Epitaxial growth of iridate pyrochlore Nd 2Ir 2O 7 films

DOE PAGES

Gallagher, J. C.; Esser, B. D.; Morrow, R.; ...

2016-02-29

Epitaxial films of the pyrochlore Nd 2Ir 2O 7 have been grown on (111)-oriented yttria-stabilized zirconia (YSZ) substrates by off-axis sputtering followed by post-growth annealing. X-ray diffraction (XRD) results demonstrate phase-pure epitaxial growth of the pyrochlore films on YSZ. Scanning transmission electron microscopy (STEM) investigation of an Nd 2Ir 2O 7 film with a short post-annealing provides insight into the mechanism for crystallization of Nd 2Ir 2O 7 during the post-annealing process. STEM images reveal clear pyrochlore ordering of Nd and Ir in the films. As a result, the epitaxial relationship between the YSZ and Nd 2Ir 2O 7 ismore » observed clearly while some interfacial regions show a thin region with polycrystalline Ir nanocrystals.« less

Modifications of structural and physical properties induced by swift heavy ions in Gd2Ti2O7 and Y2Ti2O7 pyrochlores

NASA Astrophysics Data System (ADS)

Sellami, N.; Sattonnay, G.; Grygiel, C.; Monnet, I.; Debelle, A.; Legros, C.; Menut, D.; Miro, S.; Simon, P.; Bechade, J. L.; Thomé, L.

2015-12-01

The structural transformations induced by ionization processes in Gd2Ti2O7 and Y2Ti2O7 pyrochlores irradiated with swift heavy ions have been studied using XRD and Raman experiments. Results show that irradiation induces amorphization and that the phase transformation build-up can be accounted for in the framework of a model involving a single-impact mechanism. The radiation induced amorphization build-up is faster in Gd2Ti2O7 than in Y2Ti2O7. Moreover, a decrease of the thermal conductivity (measured by the laser flash method) is induced by irradiation both in Gd2Ti2O7 and Y2Ti2O7.

Effects of Doping on Thermal Conductivity of Pyrochlore Oxides for Advanced Thermal Barrier Coatings

NASA Technical Reports Server (NTRS)

Bansal, Narottam P.; Zhu, Dongming; Eslamloo-Grami, Maryam

2006-01-01

Pyrochlore oxides of general composition, A2B2O7, where A is a 3(+) cation (La to Lu) and B is a 4(+) cation (Zr, Hf, Ti, etc.) have high melting point, relatively high coefficient of thermal expansion, and low thermal conductivity which make them suitable for applications as high-temperature thermal barrier coatings. The effect of doping at the A site on the thermal conductivity of a pyrochlore oxide La2Zr2O7, has been investigated. Oxide powders of various compositions La2Zr2O7, La(1.7)Gd(0.3)Zr2O7, La(1.7)Yb(0.3)Zr2O7 and La(1.7)Gd(0.15)Yb(0.15)Zr2O7 were synthesized by the citric acid sol-gel method. These powders were hot pressed into discs and used for thermal conductivity measurements using a steady-state laser heat flux test technique. The rare earth oxide doped pyrochlores La(1.7)Gd(0.3)Zr2O7, La(1.7)Yb(0.3)Zr2O7 and La(1.7)Gd(0.15)Yb(0.15)Zr2O7 had lower thermal conductivity than the un-doped La2Zr2O7. The Gd2O3 and Yb2O3 co-doped composition showed the lowest thermal conductivity.

Structural, photoluminescence and radioluminescence properties of Eu{sup 3+} doped La{sub 2}Hf{sub 2}O{sub 7} nanoparticles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wahid, Kareem; Pokhrel, Madhab; Mao, Yuanbing, E-mail: yuanbing.mao@utrgv.edu

This study presents the structural, optical, and radioluminescent characterization of newly synthesized europium-doped lanthanum hafnate (La{sub 2}Hf{sub 2}O{sub 7}:xmol%Eu{sup 3+}, x=0 to 35) nanoparticles (NPs) for use as phosphors and scintillation materials. Samples prepared through a combined co-precipitation and molten salt synthetic process were found to crystalize in the pyrochlore phase, a radiation tolerant structure related to the fluorite structure. These samples exhibit red luminescence under ultraviolet and X-ray excitation. Under these excitations, the optical intensity and quantum yield of the La{sub 2}Hf{sub 2}O{sub 7}:xmol%Eu{sup 3+} NPs depend on the Eu{sup 3+} concentration and are maximized at 5%. It ismore » proposed that there is a trade-off between the quenching due to defect states/cross-relaxation and dopant concentration. An optimal dopant concentration allows the La{sub 2}Hf{sub 2}O{sub 7}:5 mol%Eu{sup 3+} NPs to show the best luminescent properties of all the samples. - Graphical abstract: Incident X-ray and UV photons interact with La{sub 2}Hf{sub 2}O{sub 7}: xmol%Eu{sup 3+}(x=1–35) nanoparticles (NPs) to yield strong red luminescence centered at 612 nm. Colored spheres inside NP diagram represent pyrochlore coordination environment of La{sub 2}Hf{sub 2}O{sub 7}:xmol%Eu{sup 3+}. Blue, red, yellow, green and black spheres represent hafnium(IV) atoms, lanthanum(III)/europium(III) atoms, oxygen atoms at 48f site, oxygen atoms at 8b site and oxygen vacancies, respectively. - Highlights: • La{sub 2}Hf{sub 2}O{sub 7}:xmol%Eu{sup 3+} (x=0–35) nanoparticles with weakly-ordered pyrochlore structures were synthesized. • Optically and X-ray excited emission spectra showed strong luminescence centered at 612 nm. • Photoluminescence quantum yield increases with doping concentration up to 5% and decreases at higher concentrations.« less

Pyrochlore structure and spectroscopic studies of titanate ceramics. A comparative investigation on SmDyTi2O7 and YDyTi2O7 solid solutions

NASA Astrophysics Data System (ADS)

Garbout, A.; Férid, M.

2018-06-01

Considering the features in changing the structure and properties of rare earth titanates pyrochlores, the substituted Dy2Ti2O7 may be very attractive for various applications. Effect of Sm and Y substitution on the structural properties of Dy2Ti2O7 ceramic was established. These ceramics were prepared by solid-state reaction and characterized by X-ray diffraction and Raman spectroscopy. Both analysis show that YDyTi2O7 with the pyrochlore structure is obtained after heating at 1400 °C, but SmDyTi2O7 has already formed after sintering at 1200 °C. SEM images revealed that the average grain size was increased with the increase of heating temperature, and an un-homogeneous grain growth was detected. The average size was about 37 nm and 135 nm for the SmDyTi2O7 and YDyTi2O7 particles, respectively. Structural Rietveld refinements indicate that all prepared ceramics crystallize in cubic structure with space group of Fd3m. The refined cell parameters demonstrate an almost linear correlation with the ionic radius of Ln3+. The vibrational spectra revealed that the positions of bands are sensitive to the Ln3+-ionic radius, and the Tisbnd O bond strength decreased linearly with the increase of cubic lattice parameter. Raman spectra indicate that the wavenumber of Osbnd Tisbnd O bending mode is considerably shifted to lower region with increasing in mass of the Ln atom. This paper provides solid foundations for additional research of these solid solutions, which are very attractive for different fields as promising catalytic compounds for combustion applications or as frustrated magnetic pyrochlore ceramics.

High thermal stability of La 2O 3 and CeO 2-stabilized tetragonal ZrO 2

DOE PAGES

Wang, Shichao; Xie, Hong; Lin, Yuyuan; ...

2016-02-15

Catalyst support materials of tetragonal ZrO 2, stabilized by either La 2O 3 (La 2O 3-ZrO 2) or CeO 2 (CeO 2-ZrO 2), were synthesized under hydrothermal conditions at 200 °C with NH 4OH or tetramethylammonium hydroxide as the mineralizer. From In Situ synchrotron powder X-ray diffraction and small-angle X-ray scattering measurements, the calcined La 2O 3-ZrO 2 and CeO 2-ZrO 2 supports were nonporous nanocrystallites that exhibited rectangular shapes with thermal stability up to 1000 °C in air. These supports had an average size of ~10 nm and a surface area of 59-97 m 2/g. The catalysts Pt/La 2Omore » 3-ZrO 2 and Pt/CeO 2-ZrO 2 were prepared by using atomic layer deposition with varying Pt loadings from 6.3-12.4 wt %. Mono-dispersed Pt nanoparticles of ~3 nm were obtained for these catalysts. As a result, the incorporation of La 2O 3 and CeO 2 into the t-ZrO 2 structure did not affect the nature of the active sites for the Pt/ZrO 2 catalysts for the water-gas-shift (WGS) reaction.« less

Microstructure and dielectric properties of pyrochlore Bi2Ti2O7 thin films

NASA Astrophysics Data System (ADS)

Cagnon, Joël; Boesch, Damien S.; Finstrom, Nicholas H.; Nergiz, Saide Z.; Keane, Sean P.; Stemmer, Susanne

2007-08-01

Bi2Ti2O7 thin films were grown by radio-frequency magnetron sputtering on bare and Pt-coated sapphire substrates at low substrate temperatures (˜200 °C). Postdeposition anneals were carried out at different temperatures to crystallize the films. Nearly phase-pure Bi2Ti2O7 thin films with the cubic pyrochlore structure were obtained at annealing temperatures up to 800 °C. Impurity phases, in particular Bi4Ti3O12, formed at higher temperatures. At 1 MHz, the dielectric constants were about 140-150 with a very small tunability and the dielectric loss was about 4×10-3. The dielectric loss increased with frequency. The dielectric properties of Bi2Ti2O7 films are compared to those of pyrochlore bismuth zinc niobate films.

Ab initio molecular dynamics simulations of ion-solid interactions in zirconate pyrochlores

DOE PAGES

Xiao, Haiyan Y.; Weber, William J.; Zhang, Yanwen; ...

2015-01-31

In this paper, an ab initio molecular dynamics method is employed to study low energy recoil events in zirconate pyrochlores (A 2Zr 2O 7, A = La, Nd and Sm). It shows that both cations and anions in Nd 2Zr 2O 7 and Sm 2Zr 2O 7 are generally more likely to be displaced than those in La 2Zr 2O 7. The damage end states mainly consist of Frenkel pair defects, and the Frenkel pair formation energies in Nd 2Zr 2O 7 and Sm 2Zr 2O 7 are lower than those in La 2Zr 2O 7. These results suggest thatmore » the order–disorder structural transition more easily occurs in Nd 2Zr 2O 7 and Sm 2Zr 2O 7 resulting in a defect-fluorite structure, which agrees well with experimental observations. Our calculations indicate that oxygen migration from 48f and 8b to 8a sites is dominant under low energy irradiation. A number of new defects, including four types of cation Frenkel pairs and six types of anion Frenkel pairs, are revealed by ab initio molecular dynamics simulations. The present findings may help to advance the fundamental understanding of the irradiation response behavior of zirconate pyrochlores.« less

X-ray scattering studies of structural phase transitions in pyrochlore Cd2Nb2O7

NASA Astrophysics Data System (ADS)

Tachibana, Makoto; Fritsch, Katharina; Gaulin, Bruce D.

2013-10-01

Structural phase transitions in pyrochlore Cd2Nb2O7 were studied by means of single crystal x-ray scattering. On cooling below the ferroelastic transition at T1 = 204 K, the cubic Bragg peaks broaden in a manner consistent with weak orthorhombic distortion. The distortion evolves rather smoothly through the ferroelectric transition at T2 = 196 K, which explains the absence of sharp anomalies in the heat capacity and dielectric constant at this transition. At lower temperatures, the anomalous relaxor-like character of this compound is evident as a gradual reduction in the Bragg peak intensities, which continues down to the onset of another transition at T3 = 85 K. The studies of two Bragg peaks that are forbidden within the cubic phase reveal an interesting disparity: while the intensity for one of them increases in a classical mean-field manner below T1, the other shows unconventional behavior that is reminiscent of the pyrochlore superconductor Cd2Re2O7.

Spin-orbit-driven magnetic structure and excitation in the 5d pyrochlore Cd 2Os 2O 7

DOE PAGES

Calder, Stuart A; Vale, James G.; Bogdanov, Nikolay; ...

2016-06-07

Here, much consideration has been given to the role of spin-orbit coupling (SOC) in 5d oxides, particularly on the formation of novel electronic states and manifested metal-insulator transitions (MITs). SOC plays a dominant role in 5d 5 iridates (Ir 4+), undergoing MITs both concurrent (pyrochlores) and separated (perovskites) from the onset of magnetic order. However, the role of SOC for other 5d configurations is less clear. For example, 5d 3 (Os 5+) systems are expected to have an orbital singlet with reduced effective SOC. The pyrochlore Cd 2Os 2O 7 nonetheless exhibits a MIT entwined with magnetic order phenomenologically similarmore » to pyrochlore iridates. Here, we resolve the magnetic structure in Cd 2Os 2O 7 with neutron diffraction and then via resonant inelastic X-ray scattering determine the salient electronic and magnetic energy scales controlling the MIT. In particular, SOC plays a subtle role in creating the electronic ground state but drives the magnetic order and emergence of a multiple spin-flip magnetic excitation.« less

Uranium luminescence in La2 Zr2 O7 : effect of concentration and annealing temperature.

PubMed

Mohapatra, M; Rajeswari, B; Hon, N S; Kadam, R M

2016-12-01

The speciation of a particular element in any given matrix is a prerequisite to understanding its solubility and leaching properties. In this context, speciation of uranium in lanthanum zirconate pyrochlore (La 2 Zr 2 O 7  = LZO), prepared by a low-temperature combustion route, was carried out using a simple photoluminescence lifetime technique. The LZO matrix is considered to be a potential ceramic host for fixing nuclear and actinide waste products generated during the nuclear fuel cycle. Special emphasis has been given to understanding the dynamics of the uranium species in the host as a function of annealing temperature and concentration. It was found that, in the LZO host, uranium is stabilized as the commonly encountered uranyl species (UO 2 2+ ) up to a heat treatment of 500 °C at the surface. Above 500 °C, the uranyl ion is diffused into the matrix as the more symmetric octahedral uranate species (UO 6 6- ). The uranate ions thus formed replace the six-coordinated 'Zr' atoms at regular lattice positions. Further, it was observed that concentration quenching takes place beyond 5 mol% of uranium doping. The mechanism of the quenching was found to be a multipolar interaction. Copyright © 2016 John Wiley & Sons, Ltd. Copyright © 2016 John Wiley & Sons, Ltd.

Quantum origins of moment fragmentation in Nd2Zr2O7

NASA Astrophysics Data System (ADS)

Benton, Owen

2016-09-01

Spin-liquid states are often described as the antithesis of magnetic order. Recently, however, it has been proposed that in certain frustrated magnets the magnetic degrees of freedom may "fragment" in such a way as to give rise to a coexistence of spin liquid and ordered phases. Recent neutron-scattering results [S. Petit, E. Lhotel, B. Canals, M. Ciomaga Hatnean, J. Ollivier, H. Muttka, E. Ressouche, A. R. Wildes, M. R. Lees, and G. Balakrishnan, Nat. Phys. 12, 746 (2016), 10.1038/nphys3710] suggest that this scenario may be realized in the pyrochlore magnet Nd2Zr2O7 . These observations show the characteristic pinch-point features of a Coulombic spin liquid occurring alongside the Bragg peaks of an "all-in-all-out" ordered state. Here we explain the quantum origins of this apparent magnetic moment fragmentation, within the framework of a quantum model of nearest-neighbor exchange, appropriate to Nd2Zr2O7 . This model is able to capture both the ground-state order and the pinch points observed at finite energy. The observed fragmentation arises due to the combination of the unusual symmetry properties of the Nd3 + ionic wave functions and the structure of equations of motion of the magnetic degrees of freedom. The results of our analysis suggest that Nd2Zr2O7 is proximate to a U (1 ) spin-liquid phase and is a promising candidate for the observation of a Higgs transition in a magnetic system.

Structural transformations and disordering in zirconolite (CaZrTi2O7) at high pressure.

PubMed

Salamat, Ashkan; McMillan, Paul F; Firth, Steven; Woodhead, Katherine; Hector, Andrew L; Garbarino, Gaston; Stennett, Martin C; Hyatt, Neil C

2013-02-04

There is interest in identifying novel materials for use in radioactive waste applications and studying their behavior under high pressure conditions. The mineral zirconolite (CaZrTi(2)O(7)) exists naturally in trace amounts in diamond-bearing deep-seated metamorphic/igneous environments, and it is also identified as a potential ceramic phase for radionuclide sequestration. However, it has been shown to undergo radiation-induced metamictization resulting in amorphous forms. In this study we probed the high pressure structural properties of this pyrochlore-like structure to study its phase transformations and possible amorphization behavior. Combined synchrotron X-ray diffraction and Raman spectroscopy studies reveal a series of high pressure phase transformations. Starting from the ambient pressure monoclinic structure, an intermediate phase with P2(1)/m symmetry is produced above 15.6 GPa via a first order transformation resulting in a wide coexistence range. Upon compression to above 56 GPa a disordered metastable phase III with a cotunnite-related structure appears that is recoverable to ambient conditions. We examine the similarity between the zirconolite behavior and the structural evolution of analogous pyrochlore systems under pressure.

Defect formation energy in pyrochlore: the effect of crystal size

NASA Astrophysics Data System (ADS)

Wang, Jianwei; Ewing, Rodney C.; Becker, Udo

2014-09-01

Defect formation energies of point defects of two pyrochlores Gd2Ti2O7 and Gd2Zr2O7 as a function of crystal size were calculated. Density functional theory with plane-wave basis sets and the projector-augmented wave method were used in the calculations. The results show that the defect formation energies of the two pyrochlores diverge as the size decreases to the nanometer range. For Gd2Ti2O7 pyrochlore, the defect formation energy is higher at nanometers with respect to that of the bulk, while it is lower for Gd2Zr2O7. The lowest defect formation energy for Gd2Zr2O7 is found at 15-20 Å. The different behaviors of the defect formation energies as a function of crystal size are caused by different structural adjustments around the defects as the size decreases. For both pyrochlore compositions at large sizes, the defect structures are similar to those of the bulk. As the size decreases, for Gd2Ti2O7, additional structure distortions appear at the surfaces, which cause the defect formation energy to increase. For Gd2Zr2O7, additional oxygen Frenkel pair defects are introduced, which reduce the defect formation energy. As the size further decreases, increased structure distortions occur at the surfaces, which cause the defect formation energy to increase. Based on a hypothesis that correlates the energetics of defect formation and radiation response for complex oxides, the calculated results suggest that at nanometer range Gd2Ti2O7 pyrochlore is expected to have a lower radiation tolerance, and those of Gd2Zr2O7 pyrochlore to have a higher radiation tolerance. The highest radiation tolerance for Gd2Zr2O7 pyrochlore is expected to be found at ˜2 nanometers.

Bubble Formation and Lattice Parameter Changes Resulting from He Irradiation of Defect-Fluorite Gd2Zr2O7

DOE Office of Scientific and Technical Information (OSTI.GOV)

Taylor, Caitlin A.; Patel, Maulik K.; Aguiar, Jeffery A.

2016-08-15

Pyrochlores have long been considered as potential candidates for advanced ceramic waste-forms for the immobilization of radioactive waste nuclides. This work provides evidence that Gd2Zr2O7, often considered the most radiation tolerant pyrochlore, could be susceptible to radiation damage in the form of bubble nucleation at the highest He doses expected over geological time. Ion irradiations were utilized to experimentally simulate the radiation damage and He accumulation produced by ..alpha..-decay. Samples were pre-damaged using 7 MeV Au3+ to induce the pyrochlore to defect-fluorite phase transformation, which would occur due to ..alpha..-recoil damage within several hundred years of storage in a Gd2Zr2O7more » waste-form. These samples were then implanted to various He concentrations in order to study the long-term effects of He accumulation. Helium bubbles 1-3 nm in diameter were observed in TEM at a concentration of 4.6 at.% He. Some bubbles remained isolated, while others formed chains 10-30 nm in length parallel to the surface. GIXRD measurements showed lattice swelling after irradiating pristine Gd2Zr2O7 with 7 MeV Au3+ to a fluence of 2.2 x 1015 Au/cm2. An increase in lattice swelling was also measured after 2.2 x 1015 Au/cm2 + 2 x 1015 He/cm2 and 2.2 x 1015 Au/cm2 + 2 x 1016 He/cm2. A decrease in lattice swelling was measured after irradiation with 2.2 x 1015 Au/cm2 + 2 x 1017 He/cm2, the fluence where bubbles and bubble chains were observed in TEM. Bubble chains are thought to form in order to reduce lattice strain normal to the surface, which is produced by the Au and He irradiation damage.« less

Orange-red emitting Gd2Zr2O7:Sm3+: Structure-property correlation, optical properties and defect spectroscopy

NASA Astrophysics Data System (ADS)

Gupta, Santosh K.; Reghukumar, C.; Sudarshan, K.; Ghosh, P. S.; Pathak, Nimai; Kadam, R. M.

2018-05-01

Local structure analysis of dopant ion, understanding host to dopant energy transfer dynamics and defects characterization in a doped material which plays an important role in the designing a highly efficient opto-electronic material. In this connection a new Sm3+ doped Gd2Zr2O7 pyrochlore material was synthesized using gel-combustion technique and was characterized systematically using X-ray diffraction (XRD), time resolved photoluminescence spectroscopy (TRPLS), positron annihilation lifetime spectroscopy (PALS) and density functional theory (DFT) based ab-initio calculation. Based on DFT site selective energetics calculation and luminescence decay measurement, it was observed that the Sm3+ was distributed at both Gd3+ and Zr4+ site with higher Sm3+ fraction at the Gd3+ site. PALS was used to probe the presence of defects in the phosphor. In this work intense orange-red emission is realized through manipulating the energy transfer from host defect emission (oxygen vacancies) to Sm3+ which allows color emission from green in undoped to orange-red in doped samples. Effect of dopant concentration and annealing temperature was probed using TRPLS and PALS. These all information is highly important for researcher looking to achieve pyrochlore based phosphor materials with high quantum yield.

High pressure phase transitions and compressibilities of Er2Zr2O7 and Ho2Zr2O7

NASA Astrophysics Data System (ADS)

Zhang, F. X.; Lang, M.; Becker, U.; Ewing, R. C.; Lian, J.

2008-01-01

Phase stability and compressibility of rare earth zirconates with the defect-fluorite structure were investigated by in situ synchrotron x-ray diffraction. A sluggish defect-fluorite to a cotunnitelike phase transformation occurred at pressures of ˜22 and ˜30GPa for Er2Zr2O7 and Ho2Zr2O7, respectively. Enhanced compressibility was found for the high pressure phase as a result of increasing cation coordination number and cation-anion bond length.

Pressure-induced structural modifications of rare-earth hafnate pyrochlore

NASA Astrophysics Data System (ADS)

Turner, Katlyn M.; Rittman, Dylan R.; Heymach, Rachel A.; Tracy, Cameron L.; Turner, Madison L.; Fuentes, Antonio F.; Mao, Wendy L.; Ewing, Rodney C.

2017-06-01

Complex oxides with the pyrochlore (A2B2O7) and defect-fluorite ((A,B)4O7) structure-types undergo structural transformations under high-pressure. Rare-earth hafnates (A2Hf2O7) form the pyrochlore structure for A  =  La-Tb and the defect-fluorite structure for A  =  Dy-Lu. High-pressure transformations in A2Hf2O7 pyrochlore (A  =  Sm, Eu, Gd) and defect-fluorite (A  =  Dy, Y, Yb) were investigated up to ~50 GPa and characterized by in situ Raman spectroscopy and synchrotron x-ray diffraction (XRD). Raman spectra at ambient pressure revealed that all compositions, including the defect-fluorites, have some pyrochlore-type short-range order. In situ high-pressure synchrotron XRD showed that all of the rare earth hafnates investigated undergo a pressure-induced phase transition to a cotunnite-like (orthorhombic) structure that begins between 18 and 25 GPa. The phase transition to the cotunnite-like structure is not complete at 50 GPa, and upon release of pressure, the hafnates transform to defect-fluorite with an amorphous component. For all compositions, in situ Raman spectroscopy showed that disordering occurs gradually with increasing pressure. Pyrochlore-structured hafnates retain their short-range order to a higher pressure (30 GPa vs.  <10 GPa) than defect-fluorite-structured hafnates. Rare earth hafnates quenched from 50 GPa show Raman spectra consistent with weberite-type structures, as also reported for irradiated rare-earth stannates. The second-order Birch-Murnaghan equation of state fit gives a bulk modulus of ~250 GPa for hafnates with the pyrochlore structure, and ~400 GPa for hafnates with the defect-fluorite structure. Dy2Hf2O7 is intermediate in its response, with some pyrochlore-type ordering, based on Raman spectroscopy and the equation of state, with a bulk modulus of ~300 GPa. As predicted based on the similar ionic radius of Zr4+ and Hf4+, rare-earth hafnates show similar behavior to that

Pressure-induced structural modifications of rare-earth hafnate pyrochlore.

PubMed

Turner, Katlyn M; Rittman, Dylan R; Heymach, Rachel A; Tracy, Cameron L; Turner, Madison L; Fuentes, Antonio F; Mao, Wendy L; Ewing, Rodney C

2017-06-28

Complex oxides with the pyrochlore (A 2 B 2 O 7 ) and defect-fluorite ((A,B) 4 O 7 ) structure-types undergo structural transformations under high-pressure. Rare-earth hafnates (A 2 Hf 2 O 7 ) form the pyrochlore structure for A  =  La-Tb and the defect-fluorite structure for A  =  Dy-Lu. High-pressure transformations in A 2 Hf 2 O 7 pyrochlore (A  =  Sm, Eu, Gd) and defect-fluorite (A  =  Dy, Y, Yb) were investigated up to ~50 GPa and characterized by in situ Raman spectroscopy and synchrotron x-ray diffraction (XRD). Raman spectra at ambient pressure revealed that all compositions, including the defect-fluorites, have some pyrochlore-type short-range order. In situ high-pressure synchrotron XRD showed that all of the rare earth hafnates investigated undergo a pressure-induced phase transition to a cotunnite-like (orthorhombic) structure that begins between 18 and 25 GPa. The phase transition to the cotunnite-like structure is not complete at 50 GPa, and upon release of pressure, the hafnates transform to defect-fluorite with an amorphous component. For all compositions, in situ Raman spectroscopy showed that disordering occurs gradually with increasing pressure. Pyrochlore-structured hafnates retain their short-range order to a higher pressure (30 GPa vs.  <10 GPa) than defect-fluorite-structured hafnates. Rare earth hafnates quenched from 50 GPa show Raman spectra consistent with weberite-type structures, as also reported for irradiated rare-earth stannates. The second-order Birch-Murnaghan equation of state fit gives a bulk modulus of ~250 GPa for hafnates with the pyrochlore structure, and ~400 GPa for hafnates with the defect-fluorite structure. Dy 2 Hf 2 O 7 is intermediate in its response, with some pyrochlore-type ordering, based on Raman spectroscopy and the equation of state, with a bulk modulus of ~300 GPa. As predicted based on the similar ionic radius of Zr 4+ and Hf 4+ , rare-earth hafnates show

Coulomb spin liquid in anion-disordered pyrochlore Tb 2Hf 2O 7

DOE PAGES

Sibille, Romain; Lhotel, Elsa; Hatnean, Monica Ciomaga; ...

2017-10-12

Here, the charge ordered structure of ions and vacancies characterizing rare-earth pyrochlore oxides serves as a model for the study of geometrically frustrated magnetism. The organization of magnetic ions into networks of corner-sharing tetrahedra gives rise to highly correlated magnetic phases with strong fluctuations, including spin liquids and spin ices. It is an open question how these ground states governed by local rules are affected by disorder. Here we demonstrate in the pyrochlore Tb 2Hf 2O 7, that the vicinity of the disordering transition towards a defective fluorite structure translates into a tunable density of anion Frenkel disorder while cationsmore » remain ordered. Quenched random crystal fields and disordered exchange interactions can therefore be introduced into otherwise perfect pyrochlore lattices of magnetic ions. We show that disorder can play a crucial role in preventing long-range magnetic order at low temperatures, and instead induces a strongly fluctuating Coulomb spin liquid with defect-induced frozen magnetic degrees of freedom.« less

Thermal Conductivity and Stability of HfO2-Y2O3 and La2Zr2O7 Evaluated for 1650 Deg C Thermal/Environmental Barrier Coating Applications

NASA Technical Reports Server (NTRS)

Zhu, Dong-Ming; Bansal, Narottam P.; Miller, Robert A.

2003-01-01

HfO2-Y2O3 and La2Zr2O7 are candidate thermal and environmental barrier coating (T/EBC) materials for gas turbine ceramic matrix composite (CMC) combustor applications because of their relatively low thermal conductivity and high temperature capability. In this paper, thermal conductivity and high temperature stability of hot-pressed and plasma sprayed specimens with representative partially-stabilized and fully-cubic HfO2-Y2O3 compositions and La2Zr2O7 were evaluated at temperatures up to 1700 C using a steady-state laser heat-flux technique. Sintering behavior of the plasmasprayed coatings was determined by monitoring the thermal conductivity increases during a 20-hour test period at various temperatures. Durability and failure mechanisms of the HfO2-Y2O3 and La2Zr2O7 coatings on mullite/SiC hexoloy or SiC/SiC CMC substrates were investigated at 1650 C under thermal gradient cyclic conditions. Coating design and testing issues for the 1650 C thermal/environmental barrier coating applications are also discussed.

Structure and radiation effect of Er-stuffed pyrochlore Er2(Ti2-xErx)O7-x/2 (x = 0-0.667)

NASA Astrophysics Data System (ADS)

Yang, D. Y.; Xu, C. P.; Fu, E. G.; Wen, J.; Liu, C. G.; Zhang, K. Q.; Wang, Y. Q.; Li, Y. H.

2015-08-01

Er-stuffed pyrochlore series Er2(Ti2-xErx)O7-x/2 (x = 0, 0.162, 0.286, 0.424 and 0.667) were synthesized using conventional ceramic processing procedures. The structure of Er2(Ti2-xErx)O7-x/2 is effectively tailored by the Er stuffing level (x). In order to study the radiation effect of Er-stuffed pyrochlores, irradiation experiments were performed with 400 keV Ne2+ ions to fluences ranging from 5 × 1014 to 3.0 × 1015 ions/cm2 at cryogenic condition. Irradiation induced microstructural evolution was examined using a grazing incidence X-ray diffraction technique. It is found that the irradiated layer of Er2(Ti2-xErx)O7-x/2 undergoes significant lattice disordering and swelling at fluences of ⩽1.5 × 1015 ions/cm2 and amorphization at fluences of ⩾1.5 × 1015 ions/cm2. The radiation effect depends strongly on the chemical compositions of the samples. Both the lattice swelling percentage and the amorphous fraction decrease with increasing x. The experimental results are discussed in the context of cation antisite defect. The defect formation energy which varies as a function of x is responsible for the difference in the structural behaviors of Er2(Ti2-xErx)O7-x/2 under 400 keV Ne2+ ion irradiation.

Effect of structure and thermodynamic stability on the response of lanthanide stannate pyrochlores to ion beam irradiation.

PubMed

Lian, J; Helean, K B; Kennedy, B J; Wang, L M; Navrotsky, A; Ewing, R C

2006-02-09

The lanthanide stannates, Ln2Sn2O7, Ln=La-Lu and Y, have the isometric pyrochlore structure, A2B2O7, and their structural properties have been refined by Rietveld analysis of powder neutron and synchrotron X-ray diffraction data. In this study, the enthalpies of formation of selected stannate pyrochlores, Ln=La, Nd, Sm, Eu, Dy, and Yb, were measured by high-temperature oxide melt solution calorimetry. Their radiation response was determined by 1 MeV Kr2+ ion irradiation combined with in situ TEM observation over the temperature range of 25 to 1000 K. The enthalpy of formation from binary oxides of stannate pyrochlores became more endothermic (from -145 to -40 kJ/mol) as the size of the lanthanide in the A-site decreases. A more exothermic trend of the enthalpy of formation was observed in stannate pyrochlores with larger lanthanide ions, particularly La, possibly as a result of increased covalency in the Sn-O bond. In contrast to lanthanide titanate pyrochlores, Ln2Ti2O7, that are generally susceptible to radiation-induced amorphization and zirconate pyrochlores, Ln2Zr2O7, that are generally resistant to radiation-induced amorphization, the lanthanide stannate pyrochlores show a much greater variation in their response to ion irradiation. La, Nd, and Gd stannates experience the radiation-induced transformation to the aperiodic state, and the critical amorphization temperatures are approximately 960, 700, and 350 K, respectively. Y and Er stannate pyrochlores cannot be amorphized by ion beam irradiation, even at 25 K, and instead disorder to a defect fluorite structure. Comparison of the calorimetric and ion irradiation data for titanate, zirconate, and stannate pyrochlores reveals a strong correlation among subtle changes in crystal structure with changing composition, the energetics of the disordering process, and the temperature above which the material can no longer be amorphized. In summary, as the structure approaches the ideal, ordered pyrochlore structure

Phase Competition in the Palmer-Chalker X Y Pyrochlore Er2Pt2O7

NASA Astrophysics Data System (ADS)

Hallas, A. M.; Gaudet, J.; Butch, N. P.; Xu, Guangyong; Tachibana, M.; Wiebe, C. R.; Luke, G. M.; Gaulin, B. D.

2017-11-01

We report neutron scattering measurements on Er2Pt2O7 , a new addition to the X Y family of frustrated pyrochlore magnets. Symmetry analysis of our elastic scattering data shows that Er2Pt2O7 orders into the k =0 , Γ7 magnetic structure (the Palmer-Chalker state), at TN=0.38 K . This contrasts with its sister X Y pyrochlore antiferromagnets Er2Ti2O7 and Er2Ge2O7 , both of which order into Γ5 magnetic structures at much higher temperatures, TN=1.2 and 1.4 K, respectively. In this temperature range, the magnetic heat capacity of Er2Pt2O7 contains a broad anomaly centered at T*=1.5 K . Our inelastic neutron scattering measurements reveal that this broad heat capacity anomaly sets the temperature scale for strong short-range spin fluctuations. Below TN=0.38 K , Er2Pt2O7 displays a gapped spin-wave spectrum with an intense, flat band of excitations at lower energy and a weak, diffusive band of excitations at higher energy. The flat band is well described by classical spin-wave calculations, but these calculations also predict sharp dispersive branches at higher energy, a striking discrepancy with the experimental data. This, in concert with the strong suppression of TN, is attributable to enhanced quantum fluctuations due to phase competition between the Γ7 and Γ5 states that border each other within a classically predicted phase diagram.

Relief of frustration in the Heisenberg pyrochlore antiferromagnet Gd2Pt2O7

NASA Astrophysics Data System (ADS)

Hallas, A. M.; Sharma, A. Z.; Cai, Y.; Munsie, T. J.; Wilson, M. N.; Tachibana, M.; Wiebe, C. R.; Luke, G. M.

2016-10-01

The gadolinium pyrochlores Gd2B2O7 are among the best realizations of antiferromagnetically coupled Heisenberg spins on a pyrochlore lattice. We present a magnetic characterization of Gd2Pt2O7 , a unique member of this family. Magnetic susceptibility, heat capacity, and muon spin relaxation measurements show that Gd2Pt2O7 undergoes an antiferromagnetic ordering transition at TN=1.6 K. This transition is strongly first order, as indicated by the sharpness of the heat capacity anomaly, thermal hysteresis in the magnetic susceptibility, and a nondivergent relaxation rate in μ SR . The form of the heat capacity below TN suggests that the ground state is an anisotropic collinear antiferromagnet with an excitation spectrum that is gapped by 0.245(1) meV. The ordering temperature in Gd2Pt2O7,TN=1.6 K, is a substantial 160% increase from other gadolinium pyrochlores, which are all known to order at 1 K or lower. We attribute this enhancement in TN to the B -site cation, platinum. Despite being nonmagnetic, platinum has a filled 5 d t2 g orbital and an empty 5 d eg orbital that can facilitate superexchange. Thus, the magnetic frustration in Gd2Pt2O7 is partially "relieved," thereby promoting magnetic order.

Pyrochlore Oxide Superconductor Cd2Re2O7 Revisited

NASA Astrophysics Data System (ADS)

Hiroi, Zenji; Yamaura, Jun-ichi; Kobayashi, Tatsuo C.; Matsubayashi, Yasuhito; Hirai, Daigorou

2018-02-01

The superconducting pyrochlore oxide Cd2Re2O7 is revisited with a particular emphasis on the sample-quality issue. The compound has drawn attention as the only superconductor (Tc = 1.0 K) that has been found in the family of α-pyrochlore oxides since its discovery in 2001. Moreover, it exhibits two characteristic structural transitions from the cubic pyrochlore structure, with the inversion symmetry broken at the first one at 200 K. Recently, it has attracted increasing attention as a candidate spin-orbit coupled metal (SOCM), in which specific Fermi liquid instability is expected to lead to an odd-parity order with spontaneous inversion-symmetry breaking [L. Fu, Phys. Rev. Lett. 115, 026401 (2015)] and parity-mixing superconductivity [V. Kozii and L. Fu, Phys. Rev. Lett. 115, 207002 (2015); Y. Wang et al., Phys. Rev. B 93, 134512 (2016)]. We review our previous experimental results in comparison with those of other groups in the light of the theoretical prediction of the SOCM, which we consider meaningful and helpful for future progress in understanding this unique compound.

2.7 MeV Ar11+ ion irradiation induced structural evolution in Lu2(Ti2-xLux)O7-x/2 pyrochlores

NASA Astrophysics Data System (ADS)

Yang, D. Y.; Liu, C. G.; Zhang, K. Q.; Xia, Y.; Chen, L. J.; Liu, H.; Li, Y. H.

2015-11-01

This paper aims to study the radiation effects of nonstoichiometric pyrochlore series Lu2(Ti2-xLux)O7-x/2 (x = 0-0.667). Polycrystalline Lu2(Ti2-xLux)O7-x/2 samples were irradiated with 2.7 MeV Ar11+ ions up to a fluence of 8 × 1014 ions/cm2. The irradiated samples were characterized using grazing incidence X-ray diffraction technique. The results reveal that Lu2(Ti2-xLux)O7-x/2 samples undergo significant amorphization and lattice swelling upon irradiation. Specifically, the amorphization process is predominantly driven by ballistic nuclear energy deposition of Ar11+ ions at this energy regime, which can be well described by a direct-impact/defect-stimulated model. Both the amorphization fraction and the relative variation of lattice parameter decrease with increasing x, showing a strong dependence on the chemical composition. The results are then discussed in the framework of the structural disorder and recovery ability from damage, applying an atomic layer model.

Fluctuations and All-In-All-Out Ordering in Dipole-Octupole Nd2Zr2O7

NASA Astrophysics Data System (ADS)

Lhotel, E.; Petit, S.; Guitteny, S.; Florea, O.; Ciomaga Hatnean, M.; Colin, C.; Ressouche, E.; Lees, M. R.; Balakrishnan, G.

2015-11-01

By means of neutron scattering and magnetization measurements down to 90 mK, we determine the magnetic ground state of the spin-ice candidate Nd2Zr2O7. We show that, despite ferromagnetic interactions, Nd2Zr2O7 undergoes a transition around 285 mK towards an all-in-all-out antiferromagnetic state, with a strongly reduced ordered magnetic moment. We establish the (H ,T ) phase diagram in the three directions of the applied field and reveal a metamagnetic transition around 0.1 T, associated with an unexpected shape of the magnetization curves. We propose that this behavior results from the peculiar nature of the Nd3 + doublet, a dipolar-octupolar doublet, different from the standard Kramers doublet studied to date, thus revealing the importance of multipolar correlations in the properties of pyrochlore oxides.

High-pressure synthesis and characterizations of the R2Pt2O7 pyrochlores.

NASA Astrophysics Data System (ADS)

Cai, Yunqi; Cui, Qi; Cheng, Jinguang; Dun, Zhiling; Zhou, Haidong; Ma, Jie; Cruz, C. Dela; Yan, Jiaqiang; Li, Xiang; Zhou, Jianshi

Pyrochlore R2B2O7 where R3 + stands for rear-earth ion and B4 + for a nonmagnetic cation such as Sn4 +or Ti4 +consist of an important family of geometrically frustrated magnets, which have been the focus of extensive investigations over last decades. To further enlarge the R2B2O7, we have chosen to stabilize the Pt-based cubic pyrochlores under HPHT conditions for two reasons: (1) Pt4 + is in a low-spin state which ionic radius is located in between Ti4 + (0.605\\x85) and Sn4 + (0.69\\x85), and (2) Pt4 + has a spatially much more extended 5d orbitals and thus enhanced Pt 5d-O 2p hybridizations that might modify the local anisotropic exchange interactions. Such an effect has never been taken into account in the previous studies. In this work, we will present the detailed characterizations on the pyrochlores R2Pt2O7 obtained under HPHT conditions. This work is supported by the National Science Foundation of China (Grant Nos.11304371, 11574377), part of the work was supported by the CEM, and NSF MRSEC, under Grant DMR-1420451, and Grant No. NSF-DMR-1350002.

(Zr,Ti)O2 interface structure in ZrO2-TiO2 nanolaminates with ultrathin periodicity

NASA Astrophysics Data System (ADS)

Aita, C. R.; DeLoach, J. D.; Yakovlev, V. V.

2002-07-01

A mixed cation interfacial structure in ZrO2-TiO2 nanolaminate films with ultrathin bilayer periodicity grown by sputter deposition at 297 K was identified by x-ray diffraction and nonresonant Raman spectroscopy. This structure consists of an amorphous phase at a ZrO2-on-TiO2 bilayer interface, followed by an extensive crystalline monoclinic (Zr,Ti)O2 solid solution predicted by Vegard's law. Monoclinic (Zr,Ti)O2 has previously been reported only once, in bulk powder of a single composition (ZrTiO4) at high pressure. Its stabilization in the nanolaminates is explained by the Gibbs-Thomson effect. This complex interfacial structure is shown to be a means of accommodating chemical mixing in the absence of a driving force for heteroepitaxy.

Phase transition in lithium garnet oxide ionic conductors Li7La3Zr2O12: The role of Ta substitution and H2O/CO2 exposure

NASA Astrophysics Data System (ADS)

Wang, Yuxing; Lai, Wei

2015-02-01

High Li-content lithium garnet oxides are promising solid electrolyte materials for lithium batteries. Being the highest Li-content lithium garnet oxides, Li7La3Zr2O12 has been reported to crystallize in either the tetragonal or cubic phase with no consensus on the exact conditions under which these two phases are formed, which may be due to unintentional Al contamination and air exposure. In this work, the effects of Ta substitution and H2O/CO2 exposure have been studied under Al-contamination free conditions with minimal air exposure. We showed that 1) the Ta-substitution induced phase transition occurred through a two-phase mechanism and a minimum 0.6 mol of Ta substitution to Zr is needed to stabilize the cubic phase; 2) H2O and CO2 can individually induce the tetragonal-cubic phase transition in Li7La3Zr2O12 through proton exchange and Li extraction, respectively, which can have great influence on the transport properties of Li7La3Zr2O12.

Symmetry and light stuffing of H o 2 T i 2 O 7 ,   E r 2 T i 2 O 7 , and Y b 2 T i 2 O 7 characterized by synchrotron x-ray diffraction

DOE Office of Scientific and Technical Information (OSTI.GOV)

Baroudi, Kristen; Gaulin, Bruce D.; Lapidus, Saul H.

2015-07-01

The Ho2Ti2O7, Er2Ti2O7 and Yb2Ti2O7 pyrochlores were studied by synchrotron X-ray diffraction to determine whether the (002) peak, forbidden in the pyrochlore space group Fd-3m but observed in single crystal neutron scattering measurements, is present due to a deviation of their pyrochlore structure from Fd-3m symmetry. Synchrotron diffraction measurements on precisely synthesized stoichiometric and non-stoichiometric powders and a crushed floating zone crystal of Ho2Ti2O7 revealed that the (002) reflection is absent in all cases to a sensitivity of approximately one part in 30,000 of the strongest X-ray diffraction peak. This indicates to high sensitivity that the structural space group ofmore » these rare earth titanate pyrochlores is Fd-3m, and that thus the (002) peak observed in the neutron scattering experiments has a non-structural origin. The cell parameters and internal strain for lightly stuffed Ho2+xTi2-xO7 are also presented.« less

Crystal structure of the pyrochlore oxide superconductor KOs{sub 2}O{sub 6}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yamaura, Jun-Ichi; Yonezawa, Shigeki; Muraoka, Yuji

2006-01-15

We report the single-crystal X-ray analysis of the structure of the pyrochlore oxide superconductor KOs{sub 2}O{sub 6}. The structure was identified as the {beta}-pyrochlore structure with space group Fd3-bar m and lattice constant a=10.089(2)A at 300K: the K atom is located at the 8b site, not at the 16d site as in conventional pyrochlore oxides. We found an anomalously large atomic displacement parameter U{sub iso}=0.0735(8)A{sup 2} at 300K for the K cation, which suggests that the K cation weakly bound to an oversized Os{sub 12}O{sub 18} cage exhibits intensive rattling, as recently observed for clathrate compounds. The rattling of Amore » cations is a common feature in the series of {beta}-pyrochlore oxide superconductors AOs{sub 2}O{sub 6} (A=Cs, Rb and K), and is greatest for the smallest K cation.« less

Metal-Insulator Transition in Epitaxial Pyrochlore Iridates Bi2Ir2O7 thin Films

NASA Astrophysics Data System (ADS)

Chu, Jiun-Haw; Liu, Jian; Yi, Di; Rayan-Serrao, C.; Suresha, S.; Marti, Xavi; Riggs, Scott; Shapiro, Max; Ian, Fisher; Ramesh, R.

2013-03-01

Recently there is a surge of interest in searching for topological order in correlated electronic systems such as transition metal oxides. The strong spin-orbit interaction of 5d electrons and the geometric frustration in the crystal lattice make the pyrochlore iridate(A2Ir2O7) an ideal candidate to achieve this goal. Pioneering experiments on bulk polycrystalline and single crystal samples revealed a temperature dependent metal-insulator transition coupled to a long range magnetic order, and the transition temperature can be tuned by either A-site ionic radius or an external pressure. In this talk we present our efforts to understand and control the metal-insulator transition and the underlying electronic structure of pyrochlore iridates via epitaxial Bi2Ir2O7 thin films. Bulk Bi2Ir2O7 is located at the metallic side of the phase diagram. However as the film's thickness decreases the transport evolves from a metallic to a strongly localized character. Resonant X-ray spectroscopy suggests that the density of states near Fermi level is dominated by the Ir Je ff =1/2 states. Intriguingly, the magnetoresistance shows a linear field dependence over a wide range of fields at low temperatures, which is possibly consistent with the existence of Dirac nodes.

Antiferroquadrupolar correlations in the quantum spin ice candidate Pr2Zr2O7

NASA Astrophysics Data System (ADS)

Petit, S.; Lhotel, E.; Guitteny, S.; Florea, O.; Robert, J.; Bonville, P.; Mirebeau, I.; Ollivier, J.; Mutka, H.; Ressouche, E.; Decorse, C.; Ciomaga Hatnean, M.; Balakrishnan, G.

2016-10-01

We present an experimental study of the quantum spin ice candidate pyrochlore compound Pr2Zr2O7 by means of magnetization measurements, specific heat, and neutron scattering up to 12 T and down to 60 mK. When the field is applied along the [111 ] and [1 1 ¯0 ] directions, k =0 field-induced structures settle in. We find that the ordered moment rises slowly, even at very low temperature, in agreement with macroscopic magnetization. Interestingly, for H ∥[1 1 ¯0 ] , the ordered moment appears on the so-called α chains only. The spin excitation spectrum is essentially inelastic and consists in a broad flat mode centered at about 0.4 meV with a magnetic structure factor which resembles the spin ice pattern. For H ∥[1 1 ¯0 ] (at least up to 2.5 T), we find that a well-defined mode forms from this broad response, whose energy increases with H , in the same way as the temperature of the specific-heat anomaly. We finally discuss these results in the light of mean field calculations and propose an interpretation where quadrupolar interactions play a major role, overcoming the magnetic exchange. In this picture, the spin ice pattern appears shifted up to finite energy because of those interactions. We then propose a range of acceptable parameters for Pr2Zr2O7 that allow to reproduce several experimental features observed under field. With these parameters, the actual ground state of this material would be an antiferroquadrupolar liquid with spin-ice-like excitations.

Heavy ion irradiation-induced microstructural evolution in pyrochlore Lu{sub 2}Ti{sub 2}O{sub 7} at room temperature and 723 K

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xie, Q.R.; Zhang, J., E-mail: zhangjian@xmu.edu.cn; Dong, X.N.

Polycrystalline pyrochlore Lu{sub 2}Ti{sub 2}O{sub 7} pellets were irradiated with 600 keV Kr{sup 3+} at room temperature and 723 K to a fluence of 4×10{sup 15} ions/cm{sup 2}, corresponding to an average ballistic damage dose of 10 displacements per atom in the peak damage region. Irradiation-induced microstructural evolution was examined by grazing incidence X-ray diffraction, and cross-sectional transmission electron microscopy. Incomplete amorphization was observed in the sample irradiated at room temperature due to the formation of nano-crystal which has the identical structure of pyrochlore, and the formation of nano-crystal is attributed to the mechanism of epitaxial recrystallization. However, an orderedmore » pyrochlore phase to a swelling disordered fluorite phase transformation is occurred for the Lu{sub 2}Ti{sub 2}O{sub 7} sample irradiated at 723 K, which is due to the disordering of metal cations and anion vacancies. - Graphical Abstract: Polycrystalline pyrochlore Lu{sub 2}Ti{sub 2}O{sub 7} pellets were irradiated with 600 keV Kr{sup 3+} to a fluence of 4×10{sup 15} ions/cm{sup 2} at room temperature and 723 K, Incomplete amorphization was observed in the sample irradiated at room temperature due to the formation of nano-crystal. However, an ordered pyrochlore phase to a swelling disordered fluorite phase transformation is occurred for the Lu{sub 2}Ti{sub 2}O{sub 7} sample irradiated at 723 K, which is due to the disordering of metal cations and anion vacancies. - Highlights: Pyrochlore Lu{sub 2}Ti{sub 2}O{sub 7} pellets were irradiated by heavy ions at RT and 723 K. At RT irradiation, ~75% of amorphization was achieved. The nano-crystals were formed in the damage layer at RT irradiation. The formed nano-crystals enhanced the radiation tolerance of Lu{sub 2}Ti{sub 2}O{sub 7}. A pyrochlore to fluorite phase transformation was observed at 723 K irradiation.« less

Phase Composition and Disorder in La2(Sn,Ti)2O7 Ceramics: New Insights from NMR Crystallography.

PubMed

Fernandes, Arantxa; McKay, David; Sneddon, Scott; Dawson, Daniel M; Lawson, Sebastian; Veazey, Richard; Whittle, Karl R; Ashbrook, Sharon E

2016-09-15

An NMR crystallographic approach, involving the combination of 119 Sn NMR spectroscopy, XRD, and DFT calculations, is demonstrated for the characterization of La 2 Sn 2- x Ti x O 7 ceramics. A phase change from pyrochlore (La 2 Sn 2 O 7 ) to a layered perovskite phase (La 2 Ti 2 O 7 ) is predicted (by radius ratio rules) to occur when x ≈ 0.95. However, the sensitivity of NMR spectroscopy to the local environment is able to reveal a significant two-phase region is present, extending from x = 1.8 to ∼0.2, with limited solid solution at the two extremes, in broad agreement with powder XRD measurements. DFT calculations reveal that there is preferential site substitution of Sn in La 2 Ti 2 O 7 , with calculated shifts for Sn substitution onto Ti1 and Ti2 sites (in the "bulk" perovskite layers) in better agreement with experiment than those for Ti3 and Ti4 ("edge" sites). Substitution onto these two sites also produces structural models with lower relative enthalpy. As the Sn content decreases, there is a further preference for substitution onto Sn2. In contrast, the relative intensities of the spectral resonances suggest that Ti substitution into the pyrochlore phase is random, although only a limited solid solution is observed (up to ∼7% Ti). DFT calculations predict very similar 119 Sn shifts for Sn substitution into the two proposed models of La 2 Ti 2 O 7 (monoclinic ( P 2 1 ) and orthorhombic ( Pna 2 1 )), indicating it is not possible to distinguish between them. However, the relative energy of the Sn-substituted orthorhombic phase was higher than that of substituted monoclinic cells, suggesting that the latter is the more likely structure.

The solubility and site preference of Fe3+ in Li7−3xFexLa3Zr2O12 garnets

PubMed Central

Rettenwander, D.; Geiger, C.A.; Tribus, M.; Tropper, P.; Wagner, R.; Tippelt, G.; Lottermoser, W.; Amthauer, G.

2015-01-01

A series of Fe3+-bearing Li7La3Zr2O12 (LLZO) garnets was synthesized using solid-state synthesis methods. The synthetic products were characterized compositionally using electron microprobe analysis and inductively coupled plasma optical emission spectroscopy (ICP-OES) and structurally using X-ray powder diffraction and 57Fe Mössbauer spectroscopy. A maximum of about 0.25 Fe3+ pfu could be incorporated in Li7−3xFexLa3Zr2O12 garnet solid solutions. At Fe3+ concentrations lower than about 0.16 pfu, both tetragonal and cubic garnets were obtained in the synthesis experiments. X-ray powder diffraction analysis showed only a garnet phase for syntheses with starting materials having intended Fe3+ contents lower than 0.52 Fe3+ pfu. Back-scattered electron images made with an electron microprobe also showed no phase other than garnet for these compositions. The lattice parameter, a0, for all solid-solution garnets is similar with a value of a0≈12.98 Å regardless of the amount of Fe3+. 57Fe Mössbauer spectroscopic measurements indicate the presence of poorly- or nano-crystalline FeLaO3 in syntheses with Fe3+ contents greater than 0.16 Fe3+ pfu. The composition of different phase pure Li7−3xFexLa3Zr2O12 garnets, as determined by electron microprobe (Fe, La, Zr) and ICP-OES (Li) measurements, give Li6.89Fe0.03La3.05Zr2.01O12, Li6.66Fe0.06La3.06Zr2.01O12, Li6.54Fe0.12La3.01Zr1.98O12, and Li6.19Fe0.19La3.02Zr2.04O12. The 57Fe Mössbauer spectrum of cubic Li6.54Fe0.12La3.01Zr1.98O12 garnet indicates that most Fe3+ occurs at the special crystallographic 24d position, which is the standard tetrahedrally coordinated site in garnet. Fe3+ in smaller amounts occurs at a general 96h site, which is only present for certain Li-oxide garnets, and in Li6.54Fe0.12La3.01Zr1.98O12 this Fe3+ has a distorted 4-fold coordination. PMID:26435549

Oxygen miscibility gap and spin glass formation in the pyrochlore Lu{sub 2}Mo{sub 2}O{sub 7}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Clark, L.; Ritter, C.; Harrison, A.

2013-07-15

Rare earth (R) molybdate pyrochlores, R{sub 2}Mo{sub 2}O{sub 7}, are of interest as frustrated magnets. Polycrystalline samples of Lu{sub 2}Mo{sub 2}O{sub 7−x} prepared at 1600 °C display a coexistence of cubic pyrochlore phases. Rietveld fits to powder neutron diffraction data and chemical analyses show that the miscibility gap is between a stoichiometric x=0 and an oxygen-deficient x≈0.4 phase. Lu{sub 2}Mo{sub 2}O{sub 7} behaves as a spin glass material, with a divergence of field cooled and zero field cooled DC magnetic susceptibilities at a spin freezing temperature T{sub f}=16 K, that varies with frequency in AC measurements following a Vogel–Fulcher law.more » Lu{sub 2}Mo{sub 2}O{sub 6.6} is more highly frustrated spin glass and has T{sub f}=20 K. - Graphical abstract: The cubic Lu{sub 2}Mo{sub 2}O{sub 7−x} system exhibits a miscibility gap between coexisting pyrochlore phases at 1600 °C. Neutron powder diffraction refinement and chemical analysis shows that the gap separates stoichiometric x=0 and oxygen-deficient x≈0.4 phases. Lu{sub 2}Mo{sub 2}O{sub 7−x} has a frustrated spin glass ground state that is sensitive to the oxygen content. - Highlights: • The cubic Lu{sub 2}Mo{sub 2}O{sub 7−x} system has a miscibility gap between coexisting pyrochlore phases at 1600 °C. • Neutron powder diffraction shows that the gap separates x=0 and oxygen-deficient x≈0.4 phases. • Lu{sub 2}Mo{sub 2}O{sub 7−x} has a frustrated spin glass ground state that is sensitive to the oxygen content.« less

Structure and Thermal Expansion of YSZ and La 2Zr 2O 7 Above 1500°C from Neutron Diffraction on Levitated Samples

DOE PAGES

Ushakov, Sergey V.; Navrotsky, Alexandra; Weber, Richard J. K.; ...

2015-07-28

High-temperature time-of-flight neutron diffraction experiments were performed in this paper on cubic yttria-stabilized zirconia (YSZ, 10 mol% YO 1.5) and lanthanum zirconate (LZ) prepared by laser melting. Three spheroids of each composition were aerodynamically levitated and rotated in argon flow and heated with a CO 2 laser. Unit cell, positional and atomic displacement parameters were obtained by Rietveld analysis. Below ~1650°C the mean thermal expansion coefficient (TEC) for YSZ is higher than for LZ (13 ± 1 vs. 10.3 ± 0.6) × 10 -6/K. From ~1650°C to the onset of melting of LZ at ~2250°C, TEC for YSZ and LZmore » are similar and within (7 ± 2) × 10 -6/K. LZ retains the pyrochlore structure up to the melting temperature with Zr coordination becoming closer to perfectly octahedral. Congruently melting LZ is La deficient. The occurrence of thermal disordering of oxygen sublattice (Bredig transition) in defect fluorite structure was deduced from the rise in YSZ TEC to ~25 × 10 -6/K at 2350°C–2550°C with oxygen displacement parameters (U iso) reaching 0.1 Å 2, similar to behavior observed in UO 2. Acquisition of powder-like high-temperature neutron diffraction data from solid-levitated samples is feasible and possible improvements are outlined. Finally, this methodology should be applicable to a wide range of materials for high-temperature applications.« less

Tm-doped TiO2 and Tm2Ti2O7 pyrochlore nanoparticles: enhancing the photocatalytic activity of rutile with a pyrochlore phase.

PubMed

De Los Santos, Desiré M; Navas, Javier; Aguilar, Teresa; Sánchez-Coronilla, Antonio; Fernández-Lorenzo, Concha; Alcántara, Rodrigo; Piñero, Jose Carlos; Blanco, Ginesa; Martín-Calleja, Joaquín

2015-01-01

Tm-doped TiO2 nanoparticles were synthesized using a water-controlled hydrolysis reaction. Analysis was performed in order to determine the influence of the dopant concentration and annealing temperature on the phase, crystallinity, and electronic and optical properties of the resulting material. Various characterization techniques were utilized such as X-ray diffraction, Raman spectroscopy, X-ray photoelectron spectroscopy and UV-vis spectroscopy. For the samples annealed at 773 and 973 K, anatase phase TiO2 was obtained, predominantly internally doped with Tm(3+). ICP-AES showed that a doping concentration of up to 5.8 atom % was obtained without reducing the crystallinity of the samples. The presence of Tm(3+) was confirmed by X-ray photoelectron spectroscopy and UV-vis spectroscopy: the incorporation of Tm(3+) was confirmed by the generation of new absorption bands that could be assigned to Tm(3+) transitions. Furthermore, when the samples were annealed at 1173 K, a pyrochlore phase (Tm2Ti2O7) mixed with TiO2 was obtained with a predominant rutile phase. The photodegradation of methylene blue showed that this pyrochlore phase enhanced the photocatalytic activity of the rutile phase.

A new approach to preparing Bi2Zr2O7 photocatalysts for dye degradation

NASA Astrophysics Data System (ADS)

Luo, Yijia; Cao, Liyun; Huang, Jianfeng; Feng, Liangliang; Yao, Chunyan

2018-01-01

A new synthetic route is presented to prepared pure Bi2Zr2O7 material, in which a NaNO3/KNO3 molten salt is used to obtain the resulting Bi2Zr2O7 at a relatively low temperature of 400 °C under atmospheric pressure. Powder x-ray diffraction confirmed the structure type and purity of the as-prepared sample, and further revealed that a single-source Bi(OH)3 · Zr(OH)4 · nH2O complex precursor plays a crucial role to synthesize Bi2Zr2O7 nanocrystals. Scanning electron microscope and transmission electron microscope show the morphologies and sizes of Bi2Zr2O7 crystal in detail, and UV-vis diffuse reflectance measurements evidenced the wide light absorption range. Furthermore, the as-synthesized Bi2Zr2O7 with smaller particle size and larger specific surface area exhibit superior photocatalytic activities compared with the sample obtained without adding molten salts.

Long-range magnetic order in the Heisenberg pyrochlore antiferromagnets G d2G e2O7 and G d2P t2O7 synthesized under high pressure

NASA Astrophysics Data System (ADS)

Li, X.; Cai, Y. Q.; Cui, Q.; Lin, C. J.; Dun, Z. L.; Matsubayashi, K.; Uwatoko, Y.; Sato, Y.; Kawae, T.; Lv, S. J.; Jin, C. Q.; Zhou, J.-S.; Goodenough, J. B.; Zhou, H. D.; Cheng, J.-G.

2016-12-01

G d2S n2O7 and G d2T i2O7 have been regarded as good experimental realizations of the classical Heisenberg pyrochlore antiferromagnet with dipolar interaction. The former was found to adopt the Palmer-Chalker state via a single, first-order transition at TN≈1 K , while the latter enters a distinct, partially ordered state through two successive transitions at TN 1≈1 K and TN 2= 0.75 K . To shed more light on their distinct magnetic ground states, we have synthesized two more gadolinium-based pyrochlore oxides, G d2G e2O7 and G d2P t2O7 , under high-pressure conditions and performed detailed characterizations via x-ray powder diffraction, dc and ac magnetic susceptibility, and specific heat measurements down to 100 mK. We found that both compounds enter a long-range antiferromagnetically ordered state through a single, first-order transition at TN= 1.4 K for G d2G e2O7 and TN= 1.56 K for G d2P t2O7 , with the specific heat anomaly similar to that of G d2S n2O7 rather than G d2T i2O7 . Interestingly, the low-temperature magnetic specific heat values of both G d2G e2O7 and G d2P t2O7 were found to follow nicely the T3 dependence as expected for a three-dimensional antiferromagnet with gapless spin-wave excitations. We have rationalized the enhancement of TN in terms of the reduced Gd-Gd distances for the chemically pressurized G d2G e2O7 and the addition of extra superexchange pathways through the empty Pt -eg orbitals for G d2P t2O7 . Our current study has expanded the family of gadolinium-based pyrochlores and permits us to achieve a better understanding of their distinct magnetic properties in a more comprehensive perspective.

CaO-MgO-Al 2O 3-SiO 2 (CMAS) corrosion of Gd 2Zr 2O 7 and Sm 2Zr 2O 7

DOE PAGES

Wang, Honglong; Bakal, Ahmet; Zhang, Xingxing; ...

2016-08-08

Ceramic thermal barrier coatings are applied to superalloys used in gas turbine engineering to increase the operating temperature and the energy conversion efficiency. However, dust consisting of CaO-MgO-Al 2O 3-SiO 2 (CMAS) from the air can be injected into the engines and corrode the thermal barrier coatings. Lanthanide zirconates are promising materials in thermal barrier coatings due to their low thermal conductivities, good phase stability and good corrosion resistance. However, the corrosion resistance mechanism of CMAS on lanthanide zirconates is still not clearly understood. In this work, the corrosion mechanism of Gd 2Zr 2O 7 and Sm 2Zr 2O 7more » in CMAS is studied. Here, the results show that the CMAS can easily react with lanthanide zirconate thermal barrier coatings to form a dense layer, which can resist further corrosion« less

Vibrational and elastic properties of Ln2Sn2O7 (Ln = La, Sm, Gd, Dy, Ho, Er, Yb, or Lu)

NASA Astrophysics Data System (ADS)

Akbudak, S.; Kushwaha, A. K.

2018-04-01

In this study, an eight-parameter bond-bending force constant model was used to calculate the zone center phonon frequencies, elastic constants, and related properties of the stannate compounds Ln2Sn2O7 (Ln = La, Sm, Gd, Dy, Ho, Er, Yb, or Lu) with a pyrochlore structure. We found that the Snsbnd O bond strengths dominate the Ln-O and Osbnd O bonds. We also found that all of the materials are ductile and anisotropic in nature. The anisotropic nature of the compounds increases in the order of: La2Sn2O7 < Sm2Sn2O7 < Gd2Sn2O7 < Dy2Sn2O7 < Ho2Sn2O7 < Er2Sn2O7 < Yb2Sn2O7 < Lu2Sn2O7.

A DFT+U study of Pu immobilization in Gd2Zr2O7

NASA Astrophysics Data System (ADS)

Zhao, F. A.; Xiao, H. Y.; Jiang, M.; Liu, Z. J.; Zu, X. T.

2015-12-01

The solubility of Pu in Gd2Zr2O7 has been investigated by the density functional theory plus Hubbard U correction. It is found that the formation of PuGdZr2O7, Gd2PuZrO7 and Gd2Pu1.5Zr0.5O7 are exothermic, whereas Pu0.5Gd1.5Zr2O7, Pu1.5Gd0.5Zr2O7 and Gd2Pu0.5Zr1.5O7 are energetically less stable than their respective separated states. The calculations show that both the Gd and Zr lattice sites can be substituted by the Pu, which is consistent with the immobilization behavior of uranium in Gd2Zr2O7 observed experimentally. The site preference of Pu in Gd2Zr2O7 is found to be dependent on the chemical environment, i.e., Pu prefers to substitute for Gd-site under Gd-rich and O2-rich conditions and for Zr-site under Zr-rich and O2-rich conditions.

Comparison of the Supercooled Spin Liquid States in the Pyrochlore Magnets Dy2Ti2O7 and Ho2Ti2O7

NASA Astrophysics Data System (ADS)

Eyal, Anna; Eyvazov, Azar B.; Dusad, Ritika; Munsie, Timothy J. S.; Luke, Graeme M.; Davis, J. C. Séamus

Despite a well-ordered crystal structure and strong magnetic interactions between the Dy or Ho ions, no long-range magnetic order has been detected in the pyrochlore titanates Ho2Ti2O7 and Dy2Ti2O7. The low temperature state in these materials is governed by spin-ice rules. These constrain the Ising like spins in the materials, yet does not result in a global broken symmetry state. To explore the actual magnetic phases, we simultaneously measure the time- and frequency-dependent magnetization dynamics of Dy2Ti2O7 and Ho2Ti2O7 using toroidal, boundary-free magnetization transport techniques. We demonstrate a distinctive behavior of the magnetic susceptibility of both compounds, that is indistinguishable in form from the permittivity of supercooled dipolar liquids. Moreover, we show that the microscopic magnetic relaxation times for both materials increase along a super-Arrhenius trajectory also characteristic of supercooled glass-forming liquids. Both materials therefore exhibit characteristics of a supercooled spin liquid. Strongly-correlated dynamics of loops of spins is suggested as a possible mechanism which could account for these findings. Potential connections to many-body spin localization will also be discussed.

Synthesis, characterization, and catalytic activity of Rh-based lanthanum zirconate pyrochlores for higher alcohol synthesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Abdelsayed, Victor; Shekhawat, Dushyant; Poston, James A.

2013-05-01

Two lanthanum zirconate pyrochlores (La{sub 2}Zr{sub 2}O{sub 7}; LZ) were prepared by Pechini method and tested for higher alcohols selectivity. In one, Rh was substituted into the pyrochlore lattice (LRZ, 1.7 wt%) while for the second, Rh was supported on an unsubstituted La{sub 2}Zr{sub 2}O{sub 7} (R/LZ, 1.8 wt%). X-ray photoelectron spectroscopy (XPS) and temperature programmed reduction (TPR) results show that the surface reducibility depends on whether the Rh is in (or supported on) the LZ pyrochlore. Rhodium in the LRZ is more reducible than rhodium supported on the R/LZ pyrochlore, likely due to the presence of a perovskite phasemore » (LaRhO{sub 3}; identified by XRD), in which rhodium is more reducible. The formation of the perovskite accompanies that of the pyrochlore. CO hydrogenation results show higher ethanol selectivity for R/LZ than LRZ, possibly due to the strong interaction between Rh and LZ on the R/LZ, forming atomically close Rh{sup +}/Rh{sup 0} sites, which have been suggested to favor ethanol production.« less

Polymorphic Transitions in Cerium-Substituted Zirconolite (CaZrTi 2O 7)

DOE PAGES

Clark, Braeden M.; Sundaram, S. K.; Misture, Scott T.

2017-07-19

Compounds with the formulae CaZr 1–xCe xTi 2O 7 with x = 0.1–0.5 were synthesized by solid state reaction. Cerium was used as a surrogate for actinide elements. A transition from the 2M polymorph to the 4M polymorph (expanded unit cell due to cation ordering) in zirconolite was observed with increasing cerium content. The presence of both tri- and tetravalent Ce, contrary to formulation, was confirmed using X-ray absorption near edge spectroscopy, suggesting substitution on both Ca and Zr sites. Sintering was carried out via spark plasma sintering, during which the perovskite phase (Ca 0.4Ce 0.4TiO 3) was stabilized duemore » to the reducing conditions of this technique. Scanning electron microscopy and energy dispersive spectrometry revealed that the 2M polymorph was dilute in Ce content in comparison to the 4M-zirconolite. High temperature X-ray diffraction was used to detail the kinetics of perovskite to zirconolite transition. It was found that CaCeTi 2O 7 (cubic pyrochlore) formed as an intermediate phase during the transition. Lastly, our results show that a transition from 2M- to 4M-zirconolite occurs with increasing Ce content and can be controlled by adjusting the P O2 and the heat treatment temperature.« less

Polymorphic Transitions in Cerium-Substituted Zirconolite (CaZrTi 2O 7)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Clark, Braeden M.; Sundaram, S. K.; Misture, Scott T.

Compounds with the formulae CaZr 1–xCe xTi 2O 7 with x = 0.1–0.5 were synthesized by solid state reaction. Cerium was used as a surrogate for actinide elements. A transition from the 2M polymorph to the 4M polymorph (expanded unit cell due to cation ordering) in zirconolite was observed with increasing cerium content. The presence of both tri- and tetravalent Ce, contrary to formulation, was confirmed using X-ray absorption near edge spectroscopy, suggesting substitution on both Ca and Zr sites. Sintering was carried out via spark plasma sintering, during which the perovskite phase (Ca 0.4Ce 0.4TiO 3) was stabilized duemore » to the reducing conditions of this technique. Scanning electron microscopy and energy dispersive spectrometry revealed that the 2M polymorph was dilute in Ce content in comparison to the 4M-zirconolite. High temperature X-ray diffraction was used to detail the kinetics of perovskite to zirconolite transition. It was found that CaCeTi 2O 7 (cubic pyrochlore) formed as an intermediate phase during the transition. Lastly, our results show that a transition from 2M- to 4M-zirconolite occurs with increasing Ce content and can be controlled by adjusting the P O2 and the heat treatment temperature.« less

Fabrication of SiO2@ZrO2@Y2O3:Eu3+ core-multi-shell structured phosphor.

PubMed

Gao, Xuan; He, Diping; Jiao, Huan; Chen, Juan; Meng, Xin

2011-08-01

ZrO2 interface was designed to block the reaction between SiO2 and Y2O3 in SiO2@Y2O3:Eu coreshell structure phosphor. SiO2@ZrO2@Y2O3:Eu core-multi-shell phosphors were successfully synthesized by combing an LBL method with a Sol-gel process. Based on electron microscopy, X-ray diffraction, and spectroscopy experiments, compelling evidence for the formation of the Y2O3:Eu outer shell on ZrO2 were presented. The presence of ZrO2 layer on SiO2 core can block the reaction of SiO2 core and Y2O3 shell effectively. By this kind of structure, the reaction temperature of the SiO2 core and Y2O3 shell in the SiO2@Y2O3:Eu core-shell structure phosphor can be increased about 200-300 degrees C and the luminescent intensity of this structure phosphor can be improved obviously. Under the excitation of ultraviolet (254 nm), the Eu3+ ion mainly shows its characteristic red (611 nm, 5D0-7F2) emissions in the core-multi-shell particles from Y2O3:Eu3+ shells. The emission intensity of Eu3+ ions can be tuned by the annealing temperatures, the number of coating times, and the thickness of ZrO2 interface, respectively.

Study of Pt-Rh/CeO2-ZrO2-MxOy (M = Y, La)/Al2O3 three-way catalysts

NASA Astrophysics Data System (ADS)

Jiaxiu, Guo; Zhonghua, Shi; Dongdong, Wu; Huaqiang, Yin; Maochu, Gong; Yaoqiang, Chen

2013-05-01

CeO2-ZrO2-MxOy (M = Y; La) mixed oxides, prepared by co-precipitation method and characterized by Brunauer-Emmett-Teller (BET), X-ray diffraction (XRD), Raman spectra (RM) and oxygen pulse reaction, were comparatively investigated to elucidate the combinational effects of Y and/or La oxide promoters on the catalytic activity and anti-aging performance of monolithic cordierite honeycomb catalysts with low Pt and Rh content. The catalytic activities, water-gas shift (WGS) and steam reforming reaction (SR) were studied under a simulated gas mixture. The catalysts were also characterized by H2-temperature-programmed reduction (H2-TPR) and O2-temperature-programmed desorption (O2-TPD). The results showed that the prepared CeO2-ZrO2-MxOy oxides have a face-centered cubic fluorite structure and are nanosize. La3+ ions can significantly improve thermal stability and efficiently retard CeO2-ZrO2 crystal sintering and growth. Doped CeO2-ZrO2 with Y3+ and La3+ has 105 and 60 m2/g surface area and 460 and 390 μmol/g OSC before and after aging. The T50 of fresh Pt-Rh/CZYL/LA is 170 °C for CO, 222 °C for C3H8 and 189 °C for NO, and shift to 205, 262 and 228 °C after hydrothermal aging, which are better than those of Pt-Rh/CZY/LA or Pt-Rh/CZL/LA. WGS and SR are relate to the OSC of oxygen storage materials and absorbed oxygen species on the catalyst surface and affect the three-way catalytic activities of catalysts. The reductive property of noble metals and the dissociatively adsorbed O2 on the surface of catalysts are closely related to the catalytic activities.

High-pressure Raman study on the superconducting pyrochlore oxide Cd2Re2O7

NASA Astrophysics Data System (ADS)

Matsubayashi, Yasuhito; Hasegawa, Takumi; Ogita, Norio; Yamaura, Jun-ichi; Hiroi, Zenji

2018-05-01

The superconducting pyrochlore oxide Cd2Re2O7 (Tc = 1 K), which is now considered as a candidate of the spin-orbit-coupled metal, shows an inversion-symmetry-breaking structural transition at Ts1 = 200 K . Ts1 decreases with increasing pressure and disappears at around Pc = 4.2 GPa , where at least four high-pressure phases with tiny structural distortions are suggested by means of powder X-ray diffraction [Yamaura PRB 2017]. We have carried out Raman scattering experiments to investigate changes in the crystal symmetry under high pressures up to 4.8 GPa. A structural transition at 1.9-3.0 GPa and the recovery of inversion symmetry above Pc are observed at 12 K.

Ion irradiation of ternary pyrochlore oxides.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lumpkin, G. R.; Smith, K. L.; Blackford, M. G.

2009-05-01

Polycrystalline synthetic samples of Y{sub 2}Ti{sub 2-x}Sn{sub x}O{sub 7} with x = 0.4, 0.8, 1.2, and 1.6, together with Nd{sub 2}Zr{sub 2}O{sub 7}, Nd{sub 2}Zr{sub 1.2}Ti{sub 0.8}O{sub 7}, and La{sub 1.6}Y{sub 0.4}Hf{sub 2}O{sub 7}, were irradiated in situ in the intermediate voltage electron microscope (IVEM)-Tandem Facility at Argonne National Laboratory using 1.0 MeV Kr ions at temperatures of 50 to 650 K. Determination of the critical amorphization fluence (F{sub c}) as a function of temperature has revealed a dramatic increase in radiation tolerance with increasing Sn content on the pyrochlore B site. Nonlinear least-squares analysis of the fluence-temperature curves gavemore » critical temperatures (T{sub c}) of 666 {+-} 4, 335 {+-} 12, and 251 {+-} 51 K for the Y{sub 2}Ti{sub 2-x}Sn{sub x}O{sub 7} samples with x = 0.4, 0.8, and 1.2, respectively. The sample with x = 1.6 appears to disorder to a defect fluorite structure at a fluence below 1.25 x 10{sup 15} ions cm{sup -2} and remains crystalline to 5 x 10{sup 15} ions cm{sup -2} at 50 K. Additionally, the critical fluence-temperature response curves were determined for Nd{sub 2}Zr{sub 1.2}Ti{sub 0.8}O{sub 7} and La{sub 1.6}Y{sub 0.4}Hf{sub 2}O{sub 7}, and we obtained T{sub c} values of 685 {+-} 53 K and 473 {+-} 52 K, respectively, for these pyrochlores. Nd{sub 2}Zr{sub 2}O{sub 7} did not become amorphous after a fluence of 2.5 x 10{sup 15} ions cm{sup -2} at 50 K, but there is evidence that it may amorphize at a higher fluence, with an estimated T{sub c} of 135 K. The observed T{sub c} results are discussed with respect to the predicted T{sub c} values based upon a previously published empirical model (Lumpkin, G. R.; Pruneda, M.; Rios, S.; Smith, K. L.; Trachenko, K.; Whittle, K. R.; Zaluzec, N. J. J. Solid State Chem. 2007, 180, 1512). In the Y{sub 2}Ti{sub 2-x}Sn{sub x}O{sub 7} pyrochlores, T{sub c} appears to be linear with respect to composition, and is linear with respect to r{sub A}/r{sub B} and x

Disappearance of the metal-insulator transition in iridate pyrochlores on approaching the ideal R2Ir2O7 stoichiometry

NASA Astrophysics Data System (ADS)

Sleight, Arthur W.; Ramirez, Arthur P.

2018-07-01

Recently, rare earth iridates, R2Ir2O7, with the pyrochlore structure have been intensively investigated due to their promise as either topological Mott insulators or Weyl semimetals. Single crystals of such pyrochlores with R = Nd, Sm, Eu, and Dy were prepared hydrothermally in sealed gold tubes at 975 K and show significantly higher electrical resistivities than previously reported for either crystals or polycrystalline samples. Furthermore, none of the present crystals exhibit the metal-insulator transition found for some samples of these phases. Lower resistivities are ascribed to lack of control of x and y in R2-xIr2O7-y in other more commonly used synthesis methods, yielding uncertainty in the Ir oxidation state. We also report resistivity of R2Ru2O7 crystals for R = Yb, Gd, Eu, and Nd, prepared in the same manner. These results suggest that the observed charge transport in hydrothermally grown iridate crystals is that of essentially stoichiometric phases and is consistent a with the existence of Weyl nodes.

Isotope effect on superconductivity and Raman phonons of Pyrochlore Cd2Re2O7

NASA Astrophysics Data System (ADS)

Razavi, F. S.; Hajialamdari, M.; Reedyk, M.; Kremer, R. K.

2018-06-01

Cd2Re2O7 is the only α-Pyrochlore exhibiting superconductivity with a transition temperature (Tc) of ∼ 1 K. In this study, we present the effect of oxygen isotope (18O) as well as combined 18O and cadmium isotope (116Cd) substitution on the superconductivity and Raman scattering spectrum of Cd2Re2O7. The change of Tc and the energy gap Δ(T) are reported using various techniques including point contact spectroscopy. The shift in Raman phonon frequencies upon isotope substitution will be compared with measurement of the isotope effect on the superconducting transition temperature.

Two-magnon scattering in the 5d all-in-all-out pyrochlore magnet Cd2Os2O7.

PubMed

Nguyen, Thi Minh Hien; Sandilands, Luke J; Sohn, C H; Kim, C H; Wysocki, Aleksander L; Yang, In-Sang; Moon, S J; Ko, Jae-Hyeon; Yamaura, J; Hiroi, Z; Noh, Tae Won

2017-08-15

5d pyrochlore oxides with all-in-all-out magnetic order are prime candidates for realizing strongly correlated, topological phases of matter. Despite significant effort, a full understanding of all-in-all-out magnetism remains elusive as the associated magnetic excitations have proven difficult to access with conventional techniques. Here we report a Raman spectroscopy study of spin dynamics in the all-in-all-out magnetic state of the 5d pyrochlore Cd 2 Os 2 O 7 . Through a comparison between the two-magnon scattering and spin-wave theory, we confirm the large single ion anisotropy in this material and show that the Dzyaloshinskii-Moriya and exchange interactions play a significant role in the spin-wave dispersions. The Raman data also reveal complex spin-charge-lattice coupling and indicate that the metal-insulator transition in Cd 2 Os 2 O 7 is Lifshitz-type. Our work establishes Raman scattering as a simple and powerful method for exploring the spin dynamics in 5d pyrochlore magnets.Pyrochlore 5d transition metal oxides are expected to have interesting forms of magnetic order but are hard to study with conventional probes. Here the authors show that Raman scattering can be used to measure magnetic excitations in Cd 2 Os 2 O 7 and that it exhibits complex spin-charge-lattice coupling.

Charge dynamics in the colossal magnetoresistance pyrochlore Tl2Mn2O7

NASA Astrophysics Data System (ADS)

Okamura, H.; Koretsune, T.; Matsunami, M.; Kimura, S.; Nanba, T.; Imai, H.; Shimakawa, Y.; Kubo, Y.

2001-11-01

Optical conductivity data [σ(ω)] of the colossal magnetoresistance (CMR) pyrochlore Tl2Mn2O7 are presented as functions of temperature (T) and external magnetic field (B). Upon cooling and upon applying B near the Curie temperature, where the CMR manifests itself, σ(ω) shows a clear transition from an insulatorlike to a metallic electronic structure as evidenced by the emergence of a pronounced Drude-like component below ~0.2 eV. Analyses on the σ(ω) spectra show that both T- and B-induced evolutions of the electronic structure are very similar to each other, and that they are universally related to the development of macroscopic magnetization (M). In particular, the effective carrier density obtained from σ(ω) scales with M2 over wide ranges of T and B. The contributions to the CMR from the carrier effective mass and scattering time are also evaluated from the data.

Crystal-field, exchange interactions and magnetism in pyrochlore ferromagnet R2V2O7 (R3+=Y, Lu)

NASA Astrophysics Data System (ADS)

Ali Biswas, A.; Jana, Y. M.

2013-03-01

The temperature dependence of the observed bulk magnetic susceptibility, magnetization, paramagnetic Curie temperature θCW, magnetic specific heat of ferromagnetic semi-conducting pyrochlore-based vanadate compounds Y2V2O7 and Lu2V2O7, which are the simplest of R2M2O7 pyrochlore series of oxides, are simulated and analyzed, simultaneously and consistently, within the frame work of the appropriate crystal-field (CF) theory and a mean-field approximation by introducing effective anisotropic molecular-field tensors and also taking account of appreciable spin-orbit coupling. The electronic and magnetic properties are correlated to the structural parameters. Ten-fold degenerate 2D term of 3d1 V4+-ions is split into five Kramers doublets with overall CF splitting Δ1≈2 eV and the total splitting of the 2T2g state Δ0≈0.4 eV under combined actions of octahedral CF, trigonal (D3d) distortion at V-site and spin-orbit coupling. The ground doublet is a well-isolated effectively spin s=1/2 state, characterized by the anisotropic g-tensors and directional magnetic moments. The degeneracy of the ground state is lifted by the spin-spin correlations among V4-tetrahedra at T∼170 K, which causes the formation of ferromagnetic clusters in these pyrochlores. The temperature dependence of the calculated directional site-susceptibilities shows that the V4+ ions have a substantial easy-axis single-ion anisotropy along local <111> axis of a given V4-tetrahedron in the magnetic phase where ferromagnetic clusters coexist with paramagnetic phase.

Low energy ion-solid interactions and chemistry effects in a series of pyrochlores

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dong, Liyuan; Li, Yuhong; Devanathan, Ram

The effect of chemistry on low energy recoil events was investigated at 10 K for each type of atom in pyrochlores using molecular dynamics simulation. Contour plots of the threshold displacement energy (Ed) in Gd2Zr2O7 have been produced along more than 80 directions for each individual species. The Ed surface for each type of atom in Gd2Zr2O7 is highly anisotropic; Ed of Zr exhibits the largest degree of anisotropy, while that of O8b exhibits the smallest. The recommended values of Ed in Gd2Zr2O7 based on the observed minima are 56, 94 and 25 eV, respectively for Gd, Zr and O.more » The influence of cation radius on Ed in pyrochlores A2B2O7 (with A-site ranging from Lu3+ to La3+ and B-site ranging from Ti4+ to Ce4+) was also investigated along three directions [100], [110] and [111]. The Ed in pyrochlores strongly depended on the atom type, atom mass, knock-on direction, and lattice position. The defects produced after low energy displacement events included cation antisite defects, cation Frenkel pairs, anion Frenkel pairs, various vacancies and interstitials. Ce doping in pyrochlores may affect the radiation response, because it resulted in drastic changes in cation and anion displacement energies and formation of an unusual type of anti-site defect. This work demonstrates links between Ed and amorphization resistance.« less

Frequency dependent dielectric properties of combustion synthesized Dy2Ti2O7 pyrochlore oxide

NASA Astrophysics Data System (ADS)

Jeyasingh, T.; Saji, S. K.; Kavitha, V. T.; Wariar, P. R. S.

2018-05-01

Nanocrystalline pyrochlore material Dysprosium Titanate (Dy2Ti2O7) has been synthesized through a single step optimized combustion route. The phase purity and phase formation of the combustion product has been characterized using X-Ray diffraction analysis (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR) analysis. X-Ray diffraction analysis (XRD) reveal that Dy2Ti2O7 is highly crystalline in nature with cubic structure in the Fd3m space group. The microstructures and average particle size of the prepared nanopowder were examined by High Resolution Transmission Electron Microscopy (HR-TEM). The optical band gap of the Dy2Ti2O7 nanoparticles is determined from the absorption spectrum, was attributed to direct allowed transitions through optical band gap of 3.98 eV. The frequency dependent dielectric measurements have been carried out on the sintered pellet in the frequency range 1 Hz-10 MHz. The measured value of dielectric constant (ℇ') was ˜ 43 and loss tangent (tan δ) was 4×10-3 at 1 MHz, at room temperature.

Nuclear waste disposal—pyrochlore (A2B2O7): Nuclear waste form for the immobilization of plutonium and "minor" actinides

NASA Astrophysics Data System (ADS)

Ewing, Rodney C.; Weber, William J.; Lian, Jie

2004-06-01

During the past half-century, the nuclear fuel cycle has generated approximately 1400 metric tons of plutonium and substantial quantities of the "minor" actinides, such as Np, Am, and Cm. The successful disposition of these actinides has an important impact on the strategy for developing advanced nuclear fuel cycles, weapons proliferation, and the geologic disposal of high-level radioactive waste. During the last decade, there has been substantial interest in the use of the isometric pyrochlore structure-type, A2B2O7, for the immobilization of actinides. Most of the interest has focused on titanate-pyrochlore because of its chemical durability; however, these compositions experience a radiation-induced transition from the crystalline-to-aperiodic state due to radiation damage from the alpha-decay of actinides. Depending on the actinide concentration, the titanate pyrochlore will become amorphous in less than 1000 years of storage. Recently, systematic ion beam irradiations of a variety of pyrochlore compositions has revealed that many zirconate pyrochlores do not become amorphous, but remain crystalline as a defect fluorite structure-type due to disordering of the A- and B-site cations. The zirconate pyrochlores will remain crystalline even to very high doses, greater than 100 displacements per atom. Systematic experimental studies of actinide-doped and ion beam-irradiated pyrochlore, analyses of natural U- and Th-bearing pyrochlore, and simulations of the energetics of the disordering process now provide a rather detailed understanding of the structural and chemical controls on the response of pyrochlore to radiation. These results provide a solid basis for predicting the behavior and durability of pyrochlore used to immobilize plutonium.

Hot corrosion behavior of YSZ, Gd2Zr2O7 and YSZ/Gd2Zr2O7 thermal barrier coatings exposed to molten sulfate and vanadate salt

NASA Astrophysics Data System (ADS)

Ozgurluk, Yasin; Doleker, Kadir Mert; Karaoglanli, Abdullah Cahit

2018-04-01

Thermal barrier coatings (TBCs) are mostly used in critical components of aircraft gas turbine engines. Hot corrosion is among the main deteriorating factors in TBCs which results from the effect of molten salt on the coating-gas interface. This type of corrosion is observed as a result of contamination accumulated during combustion processes. Fuels used in aviation industry generally contain impurities such as vanadium oxide (V2O5) and sodium sulfate (Na2SO4). These impurities damage turbines' inlet at elevated temperatures because of chemical reaction. Yttria stabilized zirconia (YSZ) is a conventional top coating material for TBCs while Gd2Zr2O7 is a new promising top coating material for TBCs. In this study, CoNiCrAlY metallic bond coat was deposited on Inconel 718 nickel based superalloy substrate material with a thickness about 100 μm using cold gas dynamic spray (CGDS) method. Production of TBCs were done with deposition of YSZ, Gd2Zr2O7, YSZ/Gd2Zr2O7 ceramic top coating materials using EB-PVD method, having a total thickness of 300 μm. Hot corrosion behavior of YSZ, Gd2Zr2O7, YSZ/Gd2Zr2O7 TBC systems were exposed to 45 wt.% Na2SO4 and 55 wt.% V2O5 molten salt mixtures at 1000 °C temperature. TBC samples were investigated and compared using scanning electron microscope (SEM), energy dispersive spectroscopy (EDS) analysis and X-ray diffractometer (XRD). The hot corrosion failure mechanisms of YSZ, Gd2Zr2O7 and YSZ/Gd2Zr2O7 TBCs in the molten salts were evaluated.

Surface Crystallization of a MgO/Y2O3/SiO2/Al2O3/ZrO2 Glass: Growth of an Oriented β-Y2Si2O7 Layer and Epitaxial ZrO2

PubMed Central

Wisniewski, Wolfgang; Seidel, Sabrina; Patzig, Christian; Rüssel, Christian

2017-01-01

The crystallization behavior of a glass with the composition 54.7 SiO2·10.9 Al2O3·15.0 MgO·3.4 ZrO2·16.0 Y2O3 is studied using X-ray diffraction (XRD), scanning electron microscopy (SEM) including electron backscatter diffraction (EBSD) and (scanning) transmission electron microscopy [(S)TEM] including energy-dispersive X-ray spectrometry (EDXS). This glass shows the sole surface crystallization of four different yttrium silicates of the composition Y2Si2O7 (YS). The almost simultaneous but independent nucleation of α-, β-, δ-, and ε-YS at the surface is followed by growth into the bulk, where ε-YS quickly dominates a first crystallized layer. An accumulation of Mg at the growth front probably triggers a secondary nucleation of β-YS, which forms a thin compact layer before fragmenting into a highly oriented layer of fine grained crystals occupying the remaining bulk. The residual glass between the YS growth structures allows the crystallization of indialite, yttrium stabilized ZrO2 (Y-ZrO2) and very probably μ-cordierite during cooling. Hence, this glass basically shows the inverted order of crystallization observed in other magnesium yttrium alumosilicate glasses containing less Y2O3. An epitaxial relationship between Y-ZrO2 and ε-YS is proven and multiple twinning relationships occur in the YS phases. PMID:28281661

Fragile singlet ground-state magnetism in the pyrochlore osmates R 2 Os 2 O 7 ( R = Y and Ho)

DOE PAGES

Zhao, Z. Y.; Calder, S.; Aczel, A. A.; ...

2016-04-25

The singlet ground state magnetism in pyrochlore osmates Y 2Os 2O 7 and Ho 2Os 2O 7 is studied by DC and AC susceptibility, specific heat, and neutron powder diffraction measurements. Despite the expected non-magnetic singlet in the strong spin-orbit coupling (SOC) limit for Os 4+ (5d 4), Y 2Os 2O 7 exhibits a spin-glass (SG) ground state below 4 K with weak magnetism, suggesting possible proximity to a quantum phase transition between the non-magnetic state in the strong SOC limit and the magnetic state in the strong superexchange limit. Ho 2Os 2O 7 has the same structural distortion asmore » occurs in Y 2Os 2O 7. However, the Os sublattice in Ho 2Os 2O 7 shows long- range magnetic ordering below 36 K. We find that the sharp difference of the magnetic ground state between Y 2Os 2O 7 and Ho 2Os 2O 7 signals the singlet ground state magnetism in R 2 Os 2 O 7 is fragile and can be disturbed by the weak 4f—5d interactions.« less

Fragile singlet ground-state magnetism in the pyrochlore osmates R 2 Os 2 O 7 ( R = Y and Ho)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhao, Z. Y.; Calder, S.; Aczel, A. A.

The singlet ground state magnetism in pyrochlore osmates Y 2Os 2O 7 and Ho 2Os 2O 7 is studied by DC and AC susceptibility, specific heat, and neutron powder diffraction measurements. Despite the expected non-magnetic singlet in the strong spin-orbit coupling (SOC) limit for Os 4+ (5d 4), Y 2Os 2O 7 exhibits a spin-glass (SG) ground state below 4 K with weak magnetism, suggesting possible proximity to a quantum phase transition between the non-magnetic state in the strong SOC limit and the magnetic state in the strong superexchange limit. Ho 2Os 2O 7 has the same structural distortion asmore » occurs in Y 2Os 2O 7. However, the Os sublattice in Ho 2Os 2O 7 shows long- range magnetic ordering below 36 K. We find that the sharp difference of the magnetic ground state between Y 2Os 2O 7 and Ho 2Os 2O 7 signals the singlet ground state magnetism in R 2 Os 2 O 7 is fragile and can be disturbed by the weak 4f—5d interactions.« less

Investigation of Thermal Conductivities and Expansion Coefficients of (Yb1 - x La x )2AlTaO7 Ceramics

NASA Astrophysics Data System (ADS)

Xiaoge, Chen; Hongsong, Zhang; Sai, Su; Yongde, Zhao; An, Tang; Haoming, Zhang

2017-12-01

The (Yb1 - x La x )2AlTaO7 ( x = 0, 0.1, 0.3, 0.5) ceramics were prepared by solid-state reaction method. The phase composition, microstructure, thermophysical properties of (Yb1 - x La x )2AlTaO7 ceramics were investigated. Results reveal that (Yb1 - x La x )2AlTaO7 ( x = 0, 0.1, 0.3) ceramics exhibit a single pyrochlore-type structure, and the (Yb0.5La0.5)2AlTaO7 has an orthorhombic weberite structure. The thermal conductivities of (Yb1 - x La x )2AlTaO7 ( x = 0, 0.1, 0.3) ceramics decrease with increasing Yb2O3 contents. (Yb0.5La0.5)2AlTaO7 has the highest thermal conductivity among all the ceramics studied, within the range of 1.48-1.75 W/m K (20-1200 °C). The thermal expansion coefficients of (Yb1 - x La x )2AlTaO7 ceramics decrease gradually with increasing La2O3 fractions, and the thermal expansion coefficients are close to those of YSZ.

Oxidant effect of La(NO3)3·6H2O solution on the crystalline characteristics of nanocrystalline ZrO2 films grown by atomic layer deposition

NASA Astrophysics Data System (ADS)

Oh, Nam Khen; Kim, Jin-Tae; Kang, Goru; An, Jong-Ki; Nam, Minwoo; Kim, So Yeon; Park, In-Sung; Yun, Ju-Young

2017-02-01

Nanocrystalline ZrO2 films were synthesized by atomic layer deposition method using CpZr[N(CH3)2]3 (Cp = C5H5) as the metal precursor and La(NO3)3·6H2O solution as the oxygen source. La element in the deposited ZrO2 films could not be detected as its content was below the resolution limit of the X-ray photoelectron spectroscopy. The alternative introduction of La(NO3)3·6H2O solution to conventionally used H2O as the oxidant effectively altered the crystalline structure, grain size, and surface roughness of the grown ZrO2 films. Specifically, the crystalline structure of the ZrO2 film changed from a mixture of tetragonal and monoclinic phases to monoclinic phase. The average grain size also increased, and the resulting film surface became rougher. The average grain sizes of the ZrO2 films prepared from La(NO3)3·6H2O solution at concentrations of 10, 20, 30, and 40% were 280, 256, 208, and 200 nm, respectively, whereas that prepared using H2O oxidant was 142 nm. However, the concentration of La(NO3)3·6H2O solution minimally influenced the crystalline characteristics of the nanocrystalline ZrO2 films i.e., the crystalline structure, grain size, and surface roughness except for crystallite size.

Magnetic dilution and domain selection in the X Y pyrochlore antiferromagnet Er2Ti2O7

NASA Astrophysics Data System (ADS)

Gaudet, J.; Hallas, A. M.; Maharaj, D. D.; Buhariwalla, C. R. C.; Kermarrec, E.; Butch, N. P.; Munsie, T. J. S.; Dabkowska, H. A.; Luke, G. M.; Gaulin, B. D.

2016-08-01

Below TN=1.1 K, the X Y pyrochlore Er2Ti2O7 orders into a k =0 noncollinear, antiferromagnetic structure referred to as the ψ2 state. The magnetic order in Er2Ti2O7 is known to obey conventional three-dimensional (3D) percolation in the presence of magnetic dilution, and in that sense is robust to disorder. Recently, however, two theoretical studies have predicted that the ψ2 structure should be unstable to the formation of a related ψ3 magnetic structure in the presence of magnetic vacancies. To investigate these theories, we have carried out systematic elastic and inelastic neutron scattering studies of three single crystals of Er2 -xYxTi2O7 with x =0 (pure), 0.2 (10 %Y ) and 0.4 (20 % Y ), where magnetic Er3 + is substituted by nonmagnetic Y3 +. We find that the ψ2 ground state of pure Er2Ti2O7 is significantly affected by magnetic dilution. The characteristic domain selection associated with the ψ2 state, and the corresponding energy gap separating ψ2 from ψ3, vanish for Y3 + substitutions between 10 % Y and 20 % Y , far removed from the three-dimensional percolation threshold of ˜60 % Y . The resulting ground state for Er2Ti2O7 with magnetic dilutions from 20 % Y up to the percolation threshold is naturally interpreted as a frozen mosaic of ψ2 and ψ3 domains.

Two-magnon scattering in the 5d all-in-all-out pyrochlore magnet Cd 2Os 2O 7

DOE PAGES

Nguyen, Thi Minh Hien; Sandilands, Luke J.; Sohn, C. H.; ...

2017-08-15

5d pyrochlore oxides with all-in-all-out magnetic order are prime candidates for realizing strongly correlated, topological phases of matter. Despite significant effort, a full understanding of all-in-all-out magnetism remains elusive as the associated magnetic excitations have proven difficult to access with conventional techniques. Here we report a Raman spectroscopy study of spin dynamics in the all-in-all-out magnetic state of the 5d pyrochlore Cd 2Os 2O 7. Through a comparison between the two-magnon scattering and spin-wave theory, we confirm the large single ion anisotropy in this material and show that the Dzyaloshinskii–Moriya and exchange interactions play a significant role in the spin-wavemore » dispersions. The Raman data also reveal complex spin–charge–lattice coupling and indicate that the metal–insulator transition in Cd 2Os 2O 7 is Lifshitz-type. In conclusion, our work establishes Raman scattering as a simple and powerful method for exploring the spin dynamics in 5d pyrochlore magnets.« less

Krypton ion irradiation-induced amorphization and nano-crystal formation in pyrochlore Lu2Ti2O7 at room temperature

NASA Astrophysics Data System (ADS)

Xie, Qiu-Rong; Zhang, Jian; Yin, Dong-Min; Guo, Qi-Xun; Li, Ning

2015-12-01

Polycrystalline pyrochlore Lu2Ti2O7 pellets are irradiated with 600-keV Kr3+ ions up to a fluence of 1.45 × 1016 Kr3+/cm2. Irradiation induced structural modifications are examined by using grazing incidence x-ray diffraction (GIXRD) and cross-sectional transmission electron microscopy (TEM). The GIXRD reveals that amorphous fraction increases with the increase of fluences up to 2 × 1015 Kr3+/cm2, and the results are explained with a direct-impact model. However, when the irradiation fluence is higher than 2 × 1015 Kr3+/cm2, the amorphous fraction reaches a saturation of ∼80%. Further TEM observations imply that nano-crystal is formed with a diameter of ∼10 nm within the irradiation layer at a fluence of 4 × 1015 Kr3+/cm2. No full amorphization is achieved even at the highest fluence of 1.45 × 1016 Kr3+/cm2 (∼36 displacement per atom). The high irradiation resistance of pyrochlore Lu2Ti2O7 at higher fluence is explained on the basis of enhanced radiation tolerance of nano-crystal structure. Project sponsored by the National Natural Science Foundation of China (Grant No. 11205128) and the Fundamental Research Funds for the Central Universities, China (Grant No. 2012121034).

Correlation and the mechanism of lithium ion diffusion with the crystal structure of Li7La3Zr2O12 revealed by an internal friction technique.

PubMed

Wang, X P; Gao, Y X; Xia, Y P; Zhuang, Z; Zhang, T; Fang, Q F

2014-04-21

The correlation and transport mechanism of lithium ions with the crystal structure of a fast lithium ion conductor Li7La3Zr2O12 are mainly investigated by internal friction (IF) and AC impedance spectroscopy techniques. Compared with the poor conductivity of tetragonal Li7La3Zr2O12, the Al stabilized cubic phase exhibits a good ionic conductivity that can be up to 1.9 × 10(-4) S cm(-1) at room temperature, which can be ascribed to the disordered distribution of lithium ions in the cubic phase. A well-pronounced relaxation IF peak (labeled as peak PC) is observed in the cubic phase while a very weak IF peak (labeled as PT) is observed in the tetragonal phase, further evidencing the difference in lithium ion migration in the two phases. Peak PC can be decomposed into two sub-peaks with the activation energy and the pre-exponential factor of relaxation time being E1 = 0.41 eV and τ01 = 1.2 × 10(-14) s for the lower temperature peak PC1 and E2 = 0.35 eV and τ02 = 1.9 × 10(-15) s for the higher temperature PC2 peak, respectively. Based on the crystalline structure of a cubic garnet-type Li7La3Zr2O12 compound, an atomistic mechanism of lithium ion diffusion via vacancies is suggested, i.e. 48g(96h) ↔ 48g(96h) for peak PC1 and 48g(96h) ↔ 24d for peak PC2, respectively. The weak PT peak in the tetragonal phase is preliminarily interpreted as due to the short jump process among neighboring octahedral sites and vacant tetrahedral sites.

Method Using Water-Based Solvent to Prepare Li7La3Zr2O12 Solid Electrolytes.

PubMed

Huang, Xiao; Lu, Yang; Jin, Jun; Gu, Sui; Xiu, Tongping; Song, Zhen; Badding, Michael E; Wen, Zhaoyin

2018-05-09

Li-garnet Li 7 La 3 Zr 2 O 12 (LLZO) is a promising candidate of solid electrolytes for high-safety solid-state Li + ion batteries. However, because of its high reactivity to water, the preparation of LLZO powders and ceramics is not easy for large-scale amounts. Herein, a method applying water-based solvent is proposed to demonstrate a possible solution. Ta-doped LLZO, that is, Li 6.4 La 3 Zr 1.4 Ta 0.6 O 12 (LLZTO), and its LLZTO/MgO composite ceramics are made by attrition milling, followed by a spray-drying process using water-based slurries. The impacts of parameters of the method on the structure and properties of green and sintered pellets are studied. A relative density of ∼95%, a Li-ion conductivity of ∼3.5 × 10 -4 S/cm, and uniform grain size LLZTO/MgO garnet composite ceramics are obtained with an attrition-milled LLZTO/MgO slurry that contains 40 wt % solids and 2 wt % polyvinyl alcohol binder. Li-sulfur batteries based on these ceramics are fabricated and work under 25 °C for 20 cycles with a Coulombic efficiency of 100%. This research demonstrates a promising mass production method for the preparation of Li-garnet ceramics.

The solubility and site preference of Fe{sup 3+} in Li{sub 7−3x}Fe{sub x}La{sub 3}Zr{sub 2}O{sub 12} garnets

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rettenwander, D., E-mail: daniel.rettenwander@sbg.ac.at; Geiger, C.A.; Tribus, M.

2015-10-15

A series of Fe{sup 3+}-bearing Li{sub 7}La{sub 3}Zr{sub 2}O{sub 12} (LLZO) garnets was synthesized using solid-state synthesis methods. The synthetic products were characterized compositionally using electron microprobe analysis and inductively coupled plasma optical emission spectroscopy (ICP-OES) and structurally using X-ray powder diffraction and {sup 57}Fe Mössbauer spectroscopy. A maximum of about 0.25 Fe{sup 3+} pfu could be incorporated in Li{sub 7−3x}Fe{sub x}La{sub 3}Zr{sub 2}O{sub 12} garnet solid solutions. At Fe{sup 3+} concentrations lower than about 0.16 pfu, both tetragonal and cubic garnets were obtained in the synthesis experiments. X-ray powder diffraction analysis showed only a garnet phase for syntheses withmore » starting materials having intended Fe{sup 3+} contents lower than 0.52 Fe{sup 3+} pfu. Back-scattered electron images made with an electron microprobe also showed no phase other than garnet for these compositions. The lattice parameter, a{sub 0}, for all solid-solution garnets is similar with a value of a{sub 0}≈12.98 Å regardless of the amount of Fe{sup 3+}. {sup 57}Fe Mössbauer spectroscopic measurements indicate the presence of poorly- or nano-crystalline FeLaO{sub 3} in syntheses with Fe{sup 3+} contents greater than 0.16 Fe{sup 3+} pfu. The composition of different phase pure Li{sub 7−3x}Fe{sub x}La{sub 3}Zr{sub 2}O{sub 12} garnets, as determined by electron microprobe (Fe, La, Zr) and ICP-OES (Li) measurements, give Li{sub 6.89}Fe{sub 0.03}La{sub 3.05}Zr{sub 2.01}O{sub 12}, Li{sub 6.66}Fe{sub 0.06}La{sub 3.06}Zr{sub 2.01}O{sub 12}, Li{sub 6.54}Fe{sub 0.12}La{sub 3.01}Zr{sub 1.98}O{sub 12}, and Li{sub 6.19}Fe{sub 0.19}La{sub 3.02}Zr{sub 2.04}O{sub 12}. The {sup 57}Fe Mössbauer spectrum of cubic Li{sub 6.54}Fe{sub 0.12}La{sub 3.01}Zr{sub 1.98}O{sub 12} garnet indicates that most Fe{sup 3+} occurs at the special crystallographic 24d position, which is the standard tetrahedrally coordinated site in garnet. Fe{sup 3+} in

Effects of stuffing on the atomic and electronic structure of the pyrochlore Yb2Ti2O7

NASA Astrophysics Data System (ADS)

Ghosh, Soham S.; Manousakis, Efstratios

2018-06-01

There are reasons to believe that the ground state of the magnetic rare-earth pyrochlore Yb2Ti2O7 is on the boundary between competing ground states. We have carried out ab initio density functional calculations to determine the most stable chemical formula as a function of the oxygen chemical potential and the likely location of the oxygen atoms in the unit cell of the "stuffed" system. We find that it is energetically favorable in the stuffed crystal (with an Yb replacement on a Ti site) to contain oxygen vacancies which dope the Yb 4 f orbitals and qualitatively change the electronic properties of the system. In addition, with the inclusion of the contribution of spin-orbit coupling (SOC) on top of the GGA + U approach, we investigated the electronic structure and the magnetic moments of the most stable stuffed system. In our determined stuffed structure the valence bands as compared to those of the pure system are pushed down and a change in hybridization between the O 2 p orbitals and the metal ion states is found. Our first-principle findings should form a foundation for effective models describing the low-temperature properties of this material whose true ground state remains controversial.

Density functional analysis of fluorite-structured (Ce, Zr)O 2/CeO 2 interfaces [Density functional analysis of fluorite-structured (Ce, Zr)O 2/CeO 2 interfaces: Implications for catalysis and energy applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Weck, Philippe F.; Juan, Pierre -Alexandre; Dingreville, Remi

The structures and properties of Ce 1–xZr xO 2 (x = 0–1) solid solutions, selected Ce 1–xZr xO 2 surfaces, and Ce 1–xZr xO 2/CeO 2 interfaces were computed within the framework of density functional theory corrected for strong electron correlation (DFT+ U). The calculated Debye temperature increases steadily with Zr content in (Ce, Zr)O 2 phases, indicating a significant rise in microhardness from CeO 2 to ZrO 2, without appreciable loss in ductility as the interfacial stoichiometry changes. Surface energy calculations for the low-index CeO 2(111) and (110) surfaces show limited sensitivity to strong 4f-electron correlation. The fracture energymore » of Ce 1–xZr xO 2(111)/CeO 2(111) increases markedly with Zr content, with a significant decrease in energy for thicker Ce 1–xZr xO 2 films. These findings suggest the crucial role of Zr acting as a binder at the Ce 1–xZr xO 2/CeO 2 interfaces, due to the more covalent character of Zr–O bonds compared to Ce–O. Finally, the impact of surface relaxation upon interface cracking was assessed and found to reach a maximum for Ce 0.25Zr 0.75O 2/CeO 2 interfaces.« less

Density functional analysis of fluorite-structured (Ce, Zr)O 2/CeO 2 interfaces [Density functional analysis of fluorite-structured (Ce, Zr)O 2/CeO 2 interfaces: Implications for catalysis and energy applications

DOE PAGES

Weck, Philippe F.; Juan, Pierre -Alexandre; Dingreville, Remi; ...

2017-06-21

The structures and properties of Ce 1–xZr xO 2 (x = 0–1) solid solutions, selected Ce 1–xZr xO 2 surfaces, and Ce 1–xZr xO 2/CeO 2 interfaces were computed within the framework of density functional theory corrected for strong electron correlation (DFT+ U). The calculated Debye temperature increases steadily with Zr content in (Ce, Zr)O 2 phases, indicating a significant rise in microhardness from CeO 2 to ZrO 2, without appreciable loss in ductility as the interfacial stoichiometry changes. Surface energy calculations for the low-index CeO 2(111) and (110) surfaces show limited sensitivity to strong 4f-electron correlation. The fracture energymore » of Ce 1–xZr xO 2(111)/CeO 2(111) increases markedly with Zr content, with a significant decrease in energy for thicker Ce 1–xZr xO 2 films. These findings suggest the crucial role of Zr acting as a binder at the Ce 1–xZr xO 2/CeO 2 interfaces, due to the more covalent character of Zr–O bonds compared to Ce–O. Finally, the impact of surface relaxation upon interface cracking was assessed and found to reach a maximum for Ce 0.25Zr 0.75O 2/CeO 2 interfaces.« less

17O solid-state NMR spectroscopy of A2B2O7 oxides: quantitative isotopic enrichment and spectral acquisition?

PubMed

Fernandes, Arantxa; Moran, Robert F; Sneddon, Scott; Dawson, Daniel M; McKay, David; Bignami, Giulia P M; Blanc, Frédéric; Whittle, Karl R; Ashbrook, Sharon E

2018-02-13

The potential of 17 O NMR spectroscopy for the investigation of A 2 B 2 O 7 ceramic oxides important in the encapsulation of radioactive waste is demonstrated, with post-synthetic enrichment by exchange with 17 O 2 gas. For Y 2 Sn 2 O 7 , Y 2 Ti 2 O 7 and La 2 Sn 2 O 7 pyrochlores, enrichment of the two distinct O species is clearly non quantitative at lower temperatures (∼700 °C and below) and at shorter times, despite these being used in prior work, with preferential enrichment of OA 2 B 2 favoured over that of OA 4 . At higher temperatures, the 17 O NMR spectra suggest that quantitative enrichment has been achieved, but the integrated signal intensities do not reflect the crystallographic 1 : 6 (O1 : O2) ratio until corrected for differences in T 1 relaxation rates and, more importantly, the contribution of the satellite transitions. 17 O NMR spectra of Y 2 Zr 2 O 7 and Y 2 Hf 2 O 7 defect fluorites showed little difference with any variation in enrichment temperature or time, although an increase in the absolute level of enrichment (up to ∼7.5%) was observed at higher temperature. DFT calculations show that the six distinct resonances observed cannot be assigned unambiguously, as each has contributions from more than one of the five possible next nearest neighbour environments. For La 2 Ti 2 O 7 , which adopts a layered perovskite-like structure, little difference in the spectral intensities is observed with enrichment time or temperature, although the highest absolute levels of enrichment (∼13%) were obtained at higher temperature. This work demonstrates that 17 O NMR has the potential to be a powerful probe of local structure and disorder in oxides, but that considerable care must be taken both in choosing the conditions for 17 O enrichment and the experimental acquisition parameters if the necessary quantitative measurements are to be obtained for more complex systems.

Study of crystal-field interaction in magnetic frustrated lead pyrochlore Gd2Pb2O7

NASA Astrophysics Data System (ADS)

Swarnakar, D.; Jana, Y. M.

2018-05-01

A fine tuning between the crystal field and the molecular field to adopt unique ground state in frustrated magnetic R2M2O7 pyrochlores structures is made by the variation of chemical pressure at R-site caused by substitution of nonmagnetic cation of M-site. Existence of larger cation at M-site increases the lattice parameter or nearest-neighbor bond distance between magnetic R-spins, and causes subtle changes to the local oxygen environment surrounding each R-ion, thereby reduces the chemical pressure at R-site which leads to a dramatic change in the crystal-field and molecular field. To investigate the effect of chemical pressure, the experimental results of powder magnetic susceptibility and isothermal magnetization of the frustrated compound Gd2Pb2O7 containing largest cation, e.g. lead (Pb), at M4+-sites were simulated and analyzed employing a D3d crystal-field (CF) and anisotropic molecular field at R-sites in the self- consistent mean-field approach. The second-ordered axial parameter B20 and total CF splitting of the ground multiplet Gd-ion in Gd2Pb2O7 are 477 cm-1 and 4.8 cm-1 respectively which are the lowest among their isomorphous counterparts, implying reduced effect of the crystal-field at Gd site in Gd2Pb2O7.

A Synthesis and Crystal Chemical Study of the Fast Ion Conductor Li7–3xGaxLa3 Zr2O12 with x = 0.08 to 0.84

PubMed Central

2014-01-01

Fast-conducting phase-pure cubic Ga-bearing Li7La3Zr2O12 was obtained using solid-state synthesis methods with 0.08 to 0.52 Ga3+ pfu in the garnet. An upper limit of 0.72 Ga3+ pfu in garnet was obtained, but the synthesis was accompanied by small amounts of La2Zr2O12 and LiGaO3. The synthetic products were characterized by X-ray powder diffraction, electron microprobe and SEM analyses, ICP-OES measurements, and 71Ga MAS NMR spectroscopy. The unit-cell parameter, a0, of the various garnets does not vary significantly as a function of Ga3+ content, with a value of about 12.984(4) Å. Full chemical analyses for the solid solutions were obtained giving: Li7.08Ga0.06La2.93Zr2.02O12, Li6.50Ga0.15La2.96Zr2.05O12, Li6.48Ga0.23La2.93Zr2.04O12, Li5.93Ga0.36La2.94Zr2.01O12, Li5.38Ga0.53La2.96Zr1.99O12, Li4.82Ga0.60La2.96Zr2.00O12, and Li4.53Ga0.72La2.94Zr1.98O12. The NMR spectra are interpreted as indicating that Ga3+ mainly occurs in a distorted 4-fold coordinated environment that probably corresponds to the general 96h crystallographic site of garnet. PMID:24874559

Strain engineered pyrochlore at high pressure

DOE PAGES

Rittman, Dylan R.; Turner, Katlyn M.; Park, Sulgiye; ...

2017-05-22

Strain engineering is a promising method for next-generation materials processing techniques. Here, we use mechanical milling and annealing followed by compression in diamond anvil cell to tailor the intrinsic and extrinsic strain in pyrochlore, Dy 2Ti 2O 7 and Dy 2Zr 2O 7. Raman spectroscopy, X-ray pair distribution function analysis, and X-ray diffraction were used to characterize atomic order over short-, medium-, and long-range spatial scales, respectively, under ambient conditions. Raman spectroscopy and X-ray diffraction were further employed to interrogate the material in situ at high pressure. High-pressure behavior is found to depend on the species and concentration of defectsmore » in the sample at ambient conditions. Overall, we show that defects can be engineered to lower the phase transformation onset pressure by ~50% in the ordered pyrochlore Dy 2Ti 2O 7, and lower the phase transformation completion pressure by ~20% in the disordered pyrochlore Dy 2Zr 2O 7. Lastly, these improvements are achieved without significantly sacrificing mechanical integrity, as characterized by bulk modulus.« less

Fast crystallization of amorphous Gd{sub 2}Zr{sub 2}O{sub 7} induced by thermally activated electron-beam irradiation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Huang, Zhangyi; Qi, Jianqi, E-mail: qijianqi@scu.edu.cn; Zhou, Li

2015-12-07

We investigate the ionization and displacement effects of an electron-beam (e-beam) on amorphous Gd{sub 2}Zr{sub 2}O{sub 7} synthesized by the co-precipitation and calcination methods. The as-received amorphous specimens were irradiated under electron beams at different energies (80 keV, 120 keV, and 2 MeV) and then characterized by X-ray diffraction and transmission electron microscopy. A metastable fluorite phase was observed in nanocrystalline Gd{sub 2}Zr{sub 2}O{sub 7} and is proposed to arise from the relatively lower surface and interface energy compared with the pyrochlore phase. Fast crystallization could be induced by 120 keV e-beam irradiation (beam current = 0.47 mA/cm{sup 2}). The crystallization occurred on the nanoscale upon ionizationmore » irradiation at 400 °C after a dose of less than 10{sup 17} electrons/cm{sup 2}. Under e-beam irradiation, the activation energy for the grain growth process was approximately 10 kJ/mol, but the activation energy was 135 kJ/mol by calcination in a furnace. The thermally activated ionization process was considered the fast crystallization mechanism.« less

Structure and Stoichiometry in Supervalent Doped Li 7La 3 Zr 2O 12

DOE PAGES

Mukhopadhyay, Saikat; Thompson, Travis; Sakamoto, Jeff; ...

2015-04-20

The oxide garnet material Li 7La 3 Zr 2O 12 shows remarkably high ionic conductivity when doped with supervalent ions that are charge compensated by Li vacancies and is currently one of the best candidates for development of a technologically relevant solid electrolyte. Determination of optimal dopant concentration, however, has remained a persistent problem due to the extreme difficulty of establishing the actual (as compared to nominal) stoichiometry of intentionally doped materials and by the fact that it is still not entirely clear what level of lattice expansion/contraction best promotes. ionic diffusion. By combining careful synthesis, neutron diffraction, high-resolution X-raymore » diffraction (XRD), Raman measurements, and density functional theory calculations, we show that structure and stoichiometry are intimately related such that the former can in many cases be used as a gauge of the latter. We show that different Li-vacancy creating supervalent ions (Al 3+ vs Ta 5+) affect the structure very differently, both in terms of the lattice constant, which is easily measurable, and hi terms of the local structure, which can be difficult or impossible to access experimentally but may have important ramifications for conduction. We carefully correlate the lattice constant to dopant type/concentration via Vegard's law and then further correlate these quantities to relevant local structural parameters. In conclusion, our work opens the possibility of developing a codopant scheme that optimizes the Li vacancy concentration and the lattice size simultaneously.« less

Thermal Spray Deposition, Phase Stability and Mechanical Properties of La2Zr2O7/LaAlO3 Coatings

NASA Astrophysics Data System (ADS)

Lozano-Mandujano, D.; Poblano-Salas, C. A.; Ruiz-Luna, H.; Esparza-Esparza, B.; Giraldo-Betancur, A. L.; Alvarado-Orozco, J. M.; Trápaga-Martínez, L. G.; Muñoz-Saldaña, J.

2017-08-01

This paper deals with the deposition of La2Zr2O7 (LZO) and LaAlO3 (LAO) mixtures by air plasma spray (APS). The raw material for thermal spray, single phase LZO and LAO in a 70:30 mol.% ratio mixture was prepared from commercial metallic oxides by high-energy ball milling (HEBM) and high-temperature solid-state reaction. The HEBM synthesis route, followed by a spray-drying process, successfully produced spherical agglomerates with adequate size distribution and powder-flow properties for feeding an APS system. The as-sprayed coating consisted mainly of a crystalline LZO matrix and partially crystalline LAO, which resulted from the high cooling rate experienced by the molten particles as they impact the substrate. The coatings were annealed at 1100 °C to promote recrystallization of the LAO phase. The reduced elastic modulus and hardness, measured by nanoindentation, increased from 124.1 to 174.7 GPa and from 11.3 to 14.4 GPa, respectively, after the annealing treatment. These values are higher than those reported for YSZ coatings; however, the fracture toughness ( K IC) of the annealed coating was only 1.04 MPa m0.5.

Raman spectroscopy and electron-phonon coupling in Eu3+ doped Gd2Zr2O7 nanopowders

NASA Astrophysics Data System (ADS)

Krizan, G.; Gilic, M.; Ristic-Djurovic, J. L.; Trajic, J.; Romcevic, M.; Krizan, J.; Hadzic, B.; Vasic, B.; Romcevic, N.

2017-11-01

The Raman spectra of Eu3+ doped Gd2Zr2O7 nanopowders were measured. We registered three phonons at 177 cm-1, 268 cm-1, and 592 cm-1, as well as their overtones at 354 cm-1, 445 cm-1, 708 cm-1, 1062 cm-1, 1184 cm-1, ∼1530 cm-1, and ∼1720 cm-1. The phonon at 592 cm-1 is known to be characteristic for Gd2Zr2O7 fluorite-type structure; however, the other two have not been registered so far. We found that the position of the newly detected phonons agrees well with the observed electron-phonon interaction. On the other hand, the registered multiphonon processes were a consequence of miniaturization that further induced changes in electronic structure of Eu3+ doped Gd2Zr2O7 nanopowders.

Electronic and transport properties of fluorite structure of La2Ce2O7

NASA Astrophysics Data System (ADS)

Mahida, H. R.; Singh, Deobrat; Gupta, Sanjeev K.; Sonvane, Yogesh; Thakor, P. B.

2017-05-01

In this paper, we have symmetrically investigated the structural, electronic and transport properties of fluorite structure of lanthanum cerate oxide (La2Ce2O7) using density functional theory (DFT). The electronic band structure of La2Ce2O7 show semiconducting in nature with band gap of 1.54 eV (indirect at R-X points) and 1.71 eV (direct at R points). We have also calculated the susceptibility, hall resistance, electrical, and thermal conductivity by using Boltztrap equation. The electrical conductivity decreases where as thermal conductivity increases with increase in the temperature. Our result shows that La2Ce2O7 has application in Proton exchange membrane (PEM) fuel cells applications.

Possibility of Flat-Band Ferromagnetism in Hole-Doped Pyrochlore Oxides Sn2 Nb2 O7 and Sn2 Ta2 O7

NASA Astrophysics Data System (ADS)

Hase, I.; Yanagisawa, T.; Aiura, Y.; Kawashima, K.

2018-05-01

Quantum mechanics tells us that the hopping integral between local orbitals makes the energy band dispersive. In a lattice with geometric frustration, however, dispersionless flat bands may appear due to quantum interference. Several models possessing flat bands have been proposed theoretically, and many attracting magnetic and electronic properties are predicted. However, despite many attempts to realize these models experimentally, compounds that are appropriately described by this model have not been found so far. Here we show that pyrochlore oxides Sn2 Nb2 O7 and Sn2Ta2O7 are such examples, by performing first-principles band calculation and several tight-binding analyses. Moreover, spin-polarized band calculation shows that the hole-doped systems Sn2 Nb2 O6 N and Sn2 Ta2 O6 N have complete spin polarization, and their magnetic moments are mostly carried by Sn-s and N-p orbitals, which are usually nonmagnetic. These compounds are not only candidates for ferromagnets without a magnetic element, but also will provide an experimental platform for a flat-band model which shows a wide range of physical properties.

Pyrochlore Ce2Zr2O7 decorated over rGO: a photocatalyst that proves to be efficient towards the reduction of 4-nitrophenol and degradation of ciprofloxacin under visible light.

PubMed

Mansingh, Sriram; Acharya, Rashmi; Martha, Satyabadi; Parida, K M

2018-04-18

In the present study, a series of Ce2Zr2O7@rGO nanocomposites were synthesized using a simple solution combustion method followed by a photoreduction technique. The as-prepared samples were well characterised using various analytical techniques to determine the morphological, optical, structural, electrochemical and compositional properties. The presence of oxygen defects was observed from Raman and photoluminescence spectra. The photoreduction of GO to rGO was determined from Raman and Fourier-transform infrared (FTIR) spectroscopy results. The role of rGO proved to be quite significant for the enhanced photocatalytic activity of the nanocomposites. The synergistic communication between Ce2Zr2O7 and rGO accelerates the photoreduction of 4-nitrophenol along with the degradation of ciprofloxacin under visible light irradiation. Of the rGO nanocomposites, 3 wt% GO loaded Ce2Zr2O7 reduces 99% of 20 ppm of 4-nitrophenol to 4-aminophenol in 120 min and decomposes 10 ppm of ciprofloxacin by up to 89% in 60 min. The significant enhancement in the activity of the Ce2Zr2O7@rGO nanocomposite was ascribed to the effective charge separation of excitons through π-conjugation of graphene at the interface, which is well supported by the impedance, photoluminescence and photocatalytic results.

Effects of interfacial layer on characteristics of TiN/ZrO2 structures.

PubMed

Kim, Younsoo; Kang, Sang Yeol; Choi, Jae Hyoung; Lim, Jae Soon; Park, Min Young; Chung, Suk-Jin; Chung, Jaegwan; Lee, Hyung Ik; Kim, Ki Hong; Kyoung, Yong Koo; Heo, Sung; Yoo, Cha Young; Kang, Ho-Kyu

2011-09-01

To minimize the formation of unwanted interfacial layers, thin interfacial layer (ZrCN layer) was deposited between TiN bottom electrode and ZrO2 dielectric in TiN/ZrO2/TiN capacitor. Carbon and nitrogen were also involved in the layer because ZrCN layer was thermally deposited using TEMAZ without any reactant. Electrical characteristics of TiN/ZrO2/TiN capacitor were improved by insertion of ZrCN layer. The oxidation of TiN bottom electrode was largely inhibited at TiN/ZrCN/ZrO2 structure compared to TiN/ZrO2 structure. While the sheet resistance of TiN/ZrCN/ZrO2 structure was constantly sustained with increasing ZrO2 thickness, the large increase of sheet resistance was observed in TiN/ZrO2 structure after 6 nm ZrO2 deposition. When ZrO2 films were deposited on ZrCN layer, the deposition rate of ZrO2 also increased. It is believed that ZrCN layer acted both as a protection layer of TiN oxidation and a seed layer of ZrO2 growth.

The Pressure-Induced Structural Response of A2Hf2O7 (A=Y, Sm, Eu, Gd, Dy, Yb) Compounds from 0.1-50 GPa

NASA Astrophysics Data System (ADS)

Turner, K. M.; Rittman, D.; Heymach, R.; Turner, M.; Tracy, C.; Mao, W. L.; Ewing, R. C.

2016-12-01

A2B2O7 (A, B= cations) compounds have structures that make their properties conducive to many applications; for example they are a proposed waste-form for actinides generated in the nuclear fuel cycle. This interest in part is due to their structural responses to extreme environments of high P, T, or under intense irradiation. Depending on their cationic radius ratio, ra/rb, A2B2O7 compounds either crystallize as pyrochlore (ra/rb=1.46-1.7) or "defect fluorite" (ra/rb>1.46). The structure types are similar: they are derivatives of ideal fluorite with two cations and 1/8 missing anions. In pyrochlore, the cations and anion vacancy are ordered. In "defect fluorite"-structured oxides, the cations and anion vacancies are random. A2B2O7 compounds rarely amorphize in extreme environments. Rather, they disorder and undergo phase transitions; this resistance to amorphization contributes to the durability of this potential actinide waste-form. Under high-pressure, A2B2O7 compounds are known to disorder or form a cottunite-like phase. Their radius ratio affects their response to extreme environments; "defect fluorite" type compounds tend to disorder, and pyrochlore type compounds tend to form the cottunite-like phase. We have examined six A2Hf2O7 compounds (A=Y, Sm, Eu, Gd, Dy, Yb) in situ to 50 GPa. By keeping the B-site constant (Hf), we examined the effect of a changing radius ratio on the pressure-induced structural response of hafnates. We used symmetric DACs, ruby fluorescence, stainless steel gaskets, and methanol: ethanol (4:1 by volume) pressure medium. We characterized these materials with in situ Raman spectroscopy at Stanford University, and synchrotron X-Ray Diffraction (XRD) at APS 16 BM-D and ALS 12.2.2. The compounds were pyrochlore structured (Sm, Eu, Gd) and "defect-fluorite" structured (Y, Dy, Yb) hafnates . These compounds undergo a slow phase transition to a high-pressure cotunnite-like phase between 18-30 GPa. They undergo disordering of their cation

Structural, negative thermal expansion and photocatalytic properties of ZrV{sub 2}O{sub 7}: a comparative study between fibers and powders

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Qinqin, E-mail: liu_qin_qin@126.com; Yang, Juan; Rong, Xiaoqing

2014-10-15

Novel ZrV{sub 2}O{sub 7} microfibers with diameters about 1–3 μm were synthesized using a sol–gel technique. For comparison, ZrV{sub 2}O{sub 7} powders were prepared by the same method. The resultant structures were studied by X-ray diffraction, field-emission scanning electron microscopy and transmission electron microscopy. The results indicated that both the pure ZrV{sub 2}O{sub 7} microfibers and powders could be synthesized by the sol–gel technique. The thermal expansion property of the as-prepared ZrV{sub 2}O{sub 7} microfibers and powders was characterized by a thermal mechanical analyzer, both the fibers with cylindrical morphology and irregular powders with average size between 100 and 200more » nm showed negative thermal expansion between 150 °C and 600 °C. The photocatalytic activity of the microfibers was compared to that of powders under UV radiations. The band gap of ZrV{sub 2}O{sub 7} microfibers decreased and its absorption edge exhibited red shift. The microfibers also had a higher surface area compared with the powders, resulting in considerably higher photocatalytic characteristics. The large surface area and the enhanced photocatalytic activity of the ZrV{sub 2}O{sub 7} microfibers also offer potential applications in sensors and inorganic ion exchangers. - Graphical abstract: (a and c) SEM photos of ZrV{sub 2}O{sub 7} powders and fibers. (b and d) TEM images of ZrV{sub 2}O{sub 7} powders and fibers. (e) Thermal expansion curves of ZrV{sub 2}O{sub 7} powders and fibers. (f) Degradation curves of ZrV{sub 2}O{sub 7} powders and ZrV{sub 2}O{sub 7} fibers. - Highlights: • Novel ZrV{sub 2}O{sub 7} fibers could be synthesized using sol–gel technique. • ZrV{sub 2}O{sub 7} powders with irregular shape are also prepared for comparison. • Both ZrV{sub 2}O{sub 7} microfibers and powders exhibit negative thermal expansion property. • ZrV{sub 2}O{sub 7} microfibers show outstanding photocatalytic activity under UV irradiation. • This

Electronic structure of layered ferroelectric high-k titanate La2Ti2O7

NASA Astrophysics Data System (ADS)

Atuchin, V. V.; Gavrilova, T. A.; Grivel, J.-C.; Kesler, V. G.

2009-02-01

The electronic structure of binary titanate La2Ti2O7 has been studied by x-ray photoelectron spectroscopy. Spectral features of valence band and all constituent element core levels have been considered. The Auger parameters of titanium and oxygen in La2Ti2O7 are determined as αTi = 872.4 and αO = 1042.3 eV. Chemical bonding effects have been discussed with binding energy (BE) differences ΔTi = (BE O 1s - BE Ti 2p3/2) = 71.6 eV and ΔLa = (BE La 3d5/2 - BE O 1s) = 304.7 eV as key parameters in comparison with those in several titanium- and lanthanum-bearing oxides.

Effect of structural evolution on mechanical properties of ZrO2 coated Ti-6Al-7Nb-biomedical application

NASA Astrophysics Data System (ADS)

Zalnezhad, E.

2016-05-01

Zirconia (ZrO2) nanotube arrays were fabricated by anodizing pure zirconium (Zr) coated Ti-6Al-7Nb in fluoride/glycerol electrolyte at a constant potential of 60 V for different times. Zr was deposited atop Ti-6Al-7Nb via a physical vapor deposition magnetron sputtering (PVDMS) technique. Structural investigations of coating were performed utilizing X-ray diffraction (XRD) analysis. Field emission scanning electron microscopy (FESEM) and atomic force microscopy (AFM) were used to characterize the morphology and microstructure of coatings. Unannealed ZrO2 nanotube arrays were amorphous. Monoclinic and tetragonal ZrO2 appeared when the coated substrates were heat treated at 450 °C and 650 °C, while monoclinic ZrO2 was found at 850 °C and 900 °C. Mechanical properties, including nanohardness and modulus of elasticity, were evaluated at different annealing temperatures using a nanoindentation test. The nanoindentation results show that the nanohardness and modulus of elasticity for Ti-6AL-7Nb increased by annealing ZrO2 coated substrate at 450 °C. The nanohardness and modulus of elasticity for coated substrate decreased with annealing temperatures of 650, 850, and 900 °C. At an annealing temperature of 900 °C, cracks in the ZrO2 thin film coating occurred. The highest nanohardness and elastic modulus values of 6.34 and 218 GPa were achieved at an annealing temperature of 450 °C.

Preparation and electrochemical properties of Zr-site substituted Li7La3(Zr2-xMx)O12 (M = Ta, Nb) solid electrolytes

NASA Astrophysics Data System (ADS)

Huang, Mian; Shoji, Mao; Shen, Yang; Nan, Ce-Wen; Munakata, Hirokazu; Kanamura, Kiyoshi

2014-09-01

Li7La3Zr2O12 (LLZ) solid electrolytes with Zr site partially substituted by Ta and Nb elements were prepared via the conventional solid-state reaction. All the compositions could lead to the cubic garnet-type structure after sintering at 1150 °C. The use of γ-Al2O3 as a sintering aid in the preparation of doped LLZ was studied. It was shown that Al could help to improve the micro-structure for Nb doping, but not necessary for Ta doping. The Ta and Nb doping enhanced the ionic conductivity at 25 °C to 4.09 × 10-4 S cm-1 and 4.50 × 10-4 S cm-1, respectively. A conductivity as high as 1.23 × 10-3 S cm-1 was obtained when measured at 50 °C in air for the Nb-doped LLZ. All-solid-state batteries with LLZTa and LLZNb solid electrolytes were assembled and tested. The cyclic voltammetry (CV) measurement indicated the successful working of the batteries.

Transmission electron microscopic study of pyrochlore to defect-fluorite transition in rare-earth pyrohafnates

DOE Office of Scientific and Technical Information (OSTI.GOV)

Karthik, Chinnathambi, E-mail: Karthikchinnathambi@boisestate.edu; Center for Advanced Energy Studies, 995 University Blvd, Idaho Falls, ID 83415; Anderson, Thomas J.

2012-10-15

A structural transition in rare earth pyrohafnates, Ln{sub 2}Hf{sub 2}O{sub 7} (Ln=Y, La, Pr, Nd, Tb, Dy, Yb and Lu), has been identified. Neutron diffraction showed that the structure transforms from well-ordered pyrochloric to fully fluoritic through the lanthanide series from La to Lu with a corresponding increase in the position parameter x of the 48f (Fd3{sup Macron }m) oxygen site from 0.330 to 0.375. As evidenced by the selected area electron diffraction, La{sub 2}Hf{sub 2}O{sub 7}, Pr{sub 2}Hf{sub 2}O{sub 7} and Nd{sub 2}Hf{sub 2}O{sub 7} exhibited a well-ordered pyrocholoric structure with the presence of intense superlattice spots, which becamemore » weak and diffuse (in Dy{sub 2}Hf{sub 2}O{sub 7} and Tb{sub 2}Hf{sub 2}O{sub 7}) before disappearing completely as the series progressed towards the Lu end. High resolution electron microscopic studies showed the breakdown of the pyrochlore ordering in the form of antiphase domains resulting in diffused smoke-like superlattice spots in the case of Dy{sub 2}Hf{sub 2}O{sub 7} and Tb{sub 2}Hf{sub 2}O{sub 7}. - Graphical abstract: Transmission electron microscopic studies showed the ordered pyrochlore to defect fluorite transition in rare-earth pyrohafnates to occur via the formation of anti-phase domains to start with. Highlights: Black-Right-Pointing-Pointer Pyrochlore to fluorite structural transition in rare earth pyrohafnates. Black-Right-Pointing-Pointer La{sub 2}Hf{sub 2}O{sub 7}, Pr{sub 2}Hf{sub 2}O{sub 7} and Nd{sub 2}Hf{sub 2}O{sub 7} showed well ordered pyrochlore structure. Black-Right-Pointing-Pointer Short range ordering in Dy{sub 2}Hf{sub 2}O{sub 7} and Tb{sub 2}Hf{sub 2}O{sub 7}. Black-Right-Pointing-Pointer Break down of pyrochlore ordering due to antiphase boundaries. Black-Right-Pointing-Pointer Rest of the series showed fluoritic structure.« less

Dilute stuffing in the pyrochlore iridate Eu2Ir2O7

NASA Astrophysics Data System (ADS)

Telang, Prachi; Mishra, Kshiti; Sood, A. K.; Singh, Surjeet

2018-06-01

The pyrochlore Eu2Ir2O7 has recently attracted significant attention as a candidate Weyl semimetal. The previous reports on this compound unanimously show a thermally induced metal-to-insulator (MI) transition, concomitant with antiferromagnetic long-range ordering of the Ir moments below TN˜120 K. However, there are contradictory reports concerning the slope d ρ /d T of the resistivity plots (ρ ) in the "metallic" state above the MI transition, and the value of ρ in the insulating state, both of which show significant sample dependence. Here, we explore this issue by investigating six different Eu2Ir2O7 samples with slightly varying Eu:Ir ratio. High-resolution synchrotron powder diffraction is done to probe minor variations in the cell parameters of the various Eu2Ir2O7 samples investigated here. Specific heat (Cp) and magnetic susceptibility of all the samples showed long-range antiferromagnetic ordering upon cooling below TN˜120 K. The transitions are, however, found to be smeared out for the off-stoichiometric samples. We show that the sign of d ρ /d T above the MI transition is highly sensitive to the unit-cell length, which, in turn, depends on the level of Eu stuffing at the Ir site. Samples with composition close to the ideal stoichiometry (Eu:Ir =1 ) showed a change of sign of d ρ /d T from negative to positive upon cooling below a certain temperature T*>TMI . With increasing Eu stuffing, T* decreased until a negative d ρ /d T persisted without any sign change down to TMI.

Epitaxial thin films of pyrochlore iridate Bi 2+xIr 2-yO 7-δ: structure, defects and transport properties

DOE PAGES

Yang, W. C.; Xie, Y. T.; Zhu, W. K.; ...

2017-08-10

While pyrochlore iridate thin films are theoretically predicted to possess a variety of emergent topological properties, experimental verification of these predictions can be obstructed by the challenge in thin film growth. We report on the pulsed laser deposition and characterization of thin films of a representative pyrochlore compound Bi 2Ir 2O 7. Moreover, the films were epitaxially grown on yttria-stabilized zirconia substrates and have lattice constants that are a few percent larger than that of the bulk single crystals. The film composition shows a strong dependence on the oxygen partial pressure. Density-functional-theory calculations indicate the existence of BiIr antisite defects,more » qualitatively consistent with the high Bi: Ir ratio found in the films. Both Ir and Bi have oxidation states that are lower than their nominal values, suggesting the existence of oxygen deficiency. The iridate thin films show a variety of intriguing transport characteristics, including multiple charge carriers, logarithmic dependence of resistance on temperature, antilocalization corrections to conductance due to spin-orbit interactions, and linear positive magnetoresistance.« less

Epitaxial thin films of pyrochlore iridate Bi 2+xIr 2-yO 7-δ: structure, defects and transport properties

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yang, W. C.; Xie, Y. T.; Zhu, W. K.

While pyrochlore iridate thin films are theoretically predicted to possess a variety of emergent topological properties, experimental verification of these predictions can be obstructed by the challenge in thin film growth. We report on the pulsed laser deposition and characterization of thin films of a representative pyrochlore compound Bi 2Ir 2O 7. Moreover, the films were epitaxially grown on yttria-stabilized zirconia substrates and have lattice constants that are a few percent larger than that of the bulk single crystals. The film composition shows a strong dependence on the oxygen partial pressure. Density-functional-theory calculations indicate the existence of BiIr antisite defects,more » qualitatively consistent with the high Bi: Ir ratio found in the films. Both Ir and Bi have oxidation states that are lower than their nominal values, suggesting the existence of oxygen deficiency. The iridate thin films show a variety of intriguing transport characteristics, including multiple charge carriers, logarithmic dependence of resistance on temperature, antilocalization corrections to conductance due to spin-orbit interactions, and linear positive magnetoresistance.« less

Fabrication and characterization of La2Zr2O7 films on different buffer architectures for YBa2Cu3O7-δ coated conductors by RF magnetron sputtering.

PubMed

Xu, Da; Liu, Linfei; Xiao, Guina; Li, Yijie

2013-02-27

La2Zr2O7 (LZO) films were grown on different buffer architectures by radio frequency magnetron sputtering for the large-scale application of YBa2Cu3O7-x (YBCO)-coated conductors. The three different buffer architectures were cerium oxide (CeO2), yttria-stabilized zirconia (YSZ)/CeO2, and CeO2/YSZ/CeO2. The microstructure and surface morphology of the LZO film were studied by X-ray diffraction, optical microscopy, field emission scanning electron microscopy, and atomic force microscopy. The LZO films prepared on the CeO2, YSZ/CeO2, and CeO2/YSZ/CeO2 buffer architectures were preferentially c-axis-oriented and highly textured. The in-plane texture of LZO film on CeO2 single-buffer architecture was ∆ φ = 5.5° and the out-of-plane texture was ∆ ω = 3.4°. All the LZO films had very smooth surfaces, but LZO films grown on YSZ/CeO2 and CeO2/YSZ/CeO2 buffer architectures had cracks. The highly textured LZO film grown on CeO2-seed buffered NiW tape was suitable for the epitaxial growth of YBCO film with high currents.

Effect of Gallium Substitution on Lithium-Ion Conductivity and Phase Evolution in Sputtered Li7-3 xGa xLa3Zr2O12 Thin Films.

PubMed

Rawlence, M; Filippin, A N; Wäckerlin, A; Lin, T-Y; Cuervo-Reyes, E; Remhof, A; Battaglia, C; Rupp, J L M; Buecheler, S

2018-04-25

Replacing the liquid electrolyte in conventional lithium-ion batteries with thin-film solid-state lithium-ion conductors is a promising approach for increasing energy density, lifetime, and safety. In particular, Li 7 La 3 Zr 2 O 12 is appealing due to its high lithium-ion conductivity and wide electrochemical stability window. Further insights into thin-film processing of this material are required for its successful integration into solid-state batteries. In this work, we investigate the phase evolution of Li 7-3 x Ga x La 3 Zr 2 O 12 in thin films with various amounts of Li and Ga for stabilizing the cubic phase. Through this work, we gain valuable insights into the crystallization processes unique to thin films and are able to form dense Li 7-3 x Ga x La 3 Zr 2 O 12 layers stabilized in the cubic phase with high in-plane lithium-ion conductivities of up to 1.6 × 10 -5 S cm -1 at 30 °C. We also note the formation of cubic Li 7 La 3 Zr 2 O 12 at the relatively low temperature of 500 °C.

Stabilization of cubic Li7La3Hf2O12 by Al-doping

NASA Astrophysics Data System (ADS)

Baklanova, Yana V.; Tyutyunnik, Alexander P.; Tarakina, Nadezda V.; Fortes, A. Dominic; Maksimova, Lidiya G.; Korona, Daniil V.; Denisova, Tatyana A.

2018-07-01

In this paper we report on the stabilization of cubic Li7La3Hf2O12 by Al3+ doping and present a detailed crystal structure study and lithium ion conductivity measurements of the obtained compound. Polycrystalline Al-doped Li7La3Hf2O12 was prepared by a modified solid state method. The compound consists of micrometer size grains encapsulated by a glassy phase, which helps preventing the volatilization of lithium during annealing. Al-doped Li7La3Hf2O12 crystallizes in the garnet-related structure with a cubic unit cell (sp. gr. Ia 3 bar d (230)). A structural refinement using X-ray and neutron powder diffraction data showed that the Al3+ ions occupy only tetrahedral Li+ sites in the structure. The presence of overextended leading edges of the peaks on the XRD and NPD data is described by the introduction of an additional phase with rhombohedral distortion that occurs through a stretching of the cubic phase along the body diagonal. The activation energy as well as the total conductivity at room temperature are close to values obtained for un-doped cubic Li7La3Zr2O12 and Li7La3Hf2O12 garnets, which make Al-doped Li7La3Hf2O12 a potential candidate for the application as solid electrolyte in solid-state rechargeable lithium-ion batteries.

Fine Structure in Multi-Phase Zr8Ni21-Zr7Ni10-Zr2Ni7 Alloy Revealed by Transmission Electron Microscope

PubMed Central

Shen, Haoting; Bendersky, Leonid A.; Young, Kwo; Nei, Jean

2015-01-01

The microstructure of an annealed alloy with a Zr8Ni21 composition was studied by both scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The presence of three phases, Zr8Ni21, Zr2Ni7, and Zr7Ni10, was confirmed by SEM/X-ray energy dispersive spectroscopy compositional mapping and TEM electron diffraction. Distribution of the phases and their morphology can be linked to a multi-phase structure formed by a sequence of reactions: (1) L → Zr2Ni7 + L’; (2) peritectic Zr2Ni7 + L’ → Zr2Ni7 + Zr8Ni21 + L”; (3) eutectic L” → Zr8Ni21 + Zr7Ni10. The effect of annealing at 960 °C, which was intended to convert a cast structure into a single-phase Zr8Ni21 structure, was only moderate and the resulting alloy was still multi-phased. TEM and crystallographic analysis of the Zr2Ni7 phase show a high density of planar (001) defects that were explained as low-energy boundaries between rotational variants and stacking faults. The crystallographic features arise from the pseudo-hexagonal structure of Zr2Ni7. This highly defective Zr2Ni7 phase was identified as the source of the broad X-ray diffraction peaks at around 38.4° and 44.6° when a Cu-K was used as the radiation source. PMID:28793460

Mn 4+ emission in pyrochlore oxides

DOE PAGES

Du, Mao-Hua

2014-08-27

For the existing Mn 4+ activated red phosphors have relatively low emission energies (or long emission wavelengths) and are therefore inefficient for general lighting. Density functional calculations are performed to study Mn 4+ emission in rare-earth hafnate, zirconate, and stannate pyrochlore oxides (RE 2Hf 2O 7, RE 2Zr 2O 7, and RE 2Sn 2O 7). We show how the different sizes of the RE 3+ cation in these pyrochlores affect the local structure of the distorted MnO 6 octahedron, the Mn–O hybridization, and the Mn 4+ emission energy. The Mn 4+ emission energies of many pyrochlores are found to bemore » higher than those currently known for Mn 4+ doped oxides and should be closer to that of Y 2O 3:Eu 3+ (the current commercial red phosphor for fluorescent lighting). The O–Mn–O bond angle distortion in a MnO6 octahedron is shown to play an important role in weakening Mn–O hybridization and consequently increasing the Mn 4+ emission energy. Our result shows that searching for materials that allow significant O–Mn–O bond angle distortion in a MnO 6 octahedron is an effective approach to find new Mn 4+ activated red phosphors with potential to replace the relatively expensive Y 2O 3:Eu 3+ phosphor.« less

The pressure-induced structural response of rare earth hafnate and stannate pyrochlore from 0.1-50 GPa

NASA Astrophysics Data System (ADS)

Turner, K. M.; Rittman, D.; Heymach, R.; Turner, M.; Tracy, C.; Mao, W. L.; Ewing, R. C.

2017-12-01

Complex oxides with the pyrochlore (A2B2O7) and defect-fluorite ((A,B)4O7) structure-types undergo structural transformations under high-pressure. These compounds are under consideration for applications including as a proposed waste-form for actinides generated in the nuclear fuel cycle. High-pressure transformations in rare earth hafnates (A2Hf2O7, A=Sm, Eu, Gd, Dy, Y, Yb) and stannates (A2Sn2O7, A=Nd, Gd, Er) were investigated to 50 GPa by in situ Raman spectroscopy and synchrotron x-ray diffraction (XRD). Rare-earth hafnates form the pyrochlore structure for A=La-Tb and the defect-fluorite structure for A=Dy-Lu. Lanthanide stannates form the pyrochlore structure. Raman spectra revealed that at ambient pressure all compositions have pyrochlore-type short-range order. Stannate compositions show a larger degree of pyrochlore-type short-range ordering relative to hafnates. In situ high-pressure synchrotron XRD showed that rare earth hafnates and stannates underwent a pressure-induced phase transition to a cotunnite-like (Pnma) structure that begins between 18-25 GPa in hafnates and between 30-33 GPa in stannates. The phase transition is not complete at 50 GPa, and upon decompression, XRD indicates that all compositions transform to defect-fluorite with an amorphous component. In situ Raman spectroscopy showed that disordering in stannates and hafnates occurs gradually upon compression. Pyrochlore-structured hafnates retain short-range order to a higher pressure (30 GPa vs. <10 GPa) than defect-fluorite-structured hafnates. Hafnates and stannates decompressed from 50 GPa show Raman spectra consistent with weberite-type structures, also reported in irradiated stannates. The second-order Birch-Murnaghan equation of state fit gives a bulk modulus of 250 GPa for hafnate compositions with the pyrochlore structure, and 400 GPa for hafnate compositions with the defect-fluorite structure. Stannates have a lower bulk modulus relative to hafnates (between 80-150 GPa

Optical and structural characterization of Ge clusters embedded in ZrO2

NASA Astrophysics Data System (ADS)

Agocs, E.; Zolnai, Z.; Rossall, A. K.; van den Berg, J. A.; Fodor, B.; Lehninger, D.; Khomenkova, L.; Ponomaryov, S.; Gudymenko, O.; Yukhymchuk, V.; Kalas, B.; Heitmann, J.; Petrik, P.

2017-11-01

The change of optical and structural properties of Ge nanoclusters in ZrO2 matrix have been investigated by spectroscopic ellipsometry versus annealing temperatures. Radio-frequency top-down magnetron sputtering approach was used to produce the samples of different types, i.e. single-layers of pure Ge, pure ZrO2 and Ge-rich-ZrO2 as well as multi-layers stacked of 40 periods of 5-nm-Ge-rich-ZrO2 layers alternated by 5-nm-ZrO2 ones. Germanium nanoclusters in ZrO2 host were formed by rapid-thermal annealing at 600-800 °C during 30 s in nitrogen atmosphere. Reference optical properties for pure ZrO2 and pure Ge have been extracted using single-layer samples. As-deposited multi-layer structures can be perfectly modeled using the effective medium theory. However, annealed multi-layers demonstrated a significant diffusion of elements that was confirmed by medium energy ion scattering measurements. This fact prevents fitting of such annealed structure either by homogeneous or by periodic multi-layer models.

Ferroelectric performances and crystal structures of (Pb, La)(Zr, Ti, Nb)O{sub 3}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kitamura, Naoto; Division of Ecosystem Research, Research Institute for Science and Technology, Tokyo University of Science, 2641 Yamazaki, Noda, Chiba 278-8510; Mizoguchi, Takuma

2014-02-15

In this study, we focused on Nb and La substituted Pb(Zr, Ti)O{sub 3}: i.e., (Pb, La)(Zr, Ti, Nb)O{sub 3}. As for the samples, dependences of ferroelectric properties on La and Nb compositions were examined. In addition, the crystal structures were analyzed by the Rietveld method, and then a relationship between the metal compositions and the crystal structures were discussed. From P–E hysteresis loop measurements, it was found that the remanant polarization of Pb(Zr, Ti)O{sub 3} was increased by both the La and Nb substitutions although the heavy substitution of La had an undesirable effect. It was also indicated that themore » Curie temperature decreased with increasing La content. The Rietveld analysis using synchrotron X-ray diffraction patterns demonstrated that the structure distortion was relaxed by the La and Nb substitutions. Such a change in the crystals was well consistent with the harmful effects on the Curie temperature and the remanent polarization by the heavy La substitution. - Graphical abstract: Rietveld refinement pattern of 2 mol% PbSiO{sub 3}-added Pb{sub 0.95}La{sub 0.05}Zr{sub 0.50}Ti{sub 0.45}Nb{sub 0.05}O{sub 3} (synchrotron X-ray diffraction). Display Omitted - Highlights: • (Pb,La)(Zr,Ti,Nb)O{sub 3} were successfully synthesized. • Remanant polarization of Pb(Zr,Ti)O{sub 3} was improved by substitutions of La and Nb. • Crystal structures of (Pb,La)(Zr,Ti,Nb)O{sub 3} were refined and the distortions were estimated.« less

New dielectric ceramics Pb(Cd)BiM/sup IV/SbO/sub 7/ (M/sup IV/ = Ti, Zr, Sn) with the pyrochlore structure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lambachri, A.; Monier, M.; Mercurio, J.P.

1988-04-01

Dielectric ceramics have been obtained by natural sintering of pyrochlore phases with general formula Pb(Cd)BiM/sup IV/SbO/sub 7/ (M/sup IV/ = Ti, Zr, Sn). Low frequency dielectric characteristics have been studied with respect to the processing conditions: sintering without additive and in the presence of some low melting compounds (PbO, Pb/sub 5/Ge/sub 3/O/sub 11/, Bi/sub 12/PbO/sub 19/ and Bi/sub 12/CdO/sub 19/). The dielectric constants of these ceramics lie between 30 and 60, the dielectric losses range from 10 to 30.10/sup -4/ and the temperature coefficient of the dielectric constants (20 - 100/sup 0/C) can be tailored by means of additives inmore » the +- 30 ppm K/sup -1/ range.« less

Synthesis of Zr2WP2O12/ZrO2 Composites with Adjustable Thermal Expansion.

PubMed

Zhang, Zhiping; Sun, Weikang; Liu, Hongfei; Xie, Guanhua; Chen, Xiaobing; Zeng, Xianghua

2017-01-01

Zr 2 WP 2 O 12 /ZrO 2 composites were fabricated by solid state reaction with the goal of tailoring the thermal expansion coefficient. XRD, SEM and TMA were used to investigate the composition, microstructure, and thermal expansion behavior of Zr 2 WP 2 O 12 /ZrO 2 composites with different mass ratio. Relative densities of all the resulting Zr 2 WP 2 O 12 /ZrO 2 samples were also tested by Archimedes' methods. The obtained Zr 2 WP 2 O 12 /ZrO 2 composites were comprised of orthorhombic Zr 2 WP 2 O 12 and monoclinic ZrO 2 . As the increase of the Zr 2 WP 2 O 12 , the relative densities of Zr 2 WP 2 O 12 /ZrO 2 ceramic composites increased gradually. The coefficient of thermal expansion of the Zr 2 WP 2 O 12 /ZrO 2 composites can be tailored from 4.1 × 10 -6 K -1 to -3.3 × 10 -6 K -1 by changing the content of Zr 2 WP 2 O 12 . The 2:1 Zr 2 WP 2 O 12 /ZrO 2 specimen shows close to zero thermal expansion from 25 to 700°C with an average linear thermal expansion coefficient of -0.09 × 10 -6 K -1 . These adjustable and near zero expansion ceramic composites will have great potential application in many fields.

Synthesis of nanocrystalline Gd2Ti2O7 by combustion process and its structural, optical and dielectric properties

NASA Astrophysics Data System (ADS)

Jeyasingh, T.; Saji, S. K.; Wariar, P. R. S.

2017-07-01

Nanosized pyrochlore material Gadolinium Titanate (Gd2Ti2O7) powder was prepared by modified single step auto-ignition combustion process. The phase formation has been investigated using X-Ray diffraction analysis (XRD). The crystalline pyrochlore phase is further confirmed by the presence of metal-oxygen bonds in the FT-IR spectra. XRD analysis revealed that Gd2Ti2O7 has a cubic structure with Fd3m space group. The combustion powder was sintered to high density (97% of theoretical density) at ˜13000 C for 4h and the surface morphology was examined by Scanning Electron Microscopy (SEM). The optical band gap of Gd2Ti2O7 determined from the absorption spectrum is found to be 4.2 eV, which corresponds to direct allowed transitions. The dielectric measurements were carried out using LCR meter in the radio frequency region at room temperature. The sintered Gd2Ti2O7 has a dielectric constant (Ɛr) = 40 and dielectric loss (tan δ) = 0.01 at 1MHz.

Temperature-dependent local structural properties of redox Pt nanoparticles on TiO 2 and ZrO 2 supports

DOE PAGES

Jeong, Eun -Suk; Park, Chang -In; Jin, Zhenlan; ...

2015-01-21

This paper examined the local structural properties of Pt nanoparticles on SiO 2, TiO 2–SiO 2, and ZrO 2–SiO 2 supports to better understand the impact of oxide-support type on the performance of Pt-based catalysts. In situ X-ray absorption fine structure (XAFS) measurements were taken for the Pt L3-edge in a temperature range from 300 to 700 K in He, H 2, and O 2 gas environments. The XAFS measurements demonstrated that Pt atoms were highly dispersed on TiO 2–SiO 2 and ZrO 2–SiO 2 forming pancake-shaped nanoparticles, whereas Pt atoms formed larger particles of hemispherical shapes on SiO 2more » supports. Contrary to the SiO 2 case, the coordination numbers for Pt, Ti, and Zr around Pt atoms on the TiO 2–SiO 2 and ZrO 2–SiO 2 supports were nearly constant from 300 to 700 K under the different gas environments. These results are consistent with the improvements in thermal stability of Pt nanoparticles achieved by incorporating TiO 2 or ZrO 2 on the surface of SiO 2 supports. XAFS analysis further indicated that the enhanced dispersion and stability of Pt were a consequence of the strong metal support interaction via Pt–Ti and Pt–Zr bonds.« less

Investigation of the Structural Stability of Ion-Implanted Gd 2Ti 2-xSn xO 7 Pyrochlore-Type Oxides by Glancing Angle X-ray Absorption Spectroscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aluri, Esther Rani; Hayes, John R.; Walker, James D.S.

2016-03-24

Rare-earth titanate and stannate pyrochlore-type oxides have been investigated in the past for the sequestration of nuclear waste elements because of their resistance to radiation-induced structural damage. In order to enhance this property, it is necessary to understand the effect of radioactive decay of the incorporated actinide elements on the local chemical environment. In this study, Gd 2Ti 2–xSn xO 7 materials have been implanted with Au– ions to simulate radiation-induced structural damage. Glancing angle X-ray absorption near-edge spectroscopy (GA-XANES), glancing angle X-ray absorption fine structure (GA-EXAFS) analysis, and powder X-ray diffraction have been used to investigate changes in themore » local coordination environment of the metal atoms in the damaged surface layer. Examination of GA-XANES/EXAFS spectra from the implanted Gd 2Ti 2–xSn xO 7 materials collected at various glancing angles allowed for an investigation of how the local coordination environment around the absorbing atoms changed at different depths in the damaged surface layer. This study has shown the usefulness of GA-XANES to the examination of ion-implanted materials and has suggested that Gd 2Ti 2–xSn xO 7 becomes more susceptible to ion-beam-induced structural damage with increasing Sn concentration.« less

Supercooled spin liquid state in the frustrated pyrochlore Dy 2Ti 2O 7

DOE PAGES

Kassner, Ethan R.; Eyvazov, Azar B.; Pichler, Benjamin; ...

2015-06-30

A “supercooled” liquid develops when a fluid does not crystallize upon cooling below its ordering temperature. Instead, the microscopic relaxation times diverge so rapidly that, upon further cooling, equilibration eventually becomes impossible and glass formation occurs. Classic supercooled liquids exhibit specific identifiers including microscopic relaxation times diverging on a Vogel–Tammann–Fulcher (VTF) trajectory, a Havriliak–Negami (HN) form for the dielectric function ε(ω,T), and a general Kohlrausch–Williams–Watts (KWW) form for time-domain relaxation. Recently, the pyrochlore Dy 2Ti 2O 7 has become of interest because its frustrated magnetic interactions may, in theory, lead to highly exotic magnetic fluids. However, its true magnetic statemore » at low temperatures has proven very difficult to identify unambiguously. Here, we introduce high-precision, boundary-free magnetization transport techniques based upon toroidal geometries and gain an improved understanding of the time- and frequency-dependent magnetization dynamics of Dy 2Ti 2O 7. We demonstrate a virtually universal HN form for the magnetic susceptibility χ(ω,T), a general KWW form for the real-time magnetic relaxation, and a divergence of the microscopic magnetic relaxation rates with the VTF trajectory. Low-temperature Dy 2Ti 2O 7 therefore exhibits the characteristics of a supercooled magnetic liquid. Lastly, one implication is that this translationally invariant lattice of strongly correlated spins may be evolving toward an unprecedented magnetic glass state, perhaps due to many-body localization of spin.« less

The affects of doping Eu 3+ on structures and morphology of ZrO 2 nanocrystals

NASA Astrophysics Data System (ADS)

Yu, Lixin; Liu, Hai; Nogami, Masayuki

2010-07-01

The ZrO 2 and ZrO 2:Eu 3+ nanocrystals (NCs) were prepared by a hydrothermal method. The samples were sintered at different temperatures (500, 800 and 1100 °C). The results indicate that the Eu 3+ ions affect not only the structures of hosts (ZrO 2), but also the morphology of hosts. The shape of ZrO 2:Eu 3+ NCs heated at 1100 °C is the one-dimensional nanorod, while is the zero-dimensional nanoparticle for pure ZrO 2 samples sintered at the same temperature. The excitation and emission spectra of ZrO 2:Eu 3+ NCs were studied. In excitation spectra, the charge transfer band of Eu 3+ in ZrO 2 NCs heated at 1100 °C evidently blue-shifts in comparison with the NCs calcined at 500 and 800 °C. The relative intensity of 5D-7F transitions of Eu 3+ ions and color chromaticity for nanorods are increased in comparison with the nanoparticles.

Modifying the Surface of γ-Al2 O3 with Y2 Sn2 O7 Pyrochlore: Monolayer Dispersion Behaviour of Composite Oxides.

PubMed

Xu, Xianglan; Liu, Fang; Tian, Jinshu; Peng, Honggen; Liu, Wenming; Fang, Xiuzhong; Zhang, Ning; Wang, Xiang

2017-06-20

To investigate the dispersion behaviour of composite oxides on supports, and to obtain better supports for Pd for CO oxidation, a series of Y 2 Sn 2 O 7 /Al 2 O 3 composite oxides with different Y 2 Sn 2 O 7 loadings were prepared by a deposition-precipitation method. XRD and X-ray photoelectron spectroscopic extrapolation methods revealed that, similar to single-component metal oxides, composite oxides can also disperse spontaneously on support surfaces to form a monolayer with a certain capacity. The monolayer dispersion capacity/threshold for Y 2 Sn 2 O 7 on the surface of γ-Al 2 O 3 is 0.109 mmol per 100 m 2 γ-Al 2 O 3 , corresponding to 7.2 wt % Y 2 Sn 2 O 7 loading. This is the first work to demonstrate monolayer dispersion of a composite oxide on a support. After combining Y 2 Sn 2 O 7 with γ-Al 2 O 3 , active oxygen species can be introduced onto the catalyst surfaces. Thus, the interaction between Pd and the support is strengthened, the dispersion of Pd is improved in comparison with the single-component Y 2 Sn 2 O 7 support, and a synergistic effect is induced between Pd and the composite support, which is beneficial to catalyst activity. By tuning the γ-Al 2 O 3 surface with different amounts of pyrochlore Y 2 Sn 2 O 7 , CO oxidation activity on 1 % Pd/Y 2 Sn 2 O 7 /Al 2 O 3 was improved. These findings may provide new insights into the design and preparation of effective supported noble metal catalysts with lower contents of noble metals. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Possible observation of highly itinerant quantum magnetic monopoles in the frustrated pyrochlore Yb2Ti2O7

PubMed Central

Tokiwa, Y.; Yamashita, T.; Udagawa, M.; Kittaka, S.; Sakakibara, T; Terazawa, D.; Shimoyama, Y.; Terashima, T.; Yasui, Y.; Shibauchi, T.; Matsuda, Y.

2016-01-01

The low-energy elementary excitations in frustrated quantum magnets have fascinated researchers for decades. In frustrated Ising magnets on a pyrochlore lattice possessing macroscopically degenerate spin-ice ground states, the excitations have been discussed in terms of classical magnetic monopoles, which do not contain quantum fluctuations. Here we report unusual behaviours of magneto-thermal conductivity in the disordered spin-liquid regime of pyrochlore Yb2Ti2O7, which hosts frustrated spin-ice correlations with large quantum fluctuations owing to pseudospin-1/2 of Yb ions. The analysis of the temperature and magnetic field dependencies shows the presence of gapped elementary excitations. We find that the gap energy is largely suppressed from that expected in classical monopoles. Moreover, these excitations propagate a long distance without being scattered, in contrast to the diffusive nature of classical monopoles. These results suggests the emergence of highly itinerant quantum magnetic monopole, which is a heavy quasiparticle that propagates coherently in three-dimensional spin liquids. PMID:26912080

Possible observation of highly itinerant quantum magnetic monopoles in the frustrated pyrochlore Yb2Ti2O7.

PubMed

Tokiwa, Y; Yamashita, T; Udagawa, M; Kittaka, S; Sakakibara, T; Terazawa, D; Shimoyama, Y; Terashima, T; Yasui, Y; Shibauchi, T; Matsuda, Y

2016-02-25

The low-energy elementary excitations in frustrated quantum magnets have fascinated researchers for decades. In frustrated Ising magnets on a pyrochlore lattice possessing macroscopically degenerate spin-ice ground states, the excitations have been discussed in terms of classical magnetic monopoles, which do not contain quantum fluctuations. Here we report unusual behaviours of magneto-thermal conductivity in the disordered spin-liquid regime of pyrochlore Yb2Ti2O7, which hosts frustrated spin-ice correlations with large quantum fluctuations owing to pseudospin-1/2 of Yb ions. The analysis of the temperature and magnetic field dependencies shows the presence of gapped elementary excitations. We find that the gap energy is largely suppressed from that expected in classical monopoles. Moreover, these excitations propagate a long distance without being scattered, in contrast to the diffusive nature of classical monopoles. These results suggests the emergence of highly itinerant quantum magnetic monopole, which is a heavy quasiparticle that propagates coherently in three-dimensional spin liquids.

Crystal structure, stoichiometry, and dielectric relaxation in Bi 3.32Nb 7.09O 22.7 and structurally related ternary phases

NASA Astrophysics Data System (ADS)

Grey, I. E.; Vanderah, T. A.; Mumme, W. G.; Roth, R. S.; Guzman, J.; Nino, J. C.; Levin, I.

2008-03-01

The crystal structure of the phase previously reported to occur at 4:9 Bi 2O 3:Nb 2O 5 has been determined using single-crystal X-ray and powder neutron diffraction ( P6 3/ mmc; a=7.4363(1) Å, c=19.7587(5) Å; Z=2). The structural study combined with phase equilibrium analyses indicate that the actual composition is Bi 3.32Nb 7.09O 22.7. This binary compound is the end-member of a family of four phases which form along a line between it and the pyrochlore phase field in the Bi 2O 3:Fe 2O 3:Nb 2O 5 system. The structures are derived from the parent pyrochlore end-member by chemical twinning, and can also be described as unit-cell intergrowths of the pyrochlore and hexagonal tungsten bronze (HTB) structures. The dielectric properties of the three chemically twinned pyrochlore phases, Bi 3.32Nb 7.09O 22.7, Bi 9.3Fe 1.1Nb 16.9O 57.8 and Bi 5.67FeNb 10O 35, were characterized. All exhibit low-temperature, broad dielectric relaxation similar to that of the Bi-Fe-Nb-O pyrochlore. At 1 MHz and ≈175 K the observed relative permittivites were 345, 240, and 205, respectively, compared to 125 for the Bi-Fe-Nb-O pyrochlore. The higher relative permittivities observed for the chemically twinned pyrochlore derivatives are ascribed to the presence of HTB blocks in their structures: The Bi atoms located in the HTB blocks feature highly asymmetric coordination environments compared to pyrochlore, and the magnitude of the relative permittivity increases with the proportion of Bi located within the HTB portions of the structures.

Study the structural and optical behaviour of polyaniline/ZrO2 nanocomposites

NASA Astrophysics Data System (ADS)

Sidhu, Gaganpreet Kaur; Kumar, Naresh; Kumar, Rajesh

2018-05-01

In nanoscience, hybrid material based on polymer and nanoparticles are of great interest because of much improved properties of components. Polymers are of enormous interest because of their various properties like flexibility, low weight and easy processing. Here, we studied the influence of ZrO2 nanoparticles on the structural and optical properties of Polyaniline (PANI). ZrO2 mixed with PANI, improve its structural and optical properties. XRD studies reveal that ZrO2 nanoparticles exist in the tetragonal phase in ZrO2/PANI nanocomposites. UV-Vis spectroscopic studies have been carried out to understand the presence of various energy levels and their involvement in absorbance of light. In PANI nanocomposites, aniline monomer attach with ZrO2 nanoparticles through p-p stacking interaction, Vander waal force and hydrogen bonding interaction.

Electronic structure and electron energy-loss spectroscopy of ZrO2 zirconia

NASA Astrophysics Data System (ADS)

Dash, L. K.; Vast, Nathalie; Baranek, Philippe; Cheynet, Marie-Claude; Reining, Lucia

2004-12-01

The atomic and electronic structures of zirconia are calculated within density functional theory, and their evolution is analyzed as the crystal-field symmetry changes from tetrahedral [cubic (c-ZrO2) and tetragonal (t-ZrO2) phases] to octahedral (hypothetical rutile ZrO2 ), to a mixing of these symmetries (monoclinic phase, m-ZrO2 ). We find that the theoretical bulk modulus in c-ZrO2 is 30% larger than the experimental value, showing that the introduction of yttria in zirconia has a significant effect. Electronic structure fingerprints which characterize each phase from their electronic spectra are identified. We have carried out electron energy-loss spectroscopy experiments at low momentum transfer and compared these results to the theoretical spectra calculated within the random phase approximation. We show a dependence of the valence and 4p ( N2,3 edge) plasmons on the crystal structure, the dependence of the latter being brought into the spectra by local-field effects. Last, we attribute low energy excitations observed in EELS of m-ZrO2 to defect states 2eV above the top of the intrinsic valence band, and the EELS fundamental band gap value is reconciled with the 5.2 or 5.8eV gaps determined by vacuum ultraviolet spectroscopy.

Doped ZrO2 for future lead free piezoelectric devices

NASA Astrophysics Data System (ADS)

Starschich, S.; Böttger, U.

2018-01-01

The ferroelectric and piezoelectric properties of doped ZrO2 prepared by chemical solution deposition (CSD) are investigated. Doping with different elements such as Mg, In, La, and Y leads to a stabilization of the constricted hysteresis. As shown in a previous work, for the constricted hysteresis of ZrO2, the piezoelectric response is significantly larger compared to ZrO2 with a normal hysteresis. The Mg doped ZrO2 shows a strong temperature and cycle stability. For the piezoelectric properties, a magnesium concentration of 7% shows the largest piezoelectric response with a piezoelectric coefficient of >10 pm/V, as well as the best cycle stability. Due to thicker films, which can be realized by the CSD technique, the shown doped ZrO2 films are a promising candidate for energy related applications such as piezoelectric energy harvesting as well as for microelectromechanical systems.

Characterization of ZrO2 and (ZrO2)x(Al2O3)1-X thin films on Si substrates: effect of the Al2O3 component

NASA Astrophysics Data System (ADS)

Vitanov, P.; Harizanova, A.; Ivanova, T.

2014-05-01

ZrO2 and (ZrO2)x(Al2O3)1-x films were deposited by the sol-gel technique on Si substrates. The effect of the Al2O3 additive on the film surface morphology was studied by atomic force microscopy (AFM). The mixed oxide films showed a smoother morphology and lower values of the root-mean-square (RMS) roughness compared to ZrO2. Further, FTIR spectra indicated that ZrO2 underwent crystallization. The electrical measurements of the MIS structure revealed that the presence of Al2O3 and the amorphization affects its dielectric properties. The MIS structure with (ZrO2)x(Al2O3)1-x showed a lower fixed charge (~ 6×1010 cm-2) and an interface state density in the middle of the band gap of 6×1011 eV-1 cm-2). The dielectric constant measured was 22, with the leakage current density decreasing to 2×10-8 A cm-2 at 1×106 V cm-1.

The glass-like thermal conductivity in ZrO2-Dy3TaO7 ceramic for promising thermal barrier coating application

NASA Astrophysics Data System (ADS)

Wu, Peng; Hu, Ming Yu; Chong, Xiao Yu; Feng, Jing

2018-03-01

Using the solid-state reaction method, the (ZrO2)x-(Dy3TaO7)1-x (x = 0, 0.02, 0.04, 0.06, 0.08, and 0.1) ceramics are synthesized in this work. The identification of the crystal structures indicates that the (ZrO2)x-(Dy3TaO7)1-x ceramics belong to the orthorhombic system, and the space group is C2221 in spite of the value of x increasing to 0.1. The thermal conductivities of the (ZrO2)x-(Dy3TaO7)1-x ceramics range from 1.3 W/(m K) to 1.8 W/(m K), and this value is much lower than that of 7-8 YSZ (yttria-stabilized zirconia). Besides, the (ZrO2)x-(Dy3TaO7)1-x ceramics possess the glass-like thermal conductivity caused by intrinsic oxygen vacancies existing in the lattice of Dy3TaO7. Moreover, the results of thermal expansion rates demonstrate that the (ZrO2)x-(Dy3TaO7)1-x ceramics possess excellent high temperature phase stability, and the thermal expansion coefficients [(9.7-11) × 10-6 K-1] are comparable to that of 7-8 YSZ.

Popcorn balls-like ZnFe2O4-ZrO2 microsphere for photocatalytic degradation of 2,4-dinitrophenol

NASA Astrophysics Data System (ADS)

Chen, Xi; Liu, Yutang; Xia, Xinnian; Wang, Longlu

2017-06-01

In this paper, novel popcorn balls-like ZnFe2O4-ZrO2 composite microspheres were successfully fabricated by a simple hydrothermal method. The morphology, structure and optical property of the microspheres were characterized. The microspheres were used as the photocatalysts to degrade 2,4-dinitrophenol, and exhibited superior photocatalytic performance. Under simulated solar visible light irradiation, the degradation rate of ZnFe2O4-ZrO2 photocatalyst (mass ratio of ZnFe2O4/ZrO2 = 2:1) was almost 7.4 and 2.4 times higher than those of pure ZnFe2O4 and ZrO2. The enhancement could attribute to stronger light absorption, lower carrier recombination and multi-porous structure of the microspheres. Moreover, the popcorn balls-like photocatalysts can be easily separated, because of the magnetism of the samples. After five times runs, the photocatalyst still showed 90% of its photocatalytic degradation efficiency. This work demonstrated a good prospect for removing organic pollutants in water.

Growth of self-textured Ga3+-substituted Li7La3Zr2O12 ceramics by solid state reaction and their significant enhancement in ionic conductivity

NASA Astrophysics Data System (ADS)

Qin, Shiying; Zhu, Xiaohong; Jiang, Yue; Ling, Ming'en; Hu, Zhiwei; Zhu, Jiliang

2018-03-01

A highly self-textured Ga2O3-substituted Li7La3Zr2O12 (LLZO-Ga) solid electrolyte with a nominal composition of Li6.55Ga0.15La3Zr2O12 is obtained by a simple and low-cost solid-state reaction technique, requiring no seed crystals to achieve grain orientation. The as-prepared self-textured LLZO-Ga shows a strong (420) preferred orientation with a high Lotgering factor of 0.91. Coherently, a terrace-shaped microstructure consisting of many parallel layers, indicating a two-dimensional-like growth mode, is clearly observed in the self-textured sample. As a result, the highly self-textured garnet-type lithium-ion conducting solid electrolyte of LLZO-Ga exhibits an extremely high ionic conductivity, reaching a state-of-the-art level of 2.06 × 10-3 S cm-1 at room temperature (25 °C) and thus shedding light on an important strategy for improving the structure and ionic conductivity of solid electrolytes.

Fast ion conductivity in strained defect-fluorite structure created by ion tracks in Gd 2Ti 2O 7

DOE PAGES

Aidhy, Dilpuneet S.; Sachan, Ritesh; Zarkadoula, Eva; ...

2015-11-10

In this research, the structure and ion-conducting properties of the defect-fluorite ring structure formed around amorphous ion-tracks by swift heavy ion irradiation of Gd 2Ti 2O 7 pyrochlore are investigated. High angle annular dark field imaging complemented with ion-track molecular dynamics simulations show that the atoms in the ring structure are disordered, and have relatively larger cation-cation interspacing than in the bulk pyrochlore, illustrating the presence of tensile strain in the ring region. Density functional theory calculations show that the non-equilibrium defect-fluorite structure can be stabilized by tensile strain. The pyrochlore to defect-fluorite structure transformation in the ring region ismore » predicted to be induced by recrystallization during a melt-quench process and stabilized by tensile strain. Static pair-potential calculations show that planar tensile strain lowers oxygen vacancy migration barriers in pyrochlores, in agreement with recent studies on fluorite and perovskite materials. From these results, it is suggested that strain engineering could be simultaneously used to stabilize the defect-fluorite structure and gain control over its high ion-conducting properties.« less

Multiferroic magnetoelectric coupling effect of bilayer La1.2Sr1.8Mn2O7/PbZr0.3Ti0.7O3 complex thin film

NASA Astrophysics Data System (ADS)

Liang, K.; Zhou, P.; Ma, Z. J.; Qi, Y. J.; Mei, Z. H.; Zhang, T. J.

2017-05-01

Magnetoelectric (ME) coupling effect of 2-2-type ferromagnetic/ferroelectric bi-layer multiferroic epitaxial thin film (La1.2Sr1.8Mn2O7/PbZr0.3Ti0.7O3, LSMO/PZT) on SrRuO3 (SRO) substrate is investigated systematically by using Landau-Ginzburg-Devonshire (LGD) thermodynamic theory and modified constitutive equations. The calculating results clarify the detail relationships between ME coupling response and the residual strain, the volume fraction of constituent phases, the interface coupling coefficients, the magnetic field and the temperature. It also shows that improved ME coupling response can be modulated by these parameters. External magnetic fields (H1) induced ME coupling effect could be enhanced around Curie Temperature (Tc) of ferromagnetic phase and ME voltage coefficient (αE31) approaches a maximum at H1 ∼ 4.5 kOe near Tc. The remarkable variations of ME coupling response can be used to provide useful guidelines on the design of multifunctional devices.

Preparation of Zr(Mo,W)2O8 with a larger negative thermal expansion by controlling the thermal decomposition of Zr(Mo,W)2(OH,Cl)2∙2H2O.

PubMed

Petrushina, Mariya Yu; Dedova, Elena S; Filatov, Eugeny Yu; Plyusnin, Pavel E; Korenev, Sergei V; Kulkov, Sergei N; Derevyannikova, Elizaveta A; Sharafutdinov, Marat R; Gubanov, Alexander I

2018-03-28

Solid solutions of Zr(Mo,W) 2 O 7 (OH,Cl) 2 ∙2H 2 O with a preset ratio of components were prepared by a hydrothermal method. The chemical composition of the solutions was determined by energy dispersive X-ray spectroscopy (EDX). For all the samples of ZrMo x W 2-x O 7 (OH,Cl) 2 ∙2H 2 O (x = 0.0, 0.2, 0.4, 0.6, 0.8, 1.0, 1.2, 1.4, 1.6, 1.8, and 2.0), TGA and in situ powder X-ray diffraction (PXRD) studies (300-1100 K) were conducted. For each case, the boundaries of the transformations were determined: Zr(Mo,W) 2 O 7 (OH,Cl) 2 ∙2H 2 O → orthorhombic-ZrMo x W 2-x O 8 (425-525 K), orthorhombic-ZrMo x W 2-x O 8  → cubic-ZrMo x W 2-x O 8 (700-850 K), cubic-ZrMo x W 2-x O 8  → trigonal-ZrMo x W 2-x O 8 (800-1050 K for x > 1) and cubic-ZrMo x W 2-x O 8  → oxides (1000-1075 K for x ≤ 1). The cell parameters of the disordered cubic-ZrMo x W 2-x O 8 (space group Pa-3) were measured within 300-900 K, and the thermal expansion coefficients were calculated: -3.5∙10 -6  - -4.5∙10 -6  K -1 . For the ordered ZrMo 1.8 W 0.2 O 8 (space group P2 1 3), a negative thermal expansion (NTE) coefficient -9.6∙10 -6  K -1 (300-400 K) was calculated. Orthorhombic-ZrW2O 8 is formed upon the decomposition of ZrW 2 O 7 (OH,Cl) 2 ∙2H 2 O within 500-800 K.

Hydrodeoxygenation of p -Cresol over Pt/Al 2 O 3 Catalyst Promoted by ZrO 2 , CeO 2 , and CeO 2 –ZrO 2

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Weiyan; Wu, Kui; Liu, Pengli

2016-07-20

ZrO 2-Al 2O 3 and CeO 2-Al 2O 3 were prepared by a co-precipitation method and selected as supports for Pt catalysts. The effects of CeO 2 and ZrO 2 on the surface area and Brønsted acidity of Pt/Al 2O 3 were studied. In the hydrodeoxygenation (HDO) of p-cresol, the addition of ZrO 2 promoted the direct deoxygenation activity on Pt/ZrOO 2-Al 2O 3 via Caromatic-O bond scission without benzene ring saturation. Pt/CeOO 2-Al 2O 3 exhibited higher deoxygenation extent than Pt/Al 2O 3 due to the fact that Brønsted acid sites on the catalyst surface favored the adsorption ofmore » p-cresol. With the advantages of CeO 2 and ZrO 2 taken into consideration, CeO 2-ZrOO 2-Al 2O 3 was prepared, leading to the highest HDO activity of Pt/CeO 2-ZrOO 2-Al 2O 3. The deoxygenation extent for Pt/CeO 2-ZrOO 2-Al 2O 3 was 48.4% and 14.5% higher than that for Pt/ZrO2O 2-Al 2O 3 and Pt/CeOO 2-Al 2O 3, respectively.« less

Oriented and ordered mesoporous ZrO{sub 2}/TiO{sub 2} fibers with well-organized linear and spring structure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhu, Luyi, E-mail: zhuly@sdu.edu.cn; Liu, Benxue; Qin, Weiwei, E-mail: jiuyuan.1001@163.com

Graphical abstract: The ultra-stable order mesoporous ZrO{sub 2}/TiO{sub 2} fibers with well-organized linear and spring structure and large surface area under higher temperatures were prepared by a simple EISA process. - Highlights: • The ZrO{sub 2}/TiO{sub 2} fibers were prepared by EISA process combined with steam heat-treatment. • The mesoporous ZrO{sub 2}/TiO{sub 2} fibers have well-organized linear and spring structure. • The fibers were composed of oval rod nanocrystals of ZrTiO{sub 4}. - Abstract: The ultra-stable order mesoporous ZrO{sub 2}/TiO{sub 2} fibers with well-organized linear and spring structure and large surface areas under higher temperatures were prepared by a (simplemore » evaporation-induced assembly) EISA process. The preparation, microstructures and formation processes were characterized by Fourier transformation infrared (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and N{sub 2} adsorption–absorption measurements. The fibers take on pinstripe configuration which is very orderly along or perpendicular to the axial direction of the fibers. The diameters of the pinstripe are in the region of 200–400 nm and arranges regularly, which are composed of oval rod nanocrystals of ZrTiO{sub 4}.« less

Effect of SiO 2-ZrO 2 supports prepared by a grafting method on hydrogen production by steam reforming of liquefied natural gas over Ni/SiO 2-ZrO 2 catalysts

NASA Astrophysics Data System (ADS)

Seo, Jeong Gil; Youn, Min Hye; Song, In Kyu

SiO 2-ZrO 2 supports with various zirconium contents are prepared by grafting a zirconium precursor onto the surface of commercial Carbosil silica. Ni(20 wt.%)/SiO 2-ZrO 2 catalysts are then prepared by an impregnation method, and are applied to hydrogen production by steam reforming of liquefied natural gas (LNG). The effect of SiO 2-ZrO 2 supports on the performance of the Ni(20 wt.%)/SiO 2-ZrO 2 catalysts is investigated. SiO 2-ZrO 2 prepared by a grafting method serves as an efficient support for the nickel catalyst in the steam reforming of LNG. Zirconia enhances the resistance of silica to steam significantly and increases the interaction between nickel and the support, and furthermore, prevents the growth of nickel oxide species during the calcination process through the formation of a ZrO 2-SiO 2 composite structure. The crystalline structures and catalytic activities of the Ni(20 wt.%)/SiO 2-ZrO 2 catalysts are strongly influenced by the amount of zirconium grafted. The conversion of LNG and the yield of hydrogen show volcano-shaped curves with respect to zirconium content. Among the catalysts tested, the Ni(20 wt.%)/SiO 2-ZrO 2 (Zr/Si = 0.54) sample shows the best catalytic performance in terms of both LNG conversion and hydrogen yield. The well-developed and pure tetragonal phase of ZrO 2-SiO 2 (Zr/Si = 0.54) appears to play an important role in the adsorption of steam and subsequent spillover of steam from the support to the active nickel. The small particle size of the metallic nickel in the Ni(20 wt.%)/SiO 2-ZrO 2 (Zr/Si = 0.54) catalyst is also responsible for its high performance.

Thermo-selective Tm(x)Ti(1-x)O(2-x/2) nanoparticles: from Tm-doped anatase TiO2 to a rutile/pyrochlore Tm2Ti2O7 mixture. An experimental and theoretical study with a photocatalytic application.

PubMed

Navas, Javier; Sánchez-Coronilla, Antonio; Aguilar, Teresa; De los Santos, Desireé M; Hernández, Norge C; Alcántara, Rodrigo; Fernández-Lorenzo, Concha; Martín-Calleja, Joaquín

2014-11-07

This is an experimental and theoretical study of thulium doped TiO2 nanoparticles. From an experimental perspective, a method was used to synthesize thulium-doped TiO2 nanoparticles in which Tm(3+) replaces Ti(4+) in the lattice, which to our knowledge has neither been reported nor studied theoretically so far. Different proportions of anatase and rutile phases were obtained at different annealing temperatures, and XRD and Raman spectroscopy also revealed the presence of a pyrochlore phase (Tm2Ti2O7) at 1173 K. Thus, the structure of the Tm-doped nanoparticles was thermally-controlled. Furthermore, XPS showed the presence of Tm(3+) in the samples synthesized, which produces oxygen vacancies to maintain the local neutrality in the lattice. The presence of Tm(3+) in the samples led to changes in the UV-Vis absorption spectra, so they showed photoluminescence properties and new states in the band gap, which produce a new lower energy electronic transition than the main TiO2 one. Periodic DFT calculations were performed to understand the experimentally produced structures. The production of oxygen vacancies was analysed and the changes generated in the structure were fully detailed. The DOS and PDOS analyses confirmed the experimental results obtained using UV-Vis spectroscopy, and showed that the new electronic states in the band gap are due to interactions of the f state of Tm and the p state of O. Likewise, the charge study and the ELF analysis indicate that when Tm is introduced into the TiO2 structure, the Ti-O bond around the oxygen vacancy is strengthened. Finally, an example of a photocatalytic application was developed to show the high efficiency of the samples due to the heterojunction in the interfaces of the phases in the samples, which improved the charge separation and the good charge carrier mobility due to the presence of the pyrochlore phase, as was also shown theoretically.

Control of La-doped Pb(Zr,Ti)O3 crystalline orientation and its influence on the properties of ferroelectric random access memory

NASA Astrophysics Data System (ADS)

Wang, Wensheng; Nomura, Kenji; Yamaguchi, Hideshi; Nakamura, Ko; Eshita, Takashi; Ozawa, Soichiro; Takai, Kazuaki; Mihara, Satoru; Hikosaka, Yukinobu; Hamada, Makoto; Kataoka, Yuji

2017-10-01

We investigated the crystallization mechanisms of sputter-deposited La-doped Pb(Zr,Ti)O3 (PLZT) on a Pt/Ti metal stack in the postdeposition annealing (PDA) at 600 °C in O2-mixed Ar ambient. As-deposited amorphous PLZT generally transforms to a perovskite phase over 550 °C through a metastable pyrochlore phase during the PDA. We found that the O2 content of the PDA ambient crucially affects the pyrochlore-perovskite transformation (PPT) speed. While an O2 content much higher than 2% of the PDA ambient suppresses PPT, an O2 content much lower than 2% enhances PPT. An O2 content around of 2% of the PDA suppresses PPT near the surface of PLZT and simultaneously keeps PPT fast in the inner regions of PLZT in the pyrochlore phase because of the O2 diffusion limit from the PLZT surface, eventually resulting in almost only the growth of highly {111} oriented columnar PLZT on Pt, which reveals better electric properties than those obtained by the PDA with the ambient of O2 contents much higher or lower than 2%.

The effect of micro-structure on upconversion luminescence of Nd3+/Yb3+ co-doped La2O3-TiO2-ZrO2 glass-ceramics

NASA Astrophysics Data System (ADS)

Zhang, Minghui; Wen, Haiqin; Pan, Xiuhong; Yu, Jianding; Jiang, Meng; Yu, Huimei; Tang, Meibo; Gai, Lijun; Ai, Fei

2018-03-01

Nd3+/Yb3+ co-doped La2O3-TiO2-ZrO2 glasses have been prepared by aerodynamic levitation method. The glasses show high refractive index of 2.28 and Abbe number of 18.3. Glass-ceramics heated at 880 °C for 50 min perform the strongest upconversion luminescence. X-ray diffraction patterns of glass-ceramics with different depths indicate that rare earth ions restrain crystallization. Body crystallization mechanism mixed with surface crystallization is confirmed in the heat treatment. Surface crystals achieve priority to grow, resulting in important effects on upconversion luminescence. The results of atomic force microscope and scanning electron microscope indicate that crystal particles with uniform size distribute densely and homogenously on the surface and large amount of glass matrix exists in the glass ceramics heated at 880 °C for 50 min. Crystals in the glass-ceramics present dense structure and strong boundaries, which can reduce the mutual nonradiative relaxation rate among rare earth ions and then improve upconversion luminescence effectively. Based on micro-structural study, the mechanism that upconversion luminescence can be improved by heat treatment has been revealed. The results of micro-structural analysis agree well with the spectra.

Atomic displacements in the charge ice pyrochlore Bi2Ti2O6O' studied by neutron total scattering

NASA Astrophysics Data System (ADS)

Shoemaker, Daniel P.; Seshadri, Ram; Hector, Andrew L.; Llobet, Anna; Proffen, Thomas; Fennie, Craig J.

2010-04-01

The oxide pyrochlore Bi2Ti2O6O' is known to be associated with large displacements of Bi and O' atoms from their ideal crystallographic positions. Neutron total scattering, analyzed in both reciprocal and real space, is employed here to understand the nature of these displacements. Rietveld analysis and maximum entropy methods are used to produce an average picture of the structural nonideality. Local structure is modeled via large-box reverse Monte Carlo simulations constrained simultaneously by the Bragg profile and real-space pair distribution function. Direct visualization and statistical analyses of these models show the precise nature of the static Bi and O' displacements. Correlations between neighboring Bi displacements are analyzed using coordinates from the large-box simulations. The framework of continuous symmetry measures has been applied to distributions of O'Bi4 tetrahedra to examine deviations from ideality. Bi displacements from ideal positions appear correlated over local length scales. The results are consistent with the idea that these nonmagnetic lone-pair containing pyrochlore compounds can be regarded as highly structurally frustrated systems.

Heavy-ion irradiation effects on U3O8 incorporated Gd2Zr2O7 waste forms.

PubMed

Lu, Xirui; Shu, Xiaoyan; Chen, Shunzhang; Zhang, Kuibao; Chi, Fangtin; Zhang, Haibin; Shao, Dadong; Mao, Xueli

2018-06-12

In this research, the heavy-ion irradiation effects of U-bearing Gd 2 Zr 2 O 7 ceramics were explored for nuclear waste immobilization. U 3 O 8 was designed to be incorporated into Gd 2 Zr 2 O 7 from two different routes in the form of (Gd 1-4 x U 2 x ) 2 (Zr 1- x U x ) 2 O 7 (x = 0.1, 0.14). The self-irradiation of actinide nuclides was simulated by Xe 20+ heavy-ion radiation under different fluences. Grazing incidence X-ray diffraction (GIXRD) analysis reveals the relationship between radiation dose, damage and depth. The radiation tolerance is promoted with the increment of U 3 O 8 content in the discussed range. Raman spectroscopy testifies the enhancement of radiation tolerance and microscopically existed phase evolution from the chemical bond vibrations. In addition, the microstructure and elemental distribution of the irradiated samples were analyzed as well. The amorphization degree of the sample surface declines as the U content was elevated from x = 0.1 to x = 0.14. Copyright © 2018 Elsevier B.V. All rights reserved.

Pulsed laser deposition of {CeO_2} and {Ce_{1-x}M_xO_2} (M = La, Zr): Application to insulating barrier in cuprate heterostructures

NASA Astrophysics Data System (ADS)

Berger, S.; Contour, J.-P.; Drouet, M.; Durand, O.; Khodan, A.; Michel, D.; Régi, F.-X.

1998-03-01

SrTiO_3 had been often tentatively used as an insulating barrier for HT superconductor/insulator heterostructures. Unfortunately, the deposition of SrTiO_3 on the YBa_2Cu_3O_7 inverse interface results in a poor epitaxial regrowth producing a high roughness dislocated titanate layer. Taking into account the good matching with YBa_2Cu_3O_7 and LaAlO_3, CeO_2 and Ce_{1-x}M_xO_2 (M = La, Zr), epitaxial layers were grown by pulsed laser deposition on LaAlO_3 substrates and introduced into YBa_2Cu_3O_7 based heterostructures as insulating barrier. After adjusting the growth parameters from RHEED oscillations, epitaxial growth is achieved, the oxide crystal axes being rotated by 45^circ from those of the substrate. The surface roughness of 250 nm thick films is very low with a rms value lower than 0.5 nm over 1;μ m^2. The YBa_2Cu_3O_7 layers of a YBa_2Cu_3O_7/CeO_2 /YBa_2Cu_3O_7 heterostructures grown using these optimized parameters show an independent resistive transition, when the thickness is larger than 25 nm, respectively at T_c_1 = 89.6;K and T_c_2 = 91.4;{K}. SrTiO3 est souvent utilisé comme barrière isolante dans des hétérostructures SIS de cuprates supraconducteurs, cependant les défauts générés lors de la croissance de ce titanate sur l'interface inverse de YBa2Cu3O7 conduisent à un matériau dont la qualité cristalline et les propriétés physiques sont médiocres. L'oxyde de cérium CeO2 est également une barrière isolante potentielle intéressante pour ces structures SIS basées sur YBa2Cu3O7 car cet oxyde cubique (a = 0,5411 nm, asqrt{2}/2 = 0,3825 nm) qui est peu désaccordé par rapport au plan ab du cuprate (Δ a/a = - 0,18 %, Δ b/a = 1,6 %) présente de plus un coefficient de dilatation thermique (10,6 × 10^{-6 circ}C^{-1}) très voisin de celui de YBa2Cu3O7 (13 × 10^{-6 circ}C^{-1}). Nous avons donc étudié l'épitaxie de CeO2 et des oxydes de type Ce{1-x}MxO2 (M = La, Zr) en ablation laser pulsée afin de définir des conditions de

Miscibility of amorphous ZrO2-Al2O3 binary alloy

NASA Astrophysics Data System (ADS)

Zhao, C.; Richard, O.; Bender, H.; Caymax, M.; De Gendt, S.; Heyns, M.; Young, E.; Roebben, G.; Van Der Biest, O.; Haukka, S.

2002-04-01

Miscibility is a key factor for maintaining the homogeneity of the amorphous structure in a ZrO2-Al2O3 binary alloy high-k dielectric layer. In the present work, a ZrO2/Al2O3 laminate thin layer has been prepared by atomic layer chemical vapor deposition on a Si (100) wafer. This layer, with artificially induced inhomogeneity (lamination), enables one to study the change in homogeneity of the amorphous phase in the ZrO2/Al2O3 system during annealing. High temperature grazing incidence x-ray diffraction (HT-XRD) was used to investigate the change in intensity of the constructive interference peak of the x-ray beams which are reflected from the interfaces of ZrO2/Al2O3 laminae. The HT-XRD spectra show that the intensity of the peak decreases with an increase in the anneal temperature, and at 800 °C, the peak disappears. The same samples were annealed by a rapid thermal process (RTP) at temperatures between 700 and 1000 °C for 60 s. Room temperature XRD of the RTP annealed samples shows a similar decrease in peak intensity. Transmission electronic microscope images confirm that the laminate structure is destroyed by RTP anneals and, just below the crystallization onset temperature, a homogeneous amorphous ZrAlxOy phase forms. The results demonstrate that the two artificially separated phases, ZrO2 and Al2O3 laminae, tend to mix into a homogeneous amorphous phase before crystallization. This observation indicates that the thermal stability of ZrO2-Al2O3 amorphous phase is suitable for high-k applications.

Structural Studies of dielectric HDPE+ZrO2 polymer nanocomposites: filler concentration dependences

NASA Astrophysics Data System (ADS)

Nabiyev, A. A.; Islamov, A. Kh; Maharramov, A. M.; Nuriyev, M. A.; Ismayilova, R. S.; Doroshkevic, A. S.; Pawlukojc, A.; Turchenko, V. A.; Olejniczak, A.; Rulev, M. İ.; Almasan, V.; Kuklin, A. I.

2018-03-01

Structural properties of HDPE+ZrO2 polymer nanocomposites thin films of 80-100μm thicknesses were investigated using SANS, XRD, Laser Raman and FTIR spectroscopy. The mass fraction of the filler was 1, 3, 10, and 20%. Results of XRD analysis showed that ZrO2 powder was crystallized both in monoclinic and in cubic phase under normal conditions. The percentages of monoclinic and cubic phase were found to be 99.8% and 0.2%, respectively. It was found that ZrO2 nanoparticles did not affect the main crystal and chemical structure of HDPE, but the degree of crystallinity of the polymer decreases with increasing concentration of zirconium oxide. SANS experiments showed that at ambient conditions ZrO2 nanoparticles mainly distributed like mono-particles in the polymer matrix at all concentrations of filler.The structure of HDPE+ZrO2 does not changes up to 132°C at 1-3% of filler, excepting changing of the polymer structure at temperatures upper 82°C. At high concentrations of filler 10-20% the aggregation of ZrO2 nanoparticles occurs, forming domains of 2.5μm. The results of Raman and FTIR spectroscopy did not show additional specific chemical bonds between the filler and the polymer matrix. New peaks formation was not observed. These results suggest that core-shell structure does not exist in the polymer nanocomposite system.

Giant reversible magnetocaloric effect in the pyrochlore Er 2 Mn 2 O 7 due to a cooperative two-sublattice ferromagnetic order

DOE PAGES

Cai, Y. Q.; Jiao, Y. Y.; Cui, Qi; ...

2017-11-29

Most magnetic refrigeration materials showing a large and reversible magnetocaloric effect (MCE) undergo a second-order ferromagnetic (FM) transition involving large-moment magnetic species on one sublattice. Furthermore, a stronger MCE is expected near a cooperative FM order of two or more magnetic species with large magnetic moments residing on different sublattices, but experimental realizations are rare. Here we report on the discovery of large MCE in the cubic pyrochlore Er 2Mn 2O 7 near its second-order FM transition at T c ≈ 34K; under the magnetic field change of 1 and 5 T, the maximum magnetic entropy change –ΔS M ismore » 5.27 and 16.1Jkg –1K –1, and the estimated magnetic refrigerant capacity reaches 68 and 522Jkg –1, respectively. These latter values are among the largest for the known MCE materials. The observed giant and reversible MCE in Er 2Mn 2O 7 is mainly attributed to the large saturation moment of 18.9μ B per formula unit owing to a simultaneous FM ordering of the rear-earth Er 3+ and transition-metal Mn 4+ localized moments. Our results suggest that Er 2Mn 2O 7 pyrochlore is a promising candidate for magnetic refrigeration applications in the temperature range 20–80 K. More importantly, this work provides a new material system for developing high-performance MCE materials that can exhibit a strongly coupled FM transition involving two magnetic sublattices of large local moments in a single-phase material.« less

Giant reversible magnetocaloric effect in the pyrochlore Er 2 Mn 2 O 7 due to a cooperative two-sublattice ferromagnetic order

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cai, Y. Q.; Jiao, Y. Y.; Cui, Qi

Most magnetic refrigeration materials showing a large and reversible magnetocaloric effect (MCE) undergo a second-order ferromagnetic (FM) transition involving large-moment magnetic species on one sublattice. Furthermore, a stronger MCE is expected near a cooperative FM order of two or more magnetic species with large magnetic moments residing on different sublattices, but experimental realizations are rare. Here we report on the discovery of large MCE in the cubic pyrochlore Er 2Mn 2O 7 near its second-order FM transition at T c ≈ 34K; under the magnetic field change of 1 and 5 T, the maximum magnetic entropy change –ΔS M ismore » 5.27 and 16.1Jkg –1K –1, and the estimated magnetic refrigerant capacity reaches 68 and 522Jkg –1, respectively. These latter values are among the largest for the known MCE materials. The observed giant and reversible MCE in Er 2Mn 2O 7 is mainly attributed to the large saturation moment of 18.9μ B per formula unit owing to a simultaneous FM ordering of the rear-earth Er 3+ and transition-metal Mn 4+ localized moments. Our results suggest that Er 2Mn 2O 7 pyrochlore is a promising candidate for magnetic refrigeration applications in the temperature range 20–80 K. More importantly, this work provides a new material system for developing high-performance MCE materials that can exhibit a strongly coupled FM transition involving two magnetic sublattices of large local moments in a single-phase material.« less

Electrical characteristics of SiO2/ZrO2 hybrid tunnel barrier for charge trap flash memory

NASA Astrophysics Data System (ADS)

Choi, Jaeho; Bae, Juhyun; Ahn, Jaeyoung; Hwang, Kihyun; Chung, Ilsub

2017-08-01

In this paper, we investigate the electrical characteristics of SiO2/ZrO2 hybrid tunnel oxide in metal-Al2O3-SiO2-Si3N4-SiO2-silicon (MAONOS) structure in an effort to improve program and erase speed as well as retention characteristics. Inserting ZrO2 into the conventional MAONOS structure increased the programmed V th variation to 6.8 V, and increased the erased V th variation to -3.7 V at 17 MV/cm. The results can be understood in terms of reducing the Fowler-Nordheim (F/N) tunneling barrier due to high-k ZrO2 in the tunneling oxide. In addition, Zr diffusion in SiO2 caused the formation of Zr x Si1- x O2 at the interface region, which reduced the energy band gap of SiO2. The retention property of the hybrid tunnel oxide varied depending on the thickness of SiO2. For thin SiO2 less than 30 Å, the retention properties of the tunneling oxides were poor compared with those of the SiO2 only tunneling oxides. However, the hybrid tunneling oxides with SiO2 thickness thicker than 40 Å yielded improved retention behavior compared with those of the SiO2-only tunneling oxides. The detailed analysis in charge density of ZrO2 was carried out by ISPP test. The obtained charge density was quite small compared to that of the total charge density, which indicates that the inserted ZrO2 layer serves as a tunneling material rather than charge storage dielectric.

Synthesis, characterization, and photocatalytic application of Pd/ZrO2 and Pt/ZrO2

NASA Astrophysics Data System (ADS)

Saeed, Khalid; Sadiq, Mohammad; Khan, Idrees; Ullah, Saleem; Ali, Nauman; Khan, Adnan

2018-05-01

Zirconia-supported palladium (Pd/ZrO2) and Zirconia-supported platinum (Pt/ZrO2) nanoparticles (NPs) are synthesized from their precursors via impregnation technique. The Pd/ZrO2 and Pt/ZrO2 NPs were analyzed via SEM and EDX, while the study of indigo disulfonate dye degradation was carried out by UV/VIS spectrophotometer. The SEM micrographs illustrated that the Pd and Pt NPs were well placed on ZrO2 surface. The Pd/ZrO2 and Pt/ZrO2 NPs were also employed as photocatalysts for the photodegradation of indigo disulfonate in an aqueous medium under UV-light irradiation. The photodegradation study presented that Pd/ZrO2 and Pt/ZrO2 NPs degraded 96 and 94% of indigo disulfonate in 14 h, respectively. The effect of pH of medium and catalyst dosage and efficiency of recovered Pd/ZrO2 and Pt/ZrO2 NPs on the photocatalytic degradation were also studied. It was also found that the maximum degradation of dye was found at pH 10 (95-97%) and at 0.02 g weight (40.28%).

Electric-field control of electronic transport properties and enhanced magnetoresistance in La0.7Sr0.3MnO3/0.5BaZr0.2Ti0.8O3-0.5Ba0.7Ca0.3TiO3 lead-free multiferroic structures

NASA Astrophysics Data System (ADS)

Yan, Jian-Min; Gao, Guan-Yin; Liu, Yu-Kuai; Wang, Fei-Fei; Zheng, Ren-Kui

2017-10-01

We report the fabrication of lead-free multiferroic structures by depositing ferromagnetic La0.7Sr0.3MnO3 (LSMO) polycrystalline films on polished 0.5BaZr0.2Ti0.8O3-0.5Ba0.7Ca0.3TiO3 (BZT-BCT) piezoelectric ceramic substrates. By applying electric fields to the BZT-BCT along the thickness direction, the resistivity of LSMO films can be effectively manipulated via the piezoelectric strain of the BZT-BCT. Moreover, the LSMO polycrystalline films exhibit almost temperature independent and significantly enhanced magnetoresistance (MR) below TC. At T = 2 K and H = 8 T, the MR of polycrystalline films is approximately two orders of magnitude higher than that of LSMO epitaxial films grown on (LaAlO3)0.3(SrAl1/2Ta1/2O3)0.7 single-crystal substrates. The enhanced MR mainly results from the spin-polarized tunneling of charge carriers across grain boundaries. The LSMO/BZT-BCT structures with electric-field controllable modulation of resistivity and enhanced MR effect may have potential applications in low-energy consumption and environmentally friendly electronic devices.

Layered-structural monoclinic–orthorhombic perovskite La{sub 2}Ti{sub 2}O{sub 7} to orthorhombic LaTiO{sub 3} phase transition and their microstructure characterization

DOE Office of Scientific and Technical Information (OSTI.GOV)

Herrera, G., E-mail: manuel.herrera@enp.unam.mx; Departamento de Química Inorgánica, Universidad de Valencia, 46100 Burjasot, Valencia; Instituto de Ciencias Nucleares, Universidad Nacional Autónoma de México, 04510 México D. F.

2014-03-01

The layered-structural ceramics, such as lanthanum titanate (La{sub 2}Ti{sub 2}O{sub 7}), have been known for their good temperature and low dielectric loss at microwave frequencies that make them good candidate materials for high frequency applications. However, few studies have been conducted on the synthesis optimization by sol gel reaction, in particular by acrylamide polymerization route. The interest in La{sub 2}Ti{sub 2}O{sub 7} ceramic has been greatly increased recently due to the effect of oriented grains. This anisotropy of the microstructure leads to anisotropy in dielectric, electrical and mechanical properties. In this study, grain oriented lanthanum titanate was produced by themore » sol–gel acrylamide polymerization route. The characterizations of the samples were achieved by thermal analysis, X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), and transmission electron microscopy (TEM). X-ray diffraction indicates that the formation of monoclinic perovskite La{sub 2}Ti{sub 2}O{sub 7} nanocrystals is a necessary first step to obtain orthorhombic LaTiO{sub 3} nanocomposites (with space group Pbnm). In this work we identified that the monoclinic perovskite La{sub 2}Ti{sub 2}O{sub 7} with space group P2{sub 1} transforms its structure into one with the orthorhombic space group Cmc2{sub 1} at approximately 1073 K. The microstructure associated consisted of flaky monoclinic La{sub 2}Ti{sub 2}O{sub 7} nanocomposites in comparison with round-shaped LaTiO{sub 3} nanocomposites. - Highlights: • The flaky-like La{sub 2}Ti{sub 2}O{sub 7} compound was synthesized by sol–gel acrylamide route. • Simultaneous monitoring of the DTA and XRD with temperature was performed. • Phase transformation characterization of La{sub 2}Ti{sub 2}O{sub 7} has been carried out. • The variation of the La{sub 2}Ti{sub 2}O{sub 7} and LaTiO{sub 3} grain morphology has been compared.« less

Batievaite-(Y), Y2Ca2Ti[Si2O7]2(OH)2(H2O)4, a new mineral from nepheline syenite pegmatite in the Sakharjok massif, Kola Peninsula, Russia

NASA Astrophysics Data System (ADS)

Lyalina, L. M.; Zolotarev, A. A.; Selivanova, E. A.; Savchenko, Ye. E.; Krivovichev, S. V.; Mikhailova, Yu. A.; Kadyrova, G. I.; Zozulya, D. R.

2016-12-01

Batievaite-(Y), Y2Ca2Ti[Si2O7]2(OH)2(H2O)4, is a new mineral found in nepheline syenite pegmatite in the Sakharjok alkaline massif, Western Keivy, Kola Peninsula, Russia. The pegmatite mainly consists of nepheline, albite, alkali pyroxenes, amphiboles, biotite and zeolites. Batievaite-(Y) is a late-pegmatitic or hydrothermal mineral associated with meliphanite, fluorite, calcite, zircon, britholite-group minerals, leucophanite, gadolinite-subgroup minerals, titanite, smectites, pyrochlore-group minerals, zirkelite, cerianite-(Ce), rutile, behoite, ilmenite, apatite-group minerals, mimetite, molybdenite, and nickeline. Batievaite-(Y) is pale-cream coloured with white streak and dull, greasy or pearly luster. Its Mohs hardness is 5-5.5. No cleavage or parting was observed. The measured density is 3.45(5) g/cm3. Batievaite-(Y) is optically biaxial positive, α 1.745(5), β 1.747(5), γ 1.752(5) (λ 589 nm), 2 V meas. = 60(5)°, 2 V calc. = 65°. Batievaite-(Y) is triclinic, space group P-1, a 9.4024(8), b 5.5623(5), c 7.3784(6) Å, α 89.919(2), β 101.408(2), γ 96.621(2)°, V 375.65(6) Å3 and Z = 1. The eight strongest lines of the X-ray powder diffraction pattern [ d(Å)(I)( hkl)] are: 2.991(100)(11-2), 7.238(36)(00-1), 3.061(30)(300), 4.350(23)(0-1-1), 9.145(17)(100), 4.042(16)(11-1), 2.819(16)(3-10), 3.745(13)(2-10). The chemical composition determined by electron probe microanalysis (EPMA) is (wt.%): Nb2O5 2.25, TiO2 8.01, ZrO2 2.72, SiO2 29.96, Al2O3 0.56, Fe2O3 0.43, Y2O3 11.45, La2O3 0.22, Ce2O3 0.33, Nd2O3 0.02, Gd2O3 0.07, Dy2O3 0.47, Er2O3 1.07, Tm2O3 0.25, Yb2O3 2.81, Lu2O3 0.45, CaO 24.98, MnO 1.31, MgO 0.01, Na2O 1.13, K2O 0.02, F 2.88, Cl 0.19, H2O 6.75 (determined on the basis of crystal structure data), O = (F,Cl) -1.25, total 97.09 wt.%. The empirical formula based on the EPMA and single-crystal structure analyses is (Y0.81Ca0.65Mn0.15Zr0.12Yb0.11Er0.04Fe3+ 0.04Ce0.02Dy0.02Lu0.02La0.01Tm0.01)Σ2.00((H2O)0.75Ca0.70□0.55)Σ2.00Ca2.00(□0.61Na0

A thermal study on the structural changes of bimetallic ZrO2-modified TiO2 nanotubes synthesized using supercritical CO2.

PubMed

Lucky, R A; Charpentier, P A

2009-05-13

In this study the thermal behavior of bimetallic ZrO(2)-TiO(2) (10/90 mol/mol) nanotubes are discussed which were synthesized via a sol-gel process in supercritical carbon dioxide (scCO(2)). The effects of calcination temperature on the morphology, phase structure, mean crystallite size, specific surface area and pore volume of the nanotubes were investigated by using a variety of physiochemical techniques. We report that SEM and TEM images showed that the nanotubular structure was preserved at up to 800 degrees C calcination temperature. When exposed to higher temperatures (900-1000 degrees C) the ZrO(2)-TiO(2) tubes deformed and the crystallites fused together, forming larger crystallites, and a bimetallic ZrTiO(4) species was detected. These results were further examined using TGA, FTIR, XRD and HRTEM analysis. The BET textural properties demonstrated that the presence of a small amount of Zr in the TiO(2) matrix inhibited the grain growth, stabilized the anatase phase and increased the thermal stability.

Crystal Structure of Garnet-Related Li-Ion Conductor Li7–3xGaxLa3Zr2O12: Fast Li-Ion Conduction Caused by a Different Cubic Modification?

PubMed Central

2016-01-01

Li-oxide garnets such as Li7La3Zr2O12 (LLZO) are among the most promising candidates for solid-state electrolytes to be used in next-generation Li-ion batteries. The garnet-structured cubic modification of LLZO, showing space group Ia-3d, has to be stabilized with supervalent cations. LLZO stabilized with Ga3+ shows superior properties compared to LLZO stabilized with similar cations; however, the reason for this behavior is still unknown. In this study, a comprehensive structural characterization of Ga-stabilized LLZO is performed by means of single-crystal X-ray diffraction. Coarse-grained samples with crystal sizes of several hundred micrometers are obtained by solid-state reaction. Single-crystal X-ray diffraction results show that Li7–3xGaxLa3Zr2O12 with x > 0.07 crystallizes in the acentric cubic space group I-43d. This is the first definite record of this cubic modification for LLZO materials and might explain the superior electrochemical performance of Ga-stabilized LLZO compared to its Al-stabilized counterpart. The phase transition seems to be caused by the site preference of Ga3+. 7Li NMR spectroscopy indicates an additional Li-ion diffusion process for LLZO with space group I-43d compared to space group Ia-3d. Despite all efforts undertaken to reveal structure–property relationships for this class of materials, this study highlights the potential for new discoveries. PMID:27019548

Chemical ordering in substituted fluorite oxides: a computational investigation of Ho 2Zr 2O 7 and RE 2Th 2O 7 (RE=Ho, Y, Gd, Nd, La)

DOE PAGES

Solomon, Jonathan M.; Shamblin, Jacob; Lang, Maik; ...

2016-12-12

Fluorite-structured oxides find widespread use for applications spanning nuclear energy and waste containment, energy conversion, and sensing. In such applications the host tetravalent cation is often partially substituted by trivalent cations, with an associated formation of charge-compensating oxygen vacancies. The stability and properties of such materials are known to be influenced strongly by chemical ordering of the cations and vacancies, and the nature of such ordering and associated energetics are thus of considerable interest. Here we employ density-functional theory (DFT) calculations to study the structure and energetics of cation and oxygen-vacancy ordering in Ho 2Zr 2O 7. In a recentmore » neutron total scattering study, solid solutions in this system were reported to feature local chemical ordering based on the fluorite-derivative weberite structure. The calculations show a preferred chemical ordering qualitatively consistent with these findings, and yield values for the ordering energy of 9.5 kJ/mol-cation. Similar DFT calculations are applied to additional RE 2Th 2O 7'' fluorite compounds, spanning a range of values for the ratio of the tetravalent and trivalent (RE) cation radii. Finally, the results demonstrate that weberite-type order becomes destabilized with increasing values of this size ratio, consistent with an increasing energetic preference for the tetravalent cations to have higher oxygen coordination.« less

Chemical ordering in substituted fluorite oxides: a computational investigation of Ho2Zr2O7 and RE2Th2O7 (RE=Ho, Y, Gd, Nd, La).

PubMed

Solomon, Jonathan M; Shamblin, Jacob; Lang, Maik; Navrotsky, Alexandra; Asta, Mark

2016-12-12

Fluorite-structured oxides find widespread use for applications spanning nuclear energy and waste containment, energy conversion, and sensing. In such applications the host tetravalent cation is often partially substituted by trivalent cations, with an associated formation of charge-compensating oxygen vacancies. The stability and properties of such materials are known to be influenced strongly by chemical ordering of the cations and vacancies, and the nature of such ordering and associated energetics are thus of considerable interest. Here we employ density-functional theory (DFT) calculations to study the structure and energetics of cation and oxygen-vacancy ordering in Ho 2 Zr 2 O 7 . In a recent neutron total scattering study, solid solutions in this system were reported to feature local chemical ordering based on the fluorite-derivative weberite structure. The calculations show a preferred chemical ordering qualitatively consistent with these findings, and yield values for the ordering energy of 9.5 kJ/mol-cation. Similar DFT calculations are applied to additional RE 2 Th 2 O 7 fluorite compounds, spanning a range of values for the ratio of the tetravalent and trivalent (RE) cation radii. The results demonstrate that weberite-type order becomes destabilized with increasing values of this size ratio, consistent with an increasing energetic preference for the tetravalent cations to have higher oxygen coordination.

Chemical ordering in substituted fluorite oxides: a computational investigation of Ho2Zr2O7 and RE2Th2O7 (RE=Ho, Y, Gd, Nd, La)

PubMed Central

Solomon, Jonathan M.; Shamblin, Jacob; Lang, Maik; Navrotsky, Alexandra; Asta, Mark

2016-01-01

Fluorite-structured oxides find widespread use for applications spanning nuclear energy and waste containment, energy conversion, and sensing. In such applications the host tetravalent cation is often partially substituted by trivalent cations, with an associated formation of charge-compensating oxygen vacancies. The stability and properties of such materials are known to be influenced strongly by chemical ordering of the cations and vacancies, and the nature of such ordering and associated energetics are thus of considerable interest. Here we employ density-functional theory (DFT) calculations to study the structure and energetics of cation and oxygen-vacancy ordering in Ho2Zr2O7. In a recent neutron total scattering study, solid solutions in this system were reported to feature local chemical ordering based on the fluorite-derivative weberite structure. The calculations show a preferred chemical ordering qualitatively consistent with these findings, and yield values for the ordering energy of 9.5 kJ/mol-cation. Similar DFT calculations are applied to additional RE2Th2O7 fluorite compounds, spanning a range of values for the ratio of the tetravalent and trivalent (RE) cation radii. The results demonstrate that weberite-type order becomes destabilized with increasing values of this size ratio, consistent with an increasing energetic preference for the tetravalent cations to have higher oxygen coordination. PMID:27941870

Chemical ordering in substituted fluorite oxides: a computational investigation of Ho2Zr2O7 and RE2Th2O7 (RE=Ho, Y, Gd, Nd, La)

NASA Astrophysics Data System (ADS)

Solomon, Jonathan M.; Shamblin, Jacob; Lang, Maik; Navrotsky, Alexandra; Asta, Mark

2016-12-01

Fluorite-structured oxides find widespread use for applications spanning nuclear energy and waste containment, energy conversion, and sensing. In such applications the host tetravalent cation is often partially substituted by trivalent cations, with an associated formation of charge-compensating oxygen vacancies. The stability and properties of such materials are known to be influenced strongly by chemical ordering of the cations and vacancies, and the nature of such ordering and associated energetics are thus of considerable interest. Here we employ density-functional theory (DFT) calculations to study the structure and energetics of cation and oxygen-vacancy ordering in Ho2Zr2O7. In a recent neutron total scattering study, solid solutions in this system were reported to feature local chemical ordering based on the fluorite-derivative weberite structure. The calculations show a preferred chemical ordering qualitatively consistent with these findings, and yield values for the ordering energy of 9.5 kJ/mol-cation. Similar DFT calculations are applied to additional RE2Th2O7 fluorite compounds, spanning a range of values for the ratio of the tetravalent and trivalent (RE) cation radii. The results demonstrate that weberite-type order becomes destabilized with increasing values of this size ratio, consistent with an increasing energetic preference for the tetravalent cations to have higher oxygen coordination.

Creep Resistance of ZrO2 Ceramic Improved by the Addition of a Small Amount of Er2O3

NASA Technical Reports Server (NTRS)

Martinez-Fernandez, Julian; Sayir, Ali; Farmer, Serene C.

2003-01-01

of this class of materials. Adding Er2O3 to ZrO2 results in microstructure of stable and metastable tetragonal precipitates that with thermal treatment evolve to a tweed structure of nanosize tetragonal lamellae. The superior high-temperature creep resistance of Er2O3-doped ZrO2 is attributed to nanoscale precipitation hardening. Doping with Er2O3 will significantly increase the upper-use temperature limit of ZrO2. Potential applications include using Er2O3-doped ZrO2 as a high-temperature fiber for structural applications and adding Er2O3 to reduce the sintering rates of ZrO2 thermal barrier coatings. This work was conducted at Dpto. de F sica de la Materia Condensada, Universidad de Sevilla, Spain, and at NASA Glenn.

Stability of fluorite-type La 2Ce 2O 7 under extreme conditions

DOE PAGES

Zhang, F. X.; Tracy, C. L.; Lang, M.; ...

2016-03-03

Here, the structural stability of fluorite-type La 2Ce 2O 7 was studied at pressure up to ~40 GPa and under hydrothermal conditions (~1 GPa, 350 °C), respectively, using synchrotron x-ray diffraction (XRD) and Raman scattering measurements. XRD measurements indicated that fluorite-type La 2Ce 2O 7 is not stable at pressures greater than 22.6 GPa and slowly transforms to a high-pressure phase. The high-pressure phase is not stable and changes back to the fluorite-type structure when pressure is released. The La 2Ce 2O 7 fluorite is also not stable under hydrothermal conditions and begins to react with water at 200~250 °C.more » Both Raman and XRD results suggest that lanthanum hydroxide La(OH) 3 and La 3+-doped CeO 2 fluorite are the dominant products after hydrothermal treatment.« less

Temperature dependence of the radiation tolerance of nanocrystalline pyrochlores A 2Ti 2O 7 (A = Gd, Ho and Lu)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wen, J.; Sun, C.; Dholabhai, P. P.

A potentially enhanced radiation resistance of nanocrystalline materials, as a consequence of the high density of interfaces and surfaces, has attracted much attention both to understand the fundamental role of these defect sinks and to develop them for high-radiation environments. Here, irradiation response of nanocrystalline A 2Ti 2O 7 (A = Gd, Ho and Lu) pyrochlore powders with grain sizes of 20–30 nm was investigated by 1-MeV Kr 2+ ion bombardment. In situ transmission electron microscopy (TEM) revealed that the critical amorphization fluence for each nanocrystalline compound at room temperature was greater than that for their coarse-grained counterparts, indicating anmore » enhanced amorphization resistance. The effect of temperature on the irradiation response of one of these compounds, nanocrystalline Lu 2Ti 2O 7, was further examined by performing ion irradiation at an elevated temperature range of 480–600 K. The critical amorphization temperature (T c) was found to be noticeably higher in nanocrystalline Lu 2Ti 2O 7 (610 K) than its coarse-grained counterpart (480 K), revealing that nanocrystalline Lu 2Ti 2O 7 is less resistant to amorphization compared to its coarse-grained phase under high temperatures. We interpret these results with the aid of atomistic simulations. Molecular statics calculations find that cation antisite defects are less energetically costly to form near surfaces than in the bulk, suggesting that the nanocrystalline form of these materials is generally less susceptible to amorphization than coarse-grained counterparts at low temperatures where defect kinetics are negligible. In contrast, at high temperatures, the annealing efficiency of antisite defects by cation interstitials is significantly reduced due to the sink properties of the surfaces in the nanocrystalline pyrochlore, which contributes to the observed higher amorphization temperature in the nano-grained phase than in coarse-grained counterpart. Altogether, these

Temperature dependence of the radiation tolerance of nanocrystalline pyrochlores A 2Ti 2O 7 (A = Gd, Ho and Lu)

DOE PAGES

Wen, J.; Sun, C.; Dholabhai, P. P.; ...

2016-03-21

A potentially enhanced radiation resistance of nanocrystalline materials, as a consequence of the high density of interfaces and surfaces, has attracted much attention both to understand the fundamental role of these defect sinks and to develop them for high-radiation environments. Here, irradiation response of nanocrystalline A 2Ti 2O 7 (A = Gd, Ho and Lu) pyrochlore powders with grain sizes of 20–30 nm was investigated by 1-MeV Kr 2+ ion bombardment. In situ transmission electron microscopy (TEM) revealed that the critical amorphization fluence for each nanocrystalline compound at room temperature was greater than that for their coarse-grained counterparts, indicating anmore » enhanced amorphization resistance. The effect of temperature on the irradiation response of one of these compounds, nanocrystalline Lu 2Ti 2O 7, was further examined by performing ion irradiation at an elevated temperature range of 480–600 K. The critical amorphization temperature (T c) was found to be noticeably higher in nanocrystalline Lu 2Ti 2O 7 (610 K) than its coarse-grained counterpart (480 K), revealing that nanocrystalline Lu 2Ti 2O 7 is less resistant to amorphization compared to its coarse-grained phase under high temperatures. We interpret these results with the aid of atomistic simulations. Molecular statics calculations find that cation antisite defects are less energetically costly to form near surfaces than in the bulk, suggesting that the nanocrystalline form of these materials is generally less susceptible to amorphization than coarse-grained counterparts at low temperatures where defect kinetics are negligible. In contrast, at high temperatures, the annealing efficiency of antisite defects by cation interstitials is significantly reduced due to the sink properties of the surfaces in the nanocrystalline pyrochlore, which contributes to the observed higher amorphization temperature in the nano-grained phase than in coarse-grained counterpart. Altogether, these

ZrO2 Layer Thickness Dependent Electrical and Dielectric Properties of BST/ZrO2/BST Multilayer Thin Films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sahoo, S. K.; Misra, D.; Agrawal, D. C.

2011-01-01

Recently, high K materials play an important role in microelectronic devices such as capacitors, memory devices, and microwave devices. Now a days ferroelectric barium strontium titanate [Ba{sub x}Sr{sub 1-x}TiO{sub 3}, (BST)] thin film is being actively investigated for applications in dynamic random access memories (DRAM), field effect transistor (FET), and tunable devices because of its properties such as high dielectric constant, low leakage current, low dielectric loss, and high dielectric breakdown strength. Several approaches have been used to optimize the dielectric and electrical properties of BST thin films such as doping, graded compositions, and multilayer structures. We have found thatmore » inserting a ZrO{sub 2} layer in between two BST layers results in a significant reduction in dielectric constant, loss tangent, and leakage current in the multilayer thin films. Also it is shown that the properties of multilayer structure are found to depend strongly on the sublayer thicknesses. In this work the effect of ZrO{sub 2} layer thickness on the dielectric, ferroelectric as well as electrical properties of BST/ZrO{sub 2}/BST multilayer structure is studied. The multilayer Ba{sub 0.8}Sr{sub 0.2}TiO{sub 3}/ZrO{sub 2}/Ba{sub 0.8}Sr{sub 0.2}TiO{sub 3} film is deposited by a sol-gel process on the platinized Si substrate. The thickness of the middle ZrO{sub 2} layer is varied while keeping the top and bottom BST layer thickness as fixed. It is observed that the dielectric constant, dielectric loss tangent, and leakage current of the multilayer films reduce with the increase of ZrO{sub 2} layer thickness and hence suitable for memory device applications. The ferroelectric properties of the multilayer film also decrease with the ZrO{sub 2} layer thickness.« less

Comparison of structural and electric properties of PbZr0.2Ti0.8O3 and CoFe2O4/PbZr0.2Ti0.8O3 films on (100)LaAlO3

NASA Astrophysics Data System (ADS)

Zhang, X. D.; Dho, Joonghoe; Park, Sungmin; Kwon, Hyosang; Hwang, Jihwan; Park, Gwangseo; Kwon, Daeyoung; Kim, Bongju; Jin, Yeryeong; Kim, Bog. G.; Karpinsky, D.; Kholkin, A. L.

2011-09-01

In this work, we investigated structural, electrical, and magnetic properties of ferroelectric PbZr0.2Ti0.8O3 (PZT) and ferrimagnetic/ferroelectric [CoFe2O4(CFO)/PZT] bilayers grown on (100)LaAlO3 (LAO) substrates supplied with bottom 50 nm thick LaNiO3 electrodes. Interestingly, structural and electrical properties of the PZT layer exhibited remarkable changes after the top-layer CFO deposition. X-ray diffraction data suggested that both the c- and a-domains exist in the PZT layer and the tetragonality of the PZT decreases upon the top-layer deposition. A variation in the electrical properties of the PZT layer upon the CFO deposition was investigated by polarization versus voltage (P-V), capacitance versus voltage (C-V), and capacitance versus frequency (C-f) measurements. The CFO deposition induced a slight decrease of the remnant polarization and more symmetric behavior of P-V loops as well as led to the improvement of fatigue behavior. The tentative origin of enhanced fatigue endurance is discussed based on the measurement results. These results were corroborated by local piezoelectric measurements. Ferrimagnetic property of the CFO/PZT bilayer was confirmed by magnetic measurement at room temperature.

Schottky barrier SOI-MOSFETs with high-k La2O3/ZrO2 gate dielectrics

PubMed Central

Henkel, C.; Abermann, S.; Bethge, O.; Pozzovivo, G.; Klang, P.; Stöger-Pollach, M.; Bertagnolli, E.

2011-01-01

Schottky barrier SOI-MOSFETs incorporating a La2O3/ZrO2 high-k dielectric stack deposited by atomic layer deposition are investigated. As the La precursor tris(N,N′-diisopropylformamidinato) lanthanum is used. As a mid-gap metal gate electrode TiN capped with W is applied. Processing parameters are optimized to issue a minimal overall thermal budget and an improved device performance. As a result, the overall thermal load was kept as low as 350, 400 or 500 °C. Excellent drive current properties, low interface trap densities of 1.9 × 1011 eV−1 cm−2, a low subthreshold slope of 70-80 mV/decade, and an ION/IOFF current ratio greater than 2 × 106 are obtained. PMID:21461054

ZrO2/MoS2 heterojunction photocatalysts for efficient photocatalytic degradation of methyl orange

NASA Astrophysics Data System (ADS)

Prabhakar Vattikuti, Surya Veerendra; Byon, Chan; Reddy, Chandragiri Venkata

2016-10-01

We report a simple solution-chemistry approach for the synthesis of ZrO2/MoS2 hybrid photocatalysts, which contain MoS2 as a cocatalyst. The material is usually obtained by a wet chemical method using ZrO(NO3)2 or (NH4)6Mo7O24·4H2O and C8H6S as precursors. The structural features of obtained materials were characterized by X-ray diffraction (XRD), highresolution transmission electron microscopy (HRTEM), X-ray photoelectron spectroscopy (XPS), thermal analysis (TG-DTA), N2 adsorption-desorption, and photoluminescence (PL). The influence on the photocatalytic activity of the MoS2 cocatalyst concentration with ZrO2 nanoparticles was studied. The MZr-2 hybrid sample had the highest photocatalytic activity for the degradation of methyl orange (MO), which was 8.45 times higher than that of pristine ZrO2 ascribed to high specific surface area and absorbance efficiency. Recycling experiments revealed that the reusability of the MZr-2 hybrid was due to the low photocorrosive effect and good catalytic stability. PL spectra confirmed the electronic interaction between ZrO2 and MoS2. The photoinduced electrons could be easily transferred from CB of ZrO2 to the MoS2 cocatalyst, which facilitate effective charge separation and enhanced the photocatalytic degradation in the UV region. A photocatalytic mechanism is proposed. It is believed that the ZrO2/MoS2 hybrid structure has promise as a photocatalyst with low cost and high efficiency for photoreactions.

Atomic layer deposition and properties of ZrO2/Fe2O3 thin films

PubMed Central

Seemen, Helina; Ritslaid, Peeter; Rähn, Mihkel; Tamm, Aile; Kukli, Kaupo; Kasikov, Aarne; Link, Joosep; Stern, Raivo; Dueñas, Salvador; Castán, Helena; García, Héctor

2018-01-01

Thin solid films consisting of ZrO2 and Fe2O3 were grown by atomic layer deposition (ALD) at 400 °C. Metastable phases of ZrO2 were stabilized by Fe2O3 doping. The number of alternating ZrO2 and Fe2O3 deposition cycles were varied in order to achieve films with different cation ratios. The influence of annealing on the composition and structure of the thin films was investigated. Additionally, the influence of composition and structure on electrical and magnetic properties was studied. Several samples exhibited a measurable saturation magnetization and most of the samples exhibited a charge polarization. Both phenomena were observed in the sample with a Zr/Fe atomic ratio of 2.0. PMID:29441257

Abnormal Pressure-Induced Photoluminescence Enhancement and Phase Decomposition in Pyrochlore La2 Sn2 O7.

PubMed

Zhao, Yongsheng; Li, Nana; Xu, Cong; Li, Yan; Zhu, Hongyu; Zhu, Pinwen; Wang, Xin; Yang, Wenge

2017-09-01

La 2 Sn 2 O 7 is a transparent conducting oxide (TCO) material and shows a strong near-infrared fluorescent at ambient pressure and room temperature. By in situ high-pressure research, pressure-induced visible photoluminescence (PL) above 2 GPa near 2 eV is observed. The emergence of unusual visible PL behavior is associated with the seriously trigonal lattice distortion of the SnO 6 octehedra, under which the Sn-O1-Sn exchange angle θ is decreased below 22.1 GPa, thus enhancing the PL quantum yield leading to Sn 3 P 1 → 1 S 0 photons transition. Besides, bandgap closing followed by bandgap opening and the visible PL appearing at the point of the gap reversal, which is consistent with high-pressure phase decomposition, are discovered. The high-pressure PL results demonstrate a well-defined pressure window (7-17 GPa) with flat maximum PL yielding and sharp edges at both ends, which may provide a great calibration tool for pressure sensors for operation in the deep sea or at extreme conditions. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Labeling of HeLa cells using ZrO2:Yb3+-Er3+ nanoparticles with upconversion emission

NASA Astrophysics Data System (ADS)

Ceja-Fdez, Andrea; López-Luke, Tzarara; Oliva, Jorge; Vivero-Escoto, Juan; Gonzalez-Yebra, Ana Lilia; Rojas, Ruben A. Rodriguez; Martínez-Pérez, Andrea; de la Rosa, Elder

2015-04-01

This work reports the synthesis, structural characterization, and optical properties of ZrO2:Yb3+-Er3+ (2-1 mol%) nanocrystals. The nanoparticles were coated with 3-aminopropyl triethoxysilane (APTES) and further modified with biomolecules, such as Biotin-Anti-rabbit (mouse IgG) and rabbit antibody-AntiKi-67, through a conjugation method. The conjugation was successfully confirmed by Fourier transform infrared, zeta potential, and dynamic light scattering. The internalization of the conjugated nanoparticles in human cervical cancer (HeLa) cells was followed by two-photon confocal microscopy. The ZrO2:Yb3+-Er3+ nanocrystals exhibited strong red emission under 970-nm excitation. Moreover, the luminescence change due to the addition of APTES molecules and biomolecules on the nanocrystals was also studied. These results demonstrate that ZrO2:Yb3+-Er3+ nanocrystals can be successfully functionalized with biomolecules to develop platforms for biolabeling and bioimaging.

Disordered Route to the Coulomb Quantum Spin Liquid: Random Transverse Fields on Spin Ice in Pr 2 Zr 2 O 7

DOE PAGES

Wen, J. -J.; Koohpayeh, S. M.; Ross, K. A.; ...

2017-03-08

Inelastic neutron scattering reveals a broad continuum of excitations in Pr 2 Zr 2 O 7 , the temperature and magnetic field dependence of which indicate a continuous distribution of quenched transverse fields ( Δ ) acting on the non-Kramers Pr 3 + crystal field ground state doublets. Spin-ice correlations are apparent within 0.2 meV of the Zeeman energy. In a random phase approximation an excellent account of the data is provided and contains a transverse field distribution ρ ( Δ ) ∝ ( Δ 2 + Γ 2 ) - 1 , where Γ = 0.27 ( 1 )more » meV . Established during high temperature synthesis due to an underlying structural instability, it appears disorder in Pr 2 Zr 2 O 7 actually induces a quantum spin liquid.« less

[Preliminary study on DNA damage of ZrO(2)/LaPO(4) diphase ceramics on human peripheral blood lymphocytes in vitro].

PubMed

Zhu, Hui-fang; Chen, Li-ping; Zhang, Xiu-li; Zhang, Bao-wei

2009-06-01

To detect the genotoxicity of dental machinable ZrO(2)/LaPO(4) diphase ceramics on human peripheral blood lymphocytes in vitro. The evaluation of DNA damage on human lymphocytes was performed by comet assay for three groups of ZrO(2)/LaPO(4) diphase ceramics with 30wt% of LaPO(4) (with 3wt% and 5wt% of Y(2)O(3)) and 40wt% of LaPO(4) (with 5wt% of Y(2)O(3)). The results were analyzed with SPSS16.0 software package for one-factor ANOVA and LSD. Three experimental groups with different concentration of LaPO(4) of ZrO(2)/LaPO(4) diphase ceramics, the negative control of IPS Empress II ceramics and the blank behaved little migration of the DNA strands respectively after six-day test, and there was no significant difference in all the groups except the positive control (P>0.05). The study indicates little effect of DNA damage of ZrO(2)/LaPO(4) diphase ceramics.

Extremely dense microstructure and enhanced ionic conductivity in hot-isostatic pressing treated cubic garnet-type solid electrolyte of Ga2O3-doped Li7La3Zr2O12

NASA Astrophysics Data System (ADS)

Qin, Shiying; Zhu, Xiaohong; Jiang, Yue; Ling, Ming’En; Hu, Zhiwei; Zhu, Jiliang

A large number of pores and a low relative density that are frequently observed in solid electrolytes reduce severely their ionic conductivity and thus limit their applicability. Here, we report on the use of hot isostatic pressing (HIP) for ameliorating the garnet-type lithium-ion conducting solid electrolyte of Ga2O3-doped Li7La3Zr2O12 (Ga-LLZO) with nominal composition of Li6.55Ga0.15La3Zr2O12. The Ga-LLZO pellets were conventionally sintered at 1075∘C for 12h, and then were followed by HIP treatment at 120MPa and 1160∘C under an Ar atmosphere. It is found that the HIP-treated Ga-LLZO shows an extremely dense microstructure and a significantly enhanced ionic conductivity. Coherent with the increase in relative density from 90.5% (untreated) to 97.5% (HIP-treated), the ionic conductivity of the HIP-treated Ga-LLZO reaches as high as 1.13×10‑3S/cm at room temperature (25∘C), being two times higher than that of 4.58×10‑4S/cm for the untreated one.

Structural investigation of α-LaZr2F11 by coupling X-ray powder diffraction, 19F solid state NMR and DFT calculations

NASA Astrophysics Data System (ADS)

Martineau, Charlotte; Legein, Christophe; Body, Monique; Péron, Olivier; Boulard, Brigitte; Fayon, Franck

2013-03-01

α-LaZr2F11 has been synthesized by solid state reaction. Its crystal structure has been refined from X-ray powder diffraction data (space group no. 72 Ibam, a=7.785(1) Å, b=10.086(1) Å and c=11.102(1) Å). α-LaZr2F11 contains one La, one Zr and four F inequivalent crystallographic sites. F3 and F4 are shared between one ZrF73- polyhedron and one LaF85- polyhedron, while F1 and F2 bridge two ZrF73- polyhedra. 19F 1D MAS NMR spectra of α-LaZr2F11 are in agreement with the proposed structural model. Assignment of the 19F resonances to the corresponding crystallographic sites has been performed on the basis of both their relative intensities and their correlation patterns in a 19F 2D dipolar-based double-quantum recoupling MAS NMR spectrum. DFT calculations of the 19F chemical shielding tensors have been performed using the GIPAW method implemented in the NMR-CASTEP code, for the experimental structure and two PBE-DFT geometry optimized structures of α-LaZr2F11 (atomic position optimization and full geometry optimization with rescaling of the unit cell volume to the experimental value). Computations were done with and without using a modified La pseudopotential allowing the treatment of the 4f localized empty orbitals of La3+. A relatively nice agreement between the experimental 19F isotropic and anisotropic chemical shifts and the values calculated for the proposed structural model is obtained.

Effect of TiO2, ZrO2, and TiO2-ZrO2 on the performance of CuO-ZnO catalyst for CO2 hydrogenation to methanol

NASA Astrophysics Data System (ADS)

Xiao, Jie; Mao, Dongsen; Guo, Xiaoming; Yu, Jun

2015-05-01

The influence of TiO2, ZrO2, and TiO2-ZrO2 mixed oxide on the catalytic performance of CuO-ZnO catalyst in the methanol synthesis from CO2 hydrogenation was studied. The catalysts were prepared by oxalate co-precipitation method and characterized by TGA, N2 adsorption, XRD, reactive N2O adsorption, XPS, H2-TPR, H2-TPD, and CO2-TPD techniques. Characterization results reveal that all the additives improve the CuO dispersion in the catalyst body and increase the Cu surface area and adsorption capacities of CO2 and H2. The results of catalytic test reveal that the additives increase both the CO2 conversion and methanol selectivity, and TiO2-ZrO2 mixed oxide is more effective than single components of TiO2 or ZrO2. Moreover, the activity of methanol synthesis is correlated directly with CO2 adsorption capacity over the catalysts.

Effect of UV lamp irradiation during oxidation of Zr/Pt/Si structure on electrical properties of Pt/ZrO 2/Pt/Si structure

NASA Astrophysics Data System (ADS)

Bae, Joon Woo; Lim, Jae-Won; Mimura, Kouji; Uchikoshi, Masahito; Miyazaki, Takamichi; Isshiki, Minoru

2010-03-01

Metal-insulator-metal (MIM) capacitors were fabricated using ZrO 2 films and the effects of structural and native defects of the ZrO 2 films on the electrical and dielectric properties were investigated. For preparing ZrO 2 films, Zr films were deposited on Pt/Si substrates by ion beam deposition (IBD) system with/without substrate bias voltages and oxidized at 200 °C for 60 min under 0.1 MPa O 2 atmosphere with/without UV light irradiation ( λ = 193 nm, Deep UV lamp). The ZrO 2(˜12 nm) films on Pt(˜100 nm)/Si were characterized by X-ray diffraction pattern (XRD), field emission scanning electron microscopy (FE-SEM) and high-resolution transmission electron microscopy (HRTEM), capacitance-voltage ( C- V) and current-voltage ( I- V) measurements were carried out on MIM structures. ZrO 2 films, fabricated by oxidizing the Zr film deposited with substrate bias voltage under UV light irradiation, show the highest capacitance (784 pF) and the lowest leakage current density. The active oxygen species formed by UV irradiation are considered to play an important role in the reduction of the leakage current density, because they can reduce the density of oxygen vacancies.

CO Oxidation and Subsequent CO 2 Chemisorption on Alkaline Zirconates: Li 2 ZrO 3 and Na 2 ZrO 3

DOE Office of Scientific and Technical Information (OSTI.GOV)

Alcántar-Vázquez, Brenda; Duan, Yuhua; Pfeiffer, Heriberto

Here, two different alkaline zirconates (Li 2ZrO 3 and Na 2ZrO 3) were studied as possible bifunctional catalytic-captor materials for CO oxidation and the subsequent CO 2 chemisorption process. Initially, CO oxidation reactions were analyzed in a catalytic reactor coupled to a gas chromatograph, using Li 2ZrO 3 and Na 2ZrO 3, under different O 2 partial flows. We found results clearly showed that Na 2ZrO 3 possesses much better catalytic properties than Li 2ZrO 3. After the CO-O 2 oxidation catalytic analysis, CO2 chemisorption process was analyzed by thermogravimetric analysis, only for the Na 2ZrO 3 ceramic. The resultsmore » confirmed that Na 2ZrO 3 is able to work as a bifunctional material (CO oxidation and subsequent CO 2 chemisorption), although the kinetic CO 2 capture process was not the best one under the physicochemical condition used in this case. For Na 2ZrO 3, the best CO conversions were found between 445 and 580 °C (100%), while Li 2ZrO 3 only showed a 35% of efficiency between 460 and 503 °C. However, in the Na 2ZrO 3 case, at temperatures higher than 580 °C its catalytic activity gradually decreases as a result of CO 2 capture process. Finally, all these experiments were compared and supported with theoretical thermodynamic data.« less

CO Oxidation and Subsequent CO 2 Chemisorption on Alkaline Zirconates: Li 2 ZrO 3 and Na 2 ZrO 3

DOE PAGES

Alcántar-Vázquez, Brenda; Duan, Yuhua; Pfeiffer, Heriberto

2016-08-26

Here, two different alkaline zirconates (Li 2ZrO 3 and Na 2ZrO 3) were studied as possible bifunctional catalytic-captor materials for CO oxidation and the subsequent CO 2 chemisorption process. Initially, CO oxidation reactions were analyzed in a catalytic reactor coupled to a gas chromatograph, using Li 2ZrO 3 and Na 2ZrO 3, under different O 2 partial flows. We found results clearly showed that Na 2ZrO 3 possesses much better catalytic properties than Li 2ZrO 3. After the CO-O 2 oxidation catalytic analysis, CO2 chemisorption process was analyzed by thermogravimetric analysis, only for the Na 2ZrO 3 ceramic. The resultsmore » confirmed that Na 2ZrO 3 is able to work as a bifunctional material (CO oxidation and subsequent CO 2 chemisorption), although the kinetic CO 2 capture process was not the best one under the physicochemical condition used in this case. For Na 2ZrO 3, the best CO conversions were found between 445 and 580 °C (100%), while Li 2ZrO 3 only showed a 35% of efficiency between 460 and 503 °C. However, in the Na 2ZrO 3 case, at temperatures higher than 580 °C its catalytic activity gradually decreases as a result of CO 2 capture process. Finally, all these experiments were compared and supported with theoretical thermodynamic data.« less

Interaction of Au with thin ZrO2 films: influence of ZrO2 morphology on the adsorption and thermal stability of Au nanoparticles.

PubMed

Pan, Yonghe; Gao, Yan; Kong, Dandan; Wang, Guodong; Hou, Jianbo; Hu, Shanwei; Pan, Haibin; Zhu, Junfa

2012-04-10

The model catalysts of ZrO(2)-supported Au nanoparticles have been prepared by deposition of Au atoms onto the surfaces of thin ZrO(2) films with different morphologies. The adsorption and thermal stability of Au nanoparticles on thin ZrO(2) films have been investigated using synchrotron radiation photoemission spectroscopy (SRPES) and X-ray photoelectron spectroscopy (XPS). The thin ZrO(2) films were prepared by two different methods, giving rise to different morphologies. The first method utilized wet chemical impregnation to synthesize the thin ZrO(2) film through the procedure of first spin-coating a zirconium ethoxide (Zr(OC(2)H(5))(4)) precursor onto a SiO(2)/Si(100) substrate at room temperature followed by calcination at 773 K for 12 h. Scanning electron microscopy (SEM) investigations indicate that highly porous "sponge-like nanostructures" were obtained in this case. The second method was epitaxial growth of a ZrO(2)(111) film through vacuum evaporation of Zr metal onto Pt(111) in 1 × 10(-6) Torr of oxygen at 550 K followed by annealing at 1000 K. The structural analysis with low energy electron diffraction (LEED) of this film exhibits good long-range ordering. It has been found that Au forms smaller particles on the porous ZrO(2) film as compared to those on the ordered ZrO(2)(111) film at a given coverage. Thermal annealing experiments demonstrate that Au particles are more thermally stable on the porous ZrO(2) surface than on the ZrO(2)(111) surface, although on both surfaces, Au particles experience significant sintering at elevated temperatures. In addition, by annealing the surfaces to 1100 K, Au particles desorb completely from ZrO(2)(111) but not from porous ZrO(2). The enhanced thermal stability for Au on porous ZrO(2) can be attributed to the stronger interaction of the adsorbed Au with the defects and the hindered migration or coalescence resulting from the porous structures. © 2012 American Chemical Society

Aqueous Isolation of 17-Nuclear Zr-/Hf- Oxide Clusters during the Hydrothermal Synthesis of ZrO2/HfO2.

PubMed

Sung, Qing; Liu, Caiyun; Zhang, Guanyun; Zhang, Jian; Tung, Chen-Ho; Wang, Yifeng

2018-06-21

Novel 17-nuclear Zr-/Hf- oxide clusters ({Zr17} and {Hf17}) are isolated from aqueous systems. In the clusters, Zr/Hf ions are connected via μ3-O, μ3-OH and μ2-OH linkages into a pinwheel core which is wrapped with SO42-, HCOO- and aqua ligands. Octahedral hexanuclear Zr-/Hf- oxide clusters ({Zr6}oct and {Hf6}oct) are also isolated from the same hydrothermal system by decreasing the synthesis temperature. Structural analysis, synthetic conditions, vibrational spectra and ionic conductivity of the clusters are studied. Structural studies and synthesis inspection suggest that formation of {Zr6}oct and {Zr17} involves assembly of the same transferable building blocks, but the condensation degree and thermodynamic stability of the products increase with hydrothermal temperature. The role of {Zr6}oct and {Zr17} in the formation of ZrO2 nanocrystals are then discussed in the scenario of nonclassical nucleation theory. Besides, the Zr-oxide clusters exhibit ionic conductivity due to the mobility of protons. This study not only adds new members to the Zr-/Hf- oxide cluster family, but also establishes a connection from Zr4+ ions to ZrO2 in the hydrothermal preparation of zirconium oxide nanomaterials. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Pentavalent iridium pyrochlore C d2I r2O7 : A prototype material system for competing crystalline field and spin-orbit coupling

NASA Astrophysics Data System (ADS)

Dai, Jianhong; Yin, Yunyu; Wang, Xiao; Shen, Xudong; Liu, Zhehong; Ye, Xubin; Cheng, Jinguang; Jin, Changqing; Zhou, Guanghui; Hu, Zhiwei; Weng, Shihchang; Wan, Xiangang; Long, Youwen

2018-02-01

A new pyrochlore oxide C d2I r2O7 with an I r5 + charge state was prepared by high-pressure techniques. Although strong spin-orbit coupling (SOC) dominates the electronic states in most iridates so that a SOC-Mott state is proposed in S r2Ir O4 in the assumption of an undistorted Ir O6 octahedral crystalline field, the strongly distorted one in the current C d2I r2O7 exhibits a competing interaction with the SOC. Unexpected from a strong SOC limit, C d2I r2O7 deviates from a nonmagnetic and insulating J =0 ground state. It displays short-range ferromagnetic correlations and metallic electrical transport properties. First-principles calculations well reproduce the experimental observation, revealing the large mixture between the jeff=1 /2 and jeff=3 /2 bands near the Fermi surface due to the significant distortion of Ir O6 octahedra. This work sheds light on the critical role of a noncubic crystalline field in electronic properties which has been ignored in past studies of 5 d -electron systems.