst were investigated. The Ce addition increases the Brunauer-Emmett-Teller (BET) surface area and pore volume of the catalyst and makes the active components uniformly distributed on the catalyst surface. Formation of a stable CuAl2O4 solid solution by anchoring Cu onto the γ-Al2O3 crystal lattice leads to a significant decrease in metal leaching of the Ce-modified catalyst. The proportion of lattice oxygen in the catalyst substantially increases and the apparent activation energy of Cu-O/γ-Al2O3 catalyst decreases owing to Ce addition. Therefore, the catalytic activity and stability of the Ce-modified catalyst are considerably improved. The scavengers experiments identify the active species existed in the CWAO reaction system, with the order of reactivity: h+ > O2•- > H2O2 > HO•. This novel Cu-Ce-O/γ-Al2O3 catalyst has great potential in applications for treatment of concentrated organic wastewater due to its superior catalytic activity and improved stability.

Highly Depleted Ethane and Slightly Depleted Methanol in Comet 21P/Giacobini-Zinner: Application of Empirical g-Factors for CH3OH Near 50K

NASA Technical Reports Server (NTRS)

DiSanti, Michael A.; Bonev, Boncho P.; Mumma, Michael J.; Villanueva, Geronimo L.

2010-01-01

We report high resolution (lambda/delta lambda approximately 24,000) observations of Comet 21 P/Giacobini-Zinner (21P) between approximately 2.85 -- 3.54 micrometers, obtained with NIRSPEC at Keck 2 on UT 2005 June 03 (R(sub h) = 1.12 AU, delta = 1.45 AU). These simultaneously sampled multiple emissions from the v7 band of C2H6 and the v2 and v3 bands of CH3OH, together with several hot bands of H2O, permitting a direct measure of parent volatile abundances in 21P. Our spectra reveal highly depleted C2H6 (0.13-0.14 percent relative to H2O) and CH3OH/C2H6 approximately 10, consistent with previously published abundances from observations in the IR [1,2] and millimeter sub-mm (reporting CH3OH/H2O [3]) during its previous apparition in 1998. We observed similarly high CH3OH/C2H6, and also similar rotational temperature to that measured for 21 P, in Comet 8P/Tuttle [4,5]. We used our (higher signal-to-noise) NIRSPEC observations of 8P to produce effective (empirical) CH3OH g-factors for several lines in the v2 band. These will be presented together with interpretation of our results, including constraints on the spin temperature of water. We acknowledge support from the NASA Planetary Atmospheres, Planetary Astronomy, and Astrobiology Programs and from the NSF Astronomy and Astrophysics Research Grants Program.

Thermodynamics and performance of the Mg-H-F system for thermochemical energy storage applications.

PubMed

Tortoza, Mariana S; Humphries, Terry D; Sheppard, Drew A; Paskevicius, Mark; Rowles, Matthew R; Sofianos, M Veronica; Aguey-Zinsou, Kondo-Francois; Buckley, Craig E

2018-01-24

Magnesium hydride (MgH 2 ) is a hydrogen storage material that operates at temperatures above 300 °C. Unfortunately, magnesium sintering occurs above 420 °C, inhibiting its application as a thermal energy storage material. In this study, the substitution of fluorine for hydrogen in MgH 2 to form a range of Mg(H x F 1-x ) 2 (x = 1, 0.95, 0.85, 0.70, 0.50, 0) composites has been utilised to thermodynamically stabilise the material, so it can be used as a thermochemical energy storage material that can replace molten salts in concentrating solar thermal plants. These materials have been studied by in situ synchrotron X-ray diffraction, differential scanning calorimetry, thermogravimetric analysis, temperature-programmed-desorption mass spectrometry and Pressure-Composition-Isothermal (PCI) analysis. Thermal analysis has determined that the thermal stability of Mg-H-F solid solutions increases proportionally with fluorine content, with Mg(H 0.85 F 0.15 ) 2 having a maximum rate of H 2 desorption at 434 °C, with a practical hydrogen capacity of 4.6 ± 0.2 wt% H 2 (theoretical 5.4 wt% H 2 ). An extremely stable Mg(H 0.43 F 0.57 ) 2 phase is formed upon the decomposition of each Mg-H-F composition of which the remaining H 2 is not released until above 505 °C. PCI measurements of Mg(H 0.85 F 0.15 ) 2 have determined the enthalpy (ΔH des ) to be 73.6 ± 0.2 kJ mol -1 H 2 and entropy (ΔS des ) to be 131.2 ± 0.2 J K -1 mol -1 H 2 , which is slightly lower than MgH 2 with ΔH des of 74.06 kJ mol -1 H 2 and ΔS des = 133.4 J K -1 mol -1 H 2 . Cycling studies of Mg(H 0.85 F 0.15 ) 2 over six absorption/desorption cycles between 425 and 480 °C show an increased usable cycling temperature of ∼80 °C compared to bulk MgH 2 , increasing the thermal operating temperatures for technological applications.

Particle size effect of redox reactions for Co species supported on silica

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chotiwan, Siwaruk; Tomiga, Hiroki; Katagiri, Masaki

Conversions of chemical states during redox reactions of two silica-supported Co catalysts, which were prepared by the impregnation method, were evaluated by using an in situ XAFS technique. The addition of citric acid into the precursor solution led to the formation on silica of more homogeneous and smaller Co particles, with an average diameter of 4 nm. The supported Co{sub 3}O{sub 4} species were reduced to metallic Co via the divalent CoO species during a temperature-programmed reduction process. The reduced Co species were quantitatively oxidized with a temperature-programmed oxidation process. The higher observed reduction temperature of the smaller CoO particlesmore » and the lower observed oxidation temperature of the smaller metallic Co particles were induced by the higher dispersion of the Co oxide species, which apparently led to a stronger interaction with supporting silica. The redox temperature between CoO and Co{sub 3}O{sub 4} was found to be independent of the particle size. - Graphical abstract: Chemical state conversions of SiO{sub 2}-supported Co species and the particle size effect have been analyzed by means of in situ XAFS technique. The small CoO particles have endurance against the reduction and exist in a wide temperature range. Display Omitted - Highlights: • The conversions of the chemical state of supported Co species during redox reaction are evaluated. • In operando XAFS technique were applied to measure redox properties of small Co particles. • A small particle size affects to the redox temperatures of cobalt catalysts.« less

Manganese Oxide Nanoarray-Based Monolithic Catalysts: Tunable Morphology and High Efficiency for CO Oxidation

DOE PAGES

Chen, Sheng-Yu; Song, Wenqiao; Lin, Hui-Jan; ...

2016-03-08

In this work, a generic one-pot hydrothermal synthesis route has been successfully designed and utilized to in situ grow uniform manganese oxide nanorods and nanowires onto the cordierite honeycomb monolithic substrates, forming a series of nanoarray-based monolithic catalysts. During the synthesis process, three types of potassium salt oxidants have been used with different reduction potentials, i.e., K 2Cr 2O 7, KClO 3, and K 2S 2O 8, denoted as HM-DCM, HM-PCR, and HM-PSF, respectively. The different reduction potentials of the manganese source (Mn 2+) and oxidants induced the formation of manganese oxide nanoarrays with different morphology, surface area, and reactivitymore » of carbon monoxide (CO) oxidation. K 2Cr 2O 7 and KClO 3 can induce sharp and long nanowires with slow growth rates due to their low reduction potentials. In comparison, the nanoarrays of HM-PSF presented shorter nanorods but displayed an efficient 90% CO oxidation conversion at 200 °C (T90) without noble-metal loading. Reducibility tests for the three monolithic catalysts by hydrogen temperature-programmed reduction revealed an activation energy order of HM-PSF > HM-DCM > HM-PCR for CO oxidation. The characterizations of oxygen temperature-programmed desorption and X-ray photoelectron spectroscopy indicated the abundant surface-adsorbed oxygen and lattice oxygen contributing to the superior reactivity of HM-PSF. Finally, the straightforward synthetic process showed a scalable, low-cost, and template-free method to fabricate manganese oxide nanoarray monolithic catalysts for exhaust treatment.« less

Innovative Plasma Disinfection Technique with the Reduced-pH Method and the Plasma-Treated Water (PTW) -Safety and Powerful Disinfection with Cryopreserved PTW-

NASA Astrophysics Data System (ADS)

Kitano, Katsuhisa; Ikawa, Satoshi; Nakashima, Yoichi; Tani, Atsushi; Yokoyama, Takashi; Ohshima, Tomoko

2015-09-01

Among the applications of the plasma disinfection to human body, plasma sterilization in liquid is crucial. We found that the plasma-treated water (PTW) has strong bactericidal activity under low pH condition and the half-lives of its activity depend on temperature. Lower temperature brings longer half-life and the bactericidal activity of PTW can be kept by cryopreservation. These physicochemical properties were in accordance with Arrhenius equation both in liquid and solid states. From the experimental results of ESR (Electron Spin Resonance) measurement of O2-in liquid against PTW with spin trapping method, half-lives of PTW were also in accordance with Arrhenius equation. It suggests that high concentration PTW as integrated value can be achieved by cooling of plasma apparatus. Pure PTW has disinfection power of 22 log reduction (B. subtilis). This corresponds to 65% H2O2, 14% hypochlorous acid and 0.33% peracetic acid, which are deadly poison for human. On the other hand, PTW is deactivated soon at body temperature. This indicates that toxicity to human body seems to be low. PTW, which is a sort of indirect plasma exposure, with pH and temperature controls could be applied for safety and powerful disinfection. MEXT (15H03583, 23340176, 25108505). NCCE (23-A-15).

Effect of temperature on the efficiency of the thermo- and mesophilic aerobic batch biodegradation of high-strength distillery wastewater (potato stillage).

PubMed

Krzywonos, Małgorzata; Cibis, Edmund; Miśkiewicz, Tadeusz; Kent, Chris A

2008-11-01

The objective of the study was to assess the effect of temperature on the extent of aerobic batch biodegradation of potato stillage with a mixed culture of bacteria of the genus Bacillus. The experiments were performed in a 5-l stirred-tank reactor at 20, 30, 35, 40, 45, 50, 55, 60, 63 and 65 degrees C with the pH of 7. Only at 65 degrees C, no reduction in chemical oxygen demand (COD) was found to occur. Over the temperature range of 20-63 degrees C, the removal efficiency was very high (with an extent of COD reduction following solids separation that varied between 77.57% and 89.14% after 125 h). The process ran at the fastest rate when the temperature ranged from 30 to 45 degrees C; after 43 h at the latest, COD removal amounted to 90% of the final removal efficiency value obtained for the process. At 20, 55, 60 and 63 degrees C, a 90% removal was attained after 80 h. Two criteria were proposed for the identification of the point in time when the process is to terminate. One of these consists in maximising the product of the extent of COD reduction and the extent of N-NH4 content reduction. The other criterion is a simplified one and involves the search for the minimal value of N-NH4 concentration.

Regeneration of aluminum hydride

DOEpatents

Graetz, Jason Allan; Reilly, James J; Wegrzyn, James E

2012-09-18

The present invention provides methods and materials for the formation of hydrogen storage alanes, AlH.sub.x, where x is greater than 0 and less than or equal to 6 at reduced H.sub.2 pressures and temperatures. The methods rely upon reduction of the change in free energy of the reaction between aluminum and molecular H.sub.2. The change in free energy is reduced by lowering the entropy change during the reaction by providing aluminum in a state of high entropy, and by increasing the magnitude of the change in enthalpy of the reaction or combinations thereof.

CuO based catalysts on modified acidic silica supports tested in the de-NOx reduction.

PubMed

Bennici, Simona; Gervasini, Antonella; Lazzarin, Marta; Ragaini, Vittorio

2005-03-01

A series of dispersed CuO catalysts supported on modified silica supports with Al2O3 (SA), TiO2 (ST), and ZrO2 (SZ) were prepared optimising the adsorption method of copper deposition assisted by ultrasound treatment, already reported in a previous paper (S. Bennici, A. Gervasini, V. Ragaini, Ultrason. Sonochem. 10 (2003) 61). The obtained catalysts were characterized in their bulk (atomic absorption, X-ray diffraction, temperature programmed reduction) and surface (N2 adsorption, X-ray photoelectron spectroscopy, scanning electron microscopy) properties. The morphology of the finished materials was not deeply modified compared with that of the relevant supports. The employed complemented techniques evidenced a well dispersed CuO phase with a copper-support interaction on the most acidic supports (SA and SZ). The catalyst performances were studied in the reaction of selective catalytic reduction of NOx with ethene in oxidizing atmosphere in a flow apparatus under variable times (0.360-0.072 s) and temperatures (200-450 degrees C). The catalysts prepared on the most acidic supports (SA and SZ) were the most active and selective towards N2 formation. They showed a particular interesting activity in the reaction of NO2 reduction besides that of NO reduction.

A Ta/W mixed addenda heteropolyacid with excellent acid catalytic activity and proton-conducting property

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Shujun; Peng, Qingpo; Chen, Xuenian, E-mail: xnchen@htu.edu.cn

A new HPAs H{sub 20}[P{sub 8}W{sub 60}Ta{sub 12}(H{sub 2}O){sub 4}(OH){sub 8}O{sub 236}]·125H{sub 2}O (H-1) which comprises a Ta/W mixed addenda heteropolyanion, 20 protons, and 125 crystalline water molecules has been prepared through ion-exchange method. The structure and properties of H-1 have been explored in detail. AC impedance measurements indicate that H-1 is a good solid state proton conducting material at room temperature with a conductivity value of 7.2×10{sup −3} S cm{sup −1} (25 °C, 30% RH). Cyclic voltammograms of H-1 indicate the electrocatalytic activity towards the reduction of nitrite. Hammett acidity constant H{sub 0} of H-1 in CH{sub 3}CN ismore » −2.91, which is the strongest among the present known HPAs. Relatively, H-1 exhibits excellent catalytic activities toward acetal reaction. - Highlights: • A Ta/W mixed addenda Heteropolyacid (H-1) was isolated. • Hammett acidity constant H{sub 0} of H-1 is the strongest among the present known HPAs. • H-1 exhibits excellent catalytic activities toward acetal reaction. • H-1 is a good solid state proton conducting material at room temperature.« less

Accelerated step-temperature aging of Al/x/Ga/1-x/As heterojunction laser diodes

NASA Technical Reports Server (NTRS)

Kressel, H.; Ettenberg, M.; Ladany, I.

1978-01-01

Double-heterojunction A2(0.3)Ga(0.7)As/Al(0.08)Ga(0.92)As lasers (oxide-striped and Al2O3 facet coated) were subjected to step-temperature aging from 60 to 100 C. The change in threshold current and spontaneous output was monitored at 22 C. The average time required for a 20% pulsed threshold current increase ranges from about 500 h, when operating at 100 C, to about 5000 h at a 70 C ambience. At 22 C, the extrapolated time is about 1 million h. The time needed for a 50% spontaneous emission reduction is of the same order of magnitude. The resulting activation energies are approximately 0.95 eV for laser degradation and approximately 1.1 eV for the spontaneous output decrease

RECOZ data reduction and analysis: Programs and procedures

NASA Technical Reports Server (NTRS)

Reed, E. I.

1984-01-01

The RECOZ data reduction programs transform data from the RECOZ photometer to ozone number density and overburden as a function of altitude. Required auxiliary data are the altitude profile versus time and for appropriate corrections to the ozone cross sections and scattering effects, air pressure and temperature profiles. Air temperature and density profiles may also be used to transform the ozone density versus geometric altitude to other units, such as to ozone partial pressure or mixing ratio versus pressure altitude. There are seven programs used to accomplish this: RADAR, LISTRAD, RAW OZONE, EDIT OZONE, MERGE, SMOOTH, and PROFILE.

Treatment of Irradiated Graphite from French Bugey Reactor - 13424

DOE Office of Scientific and Technical Information (OSTI.GOV)

Brown, Thomas; Poncet, Bernard

2013-07-01

Beginning in 2009, in order to determine an alternative to direct disposal for decommissioned irradiated graphite from EDF's Bugey NPP, Studsvik and EDF began a test program to determine if graphite decontamination and destruction were practicable using Studsvik's thermal organic reduction (THOR) technology. The testing program focused primarily on the release of C-14, H-3, and Cl-36 and also monitored graphite mass loss. For said testing, a bench-scale steam reformer (BSSR) was constructed with the capability of flowing various compositions of gases at temperatures up to 1300 deg. C over uniformly sized particles of graphite for fixed amounts of time. Themore » BSSR was followed by a condenser, thermal oxidizer, and NaOH bubbler system designed to capture H-3 and C-14. Also, in a separate series of testing, high concentration acid and peroxide solutions were used to soak the graphite and leach out and measure Cl-36. A series of gasification tests were performed to scope gas compositions and temperatures for graphite gasification using steam and oxygen. Results suggested higher temperature steam (1100 deg. C vs. 900 deg. C) yielded a practicable gasification rate but that lower temperature (900 deg. C) gasification was also a practicable treatment alternative if oxygen is fed into the process. A series of decontamination tests were performed to determine the release behavior of and extent to which C-14 and H-3 were released from graphite in a high temperature (900-1300 deg. C), low flow roasting gas environment. In general, testing determined that higher temperatures and longer roasting times were efficacious for releasing H-3 completely and the majority (80%) of C-14. Manipulating oxidizing and reducing gas environments was also found to limit graphite mass loss. A series of soaking tests was performed to measure the amount of Cl-36 in the samples of graphite before and after roasting in the BSSR. Similar to C-14 release, these soaking tests revealed that 70-80% Cl-36 is released during roasting tests. (authors)« less

Effect of temperature on the low-linear energy transfer radiolysis of the ceric-cerous sulfate dosimeter: a Monte Carlo simulation study.

PubMed

Kohan, Leila Mirsaleh; Meesungnoen, Jintana; Sanguanmith, Sunuchakan; Meesat, Ridthee; Jay-Gerin, Jean-Paul

2014-05-01

The stochastic modeling of the (60)Co γ/fast-electron radiolysis of the ceric-cerous chemical dosimeter has been performed as a function of temperature from 25-350°C. The system used is a dilute solution of ceric sulfate and cerous sulfate in aqueous 0.4 M sulfuric acid. In this system, H(•) (or HO2(•) in the presence of dissolved oxygen) and H2O2 produced by the radiolytic decomposition of water both reduce Ce(4+) ions to Ce(3+) ions, while (•)OH radicals oxidize the Ce(3+) present in the solution back to Ce(4+). The net Ce(3+) yield is given by G(Ce(3+)) = g(H(•)) + 2 g(H2O2) - g((•)OH), where the primary (or "escape") yields of H(•), H2O2 and (•)OH are represented by lower case g's. At room temperature, G(Ce(3+)) has been established to be 2.44 ± 0.8 molecules/100 eV. In this work, we investigated the effect of temperature on the yield of Ce(3+) and on the underlying chemical reaction kinetics using Monte Carlo track chemistry simulations. The simulations showed that G(Ce(3+)) is time dependent, a result of the differences in the lifetimes of the reactions that make up the radiolysis mechanism. Calculated G(Ce(3+)) values were found to decrease almost linearly with increasing temperature up to about 250°C, and are in excellent agreement with available experimental data. In particular, our calculations confirmed previous estimated values by Katsumura et al. (Radiat Phys Chem 1988; 32:259-63) showing that G(Ce(3+)) at ∼250°C is about one third of its value at room temperature. Above ∼250°C, our model predicted that G(Ce(3+)) would drop markedly with temperature until, instead of Ce(4+) reduction, Ce(3+) oxidation is observed. This drop is shown to occur as a result of the reaction of hydrogen atoms with water in the homogeneous chemical stage.

Control of O-H bonds at a-IGZO/SiO2 interface by long time thermal annealing for highly stable oxide TFT

NASA Astrophysics Data System (ADS)

Jeon, Jae Kwon; Um, Jae Gwang; Lee, Suhui; Jang, Jin

2017-12-01

We report two-step annealing, high temperature and sequent low temperature, for amorphous indium-gallium-zinc-oxide (a-IGZO) thin-film transistor (TFT) to improve its stability and device performance. The annealing is carried out at 300 oC in N2 ambient for 1 h (1st step annealing) and then at 250 oC in vacuum for 10 h (2nd step annealing). It is found that the threshold voltage (VTH) changes from 0.4 V to -2.0 V by the 1st step annealing and to +0.6 V by 2nd step annealing. The mobility changes from 18 cm2V-1s-1 to 25 cm2V-1s-1 by 1st step and decreases to 20 cm2V-1s-1 by 2nd step annealing. The VTH shift by positive bias temperature stress (PBTS) is 3.7 V for the as-prepared TFT, and 1.7 V for the 1st step annealed TFT, and 1.3 V for the 2nd step annealed TFT. The XPS (X-ray photoelectron spectroscopy) depth analysis indicates that the reduction in O-H bonds at the top interface (SiO2/a-IGZO) by 2nd step annealing appears, which is related to the positive VTH shift and smaller VTH shift by PBTS.

Impact of Climate Change on Siberian High and Wintertime Air Pollution in China in Past Two Decades

NASA Astrophysics Data System (ADS)

Zhao, Shuyu; Feng, Tian; Tie, Xuexi; Long, Xin; Li, Guohui; Cao, Junji; Zhou, Weijian; An, Zhisheng

2018-02-01

China has suffered severe air pollutions during wintertime as national industrialization and urbanization have been increasingly developed in the past decades. Recent studies suggest that climate change has important impacts on extreme haze events in northern China. This study uses reanalysis datasets to analyze the trend and variability of Siberian High (SiH) intensity, and its relationship with the Arctic temperature and sea ice cover (SIC) in past two decades. The results show that Arctic is warming accompanied by a rapid decline of SIC, while Eurasia is cooling and SiH intensity is gradually enhancing. The statistics illustrates that the SiH has a significantly positive correlation to the temperature (R = 0.70), and a significant anticorrelation to the SIC (R = -0.69), and this is because the warming Arctic and the reducing SIC enhanced the SiH. The enhanced SiH leads to strengthened northerly winds in the North China Plain (NCP). The WRF-Chem model calculation reveals the strengthened northerly winds during the stronger SiH period in January 2016 produce a significant decrease in PM2.5 (particulate matter with aerodynamic diameter less than 2.5 µm) concentrations by 100-200 µg m-3 than that during the weaker one in January 2013. A sensitivity calculation figures out the reduction of PM2.5 concentrations due to a decrease of 50% in emissions is comparable to changes from the weak SiH condition to the strong SiH condition, suggesting that extreme climate variability in the past few years could have an equivalent impact as a consequence of a large emission reduction on wintertime air pollution in the NCP.

Fe Isotope Fractionation During Fe(III) Reduction to Fe(II)

NASA Astrophysics Data System (ADS)

Baker, E. A.; Greene, S.; Hardin, E. E.; Hodierne, C. E.; Rosenberg, A.; John, S.

2014-12-01

The redox chemistry of Fe(III) and Fe(II) is tied to a variety of earth processes, including biological, chemical, or photochemical reduction of Fe(III) to Fe(II). Each process may fractionate Fe isotopes, but the magnitudes of the kinetic isotope effects have not been greatly explored in laboratory conditions. Here, we present the isotopic fractionation of Fe during reduction experiments under a variety of experimental conditions including photochemical reduction of Fe(III) bound to EDTA or glucaric acid, and chemical reduction of Fe-EDTA by sodium dithionite, hydroxylamine hydrochloride, Mn(II), and ascorbic acid. A variety of temperatures and pHs were tested. In all experiments, Fe(III) bound to an organic ligand was reduced in the presence of ferrozine. Ferrozine binds with Fe(II), forming a purple complex which allows us to measure the extent of reaction. The absorbance of the experimental solutions was measured over time to determine the Fe(II)-ferrozine concentration and thus the reduction rate. After about 5% of the Fe(III) was reduced, Fe(III)-EDTA and Fe(II)-ferrozine were separated using a C-18 column to which Fe(II)-ferrozine binds. The Fe(II) was eluted and purified through anion exchange chromatography for analysis of δ56Fe by MC-ICPMS. Preliminary results show that temperature and pH both affect reduction rate. All chemical reductants tested reduce Fe(III) at a greater rate as temperature increases. The photochemical reductant EDTA reduces Fe(III) at a greater rate under more acidic conditions. Comparison of the two photochemical reductants shows that glucaric acid reduces Fe(III) significantly faster than EDTA. For chemical reduction, the magnitude of isotopic fractionation depends on the reductant used. Temperature and pH also affect the isotopic fractionation of Fe. Experiments using chemical reductants show that an increase in temperature at low temperatures produces lighter 56Fe ratios, while at high temperatures some reductants produce heavier 56Fe ratios. The magnitude of isotope fractionation is not related to the reduction rate generalized over all reductants. The measured isotopic fractionations produce δ56Fe from -3.82 to +3.05 across all of the reductants tested, highlighting the large impact that redox chemistry may have on fractionating Fe isotopes in the environment.

EPITAXIAL GROWTH OF SILICON

DTIC Science & Technology

Epitaxial growth of silicon on a silicon substrate by hydrogen reduction of SiCl4 was investigated. The chemical and physical processes involved in...silicon layers were produced at temperatures between 1100 and 1300 C. The effects of the concentration of SiCl4 in H2, the flow rate of the gas, the

Poly(N-vinyl-2-pyrrolidone)-stabilized palladium-platinum nanoparticles-catalyzed hydrolysis of ammonia borane for hydrogen generation

NASA Astrophysics Data System (ADS)

Rakap, Murat

2015-02-01

The catalytic use of highly efficient poly(N-vinyl-2-pyrrolidone)-stabilized palladium-platinum nanoparticles (4.2 ± 1.9 nm) in the hydrolysis of ammonia-borane is reported. The catalyst is prepared by co-reduction of two metal ions in ethanol/water mixture by an alcohol reduction method and characterized by transmission electron microscopy, X-ray photoelectron spectroscopy and UV-Vis spectroscopy. They are recyclable and highly active for hydrogen generation from the hydrolysis of ammonia-borane even at very low concentrations and temperature, providing a record numbers of average turnover frequency value (125 mol H2/mol cat.min-1) and maximum hydrogen generation rate (3468 L H2 min-1 (mol cat)-1). They also provide activation energy of 51.7 ± 2 kJ/mol for the hydrolysis of ammonia borane.

Sin(x)**2 + cos(x)**2 = 1. [programming identities using comparative combinatorial substitutions

NASA Technical Reports Server (NTRS)

Stoutemyer, D. R.

1977-01-01

Attempts to achieve tasteful automatic employment of the identities sin sq x + cos sq x = 1 and cos sq h x -sin sq h x = 1 in a manner which truly minimizes the complexity of the resulting expression are described. The disappointments of trigonometric reduction, trigonometric expansion, pattern matching, Poisson series, and Demoivre's theorem are related. The advantages of using the method of comparative combinatorial substitutions are illustrated.

Advanced Thermal Storage for Central Receivers with Supercritical Coolants

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kelly, Bruce D.

2010-06-15

The principal objective of the study is to determine if supercritical heat transport fluids in a central receiver power plant, in combination with ceramic thermocline storage systems, offer a reduction in levelized energy cost over a baseline nitrate salt concept. The baseline concept uses a nitrate salt receiver, two-tank (hot and cold) nitrate salt thermal storage, and a subcritical Rankine cycle. A total of 6 plant designs were analyzed, as follows: Plant Designation Receiver Fluid Thermal Storage Rankine Cycle Subcritical nitrate salt Nitrate salt Two tank nitrate salt Subcritical Supercritical nitrate salt Nitrate salt Two tank nitrate salt Supercritical Lowmore » temperature H2O Supercritical H2O Two tank nitrate salt Supercritical High temperature H2O Supercritical H2O Packed bed thermocline Supercritical Low temperature CO2 Supercritical CO2 Two tank nitrate salt Supercritical High temperature CO2 Supercritical CO2 Packed bed thermocline Supercritical Several conclusions have been drawn from the results of the study, as follows: 1) The use of supercritical H2O as the heat transport fluid in a packed bed thermocline is likely not a practical approach. The specific heat of the fluid is a strong function of the temperatures at values near 400 °C, and the temperature profile in the bed during a charging cycle is markedly different than the profile during a discharging cycle. 2) The use of supercritical CO2 as the heat transport fluid in a packed bed thermocline is judged to be technically feasible. Nonetheless, the high operating pressures for the supercritical fluid require the use of pressure vessels to contain the storage inventory. The unit cost of the two-tank nitrate salt system is approximately $24/kWht, while the unit cost of the high pressure thermocline system is nominally 10 times as high. 3) For the supercritical fluids, the outer crown temperatures of the receiver tubes are in the range of 700 to 800 °C. At temperatures of 700 °C and above, intermetallic compounds can precipitate between, and within, the grains of nickel alloys. The precipitation leads to an increase in tensile strength, and a decrease in ductility. Whether the proposed tube materials can provide the required low cycle fatigue life for the supercritical H2O and CO2 receivers is an open question. 4) A ranking of the plants, in descending order of technical and economic feasibility, is as follows: i) Supercritical nitrate salt and baseline nitrate salt: equal ratings ii) Low temperature supercritical H2O iii) Low temperature supercritical CO2 iv) High temperature supercritical CO2 v) High temperature supercritical H2O 5) The two-tank nitrate salt thermal storage systems are strongly preferred over the thermocline systems using supercritical heat transport fluids.« less

Platinum nanoparticles on carbon-nanotube support prepared by room-temperature reduction with H2 in ethylene glycol/water mixed solvent as catalysts for polymer electrolyte membrane fuel cells

NASA Astrophysics Data System (ADS)

Zheng, Yuying; Dou, Zhengjie; Fang, Yanxiong; Li, Muwu; Wu, Xin; Zeng, Jianhuang; Hou, Zhaohui; Liao, Shijun

2016-02-01

Polyol approach is commonly used in synthesizing Pt nanoparticles in polymer electrolyte membrane fuel cells. However, the application of this process consumes a great deal of time and energy, as the reduction of precursors requires elevated temperatures and several hours. Moreover, the ethylene glycol and its oxidizing products bound to Pt are difficult to remove. In this work, we utilize the advantages of ethylene glycol and prepare Pt nanoparticles through a room-temperature hydrogen gas reduction in an ethylene glycol/water mixed solvent, which is followed by subsequent harvesting by carbon nanotubes as electrocatalysts. This method is simple, facile, and time-efficient, as the entire room-temperature reduction process is completed in a few minutes. As the solvent changes from water to an ethylene glycol/water mix, the size of Pt nanoparticles varies from 10 to 3 nm and their shape transitions from polyhedral to spherical. Pt nanoparticles prepared in a 1:1 volume ratio mixture of ethylene glycol/water are uniformly dispersed with an average size of ∼3 nm. The optimized carbon nanotube-supported Pt electrocatalyst exhibits excellent methanol oxidation and oxygen reduction activities. This work demonstrates the potential use of mixed solvents as an approach in materials synthesis.

Oceanographic Observations in the Indian Ocean, March 1978. A Chemical Survey by Marine Environment Group,

DTIC Science & Technology

1980-09-01

METHOD OF COLLECTION AND ANALYSIS OF SAMPLES 2 3.1 Temperature 2 3.2 Thermometric Depth 2 3.3 Salinity 2 3.4 Dissolved Oxygen 3 3.5 Chlorinity 3 3.6 pH...or -40 to 600C) being used. The accuracZ of the temperature measurements has been quoted to be within the range ±0.03 C. 3.2 Thermometric Depth jp...Depths were calculated from temperature measurements by the method described by Pollack [91 using computer programs written at MRL. These thermometric

Thermotolerance and Heat-Shock Protein Gene Expression Patterns in Bemisia tabaci (Hemiptera: Aleyrodidae) Mediterranean in Relation to Developmental Stage.

PubMed

Jiang, Rui; Qi, Lan-Da; Du, Yu-Zhou; Li, Yuan-Xi

2017-10-01

Temperature plays an important role in the growth, development, and geographic distribution of insects. There is convincing evidence that heat-shock proteins (HSPs) play important roles in helping organisms adapt to thermal stress. To better understand the physiological and ecological influence of thermal stress on the different development stages of Bemisia tabaci (Gennadius) (Hemiptera: Aleyrodidae) Mediterranean species (MED), nymphs and adults were shocked with temperatures of 35, 38, and 41℃ for 1 and 2 h, respectively, and the survival rate, fecundity, and developmental duration were investigated in the laboratory. The expression levels of the hsp40, hsp70, and hsp90 genes were assessed using real-time PCR. The results indicate that the survival rates of the nymphs and adults decreased with increased temperature. A 2-h heat shock at 41℃ induced a significant reduction in fecundity in adults and an increase in developmental duration in young nymphs. Hsp90 showed higher temperature responses to thermal stress than hsp40 or hsp70. The expression levels of the hsps in the adults were significantly down-regulated by a 2-h heat shock at 41℃ compared with that by a 1-h treatment. A significant decrease in the expression levels of the hsps also occurred in the adults when the temperature increased from 38 to 41℃ for the 2-h treatment, whereas no significant decrease occurred in the nymphs. Compared with previous studies, we provide some evidence indicating that MED has the potential to adapt to a wider temperature range than the Middle East-Asia Minor 1 species. © The Author 2017. Published by Oxford University Press on behalf of Entomological Society of America. All rights reserved. For Permissions, please email: journals.permissions@oup.com.

Pd nanoparticle assemblies--as the substitute of HRP, in their biosensing applications for H2O2 and glucose.

PubMed

Han, Min; Liu, Suli; Bao, Jianchun; Dai, Zhihui

2012-01-15

The spherical porous Pd nanoparticle assemblies (NPAs) have been successfully synthesized by starch-assisted chemical reduction of Pd(II) species at room temperature. Such Pd NPAs are not simply used to enlarge the surface area and to promote the electron transfer. They also catalyze the reduction of H(2)O(2) which are regarded as horseradish peroxidase (HRP) substitutes in electron transfer process. By using them as electrocatalysts, as low as 6.8×10(-7) M H(2)O(2) can be detected with a linear range from 1.0×10(-6) to 8.2×10(-4) M. Moreover, through co-immobilization of such Pd NPAs and glucose oxidase (GOx), a sensitive and selective glucose biosensor is developed. The detection principle lies on measuring the increase of cathodic current by co-reduction of dissolved oxygen and the in situ generated H(2)O(2) during the enzymatic reaction. Under optimal conditions, the detection limit is down to 6.1×10(-6) M with a very wide linear range from 4.0×10(-5) to 2.2×10(-2) M. The proposed biosensor shows a fast response, good stability, high selectivity and reproducibility of serum glucose level. It provides a promising strategy to construct fast, sensitive, stable and anti-interferential amperometric biosensors for early diagnosis and prevention of diabetes. Copyright © 2011 Elsevier B.V. All rights reserved.

Hyperthermic-induced hyperventilation and associated respiratory alkalosis in humans.

PubMed

Abbiss, Chris R; Nosaka, Kazunori; Laursen, Paul B

2007-05-01

The purpose of this study was to determine if increased environmental heat leads to hyperthermic-induced hypocapnia and associated alkalosis during prolonged self-paced cycling. Nine male cyclists completed three 100 km stochastic time trials in hot (34 degrees C), neutral (22 degrees C) and cold (10 degrees C) environments. Intermittent measurements of rectal and skin temperature, expired gases, blood pH, PaCO(2), PaO(2), and bicarbonate were made throughout. Rectal temperature increased significantly throughout all trials (P < 0.001) and was significantly correlated with increases in the ventilatory equivalent for carbon dioxide (Ve/ VCo2; r = 0.77; P < 0.001) and blood pH (r = 0.69; P < 0.05). Rectal temperature was also negatively correlated with a reduction in PaCO(2) (r = -0.80; P < 0.001). PaO(2) and bicarbonate concentration remained constant throughout all trials. This study has shown that prolonged self-paced cycling is associated with a hyperthermic-induced hyperventilation, causing a decrease in arterialized carbon dioxide tension and consequential respiratory alkalosis.

Solar reduction of CO.sub.2

DOEpatents

Jensen, Reed J.; Lyman, John L.; King, Joe D.; Guettler, Robert D.

2000-01-01

The red shift of the absorption spectrum of CO.sub.2 with increasing temperature permits the use of sunlight to photolyze CO.sub.2 to CO. The process of the present invention includes: preheating CO.sub.2 to near 1800 K; exposing the preheated CO.sub.2 to sunlight, whereby CO, O.sub.2 and O are produced; and cooling the hot product mix by rapid admixture with room temperature CO.sub.2. The excess thermal energy may be used to produce electricity and to heat additional CO.sub.2 for subsequent process steps. The product CO may be used to generate H.sub.2 by the shift reaction or to synthesize methanol.

Mixed Redox Catalytic Destruction of Chlorinated Solvents in Soils and Groundwater: From the Laboratory to the Field

PubMed Central

Gao, Song; Rupp, Erik; Bell, Suzanne; Willinger, Martin; Foley, Theresa; Barbaris, Brian; Sáez, A. Eduardo; Arnold, Robert G.; Betterton, Eric

2010-01-01

A new thermocatalytic method to destroy chlorinated solvents has been developed in the laboratory and tested in a pilot field study. The method employs a conventional Pt/Rh catalyst on a ceramic honeycomb. Reactions proceed at moderate temperatures in the simultaneous presence of oxygen and a reductant (mixed redox conditions) to minimize catalyst deactivation. In the laboratory, stable operation with high conversions (above 90% at residence times shorter than 1 s) for perchloroethylene (PCE) is achieved using hydrogen as the reductant. A molar ratio of H2/O2 = 2 yields maximum conversions; the temperature required to produce maximum conversions is sensitive to influent PCE concentration. When a homologous series of aliphatic alkanes is used to replace hydrogen as the reductant, the resultant mixed redox conditions also produce high PCE conversions. It appears that the dissociation energy of the C–H bond in the respective alkane molecule is a strong determinant of the activation energy, and therefore the reaction rate, for PCE conversion. This new method was employed in a pilot field study in Tucson, Arizona. The mixed redox system was operated semicontinuously for 240 days with no degradation of catalyst performance and complete destruction of PCE and trichloroethylene in a soil vapor extraction gas stream. Use of propane as the reductant significantly reduced operating costs. Mixed redox destruction of chlorinated solvents provides a potentially viable alternative to current soil and groundwater remediation technologies. PMID:18991945

Proton Order-Disorder Phenomena in a Hydrogen-Bonded Rhodium-η(5)-Semiquinone Complex: A Possible Dielectric Response Mechanism.

PubMed

Mitsumi, Minoru; Ezaki, Kazunari; Komatsu, Yuuki; Toriumi, Koshiro; Miyatou, Tatsuya; Mizuno, Motohiro; Azuma, Nobuaki; Miyazaki, Yuji; Nakano, Motohiro; Kitagawa, Yasutaka; Hanashima, Takayasu; Kiyanagi, Ryoji; Ohhara, Takashi; Nakasuji, Kazuhiro

2015-06-26

A newly synthesized one-dimensional (1D) hydrogen-bonded (H-bonded) rhodium(II)-η(5)-semiquinone complex, [Cp*Rh(η(5)-p-HSQ-Me4)]PF6 ([1]PF6; Cp* = 1,2,3,4,5-pentamethylcyclopentadienyl; HSQ = semiquinone) exhibits a paraelectric-antiferroelectric second-order phase transition at 237.1 K. Neutron and X-ray crystal structure analyses reveal that the H-bonded proton is disordered over two sites in the room-temperature (RT) phase. The phase transition would arise from this proton disorder together with rotation or libration of the Cp* ring and PF6(-) ion. The relative permittivity εb' along the H-bonded chains reaches relatively high values (ca., 130) in the RT phase. The temperature dependence of (13)C CP/MAS NMR spectra demonstrates that the proton is dynamically disordered in the RT phase and that the proton exchange has already occurred in the low-temperature (LT) phase. Rate constants for the proton exchange are estimated to be 10(-4)-10(-6) s in the temperature range of 240-270 K. DFT calculations predict that the protonation/deprotonation of [1](+) leads to interesting hapticity changes of the semiquinone ligand accompanied by reduction/oxidation by the π-bonded rhodium fragment, producing the stable η(6)-hydroquinone complex, [Cp*Rh(3+)(η(6)-p-H2Q-Me4)](2+) ([2](2+)), and η(4)-benzoquinone complex, [Cp*Rh(+)(η(4)-p-BQ-Me4)] ([3]), respectively. Possible mechanisms leading to the dielectric response are discussed on the basis of the migration of the protonic solitons comprising of [2](2+) and [3], which would be generated in the H-bonded chain. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

In vitro evaluation of heat and moisture exchangers designed for spontaneously breathing tracheostomized patients.

PubMed

Brusasco, Claudia; Corradi, Francesco; Vargas, Maria; Bona, Margherita; Bruno, Federica; Marsili, Maria; Simonassi, Francesca; Santori, Gregorio; Severgnini, Paolo; Kacmarek, Robert M; Pelosi, Paolo

2013-11-01

Heat and moisture exchangers (HMEs) are commonly used in chronically tracheostomized spontaneously breathing patients, to condition inhaled air, maintain lower airway function, and minimize the viscosity of secretions. Supplemental oxygen (O2) can be added to most HMEs designed for spontaneously breathing tracheostomized patients. We tested the efficiency of 7 HMEs designed for spontaneously breathing tracheostomized patients, in a normothermic model, at different minute ventilations (VE) and supplemental O2 flows. HME efficiency was evaluated using an in vitro lung model at 2 VE (5 and 15 L/min) and 4 supplemental O2 flows (0, 3, 6, and 12 L/min). Wet and dry temperatures of the inspiratory flow were measured, and absolute humidity was calculated. In addition, HME efficiency at 0, 12, and 24 h use was evaluated, as well as resistance to flow at 0 and 24 h. The progressive increase in O2 flow from 0 to 12 L/min was associated with a reduction in temperature and absolute humidity. Under the same conditions, this effect was greater at lower VE. The HME with the best performance provided an absolute humidity of 26 mg H2O/L and a temperature of 27.8 °C. No significant changes in efficiency or resistance were detected during the 24 h evaluation. The efficiency of HMEs in terms of temperature and absolute humidity is significantly affected by O2 supplementation and V(E).

Increased tolerance of Vibrio cholerae O1 to temperature, pH, or drying associated with colonization of shrimp carapaces.

PubMed

Castro-Rosas, J; Escartín, E F

2005-07-15

External surfaces of samples of shrimp carapace were inoculated with Vibrio cholerae and stored at 22 degrees C for 1 h in a moist environment to facilitate their adhesion, or for 24 h to permit their colonization of the material. Colonizing cells showed a higher resistance to the effects of high temperatures, low pH, and desiccation conditions than adherent cells. Periods of 10, 5, and 3 min and 0 s were required to inactivate the pathogen when attached cells were exposed to 50, 60, 65, or 70 degrees C. The corresponding times for colonizing cells were 30, 15, 10, and 1 min. At pH 2.5 numbers of attached V. cholerae were reduced by >5 log after 16 min, whereas the reduction of colonizing cells was only 2.8 log. The survival times of the microorganism on dried carapaces stored at 5 and 22 degrees C were, respectively, 60 and 10 min for adherent cells, and 12 and 4 h for colonizing cells. The increased resistance to the effects of high temperatures, low pH, and desiccation of V. cholerae O1 colonizing shrimp carapaces may have significant implications for food safety and the epidemiology of cholera.

Formation of nanocarbon spheres by thermal treatment of woody char from fast pyrolysis process

Treesearch

Qiangu Yan; Hossein Toghiani; Zhiyong Cai; Jilei Zhang

2014-01-01

Influences of thermal treatment conditions of temperature, reaction cycle and time, and purge gas type on nanocarbon formation over bio-chars from fast pyrolysis and effects of thermal reaction cycle and purge gas type on bio-char surface functional groups were investigated by temperature-programmed desorption (TPD) and temperature programmed reduction methods....

Experiment and mechanism investigation on advanced reburning for NO(x) reduction: influence of CO and temperature.

PubMed

Wang, Zhi-Hua; Zhou, Jun-Hu; Zhang, Yan-Wei; Lu, Zhi-Min; Fan, Jian-Ren; Cen, Ke-Fa

2005-03-01

Pulverized coal reburning, ammonia injection and advanced reburning in a pilot scale drop tube furnace were investigated. Premix of petroleum gas, air and NH3 were burned in a porous gas burner to generate the needed flue gas. Four kinds of pulverized coal were fed as reburning fuel at constant rate of 1g/min. The coal reburning process parameters including 15% approximately 25% reburn heat input, temperature range from 1100 degrees C to 1400 degrees C and also the carbon in fly ash, coal fineness, reburn zone stoichiometric ratio, etc. were investigated. On the condition of 25% reburn heat input, maximum of 47% NO reduction with Yanzhou coal was obtained by pure coal reburning. Optimal temperature for reburning is about 1300 degrees C and fuel-rich stoichiometric ratio is essential; coal fineness can slightly enhance the reburning ability. The temperature window for ammonia injection is about 700 degrees C approximately 1100 degrees C. CO can improve the NH3 ability at lower temperature. During advanced reburning, 72.9% NO reduction was measured. To achieve more than 70% NO reduction, Selective Non-catalytic NO(x) Reduction (SNCR) should need NH3/NO stoichiometric ratio larger than 5, while advanced reburning only uses common dose of ammonia as in conventional SNCR technology. Mechanism study shows the oxidization of CO can improve the decomposition of H2O, which will rich the radical pools igniting the whole reactions at lower temperatures.

Experiment and mechanism investigation on advanced reburning for NOx reduction: influence of CO and temperature

PubMed Central

Wang, Zhi-hua; Zhou, Jun-hu; Zhang, Yan-wei; Lu, Zhi-min; Fan, Jian-ren; Cen, Ke-fa

2005-01-01

Pulverized coal reburning, ammonia injection and advanced reburning in a pilot scale drop tube furnace were investigated. Premix of petroleum gas, air and NH3 were burned in a porous gas burner to generate the needed flue gas. Four kinds of pulverized coal were fed as reburning fuel at constant rate of 1g/min. The coal reburning process parameters including 15%~25% reburn heat input, temperature range from 1100 °C to 1400 °C and also the carbon in fly ash, coal fineness, reburn zone stoichiometric ratio, etc. were investigated. On the condition of 25% reburn heat input, maximum of 47% NO reduction with Yanzhou coal was obtained by pure coal reburning. Optimal temperature for reburning is about 1300 °C and fuel-rich stoichiometric ratio is essential; coal fineness can slightly enhance the reburning ability. The temperature window for ammonia injection is about 700 °C~1100 °C. CO can improve the NH3 ability at lower temperature. During advanced reburning, 72.9% NO reduction was measured. To achieve more than 70% NO reduction, Selective Non-catalytic NOx Reduction (SNCR) should need NH3/NO stoichiometric ratio larger than 5, while advanced reburning only uses common dose of ammonia as in conventional SNCR technology. Mechanism study shows the oxidization of CO can improve the decomposition of H2O, which will rich the radical pools igniting the whole reactions at lower temperatures. PMID:15682503

Spent caustic oxidation using electro-generated Fenton's reagent in a batch reactor.

PubMed

Rodriguez, Nicolas; Hansen, Henrik K; Nunez, Patricio; Guzman, Jaime

2008-07-01

This work shows the results of four Electro-Fenton laboratory tests to reduce the chemical oxygen demand (COD) in spent caustic solutions. The treatment consisted of (i) a pH reduction followed by (ii) an Electro-Fenton process, which was analyzed in this work. The Fenton's reagent was produced in a specially designed reactor, where the waste stream flowed through a labyrinth made by ferrous plates. These plates acted as sacrificial anodes-releasing Fe(2 +) cations to the solution, where H(2)O(2) was also added. The Electro-Fenton process was analyzed varying the ferrous ion concentration ([Fe(+ 2)]), the spent caustic's initial temperature and the initial pH. Close to 95% removal of COD (from 8800 mg L(- 1)) was achieved at a pH of 4, a temperature of 40 degrees C and 100 mg L(- 1) of Fe(+ 2) (applying 1 A). Two models were considered to simulate the behavior of the reactor considering (i) axial dispersion and (ii) kinetic rate, respectively. The model that was based on kinetics, proved to be the slightly closest fit to the experimental values.

Nickel Nanocatalyst Ex-Solution from Ceria-Nickel Oxide Solid Solution for Low Temperature CO Oxidation.

PubMed

Singhania, Amit; Gupta, Shipra Mital

2018-07-01

In this work, in situ growth of Ni nanocatalysts to attach onto the ceria (CeO2) surface through direct Ni ex-solution from the NiO-CeO2 solid solution in a reducing atmosphere at high temperatures with an aim to improve the catalytic activity, and stability for low temperature carbon monoxide (CO) oxidation reaction have been reported. The NiO-CeO2 solid solutions were prepared by solution combustion method, and the results of XRD and RAMAN showed that doping of Ni increases the oxygen vacancies due to charge compensation. Ni is clearly visible in XRD and TEM of Ni ex-solved sample (R-UCe5Ni10) after reduction of NiO-CeO2 (UCe5Ni10) sample by 5% H2/Ar reduction at 1000 °C. TEM analysis revealed a size of 9.2 nm of Ni nanoparticle that is ex-solved on the surface CeO2. This ex-solved sample showed very high catalytic activity (T50 ~ 110 °C), and stability (100 h) for CO oxidation reaction as compared to prepared solid solution samples. This is due to the highly active metallic nano-phase which is ex-solved on the surface of CeO2 and strongly adherent to the support. The apparent activation energy Ni ex-solved sample is found out to be 48.4 kJ mol-1. Thus, the above Ni ex-solved sample shows a practical applicability for the CO reaction.

Theoretical estimation of equilibrium sulfur isotope fractionations among aqueous sulfite species: Implications for isotope models of microbial sulfate reduction

NASA Astrophysics Data System (ADS)

Eldridge, D. L.; Farquhar, J.; Guo, W.

2015-12-01

Sulfite (sensu lato), an intermediate in a variety sulfur redox processes, plays a particularly important role in microbial sulfate reduction. It exists intracellularly as multiple species between sets of enzymatic reactions that transform sulfate to sulfide, with the exact speciation depending on pH, T, and ionic strength. However, the complex speciation of sulfite is ignored in current isotope partitioning models of microbial sulfate reduction and simplified solely to the pyramidal SO32- (sulfite sensu stricto), due to a lack of appropriate constraints. We theoretically estimated the equilibrium sulfur isotope fractionations (33S/32S, 34S/32S, 36S/32S) among all documented sulfite species in aqueous solution, including sulfite (SO32-), bisulfite isomers and dimers ((HS)O3-, (HO)SO2-, S2O52-), and SO2(aq), through first principles quantum mechanical calculations. The calculations were performed at B3LYP/6-31+G(d,p) level using cluster models with 30-40 water molecules surrounding the solute. Our calculated equilibrium fractionation factors compare well to the available experimental constraints and suggest that the minor and often-ignored tetrahedral (HS)O3- isomer of bisulfite strongly influences isotope partitioning behavior in the sulfite system under most environmentally relevant conditions, particularly fractionation magnitudes and unusual temperature dependence. For example, we predict that sulfur isotope fractionation between sulfite and bulk bisulfite in solution should have an apparent inverse temperature dependence due to the influence of (HS)O3- and its increased stability at higher temperatures. Our findings highlight the need to appropriately account for speciation/isomerization of sulfur species in sulfur isotope studies. We will also present similar calculation results of other aqueous sulfur compounds (e.g., H2S/HS-, SO42-, S2O32-, S3O62-, and poorly documented SO22- species), and discuss the implication of our results for microbial sulfate reduction models and other sulfur-redox processes in nature.

Promising SiC support for Pd catalyst in selective hydrogenation of acetylene to ethylene

NASA Astrophysics Data System (ADS)

Guo, Zhanglong; Liu, Yuefeng; Liu, Yan; Chu, Wei

2018-06-01

In this study, SiC supported Pd nanoparticles were found to be an efficient catalyst in acetylene selective hydrogenation reaction. The ethylene selectivity can be about 20% higher than that on Pd/TiO2 catalyst at the same acetylene conversion at 90%. Moreover, Pd/SiC catalyst showed a stable catalytic life at 65 °C with 80% ethylene selectivity. With the detailed characterization using temperature-programmed reduction (H2-TPR), powder X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), N2 adsorption/desorption analysis, CO-chemisorption and thermo-gravimetric analysis (TGA), it was found that SiC owns a lower surface area (22.9 m2/g) and a broad distribution of meso-/macro-porosity (from 5 to 65 nm), which enhanced the mass transfer during the chemical process at high reaction rate and decreased the residence time of ethylene on catalyst surface. Importantly, SiC support has the high thermal conductivity, which favored the rapid temperature homogenization through the catalyst bed and inhabited the over-hydrogenation of acetylene. The surface electronic density of Pd on Pd/SiC catalyst was higher than that on Pd/TiO2, which could promote desorption of ethylene from surface of the catalyst. TGA results confirmed a much less coke deposition on Pd/SiC catalyst.

pH controls over methanogenesis and iron reduction along soil depth profile in Arctic tundra

NASA Astrophysics Data System (ADS)

Zheng, J.; Gu, B.; Wullschleger, S. D.; Graham, D. E.

2017-12-01

Increasing soil temperature in the Arctic is expected to accelerate rates of soil organic matter decomposition. However, the magnitude of this impact is uncertain due to the many physical, chemical, and biological processes that control the decomposition pathways. Varying soil redox conditions present a key control over pathways of organic matter decomposition by diverting the flow of reductants among different electron accepting processes and further driving acid-base reactions that alter soil pH. In this study we investigated the pH controls over anaerobic carbon mineralization, methanogenesis, Fe(III) reduction and the interplay between these processes across a range of pH and redox conditions. pH manipulation experiments were conducted by incubating soils representing organic, mineral, cryoturbated transitional layers and permafrost. In the experiments we sought to understand (1) if methanogenesis or Fe(III) reduction had similar pH optima; (2) if this pH response also occurs at `upstream' fermentation process; and (3) if pH alters organo-mineral association or organic matter sorption and desorption and its availability for microbial degradation. Our preliminary results suggest that the common bell-shaped pH response curve provides a good fit for both Fe(III) reduction and methanogenesis, with optimum pH at 6.0-7.0. Exceptions to this were found in transitional layer where methanogenesis rates positively correlated with increasing pH, with maximum rates measured at pH 8.5. It is likely that the transitional layer harbors distinct groups of methanogens that prefer a high pH. Variations in the optimum pH of Fe(III) reduction and methanogenesis may play a significant role in regulating organic matter decomposition pathways and thus greenhouse gas production in thawing soils. These results support biogeochemical modeling efforts to accurately simulate organic matter decomposition under changing redox and pH conditions.

Continuous flow room temperature reductive aqueous homo-coupling of aryl halides using supported Pd catalysts

PubMed Central

Feiz, Afsaneh; Bazgir, Ayoob; Balu, Alina M.; Luque, Rafael

2016-01-01

A convenient and environmentally friendly protocol for the preparation of biaryls at room temperature under continuous flow conditions is reported. A simple reductive homo-coupling Ullmann-type reaction was performed in an H-Cube mini using commercially available supported Pd catalysts under mild reaction conditions, with quantitative conversion to target products. Commercial Pd catalysts were found to be highly stable under the investigated reaction conditions, with a minimum Pd leaching into solution after several reaction runs (ca. 20 h on stream). PMID:27600989

Enhancement of activity of RuSex electrocatalyst by modification with nanostructured iridium towards more efficient reduction of oxygen

NASA Astrophysics Data System (ADS)

Dembinska, Beata; Kiliszek, Malgorzata; Elzanowska, Hanna; Pisarek, Marcin; Kulesza, Pawel J.

2013-12-01

Electrocatalytic activity of carbon (Vulcan XC-72) supported selenium-modified ruthenium, RuSex/C, nanoparticles for reduction of oxygen was enhanced through intentional decoration with iridium nanostructures (dimensions, 2-3 nm). The catalytic materials were characterized in oxygenated 0.5 mol dm-3 H2SO4 using cyclic and rotating ring disk voltammetric techniques as well as using transmission electron microscopy and scanning electron microscopy equipped with X-ray dispersive analyzer. Experiments utilizing gas diffusion electrode aimed at mimicking conditions existing in the low-temperature fuel cell. Upon application of our composite catalytic system, the reduction of oxygen proceeded at more positive potentials, and higher current densities were observed when compared to the behavior of the simple iridium-free system (RuSex/C) investigated under the analogous conditions. The enhancement effect was more pronounced than that one would expect from simple superposition of voltammetric responses for the oxygen reduction at RuSex/C and iridium nanostructures studied separately. Nanostructured iridium acted here as an example of a powerful catalyst for the reduction of H2O2 (rather than O2) and, when combined with such a moderate catalyst as ruthenium-selenium (for O2 reduction), it produced an integrated system of increased electrocatalytic activity in the oxygen reduction process. The proposed system retained its activity in the presence of methanol that could appear in a cathode compartment of alcohol fuel cell.

High temperature corrosion of austenitic stainless steel coils in a direct reduction plant in Mexico

DOE Office of Scientific and Technical Information (OSTI.GOV)

Juarez-Islas, J.A.; Campillo, B.; Chaudhary, N.

1996-08-01

The subject of this study is related to the performance of austenitic steels coils and tubes, in a range of temperatures between 425 to 870 C for the transport of reducing gases, in an installation involving the direct reduction of iron-ore by reforming natural gas. Evidence is presented that metal dusting is not the only unique high temperature corrosion mechanism that caused catastrophic failures of austenitic 304 (UNS S30400) coils and HK-40 (UNS J94204) tubes. Sensitization as well as stress corrosion cracking occurred in 304 stainless steel coils, and metal dusting occurred in tubes of HK-40, a high resistance alloy.more » The role of a continuous injection of H{sub 2}S to the process is suggested to avoid the high temperature metal dusting corrosion mechanism found in these kind of installations.« less

Resonant tunneling modulation in quasi-2D Cu2O/SnO2 p-n horizontal-multi-layer heterostructure for room temperature H2S sensor application

PubMed Central

Cui, Guangliang; Zhang, Mingzhe; Zou, Guangtian

2013-01-01

Heterostructure material that acts as resonant tunneling system is a major scientific challenge in applied physics. Herein, we report a resonant tunneling system, quasi-2D Cu2O/SnO2 p-n heterostructure multi-layer film, prepared by electrochemical deposition in a quasi-2D ultra-thin liquid layer. By applying a special half-sine deposition potential across the electrodes, Cu2O and SnO2 selectively and periodically deposited according to their reduction potentials. The as-prepared heterostructure film displays excellent sensitivity to H2S at room temperature due to the resonant tunneling modulation. Furthermore, it is found that the laser illumination could enhance the gas response, and the mechanism with laser illumination is discussed. It is the first report on gas sensing application of resonant tunneling modulation. Hence, heterostructure material act as resonant tunneling system is believed to be an ideal candidate for further improvement of room temperature gas sensing. PMID:23409241

Nitrite and hydroxylamine as nitrogenase substrates: mechanistic implications for the pathway of N₂ reduction.

PubMed

Shaw, Sudipta; Lukoyanov, Dmitriy; Danyal, Karamatullah; Dean, Dennis R; Hoffman, Brian M; Seefeldt, Lance C

2014-09-10

Investigations of reduction of nitrite (NO2(-)) to ammonia (NH3) by nitrogenase indicate a limiting stoichiometry, NO2(-) + 6e(-) + 12ATP + 7H(+) → NH3 + 2H2O + 12ADP + 12Pi. Two intermediates freeze-trapped during NO2(-) turnover by nitrogenase variants and investigated by Q-band ENDOR/ESEEM are identical to states, denoted H and I, formed on the pathway of N2 reduction. The proposed NO2(-) reduction intermediate hydroxylamine (NH2OH) is a nitrogenase substrate for which the H and I reduction intermediates also can be trapped. Viewing N2 and NO2(-) reductions in light of their common reduction intermediates and of NO2(-) reduction by multiheme cytochrome c nitrite reductase (ccNIR) leads us to propose that NO2(-) reduction by nitrogenase begins with the generation of NO2H bound to a state in which the active-site FeMo-co (M) has accumulated two [e(-)/H(+)] (E2), stored as a (bridging) hydride and proton. Proton transfer to NO2H and H2O loss leaves M-[NO(+)]; transfer of the E2 hydride to the [NO(+)] directly to form HNO bound to FeMo-co is one of two alternative means for avoiding formation of a terminal M-[NO] thermodynamic "sink". The N2 and NO2(-) reduction pathways converge upon reduction of NH2NH2 and NH2OH bound states to form state H with [-NH2] bound to M. Final reduction converts H to I, with NH3 bound to M. The results presented here, combined with the parallels with ccNIR, support a N2 fixation mechanism in which liberation of the first NH3 occurs upon delivery of five [e(-)/H(+)] to N2, but a total of seven [e(-)/H(+)] to FeMo-co when obligate H2 evolution is considered, and not earlier in the reduction process.

Organic reductants based leaching: A sustainable process for the recovery of valuable metals from spent lithium ion batteries.

PubMed

Chen, Xiangping; Guo, Chunxiu; Ma, Hongrui; Li, Jiazhu; Zhou, Tao; Cao, Ling; Kang, Duozhi

2018-05-01

It is significant to recover metal values from spent lithium ion batteries (LIBs) for the alleviation or prevention of potential risks towards environmental pollution and public health, as well as for the conservation of valuable metals. Herein a hydrometallurgical process was proposed to explore the possibility for the leaching of different metals from waste cathodic materials (LiCoO 2 ) of spent LIBs using organics as reductant in sulfuric acid medium. According to the leaching results, about 98% Co and 96% Li can be leached under the optimal experimental conditions of reaction temperature - 95 °C, reaction time - 120 min, reductive agent dosage - 0.4 g/g, slurry density - 25 g/L, concentration of sulfuric acid-3 mol/L in H 2 SO 4  + glucose leaching system. Similar results (96% Co and 100% Li) can be obtained in H 2 SO 4  + sucrose leaching system under optimized leaching conditions. Despite a complete leaching of Li (∼100%), only 54% Co can be dissolved in the H 2 SO 4  + cellulose leaching system under optimized leaching conditions. Finally, different characterization methods, including UV-Vis, FT-IR, SEM and XRD, were employed for the tentative exploration of reductive leaching reactions using organic as reductant in sulfuric acid medium. All the leaching and characterization results confirm that both glucose and sucrose are effective reductants during leaching, while cellulose should be further degraded to organics with low molecular weights to achieve a satisfactory leaching performance. Copyright © 2018 Elsevier Ltd. All rights reserved.

Advanced Biotelemetry Systems for Space Life Sciences: PH Telemetry

NASA Technical Reports Server (NTRS)

Hines, John W.; Somps, Chris; Ricks, Robert; Kim, Lynn; Connolly, John P. (Technical Monitor)

1995-01-01

The SENSORS 2000! (S2K!) program at NASA's Ames Research Center is currently developing a biotelemetry system for monitoring pH and temperature in unrestrained subjects. This activity is part of a broader scope effort to provide an Advanced Biotelemetry System (ABTS) for use in future space life sciences research. Many anticipated research endeavors will require biomedical and biochemical sensors and related instrumentation to make continuous inflight measurements in a variable-gravity environment. Since crew time is limited, automated data acquisition, data processing, data storage, and subject health monitoring are required. An automated biochemical and physiological data acquisition system based on non invasive or implantable biotelemetry technology will meet these requirements. The ABTS will ultimately acquire a variety of physiological measurands including temperature, biopotentials (e.g. ECG, EEG, EMG, EOG), blood pressure, flow and dimensions, as well as chemical and biological parameters including pH. Development activities are planned in evolutionary, leveraged steps. Near-term activities include 1) development of a dual channel pH/temperature telemetry system, and 2) development of a low bandwidth, 4-channel telemetry system, that measures temperature, heart rate, pressure, and pH. This abstract describes the pH/temperature telemeter.

Reduction of verotoxigenic Escherichia coli in production of fermented sausages.

PubMed

Holck, Askild L; Axelsson, Lars; Rode, Tone Mari; Høy, Martin; Måge, Ingrid; Alvseike, Ole; L'abée-Lund, Trine M; Omer, Mohamed K; Granum, Per Einar; Heir, Even

2011-11-01

After a number of foodborne outbreaks of verotoxigenic Escherichia coli involving fermented sausages, some countries have imposed regulations on sausage production. For example, the US Food Safety and Inspection Service requires a 5 log(10) reduction of E. coli in fermented products. Such regulations have led to a number of studies on the inactivation of E. coli in fermented sausages by changing processing and post-processing conditions. Several factors influence the survival of E. coli such as pre-treatment of the meat, amount of NaCl, nitrite and lactic acid, water activity, pH, choice of starter cultures and addition of antimicrobial compounds. Also process variables like fermentation temperature and storage time play important roles. Though a large variety of different production processes of sausages exist, generally the reduction of E. coli caused by production is in the range 1-2 log(10). In many cases this may not be enough to ensure microbial food safety. By optimising ingredients and process parameters it is possible to increase E. coli reduction to some extent, but in some cases still other post process treatments may be required. Such treatments may be storage at ambient temperatures, specific heat treatments, high pressure processing or irradiation. HACCP analyses have identified the quality of the raw materials, low temperature in the batter when preparing the sausages and a rapid pH drop during fermentation as critical control points in sausage production. This review summarises the literature on the reduction verotoxigenic E. coli in production of fermented sausages. Copyright © 2011 Elsevier Ltd. All rights reserved.

Temperature effect on the structural stabilities and electronic properties of X22H28 (X=C, Si and Ge) nanocrystals: A first-principles study

NASA Astrophysics Data System (ADS)

Deng, Xiao-Lin; Zhao, Yu-Jun; Wang, Ya-Ting; Liao, Ji-Hai; Yang, Xiao-Bao

2016-12-01

Based on ab initio molecular dynamic simulations, we have theoretically investigated the structural stabilities and electronic properties of X22H28 (X=C, Si, and Ge) nanocrystals, as a function of temperature with consideration of vibrational entropy effects. To compare the relative stabilities of X22H28 isomers, the vibration free energies are obtained according to the calculated phonon spectrum, where the typical modes are shown to be dominant to the structural stabilities. In addition, there is a significant gap reduction as the temperature increases from 0 K to 300 K, where the decrements are 0.2 /0.5 /0.6eV for C/Si/Ge nanocrystals, respectively. The dependence of energy gap on the variance of bond length is also analyzed according to the corresponding atomic attributions to the HOMO and LUMO levels.

Survival of Salmonella during Drying of Fresh Ginger Root (Zingiber officinale) and Storage of Ground Ginger.

PubMed

Gradl, Dana R; Sun, Lingxiang; Larkin, Emily L; Chirtel, Stuart J; Keller, Susanne E

2015-11-01

The survival of Salmonella on fresh ginger root (Zingiber officinale) during drying was examined using both a laboratory oven at 51 and 60°C with two different fan settings and a small commercially available food dehydrator. The survival of Salmonella in ground ginger stored at 25 and 37°C at 33% (low) and 97% (high) relative humidity (RH) was also examined. To inoculate ginger, a four-serovar cocktail of Salmonella was collected by harvesting agar lawn cells. For drying experiments, ginger slices (1 ± 0.5 mm thickness) were surface inoculated at a starting level of approximately 9 log CFU/g. Higher temperature (60°C) coupled with a slow fan speed (nonstringent condition) to promote a slower reduction in the water activity (aw) of the ginger resulted in a 3- to 4-log reduction in Salmonella populations in the first 4 to 6 h with an additional 2- to 3-log reduction by 24 h. Higher temperature with a higher fan speed (stringent condition) resulted in significantly less destruction of Salmonella throughout the 24-h period (P < 0.001). Survival appeared related to the rate of reduction in the aw. The aw also influenced Salmonella survival during storage of ground ginger. During storage at 97% RH, the maximum aw values were 0.85 at 25°C and 0.87 at 37°C; Salmonella was no longer detected after 25 and 5 days of storage, respectively, under these conditions. At 33% RH, the aw stabilized to approximately 0.35 at 25°C and 0.31 at 37°C. Salmonella levels remained relatively constant throughout the 365-day and 170-day storage periods for the respective temperatures. These results indicate a relationship between temperature and aw and the survival of Salmonella during both drying and storage of ginger.

Temperature- and Phase-Dependent Phonon Renormalization in 1T'-MoS2.

PubMed

Tan, Sherman Jun Rong; Sarkar, Soumya; Zhao, Xiaoxu; Luo, Xin; Luo, Yong Zheng; Poh, Sock Mui; Abdelwahab, Ibrahim; Zhou, Wu; Venkatesan, Thirumalai; Chen, Wei; Quek, Su Ying; Loh, Kian Ping

2018-05-22

Polymorph engineering of 2H-MoS 2 , which can be achieved by alkali metal intercalation to obtain either the mixed 2H/1T' phases or a homogeneous 1T' phase, has received wide interest recently, since this serves as an effective route to tune the electrical and catalytic properties of MoS 2 . As opposed to an idealized single crystal-to-single crystal phase conversion, the 2H to 1T' phase conversion results in crystal domain size reduction as well as strained lattices, although how these develop with composition is not well understood. Herein, the evolution of the phonon modes in Li-intercalated 1T'-MoS 2 (Li x MoS 2 ) are investigated as a function of different 1T'-2H compositions. We observed that the strain evolution in the mixed phases is revealed by the softening of four Raman modes, B g ( J 1 ), A g ( J 3 ), E 1 2g , and A 1g , with increasing 1T' phase composition. Additionally, the first-order temperature coefficients of the 1T' phonon mode vary linearly with increasing 1T' composition, which is explained by increased electron-phonon and strain-phonon coupling.

Analysis of Tank 38H (HTF-38-15-119, 127) Surface, Subsurface and Tank 43H (HTF-43-15-116, 117 and 118) Surface, Feed Pump Suction and Jet Suction Subsurface Supernatant Samples in Support of Enrichment, Corrosion Control and Salt Batch Planning Programs

DOE Office of Scientific and Technical Information (OSTI.GOV)

Oji, L.

Compositional feed limits have been established to ensure that a nuclear criticality event for the 2H and 3H Evaporators is not possible. The Enrichment Control Program (ECP) requires feed sampling to determine the equivalent enriched uranium content prior to transfer of waste other than recycle transfers (requires sampling to determine the equivalent enriched uranium at two locations in Tanks 38H and 43H every 26 weeks) The Corrosion Control Program (CCP) establishes concentration and temperature limits for key constituents and periodic sampling and analysis to confirm that waste supernate is within these limits. This report provides the results of analyses onmore » Tanks 38H and 43H surface and subsurface supernatant liquid samples in support of the ECP, the CCP, and the Salt Batch 10 Planning Program.« less

Reduction of selenite to elemental selenium by Enterobacter cloacae SLD1a-1

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dungan, R.S.; Frankenberger, W.T. Jr.

1998-11-01

The facultative anaerobic bacterium Enterobacter cloacae strain SLD1a-1 was studied in washed cell suspensions to assess optimal conditions required for the reduction of selenite (SeO{sub 3}{sup 2{minus}}) to elemental selenium (Se{sup 0}). Enterobacter cloacae using glucose (1.4 mM) as an electron donor removed 79% of the added SeO{sub 3}{sup 2{minus}} from solution in 2.5 h. Optimal SeO{sub 3}{sup 2{minus}} reduction occurred at a pH of 6.5 and a temperature of 40 C. Carbohydrate sources arabinose, xylose, and sorbose were found to significantly enhance SeO{sub 3}{sup 2{minus}} reduction over that of glucose. The reduction of SeO{sub 3}{sup 2{minus}} at 7.9 {micro}Mmore » was inhibited by nitrate of levels 1 to 100 times greater, nitrite at levels 5 and 10 times greater, while sulfite at levels of two to four times greater was found to stimulate the reduction of SeO{sub 3}{sup 2{minus}}. Enterobacter cloacae grows on anaerobically incubated plates containing NO{sub 3}{sup {minus}} as the sole terminal electron acceptor and acetate as the electron donor. Use of SeO{sub 3}{sup 2{minus}} as the terminal electron acceptor during anaerobic respiration did not support growth and could only be reduced to Se{sup 0} when NO{sub 3}{sup {minus}} was present.« less

Hydrometallurgical process for recovery of cobalt from waste cathodic active material generated during manufacturing of lithium ion batteries

NASA Astrophysics Data System (ADS)

Swain, Basudev; Jeong, Jinki; Lee, Jae-chun; Lee, Gae-Ho; Sohn, Jeong-Soo

The paper presents a new leaching-solvent extraction hydrometallurgical process for the recovery of a pure and marketable form of cobalt sulfate solution from waste cathodic active material generated during manufacturing of lithium ion batteries (LIBs). Leaching of the waste was carried out as a function of the leachant H 2SO 4 concentration, temperature, pulp density and reductant H 2O 2 concentration. The 93% of cobalt and 94% of lithium were leached at suitable optimum conditions of pulp density: 100 g L -1, 2 M H 2SO 4, 5 vol.% of H 2O 2, with a leaching time 30 min and a temperature 75 °C. In subsequent the solvent extraction study, 85.42% of the cobalt was recovered using 1.5 M Cyanex 272 as an extractant at an O/A ratio of 1.6 from the leach liquor at pH 5.00. The rest of the cobalt was totally recovered from the raffinate using 0.5 M of Cyanex 272 and an O/A ratio of 1, and a feed pH of 5.35. Then the co-extracted lithium was scrubbed from the cobalt-loaded organic using 0.1 M Na 2CO 3. Finally, the cobalt sulfate solution with a purity 99.99% was obtained from the cobalt-loaded organic by stripping with H 2SO 4.

Effects of Sulfation Level on the Desulfation Behavior of Presulfated Pt-BaO/Al2O3 Lean

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, D.; Szanyi, J; Kwak, J

2009-01-01

Desulfation by hydrogen of presulfated Pt (2 wt %)-BaO(20 wt %)/Al2O3 with various sulfur loading (S/Ba = 0.12, 0.31, and 0.62) were investigated by combining H2 temperature programmed reaction (TPRX), X-ray photoelectron spectroscopy (XPS), in situ sulfur K-edge X-ray absorption near-edge spectroscopy (XANES), and synchrotron time-resolved X-ray diffraction (TR-XRD) techniques. We find that the amount of H2S desorbed during the desulfation in the H2 TPRX experiments is not proportional to the amount of initial sulfur loading. The results of both in situ sulfur K-edge XANES and TR-XRD show that at low sulfur loadings, sulfates were transformed to a BaS phasemore » and remained in the catalyst rather than being removed as H2S. On the other hand, when the deposited sulfur level exceeded a certain threshold (at least S/Ba = 0.31) sulfates were reduced to form H2S, and the relative amount of the residual sulfide species in the catalyst was much less than at low sulfur loading. Unlike samples with high sulfur loading (e.g., S/Ba = 0.62), H2O did not promote the desulfation for the sample with S/Ba of 0.12, implying that the formed BaS species originating from the reduction of sulfates at low sulfur loading are more stable to hydrolysis. The results of this combined spectroscopy investigation provide clear evidence to show that sulfates at low sulfur loadings are less likely to be removed as H2S and have a greater tendency to be transformed to BaS on the material, leading to the conclusion that desulfation behavior of Pt-BaO/Al2O3 lean NOx trap catalysts is markedly dependent on the sulfation levels.« less

Kinetic Coupling of Water Splitting and Photoreforming on SrTiO 3 -Based Photocatalysts

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sanwald, Kai E.; Berto, Tobias F.; Jentys, Andreas

Coupling the anodic half-reactions of overall water splitting and oxygenate photoreforming (i.e., proton reduction and oxygenate oxidations) on Al-doped SrTiO3 decorated with a co-catalyst enables efficient photocatalytic H2 generation along with oxygenate conversion without accumulating undesired intermediates such as formaldehyde. The net H2-evolution rates result from the interplay between water oxidation, oxygenate oxidation, and the back-reaction of H2 and O2 to water. When the latter pathway is quantitatively suppressed (e.g., on RhCrOx co-catalyst or in excess of oxygenated hydrocarbons), the initial H2-evolution rates are independent of the oxygenate nature and concentration. This is a consequence of the reduction equivalents formore » H2-evolution provided by water oxidation compensating changes in the rates of oxygenate conversion. Thus, under conditions of suppressed back-reaction, water and oxygenate oxidations have equal quantum efficiencies. The selectivities to water and oxygenate oxidation depend on oxygenate nature and concentration. Transformations mediated by indirect hole transfer dominate as a result of the water oxidation at the anode and the associated intermediates generated in O2-evolution catalysis (e.g. ·OH, ·O and ·OOH). On the undecorated semiconductor, the O2 produced during overall water splitting is reductively activated to participate in glycerol oxidation without consuming evolved H2. Acknowledgements The authors would like to thank ESRF in Grenoble, France, for providing beam time at the ID26 station for XAFS experiments. K.E.S. gratefully acknowledges financial support by the Fond der Chemischen Industrie (FCI). J.A.L. and O.Y.G. acknowledge support for his contribution by the Laboratory Directed Research and Development Program at Pacific Northwest National Laboratory, a multi-program national laboratory operated by Battelle for the U.S. Department of Energy. The authors thank Xaver Hecht for BET measurements, Martin Neukamm for SEM and AAS measurements and Dr. Udishnu Sanyal for TEM imaging. Christine Schwarz is acknowledged for technical assistance in NMR experiments.« less

Reduction of ferrylmyoglobin by hydrogen sulfide. Kinetics in relation to meat greening.

PubMed

Libardi, Silvia H; Pindstrup, Helene; Cardoso, Daniel R; Skibsted, Leif H

2013-03-20

The hypervalent meat pigment ferrylmyoglobin, MbFe(IV)═O, characteristic for oxidatively stressed meat and known to initiate protein cross-linking, was found to be reduced by hydrogen sulfide to yield sulfmyoglobin. Horse heart myoglobin, void of cysteine, was used to avoid possible interference from protein thiols. For aqueous solution, the reactions were found to be second-order, and an apparent acid catalysis could be quantitatively accounted for in terms of a fast reaction between protonated ferrylmyoglobin, MbFe(IV)═O,H(+), and hydrogen sulfide, H2S (k2 = (2.5 ± 0.1) × 10(6) L mol(-1) s(-1) for 25.0 °C, ionic strengh 0.067, dominating for pH < 4), and a slow reaction between MbFe(IV)═O and HS(-) (k2 = (1.0 ± 0.7) × 10(4) L mol(-1) s(-1) for 25.0 °C, ionic strengh 0.067, dominating for pH > 7). For meat pH, a reaction via the transition state {MbFe(IV)═O···H···HS}([symbol: see text]) contributed significantly, and this reaction appeared almost independent of temperature with an apparent energy of activation of 2.1 ± 0.7 kJ mol(-1) at pH 7.4, as a result of compensation among activation energies and temperature influence on pKa values explaining low temperature greening of meat.

[Catalytic combustion of soot on combined oxide catalysts].

PubMed

He, Xu-wen; Yu, Jun-jie; Kang, Shou-fang; Hao, Zheng-ping; Hu, Chun

2005-01-01

Combined oxide catalysts are prepared for catalytic combustion of soot and regeneration from diesel emissions. Thermo-gravimetric analysis(TGA) and temperature programmed oxidation(TPO)are used to evaluate the activity of catalysts under the influence of composition,atomic ration, H2O, calcinations temperature and mass ration between catalysts and soot. Results show that Cu-Mo-O had high activity among double metal oxide catalysts. Among multicomponent metal oxide catalysts, Cu-K-Mo-O had high activity when atomic ratio Cu: K: Mo = 1:1:2 and mass ration between catalysts and soot equals 5: 1. Under this condition, soot ignition temperature of Cu-K-Mo-O catalyst was 327 degrees C. H2O addition and calcinations temperature had little influence on it,which is one kind of compatible catalyst for soot control and catalytic regeneration from diesel emissions.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gunnarsson, Fredrik; Pihl, Josh A.; Toops, Todd J.

This paper focuses on the activity for lean NO x reduction over sol-gel synthesized silver alumina (Ag/Al 2O 3) catalysts, with and without platinum doping, using ethanol (EtOH), EtOH/C 3H 6 and EtOH/gasoline blends as reducing agents. The effect of ethanol concentration, both by varying the hydrocarbon-to-NO x ratio and by alternating the gasoline concentration in the EtOH/gasoline mixture, is investigated. High activity for NO x reduction is demonstrated for powder catalysts for EtOH and EtOH/C 3H 6 as well as for monolith coated catalysts (EtOH and EtOH/gasoline). The results show that pure Ag/Al 2O 3 catalysts display higher NOmore » x reduction and lower light-off temperature as compared to the platinum doped samples. The 4 wt.% Ag/Al 2O 3 catalyst displays 100% reduction in the range 340–425 °C, with up to 37% selectivity towards NH 3. These results are also supported by DRIFTS (Diffuse reflection infrared Fourier transform spectroscopy) experiments. Finally, the high ammonia formation could, in combination with an NH 3-SCR catalyst, be utilized to construct a NO x reduction system with lower fuel penalty cf. stand alone HC-SCR. In addition, it would result in an overall decrease in CO 2 emissions.« less

Effects of temperature and gas-liquid mass transfer on the operation of small electrochemical cells for the quantitative evaluation of CO2 reduction electrocatalysts.

PubMed

Lobaccaro, Peter; Singh, Meenesh R; Clark, Ezra Lee; Kwon, Youngkook; Bell, Alexis T; Ager, Joel W

2016-09-29

In the last few years, there has been increased interest in electrochemical CO 2 reduction (CO2R). Many experimental studies employ a membrane separated, electrochemical cell with a mini H-cell geometry to characterize CO2R catalysts in aqueous solution. This type of electrochemical cell is a mini-chemical reactor and it is important to monitor the reaction conditions within the reactor to ensure that they are constant throughout the study. We show that operating cells with high catalyst surface area to electrolyte volume ratios (S/V) at high current densities can have subtle consequences due to the complexity of the physical phenomena taking place on electrode surfaces during CO2R, particularly as they relate to the cell temperature and bulk electrolyte CO 2 concentration. Both effects were evaluated quantitatively in high S/V cells using Cu electrodes and a bicarbonate buffer electrolyte. Electrolyte temperature is a function of the current/total voltage passed through the cell and the cell geometry. Even at a very high current density, 20 mA cm -2 , the temperature increase was less than 4 °C and a decrease of <10% in the dissolved CO 2 concentration is predicted. In contrast, limits on the CO 2 gas-liquid mass transfer into the cells produce much larger effects. By using the pH in the cell to measure the CO 2 concentration, significant undersaturation of CO 2 is observed in the bulk electrolyte, even at more modest current densities of 10 mA cm -2 . Undersaturation of CO 2 produces large changes in the faradaic efficiency observed on Cu electrodes, with H 2 production becoming increasingly favored. We show that the size of the CO 2 bubbles being introduced into the cell is critical for maintaining the equilibrium CO 2 concentration in the electrolyte, and we have designed a high S/V cell that is able to maintain the near-equilibrium CO 2 concentration at current densities up to 15 mA cm -2 .

Effects of temperature and gas–liquid mass transfer on the operation of small electrochemical cells for the quantitative evaluation of CO 2 reduction electrocatalysts

DOE PAGES

Lobaccaro, Peter; Singh, Meenesh R.; Clark, Ezra Lee; ...

2016-09-06

In the last few years, there has been increased interest in electrochemical CO 2 reduction (CO2R). Many experimental studies employ a membrane separated, electrochemical cell with a mini H-cell geometry to characterize CO2R catalysts in aqueous solution. This type of electrochemical cell is a mini-chemical reactor and it is important to monitor the reaction conditions within the reactor to ensure that they are constant throughout the study. Here we show that operating cells with high catalyst surface area to electrolyte volume ratios (S/V) at high current densities can have subtle consequences due to the complexity of the physical phenomena takingmore » place on electrode surfaces during CO2R, particularly as they relate to the cell temperature and bulk electrolyte CO 2 concentration. Both effects were evaluated quantitatively in high S/V cells using Cu electrodes and a bicarbonate buffer electrolyte. Electrolyte temperature is a function of the current/total voltage passed through the cell and the cell geometry. Even at a very high current density, 20 mA cm -2 , the temperature increase was less than 4 °C and a decrease of < 10% in the dissolved CO 2 concentration is predicted. In contrast, limits on the CO 2 gas-liquid mass transfer into the cells produce much larger effects. By using the pH in the cell to measure the CO 2 concentration, significant undersaturation of CO 2 is observed in the bulk electrolyte, even at more modest current densities of 10 mA cm -2 . Undersaturation of CO 2 produces large changes in the faradaic efficiency observed on Cu electrodes, with H 2 production becoming increasingly favored. Finally, we show that the size of the CO 2 bubbles being introduced into the cell is critical for maintaining the equilibrium CO 2 concentration in the electrolyte, and we have designed a high S/V cell that is able to maintain the near-equilibrium CO 2 concentration at current densities up to 15 mA cm -2.« less

Effects of temperature and gas–liquid mass transfer on the operation of small electrochemical cells for the quantitative evaluation of CO 2 reduction electrocatalysts

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lobaccaro, Peter; Singh, Meenesh R.; Clark, Ezra Lee

In the last few years, there has been increased interest in electrochemical CO 2 reduction (CO2R). Many experimental studies employ a membrane separated, electrochemical cell with a mini H-cell geometry to characterize CO2R catalysts in aqueous solution. This type of electrochemical cell is a mini-chemical reactor and it is important to monitor the reaction conditions within the reactor to ensure that they are constant throughout the study. Here we show that operating cells with high catalyst surface area to electrolyte volume ratios (S/V) at high current densities can have subtle consequences due to the complexity of the physical phenomena takingmore » place on electrode surfaces during CO2R, particularly as they relate to the cell temperature and bulk electrolyte CO 2 concentration. Both effects were evaluated quantitatively in high S/V cells using Cu electrodes and a bicarbonate buffer electrolyte. Electrolyte temperature is a function of the current/total voltage passed through the cell and the cell geometry. Even at a very high current density, 20 mA cm -2 , the temperature increase was less than 4 °C and a decrease of < 10% in the dissolved CO 2 concentration is predicted. In contrast, limits on the CO 2 gas-liquid mass transfer into the cells produce much larger effects. By using the pH in the cell to measure the CO 2 concentration, significant undersaturation of CO 2 is observed in the bulk electrolyte, even at more modest current densities of 10 mA cm -2 . Undersaturation of CO 2 produces large changes in the faradaic efficiency observed on Cu electrodes, with H 2 production becoming increasingly favored. Finally, we show that the size of the CO 2 bubbles being introduced into the cell is critical for maintaining the equilibrium CO 2 concentration in the electrolyte, and we have designed a high S/V cell that is able to maintain the near-equilibrium CO 2 concentration at current densities up to 15 mA cm -2.« less

Microbial reduction of Fe(III) in acidic sediments: isolation of Acidiphilium cryptum JF-5 capable of coupling the reduction of Fe(III) to the oxidation of glucose.

PubMed

Küsel, K; Dorsch, T; Acker, G; Stackebrandt, E

1999-08-01

To evaluate the microbial populations involved in the reduction of Fe(III) in an acidic, iron-rich sediment, the anaerobic flow of supplemental carbon and reductant was evaluated in sediment microcosms at the in situ temperature of 12 degrees C. Supplemental glucose and cellobiose stimulated the formation of Fe(II); 42 and 21% of the reducing equivalents that were theoretically obtained from glucose and cellobiose, respectively, were recovered in Fe(II). Likewise, supplemental H(2) was consumed by acidic sediments and yielded additional amounts of Fe(II) in a ratio of approximately 1:2. In contrast, supplemental lactate did not stimulate the formation of Fe(II). Supplemental acetate was not consumed and inhibited the formation of Fe(II). Most-probable-number estimates demonstrated that glucose-utilizing acidophilic Fe(III)-reducing bacteria approximated to 1% of the total direct counts of 4', 6-diamidino-2-phenylindole-stained bacteria. From the highest growth-positive dilution of the most-probable-number series at pH 2. 3 supplemented with glucose, an isolate, JF-5, that could dissimilate Fe(III) was obtained. JF-5 was an acidophilic, gram-negative, facultative anaerobe that completely oxidized the following substrates via the dissimilation of Fe(III): glucose, fructose, xylose, ethanol, glycerol, malate, glutamate, fumarate, citrate, succinate, and H(2). Growth and the reduction of Fe(III) did not occur in the presence of acetate. Cells of JF-5 grown under Fe(III)-reducing conditions formed blebs, i.e., protrusions that were still in contact with the cytoplasmic membrane. Analysis of the 16S rRNA gene sequence of JF-5 demonstrated that it was closely related to an Australian isolate of Acidiphilium cryptum (99.6% sequence similarity), an organism not previously shown to couple the complete oxidation of sugars to the reduction of Fe(III). These collective results indicate that the in situ reduction of Fe(III) in acidic sediments can be mediated by heterotrophic Acidiphilium species that are capable of coupling the reduction of Fe(III) to the complete oxidation of a large variety of substrates including glucose and H(2).

Plasma Discharge with Different Electrode Diameters for Reducing Methylene Blue Concentration

NASA Astrophysics Data System (ADS)

Rasyidah, H.; Kusumandari; Saraswati, T. E.; Anwar, M.

2018-03-01

Recently, plasma technology has gained attention since it overcomes the shortcomings of water treatment. This research studies the effect of electrode diameter of plasma discharge reactors on the concentration reduction of methylene blue as an organic solution. The plasma discharge reactor was built from a pair of stainless needle electrodes connected with high-AC voltage. The electrodes were placed approximately 2 mm above the solution and stirred at 5.5 rpm. The diameters of the electrodes were 2, 3.2 and 4 mm. The times for plasma treatment were set at 2, 4, 6, 8 and 10 min. Absorbance, temperature and pH of the solution were measured to know the effects of electrode diameter of the plasma reactor. Absorbance and pH significantly decreased after plasma treatment. The best of the absorbance reduction were obtained when the sample was treated under plasma discharge using the smallest diameter electrodes for 8-10 min.

Efficacy of vacuum steam pasteurization for inactivation of Salmonella PT 30, Escherichia coli O157:H7 and Enterococcus faecium on low moisture foods.

PubMed

Shah, Manoj K; Asa, Gladys; Sherwood, Julie; Graber, Kari; Bergholz, Teresa M

2017-03-06

Low moisture foods such as nuts, spices, and seeds have been implicated in several outbreaks due to Salmonella or E. coli O157:H7 contamination. Such foods may be consumed raw, and can be used as ingredients in other food products. While numerous thermal inactivation studies have been conducted for Salmonella on nuts, studies on other seeds and grains are minimal. Product water activity can influence the thermal resistance of pathogens, where thermal resistance increases as water activity decreases, leading to a requirement for higher temperatures and longer exposure times to achieve significant reduction of pathogen numbers. Vacuum steam pasteurization uses steam under vacuum, which can be operated at temperatures above and below 100°C. The objective of this study was to determine the efficacy of vacuum steam pasteurization for inactivation of pathogens on whole flaxseed, quinoa, sunflower kernels, milled flaxseed and whole black peppercorns. The use of E. faecium as a potential surrogate for Salmonella and E. coli O157:H7 in vacuum steam pasteurization was also evaluated. Pasteurization for 1min at 75°C yielded average log reductions of 5.48±1.22, 5.71±0.40 and 5.23±0.61 on flaxseed, 4.29±0.92, 5.89±0.26 and 2.39±0.83 on quinoa, and 4.01±0.74, 5.40±0.83 and 2.99±0.92 on sunflower kernels for Salmonella PT 30, E. coli O157:H7 and E. faecium, respectively. Similarly, on milled flaxseed and black peppercorns average log reductions of 3.02±0.79 and 6.10±0.64CFU/g were observed for Salmonella PT 30 after 1min of treatment at 75°C but, on average, >6.0 log reductions were observed after pasteurization at 85°C. Our data demonstrate that vacuum steam pasteurization can be effectively used to reduce pathogens on these low moisture foods at temperature as low as 75 and 85°C, and that E. faecium may be used as a potential surrogate for Salmonella PT 30 and E. coli O157:H7. Copyright © 2017 Elsevier B.V. All rights reserved.

The role of support morphology on the performance of Cu/ZnO-catalyst for hydrogenation of CO{sub 2} to methanol

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tasfy, Sara Faiz Hanna, E-mail: miss25208@gmail.com; Zabidi, Noor Asmawati Mohd, E-mail: noorasmawati-mzabidi@petronas.com.my; Shaharun, Maizatul Shima, E-mail: maizats@petronas.com.my

The effects of SBA-15 support morphology on the activity of Cu/ZnO catalyst in the hydrogenation of CO{sub 2} to methanol was investigated. In the hydrogenation of CO{sub 2} to methanol at 210°C, 2.25 MPa, H{sub 2}/CO{sub 2} ratio of three remarkable difference was obtained using Cu/ZnO catalyst supported on SBA-15 with different morphology. The catalysts were characterized using N{sub 2}-adsorption, field emission scanning microscopy (FESEM/EDX), transmission electron microscopy (HRTEM), and temperature-programmed reduction (TPR). Characterization of the catalyst showed that support morphology, surface area, metals dispersion, and reducibility influenced the catalytic performance. On the fiber-shaped SBA-15, copper dispersion was 29 % whereasmore » on the spherical-shaped SBA-15, the dispersion was 20 %. The experimental results showed that the catalyst supported over fiber-shaped SBA-15 exhibit higher CO{sub 2} conversion (13.96 %) and methanol selectivity (91.32 %) compare to catalyst supported over spherical-shaped SBA-15.« less

Inactivation and UV Disinfection of Murine Norovirus with TiO2 under Various Environmental Conditions▿

PubMed Central

Lee, JungEun; Zoh, KyungDuk; Ko, GwangPyo

2008-01-01

We studied inactivation and UV disinfection of murine norovirus (MNV) as a surrogate for human norovirus. We investigated the effects of different surface characteristics, temperatures, and NaCl concentrations on MNV survival using both a plaque assay and a real-time TaqMan reverse transcription (RT)-PCR assay. MNV survived more than 40 days on diaper material, on gauze, and in a stool suspension. Compared to inactivation at lower temperatures (−20 and 4°C), inactivation of MNV was greater at higher temperatures (18 and 30°C). On the surface of both gauze and diaper material, there was a <2-log10 reduction in the amount of infectious MNV in 40 days after incubation at both −20 and 4°C, compared to a >5-log10 reduction after incubation at 30°C in 24 days. MNV survived better in a stool suspension than on the surface of gauze or diaper material. A higher salt concentration increased the rate of inactivation of MNV. In 72 h, <0.3-, 1.5-, and 2.5-log10 reductions in the amount of infectious MNV occurred in distilled water and 0.5 and 1 M NaCl, respectively. We observed only minor reductions in the numbers of viral RNA copies as quantified by real-time TaqMan RT-PCR regardless of the temperature, the salt concentration, or the suspending medium. We also evaluated UV disinfection of infectious MNV with and without TiO2. The amount of MNV was significantly reduced by 254-nm UV with and without TiO2. When 25 mJ/cm2 UV was used, 3.3- and 3.6-log10 reductions in the amounts of infectious MNV occurred with and without TiO2, respectively. Our results demonstrate that MNV can persist in various environmental conditions and can be efficiently controlled by UV disinfection. PMID:18245239

Iodide-Photocatalyzed Reduction of Carbon Dioxide to Formic Acid with Thiols and Hydrogen Sulfide.

PubMed

Berton, Mateo; Mello, Rossella; González-Núñez, María Elena

2016-12-20

The photolysis of iodide anions promotes the reaction of carbon dioxide with hydrogen sulfide or thiols to quantitatively yield formic acid and sulfur or disulfides. The reaction proceeds in acetonitrile and aqueous solutions, at atmospheric pressure and room temperature by irradiation using a low-pressure mercury lamp. This transition-metal-free photocatalytic process for CO 2 capture coupled with H 2 S removal may have been relevant as a prebiotic carbon dioxide fixation. © 2016 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Frost-weathering on Mars - Experimental evidence for peroxide formation

NASA Technical Reports Server (NTRS)

Huguenin, R. L.; Miller, K. J.; Harwood, W. S.

1979-01-01

The weathering of silicates by frost is investigated in relation to the formation of surface peroxides to which Viking biology experiment results have been attributed. Samples of the minerals olivine and pyroxene were exposed to water vapor at -11 to -22 C and resultant gas evolution and pH were monitored. Experiments reveal the formation of an acidic oxidant upon interaction of the mineral and H2O frost at subfreezing temperatures, which chemical indicators have suggested to be chemisorbed hydrogen peroxide. A model for the formation of chemisorbed peroxide based on the chemical reduction of the mineral by surface frost is proposed, and it is predicted that the perioxide would decay at high temperatures to H2O and adsorbed O, consistent with the long-term storage and sterilization behavior of the soil oxidants observed in the Viking Gas Exchange and Labeled Release experiments.

Influence of TiO2 hollow sphere size on its photo-reduction activity for toxic Cr(VI) removal.

PubMed

Cai, Jiabai; Wu, Xueqing; Zheng, Fengying; Li, Shunxing; Wu, Yaling; Lin, Yanping; Lin, Liting; Liu, Biwen; Chen, Qiaoying; Lin, Luxiu

2017-03-15

After polystyrene@titanium dioxide (PS@TiO 2 ) composite with different size was calcined at designated temperature, TiO 2 hollow sphere with controllable size was obtained for high efficient photo-reduction of Cr(VI). The feature of the TiO 2 hollow sphere was investigated by SEM, TEM, XRD, UV-Vis, and photoluminescence. The photo-reduction of Cr(VI) were measured for the performance assessment of the TiO 2 hollow sphere, Cr(VI) was used as an electron acceptor. After irradiation for 2h, the photo-reduction rate of Cr(VI) (pH=2.82) for TiO 2 (450nm) was 96%, which exhibited an increase of 5% and 8% compared with TiO 2 (370nm) and TiO 2 (600nm). The absorption edges of TiO 2 hollow sphere (450nm) was largest with the increasing of hollow sphere size from 370 to 600nm. The optimal hollow sphere size of TiO 2 was 450nm for the photo-reduction of Cr(VI), because the light-harvesting efficiency (the best of absorption edge) and photo-generated electron-hole separation rate (the best of photo-reduction rate) of TiO 2 hollow sphere were controlled by its hollow sphere size. In addition, we find that the behavior of the hydrogen production was inhibited by the coexistence Cr(VI) solution. This study can improve our understanding of the mechanism for the activity enhancement by the optimal hollow sphere size of TiO 2 . Copyright © 2016 Elsevier Inc. All rights reserved.

Hydrogen desorption from hydrogen fluoride and remote hydrogen plasma cleaned silicon carbide (0001) surfaces

DOE Office of Scientific and Technical Information (OSTI.GOV)

King, Sean W., E-mail: sean.king@intel.com; Tanaka, Satoru; Davis, Robert F.

2015-09-15

Due to the extreme chemical inertness of silicon carbide (SiC), in-situ thermal desorption is commonly utilized as a means to remove surface contamination prior to initiating critical semiconductor processing steps such as epitaxy, gate dielectric formation, and contact metallization. In-situ thermal desorption and silicon sublimation has also recently become a popular method for epitaxial growth of mono and few layer graphene. Accordingly, numerous thermal desorption experiments of various processed silicon carbide surfaces have been performed, but have ignored the presence of hydrogen, which is ubiquitous throughout semiconductor processing. In this regard, the authors have performed a combined temperature programmed desorptionmore » (TPD) and x-ray photoelectron spectroscopy (XPS) investigation of the desorption of molecular hydrogen (H{sub 2}) and various other oxygen, carbon, and fluorine related species from ex-situ aqueous hydrogen fluoride (HF) and in-situ remote hydrogen plasma cleaned 6H-SiC (0001) surfaces. Using XPS, the authors observed that temperatures on the order of 700–1000 °C are needed to fully desorb C-H, C-O and Si-O species from these surfaces. However, using TPD, the authors observed H{sub 2} desorption at both lower temperatures (200–550 °C) as well as higher temperatures (>700 °C). The low temperature H{sub 2} desorption was deconvoluted into multiple desorption states that, based on similarities to H{sub 2} desorption from Si (111), were attributed to silicon mono, di, and trihydride surface species as well as hydrogen trapped by subsurface defects, steps, or dopants. The higher temperature H{sub 2} desorption was similarly attributed to H{sub 2} evolved from surface O-H groups at ∼750 °C as well as the liberation of H{sub 2} during Si-O desorption at temperatures >800 °C. These results indicate that while ex-situ aqueous HF processed 6H-SiC (0001) surfaces annealed at <700 °C remain terminated by some surface C–O and Si–O bonding, they may still exhibit significant chemical reactivity due to the creation of surface dangling bonds resulting from H{sub 2} desorption from previously undetected silicon hydride and surface hydroxide species.« less

Controlled sp(2) Functionalization of Boron Doped Diamond as a Route for the Fabrication of Robust and Nernstian pH Electrodes.

PubMed

Ayres, Zoë J; Borrill, Alexandra J; Newland, Jonathan C; Newton, Mark E; Macpherson, Julie V

2016-01-05

The development of a voltammetric boron doped diamond (BDD) pH sensor is described. To obtain pH sensitivity, laser micromachining (ablation) is utilized to introduce controlled regions of sp(2) carbon into a high quality polycrystalline BDD electrode. The resulting sp(2) carbon is activated to produce electrochemically reducible quinone groups using a high temperature acid treatment, followed by anodic polarization. Once activated, no further treatment is required. The quinone groups show a linear (R(2) = 0.999) and Nernstian (59 mV/(pH unit)) pH-dependent reductive current-voltage response over a large analyzable pH range, from pH 2 to pH 12. Using the laser approach, it is possible to optimize sp(2) coverage on the BDD surface, such that a measurable pH response is recorded, while minimizing background currents arising from oxygen reduction reactions on sp(2) carbon in the potential region of interest. This enables the sensor to be used in aerated solutions, boding well for in situ analysis. The voltammetric response of the electrode is not compromised by the presence of excess metal ions such as Pb(2+), Cd(2+), Cu(2+), and Zn(2+). Furthermore, the pH sensor is stable over a 3 month period (the current time period of testing), can be stored in air between measurements, requires no reactivation of the surface between measurements, and can be reproducibly fabricated using the proposed approach. The efficacy of this pH sensor in a real-world sample is demonstrated with pH measurements in U.K. seawater.

Characterization of real gas properties for space shuttle main engine fuel turbine and performance calculations

NASA Technical Reports Server (NTRS)

Harloff, G. J.

1986-01-01

Real thermodynamic and transport properties of hydrogen, steam, the SSME mixture, and air are developed. The SSME mixture properties are needed for the analysis of the space shuttle main engine fuel turbine. The mixture conditions for the gases, except air, are presented graphically over a temperature range from 800 to 1200 K, and a pressure range from 1 to 500 atm. Air properties are given over a temperature range of 320 to 500 K, which are within the bounds of the thermodynamics programs used, in order to provide mixture data which is more easily checked (than H2/H2O). The real gas property variation of the SSME mixture is quantified. Polynomial expressions, needed for future computer analysis, for viscosity, Prandtl number, and thermal conductivity are given for the H2/H2O SSME fuel turbine mixture at a pressure of 305 atm over a range of temperatures from 950 to 1140 K. These conditions are representative of the SSME turbine operation. Performance calculations are presented for the space shuttle main engine (SSME) fuel turbine. The calculations use the air equivalent concept. Progress towards obtaining the capability to evaluate the performance of the SSME fuel turbine, with the H2/H2O mixture, is described.

Candida parapsilosis as a Potent Biocontrol Agent against Growth and Aflatoxin Production by Aspergillus Species

PubMed Central

Niknejad, F; Zaini, F; Faramarzi, MA; Amini, M; Kordbacheh, P; Mahmoudi, M; Safara, M

2012-01-01

Background: Aflatoxin contamination of food and feed stuff is a serious health problem and significant economic concerns. In the present study, the inhibitory effect of Candida parapsilosis IP1698 on mycelial growth and aflatoxin production in aflatoxigenic strains of Aspergillus species was investigated. Methods: Mycelial growth inhibitions of nine strains of aflatoxigenic and non-aflatoxigenic Aspergillus species in the presence of C. parapsilosis investigated by pour plate technique at different pH, temperature and time of incubation. Reduction of aflatoxin was evaluated in co-cultured fungi in yeast extract sucrose broth after seven days of incubation using HPLC method. The data were analyzed by SPSS 11.5. Results: The presence of the C. parapsilosis at different pH did not affect significantly the growth rate of Aspergillus isolates. On the other hand, temperature and time of incubation showed to be significantly effective when compared to controls without C. parapsilosis (P≤0.05). In aflatoxigenic strains, minimum percentage of reductions in total aflatoxin and B1, B2, G1, G2 fractions were 92.98, 92.54, 77.48, 54.54 and 72.22 and maximum percentage of reductions were 99.59, not detectable, 94.42, and not detectable in both G1 and G2, respectively. Conclusion: C. parapsilosis might employ as a good biocontrol agent against growth and aflatoxin production by aflatoxigenic Aspergillus species PMID:23308351

Lean NO x reduction over Ag/alumina catalysts via ethanol-SCR using ethanol/gasoline blends

DOE PAGES

Gunnarsson, Fredrik; Pihl, Josh A.; Toops, Todd J.; ...

2016-09-04

This paper focuses on the activity for lean NO x reduction over sol-gel synthesized silver alumina (Ag/Al 2O 3) catalysts, with and without platinum doping, using ethanol (EtOH), EtOH/C 3H 6 and EtOH/gasoline blends as reducing agents. The effect of ethanol concentration, both by varying the hydrocarbon-to-NO x ratio and by alternating the gasoline concentration in the EtOH/gasoline mixture, is investigated. High activity for NO x reduction is demonstrated for powder catalysts for EtOH and EtOH/C 3H 6 as well as for monolith coated catalysts (EtOH and EtOH/gasoline). The results show that pure Ag/Al 2O 3 catalysts display higher NOmore » x reduction and lower light-off temperature as compared to the platinum doped samples. The 4 wt.% Ag/Al 2O 3 catalyst displays 100% reduction in the range 340–425 °C, with up to 37% selectivity towards NH 3. These results are also supported by DRIFTS (Diffuse reflection infrared Fourier transform spectroscopy) experiments. Finally, the high ammonia formation could, in combination with an NH 3-SCR catalyst, be utilized to construct a NO x reduction system with lower fuel penalty cf. stand alone HC-SCR. In addition, it would result in an overall decrease in CO 2 emissions.« less

AqSo_NaCl: Computer program to calculate p-T-V-x properties in the H2O-NaCl fluid system applied to fluid inclusion research and pore fluid calculation

NASA Astrophysics Data System (ADS)

Bakker, Ronald J.

2018-06-01

The program AqSo_NaCl has been developed to calculate pressure - molar volume - temperature - composition (p-V-T-x) properties, enthalpy, and heat capacity of the binary H2O-NaCl system. The algorithms are designed in BASIC within the Xojo programming environment, and can be operated as stand-alone project with Macintosh-, Windows-, and Unix-based operating systems. A series of ten self-instructive interfaces (modules) are developed to calculate fluid inclusion properties and pore fluid properties. The modules may be used to calculate properties of pure NaCl, the halite-liquidus, the halite-vapourus, dew-point and bubble-point curves (liquid-vapour), critical point, and SLV solid-liquid-vapour curves at temperatures above 0.1 °C (with halite) and below 0.1 °C (with ice or hydrohalite). Isochores of homogeneous fluids and unmixed fluids in a closed system can be calculated and exported to a.txt file. Isochores calculated for fluid inclusions can be corrected according to the volumetric properties of quartz. Microthermometric data, i.e. dissolution temperatures and homogenization temperatures, can be used to calculated bulk fluid properties of fluid inclusions. Alternatively, in the absence of total homogenization temperature the volume fraction of the liquid phase in fluid inclusions can be used to obtain bulk properties.

Characterization of Mexican coriander (Eryngium foetidum) essential oil and its inactivation of Listeria monocytogenes in vitro and during mild thermal pasteurization of pineapple juice.

PubMed

Ngang, Jean J Essia; Nyegue, Maximilienne A; Ndoye, Foe C; Tchuenchieu Kamgain, Alex D; Sado Kamdem, Sylvain L; Lanciotti, Rosalba; Gardini, Fausto; Etoa, François-Xavier

2014-03-01

The aim of this work was to characterize the essential oil (EO) of Eryngium foetidum (EfEO) and assess its activity toward Listeria monocytogenes in broth and during thermal inactivation of the pathogen in pineapple juice. In this respect, EfEO was chemically characterized, and its antilisteria potential in broth as a function of pH, cell load, and EfEO concentration was assessed through a central composite design. Furthermore, the inactivation kinetics of L. monocytogenes in the juice were assessed by combining EfEO and low pasteurization temperatures. A total of 81 compounds were identified from EfEO. The reduction of pH and cell load increased EO activity. The use of only 15 ppm of EfEO during pasteurization of pineapple juice at 60°C reduced the time required for a 4-log reduction in L. monocytogenes CFU/ml by 74.9% (i.e., from 8.5 to 2.1 min) compared with treatment without EfEO. It could be concluded that EfEO activity toward L. monocytogenes increases with the reduction of pH and that it can be used at sublethal concentrations in combination with low temperatures in pineapple juice pasteurization. This study demonstrates that EO-assisted pasteurization is a promising strategy for the reduction of thermal impact during juice production. EfEO is easily available and compatible with many juices and is thus promising for industrial application.

Efficacy of a Community-Based Physical Activity Program KM2H2 for Stroke and Heart Attack Prevention among Senior Hypertensive Patients: A Cluster Randomized Controlled Phase-II Trial

PubMed Central

Gong, Jie; Chen, Xinguang; Li, Sijian

2015-01-01

Objective To evaluate the efficacy of the program Keep Moving toward Healthy Heart and Healthy Brain (KM2H2) in encouraging physical activities for the prevention of heart attack and stroke among hypertensive patients enrolled in the Community-Based Hypertension Control Program (CBHCP). Design Cluster randomized controlled trial with three waves of longitudinal assessments at baseline, 3 and 6 months post intervention. Setting Community-based and patient-centered self-care for behavioral intervention in urban settings of China. Participants A total of 450 participants diagnosed with hypertension from 12 community health centers in Wuhan, China were recruited, and were randomly assigned by center to receive either KM2H2 plus standard CBHCP care (6 centers and 232 patients) or the standard care only (6 centers and 218 patients). Intervention KM2H2 is a behavioral intervention guided by the Transtheoretical Model, the Model of Personalized Medicine and Social Capital Theory. It consists of six intervention sessions and two booster sessions engineered in a progressive manner. The purpose is to motivate and maintain physical activities for the prevention of heart attack and stroke. Outcome Measures Heart attack and stroke (clinically diagnosed, primary outcome), blood pressure (measured, secondary outcome), and physical activity (self-report, tertiary outcome) were assessed at the individual level during the baseline, 3- and 6-month post-intervention. Results Relative to the standard care, receiving KM2H2 was associated with significant reductions in the incidence of heart attack (3.60% vs. 7.03%, p < .05) and stroke (5.11% vs. 9.90%, p<0.05), and moderate reduction in blood pressure (-3.72mmHg in DBP and -2.92 mmHg in DBP) at 6-month post-intervention; and significant increases in physical activity at 3- (d = 0.53, 95% CI: 0.21, 0.85) and 6-month (d = 0.45, 95% CI: 0.04, 0.85) post-intervention, respectively. Conclusion The program KM2H2 is efficacious to reduce the risk of heart attack and stroke among senior patients who are on anti-hypertensive medication. Findings of this study provide solid data supporting a formal phase-III trial to establish the effectiveness of KM2H2 for use in community settings for prevention. Trial Registration ISRCTN Register ISRCTN12608966 PMID:26426421

Pt-Doped NiFe₂O₄ Spinel as a Highly Efficient Catalyst for H₂ Selective Catalytic Reduction of NO at Room Temperature.

PubMed

Sun, Wei; Qiao, Kai; Liu, Ji-Yuan; Cao, Li-Mei; Gong, Xue-Qing; Yang, Ji

2016-04-11

H2 selective catalytic reduction (H2-SCR) has been proposed as a promising technology for controlling NOx emission because hydrogen is clean and does not emit greenhouse gases. We demonstrate that Pt doped into a nickel ferrite spinel structure can afford a high catalytic activity of H2-SCR. A superior NO conversion of 96% can be achieved by employing a novel NiFe1.95Pt0.05O4 spinel-type catalyst at 60 °C. This novel catalyst is different from traditional H2-SCR catalysts, which focus on the role of metallic Pt species and neglect the effect of oxidized Pt states in the reduction of NO. The obtained Raman and XPS spectra indicate that Pt in the spinel lattice has different valence states with Pt(2+) occupying the tetrahedral sites and Pt(4+) residing in the octahedral ones. These oxidation states of Pt enhance the back-donation process, and the lack of filling electrons of the 5d band causes Pt to more readily hybridize with the 5σ orbital of the NO molecule, especially for octahedral Pt(4+), which enhances the NO chemisorption on the Pt sites. We also performed DFT calculations to confirm the enhancement of adsorption of NO onto Pt sites when doped into the Ni-Fe spinel structure. The prepared Pt/Ni-Fe catalysts indicate that increasing the dispersity of Pt on the surfaces of the individual Ni-Fe spinel-type catalysts can efficiently promote the H2-SCR activity. Our demonstration provides new insight into designing advanced catalysts for H2-SCR.

Survival of norovirus surrogate on various food-contact surfaces.

PubMed

Kim, An-Na; Park, Shin Young; Bae, San-Cheong; Oh, Mi-Hwa; Ha, Sang-Do

2014-09-01

Norovirus (NoV) is an environmental threat to humans, which spreads easily from one infected person to another, causing foodborne and waterborne diseases. Therefore, precautions against NoV infection are important in the preparation of food. The aim of this study was to investigate the survival of murine norovirus (MNV), as a NoV surrogate, on six different food-contact surfaces: ceramic, wood, rubber, glass, stainless steel, and plastic. We inoculated 10(5) PFU of MNV onto the six different surface coupons that were then kept at room temperature for 28 days. On the food-contact surfaces, the greatest reduction in MNV was 2.28 log10 PFU/coupon, observed on stainless steel, while the lowest MNV reduction was 1.29 log10 PFU/coupon, observed on wood. The rank order of MNV reduction, from highest to lowest, was stainless steel, plastic, rubber, glass, ceramic, and wood. The values of d R (time required to reduce the virus by 90%) on survival plots of MNV determined by a modified Weibull model were 277.60 h (R(2) = 0.99) on ceramic, 492.59 h (R(2) = 0.98) on wood, 173.56 h on rubber (R(2) = 0.98), 97.18 h (R(2) = 0.94) on glass, 91.76 h (R(2) = 0.97) on stainless steel, and 137.74 h (R(2) = 0.97) on plastic. The infectivity of MNV on all food-contact surfaces remained after 28 days. These results show that MNV persists in an infective state on various food-contact surfaces for long periods. This study may provide valuable information for the control of NoV on various food-contact surfaces, in order to prevent foodborne disease.

Thermal inactivation kinetics of Bacillus coagulans spores in tomato juice.

PubMed

Peng, Jing; Mah, Jae-Hyung; Somavat, Romel; Mohamed, Hussein; Sastry, Sudhir; Tang, Juming

2012-07-01

The thermal characteristics of the spores and vegetative cells of three strains of Bacillus coagulans (ATCC 8038, ATCC 7050, and 185A) in tomato juice were evaluated. B. coagulans ATCC 8038 was chosen as the target microorganism for thermal processing of tomato products due to its spores having the highest thermal resistance among the three strains. The thermal inactivation kinetics of B. coagulans ATCC 8038 spores in tomato juice between 95 and 115°C were determined independently in two different laboratories using two different heating setups. The results obtained from both laboratories were in general agreement, with z-values (z-value is defined as the change in temperature required for a 10-fold reduction of the D-value, which is defined as the time required at a certain temperature for a 1-log reduction of the target microorganisms) of 8.3 and 8.7°C, respectively. The z-value of B. coagulans 185A spores in tomato juice (pH 4.3) was found to be 10.2°C. The influence of environmental factors, including cold storage time, pH, and preconditioning, upon the thermal resistance of these bacterial spores is discussed. The results obtained showed that a storage temperature of 4°C was appropriate for maintaining the viability and thermal resistance of B. coagulans ATCC 8038 spores. Acidifying the pH of tomato juice decreased the thermal resistance of these spores. A 1-h exposure at room temperature was considered optimal for preconditioning B. coagulans ATCC 8038 spores in tomato juice.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Yang; Kidder, Michelle; Ruther, Rose E.

In this paper, we present a new class of catalysts, InMo-ZSM- 5, which can be prepared by indium impregnation of Mo-ZSM- 5. The incorporation of indium dramatically decreases coke formation during methane dehydroaromatization. The benzene and C 2 hydrocarbons selectivity among total hydrocarbons over InMo-ZSM- 5 remains comparable to that of Mo-ZSM- 5 despite reduced methane conversion due to decreased coke formation. We found 1 wt% indium to be optimal loading for reducing coke selectivity to half that of Mo-ZSM- 5. Characterization methods were not helpful in discerning the interaction of In with Mo but experiments with bimetallic 1In2Mo-ZSM- 5more » and mechanical mixture 1In+2Mo-ZSM- 5 suggest that In and Mo need to be in close proximity to suppress coke formation. Finally, this is supported by temperature programmed reduction experiments which show that In incorporation leads to lower Mo reduction temperature in In2Mo-ZMS- 5.« less

YLL056C from Saccharomyces cerevisiae encodes a novel protein with aldehyde reductase activity.

PubMed

Wang, Han-Yu; Xiao, Di-Fan; Zhou, Chang; Wang, Lin-Lu; Wu, Lan; Lu, Ya-Ting; Xiang, Quan-Ju; Zhao, Ke; Li, Xi; Ma, Meng -Gen

2017-06-01

The short-chain dehydrogenase/reductase (SDR) family, the largest family in dehydrogenase/reductase superfamily, is divided into "classical," "extended," "intermediate," "divergent," "complex," and "atypical" groups. Recently, several open reading frames (ORFs) were characterized as intermediate SDR aldehyde reductase genes in Saccharomyces cerevisiae. However, no functional protein in the atypical group has been characterized in S. cerevisiae till now. Herein, we report that an uncharacterized ORF YLL056C from S. cerevisiae was significantly upregulated under high furfural (2-furaldehyde) or 5-(hydroxymethyl)-2-furaldehyde concentrations, and transcription factors Yap1p, Hsf1p, Pdr1/3p, Yrr1p, and Stb5p likely controlled its upregulated transcription. This ORF indeed encoded a protein (Yll056cp), which was grouped into the atypical subgroup 7 in the SDR family and localized to the cytoplasm. Enzyme activity assays showed that Yll056cp is not a quinone or ketone reductase but an NADH-dependent aldehyde reductase, which can reduce at least seven aldehyde compounds. This enzyme showed the best Vmax, Kcat, and Kcat/Km to glycolaldehyde, but the highest affinity (Km) to formaldehyde. The optimum pH and temperature of this enzyme was pH 6.5 for reduction of glycolaldehyde, furfural, formaldehyde, butyraldehyde, and propylaldehyde, and 30 °C for reduction of formaldehyde or 35 °C for reduction of glycolaldehyde, furfural, butyraldehyde, and propylaldehyde. Temperature and pH affected stability of this enzyme and this influence varied with aldehyde substrate. Metal ions, salts, and chemical protective additives, especially at high concentrations, had different influence on enzyme activities for reduction of different aldehydes. This research provided guidelines for study of more uncharacterized atypical SDR enzymes from S. cerevisiae and other organisms.

Mechanism of H adatoms improving the O2 reduction reaction on the Zn-modified anatase TiO2 (101) surface studied by first principles calculation.

PubMed

Liu, Liangliang; Li, Chongyang; Jiang, Man; Li, Xiaodong; Huang, Xiaowei; Wang, Zhu; Jia, Yu

2018-06-05

First principles calculations were performed to cast insight into the mechanism of the improvement of O2 reduction reaction (ORR) activity by Zn and H interstitials on the anatase TiO2 (101) surface. For the Zn-modified anatase TiO2 (101) surface, both surface and subsurface Zn interstitials could contribute to O2 adsorption and dissociation, but the dissociation barriers of O2 molecules are still too high, which limits the ORR activity. After a H adatom is introduced onto the Zn-modified anatase TiO2 (101) surface, the highest energy barriers are greatly reduced compared with those of the Zn-modified surface. Meanwhile, it is observed that the dissociation barriers decrease almost linearly with the increase of the charge difference of adsorption O2 between initial and transition state configurations. Specifically, subsurface Zn and surface H interstitials facilitate O2 dissociation and subsequent oxidation reactions, and further frequency analysis shows that these dissociation processes are frequent even at the room temperature of 300 K. In a word, this work provides a theoretical support to design a high ORR activity catalyst of the TiO2 nanocrystal comparable to precious Pt catalysts.

High thermoelectricpower factor in graphene/hBN devices

PubMed Central

Duan, Junxi; Wang, Xiaoming; Lai, Xinyuan; Li, Guohong; Taniguchi, Takashi; Zebarjadi, Mona; Andrei, Eva Y.

2016-01-01

Fast and controllable cooling at nanoscales requires a combination of highly efficient passive cooling and active cooling. Although passive cooling in graphene-based devices is quite effective due to graphene’s extraordinary heat conduction, active cooling has not been considered feasible due to graphene’s low thermoelectric power factor. Here, we show that the thermoelectric performance of graphene can be significantly improved by using hexagonal boron nitride (hBN) substrates instead of SiO2. We find the room temperature efficiency of active cooling in the device, as gauged by the power factor times temperature, reaches values as high as 10.35 W⋅m−1⋅K−1, corresponding to more than doubling the highest reported room temperature bulk power factors, 5 W⋅m−1⋅K−1, in YbAl3, and quadrupling the best 2D power factor, 2.5 W⋅m−1⋅K−1, in MoS2. We further show that the Seebeck coefficient provides a direct measure of substrate-induced random potential fluctuations and that their significant reduction for hBN substrates enables fast gate-controlled switching of the Seebeck coefficient polarity for applications in integrated active cooling devices. PMID:27911824

Effects of MgO on the Reduction of Vanadium Titanomagnetite Concentrates with Char

NASA Astrophysics Data System (ADS)

Chen, Chao; Sun, TiChang; Wang, XiaoPing; Hu, TianYang

2017-10-01

The effects of MgO on the carbothermic reduction behavior of vanadium titanomagnetite concentrates (VTC) from Chengde, China, were investigated via temperature-programmed heating under nitrogen atmosphere in a sealed furnace. Gaseous product content was measured by using an infrared gas analyzer, and it was found that the addition of MgO to VTC with char decreased the reduction rate and reduction degree, and the utilization of CO in VTC reduction was also reduced. X-ray diffraction results showed that magnesium titanate (Mg2TiO4) was formed but FeTi2O5 was not observed in the VTC reduction process by adding 6 wt.% MgO, which can be explained by thermodynamic analysis. Scanning electron microscopy revealed that the enrichment of Mg in the unreacted core was the main reason that the further reduction of VTC was restricted. However, comparatively pure particles of Mg2TiO4 were generated, and the titanium and iron were separated well due to the combination of magnesium and titanium.

Escherichia coli O157:H7 reduction in hamburgers with regard to premature browning of minced beef, colour score and method for determining doneness.

PubMed

Boqvist, Sofia; Fernström, Lise-Lotte; Alsanius, Beatrix W; Lindqvist, Roland

2015-12-23

This study investigated the effect of premature browning (PMB) on the survival of Escherichia coli O157:H7 in beef hamburgers after cooking with respect to interior colour of the hamburger and recommendations to cook hamburgers to a core temperature of 71 °C. Assessment of doneness by visual inspection or measurement of internal temperature was compared in terms of survival and the increased relative risk of illness due to PMB was estimated. At the last consume-by-day, hamburgers made from minced meat packaged in 80/20 O2/CO2 (MAP hamburger) and from meat minced at retail packaged in atmospheric condition (control hamburger) were inoculated with a gfp-tagged strain of E. coli O157:H7 (E. coli O157:H7gfp+). Hamburgers were cooked for different times during assessment of the core temperature every 30s and cut in halves after cooking. Doneness was evaluated based on visual judgement of the internal colour using a score chart (C-score) from 'uncooked' (score 1) to 'tan with no evidence of pink' (score 5). An alternative five point score chart (TCC-score) including texture of the meat, clarity of meat juice and internal colour was also developed. Enumeration of viable E. coli O157:H7gfp+ in cooked hamburgers was based on fluorescent colonies recovered from plates. Results showed that MAP hamburgers developed PMB when compared with controls (P=0.0003) and that the shortest cooking time for the highest C-score was 6 and 11 min for MAP and control hamburgers, respectively. The mean temperature in the MAP hamburger was then 60.3 °C. The TCC-score reduced the difference between MAP and control hamburgers. It was also shown that the survival of E. coli O157:H7gfp+ was highest in MAP hamburgers. The predicted absolute risks for illness were highest for MAP hamburgers for all C-scores and the relative risk associated with PMB increased with doneness. For a C-score of 4 (slightly pink) the predicted relative risk for illness was 300 times higher for MAP hamburger than for controls. A variable pathogen reduction was observed when cooking hamburgers to temperatures of 70-76 °C (the 5th and 95th percentile range was around 3.3 log CFU). The lower reductions, at the 5th percentile, may, depending on initial contamination levels, not be enough to ensure sufficient and safe inactivation of E. coli O157:H7. Efforts to inform consumers about PMB in minced meat packaged in high oxygen packages (≥60% O2) are needed with the aim to make consumers use thermometers correctly or at least not determine doneness based only on meat colour. Copyright © 2015. Published by Elsevier B.V.

Laboratory Studies of Solid Carbon Dioxide in Planetary and Interstellar Ices

NASA Technical Reports Server (NTRS)

White, Douglas; Sandford, Scott A.; Mastrapa, Rachel M.

2012-01-01

Laboratory spectra have shown that CO2. is a powerful diagnostic tool for analyzing infrared data from remote observations, as it has been detected on icy moons in the outer solar system as well as dust grain surfaces in the interstellar medium. IR absorption profiles of CO2 wi thin ice mixtures containing H2O and CH30H change with respect to tem perature and mixture ratios. In this particular study, the CO2 stretch mode around 235O cm (exp -1) (4.3 rricrons) is systematically observ ed in different mixtures with H2O and CH30H in temperature ranges from 15K to 150 K, as well as vibrational modes in the near-IR such as th e combination bands near 3700 cm (exp -1) (2.7 microns) and 5080 (exp -1) (2.0 microns). Additionally, some high?temperature deposits (T > 50 K) of H2O, CH30H, and CO2 ice mixtures were performed to determine the maximum temperatures at which CO2 will deposit on the sample win dow. These data may then be used to interpret spectra obtained from remote IR observations. This research was sponsored by Oak Ridge Associ ated Universities (ORAU) through the NASA Postdoctoral Program (NPP) as well as Ames Research Center and the SETI institute who provided fa cilities and equipment.

Fundamental Studies on High Temperature Deformation, Recrystallization, and Grain Growth of Two-Phase Materials.

DTIC Science & Technology

1987-02-18

17 ml) Benzalkonium Chloride (50%) 4 35 ml Ethanol The Ti-V alloys were etched with the following ethant for about 10 sec. 4% HNO 3 2% HF Bal. H 0 2...that in the last *step all the alloys were processed in the ax+ 6 field from 973 0K L 0 (700 C). The amount of work given in this step (60% reduction in...interfaces (29). The interfaces move by random jumping of atoms from grain to grain, the driving force for the process being the reduction of free

Microbial processes and factors controlling their activities in alkaline lakes of the Mongolian plateau

NASA Astrophysics Data System (ADS)

Namsaraev, Zorigto B.; Zaitseva, Svetlana V.; Gorlenko, Vladimir M.; Kozyreva, Ludmila P.; Namsaraev, Bair B.

2015-11-01

A striking feature of the Mongolian plateau is the wide range of air temperatures during a year, -30 to 30°C. High summer temperatures, atmospheric weathering and the arid climate lead to formation of numerous alkaline soda lakes that are covered by ice during 6-7 months per year. During the study period, the lakes had pH values between 8.1 to 10.4 and salinity between 1.8 and 360 g/L. According to chemical composition, the lakes belong to sodium carbonate, sodium chloride-carbonate and sodium sulfate-carbonate types. This paper presents the data on the water chemical composition, results of the determination of the rates of microbial processes in microbial mats and sediments in the lakes studied, and the results of a Principal Component Analysis of environmental variables and microbial activity data. Temperature was the most important factor that influenced both chemical composition and microbial activity. pH and salinity are also important factors for the microbial processes. Dark CO2 fixation is impacted mostly by salinity and the chemical composition of the lake water. Total photosynthesis and sulfate-reduction are impacted mostly by pH. Photosynthesis is the dominant process of primary production, but the highest rate (386 mg C/(L•d)) determined in the lakes studied were 2-3 times lower than in microbial mats of lakes located in tropical zones. This can be explained by the relatively short warm period that lasts only 3-4 months per year. The highest measured rate of dark CO2 assimilation (59.8 mg C/(L•d)) was much lower than photosynthesis. The highest rate of sulfate reduction was 60 mg S/(L•d), while that of methanogenesis was 75.6 μL CN4/(L•d) in the alkaline lakes of Mongolian plateau. The rate of organic matter consumption during sulfate reduction was 3-4 orders of magnitude higher than that associated with methanogenesis.

Inactivation of Escherichia coli O157:H7 in moisture-enhanced nonintact beef by pan-broiling or roasting with various cooking appliances set at different temperatures.

PubMed

Shen, Cangliang; Geornaras, Ifigenia; Belk, Keith E; Smith, Gary C; Sofos, John N

2011-01-01

This study evaluated inactivation of Escherichia coli O157:H7 in moisture-enhanced restructured nonintact beef cooked to 65 °C using different cooking appliances set at different temperatures. Batches (2 kg) of coarse-ground beef (approximately 5% fat) were mixed with an 8-strain composite (100 mL) of rifampicin-resistant E. coli O157:H7 (6.4 ± 0.1 log CFU/g) and a solution (100 mL) of sodium chloride plus sodium tripolyphosphate to yield concentrations (wt/wt) of 0.5% and 0.25%, respectively, in the final product. Beef portions of 2.54 cm thickness (15 cm dia) were prepared and were vacuum-packaged and frozen (-20 °C, 42 h). Partially thawed (-2.5 ± 1.0 °C) portions were pan-broiled (Presto electric skillet and Sanyo grill) or roasted (Oster toaster oven and Magic Chef kitchen oven) to 65 °C. The appliances were set at, and preheated before cooking to 149 or 204 °C (electric skillet), 149 or 218 °C (grill), 149 or 232 °C (toaster oven), and 149, 204, or 260 °C (kitchen oven). Temperatures of appliances and beef samples were monitored with thermocouples, and meat samples were analyzed for surviving microbial populations. In general, the higher the appliance temperature setting, the shorter the time needed to reach 65 °C, and the higher the edge and surface temperatures of the meat samples. Temperatures of 204 to 260 °C, regardless of appliance, resulted in greater (P < 0.05) pathogen reductions (3.3 to 5.5 log CFU/g) than those obtained at 149 °C (1.5 to 2.4 log CFU/g). The highest (P < 0.05) reduction (5.5 log CFU/g) was obtained in samples cooked in the kitchen oven set at 260 °C. The results should be useful to the food service industry for selection of effective nonintact beef cooking protocols, and for use in risk assessments for nonintact meat products. Practical Application: Results of this study should be useful for developing cooking recommendations to enhance the safety of nonintact beef products, and for use in risk assessments of such products.

Application of immobilized nanotubular TiO(2) electrode for photocatalytic hydrogen evolution: reduction of hexavalent chromium (Cr(VI)) in water.

PubMed

Yoon, Jaekyung; Shim, Eunjung; Bae, Sanghyun; Joo, Hyunku

2009-01-30

In this study, immobilized TiO(2) electrode is applied to reduce toxic Cr(VI) to non-toxic Cr(III) in aqueous solution under UV irradiation. To overcome the limitation of powder TiO(2), a novel technique of immobilization based on anodization was applied and investigated under various experimental conditions. The anodization was performed at 20V-5 degrees C for 45min with 0.5% hydrofluoric acid, and then the anodized samples were annealed under oxygen stream in the range 450-850 degrees C. Based on the results of the experiments, the photocatalytic Cr(VI) reduction was favorable in acidic conditions, with approximately 98% of the Cr(VI) being reduced within 2h at pH 3. Among the samples tested under same anodizing condition, the nanotubular TiO(2) annealed at 450 and 550 degrees C showed highest reduction efficiencies of Cr(VI). In addition, the surface characterizations (zeta potential, XRD, and SEM) of these samples proved that the Cr(VI) reduction efficiency was higher under acidic conditions and at a lower annealing temperature. From this research, it was concluded that the anodized TiO(2) has the potential to be a useful technology for environmental remediation as well as photocatalytic hydrogen production from water.

Overview of reductants utilized in nuclear fuel reprocessing/recycling

DOE Office of Scientific and Technical Information (OSTI.GOV)

Paviet-Hartmann, P.; Riddle, C.; Campbell, K.

2013-07-01

The most widely used reductant to partition plutonium from uranium in the Purex process was ferrous sulfamate, other alternates were proposed such as hydrazine-stabilized ferrous nitrate or uranous nitrate, platinum catalyzed hydrogen, and hydrazine, hydroxylamine salts. New candidates to replace hydrazine or hydroxylamine nitrate (HAN) are pursued worldwide. They may improve the performance of the industrial Purex process towards different operations such as de-extraction of plutonium and reduction of the amount of hydrazine which will limit the formation of hydrazoic acid. When looking at future recycling technologies using hydroxamic ligands, neither acetohydroxamic acid (AHA) nor formohydroxamic acid (FHA) seem promisingmore » because they hydrolyze to give hydroxylamine and the parent carboxylic acid. Hydroxyethylhydrazine, HOC{sub 2}H{sub 4}N{sub 2}H{sub 3} (HEH) is a promising non-salt-forming reductant of Np and Pu ions because it is selective to neptunium and plutonium ions at room temperature and at relatively low acidity, it could serve as a replacement of HAN or AHA for the development of a novel used nuclear fuel recycling process.« less

Meta-analysis of the Effects of Sanitizing Treatments on Salmonella, Escherichia coli O157:H7, and Listeria monocytogenes Inactivation in Fresh Produce

PubMed Central

Prado-Silva, Leonardo; Cadavez, Vasco; Gonzales-Barron, Ursula; Rezende, Ana Carolina B.

2015-01-01

The aim of this study was to perform a meta-analysis of the effects of sanitizing treatments of fresh produce on Salmonella spp., Escherichia coli O157:H7, and Listeria monocytogenes. From 55 primary studies found to report on such effects, 40 were selected based on specific criteria, leading to more than 1,000 data on mean log reductions of these three bacterial pathogens impairing the safety of fresh produce. Data were partitioned to build three meta-analytical models that could allow the assessment of differences in mean log reductions among pathogens, fresh produce, and sanitizers. Moderating variables assessed in the meta-analytical models included type of fresh produce, type of sanitizer, concentration, and treatment time and temperature. Further, a proposal was done to classify the sanitizers according to bactericidal efficacy by means of a meta-analytical dendrogram. The results indicated that both time and temperature significantly affected the mean log reductions of the sanitizing treatment (P < 0.0001). In general, sanitizer treatments led to lower mean log reductions when applied to leafy greens (for example, 0.68 log reductions [0.00 to 1.37] achieved in lettuce) compared to other, nonleafy vegetables (for example, 3.04 mean log reductions [2.32 to 3.76] obtained for carrots). Among the pathogens, E. coli O157:H7 was more resistant to ozone (1.6 mean log reductions), while L. monocytogenes and Salmonella presented high resistance to organic acids, such as citric acid, acetic acid, and lactic acid (∼3.0 mean log reductions). With regard to the sanitizers, it has been found that slightly acidic electrolyzed water, acidified sodium chlorite, and the gaseous chlorine dioxide clustered together, indicating that they possessed the strongest bactericidal effect. The results reported seem to be an important achievement for advancing the global understanding of the effectiveness of sanitizers for microbial safety of fresh produce. PMID:26362982

Hypothermic inhibition of apoptotic pathways for combined neurotoxicity of iron and ascorbic acid in differentiated PC12 cells: reduction of oxidative stress and maintenance of the glutathione redox state.

PubMed

Hasegawa, Masashi; Ogihara, Tohru; Tamai, Hiroshi; Hiroi, Mayo

2009-08-04

Recent clinical trials have demonstrated the efficacy and safety of therapeutic hypothermia for neonatal hypoxic ischemic encephalopathy (HIE). We previously reported that the levels of non-protein-bound iron and ascorbic acid (AA) are increased in the CSF of infants with HIE. In this study, we investigated the effect of hypothermia on the combined cytotoxicity of Fe and AA for differentiated PC12 cells. The optimal settings for hypothermic treatment were a temperature of 30-32 degrees C, rescue time window of less than 6 h, and minimum duration of at least 24 h. Hypothermia effectively prevented the loss of the mitochondrial transmembrane potential from 6 h to 72 h (end of the study period) and attenuated the release of apoptotic proteins (cytochrome c and apoptosis-inducing factor) at 6 h of exposure to Fe-AA. Activation of caspase-3 was also delayed until 24 h. Akt was transiently activated, although no influence of temperature was observed. Elevation of oxidative stress markers, including ortho-, meta-, and di-tyrosine (markers of protein oxidation) and 4-hydroxynonenal (lipid peroxidation) was significantly attenuated when the temperature was reduced by 5 degrees C. The half-cell reduction potential (Ehc) of GSSG/2GSH redox couple ranged from -220 to -180 mV in unstressed differentiated PC12 cells, and apoptosis was triggered when Ehc exceeded -180 mV. Hypothermia prevented Ehc from rising above -180 mV within 24 h of exposure to Fe-AA. In conclusion, hypothermia prevented cell death due to Fe-AA toxicity by inhibiting apoptotic pathways through maintenance of a reduced cellular environment, as well as by alleviating oxidative stress.

Degradation of p-Nitrophenol by Lignin and Cellulose Chars: H2O2-Mediated Reaction and Direct Reaction with the Char.

PubMed

Yang, Jing; Pignatello, Joseph J; Pan, Bo; Xing, Baoshan

2017-08-15

Chars and other black carbons are reactive toward certain compounds. Such reactivity has been attributed to reduction of O 2 by persistent free radicals in the solid to H 2 O 2 , which then back-reacts with the solid to generate reactive oxygen species (ROS; especially HO • ). We studied the decomposition of p-nitrophenol (PNP) by pure lignin and cellulose chars aged in moist air or a vacuum at room temperature for up to a month. In air, the chars chemisorbed oxygen, a portion of which was liberated as H 2 O 2 when the char was submerged in water. The evolved H 2 O 2 was simultaneously decomposed by the char. PNP reacted predominantly in the sorbed state and only reduction products (phenol, catechol) were identified. Aging the char in air sharply (within hours) reduced H 2 O 2 -producing capacity and free radical concentration, but more gradually reduced PNP decay rate over the month-long period. PNP decay was only modestly suppressed (12-30%) by H 2 O 2 removal (catalase), and had little effect on the free radical signal (<6 radicals annihilated per 1000 PNP reacted). Contrasting with previous studies, the results show that direct reaction of PNP with char predominates over H 2 O 2 -dependent reactions, and the vast majority of direct-reacting sites are nonradical in character. Nonradical sites are also responsible in part for H 2 O 2 decomposition; in fact, H 2 O 2 pretreatment depleted PNP reactive sites. Lignin char was generally more reactive than cellulose char. The Fe impurity in lignin played no role. The results are relevant to the fate of pollutants in black carbon-rich environments and the use of carbons in remediation.

High Resolution Switching Mode Inductance-to-Frequency Converter with Temperature Compensationti

PubMed Central

Matko, Vojko; Milanović, Miro

2014-01-01

This article proposes a novel method for the temperature-compensated inductance-to-frequency converter with a single quartz crystal oscillating in the switching oscillating circuit to achieve better temperature stability of the converter. The novelty of this method lies in the switching-mode converter, the use of additionally connected impedances in parallel to the shunt capacitances of the quartz crystal, and two inductances in series to the quartz crystal. This brings a considerable reduction of the temperature influence of AT-cut crystal frequency change in the temperature range between 10 and 40 °C. The oscillator switching method and the switching impedances connected to the quartz crystal do not only compensate for the crystal's natural temperature characteristics but also any other influences on the crystal such as ageing as well as from other oscillating circuit elements. In addition, the method also improves frequency sensitivity in inductance measurements. The experimental results show that through high temperature compensation improvement of the quartz crystal characteristics, this switching method theoretically enables a 2 pH resolution. It converts inductance to frequency in the range of 85–100 μH to 2–560 kHz. PMID:25325334

Real-time observation of the dehydrogenation processes of methanol on clean Ru(001) and Ru(001)-p(2×2) O surfaces by a temperature-programmed electron-stimulated desorption ion angular distribution/time-of-flight system

NASA Astrophysics Data System (ADS)

Sasaki, Takehiko; Itai, Yuichiro; Iwasawa, Yasuhiro

1999-12-01

Decomposition processes of methanol on clean and oxygen-precovered Ru(001) surfaces have been visualized in real time with a temperature-programmed (TP) electron-stimulated desorption ion angular distribution (ESDIAD)/time-of-flight (TOF) system. The mass of desorbed ions during temperature-programmed surface processes was identified by TOF measurements. In the case of methanol (CH 3OD) adsorption on Ru(001)-p(2×2)-O, a halo pattern of H + from the methyl group of methoxy species was observed at 100-200 K, followed by a broad pattern from the methyl group at 230-250 K and by a near-center pattern from O + ions originating from adsorbed CO above 300 K. The halo pattern is attributed to a perpendicular conformation of the CO bond axis of the methoxy species, leading to off-normal CH bond scission. On the other hand, methanol adsorbed on clean Ru(001) did not give any halo pattern but a broad pattern was observed along the surface normal, indicating that the conformation of the methoxy species is not ordered on the clean surface. Comparison between the ESDIAD images of the oxygen-precovered surface and the clean surface suggests that the precovered oxygen adatoms induce ordering of the methoxy species. Real-time ESDIAD measurements revealed that the oxygen atoms at the Ru(001)-p(2×2)-O surface have a positive effect on selective dehydrogenation of the methoxy species to CO+H 2 and a blocking effect on CO bond breaking of the methoxy species.

Atomic-Scale Design of Iron Fischer-Tropsch Catalysts; A Combined Computational Chemistry, Experimental, and Microkinetic Modeling Approach

DOE Office of Scientific and Technical Information (OSTI.GOV)

Manos Mavrikakis; James Dumesic; Rahul Nabar

2008-09-29

This work focuses on (1) searching/summarizing published Fischer-Tropsch synthesis (FTS) mechanistic and kinetic studies of FTS reactions on iron catalysts; (2) preparation and characterization of unsupported iron catalysts with/without potassium/platinum promoters; (3) measurement of H{sub 2} and CO adsorption/dissociation kinetics on iron catalysts using transient methods; (3) analysis of the transient rate data to calculate kinetic parameters of early elementary steps in FTS; (4) construction of a microkinetic model of FTS on iron, and (5) validation of the model from collection of steady-state rate data for FTS on iron catalysts. Three unsupported iron catalysts and three alumina-supported iron catalysts weremore » prepared by non-aqueous-evaporative deposition (NED) or aqueous impregnation (AI) and characterized by chemisorption, BET, temperature-programmed reduction (TPR), extent-of-reduction, XRD, and TEM methods. These catalysts, covering a wide range of dispersions and metal loadings, are well-reduced and relatively thermally stable up to 500-600 C in H{sub 2} and thus ideal for kinetic and mechanistic studies. Kinetic parameters for CO adsorption, CO dissociation, and surface carbon hydrogenation on these catalysts were determined from temperature-programmed desorption (TPD) of CO and temperature programmed surface hydrogenation (TPSR), temperature-programmed hydrogenation (TPH), and isothermal, transient hydrogenation (ITH). A microkinetic model was constructed for the early steps in FTS on polycrystalline iron from the kinetic parameters of elementary steps determined experimentally in this work and from literature values. Steady-state rate data were collected in a Berty reactor and used for validation of the microkinetic model. These rate data were fitted to 'smart' Langmuir-Hinshelwood rate expressions derived from a sequence of elementary steps and using a combination of fitted steady-state parameters and parameters specified from the transient measurements. The results provide a platform for further development of microkinetic models of FTS on Fe and a basis for more precise modeling of FTS activity of Fe catalysts. Calculations using periodic, self-consistent Density Functional Theory (DFT) methods were performed on various realistic models of industrial, Fe-based FTS catalysts. Close-packed, most stable Fe(110) facet was analyzed and subsequently carbide formation was found to be facile leading to the choice of the FeC(110) model representing a Fe facet with a sub-surface C atom. The Pt adatom (Fe{sup Pt}(110)) was found to be the most stable model for our studies into Pt promotion and finally the role of steps was elucidated by recourse to the defected Fe(211) facet. Binding Energies(BEs), preferred adsorption sites and geometries for all FTS relevant stable species and intermediates were evaluated on each model catalyst facet. A mechanistic model (comprising of 32 elementary steps involving 19 species) was constructed and each elementary step therein was fully characterized with respect to its thermochemistry and kinetics. Kinetic calculations involved evaluation of the Minimum Energy Pathways (MEPs) and activation energies (barriers) for each step. Vibrational frequencies were evaluated for the preferred adsorption configuration of each species with the aim of evaluating entropy-changes, pre exponential factors and serving as a useful connection with experimental surface science techniques. Comparative analysis among these four facets revealed important trends in their relative behavior and roles in FTS catalysis. Overall the First Principles Calculations afforded us a new insight into FTS catalysis on Fe and modified-Fe catalysts.« less

Enhanced Oxidative Dehydrogenation of Ethane with Facilitated Transport Membranes for Low Cost Production of Ethylene

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nemser, Stuart; Shangguan, Ning; Pennisi, Kenneth

This SBIR program has been extremely successful. We have met or exceeded all of the key objectives. We have successfully demonstrated the product and process feasibility. Compact Membrane Systems proposed a membrane separation technology which can efficiently separate ethylene from ethane in the presence of H 2O and CO 2. The CMS ethylene/ethane separation will significantly improve the economics of the Oxidative Dehydrogenation (ODH) process. We have developed membranes with high ethylene flux and high ethylene/ethane selectivity. These membranes have also shown good resistance to high concentration CO 2 and CO. Economic analysis shows at least **% cost savings comparedmore » with conventional distillation used for ethylene/ethane separation. Given our success to date, we have been able to establish key direct partnerships with other collaborators. The primary objective of the Phase I program was to develop a stable membrane that is capable of providing very efficient and cost effective production of ethylene from ethane. The CMS fluorinated membrane developed during this program was found to be able to provide very good C 2H 4/C 2H 6 selectivity and outstanding C 2H 4 permeance. With the development of the fast and highly selective ethylene CMS membrane, we have achieved all our Phase I program objectives. This is especially true of the estimated cost of ethylene production that is projected to be over **% less than the conventional method (distillation) at scale applications (** Nm3/h). The final result is better than the Phase I goal of 30% less. In summary, during the Phase I, we developed a CMS membrane with a high C 2H 4 permeance good C 2H 4/C 2H 6 selectivity. The stability and anti-fouling ability of the CMS membrane was demonstrated by exposing the membrane to a C 2H 4/C 2H 6 mixture gas for 7 weeks. A membrane based ODH production and separation system was designed and the economic and engineering evaluation using the VMGSim models predicted a cost of $***. As previously stated this is at least a 35% cost reduction from the conventional methods and higher than the Phase I goal (25% cost reduction). The successful Phase I research attracted the interest from several major industrial players who are willing to provide partnership and support of further research. Successful development of the fluoropolymer membranes for C 2H 4/C 2H 6 separation in the process of ODH will provide significant benefits to the public: 1. Development of a highly economically profitable use of shale gas resource; 2. More economic growth and job creations based on the rich shale gas resource in US; 3. Huge energy savings compared with the conventional production of ethylene.« less

Chemical oxidation of anthracite with hydrogen peroxide via the Fenton reaction

USGS Publications Warehouse

Heard, I.; Senftle, F.E.

1984-01-01

Solutions of 30% H2O2 ranging from pH = 0 to pH = 11.5 have been used to oxidize anthracite at room temperature. The inorganic impurities, primarily pyrite, catalysed the oxidation and reduction of H2O2 (the Fenton reaction) to form the hydroxyl radical; the oxidation of the organic matter was minimal and was observed only in strong acidic solutions (pH < 1.5). After acid demineralization, samples of the same anthracite underwent a significant enhancement of oxidation in both acid and alkaline solutions (pH = 0.4-11.5). As all the iron had been removed from the surface and the reactions were completed in a much shorter time, the oxidation mechanism must have been of a different nature than that for the untreated anthracite. A qualitative model based on the catalytic decomposition of H2O2 by activated carbon sites in the coal surface is used to explain the oxidation of the demineralized anthracite. ?? 1984.

Investigation of reactions in a fluidized bed reactor during chemical looping combustion of coal/steam with copper oxide-iron oxide-alumina oxygen carrier

DOE Office of Scientific and Technical Information (OSTI.GOV)

Siriwardane, Ranjani; Benincosa, William; Riley, Jarrett

This paper presents data on conversion of two different coals with a chemical looping oxygen carrier, CuO-Fe 2O 3-alumina, and over a range of conditions including steam and various levels of reduction of the oxygen carrier. Reactions of coal/steam/CuO-Fe 2O 3-alumina oxygen carrier and coal/steam/partially reduced CuO-Fe 2O 3-alumina oxygen carrier were investigated with Wyodak coal and Illinois #6 coal in a fluidized bed reactor. Temperature programmed reaction studies indicated that the oxygen carrier enhanced the steam gasification/combustion rates of both coals. Rates of gasification/combustion were higher with Wyodak coal (sub bituminous) than that with Illinois #6 coal (bituminous). Inmore » addition to the increase in reaction rates, the total moles of carbon that were gasified and combusted from coal/steam increased in the presence of the oxygen carrier. The reduced oxygen carrier promoted the water-gas shift reaction when reacted with synthesis gas in the presence of steam, but the reverse water gas shift reaction was observed when steam was not present. The partially reduced oxygen carrier enhanced the production of H 2 from coal/steam, which was different from the observations with un-reduced oxygen carrier. Water splitting reaction to produce H 2 was also observed with the reduced oxygen carrier. CuO-Fe 2O 3-alumina reacted with coal during the temperature ramp to 850 °C even in the absence of steam due to the chemical-looping oxygen uncoupling (CLOU) reaction. Here, the fourier transform infra-red (FTIR) analysis indicated the presence of volatile aromatics during the temperature ramp and these may have also contributed to the reactions with the oxygen carrier in the absence of steam. Increasing steam concentration had a negative effect on the CLOU reaction.« less

Investigation of reactions in a fluidized bed reactor during chemical looping combustion of coal/steam with copper oxide-iron oxide-alumina oxygen carrier

DOE PAGES

Siriwardane, Ranjani; Benincosa, William; Riley, Jarrett; ...

2016-10-06

This paper presents data on conversion of two different coals with a chemical looping oxygen carrier, CuO-Fe 2O 3-alumina, and over a range of conditions including steam and various levels of reduction of the oxygen carrier. Reactions of coal/steam/CuO-Fe 2O 3-alumina oxygen carrier and coal/steam/partially reduced CuO-Fe 2O 3-alumina oxygen carrier were investigated with Wyodak coal and Illinois #6 coal in a fluidized bed reactor. Temperature programmed reaction studies indicated that the oxygen carrier enhanced the steam gasification/combustion rates of both coals. Rates of gasification/combustion were higher with Wyodak coal (sub bituminous) than that with Illinois #6 coal (bituminous). Inmore » addition to the increase in reaction rates, the total moles of carbon that were gasified and combusted from coal/steam increased in the presence of the oxygen carrier. The reduced oxygen carrier promoted the water-gas shift reaction when reacted with synthesis gas in the presence of steam, but the reverse water gas shift reaction was observed when steam was not present. The partially reduced oxygen carrier enhanced the production of H 2 from coal/steam, which was different from the observations with un-reduced oxygen carrier. Water splitting reaction to produce H 2 was also observed with the reduced oxygen carrier. CuO-Fe 2O 3-alumina reacted with coal during the temperature ramp to 850 °C even in the absence of steam due to the chemical-looping oxygen uncoupling (CLOU) reaction. Here, the fourier transform infra-red (FTIR) analysis indicated the presence of volatile aromatics during the temperature ramp and these may have also contributed to the reactions with the oxygen carrier in the absence of steam. Increasing steam concentration had a negative effect on the CLOU reaction.« less

Residential indoor PM2.5 in wood stove homes: follow-up of the Libby changeout program

PubMed Central

Noonan, Curtis W.; Navidi, William; Sheppard, Lianne; Palmer, Christopher P.; Bergauff, Megan; Hooper, Kathi; Ward, Tony J.

2012-01-01

In 2005 through 2008 a small rural mountain valley community engaged in a wood stove changeout program to address concerns of poor ambient air quality. During this program we assessed changes to indoor air quality before and after the introduction of a new, lower emission wood stove. We previously reported a greater than 70% reduction in indoor PM2.5 concentrations in homes following the installation of a new EPA-certified stove within the home. We report here on follow-up of the experiences in these and other homes over three winters of sample collection. In 21 homes, we compared pre-changeout PM2.5 concentrations (mean (sd) = 45.0 (33.0) μg/m3) to multiple post-changeout measures of PM2.5 concentrations using a DustTrak. The mean reduction (and 95% confidence interval) from pre-changeout to post-changeout was −18.5 μg/m3 (−31.9, −5.2), adjusting for ambient PM2.5, ambient temperature, and other factors. Findings across homes and across years were highly variable, and a subset of homes did not experience a reduction in PM2.5 following changeout. Reductions were also observed for organic carbon, elemental carbon, and levoglucosan, but increases were observed for dehydroabietic acid and abietic acid. Despite overall improvements in indoor air quality, the varied response across homes may be due to factors other than the introduction of a new wood stove. PMID:22607315

Atmospheric autoxidation is increasingly important in urban and suburban North America

NASA Astrophysics Data System (ADS)

Praske, Eric; Otkjær, Rasmus V.; Crounse, John D.; Caleb Hethcox, J.; Stoltz, Brian M.; Kjaergaard, Henrik G.; Wennberg, Paul O.

2018-01-01

Gas-phase autoxidation—regenerative peroxy radical formation following intramolecular hydrogen shifts—is known to be important in the combustion of organic materials. The relevance of this chemistry in the oxidation of organics in the atmosphere has received less attention due, in part, to the lack of kinetic data at relevant temperatures. Here, we combine computational and experimental approaches to investigate the rate of autoxidation for organic peroxy radicals (RO2) produced in the oxidation of a prototypical atmospheric pollutant, n-hexane. We find that the reaction rate depends critically on the molecular configuration of the RO2 radical undergoing hydrogen transfer (H-shift). RO2 H-shift rate coefficients via transition states involving six- and seven-membered rings (1,5 and 1,6 H-shifts, respectively) of α-OH hydrogens (HOC-H) formed in this system are of order 0.1 s‑1 at 296 K, while the 1,4 H-shift is calculated to be orders of magnitude slower. Consistent with H-shift reactions over a substantial energetic barrier, we find that the rate coefficients of these reactions increase rapidly with temperature and exhibit a large, primary, kinetic isotope effect. The observed H-shift rate coefficients are sufficiently fast that, as a result of ongoing NOx emission reductions, autoxidation is now competing with bimolecular chemistry even in the most polluted North American cities, particularly during summer afternoons when NO levels are low and temperatures are elevated.

Temperature dependence of the electrode kinetics of oxygen reduction at the platinum/Nafion interface - A microelectrode investigation

NASA Technical Reports Server (NTRS)

Parthasarathy, Arvind; Srinivasan, Supramanian; Appleby, A. J.; Martin, Charles R.

1992-01-01

Results of a study of the temperature dependence of the oxygen reduction kinetics at the Pt/Nafion interface are presented. This study was carried out in the temperature range of 30-80 C and at 5 atm of oxygen pressure. The results showed a linear increase of the Tafel slope with temperature in the low current density region, but the Tafel slope was found to be independent of temperature in the high current density region. The values of the activation energy for oxygen reduction at the platinum/Nafion interface are nearly the same as those obtained at the platinum/trifluoromethane sulfonic acid interface but less than values obtained at the Pt/H3PO4 and Pt/HClO4 interfaces. The diffusion coefficient of oxygen in Nafion increases with temperature while its solubility decreases with temperature. These temperatures also depend on the water content of the membrane.

Direct N2H4/H2O2 Fuel Cells Powered by Nanoporous Gold Leaves

PubMed Central

Yan, Xiuling; Meng, Fanhui; Xie, Yun; Liu, Jianguo; Ding, Yi

2012-01-01

Dealloyed nanoporous gold leaves (NPGLs) are found to exhibit high electrocatalytic properties toward both hydrazine (N2H4) oxidation and hydrogen peroxide (H2O2) reduction. This observation allows the implementation of a direct hydrazine-hydrogen peroxide fuel cell (DHHPFC) based on these novel porous membrane catalysts. The effects of fuel and oxidizer flow rate, concentration and cell temperature on the performance of DHHPFC are systematically investigated. With a loading of ~0.1 mg cm−2 Au on each side, an open circuit voltage (OCV) of 1.2 V is obtained at 80°C with a maximum power density 195 mW cm−2, which is 22 times higher than that of commercial Pt/C electrocatalyst at the same noble metal loading. NPGLs thus hold great potential as effective and stable electrocatalysts for DHHPFCs. PMID:23230507

Gold nanowire assembling architecture for H2O2 electrochemical sensor.

PubMed

Guo, Shaojun; Wen, Dan; Dong, Shaojun; Wang, Erkang

2009-02-15

Morphological control of nanomaterials is of great interest due to their size and shape-dependent chemical and physical properties and very important applications in many fields such as biomedicine, sensors, electronics and others. In this paper, we reported a simple strategy for synthesizing gold nanowire assembling architecture at room temperature. It is found that two important factors, the proper volume ratio of ethanol to water and poly(vinyl pyrrolidone) (PVP), will play important roles in synthesizing flower-like short gold nanowire assembling spheres. Furthermore, the obtained flower-like gold assembling spheres with high surface-to-volume ratio have been employed as enhancing materials for electrochemical sensing H(2)O(2). The present electrochemical sensing platform exhibited good electrocatalytic activity towards the reduction of H(2)O(2). The detection limit for H(2)O(2) was found to be 1.2 microM, which was lower than certain enzyme-based biosensors.

Synthesis of ultrafine ZrB2 powders by sol-gel process

NASA Astrophysics Data System (ADS)

Yang, Li-Juan; Zhu, Shi-Zhen; Xu, Qiang; Yan, Zhen-Yu; Liu, Ling

2010-09-01

Ultrafine zirconium diboride (ZrB2) powders have been synthesized by sol-gel process using zirconium oxychloride (ZrOCl2·8H2O), boric acid (H3BO3) and phenolic resin as sources of zirconia, boron oxide and carbon, respectively. The effects of the reaction temperature, B/Zr ratio, holding time, and EtOH/H2O ratio on properties of the synthesized ZrB2 powders were investigated. It was revealed that ultrafine (average crystallite size between 100 and 400 nm) ZrB2 powders can be synthesized with the optimum processing parameters as follows: (i) the ratio of B/Zr is 4; (ii) the solvent is pure ethanol; (iii) the condition of carbothermal reduction heat treatment is at 1550°C for 20 min.

Physical and biological treatments of polyethylene-rice starch plastic films.

PubMed

el-Naggar, Manal M A; Farag, Magdy Gh

2010-04-15

This study aimed to produce an industrial applicable thermo-stable alpha-amylase from marine Bacillus amyloliquefaciens which isolated and selected according to its significant enzyme production. The effect of different pH values and temperatures on the bacterial growth and the enzyme production was estimated using an experimental statistical design; maximum amylase production and bacterial growth was obtained at pH 7.0 and 50 degrees C. Some biodegradable polyethylene rice starch plastic films (PERS-P) were manufactured using 0, 2.5, 5, 7.5 and 10% starch concentrations. The biodegradability (reduction in the plastic elongation%) was tested using the exposure to UV radiation at lambda(300-400 nm) (intensity of about 1000 W/m(2)) and the produced B. amyloliquefaciens thermo-stable alpha-amylase. A significant reduction in the elongation% of these biodegradable plastics was observed in both cases especially on testing the 10% PERS-P; they showed a reduction of 26% and 20%, respectively, compared to the untreated plastic films (180+/-5). 2009 Elsevier B.V. All rights reserved.

Evaluation of the pH- and Thermal Stability of the Recombinant Green Fluorescent Protein (GFP) in the Presence of Sodium Chloride

NASA Astrophysics Data System (ADS)

Ishii, Marina; Kunimura, Juliana Sayuri; Jeng, Hélio Tallon; Vessoni Penna, Thereza Christina; Cholewa, Olivia

The thermal stability of recombinant green fluorescent protein (GFP) in sodium chloride (NaCl) solutions at different concentrations, pH, and temperatures was evaluated by assaying the loss of fluorescence intensity as a measure of denaturation. GFP, extracted from Escherichia coli cells by the three-phase partitioning method and purified through a butyl hydrophobic interaction chromatography (HIC) column, was diluted in water for injection (WFI) (pH 6.0-7.0) and in 10 mM buffer solutions (acetate, pH 5.0; phosphate, pH 7.0; and Tris-EDTA, pH 8.0) with 0.9-30% NaCl or without and incubated at 80-95°C. The extent of protein denaturation was expressed as a percentage of the calculated decimal reduction time (D-value). In acetate buffer (pH 4.84 ±0.12), the mean D-values for 90% reduction in GFP fluorescence ranged from 2.3 to 3.6 min, independent of NaCl concentration and temperature. GFP thermal stability diluted in WFI (pH 5.94±0.60) was half that observed in phosphate buffer (pH 6.08±0.60); but in both systems, D-values decreased linearly with increasing NaCl concentration, with D-values (at 80°C) ranging from 3.44, min (WFI) to 6.1 min (phosphate buffer), both with 30% NaCl. However, D-values in Tris-EDTA (pH 7.65±0.17) were directly dependent on the NaCl concentration and 5-10 times higher than D-values for GFP in WFI at 80°C. GFP pH-and thermal stability can be easily monitored by the convenient measure of fluorescence intensity and potentially be used as an indicator to monitor that processing times and temperatures were attained.

On the Mechanism of In Nanoparticle Formation by Exposing ITO Thin Films to Hydrogen Plasmas.

PubMed

Fan, Zheng; Maurice, Jean-Luc; Chen, Wanghua; Guilet, Stéphane; Cambril, Edmond; Lafosse, Xavier; Couraud, Laurent; Merghem, Kamel; Yu, Linwei; Bouchoule, Sophie; Roca I Cabarrocas, Pere

2017-10-31

We present our systematic work on the in situ generation of In nanoparticles (NPs) from the reduction of ITO thin films by hydrogen (H 2 ) plasma exposure. In contrast to NP deposition from the vapor phase (i.e., evaporation), the ITO surface can be considered to be a solid reservoir of In atoms thanks to H 2 plasma reduction. On one hand, below the In melting temperature, solid In NP formation is governed by the island-growth mode, which is a self-limiting process because the H 2 plasma/ITO interaction will be gradually eliminated by the growing In NPs that cover the ITO surface. On the other hand, we show that above the melting temperature In droplets prefer to grow along the grain boundaries on the ITO surface and dramatic coalescence occurs when the growing NPs connect with each other. This growth-connection-coalescence behavior is even strengthened on In/ITO bilayers, where In particles larger than 10 μm can be formed, which are made of evaporated In atoms and in situ released ones. Thanks to this understanding, we manage to disperse dense evaporated In NPs under H 2 plasma exposure when inserting an ITO layer between them and substrate like c-Si wafer or glass by modifying the substrate surface chemistry. Further studies are needed for more precise control of this self-assembling method. We expect that our findings are not limited to ITO thin films but could be applicable to various metal NPs generation from the corresponding metal oxide thin films.

Purification and characterization of a novel recombinant highly enantioselective short-chain NAD(H)-dependent alcohol dehydrogenase from Thermus thermophilus.

PubMed

Pennacchio, Angela; Pucci, Biagio; Secundo, Francesco; La Cara, Francesco; Rossi, Mosè; Raia, Carlo A

2008-07-01

The gene encoding a novel alcohol dehydrogenase (ADH) that belongs to the short-chain dehydrogenase/reductase (SDR) superfamily was identified in the extremely thermophilic, halotolerant gram-negative eubacterium Thermus thermophilus HB27. The T. thermophilus ADH gene (adh(Tt)) was heterologously overexpressed in Escherichia coli, and the protein (ADH(Tt)) was purified to homogeneity and characterized. ADH(Tt) is a tetrameric enzyme consisting of identical 26,961-Da subunits composed of 256 amino acids. The enzyme has remarkable thermophilicity and thermal stability, displaying activity at temperatures up to approximately 73 degrees C and a 30-min half-inactivation temperature of approximately 90 degrees C, as well as good tolerance to common organic solvents. ADH(Tt) has a strict requirement for NAD(H) as the coenzyme, a preference for reduction of aromatic ketones and alpha-keto esters, and poor activity on aromatic alcohols and aldehydes. This thermophilic enzyme catalyzes the following reactions with Prelog specificity: the reduction of acetophenone, 2,2,2-trifluoroacetophenone, alpha-tetralone, and alpha-methyl and alpha-ethyl benzoylformates to (S)-(-)-1-phenylethanol (>99% enantiomeric excess [ee]), (R)-alpha-(trifluoromethyl)benzyl alcohol (93% ee), (S)-alpha-tetralol (>99% ee), methyl (R)-(-)-mandelate (92% ee), and ethyl (R)-(-)-mandelate (95% ee), respectively, by way of an efficient in situ NADH-recycling system involving 2-propanol and a second thermophilic ADH. This study further supports the critical role of the D37 residue in discriminating NAD(H) from NADP(H) in members of the SDR superfamily.

Heat tolerance of CCl4-treated animals and its modification by some agents

NASA Astrophysics Data System (ADS)

Ahujarai, P. L.; Bhatia, B.

1984-06-01

The rate of rise of body temperature and the survival time on exposure to a temperature of 40°C was recorded in normal Wistar rats and those given ip injection of 1 ml/kg BW of CCl4 24 h earlier with and without administration of (a) garlic oil (0.006 ml in arachis oil) 3 days earlier, (b) Dl-α-tocopherol (450 mg/kg BW) 48 h before CCl4 (c) glucose (300 mg in 2 ml saline) 30 min before exposure to heat stress. Significant protection against the reduction in heat tolerance by CCl4 was provided by glucose and garlic but not by vitamin E. The reduction in heat tolerance by CCl4 was attributed to the hypoglycemia caused by it, followed by breakdown of the thermoregulatory centres in the hypothalamus. The protective effect of glucose was attributed to the restoration of blood glucose levels and that of the garlic oil to its protective effect on hepatocytes against CCl4 toxicity.

Hydride CVD Hetero-epitaxy of B 12P 2 on 4H-SiC

DOE PAGES

Frye, C. D.; Saw, C. K.; Padavala, Balabalaji; ...

2016-11-27

Icosahedral boron phosphide (B 12P 2) is a wide bandgap semiconductor (3.35 eV) that has been reported to “self-heal” from high-energy electron bombardment, making it attractive for potential use in radioisotope batteries, radiation detection, or in electronics in high radiation environments. Our study focused on improving B 12P 2 hetero-epitaxial films by growing on 4H-SiC substrates over the temperature range of 1250–1450 °C using B 2H 6 and PH 3 precursors in a H 2 carrier gas. Furthermore, XRD scans and Laue transmission photographs revealed that the epitaxial relationship was (0001)<11more » $$\\bar{2}$$0> B12P2|| (0001)<11$$\\bar{2}$$0> 4H-SiC. The film morphology and crystallinity were investigated as a function of growth temperature and growth time. At 1250 °C, films tended to form rough, polycrystalline layers, but at 1300 and 1350 °C, films were continuous and comparatively smooth (R RMS≤7 nm). At 1400 or 1450 °C, the films grew in islands that coalesced as the films became thicker. Using XRD rocking curves to evaluate the crystal quality, 1300 °C was the optimum growth temperature tested. Finally, at 1300 °C, the rocking curve FWHM decreased with increasing film thickness from 1494 arcsec for a 1.1 μm thick film to 954 arcsec for a 2.7 µm thick film, suggesting a reduction in defects with thickness.« less

Hydride CVD Hetero-epitaxy of B 12P 2 on 4H-SiC

DOE Office of Scientific and Technical Information (OSTI.GOV)

Frye, C. D.; Saw, C. K.; Padavala, Balabalaji

Icosahedral boron phosphide (B 12P 2) is a wide bandgap semiconductor (3.35 eV) that has been reported to “self-heal” from high-energy electron bombardment, making it attractive for potential use in radioisotope batteries, radiation detection, or in electronics in high radiation environments. Our study focused on improving B 12P 2 hetero-epitaxial films by growing on 4H-SiC substrates over the temperature range of 1250–1450 °C using B 2H 6 and PH 3 precursors in a H 2 carrier gas. Furthermore, XRD scans and Laue transmission photographs revealed that the epitaxial relationship was (0001)<11more » $$\\bar{2}$$0> B12P2|| (0001)<11$$\\bar{2}$$0> 4H-SiC. The film morphology and crystallinity were investigated as a function of growth temperature and growth time. At 1250 °C, films tended to form rough, polycrystalline layers, but at 1300 and 1350 °C, films were continuous and comparatively smooth (R RMS≤7 nm). At 1400 or 1450 °C, the films grew in islands that coalesced as the films became thicker. Using XRD rocking curves to evaluate the crystal quality, 1300 °C was the optimum growth temperature tested. Finally, at 1300 °C, the rocking curve FWHM decreased with increasing film thickness from 1494 arcsec for a 1.1 μm thick film to 954 arcsec for a 2.7 µm thick film, suggesting a reduction in defects with thickness.« less

Selective Hydrogenation of Furfural to Furfuryl Alcohol in the Presence of a Recyclable Cobalt/SBA-15 Catalyst.

PubMed

Audemar, Maïté; Ciotonea, Carmen; De Oliveira Vigier, Karine; Royer, Sébastien; Ungureanu, Adrian; Dragoi, Brindusa; Dumitriu, Emil; Jérôme, François

2015-06-08

The hydrogenation of furfural to furfuryl alcohol was performed in the presence of a Co/SBA-15 catalyst. High selectivity (96 %) at a conversion higher than 95 % is reported over this catalytic system. As the conversion of furfural to furfuryl alcohol occurs over metallic Co sites, the effect of reduction temperature, H2 pressure, and reaction temperature were studied. Optimum reaction conditions were: 150 °C, 1.5 h, 2.0 MPa of H2 . The catalyst was recyclable, and furfuryl alcohol was recovered with a purity higher than 90 %. The effect of the solvent concentration was also studied. With a minimum of 50 wt % of solvent, the selectivity to furfuryl alcohol and the conversion of furfural remained high (both over 80 %). Likewise, the activity of the catalyst is maintained even in pure furfural, which confirms the real potential of the proposed catalytic system. This catalyst was also used in the hydrogenation of levulinic acid to produce γ-valerolactone selectively. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

An Aurivillius Oxide Based Cathode with Excellent CO2 Tolerance for Intermediate-Temperature Solid Oxide Fuel Cells.

PubMed

Zhu, Yinlong; Zhou, Wei; Chen, Yubo; Shao, Zongping

2016-07-25

The Aurivillius oxide Bi2 Sr2 Nb2 MnO12-δ (BSNM) was used as a cobalt-free cathode for intermediate-temperature solid oxide fuel cells (IT-SOFCs). To the best of our knowledge, the BSNM oxide is the only alkaline-earth-containing cathode material with complete CO2 tolerance that has been reported thus far. BSNM not only shows favorable activity in the oxygen reduction reaction (ORR) at intermediate temperatures but also exhibits a low thermal expansion coefficient, excellent structural stability, and good chemical compatibility with the electrolyte. These features highlight the potential of the new BSNM material as a highly promising cathode material for IT-SOFCs. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

On the effect of the Fe(2+)/Fe(3+) redox couple on oxidation of carbon in hot H3PO4

NASA Technical Reports Server (NTRS)

Dhar, H. P.; Christner, L. G.; Kush, A. K.

1986-01-01

Oxidation studies of graphite:glassy carbon composites have been carried out at 1 and 4.7 atm. pressures in conc. H3PO4 in the presence and absence of iron ions. The concentration of the acid was varied over 85-100 wt pct, and of the iron ions over 30-300 ppm; the temperature varied over 190-210 C. Unlike the effect of Fe, which has been observed to increase the corrosion of carbon in sulphuric acid, the corrosion in phosphoric acid was observed to be slightly decreased or not at all affected. This result arises because of the catalytic reduction of the oxidized surface groups of carbon by Fe(2+) ions. The catalytic reduction is possible because under the experimental conditions the redox potential of the Fe(2+)/Fe(3+) couple is lower than the open-circuit voltage of carbon.

Gas-phase measurements of combustion interaction with materials for radiation-cooled chambers

NASA Technical Reports Server (NTRS)

Barlow, R. S.; Lucht, R. P.; Jassowski, D. M.; Rosenberg, S. D.

1991-01-01

Foil samples of Ir and Pt are exposed to combustion products in a controlled premixed environment at atmospheric pressure. Electrical heating of the foil samples is used to control the surface temperature and to elevate it above the radiative equilibrium temperature within the test apparatus. Profiles of temperature and OH concentration in the boundary layer adjacent to the specimen surface are measured by laser-induced fluorescence. Measured OH concentrations are significantly higher than equilibrium concentrations calculated for the known mixture ratio and the measured temperature profiles. This result indicates that superequilibrium concentrations of H-atoms and O-atoms are also present in the boundary layer, due to partial equilibrium of the rapid binary reactions of the H2/O2 chemical kinetic system. These experiments are conducted as part of a research program to investigate fundamental aspects of the interaction of combustion gases with advanced high-temperature materials for radiation-cooled thrusters.

Ciprofloxacin vs. temperature: Antibiotic toxicity in the free-floating liverwort Ricciocarpus natans from a climate change perspective.

PubMed

Gomes, Marcelo Pedrosa; de Brito, Júlio César Moreira; Bicalho, Elisa Monteze; Silva, Janaína Guernica; de Fátima Gomides, Maria; Garcia, Queila Souza; Figueredo, Cleber Cunha

2018-07-01

The physiological responses of the aquatic liverwort Ricciocarpus natans to ciprofloxacin (Cipro) exposure under different growth temperatures were investigated. Cipro appears to act as an inhibitor of mitochondrial Complex III by blocking the oxidation of quinol, resulting in the formation of hydrogen peroxide (H 2 O 2 ). H 2 O 2 accumulation upon Cipro exposure is responsible for decreased photosynthesis in plants. The amount of H 2 O 2 in plants is kept under control by antioxidant enzymes, whose activities are central to the responses of plants to Cipro yet are influenced by temperature. Increased temperature favored Cipro uptake by plants as well as its deleterious effects on mitochondrial activity; however, it also favored the activity of antioxidant enzymes, thereby preventing the exacerbation of the deleterious effects of Cipro. The uptake of Cipro by plants appears to be largely a passive process, although some uptake must be driven by an energy-consuming process. Ricciocarpus natans should be considered for programs aimed at the reclamation of Cipro since this plant exhibits high Cipro-tolerance, the capacity for accumulation and increased uptake rates of the antibiotic with increasing temperatures (from 20 to 30 °C). Copyright © 2018 Elsevier Ltd. All rights reserved.

Loss Process for the C2H5 Radical in the Atmospheres of Jupiter and Saturn: First Direct, Absolute Measurement of the Rate Constant for the Reaction H + C2H5 at Low Pressure and Temperature

NASA Astrophysics Data System (ADS)

Stief, L. J.; Pimentel, A. S.; Payne, W. A.; Nesbitt, F. L.; Cody, R. J.

2003-05-01

Photochemical models of the atmospheres of Jupiter and Saturn predict the reaction H + C2H5 to be the most important loss process for C2H5 in these atmospheres. In addition, the reaction channel H + C2H5 -> 2 CH3 is a significant source of the methyl radical. There are only two relatively modern studies of the H + C2H5 reaction, both of which depend on extensive modeling involving eight elementary reactions. The motivation for the present study is the lack of direct, absolute measurements of the rate constant for the H + C2H5 reaction at low pressures and temperatures appropriate for outer planet models. In the present experiments the reactants H and C2H5 are rapidly and simultaneously generated by reaction of F with appropriate mixtures of H2 and C2H6. Using the technique of discharge-flow with collision-free sampling to a mass spectrometer, we monitor the decay of C2H5 in excess H. In contrast to previous studies of this reaction, the primary H + C2H5 reaction is isolated and the radical decays only by reaction with H and by loss at the wall. Secondary reactions such as the self-reaction of C2H5 are negligible. At P = 1 Torr He we measure k (298K) = 1.13 x 10-10 cm3 molecule-1 s-1 and k (202K) = 1.18 x 10-10 cm3 molecule-1 s-1. Experiments at T = 155 K are in progress. The reaction is temperature independent as expected based on studies of other atom-radical reactions. Our result at T = 298 K lies between those of the two relatively modern but complex studies of this reaction. The present total rate constant data and planned product yield studies at low pressures and temperatures will then be available for use in future photochemical models of the atmospheres of the outer planets. The Planetary Atmospheres Program of NASA Headquarters is supporting this research.

Escherichia albertii Inactivation following l-Lactic Acid Exposure or Cooking in Ground Beef.

PubMed

Jones-Ibarra, Amie M; Wall, Kayley R; Vuia-Riser, Jennifer; Kerth, Chris R; Castillo, Alejandro; Taylor, T Matthew

2016-09-01

Escherichia albertii is an emerging foodborne pathogen recovered from young children and adults exhibiting symptoms of gastroenteritis via pathogenesis factors including attaching and effacing lesions, cytolethal distending toxin, and Shiga toxin variants. Study objectives were to determine E. albertii survival following (i) exposure to lactic acid as a function of solution pH and incubation period and (ii) cooking ground beef patties to different endpoint temperatures. E. albertii was incubated in phosphate buffer containing 3.0% l-lactic acid adjusted to pH 3.0, 4.0, 5.0, or 7.0; survivors were determined every 30 min for 150 min. Ground beef patties (80% lean) were cooked to temperature endpoints simulating undercooking (62°C), the minimum temperature for safe cooking (71.1°C), and cooking to well done (76°C). Maximal pathogen reduction was observed after a 30-min exposure to pH 3.0 l-lactic acid. Reductions of 3.9, 4.4, and 4.9 log CFU/g were obtained following cooking ground beef patties to 62, 71.1, and 76°C, respectively, but the reductions did not differ as a function of the endpoint cooking temperature (P ≥ 0.05). E. albertii may be controlled on beef through the proper application of antimicrobial interventions and cooking.

Production of an ordered (B2) CuPd nanoalloy by low-temperature annealing under hydrogen atmosphere.

PubMed

Yamauchi, Miho; Tsukuda, Tatsuya

2011-05-14

CuPd (1/1) nanoalloys composed of disordered body-centered-cubic crystals (crystal size = 1.6 nm) were prepared by synchronous reduction of Cu and Pd precursor ions with NaBH(4). In situ XRD measurement revealed that Cu and Pd atoms in the CuPd nanoalloys are arranged into an ordered B2 structure under exposure to H(2) (5 kPa) at 373 K. Ordering of Cu and Pd atoms over a longer distance (up to 3.6 nm) was achieved by annealing the nanoalloys for a longer time under a H(2) atmosphere.

The oxygen status algorithm: a computer program for calculating and displaying pH and blood gas data.

PubMed

Siggaard-Andersen, O; Siggaard-Andersen, M

1990-01-01

Input parameters for the program are the arterial pH, pCO2, and pO2 (measured by a blood gas analyzer), oxygen saturation, carboxy-, met-, and total hemoglobin (measured by a multi-wavelength spectrometer), supplemented by patient age, sex, temperature, inspired oxygen fraction, fraction of fetal hemoglobin, and ambient pressure. Output parameters are the inspired and alveolar oxygen partial pressures, pH,pCO2 and pO2 referring to the actual patient temperature, estimated shunt fraction, half-saturation tension, estimated 2,3-diphosphoglycerate concentration, oxygen content and oxygen capacity, extracellular base excess, and plasma bicarbonate concentration. Three parameters related to the blood oxygen availability are calculated: the oxygen extraction tension, concentration of extractable oxygen, and oxygen compensation factor. Calculations of the 'reverse' type may also be performed so that the effect of therapeutic measures on the oxygen status or the acid-base status can be predicted. The user may choose among several different units of measurement and two different conventions for symbols. The results are presented in a data display screen comprising all quantities together with age, sex, and temperature adjusted reference values. The program generates a 'laboratory diagnosis' of the oxygen status and the acid-base status and three graphs illustrating the oxygen status and the acid-base status of the patient: the oxygen graph, the acid-base chart and the blood gas map. A printed summary in one A4 page including a graphical display can be produced with an Epson or HP Laser compatible printer. The program is primarily intended for routine laboratories with a blood gas analyzer combined with a multi-wavelength spectrometer. Calculating the derived quantities may enhance the usefulness of the analyzers and improve patient care. The program may also be used as a teaching aid in acid-base and respiratory physiology. The program requires an IBM PC, XT, AT or similar compatible computer running under DOS version 2.11 or later. A VGA color monitor is preferred, but the program also supports EGA, CGA, and Hercules monitors. The program will be freely available at the cost of a discette and mailing expenses by courtesy of Radiometer Medical A/S, Emdrupvej 72, DK-2400 Copenhagen NV, Denmark (valid through 1991). A simplified algorithm for a programmable pocket calculator avoiding iterative calculations is given as an Appendix.

Treatment of real wastewater produced from Mobil car wash station using electrocoagulation technique.

PubMed

El-Ashtoukhy, E-S Z; Amin, N K; Fouad, Y O

2015-10-01

This paper deals with the electrocoagulation of real wastewater produced from a car wash station using a new cell design featuring a horizontal spiral anode placed above a horizontal disc cathode. The study dealt with the chemical oxygen demand (COD) reduction and turbidity removal using electrodes in a batch mode. Various operating parameters such as current density, initial pH, NaCl concentration, temperature, and electrode material were examined to optimize the performance of the process. Also, characterization of sludge formed during electrocoagulation was carried out. The results indicated that the COD reduction and turbidity removal increase with increasing the current density and NaCl concentration; pH from 7 to 8 was found to be optimum for treating the wastewater. Temperature was found to have an insignificant effect on the process. Aluminum was superior to iron as a sacrificial electrode material in treating car wash wastewater. Energy consumption based on COD reduction ranged from 2.32 to 15.1 kWh/kg COD removed depending on the operating conditions. Finally, the sludge produced during electrocoagulation using aluminum electrodes was characterized by scanning electron microscopy (SEM) and energy dispersive spectrometry (EDS) analysis.

Growth and survival of Escherichia coli O157:H7 and Listeria monocytogenes in egg products held at different temperatures.

PubMed

Yang, S E; Chou, C C

2000-07-01

Growth and survival of Escherichia coli O157:H7 and Listeria monocytogenes in steamed eggs and scrambled eggs held at different temperatures (5, 18, 22, 37, 55, and 60 degrees C) were investigated in the present study. Among the holding temperatures tested, both pathogens multiplied best at 37 degrees C followed by 22, 18, and 5 degrees C. In general, E. coli O157:H7 grew better in the egg products than L. monocytogenes did at all the storage temperatures tested except at 5 degrees C. E. coli O157:H7 did not grow in steamed eggs and scrambled eggs held at 5 degrees C. L. monocytogenes showed a slight population increase of approximately 0.6 to 0.9 log CFU/g in these egg products at the end of the 36-h storage period at 5 degrees C. The population of both pathogens detected in the egg products was affected by the initial population, holding temperature, and length of the holding period. It was also noted that L. monocytogenes was more susceptible than E. coli O157:H7 in steamed eggs held at 60 degrees C. After holding at 60 degrees C for 1 h, no detectable viable cells of L. monocytogenes with a population reduction of 5.4 log CFU/g was observed in steamed eggs, whereas a lower population reduction of only approximately 0.5 log CFU/ml was noted for E. coli O157:H7.

Chemical looping of metal nitride catalysts: low-pressure ammonia synthesis for energy storage† †Electronic supplementary information (ESI) available: Experimental and computational details, free energy plots for the NH3 evolution and N2 reduction with Co3N/Co, Fe4N/Fe, Mn5N2/Mn4N, Mo2N/Mo, CrN/Cr2N, TaN/Ta2N, NbN/Nb2N, Li3N/LiH, Ba3N2/BaH2, Sr3N2/SrH2, and Ca3N2/CaH2, surface oxidation energetics, ΔGvac[NH*x, yH*] based on gas phase H2 as hydrogen source, NH3 evolution with Fe-doped Mn4N, NH3 evolution with Mn6N2.58, Ca3N2 and Sr2N after correcting for partial nitride hydrolysis, NH3 yield from Ca3N2vs. time and H2 gas flow rate. See DOI: 10.1039/c5sc00789e

PubMed Central

Avram, A. M.; Peterson, B. A.; Pfromm, P. H.; Peterson, A. A.

2015-01-01

The activity of many heterogeneous catalysts is limited by strong correlations between activation energies and adsorption energies of reaction intermediates. Although the reaction is thermodynamically favourable at ambient temperature and pressure, the catalytic synthesis of ammonia (NH3), a fertilizer and chemical fuel, from N2 and H2 requires some of the most extreme conditions of the chemical industry. We demonstrate how ammonia can be produced at ambient pressure from air, water, and concentrated sunlight as renewable source of process heat via nitrogen reduction with a looped metal nitride, followed by separate hydrogenation of the lattice nitrogen into ammonia. Separating ammonia synthesis into two reaction steps introduces an additional degree of freedom when designing catalysts with desirable activation and adsorption energies. We discuss the hydrogenation of alkali and alkaline earth metal nitrides and the reduction of transition metal nitrides to outline a promoting role of lattice hydrogen in ammonia evolution. This is rationalized via electronic structure calculations with the activity of nitrogen vacancies controlling the redox-intercalation of hydrogen and the formation and hydrogenation of adsorbed nitrogen species. The predicted trends are confirmed experimentally with evolution of 56.3, 80.7, and 128 μmol NH3 per mol metal per min at 1 bar and above 550 °C via reduction of Mn6N2.58 to Mn4N and hydrogenation of Ca3N2 and Sr2N to Ca2NH and SrH2, respectively. PMID:29218166

A Probabilistic Assessment of NASA Ultra-Efficient Engine Technologies for a Large Subsonic Transport

NASA Technical Reports Server (NTRS)

Tong, Michael T.; Jones, Scott M.; Arcara, Philip C., Jr.; Haller, William J.

2004-01-01

NASA's Ultra Efficient Engine Technology (UEET) program features advanced aeropropulsion technologies that include highly loaded turbomachinery, an advanced low-NOx combustor, high-temperature materials, intelligent propulsion controls, aspirated seal technology, and an advanced computational fluid dynamics (CFD) design tool to help reduce airplane drag. A probabilistic system assessment is performed to evaluate the impact of these technologies on aircraft fuel burn and NOx reductions. A 300-passenger aircraft, with two 396-kN thrust (85,000-pound) engines is chosen for the study. The results show that a large subsonic aircraft equipped with the UEET technologies has a very high probability of meeting the UEET Program goals for fuel-burn (or equivalent CO2) reduction (15% from the baseline) and LTO (landing and takeoff) NOx reductions (70% relative to the 1996 International Civil Aviation Organization rule). These results are used to provide guidance for developing a robust UEET technology portfolio, and to prioritize the most promising technologies required to achieve UEET program goals for the fuel-burn and NOx reductions.

Hydrogen kinetics studies of MgH2-FeTi composites

NASA Astrophysics Data System (ADS)

Meena, Priyanka; Jangir, Mukesh; Singh, Ramvir; Sharma, V. K.; Jain, I. P.

2018-05-01

MgH2 + x wt% FeTi (x=10, 25, 50) nano composites were ball milled to get nano structured material and characterized for structural, morphological and thermal properties. XRD of the milled samples revealed the formation of MgH2, FeTi, Fe2Ti and H0.06FeTi phases. Morphological studies by SEM were undertaken to investigate the effect of hydrogenation of nanostructure alloy. EDX confirmed elemental composition of the as-prepared alloy. TGA studies showed higher desorption temperature for milled MgH2 compared to x wt% FeTi added MgH2. Activation energy for hydrogen desorption was found to be -177.90, -215.69, -162.46 and -87.93 kJ/mol for milled MgH2 and Mg2+x wt% FeTi (10, 25, 50), showing 89.97 kJ/ mol reduction in activation energy for 50 wt% alloy additives resulting in improved hydrogen storage capacity. DSC investigations were carried out to investigate the effect of alloy on hydrogen absorption behavior of MgH2.

Tuneable diode laser spectroscopy correction factor investigation on ammonia measurement

NASA Astrophysics Data System (ADS)

Li, Nilton; El-Hamalawi, Ashraf; Baxter, Jim; Barrett, Richard; Wheatley, Andrew

2018-01-01

Current diesel engine aftertreatment systems, such as Selective Catalyst Reduction (SCR) use ammonia (NH3) to reduce Nitrogen Oxides (NOx) into Nitrogen (N2) and water (H2O). However, if the reaction between NH3 and NOx is unbalanced, it can lead either NH3 or NOx being released into the environment. As NH3 is classified as a dangerous compound in the environment, its accurate measurement is essential. Tuneable Diode Laser (TDL) spectroscopy is one of the methods used to measure raw emissions inside engine exhaust pipes, especially NH3. This instrument requires a real-time exhaust temperature, pressure and other interference compounds in order to adjust itself to reduce the error in NH3 readings. Most researchers believed that exhaust temperature and pressure were the most influential factors in TDL when measuring NH3 inside exhaust pipes. The aim of this paper was to quantify these interference effects on TDL when undertaking NH3 measurement. Surprisingly, the results show that pressure was the least influential factor when compared to temperature, H2O, CO2 and O2 when undertaking NH3 measurement using TDL.

Solution-chemical route to generalized synthesis of metal germanate nanowires with room-temperature, light-driven hydrogenation activity of CO2 into renewable hydrocarbon fuels.

PubMed

Liu, Qi; Zhou, Yong; Tu, Wenguang; Yan, Shicheng; Zou, Zhigang

2014-01-06

A facile solution-chemical route was developed for the generalized preparation of a family of highly uniform metal germanate nanowires on a large scale. This route is based on the use of hydrazine monohydrate/H2O as a mixed solvent under solvothermal conditions. Hydrazine has multiple effects on the generation of the nanowires: as an alkali solvent, a coordination agent, and crystal anisotropic growth director. Different-percentage cobalt-doped Cd2Ge2O6 nanowires were also successfully obtained through the addition of Co(OAc)2·4H2O to the initial reaction mixture for future investigation of the magnetic properties of these nanowires. The considerably negative conduction band level of the Cd2Ge2O6 nanowire offers a high driving force for photogenerated electron transfer to CO2 under UV-vis illumination, which facilitates CO2 photocatalytic reduction to a renewable hydrocarbon fuel in the presence of water vapor at room temperature.

Time-Temperature Studies of High Temperature Deterioration Phenomena in Lubricant Systems: Synthetic Ester Lubricants

DTIC Science & Technology

1979-01-01

fro:n the reduction procedures described below were analyzed by GLC on a 6 ft x 4 mm glass column using 3% Silar -IOC, 3,% OV-1 or 3% OV-17 on 100-120...Computer) follow:ng. gas chromatographic separation of reaction products obtained’from the -reduction and derivatization procedures wi h a 3% Silar -10C

Fischer-Tropsch Cobalt Catalyst Improvements with the Presence of TiO2, La2O3, and ZrO2 on an Alumina Support

NASA Technical Reports Server (NTRS)

Klettlinger, Jennifer Lindsey Suder

2012-01-01

The objective of this study was to evaluate the effect of titanium oxide, lanthanum oxide, and zirconium oxide on alumina supported cobalt catalysts. The hypothesis was that the presence of lanthanum oxide, titanium oxide, and zirconium oxide would reduce the interaction between cobalt and the alumina support. This was of interest because an optimized weakened interaction could lead to the most advantageous cobalt dispersion, particle size, and reducibility. The presence of these oxides on the support were investigated using a wide range of characterization techniques such as SEM, nitrogen adsorption, x-ray diffraction (XRD), temperature programmed reduction (TPR), temperature programmed reduction after reduction (TPR-AR), and hydrogen chemisorptions/pulse reoxidation. Results indicated that both La2O3 and TiO2 doped supports facilitated the reduction of cobalt oxide species in reference to pure alumina supported cobalt catalysts, however further investigation is needed to determine the effect of ZrO2 on the reduction profile. Results showed an increased corrected cluster size for all three doped supported catalysts in comparison to their reference catalysts. The increase in reduction and an increase in the cluster size led to the conclusion that the support-metal interaction weakened by the addition of TiO2 and La2O3. It is also likely that the interaction decreased upon presence of ZrO2 on the alumina, but further research is necessary. Preliminary results have indicated that the alumina-supported catalysts with titanium oxide and lanthanum oxide present are of interest because of the weakened cobalt support interaction. These catalysts showed an increased extent of reduction, therefore more metallic cobalt is present on the support. However, whether or not there is more cobalt available to participate in the Fischer-Tropsch synthesis reaction (cobalt surface atoms) depends also on the cluster size. On one hand, increasing cluster size alone tends to decrease the active site density; on the other hand, by increasing the size of the cobalt clusters, there is less likelihood of forming oxidized cobalt complexes (cobalt aluminate) during Fischer-Tropsch synthesis. Thus, from the standpoint of stability, improving the extent of reduction while increasing the particle size slightly may be beneficial for maintaining the sites, even if there is a slight decrease in overall initial active site density.

Reaction of hydrogen with Ag(111): binding states, minimum energy paths, and kinetics.

PubMed

Montoya, Alejandro; Schlunke, Anna; Haynes, Brian S

2006-08-31

The interaction of atomic and molecular hydrogen with the Ag(111) surface is studied using periodic density functional total-energy calculations. This paper focuses on the site preference for adsorption, ordered structures, and energy barriers for H diffusion and H recombination. Chemisorbed H atoms are unstable with respect to the H(2) molecule in all adsorption sites below monolayer coverage. The three-hollow sites are energetically the most favorable for H chemisorption. The binding energy of H to the surface decreases slightly up to one monolayer, suggesting a small repulsive H-H interaction on nonadjacent sites. Subsurface and vacancy sites are energetically less favorable for H adsorption than on-top sites. Recombination of chemisorbed H atoms leads to the formation of gas-phase H(2) with no molecular chemisorbed state. Recombination is an exothermic process and occurs on the bridge site with a pronounced energy barrier. This energy barrier is significantly higher than that inferred from experimental temperature-programmed desorption (TPD) studies. However, there is significant permeability of H atoms through the recombination energy barrier at low temperatures, thus increasing the rate constant for H(2) desorption due to quantum tunneling effects, and improving the agreement between experiment and theory.

The Development of a Fiber Optic Raman Temperature Measurement System for Rocket Flows

NASA Technical Reports Server (NTRS)

Degroot, Wim A.

1992-01-01

A fiberoptic Raman diagnostic system for H2/O2 rocket flows is currently under development. This system is designed for measurement of temperature and major species concentration in the combustion chamber and part of the nozzle of a 100 Newton thrust rocket currently undergoing testing. This paper describes a measurement system based on the spontaneous Raman scattering phenomenon. An analysis of the principles behind the technique is given. Software is developed to measure temperature and major species concentrations by comparing theoretical Raman scattering spectra with experimentally obtained spectra. Equipment selection and experimental approach are summarized. This experimental program is part of a program, which is in progress, to evaluate Navier-Stokes based analyses for this class of rocket.

Degradation of Zearalenone by Essential Oils under In vitro Conditions

PubMed Central

Perczak, Adam; Juś, Krzysztof; Marchwińska, Katarzyna; Gwiazdowska, Daniela; Waśkiewicz, Agnieszka; Goliński, Piotr

2016-01-01

Essential oils are volatile compounds, extracted from plants, which have a strong odor. These compounds are known for their antibacterial and antifungal properties. However, data concerning degradation of mycotoxins by these metabolites are very limited. The aim of the present study was to investigate the effect of essential oils (cedarwood, cinnamon leaf, cinnamon bark, white grapefruit, pink grapefruit, lemon, eucalyptus, palmarosa, mint, thymic, and rosemary) on zearalenone (ZEA) reduction under various in vitro conditions, including the influence of temperature, pH, incubation time and mycotoxin and essential oil concentrations. The degree of ZEA reduction was determined by HPLC method. It was found that the kind of essential oil influences the effectiveness of toxin level reduction, the highest being observed for lemon, grapefruit, eucalyptus and palmarosa oils, while lavender, thymic and rosemary oils did not degrade the toxin. In addition, the decrease in ZEA content was temperature, pH as well as toxin and essential oil concentration dependent. Generally, higher reduction was observed at higher temperature in a wide range of pH, with clear evidence that the degradation rate increased gradually with time. In some combinations (e.g., palmarosa oil at pH 6 and 4 or 20°C) a toxin degradation rate higher than 99% was observed. It was concluded that some of the tested essential oils may be effective in detoxification of ZEA. We suggested that essential oils should be recognized as an interesting and effective means of ZEA decontamination and/or detoxification. PMID:27563298

Incorporating redox processes improves prediction of carbon and nutrient cycling and greenhouse gas emission

NASA Astrophysics Data System (ADS)

Tang, Guoping; Zheng, Jianqiu; Yang, Ziming; Graham, David; Gu, Baohua; Mayes, Melanie; Painter, Scott; Thornton, Peter

2016-04-01

Among the coupled thermal, hydrological, geochemical, and biological processes, redox processes play major roles in carbon and nutrient cycling and greenhouse gas (GHG) emission. Increasingly, mechanistic representation of redox processes is acknowledged as necessary for accurate prediction of GHG emission in the assessment of land-atmosphere interactions. Simple organic substrates, Fe reduction, microbial reactions, and the Windermere Humic Aqueous Model (WHAM) were added to a reaction network used in the land component of an Earth system model. In conjunction with this amended reaction network, various temperature response functions used in ecosystem models were assessed for their ability to describe experimental observations from incubation tests with arctic soils. Incorporation of Fe reduction reactions improves the prediction of the lag time between CO2 and CH4 accumulation. The inclusion of the WHAM model enables us to approximately simulate the initial pH drop due to organic acid accumulation and then a pH increase due to Fe reduction without parameter adjustment. The CLM4.0, CENTURY, and Ratkowsky temperature response functions better described the observations than the Q10 method, Arrhenius equation, and ROTH-C. As electron acceptors between O2 and CO2 (e.g., Fe(III), SO42-) are often involved, our results support inclusion of these redox reactions for accurate prediction of CH4 production and consumption. Ongoing work includes improving the parameterization of organic matter decomposition to produce simple organic substrates, examining the influence of redox potential on methanogenesis under thermodynamically favorable conditions, and refining temperature response representation near the freezing point by additional model-experiment iterations. We will use the model to describe observed GHG emission at arctic and tropical sites.

Combined effects of fermentation temperature and pH on kinetic changes of chemical constituents of durian wine fermented with Saccharomyces cerevisiae.

PubMed

Lu, Yuyun; Voon, Marilyn Kai Wen; Huang, Dejian; Lee, Pin-Rou; Liu, Shao-Quan

2017-04-01

This study investigated the effects of temperature (20 and 30 °C) and pH (pH 3.1, 3.9) on kinetic changes of chemical constituents of the durian wine fermented with Saccharomyces cerevisiae. Temperature significantly affected growth of S. cerevisiae EC-1118 regardless of pH with a higher temperature leading to a faster cell death. The pH had a more significant effect on ethanol production than temperature with higher production at 20 °C (5.95%, v/v) and 30 °C (5.56%, v/v) at pH 3.9, relative to that at pH 3.1 (5.25 and 5.01%, v/v). However, relatively higher levels of isobutyl alcohol and isoamyl alcohol up to 64.52 ± 6.39 and 56.27 ± 3.00 mg/L, respectively, were produced at pH 3.1 than at pH 3.9 regardless of temperature. In contrast, production of esters was more affected by temperature than pH, where levels of ethyl esters (ethyl esters of octanoate, nonanoate, and decanoate) and acetate esters (ethyl acetate and isoamyl acetate) were significantly higher up to 2.13 ± 0.23 and 4.61 ± 0.22 mg/L, respectively, at 20 °C than at 30 °C. On the other hand, higher temperature improved the reduction of volatile sulfur compounds. This study illustrated that temperature control would be a more effective tool than pH in modulating the resulting aroma compound profile of durian wine.

Antimicrobial activity of a nisin-activated plastic film for food packaging.

PubMed

Mauriello, G; De Luca, E; La Storia, A; Villani, F; Ercolini, D

2005-01-01

To determine the effectiveness of a packaging film coated with nisin to inhibit Micrococcus luteus ATCC 10240 in tryptone soya broth (TSB) and the microbiota of raw milk during storage. A further aim was to examine the release of nisin from the activated film. An active package, obtained from nisin-treated film, was filled with 1 l of M. luteus ATCC 10240 (ML) suspension in TSB and stored at 4 and 25 degrees C for 2 days. After 24 h at 25 degrees C there was a remarkable reduction of M. luteus ATCC 10240 compared with the control, while at 4 degrees C a slight reduction was observed. Moreover, microbial growth was controlled when 1 l of three different kinds of milk was poured into the active package and stored at 4 degrees C for 7 days. The most significant results were observed in raw milk and pasteurized milk with a reduction of 0.9 log and 1.3 log, respectively. The release experiments showed that nisin release from the film was unpredictable, but it was favoured by low pH and high temperature. It appears that nisin-coated films were effective in inhibiting M. luteus ATCC 10240 in TSB and the bacterial flora in milk, and the release of nisin was pH and temperature dependent. Nisin-activated film may control bacterial growth, maintaining food quality, safety and extending the shelf-life of food products.