Compatibility of Halthane 88-3 urethane adhesive with the replacement cleaning solvent D-Limonene

DOE Office of Scientific and Technical Information (OSTI.GOV)

LeMay, J.D.; Mendoza, B.

1991-08-01

D-Limonene, (R)1-methyl-4-isopropenyl-1-cyclohexene, has been identified as a leading replacement for chlorinated solvents traditionally used to clean electrical assemblies and critical components in some phases of weapons production. Unfortunately, d-limonene has a much lower vapor pressure than the chlorinated solvents if replaces (<2 torr at ambient). This makes its complete elimination from cleaned subassemblies potentially difficult, and gives rise to concerns about the compatibility of d-limonene with materials in the warhead. During the past year many WR polymers and adhesives have been surveyed for their compatibility with d-limonene. Preliminary test results obtained at Sandia (Albuquerque) and Allied-Signal (KCD) showed that Aluminum/Halthanemore » 88-3/Aluminum joints were destroyed during exposure to saturated d-limonene vapor. The cause of bond failure appeared to be d-limonene induced swelling of the Halthane polymer. This report describes recent work performed at LLNL to study the swelling behavior and bond strength degradation of Halthane 88-3 resulting from exposure to d-limonene vapor.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Althouse, L.P.; Hammon, H.G.

A ninety-day aging study was performed on Halthane 73-18A to determine the thermal aging effects due to the presence of DABCO, a catalyst. Samples were taken after 14 days, 30 days, 60 days, and 90 days of exposure to air at 90/sup 0/C. Tests used to evaluate aging effects were: ring tensile, differential scanning calorimetry, dynamic dielectric spectroscopy, and solvent swell. Results of tensile tests indicated an increase in tensile properties that peaked at 30 days and decayed to 70 percent loss of peak strength in 90 days. DSC, DDS, and solvent swell data all followed the same trend. Comparativemore » analysis of all data support the hypothesis that the presence of DABCO increases the oxidative cleavage of the polyether chain segment.« less