Role of intensive milling in the processing of barium ferrite/magnetite/iron hybrid magnetic nano-composites via partial reduction of barium ferrite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Molaei, M.J., E-mail: mj.molaee@merc.ac.ir; Delft Chem Tech, Faculty of Applied Sciences, Delft University of Technology, Julianalaan 136, 2628 BL Delft; Ataie, A.

2015-03-15

In this research a mixture of barium ferrite and graphite was milled for different periods of time and then heat treated at different temperatures. The effects of milling time and heat treatment temperature on the phase composition, thermal behavior, morphology and magnetic properties of the samples have been investigated using X-ray diffraction, differential thermal analysis, high resolution transmission electron microscopy and vibrating sample magnetometer techniques, respectively. X-ray diffraction results revealed that BaFe{sub 12}O{sub 19}/Fe{sub 3}O{sub 4} nanocomposites form after a 20 h milling due to the partial reduction of BaFe{sub 12}O{sub 19}. High resolution transmission electron microscope images of amore » 40 h milled sample showed agglomerated structure consisting of nanoparticles with a mean particle size of 30 nm. Thermal analysis of the samples via differential thermal analysis indicated that for un-milled samples, heat treatment up to 900 °C did not result in α-Fe formation, while for a 20 h milled sample heat treatment at 700 °C resulted in reduction process progress to the formation of α-Fe. Wustite was disappeared in an X-ray diffraction pattern of a heat treated sample at 850 °C, by increasing the milling time from 20 to 40 h. By increasing the milling time, the structure of heat treated samples becomes magnetically softer due to an increase in saturation magnetization and a decrease in coercivity. Saturation magnetization and coercivity of a sample milled for 20 h and heat treated at 850 °C were 126.3 emu/g and 149.5 Oe which by increasing the milling time to 40 h, alter to 169.1 emu/g and 24.3 Oe, respectively. High coercivity values of milled and heat treated samples were attributed to the nano-scale formed iron particles. - Graphical abstract: Display Omitted - Highlights: • Barium ferrite and graphite were treated mechano-thermally. • Increasing milling time increases reduction progress after heat treatment. • Composites including iron nano-crystals forms by milling and heat treatment. • Shorter milling time results in higher H{sub C} of the milled and heat treated samples.« less

Change in the color of heat-treated, vacuum-packed broccoli stems and florets during storage: effects of process conditions and modeling by an artificial neural network.

PubMed

Pero, Milad; Askari, Gholamreza; Skåra, Torstein; Skipnes, Dagbjørn; Kiani, Hossein

2018-02-08

Vacuum-packed broccoli stems and florets were subjected to heat treatment (60-99 °C) for various time intervals. The activity of peroxidase was measured after processing. Thermally processed samples were then stored at 4 °C for 35 days, and the color of the samples was measured every 7 days. Effects of parameters (heating temperature and duration, storage time) on the color of broccoli were modeled and simulated by an artificial neural network (ANN). Simulations confirmed that stems were predicted to be more prone to changes than florets. More color loss was observed with longer processing or storage combinations. The simulations also confirmed that higher temperatures during heat processing could retard color changes during storage. For stems treated at 80 °C for short durations, color loss was more predominant than both 65 and 99 °C, probably due to the incomplete inactivation of enzymes besides more tissue damage, with increased enzyme access to the substrate. The greenness of both stems and florets during storage can be better preserved at higher temperatures (99 °C) and short times. The simulation results revealed that the ANN method could be used as an effective tool for predicting and analyzing the color values of heat-treated broccoli. © 2018 Society of Chemical Industry. © 2018 Society of Chemical Industry.

Analysing the Friction Stir Welded Joints of AA2219 Al-Cu Alloy in Different Heat-Treated-State

NASA Astrophysics Data System (ADS)

Venkateswarlu, D.; Cheepu, Muralimohan; Kranthi kumar, B.; Mahapatra, M. M.

2018-03-01

Aluminium alloy AA2219 is widely used in light weight structural applications where the good corrosion resistance and specific weight required. The fabrication of this alloy using friction stir welding process is gaining interest towards finding the characteristics of the weld metal properties, since this process involved in the welded materials does not melt and recast. In the present investigation, friction stir welding process was used for different heat treated conditions of 2219-T87 and 2219-T62 aluminium alloys to find the influence of base metal on characteristics of the joints. The experimental output results exhibited that, mechanical properties, weld metal characteristics and joint failure locations are significantly affected by the different heat treatment conditions of the substrate. The joints tensile and yield strength of the 2219-T87 welds was higher than the 2219-T62 welds. Hardness distribution in the stir zone was significantly varied between two different heat treaded material conditions. The microstructural features of the 2219-T62 welds reveal the coarse grains formation in the thermo-mechanically affected zone and heat affected zone. The joint efficiency of the 2219- T82 welds is 59.87%, while that of 2219-T62 welds is 39.10%. In addition, the elongation of the joint also varied and the joints failure location characteristics are different for two different types heat treated condition joints.

Process of preparing metal parts to be heated by means of infrared radiance

DOEpatents

Mayer, Howard Robinson [Cincinnati, OH; Blue, Craig A [Knoxville, TN

2009-06-09

A method for preparing metal for heating by infrared radiance to enable uniform and consistent heating. The surface of one or more metal parts, such as aluminum or aluminum alloy parts, is treated to alter the surface finish to affect the reflectivity of the surface. The surface reflectivity is evaluated, such as by taking measurements at one or more points on the surface, to determine if a desired reflectivity has been achieved. The treating and measuring are performed until the measuring indicates that the desired reflectivity has been achieved. Once the treating has altered the surface finish to achieve the desired reflectivity, the metal part may then be exposed to infrared radiance to heat the metal part to a desired temperature, and that heating will be substantially consistent throughout by virtue of the desired reflectivity.

Plasma vitrification and re-use of non-combustible fiber reinforced plastic, gill net and waste glass.

PubMed

Chu, J P; Chen, Y T; Mahalingam, T; Tzeng, C C; Cheng, T W

2006-12-01

Fiber reinforced plastic (FRP) composite material has widespread use in general tank, special chemical tank and body of yacht, etc. The purpose of this study is directed towards the volume reduction of non-combustible FRP by thermal plasma and recycling of vitrified slag with specific procedures. In this study, we have employed three main wastes such as, FRP, gill net and waste glass. The thermal molten process was applied to treat vitrified slag at high temperatures whereas in the post-heat treatment vitrified slags were mixed with specific additive and ground into powder form and then heat treated at high temperatures. With a two-stage heat treatment, the treated sample was generated into four crystalline phases, cristobalite, albite, anorthite and wollastonite. Fine and relatively high dense structures with desirable properties were obtained for samples treated by the two-stage heating treatment. Good physical and mechanical properties were achieved after heat treatment, and this study reveals that our results could be comparable with the commercial products.

Process Design of Aluminum Tailor Heat Treated Blanks.

PubMed

Kahrimanidis, Alexander; Lechner, Michael; Degner, Julia; Wortberg, Daniel; Merklein, Marion

2015-12-09

In many industrials field, especially in the automotive sector, there is a trend toward lightweight constructions in order to reduce the weight and thereby the CO₂ and NO x emissions of the products. An auspicious approach within this context is the substitution of conventional deep drawing steel by precipitation hardenable aluminum alloys. However, based on the low formability, the application for complex stamping parts is challenging. Therefore, at the Institute of Manufacturing Technology, an innovative technology to enhance the forming limit of these lightweight materials was invented. The key idea of the so-called Tailor Heat Treated Blanks (THTB) is optimization of the mechanical properties by local heat treatment before the forming operation. An accurate description of material properties is crucial to predict the forming behavior of tailor heat treated blanks by simulation. Therefore, within in this research project, a holistic approach for the design of the THTB process in dependency of the main influencing parameters is presented and discussed in detail. The capability of the approach for the process development of complex forming operations is demonstrated by a comparison of local blank thickness of a tailgate with the corresponding results from simulation.

Process Design of Aluminum Tailor Heat Treated Blanks

PubMed Central

Kahrimanidis, Alexander; Lechner, Michael; Degner, Julia; Wortberg, Daniel; Merklein, Marion

2015-01-01

In many industrials field, especially in the automotive sector, there is a trend toward lightweight constructions in order to reduce the weight and thereby the CO2 and NOx emissions of the products. An auspicious approach within this context is the substitution of conventional deep drawing steel by precipitation hardenable aluminum alloys. However, based on the low formability, the application for complex stamping parts is challenging. Therefore, at the Institute of Manufacturing Technology, an innovative technology to enhance the forming limit of these lightweight materials was invented. The key idea of the so-called Tailor Heat Treated Blanks (THTB) is optimization of the mechanical properties by local heat treatment before the forming operation. An accurate description of material properties is crucial to predict the forming behavior of tailor heat treated blanks by simulation. Therefore, within in this research project, a holistic approach for the design of the THTB process in dependency of the main influencing parameters is presented and discussed in detail. The capability of the approach for the process development of complex forming operations is demonstrated by a comparison of local blank thickness of a tailgate with the corresponding results from simulation. PMID:28793727

Corrosion Behavior of Heat-Treated AlSi10Mg Manufactured by Laser Powder Bed Fusion.

PubMed

Cabrini, Marina; Calignano, Flaviana; Fino, Paolo; Lorenzi, Sergio; Lorusso, Massimo; Manfredi, Diego; Testa, Cristian; Pastore, Tommaso

2018-06-21

This experimental work is aimed at studying the effect of microstructural modifications induced by post-processing heat treatments on the corrosion behavior of silicon-aluminum alloys produced by means of laser powder bed fusion (LPBF). The manufacturing technique leads to microstructures characterized by the presence of melt pools, which are quite different compared to casting alloys. In this study, the behavior of an AlSi10Mg alloy was evaluated by means of intergranular corrosion tests according to ISO 11846 standard on heat-treated samples ranging from 200 to 500 °C as well as on untreated samples. We found that temperatures above 200 °C reduced microhardness of the alloy, and different corrosion morphologies occurred due to the modification of both size and distribution of silicon precipitates. Selective penetrating attacks occurred at melt pool borders. The intergranular corrosion phenomena were less intense for as-produced specimens without heat treatments compared to the heat-treated specimens at 200 and 300 °C. General corrosion morphologies were noticed for specimens heat treated at temperatures exceeding 400 °C.

A study of the impact of moist-heat and dry-heat treatment processes on hazardous trace elements migration in food waste.

PubMed

Chen, Ting; Jin, Yiying; Qiu, Xiaopeng; Chen, Xin

2015-03-01

Using laboratory experiments, the authors investigated the impact of dry-heat and moist-heat treatment processes on hazardous trace elements (As, Hg, Cd, Cr, and Pb) in food waste and explored their distribution patterns for three waste components: oil, aqueous, and solid components. The results indicated that an insignificant reduction of hazardous trace elements in heat-treated waste-0.61-14.29% after moist-heat treatment and 4.53-12.25% after dry-heat treatment-and a significant reduction in hazardous trace elements (except for Hg without external addition) after centrifugal dehydration (P < 0.5). Moreover, after heat treatment, over 90% of the hazardous trace elements in the waste were detected in the aqueous and solid components, whereas only a trace amount of hazardous trace elements was detected in the oil component (<0.01%). In addition, results indicated that heat treatment process did not significantly reduce the concentration of hazardous trace elements in food waste, but the separation process for solid and aqueous components, such as centrifugal dehydration, could reduce the risk considerably. Finally, combined with the separation technology for solid and liquid components, dry-heat treatment is superior to moist-heat treatment on the removal of external water-soluble ionic hazardous trace elements. An insignificant reduction of hazardous trace elements in heat-treated waste showed that heat treatment does not reduce trace elements contamination in food waste considerably, whereas the separation process for solid and aqueous components, such as centrifugal dehydration, could reduce the risk significantly. Moreover, combined with the separation technology for solid and liquid components, dry-heat treatment is superior to moist-heat treatment for the removal of external water-soluble ionic hazardous trace elements, by exploring distribution patterns of trace elements in three waste components: oil, aqueous, and solid components.

Influence of process fluids properties on component surface convective heat emission

NASA Astrophysics Data System (ADS)

Ivanova, T. N.; Korshunov, A. I.; Zavialov, P. M.

2018-03-01

When grinding with metal-working process fluid, a thin layer of inhibited liquid is formed between the component and the grinding wheel under the action of viscous forces. This can be defined as a hydrodynamic boundary layer or a thermal boundary layer. In this work, the thickness of the layers is studied depending on the viscosity of the fluid, inertia forces, velocity and pressure of the flow; also the causes of their occurrence are identified. It is established that under turbulent flow, the viscosity of the flow and the diffusion rate are much higher than in laminar flow, which also affects heat emission. Calculation of heat transfer in a single-phase chemically homogeneous medium of process liquids has shown that their properties, such as viscosity, thermal conductivity, density and heat capacity are of primary importance. The results of experimental studies of these characteristics are presented. When determining the heat transfer coefficient, functional correlations between the physical variables of the process fluid and the change in time and space have been established. As a result of the studies carried out to determine the heat transfer coefficient of a plate immersed in the process fluid, it is established that the intensification of the cooling process of the treated surface immersed in the coolant is more intense than with other methods of coolant supplying. An increase in the pulsation rate of the process liquid flow and the length of the flow displacement path leads to an increase in the heat transfer coefficient of the treated surface and a decrease in the temperature that arises during grinding.

Thermal and Mechanical Property Characterization of the Advanced Disk Alloy LSHR

NASA Technical Reports Server (NTRS)

Gabb, Timothy P.; Gayda, John; Telesman, Jack; Kantzos, Peter T.

2005-01-01

A low solvus, high refractory (LSHR) powder metallurgy disk alloy was recently designed using experimental screening and statistical modeling of composition and processing variables on sub-scale disks to have versatile processing-property capabilities for advanced disk applications. The objective of the present study was to produce a scaled-up disk and apply varied heat treat processes to enable full-scale demonstration of LSHR properties. Scaled-up disks were produced, heat treated, sectioned, and then machined into specimens for mechanical testing. Results indicate the LSHR alloy can be processed to produce fine and coarse grain microstructures with differing combinations of strength and time-dependent mechanical properties, for application at temperatures exceeding 1300 F.

Production of glass or glass-ceramic to metal seals with the application of pressure

DOEpatents

Kelly, Michael D.; Kramer, Daniel P.

1987-11-10

In a process for preparing a glass or glass-ceramic to metal seal comprising contacting the glass with the metal and heat-treating the glass and metal under conditions whereby the glass to metal seal is effected and, optionally, the glass is converted to a glass-ceramic, an improvement comprises carrying out the heat-treating step using hot isostatic pressing.

Production of glass or glass-ceramic to metal seals with the application of pressure

DOEpatents

Kelly, M.D.; Kramer, D.P.

1985-01-04

In a process for preparing a glass or glass-ceramic to metal seal comprising contacting the glass with the metal and heat-treating the glass and metal under conditions whereby the glass to metal seal is effected and, optionally, the glass is converted to a glass-ceramic, an improvement comprises carrying out the heat-treating step using hot isostatic pressing.

Processing of baby food using pressure-assisted thermal sterilization (PATS) and comparison with thermal treatment

NASA Astrophysics Data System (ADS)

Wang, Yubin; Ismail, Marliya; Farid, Mohammed

2017-10-01

Currently baby food is sterilized using retort processing that gives an extended shelf life. However, this type of heat processing leads to reduction of organoleptic and nutrition value. Alternatively, the combination of pressure and heat could be used to achieve sterilization at reduced temperatures. This study investigates the potential of pressure-assisted thermal sterilization (PATS) technology for baby food sterilization. Here, baby food (apple puree), inoculated with Bacillus subtilis spores was treated using PATS at different operating temperatures, pressures and times and was compared with thermal only treatment. The results revealed that the decimal reduction time of B. subtilis in PATS treatment was lower than that of thermal only treatment. At a similar spore inactivation, the retention of ascorbic acid of PATS-treated sample was higher than that of thermally treated sample. The results indicated that PATS could be a potential technology for baby food processing while minimizing quality deterioration.

Wear behavior of carbonitride-treated ploughshares produced from 30MnB5 steel for soil tillage applications

NASA Astrophysics Data System (ADS)

Yazici, A.

2011-09-01

The effects of gaseous carbonitriding processes on wear characteristics of 30MnB5 steel were investigated. The matrix of the carbonitride treated samples has a better wear resistance compared to the substrates of the conventionally heat-treated sample in laboratory conditions. The carbonitriding treatment condition giving rise to the lowest wear weight loss with the pin-on-disc wear machine was selected in order to harden ploughshare specimens to be tested in field experiments. The carbonitriding process at 860°C, with 0.9% C, and 0.6 m3/h NH3 for 105 min and quenched in 60°C oil followed by a 60 min tempering process at 140°C decreased 14.65% of total wear weight loss and 26.47% of total wear dimension loss of the ploughshare specimens in comparison to the conventional heat treatment process in field operational conditions.

Synthesis of Nanostructured Carbides of Titanium and Vanadium from Metal Oxides and Ferroalloys Through High-energy Mechanical Milling and Heat Treatment

NASA Astrophysics Data System (ADS)

Basu, P.; Jian, P. F.; Seong, K. Y.; Seng, G. S.; Masrom, A. K.; Hussain, Z.; Aziz, A.

2010-03-01

Carbides of Ti and V have been synthesized directly from their oxides and ferroalloys through mechanical milling and heat treatment. The powder mixtures are milled in a planetary ball mill from 15-80 hours and subsequently heat treated at 1000-1300° C for TiO2-C mixtures, at 500-550° C for V2O5-C mixtures and at 600-1000° C for (Fe-V)-C mixtures. The milled and heat treated powders are characterized by SEM, EDAX, XRD, and BET techniques. Nanostructured TiC has been successfully synthesized under suitable processing conditions. However, carbides of vanadium is unidentified even though possibilities of V2O5-C reaction are indicated with an extent of induced amorphism in the powder mixture. Density, specific surface area and particle size of the milled and heat treated mixtures are correlated with heat treatment temperatures. Similar attempts are also made to synthesize vanadium carbides from industrial grade Fe-V.

Structural changes in slenderized yak hair induced by heat-humidity conditions using Raman spectroscopy

NASA Astrophysics Data System (ADS)

Liu, H. L.; Zhao, B. Y.; Yu, W. D.

2013-04-01

In this study, estimation of structure was accomplished with the use of deconvolution, secondary derivation and curve-fitting. The structural changes of slenderized yak hair treated by heat-humidity conditions were quantified by analyzing the disulfide bond (S-S), amide I and amide III regions. The results showed that the amount of the disulphide bond in the yak hair decreases with the increase of treating time. The secondary structure of yak hair transforms from the α-helix and β pleated to the disordered conformation during the heat humidity processing.

New Nomenclatures for Heat Treatments of Additively Manufactured Titanium Alloys

NASA Astrophysics Data System (ADS)

Baker, Andrew H.; Collins, Peter C.; Williams, James C.

2017-07-01

The heat-treatment designations and microstructure nomenclatures for many structural metallic alloys were established for traditional metals processing, such as casting, hot rolling or forging. These terms do not necessarily apply for additively manufactured (i.e., three-dimensionally printed or "3D printed") metallic structures. The heat-treatment terminology for titanium alloys generally implies the heat-treatment temperatures and their sequence relative to a thermomechanical processing step (e.g., forging, rolling). These designations include: β-processing, α + β-processing, β-annealing, duplex annealing and mill annealing. Owing to the absence of a thermomechanical processing step, these traditional designations can pose a problem when titanium alloys are first produced via additive manufacturing, and then heat-treated. This communication proposes new nomenclatures for heat treatments of additively manufactured titanium alloys, and uses the distinct microstructural features to provide a correlation between traditional nomenclature and the proposed nomenclature.

Study of dynamical process of heat denaturation in optically trapped single microorganisms by near-infrared Raman spectroscopy

NASA Astrophysics Data System (ADS)

Xie, Changan; Li, Yong-qing; Tang, Wei; Newton, Ronald J.

2003-11-01

The development of laser traps has made it possible to investigate single cells and record real-time Raman spectra during a heat-denaturation process when the temperature of the surrounding medium is increased. Large changes in the phenylalanine band (1004 cm-1) of near-infrared spectra between living and heat-treated cells were observed in yeast and Escerichia coli and Enterobacter aerogenes bacteria. This change appears to reflect the change in environment of phenylalanine as proteins within the cells unfold as a result of increasing temperatures. As a comparison, we measured Raman spectra of native and heat-denatured solutions of bovine serum albumin proteins, and a similar change in the phenylalanine band of spectra was observed. In addition, we measured Raman spectra of native and heat-treated solutions of pure phenylalanine molecules; no observable difference in vibrational spectra was observed. These findings may make it possible to study conformational changes in proteins within single cells.

Glass ceramic toughened with tetragonal zirconia

DOEpatents

Keefer, K.D.

1984-02-10

A phase transformation-toughened glass ceramic and a process for making it are disclosed. A mixture of particulate network-forming oxide, network-modifying oxide, and zirconium oxide is heated to yield a homogeneous melt, and this melt is then heat treated to precipitate an appreciable quantity of tetragonal zirconia, which is retained at ambient temperature to form a phase transformation-toughened glass ceramic. Nuclearing agents and stabilizing agents may be added to the mixture to facilitate processing and improve the ceramic's properties. Preferably, the mixture is first melted at a temperature from 1200 to 1700/sup 0/C and is then heat-treated at a temperature within the range of 800 to 1200/sup 0/C in order to precipitate tetragonal ZrO/sub 2/. The composition, as well as the length and temperature of the heat treatment, must be carefully controlled to prevent solution of the precipitated tetragonal zirconia and subsequent conversion to the monoclinic phase.

Glass ceramic toughened with tetragonal zirconia

DOEpatents

Keefer, Keith D.; Michalske, Terry A.

1986-01-01

A phase transformation-toughened glass ceramic and a process for making it are disclosed. A mixture of particulate network-forming oxide, network-modifying oxide, and zirconium oxide is heated to yield a homogeneous melt, and this melt is then heat-treated to precipitate an appreciable quantity of tetragonal zirconia, which is retained at ambient temperature to form a phase transformation-toughened glass ceramic. Nucleating agents and stabilizing agents may be added to the mixture to facilitate processing and improve the ceramic's properties. Preferably, the mixture is first melted at a temperature from 1200.degree. to 1700.degree. C. and is then heat-treated at a temperature within the range of 800.degree. to 1200.degree. C. in order to precipitate tetragonal ZrO.sub.2. The composition, as well as the length and temperature of the heat-treatment, must be carefully controlled to prevent solution of the precipitated tetragonal zirconia and subsequent conversion to the monoclinic phase.

Compositions produced using an in situ heat treatment process

DOEpatents

Roes, Augustinus Wilhelmus Maria; Nair, Vijay; Munsterman, Erwin Hunh; Van Bergen, Petrus Franciscus; Van Den Berg, Franciscus Gondulfus Antonius

2013-05-28

Methods for treating a subsurface formation and compositions produced therefrom are described herein. At least one method for producing hydrocarbons from a subsurface formation includes providing heat to the subsurface formation using an in situ heat treatment process. One or more formation particles may be formed during heating of the subsurface formation. Fluid that includes hydrocarbons and the formation particles may be produced from the subsurface formation. The formation particles in the produced fluid may include cenospheres and have an average particle size of at least 0.5 micrometers.

Compositions produced using an in situ heat treatment process

DOEpatents

Roes, Augustinus Wilhelmus Maria [Houston, TX; Nair, Vijay [Katy, TX; Munsterman, Erwin Henh [Amsterdam, NL; Van Bergen, Petrus Franciscus [Amsterdam, NL; Van Den Berg, Franciscus Gondulfus Antonius

2009-10-20

Systems, methods, and heaters for treating a subsurface formation are described herein. At least one method for producing hydrocarbons from a subsurface formation includes providing heat to the subsurface formation using an in situ heat treatment process. One or more formation particles may be formed during heating of the subsurface formation. Fluid that includes hydrocarbons and the formation particles may be produced from the subsurface formation. The formation particles in the produced fluid may include cenospheres and have an average particle size of at least 0.5 micrometers.

Fabrication of a helical coil shape memory alloy actuator

NASA Astrophysics Data System (ADS)

Odonnell, R. E.

1992-02-01

A fabrication process was developed to form, heat treat, and join NiTi shape memory alloy helical coils for use as mechanical actuators. Tooling and procedures were developed to wind both extension and compression-type coils on a manual lathe. Heat treating fixtures and techniques were used to set the 'memory' of the NiTi alloy to the desired configuration. A swaging process was devised to fasten shape memory alloy extension coils to end fittings for use in actuator testing and for potential attachment to mechanical devices. The strength of this mechanical joint was evaluated.

Microwave Crystallization of Lithium Aluminum Germanium Phosphate Solid-State Electrolyte.

PubMed

Mahmoud, Morsi M; Cui, Yuantao; Rohde, Magnus; Ziebert, Carlos; Link, Guido; Seifert, Hans Juergen

2016-06-23

Lithium aluminum germanium phosphate (LAGP) glass-ceramics are considered as promising solid-state electrolytes for Li-ion batteries. LAGP glass was prepared via the regular conventional melt-quenching method. Thermal, chemical analyses and X-ray diffraction (XRD) were performed to characterize the prepared glass. The crystallization of the prepared LAGP glass was done using conventional heating and high frequency microwave (MW) processing. Thirty GHz microwave (MW) processing setup were used to convert the prepared LAGP glass into glass-ceramics and compared with the conventionally crystallized LAGP glass-ceramics that were heat-treated in an electric conventional furnace. The ionic conductivities of the LAGP samples obtained from the two different routes were measured using impedance spectroscopy. These samples were also characterized using XRD and scanning electron microscopy (SEM). Microwave processing was successfully used to crystallize LAGP glass into glass-ceramic without the aid of susceptors. The MW treated sample showed higher total, grains and grain boundary ionic conductivities values, lower activation energy and relatively larger-grained microstructure with less porosity compared to the corresponding conventionally treated sample at the same optimized heat-treatment conditions. The enhanced total, grains and grain boundary ionic conductivities values along with the reduced activation energy that were observed in the MW treated sample was considered as an experimental evidence for the existence of the microwave effect in LAGP crystallization process. MW processing is a promising candidate technology for the production of solid-state electrolytes for Li-ion battery.

Infiltration processing of boron carbide-, boron-, and boride-reactive metal cermets

DOEpatents

Halverson, Danny C.; Landingham, Richard L.

1988-01-01

A chemical pretreatment method is used to produce boron carbide-, boron-, and boride-reactive metal composites by an infiltration process. The boron carbide or other starting constituents, in powder form, are immersed in various alcohols, or other chemical agents, to change the surface chemistry of the starting constituents. The chemically treated starting constituents are consolidated into a porous ceramic precursor which is then infiltrated by molten aluminum or other metal by heating to wetting conditions. Chemical treatment of the starting constituents allows infiltration to full density. The infiltrated precursor is further heat treated to produce a tailorable microstructure. The process at low cost produces composites with improved characteristics, including increased toughness, strength.

Characterizing precipitate evolution of an Al–Zn–Mg–Cu-based commercial alloy during artificial aging and non-isothermal heat treatments by in situ electrical resistivity monitoring

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jiang, Fulin; Department of Materials Science and Engineering, McMaster University, 1280 Main Street West, Hamilton, Ontario L8S 4L7; Zurob, Hatem S., E-mail: zurobh@mcmaster.ca

In situ electrical resistivity monitoring technique was employed to continuously evaluate the precipitate evolution of an Al–Zn–Mg–Cu-based commercial alloy during typical artificial aging treatments. The effects of artificial aging on the precipitates stability during non-isothermal heat treatments were also explored. Conventional hardness test, transmission electron microscopy and differential scanning calorimetry were also adopted to verify the electrical resistivity results. The results indicated that both the precipitation process and its timely rate could be followed by the monitored electrical resistivity during artificial aging treatments. The electrical resistivity results gave overall information on continuous precipitation and dissolution processes, especially under high heatingmore » rates. Samples artificial aging heat treated at 120 °C for 24 h followed by aging at 150 °C for 24 h presented more stable state and coarser precipitates than the samples only artificial aging heat treated at 120 °C for 24 h or triple artificial aging heat treated at 120 °C/24 h + 195 °C/15 min + 120 °/24 h. While the incoherent η precipitates in the samples artificial aging heat treated at 120 °C for 24 h followed by aging at 150 °C for 24 h were more easiness to coarsening and dissolve during non-isothermal heat treatments as well. - Highlights: • In situ electrical resistivity monitoring technique was employed on an Al-Zn-Mg-Cu alloy. • The precipitate evolution during typical artificial aging treatments was studied. • The precipitate stability during non-isothermal heat treatments was explored. • The electrical resistivity wonderfully monitored continuous precipitation and dissolution. • The alloy submitted to a T7 treatment presents a more stable state during heating due to incoherent η precipitates.« less

Heat-treating of materials

NASA Technical Reports Server (NTRS)

Widener, Edward L.

1992-01-01

The objective was to introduce those solid state transformations of material structures known as 'heat treatments' and to emphasize the commercial importance of common processes for metals as well as non-metals. Experimental procedures are explained for annealing, quenching, hardening, and temper.

No major differences found between the effects of microwave-based and conventional heat treatment methods on two different liquid foods.

PubMed

Géczi, Gábor; Horváth, Márk; Kaszab, Tímea; Alemany, Gonzalo Garnacho

2013-01-01

Extension of shelf life and preservation of products are both very important for the food industry. However, just as with other processes, speed and higher manufacturing performance are also beneficial. Although microwave heating is utilized in a number of industrial processes, there are many unanswered questions about its effects on foods. Here we analyze whether the effects of microwave heating with continuous flow are equivalent to those of traditional heat transfer methods. In our study, the effects of heating of liquid foods by conventional and continuous flow microwave heating were studied. Among other properties, we compared the stability of the liquid foods between the two heat treatments. Our goal was to determine whether the continuous flow microwave heating and the conventional heating methods have the same effects on the liquid foods, and, therefore, whether microwave heat treatment can effectively replace conventional heat treatments. We have compared the colour, separation phenomena of the samples treated by different methods. For milk, we also monitored the total viable cell count, for orange juice, vitamin C contents in addition to the taste of the product by sensory analysis. The majority of the results indicate that the circulating coil microwave method used here is equivalent to the conventional heating method based on thermal conduction and convection. However, some results in the analysis of the milk samples show clear differences between heat transfer methods. According to our results, the colour parameters (lightness, red-green and blue-yellow values) of the microwave treated samples differed not only from the untreated control, but also from the traditional heat treated samples. The differences are visually undetectable, however, they become evident through analytical measurement with spectrophotometer. This finding suggests that besides thermal effects, microwave-based food treatment can alter product properties in other ways as well.

No Major Differences Found between the Effects of Microwave-Based and Conventional Heat Treatment Methods on Two Different Liquid Foods

PubMed Central

Géczi, Gábor; Horváth, Márk; Kaszab, Tímea; Alemany, Gonzalo Garnacho

2013-01-01

Extension of shelf life and preservation of products are both very important for the food industry. However, just as with other processes, speed and higher manufacturing performance are also beneficial. Although microwave heating is utilized in a number of industrial processes, there are many unanswered questions about its effects on foods. Here we analyze whether the effects of microwave heating with continuous flow are equivalent to those of traditional heat transfer methods. In our study, the effects of heating of liquid foods by conventional and continuous flow microwave heating were studied. Among other properties, we compared the stability of the liquid foods between the two heat treatments. Our goal was to determine whether the continuous flow microwave heating and the conventional heating methods have the same effects on the liquid foods, and, therefore, whether microwave heat treatment can effectively replace conventional heat treatments. We have compared the colour, separation phenomena of the samples treated by different methods. For milk, we also monitored the total viable cell count, for orange juice, vitamin C contents in addition to the taste of the product by sensory analysis. The majority of the results indicate that the circulating coil microwave method used here is equivalent to the conventional heating method based on thermal conduction and convection. However, some results in the analysis of the milk samples show clear differences between heat transfer methods. According to our results, the colour parameters (lightness, red-green and blue-yellow values) of the microwave treated samples differed not only from the untreated control, but also from the traditional heat treated samples. The differences are visually undetectable, however, they become evident through analytical measurement with spectrophotometer. This finding suggests that besides thermal effects, microwave-based food treatment can alter product properties in other ways as well. PMID:23341982

Improvement of Electropolishing of 1100 Al Alloy for Solar Thermal Applications

NASA Astrophysics Data System (ADS)

Aguilar-Sierra, Sara María; Echeverría E, Félix

2018-03-01

Aluminum sheets-based mirrors are finding applicability in high-temperature solar concentrating technologies because they are cost-effective, lightweight and have high mechanical properties. Nonetheless, the reflectance percentages obtained by electropolishing are not close to the reflectance values of the currently used evaporated films. Therefore, controlling key factors affecting electropolishing processes became essential in order to achieve highly reflective aluminum surfaces. This study investigated the effect of both the electropolishing process and previous heat treatment on the total reflectance of the AA 1100 aluminum alloy. An acid electrolyte and a modified Brytal process were evaluated. Total reflectance was measured by means of UV-Vis spectrophotometry. Reflectance values higher than 80% at 600 nm were achieved for both electrolytes. Optical microscopy and scanning electron microscopy images showed uneven dissolution for the acid electropolished samples causing a reflectance drop in the 200-450 nm region. The influence of heat treatment, previously to electropolishing, was tested at two different temperatures and various holding times. It was found that reflectance increases around 15% for the heat-treated and electropolished samples versus the non-heat-treated ones. A heat treatment at low temperature combined with a short holding time was enough to improve the sample total reflectance.

10 CFR 71.119 - Control of special processes.

Code of Federal Regulations, 2010 CFR

2010-01-01

... shall establish measures to assure that special processes, including welding, heat treating, and nondestructive testing are controlled and accomplished by qualified personnel using qualified procedures in...

Two-step sulfonation process for the conversion of polymer fibers to carbon fibers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Barton, Bryan E.; Patton, Jasson T.; Hukkanen, Eric J.

Disclosed herein are processes for preparing carbon fibers, comprising: sulfonating a polymer fiber with a sulfonating agent that is fuming sulfuric acid, sulfuric acid, chlorosulfonic acid, or a combination thereof; treating the sulfonated polymer with a heated solvent, wherein the temperature of the heated solvent is at least 95.degree. C.; and carbonizing the resulting product by heating it to a temperature of 501-3000.degree. C. Carbon fibers prepared according to these methods are also disclosed herein.

Final Technical Report: Intensive Quenching Technology for Heat Treating and Forging Industries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aronov, Michael A.

2005-12-21

Intensive quenching (IQ) process is an alternative way of hardening (quenching) steel parts through the use of highly agitated water and then still air. It was developed by IQ Technologies, Inc. (IQT) of Akron, Ohio. While conventional quenching is usually performed in environmentally unfriendly oil or water/polymer solutions, the IQ process uses highly agitated environmentally friendly water or low concentration water/mineral salt solutions. The IQ method is characterized by extremely high cooling rates of steel parts. In contrast to conventional quenching, where parts cool down to the quenchant temperature and usually have tensile or neutral residual surface stresses at themore » end of quenching. The IQ process is interrupted when the part core is still hot and when there are maximum compressive stresses deep into the parts, thereby providing hard, ductile, better wear resistant parts. The project goal was to advance the patented IQ process from feasibility to commercialization in the heat-treating and forging industries to reduce significantly energy consumption and environmental impact, to increase productivity and to enhance economic competitiveness of these industries as well as Steel, Metal Casting and Mining industries. To introduce successfully the IQ technology in the U.S. metal working industry, the project team has completed the following work over the course of this project: A total of 33 manufacturers of steel products provided steel parts for IQ trails. IQT conducted IQ demonstrations for 34 different steel parts. Our customers tested intensively quenched parts in actual field conditions to evaluate the product service life and performance improvement. The data obtained from the field showed the following: Service life (number of holes punched) of cold-work punches (provided by EHT customer and made of S5 shock-resisting steel) was improved by two to eight times. Aluminum extrusion dies provided by GAM and made of hot work H-13 steel outperformed the standard dies by at least 50%. Dies provided by an AST customer, made of plain carbon 1045 steel and used for pellet manufacturing outperformed the standard dies by more than 100%. Concrete crusher liner wear plates provided by an EHT customer and made of 1045 steel, had the same surface hardness as the plates made of more expensive, pre-hardened high alloy HARDOX-500 material supplied by a Swedish company and used currently by the EHT customer. The 1045 material intensively quenched wear plates are currently in the field. Concrete block molding machine wear plates provided by an IQT customer and made of 8620 steel were processed at the AST production IQ system using a 40% reduced carburization cycle. An effective case depth in the intensively quenched wear plates was the same as in the standard, oil quenched parts. Base keys provided by an EHT customer and made of 8620 steel were processed using a 40% reduced carburization cycle. The intensively quenched parts showed the same performance as standard parts. IQT introduced the IQ process in heat treat practices of three commercial heat-treating shops: Akron Steel Treating Co., Summit Heat Treating Co. and Euclid Heat Treating Co. CWRU conducted a material characterization study for a variety of steels to develop a database to support changing/modification of recognized standards for quenching steel parts. IQT conducted a series of IQ workshops, published seven technical papers and participated in ASM Heat Treating Society conference and exposition and in Furnace North America Show. IQT designed and built a fully automated new IQ system installed at the Center for Intensive Quenching. This system includes the following major components: a stand-alone 1,900-gallon IQ water system, a 24'' x 24'' atmosphere pit furnace, and an automated load transfer mechanism. IQT established a ''Center for Intensive Quenching'' at the AST facilities. The 4,000 square feet Center includes the following equipment: High-velocity single part quenching IQ unit developed and built previously under EMTEC CT-65 project. The unit is equipped with a neutral salt bath furnace and a high-temperature, electric-fired, atmosphere, box furnace. New 1,900 gallon IQ system with a 24'' x 24'' atmosphere pit furnace and a load transfer mechanism. Shaker hearth furnace equipped with an IQ water tank and with a chiller to maintain the required water temperature. Potential Savings for USA Heat Treating Industry IQ Process Benefit/Annual Benefit for USA Heat Treating Industry Full elimination or 30% reduction of the carburization cycle Savings of 1,800 billion Btu of energy Cost reduction by $600,000,000 Reduction of CO2 emissions by 148,000 ton Part weight reduction by 5% Savings in material cost of $70,000,000 Savings of 300 billion Btu of energy« less

Forging of Advanced Disk Alloy LSHR

NASA Technical Reports Server (NTRS)

Gabb, Timothy P.; Gayda, John; Falsey, John

2005-01-01

The powder metallurgy disk alloy LSHR was designed with a relatively low gamma precipitate solvus temperature and high refractory element content to allow versatile heat treatment processing combined with high tensile, creep and fatigue properties. Grain size can be chiefly controlled through proper selection of solution heat treatment temperatures relative to the gamma precipitate solvus temperature. However, forging process conditions can also significantly influence solution heat treatment-grain size response. Therefore, it is necessary to understand the relationships between forging process conditions and the eventual grain size of solution heat treated material. A series of forging experiments were performed with subsequent subsolvus and supersolvus heat treatments, in search of suitable forging conditions for producing uniform fine grain and coarse grain microstructures. Subsolvus, supersolvus, and combined subsolvus plus supersolvus heat treatments were then applied. Forging and subsequent heat treatment conditions were identified allowing uniform fine and coarse grain microstructures.

Electromagnetic bonding of plastics to aluminum

NASA Technical Reports Server (NTRS)

Sheppard, A. T.; Silbert, L.

1980-01-01

Electromagnetic curing is used to bond strain gage to aluminum tensile bar. Electromagnetic energy heats only plastic/metal interface by means of skin effect, preventing degradation of heat-treated aluminum. Process can be easily applied to other metals joined by high-temperature-curing plastic adhesives.

Optical absorption and TEM studies of silver nanoparticle embedded BaO-CaF{sub 2}-P{sub 2}O{sub 5} glasses

DOE Office of Scientific and Technical Information (OSTI.GOV)

Narayanan, Manoj Kumar, E-mail: manukokkal01@gmail.com; Shashikala, H. D.

Silver nanoparticle embedded 30BaO-20CaF{sub 2}-50P{sub 2}O{sub 5}-4Ag{sub 2}O-4SnO glasses were prepared by melt-quenching and subsequent heat treatment process. Silver-doped glasses were heat treated at temperatures 500 °C, 525°C and 550 °C for a fixed duration of 10 hours to incorporate metal nanoparticles into the glass matrix. Appearance and shift in peak positions of the surface plasmon resonance (SPR) bands in the optical absorption spectra of heat treated glass samples indicated that both formation and growth of nanoparticle depended on heat treatment temperature. Glass sample heat treated at 525 °C showed a SPR peak around 3 eV, which indicated that sphericalmore » nanoparticles smaller than 20 nm were formed inside the glass matrix. Whereas sample heat treated at 550 °C showed a size dependent red shift in SPR peak due to the presence of silver nanoparticles of size larger than 20 nm. Size of the nanoparticles calculated using full-width at half-maximum (FWHM) of absorption band showed a good agreement with the particle size obtained from transmission electron microscopy (TEM) analysis.« less

10 CFR 72.158 - Control of special processes.

Code of Federal Regulations, 2010 CFR

2010-01-01

..., and applicant for a CoC shall establish measures to ensure that special processes, including welding, heat treating, and nondestructive testing, are controlled and accomplished by qualified personnel using...

Improvement of the energy conversion efficiency of Chlorella pyrenoidosa biomass by a three-stage process comprising dark fermentation, photofermentation, and methanogenesis.

PubMed

Xia, Ao; Cheng, Jun; Ding, Lingkan; Lin, Richen; Huang, Rui; Zhou, Junhu; Cen, Kefa

2013-10-01

The effects of pre-treatment methods on saccharification and hydrogen fermentation of Chlorella pyrenoidosa biomass were investigated. When raw biomass and biomass pre-treated by steam heating, by microwave heating, and by ultrasonication were used as feedstock, the hydrogen yields were only 8.8-12.7 ml/g total volatile solids (TVS) during dark fermentation. When biomass was pre-treated by steam heating with diluted acid and by microwave heating with diluted acid, the dark hydrogen yields significantly increased to 75.6 ml/g TVS and 83.3 ml/g TVS, respectively. Steam heating with diluted acid is the preferred pre-treatment method of C. pyrenoidosa biomass to improve hydrogen yield during dark fermentation and photofermentation, which is followed by methanogenesis to increase energy conversion efficiency (ECE). A total hydrogen yield of 198.3 ml/g TVS and a methane yield of 186.2 ml/g TVS corresponding to an overall ECE of 34.0% were obtained through the three-stage process (dark fermentation, photofermentation, and methanogenesis). Copyright © 2013 Elsevier Ltd. All rights reserved.

Effect of Graphitic Content on Carbon Supported Catalyst Performance

DOE Office of Scientific and Technical Information (OSTI.GOV)

Patel, Anant; Artyushkova, Kateryna; Atanassov, Plamen

2011-07-01

The effect of graphitic content on carbon supported platinum catalysts was investigated in order to investigate its influence on catalyst performance. Four catalysts of varying surface areas and graphitic content were analyzed using XPS, HREELS, and tested using RDE experiments. The catalysts were also heat treated at 150oC and 100%RH as means to uniformly age them. The heat treated samples were analyzed using the same methods to determine what changes had occurred due to this aging process. When compared to the BOL catalysts, heat treated catalysts displayed increased graphitic carbon and platinum metalic content, however they also showed depressed catalyticmore » activity. The primary cause is still under investigation, though it is believed to be related to loss of amorphous carbon content.« less

Laser heat treatment of welds for various stainless steels

NASA Astrophysics Data System (ADS)

Dontu, O.; Ganatsios, S.; Alexandrescu, N.; Predescu, C.

2008-03-01

The paper presents a study concerning the post - weld heat treatment of a duplex stainless steel. Welded joint samples were surface - treated using the same laser source adopted during welding in order to counterbalance the excess of ferrite formed in the welding process.

Mechanical Properties of a Superalloy Disk with a Dual Grain Structure

NASA Technical Reports Server (NTRS)

Gayda, John; Gabb, Timothy; Kantzos, Peter

2003-01-01

Mechanical properties from an advanced, nickel-base superalloy disk, with a dual grain structure consisting of a fine grain bore and coarse grain rim, were evaluated. The dual grain structure was produced using NASA's low cost Dual Microstructure Heat Treatment (DMHT) process. The results showed the DMHT disk to have a high strength, fatigue resistant bore comparable to a subsolvus (fine grain) heat treated disk, and a creep resistant rim comparable to a supersolvus (coarse grain) heat treated disk. Additional work on subsolvus solutioning before or after the DMHT conversion appears to be a viable avenue for further improvement in disk properties.

Marangoni Convection during Free Electron Laser Nitriding of Titanium

NASA Astrophysics Data System (ADS)

Höche, Daniel; Müller, Sven; Rapin, Gerd; Shinn, Michelle; Remdt, Elvira; Gubisch, Maik; Schaaf, Peter

2009-08-01

Pure titanium was treated by free electron laser (FEL) radiation in a nitrogen atmosphere. As a result, nitrogen diffusion occurs and a TiN coating was synthesized. Local gradients of interfacial tension due to the local heating lead to a Marangoni convection, which determines the track properties. Because of the experimental inaccessibility of time-dependent occurrences, finite element calculations were performed, to determine the physical processes such as heat transfer, melt flow, and mass transport. In order to calculate the surface deformation of the gas-liquid interface, the level set approach was used. The equations were modified and coupled with heat-transfer and diffusion equations. The process was characterized by dimensionless numbers such as the Reynolds, Peclet, and capillary numbers, to obtain more information about the acting forces and the coating development. Moreover, the nitrogen distribution was calculated using the corresponding transport equation. The simulations were compared with cross-sectional micrographs of the treated titanium sheets and checked for their validity. Finally, the process presented is discussed and compared with similar laser treatments.

Upgrading of consumer characteristics of granulated solid fuel from mixture of low-grade coal and biomass

NASA Astrophysics Data System (ADS)

Kuzmina, J. S.; Milovanov, O. Yu; Sinelshchikov, V. A.; Sytchev, G. A.; Zaichenko, V. M.

2015-11-01

Effect of torrefaction on consumer characteristics of fuel pellets made of low-grade and agricultural waste is shown. Data on the volatile content, ash content, calorific value and hygroscopicity for initial pellets and pellets, heat-treated at various temperatures are presented. The experimental study of the combustion process of initial and heat-treated pellets showed that torrefaction of pellets leads to a decreasing of the ignition temperature and an increasing of the efficiency of boiler plant.

Process for preparing metal-carbide-containing microspheres from metal-loaded resin beads

DOEpatents

Beatty, Ronald L.

1976-01-01

An improved method for treating metal-loaded resin microspheres is described which comprises heating a metal-loaded resin charge in an inert atmosphere at a pre-carbide-forming temperature under such conditions as to produce a microsphere composition having sufficient carbon as to create a substantially continuous carbon matrix and a metal-carbide or an oxide-carbide mixture as a dispersed phase(s) during carbide-forming conditions, and then heating the thus treated charge to a carbide-forming temperature.

Drying and heat decomposition of biomass during the production of biochar

NASA Astrophysics Data System (ADS)

Lyubov, V. K.; Popova, E. I.

2017-11-01

The process of wood torrefaction provides an opportunity to combine properties of biofuel and steam coal. Different degrees of biofuel heat treating leads to varied outcomes and varied biochar heating value. Therefore, the torrefaction process requires optimal operation that ensures the highest heating value of biochar with the lowest energy loss. In this paper we present the experimental results of drying cycle and thermal decomposition of particles of spruce stem wood and hydrolytic lignin in argon under various temperature conditions and basic material humidity as well as changes in the morphological structure of the biomass and its grain size composition during the torrefaction.

Processes for preparing carbon fibers using gaseous sulfur trioxide

DOEpatents

Barton, Bryan E.; Lysenko, Zenon; Bernius, Mark T.; Hukkanen, Eric J.

2016-01-05

Disclosed herein are processes for preparing carbonized polymers, such as carbon fibers, comprising: sulfonating a polymer with a sulfonating agent that comprises SO.sub.3 gas to form a sulfonated polymer; treating the sulfonated polymer with a heated solvent, wherein the temperature of said solvent is at least 95.degree. C.; and carbonizing the resulting product by heating it to a temperature of 500-3000.degree. C.

Effects of annealing heat treatment on the corrosion resistance of Zn/Mg/Zn multilayer coatings

NASA Astrophysics Data System (ADS)

Bae, KiTae; La, JoungHyun; Lee, InGyu; Lee, SangYul; Nam, KyungHoon

2017-05-01

Zn coatings alloyed with magnesium offer superior corrosion resistance compared to pure Zn or other Zn-based alloy coatings. In this study, Zn/Mg/Zn multilayer coatings with various Mg layer thicknesses were synthesized using an unbalanced magnetron sputtering process and were annealed to form Zn-Mg intermetallic phases. The effects of the annealing heat treatment on the corrosion resistance of the Zn/Mg/Zn multilayer coatings were evaluated using electrochemical measurements. The extensive diffusion of magnesium species into the upper and lower zinc layer from the magnesium layer in the middle of the coating was observed after the heat treatment. This phenomenon caused (a) the porous microstructure to transition into a dense structure and (b) the formation of a MgZn2 intermetallic phase. The results of the electrochemical measurements demonstrated that the heat treated Zn/Mg/Zn multilayer coatings possessed higher levels of corrosion resistance than the non-heat treated coatings. A Zn/Mg/Zn multilayer coating with MgZn2 and (Zn) phases showed the best corrosion resistance among the heat treated coatings, which could be attributed to the reduced galvanic corrosion effects due to a small potential gradient between the MgZn2 and zinc.

Method for producing catalysis from coal

DOEpatents

Farcasiu, Malvina; Derbyshire, Frank; Kaufman, Phillip B.; Jagtoyen, Marit

1998-01-01

A method for producing catalysts from coal is provided comprising mixing an aqueous alkali solution with the coal, heating the aqueous mixture to treat the coal, drying the now-heated aqueous mixture, reheating the mixture to form carbonized material, cooling the mixture, removing excess alkali from the carbonized material, and recovering the carbonized material, wherein the entire process is carried out in controlled atmospheres, and the carbonized material is a hydrocracking or hydrodehalogenation catalyst for liquid phase reactions. The invention also provides for a one-step method for producing catalysts from coal comprising mixing an aqueous alkali solution with the coal to create a mixture, heating the aqueous mixture from an ambient temperature to a predetermined temperature at a predetermined rate, cooling the mixture, and washing the mixture to remove excess alkali from the treated and carbonized material, wherein the entire process is carried out in a controlled atmosphere.

Method for producing catalysts from coal

DOEpatents

Farcasiu, M.; Derbyshire, F.; Kaufman, P.B.; Jagtoyen, M.

1998-02-24

A method for producing catalysts from coal is provided comprising mixing an aqueous alkali solution with the coal, heating the aqueous mixture to treat the coal, drying the now-heated aqueous mixture, reheating the mixture to form carbonized material, cooling the mixture, removing excess alkali from the carbonized material, and recovering the carbonized material, wherein the entire process is carried out in controlled atmospheres, and the carbonized material is a hydrocracking or hydrodehalogenation catalyst for liquid phase reactions. The invention also provides for a one-step method for producing catalysts from coal comprising mixing an aqueous alkali solution with the coal to create a mixture, heating the aqueous mixture from an ambient temperature to a predetermined temperature at a predetermined rate, cooling the mixture, and washing the mixture to remove excess alkali from the treated and carbonized material, wherein the entire process is carried out in a controlled atmosphere. 1 fig.

A RSM-based predictive model to characterize heat treating parameters of D2 steel using combined Barkhausen noise and hysteresis loop methods

NASA Astrophysics Data System (ADS)

Kahrobaee, Saeed; Hejazi, Taha-Hossein

2017-07-01

Austenitizing and tempering temperatures are the effective characteristics in heat treating process of AISI D2 tool steel. Therefore, controlling them enables the heat treatment process to be designed more accurately which results in more balanced mechanical properties. The aim of this work is to develop a multiresponse predictive model that enables finding these characteristics based on nondestructive tests by a set of parameters of the magnetic Barkhausen noise technique and hysteresis loop method. To produce various microstructural changes, identical specimens from the AISI D2 steel sheet were austenitized in the range 1025-1130 °C, for 30 min, oil-quenched and finally tempered at various temperatures between 200 °C and 650 °C. A set of nondestructive data have been gathered based on general factorial design of experiments and used for training and testing the multiple response surface model. Finally, an optimization model has been proposed to achieve minimal error prediction. Results revealed that applying Barkhausen and hysteresis loop methods, simultaneously, coupling to the multiresponse model, has a potential to be used as a reliable and accurate nondestructive tool for predicting austenitizing and tempering temperatures (which, in turn, led to characterizing the microstructural changes) of the parts with unknown heat treating conditions.

Emergence of a fluctuation relation for heat in nonequilibrium Landauer processes

NASA Astrophysics Data System (ADS)

Taranto, Philip; Modi, Kavan; Pollock, Felix A.

2018-05-01

In a generalized framework for the Landauer erasure protocol, we study bounds on the heat dissipated in typical nonequilibrium quantum processes. In contrast to thermodynamic processes, quantum fluctuations are not suppressed in the nonequilibrium regime and cannot be ignored, making such processes difficult to understand and treat. Here we derive an emergent fluctuation relation that virtually guarantees the average heat produced to be dissipated into the reservoir either when the system or reservoir is large (or both) or when the temperature is high. The implication of our result is that for nonequilibrium processes, heat fluctuations away from its average value are suppressed independently of the underlying dynamics exponentially quickly in the dimension of the larger subsystem and linearly in the inverse temperature. We achieve these results by generalizing a concentration of measure relation for subsystem states to the case where the global state is mixed.

Energy Savings by Treating Buildings as Systems

NASA Astrophysics Data System (ADS)

Harvey, L. D. Danny

2008-09-01

This paper reviews the opportunities for dramatically reducing energy use in buildings by treating buildings as systems, rather than focusing on device efficiencies. Systems-level considerations are relevant for the operation of heat pumps (where the temperatures at which heat or coldness are distributed are particularly important); the joint or separate provision of heating, cooling, and ventilation; the joint or separate removal of sensible heat and moisture; and in the operation of fluid systems having pumps. Passive heating, cooling, and ventilation, as well as daylighting (use of sunlight for lighting purposes) also require consideration of buildings as systems. In order to achieve the significant (50-75%) energy savings that are possible through a systems approach, the design process itself has to involve a high degree of integration between the architect and various engineering disciplines (structural, mechanical, electrical), and requires the systematic examination and adjustment of alternative designs using computer simulation models.

Characterization and processing of heat treated aluminium matrix composite

NASA Astrophysics Data System (ADS)

Doifode, Yogesh; Kulkarni, S. G.

2018-05-01

The present study is carried out to determine density and porosity of Aluminium bagasse ash reinforced composite produced by powder metallurgy method. Bagasse ash is used as reinforcement material having high silica and alumina contents and varied from 5 weight % to 40 weight%. The manufactured composite is heat treated, the main objective of heat treatment is to prepare the material structurally and physically fit for engineering application. The results showed that the density decreases with percentage increase in reinforcement of bagasse ash from 2.6618 gm/cm3 to 1.9830 gm/cm3 with the minimum value at 40 weight% bagasse ash without heat treatment whereas after heat treatment density of composite increases due filling up of voids and porous holes. Heat treatment processing is the key to this improvement, with the T6 heat treated composite to convene the reduced porosity of composite. Consequently aluminium metal matrix composite combines the strength of the reinforcement to achieve a combination of desirable properties not available in any single material. It may observe that porosity in case of powder metallurgy samples showed more porosity portions compare to the casting samples. In order to achieve optimality in structure and properties of Bagasse ash-reinforcement heat treatment techniques have evolved. Generally, the ceramic reinforcements increase the density of the base alloy during fabrication of composites. However, the addition of lightweight reinforcements reduces the density of the hybrid composites. The results also showed that, the density varies from to with minimum value at 40 wt. % BA. The results of the statistical analysis showed that there are significant differences among the means of each property of the composites at various levels of BA replacement .It was concluded that bagasse ash can be used as reinforcement and the produced composites have low density and heat treatment reduces porosity which could be used in automobile industry for the production of engine parts.

Survival and Heat Resistance of Listeria monocytogenes after Exposure to Alkali and Chlorine

PubMed Central

Taormina, P. J.; Beuchat, L. R.

2001-01-01

A strain of Listeria monocytogenes isolated from a drain in a food-processing plant was demonstrated, by determination of D values, to be more resistant to the lethal effect of heat at 56 or 59°C following incubation for 45 min in tryptose phosphate broth (TPB) at pH 12.0 than to that of incubation for the same time in TPB at pH 7.3. Cells survived for at least 6 days when they were suspended in TPB at pHs 9.0, 10.0, and 11.0 and stored at 4 or 21°C. Cells of L. monocytogenes incubated at 37°C for 45 min and then stored for 48 or 144 h in TPB at pH 10.0 were more resistant to heat treatment at 56°C than were cells stored in TPB at pH 7.3. The alkaline-stress response in L. monocytogenes may induce resistance to otherwise lethal thermal-processing conditions. Treatment of cells in 0.05 M potassium phosphate buffer (pH 7.00 ± 0.05) containing 2.0 or 2.4 mg of free chlorine per liter reduced populations by as much as 1.3 log10 CFU/ml, while treatment with 6.0 mg of free chlorine per liter reduced populations by as much as 4.02 log10 CFU/ml. Remaining subpopulations of chlorine-treated cells exhibited some injury, and cells treated with chlorine for 10 min were more sensitive to heating at 56°C than cells treated for 5 min. Contamination of foods by L. monocytogenes cells that have survived exposure to processing environments ineffectively cleaned or sanitized with alkaline detergents or disinfectants may have more severe implications than previously recognized. Alkaline-pH-induced cross-protection of L. monocytogenes against heat has the potential to enhance survival in minimally processed as well as in heat-and-serve foods and in foods on holding tables, in food service facilities, and in the home. Cells surviving exposure to chlorine, in contrast, are more sensitive to heat; thus, the effectiveness of thermal processing in achieving desired log10-unit reductions is not compromised in these cells. PMID:11375163

10 CFR 71.119 - Control of special processes.

Code of Federal Regulations, 2012 CFR

2012-01-01

... 10 Energy 2 2012-01-01 2012-01-01 false Control of special processes. 71.119 Section 71.119 Energy NUCLEAR REGULATORY COMMISSION (CONTINUED) PACKAGING AND TRANSPORTATION OF RADIOACTIVE MATERIAL Quality... shall establish measures to assure that special processes, including welding, heat treating, and...

10 CFR 71.119 - Control of special processes.

Code of Federal Regulations, 2013 CFR

2013-01-01

... 10 Energy 2 2013-01-01 2013-01-01 false Control of special processes. 71.119 Section 71.119 Energy NUCLEAR REGULATORY COMMISSION (CONTINUED) PACKAGING AND TRANSPORTATION OF RADIOACTIVE MATERIAL Quality... shall establish measures to assure that special processes, including welding, heat treating, and...

10 CFR 71.119 - Control of special processes.

Code of Federal Regulations, 2014 CFR

2014-01-01

... 10 Energy 2 2014-01-01 2014-01-01 false Control of special processes. 71.119 Section 71.119 Energy NUCLEAR REGULATORY COMMISSION (CONTINUED) PACKAGING AND TRANSPORTATION OF RADIOACTIVE MATERIAL Quality... shall establish measures to assure that special processes, including welding, heat treating, and...

10 CFR 71.119 - Control of special processes.

Code of Federal Regulations, 2011 CFR

2011-01-01

... 10 Energy 2 2011-01-01 2011-01-01 false Control of special processes. 71.119 Section 71.119 Energy NUCLEAR REGULATORY COMMISSION (CONTINUED) PACKAGING AND TRANSPORTATION OF RADIOACTIVE MATERIAL Quality... shall establish measures to assure that special processes, including welding, heat treating, and...

Thermal Processing Effects on the Adhesive Strength of PS304 High Temperature Solid Lubricant Coatings

NASA Technical Reports Server (NTRS)

DellaCorte, Christopher; Edmonds, Brian J.; Benoy, Patricia A.

2001-01-01

In this paper the effects of post deposition heat treatments on the cohesive and adhesive strength properties of PS304, a plasma sprayed nickel-chrome based, high temperature solid lubricant coating deposited on stainless steel, are studied. Plasma spray deposited coating samples were exposed in air at temperatures from 432 to 650 C for up to 500 hr to promote residual stress relief, enhance particle to particle bonding and increase coating to substrate bond strength. Coating pull-off strength was measured using a commercial adhesion tester that utilizes 13 mm diameter aluminum pull studs attached to the coating surface with epoxy. Pull off force was automatically recorded and converted to coating pull off strength. As deposited coating samples were also tested as a baseline. The as-deposited (untreated) samples either delaminated at the coating-substrate interface or failed internally (cohesive failure) at about 17 MPa. Samples heat treated at temperatures above 540 C for 100 hr or at 600 C or above for more than 24 hr exhibited strengths above 31 MPa, nearly a two fold increase. Coating failure occurred inside the body of the coating (cohesive failure) for nearly all of the heat-treated samples and only occasionally at the coating substrate interface (adhesive failure). Metallographic analyses of heat-treated coatings indicate that the Nickel-Chromium binder in the PS304 appears to have segregated into two phases, a high nickel matrix phase and a high chromium precipitated phase. Analysis of the precipitates indicates the presence of silicon, a constituent of a flow enhancing additive in the commercial NiCr powder. The exact nature and structure of the precipitate phase is not known. This microstructural change is believed to be partially responsible for the coating strength increase. Diffusion bonding between particles may also be playing a role. Increasing the heat treatment temperature, exposure time or both accelerate the heat treatment process. Preliminary measurements indicate that the heat treatment also results in a one time, permanent coating thickness increase of about 3%. Based upon these results, the incorporation of a heat treatment prior to final finishing has been incorporated in the application process of this coating technology.

Microstructural, mechanical and corrosion characteristics of heat-treated Mg-1.2Zn-0.5Ca (wt%) alloy for use as resorbable bone fixation material.

PubMed

Ibrahim, Hamdy; Klarner, Andrew D; Poorganji, Behrang; Dean, David; Luo, Alan A; Elahinia, Mohammad

2017-05-01

Mg-Zn-Ca alloys have grabbed most of the recent attention in research attempting to develop an Mg alloy for bone fixation devices due to their superior biocompatibility. However, early resorption and insufficient strength remain the main problems that hinder their use. Heat treatment has previously been thoroughly studied as a post-shaping process, especially after the fabrication of complex parts (e.g. porous structures) by 3D-printing or powder metallurgy. In this work, the effect of heat treatment on Mg-1.2Zn-0.5Ca (wt%) alloy's microstructural, mechanical and corrosion properties was studied. The surface morphology of samples was characterized by optical microscopy, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and x-ray diffraction (XRD). Hardness, compression and tensile tests were conducted, while the in vitro corrosion characteristics of the prepared samples were determined using potentiodynamic polarization (PDP) and immersion tests. It was found that increasing the age hardening duration up to 2-5h increased the heat-treated Mg-1.2Zn-0.5Ca alloy's mechanical properties. Further increase in the age hardening duration did not result in further enhancement in mechanical properties. Similarly, heat treatment significantly altered the Mg-1.2Zn-0.5Ca alloy's in vitro corrosion properties. The corrosion rate of the Mg-1.2Zn-0.5Ca alloy after the heat treatment process was reduced to half of that for the as-cast alloy. XRD results showed the formation of biocompatible agglomerations of hydroxyapatite (HA) and magnesium hydroxide (Mg(OH) 2 ) on the corroded surface of the heat-treated Mg-1.2Zn-0.5Ca alloy samples. The performed heat treatment process had a significant effect on both mechanical and corrosion properties of the prepared Mg-1.2Zn-0.5Ca alloy. The age hardening duration which caused the greatest increase in mechanical and the most slowed corrosion rate for Mg-1.2Zn-0.5Ca alloy material was between 2 and 5h. Copyright © 2017 Elsevier Ltd. All rights reserved.

Improved Heat Treatment Of Steel Alloy 4340

NASA Technical Reports Server (NTRS)

Cooper, Lawrence B.

1993-01-01

New process takes significantly less time than prior heat-treatment processes. Involves placing steel plate directly in furnace and heat-treating. Plate then quenched in slowly moving oil to reduce stresses. Any deflection then pressed out. Possible uses of 4340 steel include new and improved bulletproof vests for military and police personnel and armor for bulletproof automobiles for military, police, diplomatic, and private users. Also used in other military land vehicles as tanks and in both military and civilian aircraft. Lighter armorplate enables land vehicles and aircraft to attain greater speed and maneuverability, consume less fuel, and afford better protection from snipers or terrorists.

Effect of Heat Treatment on the Properties of CoCrMo Alloy Manufactured by Selective Laser Melting

NASA Astrophysics Data System (ADS)

Guoqing, Zhang; Junxin, Li; Xiaoyu, Zhou; Jin, Li; Anmin, Wang

2018-04-01

To obtain medical implants with better mechanical properties, it is necessary to conduct studies on the heat treatment process of the selective laser melting (SLM) manufacturing parts. The differential scanning calorimetry method was used to study the heat treatment process of the phase transition of SLM CoCrMo alloy parts. The tensile properties were tested with a tensile test machine, the quantity of carbide precipitated after heat treatment was measured by energy-dispersive x-ray spectroscopy, and the tensile fracture morphology of the parts was investigated using SEM. The obtained results were: Mechanical properties in terms of elongation and tensile strength of CoCrMo alloy manufactured by SLM that had been heat-treated at 1200 °C for 2 h followed by cooling with water were not only higher than the national standard but also higher than the experimental results of the same batch of castings. The mechanism of fracture of parts manufactured by SLM without heat treatment was brittle fracture, whereas parts which had been heat-treated at 1200 °C for 2 h combined with water cooling and at 1200 °C for 1 h with furnace cooling suffered ductile fracture. This study provides the basis for defining the applications for which CoCrMo alloys manufactured by SLM are suitable within the field of medical implants.

Effect of Heat Treatment on the Properties of CoCrMo Alloy Manufactured by Selective Laser Melting

NASA Astrophysics Data System (ADS)

Guoqing, Zhang; Junxin, Li; Xiaoyu, Zhou; Jin, Li; Anmin, Wang

2018-05-01

To obtain medical implants with better mechanical properties, it is necessary to conduct studies on the heat treatment process of the selective laser melting (SLM) manufacturing parts. The differential scanning calorimetry method was used to study the heat treatment process of the phase transition of SLM CoCrMo alloy parts. The tensile properties were tested with a tensile test machine, the quantity of carbide precipitated after heat treatment was measured by energy-dispersive x-ray spectroscopy, and the tensile fracture morphology of the parts was investigated using SEM. The obtained results were: Mechanical properties in terms of elongation and tensile strength of CoCrMo alloy manufactured by SLM that had been heat-treated at 1200 °C for 2 h followed by cooling with water were not only higher than the national standard but also higher than the experimental results of the same batch of castings. The mechanism of fracture of parts manufactured by SLM without heat treatment was brittle fracture, whereas parts which had been heat-treated at 1200 °C for 2 h combined with water cooling and at 1200 °C for 1 h with furnace cooling suffered ductile fracture. This study provides the basis for defining the applications for which CoCrMo alloys manufactured by SLM are suitable within the field of medical implants.

Stack gas treatment

DOEpatents

Reeves, Adam A.

1977-04-12

Hot stack gases transfer contained heat to a gravity flow of pebbles treated with a catalyst, cooled stacked gases and a sulfuric acid mist is withdrawn from the unit, and heat picked up by the pebbles is transferred to air for combustion or other process. The sulfuric acid (or sulfur, depending on the catalyst) is withdrawn in a recovery unit.

Infrared fiber optic temperature monitoring of biological tissues heated in a microwave oven

NASA Astrophysics Data System (ADS)

Belotserkovsky, Edward; Ashkenasy, Y.; Shenfeld, Ofer; Drizlikh, S.; Zur, Albert; Katzir, Abraham

1993-05-01

The heating of tissue by microwave radiation has attained a place of importance in various medical fields such as the treatment of malignancies, urinary retention and hypothermia. Accurate temperature measurements in these treated tissues is important for treatment planning and for the control of the heating process. It is also important to be able to measure spacial temperature distribution in the tissues because they are heated in a non uniform way by the microwave radiation. Fiber optic radiometry makes possible accurate temperature measurement in the presence of microwave radiation and does not require contact with the tissue. Using a IR silver halide fiber optic radiometric temperature sensor we obtained accurate temperature measurements of tissues heated by microwave, enabling us to control the heating process in all regions of the tissue. We also performed temperature mapping of the heated tissues and demonstrated the non-uniform temperature distributions in them.

An evaluation of GTAW-P versus GTA welding of alloy 718

NASA Technical Reports Server (NTRS)

Gamwell, W. R.; Kurgan, C.; Malone, T. W.

1991-01-01

Mechanical properties were evaluated to determine statistically whether the pulsed current gas tungsten arc welding (GTAW-P) process produces welds in alloy 718 with room temperature structural performance equivalent to current Space Shuttle Main Engine (SSME) welds manufactured by the constant current GTAW-P process. Evaluations were conducted on two base metal lots, two filler metal lots, two heat input levels, and two welding processes. The material form was 0.125-inch (3.175-mm) alloy 718 sheet. Prior to welding, sheets were treated to either the ST or STA-1 condition. After welding, panels were left as welded or heat treated to the STA-1 condition, and weld beads were left intact or machined flush. Statistical analyses were performed on yield strength, ultimate tensile strength (UTS), and high cycle fatigue (HCF) properties for all the post welded material conditions. Analyses of variance were performed on the data to determine if there were any significant effects on UTS or HCF life due to variations in base metal, filler metal, heat input level, or welding process. Statistical analyses showed that the GTAW-P process does produce welds with room temperature structural performance equivalent to current SSME welds manufactured by the GTAW process, regardless of prior material condition or post welding condition.

Evaluation of dry heat treatment of soft wheat flour for the production of high ratio cakes.

PubMed

Keppler, S; Bakalis, S; Leadley, C E; Sahi, S S; Fryer, P J

2018-05-01

An accurate method to heat treat flour samples has been used to quantify the effects of heat treatment on flour functionality. A variety of analytical methods has been used such as oscillatory rheology, rheomixer, solvent retention capacity tests, and Rapid Visco Analysis (RVA) in water and in aqueous solutions of sucrose, lactic acid, and sodium carbonate. This work supports the hypothesis that heat treatment facilitates the swelling of starch granules at elevated temperature. Results furthermore indicated improved swelling ability and increased interactions of flour polymers (in particular arabinoxylans) of heat treated flour at ambient conditions. The significant denaturation of the proteins was indicated by a lack of gluten network formation after severe heat treatments as shown by rheomixer traces. Results of these analyses were used to develop a possible cake flour specification. A method was developed using response surfaces of heat treated flour samples in the RVA using i) water and ii) 50% sucrose solution. This can uniquely characterise the heat treatment a flour sample has received and to establish a cake flour specification. This approach might be useful for the characterisation of processed samples, rather than by baking cakes. Hence, it may no longer be needed to bake a cake after flour heat treatment to assess the suitability of the flour for high ratio cake production, but 2 types of RVA tests suffice. Copyright © 2018 The Authors. Published by Elsevier Ltd.. All rights reserved.

Carbon activation process for increased surface accessibility in electrochemical capacitors

DOEpatents

Doughty, Daniel H.; Eisenmann, Erhard T.

2001-01-01

A process for making carbon film or powder suitable for double capacitor electrodes having a capacitance of up to about 300 F/cm.sup.3 is disclosed. This is accomplished by treating in aqueous nitric acid for a period of about 5 to 15 minutes thin carbon films obtained by carbonizing carbon-containing polymeric material having a high degree of molecular directionality, such as polyimide film, then heating the treated carbon film in a non-oxidizing atmosphere at a non-graphitizing temperature of at least 350.degree. C. for about 20 minutes, and repeating alternately the nitric acid step and the heating step from 7 to 10 times. Capacitors made with this carbon may find uses ranging from electronic devices to electric vehicle applications.

Mechanical-chemical analyses and sub-chronic systemic toxicity of chemical treated organic bovine bone.

PubMed

Lee, Kwang-il; Lee, Jung-soo; Lee, Keun-soo; Jung, Hong-hee; Ahn, Chan-min; Kim, Young-sik; Shim, Young-bock; Jang, Ju-woong

2015-12-01

Sequentially chemical-treated bovine bone was not only evaluated by mechanical and chemical analyses but also implanted into the gluteal muscles of rats for 12 weeks to investigate potential local pathological effects and systemic toxicities. The test (chemical treated bone) and control (heat treated bone) materials were compared using scanning electron microscope (SEM), x-ray diffraction pattern, inductively coupled plasma analysis, and bending strength test. In the SEM images, the micro-porous structure of heat-treated bone was changed to sintered ceramic-like structure. The structure of bone mineral from test and control materials was analyzed as100% hydroxyapatite. The ratio of calcium (Ca) to potassium (P), the main inorganic elements, was same even though the Ca and P percentages of the control material was relatively higher than the test material. No death or critical symptoms arose from implantation of the test (chemical treated bone) and control (physiological saline) materials during 12 weeks. The implanted sites were macroscopically examined, with all the groups showing non-irritant results. Our results indicate that chemical processed bovine bone has a better mechanical property than the heat treated bone and the implantation of this material does not produce systemic or pathological toxicity. Copyright © 2015 Elsevier Inc. All rights reserved.

Thermal Inactivation of Feline Calicivirus in Pet Food Processing.

PubMed

Haines, J; Patel, M; Knight, A I; Corley, D; Gibson, G; Schaaf, J; Moulin, J; Zuber, S

2015-12-01

Extrusion is the most common manufacturing process used to produce heat-treated dry dog and cat food (pet food) for domestic use and international trade. Due to reoccurring outbreaks of notifiable terrestrial animal diseases and their impact on international trade, experiments were undertaken to demonstrate the effectiveness of heat-treated extruded pet food on virus inactivation. The impact of extrusion processing in a pet food matrix on virus inactivation has not been previously reported and very few inactivation studies have examined the thermal inactivation of viruses in complex food matrices. The feline calicivirus vaccine strain FCV F-9 was used as a surrogate model RNA virus pathogen. Small-scale heat inactivation experiments using animal-derived pet food raw materials showed that a > 4 log10 reduction (log10 R) in infectivity occurred at 70 °C prior to reaching the minimum extrusion manufacturing operating temperature of 100 °C. As anticipated, small-scale pressure studies at extrusion pressure (1.6 MPa) showed no apparent effect on FCV F-9 inactivation. Additionally, FCV F-9 was shown not to survive the acidic conditions used to produce pet food palatants of animal origin that are typically used as a coating after the extrusion process.

Material processing: AI-MSG modification

DOE Office of Scientific and Technical Information (OSTI.GOV)

Woolsey, C.C.; Carnazzola, A.

1973-12-18

This specification establishes fabrication processing requirements such as cleaning, welding, brazing, and post-weld heat treating for the modification of the Atomics International (AI) Modular Steam Generator (MSG) for use in the Large Leak Test Rig (LLTR) for the study of sodium-water reactions.

Comparative proteomic and metabolomic profiling of citrus fruit with enhancement of disease resistance by postharvest heat treatment

PubMed Central

2013-01-01

Background From field harvest to the consumer’s table, fresh citrus fruit spends a considerable amount of time in shipment and storage. During these processes, physiological disorders and pathological diseases are the main causes of fruit loss. Heat treatment (HT) has been widely used to maintain fruit quality during postharvest storage; however, limited molecular information related to this treatment is currently available at a systemic biological level. Results Mature ‘Kamei’ Satsuma mandarin (Citrus unshiu Marc.) fruits were selected for exploring the disease resistance mechanisms induced by HT during postharvest storage. Proteomic analyses based on two-dimensional gel electrophoresis (2-DE), and metabolomic research based on gas chromatography coupled to mass spectrometry (GC-MS), and liquid chromatography quadrupole time-of-flight mass spectrometry (LC-QToF-MS) were conducted. The results show resistance associated proteins were up-regulated in heat treated pericarp, such as beta-1, 3-glucanase, Class III chitinase, 17.7 kDa heat shock protein and low molecular weight heat-shock protein. Also, redox metabolism enzymes were down-regulated in heat treated pericarp, including isoflavone reductase, oxidoreductase and superoxide dismutase. Primary metabolic profiling revealed organic acids and amino acids were down-regulated in heat treated pericarp; but significant accumulation of metabolites, including tetradecanoic acid, oleic acid, ornithine, 2-keto-d-gluconic acid, succinic acid, turanose, sucrose, galactose, myo-inositol, glucose and fructose were detected. Noticeably, H2O2 content decreased, while, lignin content increased in heat treated pericarp compared to the control, which might increase fruit resistibility in response to external stress. Also, flavonoids, substances which are well-known to be effective in reducing external stress, were up-regulated in heat treated pericarp. Conclusions This study provides a broad picture of differential accumulation of proteins and metabolites in postharvest citrus fruit, and gives new insights into HT improved fruit disease resistance during subsequent storage of ‘Kamei’ Satsuma mandarin. Interpretation of the data for the proteins and metabolites revealed reactive oxygen species (ROS) and lignin play important roles in heat treatment induced fruit resistance to pathogens and physiological disorders. PMID:23497220

Effect of heat treatment on the characteristics of tool steel deposited by the directed energy deposition process

NASA Astrophysics Data System (ADS)

Park, Jun Seok; Lee, Min-Gyu; Cho, Yong-Jae; Sung, Ji Hyun; Jeong, Myeong-Sik; Lee, Sang-Kon; Choi, Yong-Jin; Kim, Da Hye

2016-01-01

The directed energy deposition process has been mainly applied to re-work and the restoration of damaged steel. Differences in material properties between the base and the newly deposited materials are unavoidable, which may affect the mechanical properties and durability of the part. We investigated the effect of heat treatment on the characteristics of tool steel deposited by the DED process. We prepared general tool steel materials of H13 and D2 that were deposited onto heat-treated substrates of H13 and D2, respectively, using a direct metal tooling process. The hardness and microstructure of the deposited steel before and after heat treatment were investigated. The hardness of the deposited H13 steel was higher than that of wrought H13 steel substrate, while that of the deposited D2 was lower than that of wrought D2. The evolution of the microstructures by deposition and heat treatment varied depending on the materials. In particular, the microstructure of the deposited D2 steel after heat treatment consisted of fine carbides in tempered martensite and it is expected that the deposited D2 steel will have isotropic properties and high hardness after heat treatment.

75 FR 19665 - Final Regulatory Guide: Issuance, Availability

Federal Register 2010, 2011, 2012, 2013, 2014

2010-04-15

... processes, including welding, heat treating, and nondestructive testing, are controlled and accomplished by... that when stressed under operating, maintenance, testing, and postulated accident conditions (1) the...

Forging; Heat Treating and Testing; Technically Oriented Industrial Materials and Process 1: 5898.05.

ERIC Educational Resources Information Center

Dade County Public Schools, Miami, FL.

The course provides students with advanced and exploratory experience in the area of plastic deformation of metals and in the changing of the physical characteristics of metals by the controlled application and timed removal of heat. Course content includes goals, specific objectives, safety in forge work, forging tools and equipment, industrial…

Investigation on the cold rolling and structuring of cold sprayed copper-coated steel sheets

NASA Astrophysics Data System (ADS)

Bobzin, K.; Öte, M.; Wiesner, S.; Gerdt, L.; Senge, S.; Hirt, G.

2017-03-01

A current driving force of research is lightweight design. One of the approaches to reduce the weight of a component without causing an overall stiffness decrease is the use of multi-material components. One of the main challenges of this approach is the low bonding strength between different materials. Focusing on steel-aluminum multi-material components, thermally sprayed copper coatings can come into use as a bonding agent between steel sheets and high pressure die cast aluminum to improve the bonding strength. This paper presents a combination of cold gas spraying of copper coatings and their subsequent structuring by rolling as surface pretreatment method of the steel inserts. Therefore, flat rolling experiments are performed with samples in “as sprayed” and heat treated conditions to determine the influence of the rolling process on the bond strength and the formability of the coating. Furthermore, the influence of the rolling on the roughness and the hardness of the coating was examined. In the next step, the coated surface was structured, to create a surface topology suited for a form closure connection in a subsequent high-pressure die casting process. No cracks were observed after the cold rolling process with a thickness reduction of up to ε = 14 % for heat treated samples. Structuring of heat treated samples could be realized without delamination and cracking.

Silver halide fiber optic radiometry for temperature monitoring and control of tissues heated by microwave

NASA Astrophysics Data System (ADS)

Shenfeld, Ofer; Belotserkovsky, Edward; Goldwasser, Benad; Zur, Albert; Katzir, Abraham

1993-02-01

The heating of tissue by microwave radiation has attained a place of importance in various medical fields, such as the treatment of malignancies, urinary retention, and hypothermia. Accurate temperature measurements in these treated tissues is important for treatment planning and for the control of the heating process. It is also important to be able to measure spacial temperature distribution in the tissues because they are heated in a nonuniform way by the microwave radiation. Conventional temperature sensors used today are inaccurate in the presence of microwave radiation and require contact with the heated tissue. Fiber optic radiometry makes it possible to measure temperatures accurately in the presence of microwave radiation and does not require contact with the tissue. Accurate temperature measurements of tissues heated by microwave was obtained using a silver halide optic radiometer, enabling control of the heating process in other regions of the tissue samples. Temperature mappings of the heated tissues were performed and the nonuniform temperature distributions in these tissues was demonstrated.

Effect of high pressure processing on textural and microbiological quality of pink perch (Nemipterus japonicus) sausage during chilled storage

NASA Astrophysics Data System (ADS)

Kunnath, Sarika; Panda, Satyen Kumar; Jaganath, Bindu; Gudipati, Venkateshwarlu

2015-10-01

The non-thermal high pressure (HP) processing was studied on fish sausage to enhance the quality during chilled storage. Pink perch (Nemipterus japonicus) sausages, packed in poly amide casing under vacuum were subjected to 400, 500 and 600 MPa pressures (dwell time: 10 min and ramp rate: 300 MPa/min) and compared with heat-set samples for physico-chemical and microbial quality parameters. Pressurized samples formed softer and glossier gels with a slight reduction in water-holding capacity. HP made the texture of sausage softer, cohesive and less chewy and gummier than heat-treated ones. Folding test seen higher acceptance values in samples treated at 500 and 600 MPa, during storage. Maximum log reduction in microbial count was observed in 600 MPa immediately, and significant difference in cooked and pressurized sausages was seen only up to 7th day. This revealed the potential application of HP in replacing conventional heat treatment for sausages preparation with enhanced shelf-life.

Rheological and stability aspects of dry and hydrothermally heat treated aleurone-rich wheat milling fraction.

PubMed

Bucsella, Blanka; Takács, Ágnes; von Reding, Walter; Schwendener, Urs; Kálmán, Franka; Tömösközi, Sándor

2017-04-01

Novel aleurone-rich wheat milling fraction developed and produced on industry scale is investigated. The special composition of the novel flour with high protein, dietary fiber and fat content results in a unique combination of the mixing and viscosity properties. Due to the high lipid concentration, the fraction is exposed to fast rancidity. Dry heat (100°C for 12min) and hydrothermal treatment processes (96°C for 6min with 0-20 L/h steam) were applied on the aleurone-rich flour to modify the technological properties. The chemical, structural changes; the extractability of protein, carbohydrate and phenolic components and the rheological characteristics of the flours were evaluated. The dry treated flour decreased protein and carbohydrate extractability, shortened dough development time, reduced gel strength and enhanced the gelling ability. Hydrothermal treatment caused changes in the phenolic content improved the dough stability and -resistance. Heat treatment processes were able to extend the stability of the flour. Copyright © 2016 Elsevier Ltd. All rights reserved.

Rapid surface hardening and enhanced tribological performance of 4140 steel by friction stir processing

DOE PAGES

Lorenzo-Martin, Cinta; Ajayi, Oyelayo O.

2015-06-06

Tribological performance of steel materials can be substantially enhanced by various thermal surface hardening processes. For relatively low-carbon steel alloys, case carburization is often used to improve surface performance and durability. If the carbon content of steel is high enough (>0.4%), thermal treatments such as induction, flame, laser, etc. can produce adequate surface hardening without the need for surface compositional change. This paper presents an experimental study of the use of friction stir processing (FSP) as a means to hardened surface layer in AISI 4140 steel. The impacts of this surface hardening process on the friction and wear performance weremore » evaluated under both dry and lubricated contact conditions in reciprocating sliding. FSP produced the same level of hardening and superior tribological performance when compared to conventional thermal treatment, using only 10% of the energy and without the need for quenching treatments. With FSP surface hardness of about 7.8 GPa (62 Rc) was achieved while water quenching conventional heat treatment produced about 7.5 GPa (61 Rc) hardness. Microstructural analysis showed that both FSP and conventional heat treatment produced martensite. Although the friction behavior for FSP treated surfaces and the conventional heat treatment were about the same, the wear in FSP processed surfaces was reduced by almost 2× that of conventional heat treated surfaces. Furthermore, the superior performance is attributed to the observed grain refinement accompanying the FSP treatment in addition to the formation of martensite. As it relates to tribological performance, this study shows FSP to be an effective, highly energy efficient, and environmental friendly (green) alternative to conventional heat treatment for steel.« less

Processes for preparing carbon fibers using sulfur trioxide in a halogenated solvent

DOEpatents

Patton, Jasson T.; Barton, Bryan E.; Bernius, Mark T.; Chen, Xiaoyun; Hukkanen, Eric J.; Rhoton, Christina A.; Lysenko, Zenon

2015-12-29

Disclosed here are processes for preparing carbonized polymers (preferably carbon fibers), comprising sulfonating a polymer with a sulfonating agent that comprises SO.sub.3 dissolved in a solvent to form a sulfonated polymer; treating the sulfonated polymer with a heated solvent, wherein the temperature of the solvent is at least 95.degree. C.; and carbonizing the resulting product by heating it to a temperature of 500-3000.degree. C. Carbon fibers made according to these methods are also disclosed herein.

Effect of heat treatment on the antioxidant activity of extracts from citrus peels.

PubMed

Jeong, Seok-Moon; Kim, So-Young; Kim, Dong-Ryul; Jo, Seong-Chun; Nam, K C; Ahn, D U; Lee, Seung-Cheol

2004-06-02

The effect of heat treatment on the antioxidant activity of extracts from Citrus unshiu peels was evaluated. Citrus peels (CP) (5 g) were placed in Pyrex Petri dishes (8.0 cm diameter) and heat-treated at 50, 100, or 150 degrees C for 10, 20, 30, 40, 50, and 60 min in an electric muffle furnace. After heat treatment, 70% ethanol extract (EE) and water extract (WE) (0.1 g/10 mL) of CP were prepared, and total phenol contents (TPC), radical scavenging activity (RSA), and reducing power of the extracts were determined. The antioxidant activities of CP extracts increased as heating temperature increased. For example, heat treatment of CP at 150 degrees C for 60 min increased the TPC, RSA, and reducing power of EE from 71.8 to 171.0 microM, from 29.64 to 64.25%, and from 0.45 to 0.82, respectively, compared to non-heat-treated control. In the case of WE from CP heat-treated at the same conditions (150 degrees C for 60 min), the TPC, RSA, and reducing power also increased from 84.4 to 204.9 microM, from 15.81 to 58.26%, and from 0.27 to 0.96, respectively. Several low molecular weight phenolic compounds such as 2,3-diacetyl-1-phenylnaphthalene, ferulic acid, p-hydroxybenzaldoxime, 5-hydroxyvaleric acid, 2,3-diacetyl-1-phenylnaphthalene, and vanillic acid were newly formed in the CP heated at 150 degrees C for 30 min. These results indicated that the antioxidant activity of CP extracts was significantly affected by heating temperature and duration of treatment on CP and that the heating process can be used as a tool for increasing the antioxidant activity of CP.

Engineering novel synthetic strategy to develop mesocarbon microbeads for multi-functional applications

NASA Astrophysics Data System (ADS)

Chaudhary, Anisha; Teotia, Satish; Kumar, Rajeev; Ramesha, K.; Dhakate, Sanjay R.; Kumari, Saroj

2018-04-01

To assess the challenge of affordable technology, present synthetic strategies can be extended to new low-cost synthesis and processing methods that have potential to tailor the properties of the materials. Here we report, a novel method for the synthesis of mesocarbon microbeads (MCMB) through a pre-processing involved pyrolysis technique. The resulting MCMB is compressed into a product and effects of heat treatment temperature on different properties of MCMB is studied. The use of MCMB for the electromagnetic interference (EMI) shielding is new and hence, the effect of heat treatment temperature on EMI shielding effectiveness is studied in X-band. It is observed that EMI shielding effectiveness increases to ‑39.6 dB on increasing the heat treatment temperature. The high conductivity of MCMB plate heat treated upto 2500 °C contributes to highly conducting networks. Additionally, to investigate the electrochemical performance of MCMB as an anode material for lithium ion batteries, 2500 °C heat treated MCMB powder is used to fabricate the electrode. The MCMB electrode exhibits high discharge capacity of 345 mAh g‑1 with a stable capacity for over 50 cycles and good rate capability. Thus, MCMB synthesized by this novel approach can be used for the development of high performance anode materials for Li-ion batteries.

Preservation of raw milk with CO2. Sensory evaluation of heat-processed milks.

PubMed

Amigo, L; Olano, A; Calvo, M M

1995-04-01

The effect of CO2 on the growth of psychrotrophic milk spoilage organisms was studied, both in raw fresh milk and in pure cultures of three species of Pseudomonas growing in sterilised milk. Changes of sensory properties of CO2-treated samples after heat treatment were also analysed. Inhibition of psychrotrophic growth at 7 degrees C in milk treated with CO2 to a pH 6.2 or 6.0 was impaired by a gradual reduction of the CO2 content during storage. Growth inhibition was considerably improved by pH adjustment at 24-h intervals. Sensory analysis showed significant differences between non-acidified and acidified samples after heat treatment at 75 degrees C for 20 s or 110 degrees C for 5 min. No sensory differences were found between non-acidified and acidified milks degassed before heat treatment.

Effect of the Platinum Electroplated Layer Thickness on the Coatings' Microstructure

NASA Astrophysics Data System (ADS)

Zagula-Yavorska, Maryana; Gancarczyk, Kamil; Sieniawski, Jan

2017-03-01

CMSX 4 and Inconel 625 superalloys were coated by platinum layers (3 and 7 μm thick) in the electroplating process. The heat treatment of platinum layers (at 1,050 ˚C for 2 h) was performed to increase platinum adherence to the superalloys substrate. The diffusion zone obtained on CMSX 4 superalloy (3 and 7 μm platinum thick before heat treatment) consisted of two phases: γ-Ni(Al, Cr) and (Al0.25Pt0.75)Ni3. The diffusion zone obtained on Inconel 625 superalloy (3 μm platinum thick before heat treatment) consisted of the α-Pt(Ni, Cr, Al) phase. Moreover, γ-Ni(Cr, Al) phase was identified. The X-ray diffraction (XRD) results revealed the presence of platinum in the diffusion zone of the heat-treated coating (7 μm platinum thick) on Inconel 625 superalloy. The surface roughness parameter Ra of heat-treated coatings increased with the increase of platinum layers thickness. This was due to the unequal mass flow of platinum and nickel.

[Surface modification of dental alumina ceramic with silica coating].

PubMed

Xie, Hai-Feng; Zhang, Fei-Min; Wang, Xiao-Zu; Xia, Yang

2006-12-01

To make silica coating through sol-gel process, and to evaluate the wettability of dental alumina ceramic with or without coating. Silica coating was prepared with colloidal silica sol on In-Ceram alumina ceramic surface which had been treated with air particle abrasion. Coating gel after heat treatment was observed with atomic force microscope (AFM), and was analyzed by infrared spectrum (IR) with gel without sintered as control. Contact angles of oleic acid to be finished, sandblasted and coated ceramic surface of were measured. AFM pictures showed that some parts of nano-particles in coating gel conglomerated after heat treatment. It can be seen from the IR picture that bending vibration absorption kurtosis of Si-OH also vanished after heat treatment. Among contact angles of three treated surface, the ones on polished surface were the biggest (P = 0.000, P = 0.000), and sandblasting+silica coating surface the smallest (P = 0.000, P = 0.003). Silica coating can be made with sol-gel process successfully. Heat treatment may reinforce Si-O-Si net structure of coating gel. Wettability of dental alumina ceramic with silica coating is higher than with sandblasting and polishing.

Structural, dynamic, and vibrational properties during heat transfer in Si/Ge superlattices: A Car-Parrinello molecular dynamics study

NASA Astrophysics Data System (ADS)

Ji, Pengfei; Zhang, Yuwen; Yang, Mo

2013-12-01

The structural, dynamic, and vibrational properties during heat transfer process in Si/Ge superlattices are studied by analyzing the trajectories generated by the ab initio Car-Parrinello molecular dynamics simulation. The radial distribution functions and mean square displacements are calculated and further discussions are made to explain and probe the structural changes relating to the heat transfer phenomenon. Furthermore, the vibrational density of states of the two layers (Si/Ge) are computed and plotted to analyze the contributions of phonons with different frequencies to the heat conduction. Coherent heat conduction of the low frequency phonons is found and their contributions to facilitate heat transfer are confirmed. The Car-Parrinello molecular dynamics simulation outputs in the work show reasonable thermophysical results of the thermal energy transport process and shed light on the potential applications of treating the heat transfer in the superlattices of semiconductor materials from a quantum mechanical molecular dynamics simulation perspective.

Radio frequency heating for in-situ remediation of DNAPL

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kasevich, R.S.

1996-08-01

In-situ radio frequency (RF) heating technology for treating soils contaminated with dense nonaqueous phase liquids (DNAPLs) is described. RF imparts heat to non-conducting materials through the application of carefully controlled RF transmissions, improving contaminant flow characteristics and facilitating separation and removal from subsurface soils. The paper outlines advantages and limitations of RF remediation, process operations, general technology considerations, low permeability media considerations, commercial availability, and costs. Two case histories of RF remediation are briefly summarized. 13 refs., 10 figs.

Heat Treatments of ZnSe Starting Materials for Physical Vapor Transport

NASA Technical Reports Server (NTRS)

Su, Ching-Hua; Palosz, W.; Feth, S.; Lehoczky, S. L.

1998-01-01

The effect of different heat treatments on stoichiometry and residual gas pressure in ZnSe physical vapor transport system was investigated. The dependence of the amount and composition of the residual gas on various heat treatment procedures is reported. Heat treatment of ZnSe starting materials by baking under the condition of dynamic vacuum to adjust its stoichiometry was performed and the effectiveness of the treatment was confirmed by the measurements of the partial pressure of Se2, P(sub Se2), in equilibrium with the heat treated samples. Optimum heat treatment procedures on the ZnSe starting material for the physical vapor transport process are discussed and verified experimentally.

Heat Treatments of ZnSe Starting Materials for Physical Vapor Transport

NASA Technical Reports Server (NTRS)

Su, Ching-Hua; Palosz, W.; Feth, S.; Lehoczky, S. L.

1997-01-01

The effect of different heat treatments on stoichiometry and residual gas pressure in ZnSe physical vapor transport system was investigated. The dependence of the amount and composition of the residual gas on various heat treatment procedures is reported. Heat treatment of ZnSe starting materials by baking under the condition of dynamic vacuum to adjust its stoichiometry was performed and the effectiveness of the treatment was confirmed by the measurements of the partial pressure of Se2, P(sub Se2), in equilibrium with the heat treated samples. Optimum heat treatment procedures on the ZnSe starting material for the physical vapor transport process are discussed and verified experimentally.

Alterations in Pain Responses in Treated and Untreated Patients with Restless Legs Syndrome: Associations with Sleep Disruption

PubMed Central

Edwards, Robert R; Quartana, Phillip J.; Allen, Richard P; Greenbaum, Seth; Earley, Christopher J; Smith, Michael T

2011-01-01

Objective There has been recent interest in characterizing potential abnormalities of pain processing in patients with sleep disorders such as Restless Legs Syndrome (RLS). The aim of this study was to evaluate psychophysical responses to noxious heat and pressure stimuli in both treated and untreated RLS patients, compared to matched controls. Methods This study is a cross-sectional group comparison of RLS patients with matched controls. A total of 31 patients (15 treated, 16 untreated) with a confirmed diagnosis of RLS were compared to 18 controls with no history of RLS or related sleep disorders. Results RLS patients (both treated and untreated) demonstrated reduced pain thresholds and reported greater clinical pain relative to controls. Moreover, RLS patients demonstrated enhanced temporal summation of heat pain (p< .05), which may reflect aberrant central nervous system facilitation of pain transmission. Both treated and untreated RLS patients reported disrupted sleep relative to controls, and mediation analyses suggested that the reduced pain thresholds in RLS were attributable to sleep disturbance. However, the effect of RLS on the magnitude of temporal summation of heat pain was independent of sleep disturbance. Conclusions These findings suggest that central nervous system pain processing may be amplified in RLS, perhaps partially as a consequence of sleep disruption. RLS patients, even those whose symptoms are managed pharmacologically, may be at elevated long-term risk for the development or maintenance of persistent pain conditions. Further studies in larger samples could help to improve the prospects for pain management in RLS patients. PMID:21570347

Precise carbon control of fabricated stainless steel

DOEpatents

Nilsen, R.J.

1975-12-01

A process is described for controlling the carbon content of fabricated stainless steel components including the steps of heat treating the component in hydrogen atmospheres of varying dewpoints and carbon potentials.

Corrosion behavior of heat-treated intermetallic titanium-nickel in hydrochloric acid solutions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Starosvetsky, D.; Khaselev, O.; Yahalom, J.

1998-07-01

Samples of 45% Ti-55% Ni alloy (Ti-Ni) were heat-treated in air at 450 C, and their anodic behavior in 0.3 M, 1 M, 2 M, and 4 M hydrochloric acid (HCl) solutions was studied. In 0.3 M HCl, heat-treated Ti-Ni was passive, and very low anodic currents were observed. In 1 M and 2 M HCl, heat-treated Ti-Ni was dissolved actively, while heat-treated and surface-ground Ti-Ni became passive. The effect was explained by selective oxidation of Ti-Ni and formation of a layered structure on its surface with discontinuous titanium oxide and a nickel-enriched zone underneath. The latter was dissolved inmore » the HCl solutions, thus accelerating failure of the Ti-Ni samples. In 4 M HCl, heat-treated and heat-treated/ground samples were dissolved readily.« less

Optimization of Processing Condition of Nanocomposites According to the Structural Changes of Halloysite Nanotubes Under Impact Behavior

NASA Astrophysics Data System (ADS)

Kim, Yun-Hae; Park, Soo-Jeong; Nakagaito, Antonio Norio

2017-08-01

In the present study, optimal dispersion conditions were developed to disperse nanocomposites containing halloysite nanotubes (HNTs) and unsaturated polyester (UP) resin using ultrasonic dispersion method. Due to the presence of a substantial amount of water in HNTs, their properties depend on the operating temperature when dispersing. It is, therefore, important to understand the structural changes of HNTs that occur when changing the operating temperature. HNTs heat-treated at various temperatures have different structures and mechanical/chemical properties. Therefore, in this research, HNTs were treated at two temperatures, 773.15 K and 973.15 K (500 °C and 700 °C), and the correlation between UP resin and heat-treated HNTs was studied in detail. The quantities of HNTs were 0.5 and 1 wt pct, for the 773.15 K and 973.15 K (500 °C and 700 °C) heat treatment temperatures, respectively. The contents of HNTs were restricted in order to demonstrate the aggregation phenomenon. The dispersion was carried out by ultrasonication. All structural changes including dispersion behavior were examined by TEM. The mechanical properties were assessed by impact tests. The results showed that the high impact strength of the nanocomposite containing 1 wt pct of 973.15 K (700 °C) heat-treated HNT was superior. In other words, it can be said that the rheological property of the matrix resin depended on the quantities of HNTs and the heat treatment temperature.

Fatigue Properties of Butt Welded Aluminum Alloy and Carbon Steel Joints by Friction Stirring

NASA Astrophysics Data System (ADS)

Okane, M.; Shitaka, T.; Ishida, M.; Chaki, T.; Yasui, T.; Fukumoto, M.

2017-05-01

The butt dissimilar joints of Al-Mg-Si alloy JIS A6063 and carbon steel JIS S45C by means of friction stir welding were prepared for investigating fatigue properties of the joints. The joining tool used has cemented carbide thread probe and a shoulder made of alloy tool steel. All the fatigue tests were carried out under a load-controlled condition with a load ratio R=0.1 in air at room temperature. From the experimental results, it was found that hardness near the interface in A6063 was lower than that of base material. Three types of fatigue fracture occurred even in case of same welding condition. The first one was fracture at boundary between the lower hardness region and base material in A6063, the second type was initiated in the stir zone by FSW process and the last one was fracture at interface. Fatigue strength in case of the second one was lower than others. Furthermore, to investigate the effect of heat treatment on fatigue properties of the dissimilar joints, fatigue tests were also carried out with using the specimens which were heat treated under the same condition to aging process in T6 treatment. Fatigue fracture was initiated at interface between A6063 and S45C in case of the heat treated specimen, but fatigue strength was improved approximately 25% as compared with that of the non-heat treated specimen.

The influence of flame hardening process to aluminum 7075 series on the mechanical strength and micro structure

NASA Astrophysics Data System (ADS)

Koin, Sudibtia Titio; Triyono, Teguh; Surojo, Eko

2018-02-01

The 7075 series alloys are heat treatable wrought aluminum alloys based on the Al-Zn-Mg(-Cu) system. They are widely used in high-performance structural aerospace and transportation applications. Apart from compositional, casting and thermo-mechanical processing effects, the balance of properties is also significantly influenced by the way in which the materials are heat-treated. This paper describes the effect of flame hardening process to aluminum 7075 series on the increasing hardness, tensile strength, and evolution of microstructure. A test specimen had made by machining process and flame heating. Temperature of solution heat treatment is varied on 350 °C, 400 °C, 450 °C and 500 °C. After that process a test specimen would be quenched at nitrate-nitrite liquid during 45 minutes and artificial aging at 120°C until two days. The testing specimen consist of hardness and tensile strength according to ASTM. The result showed that specimen had precipitation on microstructure lead to an increase in aluminum properties. On the temperature 450°C solution heat treatment, the aluminum properties reached the highest value, namely, hardness of 129 HVN and tensile strength 570 MPa.

Process for synthesizing compounds from elemental powders and product

DOEpatents

Rabin, B.H.; Wright, R.N.

1993-12-14

A process for synthesizing intermetallic compounds from elemental powders is described. The elemental powders are initially combined in a ratio which approximates the stoichiometric composition of the intermetallic compound. The mixed powders are then formed into a compact which is heat treated at a controlled rate of heating such that an exothermic reaction between the elements is initiated. The heat treatment may be performed under controlled conditions ranging from a vacuum (pressureless sintering) to compression (hot pressing) to produce a desired densification of the intermetallic compound. In a preferred form of the invention, elemental powders of Fe and Al are combined to form aluminide compounds of Fe[sub 3] Al and FeAl. 25 figures.

Process for synthesizing compounds from elemental powders and product

DOEpatents

Rabin, Barry H.; Wright, Richard N.

1993-01-01

A process for synthesizing intermetallic compounds from elemental powders. The elemental powders are initially combined in a ratio which approximates the stoichiometric composition of the intermetallic compound. The mixed powders are then formed into a compact which is heat treated at a controlled rate of heating such that an exothermic reaction between the elements is initiated. The heat treatment may be performed under controlled conditions ranging from a vacuum (pressureless sintering) to compression (hot pressing) to produce a desired densification of the intermetallic compound. In a preferred form of the invention, elemental powders of Fe and Al are combined to form aluminide compounds of Fe.sub.3 Al and FeAl.

Influence of Oxidation Treatments and Surface Finishing on the Electrochemical Behavior of Ni-20Cr HVOF Coatings

NASA Astrophysics Data System (ADS)

Ruiz-Luna, H.; Porcayo-Calderon, J.; Alvarado-Orozco, J. M.; Mora-García, A. G.; Martinez-Gomez, L.; Trápaga-Martínez, L. G.; Muñoz-Saldaña, J.

2017-12-01

The low-temperature electrochemical behavior of HVOF Ni-20Cr coatings was assessed. The coatings were evaluated in different conditions including as-sprayed, as-ground, and heat-treated in air and argon atmospheres. A detailed analysis of the coatings was carried out by means of XRD, SEM, and EPMA, prior and after the corrosion test. The corrosion rate was analyzed in a NaCl solution saturated with CO2. Results demonstrate that the use of a low-oxygen partial pressure favors the formation of a Cr2O3 layer on the surface of the coatings. According to the electrochemical results, the lower corrosion rates were obtained for the heat-treated coatings irrespective of the surface finishing, being the ground and argon heat-treated condition that shows the best corrosion performance. This behavior is due to the synergistic effect of the low-pressure heat treatment and the grinding processes. The grinding promotes a more homogeneous reaction area without surface heterogeneities such as voids, and the pre-oxidation treatment decreases the porosity content of the coating and also allows the growing of a Cr-rich oxide scale which acts as a barrier against the ions of the aqueous solution.

The moisture outgassing kinetics of a silica reinforced polydimethylsiloxane

NASA Astrophysics Data System (ADS)

Sharma, H. N.; McLean, W.; Maxwell, R. S.; Dinh, L. N.

2016-09-01

A silica-filled polydimethylsiloxane (PDMS) composite M9787 was investigated for potential outgassing in a vacuum/dry environment with the temperature programmed desorption/reaction method. The outgassing kinetics of 463 K vacuum heat-treated samples, vacuum heat-treated samples which were subsequently re-exposed to moisture, and untreated samples were extracted using the isoconversional and constrained iterative regression methods in a complementary fashion. Density functional theory (DFT) calculations of water interactions with a silica surface were also performed to provide insight into the structural motifs leading to the obtained kinetic parameters. Kinetic analysis/model revealed that no outgassing occurs from the vacuum heat-treated samples in subsequent vacuum/dry environment applications at room temperature (˜300 K). The main effect of re-exposure of the vacuum heat-treated samples to a glove box condition (˜30 ppm by volume of H2O) for even a couple of days was the formation, on the silica surface fillers, of ˜60 ppm by weight of physisorbed and loosely bonded moisture, which subsequently outgasses at room temperature in a vacuum/dry environment in a time span of 10 yr. However, without any vacuum heat treatment and even after 1 h of vacuum pump down, about 300 ppm by weight of H2O would be released from the PDMS in the next few hours. Thereafter the outgassing rate slows down substantially. The presented methodology of using the isoconversional kinetic analysis results and some appropriate nature of the reaction as the constraints for more accurate iterative regression analysis/deconvolution of complex kinetic spectra, and of checking the so-obtained results with first principle calculations such as DFT can serve as a template for treating other complex physical/chemical processes as well.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sharma, H. N.; McLean, W.; Maxwell, R. S.

We investigated a silica-filled polydimethylsiloxane (PDMS) composite M9787 for potential outgassing in a vacuum/dry environment with the temperature programmed desorption/reaction method. The outgassing kinetics of 463 K vacuum heat-treated samples, vacuum heat-treated samples which were subsequently re-exposed to moisture, and untreated samples were extracted using the isoconversional and constrained iterative regression methods in a complementary fashion. Density functional theory (DFT) calculations of water interactions with a silica surface were also performed to provide insight into the structural motifs leading to the obtained kinetic parameters. Kinetic analysis/model revealed that no outgassing occurs from the vacuum heat-treated samples in subsequent vacuum/dry environmentmore » applications at room temperature (~300 K). Moreover, the main effect of re-exposure of the vacuum heat-treated samples to a glove box condition (~30 ppm by volume of H 2O) for even a couple of days was the formation, on the silica surface fillers, of ~60 ppm by weight of physisorbed and loosely bonded moisture, which subsequently outgasses at room temperature in a vacuum/dry environment in a time span of 10 yr. However, without any vacuum heat treatment and even after 1 h of vacuum pump down, about 300 ppm by weight of H 2O would be released from the PDMS in the next few hours. Thereafter the outgassing rate slows down substantially. Our presented methodology of using the isoconversional kinetic analysis results and some appropriate nature of the reaction as the constraints for more accurate iterative regression analysis/deconvolution of complex kinetic spectra, and of checking the so-obtained results with first principle calculations such as DFT can serve as a template for treating other complex physical/chemical processes as well.« less

The moisture outgassing kinetics of a silica reinforced polydimethylsiloxane

DOE PAGES

Sharma, H. N.; McLean, W.; Maxwell, R. S.; ...

2016-09-21

We investigated a silica-filled polydimethylsiloxane (PDMS) composite M9787 for potential outgassing in a vacuum/dry environment with the temperature programmed desorption/reaction method. The outgassing kinetics of 463 K vacuum heat-treated samples, vacuum heat-treated samples which were subsequently re-exposed to moisture, and untreated samples were extracted using the isoconversional and constrained iterative regression methods in a complementary fashion. Density functional theory (DFT) calculations of water interactions with a silica surface were also performed to provide insight into the structural motifs leading to the obtained kinetic parameters. Kinetic analysis/model revealed that no outgassing occurs from the vacuum heat-treated samples in subsequent vacuum/dry environmentmore » applications at room temperature (~300 K). Moreover, the main effect of re-exposure of the vacuum heat-treated samples to a glove box condition (~30 ppm by volume of H 2O) for even a couple of days was the formation, on the silica surface fillers, of ~60 ppm by weight of physisorbed and loosely bonded moisture, which subsequently outgasses at room temperature in a vacuum/dry environment in a time span of 10 yr. However, without any vacuum heat treatment and even after 1 h of vacuum pump down, about 300 ppm by weight of H 2O would be released from the PDMS in the next few hours. Thereafter the outgassing rate slows down substantially. Our presented methodology of using the isoconversional kinetic analysis results and some appropriate nature of the reaction as the constraints for more accurate iterative regression analysis/deconvolution of complex kinetic spectra, and of checking the so-obtained results with first principle calculations such as DFT can serve as a template for treating other complex physical/chemical processes as well.« less

Consumer acceptance of ozone-treated whole shell eggs.

PubMed

Kamotani, Setsuko; Hooker, Neal; Smith, Stephanie; Lee, Ken

2010-03-01

Ozone-based processing is a novel technology with potentially fewer adverse effects than in-shell thermal pasteurization of eggs. There are no consumer acceptance studies published on ozone-treated eggs. This study examines consumers' ability to detect changes between ozone-treated, thermal-treated, and fresh untreated eggs. Consumers (n = 111) evaluated visual attributes of uncooked eggs and a separate group of consumers (n = 132) evaluated acceptability of cooked eggs. Consumers evaluated attribute intensity of the eggs. The yolks and albumens of the thermal-treated and ozone-treated eggs were perceived to be significantly cloudier than the untreated control, while the ozone-treated eggs were more similar to control (P < 0.05). The yolks of ozone-treated eggs were perceived to have significantly lower heights and greater spreads than the others (P < 0.05). Despite these perceptions, overall visual appeal of ozone-treated eggs was not significantly different from control eggs. A separate set of consumers used hedonic scales to evaluate overall liking, appearance, aroma, flavor, and texture of cooked eggs. Just-about-right (JAR) scales were used to rate the color, moistness, and texture. There were no differences on any attribute scores between the treatments, except thermal-treated and ozone-treated were perceived as less moist than the control. There were no adverse effects on consumer acceptance of eggs, treated with ozone, with acceptance the same as an untreated control. These findings are useful as ozone pasteurization can enhance the safety of fresh shell eggs to meet the goals of the U.S. Egg Safety Action Plan. The U.S. Egg Safety Action Plan requires all shell eggs to be pasteurized to prevent foodborne illness. Heat pasteurization partially cooks the egg, so an alternative process uses ozone with less heat. This study shows the ozone pasteurization has no detectable sensory defects.

Design and performance of a new induction furnace for heat treatment of superconducting radiofrequency niobium cavities

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dhakal, Pashupati; Ciovati, Gianluigi; Myneni, Ganapati Rao

2012-06-15

Superconducting radio frequency (SRF) cavities made of high purity niobium (Nb) are the building blocks of many modern particle accelerators. The fabrication process includes several cycles of chemical and heat treatment at low ({approx}120 Degree-Sign C) and high ({approx}800 Degree-Sign C) temperatures. In this contribution, we describe the design and performance of an ultra-high-vacuum furnace which uses an induction heating system to heat treat SRF cavities. Cavities are heated by radiation from the Nb susceptor. By using an all-niobium hot zone, contamination of the Nb cavity by foreign elements during heat treatment is minimized and allows avoiding subsequent chemical etching.more » The furnace was operated up to 1400 Degree-Sign C with a maximum pressure of {approx}1 Multiplication-Sign 10{sup -5} Torr and the maximum achievable temperature is estimated to be higher than 2000 Degree-Sign C. Initial results on the performance of a single cell 1.5 GHz cavity made of ingot Nb heat treated at 1200 Degree-Sign C using this new induction furnace and without subsequent chemical etching showed a reduction of the RF losses by a factor of {approx}2 compared to cavities made of fine-grain Nb which underwent standard chemical and heat treatments.« less

Design and performance of a new induction furnace for heat treatment of superconducting radiofrequency niobium cavities

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pashupati Dhakal, Gianluigi Ciovati, Wayne Rigby, John Wallace, Ganapati Rao Myneni

2012-06-01

Superconducting radio frequency (SRF) cavities made of high purity niobium (Nb) are the building blocks of many modern particle accelerators. The fabrication process includes several cycles of chemical and heat treatment at low ({approx}120 deg C) and high ({approx}800 deg C) temperatures. In this contribution, we describe the design and performance of an ultra-high-vacuum furnace which uses an induction heating system to heat treat SRF cavities. Cavities are heated by radiation from the Nb susceptor. By using an all-niobium hot zone, contamination of the Nb cavity by foreign elements during heat treatment is minimized and allows avoiding subsequent chemical etching.more » The furnace was operated up to 1400 deg C with a maximum pressure of {approx}1 x 10{sup -5} Torr and the maximum achievable temperature is estimated to be higher than 2000 deg C. Initial results on the performance of a single cell 1.5 GHz cavity made of ingot Nb heat treated at 1200 deg C using this new induction furnace and without subsequent chemical etching showed a reduction of the RF losses by a factor of {approx}2 compared to cavities made of fine-grain Nb which underwent standard chemical and heat treatments.« less

Design and performance of a new induction furnace for heat treatment of superconducting radiofrequency niobium cavities.

PubMed

Dhakal, Pashupati; Ciovati, Gianluigi; Rigby, Wayne; Wallace, John; Myneni, Ganapati Rao

2012-06-01

Superconducting radio frequency (SRF) cavities made of high purity niobium (Nb) are the building blocks of many modern particle accelerators. The fabrication process includes several cycles of chemical and heat treatment at low (∼120 °C) and high (∼800 °C) temperatures. In this contribution, we describe the design and performance of an ultra-high-vacuum furnace which uses an induction heating system to heat treat SRF cavities. Cavities are heated by radiation from the Nb susceptor. By using an all-niobium hot zone, contamination of the Nb cavity by foreign elements during heat treatment is minimized and allows avoiding subsequent chemical etching. The furnace was operated up to 1400 °C with a maximum pressure of ∼1 × 10(-5) Torr and the maximum achievable temperature is estimated to be higher than 2000 °C. Initial results on the performance of a single cell 1.5 GHz cavity made of ingot Nb heat treated at 1200 °C using this new induction furnace and without subsequent chemical etching showed a reduction of the RF losses by a factor of ∼2 compared to cavities made of fine-grain Nb which underwent standard chemical and heat treatments.

Structural, dynamic, and vibrational properties during heat transfer in Si/Ge superlattices: A Car-Parrinello molecular dynamics study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ji, Pengfei; Zhang, Yuwen, E-mail: zhangyu@missouri.edu; Yang, Mo

The structural, dynamic, and vibrational properties during heat transfer process in Si/Ge superlattices are studied by analyzing the trajectories generated by the ab initio Car-Parrinello molecular dynamics simulation. The radial distribution functions and mean square displacements are calculated and further discussions are made to explain and probe the structural changes relating to the heat transfer phenomenon. Furthermore, the vibrational density of states of the two layers (Si/Ge) are computed and plotted to analyze the contributions of phonons with different frequencies to the heat conduction. Coherent heat conduction of the low frequency phonons is found and their contributions to facilitate heatmore » transfer are confirmed. The Car-Parrinello molecular dynamics simulation outputs in the work show reasonable thermophysical results of the thermal energy transport process and shed light on the potential applications of treating the heat transfer in the superlattices of semiconductor materials from a quantum mechanical molecular dynamics simulation perspective.« less

Electromagnetic characteristics of manganese oxide-coated Fe3O4 nanoparticles at 2-18 GHz

NASA Astrophysics Data System (ADS)

Yang, R. B.; Liang, W. F.; Lin, C. K.

2011-04-01

The dielectric and magnetic properties of manganese oxide-coated Fe3O4 nanoparticles (NPs) were measured by the transmission/reflection method in 2-18 GHz. MnOx-coated Fe3O4 NPs were prepared by sol-gel method followed by heat-treating at 300, 400, and 500 °C, respectively. The heat-treated powders were then used as magnetic fillers and added to an epoxy resin to prepare MnOx-coated Fe3O4 composites for the complex permittivity (ɛ'-jɛ″) and permeability (μ'-jμ″) measurements. After the sol-gel process, the coating of manganese oxide (mixture of major Mn2O3 and minor Mn3O4) reduced the value of ɛ'. The lower the heat-treating temperature, the larger the decrease in ɛ'. The relative decrease in ɛ', compared with uncoated Fe3O4 nanoparticles, is 28.7, 23.5, and 20.0% for coated MnOx heat-treated at 300, 400, and 500 °C, respectively, while the relative decrease in ɛ″ is 74.1, 68.8, and 65.2%, respectively. In the present study, MnOx-coated Fe3O4 exhibited a significant decrease in dielectric loss tangent of ˜100% compared to that of uncoated NPs and can be of practical use for microwave components.

Gear distortion analysis due to heat treatment process

NASA Astrophysics Data System (ADS)

Guterres, Natalino F. D. S.; Rusnaldy, Widodo, Achmad

2017-01-01

One way to extend the life time of the gear is minimizing the distortion during the manufacturing process. One of the most important processes in manufacturing to produce gears is heat treatment process. The purpose of this study is to analyze the distortion of the gear after heat treatment process. The material of gear is AISI 1045, and it was designed with the module (m) 1.75, and a number of teeth (z) 29. Gear was heat-treated in the furnace at a temperature of 800°C, holding time of 30 minutes, and then quenched in water. Furthermore, surface hardening process was also performed on gear teeth at a temperature of 820°C and holding time of 35 seconds and the similar procedure of analysis was conducted. The hardness of gear after heat treatment average 63.2 HRC and the teeth surface hardness after gear to induction hardening was 64.9 HRC at the case depth 1 mm. The microstructure of tested gear are martensitic and pearlite. The highest distortion on tooth thickness to upper than 0.063 can cause high precision at the tooth contact is not appropriate. Besides the shrinkage of tooth thickness will also affect to contact angle because the size of gear tolerance was not standardized.

Effect of Cr Contents and Heat Treating on Reverted Austenite in Maraging Steel Weldments

NASA Astrophysics Data System (ADS)

Kim, S. W.; Lee, H. W.

2018-05-01

By conducting flux cored arc welding (FCAW) on maraging steels with Cr contents of 1.4 and 5.2 wt%, this study observed the effects of Cr content and heat treating on reverted austenite formation in welded maraging steel. Aging treatment was carried out at the temperatures of 450, 480 and 530 °C for 3 h in each condition. As the aging temperature increased, reverted austenite was formed along the interdendritic and intercellular grain boundaries, and the proportion of reverted austenite increased with increasing Cr addition. The aging process led to the segregation of Ti and Mo along the interdendritic and intercellular grain boundaries. Some of the welded specimens were subjected to solution heat treatment at 820 and 1250 °C for 1 h after welding, resulting in a decrease in reverted austenite fraction.

Effect of Cr Contents and Heat Treating on Reverted Austenite in Maraging Steel Weldments

NASA Astrophysics Data System (ADS)

Kim, S. W.; Lee, H. W.

2018-03-01

By conducting flux cored arc welding (FCAW) on maraging steels with Cr contents of 1.4 and 5.2 wt%, this study observed the effects of Cr content and heat treating on reverted austenite formation in welded maraging steel. Aging treatment was carried out at the temperatures of 450, 480 and 530 °C for 3 h in each condition. As the aging temperature increased, reverted austenite was formed along the interdendritic and intercellular grain boundaries, and the proportion of reverted austenite increased with increasing Cr addition. The aging process led to the segregation of Ti and Mo along the interdendritic and intercellular grain boundaries. Some of the welded specimens were subjected to solution heat treatment at 820 and 1250 °C for 1 h after welding, resulting in a decrease in reverted austenite fraction.

Physical and chemical behavior of flowing endothermic jet fuels

NASA Astrophysics Data System (ADS)

Ward, Thomas Arthur

Hydrocarbon fuels have been used as cooling media for aircraft jet engines for decades. However, modern aircraft engines are reaching a practical heat transfer limit beyond which the convective heat transfer provided by fuels is no longer adequate. One solution is to use an endothermic fuel that absorbs heat through a series of pyrolytic chemical reactions. However, many of the physical and chemical processes involved in endothermic fuel degradation are not well understood. The purpose of this dissertation is to study different characteristics of endothermic fuels using experiments and computational models. In the first section, data from three flow experiments using heated Jet-A fuel and additives were analyzed (with the aid of CFD calculations) to study the effects of treated surfaces on surface deposition. Surface deposition is the primary impediment in creating an operational endothermic fuel heat exchanger system, because deposits can obstruct fuel pathways causing a catastrophic system failure. As heated fuel flows through a fuel system, trace species within the fuel react with dissolved O2 to form surface deposits. At relatively higher fuel temperatures, the dissolved O2 is depleted, and pyrolytic chemistry becomes dominant (at temperatures greater than ˜500 °C). In the first experiment, the dissolved O2 consumption of heated fuel was measured on different surface types over a range of temperatures. It is found that use of treated tubes significantly delays oxidation of the fuel. In the second experiment, the treated length of tubing was progressively increased, which varied the characteristics of the thermal-oxidative deposits formed. In the third experiment, pyrolytic surface deposition in either fully treated or untreated tubes is studied. It is found that the treated surface significantly reduced the formation of surface deposits for both thermal oxidative and pyrolytic degradation mechanisms. Moreover, it is found that the chemical reactions resulting in pyrolytic deposition on the untreated surface are more sensitive to pressure level than those causing pyrolytic deposition on the treated surface. The second section describes the development of a two-dimensional computational model of the heat and mass transport associated with a flowing fuel using a unique global chemical kinetics model. This model calculates the changing flow properties of a supercritical reacting fuel by use of experimentally derived proportional product distributions. The third section studies the effects of pressure on flowing; mildly-cracked, supercritical n-decane. The experimental results are studied with the aid of the computational model described in section 2, expanded to deal with variable pressures. The experiments indicate that increasing pressure enhances the processes in which n-decane converts to (C5--C9) n-alkane products instead of decomposing into lower molecular weight products (C1--C4): Increasing pressure also increases the overall conversion rate of supercritical n-decane flowing through a reactor. Computational modeling of the experiment shows how the flow properties are influenced by pressure. (Abstract shortened by UMI.)

Adsorption of mercury by carbonaceous adsorbents prepared from rubber of tyre wastes.

PubMed

Manchón-Vizuete, E; Macías-García, A; Nadal Gisbert, A; Fernández-González, C; Gómez-Serrano, V

2005-03-17

Rubber from tyre wastes has been used to prepare carbonaceous adsorbents and the products obtained have been tested as adsorbents for mercury in aqueous solution. The adsorbents have been prepared by applying thermal, chemical and combined (thermal and chemical or vice versa) treatments. Tyre rubber has been: heated at 400 or 900 degrees C for 2 h in N2, chemically-treated with H2SO4, HNO3 or H2SO4/HNO3 solution for 24 h, and in two successive steps first heated at 400 degrees C for 2h in N2 and then treated with a H2SO4/HNO3 solution for 24 h, or vice versa. Resultant products have been characterised in terms of elementary composition and textural properties. The adsorption of mercury has been studied from kinetic and equilibrium standpoints. The treatments effected to tyre rubber decrease the carbon content and the hydrogen content. The oxygen content and the nitrogen content increase for the chemically-treated products. The heat treatment of tyre rubber results in a larger development of surface area, microporosity, and mesoporosity than the chemical treatments. These treatments, however, produce a great creation of macropores. In comparison to the starting rubber, the adsorption process of mercury is faster when the material is heated or treated with the H2SO4, HNO3 or 1:3 H2SO4/HNO3 solution. These adsorbents are either a non-porous solid or possess a high mesopore volume or a wide pore size distribution in the macropore range. The adsorption capacity is larger for products prepared by heat, chemical and combined treatments of the rubber. A common textural characteristic of these adsorbents is their better developed microporosity. The ability to adsorb mercury is higher for the heated products than for the chemically-treated ones. The maximum adsorption of mercury is 211 mg g(-1). The constant Kf of the Freundlich equation is as high as 108.9 mg g(-1).

Pretreatment of coal during transport

DOEpatents

Johnson, Glenn E.; Neilson, Harry B.; Forney, Albert J.; Haynes, William P.

1977-04-19

Many available coals are "caking coals" which possess the undesirable characteristic of fusing into a solid mass when heated through their plastic temperature range (about 400.degree. C.) which temperature range is involved in many common treatment processes such as gasification, hydrogenation, carbonization and the like. Unless the caking properties are first destroyed, the coal cannot be satisfactorily used in such processes. A process is disclosed herein for decaking finely divided coal during its transport to the treating zone by propelling the coal entrained in an oyxgen-containing gas through a heated transport pipe whereby the separate transport and decaking steps of the prior art are combined into a single step.

Heat treatment of unclarified Escherichia coli homogenate improved the recovery efficiency of recombinant hepatitis B core antigen.

PubMed

Ng, Michelle Y T; Tan, Wen Siang; Abdullah, Norhafizah; Ling, Tau Chuan; Tey, Beng Ti

2006-10-01

Heat precipitation procedure has been regularly incorporated as a selective purification step in various thermostable proteins expressed in different hosts. This method is efficient in precipitation of most of the host proteins and also deactivates various host proteases that can be harmful to the desired gene products. In this study, introduction of heat treatment procedure in the purification of hepatitis B core antigen (HBcAg) produced in Escherichia coli has been investigated. Thermal treatment of the cell homogenate at 60 degrees C for 30 min prior to subsequent clarification steps has resulted in 1.4 times and 18% higher in purity and recovery yield, respectively, compared to the non-heat-treated cell homogenate. In direct capture of HBcAg by using anion-exchangers from unclarified feedstock, pre-conditioning the feedstock by heat treatment at 60 degrees C for 45 min has increased the recovery yield of HBcAg by 2.9-fold and 42% in purity compared to that treated for 10 min. Enzyme-linked immunosorbent assay (ELISA) analysis showed that the antigenicity of the core particles was not affected by the heat treatment process.

Influence of Processing Techniques on Microstructure and Mechanical Properties of a Biodegradable Mg-3Zn-2Ca Alloy

PubMed Central

Doležal, Pavel; Zapletal, Josef; Fintová, Stanislava; Trojanová, Zuzanka; Greger, Miroslav; Roupcová, Pavla; Podrábský, Tomáš

2016-01-01

New Mg-3Zn-2Ca magnesium alloy was prepared using different processing techniques: gravity casting as well as squeeze casting in liquid and semisolid states. Materials were further thermally treated; thermal treatment of the gravity cast alloy was additionally combined with the equal channel angular pressing (ECAP). Alloy processed by the squeeze casting in liquid as well as in semisolid state exhibit improved plasticity; the ECAP processing positively influenced both the tensile and compressive characteristics of the alloy. Applied heat treatment influenced the distribution and chemical composition of present intermetallic phases. Influence of particular processing techniques, heat treatment, and intermetallic phase distribution is thoroughly discussed in relation to mechanical behavior of presented alloys. PMID:28774000

Histopathological Changes in Third-Instar and Adult Anastrepha ludens (Diptera: Tephritidae) After in vitro Heat Treatment

PubMed Central

Caro-Corrales, Lorena; Caro-Corrales, Jose; Valdez-Ortiz, Angel; Lopez-Valenzuela, Jose; Lopez-Moreno, Hector; Coronado-Velazquez, Daniel; Hernandez-Ortiz, Emilio; Rendon-Maldonado, Jose

2015-01-01

The Mexican fruit fly, Anastrepha ludens Loew (Diptera: Tephritidae), is one of the most harmful pests of mango causing direct damage by oviposition on the fruit pulp. Mango for export is subjected to hydrothermal treatment as a quarantine method for the control of this pest, but exposure to heat for long periods of time reduces considerably the quality and shelf-life of treated fruit. The aim of this work was to study morphological changes of third-instar larvae and adults of A. ludens after in vitro exposure to high temperature at sublethal times. A heating block system was used to expose larvae at 46.1°C for 19.6 and 12.9 min, producing 94.6 and 70% mortality, respectively. Treated larvae were processed for optical microscopy. A fraction of surviving treated larvae was separated into containers with artificial diet to allow development into adults. Adult sexual organs were dissected and processed for transmission electron microscopy analysis. Results showed that 94.6% of the treated larvae died at 46.1°C for 19.6 min and none of the surviving larvae eclosed to adulthood, as they developed as malformed puparia. For the in vitro treatment at 46.1°C during 12.9 min, 70% of the treated larvae died and only 3.75% reached the adult stage, but ultrastructural damage in the male testes and in the female ovaries was observed. Additionally, 11.1% of the adult flies from the in vitro treatment also showed wing malformation and were incapable of flying. The analysis showed that surviving flies were unable to reproduce. PMID:25797796

Heating hydrocarbon containing formations in a line drive staged process

DOEpatents

Miller, David Scott [Katy, TX

2009-07-21

Method for treating a hydrocarbon containing formation are described herein. Methods may include providing heat to a first section of the formation with one or more first heaters in the first section. First hydrocarbons may be heated in the first section such that at least some of the first hydrocarbons are mobilized. At least some of the mobilized first hydrocarbons may be produced through a production well located in a second section of the formation. The second section may be located substantially adjacent to the first section. A portion of the second section may be provided some heat from the mobilized first hydrocarbons, but is not conductively heated by heat from the first heaters. Heat may be provided to the second section with one or more second heaters in the second section to further heat the second section.

Influence of food matrix on outgrowth heterogeneity of heat damaged Bacillus cereus spores.

PubMed

Warda, Alicja K; den Besten, Heidy M W; Sha, Na; Abee, Tjakko; Nierop Groot, Masja N

2015-05-18

Spoilage of heat treated foods can be caused by the presence of surviving spore-formers. It is virtually impossible to prevent contamination at the primary production level as spores are ubiquitous present in the environment and can contaminate raw products. As a result spore inactivation treatments are widely used by food producing industries to reduce the microbial spore loads. However consumers prefer mildly processed products that have less impact on its quality and this trend steers industry towards milder preservation treatments. Such treatments may result in damaged instead of inactivated spores, and these spores may germinate, repair, and grow out, possibly leading to quality and safety issues. The ability to repair and grow out is influenced by the properties of the food matrix. In the current communication we studied the outgrowth from heat damaged Bacillus cereus ATCC 14579 spores on Anopore membrane, which allowed following outgrowth heterogeneity of individual spores on broccoli and rice-based media as well as standard and mildly acidified (pH 5.5) meat-based BHI. Rice, broccoli and BHI pH 5.5 media resulted in delayed outgrowth from untreated spores, and increased heterogeneity compared to BHI pH 7.4, with the most pronounced effect in rice media. Exposure to wet heat for 1 min at 95 °C caused 2 log inactivation and approximately 95% of the spores in the surviving fraction were damaged resulting in substantial delay in outgrowth based on the time required to reach a maximum microcolony size of 256 cells. The delay was most pronounced for heat-treated spores on broccoli medium followed by spores on rice media (both untreated and treated). Interestingly, the increase in outgrowth heterogeneity of heat treated spores on BHI pH 7.4 was more pronounced than on rice, broccoli and BHI pH 5.5 conceivably reflecting that conditions in BHI pH 7.4 better support spore damage repair. This study compares the effects of three main factors, namely heat treatment, pH of BHI and the effect of food matrix highlighting the impact of different (model) food recovery media on outgrowth efficiency and heterogeneity of non-heat-treated and heat-damaged B. cereus spores. Copyright © 2015. Published by Elsevier B.V.

Method of thermally processing superplastically formed aluminum-lithium alloys to obtain optimum strengthening

NASA Technical Reports Server (NTRS)

Anton, Claire E. (Inventor)

1993-01-01

Optimum strengthening of a superplastically formed aluminum-lithium alloy structure is achieved via a thermal processing technique which eliminates the conventional step of solution heat-treating immediately following the step of superplastic forming of the structure. The thermal processing technique involves quenching of the superplastically formed structure using static air, forced air or water quenching.

2. SALEMBROSIUS CONTINUOUS GASFIRED HEAT TREATING LINE AT HEAT TREATMENT ...

Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

2. SALEM-BROSIUS CONTINUOUS GAS-FIRED HEAT TREATING LINE AT HEAT TREATMENT PLANT OF THE DUQUESNE WORKS. - U.S. Steel Duquesne Works, Heat Treatment Plant, Along Monongahela River, Duquesne, Allegheny County, PA

Similarity curve in solidification process of latent-heat energy storage unit with longitudinally straight fins; Part 1, Effect of Stefan number on applicability of similarity rule

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kaino, Koji

1994-09-01

Similarity curves for different Biot numbers are known to become indistinguishable with decreasing Stefan number; in other words, the similarity rule becomes more applicable for smaller Stefan number. In such a finned-tube-type storage unit as treated in this study, it has been found that the effect of Stefan number on the similarity curve varies with the number of fins. Sensible heat liberated during the solidification process has been calculated individually in a phase-change material with a heat-transfer tube and fins, and represented as a function of the frozen fraction for two specified values of Biot number, 0.1 and 1000, undermore » specified conditions of Stefan number and the number on fins. The latent-heat contribution to heat flow out of the storage unit has been examined in comparison with the sensible-heat contribution. The latent- and sensible-heat contributions are almost inversely related. This inverse relationship reduces the effect of the Stefan number on the applicability of the similarity rule.« less

Comparison of VOC emissions between air-dried and heat-treated Norway spruce ( Picea abies), Scots pine ( Pinus sylvesteris) and European aspen ( Populus tremula) wood

NASA Astrophysics Data System (ADS)

Hyttinen, Marko; Masalin-Weijo, Marika; Kalliokoski, Pentti; Pasanen, Pertti

2010-12-01

Heat-treated wood is an increasingly popular decoration material. Heat-treatment improves dimensional stability of the wood and also prevents rot fungus growth. Although production of heat-treated wood has been rapidly increasing, there is only little information about the VOC emissions of heat-treated wood and its possible influences on indoor air quality. In the present study, VOC emissions from three untreated (air-dried) and heat-treated wood species were compared during a four weeks test period. It appeared that different wood species had clearly different VOC emission profiles. Heat-treatment was found to decrease VOC emissions significantly and change their composition. Especially, emissions of terpenes decreased from softwood samples and aldehydes from European aspen samples. Emissions of total aldehydes and organic acids were at the same level or slightly higher from heat treated than air-dried softwood samples. In agreement with another recent study, the emissions of furfural were found to increase and those of hexanal to decrease from all the wood species investigated. In contrast to air-dried wood samples, emissions of VOCs were almost in steady state from heat treated wood samples even in the beginning of the test.

Demonstration of the Impact of Thermomagnetic Processing on Cast Aluminum Alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ludtka, Gerard Michael; Murphy, Bart L.; Rios, Orlando

2017-10-01

This project builds on an earlier Manufacturing Demonstration Facility Technical Collaboration phase 1 project to investigate application of high magnetic fields during solution heat treating and aging of three different cast aluminum alloys.

Superconducting MgB2 wires with vanadium diffusion barrier

NASA Astrophysics Data System (ADS)

Hušek, I.; Kováč, P.; Melišek, T.; Kulich, M.; Rosová, A.; Kopera, L.; Szundiová, B.

2017-10-01

Single-core MgB2 wires with a vanadium barrier and Cu stabilization have been made by the in situ powder-in-tube (PIT) and internal magnesium diffusion (IMD) into boron processes. Heat treatment of PIT wires was done at the temperature range of 650 °C-850 °C/30 min. Critical currents of differently treated MgB2/V/Cu wires have been measured and related with the structure of MgB2. It was found that critical current density of MgB2/V wire annealed above 700 °C decreases rapidly. The obtained results clearly show that vanadium is a well formable metal and can be applied as an effective diffusion barrier for MgB2 wires heat-treated at temperatures ≤700 °C. This temperature limit is well applicable for MgB2 wires with high current densities made by PIT and also by the IMD process.

Whey acerola-flavoured drink submitted ohmic heating processing: Is there an optimal combination of the operational parameters?

PubMed

Cappato, Leandro P; Ferreira, Marcus Vinícius S; Pires, Roberto P S; Cavalcanti, Rodrigo N; Bisaggio, Rodrigo C; Freitas, Mônica Q; Silva, Marcia C; Cruz, Adriano G

2018-04-15

Whey acerola-flavoured drink was treated using ohmic heating (OH) at 65°C for 30min to evaluate different frequencies (10, 100 and 1000Hz with 25V) and voltages (45, 60 and 80V at 60Hz) and by conventional heating (CH) with the same temperature profile (65°C/30min). Rheology parameters, color changes (h°, C∗, ΔE) microstructure (optical microscopy), and ascorbic acid (AA) degradation kinetics were performed. AA degradation rates ranged from 1.7 to 29.3% and from 2.8 to 24.8% for OH and CH, respectively. The beverages treated with both processes exhibited a pseudo-plastic behavior (n<1), higher saturation (C∗), lesser reddish color (h°), and higher color variations (ΔE∗). In microstructure analysis, OH (1000Hz-25V and 80V-60Hz) was able to rupture the cell structure. The best results were observed at low frequencies and voltage OH processes on whey acerola-flavoured drinks should be performed at low frequencies and voltages (≤100Hz and 45V), an alternating current (A/C). However, despite the use of inert electrodes, the existence of corrosion was not evaluated, being an important information to be investigated. Copyright © 2017 Elsevier Ltd. All rights reserved.

Effects of extrusion, infrared and microwave processing on Maillard reaction products and phenolic compounds in soybean.

PubMed

Zilić, Slađana; Mogol, Burçe Ataç; Akıllıoğlu, Gül; Serpen, Arda; Delić, Nenad; Gökmen, Vural

2014-01-15

The Maillard reaction indicators furosine, hydroxymethylfurfural (HMF), acrylamide and color were determined to evaluate heat effects induced during extrusion, infrared and microwave heating of soybean. In addition, the present paper aimed to study changes in the phenolic compounds, as well as in the overall antioxidant properties of different soybean products in relation to heating at 45-140 °C during the processes. Soybean proteins were highly sensible to Maillard reaction and furosine was rapidly formed under slight heating conditions during extrusion and infrared heating. Microwave heating at lower temperatures for a longer time yielded lower acrylamide levels in the final soybean products, as a result of its partial degradation. However, during infrared heating, acrylamide formation greatly increased with decreasing moisture content. After a short time of extrusion and infrared heating at 140 °C and microwave heating at 135 °C for 5 min, concentrations of HMF increased to 11.34, 26.21 and 34.97 µg g(-1), respectively. The heating conditions caused formation of acrylamide, HMF and furosine in high concentration. The results indicate that the complex structure of soybeans provides protection of phenolic compounds from thermal degradation, and that Maillard reaction products improved the antioxidant properties of heat-treated soybean. © 2013 Society of Chemical Industry.

A container for heat treating materials in microwave ovens

DOEpatents

Holcombe, C.E.; Dykes, N.L.; Kimrey, H.D. Jr.; Mills, J.E.

1988-01-26

The efficiency of a microwave oven of a conventional two-source configuration and energy level is increased by providing the oven with a container for housing a refractory material to be treated. The container is formed to top and bottom walls transparent to microwaves while the sidewalls, in a circular configuration, are formed of a nonmetallic material opaque to microwave radiation for reflecting the radiation penetrating the top and bottom walls radially inwardly into the center of the container wherein a casket of heat-insulating material is provided for housing the material to be heat treated. The reflection of the microwave radiation from the sidewalls increases the concentration of the microwaves upon the material being heat treated while the concentration of the microwaves upon the material being heat treated while the casket retains the heat to permit the heating of the material to a substantially higher temperature than achievable in the oven without the container.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sackl, S., E-mail: stephanie.sackl@unileoben.ac.at

The continuous heat treatment of high speed steels reduces the process times from several hours to a few minutes. The resulting cost savings as well as lower decarburisation and distortion make the continuous heat treatment favourable over an isothermal heat treatment. However, the microstructure-property relationship during continuous heat treatments is far from being well understood. In order to identify the key microstructural features for the future optimisation of continuous heat treatments of high speed steels this study compares a current industrial continuous and an isothermal heat treatment of steel HS 6-5-2 by means of light optical microscopy, scanning electron microscopy,more » X-ray diffraction, atom probe tomography, and red hardness. After continuous hardening the content of primary carbides is higher and the amount of retained austenite is lower compared to isothermal hardening. Due to the reduced time for dissolution of primary carbides a lower content of alloying elements is present in the martensitic matrix for subsequent tempering. Therefore, the chemical composition of the secondary hardening carbides after tempering is different for a continuous heat treatment. Although the difference in chemistry is quite pronounced, the deterioration of the hardness at elevated temperatures, which strongly influences the performance characteristics of the finished parts, is not altered. - Highlights: •We studied the continuous and isothermal heat treatment of the steel HS 6-5-2. •The amount of primary carbides is higher in a continuously heat treated steel. •The chemistry of secondary hardening carbides changes during tempering. •Continuously heat treated steels exhibit the same performance characteristics.« less

Adsorption of benzene and toluene from aqueous solutions onto activated carbon and its acid and heat treated forms: influence of surface chemistry on adsorption.

PubMed

Wibowo, N; Setyadhi, L; Wibowo, D; Setiawan, J; Ismadji, S

2007-07-19

The influence of surface chemistry and solution pH on the adsorption of benzene and toluene on activated carbon and its acid and heat treated forms were studied. A commercial coal-based activated carbon F-400 was chosen as carbon parent. The carbon samples were obtained by modification of F-400 by means of chemical treatment with HNO3 and thermal treatment under nitrogen flow. The treatment with nitric acid caused the introduction of a significant number of oxygenated acidic surface groups onto the carbon surface, while the heat treatment increases the basicity of carbon. The pore characteristics were not significantly changed after these modifications. The dispersive interactions are the most important factor in this adsorption process. Activated carbon with low oxygenated acidic surface groups (F-400Tox) has the best adsorption capacity.

Powerless fluxes and forces, and change of scale in irreversible thermodynamics

NASA Astrophysics Data System (ADS)

Ostoja-Starzewski, M.; Zubelewicz, A.

2011-08-01

We show that the dissipation function of linear processes in continuum thermomechanics may be treated as the average of the statistically fluctuating dissipation rate on either coarse or small spatial scales. The first case involves thermodynamic orthogonality due to Ziegler, while the second one involves powerless forces in a general solution of the Clausius-Duhem inequality according to Poincaré and Edelen. This formulation is demonstrated using the example of parabolic versus hyperbolic heat conduction. The existence of macroscopic powerless heat fluxes is traced here to the hidden dissipative processes at lower temporal and spatial scales.

Mechanism of the Bauschinger effect in Al-Ge-Si alloys

DOE PAGES

Gan, Wei; Bong, Hyuk Jong; Lim, Hojun; ...

2016-12-07

Here, wrought Al-Ge-Si alloys were designed and produced to ensure dislocation bypass strengthening ("hard pin" precipitates) without significant precipitate cutting/shearing ("soft pin" precipitates). They were processed from the melt, solution heat treated and aged.

Heat Transfer Analysis of Localized Heat-Treatment for Grade 91 Steel

NASA Astrophysics Data System (ADS)

Walker, Jacob D.

Many of the projects utilizing Grade 91 steel are large in scale, therefore it is necessary to assemble on site. The assembly of the major pieces requires welding in the assembly; this drastically changes the superior mechanical properties of Grade 91 steel that it was specifically developed for. Therefore, because of the adverse effects of welding on the mechanical properties of Grade 91, it is necessary to do a localized post weld heat treatment. As with most metallic materials grade 91 steel requires a very specific heat treatment process. This process includes a specific temperature and duration at that temperature to achieve the heat treatment desired. Extensive research has been done to determine the proper temperatures and duration to provide the proper microstructure for the superior mechanical properties that are inherent to Grade 91 steel. The welded sections are typically large structures that require local heat treatments and cannot be placed in an oven. The locations of these structures vary from indoors in a controlled environment to outdoors with unpredictable environments. These environments can be controlled somewhat, however in large part the surrounding conditions are unchangeable. Therefore, there is a need to develop methods to accurately apply the surrounding conditions and geometries to a theoretical model in order to provide the proper requirements for the local heat treatment procedure. Within this requirement is the requirement to define unknowns used in the heat transfer equations so that accurate models can be produced and accurate results predicted. This study investigates experimentally and numerically the heat transfer and temperature fields of Grade 91 piping in a local heat treatment. The objective of this thesis research is to determine all of the needed heat transfer coefficients. The appropriate heat transfer coefficients are determined through the inverse heat conduction method utilizing a ceramic heat blanket. This will be done through an inverse method by collecting actual data from different conditions and temperatures. Then the heat transfer coefficients are used to set up a model to determine the appropriate post-weld heat treatment conditions for Grade 91 steel. This will enable one to use the derived coefficients to run a forward analysis with the specific geometry and conditions they will encounter in the heat treatment process for their application. The analysis will provide a theoretical determination of time and temperatures needed to maintain the temperature for the proper time needed to properly heat treat the welded section in the desired areas that have been joined together through a welding process. Finally time and temperature combinations are compared with experimentally measured data. The forward model code applied to the parameters of the heat-treatment can then appropriately assist to determine the proper post-weld heat treatment conditions for the desired toughness and creep properties. This research is very beneficial to the joining of metals industry because it provides a way to ensure the method used to heat treat the welded section is being properly done, and the required heat treatment is achieved. It is applicable to many different geometries so that it can be modified to specific situations.

Aluminum alloy AA-6061 and RSA-6061 heat treatment for large mirror applications

NASA Astrophysics Data System (ADS)

Newswander, T.; Crowther, B.; Gubbels, G.; Senden, R.

2013-09-01

Aluminum mirrors and telescopes can be built to perform well if the material is processed correctly and can be relatively low cost and short schedule. However, the difficulty of making high quality aluminum telescopes increases as the size increases, starting with uniform heat treatment through the thickness of large mirror substrates. A risk reduction effort was started to build and test a ½ meter diameter super polished aluminum mirror. Material selection, the heat treatment process and stabilization are the first critical steps to building a successful mirror. In this study, large aluminum blanks of both conventional AA-6061 per AMS-A-22771 and RSA AA-6061 were built, heat treated and stress relieved. Both blanks were destructively tested with a cut through the thickness. Hardness measurements and tensile tests were completed. We present our results in this paper and make suggestions for modification of procedures and future work.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Anameric, B.; Kawatra, S.K.

The pig iron nugget process is gaining in importance as an alternative to the traditional blast furnace. Throughout the process, self-reducing-fluxing dried greenballs composed of iron ore concentrate, reducing-carburizing agent (coal), flux (limestone) and binder (bentonite) are heat-treated. During the heat treatment, dried greenballs are first transformed into direct reduced iron (DRI), then to transition direct reduced iron (TDRI) and finally to pig iron nuggets. The furnace temperature and/or residence time and the corresponding levels of carburization, reduction and metallization dictate these transformations. This study involved the determination of threshold furnace temperatures and residence times for completion of all ofmore » the transformation reactions and pig iron nugget production. The experiments involved the heat treatment of self-reducing-fluxing dried greenballs at various furnace temperatures and residence times. The products of these heat treatments were identified by utilizing optical microscopy, apparent density and microhardness measurements.« less

The impact of fouling on the process performance of the thermal treatment of pig slurry using tubular heat exchangers.

PubMed

Cunault, C; Burton, C H; Pourcher, A M

2013-03-15

The aim of this study was to determine the kinetics of fouling and their influence on the performance of a thermal treatment process used for sanitisation of pig slurry. Two temperatures (55 °C and 80 °C) were investigated. One trial was carried out at 55 °C and 80 °C in which the slurry was not re-circulated and one trial at 80 °C in which 100% or 50% of the slurry was re-circulated. Fouling of the heat exchangers was assessed by on-line monitoring of the drop in pressure, changes in treatment temperature, heat transfer coefficients, heat recycling rate, and energy consumption. Similar energy consumption of around 38 kWh m(-3) of effluent was observed at the two temperatures. The operating periods prior to excessive fouling or blockage were 18 days at 55 °C and four days at 80 °C. Recycling treated manure to obtain 50% dilution of the raw feed increased the viable operating period to 14 days at 80 °C but doubled energy consumption. At 55 °C, the significant drop in the target temperature (>7 °C) with fouling severely jeopardised the process. The nature of the decline in performance suggests that the main fouling mechanisms were bio-fouling at 55 °C and organic/mineral deposits at 80 °C. Recycling treated manure enabled the operating period to be extended but increased the total cost of heating. One hundred percent recycling showed that the fouling potential of the manure was largely eliminated after one thermal treatment, suggesting a pretreatment may be advantageous. Copyright © 2013 Elsevier Ltd. All rights reserved.

Rock Smelting of Copper Ores with Waste Heat Recovery

NASA Astrophysics Data System (ADS)

Norgate, Terry; Jahanshahi, Sharif; Haque, Nawshad

It is generally recognised that the grades of metallic ores are falling globally. This trend can be expected to increase the life cycle-based energy requirement for primary metal production due to the additional amount of material that must be handled and treated in the mining and mineral processing stages of the metal production life cycle. Rock (or whole ore) smelting has been suggested as a possible alternative processing route for low grade ores with a potentially lower energy intensity and environmental impact than traditional processing routes. In this processing route, the beneficiation stage is eliminated along with its associated energy consumption and greenhouse gas emissions, but this is partially offset by the need for more solid material to be handled and heated up to smelting temperatures. A life cycle assessment study was carried out to assess the potential energy and greenhouse gas benefits of a conceptual flowsheet of the rock smelting process, using copper ore as an example. Recovery and utilisation of waste heat in the slag (via dry slag granulation) and offgas streams from the smelting step was also included in the study, with the waste heat being utilised either for thermal applications or electricity generation.

75 FR 57864 - Importation of Wooden Handicrafts from China

Federal Register 2010, 2011, 2012, 2013, 2014

2010-09-23

... handicrafts are under 6 inches in diameter and treated with methyl bromide, they must be treated with heat... requirement that would have required that, unless the wooden handicraft is 6 inches or less and treated with methyl bromide, it must be treated with heat treatment in accordance with Sec. 319.40-7(c) or heat...

Military Curricula for Vocational & Technical Education. Metals Processing Specialist, Block VII, Classroom Course 13-8.

ERIC Educational Resources Information Center

Ohio State Univ., Columbus. National Center for Research in Vocational Education.

These curriculum materials are the fourth section of a four-part, secondary-postsecondary-level course in metals processing. The course is one of a number of military-developed curriculum packages selected for adaptation to vocational instruction and curriculum development in a civilian setting. Block VII deals with heat treating, hardness…

Synthesis of increased-density bismuth-based superconductors with cold isostatic pressing and heat treating

DOEpatents

Lanagan, Michael T.; Picciolo, John J.; Dorris, Stephen E.

1997-01-01

The present invention is directed to a process for producing high temperature superconducting ceramic materials. More particularly, the present invention is directed to a process that enhances the densification of Bi.sub.1.8 Pb.sub.0.4 Sr.sub.2 Ca.sub.2 Cu.sub.3 O.sub.10 "BSCCO" ceramics.

In Vitro Determination of the Allergenic Potential of Egg White in Processed Meat

PubMed Central

Hildebrandt, Sabine; Schütte, Larsen; Stoyanov, Stefan; Hammer, Günther; Steinhart, Hans; Paschke, Angelika

2010-01-01

Hen's egg white has been reported as a causative agent of allergic reactions, with ovalbumin, conalbumin, ovomucoid, and lysozyme being the major allergens. However, little is known about the effects of processing with heat and high pressure on the allergenicity of egg white proteins as ingredients in meat. For this purpose, the allergenic characteristics of such treated preparations were studied. The IgE-binding capacity was analyzed by EAST inhibition in raw and processed meat preparations using sera from patients with hen's egg specific IgE. Increasing heat treatment as well as the application of high pressure decreased IgE binding, which is a measure of allergenic potential. The combined application of heat (70°C) and high pressure had synergistic effects in reducing the allergenic potential nearly twice as the sum of the single treatments conducted separately. PMID:20948881

Effect of heating strategies on whey protein denaturation--Revisited by liquid chromatography quadrupole time-of-flight mass spectrometry.

PubMed

Akkerman, M; Rauh, V M; Christensen, M; Johansen, L B; Hammershøj, M; Larsen, L B

2016-01-01

Previous standards in the area of effect of heat treatment processes on milk protein denaturation were based primarily on laboratory-scale analysis and determination of denaturation degrees by, for example, electrophoresis. In this study, whey protein denaturation was revisited by pilot-scale heating strategies and liquid chromatography quadrupole time-of-flight mass spectrometer (LC/MC Q-TOF) analysis. Skim milk was heat treated by the use of 3 heating strategies, namely plate heat exchanger (PHE), tubular heat exchanger (THE), and direct steam injection (DSI), under various heating temperatures (T) and holding times. The effect of heating strategy on the degree of denaturation of β-lactoglobulin and α-lactalbumin was determined using LC/MC Q-TOF of pH 4.5-soluble whey proteins. Furthermore, effect of heating strategy on the rennet-induced coagulation properties was studied by oscillatory rheometry. In addition, rennet-induced coagulation of heat-treated micellar casein concentrate subjected to PHE was studied. For skim milk, the whey protein denaturation increased significantly as T and holding time increased, regardless of heating method. High denaturation degrees were obtained for T >100°C using PHE and THE, whereas DSI resulted in significantly lower denaturation degrees, compared with PHE and THE. Rennet coagulation properties were impaired by increased T and holding time regardless of heating method, although DSI resulted in less impairment compared with PHE and THE. No significant difference was found between THE and PHE for effect on rennet coagulation time, whereas the curd firming rate was significantly larger for THE compared with PHE. Micellar casein concentrate possessed improved rennet coagulation properties compared with skim milk receiving equal heat treatment. Copyright © 2016 American Dairy Science Association. Published by Elsevier Inc. All rights reserved.

5. DETAIL VIEW OF AJAX MAGNETHERMIC HEAT TREATING LINE AT ...

Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

5. DETAIL VIEW OF AJAX MAGNETHERMIC HEAT TREATING LINE AT THE HEAT TREATMENT PLANT OF THE DUQUESNE WORKS. - U.S. Steel Duquesne Works, Heat Treatment Plant, Along Monongahela River, Duquesne, Allegheny County, PA

4. GENERAL VIEW OF AJAX MAGNETHERMIC HEAT TREATING LINE AT ...

Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

4. GENERAL VIEW OF AJAX MAGNETHERMIC HEAT TREATING LINE AT THE HEAT TREATMENT PLANT OF THE DUQUESNE WORKS. - U.S. Steel Duquesne Works, Heat Treatment Plant, Along Monongahela River, Duquesne, Allegheny County, PA

Design of Tomato Drying System by Utilizing Brine Geothermal

NASA Astrophysics Data System (ADS)

Afuar, W.; Sibarani, B.; Abdurrahman, G.; Hendrarsakti, J.

2016-09-01

Cultivation of tomato plants in Indonesia has been started since 1961.Tomatoes generally will rot in three days if left on storage. Moreover, low quality tomatoes have cheaper price. After harvested, tomatoes need to be treated by drying process so it can last longer. Energy for drying tomatoes can be obtained by utilizing heat from geothermal brine. Purpose of this research is to design a tomato drying system by extracting heat of geothermal brine from separator with certain flow rate to heat up water by using a heat exchanger. Furthermore, this water will be used to heat up the surrounding air which is circulated by blower system to heat up the tomatoes chamber. Tomatoes drying process needs temperature range of 50-70°C to evaporate water content from 95.7% to 26%. After that treatment, the tomatoes are expected to have better durability. The objective of this study is to determine the quantity of hot brine which is needed for drying tomatoes and to design a drying system so that tomatoes can last longer.

Comparison of the effects of different heat treatment processes on rheological properties of cake and bread wheat flours.

PubMed

Bucsella, Blanka; Takács, Ágnes; Vizer, Viktoria; Schwendener, Urs; Tömösközi, Sándor

2016-01-01

Dry and hydrothermal heat treatments are efficient for modifying the technological-functional and shelf-life properties of wheat milling products. Dry heat treatment process is commonly used to enhance the volume of cakes. Hydrothermal heat treatment makes wheat flours suitable as thickener agents. In this study, cake and bread wheat flours that differed in baking properties were exposed to dry (100 °C, 12 min) and hydrothermal (95 °C, 5 min, 5-20 l/h water) heat treatments. Rheological differences caused by the treatments were investigated in a diluted slurry and in a dough matrix. Dry heat treatment resulted in enhanced dough stability. This effect was significantly higher in the cake flour than the bread flour. Altered viscosity properties of the bread flour in the slurry matrix were also observed. The characteristics of hydrothermally treated samples showed matrix dependency: their viscosity increases in the slurry and decreases in the dough matrix. These results can support us to produce flour products with specific techno-functional properties. Copyright © 2015 Elsevier Ltd. All rights reserved.

Inactivation of chemical and heat-resistant spores of Bacillus and Geobacillus by nitrogen cold atmospheric plasma evokes distinct changes in morphology and integrity of spores.

PubMed

van Bokhorst-van de Veen, Hermien; Xie, Houyu; Esveld, Erik; Abee, Tjakko; Mastwijk, Hennie; Nierop Groot, Masja

2015-02-01

Bacterial spores are resistant to severe conditions and form a challenge to eradicate from food or food packaging material. Cold atmospheric plasma (CAP) treatment is receiving more attention as potential sterilization method at relatively mild conditions but the exact mechanism of inactivation is still not fully understood. In this study, the biocidal effect by nitrogen CAP was determined for chemical (hypochlorite and hydrogen peroxide), physical (UV) and heat-resistant spores. The three different sporeformers used are Bacillus cereus a food-borne pathogen, and Bacillus atrophaeus and Geobacillus stearothermophilus that are used as biological indicators for validation of chemical sterilization and thermal processes, respectively. The different spores showed variation in their degree of inactivation by applied heat, hypochlorite, hydrogen peroxide, and UV treatments, whereas similar inactivation results were obtained with the different spores treated with nitrogen CAP. G. stearothermophilus spores displayed high resistance to heat, hypochlorite, hydrogen peroxide, while for UV treatment B. atrophaeus spores are most tolerant. Scanning electron microscopy analysis revealed distinct morphological changes for nitrogen CAP-treated B. cereus spores including etching effects and the appearance of rough spore surfaces, whereas morphology of spores treated with heat or disinfectants showed no such changes. Moreover, microscopy analysis revealed CAP-exposed B. cereus spores to turn phase grey conceivably because of water influx indicating damage of the spores, a phenomenon that was not observed for non-treated spores. In addition, data are supplied that exclude UV radiation as determinant of antimicrobial activity of nitrogen CAP. Overall, this study shows that nitrogen CAP treatment has a biocidal effect on selected Bacillus and Geobacillus spores associated with alterations in spore surface morphology and loss of spore integrity. Copyright © 2014 Elsevier Ltd. All rights reserved.

DEMONSTRATION BULLETIN: IN SITU VITRIFICATION - GEOSAFE CORPORATION

EPA Science Inventory

in Situ Vitrification (ISV) is designed to treat soils, sludges, sediments, and mine tailings contaminated with organic and inorganic compounds. The process uses electrical current to heat (mett) and vitrify the soil in place. Organic contaminants are decomposed by the extreme h...

Effective recycling of manganese oxide cathodes for lithium based batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Poyraz, Altug S.; Huang, Jianping; Cheng, Shaobo

A facile cathode recycling process is demonstrated where the previously used binder-free self-supporting cathodes (BFSSC) are removed from a cell, heat treated, and then inserted into a new cell restoring the delivered capacity and cycle life.

Processing Issues for Preliminary Melts of the Intermetallic Compound 60-NITINOL

NASA Technical Reports Server (NTRS)

Stanford, Malcolm K.; Thomas, Fransua; DellaCorte, Christopher

2012-01-01

The effect of various high temperature heat treatments and cooling rates on the hardness of cast 60-NITINOL (60wt%Ni- 40wt%Ti) was studied. The hardness ranged from approximately 33 HRC for annealed specimens to 63 HRC for water quenched specimens. Aging did not have a further effect on the hardness of the heat-treated and quenched material. The issue of material contamination and its possible effect on quench cracking during heat treatment above 1000 C was explored. The Charpy impact energy of the material was found to be relatively low (ranging from 0.4 to 1.0 J) and comparable to that of cast magnesium. Selection of service environments and applications for this material based on these findings should consider the processing route by which it was produced.

6. HOT BED FOR THE AJAX MAGNETHERMIC HEAT TREATING LINE ...

Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

6. HOT BED FOR THE AJAX MAGNETHERMIC HEAT TREATING LINE AT THE HEAT TREATMENT PLANT OF THE DUQUESNE WORKS. - U.S. Steel Duquesne Works, Heat Treatment Plant, Along Monongahela River, Duquesne, Allegheny County, PA

8. QUENCHING MECHANISM FOR THE CONTINUOUS ELECTRIC FURNACE HEAT TREATING ...

Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

8. QUENCHING MECHANISM FOR THE CONTINUOUS ELECTRIC FURNACE HEAT TREATING LINE AT THE HEAT TREATMENT PLANT OF THE DUQUESNE WORKS. - U.S. Steel Duquesne Works, Heat Treatment Plant, Along Monongahela River, Duquesne, Allegheny County, PA

The health and technological implications of a better control of neoformed contaminants by the food industry.

PubMed

Birlouez-Aragon, I; Morales, F; Fogliano, V; Pain, J-P

2010-06-01

The recent discovery of the presence of variable amounts of the carcinogenic compound acrylamide in a wide range of severely heat-treated food products, such as fried potatoes, biscuits, bread and coffee or malt, as a result of the heat process, has induced an important research in the area of the Maillard reaction in food. The interaction between a specific food composition and the heat process applied results in the development of complex oxidation and glycation reactions, which give rise to a mixture of flavoured compounds and possible neoformed contaminants (NFC). Recommendations by the European Commission aim at monitoring the content of major NFC, such as acrylamide and furan, in a list of food products commercialized in Europe. On the other hand, the Commission for European Normalization (CEN) has created recently a new workgroup (WG13) responsible for normalization of analytical method for NFC assessment. The European collective research ICARE was carried out to identify the possible health consequences of the ingestion of heat-treated products, characterize the reaction kinetics leading to NFC and evaluate some mitigation procedures proposed by the CIAA toolbox, and finally develop a simple, rapid and non destructive control method based on fluorescence acquisition on the crushed food products and chemometric analysis of the spectral information. This paper summarizes the objectives and essential results obtained in the scope of the project, highlighting the need for evaluating the distribution of NFC in food products commercialized in Europe, as well as the impact of the food formula/recipe and process on Maillard derived NFC food levels. The potential of the Fluoralys sensor regarding its ability to control food contamination with NFC is presented. A decrease in NFC concentration of heat processed food should allow significantly limiting the exposure of populations to NFC and consequently the potential related health risk. (c) 2009 Elsevier Masson SAS. All rights reserved.

Comparison of sensory, microbiological, and biochemical parameters of microwave versus indirect UHT fluid skim milk during storage.

PubMed

Clare, D A; Bang, W S; Cartwright, G; Drake, M A; Coronel, P; Simunovic, J

2005-12-01

Shelf-stable milk could benefit from sensory quality improvement. Current methods of heating cause flavor and nutrient degradation through exposure to overheated thermal exchange surfaces. Rapid heating with microwaves followed by sudden cooling could reduce or eliminate this problem. The objectives for this study were focused on designing and implementing continuous microwave thermal processing of skim fluid milks (white and chocolate) to compare sensory, microbiological, and biochemical parameters with conventionally prepared, indirect UHT milks. All test products were aseptically packaged and stored at ambient temperature for 12 mo. Every 3 mo, samples were taken for microbiological testing, reactive sulfhydryl determinations, active enzyme analysis, instrumental viscosity readings, color measurements, and descriptive sensory evaluation. Microbiological plate counts were negative on all milks at each time point. Enzymatic assays showed that plasmin was inactivated by both heat treatments. 5,5'-dithio-bis(2-nitrobenzoic acid) analysis, a measure of reactive sulfhydryl (-SH-) groups, showed that the initial thiol content was not significantly different between the microwave-processed and UHT-treated milks. However, both heating methods resulted in an increased thiol level compared with conventionally pasteurized milk samples due to the higher temperatures attained. Sulfhydryl oxidase, a milk enzyme that catalyzes disulfide bond formation using a variety of protein substrates, retained activity following microwave processing, and decreased during storage. Viscosity values were essentially equivalent in microwave- and UHT-heated white skim milks. Sensory analyses established that UHT-treated milks were visibly darker, and exhibited higher caramelized and stale/fatty flavors with increased astringency compared with the microwave samples. Sweet aromatic flavor and sweet taste decreased during storage in both UHT and microwave milk products, whereas stale/fatty flavors increased over time. Sensory effects were more apparent in white milks than in chocolate varieties. These studies suggest that microwave technology may provide a useful alternative processing method for delivery of aseptic milk products that retain a long shelf life.

Energetic approach of biomass hydrolysis in supercritical water.

PubMed

Cantero, Danilo A; Vaquerizo, Luis; Mato, Fidel; Bermejo, M Dolores; Cocero, M José

2015-03-01

Cellulose hydrolysis can be performed in supercritical water with a high selectivity of soluble sugars. The process produces high-pressure steam that can be integrated, from an energy point of view, with the whole biomass treating process. This work investigates the integration of biomass hydrolysis reactors with commercial combined heat and power (CHP) schemes, with special attention to reactor outlet streams. The innovation developed in this work allows adequate energy integration possibilities for heating and compression by using high temperature of the flue gases and direct shaft work from the turbine. The integration of biomass hydrolysis with a CHP process allows the selective conversion of biomass into sugars with low heat requirements. Integrating these two processes, the CHP scheme yield is enhanced around 10% by injecting water in the gas turbine. Furthermore, the hydrolysis reactor can be held at 400°C and 23 MPa using only the gas turbine outlet streams. Copyright © 2014 Elsevier Ltd. All rights reserved.

Study of structural, electrical, and dielectric properties of phosphate-borate glasses and glass-ceramics

NASA Astrophysics Data System (ADS)

Melo, B. M. G.; Graça, M. P. F.; Prezas, P. R.; Valente, M. A.; Almeida, A. F.; Freire, F. N. A.; Bih, L.

2016-08-01

In this work, phosphate-borate based glasses with molar composition 20.7P2O5-17.2Nb2O5-13.8WO3-34.5A2O-13.8B2O3, where A = Li, Na, and K, were prepared by the melt quenching technique. The as-prepared glasses were heat-treated in air at 800 °C for 4 h, which led to the formation of glass-ceramics. These high chemical and thermal stability glasses are good candidates for several applications such as fast ionic conductors, semiconductors, photonic materials, electrolytes, hermetic seals, rare-earth ion host solid lasers, and biomedical materials. The present work endorses the analysis of the electrical conductivity of the as-grown samples, and also the electrical, dielectric, and structural changes established by the heat-treatment process. The structure of the samples was analyzed using X-Ray powder Diffraction (XRD), Raman spectroscopy, and density measurements. Both XRD and Raman analysis confirmed crystals formation through the heat-treatment process. The electrical ac and dc conductivities, σac and σdc, respectively, and impedance spectroscopy measurements as function of the temperature, varying from 200 to 380 K, were investigated for the as-grown and heat-treated samples. The impedance spectroscopy was measured in the frequency range of 100 Hz-1 MHz.

3. HOT BED FOR SALEMBROSIUS CONTINUOUS GASFIRED HEAT TREATING LINE ...

Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

3. HOT BED FOR SALEM-BROSIUS CONTINUOUS GAS-FIRED HEAT TREATING LINE AT THE HEAT TREATMENT PLANT OF THE DUQUESNE WORKS. - U.S. Steel Duquesne Works, Heat Treatment Plant, Along Monongahela River, Duquesne, Allegheny County, PA

Effects of substrate microstructure on the formation of oriented oxide nanotube arrays on Ti and Ti alloys

NASA Astrophysics Data System (ADS)

Ferreira, C. P.; Gonçalves, M. C.; Caram, R.; Bertazzoli, R.; Rodrigues, C. A.

2013-11-01

The formation of nanotubular oxide layers on Ti and Ti alloys has been widely investigated for the photocatalytic degradation of organic compounds due to their excellent catalytic efficiency, chemical stability, and low cost and toxicity. Aiming to improve the photocatalytic efficiency of this nanostructured oxide, this work investigated the influence of substrate grain size on the growth of nanotubular oxide layers. Ti and Ti alloys (Ti-6Al, Ti-6Al-7Nb) were produced by arc melting with non-consumable tungsten electrode and water-cooled copper hearth under argon atmosphere. Some of the ingots were heat-treated at 1000 °C for 12 and 24 h in argon atmosphere, followed by slow cooling rates to reduce crystalline defects and increase the grain size of their microstructures. Three types of samples were anodized: commercial substrate, as-prepared and heat-treated samples. The anodization was performed using fluoride solution and a cell potential of 20 V. The samples were characterized by optical microscopy, field-emission scanning electron microscopy and X-ray diffraction. The heat treatment preceding the anodization process increased the grain size of pure Ti and Ti alloys and promoted the formation of Widmanstätten structures in Ti6Al7Nb. The nanotubes layers grown on smaller grain and thermally untreated samples were more regular and homogeneous. In the case of Ti-6Al-7Nb alloy, which presents a α + β phase microstructure, the morphology of nanotubes nucleated on α matrix was more regular than those of nanotubes nucleated on β phase. After the annealing process, the Ti-6Al-7Nb alloy presented full diffusion process and the growth of equilibrium phases resulting in the appearance of regions containing higher concentrations of Nb, i.e. beta phase. In those regions the dissolution rate of Nb2O5 is lower than that of TiO2, resulting in a nanoporous layer. In general, heat treating reduces crystalline defects and promotes the increasing of the grain sizes, not favoring the process of nanotube nucleation and growth on the metallic surface.

HSP90 gene expression induced by aspirin is associated with damage remission in a chicken myocardial cell culture exposed to heat stress.

PubMed

Zhang, X; Qian, Z; Zhu, H; Tang, S; Wu, D; Zhang, M; Kemper, N; Hartung, J; Bao, E

2016-08-01

To understand the potential protection of heat shock protein 90 (HSP90) induced by aspirin against heat stress damage in chicken myocardial cells, enzyme activities related to stress damage, cytopathological changes, the expression and distribution of HSP90, and HSP90 mRNA levels in the myocardial cells exposed to heat stress (42°C) for different durations with or without aspirin administration (1 mg/ml, 2 h prior) in vitro were investigated. Significant increase of enzyme levels in the supernatant of heat-stressed myocardial cells and cellular lesions characterised by acute degeneration, karyopyknosis and karyorrhexis were observed, compared to non-treated cells. However, the lesions of cells treated with aspirin were milder, characterised by earlier recovery of enzyme levels to the control levels and no obvious heat stress-related cellular necrosis. Stronger positive signals in the cytoplasm and longer retention of HSP90 signal in nuclei were observed in aspirin-treated myocardial cells than those of only heat-stressed cells. HSP90 level in the aspirin-treated myocardial cells was 11.1-fold higher than that in non-treated cells, and remained at a high level at the early stage of heat stress, whereas it was just 4.1-fold higher in only heat-stressed cells and returned rapidly to a low level. Overexpression of HSP90 mRNA in aspirin-treated cells was observed throughout the experiment, whereas HSP90 mRNA decreased significantly only in heat-stressed cells. The early higher HSP90 expression induced by aspirin during heat stress was accompanied by decreased heat stress damage, suggesting that aspirin might play an important role in preventing myocardial cells from heat stress damage in vitro.

The biodrying concept: an innovative technology creating energy from sewage sludge.

PubMed

Winkler, M-K H; Bennenbroek, M H; Horstink, F H; van Loosdrecht, M C M; van de Pol, G-J

2013-11-01

A full-scale biodrying installation was treating 150 kton (wet weight) of dewatered waste activated sludge per year. The waste was treated at thermophilic conditions (65-75 °C) in a 2-step forced aeration process reducing the total wet sludge weight by 73%. The final product had a high caloric value (7700-10,400 (kJ/kg)), allowing a combustion for energy generation in external facilities. The resulting product met the European microbial and heavy metal quality standards needed for an application as organic fertilizer. The facility used <0.5 MW of electricity and recovered 9.3 MW from biologically produced heat, which was internally used for the heating of office buildings. Produced ammonia, originating from the microbial conversion of organic matter, was recovered from the ventilated air in an acid gas scrubber as an ammonium sulphate solution 40% (w/w) (7.3 kton/year) and was sold as substitute for artificial fertilizers. The sustainability of this process is discussed relative to other sludge handling processes. Copyright © 2013 Elsevier Ltd. All rights reserved.

Tribological performance of titanium samples oxidized by fs-laser radiation, thermal heating, or electrochemical anodization

NASA Astrophysics Data System (ADS)

Kirner, S. V.; Slachciak, N.; Elert, A. M.; Griepentrog, M.; Fischer, D.; Hertwig, A.; Sahre, M.; Dörfel, I.; Sturm, H.; Pentzien, S.; Koter, R.; Spaltmann, D.; Krüger, J.; Bonse, J.

2018-04-01

Commercial grade-1 titanium samples (Ti, 99.6%) were treated using three alternative methods, (i) femtosecond laser processing, (ii) thermal heat treatment, and (iii) electrochemical anodization, respectively, resulting in the formation of differently conditioned superficial titanium oxide layers. The laser processing (i) was carried out by a Ti:sapphire laser (pulse duration 30 fs, central wavelength 790 nm, pulse repetition rate 1 kHz) in a regime of generating laser-induced periodic surface structures (LIPSS). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning setup for the processing of several square-millimeters large surface areas covered homogeneously by these nanostructures. The differently oxidized titanium surfaces were characterized by optical microscopy, micro Raman spectroscopy, variable angle spectroscopic ellipsometry, and instrumented indentation testing. The tribological performance was characterized in the regime of mixed friction by reciprocating sliding tests against a sphere of hardened steel in fully formulated engine oil as lubricant. The specific tribological performance of the differently treated surfaces is discussed with respect to possible physical and chemical mechanisms.

Optimization and Domestic Sourcing of Lithium Ion Battery Anode Materials

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wood, III, D. L.; Yoon, S.

2012-10-25

The purpose of this Cooperative Research and Development Agreement (CRADA) between ORNL and A123Systems, Inc. was to develop a low-temperature heat treatment process for natural graphite based anode materials for high-capacity and long-cycle-life lithium ion batteries. Three major problems currently plague state-of-the-art lithium ion battery anode materials. The first is the cost of the artificial graphite, which is heat-treated well in excess of 2000°C. Because of this high-temperature heat treatment, the anode active material significantly contributes to the cost of a lithium ion battery. The second problem is the limited specific capacity of state-of-the-art anodes based on artificial graphites, whichmore » is only about 200-350 mAh/g. This value needs to be increased to achieve high energy density when used with the low cell-voltage nanoparticle LiFePO4 cathode. Thirdly, the rate capability under cycling conditions of natural graphite based materials must be improved to match that of the nanoparticle LiFePO4. Natural graphite materials contain inherent crystallinity and lithium intercalation activity. They hold particular appeal, as they offer huge potential for industrial energy savings with the energy costs essentially subsidized by geological processes. Natural graphites have been heat-treated to a substantially lower temperature (as low as 1000-1500°C) and used as anode active materials to address the problems described above. Finally, corresponding graphitization and post-treatment processes were developed that are amenable to scaling to automotive quantities.« less

Effect of Three Factors in Cheese Production (pH, Salt, and Heat) on Mycobacterium avium subsp. paratuberculosis Viability

PubMed Central

Sung, Nackmoon; Collins, Michael T.

2000-01-01

Low pH and salt are two factors contributing to the inactivation of bacterial pathogens during a 60-day curing period for cheese. The kinetics of inactivation for Mycobacterium avium subsp. paratuberculosis strains ATCC 19698 and Dominic were measured at 20°C under different pH and NaCl conditions commonly used in processing cheese. The corresponding D values (decimal reduction times; the time required to kill 1 log10 concentration of bacteria) were measured. Also measured were the D values for heat-treated and nonheated M. avium subsp. paratuberculosis in 50 mM acetate buffer (pH 5.0, 2% [wt/vol] NaCl) and a soft white Hispanic-style cheese (pH 6.0, 2% [wt/vol] NaCl). Samples were removed at various intervals until no viable cells were detected using the radiometric culture method (BACTEC) for enumeration of M. avium subsp. paratuberculosis. NaCl had little or no effect on the inactivation of M. avium subsp. paratuberculosis, and increasing NaCl concentrations were not associated with decreasing D values (faster killing) in the acetate buffer. Lower pHs, however, were significantly correlated with decreasing D values of M. avium subsp. paratuberculosis in the acetate buffer. The D values for heat-treated M. avium subsp. paratuberculosis ATCC 19698 in the cheese were higher than those predicted by studies done in acetate buffer. The heat-treated M. avium subsp. paratuberculosis strains had lower D values than the nonheated cells (faster killing) both in the acetate buffer (pH 5, 2% [wt/vol] NaCl) and in the soft white cheese. The D value for heat-treated M. avium subsp. paratuberculosis ATCC 19698 in the cheese (36.5 days) suggests that heat treatment of raw milk coupled with a 60-day curing period will inactivate about 103 cells of M. avium subsp. paratuberculosis per ml. PMID:10742208

Effect of heat treatment and enzymatic digestion on the B cell epitopes of cow's milk proteins.

PubMed

Morisawa, Y; Kitamura, A; Ujihara, T; Zushi, N; Kuzume, K; Shimanouchi, Y; Tamura, S; Wakiguchi, H; Saito, H; Matsumoto, K

2009-06-01

Processing milk leads to changes in clinical allergenicity. However, the mechanism by which heat treatment affects the allergenicity of milk proteins is not fully understood. We investigated the effect of heat treatment and enzymatic digestion on the allergenicity of B cell epitopes of milk proteins using a histamine release assay. Human basophils were passively sensitized using sera from 10 patients with allergies to cow's milk. All the patients experienced symptoms immediately after ingesting milk. The human basophils were obtained from umbilical cord blood mononuclear cells after culturing the mononuclear cells for 3-4 weeks in the presence of IL-3. After sensitization with 10% patient sera for 48 h, the cells were stimulated with untreated, heat-treated, or heat-treated and pepsin-and-trypsin-digested beta-lactoglobulin or alpha-casein for 1 h. The histamine concentrations in the supernatants were then measured by radioimmunoassay. Heat treatment alone did not alter the molecular weight of beta-lactoglobulin or alpha-casein. Heat treatment of beta-lactoglobulin significantly increased its susceptibility to enzymatic digestion in a time- and temperature-dependent manner and reduced its ability to induce histamine release from sensitized basophils. Similar findings were not observed for alpha-casein. The combination of heat treatment and enzymatic digestion reduced the abilities of both beta-lactoglobulin and alpha-casein to induce histamine release from passively sensitized basophils. Heat treatment reduced the allergenicity of beta-lactoglobulin by inducing conformational changes and by increasing its susceptibility to enzymatic digestion, both of which disrupted B cell epitopes, whereas heat treatment alone did not alter the allergenicity of alpha-casein.

Microstructural Aspects in FSW and TIG Welding of Cast ZE41A Magnesium Alloy

NASA Astrophysics Data System (ADS)

Carlone, Pierpaolo; Astarita, Antonello; Rubino, Felice; Pasquino, Nicola

2016-04-01

In this paper, magnesium ZE41A alloy plates were butt joined through friction stir welding (FSW) and Tungsten Inert Gas welding processes. Process-induced microstructures were investigated by optical and SEM observations, EDX microanalysis and microhardness measurements. The effect of a post-welded T5 heat treatment on FSW joints was also assessed. Sound joints were produced by means of both techniques. Different elemental distributions and grain sizes were found, whereas microhardness profiles reflect microstructural changes. Post-welding heat treatment did not induce significant alterations in elemental distribution. The FSW-treated joint showed a more homogeneous hardness profile than the as-welded FSW joint.

Using a non-invasive technique in nutrition: synchrotron radiation infrared microspectroscopy spectroscopic characterization of oil seeds treated with different processing conditions on molecular spectral factors influencing nutrient delivery.

PubMed

Zhang, Xuewei; Yu, Peiqiang

2014-07-02

Non-invasive techniques are a key to study nutrition and structure interaction. Fourier transform infrared microspectroscopy coupled with a synchrotron radiation source (SR-IMS) is a rapid, non-invasive, and non-destructive bioanalytical technique. To understand internal structure changes in relation to nutrient availability in oil seed processing is vital to find optimal processing conditions. The objective of this study was to use a synchrotron-based bioanalytical technique SR-IMS as a non-invasive and non-destructive tool to study the effects of heat-processing methods and oil seed canola type on modeled protein structure based on spectral data within intact tissue that were randomly selected and quantify the relationship between the modeled protein structure and protein nutrient supply to ruminants. The results showed that the moisture heat-related processing significantly changed (p<0.05) modeled protein structures compared to the raw canola (control) and those processing by dry heating. The moisture heating increased (p<0.05) spectral intensities of amide I, amide II, α-helices, and β-sheets but decreased (p<0.05) the ratio of modeled α-helices to β-sheet spectral intensity. There was no difference (p>0.05) in the protein spectral profile between the raw and dry-heated canola tissue and between yellow- and brown-type canola tissue. The results indicated that different heat processing methods have different impacts on the protein inherent structure. The protein intrinsic structure in canola seed tissue was more sensitive and more response to the moisture heating in comparison to the dry heating. These changes are expected to be related to the nutritive value. However, the current study is based on limited samples, and more large-scale studies are needed to confirm our findings.

A pilot study to characterize fine particles in the environment of an automotive machining facility.

PubMed

Sioutas, C

1999-04-01

The main goal of this study was to characterize fine particles (e.g., smaller than about 3 microns) in an automotive machining environment. The Toledo Machining Plant of Chrysler Corporation was selected for this purpose. The effect of local mechanical processes as aerosol sources was a major part of this investigation. To determine the size-dependent mass concentration of particles in the plant, the Micro-Orifice Uniform Deposit Impactor (MOUDI Model 100, MSP Corp., Minneapolis, Minnesota) was used. The MOUDI was placed at central locations in departments with sources inside the plant, so that the obtained information on the size distribution realistically represents the aerosol to which plant workers are exposed. Sampling was conducted over a 4-day period, and during three periods per day, each matching the work shifts. A special effort was made to place the MOUDI at a central location of a department with relatively homogeneous particle sources. The selected sampling sites included welding, grinding, steel machining, and heat treating processes. The average 24-hour mass concentrations of particles smaller than 3.2 microns in aerodynamic diameter were 167.8, 103.9, 201.7, and 112.7 micrograms/m3 for welding, grinding, mild steel, and heat treating processes, respectively. Finally, the mass median diameters of welding, heat treatment, machining, and grinding operations were approximately 0.5, 0.5, 0.6, and 0.8 micron, respectively.

Energy recovery from thermal treatment of dewatered sludge in wastewater treatment plants.

PubMed

Yang, Qingfeng; Dussan, Karla; Monaghan, Rory F D; Zhan, Xinmin

Sewage sludge is a by-product generated from municipal wastewater treatment (WWT) processes. This study examines the conversion of sludge via energy recovery from gasification/combustion for thermal treatment of dewatered sludge. The present analysis is based on a chemical equilibrium model of thermal conversion of previously dewatered sludge with moisture content of 60-80%. Prior to combustion/gasification, sludge is dried to a moisture content of 25-55% by two processes: (1) heat recovered from syngas/flue gas cooling and (2) heat recovered from syngas combustion. The electricity recovered from the combined heat and power process can be reused in syngas cleaning and in the WWT plant. Gas temperature, total heat and electricity recoverable are evaluated using the model. Results show that generation of electricity from dewatered sludge with low moisture content (≤ 70%) is feasible within a self-sufficient sludge treatment process. Optimal conditions for gasification correspond to an equivalence ratio of 2.3 and dried sludge moisture content of 25%. Net electricity generated from syngas combustion can account for 0.071 kWh/m(3) of wastewater treated, which is up to 25.4-28.4% of the WWT plant's total energy consumption.

Evaluation of fatigue properties of EN31 steel heat treated using biodegradable gingili oil

NASA Astrophysics Data System (ADS)

Harichandra, B. P.; Prashanth, Mrudula; Prakash, S. V.

2016-09-01

Rotating bending fatigue is the most commonly encountered loading in most machines and machine tools. At the same time, modern literature in this area is very little. EN31 steel is a steel which is commonly used in load bearing applications which encounters fatigue loading. Further, studies on heat treated EN31 steel to improve fatigue strength is hardly reported. This paper takes this rare issue further ahead by using bio-degradable gingili oil to heat treat EN31 steel for fatigue applications. This paper reports the results of rotating bending fatigue study of EN31 steel. Fatigue tests were conducted for three conditions a) Untreated, b) Heat treated with water, and c) Heat treated with gingili oil, with cantilever loads ranging from 30% to 90% using double sided rotating bending fatigue testing machine. It is seen that EN31 steel heat treated using gingili oil has far superior fatigue properties than water treated and untreated ones, with gingili oil quenched specimen have ∼10 times more fatigue life than water quenched specimen and ∼100 times more than unquenched specimens when lower bending stresses are involved.

Pahoa geothermal industrial park. Engineering and economic analysis for direct applications of geothermal energy in an industrial park at Pahoa, Hawaii

DOE Office of Scientific and Technical Information (OSTI.GOV)

Moreau, J.W.

1980-12-01

This engineering and economic study evaluated the potential for developing a geothermal industrial park in the Puna District near Pahoa on the Island of Hawaii. Direct heat industrial applications were analyzed from a marketing, engineering, economic, environmental, and sociological standpoint to determine the most viable industries for the park. An extensive literature search produced 31 existing processes currently using geothermal heat. An additional list was compiled indicating industrial processes that require heat that could be provided by geothermal energy. From this information, 17 possible processes were selected for consideration. Careful scrutiny and analysis of these 17 processes revealed three thatmore » justified detailed economic workups. The three processes chosen for detailed analysis were: an ethanol plant using bagasse and wood as feedstock; a cattle feed mill using sugar cane leaf trash as feedstock; and a papaya processing facility providing both fresh and processed fruit. In addition, a research facility to assess and develop other processes was treated as a concept. Consideration was given to the impediments to development, the engineering process requirements and the governmental support for each process. The study describes the geothermal well site chosen, the pipeline to transmit the hydrothermal fluid, and the infrastructure required for the industrial park. A conceptual development plan for the ethanol plant, the feedmill and the papaya processing facility was prepared. The study concluded that a direct heat industrial park in Pahoa, Hawaii, involves considerable risks.« less

Monoclonal antibodies specific to heat-treated porcine blood.

PubMed

Raja Nhari, Raja Mohd Hafidz; Hamid, Muhajir; Rasli, Nurmunirah Mohamad; Omar, Abdul Rahman; El Sheikha, Aly Farag; Mustafa, Shuhaimi

2016-05-01

Porcine blood is potentially being utilized in food as a binder, gelling agent, emulsifier or colorant. However, for certain communities, the usage of animal blood in food is strictly prohibited owing to religious concerns and health reasons. This study reports the development of monoclonal antibodies (MAbs) against heat-treated soluble proteins (HSPs) of autoclaved porcine blood; characterization of MAbs against blood, non-blood and plasma from different animal species using qualitative indirect non-competitive enzyme-linked immunosorbent assay (ELISA); and immunoblotting of antigenic components in HSPs of porcine blood. Fifteen MAbs are specific to heat-treated and raw porcine blood and not cross-reacted with other animal blood and non-blood proteins (meat and non-meat). Twelve MAbs are specific to porcine plasma, while three MAbs specific to porcine plasma are cross-reacted with chicken plasma. Immunoblotting revealed antigenic protein bands (∼60, ∼85-100 and ∼250 kDa) in porcine blood and plasma recognized by the MAbs. Selection of MAbs that recognized 60 kDa HSPs of porcine blood and plasma as novel monoclonal antibodies would be useful for detection of porcine plasma in processed food using the immunoassay method. © 2015 Society of Chemical Industry. © 2015 Society of Chemical Industry.

Matrin 3 co-immunoprecipitates with the heat shock proteins glucose-regulated protein 78 (GRP78), GRP75 and glutathione S-transferase π isoform 2 (GSTπ2) in thymoma cells.

PubMed

Osman, Ahmed M; van Loveren, Henk

2014-06-01

Here, we report evidence that matrin 3 (MATR3), a highly conserved inner nuclear matrix phosphoprotein, whose function is largely unknown, interacts specifically with the heat shock proteins glucose-regulated protein 78 (GRP78), GRP75 and glutathione S-transferase π isoform 2 (GSTπ2). Using immunoprecipitation experiments of lysates obtained from control and tributyltin oxide (TBTO)-treated thymoma cell line (EL4), we identified MATR3 and its partners by MS/MS analysis and confirmed by immunoblot. We also show that MATR3 undergoes degradation as reported before and that this cleavage process, which is inhibited by the broad-spectrum caspase inhibitor, z-VAD-FMK, is more marked in TBTO-treated cells. Further, we found that the heat shock protein glucose-regulated protein 78 was downregulated in the TBTO-treated cells. The GRP78 protein is known to protect cells from apoptosis by complexing with procaspase 7 thereby preventing caspase activation cascade. By immunoblot analysis, we found that the levels of procaspases-3 and -7 were lower in TBTO-treated cells; in contrast, the level of p20, the active form of caspase 3, was relatively higher in the treated cells compared to that of control cells. We propose that the TBTO-mediated downregulation of GRP78 triggers the caspase cascade pathway leading to MATR3 degradation. Copyright © 2014 Elsevier Masson SAS. All rights reserved.

Identification of a process window for tailored carburization of sheet metals in hot stamping

NASA Astrophysics Data System (ADS)

Horn, Alexander; Merklein, Marion

2018-05-01

Due to governmental regulations concerning the reduction of CO2 emissions and increasing safety standards, hot stamping of high strength boron manganese steel sheets has evolved into a state of the art process for manufacturing structural car body parts. The combined forming and in-die quenching process enables the formation of a fully martensitic microstructure. Therefore, press hardened steels offer high strength, but low ductility. In order to further improve passenger safety, a tailored configuration of mechanical properties is desired. Besides state of the art methods, like the application of locally different heat treatment temperatures or varying quenching rates, the adjustment of mechanical properties of sheet metals by a tailored carburization is a novel approach. For the carburization process, the specimens are first coated with graphite and subsequently heat treated. Within this contribution, different coating strategies as well as heat treatment temperatures and dwell times are investigated. For the determination of a process window, mechanical properties such as tensile strength and microhardness will be analyzed and correlated with the resulting microstructure.

Novel water-air circulation quenching process for AISI 4140 steel

NASA Astrophysics Data System (ADS)

Zheng, Liyun; Zheng, Dawei; Zhao, Lixin; Wang, Lihui; Zhang, Kai

2013-11-01

AISI 4140 steel is usually used after quenching and tempering. During the heat treatment process in industry production, there are some problems, such as quenching cracks, related to water-cooling and low hardness due to oil quenching. A water-air circulation quenching process can solve the problems of quenching cracks with water and the high cost quenching with oil, which is flammable, unsafe and not enough to obtain the required hardness. The control of the water-cooling and air-cooling time is a key factor in the process. This paper focuses on the quenching temperature, water-air cycle time and cycle index to prevent cracking for AISI 4140 steel. The optimum heat treatment parameters to achieve a good match of the strength and toughness of AISI 4140 steel were obtained by repeated adjustment of the water-air circulation quenching process parameters. The tensile strength, Charpy impact energy at -10 °C and hardness of the heat treated AISI 4140 steel after quenching and tempering were approximately 1098 MPa, 67.5 J and 316 HB, respectively.

Collaborative Technology Assessments Of Transient Field Processing And Additive Manufacturing Technologies As Applied To Gas Turbine Components

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ludtka, Gerard Michael; Dehoff, Ryan R.; Szabo, Attila

2016-01-01

ORNL partnered with GE Power & Water to investigate the effect of thermomagnetic processing on the microstructure and mechanical properties of GE Power & Water newly developed wrought Ni-Fe-Cr alloys. Exploration of the effects of high magnetic field process during heat treatment of the alloys indicated conditions where applications of magnetic fields yields significant property improvements. The alloy aged using high magnetic field processing exhibited 3 HRC higher hardness compared to the conventionally-aged alloy. The alloy annealed at 1785 F using high magnetic field processing demonstrated an average creep life 2.5 times longer than that of the conventionally heat-treated alloy.more » Preliminary results show that high magnetic field processing can improve the mechanical properties of Ni-Fe-Cr alloys and potentially extend the life cycle of the gas turbine components such as nozzles leading to significant energy savings.« less

Alloy 690 qualification: Corrosion under prototypic heat flux and temperature conditions. Final report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Baum, A.J.

1995-05-01

The objective of this program was to perform qualification tests of industrial heats of thermally treated alloy 690 steam generator tubing under heat transfer conditions. Primary emphasis was focused on testing of alternate tube to tubesheet expansion processes. In addition, a background report was written to document the evolution of the alloy 690 process specification and the supporting qualification testing. While the testing was able to produce some localized corrosion of alloy 690 in the tube to tubesheet joint transition regions under highly alkaline conditions, the corrosion rates were between two and three orders of magnitude lower than the comparablemore » rates in mill annealed alloy 600 tubing. The corrosion morphology was a combination of intergranular and general corrosion, rather than the stress corrosion cracking typically found in mill annealed alloy 600 tubing.« less

Feasibility of new ladle-treated Hadfield steel for mining purposes

NASA Astrophysics Data System (ADS)

El Fawkhry, M. K.

2018-03-01

A debate has arisen over the possibility of using a new ladle-treated Hadfield steel instead of conventional heat-treated Hadfield steel in mining applications. This debate might be solved by identifying the differences between the mechanical properties and strain-hardening properties of conventional heat-treated Hadfield steel and its counterpart ladle-treated Hadfield steel. Tensile and compression tests demonstrated that the ductility of ladle-treated Hadfield steel is similar to that of conventional heat-treated steel. However, the strain-hardening property of the ladle-treated Hadfield steel is almost two times higher than that of the heat-treated Hadfield steel. The results of this study demonstrate that the improvement of the strain-hardening behavior is attributable to the low stacking-fault energy of the main austenite matrix, which results from the high segregation coefficient of carbon and manganese solutes of the main austenite matrix into the new eutectic phase. Superior wear abrasion resistance is a potential consequence of different strain-hardening properties under low and high loads.

EFFECT OF HEAT TREATMENT ON (Cr, Fe)7C3/γ-Fe COATINGS IN SITU SYNTHESIZED BY VACUUM ELECTRON BEAM IRRADIATION

NASA Astrophysics Data System (ADS)

Lu, Binfeng; Chen, Yunxia; Xu, Mengjia

(Cr, Fe)7C3/γ-Fe composite layer has been in situ synthesized on a low carbon steel surface by vacuum electron beam VEB irradiation. The synthesized samples were then subdued to different heat treatments to improve their impaired impact toughness. The microstructure, impact toughness and wear resistance of the heat-treated samples were studied by means of optical microscope (OM), X-ray diffraction (XRD), scanning electron microscope (SEM), microhardness tester, impact test machine and tribological tester. After heat treatment, the primary and eutectic carbides remained in their original shape and size, and a large number of secondary carbides precipitated in the iron matrix. Since the Widmanstatten ferrite in the heat affected zone (HAZ) transformed to fine ferrite completely, the impact toughness of the heat-treated samples increased significantly. The microhardness of the heat-treated samples decreased slightly due to the decreased chromium content in the iron matrix. The wear resistance of 1000∘C and 900∘C heat-treated samples was almost same with the as-synthesized sample. While the wear resistance of the 800∘C heat-treated one decreased slightly because part of the austenite matrix had transformed to ferrite matrix, which reduced the bonding of carbides particulates.

Process for fabricating continuous lengths of superconductor

DOEpatents

Kroeger, Donald M.; List, III, Frederick A.

1998-01-01

A process for manufacturing a superconductor. The process is accomplished by depositing a superconductor precursor powder on a continuous length of a first substrate ribbon, overlaying a continuous length of a second substrate ribbon on said first substrate ribbon, and applying sufficient pressure to form a bound layered superconductor precursor between said first substrate ribbon and said second substrates ribbon. The layered superconductor precursor is then heat treated to form a super conductor layer.

Recent development of anaerobic digestion processes for energy recovery from wastes.

PubMed

Nishio, Naomichi; Nakashimada, Yutaka

2007-02-01

Anaerobic digestion leads to the overall gasification of organic wastewaters and wastes, and produces methane and carbon dioxide; this gasification contributes to reducing organic matter and recovering energy from organic carbons. Here, we propose three new processes and demonstrate the effectiveness of each process. By using complete anaerobic organic matter removal process (CARP), in which diluted wastewaters such as sewage and effluent from a methane fermentation digester were treated under anaerobic condition for post-treatment, the chemical oxygen demand (COD) in wastewater was decreased to less than 20 ppm. The dry ammonia-methane two-stage fermentation process (Am-Met process) is useful for the anaerobic treatment of nitrogen-rich wastes such as waste excess sludge, cow feces, chicken feces, and food waste without the dilution of the ammonia produced by water or carbon-rich wastes. The hydrogen-methane two-stage fermentation (Hy-Met process), in which the hydrogen produced in the first stage is used for a fuel cell system to generate electricity and the methane produced in the second stage is used to generate heat energy to heat the two reactors and satisfy heat requirements, is useful for the treatment of sugar-rich wastewaters, bread wastes, and biodiesel wastewaters.

Industrial Technology Modernization Program. Project 44. Modernize Facility Equipment and Processes. Volume 1. Revision 2. Phase 2

DTIC Science & Technology

1988-05-01

OF EXTRUSION HLSGFLN XRSO ICO-F XTUINPPER PATE CUT-OFF EXTRUSION I I 7 TUMBLE S TUMBLE HEAT &SORT TML I IEC SPANK & PIERCE P A SPANK & PIERCEI IF...implementation, the Walnut Cell will utilize 50% of the "As-Is" floor space. 106 -EGREflSEII HSL 59 i.CUT OFF EXTRUSION 2. SPANK & PIERCE I 3.DEGREASE 4...FEMALE MALE CUT-OFF EXTRUSION I HOUSNG HOUNG I SPANK & PIERCE SPANK & PIERCE I CLEAN I DEG SE I I DEGREASEI I C P P E R PL A TE I HEAT TREAT I HEAT

Sour gas injection for use with in situ heat treatment

DOEpatents

Fowler, Thomas David [Houston, TX

2009-11-03

Systems, methods, and heaters for treating a subsurface formation are described herein. At least one method for providing acidic gas to a subsurface formation is described herein. The method may include providing heat from one or more heaters to a portion of a subsurface formation; producing fluids that include one or more acidic gases from the formation using a heat treatment process. At least a portion of one of the acidic gases may be introduced into the formation, or into another formation, through one or more wellbores at a pressure below a lithostatic pressure of the formation in which the acidic gas is introduced.

Container for heat treating materials in microwave ovens

DOEpatents

Holcombe, Cressie E.; Dykes, Norman L.; Kimrey, Jr., Harold D.; Mills, James E.

1989-01-01

The efficiency of a microwave oven of a conventional two-source configuration and energy level is increased by providing the oven with a container for housing a refractory material to be treated. The container is formed of top and bottom walls transparent to microwaves while the sidewalls, in a circular configuration, are formed of a nonmetallic material opaque to microwave radiation reflecting the radiation penetrating the top and bottom walls radially inwardly into the center of the container wherein a casket of heat-insulating material is provided for housing the material to be heat treated. The reflection of the microwave radiation from the sidewalls increases the concentration of the microwaves upon the material being heat treated while the casket retains the heat to permit the heating of the material to a substantially higher temperature than achieveable in the oven without the container.

Radial basis functions in mathematical modelling of flow boiling in minichannels

NASA Astrophysics Data System (ADS)

Hożejowska, Sylwia; Hożejowski, Leszek; Piasecka, Magdalena

The paper addresses heat transfer processes in flow boiling in a vertical minichannel of 1.7 mm depth with a smooth heated surface contacting fluid. The heated element for FC-72 flowing in a minichannel was a 0.45 mm thick plate made of Haynes-230 alloy. An infrared camera positioned opposite the central, axially symmetric part of the channel measured the plate temperature. K-type thermocouples and pressure converters were installed at the inlet and outlet of the minichannel. In the study radial basis functions were used to solve a problem concerning heat transfer in a heated plate supplied with the controlled direct current. According to the model assumptions, the problem is treated as twodimensional and governed by the Poisson equation. The aim of the study lies in determining the temperature field and the heat transfer coefficient. The results were verified by comparing them with those obtained by the Trefftz method.

Thermochemical conversion of waste tyres-a review.

PubMed

Labaki, Madona; Jeguirim, Mejdi

2017-04-01

A review of the energy recovery from waste tyres is presented and focuses on the three thermochemical processes used to valorise waste tyres: pyrolysis, gasification, and combustion/incineration. After recalling the chemical composition of tyres, the thermogravimetric behaviours of tyres or their components under different atmospheres are described. Different kinetic studies on the thermochemical processes are treated. Then, the three processes were investigated, with a particular attention given to the gasification, due to the information unavailability on this process. Pyrolysis is a thermochemical conversion to produce a hydrocarbon rich gas mixture, condensable liquids or tars, and a carbon-rich solid residue. Gasification is a form of pyrolysis, carried out at higher temperatures and under given atmosphere (air, steam, oxygen, carbon dioxide, etc.) in order to yield mainly low molecular weight gaseous products. Combustion is a process that needs a fuel and an oxidizer with an ignition system to produce heat and/or steam. The effects of various process parameters such as temperature, heating rate, residence time, catalyst addition, etc. on the energy efficiency and the products yields and characteristics are mainly reviewed. These thermochemical processes are considered to be the more attractive and practicable methods for recovering energy and material from waste tyres. For the future, they are the main promising issue to treat and valorise used tyres. However, efforts should be done in developing more efficient technical systems.

N and Cr ion implantation of natural ruby surfaces and their characterization

NASA Astrophysics Data System (ADS)

Rao, K. Sudheendra; Sahoo, Rakesh K.; Dash, Tapan; Magudapathy, P.; Panigrahi, B. K.; Nayak, B. B.; Mishra, B. K.

2016-04-01

Energetic ions of N and Cr were used to implant the surfaces of natural rubies (low aesthetic quality). Surface colours of the specimens were found to change after ion implantation. The samples without and with ion implantation were characterized by diffuse reflectance spectra in ultra violet and visible region (DRS-UV-Vis), field emission scanning electron microscopy (FESEM), selected area electron diffraction (SAED) and nano-indentation. While the Cr-ion implantation produced deep red surface colour (pigeon eye red) in polished raw sample (without heat treatment), the N-ion implantation produced a mixed tone of dark blue, greenish blue and violet surface colour in the heat treated sample. In the case of heat treated sample at 3 × 1017 N-ions/cm2 fluence, formation of colour centres (F+, F2, F2+ and F22+) by ion implantation process is attributed to explain the development of the modified surface colours. Certain degree of surface amorphization was observed to be associated with the above N-ion implantation.

Heat treating of manufactured components

DOEpatents

Ripley, Edward B [Knoxville, TN

2012-05-22

An apparatus for heat treating manufactured components using microwave energy and microwave susceptor material is disclosed. The system typically includes an insulating vessel placed within a microwave applicator chamber. A moderating material is positioned inside the insulating vessel so that a substantial portion of the exterior surface of each component for heat treating is in contact with the moderating material.

Effect of Processing Intensity on Immunologically Active Bovine Milk Serum Proteins.

PubMed

Brick, Tabea; Ege, Markus; Boeren, Sjef; Böck, Andreas; von Mutius, Erika; Vervoort, Jacques; Hettinga, Kasper

2017-08-31

Consumption of raw cow's milk instead of industrially processed milk has been reported to protect children from developing asthma, allergies, and respiratory infections. Several heat-sensitive milk serum proteins have been implied in this effect though unbiased assessment of milk proteins in general is missing. The aim of this study was to compare the native milk serum proteome between raw cow's milk and various industrially applied processing methods, i.e., homogenization, fat separation, pasteurization, ultra-heat treatment (UHT), treatment for extended shelf-life (ESL), and conventional boiling. Each processing method was applied to the same three pools of raw milk. Levels of detectable proteins were quantified by liquid chromatography/tandem mass spectrometry following filter aided sample preparation. In total, 364 milk serum proteins were identified. The 140 proteins detectable in 66% of all samples were entered in a hierarchical cluster analysis. The resulting proteomics pattern separated mainly as high (boiling, UHT, ESL) versus no/low heat treatment (raw, skimmed, pasteurized). Comparing these two groups revealed 23 individual proteins significantly reduced by heating, e.g., lactoferrin (log2-fold change = -0.37, p = 0.004), lactoperoxidase (log2-fold change = -0.33, p = 0.001), and lactadherin (log2-fold change = -0.22, p = 0.020). The abundance of these heat sensitive proteins found in higher quantity in native cow's milk compared to heat treated milk, renders them potential candidates for protection from asthma, allergies, and respiratory infections.

PROCESSING OF RADIOACTIVE WASTE

DOEpatents

Johnson, B.M. Jr.; Barton, G.B.

1961-11-14

A process for treating radioactive waste solutions prior to disposal is described. A water-soluble phosphate, borate, and/or silicate is added. The solution is sprayed with steam into a space heated from 325 to 400 deg C whereby a powder is formed. The powder is melted and calcined at from 800 to 1000 deg C. Water vapor and gaseous products are separated from the glass formed. (AEC)

Quality of mango nectar processed by high-pressure homogenization with optimized heat treatment.

PubMed

Tribst, Alline Artigiani Lima; Franchi, Mark Alexandrow; de Massaguer, Pilar Rodriguez; Cristianini, Marcelo

2011-03-01

This work aimed to evaluate the effect of high-pressure homogenization (HPH) with heat shock on Aspergillus niger, vitamin C, and color of mango nectar. The nectar was processed at 200 MPa followed by heat shock, which was optimized by response surface methodology by using mango nectar ratio (45 to 70), heat time (10 to 20), and temperature (60 to 85 °C) as variables. The color of mango nectar and vitamin C retention were evaluated at the optimized treatments, that is, 200 MPa + 61.5 °C/20 min or 73.5 °C/10 min. The mathematical model indicates that heat shock time and temperature showed a positive effect in the mould inactivation, whereas increasing ratio resulted in a protective effect on A. niger. The optimized treatments did not increase the retention of vitamin C, but had positive effect for the nectar color, in particular for samples treated at 200 MPa + 61.5 °C/20 min. The results obtained in this study show that the conidia can be inactivated by applying HPH with heat shock, particularly to apply HPH as an option to pasteurize fruit nectar for industries.

Opticalman 1 and C, Rate Training Manual.

ERIC Educational Resources Information Center

Naval Personnel Program Support Activity, Washington, DC.

The technical subject matter of this rate training manual is written for regular navy and naval reserve personnel. Responsibilities for optical shop administration, supervision, and training are discussed in detail. Metals are studied in connection with heat treating processes. Characteristics of light are analyzed to familiarize students with…

Acoustic and thermal properties of tissue

NASA Astrophysics Data System (ADS)

Retat, L.; Rivens, I.; ter Haar, G. R.

2012-10-01

Differences in ultrasound (US) and thermal properties of abdominal soft tissues may affect the delivery of thermal therapies such as high intensity focused ultrasound and may provide a basis for US monitoring of such therapies. 21 rat livers were obtained, within one hour of surgical removal. For a single liver, 3 lobes were selected and each treated in one of 3 ways: maintained at room temperature, water bath heated to 50°C ± 1°C for 10 ± 0.5 minutes, or water bath heated to 60°C ± 1°C for 10 ± 0.6 minutes. The attenuation coefficient, speed of sound and thermal conductivity of fresh rat liver was measured. The attenuation coefficients and speed of sound were measured using the finite-amplitude insertion-substitution (FAIS) method. For each rat liver, the control and treated lobes were scanned using a pair of weakly focused 2.5 MHz Imasonic transducers over the range 1.8 to 3 MHz. The conductivity measurement apparatus was designed to provide one-dimensional heat flow through each specimen using a combination of insulation, heat source and heat sink. Using 35 MHz US images to determine the volume of air trapped in the system, the thermal conductivity was corrected using a simulation based on the Helmhotz bio-heat equation. The process of correlating these results with biological properties is discussed.

Heat-treated (in single aliquot or batch) colostrum outperforms non-heat-treated colostrum in terms of quality and transfer of immunoglobulin G in neonatal Jersey calves.

PubMed

Kryzer, A A; Godden, S M; Schell, R

2015-03-01

The objective of this randomized clinical trial was to describe the effect on colostrum characteristics and passive transfer of IgG in neonatal calves when using the Perfect Udder colostrum management system (single-aliquot treatment; Dairy Tech Inc., Greeley, CO) compared with a negative control (fresh refrigerated or fresh frozen colostrum) and a positive control (batch heat-treated colostrum). First-milking Jersey colostrum was pooled to achieve 31 unique batches with a minimum of 22.8 L per batch. The batch was then divided into 4 with 3.8 L allocated to each treatment group: (1) heat-treated in Perfect Udder bag at 60°C for 60 min and then stored at -20°C (PU); (2) heat-treated in a batch pasteurizer (Dairy Tech Inc.) at 60°C for 60 min and then stored at -20°C in Perfect Udder bag (DTB; positive control); (3) fresh frozen colostrum stored at -20°C in Perfect Udder bag (FF; negative control); and (4) fresh refrigerated colostrum stored at 4°C in Perfect Udder bag (FR; negative control). Colostrum from all treatments was sampled for analysis of IgG concentration and bacterial culture immediately after batch assembly, after processing, and before feeding. Newborn Jersey calves were randomly assigned to be fed 3.8 L of colostrum from 1 of the 4 treatment groups. A prefeeding, 0-h blood sample was collected, calves were fed by esophageal tube within 2 h of birth, and then a 24-h postfeeding blood sample was collected. Paired serum samples from 0- and 24-h blood samples were analyzed for IgG concentration (mg/mL) using radial immunodiffusion analysis. The overall mean IgG concentration in colostrum was 77.9 g/L and was not affected by treatment. Prefeeding total plate counts (log10 cfu/mL) were significantly different for all 4 treatments and were lower for heat-treated colostrum (PU=4.23, DTB=3.63) compared with fresh colostrum (FF=5.68, FR=6.53). Total coliform counts (log10 cfu/mL) were also significantly different for all 4 treatments and were lower for heat-treated colostrum (PU=0.45, DTB=1.08) compared with fresh colostrum (FF=3.82, FR=4.80). Mean 24-h serum IgG concentrations were significantly higher for calves in the PU (41.0 mg/mL) and DTB (40.6 mg/mL) groups compared with FF (35.1 mg/mL) and FR (35.5 mg/mL) groups. Mean apparent efficiency of absorption of IgG was significantly higher for the PU (37%) and DTB (37%) groups compared with the FF (32%) and FR (32%) groups. Calves fed heat-treated colostrum (PU or DTB) experienced significantly improved AEA and serum IgG concentrations. Copyright © 2015 American Dairy Science Association. Published by Elsevier Inc. All rights reserved.

Wrapping process for fabrication of A-15 superconducting composite wires

DOEpatents

Suenaga, M.; Klamut, C.J.; Luhman, T.S.

1980-08-15

A method for fabricating superconducting wires wherein a billet of copper containing filaments of niobium or vanadium is rolled to form a strip which is wrapped about a tin-alloy core to form a composite. The alloy is a tin-copper alloy for niobium filaments and a gallium-copper alloy for vanadium filaments. The composite is then drawn down to a desired wire size and heat treated. During the heat treatment process, the tin in the bronze reacts with the niobium to form the superconductor niobium tin. In the case where vanadium is used, the gallium in the gallium bronze reacts with the vanadium to form the superconductor vanadium gallium. This new process eliminates the costly annealing steps, external tin plating and drilling of bronze ingots required in a number of prior art processes.

Effect of the interaction of heat-processing style and fat type on the micellarization of lipid-soluble pigments from green and red pungent peppers (Capsicum annuum).

PubMed

Victoria-Campos, Claudia I; Ornelas-Paz, José de Jesús; Yahia, Elhadi M; Failla, Mark L

2013-04-17

The high diversity of carotenoids and chlorophylls in foods contrasts with the reduced number of pigments that typically are investigated in micellarization studies. In this study, pepper samples (raw and heat-treated) contained 68 individual pigments, but only 38 of them were micellarized after in vitro digestion. The micellarization of pigments was majorly determined by the interaction effect of processing style (food matrix effect) and fat type (saturated and unsaturated). The highest micellarization was observed with raw peppers. Unsaturated fat increased the micellarization of carotenoid esters, while the impact of fat on the micellarization of free carotenoids seemed to be dependent on pigment structure. The micellarization efficiency was diminished as the esterification level of carotenoids increased. The type of fatty acid moiety and the polarity of the carotenoids modulated their micellarization. Chlorophylls were transformed into pheophytins by heat-processing and digestion, with the pheophytins being stable under gastrointestinal conditions. Micellarization of pheophytins was improved by fat.

Using heat-treated starch to modify the surface of biochar and improve the tensile properties of biochar-filled stryene-butadiene rubber composites

USDA-ARS?s Scientific Manuscript database

Heat-treated starch is a renewable material that can be used to modify the surface chemistry of small particles. In this work, heat-treated starch was used to coat hydrophilic biochar particles in order to make them more hydrophobic. Then when added as filler to hydrophobic styrene-butadiene rubber,...

Mechanical Properties of Heat-treated Carbon Fibers

NASA Technical Reports Server (NTRS)

Effinger, Michael R.; Patel, Bhavesh; Koenig, John; Cuneo, Jaques; Neveux, Michael G.; Demos, Chrystoph G.

2004-01-01

Carbon fibers are selected for ceramic matrix composites (CMC) are based on their as-fabricated properties or on "that is what we have always done" technical culture while citing cost and availability when there are others with similar cost and availability. However, the information is not available for proper selection of carbon fibers since heat-treated properties are not known for the fibers on the market currently. Heat-treating changes the fiber's properties. Therefore, an effort was undertaken to establish fiber properties on 19 different types of fibers from six different manufactures for both PAN and pitch fibers. Heat-treating has been done at three different temperatures.

Methods of producing compounds from plant material

DOEpatents

Werpy, Todd A.; Schmidt, Andrew J.; Frye, Jr., John G.; Zacher, Alan H.; Franz, James A.; Alnajjar, Mikhail S.; Neuenschwander, Gary G.; Alderson, Eric V.; Orth, Rick J.; Abbas, Charles A.; Beery, Kyle E.; Rammelsberg, Anne M.; Kim, Catherine J.

2006-01-03

The invention includes methods of processing plant material by adding water to form a mixture, heating the mixture, and separating a liquid component from a solid-comprising component. At least one of the liquid component and the solid-comprising component undergoes additional processing. Processing of the solid-comprising component produces oils, and processing of the liquid component produces one or more of glycerol, ethylene glycol, lactic acid and propylene glycol. The invention includes a process of forming glycerol, ethylene glycol, lactic acid and propylene glycol from plant matter by adding water, heating and filtering the plant matter. The filtrate containing starch, starch fragments, hemicellulose and fragments of hemicellulose is treated to form linear poly-alcohols which are then cleaved to produce one or more of glycerol, ethylene glycol, lactic acid and propylene glycol. The invention also includes a method of producing free and/or complexed sterols and stanols from plant material.

Methods of producing compounds from plant materials

DOEpatents

Werpy, Todd A [West Richland, WA; Schmidt, Andrew J [Richland, WA; Frye, Jr., John G.; Zacher, Alan H. , Franz; James A. , Alnajjar; Mikhail S. , Neuenschwander; Gary G. , Alderson; Eric V. , Orth; Rick J. , Abbas; Charles A. , Beery; Kyle E. , Rammelsberg; Anne M. , Kim; Catherine, J [Decatur, IL

2010-01-26

The invention includes methods of processing plant material by adding water to form a mixture, heating the mixture, and separating a liquid component from a solid-comprising component. At least one of the liquid component and the solid-comprising component undergoes additional processing. Processing of the solid-comprising component produces oils, and processing of the liquid component produces one or more of glycerol, ethylene glycol, lactic acid and propylene glycol. The invention includes a process of forming glycerol, ethylene glycol, lactic acid and propylene glycol from plant matter by adding water, heating and filtering the plant matter. The filtrate containing starch, starch fragments, hemicellulose and fragments of hemicellulose is treated to form linear poly-alcohols which are then cleaved to produce one or more of glycerol, ethylene glycol, lactic acid and propylene glycol. The invention also includes a method of producing free and/or complexed sterols and stanols from plant material.

Study of structural, electrical, and dielectric properties of phosphate-borate glasses and glass-ceramics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Melo, B. M. G.; Graça, M. P. F., E-mail: mpfg@ua.pt; Prezas, P. R.

2016-08-07

In this work, phosphate-borate based glasses with molar composition 20.7P{sub 2}O{sub 5}–17.2Nb{sub 2}O{sub 5}–13.8WO{sub 3}–34.5A{sub 2}O–13.8B{sub 2}O{sub 3}, where A = Li, Na, and K, were prepared by the melt quenching technique. The as-prepared glasses were heat-treated in air at 800 °C for 4 h, which led to the formation of glass-ceramics. These high chemical and thermal stability glasses are good candidates for several applications such as fast ionic conductors, semiconductors, photonic materials, electrolytes, hermetic seals, rare-earth ion host solid lasers, and biomedical materials. The present work endorses the analysis of the electrical conductivity of the as-grown samples, and also the electrical, dielectric,more » and structural changes established by the heat-treatment process. The structure of the samples was analyzed using X-Ray powder Diffraction (XRD), Raman spectroscopy, and density measurements. Both XRD and Raman analysis confirmed crystals formation through the heat-treatment process. The electrical ac and dc conductivities, σ{sub ac} and σ{sub dc}, respectively, and impedance spectroscopy measurements as function of the temperature, varying from 200 to 380 K, were investigated for the as-grown and heat-treated samples. The impedance spectroscopy was measured in the frequency range of 100 Hz–1 MHz.« less

Heat Treat Shop in the Technical Services Building

NASA Image and Video Library

1948-01-21

A technician prepares a metal component for a high-temperature bake in the Heat Treatment Shop at the National Advisory Committee for Aeronautics (NACA) Lewis Flight Propulsion Laboratory. Fabrication Division under Dan White and John Dalgleish created almost all of the equipment and models used at the laboratory. The Technical Services Building, referred to as the Fab Shop, contained a number of specialized shops in the 1940s and 1950s. These included a Machine Shop, Sheet Metal Shop, Wood and Pattern Shop, Instrument Shop, Thermocouple Shop, Heat Treating Shop, Metallurgical Laboratory, and Fabrication Office. The Metallurgical Laboratory contained a control lab for the Heat Treating Shop and a service lab for the NACA Lewis research divisions. This metallurgical group performed tensile and impact tests on metals to determine their suitability for specific research or equipment. The Heat Treating Shop heated metal parts to optimize their physical properties and contained a Precision Castings Foundry to manufacture equipment made of heat resisting alloys.

Power systems utilizing the heat of produced formation fluid

DOEpatents

Lambirth, Gene Richard [Houston, TX

2011-01-11

Systems, methods, and heaters for treating a subsurface formation are described herein. At least one method includes treating a hydrocarbon containing formation. The method may include providing heat to the formation; producing heated fluid from the formation; and generating electricity from at least a portion of the heated fluid using a Kalina cycle.

Global and local investigations of the electrochemical behavior the T6 heat treated Mg-Zn-RE magnesium alloy thixo-cast

NASA Astrophysics Data System (ADS)

Szklarz, Zbigniew; Bisztyga, Magdalena; Krawiec, Halina; Lityńska-Dobrzyńska, Lidia; Rogal, Łukasz

2017-05-01

The influence of semi-solid metal processing (SSM called also as thixoforming) of ZE41A magnesium alloy on the electrochemical behavior in 0.1 M NaCl solution was investigated. To describe the corrosion behavior of ZE41A alloy, the electrochemical measurements were conducted in global and local scale for two types of specimens: (1) ingot-feedstock, (2) specimen after thixoforming and T6 treatment. The heat treatment and thixoforming significantly improved mechanical properties of ZE41A alloy. The global corrosion potential is slightly higher for treated sample what is related to the presence of Zr-Zn nanoparticles distributed in solid solution. The corrosion behavior differences between feedstock and thixo-cast after T6 samples are also visible in local scale, what has been revealed by using microcapillary technique. However there is no improvement in corrosion behavior after treatment. Corrosion morphology of the treated sample indicate higher susceptibility to pitting and filiform corrosion. Corrosion rate is also slightly higher.

Heat and mass transfer in flames

NASA Technical Reports Server (NTRS)

Faeth, G. M.

1986-01-01

Heat- and mass-transfer processes in turbulent diffusion flames are discussed, considering turbulent mixing and the structure of single-phase flames, drop processes in spray flames, and nonluminous and luminous flame radiation. Interactions between turbulence and other phenomena are emphasized, concentrating on past work of the author and his associates. The conserved-scalar formalism, along with the laminar-flamelet approximation, is shown to provide reasonable estimates of the structure of gas flames, with modest levels of empiricism. Extending this approach to spray flames has highlighted the importance of drop/turbulence interactions; e.g., turbulent dispersion of drops, modification of turbulence by drops, etc. Stochastic methods being developed to treat these phenomena are yielding encouraging results.

Arrhenius parameter determination as a function of heating method and cellular microenvironment based on spatial cell viability analysis.

PubMed

Whitney, Jon; Carswell, William; Rylander, Nichole

2013-06-01

Predictions of injury in response to photothermal therapy in vivo are frequently made using Arrhenius parameters obtained from cell monolayers exposed to laser or water bath heating. However, the impact of different heating methods and cellular microenvironments on Arrhenius predictions has not been thoroughly investigated. This study determined the influence of heating method (water bath and laser irradiation) and cellular microenvironment (cell monolayers and tissue phantoms) on Arrhenius parameters and spatial viability. MDA-MB-231 cells seeded in monolayers and sodium alginate phantoms were heated with a water bath for 3-20 min at 46, 50, and 54 °C or laser irradiated (wavelength of 1064 nm and fluences of 40 W/cm(2) or 3.8 W/cm(2) for 0-4 min) in combination with photoabsorptive carbon nanohorns. Spatial viability was measured using digital image analysis of cells stained with calcein AM and propidium iodide and used to determine Arrhenius parameters. The influence of microenvironment and heating method on Arrhenius parameters and capability of parameters derived from more simplistic experimental conditions (e.g. water bath heating of monolayers) to predict more physiologically relevant systems (e.g. laser heating of phantoms) were assessed. Arrhenius predictions of the treated area (<1% viable) under-predicted the measured areas in photothermally treated phantoms by 23 mm(2) using water bath treated cell monolayer parameters, 26 mm(2) using water bath treated phantom parameters, 27 mm(2) using photothermally treated monolayer parameters, and 0.7 mm(2) using photothermally treated phantom parameters. Heating method and cellular microenvironment influenced Arrhenius parameters, with heating method having the greater impact.

Selective Laser Melting Produced Ti-6Al-4V: Post-Process Heat Treatments to Achieve Superior Tensile Properties

PubMed Central

Becker, Thorsten H.

2018-01-01

Current post-process heat treatments applied to selective laser melting produced Ti-6Al-4V do not achieve the same microstructure and therefore superior tensile behaviour of thermomechanical processed wrought Ti-6Al-4V. Due to the growing demand for selective laser melting produced parts in industry, research and development towards improved mechanical properties is ongoing. This study is aimed at developing post-process annealing strategies to improve tensile behaviour of selective laser melting produced Ti-6Al-4V parts. Optical and electron microscopy was used to study α grain morphology as a function of annealing temperature, hold time and cooling rate. Quasi-static uniaxial tensile tests were used to measure tensile behaviour of different annealed parts. It was found that elongated α’/α grains can be fragmented into equiaxial grains through applying a high temperature annealing strategy. It is shown that bi-modal microstructures achieve a superior tensile ductility to current heat treated selective laser melting produced Ti-6Al-4V samples. PMID:29342079

Proctor and gamble technology process assessment for bioenergy production

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hu, Hongqiang; Boardman, Richard Doin; Wright, Christopher Todd

P&G intends to replace as much as their current heat and power by renewable energy sources. For 2014, P&G’s total energy including electricity, natural gas and steam is approximately 1,540,000 MMBTU annually (Table 2). The biomass and wastes around P&G facility can be grouped into six categories (Figure 6): (1) Agriculture residue and grass, (2) Refuse (inorganic) solid material, (3) Food waste, (4) Organic waste stream, (5) livestock manure, (6) wastewater and sludge. The six feedstock sources can provide a total energy of 3,520,000 MMBTU per year (Table 10), among which the agriculture residue is the biggest fraction, about 67%,more » followed by livestock manures 27%. Therefore, the available energy sources around P&G facility are enough to meet their energy needs. These energy feedstocks would be treated by two processes: anaerobic digestion for biogas subsequently for heat and power and thermochemical process (combustion, pyrolysis and gasification) for heat and power (Figure 8 and 9). For AD, a one-stage complete mixing digester is preferable; and fluidized bed reactors are favorable for thermochemical process.« less

Volatile sulphur compounds in UHT milk.

PubMed

Al-Attabi, Z; D'Arcy, B R; Deeth, H C

2009-01-01

Several volatile sulphur compounds have been detected in raw and processed milk. These are hydrogen sulphide, methanethiol, carbonyl sulphide, dimethyl sulphide, carbon disulphide, dimethyl disulphide, dimethyl trisulphide, dimethyl sulphoxide, and dimethyl sulphone. Many of these increase in milk during heat processing and are associated with the cooked flavor of heat-treated milks, particularly UHT and sterilized milk. Several researchers have attempted to explain the origin of these volatiles in both raw and processed milk, and how to reduce the associated cooked flavor that has a negative impact on consumer acceptability of processed milk. These compounds are difficult to detect and analyze due to their high volatility, sensitivity to oxidation and heat, and in some cases, their very low concentrations. However, methods of detection and quantification have improved in recent years. Pre-concentration methods such as solid phase microextraction (SPME) together with gas chromatography equipped with sulphur-selective detectors now enable low concentrations of these compounds to be analyzed. In this review, methods of extraction and analyzes of these volatile sulphur compounds are compared, and their occurrence in milk is reviewed.

Gin saw wear test

USDA-ARS?s Scientific Manuscript database

Most current gin saw manufacturers use a 1074 steel or similar as a basis to manufacture their saw blades. The saw teeth are individually punched on the edges of the blades and then the blade goes through a heat treating process prior to use. There are indications from other industries with similar ...

Treatment method for emulsified petroleum wastes

DOEpatents

Sealock, Jr., L. John; Baker, Eddie G.; Elliott, Douglas C.

1990-01-01

An improved reclamation process for treating petroleum oil and water emulsions derived from producing or processing crude oil is disclosed. The process comprises heating the emulsion to a predetermined temperature at or above about 300.degree. C. and pressurizing the emulsion to a predetermined pressure above the vapor pressure of water at the predetermined temperature. The emulsion is broken by containing the heated and pressurized fluid within a vessel at the predetermined temperature and pressure for a predetermined period of time to effectively separate the emulsion into substantially distinct first, second and third phases. The three phases are then separately withdrawn from the vessel, preferably without any appreciable reduction in temperature and pressure, and at least above a withdraw temperature of about 300.degree. and above the vapor pressure of water at the withdraw temperature.

Cooling Rate Study of Nickel-Rich Material During Thermal Treatment and Quench

NASA Technical Reports Server (NTRS)

Thomas, Fransua; Murguia, Silvia Briseno (Editor)

2016-01-01

To investigate quench cracking that results from water quenching after heat treatment of binary and Ni-rich material, cooling rates of specimens were measured during quenching and hardness post-thermal treatment. For specific applications binary Ni-Ti is customarily thermally treated and quenched to attain desired mechanical properties and hardness. However, one problem emerging from this method is thermal cracking, either during the heat treatment process or during the specimen's application. This can result in material and equipment failure as well as financial losses. The objective of the study is to investigate the internal cooling rate of 60-NiTi during quenching and determine possible factors causing thermal cracking. Cubic (1 in.3) samples of both material were heat treated in air at 1000 deg C for 2 hrs and quenched in room temperature water using two methods: (1) dropped in the water and (2) agitated in the water. Hardness of the two fore-mentioned methods was measured post heat treatment. Results indicate that the quenching method had an effect on cooling rate during quenching but hardness was observed to be essentially the same through the thickness of the samples.

Microbiota dynamics and diversity at different stages of industrial processing of cocoa beans into cocoa powder.

PubMed

Lima, Lídia J R; van der Velpen, Vera; Wolkers-Rooijackers, Judith; Kamphuis, Henri J; Zwietering, Marcel H; Nout, M J Rob

2012-04-01

We sampled a cocoa powder production line to investigate the impact of processing on the microbial community size and diversity at different stages. Classical microbiological methods were combined with 16S rRNA gene PCR-denaturing gradient gel electrophoresis, coupled with clone library construction, to analyze the samples. Aerobic thermoresistant spores (ThrS) (100°C; 10 min) were also isolated and characterized (identity, genetic diversity, and spore heat resistance), in view of their relevance to the quality of downstream heat-treated cocoa-flavored drinks. In the nibs (broken, shelled cocoa beans), average levels of total aerobic microorganisms (TAM) (4.4 to 5.6 log CFU/g) and aerobic total spores (TS) (80°C; 10 min; 4.3 to 5.5 log CFU/g) were significantly reduced (P < 0.05) as a result of alkalizing, while fungi (4.2 to 4.4 log CFU/g) and Enterobacteriaceae (1.7 to 2.8 log CFU/g) were inactivated to levels below the detection limit, remaining undetectable throughout processing. Roasting further decreased the levels of TAM and TS, but they increased slightly during subsequent processing. Molecular characterization of bacterial communities based on enriched cocoa samples revealed a predominance of members of the Bacillaceae, Pseudomonadaceae, and Enterococcaceae. Eleven species of ThrS were found, but Bacillus licheniformis and the Bacillus subtilis complex were prominent and revealed great genetic heterogeneity. We concluded that the microbiota of cocoa powder resulted from microorganisms that could have been initially present in the nibs, as well as microorganisms that originated during processing. B. subtilis complex members, particularly B. subtilis subsp. subtilis, formed the most heat-resistant spores. Their occurrence in cocoa powder needs to be considered to ensure the stability of derived products, such as ultrahigh-temperature-treated chocolate drinks.

Microbiota Dynamics and Diversity at Different Stages of Industrial Processing of Cocoa Beans into Cocoa Powder

PubMed Central

Lima, Lídia J. R.; van der Velpen, Vera; Wolkers-Rooijackers, Judith; Kamphuis, Henri J.; Nout, M. J. Rob

2012-01-01

We sampled a cocoa powder production line to investigate the impact of processing on the microbial community size and diversity at different stages. Classical microbiological methods were combined with 16S rRNA gene PCR-denaturing gradient gel electrophoresis, coupled with clone library construction, to analyze the samples. Aerobic thermoresistant spores (ThrS) (100°C; 10 min) were also isolated and characterized (identity, genetic diversity, and spore heat resistance), in view of their relevance to the quality of downstream heat-treated cocoa-flavored drinks. In the nibs (broken, shelled cocoa beans), average levels of total aerobic microorganisms (TAM) (4.4 to 5.6 log CFU/g) and aerobic total spores (TS) (80°C; 10 min; 4.3 to 5.5 log CFU/g) were significantly reduced (P < 0.05) as a result of alkalizing, while fungi (4.2 to 4.4 log CFU/g) and Enterobacteriaceae (1.7 to 2.8 log CFU/g) were inactivated to levels below the detection limit, remaining undetectable throughout processing. Roasting further decreased the levels of TAM and TS, but they increased slightly during subsequent processing. Molecular characterization of bacterial communities based on enriched cocoa samples revealed a predominance of members of the Bacillaceae, Pseudomonadaceae, and Enterococcaceae. Eleven species of ThrS were found, but Bacillus licheniformis and the Bacillus subtilis complex were prominent and revealed great genetic heterogeneity. We concluded that the microbiota of cocoa powder resulted from microorganisms that could have been initially present in the nibs, as well as microorganisms that originated during processing. B. subtilis complex members, particularly B. subtilis subsp. subtilis, formed the most heat-resistant spores. Their occurrence in cocoa powder needs to be considered to ensure the stability of derived products, such as ultrahigh-temperature-treated chocolate drinks. PMID:22327588

High speed measurement of corn seed viability using hyperspectral imaging

NASA Astrophysics Data System (ADS)

Ambrose, Ashabahebwa; Kandpal, Lalit Mohan; Kim, Moon S.; Lee, Wang-Hee; Cho, Byoung-Kwan

2016-03-01

Corn is one of the most cultivated crops all over world as food for humans as well as animals. Optimized agronomic practices and improved technological interventions during planting, harvesting and post-harvest handling are critical to improving the quantity and quality of corn production. Seed germination and vigor are the primary determinants of high yield notwithstanding any other factors that may play during the growth period. Seed viability may be lost during storage due to unfavorable conditions e.g. moisture content and temperatures, or physical damage during mechanical processing e.g. shelling, or over heating during drying. It is therefore vital for seed companies and farmers to test and ascertain seed viability to avoid losses of any kind. This study aimed at investigating the possibility of using hyperspectral imaging (HSI) technique to discriminate viable and nonviable corn seeds. A group of corn samples were heat treated by using microwave process while a group of seeds were kept as control group (untreated). The hyperspectral images of corn seeds of both groups were captured between 400 and 2500 nm wave range. Partial least squares discriminant analysis (PLS-DA) was built for the classification of aged (heat treated) and normal (untreated) corn seeds. The model showed highest classification accuracy of 97.6% (calibration) and 95.6% (prediction) in the SWIR region of the HSI. Furthermore, the PLS-DA and binary images were capable to provide the visual information of treated and untreated corn seeds. The overall results suggest that HSI technique is accurate for classification of viable and non-viable seeds with non-destructive manner.

Fourth order discretization of anisotropic heat conduction operator

NASA Astrophysics Data System (ADS)

Krasheninnikova, Natalia; Chacon, Luis

2008-11-01

In magnetized plasmas, heat conduction plays an important role in such processes as energy confinement, turbulence, and a number of instabilities. As a consequence of the presence of a magnetic field, heat transport is strongly anisotropic, with energy flowing preferentially along the magnetic field direction. This in turn results in parallel and perpendicular heat conduction coefficients being separated by orders of magnitude. The computational difficulties in treating such heat conduction anisotropies are significant, as perpendicular dynamics numerically is polluted by the parallel one. In this work, we report on progress of the implementation of a fourth order, conservative finite volume discretization scheme for the anisotropic heat conduction operator into the extended MHD code PIXIE3D [1]. We will demonstrate its spatial discretization accuracy and its effectiveness with two physical applications of interest, both of which feature a strong sensitivity to the heat conduction anisotropy: the thermal instability and the neoclassical tearing mode. [1] L. Chacon Phys. Plasmas 15, 056103 (2008)

Effect of Heat Treatment Temperature on Chemical Compositions of Extracted Hydroxyapatite from Bovine Bone Ash

NASA Astrophysics Data System (ADS)

Younesi, M.; Javadpour, S.; Bahrololoom, M. E.

2011-11-01

This article presents the effect of heat treating temperature on chemical composition of hydroxyapatite (HA) that was produced by burning bovine bone, and then heat treating the obtained bone ash at different temperatures in range of 600-1100 °C in air. Bone ash and the resulting white powder from heat treating were characterized by Fourier transformed infrared spectroscopy (FT-IR) and x-ray diffractometry (XRD). The FT-IR spectra confirmed that heat treating of bone ash at temperature of 800 °C removed the total of organic substances. x-ray diffraction analysis showed that the white powder was HA and HA was the only crystalline phase indicated in heat treating product. x-ray fluorescence analyses revealed that calcium and phosphorous were the main elements and magnesium and sodium were minor impurities of produced powder at 800 °C. The results of the energy dispersive x-ray analysis showed that Ca/P ratio in produced HA varies in range of 1.46-2.01. The resulting material was found to be thermally stable up to 1100 °C.

Microwave treatment of vulcanized rubber

DOEpatents

Wicks, George G [Aiken, SC; Schulz, Rebecca L [Aiken, SC; Clark, David E [Gainesville, FL; Folz, Diane C [Gainesville, FL

2002-07-16

A process and resulting product is provided in which a vulcanized solid particulate, such as vulcanized crumb rubber, has select chemical bonds broken by microwave radiation. The direct application of microwaves in combination with uniform heating of the crumb rubber renders the treated crumb rubber more suitable for use in new rubber formulations. As a result, larger particle sizes and/or loading levels of the treated crumb rubber can be used in new rubber mixtures to produce recycled composite products with good properties.

Convection measurement package for space processing sounding rocket flights. [low gravity manufacturing - fluid dynamics

NASA Technical Reports Server (NTRS)

Spradley, L. W.

1975-01-01

The effects on heated fluids of nonconstant accelerations, rocket vibrations, and spin rates, was studied. A system is discussed which can determine the influence of the convective effects on fluid experiments. The general suitability of sounding rockets for performing these experiments is treated. An analytical investigation of convection in an enclosure which is heated in low gravity is examined. The gravitational body force was taken as a time-varying function using anticipated sounding rocket accelerations, since accelerometer flight data were not available. A computer program was used to calculate the flow rates and heat transfer in fluids with geometries and boundary conditions typical of space processing configurations. Results of the analytical investigation identify the configurations, fluids and boundary values which are most suitable for measuring the convective environment of sounding rockets. A short description of fabricated fluid cells and the convection measurement package is given. Photographs are included.

Fate of pyrrolizidine alkaloids during processing of milk of cows treated with ragwort.

PubMed

de Nijs, Monique; Mulder, Patrick P J; Klijnstra, Mirjam D; Driehuis, Frank; Hoogenboom, Ron L A P

2017-12-01

To investigate the fate of pyrrolizidine alkaloids (PAs) during milk processing, milk of cows treated via rumen fistula with a mixture of 84% (w/w) ragwort (Jacobaea vulgaris, syn. Senecio jacobaea) and 16% narrow-leaved ragwort (Senecio inaequidens) was processed using laboratory scale heating systems with industrial settings. Pasteurised and sterilised (UHT) milk were produced, as well as set-type yoghurt and cheese. Samples were analysed for 29 PAs using LC-MS/MS, of which 11 PAs were detected above LOQ in the samples (0.1 µg l -1 ). Alterations in the PA concentration and composition between the standardised milk and the corresponding end-product(s) were evaluated. The heat treatments applied for pasteurisation and UHT sterilisation to prepare semi-skimmed consumption milk did not affect the PA levels in the end-products. In yoghurt, after fermentation of standardised milk (6 h, pH 4.4), 73% of total PAs were recovered. The PA concentration, specifically dehydrojacoline, was decreased, although not quantifiable, during cheese production. A further decrease of 38% during 6 weeks of ripening was observed. The results show that the PA concentration of natural contaminated cow's milk is not affected by heat treatment applied for pasteurised and sterilised milk, but that microbial fermentation of the milk leads to a lowered PA concentration in yoghurt and cheese. This is probably due to microbiological degradation, since PAs are fairly stable under acidic conditions.

Significance of heat-moisture treatment conditions on the pasting and gelling behaviour of various starch-rich cereal and pseudocereal flours.

PubMed

Collar, Concha

2017-10-01

The impact of heat-moisture treatment processing conditions (15%, 25%, and 35% moisture content; 1, 3, and 5 h heating time at 120 ℃) on the viscosity pasting and gelling profiles of different grain flours matrices (barley, buckwheat, sorghum, high β-glucan barley, and wheat) was investigated by applying successive cooking and cooling cycles to rapid visco analyser canisters with highly hydrated samples (3.5:25, w:w). At a milder heat-moisture treatment conditions (15% moisture content, 1 h heating time), except for sorghum, heat-moisture treatment flours reached much higher viscosity values during earlier pasting and subsequent gelling than the corresponding native counterparts. Besides heat-moisture treatment wheat flour, the described behaviour found also for non-wheat-treated flours has not been previously reported in the literature. An increased hydrophobicity of prolamins and glutelins in low moisture-short heating time heat-moisture treatment of non-wheat flours with high protein content (12.92%-19.95%) could explain the enhanced viscosity profile observed.

Exploring the heat-responsive chaperones and microsatellite markers associated with terminal heat stress tolerance in developing wheat.

PubMed

Kumar, Ranjeet R; Goswami, Suneha; Shamim, Mohammad; Dubey, Kavita; Singh, Khushboo; Singh, Shweta; Kala, Yugal K; Niraj, Ravi R K; Sakhrey, Akshay; Singh, Gyanendra P; Grover, Monendra; Singh, Bhupinder; Rai, Gyanendra K; Rai, Anil K; Chinnusamy, Viswanathan; Praveen, Shelly

2017-11-01

Global warming is a major threat for agriculture and food security, and in many cases the negative impacts are already apparent. Wheat is one of the most important staple food crops and is highly sensitive to the heat stress (HS) during reproductive and grain-filling stages. Here, whole transcriptome analysis of thermotolerant wheat cv. HD2985 was carried out at the post-anthesis stage under control (22 ± 3 °C) and HS-treated (42 °C, 2 h) conditions using Illumina Hiseq and Roche GS-FLX 454 platforms. We assembled ~24 million (control) and ~23 million (HS-treated) high-quality trimmed reads using different assemblers with optimal parameters. De novo assembly yielded 52,567 (control) and 59,658 (HS-treated) unigenes. We observed 785 transcripts to be upregulated and 431 transcripts to be downregulated under HS; 78 transcripts showed >10-fold upregulation such as HSPs, metabolic pathway-related genes, etc. Maximum number of upregulated genes was observed to be associated with processes such as HS-response, protein-folding, oxidation-reduction and photosynthesis. We identified 2008 and 2483 simple sequence repeats (SSRs) markers from control and HS-treated samples; 243 SSRs were observed to be overlying on stress-associated genes. Polymorphic study validated four SSRs to be heat-responsive in nature. Expression analysis of identified differentially expressed transcripts (DETs) showed very high fold increase in the expression of catalytic chaperones (HSP26, HSP17, and Rca) in contrasting wheat cvs. HD2985 and HD2329 under HS. We observed positive correlation between RNA-seq and qRT-PCR expression data. The present study culminated in greater understanding of the heat-response of tolerant genotype and has provided good candidate genes for the marker development and screening of wheat germplasm for thermotolerance.

Evaluation of the U.S. Department of Agriculture's egg pasteurization processes on the inactivation of high pathogenicity avian influenza virus and velogenic Newcastle disease virus in processed egg products

USDA-ARS?s Scientific Manuscript database

High pathogenicity avian influenza virus (HPAIV) A/chicken/Pennsylvania/1370/1983 (H5N2), and velogenic Newcastle disease virus (vNDV) AMPV-1/California/212676/2002 were inoculated into various egg products then heat treated at various temperatures for 0 to 30 min to determine thermal inactivation p...

Sealing ceramic material in low melting point glass

NASA Technical Reports Server (NTRS)

Moritoki, M.; Fujikawa, T.; Miyanaga, J.

1984-01-01

A structured device placed in an aerated crucible to pack ceramics molding substance that is to be processed was designed. The structure is wrapped by sealing material made of pyrex glass and graphite foil or sheet with a weight attached on top of it. The crucible is made of carbon; the ceramics material to be treated through heat intervenient press process is molding substance consisting mainly of silicon nitride.

Sensible and latent heat forced divergent circulations in the West African Monsoon System

NASA Astrophysics Data System (ADS)

Hagos, S.; Zhang, C.

2008-12-01

Field properties of divergent circulation are utilized to identify the roles of various diabatic processes in forcing moisture transport in the dynamics of the West African Monsoon and its seasonal cycle. In this analysis, the divergence field is treated as a set of point sources and is partitioned into two sub-sets corresponding to latent heat release and surface sensible heat flux at each respective point. The divergent circulation associated with each set is then calculated from the Poisson's equation using Gauss-Seidel iteration. Moisture transport by each set of divergent circulation is subsequently estimated. The results show different roles of the divergent circulations forced by surface sensible and latent heating in the monsoon dynamics. Surface sensible heating drives a shallow meridional circulation, which transports moisture deep into the continent at the polar side of the monsoon rain band and thereby promotes the seasonal northward migration of monsoon precipitation during the monsoon onset season. In contrast, the circulation directly associated with latent heating is deep and the corresponding moisture convergence is within the region of precipitation. Latent heating also induces dry air advection from the north. Neither effect promotes the seasonal northward migration of precipitation. The relative contributions of the processes associated with latent and sensible heating to the net moisture convergence, and hence the seasonal evolution of monsoon precipitation, depend on the background moisture.

Effective treatment for suppression of acrylamide formation in fried potato chips using L-asparaginase from Bacillus subtilis.

PubMed

Onishi, Yohei; Prihanto, Asep A; Yano, Shigekazu; Takagi, Kazuyoshi; Umekawa, Midori; Wakayama, Mamoru

2015-10-01

It has been reported that acrylamide, a potential carcinogen, is formed from the reaction of L-asparagine (L-Asn) and reducing sugars contained in foods during heating processes and free asparagine is a limiting factor for acrylamide formation. It has been reported that potato products such as potato chips, which are made through heating processes, contain high levels of acrylamide. To decrease the amount of L-Asn in potatoes using L-asparaginase, effective treatment conditions of sliced potatoes with the enzyme have been investigated. By treating sliced potatoes with Bacillus subtilis L-asparaginase II (BAsnase; 4 U/g potato), appriximately 40 % of L-Asn in the sliced potatoes was converted into L-aspartic acid (L-Asp). To make this enzyme more effective, prior to enzymatic treatment, sliced potatoes were freeze-thawed, dried at 90 °C for 20 min, and vacuum treated for 10 min under decompressed condition, resulting in the hydrolysis of approximately 90 % of L-Asn to L-Asp. The acrylamide content of BAsnase-treated fried potato chips decreased to below 20 % of that of BAsnase-untreated fried potato chips. Treatment conditions examined in this study were found to be effective to suppress the formation of acrylamide in fried potato chips.

Study of the Productivity and Surface Quality of Hybrid EDM

NASA Astrophysics Data System (ADS)

Wankhade, Sandeepkumar Haribhau; Sharma, Sunil Bansilal

2016-01-01

The development of new, advanced engineering materials and the need for precise prototypes and low-volume production have made the electric discharge machining (EDM), an important manufacturing process to meet such demands. It is capable of machining geometrically complex and hard material components, that are precise and difficult-to-machine such as heat treated tool steels, composites, super alloys, ceramics, carbides etc. Conversely the low MRR limits its productivity. Abrasive water jet machine (AJM) tools are quick to setup and offer quick turn-around on the machine and could make parts out of virtually any material. They do not heat the material hence no heat affected zone and can make any intricate shape easily. The main advantages are flexibility, low heat production and ability to machine hard and brittle materials. Main disadvantages comprise the process produces a tapered cut and health hazards due to dry abrasives. To overcome the limitations and exploit the best of each of above processes; an attempt has been made to hybridize the processes of AJM and EDM. The appropriate abrasives routed with compressed air through the hollow electrode to construct the hybrid process i.e., abrasive jet electric discharge machining (AJEDM), the high speed abrasives could impinge on the machined surface to remove the recast layer caused by EDM process. The main process parameters were varied to explore their effects and experimental results show that AJEDM enhances the machining efficiency with better surface finish hence can fit the requirements of modern manufacturing applications.

Submammary Granular Parakeratosis Treated With Mastopexy.

PubMed

Nelson, Garrett; Lien, Mary H; Messina, Jane L; Ranjit, Sonali; Fenske, Neil Alan

2017-08-01

Granular parakeratosis, originally named axillary granular parakeratosis, is an uncommon disease with an unclear etiology. It is thought to result from defective processing of profillagrin to fillagrin, causing retention of keratohyaline granules in the epidermis. A myriad of causative factors has been proposed, including friction, moisture, heat, and contact irritants such as deodorants. We present a case in the inframammary area that resolved with mastopexy, further supporting the role of friction, moisture, and heat. Furthermore, we present electron microscopic evidence demonstrating non-degraded keratohyaline granules upon epidermal maturation. This entity, we believe, is reactive and represents a protective response of the body to moisture and heat.

J Drugs Dermatol. 2017;16(8):810-812.

Effect of heat-setting on UV protection and antibacterial properties of cotton/spandex fabric

NASA Astrophysics Data System (ADS)

Pervez, M. N.; Talukder, M. E.; Shafiq, F.; Hasan, K. M. F.; Taher, M. A.; Meraz, M. M.; Cai, Y.; Lin, Lina

2018-01-01

An unexampled approach for simultaneous heat setting process with optimized condition at C3 (140°C, 45 s) and functional finishing, i.e. UV protection and antibacterial properties of cotton/spandex fabric were studied in this research. Experimental results disclosed that, ameliorative antibacterial efficacy and perdurable UV protection of heat-treated cotton/spandex fabrics with best sample A3 among all samples was achieved and mechanical properties also improved as the temperature rose from 120 to 140°C. In addition, Ultraviolet (UV) radiation protection and antibacterial properties are becoming increasingly necessary for human health, and textiles play an important role and this report will be appurtenant to meet regular demand.

Multi-scale Microstructure Characterization for Improved Understanding of Microstructure-Property Relationship in Additive Manufacturing

NASA Astrophysics Data System (ADS)

Song, Hye Yun

Additive manufacturing (AM) is the process for making 3-D objects by adding materials layer by layer. It can result in a marked reduction of the time and cost associated with designing and producing highly complex parts. Over the past decade, significant progress has been made in machine hardware and control software for process development to achieve dimensional accuracy and mitigate defects. On the other hand, the knowledge on microstructure-property relationship in the additively manufactured builds is still being established. In additive manufacturing, the interactions between the heat source and the material lead to a series of physical phenomena including localized heating, melting, solidification and micro-segregation, and cooling. Far-from-equilibrium microstructure can form as the material experiences a large number of repeated, rapid heating and cooling cycles (i.e. temperature gyrations) during depositions. The mechanical properties of additively manufactured parts are significantly influenced by their final microstructure. The overarching goal of the present research is to improve the fundamental understanding of microstructure-property relationship for AM parts. Specially, it is investigated the high-temperature creep strength of InconelRTM 718 (abbreviated as IN718 thereafter) fabricated by laser-powder bed fusion (L-PBF) AM. The specific objectives include (1) effect of support on the local microstructure, (2) microstructure evolution during post-built heat treatment, and (3) creep strength. Detailed microstructure characterization is performed using a multitude of tools including micro-hardness mapping, scanning electron microscope (SEM) along with electron backscatter diffraction (EBSD), and transmission electron microscope (TEM) for selected area diffraction (SAD) analysis and energy-dispersive X-ray spectroscopy (EDS). The characterized microstructure is correlated to the mechanical properties. Highlights of the research findings are discussed in the following. A support is a "temporary" structure typically built in-situ with the primary part to provide the structural support to the mass of overhanging features; it is subsequently removed after fabrication. During the building process, the existence of such support can affect the local heat flow from the build to the substrate, which in turn may influence the local microstructure. The first objective of this research is to develop a fundamental understanding of the effect of the support on the microstructure fabricated by L-PBF AM. Two groups of as-built samples, with support and without support, are studied. SEM along with EBSD is used to analyze the microstructure characteristics including the growth of the microstructures, the fraction of different microstructure and the misorientation among the microstructure grains. At the nano-scale resolution, TEM is used to identify the precipitate phases. In addition, the micro-hardness values are also measured for samples built with and without support. As a precipitation-strengthened alloy, the heat treatment is critical for IN718, since the desired mechanical properties, such as high-temperature tensile and creep strength, are only acquired by the formation of the strengthening precipitates, namely gamma' prime and gamma''. Currently, the industrial standards for the heat treatment of IN718 are developed for cast and wrought cases and not specifically for AM builds. Thus, it is essential to evaluate the effect of the heat treatment on the formation of the strengthening precipitates in IN718 builds fabricated by L-PBF AM, which is the focus of the second objective. Particularly, a modification to the industry standard heat treatment is developed to maximize the fraction of the strengthening precipitates in the IN718 builds. The microstructural characterizations are performed for several modified heat treatment cases including a homogenization step, solution annealing step and aging step. The micro-hardness values are measured for as-built conditions and several heat-treated conditions including the modified homogenization, solution anneal and aging steps. Finally, the oxidation behavior during the heat treatment is also discussed and compared to that for a piece of actual cast. The third objective of the present study is the evaluation of the mechanical properties of heat-treated IN718 builds produced by L-PBF AM. Particularly, creep test are performed to quantify the mechanical properties of the heat-treated IN718 builds. The creep samples are heat-treated using the following condition: homogenization at 1100 °C for 2 hours followed by air cooling (AC), and aging at 760 °C for 10 hours also followed by AC. For the creep test, the samples are loaded at a constant stress (690 MPa or 100 ksi) at 649 °C (1200 °F) in accordance to Aerospace Material Standards (AMS) 5663. The creep rate of the heat-treated AM sample is compared with the literature data for wrought cases. The relationship of creep strength to the characteristic of the microstructures in the heat-treated IN718 builds is discussed. In summary, the research results provide insights into the microstructure-creep-strength relationship for IN718 fabricated by additive manufacturing. Particularly, a modified post-built heat treatment is developed to maximize the formation of strengthening precipitates and achieve large grains in IN718, resulting in a markedly higher creep strength when compared to the literature data for wrought cases. Taken as a whole, the new knowledge generated in this dissertation is essential to ensure the performance of additively manufactured parts in structural applications.

Mechanism of microwave sterilization in the dry state.

PubMed Central

Jeng, D K; Kaczmarek, K A; Woodworth, A G; Balasky, G

1987-01-01

With an automated computerized temperature control and a specialized temperature measurement system, dry spores of Bacillus subtilis subsp. niger were treated with heat simultaneously in a convection dry-heat oven and a microwave oven. The temperature of the microwave oven was monitored such that the temperature profiles of the spore samples in both heat sources were nearly identical. Under these experimental conditions, we unequivocally demonstrated that the mechanism of sporicidal action of the microwaves was caused solely by thermal effects. Nonthermal effects were not significant in a dry microwave sterilization process. Both heating systems showed that a dwelling time of more than 45 min was required to sterilize 10(5) inoculated spores in dry glass vials at 137 degrees C. The D values of both heating systems were 88, 14, and 7 min at 117, 130, and 137 degrees C, respectively. The Z value was estimated to be 18 degrees C. PMID:3118807

Numerical simulations of loops heated to solar flare temperatures. III - Asymmetrical heating

NASA Technical Reports Server (NTRS)

Cheng, C.-C.; Doschek, G. A.; Karpen, J. T.

1984-01-01

A numerical model is defined for asymmetric full solar flare loop heating and comparisons are made with observational data. The Dynamic Flux Tube Model is used to describe the heating process in terms of one-dimensional, two fluid conservation equations of mass, energy and momentum. An adaptive grid allows for the downward movement of the transition region caused by an advancing conduction front. A loop 20,000 km long is considered, along with a flare heating system and the hydrodynamic evolution of the loop. The model was applied to generating line profiles and spatial X-ray and UV line distributions, which were compared with SMM, P78-1 and Hintori data for Fe, Ca and Mg spectra. Little agreement was obtained, and it is suggested that flares be treated as multi-loop phenomena. Finally, it is concluded that chromospheric evaporation is not an effective mechanism for generating the soft X-ray bursts associated with flares.

New process for preparing complex-shaped dielectric film similar to Mylar

NASA Astrophysics Data System (ADS)

Lagasse, R. R.; Kraynik, A. M.

1982-02-01

A new thermoforming/heat-treatment process yields complex-shaped dielectric film having electrical and shrinkage properties similar to those of flat Mylar film. This similarity should extend to other physical properties because the new process is directly analogous to the process used to prepare Mylar. Commercially available poly(ethylene terephthalate) film is formed into a cavity at approx. 110 C and then heat treated at approx. 180 C. A laboratory-scale forming apparatus has produced cylindrically shaped films having depth/diameter ratio approx. 1, a tapered wall-section, and variation in wall thickness of 3X. Evaluation of other forming methods suggest that the production rate and thickness uniformity can be improved with existing technology. Thermal shrinkage at 150 C, 1 kHz dielectric constant from -55 to +70 C, leakage current at 1 kV, and breakdown voltage have been measured for both the complex-shaped film and Mylar.

Bacteriocin-like inhibitory activities of seven Lactobacillus delbrueckii subsp. bulgaricus strains against antibiotic susceptible and resistant Helicobacter pylori strains.

PubMed

Boyanova, L; Gergova, G; Markovska, R; Yordanov, D; Mitov, I

2017-12-01

The aim of the study was to detect anti-Helicobacter pylori activity of seven Lactobacillus delbrueckii subsp. bulgaricus (GLB) strains by four cell-free supernatant (CFS) types. Activity of non-neutralized and non-heat-treated (CFSs1), non-neutralized and heat-treated (CFSs2), pH neutralized, catalase-treated and non-heat-treated (CFSs3), or neutralized, catalase- and heat-treated (CFSs4) CFSs against 18 H. pylori strains (11 of which with antibiotic resistance) was evaluated. All GLB strains produced bacteriocin-like inhibitory substances (BLISs), the neutralized CFSs of two GLB strains inhibited >81% of test strains and those of four GLB strains were active against >71% of antibiotic resistant strains. Two H. pylori strains were BLIS resistant. The heating did not reduce the CFS activity. Briefly, all GLB strains evaluated produced heat-stable BLISs, although GLB and H. pylori strain susceptibility patterns exhibited differences. Bacteriocin-like inhibitory substance activity can be an advantage for the probiotic choice for H. pylori infection control. In this study, anti-Helicobacter pylori activity of seven Lactobacillus delbrueckii subsp. bulgaricus (GLB) strains was evaluated by four cell-free supernatant (CFS) types. The GLB strains produced heat-stable bacteriocin-like inhibitory substances (BLISs) with a strong anti-H. pylori activity and some neutralized, catalase- and heat-treated CFSs inhibited >83% of the test strains. Bacteriocin-like inhibitory substance production of GLB strains can render them valuable probiotics in the control of H. pylori infection. © 2017 The Society for Applied Microbiology.

Determination of chemical changes in heat-treated wood using ATR-FTIR and FT Raman spectrometry

NASA Astrophysics Data System (ADS)

Özgenç, Özlem; Durmaz, Sefa; Boyaci, Ismail Hakki; Eksi-Kocak, Haslet

2017-01-01

In this study, attenuated total reflectance-Fourier transform infrared (ATR-FTIR) and Fourier-transform Raman (FT-Raman) spectroscopy techniques were used to determine changes in the chemical structure of heat-treated woods. For this purpose, scots pine (Pinus sylvestris L.), oriental beech (Fagus orientalis L.), and oriental spruce (Picea orientalis L.) wood species were heat-treated at different temperatures. The effect of chemical changes on the FT-Raman and ATR-FTIR bands or ratios of heat-treated wood was related with the OH association of cellulose, functional groups, and the aromatic system of lignin. The effects of heat treatment on the carbohydrate and lignin peaks varied depending on the wood species. The spectral changes that occurred after heat treatment reflected the progress of the condensation reaction of lignin. Degradation of hemicelluloses led to a decrease in free hydroxyl groups. High temperature caused crystalline cellulose to increase due to the degradation of amorphous cellulose.

Determination of chemical changes in heat-treated wood using ATR-FTIR and FT Raman spectrometry.

PubMed

Özgenç, Özlem; Durmaz, Sefa; Boyaci, Ismail Hakki; Eksi-Kocak, Haslet

2017-01-15

In this study, attenuated total reflectance-Fourier transform infrared (ATR-FTIR) and Fourier-transform Raman (FT-Raman) spectroscopy techniques were used to determine changes in the chemical structure of heat-treated woods. For this purpose, scots pine (Pinus sylvestris L.), oriental beech (Fagus orientalis L.), and oriental spruce (Picea orientalis L.) wood species were heat-treated at different temperatures. The effect of chemical changes on the FT-Raman and ATR-FTIR bands or ratios of heat-treated wood was related with the OH association of cellulose, functional groups, and the aromatic system of lignin. The effects of heat treatment on the carbohydrate and lignin peaks varied depending on the wood species. The spectral changes that occurred after heat treatment reflected the progress of the condensation reaction of lignin. Degradation of hemicelluloses led to a decrease in free hydroxyl groups. High temperature caused crystalline cellulose to increase due to the degradation of amorphous cellulose. Copyright © 2016 Elsevier B.V. All rights reserved.

The Effects of One and Double Heat Treatment Cycles on the Microstructure and Mechanical Properties of a Ferritic-Bainitic Dual Phase Steel

NASA Astrophysics Data System (ADS)

Piri, Reza; Ghasemi, Behrooz; Yousefpour, Mardali

2018-03-01

In this study, samples with ferritic-bainitic dual phase structures consisting of 62 pct bainite were obtained from the AISI 4140 steel by applying one and double heat treatment cycles. Microstructural investigations by electron and optical microscopy indicated that the sample heat treated through double cycle benefited from finer ferrite and bainite grains. Additionally, results obtained from mechanical tests implied that the double-cycle heat-treated sample not only has a higher tensile strength as well as ultimate strength but also benefits from a higher ductility along with a higher impact energy than the one-cycle heat-treated sample. Moreover, fractography results showed that the type of fracture in both samples is a combination of the brittle and the ductile fracture. Besides, the ratio of the ductile fracture is higher for the double-cycle heat-treated sample than for the one-cycle sample, due to the lower aggregation of sulfur at grain boundaries.

Experimental study of the structure of vapor phase during boiling of R134a on heat exchange surfaces of heat pump

NASA Astrophysics Data System (ADS)

Ustinov, D. A.; Sukhikh, A. A.; Sidenkov, D. V.; Ustinov, V. A.

2017-10-01

The heat supply by means of heat pumps is considered now as a rational method of local heating which can lead to economy of primary fuel. At use of low-potential heat, for example, the heat of a ground (5 … 18 °C) or ground waters (8 … 10°C) only small depressing of temperature of these sources (on 3 … 5°C) is possible that demands application of heat exchangers with intensified heatmass transfer surfaces. In thermal laboratory of TOT department the 200 W experimental installation has been developed for research of process of boiling of freon R134a. The principle of action of the installation consists in realisation of reverse thermodynamic cycle and consecutive natural measurement of characteristics of elements of surfaces of heat exchangers of real installations at boiling points of freon from-10°C to +10°C and condensing temperatures from 15°C to 50 °C. The evaporator casing has optical windows for control of process of boiling of freon on ribbed on technology of distorting cut tubes. Temperature measurement in characteristic points of a cycle is provided by copper-constantan thermocouples which by means of ADT are connected to the computer that allows treat results of measurements in a real time mode. The structure of a two-phase flow investigated by means of the optical procedure based on laser technique.

Effect of high pressure processing on dispersive and aggregative properties of almond milk.

PubMed

Dhakal, Santosh; Giusti, M Monica; Balasubramaniam, V M

2016-08-01

A study was conducted to investigate the impact of high pressure (450 and 600 MPa at 30 °C) and thermal (72, 85 and 99 °C at 0.1 MPa) treatments on dispersive and aggregative characteristics of almond milk. Experiments were conducted using a kinetic pressure testing unit and water bath. Particle size distribution, microstructure, UV absorption spectra, pH and color changes of processed and unprocessed samples were analyzed. Raw almond milk represented the mono model particle size distribution with average particle diameters of 2 to 3 µm. Thermal or pressure treatment of almond milk shifted the particle size distribution towards right and increased particle size by five- to six-fold. Micrographs confirmed that both the treatments increased particle size due to aggregation of macromolecules. Pressure treatment produced relatively more and larger aggregates than those produced by heat treated samples. The apparent aggregation rate constant for 450 MPa and 600 MPa processed samples were k450MPa,30°C  = 0.0058 s(-1) and k600MPa,30°C  = 0.0095 s(-1) respectively. This study showed that dispersive and aggregative properties of high pressure and heat-treated almond milk were different due to differences in protein denaturation, particles coagulation and aggregates morphological characteristics. Knowledge gained from the study will help food processors to formulate novel plant-based beverages treated with high pressure. © 2015 Society of Chemical Industry. © 2015 Society of Chemical Industry.

The Effects of Substrate Material and Thermal Processing Atmosphere on the Strength of PS304: A High Temperature Solid Lubricant Coating

NASA Technical Reports Server (NTRS)

DellaCorte, Christopher

2002-01-01

PS304, a plasma spray deposited solid lubricant coating developed for high temperature sliding contacts was deposited on nine different substrate metals, heat treated at 650C in either air or argon and subsequently tested for strength using a commercially available pull-off adhesion test. Some samples were examined metallographically to help elucidate and explain the results. As deposited coatings exhibit pull-off strengths typically between 16 and 20 MPa with failure occuring (cohesively) within the coating. Heat treatment in argon at 650 C results in a slight increase in coating (cohesive) strength of about 30 percent to 21 to 27 MPa. Heat treatment in air at 650 C results in a dramatic increase in strength to over 30 MPa, exceeding the strength of the epoxy used in the pull test. Cross section metallographic analyses show that no microstructural coating changes occur following the argon heat treatments, however, exposure to air at 650C gives rise to the formation of a second chromium-rich phase precipitate within the PS304 NiCr constituent which provides a strengthening effect and a slight (approximately 5 percent) coating thickness increase. Subsequent heat treatments do not result in any further coating changes. Based upon these studies, PS304 is a suitable coating for use on a wide variety of high temperature substrates and must be heat treated following deposition to enhance strength and ensure dimensional stability.

Effect of heat treatment on the efficient adsorption of Cd2+ ions by nanosized SiO2, TiO2 and their composite

NASA Astrophysics Data System (ADS)

Waseem, M.; Muntha, S. T.; Nawaz, M.; Rehman, W.; Rehman, M. A.; Shah, K. H.

2017-01-01

In this study nanosized SiO2, TiO2 and their composite were synthesized via the oil in water (o/w) microemulsion method and their thermal treatment was performed at 378, 573, 973 and 1273 K. The physicochemical properties of the samples were studied by surface area measurements, scanning electron microscopy, Fourier transform infra-red spectroscopy and x-ray diffraction analysis. The Brunauer, Emmett and Teller surface area of all the adsorbents increases from 378 to 573 K, while it decreases upon further heat treatment. The average crystallite size decreases by heating the samples from 378 to 573 K while it increases when the adsorbents were thermally heat treated at 973 and 1273 K. The intensity of a few IR bands was reduced along with the disappearance of most of the bands at higher temperatures. The appearance of the beta-cristobalite phase in SiO2 and the rutile phase in TiO2 was confirmed from the diffraction data. The heat treated samples were subjected to preliminary adsorption of Cd2+ ions from aqueous solution at 293 K. Based on the preliminary adsorption experiments, SiO2, TiO2 and their composite heat treated at 573 K were selected for further adsorption studies. The Langmuir model was found to be fitted to the sorption data of TiO2 and the nanocomposite while the adsorption of Cd2+ ions by the SiO2 nanoparticles was explained well based on the Freundlich model. In the present study, the maximum Cd2+ adsorption capacity of SiO2, TiO2 and their composite was found to be 79.72, 98.55 and 107.17 mg g-1, respectively. The q m and K f values obtained in the present study were found to be far better than those reported in the literature. The negative values of ΔG confirm the feasibility of an adsorption process at higher temperatures. The positive values of ΔH and ΔS represent the endothermic and physical nature of the adsorption process with the increased randomness of Cd2+ ions at the solid/solution interface.

Die another day: Fate of heat-treated Geobacillus stearothermophilus ATCC 12980 spores during storage under growth-preventing conditions.

PubMed

Mtimet, Narjes; Trunet, Clément; Mathot, Anne-Gabrielle; Venaille, Laurent; Leguérinel, Ivan; Coroller, Louis; Couvert, Olivier

2016-06-01

Geobacillus stearothermophilus spores are recognized as one of the most wet-heat resistant among aerobic spore-forming bacteria and are responsible for 35% of canned food spoilage after incubation at 55 °C. The purpose of this study was to investigate and model the fate of heat-treated survivor spores of G. stearothermophilus ATCC 12980 in growth-preventing environment. G. stearothermophilus spores were heat-treated at four different conditions to reach one or two decimal reductions. Heat-treated spores were stored in nutrient broth at different temperatures and pH under growth-preventing conditions. Spore survival during storage was evaluated by count plating over a period of months. Results reveal that G. stearothermophilus spores surviving heat treatment lose their viability during storage under growth-preventing conditions. Two different subpopulations were observed during non-thermal inactivation. They differed according to the level of their resistance to storage stress, and the proportion of each subpopulation can be modulated by heat treatment conditions. Finally, tolerance to storage stress under growth-preventing conditions increases at refrigerated temperature and neutral pH regardless of heat treatment conditions. Such results suggest that spore inactivation due to heat treatment could be completed by storage under growth-preventing conditions. Copyright © 2016 Elsevier Ltd. All rights reserved.

Microbiological Safety of Animal Wastes Processed by Physical Heat Treatment: An Alternative To Eliminate Human Pathogens in Biological Soil Amendments as Recommended by the Food Safety Modernization Act.

PubMed

Chen, Zhao; Jiang, Xiuping

2017-03-01

Animal wastes have high nutritional value as biological soil amendments of animal origin for plant cultivation in sustainable agriculture; however, they can be sources of some human pathogens. Although composting is an effective way to reduce pathogen levels in animal wastes, pathogens may still survive under certain conditions and persist in the composted products, which potentially could lead to fresh produce contamination. According to the U.S. Food and Drug Administration Food Safety Modernization Act, alternative treatments are recommended for reducing or eliminating human pathogens in raw animal manure. Physical heat treatments can be considered an effective method to inactivate pathogens in animal wastes. However, microbial inactivation in animal wastes can be affected by many factors, such as composition of animal wastes, type and physiological stage of the tested microorganism, and heat source. Following some current processing guidelines for physical heat treatments may not be adequate for completely eliminating pathogens from animal wastes. Therefore, this article primarily reviews the microbiological safety and economic value of physically heat-treated animal wastes as biological soil amendments.

9 CFR 318.305 - Equipment and procedures for heat processing systems.

Code of Federal Regulations, 2011 CFR

2011-01-01

... ensure a supply of clean, dry air. The recorder timing mechanism shall be accurate. (i) Chart-type... filter systems to ensure a supply of clean, dry air. (ii) Pressure recording device. Each retort shall be... section. (2) Cooling canal water shall be chlorinated or treated with a chemical approved by the...

Manufacturing process to reduce large grain growth in zirconium alloys

DOEpatents

Rosecrans, Peter M.

1987-01-01

A method of treating cold-worked zirconium alloys to reduce large grain gth during thermal treatment at temperatures above the recrystallization temperature of the alloy comprising heating the cold-worked alloy between about 1300.degree.-1350.degree. F. for 1 to 3 hours prior to treatment above its recrystallization temperature.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Plotkowski, A.; Rios, O.; Sridharan, N.

Our present research in metal additive manufacturing (AM) focuses on designing processing parameters around existing alloys designed for traditional manufacturing. However, to maximize the benefits of AM, alloys should be designed to specifically take advantage of the unique thermal conditions of these processes. Furthermore, our study focuses on the development of a design methodology for alloys in AM, using a newly developed Al-Ce alloy as an initial case study. To evaluate the candidacy of this system for fusion based additive manufacturing, single-line laser melts were made on cast Al-12Ce plates using three different beam velocities (100, 200, and 300 mm/min).more » The microstructure was evaluated in the as-melted and heat treated conditions (24 hrs at 300°C). An extremely fine microstructure was observed within the weld pools, evolving from eutectic at the outer solid-liquid boundaries to a primary Al FCC dendritic/cellular structure nearer the melt-pool centerline. We rationalized the observed microstructures through the construction of a microstructure selection map for the Al-Ce binary system, which will be used to enable future alloy design. Interestingly, the heat treated samples exhibited no microstructural coarsening.« less

Effect of cathode vibration and heat treatment on electromagnetic properties of flake-shaped diatomite coated with Ni-Fe alloy by electroplating

NASA Astrophysics Data System (ADS)

Lan, Mingming; Li, Huiqin; Huang, Weihua; Xu, Guangyin; Li, Yan

2015-03-01

In this paper, flake-shaped diatomite particles were used as forming templates for the fabrication of the ferromagnetic functional fillers by way of electroplating Ni-Fe alloy method. The effects of cathode vibration frequency on the content of Ni-Fe alloy in the coating and the surface morphologies of the coatings were evaluated. The electromagnetic properties of the coated diatomite particles before and after heat treatment were also investigated in detail. The results show that the core-shell flake-shaped diatomite particles with high content of Ni-Fe alloy and good surface qualities of the coatings can be obtained by adjusting cathode vibration frequency. The coated diatomite particles with heat treatment filled paraffin wax composites exhibit a superior microwave absorbing and electromagnetic properties compared to the non-heat treated samples. Additionally, the peaks of reflection loss are found to be able to shift to lower frequency by the heat treatment process, which indicates the heat treatment can adjust microwave absorbing frequency band.

Metallurgical and Corrosion Characterization of POST Weld Heat Treated Duplex Stainless Steel (uns S31803) Joints by Friction Welding Process

NASA Astrophysics Data System (ADS)

Asif M., Mohammed; Shrikrishna, Kulkarni Anup; Sathiya, P.

2016-02-01

The present study focuses on the metallurgical and corrosion characterization of post weld heat treated duplex stainless steel joints. After friction welding, it was confirmed that there is an increase in ferrite content at weld interface due to dynamic recrystallization. This caused the weldments prone to pitting corrosion attack. Hence the post weld heat treatments were performed at three temperatures 1080∘C, 1150∘C and 1200∘C with 15min of aging time. This was followed by water and oil quenching. The volume fraction of ferrite to austenite ratio was balanced and highest pit nucleation resistance were achieved after PWHT at 1080∘C followed by water quench and at 1150∘C followed by oil quench. This had happened exactly at parameter set containing heating pressure (HP):40 heating time (HT):4 upsetting pressure (UP):80 upsetting time (UP):2 (experiment no. 5). Dual phase presence and absence of precipitates were conformed through TEM which follow Kurdjumov-Sachs relationship. PREN of ferrite was decreasing with increase in temperature and that of austenite increased. The equilibrium temperature for water quenching was around 1100∘C and that for oil quenching was around 1140∘C. The pit depths were found to be in the range of 100nm and width of 1.5-2μm.

Microstructural Characteristics and Oxidation Behavior of Low-Pressure Cold-Sprayed CoNiCrAlY Coatings

NASA Astrophysics Data System (ADS)

Zhang, Lin-wei; Lu, Lei; Wang, Lu; Ning, Xian-jin; Wang, Quan-sheng; Wang, Ri-xin

2017-10-01

CoNiCrAlY coatings were deposited by low-pressure cold spraying and subsequently heat-treated at 1050 °C for 4 h in a vacuum environment. The microstructural characteristics and oxidation behavior of CoNiCrAlY coatings were investigated. The as-sprayed coating exhibited low porosity and oxygen content. The high plastic deformation of the sprayed particles led to significant refinement of γ-matrix and dissolution of β-(Ni,Co)Al phase in the as-sprayed coating. After heat treatment, the single phase (γ) in the as-sprayed coating was converted into a γ/β microstructure, and a continuous single α-Al2O3 scale was formed on the coating surface. Vacuum heat treatment can postpone the formation of spinel oxides within 100 h. After being oxidized at 1050 °C for 400 h, the heat-treated coating exhibited better oxidation resistance than the as-sprayed coating. The reduced growth rate of the oxide scale and the suppression of the formation of spinel oxides can be attributed to the vacuum heat treatment, as well as the intrinsic microstructure of the cold-sprayed coating. Finally, the effects of the microstructural changes induced during the cold spraying process on the growth of the thermally grown oxide and the oxidation mechanisms of the CoNiCrAlY coatings were discussed.

Migration Study of Butylated Hydroxytoluene and Irganox 1010 from Polypropylene Treated with Severe Processing Conditions.

PubMed

Kang, Kyungmo; Chang, Yoonjee; Choi, Jae Chun; Park, Se-Jong; Han, Jaejoon

2018-04-01

Safety concerns have emerged over the increased use of polypropylene (PP) in food-packaging markets. Some antioxidants in PP can migrate to foods and cause undesirable effects in humans. In this study, migration behaviors of butylated hydroxytoluene (BHT) and Irganox 1010 (I-1010) in PP sheets were determined according to the US FDA migration test conditions. In particular, we tested the effects of severe conditions of food processing and storage, such as autoclave heating (sterilization at about 121 °C), microwave radiation (700 W), and deep freezing (-30 °C) on migration of antioxidants. Migrant concentrations were higher in 95% ethanol as lipid food simulant, because of the hydrophobic nature of both PP and antioxidants. Autoclave heating treatment increased migrant concentrations compared with other processing conditions. Moreover, increased migrant concentrations by deep freezing condition were attributed to the brittleness of PP at freezing temperature. Regardless of processing conditions, BHT which has a lower molecular weight, migrated faster than I-1010. The antioxidants with hydrophobic nature such as butylated hydroxytoluene (BHT) and Irganox 1010 (I-1010) in polypropylene sheets would be migrated to foods, which is an important issue for industrial production food packaging materials. Migration behavior was promoted by severe processing conditions such as autoclave heating, microwave radiation, freezing, and especially autoclave heating treatment led the highest migration among them. Therefore, control of chemical additive migration from polypropylene food packaging is needed for safe food processing. © 2018 Institute of Food Technologists®.

A-15 Superconducting composite wires and a method for making

DOEpatents

Suenaga, Masaki; Klamut, Carl J.; Luhman, Thomas S.

1984-01-01

A method for fabricating superconducting wires wherein a billet of copper containing filaments of niobium or vanadium is rolled to form a strip which is wrapped about a tin-alloy core to form a composite. The alloy is a tin-copper alloy for niobium filaments and a gallium-copper alloy for vanadium filaments. The composite is then drawn down to a desired wire size and heat treated. During the heat treatment process, the tin in the bronze reacts with the niobium to form the superconductor niobium tin. In the case where vanadium is used, the gallium in the gallium bronze reacts with the vanadium to form the superconductor vanadium gallium. This new process eliminates the costly annealing steps, external tin plating and drilling of bronze ingots required in a number of prior art processes.

Heat Treatment of Iron-Carbon Alloys in a Magnetic Field (Phase 2)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ludtka, Gerard Michael

Thermomagnetic processing was shown to shift the phase transformation temperatures and therefore microstructural evolution in the high performance engine valve spring 9254 steel alloy by applying a high magnetic field during cooling. These effects would be anticipated to improve performance such as high cycle fatigue as demonstrated in prior projects. Thermomagnetic processing of gears and crank shafts was constrained by the size of the prototype equipment currently available at ORNL. However, the commercial procurement viability of production scale 9-Tesla, 16-inch diameter bore thermomagnetic processing equipment for truck idler gears up to ~11-inch diameter and potential crank shaft applications was shown,more » as multiple superconducting magnet manufacturing companies (in conjunction with an induction heat treating company, AjaxTOCCO Magnethermic) offered cryogen-free or cryocooler equipment designs to Cummins.« less

Effect of the application of surface treatments before and after sintering on the flexural strength, phase transformation and surface topography of zirconia.

PubMed

Kurtulmus-Yilmaz, Sevcan; Aktore, Huseyin

2018-05-01

To evaluate the effects of airborne-particle abrasion (APA) and Er,Cr:YSGG laser irradiation on 4-point-flexural strength, phase transformation and morphologic changes of zirconia ceramics treated at pre-sintered or post-sintered stage. Three hundred and forty-two bar shaped zirconia specimens were milled with different sizes according to the flexural strength test (n = 10), X-ray diffraction (XRD) (n = 4) and field emission scanning electron microscope (FE-SEM) (n = 4) analyses. For each test protocol, specimens were divided into 4 main groups whether the surface treatments applied before or after sintering and whether the specimens received heat treatment or not as pre-sintered, post-sintered no-heat and post-sintered heat-treated groups, and a group was served as control. Main groups were further divided into 6 equal subgroups according to surface treatment method applied (2 W-, 3 W-, 4 W-, 5 W-, 6 W-laser irradiations and APA). Surface treatments were applied to pre-sintered groups before sintering and to post-sintered groups after sintering. Post-sintered heat-treated groups were subjected to veneer ceramic firing simulation after surface treatments. Flexural strength and flexural modulus values were statistically analysed and monoclinic phase content was calculated. Weibull analysis was used to evaluate strength reliability and fractographic analysis was conducted. Highest flexural strength values were detected at post-sintered no-heat APA and 4W-laser groups (P < 0.05). Pre-sintered groups showed statistically lower flexural strength values. Heat treatment decreased the strength of the specimens. Monoclinic phase content was only detected at post-sintered no-heat groups and the highest amount was detected at APA group. Rougher surfaces and deeper irregularities were detected at FE-SEM images pre-sintered groups. Application of surface treatments at pre-sintered stage may be detrimental for zirconia ceramics in terms of flexural strength. Treating the surface of zirconia ceramic before sintering process is not recommended due to significant decrease in flexural strength values. 2 W-4 W Er,Cr:YSGG laser irradiations can be regarded as alternative surface treatment methods when zirconia restoration would be subjected to veneer ceramic firing procedures. Copyright © 2018 Elsevier Ltd. All rights reserved.

Reduction of metal oxides through mechanochemical processing

DOEpatents

Froes, Francis H.; Eranezhuth, Baburaj G.; Senkov, Oleg N.

2000-01-01

The low temperature reduction of a metal oxide using mechanochemical processing techniques. The reduction reactions are induced mechanically by milling the reactants. In one embodiment of the invention, titanium oxide TiO.sub.2 is milled with CaH.sub.2 to produce TiH.sub.2. Low temperature heat treating, in the range of 400.degree. C. to 700.degree. C., can be used to remove the hydrogen in the titanium hydride.

Processes for treating cellulosic material

NASA Technical Reports Server (NTRS)

Kohlman, Karen L. (Inventor); Weil, Joseph R. (Inventor); Westgate, Paul L. (Inventor); Ladisch, Michael R. (Inventor); Yang, Yiqi (Inventor)

1998-01-01

Disclosed are processes for pretreating cellulosic materials in liquid water by heating the materials in liquid water at a temperature at or above their glass transition temperature but not substantially exceeding 220.degree. C., while maintaining the pH of the reaction medium in a range that avoids substantial autohydrolysis of the cellulosic materials. Such pretreatments minimize chemical changes to the cellulose while leading to physical changes which substantially increase susceptibility to hydrolysis in the presence of cellulase.

Fluidized bed selective pyrolysis of coal

DOEpatents

Shang, J.Y.; Cha, C.Y.; Merriam, N.W.

1992-12-15

The present invention discloses a process for the pyrolysis of coal which comprises the effective utilization of two zonal inclined fluidized beds, where said zones can be selectively controlled as to temperature and heating rate. The first zonal inclined fluidized bed serves as a dryer for crushed coal and additionally is controlled to selectively pyrolyze said coal producing substantially carbon dioxide for recycle use. The second zonal inclined fluidized bed further pyrolyses the coal to gaseous, liquid and char products under controlled temperature and heating rate zones designed to economically integrate the product mix. The gas and liquid products are recovered from the gaseous effluent stream while the char which remains can be further treated or utilized in a subsequent process step. 9 figs.

Fluidized bed selective pyrolysis of coal

DOEpatents

Shang, Jer Y.; Cha, Chang Y.; Merriam, Norman W.

1992-01-01

The present invention discloses a process for the pyrolysis of coal which comprises the effective utilization of two zonal inclined fluidized beds, where said zones can be selectively controlled as to temperature and heating rate. The first zonal inclined fluidized bed serves as a dryer for crushed coal and additionally is controlled to selectively pyrolyze said coal producing substantially carbon dioxide for recycle use. The second zonal inclined fluidized bed further pyrolyzes the coal to gaseous, liquid and char products under controlled temperature and heating rate zones designed to economically integrate the product mix. The gas and liquid products are recovered from the gaseous effluent stream while the char which remains can be further treated or utilized in a subsequent process step.

Data related to cyclic deformation and fatigue behavior of direct laser deposited Ti-6Al-4V with and without heat treatment.

PubMed

Sterling, Amanda J; Torries, Brian; Shamsaei, Nima; Thompson, Scott M

2016-03-01

Data is presented describing the strain-controlled, fully-reversed uniaxial cyclic deformation and fatigue behavior of Ti-6Al-4V specimens additively manufactured via Laser Engineered Net Shaping (LENS) - a Direct Laser Deposition (DLD) process. The data was collected by performing multiple fatigue tests on specimens with various microstructural states/conditions, i.e. in their 'as-built', annealed (below the beta transus temperature), or heat treated (above the beta transus temperature) condition. Such data aids in characterizing the mechanical integrity and fatigue resistance of DLD parts. Data presented herein also allows for elucidating the strong microstructure coupling of the fatigue behavior of DLD Ti-6Al-4V, as the data trends were found to vary with material condition (i.e. as-built, annealed or heat treated) [1]. This data is of interest to the additive manufacturing and fatigue scientific communities, as well as the aerospace and biomedical industries, since additively-manufactured parts cannot be reliably deployed for public use, until their mechanical properties are understood with high certainty.

Data related to cyclic deformation and fatigue behavior of direct laser deposited Ti–6Al–4V with and without heat treatment

PubMed Central

Sterling, Amanda J.; Torries, Brian; Shamsaei, Nima; Thompson, Scott M.

2016-01-01

Data is presented describing the strain-controlled, fully-reversed uniaxial cyclic deformation and fatigue behavior of Ti–6Al–4V specimens additively manufactured via Laser Engineered Net Shaping (LENS) – a Direct Laser Deposition (DLD) process. The data was collected by performing multiple fatigue tests on specimens with various microstructural states/conditions, i.e. in their ‘as-built’, annealed (below the beta transus temperature), or heat treated (above the beta transus temperature) condition. Such data aids in characterizing the mechanical integrity and fatigue resistance of DLD parts. Data presented herein also allows for elucidating the strong microstructure coupling of the fatigue behavior of DLD Ti–6Al–4V, as the data trends were found to vary with material condition (i.e. as-built, annealed or heat treated) [1]. This data is of interest to the additive manufacturing and fatigue scientific communities, as well as the aerospace and biomedical industries, since additively-manufactured parts cannot be reliably deployed for public use, until their mechanical properties are understood with high certainty. PMID:26949728

Effects of Heat-Treated Wood Particles on the Physico-Mechanical Properties and Extended Creep Behavior of Wood/Recycled-HDPE Composites Using the Time-Temperature Superposition Principle.

PubMed

Yang, Teng-Chun; Chien, Yi-Chi; Wu, Tung-Lin; Hung, Ke-Chang; Wu, Jyh-Horng

2017-03-30

This study investigated the effectiveness of heat-treated wood particles for improving the physico-mechanical properties and creep performance of wood/recycled-HDPE composites. The results reveal that the composites with heat-treated wood particles had significantly decreased moisture content, water absorption, and thickness swelling, while no improvements of the flexural properties or the wood screw holding strength were observed, except for the internal bond strength. Additionally, creep tests were conducted at a series of elevated temperatures using the time-temperature superposition principle (TTSP), and the TTSP-predicted creep compliance curves fit well with the experimental data. The creep resistance values of composites with heat-treated wood particles were greater than those having untreated wood particles due to the hydrophobic character of the treated wood particles and improved interfacial compatibility between the wood particles and polymer matrix. At a reference temperature of 20 °C, the improvement of creep resistance ( ICR ) of composites with heat-treated wood particles reached approximately 30% over a 30-year period, and it increased significantly with increasing reference temperature.

Effects of Heat-Treated Wood Particles on the Physico-Mechanical Properties and Extended Creep Behavior of Wood/Recycled-HDPE Composites Using the Time–Temperature Superposition Principle

PubMed Central

Yang, Teng-Chun; Chien, Yi-Chi; Wu, Tung-Lin; Hung, Ke-Chang; Wu, Jyh-Horng

2017-01-01

This study investigated the effectiveness of heat-treated wood particles for improving the physico-mechanical properties and creep performance of wood/recycled-HDPE composites. The results reveal that the composites with heat-treated wood particles had significantly decreased moisture content, water absorption, and thickness swelling, while no improvements of the flexural properties or the wood screw holding strength were observed, except for the internal bond strength. Additionally, creep tests were conducted at a series of elevated temperatures using the time–temperature superposition principle (TTSP), and the TTSP-predicted creep compliance curves fit well with the experimental data. The creep resistance values of composites with heat-treated wood particles were greater than those having untreated wood particles due to the hydrophobic character of the treated wood particles and improved interfacial compatibility between the wood particles and polymer matrix. At a reference temperature of 20 °C, the improvement of creep resistance (ICR) of composites with heat-treated wood particles reached approximately 30% over a 30-year period, and it increased significantly with increasing reference temperature. PMID:28772726

Ion release and cytotoxicity of stainless steel wires.

PubMed

Oh, Keun-Taek; Kim, Kyoung-Nam

2005-12-01

Heat treatment is generally applied to orthodontic stainless steel (SS) wires to relieve the stresses that result from their manipulation by orthodontists. The quality and thickness of the oxide films formed on the surface of heat-treated wires can vary, and it is believed that these oxide films can influence the properties of heat-treated wires. The aim of this study was to investigate the influence of heat treatment and cooling methods on the amount of metal ions released and to examine the cytotoxicity of heat-treated wires. In this study, four types of SS wires (Remanium, Permachrome, Colboloy and Orthos) with a cross-sectional area of 0.41 x 0.56 mm were investigated. These wires were heat-treated in a vacuum, air, or argon environment, and were cooled in either a furnace or a water bath. Four control groups and 24 experimental groups were classified according to the type of wires, heat treatment conditions and cooling methods. In each group, the amount of nickel released as well as its cytotoxicity was investigated. The concentration of dissolved nickel ions in artificial saliva was measured for a period of up to 12 weeks. In all groups, the concentration of dissolved nickel ions in artificial saliva was lowest for the vacuum heat treatment-furnace cooling group and a significant difference was shown compared with the other experimental groups. The concentration of dissolved nickel ions in artificial saliva was highest in the groups heat-treated in air (P < 0.05), while the amount of nickel released was highest in the Remanium and Colboloy (P < 0.05). The cytotoxicity was mild in all the experimental groups but the response index of the air groups was slightly higher than in the other groups. According to these results, SS wires retain their high corrosion resistance and low ion release rate when heat-treated in a vacuum and cooled in a furnace.

Polymer composites prepared from heat-treated starch and styrene-butadiene latex

USDA-ARS?s Scientific Manuscript database

Thermoplastic starch/latex polymer composites were prepared using styrene–butadiene (SB) latex and heat-treated cornstarch. The composites were prepared in a compression mold at 130 °C, with starch content 20%. An amylose-free cornstarch, waxy maize, was used for this research and the heat treatment...

Coupled heating/acidification pretreatment of chemical sludge for dewatering by using waste sulfuric acid at low temperature.

PubMed

Bian, Bo; Zhang, Limin; Zhang, Qin; Zhang, Shaopeng; Yang, Zhen; Yang, Weiben

2018-08-01

A cost-effective approach for pretreatment of chemical sludge for further dewatering, based on the idea of "using waste to treat waste", is provided. It is a coupled heating/acidification pretreatment method, where waste sulfuric acid is employed and relatively low temperatures (<100 °C) are applied. Effects of reaction time, temperature, and dosage of waste acid on dewatering performance (both dewatering speed and degree) are studied. Under the optimal conditions (reaction time: 30 min; temperature: 90 °C; waste acid dosage: 0.175 g/(g dried sludge)), the method of this work demonstrates three advantages compared to the conventional method using lime+polyacrylamide: lower moisture content of treated sludge; higher calorific value for incineration process; and lower cost. Detailed mechanism of the pretreatment for dewatering is investigated via characterizations and statistical analyses of various parameters, among which zeta potential, particle size, protein and polysaccharide contents, soluble chemical oxygen demand (SCOD), reduction of combined water and volatile suspended solid (VSS), are associated with dewatering performance. Both heating and acidification generate disintegration of cells in sludge, giving rise to two phenomena: more organic matters are released into solution and more bound water turns into free water. Meantime, the released organic polymers flocculate sludge particles, further accelerating the solid-liquid separation process. Copyright © 2018 Elsevier Ltd. All rights reserved.

Growth of Listeria spp. in shredded cabbage is enhanced by a mild heat treatment.

PubMed

Ells, Timothy C; Truelstrup Hansen, Lisbeth

2010-03-01

Mild thermal processing can enhance the shelf life of cut fruits and vegetables by delaying the onset of spoilage and preserving the organoleptic properties of shredded cabbage. However, food safety issues related to this process have not been fully investigated. Therefore, the survival and growth of Listeria spp. on cabbage treated in this manner was examined. Experimentally, 24 strains of Listeria spp. (including L. monocytogenes) were inoculated onto cut and intact cabbage tissues and stored at 5 degrees C. All strains on intact tissues exhibited a moderate decline in numbers (up to 1.0 log CFU/cm(2)) over the 28-day storage period. Conversely, cut tissue supported growth of most strains during the first 7 to 14 days of incubation with maximum increases of 1.2 log CFU/cm(2). Subsequently, the survival or growth on heat-treated (50 degrees C for 3 min) and untreated shredded cabbage of four L. monocytogenes and four nonpathogenic Listeria spp. strains were compared during storage for 21 days at 5 degrees C. Growth on untreated shred for all strains was similar to the results observed on cut tissue with a maximum increase of approximately 1.0 log CFU/g. However, in the heat-treated cabbage shred all strains displayed a rapid increase in growth (up to 2.5 log CFU/g) during the first 7 days of incubation, which may be indicative of the destruction of an endogenous growth-inhibiting compound within the cabbage. In conclusion, this study shows that mild thermal treatments of cut cabbage may promote pathogen growth if other inimical barriers are not implemented downstream of the thermal treatment.

Quality assurance: recommended guidelines for safe heating by capacitive-type heating technique to treat patients with metallic implants.

PubMed

Kato, Hirokazu; Kondo, Motoharu; Imada, Hajime; Kuroda, Masahiro; Kamimura, Yoshitsugu; Saito, Kazuyuki; Kuroda, Kagayaki; Ito, Koichi; Takahashi, Hideaki; Matsuki, Hidetoshi

2013-05-01

This article is a redissemination of the previous Japanese Quality Assurance Guide guidelines. Specific absorption rate and temperature distribution were investigated with respect to various aspects including metallic implant size and shape, insertion site, insertion direction, blood flow and heating power, and simulated results were compared with adverse reactions of patients treated by radio frequency capacitive-type heating. Recommended guidelines for safe heating methods for patients with metallic implants are presented based on our findings.

Thermographic Assessment of the HAZ Properties and Structure of Thermomechanically Treated Steel

NASA Astrophysics Data System (ADS)

Górka, Jacek; Janicki, Damian; Fidali, Marek; Jamrozik, Wojciech

2017-12-01

Thermomechanically processed steels are materials of great mechanical properties connected with more than good weldability. This mixture makes them interesting for different types of industrial applications. When creating welded joints, a specified amount of heat is introduced into the welding area and a so called heat-affected zone (HAZ) is formed. The key issue is to reduce the width of the HAZ, because properties of the material in the HAZ are worse than in the base material. In the paper, thermographic measurements of HAZ temperatures were presented as a potential tool for quality assuring the welding process in terms of monitoring and control. The main issue solved was the precise temperature measurement in terms of varying emissivity during a welding thermal cycle. A model of emissivity changes was elaborated and successfully applied. Additionally, material in the HAZ was tested to reveal its properties and connect changes of those properties with heating parameters. The obtained results prove that correctly modeled emissivity allows measurement of temperature, which is a valuable tool for welding process monitoring.

Modeling the heat transfer problem for the novel combined cryosurgery and hyperthermia system.

PubMed

Zhao, Gang; Bai, Xue-Fei; Luo, Da-Wei; Gao, Da-Yong

2006-01-01

A multidimensional, finite element analysis (FEA) for the freezing, holding, rewarming and heating processes of biological tissues during the cryosurgery process of the new Combined Cryosurgery/Hyperthermia System is presented to theoretically test its validity. The tissues are treated as nonideal materials freezing over a temperature range, and the thermophysical properties of which are temperature dependent. The enthalpy method is applied to solve the highly nonlinear problem. It was found that when the same boundary condition and the same target tissue presented, the novel Cryosurgery/Hyperthermia System could supply the target tissue an approximative cooling rate, a much lower minimal temperature, a much greater warming rate, and a much greater thermal gradients compared with that of the simplified Endocare system. The numerical simulation indicates that the novel combined cryosurgery and hyperthermia system can provide an excellent curative effect in the corresponding cryotherapy. And the most attractive feature of this FEA framework is that it can be easily mastered by the surgeon without in-depth theory of heat transfer to analyze the cryosurgery process beforehand due to the friendly GUI (graphical user interface) of Ansys software.

Effect of Different Heat Treatments on In Vitro Digestion of Egg White Proteins and Identification of Bioactive Peptides in Digested Products.

PubMed

Wang, Xuefen; Qiu, Ning; Liu, Yaping

2018-04-01

Chicken eggs are ingested by people after a series of processes, but to date, only a few studies have explored the nutrient variations caused by different heat treatments. In this work, the impacts of different heat treatments (4, 56, 65, and 100 °C on the in vitro digestibility of egg white proteins were investigated by hydrolysis with pepsin or pepsin + pancreatin to simulate human gastrointestinal digestion, and the digested products were identified using Nano-LC-ESI-MS/MS. Egg white proteins treated at 65 °C had the highest in vitro pepsin digestibility value whereas the pepsin + pancreatin digestibility increased significantly (P < 0.05) as the cooking temperature was raised. The molecular weight distribution of the digested products indicated that, when compared to pepsin-treated samples, pepsin + pancreatin-treated samples contained more low-molecular-weight peptides (m/z < 849.2) with higher signal intensities. The number of unique peptides identified in every digestion product showed a positive correlation with their in vitro digestibility. Additionally, bioactive peptides such as antioxidant, antimicrobial and antihypertensive peptides were found present in egg white digested products, especially in samples treated at 4 and 100 °C. These findings may facilitate a better understanding of nutritive values of egg white proteins and their digested products under different cooking temperatures, such as antibacterial and antioxidant peptides identified in the digestion samples treated, respectively at 4 and 100 °C. This study also provided information for improving the applications of eggs in the food industry as well as a theoretical basis for egg consumption. © 2018 Institute of Food Technologists®.

FISSION PRODUCT REMOVAL FROM ORGANIC SOLUTIONS

DOEpatents

Moore, R.H.

1960-05-10

The decontamination of organic solvents from fission products and in particular the treatment of solvents that were used for the extraction of uranium and/or plutonium from aqueous acid solutions of neutron-irradiated uranium are treated. The process broadly comprises heating manganese carbonate in air to a temperature of between 300 and 500 deg C whereby manganese dioxide is formed; mixing the manganese dioxide with the fission product-containing organic solvent to be treated whereby the fission products are precipitated on the manganese dioxide; and separating the fission product-containing manganese dioxide from the solvent.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tadayyon, Ghazal; Mazinani, Mohammad; Guo, Yina

Martensitic evolution in Ti-rich NiTi alloy, Ti50.5Ni49.5, has been investigated as a function of annealing, solution treatment and a combination thereof and a detailed electron microscopic investigation carried out. Self-accommodated martensite plates resulted in all heat treated samples. Martensitic < 011 > type II twins, which are common in NiTi shape memory alloys, was found in both as-received and heat-treated samples. Solution treated samples, additionally, showed {11-1} type I twinning was also found in samples that have been annealed after solution-treatment. Another common feature of the microstructure in both as-received and heat treated samples is the formation of Ti{sub 2}Nimore » precipitates. The size, number and dispersions of these precipitates can be controlled by resorting to a suitable heat treatment e.g. solution treatment.« less

Cloning and expression analysis of a small HSP26 gene of Pacific abalone (Haliotis discus hannai).

PubMed

Park, Eun Mi; Kim, Young Ok; Nam, Bo Hye; Kong, Hee Jeong; Kim, Woo Jin; Lee, Sang Jun; Jee, Young Ju; Kong, In Soo; Choi, Tae Jin

2008-07-01

Heat shock proteins (HSPs) are evolutionally conserved from micro organism to mammals and play important roles in many biological processes including thermal tolerance. We isolated a homologue of small HSP26 (sHSP26) from a subtracted cDNA library of heat shock-treated abalone (Haliotis discus hannai). The abalone sHSP26 encompossed 793 nt, including a coding region of 501 nt. The deduced amino acid sequence of the abalone sHSP26 contained well conserved alpha-crystallin domain and showed overall identities of 27-31% with the other species' sHSP proteins. The abalone sHSP26 transcript was induced by heat shock treatment, but not by cold shock treatment.

Effect of thermal processing on estimated metabolizable protein supply to dairy cattle from camelina seeds: relationship with protein molecular structural changes.

PubMed

Peng, Quanhui; Khan, Nazir A; Wang, Zhisheng; Zhang, Xuewei; Yu, Peiqiang

2014-08-20

This study evaluated the effect of thermal processing on the estimated metabolizable protein (MP) supply to dairy cattle from camelina seeds (Camelina sativa L. Crantz) and determined the relationship between heat-induced changes in protein molecular structural characteristics and the MP supply. Seeds from two camelina varieties were sampled in two consecutive years and were either kept raw or were heated in an autoclave (moist heating) or in an air-draft oven (dry heating) at 120 °C for 1 h. The MP supply to dairy cattle was modeled by three commonly used protein evaluation systems. The protein molecular structures were analyzed by Fourier transform/infrared-attenuated total reflectance molecular spectroscopy. The results showed that both the dry and moist heating increased the contents of truly absorbable rumen-undegraded protein (ARUP) and total MP and decreased the degraded protein balance (DPB). However, the moist-heated camelina seeds had a significantly higher (P < 0.05) content of ARUP and total MP and a significantly lower (P < 0.05) content of DPB than did the dry-heated camelina seeds. The regression equations showed that intensities of the protein molecular structural bands can be used to estimate the contents of ARUP, MP, and DPB with high accuracy (R(2) > 0.70). These results show that protein molecular structural characteristics can be used to rapidly assess the MP supply to dairy cattle from raw and heat-treated camelina seeds.

Enhancement of durability properties of heat-treated oil palm shell species lightweight concrete

NASA Astrophysics Data System (ADS)

Yew, Ming Kun; Yew, Ming Chian; Saw, Lip Huat; Ang, Bee Chin; Lee, Min Lee; Lim, Siong Kang; Lim, Jee Hock

2017-04-01

Oil palm shell (OPS) are non-hazardous waste materials and can be used as alternative coarse aggregates to substitute depleting conventional raw materials. A study on preparing the OPS species (dura and tenera) lightweight concrete (LWC) using with and without heat-treated OPS aggregate has been investigated. Two different species of OPS coarse aggregate are subjected to heat treatment at 65 and 130 °C with duration of 1 hour. The results reveal that the slump value of the OPSC increases significantly with an increase in temperature of heat treatment of the tenera OPS aggregates. It is found that the maximum achievable 28-days and 180-days compressive strength is 45.6 and 47.5 MPa, respectively. Furthermore, rapid chloride penetration test (RCPT) and water absorption tests were performance to signify the effects of heat-treated on OPS species LWC. The use of heat-treated OPS LWC induced the advantageous of reducing the permeability and capillary porosity as well as water absorption. Hence, the findings of this study are of primary importance as they revealed the heat treatment on OPS species LWC can be used as a new environmentally friendly method to enhance the durability of OPSLWC.

Ultra-high-pressure homogenization (UHPH) system for producing high-quality vegetable-based beverages: physicochemical, microbiological, nutritional and toxicological characteristics.

PubMed

Ferragut, Victoria; Hernández-Herrero, Manuela; Veciana-Nogués, María Teresa; Borras-Suarez, Miquel; González-Linares, Javier; Vidal-Carou, María Carmen; Guamis, Buenaventura

2015-03-30

A relatively new technology based on a continuous system of ultra-high-pressure homogenization (UHPH) was used for producing high-quality soy and almond beverages as an alternative to conventional heat treatments (pasteurization and UHT). The aim of this study was to compare those treatments by analyzing the most relevant quality parameters with a broad vision from the production to the potential toxicological changes, passing through the main nutritional characteristics. UHPH treatment at 200 MPa, 55 °C T(in) produced a higher reduction of microorganisms than pasteurization. UHPH treatment at 300 MPa, 75 °C T(in) led to complete inactivation of microorganisms, similar to UHT treatment. A much better colloidal stability was observed in both UHPH-treated almond and soy beverages compared with those processed by conventional heat treatments. UHPH treatments led to the same increase in digestibility as heat treatments and did not produce a reduction in the availability of lysine. In addition, UHPH samples of soy beverage seem to be less allergenic based on their lower gut immune response in comparison with heat-treated samples. UHPH treatments could be used to produce high-quality commercial vegetable beverages with different quality standards (fresh or long-life storage) according to consumer preference. © 2014 Society of Chemical Industry.

The Effect of Forging Variables on the Supersolvus Heat-Treatment Response of Powder-Metallurgy Nickel-Base Superalloys

NASA Astrophysics Data System (ADS)

Semiatin, S. L.; Shank, J. M.; Shiveley, A. R.; Saurber, W. M.; Gaussa, E. F.; Pilchak, A. L.

2014-12-01

The effect of subsolvus forging temperature and strain rate on the grain size developed during final supersolvus heat treatment (SSHT) of two powder-metallurgy, gamma-gamma prime superalloys, IN-100 and LSHR, was established. For this purpose, isothermal, hot compression tests were performed at temperatures ranging from 1144 K (871 °C) and 22 K (22 °C) below the respective gamma-prime solvus temperatures ( T γ') and strain rates between 0.0003 and 10 s-1. Deformed samples were then heat treated 20 K (20 °C) above the solvus for 1 h with selected additional samples exposed for shorter and longer times. For both alloys, the grain size developed during SSHT was in the range of 15 to 30 μm, except for those processing conditions consisting of pre-deformation at the highest temperature, i.e., T γ'—22 K ( T γ'—22 °C), and strain rates in the range of ~0.001 to 0.1 s-1. In these latter instances, the heat-treated grain size was approx. four times as large. The observations were interpreted in terms of the mechanisms of deformation during hot working and their effect on the driving forces for grain-boundary migration which controls the evolution of the gamma-grain size.

A study on alkaline heat treated Mg-Ca alloy for the control of the biocorrosion rate.

PubMed

Gu, X N; Zheng, W; Cheng, Y; Zheng, Y F

2009-09-01

To reduce the biocorrosion rate by surface modification, Mg-Ca alloy (1.4wt.% Ca content) was soaked in three alkaline solutions (Na(2)HPO(4), Na(2)CO(3) and NaHCO(3)) for 24h, respectively, and subsequently heat treated at 773K for 12h. Scanning electron microscopy and energy-dispersive spectroscopy results revealed that magnesium oxide layers with the thickness of about 13, 9 and 26microm were formed on the surfaces of Mg-Ca alloy after the above different alkaline heat treatments. Atomic force microscopy showed that the surfaces of Mg-Ca alloy samples became rough after three alkaline heat treatments. The in vitro corrosion tests in simulated body fluid indicated that the corrosion rates of Mg-Ca alloy were effectively decreased after alkaline heat treatments, with the following sequence: NaHCO(3) heated

Macroporous ceramics by colloidal templating

NASA Astrophysics Data System (ADS)

Subramaniam, G.; Pine, David J.

2000-04-01

We describe a novel method of fabricating macroporous ceramics employing colloidal dispersion of ultrafine ceramic particles with latex particles as the templates. The colloidal particles form a particulate gel on drying and fill the voids of the ordered latex templates. Subsequent removal of the template by calcination results in the formation of an ordered macroporous ceramic. The process has significant advantages over the traditional sol-gel process employing alkoxide precursors. Most importantly, the much lower shrinkage compared to the sol-gel process enabled us to produce larger pieces of the sample. The larger shrinkage involved in the sol-gel process often results in small and fragile pieces of the macroporous material which has to be subsequently heat treated to induce crystallization. The ability to choose crystalline colloidal particles in our method obviates the need for heat treatment to achieve crystallinity. We have synthesized a variety of materials such as macroporous silica, titania, alumina and recently have also extended the approach to macroporous silicon which is not amenable to the sol-gel process.

Cost studies of thermally enhanced in situ soil remediation technologies

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bremser, J.; Booth, S.R.

1996-05-01

This report describes five thermally enhanced technologies that may be used to remediate contaminated soil and water resources. The standard methods of treating these contaminated areas are Soil Vapor Extraction (SVE), Excavate & Treat (E&T), and Pump & Treat (P&T). Depending on the conditions at a given site, one or more of these conventional alternatives may be employed; however, several new thermally enhanced technologies for soil decontamination are emerging. These technologies are still in demonstration programs which generally are showing great success at achieving the expected remediation results. The cost savings reported in this work assume that the technologies willmore » ultimately perform as anticipated by their developers in a normal environmental restoration work environment. The five technologies analyzed in this report are Low Frequency Heating (LF or Ohmic, both 3 and 6 phase AC), Dynamic Underground Stripping (DUS), Radio Frequency Heating (RF), Radio Frequency Heating using Dipole Antennae (RFD), and Thermally Enhanced Vapor Extraction System (TEVES). In all of these technologies the introduction of heat to the formation raises vapor pressures accelerating contaminant evaporation rates and increases soil permeability raising diffusion rates of contaminants. The physical process enhancements resulting from temperature elevations permit a greater percentage of volatile organic compound (VOC) or semi- volatile organic compound (SVOC) contaminants to be driven out of the soils for treatment or capture in a much shorter time period. This report presents the results of cost-comparative studies between these new thermally enhanced technologies and the conventional technologies, as applied to five specific scenarios.« less

Pressure-assisted thermal sterilization of soup

NASA Astrophysics Data System (ADS)

Shibeshi, Kidane; Farid, Mohammed M.

2010-12-01

The overall efficiency of an existing scale-up pressure-assisted thermal sterilization (PATS) unit was investigated with regards to inactivation of Geobacillus stearothermophilus spores suspended in pumpkin soup. The PATS unit is a double pipe heat exchanger in which the soup is pumped into its inner high pressure tube and constrained by two high pressure valves, while steam is continuously passed through the annular region to heat the content. The technology is based on pressure generation by thermal expansion of the liquid in an enclosure. In this work, the addition of an air line to push the treated liquid food out of the existing PATS unit has improved the overall quality of the treated samples, as evidenced by achieving higher log reduction of the spores. Compared with thermal processing, the application of PATS shows the potential for lowering the thermal treatment temperature, offering improved food quality.

Investigation of Al Coated Mg for Biomedical Applications

NASA Astrophysics Data System (ADS)

Elmrabet, Nabila; Roe, Martin; Neate, Nigel; Grant, David M.; Brown, Paul D.

The corrosion resistant properties of 1-2 μm thick Al coatings deposited by radio frequency magnetron sputtering on polished Mg surfaces, within Ar and Ar/H2 environments, have been appraised. The coatings were heat-treated at 300°C for 5 h to induce the formation of bioinert Al2O3, and samples were corroded within phosphate buffered saline solution at 37°C to mimic the biological environment. Both the as-deposited and heat-treated coatings were found to delay the onset of corrosion, but showed higher initial corrosion rates, once established, as compared with polished Mg surfaces. Slightly improved performance of the coatings was achieved through the addition of H2 to the system which acted to inhibit Al-Mg alloying and MgO formation. However, localized accelerated corrosion associated with substrate polishing damage emphasized the need for improved process control and coating uniformity.

Metallurgy and Heat Treating. Welding Module 7. Instructor's Guide.

ERIC Educational Resources Information Center

Missouri Univ., Columbia. Instructional Materials Lab.

This guide is intended to assist vocational educators in teaching a three-unit module in metallurgy and heat treating. The module is part of a welding curriculum that has been designed to be totally integrated with Missouri's Vocational Instruction Management System. The basic principles of metallurgy and heat treatment and techniques for…

Effect of hydrogen peroxide on improving the heat stability of whey protein isolate solutions.

PubMed

Sutariya, Suresh; Patel, Hasmukh

2017-05-15

Whey protein isolate (WPI) solutions (12.8%w/w protein) were treated with varying concentrations of H 2 O 2 in the range of 0-0.144 H 2 O 2 to protein ratios (HTPR) by the addition of the required quantity of H 2 O 2 and deionized water. The samples were analyzed for heat stability, rheological properties, denaturation level of β-lactoglobulin (β-LG) and α-lactalbumin (α-LA). The samples treated with H 2 O 2 concentration >0.072 (HTPR) showed significant improvement in the heat stability, and decreased whey protein denaturation and aggregation. The WPI solution treated with H 2 O 2 (>0.072 HTPR) remained in the liquid state after heat treatment at 120°C, whereas the control samples formed gel upon heat treatment. Detailed analysis of these samples suggested that the improvement in the heat stability of H 2 O 2 treated WPI solution was attributed to the significant reduction in the sulfhydryl-disulfide interchange reaction during denaturation of β-LG and α-LA. Copyright © 2016 Elsevier Ltd. All rights reserved.

Effects of heat treatment on the mechanical properties of kenaf fiber

NASA Astrophysics Data System (ADS)

Carada, Paulo Teodoro D. L.; Fujii, Toru; Okubo, Kazuya

2016-05-01

Natural fibers are utilized in various ways. One specific application of it, is in the field natural fiber composite (NFC). Considerable amount of researches are conducted in this field due to rising concerns in the harmful effects of synthetic materials to the environment. Additionally, these researches are done in order to overcome the drawbacks which limit the wide use of natural fiber. A way to improve NFC is to look into the reinforcing component (natural fiber). Treatments, which are classified as mechanical or chemical in nature, can be done in order to improve the performance of the natural fiber. The aim of this study is to assess the effects of heat treatment in the mechanical properties of kenaf fiber. In addition, the response of mechanical properties after exposure to high moisture environment of heat-treated kenaf fibers was observed. Heat treatment was done for one hour with the following heating temperatures: 140, 160, 180, and 200 °C. X-ray diffraction analysis was done to calculate the crystallinity index of kenaf fibers after heat treatment. The results showed that increase in tensile strength can be attained when kenaf fibers are heat treated at 140 °C. However, the tensile modulus showed inconsistency with respect to heat treatment temperature. The computed crystallinity index of the fiber matched the tensile strength observed in non-treated and heat-treated kenaf fibers. The results obtained in this study can be used for applications where heat treatment on kenaf fibers is needed.

Effects of heat treatment on the mechanical properties of kenaf fiber

DOE Office of Scientific and Technical Information (OSTI.GOV)

Carada, Paulo Teodoro D. L.; Fujii, Toru; Okubo, Kazuya

Natural fibers are utilized in various ways. One specific application of it, is in the field natural fiber composite (NFC). Considerable amount of researches are conducted in this field due to rising concerns in the harmful effects of synthetic materials to the environment. Additionally, these researches are done in order to overcome the drawbacks which limit the wide use of natural fiber. A way to improve NFC is to look into the reinforcing component (natural fiber). Treatments, which are classified as mechanical or chemical in nature, can be done in order to improve the performance of the natural fiber. Themore » aim of this study is to assess the effects of heat treatment in the mechanical properties of kenaf fiber. In addition, the response of mechanical properties after exposure to high moisture environment of heat-treated kenaf fibers was observed. Heat treatment was done for one hour with the following heating temperatures: 140, 160, 180, and 200 °C. X-ray diffraction analysis was done to calculate the crystallinity index of kenaf fibers after heat treatment. The results showed that increase in tensile strength can be attained when kenaf fibers are heat treated at 140 °C. However, the tensile modulus showed inconsistency with respect to heat treatment temperature. The computed crystallinity index of the fiber matched the tensile strength observed in non-treated and heat-treated kenaf fibers. The results obtained in this study can be used for applications where heat treatment on kenaf fibers is needed.« less

Vapor phase elemental sulfur amendment for sequestering mercury in contaminated soil

DOEpatents

Looney, Brian B.; Denham, Miles E.; Jackson, Dennis G.

2014-07-08

The process of treating elemental mercury within the soil is provided by introducing into the soil a heated vapor phase of elemental sulfur. As the vapor phase of elemental sulfur cools, sulfur is precipitated within the soil and then reacts with any elemental mercury thereby producing a reaction product that is less hazardous than elemental mercury.

Method and Apparatus to Access Optimum Strength During Processing of Precipitation Strengthened Alloys

NASA Technical Reports Server (NTRS)

Cantrell, John H. (Inventor); Yost, William T. (Inventor)

2001-01-01

A method and apparatus are provided which enable the nondestructive testing of strength of a heat treated alloy. An alloy is insonified with an ultrasonic signal. The resulting convoluted signal is detected and the acoustic nonlinearity parameter is determined. The acoustic nonlinearity parameter shows a peak corresponding to a peak in material strength.

40 CFR 63.2485 - What requirements must I meet for wastewater streams and liquid streams in open systems within an...

Code of Federal Regulations, 2010 CFR

2010-07-01

... Pollutants: Miscellaneous Organic Chemical Manufacturing Emission Limits, Work Practice Standards, and... be if the contents of the wastewater tank were not heated, treated by an exothermic reaction, or... uses the term “chemical manufacturing process unit,” the term “MCPU” applies for the purposes of this...

In situ heat treatment of a tar sands formation after drive process treatment

DOEpatents

Vinegar, Harold J.; Stanecki, John

2010-09-21

A method for treating a tar sands formation includes providing a drive fluid to a hydrocarbon containing layer of the tar sands formation to mobilize at least some hydrocarbons in the layer. At least some first hydrocarbons from the layer are produced. Heat is provided to the layer from one or more heaters located in the formation. At least some second hydrocarbons are produced from the layer of the formation. The second hydrocarbons include at least some hydrocarbons that are upgraded compared to the first hydrocarbons produced by using the drive fluid.

Influence of annealing on mechanical properties of TiNi (55.8 mass % of Ni) wire made for medical purposes

NASA Astrophysics Data System (ADS)

Kaplan, M. A.; Nasakina, E. O.; Sevostyanov, M. A.; Sergienko, K. V.; Baikin, A. S.; Konushkin, S. V.; Kolmakov, A. G.; Smirnov, M. A.; Izvin, A. V.; Ustinova, Yu N.

2018-04-01

Mechanical properties of titanium nickelide processed with various heat treatments are investigated. Fractographic, microstructural and X-ray diffraction analysis’ were carried out as well as strength and plasticity measurements. It is shown that titanium nickelide (55.8 mass % of Ni) wires treated by two annealing stages, which consist of heating up to 300°C on the first stage and 450°C on the second, with 4 hours and 15 minutes long exposures on each stage respectively, conducted in an air environment, possess the best strength while saving good elasticity figures.

Laser Additive Manufacturing of F/M Steels for Radiation Tolerant Nuclear Components

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lienert, Thomas J.; Maloy, Stuart Andrew

According to the Nuclear Energy R&D Roadmap Report submitted to Congress in 2010, one the key challenges facing the nuclear energy industry involves development of new reactor designs with reduced capital costs. Two related R&D objectives outlined in the report include: 1) Making improvements in the affordability of new reactors; and 2) Development of structural materials to withstand irradiation for longer periods. Laser additive manufacturing (LAM) is particularly well suited for more rapid and economical fabrication of reactor components relative to current fabrication methods. The proposed work involving LAM directly addresses the two R&D objectives outlined above relevant to themore » pertinent mission problems. The classical Materials Science approach involving development of Process/Structure/Property/Performance (P/S/P/P) relations was employed in this project. Processing included LAM and heat-treating. Thermal cycling during LAM is discussed here, and phase diagrams and continuous cooling transformation (CCT) diagrams are used to rationalize microstructural evolution. Structures were characterized including grain size & morphology, volume fraction, morphology, composition and location of carbides in as-deposited and heat-treated conditions. In the simplest sense, the goal was to control microstructures through process manipulation with a view toward optimizing properties and performance in service.« less

Rheological and sensory behaviors of parboiled pasta cooked using a microwave pasteurization process.

PubMed

Joyner, Helen S; Jones, Kari E; Rasco, Barbara A

2017-10-01

Pasta hydration and cooking requirements make in-package microwave pasteurization of pasta a processing challenge. The objective of this study was to assess instrumental and sensory attributes of microwave-treated pasta in comparison to conventionally cooked pasta. Fettuccine pasta was parboiled for 0, 3, 6, 9, or 12 min, pasteurized by microwaves at 915 MHz, then stored under refrigeration for 1 week. Pastas were evaluated by a trained sensory panel and with rheometry. Total pasta heat treatment affected both rheological and sensory behaviors; these differences were attributed to ultrastructure differences. Significant nonlinear behavior and dominant fluid-like behavior was observed in all pastas at strains >1%. Sensory results suggested microwave pasteurization may intensify the attributes associated with the aging of pasta such as retrogradation. A clear trend between magnitude of heat treatment and attribute intensity was not observed for all sensory attributes tested. The microwave pasta with the longest parboil time showed rheological behavior most similar to conventionally cooked pasta. Principal component analysis revealed that no microwave-treated pasta was similar to the control pasta. However, pasta parboiled for 9 min before microwave treatment had the greatest number of similar sensory attributes, followed by pasta parboiled for 6 or 12 min. Further study is needed to determine overall consumer acceptance of microwave-treated pasta and whether the differences in sensory and rheological behavior would impact consumer liking. The results of this study may be applied to optimize microwave pasteurization processes for cooked pasta and similar products, such as rice. The measurement and analysis procedures can be used to evaluate processing effects on a variety of different foods to determine overall palatability. © 2017 Wiley Periodicals, Inc.

Heat treated 9 Cr-1 Mo steel material for high temperature application

DOEpatents

Jablonski, Paul D.; Alman, David; Dogan, Omer; Holcomb, Gordon; Cowen, Christopher

2012-08-21

The invention relates to a composition and heat treatment for a high-temperature, titanium alloyed, 9 Cr-1 Mo steel exhibiting improved creep strength and oxidation resistance at service temperatures up to 650.degree. C. The novel combination of composition and heat treatment produces a heat treated material containing both large primary titanium carbides and small secondary titanium carbides. The primary titanium carbides contribute to creep strength while the secondary titanium carbides act to maintain a higher level of chromium in the finished steel for increased oxidation resistance, and strengthen the steel by impeding the movement of dislocations through the crystal structure. The heat treated material provides improved performance at comparable cost to commonly used high-temperature steels such as ASTM P91 and ASTM P92, and requires heat treatment consisting solely of austenization, rapid cooling, tempering, and final cooling, avoiding the need for any hot-working in the austenite temperature range.

Bioactive Titanate Layers Formed on Titanium and Its Alloys by Simple Chemical and Heat Treatments

PubMed Central

Kokubo, Tadashi; Yamaguchi, Seiji

2015-01-01

To reveal general principles for obtaining bone-bonding bioactive metallic titanium, Ti metal was heat-treated after exposure to a solution with different pH. The material formed an apatite layer at its surface in simulated body fluid when heat-treated after exposure to a strong acid or alkali solution, because it formed a positively charged titanium oxide and negatively charged sodium titanate film on its surface, respectively. Such treated these Ti metals tightly bonded to living bone. Porous Ti metal heat-treated after exposure to an acidic solution exhibited not only osteoconductive, but also osteoinductive behavior. Porous Ti metal exposed to an alkaline solution also exhibits osteoconductivity as well as osteoinductivity, if it was subsequently subjected to acid and heat treatments. These acid and heat treatments were not effective for most Ti-based alloys. However, even those alloys exhibited apatite formation when they were subjected to acid and heat treatment after a NaOH treatment, since the alloying elements were removed from the surface by the latter. The NaOH and heat treatments were also not effective for Ti-Zr-Nb-Ta alloys. These alloys displayed apatite formation when subjected to CaCl2 treatment after NaOH treatment, forming Ca-deficient calcium titanate at their surfaces after subsequent heat and hot water treatments. The bioactive Ti metal subjected to NaOH and heat treatments has been clinically used as an artificial hip joint material in Japan since 2007. A porous Ti metal subjected to NaOH, HCl and heat treatments has successfully undergone clinical trials as a spinal fusion device. PMID:25893014

Protective effect of heat-treated cucumber (Cucumis sativus L.) juice on alcohol detoxification in experimental rats.

PubMed

Bajpai, Vivek K; Kim, Na-Hyung; Kim, Ji-Eun; Kim, Kangmin; Kang, Sun Chul

2016-05-01

In this study, heat-treated cucumber juice was assessed for its protective effect on blood alcohol levels and hepatic alcohol metabolic enzyme system in experimental rats. Initially, during detoxification of alcohol, all groups were orally dosed to 22% alcohol (6ml/kg body weight) along with different concentrations of heat-treated cucumber juice (10, 100 and 500mg/kg) and commercial goods for hangover-removal on sale (2ml/kg). Cucumber juice was dosed before 30 min, and simultaneously after 30min of alcohol administration, and its hepatoprotective effect on blood alcohol levels and hepatic alcohol metabolic enzyme system in experimental rats was evaluated. As a result, after 7h, remarkable reduction was found in the blood alcohol levels for all concentrations of cucumber juice treatment. Treatment with cucumber juice resulted in increasing dehydrogenase (ADH) and acetaldehyde dehydrogenase (ALDH) enzymatic activities in rat liver at 9h after alcohol administration thereby stimulated blood alcohol metabolism as compared with control group. The effect of heat-treated cucumber juice on alcohol detoxification was observed only in the rats treated before 30min from alcohol administration. These findings indicate that heat-treated cucumber juice has significant protective effect on alcohol detoxification in experimental rats, suggesting its usefulness in the treatment of liver injury caused by alcohol consumption.

Relief of Residual Stress in Streamline Tie Rods by Heat Treatment

NASA Technical Reports Server (NTRS)

Pollard, R E; Reinhart, Fred M

1941-01-01

About two-thirds of the residual stress in cold-worked SAE 1050 steel tie rods was relieved by heating 30 minutes at 600 degrees Fahrenheit. Cold-worked austenitic stainless-steel tie rods could be heated at temperatures up to 1000 degrees Fahrenheit without lowering the important physical properties. The corrosion resistance, in laboratory corrosion test, of straight 18:8 and titanium-treated 18:8 materials appeared to be impaired after heating at temperatures above 800 degrees or 900 degrees fahrenheit. Columbium-treated and molybdenum-treated 18:8 steel exhibited improved stability over a wide range of temperatures. Tie rods of either material could be heated 30 minutes with safety at any temperature up to 1000 degrees Fahrenheit. At this temperature most of the residual stress would be relieved.

Method of removing sulfur emissions from a fluidized-bed combustion process

DOEpatents

Vogel, Gerhard John; Jonke, Albert A.; Snyder, Robert B.

1978-01-01

Alkali metal or alkaline earth metal oxides are impregnated within refractory support material such as alumina and introduced into a fluidized-bed process for the combustion of coal. Sulfur dioxide produced during combustion reacts with the metal oxide to form metal sulfates within the porous support material. The support material is removed from the process and the metal sulfate regenerated to metal oxide by chemical reduction. Suitable pore sizes are originally developed within the support material by heat-treating to accommodate both the sulfation and regeneration while still maintaining good particle strength.

Combining the pressure effect with local heat treatment for improving the sheet metal forming process

NASA Astrophysics Data System (ADS)

Palumbo, G.; Piccininni, A.; Guglielmi, P.; Sorgente, D.; Tricarico, L.

2016-08-01

The present work deals with the advantages in the Hydromechanical Deep Drawing (HDD) when AA5754 Tailored Heat Treated Blanks (THTBs) are adopted. It is well known that the creation of a suitable distribution of material properties increases the process performance. When non heat-treatable alloys are considered, the THTB approach can be successfully applied to increase the Limit Drawing Ratio (LDR) by changing the peripheral zone into the annealed state starting from a cold-worked blank. If this approach is combined with the advantages of a counterpressure, even more remarkable improvements can be achieved. Due to the large number of involved parameters, the optimized design of both the local treatment and the pressure profile were investigated coupling an axial symmetric Finite Element model with the integration platform modeFRONTIER. Results confirmed the possibility of increasing the LDR from 2.0 (Deep Drawing using a blank in the annealed state) up to about 3.0 if combining the adoption of a THTB with the optimal pressure profile.

Streamlining your demulsification program

DOE Office of Scientific and Technical Information (OSTI.GOV)

Svetgoff, J.

1989-09-01

According to this article, demulsification should be viewed as a wide reaching concept that takes into consideration many factors. These include: oil quality, water quality, effect of solids on the demulsification process, consideration of the completeness of the dehydration process, consideration of the most effective use of surface equipment, the use of heat, and cost of the demulsification program. The author discusses how the best demulsification program results in the synergistic use of heat, demulsifier chemicals, electricity, and retention time to provide clean oil and clean water with minimum treating system problems. In addition, these goals should be accomplished atmore » a reasonable cost. However, the amount of heat, chemicals, electricity, or retention time used in a program should not be reduced to the bare minimum. A slight excess of each is necessary to ensure a trouble-free program in most oil field systems. If a producer tries to operate on the ragged edge as far as system resources are concerned, upsets will occur because of the ever-changing nature of oil field systems.« less

Experimental investigation on selective laser melting of 17-4PH stainless steel

NASA Astrophysics Data System (ADS)

Hu, Zhiheng; Zhu, Haihong; Zhang, Hu; Zeng, Xiaoyan

2017-01-01

Selective laser melting (SLM) is an additive manufacturing (AM) technique that uses powders to fabricate 3Dparts directly. The objective of this paper is to perform an experimental investigation of selective laser melted 17-4PH stainless steel. The investigation involved the influence of separate processing parameters on the density, defect, microhardness and the influence of heat-treatment on the mechanical properties. The outcomes of this study show that scan velocity and slice thickness have significant effects on the density and the characteristics of pores of the SLMed parts. The effect of hatch spacing depends on scan velocity. The processing parameters, such as scan velocity, hatch spacing and slice thickness, have effect on microhardness. Compared to the samples with no heat-treatment, the yield strength of the heat-treated sample increases significantly and the elongation decreases due to the transformation of microstructure and the changes in the precipitation strengthening phases. By a combination of changes in composition and precipitation strengthening, microhardness improved.

Microstructural Changes During Plastic Deformation and Corrosion Properties of Biomedical Co-20Cr-15W-10Ni Alloy Heat-Treated at 873 K

NASA Astrophysics Data System (ADS)

Ueki, Kosuke; Ueda, Kyosuke; Nakai, Masaaki; Nakano, Takayoshi; Narushima, Takayuki

2018-04-01

Microstructural changes were observed during the plastic deformation of ASTM F90 Co-20Cr-15W-10Ni (mass pct) alloy heat-treated at 873 K (600 °C) for 14.4 ks, and analyzed by electron backscatter diffraction and in situ X-ray diffraction techniques. The obtained results revealed that the area fraction of the ɛ-phase (f ɛ ) in the as-received alloy was higher than that in the heat-treated alloy in the low-to-middle strain region (≤ 50 pct), whereas the f ɛ of the heat-treated alloy was higher than that of the as-received alloy at the fracture point. During plastic deformation, the ɛ-phase was preferentially formed at the twin boundaries of the heat-treated alloy rather than at the grain boundaries. According to the transmission electron microscopy observations, the thin ɛ-phase layer formed due to the alloy heat treatment acted as the origin of deformation twinning, which decreased the stress concentration at the grain boundaries. The results of anodic polarization testing showed that neither the heat treatment at 873 K (600 °C) nor plastic deformation affected the alloy corrosion properties. To the best of our knowledge, this is the first study proving that the formation of a thin ɛ-phase layer during the low-temperature heat treatment of the studied alloy represents an effective method for the enhancement of the alloy ductility without sacrificing its strength and corrosion properties.

Microstructural Changes During Plastic Deformation and Corrosion Properties of Biomedical Co-20Cr-15W-10Ni Alloy Heat-Treated at 873 K

NASA Astrophysics Data System (ADS)

Ueki, Kosuke; Ueda, Kyosuke; Nakai, Masaaki; Nakano, Takayoshi; Narushima, Takayuki

2018-06-01

Microstructural changes were observed during the plastic deformation of ASTM F90 Co-20Cr-15W-10Ni (mass pct) alloy heat-treated at 873 K (600 °C) for 14.4 ks, and analyzed by electron backscatter diffraction and in situ X-ray diffraction techniques. The obtained results revealed that the area fraction of the ɛ-phase ( f ɛ ) in the as-received alloy was higher than that in the heat-treated alloy in the low-to-middle strain region (≤ 50 pct), whereas the f ɛ of the heat-treated alloy was higher than that of the as-received alloy at the fracture point. During plastic deformation, the ɛ-phase was preferentially formed at the twin boundaries of the heat-treated alloy rather than at the grain boundaries. According to the transmission electron microscopy observations, the thin ɛ-phase layer formed due to the alloy heat treatment acted as the origin of deformation twinning, which decreased the stress concentration at the grain boundaries. The results of anodic polarization testing showed that neither the heat treatment at 873 K (600 °C) nor plastic deformation affected the alloy corrosion properties. To the best of our knowledge, this is the first study proving that the formation of a thin ɛ-phase layer during the low-temperature heat treatment of the studied alloy represents an effective method for the enhancement of the alloy ductility without sacrificing its strength and corrosion properties.

Review of critical flow rate, propagation of pressure pulse, and sonic velocity in two-phase media

NASA Technical Reports Server (NTRS)

Hsu, Y.

1972-01-01

For single-phase media, the critical discharge velocity, the sonic velocity, and the pressure pulse propagation velocity can be expressed in the same form by assuming isentropic, equilibria processes. In two-phase mixtures, the same concept is not valid due to the existence of interfacial transports of momentum, heat, and mass. Thus, the three velocities should be treated differently and separately for each particular condition, taking into account the various transport processes involved under that condition. Various attempts are reviewed to predict the critical discharge rate or the propagation velocities by considering slip ratio (momentum change), evaporation (mass and heat transport), flow pattern, etc. Experimental data were compared with predictions based on various theorems. The importance is stressed of the time required to achieve equilibrium as compared with the time available during the process, for example, of passing a pressure pulse.

Corrosion behavior of Ni-based structural materials for electrolytic reduction in lithium molten salt

NASA Astrophysics Data System (ADS)

Cho, Soo Haeng; Park, Sung Bin; Lee, Jong Hyeon; Hur, Jin Mok; Lee, Han Soo

2011-05-01

In this study, the corrosion behavior of new Ni-based structural materials was studied for electrolytic reduction after exposure to LiCl-Li 2O molten salt at 650 °C for 24-216 h under an oxidizing atmosphere. The new alloys with Ni, Cr, Al, Si, and Nb as the major components were melted at 1700 °C under an inert atmosphere. The melt was poured into a preheated metallic mold to prepare an as-cast alloy. The corrosion products and fine structures of the corroded specimens were characterized by scanning electron microscope (SEM), Energy Dispersive X-ray Spectroscope (EDS), and X-ray diffraction (XRD). The corrosion products of as cast and heat treated low Si/high Ti alloys were Cr 2O 3, NiCr 2O 4, Ni, NiO, and (Al,Nb,Ti)O 2; those of as cast and heat treated high Si/low Ti alloys were Cr 2O 3, NiCr 2O 4, Ni, and NiO. The corrosion layers of as cast and heat treated low Si/high Ti alloys were continuous and dense. However, those of as cast and heat treated high Si/low Ti alloys were discontinuous and cracked. Heat treated low Si/high Ti alloy showed the highest corrosion resistance among the examined alloys. The superior corrosion resistance of the heat treated low Si/high Ti alloy was attributed to the addition of an appropriate amount of Si, and the metallurgical evaluations were performed systematically.

Heat Tolerances of Salmonella, Cronobacter sakazakii, and Pediococcus acidilactici Inoculated into Galactooligosaccharide.

PubMed

Bang, Jihyun; Choi, Moonkak; Jeong, Haeseok; Lee, Sangseob; Kim, Yoonbin; Ryu, Jee-Hoon; Kim, Hoikyung

2017-07-01

Food-grade galactooligosaccharide (GOS) with low water activity (a w of ca. 0.7) is used as an ingredient in various foods. We evaluated heat tolerances of Salmonella, Cronobacter sakazakii, and Pediococcus acidilactici at temperatures (70 to 85°C) used during the saturation process of GOS by comparing decimal reduction time (D-values) and thermal resistance constants (z-values). To determine the D- and z-values, GOS containing Salmonella (5.1 to 5.8 log CFU/g) or C. sakazakii (5.3 to 5.9 log CFU/g) was heat treated at 70, 77.5, or 85°C for up to 40, 25, or 15 s, respectively, and GOS containing P. acidilactici (6.1 to 6.5 log CFU/g) was heat treated at 70, 77.5, or 85°C for up to 150, 75, or 40 s, respectively. The D-values were calculated using a linear model for heating time versus microbial population for each bacterium. When the D-values for Salmonella, C. sakazakii, and P. acidilactici in GOS were compared, the thermal resistance of all bacteria decreased as the temperature increased. Among the three bacteria, P. acidilactici had higher D-values than did Salmonella and C. sakazakii. The z-values of Salmonella, C. sakazakii, and P. acidilactici were 30.10, 33.18, and 13.04°C, respectively. Overall order of thermal resistance was P. acidilactici > Salmonella ≈ C. sakazakii. These results will be useful for selecting appropriate heat treatment conditions for the decontamination of pathogenic microorganisms during GOS manufacturing.

Integration of Heat Treatment with Shot Peening of 17-4 Stainless Steel Fabricated by Direct Metal Laser Sintering

NASA Astrophysics Data System (ADS)

AlMangour, Bandar; Yang, Jenn-Ming

2017-11-01

Direct metal laser sintering (DMLS) is a promising powder-based additive manufacturing process for fabrication of near-net-shape parts. However, the typically poor fatigue performance of DMLS parts must be addressed for use in demanding industrial applications. Post-treatment can be applied to enhance the performance of such components. Earlier attempts at inducing grain refinement through severe plastic deformation of part surfaces using shot peening improved the physical and mechanical properties of metals without chemical alteration. However, heat treatment can modify the surface-hardening effects attained by shot peening. Hence, we examined the feasibility of applying shot peening combined with heat treatment to improve the performance of DMLS-fabricated 17-4 stainless steel parts through microstructural evolution studies and hardness measurements. Compared to a specimen treated only by shot peening, the sample exposed to additional heat treatment showed increased hardness due to aging of the dominant phase.

Microstructure and mechanical properties of selective laser melted Ti6Al4V alloy

NASA Astrophysics Data System (ADS)

Losertová, M.; Kubeš, V.

2017-11-01

The present work was focused on the properties of porous Ti6Al4V specimens processed by selective laser melting (SLM) and tested in tension and compression before and after heat treatment. The SLM samples were annealed at 955 °C, water quenched and aged at 600 °C with following air cooling. The values of the mechanical tests showed that the samples exhibited high mechanical properties. The anisotropy of tensile and compressive strength was observed, which was related to the occurrence of voids. The plastic properties of specimens were improved by means of the heat treatment that led to the transformation of martensitic to lamellar structure composed of α + β phases. The microstructure of SLM samples were evaluated before and after the heat treatment. The brittle nature of failures of non-heat treated samples can be explained by synergy of martensite presence, microcracks and residual stresses produced by SLM.

Anisotropic pyrochemical microetching of poly(tetrafluoroethylene) initiated by synchrotron radiation-induced scission of molecule bonds

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yamaguchi, Akinobu, E-mail: yamaguti@lasti.u-hyogo.ac.jp, E-mail: utsumi@lasti.u-hyogo.ac.jp; Kido, Hideki; Utsumi, Yuichi, E-mail: yamaguti@lasti.u-hyogo.ac.jp, E-mail: utsumi@lasti.u-hyogo.ac.jp

2016-02-01

We developed a process for micromachining polytetrafluoroethylene (PTFE): anisotropic pyrochemical microetching induced by synchrotron X-ray irradiation. X-ray irradiation was performed at room temperature. Upon heating, the irradiated PTFE substrates exhibited high-precision features. Both the X-ray diffraction peak and Raman signal from the irradiated areas of the substrate decreased with increasing irradiation dose. The etching mechanism is speculated as follows: X-ray irradiation caused chain scission, which decreased the number-average degree of polymerization. The melting temperature of irradiated PTFE decreased as the polymer chain length decreased, enabling the treated regions to melt at a lower temperature. The anisotropic pyrochemical etching process enabledmore » the fabrication of PTFE microstructures with higher precision than simultaneously heating and irradiating the sample.« less

Comparison of physical and chemical properties of high pressure- and heat-treated Lychee (Litchi chinensis Sonn.) in syrup

NASA Astrophysics Data System (ADS)

Dajanta, Katekan; Apichartsrangkoon, Arunee; Somsang, Soontaree

2012-03-01

Lychee usually has white flesh, but its flesh is very sensitive to thermal and enzymatic impairment and ultimately changes in color. This investigation was intended to study the magnitude of color change in lychee by high pressure and thermal processing. The lychee was packed in syrup prior to being processed. Pressurized lychee was performed at 600 MPa at 30°C or 50°C for 20 min, while the pasteurized sample was heated at 90°C for 3 min. It was found that pressurization induced lower color L*, a* and b* values, including low anthocyanin content. For enzymatic activities, high pressure could reduce the activity of polyphenoloxidase by 33-51%, whereas pasteurization markedly reduced that activity by 90%.

The processes of formation and epitaxial alignment of SrTiO3 thin films prepared by metallo-organic decomposition

NASA Astrophysics Data System (ADS)

Braunstein, G.; Paz-Pujalt, G. R.; Mason, M. G.; Blanton, T.; Barnes, C. L.; Margevich, D.

1993-01-01

The processes of formation and crystallization of thin films of SrTiO3 prepared by the method of metallo-organic decomposition have been studied with particular emphasis on the relationship between the thermal decomposition of the metallo-organic precursors and the eventual epitaxial alignment of the crystallized films. The films are deposited by spin coating onto single-crystalline silicon and SrTiO3 substrates, pyrolyzed on a hot plate at temperatures ranging from 200 to 450 °C, and subsequently heat treated in a quartz tube furnace at temperatures ranging from 300 to 1200 °C. Heat treatment at temperatures up to 450-500 °C results in the evaporation of solvents and other organic addenda, thermal decomposition of the metallo-organic (primarily metal-carboxylates) precursors, and formation of a carbonate species. This carbonate appears to be an intermediate phase in the reaction of SrCO3 and TiO2 to form SrTiO3. Relevant to this work is the fact that the carbonate species exhibits diffraction lines, indicating the formation of grains that can serve as seeds for the nucleation and growth of randomly oriented SrTiO3 crystallites, thereby leading to a polycrystalline film. Deposition on silicon substrates indeed results in the formation of polycrystalline SrTiO3. However, when the precursor solution is deposited on single-crystalline SrTiO3 substrates, the crystallization process involves a competition between two mechanisms: the random nucleation and growth of crystallites just described, and layer-by-layer solid phase epitaxy. Epitaxial alignment on SrTiO3 substrates can be achieved when the samples are heat treated at temperatures of 1100-1200 °C or at temperatures as low as 600-650 °C when the substrate is heated to about 1100 °C before spin coating.

Heat emergencies

MedlinePlus

Heatstroke; Heat illness ... who is in good shape can suffer heat illness if warning signs are ignored. The following make ... Heat cramps are the first stage of heat illness. If these symptoms are not treated, it can ...

Preparation of the porous cerium dioxide film by two-step anodization and heat treating method

NASA Astrophysics Data System (ADS)

Liu, Xiaozhen; Zhu, Bolun; Liu, Yuze; Wang, Shanshan; Chen, Jie; Wang, Xiaoyu

2017-12-01

The porous cerium dioxide films were prepared with cerium foils as raw materials by two-step anodization and heat treating method. The anodic cerium oxide films were heat treated in 25∼400°C respectively. The cerium dioxide films were characterized with X-ray diffraction (XRD), Fourier transform infrared (FTIR) techniques, energy-dispersive analyses of X-ray (EDAX) and scanning electron microcopy (SEM), respectively. The anodic cerium oxide film is composed of Ce(OH)3, CeO2 and Ce2O3. When the anodic cerium oxide films were heat treated in 300°C∼400°C for 2h, Ce(OH)3 and Ce2O3 in the anodic cerium oxide films may be converted to CeO2, and the heat treated anodic cerium oxide films are the cerium dioxide films. Water, ethylene glycol and CO2 are adsorbed in the anodic cerium oxide film. The adsorbing water, ethylene glycol and CO2 in the anodic cerium oxide film are removed at 300°C. The cerium dioxide film has strong absorption in the range of 1600∼4000cm-1. The structure of the cerium dioxide film is the porous.

Electromagnetic field therapy delays cellular senescence and death by enhancement of the heat shock response.

PubMed

Perez, Felipe P; Zhou, Ximing; Morisaki, Jorge; Jurivich, Donald

2008-04-01

Hormesis may result when mild repetitive stress increases cellular defense against diverse injuries. This process may also extend in vitro cellular proliferative life span as well as delay and reverse some of the age-dependent changes in both replicative and non-replicative cells. This study evaluated the potential hormetic effect of non-thermal repetitive electromagnetic field shock (REMFS) and its impact on cellular aging and mortality in primary human T lymphocytes and fibroblast cell lines. Unlike previous reports employing electromagnetic radiation, this study used a long wave length, low energy, and non-thermal REMFS (50MHz/0.5W) for various therapeutic regimens. The primary outcomes examined were age-dependent morphological changes in cells over time, cellular death prevention, and stimulation of the heat shock response. REMFS achieved several biological effects that modified the aging process. REMFS extended the total number of population doublings of mouse fibroblasts and contributed to youthful morphology of cells near their replicative lifespan. REMFS also enhanced cellular defenses of human T cells as reflected in lower cell mortality when compared to non-treated T cells. To determine the mechanism of REMFS-induced effects, analysis of the cellular heat shock response revealed Hsp90 release from the heat shock transcription factor (HSF1). Furthermore, REMFS increased HSF1 phosphorylation, enhanced HSF1-DNA binding, and improved Hsp70 expression relative to non-REMFS-treated cells. These results show that non-thermal REMFS activates an anti-aging hormetic effect as well as reduces cell mortality during lethal stress. Because the REMFS configuration employed in this study can potentially be applied to whole body therapy, prospects for translating these data into clinical interventions for Alzheimer's disease and other degenerative conditions with aging are discussed.

Induction of heat-shock response and alterations of protein phosphorylation by a novel topoisomerase II inhibitor, withangulatin A, in 9L rat brain tumor cells.

PubMed

Lee, W C; Lin, K Y; Chen, C M; Chen, Z T; Liu, H J; Lai, Y K

1991-10-01

Withangulatin A is a newly identified in vitro topoisomerase II inhibitor isolated from the Chinese antitumor herb Physalis angulata. In vivo, it was found to be cytotoxic, capable of suppressing general protein synthesis and of inducing the synthesis of a small set of proteins including those generated by heat-shock treatment. The 70 kDa protein generated by withangulatin A was unequivocally identified as the heat-shock protein 70 (HSP70) since both proteins migrated to the same position on two-dimensional polyacrylamide gels, could be recognized by a monoclonal antibody to human HSP70, and exhibited identical peptide maps. The induction of protein synthesis by withangulatin A was regulated at the transcriptional level since it was aborted in cells pre-treated with actinomycin D. However, the initiation of this process did not require de novo protein synthesis since it was not affected by cycloheximide. Other cellular effect of withangulatin A was alterations of protein phosphorylation including an enhancement of phosphorylation of a 65 kDa protein which was also detected in the heat-shocked cells. Moreover, this process was observed within 7.5 min after the initial heat treatment which is much faster than the onset of HSP synthesis. Therefore, increased phosphorylation of the 65 kDa protein may represent one of the earliest signals generated by both heat-shock and withangluatin A and may be involved in the upstream regulation of heat-shock response in cells.

Evolution of radiation defect and radiation hardening in heat treated SA508 Gr3 steel

NASA Astrophysics Data System (ADS)

Jin, Hyung-Ha; Kwon, Junhyun; Shin, Chansun

2014-01-01

The formation of radiation defects and corresponding radiation hardening in heat-treated SA508 Gr3 steel after Fe ion irradiation were investigated by means of transmission electron microscopy and a nano-indentation technique. As the residual dislocation density is increased in the matrix, the formation of radiation defects is considerably weakened. Comparison between the characteristics of the radiation defect and an evaluation of radiation hardening indicates that a large dislocation loop contributes little to the radiation hardening in the heat-treated SA508 Gr3 steel.

Potential New Sensor for Use With Conventional Gas Carburizing

NASA Technical Reports Server (NTRS)

deGroot, W. A.

1997-01-01

Diagnostics developed for in-situ monitoring of rocket combustion environments have been adapted for use in heat treating furnaces. Simultaneous, in-situ monitoring of the carbon monoxide, carbon dioxide, methane, water, nitrogen and hydrogen concentrations in the endothermic gas of a heat treating furnace has been demonstrated under a Space Act Agreement between NASA Lewis, the Heat Treating Network, and Akron Steel Treating Company. Equipment installed at the Akron Steel Treating Company showed the feasibility of the method. Clear and well-defined spectra of carbon monoxide, nitrogen and hydrogen were obtained by means of an optical probe mounted on the endothermic gas line of a gas generator inside the plant, with the data reduction hardware located in the basement laboratory. Signals to and from the probe were transmitted via optical fibers.

Method for reducing energy losses in laser crystals

DOEpatents

Atherton, L.J.; DeYoreo, J.J.; Roberts, D.H.

1992-03-24

A process for reducing energy losses in crystals is disclosed which comprises: a. heating a crystal to a temperature sufficiently high as to cause dissolution of microscopic inclusions into the crystal, thereby converting said inclusions into point-defects, and b. maintaining said crystal at a given temperature for a period of time sufficient to cause said point-defects to diffuse out of said crystal. Also disclosed are crystals treated by the process, and lasers utilizing the crystals as a source of light. 12 figs.

Method for reducing energy losses in laser crystals

DOEpatents

Atherton, L. Jeffrey; DeYoreo, James J.; Roberts, David H.

1992-01-01

A process for reducing energy losses in crystals is disclosed which comprises: a. heating a crystal to a temperature sufficiently high as to cause dissolution of microscopic inclusions into the crystal, thereby converting said inclusions into point-defects, and b. maintaining said crystal at a given temperature for a period of time sufficient to cause said point-defects to diffuse out of said crystal. Also disclosed are crystals treated by the process, and lasers utilizing the crystals as a source of light.

Apparatus for fabricating continuous lengths of superconductor

DOEpatents

Kroeger, Donald M.; List, III, Frederick A.

2002-01-01

A process and apparatus for manufacturing a superconductor. The process is accomplished by depositing a superconductor precursor powder on a continuous length of a first substrate ribbon, overlaying a continuous length of a second substrate ribbon on said first substrate ribbon, and applying sufficient pressure to form a bound layered superconductor comprising a layer of said superconducting precursor powder between said first substrate ribbon and said second substrates ribbon. The layered superconductor is then heat treated to establish the superconducting phase of said superconductor precursor powder.

Apparatus for fabricating continuous lengths of superconductor

DOEpatents

Kroeger, Donald M.; List, III, Frederick A.

2001-01-01

A process and apparatus for manufacturing a superconductor. The process is accomplished by depositing a superconductor precursor powder on a continuous length of a first substrate ribbon, overlaying a continuous length of a second substrate ribbon on said first substrate ribbon, and applying sufficient pressure to form a bound layered superconductor comprising a layer of said superconducting precursor powder between said first substrate ribbon and said second substrates ribbon. The layered superconductor is then heat treated to establish the superconducting phase of said superconductor precursor powder.

Heat Treating Apparatus

DOEpatents

De Saro, Robert; Bateman, Willis

2002-09-10

Apparatus for heat treating a heat treatable material including a housing having an upper opening for receiving a heat treatable material at a first temperature, a lower opening, and a chamber therebetween for heating the heat treatable material to a second temperature higher than the first temperature as the heat treatable material moves through the chamber from the upper to the lower opening. A gas supply assembly is operatively engaged to the housing at the lower opening, and includes a source of gas, a gas delivery assembly for delivering the gas through a plurality of pathways into the housing in countercurrent flow to movement of the heat treatable material, whereby the heat treatable material passes through the lower opening at the second temperature, and a control assembly for controlling conditions within the chamber to enable the heat treatable material to reach the second temperature and pass through the lower opening at the second temperature as a heated material.

Heat sterilization of ash (Fraxinus spp.) firewood : heat-treating options, temperature monitoring and thermal verification

Treesearch

Xiping Wang; Richard Bergman; T. Mace

2010-01-01

Because of the potential risk associated with moving emerald ash borer (EAB)-infested firewood, the interstate movement of all hardwood firewood in the USA is currently restricted under the Federal quarantine. Communities and firewood producers are now faced with decisions on how to treat their firewood for interstate commerce. The new US Federal regulations for heat...

Salicylic acid alleviates decreases in photosynthesis under heat stress and accelerates recovery in grapevine leaves.

PubMed

Wang, Li-Jun; Fan, Ling; Loescher, Wayne; Duan, Wei; Liu, Guo-Jie; Cheng, Jian-Shan; Luo, Hai-Bo; Li, Shao-Hua

2010-02-23

Although the effect of salicylic acid (SA) on photosynthesis of plants including grapevines has been investigated, very little is yet known about the effects of SA on carbon assimilation and several components of PSII electron transport (donor side, reaction center and acceptor side). In this study, the impact of SA pretreatment on photosynthesis was evaluated in the leaves of young grapevines before heat stress (25 degrees C), during heat stress (43 degrees C for 5 h), and through the following recovery period (25 degrees C). Photosynthetic measures included gas exchange parameters, PSII electron transport, energy dissipation, and Rubisco activation state. The levels of heat shock proteins (HSPs) in the chloroplast were also investigated. SA did not significantly (P < 0.05) influence the net photosynthesis rate (Pn) of leaves before heat stress. But, SA did alleviate declines in Pn and Rubisco activation state, and did not alter negative changes in PSII parameters (donor side, acceptor side and reaction center QA) under heat stress. Following heat treatment, the recovery of Pn in SA-treated leaves was accelerated compared with the control (H2O-treated) leaves, and, donor and acceptor parameters of PSII in SA-treated leaves recovered to normal levels more rapidly than in the controls. Rubisco, however, was not significantly (P < 0.05) influenced by SA. Before heat stress, SA did not affect level of HSP 21, but the HSP21 immune signal increased in both SA-treated and control leaves during heat stress. During the recovery period, HSP21 levels remained high through the end of the experiment in the SA-treated leaves, but decreased in controls. SA pretreatment alleviated the heat stress induced decrease in Pn mainly through maintaining higher Rubisco activation state, and it accelerated the recovery of Pn mainly through effects on PSII function. These effects of SA may be related in part to enhanced levels of HSP21.

The effect of UV exposure and heat treatment on crystallization behavior of photosensitive glasses

NASA Astrophysics Data System (ADS)

Kıbrıslı, Orhan; Ersundu, Ali Erçin

2018-05-01

In this study, photosensitive glasses in the Na2O-ZnO-Al2O3-SiO2 system with photosensitizing agents (cerium, silver, tin, antimony) and halogenides (NaF and KBr) were synthesized through a conventional melt-quenching technique. The crystallization mechanism was investigated for solely heat-treated and UV-exposed + heat-treated samples using differential thermal analysis (DTA), X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDS) and scanning electron microscopy (SEM) techniques to understand the effect of UV exposure on crystallization behavior of photosensitive glasses. Accordingly, non-isothermal DTA measurements were performed at different heating rates to determine crystallization peak, T p, and onset, T c, temperatures. For solely heat-treated samples, the kinetic parameters such as the Avrami constant, n, and morphology index, m, were calculated as 1 from the Ozawa method indicating surface crystallization and the value of crystallization activation energy was calculated as 944 kJ/mol using modified Kissinger method. On the contrary, bulk crystallization was found to be predominant for UV exposed + heat-treated samples revealing that UV exposure is the primary cause of bulk crystallization in photosensitive glasses.

Mitigation of heat stress-related complications by a yeast fermentate product.

PubMed

Giblot Ducray, Henri Alexandre; Globa, Ludmila; Pustovyy, Oleg; Reeves, Stuart; Robinson, Larry; Vodyanoy, Vitaly; Sorokulova, Iryna

2016-08-01

Heat stress results in a multitude of biological and physiological responses which can become lethal if not properly managed. It has been shown that heat stress causes significant adverse effects in both human and animals. Different approaches have been proposed to mitigate the adverse effects caused by heat stress, among which are special diet and probiotics. We characterized the effect of the yeast fermentate EpiCor (EH) on the prevention of heat stress-related complications in rats. We found that increasing the body temperature of animals from 37.1±0.2 to 40.6±0.2°C by exposure to heat (45°C for 25min) resulted in significant morphological changes in the intestine. Villi height and total mucosal thickness decreased in heat-stressed rats pre-treated with PBS in comparison with control animals not exposed to the heat. Oral treatment of rats with EH before heat stress prevented the traumatic effects of heat on the intestine. Changes in intestinal morphology of heat-stressed rats, pre-treated with PBS resulted in significant elevation of lipopolysaccharides (LPS) level in the serum of these animals. Pre-treatment with EH was effective in the prevention of LPS release into the bloodstream of heat-stressed rats. Our study revealed that elevation of body temperature also resulted in a significant increase of the concentration of vesicles released by erythrocytes in rats, pre-treated with PBS. This is an indication of a pathological impact of heat on the erythrocyte structure. Treatment of rats with EH completely protected their erythrocytes from this heat-induced pathology. Finally, exposure to heat stress conditions resulted in a significant increase of white blood cells in rats. In the group of animals pre-treated with EH before heat stress, the white blood cell count remained the same as in non-heated controls. These results showed the protective effect of the EH product in the prevention of complications, caused by heat stress. Copyright © 2016 The Authors. Published by Elsevier Ltd.. All rights reserved.

Heat treatment's effects on hydroxyapatite powders in water vapor and air atmosphere

NASA Astrophysics Data System (ADS)

Karabulut, A.; Baştan, F. E.; Erdoǧan, G.; Üstel, F.

2015-03-01

Hydroxyapatite (HA; Ca10(PO4)6(OH)2) is the main chemical constituent of bone tissue (~70%) as well as HA which is a calcium phosphate based ceramic material forms inorganic tissue of bone and tooth as hard tissues is used in production of prosthesis for synthetic bone, fractured and broken bone restoration, coating of metallic biomaterials and dental applications because of its bio compatibility. It is known that Hydroxyapatite decomposes with high heat energy after heat treatment. Therefore hydroxyapatite powders that heated in water vapor will less decomposed phases and lower amorphous phase content than in air atmosphere. In this study high purity hydroxyapatite powders were heat treated with open atmosphere furnace and water vapor atmosphere with 900, 1000, 1200 °C. Morphology of same powder size used in this process by SEM analyzed. Chemical structures of synthesized coatings have been examined by XRD. The determination of particle size and morphological structure of has been characterized by Particle Sizer, and SEM analysis, respectively. Weight change of sample was recorded by thermogravimetric analysis (TGA) during heating and cooling.

Material properties and laser cutting of composites

NASA Astrophysics Data System (ADS)

Chen, Chia-Chieh; Cheng, Wing

Laser (Light Amplification by Stimulated Emission of Radiation) has been used successfully for many material cutting, drilling, metal welding and heat treating applications. However, laser cutting of polymer composites were attempted with varying degrees of success. Because composites are heterogeneous, the energy applied by laser could result in severe resin degradation before fibers were cut. In this study, cutting of glass, Kevlar, and graphite composites were evaluated based on their material properties and laser cutting parameters. A transient heat transfer analysis was used to determine the relative heat affected zones of these composites. Kevlar composites can be cut very well while graphite composites are difficult to cut. Though the cutting process is much more complicated in reality, the analysis provides a semi-quantitative perspective on the characteristics and limitations of laser cutting of different composites.

Sapphire reinforced alumina matrix composites

NASA Technical Reports Server (NTRS)

Jaskowiak, Martha H.; Setlock, John A.

1994-01-01

Unidirectionally reinforced A1203 matrix composites have been fabricated by hot pressing. Approximately 30 volume % of either coated or uncoated sapphire fiber was used as reinforcement. Unstabilized ZrO2 was applied as the fiber coating. Composite mechanical behavior was analyzed both after fabrication and after additional heat treatment. The results of composite tensile tests were correlated with fiber-matrix interfacial shear strengths determined from fiber push-out tests. Substantially higher strength and greater fiber pull-out were observed for the coated fiber composites for all processing conditions studied. The coated fiber composites retained up to 95% and 87% of their as-fabricated strength when heat treated at 14000C for 8 or 24 hours, respectively. Electron microscopy analysis of the fracture surfaces revealed extensive fiber pull-out both before and after heat treatment.

Simulation study on heat conduction of a nanoscale phase-change random access memory cell.

PubMed

Kim, Junho; Song, Ki-Bong

2006-11-01

We have investigated heat transfer characteristics of a nano-scale phase-change random access memory (PRAM) cell using finite element method (FEM) simulation. Our PRAM cell is based on ternary chalcogenide alloy, Ge2Sb2Te5 (GST), which is used as a recording layer. For contact area of 100 x 100 nm2, simulations of crystallization and amorphization processes were carried out. Physical quantities such as electric conductivity, thermal conductivity, and specific heat were treated as temperature-dependent parameters. Through many simulations, it is concluded that one can reduce set current by decreasing both electric conductivities of amorphous GST and crystalline GST, and in addition to these conditions by decreasing electric conductivity of molten GST one can also reduce reset current significantly.

Decreased fat accumulation in 3T3-L1 pre-adipocytes treated with extracts of heat processed soy flour and breads

USDA-ARS?s Scientific Manuscript database

The antiadipogenic effects of a gluten-free soy bread developed from soy flour pretreated by germination (GS), steaming (SS), or roasting (RS) were evaluated in an in vitro adipocyte cell model. Previously we had shown that soy bread prepared by GS, SS or RS flours had acceptable sensory attributes ...

Effect of heat and radio frequency electric field treatments on membrane damage and intracellular leakage of UV-substances of Escherichia coli K-12 in apple juice

USDA-ARS?s Scientific Manuscript database

The need for a nonthermal intervention technology that can achieve microbial safety without altering nutritional quality of liquid foods led to the development of the radio frequency electric fields (RFEF) process. Previously, we documented formation of surface blebs on Escherichia coli cells treate...

75 FR 79964 - Regulation of Fuels and Fuel Additives: Modifications to Renewable Fuel Standard Program

Federal Register 2010, 2011, 2012, 2013, 2014

2010-12-21

... after July 1, 2010, may only be generated and transferred using the EPA Moderated Transaction System.... 80.1426; --Sec. 80.1426(f)(12), which clarified the requirements for gas used for process heat at a... (RINs) are treated under each program. However, in the final RFS2 rule, the section on product transfer...

Effects of dimethyl dicarbonate (DMDC) on the fermentation of litchi juice by Lactobacillus casei as an alternative of heat treatment.

PubMed

Yu, Yuanshan; Xiao, Gengsheng; Xu, Yujuan; Wu, Jijun; Wen, Jing

2014-05-01

This study investigated the effects of dimethyl dicarbonate (DMDC) on the fermentation of litchi juice by Lactobacillus casei as an alternative of heat treatment that may have undesirable effect on the juice. Quality attributes and products stability of both the fermented heat- and DMDC-treated litchi juice by L. casei were compared. It was found that residual indigenous microorganisms in both the heat- and DMDC-treated litchi juice cannot grow into dominant bacteria during further fermentation of litchi juice by L. casei. Compared with fermented heat-treated litchi juice, fermented DMDC-treated litchi juice showed a better color, flavor, and overall acceptance, and also retained more total phenolics and antioxidant capacity. The viability counts of L. casei in both the heat- and DMDC-treated litchi juice were more 8.0 lg CFU/mL after 4 wk of storage at 4 °C. Also, some quality attributes in both the fermented heat- and DMDC-treated litchi juices, including pH, total phenolics, ascorbic acid, antioxidant capacity, and so on, showed the tendency to slow decrease during storage at 4 °C, but the scores of overall acceptance showed no reduction after the storage of 4 wk at 4 °C. On the whole, the application of DMDC treatment could be an ideal alternative of heat treatment to ensure the microbial safety, consistent sensory, and nutritional quality of fermented litchi juice prior to fermentation. The pasteurization treatment is often recommended prior to fermentation of fruit juice by probiotics, as it would lead to a rapid inactivation and inhibition of spoilage and pathogenic bacteria, and ensure the fermented products with consistent sensory and nutritional quality. Dimethyl dicarbonate (DMDC) is a powerful antimicrobial agent, which was approved for use as a microbial control agent in juice beverages by FDA. This study provides a scientific basis for the application of DMDC prior to fermentation of litchi juice. © 2014 Institute of Food Technologists®

Evaluation of an Al-Ce alloy for laser additive manufacturing

DOE PAGES

Plotkowski, A.; Rios, O.; Sridharan, N.; ...

2016-12-27

Our present research in metal additive manufacturing (AM) focuses on designing processing parameters around existing alloys designed for traditional manufacturing. However, to maximize the benefits of AM, alloys should be designed to specifically take advantage of the unique thermal conditions of these processes. Furthermore, our study focuses on the development of a design methodology for alloys in AM, using a newly developed Al-Ce alloy as an initial case study. To evaluate the candidacy of this system for fusion based additive manufacturing, single-line laser melts were made on cast Al-12Ce plates using three different beam velocities (100, 200, and 300 mm/min).more » The microstructure was evaluated in the as-melted and heat treated conditions (24 hrs at 300°C). An extremely fine microstructure was observed within the weld pools, evolving from eutectic at the outer solid-liquid boundaries to a primary Al FCC dendritic/cellular structure nearer the melt-pool centerline. We rationalized the observed microstructures through the construction of a microstructure selection map for the Al-Ce binary system, which will be used to enable future alloy design. Interestingly, the heat treated samples exhibited no microstructural coarsening.« less

Impact of Si on Microstructure and Mechanical Properties of 22MnB5 Hot Stamping Steel Treated by Quenching & Partitioning (Q&P)

NASA Astrophysics Data System (ADS)

Linke, Bernd M.; Gerber, Thomas; Hatscher, Ansgar; Salvatori, Ilaria; Aranguren, Iñigo; Arribas, Maribel

2018-01-01

Based on 22MnB5 hot stamping steel, three model alloys containing 0.5, 0.8, and 1.5 wt pct Si were produced, heat treated by quenching and partitioning (Q&P), and characterized. Aided by DICTRA calculations, the thermal Q&P cycles were designed to fit into industrial hot stamping by keeping partitioning times ≤ 30 seconds. As expected, Si increased the amount of retained austenite (RA) stabilized after final cooling. However, for the intermediate Si alloy the heat treatment exerted a particularly pronounced influence with an RA content three times as high for the one-step process compared to the two-step process. It appeared that 0.8 wt pct Si sufficed to suppress direct cementite formation from within martensite laths but did not sufficiently stabilize carbon-soaked RA at higher temperatures. Tensile and bending tests showed strongly diverging effects of austenite on ductility. Total elongation improved consistently with increasing RA content independently from its carbon content. In contrast, the bending angle was not impacted by high-carbon RA but deteriorated almost linearly with the amount of low-carbon RA.

Synthesizing Pt nanoparticles in the presence of methylamine: Impact of acetic acid treatment in the electrocatalytic activity of formic acid oxidation

NASA Astrophysics Data System (ADS)

Ooi, M. D. Johan; Aziz, A. Abdul

2017-05-01

Surfactant removal from the surface of platinum nanoparticles prepared by solution based method is a prerequisite process to accomplish a high catalytic activity for electrochemical reactions. Here, we report a possible approach of combining acid acetic with thermal treatment for improving catalytic performance of formic acid oxidation. This strategy involves conversion of amine to amide in acetic acid followed by surfactant removal via subsequent thermal treatment at 85 °C. This combined activation technique produced monodisperse nanoparticle with the size of 3 to 5 nm with enhanced formic acid oxidation activity, particularly in perchloric acid solution. Pt treated in 1 h of acetic acid and heat treatment of 9 h shows high electrochemical surface area value (27.6 m2/g) compares to Pt without activation (16.6 m2/g). The treated samples also exhibit high current stability of 0.3 mA/cm2 compares to the as-prepared mA/cm2). Shorter duration of acid wash and longer duration of heating process result in high electrocatalytic activity. This work demonstrates a possible technique in improving catalytic activity of platinum nanoparticles synthesized using methylamine as surfactant.

Heat stress responses modulate calcium regulations and electrophysiological characteristics in atrial myocytes.

PubMed

Chen, Yao-Chang; Kao, Yu-Hsun; Huang, Chun-Feng; Cheng, Chen-Chuan; Chen, Yi-Jen; Chen, Shih-Ann

2010-04-01

Heat stress-induced responses change the ionic currents and calcium homeostasis. However, the molecular insights into the heat stress responses on calcium homeostasis remain unclear. The purposes of this study were to examine the mechanisms of heat stress responses on calcium handling and electrophysiological characteristics in atrial myocytes. We used indo-1 fluorimetric ratio technique and whole-cell patch clamp to investigate the intracellular calcium, action potentials, and ionic currents in isolated rabbit single atrial cardiomyocytes with or without (control) exposure to heat stress (43 degrees C, 15 min) 5+/-1 h before experiments. The expressions of sarcoplasmic reticulum ATPase (SERCA2a), and Na(+)-Ca(2+) exchanger (NCX) in the control and heat stress-treated atrial myocytes were evaluated by Western blot and real-time PCR. As compared with control myocytes, the heat stress-treated myocytes had larger sarcoplasmic reticulum calcium content and larger intracellular calcium transient with a shorter decay portion. Heat stress-treated myocytes also had larger L-type calcium currents, transient outward potassium currents, but smaller NCX currents. Heat stress responses increased the protein expressions, SERCA2a, NCX, and heat shock protein. However, heat stress responses did not change the RNA expression of SERCA2a and NCX. In conclusion, heat stress responses change calcium handling through protein but not RNA regulation. Copyright (c) 2009 Elsevier Ltd. All rights reserved.

Thermo-Chemical Conversion of Microwave Activated Biomass Mixtures

NASA Astrophysics Data System (ADS)

Barmina, I.; Kolmickovs, A.; Valdmanis, R.; Vostrikovs, S.; Zake, M.

2018-05-01

Thermo-chemical conversion of microwave activated wheat straw mixtures with wood or peat pellets is studied experimentally with the aim to provide more effective application of wheat straw for heat energy production. Microwave pre-processing of straw pellets is used to provide a partial decomposition of the main constituents of straw and to activate the thermo-chemical conversion of wheat straw mixtures with wood or peat pellets. The experimental study includes complex measurements of the elemental composition of biomass pellets (wheat straw, wood, peat), DTG analysis of their thermal degradation, FTIR analysis of the composition of combustible volatiles entering the combustor, the flame temperature, the heat output of the device and composition of the products by comparing these characteristics for mixtures with unprocessed and mw pre-treated straw pellets. The results of experimental study confirm that mw pre-processing of straw activates the thermal decomposition of mixtures providing enhanced formation of combustible volatiles. This leads to improvement of the combustion conditions in the flame reaction zone, completing thus the combustion of volatiles, increasing the flame temperature, the heat output from the device, the produced heat energy per mass of burned mixture and decreasing at the same time the mass fraction of unburned volatiles in the products.

Coal desulfurization process

NASA Technical Reports Server (NTRS)

Hsu, G. C.; Gavalas, G. R.; Ganguli, P. S.; Kalfayan, S. H.

1978-01-01

A method for chlorinolysis of coal is an organic solvent at a moderate temperautre and atmospheric pressure has been proven to be effective in removing sulfur, particularly the organic sulfur, from coal. Chlorine gas is bubbled through a slurry of moist coal in chlorinated solvent. The chlorinated coal is separated, hydrolyzed and the dechlorinated. Preliminary results of treating a high sulfutr (4.77%S) bituminous coal show that up to 70% organic sulfur, 90% hyritic sulfur and 76% total sulfur can be removed. The treated coal is dechlorinated by heating at 500 C. The presence of moisture helps to remove organic sulfur.

Fourier heat conduction as a phenomenon described within the scope of the second law

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jesudason, Christopher G.

The historical development of the Carnot cycle necessitated the construction of isothermal and adiabatic pathways within the cycle that were also mechanically 'reversible' which lead eventually to the Kelvin-Clausius development of the entropy function S where for any reversible closed path C, ∮{sub C} dS = 0 based on an infinite number of concatenated Carnot engines that approximated the said path and where for each engine ΔQ{sub 1}/T{sub 1}+ΔQ{sub 2}/T{sub 2} = 0 where the Q's and T's are the heat absorption increments and temperature respectively with the subscripts indicating the isothermal paths (1;2) where for the Carnot engine, the heat absorptionmore » is for the diathermal (isothermal) paths of the cycle only. Since 'heat' has been defined as that form of energy that is transferred as a result of a temperature difference and a corollary of the Clausius statement of the Second law is that it is impossible for heat to be transferred from a cold to a hot reservoir with no other effect on the environment, these statements suggested that the local mode of transfer of 'heat' in the isothermal segments of the pathway does imply a Fourier heat conduction mechanism (to conform to the definition of 'heat') albeit of a 'reversible' kind, but on the other hand, the Fourier mechanism is apparently irreversible, leading to an increase in entropy of the combined reservoirs at either end of the material involved in the conveyance of the heat energy. These and several other considerations lead Benofy and Quay (BQ) to postulate the Fourier heat conduction phenomenon to be an ancillary principle in thermodynamics, with this principle being strictly local in nature, where the global Second law statements could not be applied to this local process. Here we present equations that model heat conduction as a thermodynamically reversible but mechanically irreversible process where due to the belief in mechanical time reversible symmetry, thermodynamical reversibility has been unfortunately linked to mechanical reversibility, that has discouraged such an association. The modeling is based on an application of a 'recoverable transition', defined and developed earlier on ideas derived from thermal desorption of particles from a surface where the Fourier heat conduction process is approximated as a series of such desorption processes. We recall that the original Carnot engine required both adiabatic and isothermal steps to complete the zero entropy cycle, and this construct lead to the consequent deduction that any Second law statement that refers to heat-work conversion processes are only globally relevant. Here, on the other hand, we examine Fourier heat conduction from MD simulation and model this process as a zero-entropy forward scattering process relative to each of the atoms in the lattice chain being treated as a system where the Carnot cycle can be applied individually. The equations developed predicts the 'work' done to be equal to the energy transfer rate. The MD simulations conducted shows excellent agreement with the theory. Such views and results as these, if developed to a successful conclusion could imply that the Carnot cycle be viewed as describing a local process of energy-work conversion and that irreversible local processes might be brought within the scope of this cycle, implying a unified treatment of thermodynamically (i) irreversible, (ii) reversible, (iii) isothermal and (iv) adiabatic processes.« less

Corrosion behavior of sensitized duplex stainless steel.

PubMed

Torres, F J; Panyayong, W; Rogers, W; Velasquez-Plata, D; Oshida, Y; Moore, B K

1998-01-01

The present work investigates the corrosion behavior of 2205 duplex stainless steel in 0.9% NaCl solution after various heat-treatments, and compares it to that of 316L austenitic stainless steel. Both stainless steels were heat-treated at 500, 650, and 800 degrees C in air for 1 h, followed by furnace cooling. Each heat-treated sample was examined for their microstructures and Vickers micro-hardness, and subjected to the X-ray diffraction for the phase identification. Using potentiostatic polarization method, each heat-treated sample was corrosion-tested in 37 degrees C 0.9% NaCl solution to estimate its corrosion rate. It was found that simulated sensitization showed an adverse influence on both steels, indicating that corrosion rates increased by increasing the sensitization temperatures.

Studies of heat treated CSS CdS films

NASA Astrophysics Data System (ADS)

Marinskiy, D.; Marinskaya, S.; Viswanathan, V.; Morel, D. L.; Ferekides, C. S.

1999-03-01

Cadmium sulfide continues to be the most successful and widely used n-type heterojunction partner in thin film CdTe solar cells. In most cases solar cell performance is enhanced if the CdS films are heat treated prior to the deposition of the CdTe. This paper discusses the effect of H2 annealing on the resistivity of CSS-CdS films and the use of a mobility activation model to explain the observed changes in resistivity. Photoluminescence measurements of CSS CdS films heat-treated in He and in CdCl2 vapor have also been carried out. In all cases the heat treatments lead to an increase in the intensity of a photoluminescence band believed to be associated with sulfur vacancies.

Heat-treated stainless steel felt as scalable anode material for bioelectrochemical systems.

PubMed

Guo, Kun; Soeriyadi, Alexander H; Feng, Huajun; Prévoteau, Antonin; Patil, Sunil A; Gooding, J Justin; Rabaey, Korneel

2015-11-01

This work reports a simple and scalable method to convert stainless steel (SS) felt into an effective anode for bioelectrochemical systems (BESs) by means of heat treatment. X-ray photoelectron spectroscopy and cyclic voltammetry elucidated that the heat treatment generated an iron oxide rich layer on the SS felt surface. The iron oxide layer dramatically enhanced the electroactive biofilm formation on SS felt surface in BESs. Consequently, the sustained current densities achieved on the treated electrodes (1 cm(2)) were around 1.5±0.13 mA/cm(2), which was seven times higher than the untreated electrodes (0.22±0.04 mA/cm(2)). To test the scalability of this material, the heat-treated SS felt was scaled up to 150 cm(2) and similar current density (1.5 mA/cm(2)) was achieved on the larger electrode. The low cost, straightforwardness of the treatment, high conductivity and high bioelectrocatalytic performance make heat-treated SS felt a scalable anodic material for BESs. Copyright © 2015 Elsevier Ltd. All rights reserved.

Electronic and Interfacial Properties of PD/6H-SiC Schottky Diode Gas Sensors

NASA Technical Reports Server (NTRS)

Chen, Liang-Yu; Hunter, Gary W.; Neudeck, Philip G.; Bansal, Gaurav; Petit, Jeremy B.; Knight, Dak; Liu, Chung-Chiun; Wu, Qinghai

1996-01-01

Pd/SiC Schottky diodes detect hydrogen and hydrocarbons with high sensitivity. Variation of the diode temperature from 100 C to 200 C shows that the diode sensitivity to propylene is temperature dependent. Long-term heat treating at 425 C up to 140 hours is carried out to determine the effect of extended heat treating on the diode properties and gas sensitivity. The heat treating significantly affects the diode's capacitive characteristics, but the diode's current carrying characteristics are much more stable with a large response to hydrogen. Scanning Electron Microscopy and X-ray Spectrometry studies of the Pd surface after the heating show cluster formation and background regions with grain structure observed in both regions. The Pd and Si concentrations vary between grains. Auger Electron Spectroscopy depth profiles revealed that the heat treating promoted interdiffusion and reaction between the Pd and SiC dw broadened the interface region. This work shows that Pd/SiC Schottky diodes have significant potential as high temperature gas sensors, but stabilization of the structure is necessary to insure their repeatability in long-term, high temperature applications.

The Effects of Metallurgical Factors on PWSCC Crack Growth Rates in TT Alloy 690 in Simulated PWR Primary Water

NASA Astrophysics Data System (ADS)

Yonezawa, Toshio; Watanabe, Masashi; Hashimoto, Atsushi

2015-06-01

Primary water stress corrosion cracking growth rates (PWSCCGRs) in highly cold-worked thermally treated (TT) Alloy 690 have been recently reported as exhibiting significant heat-to-heat variability. Authors hypothesized that these significant differences could be due to the metallurgical characteristics of each heat. In order to confirm this hypothesis, the effect of fundamental metallurgical characteristics on PWSCCGR measurements in cold-worked TT Alloy 690 has been investigated. The following new observations were made in this study: (1) Microcracks and voids were observed in or near eutectic crystals of grain boundary (GB) M23C6 carbides (primary carbides) after cold rolling, but were not observed before cold rolling. These primary carbides with microcracks and voids were observed in both lightly forged and as-cast and cold-rolled TT Alloy 690 (heat A) as well as in a cold-rolled TT Alloy 690 (heat Y) that simulated the chemical composition and carbide banded structure of the material previously tested by Paraventi and Moshier. However, this was not observed in precipitated (secondary) M23C6 GB carbides in heavily forged and cold-rolled TT Alloy 690 heat A and a cold-rolled commercial TT Alloy 690. (2) From microstructural analyses carried out on the various TT Alloy 690 test materials before and after cold rolling, the amount of eutectic crystals (primary carbides and nitrides) M23C6 and TiN depended on the chemical composition. In particular, the amount of M23C6 depended on the fabrication process. Microcracks and voids in or near the M23C6 and TiN precipitates were generated by the cold rolling process. (3) The PWSCCGRs observed in TT Alloy 690 were different for each heat and fabrication process. The PWSCCGR decreased with increasing Vickers hardness of each heat. However, for the same heats and fabrication processes, the PWSCCGR increased with increasing Vickers hardness due to cold work. Thus, the PWSCCGR must be affected not only by hardness (or equivalently the cold working ratio) but also by grain size, microcracks, and voids of primary M23C6 carbides, etc., which in turn depend on chemical composition and the fabrication process.

Engineered Multifunctional Surfaces for Fluid Handling

NASA Technical Reports Server (NTRS)

Thomas, Chris; Ma, Yonghui; Weislogel, Mark

2012-01-01

Designs incorporating variations in capillary geometry and hydrophilic and/or antibacterial surface properties have been developed that are capable of passive gas/liquid separation and passive water flow. These designs can incorporate capillary grooves and/or surfaces arranged to create linear and circumferential capillary geometry at the micro and macro scale, radial fin configurations, micro holes and patterns, and combinations of the above. The antibacterial property of this design inhibits the growth of bacteria or the development of biofilm. The hydrophilic property reduces the water contact angle with a treated substrate such that water spreads into a thin layer atop the treated surface. These antibacterial and hydrophilic properties applied to a thermally conductive surface, combined with capillary geometry, create a novel heat exchanger capable of condensing water from a humid, two-phase water and gas flow onto the treated heat exchanger surfaces, and passively separating the condensed water from the gas flow in a reduced gravity application. The overall process to generate the antibacterial and hydrophilic properties includes multiple steps to generate the two different surface properties, and can be divided into two major steps. Step 1 uses a magnetron-based sputtering technique to implant the silver atoms into the base material. A layer of silver is built up on top of the base material. Completion of this step provides the antibacterial property. Step 2 uses a cold-plasma technique to generate the hydrophilic surface property on top of the silver layer generated in Step 1. Completion of this step provides the hydrophilic property in addition to the antibacterial property. Thermally conductive materials are fabricated and then treated to create the antibacterial and hydrophilic surface properties. The individual parts are assembled to create a condensing heat exchanger with antibacterial and hydrophilic surface properties and capillary geometry, which is capable of passive phase separation in a reduced gravity application. The plasma processes for creating antibacterial and hydrophilic surface properties are suitable for applications where water is present on an exposed surface for an extended time, such that bacteria or biofilms could form, and where there is a need to manage the water on the surface. The processes are also suitable for applications where only the hydrophilic property is needed. In particular, the processes are applicable to condensing heat exchangers (CHXs), which benefit from the antibacterial properties as well as the hydrophilic properties. Water condensing onto the control surfaces of the CHX will provide the moist conditions necessary for the growth of bacteria and the formation of biofilms. The antibacterial properties of the base layer (silver) will mitigate and prevent the growth of bacteria and formation of biofilms that would otherwise reduce the CHX performance. In addition, the hydrophilic properties reduce the water contact angle and prevent water droplets from bridging between control surfaces. Overall, the hydrophilic properties reduce the pressure drop across the CHX.

The Effect of Solution Heat Treatment on an Advanced Nickel-Base Disk Alloy

NASA Technical Reports Server (NTRS)

Gayda, J.; Gabb, T. P.; Kantzos, P. T.

2004-01-01

Five heat treat options for an advanced nickel-base disk alloy, LSHR, have been investigated. These included two conventional solution heat treat cycles, subsolvus/oil quench and supersolvus/fan cool, which yield fine grain and coarse grain microstructure disks respectively, as well as three advanced dual microstructure heat treat (DMHT) options. The DMHT options produce disks with a fine grain bore and a coarse grain rim. Based on an overall evaluation of the mechanical property data, it was evident that the three DMHT options achieved a desirable balance of properties in comparison to the conventional solution heat treatments for the LSHR alloy. However, one of the DMHT options, SUB/DMHT, produced the best set of properties, largely based on dwell crack growth data. Further evaluation of the SUB/DMHT option in spin pit experiments on a generic disk shape demonstrated the advantages and reliability of a dual grain structure at the component level.

Flavor characterization of sugar-added pennywort (Centella asiatica L.) juices treated with ultra-high pressure and thermal processes.

PubMed

Apichartsrangkoon, Arunee; Wongfhun, Pronprapa; Gordon, Michael H

2009-01-01

The flavor characteristics of pennywort juices with added sugar treated by ultra-high pressure, pasteurization, and sterilization were investigated using solid phase microextraction combined with gas chromatography-mass spectrometry. It was found that sesquiterpene hydrocarbons comprised the major class of volatile components present and the juices had a characteristic aroma due to the presence of volatiles including beta-caryophyllene and humulene and alpha-copaene. In comparison with heated juices, HPP-treated samples could retain more volatile compounds such as linalool and geraniol similar to those present in fresh juice, whereas some volatiles such as alpha-terpinene and ketone class were apparently formed by thermal treatment. All processing operations produced juice that was not significantly different in the concentration of total volatiles. Practical Application: Pennywort juice is considered a nutraceutical drink for health benefits. Therefore, to preserve all aroma and active components in this juice, a nonthermal process such as ultra-high pressure should be a more appropriate technique for retention of its nutritive values than pasteurization and sterilization.

Optimization of Composition and Heat Treating of Die Steels for Extended Lifetime

DOE Office of Scientific and Technical Information (OSTI.GOV)

David Schwam; John F. Wallace; Quanyou Zhou

2002-01-30

An ''average'' die casting die costs fifty thousand dollars. A die used in making die cast aluminum engine blocks can cost well over one million dollars. These costs provide a strong incentive for extension of die life. While vacuum quenched Premium Grade H13 dies have become the most widely used in the United States, tool makers and die casters are constantly searching for new steels and heat treating procedures to extend die life. This project was undertaken to investigate the effects of composition and heat treating on die life and optimize these parameters.

Temperature of Heating and Cooling of Massive, Thin, and Wedge-Shaped Plates from Hard-to-Machine Steels During Their Grinding

NASA Astrophysics Data System (ADS)

Dement‧ev, V. B.; Ivanova, T. N.; Dolginov, A. M.

2017-01-01

Grinding of flat parts occurs by solid abrasive particles due to the physicomechanical process of deformation and to the action of a process liquid at high temperatures in a zone small in volume and difficult for observation. The rate of heating and cooling depends on the change in the intensity of the heat flux and in the velocity and time of action of the heat source. A study has been made of the regularities of the influence of each of these parameters on the depth and character of structural transformations during the grinding of flat parts from hard-to-machine steels. A procedure to calculate temperature in grinding massive, thin, and wedge-shaped parts has been developed with account taken of the geometric and thermophysical parameters of the tool and the treated part, and also of cutting regimes. The procedure can be used as a constituent part in developing a system for automatic design of the technological process of grinding of flat surfaces. A relationship between the temperature in the grinding zone and the regimes of treatment has been established which makes it possible to control the quality of the surface layer of massive, thin, and wedge-shaped plates from hard-to-machine steels. The rational boundaries of shift of cutting regimes have been determined.

Antigenicity of Anisakis simplex s.s. L3 in parasitized fish after heating conditions used in the canning processing.

PubMed

Tejada, Margarita; Olivares, Fabiola; de las Heras, Cristina; Careche, Mercedes; Solas, María Teresa; García, María Luisa; Fernandez, Agustín; Mendizábal, Angel; Navas, Alfonso; Rodríguez-Mahillo, Ana Isabel; González-Muñoz, Miguel

2015-03-30

Some technological and food processing treatments applied to parasitized fish kill the Anisakis larvae and prevent infection and sensitization of consumers. However, residual allergenic activity of parasite allergens has been shown. The aim here was to study the effect of different heat treatments used in the fish canning processing industry on the antigen recognition of Anisakis L3. Bigeye tuna (Thunnus obesus) and yellowfin tuna (Thunnus albacares) were experimentally infected with live L3 Anisakis. After 48 h at 5 ± 1 °C, brine was added to the muscle, which was then canned raw (live larvae) or heated (90 °C, 30 min) (dead larvae) and treated at 113 °C for 60 min or at 115 °C for 90 min. Anisakis antigens and Ani s 4 were detected with anti-crude extract and anti-Ani s 4 antisera respectively. Ani s 4 decreased in all lots, but the muscle retained part of the allergenicity irrespective of the canning method, as observed by immunohistochemistry. Dot blot analysis showed a high loss of Ani s 4 recognition after canning, but residual antigenicity was present. The results indicate that heat treatment for sterilization under the conditions studied produces a decrease in Ani s 4 and suggest a potential exposure risk for Anisakis-sensitized patients. © 2014 Society of Chemical Industry.

Effective PCR detection of animal species in highly processed animal byproducts and compound feeds.

PubMed

Fumière, Olivier; Dubois, Marc; Baeten, Vincent; von Holst, Christoph; Berben, Gilbert

2006-07-01

In this paper we present a polymerase chain reaction (PCR)-based method for detecting meat and bone meal (MBM) in compound feedingstuffs. By choosing adequate DNA targets from an appropriate localisation in the genome, the real-time PCR method developed here proved to be robust to severe heat treatment of the MBM, showing high sensitivity in the detection of MBM. The method developed here permits the specific detection of processed pig and cattle materials treated at 134 degrees C in various feed matrices down to a limit of detection of about 0.1%. This technique has also been successfully applied to well-characterised MBM samples heated to as high as 141 degrees C, as well as to various blind feed samples with very low MBM contents. Finally, the method also passed several official European ring trials.

Effects of Post-Weld Heat Treatment on the Mechanical Properties of Similar- and Dissimilar-Alloy Friction Stir Welded Blanks

NASA Astrophysics Data System (ADS)

Zadpoor, Amir Abbas; Sinke, Jos

2011-01-01

Friction stir welding is a solid state joining process with relatively low welding temperatures. Nevertheless, the mechanical properties of friction stir welded blanks are degraded after welding. Indeed, both strength and ductility of the welds are decreased after welding. Often, the resulting friction stir welded blanks need to be formed to their final structural shape. Therefore, the formability of friction stir welded blanks is of primary importance in the manufacturing of structural parts. This paper studies how the mechanical properties and particularly formability of friction stir welded blanks can be improved by applying a post weld heat treatment. Two aluminum alloys from 2000 and 7000 series, namely 2024-T3 and 7075-T6, are selected for the study. The sheet thickness of both materials is 2,0 mm. The selected alloys are welded in three configurations: 2024-T3 and 2024-T3, 7075-T6 and 7075-T6, and 2024-T3 and 7075-T6. The resulting welds are naturally aged for a few months. Three sets of standard dog bone shape tensile test specimens are then machined from the welds. The first set of the specimens is tested without any heat treatment. The second set of the specimens is solution heat treated and quenched before testing. The third set of the specimens is solution heat treated, quenched, and naturally aged for a week before testing. The mechanical properties of the three different sets of specimens are compared with each other. It is shown that careful selection of post weld heat-treatment can greatly improve the formability of friction stir welded blanks.

Bone bonding bioactivity of Ti metal and Ti-Zr-Nb-Ta alloys with Ca ions incorporated on their surfaces by simple chemical and heat treatments.

PubMed

Fukuda, A; Takemoto, M; Saito, T; Fujibayashi, S; Neo, M; Yamaguchi, S; Kizuki, T; Matsushita, T; Niinomi, M; Kokubo, T; Nakamura, T

2011-03-01

Ti15Zr4Nb4Ta and Ti29Nb13Ta4.6Zr, which do not contain the potentially cytotoxic elements V and Al, represent a new generation of alloys with improved corrosion resistance, mechanical properties, and cytocompatibility. Recently it has become possible for the apatite forming ability of these alloys to be ascertained by treatment with alkali, CaCl2, heat, and water (ACaHW). In order to confirm the actual in vivo bioactivity of commercially pure titanium (cp-Ti) and these alloys after subjecting them to ACaHW treatment at different temperatures, the bone bonding strength of implants made from these materials was evaluated. The failure load between implant and bone was measured for treated and untreated plates at 4, 8, 16, and 26 weeks after implantation in rabbit tibia. The untreated implants showed almost no bonding, whereas all treated implants showed successful bonding by 4 weeks, and the failure load subsequently increased with time. This suggests that a simple and economical ACaHW treatment could successfully be used to impart bone bonding bioactivity to Ti metal and Ti-Zr-Nb-Ta alloys in vivo. In particular, implants heat treated at 700 °C exhibited significantly greater bone bonding strength, as well as augmented in vitro apatite formation, in comparison with those treated at 600 °C. Thus, with this improved bioactive treatment process these advantageous Ti-Zr-Nb-Ta alloys can serve as useful candidates for orthopedic devices. Copyright © 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Kinetics of the melting front movement in process of centrifugal induction surfacing of powder material with nanoscale modificaters

NASA Astrophysics Data System (ADS)

Sasnouski, I.; Kurylionak, A.

2018-03-01

For solving the problem of improving the powder coatings modified by nanostructure components obtained by induction surfacing method tribological characteristics it is necessary to study the kinetics of the powdered layer melting and define the minimum time of melting. For powdered layer predetermined temperature maintenance at sintering mode stage it is required to determine the temperature difference through blank thickness of the for one hundred-day of the define the warm-up swing on of the stocking up by solving the thermal conductivity stationary problem for quill (hollow) cylinder with internal heat source. Herewith, since in practice thickness of the cylinder wall is much less then its diameter and the temperature difference is comparatively small, the thermal conductivity dependence upon the temperature can be treated as negligible. As it was shown by our previous studies, in the induction heating process under powdered material centrifugal surfacing (i.e. before achieving the melting temperature) the temperature distribution in powdered layer thickness may be considered even. Hereinafter, considering the blank part induction heating process quasi-stationarity under Fo big values, it is possible to consider its internal surface heating as developing with constant velocity. As a result of development the melting front movement mathematical model in a powdered material with nanostructure modifiers the minimum surfacing time is defined. It allows to minimize negative impact of thermal influence on formation of applied coating structure, to raise productivity of the process, to lower power inputs and to ensure saving of nonferrous and high alloys by reducing the allowance for machining. The difference of developed mathematical model of melting front movement from previously known is that the surface temperature from which the heat transfer occures is a variable and varies with a time after the linear law.

Microwave-driven asbestos treatment and its scale-up for use after natural disasters.

PubMed

Horikoshi, Satoshi; Sumi, Takuya; Ito, Shigeyuki; Dillert, Ralf; Kashimura, Keiichiro; Yoshikawa, Noboru; Sato, Motoyasu; Shinohara, Naoki

2014-06-17

Asbestos-containing debris generated by the tsunami after the Great East Japan Earthquake of March 11, 2011, was processed by microwave heating. The analysis of the treated samples employing thermo gravimetry, differential thermal analysis, X-ray diffractometry, scanning electron microscopy, and phase-contrast microscopy revealed the rapid detoxification of the waste by conversion of the asbestos fibers to a nonfibrous glassy material. The detoxification by the microwave method occurred at a significantly lower processing temperature than the thermal methods actually established for the treatment of asbestos-containing waste. The lower treatment temperature is considered to be a consequence of the microwave penetration depth into the waste material and the increased intensity of the microwave electric field in the gaps between the asbestos fibers resulting in a rapid heating of the fibers inside the debris. A continuous treatment plant having a capacity of 2000 kg day(-1) of asbestos-containing waste was built in the area affected by the earthquake disaster. This treatment plant consists of a rotary kiln to burn the combustible waste (wood) and a microwave rotary kiln to treat asbestos-containing inorganic materials. The hot flue gas produced by the combustion of wood is introduced into the connected microwave rotary kiln to increase the energy efficiency of the combined process. Successful operation of this combined device with regard to asbestos decomposition is demonstrated.

Process for treating fission waste

DOEpatents

Rohrmann, Charles A.; Wick, Oswald J.

1983-01-01

A method is described for the treatment of fission waste. A glass forming agent, a metal oxide, and a reducing agent are mixed with the fission waste and the mixture is heated. After melting, the mixture separates into a glass phase and a metal phase. The glass phase may be used to safely store the fission waste, while the metal phase contains noble metals recovered from the fission waste.

Correction of small imperfections on white glazed china surfaces by laser radiation

NASA Astrophysics Data System (ADS)

Képíró, I.; Osvay, K.; Divall, M.

2007-07-01

A laser-assisted technique has been developed for correction of small diameter (1 mm) and shallow (0.5 mm) imperfections on the surface of gloss fired porcelain. To study the physics and establish the important parameters, artificially made holes in a porcelain sample have been first filled with correction material, then covered with raw glaze and treated by a pulsed, 7 kHz repetition rate CO 2 laser at 10.6 μm. The modification of the surface and the surrounding area have been quantified and studied with a large range of parameters of incident laser power (1-10 W), width of the laser pulses (10-125 μs) and duration of laser heating (60-480 s). Although the shine of the treated area, defined as the distribution of micro-droplets on the surface, is very similar to the untreated surfaces, the surroundings of the treated area usually show cracks. The measurement of both the spatial temperature distribution and the temporal cooling rate of the treated surface has revealed that a simple melting process always results in high gradient temperature distribution within the irradiated zone. Its inhomogeneous and fast cooling always generate at least micro-cracks on the surface within a few seconds after the laser was turned off. The duration and intensity of the laser irradiation have been then optimized in order to achieve the fastest possible melting of the surface, but without producing such high temperature gradients. To eliminate the cracks, more elaborated pre-heating and slowed-cooling-rate processes have been tried with prosperous results. These achievements complete our previous study, making possible to repair the most common surface imperfections and holes of gloss fired china samples.

Mice receiving infrared irradiation have a higher survival rate under forced swimming in cold.

PubMed

Tsai, Jui-Feng

2009-10-01

To explore the effect of infrared (IR) irradiation on the survival rates of mice under forced swimming in cold conditions. IR irradiation has been found to be beneficial for wound healing, tumor reduction, pain relief, and even against depression. However, whether the antidepressant effect of IR irradiation came from heat has remained unanswered. The goals of the study were originally aimed at using an animal model for depression to understand the relationship between the antidepressant effect of IR irradiation and hyperthermia as well as seasonality. Forty-four mice were housed in cages in a room subject to the outdoor temperature, and randomly assigned to the IR-treated group (n = 15), the heat-treated group (n = 14), and the control group (n = 15) during winter. The mice of the IR-treated group received whole-body IR irradiation for 60 min daily, while the heat-treated group received heat diffusion to reach the same temperature level. The control group received neither IR nor heat. All groups of mice underwent a forced swimming test weekly. Incidentally, two episodes of cold current occurred during the study period, and some mice died. The survival rates were compared pairwise against the control. The IR-treated group had a significantly reduced relative risk (p = 0.013) when compared with the control group, while the heat-treated group did not show any significant reduction (p = 0.087). There was no significant difference in body temperatures of the three groups before and after the irradiation. IR irradiation resulted in a significantly higher survival rate for mice that were concurrently subjected to cold and a forced swimming test. This result may be beyond the thermal effect.

A diet based on high-heat-treated foods promotes risk factors for diabetes mellitus and cardiovascular diseases.

PubMed

Birlouez-Aragon, Inès; Saavedra, Giselle; Tessier, Frédéric J; Galinier, Anne; Ait-Ameur, Lamia; Lacoste, Florence; Niamba, Claude-Narcisse; Alt, Nadja; Somoza, Veronika; Lecerf, Jean-Michel

2010-05-01

The modern Western lifestyle is characterized by the consumption of high-heat-treated foods because of their characteristic taste and flavor. However, it has been shown that treating food at high temperatures can generate potentially harmful compounds that promote inflammation and cardiovascular disease in subjects with diabetes. The aim of this study was to determine whether high-heat-treated foods also pose a risk for healthy subjects. A randomized, crossover, diet-controlled intervention trial with 62 volunteers was designed to compare the potential metabolic effects of 2 diets, one that was based on mild steam cooking and another that was based on high-temperature cooking. These 2 diets differed mainly in their contents of Maillard reaction products (MRPs). MRPs were assessed in the diet and in subjects' feces, blood, and urine samples, with N(epsilon)-carboxymethyllysine as an indicator of MRPs. Biological indicators of glucose and lipid metabolism as well as oxidative stress were analyzed in subjects after 1 mo on each diet. In comparison with the steamed diet, 1 mo of consuming the high-heat-treated diet induced significantly lower insulin sensitivity and plasma concentrations of long-chain n-3 (omega-3) fatty acids and vitamins C and E [-17% (P < 0.002), -13% (P < 0.0001), and -8% (P < 0.01), respectively]. However, concentrations of plasma cholesterol and triglycerides increased [+5% (P < 0.01) and +9% (P < 0.01), respectively]. A diet that is based on high-heat-treated foods increases markers associated with an enhanced risk of type 2 diabetes and cardiovascular diseases in healthy people. Replacing high-heat-treatment techniques by mild cooking techniques may help to positively modulate biomarkers associated with an increased risk of diabetes mellitus and cardiovascular diseases.

Elucidating the Relations Between Monotonic and Fatigue Properties of Laser Powder Bed Fusion Stainless Steel 316L

NASA Astrophysics Data System (ADS)

Zhang, Meng; Sun, Chen-Nan; Zhang, Xiang; Goh, Phoi Chin; Wei, Jun; Li, Hua; Hardacre, David

2018-03-01

The laser powder bed fusion (L-PBF) technique builds parts with higher static strength than the conventional manufacturing processes through the formation of ultrafine grains. However, its fatigue endurance strength σ f does not match the increased monotonic tensile strength σ b. This work examines the monotonic and fatigue properties of as-built and heat-treated L-PBF stainless steel 316L. It was found that the general linear relation σ f = mσ b for describing conventional ferrous materials is not applicable to L-PBF parts because of the influence of porosity. Instead, the ductility parameter correlated linearly with fatigue strength and was proposed as the new fatigue assessment criterion for porous L-PBF parts. Annealed parts conformed to the strength-ductility trade-off. Fatigue resistance was reduced at short lives, but the effect was partially offset by the higher ductility such that comparing with an as-built part of equivalent monotonic strength, the heat-treated parts were more fatigue resistant.

Spectroscopic properties in Er3+-doped germanotellurite glasses and glass ceramics for mid-infrared laser materials.

PubMed

Kang, Shiliang; Xiao, Xiudi; Pan, Qiwen; Chen, Dongdan; Qiu, Jianrong; Dong, Guoping

2017-03-07

Transparent Er 3+ -doped germanotellurite glass ceramics (GCs) with variable Te/Ge ratio were prepared by controllable heat-treated process. X-ray diffraction (XRD) and transmission electron microscope (TEM) confirmed the formation of nanocrystals in glass matrix. Raman spectra were used to investigate the evolution of glass structure and photon energy. Fourier transform infrared (FTIR) spectra were introduced to characterize the change of hydroxyl group (OH - ) content. Enhanced 2.7 μm emission was achieved from Er 3+ -doped GCs upon excitation with a 980 nm laser diode (LD), and the influence of GeO 2 concentration and heat-treated temperature on the spectroscopic properties were also discussed in detail. It is found that the present Er 3+ -doped GC possesses large stimulated emission cross section at around 2.7 μm (0.85 × 10 -20  cm 2 ). The advantageous spectroscopic characteristics suggest that the obtained GC may be a promising material for mid-infrared fiber lasers.

Spectroscopic properties in Er3+-doped germanotellurite glasses and glass ceramics for mid-infrared laser materials

PubMed Central

Kang, Shiliang; Xiao, Xiudi; Pan, Qiwen; Chen, Dongdan; Qiu, Jianrong; Dong, Guoping

2017-01-01

Transparent Er3+-doped germanotellurite glass ceramics (GCs) with variable Te/Ge ratio were prepared by controllable heat-treated process. X-ray diffraction (XRD) and transmission electron microscope (TEM) confirmed the formation of nanocrystals in glass matrix. Raman spectra were used to investigate the evolution of glass structure and photon energy. Fourier transform infrared (FTIR) spectra were introduced to characterize the change of hydroxyl group (OH−) content. Enhanced 2.7 μm emission was achieved from Er3+-doped GCs upon excitation with a 980 nm laser diode (LD), and the influence of GeO2 concentration and heat-treated temperature on the spectroscopic properties were also discussed in detail. It is found that the present Er3+-doped GC possesses large stimulated emission cross section at around 2.7 μm (0.85 × 10−20 cm2). The advantageous spectroscopic characteristics suggest that the obtained GC may be a promising material for mid-infrared fiber lasers. PMID:28266570

Development of a model and computer code to describe solar grade silicon production processes

NASA Technical Reports Server (NTRS)

Gould, R. K.; Srivastava, R.

1979-01-01

Two computer codes were developed for describing flow reactors in which high purity, solar grade silicon is produced via reduction of gaseous silicon halides. The first is the CHEMPART code, an axisymmetric, marching code which treats two phase flows with models describing detailed gas-phase chemical kinetics, particle formation, and particle growth. It can be used to described flow reactors in which reactants, mix, react, and form a particulate phase. Detailed radial gas-phase composition, temperature, velocity, and particle size distribution profiles are computed. Also, deposition of heat, momentum, and mass (either particulate or vapor) on reactor walls is described. The second code is a modified version of the GENMIX boundary layer code which is used to compute rates of heat, momentum, and mass transfer to the reactor walls. This code lacks the detailed chemical kinetics and particle handling features of the CHEMPART code but has the virtue of running much more rapidly than CHEMPART, while treating the phenomena occurring in the boundary layer in more detail.

Heat pipe dynamic behavior

NASA Technical Reports Server (NTRS)

Issacci, F.; Roche, G. L.; Klein, D. B.; Catton, I.

1988-01-01

The vapor flow in a heat pipe was mathematically modeled and the equations governing the transient behavior of the core were solved numerically. The modeled vapor flow is transient, axisymmetric (or two-dimensional) compressible viscous flow in a closed chamber. The two methods of solution are described. The more promising method failed (a mixed Galerkin finite difference method) whereas a more common finite difference method was successful. Preliminary results are presented showing that multi-dimensional flows need to be treated. A model of the liquid phase of a high temperature heat pipe was developed. The model is intended to be coupled to a vapor phase model for the complete solution of the heat pipe problem. The mathematical equations are formulated consistent with physical processes while allowing a computationally efficient solution. The model simulates time dependent characteristics of concern to the liquid phase including input phase change, output heat fluxes, liquid temperatures, container temperatures, liquid velocities, and liquid pressure. Preliminary results were obtained for two heat pipe startup cases. The heat pipe studied used lithium as the working fluid and an annular wick configuration. Recommendations for implementation based on the results obtained are presented. Experimental studies were initiated using a rectangular heat pipe. Both twin beam laser holography and laser Doppler anemometry were investigated. Preliminary experiments were completed and results are reported.

Effect of heat treatment on quality, thermal and pasting properties of sweet potato starch during yearlong storage.

PubMed

Hu, Wenzhong; Jiang, Aili; Jin, Liming; Liu, Chenghui; Tian, Mixia; Wang, Yanying

2011-06-01

Proper postharvest handling and storage of sweet potato is an important link in the chain from producer to consumer or manufacturing industry. Heat treatments have been used as a non-chemical means to modify the postharvest quality and reduce pathogen levels and disease development of a wide variety of horticultural products. The objective of this study was to investigate the effects of hot water treatment (HWT) on the quality, gelatinisation enthalpy and pasting properties of sweet potato starch during long-term storage. The weight loss, sprouting, spoilage and sugar content of sweet potato were also determined. HWT significantly inhibited the sprouting and decay of sweet potato during the storage period. There were no significant differences (P < 0.05) in the pasting properties and onset (T(O)), peak (T(P)) and endset (T(E)) temperatures of gelatinisation of sweet potato starch among all treatments, especially between heat-treated and non-heat-treated samples. HWT also had no significant impact on the quality of the internal components of the roots. Less than 4% of the yearlong-stored roots were discarded owing to spoilage. HWT supplied a lethal dose of heat to surface pathogens and black spot without damaging the nutritional and processing qualities of sweet potato. HWT was an effective method to reduce root sprouting and deterioration without significant impact on the quality of the internal components of sweet potato. This novel technique will open a new avenue to extend the storage life of sweet potato with good quality and minimal waste. Copyright © 2011 Society of Chemical Industry.

Comparison of the protection effectiveness of acrylic polyurethane coatings containing bark extracts on three heat-treated North American wood species: Surface degradation

NASA Astrophysics Data System (ADS)

Kocaefe, Duygu; Saha, Sudeshna

2012-04-01

High temperature heat-treatment of wood is a very valuable technique which improves many properties (biological durability, dimensional stability, thermal insulating characteristics) of natural wood. Also, it changes the natural color of wood to a very attractive dark brown color. Unfortunately, this color is not stable if left unprotected in external environment and turns to gray or white depending on the wood species. To overcome this problem, acrylic polyurethane coatings are applied on heat-treated wood to delay surface degradations (color change, loss of gloss, and chemical modifications) during aging. The acrylic polyurethane coatings which have high resistance against aging are further modified by adding bark extracts and/or lignin stabilizer to enhance their effectiveness in preventing the wood aging behavior. The aging characteristic of this coating is compared with acrylic polyurethane combined with commercially available organic UV stabilizers. In this study, their performance on three heat-treated North American wood species (jack pine, quaking aspen and white birch) are compared under accelerated aging conditions. Both the color change data and visual assessment indicate improvement in protective characteristic of acrylic polyurethane when bark extracts and lignin stabilizer are used in place of commercially available UV stabilizer. The results showed that although acrylic polyurethane with bark extracts and lignin stabilizer was more efficient compared to acrylic polyurethane with organic UV stabilizers in protecting heat-treated jack pine, it failed to protect heat-treated aspen and birch effectively after 672 h of accelerated aging. This degradation was not due to the coating adhesion loss or coating degradation during accelerated aging; rather, it was due to the significant degradation of heat-treated aspen and birch surface beneath this coating. The XPS results revealed formation of carbonyl photoproducts after aging on the coated surfaces and chain scission of Csbnd N of urethane linkages.

Pechini process-derived tin oxide and tin oxide-graphite composites for lithium-ion batteries

NASA Astrophysics Data System (ADS)

Zhang, R.; Lee, Jim Y.; Liu, Z. L.

The Pechini process [Ceram. Bull. 68 (1989) 1002] is used to obtain fine tin oxide powders that reduce the specific volume change in Li + insertion and extraction reactions. The suitability of these tin oxides as active materials for negative electrodes in lithium-ion batteries is investigated. From elemental analysis, it is found that the templating polymer network is almost completely obliterated after heating at 500 °C. The best tin oxide does not exhibit extensive crystallization of tin atoms even after 30 cycles of alloying and de-alloying reactions with Li. The structure and the specific capacity of the oxides are dependent on the heat treatment and remnants of the polymeric CH network can impose an unfavorable outcome. A capacity of 600 mAh g -1, which is unchanged for 30 cycles, can be obtained from tin oxide heat treated at 1000 °C. Composites of graphite and SnO 2 are also prepared and exhibit synergistic interactions between graphite and tin oxide which are similar to those reported previously [Electrochem. Solid State Lett. 3 (2000) 167].

Antioxidant activity of protein hydrolysates from raw and heat-treated yellow string beans (Phaseolus vulgaris L.).

PubMed

Karaś, Monika; Jakubczyk, Anna; Szymanowska, Urszula; Materska, Małgorzata; Zielińska, Ewelina

2014-01-01

Nowadays, legume plants have been considered not only a source of valuable proteins necessary for the proper functioning and growth of the body but also a source of bioactive compounds such as bioactive peptides, that may be beneficial to human health and protect against negative change in food. The aim of this study was to investigate the effect of heat treatment on the release of antioxidant peptides obtained by hydrolysis of the yellow string beans protein. The antioxidant properties of the hydrolysates were evaluated through free radical scavenging activities (DPPH and ABTS) and inhibition of iron activities (chelation of Fe2+). The results show that the heat treatment had influence on both increased peptides content and antioxidant activity after pepsin hydrolysis of string bean protein. The peptides content after protein hydrolysis derived from raw and heat treated beans were noted 2.10 and 2.50 mg·ml-1, respectively. The hydrolysates obtained from raw (PHR) and heat treated (PHT) beans showed better antioxidant properties than protein isolates (PIR and PIT). Moreover, the hydrolysates obtained from heat treated beans showed the higher ability to scavenge DPPH• (46.12%) and ABTS+• (92.32%) than obtained from raw beans (38.02% and 88.24%, correspondingly). The IC50 value for Fe2+ chelating ability for pepsin hydrolysates obtained from raw and heat treatment beans were noted 0.81 and 0.19 mg·ml-1, respectively. In conclusion, the results of this study showed that the heat treatment string beans caused increase in the antioxidant activities of peptide-rich hydrolysates.

Effect of heating strategy on power consumption and performance of a pilot plant anaerobic digester.

PubMed

Espinosa-Solares, Teodoro; Valle-Guadarrama, Salvador; Bombardiere, John; Domaschko, Max; Easter, Michael

2009-05-01

The effect of heating strategy on power consumption and performance of a pilot plant anaerobic digester treating chicken litter, under thermophilic conditions, has been studied. Heating strategy was evaluated using three different spans (0.2 degrees C, 0.6 degrees C, and 1.0 degree C) for triggering the temperature control system from target temperature (56.7 degrees C). The hydraulic retention time in the pilot plant digester was in the range of 32 to 37 days, varying the total solids concentration fed from 5% to 6%. The results showed that under the experimental conditions, heating was the most energy-demanding process with 95.5% of the energy used. Increments up to 7.5% and 3.8%, respectively, on mechanical and heating power consumption, were observed as the span, for triggering the temperature control system from target temperature, was increased. Under the experimental conditions studied here, an increment of 30.6% on the global biodigester performance index was observed when a span of 1.0 degree C was compared to the one of 0.2 degrees C.

Microwave processing of honey negatively affects honey antibacterial activity by inactivation of bee-derived glucose oxidase and defensin-1.

PubMed

Bucekova, Marcela; Juricova, Valeria; Monton, Enrique; Martinotti, Simona; Ranzato, Elia; Majtan, Juraj

2018-02-01

Microwave (MW) thermal heating has been proposed as an efficient method for honey liquefaction, while maintaining honey quality criteria. However, little is known about the effects of MW thermal heating on honey antibacterial activity. In this study, we aimed to determine the effects of MW heating on the antibacterial activity of raw rapeseed honeys against Pseudomonas aeruginosa and Staphylococcus aureus, with a particular focus on two major bee-derived antibacterial components, defensin-1 and hydrogen peroxide (H 2 O 2 ). Our results demonstrated that MW thermal heating completely abolished honey antibacterial activity whereas conventional thermal treatment at 45 and 55°C did not affect the antibacterial activity of honey samples. A significant decrease in both glucose oxidase activity and H 2 O 2 production as well as defensin-1 amount was observed in MW-treated samples. Given that defensin-1 and H 2 O 2 are regular antibacterial components of all honeys, MW heating may have similar negative effects on every type of crystallized/liquid honey. Copyright © 2017 Elsevier Ltd. All rights reserved.

[Application HTST-heating of the mash and its influence on the aroma composition during the production of apple brandy (author's transl)].

PubMed

Schreier, P; Drawert, F; Steiger, G

1978-08-18

The influence of HTST-heating of the mash aroma composition during production of apply brandy has been investigated by means of gas chromatography and coupled gas chromatography--mass spectrometry. Starting from the apple aroma the changes in aroma components were studied quantitatively during the conventional production (without enzyme inhibition) as well as after HTST-heating (enzyme inactivation) of the mash. For this purpose 98 aroma compounds were determined in the course of mash production, fermentation and distillation. When employing HTST-heating the original aroma components of the apple particularly the fruit esters were present in appreciably higher concentrations in the mash as well as in the distillate than with the conventional production method. Simultaneously HTST-heating reduced the secondary aroma substances in mash and distillate which are formed with the conventional method by enzymatic-oxidative processes. In the unaged apple brandy obtained from HTST-treated mash lower amounts of lactates and higher concentrations of acetals were found compared with the conventionally produced distillate.

Automated Array Assembly, Phase 2

NASA Technical Reports Server (NTRS)

Carbajal, B. G.

1979-01-01

The Automated Array Assembly Task, Phase 2 of the Low Cost Silicon Solar Array Project is a process development task. The contract provides for the fabrication of modules from large area tandem junction cells (TJC). During this quarter, effort was focused on the design of a large area, approximately 36 sq cm, TJC and process verification runs. The large area TJC design was optimized for minimum I squared R power losses. In the TJM activity, the cell-module interfaces were defined, module substrates were formed and heat treated and clad metal interconnect strips were fabricated.

Microwave Pasteurization of Cooked Pasta: Effect of Process Parameters on Texture and Quality for Heat-and-Eat and Ready-to-Eat Meals.

PubMed

Joyner Melito, Helen S; Jones, Kari E; Rasco, Barbara A

2016-06-01

Pasta presents a challenge to microwave processing due to its unique cooking requirements. The objective of this study was to determine the effects of microwave processing on pasta physicochemical and mechanical properties. Fettuccine pasta was parboiled for selected times, then pasteurized using a Microwave Assisted Pasteurization System and stored under refrigeration for 1 wk. Samples were analyzed using microscopy, mechanical testing, and chemical analyses after storage. While no significant differences were observed for free amylose among fresh samples, samples parboiled for ≤6 min had significantly higher free amylose, suggesting reduced starch retrogradation. Increased heat treatment increased degree of protein polymerization, observed in microstructures as increased gluten strand thickness and network density. Firmness and extensibility increased with increased parboil time; however, extension data indicated an overall weakening of microwave-treated pasta regardless of total cooking time. Overall, microwave pasteurization was shown to be a viable cooking method for pasta. © 2016 Institute of Food Technologists®

Precipitation phenomena in and electrical resistivity of high-temperature treated langatate (La3Ta0.5Ga5.5O14).

PubMed

Yaokawa, Ritsuko; Kimura, Hiromitsu; Aota, Katsumi; Uda, Satoshi

2011-06-01

La(3)Ta(0.5)Ga(5.5)O(14) (LTG) single crystals, which have no phase transition up to the melting point, were heat-treated in air at temperatures from 1000°C to 1450°C for 10 h. LaTaO(4) (LT) and LaGaO(3) (LG), which coexist with LTG in the three-phase region on the Ga-poor side, precipitated on the surface of the crystal for heat treatments above 1300°C because of Ga evaporation during the heat treatment. The Ga-poor state near the surface of the 1450°C heat-treated specimen was confirmed by electron probe micro-analysis measurements. The electrical resistivity of LTG single crystals decreased by heat treatment in the range of 1000°C to 1200°C for 10 h in air, where no precipitation was observed, whereas the resistivity increased with heat treatment over 1400°C for 10 h in air. The electrical resistivity of the Ga-poor surface region was higher than that of the interior.

Effect of Heat Treatment Parameters on the Microstructure and Properties of Inconel-625 Superalloy

NASA Astrophysics Data System (ADS)

Sukumaran, Arjun; Gupta, R. K.; Anil Kumar, V.

2017-07-01

Inconel-625 is a solid solution-strengthened alloy used for long-duration applications at high temperatures and moderate stresses. Different heat treatment cycles (temperatures of 625-1025 °C and time of 2-6 h) have been studied to obtain optimum mechanical properties suitable for a specific application. It has been observed that room temperature strength and, hardness decreased and ductility increased with increase in heat treatment temperature. The rate of change of these properties is found to be moderate for the samples heat-treated up to 850 °C, and thereafter, it increases rapidly. It is attributed to the microstructural changes like dissolution of carbides, recrystallization and grain growth. Microstructures are found to be predominantly single-phase austenitic with the presence of fine alloy carbides. The presence of twins is observed in samples heat-treated at lower temperature, which act as nucleation sites for recrystallization at 775 °C. Beyond 850 °C, the role of carbides present in the matrix is subsided by the coarsening of recrystallized grains and finally at 1025 °C, significant dissolution of carbide results in substantial reduction in strength and increase in ductility. Elongation to an extent of >71% has been obtained in sample heat-treated at 1025 °C indicating excellent tendency for cold workability. Failure of heat-treated specimens is found to be mainly due to carbide particle-matrix decohesion which acts as locations for crack initiation.

The heat treatment of duralumin

NASA Technical Reports Server (NTRS)

Nelson, WM

1927-01-01

When certain light aluminum alloys are heat-treated, quenched and aged, there is considerable improvement in their tensile properties. This paper presents different methods of accomplishing these heat treatments.

Effects of Pressure, Temperature, Treatment Time, and Storage on Rheological, Textural, and Structural Properties of Heat-Induced Chickpea Gels

PubMed Central

Alvarez, María Dolores; Fuentes, Raúl; Canet, Wenceslao

2015-01-01

Pressure-induced gelatinization of chickpea flour (CF) was studied in combination with subsequent temperature-induced gelatinization. CF slurries (with 1:5 flour-to-water ratio) and CF in powder form were treated with high hydrostatic pressure (HHP), temperature (T), and treatment time (t) at three levels (200, 400, 600 MPa; 10, 25, 50 °C; 5, 15, 25 min). In order to investigate the effect of storage (S), half of the HHP-treated CF slurries were immediately analyzed for changes in oscillatory rheological properties under isothermal heating at 75 °C for 15 min followed by cooling to 25 °C. The other half of the HHP-treated CF slurries were refrigerated (at 4 °C) for one week and subsequently analyzed for changes in oscillatory properties under the same heating conditions as the unrefrigerated samples. HHP-treated CF in powder form was analyzed for changes in textural properties of heat-induced CF gels under isothermal heating at 90 °C for 5 min and subsequent cooling to 25 °C. Structural changes during gelatinization were investigated using microscopy. Pressure had a more significant effect on rheological and textural properties, followed by T and treatment t (in that order). Gel aging in HHP-treated CF slurries during storage was supported by rheological measurements. PMID:28231191

Sensing the heat with TRPM3.

PubMed

Vriens, Joris; Voets, Thomas

2018-05-01

Heat sensation, the ability to detect warm and noxious temperatures, is an ancient and indispensable sensory process. Noxious temperatures can have detrimental effects on the physiology and integrity of cells, and therefore, the detection of environmental hot temperatures is absolutely crucial for survival. Temperature-sensitive ion channels, which conduct ions in a highly temperature-dependent manner, have been put forward as molecular thermometers expressed at the endings of sensory neurons. In particular, several temperature-sensitive members of the transient receptor potential (TRP) superfamily of ion channels have been identified, and a multitude of in vivo studies have shown that the capsaicin-sensitive TRPV1 channel plays a key role as a noxious heat sensor. However, Trpv1-deficient mice display a residual heat sensitivity suggesting the existence of additional heat sensor(s). In this chapter, we provide evidence for the role of the non-selective calcium-permeable TRPM3 ion channel as an additional heat sensor that acts independently of TRPV1, and give an update of the modulation of this channel by various molecular mechanisms. Finally, we compare antagonists of TRPM3 to specific blockers of TRPV1 as potential analgesic drugs to treat pathological pain.

Radio-frequency heating to inactivate Salmonella Typhimurium and Escherichia coli O157:H7 on black and red pepper spice.

PubMed

Kim, Sung-Youn; Sagong, Hun-Gu; Choi, Sang Ho; Ryu, Sangryeol; Kang, Dong-Hyun

2012-02-01

The efficacy of radio-frequency (RF) heating to inactivate Salmonella Typhimurium and Escherichia coli O157:H7 on black and red pepper spice was investigated. A 27.12 MHz RF heating system consisted of two parallel-plate electrodes was used, with the sample being placed between them. Black peppers (whole and ground) and red peppers (+ 16 mesh, -16 + 25 mesh, and -25 mesh) inoculated with S. Typhimurium and E. coli O157:H7 were treated with RF energy during 50s for black peppers and 40s for red peppers, and color change of samples was evaluated after treatment. RF heating for 50s resulted in 2.80 to 4.29 log CFU/g reductions of S. Typhimurium and E. coli O157:H7 in black peppers and RF heating of red peppers for 40s reduced pathogens by 3.38 log CFU/g to more than 5 log CFU/g (below the detection limit) without affecting the color quality change. The results suggest that RF heating has the potential for novel thermal process to control foodborne pathogens in spice. Copyright © 2011 Elsevier B.V. All rights reserved.

Effects of Heat Treatment on Tribological Behavior of Electroless Ni-B Coating at Elevated Temperatures

NASA Astrophysics Data System (ADS)

Mukhopadhyay, Arkadeb; Barman, Tapan Kumar; Sahoo, Prasanta

The present work investigates the effects of heat treatment on friction and wear behavior of electroless Ni-B coatings at elevated temperatures. Coating is deposited on AISI 1040 steel specimens and subjected to heat treatments at 350∘C, 400∘C and 450∘C. Coating characterization is done using scanning electron microscope, energy dispersive X-Ray analysis and X-Ray diffraction analysis. Improvement in microhardness is observed for the heat treated deposits. Further, the effect of heat treatment on the tribological behavior of the coatings at room temperature, 100∘C, 300∘C and 500∘C are analyzed on a pin-on-disc setup. Heat treatment at 350∘C causes a significant improvement in the tribological behavior at elevated temperatures. Higher heat treatment temperatures cause deterioration in the wear resistance and coefficient of friction. The wear mechanism at 100∘C is observed to be predominantly adhesive along with abrasion. While at 300∘C, abrasive wear is seen to be the governing wear phenomenon. Formation of mechanically mixed layers is noticed at both the test temperatures of 100∘C and 300∘C for the coatings heat treated at 400∘C and 450∘C test temperature. The predominant wear mechanisms at 500∘C are abrasive and fatigue for as-deposited and heat treated coatings, respectively.

Preparation of a Ammonia-Treated Lac Dye and Structure Elucidation of Its Main Component.

PubMed

Nishizaki, Yuzo; Ishizuki, Kyoko; Akiyama, Hiroshi; Tada, Atsuko; Sugimoto, Naoki; Sato, Kyoko

2016-01-01

Lac dye and cochineal extract contain laccaic acids and carminic acid as the main pigments, respectively. Both laccaic acids and carminic acid are anthraquinone derivatives. 4-Aminocarminic acid (acid-stable carmine), an illegal colorant, has been detected in several processed foods. 4-Aminocarminic acid is obtained by heating cochineal extract (carminic acid) in ammonia solution. We attempted to prepare ammonia-treated lac dye and to identify the structures of the main pigment components. Ammonia-treated lac dye showed acid stability similar to that of 4-aminocarminic acid. The structures of the main pigments in ammonia-treated lac dye were analyzed using LC/MS. One of the main pigments was isolated and identified as 4-aminolaccaic acid C using various NMR techniques, including 2D-INADEQUATE. These results indicated that ammonia-treatment of lac dye results in the generation of 4-aminolaccaic acids.

A gastrointestinal anti-infectious biotherapeutic agent: the heat-treated Lactobacillus LB

PubMed Central

Liévin-Le Moal, Vanessa

2016-01-01

Experimental in vitro and in vivo studies support the hypothesis that heat-treated, lyophilized Lactobacillus acidophilus LB cells and concentrated, neutralized spent culture medium conserve the variety of pharmacological, antimicrobial activities of the live probiotic strain against several infectious agents involved in well-established acute and persistent watery diarrhoea and gastritis. Heat-treated cells and heat-stable secreted molecules trigger multiple strain-specific activities explaining the therapeutic efficacy of L. acidophilus LB. This review discusses the current body of knowledge on the antimicrobial mechanisms of action exerted by L. acidophilus LB demonstrated in in vitro and in vivo experimental studies, and the evidence for the therapeutic efficacy of this anti-infectious biotherapeutic agent proved in randomized clinical trials for the treatment of acute and persistent watery diarrhoea associated with several intestinal infectious diseases in humans. PMID:26770268

Effects of heat treatment on oil-binding ability of rice flour.

PubMed

Tabara, Aya; Nakagawa, Mariko; Ushijima, Yuki; Matsunaga, Kotaro; Seguchi, Masaharu

2015-01-01

Heat-treated (120 °C for 120 min) rice flour showed high affinity to oil (oil-binding ability). This oil-binding ability could be observed by shaking the heat-treated rice flour (2.0 g), oil (4.0 mL), and water (20 mL) vigorously in a test tube, and the oil bound to the rice flour sank into the water. To examine the time-dependent levels of the oil-binding ability, rice flour was heat-treated at 120 °C for 10, 20, 40, 60, and 120 min, and the precipitated volume of oil/rice flour complex increased with an increase of the heating time. The oil-binding ability of the rice flour was not affected by the treatments with diethyl ether or boiled chloroform/methanol (2:1) solutions, which suggested no relationship to the oil in the rice flour, but was lost upon alkali (0.2% NaOH solution) or pepsin treatment, which suggested its relationship to the rice proteins.

Method of Heat Treating Aluminum-Lithium Alloy to Improve Formability

NASA Technical Reports Server (NTRS)

Russell, Carolyn Kurgan (Inventor); Chen, Po-Shou (Inventor)

2016-01-01

A method is provided for heat treating aluminum-lithium alloys to improve their formability. The alloy is heated to a first temperature, maintained at the first temperature for a first time period, heated at the conclusion of the first time period to a second temperature, maintained at the second temperature for a second time period, actively cooled at the conclusion of the second time period to a third temperature, maintained at the third temperature for a third time period, and then passively cooled at the conclusion of the third time period to room temperature.

Factors affecting sodium hypochlorite extraction of CCA from treated wood.

PubMed

Gezer, E D; Cooper, P A

2009-12-01

Significant amounts of chromated copper arsenate (CCA) treated wood products, such as utility poles and residential construction wood, remain in service. There is increasing public concern about environmental contamination from CCA-treated wood when it is removed from service for reuse or recycling, placed in landfills or burned in commercial incinerators. In this paper, we investigated the effects of time, temperature and sodium hypochlorite concentration on chromium oxidation and extraction of chromated copper arsenate from CCA-treated wood (Type C) removed from service. Of the conditions evaluated, reaction of milled wood with sodium hypochlorite for one hour at room temperature followed by heating at 75 degrees C for two hours gave the highest extraction efficiency. An average of 95% Cr, 99% Cu and 96% As could be removed from CCA-treated, milled wood by this process. Most of the extracted chromium was oxidized to the hexavalent state and could therefore be recycled in a CCA treating solution. Sodium hypochlorite extracting solutions could be reused several times to extract CCA components from additional treated wood samples.

Feeding heat-treated colostrum reduces morbidity in preweaned dairy calves

USDA-ARS?s Scientific Manuscript database

Previous studies have demonstrated that batch pasteurizers can be used on farms to heat-treat bovine colostrum at 60ºC for 60 minutes, resulting in a significant reduction in bacterial exposure to the calf while maintaining overall colostral Immunoglobulin G (IgG) concentrations. However, studies h...

Rapid heat treatment for anatase conversion of titania nanotube orthopedic surfaces

NASA Astrophysics Data System (ADS)

Bhosle, Sachin M.; Friedrich, Craig R.

2017-10-01

The amorphous to anatase transformation of anodized nanotubular titania surfaces has been studied by x-ray diffraction and transmission electron microscopy (TEM). A more rapid heat treatment for conversion of amorphous to crystalline anatase favorable for orthopedic implant applications was demonstrated. Nanotube titania surfaces were fabricated by electrochemical anodization of Ti6Al4V in an electrolyte containing 0.2 wt% NH4F, 60% ethylene glycol and 40% deionized water. The resulting surfaces were systematically heat treated in air with isochronal and isothermal experiments to study the temperature and time dependent transformation respectively. Energy dispersive spectroscopy shows that the anatase phase transformation of TiO2 in the as-anodized amorphous nanotube layer can be achieved in as little as 5 min at 350 °C in contrast to reports of higher temperature and much longer time. Crystallinity analysis at different temperatures and times yield transformation rate coefficients and activation energy for crystalline anatase coalescence. TEM confirms the (101) TiO2 presence within the nanotubes. These results confirm that for applications where amorphous titania nanotube surfaces are converted to crystalline anatase, a 5 min production flow-through heating process could be used instead of a 3 h batch process, reducing time, cost, and complexity.

A potential new diagnostic tool to aid DNA analysis from heat compromised bone using colorimetry: A preliminary study.

PubMed

Fredericks, Jamie D; Ringrose, Trevor J; Dicken, Anthony; Williams, Anna; Bennett, Phil

2015-03-01

Extracting viable DNA from many forensic sample types can be very challenging, as environmental conditions may be far from optimal with regard to DNA preservation. Consequently, skeletal tissue can often be an invaluable source of DNA. The bone matrix provides a hardened material that encapsulates DNA, acting as a barrier to environmental insults that would otherwise be detrimental to its integrity. However, like all forensic samples, DNA in bone can still become degraded in extreme conditions, such as intense heat. Extracting DNA from bone can be laborious and time-consuming. Thus, a lot of time and money can be wasted processing samples that do not ultimately yield viable DNA. We describe the use of colorimetry as a novel diagnostic tool that can assist DNA analysis from heat-treated bone. This study focuses on characterizing changes in the material and physical properties of heated bone, and their correlation with digitally measured color variation. The results demonstrate that the color of bone, which serves as an indicator of the chemical processes that have occurred, can be correlated with the success or failure of subsequent DNA amplification. Copyright © 2014 Forensic Science Society. Published by Elsevier Ireland Ltd. All rights reserved.

Vitrified metal finishing wastes I. Composition, density and chemical durability.

PubMed

Bingham, P A; Hand, R J

2005-03-17

Durable phosphate glasses were formed by vitrifying waste filter cakes from two metal finishing operations. Some melts formed crystalline components during cooling. Compositional analysis of dried, heat treated and vitrified samples was made using energy-dispersive X-ray spectroscopy, X-ray fluorescence spectroscopy, inductively-coupled plasma spectroscopy and Leco induction furnace combustion analysis. Hydrolytic dissolution, measured by an adapted product consistency test, was reduced by up to 3 orders of magnitude upon heat treatment or vitrification, surpassing the performance of borosilicate glass in some cases. This was attributed to the high levels of iron and zinc in the wastes, which greatly improve the durability of phosphate glasses. One of the wastes arose from a metal phosphating process and was particularly suitable for vitrification due to its high P2O5 content and favourable melting behaviour. The other waste, which arose from a number of processes, was less suitable as it had a low P2O5 content and during heating it emitted harmful corrosive gases and underwent violent reactions. Substantial volume reductions were obtained by heat treatment and vitrification of both wastes. Compositions and performances of some vitrified wastes were comparable with those of glasses which are under consideration for the immobilisation of toxic and nuclear wastes.

Process for treating fission waste. [Patent application

DOEpatents

Rohrmann, C.A.; Wick, O.J.

1981-11-17

A method is described for the treatment of fission waste. A glass forming agent, a metal oxide, and a reducing agent are mixed with the fission waste and the mixture is heated. After melting, the mixture separates into a glass phase and a metal phase. The glass phase may be used to safely store the fission waste, while the metal phase contains noble metals recovered from the fission waste.

Raney nickel catalytic device

DOEpatents

O'Hare, Stephen A.

1978-01-01

A catalytic device for use in a conventional coal gasification process which includes a tubular substrate having secured to its inside surface by expansion a catalytic material. The catalytic device is made by inserting a tubular catalytic element, such as a tubular element of a nickel-aluminum alloy, into a tubular substrate and heat-treating the resulting composite to cause the tubular catalytic element to irreversibly expand against the inside surface of the substrate.

Nanostructured Shape Memory Alloys: Adaptive Composite Materials and Components

DTIC Science & Technology

2007-12-01

placing the composites between two stainless steel sheets to minimize contamination. The process described was effective in breaking the nickel...pieced, the discs were heat-treated at 9000C for 1 hour and quenched in ice water. Each quarter piece was placed between two stainless steel sheets of 0.15... martensite interfaces. Additionally a surface preparation technique was developed to provide minimal surface deformation necessary for observation of

Effect of cooling after welding on microstructure and mechanical properties of 12 Pct Cr steel weld metals

NASA Astrophysics Data System (ADS)

Cai, Guang-Jun; Andrén, Hans-Olof; Svensson, Lars-Erik

1997-07-01

The microstructure of three 12 pct cr steel weld metals with different nickel and nitrogen contents was studied in as-welded condition and after postweld heat treatment with and without intercooling. Tensile strength and impact toughness of the weld metals were investigated in different postweld heat treatment conditions. In weld metals heat treated without intercooling, austenite decomposed by a eutectoid reaction that resulted in M23C6 aggregates around retained δ-ferrite. Two morphologies of M2N and MN precipitates were found in a low-dislocation α-ferrite. It was concluded that these phases were also transformed from austenite. In weld metals heat treated with intercooling, M23C6 precipitates were smaller and more homogeneously distributed. Different MN precipitates were found in the tempered martensite. The fracture mode of the weld metals at room temperature was mainly transgranular cleavage with some fibrous fracture. Intercooling treatment improved Charpy impact toughness of the 12 pct Cr steel weld metals substantially. It was found that the important microstructural factors affecting the impact toughness of the weld metals which were heat treated without intercooling were the sizes of the α-ferrite grains, nonmetallic inclusions, and M23C6 aggregates. For the weld metals heat treated with intercooling, the factors which affect the toughness of the weld metals were the sizes of martensite packets and nonmetallic inclusions.

Development of materials and process technology for dual alloy disks

NASA Technical Reports Server (NTRS)

Marder, J. M.; Kortovich, C. S.

1981-01-01

Techniques for the preparation of dual alloy disks were developed and evaluated. Four material combinations were evaluated in the form of HIP consolidated and heat treated cylindrical and plate shapes in terms of elevated temperature tensile, stress rupture and low cycle fatigue properties. The process evaluation indicated that the pe-HIP AF-115 rim/loose powder Rene 95 hub combination offered the best overall range of mechanical properties for dual disk applications. The feasibility of this dual alloy concept for the production of more complex components was demonstrated by the scale up fabrication of a prototype CFM-56 disk made from this AF-115/Rene 95 combination. The hub alloy ultimate tensile strength was approximately 92 percent of the program goal of 1520 MPa (220 ksi) at 480 C (900 F) and the rim alloy stress rupture goal of 300 hours at 675 C (1250 F)/925 MPa (134 ksi) was exceeded by 200 hours. The low cycle fatigue properties were equivalent to those exhibited by HIP and heat treated alloys. There was an absence of rupture notch sensitivity in both alloys. The joint tensile properties were approximately 85 percent of the weaker of the two materials (Rene 95) and the stress rupture properties were equivalent to those of the weaker of the two materials (Rene 95).

A Computational Approach to Modeling Magma Ocean Evolution in 2-D and 3-D

NASA Astrophysics Data System (ADS)

Tackley, P. J.; Louro Lourenço, D. J.; Fomin, I.

2017-12-01

Models of magma ocean evolution have typically been performed in 1-D (e.g. Abe, PEPI 1997; Solomatov and Stevenson, JGR 1993; Elkins-Tanton EPSL 2008). However, 1-D models may miss important aspects of the process, in particular the possible development of solid-state convection before the magma ocean has completely crystallised, and possible large-scale overturn driven by thermal and/or compositional gradients. On the other hand, fully resolving magma ocean evolution in 2-D or 3-D would be extremely challenging due to the small time-scales and length-scales associated with turbulent convection in the magma and the extreme viscosity contrast between regions of high melt fraction and regions of low melt fraction, which are separated by a rheological threshold associated with the solid forming an interconnected matrix. Here, an intermediate approach to treat these has been implemented within the framework of the mantle convection code StagYY (Tackley, PEPI 2008). The basic approach is to resolve processes that occur in the mostly solid state (i.e. below the rheological threshold) while parameterising processes that occur in the mostly liquid state, based largely on the works of Y. Abe. Thus, turbulent convection in magma-rich regions is treated using an effective thermal conductivity based on mixing-length theory, and segregation of solid and liquid is treated using Darcy's law for low melt fractions or crystal settling (offset by vigorous convection) for high melt fractions. At the outer surface a combined radiative-conductive heat balance is implemented, including the temperature drop over a very thin ( cm) thermal boundary layer and reduction of radiative heat loss by an atmosphere. Key to the whole process is petrology: the coexisting compositions of magma and solid under various conditions including possible fractionation, and for this different approaches have been parameterised ranging from a simple basalt-harzburgite parameterisation to a bi-eutectic lower mantle melting model based on ab initio and laboratory experiments.

A computational approach to modelling magma ocean evolution in 2-D and 3-D

NASA Astrophysics Data System (ADS)

Tackley, Paul; Lourenco, Diogo; Fomin, Ilya

2017-04-01

Models of magma ocean evolution have typically been performed in 1-D (e.g. Abe, PEPI 1997; Solomatov and Stevenson, JGR 1993; Elkins-Tanton EPSL 2008). However, 1-D models may miss important aspects of the process, in particular the possible development of solid-state convection before the magma ocean has completely crystallised, and possible large-scale overturn driven by thermal and/or compositional gradients. On the other hand, fully resolving magma ocean evolution in 2-D or 3-D would be extremely challenging due to the small time-scales and length-scales associated with turbulent convection in the magma and the extreme viscosity contrast between regions of high melt fraction and regions of low melt fraction, which are separated by a rheological threshold associated with the solid forming an interconnected matrix. Here, an intermediate approach to treat these has been implemented within the framework of the mantle convection code StagYY (Tackley, PEPI 2008). The basic approach is to resolve processes that occur in the mostly solid state (i.e. below the rheological threshold) while parameterising processes that occur in the mostly liquid state, based largely on the works of Y. Abe. Thus, turbulent convection in magma-rich regions is treated using an effective thermal conductivity based on mixing-length theory, and segregation of solid and liquid is treated using Darcy's law for low melt fractions or crystal settling (offset by vigorous convection) for high melt fractions. At the outer surface a combined radiative-conductive heat balance is implemented, including the temperature drop over a very thin ( cm) thermal boundary layer and reduction of radiative heat loss by an atmosphere. Key to the whole process is petrology: the coexisting compositions of magma and solid under various conditions including possible fractionation, and for this different approaches have been parameterised ranging from a simple basalt-harzburgite parameterisation to a bi-eutectic lower mantle melting model based on ab initio and laboratory experiments.

High-performance perovskite CH3NH3PbI3 thin films for solar cells prepared by single-source physical vapour deposition

PubMed Central

Fan, Ping; Gu, Di; Liang, Guang-Xing; Luo, Jing-Ting; Chen, Ju-Long; Zheng, Zhuang-Hao; Zhang, Dong-Ping

2016-01-01

In this work, an alternative route to fabricating high-quality CH3NH3PbI3 thin films is proposed. Single-source physical vapour deposition (SSPVD) without a post-heat-treating process was used to prepare CH3NH3PbI3 thin films at room temperature. This new process enabled complete surface coverage and moisture stability in a non-vacuum solution. Moreover, the challenges of simultaneously controlling evaporation processes of the organic and inorganic sources via dual-source vapour evaporation and the heating process required to obtain high crystallization were avoided. Excellent composition with stoichiometry transferred from the powder material, a high level of tetragonal phase-purity, full surface coverage, well-defined grain structure, high crystallization and reproducibility were obtained. A PCE of approximately 10.90% was obtained with a device based on SSPVD CH3NH3PbI3. These initial results suggest that SSPVD is a promising method to significantly optimize perovskite CH3NH3PbI3 solar cell efficiency. PMID:27426686

Friction Stir Welding in Wrought and Cast Aluminum Alloys: Weld Quality Evaluation and Effects of Processing Parameters on Microstructure and Mechanical Properties

NASA Astrophysics Data System (ADS)

Pan, Yi; Lados, Diana A.

2017-04-01

Friction stir welding (FSW) is a solid-state process widely used for joining similar and dissimilar materials for critical applications in the transportation sector. Understanding the effects of the process on microstructure and mechanical properties is critical in design for structural integrity. In this study, four aluminum alloy systems (wrought 6061-T651 and cast A356, 319, and A390) were processed in both as-fabricated and pre-weld heat-treated (T6) conditions using various processing parameters. The effects of processing and heat treatment on the resulting microstructures, macro-/micro-hardness, and tensile properties were systematically investigated and mechanistically correlated to changes in grain size, characteristic phases, and strengthening precipitates. Tensile tests were performed at room temperature both along and across the welding zones. A new method able to evaluate weld quality (using a weld quality index) was developed based on the stress concentration calculated under tensile loading. Optimum processing parameter domains that provide both defect-free welds and good mechanical properties were determined for each alloy and associated with the thermal history of the process. These results were further related to characteristic microstructural features, which can be used for component design and materials/process optimization.

Autophagy and Apoptosis Act as Partners to Induce Germ Cell Death after Heat Stress in Mice

PubMed Central

Zhang, Mianqiu; Jiang, Min; Bi, Ye; Zhu, Hui; Zhou, Zuomin; Sha, Jiahao

2012-01-01

Testicular heating suppresses spermatogenesis which is marked by germ cell loss via apoptotic pathways. Recently, it is reported that autophagy also can be induced by heat treatment in somatic cells. In this study, the status of autophagy in germ cells after heat treatment, as well as the partnership between autophagy and apoptosis in these cells was investigated. The results demonstrated that besides initiating apoptotic pathways, heat also induced autophagic pathways in germ cells. Exposure of germ cells to hyperthermia resulted in several specific features of the autophagic process, including autophagosome formation and the conversion of LC3-I to LC3-II. Furthermore, the ubiquitin-like protein conjugation system was implicated as being likely responsible for heat-induced autophagy in germ cells since all genes involving this system were found to be expressed in the testes. In addition, the upstream protein in this system, Atg7 (Autophagy-related gene 7), was found to be expressed in all types of spermatogenic cells, and its expression level was positively correlated with the level of autophagy in germ cells. As a result, Atg7 was selected as the investigative target to further analyze the role of autophagy in heat-induced germ cell death. It was shown that down expression of Atg7 protein resulted in the notable decrease in the level of autophagy in heat-treated germ cells, and this down-regulation of autophagy caused by Atg7 knockdown further reduced the apoptotic rate of germ cells. These results suggest that autophagy plays a positive role in the process of germ cell apoptosis after heat treatment. In conclusion, this study demonstrates that heat triggers autophagy and apoptosis in germ cells. These two mechanisms might act as partners, not antagonist, to induce cell death and lead to eventual destruction of spermatogenesis. PMID:22848486

Can thermal lasers promote skin wound healing?

PubMed

Capon, Alexandre; Mordon, Serge

2003-01-01

Lasers are now widely used for treating numerous cutaneous lesions, for scar revision (hypertrophic and keloid scars), for tissue welding, and for skin resurfacing and remodeling (wrinkle removal). In these procedures lasers are used to generate heat. The modulation of the effect (volatilization, coagulation, hyperthermia) of the laser is obtained by using different wavelengths and laser parameters. The heat source obtained by conversion of light into heat can be very superficial, yet intense, if the laser light is well absorbed (far-infrared:CO(2) or Erbium:Yttrium Aluminum Garnet [Er:YAG] lasers), or it can be much deeper and less intense if the laser light is less absorbed by the skin (visible or near-infrared). Lasers transfer energy, in the form of heat, to surrounding tissues and, regardless of the laser used, a 45-50 degrees C temperature gradient will be obtained in the surrounding skin. If a wound healing process exists, it is a result of live cells reacting to this low temperature increase. The generated supraphysiologic level of heat is able to induce a heat shock response (HSR), which can be defined as the temporary changes in cellular metabolism. These changes are rapid and transient, and are characterized by the production of a small family of proteins termed the heat shock proteins (HSP). Recent experimental studies have clearly demonstrated that HSP 70, which is over-expressed following laser irradiation, could play a role with a coordinated expression of other growth factors such as transforming growth factor (TGF)-beta. TGF-beta is known to be a key element in the inflammatory response and the fibrogenic process. In this process, the fibroblasts are the key cells since they produce collagen and extracellular matrix. In conclusion, the analysis of the literature, and the fundamental considerations concerning the healing process when using thermal lasers, are in favor of a modification of the growth factors synthesis after laser irradiation, induced by an HSR. An extensive review of the different techniques and several clinical studies confirm that thermal lasers could effectively promote skin wound healing, if they are used in a controlled manner.

Effects of sterilization processes on NiTi alloy: surface characterization.

PubMed

Thierry, B; Tabrizian, M; Savadogo, O; Yahia, L

2000-01-01

Sterilization is required for using any device in contact with the human body. Numerous authors have studied device properties after sterilization and reported on bulk and surface modifications of many materials after processing. These surface modifications may in turn influence device biocompatibility. Still, data are missing on the effect of sterilization procedures on new biomaterials such as nickel-titanium (NiTi). Herein we report on the effect of dry heat, steam autoclaving, ethylene oxide, peracetic acid, and plasma-based sterilization techniques on the surface properties of NiTi. After processing electropolished NiTi disks with these techniques, surface analyses were performed by Auger electron spectroscopy (AES), atomic force microscopy (AFM), and contact angle measurements. AES analyses revealed a higher Ni concentration (6-7 vs. 1%) and a slightly thicker oxide layer on the surface for heat and ethylene oxide processed materials. Studies of surface topography by AFM showed up to a threefold increase of the surface roughness when disks were dry heat sterilized. An increase of the surface energy of up to 100% was calculated for plasma treated surfaces. Our results point out that some surface modifications are induced by sterilization procedures. Further work is required to assess the effect of these modifications on biocompatibility, and to determine the most appropriate methods to sterilize NiTi. Copyright 2000 John Wiley & Sons, Inc.

Process for producing advanced ceramics

DOEpatents

Kwong, Kyei-Sing

1996-01-01

A process for the synthesis of homogeneous advanced ceramics such as SiC+AlN, SiAlON, SiC+Al.sub.2 O.sub.3, and Si.sub.3 N.sub.4 +AlN from natural clays such as kaolin, halloysite and montmorillonite by an intercalation and heat treatment method. Included are the steps of refining clays, intercalating organic compounds into the layered structure of clays, drying the intercalated mixture, firing the treated atmospheres and grinding the loosely agglomerated structure. Advanced ceramics produced by this procedure have the advantages of homogeneity, cost effectiveness, simplicity of manufacture, ease of grind and a short process time. Advanced ceramics produced by this process can be used for refractory, wear part and structure ceramics.

Processing of hydroxylapatite coatings on titanium alloy bone prostheses

DOEpatents

Nastasi, M.A.; Levine, T.E.; Mayer, J.W.; Pizziconi, V.B.

1998-10-06

Processing of hydroxylapatite sol-gel films on titanium alloy bone prostheses. A method utilizing non-line-of-sight ion beam implantation and/or rapid thermal processing to provide improved bonding of layers of hydroxylapatite to titanium alloy substrates while encouraging bone ingrowth into the hydroxylapatite layers located away from the substrate, is described for the fabrication of prostheses. The first layer of hydroxylapatite is mixed into the substrate by the ions or rapidly thermally annealed, while subsequent layers are heat treated or densified using ion implantation to form layers of decreasing density and larger crystallization, with the outermost layers being suitable for bone ingrowth.

Processing of hydroxylapatite coatings on titanium alloy bone prostheses

DOEpatents

Nastasi, Michael A.; Levine, Timothy E.; Mayer, James W.; Pizziconi, Vincent B.

1998-01-01

Processing of hydroxylapatite sol-gel films on titanium alloy bone prostheses. A method utilizing non-line-of-sight ion beam implantation and/or rapid thermal processing to provide improved bonding of layers of hydroxylapatite to titanium alloy substrates while encouraging bone ingrowth into the hydroxylapatite layers located away from the substrate, is described for the fabrication of prostheses. The first layer of hydroxylapatite is mixed into the substrate by the ions or rapidly thermally annealed, while subsequent layers are heat treated or densified using ion implantation to form layers of decreasing density and larger crystallization, with the outermost layers being suitable for bone ingrowth.

Sewage sludge drying process integration with a waste-to-energy power plant.

PubMed

Bianchini, A; Bonfiglioli, L; Pellegrini, M; Saccani, C

2015-08-01

Dewatered sewage sludge from Waste Water Treatment Plants (WWTPs) is encountering increasing problems associated with its disposal. Several solutions have been proposed in the last years regarding energy and materials recovery from sewage sludge. Current technological solutions have relevant limits as dewatered sewage sludge is characterized by a high water content (70-75% by weight), even if mechanically treated. A Refuse Derived Fuel (RDF) with good thermal characteristics in terms of Lower Heating Value (LHV) can be obtained if dewatered sludge is further processed, for example by a thermal drying stage. Sewage sludge thermal drying is not sustainable if the power is fed by primary energy sources, but can be appealing if waste heat, recovered from other processes, is used. A suitable integration can be realized between a WWTP and a waste-to-energy (WTE) power plant through the recovery of WTE waste heat as energy source for sewage sludge drying. In this paper, the properties of sewage sludge from three different WWTPs are studied. On the basis of the results obtained, a facility for the integration of sewage sludge drying within a WTE power plant is developed. Furthermore, energy and mass balances are set up in order to evaluate the benefits brought by the described integration. Copyright © 2015 Elsevier Ltd. All rights reserved.

An Experimental Investigation on Hardness and Microstructure of Heat Treated EN 9 Steel

NASA Astrophysics Data System (ADS)

Biswas, Palash; Kundu, Arnab; Mondal, Dhiraj

2017-08-01

In the modern engineering world, extensive research has led to the development of some special grades of steel, often suited for enhanced functions. EN 9 steel is one such grade, having major applications in power plants, automobile and aerospace industry. Different heat treatment processes are employed to achieve high hardness and high wear resistance, but machinability subsequently decreases. Existing literature is not sufficient to achieve a balance between hardness and machinability. The aim of this experimental work is to determine the hardness values and observe microstructural changes in EN9 steel, when it is subjected to annealing, normalizing and quenching. Finally, the effects of tempering after each of these heat treatments on hardness and microstructure have also been shown. It is seen that the tempering after normalizing the specimen achieved satisfactory results. The microstructure was also observed to be consisting of fine grains.

Texture-Induced Anisotropy in an Inconel 718 Alloy Deposited Using Electron Beam Freeform Fabrication

NASA Technical Reports Server (NTRS)

Tayon, W.; Shenoy, R.; Bird, R.; Hafley, R.; Redding, M.

2014-01-01

A test block of Inconel (IN) 718 was fabricated using electron beam freeform fabrication (EBF(sup 3)) to examine how the EBF(sup 3) deposition process affects the microstructure, crystallographic texture, and mechanical properties of IN 718. Tests revealed significant anisotropy in the elastic modulus for the as-deposited IN 718. Subsequent tests were conducted on specimens subjected to a heat treatment designed to decrease the level of anisotropy. Electron backscatter diffraction (EBSD) was used to characterize crystallographic texture in the as-deposited and heat treated conditions. The anisotropy in the as-deposited condition was strongly affected by texture as evidenced by its dependence on orientation relative to the deposition direction. Heat treatment resulted in a significant improvement in modulus of the EBF(sup 3) product to a level nearly equivalent to that for wrought IN 718 with reduced anisotropy; reduction in texture through recrystallization; and production of a more homogeneous microstructure.

Calcium contributes to photoprotection and repair of photosystem II in peanut leaves during heat and high irradiance.

PubMed

Yang, Sha; Wang, Fang; Guo, Feng; Meng, Jing-Jing; Li, Xin-Guo; Wan, Shu-Bo

2015-05-01

In this study, we investigated the effects of exogenous calcium nitrate on photoinhibition and thylakoid protein level in peanut plants under heat (40°C) and high irradiance (HI) (1,200 µmol/m(2) per s) stress. Compared with control seedlings (cultivated in 0 mmol/L Ca(NO3 )2 medium), the maximal photochemical efficiency of photosystem II (PSII) in Ca(2+) -treated plants showed a slight decrease after 5 h stress, accompanied by lower degree of PSII closure (1-qP), higher non-photochemical quenching, and lower level of membrane damage. Ca(2+) inhibitors were used to analyze the varieties of antioxidant enzymes activity and PSII proteins. These results indicated that Ca(2+) could protect the subunits of PSII reaction centers from photoinhibition by reducing the generation of reactive oxygen species. In the presence of both ethyleneglycol-bis(2-aminoethylether)-tetraacetic acid and ascorbic acid (AsA), the net degradation of the damaged D1 protein was faster than that only treated with AsA. Our previous study showed that either the transcriptional or the translational level of calmodulin was obviously higher in Ca(2+) -treated plants. These results suggested that, under heat and HI stress, the Ca(2+) signal transduction pathway can alleviate the photoinhibition through regulating the protein repair process besides an enhanced capacity for scavenging reactive oxygen species. © 2014 The Authors. Journal of Integrative Plant Biology published by Wiley Publishing Asia Pty Ltd on behalf of Institute of Botany, The Chinese Academy of Sciences.

Heat treatment of bulk gallium arsenide using a phosphosilicate glass cap

NASA Technical Reports Server (NTRS)

Mathur, G.; Wheaton, M. L.; Borrego, J. M.; Ghandhi, S. K.

1985-01-01

n-type bulk GaAs crystals, capped with chemically vapor-deposited phosphosilicate glass, were heat treated at temperatures in the range of 600 to 950 C. Measurements on Schottky diodes and solar cells fabricated on the heat-treated material, after removal of a damaged surface layer, show an increase in free-carrier concentration, in minority-carrier-diffusion length, and in solar-cell short-circuit current. The observed changes are attributed to a removal of lifetime-reducing acceptorlike impurities, defects, or their complexes.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Amman, G.D.; Ryan, K.C.

The bark beetle antiaggregative pheromones, verbenone and ipsdienol, were tested in protecting heat-injured lodgepole pine (Pinus contorta Dougl. ex Loud.) from mountain pine beetle (Dendroctonus ponderosae) infestation in the Sawtooth National Recreation Area in central Idaho. Peat moss was placed around 70 percent of the basal circumference of lodgepole pines. When the peat moss was ignited, it simulated the smoldering of natural duff, generating temperatures that killed the cambium. The four treatments tested were uninjured tree, heat-injured tree, heat-injured tree treated with verbenone, and heat-injured tree treated with verbenone plus ipsdienol. Treatments were replicated 20 times. Mountain pine beetles weremore » attracted into treatment blocks by placing mountain pine beetle tree baits on metal posts 3 to 5 meters from treated trees. Fisher's Extract Test showed that treatment and beetle infestation were not independent (P < 0.015). Check treatments contained more unattacked and mass-attacked trees, whereas pheromone treatments contained more unsuccessfully attacked trees.« less

Effect of heat treatment of wood on the morphology, surface roughness and penetration of simulated and human blood.

PubMed

Rekola, J; Lassila, L V J; Nganga, S; Ylä-Soininmäki, A; Fleming, G J P; Grenman, R; Aho, A J; Vallittu, P K

2014-01-01

Wood has been used as a model material for the development of novel fiber-reinforced composite bone substitute biomaterials. In previous studies heat treatment of wood was perceived to significantly increase the osteoconductivity of implanted wood material. The objective of this study was to examine some of the changing attributes of wood materials that may contribute to improved biological responses gained with heat treatment. Untreated and 140°C and 200°C heat-treated downy birch (Betula pubescens Ehrh.) were used as the wood materials. Surface roughness and the effect of pre-measurement grinding were measured with contact and non-contact profilometry. Liquid interaction was assessed with a dipping test using two manufactured liquids (simulated blood) as well as human blood. SEM was used to visualize possible heat treatment-induced changes in the hierarchical structure of wood. The surface roughness was observed to significantly decrease with heat treatment. Grinding methods had more influence on the surface contour and roughness than heat treatment. The penetration of the human blood in the 200°C heat-treated exceeded that in the untreated and 140°C heat-treated materials. SEM showed no significant change due to heat treatment in the dry-state morphology of the wood. The results of the liquid penetration test support previous findings in literature concerning the effects of heat treatment on the biological response to implanted wood. Heat-treatment has only a marginal effect on the surface contour of wood. The highly specialized liquid conveyance system of wood may serve as a biomimetic model for the further development of tailored fiber-composite materials.

Influence of lactic acid and post-treatment recovery time on the heat resistance of Listeria monocytogenes.

PubMed

Omori, Yasuo; Miake, Kiyotaka; Nakamura, Hiromi; Kage-Nakadai, Eriko; Nishikawa, Yoshikazu

2017-09-18

The aim of this study was to evaluate the effect of lactic acid (LA) with and without organic material at various post-treatment recovery times on the heat resistance of Listeria monocytogenes (Lm). LA decreased Lm numbers; however, the effect was remarkably attenuated by the presence of organic matter. Five strains of Lm were treated with LA and the listericidal effects were compared. The effect of LA varied depending on the strain, with ≥3.0% (w/w) LA required to kill the Lm strains in a short time. The heat resistance of Lm treated with LA was examined with respect to the time interval between the acid treatment and the subsequent manufacturing step. The heat resistance of Lm was shown to significantly increase during the post-treatment period. Heat tolerance (D value) increased up to 3.4-fold compared with the non-treated control bacteria. RNA sequencing and RT-PCR analyses suggested that several stress chaperones, proteins controlled by RecA and associated with high-temperature survival, were involved in the mechanism of enhanced heat resistance. These results are applicable to manufacturers when LA and heat treatment methods are utilized for the effective control of Lm in foods. Copyright © 2017 The Authors. Published by Elsevier B.V. All rights reserved.

46 CFR 54.25-7 - Requirement for postweld heat treatment (modifies UCS-56).

Code of Federal Regulations, 2011 CFR

2011-10-01

... 46 Shipping 2 2011-10-01 2011-10-01 false Requirement for postweld heat treatment (modifies UCS-56... ENGINEERING PRESSURE VESSELS Construction With Carbon, Alloy, and Heat Treated Steels § 54.25-7 Requirement for postweld heat treatment (modifies UCS-56). (a) Postweld heat treatment is required for all carbon...

49 CFR 179.400-12 - Postweld heat treatment.

Code of Federal Regulations, 2011 CFR

2011-10-01

... 49 Transportation 3 2011-10-01 2011-10-01 false Postweld heat treatment. 179.400-12 Section 179...-12 Postweld heat treatment. (a) Postweld heat treatment of the inner tank is not required. (b) The... postweld heat treated as prescribed in AAR Specifications for Tank Cars, appendix W (IBR, see § 171.7 of...

46 CFR 54.25-7 - Requirement for postweld heat treatment (modifies UCS-56).

Code of Federal Regulations, 2014 CFR

2014-10-01

... 46 Shipping 2 2014-10-01 2014-10-01 false Requirement for postweld heat treatment (modifies UCS-56... ENGINEERING PRESSURE VESSELS Construction With Carbon, Alloy, and Heat Treated Steels § 54.25-7 Requirement for postweld heat treatment (modifies UCS-56). (a) Postweld heat treatment is required for all carbon...

49 CFR 179.400-12 - Postweld heat treatment.

Code of Federal Regulations, 2014 CFR

2014-10-01

... 49 Transportation 3 2014-10-01 2014-10-01 false Postweld heat treatment. 179.400-12 Section 179...-12 Postweld heat treatment. (a) Postweld heat treatment of the inner tank is not required. (b) The... postweld heat treated as prescribed in AAR Specifications for Tank Cars, appendix W (IBR, see § 171.7 of...

49 CFR 179.400-12 - Postweld heat treatment.

Code of Federal Regulations, 2013 CFR

2013-10-01

... 49 Transportation 3 2013-10-01 2013-10-01 false Postweld heat treatment. 179.400-12 Section 179...-12 Postweld heat treatment. (a) Postweld heat treatment of the inner tank is not required. (b) The... postweld heat treated as prescribed in AAR Specifications for Tank Cars, appendix W (IBR, see § 171.7 of...

46 CFR 54.25-7 - Requirement for postweld heat treatment (modifies UCS-56).

Code of Federal Regulations, 2013 CFR

2013-10-01

... 46 Shipping 2 2013-10-01 2013-10-01 false Requirement for postweld heat treatment (modifies UCS-56... ENGINEERING PRESSURE VESSELS Construction With Carbon, Alloy, and Heat Treated Steels § 54.25-7 Requirement for postweld heat treatment (modifies UCS-56). (a) Postweld heat treatment is required for all carbon...

49 CFR 179.400-12 - Postweld heat treatment.

Code of Federal Regulations, 2012 CFR

2012-10-01

... 49 Transportation 3 2012-10-01 2012-10-01 false Postweld heat treatment. 179.400-12 Section 179...-12 Postweld heat treatment. (a) Postweld heat treatment of the inner tank is not required. (b) The... postweld heat treated as prescribed in AAR Specifications for Tank Cars, appendix W (IBR, see § 171.7 of...

46 CFR 54.25-7 - Requirement for postweld heat treatment (modifies UCS-56).

Code of Federal Regulations, 2012 CFR

2012-10-01

... 46 Shipping 2 2012-10-01 2012-10-01 false Requirement for postweld heat treatment (modifies UCS-56... ENGINEERING PRESSURE VESSELS Construction With Carbon, Alloy, and Heat Treated Steels § 54.25-7 Requirement for postweld heat treatment (modifies UCS-56). (a) Postweld heat treatment is required for all carbon...

46 CFR 54.25-7 - Requirement for postweld heat treatment (modifies UCS-56).

Code of Federal Regulations, 2010 CFR

2010-10-01

... 46 Shipping 2 2010-10-01 2010-10-01 false Requirement for postweld heat treatment (modifies UCS-56... for postweld heat treatment (modifies UCS-56). (a) Postweld heat treatment is required for all carbon... the storage or transportation of liquefied compressed gases shall be postweld heat treated regardless...

Effects of dietary carbohydrates sources on lipids compositions in abalone, Haliotis discus hannai Ino

NASA Astrophysics Data System (ADS)

Wang, Weifang; Mai, Kangsen; Zhang, Wenbing; Xu, Wei; Ai, Qinghui; Yao, Chunfeng; Li, Huitao

2009-09-01

A study was conducted to evaluate the effects of dietary carbohydrates on triglyceride, cholesterol and fatty acid concentrations in abalone, Haliotis discus hannai Ino. Six semi-purified diets with different carbohydrates (dextrin, heat-treated wheat starch, wheat starch, corn starch, tapioca starch and potato starch, respectively), all containing a carbohydrate level of 33.5%, were fed to abalone (initial shell length: 29.98 mm ± 0.09 mm; initial weight: 3.42 g ± 0.02 g) for 24 weeks in a recirculation system. The results indicate that serum triglyceride concentrations were significantly ( P < 0.05) higher in the abalone fed with dextrin, heat-treated wheat starch and wheat starch than those fed with corn starch, and serum cholesterol concentrations were significantly ( P < 0.05) higher in the abalone fed with dextrin, heat-treated wheat starch than those fed with corn starch. Fatty acid C20:4n-6 in the foot muscles were significantly ( P < 0.05) lower in the abalone fed with dextrin than those fed with wheat starch, corn starch, tapioca starch and potato starch. Fatty acid C20:4n-6 in hepatopancreas was significantly ( P < 0.05) lower in abalone fed with heat-treated wheat starch than those fed with corn starch, tapioca starch and potato starch. Fatty acid C22:6n-3 in the foot muscles were significantly ( P < 0.05) lower in the abalone fed with dextrin and heat-treated wheat starch than those fed with wheat starch and potato starch.

Corrosion Analysis of TiCN Coated Al-7075 Alloy for Marine Applications: A Case Study

NASA Astrophysics Data System (ADS)

Srinath, M. K.; Ganesha Prasad, M. S.

2018-05-01

Corrosion is one of the most important marine difficulties that cause long term problems, occurring in ships and submarines surrounded by a corrosive environment when coupled with chemical, temperature and stress related conditions. Corrosion of marine parts could lead to severe disasters. Coatings and heat treatment in a very effective way could be used to protect the aluminium parts against corrosion. The present case study focuses on the corrosion and microstructural properties of TiCN coatings fabricated on Al-7075 aluminium alloy substrate by using Physical Vapour Deposition technique. Corrosion properties of specimen's heat treated at 500 °C at durations of 1, 4, 8 and 12 h were tested through salt spray test. According to D-1193, ASTM standard, corrosion resistance of coated and heat treated Al-7075 samples were investigated in solution kept at 95 °F with a pH of 6.5-7.2, with 5 sections of NaCl to 95 sections of type IV water. The specimen's heat treated for 1 h showed positive corrosion resistance, while the specimens treated for longer durations had the opposite effect. The microstructures of the salt spray tested coatings were investigated by scanning electron microscope. X-ray diffraction tests were conducted on specimens to determine the atomic and molecular structure of the surface crystals and the unit cell dimensions. The corrosion mechanisms of the coated specimens under the heat treated conditions have been explored.

Effect of gamma irradiation on mistletoe (Viscum album) lectin-mediated toxicity and immunomodulatory activity☆

PubMed Central

Sung, Nak-Yun; Byun, Eui-Baek; Song, Du-Sup; Jin, Yeung-Bae; Kim, Jae-Kyung; Park, Jong-Heum; Song, Beom-Seok; Jung, Pil-Mun; Byun, Myung-Woo; Lee, Ju-Woon; Park, Sang-Hyun; Kim, Jae-Hun

2013-01-01

This study evaluated the effect of gamma irradiation on the reduction of the toxicity of mistletoe lectin using both in vitro and in vivo models. To extract the lectin from mistletoe, an (NH4)2SO4 precipitation method was employed and the precipitant purified using a Sepharose 4B column to obtain the pure lectin fraction. Purified lectin was then gamma-irradiated at doses of 0, 5, 10, 15, and 20 kGy, or heated at 100 °C for 30 min. Toxic effects of non-irradiated, irradiated, and heat-treated lectins were tested using hemagglutination assays, cytotoxicity assays, hepatotoxicity, and a mouse survival test and immunological response was tested using cytokine production activity. Hemagglutination of lectin was remarkably decreased (P < 0.05) by irradiation at doses exceeding 10 kGy and with heat treatment. However, lectin irradiated with 5 kGy maintained its hemagglutination activity. The cytotoxicity of lectin was decreased by irradiation at doses over 5 kGy and with heat treatment. In experiments using mouse model, glutamate oxaloacetate transaminase (GOT) and glutamic pyruvic transaminase (GPT) levels were decreased in the group treated with the 5 kGy irradiated and heat-treated lectins as compared to the intact lectin, and it was also shown that 5 kGy irradiated and heat-treated lectins did not cause damage in liver tissue or mortality. In the result of immunological response, tumor necrosis factor (TNF-α) and interleukin (IL-6) levels were significantly (P < 0.05) increased in the 5 kGy gamma-irradiated lectin treated group. These results indicate that 5 kGy irradiated lectin still maintained the immunological response with reduction of toxicity. Therefore, gamma-irradiation may be an effective method for reducing the toxicity of lectin maintaining the immune response. PMID:23847758

Nanostructuring effect of multi-walled carbon nanotubes on electrochemical properties of carbon foam as constructive electrode for lead acid battery

NASA Astrophysics Data System (ADS)

Kumar, Rajeev; Kumari, Saroj; Mathur, Rakesh B.; Dhakate, Sanjay R.

2015-01-01

In the present study, nanostructuring effect of multi-walled carbon nanotubes (MWCNTs) on electrochemical properties of coal tar pitch (CTP) based carbon foam (CFoam) was investigated. The different weight fractions of MWCNTs were mixed with CTP and foam was developed from the mixture of CTP and MWCNTs by sacrificial template technique and heat treated at 1,400 and 2,500 °C in inert atmosphere. These foams were characterized by scanning electron microscopy, X-ray diffraction, and potentiostat PARSTAT for cyclic voltammetry. It was observed that, bulk density of CFoam increases with increasing MWCNTs content and decreases after certain amount. The MWCNTs influence the morphology of CFoam and increase the width of ligaments as well as surface area. During the heat treatment, stresses exerting at MWCNTs/carbon interface accelerate ordering of the graphene layer which have positive effect on the electrochemical properties of CFoam. The current density increases from 475 to 675 mA/cm2 of 1,400 °C heat treated and 95 to 210 mA/cm2 of 2,500 °C heat-treated CFoam with 1 wt% MWCNTs. The specific capacitance was decreases with increasing the scan rate from 100 to 1,000 mV/s. In case of 1 % MWCNTs content CFoam the specific capacitance at the scan rate 100 mV/s was increased from 850 to 1,250 μF/cm2 and 48 to 340 μF/cm2 of CFoam heat treated at 1,400 °C and 2,500 °C respectively. Thus, the higher value surface area and current density of MWCNTs-incorporated CFoam heat treated to 1,400 °C can be suitable for lead acid battery electrode with improved charging capability.

Microstructure and Mechanical Properties of Heat-Treated B319 Alloy Diesel Cylinder Heads

NASA Astrophysics Data System (ADS)

Chaudhury, S. K.; Apelian, D.; Meyer, P.; Massinon, D.; Morichon, J.

2015-07-01

Microstructure and mechanical properties of B319 alloy diesel cylinder heads were investigated in this study. Cylinder heads were heat treated to T5, T6, and T7 tempers using fluidized bed technology. Three different fluidized beds were used, each to solutionize, quench, and age the castings. For comparative purposes, castings were also aged using conventional forced-air circulation electric-resistance furnace. Effects of processing parameters such as temperature, time, and heating rate on microstructural evolution and mechanical properties namely tensile properties and hardness of B319 alloy castings were studied. The number density and size range of precipitates were measured. Results show that the T5 temper has no effect on eutectic phases such as Si- and Fe-rich intermetallic, and Al2Cu. On contrary, both T6 and T7 tempers result in spherodization of the eutectic Si and partial dissolution of the Al2Cu phase. Prolonged solution heat treatment for 8 hours in fluidized bed results in limited dissolution of the secondary eutectic Al2Cu phase. Aging (T6, T7, and T5) results in precipitation of Al5Cu2Mg8Si6 and Al2Cu phases in B319 alloy. The number density of precipitates in T6 temper is greater than in T7 and T5 tempers. The number density of precipitates is also affected by the duration of solution heat treatment. In general, long solution heat treatment (8 hours) results in greater precipitate density than short solution treatment (2 hours). The distribution of precipitates is inhomogeneous and varied across the dendritic structure. In general, precipitation rate of Al5Cu2Mg8Si6 phase is greater near the periphery of the dendrite as compared to the center. This is because Al5Cu2Mg8Si6 nucleates on Si particle, grain boundaries, and triple junction between recrystallized Al grains and Si particles. Similarly, heterogeneous sites such as grain boundaries and Al/Si interface also act as nucleating sites for the precipitation of Al2Cu phase. In general, the coarsening rate of precipitates near to the periphery of the dendrite is greater than in the center. This is because the Al matrix region close to the eutectic Si particles is subjected to in situ thermal stresses, which is generated due to the thermal mismatch between Al and Si particles. Thermal stress is highest at the Si/Al interface and decreases significantly away from the Al/Si interface. The precipitation and growth rate of the alloy aged in fluidized bed is greater than in conventional furnace. This is because heating rates of casting in fluidized bed (FB) are greater than conventional furnace, which result in greater precipitation rate. This study establishes a correlation between structure, thermal processing, and property of B319 alloy treated to various heat treatments. Reasonably good mechanical properties were obtained in less time using fluidized bed furnace. This work clearly demonstrates the significant potential of FB to save time and energy.

The Effect of Rod-Shaped Long-Period Stacking Ordered Phases Evolution on Corrosion Behavior of Mg95.33Zn2Y2.67 Alloy

PubMed Central

Wang, Jingfeng; Jiang, Weiyan; Li, Yang; Ma, Yao

2018-01-01

The morphology evolution of long-period stacking ordered (LPSO) phases on corrosion behavior of Mg95.33Zn2Y2.67 alloy is investigated systematically during as-cast, pre-extrusion heat-treated, as-extruded and post-extrusion heat-treated conditions. The second phases in the as-cast alloy are only LPSO phases with a few Y particles. The pre-extrusion heat treatment changed LPSO phases from blocks into a rudimentary rod shape with lamellar structure, subsequently into fine fragments by extrusion, and then into a regular rod shape with lamellar structure followed by post-extrusion heat treatment. Immersion tests and electrochemical measurements in 3.5 wt % NaCl solution reveal that the post-extrusion heat-treated alloy has the best corrosion resistance with the lowest corrosion rate. This is attributed to the rod-shaped LPSO phases, which could hinder corrosion proceeding, and result in corrosion orientated along the direction of rods and forming relatively dense long-strip corrosion products. Our findings demonstrate that the improved corrosion resistance of magnesium alloys with LPSO phases can be tailored effectively by the proceeding technology and post-heat treatment. PMID:29772721

6-gingerol ameliorates gentamicin induced renal cortex oxidative stress and apoptosis in adult male albino rats.

PubMed

Hegazy, Ahmed M S; Mosaed, Mohammed M; Elshafey, Saad H; Bayomy, Naglaa A

2016-06-01

Ginger or Zingiber officinale which is used in traditional medicine has been found to possess antioxidant effect that can control the generation of free radicals. Free radicals are the causes of renal cell degeneration that leads to renal failure in case of gentamicin induced toxicity. This study was done to evaluate the possible protective effects of 6-gingerol as natural antioxidant on gentamicin-induced renal cortical oxidative stress and apoptosis in adult male albino rats. Forty adult male albino rats were used in this study and were randomly divided into four groups, control group; 6-gingerol treated group; gentamicin treated group and protected group (given simultaneous 6-gingerol and gentamicin). At the end of the study, blood samples were drawn for biochemical study. Kidney sections were processed for histological, and immunohistochemical examination for caspase-3 to detect apoptosis and anti heat shock protein 47 (HSP47) to detect oxidative damage. Gentamicin treated rats revealed a highly significant increase in renal function tests, tubular dilatation with marked vacuolar degeneration and desquamation of cells, interstitial hemorrhage and cellular infiltration. Immunohistochemically, gentamicin treated rats showed a strong positive immunoreaction for caspase-3 and anti heat shock protein 47 (HSP47). Protected rats showed more or less normal biochemical, histological, and immunohistochemical pictures. In conclusion, co-administration of 6-gingerol during gentamicin 'therapy' has a significant reno-protective effect in a rat model of gentamicin-induced renal damage. It is recommended that administration of ginger with gentamicin might be beneficial in men who receive gentamicin to treat infections. Copyright © 2016 Elsevier Ltd. All rights reserved.

Occurrence, distribution and contamination levels of heat-resistant moulds throughout the processing of pasteurized high-acid fruit products.

PubMed

Santos, Juliana Lane Paixão Dos; Samapundo, Simbarashe; Biyikli, Ayse; Van Impe, Jan; Akkermans, Simen; Höfte, Monica; Abatih, Emmanuel Nji; Sant'Ana, Anderson S; Devlieghere, Frank

2018-05-19

Heat-resistant moulds (HRMs) are well known for their ability to survive pasteurization and spoil high-acid food products, which is of great concern for processors of fruit-based products worldwide. Whilst the majority of the studies on HRMs over the last decades have addressed their inactivation, few data are currently available regarding their contamination levels in fruit and fruit-based products. Thus, this study aimed to quantify and identify heat-resistant fungal ascospores from samples collected throughout the processing of pasteurized high-acid fruit products. In addition, an assessment on the effect of processing on the contamination levels of HRMs in these products was carried out. A total of 332 samples from 111 batches were analyzed from three processing plants (=three processing lines): strawberry puree (n = 88, Belgium), concentrated orange juice (n = 90, Brazil) and apple puree (n = 154, the Netherlands). HRMs were detected in 96.4% (107/111) of the batches and 59.3% (197/332) of the analyzed samples. HRMs were present in 90.9% of the samples from the strawberry puree processing line (1-215 ascospores/100 g), 46.7% of the samples from the orange juice processing line (1-200 ascospores/100 g) and 48.7% of samples from the apple puree processing line (1-84 ascospores/100 g). Despite the high occurrence, the majority (76.8%, 255/332) of the samples were either not contaminated or presented low levels of HRMs (<10 ascospores/100 g). For both strawberry puree and concentrated orange juice, processing had no statistically significant effect on the levels of HRMs (p > 0.05). On the contrary, a significant reduction (p < 0.05) in HRMs levels was observed during the processing of apple puree. Twelve species were identified belonging to four genera - Byssochlamys, Aspergillus with Neosartorya-type ascospores, Talaromyces and Rasamsonia. N. fumigata (23.6%), N. fischeri (19.1%) and B. nivea (5.5%) were the predominant species in pasteurized products. The quantitative data (contamination levels of HRMs) were fitted to exponential distributions and will ultimately be included as input to spoilage risk assessment models which would allow better control of the spoilage of heat treated fruit products caused by heat-resistant moulds. Copyright © 2018 Elsevier B.V. All rights reserved.

Thermal and mechanical treatments for nickel and some nickel-base alloys: Effects on mechanical properties

NASA Technical Reports Server (NTRS)

Hall, A. M.; Beuhring, V. F.

1972-01-01

This report deals with heat treating and working nickel and nickel-base alloys, and with the effects of these operations on the mechanical properties of the materials. The subjects covered are annealing, solution treating, stress relieving, stress equalizing, age hardening, hot working, cold working, combinations of working and heat treating (often referred to as thermomechanical treating), and properties of the materials at various temperatures. The equipment and procedures used in working the materials are discussed, along with the common problems that may be encountered and the precautions and corrective measures that are available.

Wear Enhancement of Wheel-Rail Interaction by Ultrasonic Nanocrystalline Surface Modification Technique.

PubMed

Chang, Seky; Pyun, Young-Sik; Amanov, Auezhan

2017-02-16

In this study, an ultrasonic nanocrystalline surface modification (UNSM) technique was applied to normal and heat-treated rails made of 60 kgK steel to enhance the wear resistance of the wheel-rail interaction. The hardness and compressive residual stress values of the untreated and UNSM-treated rails were measured by the Brinell hardness tester and X-ray diffraction technique, respectively. It was found, according to the measurement results, that the hardness was increased by about 20% and 8%, whereas the compressive residual stress was induced by about 52% and 62% for the UNSM-treated normal and heat-treated rails, respectively. The UNSM-treated normal rail showed a slightly higher hardness than the heat-treated rail. The wear resistance of rails with respect to rotating speed and rolling time was assessed using a rolling contact wear (RCW) tester under dry conditions. The RCW test results revealed that the wear of the UNSM-treated rails was enhanced in comparison with those of the untreated rails. Also, the wear amount of the rails was increased with increasing the rotation speed. The UNSM-treated normal rail exhibited the highest wear resistance with respect to the rotation speed. The wear mechanisms of the rails are also discussed based on microscopic images of the worn out surfaces.

Wear Enhancement of Wheel-Rail Interaction by Ultrasonic Nanocrystalline Surface Modification Technique

PubMed Central

Chang, Seky; Pyun, Young-Sik; Amanov, Auezhan

2017-01-01

In this study, an ultrasonic nanocrystalline surface modification (UNSM) technique was applied to normal and heat-treated rails made of 60 kgK steel to enhance the wear resistance of the wheel-rail interaction. The hardness and compressive residual stress values of the untreated and UNSM-treated rails were measured by the Brinell hardness tester and X-ray diffraction technique, respectively. It was found, according to the measurement results, that the hardness was increased by about 20% and 8%, whereas the compressive residual stress was induced by about 52% and 62% for the UNSM-treated normal and heat-treated rails, respectively. The UNSM-treated normal rail showed a slightly higher hardness than the heat-treated rail. The wear resistance of rails with respect to rotating speed and rolling time was assessed using a rolling contact wear (RCW) tester under dry conditions. The RCW test results revealed that the wear of the UNSM-treated rails was enhanced in comparison with those of the untreated rails. Also, the wear amount of the rails was increased with increasing the rotation speed. The UNSM-treated normal rail exhibited the highest wear resistance with respect to the rotation speed. The wear mechanisms of the rails are also discussed based on microscopic images of the worn out surfaces. PMID:28772549

Low-rank coal oil agglomeration product and process

DOEpatents

Knudson, Curtis L.; Timpe, Ronald C.; Potas, Todd A.; DeWall, Raymond A.; Musich, Mark A.

1992-01-01

A selectively-sized, raw, low-rank coal is processed to produce a low ash and relative water-free agglomerate with an enhanced heating value and a hardness sufficient to produce a non-decrepitating, shippable fuel. The low-rank coal is treated, under high shear conditions, in the first stage to cause ash reduction and subsequent surface modification which is necessary to facilitate agglomerate formation. In the second stage the treated low-rank coal is contacted with bridging and binding oils under low shear conditions to produce agglomerates of selected size. The bridging and binding oils may be coal or petroleum derived. The process incorporates a thermal deoiling step whereby the bridging oil may be completely or partially recovered from the agglomerate; whereas, partial recovery of the bridging oil functions to leave as an agglomerate binder, the heavy constituents of the bridging oil. The recovered oil is suitable for recycling to the agglomeration step or can serve as a value-added product.

Low-rank coal oil agglomeration product and process

DOEpatents

Knudson, C.L.; Timpe, R.C.; Potas, T.A.; DeWall, R.A.; Musich, M.A.

1992-11-10

A selectively-sized, raw, low-rank coal is processed to produce a low ash and relative water-free agglomerate with an enhanced heating value and a hardness sufficient to produce a non-degradable, shippable fuel. The low-rank coal is treated, under high shear conditions, in the first stage to cause ash reduction and subsequent surface modification which is necessary to facilitate agglomerate formation. In the second stage the treated low-rank coal is contacted with bridging and binding oils under low shear conditions to produce agglomerates of selected size. The bridging and binding oils may be coal or petroleum derived. The process incorporates a thermal deoiling step whereby the bridging oil may be completely or partially recovered from the agglomerate; whereas, partial recovery of the bridging oil functions to leave as an agglomerate binder, the heavy constituents of the bridging oil. The recovered oil is suitable for recycling to the agglomeration step or can serve as a value-added product.

Friction Freeform Fabrication of Superalloy Inconel 718: Prospects and Problems

NASA Astrophysics Data System (ADS)

Dilip, J. J. S.; Janaki Ram, G. D.

2014-01-01

Friction Freeform Fabrication is a new solid-state additive manufacturing process. The present investigation reports a detailed study on the prospects of this process for additive part fabrication in superalloy Inconel 718. Using a rotary friction welding machine and employing alloy 718 consumable rods in solution treated condition, cylindrical-shaped multi-layer friction deposits (10 mm diameter) were successfully produced. In the as-deposited condition, the deposits showed very fine grain size with no grain boundary δ phase. The deposits responded well to direct aging and showed satisfactory room-temperature tensile properties. However, their stress rupture performance was unsatisfactory because of their layered microstructure with very fine grain size and no grain boundary δ phase. The problem was overcome by heat treating the deposits first at 1353 K (1080 °C) (for increasing the grain size) and then at 1223 K (950 °C) (for precipitating the δ phase). Overall, the current study shows that Friction Freeform Fabrication is a very useful process for additive part fabrication in alloy 718.

Optimizing the Hot-Corrosion Resistance-of-Novel gamma-Ni+gamma-prime-Ni3A1-Based Alloys and Coatings

DTIC Science & Technology

2006-07-01

TBC benefit Substrale limit 1 1 0 0 ---------- .- -.. . . . . . . --- I single crystal S1000 conventlonally cest allos . .- alloy. E directionally...usually heat treated or processed) forms. Developments in casting technologies made it possible to produce directionally-solidified and single - crystal ...advanced single - crystal superalloys with improved strength meant reductions in chromium and silicon contents. The scale growth and spallation rates can be

Investigation and development of a production operation for rapid carbonitriding of automobile parts

NASA Astrophysics Data System (ADS)

Bodyako, B. M.; Shipko, A. A.; Gurchenko, P. S.

1986-08-01

The use of carbonitriding with induction heating in the vapors of liquid media makes it possible to eliminate local overheating of the surface being treated, to improve the reproducibility of the process, to solve the problem of rational delivery and removal of the reaction products from the surface being impregnated, to accurately regulate the parameters of the case, and to increase economy in treatment and production culture.

Alloys For Corrosive, Hydrogen-Rich Environments

NASA Technical Reports Server (NTRS)

Mcpherson, William B.; Bhat, Biliyar N.; Chen, Po-Shou; Kuruvilla, A. K.; Panda, Binayak

1993-01-01

"NASA-23" denotes class of alloys resisting both embrittlement by hydrogen and corrosion. Weldable and castable and formed by such standard processes as rolling, forging, and wire drawing. Heat-treated to obtain desired combinations of strength and ductility in ranges of 100 to 180 kpsi yield strength, 120 to 200 kpsi ultimate tensile strength, and 10 to 30 percent elongation at break. Used in place of most common aerospace structural alloy, Inconel(R) 718.

Treatment of adjuvant arthritis with granulocyte-colony stimulating factor and peptide derived from heat shock protein 65.

PubMed

Brendolan, Andrea; Higuchi, Masanori; Sibley, Richard; Strober, Samuel

2003-01-01

Adjuvant arthritis in Lewis rats is induced by the subcutaneous injection of Mycobacterium tuberculosis in mineral oil, and the predominant T cell immune reactivity is against the heat shock protein 65 derived peptide 176-190. We treated Lewis rats with human recombinant G-CSF followed by (i.v) administration of peptide 176-190 after induction of adjuvant arthritis (AA), and observed decreased disease severity, joint destruction, new bone formation and joint ankylosis. Treatment with G-CSF alone was also effective, but to a lesser extent. In addition, we found that splenocytes from rats treated with G-CSF had reduced antigen presenting capacity compared with splenocytes from vehicle treated rats. Primed lymph node cells from G-CSF plus peptide treated rats showed a marked reduction in proliferation and secretion of IFN-gamma after stimulation with the heat shock protein peptide in vitro as compared to controls.

Change in Color and Volatile Composition of Skim Milk Processed with Pulsed Electric Field and Microfiltration Treatments or Heat Pasteurization.

PubMed

Chugh, Anupam; Khanal, Dipendra; Walkling-Ribeiro, Markus; Corredig, Milena; Duizer, Lisa; Griffiths, Mansel W

2014-04-23

Non-thermal processing methods, such as pulsed electric field (PEF) and tangential-flow microfiltration (TFMF), are emerging processing technologies that can minimize the deleterious effects of high temperature short time (HTST) pasteurization on quality attributes of skim milk. The present study investigates the impact of PEF and TFMF, alone or in combination, on color and volatile compounds in skim milk. PEF was applied at 28 or 40 kV/cm for 1122 to 2805 µs, while microfiltration (MF) was conducted using membranes with three pore sizes (lab-scale 0.65 and 1.2 µm TFMF, and pilot-scale 1.4 µm MF). HTST control treatments were applied at 75 or 95 °C for 20 and 45 s, respectively. Noticeable color changes were observed with the 0.65 µm TFMF treatment. No significant color changes were observed in PEF-treated, 1.2 µm TFMF-treated, HTST-treated, and 1.4 µm MF-treated skim milk ( p ≥ 0.05) but the total color difference indicated better color retention with non-thermal preservation. The latter did not affect raw skim milk volatiles significantly after single or combined processing ( p ≥ 0.05), but HTST caused considerable changes in their composition, including ketones, free fatty acids, hydrocarbons, and sulfur compounds ( p < 0.05). The findings indicate that for the particular thermal and non-thermal treatments selected for this study, better retention of skim milk color and flavor components were obtained for the non-thermal treatments.

Water availability as dominant control of heat stress responses in two contrasting tree species.

PubMed

Ruehr, Nadine K; Gast, Andreas; Weber, Christina; Daub, Baerbel; Arneth, Almut

2016-02-01

Heat waves that trigger severe droughts are predicted to increase globally; however, we lack an understanding of how trees respond to the combined change of extreme temperatures and water availability. Here, we studied the impacts of two consecutive heat waves as well as post-stress recovery in young Pseudotsuga menziesii (Mirb.) Franco (Douglas-fir) and Robinia pseudoacacia L. (black locust) growing under controlled conditions. Responses were compared under water supply close to the long-term average and under reduced irrigation to represent drought. Exposure to high temperatures (+10 °C above ambient) and vapour pressure deficit strongly affected the trees in terms of water relations, photosynthesis and growth. Douglas-fir used water resources conservatively, and transpiration decreased in response to mild soil water limitation. In black locust, heat stress led to pronounced tree water deficits (stem diameter shrinkage), accompanied by leaf shedding to alleviate stress on the hydraulic system. The importance of water availability during the heat waves became further apparent by a concurrent decline in photosynthesis and stomatal conductance with increasing leaf temperatures in both species, reaching the lowest rates in the heat-drought treatments. Stress severity determined both the speed and the amount of recovery. Upon release of stress, photosynthesis recovered rapidly in drought-treated black locust, while it remained below control rates in heat (t = -2.4, P < 0.05) and heat-drought stressed trees (t = 2.96, P < 0.05). In Douglas-fir, photosynthesis recovered quickly, while water-use efficiency increased in heat-drought trees because stomatal conductance remained reduced (t = -2.92, P < 0.05). Moreover, Douglas-fir was able to compensate for stem-growth reductions following heat (-40%) and heat-drought stress (-68%), but most likely at the expense of storage and other growth processes. Our results highlight the importance of studying heat waves alongside changes in water availability. They further suggest that we should look beyond the actual stress event to identify lagged effects and acclimation processes that may determine tree resilience in the long term. © The Author 2015. Published by Oxford University Press. All rights reserved. For Permissions, please email: journals.permissions@oup.com.

Effects of anodizing parameters and heat treatment on nanotopographical features, bioactivity, and cell culture response of additively manufactured porous titanium.

PubMed

Amin Yavari, S; Chai, Y C; Böttger, A J; Wauthle, R; Schrooten, J; Weinans, H; Zadpoor, A A

2015-06-01

Anodizing could be used for bio-functionalization of the surfaces of titanium alloys. In this study, we use anodizing for creating nanotubes on the surface of porous titanium alloy bone substitutes manufactured using selective laser melting. Different sets of anodizing parameters (voltage: 10 or 20V anodizing time: 30min to 3h) are used for anodizing porous titanium structures that were later heat treated at 500°C. The nanotopographical features are examined using electron microscopy while the bioactivity of anodized surfaces is measured using immersion tests in the simulated body fluid (SBF). Moreover, the effects of anodizing and heat treatment on the performance of one representative anodized porous titanium structures are evaluated using in vitro cell culture assays using human periosteum-derived cells (hPDCs). It has been shown that while anodizing with different anodizing parameters results in very different nanotopographical features, i.e. nanotubes in the range of 20 to 55nm, anodized surfaces have limited apatite-forming ability regardless of the applied anodizing parameters. The results of in vitro cell culture show that both anodizing, and thus generation of regular nanotopographical feature, and heat treatment improve the cell culture response of porous titanium. In particular, cell proliferation measured using metabolic activity and DNA content was improved for anodized and heat treated as well as for anodized but not heat-treated specimens. Heat treatment additionally improved the cell attachment of porous titanium surfaces and upregulated expression of osteogenic markers. Anodized but not heat-treated specimens showed some limited signs of upregulated expression of osteogenic markers. In conclusion, while varying the anodizing parameters creates different nanotube structure, it does not improve apatite-forming ability of porous titanium. However, both anodizing and heat treatment at 500°C improve the cell culture response of porous titanium. Copyright © 2015 Elsevier B.V. All rights reserved.

Wear Resistant Coatings for Titanium.

DTIC Science & Technology

1980-10-01

A-AllI 716 PRATT AND WHITNEY AIRCRAFT GROUP WEST PALM BEACH FL O-ETC P/f 11/6 WEAR RESISTANT COATINGS FOR TITANI WI.(U) OCT GO P L MCDANIEL, R E...treat cycle should be com- patible with previous heat-treat history and selected in accordance with MIL-H-81200. 11. (Option) - Vapor blast surfaces. 27...heat-treat history of the base metal and selected in accordance with MIL-H-81200 unless otherwise specified (see 6.2). Titanium alloys not covered by

Effects of urea formaldehyde condensation polymer treatment of flaxseed on ruminal digestion and lactation in dairy cows.

PubMed

Hawkins, A; Yuan, K; Armendariz, C K; Highland, G; Bello, N M; Winowiski, T; Drouillard, J S; Titgemeyer, E C; Bradford, B J

2013-06-01

Flaxseed is a potent source of the n-3 fatty acid α-linolenic acid (ALA), yet most ALA is lost during ruminal biohydrogenation when ground flaxseed is fed to ruminants. Heat processing and urea formaldehyde condensation polymer (UFCP) treatment of flaxseed were investigated as possible means of protecting ALA from ruminal degradation. Ground flaxseed (GF), heated ground flaxseed (HGF), or UFCP-treated ground flaxseed (UFCPGF) were incubated for 0, 4, 8, and 12h in 4 ruminally cannulated multiparous lactating Holstein cows. Compared with GF, HGF and UFCPGF decreased ruminal disappearance of dry matter, crude protein, and ALA. Pepsin-digestible protein remaining after 12h of ruminal incubation was greater for UFCPGF and HGF than for GF. Twenty-four lactating Holstein cows (207 ± 37 d in milk, 668 ± 66 kg of body weight, and 1.33 ± 0.56 lactations) were then used in a randomized complete block design experiment with a basal feeding period to assess effects of flaxseed treatment on ALA enrichment of plasma and milk as well as lactational performance. No evidence existed that supplementation of HGF and UFCPGF affected dry matter intake, milk fat content, milk protein content, or energy-corrected milk yield, but UFCPGF marginally decreased milk yield compared with HGF. Plasma concentration of ALA was not affected by treatment. Concentrations of n-3 fatty acids and conjugated linoleic acids in milk fat were increased by UFCPGF relative to HGF, but ALA yield was not affected. Taken together, in situ results suggest that heat-treated flaxseed, with or without UFCP treatment, slowed ruminal disappearance of ALA. Feeding UFCP-treated flaxseed failed to alter ALA content of plasma or milk ALA yield relative to heating alone. Copyright © 2013 American Dairy Science Association. Published by Elsevier Inc. All rights reserved.

46 CFR 54.25-1 - Scope.

Code of Federal Regulations, 2013 CFR

2013-10-01

... 46 Shipping 2 2013-10-01 2013-10-01 false Scope. 54.25-1 Section 54.25-1 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING PRESSURE VESSELS Construction With Carbon, Alloy, and Heat Treated Steels § 54.25-1 Scope. The carbon, alloy, and heat treated steels used in construction of pressure vessels and parts shal...

46 CFR 54.25-1 - Scope.

Code of Federal Regulations, 2012 CFR

2012-10-01

... 46 Shipping 2 2012-10-01 2012-10-01 false Scope. 54.25-1 Section 54.25-1 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING PRESSURE VESSELS Construction With Carbon, Alloy, and Heat Treated Steels § 54.25-1 Scope. The carbon, alloy, and heat treated steels used in construction of pressure vessels and parts shal...

46 CFR 54.25-1 - Scope.

Code of Federal Regulations, 2011 CFR

2011-10-01

... 46 Shipping 2 2011-10-01 2011-10-01 false Scope. 54.25-1 Section 54.25-1 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING PRESSURE VESSELS Construction With Carbon, Alloy, and Heat Treated Steels § 54.25-1 Scope. The carbon, alloy, and heat treated steels used in construction of pressure vessels and parts shal...

46 CFR 54.25-1 - Scope.

Code of Federal Regulations, 2010 CFR

2010-10-01

... 46 Shipping 2 2010-10-01 2010-10-01 false Scope. 54.25-1 Section 54.25-1 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING PRESSURE VESSELS Construction With Carbon, Alloy, and Heat Treated Steels § 54.25-1 Scope. The carbon, alloy, and heat treated steels used in construction of pressure vessels and parts shal...

46 CFR 54.25-1 - Scope.

Code of Federal Regulations, 2014 CFR

2014-10-01

... 46 Shipping 2 2014-10-01 2014-10-01 false Scope. 54.25-1 Section 54.25-1 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING PRESSURE VESSELS Construction With Carbon, Alloy, and Heat Treated Steels § 54.25-1 Scope. The carbon, alloy, and heat treated steels used in construction of pressure vessels and parts shal...

Understanding decay resistance, dimensional stability and strength changes in heat treated and acetylated wood

Treesearch

Roger M. Rowell; Rebecca E. Ibach; James McSweeny; Thomas Nilsson

2009-01-01

Reductions in hygroscopicity, increased dimensional stability and decay resistance of heat-treated wood depend on decomposition of a large portion of the hemicelluloses in the wood cell wall. In theory, these hemicelluloses are converted to small organic molecules, water and volatile furan-type intermediates that can polymerize in the cell wall. Reductions in...

Resistant starch improvement of rice starches under a combination of acid and heat-moisture treatments.

PubMed

Hung, Pham Van; Vien, Ngo Lam; Lan Phi, Nguyen Thi

2016-01-15

The effects of a combination of acid and heat-moisture treatment on formation of resistant starch (RS) and characteristics of high-amylose, normal and waxy rice starches were investigated in this study. The degrees of polymerization of the rice starches treated with citric acid, lactic acid or acetic acid were significantly reduced as compared to the native starches. The RS contents of acid and heat-moisture treated rice starches were in a range of 30.1-39.0%, significantly higher than those of native rice starches (6.3-10.2%) and those of heat-moisture treated rice starches (18.5-23.9%). The acid and heat-moisture treatments reduced swelling power and viscosity, but increased solubility of the starches, while the crystalline structure did not change. Among the organic acids used, citric acid had the most impact on starch characteristics and RS formation, followed by lactic acid and acetic acid. The results are useful in production of RS for functional food application. Copyright © 2015 Elsevier Ltd. All rights reserved.

Inter- and intra-species variability in heat resistance and the effect of heat treatment intensity on subsequent growth of Byssochlamys fulva and Byssochlamys nivea.

PubMed

Santos, Juliana L P; Samapundo, Simbarashe; Gülay, Sonay M; Van Impe, Jan; Sant'Ana, Anderson S; Devlieghere, Frank

2018-04-21

The major aims of this study were to assess inter- and intra-species variability of heat resistant moulds (HRMs), Byssochlamys fulva and Byssochlamys nivea, with regards to (i) heat resistance and (ii) effect of heat treatment intensity on subsequent outgrowth. Four-week-old ascospores were suspended in buffered glucose solution (13° Brix, pH 3.5) and heat treated in a thermal cycler adjusted at 85 °C, 90 °C and 93 °C. Two variants of the Weibull model were fitted to the survival data and the following inactivation parameters estimated: b (inactivation rate, min -1 ), n (curve shape) and δ (the time taken for first decimal reduction, min). In addition to the assessment of heat resistance, outgrowth of Byssochlamys sp. from ascospores heated at 70 °C, 75 °C, 80 °C, 85 °C and 90 °C for 10 min and at 93 °C for 30 and 70 s was determined at 22 °C for up to 30 days. The Baranyi and Roberts model was fitted to the growth data to estimate the radial growth rates (μ max , mm.day -1 ) and lag times (λ, days). Inter-species variability and significant differences (p < 0.05) were observed for both inactivation and growth estimated parameters among B. fulva and B. nivea strains. The effect of heat treatment intensity on outgrowth of B. fulva strains was more apparent at the most intense heat treatment evaluated (90 °C/10 min), which was also the condition in which greater dispersion of the estimated kinetic parameters was observed. On the other hand, B. nivea strains were more affected by heating, resulting in greater variability of growth parameters estimated at different heating intensities and in very long lag phases (up to 25 days). The results show that inter- and intra-species variability in the kinetic parameters of Byssochlamys sp. needs to be taken into account for more accurate spoilage prediction. Furthermore, the effect of thermal treatments on subsequent outgrowth from ascospores should be explored in combination with other relevant factors such as °Brix and oxygen to develop thermal processes and storage conditions which can prevent the growth of HRMs and spoilage of heat treated food products. Copyright © 2018 Elsevier B.V. All rights reserved.

KSC-04pd0388

NASA Image and Video Library

2004-03-05

KENNEDY SPACE CENTER, FLA. - At the SRB Assembly and Refurbishment Facility, STS-114 Mission Specialists Andrew Thomas (center) and Charles Camarda (right) look at a test panel of insulation material (left) cut in a liquid nitrogen process and a round aft heat seal (right) also treated in a liquid nitrogen process. At left is Mike Leppert, Manufacturing Operations project lead with United Space Alliance. The crew is at KSC for familiarization with Shuttle and mission equipment. The STS-114 mission is Logistics Flight 1, which is scheduled to deliver supplies and equipment, plus the external stowage platform, to the International Space Station.

Palladium/kieselguhr composition and method

DOEpatents

Mosley, W.C. Jr.

1993-09-28

A hydrogen-absorbing composition and method for making such a composition are described. The composition comprises a metal hydride, preferably palladium, deposited onto a porous substrate such as kieselguhr, for use in hydrogen-absorbing processes. The composition is made by immersing a substrate in a concentrated solution containing palladium, such as tetra-amine palladium nitrate. Palladium from the solution is deposited onto the porous substrate, which is preferably in the form of kieselguhr particles. The substrate is then removed from the solution, calcined, and heat treated. This process is repeated until the desired amount of palladium has been deposited onto the substrate.

Palladium/kieselguhr composition and method

DOEpatents

Mosley, Jr., Wilbur C.

1993-01-01

A hydrogen-absorbing composition and method for making such a composition. The composition comprises a metal hydride, preferably palladium, deposited onto a porous substrate such as kieselguhr, for use in hydrogen-absorbing processes. The composition is made by immersing a substrate in a concentrated solution containing palladium, such as tetra-amine palladium nitrate. Palladium from the solution is deposited onto the porous substrate, which is preferably in the form of kieselguhr particles. The substrate is then removed from the solution, calcined, and heat treated. This process is repeated until the desired amount of palladium has been deposited onto the substrate.

VOLATILE CHLORIDE PROCESS FOR THE RECOVERY OF METAL VALUES

DOEpatents

Hanley, W.R.

1959-01-01

A process is presented for recovering uranium, iron, and aluminum from centain shale type ores which contain uranium in minute quantities. The ore is heated wiih a chlorinating agent. such as chlorine, to form a volatilized stream of metal chlorides. The chloride stream is then passed through granular alumina which preferentially absorbs the volatile uranium chloride and from which the uranium may later be recovered. The remaining volatilized chlorides, chiefly those of iron and aluminum, are further treated to recover chlorine gas for recycle, and to recover ferric oxide and aluminum oxide as valuable by-products.

Fundamental Effects of Aging on Creep Properties of Solution-Treated Low-Carbon N-155 Alloy

NASA Technical Reports Server (NTRS)

Frey, D N; Freeman, J W; White, A E

1950-01-01

A method is developed whereby the fundamental mechanisms are investigated by which processing, heat treatment, and chemical composition control the properties of alloys at high temperatures. The method used metallographic examination -- both optical and electronic --studies of x-ray diffraction-line widths, intensities, and lattice parameters, and hardness surveys to evaluate fundamental structural conditions. Mechanical properties at high temperatures are then measured and correlated with these measured structural conditions. In accordance with this method, a study was made of the fundamental mechanism by which aging controlled the short-time creep and rupture properties of solution-treated low-carbon n-155 alloy at 1200 degrees F.

Diagnostics Adapted for Heat-Treating Furnace Environment

NASA Technical Reports Server (NTRS)

2005-01-01

Diagnostics developed for the in situ monitoring of rocket combustion environments were adapted for use in heat-treating furnaces. Simultaneous, in situ monitoring of the carbon monoxide, carbon dioxide, methane, water, and hydrogen concentrations in the endothermic gas of a heat-treating furnace were demonstrated under a Space Act Agreement between the NASA Lewis Research Center, the Heat Treating Network, and Akron Steel Treating Company. This endothermic gas, or "endogas," is produced in a catalytic process, where natural gas is "cracked" in the presence of air. Variations in the composition of the natural gas supplied lead to variations in the composition of the endothermic gas. These variations could lead to an unacceptable quality of steel products that are hardened through the carborization process that uses this gas. Conventional methods of monitoring the endogas include measuring the dew point of the gas and the oxygen concentration. From these data, the carbon monoxide content of the gas can be calculated. This carbon monoxide concentration creates the carbon potential needed for carburization. Several weak links are present in this approach. The oxygen monitor deteriorates over time, and the measurement might be inaccurate by 50 percent. Also, the chemistry equations, which are based on several assumptions, such as secondary species concentrations, provide only an approximate estimate of the carbon monoxide concentration. To address these weaknesses, we investigated a new method based on ordinary Raman spectroscopy, in which the carbon monoxide concentration is measured directly and in situ. This method measures the laser light scattered from the molecules. Each species interacts with the light and scatters the light at a different frequency. Spectral monitoring of the scattered light intensity at each molecular frequency of interest provides the species concentrations. One advantage over the conventional method is that several species can be monitored simultaneously. A second advantage is that the measurement is direct; there is no need to make assumptions, to filter the gas, or to calibrate the instrument. An instrument was designed consisting of a laser and a detection system within an enclosure, connected to an optical probe by fibers. For determining carbon monoxide concentration, the probe is mounted on the endothermic gas line, close to the generator. Optical fibers with a length of 150 ft have been used to transmit laser light from the instrument to the probe. There, the light is focused into the gas, and the scattered light is collected and transmitted back to the instrument where it is analyzed with a photomultiplier and lock-in amplifier. Laboratory tests have shown that with the current system the concentration of carbon monoxide, water, nitrogen, oxygen, and hydrogen in the air can be monitored with an accuracy of 1 percent. The concentration of carbon dioxide in the air can be monitored with an accuracy of 0.5 percent, and the concentration of methane with an accuracy of 0.2 percent. This instrument was taken to the Akron Steel Treating Plant, where field tests are in progress to verify the system capabilities. Planned developments are improving the accuracy, monitoring multiple locations, and reducing instrument size and cost.

Exertional heat illness: emerging concepts and advances in prehospital care.

PubMed

Pryor, Riana R; Roth, Ronald N; Suyama, Joe; Hostler, David

2015-06-01

Exertional heat illness is a classification of disease with clinical presentations that are not always diagnosed easily. Exertional heat stroke is a significant cause of death in competitive sports, and the increasing popularity of marathons races and ultra-endurance competitions will make treating many heat illnesses more common for Emergency Medical Services (EMS) providers. Although evidence is available primarily from case series and healthy volunteer studies, the consensus for treating exertional heat illness, coupled with altered mental status, is whole body rapid cooling. Cold or ice water immersion remains the most effective treatment to achieve this goal. External thermometry is unreliable in the context of heat stress and direct internal temperature measurement by rectal or esophageal probes must be used when diagnosing heat illness and during cooling. With rapid recognition and implementation of effective cooling, most patients suffering from exertional heat stroke will recover quickly and can be discharged home with instructions to rest and to avoid heat stress and exercise for a minimum of 48 hours; although, further research pertaining to return to activity is warranted.

Major role of HSP70 as a paracrine inducer of cytokine production in human oxidized LDL treated macrophages.

PubMed

Svensson, Per-Arne; Asea, Alexzander; Englund, Mikael C O; Bausero, Maria A; Jernås, Margareta; Wiklund, Olov; Ohlsson, Bertil G; Carlsson, Lena M S; Carlsson, Björn

2006-03-01

Lipid accumulation and inflammation are key hallmarks of the atherosclerotic plaque and macrophage uptake of oxidized low-density lipoprotein (oxLDL) is believed to drive these processes. Initial experiments show that supernatants from oxLDL treated macrophages could induce IL-1beta production in naïve macrophages. To search for potential paracrine mediators that could mediate this effect a DNA microarray scan of oxLDL treated human macrophages was performed. This analysis revealed that oxLDL induced activation of heat shock protein (HSP) expression. HSPs have been implicated in the development of atherosclerosis, but the exact mechanisms for this is unclear. Extracellular heat shock protein 70 (HSP70) has been shown to elicit a pro-inflammatory cytokine response in monocytes and could therefore be a potential paracrine pro-inflammatory mediator. After 24 h of oxLDL treatment there was a significant increase of HSP70 concentrations in supernatants from oxLDL treated macrophages (oxLDLsup) compared to untreated controls (P<0.05). OxLDLsup could induce both interleukin (IL)-1beta and IL-12 secretion in naïve macrophages. We also demonstrate that the effect of oxLDLsup on cytokine production and release could be blocked by inhibition of HSP70 transcription or secretion or by the use of HSP70 neutralizing antibodies. This suggests that extracellular HSP70 can mediate pro-inflammatory changes in macrophages in response to oxLDL.

Major role of HSP70 as a paracrine inducer of cytokine production in human oxidized LDL treated macrophages

PubMed Central

Svensson, Per-Arne; Asea, Alexzander; Englund, Mikael C.O.; Bausero, Maria A.; Jernås, Margareta; Wiklund, Olov; Ohlsson, Bertil G.; Carlsson, Lena M.S.; Carlsson, Björn

2006-01-01

Lipid accumulation and inflammation are key hallmarks of the atherosclerotic plaque and macrophage uptake of oxidized low-density lipoprotein (oxLDL) is believed to drive these processes. Initial experiments show that supernatants from oxLDL treated macrophages could induce IL-1β production in naïve macrophages. To search for potential paracrine mediators that could mediate this effect a DNA microarray scan of oxLDL treated human macrophages was performed. This analysis revealed that oxLDL induced activation of heat shock protein (HSP) expression. HSPs have been implicated in the development of atherosclerosis, but the exact mechanisms for this is unclear. Extracellular heat shock protein 70 (HSP70) has been shown to elicit a pro-inflammatory cytokine response in monocytes and could therefore be a potential paracrine pro-inflammatory mediator. After 24 h of oxLDL treatment there was a significant increase of HSP70 concentrations in supernatants from oxLDL treated macrophages (oxLDLsup) compared to untreated controls (P < 0.05). OxLDLsup could induce both interleukin (IL)-1β and IL-12 secretion in naïve macrophages. We also demonstrate that the effect of oxLDLsup on cytokine production and release could be blocked by inhibition of HSP70 transcription or secretion or by the use of HSP70 neutralizing antibodies. This suggests that extracellular HSP70 can mediate pro-inflammatory changes in macrophages in response to oxLDL. PMID:15993884

Risk assessment of Salmonella in Danish meatballs produced in the catering sector.

PubMed

Møller, Cleide O de A; Nauta, Maarten J; Schaffner, Donald W; Dalgaard, Paw; Christensen, Bjarke B; Hansen, Tina B

2015-03-02

A modular process risk model approach was used to assess health risks associated with Salmonella spp. after consumption of the Danish meatball product (frikadeller) produced with fresh pork in a catering unit. Meatball production and consumption were described as a series of processes (modules), starting from 1.3kg meat pieces through conversion to 70g meatballs, followed by a dose response model to assess the risk of illness from consumption of these meatballs. Changes in bacterial prevalence, concentration, and unit size were modelled within each module. The risk assessment was built using observational data and models that were specific for Salmonella spp. in meatballs produced in the catering sector. Danish meatballs are often pan-fried followed by baking in an oven before consumption, in order to reach the core temperature of 75°C recommended by the Danish Food Safety Authority. However, in practice this terminal heat treatment in the oven may be accidentally omitted. Eleven production scenarios were evaluated with the model, to test the impact of heat treatments and cooling rates at different room temperatures. The risk estimates revealed that a process comprising heat treatment of meatballs to core temperatures higher than 70°C, and subsequent holding at room temperatures lower than 20°C, for no longer than 3.5h, were very effective in Salmonella control. The current Danish Food Safety Authority recommendation of cooking to an internal temperature of 75°C is conservative, at least with respect to Salmonella risk. Survival and growth of Salmonella during cooling of meatballs not heat treated in oven had a significant impact on the risk estimates, and therefore, cooling should be considered a critical step during meatball processing. Copyright © 2014. Published by Elsevier B.V.

Anisotropic Responses of Mechanical and Thermal Processed Cast Al-Si-Mg-Cu Alloy

NASA Astrophysics Data System (ADS)

Adeosun, S. O.; Akpan, E. I.; Balogun, S. A.; Onoyemi, O. K.

2015-05-01

The effects of ambient directional rolling and heat treatments on ultimate tensile strength (UTS), hardness (HD), percent elongation (PE), and impact energy (IE) on Al-Si-Mg-Cu alloy casting with reference to inclination to rolling direction are discussed in this article. The results show that rolled and quenched (CQ) sample possess superior UTS and HD to as-cast and those of rolled and aged samples (CA). Improved IE resistance with ductility is shown by both CQ and CA samples. However, these mechanical properties are enhanced as changes in the test sample direction moved away from rolling direction for all heat-treated samples. The CQ samples displayed highest tensile strength (108 MPa) and PE (19.8%) in the 90° direction.

Method of forming oxide coatings. [for solar collector heating panels

NASA Technical Reports Server (NTRS)

Mcdonald, G. E. (Inventor)

1983-01-01

This invention is concerned with an improved plating process for covering a substrate with a black metal oxide film. The invention is particularly directed to making a heating panel for a solar collector. A compound is electrodeposited from an aqueous solution containing cobalt metal salts onto a metal substrate. This compound is converted during plating into a black, highly absorbing oxide coating which contains hydrated oxides. This is achieved by the inclusion of an oxidizing agent in the plating bath. The inclusion of an oxidizing agent in the plating bath is contrary to standard electroplating practice. The hydrated oxides are converted to oxides by treatment in a hot bath, such as boiling water. An oxidizing agent may be added to the hot liquid treating bath.

On the understanding and control of the spontaneous heating of dried tannery wastewater sludge.

PubMed

Biasin, A; Della Zassa, M; Zerlottin, M; Refosco, D; Bertani, R; Canu, P

2014-04-01

We studied the spontaneous heating of dried sludge produced by treating wastewater mainly originating from tanneries. Heating up to burning has been observed in the presence of air and moisture, starting at ambient temperature. To understand and prevent the process we combined chemical and morphological analyses (ESEM) with thermal activity monitoring in insulated vessels. Selective additions of chemicals, either to amplify or depress the reactivity, have been used to investigate and identify both the chemical mechanism causing the sludge self-heating, and a prevention or a mitigation strategy. FeS additions accelerate the onset of reactivity, while S sustains it over time. On the contrary, Ca(OH)2, Na2CO3, NaHCO3, FeCl2, EDTA, NaClO can limit, up to completely preventing, the exothermic activity. All the experimental evidences show that the reactions supporting the dried sludge self-heating involve the Fe/S/O system. The total suppression of the reactivity requires amounts of additives that are industrially incompatible with waste reduction and economics. The best prevention requires reduction or removal of S and Fe from the dried solid matrix. Copyright © 2014 Elsevier Ltd. All rights reserved.

Changes in water-soluble vitamins and antioxidant capacity of fruit juice-milk beverages as affected by high-intensity pulsed electric fields (HIPEF) or heat during chilled storage.

PubMed

Salvia-Trujillo, Laura; Morales-de la Peña, Mariana; Rojas-Graü, Alejandra; Martín-Belloso, Olga

2011-09-28

The effect of high-intensity pulsed electric fields (HIPEF) or thermal processes and refrigerated storage on water-soluble vitamins and antioxidant capacity of beverages containing fruit juices and whole (FJ-WM) or skim milk (FJ-SM) was assessed. Peroxidase (POD) and lipoxygenase (LOX) inactivation as well as color changes were also studied. High vitamin C retention was observed in HIPEF and thermally treated beverages, but a significant depletion of the vitamin during storage occurred, which was correlated with antioxidant capacity. HIPEF treatment did not affect the concentration of group B vitamins, which also remained constant over time, but thermally treated beverages showed lower riboflavin (vitamin B2) concentration. With regard to enzyme activity, thermal processing was more effective than HIPEF on POD and LOX inactivation. The color of the beverages was maintained after HIPEF processing and during storage. Consequently, HIPEF processing could be a feasible technology to attain beverages with fruit juices and milk with high vitamin content and antioxidant potential.

Fatigue curve needs for higher strength 2-1/4Cr-1Mo steel for petroleum process vessels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jaske, C.E.

This paper reviews the data needed to develop fatigue design rules for pressure vessels fabricated from heat-treated 2-1/4Cr-1Mo steel (SA-387, Grade 22, Class 2 plates and SA-336, Grade F22 forgings) that are operated or designed to operate at temperatures greater than 371 C (700F). The available data were reviewed, and the results of that review were used to develop recommendations for needed analytical and experimental work. Extension of the fatigue-curve approach currently used for temperatures up to 371 C (700F) and development of a fracture-mechanics-based, crack-growth approach were addressed. Both of these two approaches must include means for assessing themore » time-dependent effects of oxidation and/or creep when fatigue cycling occurs at low stain rates or includes hold times. The recommendations of this study provide a plan for the development of fatigue design rules for the use of heat-treated 2-1/4Cr-1Mo steel at temperatures in the range of 371 to 482 C (700 to 900 F).« less

Transport processes in magnetically confined plasmas in the nonlinear regime.

PubMed

Sonnino, Giorgio

2006-06-01

A field theory approach to transport phenomena in magnetically confined plasmas is presented. The thermodynamic field theory (TFT), previously developed for treating the generic thermodynamic system out of equilibrium, is applied to plasmas physics. Transport phenomena are treated here as the effect of the field linking the thermodynamic forces with their conjugate flows combined with statistical mechanics. In particular, the Classical and the Pfirsch-Schluter regimes are analyzed by solving the thermodynamic field equations of the TFT in the weak-field approximation. We found that, the TFT does not correct the expressions of the ionic heat fluxes evaluated by the neoclassical theory in these two regimes. On the other hand, the fluxes of matter and electronic energy (heat flow) is further enhanced in the nonlinear Classical and Pfirsch-Schluter regimes. These results seem to be in line with the experimental observations. The complete set of the electronic and ionic transport equations in the nonlinear Banana regime, is also reported. A paper showing the comparison between our theoretic results and the experimental observations in the JET machine is currently in preparation.

Using micro-patterned surfaces to inhibit settlement and biofilm formation by Bacillus subtilis.

PubMed

Chang, Siyuan; Chen, Xiaodong; Jiang, Shuo; Chen, Jinchun; Shi, Lin

2017-07-01

Biofilm is a biological complex caused by bacteria attachment to the substrates and their subsequent reproduction and secretion. This phenomenon reduces heat transfer efficiency and causes significant losses in treated sewage heat-recovering systems. This paper describes a physical approach to inhibit bacteria settlement and biofilm formation by Bacillus subtilis, which is the dominant species in treated sewage. Here, micro-patterned surfaces with different characteristics (stripe and cube) and dimensions (1-100 μm) were fabricated as surfaces of interest. Model sewage was prepared and a rotating coupon device was used to form the biofilms. Precision balance, scanning electron microscopy, and confocal laser scanning microscopy (CLSM) were employed to investigate the inhibitory effects and the mechanisms of the biofilm-surface interactions. The results have shown that surfaces with small pattern sizes (1 and 2 μm) all reduced biofilm formation significantly. Interestingly, the CLSM images showed that the surfaces do not play a role in "killing" the bacteria. These findings are useful for future development of new process surfaces on which bacteria settlement and biofilm formation can be inhibited or minimized.

49 CFR 179.201-5 - Postweld heat treatment and corrosion resistance.

Code of Federal Regulations, 2011 CFR

2011-10-01

... 49 Transportation 3 2011-10-01 2011-10-01 false Postweld heat treatment and corrosion resistance....201-5 Postweld heat treatment and corrosion resistance. (a) Tanks and attachments welded directly thereto must be postweld heat treated as a unit at the proper temperature except as indicated below. Tanks...

Oral opioid administration and hyperalgesia in patients with cancer or chronic nonmalignant pain.

PubMed

Reznikov, Igor; Pud, Dorit; Eisenberg, Elon

2005-09-01

Previous research has reported on reduced paw withdrawal latencies to heat and mechanical stimuli after parenteral administration of opioids in animals and on increased pain sensitivity in humans subsequent to postoperative infusions of short-acting opioids or in drug addicts. The aim of the present study was to explore the possibility that oral opioid treated patients with cancer-related or chronic nonmalignant pain differ in their pain sensitivity from patients treated with non-opioid analgesics. The study population consisted of 224 patients, including 142 in the opioid-treated group and 82 in the non-opioid-treated group. Pain thresholds for punctuate measured by von Frey filaments (g), mechanical pressure measured by pressure algometer (mmHg), heat stimuli measured by quantitative sensory testing (degrees C), as well as suprathreshold tonic heat pain intensity (46.5 degrees C for 1 min) measured by 0-10 numerical pain scale (NPS) were obtained at a nonpainful site (thenar eminence) in all patients. No differences between the groups were found for gender, age, duration of pain, or duration of treatment (independent variables). No significant differences between the groups were found in punctuate (difference = 17.0 g (95% CI -8.8, 42.8), P = 0.19), pressure (2.2 mmHg (-28.7, 33.2), P = 0.89) and heat (-0.3 degrees C (-1.5, 0.9), P = 0.70) pain thresholds, or in suprathreshold heat pain intensity (difference between maximal pain intensities -0.4 NPS units (95% CI -1.2, 0.4), P = 0.31). Pearson correlations within the opioid-treated group failed to show significant relationships between any of the independent variables and the outcome measures. A further comparison of the outcomes between the 'weak' opioid-treated subgroup and the 'strong' opioid-treated subgroup again revealed insignificant results. These results suggest that the administration of 'commonly used' dosages of oral opioids does not result in abnormal pain sensitivity beyond that of patients receiving non-opioid analgesia.

The technology for creating of decorative plywood with low formaldehyde emission

NASA Astrophysics Data System (ADS)

Safin, R. R.; Khasanshin, R. R.; Shaikhutdinova, A. R.; Ziatdinov, R. R.

2015-10-01

The development of new technologies of processing of industrial art products to improve their functional, ergonomic and aesthetic properties is one of the important directions of improvement of product design. The article presents the technology of preliminary contact thermal modification of sheets of veneer in the production of low-toxic decorative plywood and laminated products, which lets significantly improve their water resistance. It has been established that thermal modification of wood material causes a decrease in density with increasing temperature and duration of treatment. A mathematical model describing the process of heat treatment of wood veneer and allowing predicting the degree of thermal modification of wood material depending on the modes of modification has been developed. Several studies to determine the basic properties of plywood made on the basis of heat-treated veneer were conducted in the work. Studies have shown that the thermal effect on veneer in the manufacture of plywood provides improves water-repellent properties of it, while not increasing its toxicity. It has also been found that the alternating of layers of wood with varying degrees of heat treatment when creating laminated products greatly enhances the decorative features of the products.

Effect of the raw material type and the reaction time on the synthesis of halloysite based Zeolite Na-P1

NASA Astrophysics Data System (ADS)

Meftah, Mahdi; Oueslati, Walid; Chorfi, Nejmeddine; Ben Haj Amara, Abdesslem

Zeolites are currently one of the most important classes of inorganic materials because of their multiple applications not only as ions exchangers and molecular sieves, but also as catalysts. This works focus the synthesis and the characterization of Zeolite Na-P1 using halloysite (collected near Ain Khemouda, western Tunisia) as the starting material. Two parameters, such as the host materials type (natural or treated) and the reaction time, involved in the synthesis process are investigated. The intermediate phases and final products were characterized by X-ray diffraction, Infrared IR spectroscopy, scanning electron microscopy and high-resolution 29Si and 27Al MAS NMR. Obtained results show that the hydrothermal synthesis from natural and heated-halloysite leads to formation of homogenous Zeolite Na-P1. The difference in the crystallization/transformation time process is explained by the effect of the dissolution rate of the starting materials in sodium hydroxide solution. In the case of heated halloysite, the synthesis reaction with alkali solution occurs very readily and achieved without prior thermal activation at high temperature. The optimal conditions of Zeolite Na-P1 crystallization, from heated-halloysite, are reached at 120 °C.

Development of microstructure and mechanical properties during annealing of a cold-swaged Co-Cr-Mo alloy rod.

PubMed

Mori, Manami; Sato, Nanae; Yamanaka, Kenta; Yoshida, Kazuo; Kuramoto, Koji; Chiba, Akihiko

2016-12-01

In this study, we investigated the evolution of the microstructure and mechanical properties during annealing of a cold-swaged Ni-free Co-Cr-Mo alloy for biomedical applications. A Co-28Cr-6Mo-0.14N-0.05C (mass%) alloy rod was processed by cold swaging, with a reduction in area of 27.7%, and then annealed at 1173-1423K for various periods up to 6h. The duplex microstructure of the cold-swaged rod consisted of a face-centered cubic γ-matrix and hexagonal closed-packed ε-martensite developed during cold swaging. This structure transformed nearly completely to the γ-phase after annealing and many annealing twin boundaries were observed as a result of the heat treatment. A small amount of the ε-phase was identified in specimens annealed at 1173K. Growth of the γ-grains occurred with increasing annealing time at temperatures ≥1273K. Interestingly, the grain sizes remained almost unchanged at 1173K and a very fine grain size of approximately 8μm was obtained. The precipitation that occurred during annealing was attributed to the limited grain coarsening during heat treatment. Consequently, the specimens treated at this temperature showed the highest tensile strength and lowest ductility among the specimens prepared. An elongation-to-failure value larger than 30% is sufficient for the proposed applications. The other specimens treated at higher temperatures possessed similar tensile properties and did not show any significant variations with different annealing times. Optimization of the present rod manufacturing process, including cold swaging and interval annealing heat treatment, is discussed. Copyright © 2016 Elsevier Ltd. All rights reserved.

Characterization of polyparaphenylene subjected to different heat treatment temperatures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Brown, S.D.M.; Matthews, M.J.; Marucci, A.

1998-07-01

The authors investigated the structural and electronic properties of samples of polyparaphenylene (PPP), derived from two synthesis methods (the Kovacic and Yamamoto methods). These samples have been subjected to different heat-treatment temperatures (650 C {le} T{sub HT} {le} 2,000 C) and their properties are compared to the polymer prior to heat-treatment (T{sub HT} = 0 C). The photoluminescence (PL) spectra of heat-treated PPP based on the two synthesis methods reflects the differences in electronic structure of the starting polymers. The PL emission from the heat-treated Yamamoto polymer is quenched at much lower T{sub HT} than from the Kovacic material. However,more » Raman spectra taken of the material resulting from heat-treatment of the polymer (using both preparation methods) indicate the presence of phonon modes for PPP in samples at T{sub HT} up to 650 C.« less

Quality of cut lettuce treated by heat shock: prevention of enzymatic browning, repression of phenylalanine ammonia-lyase activity, and improvement on sensory evaluation during storage.

PubMed

Murata, Masatsune; Tanaka, Eriko; Minoura, Emiko; Homma, Seiichi

2004-03-01

Stored cut lettuce gradually turns brown on the cut section after several days of storage, because cutting induces phenylalanine ammonia-lyase (PAL) activity, the biosynthesis of polyphenol is promoted, and the polyphenols are oxidized by polyphenol oxidase. Here, the effect of heat shock treatment at 50 degrees C for 90 s on the quality of cut lettuce during cold storage was examined. The heat shock treatment significantly repressed the induction of PAL activity and phenolics accumulation in cut lettuce during storage, and prevented the browning of cut lettuce. Ascorbic acid content was not affected by the heat shock treatment. The sensory analysis showed that the organoleptic quality of cut lettuce treated by heat shock was significantly better than that of the control cut lettuce. These results show that heat shock treatment is useful for prolonging the shelf life of cut lettuce.

Heat and mass transport during a groundwater replenishment trial in a highly heterogeneous aquifer

NASA Astrophysics Data System (ADS)

Seibert, Simone; Prommer, Henning; Siade, Adam; Harris, Brett; Trefry, Mike; Martin, Michael

2014-12-01

Changes in subsurface temperature distribution resulting from the injection of fluids into aquifers may impact physiochemical and microbial processes as well as basin resource management strategies. We have completed a 2 year field trial in a hydrogeologically and geochemically heterogeneous aquifer below Perth, Western Australia in which highly treated wastewater was injected for large-scale groundwater replenishment. During the trial, chloride and temperature data were collected from conventional monitoring wells and by time-lapse temperature logging. We used a joint inversion of these solute tracer and temperature data to parameterize a numerical flow and multispecies transport model and to analyze the solute and heat propagation characteristics that prevailed during the trial. The simulation results illustrate that while solute transport is largely confined to the most permeable lithological units, heat transport was also affected by heat exchange with lithological units that have a much lower hydraulic conductivity. Heat transfer by heat conduction was found to significantly influence the complex temporal and spatial temperature distribution, especially with growing radial distance and in aquifer sequences with a heterogeneous hydraulic conductivity distribution. We attempted to estimate spatially varying thermal transport parameters during the data inversion to illustrate the anticipated correlations of these parameters with lithological heterogeneities, but estimates could not be uniquely determined on the basis of the collected data.

Heat Shock Protein 90 Inhibitor Decreases Collagen Synthesis of Keloid Fibroblasts and Attenuates the Extracellular Matrix on the Keloid Spheroid Model.

PubMed

Lee, Won Jai; Lee, Ju Hee; Ahn, Hyo Min; Song, Seung Yong; Kim, Yong Oock; Lew, Dae Hyun; Yun, Chae-Ok

2015-09-01

The 90-kDa heat-shock protein (heat-shock protein 90) is an abundant cytosolic chaperone, and inhibition of heat-shock protein 90 by 17-allylamino-17-demethoxygeldanamycin (17-AAG) compromises transforming growth factor (TGF)-β-mediated transcriptional responses by enhancing TGF-β receptor I and II degradation, thus preventing Smad2/3 activation. In this study, the authors evaluated whether heat-shock protein 90 regulates TGF-β signaling in the pathogenesis and treatment of keloids. Keloid fibroblasts were treated with 17-AAG (10 μM), and mRNA levels of collagen types I and III were determined by real-time reverse- transcriptase polymerase chain reaction. Also, secreted TGF-β1 was assessed by enzyme-linked immunosorbent assay. The effect of 17-AAG on protein levels of Smad2/3 complex was determined by Western blot analysis. In addition, in 17-AAG-treated keloid spheroids, the collagen deposition and expression of major extracellular matrix proteins were investigated by means of Masson trichrome staining and immunohistochemistry. The authors found that heat-shock protein 90 is overexpressed in human keloid tissue compared with adjacent normal tissue, and 17-AAG decreased mRNA levels of type I collagen, secreted TGF-ß1, and Smad2/3 complex protein expression in keloid fibroblasts. Masson trichrome staining revealed that collagen deposition was decreased in 17-AAG-treated keloid spheroids, and immunohistochemical analysis showed that expression of collagen types I and III, elastin, and fibronectin was markedly decreased in 17-AAG-treated keloid spheroids. These results suggest that the antifibrotic action of heat-shock protein 90 inhibitors such as 17-AAG may have therapeutic effects on keloids.

Correlation of x-ray diffraction and Mössbauer effect measurements with magnetic properties of heat-treated Cu80Co15Fe5 ribbons

NASA Astrophysics Data System (ADS)

Harris, V. G.; Rubinstein, M.; Das, B. N.; Koon, N. C.

1994-05-01

X-ray diffraction (XRD) and Mössbauer Effect (ME) measurements were performed on heat-treated Cu80Co15Fe5 melt-spun ribbons in an attempt to understand the trends in magnetic properties with heat treatment. ME measurements indicate that the majority of Fe atoms (86%) occupy sites in ferromagnetic FCC CoFe clusters after the initial quench. A heat treatment at 900 °C acts to complete the chemical separation of Fe from the Cu matrix. The presence of Co in the Cu matrix, even after high temperature anneals, provides a paramagnetic component that prohibits saturation even at high fields.