Fe-Al alloy single-crystal thin film preparation for basic magnetic measurements

NASA Astrophysics Data System (ADS)

Abe, Tatsuya; Kawai, Tetsuroh; Futamoto, Masaaki; Ohtake, Mitsuru; Inaba, Nobuyuki

2018-04-01

Fe100-xAlx (x = 0, 4, 10, 20, 30 at. %) alloy films of 40 nm thickness are prepared on MgO(001) single-crystal substrates by varying substrate temperature from room temperature to 600 °C. Single-crystal films of (001) orientation with bcc-based disordered A2 structure are obtained for the Al content range of x = 0 - 20 at. %. An ordered phase of DO3 structure is observed in Fe70Al30 films prepared at temperatures higher than 200 °C, whereas (001) oriented single-crystal films of A2 structure are obtained when prepared at room temperature. The film surface profile does not depend much on the film composition, while the surface roughness increases with increasing substrate temperature. Island-like crystals are observed for films prepared at 600°C for all compositions. Difference in lattice spacing measured parallel and perpendicular to the substrate is noted for the single-crystal thin films and it increases with increasing Al content. The lattice strain in single-crystal film is caused possibly to accommodate the lattice mismatch with the MgO substrate. The (001)-oriented single-crystal films with A2 structure show four-fold symmetries in in-plane magnetic anisotropy with the easy magnetization axis A2[100] and the hard magnetization axis A2[110], whereas the films with DO3 ordered structure show almost isotropic magnetic properties.

Thermodynamic properties of a hard/soft-magnetic bilayer model

DOE Office of Scientific and Technical Information (OSTI.GOV)

Taaev, T. A., E-mail: taaev89@mail.ru; Khizriev, K. Sh.; Murtazaev, A. K.

2016-05-15

A model for describing the thermodynamic properties of a hard/soft-magnetic bilayer is proposed and thoroughly studied using the Monte Carlo method. Temperature dependences of the heat capacity, total magnetization, magnetizations of the hard- and soft-magnetic layers, total magnetic susceptibility, and susceptibilities of the hard- and soft-magnetic layers have been calculated by this method in the framework of the proposed model. The obtained temperature dependences of the heat capacity and magnetic susceptibility display double maxima that result from the two phase transitions that take place in the system. The influence of system dimensions on the thermodynamic properties of the model hasmore » been considered.« less

Computational search for rare-earth free hard-magnetic materials

NASA Astrophysics Data System (ADS)

Flores Livas, José A.; Sharma, Sangeeta; Dewhurst, John Kay; Gross, Eberhard; MagMat Team

2015-03-01

It is difficult to over state the importance of hard magnets for human life in modern times; they enter every walk of our life from medical equipments (NMR) to transport (trains, planes, cars, etc) to electronic appliances (for house hold use to computers). All the known hard magnets in use today contain rare-earth elements, extraction of which is expensive and environmentally harmful. Rare-earths are also instrumental in tipping the balance of world economy as most of them are mined in limited specific parts of the world. Hence it would be ideal to have similar characteristics as a hard magnet but without or at least with reduced amount of rare-earths. This is the main goal of our work: search for rare-earth-free magnets. To do so we employ a combination of density functional theory and crystal prediction methods. The quantities which define a hard magnet are magnetic anisotropy energy (MAE) and saturation magnetization (Ms), which are the quantities we maximize in search for an ideal magnet. In my talk I will present details of the computation search algorithm together with some potential newly discovered rare-earth free hard magnet. J.A.F.L. acknowledge financial support from EU's 7th Framework Marie-Curie scholarship program within the ``ExMaMa'' Project (329386).

Magnetic properties of hybrid elastomers with magnetically hard fillers: rotation of particles

NASA Astrophysics Data System (ADS)

Stepanov, G. V.; Borin, D. Yu; Bakhtiiarov, A. V.; Storozhenko, P. A.

2017-03-01

Hybrid magnetic elastomers belonging to the family of magnetorheological elastomers contain magnetically hard components and are of the utmost interest for the development of semiactive and active damping devices as well as actuators and sensors. The processes of magnetizing of such elastomers are accompanied by structural rearrangements inside the material. When magnetized, the elastomer gains its own magnetic moment resulting in changes of its magneto-mechanical properties, which remain permanent, even in the absence of external magnetic fields. Influenced by the magnetic field, magnetized particles move inside the matrix forming chain-like structures. In addition, the magnetically hard particles can rotate to align their magnetic moments with the new direction of the external field. Such an elastomer cannot be demagnetized by the application of a reverse field.

Thin film superconductor magnetic bearings

DOEpatents

Weinberger, Bernard R.

1995-12-26

A superconductor magnetic bearing includes a shaft (10) that is subject to a load (L) and rotatable around an axis of rotation, a magnet (12) mounted to the shaft, and a stator (14) in proximity to the shaft. The stator (14) has a superconductor thin film assembly (16) positioned to interact with the magnet (12) to produce a levitation force on the shaft (10) that supports the load (L). The thin film assembly (16) includes at least two superconductor thin films (18) and at least one substrate (20). Each thin film (18) is positioned on a substrate (20) and all the thin films are positioned such that an applied magnetic field from the magnet (12) passes through all the thin films. A similar bearing in which the thin film assembly (16) is mounted on the shaft (10) and the magnet (12) is part of the stator (14) also can be constructed.

Studies on high-moment soft magnetic FeCo/Co thin films

NASA Astrophysics Data System (ADS)

Fu, Yu; Yang, Zheng; Matsumoto, Mitsunori; Liu, Xiao-Xi; Morisako, Akimitsu

2006-06-01

The dependences of soft magnetic properties and microstructures of the sputtered FeCo (=Fe65Co35) films on Co underlayer thickness tCo, FeCo thickness tFeCo, substrate temperature Ts and target-substrate spacing dT-S are studied. FeCo single layer generally shows a high coercivity with no obvious magnetic anisotropy. Excellent soft magnetic properties with saturation magnetization μ0Ms of 2.35 T and hard axis coercivity Hch of 0.25 kA/m in FeCo films can be achieved by introducing a Co underlayer. It is shown that sandwiching a Co underlayer causes a change in orientation and reduction in grain size from 70 nm to about 10 nm in the FeCo layer. The magnetic softness can be explained by the Hoffmann's ripple theory due to the effect of grain size. The magnetic anisotropy can be controlled by changing dT-S and a maximum of 14.3 kA/m for anisotropic field Hk is obtained with dT-S=18.0 cm.

Field dependent magnetic anisotropy of Ga0.2Fe0.8 thin films

NASA Astrophysics Data System (ADS)

Resnick, Damon A.; McClure, A.; Kuster, C. M.; Rugheimer, P.; Idzerda, Y. U.

2011-04-01

Using longitudinal MOKE in combination with a variable strength rotating magnetic field, called the rotational MOKE (ROTMOKE) method, we show that the magnetic anisotropy for a Ga0.2Fe0.8 single crystal film with a thickness of 17 nm, grown on GaAs (001) with a thick ZnSe buffer layer, depends linearly on the strength of the applied magnetic field. The torque moment curves generated using ROTMOKE are well fit with a model that accounts for the uniaxial, cubic, or fourfold anisotropy, as well as additional terms with a linear dependence on the applied magnetic field. The uniaxial and cubic anisotropy fields, taken from both the hard and the easy axis scans, are seen to remain field independent. The field dependent terms are evidence of a large affect of the magnetostriction and its contribution to the effective magnetic anisotropy in GaxFe1-x thin films.

Tactile sensor of hardness recognition based on magnetic anomaly detection

NASA Astrophysics Data System (ADS)

Xue, Lingyun; Zhang, Dongfang; Chen, Qingguang; Rao, Huanle; Xu, Ping

2018-03-01

Hardness, as one kind of tactile sensing, plays an important role in the field of intelligent robot application such as gripping, agricultural harvesting, prosthetic hand and so on. Recently, with the rapid development of magnetic field sensing technology with high performance, a number of magnetic sensors have been developed for intelligent application. The tunnel Magnetoresistance(TMR) based on magnetoresistance principal works as the sensitive element to detect the magnetic field and it has proven its excellent ability of weak magnetic detection. In the paper, a new method based on magnetic anomaly detection was proposed to detect the hardness in the tactile way. The sensor is composed of elastic body, ferrous probe, TMR element, permanent magnet. When the elastic body embedded with ferrous probe touches the object under the certain size of force, deformation of elastic body will produce. Correspondingly, the ferrous probe will be forced to displace and the background magnetic field will be distorted. The distorted magnetic field was detected by TMR elements and the output signal at different time can be sampled. The slope of magnetic signal with the sampling time is different for object with different hardness. The result indicated that the magnetic anomaly sensor can recognize the hardness rapidly within 150ms after the tactile moment. The hardness sensor based on magnetic anomaly detection principal proposed in the paper has the advantages of simple structure, low cost, rapid response and it has shown great application potential in the field of intelligent robot.

Perpendicular magnetic anisotropy and magnetization dynamics in oxidized CoFeAl films

PubMed Central

Wu, Di; Zhang, Zhe; Li, Le; Zhang, Zongzhi; Zhao, H. B.; Wang, J.; Ma, B.; Jin, Q. Y.

2015-01-01

Half-metallic Co-based full-Heusler alloys with perpendicular magnetic anisotropy (PMA), such as Co2FeAl in contact with MgO, are receiving increased attention recently due to its full spin polarization for high density memory applications. However, the PMA induced by MgO interface can only be realized for very thin magnetic layers (usually below 1.3 nm), which would have strong adverse effects on the material properties of spin polarization, Gilbert damping parameter, and magnetic stability. In order to solve this issue, we fabricated oxidized Co50Fe25Al25 (CFAO) films with proper thicknesses without employing the MgO layer. The samples show controllable PMA by tuning the oxygen pressure (PO2) and CFAO thickness (tCFAO), large perpendicular anisotropy field of ~8.0 kOe can be achieved at PO2 = 12% for the sample of tCFAO = 2.1 nm or at PO2 = 7% for tCFAO = 2.8 nm. The loss of PMA at thick tCFAO or high PO2 results mainly from the formation of large amount of CoFe oxides, which are superparamagnetic at room temperature but become hard magnetic at low temperatures. The magnetic CFAO films, with strong PMA in a relatively wide thickness range and small intrinsic damping parameter below 0.028, would find great applications in developing advanced spintronic devices. PMID:26190066

Antidot patterned single and bilayer thin films based on ferrimagnetic Tb-Co alloy with perpendicular magnetic anisotropy

NASA Astrophysics Data System (ADS)

Kulesh, N. A.; Vázquez, M.; Lepalovskij, V. N.; Vas'kovskiy, V. O.

2018-02-01

Hysteresis properties and magnetization reversal in TbCo(30 nm) and FeNi(10 nm)/TbCo(30 nm) films with nanoscale antidot lattices are investigated to test the effect of nanoholes on the perpendicular anisotropy in the TbCo layer and the induced exchange bias in the FeNi layer. The antidots are introduced by depositing the films on top of hexagonally ordered porous anodic alumina substrates with pore diameter and interpore distance fixed to 75 nm and 105 nm, respectively. The analysis of combined vibrating sample magnetometry, Kerr microscopy and magnetic force microscopy imaging measurements has allowed us to link macroscopic and local magnetization reversal processes. For magnetically hard TbCo films, we demonstrate the tunability of magnetic anisotropy and coercive field (i.e., it increases from 0.2 T for the continuous film to 0.5 T for the antidot film). For the antidot FeNi/TbCo film, magnetization of FeNi is confirmed to be in plane. Although an exchange bias has been locally detected in the FeNi layer, the integrated hysteresis loop has increased coercivity and zero shift along the field axis due to the significantly decreased magnetic anisotropy of TbCo layer.

Structural, mechanical, and magnetic properties of ferrite-austenite mixture in evaporated 304 stainless steel thin films

NASA Astrophysics Data System (ADS)

Merakeb, Noureddine; Messai, Amel; Djelloul, Abdelkader; Ayesh, Ahmad I.

2015-11-01

In this paper, we investigate the structure, composition, magnetic, and mechanical properties of stainless steel thin films formed by thermal evaporation technique. These thin films reveal novel structural and physical properties where they were found to consist of nanocrystals that are ~90 % body-centred cubic crystal structure which holds ferromagnetic properties (α-phase), and ~10 % face-centred cubic crystal structure which is paramagnetic at room temperature (γ-phase). The presence of the above phases was quantified by X-ray diffraction, transmission electron microscopy, and conversion electron Mössbauer spectroscopy. The magnetic properties were evaluated by a superconducting quantum interference device magnetometer, and they confirmed the dual-phase crystal structure of the stainless thin films, where the presence of γ-phase reduced the magnetization of the produced thin films. In addition, the fabricated stainless steel thin films did not contain micro-cracks, and they exhibit a tensile stress of about 1.7 GPa, hardness of 7.5 GPa, and elastic modulus of 104 GPa.

Hard-hard coupling assisted anomalous magnetoresistance effect in amine-ended single-molecule magnetic junction

NASA Astrophysics Data System (ADS)

Tang, Y.-H.; Lin, C.-J.; Chiang, K.-R.

2017-06-01

We proposed a single-molecule magnetic junction (SMMJ), composed of a dissociated amine-ended benzene sandwiched between two Co tip-like nanowires. To better simulate the break junction technique for real SMMJs, the first-principles calculation associated with the hard-hard coupling between a amine-linker and Co tip-atom is carried out for SMMJs with mechanical strain and under an external bias. We predict an anomalous magnetoresistance (MR) effect, including strain-induced sign reversal and bias-induced enhancement of the MR value, which is in sharp contrast to the normal MR effect in conventional magnetic tunnel junctions. The underlying mechanism is the interplay between four spin-polarized currents in parallel and anti-parallel magnetic configurations, originated from the pronounced spin-up transmission feature in the parallel case and spiky transmission peaks in other three spin-polarized channels. These intriguing findings may open a new arena in which magnetotransport and hard-hard coupling are closely coupled in SMMJs and can be dually controlled either via mechanical strain or by an external bias.

Deposition of hard elastic hydrogenated fullerenelike carbon films

NASA Astrophysics Data System (ADS)

Wang, Zhou; Zhang, Junyan

2011-05-01

Hydrogenated fullerenelike carbon (H-FLC) films, with high hardness of 41.7 ± 1.4 GPa and elastic recovery of ˜75.1%, have been uniformly deposited at low temperature by pulse direct current plasma enhanced chemical vapor deposition (pulse DC PECVD). The superior mechanical properties of the H-FLC films are attributed to the unique curvature and interconnection of graphitic basal planes. We propose the fullerenelike structures are formed in the far nonequilibrium pulse plasma environment and stabilized in the sequential fast quenching process. It is expected that the facile deposition of H-FLC films will promote the large-scale low-temperature preparation of engineering protective films for industrial applications.

Effect of tungsten (W) on structural and magnetic properties of electroplated NiFe thin films for MEMS applications

NASA Astrophysics Data System (ADS)

Kannan, R.; Devaki, P.; Premkumar, P. S.; Selvambikai, M.

2018-04-01

Electrodeposition of nanocrystalline NiFe and NiFeW thin films were carried out from ammonium citrate bath at a constant current density and controlled pH of 8 by varying the bath temperature from 40 °C to 70 °C. The surface morphology and chemical composition of the electrodeposited NiFe and NiFeW soft magnetic thin films were studied by using SEM and EDAX. The SEM micrographs of the films coated at higher electrodeposited bath temperature have no micro cracks and also the films have more uniform surface morphology. The existence of crystalline nature of the coated films were analysed by XRD. The presence of predominant peaks in x-ray diffraction pattern (compared with JCPDS data) reveal that the average crystalline size was in the order of few tens of nano meters. The magnetic properties such as coercivity, saturation magnetization and magnetic flux density have been calculated from vibrating sample magnetometer analysis. The VSM result shows that the NiFeW thin film synthesised at 70 °C exhibit the lower coercivity with higher saturation magnetization. The hardness and adhesion of the electroplated films have been investigated. Reasons for variation in magnetic properties and structural characteristics are also discussed. The electroplated NiFe and NiFeW thin films can be used for Micro Electro Mechanical System (MEMS) applications due to their excellent soft magnetic behaviour.

Synthesis of hard magnetic Mn3Ga micro-islands by e-beam evaporation

NASA Astrophysics Data System (ADS)

Akdogan, O.

2018-05-01

The permanent magnet industry heavily depends on Nd-Fe-B and Sm-Co alloys because of their high-energy product and high room temperature coercivity. Main ingredient for having such superior magnetic properties compared to other known ferromagnetic materials is rare earth elements (Nd, Sm, Dy…). However recent worldwide reserve and export limitation problem of rare earths, shifted researchers' focus to rare earth free permanent magnets. Among many alternatives (FePt, Zr2Co11, FeNi …), Mn-based alloys are the most suitable due to abundance of the forming elements and trivial formation of the necessary hard phases. In this study, Mn3Ga micro islands have been prepared. Mn3Ga owes its hard magnetic properties to tetragonal D022 phase with magnetic anisotropy energy of 2 MJ/m3. Thin films and islands of Cr/MnGa/Cr layers have been deposited on Si/SiO2 wafers using combination of e-beam and thermal evaporation techniques. Cr has been used as buffer and cover layer to protect the sample from the substrate and prevent oxidation during annealing. Annealing under Ar/H2 forming gas has been performed at 350oC for 10 min. Nano thick islands of 25, 50 and 100 μm lateral size have been produced by photolithography technique. Room temperature coercivity of 7.5 kOe has been achieved on 100 μm micro islands of Mn3Ga. Produced micro islands could be a rare earth free alternative for magnetic memory and MEMS applications.

Characterization of the magnetic properties of NdFeB thick films exposed to elevated temperatures

NASA Astrophysics Data System (ADS)

Fujiwara, Ryogen; Devillers, Thibaut; Givord, Dominique; Dempsey, Nora M.

2018-05-01

Hard magnetic films used in magnetic micro-systems may be exposed to elevated temperatures during film and system fabrication and also during use of the micro-system. In this work, we studied the influence of temperature on the magnetic properties of 10 μm thick out-of-plane textured NdFeB films fabricated by high rate triode sputtering. Out-of-plane hysteresis loops were measured in the range 300K - 650K to establish the temperature dependence of coercivity, magnetization at 7 T and remanent magnetization. Thermal demagnetization was measured and magnetization losses were recorded from 350K in films heated under zero or low (-0.1 T) external field and from 325 K for films heated under an external field of -0.5 T. The effect of thermal cycling under zero field on the remanent magnetization was also studied and it was found that cycling between room temperature and 323 K did not lead to any significant loss in remanence at room temperature, while a 4% drop is recorded when the sample is cycled between RT and 343K. Measurement of hysteresis loops at room temperature following exposure to elevated temperatures reveals that while remanent magnetisation is practically recovered in all cases, irreversible losses in coercivity occur (6.7 % following heating to 650K, and 1.3 % following heating to 343K). The relevance of these results is discussed in terms of system fabrication and use.

Magnetic anisotropies and magnetic switching in Co films

NASA Astrophysics Data System (ADS)

Bland, J. A. C.; Baird, M. J.; Leung, H. T.; Ives, A. J. R.; Mackay, K. D.; Hughes, H. P.

1992-07-01

We have used the magneto-optical Kerr effect to investigate the role of the substrate and growth conditions in determining the magnetic switching behaviour of Co films in the thickness range 100-200 Å supported by GaAs(001) and Si(111) substrates. We discuss the anisotropic magnetic hysteresis behaviour observed for Co/GaAs and Co/Si films in terms of coherent rotation of the magnetisation vector during magnetic switching. Equivalent films supported by glass substrates are found to be almost isotropic in-plane. The in-plane coercive and saturation fields are observed to lie in the range 20-80 Oe but perpendicular saturation fields of 25 and 19 kOe are found for the Co/Si and Co/GaAs systems respectively which substantially exceed the demagnetising field in each case. The measured perpendicular anisotropy fields differ strongly from the values for hcp and bcc Co and are attributed to the details of the interface and film structure. We also report strongly frequency dependent magnetic switching behaviour in these Co films.

A Simple Analytical Model for Magnetization and Coercivity of Hard/Soft Nanocomposite Magnets

DOE Office of Scientific and Technical Information (OSTI.GOV)

Park, Jihoon; Hong, Yang-Ki; Lee, Woncheol

Here, we present a simple analytical model to estimate the magnetization (σ s) and intrinsic coercivity (Hci) of a hard/soft nanocomposite magnet using the mass fraction. Previously proposed models are based on the volume fraction of the hard phase of the composite. But, it is difficult to measure the volume of the hard or soft phase material of a composite. We synthesized Sm 2Co 7/Fe-Co, MnAl/Fe-Co, MnBi/Fe-Co, and BaFe 12O 19/Fe-Co composites for characterization of their σs and Hci. The experimental results are in good agreement with the present model. Therefore, this analytical model can be extended to predict themore » maximum energy product (BH) max of hard/soft composite.« less

A Simple Analytical Model for Magnetization and Coercivity of Hard/Soft Nanocomposite Magnets

DOE PAGES

Park, Jihoon; Hong, Yang-Ki; Lee, Woncheol; ...

2017-07-10

Here, we present a simple analytical model to estimate the magnetization (σ s) and intrinsic coercivity (Hci) of a hard/soft nanocomposite magnet using the mass fraction. Previously proposed models are based on the volume fraction of the hard phase of the composite. But, it is difficult to measure the volume of the hard or soft phase material of a composite. We synthesized Sm 2Co 7/Fe-Co, MnAl/Fe-Co, MnBi/Fe-Co, and BaFe 12O 19/Fe-Co composites for characterization of their σs and Hci. The experimental results are in good agreement with the present model. Therefore, this analytical model can be extended to predict themore » maximum energy product (BH) max of hard/soft composite.« less

Periodically microstructured composite films made by electric- and magnetic-directed colloidal assembly

PubMed Central

Demirörs, Ahmet Faik; Courty, Diana; Libanori, Rafael; Studart, André R.

2016-01-01

Living organisms often combine soft and hard anisotropic building blocks to fabricate composite materials with complex microstructures and outstanding mechanical properties. An optimum design and assembly of the anisotropic components reinforces the material in specific directions and sites to best accommodate multidirectional external loads. Here, we fabricate composite films with periodic modulation of the soft–hard microstructure by simultaneously using electric and magnetic fields. We exploit forefront directed-assembly approaches to realize highly demanded material microstructural designs and showcase a unique example of how one can bridge colloidal sciences and composite technology to fabricate next-generation advanced structural materials. In the proof-of-concept experiments, electric fields are used to dictate the position of the anisotropic particles through dielectrophoresis, whereas a rotating magnetic field is used to control the orientation of the particles. By using such unprecedented control over the colloidal assembly process, we managed to fabricate ordered composite microstructures with up to 2.3-fold enhancement in wear resistance and unusual site-specific hardness that can be locally modulated by a factor of up to 2.5. PMID:27071113

Supernormal hardness increase of dilute Ga(As, N) thin films

NASA Astrophysics Data System (ADS)

Berggren, Jonas; Hanke, Michael; Luna, Esperanza; Trampert, Achim

2017-03-01

Hardness of epitaxial GaAs1-xNx films on GaAs(001) with different film thicknesses, varying from 80 to 700 nm, and nitrogen compositions x between zero (pure GaAs) and 0.031, were studied by means of nano-indentation. As a result, a disproportionate and monotonic increase by 17% in hardness was proved in the dilute range from GaAs to GaAs0.969N0.031. We are tracing this observation to solid solution strengthening, an extrinsic effect based on dislocation pinning due to interstitial nitrogen. On the other hand, intrinsic effects related to different electronegativities of As and N (i.e., altered bonding conditions) could be ruled out. Furthermore, in tensilely strained GaAs1-xNx layers, the appearance of cracks acts as the main strain relieving mechanism. A correlation between cracking and hardness reduction is investigated and discussed as a further relaxation pathway.

Magnetic properties of Sm-Co thin films grown on MgO(100) deposited from a single alloy target

DOE Office of Scientific and Technical Information (OSTI.GOV)

Verhagen, T. G. A.; Boltje, D. B.; Ruitenbeek, J. M. van

2014-08-07

We have grown epitaxial Sm-Co thin films by sputter deposition from a single alloy target with a nominal SmCo{sub 5} composition on Cr(100)-buffered MgO(100) single-crystal substrates. By varying the Ar gas pressure, we can change the composition of the film from a SmCo{sub 5}-like to a Sm{sub 2}Co{sub 7}-like phase. The composition, crystal structure, morphology, and magnetic properties of these films have been determined using Rutherford Backscattering, X-ray diffraction, and magnetization measurements. We find that we can grow films with, at room temperature, coercive fields as high as 3.3 T, but with a remanent magnetization which is lower than can bemore » expected from the texturing. This appears to be due to the Sm content of the films, which is higher than expected from the content of the target, even at the lowest possible sputtering pressures. Moreover, we find relatively large variations of film properties using targets of nominally the same composition. At low temperatures, the coercive fields increase, as expected for these hard magnets, but in the magnetization, we observe a strong background signal from the paramagnetic impurities in the MgO substrates.« less

Improved adhesion of ultra-hard carbon films on cobalt–chromium orthopaedic implant alloy

PubMed Central

Vaid, Rishi; Diggins, Patrick; Weimer, Jeffrey J.; Koopman, M.; Vohra, Yogesh K.

2010-01-01

While interfacial graphite formation and subsequent poor film adhesion is commonly reported for chemical vapor deposited hard carbon films on cobalt-based materials, we find the presence of O2 in the feedgas mixture to be useful in achieving adhesion on a CoCrMo alloy. Nucleation studies of surface structure before formation of fully coalesced hard carbon films reveal that O2 feedgas helps mask the catalytic effect of cobalt with carbon through early formation of chromium oxides and carbides. The chromium oxides, in particular, act as a diffusion barrier to cobalt, minimizing its migration to the surface where it would otherwise interact deleteriously with carbon to form graphite. When O2 is not used, graphitic soot forms and films delaminate readily upon cooling to room temperature. Continuous 1 μm-thick nanostructured carbon films grown with O2 remain adhered with measured hardness of 60 GPa and show stable, non-catastrophic circumferential micro-cracks near the edges of indent craters made using Rockwell indentation. PMID:21221739

A review of high magnetic moment thin films for microscale and nanotechnology applications

DOE PAGES

Scheunert, Gunther; Heinonen, O.; Hardeman, R.; ...

2016-02-17

Here, the creation of large magnetic fields is a necessary component in many technologies, ranging from magnetic resonance imaging, electric motors and generators, and magnetic hard disk drives in information storage. This is typically done by inserting a ferromagnetic pole piece with a large magnetisation density M S in a solenoid. In addition to large M S, it is usually required or desired that the ferromagnet is magnetically soft and has a Curie temperature well above the operating temperature of the device. A variety of ferromagnetic materials are currently in use, ranging from FeCo alloys in, for example, hard diskmore » drives, to rare earth metals operating at cryogenic temperatures in superconducting solenoids. These latter can exceed the limit on M S for transition metal alloys given by the Slater-Pauling curve. This article reviews different materials and concepts in use or proposed for technological applications that require a large M S, with an emphasis on nanoscale material systems, such as thin and ultra-thin films. Attention is also paid to other requirements or properties, such as the Curie temperature and magnetic softness. In a final summary, we evaluate the actual applicability of the discussed materials for use as pole tips in electromagnets, in particular, in nanoscale magnetic hard disk drive read-write heads; the technological advancement of the latter has been a very strong driving force in the development of the field of nanomagnetism.« less

Investigation of hydrogen concentration and hardness of ion irradiated organically modified silicate thin films

NASA Astrophysics Data System (ADS)

Qi, Y.; Prenzel, T.; Harriman, T. A.; Wang, Y. Q.; Lucca, D. A.; Williams, D.; Nastasi, M.; Dong, J.; Mehner, A.

2010-06-01

A study of the effects of ion irradiation of organically modified silicate thin films on the loss of hydrogen and increase in hardness is presented. NaOH catalyzed SiNa wO xC yH z thin films were synthesized by sol-gel processing from tetraethylorthosilicate (TEOS) and methyltriethoxysilane (MTES) precursors and spin-coated onto Si substrates. After drying at 300 °C, the films were irradiated with 125 keV H + or 250 keV N 2+ at fluences ranging from 1 × 10 14 to 2.5 × 10 16 ions/cm 2. Elastic Recoil Detection (ERD) was used to investigate resulting hydrogen concentration as a function of ion fluence and irradiating species. Nanoindentation was used to measure the hardness of the irradiated films. FT-IR spectroscopy was also used to examine resulting changes in chemical bonding. The resulting hydrogen loss and increase in hardness are compared to similarly processed acid catalyzed silicate thin films.

Preparation of multi-layer film consisting of hydrogen-free DLC and nitrogen-containing DLC for conductive hard coating

NASA Astrophysics Data System (ADS)

Iijima, Yushi; Harigai, Toru; Isono, Ryo; Degai, Satoshi; Tanimoto, Tsuyoshi; Suda, Yoshiyuki; Takikawa, Hirofumi; Yasui, Haruyuki; Kaneko, Satoru; Kunitsugu, Shinsuke; Kamiya, Masao; Taki, Makoto

2018-01-01

Conductive hard-coating films have potential application as protective films for contact pins used in the electrical inspection process for integrated circuit chips. In this study, multi-layer diamond-like carbon (DLC) films were prepared as conductive hard-coating films. The multi-layer DLC films consisting of DLC and nitrogen-containing DLC (N-DLC) film were prepared using a T-shape filtered arc deposition method. Periodic DLC/N-DLC four-layer and eight-layer films had the same film thickness by changing the thickness of each layer. In the ball-on-disk test, the N-DLC mono-layer film showed the highest wear resistance; however, in the spherical polishing method, the eight-layer film showed the highest polishing resistance. The wear and polishing resistance and the aggressiveness against an opponent material of the multi-layer DLC films improved by reducing the thickness of a layer. In multi-layer films, the soft N-DLC layer between hard DLC layers is believed to function as a cushion. Thus, the tribological properties of the DLC films were improved by a multi-layered structure. The electrical resistivity of multi-layer DLC films was approximately half that of the DLC mono-layer film. Therefore, the periodic DLC/N-DLC eight-layer film is a good conductive hard-coating film.

Monte Carlo study of magnetization reversal in the model of a hard/soft magnetic bilayer

NASA Astrophysics Data System (ADS)

Taaev, T. A.; Khizriev, K. Sh.; Murtazaev, A. K.

2017-06-01

Magnetization reversal in the model of a hard/soft magnetic bilayer under the action of an external magnetic field has been investigated by the Monte Carlo method. Calculations have been performed for three systems: (i) the model without a soft-magnetic layer (hard-magnetic layer), (ii) the model with a soft-magnetic layer of thickness 25 atomic layers (predominantly exchange-coupled system), and (iii) with 50 (weak exchange coupling) atomic layers. The effect of a soft-magnetic phase on the magnetization reversal of the magnetic bilayer and on the formation of a 1D spin spring in the magnetic bilayer has been demonstrated. An inf lection that has been detected on the arch of the hysteresis loop only for the system with weak exchange coupling is completely determined by the behavior of the soft layer in the external magnetic field. The critical fields of magnetization reversal decrease with increasing thickness of the soft phase.

Tailoring magnetic domains in Gd-Fe thin films

NASA Astrophysics Data System (ADS)

Talapatra, A.; Chelvane, J. Arout; Mohanty, J.

2018-05-01

This paper presents the global modification of magnetic domains and magnetic properties in amorphous Gd19Fe81 thin films with rapid thermal processing at two distinct temperatures (250oC and 450oC), and with different time intervals viz., 2, 5, 10 and 20 minutes. 100 nm thick as-prepared films display nano-scale meandering stripe domains with high magnetic phase contrast which is the signature of perpendicular magnetic anisotropy. The films processed at 250oC for various time intervals show successive reduction in magnetic phase contrast and domain size. The domain pattern completely disappeared, and topography dominated mixed magnetic phase has been obtained for the films processed at 450oC for time intervals greater than 2 minutes. The magnetization measurements indicate the reduction in perpendicular magnetic anisotropy with increase in saturation magnetization for all the rapid thermal processed films. The experimental outputs have been used to simulate the domain pattern. Reduction in uniaxial anisotropy along with the increase in saturation magnetization successfully explain the experimental trend of decrease in domain size and magnetic contrast.

Soft Magnetic Multilayered Thin Films for HF Applications

NASA Astrophysics Data System (ADS)

Loizos, George; Giannopoulos, George; Serletis, Christos; Maity, Tuhin; Roy, Saibal; Lupu, Nicoleta; Kijima, Hanae; Yamaguchi, Masahiro; Niarchos, Dimitris

Multilayered thin films from various soft magnetic materials were successfully prepared by magnetron sputtering in Ar atmosphere. The magnetic properties and microstructure were investigated. It is found that the films show good soft magnetic properties: magnetic coercivity of 1-10 Oe and saturation magnetization higher than 1T. The initial permeability of the films is greater than 300 and flattens up to 600 MHz. The multilayer thin film properties in combination with their easy, fast and reproducible fabrication indicate that they are potential candidates for high frequency applications.

Flexible magnetic thin films and devices

NASA Astrophysics Data System (ADS)

Sheng, Ping; Wang, Baomin; Li, Runwei

2018-01-01

Flexible electronic devices are highly attractive for a variety of applications such as flexible circuit boards, solar cells, paper-like displays, and sensitive skin, due to their stretchable, biocompatible, light-weight, portable, and low cost properties. Due to magnetic devices being important parts of electronic devices, it is essential to study the magnetic properties of magnetic thin films and devices fabricated on flexible substrates. In this review, we mainly introduce the recent progress in flexible magnetic thin films and devices, including the study on the stress-dependent magnetic properties of magnetic thin films and devices, and controlling the properties of flexible magnetic films by stress-related multi-fields, and the design and fabrication of flexible magnetic devices. Project supported by the National Key R&D Program of China (No. 2016YFA0201102), the National Natural Science Foundation of China (Nos. 51571208, 51301191, 51525103, 11274321, 11474295, 51401230), the Youth Innovation Promotion Association of the Chinese Academy of Sciences (No. 2016270), the Key Research Program of the Chinese Academy of Sciences (No. KJZD-EW-M05), the Ningbo Major Project for Science and Technology (No. 2014B11011), the Ningbo Science and Technology Innovation Team (No. 2015B11001), and the Ningbo Natural Science Foundation (No. 2015A610110).

Thin-Film Permanent Magnets for Integrated Electromagnetic Components.

DTIC Science & Technology

1992-06-01

crystallization growth temperature, the self demagnetization energy can be used to favor the growth of crystallites with the easy axes of magnetization ...due to the demagnetization energy. 5 Relatively thick films of Sm-Co based permanent magnet films have been deposited onto precoated sapphire and A12 0...of films with the easy axes of magnetization aligned onto the film plane. The self demagnetization field can only affect the film texture for systems

Ultra-hard amorphous AlMgB14 films RF sputtered onto curved substrates

NASA Astrophysics Data System (ADS)

Grishin, A. M.; Putrolaynen, V. V.; Yuzvyuk, M. H.

2017-03-01

Recently, hard AlMgB14 (BAM) coatings were deposited for the first time by RF magnetron sputtering using a single stoichiometric ceramic target. High target sputtering power and sufficiently short target-to-substrate distance were found to be critical processing conditions. They enabled fabrication of stoichiometric in-depth compositionally homogeneous films with the peak values of nanohardness 88 GPa and Young’s modulus 517 GPa at the penetration depth of 26 nm and, respectively, 35 GPa and 275 GPa at 200 nm depth in 2 µm thick film (Grishin et al 2014 JETP Lett. 100 680). The narrow range of sufficiently short target-to-substrate distance makes impossible to coat non flat specimens. To achieve ultimate BAM films’ characteristics onto curved surfaces we developed two-step sputtering process. The first thin layer is deposited as a template at low RF power that facilitates a layered Frank van der Merwe mode growth of smooth film occurs. The next layer is grown at high RF target sputtering power. The affinity of subsequent flow of sputtered atoms to already evenly condensed template fosters the development of smooth film surface. As an example, we made BAM coating onto hemispherical 5 mm in diameter ball made from a hard tool steel and used as a head of a special gauge. Very smooth (6.6 nm RMS surface roughness) and hard AlMgB14 films fabricated onto commercial ball-shaped items enhance hardness of tool steel specimens by a factor of four.

Synthesis and magnetic properties of the thin film exchange spring system of MnBi/FeCo

NASA Astrophysics Data System (ADS)

Sabet, S.; Hildebrandt, E.; Alff, L.

2017-10-01

Manganese bismuth thin films with a nominal thickness of ∼40 nm were grown at room temperature onto quartz glass substrate in a DC magnetron sputtering unit. In contrast to the usual multilayer approach, the MnBi films were deposited using a single sputtering target with a stoichiometry of Mn55Bi45 (at. %). A subsequent in-situ annealing step was performed in vacuum in order to form the ferromagnetic LTP of MnBi. X-ray diffraction confirmed the formation of a textured LTP MnBi hard phase after annealing at 330 °C. This film shows a maximum saturation magnetization of 530 emu/cm3, high out-of-plane coercivity of 15 kOe induced by unreacted bismuth. The exchange coupling effect was investigated by deposition of a second layer of FeCo with 1 nm and 2 nm thickness onto the LTP MnBi films. The MnBi/FeCo double layer showed as expected higher saturation magnetization with increasing thickness of the FeCo layer while the coercive field remained constant. The fabrication of the MnBi/FeCo double layer for an exchange spring magnet was facilitated by deposition from a single stoichiometric target.

Thermally evaporated mechanically hard tin oxide thin films for opto-electronic apllications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tripathy, Sumanta K.; Rajeswari, V. P.

2014-01-28

Tungsten doped tin oxide (WTO) and Molybdenum doped tin oxide (MoTO) thin film were deposited on corn glass by thermal evaporation method. The films were annealed at 350°C for one hour. Structural analysis using Xray diffraction data shows both the films are polycrystalline in nature with monoclinic structure of tin oxide, Sn{sub 3}O{sub 4}, corresponding to JCPDS card number 01-078-6064. SEM photograph showed that both the films have spherical grains with size in the range of 20–30 nm. Compositional analysis was carried out using EDS which reveals the presence of Sn, O and the dopant Mo/W only thereby indicating themore » absence of any secondary phase in the films. The films are found to contain nearly 6 wt% of Mo, 8 wt% of W as dopants respectively. The transmission pattern for both the films in the spectral range 200 – 2000 nm shows that W doping gives a transparency of nearly 80% from 380 nm onwards while Mo doping has less transparency of 39% at 380nm. Film hardness measurement using Triboscope shows a film hardness of about 9–10 GPa for both the films. It indicates that W or M doping in tin oxide provides the films the added advantage of withstanding the mechanical wear and tear due to environmental fluctuations By optimizing the optical and electrical properties, W/Mo doped tin oxide films may be explored as window layers in opto-electronic applications such as solar cells.« less

Electroplated L1{sub 0} CoPt thick-film permanent magnets

DOE Office of Scientific and Technical Information (OSTI.GOV)

Oniku, Ololade D., E-mail: ololadeoniku@ufl.edu; Qi, Bin; Arnold, David P.

2014-05-07

The fabrication and magnetic characterization of 15-μm-thick electroplated L1{sub 0} CoPt hard magnets with good magnetic properties is reported in this paper. Experimental study of the dependence of the magnets' properties on annealing temperature reveals that an intrinsic coercivity H{sub ci} = ∼800 kA/m (10 kOe), squareness >0.8, and energy product of >150 kJ/m{sup 3} are obtained for photolithographically patterned structures (250 μm × 2 mm stripes; 15 μm thickness) electroplated on silicon substrates and annealed in hydrogen forming gas at 700 °C. Scanning electron microscopy is used to inspect the morphology of both the as-deposited and annealed magnetic layers, and X-ray Diffractometer analysis on the magnets annealed at 700 °Cmore » confirm a phase transformation to an ordered L1{sub 0} CoPt structure, with a minor phase of hcp Co. These thick films are intended for microsystems/MEMS applications.« less

Magnetic Yoking and Tunable Interactions in FePt-Based Hard/Soft Bilayers

PubMed Central

Gilbert, Dustin A.; Liao, Jung-Wei; Kirby, Brian J.; Winklhofer, Michael; Lai, Chih-Huang; Liu, Kai

2016-01-01

Magnetic interactions in magnetic nanostructures are critical to nanomagnetic and spintronic explorations. Here we demonstrate an extremely sensitive magnetic yoking effect and tunable interactions in FePt based hard/soft bilayers mediated by the soft layer. Below the exchange length, a thin soft layer strongly exchange couples to the perpendicular moments of the hard layer; above the exchange length, just a few nanometers thicker, the soft layer moments turn in-plane and act to yoke the dipolar fields from the adjacent hard layer perpendicular domains. The evolution from exchange to dipolar-dominated interactions is experimentally captured by first-order reversal curves, the ΔM method, and polarized neutron reflectometry, and confirmed by micromagnetic simulations. These findings demonstrate an effective yoking approach to design and control magnetic interactions in wide varieties of magnetic nanostructures and devices. PMID:27604428

Laser Deposition of Polymer Nanocomposite Thin Films and Hard Materials and Their Optical Characterization

DTIC Science & Technology

2013-12-05

visible light on instruments such as microscope tips and micro- surgical tools. Hard carbon known as diamond-like carbon films produced by pulsed laser ...visible (610 nm) LED source and a supplemental infra-red 980-nm laser diode (for the studies of the upconversion fluorescence). The basic package...5/2013 Final Performance Report 15 Sep 2012- 14 Sep 2013 LASER DEPOSITION OF POLYMER NANOCOMPOSITE THIN FILMS AND HARD MATERIALS AND THEIR OPTICAL

Skyrmion morphology in ultrathin magnetic films

NASA Astrophysics Data System (ADS)

Gross, I.; Akhtar, W.; Hrabec, A.; Sampaio, J.; Martínez, L. J.; Chouaieb, S.; Shields, B. J.; Maletinsky, P.; Thiaville, A.; Rohart, S.; Jacques, V.

2018-02-01

Nitrogen-vacancy magnetic microscopy is employed in the quenching mode as a noninvasive, high-resolution tool to investigate the morphology of isolated skyrmions in ultrathin magnetic films. The skyrmion size and shape are found to be strongly affected by local pinning effects and magnetic field history. Micromagnetic simulations including a static disorder, based on the physical model of grain-to-grain thickness variations, reproduce all experimental observations and reveal the key role of disorder and magnetic history in the stabilization of skyrmions in ultrathin magnetic films. This work opens the way to an in-depth understanding of skyrmion dynamics in real, disordered media.

Structural, magnetic and magnetocaloric properties of sputtered Gd films

NASA Astrophysics Data System (ADS)

Kumar, N. Pavan; Shaleni, V.; Satyanarayana, L.; Manorama, S. V.; Raja, M. Manivel

2018-05-01

Gd films with different thicknesses varying from 100 nm to 750 nm have been deposited on single crystal Si (100) substrate by ultra high vacuum magnetron sputtering system. X-ray diffraction analysis reveals the crystalline nature and hcp crystal structure of the films. Microstructure investigations have been carried to study the surface morphology of the films. Thermo magnetic studies confirm the magnetic transition of the films and are ˜275 K, close to bulk. Magnetocaloric effect (MCE) has been studied from magnetic isotherms measured around magnetic transition and the maximum isothermal entropy change of 2.0 J/kg-K is achieved for a magnetic field change of 2 T for the 750 nm film. The sputtered Gd films are useful for micro cooling device applications.

Spin–orbit torque-assisted switching in magnetic insulator thin films with perpendicular magnetic anisotropy

DOE PAGES

Li, Peng; Liu, Tao; Chang, Houchen; ...

2016-09-01

As an in-plane charge current flows in a heavy metal film with spin-orbit coupling, it produces a torque on and thereby switches the magnetization in a neighbouring ferromagnetic metal film. Such spin-orbit torque (SOT)-induced switching has been studied extensively in recent years and has shown higher efficiency than switching using conventional spin-transfer torque. Here we report the SOT-assisted switching in heavy metal/magnetic insulator systems. The experiments used a Pt/BaFe 12O 19 bilayer where the BaFe 12O 19 layer exhibits perpendicular magnetic anisotropy. As a charge current is passed through the Pt film, it produces a SOT that can control themore » up and down states of the remnant magnetization in the BaFe 12O 19 film when the film is magnetized by an in-plane magnetic field. Furthermore, it can reduce or increase the switching field of the BaFe 12O 19 film by as much as about 500 Oe when the film is switched with an out-of-plane field.« less

Spin-orbit torque-assisted switching in magnetic insulator thin films with perpendicular magnetic anisotropy

NASA Astrophysics Data System (ADS)

Li, Peng; Liu, Tao; Chang, Houchen; Kalitsov, Alan; Zhang, Wei; Csaba, Gyorgy; Li, Wei; Richardson, Daniel; Demann, August; Rimal, Gaurab; Dey, Himadri; Jiang, J. S.; Porod, Wolfgang; Field, Stuart B.; Tang, Jinke; Marconi, Mario C.; Hoffmann, Axel; Mryasov, Oleg; Wu, Mingzhong

2016-09-01

As an in-plane charge current flows in a heavy metal film with spin-orbit coupling, it produces a torque on and thereby switches the magnetization in a neighbouring ferromagnetic metal film. Such spin-orbit torque (SOT)-induced switching has been studied extensively in recent years and has shown higher efficiency than switching using conventional spin-transfer torque. Here we report the SOT-assisted switching in heavy metal/magnetic insulator systems. The experiments used a Pt/BaFe12O19 bilayer where the BaFe12O19 layer exhibits perpendicular magnetic anisotropy. As a charge current is passed through the Pt film, it produces a SOT that can control the up and down states of the remnant magnetization in the BaFe12O19 film when the film is magnetized by an in-plane magnetic field. It can reduce or increase the switching field of the BaFe12O19 film by as much as about 500 Oe when the film is switched with an out-of-plane field.

Nanosphere lithography applied to magnetic thin films

NASA Astrophysics Data System (ADS)

Gleason, Russell

Magnetic nanostructures have widespread applications in many areas of physics and engineering, and nanosphere lithography has recently emerged as promising tool for the fabrication of such nanostructures. The goal of this research is to explore the magnetic properties of a thin film of ferromagnetic material deposited onto a hexagonally close-packed monolayer array of polystyrene nanospheres, and how they differ from the magnetic properties of a typical flat thin film. The first portion of this research focuses on determining the optimum conditions for depositing a monolayer of nanospheres onto chemically pretreated silicon substrates (via drop-coating) and the subsequent characterization of the deposited nanosphere layer with scanning electron microscopy. Single layers of permalloy (Ni80Fe20) are then deposited on top of the nanosphere array via DC magnetron sputtering, resulting in a thin film array of magnetic nanocaps. The coercivities of the thin films are measured using a home-built magneto-optical Kerr effect (MOKE) system in longitudinal arrangement. MOKE measurements show that for a single layer of permalloy (Py), the coercivity of a thin film deposited onto an array of nanospheres increases compared to that of a flat thin film. In addition, the coercivity increases as the nanosphere size decreases for the same deposited layer. It is postulated that magnetic exchange decoupling between neighboring nanocaps suppresses the propagation of magnetic domain walls, and this pinning of the domain walls is thought to be the primary source of the increase in coercivity.

Wearable near-field communication antennas with magnetic composite films

NASA Astrophysics Data System (ADS)

Zhan, Bihong; Su, Dan; Liu, Sheng; Liu, Feng

2017-06-01

The flexible near-field communication (NFC) antennas integrated with Fe3O4/ethylene-vinyl acetate copolymer (EVA) magnetic films were presented, and the influence of the magnetic composite films on the performance and miniaturization capability of the NFC antennas was investigated. Theoretical analysis and experimental results show that the integration of the magnetic composite films is conducive to the miniaturization of the NFC antennas. However, the pattern design of the integrated magnetic film is very important to improve the communication performance of NFC antenna. When magnetic film covers whole antenna, the inductance (L) and quality factor (Q) of the NFC antenna at 13MHz are increased by 60% and 5% respectively, but the communication distance of NFC system is decreased by 70%. When the magnetic film is located at the center of the antenna, the L value, Q value and communication distance of the NFC antenna are increased by 16.5%, 15.5% and 20% respectively. It can be seen that the application of the integrated magnetic film with optimized pattern to the NFC antenna can not only reduce the size of the antenna, but also improve the overall performance of the antenna.

Magnetic thin-film split-domain current sensor-recorder

DOEpatents

Hsieh, Edmund J.

1979-01-01

A sensor-recorder for recording a representation of the direction and peak amplitude of a transient current. A magnetic thin film is coated on a glass substrate under the influence of a magnetic field so that the finished film is magnetically uniaxial and anisotropic. The film is split into two oppositely magnetized contiguous domains with a central boundary by subjecting adjacent portions of the film simultaneously to magnetic fields that are opposed 180.degree.. With the split-domain sensor-recorder placed with the film plane and domain boundary either perpendicular or parallel to the expected conductive path of a transient current, the occurrence of the transient causes switching of a portion of one domain to the direction of the other domain. The amount of the switched domain portion is indicative of the amplitude of the peak current of the transient, while the particular domain that is switched is indicative of the direction of the current. The resulting domain patterns may be read with a passive magnetic tape viewer.

Strain-induced modification of magnetic structure and new magnetic phases in rare-earth epitaxial films

NASA Astrophysics Data System (ADS)

Dufour, C.; Dumesnil, K.; Mangin, Ph

2006-07-01

Rare earths exhibit complex magnetic phase diagrams resulting from the competition between various contributions to the magnetic energy: exchange, anisotropy and magnetostriction. The epitaxy of a rare-earth film on a substrate induces (i) a clamping to the substrate and (ii) pseudomorphic strains. Both these effects are shown to lead to modifications of the magnetic properties in (0 0 1)Dy, (0 0 1)Tb and (1 1 0)Eu films. In Dy and Tb films, spectacular variations of the Curie temperature have been evidenced. Additionally, Tb films exhibit a new large wavelength magnetic modulation. In Eu films, one of the helical magnetic domains disappears at low temperature whereas the propagation vectors of the other helices are tilted. The link between structural and magnetic properties is underlined via magnetoelastic models. Moreover, molecular beam epitaxy permits the growth of Sm in a metastable dhcp phase. The magnetic structure of dhcp Sm has been elucidated for the first time. In this review, neutron scattering is shown to be a powerful technique to reveal the magnetic structures of rare-earth films.

MAGNETIC PROPERTIES OF TWO-LAYERS FILMS,

DTIC Science & Technology

DATA STORAGE SYSTEMS, METAL FILMS), (*THIN FILM STORAGE DEVICES, MAGNETIC PROPERTIES ), VAPOR PLATING, VACUUM APPARATUS, NICKEL ALLOYS, IRON ALLOYS, COBALT ALLOYS, ANISOTROPY, MULTIPLE OPERATION, USSR

Friction and hardness of gold films deposited by ion plating and evaporation

NASA Technical Reports Server (NTRS)

Miyoshi, K.; Spalvins, T.; Buckley, D. H.

1983-01-01

Sliding friction experiments were conducted with ion-plated and vapor-deposited gold films on various substrates in contact with a 0.025-mm-radius spherical silicon carbide rider in mineral oil. Hardness measurements were also made to examine the hardness depth profile of the coated gold on the substrate. The results indicate that the hardness is influenced by the depth of the gold coating from the surface. The hardness increases with an increase in the depth. The hardness is also related to the composition gradient in the graded interface between the gold coating and the substrate. The graded interface exhibited the highest hardness resulting from an alloy hardening effect. The coefficient of friction is inversely related to the hardness, namely, the load carrying capacity of the surface. The greater the hardness that the metal surface possesses, the lower is the coefficient of friction. The graded interface exhibited the lowest coefficient of friction.

Direct laser interference patterning of magnetic thin films

NASA Astrophysics Data System (ADS)

Aktag, Aliekber

Recently, patterned magnetic thin films have attracted much attention for a variety of applications such as high density magnetic recording, magnetoresistive sensing, and magnetic random access memories. In the case of magnetic recording, one scheme calls for the films to be patterned into single domain "dots", where every dot represents a thermally stable bit. In this thesis, we extended a technique called direct laser interference patterning (DLIP), originally developed by Polushkin and co-workers, to pattern and locally modify the materials properties of magnetic thin films. In this technique, a high-intensity Nd:YAG pulse laser beam was split into two, three, or four beams, which are then recombined to interfere on a sample surface. The interference intensity maxima can modify the local materials properties of the film through local "annealing" or, more drastically, by ablation. We carried out some preliminary investigations of the DLIP process in several films including co-sputtered Co-C, amorphous Dy/Co:SiO2 multilayers, and Co/SiO2 multilayers in order to refine our techniques. We successfully produced regular arrays of lines, dots, or antidots formed by ablation of the thin film. The preliminary studies also showed that, in the regime of more modest pulse energies, it is possible to modify the magnetic properties of the films without noticeably changing the film topography. We then prepared perpendicular magnetic anisotropy Co/Pt multilayers with a SiO x passivation layer and applied DLIP at fairly modest intensities to pattern the film. We then studied the structural and magnetic changes that occurred in some detail. X-ray diffraction scans showed the Co/Pt:SiO x multilayer films to be nanocrystalline before and after patterning. Atomic force microscopy images showed no evidence for topographic changes of the Co/Pt:SiOx during patterning. In contrast, magnetic force microscopy showed regular periodic dot arrays, indicating that the local magnetic

Relationship between thin-film bond strength as measured by a scratch test, and indentation hardness for bonding agents.

PubMed

Kusakabe, Shusuke; Rawls, H Ralph; Hotta, Masato

2016-03-01

To evaluate thin-film bond strength between a bonding agent and human dentin, using a scratch test, and the characteristics and accuracy of measurement. One-step bonding agents (BeautiBond; Bond Force; Adper Easy Bond; Clearfil tri-S Bond) and two-step bonding agents (Cleafil SE Bond; FL-Bond II) were investigated in this study. Flat dentin surfaces were prepared for extracted human molars. The dentin surfaces were ground and bonding agents were applied and light cured. The thin-film bond strength test of the specimens was evaluated by the critical load at which the coated bonding agent failed and dentin appeared. The scratch mark sections were then observed under a scanning electron microscope. Indentation hardness was evaluated by the variation in depth under an applied load of 10gf. Data were compared by one-way ANOVA with the Scheffé's post hoc multiple comparison test (p<0.05). In addition, thin-film bond strength and indentation hardness were analyzed using analysis of correlation and covariance. The thin-film bond strength of two-step bonding agents were found to be significantly higher than that of one-step bonding agents with small standard deviations. Scratch marks consistently showed adhesive failure in the vicinity of the bonding agent/dentin interface. The indentation hardness showed a trend that two-step bonding agents have greater hardness than one-step bonding agents. A moderately significant correlation (r(2)=0.31) was found between thin-film bond strength and indentation hardness. Thin-film bond strength test is a valid and reliable means of evaluating bond strength in the vicinity of the adhesive interface and is more accurate than other methods currently in use. Further, the thin-film bond strength is influenced by the hardness of the cued bonding agent. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of deposition temperature on morphological, magnetic and elastic properties of ultrathin Co49Pt51 films

NASA Astrophysics Data System (ADS)

Si Abdallah, F.; Chérif, S. M.; Bouamama, Kh.; Roussigné, Y.; Hsu, J.-H.

2018-03-01

Morphological, magnetic and elastic properties of 5 nm-thick Co49Pt51 films, sputtered on glass substrates, with 20 nm-thick Ta (seed) and Pt (buffer) layers were studied as function of the deposition temperature Td ranging between room temperature and 350° C. Atomic and magnetic force microscopy, vibrating sample magnetometer and Brillouin light scattering techniques were used to investigate the root mean square (RMS) roughness, the magnetic domain configuration, the coercive field (Hc), the perpendicular magnetic anisotropy (PMA), and the dynamic magnetic and elastic properties of the films with Td. The results show that surface uniformity was enhanced since the RMS roughness decreases with Td while magnetic domains typical of films with high PMA are observed. Hc and PMA are found to sensibly increase with Td. The dynamic magnetization behavior is characterized by magnetic modes related with the co-existence of hard and soft magnetic areas within the samples. The elastic properties of the stack were first analyzed by means of a model describing the main variation of the elastic wave frequencies within the frame of weighted average thickness, density, Young's modulus and Poisson coefficient of all the layers constituting the stacks. However, while Hc and PMA keep increasing with Td, a more precise experimental analysis of the mechanical behavior shows that the group velocity starts increasing and finally decreases with Td, suggesting that knowledge of the influence of Td on the mechanical properties of each individual layer composing the stack is required to obtain a more accurate analysis.

Magnetic properties of partially oxidized Fe films

NASA Astrophysics Data System (ADS)

Garcia, Miguel Angel; Lopez-Dominguez, Victor; Hernando, Antonio

Hybrid magnetic nanostructures exhibit appealing properties due to interface and proximity effects. A simple and interesting system of hybrid magnetic nanomaterials are partially oxidized ferromagnetic films. We have fabricated Fe films by thermal evaporation and performed a partial oxidation to magnetite (Fe3O4) by annealing in air at different times and temperatures. The magnetic properties of the films evolve from those of pure metallic iron to pure magnetite, showing intermediate states where the proximity effects control the magnetic behavior. At some stages, the magnetization curves obtained by SQUID and MOKE magnetometry exhibit important differences due to the dissimilar contribution of both phases to the magneto-optical response of the system This work has been supported by the Ministerio Español de Economia y Competitividad (MINECO) MAT2013-48009-C4-1. V.L.D and M.A.G. acknowledges financial support from BBVA foundation.

2D Magnetic Texture Analysis of Co-Cu Films

NASA Astrophysics Data System (ADS)

Bayirli, Mehmet; Karaagac, Oznur; Kockar, Hakan; Alper, Mursel

2017-05-01

The magnetic textures for the produced magnetic materials are important concepts in accordance with technical applications. Therefore, the aim of this article is to determine 2D magnetic textures of electrodeposited Co-Cu films by the measurement of hysteresis loops at the incremented angles. For that, Co-Cu films were deposited with different Co2+ in the electrolyte. In addition, the easy-axis orientation in the films from the squareness values of the angles, Mp(β) obtained by the hysteresis loops have been numerically studied using the Fourier series analysis. The differences observed in the magnetic easy-axis distributions were attributed to changes of the incorporation of Co in the films with the change of Co2+ in the electrolyte. The coefficients of Fourier series (A0 and A2n ) were also computed for 2D films. It is seen that a systematic and small decrease in A0 and an obvious decrease in A2n (n=1) were observed with increasing incorporated Co in the films. Results imply that interactions cause slightly demagnetization effect accordance with higher incorporation of Co in the films. Furthermore, the crystal structure of the Co-Cu films analysed by X-ray diffraction revealed that the films have dominantly face-centred cubic structure. Film contents analysed by energy-dispersive X-ray spectroscopy and film morphologies observed by scanning electron microscope also support the magnetic texture analysis results found by numerical computation.

Remanent-magnetization decay in CoCr films

NASA Astrophysics Data System (ADS)

Skorjanec, J.; Cottles, V.; Close, J.; Iverson, P.; Edwards, J.; Dahlberg, E. Dan

1990-05-01

The decay of the remanent magnetization of several thin films of CoCr has been studied using the extraordinary Hall effect as a probe of the component of the magnetization perpendicular to the plane of the films. Consistent with previous measurements of CoCr, the remanent magnetization decays quasilogarithmically with time after the removal of a saturating magnetic field. In the present work the effect of a magnetically soft keeper layer on the decay of the magnetization has been investigated. It is found that the keeper layer does not affect the remanent magnetization nor does it decrease the decay rate of the perpendicular magnetization. This result indicates that the soft keeper layer is not effective at screening the demagnetization field on a length scale relevant to the decay-producing fields.

Mechanics of hard films on soft substrates

NASA Astrophysics Data System (ADS)

Lu, Nanshu

2009-12-01

Flexible electronics have been developed for various applications, including paper-like electronic readers, rollable solar cells, electronic skins etc., with the merits of light weight, low cost, large area, and ruggedness. The systems may be subject to one-time or repeated large deformation during manufacturing and application. Although organic materials can be highly deformable, currently they are not able to fulfill every electronic function. Therefore flexible electronic devices are usually made as organic/inorganic hybrids, with diverse materials, complex architecture, and micro features. While the polymer substrates can recover from large deformations, thin films of electronic materials such as metals, silicon, oxides, and nitrides fracture at small strains, usually less than a few percent. Mechanics of hard films on soft substrates hence holds the key to build high-performance and highly reliable flex circuits. This thesis investigates the deformability and failure mechanisms of thin films of metallic and ceramic materials supported by soft polymeric substrates through combined experimental, theoretical, and numerical methods. When subject to tension, micron-thick metal films with stable microstructure and strong interfacial adhesion to the substrate can be stretched beyond 50% without forming cracks. They eventually rupture by a ductile transgranular fracture which involves simultaneous necking and debonding. When metal films become nanometer-thick, intergranular fracture dominates the failure mode at elongations of only a few percent. Unannealed films show unstable microstructure at room temperature when subject to mechanical loading. In this case, films also rupture at small strains but by three concurrent mechanisms: deformation-induced grain growth, strain localization at large grains, and simultaneous debonding. In contrast to metal films, ceramic films rupture by brittle mechanisms. The only way to prevent rupture of ceramic films is to reduce the

Full magnetization process of 3d-4f hard magnetic materials in ultrahigh magnetic fields (an example: RFe11Ti)

NASA Astrophysics Data System (ADS)

Kuz'min, M. D.; Zvezdin, A. K.

1998-03-01

The prospects of using the free-powder high-field magnetization method for a quantitative study of inter-sublattice exchange interaction in 3d-4f hard magnetic materials are analyzed. Such analysis is stimulated by the availability of pulsed magnetic fields ˜103 T generated by implosion. Particular attention is paid to effects due to magnetic anisotropy, essential for these materials. The 3d-4f ferrimagnets where both sublattices contribute positively to the easy-axis anisotropy are shown to be suitable objects of study by the free-powder method, because (i) anomalies in their low-temperature magnetizatization curves are sharp and (ii) anisotropic effects can be allowed for without quantitative knowledge of the anisotropy constants. Moreover, these "good" hard magnetic materials can be brought into metamagnetic regime by diluting the rare earth sublattice with nonmagnetic yttrium; then, regardless of the anisotropy constants, the magnetization curve at low temperatures has just one steplike anomaly, the threshold field being equal exactly to the molecular field acting on the rare earth.

Composite nanoplatelets combining soft-magnetic iron oxide with hard-magnetic barium hexaferrite

NASA Astrophysics Data System (ADS)

Primc, D.; Makovec, D.

2015-01-01

By coupling two different magnetic materials inside a single composite nanoparticle, the shape of the magnetic hysteresis can be engineered to meet the requirements of specific applications. Sandwich-like composite nanoparticles composed of a hard-magnetic Ba-hexaferrite (BaFe12O19) platelet core in between two soft-magnetic spinel iron oxide maghemite (γ-Fe2O3) layers were synthesized using a new, simple and inexpensive method based on the co-precipitation of Fe3+/Fe2+ ions in an aqueous suspension of hexaferrite core nanoparticles. The required close control of the supersaturation of the precipitating species was enabled by the controlled release of the Fe3+ ions from the nitrate complex with urea ([Fe((H2N)2C&z.dbd;O)6](NO3)3) and by using Mg(OH)2 as a solid precipitating agent. The platelet Ba-hexaferrite nanoparticles of different sizes were used as the cores. The controlled coating resulted in an exclusively heterogeneous nucleation and the topotactic growth of the spinel layers on both basal surfaces of the larger hexaferrite nanoplatelets. The direct magnetic coupling between the core and the shell resulted in a strong increase of the energy product |BH|max. Ultrafine core nanoparticles reacted with the precipitating species and homogeneous product nanoparticles were formed, which differ in terms of the structure and composition compared to any other compound in the BaO-Fe2O3 system.By coupling two different magnetic materials inside a single composite nanoparticle, the shape of the magnetic hysteresis can be engineered to meet the requirements of specific applications. Sandwich-like composite nanoparticles composed of a hard-magnetic Ba-hexaferrite (BaFe12O19) platelet core in between two soft-magnetic spinel iron oxide maghemite (γ-Fe2O3) layers were synthesized using a new, simple and inexpensive method based on the co-precipitation of Fe3+/Fe2+ ions in an aqueous suspension of hexaferrite core nanoparticles. The required close control of the

The correlation between nano-hardness and elasticity and fullerene-like clusters in hydrogenated amorphous carbon films

NASA Astrophysics Data System (ADS)

Wang, Yongfu; Gao, Kaixiong; Wang, Qi; Zhang, Junyan

2018-01-01

Fullerene-like hydrogenated carbon films have outstanding mechanical and frictional properties, but their structures have never enjoyed elaboration. In this study, we investigate the relation between nano-hardness and elasticity and fullerene-like clusters by changing energy supply form (direct current and pulse) and H2 concentration in the feedstock. It is found that the films have a network of H-rich amorphous carbon and H-poor or -deficient fullerene-like carbon, and the network change can affect hardness and elastic recovery. This is due to the energy minimization process of the film growing system in a very short pulse period at low temperature.

Examining the Magnetic Properties of LaCoO3 Thin Films Using Magnetic Force Microscopy

NASA Astrophysics Data System (ADS)

Berg, Morgann; Posadas, Agham; de Lozanne, Alex; Demkov, Alexander

2011-03-01

In contrast to the non-magnetic ground state of bulk LaCo O3 (LCO) at low temperatures, ferromagnetism has been observed in elastically strained thin film specimens. The origins of ferromagnetism in strained LCO thin films have been obscured by conflicting experimental results. Pulsed laser deposition (PLD) is the current standard of preparation techniques used to grow thin films of LCO, but results from thin film LCO samples prepared by PLD have been questioned on the basis of chemical inhomogeneity and film defects. Using magnetic force microscopy, we investigate the microscale magnetic properties of strained thin films of LCO prepared by molecular beam epitaxy and deposited on lanthanum aluminate and strontium titanate substrates. We observe these properties across a temperature range surrounding the Curie temperature (Tc ~ 80 K) and compare our results to global magnetic characteristics of these films as measured by a SQUID magnetometer. Supported by NSF-DMR and NSF-IGERT.

Tailoring magnetic properties of Co nanocluster assembled films using hydrogen

NASA Astrophysics Data System (ADS)

Romero, C. P.; Volodin, A.; Paddubrouskaya, H.; Van Bael, M. J.; Van Haesendonck, C.; Lievens, P.

2018-07-01

Tailoring magnetic properties in nanocluster assembled cobalt (Co) thin films was achieved by admitting a small percentage of H2 gas (∼2%) into the Co gas phase cluster formation chamber prior to deposition. The oxygen content in the films is considerably reduced by the presence of hydrogen during the cluster formation, leading to enhanced magnetic interactions between clusters. Two sets of Co samples were fabricated, one without hydrogen gas and one with hydrogen gas. Magnetic properties of the non-hydrogenated and the hydrogen-treated Co nanocluster assembled films are comparatively studied using magnetic force microscopy and vibrating sample magnetometry. When comparing the two sets of samples the considerably larger coercive field of the H2-treated Co nanocluster film and the extended micrometer-sized magnetic domain structure confirm the enhancement of magnetic interactions between clusters. The thickness of the antiferromagnetic CoO layer is controlled with this procedure and modifies the exchange bias effect in these films. The exchange bias shift is lower for the H2-treated Co nanocluster film, which indicates that a thinner antiferromagnetic CoO reduces the coupling with the ferromagnetic Co. The hydrogen-treatment method can be used to tailor the oxidation levels thus controlling the magnetic properties of ferromagnetic cluster-assembled films.

Thickness dependence of the magnetic anisotropy and dynamic magnetic response of ferromagnetic NiFe films

NASA Astrophysics Data System (ADS)

Silva, E. F.; Corrêa, M. A.; Della Pace, R. D.; Plá Cid, C. C.; Kern, P. R.; Carara, M.; Chesman, C.; Alves Santos, O.; Rodríguez-Suárez, R. L.; Azevedo, A.; Rezende, S. M.; Bohn, F.

2017-05-01

We investigate the thickness dependence of the magnetic anisotropy and dynamic magnetic response of ferromagnetic NiFe films. We go beyond quasi-static measurements and focus on the dynamic magnetic response by considering three complementary techniques: the ferromagnetic resonance, magnetoimpedance and magnetic permeability measurements. We verify remarkable modifications in the magnetic anisotropy, i.e. the well-known behavior of in-plane uniaxial magnetic anisotropy systems gives place to a complex magnetic behavior as the thickness increases, and splits the films in two groups according to the magnetic properties. We identify magnetoimpedance and magnetic permeability curves with multiple resonance peaks, as well as the evolution of the ferromagnetic resonance absorption spectra, as fingerprints of strong changes of the magnetic properties associated to the vanishing of the in-plane magnetic anisotropy and to the emergence of non-homogeneous magnetization configuration, local anisotropies and out-of-plane anisotropy contribution arisen as a consequence of the non-uniformities of the stress stored in the film as the thickness is increased and/or to the columnar growth of the film. We interpret the experimental results in terms of the structural and morphological properties, quasi-static magnetic behavior, magnetic domain structure and different mechanisms governing the magnetization dynamics at distinct frequency ranges.

Modification of the structural and magnetic properties of granular FePt films by seed layer conditioning

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wicht, S., E-mail: s.wicht@ifw-dresden.de; TU Dresden, Institut für Werkstoffwissenschaft, Helmholtzstraße 10, D-01069 Dresden; Neu, V.

2015-01-07

The steadily increasing amount of digital information necessitates the availability of reliable high capacity magnetic data storage. Here, future hard disk drives with extended areal storage densities beyond 1.0 Tb/in{sup 2} are envisioned by using high anisotropy granular and chemically L1{sub 0}-ordered FePt (002) perpendicular media within a heat-assisted magnetic recording scheme. Perpendicular texturing of the [001] easy axes of the individual grains can be achieved by using MgO seed layers. It is therefore investigated, if and how an Ar{sup +} ion irradiation of the MgO seed layer prior to the deposition of the magnetic material influences the MgO surfacemore » properties and hereby the FePt [001] texture. Structural investigations reveal a flattening of the seed layer surface accompanied by a change in the morphology of the FePt grains. Moreover, the fraction of small second layer particles and the degree of coalescence of the primarily deposited FePt grains strongly increases. As for the magnetic performance, this results in a reduced coercivity along the magnetic easy axis (out of plane) and in enhanced hard axis (in-plane) remanence values. The irradiation induced changes in the magnetic properties of the granular FePt-C films are traced back to the accordingly modified atomic structure of the FePt-MgO interface region.« less

Structural and magnetic studies of Cr doped nickel ferrite thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Panwar, Kalpana, E-mail: kalpanapanwar99@gmail.com; Department of Physics, Govt. Women Engg. College, Ajmer-305002; Heda, N. L.

We have studied the structural and magnetic properties of Cr doped nickel ferrite thin films deposited on Si (100) and Si (111) using pulsed laser deposition technique. The films were deposited under vacuum and substrate temperature was kept at 700°C. X-ray diffraction analysis revealed that films on both substrates have single phase cubic spinel structure. However, the film grown on Si (111) shows better crystalline behavior. Fourier transform infrared spectroscopy suggests that films on both substrates have mixed spinel structure. These films show magnetic hysteresis behavior and magnetization value of film on Si (100) is larger than that on Simore » (111). It turns out that structural and magnetic properties of these two films are correlated.« less

Magnetic nonuniformity and thermal hysteresis of magnetism in a manganite thin film.

PubMed

Singh, Surendra; Fitzsimmons, M R; Lookman, T; Thompson, J D; Jeen, H; Biswas, A; Roldan, M A; Varela, M

2012-02-17

We measured the chemical and magnetic depth profiles of a single crystalline (La(1-x)Pr(x))(1-y)Ca(y)MnO(3-δ) (x=0.52±0.05, y=0.23±0.04, δ=0.14±0.10) film grown on a NdGaO(3) substrate using x-ray reflectometry, electron microscopy, electron energy-loss spectroscopy, and polarized neutron reflectometry. Our data indicate that the film exhibits coexistence of different magnetic phases as a function of depth. The magnetic depth profile is correlated with a variation of chemical composition with depth. The thermal hysteresis of ferromagnetic order in the film suggests a first-order ferromagnetic transition at low temperatures.

Magnetization reversal of in-plane uniaxial Co films and its dependence on epitaxial alignment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Idigoras, O., E-mail: o.idigoras@nanogune.eu; Suszka, A. K.; Berger, A.

2014-02-28

This work studies the influence of crystallographic alignment onto magnetization reversal in partially epitaxial Co films. A reproducible growth sequence was devised that allows for the continuous tuning of grain orientation disorder in Co films with uniaxial in-plane anisotropy by the controlled partial suppression of epitaxy. While all stable or meta-stable magnetization states occurring during a magnetic field cycle exhibit a uniform magnetization for fully epitaxial samples, non-uniform states appear for samples with sufficiently high grain orientation disorder. Simultaneously with the occurrence of stable domain states during the magnetization reversal, we observe a qualitative change of the applied field anglemore » dependence of the coercive field. Upon increasing the grain orientation disorder, we observe a disappearance of transient domain wall propagation as the dominating reversal process, which is characterized by an increase of the coercive field for applied field angles away from the easy axis for well-ordered epitaxial samples. Upon reaching a certain disorder threshold level, we also find an anomalous magnetization reversal, which is characterized by a non-monotonic behavior of the remanent magnetization and coercive field as a function of the applied field angle in the vicinity of the nominal hard axis. This anomaly is a collective reversal mode that is caused by disorder-induced frustration and it can be qualitatively and even quantitatively explained by means of a two Stoner-Wohlfarth particle model. Its predictions are furthermore corroborated by Kerr microscopy and by Brillouin light scattering measurements.« less

Integrated CoPtP Permanent Magnets for MEMS Electromagnetic Energy Harvesting Applications

NASA Astrophysics Data System (ADS)

Mallick, Dhiman; Roy, Saibal

2016-10-01

This work reports the development of integrated Co rich CoPtP hard magnetic material for MEMS applications such as Electromagnetic Vibration Energy Harvesting. We report a new method of electrodeposition compared to the conventional DC plating, involving a combination of forward and reverse pulses for optimized deposition of Co rich CoPtP hard magnetic material. This results in significant improvements in the microstructure of the developed films as the pulse reverse plated films are smooth, stress free and uniform. Such improvements in the structural properties are reflected in the hard magnetic properties of the material as well. The intrinsic coercivities of the pulse reverse deposited film are more than 6 times higher for both in-plane and out-of-plane measurement directions and the squareness of the hysteresis loops also improve due to the similar reasons.

Magnetic fields are causing small, but significant changes of the radiochromic EBT3 film response to 6 MV photons.

PubMed

Delfs, Björn; Schoenfeld, Andreas A; Poppinga, Daniela; Kapsch, Ralf-Peter; Jiang, Ping; Harder, Dietrich; Poppe, Björn; Looe, Hui Khee

2018-01-31

light experiencing the largest transmission through EBT3 films remained unaltered after film exposure in the magnetic fields. The observed small modification of the OD versus D curve of the radiochromic film EBT3 in the range up to 20 Gy and 1.42 T, hardly exceeding the experimental uncertainty margin, numerically confirms other recent studies on EBT3 film. A stronger magnetic field effect had been observed with the previous product EBT2 exposed to 60 Co gamma radiation at 0.35 T.

Magnetic damping phenomena in ferromagnetic thin-films and multilayers

NASA Astrophysics Data System (ADS)

Azzawi, S.; Hindmarch, A. T.; Atkinson, D.

2017-11-01

Damped ferromagnetic precession is an important mechanism underpinning the magnetisation processes in ferromagnetic materials. In thin-film ferromagnets and ferromagnetic/non-magnetic multilayers, the role of precession and damping can be critical for spintronic device functionality and as a consequence there has been significant research activity. This paper presents a review of damping in ferromagnetic thin-films and multilayers and collates the results of many experimental studies to present a coherent synthesis of the field. The terms that are used to define damping are discussed with the aim of providing consistent definitions for damping phenomena. A description of the theoretical basis of damping is presented from early developments to the latest discussions of damping in ferromagnetic thin-films and multilayers. An overview of the time and frequency domain methods used to study precessional magnetisation behaviour and damping in thin-films and multilayers is also presented. Finally, a review of the experimental observations of magnetic damping in ferromagnetic thin-films and multilayers is presented with the most recent explanations. This brings together the results from many studies and includes the effects of ferromagnetic film thickness, the effects of composition on damping in thin-film ferromagnetic alloys, the influence of non-magnetic dopants in ferromagnetic films and the effects of combining thin-film ferromagnets with various non-magnetic layers in multilayered configurations.

Imaging Local Magnetic Domain Rearrangement in Strained LaCoO3 Thin Films Using Magnetic Force Microscopy

NASA Astrophysics Data System (ADS)

Berg, Morgann; Leon, Neliza; Posadas, Agham; Lee, Alfred; Kim, Jeehoon; de Lozanne, Alex; Demkov, Alex

2012-02-01

Previous studies we have conducted on thin films of lanthanum cobaltate (LCO) under tensile strain have revealed a tendency toward local magnetic domain rearrangement into streak-like configurations near the ferromagnetic to paramagnetic phase transition. Moreover, the persistence of these streak-like characteristics to lower temperatures after field-cooling appears to be linked to the strength of the applied magnetic field in which these films are field-cooled. This tendency has not yet been verified for thin films of LCO under compressive strain which could indicate whether this magnetic domain rearrangement is intrinsic to thin film samples of LCO or is merely an effect of tensile strain. Using magnetic force microscopy, we investigate the microscale magnetic properties of a thin film of LCO under compressive strain, prepared by molecular beam epitaxy and deposited on a lanthanum aluminate substrate. We observe these properties across a wide temperature range and compare our results to global magnetic characteristics of this film as measured by a SQUID magnetometer.

Co-based amorphous thin films on silicon with soft magnetic properties

NASA Astrophysics Data System (ADS)

Masood, Ansar; McCloskey, P.; Mathúna, Cian Ó.; Kulkarni, S.

2018-05-01

The present work investigates the emergence of multiple modes in the high-frequency permeability spectrum of Co-Zr-Ta-B amorphous thin films. Amorphous thin films of different thicknesses (t=100-530 nm) were deposited by DC magnetron sputtering. Their static and dynamic soft magnetic properties were investigated to explore the presence of multi-magnetic phases in the films. A two-phase magnetic behavior of the thicker films (≥333 nm) was revealed by the in-plane hysteresis loops. Multiple resonance peaks were observed in the high-frequency permeability spectrum of the thicker films. The thickness dependent multiple resonance peaks below the main ferromagnetic resonance (FMR) can be attributed to the two-phase magnetic behaviors of the films.

Thermally assisted magnetization reversal in sub-micron sized magnetic thin films

NASA Astrophysics Data System (ADS)

Koch, Roger H.

2000-03-01

We have measured the rate of thermally assisted magnetization reversal of sub-micron sized magnetic thin film elements. For fields H just less than the zero-temperature coercive field H_C, the probability of reversal, P^exps (t), increases for short times, t, achieves a maximum value, and then decreases exponentially. The temperature dependence of the reversal is consistent with a temperature independent barrier height. Micromagnetic simulations exhibit the same behavior, and show that the reversal for a film without disorder proceeds through the annihilation of two domain walls that move from opposite sides of the sample. The behavior of P^exps (t) can be understood using a simple ``energy-ladder" model of thermal activation. In this model, the film reverses its magnetization direction by thermally activating (reversibly) through a ladder of intermediate metastable states. The measured data are consistent with there being a handful of these states in the energy landscape of the film. These states are a result of the disorder in the film and we will show micromagnetic simulation movies depicting this behavior. In collaboration with G. Grinstein, G.A. Keefe, Yu Lu, P.L. Trouilloud, W. J. Gallagher, S.S.P. Parkin, S. Ingvarson, and G. Xaio

Probing Active Nematic Films with Magnetically Manipulated Colloids

NASA Astrophysics Data System (ADS)

Rivas, David; Chen, Kui; Henry, Robert; Reich, Daniel; Leheny, Robert

We study microtubule-based extensile active nematic films using rod-like and disk-shaped magnetic colloids to probe the mechanical and hydrodynamic properties of this quasi-two dimensional out-of-equilibrium system. The active nematics are driven by molecular motors that hydrolyze ATP and cause sliding motion between microtubular bundles. This motion produces a dynamic nematic director field, which continuously creates pairs of +1/2 and -1/2 defects. In the absence of externally applied forces or torques, we observe that the magnetic rods in contact with the films align with the local director, indicating the existence of mechanical coupling between the film and probe. By applying known magnetic torques to the rods and observing their rotation with respect to the director, we gain insight into this coupling. We also find that by rotating magnetic microdisks using magnetic fields, hydrodynamic flows are produced that compete with the films' intrinsic flow, leading to significant effects on the director field and the defect landscape. At certain rotation rates, the disks produce a vortex-like structure in the director field and cause the creation and shedding of defects from the disk boundary.

Design and Implementation of a Hall Effect Sensor Array Applied to Recycling Hard Drive Magnets

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kisner, Roger; Lenarduzzi, Roberto; Killough, Stephen M

Rare earths are an important resource for many electronic components and technologies. Examples abound including Neodymium magnets used in mobile devices and computer hard drives (HDDs), and a variety of renewable energy technologies (e.g., wind turbines). Approximately 21,000 metric tons of Neodymium is processed annually with less than 1% being recycled. An economic system to assist in the recycling of magnet material from post-consumer goods, such as Neodymium Iron Boron magnets commonly found in hard drives is presented. A central component of this recycling measurement system uses an array of 128 Hall Effect sensors arranged in two columns to detectmore » the magnetic flux lines orthogonal to the HDD. Results of using the system to scan planar shaped objects such as hard drives to identify and spatially locate rare-earth magnets for removal and recycling from HDDs are presented. Applications of the sensor array in other identification and localization of magnetic components and assemblies will be presented.« less

Magnetization-induced second- and third-harmonic generation in transparent magnetic films

NASA Astrophysics Data System (ADS)

Ohkoshi, Shin-Ichi; Shimura, Jusuke; Ikeda, Katsuyoshi; Hashimoto, Kazuhito

2005-01-01

We describe the magnetization-induced second-harmonic (SH) generation in (FeIIxCrII1-x)1.5[CrIII(CN)6]. 7.5H2O and the magnetization-induced third-harmonic (TH) generation in Y1.5Bi1.5Fe3.8Al1.2O12 (Bi, Al:YIG). The polarization plane of a SH wave from a (FeIIxCrII1-x)1.5[CrIII(CN)6].7.5H2O film was rotated by an applied external magnetic field. This SH rotation is ascribed to the interaction between the electric polarization along the out-of-plane and spontaneous magnetizations. In particular, the magnetic linear term χijkLmagn(1) contributed to the SH rotation. Applying a longitudinal external magnetic field to a Bi,Al:YIG magnetic film rotated the polarization plane of the TH wave. This TH rotation is understood by the contribution of the magnetic term of χyxxxZmagn(1) in a third-order nonlinear optical susceptibility.

Influence of Stoichiometry on the Magnetic Properties of Electrodeposited Thin Films of Iron Chromium Hexacyanide Based Molecular Magnet

NASA Astrophysics Data System (ADS)

Bhatt, Pramod; Yusuf, S. M.; Mukadam, M. D.; Yakhmi, J. V.

2010-12-01

Present paper deals with investigation of magnetic properties of electrochemically prepared crystalline films of Prussian blue analogues (PBAs) based molecular magnet, KjFek[Cr(CN)6]lṡmH2O with varying film stoichiometry. Film stoichiometry has been varied by depositing films at -0.5, -0.6 and -0.8 V at room temperature. It has been observed that the alkali metal ions are introduced into the films just by using suitable electrode voltage, contrary to usual method where alkali metal ions are intentionally introduced into the lattice by using additional compounds of alkali metals as starting materials. Magnetization data show ferromagnetic (parallel spin ordering) nature of all deposited film with the Curie temperature (TC)˜11 K for Fe1.5[Cr(CN)6]ṡ7.5H2O film. Changes in the magnetic properties such as TC, coercivity and saturation magnetization have also been observed with variation in film stoichiometry. The observed changes are mainly attributed to the inclusion of potassium ion, which alters FeII/CrIII ratio, thus magnetic properties.

Magnetic fields are causing small, but significant changes of the radiochromic EBT3 film response to 6 MV photons

NASA Astrophysics Data System (ADS)

Delfs, Björn; Schoenfeld, Andreas A.; Poppinga, Daniela; Kapsch, Ralf-Peter; Jiang, Ping; Harder, Dietrich; Poppe, Björn; Khee Looe, Hui

2018-02-01

vector of polarised light experiencing the largest transmission through EBT3 films remained unaltered after film exposure in the magnetic fields. The observed small modification of the OD versus D curve of the radiochromic film EBT3 in the range up to 20 Gy and 1.42 T, hardly exceeding the experimental uncertainty margin, numerically confirms other recent studies on EBT3 film. A stronger magnetic field effect had been observed with the previous product EBT2 exposed to 60Co gamma radiation at 0.35 T.

Mechanochemical synthesis of LaCo5 magnetically hard anisotropic powder

NASA Astrophysics Data System (ADS)

Gabay, A. M.; Hadjipanayis, G. C.

2014-05-01

LaCo5 particles were prepared from La2O3 and Co powders processed in the presence of Ca as a reducing agent and a CaO dispersant. After high-energy ball milling followed by a short annealing at 900 °C, the particles exhibited a room-temperature intrinsic coercivity of 24.5 kOe. Separation of the hard magnetic particles with water is accompanied by the release of hydrogen and this leads to replacement of the LaCo5 structure by various LaCo5Hx hydrides. The LaCo5 structure was restored by removing hydrogen via vacuum annealing. The resulting particles were polydispersed with an average size of 540 nm and crystallographically anisotropic; they exhibited a remanent magnetization of 83.8 emu g-1 (8.7 kG) and a coercivity of 9.6 kOe. The dramatic improvement of the hard magnetic properties as compared to those obtained by standard milling is attributed to a lower density of anisotropy defects at the surface of the mechanochemically synthesized particles. This advantage may allow for the commercial utilization of more abundant/less expensive raw materials for permanent magnets.

Perpendicular magnetic anisotropy in amorphous NdxCo1 -x thin films studied by x-ray magnetic circular dichroism

NASA Astrophysics Data System (ADS)

Cid, R.; Alameda, J. M.; Valvidares, S. M.; Cezar, J. C.; Bencok, P.; Brookes, N. B.; Díaz, J.

2017-06-01

The origin of perpendicular magnetic anisotropy (PMA) in amorphous NdxCo1 -x thin films is investigated using x-ray magnetic circular dichroism (XMCD) spectroscopy at the Co L2 ,3 and Nd M4 ,5 edges. The magnetic orbital and spin moments of the 3 d cobalt and 4 f neodymium electrons were measured as a function of the magnetic field orientation, neodymium concentration, and temperature. In all the studied samples, the magnetic anisotropy of the neodymium subnetwork is always oriented perpendicular to the plane, whereas the anisotropy of the orbital moment of cobalt is in the basal plane. The ratio Lz/Sz of the neodymium 4 f orbitals changes with the sample orientation angle, being higher and closer to the atomic expected value at normal orientation and smaller at grazing angles. This result is well explained by assuming that the 4 f orbital is distorted by the effect of an anisotropic crystal field when it is magnetized along its hard axis, clearly indicating that the 4 f states are not rotationally invariant. The magnetic anisotropy energy associated to the neodymium subnetwork should be proportional to this distortion, which we demonstrate is accessible by applying the XMCD sum rules for the spin and intensity at the Nd M4 ,5 edges. The analysis unveils a significant portion of neodymium atoms magnetically uncoupled to cobalt, i.e., paramagnetic, confirming the inhomogeneity of the films and the presence of a highly disordered neodymium rich phase already detected by extended x-ray-absorption fine structure (EXAFS) spectroscopy. The presence of these inhomogeneities is inherent to the evaporation preparation method when the chosen concentration in the alloy is far from its eutectic concentrations. An interesting consequence of the particular way in which cobalt and neodymium segregates in this system is the enhancement of the cobalt spin moment which reaches 1.95 μB in the sample with the largest segregation.

Magnetic properties of ultrathin tetragonal Heusler D022-Mn3Ge perpendicular-magnetized films

NASA Astrophysics Data System (ADS)

Sugihara, A.; Suzuki, K. Z.; Miyazaki, T.; Mizukami, S.

2015-05-01

We investigated the crystal structure and magnetic properties of Manganese-germanium (Mn3Ge) films having the tetragonal D022 structure, with varied thicknesses (5-130 nm) prepared on chromium (Cr)-buffered single crystal MgO(001) substrates. A crystal lattice elongation in the in-plane direction, induced by the lattice mismatch between the D022-Mn3Ge and the Cr buffer layer, increased with decreasing thickness of the D022-Mn3Ge layer. The films exhibited clear magnetic hysteresis loops with a squareness ratio close to unity, and a step-like magnetization reversal even at a 5-nm thickness under an external field perpendicular to the film's plane. The uniaxial magnetic anisotropy constant of the films showed a reduction to less than 10 Merg/cm3 in the small thickness range (≤20 nm), likely due to the crystal lattice elongation in the in-plane direction.

Indirect Coupling of Magnetic Layers via Domain Wall Fringing fields

NASA Astrophysics Data System (ADS)

Parkin, Stuart

2001-03-01

Ferromagnetic films separated by thin metallic spacer layers are usually coupled through an indirect exchange interaction which oscillates in sign between ferro and antiferromagnetic coupling as a function of the spacer layer thickness^1. For both such metallic systems, and for multilayered systems in which the ferromagnetic films are separated by thin insulating layers, correlated roughness of the magnetic layers gives rise to a weak ferromagnetic coupling via dipole fields. Another type of dipolar coupling mechanism, which has largely been ignored, is that arising from domain wall fringing fields. These fields can be locally very large^2 and can result in the demagnetization of ferromagnetic films which are nominally highly coercive ("hard") in sandwiches comprised of "hard" and "soft" ferromagnetic layers. When the moment of the soft layer is reversed back and forth in small magnetic fields, much too small to affect the moment of the hard layer, substantial local fringing fields from domain walls created in the soft film gradually result in the demagnetization of the hard film. In some cases the moment of the hard layer decays in an oscillatory manner as it is successively partially demagnetized and remagnetized. This process has been observed on both macroscopic and microscopic length scales using SQUID magnetometry and high resolution photoemission electron microscopy, respectively^3. Magnetic interactions from domain wall fringing fields may be very important for magnetic devices, especially, magnetoresistance sensors and memory elements. [1] S.S.P. Parkin, N. More and K.P. Roche, Phys. Rev. Lett. 64, 2304 (1990); S.S.P. Parkin, Phys. Rev. Lett., 67, 3598 (1991). [2] L. Thomas, M. Samant and S.S.P. Parkin, Phys. Rev. Lett. 84, 1816 (2000). [3] L. Thomas, J Lüning, A. Scholl, F. Nolting, S. Anders, J. Stöhr and S.S.P. Parkin, Phys. Rev. Lett. 84, 3462 (2000).

Magnetization pinning in conducting films demonstrated using broadband ferromagnetic resonance

NASA Astrophysics Data System (ADS)

Kostylev, M.; Stashkevich, A. A.; Adeyeye, A. O.; Shakespeare, C.; Kostylev, N.; Ross, N.; Kennewell, K.; Magaraggia, R.; Roussigné, Y.; Stamps, R. L.

2010-11-01

The broadband microstrip ferromagnetic resonance (FMR), cavity FMR, and Brillouin light scattering spectroscopy techniques have been applied for detection and characterization of a magnetic inhomogeneity in a film sample. In the case of a 100 nm thick permalloy film, an additional magnetically depleted top sublayer has been detected due to pinning effect it produces on the magnetization in the bulk of the film. The pinning results in appearance of an exchange standing spin wave mode in the broadband FMR absorption spectrum, whose amplitudes are different depending on whether the film or the film substrate faces the microstrip transducer. Comparison of the experimental amplitudes for this mode with results of our theory for both film placements revealed that the depleted layer is located at the film surface facing away from the film substrate. Subsequent broadband FMR characterization of a large number of other presumably single-layer films with thicknesses in the range 30-100 nm showed the same result.

Thickness Dependence of Magnetic Blocking in Granular Metallic Thin Films

NASA Astrophysics Data System (ADS)

Wang, J.-Q.; Zhao, Z.-D.; Whittenburg, S. L.

2002-03-01

Inter-particle interaction among single domain nano-size magnetic particles embedded in nonmagnetic matrix was studied. Attention was paid to concentrated Cu-Co granular thin films with a fixed magnetic volume fraction. By analyzing theoretical models and comparing with experimental results, we studied a dimensional constraint on the magnetic properties and found that as the film thickness reduces toward thin limit the inter-particle interaction plays important roles in modifying magnetic behavior. Experimental evidence showed that the peak temperature of the susceptibility for Cu80Co20 granular thin films strongly depends on the film thickness in the range of 0 120 nm (1). It was also observed that the spontaneous magnetization of the Co phase varies with the thickness though particle size remains constant. We calculated the dipolar interaction energy among magnetic particles including far-neighbor interaction for films with different thickness values. The calculation revealed that the interaction energy varies across the film from edge to edge and the average interaction energy is strongly dependent on film thickness. Good quantitative agreement of the calculated energy curve with the experimental blocking curve was achieved after taking the magnetization variation into account. In the calculation it is assumed the existence of 100 nm sized domain structures in granular film as demonstrate (2) by previous studies. *supported by DoD/DARPA grant No. MDA972-97-1-003. (1) L. M. Malkinski, J.-Q. Wang, et al, Appl. Phys. Lett. 75, 844 (1999). (2) A. Gavrin, et al, Appl. Phys. Lett. 66, 1683 (1995); Y. J. Chen, et al, Appl. Phys. Lett. 72, 2472 (1998).

Surface and magnetic characteristics of Ni-Mn-Ga/Si (100) thin film

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kumar, S. Vinodh; Pandyan, R. Kodi; Mahendran, M., E-mail: manickam-mahendran@tce.edu, E-mail: perialangulam@gmail.com

2016-05-23

Polycrystalline Ni-Mn-Ga thin films have been deposited on Si (100) substrate with different film thickness. The influence of film thickness on the phase structure and magnetic domain of the films has been examined by scanning electron microscope, atomic force microscopy and magnetic force microscopy. Analysis of structural parameters indicates that the film at lower thickness exhibits the coexistence of both austenite and martensite phase, whereas at higher thickness L1{sub 2} cubic non magnetic phase is noticed. The grains size and the surface roughness increase along with the film thickness and attain the maximum of 45 nm and 34.96 nm, respectively.more » At lower film thickness, the magnetic stripe domain is found like maze pattern with dark and bright images, while at higher thickness the absence of stripe domains is observed. The magnetic results reveal that the films strongly depend on their phase structure and microstructure which influence by the film thickness.« less

Surface and magnetic characteristics of Ni-Mn-Ga/Si (100) thin film

NASA Astrophysics Data System (ADS)

Kumar, S. Vinodh; Raja, M. Manivel; Pandi, R. Senthur; Pandyan, R. Kodi; Mahendran, M.

2016-05-01

Polycrystalline Ni-Mn-Ga thin films have been deposited on Si (100) substrate with different film thickness. The influence of film thickness on the phase structure and magnetic domain of the films has been examined by scanning electron microscope, atomic force microscopy and magnetic force microscopy. Analysis of structural parameters indicates that the film at lower thickness exhibits the coexistence of both austenite and martensite phase, whereas at higher thickness L12 cubic non magnetic phase is noticed. The grains size and the surface roughness increase along with the film thickness and attain the maximum of 45 nm and 34.96 nm, respectively. At lower film thickness, the magnetic stripe domain is found like maze pattern with dark and bright images, while at higher thickness the absence of stripe domains is observed. The magnetic results reveal that the films strongly depend on their phase structure and microstructure which influence by the film thickness.

Fabrication of scrolled magnetic thin film patterns

NASA Astrophysics Data System (ADS)

Min, Seonggi; Lim, Jin-Hee; Gaffney, John; Kinttle, Kristofer; Wiley, John B.; Malkinski, Leszek

2012-04-01

Magnetic film scrolls have been fabricated via a deterministic release of rectangular patterns of bimetallic Ti (20 nm)/Ni (20 , 30 or 40 nm) films from a sacrificial Cu underlayer. The diameter of the scrolls varied from 2.64 μm to 4.28 μm with increasing thickness of the Ni layer from 20 to 40 nm. This behavior was found to be consistent with the model of bilayered film with interfacial strain between the Ti and Ni layers of about Δɛ = 0.01. Changing the geometry of the patterns from flat patterns to scrolls led to changes in their magnetic properties.

Magnetoelastic Properties of Magnetic Thin Films Using the Magnetooptic Kerr Effect

NASA Astrophysics Data System (ADS)

Mayo, Elizabeth; Lederman, David

1998-03-01

The magnetoelastic properties of Co and Fe thin films were measured using the magnetooptic Kerr effect (MOKE). Films were grown via magnetron sputtering on thin mica substrates. Magnetization loops were measured using MOKE with the magnetic field along different in-plane directions. Subsequently, the samples were mounted on a cylindrical sample holder, which imposed a well-defined strain to the film. This caused the magnetization loops to change dramatically due to the magnetoelastic coefficient of the thin film materials. The effects of the surface roughness and film thickness will also be discussed.

Thin film metallic sensors in an alternating magnetic field for magnetic nanoparticle hyperthermia cancer therapy

NASA Astrophysics Data System (ADS)

Hussein, Z. A.; Boekelheide, Z.

In magnetic nanoparticle hyperthermia in an alternating magnetic field for cancer therapy, it is important to monitor the temperature in situ. This can be done optically or electrically, but electronic measurements can be problematic because conducting parts heat up in a changing magnetic field. Microfabricated thin film sensors may be advantageous because eddy current heating is a function of size, and are promising for further miniaturization of sensors and fabrication of arrays of sensors. Thin films could also be used for in situ magnetic field sensors or for strain sensors. For a proof of concept, we fabricated a metallic thin film resistive thermometer by photolithographically patterning a 500Å Au/100Å Cr thin film on a glass substrate. Measurements were taken in a solenoidal coil supplying 0.04 T (rms) at 235 kHz with the sensor parallel and perpendicular to the magnetic field. In the parallel orientation, the resistive thermometer mirrored the background heating from the coil, while in the perpendicular orientation self-heating was observed due to eddy current heating of the conducting elements by Faraday's law. This suggests that metallic thin film sensors can be used in an alternating magnetic field, parallel to the field, with no significant self-heating.

Exploring the Hard and Soft X-ray Emission of Magnetic Cataclysmic Variables

NASA Astrophysics Data System (ADS)

de Martino, D.; Anzolin, G.; Bonnet-Bidaud, J.-M.; Falanga, M.; Matt, G.; Mouchet, M.; Mukai, K.; Masetti, N.

2009-05-01

A non-negligible fraction of galactic hard (>20 keV) X-ray sources were identified as CVs of the magnetic Intermediate Polar type in INTEGRAL, SWIFT and RXTE surveys, that suggests a still hidden but potentially important population of faint hard X-ray sources. Simbol-X has the unique potential to simultaneously characterize their variable and complex soft and hard X-ray emission thus allowing to understand their putative role in galactic populations of X-ray sources.

Control of magnetization reversal in oriented strontium ferrite thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Roy, Debangsu, E-mail: debangsu@physics.iisc.ernet.in; Anil Kumar, P. S.

2014-02-21

Oriented Strontium Ferrite films with the c axis orientation were deposited with varying oxygen partial pressure on Al{sub 2}O{sub 3}(0001) substrate using Pulsed Laser Deposition technique. The angle dependent magnetic hysteresis, remanent coercivity, and temperature dependent coercivity had been employed to understand the magnetization reversal of these films. It was found that the Strontium Ferrite thin film grown at lower (higher) oxygen partial pressure shows Stoner-Wohlfarth type (Kondorsky like) reversal. The relative importance of pinning and nucleation processes during magnetization reversal is used to explain the type of the magnetization reversal with different oxygen partial pressure during growth.

One-step synthesis of magnetic chitosan polymer composite films

NASA Astrophysics Data System (ADS)

Cesano, Federico; Fenoglio, Gaia; Carlos, Luciano; Nisticò, Roberto

2015-08-01

In this study, a magnetic iron oxide-chitosan composite film is synthesized by one-step method and thoroughly investigated in order to better understand its inorganic/organic properties. A deep physico-chemical characterization of the magnetic films has been performed. In particular, the material composition was evaluated by means of XRD and ATR-FTIR spectroscopy, whereas the thermal stability and the subsequent inorganic phase transitions involving iron oxide species were followed by TGA analyses carried out at different experimental conditions (i.e. inert and oxidative atmosphere). The magnetic properties of the films were tested at the bulk and at the surface level, performing respectively magnetization hysteresis curve and magnetic force microscopy (MFM) surface mapping. Results indicate that the synthesized material can be prepared through a very simple synthetic procedure and suggests that it can be successfully applied for instance to environmental applications, such as the adsorption of contaminants from solid and liquid media thanks to its pronounced magnetic properties, which favour its recover.

Functionally gradient hard carbon composites for improved adhesion and wear

NASA Astrophysics Data System (ADS)

Narayan, Roger Jagdish

A new approach is proposed for fabricating biomedical devices that last longer and are more biocompatible than those presently available. In this approach, a bulk material is chosen that has desirable mechanical properties (low modulus, high strength, high ductility and high fatigue strength). This material is coated with corrosion-resistant, wear-resistant, hard, and biocompatible hard carbon films. One of the many forms of carbon, tetrahedral amorphous carbon, consists mainly of sp3-bonded atoms. Tetrahedral amorphous carbon possesses properties close to diamond in terms of hardness, atomic smoothness, and inertness. Tetrahedral amorphous carbon and diamond films usually contain large amounts of compressive and sometimes tensile stresses; adhesive failure from these stresses has limited widespread use of these materials. This research involves processing, characterization and modeling of functionally gradient tetrahedral amorphous carbon and diamond composite films on metals (cobalt-chromium and titanium alloys) and polymers (polymethylmethacrylate and polyethylene) used in biomedical applications. Multilayer discontinuous thin films of titanium carbide, titanium nitride, aluminum nitride, and tungsten carbide have been developed to control stresses and graphitization in diamond films. A morphology of randomly interconnected micron sized diamond crystallites provides increased toughness and stress reduction. Internal stresses in tetrahedral amorphous carbon were reduced via incorporation of carbide forming elements (silicon and titanium) and noncarbide forming elements (copper, platinum, and silver). These materials were produced using a novel target design during pulsed laser deposition. These alloying atoms reduce hardness and sp3-bonded carbon content, but increase adhesion and wear resistance. Silver and platinum provide the films with antimicrobial properties, and silicon provides bioactivity and aids bone formation. Bilayer coatings were created that couple

Direct observation of local magnetic properties in strain engineered lanthanum cobaltate thin films

NASA Astrophysics Data System (ADS)

Park, S.; Wu, Weida; Freeland, J. W.; Ma, J. X.; Shi, J.

2009-03-01

Strain engineered thin film devices with emergent properties have significant impacts on both technical application and material science. We studied strain-induced modification of magnetic properties (Co spin state) in epitaxially grown lanthanum cobaltate (LaCoO3) thin films with a variable temperature magnetic force microscopy (VT-MFM). The real space observation confirms long range magnetic ordering on a tensile-strained film and non-magnetic low-spin configuration on a low-strained film at low temperature. Detailed study of local magnetic properties of these films under various external magnetic fields will be discussed. Our results also demonstrate that VT-MFM is a very sensitive tool to detect the nanoscale strain induced magnetic defects.

Magnetization-induced second-harmonic generation in electrochemically synthesized magnetic films of ternary metal Prussian blue analogs

NASA Astrophysics Data System (ADS)

Ikeda, Katsuyoshi; Ohkoshi, Shin-ichi; Hashimoto, Kazuhito

2003-02-01

We observed magnetic field effects on transmitted second-harmonic generation (SHG) in electrochemically synthesized (FexIICr1-xII)1.5[CrIII(CN)6]ṡ7.5H2O magnetic films. These films showed a variety of temperature dependences for SH intensities below magnetic phase transition temperatures (TC). The SH intensity for x=0.25 increased monotonically with decreasing temperature and that for x=0.13 exhibited a minimum value around the magnetic compensation temperature under a zero magnetic field. These temperature dependences resembled those of the absolute value of magnetization, indicating that the magnetic strain of the films is responsible for the increase in SH below TC. In addition, the polarization of SH light was rotated by an applied external magnetic field. The observed SH rotation angle of 1.3° was much larger than the Faraday rotation angle of 0.079° at 388 nm. This SH rotation can be understood by the mechanism of magnetization-induced SHG caused by interaction between the electric polarization along the out-of-plane of film and spontaneous magnetization. The magnetic linear term [χijkLmagn(1)] contributed particularly to the SH rotation. The value of the magnetic linear tensor component relative to the crystallographic tensor component [|χyyyXmagn(1)|/|χzyycr], which induced the SH rotation, was 0.023 at 50 K under 10 kOe.

Evolution of structural and magnetic properties of amorphous CoFeB film with thermal annealing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gupta, Ranjeeta; Gupta, Ajay; Gupta, Mukul

2013-08-14

Evolution of structural and magnetic properties of amorphous Co{sub 68}Fe{sub 14}B{sub 18} thin film with thermal annealing has been studied. Initially, the film exhibits a structural relaxation as evidenced by annihilation of excess free volume and an increase in topological short range order. Annealing at 473 K results in precipitation of primary phase followed by formation of boride phase at a still higher temperature of 598 K. Iron preferentially precipitates out in the primary phase, resulting in the formation of bcc Co{sub 58}Fe{sub 41}. This suggests an affinity of Co towards B. Such affinity between Co and B is evidencedmore » even in the as-deposited film, using hard x-ray photoelectron spectroscopy (HAXPES) measurements. As-deposited film exhibits an in-plane uniaxial magnetic anisotropy which disappears at a temperature well beyond crystallization temperature, suggesting that the origin of anisotropy is mainly a chemical short range order in the system. Variation in the coercivity with thermal annealing can be understood in terms of random anisotropy model. Precise measurement of Fe self-diffusion using neutron reflectivity shows that diffusion length associated with annihilation of excess free volume in the film is about 0.5 nm. This agrees with the length scale of structural fluctuations in amorphous alloys. Secondary ion mass spectrometry measurements show that thermal annealing results in depletion of B in the region of the interface with the substrate, with associated faster Fe diffusion in this region. This faster diffusion of Fe may be a possible cause of preferential crystallization of the film in the interfacial region as seen in some earlier studies.« less

Phase separation in NiCrN coatings induced by N2 addition in the gas phase: A way to generate magnetic thin films by reactive sputtering of a non-magnetic NiCr target

NASA Astrophysics Data System (ADS)

Luciu, I.; Duday, D.; Choquet, P.; Perigo, E. A.; Michels, A.; Wirtz, T.

2016-12-01

Magnetic coatings are used for a lot of applications from data storage in hard discs, spintronics and sensors. Meanwhile, magnetron sputtering is a process largely used in industry for the deposition of thin films. Unfortunately, deposition of magnetic coatings by magnetron sputtering is a difficult task due to the screening effect of the magnetic target lowering the magnetic field strength of the magnet positioned below the target, which is used to generate and trap ions in the vicinity of the target surface to be sputtered. In this work we present an efficient method to obtain soft magnetic thin films by reactive sputtering of a non-magnetic target. The aim is to recover the magnetic properties of Ni after dealloying of Ni and Cr due to the selective reactivity of Cr with the reactive nitrogen species generated during the deposition process. The effects of nitrogen content on the dealloying and DC magnetron sputtering (DCMS) deposition processes are studied here. The different chemical compositions, microstructures and magnetic properties of DCMS thin films obtained by sputtering in reactive gas mixtures with different ratios of Ar/N2 from a non-magnetic Ni-20Cr target have been determined. XPS data indicate that the increase of nitrogen content in the films has a strong influence on the NiCr phase decomposition into Ni and CrN, leading to ferromagnetic coatings due to the Ni phase. XRD results show that the obtained Ni-CrN films consist of a metallic fcc cubic Ni phase mixed with fcc cubic CrN. The lattice parameter decreases with the N2 content and reaches the theoretical value of the pure fcc-Ni, when Cr is mostly removed from the Ni-Cr phase. Dealloying of Cr from a Ni80-Cr20 solid solution is achieved in our experimental conditions and the deposition of Ni ferromagnetic coatings embedding CrN from a non-magnetic target is possible with reactive DC magnetron sputtering.

Influence of magnetic disorders on quantum anomalous Hall effect in magnetic topological insulator films beyond the two-dimensional limit

NASA Astrophysics Data System (ADS)

Xing, Yanxia; Xu, Fuming; Cheung, King Tai; Sun, Qing-feng; Wang, Jian; Yao, Yugui

2018-04-01

Quantum anomalous Hall effect (QAHE) has been experimentally realized in magnetic topological insulator (MTI) thin films fabricated on magnetically doped {({{Bi}},{{Sb}})}2{{{Te}}}3. In an MTI thin film with the magnetic easy axis along the normal direction (z-direction), orientations of magnetic dopants are randomly distributed around the magnetic easy axis, acting as magnetic disorders. With the aid of the non-equilibrium Green's function and Landauer–Büttiker formalism, we numerically study the influence of magnetic disorders on QAHE in an MTI thin film modeled by a three-dimensional tight-binding Hamiltonian. It is found that, due to the existence of gapless side surface states, QAHE is protected even in the presence of magnetic disorders as long as the z-component of magnetic moment of all magnetic dopants are positive. More importantly, such magnetic disorders also suppress the dissipation of the chiral edge states and enhance the quality of QAHE in MTI films. In addition, the effect of magnetic disorders depends very much on the film thickness, and the optimal influence is achieved at certain thickness. These findings are new features for QAHE in three-dimensional systems, not present in two-dimensional systems.

Development of High Resistive and High Magnetization Soft Thin Film and Fabrication of Thin Film Inductors

DTIC Science & Technology

2004-11-01

properties of Co- doped ZnO nanocluster films", .J. of Appl. Phys. in press, 2005 2. Presentations (contributed): Conference Contributions: 1) Y. Qiang...gigahertz band applications. The effects of substrates bias, sputter parameters, and seed-layer have thoroughly been investigated. The magnetic...Adequate properties of soft magnetic thin film were evaluated by an analytical calculation [1] to meet the requirement for gigahertz band thin-film

The effect of underlayers on the reversal of perpendicularly magnetized multilayer thin films for magnetic micro- and nanoparticles

NASA Astrophysics Data System (ADS)

Vemulkar, T.; Mansell, R.; Petit, D. C. M. C.; Cowburn, R. P.; Lesniak, M. S.

2017-01-01

Perpendicularly magnetized microparticles offer the ability to locally apply high torques on soft matter under an applied magnetic field. These particles are engineered to have a zero remanence magnetic configuration via synthetic antiferromagnetic coupling using a Ru coupling interlayer. The flexibility offered by the top down thin film fabrication process in a CoFeB/Pt perpendicular thin film is demonstrated by using the Pt interlayer thicknesses in a Pt/Ru/Pt antiferromagnetic coupling multilayer to tune the applied magnetic field value of the easy axis spin-flip transition to saturation and hence the field value at which the magnetic particles are magnetically activated via a distinct transition to saturation. The importance of a Ta buffer layer on the magnetic behavior of the stack is shown. While Au capping layers are desirable for biotechnology applications, we demonstrate that they can drastically change the nucleation and propagation of domains in the film, thereby altering the reversal behavior of the thin film. The effect of Au underlayers on a multilayer thin film composed of repeated motifs of a synthetic antiferromagnetic building block is also investigated.

Magnetization reversal mechanism of magnetic tunnel junctions

NASA Astrophysics Data System (ADS)

Liu, Cun-Ye; Li, Jian; Wang, Yue; Chen, Jian-Yong; Xu, Qing-Yu; Ni, Gang; Sang, Hai; Du, You-Wei

2002-01-01

Using the ion-beam-sputtering technique, we have fabricated Fe/Al2O3/Fe magnetic tunnelling junctions (MTJs). We have observed double-peaked shapes of curves, which have a level summit and a symmetrical feature, showing the magnetoresistance of the junction as a function of applied field. We have measured the tunnel conductance of MTJs which have insulating layers of different thicknesses. We have studied the dependence of the magnetoresistance of MTJs on tunnel conductance. The microstructures of hard- and soft-magnetic layers and interfaces of ferromagnets and insulators were probed. Analysing the influence of MJT microstructures, including those having clusters or/and granules in magnetic and non-magnetic films, a magnetization reversal mechanism (MRM) is proposed, which suggests that the MRM of tunnelling junctions may be explained by using a group-by-group reversal model of magnetic moments of the mesoscopical particles. We discuss the influence of MTJ microstructures, including those with clusters or/and granules in the ferromagnetic and non-magnetic films, on the MRM.

LC and ferromagnetic resonance in soft/hard magnetic microwires

NASA Astrophysics Data System (ADS)

Tian, Bin; Vazquez, Manuel

2015-12-01

The magnetic behavior of soft/hard biphase microwires is introduced here. The microwires consist of a Co59.1Fe14.8Si10.2B15.9 soft magnetic nucleus and a Co90Ni10 hard outer shell separated by an intermediate insulating Pyrex glass microtube. By comparing the resistance spectrums of welding the ends of metallic core (CC) or welding the metallic core and outer shell (CS) to the connector, it is found that one of the two peaks in the resistance spectrum is because the LC resonance depends on the inductor and capacitors in which one is the capacitor between the metallic core and outer shell, and the other is between the outer shell and connector. Correspondingly, another peak is for the ferromagnetic resonance of metallic core. After changing the capacitance of the capacitors, the frequency of LC resonance moves to high frequency band, and furthermore, the peak of LC resonance in the resistance spectrum disappeared. These magnetostatically coupled biphase systems are thought to be of large potential interest as sensing elements in sensor devices.

Magnetization and anisotropy of cobalt ferrite thin films

NASA Astrophysics Data System (ADS)

Eskandari, F.; Porter, S. B.; Venkatesan, M.; Kameli, P.; Rode, K.; Coey, J. M. D.

2017-12-01

The magnetization of thin films of cobalt ferrite frequently falls far below the bulk value of 455 kA m-1 , which corresponds to an inverse cation distribution in the spinel structure with a significant orbital moment of about 0.6 μB that is associated with the octahedrally coordinated Co2+ ions. The orbital moment is responsible for the magnetostriction and magnetocrystalline anisotropy and its sensitivity to imposed strain. We have systematically investigated the structure and magnetism of films produced by pulsed-laser deposition on different substrates (Ti O2 , MgO, MgA l2O4 , SrTi O3 , LSAT, LaAl O3 ) and as a function of temperature (500 -700 °C) and oxygen pressure (10-4-10 Pa ) . Magnetization at room-temperature ranges from 60 to 440 kA m-1 , and uniaxial substrate-induced anisotropy ranges from +220 kJ m-3 for films on deposited on MgO (100) to -2100 kJ m-3 for films deposited on MgA l2O4 (100), where the room-temperature anisotropy field reaches 14 T. No rearrangement of high-spin Fe3+ and Co2+ cations on tetrahedral and octahedral sites can reduce the magnetization below the bulk value, but a switch from Fe3+ and Co2+ to Fe2+ and low-spin Co3+ on octahedral sites will reduce the low-temperature magnetization to 120 kA m-1 , and a consequent reduction of Curie temperature can bring the room-temperature value to near zero. Possible reasons for the appearance of low-spin cobalt in the thin films are discussed.

Angular tuning of the magnetic birefringence in rippled cobalt films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Arranz, Miguel A., E-mail: MiguelAngel.Arranz@uclm.es; Colino, José M.

We report the measurement of magnetically induced birefringence in rippled Co films. For this purpose, the magneto-optical properties of ion beam eroded ferromagnetic films were studied using Kerr magnetometry and magnetic birefringence in the transmitted light intensity. Upon sufficient ion sculpting, these ripple surface nanostructures developed a defined uniaxial anisotropy in the in-plane magnetization, finely tuning the magnetic birefringence effect. We have studied its dependence on the relative orientation between the ripple direction and the magnetic field, and found this effect to be dramatically correlated with the capability to neatly distinguish the mechanisms for the in-plane magnetization reversal, i.e., rotationmore » and nucleation. This double refraction corresponds univocally to the two magnetization axes, parallel and perpendicular to the ripples direction. We have also observed that tuned birefringence in stack assemblies of rippled Co films, which enables us to technically manipulate the number and direction of refraction axes.« less

A Geometric Interpretation of the Effective Uniaxial Anisotropy Field in Magnetic Films

NASA Astrophysics Data System (ADS)

Kozlov, V. I.

2018-01-01

It is shown that the effective uniaxial anisotropy field that is usually applied in thin magnetic films (TMFs), which is noncollinear to the magnetization vector, is insufficient for deeper understanding of these processes, although it explains many physical processes in films. The analysis of the magnetization discontinuity in films under certain conditions yields the component of the effective uniaxial anisotropy field collinear to the magnetization vector. This component explains the magnetization discontinuity and allows one to speak of the total effective uniaxial anisotropy field in TMFs.

Effects of surface topography on magnetization reversal of magnetic thin films.

PubMed

Girgis, E; Pogossian, S P; Benkhedar, M L

2006-04-01

The influence of the created surface roughness on the coercivity of magnetic thin films has been investigated. The magnetic thin films (CoFe and alternatively NiFe) are sputtered on top of smooth substrates that were previously covered with an array of considerably rougher lines with one of these materials Pt, Cu, CoFe, and NiFe. The lines have been patterned using optical lithography into arrays that are deposited with different thicknesses varying between 5 nm-15 nm. The lines have been designed to have a very rough edge and seated in two different angles relative to the wafer edge (zero and 45 degrees). Magneto-optic Kerr effect (MOKE) measurements showed two distinct switching fields in the hysteresis loops that are due to magnetic domain wall trapping created by the surface roughness. The magnetization reversal showed a strong dependence on the height, the orientation angle, and the material's type of the created surface roughness (the lines).

Bioactive films of zein/magnetite magnetically stimuli-responsive for controlled drug release

NASA Astrophysics Data System (ADS)

Marín, Tíffany; Montoya, Paula; Arnache, Oscar; Pinal, Rodolfo; Calderón, Jorge

2018-07-01

The Zein films in two configurations with magnetite nanoparticles (zein/NPs) and magnetite-acetaminophen (zein/NPs/Drug) were used as magnetically stimuli-responsive systems to propose a model of controlled release by dissolution and diffusion mechanism. Composite material films of zein/NPs and zein/NPs/Drug were made by dispersion of magnetite nanoparticles into zein solution then solvent casting of the solution on a flat Teflon substrate. The properties of composite films were analyzed by magnetization curves of (MvsH) and measurements of magnetic force microscopy (MFM). Drug release from the zein/NPs/Drug composite films was determined using a type II dissolution apparatus for a period of 2 h under applied magnetic field conditions. In addition, the diffusion mechanism was tested with zein/NPs films into diffusion cell containing acetaminophen solution for 24 h and using a permanent magnet as a remote trigger device. The results showed that the magnetite nanoparticles contained in the zein/NPs and zein/NPs/Drug composite films are stable, i.e., they do not undergo sufficiently high levels of oxidation as to alter their magnetic properties. Furthermore, the dissolution and diffusion results lead us to conclude that zein composite films effectively behave as stimuli-responsive systems triggered by an external magnetic field applied. The result is a model controlled release system whereby drug release can be controlled by adjusting the magnitude of the applied magnetic field.

Structure and magnetization of Co4N thin film

NASA Astrophysics Data System (ADS)

Pandey, Nidhi; Gupta, Mukul; Gupta, Rachana; Rajput, Parasmani; Stahn, Jochen

2018-02-01

In this work, we studied the local structure and the magnetization of Co4N thin films deposited by a reactive dc magnetron sputtering process. The interstitial incorporation of N atoms in a fcc Co lattice is expected to expand the structure. This expansion yields interesting magnetic properties e.g. a larger magnetic moment (than Co) and a very high value of spin polarization ratio in Co4N . By optimizing the growth conditions, we prepared Co4N film having lattice parameter close to its theoretically predicted value. The N concentration was measured using secondary ion mass spectroscopy. Detailed magnetization measurements using bulk magnetization method and polarized neutron reflectivity confirm that the magnetic moment of Co in Co4N is higher than that of Co.

Growth, structure, morphology, and magnetic properties of Ni ferrite films.

PubMed

Dong, Chunhui; Wang, Gaoxue; Guo, Dangwei; Jiang, Changjun; Xue, Desheng

2013-04-27

The morphology, structure, and magnetic properties of nickel ferrite (NiFe2O4) films fabricated by radio frequency magnetron sputtering on Si(111) substrate have been investigated as functions of film thickness. Prepared films that have not undergone post-annealing show the better spinel crystal structure with increasing growth time. Meanwhile, the size of grain also increases, which induces the change of magnetic properties: saturation magnetization increased and coercivity increased at first and then decreased. Note that the sample of 10-nm thickness is the superparamagnetic property. Transmission electron microscopy displays that the film grew with a disorder structure at initial growth, then forms spinel crystal structure as its thickness increases, which is relative to lattice matching between substrate Si and NiFe2O4.

Magnetic Nonuniformity and Thermal Hysteresis of Magnetism in a Manganite Thin Film [Depth profiling of magnetization and coupling of strain with magnetization in (La 0.4Pr 0.6) 0.67Ca 0.33MnO 3 films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Singh, Surendra; Fitzsimmons, M. R.; Lookman, T.

We measured the chemical and magnetic depth profiles of a single crystalline film grown on a NdGaO 3 substrate using x-ray reflectometry, electron microscopy, electron energy-loss spectroscopy and polarized neutron reflectometry. Our data indicate that the film exhibits coexistence of different magnetic phases as a function of depth. The magnetic depth profile is correlated with a variation of chemical composition with depth. The thermal hysteresis of ferromagnetic order in the film suggests a first order ferromagnetic transition at low temperatures

High-field magnets using high-critical-temperature superconducting thin films

DOEpatents

Mitlitsky, F.; Hoard, R.W.

1994-05-10

High-field magnets fabricated from high-critical-temperature superconducting ceramic (HTSC) thin films which can generate fields greater than 4 Tesla are disclosed. The high-field magnets are made of stackable disk-shaped substrates coated with HTSC thin films, and involves maximizing the critical current density, superconducting film thickness, number of superconducting layers per substrate, substrate diameter, and number of substrates while minimizing substrate thickness. The HTSC thin films are deposited on one or both sides of the substrates in a spiral configuration with variable line widths to increase the field. 4 figures.

High-field magnets using high-critical-temperature superconducting thin films

DOEpatents

Mitlitsky, Fred; Hoard, Ronald W.

1994-01-01

High-field magnets fabricated from high-critical-temperature superconducting ceramic (HTSC) thin films which can generate fields greater than 4 Tesla. The high-field magnets are made of stackable disk-shaped substrates coated with HTSC thin films, and involves maximizing the critical current density, superconducting film thickness, number of superconducting layers per substrate, substrate diameter, and number of substrates while minimizing substrate thickness. The HTSC thin films are deposited on one or both sides of the substrates in a spiral configuration with variable line widths to increase the field.

Spin-Orbit Torque-Assisted Switching in Magnetic Insulator Thin Films with Perpendicular Magnetic Anisotropy

NASA Astrophysics Data System (ADS)

Wu, Mingzhong

As an in-plane charge current flows in a heavy metal film with spin-orbit coupling, it produces a torque that can induce magnetization switching in a neighboring ferromagnetic metal film. Such spin-orbit torque (SOT)-induced switching has been studied extensively in recent years and has shown higher efficiency than switching using conventional spin-transfer torque. This presentation reports the SOT-assisted switching in heavy metal/magnetic insulator systems.1 The experiments made use of Pt/BaFe12O19 bi-layered structures. Thanks to its strong spin-orbit coupling, Pt has been widely used to produce pure spin currents in previous studies. BaFe12O19 is an M-type barium hexagonal ferrite and is often referred as BaM. It is one of the few magnetic insulators with strong magneto-crystalline anisotropy and shows an effective uniaxial anisotropy field of about 17 kOe. It's found that the switching response in the BaM film strongly depends on the charge current applied to the Pt film. When a constant magnetic field is applied in the film plane, the charge current in the Pt film can switch the normal component of the magnetization (M⊥) in the BaM film between the up and down states. The current also dictates the up and down states of the remnant magnetization when the in-plane field is reduced to zero. When M⊥ is measured by sweeping an in-plane field, the response manifests itself as a hysteresis loop, which evolves in a completely opposite manner if the sign of the charge current is flipped. When the coercivity is measured by sweeping an out-of-plane field, its value can be reduced or increased by as much as about 500 Oe if an appropriate charge current is applied. 1. P. Li, T. Liu, H. Chang, A. Kalitsov, W. Zhang, G. Csaba, W. Li, D. Richardson, A. Demann, G. Rimal, H. Dey, J. S. Jiang, W. Porod, S. Field, J. Tang, M. C. Marconi, A. Hoffmann, O. Mryasov, and M. Wu, Nature Commun. 7:12688 doi: 10.1038/ncomms12688 (2016).

Large Electric Field–Enhanced–Hardness Effect in a SiO2 Film

PubMed Central

Revilla, Reynier I.; Li, Xiao-Jun; Yang, Yan-Lian; Wang, Chen

2014-01-01

Silicon dioxide films are extensively used in nano and micro–electromechanical systems. Here we studied the influence of an external electric field on the mechanical properties of a SiO2 film by using nanoindentation technique of atomic force microscopy (AFM) and friction force microscopy (FFM). A giant augmentation of the relative elastic modulus was observed by increasing the localized electric field. A slight decrease in friction coefficients was also clearly observed by using FFM with the increase of applied tip voltage. The reduction of the friction coefficients is consistent with the great enhancement of sample hardness by considering the indentation–induced deformation during the friction measurements. PMID:24681517

Large Electric Field-Enhanced-Hardness Effect in a SiO2 Film

NASA Astrophysics Data System (ADS)

Revilla, Reynier I.; Li, Xiao-Jun; Yang, Yan-Lian; Wang, Chen

2014-03-01

Silicon dioxide films are extensively used in nano and micro-electromechanical systems. Here we studied the influence of an external electric field on the mechanical properties of a SiO2 film by using nanoindentation technique of atomic force microscopy (AFM) and friction force microscopy (FFM). A giant augmentation of the relative elastic modulus was observed by increasing the localized electric field. A slight decrease in friction coefficients was also clearly observed by using FFM with the increase of applied tip voltage. The reduction of the friction coefficients is consistent with the great enhancement of sample hardness by considering the indentation-induced deformation during the friction measurements.

Microstructural, Magnetic Anisotropy, and Magnetic Domain Structure Correlations in Epitaxial FePd Thin Films with Perpendicular Magnetic Anisotropy

NASA Technical Reports Server (NTRS)

Skuza, J. R.; Clavero, C.; Yang, K.; Wincheski, B.; Lukaszew, R. A.

2009-01-01

L1(sub 0)-ordered FePd epitaxial thin films were prepared using dc magnetron sputter deposition on MgO (001) substrates. The films were grown with varying thickness and degree of chemical order to investigate the interplay between the microstructure, magnetic anisotropy, and magnetic domain structure. The experimentally measured domain size/period and magnetic anisotropy in this high perpendicular anisotropy system were found to be correlated following the analytical energy model proposed by Kooy and Enz that considers a delicate balance between the domain wall energy and the demagnetizing stray field energy.

Charged magnetic domain walls as observed in nanostructured thin films: dependence on both film thickness and anisotropy.

PubMed

Favieres, C; Vergara, J; Madurga, V

2013-02-13

The magnetic domain configurations of soft magnetic, nanostructured, pulsed laser-deposited Co films were investigated. Their dependence on both the thickness t (20 nm ≤ t ≤ 200 nm) and the anisotropy was studied. Charged zigzag walls, with a characteristic saw-tooth vertex angle θ, were observed. θ changed with t from θ ≈ 17° to ≈25°, presenting an intermediate sharp maximum that has not been described before. The reduced length of the zigzag walls also exhibited a peak at t ≈ 70 nm. The relationship between the total reduced length and the density energy of the magnetic wall allowed us to establish a change from a Néel-type to a Bloch-type core of the zigzag walls at this thickness, t ≈ 70 nm. We also accounted for the magnetic energy arising from the surface roughness of the thinner films after imaging the film surface morphologies. Moreover, this distinctive behaviour of the zigzag walls of these low-anisotropy films was compared to that of high-anisotropy films.

Ultrahigh hardness and high electrical resistivity in nano-twinned, nanocrystalline high-entropy alloy films

NASA Astrophysics Data System (ADS)

Huo, Wenyi; Liu, Xiaodong; Tan, Shuyong; Fang, Feng; Xie, Zonghan; Shang, Jianku; Jiang, Jianqing

2018-05-01

Nano-twinned, nanocrystalline CoCrFeNi high-entropy alloy films were produced by magnetron sputtering. The films exhibit a high hardness of 8.5 GPa, the elastic modulus of 161.9 GPa and the resistivity as high as 135.1 μΩ·cm. The outstanding mechanical properties were found to result from the resistance of deformation created by nanocrystalline grains and nano-twins, while the electrical resistivity was attributed to the strong blockage effect induced by grain boundaries and lattice distortions. The results lay a solid foundation for the development of advanced films with structural and functional properties combined in micro-/nano-electronic devices.

Growth, structure, morphology, and magnetic properties of Ni ferrite films

PubMed Central

2013-01-01

The morphology, structure, and magnetic properties of nickel ferrite (NiFe2O4) films fabricated by radio frequency magnetron sputtering on Si(111) substrate have been investigated as functions of film thickness. Prepared films that have not undergone post-annealing show the better spinel crystal structure with increasing growth time. Meanwhile, the size of grain also increases, which induces the change of magnetic properties: saturation magnetization increased and coercivity increased at first and then decreased. Note that the sample of 10-nm thickness is the superparamagnetic property. Transmission electron microscopy displays that the film grew with a disorder structure at initial growth, then forms spinel crystal structure as its thickness increases, which is relative to lattice matching between substrate Si and NiFe2O4. PMID:23622034

Static magnetism and thermal switching in randomly oriented L10 FePt thin films

NASA Astrophysics Data System (ADS)

Lisfi, A.; Pokharel, S.; Alqarni, A.; Akioya, O.; Morgan, W.; Wuttig, M.

2018-05-01

Static magnetism and thermally activated magnetic relaxation were investigated in granular FePt films (20 nm-200 nm thick) with random magnetic anisotropy through hysteresis loop, torque curve and magnetization time dependence measurements. While the magnetism of thicker film (200 nm thick) is dominated by a single switching of the ordered L10 phase, thinner film (20 nm) displays a double switching, which is indicative of the presence of the disordered cubic phase. The pronounced behavior of double switching in thinner film suggests that the film grain boundary is composed of soft cubic magnetic phase. The magnetic relaxation study reveals that magnetic viscosity S of the films is strongly dependent on the external applied field and exhibits a maximum value (12 kAm) around the switching field and a vanishing behavior at low (1 kOe) and large (12 kOe) fields. The activation volume of the thermal switching was found to be much smaller than the physical volume of the granular structure due to the incoherent rotation mode of the magnetization reversal mechanism, which is established to be domain wall nucleation.

Magnetic x-ray dichroism in ultrathin epitaxial films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tobin, J.G.; Goodman, K.W.; Cummins, T.R.

1997-04-01

The authors have used Magnetic X-ray Linear Dichroism (MXLD) and Magnetic X-ray Circular Dichroism (MXCD) to study the magnetic properties of epitaxial overlayers in an elementally specific fashion. Both MXLD and MXCD Photoelectron Spectroscopy were performed in a high resolution mode at the Spectromicroscopy Facility of the ALS. Circular Polarization was obtained via the utilization of a novel phase retarder (soft x-ray quarter wave plate) based upon transmission through a multilayer film. The samples were low temperature Fe overlayers, magnetic alloy films of NiFe and CoNi, and Gd grown on Y. The authors results include a direct comparison of highmore » resolution angle resolved Photoelectron Spectroscopy performed in MXLD and MXCD modes as well as structural studies with photoelectron diffraction.« less

Magnetic domains in Tb-Fe-Co thin films under anisotropy tilt

NASA Astrophysics Data System (ADS)

Talapatra, A.; Umadevi, K.; Arout Chelvane, J.; Mohanty, J.; Jayalakshmi, V.

2018-04-01

Tailoring of magnetic domains of Tb-Fe-Co thin films with rapid thermal processing has been reported in this paper. While the as-deposited films show elongated, inter-connected domains with high out-of-plane magnetic phase contrast, the rapid thermal processed films at 550 °C with different time intervals display deterioration of magnetic contrast. A longitudinal extension of domains has been observed with the processing time of 5 min. With subsequent increase in processing time, the domain patterns exhibit considerable decrease in magnetic phase difference combined with strong intermixing between two oppositely magnetized areas. The out-of-plane magnetic contrast is seen to be very weak for the Tb-Fe-Co film processed for 30 min. The domain morphology and the contrast variation have been modeled with micromagnetic simulations, considering the in-plane (along xz plane) tilt of anisotropy axis. The ground state energy profile and the variation in magnetic properties indicate the threshold tilt angle to be around 30 ° wherein the in-plane and out-of-plane squareness ratio and coercivities are comparable and hence the system shows a spin re-orientation behavior at higher tilt angles.

Enhanced magnetic moment in ultrathin Fe-doped CoFe2O4 films

NASA Astrophysics Data System (ADS)

Moyer, J. A.; Vaz, C. A. F.; Kumah, D. P.; Arena, D. A.; Henrich, V. E.

2012-11-01

The effect of film thickness on the magnetic properties of ultrathin Fe-doped cobalt ferrite (Co1-xFe2+xO4) grown on MgO (001) substrates is investigated by superconducting quantum interference device magnetometry and x-ray magnetic linear dichroism, while the distribution of the Co2+ cations between the octahedral and tetrahedral lattice sites is studied with x-ray absorption spectroscopy. For films thinner than 10 nm, there is a large enhancement of the magnetic moment; conversely, the remanent magnetization and coercive fields both decrease, while the magnetic spin axes of all the cations become less aligned with the [001] crystal direction. In particular, at 300 K the coercive fields of the thinnest films vanish. The spectroscopy data show that no changes occur in the cation distribution as a function of film thickness, ruling this out as the origin of the enhanced magnetic moment. However, the magnetic measurements all support the possibility that these ultrathin Fe-doped CoFe2O4 films are transitioning into a superparamagnetic state, as has been seen in ultrathin Fe3O4. A weakening of the magnetic interactions at the antiphase boundaries, leading to magnetically independent domains within the film, could explain the enhanced magnetic moment in ultrathin Fe-doped CoFe2O4 and the onset of superparamagnetism at room temperature.

High quality TmIG films with perpendicular magnetic anisotropy grown by sputtering

NASA Astrophysics Data System (ADS)

Wu, C. N.; Tseng, C. C.; Yeh, S. L.; Lin, K. Y.; Cheng, C. K.; Fanchiang, Y. T.; Hong, M.; Kwo, J.

Ferrimagnetic thulium iron garnet (TmIG) films grown on gadolinium gallium garnet substrates recently showed stress-induced perpendicular magnetic anisotropy (PMA), attractive for realization of quantum anomalous Hall effect (QAHE) of topological insulator (TI) films via the proximity effect. Moreover, current induced magnetization switching of Pt/TmIG has been demonstrated for the development of room temperature (RT) spintronic devices. In this work, high quality TmIG films (about 25nm) were grown by sputtering at RT followed by post-annealing. We showed that the film composition is tunable by varying the growth parameters. The XRD results showed excellent crystallinity of stoichiometric TmIG films with an out-of-plane lattice constant of 1.2322nm, a narrow film rocking curve of 0.017 degree, and a film roughness of 0.2 nm. The stoichiometric films exhibited PMA and the saturation magnetization at RT was 109 emu/cm3 (RT bulk value 110 emu/cm3) with a coercive field of 2.7 Oe. In contrast, TmIG films of Fe deficiency showed in-plane magnetic anisotropy. The high quality sputtered TmIG films will be applied to heterostructures with TIs or metals with strong spin-orbit coupling for novel spintronics.

Low Temperature Chemical Vapor Deposition Of Thin Film Magnets

DOEpatents

Miller, Joel S.; Pokhodnya, Kostyantyn I.

2003-12-09

A thin-film magnet formed from a gas-phase reaction of tetracyanoetheylene (TCNE) OR (TCNQ), 7,7,8,8-tetracyano-P-quinodimethane, and a vanadium-containing compound such as vanadium hexcarbonyl (V(CO).sub.6) and bis(benzene)vanalium (V(C.sub.6 H.sub.6).sub.2) and a process of forming a magnetic thin film upon at least one substrate by chemical vapor deposition (CVD) at a process temperature not exceeding approximately 90.degree. C. and in the absence of a solvent. The magnetic thin film is particularly suitable for being disposed upon rigid or flexible substrates at temperatures in the range of 40.degree. C. and 70.degree. C. The present invention exhibits air-stable characteristics and qualities and is particularly suitable for providing being disposed upon a wide variety of substrates.

Piezoelectric response of a PZT thin film to magnetic fields from permanent magnet and coil combination

NASA Astrophysics Data System (ADS)

Guiffard, B.; Seveno, R.

2015-01-01

In this study, we report the magnetically induced electric field E 3 in Pb(Zr0.57Ti0.43)O3 (PZT) thin films, when they are subjected to both dynamic magnetic induction (magnitude B ac at 45 kHz) and static magnetic induction ( B dc) generated by a coil and a single permanent magnet, respectively. It is found that highest sensitivity to B dc——is achieved for the thin film with largest effective electrode. This magnetoelectric (ME) effect is interpreted in terms of coupling between eddy current-induced Lorentz forces (stress) in the electrodes of PZT and piezoelectricity. Such coupling was evidenced by convenient modelling of experimental variations of electric field magnitude with both B ac and B dc induction magnitudes, providing imperfect open circuit condition was considered. Phase angle of E 3 versus B dc could also be modelled. At last, the results show that similar to multilayered piezoelectric-magnetostrictive composite film, a PZT thin film made with a simple manufacturing process can behave as a static or dynamic magnetic field sensor. In this latter case, a large ME voltage coefficient of under B dc = 0.3 T was found. All these results may provide promising low-cost magnetic energy harvesting applications with microsized systems.

Iron-platinum multilayer thin film reactions to form L1(0) iron-platinum and exchange spring magnets

NASA Astrophysics Data System (ADS)

Yao, Bo

(substrate temperature, periodicity) have a strong influence on the structure (effective interdiffusivity, L1 0 phase volume fraction, grain size, and density) and magnetic properties. The correlation of these parameters suggests that the annealed [Fe/Pt]n multilayer films have limited nuclei, and the subsequent growth of L10 phase is very important to the extent of ordered phase formed. A correlation between the grain size of fcc FePt phase, grain size of the L10 FePt phase, the L10 FePt phase fraction, and magnetic properties strongly suggests that the phase transformation of fcc →L10 is highly dependent on the grain size of the parent fcc FePt phase. A selective phase growth model is proposed to explain the phenomena observed. An investigation of the influence of total film thickness on the phase formation of the L10 FePt phase in [Fe/Pt] n multilayer films and a comparison of this to that of FePt co-deposited alloy films is also conducted. A general trend of greater L1 0 phase formation in thicker films was observed in both types of films. It was further found that the thickness dependence of the structure and of the magnetic properties in [Fe/Pt]n multilayer films is much stronger than that in FePt alloy films. This is related to the greater chemical energy contained in [Fe/Pt]n films than FePt alloy films, which is helpful for the L10 FePt phase growth. However, the initial nucleation temperature of [Fe/Pt]n multilayers and co-deposited alloy films was found to be similar. An investigation of L10 FePt-based exchange spring magnets is presented based on our understanding of the L10 formation in [Fe/Pt] n multilayer films. It is known that exchange coupling is an interfacial magnetic interaction and it was experimentally shown that this interaction is limited to within several nanometers of the interface. A higher degree of order of the hard phase is shown to increase the length scale slightly. Two approaches can be used to construct the magnets. For samples with

Lattice structure and magnetization of LaCoO3 thin films

NASA Astrophysics Data System (ADS)

Rata, A. D.; Herklotz, A.; Schultz, L.; Dörr, K.

2010-07-01

We investigate the structure and magnetic properties of thin films of the LaCoO3 compound. Thin films are deposited by pulsed laser deposition on various substrates in order to tune the strain from compressive to tensile. Single-phase (001) oriented LaCoO3 layers were grown on all substrates despite large misfits. The tetragonal distortion of the films covers a wide range from -2% to 2.8%. Our LaCoO3 films are ferromagnetic with Curie temperature around 85 K, contrary to the bulk. The total magnetic moment is below 1 μ B /Co3+, a value relatively small for an exited spin-state of the Co3+ ions, but comparable to values reported in literature. A correlation of strain states and magnetic moment of Co3+ ions in LaCoO3 thin films is observed.

Effect of recording condition on the diffraction efficiency of magnetic hologram with magnetic garnet films

NASA Astrophysics Data System (ADS)

Nakamura, Yuichi; Takagi, Hiroyuki; Lim, Pang Boey; Inoue, Mitsuteru

2014-09-01

A holographic memory has been attracting attention as recording media with high recording density and high data transfer rate. We have studied the magnetic garnets as a rewritable and long life media for magnetic holography. However, since the signal intensity of reconstructed image was relatively low, the effects of recording conditions on the diffraction efficiency of magnetic hologram were investigated with experiments and the numerical simulation using COMSOL multi-physics. The diffraction efficiency tends to decrease as increasing the spatial frequency, and the use of short pulse laser with the pulse width of 50 ps was found to be effective to achieve high diffraction efficiency. This suggests that the formation of clear magnetic fringe similar to interference pattern can be obtained by the use of short pulse laser since undesirable heat diffusion during radiation does not occur. On the other hand, the diffraction efficiency increased as increasing the film thickness up to 3.1 μm but was saturated in the garnet film thicker than 3.1 μm in the case of spatial frequency of 1500 line pair/mm. The numerical simulation showed that the effective depth of magnetic fringe was limited about 1.8 μm irrespective of the garnet film thickness because the fringes were connected by thermal diffusion near the surface of the film, and the effective depth is limited due to this connection of the magnetic fringe. Avoiding this fringe connection, much higher diffraction efficiency will be achieved.

Investigation of the magnetic properties of Nd-Fe-B based hard magnetic materials

NASA Astrophysics Data System (ADS)

Grössinger, R.; Hilscher, G.; Kirchmayr, H.; Sassik, H.; Strnat, R.; Wiesinger, G.

1985-05-01

Nd-Fe-B type magnets were prepared by a melt spinning technique. The resulting ribbons were used as starting material for plastic bonded aligned powder magnets. The hard magnetic properties were studied in static fields up to 50 kG as well as in pulsed fields up to 150 kG. The coercivity measured on ribbons ( 1H' c) was found for high values to be larger than that obtained from the plastic bonded magnets ( 1Hc), which we attribute to the influence of the grinding procedure. The anisotropy field HA determined by applying the SPD (Singular Point Detection) technique, was found (for υ < 13 m/s) to depend strongly on the wheel velocity υ, however for velocities exceeding this value, HA remained essentially constant (∼ 75 kG). Mössbauer spectra were recorded at room as well as at liquid helium temperature. The different shape of the respective spectra reflects the change of the easy axis with temperature. A phase analysis performed by computer fitting the spectra showed that the amount of Fe-precipitates influences the formation of the coercivity.

Magnetically induced orientation of mesochannels in mesoporous silica films at 30 tesla.

PubMed

Yamauchi, Yusuke; Sawada, Makoto; Komatsu, Masaki; Sugiyama, Atsushi; Osaka, Tetsuya; Hirota, Noriyuki; Sakka, Yoshio; Kuroda, Kazuyuki

2007-12-03

We demonstrate the magnetically induced orientation of mesochannels in mesoporous silica films prepared with low-molecular-weight surfactants under an extremely high magnetic field of 30 T. This process is principally applicable to any type of surfactant that has magnetic anisotropy because such a high magnetic field provides sufficient magnetic energy for smooth magnetic orientation. Hexadecyltrimethylammonium bromide (CTAB) and polyoxyethylene-10-cetyl ether (Brij 56) were used as cationic and nonionic surfactants, respectively. According to XRD and cross-sectional TEM, mesochannels aligned perpendicular to the substrates were observed in films prepared with low-molecular-weight surfactants, although the effect was incomplete. The evolution of these types of films should lead to future applications such as highly sensitive chemical sensors and selective separation.

Magnetic properties of in-plane oriented barium hexaferrite thin films prepared by direct current magnetron sputtering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Xiaozhi; Yue, Zhenxing, E-mail: yuezhx@mail.tsinghua.edu.cn; Meng, Siqin

2014-12-28

In-plane c-axis oriented Ba-hexaferrite (BaM) thin films were prepared on a-plane (112{sup ¯}0) sapphire (Al{sub 2}O{sub 3}) substrates by DC magnetron sputtering followed by ex-situ annealing. The DC magnetron sputtering was demonstrated to have obvious advantages over the traditionally used RF magnetron sputtering in sputtering rate and operation simplicity. The sputtering power had a remarkable influence on the Ba/Fe ratio, the hematite secondary phase, and the grain morphology of the as-prepared BaM films. Under 80 W of sputtering power, in-plane c-axis highly oriented BaM films were obtained. These films had strong magnetic anisotropy with high hysteresis loop squareness (M{sub r}/M{sub s}more » of 0.96) along the in-plane easy axis and low M{sub r}/M{sub s} of 0.03 along the in-plane hard axis. X-ray diffraction patterns and pole figures revealed that the oriented BaM films grew via an epitaxy-like growth process with the crystallographic relationship BaM (101{sup ¯}0)//α-Fe{sub 2}O{sub 3}(112{sup ¯}0)//Al{sub 2}O{sub 3}(112{sup ¯}0)« less

Defect-induced magnetic order in pure ZnO films

NASA Astrophysics Data System (ADS)

Khalid, M.; Ziese, M.; Setzer, A.; Esquinazi, P.; Lorenz, M.; Hochmuth, H.; Grundmann, M.; Spemann, D.; Butz, T.; Brauer, G.; Anwand, W.; Fischer, G.; Adeagbo, W. A.; Hergert, W.; Ernst, A.

2009-07-01

We have investigated the magnetic properties of pure ZnO thin films grown under N2 pressure on a -, c -, and r -plane Al2O3 substrates by pulsed-laser deposition. The substrate temperature and the N2 pressure were varied from room temperature to 570°C and from 0.007 to 1.0 mbar, respectively. The magnetic properties of bare substrates and ZnO films were investigated by SQUID magnetometry. ZnO films grown on c - and a -plane Al2O3 substrates did not show significant ferromagnetism. However, ZnO films grown on r -plane Al2O3 showed reproducible ferromagnetism at 300 K when grown at 300-400°C and 0.1-1.0 mbar N2 pressure. Positron annihilation spectroscopy measurements as well as density-functional theory calculations suggest that the ferromagnetism in ZnO films is related to Zn vacancies.

Thin-film-based scintillators for hard x-ray microimaging detectors: the ScinTAX Project

NASA Astrophysics Data System (ADS)

Rack, A.; Cecilia, A.; Douissard, P.-A.; Dupré, K.; Wesemann, V.; Baumbach, T.; Couchaud, M.; Rochet, X.; Riesemeier, H.; Radtke, M.; Martin, T.

2014-09-01

The project ScinTAX developed novel thin scintillating films for the application in high performance X-ray imaging and subsequent introduced new X-ray detectors to the market. To achieve this aim lutetium orthosilicate (LSO) scintillators doped with different activators were grown successfully by liquid phase epitaxy. The high density of LSO (7.4 g/cm3), the effective atomic number (65.2) and the high light yield make this scintillator highly applicable for indirect X-ray detection in which the ionizing radiation is converted into visible light and then registered by a digital detector. A modular indirect detection system has been developed to fully exploit the potential of this thin film scintillator for radiographic and tomographic imaging. The system is compatible for high-resolution imaging with moderate dose as well as adaptable to intense high-dose applications where radiation hard microimaging detectors are required. This proceedings article shall review the achieved performances and technical details on this high-resolution detector system which is now available. A selected example application demonstrates the great potential of the optimized detector system for hard X-ray microimaging, i.e. either to improve image contrast due to the availability of efficient thin crystal films or to reduce the dose to the sample.

Magnetic domain formation in monolayer nanoparticle films

NASA Astrophysics Data System (ADS)

Maranville, Brian; Krycka, Kathryn; Borchers, Julie; Hogg, Charles; Majetich, Sara; Ijiri, Yumi

2009-03-01

Self-assembled magnetic nanoparticle films offer promise as data storage media, but an understanding of the interactions is missing. Modified Langmuir-Blodgett methods were used to prepare monolayer films of 7 and 11 nm diameter Fe3O4 nanoparticles with large structural domains. Small-angle neutron scattering (SANS) shows a peak at a wavevector Q corresponding to the particle size and spacing, and scattering at intermediate Q indicating possible long-range correlations. We extend to lower Q with off-specular neutron reflectivity, achieving high intensity by sacrificing resolution along one in-plane direction y while retaining high resolution in the other in-plane direction x and the normal direction z. We measure in saturation and zero field to extract magnetic scattering. In high fields, the specular scattering (Qx=0) is increased, consistent with aligned moments. Preliminary results show weak magnetic scattering for nonzero Qx . Since the maximal Qx roughly corresponds to the lowest Q in SANS, the combination of these techniques allows us to quantify field-dependent magnetic domain size.

Crystal-field splittings in rare-earth-based hard magnets: An ab initio approach

NASA Astrophysics Data System (ADS)

Delange, Pascal; Biermann, Silke; Miyake, Takashi; Pourovskii, Leonid

2017-10-01

We apply the first-principles density functional theory + dynamical mean-field theory framework to evaluate the crystal-field splitting on rare-earth sites in hard magnetic intermetallics. An atomic (Hubbard-I) approximation is employed for local correlations on the rare-earth 4 f shell and self-consistency in the charge density is implemented. We reduce the density functional theory self-interaction contribution to the crystal-field splitting by properly averaging the 4 f charge density before recalculating the one-electron Kohn-Sham potential. Our approach is shown to reproduce the experimental crystal-field splitting in the prototypical rare-earth hard magnet SmCo5. Applying it to R Fe12 and R Fe12X hard magnets (R =Nd , Sm and X =N , Li), we obtain in particular a large positive value of the crystal-field parameter A20〈r2〉 in NdFe12N resulting in a strong out-of-plane anisotropy observed experimentally. The sign of A20〈r2〉 is predicted to be reversed by substituting N with Li, leading to a strong out-of-plane anisotropy in SmFe12Li . We discuss the origin of this strong impact of N and Li interstitials on the crystal-field splitting on rare-earth sites.

Magnetic Fe-Co films electroplated in a deep-eutectic-solvent-based plating bath

NASA Astrophysics Data System (ADS)

Yanai, T.; Shiraishi, K.; Watanabe, Y.; Ohgai, T.; Nakano, M.; Suzuki, K.; Fukunaga, H.

2015-05-01

We fabricated Fe-Co films from a deep eutectic solvent (DES)-based plating bath and investigated magnetic properties of the plated films. The plating baths were obtained by stirring the mixture of choline chloride, ethylene glycol, FeCl2.4H2O, and CoCl2.6H2O. The composition of the plated films depended on the amount of FeCl2.4H2O in the plating bath, and Fe content of the films was varied from 0 to 100 at. %. Depending on the Fe content, the saturation magnetization and the coercivity of the films varied. The Fe76Co24 film shows high saturation magnetization and smooth surface, and the change in the saturation magnetization shows good agreement with the expected change by the Slater-Pauling curve. High current efficiency (>90%) could be obtained in the wide film composition. From these results, we concluded that the DES-based plating bath is one of effective baths for the Fe-Co films with high current efficiency.

Defect characterization and magnetic properties in un-doped ZnO thin film annealed in a strong magnetic field

NASA Astrophysics Data System (ADS)

Ning, Shuai; Zhan, Peng; Wang, Wei-Peng; Li, Zheng-Cao; Zhang, Zheng-Jun

2014-12-01

Highly c-axis oriented un-doped zinc oxide (ZnO) thin films, each with a thickness of ~ 100 nm, are deposited on Si (001) substrates by pulsed electron beam deposition at a temperature of ~ 320 °C, followed by annealing at 650 °C in argon in a strong magnetic field. X-ray photoelectron spectroscopy (XPS), positron annihilation analysis (PAS), and electron paramagnetic resonance (EPR) characterizations suggest that the major defects generated in these ZnO films are oxygen vacancies. Photoluminescence (PL) and magnetic property measurements indicate that the room-temperature ferromagnetism in the un-doped ZnO film originates from the singly ionized oxygen vacancies whose number depends on the strength of the magnetic field applied in the thermal annealing process. The effects of the magnetic field on the defect generation in the ZnO films are also discussed.

Characterizing superconducting thin films using AC Magnetic Susceptibility

NASA Astrophysics Data System (ADS)

Mahoney, C. H.; Porzio, J.; Sullivan, M. C.

2014-03-01

We present our work on using ac magnetic susceptibility to determine the critical temperature of superconducting thin films. In ac magnetic susceptibility, the thin film is placed between two coils. One coil carries an ac signal, creating a varying external magnetic field. We measure the voltage induced in the pick-up coil on the opposite side of the sample and measure how the sample magnetization changes as the temperature changes. We will present our work to use ac susceptibility to determine critical temperature and superconducting volume fraction. Using our own analysis program, we are able to accurately locate the critical temperatures of the samples and determine the transition width. For the superconducting volume fraction, we etch samples in order to control the thicknesses of the sample and measure how much of the material grown on the surface is superconducting. Supported by NFS grant DMR-1305637.

Magnetic Property in Large Array Niobium Antidot Thin Films

NASA Astrophysics Data System (ADS)

Tinghui, Chen; Hsiang-Hsi, Kung; Wei-Li, Lee; Institute of Physics, Academia Sinica, Taipei, Taiwan Team

2014-03-01

In a superconducting ring, the total flux inside the ring is required to be an integer number of the flux quanta. Therefore, a supercurrent current can appear within the ring in order to satisfy this quantization rule, which gives rise to certain magnetic response. By using a special monolayer polymer/nanosphere hybrid we developed previously, we fabricated a series of superconducting niobium antidot thin films with different antidot diameters. The antidots form well-ordered triangular lattice with a lattice spacing about 200 nm and extend over an area larger than 1 cm2, which enables magnetic detections simply by a SQUID magnetometer. We observed magnetization oscillation with external magnetic field due to the supercurrent screening effect, where different features for large and small antidot thin films were found. Detailed size and temperature dependencies of the magnetization in niobium antidot nanostructures will be presented.

High-frequency electromagnetic properties of soft magnetic metal-polyimide hybrid thin films

NASA Astrophysics Data System (ADS)

Kim, Sang Woo; Yoon, Chong S.

2007-09-01

Although there are a lot of demands for suppression of unwanted high-frequency electromagnetic noise in highly integrated electronic devices such as mobile phones and notebook computers, electromagnetic thin films that effectively work in the high-frequency range have still been underdeveloped. Soft magnetic metal-polyimide (PI) hybrid films with high electrical resistivity were prepared by thermal imidization and selective oxidation between the metal alloy layer and polyamic acid (PAA) layer. Electromagnetic properties of the hybrid thin films in the radio-frequency range were characterized by using the microstrip line method and were correlated with their material parameters. Although anisotropy field of the CoFe/NiFe hybrid film was two times lower than that of the NiFe hybrid film, the saturation magnetization of the CoFe/NiFe hybrid film was three times higher than that of the NiFe hybrid film. The CoFe/NiFe hybrid film showed higher power loss in the frequency range of 3-6 GHz compared to the NiFe hybrid film. The high power loss of the CoFe/NiFe hybrid film was caused by high relative permeability and high ferromagnetic resonance (FMR) frequency due to high saturation magnetization.

Magnetic anisotropy modulation of epitaxial Fe3O4 films on MgO substrates

NASA Astrophysics Data System (ADS)

Chichvarina, O.; Herng, T. S.; Xiao, W.; Hong, X.; Ding, J.

2015-05-01

Fe3O4 has been widely studied because of its great potential in spintronics and other applications. As a magnetic electrode, it is highly desired if magnetic anisotropy can be controlled. Here, we report the results from our systematic study on the magnetic properties of magnetite (Fe3O4) thin films epitaxially grown on various MgO substrates. Strikingly, we observed a prominent perpendicular magnetic anisotropy in Fe3O4 film deposited on MgO (111) substrate. When measured in out-of-plane direction, the film (40 nm thick) exhibits a well-defined square hysteresis loop with coercivity (Hc) above 1 kOe, while much lower coercivity was obtained in the in-plane orientation. In sharp contrast, the films deposited onto MgO (100) and MgO (110) substrates show in-plane magnetic anisotropy. These films exhibit a typical soft magnet characteristic—Hc lies within the range of 200-400 Oe. All the films showed a clear Verwey transition near 120 K—a characteristic of Fe3O4 material. In addition, a series of magnetoresistance (MR) measurements is performed and the MR results are in good agreement with the magnetic observations. The role of the substrate orientation and film thickness dependency is also investigated.

The Structure and Bonding State for Fullerene-Like Carbon Nitride Films with High Hardness Formed by Electron Cyclotron Resonance Plasma Sputtering

NASA Astrophysics Data System (ADS)

Kamata, Tomoyuki; Niwa, Osamu; Umemura, Shigeru; Hirono, Shigeru

2012-12-01

We studied pure carbon films and carbon nitride (CN) films by using electron cyclotron resonance (ECR) sputtering. The main feature of this method is high density ion irradiation during deposition, which enables the pure carbon films to have fullerene-like (FL) structures without nitrogen incorporation. Furthermore, without substrate heating, the ECR sputtered CN films exhibited an enhanced FL microstructure and hardness comparable to that of diamond at intermediate nitrogen concentration. This microstructure consisted of bent and cross-linked graphene sheets where layered areas remarkably decreased due to increased sp3 bonding. Under high nitrogen concentration conditions, the CN films demonstrated extremely low hardness because nitrile bonding not only decreased the covalent-bonded two-dimensional hexagonal network but also annihilated the bonding there. By evaluating lattice images obtained by transmission electron microscopy and the bonding state measured by X-ray photoelectron spectroscopy, we classified the ECR sputtered CN films and offered phase diagram and structure zone diagram.

CoPtB(O) alloy films as new perpendicular recording media

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hayashi, K.; Hayakawa, M.; Ohmori, H.

In search of new hard magnetic materials with high saturation magnetization and large coercivity, a comprehensive study was made on numerous Co- and CoPt-base crystalline alloys by means of sputtering techniques. It revealed that a newly found CoPtB(O) alloy system possessed excellent hard magnetic properties with remarkably large perpendicular coercivity and high saturation magnetization. This new alloy film, deposited onto room temperature substrates, shows the magnetic properties of 4{pi}{ital M}{sub {ital s}}=12 kG, {ital H}{sup {perpendicular}}{sub {ital c}}=4000 Oe, and perpendicular anisotropy field {ital H}{sub {ital k}}=22 kOe. These values are superior to those of prevailing materials such as CoCrmore » perpendicular and CoPt or CoNi longitudinal recording media. The typical composition is Co{sub 69}Pt{sub 20}B{sub 6}O{sub 5} (at. %), and oxygen plays a momentous role on the coercivity in this alloy film. As a magnetic recording medium, a write/read experiment of this film shows that the readout signal has a +9 dB peak-to-peak amplitude compared with that of metal particle tape at 1 {mu}m wavelength and has +10 dB compared with that of a CoCr perpendicular medium at 0.5 {mu}m wavelength.« less

Collective magnetic response of inhomogeneous nanoisland FeNi films around the percolation transition

NASA Astrophysics Data System (ADS)

Kovaleva, Natalia N.; Bagdinov, Anton V.; Stupakov, Alexandr; Dejneka, Alexandr; Demikhov, Evgenii I.; Gorbatsevich, Alexandr A.; Pudonin, Fedor A.; Kugel, Kliment I.; Kusmartsev, Feodor V.

2018-04-01

By using superconducting quantum interference device (SQUID) magnetometry, we investigated anisotropic high-field ( H ≲ 7T) low-temperature (10 K) magnetization response of inhomogeneous nanoisland FeNi films grown by rf sputtering deposition on Sitall (TiO2) glass substrates. In the grown FeNi films, the FeNi layer nominal thickness varied from 0.6 to 2.5 nm, across the percolation transition at the d c ≃ 1.8 nm. We discovered that, beyond conventional spin-magnetism of Fe21Ni79 permalloy, the extracted out-of-plane magnetization response of the nanoisland FeNi films is not saturated in the range of investigated magnetic fields and exhibits paramagnetic-like behavior. We found that the anomalous out-of-plane magnetization response exhibits an escalating slope with increase in the nominal film thickness from 0.6 to 1.1 nm, however, it decreases with further increase in the film thickness, and then practically vanishes on approaching the FeNi film percolation threshold. At the same time, the in-plane response demonstrates saturation behavior above 1.5-2T, competing with anomalously large diamagnetic-like response, which becomes pronounced at high magnetic fields. It is possible that the supported-metal interaction leads to the creation of a thin charge-transfer (CT) layer and a Schottky barrier at the FeNi film/Sitall (TiO2) interface. Then, in the system with nanoscale circular domains, the observed anomalous paramagnetic-like magnetization response can be associated with a large orbital moment of the localized electrons. In addition, the inhomogeneous nanoisland FeNi films can possess spontaneous ordering of toroidal moments, which can be either of orbital or spin origin. The system with toroidal inhomogeneity can lead to anomalously strong diamagnetic-like response. The observed magnetization response is determined by the interplay between the paramagnetic- and diamagnetic-like contributions.

Magnetic properties of epitaxial hexagonal HoFeO3 thin films

NASA Astrophysics Data System (ADS)

Wang, Xiao; Xiao, Zhuyun; Xu, Xiaoshan; Wang, Wenbin; Keavney, David; Liu, Yaohua; Cheng, X. M.

2014-03-01

Multiferroic materials exhibit multiple ferroic orders simultaneously and thus have great potential applications in information technology, sensing and actuation. Epitaxial hexagonal HoFeO3 (h-HFO) films are very promising candidates as multiferroic materials with room temperature ferromagnetism, because magnetic Ho3+ ions are expected to have stronger exchange interactions with Fe3+ ions than the well-studied h-LuFeO3 films. We report study of magnetic properties of epitaxial h-HFO thin films deposited using laser molecular beam epitaxy on Yttria-stabilized zirconia (YSZ) substrates. X-ray diffraction measurements confirmed the epitaxial registry and six-fold symmetry of the film. Temperature dependence of magnetization of the film measured by a Quantum Design SQUID magnetometer shows dominating paramagnetic characteristic. Element specific x-ray magnetic circular dichroism measurements performed at beamline 4-ID-C of the Advanced Photon Source show a ferromagnetic ordering of Fe and an exchange coupling between Ho3+ and Fe3+ ions. Work at BMC is supported by NSF Career award (DMR 1053854). Work at ANL is supported by US-DOE, Office of Science, BES (No. DE-AC02-06CH11357).

Ultrasoft magnetic films investigated with Lorentz tranmission electron microscopy and electron holography.

PubMed

De Hosson, Jeff Th M; Chechenin, Nicolai G; Alsem, Daan-Hein; Vystavel, Tomas; Kooi, Bart J; Chezan, Antoni R; Boerma, Dik O

2002-08-01

As a tribute to the scientific work of Professor Gareth Thomas in the field of structure-property relationships this paper delineates a new possibility of Lorentz transmission electron microscopy (LTEM) to study the magnetic properties of soft magnetic films. We show that in contrast to the traditional point of view, not only does the direction of the magnetization vector in nano-crystalline films make a correlated small-angle wiggling, but also the magnitude of the magnetization modulus fluctuates. This fluctuation produces a rapid modulation in the LTEM image. A novel analysis of the ripple structure in nano-crystalline Fe-Zr-N film corresponds to an amplitude of the transversal component of the magnetization deltaMy of 23 mT and a longitudinal fluctuation of the magnetization of the order of deltaMx = 30 mT. The nano-crystalline (Fe99Zr1)1-xNx films have been prepared by DC magnetron reactive sputtering with a thickness between 50 and 1000 nm. The grain size decreased monotonically with N content from typically 100 nm in the case of N-free films to less than 10 nm for films containing 8 at%. The specimens were examined with a JEOL 2010F 200 kV transmission electron microscope equipped with a post column energy filter (GIF 2000 Gatan Imaging Filter). For holography, the microscope is mounted with a biprism (JEOL biprism with a 0.6 microm diameter platinum wire).

Mechanical design of thin-film diamond crystal mounting apparatus for coherence preservation hard x-ray optics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shu, Deming, E-mail: shu@aps.anl.gov; Shvyd’ko, Yuri V.; Stoupin, Stanislav

2016-07-27

A new thin-film diamond crystal mounting apparatus has been designed at the Advanced Photon Source (APS) for coherence preservation hard x-ray optics with optimized thermal contact and minimized crystal strain. This novel mechanical design can be applied to new development in the field of: x-ray optics cavities for hard x-ray free-electron laser oscillators (XFELOs), self-seeding monochromators for hard x-ray free-electron laser (XFEL) with high average thermal loading, high heat load diamond crystal monochromators and beam-sharing/beam-split-and-delay devices for XFEL facilities and future upgraded high-brightness coherent x-ray source in the MBA lattice configuration at the APS.

Reading magnetic ink patterns with magnetoresistive sensors

NASA Astrophysics Data System (ADS)

Merazzo, K. J.; Costa, T.; Franco, F.; Ferreira, R.; Zander, M.; Türr, M.; Becker, T.; Freitas, P. P.; Cardoso, S.

2018-05-01

Information storage and monitoring relies on sensitive transducers with high robustness and reliability. This paper shows a methodology enabling the qualification of magnetic sensors for magnetic pattern readout, in applications different than hard disk magnetic recording. A magnetic tunnel junction MTJ sensor was incorporated in a reader setup for recognition of the magnetization of patterned arrays made of CoCrPt thin films and magnetic ink. The geometry of the sensor (in particular, the footprint and vertical distance to the media) was evaluated for two sensor configurations. The readout conditions were optimized to cope for variable media field intensity, resulting from CoCrPt film or magnetic ink thickness, with fixed reading distance and dimensions of the pattern. The calibration of the ink magnetic signal could be inferred from the analytical calculations carried out to validate the CoCrPt results.

Different magnetic origins of (Mn, Fe)-codoped ZnO powders and thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fan, Jiuping; Jiang, Fengxian; Quan, Zhiyong

2012-11-15

Graphical abstract: The effects of the sample forms, fabricated methods, and process conditions on the structural and magnetic properties of (Mn, Fe)-codoped ZnO powders and films were systematically studied. The origins of ferromagnetism in the vacuum-annealed powder and PLD-deposited film are different. The former originates from the impurities of magnetic clusters, whereas the latter comes from the almost homogenous phase. Highlights: ► The magnetic natures of Zn{sub 0.98}Mn{sub 0.01}Fe{sub 0.01}O powders and thin films come from different origins. ► The ferromagnetism of the powder is mainly from the contribution of magnetic clusters. ► Whereas the ferromagnetic behavior of the filmmore » comes from the almost homogenous phase. -- Abstract: The structural and magnetic properties of (Mn, Fe)-codoped ZnO powders as well as thin films were investigated. The X-ray diffraction and magnetic measurements indicated that the higher sintering temperature facilitates more Mn and Fe incorporation into ZnO. Magnetic measurements indicated that the powder sintered in air at 800 °C showed paramagnetic, but it exhibited obvious room temperature ferromagnetism after vacuum annealing at 600 °C. The results revealed that magnetic clusters were the major contributors to the observed ferromagnetism in vacuum-annealed Zn{sub 0.98}Mn{sub 0.01}Fe{sub 0.01}O powder. Interestingly, the room temperature ferromagnetism was also observed in the Zn{sub 0.98}Mn{sub 0.01}Fe{sub 0.01}O film deposited via pulsed laser deposition from the air-sintered paramagnetic target, but the secondary phases in the film were not detected from X-ray diffraction, transmission electron microscopy, and zero-field cooling and field cooling. Apparently, the magnetic natures of powders and films come from different origins.« less

Perpendicular magnetic anisotropy in Mn2CoAl thin film

NASA Astrophysics Data System (ADS)

Sun, N. Y.; Zhang, Y. Q.; Fu, H. R.; Che, W. R.; You, C. Y.; Shan, R.

2016-01-01

Heusler compound Mn2CoAl (MCA) is attracting more attentions due to many novel properties, such as high resistance, semiconducting behavior and suggestion as a spin-gapless material with a low magnetic moment. In this work, Mn2CoAl epitaxial thin film was prepared on MgO(100) substrate by magnetron sputtering. The transport property of the film exhibits a semiconducting-like behavior. Moreover, our research reveals that perpendicular magnetic anisotropy (PMA) can be induced in very thin Mn2CoAl films resulting from Mn-O and Co-O bonding at Mn2CoAl/MgO interface, which coincides with a recent theoretical prediction. PMA and low saturation magnetic moment could lead to large spin-transfer torque with low current density in principle, and thus our work may bring some unanticipated Heusler compounds into spintronics topics such as the domain wall motion and the current-induced magnetization reversal.

Hard TiCx/SiC/a-C:H nanocomposite thin films using pulsed high energy density plasma focus device

NASA Astrophysics Data System (ADS)

Umar, Z. A.; Rawat, R. S.; Tan, K. S.; Kumar, A. K.; Ahmad, R.; Hussain, T.; Kloc, C.; Chen, Z.; Shen, L.; Zhang, Z.

2013-04-01

Thin films of TiCx/SiC/a-C:H were synthesized on Si substrates using a complex mix of high energy density plasmas and instability accelerated energetic ions of filling gas species, emanated from hot and dense pinched plasma column, in dense plasma focus device. The conventional hollow copper anode of Mather type plasma focus device was replaced by solid titanium anode for synthesis of TiCx/SiC/a-C:H nanocomposite thin films using CH4:Ar admixture of (1:9, 3:7 and 5:5) for fixed 20 focus shots as well as with different number of focus shots with fixed CH4:Ar admixture ratio 3:7. XRD results showed the formation of crystalline TiCx/SiC phases for thin film synthesized using different number of focus shots with CH4:Ar admixture ratio fixed at 3:7. SEM results showed that the synthesized thin films consist of nanoparticle agglomerates and the size of agglomerates depended on the CH4:Ar admixture ratio as well as on the number of focus shots. Raman analysis showed the formation of polycrystalline/amorphous Si, SiC and a-C for different CH4:Ar ratio as well as for different number of focus shots. The XPS analysis confirmed the formation of TiCx/SiC/a-C:H composite thin film. Nanoindentation results showed that the hardness and elastic modulus values of composite thin films increased with increasing number of focus shots. Maximum values of hardness and elastic modulus at the surface of the composite thin film were found to be about 22 and 305 GPa, respectively for 30 focus shots confirming the successful synthesis of hard composite TiCx/SiC/a-C:H coatings.

Electric-field assisted switching of magnetization in perpendicularly magnetized (Ga,Mn)As films at high temperatures

NASA Astrophysics Data System (ADS)

Wang, Hailong; Ma, Jialin; Yu, Xueze; Yu, Zhifeng; Zhao, Jianhua

2017-01-01

The electric-field effects on the magnetism in perpendicularly magnetized (Ga,Mn)As films at high temperatures have been investigated. An electric-field as high as 0.6 V nm-1 is applied by utilizing a solid-state dielectric Al2O3 film as a gate insulator. The coercive field, saturation magnetization and magnetic anisotropy have been clearly changed by the gate electric-field, which are detected via the anomalous Hall effect. In terms of the Curie temperature, a variation of about 3 K is observed as determined by the temperature derivative of the sheet resistance. In addition, electrical switching of the magnetization assisted by a fixed external magnetic field at 120 K is demonstrated, employing the gate-controlled coercive field. The above experimental results have been attributed to the gate voltage modulation of the hole density in (Ga,Mn)As films, since the ferromagnetism in (Ga,Mn)As is carrier-mediated. The limited modulation magnitude of magnetism is found to result from the strong charge screening effect introduced by the high hole concentration up to 1.10  ×  1021 cm-3, while the variation of the hole density is only about 1.16  ×  1020 cm-3.

Magnetic domain pattern in hierarchically twinned epitaxial Ni-Mn-Ga films.

PubMed

Diestel, Anett; Neu, Volker; Backen, Anja; Schultz, Ludwig; Fähler, Sebastian

2013-07-03

Magnetic shape memory alloys exhibit a hierarchically twinned microstructure, which has been examined thoroughly in epitaxial Ni-Mn-Ga films. Here we analyze the consequences of this 'twin within twins' microstructure on the magnetic domain pattern. Atomic and magnetic force microscopy are used to probe the correlation between the martensitic microstructure and magnetic domains. We examine the consequences of different twin boundary orientations with respect to the substrate normal as well as variant boundaries between differently aligned twinned laminates. A detailed micromagnetic analysis is given which describes the influence of the finite film thickness on the formation of magnetic band domains in these multiferroic materials.

Defect-mediated magnetism of transition metal doped zinc oxide thin films

NASA Astrophysics Data System (ADS)

Roberts, Bradley Kirk

Magnetism in transition metal doped wide band-gap materials is of interest to further the fundamental science of materials and future spintronics applications. Large inter-dopant separations require mediation of ferromagnetism by some method; carrier-mediated mechanisms are typically applicable to dilute magnetic semiconductors with low Curie temperatures. Dilute magnetic oxides, commonly with poor conductivity and TC above room temperature, cannot be described within this theory. Recent experiment and theory developments suggest that ferromagnetic exchange in these materials can be mediated by defects. This research includes experimental results justifying and developing this approach. Thin films of Cr doped ZnO (band gap ˜3.3 eV) were deposited with several processing variations to enhance the effects of either 0-dimensional (vacancy, hydrogen-related defect) or two-dimensional defects (surface/interface) and thereby affect magnetism and conductivity. We observe surface magnetism in dielectric thin films of oxygen-saturated ZnO:Cr with spontaneous magnetic moment and conductance dropping approximately exponentially with increasing thickness. Uniform defect concentrations would not result in such magnetic ordering behavior indicating that magnetism is mediated either by surface defects or differing concentrations of point defects near the surface. Polarized neutron reflectivity profiling confirms a magnetically active region of ˜8 nm at the film surface. Hydrogen is notoriously present as a defect and carrier dopant in ZnO, and artificial introduction of hydrogen in dielectric ZnO:Cr films results in varying electronic and magnetic behavior. Free carriers introduced with hydrogen doping are not spin-polarized requiring an alternative explanation for ferromagnetism. We find from positron annihilation spectroscopy measurements that hydrogen doping increases the concentration of an altered VZn-related defect (a preliminary interpretation) throughout the film, which

Epitaxially grown BaM hexaferrite films having uniaxial axis in the film plane for self-biased devices

PubMed Central

Zhang, Xiaozhi; Meng, Siqin; Song, Dongsheng; Zhang, Yao; Yue, Zhenxing; Harris, Vincent G.

2017-01-01

Barium hexaferrite (BaM) films with in-plane c-axis orientation are promising and technically important materials for self-biased magnetic microwave devices. In this work, highly oriented BaM films with different thickness and an in-plane easy axis (c-axis) of magnetization were grown on a-plane single-crystal sapphire substrates by direct current magnetron sputtering. A procedure involving seed layers, layer-by-layer annealing was adopted to reduce the substrate-induced strains and allow for the growth of thick (~3.44 μm) films. The epitaxial growth of the BaM film on sapphire was revealed by high-resolution transmission electron microscopy with dislocations being observed at the film-substrate interface. The orientation was also verified by X-ray diffraction and more notably, polarized Raman scattering. The magnetic properties and ferromagnetic resonant frequencies were experimentally characterized by a vibrating sample magnetometry and a frequency-swept ferromagnetic resonant flip-chip technique, respectively. The micron-thick BaM films exhibited a large remanence ratio of 0.92 along in-plane easy axis and a small one of 0.09 for the in-plane hard axis loop measurement. The FMR frequency was 50.3 GHz at zero field and reached 57.9 GHz under a magnetic field of 3 kOe, indicating that the epitaxial BaM films with strong self-biased behaviors have good electromagnetic properties in millimeter-wave range. PMID:28276492

Epitaxially grown BaM hexaferrite films having uniaxial axis in the film plane for self-biased devices.

PubMed

Zhang, Xiaozhi; Meng, Siqin; Song, Dongsheng; Zhang, Yao; Yue, Zhenxing; Harris, Vincent G

2017-03-09

Barium hexaferrite (BaM) films with in-plane c-axis orientation are promising and technically important materials for self-biased magnetic microwave devices. In this work, highly oriented BaM films with different thickness and an in-plane easy axis (c-axis) of magnetization were grown on a-plane single-crystal sapphire substrates by direct current magnetron sputtering. A procedure involving seed layers, layer-by-layer annealing was adopted to reduce the substrate-induced strains and allow for the growth of thick (~3.44 μm) films. The epitaxial growth of the BaM film on sapphire was revealed by high-resolution transmission electron microscopy with dislocations being observed at the film-substrate interface. The orientation was also verified by X-ray diffraction and more notably, polarized Raman scattering. The magnetic properties and ferromagnetic resonant frequencies were experimentally characterized by a vibrating sample magnetometry and a frequency-swept ferromagnetic resonant flip-chip technique, respectively. The micron-thick BaM films exhibited a large remanence ratio of 0.92 along in-plane easy axis and a small one of 0.09 for the in-plane hard axis loop measurement. The FMR frequency was 50.3 GHz at zero field and reached 57.9 GHz under a magnetic field of 3 kOe, indicating that the epitaxial BaM films with strong self-biased behaviors have good electromagnetic properties in millimeter-wave range.

A comparison study of Co and Cu doped MgO diluted magnetic thin films

NASA Astrophysics Data System (ADS)

Sarıtaş, S.; ćakıcı, T.; Muǧlu, G. Merhan; Kundakcı, M.; Yıldırım, M.

2017-02-01

Transition metal-doped MgO diluted magnetic thin films are appropriate candidates for spintronic applications and designing magnetic devices and sensors. Therefore, MgO:Co and MgO:Cu films were deposited on glass substrates by Chemical Spray Pyrolysis (CSP) method different thin film deposition parameters. Deposited different transition metal doped MgO thin films were compared in terms of optic and structural properties. Comparison optic analysis of the films was investigated spectral absorption and transmittance measurements by UV-Vis double beam spectrophotometer technique. Comparison structural analysis of the thin films was examined by using XRD, Raman Analysis, SEM, EDX and AFM techniques. The transition metal-doped; MgO:Co and MgO:Cu thin films maybe have potential applications in spintronics and magnetic data storage.

Composition dependence of charge and magnetic length scales in mixed valence manganite thin films

PubMed Central

Singh, Surendra; Freeland, J. W.; Fitzsimmons, M. R.; Jeen, H.; Biswas, A.

2016-01-01

Mixed-valence manganese oxides present striking properties like the colossal magnetoresistance, metal-insulator transition (MIT) that may result from coexistence of ferromagnetic, metallic and insulating phases. Percolation of such phase coexistence in the vicinity of MIT leads to first-order transition in these manganites. However the length scales over which the electronic and magnetic phases are separated across MIT which appears compelling for bulk systems has been elusive in (La1−yPry)1−xCaxMnO3 films. Here we show the in-plane length scale over which charge and magnetism are correlated in (La0.4Pr0.6)1−xCaxMnO3 films with x = 0.33 and 0.375, across the MIT temperature. We combine electrical transport (resistance) measurements, x-ray absorption spectroscopy (XAS), x-ray magnetic circular dichroism (XMCD), and specular/off-specular x-ray resonant magnetic scattering (XRMS) measurements as a function of temperature to elucidate relationships between electronic, magnetic and morphological structure of the thin films. Using off-specular XRMS we obtained the charge-charge and charge-magnetic correlation length of these LPCMO films across the MIT. We observed different charge-magnetic correlation length for two films which increases below the MIT. The different correlation length shown by two films may be responsible for different macroscopic (transport and magnetic) properties. PMID:27461993

Microplasma Jet Synthesis of Ni-Fe Oxide Films for Magnetic Exchange Bias and Electrocatalytic Studies

NASA Astrophysics Data System (ADS)

Pebley, Andrew Christian

Ni-Fe oxides have received significant interest from the scientific community because they have attractive magnetic and electrochemical properties for use in next generation data storage and energy conversion technologies. For example, the NiFe2O4/NiO nanogranular system exhibits the exchange bias effect, a magnetic phenomenon occurring at the interface of a ferro- or ferrimagnet (FM or FiM) and an antiferromagnet (AFM), where the AFM acts to increase the magnetic hardness of the corresponding FM or FiM. Additionally, doping of NiO with Fe has resulted in remarkably high catalytic activities for water splitting, a potential clean energy alternative to fossil fuels. A key challenge in implementing these Ni-Fe oxides for magnetic and electrocatalytic applications is the ability to control film morphology, crystallinity, composition, chemical phase, and doping during synthesis. Moreover, how these physiochemical properties effect magnetic and electrochemical behavior in the Ni-Fe oxide system is not fully understood. This dissertation focuses on the development and use of a novel synthesis technique, known as microplasma (MP) jet-based deposition, for the fabrication of biphasic NiFe2O4 (FiM)/NiO (AFM) and Fe-doped NiO nanostructured films for fundamental studies of exchange bias and electrocatalysis, respectively. The goal of this work was to understand how MP operation and deposition conditions (e.g., precursor composition, flux, substrate temperature, and post-deposition heat treatment) influence Ni-Fe oxide growth and film microstructure. Specifically, the role of composition, phase fraction, grain size, temperature, and interfacial density on exchange bias phenomena in NiFe 2O4/NiO nanogranular films was investigated. MP jets were also used to realize metastable Fe-doped NiO films with high surface area to assess how doping affects the electrochemical properties of NiO for the oxygen evolution reaction (OER). Biphasic NiFe2O4/NiO films of different composition

Exciting transition metal doped dilute magnetic thin films: MgO:Er and ZnO:Er

NASA Astrophysics Data System (ADS)

Ćakıcı, T.; Sarıtaş, S.; Muǧlu, G. Merhan; Yıldırım, M.

2017-02-01

Erbium doped MgO and doped ZnO thin films have reasonably important properties applications in spintronic devices. These films were synthesized on glass substrates by Chemical Spray Pyrolysis (CSP) method. In the literature there has been almost no report on preparation of MgO:Er dilute magnetic thin films by means of CSP. Because doped thin films show different magnetic behaviors, depending upon the type of magnetic material ions, concentration of them, synthesis route and experimental conditions, synthesized MgO:Er and ZnO:Er films were compared to thin film properties. Optical analyses of the synthesized thin films were examined spectral absorption and transmittance measurements by UV-Vis double beam spectrophotometer technique. Structural analysis of the thin films was examined by using XRD, Raman Analysis, FE-SEM, EDX and AFM techniques. Also, magnetic properties of the MgO:Er and ZnO:Er films were investigated by vibrating sample magnetometer (VSM) which show that diamagnetic behavior of the MgO:Er thin film and ferromagnetic (FM) behavior of the ZnO:Er film were is formed.

Control of magnetism in dilute magnetic semiconductor (Ga,Mn)As films by surface decoration of molecules

NASA Astrophysics Data System (ADS)

Wang, Hailong; Wang, Xiaolei; Xiong, Peng; Zhao, Jianhua

2016-03-01

The responses of magnetic moments to external stimuli such as magnetic-field, heat, light and electric-field have been utilized to manipulate the magnetism in magnetic semiconductors, with many of the novel ideas applied even to ferromagnetic metals. Here, we review a new experimental development on the control of magnetism in (Ga,Mn)As thin films by surface decoration of organic molecules: Molecules deposited on the surface of (Ga,Mn)As thin films are shown to be capable of significantly modulating their saturation magnetization and Curie temperature. These phenomena are shown to originate from the carrier-mediated ferromagnetism in (Ga,Mn)As and the surface molecules acting as acceptors or donors depending on their highest occupied molecular orbitals, resembling the charge transfer mechanism in a pn junction in which the equilibrium state is reached on the alignment of Fermi levels.

Transport in ultrathin gold films decorated with magnetic Gd atoms

NASA Astrophysics Data System (ADS)

Alemani, Micol; Helgren, Erik; Hugel, Addison; Hellman, Frances

2008-03-01

We have performed four-probe transport measurements of ultrathin Au films decorated with Gd ad-atoms. The samples were prepared by quench condensation, i.e., sequential evaporation on a cryogenically cooled substrate under UHV conditions while monitoring the film thickness and resistance. Electrically continuous Au films at thickness of about 2 mono-layers of material are grown on an amorphous Ge wetting layer. The quench condensation method provides a sensitive control on the sample growth process, allowing us to tune the morphological and electrical configuration of the system. The ultrathin gold films develop from an insulating to a metallic state as a function of film thickness. The temperature dependence of the Au conductivity for different thickness is studied. It evolves from hopping transport for the insulating films, to a ln T dependence for thicker films. For gold films in the insulating regime we found a decreasing resistance by adding Gd. This is in agreement with a decreasing tunneling barrier height between metallic atoms. The Gd magnetic moments are randomly oriented for isolated atoms. This magnetic disorder leads to scattering of the charge carriers and a reduced conductivity compared to nonmagnetic materials.

Combinatorial investigation of Fe–B thin-film nanocomposites

PubMed Central

Brunken, Hayo; Grochla, Dario; Savan, Alan; Kieschnick, Michael; Meijer, Jan D; Ludwig, Alfred

2011-01-01

Combinatorial magnetron sputter deposition from elemental targets was used to create Fe–B composition spread type thin film materials libraries on thermally oxidized 4-in. Si wafers. The materials libraries consisting of wedge-type multilayer thin films were annealed at 500 or 700 °C to transform the multilayers into multiphase alloys. The libraries were characterized by nuclear reaction analysis, Rutherford backscattering, nanoindentation, vibrating sample magnetometry, x-ray diffraction (XRD) and transmission electron microscopy (TEM). Young's modulus and hardness values were related to the annealing parameters, structure and composition of the films. The magnetic properties of the films were improved by annealing in a H2 atmosphere, showing a more than tenfold decrease in the coercive field values in comparison to those of the vacuum-annealed films. The hardness values increased from 8 to 18 GPa when the annealing temperature was increased from 500 to 700 °C. The appearance of Fe2B phases, as revealed by XRD and TEM, had a significant effect on the mechanical properties of the films. PMID:27877435

Magnetic pinning in a superconducting film by a ferromagnetic layer with stripe domains

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mancusi, D.; Di Giorgio, C.; Bobba, F.

2014-10-31

A magnetic study of superconductor/ferromagnet bilayers was performed by hysteresis loops and temperature-dependent magnetization measurements. The superconductor/ferromagnet bilayers consist of a Nb film deposited on a Py film with weak perpendicular magnetic anisotropy. By comparing the temperature-dependent magnetization data obtained on samples with different ferromagnetic layer thickness, a decrease of the magnetic pinning with increasing thickness of the ferromagnetic layer has been found. This is confirmed by the reduction of the Nb film critical current density at low fields extracted by using the magnetic irreversibility of the hysteresis loops. As the ferromagnetic layer exhibits a magnetic structure with stripe domains,more » whose width increases for increasing thickness as observed by magnetic force microscopy (MFM) measurements, we relate the reduction of the superconducting critical current in samples with thicker ferromagnetic layers to a weaker interaction between the vortices guided by the underlying magnetic template.« less

Mapping hard magnetic recording disks by TOF-SIMS

NASA Astrophysics Data System (ADS)

Spool, A.; Forrest, J.

2008-12-01

Mapping of hard magnetic recording disks by TOF-SIMS was performed both to produce significant analytical results for the understanding of the disk surface and the head disk interface in hard disk drives, and as an example of a macroscopic non-rectangular mapping problem for the technique. In this study, maps were obtained by taking discrete samples of the disk surface at set intervals in R and Θ. Because both in manufacturing, and in the disk drive, processes that may affect the disk surface are typically circumferential in nature, changes in the surface are likely to be blurred in the Θ direction. An algorithm was developed to determine the optimum relative sampling ratio in R and Θ. The results confirm what the experience of the analysts suggested, that changes occur more rapidly on disks in the radial direction, and that more sampling in the radial direction is desired. The subsequent use of statistical methods principle component analysis (PCA), maximum auto-correlation factors (MAF), and the algorithm inverse distance weighting (IDW) are explored.

Enhanced magnetostriction derived from magnetic single domain structures in cluster-assembled SmCo films

NASA Astrophysics Data System (ADS)

Bai, Yulong; Yang, Bo; Guo, Fei; Lu, Qingshan; Zhao, Shifeng

2017-11-01

Cluster-assembled SmCo alloy films were prepared by low energy cluster beam deposition. The structure, magnetic domain, magnetization, and magnetostriction of the films were characterized. It is shown that the as-prepared films are assembled in compact and uniformly distributed spherical cluster nanoparticles, most of which, after vacuum in situ annealing at 700 K, aggregated to form cluster islands. These cluster islands result in transformations from superparamagnetic states to magnetic single domain (MSD) states in the films. Such MSD structures contribute to the enhanced magnetostrictive behaviors with a saturation magnetostrictive coefficient of 160 × 10-6 in comparison to 105 × 10-6 for the as-prepared films. This work demonstrates candidate materials that could be applied in nano-electro-mechanical systems, low power information storage, and weak magnetic detecting devices.

Perpendicular magnetic anisotropy in Mn2VIn (001) films: An ab initio study

NASA Astrophysics Data System (ADS)

Zipporah, Muthui; Robinson, Musembi; Julius, Mwabora; Arti, Kashyap

2018-05-01

First principles study of the magnetic anisotropy of Mn2VIn (001) films show perpendicular magnetic anisotropy (PMA), which increases as a function of the thickness of the film. Density functional theory (DFT) as implemented in the Vienna Ab initio simulation package (VASP) is employed here to perform a comprehensive theoretical investigation of the structural, electronic and magnetic properties of the Mn2VIn(001) films of varying thickness. Our calculations were performed on fully relaxed structures, with five to seventeen mono layers (ML). The degree of spin polarization is higher in the (001) Mn2VIn thin films as compared to the bulk in contrast to what is usually the case and as in Mn2VAl, which is isoelectronic to Mn2VIn as well as inCo2VIn (001) films studied for comparison. Tetragonal distortions are found in all the systems after relaxation. The distortion in the Mn2VIn system persists even for the 17ML thin film, resulting in PMA in the Mn2VIn system. This significant finding has potential to contribute to spin transfer torque (STT) and magnetic random access memory MRAM applications, as materials with PMA derived from volume magnetocrystalline anisotropy are being proposed as ideal magnetic electrodes.

Object representation and magnetic moments in thin alkali films

NASA Astrophysics Data System (ADS)

Garrett, Douglas C.

2008-10-01

This thesis is broken into two parts a computer vision part and a solid state physics part. In the computer vision part of the thesis (chapters 1 through 5), the concept of an architecture is discussed with a review of what is known about the brain's visual architecture as it applies to object representation. With this in mind we review the two main types of architectures that are used in computer vision for object representation. A specific object representation is then implemented and optimized to solve a problem in object tracking. This representation is then used to derive the fiducial points of a face using two distinct methods. One using evolutionary algorithms and another by a Bayesian analysis of the feature responses drawn from a gallery of faces. The evolved fiducial representation is tested as a facial detection system. It is shown that the Bayesian analysis of facial images gives an entropy measure that can be used to further improve detection results in the facial detection system. In addition, two similarity metrics are explored in the context of facial detection. It is found that a normalized vector dot product substantially outperforms the Euclidean distance measure. The solid state part of the thesis is composed of two self contained chapters. An effort has been made to reduce the redundancies between the material but some will necessarily remain (i.e., short descriptions of the experimental setup). Both chapters deal with the phenomenon of magnetism of atomic impurities in and on thin metal host films. The important difference between the chapters, besides the results, lies in the experimental technique used to measure the magnetism. In chapter 6, thin films of Pb are covered in situ with sub monolayers of V, Mo and Co in the range between 0.01 and 1 monolayers. If the surface impurities are magnetic they will reduce the superconducting transition temperature of the Pb film. From the reduction of Tc the magnetic dephasing rate of the surface

EDITORIAL: Selected papers from the 19th International Colloquium on Magnetic Films and Surfaces

NASA Astrophysics Data System (ADS)

Miyazaki, T.; Inoue, J.

2007-03-01

The 19th International Colloquium on Magnetic Films and Surfaces (ICMFS 2006) was held on 14-18 August 2006 at the Sendai International Center in Sendai, Japan. The purpose of the Colloquium was to bring together scientists working on magnetic thin films and surfaces and to provide an opportunity for presentation and discussion of recent experimental and theoretical advances in the field. 285 scientists from 17 countries (Japan: 167, overseas: 118) participated in the Colloquium, as well as 6 family members. There were 56 oral and 178 poster presentations. The oral presentations consisted of 3 plenary talks, 23 invited talks and 30 contributed talks. The number of presentations by scientific category are as follows: Spin dependent transport: 43 Magnetic storage/memory: 9 Magnetization reversal and fast dynamics: 15 Spin injection and spin transfer torque: 26 Magnetic thin films and multilayers: 71 High spin polarization materials: 17 Hard and soft magnetic materials: 3 Magneto-optics: 5 Characterization techniques for thin films and surfaces: 7 Exchange coupling: 13 Micro- and nanopatterned magnetic structures: 18 Micromagnetic modelling: 2 One of the characteristics of the present Colloquium is an increase in the number of presentations in the field of spin-electronics, as seen above. This Cluster Issue of Journal of Physics D: Applied Physics includes several important papers in this rapidly developing field. We believe that, in the future, the field of magnetic materials will maintain its popularity and, on top of that, other fields such as spintronics materials, materials related to life sciences and medicine and also materials related to the environment will be investigated further. The ICMFS Conference started in London in 1964, and is now one of the world-wide conferences on magnetism. The Colloquium has been held in Japan four times now: the previous ones being the 5th ICMFS in the Mount Fuji area, the 10th at Yokohama and the 17th at Kyoto, which was

Microstructures and magnetic properties of Co-Al-O granular thin films

NASA Astrophysics Data System (ADS)

Ohnuma, M.; Hono, K.; Onodera, H.; Ohnuma, S.; Fujimori, H.; Pedersen, J. S.

2000-01-01

The microstructures of Co-Al-O thin films of wide varieties of compositions are studied by transmission electron microscopy and small angle x-ray scattering (SAXS). In the superparamagnetic specimens, high resolution electron microscope images reveal that isolated spherical Co particles are surrounded by an amorphous aluminum oxide matrix. However, in the soft ferromagnetic films, the shape of the Co particles is prolate ellipsoidal. SAXS intensities from the soft magnetic specimens decrease inversely with the wave vector, q, in a low wave-vector region, while an interparticle interference peak is observed for the superparamagnetic specimens. The scattering profiles of the soft magnetic films imply that the Co particles have a cylindrical shape and are randomly oriented. The correlation between the magnetic properties and the microstructures is discussed.

Magnetic Hysteresis in Nanocomposite Films Consisting of a Ferromagnetic AuCo Alloy and Ultrafine Co Particles

PubMed Central

Chinni, Federico; Spizzo, Federico; Montoncello, Federico; Mattarello, Valentina; Maurizio, Chiara; Mattei, Giovanni; Del Bianco, Lucia

2017-01-01

One fundamental requirement in the search for novel magnetic materials is the possibility of predicting and controlling their magnetic anisotropy and hence the overall hysteretic behavior. We have studied the magnetism of Au:Co films (~30 nm thick) with concentration ratios of 2:1, 1:1, and 1:2, grown by magnetron sputtering co-deposition on natively oxidized Si substrates. They consist of a AuCo ferromagnetic alloy in which segregated ultrafine Co particles are dispersed (the fractions of Co in the AuCo alloy and of segregated Co increase with decreasing the Au:Co ratio). We have observed an unexpected hysteretic behavior characterized by in-plane anisotropy and crossed branches in the loops measured along the hard magnetization direction. To elucidate this phenomenon, micromagnetic calculations have been performed for a simplified system composed of two exchange-coupled phases: a AuCo matrix surrounding a Co cluster, which represents an aggregate of particles. The hysteretic features are qualitatively well reproduced provided that the two phases have almost orthogonal anisotropy axes. This requirement can be plausibly fulfilled assuming a dominant magnetoelastic character of the anisotropy in both phases. The achieved conclusions expand the fundamental knowledge on nanocomposite magnetic materials, offering general guidelines for tuning the hysteretic properties of future engineered systems. PMID:28773075

Observation and manipulation of magnetic domains in sol gel derived thin films of spinel ferrites

NASA Astrophysics Data System (ADS)

Datar, Ashwini A.; Mathe, Vikas L.

2017-12-01

Thin films of spinel ferrites, namely zinc substituted nickel, cobalt ferrite, and manganese substituted cobalt ferrite, were synthesized using sol-gel derived spin-coating techniques. The films were characterized using x-ray diffraction, field emission scanning electron microscopy, Fourier transform infrared spectroscopy and Raman spectroscopy techniques for the analysis of structural, morphological and vibrational band transition properties, which confirm the spinel phase formation of the films. The magnetic force microscopy (MFM) technique was used to observe the magnetic domain structure present in the synthesized films. Further, the films were subjected to an external DC magnetic field of 2 kG to orient the magnetic domains and analyzed using an ex situ MFM technique.

Stress-induced magnetization for epitaxial spinel ferrite films through interface engineering

NASA Astrophysics Data System (ADS)

Wakiya, Naoki; Shinozaki, Kazuo; Mizutani, Nobuyasu

2004-08-01

This study found "stress-induced magnetization" for epitaxial ferrite films with spinel structure. We grew (111)- and (001)-epitaxial Ni0.17Zn0.23Fe2.60O4(NZF) films on CeO2/Y0.15Zr0.85O1.93(YSZ )/Si(001) and oxide single-crystal substrates, respectively. There is a window of lattice mismatch (between 0 and 6.5%) to achieve bulk saturation magnetization (Ms). An NZF film grown on CeO2/YSZ //Si(001) showed tensile stress, but that stress was relaxed by introducing a ZnCo2O4(ZC ) buffer layer. NZF films grown on SrTiO3(ST )(001) and (La,Sr)(Al,Ta)O3(LSAT)(001) had compressive stress, which was enhanced by introducing a ZC buffer layer. In both cases, bulk Ms was achieved by introducing the ZC buffer layer. This similarity suggests that magnetization can be controlled by the stress.

Temperature characteristics and magnetization mechanism of Fe1.2Co films

NASA Astrophysics Data System (ADS)

Dong, Dashun; Fang, Qingqing; Wang, Wenwen; Yang, Jingjing

2017-11-01

Fe1.2Co films with various thicknesses were prepared on glass substrates by pulsed laser deposition (PLD). The Fe1.2Co crystal structure exhibited a preferred orientation in the <1 1 0> direction. Also, we found that changing the film thickness affected its magnetic properties and the formation of its reversed nucleus. By measuring magnetism-temperature (M-T) curves under applied field cooling (FC) and zero-field cooling (ZFC), we found that the mechanism of the formation and growth of the reversed nucleus played a main role in blocking the motion of domain walls: the mechanism was competition between a ferromagnetic phase (FM) and an anti-ferromagnetic phase (AFM) at 10-300 K. Moreover, we found that the reversed nucleus blocked the motion of magnetic domains more at 10 K than at 300 K. We suggest that the reversed nucleus affects the magnetism more at low temperatures, which causes the coercivity to be higher at low temperature than at room temperature. These results will help us to understand the magnetic properties and temperature characteristics of FeCo thin films.

Magnetic Properties of Hard Magnetic Alloy Fe - 28% Cr - 13.4% Co - 2% Mo - 0.5% Si

NASA Astrophysics Data System (ADS)

Vompe, T. A.; Milyaev, I. M.; Yusupov, V. S.

2017-01-01

The method of regression analysis is used to obtain equations describing the dependences of magnetic hysteresis properties of magnetically hard powder alloy Fe - 28% Cr - 13.4% Co - 2% Mo - 0.5% Si on regimes of thermomagnetic treatment (the temperatures of the start of the treatment and the rates of cooling in magnetic field). The determined treatment modes make it possible to obtain in an alloy with a coercive force H c up to 40 kA/m, a residual induction B r up to 1.2 T, and a maximum energy product ( BH)max up to 25 kJ/m3. The alloy may find application in the production of rotors of synchronous hysteresis-reluctance motors.

Ferromagnetic resonance linewidth and damping in perpendicular-anisotropy magnetic multilayers thin films

NASA Astrophysics Data System (ADS)

Beaujour, Jean-Marc

2010-03-01

Transition metal ferromagnetic films with perpendicular magnetic anisotropy (PMA) have ferromagnetic resonance (FMR) linewidths that are one order of magnitude larger than soft magnetic materials, such as pure iron (Fe) and permalloy (NiFe) thin films. We have conducted systematic studies of a variety of thin film materials with perpendicular magnetic anisotropy to investigate the origin of the enhanced FMR linewidths, including Ni/Co and CoFeB/Co/Ni multilayers. In Ni/Co multilayers the PMA was systematically reduced by irradiation with Helium ions, leading to a transition from out-of-plane to in-plane easy axis with increasing He ion fluence [1,2]. The FMR linewidth depends linearly on frequency for perpendicular applied fields and increases significantly when the magnetization is rotated into the film plane with an applied in-plane magnetic field. Irradiation of the film with Helium ions decreases the PMA and the distribution of PMA parameters, leading to a large reduction in the FMR linewidth for in-plane magnetization. These results suggest that fluctuations in the PMA lead to a large two magnon scattering contribution to the linewidth for in-plane magnetization and establish that the Gilbert damping is enhanced in such materials (α˜0.04, compared to α˜0.002 for pure Fe) [2]. We compare these results to those on CoFeB/Co/Ni and published results on other thin film materials with PMA [e.g., Ref. 3]. [1] D. Stanescu et al., J. Appl. Phys. 103, 07B529 (2008). [2] J-M. L. Beaujour, D. Ravelosona, I. Tudosa, E. Fullerton, and A. D. Kent, Phys. Rev. B RC 80, 180415 (2009). [3] N. Mo, J. Hohlfeld, M. ulIslam, C. S. Brown, E. Girt, P. Krivosik, W. Tong, A. Rebel, and C. E. Patton, Appl. Phys. Lett. 92, 022506 (2008). *Research done in collaboration with: A. D. Kent, New York University, D. Ravelosona, Institut d'Electronique Fondamentale, UMR CNRS 8622, Universit'e Paris Sud, E. E. Fullerton, Center for Magnetic Recording Research, UCSD, and supported by NSF

Microwave magnetic properties of spinel ferrite films deposited by one-step electrochemical method

NASA Astrophysics Data System (ADS)

Zhang, Yao; Yuan, Lixin; Zhang, Xiaozhi; Zhang, Jie; Yue, Zhenxing; Li, Longtu

2017-07-01

Spinel ferrites have been widely used in microwave devices due to their excellent electromagnetic properties. In this study, two kinds of spinel ferrite films, Fe3O4 and Co xFe3-xO4, were grown on Pt(111)/Ti/SiO2/Si substrates by one-step electrochemical deposition method. The XRD and SEM characterizations demonstrated that the orientation of the ferrite films changed from (111) to (100) with the increase of depositing time. The cobalt content within Co xFe3-xO4 films was studied in detail by EDS analysis. The ferromagnetic resonance (FMR) responses of the ferrite films were measured by the flip-chip method using a vector network analyzer (VNA). It showed that the FMR frequency of Fe3O4 films reached to 10.5 GHz under an out-plane magnetic field of 5 kOe, while it reached to 27 GHz under an in-plane magnetic field of 5 kOe for Co xFe3-xO4 films. Meanwhile, whether the magnetic field was applied parallelly or perpendicularly, the resonant peaks were increased linearly with increasing the magnetic field, indicating that the films are promising candidates for applications in tunable wave-absorbing materials or other tunable frequency devices.

Study of electrical and magnetic properties of RE doped layered cobaltite thin films

NASA Astrophysics Data System (ADS)

Bapna, K.; Choudhary, R. J.; Phase, D. M.; Rawat, R.; Ahuja, B. L.

2018-05-01

Thin films of layered perovskites Sr1.5RE0.5CoO4 (RE = La, Gd) were grown on MgO (0 0 1) substrate using pulsed laser ablation method. Structural, electrical and magnetic properties of single phase oriented films were studied. Films reveal semiconducting behavior in the entire measured temperature range. The films show thermally activated behavior at high temperature regime, with a higher value of activation energy for SGCO than that for SLCO. The low temperature behavior is well fitted with 3D-variable range hopping mechanism. Both films showed negative magneto-resistance measured in temperature range of 10-200 K. The value of MR is large for SGCO film as compared to its bulk counterpart as well as SLCO film, suggesting its high potential in the spintronics applications. A pinch-shaped M-H behaviour as observed in both the films, suggests the presence of two-magnetic phases. Occurrence of pinch-shape behaviour is although in line with that of SLCO bulk counterpart, interestingly, it was absent in SGCO polycrystalline powder. It suggests major role of film growth kinetics in modifying the magnetic properties in cobaltites.

Magnetic properties of Pr-Fe-B thick-film magnets deposited on Si substrates with glass buffer layer

NASA Astrophysics Data System (ADS)

Nakano, M.; Kurosaki, A.; Kondo, H.; Shimizu, D.; Yamaguchi, Y.; Yamashita, A.; Yanai, T.; Fukunaga, H.

2018-05-01

In order to improve the magnetic properties of PLD-made Pr-Fe-B thick-film magnets deposited on Si substrates, an adoption of a glass buffer layer was carried out. The glass layer could be fabricated under the deposition rate of approximately 70 μm/h on a Si substrate using a Nd-YAG pulse laser in the vacuum atmosphere. The use of the layer enabled us to reduce the Pr content without a mechanical destruction and enhance (BH)max value by approximately 20 kJ/m3 compared with the average value of non-buffer layered Pr-Fe-B films with almost the same thickness. It is also considered that the layer is also effective to apply a micro magnetization to the films deposited on Si ones.

Tailoring of the soft magnetic property and uniaxial anisotropy of magnetostrictive films by interlayer

NASA Astrophysics Data System (ADS)

Wen, Dandan; Bai, Feiming; Wang, Yicheng; Zhong, Zhiyong; Zhang, Huaiwu

2013-05-01

Laminated amorphous FeSiBC films with various spacer layers, including Cu, Co0.45Cu0.55, Co0.8Cu0.2, and CoFe, were prepared in order to study the effect of interface structure and magnetic exchange interaction on the magnetic softness and uniaxial anisotropy of multilayered film. It is found that laminating FeSiBC film with thin nonmagnetic or weak magnetic spacers yields much lower coercivity and higher remanent magnetization than those with magnetic spacers. Optimal films with the desired properties of Hc ˜ 1.5 Oe, Mr/Ms = 95%, and Hk ˜ 16 Oe were obtained. Therefore, it is confirmed that the exchange interaction constant of spacer layer plays a more important role than that of interface structure. Furthermore, laminating FeSiBC with nonmagnetic layers only slightly changes magnetostrictive coefficient.

Fabrication and properties of Nd(Tb,Dy)Co/Cr films with perpendicular magnetic anisotropy

NASA Astrophysics Data System (ADS)

Cheng, Weiming; Miao, Xiangshui; Yan, Junbing; Cheng, Xiaomin

2009-08-01

Light rare earth-heavy rare earth-transition metal films (LRE-HRE-TM)have large saturation magnetization (Ms) and are the promising media for hybrid recording. In this paper, Nd(Tb,Dy)Co/Cr films with perpendicular magnetic anisotropy were successfully fabricated onto glass substrate by RF magnetron sputtering and the effects of sputtering technology parameters and Nd substitution for HRE atoms on the magnetic properties were investigated. It was found that when the sputtering power and sputtering time are 250W and 4min, respectively, the magnetic properties of Nd(Tb,Dy)Co/Cr films obtain optimization, perpendicular coercivity, Ms and remanence square ratio(S) of NdTbCo/Cr film reach 3.8kOe, 247emu/cm3 and 0.801, respectively. With the increasing of Nd concentration, Ms increases, while the coercivity (Hc)and the temperature stability of magnetic properties decrease distinctly. These results can be explained by the ferri-magnetic structure of the RE-TM alloy.

Perpendicular magnetic anisotropy in Mn{sub 2}CoAl thin film

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sun, N. Y.; Zhang, Y. Q.; Che, W. R.

Heusler compound Mn{sub 2}CoAl (MCA) is attracting more attentions due to many novel properties, such as high resistance, semiconducting behavior and suggestion as a spin-gapless material with a low magnetic moment. In this work, Mn{sub 2}CoAl epitaxial thin film was prepared on MgO(100) substrate by magnetron sputtering. The transport property of the film exhibits a semiconducting-like behavior. Moreover, our research reveals that perpendicular magnetic anisotropy (PMA) can be induced in very thin Mn{sub 2}CoAl films resulting from Mn-O and Co-O bonding at Mn{sub 2}CoAl/MgO interface, which coincides with a recent theoretical prediction. PMA and low saturation magnetic moment could leadmore » to large spin-transfer torque with low current density in principle, and thus our work may bring some unanticipated Heusler compounds into spintronics topics such as the domain wall motion and the current-induced magnetization reversal.« less

Observation of spin superfluidity: YIG magnetic films and beyond

NASA Astrophysics Data System (ADS)

Sonin, Edouard

2018-03-01

From topology of the order parameter of the magnon condensate observed in yttrium-iron-garnet (YIG) magnetic films one must not expect energetic barriers making spin supercurrents metastable. But we show that some barriers of dynamical origin are possible nevertheless until the gradient of the phase (angle of spin precession) does not exceed the critical value (analog of the Landau critical velocity in superfluids). On the other hand, recently published claims of experimental detection of spin superfluidity in YIG films and antiferromagnets are not justified, and spin superfluidity in magnetically ordered solids has not yet been experimentally confirmed.

Effect of heat treatment on interface driven magnetic properties of CoFe films

NASA Astrophysics Data System (ADS)

Singh, Akhilesh Kr.; Hsu, Jen-Hwa

2017-06-01

We report systematic studies on non-magnetic Ta underlayer and cap layer driven microstructural and magnetic properties at a wide temperature range for CoFe films. All the films were grown at room temperature and post annealed at different annealing temperatures (TA = 200 °C, 250 °C, 300 °C, 350 °C, 400 °C and 450 °C). The in-plane magnetic hysteresis (M-H) loops of 10 nm thick CoFe single layer films, grown directly on thermally oxidized Si substrate, exhibit anisotropic nature for TA above 250 °C. However, the CoFe (10 nm) films grown on the 5 nm thick Ta underlayer show reduced anisotropy. Moreover, with underlayer and cap layers (2 nm) the anisotropy is disappeared. The in-plane coercivity (HC) shows a strong variation with TA, underlayer and cap layers. HC increases significantly with Ta underlayer and cap layers. The out of plane M-H loops exhibit increase in the remanence magnetization and squareness with both Ta underlayer and cap layers due to transition of in-plane magnetization component to the out of plane direction. The atomic force microscopic observations revealed that grain/particle size and shape depend strongly on TA and Ta layers. Moreover, a large reduction in the surface roughness is observed with the Ta cap layer. The magnetic domain patterns depend on the TA, and Ta layers. However, for Ta/CoFe/Ta films no clear domains were observed for all the TA. Hence, the Ta cap layers not only protect the CoFe magnetic layer against the heat treatment, but also show a smooth surface at a wide temperature range. These results could be discussed on the basis of random anisotropy model, TA, underlayer and cap layers driven microstructure and magnetization orientation of the CoFe films.

Impact of magnetic fields on the morphology of hybrid perovskite films for solar cells

NASA Astrophysics Data System (ADS)

Corpus-Mendoza, Asiel N.; Moreno-Romero, Paola M.; Hu, Hailin

2018-05-01

The impact of magnetic fields on the morphology of hybrid perovskite films is assessed via scanning electron microscopy and X-ray diffraction. Small-grain non-uniform perovskite films are obtained when a large magnetic flux density is applied to the sample during reaction of PbI2 and methylammonium iodide (chloride). Similarly, X-ray diffraction reveals a change of preferential crystalline planes when large magnetic fields are applied. Furthermore, we experimentally demonstrate that the quality of the perovskite film is affected by the magnetic field induced by the magnetic stirring system of the hot plate where the samples are annealed. As a consequence, optimization of the perovskite layer varies with magnetic field and annealing temperature. Finally, we prove that uncontrolled magnetic fields on the environment of preparation can severely influence the reproducibility of results.

Study on Properties of CoNi Films with mn Doping Prepared by Magnetic Fields Induced Codeposition Technology

NASA Astrophysics Data System (ADS)

Gang, Liang; Yu, Yundan; Ge, Hongliang; Wei, Guoying; Jiang, Li; Sun, Lixia

Magnetic field parallel to electric field was induced during plating process to prepare CoNiMn alloy films on copper substrate. Electrochemistry mechanism and properties of CoNiMn alloy films were investigated in this paper. Micro magnetohydrodynamic convection phenomenon caused by vertical component of current density and parallel magnetic field due to deformation of current distribution contributed directly to the improvement of cathode current and deposition rate. Cathode current of the CoNiMn plating system increased about 30% with 1T magnetic field induced. It was found that CoNiMn films electrodeposited with magnetic fields basically belonged to a kind of progressive nucleation mode. Higher magnetic intensity intended to obtain CoNiMn films with good crystal structures and highly preferred orientations. With the increase of magnetic intensities, surface morphology of CoNiMn alloy films changed from typically nodular to needle-like structures. Compared with coatings electrodeposited without magnetic field, CoNiMn alloy films prepared with magnetic fields possessed better magnetic properties. Coercivity, remanence and saturation magnetization of samples increased sharply when 1T magnetic field was induced during plating process.

Strain effect on the magnetic and transport properties of LaCoO3 thin films

NASA Astrophysics Data System (ADS)

Li, Y.; Peng, S. J.; Wang, D. J.; Wu, K. M.; Wang, S. H.

2018-05-01

LaCoO3 (LCO) has attracted much attention due to the unique magnetic transition and spin transition of Co3+ ions. Epitaxial LCO film exhibits an unexpected ferromagnetism, in contrast to the non-magnetism of bulk LCO. An in-depth study on the property of strained LCO film is of great importance. We have fabricated 30 nm LCO films on various substrates and studied the magnetic and transport properties of films in different strain states (compressed strain for LCO/LaAlO3, tensile strain for LCO/(LaAlO3)0.3(Sr2TaAlO6)0.35, SrTiO3). The in-plane tensiled LCO films exhibit ferromagnetic ground state at 5K and magnetic transition with TC around 85K, while compressed LCO/LaAlO3 film has a negligibly small moment signal. Our results reveal that in-plane tensile strain and tetragonal distortion are much more favorable for stabilizing the FM order in LCO films.

Noise suppression and crosstalk analysis of on-chip magnetic film-type noise suppressor

NASA Astrophysics Data System (ADS)

Ma, Jingyan; Muroga, Sho; Endo, Yasushi; Hashi, Shuichiro; Naoe, Masayuki; Yokoyama, Hiroo; Hayashi, Yoshiaki; Ishiyama, Kazushi

2018-05-01

This paper discusses near field, conduction and crosstalk noise suppression of magnetic films with uniaxial anisotropy on transmission lines for a film-type noise suppressor in the GHz frequency range. The electromagnetic noise suppressions of magnetic films with different permeability and resistivity were measured and simulated with simple microstrip lines. The experimental and simulated results of Co-Zr-Nb and CoPd-CaF2 films agreed with each other. The results indicate that the higher permeability leads to a better near field shielding, and in the frequency range of 2-7 GHz, a higher conduction noise suppression. It also suggests that the higher resistivity results in a better crosstalk suppression in the frequency range below 2 GHz. These results can support the design guidelines of the magnetic film-type noise suppressor used in the next generation IC chip.

Composition dependence of electronic, magnetic, transport and morphological properties of mixed valence manganite thin films

DOE PAGES

Singh, Surendra; Freeland, J. W.; Fitzsimmons, Michael R.; ...

2016-07-27

Mixed-valence manganese oxides present striking properties like the colossal magnetoresistance, metal-insulator transition (MIT) that may result from coexistence of ferromagnetic, metallic and insulating phases. Percolation of such phase coexistence in the vicinity of MIT leads to first-order transition in these manganites. However the length scales over which the electronic and magnetic phases are separated across MIT which appears compelling for bulk systems has been elusive in (La 1-yPr y) 1-xCaxMnO 3 films. Here we show the in-plane length scale over which charge and magnetism are correlated in (La 0.4Pr 0.6) 1-xCaxMnO3 films with x = 0.33 and 0.375, across themore » MIT temperature. We combine electrical transport (resistance) measurements, x-ray absorption spectroscopy (XAS), x-ray magnetic circular dichroism (XMCD), and specular/off-specular x-ray resonant magnetic scattering (XRMS) measurements as a function of temperature to elucidate relationships between electronic, magnetic and morphological structure of the thin films. Using off-specular XRMS we obtained the charge-charge and charge-magnetic correlation length of these LPCMO films across the MIT. We observed different charge-magnetic correlation length for two films which increases below the MIT. The different correlation length shown by two films may be responsible for different macroscopic (transport and magnetic) properties.« less

Temperature dependence dynamical permeability characterization of magnetic thin film using near-field microwave microscopy

NASA Astrophysics Data System (ADS)

Hung, Le Thanh; Phuoc, Nguyen N.; Wang, Xuan-Cong; Ong, C. K.

2011-08-01

A temperature dependence characterization system of microwave permeability of magnetic thin film up to 5 GHz in the temperature range from room temperature up to 423 K is designed and fabricated as a prototype measurement fixture. It is based on the near field microwave microscopy technique (NFMM). The scaling coefficient of the fixture can be determined by (i) calibrating the NFMM with a standard sample whose permeability is known; (ii) by calibrating the NFMM with an established dynamic permeability measurement technique such as shorted microstrip transmission line perturbation method; (iii) adjusting the real part of the complex permeability at low frequency to fit the value of initial permeability. The algorithms for calculating the complex permeability of magnetic thin films are analyzed. A 100 nm thick FeTaN thin film deposited on Si substrate by sputtering method is characterized using the fixture. The room temperature permeability results of the FeTaN film agree well with results obtained from the established short-circuited microstrip perturbation method. Temperature dependence permeability results fit well with the Landau-Lifshitz-Gilbert equation. The temperature dependence of the static magnetic anisotropy H_K^{sta}, the dynamic magnetic anisotropy H_K^{dyn}, the rotational anisotropy Hrot, together with the effective damping coefficient αeff, ferromagnetic resonance fFMR, and frequency linewidth Δf of the thin film are investigated. These temperature dependent magnetic properties of the magnetic thin film are important to the high frequency applications of magnetic devices at high temperatures.

Selective and directional actuation of elastomer films using chained magnetic nanoparticles

NASA Astrophysics Data System (ADS)

Mishra, Sumeet R.; Dickey, Michael D.; Velev, Orlin D.; Tracy, Joseph B.

2016-01-01

We report selective and directional actuation of elastomer films utilizing magnetic anisotropy introduced by chains of Fe3O4 magnetic nanoparticles (MNPs). Under uniform magnetic fields or field gradients, dipolar interactions between the MNPs favor magnetization along the chain direction and cause selective lifting. This mechanism is described using a simple model.We report selective and directional actuation of elastomer films utilizing magnetic anisotropy introduced by chains of Fe3O4 magnetic nanoparticles (MNPs). Under uniform magnetic fields or field gradients, dipolar interactions between the MNPs favor magnetization along the chain direction and cause selective lifting. This mechanism is described using a simple model. Electronic supplementary information (ESI) available: Two videos for actuation while rotating the sample, experimental details of nanoparticle synthesis, polymer composite preparation, and alignment and bending studies, details of the theoretical model of actuation, and supplemental figures for understanding the behavior of rotating samples and results from modelling. See DOI: 10.1039/c5nr07410j

Noncircular skyrmion and its anisotropic response in thin films of chiral magnets under a tilted magnetic field

DOE PAGES

Lin, Shi-Zeng; Saxena, Avadh

2015-11-03

Here we study the equilibrium and dynamical properties of skyrmions in thin films of chiral magnets with oblique magnetic field. The shape of an individual skyrmion is non-circular and the skyrmion density decreases with the tilt angle from the normal of films. As a result, the interaction between two skyrmions depends on the relative angle between them in addition to their separation. The triangular lattice of skyrmions under a perpendicular magnetic field is distorted into a centered rectangular lattice for a tilted magnetic field. For a low skyrmion density, skyrmions form a chain like structure. Lastly, the dynamical response ofmore » the non-circular skyrmions depends on the direction of external currents.« less

Broadband complex permeability characterization of magnetic thin films using shorted microstrip transmission-line perturbation

NASA Astrophysics Data System (ADS)

Liu, Yan; Chen, Linfeng; Tan, C. Y.; Liu, H. J.; Ong, C. K.

2005-06-01

A brief review of the methods used for broadband complex permeability measurement of magnetic thin films up to microwave frequencies is given. In particular, the working principles of the transmission-line perturbation methods for the characterization of magnetic thin films are discussed, with emphasis on short-circuited planar transmission-line perturbation methods. The algorithms for calculating the complex permeability of magnetic thin films for short-circuited planar transmission-line perturbation methods are analyzed. A shorted microstrip line is designed and fabricated as a prototype measurement fixture. The structure of the microstrip fixture and the corresponding measurement procedure are discussed in detail. A piece of 340 nm thick FeTaN thin film deposited on Si substrate using sputtering method is characterized using the microstrip fixture. An improved technique for obtaining permeability by using a saturation magnetization field is demonstrated here, and the results fit well with the Landau-Lifchitz-Gilbert theory. Approaches to extending this method to other aspects in the investigation of magnetic thin film are also discussed.

A film producer focuses on issues of social justice and nurses: an interview with Richard Harding. Interviewed by Kathleen McHugh.

PubMed

Harding, Richard

2012-01-01

This case study of Richard Harding, a producer currently making a film about the Benghazi Six, includes an introductory biography, an interview with the producer, and a brief conclusion. Harding's commitments to both filmmaking and social justice issues led him to The Benghazi Six and the injustices suffered by these Bulgarian nurses, who were persecuted and imprisoned in Libya for 9 years on false charges of infecting Libyan children with HIV. The film production ran alongside of and aided international efforts to free the nurses and one physician from Libya. Copyright © 2012 Elsevier Inc. All rights reserved.

Influence of film thickness on topology and related magnetic interactions in Fe nanoparticle films

NASA Astrophysics Data System (ADS)

Ausanio, G.; Iannotti, V.; Amoruso, S.; Bruzzese, R.; Wang, X.; Aruta, C.; Arzeo, M.; Lanotte, L.

2013-08-01

Fe nanoparticle (NP)-assembled thin films with different thickness were prepared by femtosecond-pulsed laser deposition using different deposition times. The proper selection of the deposition time allows to control, to a certain degree, the morphology and topology of the deposited Fe nanoparticles (NPs) assembly, fostering non-uniform dense assemblies of NPs, with the consequent reduction of the influence of the exchange interactions on the macroscopic magnetic properties with decreasing thickness. The magnetic behavior of the Fe NP-assembled films with decreasing thickness is characterized by higher coercive field ( H c) values (a factor ≈4.5) and a good compromise between the hysteresis loops squareness and moderate exchange interactions, strongly correlated with the NPs topology.

Cap-Induced Magnetic Anisotropy in Ultra-thin Fe/MgO(001) Films

NASA Astrophysics Data System (ADS)

Brown-Heft, Tobias; Pendharkar, Mihir; Lee, Elizabeth; Palmstrom, Chris

Magnetic anisotropy plays an important role in the design of spintronic devices. Perpendicular magnetic anisotropy (PMA) is preferred for magnetic tunnel junctions because the resulting energy barrier between magnetization states can be very high and this allows enhanced device scalability suitable for magnetic random access memory applications. Interface induced anisotropy is often used to control magnetic easy axes. For example, the Fe/MgO(001) system has been predicted to exhibit PMA in the ultrathin Fe limit. We have used in-situ magneto optic Kerr effect and ex-situ SQUID to study the changes in anisotropy constants between bare Fe/MgO(001) films and those capped with MgO, Pt, and Ta. In some cases in-plane anisotropy terms reverse sign after capping. We also observe transitions from superparamagnetic to ferromagnetic behavior induced by capping layers. Perpendicular anisotropy is observed for Pt/Fe/MgO(001) films after annealing to 300°C. These effects are characterized and incorporated into a magnetic simulation that accurately reproduces the behavior of the films. This work was supported in part by the Semiconductor Research Corporation programs (1) MSR-Intel, and (2) C-SPIN.

Magnetic Thin Films for Perpendicular Magnetic Recording Systems

NASA Astrophysics Data System (ADS)

Sugiyama, Atsushi; Hachisu, Takuma; Osaka, Tetsuya

In the advanced information society of today, information storage technology, which helps to store a mass of electronic data and offers high-speed random access to the data, is indispensable. Against this background, hard disk drives (HDD), which are magnetic recording devices, have gained in importance because of their advantages in capacity, speed, reliability, and production cost. These days, the uses of HDD extend not only to personal computers and network servers but also to consumer electronics products such as personal video recorders, portable music players, car navigation systems, video games, video cameras, and personal digital assistances.

Optical investigation of domain resonances in magnetic garnet films

NASA Astrophysics Data System (ADS)

Bahlmann, N.; Gerhardt, R.; Dötsch, H.

1996-08-01

Magnetic garnet films of composition (Y,Bi) 3(Fe,Al) 5O 12 are grown by liquid phase epitaxy on [111] oriented substrates of Gd 3Ga 5O 12. Lattices of parallel stripe domains are stabilized by a static induction applied in the film plane. The two branches DR ± of the domain resonance and the domain wall resonance DWR are excited by microwave magnetic fields in the frequency range up to 6 GHz. Light passing the stripe domain lattice parallel to the film normal is modulated at the excitation frequency. A modulation bandwidth of more than 2 GHz is observed. The resonances can be calculated with high accuracy by a hybridization model, if the quality factor Q of the film exceeds 0.5. For Q < 0.5 a simple approximation is used to describe the superposition of the DR + and DR - resonances. The superposition model predicts two stability states of the resonance DR + which are observed experimentally. From the optical measurements precession angles of the resonance DR - of nearly 6° and wall oscillation amplitudes up to 25 nm are derived.

Field dependent magnetic anisotropy of Fe1-xZnx thin films

NASA Astrophysics Data System (ADS)

Resnick, Damon A.; McClure, A.; Kuster, C. M.; Rugheimer, P.; Idzerda, Y. U.

2013-05-01

Using longitudinal magneto-optical Kerr effect in combination with a variable strength rotating magnetic field, called the Rotational Magneto-Optic Kerr Effect (ROTMOKE) method, we show that the magnetic anisotropy for thin Fe82Zn18 single crystal films, grown on MgO(001) substrates, depends linearly on the strength of the applied magnetic field at low fields but is constant (saturates) at fields greater than 350 Oe. The torque moment curves generated using ROTMOKE are well fit with a model that accounts for the uniaxial and cubic anisotropy with the addition of a cubic anisotropy that depends linearly on the applied magnetic field. The field dependent term is evidence of a large effect on the effective magnetic anisotropy in Fe1-xZnx thin films by the magnetostriction.

Electronic structure and magnetic anisotropy of L1{sub 0}-FePt thin film studied by hard x-ray photoemission spectroscopy and first-principles calculations

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ueda, S.; Synchrotron X-ray Station at SPring-8, National Institute for Materials Science, Sayo, Hyogo 679-5148; Mizuguchi, M.

2016-07-25

We have studied the electronic structure of the L1{sub 0} ordered FePt thin film by hard x-ray photoemission spectroscopy (HAXPES), cluster model, and first-principles calculations to investigate the relationship between the electronic structure and perpendicular magneto-crystalline anisotropy (MCA). The Fe 2p core-level HAXPES spectrum of the ordered film revealed the strong electron correlation in the Fe 3d states and the hybridization between the Fe 3d and Pt 5d states. By comparing the experimental valence band structure with the theoretical density of states, the strong electron correlation in the Fe 3d states modifies the valence band electronic structure of the L1{submore » 0} ordered FePt thin film through the Fe 3d-Pt 5d hybridization. These results strongly suggest that the strong electron correlation effect in the Fe 3d states and the Fe 3d-Pt 5d hybridization as well as the spin-orbit interaction in the Pt 5d states play important roles in the perpendicular MCA for L1{sub 0}-FePt.« less

Magnetic vortex state and multi-domain pattern in electrodeposited hemispherical nanogranular nickel films

NASA Astrophysics Data System (ADS)

Samardak, Alexander; Sukovatitsina, Ekaterina; Ognev, Alexey; Stebliy, Maksim; Davydenko, Alexander; Chebotkevich, Ludmila; Keun Kim, Young; Nasirpouri, Forough; Janjan, Seyed-Mehdi; Nasirpouri, Farzad

2014-12-01

Magnetic states of nickel nanogranular films were studied in two distinct structures of individual and agglomerated granules electrodeposited on n-type Si(1 1 1) surface from a modified Watts bath at a low pH of 2. Magnetic force microscopy and micromagnetic simulations revealed three-dimensional out-of-plane magnetic vortex states in stand-alone hemispherical granules and their arrays, and multi-domain patterns in large agglomerates and integrated films. Once the granules coalesce into small chains or clusters, the coercivity values increased due to the reduction of inter-granular spacing and strengthening of the magnetostatic interaction. Further growth leads to the formation of a continuous granulated film which strongly affected the coercivity and remanence. This was characterized by the domain wall nucleation and propagation leading to a stripe domain pattern. Magnetoresistance measurements as a function of external magnetic field are indicative of anisotropic magnetoresistance (AMR) for the continuous films electrodeposited on Si substrate.

Enhanced lubricant film formation through micro-dimpled hard-on-hard artificial hip joint: An in-situ observation of dimple shape effects.

PubMed

Choudhury, Dipankar; Rebenda, David; Sasaki, Shinya; Hekrle, Pavel; Vrbka, Martin; Zou, Min

2018-05-01

This study evaluates the impact of dimple shapes on lubricant film formation in artificial hip joints. Micro-dimples with 20-50 µm lateral size and 1 ± 0.2 µm depths were fabricated on CrCoMo hip joint femoral heads using a picosecond laser. Tribological studies were performed using a pendulum hip joint simulator to apply continuous swing flexion-extension motions. The results revealed a significantly enhanced lubricant film thickness (≥ 500 nm) with micro-dimpled prosthesis heads at equilibrium position after the lubricant film has fully developed. The average lubricant film thickness of dimpled prostheses with square- and triangular-shaped dimple arrays over time is about 3.5 that of the non-dimpled prosthesis (204 nm). Remarkably, the prosthesis with square-shaped dimple arrays showed a very fast lubricant film formation reaching their peak values within 0.5 s of pendulum movement, followed by prosthesis with triangular-shaped dimple arrays with a transition period of 42.4 s. The fully developed lubricant film thicknesses (≥ 700 nm) are significantly higher than the surface roughness (≈ 25 nm) demonstrating a hydrodynamic lubrication. Hardly any scratches appeared on the post-experimental prosthesis with square-shaped dimple array and only a few scratches were found on the post-experimental prosthesis with triangular-shaped dimple arrays. Thus, prostheses with square-shaped dimple arrays could be a potential solution for durable artificial hip joints. Copyright © 2018 Elsevier Ltd. All rights reserved.

Composition gradient, structure, stress, roughness and magnetic properties of 5-500 nm thin NiFe films obtained by electrodeposition

NASA Astrophysics Data System (ADS)

Gong, Jie; Riemer, Steve; Kautzky, Michael; Tabakovic, Ibro

2016-01-01

The composition gradients of 5-500 nm thin NiFe films on Cu and NiP substrates obtained by electrodeposition in stirred plating solutions at pH 3.0 on 8 in wafers were studied. It was found that the average elemental composition of the NiFe changes during electrodeposition with steep downturns of Fe-content, from 58 to 50 wt% Fe, in composition gradient zone near the substrate interface in the thickness range 5-250 nm depending on the electrode substrate (Cu and NiP). The increase of Fe-content in the composition gradient zone is accompanied by the increase of coercivity, Hc, magnetic flux saturation, Bs, saturation magnetostriction, λs, increase of dimensionless roughness, ρrms, and change of stress, σ. The coercivity (easy and hard axis) follows the Neel's relation Hc=ct-n (t is thickness and c is a constant). The mechanisms related to the change of coercivity of the NiFe films deposited on different substrates (Cu and NiP) are discussed in terms of material properties of these films.

Thick film magnetic nanoparticulate composites and method of manufacture thereof

NASA Technical Reports Server (NTRS)

Ge, Shihui (Inventor); Yan, Dajing (Inventor); Xiao, Danny T. (Inventor); Ma, Xinqing (Inventor); Zhang, Yide (Inventor); Zhang, Zongtao (Inventor)

2009-01-01

Thick film magnetic/insulating nanocomposite materials, with significantly reduced core loss, and their manufacture are described. The insulator coated magnetic nanocomposite comprises one or more magnetic components, and an insulating component. The magnetic component comprises nanometer scale particles (about 1 to about 100 nanometers) coated by a thin-layered insulating phase. While the intergrain interaction between the immediate neighboring magnetic nanoparticles separated by the insulating phase provides the desired soft magnetic properties, the insulating material provides high resistivity, which reduces eddy current loss.

Coercivity mechanisms and thermal stability of thin film magnetic recording media

NASA Astrophysics Data System (ADS)

Yang, Cheng

1999-09-01

Coercivity mechanisms and thermal stability of magnetic recording media were studied. It was found that magnetization reversal mainly occurs by nucleation mechanism. The correlation was established between the c/ a ratio of Co HCP structure and other process parameters that are thought to be the dominant factors in determining the anisotropy and therefore the coercivity of Co based thin film magnetic recording media. Time decay and switching of the magnetization in thin film magnetic recording media depend on the grain size distribution and easy-axis orientation distribution according to the proposed two- energy-level model. Relaxation time is the most fundamental parameter that determines the time decay performance of the magnetic recording media. An algorithm was proposed to calculate its distribution directly from the experimental data without any presumption. It was found for the first time that the distribution of relaxation time takes the form of Weibull distribution.

Dynamical formation of spatially localized arrays of aligned nanowires in plastic films with magnetic anisotropy.

PubMed

Fragouli, Despina; Buonsanti, Raffaella; Bertoni, Giovanni; Sangregorio, Claudio; Innocenti, Claudia; Falqui, Andrea; Gatteschi, Dante; Cozzoli, Pantaleo Davide; Athanassiou, Athanassia; Cingolani, Roberto

2010-04-27

We present a simple technique for magnetic-field-induced formation, assembling, and positioning of magnetic nanowires in a polymer film. Starting from a polymer/iron oxide nanoparticle casted solution that is allowed to dry along with the application of a weak magnetic field, nanocomposite films incorporating aligned nanocrystal-built nanowire arrays are obtained. The control of the dimensions of the nanowires and of their localization across the polymer matrix is achieved by varying the duration of the applied magnetic field, in combination with the evaporation dynamics. These multifunctional anisotropic free-standing nanocomposite films, which demonstrate high magnetic anisotropy, can be used in a wide field of technological applications, ranging from sensors to microfluidics and magnetic devices.

Electrodeposition of catalytic and magnetic gold nanoparticles on dendrimer-carbon nanotube layer-by-layer films.

PubMed

Siqueira, José R; Gabriel, Rayla C; Zucolotto, Valtencir; Silva, Anielle C A; Dantas, Noelio O; Gasparotto, Luiz H S

2012-11-07

Magnetic and catalytic gold nanoparticles were electrodeposited through potential pulse on dendrimer-carbon nanotube layer-by-layer (LbL) films. A plasmon absorption band at about 550 nm revealed the presence of nanoscale gold in the film. The location of the Au nanoparticles in the film was clearly observed by selecting the magnetic force microscopy mode. To our knowledge, this is the first report on the electrochemical synthesis of magnetic Au nanoparticles. In addition to the magnetic properties, the Au nanoparticles also exhibited high catalytic activity towards ethanol and glycerol oxidation in alkaline medium.

Improvement in surface conditions of electroplated Fe-Pt thick-film magnets

NASA Astrophysics Data System (ADS)

Yanai, T.; Honda, J.; Hamamura, R.; Omagari, Y.; Yamada, H.; Fujita, N.; Takashima, K.; Nakano, M.; Fukunaga, H.

2018-05-01

Fe-Pt thick-films were electroplated on Ta, Ti, Co, Ni, and Cu plates (substrates) using a direct current, and the surface morphology, the magnetic properties, and the crystal structure of the films were evaluated. The films plated on the Co, Ni, and Cu substrates showed much smooth surface compared with those for the Ta and Ti ones, and we confirmed that the Cu plate was the most attractive substrate due to very small cracks after an annealing for L10 ordering. High coercivity (>800 kA/m) for the Cu substrate is almost the same as that for our previous study in which we employed the Ta substrate, and we found that the Cu plate is a hopeful substrate to improve the surface conditions of electroplated Fe-Pt thick-film magnets.

Octahedral tilt independent magnetism in confined GdTiO3 films

NASA Astrophysics Data System (ADS)

Need, R. F.; Isaac, B. J.; Kirby, B. J.; Borchers, J. A.; Stemmer, S.; Wilson, Stephen D.

2018-03-01

Low temperature polarized neutron reflectometry measurements are presented, exploring the evolution of ferrimagnetism in thin GdTiO3 films embedded within a SrTiO3 matrix. In GdTiO3 films thinner than ˜4 nm, the TiO6 octahedral tilts endemic to GdTiO3 coherently relax toward the undistorted, cubic phase of SrTiO3. Our measurements indicate that the ferrimagnetic state within the GdTiO3 layers survives as these TiO6 octahedral tilts are suppressed. Furthermore, our data suggest that layers of suppressed magnetization (i.e., magnetic dead layers) develop within the GdTiO3 layer at each GdTiO3/SrTiO3 interface and explain the apparent magnetization suppression observed in thin GdTiO3 films when using volume-averaged techniques. Our data show that the low temperature magnetic moment inherent to the core GdTiO3 layers is only weakly impacted as the octahedral tilt angles are suppressed by more than 50% and the t2 g bandwidth is dramatically renormalized.

Spin Currents and Ferromagnetic Resonance in Magnetic Thin Films

NASA Astrophysics Data System (ADS)

Ellsworth, David

Spin currents represent a new and exciting phenomenon. There is both a wealth of new physics to be discovered and understood, and many appealing devices which may result from this area of research. To fully realize the potential of this discipline it is necessary to develop new methods for realizing spin currents and explore new materials which may be suitable for spin current applications. Spin currents are an inherently dynamic phenomenon involving the transfer of angular momentum within and between different thin films. In order to understand and optimize such devices the dynamics of magnetization must be determined. This dissertation reports on novel approaches for spin current generation utilizing the magnetic insulators yttrium iron garnet (YIG) and M-type barium hexagonal ferrite (BaM). First, the light-induced spin Seebeck effect is reported for the first time in YIG. Additionally, the first measurement of the spin Seebeck effect without an external magnetic field is demonstrated. To accomplish this the self-biased BaM thin films are utilized. Second, a new method for the generation of spin currents is presented: the photo-spin-voltaic effect. In this new phenomenon, a spin current may be generated by photons in a non-magnetic metal that is in close proximity to a magnetic insulator. On exposure to light, there occurs a light induced, spin-dependent excitation of electrons in a few platinum layers near the metal/magnetic insulator interface. This excitation gives rise to a pure spin current which flows in the metal. This new effect is explored in detail and extensive measurements are carried out to confirm the photonic origin of the photo-spin-voltaic effect and exclude competing effects. In addition to the spin current measurements, magnetization dynamics were probed in thin films using ferromagnetic resonance (FMR). In order to determine the optimal material configuration for magnetic recording write heads, FMR measurements were used to perform damping

The rotational hysteresis losses in thin films with unidirectional magnetic anisotropy

NASA Astrophysics Data System (ADS)

Mucha, J. M.; Vatskichev, L.; Vatskicheva, M.

1992-03-01

Using the Planar Hall Effect (PHE) the rotational hysteresis losses in NiFeGe thin magnetic films were measured. The calculation of the critical field for magnetization and rotational hysteresis losses based on extended Stoner-Wohlfarth theory including an exchange magnetic field is given.

Experimental Evidence of Dipolar Interaction in Bilayer Nanocomposite Magnets

DTIC Science & Technology

2010-11-25

corporated to improve experimental systems. However, re- ported bulk nanocomposite magnets exhibit (BH)max val- ues that are far below the...Appl Phys A DOI 10.1007/s00339-010-6073-6 Experimental evidence of dipolar interaction in bilayer nanocomposite magnets A.J. Zambano · H. Oguchi · I...Abstract We use magnetic thin film hard/non/soft-mag- netic trilayer systems to probe the nature of the hard–soft phase interaction and the role

Electronic and magnetic properties of manganite thin films with different compositions and its correlation with transport properties: An X-ray resonant magnetic scattering study

DOE PAGES

Singh, Surendra; Freeland, J. W.; Fitzsimmons, M. R.; ...

2014-12-08

Here, we present x-ray resonant magnetic dichroism and x-ray resonant magnetic scattering measurements of the temperature dependence of magnetism in Pr-doped La-Ca-Mn-O films grown on (110) NdGaO3 substrates. We observed thermal hysteresis of the ferromagnetism in one film that also showed large thermal hysteresis of ~18K in transport measurements. While in a second film of a different nominal chemistry, which showed very small thermal hysteresis ~3K in transport measurements, no thermal hysteresis of the ferromagnetism was observed. As a result, these macroscopic properties are correlated with evolution of surface magnetization across metal insulator transition for these films as observed bymore » soft x-ray resonant magnetic scattering measurements.« less

Influences of different parameters on the microstructure of magnetic-field-induced self-assembled film

NASA Astrophysics Data System (ADS)

Dan, X.; Yang, J. J.

2016-07-01

Self-assembled films with needle-like microarrays were fabricated using a mixture of cobalt and fluorocarbon resin under a magnetic field. The various influences of magnetic powder content, viscosity and size distribution on the structure of the self-assembled films were investigated. The self-assembled film morphologies were characterized by stereomicroscope and scanning electron microscopy. Experimental results indicate that an increase in magnetic powder content results in greater unit height and diameter, and that a reduction in viscosity results in increasing array density and decreasing unit width. Additionally, particles with narrow size distribution were able to attain more regular microarray structures. The structural alterations were closely related to numerous effects such as van der Waals forces, dipole-dipole interactions, and external-dipole interactions. The self-assembled film demonstrated magnetic anisotropy, as identified by vibrating sample magnetometry (VSM).

Eddy Current, Magnetic Particle and Hardness Testing, Aviation Quality Control (Advanced): 9227.04.

ERIC Educational Resources Information Center

Dade County Public Schools, Miami, FL.

This unit of instruction includes the principles of eddy current, magnetic particle and hardness testing; standards used for analyzing test results; techniques of operating equipment; interpretation of indications; advantages and limitations of these methods of testing; care and calibration of equipment; and safety and work precautions. Motion…

Influence of external magnetic field on the microwave absorption properties of carbonyl iron and polychloroprene composites film

NASA Astrophysics Data System (ADS)

Wang, Haiyan; Li, Mingjie; Li, Xueai

2016-12-01

The carbonyl iron particles were dispersed in a polychloroprene rubber (CR) matrix under a magnetic field for a practical application as microwave absorption composites film. In comparison with the carbonyl iron particles (CIP)/CR composites film prepared by general route, such films made with external magnetic field exhibit excellent microwave absorption properties, strongly depending on the increment of anisotropy and rearrangement of magnetic particles. The film made under external magnetic field with a thickness of only 0.54 mm shows least reflection loss of -15.98 dB and the reflection loss value less than -10.0 dB over the frequency range of 11.4˜14.8 GHz. The results indicated the composite film made under external magnetic field have excellent microwave absorption properties, which suggest that the composites thin film could be used as a thinner and lighter microwave absorber.

Oxygen content tailored magnetic and electronic properties in cobaltite double perovskite thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Harrell, Zach John; Enriquez, Erik M.; Chen, Aiping

Oxygen content in transition metal oxides is one of the most important parameters to control for the desired physical properties. Recently, we have systematically studied the oxygen content and property relationship of the double perovskite PrBaCo 2O 5.5+δ (PBCO) thin films deposited on the LaAlO 3 substrates. The oxygen content in the films was varied by in-situ annealing in a nitrogen, oxygen, or ozone environment. Associated with the oxygen content, the out-of-plane lattice parameter progressively decreases with increasing oxygen content in the films. The saturated magnetization shows a drastic increase and resistivity is significantly reduced in the ozone annealed samples,more » indicating the strong coupling between physical properties and oxygen content. Furthermore, these results demonstrate that the magnetic properties of PBCO films are highly dependent on the oxygen contents, or the film with higher oxygen uptake has the largest magnetization.« less

Oxygen content tailored magnetic and electronic properties in cobaltite double perovskite thin films

DOE PAGES

Harrell, Zach John; Enriquez, Erik M.; Chen, Aiping; ...

2017-02-27

Oxygen content in transition metal oxides is one of the most important parameters to control for the desired physical properties. Recently, we have systematically studied the oxygen content and property relationship of the double perovskite PrBaCo 2O 5.5+δ (PBCO) thin films deposited on the LaAlO 3 substrates. The oxygen content in the films was varied by in-situ annealing in a nitrogen, oxygen, or ozone environment. Associated with the oxygen content, the out-of-plane lattice parameter progressively decreases with increasing oxygen content in the films. The saturated magnetization shows a drastic increase and resistivity is significantly reduced in the ozone annealed samples,more » indicating the strong coupling between physical properties and oxygen content. Furthermore, these results demonstrate that the magnetic properties of PBCO films are highly dependent on the oxygen contents, or the film with higher oxygen uptake has the largest magnetization.« less

Magnetic field dependence of the current flowing in the spin-coated chlorophyll thin films

NASA Astrophysics Data System (ADS)

Aji, J. R. P.; Kusumandari; Purnama, B.

2018-03-01

The magnetic dependence of the current flowing in the spin coated chlorophyll films on a patterned Cu PCB substrate has been presented. Chlorophyll was isolated from Spirulina sp and deposited by spin coated methods. The reducing of current by the change of magnetic field (magneto conductance effect) was performed by inducing the magnetic field parallel to the inplane of film at room temp. The magnetoconductance ratio decreases as the increase of voltage. It was indicated that the origin of carrier charge in chlorophyll films should be different with the carrier charge injection (electron).

Characteristics of Iron-Palladium alloy thin films deposited by magnetron sputtering

NASA Astrophysics Data System (ADS)

Chiu, Y.-J.; Shen, C.-Y.; Chang, H.-W.; Jian, S.-R.

2018-06-01

The microstructural features, magnetic, nanomechanical properties and wettability behaviors of Iron-Palladium (FePd) alloy thin films are investigated by using X-ray diffraction (XRD), atomic force microscopy (AFM), vibrating sample magnetometer (VSM), nanoindentation and water contact angle (CA) techniques, respectively. The FePd alloy thin films were deposited on glass substrates using a magnetron sputtering system. The post-annealing processes of FePd alloy thin films were carried out at 400 °C and 750 °C and resulted in a significant increase of both the average grain size and surface roughness. The XRD analysis showed that FePd alloy thin films exhibited a predominant (1 1 1) orientation. The magnetic field dependence of magnetization of all FePd thin films are measured at room temperature showed the ferromagnetic characteristics. The nanoindentation with continuous stiffness measurement (CSM) is used to measure the hardness and Young's modulus of present films. The contact angle (θCA) increased with increasing surface roughness. The maximum θCA of 75° was achieved for the FePd alloy thin film after annealing at 750 °C and a surface roughness of 4.2 nm.

Tuning the Magnetic and Electronic Properties of Iron(x )Silicon(1-x) Thin Films for Spintronics

NASA Astrophysics Data System (ADS)

Karel, Julie Elizabeth

average there are the same number of Fe-Fe first nearest neighbor pairs in both structures. Only the second nearest neighbor environments, which have a weaker effect on the magnetic moment, are different. An enhanced magnetic moment due to enhanced spin and orbital moments was observed in all amorphous films versus crystalline films of the same composition. Not surprisingly, the electronic properties were also found to depend strongly on chemical and structural order, based on hard X-ray photoemission spectroscopy and DFT calculations. The core-level peaks in the amorphous structure (x=0.67) show little broadening despite a significant energy shift, suggesting that the local environment around the Si atoms is different than in the crystalline materials but far more uniform than expected, consistent with XAFS results, which showed that Si is well-ordered. A well-resolved Si 2p spin-orbit splitting for two epitaxial alloys, x=0.72 (D03) and 0.67 (B2) suggests that nearest-neighbor interactions are the dominant effect on binding energy for the Si atoms in the sample. The Si 2p peak in the amorphous sample also shows spin-orbit splitting, another indication that the local structure around each Si atom is relatively well defined. The valence bands show a broadening of the features when chemical and structural disorder is increased, consistent with theoretical band structure calculations for D03, B2, A2 and amorphous structures. Lastly, the anomalous Hall effect, observed in all films, was very large in the amorphous films versus epitaxial films with the same composition. To investigate the origins of the AHE, sigmaxy/M z was plotted versus sigmaxx, allowing for comparison to recent theoretical calculations. In the epitaxial films, sigma xy/Mz is constant, meaning the AHE is dominated by the intrinsic mechanism, as predicted theoretically in this moderate longitudinal conductivity regime. The AHE in the low conductivity regime (amorphous films) shows a scaling with conductivity

Magnetic properties and thermal stability of Ti-doped CrO2 films

NASA Astrophysics Data System (ADS)

Zhang, Z.; Cheng, M.; Lu, Z.; Yu, Z.; Liu, S.; Liang, R.; Liu, Y.; Shi, J.; Xiong, R.

2018-04-01

Chromium dioxide (CrO2) is a striking half metal material which may have important applications in the field of spintronics. However, pure CrO2 film is metastable at room temperature and the synthesis process can be only performed in a narrow temperature range of 390-410 °C with TiO2 used as substrate material. Here, we report the preparation and investigation of (1 0 0) oriented Ti-doped CrO2 films on TiO2 substrates. It is found that Ti-doped films can maintain pure rutile phase even after a 510 °C post-annealing, showing much better thermal stability than pure CrO2 films. Ti-doped films can be prepared in a wider temperature window (390-470 °C), which may be attributed to the improvement of thermal stability. The broadening of process window may be beneficial for further improvement of film quality by optimizing growth temperature in a larger range. In addition to the improvement of thermal stability, the magnetic properties of Ti-doped CrO2 are also found to be tuned by Ti doping: saturation magnetizations of Ti-doped films at room temperature are significantly lower, and magnetic anisotropy decreases as the Ti-concentration increases, which is beneficial for decreasing switching current density in STT-based spintronic devices.

Three-dimensional simulations of thin ferro-fluid films and drops in magnetic fields

NASA Astrophysics Data System (ADS)

Conroy, Devin; Wray, Alex; Matar, Omar

2016-11-01

We consider the interfacial dynamics of a thin, ferrofluidic film flowing down an inclined substrate, under the action of a magnetic field, bounded above by an inviscid gas. The fluid is assumed to be weakly-conducting. Its dynamics are governed by a coupled system of the steady Maxwell's, the Navier-Stokes, and continuity equations. The magnetisation of the film is a function of the magnetic field, and is prescribed by a Langevin function. We make use of a long-wave reduction in order to solve for the dynamics of the pressure, velocity, and magnetic fields inside the film. The potential in the gas phase is solved with the use of Fourier Transforms. Imposition of appropriate interfacial conditions allows for the construction of an evolution equation for the interfacial shape, via use of the kinematic condition, and the magnetic field. We consider the three-dimensional evolution of the film to spawise perturbations by solving the non-linear equations numerically. The constant flux configuration is considered, which corresponds to a thin film and drop flowing down an incline, and a parametric study is performed to understand the effect of a magnetic field on the stability and structure of the formed drops. EPSRC UK platform Grant MACIPh (EP/L020564/1) and programme Grant MEMPHIS (EP/K003976/1).

Modification of structure and magnetic anisotropy of epitaxial CoFe₂O₄ films by hydrogen reduction

DOE PAGES

Chen, Aiping; Poudyal, Narayan; Xiong, Jie; ...

2015-03-16

Heteroepitaxial CoFe₂O₄ (CFO) thin films with different thicknesses were deposited on MgO (001) substrates. The as-deposited CFO films show a clear switching of magnetic anisotropy with increasing film thickness. The thinner films (<100 nm) show a perpendicular magnetic anisotropy due to the out-of-plane compressive strain. The thicker films exhibit an in-plane easy axis owing to the dominating shape anisotropy effect. The magnetostriction coefficient of CFO films is estimated to be λ[001] =-188 × 10⁻⁶. Metallic CoFe₂ films were obtained by annealing the as-deposited CFO films in forming gas (Ar 93% + H₂ 7%) at 450 °C. XRD shows that CoFe₂more » films are textured out-of-plane and aligned in-plane, owing to lattice matching between CoFe₂ and MgO substrate. TEM results indicate that as-deposited films are continuous while the annealed films exhibit a nanopore mushroom structure. The magnetic anisotropy of CoFe₂ films is dominated by the shape effect. The results demonstrate that hydrogen reduction can be effectively used to modify microstructures and physical properties of complex metal oxide materials.« less

Unexpected structural and magnetic depth dependence of YIG thin films

NASA Astrophysics Data System (ADS)

Cooper, J. F. K.; Kinane, C. J.; Langridge, S.; Ali, M.; Hickey, B. J.; Niizeki, T.; Uchida, K.; Saitoh, E.; Ambaye, H.; Glavic, A.

2017-09-01

We report measurements on yttrium iron garnet (YIG) thin films grown on both gadolinium gallium garnet (GGG) and yttrium aluminum garnet (YAG) substrates, with and without thin Pt top layers. We provide three principal results: the observation of an interfacial region at the Pt/YIG interface, we place a limit on the induced magnetism of the Pt layer, and confirm the existence of an interfacial layer at the GGG/YIG interface. Polarized neutron reflectometry (PNR) was used to give depth dependence of both the structure and magnetism of these structures. We find that a thin film of YIG on GGG is best described by three distinct layers: an interfacial layer near the GGG, around 5 nm thick and nonmagnetic, a magnetic "bulk" phase, and a nonmagnetic and compositionally distinct thin layer near the surface. We theorize that the bottom layer, which is independent of the film thickness, is caused by Gd diffusion. The top layer is likely to be extremely important in inverse spin Hall effect measurements, and is most likely Y2O3 or very similar. Magnetic sensitivity in the PNR to any induced moment in the Pt is increased by the existence of the Y2O3 layer; any moment is found to be less than 0.02 μB/atom .

Conductive, magnetic and structural properties of multilayer films

NASA Astrophysics Data System (ADS)

Kotov, L. N.; Turkov, V. K.; Vlasov, V. S.; Lasek, M. P.; Kalinin, Yu E.; Sitnikov, A. V.

2013-12-01

Composite-semiconductor and composite-dielectric multilayer films were obtained by the ion beam sputtering method in the argon and hydrogen atmospheres with compositions: {[(Co45-Fe45-Zr10)x(Al2O3)y]-[α-Si]}120, {[(Co45-Ta45-Nb10)x(SiO2)y]-[SiO2]}56, {[(Co45-Fe45-Zr10)x(Al2O3)y]-[α-Si:H]}120. The images of surface relief and distribution of the dc current on composite layer surface were obtained with using of atomic force microscopy (AFM). The dependencies of specific electric resistance, ferromagnetic resonance (FMR) fields and width of line on metal (magnetic) phase concentration x and nanolayers thickness of multilayer films were obtained. The characteristics of FMR depend on magnetic interaction among magnetic granules in the composite layers and between the layers. These characteristics depend on the thickness of composite and dielectric or semiconductor nanolayers. The dependences of electric microwave losses on the x and alternating field frequency were investigated.

Effects of thermal annealing on the structural, mechanical, and tribological properties of hard fluorinated carbon films deposited by plasma enhanced chemical vapor deposition

NASA Astrophysics Data System (ADS)

Maia da Costa, M. E. H.; Baumvol, I. J. R.; Radke, C.; Jacobsohn, L. G.; Zamora, R. R. M.; Freire, F. L.

2004-11-01

Hard amorphous fluorinated carbon films (a-C:F) deposited by plasma enhanced chemical vapor deposition were annealed in vacuum for 30 min in the temperature range of 200-600 °C. The structural and compositional modifications were followed by several analytical techniques: Rutherford backscattering spectrometry (RBS), elastic recoil detection analysis (ERDA), x-ray photoelectron spectroscopy (XPS) and Raman spectroscopy. Nanoidentation measurements and lateral force microscopy experiments were carried out in order to provide the film hardness and the friction coefficient, respectively. The internal stress and contact angle were also measured. RBS, ERDA, and XPS results indicate that both fluorine and hydrogen losses occur for annealing temperatures higher than 300 °C. Raman spectroscopy shows a progressive graphitization upon annealing, while the surface became slightly more hydrophobic as revealed by the increase of the contact angle. Following the surface wettability reduction, a decrease of the friction coefficient was observed. These results highlight the influence of the capillary condensation on the nanoscale friction. The film hardness and the internal stress are constant up to 300 °C and decrease for higher annealing temperatures, showing a direct correlation with the atomic density of the films. Since the thickness variation is negligible, the mass loss upon thermal treatment results in amorphous structures with a lower degree of cross-linking, explaining the deterioration of the mechanical properties of the a-C:F films.

Synthesis and magnetic properties of cobalt-iron/cobalt-ferrite soft/hard magnetic core/shell nanowires

NASA Astrophysics Data System (ADS)

Leandro Londoño-Calderón, César; Moscoso-Londoño, Oscar; Muraca, Diego; Arzuza, Luis; Carvalho, Peterson; Pirota, Kleber Roberto; Knobel, Marcelo; Pampillo, Laura Gabriela; Martínez-García, Ricardo

2017-06-01

A straightforward method for the synthesis of CoFe2.7/CoFe2O4 core/shell nanowires is described. The proposed method starts with a conventional pulsed electrodeposition procedure on alumina nanoporous template. The obtained CoFe2.7 nanowires are released from the template and allowed to oxidize at room conditions over several weeks. The effects of partial oxidation on the structural and magnetic properties were studied by x-ray spectrometry, magnetometry, and scanning and transmission electron microscopy. The results indicate that the final nanowires are composed of 5 nm iron-cobalt alloy nanoparticles. Releasing the nanowires at room conditions promoted surface oxidation of the nanoparticles and created a CoFe2O4 shell spinel-like structure. The shell avoids internal oxidation and promotes the formation of bi-magnetic soft/hard magnetic core/shell nanowires. The magnetic properties of both the initial single-phase CoFe2.7 nanowires and the final core/shell nanowires, reveal that the changes in the properties from the array are due to the oxidation more than effects associated with released processes (disorder and agglomeration).

Synthesis and magnetic properties of cobalt-iron/cobalt-ferrite soft/hard magnetic core/shell nanowires.

PubMed

Londoño-Calderón, César Leandro; Moscoso-Londoño, Oscar; Muraca, Diego; Arzuza, Luis; Carvalho, Peterson; Pirota, Kleber Roberto; Knobel, Marcelo; Pampillo, Laura Gabriela; Martínez-García, Ricardo

2017-06-16

A straightforward method for the synthesis of CoFe 2.7 /CoFe 2 O 4 core/shell nanowires is described. The proposed method starts with a conventional pulsed electrodeposition procedure on alumina nanoporous template. The obtained CoFe 2.7 nanowires are released from the template and allowed to oxidize at room conditions over several weeks. The effects of partial oxidation on the structural and magnetic properties were studied by x-ray spectrometry, magnetometry, and scanning and transmission electron microscopy. The results indicate that the final nanowires are composed of 5 nm iron-cobalt alloy nanoparticles. Releasing the nanowires at room conditions promoted surface oxidation of the nanoparticles and created a CoFe 2 O 4 shell spinel-like structure. The shell avoids internal oxidation and promotes the formation of bi-magnetic soft/hard magnetic core/shell nanowires. The magnetic properties of both the initial single-phase CoFe 2.7 nanowires and the final core/shell nanowires, reveal that the changes in the properties from the array are due to the oxidation more than effects associated with released processes (disorder and agglomeration).

Nanofabrication and ion milling introduced effects on magnetic properties in magnetic recording

NASA Astrophysics Data System (ADS)

Sun, Zhenzhong

Perpendicular magnetic nanostructures have played an important role in magnetic recording technologies. In this dissertation, a systematic study on the CoPt magnetic nanostructures from fabrication, characterization to computer simulation has been performed. During the fabrication process, ion irradiation/bombardment in ion mill can cause physical damage to the magnetic nanostructures and degrade their magnetic properties. To study the effect of ion damage on CoPt nanostructures, different degrees of ion damage are introduced into CoPt nanopillars by varying the accelerating voltage in ion mill. The results demonstrate that the ion damage can reduce the coercivity by softening circumferential edge, and therefore changes the switching mechanism from coherent rotation to nucleation followed by rapid domain wall propagation. The SFD of CoPt nanostructures is independent of ion damage and is mainly determined by the intrinsic anisotropy distribution of the film rather than the nanostructure size distribution. Anisotropy-graded bit-patterned media are fabricated and studied based on high anisotropy L10-FePt material system. L10-FePt thin films with linearly and quadratically distributed anisotropy are achieved by varying substrate temperature during film growth. After patterning, the anisotropy-graded L10-FePt nanopillars display a reduced switching field and maintain a good thermal stability compared to the non-graded one. Experimental investigation and comparison further prove the concept of "anisotropy-graded" bit-patterned media and their potential application in the future magnetic recording. During magnetic write head fabrication, ion-beam damage may degrade the performance of the magnetic write pole. A surface sensitive MOKE is used to characterize the magnetic properties of these etched FeCo films. MOKE measurement shows a hard axis hysteresis loop with a high Mr in the high power etched film due to the ion beam introduced defects. The high power etched film

Substrate effect on the magnetic microstructure of La{sub 0.7}Sr{sub 0.3}MnO{sub 3} thin films studied by magnetic force microscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Desfeux, R.; Bailleul, S.; Da Costa, A.

2001-06-04

Colossal magnetoresistive La{sub 0.7}Sr{sub 0.3}MnO{sub 3} thin films have been grown under tensile strains on (100)-SrTiO{sub 3} substrates and compressive strains on (100)-LaAlO{sub 3} and (110)-NdGaO{sub 3} substrates by pulsed laser deposition. Using magnetic force microscopy (MFM), a {open_quotes}feather-like{close_quotes} magnetic pattern, characteristic of films with an in-plane magnetization, is observed for films deposited on both SrTiO{sub 3} and NdGaO{sub 3} while a {open_quotes}bubble{close_quotes} magnetic pattern, typical of films with an out-of-plane magnetization, is recorded for LaAlO{sub 3}. We show that the shape of the magnetic pattern imaged by MFM is fully correlated to the easy direction of the magnetization inmore » the film. {copyright} 2001 American Institute of Physics.« less

Structural and Magnetic Properties of Sputter-Deposited Polycrystalline Ni-Mn-Ga Ferromagnetic Shape-Memory Thin Films

NASA Astrophysics Data System (ADS)

Vinodh Kumar, S.; Seenithurai, S.; Manivel Raja, M.; Mahendran, M.

2015-10-01

Polycrystalline Ni-Mn-Ga ferromagnetic shape-memory thin films have been deposited on Si (100) substrates using a direct-current magnetron sputtering technique. The microstructure and the temperature dependence of magnetic properties of the films have been investigated by x-ray diffraction, scanning electron microscopy, and thermomagnetic measurements. As-deposited Ni50.2Mn30.6Ga19.2 film showed quasi-amorphous structure with paramagnetic nature at room temperature. When annealed at 873 K, the quasi-amorphous film attained crystallinity and possessed L21 cubic ordering with high magnetic transition temperature. Saturation magnetization and coercivity values for the annealed film were found to be 220 emu/cm3 and 70 Oe, respectively, indicating soft ferromagnetic character with low magnetocrystalline anisotropy. The magnetic transitions of the film deposited at 100 W were above room temperature, making this a potential candidate for use in microelectromechanical system devices.

Effect of magnetization boundary condition on cavity magnon polariton of YIG thin film.

PubMed

Jiang, H H; Xiao, Y; Hu, C M; Guo, H; Xia, K

2018-06-22

Motivated by recent studies of cavity magnon polariton (CMP), we extended a previous theoretical work to generalize microwave transmission calculation with various magnetization boundary condition of YIG thin film embedded in cavity. It is found that numerical implementation given in this paper can be easily applied to other magnetization boundary condition and extended to magnetic multilayers. Numerical results show that ferromagnetic resonance mode of microwave transmission spectrum, which is absent in previous calculation, can be recovered by altering the pinning condition of surface spins. The demonstrated reliability of our theory opens attractive perspectives for studying CMP of thin film with complicated surface magnetization distribution and magnetic multilayers.

Electronic structure and magnetic properties of Ni-doped SnO2 thin films

NASA Astrophysics Data System (ADS)

Sharma, Mayuri; Kumar, Shalendra; Alvi, P. A.

2018-05-01

This paper reports the electronic structure and magnetic properties of Ni-doped SnO2 thin film which were grown on Si (100) substrate by PLD (pulse laser deposition) technique under oxygen partial pressure (PO2). For getting electronic structure and magnetic behavior, the films were characterized using near edge X-ray absorption fine structure spectroscopy (NEXAFS) and DC magnetization measurements. The NEXAFS study at Ni L3,2 edge has been done to understand the local environment of Ni and Sn ions within SnO2 lattice. DC magnetization measurement shows that the saturation magnetization increases with the increase in substitution of Ni2+ ions in the system.

Effect of magnetization boundary condition on cavity magnon polariton of YIG thin film

NASA Astrophysics Data System (ADS)

Jiang, H. H.; Xiao, Y.; Hu, C. M.; Guo, H.; Xia, K.

2018-06-01

Motivated by recent studies of cavity magnon polariton (CMP), we extended a previous theoretical work to generalize microwave transmission calculation with various magnetization boundary condition of YIG thin film embedded in cavity. It is found that numerical implementation given in this paper can be easily applied to other magnetization boundary condition and extended to magnetic multilayers. Numerical results show that ferromagnetic resonance mode of microwave transmission spectrum, which is absent in previous calculation, can be recovered by altering the pinning condition of surface spins. The demonstrated reliability of our theory opens attractive perspectives for studying CMP of thin film with complicated surface magnetization distribution and magnetic multilayers.

Unidirectional magnetoresistance in magnetic thin films with non-uniform thickness

NASA Astrophysics Data System (ADS)

Jia, M. W.; Zhou, C.; Zeng, F. L.; Wu, Y. Z.

2018-05-01

The magnetoresistance (MR) of Co film and Co/Pt bilayers was studied systematically as a function of Co and Pt thickness at room temperature. In the samples with the wedge shape, we found the unidirectional MR which has the characteristics of R (Mz )≠R (-Mz ) with the magnetization normal to the film. The measured unidirectional MR is attributed to the differential anomalous Hall resistance due to the thickness difference at the electrodes for the longitudinal resistance measurements. The unidirectional MR effect in the Co/Pt bilayers can be greatly suppressed by a non-magnetic Cu inserting layer.

Tunable Snell's law for spin waves in heterochiral magnetic films

NASA Astrophysics Data System (ADS)

Mulkers, Jeroen; Van Waeyenberge, Bartel; Milošević, Milorad V.

2018-03-01

Thin ferromagnetic films with an interfacially induced DMI exhibit nontrivial asymmetric dispersion relations that lead to unique and useful magnonic properties. Here we derive an analytical expression for the magnon propagation angle within the micromagnetic framework and show how the dispersion relation can be approximated with a comprehensible geometrical interpretation in the k space of the propagation of spin waves. We further explore the refraction of spin waves at DMI interfaces in heterochiral magnetic films, after deriving a generalized Snell's law tunable by an in-plane magnetic field, that yields analytical expressions for critical incident angles. The found asymmetric Brewster angles at interfaces of regions with different DMI strengths, adjustable by magnetic field, support the conclusion that heterochiral ferromagnetic structures are an ideal platform for versatile spin-wave guides.

Magnetic Field Enhanced Superconductivity in Epitaxial Thin Film WTe2.

PubMed

Asaba, Tomoya; Wang, Yongjie; Li, Gang; Xiang, Ziji; Tinsman, Colin; Chen, Lu; Zhou, Shangnan; Zhao, Songrui; Laleyan, David; Li, Yi; Mi, Zetian; Li, Lu

2018-04-25

In conventional superconductors an external magnetic field generally suppresses superconductivity. This results from a simple thermodynamic competition of the superconducting and magnetic free energies. In this study, we report the unconventional features in the superconducting epitaxial thin film tungsten telluride (WTe 2 ). Measuring the electrical transport properties of Molecular Beam Epitaxy (MBE) grown WTe 2 thin films with a high precision rotation stage, we map the upper critical field H c2 at different temperatures T. We observe the superconducting transition temperature T c is enhanced by in-plane magnetic fields. The upper critical field H c2 is observed to establish an unconventional non-monotonic dependence on temperature. We suggest that this unconventional feature is due to the lifting of inversion symmetry, which leads to the enhancement of H c2 in Ising superconductors.

Distinctive uniaxial magnetic anisotropy and positive magnetoresistance in (110)-oriented Fe3O4 films

NASA Astrophysics Data System (ADS)

Dho, Joonghoe; Kim, Byeong-geon; Ki, Sanghoon

2015-04-01

Magnetite (Fe3O4) films were synthesized on (110)-oriented MgO, MgAl2O4, and SrTiO3 substrates for comparative studies of the substrates' effects on magnetic and magnetoresistance properties of the films. For the [-110] direction, the hysteresis loops of the Fe3O4 film on MgAl2O4 exhibited a good squareness with the largest coercivity of ˜1090 Oe, and the ratio of remanent magnetization to saturation magnetization was ˜0.995. For the [001] direction, positive magnetoresistance in weak magnetic fields was most distinct for the (110) SrTiO3 substrate with the largest lattice mismatch. Positive magnetoresistance in the (110) Fe3O4 films was presumably affected by imperfect atomic arrangements at anti-phase boundaries.

Strain control of giant magnetic anisotropy in metallic perovskite SrCoO3-δ thin films.

PubMed

Hu, Songbai; Cazorla, Claudio; Xiang, Feixiang; Ma, Hongfei; Wang, Jianyuan; Wang, Jianbo; Wang, Xiaolin; Ulrich, Clemens; Chen, Lang; Seidel, Jan

2018-06-08

Magnetic materials with large magnetic anisotropy are essential for workaday applications such as permanent magnets and magnetic data storage. There is widespread interest in finding efficient ways of controlling magnetic anisotropy, among which strain control has proven to be a very powerful technique. Here we demonstrate strain-mediated magnetic anisotropy in SrCoO3-δ thin film, a perovskite oxide that is metallic and adopts a cubic structure at δ ≤ 0.25. We find that the easy-magnetization axis in SrCoO3-δ can be rotated by 90º upon application of moderate epitaxial strains ranging from -1.2% to +1.8%. The magnetic anisotropy in compressive SrCoO3-δ thin films is giant as shown by magnetic hysteresis loops rendering an anisotropy energy density of ~106 erg/cm3. The local variance of magnetic force microscopy (MFM) upon temperature and magnetic field reveals that the evolution of magnetic domains in SCO thin film is strongly dependent on the magnetic anisotropy.

A magnetic model for low/hard state of black hole binaries

NASA Astrophysics Data System (ADS)

Wang, Ding-Xiong

2015-08-01

A magnetic model for low/hard state (LHS) of black hole X-ray binaries (BHXBs), H1743-322 and GX 339-4, is proposed based on the transportation of magnetic field from a companion into an accretion disc around a black hole (BH). This model consists of a truncated thin disc with an inner advection-dominated accretion flow (ADAF). The spectral profiles of the sources are fitted in agreement with the data observed at four different dates corresponding to the rising stage of the LHS. In addition, the association of the LHS with quasi-steady jet is modelled based on the transportation of magnetic field, where the Blandford-Znajek (BZ) and Blandford-Payne (BP) processes are invoked to drive the jets from BH and inner ADAF. It turns out that the steep radio-X-ray correlations observed in H1743-322 and GX 339-4 can be interpreted based on our model. It is suggested that large-scale magnetic field can be regarded as the second parameter for governing the state transitions in some BHXBs.

Novel hard, tough HfAlSiN multilayers, defined by alternating Si bond structure, deposited using modulated high-flux, low-energy ion irradiation of the growing film

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fager, Hanna, E-mail: hanfa@ifm.liu.se; Greczynski, Grzegorz; Jensen, Jens

Hf{sub 1−x−y}Al{sub x}Si{sub y}N (0 ≤ x ≤ 0.14, 0 ≤ y ≤ 0.12) single layer and multilayer films are grown on Si(001) at 250 °C using ultrahigh vacuum magnetically unbalanced reactive magnetron sputtering from a single Hf{sub 0.6}Al{sub 0.2}Si{sub 0.2} target in mixed 5%-N{sub 2}/Ar atmospheres at a total pressure of 20 mTorr (2.67 Pa). The composition and nanostructure of Hf{sub 1−x−y}Al{sub x}Si{sub y}N films are controlled by varying the energy E{sub i} of the ions incident at the film growth surface while maintaining the ion-to-metal flux ratio constant at eight. Switching E{sub i} between 10 and 40 eV allows the growthmore » of Hf{sub 0.78}Al{sub 0.10}Si{sub 0.12}N/Hf{sub 0.78}Al{sub 0.14}Si{sub 0.08}N multilayers with similar layer compositions, but in which the Si bonding state changes from predominantly Si–Si/Si–Hf for films grown with E{sub i} = 10 eV, to primarily Si–N with E{sub i} = 40 eV. Multilayer hardness values, which vary inversely with bilayer period Λ, range from 20 GPa with Λ = 20 nm to 27 GPa with Λ = 2 nm, while fracture toughness increases directly with Λ. Multilayers with Λ = 10 nm combine relatively high hardness, H ∼ 24 GPa, with good fracture toughness.« less

Electric-field control of magnetic properties for α-Fe2O3/Al2O3 films

NASA Astrophysics Data System (ADS)

Cheng, Bin; Qin, Hongwei; Liu, Liang; Xie, Jihao; Zhou, Guangjun; Chen, Lubin; Hu, Jifan

2018-06-01

α-Fe2O3/Al2O3 films can exhibit weak ferromagnetism at room temperature. The saturation magnetization of the thinner film is larger than that of the thick one deposited at the same temperature of 500 °C, which implies that the weak ferromagnetism at room temperature comes not only from the intrinsic canted magnetic structure, but also from the effects of interface between α-Fe2O3/Al2O3, such as the effect of Al diffusion into α-Fe2O3 film. Perpendicular electric field upon α-Fe2O3/Al2O3 film at room temperature could adjust the magnetic properties (saturation magnetization, magnetic remanence, coercivity and saturation magnetizing field). The positive electric field can enhance the magnetism of α-Fe2O3/Al2O3 thin film, while negative electric field can reduce it. The change induced by electric field may be connected with the migration effects of Al3+ ions. The steps of curve for saturation magnetization versus the electric field may reflect these complicated processes. The magnetization of the film deposited at a higher temperature can be changed by electric field more easily. This study may inspire more in-depth research and lead to an alternative approach to future magneto-electronic devices.

Superconducting Magnet Power Supply and Hard-Wired Quench Protection at Jefferson Lab for 12 GeV Upgrade

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ghoshal, Probir K.; Bachimanchi, Ramakrishna; Fair, Ruben J.

The superconducting magnet system in Hall B being designed and built as part of the Jefferson Lab 12 GeV upgrade requires powering two conduction cooled superconducting magnets - a torus and a solenoid. The torus magnet is designed to operate at 3770 A and solenoid at 2416 A. Failure Modes and Effects Analysis (FMEA) determined that voltage level thresholds and dump switch operation for magnet protection should be tested and analyzed before incorporation into the system. The designs of the quench protection and voltage tap sub-systems were driven by the requirement to use a primary hard-wired quench detection sub-system togethermore » with a secondary PLC-based protection. Parallel path voltage taps feed both the primary and secondary quench protection sub-systems. The PLC based secondary protection is deployed as a backup for the hard-wired quench detection sub-system and also acts directly on the dump switch. Here, we describe a series of tests and modifications carried out on the magnet power supply and quench protection system to ensure that the superconducting magnet is protected for all fault scenarios.« less

Superconducting Magnet Power Supply and Hard-Wired Quench Protection at Jefferson Lab for 12 GeV Upgrade

DOE PAGES

Ghoshal, Probir K.; Bachimanchi, Ramakrishna; Fair, Ruben J.; ...

2017-10-05

The superconducting magnet system in Hall B being designed and built as part of the Jefferson Lab 12 GeV upgrade requires powering two conduction cooled superconducting magnets - a torus and a solenoid. The torus magnet is designed to operate at 3770 A and solenoid at 2416 A. Failure Modes and Effects Analysis (FMEA) determined that voltage level thresholds and dump switch operation for magnet protection should be tested and analyzed before incorporation into the system. The designs of the quench protection and voltage tap sub-systems were driven by the requirement to use a primary hard-wired quench detection sub-system togethermore » with a secondary PLC-based protection. Parallel path voltage taps feed both the primary and secondary quench protection sub-systems. The PLC based secondary protection is deployed as a backup for the hard-wired quench detection sub-system and also acts directly on the dump switch. Here, we describe a series of tests and modifications carried out on the magnet power supply and quench protection system to ensure that the superconducting magnet is protected for all fault scenarios.« less

The relationship between the microstructure and magnetic properties of sputtered Co/Pt multilayer films

NASA Astrophysics Data System (ADS)

Kim, Y. H.; Petford-Long, Amanda K.; Jakubovics, J. P.

1994-11-01

Co/Pd multilayer films (MLFs) are of interest because of their potential application as high-density magneto-optical recording media. Co/Pd MLFs with varying Co and Pd layer thicknesses were grown by sputter-deposition onto (100) Si wafers. X-ray diffraction and high resolution electron microscopy were used to study the microstructure of the films, and Lorentz microscopy was used to analyze their magnetic domain structure. The films show an fcc crystal structure with a compromised lattice parameter and a strong (111) crystallographic texture in the growth direction. The compromised interplanar spacing parallel to the surface increased with decreasing thickness ratio (t(sub Co)/t(sub Pd), and the columnar grain size decreased with increasing Pd layer thickness. Films with t(sub Co) = 0.35 nm and t(sub Pd) = 2.8 nm (columnar grain diameter 20 nm) showed promising magnetic properties, namely a high perpendicular magnetic anisotropy (1.85x10(exp 5) J/cu m), with a perpendicular coercivity of 98.7 kA/m, a perpendicular remanence ratio of 99%, and a perpendicular coercivity ratio of 88%. The magnetic domains were uniform and of a narrow stripe type, confirming the perpendicular easy axis of magnetization. The Curie temperature was found to be about 430 C. Films of pure Co and Pd, grown for comparison, also showed columnar grain structure with grain-sizes of the same order as those seen in the MLFs. In addition the Pd films showed a (111) textured fcc structure.

Patterning of magnetic thin films and multilayers using nanostructured tantalum gettering templates.

PubMed

Qiu, Wenlan; Chang, Long; Lee, Dahye; Dannangoda, Chamath; Martirosyan, Karen; Litvinov, Dmitri

2015-03-25

This work demonstrates that a nonmagnetic thin film of cobalt oxide (CoO) sandwiched between Ta seed and capping layers can be effectively reduced to a magnetic cobalt thin film by annealing at 200 °C, whereas CoO does not exhibit ferromagnetic properties at room temperature and is stable at up to ∼400 °C. The CoO reduction is attributed to the thermodynamically driven gettering of oxygen by tantalum, similar to the exothermic reduction-oxidation reaction observed in thermite systems. Similarly, annealing at 200 °C of a nonmagnetic [CoO/Pd]N multilayer thin film sandwiched between Ta seed and Ta capping layers results in the conversion into a magnetic [Co/Pd]N multilayer, a material with perpendicular magnetic anisotropy that is of interest for magnetic data storage applications. A nanopatterning approach is introduced where [CoO/Pd]N multilayers is locally reduced into [Co/Pd]N multilayers to achieve perpendicular magnetic anisotropy nanostructured array. This technique can potentially be adapted to nanoscale patterning of other systems for which thermodynamically favorable combination of oxide and gettering layers can be identified.

Methods for Probing Magnetic Films with Neutrons

NASA Astrophysics Data System (ADS)

Kozhevnikov, S. V.; Ott, F.; Radu, F.

2018-03-01

We review various methods in the investigation of magnetic films with neutrons, including those based on the effects of Larmor precession, Zeeman spatial splitting of the beam, neutron spin resonance, and polarized neutron channeling. The underlying principles, examples of the investigated systems, specific features, applications, and perspectives of these methods are discussed.

Optical and magnetic properties of porous anodic alumina/Ni nanocomposite films

NASA Astrophysics Data System (ADS)

Zhang, Jing-Jing; Li, Zi-Yue; Zhang, Zhi-Jun; Wu, Tian-Shan; Sun, Hui-Yuan

2013-06-01

A simple method to tune the optical properties of porous anodic alumina (PAA) films embedded with Ni is reported. The films display highly saturated colors after being synthesized by an ac electrodeposition method. The optical properties of the samples can be effectively tuned by varying the oxidation time of aluminum. The ultrashort Ni nanowires (100 nm long and 50 nm in diameter) present only fcc phase and show no apparent averaged effective magnetic anisotropy. The coercivity mechanism of the Ni nanowires in our case is consistent with fanning mechanism based on a chain-of-spheres model. PAA/Ni films with structural color and magnetic properties have friability-resistant feature and can be used in many areas, including decoration, display, and multifunctional anti-counterfeiting technology.

Methods for making radially anisotropic thin-film magnetic torroidal cores

DOE Office of Scientific and Technical Information (OSTI.GOV)

Qiu, Jizheng; Sullivan, Charles R.

2017-05-23

A method of forming a radially anisotropic toroidal magnetic core includes providing apparatus having a first magnet for providing a radial magnetic field extending across a cavity from an axial spindle to a surrounding second magnetic element, placing a substrate in the cavity, the substrate having a hole fitting around the head of the spindle; and sputter-depositing a film of ferromagnetic material onto the substrate. In an embodiment, the spindle is magnetically coupled to a first pole of the first magnet, the second magnetic element is coupled to a second pole of the first magnet, and a thermally conductive, nonmagnetic,more » insert separates the spindle and the second magnetic element.« less

Growth and magnetic properties of multiferroic LaxBi1-xMnO3 thin films

NASA Astrophysics Data System (ADS)

Gajek, M.; Bibes, M.; Wyczisk, F.; Varela, M.; Fontcuberta, J.; Barthélémy, A.

2007-05-01

A comparative study of LaxBi1-xMnO3 thin films grown on SrTiO3 substrates is reported. It is shown that these films grow epitaxially in a narrow pressure-temperature range. A detailed structural and compositional characterization of the films is performed within the growth window. The structure and the magnetization of this system are investigated. We find a clear correlation between the magnetization and the unit-cell volume that we ascribe to Bi deficiency and the resultant introduction of a mixed valence on the Mn ions. On these grounds, we show that the reduced magnetization of LaxBi1-xMnO3 thin films compared to the bulk can be explained quantitatively by a simple model, taking into account the deviation from nominal composition and the Goodenough-Kanamori-Anderson rules of magnetic interactions.

Magnetic field induced switching of the antiferromagnetic order parameter in thin films of magnetoelectric chromia

NASA Astrophysics Data System (ADS)

Fallarino, Lorenzo; Berger, Andreas; Binek, Christian

2015-02-01

A Landau-theoretical approach is utilized to model the magnetic field induced reversal of the antiferromagnetic order parameter in thin films of magnetoelectric antiferromagnets. A key ingredient of this peculiar switching phenomenon is the presence of a robust spin polarized state at the surface of the antiferromagnetic films. Surface or boundary magnetization is symmetry allowed in magnetoelectric antiferromagnets and experimentally established for chromia thin films. It couples rigidly to the antiferromagnetic order parameter and its Zeeman energy creates a pathway to switch the antiferromagnet via magnetic field application. In the framework of a minimalist Landau free energy expansion, the temperature dependence of the switching field and the field dependence of the transition width are derived. Least-squares fits to magnetometry data of (0001 ) textured chromia thin films strongly support this model of the magnetic reversal mechanism.

A magnetic model for low/hard state of black hole binaries

NASA Astrophysics Data System (ADS)

Ye, Yong-Chun; Wang, Ding-Xiong; Huang, Chang-Yin; Cao, Xiao-Feng

2016-03-01

A magnetic model for the low/hard state (LHS) of two black hole X-ray binaries (BHXBs), H1743-322 and GX 339-4, is proposed based on transport of the magnetic field from a companion into an accretion disk around a black hole (BH). This model consists of a truncated thin disk with an inner advection-dominated accretion flow (ADAF). The spectral profiles of the sources are fitted in agreement with the data observed at four different dates corresponding to the rising phase of the LHS. In addition, the association of the LHS with a quasi-steady jet is modeled based on transport of magnetic field, where the Blandford-Znajek (BZ) and Blandford-Payne (BP) processes are invoked to drive the jets from BH and inner ADAF. It turns out that the steep radio/X-ray correlations observed in H1743-322 and GX 339-4 can be interpreted based on our model.

Structural and magnetic fluence dependence in cobalt titanate thin films synthesized by pulse laser deposition

NASA Astrophysics Data System (ADS)

Prisbrey, Shon Thomas

Knowledge of the fundamental structure and magnetic characteristics of dilute magnetic semiconductors (DMSs) is an essential step towards the development of spin-polarized electronics (spintronics). Recently (2001), the report of ferromagnetism in cobalt-doped anatase titania films synthesized by pulse laser deposition (PLD) elicited interest as a possible DMS oxide. Other investigations of the CoxTi1-xO2-delta material system, utilizing a myriad of deposition techniques, yielded conflicting results as to the source of magnetism and the local environment of the deposited cobalt. No complete characterization of PLD synthesized films has been reported. This dissertation quantifies the effect of laser fluence on film morphology, structure, and magnetic properties by fully characterizing CoxTi1-x O2-delta films grown under optimal PLD deposition conditions that were identified separately in prior published work. The construction of a custom PLD system that provided repeatable laser/target interaction via a combination of fluence and target movement is addressed. A brief outline of magnetism and its relation to structure is also given. The remainder of the dissertation details the effect of laser fluence on Co0.049Ti0.951O2-delta and Co 0.038Ti0.962O2-delta films. Film structure, morphology, and magnetic properties were determined for illumination conditions corresponding to laser fluences varying from 0.57 to 1.37 J/cm2. The local cobalt environment is strongly correlated with laser fluence. Cobalt in 4.9% concentration films grown with a laser fluence between 0.7 and 0.93 J/cm2 were octahedrally coordinated, as were 3.8% films grown with a fluence less than 0.93 J/cm2. Departure of the laser fluence from these ranges results in a multitude of cobalt environments in the films. The film magnetization is observed to be a function of laser fluence with a maximum moment of ˜3.19 muB per cobalt atom occurring at 0.93 J/cm2 in the 4.9% films and ˜1.9 muB per cobalt atom at

Structure and magnetism of Fe-doped BaSnO 3 thin films

DOE PAGES

Alaan, Urusa S.; N’Diaye, Alpha T.; Shafer, Padraic; ...

2017-02-28

BaSnO 3 is an excellent candidate system for developing a new class of perovskite-based dilute magnetic semiconductors. Here in this study, we show that BaSn 0.95Fe 0.05O 3 can be grown from a background pressure of ~2×10-3 mTorr to oxygen pressures of 300 mTorr with high crystallinity and excellent structural quality. When grown in vacuum, the films may be weakly ferromagnetic with a nonzero x-ray magnetic circular dichroism signal on the Fe L 3 edge. Growth with oxygen flow appears to suppress magnetic ordering. Even for very thick films grown in 100 mTorr O 2, the films are paramagnetic. Finally,more » the existence of ferromagnetism in vacuum-grown BaSnO 3 may be attributed to the F-center exchange mechanism, which relies on the presence of oxygen vacancies to facilitate the ferromagnetism. However, other possible extrinsic contributions to the magnetic ordering, such as clusters of Fe 3O 4 and FeO or contamination can also explain the observed behavior.« less

Magnetic and exchange bias properties of YCo thin films and IrMn/YCo bilayers

NASA Astrophysics Data System (ADS)

Venkat Narayana, M.; Manivel Raja, M.; Jammalamadaka, S. Narayana

2018-02-01

We report on the structural and magnetic properties of YCo thin films and IrMn/YCo bilayers. X-ray diffraction infer that all the films are amorphous in nature. Magnetization versus magnetic field measurements reveal room temperature soft ferromagnetism in all the YCo films. Thin films which were grown at 100 W sputter power with growth rates of 0.677, 0.694 and 0.711 Å/sec show better morphology and composition than 50 W (0.333, 0.444 and 0.277 Å/sec) grown films. Perpendicular exchange bias in as deposited bilayers is evident for IrMn/YCo bilayers. Exchange bias (EB) decreases in case of in plane measurements and enhances for out of plane measurements after perpendicular field annealing. EB is more in case of out of plane direction due to large perpendicular anisotropy in comparison with in plane direction. Above the critical thickness, EB variation is explained on the basis of random field model in the Heisenberg regime, which has been proposed by Malozemoff. Indeed there exists an inverse relationship between EB and IrMn layer thickness. Evidenced vertical shift apart from the horizontal shift for magnetization loops is attributed to frozen magnetic moments in one of the layers at the interface. Present results would prove to be helpful in spintronic device applications.

Enhancement of Magnetization in Y3Fe5O12 Epitaxial Thin Films

NASA Astrophysics Data System (ADS)

Brangham, Jack T.; Gallagher, James C.; Yang, Angela S.; White, Shane P.; Adur, Rohan; Ruane, Willam T.; Esser, Bryan D.; Page, Michael R.; Hammel, P. Chris; McComb, David W.; Yang, Fengyuan

The ability to generate pure spin currents has applications in telecommunications, radar, and spin-based logic. Y3Fe5O12 (YIG) is one of the best materials for dynamic generation of spin currents due to its low damping, narrow ferromagnetic resonance (FMR) linewidth, and insulating behavior. We grow stoichiometric, high quality, epitaxial YIG thin films with thicknesses ranging from 4 to 250 nm on Gd3Ga5O12 by off-axis magnetron sputtering and characterize the YIG films by various techniques. The temperature dependence of the saturation magnetization was independently measured by in-plane vibrating sample magnetometry, out-of-plane magnetic shape anisotropy, and angular-dependent FMR absorption from 10 K to the Curie temperature of 530 K. The room temperature saturation magnetization was also measured with frequency dependent FMR. All measurements show a magnetization enhancement of 15% or greater when compared to reported magnetization values of bulk YIG crystals. We speculate this is due to suppression of the long wavelength magnons due to the finite size of the films.

Optimization of L1{sub 0} FePt/Fe{sub 45}Co{sub 55} thin films for rare earth free permanent magnet applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Giannopoulos, G., E-mail: g.giannopoulos@inn.demokritos.gr; Psycharis, V.; Niarchos, D.

The magnetic properties of magnetron sputtered bilayers consisting of Fe{sub 45}Co{sub 55} ultrathin layers on top of L1{sub 0} FePt films epitaxially grown on MgO substrates are studied in view of their possible application as rare earth free permanent magnets. It is found that FePt layers induce a tetragonal distortion to the Fe-Co layers which leads to increased anisotropy. This allows to take advantage of the Fe-Co high magnetic moment with less significant loss of the coercivity compared to a typical hard/soft exchange spring system. A maximum energy product approaching 50 MGOe is obtained for a FePt(7 ML)/FeCo/(5 ML) sample.more » The results are in accordance with first-principles computational methods, which predict that even higher energy products are possible for micromagnetically optimized microstructures.« less

Direct-current cathodic vacuum arc system with magnetic-field mechanism for plasma stabilization.

PubMed

Zhang, H-S; Komvopoulos, K

2008-07-01

Filtered cathodic vacuum arc (FCVA) deposition is characterized by plasma beam directionality, plasma energy adjustment via substrate biasing, macroparticle filtering, and independent substrate temperature control. Between the two modes of FCVA deposition, namely, direct current (dc) and pulsed arc, the dc mode yields higher deposition rates than the pulsed mode. However, maintaining the dc arc discharge is challenging because of its inherent plasma instabilities. A system generating a special configuration of magnetic field that stabilizes the dc arc discharge during film deposition is presented. This magnetic field is also part of the out-of-plane magnetic filter used to focus the plasma beam and prevent macroparticle film contamination. The efficiency of the plasma-stabilizing magnetic-field mechanism is demonstrated by the deposition of amorphous carbon (a-C) films exhibiting significantly high hardness and tetrahedral carbon hybridization (sp3) contents higher than 70%. Such high-quality films cannot be produced by dc arc deposition without the plasma-stabilizing mechanism presented in this study.

Magnetic anisotropy and transport properties of 70 nm SrRuO3 films grown on different substrates

NASA Astrophysics Data System (ADS)

Wang, X. W.; Zhang, Y. Q.; Meng, H.; Wang, Z. J.; Li, D.; Zhang, Z. D.

2011-04-01

Magnetic and transport properties of 70 nm SrRuO3 films grown on (001) SrTiO3, (001) LaAlO3 and (001) MgO have been investigated. A perpendicular magnetic anisotropy is observed in compressive strained films grown on SrTiO3. A weaker perpendicular magnetic anisotropy and a weak in-plane magnetic anisotropy are found in strain-free films grown on MgO and LAO, respectively, possibly due to different growth mechanisms. In addition, metallic behavior is observed in all the as-grown films and the resistivity of the film grown on MgO is lowest (230 μΩ cm at 300 K), which is close to that of bulk single crystal SrRuO3 (about 195 μΩ cm). The relation between structure and properties indicates that the magnetic anisotropy, as well as the magnitude of resistivity of SrRuO3 films, can be effectively tailored by taking advantage of different strains and growth mechanisms induced by growth on different substrates.

High efficiency microcolumnar Lu2O3:Eu scintillator thin film for hard X-ray microtomography

NASA Astrophysics Data System (ADS)

Marton, Z.; Bhandari, H. B.; Brecher, C.; Miller, S. R.; Singh, B.; Nagarkar, V. V.

2013-03-01

We have developed microstructured Lu2O3:Eu scintillator films capable of providing spatial resolution on the order of micrometers for hard X-ray imaging. In addition to their extraordinary resolution, Lu2O3:Eu films simultaneously provide high absorption efficiency for 20 to 100 keV X-rays, and bright 610 nm emission, with intensity rivalling that of the brightest known scintillators. At present, high spatial resolution of such a magnitude is achieved using ultra-thin scintillators measuring only about 1 to 5 μm in thickness, which limits absorption efficiency to ~3% for 12 keV X-rays and less than 0.1% for 20 to 100 keV X-rays, resulting in excessive measurement time and exposure to the specimen. Lu2O3:Eu would significantly improve that (99.9% @12 keV and 30% @ 70 keV). Important properties and features of our Lu2O3:Eu scintillator material, fabricated by our electron-beam physical vapour deposition (EB-PVD) process, combines superior density of 9.5 g/cm3, microcolumnar structure emitting 48000 photons/MeV whose wavelength is an ideal match for the underlying CCD detector array. We grew thin films measuring 5-50μm in thickness as well as covering areas up to 5 × 5 cm2 which can be a suitable basis for microtomography, digital radiography as well as CT and hard X-ray Micro-Tomography (XMT).

CoPt/TiN films nanopatterned by RF plasma etching towards dot-patterned magnetic media

NASA Astrophysics Data System (ADS)

Szívós, János; Pothorszky, Szilárd; Soltys, Jan; Serényi, Miklós; An, Hongyu; Gao, Tenghua; Deák, András; Shi, Ji; Sáfrán, György

2018-03-01

CoPt thin films as possible candidates for Bit Patterned magnetic Media (BPM) were prepared and investigated by electron microscopy techniques and magnetic measurements. The structure and morphology of the Direct Current (DC) sputtered films with N incorporation were revealed in both as-prepared and annealed state. Nanopatterning of the samples was carried out by means of Radio Frequency (RF) plasma etching through a Langmuir-Blodgett film of silica nanospheres that is a fast and high throughput technique. As a result, the samples with hexagonally arranged 100 nm size separated dots of fct-phase CoPt were obtained. The influence of the order of nanopatterning and anneling on the nanostructure formation was revealed. The magnetic properties of the nanopatterned fct CoPt films were investigated by Vibrating Sample Magnetometer (VSM) and Magnetic Force Microscopy (MFM). The results show that CoPt thin film nanopatterned by means of the RF plasma etching technique is promising candidate to a possible realization of BPM. Furthermore, this technique is versatile and suitable for scaling up to technological and industrial applications.

Pancreatic hardness: Correlation of surgeon's palpation, durometer measurement and preoperative magnetic resonance imaging features.

PubMed

Hong, Tae Ho; Choi, Joon-Il; Park, Michael Yong; Rha, Sung Eun; Lee, Young Joon; You, Young Kyoung; Choi, Moon Hyung

2017-03-21

To evaluate the correlation between subjective assessments of pancreatic hardness based on the palpation, objective measurements using a durometer, and magnetic resonance imaging (MRI) findings for assessing pancreatic hardness. Eighty-three patients undergoing pancreatectomies were enrolled. An experienced surgeon subjectively evaluated the pancreatic hardness in the surgical field by palpation. The pancreatic hardness was also objectively evaluated using a durometer. Preoperative MRI findings were evaluated by a radiologist in terms of the apparent diffusion coefficient (ADC) values, the relative signal intensity decrease (RSID) of the pancreatic parenchyma, and the diameter of the pancreatic parenchyma and duct. Durometer measurement results, ADC values, RSID, pancreatic duct and parenchyma diameters, and the ratio of the diameters of the duct and parenchyma were compared between pancreases judged to be soft or hard pancreas on the palpation. A correlation analysis was also performed between the durometer and MRI measurements. The palpation assessment classified 44 patients as having a soft pancreas and 39 patients as having a hard pancreas. ADC values were significantly lower in the hard pancreas group. The ductal diameter and duct-to-pancreas ratio were significantly higher in the hard pancreas group. For durometer measurements, a correlation analysis showed a positive correlation with the ductal diameter and the duct-to-pancreas ratio and a negative correlation with ADC values. Hard pancreases showed lower ADC values, a wider pancreatic duct diameter and a higher duct-to-pancreas ratio than soft pancreases. Additionally, the ADC values, diameter of the pancreatic duct and duct-to-pancreas ratio were closely correlated with the durometer results.

Hard-Core Unemployment: A Selected, Annotated Bibliography.

ERIC Educational Resources Information Center

Cameron, Colin, Comp.; Menon, Anila Bhatt, Comp.

This annotated bibliography contains references to various films, articles, and books on the subject of hard-core unemployment, and is divided into the following sections: (1) The Sociology of the Hard-Core Milieu, (2) Training Programs, (3) Business and the Hard-Core, (4) Citations of Miscellaneous References on Hard-Core Unemployment, (5)…

Stress-induced surface magnetization of (La{sub 0.7}Sr{sub 0.3})MnO{sub 3} thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kwon, C.; Lofland, S.E.; Bhagat, S.M.

1997-09-01

The role of stress on magnetic properties of epitaxial (La{sub 0.7}Sr{sub 0.3}) MnO{sub 3} (LSMO) films has been studied. The authors have investigated 1,100 {angstrom} thick LSMO films deposited on LaAlO{sub 3} (Sample L, under a compressive stress) and SrTiO{sub 3} (Sample S, under a tensile stress) using the magnetic force microscopy (MFM), DC hysteresis loop, ferromagnetic resonance (FMR) measurements. The magnetic force microscope image of Sample L shows a maze-like pattern indicating a sizable out-of-plane magnetization, while the magnetic image of Sample S shows a feather-like pattern indicative of an in-plane magnetization. The hysteresis loop and ferromagnetic resonance measurementsmore » give quantitative evidence for the role of the lattice mismatch between the film and the substrate in the magnetic anisotropy of the two films. The systematic examination of various thickness LSMO films on LaAlO{sub 3} reveals that the maze pattern is exhibited only between 500 {angstrom} and 1,700 {angstrom} thick films. Despite of larger anisotropy, no maze pattern is observed in films thinner than 360 {angstrom}.« less

Atomic layer deposition of titanium oxide films on As-synthesized magnetic Ni particles: Magnetic and safety properties

NASA Astrophysics Data System (ADS)

Uudeküll, Peep; Kozlova, Jekaterina; Mändar, Hugo; Link, Joosep; Sihtmäe, Mariliis; Käosaar, Sandra; Blinova, Irina; Kasemets, Kaja; Kahru, Anne; Stern, Raivo; Tätte, Tanel; Kukli, Kaupo; Tamm, Aile

2017-05-01

Spherical nickel particles with size in the range of 100-400 nm were synthesized by non-aqueous liquid phase benzyl alcohol method. Being developed for magnetically guided biomedical applications, the particles were coated by conformal and antimicrobial thin titanium oxide films by atomic layer deposition. The particles retained their size and crystal structure after the deposition of oxide films. The sensitivity of the coated particles to external magnetic fields was increased compared to that of the uncoated powder. Preliminary toxicological investigations on microbial cells and small aquatic crustaceans revealed non-toxic nature of the synthesized particles.

Thermal annealing and transient electronic excitations induced interfacial and magnetic effects on Pt/Co/Pt trilayer

NASA Astrophysics Data System (ADS)

Sehdev, Neeru; Medwal, Rohit; Malik, Rakesh; Kandasami, Asokan; Kanjilal, Dinakar; Annapoorni, S.

2018-04-01

Present study investigates the importance of thermal annealing and transient electronic excitations (using 100 MeV oxygen ions) in assisting the interfacial atomic diffusion, alloy composition, and magnetic switching field distributions in Pt/Co/Pt stacked trilayer. X-ray diffraction analysis reveals that thermal annealing results in the formation of the face centered tetragonal L1°CoPt phase. The Rutherford back scattering spectra shows a trilayer structure for as-deposited and as-irradiated films. Interlayer mixing on the thermally annealed films further improves by electronic excitations produced by high energy ion irradiation. Magnetically hard face centered tetragonal CoPt alloy retains its hard phase after ion irradiation and reveals an enhancement in the structural ordering and magnetic stability. Enhancement in the homogeneity of alloy composition and its correlation with the magnetic switching field is evident from this study. A detailed investigation of the contributing parameters shows that the magnetic switching behaviour varies with the type of thermal annealing, transient electronic excitations of ion beams and combination of these processes.

Reversible strain effect on the magnetization of LaCoO3 films

NASA Astrophysics Data System (ADS)

Herklotz, A.; Rata, A. D.; Schultz, L.; Dörr, K.

2009-03-01

The magnetization (M) of a LaCoO3 film grown epitaxially on a piezoelectric substrate has been investigated in dependence on the biaxial in-plane strain. M decreases with the reversible release of tensile strain, with a maximum change of at least 6% per 0.1% of biaxial strain near the Curie temperature (TC) . The biaxial strain response of TC is estimated to be below 5 K/% in the tensile strain state. This is in agreement with results from statically strained films on various substrates. As possible origins of the strain-induced magnetization are considered (i) the strain-dependent Curie temperature, (ii) a strain-dependent magnetically inhomogeneous (phase-separated) state, and (iii) a strain-dependent magnetic moment (spin state) of Co ions. The TC shift is found insufficient to explain the measured strain-induced magnetization change but contributions from mechanism (ii) or (iii) must be involved.

Oxygen-enabled control of Dzyaloshinskii-Moriya Interaction in ultra-thin magnetic films.

PubMed

Belabbes, Abderrezak; Bihlmayer, Gustav; Blügel, Stefan; Manchon, Aurélien

2016-04-22

The search for chiral magnetic textures in systems lacking spatial inversion symmetry has attracted a massive amount of interest in the recent years with the real space observation of novel exotic magnetic phases such as skyrmions lattices, but also domain walls and spin spirals with a defined chirality. The electrical control of these textures offers thrilling perspectives in terms of fast and robust ultrahigh density data manipulation. A powerful ingredient commonly used to stabilize chiral magnetic states is the so-called Dzyaloshinskii-Moriya interaction (DMI) arising from spin-orbit coupling in inversion asymmetric magnets. Such a large antisymmetric exchange has been obtained at interfaces between heavy metals and transition metal ferromagnets, resulting in spin spirals and nanoskyrmion lattices. Here, using relativistic first-principles calculations, we demonstrate that the magnitude and sign of DMI can be entirely controlled by tuning the oxygen coverage of the magnetic film, therefore enabling the smart design of chiral magnetism in ultra-thin films. We anticipate that these results extend to other electronegative ions and suggest the possibility of electrical tuning of exotic magnetic phases.

Oxygen-enabled control of Dzyaloshinskii-Moriya Interaction in ultra-thin magnetic films

PubMed Central

Belabbes, Abderrezak; Bihlmayer, Gustav; Blügel, Stefan; Manchon, Aurélien

2016-01-01

The search for chiral magnetic textures in systems lacking spatial inversion symmetry has attracted a massive amount of interest in the recent years with the real space observation of novel exotic magnetic phases such as skyrmions lattices, but also domain walls and spin spirals with a defined chirality. The electrical control of these textures offers thrilling perspectives in terms of fast and robust ultrahigh density data manipulation. A powerful ingredient commonly used to stabilize chiral magnetic states is the so-called Dzyaloshinskii-Moriya interaction (DMI) arising from spin-orbit coupling in inversion asymmetric magnets. Such a large antisymmetric exchange has been obtained at interfaces between heavy metals and transition metal ferromagnets, resulting in spin spirals and nanoskyrmion lattices. Here, using relativistic first-principles calculations, we demonstrate that the magnitude and sign of DMI can be entirely controlled by tuning the oxygen coverage of the magnetic film, therefore enabling the smart design of chiral magnetism in ultra-thin films. We anticipate that these results extend to other electronegative ions and suggest the possibility of electrical tuning of exotic magnetic phases. PMID:27103448

Molecular dynamic heterogeneity of confined lipid films by 1H magnetization-exchange nuclear magnetic resonance

NASA Astrophysics Data System (ADS)

Buda, A.; Demco, D. E.; Jagadeesh, B.; Blümich, B.

2005-01-01

The molecular dynamic heterogeneity of monolayer to submonolayer thin lecithin films confined to submicron cylindrical pores were investigated by 1H magnetization exchange nuclear magnetic resonance. In this experiment a z-magnetization gradient was generated by a double-quantum dipolar filter. The magnetization-exchange decay and buildup curves were interpreted with the help of a theoretical model based on the approximation of a one-dimensional spin-diffusion process in a three-domain morphology. The dynamic heterogeneity of the fatty acid chains and the effects of the surface area per molecule, the diameter of the pores, and the temperature were characterized with the help of local spin-diffusion coefficients. The effect of various parameters on the molecular dynamics of the mobile region of the fatty acid chains was quantified by introducing an ad hoc Gaussian distribution function of the 1H residual dipolar couplings. For the lipid films investigated in this study, the surface induced order and the geometrical confinement affect the chain dynamics of the entire molecule. Therefore, each part of the chain independently reflects the effect of surface coverage, pore size, and temperature.

Structural, XPS and magnetic studies of pulsed laser deposited Fe doped Eu{sub 2}O{sub 3} thin film

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kumar, Sandeep; Prakash, Ram, E-mail: rpgiuc@gmail.com; Choudhary, R.J.

2015-10-15

Highlights: • Growth of Fe doped Eu{sub 2}O{sub 3} thin films by PLD. • XRD and Raman’s spectroscopy used for structure confirmation. • The electronic states of Eu and Fe are confirmed by XPS. • Magnetic properties reveals room temperature magnetic ordering in deposited film. - Abstract: Fe (4 at.%) doped europium (III) oxide thin film was deposited on silicon (1 0 0) substrate by pulsed laser deposition technique. Structural, spectral and magnetic properties were studied by X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS) and magnetization measurements. XRD and Raman spectroscopy reveal that the grown film is singlemore » phased and belongs to the cubic structure of Eu{sub 2}O{sub 3}. XPS study of the Eu{sub 1.92}Fe{sub 0.08}O{sub 3} film shows that Fe exists in Fe{sup 3+} ionic state in the film. The film exhibits magnetic ordering at room temperature.« less

Application of Coaxial Ion Gun for Film Generation and Ion Implantation

NASA Astrophysics Data System (ADS)

Takatsu, Mikio; Asai, Tomohiko; Kurumi, Satoshi; Suzuki, Kaoru; Hirose, Hideharu; Masutani, Shigeyuki

A magnetized coaxial plasma gun (MCPG) is here utilized for deposition on high-melting-point metals. MCPGs have hitherto been studied mostly in the context of nuclear fusion research, for particle and magnetic helicity injection and spheromak formation. During spheromak formation, the electrode materials are ionized and mixed into the plasmoid. In this study, this ablation process by gun-current sputtering is enhanced for metallic thin-film generation. In the proposed system geometry, only ionized materials are electromagnetically accelerated by the self-Lorentz force, with ionized operating gas as a magnetized thermal plasmoid, contributing to the thin-film deposition. This reduces the impurity and non-uniformity of the deposited thin-film. Furthermore, as the ions are accelerated in a parallel direction to the injection axis, vertical implantation of the ions into the substrate surface is achieved. To test a potential application of the developed system, experiments were conducted involving the formation of a buffer layer on hard ceramics, for use in dental materials.

Symposium Q: Magnetic Thin Films, Heterostructures, and Device Materials

DTIC Science & Technology

2007-05-22

results in the formation of sodium carboxylate groups, that electronics, also known as magnetoelectronics or spintronics. Mn promoted the adsorption of...Q8.29 Magnetic Properties of Microcrystalline Si Thin films and Nickel Silicide Nanowires. Joondong Kim’, Seongjin Jang 2 , Bi-Ching Shih 2 , Hao...Buffalo, New York. The silicides , such as NiSi 2 and CoSi2 , have been attractive materials to crystallize Si and grow an epitaxial Si film with a small

Giant perpendicular magnetic anisotropy in Fe/III-V nitride thin films

PubMed Central

2018-01-01

Large perpendicular magnetic anisotropy (PMA) in transition metal thin films provides a pathway for enabling the intriguing physics of nanomagnetism and developing broad spintronics applications. After decades of searches for promising materials, the energy scale of PMA of transition metal thin films, unfortunately, remains only about 1 meV. This limitation has become a major bottleneck in the development of ultradense storage and memory devices. We discovered unprecedented PMA in Fe thin-film growth on the (0001¯) N-terminated surface of III-V nitrides from first-principles calculations. PMA ranges from 24.1 meV/u.c. in Fe/BN to 53.7 meV/u.c. in Fe/InN. Symmetry-protected degeneracy between x2 − y2 and xy orbitals and its lift by the spin-orbit coupling play a dominant role. As a consequence, PMA in Fe/III-V nitride thin films is dominated by first-order perturbation of the spin-orbit coupling, instead of second-order in conventional transition metal/oxide thin films. This game-changing scenario would also open a new field of magnetism on transition metal/nitride interfaces. PMID:29670948

Magnetic domain observation of FeCo thin films fabricated by alternate monoatomic layer deposition

NASA Astrophysics Data System (ADS)

Ohtsuki, T.; Kojima, T.; Kotsugi, M.; Ohkochi, T.; Mizuguchi, M.; Takanashi, K.

2014-01-01

FeCo thin films are fabricated by alternate monoatomic layer deposition method on a Cu3Au buffer layer, which in-plane lattice constant is very close to the predicted value to obtain a large magnetic anisotropy constant. The variation of the in-plane lattice constant during the deposition process is investigated by reflection high-energy electron diffraction. The magnetic domain images are also observed by a photoelectron emission microscope in order to microscopically understand the magnetic structure. As a result, element-specific magnetic domain images show that Fe and Co magnetic moments align parallel. A series of images obtained with various azimuth reveal that the FeCo thin films show fourfold in-plane magnetic anisotropy along ⟨110⟩ direction, and that the magnetic domain structure is composed only of 90∘ wall.

Vortex-antivortex lattices in superconducting films with arrays of magnetic dots

NASA Astrophysics Data System (ADS)

Milosevic, M. V.; Peeters, F. M.

2004-03-01

Using the numerical approach within the phenomenological Ginzburg-Landau (GL) theory, we investigate the vortex structure of a thin superconducting film (SC) with a regular matrix of out-of-plane magnetized ferromagnetic dots (FD) deposited on top of it. The perturbation of the superconducting order parameter in the SC film as subject of the inhomogeneous magnetic field of the FDs is studied, and various vortex-antivortex configurations are observed, with net vorticity equal zero. In the case of a periodic array of magnetic disks, vortices are confined under the disks, while the antivortices form a rich spectra of lattice states. In the ground state, antivortices are arranged in the so-called matching configurations between the FDs, while other configurational varieties have higher energy. In the metastable regime, the states with fractional number of vortex-antivortex pairs per unit cell are found, some of which with strongly distorted vortex cores. The exact (anti)vortex structure depends on the size, thickness and magnetization of the magnetic dots, periodicity of the FD-rooster and the properties of the SC expressed through the effective Ginzburg-Landau parameter κ ^* . We discuss the further experimental implications, such as magnetic-field-induced superconductivity.

Imprinting superconducting vortex footsteps in a magnetic layer

PubMed Central

Brisbois, Jérémy; Motta, Maycon; Avila, Jonathan I.; Shaw, Gorky; Devillers, Thibaut; Dempsey, Nora M.; Veerapandian, Savita K. P.; Colson, Pierre; Vanderheyden, Benoît; Vanderbemden, Philippe; Ortiz, Wilson A.; Nguyen, Ngoc Duy; Kramer, Roman B. G.; Silhanek, Alejandro V.

2016-01-01

Local polarization of a magnetic layer, a well-known method for storing information, has found its place in numerous applications such as the popular magnetic drawing board toy or the widespread credit cards and computer hard drives. Here we experimentally show that a similar principle can be applied for imprinting the trajectory of quantum units of flux (vortices), travelling in a superconducting film (Nb), into a soft magnetic layer of permalloy (Py). In full analogy with the magnetic drawing board, vortices act as tiny magnetic scribers leaving a wake of polarized magnetic media in the Py board. The mutual interaction between superconducting vortices and ferromagnetic domains has been investigated by the magneto-optical imaging technique. For thick Py layers, the stripe magnetic domain pattern guides both the smooth magnetic flux penetration as well as the abrupt vortex avalanches in the Nb film. It is however in thin Py layers without stripe domains where superconducting vortices leave the clearest imprints of locally polarized magnetic moment along their paths. In all cases, we observe that the flux is delayed at the border of the magnetic layer. Our findings open the quest for optimizing magnetic recording of superconducting vortex trajectories. PMID:27263660

Imprinting superconducting vortex footsteps in a magnetic layer

NASA Astrophysics Data System (ADS)

Brisbois, Jérémy; Motta, Maycon; Avila, Jonathan I.; Shaw, Gorky; Devillers, Thibaut; Dempsey, Nora M.; Veerapandian, Savita K. P.; Colson, Pierre; Vanderheyden, Benoît; Vanderbemden, Philippe; Ortiz, Wilson A.; Nguyen, Ngoc Duy; Kramer, Roman B. G.; Silhanek, Alejandro V.

2016-06-01

Local polarization of a magnetic layer, a well-known method for storing information, has found its place in numerous applications such as the popular magnetic drawing board toy or the widespread credit cards and computer hard drives. Here we experimentally show that a similar principle can be applied for imprinting the trajectory of quantum units of flux (vortices), travelling in a superconducting film (Nb), into a soft magnetic layer of permalloy (Py). In full analogy with the magnetic drawing board, vortices act as tiny magnetic scribers leaving a wake of polarized magnetic media in the Py board. The mutual interaction between superconducting vortices and ferromagnetic domains has been investigated by the magneto-optical imaging technique. For thick Py layers, the stripe magnetic domain pattern guides both the smooth magnetic flux penetration as well as the abrupt vortex avalanches in the Nb film. It is however in thin Py layers without stripe domains where superconducting vortices leave the clearest imprints of locally polarized magnetic moment along their paths. In all cases, we observe that the flux is delayed at the border of the magnetic layer. Our findings open the quest for optimizing magnetic recording of superconducting vortex trajectories.

Optical fiber magnetic field sensors with TbDyFe magnetostrictive thin films as sensing materials.

PubMed

Yang, Minghong; Dai, Jixiang; Zhou, Ciming; Jiang, Desheng

2009-11-09

Different from usually-used bulk magnetostrictive materials, magnetostrictive TbDyFe thin films were firstly proposed as sensing materials for fiber-optic magnetic field sensing characterization. By magnetron sputtering process, TbDyFe thin films were deposited on etched side circle of a fiber Bragg Grating (FBG) as sensing element. There exists more than 45pm change of FBG wavelength when magnet field increase up to 50 mT. The response to magnetic field is reversible, and could be applicable for magnetic and current sensing.

Preparation of dilute magnetic semiconductor films by metalorganic chemical vapor deposition

NASA Technical Reports Server (NTRS)

Nouhi, Akbar (Inventor); Stirn, Richard J. (Inventor)

1990-01-01

A method for preparation of a dilute magnetic semiconductor (DMS) film is provided, wherein a Group II metal source, a Group VI metal source and a transition metal magnetic ion source are pyrolyzed in the reactor of a metalorganic chemical vapor deposition (MOCVD) system by contact with a heated substrate. As an example, the preparation of films of Cd.sub.1-x Mn.sub.x Te, wherein 0.ltoreq..times..ltoreq.0.7, on suitable substrates (e.g., GaAs) is described. As a source of manganese, tricarbonyl (methylcyclopentadienyl) maganese (TCPMn) is employed. To prevent TCPMn condensation during the introduction thereof int the reactor, the gas lines, valves and reactor tubes are heated. A thin-film solar cell of n-i-p structure, wherein the i-type layer comprises a DMS, is also described; the i-type layer is suitably prepared by MOCVD.

Fabrication, characterization and in-vitro cytotoxicity of magnetic nanocomposite polymeric film for multi-functional medical application

NASA Astrophysics Data System (ADS)

Zhao, Lingyun; Xu, Xiaoyu; Wang, Xiaowen; Zhang, Xiaodong; Gao, Fuping; Tang, Jintian

2009-07-01

Cancer comprehensive treatment has been fully acknowledged as it can provide an effective multimodality approach for fighting cancers. In this study, various innovative technologies for cancer treatment including cancer nanotechnology, chemotherapy by sustainable release, as well as magnetic induction hyperthermia (MIH) have been integrated for the purpose of cancer comprehensive treatment. Briefly, such kind of treatment can be realized by applying of the tailored magnetic nanoparticles (MNPs) composite polymeric film. Fe3O4 MNPs acting as the agent for MIH, and anti-cancer drug docetaxel as chemotherapeutic agent were incorporated within the biodegradable polymeric film. Physiochemical characterizations on MNPs and the film have been systematically carried out by various instrumental analyses. Our results demonstrated that the film has been successfully fabricated by the solvent cast method. Hyperthermia could be induced by stimulating the nanocomposite film under an alternative magnetic field (AMF). The incorporation of MNPs, as well as hyperthermia would facilitate the drug release from the polymeric film. The in-vitro cytotoxicity results indicated the bi-modal cancer treatment approach for combined MIH and chemotherapy is more effective than the mono-modal treatment by docetaxel treatment. The magnetic nanocomposite film can realize cancer comprehensive treatment thus has great potential in clinical application.

Permanent magnetic properties of NdFe12Nx sputtered films epitaxially grown on V buffer layer

NASA Astrophysics Data System (ADS)

Sato, T.; Ohsuna, T.; Yano, M.; Kato, A.; Kaneko, Y.

2017-08-01

To clarify the magnetic properties of the NdFe12Nx compound, which shows promise as a high-performance permanent magnet material, NdFe12Nx epitaxial films fabricated by using a V underlayer on MgO (100) single-crystalline substrates were investigated. Nd-Fe films deposited on a V underlayer consist of NdFe12 grains, which have a c-axis orientation perpendicular to the film plane, as well as α-Fe and Nd2Fe17 phases. In the Nd-Fe-N film obtained by subsequent nitridation of the Nd-Fe film, NdFe12Nx grains grew as the dominant phase, and the volume fractions of α-Fe phases dropped below 5%. A Nd-Fe-N film with a thickness of 50 nm exhibits a saturation magnetization (Ms) of 1.7 T, an anisotropy field (HA) of ˜60 kOe, a magnetocrystalline anisotropy energy (K1) of ˜4.1 MJ/m3, and a coercivity (Hc) of 1.7 kOe. The Hc of a Nd-Fe-N film with a thickness of 25 nm is 4.3 kOe. These results indicate that NdFe12Nx compounds have a superior Ms compared to Nd-Fe-B magnets, while the enhancement in Hc is indispensable.

Weak magnetism of Aurivillius-type multiferroic thin films probed by polarized neutron reflectivity

NASA Astrophysics Data System (ADS)

Zhai, Xiaofang; Grutter, Alexander J.; Yun, Yu; Cui, Zhangzhang; Lu, Yalin

2018-04-01

Unambiguous magnetic characterization of room-temperature multiferroic materials remains challenging due in part to the difficulty of distinguishing their very weak ferromagnetism from magnetic impurity phases and other contaminants. In this study, we used polarized neutron reflectivity to probe the magnetization of B i6FeCoT i3O18 and LaB i5FeCoT i3O18 in their epitaxial thin films while eliminating a variety of impurity contributions. Our results show that LaB i5FeCoT i3O18 exhibits a magnetization of about 0.016 ±0.027 μB/Fe -Co pair at room temperature, while the B i6FeCoT i3O18 thin film only exhibits a weak magnetic moment below room temperature, with a saturation magnetization of 0.049 ±0.015 μB/Fe -Co pair at 50 K. This polarized-neutron-reflectivity study places an upper magnetization limit on the matrix material of the magnetically doped Aurivillius oxides and helps to clarify the true mechanism behind the room-temperature magnetic performance.

Magnetic glass-film based on single-nanosize 𝜺 -Fe2O3 nanoparticles

NASA Astrophysics Data System (ADS)

Yoshikiyo, Marie; Namai, Asuka; Nakagawa, Kosuke; Ohkoshi, Shin-ichi

2017-05-01

We report a magnetic thin film of single-nanosize ɛ-Fe2O3 in SiO2 matrix. The glass-film was prepared by sintering a silica coated iron oxide hydroxide on a quartz substrate in air. The glass-film consists of ɛ-Fe2O3 of 8.8 nm size, and its thickness was 570 nm (0.57 μm) with a roughness of 10 nm (0.01 μm). UV-vis spectrum showed that the glass-film has small absorbance of 0.043 at 500 nm. The magneto-optical effect was investigated, and Faraday ellipticity showed a magnetic hysteresis loop with a coercive field of 3.0 ± 0.2 kOe. Furthermore, single-nanosize ɛ-Fe2O3 without silica was prepared as a reference sample, and ferroelectricity was observed. Therefore, the present thin glass-film consists of single-nanosize ferroelectric-ferromagnetic nanoparticles.

Anisotropic magnetism and spin-dependent transport in Co nanoparticle embedded ZnO thin films

NASA Astrophysics Data System (ADS)

Li, D. Y.; Zeng, Y. J.; Pereira, L. M. C.; Batuk, D.; Hadermann, J.; Zhang, Y. Z.; Ye, Z. Z.; Temst, K.; Vantomme, A.; Van Bael, M. J.; Van Haesendonck, C.

2013-07-01

Oriented Co nanoparticles were obtained by Co ion implantation in crystalline ZnO thin films grown by pulsed laser deposition. Transmission electron microscopy revealed the presence of elliptically shaped Co precipitates with nanometer size, which are embedded in the ZnO thin films, resulting in anisotropic magnetic behavior. The low-temperature resistance of the Co-implanted ZnO thin films follows the Efros-Shklovskii type variable-range-hopping. Large negative magnetoresistance (MR) exceeding 10% is observed in a magnetic field of 1 T at 2.5 K and the negative MR survives up to 250 K (0.3%). The negative MR reveals hysteresis as well as anisotropy that correlate well with the magnetic properties, clearly demonstrating the presence of spin-dependent transport.

Cross-tie walls and magnetic singularities on the surface of permalloy films (abstract)

NASA Astrophysics Data System (ADS)

Lee, Y.; Kueny, A.; Koymen, A. R.

1997-04-01

An understanding of the surface magnetic microstructure of thin polycrystalline permalloy films is important for the development of improved magnetoresistive sensors. Scanning electron microscopy with polarization analysis (SEMPA) was used to image the surface magnetic domain structure of permalloy films in ultrahigh vacuum. The SEMPA system uses a compact Mott electron spin polarimeter with a Th foil (operating at 25 keV) that has been attached to the back of a hemispherical energy analyzer. Two orthogonal in-plane components of the electron spin polarization were measured to obtain magnetic domain images with excellent contrast. 350 Å Ni83Fe17 films, deposited by Honeywell-Micro Switch using dc magnetron sputtering, were studied. The samples were demagnetized along the easy axis by an ac magnetic field with decreasing amplitude. Using SEMPA, zigzag domain walls separating two large approximately head-on domains were observed. Cross-tie walls were observed with a periodic vortex structure along the straight edges of the zigzag domain walls. The cross-tie walls occur at the points where the magnetization is reversed by 180° across the straight edges of the wall. At high magnification, the elliptical and hyperbolic singularities at the cross-tie walls were clearly observed. In addition, the Néel part and the Bloch part of the cross-tie were distinguished This is a detailed study of cross-tie walls on sputter deposited thin permalloy films using SEMPA and our results are in good agreement with theoretical calculations.

Modeling of non-ideal hard permanent magnets with an affine-linear model, illustrated for a bar and a horseshoe magnet

NASA Astrophysics Data System (ADS)

Glane, Sebastian; Reich, Felix A.; Müller, Wolfgang H.

2017-11-01

This study is dedicated to continuum-scale material modeling of isotropic permanent magnets. An affine-linear extension to the commonly used ideal hard model for permanent magnets is proposed, motivated, and detailed. In order to demonstrate the differences between these models, bar and horseshoe magnets are considered. The structure of the boundary value problem for the magnetic field and related solution techniques are discussed. For the ideal model, closed-form analytical solutions were obtained for both geometries. Magnetic fields of the boundary value problems for both models and differently shaped magnets were computed numerically by using the boundary element method. The results show that the character of the magnetic field is strongly influenced by the model that is used. Furthermore, it can be observed that the shape of an affine-linear magnet influences the near-field significantly. Qualitative comparisons with experiments suggest that both the ideal and the affine-linear models are relevant in practice, depending on the magnetic material employed. Mathematically speaking, the ideal magnetic model is a special case of the affine-linear one. Therefore, in applications where knowledge of the near-field is important, the affine-linear model can yield more accurate results—depending on the magnetic material.

Isotropic rare earth based hard magnets through non-equilibrium processing

NASA Astrophysics Data System (ADS)

Sultana, Dilara

The aim of this thesis was to understand better the relationship of hard magnetic properties to the microstructure and use this knowledge to design a better magnet. The first project was focused on the development of isotropic Pr 9Fe85B6 ribbons with enhanced remanence, high coercivity and high (BH)max. The optimization was achieved by adjusting the composition, controlling the microstructure and processing parameters. The crystal structure in all the samples studied was found to consist of a fine mixture of hard phase 2:14:1 and soft alpha-Fe phase. In all the samples the optimum (BH)max obtained was in the optimally quenched ribbons. Annealing did improve the magnetic properties but did not exceed the highest (BH)max value obtained in the optimally quenched ribbons. Small additions of Tb and Co were found to improve the magnetic properties. The properties were optimized by first adjusting the wheel speed and then the ejection temperature of melt. A maximum (BH)max 21 MGOe and a remanence of 117 emu/g were obtained in the ribbons spun at 18 m/s and ejected at a temperature of 1360°C with a average grain size of 20 nm. This investigation suggests that a proper combination of composition and processing parameters is essential for the optimum (BH)max value for the Pr-Fe-B magnets. The second project was focused on the development of a single phase nanocrystalline Sm2(Co, Fe)17 magnets. The magnetic properties such as coercivity and energy product were optimized via the design of composition, control of melt-spinning parameters and heat treatment. The effect of non magnetic elements like Si, B, addition on the Sm(Co, Fe, M)z alloys were investigated. The effect of C addition on the Smx(Co 1-yMy)100-x-zCz series alloys where, M= Fe or Fe+Mn , X=10-15, Y= 0-0.375, Z= 0-6 were studied thoroughly. It is observed that the crystal structure of Sm(Co0.75Fe0.25) 7, Sm(Co0.65Fe0.25Si0.1)7 and Sm(Co0.65Fe0.25Si0.05B0.05 )8 alloy ribbons spun at low wheel speed shows the

Magnetic domain observation of FeCo thin films fabricated by alternate monoatomic layer deposition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ohtsuki, T., E-mail: ohtsuki@spring8.or.jp; Kotsugi, M.; Ohkochi, T.

2014-01-28

FeCo thin films are fabricated by alternate monoatomic layer deposition method on a Cu{sub 3}Au buffer layer, which in-plane lattice constant is very close to the predicted value to obtain a large magnetic anisotropy constant. The variation of the in-plane lattice constant during the deposition process is investigated by reflection high-energy electron diffraction. The magnetic domain images are also observed by a photoelectron emission microscope in order to microscopically understand the magnetic structure. As a result, element-specific magnetic domain images show that Fe and Co magnetic moments align parallel. A series of images obtained with various azimuth reveal that themore » FeCo thin films show fourfold in-plane magnetic anisotropy along 〈110〉 direction, and that the magnetic domain structure is composed only of 90∘ wall.« less

Growth dependent magnetization reversal in Co2MnAl full Heusler alloy thin films

NASA Astrophysics Data System (ADS)

Barwal, Vineet; Husain, Sajid; Behera, Nilamani; Goyat, Ekta; Chaudhary, Sujeet

2018-02-01

Angular dependent magnetization reversal has been investigated in Co2MnAl (CMA) full Heusler alloy thin films grown on Si(100) at different growth temperatures (Ts) by DC-magnetron sputtering. An M -shaped curve is observed in the in-plane angular (0°-360°) dependent coercivity (ADC) by magneto-optical Kerr effect measurements. The dependence of the magnetization reversal on Ts is investigated in detail to bring out the structure-property correlation with regards to ADC in these polycrystalline CMA thin films. This magnetization reversal ( M -shaped ADC behavior) is well described by the two-phase model, which is a combination of Kondorsky (domain wall motion) and Stoner Wohlfarth (coherent rotation) models. In this model, magnetization reversal starts with depinning of domain walls, with their gradual displacement explained by the Kondorsky model, and at a higher field (when the domain walls merge), the system follows coherent rotation before reaching its saturation following the Stoner Wohlfarth model. Further, the analysis of angular dependent squareness ratio (Mr/Ms) indicates that our films clearly exhibited twofold uniaxial anisotropy, which is related to self-steering effect arising due to the obliquely incident flux during the film-growth.

PLD growth of CoPd thin films and characterization of their magnetic properties by magneto optical Kerr effect

NASA Astrophysics Data System (ADS)

Sedrpooshan, Mehran; Ahmadvand, Hossein; Ranjbar, Mehdi; Salamati, Hadi

2018-06-01

CoPd alloy thin films with different thicknesses and Co/Pd ratios have been deposited on Si (100) substrate by pulsed laser deposition (PLD). The magnetic properties were investigated by using the magneto-optical Kerr effect (MOKE) in both longitudinal and polar geometries. The results show that the films with thickness in the range of 6-24 nm, deposited at a low substrate temperature of 200 °C, are mostly magnetized in the plane of film. Higher deposition temperature forces the magnetic easy axis to orient in the perpendicular direction of the films.

Origin of steps in magnetization loops of martensitic Ni-Mn-Ga films on MgO(001)

NASA Astrophysics Data System (ADS)

Laptev, Aleksej; Lebecki, Kristof; Welker, Gesa; Luo, Yuansu; Samwer, Konrad; Fonin, Mikhail

2016-09-01

We study the temperature dependent magnetization properties of (010)-oriented Ni-Mn-Ga epitaxial films on MgO(001) substrates. In the martensitic phase, we observe pronounced abrupt slope changes in the magnetization loops for all studied samples. Our experimental findings are discussed in conjunction with the micromagnetic simulations, revealing that the characteristic magnetization behavior is governed solely by the magnetization switching within the specific martensitic variant pattern, and no reorientation of twin variants is involved in the process. Our study emphasizes the important role of the magnetostatic interactions in the magnetization behavior of magnetic shape memory alloy thin films.

Magnetic field effect in organic films and devices

NASA Astrophysics Data System (ADS)

Gautam, Bhoj Raj

In this work, we focused on the magnetic field effect in organic films and devices, including organic light emitting diodes (OLEDs) and organic photovoltaic (OPV) cells. We measured magnetic field effect (MFE) such as magnetoconductance (MC) and magneto-electroluminescence (MEL) in OLEDs based on several pi- conjugated polymers and small molecules for fields |B|<100 mT. We found that both MC(B) and MEL(B) responses in bipolar devices and MC(B) response in unipolar devices are composed of two B-regions: (i) an 'ultra-small' region at |B| < 1-2 mT, and (ii) a monotonic response region at |B| >˜2mT. Magnetic field effect (MFE) measured on three isotopes of Poly (dioctyloxy) phenylenevinylene (DOO-PPV) showed that both regular and ultra-small effects are isotope dependent. This indicates that MFE response in OLED is mainly due to the hyperfine interaction (HFI). We also performed spectroscopy of the MFE including magneto-photoinduced absorption (MPA) and magneto-photoluminescence (MPL) at steady state conditions in several systems. This includes pristine Poly[2-methoxy-5-(2-ethylhexyl-oxy)-1,4-phenylene-vinylene] (MEH-PPV) films, MEH-PPV films subjected to prolonged illumination, and MEH-PPV/[6,6]-Phenyl C61 butyric acid methyl ester (PCBM) blend, as well as annealed and pristine C60 thin films. For comparison, we also measured MC and MEL in organic diodes based on the same materials. By directly comparing the MPA and MPL responses in films to MC and MEL in organic diodes based on the same active layers, we are able to relate the MFE in organic diodes to the spin densities of the excitations formed in the device, regardless of whether they are formed by photon absorption or carrier injection from the electrodes. We also studied magneto-photocurrent (MPC) and power conversion efficiency (PCE) of a 'standard' Poly (3-hexylthiophene)/PCBM device at various Galvinoxyl radical wt%. We found that the MPC reduction with Galvinoxyl wt% follows the same trend as that of the

Relationship between microstructural and magnetic properties of PrCo-based films prepared by the vacuum evaporation method

NASA Astrophysics Data System (ADS)

Fersi, R.; Bouzidi, W.; Bezergheanu, A.; Cizmas, C. B.; Bessais, L.; Mliki, N.

2018-04-01

In this work, Ce2Ni7 type structural PrCo-based films were deposited on Si(1 0 0) substrate by ultra-high (UHV) vacuum evaporation process. The structural and magnetic properties of these films have been performed using X-ray diffraction (XRD), atomic force microscopy (AFM), vibrating sample magnetometer (VSM) and magnetic force microscopy (MFM) techniques. Two effects on structural and magnetic properties of PrCo films have been investigated: the effect of the annealing temperature (Ta) and the effect of the variation of the magnetic X-layer thickness. The as deposited PrCo films have a magnetic coercivity (Hc) of about 40-100 Oe. But after annealing at 600 °C, Hc has increased hight about 9.5 kOe for PrCo(X = 20 nm) and 10.2 kOe for PrCo(X = 50 nm) were observed. The magnetic properties were affected by the thickness due to the morphology, also the relationship between the intergrain exchange coupling (IEC), the size and quantity of the PrCo grains. The hight extrinsic properties of Hc = 10.2 kOe, maximum energy product (BH)max of 5.12 MGOe and remanence ratio Mr /Ms = 0.53 are reported for the PrCo(X = 50 nm) films. These properties are highly desirable for extremely high-density magnetic recording media applications.

Effects of substitution on the exchange stiffness and magnetization of Co films

NASA Astrophysics Data System (ADS)

Eyrich, C.; Zamani, A.; Huttema, W.; Arora, M.; Harrison, D.; Rashidi, F.; Broun, D.; Heinrich, B.; Mryasov, O.; Ahlberg, M.; Karis, O.; Jönsson, P. E.; From, M.; Zhu, X.; Girt, E.

2014-12-01

An antiferromagnetically coupled FM/NM/FM (FM = ferromagnet, NM = normal metal) trilayer structure responds to an external magnetic field by the formation of a magnetic-moment spring within the FM layers. We show that the exchange stiffness (Aex) of an FM layer can be determined by fitting the field-dependent magnetization, M (H ) , of the FM/NM/FM trilayer to a micromagnetic model. Using this method, we have measured the exchange stiffness of thin-film Co alloyed with Cr, Fe, Ni, Pd, Pt, and Ru. The results show that the rate at which a substituent element reduces the exchange stiffness is not directly related to its effect on the magnetization of the alloy. The observed trends have been understood by material-specific modeling based on density functional theory within the local density approximation. The stiffness measurements are in agreement with Brillouin light scattering carried out on thicker Co films.

Study of Nonlinear MHD Tribological Squeeze Film at Generalized Magnetic Reynolds Numbers Using DTM.

PubMed

Rashidi, Mohammad Mehdi; Freidoonimehr, Navid; Momoniat, Ebrahim; Rostami, Behnam

2015-01-01

In the current article, a combination of the differential transform method (DTM) and Padé approximation method are implemented to solve a system of nonlinear differential equations modelling the flow of a Newtonian magnetic lubricant squeeze film with magnetic induction effects incorporated. Solutions for the transformed radial and tangential momentum as well as solutions for the radial and tangential induced magnetic field conservation equations are determined. The DTM-Padé combined method is observed to demonstrate excellent convergence, stability and versatility in simulating the magnetic squeeze film problem. The effects of involved parameters, i.e. squeeze Reynolds number (N1), dimensionless axial magnetic force strength parameter (N2), dimensionless tangential magnetic force strength parameter (N3), and magnetic Reynolds number (Rem) are illustrated graphically and discussed in detail. Applications of the study include automotive magneto-rheological shock absorbers, novel aircraft landing gear systems and biological prosthetics.

Study of Nonlinear MHD Tribological Squeeze Film at Generalized Magnetic Reynolds Numbers Using DTM

PubMed Central

Rashidi, Mohammad Mehdi; Freidoonimehr, Navid; Momoniat, Ebrahim; Rostami, Behnam

2015-01-01

In the current article, a combination of the differential transform method (DTM) and Padé approximation method are implemented to solve a system of nonlinear differential equations modelling the flow of a Newtonian magnetic lubricant squeeze film with magnetic induction effects incorporated. Solutions for the transformed radial and tangential momentum as well as solutions for the radial and tangential induced magnetic field conservation equations are determined. The DTM-Padé combined method is observed to demonstrate excellent convergence, stability and versatility in simulating the magnetic squeeze film problem. The effects of involved parameters, i.e. squeeze Reynolds number (N 1), dimensionless axial magnetic force strength parameter (N 2), dimensionless tangential magnetic force strength parameter (N 3), and magnetic Reynolds number (Re m) are illustrated graphically and discussed in detail. Applications of the study include automotive magneto-rheological shock absorbers, novel aircraft landing gear systems and biological prosthetics. PMID:26267247

Role of magnetic exchange interaction due to magnetic anisotropy on inverse spin Hall voltage at FeSi3%/Pt thin film bilayer interface

NASA Astrophysics Data System (ADS)

Shah, Jyoti; Ahmad, Saood; Chaujar, Rishu; Puri, Nitin K.; Negi, P. S.; Kotnala, R. K.

2017-12-01

In our recent studies inverse spin Hall voltage (ISHE) was investigated by ferromagnetic resonance (FMR) using bilayer FeSi3%/Pt thin film prepared by pulsed laser deposition (PLD) technique. In ISHE measurement microwave signal was applied on FeSi3% film along with DC magnetic field. Higher magnetization value along the film-plane was measured by magnetic hysteresis (M-H) loop. Presence of magnetic anisotropy has been obtained by M-H loop which showed easy direction of magnetization when applied magnetic field is parallel to the film plane. The main result of this study is that FMR induced inverse spin Hall voltage 12.6 μV at 1.0 GHz was obtained across Pt layer. Magnetic exchange field at bilayer interface responsible for field torque was measured 6 × 1014 Ω-1 m-2 by spin Hall magnetoresistance. The damping torque and spin Hall angle have been evaluated as 0.084 and 0.071 respectively. Presence of Si atom in FeSi3% inhomogenize the magnetic exchange field among accumulated spins at bilayer interface and feebly influenced by spin torque of FeSi3% layer. Weak field torque suppresses the spin pumping to Pt layer thus low value of inverse spin Hall voltage is obtained. This study provides an excellent opportunity to investigate spin transfer torque effect, thus motivating a more intensive experimental effort for its utilization at maximum potential. The improvement in spin transfer torque may be useful in spin valve, spin battery and spin transistor application.

Tuning Magnetic Order in Transition Metal Oxide Thin Films

NASA Astrophysics Data System (ADS)

Grutter, Alexander John

In recent decades, one of the most active and promising areas of condensed matter research has been that of complex oxides. With the advent of new growth techniques such as pulsed laser deposition and molecular beam epitaxy, a wealth of new magnetic and electronic ground states have emerged in complex oxide heterostructures. The wide variety of ground states in complex oxides is well known and generally attributed to the unprecedented variety of valence, structure, and bonding available in these systems. The tunability of this already diverse playground of states and interactions is greatly multiplied in thin films and heterostructures by the addition of parameters such as substrate induced strain and interfacial electronic reconstruction. Thus, recent studies have shown emergent properties such as the stabilization of ferromagnetism in a paramagnetic system, conductivity at the interface of two insulators, and even exchange bias at the interface between a paramagnet and a ferromagnet. Despite these steps forward, there remains remarkable disagreement on the mechanisms by which these emergent phenomena are stabilized. The contributions of strain, stoichiometry, defects, intermixing, and electronic reconstruction are often very difficult to isolate in thin films and superlattices. This thesis will present model systems for isolating the effects of strain and interfacial electronic interactions on the magnetic state of complex oxides from alternative contributions. We will focus first on SrRuO3, an ideal system in which to isolate substrate induced strain effects. We explore the effects of structural distortions in the simplest case of growth on (100) oriented substrates. We find that parameters including saturated magnetic moment and Curie temperature are all highly tunable through substrate induced lattice distortions. We also report the stabilization of a nonmagnetic spin-zero configuration of Ru4+ in tetragonally distorted films under tensile strain. Through

A double exposed portal image comparison between electronic portal imaging hard copies and port films in radiation therapy treatment setup confirmation to determine its clinical application in a radiotherapy center.

PubMed

Hatherly, K E; Smylie, J C; Rodger, A; Dally, M J; Davis, S R; Millar, J L

2001-01-01

At the William Buckland Radiotherapy Center (WBRC), field-only electronic portal image (EPI) hard copies are used for radiation treatment field verification for whole brain, breast, chest, spine, and large pelvic fields, as determined by a previous study. A subsequent research project, addressing the quality of double exposed EPI hard copies for sites where field only EPI was not considered adequate to determine field placement, has been undertaken. The double exposed EPI hard copies were compared to conventional double exposed port films for small pelvic, partial brain, and head and neck fields and for a miscellaneous group. All double exposed EPIs were captured during routine clinical procedures using liquid ion chamber cassettes. EPI hard copies were generated using a Visiplex multi-format camera. In sites where port film remained the preferred verification format, the port films were generated as per department protocol. In addition EPIs were collected specifically for this project. Four radiation oncologists performed the evaluation of EPI and port film images independently with a questionnaire completed at each stage of the evaluation process to assess the following: Adequacy of information in the image to assess field placement. Adequacy of information for determining field placement correction. Clinician's preferred choice of imaging for field placement assessment The results indicate that double exposed EPI hard copies generally do containsufficient information to permit evaluation of field placement and can replace conventionaldouble exposed port films in a significant number of sites. These include the following:pelvis fields < 12 X 12 cm, partial brain fields, and a miscellaneous group. However forradical head and neck fields, the preferred verification image format remained port film dueto the image hard copy size and improved contrast for this media. Thus in this departmenthard copy EPI is the preferred modality of field verification for all sites

Tuning the magnetic properties of LaCoO3 thin films by epitaxial strain

NASA Astrophysics Data System (ADS)

Fuchs, D.; Arac, E.; Pinta, C.; Schuppler, S.; Schneider, R.; v. Löhneysen, H.

2008-01-01

Ferromagnetic order can be induced in LaCoO3 (LCO) thin films by epitaxial strain. Here, we show that the magnetic properties can be “tuned” by epitaxial strain imposed on LCO thin films by the epitaxial growth on various substrate materials, i.e., (001) oriented SrLaAlO4 , LaAlO3 , SrLaGaO4 , (LaAlO3)0.3(Sr2AlTaO6)0.7 , and SrTiO3 . The lattice mismatch at room temperature of the in-plane lattice parameters between the substrate, as , and bulk LCO, ab , ranges from -1.31% to +2.63% . Single-phase, ⟨001⟩ oriented LCO thin films were grown by pulsed laser deposition on all these substrates. Due to the difference of the thermal-expansion coefficients between LCO and the substrates, the films experience an additional tensile strain of about +0.3% during the cooling process after the deposition at Ts=650°C . The film lattice parameters display an elastic behavior, i.e., an increase of the in-plane film lattice parameter with increasing as . From the ratio between the out-of-plane and in-plane strain, we obtain a Poisson ratio of ν≈1/3 . All films show a ferromagnetic transition as determined from magnetization measurements. The magnetization increases strongly with increasing tensile strain, whereas the transition temperature TC after a rapid initial rise appears to saturate at TC≈85K above a=3.86Å . The effective magnetic moment μeff in the paramagnetic state increases almost linearly as a function of the mean lattice parameter ⟨a⟩ , indicating an enhanced population of higher spin states, i.e., intermediate- or high-spin states. The experimental results are discussed in terms of a decrease of the octahedral-site rotation with increasing tensile strain.

Ferromagnetic MnGaN thin films with perpendicular magnetic anisotropy for spintronics applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lee, Hwachol; Sukegawa, Hiroaki, E-mail: sukegawa.hiroaki@nims.go.jp; Ohkubo, Tadakatsu

2015-07-20

Perpendicularly magnetized flat thin films of antiperovskite Mn{sub 67}Ga{sub 24}N{sub 9} were grown on an MgO(001) substrate by reactive sputtering using an argon/1% nitrogen gas mixture and a Mn{sub 70}Ga{sub 30} target. The films showed a saturation magnetization of 80 –100 kA/m, an effective perpendicular magnetic anisotropy (PMA) energy of 0.1–0.2 MJ/m{sup 3}, and a Curie temperature of 660–740 K. Upon increasing the N composition, the films transformed from ferromagnetic to antiferromagnetic as expected in the stoichiometric Mn{sub 3}GaN phase. Point contact Andreev reflection spectroscopy revealed that the ferromagnetic MnGaN has a current spin polarization of 57%, which is comparable to D0{sub 22}-MnGa. Thesemore » findings suggest that MnGaN is a promising PMA layer for future spintronics devices.« less

Properties of Exchange Coupled All-garnet Magneto-Optic Thin Film Multilayer Structures

PubMed Central

Nur-E-Alam, Mohammad; Vasiliev, Mikhail; Kotov, Viacheslav A.; Balabanov, Dmitry; Akimov, Ilya; Alameh, Kamal

2015-01-01

The effects of exchange coupling on magnetic switching properties of all-garnet multilayer thin film structures are investigated. All-garnet structures are fabricated by sandwiching a magneto-soft material of composition type Bi1.8Lu1.2Fe3.6Al1.4O12 or Bi3Fe5O12:Dy2O3 in between two magneto-hard garnet material layers of composition type Bi2Dy1Fe4Ga1O12 or Bi2Dy1Fe4Ga1O12:Bi2O3. The fabricated RF magnetron sputtered exchange-coupled all-garnet multilayers demonstrate a very attractive combination of magnetic properties, and are of interest for emerging applications in optical sensors and isolators, ultrafast nanophotonics and magneto-plasmonics. An unconventional type of magnetic hysteresis behavior not observed previously in magnetic garnet thin films is reported and discussed. PMID:28788043

Influence of Under-layer Morphology on Structural and Magnetic Properties of Sputtered Co81Pd19 Films

NASA Astrophysics Data System (ADS)

Ponchaiya, Pairin; Rattanasakulthong, Watcharee

2017-09-01

Sputtered Co81Pd19 films with thickness of about 60 nm were deposited on various under-layers (Co, Ni, Cr and Al) and on glass substrate. Structural, morphological and magnetic properties of Co81Pd19 films were investigated. All of prepared Co81Pd19 film showed CoPd-FCC phase in (111) direction on CoO-FCC (111), NiO-FCC (200), Cr-BCC (200) and (201) and AlO-FCC (200) phases of Co, Ni, Cr and Al under-layer, respectively. AFM images revealed that the film on Cr under-layers and glass substrate exhibited the maximum roughness with the highest grain size and the minimum roughness with the continuous grain size, respectively. Both parallel and perpendicular maximum coercive field were found in the film on glass under-layer and the film on Co-under-layer film showed the highest saturation magnetization from both in-plane and out-of-plane measurements. These results confirmed that the structural and magnetic properties of sputtered Co81Pd19 films were affected by under-layer surface roughness and morphology by the virtue of particle size and distribution on the under-layer film surface.

Magnetization enhancement due to incorporation of non-magnetic nitrogen content in (Co{sub 84}Zr{sub 16})N{sub x} nano-composite films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Singh, Jitendra, E-mail: jitendra@ceeri.ernet.in; Akhtar, Jamil; Academy of Scientific and Innovative Research, New Delhi 110001

We report the magnetic, electronic, and structural properties of nano-composite (Co{sub 84}Zr{sub 16})N{sub x} or CZN films prepared by reactive co-sputter deposition method. As-deposited CZN films have shown enhancement in magnetization (M{sub s}) with incorporation of nitrogen content, which is related to the evolution of nano-composite phase. X-ray diffraction study has confirmed poly-crystalline growth of CZN films with fcc(331) and fcc(422) phases. High-resolution transmission electron microscope study reveals that CZN films are composed of ordered and crystalline ferromagnetic Co nano-clusters, which are embedded in the nano-composite matrix. Photoemission measurements show the change in the intensity near the Fermi level mostmore » likely due to defects and shift in the core-levels binding energy with nitrogen concentration. Raman spectroscopy data show an increase in the intensity of the Raman lines with nitrogen concentration upto 20%. However, the intensity is significantly lower for 30% sample. This indicates that less nitrogen or defect states are being substituted into the lattice above 20% and is consistent with the observed magnetic behavior. Our studies indicate that defects induced due to the incorporation of non-magnetic nitrogen content play a key role to enhance the magnetization.« less

Retrieving spin textures on curved magnetic thin films with full-field soft X-ray microscopies

DOE PAGES

Streubel, Robert; Kronast, Florian; Fischer, Peter; ...

2015-07-03

X-ray tomography is a well-established technique to characterize 3D structures in material sciences and biology; its magnetic analogue—magnetic X-ray tomography—is yet to be developed. We demonstrate the visualization and reconstruction of magnetic domain structures in a 3D curved magnetic thin films with tubular shape by means of full-field soft X-ray microscopies. In the 3D arrangement of the magnetization is retrieved from a set of 2D projections by analysing the evolution of the magnetic contrast with varying projection angle. By using reconstruction algorithms to analyse the angular evolution of 2D projections provides quantitative information about domain patterns and magnetic coupling phenomenamore » between windings of azimuthally and radially magnetized tubular objects. In conclusion, the present approach represents a first milestone towards visualizing magnetization textures of 3D curved thin films with virtually arbitrary shape.« less

Retrieving spin textures on curved magnetic thin films with full-field soft X-ray microscopies

DOE Office of Scientific and Technical Information (OSTI.GOV)

Streubel, Robert; Kronast, Florian; Fischer, Peter

X-ray tomography is a well-established technique to characterize 3D structures in material sciences and biology; its magnetic analogue—magnetic X-ray tomography—is yet to be developed. We demonstrate the visualization and reconstruction of magnetic domain structures in a 3D curved magnetic thin films with tubular shape by means of full-field soft X-ray microscopies. In the 3D arrangement of the magnetization is retrieved from a set of 2D projections by analysing the evolution of the magnetic contrast with varying projection angle. By using reconstruction algorithms to analyse the angular evolution of 2D projections provides quantitative information about domain patterns and magnetic coupling phenomenamore » between windings of azimuthally and radially magnetized tubular objects. In conclusion, the present approach represents a first milestone towards visualizing magnetization textures of 3D curved thin films with virtually arbitrary shape.« less

Experiments and numerical modeling of fast flowing liquid metal thin films under spatially varying magnetic field conditions

NASA Astrophysics Data System (ADS)

Narula, Manmeet Singh

Innovative concepts using fast flowing thin films of liquid metals (like lithium) have been proposed for the protection of the divertor surface in magnetic fusion devices. However, concerns exist about the possibility of establishing the required flow of liquid metal thin films because of the presence of strong magnetic fields which can cause flow disrupting MHD effects. A plan is underway to design liquid lithium based divertor protection concepts for NSTX, a small spherical torus experiment at Princeton. Of these, a promising concept is the use of modularized fast flowing liquid lithium film zones, as the divertor (called the NSTX liquid surface module concept or NSTX LSM). The dynamic response of the liquid metal film flow in a spatially varying magnetic field configuration is still unknown and it is suspected that some unpredicted effects might be lurking. The primary goal of the research work being reported in this dissertation is to provide qualitative and quantitative information on the liquid metal film flow dynamics under spatially varying magnetic field conditions, typical of the divertor region of a magnetic fusion device. The liquid metal film flow dynamics have been studied through a synergic experimental and numerical modeling effort. The Magneto Thermofluid Omnibus Research (MTOR) facility at UCLA has been used to design several experiments to study the MHD interaction of liquid gallium films under a scaled NSTX outboard divertor magnetic field environment. A 3D multi-material, free surface MHD modeling capability is under development in collaboration with HyPerComp Inc., an SBIR vendor. This numerical code called HIMAG provides a unique capability to model the equations of incompressible MHD with a free surface. Some parts of this modeling capability have been developed in this research work, in the form of subroutines for HIMAG. Extensive code debugging and benchmarking exercise has also been carried out. Finally, HIMAG has been used to study the

Magnetic anisotropies in ultrathin fcc Fe(001) films grown on Cu(001) substrates

NASA Astrophysics Data System (ADS)

Cochran, J. F.; Rudd, J. M.; From, M.; Heinrich, B.; Bennett, W.; Schwarzacher, W.; Egelhoff, W. F., Jr.

1992-03-01

Ferromagnetic resonance absorption measurements at 36.3 GHz and at room temperature have been used to determine the g factor and anisotropy parameters for a series of bilayers composed of two 3-ML-thick fcc Fe (001) films separated by a variable thickness of fcc Cu(001). The resonance field and linewidth were measured versus the out-of-plane magnetic-field angle, θH. The magnetic properties of these ten coupled bilayer films were found to be remarkably similar from specimen to specimen, despite the fact that each member of the bilayer was only 3 ML thick. The average g factor was found to be =2.08+/-0.02, and the average effective magnetization was found to be -5.5+/-0.5 kOe; i.e., the specimens were magnetized normal to the specimen plane in zero applied magnetic field. If the effective field along the specimen normal can be attributed to a second-order surface anisotropy energy of the form Fs=-KU1 sin2θM, then =1.25+/-0.06 ergs/cm2, assuming a value 4πMs=21.6 kOe for the saturation magnetization and using d=5.4 Å for each film thickness. (This energy includes both sides of the film; the energy corresponding to a single Fe-Cu interface is 0.63 erg/cm2.) These specimens exhibited no measurable in-plane anisotropy. The linewidth was found to exhibit a sharp decrease for θH near 20°. This decrease could be explained in terms of the angular dependence of inhomogeneous line broadening due to a 1% variation in the perpendicular effective field from place to place in the sample plane.

Preparation of dilute magnetic semiconductor films by metalorganic chemical vapor deposition

NASA Technical Reports Server (NTRS)

Nouhi, Akbar (Inventor); Stirn, Richard J. (Inventor)

1988-01-01

A method for preparation of a dilute magnetic semiconductor (DMS) film is provided, in which a Group II metal source, a Group VI metal source and a transition metal magnetic ion source are pyrolyzed in the reactor of a metalorganic chemical vapor deposition (MOCVD) system by contact with a heated substrate. As an example, the preparation of films of Cd(sub 1-x)Mn(sub x)Te, in which 0 is less than or equal to x less than or equal to 0.7, on suitable substrates (e.g., GaAs) is described. As a source of manganese, tricarbonyl (methylcyclopentadienyl) manganese (TCPMn) is employed. To prevent TCPMn condensation during its introduction into the reactor, the gas lines, valves and reactor tubes are heated. A thin-film solar cell of n-i-p structure, in which the i-type layer comprises a DMS, is also described; the i-type layer is suitably prepared by MOCVD.

Effect of post-annealing on the magnetic properties of sputtered Mn56Al44 thin films

NASA Astrophysics Data System (ADS)

Gupta, Nanhe Kumar; Husain, Sajid; Barwal, Vineet; Behera, Nilamani; Chaudhary, Sujeet

2018-05-01

Mn56Al44 (MnAl) thin films of constant thickness (˜30nm) were grown on naturally oxidized Si substrates using DC-magnetron sputtering. Effect of deposition parameters such as sputtering power, substrate temperature (Ts), and post-annealing temperature have been systematically invstigated. X-ray diffraction patterns revealed the presence of mixed phases, namely the τ- and β-MnAl. The highest saturation magnetization (MS) was found to be 65emu/cc using PPMS-VSM in film grown at Ts=500°C. The magnetic ordering was found to get significantly improved by performing post-annealing of these as-grwon at 400°C for 1 hr in the presence of out-of-plane magnetic field of ˜1500Oe in vacuum. In particular, at room temperature (RT), the MS got enhanced after magnetic annealing from 65emu/cc to 500 emu/cc in MnAl films grown at Ts=500°C. This sample exhibited a magneto-resistance of ˜1.5% at RT. The tuning of the structural and magnetic properties of MnAl binary alloy thin films as established here by varying the growth parameters is critical with regards to the prospective applications of MnAl, a metastable ferromagnetic system which possesses the highest perpendicular magnetic anisotropy at RT till date.

Room temperature ferromagnetism with large magnetic moment at low field in rare-earth-doped BiFeO₃ thin films.

PubMed

Kim, Tae-Young; Hong, Nguyen Hoa; Sugawara, T; Raghavender, A T; Kurisu, M

2013-05-22

Thin films of rare earth (RE)-doped BiFeO3 (where RE=Sm, Ho, Pr and Nd) were grown on LaAlO3 substrates by using the pulsed laser deposition technique. All the films show a single phase of rhombohedral structure with space group R3c. The saturated magnetization in the Ho- and Sm-doped films is much larger than the values reported in the literature, and is observed at quite a low field of 0.2 T. For Ho and Sm doping, the magnetization increases as the film becomes thinner, suggesting that the observed magnetism is mostly due to a surface effect. In the case of Nd doping, even though the thin film has a large magnetic moment, the mechanism seems to be different.

Growth, structure, and magnetic properties of γ-Fe2O3 epitaxial films on MgO

NASA Astrophysics Data System (ADS)

Gao, Y.; Kim, Y. J.; Thevuthasan, S.; Chambers, S. A.; Lubitz, P.

1997-04-01

Single-crystal epitaxial thin films of γ-Fe2O3(001) have been grown on MgO(001) using oxygen-plasma-assisted molecular beam epitaxy. The structure and magnetic properties of these films have been characterized by a variety of techniques, including reflection high-energy electron diffraction (RHEED), low-energy electron diffraction (LEED), x-ray photoelectron spectroscopy and x-ray photoelectron/Auger electron diffraction (XPD/AED), vibrating sample magnetometry, and ferromagnetic resonance. Real-time RHEED reveals that the film growth occurs in a layer-by-layer fashion. The γ-Fe2O3(001) film surface exhibits a (1×1) LEED pattern. The growth of γ-Fe2Ooverflow="scroll">3 films at 450 °C is accompanied by significant Mg outdiffusion. AED of Mg KLL Auger emission reveals that Mg substitutionally incorporates in the γ-Fe2O3 lattice, occupying the octahedral sites. Magnetic moments are ˜2300 G and ˜4500 G for γ-Fe2O3 films grown at 250 °C and 450 °C, respectively. The high magnetic moment for the films grown at 450 °C could be attributed to the high degree of structural order of the films and Mg substitution at octahedral sites.

Effect of CoSi2 buffer layer on structure and magnetic properties of Co films grown on Si (001) substrate

NASA Astrophysics Data System (ADS)

Hu, Bo; He, Wei; Ye, Jun; Tang, Jin; Syed Sheraz, Ahmad; Zhang, Xiang-Qun; Cheng, Zhao-Hua

2015-01-01

Buffer layer provides an opportunity to enhance the quality of ultrathin magnetic films. In this paper, Co films with different thickness of CoSi2 buffer layers were grown on Si (001) substrates. In order to investigate morphology, structure, and magnetic properties of films, scanning tunneling microscope (STM), low energy electron diffraction (LEED), high resolution transmission electron microscopy (HRTEM), and surface magneto-optical Kerr effect (SMOKE) were used. The results show that the crystal quality and magnetic anisotropies of the Co films are strongly affected by the thickness of CoSi2 buffer layers. Few CoSi2 monolayers can prevent the interdiffusion of Si substrate and Co film and enhance the Co film quality. Furthermore, the in-plane magnetic anisotropy of Co film with optimal buffer layer shows four-fold symmetry and exhibits the two-jumps of magnetization reversal process, which is the typical phenomenon in cubic (001) films. Project supported by the National Basic Research Program of China (Grant Nos. 2011CB921801 and 2012CB933102), the National Natural Science Foundation of China (Grant Nos. 11374350, 11034004, 11274361, and 11274033), and the Research Fund for the Doctoral Program of Higher Education of China (Grant No. 20131102130005).

Pancreatic hardness: Correlation of surgeon’s palpation, durometer measurement and preoperative magnetic resonance imaging features

PubMed Central

Hong, Tae Ho; Choi, Joon-Il; Park, Michael Yong; Rha, Sung Eun; Lee, Young Joon; You, Young Kyoung; Choi, Moon Hyung

2017-01-01

AIM To evaluate the correlation between subjective assessments of pancreatic hardness based on the palpation, objective measurements using a durometer, and magnetic resonance imaging (MRI) findings for assessing pancreatic hardness. METHODS Eighty-three patients undergoing pancreatectomies were enrolled. An experienced surgeon subjectively evaluated the pancreatic hardness in the surgical field by palpation. The pancreatic hardness was also objectively evaluated using a durometer. Preoperative MRI findings were evaluated by a radiologist in terms of the apparent diffusion coefficient (ADC) values, the relative signal intensity decrease (RSID) of the pancreatic parenchyma, and the diameter of the pancreatic parenchyma and duct. Durometer measurement results, ADC values, RSID, pancreatic duct and parenchyma diameters, and the ratio of the diameters of the duct and parenchyma were compared between pancreases judged to be soft or hard pancreas on the palpation. A correlation analysis was also performed between the durometer and MRI measurements. RESULTS The palpation assessment classified 44 patients as having a soft pancreas and 39 patients as having a hard pancreas. ADC values were significantly lower in the hard pancreas group. The ductal diameter and duct-to-pancreas ratio were significantly higher in the hard pancreas group. For durometer measurements, a correlation analysis showed a positive correlation with the ductal diameter and the duct-to-pancreas ratio and a negative correlation with ADC values. CONCLUSION Hard pancreases showed lower ADC values, a wider pancreatic duct diameter and a higher duct-to-pancreas ratio than soft pancreases. Additionally, the ADC values, diameter of the pancreatic duct and duct-to-pancreas ratio were closely correlated with the durometer results. PMID:28373771

Influence of annealing temperature on structural and magnetic properties of pulsed laser-deposited YIG films on SiO2 substrate

NASA Astrophysics Data System (ADS)

Nag, Jadupati; Ray, Nirat

2018-05-01

Yttrium Iron Garnet (Y3Fe5O12) was synthesized by solid state/ceramic process. Thin films of YIG were deposited on SiO2 substrate at room temperature(RT) and at substrate temperature (Ts) 700 °C using pulsed laser deposition (PLD) technique. RT deposited thin films are amorphous in nature and non-magnetic. After annealing at temperature 800 ° RT deposited thin films showed X-ray peaks as well as the magnetic order. Magnetic ordering is enhanced by annealing temperature(Ta ≥ 750 °C) and resulted good quality of films with high magnetization value.

Correcting and coating thin walled X-ray Optics via a combination of controlled film deposition and magnetic smart materials

NASA Astrophysics Data System (ADS)

Ulmer, Melville

The project goal is to demonstrate that thin walled (<400 micron thick) X-ray optics can be controllably shaped to produce high quality (~1" or better) X-ray optics at an affordable price. Since the desired surface area for the next generation X-ray telescope is >10x that of Chandra, the >10x requirement is then for >200 m^2 of surface area with a surface finish of better than 0.5 nm. Therefore, replication of some sort is called for. Because no replication technology has been shown to achieve ≤1" angular resolution, post fabrication figure corrections are likely going to be necessary. Some have proposed to do this in orbit and others prelaunch including us. Our prelaunch approach is to apply in-plane stresses to the thin walled mirror shells via a magnetic field. The field will be held in by some magnetically hard material such as NiCo. By use of a so called magnetic smart material (MSM) such as Terfenol-D, we already shown that strong enough stresses can be generated. Preliminary work has also shown that the magnetic field can be held in well enough to apply the figure correcting stresses pre-launch. What we call "set-it and forget-it." However, what is unique about our approach is that at the cost of complexity and some areal coverage, our concept will also accommodate in-orbit adjustments. Furthermore, to the best of our knowledge ours is one of two known stress modification processes that are bi-axial. Our plan is first to validate set-it and forget-it first on cantilevers and then to expand this to working on 5 cm x 5 cm pieces. We will work both with NiCo and glass or Si coated with Terfenol-D. Except for the NiCo, substrates we will also coat the samples with NiCo in order to have a film that will hold in the magnetic field. As part of the coating process, we will control the stress of the film by varying the voltage bias while coating. The bias stress control can be used to apply films with minimal stress such as Terfenol-D and X-ray reflecting coatings

3D vector distribution of the electro-magnetic fields on a random gold film

NASA Astrophysics Data System (ADS)

Canneson, Damien; Berini, Bruno; Buil, Stéphanie; Hermier, Jean-Pierre; Quélin, Xavier

2018-05-01

The 3D vector distribution of the electro-magnetic fields at the very close vicinity of the surface of a random gold film is studied. Such films are well known for their properties of light confinement and large fluctuations of local density of optical states. Using Finite-Difference Time-Domain simulations, we show that it is possible to determine the local orientation of the electro-magnetic fields. This allows us to obtain a complete characterization of the fields. Large fluctuations of their amplitude are observed as previously shown. Here, we demonstrate large variations of their direction depending both on the position on the random gold film, and on the distance to it. Such characterization could be useful for a better understanding of applications like the coupling of point-like dipoles to such films.

Magnetism of Amorphous and Nano-Crystallized Dc-Sputter-Deposited MgO Thin Films

PubMed Central

Mahadeva, Sreekanth K.; Fan, Jincheng; Biswas, Anis; Sreelatha, K.S.; Belova, Lyubov; Rao, K.V.

2013-01-01

We report a systematic study of room-temperature ferromagnetism (RTFM) in pristine MgO thin films in their amorphous and nano-crystalline states. The as deposited dc-sputtered films of pristine MgO on Si substrates using a metallic Mg target in an O2 containing working gas atmosphere of (N2 + O2) are found to be X-ray amorphous. All these films obtained with oxygen partial pressure (PO2) ~10% to 80% while maintaining the same total pressure of the working gas are found to be ferromagnetic at room temperature. The room temperature saturation magnetization (MS) value of 2.68 emu/cm3 obtained for the MgO film deposited in PO2 of 10% increases to 9.62 emu/cm3 for film deposited at PO2 of 40%. However, the MS values decrease steadily for further increase of oxygen partial pressure during deposition. On thermal annealing at temperatures in the range 600 to 800 °C, the films become nanocrystalline and as the crystallite size grows with longer annealing times and higher temperature, MS decreases. Our study clearly points out that it is possible to tailor the magnetic properties of thin films of MgO. The room temperature ferromagnetism in MgO films is attributed to the presence of Mg cation vacancies. PMID:28348346

Studies of electronic and magnetic properties of LaVO3 thin film

NASA Astrophysics Data System (ADS)

Jana, Anupam; Karwal, Sharad; Choudhary, R. J.; Phase, D. M.

2018-04-01

We have investigated the electronic and magnetic properties of pulsed laser deposited Mott insulator LaVO3 (LVO) thin film. Structural characterization revels the single phase [00l] oriented LVO thin film. Enhancement of out of plane lattice parameter indicates the compressively strained LVO film. Electron spectroscopic studies demonstrate that vanadium is present in V3+ state. An energy dispersive X-ray spectroscopic study ensures the stoichiometric growth of the film. Very smooth surface is observed in scanning electron micrograph. Colour mapping for elemental distribution reflect the homogeneity of LVO film. The bifurcation between zero-field-cooled and Field-cooled curves clearly points towards the weak ferromagnetic phase presence in compressively strained LVO thin film. A finite value of coercivity at 300 K reflects the possibility of room temperature ferromagnetism of LVO thin film.

Dynamic depinning phase transition in magnetic thin film with anisotropy

NASA Astrophysics Data System (ADS)

Xiong, L.; Zheng, B.; Jin, M. H.; Wang, L.; Zhou, N. J.

2018-02-01

The dynamic pinning effects induced by quenched disorder are significant in manipulating the domain-wall motion in nano-magnetic materials. Through numerical simulations of the nonstationary domain-wall dynamics with the Landau-Lifshitz-Gilbert equation, we confidently detect a dynamic depinning phase transition in a magnetic thin film with anisotropy, which is of second order. The transition field, static and dynamic exponents are accurately determined, based on the dynamic scaling behavior far from stationary.

Additive patterning of ion-beam-sputtered non-conformal Ni80Fe20 and Co70Fe30 magnetic films

NASA Astrophysics Data System (ADS)

Redondo, C.; Moralejo, S.; Castaño, F.; Lee, W.; Nielsch, K.; Ross, C. A.; Castaño, F. J.

2006-04-01

Additive patterning processes of magnetic films grown using an ion-beam sputter (IBS) system designed to produce non-conformal films are described. The effects of the ion-gun beam current and Ar pressure on the sputtering rates and roughness of Ni80Fe20 and Co70Fe30 magnetic thin films are investigated using atomic-force microscopy (AFM) and the films' magnetic properties are measured using spatially resolved magneto-optical magnetometry. By tailoring the plasma solid angle, non-conformal film growth allows for simple additive patterning down to lateral dimensions ranging from a few microns to the deep-submicron regime, using templates defined by photolithography or electron-beam lithography, and shadow masks created using templated self-assembly. The magnetization reversal exhibited by patterned sub-200 nm nanodisc arrays with different lateral edge-roughness will be discussed.

Temperature and field dependent magnetization studies on nano-crystalline ZnFe2O4 thin films

NASA Astrophysics Data System (ADS)

Sahu, B. N.; Suresh, K. G.; Venkataramani, N.; Prasad, Shiva; Krishnan, R.

2018-05-01

Single phase nano-crystalline zinc ferrite (ZnFe2O4) thin films were deposited on fused quartz substrate using the pulsed laser deposition technique. The films were deposited at different substrate temperatures. The field dependence of magnetization at 10 K shows hysteresis loops for all the samples. Temperature dependence of the field cooled (FC) and zero field cooled (ZFC) magnetization indicated irreversible behavior between the FC and ZFC data, and the irreversibility depends on the measuring magnetic field. The thermo-magnetic irreversibility in the magnetization data is correlated with the magnitude of the applied field and the coercivity (HC) obtained from the M-H loops.

Size effect in the spin glass magnetization of thin AuFe films as studied by polarized neutron reflectometry.

PubMed

Saoudi, M; Fritzsche, H; Nieuwenhuys, G J; Hesselberth, M B S

2008-02-08

We used polarized neutron reflectometry to determine the temperature dependence of the magnetization of thin AuFe films with 3% Fe concentration. We performed the measurements in a large magnetic field of 6 T in a temperature range from 295 to 2 K. For the films in the thickness range from 500 to 20 nm we observed a Brillouin-type behavior from 295 K down to 50 K and a constant magnetization of about 0.9 micro(B) per Fe atom below 30 K. However, for the 10 nm thick film we observed a Brillouin-type behavior down to 20 K and a constant magnetization of about 1.3 micro(B) per Fe atom below 20 K. These experiments are the first to show a finite-size effect in the magnetization of single spin-glass films in large magnetic fields. Furthermore, the ability to measure the deviation from the paramagnetic behavior enables us to prove the existence of the spin-glass state where other methods relying on a cusp-type behavior fail.

Perpendicular magnetic anisotropy of Pd-Co alloy films and related multilayers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tsunashima, S.; Nagase, K.; Nakamura, K.

1989-09-01

Magnetic anisotropy of Pd/sub x/Co/sub 1-x/alloy films and Pd/sub 67/Co/sub 33/, Pd/sub 67/Co/sub 33/, Pd/sub 67/Co/sub 33//Cu multilayers are investigated. Vacuum deposited PdCo alloy films exhibit uniaxial anisotropy Ku with the easy axis perpendicular to the film plane. The maximum Ku is about 5X10/sup 6/erg/cm/sup 3/ for x=0.35 to 0.50. Compositional dependence of Ku is similar to that of the magnetostriction constant {lambda}/sub 111/, which suggests magnetostrictive origin. In multilayer films, PdCo/Pt and PdCo/Pd showed positive Ku while PdCo/Cu showed negative.

Tuning magnetic exchange interactions in crystalline thin films of substituted Cobalt Phthalocyanine

NASA Astrophysics Data System (ADS)

Rawat, Naveen; Manning, Lane; Hua, Kim-Ngan; Headrick, Randall; Bishop, Michael; McGill, Stephen; Waterman, Rory; Furis, Madalina

Magnetic exchange interactions in diluted organometallic crystalline thin film alloys of Phthalocyanines (Pcs) made of a organo-soluble derivatives of Cobalt Pc and metal-free (H2Pc) molecule and is investigated. To this end, we synthesized a organosoluble CoPc and successfully employed a novel solution-based pen-writing deposition technique to fabricate long range ordered thin films of mixtures of different ratios ranging from 1:1 to 10:1 H2Pc:CoPc. Our previous magnetic circular dichroism (MCD) results on the parent CoPc crystalline thin films identified different electronic states mediating exchange interactions and indirect exchange interaction competing with superexchange interaction. This understanding of spin-dependent exchange interaction between delocalized π-electrons with unpaired d spins along with the excitonic delocalization character enabled the further tuning of these interactions by essentially varying the spatial distance between the spins. Furthermore, high magnetic field (B < 25 T) MCD and magneto-photoluminescence show evidence of spin-polarized band-edge excitons in the same materials. This work was possible due to support by the National Science Foundation, Division of Materials Research MRI, CAREER and EPM program Awards: DMR-0722451, DMR-0821268, DMR-1307017 and DMR-1056589, DMR-1229217.

Thin chitosan films containing super-paramagnetic nanoparticles with contrasting capability in magnetic resonance imaging.

PubMed

Farjadian, Fatemeh; Moradi, Sahar; Hosseini, Majid

2017-03-01

Magnetic nanoparticles have found application as MRI contrasting agents. Herein, chitosan thin films containing super-paramagnetic iron oxide nanoparticles (SPIONs) are evaluated in magnetic resonance imaging (MRI). To determine their contrasting capability, super-paramagnetic nanoparticles coated with citrate (SPIONs-cit) were synthesized. Then, chitosan thin films with different concentrations of SPIONs-cit were prepared and their MRI data (i.e., r 2 and r 2 *) was evaluated in an aqueous medium. The synthesized SPIONs-cit and chitosan/SPIONs-cit films were characterized by FTIR, EDX, XRD as well as VSM with the morphology evaluated by SEM and AFM. The nanoparticle sizes and distribution confirmed well-defined nanoparticles and thin films formation along with high contrasting capability in MRI. Images revealed well-dispersed uniform nanoparticles, averaging 10 nm in size. SPIONs-cit's hydrodynamic size averaged 23 nm in diameter. The crystallinity obeyed a chitosan and SPIONs pattern. The in vitro cellular assay of thin films with a novel route was performed within Hek293 cell lines showing that thin films can be biocompatible.

Enhanced magnetic and thermoelectric properties in epitaxial polycrystalline SrRuO3 thin films.

PubMed

Woo, Sungmin; Lee, Sang A; Mun, Hyeona; Choi, Young Gwan; Zhung, Chan June; Shin, Soohyeon; Lacotte, Morgane; David, Adrian; Prellier, Wilfrid; Park, Tuson; Kang, Won Nam; Lee, Jong Seok; Kim, Sung Wng; Choi, Woo Seok

2018-03-01

Transition metal oxide thin films show versatile electric, magnetic, and thermal properties which can be tailored by deliberately introducing macroscopic grain boundaries via polycrystalline solids. In this study, we focus on the modification of magnetic and thermal transport properties by fabricating single- and polycrystalline epitaxial SrRuO 3 thin films using pulsed laser epitaxy. Using the epitaxial stabilization technique with an atomically flat polycrystalline SrTiO 3 substrate, an epitaxial polycrystalline SrRuO 3 thin film with the crystalline quality of each grain comparable to that of its single-crystalline counterpart is realized. In particular, alleviated compressive strain near the grain boundaries due to coalescence is evidenced structurally, which induced the enhancement of ferromagnetic ordering of the polycrystalline epitaxial thin film. The structural variations associated with the grain boundaries further reduce the thermal conductivity without deteriorating the electronic transport, and lead to an enhanced thermoelectric efficiency in the epitaxial polycrystalline thin films, compared with their single-crystalline counterpart.

Soft magnetic properties of nanocrystalline FeRuGaSi-Hf alloy films and head characteristics for the embedded thin film tape head

NASA Astrophysics Data System (ADS)

Ohmori, H.; Shoji, M.; Kobayashi, T.; Yamamoto, T.; Sugiyama, Y.; Hayashi, K.; Hono, K.

1996-04-01

The Hf-added FeRuGaSi alloy film has an amorphous structure in the as-deposited state and becomes nanocrystalline after annealing. Due to this structure change from crystalline to amorphous by the addition of Hf, soft magnetic degradation of the film deposited on the slant grooved substrate, which is necessary for the sophisticated embedded thin film (ETF) head structure, is greatly suppressed and the undesirable film stress is relieved. The FeRuGaSi-Hf alloy film has higher resistivity and permeability at high frequencies than those of sendust film, and the read/write characteristics of this alloy film show better performance than sendust film.

Ultrafast magnetization modulation induced by the electric field component of a terahertz pulse in a ferromagnetic-semiconductor thin film.

PubMed

Ishii, Tomoaki; Yamakawa, Hiromichi; Kanaki, Toshiki; Miyamoto, Tatsuya; Kida, Noriaki; Okamoto, Hiroshi; Tanaka, Masaaki; Ohya, Shinobu

2018-05-02

High-speed magnetization control of ferromagnetic films using light pulses is attracting considerable attention and is increasingly important for the development of spintronic devices. Irradiation with a nearly monocyclic terahertz pulse, which can induce strong electromagnetic fields in ferromagnetic films within an extremely short time of less than ~1 ps, is promising for damping-free high-speed coherent control of the magnetization. Here, we successfully observe a terahertz response in a ferromagnetic-semiconductor thin film. In addition, we find that a similar terahertz response is observed even in a non-magnetic semiconductor and reveal that the electric-field component of the terahertz pulse plays a crucial role in the magnetization response through the spin-carrier interactions in a ferromagnetic-semiconductor thin film. Our findings will provide new guidelines for designing materials suitable for ultrafast magnetization reversal.

Novel Chiral Magnetic Domain Wall Structure in Fe/Ni/Cu(001) Films

NASA Astrophysics Data System (ADS)

Chen, G.; Zhu, J.; Quesada, A.; Li, J.; N'Diaye, A. T.; Huo, Y.; Ma, T. P.; Chen, Y.; Kwon, H. Y.; Won, C.; Qiu, Z. Q.; Schmid, A. K.; Wu, Y. Z.

2013-04-01

Using spin-polarized low energy electron microscopy, we discovered a new type of domain wall structure in perpendicularly magnetized Fe/Ni bilayers grown epitaxially on Cu(100). Specifically, we observed unexpected Néel-type walls with fixed chirality in the magnetic stripe phase. Furthermore, we find that the chirality of the domain walls is determined by the film growth order with the chirality being right handed in Fe/Ni bilayers and left handed in Ni/Fe bilayers, suggesting that the underlying mechanism is the Dzyaloshinskii-Moriya interaction at the film interfaces. Our observations may open a new route to control chiral spin structures using interfacial engineering in transition metal heterostructures.

Aspects of passive magnetic levitation based on high-T(sub c) superconducting YBCO thin films

NASA Technical Reports Server (NTRS)

Schoenhuber, P.; Moon, F. C.

1995-01-01

Passive magnetic levitation systems reported in the past were mostly confined to bulk superconducting materials. Here we present fundamental studies on magnetic levitation employing cylindrical permanent magnets floating above high-T(sub c) superconducting YBCO thin films (thickness about 0.3 mu m). Experiments included free floating rotating magnets as well as well-established flexible beam methods. By means of the latter, we investigated levitation and drag force hysteresis as well as magnetic stiffness properties of the superconductor-magnet arrangement. In the case of vertical motion of the magnet, characteristic high symmetry of repulsive (approaching) and attractive (withdrawing) branches of the pronounced force-displacement hysteresis could be detected. Achievable force levels were low as expected but sufficient for levitation of permanent magnets. With regard to magnetic stiffness, thin films proved to show stiffness-force ratios about one order of magnitude higher than bulk materials. Phenomenological models support the measurements. Regarding the magnetic hysteresis of the superconductor, the Irie-Yamafuji model was used for solving the equation of force balance in cylindrical coordinates allowing for a macroscopic description of the superconductor magnetization. This procedure provided good agreement with experimental levitation force and stiffness data during vertical motion. For the case of (lateral) drag force basic qualitative characteristics could be recovered, too. It is shown that models, based on simple asymmetric magnetization of the superconductor, describe well asymptotic transition of drag forces after the change of the magnet motion direction. Virgin curves (starting from equilibrium, i.e. symmetric magnetization) are approximated by a linear approach already reported in literature only. This paper shows that basic properties of superconducting thin films allow for their application to magnetic levitation or - without need of levitation

Strain of optic-fiber/giant magnetostrictive film structure in magnetic field by finite element analysis

NASA Astrophysics Data System (ADS)

Hu, Jiafei; Pan, Mengchun; Xin, Jianguang; Chen, Dixiang

2008-12-01

The magnetostrictive transducer is the most important part of the optic-fiber magnetic field sensor, and the optic-fiber/giant magnetostrictive(GMS) film coupled structure is a novel coupling form of the magnetostrictive transducer. Always we analyze the coupled structure based on the entire coupled structure being sputtered GMS material without tail-fibers. In practical application, the coupled structure has tail-fibers without films at two ends. When the entire coupled structure is immersed in the detected magnetic field, the detected magnetic field causes the GMS film strain then causing optic-fiber strain. This strain transmission process is different from it in the coupled structure entirely with GMS films without tail-fibers. The strain transmission relationship can be calculated theoretically in the coupled structure without tail-fibers, but it's complicated to theoretically calculate the strain transmission relationship in the coupled structure with tail-fibers. After large numbers of calculations and analyses by ANSYS software, we figure out some relationships of the two strain transmission processes in the respective structures and the stress distribution in the tail-fibers. These results are helpful to the practical application of the optic-fiber/ GMS film coupled structure.

Microscopic theory of exchange and dipole-exchange spin waves in magnetic thin films

NASA Astrophysics Data System (ADS)

Pereira, Joao Milton, Jr.

The aim of this work is to develop a microscopic theory of bulk and surface spin wave modes (or magnons) in thin films of some specific ordered magnetic materials, particularly antiferromagnets. Both exchange and magnetic dipole-dipole interactions are taken into account, depending on the material and the wavevector regime. First we study the dispersion relations of spin waves for situations in which the dominant interaction is the short-range exchange coupling between the magnetic sites. We begin by investigating ferromagnetic films with a cubic body centered (b.c.c.) crystal structure a surfaces corresponding to (111) crystal planes. The spin wave frequencies are calculated by a method that generalizes previous techniques used for simpler systems, which allows us to find analytical solutions. The results are then compared with recent experimental data for Ni films grown epitaxially on a W substrate. Then we investigate spin waves in antiferromagnetic systems. Calculations are made for the dispersion relations of exchange-dominated spin waves in antiferromagnetic thin films with simple cubic (s.c.) crystal structures, for three different surface orientations, namely (001), (101) and (111). The results are obtained by using a method similar to the one developed for the ferromagnetic film in the previous chapter. We calculate the effect of finite film thickness in coupling the spin wave modes localized near the two surfaces, leading to a splitting of several of the mode branches that occur in the semi-infinite limit. Another aspect that we consider is the influence, for the (101) orientation, of the direction of propagation on the spin wave frequencies, as well as the effect of non-equivalent sublattices in the (111) case. Next, we investigate the spin waves in antiferromagnetic films made of materials in which the long-range dipole-dipole interaction between the magnetic sites is included, along with the exchange coupling. In this case, we employ a Hamiltonian

Interface effects in ultra-thin films: Magnetic and chemical properties

NASA Astrophysics Data System (ADS)

Park, Sungkyun

When the thickness of a magnetic layer is comparable to (or smaller than) the electron mean free path, the interface between magnetic and non-magnetic layers becomes very important factor to determine magnetic properties of the ultra-thin films. The quality of interface can enhance (or reduce) the desired properties. Several interesting physical phenomena were studied using these interface effects. The magnetic anisotropy of ultra-thin Co films is studied as function of non-magnetic underlayer thickness and non- magnetic overlayer materials using ex situ Brillouin light scattering (BLS). I observed that perpendicular magnetic anisotropy (PMA) increases with underlayer thickness and saturates after 5 ML. This saturation can be understood as a relaxation of the in-plane lattice parameter of Au(111) on top of Cu(111) to its bulk value. For the overlayer study, Cu, Al, and Au are used. An Au overlayer gives the largest PMA due to the largest in-plane lattice mismatch between Co and Au. An unusual effect was found by adding an additional layer on top of the Au overlayer. An additional Al capping layer on top of the Au overlayer reduces the PMA significantly. The possible explanation is that the misfit strain at the interface between the Al and the Au can be propagated through the Au layer to affect the magnetic properties of Co even though the in- plane lattice mismatch is less than 1%. Another interesting problem in interface interdiffusion and thermal stability in magnetic tunnel junction (MTJ) structures is studied using X-ray photoelectron spectroscopy (XPS). Since XPS is a very chemically sensitive technique, it allows us to monitor interface interdiffusion of the MTJ structures as-deposited and during post-deposition processing. For the plasma- oxidized samples, Fe only participates in the oxidation reduction process. In contrast to plasma-oxidized samples, there were no noticeable chemical shifts as- deposited and during post-deposition processing in air

Tailoring of Perpendicular Magnetic Anisotropy in Dy13Fe87 Thin Films with Hexagonal Antidot Lattice Nanostructure.

PubMed

Salaheldeen, Mohamed; Vega, Victor; Ibabe, Angel; Jaafar, Miriam; Asenjo, Agustina; Fernandez, Agustin; Prida, Victor M

2018-04-08

In this article, the magnetic properties of hexagonally ordered antidot arrays made of Dy 13 Fe 87 alloy are studied and compared with corresponding ones of continuous thin films with the same compositions and thicknesses, varying between 20 nm and 50 nm. Both samples, the continuous thin films and antidot arrays, were prepared by high vacuum e-beam evaporation of the alloy on the top-surface of glass and hexagonally self-ordered nanoporous alumina templates, which serve as substrates, respectively. By using a highly sensitive magneto-optical Kerr effect (MOKE) and vibrating sample magnetometer (VSM) measurements an interesting phenomenon has been observed, consisting in the easy magnetization axis transfer from a purely in-plane (INP) magnetic anisotropy to out-of-plane (OOP) magnetization. For the 30 nm film thickness we have measured the volume hysteresis loops by VSM with the easy magnetization axis lying along the OOP direction. Using magnetic force microscopy measurements (MFM), there is strong evidence to suggest that the formation of magnetic domains with OOP magnetization occurs in this sample. This phenomenon can be of high interest for the development of novel magnetic and magneto-optic perpendicular recording patterned media based on template-assisted deposition techniques.

Novel Magnetic Phenomena in Oxide Thin Films, Interfaces and Heterostructures

NASA Astrophysics Data System (ADS)

Venkatesan, Thirumalai

2015-03-01

Oxide films, heterostructures and interfaces present wonderful opportunities for exploring novel magnetic phenomena. The idea of cationic vacancy induced ferromagnetism was demonstrated by observing ferromagnetism in TaxTi1-xO2(x = 2 - 6%). Using XAS, XPS and XMCD, the magnetism was mainly located at the Ti sites and was shown to arise from Ti vacancies as opposed to Ti3+. The substrate-film interface was crucial for observing the ferromagnetism, as the required concentration of Ti vacancies could only be maintained close to the interface. With electron transport we were able to see with increasing thickness the emerging role of Kondo scattering (mediated by Ti3+) and at larger thickness impurity scattering. The polar LaAlO3/non-polar SrTiO3 interface exhibits a mixture of magnetic phases most likely arising from cationic defects and selective electron occupancy in Ti t2g levels. Using XMCD ferromagnetism was seen at these interfaces even at room temperature. Unlike LaAlO3, polar LaMnO3 is an insulator exhibiting orbital order that has a smaller band gap than SrTiO3. It is a traditional antiferromagnetic material, but when grown on SrTiO3, LaMnO3 exhibits ferromagnetism for film thicknesses exceeding 5 unit cells. This is discussed in terms of electronic reconstruction with polar charge transfer to the LaMnO3 side of the interface and also to the surface of the over layer. Novel magnetic coupling effects are seen in perovskite ferromagnets separated by a polar oxide layer such as LaAlO3 or NdGaO3, whereas non-polar oxides do not show the same effect. The coupling between the ferromagnetic layers oscillates in sign between FM and AFM, depending on the barrier thickness. Such coupling is totally unexpected in the absence of any itinerary electrons, with insulating barriers that are too thick for tunneling. The novel magnetic coupling is shown to be mediated by spin-orbit coupling and also magnetic excitation of defect levels in the polar oxide planes.

Atomic moments in Mn 2CoAl thin films analyzed by X-ray magnetic circular dichroism

DOE PAGES

Jamer, M. E.; Assaf, B. A.; Sterbinsky, G. E.; ...

2014-12-05

Spin gapless semiconductors are known to be strongly affected by structural disorder when grown epitaxially as thin films. The magnetic properties of Mn 2CoAl thin films grown on GaAs (001) substrates are investigated here as a function of annealing. This study investigates the atomic-specific magnetic moments of Mn and Co atoms measured through X-ray magnetic circular dichroism as a function of annealing and the consequent structural ordering. Results indicate that the structural distortion mainly affects the Mn atoms as seen by the reduction of the magnetic moment from its predicted value.

Increased magnetic damping in ultrathin films of Co2FeAl with perpendicular anisotropy

NASA Astrophysics Data System (ADS)

Takahashi, Y. K.; Miura, Y.; Choi, R.; Ohkubo, T.; Wen, Z. C.; Ishioka, K.; Mandal, R.; Medapalli, R.; Sukegawa, H.; Mitani, S.; Fullerton, E. E.; Hono, K.

2017-06-01

We estimated the magnetic damping constant α of Co2FeAl (CFA) Heusler alloy films of different thicknesses with an MgO capping layer by means of time-resolved magneto-optical Kerr effect and ferromagnetic resonance measurements. CFA films with thicknesses of 1.2 nm and below exhibited perpendicular magnetic anisotropy arising from the presence of the interface with MgO. While α increased gradually with decreasing CFA film thickness down to 1.2 nm, it was increased substantially when the thickness was reduced further to 1.0 nm. Based on the microstructure analyses and first-principles calculations, we attributed the origin of the large α in the ultrathin CFA film primarily to the Al deficiency in the CFA layer, which caused an increase in the density of states and thereby in the scatterings of their spins.