Cattle waste products high in nitrogen (N) that enter waterways via rainfall runoff can contribute to aquatic ecosystem health deterioration. It is well established that N leaching from this source can be reduced by plant assimilation, e.g. pasture grass. Additionally, N leaching can be reduced when there is sufficient carbon (C) in the soil such as plant litterfall to stimulate microbial processes, i.e. denitrification, which off-gas N from the soil profile. However, the relative importance of these two processes is not well understood. A soil microcosm experiment was conducted to determine the role of biotic processes, pasture grass and microbial activity, and abiotic processes such as soil sorption, in reducing N leaching loss, during successive additions of bovine urine. Pasture grass was the most effective soil cover in reducing N leaching losses, which leached 70% less N compared to exposed soil. Successive application of urine to the soil resulted in N accumulation, after which there was a breaking point indicated by high N leaching losses. This is likely to be due to the low C:N ratio within the soil profiles treated with urine (molar ratio 8:1) compared to water treated soils (30:1). In this experiment we examined the role of C addition in reducing N losses and showed that the addition of glucose can temporarily reduce N leaching. Overall, our results demonstrated that plant uptake of N was a more important process in preventing N leaching than microbial processes. Copyright © 2016 Elsevier Ltd. All rights reserved.

Ultrasound augmented leaching of nickel sulfate in sulfuric acid and hydrogen peroxide media.

PubMed

Li, Haoyu; Li, Shiwei; Peng, Jinhui; Srinivasakannan, Chandrasekar; Zhang, Libo; Yin, Shaohua

2018-01-01

A new method of preparation high purity nickel sulfate assisted by ultrasonic was studied. The process mechanism was analyzed by Inductively Coupled Plasma (ICP), X-ray diffraction (XRD), Scanning electron microscopy (SEM), and Energy dispersive X-ray spectrometry (EDS).The reaction mechanisms of oxidizing leaching and ultrasonic leaching were explored, respectively. Results showed that ultrasonic treatment peel off the oxide film on the surface of nickel. The leachate under strongly agitated, the yield rate of nickel sulfate was accelerate. And the reaction area was increased by the cavitation effect, the liquid-solid reaction was promoted, and the activation energy was reduced. The leaching rate of nickel reached 46.29% by conventional leaching, which takes about 5h. Under the same conditions, the ultrasonic leaching rate reached 40%, only half of the conventional leaching time. Concentration of leaching agent, reaction temperature, ultrasonic power, leaching time had significant effect on the enhancement of the leaching reaction with ultrasonic radiation. The leaching rate of 60.41% under the optimum experiment conditions as follows: sulfuric acid concentration 30%, hydrogen peroxide 10%, leaching temperature 333K, ultrasonic power 200W and leaching time 4h. The kinetic study of the system was investigated, and the reaction rates of conventional leaching and ultrasonic leaching were controlled by diffusion, and the apparent activation energies were 16.2kJ/mol and 11.83kJ/mol. Copyright © 2017. Published by Elsevier B.V.

Catalytic effect of Ag⁺ on arsenic bioleaching from orpiment (As₂S₃) in batch tests with Acidithiobacillus ferrooxidans and Sulfobacillus sibiricus.

PubMed

Zhang, Guangji; Chao, Xingwu; Guo, Pei; Cao, Junya; Yang, Chao

2015-01-01

Orpiment is one of the major arsenic sulfide minerals which commonly occurs in the gold mine environment and the weathering of this mineral can lead to the contamination of arsenic. In this study, chemical leaching experiments using 10g/L Fe(3+) at 35°C and 50°C were carried out and the results show that orpiment can be leached by Fe(3+) and the leaching rate of orpiment was significantly enhanced in the presence of Ag(+). The bioleaching experiments with mesophilic bacteria Acidithiobacillus ferrooxidans and moderate thermophilic bacteria Sulfobacillus sibiricus were carried out, showing that these two strains can survive in the mineral pulp and oxidize Fe(2+) to regenerate Fe(3+). Based on above results, it is believed that the leaching action of the acidic mining drainage by some bacteria can lead to the release of arsenic from orpiment. Different performances of At. ferrooxidans and S. sibiricus in the tests suggest they follow two different mechanisms and this point of view is further confirmed based on analyses of the composition and morphology of the mineral residue by SEM and EDS. Copyright © 2014 Elsevier B.V. All rights reserved.

Dry deposition of sulfate to Quercus rubra and Liriodendron tulipifera foliage

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vandenberg, J.J.

1987-01-01

Estimates were made of the rate of dry deposition to red oak (Quercus rubra) and tulip poplar (Liriodendron tulipifera) foliage. In the laboratory, radioactive ammonium sulfate aerosols were generated in an exposure chamber. These aerosols were dry deposited onto leaves that were sequentially washed to examine the efficacy of washing procedures in removal of surface deposits. Over 90% of dry deposited sulfate was removed after a 30 second wash duration. Laboratory procedures also estimated the magnitude of foliar sulfur that leached into leaf wash solutions. The majority of laboratory leaves demonstrated no leaching of sulfur from the internal pool. However,more » some leaves showed significant sulfur leaching. It was concluded that leaching of internal sulfur was highly leaf specific. This indicated that each leaf used in field experiments needed to be individually examined for leaching.« less

Assessment of metal contaminations leaching out from recycling plastic bottles upon treatments.

PubMed

Cheng, Xiaoliang; Shi, Honglan; Adams, Craig D; Ma, Yinfa

2010-08-01

Heavy metal contaminants in environment, especially in drinking water, are always of great concern due to their health impact. Due to the use of heavy metals as catalysts during plastic syntheses, particularly antimony, human exposure to metal release from plastic bottles has been a serious concern in recent years. The aim and scope of this study were to assess metal contaminations leaching out from a series of recycling plastic bottles upon treatments. In this study, leaching concentrations of 16 metal elements were determined in 21 different types of plastic bottles from five commercial brands, which were made of recycling materials ranging from no. 1 to no. 7. Several sets of experiments were conducted to study the factors that could potentially affect the metal elements leaching from plastic bottles, which include cooling with frozen water, heating with boiling water, microwave, incubating with low-pH water, outdoor sunlight irradiation, and in-car storage. Heating and microwave can lead to a noticeable increase of antimony leaching relative to the controls in bottle samples A to G, and some even reached to a higher level than the maximum contamination level (MCL) of the US Environmental Protection Agency (USEPA) regulations. Incubation with low-pH water, outdoor sunlight irradiation, and in-car storage had no significant effect on antimony leaching relative to controls in bottle samples A to G, and the levels of antimony leaching detected were below 6 ppb which is the MCL of USEPA regulations. Cooling had almost no effect on antimony leaching based on our results. For the other interested 15 metal elements (Al, V, Cr, Mn, Co, Ni, Cu, As, Se, Mo, Ag, Cd, Ba, Tl, Pb), no significant leaching was detected or the level was far below the MCL of USEPA regulations in all bottle samples in this study. In addition, washing procedure did contribute to the antimony leaching concentration for polyethylene terephthalate (PET) bottles. The difference of antimony leaching concentration between washing procedure involved and no washing procedure involved (AC) was larger than zero for samples A to G. This interesting result showed that higher antimony concentration was detected in experiments with no washing procedures compared with those experiments with washing procedures. Our study results indicate that partial antimony leaching from PET bottles comes from contaminations on the surface of plastic during manufacturing process, while major antimony leaching comes from conditional changes. The results revealed that heating and microwaving enhance antimony leaching significantly in PET plastic bottles. Plastic bottle manufacturers should consider the contaminations during manufacturing process and washing bottles before first use was strongly recommended to remove those contaminants.

Effects of Simple Leaching of Crushed and Powdered Materials on High-precision Pb Isotope Analyses

NASA Astrophysics Data System (ADS)

Todd, E.; Stracke, A.

2013-12-01

We present new results of simple leaching experiments on the Pb isotope composition of USGS standard reference material powders and on ocean island basalt whole rock splits and powders. Rock samples were leached with 6N HCl in two steps, first hot and then in an ultrasonic bath, and washed with ultrapure H2O before conventional sample digestion and chromatographic purification of Pb. Pb isotope analyses were determined with Tl-doped MC-ICP-MS. Intra- and inter-session analytical reproducibility of repeated analyses of both synthetic Pb solutions and Pb from single digests of chemically processed natural samples were generally < 100 ppm (2 S.D.). The comparison of leached and unleached samples shows that leaching reliably removes variable amounts of different contaminants for different starting materials. For repeated digests of a single sample, the leached samples reproduce better than the unleached ones, showing that leaching effectively removes heterogeneously distributed extraneous Pb. However, the reproducibility of repeated digests of variably contaminated natural samples is up to an order of magnitude worse than the analytical reproducibility of ca. 100 ppm. More complex leaching methods (e.g., Nobre Silva et al., 2009) yield Pb isotope ratios within error of and with similar reproducibility to our method, showing that the simple leaching method is reliable. The remaining Pb isotope heterogeneity of natural samples, which typically exceeds 100 ppm, is thus attributed to inherent isotopic sample heterogeneity. Tl-doped MC-ICP-MS Pb ratio determination is therefore a sufficiently precise method for Pb isotope analyses in natural rocks. More precise Pb double- or triple-spike methods (e.g., Galer, 1999; Thirlwall, 2000), may exploit their full potential only in cases where natural isotopic sample heterogeneity is demonstrably negligible. References: Galer, S., 1999, Chem. Geol. 157, 255-274. Nobre Silva, et al. 2009, Geochemistry Geophysics Geosystems 10, Q08012. Thirlwall, M.F., 2000, Chem. Geol. 163, 299-322.

Extraction of magnesium from calcined dolomite ore using hydrochloric acid leaching

NASA Astrophysics Data System (ADS)

Royani, Ahmad; Sulistiyono, Eko; Prasetiyo, Agus Budi; Subagja, Rudi

2018-05-01

Magnesium is widely used in varieties industrial sector. Dolomite is one source of magnesium besides seawater. The extraction of magnesium from dolomite ores can be done by leaching process. In this work, the dolomite leaching to extract magnesium by hydrochloric acid was investigated. The leaching experiments were performed in a spherical glass batch reactor having a capacity of 1000 ml. The effects of the stirring speed, acid concentration, reaction temperature and liquid-solid ratio for each reaction time of 1; 2; and 3 h on the Mg leaching have been evaluated. 5 ml of solution sample were collected from the leached solutions, then it was filtered prior to analysis by ICP OES. The experimental results show that the magnesium extraction increases along with the increase of acid concentration, liquid-solid ratio and temperature. The optimum conditions for magnesium extraction were achieved at temperature 75 °C, extraction time 3 h, the HCl concentration of 2 M, the liquid-solid ratio 20 ml/g and stirring speed of 400 rpm. At this condition 98, 82 % of magnesium were extracted from dolomite. The conclusion obtained from this leaching process is that the magnesium can be extracted from dolomite by using hydrochloric acid solutions.

Leaching variations of heavy metals in chelator-assisted phytoextraction by Zea mays L. exposed to acid rainfall.

PubMed

Lu, Yayin; Luo, Dinggui; Liu, Lirong; Tan, Zicong; Lai, An; Liu, Guowei; Li, Junhui; Long, Jianyou; Huang, Xuexia; Chen, Yongheng

2017-11-01

Chelant-enhanced phytoextraction method has been put forward as an effective soil remediation method, whereas the heavy metal leaching could not be ignored. In this study, a cropping-leaching experiment, using soil columns, was applied to study the metal leaching variations during assisted phytoextraction of Cd- and Pb-polluted soils, using seedlings of Zea mays, applying three different chelators (EDTA, EDDS, and rhamnolipid), and artificial rainfall (acid rainfall or normal rainfall). It showed that artificial rainfall, especially artificial acid rain, after chelator application led to the increase of heavy metals in the leaching solution. EDTA increased both Cd and Pb concentrations in the leaching solution, obviously, whereas EDDS and rhamnolipid increased Cd concentration but not Pb. The amount of Cd and Pb decreased as the leaching solution increased, the patterns as well matched LRMs (linear regression models), with R-square (R 2 ) higher than 90 and 82% for Cd and Pb, respectively. The maximum cumulative Cd and Pb in the leaching solutions were 18.44 and 16.68%, respectively, which was amended by EDTA and acid rainwater (pH 4.5), and followed by EDDS (pH 4.5), EDDS (pH 6.5), rhamnolipid (0.5 g kg -1 soil, pH 4.5), and rhamnolipid (pH 6.5).

Leaching composted lignocellulosic wastes to prepare container media: feasibility and environmental concerns.

PubMed

Fornes, Fernando; Carrión, Carolina; García-de-la-Fuente, Rosana; Puchades, Rosa; Abad, Manuel

2010-08-01

The leaching of salt and mineral elements from three composts prepared with residual vegetable crop biomass (melon, pepper or zucchini) was studied using methacrylate columns and distilled water. The benefits of the leached composts to be used for ornamental potted plant production were also analysed. After leaching 5 container capacities of effluent, both the electrical conductivity and the concentration of soluble mineral elements in compost leachates decreased substantially and remained close to the target levels. Composts reacted differently to leaching due to differences in the raw waste sources and the composting process and hence, in their physical and chemical characteristics. At the end of the experiment, after pouring 8 container capacities of water, the leaching efficiency of the salts was 96%, 93% and 87% for melon, pepper and zucchini-based composts, respectively. Mineral elements differed in their ability to be removed from the composts; N (NH(4)(+) and NO(3)(-)), K(+), Na(+), Cl(-), and SO(4)(2-) were leached readily, whereas H(2)PO(4)(-), Ca(2+), and Mg(2+) were removed hardly. Leached composts showed a range of physico-chemical and chemical characteristics suitable for use as growing media constituents. Potted Calendula and Calceolaria plants grew in the substrates prepared with the leached composts better than in those made with the non-leached ones. Finally, special emphasis must be paid to the management of the effluents produced under commercial conditions to avoid environmental pollution. Copyright 2010 Elsevier Ltd. All rights reserved.

Leaching Characteristics of Calcium and Strontium from Phosphogypsum Under Acid Rain.

PubMed

Wang, Mei; Luo, Houqiao; Chen, Yong; Yang, Jinyan

2018-02-01

Phosphogypsum (PG) stored close to phosphorus chemical plants has caused worldwide environmental problems. Column leaching experiments were conducted to evaluate Ca and Sr leaching from PG under simulated acid rain at pH levels typical for rain in the study region (Shifang, China). High concentrations of Ca and Sr in leachates in the first five leaching events could pollute the soil and groundwater around the PG. Leachates pH was lower than and had no correlation with simulated rain pH. No correlations between simulated rain pH and cumulative Ca and Sr content in leachates were noted. Around 2.0%-2.2% of Ca and 0.5%-0.6% of Sr were leached out from PG by the simulated summer rainfall in Shifang. Electrical conductivity values, Ca and Sr concentrations at bottom sections of PG columns were higher than those of top sections, while pH values showed a reverse trend. More precautions should be taken to protect the environment around PG stacks.

Biocide leaching during field experiments on treated articles.

PubMed

Schoknecht, Ute; Mathies, Helena; Wegner, Robby

2016-01-01

Biocidal products can be sources of active substances in surface waters caused by weathering of treated articles. Marketing and use of biocidal products can be limited according to the European Biocidal Products Regulation if unacceptable risks to the environment are expected. Leaching of active substances from treated articles was observed in field experiments to obtain information on leaching processes and investigate the suitability of a proposed test method. Leaching under weathering conditions proceeds discontinuously and tends to decrease with duration of exposure. It does not only mainly depend on the availability of water but is also controlled by transport processes within the materials and stability of the observed substances. Runoff amount proved to be a suitable basis to compare results from different experiments. Concentrations of substances are higher in runoff collected from vertical surfaces compared to horizontal ones, whereas the leached amounts per surface area are higher from horizontal surfaces. Gaps in mass balances indicate that additional processes such as degradation and evaporation may be relevant to the fate of active substances in treated articles. Leached amounts of substances were considerably higher when the materials were exposed to intermittent water contact under laboratory conditions as compared to weathering of vertically exposed surfaces. Experiences from the field experiments were used to define parameters of a procedure that is now provided to fulfil the requirements of the Biocidal Products Regulation. The experiments confirmed that the amount of water which is in contact with exposed surfaces is the crucial parameter determining leaching of substances.

The use of NTA for lead phytoextraction from soil from a battery recycling site.

PubMed

Freitas, Eriberto Vagner de Souza; do Nascimento, Clístenes Williams Araújo

2009-11-15

The application of synthetic aminopolycarboxylic acids to soil increases metal solubility, and therefore enhances phytoextraction. However, synthetic chelants degrade poorly in soil, and metal leaching threatens human and animal health. The aim of this study is to assess the use of a biodegradable chelant (NTA) for Pb phytoextraction from a soil contaminated by battery-casing disposal. EDTA was also included in the experiment to assess the behavior of a non-degradable chelant. Each synthetic chelant was applied to soil pots cultivated with maize plants at rates of 0, 2, 5, 10, and 20 mmol kg(-1). Soil samples were extracted with CaCl(2) and by sequential extraction for Pb. In addition, a soil column experiment was set up to study the leaching of Pb from the chelant-amended soil. The results showed that both NTA and EDTA were highly effective in solubilizing Pb from soil. The Pb distribution into soil fractions after chelant addition followed the sequence: Ex (exchangeable)>OM (organic matter)>AFeOx (amorphous iron oxides)>CFeOx (crystalline iron oxides). The 5 mmol kg(-1) dose of EDTA increased the Pb concentration in maize shoots to 1.1%, but it promoted unacceptable Pb leaching rates. On the other hand, the results showed that phytoremediating the site using 5 mmol kg(-1) NTA could be feasible with no environmental effects due to Pb leaching over a five-year period.

Improving ammonium and nitrate release from urea using clinoptilolite zeolite and compost produced from agricultural wastes.

PubMed

Omar, Latifah; Ahmed, Osumanu Haruna; Ab Majid, Nik Muhamad

2015-01-01

Improper use of urea may cause environmental pollution through NH3 volatilization and NO3 (-) leaching from urea. Clinoptilolite zeolite and compost could be used to control N loss from urea by controlling NH4 (+) and NO3 (-) release from urea. Soil incubation and leaching experiments were conducted to determine the effects of clinoptilolite zeolite and compost on controlling NH4 (+) and NO3 (-) losses from urea. Bekenu Series soil (Typic Paleudults) was incubated for 30, 60, and 90 days. A soil leaching experiment was conducted for 30 days. Urea amended with clinoptilolite zeolite and compost significantly reduced NH4 (+) and NO3 (-) release from urea (soil incubation study) compared with urea alone, thus reducing leaching of these ions. Ammonium and NO3 (-) leaching losses during the 30 days of the leaching experiment were highest in urea alone compared with urea with clinoptilolite zeolite and compost treatments. At 30 days of the leaching experiment, NH4 (+) retention in soil with urea amended with clinoptilolite zeolite and compost was better than that with urea alone. These observations were because of the high pH, CEC, and other chemical properties of clinoptilolite zeolite and compost. Urea can be amended with clinoptilolite zeolite and compost to improve NH4 (+) and NO3 (-) release from urea.

Leaching Process Investigation of Secondary Aluminum Dross: The Effect of CO2 on Leaching Process of Salt Cake from Aluminum Remelting Process

NASA Astrophysics Data System (ADS)

Li, Peng; Guo, Min; Zhang, Mei; Teng, Lidong; Seetharaman, Seshadri

2012-10-01

For the recycling/disposal of aluminum dross/salt cake from aluminum remelting, aqueous leaching offers an interesting economic process route. One major obstacle is the reaction between the AlN present in the dross and the aqueous phase, which can lead to the emission of NH3 gas, posing a serious environmental problem. In the current work, a leaching process using CO2-saturated water is attempted with a view to absorb the ammonia formed in situ. The current results show that at a solid-to-liquid ratio of 1:20 and 3 hours at 291 K (18 °C), the extraction of Na and K from the dross could be kept as high as 95.6 pct and 95.9 pct respectively. At the same time, with continuous CO2 bubbling, the mass of escaping NH3 gas decreased from 0.25 mg in pure water down to <0.006 mg, indicating effective absorption of ammonia by carbonized water. Furthermore, the results in the case of the leaching experiments with synthetic AlN show that the introduction of CO2 causes hindrance to the hydrolysis of AlN. The plausible mechanisms for the observed phenomena are discussed. The concept of the leaching of the salt cake by carbonated water and the consequent retention of AlN in the leach residue opens up a promising route toward an environment-friendly recycling process for the salt cake viz. recovery of the salts, utilization of CO2, and further processing of the dross residue, toward the synthesis of AlON from the leach residues.

Phosphorus vertical migration in aquic brown soil and light chernozem under different phosphorous application rate: a soil column leaching experiment.

PubMed

Zhao, Muqiu; Chen, Xin; Shi, Yi; Zhou, Quanlai; Lu, Caiyan

2009-01-01

A soil column leaching experiment was conducted to study the vertical migration of phosphorus in aquic brown soil and light chernozem under different phosphorus fertilization rates. The results showed that total dissolved phosphorus concentration in the leachates from the two soils was nearly the same, but dissolved inorganic phosphorus concentration was obviously different. In all fertilization treatments, aquic brown soil had a higher content of phosphorus in calcium chloride extracts compared with light chernozem. But Olsen phosphorus content was higher at the soil depth beneath 0-20 cm, and increased with increasing phosphorus application rate.

A long-term static immersion experiment on the leaching behavior of heavy metals from waste printed circuit boards.

PubMed

Zhao, Guo-Hua; Luo, Xing-Zhang; Chen, Gui; Zhao, Yong-Jun

2014-08-01

Printed circuit boards (PCBs) are the main components of electrical and electronic equipment (EEE). Waste PCBs contain several kinds of heavy metals, including Cu, Pb and Zn. We characterize the leaching of heavy metals (Cu, Pb, Zn and Ni) from waste PCBs in a pH range of 3.0 to 5.6 using a novel approach based on batch pH-static leaching experiments in this work. The results indicate that the leaching behavior of Cu, Pb, Zn and Ni is strongly dependent on pH. Leaching behavior also varies with different pH values and leaching times. The maximum concentrations of Cu, Pb, Zn and Ni in leachate from waste PCBs were 335.00, 17.57, 2.40 and 2.33 mg L(-1), respectively. The highest Pb, Ni, and Cu concentrations leached significantly exceeded the European Union waste-acceptance limit values with respect to inert waste landfills. The leaching of metals follows the shrinking core model with surface reaction control.

Reducing the Use of Agrochemicals: A Simple Experiment

ERIC Educational Resources Information Center

Vidal, M. M.; Filipe, Olga M. S.; Costa, M. C. Cruz

2006-01-01

An experiment was performed on polymeric-based controlled-release agrochemicals that minimize leaching into groundwater while maintaining an adequate quantity for the desired agrochemical benefits. Gelatin gel containing inorganic Phosphorous provides controlled-release of an agrochemical where release curves show a linear relationship between…

Microcosm experiments approach to quantify nitrogen leaching from mineral and organic fertilized soil

NASA Astrophysics Data System (ADS)

Severus Sandor, Mignon; Sandor, Valentina; Mihai Onica, Bogdan; Brad, Traian

2017-04-01

The use of nitrogen inputs to improve agricultural soils fertility is a common practice in arable lands. Depending of nitrogen forms only a part of introduced nitrogen will be effectively used by the crops while another part can be leached from soil with negative impact on the environment. In temperate climate these losses are greater during spring time when rains are frequent and crop plants are in the early growth stage. In a microcosm experiments we simulated this kind of conditions in order to assess nitrogen losses from two different soils (Chernozem, Luvisol) fertilized with mineral (ammonium nitrate) and organic (mustard as green manure, slurry manure and cattle manure) fertilizers. From each microcosms we obtained 100 ml of leachate which was filtered and analyzed from N-NO3 and N-NH4. The leachate was obtained by adding distillate water at the microcosm surface two times during the experiment at a ten days interval. Preliminary results showed that only small quantity of ammonium was leached from fertilized soils, mainly after 20 days of incubation. These amounts were higher in Chernozem soil than in Luvisol and registered the highest amount in cattle manure fertilized soils. In general, the nitrate was leached from soils in high quantities. The highest value was measured in Chernozem soil when cattle manure was used as fertilizer (1200 mg/l) and represents a cumulative amount. For most of the treatments the cumulative loss of nitrate nitrogen was double in Chernozem soil than in Luvisol. The highest quantity of leaching nitrate was measured for both soils in manure fertilized soil.

Impact of chemical leaching on permeability and cadmium removal from fine-grained soils.

PubMed

Lin, Zhongbing; Zhang, Renduo; Huang, Shuang; Wang, Kang

2017-08-01

The aim of this study was to investigate the influence of chemical leaching on permeability and Cd removal from fine-grained polluted soils. Column leaching experiments were conducted using two types of soils (i.e., artificially Cd-polluted loam and historically polluted silty loam). Chemical agents of CaCl 2 , FeCl 3 , citric acid, EDTA, rhamnolipid, and deionized water were used to leach Cd from the soils. Results showed that organic agents reduced permeability of both soils, and FeCl 3 reduced permeability of loam soil, compared with inorganic agents and deionized water. Entrapment and deposition of colloids generated from the organic agents and FeCl 3 treatments reduced the soil permeability. The peak Cd effluence from the artificially polluted loam columns was retarded. For the artificially polluted soils treated with EDTA and the historically polluted soils with FeCl 3 , Cd precipitates were observed at the bottom after chemical leaching. When Cd was associated with large colloid particles, the reduction of soil permeability caused Cd accumulation in deeper soil. In addition, the slow process of disintegration of soil clay during chemical leaching might result in the retardation of peak Cd effluence. These results suggest the need for caution when using chemical-leaching agents for Cd removal in fine-grained soils.

Metal removal from Municipal Solid Waste Incineration fly ash: A comparison between chemical leaching and bioleaching.

PubMed

Funari, V; Mäkinen, J; Salminen, J; Braga, R; Dinelli, E; Revitzer, H

2017-02-01

Bio- and hydrometallurgical experimental setups at 2-l reactor scale for the processing of fly ash from municipal waste incinerators were explored. We aimed to compare chemical H 2 SO 4 leaching and bioleaching; the latter involved the use of H 2 SO 4 and a mixed culture of acidophilic bacteria. The leaching yields of several elements, including some of those considered as critical (Mg, Co, Ce, Cr, Ga, Nb, Nd, Sb and Sm), are provided. At the end of the experiments, both leaching methods resulted in comparable yields for Mg and Zn (>90%), Al and Mn (>85%), Cr (∼65%), Ga (∼60%), and Ce (∼50%). Chemical leaching showed the best yields for Cu (95%), Fe (91%), and Ni (93%), whereas bioleaching was effective for Nd (76%), Pb (59%), and Co (55%). The two leaching methods generated solids of different quality with respect to the original material as we removed and significantly reduced the metals amounts, and enriched solutions where metals can be recovered for example as mixed salts for further treatment. Compared to chemical leaching the bioleaching halved the use of H 2 SO 4 , i.e., a part of agent costs, as a likely consequence of bio-produced acid and improved metal solubility. Copyright © 2016 Elsevier Ltd. All rights reserved.

Pollution attenuation by soils receiving cattle slurry after passage of a slurry-like feed solution. Column experiments.

PubMed

Núñez-Delgado, Avelino; López-Períago, Eugenio; Diaz-Fierros-Viqueira, Francisco

2002-09-01

Designing soil filtration systems or vegetated filter strips as a means of attenuating water pollution should take into account soil purging capacity. Here we report data on laboratory column trials used to investigate the capacity of a Hortic Anthrosol to attenuate contamination due to downward leaching from cattle slurry applied at the surface. The columns comprised 900 g of soil to a depth of about 20-25 cm, and had been used previously in an experiment involving passage of at least 5 pore volumes of an ion-containing cattle slurry-like feed solution. For the present experiments, the columns were first washed through with distilled water (simulating resting and rain falling after passage of the feed solution), and then received a single slurry dose equivalent to about 300 m3 ha(-1). The columns were then leached with distilled water, with monitoring of chemical oxygen demand (COD) and ion contents in outflow. The results indicated that the pollution-neutralising capacity of the soil was still high but clearly lower than in the earlier experiments with the feed solution. Furthermore, the time-course of COD showed that organic acids were leached through the column even more rapidly than chloride (often viewed as an inert tracer) enhancing the risk of heavy metals leaching and subsequent water pollution. Resting and alternate use of different soil-plant buffer zones would increase the lifespan of purging systems that use soil like the here studied one.

Effects of bioleaching on the mechanical and chemical properties of waste rocks

NASA Astrophysics Data System (ADS)

Yin, Sheng-Hua; Wu, Ai-Xiang; Wang, Shao-Yong; Ai, Chun-Ming

2012-01-01

Bioleaching processes cause dramatic changes in the mechanical and chemical properties of waste rocks, and play an important role in metal recovery and dump stability. This study focused on the characteristics of waste rocks subjected to bioleaching. A series of experiments were conducted to investigate the evolution of rock properties during the bioleaching process. Mechanical behaviors of the leached waste rocks, such as failure patterns, normal stress, shear strength, and cohesion were determined through mechanical tests. The results of SEM imaging show considerable differences in the surface morphology of leached rocks located at different parts of the dump. The mineralogical content of the leached rocks reflects the extent of dissolution and precipitation during bioleaching. The dump porosity and rock size change under the effect of dissolution, precipitation, and clay transportation. The particle size of the leached rocks decreased due to the loss of rock integrity and the conversion of dry precipitation into fine particles.

Using mixture design of experiments to assess the environmental impact of clay-based structural ceramics containing foundry wastes.

PubMed

Coronado, M; Segadães, A M; Andrés, A

2015-12-15

This work describes the leaching behavior of potentially hazardous metals from three different clay-based industrial ceramic products (wall bricks, roof tiles, and face bricks) containing foundry sand dust and Waelz slag as alternative raw materials. For each product, ten mixtures were defined by mixture design of experiments and the leaching of As, Ba, Cd, Cr, Cu, Mo, Ni, Pb, and Zn was evaluated in pressed specimens fired simulating the three industrial ceramic processes. The results showed that, despite the chemical, mineralogical and processing differences, only chrome and molybdenum were not fully immobilized during ceramic processing. Their leaching was modeled as polynomial equations, functions of the raw materials contents, and plotted as response surfaces. This brought to evidence that Cr and Mo leaching from the fired products is not only dependent on the corresponding contents and the basicity of the initial mixtures, but is also clearly related with the mineralogical composition of the fired products, namely the amount of the glassy phase, which depends on both the major oxides contents and the firing temperature. Copyright © 2015 Elsevier B.V. All rights reserved.

Occurrence, leaching, and degradation of Cry1Ab protein from transgenic maize detritus in agricultural streams

DOE PAGES

Griffiths, Natalie A.; Tank, Jennifer L.; Royer, Todd V.; ...

2017-03-15

The insecticidal Cry1Ab protein expressed by transgenic (Bt) maize can enter adjacent water bodies via multiple pathways, but its fate in stream ecosystems is not as well studied as in terrestrial systems. In this study, we used a combination of field sampling and laboratory experiments to examine the occurrence, leaching, and degradation of soluble Cry1Ab protein derived from Bt maize in agricultural streams. We surveyed 11 agricultural streams in northwestern Indiana, USA, on 6 dates that encompassed the growing season, crop harvest, and snowmelt/spring flooding, and detected Cry1Ab protein in the water column and in flowing subsurface tile drains atmore » concentrations of 3–60 ng/L. In a series of laboratory experiments, submerged Bt maize leaves leached Cry1Ab into stream water with 1% of the protein remaining in leaves after 70 d. Laboratory experiments suggested that dissolved Cry1Ab protein degraded rapidly in microcosms containing water-column microorganisms, and light did not enhance breakdown by stimulating assimilatory uptake of the protein by autotrophs. Here, the common detection of Cry1Ab protein in streams sampled across an agricultural landscape, combined with laboratory studies showing rapid leaching and degradation, suggests that Cry1Ab may be pseudo-persistent at the watershed scale due to the multiple input pathways from the surrounding terrestrial environment.« less

Occurrence, leaching, and degradation of Cry1Ab protein from transgenic maize detritus in agricultural streams

DOE Office of Scientific and Technical Information (OSTI.GOV)

Griffiths, Natalie A.; Tank, Jennifer L.; Royer, Todd V.

The insecticidal Cry1Ab protein expressed by transgenic (Bt) maize can enter adjacent water bodies via multiple pathways, but its fate in stream ecosystems is not as well studied as in terrestrial systems. In this study, we used a combination of field sampling and laboratory experiments to examine the occurrence, leaching, and degradation of soluble Cry1Ab protein derived from Bt maize in agricultural streams. We surveyed 11 agricultural streams in northwestern Indiana, USA, on 6 dates that encompassed the growing season, crop harvest, and snowmelt/spring flooding, and detected Cry1Ab protein in the water column and in flowing subsurface tile drains atmore » concentrations of 3–60 ng/L. In a series of laboratory experiments, submerged Bt maize leaves leached Cry1Ab into stream water with 1% of the protein remaining in leaves after 70 d. Laboratory experiments suggested that dissolved Cry1Ab protein degraded rapidly in microcosms containing water-column microorganisms, and light did not enhance breakdown by stimulating assimilatory uptake of the protein by autotrophs. Here, the common detection of Cry1Ab protein in streams sampled across an agricultural landscape, combined with laboratory studies showing rapid leaching and degradation, suggests that Cry1Ab may be pseudo-persistent at the watershed scale due to the multiple input pathways from the surrounding terrestrial environment.« less

Improving Ammonium and Nitrate Release from Urea Using Clinoptilolite Zeolite and Compost Produced from Agricultural Wastes

PubMed Central

Omar, Latifah; Ahmed, Osumanu Haruna; Majid, Nik Muhamad Ab.

2015-01-01

Improper use of urea may cause environmental pollution through NH3 volatilization and NO3 − leaching from urea. Clinoptilolite zeolite and compost could be used to control N loss from urea by controlling NH4 + and NO3 − release from urea. Soil incubation and leaching experiments were conducted to determine the effects of clinoptilolite zeolite and compost on controlling NH4 + and NO3 − losses from urea. Bekenu Series soil (Typic Paleudults) was incubated for 30, 60, and 90 days. A soil leaching experiment was conducted for 30 days. Urea amended with clinoptilolite zeolite and compost significantly reduced NH4 + and NO3 − release from urea (soil incubation study) compared with urea alone, thus reducing leaching of these ions. Ammonium and NO3 − leaching losses during the 30 days of the leaching experiment were highest in urea alone compared with urea with clinoptilolite zeolite and compost treatments. At 30 days of the leaching experiment, NH4 + retention in soil with urea amended with clinoptilolite zeolite and compost was better than that with urea alone. These observations were because of the high pH, CEC, and other chemical properties of clinoptilolite zeolite and compost. Urea can be amended with clinoptilolite zeolite and compost to improve NH4 + and NO3 − release from urea. PMID:25793220

Microfluidic Platform for High-throughput Screening of Leach Chemistry.

PubMed

Yang, Die; Priest, Craig

2018-06-20

We demonstrate an optofluidic screening platform for studying thiosulfate leaching of Au in a transparent microchannel. The approach permits in situ (optical) monitoring of Au thickness, reduced reagent use, rapid optimization of reagent chem-istry, screening of temperature, and determination of the activation energy. The results demonstrate the critical importance of the (1) preparation and storage of the leach solution, (2) deposition and annealing of the Au film, and (3) lixiviant chem-istry. The density of sputter deposited Au films decreased with depth resulting in accelerating leach rates during experiments. Atomic leach rates were determined and were constant throughout each experiment. Annealing above 270 °C was found to prevent leaching, which can be attributed to diffusion of the chromium adhesion layer into the Au film. The optofluidic analysis revealed leach rates that are sensitive to the stoichiometric ratio of thiosulphate, ammonia and copper in the leach solution, and optimized for 10 mM CuSO 4 , 1 M Na 2 S 2 O 3 and 1 M NH 4 OH. The temperature dependence of the leach rate gave an apparent activation energy of ~ 40 kJ.mol -1 , based on Arrhenius' relationship.

Effects of radiation on the leach rates of vitrified radioactive waste

NASA Astrophysics Data System (ADS)

Burns, W. G.; Hughes, A. E.; Marples, J. A. C.; Nelson, R. S.; Stoneham, A. M.

1982-06-01

This report reviews the possible effects of both radiation damage to the glass and of radiolysis of the leachant on the leaching behaviour of vitrified radioactive waste. It has been stimulated particularly by recent papers, which have suggested that the leach rates of glasses will be enhanced by large factors after a 'critical' dose of radiation from alpha decays. These experiments have been conducted at highly accelerated rates using ion beams. The relationship between these experiments and the situation in vitrified waste has been assessed, taking into account the fact that experiments using alpha emitters incorporated in the glass have failed to find significantly enhanced leach rates after doses about five times larger than those equivalent to this 'critical' dose. It is concluded that these differences are observed partly because the ion beam experiments are carried out at such high dose rates that some recovery effects important at lower rates do not come into play. In the case of experiments with 2 keV argon ions, surface effects other than genuine radiation damage must be taken into account. In practice, if water has penetrated the canister, vitrified waste will be irradiated in the presence of the leaching solution. Enhancements of the leach rate due to the transient effects of radiation in the solid are shown to be completely negligible. The effects of radiolysis of the leaching solution and of any air in contact with the solution have also been considered in some detail and related to recent experiments by McVay and Pederson. It is shown that these radiolysis effects will not lead to any situations requiring special precautions in practice, although changes in surface leach rate by small factors can be expected under some circumstances. Any effect of irradiation on leach rates must be seen in the context of a waste repository. Along with other studies we hold the view that the rate of loss of material will be limited by the access of water to the repository, and will therefore depend on the effective saturation solubility of the glass in the leachant, not on the leach rate as usually determined in laboratory tests. Radiation damage is not expected to change the saturation solubility by more than a factor of two or three.

Aging of vitrified wastes: An experimental and analogical approach

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sterpenich, J.; Forestier, L. Le; Libourel, G.

1995-12-31

In order to tackle the problems of the longevity of vitrified wastes, the authors used two complementary approaches: an analogical approach to examine the leaching processes of vitreous matrices as a function of time and to evaluate the longevity of vitrified wastes, and an experimental approach based on leaching experiments which allowed the determination of the rate and the kinetics of release of each element under well known conditions. Despite the very different durations of alteration, around 1,000 years for the medieval stained glasses and several weeks for leaching experiments, the authors show that the results obtained in laboratory andmore » under natural conditions are comparable. Thus, studies of medieval stained glasses allow prediction of the alteration of vitreous matrices and in particular, of vitrified wastes, and can be used to determine the rates and kinetics of release of pollutants. Medieval stained glasses furnish an excellent model for understanding the aging of vitrified wastes over time periods of up to a thousand years.« less

Mechanistic study of lead desorption during the leaching process of ion-absorbed rare earths: pH effect and the column experiment

NASA Astrophysics Data System (ADS)

Xue, Q.; Tang, J., Sr.; Chen, H.

2017-12-01

High concentrations of ammonium sulfate, often used in the in-situ mining process, can result in a decrease of pH in the environment and dissolution of rare earth metals. Ammonium sulfate can also cause desorption of toxic heavy metals, leading to environmental and human health implications. In this study, the desorption behavior and fraction changes of lead in the ion-absorbed rare earth ore were studied using batch desorption experiments and column leaching tests. Results from batch desorption experiments showed that the desorption process of lead included fast and slow stages, and followed an Elovich model well. The desorption rate and the proportion of lead content in the solution to the total lead in the soil were observed to increase with a decrease in the initial pH of the ammonium sulfate solution. The lead in soil included an acid extractable fraction, reducible fraction, oxidizable fraction, and a residual fraction, with the predominant fractions being the reducible and acid extractable fractions. 96% of the extractable fraction in soil were desorbed into solution at pH=3.0, and the content of the reducible fraction was observed to initially increase (when pH>4.0) and then decrease (when pH<4.0) with a decrease in pH. Column leaching tests indicated that the content of lead in the different fractions of soil followed the trend of reducible fraction > oxidizable fraction > acid extractable fraction > residual fraction after the simulating leaching mining process. The change in pH was also found to have a larger influence on the acid extractable and reducible fractions than the other two fractions. The proportion of the extractable fraction being leached was ca. 86%, and the reducible fraction was enriched along the migration direction of the leaching liquid. These results suggest that certain lead fractions may desorb again and contaminate the environment via acid rain, which provides significant information for environmental assessment and remediation after mining process.

The potential of oceanic transport and onshore leaching of additive-derived lead by marine macro-plastic debris.

PubMed

Nakashima, Etsuko; Isobe, Atsuhiko; Kako, Shin'ichiro; Itai, Takaaki; Takahashi, Shin; Guo, Xinyu

2016-06-15

The long-distance transport potential of toxic lead (Pb) by plastic marine debris was examined by pure water leaching experiments using plastic fishery floats containing high level of additive-Pb such as 5100±74.3mgkg(-1). The leaching of Pb ended after sequential 480-h leaching experiments, and the total leaching amount is equivalent to approximately 0.1% of total Pb in a float. But it recovered when the float was scratched using sandpaper. We propose that a "low-Pb layer," in which Pb concentration is negligibly small, be generated on the float surface by the initial leaching process. Thickness of the layer is estimated at 2.5±1.2μm, much shallower than flaws on floats scratched by sandpaper and floats littering beaches. The result suggests that the low-Pb layer is broken by physical abrasion when floats are washed ashore, and that Pb inside the floats can thereafter leach into beaches. Copyright © 2016 Elsevier Ltd. All rights reserved.

Biochar application mode influences nitrogen leaching and NH3 volatilization losses in a rice paddy soil irrigated with N-rich wastewater.

PubMed

Sun, Haijun; Min, Ju; Zhang, Hailin; Feng, Yanfang; Lu, Kouping; Shi, Weiming; Yu, Min; Li, Xuewen

2017-07-11

Impacts of biochar application mode on nitrogen (N) leaching, ammonia (NH 3 ) volatilization, rice grain yield and N use efficiency (NUE) are not well understood. Therefore, a field experiment was conducted to evaluate those impacts in a rice paddy soil received 225 kg N ha -1 from either urea or N-rich wastewater. One treatment received 10 t ha -1 biochar with the basal fertilization, and the other received same total amount of biochar but split applied with the three split N applications with same ratio as N fertilizer split ratio (40%, 30% and 30%). Results showed that N leaching loads were 4.20-6.22 kg ha -1 . Biochar one-time application reduced N leaching by 23.1%, and biochar split application further reduced N leaching by 32.4%. Total NH 3 volatilization loss was 15.5-24.5 kg ha -1 . Biochar one-time application did not influence the NH 3 volatilization, but biochar split application stimulated the cumulative NH 3 volatilization by 57.7%. Both biochar treatments had no influence on NUE and rice grain yield. In conclusion, biochar application mode indeed influences the N leaching and NH 3 volatilization in rice paddy soils, and biochar one-time application should be recommended for reducing N leaching without increasing NH 3 volatilization.

Facilitated Leaching of Additive-Derived PBDEs from Plastic by Seabirds' Stomach Oil and Accumulation in Tissues.

PubMed

Tanaka, Kosuke; Takada, Hideshige; Yamashita, Rei; Mizukawa, Kaoruko; Fukuwaka, Masa-Aki; Watanuki, Yutaka

2015-10-06

Our previous study suggested the transfer of polybrominated diphenyl ether (PBDE) flame retardants from ingested plastics to seabirds' tissues. To understand how the PBDEs are transferred, we studied leaching from plastics into digestive fluids. We hypothesized that stomach oil, which is present in the digestive tract of birds in the order Procellariiformes, acts as an organic solvent, facilitating the leaching of hydrophobic chemicals. Pieces of plastic compounded with deca-BDE were soaked in several leaching solutions. Trace amounts were leached into distilled water, seawater, and acidic pepsin solution. In contrast, over 20 times as much material was leached into stomach oil, and over 50 times as much into fish oil (a major component of stomach oil). Analysis of abdominal adipose, liver tissue, and ingested plastics from 18 wild seabirds collected from the North Pacific Ocean showed the occurrence of deca-BDE or hexa-BDEs in both the tissues and the ingested plastics in three of the birds, suggesting transfer from the plastic to the tissues. In birds with BDE209 in their tissues, the dominance of BDE207 over other nona-BDE isomers suggested biological debromination at the meta position. Model calculation of PBDE exposure to birds based on the results of the leaching experiments combined with field observations suggested the dominance of plastic-mediated internal exposure to BDE209 over exposure via prey.

Food processing by animals: do beavers leach tree bark to improve palatability?

PubMed

Müller-Schwarze, D; Brashear, H; Kinnel, R; Hintz, K A; Lioubomirov, A; Skibo, C

2001-05-01

Beavers store and consume tree parts in the bodies of water where they live. We examined whether such soaking renders food more palatable by leaching out undesirable compounds. In experiment 1, saplings of red maple, Acer rubrum (RM), were first soaked in a pond for periods of 2, 18, and 36 days, then offered to free-ranging beavers. Soaking for two days rendered RM slightly more acceptable to beavers. To further examine the time window around two days, RM sticks were soaked in distilled water in the laboratory for 1, 2, 4, and 6 days before presenting them to beavers (experiment 2). In experiment 3, twigs of three species were placed on land. Beavers placed RM in the water for 1 to 3 days before consuming the twigs. In experiment 4, sticks were provided in the water at Cranberry Lake Biological Station (CLBS). Most quaking aspen (QA) was consumed during the first night, and most witch hazel, Hamamelis virginiana (WH), during the third night. At Allegany State Park (ASP), no such difference was found. Twigs were provided in the water in experiment 5. At ASP, WH was taken after three days in the water, and at CLBS little WH was consumed, and only during the third night. A meta-analysis of all experiments shows that relatively more WH is consumed after two days than any other species. Experiment 6 traced the time beavers left their own harvested branches in the water. Unlike other tree species, WH remained in the water for two to four days before being consumed. Experiment 7 measured the phenolics leached into water from RM twigs and small pieces of bark soaked for 10 and 8 days, respectively. Shredded bark lost 50-60% of leachable phenolics into the water, and twigs 70-80%. We conclude that beavers can use water to leach undesirable compounds from their food. Although this effect was not robust, our study is the first of its kind.

Biofilm formation and interspecies interactions in mixed cultures of thermo-acidophilic archaea Acidianus spp. and Sulfolobus metallicus.

PubMed

Castro, Camila; Zhang, Ruiyong; Liu, Jing; Bellenberg, Sören; Neu, Thomas R; Donati, Edgardo; Sand, Wolfgang; Vera, Mario

2016-09-01

The understanding of biofilm formation by bioleaching microorganisms is of great importance for influencing mineral dissolution rates and to prevent acid mine drainage (AMD). Thermo-acidophilic archaea such as Acidianus, Sulfolobus and Metallosphaera are of special interest due to their ability to perform leaching at high temperatures, thereby enhancing leaching rates. In this work, leaching experiments and visualization by microscopy of cell attachment and biofilm formation patterns of the crenarchaeotes Sulfolobus metallicus DSM 6482(T) and the Acidianus isolates DSM 29038 and DSM 29099 in pure and mixed cultures on sulfur or pyrite were studied. Confocal laser scanning microscopy (CLSM) combined with fluorescent dyes as well as fluorescently labeled lectins were used to visualize different components (e.g. DNA, proteins or glycoconjugates) of the aforementioned species. The data indicate that cell attachment and the subsequently formed biofilms were species- and substrate-dependent. Pyrite leaching experiments coupled with pre-colonization and further inoculation with a second species suggest that both species may negatively influence each other during pyrite leaching with respect to initial attachment and pyrite dissolution rates. In addition, the investigation of binary biofilms on pyrite showed that both species were heterogeneously distributed on pyrite surfaces in the form of individual cells or microcolonies. Physical contact between the two species seems to occur, as revealed by specific lectins able to specifically bind single species within mixed cultures. Copyright © 2016 Institut Pasteur. Published by Elsevier Masson SAS. All rights reserved.

A study on the selection of indigenous leaching-bacteria for effective bioleaching

NASA Astrophysics Data System (ADS)

Oh, S. J.; Cho, K. H.; Kim, B. J.; Choi, N. C.; Park, C. Y.

2012-04-01

Bioleaching technology, which is based on the ability of microorganisms to transform solid compounds into soluble and extractable valuable elements that can be recovered, has been rapidly developed in recent decades for its advantages, which include mild reaction condition, low energy consumption, simple process, low environmental impact and being suitable for low grade mine tailings and residues. The bacteria activities (survival, adaptation of toxically environments etc.) in the bioleaching technology play a key role in the solubilization of metals. The purpose of this study was to selection of optimal leaching-bacteria through changed pH and redox potential on bio-oxidation in batch experiments for successful bioleaching technology. Twenty three indigenous bacteria used throughout this study, leaching-bacteria were obtained from various geochemical conditions; bacteria inhabitation type (acid mine drainage, mine wastes leachate and sulfur hot springs) and base-metal type (sulfur, sulfide, iron and coal). Bio-oxidation experiment result was showed that 9 cycles (1 cycle - 28days) after the leaching-bacteria were inoculated to a leaching medium, pH was observed decreasing and redox potential increased. In the bacteria inhabitation type, bio-oxidation of sulfur hot springs bacteria was greater than other types (acid mine drainage and mine wastes leachate). In addition, bio-oxidation on base-metal type was appeared sulfur was greater than other types (sulfide, iron and coal). This study informs basic knowledge when bacteria apply to eco-/economic resources utilization studies including the biomining and the recycling of mine waste system.

Concomitant Leaching and Electrochemical Extraction of Rare Earth Elements from Monazite.

PubMed

Maes, Synthia; Zhuang, Wei-Qin; Rabaey, Korneel; Alvarez-Cohen, Lisa; Hennebel, Tom

2017-02-07

Rare earth elements (REEs) have become increasingly important in modern day technologies. Unfortunately, their recycling is currently limited, and the conventional technologies for their extraction and purification are exceedingly energy and chemical intensive. New sustainable technologies for REE extraction from both primary and secondary resources would be extremely beneficial. This research investigated a two-stage recovery strategy focused on the recovery of neodymium (Nd) and lanthanum (La) from monazite ore that combines microbially based leaching (using citric acid and spent fungal supernatant) with electrochemical extraction. Pretreating the phosphate-based monazite rock (via roasting) dramatically increased the microbial REE leaching efficiency. Batch experiments demonstrated the effective and continued leaching of REEs by recycled citric acid, with up to 392 mg of Nd L -1 and 281 mg of La L -1 leached during seven consecutive 24 h cycles. Neodymium was further extracted in the catholyte of a three-compartment electrochemical system, with up to 880 mg of Nd L -1 achieved within 4 days (at 40 A m -2 ). Meanwhile, the radioactive element thorium and counterions phosphate and citrate were separated effectively from the REEs in the anolyte, favoring REE extraction and allowing sustainable reuse of the leaching agent. This study shows a promising technology that is suitable for primary ores and can further be optimized for secondary resources.

The enhancing of Au-Ag-Te content in tellurium-bearing ore mineral by bio-oxidation-leaching

NASA Astrophysics Data System (ADS)

Kim, PyeongMan; Kim, HyunSoo; Myung, EunJi; Kim, YoonJung; Lee, YongBum; Park*, CheonYoung

2015-04-01

The purpose of this study is to enhance the content of valuable metals such as Au-Ag-Te in tellurium-bearing minerals by bio-oxidation-leaching. It was confirmed that pyrite, chalcopyrite, sphalerite and galena were produced together with tellurium-bearing minerals including hessite, sylvanite and tellurobismuthite from ore minerals and concentrates through microscopic observation and SEM/EDS analysis. In a bio-oxidation-leaching experiment, with regard to Au, Ag, Te, Cu and Fe, the changes in the amount of leaching and the content of leaching residues were compared and analyzed with each other depending on the adaptation of an indigenous microbe identified as Acidithiobacillus ferrooxidans. As a result of the experiment, the Au-Ag-Te content in tellurium-bearing ore mineral was enhanced in the order of physical oxidation leaching, physical/non-adaptive bio-oxidation-leaching and physical/adaptive biological leaching. It suggests that the bio-oxidation-leaching using microbes adapted in tellurium-bearing ore mineral can be used as a pre-treatment and a main process in a recovery process of valuable metals. "This research was supported by Basic Science Research Program through the National Research Foundation of Korea(NRF) funded by the Ministry of Education(NRF-2013R1A1A2004898)"

Nitrogen leaching from natural ecosystems under global change: a modelling study

NASA Astrophysics Data System (ADS)

Braakhekke, Maarten C.; Rebel, Karin T.; Dekker, Stefan C.; Smith, Benjamin; Beusen, Arthur H. W.; Wassen, Martin J.

2017-12-01

To study global nitrogen (N) leaching from natural ecosystems under changing N deposition, climate, and atmospheric CO2, we performed a factorial model experiment for the period 1901-2006 with the N-enabled global terrestrial ecosystem model LPJ-GUESS (Lund-Potsdam-Jena General Ecosystem Simulator). In eight global simulations, we used either the true transient time series of N deposition, climate, and atmospheric CO2 as input or kept combinations of these drivers constant at initial values. The results show that N deposition is globally the strongest driver of simulated N leaching, individually causing an increase of 88 % by 1997-2006 relative to pre-industrial conditions. Climate change led globally to a 31 % increase in N leaching, but the size and direction of change varied among global regions: leaching generally increased in regions with high soil organic carbon storage and high initial N status, and decreased in regions with a positive trend in vegetation productivity or decreasing precipitation. Rising atmospheric CO2 generally caused decreased N leaching (33 % globally), with strongest effects in regions with high productivity and N availability. All drivers combined resulted in a rise of N leaching by 73 % with strongest increases in Europe, eastern North America and South-East Asia, where N deposition rates are highest. Decreases in N leaching were predicted for the Amazon and northern India. We further found that N loss by fire regionally is a large term in the N budget, associated with lower N leaching, particularly in semi-arid biomes. Predicted global N leaching from natural lands rose from 13.6 Tg N yr-1 in 1901-1911 to 18.5 Tg N yr-1 in 1997-2006, accounting for reductions of natural land cover. Ecosystem N status (quantified as the reduction of vegetation productivity due to N limitation) shows a similar positive temporal trend but large spatial variability. Interestingly, this variability is more strongly related to vegetation type than N input. Similarly, the relationship between N status and (relative) N leaching is highly variable due to confounding factors such as soil water fluxes, fire occurrence, and growing season length. Nevertheless, our results suggest that regions with very high N deposition rates are approaching a state of N saturation.

Heavy metal uptake and leaching from polluted soil using permeable barrier in DTPA-assisted phytoextraction.

PubMed

Zhao, Shulan; Shen, Zhiping; Duo, Lian

2015-04-01

Application of sewage sludge (SS) in agriculture is an alternative technique of disposing this waste. But unreasonable application of SS leads to excessive accumulation of heavy metals in soils. A column experiment was conducted to test the availability of heavy metals to Lolium perenne grown in SS-treated soils following diethylene triamine penta acetic acid (DTPA) application at rates of 0, 10 and 20 mmol kg(-1) soil. In order to prevent metal leaching in DTPA-assisted phytoextraction process, a horizontal permeable barrier was placed below the treated soil, and its effectiveness was also assessed. Results showed that DTPA addition significantly increased metal uptake by L. perenne shoots and metal leaching. Permeable barriers increased metal concentrations in plant shoots and effectively decreased metal leaching from the treated soil. Heavy metals in SS-treated soils could be gradually removed by harvesting L. perenne many times in 1 year and adding low dosage of DTPA days before each harvest.

Leaching of chalcopyrite with sodium hypochlorite

NASA Astrophysics Data System (ADS)

Garlapalli, Ravinder Kumar

Chalcopyrite is the most important copper mineral source and also a refractory mineral for leaching. Several processing routes have been proposed to overcome the environmental problems related to copper extraction from chalcopyrite. In this study, the leaching of chalcopyrite has been investigated with a new reagent sodium hypochlorite (NaOCl). Experiments were carried out in two stages: conversion of chalcopyrite to cupric oxide with NaOCl solution in the first stage, followed by dissolution of the cupric oxide to cupric ion with 1 normal sulfuric acid at room temperature in the second stage. In the first stage leaching, the initial pH varied from 12.5 to 13.7; the temperature, from 35 to 75°C; NaOCl concentration, from 0.2 to 0.85 molar; and the chalcopyrite dosage, from 1 to 10 grams/500 ml. The leaching conversion showed a maximum (68.3%) around pH 13.2 at 0.5 molar of hypochlorite concentration and 65°C in 1 hour. The reagent consumption ratio, defined as the number of moles of hypochlorite consumed to leach one mole of chalcopyrite is found to be much higher than its stoichiometric ratio of 8.5. It reached 57.6 when the solid dosage was 1 gram/500 ml and decreased to 12.9 when the solid dosage was increased to 10 grams/500 ml. It was found that the leaching rate of chalcopyrite in the first stage was controlled by chemical reaction with the activation energy of 50.2 kJ/mol (12.0 kcal/mol). A leaching scheme was identified in which 98% chalcopyrite was leached by adding hypochlorite stock solution stepwise in less than three hours.

LEACHING OF METALS FROM MINERAL PROCESSING WASTE

EPA Science Inventory

The purpose of this project is to test the leaching of Mineral processing Waste (MPW) contaminated with heavy metals using scientifically defendable leaching tests other than TCLP. Past experience and literature have shown that TCLP underestiates the levels of metals such as oxoa...

LEACHING OF METALS FROM MINERAL PROCESSING WASTE

EPA Science Inventory

The purpose of this project is to test the leaching of Mineral Processing Waste (MPW) contaminated with heavy metals using scientifically defendable leaching tests other than TCLP. Past experience and literature have shown that TCLP underestimates the levels of metals such as oxo...

Impacts of road salts on leaching behavior of lead contaminated soil.

PubMed

Wu, Jingjing; Kim, Hwidong

2017-02-15

Research was conducted to explore the effects of road salts on lead leaching from lead contaminated soil samples that were collected in an old residence area in Erie, PA. The synthetic precipitate leaching procedure (SPLP) test was employed to evaluate lead leaching from one of the lead contaminated soils in the presence of various levels of road salts (5%, 10%, 20%, 30% and 40%). The results of the leaching test showed that lead leaching dramatically increased as the road salt content increased as a result of the formation of lead-chloride complexes, but different lead leaching patterns were observed in the presence of NaCl- and CaCl 2 -based road salts at a high content of road salts (>20%). Additional leaching tests that include 30% road salts and different soil samples showed a variety of leaching patterns by soil samples. The sequential extraction of each soil sample showed that a high fraction of organic matter bound lead was associated with lead contamination. The higher the fraction of organic matter bound lead contained in soil, the greater the effects of calcium on reducing lead leaching, observations showed. Copyright © 2016 Elsevier B.V. All rights reserved.

Evaluation of leaf litter leaching kinetics through commonly-used mathematical models

NASA Astrophysics Data System (ADS)

Montoya, J. V.; Bastianoni, A.; Mendez, C.; Paolini, J.

2012-04-01

Leaching is defined as the abiotic process by which soluble compounds of the litter are released into the water. Most studies dealing with leaf litter breakdown and leaching kinetics apply the single exponential decay model since it corresponds well with the understanding of the biology of decomposition. However, during leaching important mass losses occur and mathematical models often fail in describing this process adequately. During the initial hours of leaching leaf litter experience high decay rates which are not properly modelled. Adjusting leaching losses to mathematical models has not been investigated thoroughly and the use of models assuming constant decay rates leads to inappropriate assessments of leaching kinetics. We aim to describe, assess, and compare different leaching kinetics models fitted to leaf litter mass losses from six Neotropical riparian forest species. Leaf litter from each species was collected in the lower reaches of San Miguel stream in Northern Venezuela. Air-dried leaves from each species were incubated in 250 ml of water in the dark at room temperature. At 1h, 6h, 1d, 2d, 4d, 8d and 15d, three jars were removed from the assay in a no-replacement experimental design. At each time leaves from each jar were removed and oven-dried. Afterwards, dried up leaves were weighed and remaining dry mass was determined and expressed as ash-free dry mass. Mass losses of leaf litter showed steep declines for the first two days followed by a steady decrease in mass loss. Data was fitted to three different models: single-exponential, power and rational. Our results showed that the mass loss predicted with the single-exponential model did not reflect the real data at any stage of the leaching process. The power model showed a better adjustment, but fails predicting successfully the behavior during leaching's early stages. To evaluate the performance of our models we used three criteria: Adj-R2, Akaike's Information Criteria (AIC), and residual distribution. Higher Adj-R2 were obtained for the power and the rational-type models. However, when AIC and residuals distribution were used, the only model that could satisfactory predict the behavior of our dataset was the rational-type. Even if the Adj-R2 was higher for some species when using the power model compared to the rational-type; our results showed that this criterion alone cannot demonstrate the predicting performance of any model. Usually Adj-R2 is used when assessing the goodness of fit for any mathematical model disregarding the fact that a good Adj-R2 could be obtained even when statistical assumptions required for the validity of the model are not satisfied. Our results showed that sampling at the initial stages of leaching is necessary to adequately describe this process. We also provided evidence that using traditional mathematical models is not the best option to evaluate leaching kinetics because of its mathematical inability to properly describe the abrupt changes that occur during the early stages of leaching. We also found useful applying different criteria to evaluate the goodness-of-fit and performance of any model considered taking into account both statistical and biological meaning of the results.

Environmental implications of material leached from coal.

PubMed

Moyo, Stanley; Mujuru, Munyaradzi; McCrindle, Rob I; Mokgalaka-Matlala, Ntebogeng

2011-05-01

Samples of coal were collected from different seams at a South African coal mine and comparative leaching experiments were carried out under various pH conditions and times to investigate the leaching behavior and potential environmental impact of possibly hazardous elements such as As, Cd, Co, Cr, Mn, Ni, Pb, Th and U. The calculated leaching intensities, sequential extraction results and cumulative percentages demonstrate that the leaching behavior of the elements is strongly influenced by the pH, the leaching time and the properties and occurrences of the elements. The leached concentrations of As, Cd, Co, Cr, Mn, Ni and Pb exceeded the maximum concentrations recommended by the Environmental Protection Agency (EPA) for surface water.

Selenium mobility and distribution in irrigated and nonirrigated alluvial soils

USGS Publications Warehouse

Fio, John L.; Fujii, Roger; Deverel, S.J.

1991-01-01

Dissolution and leaching of soil salts by irrigation water is a primary source of Se to shallow groundwater in the western San Joaquin Valley, California. In this study, the mobility and distribution of selenite and selenate in soils with different irrigation and drainage histories was evaluated using sorption experiments and an advection-dispersion model. The sorption studies showed that selenate (15–12400 µg Se L−1) is not adsorbed to soil, whereas selenite (10–5000 µg Se L−1) is rapidly adsorbed. The time lag between adsorption and desorption of selenite is considerable, indicating a dependence of reaction rate on reaction direction (hysteresis). Selenite adsorption and desorption isotherms were different, and both were described with the Freundlich equation. Model results and chemical analyses of extracts from the soil samples showed that selenite is resistant to leaching and therefore can represent a potential long-term source of Se to groundwater. In contrast, selenate behaves as a conservative constituent under alkaline and oxidized conditions and is easily leached from soil.

Mineralogy and pore water chemistry of a boiler ash from a MSW fluidized-bed incinerator.

PubMed

Bodénan, F; Guyonnet, D; Piantone, P; Blanc, P

2010-07-01

This paper presents an investigation of the mineralogy and pore water chemistry of a boiler ash sampled from a municipal solid waste fluidized-bed incinerator, subject to 18 months of dynamic leaching in a large percolation column experiment. A particular focus is on the redox behaviour of Cr(VI) in relation to metal aluminium Al(0), as chromium may represent an environmental or health hazard. The leaching behaviour and interaction between Cr(VI) and Al(0) are interpreted on the basis of mineralogical evolutions observed over the 18-month period and of saturation indices calculated with the geochemical code PhreeqC and reviewed thermodynamic data. Results of mineralogical analyses show in particular the alteration of mineral phases during leaching (e.g. quartz and metal aluminium grains), while geochemical calculations suggest equilibria of percolating fluids with respect to specific mineral phases (e.g. monohydrocalcite and aluminium hydroxide). The combination of leaching data on a large scale and mineralogical analyses document the coupled leaching behaviour of aluminium and chromium, with chromium appearing in the pore fluids in its hexavalent and mobile state once metal aluminium is no longer available for chromium reduction. Copyright (c) 2010 Elsevier Ltd. All rights reserved.

Research on the effect of alkali roasting of copper dross on leaching rate of indium

NASA Astrophysics Data System (ADS)

Dafang, Liu; Fan, Xingxiang; Shi, Yifeng; Yang, Kunbin

2017-11-01

The byproduct copper dross produced during refining crude lead was characterized by X-ray diffraction (XRD), scanning electron microscope (SEM) and fluorescence spectrometer (XRF), which showed that copper dross mainly contained lead, copper, zinc, arsenic, antimony, bismuth, sulfur and a small amount of indium and silver etc. The mineralogical phase change of oxidation roasting of copper dross by adding sodium hydroxide was analyzed with the help of XRD and SEM. The effects of water leaching, ratio of sodium hydroxide, roasting time, and roasting temperature on leaching rate of indium were investigated mainly. The experimental results showed that phase of lead metal and sulfides of lead, copper and zinc disappeared after oxidation roasting of copper dross by adding sodium hydroxide, new phase of oxides of lead, copper, zinc and sodium salt of arsenic and antimony appeared. Water leaching could remove arsenic, and acid leaching residue obtained was then leached with acid. The leaching rate of indium was higher 6.98% compared with alkali roasting of copper dross-acid leaching. It showed that removing arsenic by water leaching and acid leaching could increase the leaching rate of indium and be beneficial to reducing subsequent acid consumption of extracting indium by acid leaching. The roasting temperature had a significant effect on the leaching rate of indium, and leaching rate of indium increased with the rise of roasting temperature. When roasting temperature ranged from 450°C to 600°C, leaching rate of indium increased significantly with the rise of roasting temperature. When roasting temperature rose from 450°C to 600°C, leaching rate of indium increased by 60.29%. The amount of sodium hydroxide had an significant effect on the leaching rate of indium, and the leaching of indium increased with the increase of the amount of sodium hydroxide, and the leaching rate of indium was obviously higher than that of copper dross blank roasting and acid leaching.

Maximization of organic acids production by Aspergillus niger in a bubble column bioreactor for V and Ni recovery enhancement from power plant residual ash in spent-medium bioleaching experiments.

PubMed

Rasoulnia, P; Mousavi, S M

2016-09-01

Spent-medium bioleaching of V and Ni from a power plant residual ash (PPR ash) was conducted using organic acids produced by Aspergillus niger. The production of organic acids in a bubble column bioreactor was optimized through selecting three most influencing factors. Under optimum condition of aeration rate of 762.5(ml/min), sucrose concentration of 101.9(g/l) and inoculum size of 40(ml/l), respectively 17,185, 4539, 1042 and 502(ppm) of oxalic, gluconic, citric and malic acids were produced. Leaching experiments were carried out using biogenic produced organic acids under leaching environment temperature of 60°C and rotary shaking speed of 135rpm, with various pulp densities of 1, 2, 3, 5, 7 and 9(%w/v). The results showed that biogenic produced organic acids leached V much more efficiently than Ni so that even at high pulp density of 9(%w/v), 83% of V was recovered while Ni recovery yield was 30%. Copyright © 2016 Elsevier Ltd. All rights reserved.

Assessment of the leaching of metallic elements in the technology of solidification in aqueous solution.

PubMed

Rossetti, V Alunno; Di Palma, L; Medici, F

2002-01-01

Results are presented of experiments performed to optimize the solidification/stabilization system for metallic elements in aqueous solution. This system involves mixing cement and a solution of metallic elements in a conventional mixer: the paste thus obtained is transferred drop by drop into a recipient filled with an aqueous solution of NaOH at 20% by weight, in which it solidifies immediately. The separate use of chloride solutions of Li+, Cr3+, Pb2+ and Zn2+ makes it possible to obtain granules displaying various levels of compressive strength. Three different inertization matrices were used in the experiments, the first consisting solely of Portland cement, the second of Portland cement and a superplasticizer additive, and the third of Portland cement partially replaced with silica-fume and superplasticizer. The results of the tests performed showed a very low level of leaching into the alkaline solidification solution for Cr3+, the quantity leached being under 2% as against higher levels for the other metallic elements. For all the considered elements, the best results were obtained by using silica-fume in the inertization matrix.

Sustainable Soil Washing: Shredded Card Filtration of Potentially Toxic Elements after Leaching from Soil Using Organic Acid Solutions

PubMed Central

Ash, Christopher; Drábek, Ondřej; Tejnecký, Václav; Jehlička, Jan; Michon, Ninon; Borůvka, Luboš

2016-01-01

Shredded card (SC) was assessed for use as a sorbent of potentially toxic elements (PTE) carried from contaminated soil in various leachates (oxalic acid, formic acid, CaCl2, water). We further assessed SC for retention of PTE, using acidified water (pH 3.4). Vertical columns and a peristaltic pump were used to leach PTE from soils (O and A/B horizons) before passing through SC. Sorption onto SC was studied by comparing leachates, and by monitoring total PTE contents on SC before and after leaching. SC buffers against acidic soil conditions that promote metals solubility; considerable increases in solution pH (+4.49) were observed. Greatest differences in solution PTE content after leaching with/without SC occurred for Pb. In oxalic acid, As, Cd, Pb showed a high level of sorption (25, 15, and 58x more of the respective PTE in leachates without SC). In formic acid, Pb sorption was highly efficient (219x more Pb in leachate without SC). In water, only Pb showed high sorption (191x more Pb in leachate without SC). In desorption experiments, release of PTE from SC varied according to the source of PTE (organic/mineral soil), and type of solvent used. Arsenic was the PTE most readily leached in desorption experiments. Low As sorption from water was followed by fast release (70% As released from SC). A high rate of Cd sorption from organic acid solutions was followed by strong retention (~12% Cd desorption). SC also retained Pb after sorption from water, with subsequent losses of ≤8.5% of total bound Pb. The proposed use of this material is for the filtration of PTE from extract solution following soil washing. Low-molecular-mass organic acids offer a less destructive, biodegradable alternative to strong inorganic acids for soil washing. PMID:26900684

Bioleaching combined brine leaching of heavy metals from lead-zinc mine tailings: Transformations during the leaching process.

PubMed

Ye, Maoyou; Yan, Pingfang; Sun, Shuiyu; Han, Dajian; Xiao, Xiao; Zheng, Li; Huang, Shaosong; Chen, Yun; Zhuang, Shengwei

2017-02-01

During the process of bioleaching, lead (Pb) recovery is low. This low recovery is caused by a problem with the bioleaching technique. This research investigated the bioleaching combination of bioleaching with brine leaching to remove heavy metals from lead-zinc mine tailings. The impact of different parameters were studied, including the effects of initial pH (1.5-3.0) and solid concentration (5-20%) for bioleaching, and the effects of sodium chloride (NaCl) concentration (10-200 g/L) and temperature (25 and 50 °C) for brine leaching. Complementary characterization experiments (Sequential extraction, X-ray diffractometer (XRD), scanning electronic microscope (SEM)) were also conducted to explore the transformation of tailings during the leaching process. The results showed that bioleaching efficiency was significantly influenced by initial pH and solid concentration. Approximately 85.45% of iron (Fe), 4.12% of Pb, and 97.85% of zinc (Zn) were recovered through bioleaching in optimum conditions. Increasing the brine concentration and temperature promoted lead recovery. Lead was recovered from the bioleaching residues at a rate of 94.70% at 25 °C and at a rate of 99.46% at 50 °C when the NaCl concentration was 150 g/L. The study showed that bioleaching significantly changed the speciation of heavy metals and the formation and surface morphology of tailings. The metals were mainly bound in stable fractions after bioleaching. Copyright © 2016 Elsevier Ltd. All rights reserved.

[Monitoring of water and salt transport in silt and sandy soil during the leaching process].

PubMed

Fu, Teng-Fei; Jia, Yong-Gang; Guo, Lei; Liu, Xiao-Lei

2012-11-01

Water and salt transport in soil and its mechanism is the key point of the saline soil research. The dynamic rule of water and transport in soil during the leaching process is the theoretical basis of formation, flush, drainage and improvement of saline soil. In this study, a vertical infiltration experiment was conducted to monitor the variation in the resistivity of silt and sandy soil during the leaching process by the self-designed automatic monitoring device. The experimental results showed that the peaks in the resistivity of the two soils went down and faded away in the course of leaching. It took about 30 minutes for sandy soil to reach the water-salt balance, whereas the silt took about 70 minutes. With the increasing leaching times, the desalination depth remained basically the same, being 35 cm for sandy soil and 10 cm for the silt from the top to bottom of soil column. Therefore, 3 and 7 leaching processes were required respectively for the complete desalination of the soil column. The temporal and spatial resolution of this monitoring device can be adjusted according to the practical demand. This device can not only achieve the remote, in situ and dynamic monitoring data of water and salt transport, but also provide an effective method in monitoring, assessment and early warning of salinization.

Bioleaching of metals from spent refinery petroleum catalyst using moderately thermophilic bacteria: effect of particle size.

PubMed

Srichandan, Haragobinda; Singh, Sradhanjali; Pathak, Ashish; Kim, Dong-Jin; Lee, Seoung-Won; Heyes, Graeme

2014-01-01

The present work investigated the leaching potential of moderately thermophilic bacteria in the recovery of metals from spent petroleum catalyst of varying particle sizes. The batch bioleaching experiments were conducted by employing a mixed consortium of moderate thermophilic bacteria at 45°C and by using five different particle sizes (from 45 to >2000 μm) of acetone-washed spent catalyst. The elemental mapping by FESEM confirmed the presence of Al, Ni, V and Mo along with sulfur in the spent catalyst. During bioleaching, Ni (92-97%) and V (81-91%) were leached in higher concentrations, whereas leaching yields of Al (23-38%) were found to be lowest in all particle sizes investigated. Decreasing the particle size from >2000 μm to 45-106 μm caused an increase in leaching yields of metals during initial hours. However, the final metals leaching yields were almost independent of particle sizes of catalyst. Leaching kinetics was observed to follow the diffusion-controlled model showing the linearity more close than the chemical control. The results of the present study suggested that bioleaching using moderate thermophilic bacteria was highly effective in removing the metals from spent catalyst. Moreover, bioleaching can be conducted using spent catalyst of higher particle size (>2000 μm), thus saving the grinding cost and making process attractive for larger scale application.

Retention and leaching of nitrite by municipal solid waste incinerator bottom ash under the landfill circumstance.

PubMed

Yao, Jun; Kong, Qingna; Zhu, Huayue; Long, Yuyang; Shen, Dongsheng

2015-01-01

The retention and leaching of nitrite by municipal solid waste incinerator (MSWI) bottom ash could affect its migration in the landfill. In this study, the effect of the dosage of MSWI bottom ash as well as the variation of the landfill environmental parameters including pH, anions and organic matter on the nitrite retention and leaching behavior was investigated by batch experiments. The highest removal percentage (73.0%) of nitrite was observed when the dosage of MSWI bottom ash was 10 g L(-1) in 2 mg L(-1) nitrite solution. Further increase of the dosage would retard the retention, as the nitrite leaching from MSWI bottom ash was enhanced. The optimum retention of nitrite was observed when the pH was 5.0, while the leaching of nitrite showed a consistent reduction with the increase of pH. Besides, the presence of Cl(-), SO4(2)(-) and acetic acid could enhance the leaching of nitrite and mitigate the retention process. However, the retention of nitrite was enhanced by PO4(3)(-), which was probably due to the formation of the apatite, an active material for the adsorption of the nitrite. These results suggested that MSWI bottom ash could affect the migration of nitrite in the landfill, which was related to the variation of the landfill circumstance. Copyright © 2014 Elsevier Ltd. All rights reserved.

Mechanistic study of lead desorption during the leaching process of ion-absorbed rare earths: pH effect and the column experiment.

PubMed

Tang, Jie; Xue, Qiang; Chen, Honghan; Li, Wenting

2017-05-01

High concentrations of ammonium sulfate, often used in the in situ mining process, can result in a decrease of pH in the environment and dissolution of rare earth metals. Ammonium sulfate can also cause desorption of toxic heavy metals, leading to environmental and human health implications. In this study, the desorption behavior and fraction changes of lead in the ion-absorbed rare earth ore were studied using batch desorption experiments and column leaching tests. Results from batch desorption experiments showed that the desorption process of lead included fast and slow stages and followed an Elovich model well. The desorption rate and the proportion of lead content in the solution to the total lead in the soil were observed to increase with a decrease in the initial pH of the ammonium sulfate solution. The lead in soil included an acid-extractable fraction, reducible fraction, oxidizable fraction, and a residual fraction, with the predominant fractions being the reducible and acid-extractable fractions. Ninety-six percent of the extractable fraction in soil was desorbed into solution at pH = 3.0, and the content of the reducible fraction was observed to initially increase (when pH >4.0) and then decrease (when pH <4.0) with a decrease in pH. Column leaching tests indicated that the content of lead in the different fractions of soil followed the trend of reducible fraction > oxidizable fraction > acid-extractable fraction > residual fraction after the simulating leaching mining process. The change in pH was also found to have a larger influence on the acid-extractable and reducible fractions than the other two fractions. The proportion of the extractable fraction being leached was ca. 86%, and the reducible fraction was enriched along the migration direction of the leaching liquid. These results suggest that certain lead fractions may desorb again and contaminate the environment via acid rain, which provides significant information for environmental assessment and remediation after mining process. Graphical abstract ᅟ.

[Fertility and Environmental Impacts of Urban Scattered Human Feces Used as Organic Granular Fertilizer for Leaf Vegetables].

PubMed

Lü, Wen-zhou; Qiao, Yu-xiang; Yu, Ning; Shi, Rong-hua; Wang, Guang-ming

2015-09-01

The disposal of urban scattered human feces has become a difficult problem for the management of modern city. In present study, the scattered human feces underwent the collection, scum removal, flocculation and dehydration, finally became the granular fertilizer; the effects of the ratio of fertilizer to soil on the growth of the pakchoi and the quality of soil and leaching water were evaluated, and the feasibility of granular fertilizer manuring the pakchoi was discussed by pot experiments. The results showed that the granular fertilizer significantly enhanced the production of the pakchoi which were not polluted by the intestinal microorganisms under the experiment conditions; meanwhile, at the proper ratio of fertilizer to soil, the concentration of these microorganisms in the leaching water was lower than that in the control check. Chemical analyses of soil revealed that the nutrient content of nitrogen, phosphorus, potassium and organic matters in soil became much richer in all treatments. In addition, the granular fertilizer improved the physical- chemical properties of soil, including raising the level of soil porosity and reducing the volume weight of soil. Application of granular fertilizer won't pollute the soil or leaching water; instead, it can also prevent nitrogen, potassium and intestinal microorganisms from leaching inio ground water at the proper ratio of granular fertilizer to soil.

Leaching behavior of heavy metals and transformation of their speciation in polluted soil receiving simulated acid rain.

PubMed

Zheng, Shun-an; Zheng, Xiangqun; Chen, Chun

2012-01-01

Heavy metals that leach from contaminated soils under acid rain are of increasing concern. In this study, simulated acid rain (SAR) was pumped through columns of artificially contaminated purple soil. Column leaching tests and sequential extraction were conducted for the heavy metals Cu, Pb, Cd, and Zn to determine the extent of their leaching as well as to examine the transformation of their speciation in the artificially contaminated soil columns. Results showed that the maximum leachate concentrations of Cu, Pb, Cd, and Zn were less than those specified in the Chinese Quality Standards for Groundwater (Grade IV), thereby suggesting that the heavy metals that leached from the polluted purple soil receiving acid rain may not pose as risks to water quality. Most of the Pb and Cd leachate concentrations were below their detection limits. By contrast, higher Cu and Zn leachate concentrations were found because they were released by the soil in larger amounts as compared with those of Pb and Cd. The differences in the Cu and Zn leachate concentrations between the controls (SAR at pH 5.6) and the treatments (SAR at pH 3.0 and 4.5) were significant. Similar trends were observed in the total leached amounts of Cu and Zn. The proportions of Cu, Pb, Cd, and Zn in the EXC and OX fractions were generally increased after the leaching experiment at three pH levels, whereas those of the RES, OM, and CAR fractions were slightly decreased. Acid rain favors the leaching of heavy metals from the contaminated purple soil and makes the heavy metal fractions become more labile. Moreover, a pH decrease from 5.6 to 3.0 significantly enhanced such effects.

Leaching Behavior of Heavy Metals and Transformation of Their Speciation in Polluted Soil Receiving Simulated Acid Rain

PubMed Central

Zheng, Shun-an; Zheng, Xiangqun; Chen, Chun

2012-01-01

Heavy metals that leach from contaminated soils under acid rain are of increasing concern. In this study, simulated acid rain (SAR) was pumped through columns of artificially contaminated purple soil. Column leaching tests and sequential extraction were conducted for the heavy metals Cu, Pb, Cd, and Zn to determine the extent of their leaching as well as to examine the transformation of their speciation in the artificially contaminated soil columns. Results showed that the maximum leachate concentrations of Cu, Pb, Cd, and Zn were less than those specified in the Chinese Quality Standards for Groundwater (Grade IV), thereby suggesting that the heavy metals that leached from the polluted purple soil receiving acid rain may not pose as risks to water quality. Most of the Pb and Cd leachate concentrations were below their detection limits. By contrast, higher Cu and Zn leachate concentrations were found because they were released by the soil in larger amounts as compared with those of Pb and Cd. The differences in the Cu and Zn leachate concentrations between the controls (SAR at pH 5.6) and the treatments (SAR at pH 3.0 and 4.5) were significant. Similar trends were observed in the total leached amounts of Cu and Zn. The proportions of Cu, Pb, Cd, and Zn in the EXC and OX fractions were generally increased after the leaching experiment at three pH levels, whereas those of the RES, OM, and CAR fractions were slightly decreased. Acid rain favors the leaching of heavy metals from the contaminated purple soil and makes the heavy metal fractions become more labile. Moreover, a pH decrease from 5.6 to 3.0 significantly enhanced such effects. PMID:23185399

Effect of nanohydroxyapatite on cadmium leaching and environmental risks under simulated acid rain.

PubMed

Zhao, Chenchen; Ren, Shuxia; Zuo, Qingqing; Wang, Shutao; Zhou, Yapeng; Liu, Wei; Liang, Shuxuan

2018-06-15

Cadmium (Cd) contamination in soil is a global environmental pollution issue. Nanohydroxyapatite (NHAP) has been used in soil remediation to immobilize cadmium in contaminated soils. However, the effect of acid rain on the export of cadmium from topsoil and its behavior in deep soil and leachate is unclear. In this study, column experiments and development of parsimonious model were performed to estimate Cd leaching behavior from topsoil and environmental risk of groundwater after 0.5% NHAP remediation. Four leaching events were performed and total Cd, different fractions of Cd determined by sequential extraction procedure and pH were determined for each leaching. The results show that with the export of Cd in topsoil, the total Cd concentration in soil at different depths had the following vertical distributions: 0-5 cm > 5-10 cm > 10-15 cm > 15-20 cm. NHAP treatment increased the soil pH and decreased Cd leaching loss by 56.45% compared to the control, and the results fit the parabolic diffusion model. With sequential extraction it was observed that NHAP application increased the residual fraction of cadmium in soil. After leaching, there was a positive correlation between soil pH and Cd concentration with regards to the exchangeable, reducible, oxidizable and residual Cd fractions. The parabolic diffusion model showed that Cd-contaminated soil with NHAP remediation is harmless to humans after sufficient remediation duration, whereas the resultant concentrations from the CK treatment could be toxic. The results indicate that nanohydroxyapatite could significantly reduce the bioavailability of cadmium and the environmental risk. However, the release of Ca and P from the dissolution of NHAP should be carefully studied as this will impact the mobilization of Cd or colloid Cd, and high leaching of P may result in P-induced eutrophication risk. Copyright © 2018 Elsevier B.V. All rights reserved.

Leaching characteristics of vanadium in mine tailings and soils near a vanadium titanomagnetite mining site.

PubMed

Yang, Jinyan; Tang, Ya; Yang, Kai; Rouff, Ashaki A; Elzinga, Evert J; Huang, Jen-How

2014-01-15

A series of column leaching experiments were performed to understand the leaching behaviour and the potential environmental risk of vanadium in a Panzhihua soil and vanadium titanomagnetite mine tailings. Results from sequential extraction experiments indicated that the mobility of vanadium in both the soil and the mine tailings was low, with <1% of the total vanadium readily mobilised. Column experiments revealed that only <0.1% of vanadium in the soil and mine tailing was leachable. The vanadium concentrations in the soil leachates did not vary considerably, but decreased with the leachate volume in the mine tailing leachates. This suggests that there was a smaller pool of leachable vanadium in the mine tailings compared to that in the soil. Drought and rewetting increased the vanadium concentrations in the soil and mine tailing leachates from 20μgL(-1) to 50-90μgL(-1), indicating the potential for high vanadium release following periods of drought. Experiments with soil columns overlain with 4, 8 and 20% volume mine tailings/volume soil exhibited very similar vanadium leaching behaviour. These results suggest that the transport of vanadium to the subsurface is controlled primarily by the leaching processes occurring in soils. Copyright © 2013 Elsevier B.V. All rights reserved.

Long-term high-level waste technology. Composite report

NASA Astrophysics Data System (ADS)

Cornman, W. R.

1981-12-01

Research and development studies on the immobilization of high-level wastes from the chemical reprocessing of nuclear reactor fuels are summarized. The reports are grouped under the following tasks: (1) program management and support; (2) waste preparation; (3) waste fixation; and (4) final handling. Some of the highlights are: leaching properties were obtained for titanate and tailored ceramic materials being developed at ICPP to immobilize zirconia calcine; comparative leach tests, hot-cell tests, and process evaluations were conducted of waste form alternatives to borosilicate glass for the immobilization of SRP high-level wastes, experiments were run at ANL to qualify neutron activation analysis and radioactive tracers for measuring leach rates from simulated waste glasses; comparative leach test samples of SYNROC D were prepared, characterized, and tested at LLNL; encapsulation of glass marbles with lead or lead alloys was demonstrated on an engineering scale at PNL; a canister for reference Commercial HLW was designed at PNL; a study of the optimization of salt-crete was completed at SRL; a risk assessment showed that an investment for tornado dampers in the interim storage building of the DWPF is unjustified.

Effect of preconditioning on silver leaching and bromide removal properties of silver-impregnated activated carbon (SIAC).

PubMed

Rajaeian, Babak; Allard, Sébastien; Joll, Cynthia; Heitz, Anna

2018-07-01

Silver impregnated activated carbon (SIAC) has been found to be effective in mitigating the formation of brominated-disinfection by products during drinking water treatment. However, there are still uncertainties regarding its silver leaching properties, and strategies for the prevention of silver leaching have remained elusive. This study focused on the evaluation of one type of commercially available SIAC for its ability to remove bromide while minimising silver leaching from the material. Both synthetic and real water matrices were tested. Depending on solution pH, it was found that changing the surface charge properties of SIAC, as measured by the point of zero charge pH, can result in additional bromide removal while minimising the extent of silver leaching. To better understand the mechanism of silver leaching from the SIAC, eight preconditioning environments, i.e. variable pH and ionic strength were tested for a fixed amount of SIAC and two preconditioning environments were selected for a more detailed investigation. Experiments carried out in synthetic water showed that preconditioning at pH 10.4 did not deteriorate the capacity of SIAC to remove bromide, but significantly decreased the release of silver in the form of ionic silver (Ag + ), silver bromide (AgBr) and silver chloride (AgCl) from 40% for the pristine to 3% for the treated SIAC. This was confirmed using a groundwater sample. These results suggest that preconditioned SIAC has the potential to be an effective method for bromide removal with minimised silver leaching in a long-term field application for drinking water production. Copyright © 2018 Elsevier Ltd. All rights reserved.

Bioleaching of arsenic from highly contaminated mine tailings using Acidithiobacillus thiooxidans.

PubMed

Lee, Eunseong; Han, Yosep; Park, Jeonghyun; Hong, Jeongsik; Silva, Rene A; Kim, Seungkon; Kim, Hyunjung

2015-01-01

The behavior of arsenic (As) bioleaching from mine tailings containing high amount of As (ca. 34,000 mg/kg) was investigated using Acidithiobacillus thiooxidans to get an insight on the optimal conditions that would be applied to practical heap and/or tank bioleaching tests. Initial pH (1.8-2.2), temperature (25-40 °C), and solid concentration (0.5-4.0%) were employed as experimental parameters. Complementary characterization experiments (e.g., XRD, SEM-EDS, electrophoretic mobility, cell density, and sulfate production) were also carried out to better understand the mechanism of As bioleaching. The results showed that final As leaching efficiency was similar regardless of initial pH. However, greater initial As leaching rate was observed at initial pH 1.8 than other conditions, which could be attributed to greater initial cell attachment to mine tailings. Unlike the trend observed when varying the initial pH, the final As leaching efficiency varied with the changes in temperature and solid concentration. Specifically, As leaching efficiency tended to decrease with increasing temperature due to the decrease in the bacterial growth rate at higher temperature. Meanwhile, As leaching efficiency tended to increase with decreasing solid concentration. The results for jarosite contents in mine tailings residue after bioleaching revealed that much greater amount of the jarosite was formed during the bioleaching reaction at higher solid concentration, suggesting that the coverage of the surface of the mine tailings by jarosite and/or the co-precipitation of the leached As with jarosite could be a dominant factor reducing As leaching efficiency. Copyright © 2014 Elsevier Ltd. All rights reserved.

[Effect of acidification on the dewaterability of sewage sludge in bioleaching].

PubMed

Zhu, Hai-Feng; Zhou, Li-Xiang; Wang, Dian-Zhan

2012-03-01

Batch experiments were performed to exploit the effect and the mechanism of bioleaching on sludge dewaterability by the inoculation of Acidithiobacillus ferrooxidans LX5 in this study. Besides, chemical leaching experiments using sulphuric acid were also performed as control to study the effect of acidification on sludge dewaterability. During the processes of both biological and chemical leaching, Zeta potential, cell lyses, morphology and structure of sludge flocs were monitored. Results showed that along with the acid production and hence the decrease of pH during bioleaching, the specific resistance of bioleached sludge decreased systematically from 1.81 x 10(12) m x kg(-1) to 0.59 x 10(12) m x kg(-1), whilst Zeta potential increased from -25.2 mV to 9.6 mV, and the natural sedimentation rate increased to as high as 48% at pH 2.90. In chemical leaching, the specific resistance decreased continuously to a minimum value of 2.6 x 10(12) m x kg(-1) at pH 3.35 and then started to increase. Zeta potential increased with the decrease of pH, and reached zero at pH 2.90. At strong acid condition, sludge cells could be decomposed, resulting in the increase of total dissolved phosphorus in centrifugal liquor of chemical leached sludge. However, this phenomenon was not observed in bioleaching process because that the phosphorus was utilized by the abundant microorganism in system. Observation by SEM showed that there was no obvious change in the flocs structure of both sludge at pH 3.35 except for that some secondary minerals appeared only in bioleached sludge. These results revealed that decrease of absolute value of Zeta potential and formation of secondary minerals caused by bioleaching were responsible for the improvement of sludge dewaterability.

Biodegradable hydrogel derived from cellulose acetate and EDTA as a reduction substrate of leaching NPK compound fertilizer and water retention in soil.

PubMed

Senna, André M; Botaro, Vagner R

2017-08-28

To study the behavior of a biodegradable hydrogel derived from cellulose acetate and ethylenediaminetetraacetic dianhydride (EDTAD), as a reduction substrate of NPK fertilizer in soil. The biodegradable hydrogel (HEDTA) was prepared from cellulose acetate (CA) with a degree substitution (DS) 2.5 by esterification crosslinking with EDTAD catalyzed by triethylamine. We systematically investigated the performance of the HEDTA in the reducing NPK (Ammonium, phosphate and potassium) fertilizer leaching. We also compare the percentage of leaching between the HEDTA and commercial fertilizers. To characterize the esterification and crosslinking between CA and EDTAD, FTIR spectroscopy and thermogravimetric analysis (DTG) were employed. The biodegradation experiments were carried out in simulated soil (23% of sand, 23% of cattle manure, 23% of soil and 31% of water) and the HEDTA was tested in the eucalyptus planting during the dry season in the São Paulo state, Brazil. The HEDTA was able to reduce the leaching of fertilizers and improve the performance of eucalyptus seedlings and reduced the mortality of the seedlings. The HEDTA showed to be an excellent substrate for slow release and water-retention in soil, reducer of the fertilizers leaching, in addition being nontoxic, biodegradable in the soil and environmentally-friendly. Copyright © 2017 Elsevier B.V. All rights reserved.

Hydrogen sulfide production by sulfate-reducing bacteria utilizing additives eluted from plastic resins.

PubMed

Tsuchida, Daisuke; Kajihara, Yusuke; Shimidzu, Nobuhiro; Hamamura, Kengo; Nagase, Makoto

2011-06-01

In the present study it was demonstrated that organic additives eluted from plastic resins could be utilized as substrates by sulfate-reducing bacteria. Two laboratory-scale experiments, a microcosm experiment and a leaching experiment, were conducted using polyvinyl chloride (PVC) as a model plastic resin. In the former experiment, the conversion of sulfate to sulfide was evident in microcosms that received plasticized PVC as the sole carbon source, but not in those that received PVC homopolymer. Additionally, dissolved organic carbon accumulated only in microcosms that received plasticized PVC, indicating that the dissolved organic carbon originated from additives. In the leaching experiment, phenol and bisphenol A were found in the leached solutions. These results suggest that the disposal of waste plastics in inert waste landfills may result in the production of H(2)S.

Gold Leaching Characteristics and Intensification of a High S and As-Bearing Gold Concentrate

NASA Astrophysics Data System (ADS)

Yang, Yong-bin; Liu, Xiao-liang; Jiang, Tao; Li, Qian; Xu, Bin; Zhang, Yan

Some high sulfur and arsenic-bearing gold concentrate has a gold leaching rate less than 80% by oxidation roasting-pickling-cyanidation process. The characteristics and intensification of gold leaching were studied systemically. By combining chemical composition and phase analysis, the low gold leaching rate was found to lie in the capsulation of gold by iron-containing phases including iron oxides, arsenopyrite and pyrite. 96.66% of gold in the industrial leaching residue was capsulated and 95.88% of the capsulated turned out to be in the iron-containing phases. The results of laboratory pickling-cyanidation experiments on the calcine and industrial leaching residue presented further demonstration for the fact that gold capsulated in the iron-containing phases was hard to be leached. However, the gold cyanide leaching rate of calcine could be raised over 95% by a reduction roasting-pickling pretreatment which played such a significant role in exposing the capsulated gold that gold leaching was intensified remarkably.

Detoxification of mercury pollutant leached from spent fluorescent lamps using bacterial strains.

PubMed

Al-Ghouti, Mohammad A; Abuqaoud, Reem H; Abu-Dieyeh, Mohammed H

2016-03-01

The spent fluorescent lamps (SFLs) are being classified as a hazardous waste due to having mercury as one of its main components. Mercury is considered the second most toxic heavy metal (arsenic is the first) with harmful effects on animal nervous system as it causes different neurological disorders. In this research, the mercury from phosphor powder was leached, then bioremediated using bacterial strains isolated from Qatari environment. Leaching of mercury was carried out with nitric and hydrochloric acid solutions using two approaches: leaching at ambient conditions and microwave-assisted leaching. The results obtained from this research showed that microwave-assisted leaching method was significantly better in leaching mercury than the acid leaching where the mercury leaching efficiency reached 76.4%. For mercury bio-uptake, twenty bacterial strains (previously isolated and purified from petroleum oil contaminated soils) were sub-cultured on Luria Bertani (LB) plates with mercury chloride to check the bacterial tolerance to mercury. Seven of these twenty strains showed a degree of tolerance to mercury. The bio-uptake capacities of the promising strains were investigated using the mercury leached from the fluorescent lamps. Three of the strains (Enterobacter helveticus, Citrobacter amalonaticus, and Cronobacter muytjensii) showed bio-uptake efficiency ranged from 28.8% to 63.6%. Copyright © 2015 Elsevier Ltd. All rights reserved.

[Characteristics of Adsorption Leaching and Influencing Factors of Dimethyl Phthalate in Purple Soil].

PubMed

Wang, Qiang; Song, Jiao-yan; Zeng, Wei; Wang, Fa

2016-02-15

The typical soil-purple soil in Three Gorges Reservoir was the tested soil, the characteristics of adsorption leaching of dimethyl phthalate (DMP) in contaminated water by the soil, and the influencing factors in the process were conducted using soil column leaching experiment. The results showed that the parabolic equation was the best equation describing adsorption kinetics of DMP by soils. The concentration of DMP in the leaching solution had significant effect on the adsorption amounts of DMP. With the increasing concentration of DMP in the leaching solution, the adsorption capacities of DMP by purple soil increased linearly. The ionic strength and pH in leaching solution had significant effects on adsorption of DMP. On the whole, increasing of the ionic strength restrained the adsorption. The adsorption amounts at pH 5.0-7.0 were more than those under other pH condition. The addition of exogenous organic matter (OM) in purple soil increased the adsorption amount of DMP by purple soil. However, the adsorption amount was less than those with other addition amounts of exogenous OM when the addition of exogenous OM was too high (> or = 30 g x kg(-1)). The addition of surfactant sodium dodecylbenzene sulfonic acid (SDBS) in purple soil increased the adsorption amount of DMP by purple soil. The adsorption amount was maximal when the addition amount of SDBS was 50 mg x kg(-1). However, the adsorption amounts decreased with increasing addition amounts of SDBS although the adsorption amounts were still more than that of the control group, and the adsorption amount was almost equal to that of the control group when the addition amount of SDBS was 800 mg x kg(-1). Continuous leaching time affected the vertical distribution of DMP in the soil column. When the leaching time was shorter, the upper soil column adsorbed more DMP, while the DMP concentrations in upper and lower soil columns became similar with the extension of leaching time.

Characterization of interactions between soil solid phase and soil solution in the initial ecosystem development phase

NASA Astrophysics Data System (ADS)

Zimmermann, Claudia; Schaaf, Wolfgang

2010-05-01

In the initial phase of soil formation interactions between solid and liquid phases and processes like mineral weathering, formation of reactive surfaces and accumulation of organic matter play a decisive role in developing soil properties. As part of the Transregional Collaborative Research Centre (SFB/TRR 38) 'Patterns and processes of initial ecosystem development' in an artificial catchment, these interactions are studied at the catchment 'Chicken Creek' (Gerwin et al. 2009). To link the interactions between soil solid phase and soil solution at the micro-scale with observed processes at the catchment scale, microcosm experiments under controlled laboratory conditions were carried out. Main objectives were to determine the transformation processes of C and N from litter decomposition within the gaseous, liquid and solid phase, the interaction with mineral surfaces and its role for the establishment of biogeochemical cycles. The microcosm experiments were established in a climate chamber at constant 10 ° C. In total 48 soil columns (diameter: 14.4 cm; height: 30 cm) were filled with two different quaternary substrates (sand and loamy sand) representing the textural variation within the catchment at a bulk density of 1.4-1.5 g*cm-3. The columns were automatically irrigated four times a day with 6.6 ml each (corresponding to 600 mm*yr-1). The gaseous phase in the headspace of the microcosms was analysed continuously for CO2 and N2O contents. C and N transformation processes were studied using 13C and 15N labelled litter of two different plant species occurring at the catchment (Lotus corniculatus, Calamagrostis epigejos) that was incorporated into the microcosm surface. All treatments including a control ran with four replicates over a period of 40 weeks. Two additional microcosms act as pure litter controls where substrate was replaced by glass pearls. Litter and substrate were analysed before and after the experiment. Percolate was continuously collected and analyzed in two weeks intervals for C and N contents (including δ13C), pH and ion concentrations. The results show that the initial phase of the experiment is characterized by intensive leaching of C and N from the litter and transformation as well as leaching from the substrate. Calcium leaching is caused mainly by carbonate dissolution from the substrates. In contrast, magnesium and especially potassium are leached in initially high amounts from the litter, but are strongly retained in the soil. The addition of litter promotes microbial CO2 production as shown by a strong increase of respiration due to easily available organic substances at the beginning of the experiment. Litter of L. corniculatus induced also a high initial peak in N2O emission as well as higher nitrification and NO3-N leaching. Leaching of DOC and TDN was clearly affected by the substrate texture, illustrated by intensive DOC leaching from the sand at the beginning of the experiment but shifting later to higher leaching rates from the loamy sand. References: Gerwin W, Schaaf W, Biemelt D, Fischer A, Winter S, Hüttl RF (2009) The artificial catchment 'Chicken Creek' (Lusatia, Germany) - a landscape laboratory for interdisciplinary studies of initial ecosystem development. Ecolological Engineering 35, 1786-1796.

Different low-molecular-mass organic acids specifically control leaching of arsenic and lead from contaminated soil.

PubMed

Ash, Christopher; Tejnecký, Václav; Borůvka, Luboš; Drábek, Ondřej

2016-04-01

Low-molecular-mass organic acids (LMMOA) are of key importance for mobilisation and fate of metals in soil, by functioning as ligands that increase the amount of dissolved metal in solution or by dissociation of metal binding minerals. Column leaching experiments were performed on soil polluted with As and Pb, in order to determine the specificity of LMMOA related release for individual elements, at varying organic acid concentrations. Acetic, citric and oxalic acids were applied in 12h leaching experiments over a concentration range (0.5-25 mM) to soil samples that represent organic and mineral horizons. The leaching of As followed the order: oxalic>citric>acetic acid in both soils. Arsenic leaching was attributed primarily to ligand-enhanced dissolution of mineral oxides followed by As released into solution, as shown by significant correlation between oxalic and citric acids and content of Al and Fe in leaching solutions. Results suggest that subsurface mineral soil layers are more vulnerable to As toxicity. Leaching of Pb from both soils followed the order: citric>oxalic>acetic acid. Mineral soil samples were shown to be more susceptible to leaching of Pb than samples characterised by a high content of organic matter. The leaching efficiency of citric acid was attributed to formation of stable complexes with Pb ions, which other acids are not capable of. Results obtained in the study are evidence that the extent of As and Pb leaching in contaminated surface and subsurface soil depends significantly on the types of carboxylic acid involved. The implications of the type of acid and the specific element that can be mobilised become increasingly significant where LMMOA concentrations are highest, such as in rhizosphere soil. Copyright © 2016 Elsevier B.V. All rights reserved.

Leaching of CCA-treated wood: implications for waste disposal.

PubMed

Townsend, Timothy; Tolaymat, Thabet; Solo-Gabriele, Helena; Dubey, Brajesh; Stook, Kristin; Wadanambi, Lakmini

2004-10-18

Leaching of arsenic, chromium, and copper from chromated copper arsenate (CCA)-treated wood poses possible environmental risk when disposed. Samples of un-weathered CCA-treated wood were tested using a variety of the US regulatory leaching procedures, including the toxicity characteristic leaching procedure (TCLP), synthetic precipitation leaching procedure (SPLP), extraction procedure toxicity method (EPTOX), waste extraction test (WET), multiple extraction procedure (MEP), and modifications of these procedures which utilized actual MSW landfill leachates, a construction and demolition (C and D) debris leachate, and a concrete enhanced leachate. Additional experiments were conducted to assess factors affecting leaching, such as particle size, pH, and leaching contact time. Results from the regulatory leaching tests provided similar results with the exception of the WET, which extracted greater quantities of metals. Experiments conducted using actual MSW leachate, C and D debris leachate, and concrete enhanced leachate provided results that were within the same order of magnitude as results obtained from TCLP, SPLP, and EPTOX. Eleven of 13 samples of CCA-treated dimensional lumber exceeded the US EPA's toxicity characteristic (TC) threshold for arsenic (5 mg/L). If un-weathered arsenic-treated wood were not otherwise excluded from the definition of hazardous waste, it frequently would require management as such. When extracted with simulated rainwater (SPLP), 9 of the 13 samples leached arsenic at concentrations above 5 mg/L. Metal leachability tended to increase with decreasing particle size and at pH extremes. All three metals leached above the drinking water standards thus possibly posing a potential risk to groundwater. Arsenic is a major concern from a disposal point of view with respect to ground water quality.

Comparison of ultrasonic-assisted and regular leaching of germanium from by-product of zinc metallurgy.

PubMed

Zhang, Libo; Guo, Wenqian; Peng, Jinhui; Li, Jing; Lin, Guo; Yu, Xia

2016-07-01

A major source of germanium recovery and also the source of this research is the by-product of lead and zinc metallurgical process. The primary purpose of the research is to investigate the effects of ultrasonic assisted and regular methods on the leaching yield of germanium from roasted slag containing germanium. In the study, the HCl-CaCl2 mixed solution is adopted as the reacting system and the Ca(ClO)2 used as the oxidant. Through six single factor (leaching time, temperature, amount of Ca(ClO)2, acid concentration, concentration of CaCl2 solution, ultrasonic power) experiments and the comparison of the two methods, it is found the optimum collective of germanium for ultrasonic-assisted method is obtained at temperature 80 °C for a leaching duration of 40 min. The optimum concentration for hydrochloric acid, CaCl2 and oxidizing agent are identified to be 3.5 mol/L, 150 g/L and 58.33 g/L, respectively. In addition, 700 W is the best ultrasonic power and an over-high power is adverse in the leaching process. Under the optimum condition, the recovery of germanium could reach up to 92.7%. While, the optimum leaching condition for regular leaching method is same to ultrasonic-assisted method, except regular method consume 100 min and the leaching rate of Ge 88.35% is lower about 4.35%. All in all, the experiment manifests that the leaching time can be reduced by as much as 60% and the leaching rate of Ge can be increased by 3-5% with the application of ultrasonic tool, which is mainly thanks to the mechanical action of ultrasonic. Copyright © 2015 Elsevier B.V. All rights reserved.

Different low-molecular-mass organic acids specifically control leaching of arsenic and lead from contaminated soil

NASA Astrophysics Data System (ADS)

Ash, Christopher; Tejnecký, Václav; Borůvka, Luboš; Drábek, Ondřej

2016-04-01

Low-molecular-mass organic acids (LMMOA) are of key importance for mobilisation and fate of metals in soil, by functioning as ligands that increase the amount of dissolved metal in solution or by dissociation of metal binding minerals. Column leaching experiments were performed on soil polluted with As and Pb, in order to determine the specificity of LMMOA related release for individual elements, at varying organic acid concentrations. Acetic, citric and oxalic acids were applied in 12 h leaching experiments over a concentration range (0.5-25 mM) to soil samples that represent organic and mineral horizons. The leaching of As followed the order: oxalic > citric > acetic acid in both soils. Arsenic leaching was attributed primarily to ligand-enhanced dissolution of mineral oxides followed by As released into solution, as shown by significant correlation between oxalic and citric acids and content of Al and Fe in leaching solutions. Results suggest that subsurface mineral soil layers are more vulnerable to As toxicity. Leaching of Pb from both soils followed the order: citric > oxalic > acetic acid. Mineral soil samples were shown to be more susceptible to leaching of Pb than samples characterised by a high content of organic matter. The leaching efficiency of citric acid was attributed to formation of stable complexes with Pb ions, which other acids are not capable of. Results obtained in the study are evidence that the extent of As and Pb leaching in contaminated surface and subsurface soil depends significantly on the types of carboxylic acid involved. The implications of the type of acid and the specific element that can be mobilised become increasingly significant where LMMOA concentrations are highest, such as in rhizosphere soil.

Bioleaching of two different genetic types of chalcopyrite and their comparative mineralogical assessment.

PubMed

Deng, Sha; Gu, Guohua; Ji, Jing; Xu, Baoke

2018-02-01

The bioleaching of two different genetic types of chalcopyrite by the moderate thermophile Sulfobacillus thermosulfidooxidans was investigated by leaching behaviors elucidation and their comparative mineralogical assessment. The leaching experiment showed that the skarn-type chalcopyrite (STC) revealed a much faster leaching rate with 33.34% copper extracted finally, while only 23.53% copper was bioleached for the porphyry-type chalcopyrite (PTC). The mineralogical properties were analyzed by XRD, SEM, XPS, and Fermi energy calculation. XRD indicated that the unit cell volume of STC was a little larger than that of PTC. SEM indicated that the surface of STC had more steps and ridges. XPS spectra showed that Cu(I) was the dominant species of copper on the surfaces of the two chalcopyrite samples, and STC had much more copper with lower Cu 2p 3/2 binding energy. Additionally, the Fermi energy of STC was much higher than that of PTC. These mineralogical differences were in good agreement with the bioleaching behaviors of chalcopyrite. This study will provide some new information for evaluating the oxidation kinetics of chalcopyrite.

Modeling nitrate leaching and optimizing water and nitrogen management under irrigated maize in desert oases in Northwestern China.

PubMed

Hu, Kelin; Li, Yong; Chen, Weiping; Chen, Deli; Wei, Yongping; Edis, Robert; Li, Baoguo; Huang, Yuanfang; Zhang, Yuanpei

2010-01-01

Understanding water and N transport through the soil profile is important for efficient irrigation and nutrient management to minimize nitrate leaching to the groundwater, and to promote agricultural sustainable development in desert oases. In this study, a process-based water and nitrogen management model (WNMM) was used to simulate soil water movement, nitrate transport, and crop growth (maize [Zea mays L.]) under desert oasis conditions in northwestern China. The model was calibrated and validated with a field experiment. The model simulation results showed that about 35% of total water input and 58% of the total N input were leached to <1.8 m depth under traditional management practice. Excessive irrigation and N fertilizer application, high nitrate concentration in the irrigation water, together with the sandy soil texture, resulted in large nitrate leaching. Nitrate leaching was significantly reduced under the improved management practice suggested by farm extension personnel; however, the water and nitrate inputs still far exceeded the crop requirements. More than 1700 scenarios combining various types of irrigation and fertilizer practices were simulated. Quantitative analysis was conducted to obtain the best management practices (BMPs) with simultaneous consideration of crop yield, water use efficiency, fertilizer N use efficiency, and nitrate leaching. The results indicated that the BMPs under the specific desert oasis conditions are to irrigate the maize with 600 mm of water in eight times with a single fertilizer application at a rate of 75 kg N ha(-1).

Leaching potential of pervious concrete and immobilization of Cu, Pb and Zn using pervious concrete.

PubMed

Solpuker, U; Sheets, J; Kim, Y; Schwartz, F W

2014-06-01

This paper investigates the leaching potential of pervious concrete and its capacity for immobilizing Cu, Pb and Zn, which are common contaminants in urban runoff. Batch experiments showed that the leachability of Cu, Pb and Zn increased when pH<8. According to PHREEQC equilibrium modeling, the leaching of major ions and trace metals was mainly controlled by the dissolution/precipitation and surface complexation reactions, respectively. A 1-D reactive transport experiment was undertaken to better understand how pervious concrete might function to attenuate contaminant migration. A porous concrete block was sprayed with low pH water (pH=4.3±0.1) for 190 h. The effluent was highly alkaline (pH~10 to 12). In the first 50 h, specific conductance and trace-metal were high but declined towards steady state values. PHREEQC modeling showed that mixing of interstitial alkaline matrix waters with capillary pore water was required in order to produce the observed water chemistry. The interstitial pore solutions seem responsible for the high pH values and relatively high concentrations of trace metals and major cations in the early stages of the experiment. Finally, pervious concrete was sprayed with a synthetic contaminated urban runoff (10 ppb Cu, Pb and Zn) with a pH of 4.3±0.1 for 135 h. It was found that Pb immobilization was greater than either Cu or Zn. Zn is the most mobile among three and also has the highest variation in the observed degree of immobilization. Copyright © 2014 Elsevier B.V. All rights reserved.

Synthesis and characterization of poly(3-sulfopropylmethacrylate) brushes for potential antibacterial applications.

PubMed

Ramstedt, Madeleine; Cheng, Nan; Azzaroni, Omar; Mossialos, Dimitris; Mathieu, Hans Jörg; Huck, Wilhelm T S

2007-03-13

This article describes the aqueous atom transfer radical polymerization synthesis of poly(3-sulfopropylmethacrylate) brushes onto gold and Si/SiO2 surfaces in a controlled manner. The effect of Cu(I)/Cu(II) ratio was examined, and a quartz crystal microbalance was used to study the kinetics of the brush synthesis. The synthesized brushes displayed a thickness from a few nanometers to several hundred nanometers and were characterized using atomic force microscopy, ellipsometry, Fourier transform infrared spectroscopy (FTIR), contact angle measurements, and X-ray photoelectron spectroscopy (XPS). The as-synthesized sulfonate brushes had very good ion-exchange properties for the ions tested in this study, i.e., Na+, K+, Cu2+, and Ag+. FTIR and XPS show that the metal ions are coordinating to sulfonate moieties inside the brushes. The brushes were easily loaded with silver ions, and the effect of silver ion concentration on silver loading of the brush was examined. The silver-loaded brushes were shown to be antibacterial toward both gram negative and gram positive bacteria. The silver leaching was studied through leaching experiments into water, NaNO3, and NaCl (physiological medium). The results from these leaching experiments are compared and discussed in the article.

Evaluation of Pollutant Leaching Potential of Coal Ashes for Recycling

NASA Astrophysics Data System (ADS)

Park, D.; Woo, N. C.; Kim, H.; Yoon, H.; Chung, D.

2011-12-01

By 2009, coal ashes produced from coal-based power plants in Korea have been reused as cement supplement materials; however, the rest is mostly disposed in landfills inside the plant properties. Continuous production of coal ashes and limited landfill sites require more recycles of coal ashes as base materials, specifically in constructions of roads and of huge industrial complex. Previous researches showed that coal ashes could contain various metals such as arsenic(As), chromium(Cr), lead(Pb), nickel(Ni), selenium(Se), etc. In this study, we collected four types of bottom ashes and two of fly ashes from four coal-based power plants. These ash samples were tested with distilled water through the column leaching process in oxidized conditions. The column test results were compared with those of total digestion, sequential extraction processes and TCLP. Concentrations of metals in outflows from columns are generally greater in fly ashes than in bottom ashes, specifically for As, Se, B, Sr and SO4. Only one fly ash (J2-F) shows high concentrations of arsenic and selenium in leachate. Sequential extraction results indicate that these metals are in readily soluble forms, such as adsorbed, carbonated, and reducible forms. Results of TCLP analysis indicate no potential contaminants leached from the ashes. In conclusion, recycling of coal combustion ashes could be encouraged with proper tests such as sequential and leaching experiments.

Comparative study on copper leaching from waste printed circuit boards by typical ionic liquid acids.

PubMed

Chen, Mengjun; Huang, Jinxiu; Ogunseitan, Oladele A; Zhu, Nengming; Wang, Yan-min

2015-07-01

Waste printed circuit boards (WPCBs) are attracting increasing concerns because the recovery of its content of valuable metallic resources is hampered by the presence of hazardous substances. In this study, we used ionic liquids (IL) to leach copper from WPCBs. [BSO3HPy]OTf, [BSO3HMIm]OTf, [BSO4HPy]HSO4, [BSO4HMim]HSO4 and [MIm]HSO4 were selected. Factors that affect copper leaching rate were investigated in detail and their leaching kinetics were also examined with the comparison of [Bmim]HSO4. The results showed that all six IL acids could successfully leach copper out, with near 100% recovery. WPCB particle size and leaching time had similar influences on copper leaching performance, while IL acid concentration, hydrogen peroxide addition, solid to liquid ratio, temperature, showed different influences. Moreover, IL acid with HSO4(-) was more efficient than IL acid with CF3SO3(-). These six IL acids indicate a similar behavior with common inorganic acids, except temperature since copper leaching rate of some IL acids decreases with its increase. The results of leaching kinetics studies showed that diffusion plays a more important role than surface reaction, whereas copper leaching by inorganic acids is usually controlled by surface reaction. This innovation provides a new option for recovering valuable materials such as copper from WPCBs. Copyright © 2015 Elsevier Ltd. All rights reserved.

Regional modelling of nitrate leaching from Swiss organic and conventional cropping systems under climate change

NASA Astrophysics Data System (ADS)

Calitri, Francesca; Necpalova, Magdalena; Lee, Juhwan; Zaccone, Claudio; Spiess, Ernst; Herrera, Juan; Six, Johan

2016-04-01

Organic cropping systems have been promoted as a sustainable alternative to minimize the environmental impacts of conventional practices. Relatively little is known about the potential to reduce NO3-N leaching through the large-scale adoption of organic practices. Moreover, the potential to mitigate NO3-N leaching and thus the N pollution under future climate change through organic farming remain unknown and highly uncertain. Here, we compared regional NO3-N leaching from organic and conventional cropping systems in Switzerland using a terrestrial biogeochemical process-based model DayCent. The objectives of this study are 1) to calibrate and evaluate the model for NO3-N leaching measured under various management practices from three experiments at two sites in Switzerland; 2) to estimate regional NO3-N leaching patterns and their spatial uncertainty in conventional and organic cropping systems (with and without cover crops) for future climate change scenario A1B; 3) to explore the sensitivity of NO3-N leaching to changes in soil and climate variables; and 4) to assess the nitrogen use efficiency for conventional and organic cropping systems with and without cover crops under climate change. The data for model calibration/evaluation were derived from field experiments conducted in Liebefeld (canton Bern) and Eschikon (canton Zürich). These experiments evaluated effects of various cover crops and N fertilizer inputs on NO3-N leaching. The preliminary results suggest that the model was able to explain 50 to 83% of the inter-annual variability in the measured soil drainage (RMSE from 12.32 to 16.89 cm y-1). The annual NO3-N leaching was also simulated satisfactory (RMSE = 3.94 to 6.38 g N m-2 y-1), although the model had difficulty to reproduce the inter-annual variability in the NO3-N leaching losses correctly (R2 = 0.11 to 0.35). Future climate datasets (2010-2099) from the 10 regional climate models (RCM) were used in the simulations. Regional NO3-N leaching predictions for conventional cropping system with a three years rotation (silage maize, potatoes and winter wheat) in Zurich and Bern cantons varied from 6.30 to 16.89 g N m-2 y-1 over a 30-years period. Further simulations and analyses will follow to provide insights into understanding of driving variables and patterns of N losses by leaching in response to changes from conventional to organic cropping systems, and climate change.

Leaching Behavior of Slags from AN Old Lead Smelter in Chihuahua, Mexico: Metals, Chlorides, Nitrates, Sulfates and Tds Analyses

NASA Astrophysics Data System (ADS)

Espejel-Garcia, D.; Wenglas-Lara, G.; Villalobos-Aragon, A.; Espejel-Garcia, V. V.

2013-05-01

Waste materials (such as, smelter slags, waste glass, tires, plastics, rubbish, ashes, etc.), have a large potential to substitute natural materials, reducing costs, especially for the construction industry. Smelter slags are resistant and have better compression strength values in comparison to natural aggregates, and generally are far beyond of what the standard ratios need to qualify a material as a good one for construction. But this material has a big problem within it: the existence of toxic elements and compounds in high concentrations, which means that water and soil contamination can be present after water infiltrates through this material; so we perform leaching experiments to characterize and measure the possible contamination under controlled conditions. To perform the slags-leaching experiments, we used an EA-NEN-7375-2004 tank test standard from Netherlands. This test was selected because to our knowledge it is the only one which allows the use of coarse material, as the one utilized in construction. The leaching experiments sampling was performed at different times: 6, 24, 168 and 360 hours, to compare the leachate concentration at the two different pH's values (5 and 8) selected to simulate real conditions. For the leaching experiments, the slags were mixed with natural road base material (gravel-sands from volcanic rocks) at different proportions of 30% and 50%. In order to understand the slags' leaching behavior, other experiments were carried out with the pure material, for both (slags and natural aggregates). After analyses by ICP-OES , the slags from this smelter in Chihuahua contain Pb (0.5 - 4 wt.%), Zn (15-35 wt.%) and As (0.6 wt.%), as well such as: bicarbonates, chlorides, nitrates, sulfates, Mg, K, Na, Ca and TDS. Based on the results of the leaching analyses, via atomic absorption technique, we conclude that Pb and As concentrations are provided by the slags, meanwhile, the bicarbonates, chlorides, Na and Ca are contributed by the road base natural materials. Summarizing, he possibility exists to use the slags as a minor constituent (<30%) in road base materials.

Effect of runoff during production of sweet viburnum

USDA-ARS?s Scientific Manuscript database

Results from this experiment showed that spacing containers at planting instead of later in the season increased leaching losses of N, P, and K on a per-container basis. Regardless of any effects on runoff, spacing plants early decreased plant growth and, therefore, would not be recommended. The fin...

Changes in mineralogical and leaching properties of converter steel slag resulting from accelerated carbonation at low CO2 pressure.

PubMed

van Zomeren, André; van der Laan, Sieger R; Kobesen, Hans B A; Huijgen, Wouter J J; Comans, Rob N J

2011-11-01

Steel slag can be applied as substitute for natural aggregates in construction applications. The material imposes a high pH (typically 12.5) and low redox potential (Eh), which may lead to environmental problems in specific application scenarios. The aim of this study is to investigate the potential of accelerated steel slag carbonation, at relatively low pCO2 pressure (0.2 bar), to improve the environmental pH and the leaching properties of steel slag, with specific focus on the leaching of vanadium. Carbonation experiments are performed in laboratory columns with steel slag under water-saturated and -unsaturated conditions and temperatures between 5 and 90 °C. Two types of steel slag are tested; free lime containing (K3) slag and K1 slag with a very low free lime content. The fresh and carbonated slag samples are investigated using a combination of leaching experiments, geochemical modelling of leaching mechanisms and microscopic/mineralogical analysis, in order to identify the major processes that control the slag pH and resulting V leaching. The major changes in the amount of sequestered CO2 and the resulting pH reduction occurred within 24h, the free lime containing slag (K3-slag) being more prone to carbonation than the slag with lower free lime content (K1-slag). While carbonation at these conditions was found to occur predominantly at the surface of the slag grains, the formation of cracks was observed in carbonated K3 slag, suggesting that free lime in the interior of slag grains had also reacted. The pH of the K3 slag (originally pH±12.5) was reduced by about 1.5 units, while the K1 slag showed a smaller decrease in pH from about 11.7 to 11.1. However, the pH reduction after carbonation of the K3 slag was observed to lead to an increased V-leaching. Vanadium leaching from the K1 slag resulted in levels above the limit values of the Dutch Soil Quality Decree, for both the untreated and carbonated slag. V-leaching from the carbonated K3 slag remained below these limit values at the relatively high pH that remained after carbonation. The V-bearing di-Ca silicate (C2S) phase has been identified as the major source of the V-leaching. It is shown that the dissolution of this mineral is limited in fresh steel slag, but strongly enhanced by carbonation, which causes the observed enhanced release of V from the K3 slag. The obtained insights in the mineral transformation reactions and their effect on pH and V-leaching provide guidance for further improvement of an accelerated carbonation technology. Copyright © 2011 Elsevier Ltd. All rights reserved.

Ion mobility based on column leaching of South African gold tailings dam with chemometric evaluation.

PubMed

Cukrowska, Ewa M; Govender, Koovila; Viljoen, Morris

2004-07-01

New column leaching experiments were designed and used as an alternative rapid screening approach to element mobility assessment. In these experiments, field-moist material was treated with an extracting solution to assess the effects of acidification on element mobility in mine tailings. The main advantage of this version of column leaching experiments with partitioned segments is that they give quick information on current element mobility in conditions closely simulating field conditions to compare with common unrepresentative air-dried, sieved samples used for column leaching experiments. Layers from the tailings dump material were sampled and packed into columns. The design of columns allows extracting leachates from each layer. The extracting solutions used were natural (pH 6.8) and acidified (pH 4.2) rainwater. Metals and anions were determined in the leachates. The concentrations of metals (Ca, Mg, Fe, Mn, Al, Cr, Ni, Co, Zn, and Cu) in sample leachates were determined using ICP OES. The most important anions (NO3-, Cl-, and SO4(2)-) were determined using the closed system izotacophoresis ITP analyser. The chemical analytical data from tailings leaching and physico-chemical data from field measurements (including pH, conductivity, redox potential, temperature) were used for chemometric evaluation of element mobility. Principal factor analysis (PFA) was used to evaluate ions mobility from different layers of tailings dump arising from varied pH and redox conditions. It was found that the results from the partitioned column leaching illustrate much better complex processes of metals mobility from tailings dump than the total column. The chemometric data analysis (PFA) proofed the differences in the various layers leachability that are arising from physico-chemical processes due to chemical composition of tailings dump deposit. Copyright 2004 Elsevier Ltd.

Leachate Testing of Hamlet City Lake, North Carolina, Sediment

DTIC Science & Technology

1992-11-01

release; distribution is unlimited. 13. ABSTRACT (Maximum 200 words) Sediment leaching studies of Hamlet City Lake, Hamlet, NC, were conducted in...laboratories at the U.S. Army Engineer Waterways Experiment Station. The pur- pose of these studies was to provide quantitative information on the...conditions similar to landfarming. The study involved three elements: batch leach tests, column leach tests, and simulations using the Hydrologic

Comparison of ultrasound-assisted and traditional caustic leaching of spent cathode carbon (SCC) from aluminum electrolysis.

PubMed

Xiao, Jin; Yuan, Jie; Tian, Zhongliang; Yang, Kai; Yao, Zhen; Yu, Bailie; Zhang, Liuyun

2018-01-01

The spent cathode carbon (SCC) from aluminum electrolysis was subjected to caustic leaching to investigate the different effects of ultrasound-assisted and traditional methods on element fluorine (F) leaching rate and leaching residue carbon content. Sodium hydroxide (NaOH) dissolved in deionized water was used as the reaction system. Through single-factor experiments and a comparison of two leaching techniques, the optimum F leaching rate and residue carbon content for ultrasound-assisted leaching process were obtained at a temperature of 70°C, residue time of 40min, initial mass ratio of alkali to SCC (initial alkali-to-material ratio) of 0.6, liquid-to-solid ratio of 10mL/g, and ultrasonic power of 400W, respectively. Under the optimal conditions, the leaching residue carbon content was 94.72%, 2.19% larger than the carbon content of traditional leaching residue. Leaching wastewater was treated with calcium chloride (CaCl 2 ) and bleaching powder and the treated wastewater was recycled caustic solution. All in all, benefiting from advantage of the ultrasonication effects, ultrasound-assisted caustic leaching on spent cathode carbon had 55.6% shorter residue time than the traditional process with a higher impurity removal rate. Copyright © 2017 Elsevier B.V. All rights reserved.

Decontamination and decommissioning of the BORAX-V leach pond. Final report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Smith, D.L.

1985-01-01

This report describes the decontamination and decommissioning (D and D) of the BORAX-V leach pond located at the Idaho National Engineering Laboratory (INEL). The leach pond became radioactively contaminated from the periodic discharge of low-level liquid waste during operation of the Boiling Water Reactor Experiments (BORAX) from 1954 to 1964. This report describes work performed to accomplish the D and D objectives of stabilizing the leach pond and preventing the spread of contamination. D and D of the BORAX-V leach pond consisted to backfilling the pond with clean soil, grading and seeding the area, and erecting a permanent marker tomore » identify very low-level subsurface contamination.« less

Preparation of Rutile from Ilmenite Concentrate Through Pressure Leaching with Hydrochloric Acid

NASA Astrophysics Data System (ADS)

Xiang, Junyi; Liu, Songli; Lv, Xuewei; Bai, Chenguang

2017-04-01

Take into account the fact that the natural rutile utilized for the production of titanium dioxide pigment through chloride process is desperately lacking worldwide especially in China, an attempt was exploited for extracting synthetic rutile from Yunnan ilmenite concentrate with hydrochloric acid pressure leaching process. The leaching parameters for one step leaching process were investigated. The results shown that the optimum condition is leaching temperature of 413 K (140 °C), acid concentration of 20 pct HCl, leaching time of 4 hours and liquid/solid mass ratio of 8:1. A two steps leaching process was also suggested to reutilize the leaching liquor which with a high content of HCl. The results showed that the content of HCl decreased from 135 to 75 g/L, total iron increased from 44.5 g/L to about 87.6 g/L, and the liquid/solid mass ratio decreased to 5:1 with a two steps leaching process. The leaching product produced through a two steps leaching process shows a pure golden red with a high content of titanium (92.65 pct TiO2), a relatively low content of calcium (0.10 pct CaO) and magnesium (0.12 pct MgO), but high content of silicon (5.72 pct SiO2).

Photodegradation of octylisothiazolinone and semi-field emissions from facade coatings

NASA Astrophysics Data System (ADS)

Bollmann, Ulla E.; Minelgaite, Greta; Schlüsener, Michael; Ternes, Thomas A.; Vollertsen, Jes; Bester, Kai

2017-01-01

Amongst others, 2-octyl-isothiazol-3(2 H)-one (OIT) is used as film preservative in water-based polymer resin paints and renders to prevent the growth of moulds and bacteria. It is known that biocides leach from facades with rainwater and end up in the environment via stormwater runoff. In the present study the leaching and fate of OIT used in facade coatings was determined under natural conditions. Potential phototransformation products were initially identified in laboratory experiments using UV-light. Afterwards, the leaching of OIT and seven degradation products were studied on artificial walls equipped with organic top coatings formulated with OIT. A mass balance, including the leached and remaining amounts of OIT and its seven transformation products, can explain up to 40% of the initial amount of OIT. The OIT remaining in the material after 1.5 yr is by far the largest fraction. The study shows that in the assessment of biocides in coating material, transformation products need to be taken into account both in leachate and remaining in the material. Furthermore, in case of volatile degradation products, the emissions to air might be relevant.

Photodegradation of octylisothiazolinone and semi-field emissions from facade coatings.

PubMed

Bollmann, Ulla E; Minelgaite, Greta; Schlüsener, Michael; Ternes, Thomas A; Vollertsen, Jes; Bester, Kai

2017-01-27

Amongst others, 2-octyl-isothiazol-3(2 H)-one (OIT) is used as film preservative in water-based polymer resin paints and renders to prevent the growth of moulds and bacteria. It is known that biocides leach from facades with rainwater and end up in the environment via stormwater runoff. In the present study the leaching and fate of OIT used in facade coatings was determined under natural conditions. Potential phototransformation products were initially identified in laboratory experiments using UV-light. Afterwards, the leaching of OIT and seven degradation products were studied on artificial walls equipped with organic top coatings formulated with OIT. A mass balance, including the leached and remaining amounts of OIT and its seven transformation products, can explain up to 40% of the initial amount of OIT. The OIT remaining in the material after 1.5 yr is by far the largest fraction. The study shows that in the assessment of biocides in coating material, transformation products need to be taken into account both in leachate and remaining in the material. Furthermore, in case of volatile degradation products, the emissions to air might be relevant.

Photodegradation of octylisothiazolinone and semi-field emissions from facade coatings

PubMed Central

Bollmann, Ulla E.; Minelgaite, Greta; Schlüsener, Michael; Ternes, Thomas A.; Vollertsen, Jes; Bester, Kai

2017-01-01

Amongst others, 2-octyl-isothiazol-3(2 H)-one (OIT) is used as film preservative in water-based polymer resin paints and renders to prevent the growth of moulds and bacteria. It is known that biocides leach from facades with rainwater and end up in the environment via stormwater runoff. In the present study the leaching and fate of OIT used in facade coatings was determined under natural conditions. Potential phototransformation products were initially identified in laboratory experiments using UV-light. Afterwards, the leaching of OIT and seven degradation products were studied on artificial walls equipped with organic top coatings formulated with OIT. A mass balance, including the leached and remaining amounts of OIT and its seven transformation products, can explain up to 40% of the initial amount of OIT. The OIT remaining in the material after 1.5 yr is by far the largest fraction. The study shows that in the assessment of biocides in coating material, transformation products need to be taken into account both in leachate and remaining in the material. Furthermore, in case of volatile degradation products, the emissions to air might be relevant. PMID:28128314

Changes in mineralogical and leaching properties of converter steel slag resulting from accelerated carbonation at low CO{sub 2} pressure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zomeren, Andre van; Laan, Sieger R. van der; Kobesen, Hans B.A.

2011-11-15

Highlights: > Accelerated carbonation studied to improve environmental properties of steel slag. > Carbonation found to occur predominantly at surface of the steel slag grains. > Combined geochemical modelling and mineral analysis revealed controlling processes. > Enhanced V-leaching with di-Ca silicate (C2S) dissolution identified as major source. > Identified mineral transformations provide guidance for further quality improvement. - Abstract: Steel slag can be applied as substitute for natural aggregates in construction applications. The material imposes a high pH (typically 12.5) and low redox potential (Eh), which may lead to environmental problems in specific application scenarios. The aim of this studymore » is to investigate the potential of accelerated steel slag carbonation, at relatively low pCO{sub 2} pressure (0.2 bar), to improve the environmental pH and the leaching properties of steel slag, with specific focus on the leaching of vanadium. Carbonation experiments are performed in laboratory columns with steel slag under water-saturated and -unsaturated conditions and temperatures between 5 and 90 {sup o}C. Two types of steel slag are tested; free lime containing (K3) slag and K1 slag with a very low free lime content. The fresh and carbonated slag samples are investigated using a combination of leaching experiments, geochemical modelling of leaching mechanisms and microscopic/mineralogical analysis, in order to identify the major processes that control the slag pH and resulting V leaching. The major changes in the amount of sequestered CO{sub 2} and the resulting pH reduction occurred within 24 h, the free lime containing slag (K3-slag) being more prone to carbonation than the slag with lower free lime content (K1-slag). While carbonation at these conditions was found to occur predominantly at the surface of the slag grains, the formation of cracks was observed in carbonated K3 slag, suggesting that free lime in the interior of slag grains had also reacted. The pH of the K3 slag (originally pH {+-} 12.5) was reduced by about 1.5 units, while the K1 slag showed a smaller decrease in pH from about 11.7 to 11.1. However, the pH reduction after carbonation of the K3 slag was observed to lead to an increased V-leaching. Vanadium leaching from the K1 slag resulted in levels above the limit values of the Dutch Soil Quality Decree, for both the untreated and carbonated slag. V-leaching from the carbonated K3 slag remained below these limit values at the relatively high pH that remained after carbonation. The V-bearing di-Ca silicate (C2S) phase has been identified as the major source of the V-leaching. It is shown that the dissolution of this mineral is limited in fresh steel slag, but strongly enhanced by carbonation, which causes the observed enhanced release of V from the K3 slag. The obtained insights in the mineral transformation reactions and their effect on pH and V-leaching provide guidance for further improvement of an accelerated carbonation technology.« less

Lateral spread affects nitrogen leaching from urine patches.

PubMed

Cichota, Rogerio; Vogeler, Iris; Snow, Val; Shepherd, Mark; McAuliffe, Russell; Welten, Brendon

2018-09-01

Nitrate leaching from urine deposited by grazing animals is a critical constraint for sustainable dairy farming in New Zealand. While considerable progress has been made to understand the fate of nitrogen (N) under urine patches, little consideration has been given to the spread of urinary N beyond the wetted area. In this study, we modelled the lateral spread of nitrogen from the wetted area of a urine patch to the soil outside the patch using a combination of two process-based models (HYDRUS and APSIM). The simulations provided insights on the extent and temporal pattern for the redistribution of N in the soil following a urine deposition and enabled investigating the effect of lateral spread of urinary N on plant growth and N leaching. The APSIM simulation, using an implementation of a dispersion-diffusion function, was tested against experimental data from a field experiment conducted in spring on a well-drained soil. Depending on the geometry considered for the dispersion-diffusion function (plate or cylindrical) the area-averaged N leaching decreased by 8 and 37% compared with simulations without lateral N spread; this was due to additional N uptake from pasture on the edge area. A sensitivity analysis showed that area-averaged pasture growth was not greatly affected by the value of the dispersion factor used in the model, whereas N leaching was very sensitive. Thus, the need to account for the edge effect may depend on the objective of the simulations. The modelling results also showed that considering lateral spread of urinary N was sufficient to describe the experimental data, but plant root uptake across urine patch zones may still be relevant in other conditions. Although further work is needed for improving accuracy, the simulated and experimental results demonstrate that accounting for the edge effect is important for determining N leaching from urine-affected areas. Copyright © 2018 Elsevier B.V. All rights reserved.

Multiple applications of the U.S. EPA 1312 leach procedure to mine waste from the Animas watershed, SW Colorado

USGS Publications Warehouse

Fey, David L.; Church, Stan E.; Driscoll, Rhonda L.; Adams, Monique G.

2011-01-01

Eleven acid-sulphate and quartz-sericite-pyrite altered mine waste samples from the Animas River watershed in SW Colorado were subjected to a series of 5 to 6 successive leaches using the US EPA 1312 leach protocol to evaluate the transport of metals and loss of acidity from mine wastes as a function of time. Multi-acid digestion ICP-AES analyses, X-ray diffraction (XRD) mineral identification, total sulphur, and net acid potential (NAP) determinations were performed on the initial starting materials. Multiple leaching steps generally showed a 'flushing' effect, whereby elements loosely bound, presumably as water-soluble salts, were removed. Aluminum, Cd, Fe, Mg, Mn, Sr, Zn, and S showed decreasing concentration trends, whereas Cu concentrations showed initially decreasing trends, followed by increasing trends in later steps. Concentrations of Zn in the first leach step were independent of whole-sample Zn content. Lead and Ba concentrations consistently increased with each step, indicating that anglesite (PbSO4) and barite (BaSO4), respectively, were dissolving in successive leach steps. Comparison of Fe content with NAP resulted in a modest correlation. However, using the S analyses and XRD identification of sulphide minerals to apportion S amongst enargite, barite, anglesite/galena, and sphalerite, and assigning the remaining S to pyrite, provided a useful correlation between estimated pyrite content and NAP. Whole-sample mass loss correlated well with NAP, but individual elements' behaviors varied between positive correlation (e.g. Al, Fe, Mg), no apparent correlation (Ca, Cd, Pb, Zn), and negative correlation (Cu). Comparison of the summed titrated acidities of the leachates with the whole-sample NAP values yielded an estimate of the fraction of NAP consumed, and led to an estimate of the time it would take to consume the sample acidity by weathering. We estimate, on the basis of these experiments, the acidity in the upper 30 cm would be consumed in 200–1000 years. In addition, calculations suggest that the acidity would be depleted before the complete store of the metals Cu-Cd-Zn in these mine wastes would be released to the environment.

Multiple applications of the U.S. EPA 1312 leach procedure to mine waste from the animas watershed, SW Colorado

USGS Publications Warehouse

Fey, D.L.; Church, S.E.; Driscoll, R.L.; Adams, M.G.

2011-01-01

Eleven acid-sulphate and quartz-sericite-pyrite altered mine waste samples from the Animas River watershed in SW Colorado were subjected to a series of 5 to 6 successive leaches using the US EPA 1312 leach protocol to evaluate the transport of metals and loss of acidity from mine wastes as a function of time. Multi-acid digestion ICP-AES analyses, X-ray diffraction (XRD) mineral identification, total sulphur, and net acid potential (NAP) determinations were performed on the initial starting materials. Multiple leaching steps generally showed a 'flushing' effect, whereby elements loosely bound, presumably as water-soluble salts, were removed. Aluminum, Cd, Fe, Mg, Mn, Sr, Zn, and S showed decreasing concentration trends, whereas Cu concentrations showed initially decreasing trends, followed by increasing trends in later steps. Concentrations of Zn in the first leach step were independent of whole-sample Zn content. Lead and Ba concentrations consistently increased with each step, indicating that anglesite (PbSO4) and barite (BaSO4), respectively, were dissolving in successive leach steps. Comparison of Fe content with NAP resulted in a modest correlation. However, using the S analyses and XRD identification of sulphide minerals to apportion S amongst enargite, barite, anglesite/galena, and sphalerite, and assigning the remaining S to pyrite, provided a useful correlation between estimated pyrite content and NAP. Whole-sample mass loss correlated well with NAP, but individual elements' behaviors varied between positive correlation (e.g. Al, Fe, Mg), no apparent correlation (Ca, Cd, Pb, Zn), and negative correlation (Cu). Comparison of the summed titrated acidities of the leachates with the whole-sample NAP values yielded an estimate of the fraction of NAP consumed, and led to an estimate of the time it would take to consume the sample acidity by weathering. We estimate, on the basis of these experiments, the acidity in the upper 30 cm would be consumed in 200-1000 years. In addition, calculations suggest that the acidity would be depleted before the complete store of the metals Cu-Cd-Zn in these mine wastes would be released to the environment. ?? 2011 AAG/Geological Society of London.

NLEAP/GIS approach for identifying and mitigating regional nitrate-nitrogen leaching

USGS Publications Warehouse

Shaffer, M.J.; Hall, M.D.; Wylie, B.K.; Wagner, D.G.; Corwin, D.L.; Loague, K.

1996-01-01

Improved simulation-based methodology is needed to help identify broad geographical areas where potential NO3-N leaching may be occurring from agriculture and suggest management alternatives that minimize the problem. The Nitrate Leaching and Economic Analysis Package (NLEAP) model was applied to estimate regional NO3-N leaching in eastern Colorado. Results show that a combined NLEAP/GIS technology can be used to identify potential NO3-N hot spots in shallow alluvial aquifers under irrigated agriculture. The NLEAP NO3-N Leached (NL) index provided the most promising single index followed by NO3-N Available for Leaching (NAL). The same combined technology also shows promise in identifying Best Management Practice (BMP) methods that help minimize NO3-N leaching in vulnerable areas. Future plans call for linkage of the NLEAP/GIS procedures with groundwater modeling to establish a mechanistic analysis of agriculture-aquifer interactions at a regional scale.

Experimental evidence for mobility of Zr and other trace elements in soils

NASA Astrophysics Data System (ADS)

Hodson, Mark E.

2002-03-01

A Soxhlet extraction was carried out over a period of 27 d on a column comprising 3 cm of quartz overlain by 4 cm of soil from the B horizon and then 1 cm of soil from the A horizon of a granitic podzol. Major and trace elements were leached from the column and accumulated in a reservoir at the base of the column. Total loss of elements from the soil over the course of the experiment ranged from 0.002 to 1 wt% with major elements and the light and heavy rare earth elements (REE) showing the largest percentage losses. Zirconium (0.002%) and then Al (0.008%) showed the lowest percentage loss. The light REE were leached out of the soil preferentially to the mid REE. All elements showed accumulation, by a factor of 2 to 11, in the quartz layers at the base of the column, particularly in the upper first 1 cm of the quartz. Major elements were leached from the column at a rate of 0.02 to 0.59 μmol h-1 whereas Zr, Nd, Sm, Gd, Dy, Rb, and Sr were leached at the rate of 0.5 to 30 × 10-6 μmol h-1. Concentrations of other REE in the reservoir increased over the duration of the experiment, but they were poorly correlated with time, so leaching rates were not calculated. Normalization of the major element leaching rates to take into account the constant flushing of water through the column, the average annual rainfall in the Allt a'Mharcaidh catchment in Scotland from where the soil was sampled, and the cross-sectional area of the soil in the column, together with the temperature of the soil in the column (70°C) compared with the average annual temperature of the Allt a'Mharcaidh catchment (5.7°C), gave major element release rates from the soil of 0.002 to 0.97 mEq m-2 yr-1 (depending on the choice of Ea, the dissolution activation energy), which are generally less than those measured in the field of 0.1 to 40.9 mEq m-2 yr-1. Calculations showed that despite the redistribution and loss of Zr from the column, assumptions of Zr mobility would have had a negligible effect on calculated element release rates of Na, Ca, Fe, and Mg. However, significant underestimates of the release of K (5%), Ti (57%), Al (5%), and Si (10%) as well as some trace elements (e.g., Nd, 23%; Rb, 54%; Sr, 24%) would have occurred. Concentrations of Ca and Sr leached from the column correlated well (RSQ = 0.93, p < 0.01), supporting the idea of the use of Sr release as a proxy for Ca release in weathering rate calculations. The release rates and percentage loss of REE from the soil varied between elements indicating that REE distribution patterns of rocks and soils may not be preserved in drainage waters.

In situ 15N labeling experiment reveals different long-term responses to ammonium and nitrate inputs in N-saturated subtropical forest

NASA Astrophysics Data System (ADS)

Liu, Wenjing; Yu, Longfei; Zhang, Ting; Kang, Ronghua; Zhu, Jing; Mulder, Jan; Huang, Yongmei; Duan, Lei

2017-09-01

Chronically elevated deposition of reactive nitrogen (N), as ammonium (NH4+) and nitrate (NO3-), in subtropical forests with monsoonal climate has caused widespread N leaching in southern China. So far, little is known about the effect of further increases in N input and changes in the relative proportion of NH4+ and NO3- on turnover rate and fate of atmogenic N. Here we report a 15N tracer experiment in Tieshanping (TSP) forest, SW China, conducted as part of a long-term N fertilization experiment, using NH4NO3 and NaNO3, where effects of a doubling of monthly N inputs were compared. In June 2012, the regular N fertilizers were replaced by their 15N-labeled forms, viz., 15NH4NO3 and Na15NO3, as a single-dose addition. Mass balances of N for the initial 1.5 years following label addition showed that for both treatments, 70% to 80% of the annual N input was leached as NO3-, both at ambient and at double N input rates. This confirms the earlier reported extreme case of N saturation at TSP. The 15N, added as Na15NO3, showed recoveries of about 74% in soil leachates, indicating that NO3- input at TSP is subject to a rapid and nearly quantitative loss through direct leaching as a mobile anion. By contrast, recoveries of 15N in soil leachates of only 33% were found if added as 15NH4NO3. Much of the 15N was immobilized in the soil and to a lesser extent in the vegetation. Thus, immobilization of fresh N input is significantly greater if added as NH4+, than as NO3-.

Impact of simulated acid rain on trace metals and aluminum leaching in latosol from Guangdong Province, China

Treesearch

Jia-En Zhang; Jiayu Yu; Ying Ouyang; Huaqin Xu

2014-01-01

Acid rain is one of the most serious ecological and environmental problems worldwide. This study investigated the impacts of simulated acid rain (SAR) upon leaching of trace metals and aluminum (Al) from a soil. Soil pot leaching experiments were performed to investigate the impacts of SAR at five different pH levels (or treatments) over a 34-day period upon the...

Effects of ditch-buried straw return on water percolation, nitrogen leaching and crop yields in a rice-wheat rotation system.

PubMed

Yang, Haishui; Xu, Mingmin; Koide, Roger T; Liu, Qian; Dai, Yajun; Liu, Ling; Bian, Xinmin

2016-03-15

Crop residue management and nitrogen loss are two important environmental problems in the rice-wheat rotation system in China. This study investigated the effects of burial of straw on water percolation, nitrogen loss by leaching, crop growth and yield. Greenhouse mesocosm experiments were conducted over the course of three simulated cropping seasons in a rice1-wheat-rice2 rotation. Greater amounts of straw resulted in more water percolation, irrespective of crop season. Burial at 20 and 35 cm significantly reduced, but burial at 50 cm increased nitrogen leaching. Straw at 500 kg ha(-1) reduced, but at 1000 kg ha(-1) and at 1500 kg ha(-1) straw increased nitrogen leaching in three consecutive crop rotations. In addition, straw at 500 kg ha(-1) buried at 35 cm significantly increased yield and its components for both crops. This study suggests that N losses via leaching from the rice-wheat rotation may be reduced by the burial of the appropriate amount of straw at the appropriate depth. Greater amounts of buried straw, however, may promote nitrogen leaching and negatively affect crop growth and yields. Complementary field experiments must be performed to make specific agronomic recommendations. © 2015 Society of Chemical Industry.

Leaching of PAHs from agricultural soils treated with oil shale combustion ash: an experimental study.

PubMed

Jefimova, Jekaterina; Adamson, Jasper; Reinik, Janek; Irha, Natalya

2016-10-01

The present study focuses on the fate of polycyclic aromatic hydrocarbons (PAHs) in soils amended with oil shale ash (OSA). Leachability studies to assess the release of PAHs to the environment are essential before the application of OSA in agriculture. A quantitative estimation of the leaching of PAHs from two types of soil and two types of OSA was undertaken in this study. Two leaching approaches were chosen: (1) a traditional one step leaching scheme and (2) a leaching scheme with pretreatment, i.e.., incubation of the material in wet conditions imitating the field conditions, followed by a traditional leaching procedure keeping the total amount of water constant. The total amount of PAHs leached from soil/OSA mixtures was in the range of 15 to 48 μg/kg. The amount of total PAHs leached was higher for the incubation method, compared to the traditional leaching method, particularly for Podzolic Gleysols soil. This suggests that for the incubation method, the content of organic matter and clay minerals of the soil influence the fate of PAHs more strongly compared to the traditional leaching scheme. The amount of PAHs leached from OSA samples is higher than from soil/OSA mixtures, which suggests soils to inhibit the release of PAHs. Calculated amount of PAHs from experimental soil and OSA leaching experiments differed considerably from real values. Thus, it is not possible to estimate the amount of PAHs leached from soil/OSA mixtures based on the knowledge of the amount of PAHs leached from soil and OSA samples separately.

Nitrate leaching in a winter wheat-summer maize rotation on a calcareous soil as affected by nitrogen and straw management.

PubMed

Huang, Tao; Ju, Xiaotang; Yang, Hao

2017-02-08

Nitrate leaching is one of the most important pathways of nitrogen (N) loss which leads to groundwater contamination or surface water eutrophication. Clarifying the rates, controlling factors and characteristics of nitrate leaching is the pre-requisite for proposing effective mitigation strategies. We investigated the effects of interactions among chemical N fertilizer, straw and manure applications on nitrogen leaching in an intensively managed calcareous Fluvo-aquic soil with winter wheat-summer maize cropping rotations on the North China Plain from October 2010 to September 2013 using ceramic suction cups and seepage water calculations based on a long-term field experiment. Annual nitrate leaching reached 38-60 kg N ha -1 from conventional N managements, but declined by 32-71% due to optimum N, compost manure or municipal waste treatments, respectively. Nitrate leaching concentrated in the summer maize season, and fewer leaching events with high amounts are the characteristics of nitrate leaching in this region. Overuse of chemical N fertilizers, high net mineralization and nitrification, together with predominance of rainfall in the summer season with light soil texture are the main controlling factors responsible for the high nitrate leaching loss in this soil-crop-climatic system.

Nitrate leaching in a winter wheat-summer maize rotation on a calcareous soil as affected by nitrogen and straw management

NASA Astrophysics Data System (ADS)

Huang, Tao; Ju, Xiaotang; Yang, Hao

2017-02-01

Nitrate leaching is one of the most important pathways of nitrogen (N) loss which leads to groundwater contamination or surface water eutrophication. Clarifying the rates, controlling factors and characteristics of nitrate leaching is the pre-requisite for proposing effective mitigation strategies. We investigated the effects of interactions among chemical N fertilizer, straw and manure applications on nitrogen leaching in an intensively managed calcareous Fluvo-aquic soil with winter wheat-summer maize cropping rotations on the North China Plain from October 2010 to September 2013 using ceramic suction cups and seepage water calculations based on a long-term field experiment. Annual nitrate leaching reached 38-60 kg N ha-1 from conventional N managements, but declined by 32-71% due to optimum N, compost manure or municipal waste treatments, respectively. Nitrate leaching concentrated in the summer maize season, and fewer leaching events with high amounts are the characteristics of nitrate leaching in this region. Overuse of chemical N fertilizers, high net mineralization and nitrification, together with predominance of rainfall in the summer season with light soil texture are the main controlling factors responsible for the high nitrate leaching loss in this soil-crop-climatic system.

Report on Initial Direct Soil Leaching Experiments Using Post-Detonation Debris

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gostic, R.; Knight, K. B.; Borg, L.

2011-08-01

A key challenge of nuclear forensics is reducing the time and manpower effort required to measure nuclear debris compositions. The overall motivation for this work is to explore development of a robust, automated system that can be used to concurrently analyze several elements/isotopes associated with the forensic signature of nuclear materials. The primary focus of this research has been to methodically investigate if rapid partial leaching of post-detonation debris can yield usable elemental and isotopic information for interpretation. The unique requirements of post-detonation nuclear forensics have not been fully adapted to or fully incorporated contemporary chemical separation techniques. Challenges includemore » addressing the range of material matrices or mixed fission product and actinide compositions and concentrations that might be encountered. These include, but are not limited to, puddle melt glass, urban debris, seawater, air filters, iron-rich urban debris, asphalt, and silica sand. Separation of these elements and their subsequent measurement is a key element of related laboratory analysis activity. Existing practices at LLNL rely on proven but time-consuming and labor intensive processes. Significant time and labor savings are possible in chemical separations, however, if rapid processing methods can be adapted to post-detonation debris. Development of a simple and reliable leaching technique could shorten analytical times and would be useful as a field deployable method for the preliminary characterization of actinide isotopic ratios in soils. Measurement of isotopic ratios in the field using modern mass spectrometry capabilities such as Inductively Coupled Plasma Mass Spectrometry (ICP-MS) is desirable, taking advantage of the extended range of isotopic systems measureable using such instruments. Sample introduction to these types of mass spectrometry instruments requires partial leaching or full dissolution of a sample to remove isobaric (same mass) interferences, and, in some cases, to concentrate the elements(s) of interest. To develop a field-deployable mass spectrometry capability, therefore, automated and robust leaching of likely debris samples (ranging from silicates and oxides to metals and urban materials such as concrete and asphalt), followed by separation/purification through cation exchange column chemistry is necessary. In a post-detonation environment, analysis of melt glasses via rapid leaching and ICP-MS could be a viable route to the same goal. This report presents initial leaching experiments on ‘uncontaminated’ soils, as well as data from melt glass from a single nuclear weapons test. Samples were characterized by gamma spectrometry, then aliquoted for rapid leaching experiments. Experiments were conducted using two different rapid acid treatments to leach the soils. Following leaching, the leachate solutions were analyzed by ICP-MS to determine if U isotopic composition. We present these data to address the question as to whether or not rapid (~1 hr) leaching techniques have the potential to yield meaningful U isotopic compositions, without the need for a complete (time consuming) sample dissolution and separation.« less

Use of different organic wastes as strategy to mitigate the leaching potential of phenylurea herbicides through the soil.

PubMed

Fenoll, José; Garrido, Isabel; Hellín, Pilar; Flores, Pilar; Vela, Nuria; Navarro, Simón

2015-03-01

In this study, the leaching of 14 substituted phenylurea herbicides (PUHs) through disturbed soil columns packed with three different soils was investigated in order to determine their potential for groundwater pollution. Simultaneously, a series of experiments were conducted to demonstrate the effect of four different organic wastes (composted sheep manure (CSM), composted pine bark (CPB), spent coffee grounds (SCG) and coir (CR)) on their mobility. All herbicides, except difenoxuron, showed medium/high leachability through the unamended soils. In general, addition of agro-industrial and composted organic wastes at a rate of 10% (w/w) increased the adsorption of PUHs and decreased their mobility in the soil, reducing their leaching. In all cases, the groundwater ubiquity score (GUS) index was calculated for each herbicide on the basis of its persistence (as t ½) and mobility (as K OC). The results obtained point to the interest in the use of agro-industrial and composted organic wastes in reducing the risk of groundwater pollution by pesticide drainage.

Metal-contaminated soil remediation by using sludges of the marble industry: toxicological evaluation.

PubMed

Pérez-Sirvent, C; García-Lorenzo, M L; Martínez-Sánchez, M J; Navarro, M C; Marimón, J; Bech, J

2007-05-01

The major risks due to metal pollution of sediments consist of leaching to groundwater and potential toxicity to animals and/or plants. The objective of this study was to evaluate by means of an ecotoxicological approach the effects of the addition of cutting marble sludges on the mobile metal fraction of sediments polluted with heavy metals. The study was carried out on two sediments derived from mining activities in Portman Bay (SE, Spain) polluted by heavy metals. These sediments were mixed with sludges left after the cutting of marble. The results obtained by leaching experiments showed that the addition of marble cutting sludge, consisting mainly of carbonates, to a heavy-metal polluted sediment produces a decrease of available metal forms. The carbonate content seems to play a role in chemical stabilisation of metals and in a decrease of toxicity of sediments. The leached solutions have a non-toxic effect. The mild remediation by addition of sludge has moreover effects to long term.

Influencing factors and kinetics analysis on the leaching of iron from boron carbide waste-scrap with ultrasound-assisted method.

PubMed

Li, Xin; Xing, Pengfei; Du, Xinghong; Gao, Shuaibo; Chen, Chen

2017-09-01

In this paper, the ultrasound-assisted leaching of iron from boron carbide waste-scrap was investigated and the optimization of different influencing factors had also been performed. The factors investigated were acid concentration, liquid-solid ratio, leaching temperature, ultrasonic power and frequency. The leaching of iron with conventional method at various temperatures was also performed. The results show the maximum iron leaching ratios are 87.4%, 94.5% for 80min-leaching with conventional method and 50min-leaching with ultrasound assistance, respectively. The leaching of waste-scrap with conventional method fits the chemical reaction-controlled model. The leaching with ultrasound assistance fits chemical reaction-controlled model, diffusion-controlled model for the first stage and second stage, respectively. The assistance of ultrasound can greatly improve the iron leaching ratio, accelerate the leaching rate, shorten leaching time and lower the residual iron, comparing with conventional method. The advantages of ultrasound-assisted leaching were also confirmed by the SEM-EDS analysis and elemental analysis of the raw material and leached solid samples. Copyright © 2017 Elsevier B.V. All rights reserved.

Effects of simulated acid rain on microbial characteristics in a lateritic red soil.

PubMed

Xu, Hua-qin; Zhang, Jia-en; Ouyang, Ying; Lin, Ling; Quan, Guo-ming; Zhao, Ben-liang; Yu, Jia-yu

2015-11-01

A laboratory experiment was performed to examine the impact of simulated acid rain (SAR) on nutrient leaching, microbial biomass, and microbial activities in a lateritic red soil in South China. The soil column leaching experiment was conducted over a 60-day period with the following six SAR pH treatments (levels): 2.5, 3.0, 3.5, 4.0, 4.5, and 5.0 and one control treatment (pH = 7). Compared with the control treatment, the concentrations of soil organic matter, total nitrogen, total phosphorus, total potassium, soil microbial biomass carbon (MBC), soil microbial biomass nitrogen (MBN), and average well color density (AWCD) in the Ecoplates were all significantly decreased by leaching with SAR at different pH levels. The decrease in MBC and MBN indicated that acid rain reduced the soil microbial population, while the decrease in AWCD revealed that acid rain had a negative effect on soil bacterial metabolic function. Soil basal respiration increased gradually from pH 4.0 to 7.0 but decreased dramatically from pH 2.5 to 3.0. The decrease in soil nutrient was the major reason for the change of soil microbial functions. A principal component analysis showed that the major carbon sources used by the bacteria were carbohydrates and carboxylic acids.

Determination of the mode of occurrence of As, Cr, and Hg in three Chinese coal samples by sequential acid leaching

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, B.; Li, W.; Wang, G.

2007-07-01

Sequential acid leaching was used to leach minerals and the trace elements they contain. One-step leaching uses concentrated nitric acid as solvent, while three-step leaching uses 5M hydrochloric acid, concentrated hydrofluoric acid, and concentrated hydrochloric acid as solvents. The sequential acid leaching by three-and one-step leach was also examined. The results showed that one-step leaching could leach over 80% of arsenic from coal samples, and also could leach mercury to a certain degree. During one-step leaching, little chromium is removed, but it is available to leach by three-step leaching; and during the sequential acid leaching by three and one-step leaching,more » almost 98% ash is leached. The result of acid leaching could also give detailed information on mode of occurrence of As, Cr, and Hg, which could be classified into: silicate association, pyrite association, organic association, and carbonates and sulfates association. Over half of chromium in the three coals is associated with organic matters and the rest is associated with silicates. The mode of occurrence of arsenic and mercury is mainly associated with different mineral matters depending on the coal samples studied.« less

Leaching characteristics of arsenic and selenium from coal fly ash: role of calcium

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tian Wang; Jianmin Wang; Yulin Tang

2009-05-15

Understanding the leaching behavior of arsenic (As) and selenium (Se) in coal fly ash is important in evaluating the potential environmental impact of coal fly ash. Batch experiments were employed to systematically investigate the leaching behavior of As and Se in two major types of coal fly ashes, bituminous coal ash and sub-bituminous coal ash, and to determine the underlying processes that control As and Se leaching. The effects of pH, solid/liquid (S/L) ratio, calcium addition, and leaching time on the release of As and Se were studied. Overall, bituminous coal ash leached significantly more As and Se than sub-bituminousmore » coal ash, and Se was more readily leachable, in both absolute concentration and relative fraction, than As for both types of fly ashes. Adsorption/desorption played a major role on As and Se leaching from bituminous coal ashes. However, calcium precipitation played the most important role in reducing As and Se leaching from sub-bituminous coal ashes in the entire experimental pH range. The leaching of As and Se from bituminous coal ashes generally increased with increases in the S/L ratio and leaching time. However, for sub-bituminous coal ashes, the leaching of As was not detected under most experimental conditions, while the leaching of Se increased with increases in the S/L ratio and leaching time. As{sup V} and Se{sup IV} were found to be the major species in all ash leachates in this study. 46 refs., 7 figs., 1 tab.« less

Organic compounds in water extracts of coal: links to Balkan endemic nephropathy.

PubMed

Maharaj, S V M; Orem, W H; Tatu, C A; Lerch, H E; Szilagyi, D N

2014-02-01

The Pliocene lignite hypothesis is an environmental hypothesis that has been proposed to explain the etiology of Balkan endemic nephropathy (BEN). Aqueous leaching experiments were conducted on a variety of coal samples in order to simulate groundwater leaching of organic compounds, and to further test the role of the Pliocene lignite hypothesis in the etiology of BEN. Experiments were performed on lignite coal samples from endemic BEN areas in Romania and Serbia, and lignite and bituminous coals from nonendemic regions in Romania and the USA. Room temperature, hot water bath, and Soxhlet aqueous extraction experiments were conducted between 25 and 80 °C, and from 5 to 128 days in duration. A greater number of organic compounds and in higher concentrations were present in all three types of leaching experiments involving endemic area Pliocene lignite samples compared to all other coals examined. A BEN causing molecule or molecules may be among phenols, PAHs, benzenes, and/or lignin degradation compounds. The proposed transport pathway of the Pliocene lignite hypothesis for organic compound exposure from endemic area Pliocene lignite coals to well and spring drinking water, is likely. Aromatic compounds leached by groundwater from Pliocene lignite deposits in the vicinity of endemic BEN areas may play a role in the etiology of the disease. A better understanding of organic compounds leached by groundwater from Pliocene lignite deposits may potentially lead to the identification and implementation of effective strategies for the prevention of exposure to the causative agent(s) for BEN, and in turn, prevention of the disease.

In what root-zone N concentration does nitrate start to leach significantly? A reasonable answer from modeling Mediterranean field data and closed root-zone experiments

NASA Astrophysics Data System (ADS)

Kurtzman, D.; Kanner, B.; Levy, Y.; Shapira, R. H.; Bar-Tal, A.

2017-12-01

Closed-root-zone experiments (e.g. pots, lyzimeters) reveal in many cases a mineral-nitrogen (N) concentration from which the root-N-uptake efficiency reduces significantly and nitrate leaching below the root-zone increases dramatically. A les-direct way to reveal this threshold concentration in agricultural fields is to calibrate N-transport models of the unsaturated zone to nitrate data of the deep samples (under the root-zone) by fitting the threshold concentration of the nitrate-uptake function. Independent research efforts of these two types in light soils where nitrate problems in underlying aquifers are common reviled: 1) that the threshold exists for most crops (filed, vegetables and orchards); 2) nice agreement on the threshold value between the two very different research methodologies; and 3) the threshold lies within 20-50 mg-N/L. Focusing on being below the threshold is a relatively simple aim in the way to maintain intensive agriculture with limited effects on the nitrate concentration in the underlying water resource. Our experience show that in some crops this threshold coincides with the end-of-rise of the N-yield curve (e.g. corn); in this case, it is relatively easy to convince farmers to fertilize below threshold. In other crops, although significant N is lost to leaching the crop can still use higher N concentration to increase yield (e.g. potato).

Direct and indirect effects of biochar on the mobility of metals and nutrients in contaminated soils: a two-column leaching experiment

NASA Astrophysics Data System (ADS)

Rees, Frédéric; Simonnot, Marie-Odile; Morel, Jean-Louis

2014-05-01

Biochar has been claimed to be not only a promising carbon sequestration or fertilizing agent in soils but also a high capacity sorbent, of particular interest for the management of contaminated soils. Several studies have described its positive effects on the mobility of different potentially toxic elements in soils, but many doubts remain about the underlying mechanisms. In particular, the distinction between the actual adsorption of elements on biochar and their biochar-induced retention on soil particles is often impossible to achieve. We studied here the dynamic interactions between one biochar produced at 450°C from a mix of hard wood and soft wood, and two soils contaminated by Cd, Pb and Zn which were sampled near a smelter and only differed from their pH. In order to distinguish between the actual immobilization of elements on biochar and their modified retention on soil particles, we developed a two-column leaching experiment using calcium nitrate as the initial leaching solution. The first column was filled with one of the two soils, and was linked in a closed loop with the second column containing a mass of pure biochar equivalent to 10% of the soil mass. The leaching solution circulated first in the soil column, then through the biochar column and again in the soil column and so on, so that it became progressively equilibrated with both soil and biochar. Each experiment lasted for 12 days at a flow rate of 1 mL/min. The pH and electrical conductivity of the leaching solution was continuously monitored at the outlet of the biochar column, and samples of the leaching solution were regularly taken for further analysis, both before and after having passed each of the columns. Our results show that the chemical equilibrium between soil and biochar was obtained in a short time for major elements such as Na, K and Mg, whereas for heavy metals and other elements as well as for pH and dissolved carbon, the equilibrium was still not reached at the end of the experiment. This observation highlights the slow, diffusive nature of biochar chemical interactions with the soil. The comparison of samples enabled us to quantify the immobilization of elements on biochar from its indirect effect on the retention capacity of the soil, mostly due to the increase of pH and the dynamics of inorganic and organic carbon in the solution. Altogether, these results provide new information about the complex effects of biochar on soil properties and about its efficiency in the context of soil remediation.

Geochemical assessments and classification of coal mine spoils for better understanding of potential salinity issues at closure.

PubMed

Park, Jin Hee; Li, Xiaofang; Edraki, Mansour; Baumgartl, Thomas; Kirsch, Bernie

2013-06-01

Coal mining wastes in the form of spoils, rejects and tailings deposited on a mine lease can cause various environmental issues including contamination by toxic metals, acid mine drainage and salinity. Dissolution of salt from saline mine spoil, in particular, during rainfall events may result in local or regional dispersion of salts through leaching or in the accumulation of dissolved salts in soil pore water and inhibition of plant growth. The salinity in coal mine environments is from the geogenic salt accumulations and weathering of spoils upon surface exposure. The salts are mainly sulfates and chlorides of calcium, magnesium and sodium. The objective of the research is to investigate and assess the source and mobility of salts and trace elements in various spoil types, thereby predicting the leaching behavior of the salts and trace elements from spoils which have similar geochemical properties. X-ray diffraction analysis, total digestion, sequential extraction and column experiments were conducted to achieve the objectives. Sodium and chloride concentrations best represented salinity of the spoils, which might originate from halite. Electrical conductivity, sodium and chloride concentrations in the leachate decreased sharply with increasing leaching cycles. Leaching of trace elements was not significant in the studied area. Geochemical classification of spoil/waste defined for rehabilitation purposes was useful to predict potential salinity, which corresponded with the classification from cluster analysis based on leaching data of major elements. Certain spoil groups showed high potential salinity by releasing high sodium and chloride concentrations. Therefore, the leaching characteristics of sites having saline susceptible spoils require monitoring, and suitable remediation technologies have to be applied.

Corrosion control in water supply systems: effect of pH, alkalinity, and orthophosphate on lead and copper leaching from brass plumbing.

PubMed

Tam, Y S; Elefsiniotis, P

2009-10-01

This study explored the potential of lead and copper leaching from brass plumbing in the Auckland region of New Zealand. A five-month field investigation, at six representative locations, indicated that Auckland's water can be characterized as soft and potentially corrosive, having low alkalinity and hardness levels and a moderately alkaline pH. More than 90% of the unflushed samples contained lead above the maximum acceptable value (MAV) of 10 microg/L (New Zealand Standards). In contrast, the copper level of unflushed samples remained consistently below the corresponding MAV of 2 mg/L. Flushing however reduced sharply metal concentrations, with lead values well below the MAV limit. Generally, metal leaching patterns showed a limited degree of correlation with the variations in temperature, dissolved oxygen and free chlorine residual at all sampling locations. Furthermore, a series of bench-scale experiments was conducted to evaluate the effectiveness of pH and alkalinity adjustment, as well as orthophosphate addition as corrosion control tools regarding lead and copper dissolution. Results demonstrated that lead and copper leaching was predominant during the first 24 hr of stagnation, but reached an equilibrium state afterwards. Since the soluble fraction of both metals was small (12% for lead, 29% for copper), it is apparent that the non-soluble compounds play a predominant role in the dissolution process. The degree of leaching however was largely affected by the variations in pH and alkalinity. At pH around neutrality, an increase in alkalinity promoted metal dissolution, while at pH 9.0 the effect of alkalinity on leaching was marginal. Lastly, addition of orthophosphate as a corrosion inhibitor was more effective at pH 7.5 or higher, resulting in approximately 70% reduction in both lead and copper concentrations.

Hazardous properties of paint residues from the furniture industry.

PubMed

Vaajasaari, Kati; Kulovaara, Maaret; Joutti, Anneli; Schultz, Eija; Soljamo, Kari

2004-01-30

The objective of this study was to screen nine excess paint residues for environmental hazard and to evaluate their disposability in a non-hazardous or hazardous-waste landfill. These residues were produced in the process of spray-painting furniture. Residues were classified according to their leaching and ecotoxicological properties. Leaching properties were determined with the European standard SFS-EN 12457-2 leaching-test. The toxicity of the leaching-test eluates was measured with plant-, bacteria- and enzyme-inhibition bioassays. Total organic carbon, formaldehyde and solvent concentrations in the solid wastes and in the leaching-test eluates were analysed. It seemed likely that leached formaldehyde caused very high acute toxicity in leaching-test eluates of the dry-booth residues. This hypothesis was based on the fact that the formaldehyde concentrations in the leaching-test eluates of the dry-booth residues were 62-75 times higher than the EC50 value reported in the literature for formaldehyde. The results of the water-curtain booth residues showed that the samples with the highest TOC and aromatic solvent concentrations were also the most toxic. The studied excess paint residues were complex organic mixtures and contained large amounts of compounds not identifiable from chemical data. Therefore, the evaluation of the hazard based solely on available chemical data is unlikely to be sufficient, as evidenced by our study. Our results show that harmful compounds remain in the solid waste and the toxicity results of their leaching-test eluates show that toxicity may leach from residues in contact with water at landfill sites. They also confirm the benefit of combining chemical and ecotoxicological assays in assessing the potential environmental hazard of complex organic mixtures found in wastes. Copyright 2003 Elsevier B.V.

Leaching characteristics of toxic constituents from coal fly ash mixed soils under the influence of pH

DOE Office of Scientific and Technical Information (OSTI.GOV)

Komonweeraket, Kanokwan; Cetin, Bora, E-mail: bora.cetin@sdsmt.edu; Benson, Craig H., E-mail: chbenson@wisc.edu

Highlights: • The impact of pH on the leaching of elements and metals from fly ash mixed soils. • Generally Ca, Cd, Mg, and Sr follows a cationic leaching pattern. • The leaching of As and Se shows an oxyanionic leaching pattern. • The leaching behavior of elements does not change based on material type. • Different fly ash types show different abilities in immobilizing trace elements. - Abstract: Leaching behaviors of Arsenic (As), Barium (Ba), Calcium (Ca), Cadmium (Cd), Magnesium (Mg), Selenium (Se), and Strontium (Sr) from soil alone, coal fly ash alone, and soil-coal fly ash mixtures, weremore » studied at a pH range of 2–14 via pH-dependent leaching tests. Seven different types of soils and coal fly ashes were tested. Results of this study indicated that Ca, Cd, Mg, and Sr showed cationic leaching pattern while As and Se generally follows an oxyanionic leaching pattern. On the other hand, leaching of Ba presented amphoteric-like leaching pattern but less pH-dependent. In spite of different types and composition of soil and coal fly ash investigated, the study reveals the similarity in leaching behavior as a function of pH for a given element from soil, coal fly ash, and soil-coal fly ash mixtures. The similarity is most likely due to similar controlling mechanisms (e.g., solubility, sorption, and solid-solution formation) and similar controlling factors (e.g., leachate pH and redox conditions). This offers the opportunity to transfer knowledge of coal fly ash that has been extensively characterized and studied to soil stabilized with coal fly ash. It is speculated that unburned carbon in off-specification coal fly ashes may provide sorption sites for Cd resulting in a reduction in concentration of these elements in leachate from soil-coal fly ash mixture. Class C fly ash provides sufficient CaO to initiate the pozzolanic reaction yielding hydrated cement products that oxyanions, including As and Se, can be incorporated into.« less

Nitrate leaching in a winter wheat-summer maize rotation on a calcareous soil as affected by nitrogen and straw management

PubMed Central

Huang, Tao; Ju, Xiaotang; Yang, Hao

2017-01-01

Nitrate leaching is one of the most important pathways of nitrogen (N) loss which leads to groundwater contamination or surface water eutrophication. Clarifying the rates, controlling factors and characteristics of nitrate leaching is the pre-requisite for proposing effective mitigation strategies. We investigated the effects of interactions among chemical N fertilizer, straw and manure applications on nitrogen leaching in an intensively managed calcareous Fluvo-aquic soil with winter wheat-summer maize cropping rotations on the North China Plain from October 2010 to September 2013 using ceramic suction cups and seepage water calculations based on a long-term field experiment. Annual nitrate leaching reached 38–60 kg N ha−1 from conventional N managements, but declined by 32–71% due to optimum N, compost manure or municipal waste treatments, respectively. Nitrate leaching concentrated in the summer maize season, and fewer leaching events with high amounts are the characteristics of nitrate leaching in this region. Overuse of chemical N fertilizers, high net mineralization and nitrification, together with predominance of rainfall in the summer season with light soil texture are the main controlling factors responsible for the high nitrate leaching loss in this soil-crop-climatic system. PMID:28176865

Trees' role in nitrogen leaching after organic, mineral fertilization: a greenhouse experiment.

PubMed

López-Díaz, M L; Rolo, V; Moreno, G

2011-01-01

New sustainable agriculture techniques are arising in response to the environmental problems caused by intensive agriculture, such as nitrate leaching and surface water eutrophication. Organic fertilization (e.g., with sewage sludge) and agroforestry could be used to reduce nutrient leaching. We assessed the efficiency of establishing trees and pasture species in environmentally sensitive, irrigated Mediterranean grassland soils in controlling nitrate leaching. Four vegetation systems-bare soil, pasture species, cherry trees [ (L.) L.], and pasture-tree mixed plantings-and five fertilization treatments-control, two doses of mineral fertilizer, and two doses of organic fertilizer (sewage sludge)-were tested in a greenhouse experiment over 2 yr. In the experiment, the wet and warm climate characteristics of Mediterranean irrigated croplands and the plant-to-plant and soil-to-plant interactions that occur in open-field agroforestry plantations were simulated. Following a factorial design with six replicates, 120 pots (30-cm radius and 120 cm deep) were filled with a sandy, alluvial soil common in the cultivated fluvial plains of the region. The greatest pasture production and tree growth were obtained with sewage sludge application. Both pasture production and tree growth decreased significantly in the pasture-tree mixed planting. Nitrate leaching was negligible in this latter treatment, except under the highest dose of sewage sludge application. The rapid mineralization of sludge suggested that this organic fertilizer should be used very cautiously in warm, irrigated Mediterranean soils. Mixed planting of pasture species and trees, such as , could be a useful tool for mitigating nitrate leaching from irrigated Mediterranean pastures on sandy soils. American Society of Agronomy, Crop Science Society of America, and Soil Science Society of America.

Strontium and cesium release mechanisms during unsaturated flow through waste-weathered Hanford sediments.

PubMed

Chang, Hyun-Shik; Um, Wooyong; Rod, Kenton; Serne, R Jeff; Thompson, Aaron; Perdrial, Nicolas; Steefel, Carl I; Chorover, Jon

2011-10-01

Leaching behavior of Sr and Cs in the vadose zone of Hanford site (Washington) was studied with laboratory-weathered sediments mimicking realistic conditions beneath the leaking radioactive waste storage tanks. Unsaturated column leaching experiments were conducted using background Hanford pore water focused on first 200 pore volumes. The weathered sediments were prepared by 6 months reaction with a synthetic Hanford tank waste leachate containing Sr and Cs (10(-5) and 10(-3) molal representative of LO- and HI-sediment, respectively) as surrogates for (90)Sr and (137)Cs. The mineral composition of the weathered sediments showed that zeolite (chabazite-type) and feldspathoid (sodalite-type) were the major byproducts but different contents depending on the weathering conditions. Reactive transport modeling indicated that Cs leaching was controlled by ion-exchange, while Sr release was affected primarily by dissolution of the secondary minerals. The later release of K, Al, and Si from the HI-column indicated the additional dissolution of a more crystalline mineral (cancrinite-type). A two-site ion-exchange model successfully simulated the Cs release from the LO-column. However, a three-site ion-exchange model was needed for the HI-column. The study implied that the weathering conditions greatly impact the speciation of the secondary minerals and leaching behavior of sequestrated Sr and Cs.

[Effects of different amounts of phosphate fertilizers on copper, zinc transfer in red soil under the application of KH2PO4].

PubMed

Guo, Liang; Li, Zhong-wu; Huang, Bin; Wang, Yan; Zhang, Yan

2014-09-01

In order to study the effects of different phosphate addition amounts on migration and transformation of heavy metals (Cu, Zn) in soil, an indoor leaching experiment using soil columns was carry out to study the leaching behavior of Cu and Zn. The KH2PO4 was chosen as the fertilizer application at the doses of 5 mg.kg-1, 15 mg.kg-1 and 25 mg.kg-1. The results showed that KH2PO4, could reduce the leachate pH, but different phosphate amounts had little effect on leachate pH, pH in leachate kept rising in the whole leaching process. With the application of KH2PO4, Cu migration was mainly in the surface layer while Zn migrated into deeper soil. Concentrations of Cu, Zn in deep soil leachate were low indicating that it was harmless to the shallow groundwater. After leaching, heavy metals mainly existed in the residual form in soil, the proportion of residual form of Cu was around 60% and the proportion of residual form of Zn was around 40%. High concentration of KH2PO4 helps the transformation of Zn from residual organic combination state to exchange state.

Evidence of Coal-Fly-Ash Toxic Chemical Geoengineering in the Troposphere: Consequences for Public Health.

PubMed

Herndon, J Marvin

2015-08-11

The widespread, intentional and increasingly frequent chemical emplacement in the troposphere has gone unidentified and unremarked in the scientific literature for years. The author presents evidence that toxic coal combustion fly ash is the most likely aerosolized particulate sprayed by tanker-jets for geoengineering, weather-modification and climate-modification purposes and describes some of the multifold consequences on public health. Two methods are employed: (1) Comparison of 8 elements analyzed in rainwater, leached from aerosolized particulates, with corresponding elements leached into water from coal fly ash in published laboratory experiments, and (2) Comparison of 14 elements analyzed in dust collected outdoors on a high-efficiency particulate air (HEPA) filter with corresponding elements analyzed in un-leached coal fly ash material. The results show: (1) the assemblage of elements in rainwater and in the corresponding experimental leachate are essentially identical. At a 99% confidence interval, they have identical means (T-test) and identical variances (F-test); and (2) the assemblage of elements in the HEPA dust and in the corresponding average un-leached coal fly ash are likewise essentially identical. The consequences on public health are profound, including exposure to a variety of toxic heavy metals, radioactive elements, and neurologically-implicated chemically mobile aluminum released by body moisture in situ after inhalation or through transdermal induction.

Total recovery of nitrogen and phosphorus from three wetland plants by fast pyrolysis technology.

PubMed

Liu, Wu-Jun; Zeng, Fan-Xin; Jiang, Hong; Yu, Han-Qing

2011-02-01

Fast pyrolysis of three wetland plants (Alligator weed, Oenanthe javanica and Typha angustifolia) in a vertical drop fixed bed reactor was investigated in this study. The experiments were carried out at different pyrolysis temperatures, and the maximum bio-oil yields achieved were 42.3%, 40.2% and 43.6% for Alligator weed, Oenanthe javanica and Typha angustifolia, respectively. The elemental composition of the bio-oil and char were analyzed, and the results show that a low temperature was appropriate for the nitrogen and phosphorus enrichment in char. GC-MS analysis shows that nitrogenous compounds, phenols and oxygenates were the main categories in the bio-oil. A series of leaching tests were carried out to examine the recovery of the nitrogen and phosphorus in the char, and the results indicate that significant fractions of nitrogen and phosphorus could be recovered by leaching process. Copyright © 2010 Elsevier Ltd. All rights reserved.

Leaching of natural colloids from forest topsoils and their relevance for phosphorus mobility.

PubMed

Missong, Anna; Holzmann, Stefan; Bol, Roland; Nischwitz, Volker; Puhlmann, Heike; V Wilpert, Klaus; Siemens, Jan; Klumpp, Erwin

2018-09-01

The leaching of P from the upper 20cm of forest topsoils influences nutrient (re-)cycling and the redistribution of available phosphate and organic P forms. However, the effective leaching of colloids and associated P forms from forest topsoils was so far sparsely investigated. We demonstrated through irrigation experiments with undisturbed mesocosm soil columns, that significant proportions of P leached from acidic forest topsoils were associated with natural colloids. These colloids had a maximum size of 400nm. By means of Field-flow fractionation the leached soil colloids could be separated into three size fractions. The size and composition was comparable to colloids present in acidic forest streams known from literature. The composition of leached colloids of the three size classes was dominated by organic carbon. Furthermore, these colloids contained large concentrations of P which amounted between 12 and 91% of the totally leached P depending on the type of the forest soil. The fraction of other elements leached with colloids ranged between 1% and 25% (Fe: 1-25%; C org : 3-17%; Al: <4%; Si, Ca, Mn: all <2%). The proportion of colloid-associated P decreased with increasing total P leaching. Leaching of total and colloid-associated P from the forest surface soil did not increase with increasing bulk soil P concentrations and were also not related to tree species. The present study highlighted that colloid-facilitated P leaching can be of higher relevance for the P leaching from forest surface soils than dissolved P and should not be neglected in soil water flux studies. Copyright © 2018 Elsevier B.V. All rights reserved.

Effects of simulated acid rain on microbial characteristics in a lateritic red soil

Treesearch

Hua-qin Xu; Jia-en Zhang; Ying Ouyang; Ling Lin; Guo-ming Quan; Ben-liang Zhao; Jia-yu Yu

2015-01-01

A laboratory experiment was performed to examine the impact of simulated acid rain (SAR) on nutrient leaching, microbial biomass, and microbial activities in a lateritic red soil in South China. The soil column leaching experiment was conducted over a 60-day period with the following six SAR pH treatments (levels): 2.5, 3.0, 3.5, 4.0, 4.5, and 5.0 and one control...

Leaching lithium from the anode electrode materials of spent lithium-ion batteries by hydrochloric acid (HCl).

PubMed

Guo, Yang; Li, Feng; Zhu, Haochen; Li, Guangming; Huang, Juwen; He, Wenzhi

2016-05-01

Spent lithium-ion batteries (LIBs) are considered as an important secondary resource for its high contents of valuable components, such as lithium and cobalt. Currently, studies mainly focus on the recycling of cathode electrodes. There are few studies concentrating on the recovery of anode electrodes. In this work, based on the analysis result of high amount of lithium contained in the anode electrode, the acid leaching process was applied to recycle lithium from anode electrodes of spent LIBs. Hydrochloric acid was introduced as leaching reagent, and hydrogen peroxide as reducing agent. Within the range of experiment performed, hydrogen peroxide was found to have little effect on lithium leaching process. The highest leaching recovery of 99.4wt% Li was obtained at leaching temperature of 80°C, 3M hydrochloric acid and S/L ratio of 1:50g/ml for 90min. The graphite configuration with a better crystal structure obtained after the leaching process can also be recycled. Copyright © 2015 Elsevier Ltd. All rights reserved.

[Leaching Remediation of Copper and Lead Contaminated Lou Soil by Saponin Under Different Conditions].

PubMed

Deng, Hong-xia; Yang, Ya-li; Li, Zhen; Xu, Yan; Li, Rong-hua; Meng, Zhao-fu; Yang, Ya-ti

2015-04-01

In order to investigate the leaching remediation effect of the eco-friendly biosurfactant saponin for Cu and Pb in contaminated Lou soil, batch tests method was used to study the leaching effect of saponin solution on single Cu, Pb contaminated Lou soil and mixed Cu and Pb contaminated Lou soil under different conditions such as reaction time, mass concentration of saponin, pH, concentration of background electrolyte and leaching times. The results showed that the maximum leaching removal effect of Cu and Pb in contaminated Lou soil was achieved by complexation of the heavy metals with saponin micelle, when the mass concentration of saponin solution was 50 g x L(-1), pH was 5.0, the reaction time was 240 min, and there was no background electrolyte. In single and mixed contaminated Lou soil, the leaching percentages of Cu were 29.02% and 25.09% after a single leaching with 50 g x L(-1) saponin under optimal condition, while the single leaching percentages of Pb were 31.56% and 28.03%, respectively. The result indicated the removal efficiency of Pb was more significant than that of Cu. After 4 times of leaching, the cumulative leaching percentages of Cu reached 58.92% and 53.11%, while the cumulative leaching percentages of Pb reached 77.69% and 65.32% for single and mixed contaminated Lou soil, respectively. The fractionation results of heavy metals in soil before and after a single leaching showed that the contents of adsorbed and exchangeable Cu and Pb increased in the contaminated soil, while the carbonate-bound, organic bound and sulfide residual Cu and Pb in the contaminated Lou soil could be effectively removed by saponin.

Leaching Behavior Of Mineral Processing Waste: Comparison Of Batch And Column Investigations

EPA Science Inventory

In this study, a comparison of laboratory batch and column experiments on metal release profile from a mineral processing waste (MPW) is presented. Batch (equilibrium) and column (dynamic) leaching tests were conducted on ground MPW at different liquid–solid ratios (LS) to determ...

Heavy metals in urban soils of East St. Louis, IL. Part II: Leaching characteristics and modeling.

PubMed

Kaminski, M D; Landsberger, S

2000-09-01

The city of East St. Louis, IL, has a history of abundant industrial activities including smelters of ferrous and non-ferrous metals, a coal-fired power plant, companies that produced organic and inorganic chemicals, and petroleum refineries. Following a gross assessment of heavy metals in the community soils (see Part I of this two-part series), leaching tests were performed on specific soils to elucidate heavy metal-associated mineral fractions and general leachability. Leaching experiments, including the Toxicity Characteristic Leaching Procedure (TLCP) and column tests, and sequential extractions, illustrated the low leachability of metals in East St. Louis soils. The column leachate results were modeled using a formulation developed for fly ash leaching. The importance of instantaneous dissolution was evident from the model. By incorporating desorption/adsorption terms into the source term, the model was adapted very well to the time-dependent heavy metal leachate concentrations. The results demonstrate the utility of a simple model to describe heavy metal leaching from contaminated soils.

Heavy Metals in Urban Soils of East St. Louis, IL Part II: Leaching Characteristics and Modeling.

PubMed

Kaminski, Michael D; Landsberger, Sheldon

2000-09-01

The city of East St. Louis, IL, has a history of abundant industrial activities including smelters of ferrous and non-ferrous metals, a coal-fired power plant, companies that produced organic and inorganic chemicals, and petroleum refineries. Following a gross assessment of heavy metals in the community soils (see Part I of this two-part series), leaching tests were performed on specific soils to elucidate heavy metal-associated mineral fractions and general leachability. Leaching experiments, including the Toxicity Characteristic Leaching Procedure (TLCP) and column tests, and sequential extractions, illustrated the low leachability of metals in East St. Louis soils. The column leachate results were modeled using a formulation developed for fly ash leaching. The importance of instantaneous dissolution was evident from the model. By incorporating desorption/adsorption terms into the source term, the model was adapted very well to the time-dependent heavy metal leachate concentrations. The results demonstrate the utility of a simple model to describe heavy metal leaching from contaminated soils.

Simultaneous leaching of arsenite, arsenate, selenite and selenate, and their migration in tunnel-excavated sedimentary rocks: I. Column experiments under intermittent and unsaturated flow.

PubMed

Tabelin, Carlito Baltazar; Sasaki, Ryosuke; Igarashi, Toshifumi; Park, Ilhwan; Tamoto, Shuichi; Arima, Takahiko; Ito, Mayumi; Hiroyoshi, Naoki

2017-11-01

Rocks excavated in tunnel construction projects for roads and railways throughout Japan often leached out hazardous trace elements like arsenic (As) and selenium (Se) upon their exposure to the environment. In nature, the various oxyanionic species of As and Se not only coexist but also exhibit contrasting adsorption-desorption behaviors, so speciation is a crucial factor in their migration through natural geologic media. In this study, the leaching and transport of arsenite (As III ), arsenate (As V ), selenite (Se IV ) and selenate (Se VI ) in four tunnel-excavated rocks from the Cretaceous-Paleocene Yezo forearc basin were investigated using laboratory column experiments supplemented by batch leaching experiments. The single- and consecutive-batch leaching results revealed that As III , As V , Se IV and Se VI were released simultaneously, which could be attributed to the rapid dissolution of trace evaporite salts found in the rocks. Arsenic in the leachates was also predominated by As V while Se IV and Se VI concentrations were nearly equal, which are both consistent with predictions of equilibrium Eh-pH diagrams. Under intermittent and unsaturated flow, however, periods when As III and Se VI predominated in the effluents were observed. Spatial distributions of As and Se species with depth at the end of the column experiments suggest that migrations of As III , As V and Se IV were delayed, the extent of which depended on the rock. These results indicate that migration and speciation of As and Se in the rocks are controlled by preferential adsorption-desorption reactions, the effects of which were most probably magnified by changes in the pH and concentrations of coexisting ions due to intermittent and unsaturated flow. Copyright © 2017 Elsevier Ltd. All rights reserved.

Preferential flow, nitrogen transformations and 15N balance under urine-affected areas of irrigated and non-irrigated clover-based pastures

NASA Astrophysics Data System (ADS)

Pakro, Naser; Dillon, Peter

1995-12-01

Urine-affected areas can lead to considerable losses of N by leaching, ammonia volatilisation and denitrification from dairy pastures in the southeast of South Australia. Potable groundwater supplies are considered to have become contaminated by nitrate as a result of leaching from these leguminous pastures. Dairy cow urine, labelled with 15N urea, was applied to micro-plots and mini-lysimeters installed in two adjacent irrigated (white clover-rye grass) and non-irrigated (subterranean clover-annual grasses) paddocks of a dairy farm on four occasions representing different seasonal conditions. These experiments allowed measurement of nitrogen transformations, recovery of 15N in the pasture and soil, and leaching below various depths. Gaseous losses were calculated from the nitrogen balance. The results of the four experiments showed that within a day of urine application up to 40% of the applied urinary-N was leached below a depth of 150 mm as a result of macropore flow in the irrigated paddock, and up to 24% in the non-irrigated one. After application to the irrigated paddock 17% of the urinary-N moved immediately below 300 mm but only 2% below the 450-mm depth. The urinary-N remaining in the soil was converted from urea to ammonium within a day regardless of season. Within the first 7 days of application six times more nitrate was produced in summer than in winter. This has obvious implications for leaching potential. Leaching of 15N from the top 150 mm of soil, following urine applications in all seasons, was between 41% and 62% of the applied 15N in the irrigated paddock and 25-51% in the non-irrigated paddock. However, leaching losses measured at depths of 300 or 450 mm were smaller by a factor of 2-4. The leaching loss of 15N applied in spring in both paddocks was 41% below 150 mm and 12% below 450 mm. Recovery of 15N from the soil-plant system in the 450-nm deep lysimeters was ˜60% of that applied. Estimated ammonia was ˜9% of applied 15N with no paddock or season effect. No denitrification was evident in summer nor in the non-irrigated paddock in winter but 12% of the applied 15N was lost due denitrification following winter application to the irrigated paddock. Estimated 15N loss due to denitrification from urine applied in spring was ˜13% of that applied and no difference was found between paddocks. The combination of mini-lysimeters, micro-plots and 15N measurements enabled the nitrogen budget to be determined during four periods throughout the year.

Spatial distribution of solute leaching with snowmelt and irrigation: measurements and simulations

NASA Astrophysics Data System (ADS)

Schotanus, D.; van der Ploeg, M. J.; van der Zee, S. E. A. T. M.

2013-04-01

Transport of a tracer and a degradable solute in a heterogeneous soil was measured in the field, and simulated with several transient and steady state infiltration rates. Leaching surfaces were used to investigate the solute leaching in space and time simultaneously. In the simulations, a random field for the scaling factor in the retention curve was used for the heterogeneous soil, which was based on the spatial distribution of drainage in an experiment with a multi-compartment sampler. As a criterion to compare the results from simulations and observations, the sorted and cumulative total drainage in a cell was used. The effect of the ratio of the infiltration rate over the degradation rate on leaching of degradable solutes was investigated. Furthermore, the spatial distribution of the leaching of degradable and non-degradable solutes was compared. The infiltration rate determines the amount of leaching of the degradable solute. This can be partly explained by a decreasing travel time with an increasing infiltration rate. The spatial distribution of the leaching also depends on the infiltration rate. When the infiltration rate is high compared to the degradation rate, the leaching of the degradable solute is similar as for the tracer. The fraction of the pore space of the soil that contributes to solute leaching increases with an increasing infiltration rate. This fraction is similar for a tracer and a degradable solute. With increasing depth, the leaching becomes more homogeneous, as a result of dispersion. The spatial distribution of the solute leaching is different under different transient infiltration rates, therefore, also the amount of leaching is different. With independent stream tube approaches, this effect would be ignored.

Spatial distribution of solute leaching with snowmelt and irrigation: measurements and simulations

NASA Astrophysics Data System (ADS)

Schotanus, D.; van der Ploeg, M. J.; van der Zee, S. E. A. T. M.

2012-12-01

Transport of a tracer and a degradable solute in a heterogeneous soil was measured in the field, and simulated with several transient and steady state infiltration rates. Leaching surfaces were used to investigate the solute leaching in space and time simultaneously. In the simulations, a random field for the scaling factor in the retention curve was used for the heterogeneous soil, which was based on the spatial distribution of drainage in an experiment with a multi-compartment sampler. As a criterion to compare the results from simulations and observations, the sorted and cumulative total drainage in a cell was used. The effect of the ratio of the infiltration rate over the degradation rate on leaching of degradable solutes was investigated. Furthermore, the spatial distribution of the leaching of degradable and non-degradable solutes was compared. The infiltration rate determines the amount of leaching of the degradable solute. This can be partly explained by a decreasing travel time with an increasing infiltration rate. The spatial distribution of the leaching also depends on the infiltration rate. When the infiltration rate is high compared to the degradation rate, the leaching of the degradable solute is similar as for the tracer. The fraction of the soil that contributes to solute leaching increases with an increasing infiltration rate. This fraction is similar for a tracer and a degradable solute. With increasing depth, the leaching becomes more homogeneous, as a result of dispersion. The spatial distribution of the solute leaching is different under different transient infiltration rates, therefore also the amount of leaching is different. With independent stream tube approaches, this effect would be ignored.

Identifying a rainfall event threshold triggering herbicide leaching by preferential flow

NASA Astrophysics Data System (ADS)

McGrath, G. S.; Hinz, C.; Sivapalan, M.; Dressel, J.; Pütz, T.; Vereecken, H.

2010-02-01

How can leaching risk be assessed if the chemical flux and/or the toxicity is highly uncertain? For many strongly sorbing pesticides it is known that their transport through the unsaturated zone occurs intermittently through preferential flow, triggered by significant rainfall events. In these circumstances the timing and frequency of these rainfall events may allow quantification of leaching risk to overcome the limitations of flux prediction. In this paper we analyze the leaching behavior of bromide and two herbicides, methabenzthiazuron and ethidimuron, using data from twelve uncropped lysimeters, with high-resolution climate data, in order to identify the rainfall controls on rapid solute leaching. A regression tree analysis suggested that a coarse-scale fortnightly to monthly water balance was a good predictor of short-term increases in drainage and bromide transport. Significant short-term herbicide leaching, however, was better predicted by the occurrence of a single storm with a depth greater than a 19 mm threshold. Sampling periods where rain events exceeded this threshold accounted for between 38% and 56% of the total mass of herbicides leached during the experiment. The same threshold only accounted for between 1% and 10% of the total mass of bromide leached. On the basis of these results, we conclude that in this system, the leaching risks of strongly sorbing chemicals can be quantified by the timing and frequency of these large rainfall events. Empirical and modeling approaches are suggested to apply this frequentist approach to leaching risk assessment to other soil-climate systems.

Selective recovery of gold from waste mobile phone PCBs by hydrometallurgical process.

PubMed

Kim, Eun-young; Kim, Min-seuk; Lee, Jae-chun; Pandey, B D

2011-12-30

The leaching of gold from the scrap mobile phone PCBs by electro-generated chlorine as an oxidant and its recovery by ion exchange process was investigated. The leaching experiments were carried out by employing separate leaching reactor connected with the anode compartment of a Cl(2) gas generator. The leaching of gold increased with increase in temperature and initial concentration of chlorine, and was favorable even at low concentration of acid, whereas copper leaching increased with increase in concentration of acid and decrease in temperature. In a two-stage leaching process, copper was mostly dissolved (97%) in 165 min at 25°C during the 1st stage leaching in 2.0 mol/L HCl by electro-generated chlorine at a current density of 714A/m(2) along with a minor recovery of gold (5%). In the 2nd stage gold was mostly leached out (93% recovery, ∼67 mg/L) from the residue of the 1st stage by the electro-generated chlorine in 0.1 mol/L HCl. Gold recovery from the leach liquor by ion exchange using Amberlite XAD-7HP resin was found to be 95% with the maximum amount of gold adsorbed as 46.03 mg/g resin. A concentrated gold solution, 6034 mg/L with 99.9% purity was obtained in the ion exchange process. Copyright © 2011 Elsevier B.V. All rights reserved.

Herbicide Leaching Column for a Weed Science Teaching Laboratory.

ERIC Educational Resources Information Center

Ahrens, W. H.

1986-01-01

Presents an experiment which enables weed science students to observe first-hand the process of herbicide leaching in soils. Features of this technique which demonstrate the movement of herbicide within a column of soil are outlined. Diagrams are provided of the apparatus employed in the exercise. (ML)

Research on the Characteristics and Mechanism of the Cumulative Release of Antimony from an Antimony Smelting Slag Stacking Area under Rainfall Leaching

PubMed Central

Zhou, Yingying; Deng, Renjian

2017-01-01

We aimed to study the characteristics and the mechanism of the cumulative release of antimony at an antimony smelting slag stacking area in southern China. A series of dynamic and static leaching experiments to simulate the effects of rainfall were carried out. The results showed that the release of antimony from smelting slag increased with a decrease in the solid-liquid ratio, and the maximum accumulated release was found to be 42.13 mg Sb/kg waste and 34.26 mg Sb/kg waste with a solid/liquid ratio of 1 : 20; the maximum amount of antimony was released within 149–420 μm size fraction with 7.09 mg/L of the cumulative leaching. Also, the antimony release was the greatest and most rapid at pH 7.0 with the minimum release found at pH 4.0. With an increase in rainfall duration, the antimony release increased. The influence of variation in rainfall intensity on the release of antimony from smelting slag was small. PMID:28804669

The mineralogical phase transformation of invisible gold-concentrate by microwave heating, and enhancement of their gold leaching rate

NASA Astrophysics Data System (ADS)

Bak, Geonyoung; Kim, Bongju; Choi, Nagchoul; Park*, Cheonyoung

2015-04-01

In this study, in order to obtain the maximum Au leaching rate, an invisible gold concentrate sample was microwave-treated and a thiourea leaching experiment was performed. It is found that gold exists as invisible as a result of observation with an optical microscope and an electron microscope. As the invisible gold concentrate sample was exposed to microwave longer, its temperature and weight loss were increased together and its S content was decreased. The conditions for the maximum Au leaching rate and the fast leaching effect were a particle size of -325×400 mesh, exposure to microwave for 70 minutes, 1.0 g of thiourea, 0.0504 g of sodium sulfite and 0.425 g of ferric sulfate. However, the condition under which Au was leached out to the maximum was applied to the control sample, but its Au leaching rate was just in a range of 78% to 88%. Such results suggest that the effect of sodium sulfite and ferric sulfate was more effective in the microwave-treated sample than in the control sample. Therefore, it was confirmed that the complete and very fast Au leaching can be achieved by means of the microwave pretreatment of invisible gold concentrate.

Evaluation of selected static methods used to estimate element mobility, acid-generating and acid-neutralizing potentials associated with geologically diverse mining wastes

USGS Publications Warehouse

Hageman, Philip L.; Seal, Robert R.; Diehl, Sharon F.; Piatak, Nadine M.; Lowers, Heather

2015-01-01

A comparison study of selected static leaching and acid–base accounting (ABA) methods using a mineralogically diverse set of 12 modern-style, metal mine waste samples was undertaken to understand the relative performance of the various tests. To complement this study, in-depth mineralogical studies were conducted in order to elucidate the relationships between sample mineralogy, weathering features, and leachate and ABA characteristics. In part one of the study, splits of the samples were leached using six commonly used leaching tests including paste pH, the U.S. Geological Survey (USGS) Field Leach Test (FLT) (both 5-min and 18-h agitation), the U.S. Environmental Protection Agency (USEPA) Method 1312 SPLP (both leachate pH 4.2 and leachate pH 5.0), and the USEPA Method 1311 TCLP (leachate pH 4.9). Leachate geochemical trends were compared in order to assess differences, if any, produced by the various leaching procedures. Results showed that the FLT (5-min agitation) was just as effective as the 18-h leaching tests in revealing the leachate geochemical characteristics of the samples. Leaching results also showed that the TCLP leaching test produces inconsistent results when compared to results produced from the other leaching tests. In part two of the study, the ABA was determined on splits of the samples using both well-established traditional static testing methods and a relatively quick, simplified net acid–base accounting (NABA) procedure. Results showed that the traditional methods, while time consuming, provide the most in-depth data on both the acid generating, and acid neutralizing tendencies of the samples. However, the simplified NABA method provided a relatively fast, effective estimation of the net acid–base account of the samples. Overall, this study showed that while most of the well-established methods are useful and effective, the use of a simplified leaching test and the NABA acid–base accounting method provide investigators fast, quantitative tools that can be used to provide rapid, reliable information about the leachability of metals and other constituents of concern, and the acid-generating potential of metal mining waste.

Aminocyclopyrachlor sorption-desorption and leaching from three Brazilian soils.

PubMed

Francisco, Jeane G; Mendes, Kassio F; Pimpinato, Rodrigo F; Tornisielo, Valdemar L; Guimarães, Ana C D

2017-07-03

This study aimed to evaluate the sorption-desorption and leaching of aminocyclopyrachlor from three Brazilian soils. The sorption-desorption of 14 C-aminocyclopyrachlor was evaluated using the batch method and leaching was assessed in glass columns. The Freundlich model showed an adequate fit for the sorption-desorption of aminocyclopyrachlor. The Freundlich sorption coefficient [K f (sorption) ] ranged from 0.37 to 1.34 µmol (1-1/n) L 1/n kg -1 and showed a significant positive correlation with the clay content of the soil, while the K f (desorption) ranged from 3.62 to 5.36 µmol (1-1/n) L 1/n kg -1 . The K f (desorption) values were higher than their respective K f (sorption) , indicating that aminocyclopyrachlor sorption is reversible, and the fate of this herbicide in the environment can be affected by leaching. Aminocyclopyrachlor was detected at all depths (0-30 cm) in all the studied soils, where leaching was influenced by soil texture. The total herbicide leaching from the sandy clay and clay soils was <0.06%, whereas, ∼3% leached from the loamy sand soil. The results suggest that aminocyclopyrachlor has a high potential of leaching, based on its low sorption and high desorption capacities. Therefore, this herbicide can easily contaminate underground water resources.

Comparison of mine waste assessment methods at the Rattler mine site, Virginia Canyon, Colorado

USGS Publications Warehouse

Hageman, Phil L.; Smith, Kathleen S.; Wildeman, Thomas R.; Ranville, James F.

2005-01-01

In a joint project, the mine waste-piles at the Rattler Mine near Idaho Springs, Colorado, were sampled and analyzed by scientists from the U.S. Geological Survey (USGS) and the Colorado School of Mines (CSM). Separate sample collection, sample leaching, and leachate analyses were performed by both groups and the results were compared. For the study, both groups used the USGS sampling procedure and the USGS Field Leach Test (FLT). The leachates generated from these tests were analyzed for a suite of elements using ICP-AES (CSM) and ICP-MS (USGS). Leachate geochemical fingerprints produced by the two groups for composites collected from the same mine waste showed good agreement. In another set of tests, CSM collected another set of Rattler mine waste composite samples using the USGS sampling procedure. This set of composite samples was leached using the Colorado Division of Minerals and Geology (CDMG) leach test, and a modified Toxicity Characteristic Leaching Procedure (TCLP) leach test. Leachate geochemical fingerprints produced using these tests showed a variation of more than a factor of two from the geochemical fingerprints produced using the USGS FLT leach test. We have concluded that the variation in the results is due to the different parameters of the leaching tests and not due to the sampling or analytical methods.

Leaching of Cu, Cd, Pb, and phosphorus and their availability in the phosphate-amended contaminated soils under simulated acid rain.

PubMed

Cui, Hongbiao; Zhang, Shiwen; Li, Ruyan; Yi, Qitao; Zheng, Xuebo; Hu, Youbiao; Zhou, Jing

2017-09-01

Phosphate amendments have been used to immobilize heavy metal-contaminated soils. However, phosphate amendments contain large amounts of phosphorus, which could leach out to potentially contaminate groundwater and surface water. A laboratory column leaching experiment was designed to study the effects of simulated acid rain (SAR) on the potential release of copper (Cu), lead (Pb), cadmium (Cd), and phosphorus (P), and their availability after immobilizing with hydroxyapatite (HAP) and potassium dihydrogen phosphate (PDP). The application of HAP and PDP enhanced the leachate electrical conductivity, total organic carbon, and pH. Higher P was found in the PDP- (>4.29 mg L -1 ) and HAP-treated (>1.69 mg L -1 ) columns than that in untreated (<0.2 mg L -1 ) columns, and they were both over the class V limit (0.4 mg L -1 ) mandated by the Chinese National Quality Standards for Surface Waters (GB 3838-2002). PDP application decreased the leachate Cu, Pb, and Cd effectively; however, HAP addition increased leachate Cu and Pb. HAP and PDP applications decreased the soil CaCl 2 -extractable and exchangeable fraction of Cu, Pb, and Cd, and increased resin P. However, eluviations transformed the heavy metals from inactive to active fractions and reduced soil labile P. These findings showed that HAP and PDP had a potential risk of excessive P-induced eutrophication. Meanwhile, more attention should be paid to the leaching loss of multiple metals because phosphate amendments might promote the leaching of some metals while immobilizing others.

Risk of Leaching in Soils Amended by Compost and Digestate from Municipal Solid Waste

PubMed Central

Tarquis, Ana M.; Cartagena, M. Carmen

2014-01-01

New European directives have proposed the direct application of compost and digestate produced from municipal solid wastes as organic matter sources in agricultural soils. Therefore information about phosphorus leaching from these residues when they are applied to the soil is increasingly important. Leaching experiments were conducted to determine the P mobility in compost and digestate mixtures, supplying equivalent amounts to 100 kg P ha−1 to three different types of soils. The tests were performed in accordance with CEN/TS 14405:2004 analyzing the maximum dissolved reactive P and the kinetic rate in the leachate. P biowaste fractionation indicated that digestate has a higher level of available P than compost has. In contrast, P losses in leaching experiments with soil-compost mixtures were higher than in soil-digestate mixtures. For both wastes, there was no correlation between dissolved reactive P lost and the water soluble P. The interaction between soil and biowaste, the long experimentation time, and the volume of leachate obtained caused the waste's wettability to become an influential parameter in P leaching behavior. The overall conclusion is that kinetic data analysis provides valuable information concerning the sorption mechanism that can be used for predicting the large-scale behavior of soil systems. PMID:25003139

Kinetic and Mechanism Study of Vanadium Acid Leaching from Black Shale Using Microwave Heating Method

NASA Astrophysics Data System (ADS)

Wang, Jing-peng; Zhang, Yi-min; Huang, Jing; Liu, Tao

2018-04-01

The leaching kinetics of the vanadium leaching process were investigated by the comparison of microwave heating and conventional heating methods. Microwave heating with CaF2 had a synergistic effect and improved the vanadium leaching efficiency. In contrast to conventional heating leaching, microwave heating accelerated the vanadium leaching rate by approximately 1-3% and by approximately 15% when CaF2 was also used. The kinetics analysis showed that the calculated activation energy decreased in the microwave heating method in the presence and absence of CaF2. The control procedure of leaching also changed from a chemical reaction control step to a mixed chemical diffusion control step upon the addition of CaF2. Microwave heating was shown to be suitable for leaching systems with diffusion or mixed chemical diffusion control steps when the target mineral does not have a microwave absorbing ability.

Kinetic and Mechanism Study of Vanadium Acid Leaching from Black Shale Using Microwave Heating Method

NASA Astrophysics Data System (ADS)

Wang, Jing-peng; Zhang, Yi-min; Huang, Jing; Liu, Tao

2018-06-01

The leaching kinetics of the vanadium leaching process were investigated by the comparison of microwave heating and conventional heating methods. Microwave heating with CaF2 had a synergistic effect and improved the vanadium leaching efficiency. In contrast to conventional heating leaching, microwave heating accelerated the vanadium leaching rate by approximately 1-3% and by approximately 15% when CaF2 was also used. The kinetics analysis showed that the calculated activation energy decreased in the microwave heating method in the presence and absence of CaF2. The control procedure of leaching also changed from a chemical reaction control step to a mixed chemical diffusion control step upon the addition of CaF2. Microwave heating was shown to be suitable for leaching systems with diffusion or mixed chemical diffusion control steps when the target mineral does not have a microwave absorbing ability.

Leaching of metals from large pieces of printed circuit boards using citric acid and hydrogen peroxide.

PubMed

Jadhav, Umesh; Su, C; Hocheng, Hong

2016-12-01

In the present study, the leaching of metals from large pieces of computer printed circuit boards (CPCBs) was studied. A combination of citric acid (0.5 M) and 1.76 M hydrogen peroxide (H 2 O 2 ) was used to leach the metals from CPCB piece. The influence of system variables such as H 2 O 2 concentration, concentration of citric acid, shaking speed, and temperature on the metal leaching process was investigated. The complete metal leaching was achieved in 4 h from a 4 × 4 cm CPCB piece. The presence of citric acid and H 2 O 2 together in the leaching solution is essential for complete metal leaching. The optimum addition amount of H 2 O 2 was 5.83 %. The citric acid concentration and shaking speed had an insignificant effect on the leaching of metals. The increase in the temperature above 30 °C showed a drastic effect on metal leaching process.

[Biooxidation of gold-bearing sulfide ore and subsequent biological treatment of cyanidation residues].

PubMed

Kanaev, A T; Bulaev, A G; Semenchenko, G V; Kanaeva, Z K; Shilmanova, A A

2016-01-01

The percolation biooxidation parameters of ore from the Bakyrchik deposit were studied. An investigation of the technological parameters (such as the concentration of leaching agents, irrigation intensity, and pauses at various stages of the leaching) revealed the optimal mode for precious metal extraction. The stages of the ore processing were biooxidation, gold extraction by cyanidation or thiosulfate leaching, and biological destruction of cyanide. The gold and silver recovery rates by cyanidation were 64.0 and 57.3%, respectively. The gold and silver recovery rates by thiosulfate leaching were 64.0 and 57.3%, respectively. Gold and silver recovery rates from unoxidized ore (control experiment) by cyanidation were 20.9 and 26.8%, respectively. Thiosulfate leaching of unoxidized ore allowed the extraction of 38.8 and 24.2% of the gold and silver, respectively. Cyanidation residues were treated with bacteria of the genus Alcaligenes in order to destruct cyanide.

Use of flue gas desulfurization gypsum for leaching Cd and Pb in reclaimed tidal flat soil.

PubMed

Yang, Ping; Li, Xian; Tong, Ze-Jun; Li, Qu-Sheng; He, Bao-Yan; Wang, Li-Li; Guo, Shi-Hong; Xu, Zhi-Min

2016-04-01

A soil column leaching experiment was conducted to eliminate heavy metals from reclaimed tidal flat soil. Flue gas desulfurization (FGD) gypsum was used for leaching. The highest removal rates of Cd and Pb in the upper soil layers (0-30 cm) were 52.7 and 30.5 %, respectively. Most of the exchangeable and carbonate-bound Cd and Pb were removed. The optimum FGD gypsum application rate was 7.05 kg·m(-2), and the optimum leaching water amount for the application was 217.74 L·m(-2). The application of FGD gypsum (two times) and the extension of the leaching interval time to 20 days increased the heavy metal removal rate in the upper soil layers. The heavy metals desorbed from the upper soil layers were re-adsorbed and fixed in the 30-70 cm soil layers.

Thermal treatment of stabilized air pollution control residues in a waste incinerator pilot plant. Part 2: Leaching characteristics of bottom ashes.

PubMed

Baun, Dorthe L; Christensen, Thomas H; Bergfeldt, Brita; Vehlow, Jürgen; Mogensen, Erhardt P B

2004-02-01

With the perspective of generating only one solid residue from waste incineration, co-feeding of municipal solid waste and air pollution control residues stabilized by the Ferrox process was investigated in the TAMARA pilot plant incinerator as described in Bergfeldt et al. (Waste Management Research, 22, 49-57, 2004). This paper reports on leaching from the combined bottom ashes. Batch leaching test, pH-static leaching tests, availability tests and column leaching tests were used to characterize the leaching properties. The leaching properties are key information in the context of reuse in construction or in landfilling of the combined residue. In general, the combined bottom ashes had leaching characteristics similar to the reference bottom ash, which contained no APC residue. However, As and Pb showed slightly elevated leaching from the combined bottom ashes, while Cr showed less leaching. The investigated combined bottom ashes had contents of metals comparable to what is expected at steady state after continuous co-feeding of APC residues. Only Cd and Pb were partly volatilized (30-40%) during the incineration process and thus the combined bottom ashes had lower contents of Cd and Pb than expected at steady state. Furthermore, a major loss of Hg was, not surprisingly, seen and co-feeding of Ferrox-products together with municipal solid waste will require dedicated removal of Hg in the flue gas to prevent a build up of Hg in the system. In spite of this, a combined single solid residue from waste incineration seems to be a significant environmental improvement to current technology.

Long-term simulations of water and isoproturon dynamics in a heterogeneous soil receiving different urban waste composts

NASA Astrophysics Data System (ADS)

Filipović, Vilim; Coquet, Yves; Pot, Valérie; Romić, Davor; Benoit, Pierre; Houot, Sabine

2016-04-01

Implementing various compost amendments and tillage practices has a large influence on soil structure and can create heterogeneities at the plot/field scale. While tillage affects soil physical properties, compost application influences also chemical properties like pesticide sorption and degradation. A long-term field experiment called "QualiAgro" (https://www6.inra.fr/qualiagro_eng/), conducted since 1998 aims at characterizing the agronomic value of urban waste composts and their environmental impacts. A modeling study was carried out using HYDRUS-2D for the 2004-2010 period to confront the effects of two different compost types combined with the presence of heterogeneities due to tillage in terms of water and isoproturon dynamics in soil. A municipal solid waste compost (MSW) and a co-compost of sewage sludge and green wastes (SGW) have been applied to experimental plots and compared to a control plot without any compost addition (CONT). Two wick lysimeters, 5 TDR probes, and 7 tensiometers were installed per plot to monitor water and isoproturon dynamics. In the ploughed layer, four zones with differing soil structure were identified: compacted clods (Δ), non-compacted soil (Γ), interfurrows (IF), and the plough pan (PP). These different soil structural zones were implemented into HYDRUS-2D according to field observation and using measured soil hydraulic properties. Lysimeter data showed (2004 -2010 period) that the CONT plot had the largest cumulative water outflow (1388 mm) compared to the MSW plot (962 mm) and SGW plot (979 mm). HYDRUS-2D was able to describe cumulative water outflow after calibration of soil hydraulic properties, for the whole 2004-2010 period with a model efficiency value of 0.99 for all three plots. Isoproturon leaching showed had the largest cumulative value in the CONT plot (21.31 μg) while similar cumulated isoproturon leachings were measured in the SGW (0.663 μg) and MSW (0.245 μg) plots. The model was able to simulate isoproturon leaching patterns except for the large preferential flow events that were observed in the MSW and CONT plots. The timing of these preferential flow events could be reproduced by the model but not their magnitude. Additional simulations were carried out, assuming temporal variation of the IPU degradation rate to explain the leaching events observed at the end of the monitoring period (2010). Modeling results indicate that spatial and temporal variations in pesticide degradation rate due to tillage and compost application play a major role in the dynamics of isoproturon leaching. Both types of compost were found to reduce isoproturon leaching on the long-term (6 years) duration of the field experiment. Keywords: Compost amendment; Soil heterogeneity; Conventional tillage; Water flow; Isoproturon; HYDRUS-2D

Investigation of the leaching behavior of lead in stabilized/solidified waste using a two-year semi-dynamic leaching test.

PubMed

Xue, Qiang; Wang, Ping; Li, Jiang-Shan; Zhang, Ting-Ting; Wang, Shan-Yong

2017-01-01

Long-term leaching behavior of contaminant from stabilization/solidification (S/S) treated waste stays unclear. For the purpose of studying long-term leaching behavior and leaching mechanism of lead from cement stabilized soil under different pH environment, semi-dynamic leaching test was extended to two years to investigate leaching behaviors of S/S treated lead contaminated soil. Effectiveness of S/S treatment in different scenarios was evaluated by leachability index (LX) and effective diffusion coefficient (D e ). In addition, the long-term leaching mechanism was investigated at different leaching periods. Results showed that no significant difference was observed among the values of the cumulative release of Pb, D e and LX in weakly alkaline and weakly acidic environment (pH value varied from 5.00 to 10.00), and all the controlling leaching mechanisms of the samples immersed in weakly alkaline and weakly acidic environments turned out to be diffusion. Strong acid environment would significantly affect the leaching behavior and leaching mechanism of lead from S/S monolith. The two-year variation of D e appeared to be time dependent, and D e values increased after the 210 th day in weakly alkaline and weakly acidic environment. Copyright © 2016 Elsevier Ltd. All rights reserved.

Presence and leaching of bisphenol a (BPA) from dental materials.

PubMed

Becher, Rune; Wellendorf, Hanne; Sakhi, Amrit Kaur; Samuelsen, Jan Tore; Thomsen, Cathrine; Bølling, Anette Kocbach; Kopperud, Hilde Molvig

2018-01-01

BPA has been reported to leach from some resin based dental restorative materials and materials used for orthodontic treatment. To confirm and update previous findings, especially in light of the new temporary lower threshold value for tolerable daily BPA intake, we have investigated the leaching of BPA from 4 composite filling materials, 3 sealants and 2 orthodontic bonding materials. The materials were either uncured and dissolved in methanol or cured. The cured materials were kept in deionized water for 24 hours or 2 weeks. Samples were subsequently analyzed by ultra-performance liquid chromatography coupled to mass spectrometry (UPLC-MS-MS). The composite filling material Tetric EvoFlow ® and the fissure sealant DELTON ® showed significantly higher levels of BPA leaching compared to control samples for all test conditions (uncured, 24 h leaching and 2 weeks leaching). There were no significant differences in amount of leached BPA for any of the tested materials after 24 hours compared to 2 weeks. These results show that BPA is still released from some dental materials despite the general concern about potential adverse effects of BPA. However, the amounts of BPA were relatively low and most likely represent a very small contribution to the total BPA exposure.

Effect of some amendments on leachate properties of a calcareous saline- sodic soil: A laboratory experiment

NASA Astrophysics Data System (ADS)

Yazdanpanah, Najme; Mahmoodabadi, Majid

2010-05-01

Soil salinity and sodicity are escalating problems worldwide, especially in Iran since 90 percent of the country is located in arid and semi-arid. Reclamation of sodic soils involves replacement of exchangeable Na by Ca. While some researches have been undertaken in the controllable laboratory conditions using soil column with emphasis on soil properties, the properties of effluent as a measure of soil reclamation remain unstudied. In addition, little attention has been paid to the temporal variability of effluent quality. The objective of this study was to investigate the effect of different amendments consist of gypsum, manure, pistachio residue, and their combination for ameliorating a calcareous saline sodic soil. Temporal variability of effluent properties during reclamation period was studied, as well. A laboratory experiment was conducted to evaluate the effect of different amendments using soil columns. The amendment treatments were: control, manure, pistachio residue, gypsum powder (equivalent of gypsum requirement), manure+gypsum and pistachio residue+gypsum, which were applied once in the beginning of the experiment. The study was performed in 120 days period and totally four irrigation treatments were supplied to each column. After irrigations, the effluent samples were collected every day at the bottom of the soil columns and were analyzed. The results show that for all treatments, cations (e.g. Ca, Mg, Na and K) in the outflow decreased with time, exponentially. Manure treatment resulted in highest rate of Ca, Mg, Na leaching from soil solution, in spite of the control which had the lowest rate. In addition, pistachio residue had the most effect on K leaching. Manure treatment showed the most EC and SAR in the leachate, while gypsum application leads to the least rate of them. The findings of this research reveal different rates of cations leaching from soil profile, which is important in environmental issues. Keywords: Saline sodic soil, Reclamation, Organic Matter, Gypsum, Leachate.

Study on gold concentrate leaching by iodine-iodide

NASA Astrophysics Data System (ADS)

Wang, Hai-xia; Sun, Chun-bao; Li, Shao-ying; Fu, Ping-feng; Song, Yu-guo; Li, Liang; Xie, Wen-qing

2013-04-01

Gold extraction by iodine-iodide solution is an effective and environment-friendly method. In this study, the method using iodine-iodide for gold leaching is proved feasible through thermodynamic calculation. At the same time, experiments on flotation gold concentrates were carried out and encouraging results were obtained. Through optimizing the technological conditions, the attained high gold leaching rate is more than 85%. The optimum process conditions at 25°C are shown as follows: the initial iodine concentration is 1.0%, the iodine-to-iodide mole ratio is 1:8, the solution pH value is 7, the liquid-to-solid mass ratio is 4:1, the leaching time is 4 h, the stirring intensity is 200 r/mim, and the hydrogen peroxide consumption is 1%.

Strontium and cesium release mechanisms during unsaturated flow through waste-weathered Hanford sediments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chang, Hyun-Shik; Um, Wooyong; Rod, Kenton A.

2011-10-01

Leaching behavior of Sr and Cs in the vadose zone of Hanford site (WA, USA) was studied with laboratory-weathered sediments mimicking realistic conditions beneath the leaking radioactive waste storage tanks. Unsaturated column leaching experiments were conducted using background Hanford pore water focused on first 200 pore volumes. The weathered sediments were prepared by 6 months reaction with a synthetic Hanford tank waste leachate containing Sr and Cs (10-5 and 10-3 molal representative of LO- and HI-sediment, respectively) as surrogates for 90Sr and 137Cs. The mineral composition of the weathered sediments showed that zeolite (chabazite-type) and feldspathoid (sodalite-type) were the majormore » byproducts but different contents depending on the weathering conditions. Reactive transport modeling indicated that Cs leaching was controlled by ion-exchange, while Sr release was affected primarily by dissolution of the secondary minerals. The later release of K, Al, and Si from the HI-column indicated the additional dissolution of a more crystalline mineral (cancrinite-type). A two-site ion-exchange model successfully simulated the Cs release from the LO-column. However, a three-site ion-exchange model was needed for the HI-column. The study implied that the weathering conditions greatly impact the speciation of the secondary minerals and leaching behavior of sequestrated Sr and Cs.« less

[Nitrogen Loss Through Different Ways in Cropland Under Conventional Fertilization: An In-situ Study of Summer Maize Season in the Middle and Lower Reaches of the Yangtze River].

PubMed

Sang, Meng-meng; Fan, Hui; Jiang, Shan-shan; Jiang, Jing-yan

2015-09-01

In order to better understand the characteristics of nitrogen loss through different pathways under conventional fertilization conditions, a field experiment was conducted to investigate the variations of N2O emission, NH3 volatilization, N losses through surface runoff and leaching caused by the application of nitrogen fertilizers during summer maize growing season in the Middle and Lower reaches of the Yangtze River, China. Our results showed that when compound fertilizer was used as basal fertilizer at the nitrogen rate of 150 kg.hm-2, and urea with the same level of fertilizing as topdressing, the N2O emission coefficient in the entire growing season was 3. 3%, NH3 volatilization loss rate was 10. 2%, and nitrogen loss rate by leaching and surface runoff was 11. 2% and 5. 1%, respectively. In addition, leaching was the main pathway of nitrogen loss after basal fertilizer, while NH, volatilization and nitrogen leaching accounted for the majority of nitrogen loss after topdressing, which suggested that nitrogen loss from different pathways mainly depended on the type of nitrogen fertilizer. Taken together, it appears to be effective to apply the new N fertilizer with low ammonia volatilization instead of urea when maize needs topdressing, so as to reduce N losses from N fertilizer.

Evidence of Coal-Fly-Ash Toxic Chemical Geoengineering in the Troposphere: Consequences for Public Health

PubMed Central

Herndon, J. Marvin

2015-01-01

The widespread, intentional and increasingly frequent chemical emplacement in the troposphere has gone unidentified and unremarked in the scientific literature for years. The author presents evidence that toxic coal combustion fly ash is the most likely aerosolized particulate sprayed by tanker-jets for geoengineering, weather-modification and climate-modification purposes and describes some of the multifold consequences on public health. Two methods are employed: (1) Comparison of 8 elements analyzed in rainwater, leached from aerosolized particulates, with corresponding elements leached into water from coal fly ash in published laboratory experiments, and (2) Comparison of 14 elements analyzed in dust collected outdoors on a high-efficiency particulate air (HEPA) filter with corresponding elements analyzed in un-leached coal fly ash material. The results show: (1) the assemblage of elements in rainwater and in the corresponding experimental leachate are essentially identical. At a 99% confidence interval, they have identical means (T-test) and identical variances (F-test); and (2) the assemblage of elements in the HEPA dust and in the corresponding average un-leached coal fly ash are likewise essentially identical. The consequences on public health are profound, including exposure to a variety of toxic heavy metals, radioactive elements, and neurologically-implicated chemically mobile aluminum released by body moisture in situ after inhalation or through transdermal induction. PMID:26270671

Leaching of Silver from Silver-Impregnated Food Storage Containers

ERIC Educational Resources Information Center

Hauri, James F.; Niece, Brian K.

2011-01-01

The use of silver in commercial products has proliferated in recent years owing to its antibacterial properties. Food containers impregnated with micro-sized silver promise long food life, but there is some concern because silver can leach out of the plastic and into the stored food. This laboratory experiment gives students the opportunity to…

LEAD LEACHING FROM IN-LINE BRASS DEVICES: A CRITICAL EVALUATION OF THE EXISTING STANDARD

EPA Science Inventory

The ANSI/NSF 61, Section 8 standard is intended to protect the public from in-line brass plumbing products that might leach excessive levels of lead to potable water. Experiments were conducted to examine the practical rigor of this test. Contrary to expectations, the test was no...

Study on copper kinetics in processing sulphide ore mixed with copper and zinc with sulfuric acid leaching under pressure

NASA Astrophysics Data System (ADS)

Wen-bo, LUO; Ji-kun, WANG; Yin, GAN

2018-01-01

Sulphide ore mixed with copper and zinc is processed with pressure acid leaching. Research is conducted on the copper kinetic. The stirring rate is set at 600 rpm which could eliminate the influence of external diffusions. Research is conducted on the factors affecting the copper leaching kinetic are temperature, pressure, concentration of sulfuric acid, particle size. The result shows that the apparent activity energy is 50.7 KJ/mol. We could determine that the copper leaching process is shrinking core model of chemical reaction control and work out the leaching equation.

Recycling of spent lithium-ion battery cathode materials by ammoniacal leaching.

PubMed

Ku, Heesuk; Jung, Yeojin; Jo, Minsang; Park, Sanghyuk; Kim, Sookyung; Yang, Donghyo; Rhee, Kangin; An, Eung-Mo; Sohn, Jeongsoo; Kwon, Kyungjung

2016-08-05

As the production and consumption of lithium ion batteries (LIBs) increase, the recycling of spent LIBs appears inevitable from an environmental, economic and health viewpoint. The leaching behavior of Ni, Mn, Co, Al and Cu from treated cathode active materials, which are separated from a commercial LIB pack in hybrid electric vehicles, is investigated with ammoniacal leaching agents based on ammonia, ammonium carbonate and ammonium sulfite. Ammonium sulfite as a reductant is necessary to enhance leaching kinetics particularly in the ammoniacal leaching of Ni and Co. Ammonium carbonate can act as a pH buffer so that the pH of leaching solution changes little during leaching. Co and Cu can be fully leached out whereas Mn and Al are hardly leached and Ni shows a moderate leaching efficiency. It is confirmed that the cathode active materials are a composite of LiMn2O4, LiCoxMnyNizO2, Al2O3 and C while the leach residue is composed of LiNixMnyCozO2, LiMn2O4, Al2O3, MnCO3 and Mn oxides. Co recovery via the ammoniacal leaching is believed to gain a competitive edge on convenitonal acid leaching both by reducing the sodium hydroxide expense for increasing the pH of leaching solution and by removing the separation steps of Mn and Al. Copyright © 2016 Elsevier B.V. All rights reserved.

Thermal treatment and leaching of biochar alleviates plant growth inhibition from mobile organic compounds

PubMed Central

Sackett, Tara E.; Thomas, Sean C.

2016-01-01

Recent meta-analyses of plant responses to biochar boast positive average effects of between 10 and 40%. Plant responses, however, vary greatly across systems, and null or negative biochar effects are increasingly reported. The mechanisms responsible for such responses remain unclear. In a glasshouse experiment we tested the effects of three forestry residue wood biochars, applied at five dosages (0, 5, 10, 20, and 50 t/ha) to a temperate forest drystic cambisol as direct surface applications and as complete soil mixes on the herbaceous pioneers Lolium multiflorum and Trifolium repens. Null and negative effects of biochar on growth were found in most cases. One potential cause for null and negative plant responses to biochar is plant exposure to mobile compounds produced during pyrolysis that leach or evolve following additions of biochars to soil. In a second glasshouse experiment we examined the effects of simple leaching and heating techniques to ameliorate potentially phytotoxic effects of volatile and leachable compounds released from biochar. We used Solid Phase Microextraction (SPME)–gas chromatography–mass spectrometry (GC-MS) to qualitatively describe organic compounds in both biochar (through headspace extraction), and in the water leachates (through direct injection). Convection heating and water leaching of biochar prior to application alleviated growth inhibition. Additionally, growth was inhibited when filtrate from water-leached biochar was applied following germination. SPME-GC-MS detected primarily short-chained carboxylic acids and phenolics in both the leachates and solid chars, with relatively high concentrations of several known phytotoxic compounds including acetic acid, butyric acid, 2,4-di-tert-butylphenol and benzoic acid. We speculate that variable plant responses to phytotoxic organic compounds leached from biochars may largely explain negative plant growth responses and also account for strongly species-specific patterns of plant responses to biochar amendments in short-term experiments. PMID:27635349

Semi-dynamic leaching tests of nickel containing wastes stabilized/solidified with magnesium potassium phosphate cements.

PubMed

Torras, Josep; Buj, Irene; Rovira, Miquel; de Pablo, Joan

2011-02-28

Herein is presented a study on the long-term leaching behaviour of nickel containing wastes stabilized/solidified with magnesium potassium phosphate cements. Two different semi-dynamic leaching tests were carried out on monolithic materials: ANS 16.1 test with liquid-to-solid ratio (L/S) of 10 dm(3) kg(-1) and increasing renewal times, and ASTM C1308 test with liquid-to-solid ratio (L/S) of 100 dm(3) kg(-1) and constant renewal time of 1 day. ASTM C1308 provides a lower degree of saturation of the leachant with respect to the leached material. The effectiveness of magnesium potassium phosphate cements for the inertization of nickel was proved. XRD analyses showed the presence of bobierrite on the monolith's surface after the leaching test, which had not been detected prior to the leaching test. In addition, the calculated cumulative release of the main components of the stabilization matrix (Mg(2+), total P and K(+)) was represented versus time in logarithmic scale and it was determined if the leaching mechanism corresponds to diffusion. Potassium is released by diffusion, while total phosphorous and magnesium show dissolution. Magnesium release in ANS 16.1 is slowed down because of saturation of the leachant. Experimental results demonstrate the importance of L/S ratio and renewal times in semi-dynamic leaching tests. Copyright © 2010 Elsevier B.V. All rights reserved.

Comparative evaluation of short-term leach tests for heavy metal release from mineral processing waste

USGS Publications Warehouse

Al-Abed, S. R.; Hageman, P.L.; Jegadeesan, G.; Madhavan, N.; Allen, D.

2006-01-01

Evaluation of metal leaching using a single leach test such as the Toxicity Characteristic Leaching Procedure (TCLP) is often questionable. The pH, redox potential (Eh), particle size and contact time are critical variables in controlling metal stability, not accounted for in the TCLP. This paper compares the leaching behavior of metals in mineral processing waste via short-term extraction tests such as TCLP, Field Leach Test (FLT) used by USGS and deionized water extraction tests. Variation in the extracted amounts was attributed to the use of different particle sizes, extraction fluid and contact time. In the controlled pH experiments, maximum metal extraction was obtained at acidic pH for cationic heavy metals such as Cu, Pb and Zn, while desorption of Se from the waste resulted in high extract concentrations in the alkaline region. Precipitation of iron, caused by a pH increase, probably resulted in co-precipitation and immobilization of Cu, Pb and Zn in the alkaline pH region. A sequential extraction procedure was performed on the original waste and the solid residue from the Eh-pH experiments to determine the chemical speciation and distribution of the heavy metals. In the as-received waste, Cu existed predominantly in water soluble or sulfidic phases, with no binding to carbonates or iron oxides. Similar characteristics were observed for Pb and Zn, while Se existed mostly associated with iron oxides or sulfides. Adsorption/co-precipitation of Cu, Se and Pb on precipitated iron hydroxides was observed in the experimental solid residues, resulting in metal immobilization above pH 7.

Nitrate Leaching from Winter Cereal Cover Crops Using Undisturbed Soil-Column Lysimeters.

PubMed

Meisinger, John J; Ricigliano, Kristin A

2017-05-01

Cover crops are important management practices for reducing nitrogen (N) leaching, especially in the Chesapeake Bay watershed, which is under total maximum daily load (TMDL) restraints. Winter cereals are common cool-season crops in the Bay watershed, but studies have not directly compared nitrate-N (NO-N) leaching losses from these species. A 3-yr cover crop lysimeter study was conducted in Beltsville, MD, to directly compare NO-N leaching from a commonly grown cultivar of barley ( L.), rye ( L.), and wheat ( L.), along with a no-cover control, using eight tension-drained undisturbed soil column lysimeters in a completely randomized design with two replicates. The lysimeters were configured to exclude runoff and to estimate NO-N leaching and flow-weighted NO-N concentration (FWNC). The temporal pattern of NO-N leaching showed a consistent highly significant ( < 0.001) effect of lower NO-N leaching with cover crops compared with no cover but showed only small and periodically significant ( < 0.05) effects among the cultivars of barley, rye, and wheat covers. Nitrate-N leaching was more affected by the quantity of establishment-season (mid-October to mid-December) precipitation than by cover crop species. For example, compared with no cover, winter cereal covers reduced NO-N leaching 95% in a dry year and 50% in wet years, with corresponding reductions in FWNC of 92 and 43%, respectively. These results are important for scientists, nutrient managers, and policymakers because they directly compare NO-N leaching from winter cereal covers and expand knowledge for developing management practices for winter cereals that can improve water quality and increase N efficiency in cropping systems. Copyright © by the American Society of Agronomy, Crop Science Society of America, and Soil Science Society of America, Inc.

Ionic liquids for metal extraction from chalcopyrite: solid, liquid and gas phase studies.

PubMed

Kuzmina, O; Symianakis, E; Godfrey, D; Albrecht, T; Welton, T

2017-08-16

We studied leaching of Cu and Fe from naturally occurring chalcopyrite ore using aqueous solutions of ionic liquids (ILs) based on imidazolium and ethylammonium cations and hydrogensulfate, nitrate, acetate or dicyanamide anions. Liquid, solid and gas phases of the leaching systems were characterised. We have shown that nonoxidative leaching is greatly dependant not only on temperature and pH, but on the anion species of the IL. Solutions of 1-butylimidazolium hydrogen sulfate exhibited the best leaching performance among hydrogen sulphate ILs. We have suggested that the formation of an oxide layer in some ILs may be responsible for a reduced leaching ability. The analysis of the gas phase showed the production of CO 2 and CS 2 in all leached samples. Our results suggested that the CS 2 produced upon leaching could be responsible for decreasing the sulfur, but not oxide, layer on the surface of chalcopyrite samples and therefore more efficient leaching. This is the first study, to our knowledge, to provide a systematic comparison of the leaching performance of ILs composed of different anions and cations and without added oxidants.

Impact of wheat straw biochar addition to soil on the sorption, leaching, dissipation of the herbicide (4-chloro-2-methylphenoxy)acetic acid and the growth of sunflower (Helianthus annuus L.).

PubMed

Tatarková, Veronika; Hiller, Edgar; Vaculík, Marek

2013-06-01

Biochar addition to agricultural soils might increase the sorption of herbicides, and therefore, affect other sorption-related processes such as leaching, dissipation and toxicity for plants. In this study, the impact of wheat straw biochar on the sorption, leaching and dissipation in a soil, and toxicity for sunflower of (4-chloro-2-methylphenoxy)acetic acid (MCPA), a commonly used ionizable herbicide, was investigated. The results showed that MCPA sorption by biochar and biochar-amended soil (1.0wt% biochar) was 82 and 2.53 times higher than that by the non-amended soil, respectively. However, desorption of MCPA from biochar-amended soil was only 1.17 times lower than its desorption in non-amended soil. Biochar addition to soil reduced both MCPA leaching and dissipation. About 35% of the applied MCPA was transported through biochar-amended soil, while up to 56% was recovered in the leachates transported through non-amended soil. The half-life value of MCPA increased from 5.2d in non-amended soil to 21.5 d in biochar-amended soil. Pot experiments with sunflower (Helianthus annuus L.) grown in MCPA-free, but biochar-amended soil showed no positive effect of biochar on the growth of sunflower in comparison to the non-amended soil. However, biochar itself significantly reduced the content of photosynthetic pigments (chlorophyll a, b) in sunflower. There was no significant difference in the phytotoxic effects of MCPA on sunflowers between the biochar-amended soil and the non-amended soil. Furthermore, MCPA had no effect on the photosynthetic pigment contents in sunflower. Copyright © 2013 Elsevier Inc. All rights reserved.

Earthworm Comet Assay for Assessing the Risk of Weathered Petroleum Hydrocarbon Contaminated Soils: Need to Look Further than Target Contaminants.

PubMed

Ramadass, Kavitha; Palanisami, Thavamani; Smith, Euan; Mayilswami, Srinithi; Megharaj, Mallavarapu; Naidu, Ravi

2016-11-01

Earthworm toxicity assays contribute to ecological risk assessment and consequently standard toxicological endpoints, such as mortality and reproduction, are regularly estimated. These endpoints are not enough to better understand the mechanism of toxic pollutants. We employed an additional endpoint in the earthworm Eisenia andrei to estimate the pollutant-induced stress. In this study, comet assay was used as an additional endpoint to evaluate the genotoxicity of weathered hydrocarbon contaminated soils containing 520 to 1450 mg hydrocarbons kg -1 soil. Results showed that significantly higher DNA damage levels (two to sixfold higher) in earthworms exposed to hydrocarbon impacted soils. Interestingly, hydrocarbons levels in the tested soils were well below site-specific screening guideline values. In order to explore the reasons for observed toxicity, the contaminated soils were leached with rainwater and subjected to earthworm tests, including the comet assay, which showed no DNA damage. Soluble hydrocarbon fractions were not found originally in the soils and hence no hydrocarbons leached out during soil leaching. The soil leachate's Electrical Conductivity (EC) decreased from an average of 1665 ± 147 to 204 ± 20 µS cm -1 . Decreased EC is due to the loss of sodium, magnesium, calcium, and sulphate. The leachate experiment demonstrated that elevated salinity might cause the toxicity and not the weathered hydrocarbons. Soil leaching removed the toxicity, which is substantiated by the comet assay and soil leachate analysis data. The implication is that earthworm comet assay can be included in future eco (geno) toxicology studies to assess accurately the risk of contaminated soils.

Inorganic Nitrogen Leaching from Organic and Conventional Rice Production on a Newly Claimed Calciustoll in Central Asia

PubMed Central

Meng, Fanqiao; Olesen, Jørgen E.; Sun, Xiangping; Wu, Wenliang

2014-01-01

Characterizing the dynamics of nitrogen (N) leaching from organic and conventional paddy fields is necessary to optimize fertilization and to evaluate the impact of these contrasting farming systems on water bodies. We assessed N leaching in organic versus conventional rice production systems of the Ili River Valley, a representative aquatic ecosystem of Central Asia. The N leaching and overall performance of these systems were measured during 2009, using a randomized block experiment with five treatments. PVC pipes were installed at soil depths of 50 and 180 cm to collect percolation water from flooded organic and conventional paddies, and inorganic N (NH4-N+NO3-N) was analyzed. Two high-concentration peaks of NH4-N were observed in all treatments: one during early tillering and a second during flowering. A third peak at the mid-tillering stage was observed only under conventional fertilization. NO3-N concentrations were highest at transplant and then declined until harvest. At the 50 cm soil depth, NO3-N concentration was 21–42% higher than NH4-N in percolation water from organic paddies, while NH4-N and NO3-N concentrations were similar for the conventional and control treatments. At the depth of 180 cm, NH4-N and NO3-N were the predominant inorganic N for organic and conventional paddies, respectively. Inorganic N concentrations decreased with soil depth, but this attenuation was more marked in organic than in conventional paddies. Conventional paddies leached a higher percentage of applied N (0.78%) than did organic treatments (0.32–0.60%), but the two farming systems leached a similar amount of inorganic N per unit yield (0.21–0.34 kg N Mg−1 rice grains). Conventional production showed higher N utilization efficiency compared to fertilized organic treatments. These results suggest that organic rice production in the Ili River Valley is unlikely to reduce inorganic N leaching, if high crop yields similar to conventional rice production are to be maintained. PMID:24858826

Analysis of SPR salt cavern remedial leach program 2013.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Weber, Paula D.; Gutierrez, Karen A.; Lord, David L.

The storage caverns of the US Strategic Petroleum Reserve (SPR) exhibit creep behavior resulting in reduction of storage capacity over time. Maintenance of oil storage capacity requires periodic controlled leaching named remedial leach. The 30 MMB sale in summer 2011 provided space available to facilitate leaching operations. The objective of this report is to present the results and analyses of remedial leach activity at the SPR following the 2011 sale until mid-January 2013. This report focuses on caverns BH101, BH104, WH105 and WH106. Three of the four hanging strings were damaged resulting in deviations from normal leach patterns; however, themore » deviations did not affect the immediate geomechanical stability of the caverns. Significant leaching occurred in the toes of the caverns likely decreasing the number of available drawdowns until P/D ratio criteria are met. SANSMIC shows good agreement with sonar data and reasonably predicted the location and size of the enhanced leaching region resulting from string breakage.« less

Tradeoffs between Maize Silage Yield and Nitrate Leaching in a Mediterranean Nitrate-Vulnerable Zone under Current and Projected Climate Scenarios

PubMed Central

Basso, Bruno; Giola, Pietro; Dumont, Benjamin; Migliorati, Massimiliano De Antoni; Cammarano, Davide; Pruneddu, Giovanni; Giunta, Francesco

2016-01-01

Future climatic changes may have profound impacts on cropping systems and affect the agronomic and environmental sustainability of current N management practices. The objectives of this work were to i) evaluate the ability of the SALUS crop model to reproduce experimental crop yield and soil nitrate dynamics results under different N fertilizer treatments in a farmer’s field, ii) use the SALUS model to estimate the impacts of different N fertilizer treatments on NO3- leaching under future climate scenarios generated by twenty nine different global circulation models, and iii) identify the management system that best minimizes NO3- leaching and maximizes yield under projected future climate conditions. A field experiment (maize-triticale rotation) was conducted in a nitrate vulnerable zone on the west coast of Sardinia, Italy to evaluate N management strategies that include urea fertilization (NMIN), conventional fertilization with dairy slurry and urea (CONV), and no fertilization (N0). An ensemble of 29 global circulation models (GCM) was used to simulate different climate scenarios for two Representative Circulation Pathways (RCP6.0 and RCP8.5) and evaluate potential nitrate leaching and biomass production in this region over the next 50 years. Data collected from two growing seasons showed that the SALUS model adequately simulated both nitrate leaching and crop yield, with a relative error that ranged between 0.4% and 13%. Nitrate losses under RCP8.5 were lower than under RCP6.0 only for NMIN. Accordingly, levels of plant N uptake, N use efficiency and biomass production were higher under RCP8.5 than RCP6.0. Simulations under both RCP scenarios indicated that the NMIN treatment demonstrated both the highest biomass production and NO3- losses. The newly proposed best management practice (BMP), developed from crop N uptake data, was identified as the optimal N fertilizer management practice since it minimized NO3- leaching and maximized biomass production over the long term. PMID:26784113

A Tier-I leaching risk assessment of three anticoagulant compounds in the forested areas of Hawai'i.

PubMed

D'Alessio, Matteo; Wang, Tiejun; Swift, Catherine E; Shanmungam, Mohana Sundaram; Ray, Chittaranjan

2018-07-15

The anticoagulant rodenticides brodifacoum, chlorophacinone, and diphacinone have been proposed for broadcast application in some forested areas in Hawai'i to protect rare and endangered native bird species from introduced mice and rats. Groundwater resources in Hawai'i are prone to contamination due to the intrinsic aquifer vulnerability to leaching from the land surface. Because of the hydrogeologic complexity, Hawai'i uses a Tier-I leaching assessment tool, CLERS, to make registration decisions for new or existing chemicals. The CLERS tool uses soil and pesticide properties as well as water recharge through the soil profile in a GIS framework to estimate mass attenuation of the chemicals at a given depth and compares against this attenuation factor against those of a known leacher and a non-leacher. Disturbed soil samples were collected across the state of Hawai'i, including the islands of Hawai'i, Kaho'olawe, Kaua'i, Lana'i, Maui, Moloka'i, and O'ahu, with two sampling locations per island, except for Kaua'i which had three. As only limited information on chemical properties of these anticoagulants in soils is available, laboratory experiments were performed to determine the sorption capacity (K d ) and the degradation rate (T 1/2 ) of brodifacoum, chlorophacinone, and diphacinone to construct a proper chemical database. Depending on the soil type, T 1/2 values ranged between 37 and 248days for diphacinone, between 39 and 1000days for chlorophacinone, and between 72 and 462days for brodifacoum. These data were used in the CLERS tool to estimate leaching risks for these chemicals primarily in forested areas of the state where the chemicals are likely to be applied. The results from the CLERS tool indicate low risks of leaching of these three compounds into aquifers in five out of six major Hawaiian Islands. Diphacinone showed medium risk of leaching in a few remote areas in Maui. Copyright © 2018 Elsevier B.V. All rights reserved.

Leaching of boron, arsenic and selenium from sedimentary rocks: II. pH dependence, speciation and mechanisms of release.

PubMed

Tabelin, Carlito Baltazar; Hashimoto, Ayaka; Igarashi, Toshifumi; Yoneda, Tetsuro

2014-03-01

Sedimentary rocks excavated in Japan from road- and railway-tunnel projects contain relatively low concentrations of hazardous trace elements like boron (B), arsenic (As) and selenium (Se). However, these seemingly harmless waste rocks often produced leachates with concentrations of hazardous trace elements that exceeded the environmental standards. In this study, the leaching behaviors and release mechanisms of B, As and Se were evaluated using batch leaching experiments, sequential extraction and geochemical modeling calculations. The results showed that B was mostly partitioned with the residual/crystalline phase that is relatively stable under normal environmental conditions. In contrast, the majority of As and Se were associated with the exchangeable and organics/sulfides phases that are unstable under oxidizing conditions. Dissolution of water-soluble phases controlled the leaching of B, As and Se from these rocks in the short term, but pyrite oxidation, calcite dissolution and adsorption/desorption reactions became more important in the long term. The mobilities of these trace elements were also strongly influenced by the pH of the rock-water system. Although the leaching of Se only increased in the acidic region, those of B and As were enhanced under both acidic and alkaline conditions. Under strongly acidic conditions, the primarily release mechanism of B, As and Se was the dissolution of mineral phases that incorporated and/or adsorbed these elements. Lower concentrations of these trace elements in the circumneutral pH range could be attributed to their strong adsorption onto minerals like Al-/Fe-oxyhydroxides and clays, which are inherently present and/or precipitated in the rock-water system. The leaching of As and B increased under strongly alkaline conditions because of enhanced desorption and pyrite oxidation while that of Se remained minimal due to its adsorption onto Fe-oxyhydroxides and co-precipitation with calcite. Copyright © 2013 Elsevier B.V. All rights reserved.

Utilizing on-farm best management practices: Managing Nitrate Leaching Using Evapotranspiration Based Irrigation Methods

NASA Astrophysics Data System (ADS)

Zaragosa, I.; Melton, F. S.; Dexter, J.; Post, K.; Haffa, A.; Kortman, S.; Spellenberg, R.; Cahn, M.

2017-12-01

In efforts to provide tools to allow farmers to optimize and quantify water usage and fertilizer applications, University of California Cooperative Extension (UCCE) developed the CropManage irrigation and nitrogen scheduling tool that provides real time evapotranspiration (ETc) based irrigation recommendations and fertilizer recommendations on a per field basis. CropManage incorporates satellite based estimates of fractional cover from web data services from the Satellite Irrigation Management Information Support (SIMS) system developed by NASA Ames Research Center in collaboration with California State University Monterey Bay (CSUMB). In this study, we conducted field trials to quantify the benefits of using these tools to support best management practices (BMPs) for irrigation and nutrient management in strawberries and lettuce in the Salinas Valley, California. We applied two different irrigation treatments based on full replacement (100%) of crop evapotranspiration (ETc), and irrigation at 130% of ETc replacement to approximate irrigation under business as usual irrigation management. Both field studies used a randomized block design with four replicates each. We used CropManage to calculate the 100% and 130% ETc replacement requirements prior to each irrigation event. We collected drainage volume and samples and analyzed them for 8500 to nitrate as (NO3-) concentrations. Experimental results for both strawberries and lettuce showed a significant decrease in the percentage of applied nitrogen leached for the 100% ETc replacement treatment against the 130% ETc replacement treatment. For strawberries, we observed that 24% of applied nitrogen was leached under the 100% ETc replacement treatment, versus 51% of applied nitrogen that was leached under the 130% ETc replacement treatment. For lettuce, we observe that 2% of the applied nitrogen leached bellow the soil profile, versus 6% of the applied nitrogen for the 130%ETc replacement treatment. In both experiments, we observed significant differences in the amount of leached nitrogen, both as in terms of total volume and as a percent of nitrogen applied, with no significant differences in yield.

Evaluation of metal mobility from copper mine tailings in northern Chile.

PubMed

Lam, Elizabeth J; Gálvez, M E; Cánovas, M; Montofré, I L; Rivero, D; Faz, A

2016-06-01

This work shows the results obtained on a copper mine tailing in the Antofagasta Region, Chile. The tailing was classified as saline-sodic with high concentrations of metals, especially Cu and Fe, with pH 8.4. Our objectives were to (1) compare the physicochemical properties of the tailing with surrounding soils of the mine under study, and (2) evaluate the effect of two amendments (CaCO3 and compost) and their mixtures on Cu(2+), Mn, Fe, Zn, Mg(2+), and K(+) and Ca(2+), SO4 (2-), NO3 (-), and PO4 (3-) leaching. The data obtained were submitted to variance and covariance analysis. The results from the comparison between both substrates showed that in general, the tailing presented greater content of metals. Regarding tailing leaching, pH, electrical conductivity (EC), and concentration of the elements of interest were measured. The statistical analysis showed that Cu(2+) leaching and immobilization of Fe occurred to the greatest extent with compost. The EC decreased throughout the experiment with irrigation and increased upon treatment with compost. The major interactions found among the chemical parameters were (1) tailings without treatment, Cu(2+)/Fe and NO3 (-)/SO4 (2-); (2) tailings treated with CaCO3, Cu(2+)/K(+); (3) tailings treated with compost, NO3 (-)/SO4 (-2) and EC/Cu(2+); and (4) tailings treated with both amendments, EC/Fe and Cu(2+)/Fe. The ANOVA showed that the number of irrigations and the amendments statistically significantly affected the copper mobility and the organic amendment significantly influenced the iron mobility.

The pH-dependent leaching behavior of slags from various stages of a copper smelting process: Environmental implications.

PubMed

Jarošíková, Alice; Ettler, Vojtěch; Mihaljevič, Martin; Kříbek, Bohdan; Mapani, Ben

2017-02-01

The leaching behaviors of primary copper (Cu) slags originating from Ausmelt, reverbatory, and converter furnaces operating under a single technological process were compared to a residual slag tailing obtained by slag re-processing via flotation and metal recovery. The EN 12457-2 leaching test, used for assessment of the hazardous properties, was followed by the CEN/TS 14997 pH-static leaching test (pH range 3-12). Both leaching experiments were coupled with a mineralogical investigation of the primary and secondary phases as well as geochemical modeling. Metals (Cd, Cu, Pb, Zn) exhibit the highest leaching at low pH. Under acidic conditions (pH 3-6), Ausmelt slag and slag tailing exhibited higher metal leaching compared to other slag types. Very low leaching of metals (far below EU limits for non-hazardous waste) was observed at natural pH (7.9-9.0) for all the studied slag samples. In contrast, relatively high leaching of As was observed over the entire pH range, especially for Ausmelt slag (exceeding the EU limit for hazardous waste by 1.7×). However, geochemical modeling and scanning electron microscopy indicated that formation of stable Ca-Cu-Pb arsenates and the binding of As to newly formed Fe (oxyhydr)oxides play an important role in efficient As immobilization at the slag-water interface. In contrast, no controls were predicted for Sb, whose leaching was almost pH-independent. Nevertheless Sb leached concentrations at natural pH were below EU limit for hazardous waste. Re-processing of primary Cu slags for metal recovery, and subsequent co-disposal of the resulting slag tailing with dolomite-rich mine tailing and local laterite is suitable for stabilizing the remaining contaminants (except Sb) and limiting their leaching into the environment. Copyright © 2016 Elsevier Ltd. All rights reserved.

Arsenic Speciation of Solvent-Extracted Leachate from New and Weathered CCA-Treated Wood

PubMed Central

KHAN, BERNINE I.; SOLO - GABRIELE, HELENA M.; DUBEY, BRAJESH K.; TOWNSEND, TIMOTHY G.; CAI, YONG

2009-01-01

For the past 60 yr, chromate-copper-arsenate (CCA) has been used to pressure-treat millions of cubic meters of wood in the United States for the construction of many outdoor structures. Leaching of arsenic from these structures is a possible health concern as there exists the potential for soil and groundwater contamination. While previous studies have focused on total arsenic concentrations leaching from CCA-treated wood, information pertaining to the speciation of arsenic leached is limited. Since arsenic toxicity is dependent upon speciation, the objective of this study was to identify and quantify arsenic species leaching from new and weathered CCA-treated wood and CCA-treated wood ash. Solvent-extraction experiments were carried out by subjecting the treated wood and the ash to solvents of varying pH values, solvents defined in the EPA’s Synthetic Precipitation Leaching Procedure (SPLP) and Toxicity Characteristic Leaching Procedure (TCLP), rainwater, deionized water, and seawater. The generated leachates were analyzed for inorganic As(III) and As(V) and the organoarsenic species, monomethylarsonic acid (MMAA) and dimethylarsinic acid (DMAA), using high-performance liquid chromatography followed by hydride generation and atomic fluorescence spectrometry (HPLC–HG-AFS). Only the inorganic species were detected in any of the wood leachates; no organoarsenic species were found. Inorganic As(V) was the major detectable species leaching from both new and weathered wood. The weathered wood leached relatively more overall arsenic and was attributed to increased inorganic As(III) leaching. The greater presence of As(III) in the weathered wood samples as compared to the new wood samples may be due to natural chemical and biological transformations during the weathering process. CCA-treated wood ash leached more arsenic than unburned wood using the SPLP and TCLP, and ash samples leached more inorganic As(III) than the unburned counterparts. Increased leaching was due to higher concentrations of arsenic within the ash and to the conversion of some As(V) to As(III) during combustion. PMID:15461159

The complicated substrates enhance the microbial diversity and zinc leaching efficiency in sphalerite bioleaching system.

PubMed

Xiao, Yunhua; Xu, YongDong; Dong, Weiling; Liang, Yili; Fan, Fenliang; Zhang, Xiaoxia; Zhang, Xian; Niu, Jiaojiao; Ma, Liyuan; She, Siyuan; He, Zhili; Liu, Xueduan; Yin, Huaqun

2015-12-01

This study used an artificial enrichment microbial consortium to examine the effects of different substrate conditions on microbial diversity, composition, and function (e.g., zinc leaching efficiency) through adding pyrite (SP group), chalcopyrite (SC group), or both (SPC group) in sphalerite bioleaching systems. 16S rRNA gene sequencing analysis showed that microbial community structures and compositions dramatically changed with additions of pyrite or chalcopyrite during the sphalerite bioleaching process. Shannon diversity index showed a significantly increase in the SP (1.460), SC (1.476), and SPC (1.341) groups compared with control (sphalerite group, 0.624) on day 30, meanwhile, zinc leaching efficiencies were enhanced by about 13.4, 2.9, and 13.2%, respectively. Also, additions of pyrite or chalcopyrite could increase electric potential (ORP) and the concentrations of Fe3+ and H+, which were the main factors shaping microbial community structures by Mantel test analysis. Linear regression analysis showed that ORP, Fe3+ concentration, and pH were significantly correlated to zinc leaching efficiency and microbial diversity. In addition, we found that leaching efficiency showed a positive and significant relationship with microbial diversity. In conclusion, our results showed that the complicated substrates could significantly enhance microbial diversity and activity of function.

Titanium leaching from red mud by diluted sulfuric acid at atmospheric pressure.

PubMed

Agatzini-Leonardou, S; Oustadakis, P; Tsakiridis, P E; Markopoulos, Ch

2008-09-15

Laboratory-scale research has focused on the recovery of titanium from red mud, which is obtained from bauxite during the Bayer process for alumina production. The leaching process is based on the extraction of this element with diluted sulfuric acid from red mud under atmospheric conditions and without using any preliminary treatment. Statistical design and analysis of experiments were used, in order to determine the main effects and interactions of the leaching process factors, which were: acid normality, temperature and solid to liquid ratio. The titanium recovery efficiency on the basis of red mud weight reached 64.5%. The characterization of the initial red mud, as well as this of the leached residues was carried out by X-ray diffraction, TG-DTA and scanning electron microscopy.

Determination of the Optimum Conditions for Leaching of Zinc Cathode Melting Furnace Slag in Ammonium Chloride Media

NASA Astrophysics Data System (ADS)

Behnajady, Bahram; Babaeidehkordi, Amin; Moghaddam, Javad

2014-04-01

This research is part of a continuing effort to leach zinc from zinc cathode melting furnace slags (ZCMFSs) to produce zinc oxide. The slag with an assay of 68.05 pct Zn was used in ammonium chloride leaching for zinc extraction. In this paper, the effects of influential factors on extraction efficiency of Zn from a ZCMFS were investigated. The Taguchi's method based on orthogonal array (OA) design has been used to arrange the experimental runs in order to maximize zinc extraction from a slag. The softwares named Excel and Design-Expert 7 have been used to design experiments and subsequent analysis. OA L 25 (55) consisting of five parameters, each with five levels, was employed to evaluate the effects of reaction time ( t = 10, 30, 50, 70, 90 minutes), reaction temperature [ T = 313, 323, 333, 343, 353 (40, 50, 60, 70, 80) K (°C)], pulp density ( S/ L = 20, 40, 60, 80, 100 g/L), stirring speed ( R = 300, 400, 500, 600, 700 rpm), and ammonium chloride concentration ( C = 10, 15, 20, 25, 30 pctwt), on zinc extraction percent. Statistical analysis, ANOVA, was also employed to determine the relationship between experimental conditions and yield levels. The results showed that the significant parameters affecting leaching of slag were ammonium chloride concentration and pulp density, and increasing pulp density reduced leaching efficiency of zinc. However, increasing ammonium chloride concentration promoted the extraction of zinc. The optimum conditions for this study were found to be t 4: 70 minutes, T 5: 353 K (80 °C), ( S/ L)2: 40 g/L, R 3: 500 rpm, and C 4: 25 pctwt. Under these conditions, the dissolution percentage of Zn in ammonium chloride media was 94.61 pct.

Kinetic and thermodynamic study of the thorium phosphate-diphosphate dissolution

NASA Astrophysics Data System (ADS)

Thomas, A. C.; Dacheux, N.; Le Coustumer, P.; Brandel, V.; Genet, M.

2000-10-01

The dissolution of the thorium phosphate-diphosphate (TPD), which was proposed for the actinides immobilization, was systematically studied as a function of several parameters such as surface, leaching flow, temperature, acidity or basicity of the leachate and phosphate concentration. The dependence of the normalized leaching rate on the temperature leads to an activation energy equal to about 42±3 kJ mol -1. The normalized leaching rate is slightly increased when increasing the acidity or the basicity of the leachate. The partial orders related to proton and hydroxide ions are equal to 0.31-0.35 and 0.35, respectively. For the pH range studied, i.e., 1

Flow-Through Leaching of Marine Barite: New Insights on its Composition and Diagenesis

NASA Astrophysics Data System (ADS)

Hsieh, C.; Torres, M. E.; Ungerer, A.; Klinkhammer, G. P.

2007-12-01

The distribution of stable mineral barite (BaSO4) in marine sediments has long been studied as a proxy for paleoproductivity. It is important to investigate the variation in Sr/Ba ratios of crystal barite, as it has a great influence on barite solubility and its early diagenetic processes. In addition, the role of alternative barium carriers to the sediments (e.g. aluminum silicates and oxyhydroxides) and their contributions to overall barium budget and burial efficiency need to be resolved. The techniques currently used to describe and quantify barium phases are all based on batch leaching techniques that define barium phases operationally, not chemically. Because during batch analyses each phase is characterized by a single-point measurement, variations due to phase heterogeneities cannot be resolved; nor can the results of these experiments be related in any systematic way to what happens in nature. To overcome this problem, we are developing a flow-through method that makes use of automated chromatographic techniques, which allows complete monitoring of the dissolution of barite samples with time-resolved analysis (TRA) as each phase is sequentially leached using different reagents. We have analyzed a barite sample recovered from seeps along the San Clemente escarpment, and show that we can attain complete dissolution of the sample (>85%) in 2 hours, using DTPA at 80°C. Approximately 100 μg of barite are first leached with distilled water (pH 5) for 30 minutes. During this step ~2% of the barite is removed. This highly soluble phase has Sr/Ba ratios that range from 30 to 120 mmol/mol. Acid leaching of the samples with 10 mM HNO3 removes an additional 4~8% of the barite, and this phase has Sr/Ba ratios ranging from 13 to 35 mmol/mol. Higher acid concentration (100 mM HNO3) dissolves up to 40% of the barite. These results are consistent with electron microprobe data that show clear oscillatory zoning of the (Ba,Sr)SO4. Unlike the barite sample, sediment samples collected at the base of the escarpment did not show a Ba release in the water leach. We might speculate that the highly susceptible Sr-rich barium phase present in the barite sample, dissolved during transport from a seep site leaving a barite with a lower Sr/Ba ratio, as found in the sediment samples. Our analytical approach has the potential to further address a variety of outstanding questions on the complex geochemical cycle of barium and its applications to climate change, upper ocean fertility and ocean circulation through time.

Presence and leaching of bisphenol a (BPA) from dental materials

PubMed Central

Becher, Rune; Wellendorf, Hanne; Sakhi, Amrit Kaur; Samuelsen, Jan Tore; Thomsen, Cathrine; Bølling, Anette Kocbach; Kopperud, Hilde Molvig

2018-01-01

Abstract BPA has been reported to leach from some resin based dental restorative materials and materials used for orthodontic treatment. To confirm and update previous findings, especially in light of the new temporary lower threshold value for tolerable daily BPA intake, we have investigated the leaching of BPA from 4 composite filling materials, 3 sealants and 2 orthodontic bonding materials. The materials were either uncured and dissolved in methanol or cured. The cured materials were kept in deionized water for 24 hours or 2 weeks. Samples were subsequently analyzed by ultra-performance liquid chromatography coupled to mass spectrometry (UPLC-MS-MS). The composite filling material Tetric EvoFlow® and the fissure sealant DELTON® showed significantly higher levels of BPA leaching compared to control samples for all test conditions (uncured, 24 h leaching and 2 weeks leaching). There were no significant differences in amount of leached BPA for any of the tested materials after 24 hours compared to 2 weeks. These results show that BPA is still released from some dental materials despite the general concern about potential adverse effects of BPA. However, the amounts of BPA were relatively low and most likely represent a very small contribution to the total BPA exposure. PMID:29868625

Investigations into Recycling Zinc from Used Metal Oxide Varistors via pH Selective Leaching: Characterization, Leaching, and Residue Analysis

PubMed Central

Gutknecht, Toni; Gustafsson, Anna; Forsgren, Christer; Steenari, Britt-Marie

2015-01-01

Metal oxide varistors (MOVs) are a type of resistor with significantly nonlinear current-voltage characteristics commonly used in power lines to protect against overvoltages. If a proper recycling plan is developed MOVs can be an excellent source of secondary zinc because they contain over 90 weight percent zinc oxide. The oxides of antimony, bismuth, and to a lesser degree cobalt, manganese, and nickel are also present in varistors. Characterization of the MOV showed that cobalt, nickel, and manganese were not present in the varistor material at concentrations greater than one weight percent. This investigation determined whether a pH selective dissolution (leaching) process can be utilized as a starting point for hydrometallurgical recycling of the zinc in MOVs. This investigation showed it was possible to selectively leach zinc from the MOV without coleaching of bismuth and antimony by selecting a suitable pH, mainly higher than 3 for acids investigated. It was not possible to leach zinc without coleaching of manganese, cobalt, and nickel. It can be concluded from results obtained with the acids used, acetic, hydrochloric, nitric, and sulfuric, that sulfate leaching produced the most desirable results with respect to zinc leaching and it is also used extensively in industrial zinc production. PMID:26421313

Evaluation of heavy metal leaching from coal ash-versus conventional concrete monoliths and debris.

PubMed

Gwenzi, Willis; Mupatsi, Nyarai M

2016-03-01

Application of coal ash in construction materials is constrained by the potential risk of heavy metal leaching. Limited information is available on the comparative heavy metal leaching from coal ash-versus conventional concrete. The current study compared total and leached heavy metal concentrations in unbound coal ash, cement and sand; and investigated the effect of initial leachant pH on heavy metal leaching from coal-ash versus conventional concrete monoliths and their debris. Total Pb, Mn and Zn in coal ash were lower than or similar to that of other materials, while Cu and Fe showed the opposite trend. Leached concentrations of Zn, Pb, Mn, Cu and Fe in unbound coal ash, its concrete and debris were comparable and in some cases even lower than that for conventional concrete. In all cases, leached concentrations accounted for just <1% of the total concentrations. Log-log plots of concentration and cumulative release of Fe versus time based on tank leaching data showed that leaching was dominated by diffusion. Overall, the risk of Zn, Pb, Mn, Cu and Fe leaching from coal ash and its concrete was minimal and comparable to that of conventional concrete, a finding in contrast to widely held public perceptions and earlier results reported in other regions such as India. In the current study the coal ash, and its concrete and debris had highly alkaline pH indicative of high acid neutralizing and pH buffering capacity, which account for the stabilization of Zn, Pb, Mn, Cu and Fe. Based on the low risk of Zn, Pb, Mn, Cu and Fe leaching from the coal ash imply that such coal ash can be incorporated in construction materials such as concrete without adverse impacts on public and environmental health from these constituents. Copyright © 2015 Elsevier Ltd. All rights reserved.

Technospheric Mining of Rare Earth Elements from Bauxite Residue (Red Mud): Process Optimization, Kinetic Investigation, and Microwave Pretreatment.

PubMed

Reid, Sable; Tam, Jason; Yang, Mingfan; Azimi, Gisele

2017-11-10

Some rare earth elements (REEs) are classified under critical materials, i.e., essential in use and subject to supply risk, due to their increasing demand, monopolistic supply, and environmentally unsustainable and expensive mining practices. To tackle the REE supply challenge, new initiatives have been started focusing on their extraction from alternative secondary resources. This study puts the emphasis on technospheric mining of REEs from bauxite residue (red mud) produced by the aluminum industry. Characterization results showed the bauxite residue sample contains about 0.03 wt% REEs. Systematic leaching experiments showed that concentrated HNO 3 is the most effective lixiviant. However, because of the process complexities, H 2 SO 4 was selected as the lixiviant. To further enhance the leaching efficiency, a novel process based on microwave pretreatment was employed. Results indicated that microwave pretreatment creates cracks and pores in the particles, enabling the lixiviant to diffuse further into the particles, bringing more REEs into solution, yielding of 64.2% and 78.7% for Sc and Nd, respectively, which are higher than the maximum obtained when HNO 3 was used. This novel process of "H 2 SO 4 leaching-coupled with-microwave pretreatment" proves to be a promising technique that can help realize the technological potential of REE recovery from secondary resources, particularly bauxite residue.

Leaching of mixtures of biochar and fly ash

DOE Office of Scientific and Technical Information (OSTI.GOV)

Palumbo, Anthony V.; Porat, Iris; Phillips, Jana R.

2009-06-22

Increasing atmospheric levels of greenhouse gases, especially CO2, and their effects on global temperature have led to interest in the possibility of carbon storage in terrestrial environments. Both the residual char from biomass pyrolysis (biochar) and fly ash from coal combustion have the potential to significantly expand terrestrial sequestration options. Both biochar and fly ash also have potentially beneficial effects on soil properties. Fly ash has been shown to increase porosity, water-holding capacity, pH, conductivity, and dissolved SO42-, CO32-, Cl- and basic cations. Adding biochar to soil generally raises pH, increases total nitrogen and total phosphorous, encourages greater root development,more » improves cation exchange capacity and decreases available aluminum. A combination of these benefits likely is responsible for observed increases in yields for crops such as corn and sugarcane. In addition, it has been found that soils with added biochar emit lower amounts of other greenhouse gases (methane and nitrous oxide) than do unamended soils. Biochar and fly ash amendments may be useful in promoting terrestrial carbon sequestration on currently underutilized and degraded lands. For example, about 1% of the US surface lands consist of previously mined lands or highway rights-of-way. Poorly managed lands could count for another 15% of US area. Biochar and fly ash amendments could increase productivity of these lands and increase carbon storage in the soil. Previous results showed minimal leaching of organic carbon and metals from a variety of fly ashes. In the present study, we examined the properties of mixtures of biochar, fly ash, and soil and evaluated the leaching of organic carbon and metals from these mixtures. The carbon sorption experiments showed release of carbon from biochar, rather than sorption, except at the highest concentrations in the Biochar HW sample. Similar results were obtained by others for oxidative leaching of bituminous coal, in which more C was released as dissolved C than was oxidized to CO2 by the oxygen in water. We confirmed that both fly ash and two types of biochar (oak char [OKEB], and hardwood [HW] char) exhibited minimal leaching of heavy metals including Cr, Ni, Zn, Ga, and Ag, and no detectable leaching of Pb or Cd (data not shown) under the conditions tested. The Biochar HW had a slightly higher C/N ratio (334) and pH (7.7) than did the Biochar OKEB (284 and 6.5). There was no toxicity exhibited by the fly ash (not shown) or biochar leachates as measured by the Microtox© assay under the conditions tested. In previous results no toxicity was reported in testing the fly ash samples except for one high-pH sample. The most notable leachate component from both types of biochar, but not the fly ash, was organic carbon with the HW biochar leaching less organic carbon than the OKEB biochar (5.71 ppm vs. 59.3 ppm). Alone (in batch sorption experiments), or in mixtures of 90% soil and 10% biochar (column studies), we noted significant loss of carbon from the biochar into soluble components. However, when we added fly ash to the column experiments (80% soil, 10% fly ash, and 10% biochar) we observed significant decreases in the amounts of C leached (20% for HW, and 47% for OKEB). The results indicate that applying a combination of fly ash and biochar may result in maximizing the amount of carbon sequestration in soil while also increasing beneficial soil properties and fertility. The lower amount of carbon leached from the HW biochar compared to the OKEB biochar is likely due to the more recalcitrant form of the carbon in the HW char, due to its preparation at a higher temperature (600 ºC) than the OKEB biochar (450 ºC). High heat treatment temperatures during biochar preparation increase both the total carbon content of the biochar and the proportion of the carbon that is present in fused aromatic rings resistant to chemical and physical degradation.« less

Separation of Ce and La from Synthetic Chloride Leach Solution of Monazite Sand by Precipitation and Solvent Extraction

NASA Astrophysics Data System (ADS)

Banda, Raju; Jeon, Ho Seok; Lee, Man Seung

2014-12-01

Precipitation and solvent extraction experiments have been performed to recover light rare earths from simulated monazite sand chloride leach solutions. Precipitation conditions were obtained to recover Ce by adding NaClO as an oxidant. Among some cationic extractants (PC 88A, D2EHPA, Cyanex 272, LIX 63), PC 88A showed the best performance to separate La from the resulting chloride solution. Furthermore, the mixture of PC 88A with other solvating (TBP, TOPO) and amine extractants (Alamine 336, Aliquat 336) was tested to increase the separation factor of La from Pr and Nd. The use of mixed extractants greatly enhanced the separation of La from the two other metals. McCabe-Thiele diagrams for the extraction of Pr and Nd with the PC 88A/Alamine 336 mixture were constructed.

Leaching and sorption of neonicotinoid insecticides and fungicides from seed coatings

USGS Publications Warehouse

Smalling, Kelly; Hladik, Michelle; Sanders, Corey; Kuivila, Kathryn

2018-01-01

Seed coatings are a treatment used on a variety of crops to improve production and offer protection against pests and fungal outbreaks. The leaching of the active ingredients associated with the seed coatings and the sorption to soil was evaluated under laboratory conditions using commercially available corn and soybean seeds to study the fate and transport of these pesticides under controlled conditions. The active ingredients (AI) included one neonicotinoid insecticide (thiamethoxam) and five fungicides (azoxystrobin, fludioxonil, metalaxyl, sedaxane thiabendazole). An aqueous leaching experiment was conducted with treated corn and soybean seeds. Leaching potential was a function of solubility and seed type. The leaching of fludioxonil, was dependent on seed type with a shorter time to equilibrium on the corn compared to the soybean seeds. Sorption experiments with the treated seeds and a solution of the AIs were conducted using three different soil types. Sorption behavior was a function of soil organic matter as well as seed type. For most AIs, a negative relationship was observed between the aqueous concentration and the log Koc. Sorption to all soils tested was limited for the hydrophilic pesticides thiamethoxam and metalaxyl. However, partitioning for the more hydrophobic fungicides was dependent on both seed type and soil properties. The mobility of fludioxonil in the sorption experiment varied by seed type indicating that the adjuvants associated with the seed coating could potentially play a role in the environmental fate of fludioxonil. This is the first study to assess, under laboratory conditions, the fate of pesticides associated with seed coatings using commercially available treated seeds. This information can be used to understand how alterations in agricultural practices (e.g., increasing use of seed treatments) can impact the exposure (concentration and duration) and potential effects of these chemicals to aquatic and terrestrial organisms.

Soil-pit Method for Distribution and Leaching Loss of Nitrogen in Winter Wheat’s Soil, Weishan Irrigation District

NASA Astrophysics Data System (ADS)

Zhao, Erni; Xu, Lirong; Wang, Rongzhen

2018-01-01

Unreasonable application of irrigation and fertilizer will cause the waste of water and nitrogen and environmental pollution. In this paper, a series of soil-pit experiments were carried out to study the distribution and leaching loss of nitrogen in winter wheat’s soil. The results showed that NO3 - concentration at 20-80cm depth mainly responded to fertilizer application at the beginning of field experiment, but the amount of irrigation became the dominant factor with the growth of winter wheat. It is noteworthy that the distribution of NO3 - was mainly affected by the amount of fertilizer applied at the depth of 120-160cm in the whole period of growth of winter wheat. The accumulation position of NH4 + was deepened as the amount of irrigation increased, however, the maximum aggregation depth of ammonium nitrogen was no more than 80cm owing to its poor migration. It can be concluded that the influence of irrigation amount on the concentration of NH4 + in soil solution was more obvious than that of fertilizer. Compared with fertilizer, the amount of irrigation played a leading role in the utilization ratio of nitrogen and the yield of winter wheat. In summary, the best water and fertilizer treatment occurred in No.3 soil-pit, which meant that the middle amount of water and fertilizer could get higher wheat yield and less nitrogen leaching losses in the study area.

Mechanism of Phosphorus Removal from Hanford Tank Sludge by Caustic Leaching

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lumetta, Gregg J.

Two experiments were conducted to explore the mechanism by which phosphorus is removed from Hanford tank sludge by caustic leaching. In the first experiment, a series of phosphate salts were treated with 3 M NaOH under conditions prototypic of the actual leaching process to be performed in the Waste Treatment and Immobilization Plant (WTP). The phosphates used were aluminum phosphate, bismuth phosphate, chromium(III) phosphate, and β-tri-calcium phosphate; all of these phases have previously been determined to exist in Hanford tank sludge. The leachate solution was sampled at selected time intervals and analyzed for the specific metal ion involved (Al, Bi,more » Ca, or Cr) and for P (total and as phosphate). The solids remaining after completion of the caustic leaching step were analyzed to determine the reaction product. In the second experiment, the dependence of P removal from bismuth phosphate was examined as a function of the hydroxide ion concentration. It was anticipated that a plot of log[phosphate] versus log[hydroxide] would provide insight into the phosphorus-removal mechanism. This report describes the test activities outlined in Section 6.3.2.1, Preliminary Investigation of Phosphate Dissolution, in Test Plan TP-RPP-WTP-467, Rev.1. The objectives, success criteria, and test conditions of Section 6.3.2.1 are summarized here.« less

Leaching of Zinc Sulfide by Thiobacillus ferrooxidans: Experiments with a Controlled Redox Potential Indicate No Direct Bacterial Mechanism

PubMed Central

Fowler, T. A.; Crundwell, F. K.

1998-01-01

The role of Thiobacillus ferrooxidans in bacterial leaching of mineral sulfides is controversial. Much of the controversy is due to the fact that the solution conditions, especially the concentrations of ferric and ferrous ions, change during experiments. The role of the bacteria would be more easily discernible if the concentrations of ferric and ferrous ions were maintained at set values throughout the experimental period. In this paper we report results obtained by using the constant redox potential apparatus described previously (P. I. Harvey and F. K. Crundwell, Appl. Environ. Microbiol. 63:2586–2592, 1997). This apparatus is designed to control the redox potential in the leaching compartment of an electrolytic cell by reduction or oxidation of dissolved iron. By controlling the redox potential the apparatus maintains the concentrations of ferrous and ferric ions at their initial values. Experiments were conducted in the presence of T. ferrooxidans and under sterile conditions. Analysis of the conversion of zinc sulfide in the absence of the bacteria and analysis of the conversion of zinc sulfate in the presence of the bacteria produced the same results. This indicates that the only role of the bacteria under the conditions used is regeneration of ferric ions in solution. In this work we found no evidence that there is a direct mechanism for bacterial leaching. PMID:9758769

Heavy metal leaching from mine tailings as affected by plants

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhu, D.; Schwab, A.P.; Banks, M.K.

A column experiment was conducted to determine the impact of soil cover and plants on heavy metal leaching from mine tailings and heavy metal contaminated soil. Columns made of PVC were constructed with 30 cm subsoil covered by 30 cm of mine tailings followed by 0, 30, or 60 cm subsoil covered by 30 cm of mine tailings followed by 0, 30, or 60 cm of clean topsoil. Two grasses, tall fescue (Festuca arundinacea Schreb.) and big bluestem (Andropogon gerardii), were grown in the columns. The columns were leached at a slow rate for 1 yr with a 0.001 Mmore » CaCl{sub 2} solution under unsaturated conditions. The presence of both tall fescue and big bluestem increased Zn and Cd concentrations in the leachate. Lead concentrations in leachates were not affected by the presence of plants. Although plants generally reduced the total amount of water leached, total mass of Zn and Cd leached generally was not impacted by plants. Total mass of Pb leached was positively correlated with total leachate collected from each column. Covering the mine tailings with 60 cm of topsoil increased the mass of Zn and Cd leached relative to no topsoil. When the subsoil was absent, Zn and Cd leaching increased by as much as 20-fold, verifying the ability of soil to act as a sink for metals. Mine tailing remediation by establishing vegetation can reduce Pb movement but may enhance short-term Cd and Zn leaching. However, the changes were relatively small and do not outweigh the benefits of using vegetation in mine tailings reclamation.« less

Nutrient leaching in a Colombian savanna Oxisol amended with biochar.

PubMed

Major, Julie; Rondon, Marco; Molina, Diego; Riha, Susan J; Lehmann, Johannes

2012-01-01

Nutrient leaching in highly weathered tropical soils often poses a challenge for crop production. We investigated the effects of applying 20 t ha biochar (BC) to a Colombian savanna Oxisol on soil hydrology and nutrient leaching in field experiments. Measurements were made over the third and fourth years after a single BC application. Nutrient contents in the soil solution were measured under one maize and one soybean crop each year that were routinely fertilized with mineral fertilizers. Leaching by unsaturated water flux was calculated using soil solution sampled with suction cup lysimeters and water flux estimates generated by the model HYDRUS 1-D. No significant difference ( > 0.05) was observed in surface-saturated hydraulic conductivity or soil water retention curves, resulting in no relevant changes in water percolation after BC additions in the studied soils. However, due to differences in soil solution concentrations, leaching of inorganic N, Ca, Mg, and K measured up to a depth of 0.6 m increased ( < 0.05), whereas P leaching decreased, and leaching of all nutrients (except P) at a depth of 1.2 m was significantly reduced with BC application. Changes in leaching at 2.0 m depth with BC additions were about one order of magnitude lower than at other depths, except for P. Biochar applications increased soil solution concentrations and downward movement of nutrients in the root zone and decreased leaching of Ca, Mg, and Sr at 1.2 m, possibly by a combination of retention and crop nutrient uptake. Copyright © by the American Society of Agronomy, Crop Science Society of America, and Soil Science Society of America, Inc.

Carbonate ions and arsenic dissolution by groundwater

USGS Publications Warehouse

Kim, M.-J.; Nriagu, J.; Haack, S.

2000-01-01

Samples of Marshall Sandstone, a major source of groundwater with elevated arsenic levels in southeast Michigan, were exposed to bicarbonate ion under controlled chemical conditions. In particular, effects of pH and redox conditions on arsenic release were evaluated. The release of arsenic from the aquifer rock was strongly related to the bicarbonate concentration in the leaching solution. The results obtained suggest that the carbonation of arsenic sulfide minerals, including orpiment (As2S3) and realgar (As2S2), is an important process in leaching arsenic into groundwater under anaerobic conditions. The arseno-carbonate complexes formed, believed to be As(CO3)2-, As(CO3)(OH)2-, and AsCO3+, are stable in groundwater. The reaction of ferrous ion with the thioarsenite from carbonation process can result in the formation of arsenopyrite which is a common mineral in arsenic-rich aquifers.Samples of Marshall Sandstone, a major source of groundwater with elevated arsenic levels in southeast Michigan, were exposed to bicarbonate ion under controlled chemical conditions. In particular, effects of pH and redox conditions on arsenic release were evaluated. The release of arsenic from the aquifer rock was strongly related to the bicarbonate concentration in the leaching solution. The results obtained suggest that the carbonation of arsenic sulfide minerals, including orpiment (As2S3) and realgar (As2S2), is an important process in leaching arsenic into groundwater under anaerobic conditions. The arseno-carbonate complexes formed, believed to be As(CO3)2-, As(CO3)(OH)2-, and AsCO3+, are stable in groundwater. The reaction of ferrous ion with the thioarsenite from carbonation process can result in the formation of arsenopyrite which is a common mineral in arsenic-rich aquifers.The role of bicarbonate in leaching arsenic into groundwater was investigated by conducting batch experiments using core samples of Marshall Sandstone from southeast Michigan and different bicarbonate solutions. The effects of pH and redox conditions on As dissolution were examined. Results showed that As was not leached significantly out of the Marshall Sandstone samples after 3 d using either deionized water or groundwater, but As was leached efficiently by sodium bicarbonate, potassium bicarbonate, and ferric chloride solutions. The leaching rate with sodium bicarbonate was about 25% higher than that with potassium bicarbonate. The data indicated that bicarbonate ion was involved primarily in As dissolution and that hydroxyl radical ion did not affect As dissolution to any significant degree. The amount of As leached was dependent upon the sodium bicarbonate concentration, increasing with reaction time for each concentration. Significant As leaching was found in the extreme pH ranges of <1.9 and 8.0-10.4. The resulting arseno-carbonate complexes formed were stable in groundwater.

Salt as a mitigation option for decreasing nitrogen leaching losses from grazed pastures.

PubMed

Ledgard, Stewart F; Welten, Brendon; Betteridge, Keith

2015-12-01

The main source of nitrogen (N) leaching from grazed pastures is animal urine with a high N deposition rate (i.e. per urine patch), particularly between late summer and early winter. Salt is a potential mitigation option as a diuretic to induce greater drinking-water intake, increase urination frequency, decrease urine N concentration and urine N deposition rate, and thereby potentially decrease N leaching. This hypothesis was tested in three phases: a cattle metabolism stall study to examine effects of salt supplementation rate on water consumption, urination frequency and urine N concentration; a grazing trial to assess effects of salt (150 g per heifer per day) on urination frequency; and a lysimeter study on effects of urine N rate on N leaching. Salt supplementation increased cattle water intake. Urination frequency increased by up to 69%, with a similar decrease in urine N deposition rate and no change in individual urination volume. Under field grazing, sensors showed increased urination frequency by 17%. Lysimeter studies showed a proportionally greater decrease in N leaching with decreased urine N rate. Modelling revealed that this could decrease per-hectare N leaching by 10-22%. Salt supplementation increases cattle water intake and urination frequency, resulting in a lower urine N deposition rate and proportionally greater decrease in urine N leaching. Strategic salt supplementation in autumn/early winter with feed is a practical mitigation option to decrease N leaching in grazed pastures. © 2015 Society of Chemical Industry.

Characterization of solidified radioactive waste due to the incorporation of high- and low-density polyethylene granules and titanium dioxide in mortar matrices

DOE Office of Scientific and Technical Information (OSTI.GOV)

Peric, A.

1997-12-31

The rutile form of titanium dioxide and granules of high density polyethylene (PEHD) and low density polyethylene (PELD) were used to prepare mortar matrices for immobilization of radioactive waste materials containing {sup 137}Cs. PELD, PEHD and TiO{sub 2} were added to mortar matrix preparations with the objective of improving physico-chemical characteristics of the radwaste-mortar matrix mixtures, in particular the leach-rate of the immobilized radionuclide. One type of PELD and two types of PEHD were used to replace 50 wt.% of stone granules normally used in the matrix, in order to decrease the porosity and density of the mortar matrix andmore » to avoid segregation of the stone particles at the bottom of the immobilized radioactive waste cylindrical form. TiO{sub 2} was also added to the mortar formulation, replacing 5 and 8 wt.% of the total cement weight. Cured samples were investigated under temperature stress conditions, where the temperature extremes were: T{sub min} = {minus}20 C, T{sub max} = +70 C. Samples were periodically immersed in distilled water at the ambient room temperature, after each freezing and heating treatment. Results of accelerated leaching experiments for these samples and samples prepared exclusively with polyethylenes replacing 100% of the stone granules and TiO{sub 2}, treated in nonaccelerated leaching experiments, were compared. Even using an accelerated ageing leach test that overestimates {sup 137}Cs leach rates, it can be deduced, that radionuclide leach rates from the radioactive waste mortar mixture forms were improved. Leach rates decreased from 5%, for the material prepared with stone aggregate, to 3.1 to 4.0%, for the materials prepared solely with PEHD, PELD or TiO{sub 2}, and to about 3% for all six types of the TiO{sub 2}-PEHD and TiO{sub 2}-PELD mixtures tested.« less

Minimization of methabenzthiazuron residues in leaching water using amended soils and photocatalytic treatment with TiO2 and ZnO.

PubMed

Fenoll, José; Flores, Pilar; Hellín, Pilar; Hernández, Joaquín; Navarro, Simon

2014-04-01

In the present work, potential groundwater pollution by methabenzthiazuron (MTBU) and the effect of three different amendments (composted sheep manure, composted pine bark and spent coffee grounds) on its mobility were investigated under laboratory conditions. The efficiency of ZnO and TiO2 suspensions in the photocatalytic degradation of MTBU in leaching water was also investigated. The relative and cumulative breakthrough curves were obtained from disturbed soil columns. The presence and/or addition of organic matter drastically reduced the movement of the herbicide. On other hand, photocatalytic experiments showed that the addition of ZnO and TiO2 strongly enhances the degradation rate of this herbicide compared with the results of photolytic experiments under artificial light. ZnO appeared to be more effective in MTBU oxidation than TiO2. The results obtained point to the interest of using organic wastes and heterogeneous photocatalysis for reducing the pollution of groundwater by pesticide drainage. Copyright © 2014 The Research Centre for Eco-Environmental Sciences, Chinese Academy of Sciences. Published by Elsevier B.V. All rights reserved.

Leachate Properties and Cadmium Migration Through Freeze-thaw Treated Soil Columns.

PubMed

Xu, Meng; Zheng, Yue; Chen, Weiwei; Mao, Na; Guo, Ping

2017-01-01

Soil column leaching experiments were conducted to study the effects of multiple freeze-thaw cycles on the vertical migration of cadmium (Cd). Three Cd-spiked leaching solutions of different properties were derived from snowmelt, sludge, and straw, designated as B, W and J, respectively. The leaching solutions varied in dissolved organic matter (DOM) concentrations in the order of J > W > B. Changes in leachate properties and Cd concentration were observed. The results showed that pH values of all the leachate solutions through freeze-thaw treated soil columns were higher than those of leachates through unfrozen soils. However, electrical conductivity (EC) values decreased compared with leachates in unfrozen treated soil columns. Although the concentrations of DOM in leachate solutions had no evident differences between the freeze-thaw and unfrozen treated soil columns, the concentrations of DOM in the leachate solutions B, W and J were different. Freeze-thaw cycles resulted in increased concentrations of Cd in the leachate solutions in the order J > W > B, and promoted a deeper migration of Cd in the soil columns. Thus, it was shown that freeze-thaw cycles may increase the risk of groundwater pollution by Cd.

Ranking Coal Ash Materials for Their Potential to Leach Arsenic and Selenium: Relative Importance of Ash Chemistry and Site Biogeochemistry

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schwartz, Grace E.; Hower, James C.; Phillips, Allison L.

The chemical composition of coal ash is highly heterogeneous and dependent on the origin of the source coal, combustion parameters, and type and configuration of air pollution control devices. This heterogeneity results in uncertainty in the evaluation of leaching potential of contaminants from coal ash. The goal of this work was to identify whether a single leaching protocol could roughly group high-leaching potential coal ash from low-leaching potential coal ash, with respect to arsenic (As) and selenium (Se). We used four different leaching tests, including the Toxicity Characteristic Leaching Protocol (TCLP), natural pH, aerobic sediment microcosms, and anaerobic sediment microcosmsmore » on 10 different coal ash materials, including fly ash, lime-treated ash, and flue gas desulfurization materials. Leaching tests showed promise in categorizing high and low-leaching potential ash materials, indicating that a single point test could act as a first screening measure to identify high-risk ash materials. However, the amount of contaminant leached varied widely across tests, reflecting the importance of ambient conditions (pH, redox state) on leaching. These results demonstrate that on-site geochemical conditions play a critical role in As and Se mobilization from coal ash, underscoring the need to develop a situation-based risk assessment framework for contamination by coal ash pollutants.« less

Ranking Coal Ash Materials for Their Potential to Leach Arsenic and Selenium: Relative Importance of Ash Chemistry and Site Biogeochemistry

DOE PAGES

Schwartz, Grace E.; Hower, James C.; Phillips, Allison L.; ...

2018-01-23

The chemical composition of coal ash is highly heterogeneous and dependent on the origin of the source coal, combustion parameters, and type and configuration of air pollution control devices. This heterogeneity results in uncertainty in the evaluation of leaching potential of contaminants from coal ash. The goal of this work was to identify whether a single leaching protocol could roughly group high-leaching potential coal ash from low-leaching potential coal ash, with respect to arsenic (As) and selenium (Se). We used four different leaching tests, including the Toxicity Characteristic Leaching Protocol (TCLP), natural pH, aerobic sediment microcosms, and anaerobic sediment microcosmsmore » on 10 different coal ash materials, including fly ash, lime-treated ash, and flue gas desulfurization materials. Leaching tests showed promise in categorizing high and low-leaching potential ash materials, indicating that a single point test could act as a first screening measure to identify high-risk ash materials. However, the amount of contaminant leached varied widely across tests, reflecting the importance of ambient conditions (pH, redox state) on leaching. These results demonstrate that on-site geochemical conditions play a critical role in As and Se mobilization from coal ash, underscoring the need to develop a situation-based risk assessment framework for contamination by coal ash pollutants.« less

Leaching of soils during laboratory incubations does not affect soil organic carbon mineralisation but solubilisation.

PubMed

González-Domínguez, Beatriz; Studer, Mirjam S; Hagedorn, Frank; Niklaus, Pascal A; Abiven, Samuel

2017-01-01

Laboratory soil incubations provide controlled conditions to investigate carbon and nutrient dynamics; however, they are not free of artefacts. As carbon and nitrogen cycles are tightly linked, we aimed at investigating whether the incubation-induced accumulation of mineral nitrogen (Nmin) biases soil organic carbon (SOC) mineralisation. For this, we selected two soils representative of the C:N ratio values found in European temperate forests, and applied two incubation systems: 'closed' beakers and 'open' microlysimeters. The latter allowed leaching the soil samples during the incubation. By the end of the 121-day experiment, the low C:N soil significantly accumulated more Nmin in beakers (5.12 g kg-1 OC) than in microlysimeters (3.00 g kg-1 OC) but there was not a significant difference in SOC mineralisation at any point of the experiment. On the other hand, Nmin did not accumulate in the high C:N soil but, by the end of the experiment, leaching had promoted 33.9% more SOC solubilisation than beakers. Therefore, we did not find evidence that incubation experiments introduce a bias on SOC mineralisation. This outcome strengthens results from soil incubation studies.

Leaching of soils during laboratory incubations does not affect soil organic carbon mineralisation but solubilisation

PubMed Central

Studer, Mirjam S.; Hagedorn, Frank; Niklaus, Pascal A.; Abiven, Samuel

2017-01-01

Laboratory soil incubations provide controlled conditions to investigate carbon and nutrient dynamics; however, they are not free of artefacts. As carbon and nitrogen cycles are tightly linked, we aimed at investigating whether the incubation-induced accumulation of mineral nitrogen (Nmin) biases soil organic carbon (SOC) mineralisation. For this, we selected two soils representative of the C:N ratio values found in European temperate forests, and applied two incubation systems: ‘closed’ beakers and ‘open’ microlysimeters. The latter allowed leaching the soil samples during the incubation. By the end of the 121-day experiment, the low C:N soil significantly accumulated more Nmin in beakers (5.12 g kg-1 OC) than in microlysimeters (3.00 g kg-1 OC) but there was not a significant difference in SOC mineralisation at any point of the experiment. On the other hand, Nmin did not accumulate in the high C:N soil but, by the end of the experiment, leaching had promoted 33.9% more SOC solubilisation than beakers. Therefore, we did not find evidence that incubation experiments introduce a bias on SOC mineralisation. This outcome strengthens results from soil incubation studies. PMID:28380005

Leaching of DOC, DN, and inorganic constituents from scrap tires.

PubMed

Selbes, Meric; Yilmaz, Ozge; Khan, Abdul A; Karanfil, Tanju

2015-11-01

One concern for recycle and reuse of scrap tires is the leaching of tire constituents (organic and inorganic) with time, and their subsequent potential harmful impacts in environment. The main objective of this study was to examine the leaching of dissolved organic carbon (DOC), dissolved nitrogen (DN), and selected inorganic constituents from scrap tires. Different sizes of tire chips and crumb rubber were exposed to leaching solutions with pH's ranging from 3.0 to 10.0 for 28days. The leaching of DOC and DN were found to be higher for smaller size tire chips; however, the leaching of inorganic constituents was independent of the size. In general, basic pH conditions increased the leaching of DOC and DN, whereas acidic pH conditions led to elevated concentrations of metals. Leaching was minimal around the neutral pH values for all the monitored parameters. Analysis of the leaching rates showed that components associated with the rubbery portion of the tires (DOC, DN, zinc, calcium, magnesium, etc.) exhibited an initial rapid followed by a slow release. On the other hand, a constant rate of leaching was observed for iron and manganese, which are attributed to the metal wires present inside the tires. Although the total amounts that leached varied, the observed leaching rates were similar for all tire chip sizes and leaching solutions. Operation under neutral pH conditions, use of larger size tire chips, prewashing of tires, and removal of metal wires prior to application will reduce the impact of tire recycle and reuse. Copyright © 2015 Elsevier Ltd. All rights reserved.

Process optimization and leaching kinetics of zinc and manganese metals from zinc-carbon and alkaline spent batteries using citric acid reagent

NASA Astrophysics Data System (ADS)

Yuliusman; Amiliana, R. A.; Wulandari, P. T.; Huda, M.; Kusumadewi, F. A.

2018-03-01

Zn-Carbon and Alkaline spent batteries contains heavy metals, such as zinc and manganese, which can causes environmental problem if not handled properly. Usually the recovery of these metals were done by leaching method using strong acid, but the use of strong acids as leaching reagents can be harmful to the environment. This paper concerns the recovery of Zn and Mn metals from Zn-C and alkaline spent batteries with leaching method using citric acid as the environmental friendly leaching reagent. The leaching conditions using citric acid were optimized and the leaching kinetics of Zn and Mn in citric acid solution was investigated. The leaching of 89.62% Zn and 63.26% Mn was achieved with 1.5 M citric acid, 90°C temperature, and 90 minutes stirring time. Kinetics data for the dissolution of Zn showed the best fit to chemical control shrinking core model, while the diffusion controlled model was suitable for the dissolution of Mn kinetics data. The activation energy of 6.12 and 1.73 kcal/mol was acquired for the leaching of Zn and Mn in the temperature range 60°C-90°C.

Coatings to reduce wood preservative leaching.

PubMed

Nejad, Mojgan; Cooper, Paul

2010-08-15

The efficiency of semitransparent penetrating stains to reduce leaching of wood preservative components was evaluated. Five commercial wood deck finishes were applied to untreated and chromated copper arsenate (CCA), alkaline copper quat (ACQ), and copper azole (CA) treated wood, and leachates were collected and analyzed during 3 years of natural weathering exposure in Toronto, Canada. All stains evaluated effectively reduced the cumulative leaching of all inorganic preservative components by about 60% on average. Although most coatings showed significant film degradation starting around 12 months, the reduced leaching persisted even after 3 years. This suggests that temporary protection of wood with a coating during the early stages of use resulted in long-term reduction in preservative leaching potential. A two-week screening leaching test was able to predict the long-term leaching performance of different coatings reasonably well. Cured coating glass transition temperature (Tg) and liquid coating viscosity were the most important variables affecting a leaching prediction model. To effectively reduce leaching of preservative components from treated wood, coatings should have Tg low enough to withstand stresses caused by freezing in winter and have adequate viscosity to form a barrier film layer on the wood surface.

Soil pH on mobility of imazaquin in oxisols with positive balance of charges.

PubMed

Regitano, Jussara B; da Rocha, Wadson S D; Alleoni, Luís R F

2005-05-18

The influence of soil pH on the leaching potential of the ionizable herbicide imazaquin was assessed on the profile of two highly weathered soils having a net positive charge in the B horizon, in contrast to a soil having a net negative charge in the whole profile, using packed soil column experiments. Imazaquin leached to a large extent and faster at Kd values lower than 1.0 L kg(-1), a much more lenient limit than usually proposed for pesticides in the literature (Kd < 5.0 L kg(-1)). The amount of imazaquin leached increased with soil pH. As the soil pH increased, the percentage of imazaquin in the anionic forms, the negative surface potential of the soils, as well as imazaquin water solubility also increased, thus reducing sorption because of repulsive electrostatic forces (hydrophilic interactions). For all surface samples (0-0.2 m), imazaquin did not leach at soil pH values lower than pKa (3.8) and more than 80% of the applied amount was leached at pH values higher than 5.5. For subsurface samples from the acric soils, imazaquin only began to leach at soil pH values > zero point of salt effects (ZPSE > 5.7). In conclusion, the use of surface K(oc) values to predict the amount of imazaquin leached within soil profiles having a positive balance of charges may greatly overestimate its actual leaching potential.

Controls on atrazine leaching through a soil-unsaturated fractured limestone sequence at Brévilles, France.

PubMed

Roulier, Stéphanie; Baran, Nicole; Mouvet, Christophe; Stenemo, Fredrik; Morvan, Xavier; Albrechtsen, Hans-Jørgen; Clausen, Liselotte; Jarvis, Nicholas

2006-03-01

The objective of this study was to identify the main controls on atrazine leaching through luvisols and calcisols overlying fissured limestone using the dual-permeability model MACRO. The model parameterisation was based on a combination of direct measurements (e.g. hydraulic properties, adsorption and degradation), literature data and calibration against bromide leaching experiments in field plots. A Monte Carlo sensitivity analysis was carried out for a typical application pattern, considering two different depths of unsaturated limestone (15 and 30 m). MACRO calibrations to the field experiments demonstrated the occurrence of strong macropore flow in the luvisol, while transport in the calcisol could be described by the advection-dispersion equation. MACRO simulations of tritium and atrazine leaching qualitatively matched tritium concentration profiles measured in the limestone and atrazine concentrations measured in piezometers and in aquifer discharge via a spring. The sensitivity analysis suggested that the thickness of the limestone, as well as the transport properties and processes occurring in the unsaturated rock (e.g. matrix vs. fissure flow) will have little significant long-term effect on atrazine leaching, mainly because degradation is very slow in the limestone. No mineralization of atrazine was detected in one-year incubations and a mean half-life of 10 years was assumed in the simulations. Instead, processes occurring in the soil exerted the main control on predicted atrazine leaching, especially variations in the degradation rate and the strength of sorption and macropore flow. However, fissure flow in unsaturated rock is expected to exert a much more significant control on groundwater contamination for compounds that degrade more readily in the deep vadose zone.

EDTA-assisted phytoextraction of heavy metals by turfgrass from municipal solid waste compost using permeable barriers and associated potential leaching risk.

PubMed

Zhao, Shulan; Lian, Fei; Duo, Lian

2011-01-01

A column experiment with horizontal permeable barriers was conducted to investigate phytoextraction of heavy metals by Lolium perenne L. from municipal solid waste compost following EDTA application, as well as to study the effects of L. perenne and permeable barriers on preventing metal from leaching. In columns with barriers, EDTA addition yielded maximum concentrations of Cu, Zn and Pb of 155, 541 and 33.5 mg kg(-1) in shoot, respectively. This led to 4.2, 2.1 and 7.4 times higher concentrations of Cu, Zn and Pb compared to treatment with no chelating agent, respectively. In treatments with 10 mmol kg(-1) EDTA, the barriers reduced leaching of Cu, Zn and Pb by approximately three times, respectively, resulting in leaching of total initial Cu, Zn and Pb by 27.3%, 25.2% and 28.8%, respectively, after four times' irrigation. These results indicate that L. perenne and permeable barriers are effective to reduce leaching of heavy metals and minimize the risk of contaminating groundwater in EDTA-enhanced phytoremediation. Thus these findings highlight that turfgrass and permeable barriers can effectively prevent metal leaching. Copyright © 2010 Elsevier Ltd. All rights reserved.

Biocatalytic and chemical leaching of a low-grade nickel laterite ore

NASA Astrophysics Data System (ADS)

Ciftci, Hasan; Atik, Suleyman; Gurbuz, Fatma

2018-04-01

Nickel and cobalt recovery from a low-grade nickel laterite ore, supplied from Çaldağ deposit (Manisa, Turkey) were investigated by bio and chemical leaching processes. The fungus, Aspergillus niger was used for biocatalytic leaching experiments. The effects of parameters (solid ratio and sucrose concentration) on the biocatalytic leaching of the ore were initially tested in flasks to obtain the optimum conditions for the A. niger. Then chemical leaching was applied as a comparison to bioleaching, using organic acids (citric, oxalic, acetic and gluconic acids) as well as a mixture of acids. According the results, the maximum dissolution yield of nickel, cobalt and iron were detected respectively as 95.3%, 74.3% and 50.0% by biocatalytic processes which containing 25% (w/v) sucrose and 1% (w/v) solids. The increase in the solid ratio adversely influenced the biocatalytic activity of A. niger. Finally, further tests in reactors (v = 1 and 10 L) were performed using the optimum conditions from the flask tests. The difference in metals recovery between biocatalytic and chemical leaching was significantly important. Bioleaching produced higher Ni and Co extractions (34.3-75.6%) than chemical process.

Variation law of gas holdup in an autoclave during the pressure leaching process by using a mixed-flow agitator

NASA Astrophysics Data System (ADS)

Tian, Lei; Liu, Yan; Tang, Jun-jie; Lü, Guo-zhi; Zhang, Ting-an

2017-08-01

The multiphase reaction process of pressure leaching is mainly carried out in the liquid phase. Therefore, gas holdup is essential for the gas-liquid-solid phase reaction and the extraction rate of valuable metals. In this paper, a transparent quartz autoclave, a six blades disc turbine-type agitator, and a high-speed camera were used to investigate the gas holdup of the pressure leaching process. Furthermore, experiments determining the effects of agitation rate, temperature, and oxygen partial pressure on gas holdup were carried out. The results showed that when the agitation rate increased from 350 to 600 r/min, the gas holdup increased from 0.10% to 0.64%. When the temperature increased from 363 to 423 K, the gas holdup increased from 0.14% to 0.20%. When the oxygen partial pressure increased from 0.1 to 0.8 MPa, the gas holdup increased from 0.13% to 0.19%. A similar criteria relationship was established by Homogeneous Principle and Buckingham's theorem. Comprehensively, empirical equation of gas holdup was deduced on the basis of experimental data and the similarity theory, where the criterion equation was determined as ɛ = 4.54 × 10-11 n 3.65 T 2.08 P g 0.18. It can be seen from the formula that agitation rate made the most important impact on gas holdup in the pressure leaching process using the mixed-flow agitator.

Investigation of biosolids degradation under flooded environments for use in underwater cover designs for mine tailing remediation.

PubMed

Jia, Yu; Nason, Peter; Maurice, Christian; Alakangas, Lena; Öhlander, Björn

2015-07-01

To evaluate the potential suitability of digested sewage sludge (frequently termed biosolids) for use as underwater cover material for mine waste tailings, the degradability of biosolids at 20 - 22 °C under flooded anaerobic conditions was evaluated during incubation for 230 days. Leaching of elements from the flooded anaerobic system was also evaluated. Biosolid degradation was confirmed by the generation and accumulation of CH4 and CO2. Specifically, approximately 1.65 mmoL gas/g biosolids was generated as a result of incubation, corresponding to degradation of 7.68% of the organic matter, and the residue was stable at the end of the laboratory experiment. Under field conditions in northern Sweden, it is expected that the degradation rate will be much slower than that observed in the present study (Nason et al. Environ Earth Sci 70:30933105, 2013). Although the majority of biosolid fractions (>92%) were shown to be recalcitrant during the incubation period, long-term monitoring of further degradability of residue is necessary. The leaching results showed that most of the metals and metalloids leached from the biosolids at day 230 were below the limit value for non-hazardous waste, although Ni was the only element approximately three times higher than the limit value for inert material at the landfill site. In conclusion, biosolids have potential for use as covering material for underwater storage of tailings based on their biodegradability and leaching of elements.

Upgrading tantalum and niobium oxides content in Bangka tin slag with double leaching

NASA Astrophysics Data System (ADS)

Soedarsono, J. W.; Permana, S.; Hutauruk, J. K.; Adhyputra, R.; Rustandi, A.; Maksum, A.; Widana, K. S.; Trinopiawan, K.; Anggraini, M.

2018-03-01

Tantalum has become one of the 14 types of critical materials where the level of its availability is assumed as the midterm critical metal. Benefits of the element tantalum in the electronics field increased the deficit balance of supply / demand, as more variations of electronic products developed. The tantalum experts calculated the level of availability until 2020. Base on the previous studies, tin slag is a secondary source of tantalum and niobium. This study uses tin slag from Bangka, Indonesia, abbreviated, Bangka Tin Slag (BTS). BTS was roasted, water quenched and sieved, abbreviated BTS-RQS.BTS was roasted, water quenched and sieved, abbreviated BTS-RQS.BTS-RQS was roasted at a temperature 700□C given sample code BTS-R700QS, while roasted at 800°C given sample code BTS-R800QS.A variable leaching experiment on BTS-R700QS was solvent concentration variable and on BTS-R800QS was time variable. The entire residue was characterized by X-Ray Fluorescence (XRF), and the optimum results are on the BTS-R800QS leaching into 5 M NaOH for 20 min followed by 5M HCl for 50 min, with content of Ta2O5 and Nb2O51.56% and 1.11%, respectively. The result of XRF measurement showed was the increasing of TNO content due to the increasing solvent concentration and time of acid leaching. The discussion of thermodynamics this study used was HSC Chemistry 6 as a supporting data.

Evaluating the biogas potential of the dry fraction from pretreatment of food waste from households.

PubMed

Murto, Marika; Björnsson, Lovisa; Rosqvist, Håkan; Bohn, Irene

2013-05-01

At the waste handling company NSR, Helsingborg, Sweden, the food waste fraction of source separated municipal solid waste is pretreated to obtain a liquid fraction, which is used for biogas production, and a dry fraction, which is at present incinerated. This pretreatment and separation is performed to remove impurities, however also some of the organic material is removed. The possibility of realising the methane potential of the dry fraction through batch-wise dry anaerobic digestion was investigated. The anaerobic digestion technique used was a two-stage process consisting of a static leach bed reactor and a methane reactor. Treatment of the dry fraction alone and in a mixture with structural material was tested to investigate the effect on the porosity of the leach bed. A tracer experiment was carried out to investigate the liquid flow through the leach beds, and this method proved useful in demonstrating a more homogenous flow through the leach bed when structural material was added. Addition of structural material to the dry fraction was needed to achieve a functional digestion process. A methane yield of 98 m3/ton was obtained from the dry fraction mixed with structural material after 76 days of digestion. This was in the same range as obtained in the laboratory scale biochemical methane potential test, showing that it was possible to extract the organic content in the dry fraction in this type of dry digestion system for the production of methane. Copyright © 2013 Elsevier Ltd. All rights reserved.

Effect of nitrification inhibitor DMPP on nitrogen leaching, nitrifying organisms, and enzyme activities in a rice-oilseed rape cropping system.

PubMed

Li, Hua; Liang, Xinqiang; Chen, Yingxu; Lian, Yanfeng; Tian, Guangming; Ni, Wuzhong

2008-01-01

DMPP (3,4-dimethylpyrazole phosphate) has been used to reduce nitrogen (N) loss from leaching or denitrification and to improve N supply in agricultural land. However, its impact on soil nitrifying organisms and enzyme activities involved in N cycling is largely unknown. Therefore, an on-farm experiment, for two years, has been conducted, to elucidate the effects of DMPP on mineral N (NH4(+)-N and NO3(-)-N) leaching, nitrifying organisms, and denitrifying enzymes in a rice-oilseed rape cropping system. Three treatments including urea alone (UA), urea + 1% DMPP (DP), and no fertilizer (CK), have been carried out. The results showed that DP enhanced the mean NH4(+)-N concentrations by 19.1%--24.3%, but reduced the mean NO3(-)-N concentrations by 44.9%--56.6% in the leachate, under a two-year rice-rape rotation, compared to the UA treatment. The population of ammonia oxidizing bacteria, the activity of nitrate reductase, and nitrite reductase in the DP treatment decreased about 24.5%--30.9%, 14.9%--43.5%, and 14.7%--31.6%, respectively, as compared to the UA treatment. However, nitrite oxidizing bacteria and hydroxylamine reductase remained almost unaffected by DMPP. It is proposed that DMPP has the potential to either reduce NO3(-)-N leaching by inhibiting ammonia oxidization or N losses from denitrification, which is in favor of the N conversations in the rice-oilseed rape cropping system.

Comparison of leaching characteristics of heavy metals in APC residue from an MSW incinerator using various extraction methods.

PubMed

Chiang, Kung-Yuh; Tsai, Chen-Chiu; Wang, Kuen-Sheng

2009-01-01

This study investigates four extraction methods (water extraction, toxicity characteristics leaching procedure (TCLP), modified TCLP with pH control, and sequential chemical extraction (SCE)), each representing different liquid-to-solid (L/S) ratios, pH controls, and types of leachant, and their effects on the leaching concentration of heavy metals in municipal solid waste (MSW) incinerator air pollution control (APC) residue. The results indicated that for extraction with distilled water, the heavy metal leaching concentration (mg/l) decreased with L/S ratio, but the amount of heavy metal released (AHMR), defined as the leached amount of heavy metals to the weight of the tested sample (mg/kg), increased with an increase in L/S ratio, in the range of 2-100. The results also showed that both the leaching concentration and the amount of released metals were strongly pH-dependent in the TCLP and modified TCLP tests. In the case of pHs lower than 6.5, the leaching concentrations of Cd, Pb, Cu, Zn, and Cr decreased with an increase in pH. As pH increased higher than 6.5, Cr and Zn were almost insoluble. Meanwhile, Cd and Cu also showed a similar trend but at pHs of 8.5 and 7.5, respectively. Due to the nature of amphoteric elements, in the case of pHs higher than 7, the Pb leaching concentration increased with increasing pH. In modified TCLP tests with the pH value controlled at the same level as in the SCE test, the heavy metal speciation approached the extractable carbonate bound fraction by the SCE. Both amounts of targeted metals leached from the SCE and modified TCLP tests were much higher than those for the regular TCLP and water extraction tests.

Study on mechanisms of different sulfuric acid leaching technologies of chromite

NASA Astrophysics Data System (ADS)

Shi, Pei-yang; Liu, Cheng-jun; Zhao, Qing; Shi, Hao-nan

2017-09-01

The extraction of chromate from chromite via the sulfuric acid leaching process has strong potential for practical use because it is a simple and environmentally friendly process. This paper aims to study the sulfuric acid leaching process using chromite as a raw material via either microwave irradiation or in the presence of an oxidizing agent. The results show that the main phases in Pakistan chromite are ferrichromspinel, chrompicotite, hortonolite, and silicate embedded around the spinel phases. Compared with the process with an oxidizing agent, the process involving microwaves has a higher leaching efficiency. When the mass fraction of sulfuric acid was 80% and the leaching time was 20 min, the efficiency could exceed 85%. In addition, the mechanisms of these two technologies fundamentally differ. When the leaching was processed in the presence of an oxidizing agent, the silicate was leached first and then expanded. By contrast, in the case of leaching under microwave irradiation, the chromite was dissolved layer by layer and numerous cracks appeared at the particle surface because of thermal shock. In addition, the silicate phase shrunk instead of expanding.

Optimization of HNO3 leaching of copper from old AMD Athlon processors using response surface methodology.

PubMed

Javed, Umair; Farooq, Robina; Shehzad, Farrukh; Khan, Zakir

2018-04-01

The present study investigates the optimization of HNO 3 leaching of Cu from old AMD Athlon processors under the effect of nitric acid concentration (%), temperature (°C) and ultrasonic power (W). The optimization study is carried out using response surface methodology with central composite rotatable design (CCRD). The ANOVA study concludes that the second degree polynomial model is fitted well to the fifteen experimental runs based on p-value (0.003), R 2 (0.97) and Adj-R 2 (0.914). The study shows that the temperature is the most significant process variable to the leaching concentration of Cu followed by nitric acid concentration. However, ultrasound power shows no significant impact on the leaching concentration. The optimum conditions were found to be 20% nitric acid concentration, 48.89 °C temperature and 5.52 W ultrasound power for attaining maximum concentration of 97.916 mg/l for Cu leaching in solution. Copyright © 2018 Elsevier Ltd. All rights reserved.

Leaching of manganese from electrolytic manganese residue by electro-reduction.

PubMed

Shu, Jiancheng; Liu, Renlong; Liu, Zuohua; Chen, Hongliang; Tao, Changyuan

2017-08-01

In this study, an improved process for leaching manganese from electrolytic manganese residue (EMR) by electro-reduction was developed. The mechanisms of the electro-reduction leaching were investigated through X-ray diffraction, scanning electron microscopy, X-ray fluorescence, and Brunauer Emmett Teller. The results show that the electric field could change the surface charge distribution of EMR particles, and the high-valent manganese can be reduced by electric field. The leaching efficient of manganese reached 84.1% under the optimal leaching condition: 9.2 wt% H 2 SO 4 , current density of 25 mA/cm 2 , solid-to-liquid ratio of 1:5, and leaching time for 1 h. It is 37.9% higher than that attained without an electric field. Meanwhile, the manganese content in EMR decreased from 2.57% to 0.48%.

Dynamics analysis of extraction of manganese intensified by electric field

NASA Astrophysics Data System (ADS)

Ma, Wenrui; Tao, Changyuan; Li, Huizhan; Liu, Zuohua; Liu, Renlong

2018-06-01

In this study, a process reinforcement technology for leaching process of pyrolusite was developed. The electric field was introduced to decrease reaction temperature and improve the leaching rate of pyrolusite. The mechanisms of electric field intensifying leaching process of pyrolusite were investigated through X-ray diffraction (XRD), and Brunauer Emmett Teller (BET) in detail. The results showed that the electric field could decrease obviously the apparent activation energy of leaching process of pyrolusite. The apparent activation energy of the leaching of pyrolusite intensified by electric field was calculated to be 53.76 kJ.mol-1. In addition, the leaching efficiency of manganese was effectively increased by 10% to 20% than that without electric field under the same conditions. This was because that the electron conduit between Fe (II)/Fe (III) and pyrite was dredged effectively by electric field.

Recovery of Precious and Base Metals from Waste Printed Circuit Boards Using a Sequential Leaching Procedure

NASA Astrophysics Data System (ADS)

Batnasan, Altansukh; Haga, Kazutoshi; Shibayama, Atsushi

2018-02-01

This paper considers the issue of recycling of waste printed circuit boards (WPCBs) containing precious and base metals in appreciable amounts. High-pressure oxidative leaching (HPOL) with dilute sulfuric acid resulted in removal of a significant amount of base metals from a WPCB ash sample obtained by incineration at 800°C. The parameters investigated in the precious metal leaching from WPCB residue after HPOL included the sulfuric acid concentration, thiourea concentration, oxidant concentration, leaching temperature, and leaching time. Recovery of gold, silver, and palladium of 100%, 81%, and 13% from the WPCB residue sample was achieved by thiourea leaching under optimized conditions. The results show that the efficiency of precious metal dissolution from the WPCB sample using thiourea solution depended strongly on the concentration of both thiourea and oxidant.

Recovery of Precious and Base Metals from Waste Printed Circuit Boards Using a Sequential Leaching Procedure

NASA Astrophysics Data System (ADS)

Batnasan, Altansukh; Haga, Kazutoshi; Shibayama, Atsushi

2017-12-01

This paper considers the issue of recycling of waste printed circuit boards (WPCBs) containing precious and base metals in appreciable amounts. High-pressure oxidative leaching (HPOL) with dilute sulfuric acid resulted in removal of a significant amount of base metals from a WPCB ash sample obtained by incineration at 800°C. The parameters investigated in the precious metal leaching from WPCB residue after HPOL included the sulfuric acid concentration, thiourea concentration, oxidant concentration, leaching temperature, and leaching time. Recovery of gold, silver, and palladium of 100%, 81%, and 13% from the WPCB residue sample was achieved by thiourea leaching under optimized conditions. The results show that the efficiency of precious metal dissolution from the WPCB sample using thiourea solution depended strongly on the concentration of both thiourea and oxidant.

Mercury mobilization and speciation linked to bacterial iron oxide and sulfate reduction: A column study to mimic reactive transfer in an anoxic aquifer.

PubMed

Hellal, Jennifer; Guédron, Stéphane; Huguet, Lucie; Schäfer, Jörg; Laperche, Valérie; Joulian, Catherine; Lanceleur, Laurent; Burnol, André; Ghestem, Jean-Philippe; Garrido, Francis; Battaglia-Brunet, Fabienne

2015-09-01

Mercury (Hg) mobility and speciation in subsurface aquifers is directly linked to its surrounding geochemical and microbial environment. The role of bacteria on Hg speciation (i.e., methylation, demethylation and reduction) is well documented, however little data is available on their impact on Hg mobility. The aim of this study was to test if (i) Hg mobility is due to either direct iron oxide reduction by iron reducing bacteria (IRB) or indirect iron reduction by sulfide produced by sulfate reducing bacteria (SRB), and (ii) to investigate its subsequent fate and speciation. Experiments were carried out in an original column setup combining geochemical and microbiological approaches that mimic an aquifer including an interface of iron-rich and iron depleted zones. Two identical glass columns containing iron oxides spiked with Hg(II) were submitted to (i) direct iron reduction by IRB and (ii) to indirect iron reduction by sulfides produced by SRB. Results show that in both columns Hg was leached and methylated during the height of bacterial activity. In the column where IRB are dominant, Hg methylation and leaching from the column was directly correlated to bacterial iron reduction (i.e., Fe(II) release). In opposition, when SRB are dominant, produced sulfide induced indirect iron oxide reduction and rapid adsorption of leached Hg (or produced methylmercury) on neoformed iron sulfides (e.g., Mackinawite) or its precipitation as HgS. At the end of the SRB column experiment, when iron-oxide reduction was complete, filtered Hg and Fe concentrations increased at the outlet suggesting a leaching of Hg bound to FeS colloids that may be a dominant mechanism of Hg transport in aquifer environments. These experimental results highlight different biogeochemical mechanisms that can occur in stratified sub-surface aquifers where bacterial activities play a major role on Hg mobility and changes in speciation. Copyright © 2015 Elsevier B.V. All rights reserved.

Iron removal on feldspar by using Averrhoa bilimbii as bioleaching agent

NASA Astrophysics Data System (ADS)

Amin, Muhammad; Aji, Bramantyo B.; Supriyatna, Yayat Iman; Bahfie, Fathan

2017-01-01

Investigation of Averrhoa bilimbii as bioleaching agent was carried out. Parameters of leaching duration, acid concentration, and temperature were performed in iron removal process. Feldspar with sized 149 µm was diluted in 30 ml acid solution in order to reduce its iron content. The experimental results showed a good technical feasibility of the process which iron oxide content of feldspar was decreased from 2.24% to 0.29%. The lowest iron concentration remained was obtained after 5 hours of leaching treatment at 60 °C, and concentrated (100 vol%) Averrhoa bilimbii extract as bioleaching agent. SEM characterizations were carried out on the feldspar before and after the leaching treatment. The result shows that there were no significant effect of leaching process on the ore morphology.

Study on Cr(VI) Leaching from Cement and Cement Composites

PubMed Central

Palascakova, Lenka; Kanuchova, Maria

2018-01-01

This paper reports an experimental study on hexavalent chromium leaching from cement samples and cement composites containing silica fume and zeolite additions that were subjected to various leaching agents. The water-soluble Cr(VI) concentrations in cements ranged from 0.2 to 3.2 mg/kg and represented only 1.8% of the total chromium content. The presence of chromium compounds with both chromium oxidation states of III and VI was detected in the cement samples by X-ray photoelectron spectroscopy (XPS). Leaching tests were performed in a Britton-Robinson buffer to simulate natural conditions and showed increased dissolution of Cr(VI) up to 6 mg/kg. The highest amount of leached hexavalent chromium was detected after leaching in HCl. The findings revealed that the leaching of chromium from cements was higher by 55–80% than that from the cement composites. A minimum concentration was observed for all cement samples when studying the relationship between the soluble Cr(VI) and the cement storage time. PMID:29690550

Study on Cr(VI) Leaching from Cement and Cement Composites.

PubMed

Estokova, Adriana; Palascakova, Lenka; Kanuchova, Maria

2018-04-22

This paper reports an experimental study on hexavalent chromium leaching from cement samples and cement composites containing silica fume and zeolite additions that were subjected to various leaching agents. The water-soluble Cr(VI) concentrations in cements ranged from 0.2 to 3.2 mg/kg and represented only 1.8% of the total chromium content. The presence of chromium compounds with both chromium oxidation states of III and VI was detected in the cement samples by X-ray photoelectron spectroscopy (XPS). Leaching tests were performed in a Britton-Robinson buffer to simulate natural conditions and showed increased dissolution of Cr(VI) up to 6 mg/kg. The highest amount of leached hexavalent chromium was detected after leaching in HCl. The findings revealed that the leaching of chromium from cements was higher by 55⁻80% than that from the cement composites. A minimum concentration was observed for all cement samples when studying the relationship between the soluble Cr(VI) and the cement storage time.

Recovery of valuable metals from waste diamond cutters through ammonia-ammonium sulfate leaching

NASA Astrophysics Data System (ADS)

Xue, Ping; Li, Guang-qiang; Yang, Yong-xiang; Qin, Qin-wei; Wei, Ming-xing

2017-12-01

Copper and zinc were recovered from waste diamond cutters through leaching with an ammonia-ammonium sulfate system and air as an oxidant. The effects of experimental parameters on the leaching process were investigated, and the potential-pH ( E-pH) diagrams of Cu-NH3-SO4 2--H2O and Zn-NH3-SO4 2--H2O at 25°C were drawn. Results showed that the optimal parameters for the leaching reaction are as follows: reaction temperature, 45°C; leaching duration, 3 h; liquid-to-solid ratio, 50:1 (mL/g); stirring speed, 200 r/min; ammonia concentration, 4.0 mol/L; ammonium sulfate concentration, 1.0 mol/L; and air flow rate, 0.2 L/min. The results of the kinetics study indicated that the leaching is controlled by the surface chemical reaction at temperatures below 35°C, and the leaching is controlled by diffusion through the product layer at temperatures above 35°C.

Leaching of indaziflam applied at two rates under different rainfall situations in Florida Candler soil.

PubMed

Jhala, Amit J; Ramirez, Analiza H M; Singh, Megh

2012-03-01

Indaziflam {N-[(1R, 2S)-2,3-dihydro-2,6-dimethyl-1H-inden-1-yl]-6-[(1RS)-1fluoroethyl]-1,3,5-triazine-2,4-diamine} is a new pre-emergence herbicide recently registered for a broad spectrum weed control in Florida citrus. Experiments were conducted to evaluate leaching of indaziflam applied at 73 and 145 g ai ha(-1) in Florida Candler soil under simulated rainfall of 5, 10, and 15 cm ha(-1). Indaziflam leached the least (12.6 ± 0.6 cm) when applied at 73 g ai ha(-1) under 5 cm ha(-1) rainfall. Indaziflam leached furthest (30.2 ± 0.9 cm) when applied at 145 g ai ha(-1) under 15 cm ha(-1) rainfall. The visual control ratings of a bio-indicator species ryegrass (Lolium multiflorum L.) was 97% at 15 cm ha(-1) rainfall when indaziflam applied at 145 g ai ha(-1) in the 26 to 30 cm horizon indicating the maximum movement and activity of indaziflam. A dose response experiment was conducted to determine the sensitivity of ryegrass to various doses of indaziflam that confirmed that application of indaziflam at 29.20 g ai ha(-1) was sufficient to prevent germination of ryegrass. There was no mortality of ryegrass plants beyond the 30 cm and the biomass of ryegrass was comparable with untreated control indicating that indaziflam did not leach beyond this distance even under 15 cm ha(-1) rainfall.

Leach test of cladding removal waste grout using Hanford groundwater

DOE Office of Scientific and Technical Information (OSTI.GOV)

Serne, R.J.; Martin, W.J.; Legore, V.L.

1995-09-01

This report describes laboratory experiments performed during 1986-1990 designed to produce empirical leach rate data for cladding removal waste (CRW) grout. At the completion of the laboratory work, funding was not available for report completion, and only now during final grout closeout activities is the report published. The leach rates serve as inputs to computer codes used in assessing the potential risk from the migration of waste species from disposed grout. This report discusses chemical analyses conducted on samples of CRW grout, and the results of geochemical computer code calculations that help identify mechanisms involved in the leaching process. Themore » semi-infinite solid diffusion model was selected as the most representative model for describing leaching of grouts. The use of this model with empirically derived leach constants yields conservative predictions of waste release rates, provided no significant changes occur in the grout leach processes over long time periods. The test methods included three types of leach tests--the American Nuclear Society (ANS) 16.1 intermittent solution exchange test, a static leach test, and a once-through flow column test. The synthetic CRW used in the tests was prepared in five batches using simulated liquid waste spiked with several radionuclides: iodine ({sup 125}I), carbon ({sup 14}C), technetium ({sup 99}Tc), cesium ({sup 137}Cs), strontium ({sup 85}Sr), americium ({sup 241}Am), and plutonium ({sup 238}Pu). The grout was formed by mixing the simulated liquid waste with dry blend containing Type I and Type II Portland cement, class F fly ash, Indian Red Pottery clay, and calcium hydroxide. The mixture was allowed to set and cure at room temperature in closed containers for at least 46 days before it was tested.« less

The pH-dependent contaminant leaching from the copper smelter fly ash and slag

NASA Astrophysics Data System (ADS)

Jarosikova, Alice; Ettler, Vojtech; Mihaljevic, Martin; Penizek, Vit

2014-05-01

Metallurgical wastes produced during smelting processes represent a potential risk of environmental contamination, depending particularly on the content and mobility of the elements contained. Due to leaching, serious environmental impact especially in contaminated soil systems in the vicinity of the smelting plants may occur. In this respect two potentially hazardous metallurgical wastes from the copper smelter Tsumeb (Namibia, Africa) were investigated by laboratory leaching experiments. The leaching behaviours of (i) Ausmelt slag from Cu smelting (9500 ppm As, 24000 ppm Cu, 10200 ppm Pb, 24500 ppm Zn; mineralogy: glass, fayalite, spinel, metallic/sulphide droplets) and (ii) fly ash from Cu smelter bag house filters (43.7 wt% As, 13000 ppm Cu, 39700 ppm Pb, 20000 ppm Zn; mineralogy: arsenolite, galena, gypsum, litharge, anglesite) were studied using a 48-h pH-static leaching test (CEN/TS 14997). The release of metals/metalloids at a range of pH 3-12, investigation of changes in mineralogical composition and PHREEQC speciation-solubility modelling were used to understand processes governing the contaminant leaching from these waste materials. It was observed that the contaminant leaching was highly pH-dependent. The release of metals from slag corresponded to "L-type" leaching curve with Cu being the key contaminant leached (up to 1780 mg/kg). In contrast, As was highly leached also in alkaline conditions (31-173 mg/kg) and significantly exceeded the limit value for hazardous waste materials in all cases (25 mg/kg). Fly ash was found to be extremely reactive in terms of the As release with a "J-type" leaching curve indicating the highest leaching at pH of 11 and 12 (up to 314 g/kg). Arsenic was considered to be the most important contaminant for both waste materials and its release can represent a risk for the environment, especially in case, where the fly ash- or slag-derived particulates are deposited into the soil systems. This study was supported by the Czech Science Foundation (projects no. 13-17501S and P210/12/1413) and IGCP project no. 594.

Potential for leaching of arsenic from excavated rock after different drying treatments.

PubMed

Li, Jining; Kosugi, Tomoya; Riya, Shohei; Hashimoto, Yohey; Hou, Hong; Terada, Akihiko; Hosomi, Masaaki

2016-07-01

Leaching of arsenic (As) from excavated rock subjected to different drying methods is compared using sequential leaching tests and rapid small-scale column tests combined with a sequential extraction procedure. Although the total As content in the rock was low (8.81 mg kg(-1)), its resulting concentration in the leachate when leached at a liquid-to-solid ratio of 10 L kg(-1) exceeded the environmental standard (10 μg L(-1)). As existed mainly in dissolved forms in the leachates. All of the drying procedures applied in this study increased the leaching of As, with freeze-drying leading to the largest increase. Water extraction of As using the two tests showed different leaching behaviors as a function of the liquid-to-solid ratio, and achieved average extractions of up to 35.7% and 25.8% total As, respectively. Dissolution of As from the mineral surfaces and subsequent re-adsorption controlled the short-term release of As; dissolution of Fe, Al, and dissolved organic carbon played important roles in long-term As leaching. Results of the sequential extraction procedure showed that use of 0.05 M (NH4)2SO4 underestimates the readily soluble As. Long-term water extraction removed almost all of the non-specifically sorbed As and most of the specifically sorbed As. The concept of pollution potential indices, which are easily determined by the sequential leaching test, is proposed in this study and is considered for possible use in assessing efficacy of treatment of excavated rocks. Copyright © 2016 Elsevier Ltd. All rights reserved.

Bioleaching of rare earth elements from waste phosphors and cracking catalysts

DOE Office of Scientific and Technical Information (OSTI.GOV)

Reed, David W.; Fujita, Yoshiko; Daubaras, Dayna L.

Four microbial cultures were evaluated for organic acid production and their potential utility for leaching of rare earth elements (REE) from retorted phosphor powder (RPP) and spent fluidized cracking catalyst (FCC). Three of the cultures (2 bacterial, 1 fungal) were isolated from environmental and industrial materials known to contain rare earth elements. The other was the well-known and industrially important bacterium Gluconobacter oxydans. Gluconic acid was the predominant identified organic acid produced by all of the cultures; citric and acetic acid were among the other acids detected. There was also maximum REE leaching by cell free culture supernatants obtained withmore » Gluconobacter and the FCC; 49% of total REE was recovered, with preferential recovery of lanthanum over cerium. The phosphor powder was more difficult to leach; only ~2 % total REE was leached from RPP with Gluconobacter. Tests with the RPP indicated that the extent of REE solubilization was similar whether whole cell cultures or cell-free supernatants were used. However, Gluconobacter cell-free culture supernatants with 10-15 mM gluconic acid outperformed abiotically prepared leaching solutions with 30 mM gluconic acid concentrations. Abiotic tests showed that increasing gluconic acid concentrations increased leaching efficiency; for example, total REE leaching from FCC increased from 24 to 36 to 45% when gluconic acid was increased from 10 to 30 to 90 mM. Our research shows that utilizing microorganisms that produce gluconic acid can result in effective leaching of REE from waste materials, and optimizing gluconic acid production will improve recovery.« less

Bioleaching of rare earth elements from waste phosphors and cracking catalysts

DOE PAGES

Reed, David W.; Fujita, Yoshiko; Daubaras, Dayna L.; ...

2016-08-22

Four microbial cultures were evaluated for organic acid production and their potential utility for leaching of rare earth elements (REE) from retorted phosphor powder (RPP) and spent fluidized cracking catalyst (FCC). Three of the cultures (2 bacterial, 1 fungal) were isolated from environmental and industrial materials known to contain rare earth elements. The other was the well-known and industrially important bacterium Gluconobacter oxydans. Gluconic acid was the predominant identified organic acid produced by all of the cultures; citric and acetic acid were among the other acids detected. There was also maximum REE leaching by cell free culture supernatants obtained withmore » Gluconobacter and the FCC; 49% of total REE was recovered, with preferential recovery of lanthanum over cerium. The phosphor powder was more difficult to leach; only ~2 % total REE was leached from RPP with Gluconobacter. Tests with the RPP indicated that the extent of REE solubilization was similar whether whole cell cultures or cell-free supernatants were used. However, Gluconobacter cell-free culture supernatants with 10-15 mM gluconic acid outperformed abiotically prepared leaching solutions with 30 mM gluconic acid concentrations. Abiotic tests showed that increasing gluconic acid concentrations increased leaching efficiency; for example, total REE leaching from FCC increased from 24 to 36 to 45% when gluconic acid was increased from 10 to 30 to 90 mM. Our research shows that utilizing microorganisms that produce gluconic acid can result in effective leaching of REE from waste materials, and optimizing gluconic acid production will improve recovery.« less

Leaching characteristics of rare metal elements and chlorine in fly ash from ash melting plants for metal recovery.

PubMed

Jung, Chang-Hwan; Osako, Masahiro

2009-05-01

In terms of resource recovery and environmental impact, melting furnace fly ash (MFA) is attracting much attention in Japan due to its high metal content. The study aims to obtain fundamental information on using a water extraction method not only to concentrate valuable rare metals but also to remove undesirable substances such as chlorine for their recovery from MFA. The composition and leaching characteristics of MFA was investigated. The results revealed that the metal content in MFA is nearly equal to raw ore quality. The content of Ag, In, Pd, Pb, and Zn is, in fact, higher than the content of raw ore. As for leaching behavior, Ag, Bi, In, Ga, Ge, Sb, Sn, and Te showed the lowest release at a neutral pH range. Pd was leached constantly regardless of pH, but its concentration was quite low. On the other hand, most of the Tl was easily leached, revealing that water extraction is not appropriate for Tl recovery from MFA. Major elements Cl, Ca, Na, and K, occupying about 70% of MFA, were mostly leached regardless of pH. Base metal elements Cu, Pb, and Zn showed minimum solubility at a neutral pH. The leaching ratio of target rare metal elements and base metal elements suggests that the optimal pH for water extraction is 8-10, at which the leaching concentration is minimized. The water extraction process removed most of the Cl, Ca, Na, and K, and the concentration of rare metals and base metals increased by four or five times.

Column Experiments to Interpret Weathering in Columbia Hills

NASA Technical Reports Server (NTRS)

Hausrath, E. M.; Morris, R.V.; Ming, D.W.; Golden, D.C.; Galindo, C.; Sutter, B.

2009-01-01

Phosphate mobility has been postulated as an indicator of early aqueous activity on Mars. In addition, rock surfaces analyzed by the Mars Exploration Rover Spirit are consistent with the loss of a phosphate- containing mineral To interpret phosphate alteration behavior on Mars, we performed column dissolution experiments leaching the primary phases Durango fluorapatite, San Carlos olivine, and basalt glass (Stapafjell Volcano, courtesy of S. Gislason, University of Iceland) [3,4]) with acidic solutions. These phases were chosen to represent quickly dissolving phases likely present in Columbia Hills. Column dissolution experiments are closer to natural dissolution conditions than batch experiments, although they can be difficult to interpret. Acidic solutions were used because the leached layers on the surfaces of these rocks have been interpreted as resulting from acid solutions [5].

An active dealkalization of red mud with roasting and water leaching.

PubMed

Zhu, Xiaobo; Li, Wang; Guan, Xuemao

2015-04-09

The research has focused on the dealkalization of red mud after active roasting and water leaching, which is obtained from bauxite during alumina production. The main factors such as roasting temperature, roasting time, water leaching stage, leaching temperature, leaching reaction time and liquid to solid ratio were investigated. The mechanism of dealkalization was in-depth studied by using ICP-AES, XRD, TG-DSC, SEM-EDS and leaching kinetic. The results show that the dealkalization rate reached 82% under the condition of roasting temperature of 700 °C, roasting time of 30 min, four stage water leaching, liquid to solid ratio of 7 mL/g, leaching temperature of 90 °C and reaction time of 60 min. The diffraction peak of Na6CaAl6Si6(CO3)O24 · 2H2O in red mud was decreased during the active roasting process, whereas the mineral phases of NaOH · H2O and Na2Ca(CO3)2 were appeared. The content of alkali obviously decreased and the grade of other elements increased during the process of active roasting and water leaching, which was in favor of next application process of red mud. The water leaching was controlled by internal diffusion of SCM and the apparent activation energy was 22.63 kJ/mol. Copyright © 2014 Elsevier B.V. All rights reserved.

Fradkin-Bacry-Ruegg-Souriau perihelion vector for Gorringe-Leach equations

NASA Astrophysics Data System (ADS)

Grandati, Yves; Bérard, Alain; Mohrbach, Hervé

2010-02-01

We show that every generalized Gorringe-Leach equation admits an associated Fradkin-Bacry-Ruegg-Souriau’s vector which, in general, is only a piecewise conserved quantity. In the case of dualizable generalized Gorringe-Leach equations, which include the case of conservative motions in central power law potentials, the image sets of the FBRS vectors for dual classes are dual images of each other.

About microcracking due to leaching in cementitious composites: X-ray microtomography description and numerical approach

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rougelot, Thomas; Burlion, Nicolas, E-mail: nicolas.burlion@polytech-lille.f; Bernard, Dominique

2010-02-15

Chemical shock of cement based materials leads to significant degradation of their physical properties. A typical scenario is a calcium leaching due to water (water with very low pH compared with that of pore fluid). The main objective of this paper is to evaluate the evolution of microstructure induced by leaching of a cementitious composite using synchrotron X-ray micro tomography, mainly from an experimental point of view. In this particular case, it was possible to identify cracking induced by leaching. After a description of the degradation mechanism and the X-ray synchrotron microtomographic analysis, numerical simulations are performed in order tomore » show that cracking is induced by an initial pre-stressing of the composite, coupled with decalcification shrinkage and dramatic decrease in tensile strength during leaching. X-ray microtomography analysis allowed to make evidence of an induced microcracking in cementitious material submitted to leaching.« less

Study on optimum technological conditions of ore sintering flue gas desulfurization by using poor manganese

NASA Astrophysics Data System (ADS)

Li, H. Y.; Li, S. E.; Long, Z. G.; Wu, F. Z.; Cui, T. M.; Zhou, X. Z.

2017-11-01

Orthogonal experiments were conducted to study the effect of each single factor on the desulfurization rate and leaching rate of Mn2+ to obtain improved process parameters. The results showed that the use of pyrolusite flue gas and the process method of by-product MnSO4 can not only effectively remove the sulfur in the gas, thereby controlling environmental pollution, but can also recover sulfur.

Leaching behavior and chemical stability of copper butyl xanthate complex under acidic conditions.

PubMed

Chang, Yi Kuo; Chang, Juu En; Chiang, Li Choung

2003-08-01

Although xanthate addition can be used for treating copper-containing wastewater, a better understanding of the leaching toxicity and the stability characteristics of the copper xanthate complexes formed is essential. This work was undertaken to evaluate the leaching behavior of copper xanthate complex precipitates by means of toxicity characteristics leaching procedure (TCLP) and semi-dynamic leaching test (SDLT) using 1 N acetic acid solution as the leachant. Also, the chemical stability of the copper xanthate complex during extraction has been examined with the studying of variation of chemical structure using UV-vis, Fourier transform infrared and X-ray photoelectron spectroscopies (XPS). Both TCLP and SDLT results showed that a negligible amount of copper ion was leached out from the copper xanthate complex precipitate, indicating that the complex exhibited a high degree of copper leaching stability under acidic conditions. Nevertheless, chemical structure of the copper xanthate complex precipitate varied during the leaching tests. XPS data suggested that the copper xanthate complex initially contained both cupric and cuprous xanthate, but the unstable cupric xanthate change to the cuprous form after acid extraction, indicating the cuprous xanthate to be the final stabilizing structure. Despite that, the changes of chemical structure did not induce the rapid leaching of copper from the copper xanthate complex.

Study of experiment on leaching of bisphenol A from infant books to artificial saliva.

PubMed

Sajiki, Junko; Yanagibori, Ryoko; Kobayashi, Yaeko

2010-05-01

To assess the risk of bisphenol A (BPA) exposure when infants suck or chew infant books, the concentration of BPA leaching from infant books published by Japanese makers to artificial saliva was measured. The concentration of BPA leaching from 10 infant books to 15 ml artificial saliva or water was measured at 37 degrees C for 20 hrs. BPA concentration was measured by high-performance liquid chromatography-electrochemical detection (HPLC-ECD) with solid-phase extraction. BPA was leached from all books when pieces of them were dipped both into saliva and water for 20 hrs. The highest concentration of BPA leaching from one out of 10 books was 43.4 ng/ml (for 2 hrs) in saliva, which was estimated to be approximately 0.052 mg/kg body weight/day for infants aged 6-10 months. As BPA has endocrine-disrupting effects and poses higher risks in infants than in adults, it is desired to reduce BPA use in the printing of infant books from the viewpoint of child health.

Multistage leaching of metals from spent lithium ion battery waste using electrochemically generated acidic lixiviant.

PubMed

Boxall, N J; Adamek, N; Cheng, K Y; Haque, N; Bruckard, W; Kaksonen, A H

2018-04-01

Lithium ion battery (LIB) waste contains significant valuable resources that could be recovered and reused to manufacture new products. This study aimed to develop an alternative process for extracting metals from LIB waste using acidic solutions generated by electrolysis for leaching. Results showed that solutions generated by electrolysis of 0.5 M NaCl at 8 V with graphite or mixed metal oxide (MMO) electrodes were weakly acidic and leach yields obtained under single stage (batch) leaching were poor (<10%). This was due to the highly acid-consuming nature of the battery waste. Multistage leaching with the graphite electrolyte solution improved leach yields overall, but the electrodes corroded over time. Though yields obtained with both electrolyte leach solutions were low when compared to the 4 M HCl control, there still remains potential to optimise the conditions for the generation of the acidic anolyte solution and the solubilisation of valuable metals from the LIB waste. A preliminary value proposition indicated that the process has the potential to be economically feasible if leach yields can be improved, especially based on the value of recoverable cobalt and lithium. Copyright © 2018 Elsevier Ltd. All rights reserved.

A comparison of ultrasound-augmented and conventional leaching of silver from sintering dust using acidic thiourea.

PubMed

Chang, Jun; Zhang, Er-Dong; Zhang, Li-Bo; Peng, Jin-Hui; Zhou, Jun-Wen; Srinivasakannan, C; Yang, Chang-Jiang

2017-01-01

In the process of steel manufacture, up to ten millions of tons of sintering dust (SD) are produced annually in China, which contain noble metals such as Ag. Therefore, recovery of silver (Ag) from SD could be a potential economic and environmental activity. The purpose of this article is to generate information about reaction kinetics of silver leaching with thiourea from SD, comparing the conventional and ultrasonic-augment leaching. The effects of various control parameters such as the ultrasound power, particle size, leaching temperature and thiourea concentration on leaching rate of silver were studied. The results showed 89% silver recovery for conventional process against 95% for ultrasound assisted leaching. The ultrasonic wave increased the leaching rate and shorten the reaction time. The rate controlling step was analyzed using shrinking core model and the rate controlling step is identified to be the diffusion through the product layer in both conventional and ultrasonic-augment leaching processes. The activation energies were estimated to be 28.01kJ/mol and 18.19kJ/mol, and the reaction order were 0.89 and 0.71, respectively. Copyright © 2016 Elsevier B.V. All rights reserved.

Evaluation of six pesticides leaching indexes using field data of herbicide application in Casablanca Valley, Chile.

PubMed

Kogan, M; Rojas, S; Gómez, P; Suárez, F; Muñoz, J F; Alister, C

2007-01-01

A field study was performed to evaluate the accuracy of six pesticide screening leaching indexes for herbicide movement. Adsorption, dissipation and soil movement were studied in a vineyard in a sandy loam soil during 2005 season. Simazine, diuron, pendimethalin, oxyfluorfen and flumioxazin were applied to bare soil at rates commonly used, and their soil concentrations throughout soil profile were determined at 0, 10, 20, 40 and 90 days after application (DAA). Herbicides were subjected to two pluviometric regimens, natural field condition and modified conditions (plus natural rainfall 180 mm). Leaching indexes utilized were: Briggs's Rf, Hamaker's Rf, LEACH, LPI, GUS and LIX. Simazine reached 120 cm, diuron 90 cm, flumioxazin 30 cm soil depth respectively. Pendimethalin and oxyfluorfen were retained up to 5 cm. None of the herbicides leaching was affected by rainfall regimen. Only flumioxazin field dissipation was clearly affected by pluviometric condition. The best representation of the herbicide soil depth movement and leaching below 15 cm soil depth were: Hamaker's Rf < Briggs's Rf < GUS < LPI, < LEACH < LIX. Field results showed a good correlation between herbicides K(d) and their soil depth movement and mass leached below 15 cm soil depth.

Co-treatment of spent cathode carbon in caustic and acid leaching process under ultrasonic assisted for preparation of SiC.

PubMed

Yuan, Jie; Xiao, Jin; Li, Fachuang; Wang, Bingjie; Yao, Zhen; Yu, Bailie; Zhang, Liuyun

2018-03-01

Spent cathode carbon (SCC) from aluminum electrolysis has been treated in ultrasonic-assisted caustic leaching and acid leaching process, and purified SCC used as carbon source to synthesize silicon carbide (SiC) was investigated. Chemical and mineralogical properties have been characterized by X-ray diffraction (XRD), X-ray fluorescence (XRF), scanning electron microscopy (SEM), and thermogravimetry and differential scanning calorimetry (TGA-DSC). Various experimental factors temperature, time, liquid-solid ratio, ultrasonic power, and initial concentration of alkali or acid affecting on SCC leaching result were studied. After co-treatment with ultrasonic-assisted caustic leaching and acid leaching, carbon content of leaching residue was 97.53%. SiC power was synthesized by carbothermal reduction at 1600 °C, as a result of yield of 76.43%, and specific surface area of 4378 cm 2 /g. This is the first report of using purified SCC and gangue to prepare SiC. The two industrial wastes have been used newly as secondary sources. Furthermore, ultrasonic showed significant effect in SCC leaching process. Copyright © 2017 Elsevier B.V. All rights reserved.

Removal of hazardous metals from MSW fly ash--an evaluation of ash leaching methods.

PubMed

Fedje, Karin Karlfeldt; Ekberg, Christian; Skarnemark, Gunnar; Steenari, Britt-Marie

2010-01-15

Incineration is a commonly applied management method for municipal solid waste (MSW). However, significant amounts of potentially hazardous metal species are present in the resulting ash, and these may be leached into the environment. A common idea for cleaning the ash is to use enhanced leaching with strong mineral acids. However, due to the alkalinity of the ash, large amounts of acid are needed and this is a drawback. Therefore, this work was undertaken in order to investigate some alternative leaching media (EDTA, ammonium nitrate, ammonium chloride and a number of organic acids) and to compare them with the usual mineral acids and water. All leaching methods gave a significant increase in ash specific surface area due to removal of soluble bulk (matrix) compounds, such as CaCO(3) and alkali metal chlorides. The use of mineral acids and EDTA mobilised many elements, especially Cu, Zn and Pb, whereas the organic acids generally were not very effective as leaching agents for metals. Leaching using NH(4)NO(3) was especially effective for the release of Cu. The results show that washing of MSW filter ash with alternative leaching agents is a possible way to remove hazardous metals from MSW fly ash.

The influence of ZnO incorporation on the aqueous leaching characteristics of a borosilicate glass

NASA Astrophysics Data System (ADS)

Vance, E. R.; Gregg, D. J.; Karatchevtseva, I.; Griffiths, G. J.; Olufson, K.; Rees, Gregory J.; Hanna, John V.

2017-10-01

With increasing ZnO content, short term aqueous durability enhancement of all elements in borosilicate glasses containing 1.0 and 3.85 wt% ZnO was evident in 7-day PCT-B tests. In 14-day MCC-1 type leach tests conducted at 90 °C, surface alteration was very clear in the undoped glass via the formation of strongly altered amorphous material which tended to spall off the surface. No sign of crystallinity was detected by grazing incidence X-ray diffraction or electron microscopy of the surface layers and the surface material was very rich in silica. For the ZnO-bearing glasses, significant growth of particles following PCT leaching for 7 days was observed, due to a build-up of surface ZnO-containing Si-rich material and possible agglomeration. This alteration layer was also observed in MCC-1 type experiments in which cross-section SEM-EDS data were obtained. Raman, infrared and 11B and 29Si MAS NMR spectroscopy showed only slight changes in boron speciation on the addition of up to 9.1 wt% ZnO. Bulk positron annihilation lifetime spectra (PALS) of glasses containing 0-3.85 wt% ZnO could be analysed with three distinct lifetimes and also showed only slight differences. These results indicate that the basic glass structure was essentially not influenced by the ZnO content and that the passivation of the alteration layer is promoted by ZnO content.

Simultaneous leaching of arsenite, arsenate, selenite and selenate, and their migration in tunnel-excavated sedimentary rocks: II. Kinetic and reactive transport modeling.

PubMed

Tabelin, Carlito Baltazar; Sasaki, Ryosuke; Igarashi, Toshifumi; Park, Ilhwan; Tamoto, Shuichi; Arima, Takahiko; Ito, Mayumi; Hiroyoshi, Naoki

2017-12-01

Predicting the fates of arsenic (As) and selenium (Se) in natural geologic media like rocks and soils necessitates the understanding of how their various oxyanionic species behave and migrate under dynamic conditions. In this study, geochemical factors and processes crucial in the leaching and transport of arsenite (As III ), arsenate (As V ), selenite (Se IV ) and selenate (Se VI ) in tunnel-excavated rocks of marine origin were investigated using microscopic/extraction techniques, column experiments, dissolution-precipitation kinetics and one-dimensional reactive transport modeling. The results showed that evaporite salts were important because aside from containing As and Se, they played crucial roles in the evolution of pH and concentrations of coexisting ions, both of which had strong effects on adsorption-desorption reactions of As and Se species with iron oxyhydroxide minerals/phases. The observed leaching trends of As V , As III , Se IV and Se VI were satisfactorily simulated by one-dimensional reactive transport models, which predict that preferential adsorptions of As V and Se IV were magnified by geochemical changes in the columns due to water flow. Moreover, our results showed that migrations of As III , Se IV and Se VI could be predicted adequately by 1D solute transport with simple activity-K' d approach, but surface complexation was more reliable to simulate adsorption-desorption behavior of As V . Copyright © 2017 Elsevier Ltd. All rights reserved.

Recycling of electronic waste: Printed wiring boards

NASA Astrophysics Data System (ADS)

Luyima, Alex

Pyrolysis and leaching are the dominant techniques applied in the recycling of waste printed wiring boards (PWBs). Waste PWB pyrolysis is a highly polluting technology and produces brominated pyrolysis oils in addition to hydrogen bromide (HBr) gas. Moreover, leaching as a treatment process of waste PWBs is not well investigated. In this work, the pyrolysis of waste PWBs has been studied with the aim of reducing the amount of brominated oils and HBr gas evolved. The effects of powder inorganic chemicals (CaO, CaCO3, Fe 2O3, Al2O3, Y-Zeolite, and ZSM-5) additions on the pyrolysis of waste PWBs has been studied through experiments using a thermogravimetric-differential thermal analyzer connected to a mass spectrometer (TG-DTA-MS) and in a tube furnace at 900 °C. It has been shown that the kinetic models by Friedman, Flynn-Wall-Ozawa, and Kissinger are applicable to waste PWB pyrolysis at temperatures below 400 °C. Moreover, CaO, CaCO3, Fe2O3, Y-Zeolite, and ZSM-5 show a potential to reduce the amount of HBr gas evolved during pyrolysis in TG-DTA-MS. However, in the tube furnace pyrolysis experiments, CaO and CaCO3 were found to be the most effective chemical additions, with more than 90% reduction in total bromine (HBr and other brominated gases) evolved. It has also been demonstrated that the sequential leaching of waste PWBs with hydrochloric acid, nitric acid and aqua regia is capable of selective recovery of base and precious metals contained in waste PWBs.

Nitrate transport and transformation processes in unsaturated porous media

USGS Publications Warehouse

Tindall, James A.; Petrusak, Robin L.; McMahon, Peter B.

1995-01-01

A series of experiments was conducted on two contrasting agricultural soils to observe the influence of soil texture, preferential flow, and plants on nitrate transport and denitrification under unsaturated conditions. Calcium nitrate fertilizer was applied to the surface of four large undisturbed soil cores (30 cm diameter by 40 cm height). Two of the cores were a structured clay obtained from central Missouri and two were an unstructured fine sand obtained from central Florida. The cores were irrigated daily and maintained at a matric potential of -20 kPa, representative of soil tension in the rooting zone of irrigated agricultural fields. Volumetric water content (θ), concentration of nitrate-N in the soil solution, and nitrous oxide flux at the surface, 10, 20, and 30 cm were monitored daily. Leaching loss of surface-applied N03− -N was significant in both the sand and the clay. In unplanted sand cores, almost all of the applied nitrate was leached below 30 cm within 10 days. Gaseous N loss owing to denitrification was no greater than 2% of the nitrate-N applied to the unplanted sand cores and, in general, was less than 1 %. Although leaching was somewhat retarded in the clay cores, about 60% of the applied nitrate-N was leached from the unplanted clay soil in 5–6 weeks. Under unsaturated conditions, the clay had little to no tendency to denitrify despite the greater moisture content of the clay and retarded leaching of nitrate in the clay. The planted sand cores had surprisingly large gaseous N loss owing to denitrification, as much as 17% of the nitrate-N. Results from both the clay and sand experiments show that the dynamics of nitrate transport and transformation in unsaturated soils are affected by small, localized variations in the soil moisture content profile, the gaseous diffusion coefficient of the soil, the rate at which the nitrate pulse passes through the soil, the solubility of N2O and N2 and the diffusion of the gasses through the soil solution, and development of a water content profile in the soil. Limited dentrification in the clay soil was due to a limited volume of soil available for infiltration after internal catchment and the development of denitrifying conditions resulting from the presence of an extensive macropore system.

Can nitrate contaminated groundwater be remediated by optimizing flood irrigation rate with high nitrate water in a desert oasis using the WHCNS model?

PubMed

Liang, Hao; Qi, Zhiming; Hu, Kelin; Prasher, Shiv O; Zhang, Yuanpei

2016-10-01

Nitrate contamination of groundwater is an environmental concern in intensively cultivated desert oases where this polluted groundwater is in turn used as a major irrigation water resource. However, nitrate fluxes from root zone to groundwater are difficult to monitor in this complex system. The objectives of this study were to validate and apply the WHCNS (soil Water Heat Carbon Nitrogen Simulator) model to simulate water drainage and nitrate leaching under different irrigation and nitrogen (N) management practices, and to assess the utilization of groundwater nitrate as an approach to remediate nitrate contaminated groundwater while maintain crop yield. A two-year field experiment was conducted in a corn field irrigated with high nitrate groundwater (20 mg N L(-1)) in Alxa, Inner Mongolia, China. The experiment consisted of two irrigation treatments (Istd, standard, 750 mm per season; Icsv, conservation, 570 mm per season) factorially combined with two N fertilization treatments (Nstd, standard, 138 kg ha(-1); Ncsv, conservation, 92 kg ha(-1)). The validated results showed that the WHCNS model simulated values of crop dry matter, yield, soil water content and soil N concentration in soil profile all agreed well with the observed values. Compared to the standard water management (Istd), the simulated drainage and nitrate leaching decreased about 65% and 59%, respectively, under the conservation water management (Icsv). Nearly 55% of input N was lost by leaching under the IstdNstd and IstdNcsv treatments, compared to only 26% under the IcsvNstd and IcsvNcsv treatments. Simulations with more than 240 scenarios combing different levels of irrigation and fertilization indicated that irrigation was the main reason leading to the high risk of nitrate leaching, and the nitrate in irrigation groundwater can be best utilized without corn yield loss when the total irrigation was reduced from the current 750 mm to 491 mm. This reduced irrigation rate facilitated the use of approximately 42 kg N ha(-1) yr(-1) of nitrate from groundwater, which would gradually improve the groundwater quality. Future field studies on nitrate leaching in this area are suggested to investigate water and N dynamics under irrigation rates near 490 mm per season. Copyright © 2016 Elsevier Ltd. All rights reserved.

Leaching behavior of copper from waste printed circuit boards with Brønsted acidic ionic liquid

DOE Office of Scientific and Technical Information (OSTI.GOV)

Huang, Jinxiu; Chen, Mengjun, E-mail: kyling@swust.edu.cn; Chen, Haiyan

2014-02-15

Highlights: • A Brønsted acidic ILs was used to leach Cu from WPCBs for the first time. • The particle size of WPCBs has significant influence on Cu leaching rate. • Cu leaching rate was higher than 99% under the optimum leaching conditions. • The leaching process can be modeled with shrinking core model, and the E{sub a} was 25.36 kJ/mol. - Abstract: In this work, a Brønsted acidic ionic liquid, 1-butyl-3-methyl-imidazolium hydrogen sulfate ([bmim]HSO{sub 4}), was used to leach copper from waste printed circuit boards (WPCBs, mounted with electronic components) for the first time, and the leaching behavior ofmore » copper was discussed in detail. The results showed that after the pre-treatment, the metal distributions were different with the particle size: Cu, Zn and Al increased with the increasing particle size; while Ni, Sn and Pb were in the contrary. And the particle size has significant influence on copper leaching rate. Copper leaching rate was higher than 99%, almost 100%, when 1 g WPCBs powder was leached under the optimum conditions: particle size of 0.1–0.25 mm, 25 mL 80% (v/v) ionic liquid, 10 mL 30% hydrogen peroxide, solid/liquid ratio of 1/25, 70 °C and 2 h. Copper leaching by [bmim]HSO{sub 4} can be modeled with the shrinking core model, controlled by diffusion through a solid product layer, and the kinetic apparent activation energy has been calculated to be 25.36 kJ/mol.« less

Leaching and geochemical behavior of fired bricks containing coal wastes.

PubMed

Taha, Yassine; Benzaazoua, Mostafa; Edahbi, Mohamed; Mansori, Mohammed; Hakkou, Rachid

2018-03-01

High amounts of mine wastes are continuously produced by the mining industry all over the world. Recycling possibility of some wastes in fired brick making has been investigated and showed promising results. However, little attention is given to the leaching behavior of mine wastes based fired bricks. The objective of this paper is to evaluate the geochemical behavior of fired bricks containing different types of coal wastes. The leachates were analyzed for their concentration of As, Ba, Cd, Co, Cr, Cu, Mo, Ni, Pb, Zn and sulfates using different leaching tests; namely Tank Leaching tests (NEN 7375), Toxicity Characteristic Leaching Procedure (TCLP) and pH dependence test (EPA, 1313). The results showed that the release of constituents of potential interest was highly reduced after thermal treatment and were immobilized within the glassy matrix of the fired bricks. Moreover, it was also highlighted that the final pH of all fired samples changed and stabilized around 8-8.5 when the initial pH of leaching solution was in the range 2.5-11.5. The release of heavy metals and metalloids (As) tended to decrease with the increase of pH from acidic to alkaline solutions while Mo displayed a different trend. Copyright © 2017 Elsevier Ltd. All rights reserved.

Automobile shredded residue valorisation by hydrometallurgical metal recovery.

PubMed

Granata, Giuseppe; Moscardini, Emanuela; Furlani, Giuliana; Pagnanelli, Francesca; Toro, Luigi

2011-01-15

The aim of this work was developing a hydrometallurgical process to recover metals from automobile shredded residue (or car fluff). Automobile shredded residue (ASR) was characterised by particle size distribution, total metal content and metal speciation in order to guide the choice of target metals and the operating conditions of leaching. Characterisation results showed that Fe is the most abundant metal in the waste, while Zn was the second abundant metal in the fraction with diameter lower than 500 μm. Sequential extractions denoted that Zn was easily extractable by weak acid attack, while Fe and Al required a strong acid attack to be removed. In order to recover zinc from <500 μm fraction leaching tests were operated using acetic acid, sulphuric acid and sodium hydroxide at different concentrations. Sulphuric acid determined the highest zinc extraction yield, while acetic acid determined the highest zinc extractive selectivity. Sodium hydroxide promoted an intermediate situation between sulphuric and acetic acid. Zn recovery by electro winning using acetic leach liquor determined 95% of Zn electro deposition yield in 1h, while using sulphuric leach liquor 40% yield in 1h and 50% yield in 2h were obtained. Simulation results showed that the sulphuric leaching process was more attractive than acetic leaching process. Copyright © 2010 Elsevier B.V. All rights reserved.

Numerical simulation of trace element transport on subsurface environment pollution in coal mine spoil.

PubMed

Qiang, Xue; Bing, Liang; Hui-yun, Wang; Lei, Liu

2006-01-01

An understanding of the dynamic behavior of trace elements leaching from coal mine spoil is important in predicting the groundwater quality. The relationship between trace element concentrations and leaching times, pH values of the media is studied. Column leaching tests conducted in the laboratory showed that there was a close correlation between pH value and trace element concentrations. The longer the leaching time, the higher the trace element concentrations. Different trace elements are differently affected by pH values of leaching media. A numerical model for water flow and trace element transport has been developed based on analyzing the characteristics of migration and transformation of trace elements leached from coal mine spoil. Solutions to the coupled model are accomplished by Eulerian-Lagrangian localized adjoint method. Numerical simulation shows that rainfall intensity determined maximum leaching depth. As rainfall intensity is 3.6ml/s, the outflow concentrations indicate a breakthrough of trace elements beyond the column base, with peak concentration at 90cm depth. And the subsurface pollution range has a trend of increase with time. The model simulations are compared to experimental results of trace element concentrations, with reasonable agreement between them. The analysis and modeling of trace elements suggested that the infiltration of rainwater through the mine spoil might lead to potential groundwater pollution. It provides theoretical evidence for quantitative assessment soil-water quality of trace element transport on environment pollution.

Influence of moisture content and temperature on degree of carbonation and the effect on Cu and Cr leaching from incineration bottom ash.

PubMed

Lin, Wenlin Yvonne; Heng, Kim Soon; Sun, Xiaolong; Wang, Jing-Yuan

2015-09-01

This study investigated the influence of moisture content and temperature on the degree of carbonation of municipal solid waste (MSW) incineration bottom ash (IBA) from two different incineration plants in Singapore. The initial rate of carbonation was affected by the nominal moisture content used. Carbonation temperature seemed to play a part in changing the actual moisture content of IBA during carbonation, which in turn affected the degree of carbonation. Results showed that 2h of carbonation was sufficient for the samples to reach a relatively high degree of carbonation that was close to the degree of carbonation observed after 1week of carbonation. Both Cu and Cr leaching also showed significant reduction after only 2h of carbonation. Therefore, the optimum moisture content and temperature were selected based on 2h of carbonation. The optimum moisture content was 15% for both incineration plants while the optimum temperature was different for the two incineration plants, at 35°C and 50°C. The effect on Cu and Cr leaching from IBA after accelerated carbonation was evaluated as a function of carbonation time. Correlation coefficient, Pearson's R, was used to determine the dominant leaching mechanism. The reduction in Cu leaching was found to be contributed by both formation of carbonate mineral and reduction of DOC leaching. On the other hand, Cr leaching seemed to be dominantly controlled by pH. Copyright © 2015 Elsevier Ltd. All rights reserved.

Analysis and interpretation of the leaching behaviour of waste thermal treatment bottom ash by batch and column tests.

PubMed

Di Gianfilippo, Martina; Costa, Giulia; Verginelli, Iason; Gavasci, Renato; Lombardi, Francesco

2016-10-01

This paper investigates the leaching behaviour of specific types of waste thermal treatment bottom ash (BA) as a function of both pH and the liquid-to-solid ratio (L/S). Specifically, column percolation tests and different types of batch tests (including pH-dependence) were applied to BA produced by hospital waste incineration (HW-I), Refuse Derived Fuel (RDF) gasification (RDF-G) and RDF incineration (RDF-I). The results of these tests were interpreted applying an integrated graphical and modelling approach aimed at identifying the main mechanisms (solubility, availability or time-controlled dissolution and diffusion) governing the release of specific constituents from each type of BA. The final aim of this work was in fact to gain insight on the information that can be provided by the leaching tests applied, and hence on which ones may be more suitable to apply for assessing the leaching concentrations expected in the field. The results of the leaching tests showed that the three samples of analysed BA presented differences of orders of magnitude in their leaching behaviour, especially as a function of pH, but also in terms of the L/S. These were mainly related to the differences in mineralogy of the samples. In addition, for the same type of bottom ash, the comparison between the results of batch and percolation column tests, expressed in terms of cumulative release, showed that for some constituents (e.g. Mg for HW-I BA and Cu for RDF-G BA) differences of over one order of magnitude were obtained due to variations in pH and DOC release. Similarly, the eluate concentrations observed in the percolation tests, for most of the investigated elements, were not directly comparable with the results of the pH-dependence tests. In particular, in some cases the percolation test results showed eluate concentrations of some constituents (e.g. K and Ca in HW-I BA) of up to one order of magnitude higher than the values obtained from the pH-dependence experiments at the same pH value. This was attributed to a rapid washout from the column of the soluble phases present in the BA. In contrast, for other constituents (e.g. Mg and Ba for the RDF-G BA), especially at high L/S ratios, the concentrations in the column tests were of up to one order of magnitude lower than the solubility value, indicating release under non-equilibrium conditions. In these cases, batch pH-dependence tests should be preferred, since column tests results could underestimate the concentrations expected in the field. Copyright © 2016 Elsevier Ltd. All rights reserved.

Contaminant Leach Testing of Hanford Tank 241-C-104 Residual Waste

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cantrell, Kirk J.; Snyder, Michelle M.V.; Wang, Guohui

2015-07-01

Leach testing of Tank C-104 residual waste was completed using batch and column experiments. Tank C-104 residual waste contains exceptionally high concentrations of uranium (i.e., as high as 115 mg/g or 11.5 wt.%). This study was conducted to provide data to develop contaminant release models for Tank C-104 residual waste and Tank C-104 residual waste that has been treated with lime to transform uranium in the waste to a highly insoluble calcium uranate (CaUO4) or similar phase. Three column leaching cases were investigated. In the first case, C-104 residual waste was leached with deionized water. In the second case, crushedmore » grout was added to the column so that deionized water contacted the grout prior to contacting the waste. In the third case, lime was mixed in with the grout. Results of the column experiments demonstrate that addition of lime dramatically reduces the leachability of uranium from Tank C-104 residual waste. Initial indications suggest that CaUO4 or a similar highly insoluble calcium rich uranium phase forms as a result of the lime addition. Additional work is needed to definitively identify the uranium phases that occur in the as received waste and the waste after the lime treatment.« less

Modelling the dissipation and leaching of two herbicides in decomposing mulch of crop residues

NASA Astrophysics Data System (ADS)

Aslam, Sohaib; Iqbal, Akhtar; Lafolie, François; Recous, Sylvie; Benoit, Pierre; Garnier, Patricia

2013-04-01

Conservation agricultural practices are increasingly adopted because of ecosystem services such as conservation of soil and water resources. These farming systems are characterized mainly by the presence of mulch made of residues of harvested or cover crops on soil surface. The mulch can intercept and retain applied pesticides depending on pesticide molecule and rainfall timing. The pesticide wash-off from mulch is considered a key process in pesticide fate and can have effects on degradation and transport processes. This work highlights a modelling approach to study the pesticide wash-off from mulch residues and their further transport in soil under two rainfall regimes. Transformation and leaching of two herbicides, s-metolachlor and glyphosate, was studied and simulated by Pastis-mulch model. A pesticide module describing pesticide degradation in mulch and soil was coupled to a transport model including a mulch module. The model was tested to simulate the pesticide dissipation, wash-off from mulch and further leaching in soil. Pesticide degradation parameters in mulch were estimated from incubation experiments with 14C-labelled molecules in small cylinders. The model was then tested using the data obtained through a soil column experiment (reconstructed soil cores :15 cm diameter x 35 cm depth), a mulch of Zea mais + Doliquos lablab and with two treatments varied by water regimes: i) frequent rain (temperate, twice a week) with week intensity (6 mm/hr); and ii) occasional rain (tropical, twice a month) with stronger intensity (20 mm/hr). Columns were incubated at 20 °C for 84 days to monitor soil water, C, N and pesticide dynamics. Model successfully simulated the experimental data of pesticide dissipation in mulch residues. Results showed that the rain regime affected more S-metolachlor than glyphosate behavior. The simulated results indicated also that the dynamics in mulch of the two molecules differed according to the rain treatment. Glyphosate showed a greater leaching from mulch than S-metolachlor because of its lower adsorption coefficients to organic mulch. Moreover, simulated results showed a much faster degradation of glyphosate but greater non-extractable residue formation for S-metolachlor. Keywords: Mulch; Pesticides; Transport; Degradation; Modeling; Pastis-mulch References Findeling, A., Garnier, P., Coppens, F., Lafolie, F., Recous, S., 2007. Modelling water, carbon and nitrogen dynamics in soil covered with decomposing mulch. European Journal of Soil Science 58, 196-206. Lashermes, G., Zhang, Y., Houot, S., Barriuso, E., Steyer, J.P., Patureau, D., Garnier, P., 2013. A model coupling organic carbon and organic pollutant dynamics during composting. Journal of Environmental Quality. In Press.

Characterization of Sumbawa manganese ore and recovery of manganese sulfate as leaching products

NASA Astrophysics Data System (ADS)

Kusumaningrum, Retno; Rahmani, Siti Astari; Widayatno, Wahyu Bambang; Wismogroho, Agus Sukarto; Nugroho, Dwi Wahyu; Maulana, Syahrizal; Rochman, Nurul Taufiqu; Amal, M. Ikhlasul

2018-05-01

The aims of this research were to study the leaching process of manganese ore which originated from Sumbawa, Indonesia and its characterization. A high grade Indonesian manganese ore from Sumbawa, West of Nusa Tenggara was characterized by X-Ray Fluorescence (XRF). The result showed composition of 78.8 % Mn, 17.77% Fe and the rest were trace elements such as Si, Co, Ti, Zn, V and Zr contents. X-Ray Diffraction analysis showed that the manganese ore was consisted of pyrolusite (MnO2), rhodonite (MnSiO3), rhodochrosite (MnCO3) and hematite (Fe2O3). Manganese ore was also analyzed by thermal analysis to observe their thermal decomposition character. In this study, sulphuric acid (H2SO4, 6 M) was deployed as leaching agent. The leaching process was performed at 90 °C for two hours with the addition of NH4OH to control pH. Recovery percentage of leaching process yielded of 87 % Mn extracted. The crystallization process result at heating temperature of 200 °C was confirmed by XRD as manganese sulfate.

Fluorescein Dye Penetration in Round Top Rhyolite (Hudspeth County, Texas, USA) to Reveal Micro-permeability and Optimize Grain Size for Heavy REE Heap Leach

NASA Astrophysics Data System (ADS)

Negron, L. M.; Clague, J. W.; Gorski, D.; Amaya, M. A.; Pingitore, N. E.

2013-12-01

Millimeter- and micrometer-scale permeability of fine-grained igneous rocks has generated limited research interest. Nonetheless, the scale and distribution of such micro-permeability determines fluid penetration and pathways, parameters that define both the ability to heap leach a rock and the optimal grain size for such an operation. Texas Rare Earth Resources is evaluating the possibility of heap leaching of yttrium and heavy rare earth elements (YHREE) from the peraluminous rhyolite laccolith that forms one-mile-diameter Round Top Mountain. The YHREEs in this immense, surface-exposed deposit (minimum 1.6 billion tons, Texas Bureau Economic Geology) are dilute and diffuse, suggesting leaching as the best option for recovery. The REE grade is 0.05% and YHREEs comprise more than 70% of the total REE content. The YHREEs are hosted exclusively in micron-scale yttrofluorite grains, which proved soluble in dilute sulfuric acid. Laboratory experiments showed YHREE recoveries of up to 90%. Within limits, recoveries decrease with larger grain sizes, and increase with acid strength and exposure time. Our research question centers on dissolution effectiveness: Is YHREE recovery, relative to grain size, limited by (1) diffusion time of acid into, and dissolved solids, including YHREEs, out of the micro-permeability paths inherent in the rock particles; (2) the effective lengths of the natural micro-permeability paths in the rock; or (3) the putative role of the acid in dissolving new micro-paths into the grains? The maximum grain size should not exceed twice the typical path length (unless acid creates new paths), lest YHREEs in the core of a larger grain than that not be reached by acid. If instead diffusion time is limiting, longer leach time may prove effective. Rather than perform an extensive and expensive series of laboratory leaching experiments--some of which would be several months in duration--to determine optimal grain size, we developed a technique to efficiently determine the limits of penetration of water into the rhyolite. We cut parallel-sided slabs of Round Top rhyolite at staged thickness up to 10 mm. We then wet one side and view the opposite side over time under UV light to detect breakthrough of the fluorescein dye. Because of its extremely low visual detection limits, well below the ppm level, the dye has been widely used in biochemical research, as a tracer in surface and ground water studies, in delineating invisible cracks in such structural material as motor blocks, and in detecting corneal abrasions. We have been successful in detecting breakthrough at different rhyolite thicknesses. Continuing studies focus on mapping of the 2-dimensional distribution of the permeability via hand lens and low-power microscope; use of visible light dyes; and examination of specimens pre- and post-acid leaching to determine whether acid exposure produced significant new micro-permeability.

Removal of Sb-125 and Tc-99 from Liquid Radwaste by Novel Adsorbents

DOE Office of Scientific and Technical Information (OSTI.GOV)

Harjula, R.O.; Koivula, R.; Paajanen, A.

2006-07-01

Novel proprietary metal oxide materials (MOM) have been tested for the removal of Sb-125 from simulated Floor Drain Waters of BWR. Antimony was present in the solutions as oxidized anionic form. Long term column experiment with simulated liquid that showed high Sb-125 removal at least up to 8000 bed volumes. One column experiments was carried out using nonradioactive Sb to exhaust the column. Leaching tests with 1000 ppm boric acid showed that 100 % of absorbed Sb remains in the sorbent material. Column experiments with real Fuel Pond Water from Olkiluoto NPP (BWR) showed reduction of Sb-125 (feed level 400more » Bq/L, 1.10{sup -5} {mu}Ci/mL) below detection limit (MDA = 1.7 Bq/L, 5.10{sup -8},{mu}Ci/mL). Additional experiments have also been carried out with pertechnetate (Tc-99) ions. Results indicate that MOM materials are efficient also for the removal of Tc-99 from concentrated NaNO{sub 3} solution. (authors)« less

Effects of Leaching Behavior of Calcium Ions on Compression and Durability of Cement-Based Materials with Mineral Admixtures

PubMed Central

Cheng, An; Chao, Sao-Jeng; Lin, Wei-Ting

2013-01-01

Leaching of calcium ions increases the porosity of cement-based materials, consequently resulting in a negative effect on durability since it provides an entry for aggressive harmful ions, causing reinforcing steel corrosion. This study investigates the effects of leaching behavior of calcium ions on the compression and durability of cement-based materials. Since the parameters influencing the leaching behavior of cement-based materials are unclear and diverse, this paper focuses on the influence of added mineral admixtures (fly ash, slag and silica fume) on the leaching behavior of calcium ions regarding compression and durability of cemented-based materials. Ammonium nitrate solution was used to accelerate the leaching process in this study. Scanning electron microscopy, X-ray diffraction analysis, and thermogravimetric analysis were employed to analyze and compare the cement-based material compositions prior to and after calcium ion leaching. The experimental results show that the mineral admixtures reduce calcium hydroxide quantity and refine pore structure through pozzolanic reaction, thus enhancing the compressive strength and durability of cement-based materials. PMID:28809247

Selection of organic acid leaching reagent for recovery of zinc and manganese from zinc-carbon and alkaline spent batteries

NASA Astrophysics Data System (ADS)

Yuliusman; Amiliana, R. A.; Wulandari, P. T.; Ramadhan, I. T.; Kusumadewi, F. A.

2018-03-01

Zinc-carbon and alkaline batteries are often used in electronic equipment that requires small quantities of power. The waste from these batteries contains valuable metals, such as zinc and manganese, that are needed in many industries and can pollute the environment if not treated properly. This paper concerns the recovery of zinc and manganese metals from zinc-carbon and alkaline spent batteries with leaching method and using organic acid as the environmental friendly leaching reagent. Three different organic acids, namely citric acid, malic acid and aspartic acid, were used as leaching reagents and compared with sulfuric acid as non-organic acid reagents that often used for leaching. The presence of hydrogen peroxide as manganese reducers was investigated for both organic and non-organic leaching reagents. The result showed that citric acid can recover 64.37% Zinc and 51.32% Manganese, while malic acid and aspartic acid could recover less than these. Hydrogen peroxide gave the significant effect for leaching manganese with non-organic acid, but not with organic acid.

Leaching Behavior of Selected Trace and Toxic Metals in Coal Fly Ash Samples Collected from Two Thermal Power Plants, India.

PubMed

Sandeep, P; Sahu, S K; Kothai, P; Pandit, G G

2016-09-01

Studies on leaching behavior of metals associated with coal fly ash (FA) are of great concern because of possible contamination of the aquatic environment. In the present study, leaching behavior of metals (As, Se, Cr, Pb, V, Zn, etc.) in two different FA samples (FA1 and FA2) was investigated at various pH (2-12), temperatures of leachate solution and using TCLP. At pH 2, the highest leaching was observed for Fe (21.6 and 32.8 µg/g), whereas at pH 12, Arsenic was found to have the highest leaching (1.5 and 2.4 µg/g) in FA1 and FA2. Leachate solution temperature showed a positive effect on the metal's leachability. In TCLP, most of the metal's leachability was observed to be higher than that of batch leaching tests. The present study suggests that, leaching of As and Se from FA samples can moderately affect ground/surface water quality at the study locations.

Succinic acid-based leaching system: A sustainable process for recovery of valuable metals from spent Li-ion batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Li; Qu, Wenjie; Zhang, Xiaoxiao

A hydrometallurgical method involving natural organic acid leaching has been developed for recovery of lithium and cobalt from the cathode active materials in spent lithium-ion batteries. Succinic acid is employed as leaching agent and H2O2 as reductant. The cobalt and lithium contents from the succinic acid-based treatment of spent batteries are determined by inductively coupled plasma-optical emission spectroscopy to calculate the leaching efficiency. The spent LiCoO2 samples after calcination and the residues after leaching are characterized by X-ray diffraction and scanning electron microscopy. The results show that nearly 100% of cobalt and more than 96% of lithium are leached undermore » optimal conditions: succinic acid concentration of 1.5 mol L-1, H2O2 content of 4 vol.%, solid-to-liquid ratio of 15 g L-1, temperature of 70 °C, and reaction time of 40 min. Results are also given for fitting of the experimental data to acid leaching kinetic models.« less

The analysis of heavy metal in leaching liquid of coal

NASA Astrophysics Data System (ADS)

Cao, Hongmei; Li, Guanglou; Zhang, Lu

2018-02-01

In this paper, heavy metals in coal were extracted by pure water to simulate the leaching effect of natural precipitation or artificial rainfall on outdoor storage of coal. The results show that the leaching liquid pH was slightly declining, and Cu, Zn, Pb, Cd were in μg/L level, far less than the hazardous waste identification standard of GB5085.3-2007. It suggests that leaching liquid was less harmful to environment when coal was immersed by big amount of water. In the case of spray or precipitation less, the pH drop was more obvious, leaching of heavy metals more, and the general elution of the initial dissolution of the most obvious. Although the amount of small but more toxic, the relevant management should be alert to its harmful.

Release of heavy metals during long-term land application of sewage sludge compost: Percolation leaching tests with repeated additions of compost.

PubMed

Fang, Wen; Delapp, Rossane C; Kosson, David S; van der Sloot, Hans A; Liu, Jianguo

2017-02-01

Leaching assessment procedures have been used to determine the leachability of heavy metals as input for evaluating the risk from sewage sludge compost land application. However, relatively little attention has been paid to understanding leaching from soils with repeated application of sewage sludge compost with elevated levels of heavy metals. In this paper, leaching assessment is extended to evaluate the potential leaching of heavy metals during repetitive application of composted sewage sludge to soils. Four cycling of compost additions and percolation leaching were conducted to investigate how leaching behavior of heavy metals changed with repeated additions of compost. Results showed that repetitive additions of compost to soil significantly increased the content of organic matter, which favored the formation of reducing condition due to improved microbial activities and oxygen consumption. Establishment of reducing conditions can enhance the leaching concentrations of As by approximately 1 order of magnitude, especially for the soil rich in organic matter. For Cd, Cr, Cu, and Pb, repeated additions of compost will cause accumulation in total contents but not enhancement in leaching concentrations. The infiltration following compost additions will leach out the mobile fraction and the residual fraction might not release in the next cycling of compost addition and infiltration. The cumulative release of Cd, Cr, Cu, and Pb accounted for less than 5% of the total contents during four times of compost applications. Copyright © 2016 Elsevier Ltd. All rights reserved.

Environmental Behavior of Chlorpyrifos and Endosulfan in a Tropical Soil in Central Brazil.

PubMed

Dores, Eliana F G C; Spadotto, Claudio A; Weber, Oscarlina L S; Dalla Villa, Ricardo; Vecchiato, Antonio B; Pinto, Alicio A

2016-05-25

The environmental behavior of chlorpyrifos and endosulfan in soil was studied in the central-western region of Brazil by means of a field experiment. Sorption was evaluated in laboratory batch experiments. Chlorpyrifos and endosulfan were applied to experimental plots on uncultivated soil and the following processes were studied: leaching, runoff, and dissipation in top soil. Field dissipation of chlorpyrifos and endosulfan was more rapid than reported in temperate climates. Despite the high Koc of the studied pesticides, the two endosulfan isomers and endosulfan sulfate as well as chlorpyrifos were detected in percolated water. In runoff water and sediment, both endosulfan isomers and endosulfan sulfate were detected throughout the period of study. Observed losses of endosulfan by leaching (below a depth of 50 cm) and runoff were 0.0013 and 1.04% of the applied amount, whereas chlorpyrifos losses were 0.003 and 0.032%, respectively. Leaching of these highly adsorbed pesticides was attributed to preferential flow.

Design of Perovskite Oxides as Anion-Intercalation-Type Electrodes for Supercapacitors: Cation Leaching Effect.

PubMed

Liu, Yu; Dinh, Jim; Tade, Moses O; Shao, Zongping

2016-09-14

Oxygen ions can be exploited as a charge carrier to effectively realize a new type of anion-intercalation supercapacitor. In this study, to get some useful guidelines for future materials development, we comparatively studied SrCoO3-δ (SC), Ba0.5Sr0.5Co0.8Fe0.2O3-δ (BSCF), and Co3O4 as electrodes in supercapacitors with aqueous alkaline electrolyte. The effect of interaction between the electrode materials with the alkaline solution was focused on the structure and specific surface area of the electrode material, and ultimately the electrochemical performance was emphasized. Both BSCF and SC were found to experience cation leaching in alkaline solution, resulting in an increase in the specific surface area of the material, but overleaching caused the damage of perovskite structure of BSCF. Barium leaching was more serious than strontium, and the cation leaching was component dependent. Although high initial capacitance was achieved for BSCF, it was not a good candidate as intercalation-type electrode for supercapacitor because of poor cycling stability from serious Ba(2+) and Sr(2+) leaching. Instead, SC was a favorable electrode candidate for practical use in supercapacitors due to its high capacity and proper cation leaching capacity, which brought beneficial effect on cycling stability. It is suggested that cation leaching effect should be seriously considered in the development of new perovskite materials as electrodes for supercapacitors.

Cement-based stabilization/solidification of oil refinery sludge: Leaching behavior of alkanes and PAHs.

PubMed

Karamalidis, Athanasios K; Voudrias, Evangelos A

2007-09-05

Stabilization/solidification is a process widely applied for the immobilization of inorganic constituents of hazardous wastes, especially for metals. Cement is usually one of the most common binders for that purpose. However, limited results have been presented on immobilization of hydrocarbons in cement-based stabilized/solidified petroleum solid waste. In this study, real oil refinery sludge samples were stabilized and solidified with various additions of I42.5 and II42.5 cement (Portland and blended cement, respectively) and subject to leaching. The target analytes were total petroleum hydrocarbons, alkanes and 16 polycyclic aromatic hydrocarbons of the EPA priority pollutant list. The experiments showed that the waste was confined in the cement matrix by macroencapsulation. The rapture of the cement structure led to the increase of leachability for most of the hydrocarbons. Leaching of n-alkanes from II42.5 cement-solidified samples was lower than that from I42.5 solidified samples. Leaching of alkanes in the range of n-C(10) to n-C(27) was lower than that of long chain alkanes (>n-C(27)), regardless the amount of cement addition. Generally, increasing the cement content in the solidified waste samples, increased individual alkane leachability. This indicated that cement addition resulted in destabilization of the waste. Addition of I42.5 cement favored immobilization of anthracene, benzo[a]anthracene, benzo[b]fluoroanthene, benzo[k]fluoroanthene, benzo[a]pyrene and dibenzo[a,h]anthracene. However, addition of II42.5 favored 5 out of 16, i.e., naphthalene, anthracene, benzo[b]fluoroanthene, benzo[k]fluoroanthene and dibenzo[a,h]anthracene.

The dissolution kinetics of major elements in municipal solid waste incineration bottom ash particles

NASA Astrophysics Data System (ADS)

Bendz, David; Tüchsen, Peter L.; Christensen, Thomas H.

2007-12-01

Leaching and tracer experiments in batches at L/S 20 were performed with 3-month-old MSWI bottom ash separated into eight different particle sizes. The time-dependent leaching of major elements (Ca 2+, K +, Na +, Cl - and SO 4- 2 ) was monitored for up to 747 h. Physical properties of the particles, the specific surface (BET), pore volume and pore volume distribution over pore sizes (BJH) were determined for all particle classes by N 2 adsorption/desorption experiments. Some common features of physical pore structure for all particles were revealed. The specific surface and the particle pore volume were found to be negatively correlated with particle size, ranging from 3.2 m 2/g to 25.7 m 2/g for the surface area and from 0.0086 cm 3/g to 0.091 cm 3/g for the pore volume. Not surprisingly, the specific surface area was found to be the major material parameter that governed the leaching behavior for all elements (Ca 2+, K +, Na +, Cl - and SO 4- 2 ) and particle sizes. The diffusion resistance was determined independently by separate tracer (tritium) experiments. Diffusion gave a significant contribution to the apparent leaching kinetics for all elements during the first 10-40 h (depending on the particle size) of leaching and surface reaction was the overall rate controlling mechanism at late times for all particle sizes. For Ca 2+ and SO 4- 2 , the coupled effect of diffusion resistance and the degree of undersaturation in the intra particle pore volume was found to be a major rate limiting dissolution mechanism for both early and late times. The solubility control in the intra particulate porosity may undermine any attempt to treat bottom ash by washing out the sulfate. Even for high liquid/solid ratios, the solubility in the intra-particular porosity will limit the release rate.

The potential of on-line continuous leach ICP-MS analysis for linking trace elements to mineralogy

NASA Astrophysics Data System (ADS)

Roskam, Gerlinde; Verheul, Marc; Moraetis, Daniel; Giannakis, George; van Gaans, Pauline

2014-05-01

A set of five soil samples was subjected to an on-line continuous leach inductively coupled plasma mass spectrometry experiment, with progressively reactive solvents (0.01M CaCl2, 0.1 M HNO3, 1M HNO3, 4M HNO3) Each sample was packed in a quartz tube (Ø= 1 cm, length 2 cm) and diluted 1:1 with acid washed quartz to prevent clogging. The gas that was produced during the extraction was removed by leading the effluent into a small container, from where the sample was directly pumped into the ICP-MS. 115In was used as an internal standard. Continuous leach experiments have the advantage of real time (every 2 seconds) full elemental analysis. Mineral breakdown reactions can be monitored via the major elements. The trace elements associated with the minerals are monitored simultaneously, thus eliminating the uncertainties of host mineral-trace element combinations in traditional off-line sequential extractions. The continuous leach experimental data are correlated to XRD-results for mineralogy and total elemental concentrations. The soil samples used were collected from different sites in the Koiliaris River watershed, Crete, Greece 1). The selection of the sites was based on variability in bedrock (limestone, metamorphic and alluvial sediments) and current land use (grape farming, olive trees). Soils were sampled at two depths: at the surface and just above the bedrock. No large differences in the major elements between the two depths were measured. To provide background to the on-line sequential data, also total concentrations of the major elements were analysed by XRF and the mineralogy was analysed by XRD. The fraction <2mm was sieved and digested with HF, HClO4 and HNO3 for additional trace element analysis. 1) See related abstract Roskam et al., 2014: REE profiles in continuous leach ICP-MS (CL-ICP-MS) experiments in soil, linked to REE profiles in surface water in the Koiliaris River Critical Zone Observatory (CZO), Crete, Greece.

Integrated copper-containing wastewater treatment using xanthate process.

PubMed

Chang, Yi-Kuo; Chang, Juu-En; Lin, Tzong-Tzeng; Hsu, Yu-Ming

2002-09-02

Although, the xanthate process has been shown to be an effective method for heavy metal removal from contaminated water, a heavy metal contaminated residual sludge is produced by the treatment process and the metal-xanthate sludge must be handled in accordance with the Taiwan EPA's waste disposal requirements. This work employed potassium ethyl xanthate (KEX) to remove copper ions from wastewater. The toxicity characteristic leaching procedure (TCLP) and semi-dynamic leaching test (SDLT) were used to determine the leaching potential and stability characteristics of the residual copper xanthate (Cu-EX) complexes. Results from metal removal experiments showed that KEX was suitable for the treatment of copper-containing wastewater over a wide copper concentration range (50, 100, 500, and 1000 mg/l) to the level that meets the Taiwan EPA's effluent regulations (3mg/l). The TCLP results of the residual Cu-EX complexes could meet the current regulations and thus the Cu-EX complexes could be treated as a non-hazardous material. Besides, the results of SDLT indicated that the complexes exhibited an excellent performance for stabilizing metals under acidic conditions, even slight chemical changes of the complexes occurred during extraction. The xanthate process, mixing KEX with copper-bearing solution to form Cu-EX precipitates, offered a comprehensive strategy for solving both copper-containing wastewater problems and subsequent sludge disposal requirements.

Extraction of uranium from tailings by sulfuric acid leaching with oxidants

NASA Astrophysics Data System (ADS)

Huang, Jing; Li, Mi; Zhang, Xiaowen; Huang, Chunmei; Wu, Xiaoyan

2017-06-01

Recovery of uranium have been performed by leaching uranium-containing tailings in sulfuric acid system with the assistance of HF, HClO4, H2O2 and MnO2. The effect of reagent dosage, sulfuric acid concentration, Liquid/solid ratio, reaction temperature and particle size on the leaching of uranium were investigated. The results show that addiction of HF, HClO4, H2O2 and MnO2 significantly increased the extraction of uranium under 1M sulphuric acid condition and under the optimum reaction conditions a dissolution fraction of 85% by HClO4, 90% by HF, 95% by H2O2 can be reached respectively. The variation of technological mineralogy properites of tailings during leaching process show that the assistants can break gangue effectively. These observations suggest that optimum oxidants could potentially influence the extraction of uranium from tailings even under dilute acid condition.

The improvement and simulation for LEACH clustering routing protocol

NASA Astrophysics Data System (ADS)

Ji, Ai-guo; Zhao, Jun-xiang

2017-01-01

An energy-balanced unequal multi-hop clustering routing protocol LEACH-EUMC is proposed in this paper. The candidate cluster head nodes are elected firstly, then they compete to be formal cluster head nodes by adding energy and distance factors, finally the date are transferred to sink through multi-hop. The results of simulation show that the improved algorithm is better than LEACH in network lifetime, energy consumption and the amount of data transmission.

Structural ceramics containing electric arc furnace dust.

PubMed

Stathopoulos, V N; Papandreou, A; Kanellopoulou, D; Stournaras, C J

2013-11-15

In the present work the stabilization of electric arc furnace dust EAFD waste in structural clay ceramics was investigated. EAFD was collected over eleven production days. The collected waste was characterized for its chemical composition by Flame Atomic Absorption Spectroscopy. By powder XRD the crystal structure was studied while the fineness of the material was determined by a laser particle size analyzer. The environmental characterization was carried out by testing the dust according to EN12457 standard. Zn, Pb and Cd were leaching from the sample in significant amounts. The objective of this study is to investigate the stabilization properties of EAFD/clay ceramic structures and the potential of EAFD utilization into structural ceramics production (blocks). Mixtures of clay with 2.5% and 5% EAFD content were studied by TG/DTA, XRD, SEM, EN12457 standard leaching and mechanical properties as a function of firing temperature at 850, 900 and 950 °C. All laboratory facilities maintained 20 ± 1 °C. Consequently, a pilot-scale experiment was conducted with an addition of 2.5% and 5% EAFD to the extrusion mixture for the production of blocks. During blocks manufacturing, the firing step reached 950 °C in a tunnel kiln. Laboratory heating/cooling gradients were similar to pilot scale production firing. The as produced blocks were then subjected to quality control tests, i.e. dimensions according to EN772-17, water absorbance according to EN772-6, and compressive strength according to EN772-1 standard, in laboratory facilities certified under EN17025. The data obtained showed that the incorporation of EAFD resulted in an increase of mechanical strength. Moreover, leaching tests performed according to the Europeans standards on the EAFD-block samples showed that the quantities of heavy metals leached from crushed blocks were within the regulatory limits. Thus the EAFD-blocks can be regarded as material of no environmental concern. Copyright © 2013 Elsevier B.V. All rights reserved.

The effects of acid leaching on 40Ar/39Ar age dating results using samples from the Walvis Ridge hotspot trail

NASA Astrophysics Data System (ADS)

Klath, J. F.; Koppers, A. A.; Heaton, D. E.; Schnur, S.

2013-12-01

In this study we systematically explore how acid leaching can be used to reduce the negative effects of seawater alteration on the 40Ar/39Ar age dating of submarine basalts. Koppers et al (2000) showed that acid leaching of groundmass samples generated more consistent ages as well as ages more concordant with phenocrystic mineral phases, compared to samples that were left untreated. By studying the effects of progressively increasing the strength and length of acid treatment, we will show how acid leaching of groundmass separates reduces alteration while leaving the initial eruption signature intact. Samples were chosen from the Walvis ridge hotspot trail in the southeast Atlantic. Three samples were selected based on degree and style of alteration. Two samples (basalt and basaltic andesite) appear highly altered in thin section. The basalt contains diffuse iddingsite alteration that is pervasive throughout the groundmass. The basaltic andesite displays focused secondary mineral phases within and around abundant vesicles. The third sample, a trachyte, shows relatively minor degrees of alteration in thin section. These groundmass separates were divided into four splits and treated with a progressively stronger acid and for longer duration. One split from each rock was left untreated to act as a baseline. Of the other three splits from each sample, one was treated with a mild leach (1N HCl and 1N HNO3), one a strong leach (1N HCl, 1N HNO3, 6N HCl, and 3N HNO3), and lastly the strong leach performed twice. The samples were then handpicked to remove any remaining visible alteration. The untreated samples were picked as well, removing the most distinctly altered grains. All splits were analyzed by electron microprobe, x-ray fluorescence (XRF) and the incremental heating 40Ar/39Ar dating method. We will report on the results of an image analysis of microprobe backscatter images and elemental maps taken of individual groundmass grains. This analysis will show the location of alteration within the groundmass and how it is changing as acid leaching strength and duration progresses. We will discuss bulk composition comparisons as well as how depletions and enrichments vary amongst major and trace elements. Lastly, we will report 40Ar/39Ar step heating results, in particular K/Ca ratios and age spectra, to better understand the effect of leaching strength on the effective removal of groundmass alteration during 40Ar/39Ar age dating.

Characterization of phosphorus leaching from phosphate waste rock in the Xiangxi River watershed, Three Gorges Reservoir, China.

PubMed

Jiang, Li-Guo; Liang, Bing; Xue, Qiang; Yin, Cheng-Wei

2016-05-01

Phosphate mining waste rocks dumped in the Xiangxi River (XXR) bay, which is the largest backwater zone of the Three Gorges Reservoir (TGR), are treated as Type I industry solid wastes by the Chinese government. To evaluate the potential pollution risk of phosphorus leaching from phosphate waste rocks, the phosphorus leaching behaviors of six phosphate waste rock samples with different weathering degrees under both neutral and acidic conditions were investigated using a series of column leaching experiments, following the Method 1314 standard of the US EPA. The results indicate that the phosphorus release mechanism is solubility-controlled. Phosphorus release from waste rocks increases as pH decreases. The phosphorus leaching concentration and cumulative phosphorus released in acidic leaching conditions were found to be one order of magnitude greater than that in neutral leaching conditions. In addition, the phosphorus was released faster during the period when environmental pH turned from weak alkalinity to slight acidity, with this accelerated release period appearing when L/S was in the range of 0.5-2.0 mL/g. In both neutral and acidic conditions, the average values of Total Phosphorus (TP), including orthophosphates, polyphosphates and organic phosphate, leaching concentration exceed the availability by regulatory (0.5 mg/L) in the whole L/S range, suggesting that the phosphate waste rocks stacked within the XXR watershed should be considered as Type II industry solid wastes. Therefore, the phosphate waste rocks deposited within the study area should be considered as phosphorus point pollution sources, which could threaten the adjacent surface-water environment. Copyright © 2016 Elsevier Ltd. All rights reserved.

Factors influencing leaching of PBDEs from waste cathode ray tube plastic housings.

PubMed

Stubbings, William A; Harrad, Stuart

2016-11-01

Samples of waste cathode ray tube (CRT) plastic housings were exposed to Milli-Q® water containing dissolved humic matter at concentrations of 0, 100 and 1000mgL(-1) as leaching fluid under laboratory conditions, and polybrominated diphenyl ethers (PBDEs) determined in the resulting leachate. Despite the relatively hydrophobic physicochemical properties of PBDEs, concentrations of ƩPBDEs in the leachate from the leaching experiments in this study ranged from 14,000 to 200,000ngL(-1). PBDE leaching appears to be a second order process, whereby a period of initially intense dissolution of more labile PBDEs is followed by a slower stage corresponding to external diffusion of the soluble residue in the material. The bulk of transfer of PBDEs to the leaching fluid occurs within the first 6h of contact, during which time we suggest that the most labile PBDEs are "washed" off the surface of the CRT plastics. The predominant congeners in the chips were BDE-209 (2600mgkg(-1)) and BDE 183 (220mgkg(-1)). The impacts on PBDE leaching of leachate pH and temperature were also examined. Increasing the temperature of leaching fluids from 20 to 80°C, enhances the leachability of BDE-209 and BDE-99 from plastics. In all cases, the alkaline pH8.5 examined, resulted in the greatest PBDE concentrations in leachate. Agitation of the waste/leachate mixture enhances PBDE leaching from CRT plastics. Potential evidence for debromination of heavy congeners to the lower brominated and more bioavailable BDEs was observed. Specifically, BDEs-47, -85 and -100 were detected in the leachates, but were absent from the CRT plastics themselves. Copyright © 2016. Published by Elsevier B.V.

Geochemical characterization and leaching behavior of slags: by-product materials from an old lead smelter in Chihuahua, Mexico

NASA Astrophysics Data System (ADS)

Espejel-Garcia, D.; Wenglas-Lara, G.; Villalobos-Aragon, A.; Espejel-Garcia, V. V.

2012-12-01

Steel slags are stored in piles or stocks around or near the smelter site. Currently, there is an increasing interest in the use of waste materials, especially in the construction industry, to replace natural aggregates, help the environment and reduce the costs. Slags are being used widely as road ballast, road base or sub-base material, sandblasting agents or cement additives, but normally contain high concentrations of potentially toxic metals. Although these metals are associated with glass, silicate and oxide minerals, with slow solubilities in water, a characterization of the leaching behavior is essential in environmental evaluation for reuse scenarios. The state of Chihuahua is located in northern Mexico, and mining has been an important economic activity since the 18th century. In the early 1900's, a lead smelter operated in Avalos, Chihuahua (in the southern surroundings of Chihuahua city), and left considerable slag piles after their closure in the 1980's. In this study, this material has been geochemically analyzed to identify the metals contained in it, and used in "tank tests" experiments, to assess its leaching behavior. The slags from Chihuahua contain Pb (0.5 - 4 wt.%), Zn (15-35 wt.%) and As (0.6 wt.%) in different minerals such as hardystonite (Ca2ZnSi2O7), melanotekite (Pb2Fe3+3O2Si2O7), kentrolite (Pb2Mn2Si2O9) and sphalerite (ZnS) or trapped in the glass. Major elements are present in phases such as monticellite (CaMgSiO4), kirschsteinite (CaFe2+SiO4), hedenbergite (CaFeSi2O6), babingtonite (Fe2Si3O9), magnetite (Fe3O4), and calcite (CaCO3). The leaching experiments were performed for 6, 24, 168 and 360 hours in mixtures of 30 and 50% of slags with natural road base material using distilled water at a pH 5 and 8 to recreate acidic and alkaline waters. The amounts of leached Pb ranges from 0.1 to 0.5 ppm, Zn from 0.1 to 0.6 ppm, As from 0 to 0.09 ppm, and Ca from 40 to 180 ppm, being the acidic experiments the ones that leached out the highest amounts of metals. Based on the results of analyses and experiments, it is recommended to use the waste material (slags) as aggregates in road construction, but only as minor constituent (<30%) in base materials.

Leaching of rare earth elements from fluorescent powder using the tea fungus Kombucha.

PubMed

Hopfe, Stefanie; Flemming, Katrin; Lehmann, Falk; Möckel, Robert; Kutschke, Sabine; Pollmann, Katrin

2017-04-01

In most modern technologies such as flat screens, highly effective magnets and lasers, as well as luminescence phosphors, Rare Earth Elements (REE) are used. Unfortunately no environmentally friendly recycling process exists so far. In comparison to other elements the interaction of microorganisms with REE has been studied to a less extent. However, as REE are ubiquitously present in nature it can be assumed that microorganisms play an important role in the biogeochemistry of REE. This study investigates the potential of organic acid-producing microbes for extracting REE from industrial waste. In Germany, 175 tons of fluorescent phosphor (FP) are collected per year as a distinct fraction from the recycling of compact fluorescent lamps. Because the FP contains about 10% of REE-oxides bound in the so-called triband dyes it is a readily accessible secondary resource of REE. Using the symbiotic mixed culture Kombucha, consisting of yeasts and acetic acid bacteria, REE were leached at a significant rate. The highest leaching-rates were observed in shake cultures using the entire Kombucha-consortium or its supernatant as leaching agent compared to experiments using the isolates Zygosaccharomyces lentus and Komagataeibacter hansenii as leaching organisms. During the cultivation, the pH decreased as a result of organic acid production (mainly acetic and gluconic acid). Thus, the underlying mechanism of the triband dye solubilisation is probably linked to the carboxyl-functionality or a proton excess. In accordance with the higher solubility of REE-oxides compared to REE-phosphates and -aluminates, the red dye Y 2 O 3 :Eu 2+ containing relatively expensive REE was shown to be preferentially solubilized. These results show that it is possible to dissolve the REE-compounds of FP with the help of microbial processes. Moreover, they provide the basis for the development of an eco-friendly alternative to the currently applied methods that use strong inorganic acids or toxic chemicals. Copyright © 2017 Elsevier Ltd. All rights reserved.

Evaluation of the Accumulation of Trace Metals (as, U, CR, CU, PB, Zn) on Iron-Manganese Coatings on in Situ Stream Pebbles and Emplaced Substrates

NASA Astrophysics Data System (ADS)

Turpin, M. M.; Blake, J.; Crossey, L. J.; Ali, A.; Hansson, L.

2015-12-01

Exposure to trace metals (As, U, Cr, Cu, Pb, Zn) has potential negative health effects on human populations and wildlife. Geothermal waters often have elevated concentrations of trace elements and understanding the geochemical cycling of these elements can be challenging. Previous studies have utilized in situ stream pebbles and glass or ceramic substrates with iron-manganese oxide coatings to understand contamination and or chemical cycling. This project's main focus is to develop an ideal tracing method using adsorption onto substrate surfaces and to define key parameters that are necessary for the phenomenon of adsorption between trace metals and these surface coatings to occur. Sampling locations include the Jemez River and Rio San Antonio in the Jemez mountains, northern New Mexico. Both streams have significant geothermal inputs. Pebbles and cobbles were gathered from the active stream channel and 6mm glass beads and 2 X1 in. ceramic plates were placed in streams for three weeks to allow for coating accumulation. Factors such as leachate type, water pH, substrate type, coating accumulation period and leach time were all considered in this experiment. It was found that of the three leachates (aqua regia, 10% aqua regia and hydroxylamine), hydroxylamine was the most effective at leaching coatings without dissolving substrates. Samples leached with aqua regia and 10% aqua regia were found to lose weight and mass over the following 5, 7, and 10 day measurements. Glass beads were determined to be more effective than in stream pebbles as an accumulation substrate: coatings were more easily controlled and monitored. Samples leached with hydroxylamine for 5 hours and 72 hours showed little difference in their leachate concentrations, suggesting that leach time has little impact on the concentration of leachate samples. This research aims to find the best method for trace metal accumulation in streams to aid in understanding geochemical cycling.

Investigation of recovery and recycling of rare earth elements from waste fluorescent lamp phosphors

NASA Astrophysics Data System (ADS)

Eduafo, Patrick Max

Characterization techniques and experimental measurements were used to evaluate a process for recycling rare earth elements (REEs) from spent fluorescent lamp phosphors. QEMSCAN analysis revealed that over 60% of the rare earth bearing minerals was less than 10 microm. A representative sample of the as-received feed contained 14.59 wt% total rare earth elements (TREE) and upon sieving to below 75 microm, the grade increased to 19.60 wt% REE with 98.75% recovery. Based on experimental work, a new process for extracting the chief REEs from end of life fluorescent lamps has been developed. The proposed flowsheet employs a three-stage leaching and precipitation process for selective extraction and recovery of the REEs. Hydrochloric acid was used as lixiviant in batch leach experiments on the phosphor powder. The maximum extraction obtained was 100% for both yttrium and europium under the following leaching conditions: 2.5 M HCl, 70°C, 1 hour, 180 g/L and 600 rpm. However, the solubility of cerium, lanthanum and terbium remained low at these conditions. Kinetic data of the leaching of yttrium and europium showed best fit to the logarithmic rate expression of the empirical model of leaching. Activation energy was calculated to be 77.49 kJ/mol for Y and 72.75 kJ/mol for Eu in the temperature range of 298 to 343 K. Precipitation tests demonstrate that at least 50% excess the stoichiometric amount of oxalic acid is needed to recover yttrium and europium efficiently to produce a pure (Y, Eu) mixed oxide. Total recovery of the REEs was achieved even at very low pH or without any base added. Over 99% pure mixed rare earth oxide at 99% recovery has been attained. An economic assessment of the developed process using operating and capital cost have be undertaken and based on the analysis of the three economic scenarios, two are economic and one is non-economic.

Leaching behavior of rare earth elements in fort union lignite coals of North America

DOE PAGES

Laudal, Daniel A.; Benson, Steven A.; Addleman, Raymond Shane; ...

2018-03-30

Fort Union lignite coal samples were subjected to a series of aqueous leaching experiments to understand the extraction behavior of the rare earth elements (REE). This testing was aimed at understanding the modes of occurrence of the REE in the lignite coals, as well as to provide foundational data for development of rare earth extraction processes. In a first series of tests, a sequential leaching process was used to investigate modes of occurrence of the REE of select lignite coals. The tests involved sequential exposure to solvents consisting of water, ammonium acetate and dilute hydrochloric acid (HCl). The results indicatedmore » that water and ammonium acetate extracted very little of the REE, indicating the REE are not present as water soluble or ion-exchangeable forms. However, the data shows that a large percentage of the REE were extracted with the hydrochloric acid (80–95 wt%), suggesting presence in HCl-soluble mineral forms such as carbonates, and/or presence as organic complexes. A second series of tests was performed involving single-step leaching with dilute acids and various operating parameters, including acid type, acid concentration, acid/coal contact time and coal particle size. For select samples, additional tests were performed to understand the results of leaching, including float-sink density separations and humic acid extraction. The results have shown that the majority of REE in Fort Union lignites appear to be associated weakly with the organic matrix of the coals, most likely as coordination complexes of carboxylic acid groups. The light REE and heavy REE exhibit different behaviors, however. The extractable light REE appear to have association both in acid-soluble mineral forms and as organic complexes, whereas the extractable heavy REE appear to be almost solely associated with the organics. In conclusion, scandium behavior was notably different than yttrium and the lanthanides, and the data suggests the extractable content is primarily associated as acid-soluble mineral forms.« less

Leaching behavior of rare earth elements in fort union lignite coals of North America

DOE Office of Scientific and Technical Information (OSTI.GOV)

Laudal, Daniel A.; Benson, Steven A.; Addleman, Raymond Shane

Fort Union lignite coal samples were subjected to a series of aqueous leaching experiments to understand the extraction behavior of the rare earth elements (REE). This testing was aimed at understanding the modes of occurrence of the REE in the lignite coals, as well as to provide foundational data for development of rare earth extraction processes. In a first series of tests, a sequential leaching process was used to investigate modes of occurrence of the REE of select lignite coals. The tests involved sequential exposure to solvents consisting of water, ammonium acetate and dilute hydrochloric acid (HCl). The results indicatedmore » that water and ammonium acetate extracted very little of the REE, indicating the REE are not present as water soluble or ion-exchangeable forms. However, the data shows that a large percentage of the REE were extracted with the hydrochloric acid (80–95 wt%), suggesting presence in HCl-soluble mineral forms such as carbonates, and/or presence as organic complexes. A second series of tests was performed involving single-step leaching with dilute acids and various operating parameters, including acid type, acid concentration, acid/coal contact time and coal particle size. For select samples, additional tests were performed to understand the results of leaching, including float-sink density separations and humic acid extraction. The results have shown that the majority of REE in Fort Union lignites appear to be associated weakly with the organic matrix of the coals, most likely as coordination complexes of carboxylic acid groups. The light REE and heavy REE exhibit different behaviors, however. The extractable light REE appear to have association both in acid-soluble mineral forms and as organic complexes, whereas the extractable heavy REE appear to be almost solely associated with the organics. In conclusion, scandium behavior was notably different than yttrium and the lanthanides, and the data suggests the extractable content is primarily associated as acid-soluble mineral forms.« less

Treatment of electronic waste to recover metal values using thermal plasma coupled with acid leaching--a response surface modeling approach.

PubMed

Rath, Swagat S; Nayak, Pradeep; Mukherjee, P S; Roy Chaudhury, G; Mishra, B K

2012-03-01

The global crisis of the hazardous electronic waste (E-waste) is on the rise due to increasing usage and disposal of electronic devices. A process was developed to treat E-waste in an environmentally benign process. The process consisted of thermal plasma treatment followed by recovery of metal values through mineral acid leaching. In the thermal process, the E-waste was melted to recover the metal values as a metallic mixture. The metallic mixture was subjected to acid leaching in presence of depolarizer. The leached liquor mainly contained copper as the other elements like Al and Fe were mostly in alloy form as per the XRD and phase diagram studies. Response surface model was used to optimize the conditions for leaching. More than 90% leaching efficiency at room temperature was observed for Cu, Ni and Co with HCl as the solvent, whereas Fe and Al showed less than 40% efficiency. Copyright © 2011 Elsevier Ltd. All rights reserved.

Evaluation of shrinking core model in leaching process of Pomalaa nickel laterite using citric acid as leachant at atmospheric conditions

NASA Astrophysics Data System (ADS)

Wanta, K. C.; Perdana, I.; Petrus, H. T. B. M.

2016-11-01

Most of kinetics studies related to leaching process used shrinking core model to describe physical phenomena of the process. Generally, the model was developed in connection with transport and/or reaction of reactant components. In this study, commonly used internal diffusion controlled shrinking core model was evaluated for leaching process of Pomalaa nickel laterite using citric acid as leachant. Particle size was varied at 60-70, 100-120, -200 meshes, while the operating temperature was kept constant at 358 K, citric acid concentration at 0.1 M, pulp density at 20% w/v and the leaching time was for 120 minutes. Simulation results showed that the shrinking core model was inadequate to closely approach the experimental data. Meanwhile, the experimental data indicated that the leaching process was determined by the mobility of product molecules in the ash layer pores. In case of leaching resulting large product molecules, a mathematical model involving steps of reaction and product diffusion might be appropriate to develop.

Leaching for recovery of copper from municipal solid waste incineration fly ash: influence of ash properties and metal speciation.

PubMed

Lassesson, Henric; Fedje, Karin Karlfeldt; Steenari, Britt-Marie

2014-08-01

Recovery of metals occurring in significant amounts in municipal solid waste incineration fly ash, such as copper, could offer several advantages: a decreased amount of potentially mobile metal compounds going to landfill, saving of natural resources and a monetary value. A combination of leaching and solvent extraction may constitute a feasible recovery path for metals from municipal solid waste incineration fly ash. However, it has been shown that the initial dissolution and leaching is a limiting step in such a recovery process. The work described in this article was focused on elucidating physical and chemical differences between two ash samples with the aim of explaining the differences in copper release from these samples in two leaching methods. The results showed that the chemical speciation is an important factor affecting the release of copper. The occurrence of copper as phosphate or silicate will hinder leaching, while sulphate and chloride will facilitate leaching. © The Author(s) 2014.

Mobility of as, Cu, Cr, and Zn from tailings covered with sealing materials using alkaline industrial residues: a comparison between two leaching methods.

PubMed

Jia, Yu; Maurice, Christian; Öhlander, Björn

2016-01-01

Different alkaline residue materials (fly ash, green liquor dregs, and lime mud) generated from the pulp and paper industry as sealing materials were evaluated to cover aged mine waste tailings (<1% sulfur content, primarily pyrite). The mobility of four selected trace elements (Cr, Cu, Zn, and As) was compared based on batch and column leaching studies to assess the effectiveness of these alkaline materials as sealing agents. Based on the leaching results, Cr, Cu, and Zn were immobilized by the alkaline amendments. In the amended tailings in the batch system only As dramatically exceeded the limit values at L/S 10 L/kg. The leaching results showed similar patterns to the batch results, though leached Cr, Cu, and Zn showed higher levels in the column tests than in the batch tests. However, when the columns were compared with the batches, the trend for Cu was opposite for the unamended tailings. By contrast, both batch and column results showed that the amendment caused mobilization of As compared with the unamended tailings in the ash-amended tailings. The amount of As released was greatest in the ash column and decreased from the dregs to the lime columns. The leaching of As at high levels can be a potential problem whenever alkaline materials (especially for fly ash) are used as sealing materials over tailings. The column test was considered by the authors to be a more informative method in remediation of the aged tailings with low sulfur content, since it mimics better actual situation in a field.

Leaching kinetics of bottom ash waste as a source of calcium ions.

PubMed

Koech, Lawrence; Everson, Ray; Neomagus, Hein; Rutto, Hilary

2015-02-01

Bottom ash is a waste material from coal-fired power plants, and it is known to contain elements that are potentially toxic at high concentration levels when disposed in landfills. This study investigates the use of bottom ash as a partial substitute sorbent for wet flue gas desulfurization (FGD) processes by focusing on its leaching kinetics in adipic acid. This was studied basing on the shrinking core model that was applied to the experimental data obtained by the authors presented at the International Conference on Industrial, Manufacturing, Automation and Mechanical Engineering, Johannesburg, South Africa, November 27-28, 2013) on dissolution of bottom ash. The leaching rate constant was obtained from different reaction variables, namely, temperature, pH, acid concentration, and solid-to-liquid ratio, that could affect the leaching process. The solid sample of bottom ash was characterized at different leaching periods using X-ray diffraction (XRD) and scanning electron microscopy (SEM). It was found that solid-to-liquid ratio had a significant effect on the leaching rate constant when compared with other variables. The leaching kinetics showed that diffusion through the product layer was the rate-controlling step during leaching, and the activation energy for the process was found to be 18.92 kJ/mol.

How inhibiting nitrification affects nitrogen cycle and reduces environmental impacts of anthropogenic nitrogen input.

PubMed

Qiao, Chunlian; Liu, Lingli; Hu, Shuijin; Compton, Jana E; Greaver, Tara L; Li, Quanlin

2015-03-01

Anthropogenic activities, and in particular the use of synthetic nitrogen (N) fertilizer, have doubled global annual reactive N inputs in the past 50-100 years, causing deleterious effects on the environment through increased N leaching and nitrous oxide (N2 O) and ammonia (NH3 ) emissions. Leaching and gaseous losses of N are greatly controlled by the net rate of microbial nitrification. Extensive experiments have been conducted to develop ways to inhibit this process through use of nitrification inhibitors (NI) in combination with fertilizers. Yet, no study has comprehensively assessed how inhibiting nitrification affects both hydrologic and gaseous losses of N and plant nitrogen use efficiency. We synthesized the results of 62 NI field studies and evaluated how NI application altered N cycle and ecosystem services in N-enriched systems. Our results showed that inhibiting nitrification by NI application increased NH3 emission (mean: 20%, 95% confidential interval: 33-67%), but reduced dissolved inorganic N leaching (-48%, -56% to -38%), N2 O emission (-44%, -48% to -39%) and NO emission (-24%, -38% to -8%). This amounted to a net reduction of 16.5% in the total N release to the environment. Inhibiting nitrification also increased plant N recovery (58%, 34-93%) and productivity of grain (9%, 6-13%), straw (15%, 12-18%), vegetable (5%, 0-10%) and pasture hay (14%, 8-20%). The cost and benefit analysis showed that the economic benefit of reducing N's environmental impacts offsets the cost of NI application. Applying NI along with N fertilizer could bring additional revenues of $163 ha(-1)  yr(-1) for a maize farm, equivalent to 8.95% increase in revenues. Our findings showed that NIs could create a win-win scenario that reduces the negative impact of N leaching and greenhouse gas production, while increases the agricultural output. However, NI's potential negative impacts, such as increase in NH3 emission and the risk of NI contamination, should be fully considered before large-scale application. © 2014 John Wiley & Sons Ltd.

Leaching behavior of nitrogen in a long-term experiment on rice under different N management systems.

PubMed

Luo, Liang-Guo; Itoh, Sumio; Zhang, Qing-Wen; Yang, Shi-Qi; Zhang, Qing-Zhong; Yang, Zheng-Li

2011-06-01

The leaching behavior of nitrogen was studied in single rice paddy production ecosystems in Tsukuba, Japan after 75 years of consistent fertilization regimes (no fertilizer, ammonium sulfate, a combination of composted rice straw with soybean cake, and fresh clover). During the 75-year period, management was unchanged with respect to rice planting density, irrigation, and net N fertilization for each field to which an N-source was added. Percolation water was collected, from May 2001 to April 2002, using porous suction cups installed in the fields at depths of 15, 40, and 60 cm. All water samples were taken to the laboratory for the measurement of both NH(4) ( + )-N and NO(3) ( - )-N concentrations using a continuous-flow nitrogen analyzer. The result indicated that there were significant differences in N leaching losses between treatments during the rice growing season. Total N leaching was significantly lower with the application of composted rice straw plus soybean cake (0.58 kg N ha( - 1)) than with ammonium sulfate (2.41 kg N ha( - 1)), which resulted in N leaching at a similar level to that with the fresh clover treatment (no significant difference). The majority of this N leaching was not due to NO(3) ( - )-N loss, but to that of NH(4) ( + )-N. The mean N leaching for all fertilizer treatments during the entire rice growing season was 1.58 kg N ha( - 1). Composted rice straw plus soybean cake produced leaching losses which were 65-75% lower than those with the application of fresh clover and ammonium sulfate. N accumulation resulting from nitrification in the fallow season could be a key source of nitrate-N leaching when fields become re-flooded before rice transplanting in the following year; particular attention should be paid to this phenomenon.

Fractionation and leachability of heavy metals from aged and recent Zn metallurgical leach residues from the Três Marias zinc plant (Minas Gerais, Brazil).

PubMed

Sethurajan, Manivannan; Huguenot, David; Lens, Piet N L; Horn, Heinrich A; Figueiredo, Luiz H A; van Hullebusch, Eric D

2016-04-01

Various mineral processing operations to produce pure metals from mineral ores generate sludges, residues, and other unwanted by-products/wastes. As a general practice, these wastes are either stored in a reservoir or disposed in the surrounding of mining/smelting areas, which might cause adverse environmental impacts. Therefore, it is important to understand the various characteristics like heavy metal leaching features and potential toxicity of these metallurgical wastes. In this study, zinc plant leach residues (ZLRs) were collected from a currently operating Zn metallurgical industry located in Minas Gerais (Brazil) and investigated for their potential toxicity, fractionation, and leachability. Three different ZLR samples (ZLR1, ZLR2, and ZLR3) were collected, based on their age of production and deposition. They mainly consisted of Fe (6-11.5 %), Zn (2.5 to 5.0 %), and Pb (1.5 to 2.5 %) and minor concentrations of Al, Cd, Cu, and Mn, depending on the sample age. Toxicity Characteristic Leaching Procedure (TCLP) results revealed that these wastes are hazardous for the environment. Accelerated Community Bureau of Reference (BCR) sequential extraction clearly showed that potentially toxic heavy metals such as Cd, Cu, Pb, and Zn can be released into the environment in high quantities under mild acidic conditions. The results of the liquid-solid partitioning as a function of pH showed that pH plays an important role in the leachability of metals from these residues. At low pH (pH 2.5), high concentrations of metals can be leached: 67, 25, and 7 % of Zn can be leached from leach residues ZLR1, ZLR2, and ZLR3, respectively. The release of metals decreased with increasing pH. Geochemical modeling of the pH-dependent leaching was also performed to determine which geochemical process controls the leachability/solubility of the heavy metals. This study showed that the studied ZLRs contain significant concentrations of non-residual extractable fractions of Zn and can be seen as a potential secondary resource for Zn.

Leaching characteristics of calcium-based compounds in MSWI Residues: From the viewpoint of clogging risk.

PubMed

Xia, Yi; Zhang, Hua; Phoungthong, Khamphe; Shi, Dong-Xiao; Shen, Wen-Hui; Shao, Li-Ming; He, Pin-Jing

2015-08-01

Leachate collection system (LCS) clogging caused by calcium precipitation would be disadvantageous to landfill stability and operation. Meanwhile, calcium-based compounds are the main constituents in both municipal solid waste incineration bottom ash (MSWIBA) and stabilized air pollution control residues (SAPCR), which would increase the risk of LCS clogging once these calcium-rich residues were disposed in landfills. The leaching behaviors of calcium from the four compounds and municipal solid waste incineration (MSWI) residues were studied, and the influencing factors on leaching were discussed. The results showed that pH was the crucial factor in the calcium leaching process. CaCO3 and CaSiO3 began leaching when the leachate pH decreased to less than 7 and 10, respectively, while Ca3(PO4)2 leached at pH<12. CaSO4 could hardly dissolve in the experimental conditions. Moreover, the sequence of the leaching rate for the different calcium-based compounds is as follows: CaSiO3>Ca3(PO4)2>CaCO3. The calcium leaching from the MSWIBA and SAPCR separately started from pH<7 and pH<12, resulting from CaCO3 and Ca3(PO4)2 leaching respectively, which was proven by the X-ray diffraction results. Based on the leaching characteristics of the different calcium compounds and the mineral phase of calcium in the incineration residues, simulated computation of their clogging potential was conducted, providing the theoretical basis for the risk assessment pertaining to LCS clogging in landfills. Copyright © 2015 Elsevier Ltd. All rights reserved.

Leaching behaviour of hazardous waste under the impact of different ambient conditions.

PubMed

Pecorini, Isabella; Baldi, Francesco; Bacchi, Donata; Carnevale, Ennio Antonio; Corti, Andrea

2017-05-01

The overall objective of this study is to provide an improved basis for the assessment of the leaching behaviour of waste marked as hazardous partly stabilised (European waste catalogue code 19 03 04 ∗ ). Four samples of hazardous partly stabilised waste were subjected to two leaching tests: up-flow column tests and batch equilibrium tests. The research was carried out in two directions: the first aims at comparing the results of the two experimental setups while the second aims at assessing the impact of different ambient conditions on the leaching behaviour of waste. Concerning this latter objective the effect of mesophilic temperature, mechanical constraints and acid environment were tested through column percolation tests. Results showed no significant differences between batch and column leaching test outcomes when comparing average concentrations calculated at a liquid to solid ratio of 10:1 l kg -1  TS. Among the tested ambient conditions, the presence of an acid environment (pH=4.5) accelerated the leaching process resulting in a higher cumulative released quantity measured on the majority of the investigated polluting substances. On the contrary, the effect of temperature and mechanical constraints seemed to not affect the process showing final contents even lower than values found for the standard test. This result was furthermore confirmed by the application of the principal component analysis. Copyright © 2016 Elsevier Ltd. All rights reserved.

Durability test on irradiated rock-like oxide fuels

NASA Astrophysics Data System (ADS)

Kuramoto, K.; Nitani, N.; Yamashita, T.

2003-06-01

For a profitable use of Pu, Japan Atomic Energy Research Institute has been promoting researches for once-through type fuels. The strategy consists of stable rock-like oxide fuel fabrication in conventional fuel facilities followed by almost complete Pu burning in LWR and disposal of chemically stable spent fuel without further processing. Because leach rates of hazardous nuclides, such as TRU and β-emitters, that have long half-lives, are very important for the evaluation of geological safety, leaching tests in deionized water at 363 K were performed with reference to the MCC-1 method. Five irradiated fuel pellets, a single phase fuel of a yttria-stabilized zirconia (YSZ) containing UO 2 (U-YSZ), two fuels of U-YSZ particle dispersed in MgAl 2O 4 (SPI) or Al 2O 3 (COR) matrix, two homogeneous-blended fuels of U-YSZ and SPI or COR powders, were submitted to the tests. Stainless steel containers with Au coating and ethylene propylene diene monomer were used as leaching vessels and packing, respectively. The evaluated normalized leach rates of Zr, U and Pu were obviously lower than those of the other important elements and nuclides. Americium, Np and especially Y showed unexpectedly high evaluated normalized leach rates. The volatile elements, Cs and I, showed enhanced leaching within particle-dispersed type fuels because of crack formation around the particle.

Leaching characteristics of calcium-based compounds in MSWI Residues: From the viewpoint of clogging risk

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xia, Yi; Institute of Waste Treatment and Reclamation, Tongji University, Shanghai 200092; Zhang, Hua, E-mail: zhanghua_tj@tongji.edu.cn

Highlights: • The leaching behavior of Ca-based compounds commonly in MSWI residues was studied. • pH is the crucial factor for calcium leaching process. • CaCO{sub 3} was the most sensitive to leaching temperature and Ca{sub 3}(PO{sub 4}){sub 2} was the least. • Ca leaching of MSWIBA and SAPCR attributed to CaCO{sub 3} and Ca{sub 3}(PO{sub 4}){sub 2} respectively. • Potential clogging ability of MSWI residues leachate in open air was calculated. - Abstract: Leachate collection system (LCS) clogging caused by calcium precipitation would be disadvantageous to landfill stability and operation. Meanwhile, calcium-based compounds are the main constituents in bothmore » municipal solid waste incineration bottom ash (MSWIBA) and stabilized air pollution control residues (SAPCR), which would increase the risk of LCS clogging once these calcium-rich residues were disposed in landfills. The leaching behaviors of calcium from the four compounds and municipal solid waste incineration (MSWI) residues were studied, and the influencing factors on leaching were discussed. The results showed that pH was the crucial factor in the calcium leaching process. CaCO{sub 3} and CaSiO{sub 3} began leaching when the leachate pH decreased to less than 7 and 10, respectively, while Ca{sub 3}(PO{sub 4}){sub 2} leached at pH < 12. CaSO{sub 4} could hardly dissolve in the experimental conditions. Moreover, the sequence of the leaching rate for the different calcium-based compounds is as follows: CaSiO{sub 3} > Ca{sub 3}(PO{sub 4}){sub 2} > CaCO{sub 3}. The calcium leaching from the MSWIBA and SAPCR separately started from pH < 7 and pH < 12, resulting from CaCO{sub 3} and Ca{sub 3}(PO{sub 4}){sub 2} leaching respectively, which was proven by the X-ray diffraction results. Based on the leaching characteristics of the different calcium compounds and the mineral phase of calcium in the incineration residues, simulated computation of their clogging potential was conducted, providing the theoretical basis for the risk assessment pertaining to LCS clogging in landfills.« less

Horse paddocks - an emerging source of agricultural water pollution

NASA Astrophysics Data System (ADS)

Masud Parvage, Mohammed; Ulén, Barbro; Kirchmann, Holger

2015-04-01

Horse farms occupy about 4% of the total agricultural land in the EU but are not well investigated with regard to their impact on water quality. Horse paddocks commonly hold horses on a limited space and the animal density often exceeds the recommended density. Therefore, paddock soils receive significant amounts of phosphorus (P) and nitrogen (N) through feed residues and deposition of faeces and urine, which can lead to nutrient build-up in the soil and subsequent losses to aquatic systems. This study characterized the potential risk of phosphorus (P) and nitrogen (N) leaching losses from Swedish horse paddocks through three stage examination of soil and water P and N status. The experiment began with a pilot study where surface soil P status and eight years of drainage P data were examined from a paddock catchment and an adjacent arable catchment both receiving similar amount of P and N over years. Results showed that there were no signi?cant differences in water-soluble P (WSP) or total P data in soils but the drainage water P concentrations, being higher in the paddock catchment (0.33 mg P l-1, mainly in dissolved reactive form) than the arable catchment (0.10 mg P l-1). In the second experiment, soil P and N status were examined in different parts of horse paddocks (feeding, grazing, and excretion areas) to identify existence of any potential hotspots for losses within the paddock. In total, seven horse farms, covering different grazing densities and soil textures representative of Swedish horse paddocks were examined. The results showed that concentrations of WSP, plant available P or P-AL (P extracted in ammonium acetate lactate solution at pH 3.75), and total N were highest in feeding and excretion areas within the paddocks. It was also observed that the WSP concentration in the paddocks was strongly correlated with horse density (R2 = 0.80, p < 0.001) and P-AL with years of paddock management (R2 = 0.78, p < 0.001). In the final experiment, topsoil columns (0-20 cm) from the different segments of the paddock were isolated and potential leaching losses of P, N and carbon (C) were measured from two representative horse paddock (a clay and a loamy sand) following simulated rainfall events in the laboratory. Results showed that the leachate concentrations and net release of P, N, and dissolved organic C (DOC) from paddock topsoils were highest in feeding and excretion areas and considerably higher from the loamy sand than the clay paddock topsoil. It was concluded that: i) horse paddocks pose a potential threat to water quality via leaching of excess P and N, ii) feeding and excretion areas are potential hotspots for highly enhanced leaching losses, and iii) paddocks established on sandy soils are particularly susceptible to high losses.

An advanced study on the hydrometallurgical processing of waste computer printed circuit boards to extract their valuable content of metals.

PubMed

Birloaga, Ionela; Coman, Vasile; Kopacek, Bernd; Vegliò, Francesco

2014-12-01

This study refers to two chemical leaching systems for the base and precious metals extraction from waste printed circuit boards (WPCBs); sulfuric acid with hydrogen peroxide have been used for the first group of metals, meantime thiourea with the ferric ion in sulfuric acid medium were employed for the second one. The cementation process with zinc, copper and iron metal powders was attempted for solutions purification. The effects of hydrogen peroxide volume in rapport with sulfuric acid concentration and temperature were evaluated for oxidative leaching process. 2M H2SO4 (98% w/v), 5% H2O2, 25 °C, 1/10 S/L ratio and 200 rpm were founded as optimal conditions for Cu extraction. Thiourea acid leaching process, performed on the solid filtrate obtained after three oxidative leaching steps, was carried out with 20 g/L of CS(NH2)2, 6g/L of Fe(3+), 0.5M H2SO4, The cross-leaching method was applied by reusing of thiourea liquid suspension and immersing 5 g/L of this reagent for each other experiment material of leaching. This procedure has lead to the doubling and, respectively, tripling, of gold and silver concentrations into solution. These results reveal a very efficient, promising and environmental friendly method for WPCBs processing. Copyright © 2014 Elsevier Ltd. All rights reserved.

Leaching of biocides from building facades: Upscaling of a local two-region leaching model to the city scale

NASA Astrophysics Data System (ADS)

Coutu, S.; Rota, C.; Rossi, L.; Barry, D. A.

2011-12-01

Facades are protected by paints that contain biocides as protection against degradation. These biocides are leached by rainfall (albeit at low concentrations). At the city scale, however, the surface area of building facades is significant, and leached biocides are a potential environmental risk to receiving waters. A city-scale biocide-leaching model was developed based on two main steps. In the first step, laboratory experiments on a single facade were used to calibrate and validate a 1D, two-region phenomenological model of biocide leaching. The same data set was analyzed independently by another research group who found empirically that biocide leachate breakthrough curves were well represented by a sum of two exponentials. Interestingly, the two-region model was found analytically to reproduce this functional form as a special case. The second step in the method is site-specific, and involves upscaling the validated single facade model to a particular city. In this step, (i) GIS-based estimates of facade heights and areas are deduced using the city's cadastral data, (ii) facade flow is estimated using local meteorological data (rainfall, wind direction) and (iii) paint application rates are modeled as a stochastic process based on manufacturers' recommendations. The methodology was applied to Lausanne, Switzerland, a city of about 200,000 inhabitants. Approximately 30% of the annually applied mass of biocides was estimated to be released to the environment.

Comparative characterization of sewage sludge compost and soil: Heavy metal leaching characteristics.

PubMed

Fang, Wen; Wei, Yonghong; Liu, Jianguo

2016-06-05

The leaching and accumulation of heavy metals are major concerns following the land application of sewage sludge compost (SSC). We comparatively characterized SSC, the reference soil, and the SSC amended soil to investigate their similarities and differences regarding heavy metal leaching behavior and then to evaluate the effect of SSC land application on the leaching behavior of soil. Results showed that organic matter, including both of particulate organic matter (POM) and dissolved organic matter (DOM), were critical factors influencing heavy metal leaching from both of SSC and the soil. When SSC was applied to soil at the application rate of 48t/ha, the increase of DOM content slightly enhanced heavy metal leaching from the amended soil over the applicable pH domain (6

Leaching behaviour of coal-ash: a case study.

PubMed

Hajarnavis, M R; Bhide, A D

2003-10-01

Leaching of trace elements from fly ash dumps to subsoil layer due to the rain water results in contamination of ground water. The ground water pollution due to fly ash deposition on land so occurring was assessed by simulating the disposal site conditions using two lysimeter with two different soils. Leachate was collected and analysed daily to help understand the phenomenon of leaching of fly-ash constituents in the environment. The trace metals and physico-chemical parameters of fly ash and soil used were measured before and after the experiment. Results of analysis of soil and fly ash samples were then compared with the results of lysimeter-I and lysimeter-II. The study reveals that metals respond differently at dumping site while reacting with soil and water.

Aluminium leaching from red mud by filamentous fungi.

PubMed

Urík, Martin; Bujdoš, Marek; Milová-Žiaková, Barbora; Mikušová, Petra; Slovák, Marek; Matúš, Peter

2015-11-01

This contribution investigates the efficient and environmentally friendly aluminium leaching from red mud (bauxite residue) by 17 species of filamentous fungi. Bioleaching experiments were examined in batch cultures with the red mud in static, 7-day cultivation. The most efficient fungal strains in aluminium bioleaching were Penicillium crustosum G-140 and Aspergillus niger G-10. The A. niger G-10 strain was capable to extract up to approximately 141 mg·L(-1) of aluminium from 0.2 g dry weight red mud. Chemical leaching with organic acids mixture, prepared according to A. niger G-10 strain's respective fungal excretion during cultivation, proved that organic acids significantly contribute to aluminium solubilization from red mud. Copyright © 2015 Elsevier Inc. All rights reserved.

Evaluation of the leaching behavior of incineration bottom ash using seawater: A comparison with standard leaching tests.

PubMed

Lin, Wenlin Yvonne; Heng, Kim Soon; Nguyen, Minh Quan; Ho, Jin Rui Ivan; Mohamed Noh, Omar Ahmad Bin; Zhou, Xue Dong; Liu, Alec; Ren, Fei; Wang, Jing-Yuan

2017-04-01

Batch and column tests were conducted on untreated incineration bottom ash (IBA) samples from two incineration plants in Singapore, using seawater as the leachant. The main objective of this study was to investigate the change in the leaching behavior of certain elements (i.e. As, Cd, Cr, Cu, Ni, Pb, Sb, Se and Zn) when IBA comes into contact with seawater. Such an investigation using seawater as leachant was not commonly carried out when investigating leaching behavior in IBA. The leaching tests were then carried out on the same IBA samples using DI water, as a comparison. Lower level of leaching was observed for Pb and Zn when seawater was used as the leachant. Cr and Sb showed significant cumulative release at Liquid-to-Solids (L/S) ratio 5 in the seawater column leaching. The influence of Dissolved Organic Carbon (DOC) on Cu leaching seems to decrease after L/S 2 when using seawater in the column test. Although the leaching behavior of IBA was affected when seawater was used, for the column test, there was no significant difference during the initial release when compared to DI water. The initial L/S fractions collected were important as the low L/S ratios represent the pore water concentration and the maximum output in an actual application. The results from this study would be useful for the future study on using IBA in marine applications. Copyright © 2016 Elsevier Ltd. All rights reserved.

A green salt-leaching technique to produce sericin/PVA/glycerin scaffolds with distinguished characteristics for wound-dressing applications.

PubMed

Aramwit, Pornanong; Ratanavaraporn, Juthamas; Ekgasit, Sanong; Tongsakul, Duangta; Bang, Nipaporn

2015-05-01

Sericin/PVA/glycerin scaffolds could be fabricated using the freeze-drying technique; they showed good physical and biological properties and can be applied as wound dressings. However, freeze-drying is an energy- and time-consuming process with a high associated cost. In this study, an alternative, solvent-free, energy- and time-saving, low-cost salt-leaching technique is introduced as a green technology to produce sericin/PVA/glycerin scaffolds. We found that sericin/PVA/glycerin scaffolds were successfully fabricated without any crosslinking using a salt-leaching technique. The salt-leached sericin/PVA/glycerin scaffolds had a porous structure with pore interconnectivity. The sericin in the salt-leached scaffolds had a crystallinity that was as high as that of the freeze-dried scaffolds. Compared to the freeze-dried scaffolds with the same composition, the salt-leached sericin/PVA/glycerin scaffolds has larger pores, a lower Young's modulus, and faster rates of biodegradation and sericin release. When cultured with L929 mouse fibroblast cells, a higher number of cells were found in the salt-leached scaffolds. Furthermore, the salt-leached scaffolds were less adhesive to the wound, which would reduce pain upon removal. Therefore, salt-leached sericin/PVA/glycerin scaffolds with distinguished characteristics were introduced as another choice of wound dressing, and their production process was simpler, more energy efficient, and saved time and money compared to the freeze-dried scaffolds. © 2014 Wiley Periodicals, Inc.

SANSMIC Validation.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Weber, Paula D.; Rudeen, David Keith; Lord, David L.

2014-08-01

SANSMIC is solution mining software that was developed and utilized by SNL in its role as geotechnical advisor to the US DOE SPR for planning purposes. Three SANSMIC leach modes - withdrawal, direct, and reverse leach - have been revalidated with multiple test cases for each mode. The withdrawal mode was validated using high quality data from recent leach activity while the direct and reverse modes utilized data from historical cavern completion reports. Withdrawal results compared very well with observed data, including the location and size of shelves due to string breaks with relative leached volume differences ranging from 6more » - 10% and relative radius differences from 1.5 - 3%. Profile comparisons for the direct mode were very good with relative leached volume differences ranging from 6 - 12% and relative radius differences from 5 - 7%. First, second, and third reverse configurations were simulated in order to validate SANSMIC over a range of relative hanging string and OBI locations. The first-reverse was simulated reasonably well with relative leached volume differences ranging from 1 - 9% and relative radius differences from 5 - 12%. The second-reverse mode showed the largest discrepancies in leach profile. Leached volume differences ranged from 8 - 12% and relative radius differences from 1 - 10%. In the third-reverse, relative leached volume differences ranged from 10 - 13% and relative radius differences were %7E4 %. Comparisons to historical reports were quite good, indicating that SANSMIC is essentially the same as documented and validated in the early 1980's.« less

Copper leaching of MSWI bottom ash co-disposed with refuse: effect of short-term accelerated weathering.

PubMed

Su, Lianghu; Guo, Guangzhai; Shi, Xinlong; Zuo, Minyu; Niu, Dongjie; Zhao, Aihua; Zhao, Youcai

2013-06-01

Co-disposal of refuse with municipal solid waste incinerator (MSWI) bottom ash (IBA) either multi-layered as landfill cover or mixed with refuse could pose additional risk to the environment because of enhanced leaching of heavy metals, especially Cu. This study applied short-term accelerated weathering to IBA, and monitored the mineralogical and chemical properties of IBA during the weathering process. Cu extractability of the weathered IBA was then evaluated using standard leaching protocols (i.e. SPLP and TCLP) and co-disposal leaching procedure. The results showed that weathering had little or no beneficial effect on Cu leaching in SPLP and TCLP, which can be explained by the adsorption and complexation of Cu with DOM. However, the Cu leaching of weathered IBA was reduced significantly when situated in fresh simulated landfill leachate. This was attributed to weakening Cu complexation with fulvic acid or hydrophilic fractions and/or intensifying Cu absorption to neoformed hydr(oxide) minerals in weathered IBA. The amount of total leaching Cu and Cu in free or labile complex fraction (the fraction with the highest mobility and bio-toxicity) of the 408-h weathered IBA were remarkably decreased by 86.3% and 97.6% in the 15-day co-disposal leaching test. Accelerated weathering of IBA may be an effective pretreatment method to decrease Cu leaching prior to its co-disposal with refuse. Copyright © 2013 Elsevier Ltd. All rights reserved.

Arsenic removal from alkaline leaching solution using Fe (III) precipitation.

PubMed

Wang, Yongliang; Lv, Cuicui; Xiao, Li; Fu, Guoyan; Liu, Ya; Ye, Shufeng; Chen, Yunfa

2018-02-02

The alkaline leaching solution from arsenic-containing gold concentrate contains a large amount of arsenate ions, which should be removed because it is harmful to the production process and to the environment. In this study, conventional Fe (III) precipitation was used to remove arsenic from the leaching solution. The precipitation reaction was carried out at the normal temperature, and the effects of pH value and Fe/As ratio on the arsenic removal were investigated. The results show that the removal rate of arsenic is distinctive at different pH values, and the effect is best within the pH range of 5.25-5.96. The removal rate can be further increased by increasing the ratio of Fe/As. When the pH = 5.25-5.96 and Fe/As > 1.8, the arsenic in the solution can be reduced to below 5 mg/L. However, the crystallinity of ferric arsenate is poor, and the particle size is small, most of which is about 1 μm. The leaching toxicity test shows the leaching toxicity of precipitates gradually decreased by the increase of Fe/As. The precipitates can be stored safely as the ratio of Fe/As exceeded 2.5.

Leaching behaviour of bottom ash from RDF high-temperature gasification plants

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gori, M., E-mail: manuela.gori@dicea.unifi.it; Pifferi, L.; Sirini, P.

2011-07-15

This study investigated the physical properties, the chemical composition and the leaching behaviour of two bottom ash (BA) samples from two different refuse derived fuel high-temperature gasification plants, as a function of particle size. The X-ray diffraction patterns showed that the materials contained large amounts of glass. This aspect was also confirmed by the results of availability and ANC leaching tests. Chemical composition indicated that Fe, Mn, Cu and Cr were the most abundant metals, with a slight enrichment in the finest fractions. Suitability of samples for inert waste landfilling and reuse was evaluated through the leaching test EN 12457-2.more » In one sample the concentration of all metals was below the limit set by law, while limits were exceeded for Cu, Cr and Ni in the other sample, where the finest fraction showed to give the main contribution to leaching of Cu and Ni. Preliminary results of physical and geotechnical characterisation indicated the suitability of vitrified BA for reuse in the field of civil engineering. The possible application of a size separation pre-treatment in order to improve the chemical characteristics of the materials was also discussed.« less

Observing phthalate leaching from plasticized polymer films at the molecular level.

PubMed

Zhang, Xiaoxian; Chen, Zhan

2014-05-06

Phthalates, the most widely used plasticizers in poly(vinyl chloride) (PVC), have been extensively studied. In this paper, a highly sensitive, easy, and effective method was developed to examine short-term phthalate leaching from PVC/phthalate films at the molecular level using sum frequency generation vibrational spectroscopy (SFG). Combining SFG and Fourier transform infrared spectroscopy (FTIR), surface and bulk molecular structures of PVC/phthalate films were also comprehensively evaluated during the phthalate leaching process under various environments. The leaching processes of two phthalates, diethyl phthalate (DEP) and dibutyl phthalate (DBP), from the PVC/phthalate films with various weight ratios were studied. Oxygen plasma was applied to treat the PVC/phthalate film surfaces to verify its efficacy on preventing/reducing phthalate leaching from PVC. Our results show that DBP is more stable than DEP in PVC/phthalate films. Even so, DBP molecules were still found to very slowly leach to the environment from PVC at 30 °C, at a rate much slower than DEP. Also, the bulk DBP content substantially influences the DBP leaching. Higher DBP bulk concentration yields less stable DBP molecules in the PVC matrix, allowing molecules to leach from the polymer film more easily. Additionally, DBP leaching is very sensitive to temperature changes; higher temperature can strongly enhance the leaching process. For most cases, the oxygen plasma treatment can effectively prevent phthalate leaching from PVC films (e.g., for samples with low bulk concentrations of DBP-5 and 30 wt %). It is also capable of reducing phthalate leaching from high DBP bulk concentration PVC samples (e.g., 70 wt % DBP in PVC/DBP mixture). This research develops a highly sensitive method to detect chemicals at the molecular level as well as provides surface and bulk molecular structural changes. The method developed here is general and can be applied to detect small amounts of chemical/biological environmental contaminants.

Use of an intact core and stable-metal isotopes to examine leaching characteristics of a fluvial tailings deposit

USGS Publications Warehouse

Ranville, James F.; Smith, Kathleen S.; Lamothe, Paul J.; Jackson, Brian P.; Walton-Day, Katherine

2003-01-01

In this paper, we use Cd as an example of the utility of stable-metal isotopes in geochemical studies. In the case of Cd, after the core was partially saturated, the 111Cd spike was released as evidenced by a change in the Cd isotope ratios in the effluent. This release continued during the fully saturated leaching phase, however, the total Cd concentration did not increase. These results suggest that the 111Cd spike was retained inside the core during the unsaturated leaching phase, and only partially released as reducing conditions developed. Results from this core-leaching experiment indicate there is a large reservoir of water-soluble material within the fluvial tailings deposit, which yields elevated metal concentrations and high acidity, and which may degrade adjacent ground- and surface-water quality. Use of stable metal isotopes in this study facilitated the determination of different metal-retention processes, metal-release processes, and metal sources in the fluvial tailings deposit in response to changing geochemical conditions.

The Trace Element Geochemistry of Marine Biogenic Particulate Matter.

DTIC Science & Technology

1981-02-01

while the sample remains in the sea water suspension due to mechanical, bacterial, or autolytic decomposition, but is accelerated by suspension in the...acid leaching experiments is that which contains a very refractory component which is only partly released by HNO 3 or remains in the residual particles...significant percentages of their total concentrations remaining in the frustules after leaching with O.1N HCl. The residual Fe and Al in the sample are in

Comparison of EDTA-enhanced phytoextraction and phytostabilisation strategies with Lolium perenne on a heavy metal contaminated soil.

PubMed

Lambrechts, Thomas; Gustot, Quentin; Couder, Eléonore; Houben, David; Iserentant, Anne; Lutts, Stanley

2011-11-01

Phytoremediation is a promising and cost-effective strategy to manage heavy metal polluted sites. In this experiment, we compared simultaneously phytoextraction and phytostabilisation techniques on a Cd and Zn contaminated soil, through monitoring of plant accumulation and leaching. Lolium perenne plants were cultivated for 2 months under controlled environmental conditions in a 27.6 dm(3)-pot experiment allowing the collect of leachates. The heavy metal phytoextraction was promoted by adding Na-EDTA (0.5 g kg(-1) of soil) in watering solution. Phytostabilisation was assessed by mixing soil with steel shots (1%) before L. perenne sowing. Presence of plants exacerbated heavy metal leaching, by improving soil hydraulic conductivity. Use of EDTA for phytoextraction led to higher concentration of heavy metal in shoots. However, this higher heavy metal extraction was insufficient to satisfactory reduce the heavy metal content in soil, and led to important heavy metal leaching induced by EDTA. On the other hand, addition of steel shots efficiently decreased both Cd and Zn mobility, according to 0.01 M CaCl(2) extraction, and leaching. However, improvement of growth conditions by steel shots led to higher heavy metal mass in shoot tissues. Therefore, soil heavy metal mobility and plant metal uptake are not systematically positively correlated. Copyright © 2011 Elsevier Ltd. All rights reserved.

The effects of more extreme rainfall patterns on nitrogen leaching from a field crop system in the upper Midwest, USA

NASA Astrophysics Data System (ADS)

Hess, L.; Hinckley, E. L. S.; Robertson, G. P.; Matson, P. A.

2016-12-01

As global surface temperatures rise, the proportion of total rainfall that falls in heavy storm events is increasing in many areas, in particular the US Midwest, a major agricultural region. These changes in rainfall patterns may have consequences for ecosystem nutrient losses, especially from agricultural ecosystems. We conducted a multi-year rainfall manipulation experiment to examine how more extreme rainfall patterns affect nitrogen (N) leaching from row-crop ecosystems in the upper Midwest, and to what extent tillage may moderate these effects. 5x5m rainout shelters were installed in April 2015 to impose control and extreme rainfall patterns in replicated plots under conventional tillage and no-till management at the Kellogg Biological Station LTER site. Plots exposed to the control rainfall treatment received ambient rainfall, and those exposed to the extreme rainfall treatment received the same total amount of water but applied once every 2 weeks, to simulate larger, less frequent storms. N leaching was calculated as the product of measured soil water N concentrations and modeled soil water drainage at 1.2m depth using HYDRUS-1D. Based on data to date, more N has been leached from both tilled and no-till soils exposed to the extreme rainfall treatment compared to the control rainfall treatment. Results thus far suggest that greater soil water drainage is a primary driver of this increase, and changes in within-system nitrogen cycling - such as net N mineralization and crop N uptake - may also play a role. The experiment is ongoing, and our results so far suggest that intensifying precipitation patterns may exacerbate N leaching from agricultural soils, with potentially negative consequences for receiving ground- and surface waters, as well as for farmers.

Bone char effects on soil: sequential fractionations and XANES spectroscopy

NASA Astrophysics Data System (ADS)

Morshedizad, Mohsen; Panten, Kerstin; Klysubun, Wantana; Leinweber, Peter

2018-01-01

The acceptability of novel bone char fertilizers depends on their P release, but reactions at bone char surfaces and impacts on soil P speciation are insufficiently known. By using sequential fractionation and synchrotron-based X-ray absorption near-edge structure (XANES) spectroscopy we investigated whether and how the chemical composition of bone char particles has been altered in soil and has consequently affected the P speciation of amended soils. Therefore, two different kinds of bone char particles (BC produced by the pyrolysis of degreased animal bone chips at 800 °C and BCplus, a BC enriched with reduced sulfur compounds) were manually separated from the soil at the end of two different experiments: incubation leaching and ryegrass cultivation. Sequential P fractionation of amended soils showed P enrichment in all fractions compared to the control. The most P increase between all treatments significantly occurred in the NaOH-P and resin-P fractions in response to BCplus application in both incubation-leaching and ryegrass cultivation experiments. This increase in the readily available P fraction in BCplus-treated soils was confirmed by linear combination fitting (LCF) analysis on P K-edge XANES spectra of BC particles and amended soils. The proportion of Ca hydroxyapatite decreased, whereas the proportion of CaHPO4 increased in BCplus particles after amended soils had been incubated and leached and cropped by ryegrass. Based on P XANES speciation as determined by LCF analysis, the proportion of inorganic Ca(H2PO4)2 increased in amended soils after BCplus application. These results indicate that soil amendment with BCplus particles leads to elevated P concentration and maintains more soluble P species than BC particles even after 230 days of ryegrass cultivation.

Biogeochemical transfer and dynamics of iodine in a soil-plant system.

PubMed

Weng, Huan-Xin; Yan, Ai-Lan; Hong, Chun-Lai; Qin, Ya-Chao; Pan, Lehua; Xie, Ling-Li

2009-06-01

Radioactive iodide (125I) is used as a tracer to investigate the fate and transport of iodine in soil under various leaching conditions as well as the dynamic transfer in a soil-plant (Chinese cabbage) system. Results show that both soils (the paddy soil and the sandy soil) exhibit strong retention capability, with the paddy soil being slightly stronger. Most iodine is retained by soils, especially in the top 10 cm, and the highest concentration occurs at the top most section of the soil columns. Leaching with 1-2 pore volume water does not change this pattern of vertical distributions. Early breakthrough and long tailing are two features observed in the leaching experiments. Because of the relatively low peak concentration, the early breakthrough is really not an environmental concern of contamination to groundwater. The long tailing implies that the retained iodine is undergoing slow but steady release and the soils can provide a low but stable level of mobile iodine after a short period. The enrichment factors of 125I in different plant tissues are ranked as: root > stem > petiole > leaf, and the 125I distribution in the young leaves is obviously higher than that in the old ones. The concentrations of 125I in soil and Chinese cabbage can be simulated with a dual-chamber model very well. The biogeochemical behaviors of iodine in the soil-cabbage system show that cultivating iodized cabbage is an environmentally friendly and effective technique to eliminate iodine deficiency disorders (IDD). Planting vegetables such as cabbage on the 129I-contaminated soil could be a good remediation technique worthy of consideration.

Recovery of valuable metals from spent lithium-ion batteries by ultrasonic-assisted leaching process

NASA Astrophysics Data System (ADS)

Li, Li; Zhai, Longyu; Zhang, Xiaoxiao; Lu, Jun; Chen, Renjie; Wu, Feng; Amine, Khalil

2014-09-01

The anticipated significant use of lithium-ion batteries (LIBs) for energy storage applications in electric grid modernization and vehicle electrification shall generate a large quantity of solid waste that could become potential environmental hazards and waste natural resources. Recycling of the major components from spent LIBs is, therefore, considered desirable to prevent environmental pollution and to recycle valuable metals. This study reports on the application of ultrasonic-assisted technology to the leaching of cobalt and lithium from the cathode active materials of spent LIBs. Three acids were tested for the leaching process: two inorganic acids (H2SO4 and HCl) and one organic acid (citric acid, C6H8O7·H2O). The results show that the leaching of Co and Li is more efficient with citric acid than with the two inorganic acids. More than 96% Co and nearly 100% Li were recovered from spent LIBs. The optimal leaching conditions were 0.5 M citric acid with 0.55 M H2O2, a solid-to-liquid ratio of 25 g L-1, a temperature of 60 °C, leaching time of 5 h, and ultrasonic power of 90 W. The high leaching efficiency is mainly ascribed to the unique cavitation action of the ultrasonic waves. This ultrasonic-assisted leaching process with organic acid is not only effective but also environmentally friendly.

Leaching assessment of road materials containing primary lead and zinc slags.

PubMed

Barna, R; Moszkowicz, P; Gervais, C

2004-01-01

Characterisation of the leaching behaviour of waste-containing materials is a crucial step in the environmental assessment for reuse scenarios. In our research we applied the multi-step European methodology ENV 12-920 to the leaching assessment of road materials containing metallurgical slag. A Zn slag from an imperial smelting furnace (ISF) and a Pb slag from a lead blast furnace (LBF) are investigated. The two slags contain up to 11.2 wt% of lead and 3.5 wt% of zinc and were introduced as a partial substitute for sand in two road materials, namely sand-cement and sand-bitumen. At the laboratory scale, a leaching assessment was performed first through batch equilibrium leaching tests. Second, the release rate of the contaminants was evaluated using saturated leaching tests on monolithic material. Third, laboratory tests were conducted on monolithic samples under intermittent wetting conditions. Pilot-scale tests were conducted for field testing of intermittent wetting conditions. The results show that the release of Pb and Zn from the materials in a saturated scenario was controlled by the pH of the leachates. For the intermittent wetting conditions, an additional factor, blocking of the pores by precipitation during the drying phase is proposed. Pilot-scale leaching behaviour only partially matched with the laboratory-scale test results: new mass transfer mechanisms and adapted laboratory leaching tests are discussed.

A hydrometallurgical process for the recovery of terbium from fluorescent lamps: Experimental design, optimization of acid leaching process and process analysis.

PubMed

Innocenzi, Valentina; Ippolito, Nicolò Maria; De Michelis, Ida; Medici, Franco; Vegliò, Francesco

2016-12-15

Terbium and rare earths recovery from fluorescent powders of exhausted lamps by acid leaching with hydrochloric acid was the objective of this study. In order to investigate the factors affecting leaching a series of experiments was performed in according to a full factorial plan with four variables and two levels (4 2 ). The factors studied were temperature, concentration of acid, pulp density and leaching time. Experimental conditions of terbium dissolution were optimized by statistical analysis. The results showed that temperature and pulp density were significant with a positive and negative effect, respectively. The empirical mathematical model deducted by experimental data demonstrated that terbium content was completely dissolved under the following conditions: 90 °C, 2 M hydrochloric acid and 5% of pulp density; while when the pulp density was 15% an extraction of 83% could be obtained at 90 °C and 5 M hydrochloric acid. Finally a flow sheet for the recovery of rare earth elements was proposed. The process was tested and simulated by commercial software for the chemical processes. The mass balance of the process was calculated: from 1 ton of initial powder it was possible to obtain around 160 kg of a concentrate of rare earths having a purity of 99%. The main rare earths elements in the final product was yttrium oxide (86.43%) following by cerium oxide (4.11%), lanthanum oxide (3.18%), europium oxide (3.08%) and terbium oxide (2.20%). The estimated total recovery of the rare earths elements was around 70% for yttrium and europium and 80% for the other rare earths. Copyright © 2016 Elsevier Ltd. All rights reserved.

The partitioning of copper among selected phases of geologic media of two porphyry copper districts, Puerto Rico

USGS Publications Warehouse

Learned, R.E.; Chao, T.T.; Sanzolone, R.F.

1981-01-01

In experiments designed to determine the manner in which copper is partitioned among selected phases that constitute geologic media, we have applied the five-step sequential extraction procedure of Chao and Theobald to the analysis of drill core, soils, and stream sediments of the Rio Vivi and Rio Tanama porphyry copper districts of Puerto Rico. The extraction procedure affords a convenient means of determining the trace-metal content of the following fractions: (1) Mn oxides and "reactive" Fe oxides; (2) "amorphous" Fe oxides; (3) "crystalline" Fe oxides; (4) sulfides and magnetite; and (5) silicates. An additional extraction between steps (1) and (2) was performed to determine organic-related copper in stream sediments. The experimental results indicate that apportionment of copper among phases constituting geologic media is a function of geochemical environment. Distinctive partitioning patterns were derived from the analysis of drill core from each of three geochemical zones: (a) the supergene zone of oxidation; (b) the supergene zone of enrichment; and (c) the hypogene zone; and similarly, from the analysis of; (d) soils on a weakly leached capping; (e) soils on a strongly leached capping; and (f) active stream sediment. The experimental results also show that geochemical contrasts (anomaly-to-background ratios) vary widely among the five fractions of each sampling medium investigated, and that at least one fraction of each medium provides substantially stronger contrast than does the bulk medium. Fraction (1) provides optimal contrast for stream sediments of the district; fraction (2) provides optimal contrast for soils on a weakly leached capping; fraction (3) provides optimal contrast for soils on a strongly leached capping. Selective extraction procedures appear to have important applications to the orientation and interpretive stages of geochemical exploration. Further investigation and testing of a similar nature are recommended. ?? 1981.

Ammonium, Nitrate, and Phosphate Sorption to and Solute Leaching from Biochars Prepared from Corn Stover ( L.) and Oak Wood ( spp.).

PubMed

Hollister, C Colin; Bisogni, James J; Lehmann, Johannes

2013-01-01

Biochar (BC) was evaluated for nitrogen (N) and phosphorus (P) removal from aqueous solution to quantify its nutrient pollution mitigation potential in agroecosystems. Sorption isotherms were prepared for solutions of ammonium (NH), nitrate (NO), and phosphate (PO-P) using BC of corn ( L.) and oak ( spp.) feedstock, each pyrolyzed at 350 and 550°C highest treatment temperature (HTT). Sorption experiments were performed on original BC as well as on BC that went through a water extraction pretreatment (denoted WX-BC). Ammonium sorption was observed for WX-Oak-BC and WX-Corn-BC, and Freundlich model linearization showed that a 200°C increase in HTT resulted in a 55% decrease in * values for WX-Oak-BC and a 69% decrease in * for WX-Corn-BC. Nitrate sorption was not observed for any BC. Removing metals by water extraction from WX-Oak-350 and WX-Oak-550 resulted in a 25 to 100% decrease in phosphate removal efficiency relative to original Oak-350 and Oak-550, respectively. No PO-P sorption was observed using any Corn-BC. Calcium (Ca) leached from BC produced at 550°C was 63 and 104% higher than from BC produced at 350°C for corn and oak, respectively. Leaching of P was two orders of magnitude lower in WX-Oak-BC than in WX-Corn-BC, concurrent with similar difference in magnesium (Mg). Nitrate and NH leaching from consecutive water extractions of all tested BCs was mostly below detection limits. Copyright © by the American Society of Agronomy, Crop Science Society of America, and Soil Science Society of America, Inc.

A possible link between Balkan endemic nephropathy and the leaching of toxic organic compounds from Pliocene lignite by groundwater: Preliminary investigation

USGS Publications Warehouse

Orem, W.H.; Feder, G.L.; Finkelman, R.B.

1999-01-01

Balkan endemic nephropathy (BEN) is a fatal kidney disease that is known to occur only in clusters of villages in alluvial valleys of tributaries of the Danube River in Bulgaria, Romania, Yugoslavia, Bosnia, and Croatia. The confinement of this disease to a specific geographic area has led to speculation that an environmental factor may be involved in the etiology of BEN. Numerous environmental factors have been suggested as causative agents for producing BEN, including toxic metals in drinking water, metal deficiency in soils of BEN areas, and environmental mycotoxins to name a few. These hypotheses have either been disproved or have failed to conclusively demonstrate a connection to the etiology of BEN, or the clustering of BEN villages. In previous work, we observed a distinct geographic relationship between the distribution of Pliocene lignites in the Balkans and BEN villages. We hypothesized that the long-term consumption of well water containing toxic organic compounds derived from the leaching of nearby Pliocene lignites by groundwater was a primary factor in the etiology of BEN. In our current work, chemical analysis using 13C nuclear magnetic resonance (13CNMR) spectroscopy indicated a high degree of organic functionality in Pliocene lignite from the Balkans, and suggested that groundwater can readily leach organic matter from these coal beds. Semi-quantitative gas chromatography/mass spectroscopy analysis of solvent extracts of groundwater from shallow wells in BEN villages indicated the presence of potentially toxic aromatic compounds, such as napthalene, fluorene, phenanthrene, and pyrene at concentrations in the ppb range. Laboratory leaching of Balkan Pliocene lignites with distilled water yielded soluble organic matter (> 500 MW) containing large amounts of aromatic structures similar to the simple/discrete aromatic compounds detected in well water from BEN villages. These preliminary results are permissive of our hypothesis and suggest that further work on the possible relationship between the etiology of BEN and toxic aromatic substances leached from Pliocene lignites in well water is warranted.A distinct geographic relationship between the distribution of Pliocene lignites in the Balkans and villages where Balkan endemic nephropathy (BEN) occurs has been observed, indicating a possible link between BEN and the long-term consumption of well water containing toxic organic compounds derived from the leaching of nearby Pliocene lignites. Preliminary investigations by NMR spectroscopy, gas chromatography/mass spectroscopy and leaching experiments show a high degree of organic functionality in the Pliocene lignites, high-leachability by groundwater of organic matter from these beds, and the presence of toxic aromatic compounds.

Development of Biomimetic Hybrid Porous Scaffold of Chitosan/Polyvinyl Alcohol/Carboxymethyl Cellulose by Freeze-Dried and Salt Leached Technique.

PubMed

Kanimozhi, K; Basha, S Khaleel; Kumari, V Sugantha; Kaviyarasu, K

2018-07-01

Freeze drying and salt leaching methods were applied to fabricate Chitosan/Poly(vinyl alcohol)/Carboxymethyl cellulose (CPCMC) biomimetic porous scaffolds for soft tissue engineering. The properties of these scaffolds were investigated and compared to those by freeze drying and salt leaching methods respectively. The salt-leached CS/PVA/CMC scaffolds were easily formed into desired shapes with a uniformly distributed and interconnected pore structure with an average pore size. The mechanical strength of the scaffolds increased with the porosity, and were easily modulated by the addition of carboxymethyl cellulose. The morphology of the porous scaffolds observed using a SEM exhibited good porosity and interconnectivity of pores. MTT assay using L929 fibroblast cells demonstrated that the cell viability of the porous scaffold was good. Scaffolds prepared by salt leached method show larger swelling capacity, and mechanical strength, potent antibacterial activity and more cell viability than freeze dried method. It is found that salt leaching method has distinguished characteristics of simple, efficient, feasible and less economic than freeze dried scaffolds.

Dissolution characteristics of sericite in chalcopyrite bioleaching and its effect on copper extraction

NASA Astrophysics Data System (ADS)

Dong, Ying-bo; Li, Hao; Lin, Hai; Zhang, Yuan

2017-04-01

The effects of sericite particle size, rotation speed, and leaching temperature on sericite dissolution and copper extraction in a chalcopyrite bioleaching system were examined. Finer particles, appropriate temperature and rotation speed for Acidithiobacillus ferrooxidans resulted in a higher Al3+ dissolution concentration. The Al3+ dissolution concentration reached its highest concentration of 38.66 mg/L after 48-d leaching when the sericite particle size, temperature, and rotation speed were -43 μm, 30°C, and 160 r/min, respectively. Meanwhile, the sericite particle size, rotation speed, and temperature can affect copper extraction. The copper extraction rate is higher when the sericite particle size is finer. An appropriately high temperature is favorable for copper leaching. The dissolution of sericite fitted the shrinking core model, 1-(2/3) α-(1- α)2/3 = k 1 t, which indicates that internal diffusion is the decision step controlling the overall reaction rate in the leaching process. Scanning electron microscopy analysis showed small precipitates covered on the surface of sericite after leaching, which increased the diffusion resistance of the leaching solution and dissolved ions.

Formation of nickel and copper ferrites in ceramics: a potential reaction in the reuse of iron-rich sludge incineration ash.

PubMed

Shih, Kaimin

2012-12-01

This study investigates potential solid-state reactions for the stabilization of hazardous metals when reusing the incineration ash from chemically enhanced primary treatment (CEPT) sludge to fabricate ceramic products. Nickel and copper were used as examples of hazardous metals, and the iron content in the reaction system was found to play a major role in incorporating these hazardous metals into their ferrite phases (NiFe2O4 and CuFe2O4). The results from three-hour sintering experiments on NiO + Fe2O3 and CuO + Fe2O3 systems clearly demonstrate the potential for initiating metal incorporation mechanisms using an iron-containing precursor at attainable ceramic sintering temperatures (above 750 degrees C). Both ferrite phases were examined using a prolonged leaching experiment modified from the widely used toxicity characteristic leaching procedure (TCLP) to evaluate their long-term metal leachability. The leaching results indicate that both the NiFe2O4 and the CuFe2O4 products were significantly superior to their oxide forms in immobilizing hazardous metals.

Si-based technologies for reduction of the pollutant leaching from landfills and mine tails.

PubMed

Bocharnikova, E; Matichenkov, V; Jiang, J; Yuejin, C

2017-07-01

Monosilicic and polysilicic acids were shown to react with different types of the pollutants. The direction of these reactions can be managed by changing the monosilicic and polysilicic acid concentration in soil or water media. The objective of this study was to determine the effect of Si-treated calcium metallurgical slag and battery slag on the As, Se, Cd, Pb, Ni, Cr, and Hg mobility and bioavailability in mine tailings (Xikuangshan mine, Hunan, China). The results of column experiment showed that the Si-activated slags reduced leaching of As, Se, Cd, Pb, Ni, Cr, and Hg by 13-89% and transformed them into plant-unavailable forms. The greenhouse test has demonstrated that the Si-treated slags provided reinforced plant resistance to heavy metal toxicity and reduced pollutants in barley and pea leaves. Si-treated local solid slags could be used for creating the biogeochemical barriers on the pollutant streams from landfills or mine tailings sites.

Zinc bioleaching from an iron concentrate using Acidithiobacillus ferrooxidans strain from Hercules Mine of Coahuila, Mexico

NASA Astrophysics Data System (ADS)

Núñez-Ramírez, Diola Marina; Solís-Soto, Aquiles; López-Miranda, Javier; Pereyra-Alférez, Benito; Rutiaga-Quiñónes, Miriam; Medina-Torres, Luis; Medrano-Roldán, Hiram

2011-10-01

The iron concentrate from Hercules Mine of Coahuila, Mexico, which mainly contained pyrite and pyrrhotite, was treated by the bioleaching process using native strain Acidithiobacillus ferrooxidans ( A. ferrooxidans) to determine the ability of these bacteria on the leaching of zinc. The native bacteria were isolated from the iron concentrate of the mine. The bioleaching experiments were carried out in shake flasks to analyze the effects of pH values, pulp density, and the ferrous sulfate concentration on the bioleaching process. The results obtained by microbial kinetic analyses for the evaluation of some aspects of zinc leaching show that the native bacteria A. ferrooxidans, which is enriched with a 9K Silverman medium under the optimum conditions of pH 2.0, 20 g/L pulp density, and 40 g/L FeSO4, increases the zinc extraction considerably observed by monitoring during15 d, i.e., the zinc concentration has a decrease of about 95% in the iron concentrate.

Remediation of chromium-slag leakage with electricity cogeneration via a urea-Cr(VI) cell

PubMed Central

Yu, Binbin; Zhang, Huimin; Xu, Wei; Li, Gang; Wu, Zucheng

2014-01-01

Chromium pollution has been historically widespread throughout the world. Most available remediation technologies often require energy consumption. This study is aimed to develop electrochemical remediation for Cr(VI) in chromium-slag leakage with self-generated electricity. Dynamic leaching experiments of chromium-slag samples were conducted to survey the release and leaching behavior of Cr(VI). Based on previous work, a unique urea-Cr(VI) was designed, in which urea was employed as the fuel and Cr(VI) from the leakage of the dichromate slag served as the oxidant. Furthermore, the electrochemical results showed that the removal percent of Cr(VI) was more than 96% after 18 h with the leakage Cr(VI) concentration of 2.69 mM. The open circuit potential (OCP) varied in the range of 1.56 ~ 1.59 V under different initial Cr(VI) leakage concentrations. The approach explores the feasibility of the promising technique without the need of energy input for simultaneous chromium-slag remediation and generation of electricity. PMID:25168513

Syntrophic effect of indigenous and inoculated microorganisms in the leaching of rare earth elements from Western Australian monazite.

PubMed

Corbett, Melissa K; Eksteen, Jacques J; Niu, Xi-Zhi; Watkin, Elizabeth Lj

2018-05-28

The unique physiochemical properties exhibited by rare earth elements (REEs) and their increasing application in high-tech industries has created a demand for secure supply lines with established recovery procedures that create minimal environmental damage. Bioleaching experiments conducted on a non-sterile monazite concentrate with a known phosphate solubilising microorganism (PSM) resulted in greater mobilisation of REEs into solution in comparison to experiments conducted on sterile monazite. By combining the native consortia with an introduced PSM, a syntrophic effect between the populations effectively leached a greater amount of REEs than either a single PSM or the indigenous population alone. With sterile monazite, Penicillium sp.CF1 inoculated experiments released a total REE concentration of 12.32 mg L -1 after incubation for 8 days, whereas on non-sterile ore, double the soluble REE concentration was recorded (23.7 mg L -1 ). Comparable effects were recorded with Enterobacter aerogenes, Pantoea agglomerans and Pseudomonas putida. Alterations in the microbial populations during bioleaching of the monazite ore were determined by diversity profiling and demonstrated noticeable changes in community inhabitants over 14 days. The presence of native Firmicutes on the monazite appears to greatly contribute to the increased leaching recorded when using non-sterile monazite for REE recovery. Copyright © 2018. Published by Elsevier Masson SAS.

Bioleaching of ilmenite and basalt in the presence of iron-oxidizing and iron-scavenging bacteria

NASA Astrophysics Data System (ADS)

Navarrete, Jesica U.; Cappelle, Ian J.; Schnittker, Kimberlin; Borrok, David M.

2013-04-01

Bioleaching has been suggested as an alternative to traditional mining techniques in extraterrestrial environments because it does not require extensive infrastructure and bulky hardware. In situ bioleaching of silicate minerals, such as those found on the moon or Mars, has been proposed as a feasible alternative to traditional extraction techniques that require either extreme heat and/or substantial chemical treatment. In this study, we investigated the biotic and abiotic leaching of basaltic rocks (analogues to those found on the moon and Mars) and the mineral ilmenite (FeTiO3) in aqueous environments under acidic (pH ˜ 2.5) and circumneutral pH conditions. The biological leaching experiments were conducted using Acidithiobacillus ferrooxidans, an iron (Fe)-oxidizing bacteria, and Pseudomonas mendocina, an Fe-scavenging bacteria. We found that both strains were able to grow using the Fe(II) derived from the tested basaltic rocks and ilmenite. Although silica leaching rates were the same or slightly less in the bacterial systems with A. ferrooxidans than in the abiotic control systems, the extent of Fe, Al and Ti released (and re-precipitated in new solid phases) was actually greater in the biotic systems. This is likely because the Fe(II) leached from the basalt was immediately oxidized by A. ferrooxidans, and precipitated into Fe(III) phases which causes a change in the equilibrium of the system, i.e. Le Chatelier's principle. Iron(II) in the abiotic experiment was allowed to build up in solution which led to a decrease in its overall release rate. For example, the percentage of Fe, Al and Ti leached (dissolved + reactive mineral precipitates) from the Mars simulant in the A. ferrooxidans experimental system was 34, 41 and 13% of the total Fe, Al and Ti in the basalt, respectively, while the abiotic experimental system released totals of only 11, 25 and 2%. There was, however, no measurable difference in the amounts of Fe and Ti released from ilmenite in the experiments with A. ferrooxidans versus the abiotic controls. P. mendocina scavenged some Fe from the rock/mineral substrates, but the overall amount of leaching was small (<2% of total Fe in rocks) when compared with the acidophilic systems. Although the mineralogy of the tested basaltic rocks was roughly similar, the surface areas of the lunar and Mars simulants varied greatly and thus were possible factors in the overall amount of metals released. Overall, our results indicate that the presence of bacteria does not increase the overall silica leaching rates of basaltic rocks; however, the presence of A. ferrooxidans does lead to enhanced release of Fe, Al and Ti and subsequent sequestration of Fe (and other metals) in Fe(III)-precipitates.

[HPLC method to determine DEHP released into blood from a disposable extracorporeal circulation tube].

PubMed

Liu, Xi; Yu, Jingjing; Li, Shen; Wang, Hong; Liu, Jiaxin

2013-08-01

We used blood as leaching medium, simulating clinical operation under maximum condition, to develop Liquid-phase extraction- High Performance Liquid Chromatography (HPLC) method for determination of plasticizer Di-(2-ethylhexyl)phthalate (DEHP) released from Disposable Extracorporeal Circulation Tube in order to lay the foundation of risk analysis of this product. The characteristic wavelength of DEHP in methanol was detected. Acetonitrile was added to the leaching blood in proportion and extracted DEHP from blood. The methodology for HPLC to quantify DEHP was established and the DEHP amount released from this disposable extracorporeal circulation tube was measured. The experiments showed good results as follows. The characteristic wavelength of DEHP was 272nm. The concentration of DEHP (5-250 microg/mL) kept good linear relationship with peak area (r=0.9999). Method sensitivity was 1 microg/mL. Precisions showed RSD<5%. The adding standard extraction Recovery Rates of 25, 100 and 250 microg DEHP standard were 61.91 +/- 3.32)%, (69.38 +/- 0.55)% and (68.47 +/- 1.15)%. The DEHP maximum amounts released from 3 sets of this disposable extracorporeal circulation tube were 204.14, 106.30 and 165.34 mg/set. Our Liquid-phase Extraction-HPLC method showed high accuracy and precision, and relatively stable recovery rate. Its operation was also convenient.

The fate of bisphenol A, 4-tert-octylphenol and 4-nonylphenol leached from plastic debris into marine water--experimental studies on biodegradation and sorption on suspended particulate matter and nano-TiO2.

PubMed

Staniszewska, Marta; Graca, Bożena; Nehring, Iga

2016-02-01

Experiments were carried out, the aim of which was to determine the leaching rates for bisphenol A (4,4'-(propane-2,2-diyl)diphenol - BPA), 4-tert-octylphenol (OP), 4-nonylphenol (NP) from polycarbonate and recycled tyre granules into the seawater. Additionally biodegradation, sorption on marine suspended particulate matter and sorption on various types of nano-TiO2 of BPA, OP, NP were studied. Experiments were carried out on plastics at various stages of degradation. The conducted experiment confirmed the flux of BPA, OP and NP from the studied plastics into seawater. The initial photodegradation of the plastic had a significant influence on the amount of the studied components released into water. During the first days of the experiment leaching was weaker from aged materials. After 60 days leaching of BPA and OP was higher for aged plastic compared to unaged. On average, suspension adsorbed OP, BPA and NP from seawater at respective levels of 37%, 75% and 100%. On the other hand, during biodegradation on average 25%, 9% and 2% of OP, BPA and NP respectively are removed from water. Nano-TiO2 of 21 nm pore size diameter adsorbed all the compounds more strongly than nano-TiO2 of 15 nm pores sized coated with Al and stearic acid. The strongest sorption (100%) on different types of nano-TiO2 was that of the most hydrophobic and more linear structured NP with just one phenol group. The weakest sorption was observed in the case of BPA, which is the least hydrophobic, and characterized by higher compared to NP and OP steric hindrance and electrostatic repulsion. Copyright © 2015 Elsevier Ltd. All rights reserved.

Physical and chemical mechanism underlying ultrasonically enhanced hydrochloric acid leaching of non-oxidative roasting of bastnaesite.

PubMed

Zhang, Dongliang; Li, Mei; Gao, Kai; Li, Jianfei; Yan, Yujun; Liu, Xingyu

2017-11-01

In this study, we investigated an alternative to the conventional hydrochloric acid leaching of roasted bastnaesite. The studies suggested that the rare earth oxyfluorides in non-oxidatively roasted bastnaesite can be selectively leached only at elevated temperatures Further, the Ce(IV) in oxidatively roasted bastnaesite does not leach readily at low temperatures, and it is difficult to induce it to form a complex with F - ions in order to increase the leaching efficiency. Moreover, it is inevitably reduced to Ce(III) at elevated temperatures. Thus, the ultrasonically-assisted hydrochloric acid leaching of non-oxidatively roasted bastnaesite was studied in detail, including, the effects of several process factors and the, physical and chemical mechanisms underlying the leaching process. The results show that the leaching rate for the ultrasonically assisted process at 55°C (65% rare earth oxides) is almost the same as that for the conventional leaching process at 85°C. Based on the obtained results, it is concluded that ultrasonic cavitation plays a key role in the proposed process, resulting not only in a high shear stress, which damages the solid surface, but also in the formation of hydroxyl radicals (OH) and hydrogen peroxide (H 2 O 2 ). Standard electrode potential analysis and experimental results indicate that Ce(III) isoxidized by the hydroxyl radicals to Ce(IV), which can be leached with F - ions in the form of a complex, and that the Ce(IV) can subsequently be reduced to Ce(III) by the H 2 O 2. This prevents the Cl - ions in the solution from being oxidized to form chlorine. These results imply that the ultrasonically-assisted process can be used for the leaching of non-oxidatively roasted bastnaesite at low temperatures in the absence of a reductant. Copyright © 2017 Elsevier B.V. All rights reserved.

Comparative leaching of six toxic metals from raw and chemically stabilized MSWI fly ash using citric acid.

PubMed

Wang, Huawei; Fan, Xinxiu; Wang, Ya-Nan; Li, Weihua; Sun, Yingjie; Zhan, Meili; Wu, Guizhi

2018-02-15

The leaching behavior of six typical toxic metals (Pb, Zn, Cr, Cd, Cu and Ni) from raw and chemically stabilized (phosphate and chelating agent) municipal solid waste incineration (MSWI) fly ash were investigated using citric acid. Leaching tests indicated that phosphate stabilization can effectively decrease the leaching of Zn, Cd and Cr; whereas chelating agent stabilization shows a strong ability to lower the release of Pb, Cd and Cu, but instead increases the solubility of Zn and Cr at low pH conditions. Sequential extraction results suggested that the leaching of Pb, Zn and Cd in both the stabilized MSWI fly ash samples led to the decrease in Fe/Mn oxide fraction and the increase in exchangeable and carbonate fractions. The leaching of Cr was due to the decrease in exchangeable, carbonate and Fe/Mn oxide fractions in phosphate-stabilized and chelating agent-stabilized MSWI fly ash. The leaching of Cu in both stabilized MSWI fly ash was greatly ascribed to the decrease in Fe/Mn oxide and oxidisable fractions. Moreover, predicted curves by geochemical model indicated that both stabilized MSWI fly ash have the risk of releasing toxic metals under strong acid environment. Copyright © 2017 Elsevier Ltd. All rights reserved.

Dynamic leaching behavior of geogenic As in soils after cement-based stabilization/solidification.

PubMed

Li, Jiang-Shan; Wang, Lei; Tsang, Daniel C W; Beiyuan, Jingzi; Poon, Chi Sun

2017-12-01

Cement-based stabilization/solidification (S/S) is a practical treatment approach for hazardous waste with anthropogenic As sources; however, its applicability for geogenic As-containing soil and the long-term leaching potential remain uncertain. In this study, semi-dynamic leaching test was performed to investigate the influence of S/S binders (cement blended with fuel ash (FA), furnace bottom ash (FBA), or ground granulated blast furnace slag (GGBS)) on the long-term leaching characteristics of geogenic As. The results showed that mineral admixtures with higher Ca content and pozzolanic activity were more effective in reducing the leached As concentrations. Thus, cement blended with FBA was inferior to other binders in suppressing the As leaching, while 20% replacement of ordinary Portland cement by GGBS was considered most feasible for the S/S treatment of As-containing soils. The leachability of geogenic As was suppressed by the encapsulation effect of solidified matrix and interlocking network of hydration products that were supported by scanning electron microscopy (SEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS) results. The long-term leaching of geogenic As from the monolithic samples was diffusion-controlled. Increasing the Ca content in the samples led to a decrease in diffusion coefficient and an increase in feasibility for "controlled utilization" of the S/S-treated soils.

Efficiency of several leaching reagents on removal of Cu, Pb, Cd, and Zn from highly contaminated paddy soil.

PubMed

Gao, Ruili; Zhu, Pengfei; Guo, Guangguang; Hu, Hongqing; Zhu, Jun; Fu, Qingling

2016-11-01

The efficiency of five different single leaching reagents (tartaric acid (TA), citric acid (CA), CaCl 2 , FeCl 3 , EDTA) and two different composite leaching reagents (CA + FeCl 3 , CA + EDTA) on removing Cu, Pb, Zn, and Cd from contaminated paddy soil in Hunan Province (in China) was studied. The results indicated that the efficiencies of CA, FeCl 3 , and EDTA on extracting Cu, Pb, Cd, and Zn from soil were greater than that of TA and CaCl 2 , and their extraction efficiencies were EDTA ≥ FeCl 3 > CA. The efficiencies of CA + FeCl 3 on extracting Cu, Pb, Cd, and Zn were higher than that of single CA or FeCl 3 . The 25 mmol L -1 CA + 20 mmol L -1 FeCl 3 was a promising composite leaching reagent for paddy soil, and it could remove Cu (57.6 %), Pb (59.3 %), Cd (84.8 %), and Zn (28.0 %), respectively. With the same amount of leaching reagent, the efficiency of continuous leaching by several times was higher than that by once. In addition, the easily reducible and oxidizable fractions of heavy metals showed significant decrease during the process of leaching.

Demonstration of the efficiency and robustness of an acid leaching process to remove metals from various CCA-treated wood samples.

PubMed

Coudert, Lucie; Blais, Jean-François; Mercier, Guy; Cooper, Paul; Janin, Amélie; Gastonguay, Louis

2014-01-01

In recent years, an efficient and economically attractive leaching process has been developed to remove metals from copper-based treated wood wastes. This study explored the applicability of this leaching process using chromated copper arsenate (CCA) treated wood samples with different initial metal loading and elapsed time between wood preservation treatment and remediation. The sulfuric acid leaching process resulted in the solubilization of more than 87% of the As, 70% of the Cr, and 76% of the Cu from CCA-chips and in the solubilization of more than 96% of the As, 78% of the Cr and 91% of the Cu from CCA-sawdust. The results showed that the performance of this leaching process might be influenced by the initial metal loading of the treated wood wastes and the elapsed time between preservation treatment and remediation. The effluents generated during the leaching steps were treated by precipitation-coagulation to satisfy the regulations for effluent discharge in municipal sewers. Precipitation using ferric chloride and sodium hydroxide was highly efficient, removing more than 99% of the As, Cr, and Cu. It appears that this leaching process can be successfully applied to remove metals from different CCA-treated wood samples and then from the effluents. Copyright © 2013 Elsevier Ltd. All rights reserved.

Leaching mechanisms of constituents from fly ash under the influence of humic acid.

PubMed

Zhao, Shengxin; Chen, Zhonglin; Shen, Jimin; Kang, Jing; Zhang, Jin; Shen, Yanqing

2017-01-05

As a low-cost material for adsorption, FA is one of the most efficient adsorbents of HA. However, the leaching of elements from FA is problematic during utilization in water treatment. In this investigation, the potential leaching behaviors of Calcium, Arsenic, Born, Chromium, and other elements from FA in HA solution were studied via batch test. The data show that HA had an effect on the leaching of each element of FA, depending on the pH, the initial concentration of HA and the addition of calcium oxide (CaO). The Langmuir isotherm could better fit the equilibrium data in different initial concentrations of HA from 10 to 100mg/L. Because of the interaction between HA and the FA leaching elements, multi-layer adsorption occurred when the initial concentration of HA was more than 100mg/L. The pH and free CaO content played major roles in HA adsorption and FA leaching. Using SEM and XRD to characterize the solid of FA being mixed with CaO treated in solution, the results demonstrated that the reaction between FA and CaO could generate crystal minerals, such as portlandite, gismondine, ettringite (AFt) and calcite, which effectively restrained the leaching of elements, reduced secondary pollution. Copyright © 2016 Elsevier B.V. All rights reserved.

The Study and Application of Hydrometallurgical Gold Leaching in the Analysis of Refractory Precious Metals

NASA Astrophysics Data System (ADS)

Yang, M.; Geng, X.; Wang, Y. L.; Li, D. X.

2017-05-01

Three orthogonal tests are separately designed for each hydrometallurgical gold leaching process to finding the optimum reaction conditions of melting gold and palladium in each process. Under the optimum condition, the determination amount of gold and palladium in aqua regia—hydrofluoric acid, Sodium thiosulfate, and potassium iodide reaches 2.87g/kg and 8.34 g/kg, 2.39g/kg and 8.12 g/kg, 2.51g/kg and 7.84g/kg. From the result, the content of gold and palladium using the leaching process of combining Aqua regia, hydrofluoric acid and hydrogen peroxide is relatively higher than the other processes. In addition, the experiment procedure of aqua regia digestion operates easily, using less equipment, and its period is short.

Metaldehyde removal from aqueous solution by adsorption and ion exchange mechanisms onto activated carbon and polymeric sorbents.

PubMed

Tao, Bing; Fletcher, Ashleigh J

2013-01-15

Metaldehyde removal from aqueous solution was evaluated using granular activated carbon (GAC), a non-functionalised hyper-cross-linked polymer Macronet (MN200) and an ion-exchange resin (S957) with sulfonic and phosphonic functional groups. Equilibrium experimental data were successfully described by Freundlich isotherm models. The maximum adsorption capacity of S957 (7.5 g metaldehyde/g S957) exceeded those of MN200 and GAC. Thermodynamic studies showed that sorption of metaldehyde onto all sorbents is endothermic and processes are controlled by entropic rather than enthalpic changes. Kinetic experiments demonstrated that experimental data for MN200 and GAC obey pseudo-second order models with rates limited by particle diffusion. Comparatively, S957 was shown to obey a pseudo-first order model with a rate-limiting step of metaldehyde diffusion through the solid/liquid interface. Results obtained suggest that metaldehyde adsorption onto MN200 and GAC are driven by hydrophobic interactions and hydrogen bonding, as leaching tendencies were high since no degradation of metaldehyde occurred. Conversely, adsorption of metaldehyde onto S957 occurs via ion-exchange processes, where sulfonic and phosphonic functionalities degrade adsorbed metaldehyde molecules and failure to detect metaldehyde in leaching studies for S957 supports this theory. Consequently, the high adsorption capacity and absence of leaching indicate S957 is promising for metaldehyde removal from source water. Copyright © 2012 Elsevier B.V. All rights reserved.

Climate Change Increasing Calcium and Magnesium Leaching from Granitic Alpine Catchments.

PubMed

Kopáček, Jiří; Kaňa, Jiří; Bičárová, Svetlana; Fernandez, Ivan J; Hejzlar, Josef; Kahounová, Marie; Norton, Stephen A; Stuchlík, Evžen

2017-01-03

Climate change can reverse trends of decreasing calcium and magnesium [Ca + Mg] leaching to surface waters in granitic alpine regions recovering from acidification. Despite decreasing concentrations of strong acid anions (-1.4 μeq L -1 yr -1 ) during 2004-2016 in nonacidic alpine lakes in the Tatra Mountains (Central Europe), the average [Ca + Mg] concentrations increased (2.5 μeq L -1 yr -1 ), together with elevated terrestrial export of bicarbonate (HCO 3 - ; 3.6 μeq L -1 yr -1 ). The percent increase in [Ca + Mg] concentrations in nonacidic lakes (0.3-3.2% yr -1 ) was significantly and positively correlated with scree proportion in the catchment area and negatively correlated with the extent of soil cover. Leaching experiments with freshly crushed granodiorite, the dominant bedrock, showed that accessory calcite and (to a lesser extent) apatite were important sources of Ca. We hypothesize that elevated terrestrial export of [Ca + Mg] and HCO 3 - resulted from increased weathering caused by accelerated physical erosion of rocks due to elevated climate-related mechanical forces (an increasing frequency of days with high precipitation amounts and air temperatures fluctuating around 0 °C) during the last 2-3 decades. These climatic effects on water chemistry are especially strong in catchments where fragmented rocks are more exposed to weathering, and their position is less stable than in soil.

Combining Nitrilotriacetic Acid and Permeable Barriers for Enhanced Phytoextraction of Heavy Metals from Municipal Solid Waste Compost by and Reduced Metal Leaching.

PubMed

Zhao, Shulan; Jia, Lina; Duo, Lian

2016-05-01

Phytoextraction has the potential to remove heavy metals from contaminated soil, and chelants can be used to improve the capabilities of phytoextraction. However, environmentally persistent chelants can cause metal leaching and groundwater pollution. A column experiment was conducted to evaluate the viability of biodegradable nitrilotriacetic acid (NTA) to increase the uptake of heavy metals (Cd, Cr, Ni, Pb, Cu, and Zn) by L. in municipal solid waste (MSW) compost and to evaluate the effect of two permeable barrier materials, bone meal and crab shell, on metal leaching. The application of NTA significantly increased the concentrations and uptake of heavy metals in . The enhancement was more pronounced at higher dosages of NTA. In the 15 mmol kg NTA treatment using a crab shell barrier, the Cr and Ni concentrations in the plant shoots increased by approximately 8- and 10-fold, respectively, relative to the control. However, the addition of NTA also caused significant heavy metal leaching from the MSW compost. Bone meal and crab shell barriers positioned between the compost and the subsoil were effective in preventing metal leaching down through the soil profile by the retention of metals in the barrier. The application of a biodegradable chelant and the use of permeable barriers is a viable form of enhanced phytoextraction to increase the removal of metals and to reduce possible leaching. Copyright © by the American Society of Agronomy, Crop Science Society of America, and Soil Science Society of America, Inc.

Non-combustible waste vitrification with plasma torch melter.

PubMed

Park, J K; Moon, Y P; Park, B C; Song, M J; Ko, K S; Cho, J M

2001-05-01

Non-combustible radioactive wastes generated from Nuclear Power Plants (NPPs) are composed of concrete, glass, asbestos, metal, sand, soil, spent filters, etc. The melting tests for concrete, glass, sand, and spent filters were carried out using a 60 kW plasma torch system. The surrogate wastes were prepared for the tests. Non-radioactive Co and Cs were added to the surrogates in order to simulate the radioactive waste. Several kinds of surrogate prepared by their own mixture or by single waste were melted with the plasma torch system to produce glassy waste forms. The characteristics of glassy waste forms were examined for the volume reduction factor (VRF) and the leach rate. The VRFs were estimated through the density measurement of the surrogates and the glassy waste forms, and were turned out to be 1.2-2.4. The EPA (Environmental Protection Agency) Toxicity Characteristic Leaching Procedure (TCLP) was used to determine the leach resistance for As, Ba, Hg, Pb, Cd, Cr, Se, Co, and Cs. The leaching index was calculated using the total content of each element in both the waste forms and the leachant. The TCLP tests resulted in that the leach rates for all elements except Co and Cs were lower than those of the Universal Treatment Standard (UTS) limits. There were no UTS limits for Co and Cs, and their leach rate & index from the experiments were resulted in around 10 times higher than those of other elements.

Cation and anion leaching and growth of Acacia saligna in bauxite residue sand amended with residue mud, poultry manure and phosphogypsum.

PubMed

Jones, B E H; Haynes, R J; Phillips, I R

2012-03-01

To examine (1) the effect of organic (poultry manure) and inorganic (residue mud and phosphogypsum) amendments on nutrient leaching losses from residue sand and (2) whether amendments improve the growth of plants in residue sand. Leaching columns were established using residue sand. The phosphogypsum-treated surface layer (0-15 cm) was amended with poultry manure and/or bauxite residue mud and the subsurface layer (15-45 cm) was either left untreated or amended with phosphogypsum. Much of the Na⁺, K⁺, Cl⁻ and SO₄²⁻ was lost during the first four leachings. Additions of phosphogypsum to both surface and subsurface layers resulted in partial neutralization of soluble alkalinity. Mean pH of leachates ranged from 8.0 to 8.4, the major cation leached was Na⁺ and the major balancing anion was SO₄²⁻ . Where gypsum was not applied to the subsurface, mean pH of leachates was 10.0-10.9, the main cation leached was still Na⁺ and the main balancing anions were a combination of SO₄²⁻ and HCO₃⁻/CO₃²⁻. At the end of the experiment, concentrations of exchangeable Na⁺ in the subsurface layers were similar regardless of whether gypsum had been applied to that layer or not. Yields of Acacia saligna were promoted by additions of poultry manure to the surface layer but unaffected by gypsum incorporation into the subsurface layer. Lack of reaction of phosphogypsum with the subsurface layer is unlikely to be a major factor limiting revegetation of residue sand since in the absence of phosphogypsum the excess Na⁺ leaches with the residual alkalinity (HCO₃⁻/CO₃²⁻) rather than SO₄²⁻.

Prolonged toxicity characteristic leaching procedure for nickel and copper aluminates.

PubMed

Shih, Kaimin; Tang, Yuanyuan

2011-04-01

The toxicity characteristic leaching procedure (TCLP) is a regulatory testing method widely employed to evaluate the environmental friendliness of waste materials. TCLP analysis provides a fast, easy and economical way to determine the mobility of waste pollutants under simulated landfill conditions. Recent studies on metal stabilization have reported the potential for nickel and copper aluminates to form in thermal treatment conditions, and suggested a more reliable method of stabilizing hazardous metals, particularly when products are to be reused. There is thus an urgent need for a convenient and effective method of quantifying metal leachability and identifying the metal leaching behavior of sparingly soluble materials. In this study, standard TCLP analysis was modified into a prolonged leaching experiment to investigate the leaching behavior of nickel and copper oxides (NiO and CuO) and their aluminates (NiAl(2)O(4), CuAl(2)O(4) and CuAlO(2)). The results demonstrate the difficulty of differentiating the leachability of highly insoluble phases, such as NiO and NiAl(2)O(4), using the standard TCLP. The prolonged TCLP method, however, confirmed NiAl(2)O(4) to have a lower degree of intrinsic leachability than NiO and that it could be expected to undergo congruent dissolution under landfill conditions. For the more soluble copper system, the aluminates were still found to possess a much lower degree of leachability, and their leaching behavior to follow an incongruent dissolution pattern. The results of this study prove prolonged TCLP analysis to be a convenient and effective way to evaluate the environmental friendliness of metal waste and to identify the leaching behavior of waste materials.

No-tillage and fertilization management on crop yields and nitrate leaching in North China Plain

PubMed Central

Huang, Manxiang; Liang, Tao; Wang, Lingqing; Zhou, Chenghu

2015-01-01

A field experiment was performed from 2003 to 2008 to evaluate the effects of tillage system and nitrogen management regimes on crop yields and nitrate leaching from the fluvo-aquic soil with a winter wheat (Triticum aestivum L.)–maize (Zea mays L.) double-cropping system. The tillage systems consisted of conventional tillage (CT) and no-tillage (NT). Three nitrogen management regimes were included: 270 kg N ha−1 of urea for wheat and 225 kg N ha−1 of urea for maize (U), 180 kg N ha−1 of urea and 90 kg N ha−1 of straw for wheat and 180 kg N of urea and 45 kg N ha−1 of straw for maize (S), 180 kg N ha−1 of urea and 90 kg N ha−1 of manure for wheat and 180 kg N ha−1 of urea and 45 kg N ha−1 of manure for maize (M). An array of tension-free pan lysimeters (50 cm × 75 cm) were installed (1.2 m deep) to measure water flow and -N movement. No significant effect of the N management regime on yields of winter wheat and maize grain was found in the 5-year rotation. Tillage systems had significant influences on -N leaching from the second year and thereafter interacted with N management regimes on -N loads during all maize seasons. The average yield-scaled -N leaching losses were in order of CTS < NTS< CTU < NTU

Radium release mechanisms during hydraulic fracturing of Marcellus Shale

NASA Astrophysics Data System (ADS)

Sharma, M.; Landis, J. D.; Renock, D. J.

2016-12-01

Wastewater co-produced with methane from Devonian Marcellus Shale is hypersaline and enriched in Ra. Recent studies find that water injected during hydraulic fracturing can leach out significant quantities of Na, Ca, Ba and Sr from solid phases in the shale over just hours to days. Here, we show with water-rock leaching experiments that the measured 226Ra/228Ra ratios of Marcellus wastewater could also derive from rapid leaching of mineral and organic phases of the shale. Radium isotopes 226Ra (t1/2 = 1600 a) and 228Ra (t1/2 = 5.8 a) are produced through radioactive decay of 238U (t1/2 = 4.5 Ga) and 232Th (t1/2 = 14 Ga), respectively. In the absence of processes that fractionate U, Th and Ra from one another, the decay rates of each parent-daughter pair become identical over 5 half-lives of the daughter radionuclide reaching a condition of secular equilibrium. Water-rock interaction may induce pronounced deviations from secular equilibrium in the water phase, however. Such is the case during hydraulic fracturing, where Ra is soluble and mobile, and is orphaned from insoluble U and Th parents. Once 226Ra and 228Ra are mobilized no fractionation between these isotopes is expected during their transport to the surface. Thus the 226Ra/228Ra ratio in wastewater provides a fingerprint of Ra source(s). Leaching Marcellus Shale with pure water under anoxic conditions releases mainly 228Ra from clays; extraction of 228Ra from radiation damaged sites is likely the dominant contributing mechanism. Using a novel isotope dilution technique we find that 90% of the Ra released in pure water partitions back onto rock (possibly clays). In comparison, leaching with high ionic strength solutions induces the release of 226Ra from mainly organics; the breakdown of organic matter in these solutions may be the driving mechanism controlling 226Ra release in solution. Radium released by high ionic strength solutions strongly partitions into water and results in the development of leachates with high 226Ra/228Ra ratios that are comparable to those of Marcellus wastewaters. Our results suggest that hydraulic fracturing using dilute HCl solution releases Ca and Na from the shale and effects rapid Ra release from the rock. Hypersaline and radioactive wastewater is thus a consequence of active leaching of shale during hydraulic fracturing.

Assessing the efficacy of corn-based bait containing antimycin-a to control common carp populations using laboratory and pond experiments

USGS Publications Warehouse

Poole, Joshua R.; Sauey, Blake W.; Amberg, Jon J.; Bajer, Przemyslaw G.

2018-01-01

Strategic use of oral toxicants could allow for practical and sustainable control schemes for the invasive common carp (Cyprinus carpio, or ‘carp’) if a toxicant selectively targeted carp and not native species. In this study, we incorporated antimycin-a (ANT-A), a known fish toxicant, into a corn-based bait and conducted a series of experiments to determine its toxicity, leaching rate, and species-specificity. Our results showed that ANT-A was lethal to carp at doses ≥ 4 mg/kg and that the amount of ANT-A that leached out of the bait in 72 h was not lethal to carp or bluegill (Lepomis macrochirus). Species-specificity trials were conducted in 227 L tanks, in which carp were stocked with three native species representing families that occur sympatrically with carp in our study region: the fathead minnow (Pimephales promelas), yellow perch (Perca flavescens) and bluegill. These trials showed high mortality of carp (46%) and fathead minnows (76%) but no significant mortality of perch or bluegill. Finally, a pond study, which used the same species composition except for fathead minnows, resulted in 37% morality among adult carp and no mortality among perch or bluegill. Our results suggest that corn-based bait that contains ANT-A could be used to selectively control carp in ecosystems dominated by percids or centrarchids, such as lakes across the Great Plains ecoregion of North America, where carp are especially problematic.

Heavy metal stabilization in contaminated road-derived sediments.

PubMed

Rijkenberg, Micha J A; Depree, Craig V

2010-02-01

There is increasing interest in the stabilization of heavy metals in road-derived sediments (RDS), to enable environmentally responsible reuse applications and circumvent the need for costly landfill disposal. To reduce the mobility of heavy metals (i.e. Cu, Pb and Zn) the effectiveness of amendments using phosphate, compost and fly ash addition were investigated using batch leaching experiments. In general, phosphate amendments of RDS were found to be ineffective at stabilizing heavy metals, despite being used successfully in soils. Phosphate amendment resulted in enhanced concentrations of dissolved organic carbon (DOC), which increased the solubilisation of heavy metals via complexation. Amendment with humified organic matter (compost) successfully stabilized Cu and Pb in high DOC leaching RDS with an optimum loading of 15-20% (w/w). Compost, however, was ineffective at stabilizing Zn. Increasing the pH by amending RDS/compost blends with 2.5-15% (w/w) coal fly ash resulted in the stabilization of Zn, Cu and Pb. However, above a pH of approximately 7.5 and 8 enhanced leaching of organic matter resulted in an increase in leached Cu and Pb, respectively. Accordingly, the optimum level of fly ash amendment for the RDS/compost blends was estimated to be ca. 10%. Boosted regression trees analysis (BRT) of the data revealed that DOC accounted for 56% and 65% of the Cu and Pb leaching, respectively, whereas pH only accounted for ca. 18% of Cu and Pb leaching. RDS sample characteristics (i.e. metal concentrations, size fractionation and organic matter content) were more important at reconciling the leaching concentrations of copper Cu (27%) than Pb (16%). The most important parameter explaining Zn leaching was pH. Overall, the choice of a suitable stabilization agent/s depends on the composition of RDS with respect to the amount of organic matter present, and the sorption chemistry of the heavy metal of interest. Copyright 2009 Elsevier B.V. All rights reserved.

Copper extraction from coarsely ground printed circuit boards using moderate thermophilic bacteria in a rotating-drum reactor.

PubMed

Rodrigues, Michael L M; Leão, Versiane A; Gomes, Otavio; Lambert, Fanny; Bastin, David; Gaydardzhiev, Stoyan

2015-07-01

The current work reports on a new approach for copper bioleaching from Printed Circuit Board (PCB) by moderate thermophiles in a rotating-drum reactor. Initially leaching of PCB was carried out in shake flasks to assess the effects of particle size (-208μm+147μm), ferrous iron concentration (1.25-10.0g/L) and pH (1.5-2.5) on copper leaching using mesophile and moderate thermophile microorganisms. Only at a relatively low solid content (10.0g/L) complete copper extraction was achieved from the particle size investigated. Conversely, high copper extractions were possible from coarse-ground PCB (20mm-long) working with increased solids concentration (up to 25.0g/L). Because there was as the faster leaching kinetics at 50°C Sulfobacillus thermosulfidooxidans was selected for experiments in a rotating-drum reactor with the coarser-sized PCB sheets. Under optimal conditions, copper extraction reached 85%, in 8days and microscopic observations by SEM-EDS of the on non-leached and leached material suggested that metal dissolution from the internal layers was restricted by the fact that metal surface was not entirely available and accessible for the solution in the case of the 20mm-size sheets. Copyright © 2015 Elsevier Ltd. All rights reserved.

Mobility of Pb, Cu, and Zn in the phosphorus-amended contaminated soils under simulated landfill and rainfall conditions.

PubMed

Cao, Xinde; Liang, Yuan; Zhao, Ling; Le, Huangying

2013-09-01

Phosphorus-bearing materials have been widely applied in immobilization of heavy metals in contaminated soils. However, the study on the stability of the initially P-induced immobilized metals in the contaminated soils is far limited. This work was conducted to evaluate the mobility of Pb, Cu, and Zn in two contrasting contaminated soils amended with phosphate rock tailing (PR) and triple superphosphate fertilizer (TSP), and their combination (P + T) under simulated landfill and rainfall conditions. The main objective was to determine the stability of heavy metals in the P-treated contaminated soils in response to the changing environment conditions. The soils were amended with the P-bearing materials at a 2:1 molar ratio of P to metals. After equilibrated for 2 weeks, the soils were evaluated with the leaching procedures. The batch-based toxicity characteristic leaching procedure (TCLP) was conducted to determine the leachability of heavy metals from both untreated and P-treated soils under simulated landfill condition. The column-based synthetic precipitation leaching procedure (SPLP) were undertaken to measure the downward migration of metals from untreated and P-treated soils under simulated rainfall condition. Leachability of Pb, Cu, and Zn in the TCLP extract followed the order of Zn > Cu > Pb in both soils, with the organic-C- and clay-poor soil showing higher metal leachability than the organic-C- and clay-rich soil. All three P treatments reduced leachability of Pb, Cu, and Zn by up to 89.2, 24.4, and 34.3 %, respectively, compared to the untreated soil, and TSP revealed more effectiveness followed by P + T and then PR. The column experiments showed that Zn had the highest downward migration upon 10 pore volumes of SPLP leaching, followed by Pb and then Cu in both soils. However, migration of Pb and Zn to subsoil and leachate were inhibited in the P-treated soil, while Cu in the leachate was enhanced by P treatment in the organic-C-rich soil. More than 73 % P in the amendments remained in the upper 0-10 cm soil layers. However, leaching of P from soluble TSP was significant with 24.3 % of P migrated in the leachate in the organic-C-poor soil. The mobility of heavy metals in the P-treated soil varies with nature of P sources, heavy metals, and soils. Caution should be taken on the multi-metal stabilization since the P amendment may immobilize some metals while promoting others' mobility. Also, attention should be paid to the high leaching of P from soluble P amendments since it may pose the risk of excessive P-induced eutrophication.

Immobilization of antimony in waste-to-energy bottom ash by addition of calcium and iron containing additives.

PubMed

Van Caneghem, Jo; Verbinnen, Bram; Cornelis, Geert; de Wijs, Joost; Mulder, Rob; Billen, Pieter; Vandecasteele, Carlo

2016-08-01

The leaching of Sb from waste-to-energy (WtE) bottom ash (BA) often exceeds the Dutch limit value of 0.32mgkg(-1) for recycling of BA in open construction applications. From the immobilization mechanisms described in the literature, it could be concluded that both Ca and Fe play an important role in the immobilization of Sb in WtE BA. Therefore, Ca and Fe containing compounds were added to the samples of the sand fraction of WtE BA, which in contrast to the granulate fraction is not recyclable to date, and the effect on the Sb leaching was studied by means of batch leaching tests. Results showed that addition of 0.5 and 2.5% CaO, 5% CaCl2, 2.5% Fe2(SO4)3 and 1% FeCl3 decreased the Sb leaching from 0.62±0.02mgkgDM(-1) to 0.20±0.02, 0.083±0.044, 0.25±0.01, 0.27±0.002 and 0.29±0.02mgkgDM(-1), respectively. Due to the increase in pH from 11.41 to 12.53 when 2.5% CaO was added, Pb and Zn leaching increased and exceeded the respective leaching limits. Addition of 5% CaCO3 had almost no effect on the Sb leaching, as evidenced by the resulting 0.53mgkgDM(-1) leaching concentration. This paper shows a complementary enhancement of the effect of Ca and Fe, by comparing the aforementioned Sb leaching results with those of WtE BA with combined addition of 2.5% CaO or 5% CaCl2 with 2.5% Fe2(SO4)3 or 1% FeCl3. These lab scale results suggest that formation of romeites with a high Ca content and formation of iron antimonate (tripuhyite) with a very low solubility are the main immobilization mechanisms of Sb in WtE BA. Besides the pure compounds and their mixtures, also addition of 10% of two Ca and Fe containing residues of the steel industry, hereafter referred to as R1 and R2, was effective in decreasing the Sb leaching from WtE BA below the Dutch limit value for reuse in open construction applications. To evaluate the long term effect of the additives, pilot plots of WtE BA with 10% of R1 and 5% and 10% of R2 were built and samples were submitted to leaching tests at regular intervals over time. The Sb leaching from untreated WtE BA was just below or above the Dutch limit value. The Sb leaching from the pilot plots of BA with additives first remained stable around 0.13mgkg(-1) but had a tendency to slightly increase after 6months, indicating the need for further research on the effect of weathering, and more specifically of carbonation, on Sb leaching from WtE BA. Copyright © 2016 Elsevier Ltd. All rights reserved.

Simulation of acid mine drainage generation around Küre VMS Deposits, Northern Turkey

NASA Astrophysics Data System (ADS)

Demirel, Cansu; Kurt, Mehmet Ali; Çelik Balci, Nurgül

2015-04-01

This study investigated comparative leaching characteristics of acidophilic bacterial strains under shifting environmental conditions at proposed two stages as formation stage or post acidic mine drainage (AMD) generation. At the first stage, initial reactions associated with AMD generation was simulated in shaking flasks containing massive pyritic chalcopyrite ore by using a pure strain Acidithiobacillus ferrooxidans and a mixed culture of Acidithiobacillus sp. mostly dominated by A. ferrooxidans and A. thiooxidans at 26oC. At the second stage, long term bioleaching experiments were carried out with the same strains at 26oC and 40oC to investigate the leaching characteristics of pyritic chalcopyrite ore under elevated heavy metal and temperature conditions. During the experiments, physicochemical characteristics (e.i. Eh, pH, EC) metal (Fe, Co, Cu, Zn) and sulfate concentration of the experimental solution were monitored during 180 days. Significant acid generation and sulfate release were determined during bioleaching of the ore by mixed acidophilic cultures containing both iron and sulfur oxidizers. In the early stage of the experiments, heavy metal release from the ore was caused by generation of acid due to accelerated bacterial oxidation of the ore. Generally high concentrations of Co and Cu were released into the solution from the experiments conducted by pure cultures of Acidithiobacillus ferrooxidans whereas high Zn and Fe was released into the solution from the mixed culture experiments. In the later stage of AMD generation and post AMD, chemical oxidation is accelerated causing excessive amounts of contamination, even exceeding the amounts resulted from bacterial oxidation by mixed cultures. Acidithibacillus ferrooxidans was found to be more effective in leaching Cu, Fe and Co at higher temperatures in contrary to mixed acidophiles that are more prone to operate at optimal moderate conditions. Moreover, decreasing Fe values are noted in bioleaching experiments with mixed acidophiles at higher temperatures. Further depleted Fe(III) values coinciding with decreasing pH may point to precipitation of secondary phases (i.e. jarosite). This study revealed that the metals (Fe, Cu, Co and Zn) released during short term leaching of the ore (34 days) are generally caused by acid produced by dissolution reactions rather than oxidation. In the long term experiments a more complex biogeochemical reactions (oxidation and dissolution) take place in conjunction. Key words: Bioleaching, AMD, heavy metal release, environment, acidophilic bacteria, Küre copper ore deposits, volcanogenic massive sulfide deposits

Regional assessment of NLEAP NO3-N leaching indices

USGS Publications Warehouse

Wylie, B.K.; Shaffer, M.J.; Hall, M.D.

1995-01-01

Nonpoint source ground water contamination by nitrate nitrogen (NO3-N) leached from agricultural lands can be substantial and increase health risks to humans and animals. Accurate and rapid methods are needed to identify and map localities that have a high potential for contamination of shallow aquifers with NO3-N leached from agriculture. Evaluation of Nitrate Leaching and Economic Analysis Package (NLEAP) indices and input variables across an irrigated agricultural area on an alluvial aquifer in Colorado indicated that all leaching indices tested were more strongly correlated with aquifer NO3-N concentration than with aquifer N mass. Of the indices and variables tested, the NO3-N Leached (NL) index was the NLEAP index most strongly associated with groundwater NO3-N concentration (r2 values from 0.37 to 0.39). NO3-N concentration of the leachate was less well correlated with ground water NO3-N concentration (r2values from 0.21 to 0.22). Stepwise regression analysis indicated that, although inorganic and organic/inorganic fertilizer scenarios had similar r2 values, the Feedlot Indicator (proximity) variable was significant over and above the NO3-N Leached index for the inorganic scenario. The analysis also showed that combination of either Movement Risk Index (MIRI) or NO3-N concentration of the leachate with the NO3-N Leached index leads to an improved regression, which provides insight into area-wide associations between agricultural activities and ground water NO3-N concentration.

Recovery of valuable metals from cathodic active material of spent lithium ion batteries: Leaching and kinetic aspects.

PubMed

Meshram, Pratima; Pandey, B D; Mankhand, T R

2015-11-01

This work is focussed on the processing of cathodic active material of spent lithium ion batteries (LIBs) to ensure resource recovery and minimize environmental degradation. The sulfuric acid leaching of metals was carried out for the recovery of all the valuable metals including nickel and manganese along with the frequently targeted metals like lithium and cobalt. The process parameters such as acid concentration, pulp density, time and temperature for the leaching of metals from the cathode powder containing 35.8% Co, 6.5% Li, 11.6% Mn and 10.06% Ni, were optimized. Results show the optimized leach recovery of 93.4% Li, 66.2% Co, 96.3% Ni and 50.2% Mn when the material was leached in 1M H2SO4 at 368 K and 50 g/L pulp density for 240 min. The need of a reductant for improved recovery of cobalt and manganese has been explained by the thermodynamic analysis (Eh-pH diagram) for these metals. Leaching of the valuable metals was found to follow the logarithmic rate law controlled by surface layer diffusion of the lixiviant reacting with the particles. The mode of leaching of the metals from the spent LIBs was further examined by chemical analysis of the samples at various stage of processing which was further corroborated by characterizing the untreated sample and the leach residues by XRD phase identification and the SEM-EDS studies. Copyright © 2015 Elsevier Ltd. All rights reserved.

Effect of acid rain pH on leaching behavior of cement stabilized lead-contaminated soil.

PubMed

Du, Yan-Jun; Wei, Ming-Li; Reddy, Krishna R; Liu, Zhao-Peng; Jin, Fei

2014-04-30

Cement stabilization is a practical approach to remediate soils contaminated with high levels of lead. However, the potential for leaching of lead out of these stabilized soils under variable acid rain pH conditions is a major environmental concern. This study investigates the effects of acid rain on the leaching characteristics of cement stabilized lead contaminated soil under different pH conditions. Clean kaolin clay and the same soil spiked with 2% lead contamination are stabilized with cement contents of 12 and 18% and then cured for 28 days. The soil samples are then subjected to a series of accelerated leaching tests (or semi-dynamic leaching tests) using a simulated acid rain leachant prepared at pH 2.0, 4.0 or 7.0. The results show that the strongly acidic leachant (pH ∼2.0) significantly altered the leaching behavior of lead as well as calcium present in the soil. However, the differences in the leaching behavior of the soil when the leachant was mildly acidic (pH ∼4.0) and neutral (pH ∼7.0) prove to be minor. In addition, it is observed that the lead contamination and cement content levels can have a considerable impact on the leaching behavior of the soils. Overall, the leachability of lead and calcium is attributed to the stability of the hydration products and their consequent influence on the soil buffering capacity and structure. Copyright © 2014 Elsevier B.V. All rights reserved.

Identifying critical nitrogen application rate for maize yield and nitrate leaching in a Haplic Luvisol soil using the DNDC model.

PubMed

Zhang, Yitao; Wang, Hongyuan; Liu, Shen; Lei, Qiuliang; Liu, Jian; He, Jianqiang; Zhai, Limei; Ren, Tianzhi; Liu, Hongbin

2015-05-01

Identification of critical nitrogen (N) application rate can provide management supports for ensuring grain yield and reducing amount of nitrate leaching to ground water. A five-year (2008-2012) field lysimeter (1 m × 2 m × 1.2 m) experiment with three N treatments (0, 180 and 240 kg Nha(-1)) was conducted to quantify maize yields and amount of nitrate leaching from a Haplic Luvisol soil in the North China Plain. The experimental data were used to calibrate and validate the process-based model of Denitrification-Decomposition (DNDC). After this, the model was used to simulate maize yield production and amount of nitrate leaching under a series of N application rates and to identify critical N application rate based on acceptable yield and amount of nitrate leaching for this cropping system. The results of model calibration and validation indicated that the model could correctly simulate maize yield and amount of nitrate leaching, with satisfactory values of RMSE-observation standard deviation ratio, model efficiency and determination coefficient. The model simulations confirmed the measurements that N application increased maize yield compared with the control, but the high N rate (240 kg Nha(-1)) did not produce more yield than the low one (120 kg Nha(-1)), and that the amount of nitrate leaching increased with increasing N application rate. The simulation results suggested that the optimal N application rate was in a range between 150 and 240 kg ha(-1), which would keep the amount of nitrate leaching below 18.4 kg NO₃(-)-Nha(-1) and meanwhile maintain acceptable maize yield above 9410 kg ha(-1). Furthermore, 180 kg Nha(-1) produced the highest yields (9837 kg ha(-1)) and comparatively lower amount of nitrate leaching (10.0 kg NO₃(-)-Nha(-1)). This study will provide a valuable reference for determining optimal N application rate (or range) in other crop systems and regions in China. Copyright © 2015 Elsevier B.V. All rights reserved.

Rare-earth leaching from Florida phosphate rock in wet-process phosphoric acid production

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liang, Haijun; Zhang, Patrick; Jin, Zhen

Phosphorite, or phosphate rock, is the most significant secondary rare-earth resource. It contains high amounts of phosphate-bearing minerals along with low contents of rare earth elements (REEs). In Florida, about 19 Mt of phosphate rock are mined annually and most are used to manufacture fertilizers using a wet process, in which sulfuric acid reacts with phosphates to produce phosphoric acid and phosphogypsum. In the wet process, REEs are also leached out into solution and eventually get lost in the leaching residue and phosphate fertilizer. Recovering REEs from Florida phosphate rock in the wet process will be beneficial to broadening rare-earthmore » availability, improving the quality of phosphoric acid product and protecting the environment. Here, this study focuses on the influences of wet-process operating conditions on REE leaching efficiency. The results indicate that REE leaching efficiency increases with phosphoric acid addition in the initial pulp. At a temperature of 75 °C, a stoichiometric ratio of sulfuric acid (H2 SO4 ) to calcium oxide (CaO) of 1.05 and a weight ratio of liquid to solid of 3.5, REE leaching efficiency reached a relatively high value of 52.82 percent. The trends of REE leaching efficiency were similar to those for phosphoric acid (P2O5 ). Extensive tests on the leaching residue showed that during leaching, about 90 percent of the REEs were released from the phosphate rock but only 52.82 percent ended up in the leaching solution. This phenomenon can be attributed to two factors: (1) the effect of phosphate ions (PO43-) in the solution, which caused REE ions to form REE phosphates and be precipitated into the leaching residue, and (2) the influence of large amounts of anions such as sulfate (SO42-), dihydrogen phosphate (H2 PO4-) and hydrogen phosphate (HPO42-) anions as well as the polar molecule H3 PO4 , which surrounded the REE cations and formed an ion atmosphere that prevented the PO43- from contacting and combining with REE cations. Finally, interaction of these two opposite effects determined the REE distribution between leaching solution and residue.« less

Rare-earth leaching from Florida phosphate rock in wet-process phosphoric acid production

DOE PAGES

Liang, Haijun; Zhang, Patrick; Jin, Zhen; ...

2017-08-01

Phosphorite, or phosphate rock, is the most significant secondary rare-earth resource. It contains high amounts of phosphate-bearing minerals along with low contents of rare earth elements (REEs). In Florida, about 19 Mt of phosphate rock are mined annually and most are used to manufacture fertilizers using a wet process, in which sulfuric acid reacts with phosphates to produce phosphoric acid and phosphogypsum. In the wet process, REEs are also leached out into solution and eventually get lost in the leaching residue and phosphate fertilizer. Recovering REEs from Florida phosphate rock in the wet process will be beneficial to broadening rare-earthmore » availability, improving the quality of phosphoric acid product and protecting the environment. Here, this study focuses on the influences of wet-process operating conditions on REE leaching efficiency. The results indicate that REE leaching efficiency increases with phosphoric acid addition in the initial pulp. At a temperature of 75 °C, a stoichiometric ratio of sulfuric acid (H2 SO4 ) to calcium oxide (CaO) of 1.05 and a weight ratio of liquid to solid of 3.5, REE leaching efficiency reached a relatively high value of 52.82 percent. The trends of REE leaching efficiency were similar to those for phosphoric acid (P2O5 ). Extensive tests on the leaching residue showed that during leaching, about 90 percent of the REEs were released from the phosphate rock but only 52.82 percent ended up in the leaching solution. This phenomenon can be attributed to two factors: (1) the effect of phosphate ions (PO43-) in the solution, which caused REE ions to form REE phosphates and be precipitated into the leaching residue, and (2) the influence of large amounts of anions such as sulfate (SO42-), dihydrogen phosphate (H2 PO4-) and hydrogen phosphate (HPO42-) anions as well as the polar molecule H3 PO4 , which surrounded the REE cations and formed an ion atmosphere that prevented the PO43- from contacting and combining with REE cations. Finally, interaction of these two opposite effects determined the REE distribution between leaching solution and residue.« less

Stabilization of carbon dioxide and chromium slag via carbonation.

PubMed

Wu, Xingxing; Yu, Binbin; Xu, Wei; Fan, Zheng; Wu, Zucheng; Zhang, Huimin

2017-08-01

As the main greenhouse gas, CO 2 is considered as a threat in the context of global warming. Many available technologies to reduce CO 2 emission was about CO 2 separation from coal combustion and geological sequestration. However, how to deal with the cost-effective storage of CO 2 has become a new challenge. Moreover, chromium pollution, the treatment of which requires huge energy consumption, has attracted people's widespread attention. This study is aimed to develop the sequestration of CO 2 via chromium slag. A dynamic leaching experiment of chromium slag was designed to testify the ability of CO 2 adsorption onto chromium slag and to release Cr(VI) for stabilization. The results showed that the accumulative amounts of Cr(VI) were ca. 2.6 mg/g released from the chromium slag after 24 h of leaching. In addition, ca. 89 mg/g CO 2 was adsorbed by using pure CO 2 in the experiment at 12 h. Calcite is the only carbonate species in the post-carbonated slag analyzed by powder X-ray diffraction and thermal analysis. The approach provides the feasibility of the utilization of chromium slag and sequestration of the carbon dioxide at the same time at ordinary temperatures and pressures.

Interactions of metallic substances and acidic ground water in the New Jersey Coastal Plan

USGS Publications Warehouse

Barringer, J.L.

1994-01-01

Four ancillary studies were undertaken in support of an investigation into the extent and distribution of corrosive ground water in the Kirkwood- Cohansey aquifer system of southern New Jersey.The ancillary studies were (1) analysis of tap-water samples for metals and the acquisition of metal data from a county study, (2) leaching experiments in which copper pipe with various types of solder were exposed to a variety of ground-water types, (3) analysis of pipe-scale deposits on plumbing from houses with wells that tap the Kirkwood-Cohansey aquifer system, and (4) measurement of corrosion rates for carbon steel and copper exposed to shallow ground water from the Kirkwood-Cohansey aquifer system. The results studies indicate that substantial concentrations of lead, copper, and zinc can leach from plumbing materials exposed to corrosive water from the Kirkwood-Cohansey aquifer system, and that leaching appears more pronounced during the summer than during the winter. The leaching experiments indicate that the corrosiveness of water, as estimated by the calculation of a corrosion index (the Aggressive Index), is related to the concentration of trace metals in the leachate.Further, although the leaching of lead-bearing solders produced lead concentrations in leachate above the Primary Drinking Water Criterion in effect at the time of the study (50 micrograms per liter), no potentially toxic levels of metals were leached from lead-free solders, although copper concentrations in some leachate samples were in excess of the Secondary Drinking Water Criterion of 1,000 micrograms per liter. Analyses of pipe-scale deposits indicate the formation of iron oxide coatings on some copper-pipe interiors exposed to untreated well water. Treated water from a public-supply system precipitated copper carbonate and copper chloride minerals. Corrosion rates measured for copper exposed to corrosive water from the Kirkwood-Cohansey aquifer system were slow (less than 0.0254 millimeters per year). Carbon-steel corrosion rates were faster; the fastest rate (0.229 millimeters per year) was measured in oxygen-saturated water.

Modeling fungicides mobility in undisturbed vineyard soil cores unamended and amended with spent mushroom substrates.

PubMed

Marín-Benito, Jesús María; Rodríguez-Cruz, María Sonia; Sánchez-Martín, María Jesús; Mamy, Laure

2015-09-01

The performance of the pesticide fate model PRZM to predict the fate of two fungicides, penconazole and metalaxyl, and the major metabolite of metalaxyl (CGA-62826), in amended and unamended vineyard soils was tested from undisturbed soils columns experiments. Three different treatments were tested in two soils: control soil (unamended), and soil amended with fresh or composted spent mushroom substrates, which correspond to common agricultural practices in Spain. Leaching experiments were performed under non-saturated flow conditions. The model was parameterized with laboratory and literature data, and using pedotransfer functions. It was first calibrated for water flow against chloride breakthrough curves. The key parameter was the hydrodynamic dispersion coefficient (DISP). No leaching of penconazole, the most hydrophobic fungicide, was observed. It remained in the top 0-8 cm of the column. In any case, simulations were highly correlated to the experimental results. On the contrary, metalaxyl and its metabolite were consistently found in the leachates. A calibration step of the Kd of metalaxyl and CGA-62826 and of DISP for CGA-62826 was necessary to obtain good prediction of the leaching of both compounds. PRZM generally simulated acceptable metalaxyl vertical distribution in the soil profiles although results were overestimated for its metabolite. Nevertheless, PRZM can be reasonably used to assess the leaching (through breakthrough curves) and vertical distribution of fungicides in amended soils, knowing their DISP values. Copyright © 2015 Elsevier Ltd. All rights reserved.

Speciation and leaching of trace metal contaminants from e-waste contaminated soils.

PubMed

Cui, Jin-Li; Luo, Chun-Ling; Tang, Chloe Wing-Yee; Chan, Ting-Shan; Li, Xiang-Dong

2017-05-05

Primitive electrical and electronic waste (e-waste) recycling activities have caused serious environmental problems. However, little is known about the speciation and leaching behaviors of metal contaminants at e-waste contaminated sites. This study investigated trace metal speciation/mobilization from e-waste polluted soil through column leaching experiments involving irrigation with rainwater for almost 2.5 years. Over the experimental period, Cu and Zn levels in the porewater were 0.14±0.08mg/L, and 0.16±0.08mg/L, respectively, increasing to 0.33±0.16mg/L, and 0.69±0.28mg/L with plant growth. The amounts of Cu, Zn, and Pb released in surface soil (0-2cm) contributed 43.8%, 22.5%, and 13.8%, respectively, to the original levels. The released Cu and Zn were primarily caused by the mobilization of the carbonate species of metals, including Cu(OH) 2 , CuCO 3 , and Zn 5 (CO 3 ) 2 (OH) 6 , and amorphous Fe/Mn oxides associated fractions characterized by sequential extraction coupling with X-ray absorption spectroscopy. During the experiments, trace metals were not detected in the effluent, and the re-sequestration of trace metals was mainly attributed to the adsorption on the abundant Fe/Mn oxides in the sub-layer soil. This study quantitatively elucidated the molecular speciation of Cu and Zn in e-waste contaminated soil during the column leaching process. Copyright © 2017 Elsevier B.V. All rights reserved.

Pollution potential leaching index as a tool to assess water leaching risk of arsenic in excavated urban soils.

PubMed

Li, Jining; Kosugi, Tomoya; Riya, Shohei; Hashimoto, Yohey; Hou, Hong; Terada, Akihiko; Hosomi, Masaaki

2018-01-01

Leaching of hazardous trace elements from excavated urban soils during construction of cities has received considerable attention in recent years in Japan. A new concept, the pollution potential leaching index (PPLI), was applied to assess the risk of arsenic (As) leaching from excavated soils. Sequential leaching tests (SLT) with two liquid-to-solid (L/S) ratios (10 and 20Lkg -1 ) were conducted to determine the PPLI values, which represent the critical cumulative L/S ratios at which the average As concentrations in the cumulative leachates are reduced to critical values (10 or 5µgL -1 ). Two models (a logarithmic function model and an empirical two-site first-order leaching model) were compared to estimate the PPLI values. The fractionations of As before and after SLT were extracted according to a five-step sequential extraction procedure. Ten alkaline excavated soils were obtained from different construction projects in Japan. Although their total As contents were low (from 6.75 to 79.4mgkg -1 ), the As leaching was not negligible. Different L/S ratios at each step of the SLT had little influence on the cumulative As release or PPLI values. Experimentally determined PPLI values were in agreement with those from model estimations. A five-step SLT with an L/S of 10Lkg -1 at each step, combined with a logarithmic function fitting was suggested for the easy estimation of PPLI. Results of the sequential extraction procedure showed that large portions of more labile As fractions (non-specifically and specifically sorbed fractions) were removed during long-term leaching and so were small, but non-negligible, portions of strongly bound As fractions. Copyright © 2017 Elsevier Inc. All rights reserved.

Hydrometallurgical recovery of heavy metals from low grade automobile shredder residue (ASR): An application of advanced Fenton process (AFP).

PubMed

Singh, Jiwan; Lee, Byeong-Kyu

2015-09-15

To investigate the leaching and recovery of heavy metals from low-grade automobile shredder residue (ASR), the effects of nitric acid (HNO3) and hydrogen peroxide (H2O2) concentrations, liquid/solid (L/S) ratio, leaching temperature and ASR particle size fractions on the heavy metal leaching rate were determined. The heavy metals were recovered by fractional precipitation and advanced Fenton process (AFP) at different pHs. The toxicity characteristic leaching procedure (TCLP) test was also performed in the residue remaining after heavy metal leaching to evaluate the potential toxicity of ASR. The heavy metal leaching efficiency was increased with increasing HNO3 and H2O2 concentrations, L/S ratio and temperature. The heavy metal leaching efficiencies were maximized in the lowest ASR size fraction at 303 K and L/S ratio of 100 mL/g. The kinetic study showed that the metal leaching was best represented by a second-order reaction model, with a value of R(2) > 0.99 for all selected heavy metals. The determined activation energy (kJ/mol) was 21.61, 17.10, 12.15, 34.50, 13.07 and 11.45 for Zn, Fe, Ni, Pb, Cd and Cr, respectively. In the final residue, the concentrations of Cd, Cr and Pb were under their threshold limits in all ASR size fractions. Hydrometallurgical metal recovery was greatly increased by AFP up to 99.96% for Zn, 99.97% for Fe, 95.62% for Ni, 99.62% for Pb, 94.11% for Cd and 96.79% for Cr. AFP is highly recommended for the recovery of leached metals from solution even at low concentrations. Copyright © 2015 Elsevier Ltd. All rights reserved.

Weatherability and Leach Resistance of Wood Impregnated with Nano-Zinc Oxide

NASA Astrophysics Data System (ADS)

Clausen, Carol A.; Green, Frederick; Nami Kartal, S.

2010-09-01

Southern pine specimens vacuum-treated with nano-zinc oxide (nano-ZnO) dispersions were evaluated for leach resistance and UV protection. Virtually, no leaching occurred in any of the nano-ZnO-treated specimens in a laboratory leach test, even at the highest retention of 13 kg/m3. However, specimens treated with high concentrations of nano-ZnO showed 58-65% chemical depletion after 12 months of outdoor exposure. Protection from UV damage after 12 months exposure is visibly obvious on both exposed and unexposed surfaces compared to untreated controls. Graying was markedly diminished, although checking occurred in all specimens. Nano-zinc oxide treatment at a concentration of 2.5% or greater provided substantial resistance to water absorption following 12 months of outdoor exposure compared to untreated and unweathered southern pine. We conclude that nano-zinc oxide can be utilized in new wood preservative formulations to impart resistance to leaching, water absorption and UV damage of wood.

The effect of lizardite surface characteristics on pyrite flotation

NASA Astrophysics Data System (ADS)

Feng, Bo; Feng, Qiming; Lu, Yiping

2012-10-01

The effect of lizardite surface characteristics on pyrite flotation has been investigated through flotation tests, adsorption tests, zeta potential measurements, FTIR study, X-ray photoelectron spectroscopy (XPS) and sedimentation tests. The flotation results show that at pH value 9, where flotation of nickel sulfide ores is routinely performed, two kinds of lizardite samples (native lizardite and leached lizardite) have different effects on the flotation of pyrite. The native lizardite adheres to the surface of pyrite and reduces pyrite flotation recovery while the leached lizardite does not interfere with pyrite flotation. Infrared analyses and XPS tests illustrate that acid leaching changed the surface characteristics of lizardite mineral and the leached lizardite has less magnesium on its surface. It has been determined that the electro-kinetic behavior of lizardite aqueous suspensions is mainly a function of the Mg/Si atomic ratio on lizardite surface. So, the low isoelectric point observed in the leached sample has been linked to values of this ratio lower than that of the native lizardite.

The composition, leaching, and sorption behavior of some alternative sources of phosphorus for soils.

PubMed

Stutter, Marc I

2015-03-01

Concerns about the sustainability of inorganic fertilizers necessitate the characterization of alternative P source materials for agronomic P-efficiencies and P losses via leaching. Firstly, this study examined nutrient compositions including P speciation of seven soil amendments: sewage sludge (SS), anaerobic digestate (AD), green compost (GC), food waste compost (FWC), chicken manure (CM), biochar, and seaweed. Secondly, soil P leaching and availability was studied on a subset of four materials (SS, AD, GC, and CM). Sorption of extracts onto columns of a test soil showed strong P retention for SS and compost, but weak P sorption for CM and especially AD, suggesting short-term leaching risks for soil applied AD. Limited P desorption with water or citrate indicated sorbed P was strongly fixed, potentially limiting crop availability. These data indicate that variation in P forms and environmental behavior should be understood to maximize P usage, but minimize leaching and soil P accumulation. Hence, different alternative P source materials need differing recommendations for their agronomic management.

Experimental design and optimization of leaching process for recovery of valuable chemical elements (U, La, V, Mo, Yb and Th) from low-grade uranium ore.

PubMed

Zakrzewska-Koltuniewicz, Grażyna; Herdzik-Koniecko, Irena; Cojocaru, Corneliu; Chajduk, Ewelina

2014-06-30

The paper deals with experimental design and optimization of leaching process of uranium and associated metals from low-grade, Polish ores. The chemical elements of interest for extraction from the ore were U, La, V, Mo, Yb and Th. Sulphuric acid has been used as leaching reagent. Based on the design of experiments the second-order regression models have been constructed to approximate the leaching efficiency of elements. The graphical illustrations using 3-D surface plots have been employed in order to identify the main, quadratic and interaction effects of the factors. The multi-objective optimization method based on desirability approach has been applied in this study. The optimum condition have been determined as P=5 bar, T=120 °C and t=90 min. Under these optimal conditions, the overall extraction performance is 81.43% (for U), 64.24% (for La), 98.38% (for V), 43.69% (for Yb) and 76.89% (for Mo) and 97.00% (for Th). Copyright © 2014 Elsevier B.V. All rights reserved.

The use of a biodegradable chelator for enhanced phytoextraction of heavy metals by Festuca arundinacea from municipal solid waste compost and associated heavy metal leaching.

PubMed

Zhao, Shulan; Jia, Lina; Duo, Lian

2013-02-01

In a column experiment with horizontal permeable barriers, the effects of a biodegradable chelator-nitrilotriacetic acid (NTA) on the uptake of heavy metals from municipal solid waste (MSW) compost by Festuca arundinacea and metal leaching were investigated. The use of NTA was effective in increasing Cu, Pb, and Zn uptakes in shoots of two crops of F. arundinacea. In columns with barriers and treated with 20 mmol NTA per kg MSW compost, metal uptakes by the first and second crop of F. arundinacea were, respectively, 3.8 and 4.0 times for Pb, and 1.8 and 1.7 times for Zn greater with the added NTA than without it. Though NTA application mobilized metals, it caused only slight leaching of metals from MSW compost. Permeable barriers positioned between compost and soil effectively reduced metal leaching. NTA-assisted phytoextraction by turfgrass with permeable barriers to cleanup heavy metal contaminated MSW compost should be environmentally safe. Copyright © 2012 Elsevier Ltd. All rights reserved.

Understanding how brass ball valves passing certification testing can cause elevated lead in water when installed.

PubMed

Triantafyllidou, Simoni; Raetz, Meredith; Parks, Jeffrey; Edwards, Marc

2012-06-15

The lead leaching potential of new brass plumbing devices has come under scrutiny as a significant source of lead in drinking water (>300 μg/L) of new buildings around the world. Experiments were conducted using ball valves that were sold as certified and known to have caused problems in practice, in order to better understand how installed products could create such problems, even if they passed "leaching tests" such as National Sanitation Foundation (NSF) Standard 61 Section 8. Diffusion of lead from within the device into water when installed can increase lead leaching by orders of magnitude relative to results of NSF testing, which once only required exposure of very small volumes of water within the device. "Normalization" of the lead-in-water result tended to produce estimates of lead concentration that were much lower than actual lead measured at the tap. Finally, the presence of flux could also dramatically increase lead leaching, whereas high water velocity had relatively little effect. Copyright © 2012. Published by Elsevier Ltd.

Qualitative impact of salinity, UV radiation and turbulence on leaching of organic plastic additives from four common plastics - A lab experiment.

PubMed

Suhrhoff, Tim Jesper; Scholz-Böttcher, Barbara M

2016-01-15

Four common consumer plastic samples (polyethylene, polystyrene, polyethylene terephthalate, polyvinylchloride) were studied to investigate the impact of physical parameters such as turbulence, salinity and UV irradiance on leaching behavior of selected plastic components. Polymers were exposed to two different salinities (i.e. 0 and 35 g/kg), UV radiation and turbulence. Additives (e.g. bisphenol A, phthalates, citrates, and Irgafos® 168 phosphate) and oligomers were detected in initial plastics and aqueous extracts. Identification and quantification was performed by GC-FID/MS. Bisphenol A and citrate based additives are leached easier compared to phthalates. The print highly contributed to the chemical burden of the analyzed polyethylene bag. The study underlines a positive relationship between turbulence and magnitude of leaching. Salinity had a minor impact that differs for each analyte. Global annual release of additives from assessed plastics into marine environments is estimated to be between 35 and 917 tons, of which most are derived from plasticized polyvinylchloride. Copyright © 2015 Elsevier Ltd. All rights reserved.

LEACHING OF TITANIUM FROM MONOSODIUM TITANATE AND MODIFIED MST

DOE Office of Scientific and Technical Information (OSTI.GOV)

Taylor-Pashow, K.; Fondeur, F.; Fink, S.

2012-08-01

Analysis of a fouled coalescer and pre-filters from Actinide Removal Process/Modular Caustic Side Solvent Extraction Unit (ARP/MCU) operations showed evidence of Ti containing solids. Based on these results a series of tests were planned to examine the extent of Ti leaching from monosodium titanate (MST) and modified monosodium titanate (mMST) in various solutions. The solutions tested included a series of salt solutions with varying free hydroxide concentrations, two sodium hydroxide concentrations, 9 wt % and 15 wt %, nitric and oxalic acid solutions. Overall, the amount of Ti leached from the MST and mMST was much greater in the acidmore » solutions compared to the sodium hydroxide or salt solutions, which is consistent with the expected trend. The leaching data also showed that increasing hydroxide concentration, whether pure NaOH solution used for filter cleaning in ARP or the waste salt solution, increased the amount of Ti leached from both the MST and mMST. For the respective nominal contact times with the MST solids - for filter cleaning or the normal filter operation, the dissolved Ti concentrations are comparable suggesting either cause may contribute to the increased Ti fouling on the MCU coalescers. Tests showed that Ti containing solids could be precipitated from solution after the addition of scrub acid and a decrease in temperature similar to expected in MCU operations. FTIR analysis of these solids showed some similarity to the solids observed on the fouled coalescer and pre-filters. Although only a cursory study, this information suggests that the practice of increasing free hydroxide in feed solutions to MCU as a mitigation to aluminosilicate formation may be offset by the impact of formation of Ti solids in the overall process. Additional consideration of this finding from MCU and SWPF operation is warranted.« less

Characterization and metal availability of copper, lead, antimony and zinc contamination at four Canadian small arms firing ranges.

PubMed

Laporte-Saumure, Mathieu; Martel, Richard; Mercier, Guy

2011-01-01

Backstop soils of four small-arms firing ranges (SAFRs) of the Canadian Force Bases (CFBs) were characterized in terms of their total soil Cu, Pb, Sb and Zn concentrations, grain size distribution, mineralogy, chemical properties, vertical in-depth contamination distribution (for one CFB), and scanning electron microscope (SEM-EDS) characterization. Metal availability from the soils was evaluated with three leaching tests: the toxicity characteristics leaching procedure (TCLP), representing a landfill leachate; the synthetic precipitation leaching procedure (SPLP), representing field conditions; and the gastric juice simulation test (GJST), representing the leachate of the human stomach during the digestive process and, therefore, the potential metal transfer to humans in the case of soil ingestion. Metal analyses of soils and leaching test extracts were conducted with an Inductively Coupled Plasma Atomic Emission Spectrometry (ICP-AES) instrument. Total soil results showed maximal concentrations of 27,100 mg/kg for Pb, 7720 mg/kg for Cu, 1080 mg/kg for Zn, and 570 mg/kg for Sb. The SEM-EDS analysis showed significant amounts of lead carbonates, which resulted from the alteration of the initial metallic Pb particles. Metal availability evaluation with the leaching tests showed that TCLP Pb and Sb thresholds were exceeded. For the SPLP and the GJST, the drinking water thresholds of the Ministère du Développement Durable, de l'Environnement et des Pares (MDDEP) of Quebec were exceeded by Pb and Sb. The metal availability assessment showed that SAFR backstop soils may pose a potential risk to the environment, groundwater and humans, and affect the management of such soils in order to minimize potential metal dispersion in the environment.

Conducting LaAlO3/SrTiO3 heterointerfaces on atomically-flat substrates prepared by deionized-water

PubMed Central

Connell, J. G.; Nichols, J.; Gruenewald, J. H.; Kim, D.-W.; Seo, S. S. A.

2016-01-01

We have investigated how the recently-developed water-leaching method for atomically-flat SrTiO3 (STO) substrates affects the transport properties of LaAlO3 (LAO) and STO heterointerfaces. Using pulsed laser deposition at identical growth conditions, we have synthesized epitaxial LAO thin-films on two different STO substrates, which are prepared by water-leaching and buffered hydrofluoric acid (BHF) etching methods. The structural, transport, and optical properties of LAO/STO heterostructures grown on water-leached substrates show the same high-quality as the samples grown on BHF-etched substrates. These results indicate that the water-leaching method can be used to grow complex oxide heterostructures with atomically well-defined heterointerfaces without safety concerns. PMID:27033248

Effects of aerobic and anaerobic biological processes on leaching of heavy metals from soil amended with sewage sludge compost.

PubMed

Fang, Wen; Wei, Yonghong; Liu, Jianguo; Kosson, David S; van der Sloot, Hans A; Zhang, Peng

2016-12-01

The risk from leaching of heavy metals is a major factor hindering land application of sewage sludge compost (SSC). Understanding the change in heavy metal leaching resulting from soil biological processes provides important information for assessing long-term behavior of heavy metals in the compost amended soil. In this paper, 180days aerobic incubation and 240days anaerobic incubation were conducted to investigate the effects of the aerobic and anaerobic biological processes on heavy metal leaching from soil amended with SSC, combined with chemical speciation modeling. Results showed that leaching concentrations of heavy metals at natural pH were similar before and after biological process. However, the major processes controlling heavy metals were influenced by the decrease of DOC with organic matter mineralization during biological processes. Mineralization of organic matter lowered the contribution of DOC-complexation to Ni and Zn leaching. Besides, the reducing condition produced by biological processes, particularly by the anaerobic biological process, resulted in the loss of sorption sites for As on Fe hydroxide, which increased the potential risk of As release at alkaline pH. Copyright © 2016 Elsevier Ltd. All rights reserved.

Use of fly ash, phosphogypsum and red mud as a liner material for the disposal of hazardous zinc leach residue waste.

PubMed

Coruh, Semra; Ergun, Osman Nuri

2010-01-15

Increasing amounts of residues and waste materials coming from industrial activities in different processes have become an increasingly urgent problem for the future. The release of large quantities of heavy metals into the environment has resulted in a number of environmental problems. The present study investigated the safe disposal of the zinc leach residue waste using industrial residues such as fly ash, phosphogypsum and red mud. In the study, leachability of heavy metals from the zinc leach residue has been evaluated by mine water leaching procedure (MWLP) and toxicity characteristic leaching procedure (TCLP). Zinc removal from leachate was studied using fly ash, phosphogypsum and red mud. The adsorption capacities and adsorption efficiencies were determined. The adsorption rate data was analyzed according to the pseudo-second-order kinetic, Elovich kinetic and intra-particle diffusion kinetic models. The pseudo-second-order kinetic was the best fit kinetic model for the experimental data. The results show that addition of fly ash, phosphogypsum and red mud to the zinc leach residue drastically reduces the heavy metal content in the leachate and could be used as liner materials.

Geochemical anomalies from bottom ash in a road construction--comparison of the leaching potential between an ash road and the surroundings.

PubMed

Lind, Bo B; Norrman, Jenny; Larsson, Lennart B; Ohlsson, Sten-Ake; Bristav, Henrik

2008-01-01

A study was performed between June 2001 and December 2004 with the primary objective of assessing long-term leaching from municipal solid waste incineration bottom ash in a test road construction in relation to a reference road made up of conventional materials and the natural geochemical conditions in the surroundings. The metal leaching from the test road and the reference road was compared with the natural weathering in the regional surroundings for three time scales: 16, 80 and 1000 years. The results show that Cu and Zn cause a geochemical anomaly from the test road compared with the surroundings. The leaching of Cu from the test road is initially high but will decline with time and will in the long term be exceeded by natural weathering. Zn on the other hand has low initial leaching, which will increase with time and will in the long term exceed that of the test road and the surroundings by a factor of 100-300. For the other metals studied, Al, Na, K and Mg, there is only very limited leaching over time and the potential accumulation will not exceed the background values in a 1000 years.

Manganese ore tailing: optimization of acid leaching conditions and recovery of soluble manganese.

PubMed

Santos, Olívia de Souza Heleno; Carvalho, Cornélio de Freitas; Silva, Gilmare Antônia da; Santos, Cláudio Gouvêa Dos

2015-01-01

Manganese recovery from industrial ore processing waste by means of leaching with sulfuric acid was the objective of this study. Experimental conditions were optimized by multivariate experimental design approaches. In order to study the factors affecting leaching, a screening step was used involving a full factorial design with central point for three variables in two levels (2(3)). The three variables studied were leaching time, concentration of sulfuric acid and sample amount. The three factors screened were shown to be relevant and therefore a Doehlert design was applied to determine the best working conditions for leaching and to build the response surface. By applying the best leaching conditions, the concentrations of 12.80 and 13.64 %w/w of manganese for the global sample and for the fraction -44 + 37 μm, respectively, were found. Microbeads of chitosan were tested for removal of leachate acidity and recovering of soluble manganese. Manganese recovery from the leachate was 95.4%. Upon drying the leachate, a solid containing mostly manganese sulfate was obtained, showing that the proposed optimized method is efficient for manganese recovery from ore tailings. Copyright © 2014 Elsevier Ltd. All rights reserved.

Economical recycling process for spent lithium-ion batteries and macro- and micro-scale mechanistic study

NASA Astrophysics Data System (ADS)

Li, Li; Bian, Yifan; Zhang, Xiaoxiao; Xue, Qing; Fan, Ersha; Wu, Feng; Chen, Renjie

2018-02-01

An economical effective method is developed for recycling spent LiNi1/3Co1/3Mn1/3O2 cathodes, where more than 98% Li, Co, Ni and Mn can be leached out with different organic acids, and resynthesized to LiNi1/3Co1/3Mn1/3O2. The leaching mechanism is investigated at macro- and micro-scales. The particles undergo a loosening-breaking-shrinking change for two acids, while the FTIR and UV-vis spectra indicate different coordination reactions. The performance of LiNi1/3Co1/3Mn1/3O2 resynthesized from the leachate of the acetic acid leaching (NCM-Ac) and maleic acid leaching (NCM-Ma) are compared. The first discharge capacity of NCM-Ma and NCM-Ac at 0.2C are 151.6 and 115.0 mA h g-1, respectively. The much better performance of NCM-Ma than NCM-Ac results from the different coordination of the two acids in the sol-gel process, where the maleic acid can esterify to establish a stable network to chelate metal ions, while the weak chelation of acetic acid leads to the formation of impurities. The economics analysis including the cost of leaching acid and energy consumption shows that the price of organic acids and reducing agents, short leaching time, low temperature and high-valued products are the effective way to increase recycling and environmental benefits, which shows advantages in terms of resources cost and added value.

Treatment of Petroleum Sludge By Using Solidification/Stabilization (S/S) Method : Effect of Hydration Days to Heavy Metals Leaching and Strength

NASA Astrophysics Data System (ADS)

Murshid, N.; Kamil, N. A. F. M.; Kadir, A. A.

2018-04-01

Petroleum sludge is one of the major solid wastes generated in the petroleum industry. Generally, there are numbers of heavy metals in petroleum sludge and one treatment that is gaining prominence to treat a variety of mixed organic and inorganic waste is solidification/stabilization (S/S) method. The treatment protects human health and the environment by immobilizing contaminants within the treated material and prevents migration of the contaminants. In this study, solidification/stabilization (S/S) method has been used to treat the petroleum sludge. The comparison of hydration days, namely, 7th and 28th days in these cement-based waste materials were studied by using Synthetic Precipitate Leaching Procedure (SPLP). The results were compared to the United States Environmental Protection Agency (USEPA) standards. The results for leaching test concluded that less percentage OPC gave maximum concentration of heavy metals leaching due to deficient in Calcium Oxide (CaO), which is can caused weak solidification in the mixture. Physical and mechanical properties conducted such as compressive strength and density test. From the results, it shows addition up to of 30percentage PS give results which comply with minimum landfill dispose limit. The results shows correlation between strength and density are strong regression coefficient of 82.7%. In conclusion, S/S method can be alternative disposal method for PS in the same time complies with standard for minimum landfill disposal limit. The results for leaching test concluded the less OPC percentage gave maximum concentration of heavy metals leaching.

Toxic metal immobilization in contaminated sediment using bentonite- and kaolinite-supported nano zero-valent iron

NASA Astrophysics Data System (ADS)

Tomašević, D. D.; Kozma, G.; Kerkez, Dj. V.; Dalmacija, B. D.; Dalmacija, M. B.; Bečelić-Tomin, M. R.; Kukovecz, Á.; Kónya, Z.; Rončević, S.

2014-08-01

The objective of this study was to investigate the possibility of using supported nanoscale zero-valent iron with bentonite and kaolinite for immobilization of As, Pb and Zn in contaminated sediment from the Nadela river basin (Serbia). Assessment of the sediment quality based on the pseudo-total metal content (As, Pb and Zn) according to the corresponding Serbian standards shows its severe contamination, such that it requires disposal in special reservoirs and, if possible, remediation. A microwave-assisted sequential extraction procedure was employed to assess potential metal mobility and risk to the aquatic environment. According to these results, As showed lower risk to the environment than Pb and Zn, which both represent higher risk to the environment. The contaminated sediment, irrespective of the different speciation of the treated metals, was subjected to the same treatment. Semi-dynamic leaching test, based on leachability index and effective diffusion coefficients, was conducted for As-, Pb- and Zn-contaminated sediments in order to assess the long-term leaching behaviour. In order to simulate "worst case" leaching conditions, the test was modified using acetic and humic acid solution as leachants instead of deionized water. A diffusion-based model was used to elucidate the controlling leaching mechanisms; in the majority of samples, the controlling leaching mechanism appeared to be diffusion. Three different single-step leaching tests were applied to evaluate the extraction potential of examined metals. Generally, the test results indicated that the treated sediment is safe for disposal and could even be considered for "controlled utilization".

Hydrometallurgical Recovery of Metals from Large Printed Circuit Board Pieces.

PubMed

Jadhav, U; Hocheng, H

2015-09-29

The recovery of precious metals from waste printed circuit boards (PCBs) is an effective recycling process. This paper presents a promising hydrometallurgical process to recover precious metals from waste PCBs. To simplify the metal leaching process, large pieces of PCBs were used instead of a pulverized sample. The chemical coating present on the PCBs was removed by sodium hydroxide (NaOH) treatment prior to the hydrometallurgical treatment. Among the leaching reagents examined, hydrochloric acid (HCl) showed great potential for the recovery of metals. The HCl-mediated leaching of waste PCBs was investigated over a range of conditions. Increasing the acid concentration decreased the time required for complete metal recovery. The shaking speed showed a pronounced positive effect on metal recovery, but the temperature showed an insignificant effect. The results showed that 1 M HCl recovered all of the metals from 4 cm × 4 cm PCBs at room temperature and 150 rpm shaking speed in 22 h.

Hydrometallurgical Recovery of Metals from Large Printed Circuit Board Pieces

PubMed Central

Jadhav, U.; Hocheng, H.

2015-01-01

The recovery of precious metals from waste printed circuit boards (PCBs) is an effective recycling process. This paper presents a promising hydrometallurgical process to recover precious metals from waste PCBs. To simplify the metal leaching process, large pieces of PCBs were used instead of a pulverized sample. The chemical coating present on the PCBs was removed by sodium hydroxide (NaOH) treatment prior to the hydrometallurgical treatment. Among the leaching reagents examined, hydrochloric acid (HCl) showed great potential for the recovery of metals. The HCl-mediated leaching of waste PCBs was investigated over a range of conditions. Increasing the acid concentration decreased the time required for complete metal recovery. The shaking speed showed a pronounced positive effect on metal recovery, but the temperature showed an insignificant effect. The results showed that 1 M HCl recovered all of the metals from 4 cm × 4 cm PCBs at room temperature and 150 rpm shaking speed in 22 h. PMID:26415827

Geopolymerisation of fly ashes with waste aluminium anodising etching solutions.

PubMed

Ogundiran, M B; Nugteren, H W; Witkamp, G J

2016-10-01

Combined management of coal combustion fly ash and waste aluminium anodising etching solutions using geopolymerisation presents economic and environmental benefits. The possibility of using waste aluminium anodising etching solution (AES) as activator to produce fly ash geopolymers in place of the commonly used silicate solutions was explored in this study. Geopolymerisation capacities of five European fly ashes with AES and the leaching of elements from their corresponding geopolymers were studied. Conventional commercial potassium silicate activator-based geopolymers were used as a reference. The geopolymers produced were subjected to physical, mechanical and leaching tests. The leaching of elements was tested on 28 days cured and crushed geopolymers using NEN 12457-4, NEN 7375, SPLP and TCLP leaching tests. After 28 days ambient curing, the geopolymers based on the etching solution activator showed compressive strength values between 51 and 84 MPa, whereas the commercial potassium silicate based geopolymers gave compressive strength values between 89 and 115 MPa. Based on the regulatory limits currently associated with the used leaching tests, all except one of the produced geopolymers (with above threshold leaching of As and Se) passed the recommended limits. The AES-geopolymer geopolymers demonstrated excellent compressive strength, although less than geopolymers made from commercial activator. Additionally, they demonstrated low element leaching potentials and therefore can be suitable for use in construction works. Copyright © 2016. Published by Elsevier Ltd.

Alkali activation of recovered fuel-biofuel fly ash from fluidised-bed combustion: Stabilisation/solidification of heavy metals.

PubMed

Yliniemi, Juho; Pesonen, Janne; Tiainen, Minna; Illikainen, Mirja

2015-09-01

Recovered fuel-biofuel fly ash from a fluidized bed boiler was alkali-activated and granulated with a sodium-silicate solution in order to immobilise the heavy metals it contains. The effect of blast-furnace slag and metakaolin as co-binders were studied. Leaching standard EN 12457-3 was applied to evaluate the immobilisation potential. The results showed that Ba, Pb and Zn were effectively immobilised. However, there was increased leaching after alkali activation for As, Cu, Mo, Sb and V. The co-binders had minimal or even negative effect on the immobilisation. One exception was found for Cr, in which the slag decreased leaching, and one was found for Cu, in which the slag increased leaching. A sequential leaching procedure was utilized to gain a deeper understanding of the immobilisation mechanism. By using a sequential leaching procedure it is possible fractionate elements into watersoluble, acid-soluble, easily-reduced and oxidisable fractions, yielding a total 'bioavailable' amount that is potentially hazardous for the environment. It was found that the total bioavailable amount was lower following alkali activation for all heavy metals, although the water-soluble fraction was higher for some metals. Evidence from leaching tests suggests the immobilisation mechanism was chemical retention, or trapping inside the alkali activation reaction products, rather than physical retention, adsorption or precipitation as hydroxides. Copyright © 2015 Elsevier Ltd. All rights reserved.

Effects of increased deposition of atmospheric nitrogen on an upland moor: leaching of N species and soil solution chemistry.

PubMed

Pilkington, M G; Caporn, S J M; Carroll, J A; Cresswell, N; Lee, J A; Ashenden, T W; Brittain, S A; Reynolds, B; Emmett, B A

2005-05-01

This study was designed to investigate the leaching response of an upland moorland to long-term (10 yr) ammonium nitrate additions of 40, 80 and 120 kg N ha(-1) yr(-1) and to relate this response to other indications of potential system damage, such as acidification and cation displacement. Results showed increases in nitrate leaching only in response to high rates of N input, in excess of 96 and 136 kg total N input ha(-1) yr(-1) for the organic Oh horizon and mineral Eag horizon, respectively. Individual N additions did not alter ammonium leaching from either horizon and ammonium was completely retained by the mineral horizon. Leaching of dissolved organic nitrogen (DON) from the Oh horizon was increased by the addition of 40 kg N ha(-1) yr(-1), but in spite of increases, retention of total dissolved nitrogen reached a maximum of 92% and 95% of 80 kg added N ha(-1) yr(-1) in the Oh and Eag horizons, respectively. Calcium concentrations and calcium/aluminium ratios were decreased in the Eag horizon solution with significant acidification mainly in the Oh horizon leachate. Nitrate leaching is currently regarded as an early indication of N saturation in forest systems. Litter C:N ratios were significantly lowered but values remained above a threshold predicted to increase leaching of N in forests.

Assessment of mobility and bioavailability of contaminants in MSW incineration ash with aquatic and terrestrial bioassays.

PubMed

Ribé, V; Nehrenheim, E; Odlare, M

2014-10-01

Incineration of municipal solid waste (MSW) is a waste treatment method which can be sustainable in terms of waste volume reduction as well as a source of renewable energy. In the process fly and bottom ash is generated as a waste material. The ash residue may vary greatly in composition depending on the type of waste incinerated and it can contain elevated levels of harmful contaminants such as heavy metals. In this study, the ecotoxicity of a weathered, untreated incineration bottom ash was characterized as defined by the H14 criterion of the EU Waste Framework Directive by means of an elemental analysis, leaching tests followed by a chemical analysis and a combination of aquatic and solid-phase bioassays. The experiments were conducted to assess the mobility and bioavailability of ash contaminants. A combination of aquatic and terrestrial bioassays was used to determine potentially adverse acute effects of exposure to the solid ash and aqueous ash leachates. The results from the study showed that the bottom ash from a municipal waste incineration plant in mid-Sweden contained levels of metals such as Cu, Pb and Zn, which exceeded the Swedish EPA limit values for inert wastes. The chemical analysis of the ash leachates showed high concentrations of particularly Cr. The leachate concentration of Cr exceeded the limit value for L/S 10 leaching for inert wastes. Filtration of leachates prior to analysis may have underestimated the leachability of complex-forming metals such as Cu and Pb. The germination test of solid ash and ash leachates using T. repens showed a higher inhibition of seedling emergence of seeds exposed to the solid ash than the seeds exposed to ash leachates. This indicated a relatively low mobility of toxicants from the solid ash into the leachates, although some metals exceeded the L/S 10 leaching limit values for inert wastes. The Microtox® toxicity test showed only a very low toxic response to the ash leachate exposure, while the D. magna immobility test showed a moderately high toxic effect of the ash leachates. Overall, the results from this study showed an ecotoxic effect of the solid MSW bottom ash and the corresponding ash leachates. The material may therefore pose an environmental risk if used in construction applications. However, as the testing of the solid ash was rather limited and the ash leachate showed an unusually high leaching of Cr, further assessments are required in order to conclusively characterize the bottom ash studied herein as hazardous according to the H14 criterion. Copyright © 2014 Elsevier Ltd. All rights reserved.

Modeling and mitigation of denitrification 'woodchip' bioreactor phosphorus releases during treatment of aquaculture wastewater

USDA-ARS?s Scientific Manuscript database

Denitrification 'woodchip' bioreactors designed to remove nitrate from agricultural waters may either be phosphorus sources or sinks. A 24 d batch test showed woodchip leaching is an important source of phosphorus during bioreactor start-up with a leaching potential of approximately 20 -30 mg P per ...

Effect of winter cover crops on soil nitrogen availability, corn yield, and nitrate leaching.

PubMed

Kuo, S; Huang, B; Bembenek, R

2001-10-25

Biculture of nonlegumes and legumes could serve as cover crops for increasing main crop yield, while reducing NO3 leaching. This study, conducted from 1994 to 1999, determined the effect of monocultured cereal rye (Secale cereale L.), annual ryegrass (Lolium multiflorum), and hairy vetch (Vicia villosa), and bicultured rye/vetch and ryegrass/vetch on N availability in soil, corn (Zea mays L.) yield, and NO3-N leaching in a silt loam soil. The field had been in corn and cover crop rotation since 1987. In addition to the cover crop treatments, there were four N fertilizer rates (0, 67, 134, and 201 kg N ha(-1), referred to as N0, N1, N2, and N3, respectively) applied to corn. The experiment was a randomized split-block design with three replications for each treatment. Lysimeters were installed in 1987 at 0.75 m below the soil surface for leachate collection for the N 0, N 2, and N 3 treatments. The result showed that vetch monoculture had the most influence on soil N availability and corn yield, followed by the bicultures. Rye or ryegrass monoculture had either no effect or an adverse effect on corn yield and soil N availability. Leachate NO3-N concentration was highest where vetch cover crop was planted regardless of N rates, which suggests that N mineralization of vetch N continued well into the fall and winter. Leachate NO3-N concentration increased with increasing N fertilizer rates and exceeded the U.S. Environmental Protection Agency's drinking water standard of 10 mg N l(-1) even at recommended N rate for corn in this region (coastal Pacific Northwest). In comparisons of the average NO3-N concentration during the period of high N leaching, monocultured rye and ryegrass or bicultured rye/vetch and ryegrass/vetch very effectively decreased N leaching in 1998 with dry fall weather. The amount of N available for leaching (determined based on the presidedress nitrate test, the amount of N fertilizer applied, and N uptake) correlated well with average NO3-N during the high N leaching period for vetch cover crop treatment and for the control without the cover crops. The correlation, however, failed for other cover crops largely because of variable effectiveness of the cover crops in reducing NO3 leaching during the 5 years of this study. Further research is needed to determine if relay cover crops planted into standing summer crops is a more appropriate approach than fall seeding in this region to gain sufficient growth of the cover crop by fall. Testing with other main crops that have earlier harvest dates than corn is also needed to further validate the effectiveness of the bicultures to increase soil N availability while protecting the water quality.

Effect of accelerated carbonation and zero valent iron on metal leaching from bottom ash.

PubMed

Nilsson, M; Andreas, L; Lagerkvist, A

2016-05-01

About 85% of the ashes produced in Sweden originated from the incineration of municipal solid waste and biofuel. The rest comes from the thermal treatment of recycled wood, peat, charcoal and others. About 68% of all ashes annually produced in Sweden are used for constructions on landfills, mainly slopes, roads and embankments, and only 3% for construction of roads and working surfaces outside the landfills (SCB, 2013). Since waste bottom ash (BA) often has similar properties to crushed bedrock or gravel, it could be used for road constructions to a larger extent. However, the leaching of e.g. Cr, Cu, Mo, Pb and Zn can cause a threat to the surrounding environment if the material is used as it is. Carbonation is a commonly used pre-treatment method, yet it is not always sufficient. As leaching from aged ash is often controlled by adsorption to iron oxides, increasing the number of Fe oxide sorption sites can be a way to control the leaching of several critical elements. The importance of iron oxides as sorption sites for metals is known from both mineralogical studies of bottom ash and from the remediation of contaminated soil, where iron is used as an amendment. In this study, zero valent iron (Fe(0)) was added prior to accelerated carbonation in order to increase the number of adsorption sites for metals and thereby reduce leaching. Batch, column and pHstat leaching tests were performed and the leaching behaviour was evaluated with multivariate data analysis. It showed that leaching changed distinctly after the tested treatments, in particular after the combined treatment. Especially, the leaching of Cr and Cu clearly decreased as a result of accelerated carbonation. The combination of accelerated carbonation with Fe(0) addition reduced the leaching of Cr and Cu even further and reduced also the leaching of Mo, Zn, Pb and Cd compared to untreated BA. Compared with only accelerated carbonation, the Fe(0) addition significantly reduced the leaching of Cr, Cu and Mo. The effects of Fe(0) addition can be related to binding of the studied elements to newly formed iron oxides. The effects of Fe(0) addition were often more distinct at pH values between 7 and 9, which indicates that a single treatment with only Fe addition would be less effective and a combined treatment is recommended. The pHstat results showed that accelerated carbonation in combination with Fe(0)(0) addition widens the pH range for low solubility of about one unit for several of the studied elements. This indicates that pre-treating the bottom ash with a combination of accelerated carbonation and Fe(0) addition makes the leaching properties of the ash less sensitive to pH changes that may occur during reuse. All in all, the addition of Fe(0) in combination with carbonation could be an effective pre-treatment method for decreasing the mobility of potentially harmful components in bottom ash. Copyright © 2015 The Authors. Published by Elsevier Ltd.. All rights reserved.

Functional test of pedotransfer functions to predict water flow and solute transport with the dual-permeability model MACRO

NASA Astrophysics Data System (ADS)

Moeys, J.; Larsbo, M.; Bergström, L.; Brown, C. D.; Coquet, Y.; Jarvis, N. J.

2012-07-01

Estimating pesticide leaching risks at the regional scale requires the ability to completely parameterise a pesticide fate model using only survey data, such as soil and land-use maps. Such parameterisations usually rely on a set of lookup tables and (pedo)transfer functions, relating elementary soil and site properties to model parameters. The aim of this paper is to describe and test a complete set of parameter estimation algorithms developed for the pesticide fate model MACRO, which accounts for preferential flow in soil macropores. We used tracer monitoring data from 16 lysimeter studies, carried out in three European countries, to evaluate the ability of MACRO and this "blind parameterisation" scheme to reproduce measured solute leaching at the base of each lysimeter. We focused on the prediction of early tracer breakthrough due to preferential flow, because this is critical for pesticide leaching. We then calibrated a selected number of parameters in order to assess to what extent the prediction of water and solute leaching could be improved. Our results show that water flow was generally reasonably well predicted (median model efficiency, ME, of 0.42). Although the general pattern of solute leaching was reproduced well by the model, the overall model efficiency was low (median ME = -0.26) due to errors in the timing and magnitude of some peaks. Preferential solute leaching at early pore volumes was also systematically underestimated. Nonetheless, the ranking of soils according to solute loads at early pore volumes was reasonably well estimated (concordance correlation coefficient, CCC, between 0.54 and 0.72). Moreover, we also found that ignoring macropore flow leads to a significant deterioration in the ability of the model to reproduce the observed leaching pattern, and especially the early breakthrough in some soils. Finally, the calibration procedure showed that improving the estimation of solute transport parameters is probably more important than the estimation of water flow parameters. Overall, the results are encouraging for the use of this modelling set-up to estimate pesticide leaching risks at the regional-scale, especially where the objective is to identify vulnerable soils and "source" areas of contamination.

Acidic leaching of potentially toxic metals cadmium, cobalt, chromium, copper, nickel, lead, and zinc from two Zn smelting slag materials incubated in an acidic soil.

PubMed

Liu, Taoze; Li, Feili; Jin, Zhisheng; Yang, Yuangen

2018-07-01

A column leaching study, coupled with acid deposition simulation, was conducted to investigate the leaching of potentially toxic metals (PTM) from zinc smelting slag materials (SSM) after being incubated in an acid Alfisol for 120 days at room temperature. Two SSMs (SSM-A: acidic, 10 yrs exposure with moderate high PTM concentrations versus SSM-B: alkaline, 2 yrs exposure with extremely high PTM concentrations), were used for the incubation at 0.5, 1, 2.5, 5 wt% amendment ratios in triplicate. Five leaching events were conducted at day 1, 3, 7, 14, and 28, and the leaching of PTMs mainly occurred in the first three leaching events, with the highest PTM concentrations in leachate measured from 5 wt% SSM amendments. After leaching, 2.5, 12, 5.5, 14, 11, and 9 wt% of M3 extractable Pb, Zn, Cd, Co, Cr, and Ni could be released from 5 wt% SSM-A amended soils, being respectively 25, 12, 4, 2, 2, and 2 times more than those from 5 wt% SSM-B amended soils. In the leachates, the concentrations of PTMs were mostly affected by leachant pH and were closely correlated to the concentrations of Fe, Al, Ca, Mg and P with Cd, Pb, and Zn showing the most environmental concern. Visual MINTEQ 3.1 modeling suggested metallic ions and sulfate forms as the common chemical species of PTMs in the leachates; whereas, organic bound species showed importance for Cd, Pb, Cu, and Ni, and CdCl + was observed for Cd. Aluminum hydroxy, phosphate, and sulfate minerals prevailed as the saturated minerals, followed by chloropyromorphite (Pb 5 (PO 4 ) 3 Cl) and plumbogummite (PbAl 3 (PO 4 ) 2 (OH) 5 ·H 2 O) in the leachates. This study suggested that incubation of SSMs in acidic soil for a long term can enhance the release of PTMs as the forms of metallic ions and sulfate when subjected to acid deposition leaching. Copyright © 2018 Elsevier Ltd. All rights reserved.

Reducing acid leaching of manganiferous ore: effect of the iron removal operation on solid waste disposal.

PubMed

De Michelis, Ida; Ferella, Francesco; Beolchini, Francesca; Vegliò, Francesco

2009-01-01

The process of reducing acid leaching of manganiferous ore is aimed at the extraction of manganese from low grade manganese ores. This work is focused on the iron removal operation. The following items have been considered in order to investigate the effect of the main operating conditions on solid waste disposal and on the process costs: (i) type and quantity of the base agent used for iron precipitation, (ii) effective need of leaching waste separation prior to the iron removal operation, (iii) presence of a second leaching stage with the roasted ore, which might also act as a preliminary iron removal step, and (iv) effect of tailings washing on the solid waste classification. Different base compounds have been tested, including CaO, CaCO3, NaOH, and Na2CO3. The latter gave the best results concerning both the precipitation process kinetics and the reagent consumption. The filtration of the liquor leach prior to iron removal was not necessary, implying significant savings in capital costs. A reduction of chemical consumption and an increase of manganese concentration in the solution were obtained by introducing secondary leaching tests with the previously roasted ore; this additional step was introduced without a significant decrease of global manganese extraction yield. Finally, toxicity characteristic leaching procedure (TCLP) tests carried out on the leaching solid waste showed: (i) a reduction of arsenic mobility in the presence of iron precipitates, and (ii) the need for a washing step in order to produce a waste that is classifiable as not dangerous, taking into consideration the existing Environmental National Laws.

Analyses of heavy metals in mineral trioxide aggregate and Portland cement.

PubMed

Schembri, Matthew; Peplow, George; Camilleri, Josette

2010-07-01

Portland cement is used in the construction industry as a binder in concrete. It is manufactured from chalk, limestone, and clay, which are clinkered at very high temperatures and ground with gypsum to form Portland cement. The raw materials and the manufacturing process can result in the inclusion of heavy metals in Portland cement. Portland cement with a four to one addition of bismuth oxide is marketed as mineral trioxide aggregate (MTA), which is used mainly as a dental material. Heavy metal inclusion can be of concern because MTA is in contact with hard and soft tissues. Measurements of arsenic, lead, and chromium in hydrated gray and white Portland cement, ProRoot MTA, and MTA Angelus were conducted with graphite furnace atomic absorption spectrophotometry after acid digestion on the hydrated material. The leaching of the metal ions from the solid material in water and simulated body fluid (SBF) was also determined. All cement types showed high relative values of leached chromium compared with arsenic and lead in both the total metal content and leached species. The gray Portland cement showed the highest total amount of metal. The white Portland and both MTAs had lower values for all the leached metal ions. Both MTAs released more arsenic than the amount specified in ISO 9917-1 (2007). Portland cements and MTAs showed evidence of heavy metals in the acid-soluble form as well as leaching in deionized water and SBF. MTA contained levels of arsenic higher than the safe limit specified by the ISO 9917-1 (2007). Copyright 2010 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

Leaching characteristics of ash from the May 18, 1980, eruption of Mount St. Helens Volcano, Washington

USGS Publications Warehouse

Smith, David Burl; Zielinski, Robert A.; Taylor, Howard E.

1982-01-01

Leaching of freshly erupted air-fall ash, unaffected by rain, from the May 18, 1.980,eruption of Mount St. Helens volcano, Washington, shows that Ca 2+, Na+, Mg+, SO4 2-, and Cl- are the predominant chemical species released on first exposure of the ash to water. Extremely high correlation of Ca with SO4 and Na with Cl in water leachates suggests the presence of CaSO4 and NaCl salts on the ash. The amount of water soluble material on ash increases with distance from source and with the weight fraction of small (less than 63 micrometers) ash particles of high-surface area. This suggests that surface reactions such as adsorption are responsible for concentrating the soluble material. CaSO4, NaCl, and other salts are probably formed as microscopic crystals in the high-temperature core of the eruption column and are then adsorbed by silicate ash particles. The environmentally important elements Zn, Cu, Cd, F, Pb, and Ba are released by a water leach in concentrations which could pose short-term hazards to some forms of aquatic life. However, calculated concentrations are based on a water-to-ash ratio of 4:1 or less, which is probably an underestimation of the regionally operative ratio. A subsequent leach of ash by warm alkaline solution shows dramatic increases in the amount of dissolved SiO2, U, and V, which are probably caused by increased dissolution of the glassy component of ash. Glass dissolution by alkaline ground water is a mechanism for providing these three elements to sedimentary traps where they may co-accumulate as uraniferous silica or U-V minerals. Leaching characteristics of ash from Mount St. Helens are comparable to characteristics of ash of similar composition from volcanoes in Guatemala. Ashes from each locality show similar ions predominating for a given leachate and similar fractions of a particular element in the ash removed on contact with the leach solution.

Decay resistance of wood treated with boric acid and tall oil derivates.

PubMed

Temiz, Ali; Alfredsen, Gry; Eikenes, Morten; Terziev, Nasko

2008-05-01

In this study, the effect of two boric acid concentrations (1% and 2%) and four derivates of tall oil with varying chemical composition were tested separately and in combination. The tall oil derivates were chosen in a way that they consist of different amounts of free fatty, resin acids and neutral compounds. Decay tests using two brown rot fungi (Postia placenta and Coniophora puteana) were performed on both unleached and leached test samples. Boric acid showed a low weight loss in test samples when exposed to fungal decay before leaching, but no effect after leaching. The tall oil derivates gave better efficacy against decay fungi compared to control, but are not within the range of the efficacy needed for a wood preservative. Double impregnation with boric acid and tall oil derivates gave synergistic effects for several of the double treatments both in unleached and leached samples. In the unleached samples the double treatment gave a better efficacy against decay fungi than tall oil alone. In leached samples a better efficacy against brown rot fungi were achieved than in samples with boron alone and a nearly similar or better efficacy than for tall oil alone. Boric acid at 2% concentration combined with the tall oil derivate consisting of 90% free resin acids (TO-III) showed the best performance against the two decay fungi with a weight loss less than 3% after a modified pure culture test.

Impact of rainfall patterns and frequency on the export of pesticides and heavy-metals from agricultural soils.

PubMed

Meite, Fatima; Alvarez-Zaldívar, Pablo; Crochet, Alexandre; Wiegert, Charline; Payraudeau, Sylvain; Imfeld, Gwenaël

2018-03-01

The combined influence of soil characteristics, pollutant aging and rainfall patterns on the export of pollutants from topsoils is poorly understood. We used laboratory experiments and parsimonious modeling to evaluate the impact of rainfall characteristics on the ponding and the leaching of a pollutant mixture from topsoils. The mixture included the fungicide metalaxyl, the herbicide S-metolachlor, as well as copper (Cu) and zinc (Zn). Four rainfall patterns, which differed in their durations and intensities, were applied twice successively with a 7days interval on each soil type. To evaluate the influence of soil type and aging, experiments included crop and vineyard soils and two stages of pollutant aging (0 and 10days). The global export of pollutants was significantly controlled by the rainfall duration and frequency (P<0.01). During the first rainfall event, the longest and most intense rainfall pattern yielded the largest export of metalaxyl (44.5±21.5% of the initial mass spiked in the soils), S-metolachlor (8.1±3.1%) and Cu (3.1±0.3%). Soil compaction caused by the first rainfall reduced in the second rainfall the leaching of remaining metalaxyl, S-metolachlor, Cu and Zn by 2.4-, 2.9-, 30- and 50-fold, respectively. In contrast, soil characteristics and aging had less influence on pollutant mass export. The soil type significantly influenced the leaching of Zn, while short-term aging impacted Cu leaching. Our results suggest that rainfall characteristics predominantly control export patterns of metalaxyl and S-metolachlor, in particular when the aging period is short. We anticipate our study to be a starting point for more systematic evaluation of the dissolved pollutant ponding/leaching partitioning and the export of pollutant mixtures from different soil types in relation to rainfall patterns. Copyright © 2017 Elsevier B.V. All rights reserved.

Leaching under Oxygen Pressure with Carbonate Solution Reduction by Hydrogen; LIXIVIATION OXYDANTE DES PECHBLENDES ET PRECIPITATION DE L'URANIUM PAR L'HYDROGENE. APPLICATION AUX MINERAIS PAUVRES FRANCAIS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Balaceanu, J.C.; Coussemant, F.; Mouret, P.

1959-10-31

A study was made of the basic characteristics of the leaching with carbonate solution under oxygen pressure and of the catalytic hydrogen reduction of low-grade French ores. Pure U/sub 3/O/sub 8/ was used in the investigations on leaching. The effects of oxygen pressure, temperature, initial surface of the oxide, surfuce during the course of the reaction, and concentration of the carbonate solution were determined. It was shown that the heterogeneous reactions involve a constant surface and two steps. A pilot plant experiment was made on a number of low-grade French ores. With ores the leaching is not sensitive to oxygenmore » pressure. Dilute solutions of sodium uranyl carbonate are obtained from the leaching. The uranium can be precipitated as an oxide of a lower valent state by catalytic reduction with hydrogen. The study of this step was made on pure solutions of sodium uranyl carbonate in the presence of nickel and platinum catalysts. The reaction is strongly modified by the presence of even low concentrations of sodium bicarbonate. The reaction velocity increases with hydrogen pressure up to 5 atm, but then becomes independent of the pressure. The precipitation is accelerated by an increase in temperature. (J.S.R.)« less

Effects of cement on redistribution of trace metals and dissolution of organics in sewage sludge and its inorganic waste-amended products.

PubMed

Lim, T T; Chu, J; Goi, M H

2006-01-01

The suitability of using cement-stabilized sludge products as artificial soils in earth works was evaluated. The sludge products investigated were cemented sludge, cement-treated clay-amended sludge (SS+MC), and cement-treated copper slag-amended sludge (SS+CS). The leachability of lead (Pb), zinc (Zn), copper (Cu), and chromium (Cr) were assessed using the sequential extraction technique, toxicity characteristic leaching procedure (TCLP), NEN 7341 availability test, and column leaching test. The results indicated that Zn leachability was reduced in all the cement-stabilized sludge products. In contrast, Cu was transferred from the organic fraction to the readily leachable phases in the cement-stabilized sludge products and therefore exhibited increased leachability. The increased Cu leachability could be attributed to dissolution of humic substances in the sludge as a result of elevated pH. Good correlation between dissolved organic carbon (DOC) and heavy metal leaching from the cement-stabilized sludge products was observed in the column leaching experiment. Even with a cement percentage as small as 12.5%, calcium silicate hydrate (C-S-H) was formed in the SS+MC and SS+CS products. Inclusion of the marine clay in the SS+MC products could reduce the leaching potentials of Zn, and this was the great advantage of the marine clay over the copper slag for sludge amendment.

Leaching heavy metals from the surface soil of reclaimed tidal flat by alternating seawater inundation and air drying.

PubMed

Guo, Shi-Hong; Liu, Zhen-Ling; Li, Qu-Sheng; Yang, Ping; Wang, Li-Li; He, Bao-Yan; Xu, Zhi-Min; Ye, Jin-Shao; Zeng, Eddy Y

2016-08-01

Leaching experiments were conducted in a greenhouse to simulate seawater leaching combined with alternating seawater inundation and air drying. We investigated the heavy metal release of soils caused by changes associated with seawater inundation/air drying cycles in the reclaimed soils. After the treatment, the contents of all heavy metals (Cd, Pb, Cr, and Cu), except Zn, in surface soil significantly decreased (P < 0.05), with removal rates ranging from 10% to 51%. The amounts of the exchangeable, carbonate, reducible, and oxidizable fractions also significantly decreased (P < 0.05). Moreover, prolonged seawater inundation enhanced the release of heavy metals. Measurement of diffusive gradients in thin films indicated that seawater inundation significantly increased the re-mobility of heavy metals. During seawater inundation, iron oxide reduction induced the release of heavy metals in the reducible fraction. Decomposition of organic matter, and complexation with dissolved organic carbon decreased the amount of heavy metals in the oxidizable fraction. Furthermore, complexation of chloride ions and competition of cations during seawater inundation and/or leaching decreased the levels of heavy metals in the exchangeable fraction. By contrast, air drying significantly enhanced the concentration of heavy metals in the exchangeable fraction. Therefore, the removal of heavy metals in the exchangeable fraction can be enhanced during subsequent leaching with seawater. Copyright © 2016 Elsevier Ltd. All rights reserved.

Characterization of dross and its recovery by sulphuric acid leaching

NASA Astrophysics Data System (ADS)

Rahmani, S. A.; Meidianto, A.; Amal, M. I.; Wismogroho, A. S.; Widayatno, W. B.

2018-03-01

This paper reports the characterization of dross from galvanizing process and its recovery using acidic leaching method. The diffraction profile of dross showed identical peaks with that of ZnO. The X-ray Fluorescence (XRF) analysis identified the content of following metals: Zn, Fe, Mn, Ga, Co, and W. The thermal behaviour examination revealed the existence of some volatiles within the initial sample. The acidic leaching at various concentrations of sulphuric acid was conducted to determine the optimum concentration for zinc recovery and the highest yield of zinc sulphate. It is concluded that the optimum concentration of H2SO4 for this kind of dross is 4 M with 71.9% yield of ZnSO4. The result of leaching process was confirmed by infrared spectrum, where various absorptions corresponding to SO4 2- and Zn-O bands were observed.

Immobilization of simulated radioactive soil waste containing cerium by self-propagating high-temperature synthesis

NASA Astrophysics Data System (ADS)

Mao, Xianhe; Qin, Zhigui; Yuan, Xiaoning; Wang, Chunming; Cai, Xinan; Zhao, Weixia; Zhao, Kang; Yang, Ping; Fan, Xiaoling

2013-11-01

A simulated radioactive soil waste containing cerium as an imitator element has been immobilized by a thermite self-propagating high-temperature synthesis (SHS) process. The compositions, structures, and element leaching rates of products with different cerium contents have been characterized. To investigate the influence of iron on the chemical stability of the immobilized products, leaching tests of samples with different iron contents with different leaching solutions were carried out. The results showed that the imitator element cerium mainly forms the crystalline phases CeAl11O18 and Ce2SiO5. The leaching rate of cerium over a period of 28 days was 10-5-10-6 g/(m2 day). Iron in the reactants, the reaction products, and the environment has no significant effect on the chemical stability of the immobilized SHS products.

Watershed soil Cd loss after long-term agricultural practice and biochar amendment under four rainfall levels.

PubMed

Ouyang, Wei; Huang, Weijia; Hao, Xin; Tysklind, Mats; Haglund, Peter; Hao, Fanghua

2017-10-01

Some heavy metals in farmland soil can be transported into the waterbody, affecting the water quality and sediment at the watershed outlet, which can be used to determine the historical loss pattern. Cd is a typical heavy metal leached from farmland that is related to phosphate fertilizers and carries serious environmental risk. The spatial-vertical pattern of Cd in soil and the vertical trend of Cd in the river sediment core were analyzed, which showed the migration and accumulation of Cd in the watershed. To prevent watershed Cd loss, biochar was employed, and leaching experiments were conducted to investigate the Cd loss from soil depending on the initial concentration. Four rainfall intensities, 1.25 mm/h, 2.50 mm/h, 5.00 mm/h, and 10.00 mm/h, were used to simulate typical rainfall scenarios for the study area. Biochar was prepared from corn straw after pretreatment with ammonium dihydrogen phosphate (ADP) and pyrolysis at 400 °C under anoxic conditions. To identify the effects of biochar amendment on Cd migration, the biochar was mixed with soil for 90 days at concentrations of 0%, 0.5%, 1.0%, 3.0%, and 5.0% soil by weight. The results showed that the Cd leaching load increased as the initial load and rainfall intensity increased and that eluviation caused surface Cd to diffuse to the deep soils. The biochar application caused more of the heavy metals to be immobilized in the amended soil rather than transported into the waterbody. The sorption efficiency of the biochar for Cd increased as the addition level increased to 3%, which showed better performance than the 5% addition level under some initial concentration and rainfall conditions. The research indicated that biochar is a potential material to prevent diffuse heavy metal pollution and that a lower addition makes the application more feasible. Copyright © 2017 Elsevier Ltd. All rights reserved.

DISTRIBUTION COEFICIENTS (KD) GENERATED FROM A CORE SAMPLE COLLECTED FROM THE SALTSTONE DISPOSAL FACILITY

DOE Office of Scientific and Technical Information (OSTI.GOV)

Almond, P.; Kaplan, D.

Core samples originating from Vault 4, Cell E of the Saltstone Disposal Facility (SDF) were collected in September of 2008 (Hansen and Crawford 2009, Smith 2008) and sent to SRNL to measure chemical and physical properties of the material including visual uniformity, mineralogy, microstructure, density, porosity, distribution coefficients (K{sub d}), and chemical composition. Some data from these experiments have been reported (Cozzi and Duncan 2010). In this study, leaching experiments were conducted with a single core sample under conditions that are representative of saltstone performance. In separate experiments, reducing and oxidizing environments were targeted to obtain solubility and Kd valuesmore » from the measurable species identified in the solid and aqueous leachate. This study was designed to provide insight into how readily species immobilized in saltstone will leach from the saltstone under oxidizing conditions simulating the edge of a saltstone monolith and under reducing conditions, targeting conditions within the saltstone monolith. Core samples were taken from saltstone poured in December of 2007 giving a cure time of nine months in the cell and a total of thirty months before leaching experiments began in June 2010. The saltstone from Vault 4, Cell E is comprised of blast furnace slag, class F fly ash, portland cement, and Deliquification, Dissolution, and Adjustment (DDA) Batch 2 salt solution. The salt solution was previously analyzed from a sample of Tank 50 salt solution and characterized in the 4QCY07 Waste Acceptance Criteria (WAC) report (Zeigler and Bibler 2009). Subsequent to Tank 50 analysis, additional solution was added to the tank solution from the Effluent Treatment Project as well as from inleakage from Tank 50 pump bearings (Cozzi and Duncan 2010). Core samples were taken from three locations and at three depths at each location using a two-inch diameter concrete coring bit (1-1, 1-2, 1-3; 2-1, 2-2, 2-3; 3-1, 3-2, 3-3) (Hansen and Crawford 2009). Leaching experiments were conducted with a section of core sample 3-2. All cores from location 3 were drilled without using water. Core sample 3-2 was drilled from approximately six inches to a depth of approximately 13 inches. Approximately six inches of the core was removed but it broke into two pieces during removal from the bit. At the time of drilling, core material appeared olive green in color (Smith 2008). The fact that the samples were cored as olive green and were received after storage with a gray outer layer is indicative that some oxidation had occurred prior to leaching studies.« less

A field experiment with variable-suction multi-compartment samplers to measure the spatio-temporal distribution of solute leaching in an agricultural soil.

PubMed

Bloem, E; Hogervorst, F A N; de Rooij, G H

2009-04-01

Solutes spread out in time and space as they move downwards from the soil surface with infiltrating water. Solute monitoring in the field is often limited to observations of resident concentrations, while flux concentrations govern the movement of solutes in soils. A recently developed multi-compartment sampler is capable of measuring fluxes at a high spatial resolution with minimal disturbance of the local pressure head field. The objective of this paper is to use this sampler to quantify the spatial and temporal variation of solute leaching below the root zone in an agricultural field under natural rainfall in winter and spring. We placed two samplers at 31 and 25 cm depth in an agricultural field, leaving the soil above undisturbed. Each sampler contained 100 separate cells of 31x31 mm. Water fluxes were measured every 5 min for each cell. We monitored leaching of a chloride pulse under natural rainfall by frequently extracting the collected leachate while leaving the samplers buried in situ. This experiment was followed by a dye tracer experiment. This setting yielded information that widely surpassed the information that can be provided by separate anionic and dye tracer trials, and solute transport monitoring by coring or suction cups. The detailed information provided by the samplers showed that percolation at the sampling depth started much faster (approximately 3 h after the start of rainfall) in initially wet soil (pressure head above -65 cm) than in drier soil (more than 14 h at pressure heads below -80 cm). At any time, 25% of the drainage passed through 5-6% of the sampled area, reflecting the effect of heterogeneity on the flow paths. The amount of solute carried by individual cells varied over four orders of magnitude. The lateral concentration differences were limited though. This suggests a convective-dispersive regime despite the short vertical travel distance. On the other hand, the dilution index indicates a slight tendency towards stochastic-convective transport at this depth. There was no evidence in the observed drainage patterns and dye stained profiles of significant disturbance of the flow field by the samplers.

The role of nano-perovskite in the negligible thorium release in seawater from Greek bauxite residue (red mud)

PubMed Central

Gamaletsos, Platon N.; Godelitsas, Athanasios; Kasama, Takeshi; Kuzmin, Alexei; Lagos, Markus; Mertzimekis, Theo J.; Göttlicher, Jörg; Steininger, Ralph; Xanthos, Stelios; Pontikes, Yiannis; Angelopoulos, George N.; Zarkadas, Charalampos; Komelkov, Aleksandr; Tzamos, Evangelos; Filippidis, Anestis

2016-01-01

We present new data about the chemical and structural characteristics of bauxite residue (BR) from Greek Al industry, using a combination of microscopic, analytical, and spectroscopic techniques. SEM-EDS indicated a homogeneous dominant “Al-Fe-Ca-Ti-Si-Na-Cr matrix”, appearing at the microscale. The bulk chemical analyses showed considerable levels of Th (111 μg g−1), along with minor U (15 μg g−1), which are responsible for radioactivity (355 and 133 Bq kg−1 for 232Th and 238U, respectively) with a total dose rate of 295 nGy h−1. Leaching experiments, in conjunction with SF-ICP-MS, using Mediterranean seawater from Greece, indicated significant release of V, depending on S/L ratio, and negligible release of Th at least after 12 months leaching. STEM-EDS/EELS & HR-STEM-HAADF study of the leached BR at the nanoscale revealed that the significant immobility of Th4+ is due to its incorporation into an insoluble perovskite-type phase with major composition of Ca0.8Na0.2TiO3 and crystallites observed in nanoscale. The Th LIII-edge EXAFS spectra demonstrated that Th4+ ions, which are hosted in this novel nano-perovskite of BR, occupy Ca2+ sites, rather than Ti4+ sites. That is most likely the reason of no Th release in Mediterranean seawater. PMID:26899139

Geochemically structural characteristics of municipal solid waste incineration fly ash particles and mineralogical surface conversions by chelate treatment.

PubMed

Kitamura, Hiroki; Sawada, Takaya; Shimaoka, Takayuki; Takahashi, Fumitake

2016-01-01

Leaching behaviors of heavy metals contained in municipal solid waste incineration (MSWI) fly ash have been studied well. However, micro-characteristics of MSWI fly ash particles are still uncertain and might be non-negligible to describe their leaching behaviors. Therefore, this study investigated micro-characteristics of MSWI fly ash particles, especially their structural properties and impacts of chelate treatment on surface characteristics. According to SEM observations, raw fly ash particles could be categorized into four types based on their shapes. Because chelate treatment changed the surface of fly ash particles dramatically owing to secondary mineral formations like ettringite, two more types could be categorized for chelate-treated fly ash particles. Acid extraction experiments suggest that fly ash particles, tested in this study, consist of Si-base insoluble core structure, Al/Ca/Si-base semi-soluble matrices inside the body, and KCl/NaCl-base soluble aggregates on the surface. Scanning electron microscope (SEM) observations of the same fly ash particles during twice moistening treatments showed that KCl/NaCl moved under wet condition and concentrated at different places on the particle surface. However, element mobility depended on secondary mineral formations. When insoluble mineral like gypsum was generated and covered the particle surface, it inhibited element transfer under wet condition. Surface characteristics including secondary mineral formation of MSWI fly ash particles are likely non-negligible to describe trace element leaching behaviors.

Copper aluminate spinel in the stabilization and detoxification of simulated copper-laden sludge.

PubMed

Tang, Yuanyuan; Shih, Kaimin; Chan, King

2010-06-01

This study aims to evaluate the feasibility of stabilizing copper-laden sludge by the application of alumina-based ceramic products. The processing temperature, material leaching behaviour, and the effect of detoxification were investigated in detail. CuO was used to simulate the copper-laden sludge and X-ray Diffraction was performed to monitor the incorporation of copper into the copper aluminate spinel (CuAl(2)O(4)) phase in ceramic products. It was found that the development of CuAl(2)O(4) increased with elevating temperatures up to and including 1000 degrees C in the 3h short-sintering scheme. When the sintering temperature went above 1000 degrees C, the CuAl(2)O(4) phase began to decompose due to the high temperature transformation to CuAlO(2). The leachability and leaching behaviour of CuO and CuAl(2)O(4) were compared by usage of a prolonged leaching test modified from US EPA's toxicity characteristic leaching procedure. The leaching results show that CuAl(2)O(4) is superior to CuO for the purpose of copper immobilization over longer leaching periods. Furthermore, the detoxification effect of CuAl(2)O(4) was tested through bacterial adhesion with Escherichia coli K12, and the comparison of bacterial adhesion on CuO and CuAl(2)O(4) surfaces shows the beneficial detoxification effect in connection with the formation of the CuAl(2)O(4) spinel. This study demonstrates the feasibility of transforming copper-laden sludge into the spinel phase by using readily available and inexpensive ceramic materials, and achieving a successful reduction of metal mobility and toxicity.

Environmental impact of ferrochrome slag in road construction.

PubMed

Lind, B B; Fällman, A M; Larsson, L B

2001-01-01

Vargon Alloys in Western Sweden is one of the largest producers of ferrochrome slag in Europe. Ferrochrome slag is a by-product from the production of ferrochrome, an essential component in stainless steel. Extensive tests have been carried out on the physical properties of the ferrochrome slag from Vargon Alloys and it was found to be highly suitable as road construction material. The composition and leaching tests of the ferrochrome slag show that the chromium content is high, 1-3%, although leaching under normal conditions is very low. With the exception of potassium (K), which had a potential leaching capacity (availability test) of around 16%, the leaching of chromium, nickel, zinc and other elements was just a few per cent. However, all these tests were conducted in the laboratory. What happens out in the field, under the influence of acid rain and biological activity, and how does this compare with the laboratory results? To answer this question an investigation was carried out to study the environmental impact of ferrochrome slag in roads that were built in 1994. The investigation includes soil sampling (total content and leachable amounts of metals) and groundwater analysis (filtered and non-filtered samples). In addition, a new method involving the bio-uptake of chromium and other metals by the roots of the dandelion (Taraxacum officinale) was tested. The results show that there was a low migration of particles from the slag to the underlying soil and that the leaching into the groundwater was also low for all the elements analysed. However, there seemed to be a significant uptake of Cr by plants growing with their roots in the slag. An investigation of plant uptake was an important complement to laboratory leaching tests on alternative materials.

Effects of thin-film accelerated carbonation on steel slag leaching.

PubMed

Baciocchi, R; Costa, G; Polettini, A; Pomi, R

2015-04-09

This paper discusses the effects of accelerated carbonation on the leaching behaviour of two types of stainless steel slags (electric arc furnace and argon oxygen decarburisation slag). The release of major elements and toxic metals both at the natural pH and at varying pH conditions was addressed. Geochemical modelling of the eluates was used to theoretically describe leaching and derive information about mineralogical changes induced by carbonation. Among the investigated elements, Ca and Si were most appreciably affected by carbonation. A very clear effect of carbonation on leaching was observed for silicate phases; geochemical modelling indicated that the Ca/Si ratio of Ca-controlling minerals shifted from ∼ 1 for the untreated slag to 0.5-0.67 for the carbonated samples, thus showing that the carbonation process left some residual Ca-depleted silicate phases while the extracted Ca precipitated in the form of carbonate minerals. For toxic metals the changes in leaching induced by carbonation appeared to be mainly related to the resulting pH changes, which were as high as ∼ 2 orders of magnitude upon carbonation. Depending on the specific shape of the respective solubility curves, the extent of leaching of toxic metals from the slag was differently affected by carbonation. Copyright © 2014 Elsevier B.V. All rights reserved.

Treatment of electronic waste to recover metal values using thermal plasma coupled with acid leaching - A response surface modeling approach

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rath, Swagat S., E-mail: swagat.rath@gmail.com; Nayak, Pradeep; Mukherjee, P.S.

2012-03-15

Highlights: Black-Right-Pointing-Pointer Sentences/phrases were modified. Black-Right-Pointing-Pointer Necessary discussions for different figures were included. Black-Right-Pointing-Pointer More discussion have been included on the flue gas analysis. Black-Right-Pointing-Pointer Queries to both the reviewers have been given. - Abstract: The global crisis of the hazardous electronic waste (E-waste) is on the rise due to increasing usage and disposal of electronic devices. A process was developed to treat E-waste in an environmentally benign process. The process consisted of thermal plasma treatment followed by recovery of metal values through mineral acid leaching. In the thermal process, the E-waste was melted to recover the metal values asmore » a metallic mixture. The metallic mixture was subjected to acid leaching in presence of depolarizer. The leached liquor mainly contained copper as the other elements like Al and Fe were mostly in alloy form as per the XRD and phase diagram studies. Response surface model was used to optimize the conditions for leaching. More than 90% leaching efficiency at room temperature was observed for Cu, Ni and Co with HCl as the solvent, whereas Fe and Al showed less than 40% efficiency.« less

Recovery of cobalt from spent lithium-ion batteries using supercritical carbon dioxide extraction.

PubMed

Bertuol, Daniel A; Machado, Caroline M; Silva, Mariana L; Calgaro, Camila O; Dotto, Guilherme L; Tanabe, Eduardo H

2016-05-01

Continuing technological development decreases the useful lifetime of electronic equipment, resulting in the generation of waste and the need for new and more efficient recycling processes. The objective of this work is to study the effectiveness of supercritical fluids for the leaching of cobalt contained in lithium-ion batteries (LIBs). For comparative purposes, leaching tests are performed with supercritical CO2 and co-solvents, as well as under conventional conditions. In both cases, sulfuric acid and H2O2 are used as reagents. The solution obtained from the supercritical leaching is processed using electrowinning in order to recover the cobalt. The results show that at atmospheric pressure, cobalt leaching is favored by increasing the amount of H2O2 (from 0 to 8% v/v). The use of supercritical conditions enable extraction of more than 95wt% of the cobalt, with reduction of the reaction time from 60min (the time employed in leaching at atmospheric pressure) to 5min, and a reduction in the concentration of H2O2 required from 8 to 4% (v/v). Electrowinning using a leach solution achieve a current efficiency of 96% and a deposit with cobalt concentration of 99.5wt%. Copyright © 2016 Elsevier Ltd. All rights reserved.

Combustion and leaching behavior of elements in the argonne premium coal samples

USGS Publications Warehouse

Finkelman, R.B.; Palmer, C.A.; Krasnow, M.R.; Aruscavage, P. J.; Sellers, G.A.; Dulong, F.T.

1990-01-01

Eight Argonne Premium Coal samples and two other coal samples were used to observe the effects of combustion and leaching on 30 elements. The results were used to infer the modes of occurrence of these elements. Instrumental neutron activation analysis indicates that the effects of combustion and leaching on many elements varied markedly among the samples. As much as 90% of the selenium and bromine is volatilized from the bituminous coal samples, but substantially less is volatilized from the low-rank coals. We interpret the combustion and leaching behavior of these elements to indicate that they are associated with the organic fraction. Sodium, although nonvolatile, is ion-exchangeable in most samples, particularly in the low-rank coal samples where it is likely to be associated with the organic constituents. Potassium is primarily in an ion-exchangeable form in the Wypdak coal but is in HF-soluble phases (probably silicates) in most other samples. Cesium is in an unidentified HNO3-soluble phase in most samples. Virtually all the strontium and barium in the low-rank coal samples is removed by NH4OAc followed by HCl, indicating that these elements probably occur in both organic and inorganic phases. Most tungsten and tantalum are in insoluble phases, perhaps as oxides or in organic association. Hafnium is generally insoluble, but as much as 65% is HF soluble, perhaps due to the presence of very fine grained or metamict zircon. We interpret the leaching behavior of uranium to indicate its occurrence in chelates and its association with silicates and with zircon. Most of the rare-earth elements (REE) and thorium appear to be associated with phosphates. Differences in textural relationships may account for some of the differences in leaching behavior of the REE among samples. Zinc occurs predominantly in sphalerite. Either the remaining elements occur in several different modes of occurrence (scandium, iron), or the leaching data are equivocal (arsenic, antimony, chromium, cobalt, and nickel). The results of these combustion and leaching experiments indicate that some previously held assumptions concerning modes of occurrence of elements in coal should be reconsidered.

Synopsis of research needs workshop: Development of leach tests for contaminated dredged material held in Baton Rouge, Louisiana on 23-24 June 1988. Final report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

1990-02-01

This report presents the findings of a research needs workshop on the development of leach tests for contaminated dredged material, held 23-24 June 1988 in Baton Rouge, LA. The workshop was hosted by the Louisiana Water Resources Research Institute and the US Army Engineer Waterways Experiment Station (WES). The workshop participants reviewed results of research on test procedures developed by the WES and provided eight recommendations for directing future research in this area. Workshop panelists were of the opinion that research conducted to date was good and generally validated the basic technical approaches suggested by the 1984 Corps leachate qualitymore » working group. However, the consensus was that much research remains to be done before a leach test (s) will be available for routine use.« less

Severe leaching of calcium ions from fir needles caused by acid fog.

PubMed

Igawa, Manabu; Kase, Toshiyuki; Satake, Kosuke; Okochi, Hiroshi

2002-01-01

We have measured the components of the throughfall under fir trees (Abies firma) in the field around Mt. Oyama, where the forest appears to be declining, for the period 1994-1998. Exposure experiments of a simulated acid fog to fir twigs were performed under field conditions. There was a similarity between the acid response in the field and that in the laboratory. In both studies, the severe leaching of calcium ions from the needle surface was caused by exposure to acid fog. We also applied acid fog to fir seedlings over 1 year and observed a decrease in the growth of the seedlings due to this application in the dormant season. These results suggest that the severe leaching of calcium ions due to acid fog may cause the deficiency of calcium and be responsible for the decline of the fir trees.

Recovery of cyanide in gold leach waste solution by volatilization and absorption.

PubMed

Gönen, N; Kabasakal, O S; Ozdil, G

2004-09-10

In this study, the effects of pH, time and temperature in regeneration of cyanide in the leaching waste solution of gold production from disseminated gold ore by cyanidation process were investigated and the optimum conditions, consumptions and cyanide recovery values were determined. The sample of waste solution containing 156 mg/l free CN- and 358 mg/l total CN-, that was obtained from Gümüşhane-Mastra/Turkey disseminated gold ores by cyanidation and carbon-in-pulp (CIP) process under laboratory conditions was used in the experiments. Acidification with H2SO4, volatilization of hydrogen cyanide (HCN) with air stripping and absorption of HCN in a basic solution stages were applied and under optimum conditions, 100% of free cyanide and 48% of complex cyanide and consequently 70% of the total cyanide in the liquid phase of gold leach effluent are recovered.

[Mixture Leaching Remediation Technology of Arsenic Contaminated Soil].

PubMed

Chen, Xun-feng; Li, Xiao-ming; Chen, Can; Yang, Qi; Deng, Lin-jing; Xie, Wei-qiang; Zhong, Yui; Huang, Bin; Yang, Wei-qiang; Zhang, Zhi-bei

2016-03-15

Soil contamination of arsenic pollution has become a severely environmental issue, while soil leaching is an efficient method for remediation of arsenic-contaminated soil. In this study, batch tests were primarily conducted to select optimal mixture leaching combination. Firstly, five conventional reagents were selected and combined with each other. Secondly, the fractions were analyzed before and after the tests. Finally, to explore the feasibility of mixed leaching, three soils with different arsenic pollution levels were used to compare the leaching effect. Comparing with one-step washing, the two-step sequential washing with different reagents increased the arsenic removal efficiency. These results showed that the mixture of 4 h 0.5 mol · L⁻¹ NaOH + 4 h 0.1 mol · L⁻¹ EDTA was found to be practicable, which could enhance the removal rate of arsenic from 66.67% to 91.83%, and the concentration of arsenic in soil was decreased from 186 mg · kg⁻¹ to 15.2 mg · kg⁻¹. Furthermore, the results indicated that the distribution of fractions of arsenic in soil changed apparently after mixture leaching. Leaching process could significantly reduce the available contents of arsenic in soil. Moreover, the mixture of 0.5 mol · L⁻¹ NaOH + 0.1 mol L⁻¹ EDTA could well decrease the arsenic concentration in aluminum-type soils, while the mixture of 0.5 mol · L⁻¹ OX + 0.5 mol · L⁻¹ NaOH could well decrease the arsenic concentration in iron-type soils.

Characterisation and classification of solid wastes coming from reductive acid leaching of low-grade manganiferous ore.

PubMed

De Michelis, Ida; Ferella, Francesco; Beolchini, Francesca; Olivieri, Agostino; Vegliò, Francesco

2009-03-15

The present work was focused on the acid leaching process for manganese extraction in reducing environment to low-grade manganiferous ore that comes from Central Italy. The aim of this study was to establish optimum leaching operating conditions to reduce treatment costs of waste or, even better, to allow a waste valorisation as raw materials for other applications. Consequently, the main focus of the work was the characterization and classification of the solid wastes coming from the process carried out at different operating conditions; at the same moment the effect of process parameters on Mn extraction was also analysed. The effect of particles size on the manganese extraction in reductive acid leaching process was investigated, by using lactose as reducing agent. Particle size did not show a large influence on the Mn extraction yields in the investigated process conditions. This aspect suggests the use of the leaching waste for civil and/or environmental application: use of leaching solid wastes like filling material is to be applied, for example, for environmental restoration. The classification of the solid wastes, according to the Italian Laws about Release Test (RT), has demonstrated that the solid waste produced by leaching can be classifiable as "hazardous special waste". An improvement of solid washing let to reduce the SO(4)(2-) and an appropriate treatment is necessary to reduce the dangerousness of these solids. Possible application of ore and waste as raw materials in the ceramic industry was demonstrated not to be feasible.

Reproducing ten years of road ageing--accelerated carbonation and leaching of EAF steel slag.

PubMed

Suer, Pascal; Lindqvist, Jan-Erik; Arm, Maria; Frogner-Kockum, Paul

2009-09-01

Reuse of industrial aggregates is still hindered by concern for their long-term properties. This paper proposes a laboratory method for accelerated ageing of steel slag, to predict environmental and technical properties, starting from fresh slag. Ageing processes in a 10-year old asphalt road with steel slag of electric arc furnace (EAF) type in the subbase were identified by scanning electron microscopy (SEM) and leaching tests. Samples from the road centre and the pavement edge were compared with each other and with samples of fresh slag. It was found that slag from the pavement edge showed traces of carbonation and leaching processes, whereas the road centre material was nearly identical to fresh slag, in spite of an accessible particle structure. Batches of moisturized road centre material exposed to oxygen, nitrogen or carbon dioxide (CO2) were used for accelerated ageing. Time (7-14 days), temperature (20-40 degrees C) and initial slag moisture content (8-20%) were varied to achieve the carbonation (decrease in pH) and leaching that was observed in the pavement edge material. After ageing, water was added to assess leaching of metals and macroelements. 12% moisture, CO2 and seven days at 40 degrees C gave the lowest pH value. This also reproduced the observed ageing effect for Ca, Cu, Ba, Fe, Mn, Pb, Ca (decreased leaching) and for V, Si, and Al (increased leaching). However, ageing effects on SO4, DOC and Cr were not reproduced.

The leaching kinetics of cadmium from hazardous Cu-Cd zinc plant residues.

PubMed

Li, Meng; Zheng, Shili; Liu, Biao; Du, Hao; Dreisinger, David Bruce; Tafaghodi, Leili; Zhang, Yi

2017-07-01

A large amount of Cu-Cd zinc plant residues (CZPR) are produced from the hydrometallurgical zinc plant operations. Since these residues contain substantial amount of heavy metals including Cd, Zn and Cu, therefore, they are considered as hazardous wastes. In order to realize decontamination treatment and efficient extraction of the valuable metals from the CZPR, a comprehensive recovery process using sulfuric acid as the leaching reagent and air as the oxidizing reagent has been proposed. The effect of temperature, sulfuric acid concentration, particle size, solid/liquid ratio and stirring speed on the cadmium extraction efficiency was investigated. The leaching kinetics of cadmium was also studied. It was concluded that the cadmium leaching process was controlled by the solid film diffusion process. Moreover, the order of the reaction rate constant versus H 2 SO 4 concentration, particle size, solid/liquid ratio and stirring speed was calculated. The XRD and SEM-EDS analysis results showed that the main phases of the secondary sulfuric acid leaching residues were lead sulfate and calcium sulfate. Copyright © 2017 Elsevier Ltd. All rights reserved.

Leaching characteristics of copper flotation waste before and after vitrification.

PubMed

Coruh, Semra; Ergun, Osman Nuri

2006-12-01

Copper flotation waste from copper production using a pyrometallurgical process contains toxic metals such as Cu, Zn, Co and Pb. Because of the presence of trace amounts of these highly toxic metals, copper flotation waste contributes to environmental pollution. In this study, the leaching characteristics of copper flotation waste from the Black Sea Copper Works in Samsun, Turkey have been investigated before and after vitrification. Samples obtained from the factory were subjected to toxicity tests such as the extraction procedure toxicity test (EP Tox), the toxicity characteristic leaching procedure (TCLP) and the "method A" extraction procedure of the American Society of Testing and Materials. The leaching tests showed that the content of some elements in the waste before vitrification exceed the regulatory limits and cannot be disposed of in the present form. Therefore, a stabilization or inertization treatment is necessary prior to disposal. Vitrification was found to stabilize heavy metals in the copper flotation waste successfully and leaching of these metals was largely reduced. Therefore, vitrification can be an acceptable method for disposal of copper flotation waste.

Lead, cadmium and cobalt (Pb, Cd, and Co) leaching of glass-clay containers by pH effect of food.

PubMed

Valadez-Vega, Carmen; Zúñiga-Pérez, Clara; Quintanar-Gómez, Samuel; Morales-González, José A; Madrigal-Santillán, Eduardo; Villagómez-Ibarra, José Roberto; Sumaya-Martínez, María Teresa; García-Paredes, Juan Diego

2011-01-01

Recent studies have shown that handcrafted glass-clay containers are a health risk because they can be contaminated by heavy metals, which can be transferred to food, thus reaching the human body to potentially cause illness. Therefore, in the present work, we evaluate the leaching of lead, cadmium, and cobalt from glass-clay containers into two types of food: tomato sauce (salsa), and chickpea puree. The containers were obtained from four regions in the Mexican state of Hidalgo. Repetitive extractions from the containers were carried out to quantify the leaching of the heavy metals into the salsa, the chickpea puree, and acetic acid using the technique proposed by the USFDA. The results show that greater use of the containers leads to more leaching of heavy metals into both types of food and into the acetic acid, with the greatest metal extraction recorded for the Ixmiquilpan vessels. These results indicate that the metals present in the glass-clay containers leach into the food and that increased reuse increases the risk to the people who use them in food preparation.

Lead, Cadmium and Cobalt (Pb, Cd, and Co) Leaching of Glass-Clay Containers by pH Effect of Food

PubMed Central

Valadez-Vega, Carmen; Zúñiga-Pérez, Clara; Quintanar-Gómez, Samuel; Morales-González, José A.; Madrigal-Santillán, Eduardo; Villagómez-Ibarra, José Roberto; Sumaya-Martínez, María Teresa; García-Paredes, Juan Diego

2011-01-01

Recent studies have shown that handcrafted glass-clay containers are a health risk because they can be contaminated by heavy metals, which can be transferred to food, thus reaching the human body to potentially cause illness. Therefore, in the present work, we evaluate the leaching of lead, cadmium, and cobalt from glass-clay containers into two types of food: tomato sauce (salsa), and chickpea puree. The containers were obtained from four regions in the Mexican state of Hidalgo. Repetitive extractions from the containers were carried out to quantify the leaching of the heavy metals into the salsa, the chickpea puree, and acetic acid using the technique proposed by the USFDA. The results show that greater use of the containers leads to more leaching of heavy metals into both types of food and into the acetic acid, with the greatest metal extraction recorded for the Ixmiquilpan vessels. These results indicate that the metals present in the glass-clay containers leach into the food and that increased reuse increases the risk to the people who use them in food preparation. PMID:21731445

Study on the properties of chromium residue-cement matrices (CRCM) and the influences of superplasticizers on chromium(VI)-immobilising capability of cement matrices.

PubMed

Shi, Hui-Sheng; Kan, Li-Li

2009-03-15

The study of cementitious activity of chromium residue (CR) was carried out to formulate the properties of chromium residue-cement matrices (CRCM) by blending CR with Ordinary Portland Cement (OPC). The particle size distribution, microstructures of CR were investigated by some apparatuses, and physical properties, leaching behavior of hexavalent chromium [Cr(VI)] of CRCM were also determined by some experiments. Three types of commonly used superplasticizers (sulphonated acetone formaldehyde superplasticizer (J1), polycarboxylate-based superplasticizer (J2) and naphthalene superplasticizer (J3)) were chosen to investigate their influences on the physical properties and the Cr(VI)-immobilisation in the leachate of the CRCM hardened pastes. The results show that the CR has a certain cementitious activity. The incorporation of CR improves the pore size distribution of CRCM. The Cr(VI) concentrations in the leachate of CRCM significantly decrease by incorporation of J2. Among three superplasticizers, J2 achieves lowest Cr(VI) leaching ratio. Based on this study, it is likely to develop CR as a potential new additive used in cement-based materials.

Effect of mineral constituents in the bioleaching of uranium from uraniferous sedimentary rock samples, Southwestern Sinai, Egypt.

PubMed

Amin, Maisa M; Elaassy, Ibrahim E; El-Feky, Mohamed G; Sallam, Abdel Sattar M; Talaat, Mona S; Kawady, Nilly A

2014-08-01

Bioleaching, like Biotechnology uses microorganisms to extract metals from their ore materials, whereas microbial activity has an appreciable effect on the dissolution of toxic metals and radionuclides. Bioleaching of uranium was carried out with isolated fungi from uraniferous sedimentary rocks from Southwestern Sinai, Egypt. Eight fungal species were isolated from different grades of uraniferous samples. The bio-dissolution experiments showed that Aspergillus niger and Aspergillus terreus exhibited the highest leaching efficiencies of uranium from the studied samples. Through monitoring the bio-dissolution process, the uranium grade and mineralogic constituents of the ore material proved to play an important role in the bioleaching process. The tested samples asserted that the optimum conditions of uranium leaching are: 7 days incubation time, 3% pulp density, 30 °C incubation temperature and pH 3. Both fungi produced the organic acids, namely; oxalic, acetic, citric, formic, malonic, galic and ascorbic in the culture filtrate, indicating an important role in the bioleaching processes. Copyright © 2014 Elsevier Ltd. All rights reserved.

Spatial variation in herbicide leaching from a marine clay soil via subsurface drains

PubMed Central

Ulén, Barbro M; Larsbo, Mats; Kreuger, Jenny K; Svanbäck, Annika

2013-01-01

Background Subsurface transport via tile drains can significantly contribute to pesticide contamination of surface waters. The spatial variation in subsurface leaching of normally applied herbicides was examined together with phosphorus losses in 24 experimental plots with water sampled flow-proportionally. The study site was a flat, tile-drained area with 60% marine clay in the topsoil in southeast Sweden. The objectives were to quantify the leaching of frequently used herbicides from a tile drained cracking clay soil and to evaluate the variation in leaching within the experimental area and relate this to topsoil management practices (tillage method and structure liming). Results In summer 2009, 0.14, 0.22 and 1.62%, respectively, of simultaneously applied amounts of MCPA, fluroxypyr and clopyralid were leached by heavy rain five days after spraying. In summer 2011, on average 0.70% of applied bentazone was leached by short bursts of intensive rain 12 days after application. Peak flow concentrations for 50% of the treated area for MCPA and 33% for bentazone exceeded the Swedish no-effect guideline values for aquatic ecosystems. Approximately 0.08% of the glyphosate applied was leached in dissolved form in the winters of 2008/2009 and 2010/2011. Based on measurements of glyphosate in particulate form, total glyphosate losses were twice as high (0.16%) in the second winter. The spatial inter-plot variation was large (72–115%) for all five herbicides studied, despite small variations (25%) in water discharge. Conclusions The study shows the importance of local scale soil transport properties for herbicide leaching in cracking clay soils. © 2013 The Authors. Pest Management Science published by John Wiley & Sons Ltd on behalf of Society of Chemical Industry. PMID:23658148

Process optimization and kinetics for leaching of rare earth metals from the spent Ni-metal hydride batteries.

PubMed

Meshram, Pratima; Pandey, B D; Mankhand, T R

2016-05-01

Nickel-metal hydride batteries (Ni-MH) contain not only the base metals, but valuable rare earth metals (REMs) viz. La, Sm, Nd, Pr and Ce as well. In view of the importance of resource recycling and assured supply of the contained metals in such wastes, the present study has focussed on the leaching of the rare earth metals from the spent Ni-MH batteries. The conditions for the leaching of REMs from the spent batteries were optimized as: 2M H2SO4, 348K temperature and 120min of time at a pulp density (PD) of 100g/L. Under this condition, the leaching of 98.1% Nd, 98.4% Sm, 95.5% Pr and 89.4% Ce was achieved. Besides the rare earth metals, more than 90% of base metals (Ni, Co, Mn and Zn) were also leached out in this condition. Kinetic data for the dissolution of all the rare earth metals showed the best fit to the chemical control shrinking core model. The leaching of metals followed the mechanism involving the chemical reaction proceeding on the surface of particles by the lixiviant, which was corroborated by the XRD phase analysis and SEM-EDS studies. The activation energy of 7.6, 6.3, 11.3 and 13.5kJ/mol was acquired for the leaching of neodymium, samarium, praseodymium and cerium, respectively in the temperature range 305-348K. From the leach liquor, the mixed rare earth metals were precipitated at pH∼1.8 and the precipitated REMs was analyzed by XRD and SEM studies to determine the phases and the morphological features. Copyright © 2015. Published by Elsevier Ltd.

Leaching characteristics of toxic constituents from coal fly ash mixed soils under the influence of pH.

PubMed

Komonweeraket, Kanokwan; Cetin, Bora; Benson, Craig H; Aydilek, Ahmet H; Edil, Tuncer B

2015-04-01

Leaching behaviors of Arsenic (As), Barium (Ba), Calcium (Ca), Cadmium (Cd), Magnesium (Mg), Selenium (Se), and Strontium (Sr) from soil alone, coal fly ash alone, and soil-coal fly ash mixtures, were studied at a pH range of 2-14 via pH-dependent leaching tests. Seven different types of soils and coal fly ashes were tested. Results of this study indicated that Ca, Cd, Mg, and Sr showed cationic leaching pattern while As and Se generally follows an oxyanionic leaching pattern. On the other hand, leaching of Ba presented amphoteric-like leaching pattern but less pH-dependent. In spite of different types and composition of soil and coal fly ash investigated, the study reveals the similarity in leaching behavior as a function of pH for a given element from soil, coal fly ash, and soil-coal fly ash mixtures. The similarity is most likely due to similar controlling mechanisms (e.g., solubility, sorption, and solid-solution formation) and similar controlling factors (e.g., leachate pH and redox conditions). This offers the opportunity to transfer knowledge of coal fly ash that has been extensively characterized and studied to soil stabilized with coal fly ash. It is speculated that unburned carbon in off-specification coal fly ashes may provide sorption sites for Cd resulting in a reduction in concentration of these elements in leachate from soil-coal fly ash mixture. Class C fly ash provides sufficient CaO to initiate the pozzolanic reaction yielding hydrated cement products that oxyanions, including As and Se, can be incorporated into. Copyright © 2014 Elsevier Ltd. All rights reserved.

Leaching of S-metolachlor, terbuthylazine, desethyl-terbuthylazine, mesotrione, flufenacet, isoxaflutole, and diketonitrile in field lysimeters as affected by the time elapsed between spraying and first leaching event.

PubMed

Milan, Marco; Ferrero, Aldo; Fogliatto, Silvia; Piano, Serenella; Vidotto, Francesco

2015-01-01

The effect of elapsed time between spraying and first leaching event on the leaching behavior of five herbicides (terbuthylazine, S-metolachlor, mesotrione, flufenacet, and isoxaflutole) and two metabolites (desethyl-terbuthylazine and diketonitrile) was evaluated in a 2011-2012 study in northwest Italy. A battery of 12 lysimeters (8.4 m(2) long with a depth of 1.8 m) were used in the study, each filled with silty-loam soil and treated during pre-emergence with the selected herbicides by applying a mixture of commercial products Lumax (4 L ha(-1)) and Merlin Gold (1 L ha(-1)). During treatment periods, no gravity water was present in lysimeters. Irrigation events capable of producing leaching (40 mm) were conducted on independent groups of three lysimeters on 1 day after treatment (1 DAT), 7 DAT, 14 DAT, and 28 DAT. The series was then repeated 14 days later. Leachate samples were collected a few days after irrigation; compounds were extracted by solid phase extraction and analyzed by high-performance liquid chromatography and gas chromatography-mass spectrometry. Under study conditions, terbuthylazine and S-metolachlor showed the highest leaching potentials. Specifically, S-metolachlor concentrations were always found above 0.25 µg L(-1). Desethyl-terbuthylazine was often detected in leached waters, in most cases at concentrations above 0.1 µg L(-1). Flufenacet leached only when irrigation occurred close to the time of herbicide spraying. Isoxaflutole and mesotrione were not measured (<0.1 µg L(-1)), while diketonitrile was detected in concentrations above 0.1 µg L(-1) on 1 DAT in 2011 only.

Reducing acid leaching of manganiferous ore: Effect of the iron removal operation on solid waste disposal

DOE Office of Scientific and Technical Information (OSTI.GOV)

De Michelis, Ida; Ferella, Francesco; Beolchini, Francesca

2009-01-15

The process of reducing acid leaching of manganiferous ore is aimed at the extraction of manganese from low grade manganese ores. This work is focused on the iron removal operation. The following items have been considered in order to investigate the effect of the main operating conditions on solid waste disposal and on the process costs: (i) type and quantity of the base agent used for iron precipitation, (ii) effective need of leaching waste separation prior to the iron removal operation, (iii) presence of a second leaching stage with the roasted ore, which might also act as a preliminary ironmore » removal step, and (iv) effect of tailings washing on the solid waste classification. Different base compounds have been tested, including CaO, CaCO{sub 3}, NaOH, and Na{sub 2}CO{sub 3}. The latter gave the best results concerning both the precipitation process kinetics and the reagent consumption. The filtration of the liquor leach prior to iron removal was not necessary, implying significant savings in capital costs. A reduction of chemical consumption and an increase of manganese concentration in the solution were obtained by introducing secondary leaching tests with the previously roasted ore; this additional step was introduced without a significant decrease of global manganese extraction yield. Finally, toxicity characteristic leaching procedure (TCLP) tests carried out on the leaching solid waste showed: (i) a reduction of arsenic mobility in the presence of iron precipitates, and (ii) the need for a washing step in order to produce a waste that is classifiable as not dangerous, taking into consideration the existing Environmental National Laws.« less

Catch crops as universal and effective method for reducing nitrogen leaching loss in spring cereal production: A meta-analysis.

NASA Astrophysics Data System (ADS)

Valkama, Elena; Lemola, Riitta; Känkänen, Hannu; Turtola, Eila

2016-04-01

Sustainable farms produce adequate amounts of a high-quality product, protect their resources and are both environmentally friendly and economically profitable. Nitrogen (N) fertilization decisively influences the cereal yields as well as increases soil N balance (N input in fertilizer - N output in harvested yield), thereby leading to N losses to the environment. However, while N input reduction affects soil N balance, such approach would markedly reduce N leaching loss only in case of abnormally high N balances. As an alternative approach, the growing of catch crops aims to prevent nutrient leaching in autumn after harvest and during the following winter, but due to competition, catch crops may also reduce yields of the main crop. Although studies have explored the environmental effects of catch crops in cereal production in the Nordic countries (Denmark, Sweden, Finland and Norway) during the past 40 years, none has yet carried out a meta-analysis. We quantitatively summarized 35 studies on the effect of catch crops (non-legume and legume) undersown in spring cereals on N leaching loss or its risk as estimated by the content of soil nitrate N or its sum with ammonium in late autumn. The meta-analysis also included the grain yield and N content of spring cereals. To identify sources of variation, we studied the effects of soil texture and management (ploughing time, the amount of N applied, fertilizer type), as well as climatic (annual precipitation) and experimental conditions (duration of experiments, lysimeter vs. field experiments). Finally, we examined whether the results differed between the countries or over the decades. Compared to control groups with no catch crops, non-legume catch crops, mainly ryegrass species, reduced N leaching loss by 50% on average, and soil nitrate N or inorganic N by 35% in autumn. Italian ryegrass depleted soil N more effectively (by 60%) than did perennial ryegrass or Westerwolds ryegrass (by 25%). In contrast, legumes (white and red clovers) did not diminish the risk for N leaching. Otherwise, the effect on N leaching and its risk were consistent across the studies conducted in different countries on clay and coarse-textured mineral soils with different ploughing times, N fertilization rates (50-160 kg/ ha), and amounts of annual precipitation (480-1040 mm). Non-legume catch crops reduced grain yield by 3% with no changes in grain N content. In contrast, legumes and mixed catch crops increased both grain yield and grain N content by 6%. In spring cereal production, undersown non-legume catch crops are deemed a universal and effective method for reducing N leaching loss across the various soils, management practices and weather conditions in the Nordic countries. The environmental benefits of using non-legume catch crops appear considerable compared to the adverse reduction in grain yields, amounting to only a few percent. Catch crops are advisable for fields at high risk for N leaching (e.g., sandy soils or soils and crops requiring high N fertilization).

Trace elements in coal ash

USGS Publications Warehouse

Deonarine, Amrika; Kolker, Allan; Doughten, Michael W.

2015-01-01

In this fact sheet, the form, distribution, and behavior of trace elements of environmental interest in samples of coal fly ash were investigated in response to concerns about element mobility in the event of an ash spill. The study includes laboratory-based leaching experiments to examine the behavior of trace elements, such as arsenic (As) and chromium (Cr), in response to key environmental factors including redox conditions (degree of oxygenation), which are known to vary with depth within coal ash impoundments and in natural ecosystems. The experiments show that As dissolves from samples of coal fly ash into simulated freshwater under both oxic (highly oxygenated) and anoxic (poorly oxygenated) conditions, whereas dissolved Cr concentrations are very redox dependent. This U.S. Geological Survey research helps define the distribution of elements such as As in coal ash and shows that element mobility can vary considerably under different conditions expected in the environment.

Studies on aluminium leaching from cookware in tea and coffee and estimation of aluminium content in toothpaste, baking powder and paan masala.

PubMed

Rajwanshi, P; Singh, V; Gupta, M K; Kumari, V; Shrivastav, R; Ramanamurthy, M; Dass, S

1997-01-30

Studies were conducted in order to assess the level of aluminium (Al) in samples of Indian tea, coffee, toothpaste, paan masala (mouth freshener) and baking powder. Leaching of Al from cookware while preparing tea and coffee was also studied. Experiments were also conducted to study the sequential leaching of Al from cookware by preparing tea and coffee in the presence of standard size Al sheets (coupons). A small amount of Al was found to have leached from coupons during preparation of tea. Tea leaves, were found to be a rich source of Al and a maximum of 2.2% Al is extracted in tea infusions. Coffee powder on the other hand was not found to be a rich source of Al. Baking powder was found to be a rich source of Al and 1 kg of cake prepared with 1-3 teaspoon of baking powder may contain 2-12.7 mg of Al in each serving (25 g). Toothpaste also contains a significant quantity of Al, more so, when packed in Al tubes. Ingestion pattern of Al from these items by humans is also discussed.

Re-evaluation of the sorption behaviour of Bromide and Sulfamethazine under field conditions using leaching data and modelling methods

NASA Astrophysics Data System (ADS)

Gassmann, Matthias; Olsson, Oliver; Höper, Heinrich; Hamscher, Gerd; Kümmerer, Klaus

2016-04-01

The simulation of reactive transport in the aquatic environment is hampered by the ambiguity of environmental fate process conceptualizations for a specific substance in the literature. Concepts are usually identified by experimental studies and inverse modelling under controlled lab conditions in order to reduce environmental uncertainties such as uncertain boundary conditions and input data. However, since environmental conditions affect substance behaviour, a re-evaluation might be necessary under environmental conditions which might, in turn, be affected by uncertainties. Using a combination of experimental data and simulations of the leaching behaviour of the veterinary antibiotic Sulfamethazine (SMZ; synonym: sulfadimidine) and the hydrological tracer Bromide (Br) in a field lysimeter, we re-evaluated the sorption concepts of both substances under uncertain field conditions. Sampling data of a field lysimeter experiment in which both substances were applied twice a year with manure and sampled at the bottom of two lysimeters during three subsequent years was used for model set-up and evaluation. The total amount of leached SMZ and Br were 22 μg and 129 mg, respectively. A reactive transport model was parameterized to the conditions of the two lysimeters filled with monoliths (depth 2 m, area 1 m²) of a sandy soil showing a low pH value under which Bromide is sorptive. We used different sorption concepts such as constant and organic-carbon dependent sorption coefficients and instantaneous and kinetic sorption equilibrium. Combining the sorption concepts resulted in four scenarios per substance with different equations for sorption equilibrium and sorption kinetics. The GLUE (Generalized Likelihood Uncertainty Estimation) method was applied to each scenario using parameter ranges found in experimental and modelling studies. The parameter spaces for each scenario were sampled using a Latin Hypercube method which was refined around local model efficiency maxima. Results of the cumulative SMZ leaching simulations suggest a best conceptualization combination of instantaneous sorption to organic carbon which is consistent with the literature. The best Nash-Sutcliffe efficiency (Neff) was 0.96 and the 5th and 95th percentile of the uncertainty estimation were 18 and 27 μg. In contrast, both scenarios of kinetic Br sorption had similar results (Neff =0.99, uncertainty bounds 110-176 mg and 112-176 mg) but were clearly better than instantaneous sorption scenarios. Therefore, only the concept of sorption kinetics could be identified for Br modelling whereas both tested sorption equilibrium coefficient concepts performed equally well. The reasons for this specific case of equifinality may be uncertainties of model input data under field conditions or an insensitivity of the sorption equilibrium method due to relatively low adsorption of Br. Our results show that it may be possible to identify or at least falsify specific sorption concepts under uncertain field conditions using a long-term leaching experiment and modelling methods. Cases of environmental fate concept equifinality arouse the possibility of future model structure uncertainty analysis using an ensemble of models with different environmental fate concepts.

Nutrient leaching losses in lowland forests converted to oil palm and rubber plantations in Sumatra, Indonesia

NASA Astrophysics Data System (ADS)

Kurniawan, Syahrul; Corre, Marife D.; Rahayu Utami, Sri; Veldkamp, Edzo

2015-04-01

In the last two decades, Sumatra, Indonesia is experiencing rapid expansion of oil palm and rubber plantations by conversion of rainforest. This is evident from the 2.9 thousand km2 decrease in forest area in this region over the last 15 years. Such rapid land-use change necessitates assessment of its environmental impacts. Our study was aimed to assess the impact of forest conversion to oil palm and rubber plantations on nutrient leaching losses. Land-use conversion increases nutrient leaching losses due to changes in vegetation litter input, rooting depth, nutrient cycling and management (e.g. fertilization) practices. Our study area was in Jambi Province, Sumatra, Indonesia. We selected two soil landscapes in this region: loam and clay Acrisol soils. At each soil landscape, we investigated four land-use systems: lowland secondary rainforest, secondary forest with regenerating rubber (referred here as jungle rubber), rubber (7-17 years old) and oil palm plantations (9-16 years old). Each land use in each soil landscape was represented by four sites as replicates, totaling to 32 sites. We measured leaching losses using suction lysimeters installed at 1.5-m soil depth, which was well below the rooting depth, with bi-weekly to monthly sampling from February to December 2013. In general, the loam Acrisol landscape, particularly the forest and oil palm plantations, had lower soil solution pH and higher leaching fluxes of dissolved organic N, Na, Ca, Mg, total Al, total S and Cl than the clay Acrisol of the same land uses (all P ≤ 0.05). Among land uses in the loam Acrisol landscape, oil palm had lower soil solution pH and higher leaching fluxes of NH4+, NO3-, dissolved organic C, total P, total S and Cl than rubber plantation whereas forest and jungle rubber showed intermediate fluxes (all P ≤ 0.05, except P ≤ 0.09 for total P); oil palm had also higher Na, Ca, Mg and total Al leaching fluxes than all the other land uses (all P ≤ 0.05, except P ≤ 0.09 for Na and Mg). In the clay Acrisol landscape, oil palm showed higher leaching losses of dissolved organic C and Ca than forest whereas jungle rubber and rubber plantation had intermediate fluxes; oil palm had also higher Na, Mg and total Si leaching losses than all the other land uses (all P ≤ 0.05). The low soil solution pH, which was negatively correlated with total Al, and large mineral N and total P leaching losses in oil palm were due to N and P fertilization, and the large base cation losses were attributable to liming and ash from biomass burning. Such increased nutrient leaching losses with forest conversion to oil palm plantation calls for improved management to minimize losses and its effects on ground water quality.

Selective reductive leaching of cobalt and lithium from industrially crushed waste Li-ion batteries in sulfuric acid system.

PubMed

Peng, Chao; Hamuyuni, Joseph; Wilson, Benjamin P; Lundström, Mari

2018-06-01

Recycling of valuable metals from secondary resources such as waste Li-ion batteries (LIBs) has recently attracted significant attention due to the depletion of high-grade natural resources and increasing interest in the circular economy of metals. In this article, the sulfuric acid leaching of industrially produced waste LIBs scraps with 23.6% cobalt (Co), 3.6% lithium (Li) and 6.2% copper (Cu) was investigated. The industrially produced LIBs scraps were shown to provide higher Li and Co leaching extractions compared to dissolution of corresponding amount of pure LiCoO 2 . In addition, with the addition of ascorbic acid as reducing agent, copper extraction showed decrease, opposite to Co and Li. Based on this, we propose a new method for the selective leaching of battery metals Co and Li from the industrially crushed LIBs waste at high solid/liquid ratio (S/L) that leaves impurities like Cu in the solid residue. Using ascorbic acid (C 6 H 8 O 6 ) as reductant, the optimum conditions for LIBs leaching were found to be T = 80 °C, t = 90 min, [H 2 SO 4 ] = 2 M, [C 6 H 8 O 6 ] = 0.11 M and S/L = 200 g/L. This resulted in leaching efficiencies of 95.7% for Li and 93.8% for Co, whereas in contrast, Cu extraction was only 0.7%. Consequently, the proposed leaching method produces a pregnant leach solution (PLS) with high Li (7.0 g/L) and Co (44.4 g/L) concentration as well as a leach residue rich in Cu (up to 12 wt%) that is suitable as a feed fraction for primary or secondary copper production. Copyright © 2018 Elsevier Ltd. All rights reserved.

The contribution of leaching to the rapid release of nutrients and carbon in the early decay of wetland vegetation

USGS Publications Warehouse

Davis, S. E.; Childers, D.L.; Noe, G.B.

2006-01-01

Our goal was to quantify the coupled process of litter turnover and leaching as a source of nutrients and fixed carbon in oligotrophic, nutrient-limited wetlands. We conducted poisoned and non-poisoned incubations of leaf material from four different perennial wetland plants (Eleocharis spp., Cladium jamaicense, Rhizophora mangle and Spartina alterniflora) collected from different oligotrophic freshwater and estuarine wetland settings. Total phosphorus (TP) release from the P-limited Everglades plant species (Eleocharis spp., C. jamaicense and R. mangle) was much lower than TP release by the salt marsh plant S. alterniflora from N-limited North Inlet (SC). For most species and sampling times, total organic carbon (TOC) and TP leaching losses were much greater in poisoned than non-poisoned treatments, likely as a result of epiphytic microbial activity. Therefore, a substantial portion of the C and P leached from these wetland plant species was bio-available to microbial communities. Even the microbes associated with S. alterniflora from N-limited North Inlet showed indications of P-limitation early in the leaching process, as P was removed from the water column. Leaves of R. mangle released much more TOC per gram of litter than the other species, likely contributing to the greater waterborne [DOC] observed by others in the mangrove ecotone of Everglades National Park. Between the two freshwater Everglades plants, C. jamaicense leached nearly twice as much P than Eleocharis spp. In scaling this to the landscape level, our observed leaching losses combined with higher litter production of C. jamaicense compared to Eleocharis spp. resulted in a substantially greater P leaching from plant litter to the water column and epiphytic microbes. In conclusion, leaching of fresh plant litter can be an important autochthonous source of nutrients in freshwater and estuarine wetland ecosystems. ?? Springer 2006.

Roasting and leaching behaviors of vanadium and chromium in calcification roasting-acid leaching of high-chromium vanadium slag

NASA Astrophysics Data System (ADS)

Wen, Jing; Jiang, Tao; Zhou, Mi; Gao, Hui-yang; Liu, Jia-yi; Xue, Xiang-xin

2018-05-01

Calcification roasting-acid leaching of high-chromium vanadium slag (HCVS) was conducted to elucidate the roasting and leaching behaviors of vanadium and chromium. The effects of the purity of CaO, molar ratio between CaO and V2O5 ( n(CaO)/ n(V2O5)), roasting temperature, holding time, and the heating rate used in the oxidation-calcification processes were investigated. The roasting process and mechanism were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), and thermogravimetry-differential scanning calorimetry (TG-DSC). The results show that most of vanadium reacted with CaO to generate calcium vanadates and transferred into the leaching liquid, whereas almost all of the chromium remained in the leaching residue in the form of (Fe0.6Cr0.4)2O3. Variation trends of the vanadium and chromium leaching ratios were always opposite because of the competitive reactions of oxidation and calcification between vanadium and chromium with CaO. Moreover, CaO was more likely to combine with vanadium, as further confirmed by thermodynamic analysis. When the HCVS with CaO added in an n(CaO)/ n(V2O5) ratio of 0.5 was roasted in an air atmosphere at a heating rate of 10°C/min from room temperature to 950°C and maintained at this temperature for 60 min, the leaching ratios of vanadium and chromium reached 91.14% and 0.49%, respectively; thus, efficient extraction of vanadium from HCVS was achieved and the leaching residue could be used as a new raw material for the extraction of chromium. Furthermore, the oxidation and calcification reactions of the spinel phases occurred at 592 and 630°C for n(CaO)/ n(V2O5) ratios of 0.5 and 5, respectively.

Estimation of Cadmium uptake by tobacco plants from laboratory leaching tests.

PubMed

Marković, Jelena P; Jović, Mihajlo D; Smičiklas, Ivana D; Šljivić-Ivanović, Marija Z; Smiljanić, Slavko N; Onjia, Antonije E; Popović, Aleksandar R

2018-03-21

The objective of the present study was to determine the impact of cadmium (Cd) concentration in the soil on its uptake by tobacco plants, and to compare the ability of diverse extraction procedures for determining Cd bioavailability and predicting soil-to-plant transfer and Cd plant concentrations. The pseudo-total digestion procedure, modified Tessier sequential extraction and six standard single-extraction tests for estimation of metal mobility and bioavailability were used for the leaching of Cd from a native soil, as well as samples artificially contaminated over a wide range of Cd concentrations. The results of various leaching tests were compared between each other, as well as with the amounts of Cd taken up by tobacco plants in pot experiments. In the native soil sample, most of the Cd was found in fractions not readily available under natural conditions, but with increasing pollution level, Cd amounts in readily available forms increased. With increasing concentrations of Cd in the soil, the quantity of pollutant taken up in tobacco also increased, while the transfer factor (TF) decreased. Linear and non-linear empirical models were developed for predicting the uptake of Cd by tobacco plants based on the results of selected leaching tests. The non-linear equations for ISO 14870 (diethylenetriaminepentaacetic acid extraction - DTPA), ISO/TS 21268-2 (CaCl 2 leaching procedure), US EPA 1311 (toxicity characteristic leaching procedure - TCLP) single step extractions, and the sum of the first two fractions of the sequential extraction, exhibited the best correlation with the experimentally determined concentrations of Cd in plants over the entire range of pollutant concentrations. This approach can improve and facilitate the assessment of human exposure to Cd by tobacco smoking, but may also have wider applicability in predicting soil-to-plant transfer.

The association of uranium with organic matter in Holocene peat: An experimental leaching study

USGS Publications Warehouse

Zielinski, R.A.; Meier, A.L.

1988-01-01

Uraniferous peat was sampled from surface layers of a Holocene U deposit in northeastern Washington State. Dried, sized, and homogenized peat that contained 5980 ??307 ppm U was subjected to a variety of leaching conditions to determine the nature and strength of U-organic bonding in recently accumulated organic matter. The results complement previous experimental studies of U uptake on peat and suggest some natural or anthropogenic disturbances that are favorable for remobilizing U. The fraction of U leached in 24 h experiments at 25??C ranged from 0 to 95%. The most effective leach solutions contained anions capable of forming stable dissolved complexes with uranyl (UO2+2) cation. These included H2SO4 (pH = 1.5) and concentrated (>0.01 M) solutions of sodium bicarbonate-carbonate (pH = 7.0-10.0), or sodium pyrophosphate (pH = 10). Effective leaching by carbonate and pyrophosphate in the absence of added oxidant, and the insignificant effect of added oxidant (as pressurized O2) strongly suggest that U is initially fixed on organic matter as an oxidized U(VI) species. Uranium is more strongly bound than some other polyvalent cations, based on its resistance to exchange in the presence of large excesses of dissolved Ca2+ and Cu2+. Measurements of the rate of U leaching indicate faster rates in acid solution compared to carbonate solution, and are consisten with simultaneous attack of sites with different affinities for U. Sulfuric acid appears a good choice for commercial extraction of U from mined peat. In situ disturbances such as overliming of peat soils, addition of fertilizers containing pyrophosphate, or incursions of natural carbonate-rich waters could produce significant remobilization of U, and possibly compromise the quality of local domestic water supplies. ?? 1988.

Longer thaw seasons increase nitrogen availability for leaching during fall in tundra soils

DOE PAGES

Treat, Claire C.; Wollheim, Wilfred M.; Varner, Ruth K.; ...

2016-06-15

Climate change has resulted in warmer soil temperatures, earlier spring thaw and later fall freeze-up, resulting in warmer soil temperatures and thawing of permafrost in tundra regions. While these changes in temperature metrics tend to lengthen the growing season for plants, light levels, especially in the fall, will continue to limit plant growth and nutrient uptake. We conducted a laboratory experiment using intact soil cores with and without vegetation from a tundra peatland to measure the effects of late freeze and early spring thaw on carbon dioxide (CO 2) exchange, methane (CH 4) emissions, dissolved organic carbon (DOC) and nitrogenmore » (N) leaching from soils. We compared soil C exchange and N production with a 30 day longer seasonal thaw during a simulated annual cycle from spring thaw through freeze-up and thaw. Across all cores, fall N leaching accounted for similar to 33% of total annual N loss despite significant increases in microbial biomass during this period. Nitrate(NO 3 -) leaching was highest during the fall (5.33 ± 1.45 mgNm -2 d -1) following plant senescence and lowest during the summer (0.43 ± 0.22 mg Nm -2 d -1). In the late freeze and early thaw treatment, we found 25% higher total annual ecosystem respiration but no significant change in CH 4 emissions or DOC loss due to high variability among samples. The late freeze period magnified N leaching and likely was derived from root turnover and microbial mineralization of soil organic matter coupled with little demand from plants or microbes. Furthermore, large N leaching during the fall will affect N cycling in low-lying areas and streams and may alter terrestrial and aquatic ecosystem nitrogen budgets in the arctic.« less

Risk mitigation by waste-based permeable reactive barriers for groundwater pollution control at e-waste recycling sites.

PubMed

Beiyuan, Jingzi; Tsang, Daniel C W; Yip, Alex C K; Zhang, Weihua; Ok, Yong Sik; Li, Xiang-Dong

2017-02-01

Permeable reactive barriers (PRBs) have proved to be a promising passive treatment to control groundwater contamination and associated human health risks. This study explored the potential use of low-cost adsorbents as PRBs media and assessed their longevity and risk mitigation against leaching of acidic rainfall through an e-waste recycling site, of which Cu, Zn, and Pb were the major contaminants. Batch adsorption experiments suggested a higher adsorption capacity of inorganic industrial by-products [acid mine drainage sludge (AMDS) and coal fly ash (CFA)] and carbonaceous recycled products [food waste compost (FWC) and wood-derived biochar] compared to natural inorganic minerals (limestone and apatite). Continuous leaching tests of sand columns with 10 wt% low-cost adsorbents were then conducted to mimic the field situation of acidic rainfall infiltration through e-waste-contaminated soils (collected from Qingyuan, China) by using synthetic precipitation leaching procedure (SPLP) solution. In general, Zn leached out first, followed by Cu, and finally delayed breakthrough of Pb. In the worst-case scenario (e.g., at initial concentrations equal to 50-fold of average SPLP result), the columns with limestone, apatite, AMDS, or biochar were effective for a relatively short period of about 20-40 pore volumes of leaching, after which Cu breakthrough caused non-cancer risk concern and later-stage Pb leaching considerably increased both non-cancer and lifetime cancer risk associated with portable use of contaminated water. In contrast, the columns with CFA or FWC successfully mitigated overall risks to an acceptable level for a prolonged period of 100-200 pore volumes. Therefore, with proper selection of low-cost adsorbents (or their mixture), waste-based PRBs is a technically feasible and economically viable solution to mitigate human health risk due to contaminated groundwater at e-waste recycling sites.

Release of Arsenic to the Environment from CCA-Treated Wood: Part II – Leaching and Speciation during Disposal

PubMed Central

KHAN, BERNINE I.; JAMBECK, JENNA; SOLO-GABRIELE, HELENA M.; TOWNSEND, TIMOTHY G.; CAI, YONG

2008-01-01

Wood treated with chromated copper arsenate (CCA) is primarily disposed within construction and demolition (C&D) debris landfills, with wood monofills and municipal solid waste (MSW) landfills as alternative disposal options. This study evaluated the extent and speciation of arsenic leaching from landfills containing CCA-treated wood. In control lysimeters where untreated wood was used, DMAA represented the major arsenic species. The dominant arsenic species differed in the lysimeters containing CCA-treated wood, with As(V) greatest in the monofill and C&D lysimeters and As(III) greatest in the MSW lysimeters. In CCA-containing lysimeters, the organoarsenic species MMAA and DMAA were virtually absent in the monofill lysimeter and observed in the C&D and MSW lysimeters. Overall arsenic leaching rate varied for the wood monofill (0.69% per meter of water added), C&D (0.36% per m), and MSW (0.84% per m) lysimeters. Utilizing these rates with annual disposal data, a mathematical model was developed to quantify arsenic leaching from CCA-treated wood disposed to Florida landfills. Model findings showed between 20 to 50 metric tons of arsenic (depending on lysimeter type) had leached prior to 2000 with an expected increase between 350 to 830 metric tons by 2040. Groundwater analysis from 21 Florida C&D landfills suspected of accepting CCA-treated wood showed that groundwater at 3 landfills were characterized by elevated arsenic concentrations with only 1 showing impacts from the C&D waste. The slow release of arsenic from disposed treated wood may account for the lack of significant impact to groundwater near most C&D facilities at this time. However, greater impacts are anticipated in the future given that the maximum releases of arsenic are expected by the year 2100. PMID:16509348

Volcanic ash leachate compositions and assessment of health and agricultural hazards from 2012 hydrothermal eruptions, Tongariro, New Zealand

NASA Astrophysics Data System (ADS)

Cronin, S. J.; Stewart, C.; Zernack, A. V.; Brenna, M.; Procter, J. N.; Pardo, N.; Christenson, B.; Wilson, T.; Stewart, R. B.; Irwin, M.

2014-10-01

After almost 80 years of quiescence, the upper Te Maari vent on Mt. Tongariro erupted suddenly at 2352 h (NZ time) on 6 August 2012. The short-lived hydrothermal eruption distributed a fine ash of minor volume (~ 5 × 105 m3) over 200 km from source. The threat of further eruptions prompted an investigation of the possible health and agricultural impacts of any future eruptions from this volcano, particularly since the most recent large-scale ash falls in New Zealand in 1995-1996 had generated significant agricultural problems, including livestock deaths. Deposited ash was sampled between 5 and 200 km from the volcano as soon as possible after the eruption. Two sub-lobes of ash were identified from different vent areas and displayed subtly different leaching properties. The first was an initial small lobe directed NNE, likely formed from drifting low-level clouds associated with the initial lateral explosive blast and surges. The main fall lobe, directed eastward, was sourced from a short-lived vertical plume that rose up to c. 8 km. Ash from the initial fall lobe had higher concentrations of F and Al, in single-step leaches as well as in the totals of three, sequential extractions. Further, the initial lobe showed a higher proportion of soluble F and Al extracted in the first leach, compared to totals. A linear relationship between concentrations of Al and F in single leaches from the 6 August eruption was highly significant (Pearson correlation coefficient r = 0.987 for 1:20 leaching ratios and r = 0.971 for 1:100), suggesting the presence of soluble alumino-fluoride complexes (AlFx+ 3 - x). An even more significant 1:1 ratio is displayed for the largest concentration leached ions of Ca and SO4, which correspond to the presence of crystalline gypsum throughout the newly excavated hydrothermal system. Although no fresh magma was erupted in this event, a shallow intrusion prior to the hydrothermal explosion apparently provided significant contents of volcanic gas that was dissolved within the hydrothermal fluids and adhering to ejected particles. This and the ubiquitous presence of gypsum dominated the soluble components of these ash deposits leading to a complex leaching profile. The leaching study carried out here showed that agricultural and human health hazard assessment (particularly of F and S) is not straightforward, particularly because F solubility may be complex and not well characterised by simple leaching studies. In the case of S, which is agriculturally important, saturation effects are apparent using normal leaching protocols and also imply a need for modification of standard methods.

Acid leaching of natural chrysotile asbestos to mesoporous silica fibers

NASA Astrophysics Data System (ADS)

Maletaškić, Jelena; Stanković, Nadežda; Daneu, Nina; Babić, Biljana; Stoiljković, Milovan; Yoshida, Katsumi; Matović, Branko

2018-04-01

Nanofibrous silica with a high surface area was produced from chrysotile by the acid-leaching method. Natural mineral chrysotile asbestos from Stragari, Korlace in Serbia was used as the starting material. The fibers were modified by chemical treatment with 1 M HCl and the mineral dissolution was monitored by transmission electron microscopy, X-ray powder diffraction, inductively coupled plasma spectrometry and low-temperature nitrogen adsorption techniques to highlight the effects of the leaching process. The results showed that the applied concentration of acid solution and processing time of 4 h were sufficient to effectively remove the magnesium hydroxide layer and transform the crystal structure of the hazardous starting chrysotile to porous SiO2 nanofibers. With prolonged acid leaching, the specific surface area, S BET, calculated by BET equation, was increased from 147 up to 435 m2 g- 1, with micropores representing a significant part of the specific surface.

Study on leaching of pollutants from vegetable tanning residue.

PubMed

Mazumder, Debabrata; Biswas, Santosh; Bandyopadhyay, Pratip

2006-07-01

The processing of heavy leather employs the vegetable tanning method involving use of tan liquor. The solid residue of this vegetable tanning process aggravates the water pollution by means of leaching of tannin and other associatedpollutants. Tannin is a biologically resistant compound causing several problems in animal body. The present study dealt with the pollution hazard arising out of leaching of pollutants from the open dumped vegetable tanning residue by rainfall washing. The concerned pollutants were pH, Chemical Oxygen Demand (COD), tannin,sulfate and chloride concentration. To explore the possible extent of contamination of these pollutants in the leached water, two different masses (2 kg and 3 kg) of tanning residue were employed. The results of the study showed that there was a continuous release of pollutants from the vegetable tanning residue. Moreover, there was no regular variation in various pollutant concentrations in both the cases solely due to non-homogeneity of the residue.

Experimental investigation of influence of acid rain on leaching and hydraulic characteristics of cement-based solidified/stabilized lead contaminated clay.

PubMed

Du, Yan-Jun; Jiang, Ning-Jun; Shen, Shui-Long; Jin, Fei

2012-07-30

Remediation of contaminated lands in China urban areas is of great concern. Degradation of construction facilities caused by acid rain is a serious environmental pollution issue in China. This paper presents an investigation of the effects of acid rain on leaching and hydraulic properties of cement-based solidified/stabilized lead contaminated soil. Laboratory tests including infiltration test and soaking test are conducted. It is found that the soil hydraulic conductivity decreases with increase in the pore volume of flow of permeant liquids (acid rain and distilled water). The decreasing rate in the case of the acid rain is lower than that in the case of the distilled water. The soaking test results show that pH and the presence of sulfate ions of acid rain have considerable influence on the leached concentrations and leaching rate of calcium. Copyright © 2012 Elsevier B.V. All rights reserved.

Extensive Management Promotes Plant and Microbial Nitrogen Retention in Temperate Grassland

PubMed Central

de Vries, Franciska T.; Bloem, Jaap; Quirk, Helen; Stevens, Carly J.; Bol, Roland; Bardgett, Richard D.

2012-01-01

Leaching losses of nitrogen (N) from soil and atmospheric N deposition have led to widespread changes in plant community and microbial community composition, but our knowledge of the factors that determine ecosystem N retention is limited. A common feature of extensively managed, species-rich grasslands is that they have fungal-dominated microbial communities, which might reduce soil N losses and increase ecosystem N retention, which is pivotal for pollution mitigation and sustainable food production. However, the mechanisms that underpin improved N retention in extensively managed, species-rich grasslands are unclear. We combined a landscape-scale field study and glasshouse experiment to test how grassland management affects plant and soil N retention. Specifically, we hypothesised that extensively managed, species-rich grasslands of high conservation value would have lower N loss and greater N retention than intensively managed, species-poor grasslands, and that this would be due to a greater immobilisation of N by a more fungal-dominated microbial community. In the field study, we found that extensively managed, species-rich grasslands had lower N leaching losses. Soil inorganic N availability decreased with increasing abundance of fungi relative to bacteria, although the best predictor of soil N leaching was the C/N ratio of aboveground plant biomass. In the associated glasshouse experiment we found that retention of added 15N was greater in extensively than in intensively managed grasslands, which was attributed to a combination of greater root uptake and microbial immobilisation of 15N in the former, and that microbial immobilisation increased with increasing biomass and abundance of fungi. These findings show that grassland management affects mechanisms of N retention in soil through changes in root and microbial uptake of N. Moreover, they support the notion that microbial communities might be the key to improved N retention through tightening linkages between plants and microbes and reducing N availability. PMID:23227252

Effects of biodegradation and mechanical activation on gold recovery by thiourea leaching

NASA Astrophysics Data System (ADS)

Kušnierová, Mária; Šepelák, Vladimír; Briančin, Jaroslav

1993-12-01

The work reported here shows the positive influence of the biodegradation of the crystal lattice of sulfides on the thiourea leaching of gold from an arsenopyrite-pyrite concentrate. Physical processing of the original as well as of the biologically processed concentrate favorably influenced gold recovery. Mechanical activation appears to be unimportant for gold extraction from the investigated concentrate.

Life cycle assessment of construction and demolition waste management.

PubMed

Butera, Stefania; Christensen, Thomas H; Astrup, Thomas F

2015-10-01

Life cycle assessment (LCA) modelling of construction and demolition waste (C&DW) management was carried out. The functional unit was management of 1 Mg mineral, source separated C&DW, which is either utilised in road construction as a substitute for natural aggregates, or landfilled. The assessed environmental impacts included both non-toxic and toxic impact categories. The scenarios comprised all stages of the end-of-life management of C&DW, until final disposal of all residues. Leaching of inorganic contaminants was included, as was the production of natural aggregates, which was avoided because of the use of C&DW. Typical uncertainties related to contaminant leaching were addressed. For most impact categories, utilisation of C&DW in road construction was preferable to landfilling; however, for most categories, utilisation resulted in net environmental burdens. Transportation represented the most important contribution for most nontoxic impacts, accounting for 60-95 per cent of these impacts. Capital goods contributed with negligible impacts. Leaching played a critical role for the toxic categories, where landfilling had lower impacts than utilisation because of the lower levels of leachate per ton of C&DW reaching the groundwater over a 100-year perspective. Leaching of oxyanions (As, V and Sb) was critical with respect to leaching. Typical experimental uncertainties in leaching data did not have a pivotal influence on the results; however, accounting for Cr immobilisation in soils as part of the impact assessment was critical for modelling the leaching impacts. Compared with the overall life cycle of building and construction materials, leaching emissions were shown to be potentially significant for toxicity impacts, compared with contributions from production of the same materials, showing that end-of-life impacts and leaching should not be disregarded when assessing environmental impacts from construction products and materials. CO2 uptake in the C&DW corresponding to 15 per cent carbonation could out-balance global warming impacts from transportation; however, carbonation would also likely result in increased toxicity impacts due to higher leaching of oxyanions. Copyright © 2015 Elsevier Ltd. All rights reserved.

Determination of nitrogen balance in agroecosystems.

PubMed

Sainju, Upendra M

2017-01-01

Nitrogen balance in agroecosystems provides a quantitative framework of N inputs and outputs and retention in the soil that examines the sustainability of agricultural productivity and soil and environmental quality. Nitrogen inputs include N additions from manures and fertilizers, atmospheric depositions including wet and dry depositions, irrigation water, and biological N fixation. Nitrogen outputs include N removal in crop grain and biomass and N losses through leaching, denitrification, volatilization, surface runoff, erosion, gas emissions, and plant senescence. Nitrogen balance, which is the difference between N inputs and outputs, can be reflected in changes in soil total (organic + inorganic) N during the course of the experiment duration due to N immobilization and mineralization. While increased soil N retention and mineralization can enhance crop yields and decrease N fertilization rate, reduced N losses through N leaching and gas emissions (primarily NH 4 and NO x emissions, out of which N 2 O is a potent greenhouse gas) can improve water and air quality. •This paper discusses measurements and estimations (for non-measurable parameters due to complexity) of all inputs and outputs of N as well as changes in soil N storage during the course of the experiment to calculate N balance.•The method shows N flows, retention in the soil, and losses to the environment from agroecosystems.•The method can be used to measure agroecosystem performance and soil and environmental quality from agricultural practices.

Phytoextraction of heavy metals from contaminated soil by co-cropping with chelator application and assessment of associated leaching risk.

PubMed

Wei, Z B; Guo, X F; Wu, Q T; Long, X X; Penn, C J

2011-08-01

Phytoextraction using hyperaccumulating plants is generally time-consuming and requires the cessation of agriculture. We coupled chelators and a co-cropping system to enhance phytoextraction rates, while allowing for agricultural production. An experiment on I m3 lysimeter beds was conducted with a co-cropping system consisting of the hyperaccumulator Sedum alfredii and low-accumulating corn (Zea Mays, cv. Huidan-4), with addition ofa mixture of chelators (MC), to assess the efficiency of chelator enhanced co-crop phytoextraction and the leaching risk caused by the chelator. The results showed that the addition of MC promoted the growth of S. alfredii in the first crop (spring-summer season) and significantly increased the metal phytoextraction. The DTPA-extractable and total metal concentrations in the topsoil were also reduced more significantly with the addition of MC compared with the control treatments. However, mono-cropped S. alfredii without MC was more suitable for maximizing S. alfredii growth and therefore phytoextraction of Zn and Cd during the autumn-winter seasons. No adverse impact to groundwater due to MC application was observed during the experiments with three crops and three MC applications. But elevated total Cd and Pb concentrations among subsoils compared to the initial subsoil concentrations were found for the co-crop + MC treatment after the third crop.

Androgens and androgenic activity in broiler manure assessed by means of chemical analyses and in vitro bioassays.

PubMed

Valdehita, Ana; Fernández-Cruz, María-Luisa; González-Gullón, María Isabel; Becerra-Neira, Eduardo; Delgado, María Mar; García-González, Mari Cruz; Navas, José María

2017-07-01

The use of manure as an agricultural amendment is increasing the release of steroid hormones into the environment. Most research in this field has focused on estrogenic phenomena, with less attention paid to androgenic substances. The present study assessed androgenic activity in broiler manure using in vitro approaches based on cells stably transfected with androgen receptor. Leaching experiments were also performed to observe whether endocrine disruptors present in manure pass through a soil column and potentially reach groundwater. In parallel, an analytical chemistry method was used to determine the contribution of the most important natural androgens to androgenicity. Samplings were performed at 4 farms in 2 seasons. All but 2 samples showed androgen activity. In leakage experiments, however, no androgenic activity was detectable in leachates or in soils after leaching. According to the analytical results, androgenicity can be attributed mainly (but not completely) to androstenedione, and dihydrotestosterone. Similarly to the bioassays, chemical analysis did not reveal the presence of any androgen in leachates or soils. These results point to a rapid degradation of the substances responsible for androgenic activity in soils under the experimental conditions of the present study. However, the long-term effects associated with the constant and intensive application of manure to agricultural land require further attention. Environ Toxicol Chem 2017;36:1746-1754. © 2016 SETAC. © 2016 SETAC.

Changes in the dissolved organic matter leaching from soil under severe temperature and N-deposition.

PubMed

Nguyen, Hang Vo-Minh; Choi, Jung Hyun

2015-06-01

In this study, we conducted growth chamber experiments using three types of soil (wetland, rice paddy, and forest) under the conditions of a severe increase in the temperature and N-deposition in order to investigate how extreme weather influences the characteristics of the dissolved organic matter (DOM) leaching from different soil types. This leachate controls the quantity and quality of DOM in surface water systems. After 5 months of incubation, the dissolved organic carbon (DOC) concentrations decreased in the range of 21.1 to 88.9 %, while the specific UV absorption (SUVA) values increased substantially in the range of 19.9 to 319.9 % for all of the samples. Higher increases in the SUVA values were observed at higher temperatures, whereas the opposite trend was observed for samples with N-addition. The parallel factor analysis (PARAFAC) results showed that four fluorescence components: terrestrial humic-like (component 1 (C1)), microbial humic-like (component 2 (C2)), protein-like (component 3 (C3)), and anthropogenic humic-like (component 4 (C4)) constituted the fluorescence matrices of soil samples. During the experiment, labile DOM from the soils was consumed and transformed into resistant aromatic carbon structures and less biodegradable components via microbial processes. The principle component analysis (PCA) results indicated that severe temperatures and N-deposition could enhance the contribution of the aromatic carbon compounds and humic-like components in the soil samples.

Importance of lateral flux and its percolation depth on organic carbon export in Arctic tundra soil: Implications from a soil leaching experiment

NASA Astrophysics Data System (ADS)

Zhang, Xiaowen; Hutchings, Jack A.; Bianchi, Thomas S.; Liu, Yina; Arellano, Ana R.; Schuur, Edward A. G.

2017-04-01

Temperature rise in the Arctic is causing deepening of active layers and resulting in the mobilization of deep permafrost dissolved organic matter (DOM). However, the mechanisms of DOM mobilization from Arctic soils, especially upper soil horizons which are drained most frequently through a year, are poorly understood. Here we conducted a short-term leaching experiment on surface and deep organic active layer soils, from the Yukon River basin, to examine the effects of DOM transport on bulk and molecular characteristics. Our data showed a net release of DOM from surface soils equal to an average of 5% of soil carbon. Conversely, deep soils percolated with surface leachates retained up to 27% of bulk DOM while releasing fluorescent components (up to 107%), indicating selective release of aromatic components (e.g., lignin and tannin), while retaining nonchromophoric components, as supported by spectrofluorometric and ultrahigh-resolution mass spectroscopic techniques. Our findings highlight the importance of the lateral flux of DOM on ecosystem carbon balance as well as processing of DOM transport through organic active layer soils en route to rivers and streams. This work also suggests the potential role of leachate export as an important mechanism of C losses from Arctic soils, in comparison with the more traditional pathway from soil to atmosphere in a warming Arctic.

Evaluating the biogas potential of the dry fraction from pretreatment of food waste from households

DOE Office of Scientific and Technical Information (OSTI.GOV)

Murto, Marika, E-mail: marika.murto@biotek.lu.se; Björnsson, Lovisa, E-mail: lovisa.bjornsson@miljo.lth.se; Environmental and Energy Systems Studies, Lund University, P.O. Box 118, SE-221 00 Lund

2013-05-15

Highlights: ► A novel approach for biogas production from a waste fraction that today is incinerated. ► Biogas production is possible in spite of the impurities of the waste. ► Tracer studies are applied in a novel way. ► Structural material is needed to improve the flow pattern of the waste. ► We provide a solution to biological treatment for the complex waste fraction. - Abstract: At the waste handling company NSR, Helsingborg, Sweden, the food waste fraction of source separated municipal solid waste is pretreated to obtain a liquid fraction, which is used for biogas production, and a drymore » fraction, which is at present incinerated. This pretreatment and separation is performed to remove impurities, however also some of the organic material is removed. The possibility of realising the methane potential of the dry fraction through batch-wise dry anaerobic digestion was investigated. The anaerobic digestion technique used was a two-stage process consisting of a static leach bed reactor and a methane reactor. Treatment of the dry fraction alone and in a mixture with structural material was tested to investigate the effect on the porosity of the leach bed. A tracer experiment was carried out to investigate the liquid flow through the leach beds, and this method proved useful in demonstrating a more homogenous flow through the leach bed when structural material was added. Addition of structural material to the dry fraction was needed to achieve a functional digestion process. A methane yield of 98 m{sup 3}/ton was obtained from the dry fraction mixed with structural material after 76 days of digestion. This was in the same range as obtained in the laboratory scale biochemical methane potential test, showing that it was possible to extract the organic content in the dry fraction in this type of dry digestion system for the production of methane.« less

Capacity of model biobeds to retain and degrade mecoprop and isoproturon.

PubMed

Henriksen, Vibeke V; Helweg, Arne; Spliid, Niels Henrik; Felding, Gitte; Stenvang, Lars

2003-10-01

Biobeds are used to increase the adsorption and degradation of pesticide spillage on sites used for mixing and loading and for cleaning of sprayers. The adsorption and the rate of degradation of 14C-labelled isoproturon and mecoprop (MCPP) at concentrations from 0.0005 to 25 000 mgkg(-1) were determined in biobed soil. Further leaching of the two herbicides was determined in a model biobed with a surface area of 2 m2. The biobed material showed enhanced ability to adsorb the two herbicides. Kd was 5.2 litre kg(-1) for isoproturon and 1.6 litre kg(-1) for MCPP in biobed material, which is higher than in natural soil. In different experiments with natural soil, Kd ranges from 0.07 to 0.6 litrekg(-1) for MCPP and from 1.5 to 4.6 litre kg(-1) for isoproturon in soils with varying organic carbon content. Degradation of MCPP was rapid at concentrations from 0.0005 to 500 mg kg(-1), delayed at 5000 mg kg(-1), and very slow at 25 000 mg kg(-1). For isoproturon, the relative degradation was most rapid at the lowest concentration and decreasing with increasing concentrations. After 120 days, between 55% and 8% 14C was evolved as 14CO2 at concentrations between 0.0005 and 25 000 mg kg(-1). The rate of evolution of 14CO2 indicated that degradation rates at low concentrations were of first-order and at higher concentrations of zero-order. Leaching of MCPP and isoproturon was determined in a newly established model biobed during a 2-year period. About 13% of applied MCPP and 1.4% of applied isoproturon leached out during the winter following the first autumn application (worst-case scenario). Leaching was completely prevented when the biobed had a well-developed grass cover and was covered during the winter.

Extended sorption partitioning models for pesticide leaching risk assessments: Can we improve upon the koc concept?

PubMed

Jarvis, Nicholas

2016-01-01

Models used to assess leaching of pesticides to groundwater still rely on the sorption koc value, even though its limitations have been known for several decades, especially for soils of low organic carbon content (i.e. subsoils). This is mainly because the general applicability of any improved model approach that is also simple enough to use for regulatory purposes has not been demonstrated. The objective of this study was to test and compare alternative models of sorption that could be useful in pesticide risk assessment and management. To this end, a database containing the results of batch sorption experiments for pesticides was compiled from published studies in the literature, which placed at least as much emphasis on measurements in subsoil horizons as in topsoil. The database includes 785 data entries from 34 different published studies and for 21 different active substances. Overall, the apparent koc value, koc(app), roughly doubled as the soil organic carbon content decreased by a factor of ten. Nevertheless, in nearly half of the individual datasets, a constant koc value proved to be an adequate model. Further analysis showed that significant increases in koc(app) in subsoil were found primarily for the more weakly adsorbing compounds (koc values

Preparation and adsorption characteristics for heavy metals of active silicon adsorbent from leaching residue of lead-zinc tailings.

PubMed

Lei, Chang; Yan, Bo; Chen, Tao; Xiao, Xian-Ming

2018-05-19

To comprehensively reuse the leaching residue obtained from lead-zinc tailings, an active silicon adsorbent (ASA) was prepared from leaching residue and studied as an adsorbent for copper(II), lead(II), zinc(II), and cadmium(II) in this paper. The ASA was prepared by roasting the leaching residue with either a Na 2 CO 3 /residue ratio of 0.6:1 at 700 °C for 1 h or a CaCO 3 /residue ratio of 0.8:1 at 800 °C for 1 h. Under these conditions, the available SiO 2 content of the ASA was more than 20%. The adsorption behaviors of the metal ions onto the ASA were investigated and the Langmuir, Freundlich, and Dubinin-Radushkevich isotherm models were used to analyze the adsorption isotherm. The result showed that the maximum adsorption capacities of copper(II), lead(II), cadmium(II), and zinc(II) calculated by the Langmuir model were 3.40, 2.83, 0.66, and 0.62 mmol g -1 , respectively. The FT-IR spectra of the ASA and the mean free adsorption energies indicated that ion exchange was the mechanism of copper(II), lead(II), and cadmium(II) adsorption and that chemical reaction was the mechanism of zinc(II) adsorption. These results provide a method for reusing the leaching residue obtained from lead-zinc tailings and show that the ASA is an effective adsorbent for heavy metal pollution remediation.

The influence of pH on the leaching behaviour of inorganic components from municipal solid waste APC residues

DOE Office of Scientific and Technical Information (OSTI.GOV)

Quina, Margarida J.; Bordado, Joao C.M.; Quinta-Ferreira, Rosa M.

2009-09-15

The influence of pH on the leaching behaviour of air pollution control (APC) residues produced in municipal solid waste incineration (MSWI) is addressed in this study. The residue is considered hazardous waste, and in accordance with their chemical properties, the leaching of contaminants into the environment is the main concern. Several leaching tests can be used for research studies or regulatory purposes, where a wide variety of conditions may be tested. Our work deals mainly with the leaching behaviour of toxic heavy metals (Pb, Cd, Zn, Cr, Ni, Cu) and inorganics associated with soluble salts (Na, K, Ca, Cl). Themore » main goal is to obtain an overview of the leachability of APC residues produced in a Portuguese MSWI process. Among the different variables that may have influence on the leaching behaviour, pH of the leachant solution is the most important one, and was evaluated through pH static tests. The acid neutralization capacity (ANC) of the residue was also determined, which is in the range of 6.2-6.8 meq g{sup -1} (for pH = 7) and 10.1-11.6 meq g{sup -1} (for pH = 4). The analysis of the leaching behaviour is particularly important when the leaching is solubility controlled. The amphoteric behaviour of some elements was observed, namely for Pb and Zn, which is characterized through high solubilization at low and high pH and moderate or low solubility at neutral or moderate high pH. The solubility curves for Pb, Cd, Zn, Cr, Ni and Cu as a function of pH were obtained, which are very useful for predicting the leaching behaviour in different scenarios. The solubility of K and Na reveals to be nearly independent of the solution pH and the released amount is mainly availability-controlled. Moreover, the pH static test showed that Cl{sup -} is the most pH-independent species. The APC residue turns out to be a hazardous waste because of the high leaching of lead and chloride. On the other hand, leaching of elements like cadmium, nickel and copper is limited by the high pH of the residue, and as long as the waste keeps its ANC, the risk of mobilization of these elements is low.« less

How does the composition affect the mechanical behaviour of simulated clay-rich fault gouges?

NASA Astrophysics Data System (ADS)

Bakker, Elisenda; Spiers, Christopher J.; Hangx, Suzanne J. T.

2014-05-01

CO2 capture and storage (CCS) in depleted oil and gas reservoirs is seen as one of the most promising large-scale CO2-mitigation strategies. Prediction of the effect of fluid-rock interaction on the mechanical integrity and sealing capacity of a reservoir-seal system, on timescales of the order of 1,000 or 10,000 years, is important to ensure the safety and containment of a reservoir in relation to long-term CO2 storage. However, most chemical reactions in rock/CO2/brine systems are slow, which means that long-term effects of fluids on rock composition, microstructure, mechanical properties and transport properties cannot be easily reproduced under laboratory conditions. One way to overcome this problem is to use simulated fault gouges in experiments, investigating a range of possible mineralogical compositions resulting from CO2-exposure. Previous studies have shown that the mechanical and transport properties of clay-rich fault gouges are significantly influenced by the mineralogy, particularly by the presence and relative amount of secondary phases, such as quartz and/or carbonate. In CCS settings, where dissolution and/or precipitation of carbonates may play an important role, the carbonate:clay ratio is expected to influence fault frictional behaviour. This is supported by the different behaviour of phyllosilicates, which generally show stable slip behaviour (aseismic), compared to carbonates, which have shown to become prone to unstable slip (potentially seismic) with increasing temperature. However, little is known about the mechanical and transport properties of carbonate/clay mixtures. We investigated the effect of the carbonate:clay ratio on fault friction, fault reactivation potential and slip stability, i.e. seismic vs. aseismic behaviour, as well as transmissivity evolution during and after fault reactivation. We used two types of starting material, derived from crushed Opalinus Claystone (Mont Terri, Switzerland): i) untreated samples consisting mainly of phyllosilicates (60%), quartz (~20%) and calcite (~15-25%) and ii) "leached" samples consisting of phyllosilicate (65%) and quartz (35%), where the removal of the calcite represents a worst-case scenario for rock/CO2/brine (dissolution) reactions. We performed triaxial direct shear experiments at relevant in-situ temperatures (60-120°C) under saturated conditions (Pp = 25 MPa), using demineralized water as pore fluid, at an effective normal stress (σn) of 50 MPa and shear velocities of 0.22 to 10.9 μm/s. Preliminary results show that the shear strength of the leached samples decreases by ~10-15% with respect to the natural, untreated clay samples. Typical steady-state friction coefficient values obtained for the natural samples are in the range 0.27-0.33, whereas for the leached samples they vary between 0.24 and 0.27. These values are significantly lower than typical friction coefficient values obtained for pure calcite (i.e. 0.62 to 0.71). Both natural and leached samples show velocity strengthening behaviour. The slip stability of the natural gouge appears to be slightly more temperature dependent, showing somewhat higher values of the stability (rate and state friction) parameter (a-b) for lower temperatures.

Leaching behaviour of and Cs disposition in a UMo powellite glass-ceramic

NASA Astrophysics Data System (ADS)

Vance, E. R.; Davis, J.; Olufson, K.; Gregg, D. J.; Blackford, M. G.; Griffiths, G. R.; Farnan, I.; Sullivan, J.; Sprouster, D.; Campbell, C.; Hughes, J.

2014-05-01

A UMo powellite glass-ceramic designed by French workers to immobilise Mo-rich intermediate-level waste was found to be quite leach resistant in water at 90 °C with the dissolution of Cs, Mo, Na, B and Ca not exceeding 2 g/L in normalised PCT tests. 133Cs solid state nuclear magnetic resonance and scanning electron microscopy (SEM) showed the Cs to inhabit the glass phase. The microstructures were not greatly affected by cooling rates between 1 and 5 °C/min or by introducing 10 times as much Cs and Sr. Protracted leach tests at 90 °C showed surface alteration as evidenced by SEM and particularly transmission electron microscopy; the main alteration phase was a Zn aluminosilicate but several other alteration phases were evident. Voidage in the alteration layers was indicated from enhanced lifetimes in positron annihilation lifetime spectroscopy.

Effect of PMMA polymer on the dynamic viscoelasticity and plasticizer leachability of PEMA-based tissue conditioners.

PubMed

Hong, Guang; Maeda, Takeshi; Li, YingAi; Sadamori, Shinsuke; Hamada, Taizo; Murata, Hiroshi

2010-08-01

The purpose of this study was to determine the effect of PMMA polymer on dynamic viscoelasticity and plasticizer leachability of PEMA-based tissue conditioners. One PEMA polymer and one PMMA polymer were used in powder form with four formulations. The combination of 80 wt% ATBC, 15 wt% BPBG and 5 wt% ethyl alcohol was used as the liquid phase. The dynamic viscoelasticity and plasticizer leaching of each specimen were measured after 0, 1, 3, 7, and 14 days of immersion (37 degrees C distilled water) using DMA and HPLC. A significant difference was found among the materials in the dynamic viscoelasticity and leaching of plasticizer. The materials containing 10 wt% PMMA showed the most stable dynamic viscoelasticity, and showed the lowest leaching of plasticizer. The results suggest that the addition of the PMMA polymer to the powder of a tissue conditioner can improve the durability of the PEMA-based tissue conditioner.

Surface alteration and physical properties of glass from the Cretaceous-Tertiary boundary

USGS Publications Warehouse

Barkatt, A.; Sang, J.C.; Thorpe, A.N.; Senftle, F.E.; Talmy, I.G.; Norr, M.K.; Mazer, J.J.; Izett, G.; Sigurdsson, Haraldur

1994-01-01

The scalloped surface feature on Cretaceous-Tertiary boundary glass is often explained as being due to terrestrial aqueous leaching. Leaching of man-made glass results in a reduction in density of the glass. Also, Fe, because of its relative insolubility, is concentrated by the leaching process. Thus, the Haitian glass specimens which have been heavily altered should have a thin rim of less dense glass in which the Fe is concentrated compared to the core glass. The higher Fe concentration in the rim glass should cause it to have an enhanced Curie constant and a lower density compared to the unaltered glass. The magnetic Curie constant, density, and scanning electron microscopic studies were made on altered specimens of Haitian glass and also on specimens showing a minimum of alteration. The results show that the less altered samples have the highest density and the lowest Curie constant. The data substantiate the terrestrial hypothesis. ?? 1994.

Leaching of Heavy Metals from Water Bottle Components into the Drinking Water of Rodents

PubMed Central

Nunamaker, Elizabeth A; Otto, Kevin J; Artwohl, James E; Fortman, Jeffrey D

2013-01-01

Providing high-quality, uncontaminated drinking water is an essential component of rodent husbandry. Acidification of drinking water is a common technique to control microbial growth but is not a benign treatment. In addition to its potential biologic effects, acidified water might interact with the water-delivery system, leading to the leaching of heavy metals into the drinking water. The goal of the current study was to evaluate the effects of water acidification and autoclaving on water-bottle assemblies. The individual components of the system (stainless-steel sipper tubes, rubber stoppers, neoprene stoppers, and polysulfone water bottles) were acid-digested and analyzed for cadmium, chromium, copper, iron, lead, magnesium, manganese, selenium, and zinc to quantify the metal composition of each material. In addition the amounts of these metals that leached into tap and acidified water with and without autoclaving were quantified after 1 wk of contact time. On a weight basis, sipper tubes contained the largest quantities of all metals except magnesium and zinc, which were greatest in the neoprene stoppers. Except for cadmium and selenium, all metals had leached into the water after 1 wk, especially under the acidified condition. The quantities of copper, lead, and zinc that leached into the drinking water were the most noteworthy, because the resulting concentrations had the potential to confound animal experiments. On the basis of these findings, we suggest that water-quality monitoring programs include heavy metal analysis at the level of water delivery to animals. PMID:23562029

Leaching of heavy metals from water bottle components into the drinking water of rodents.

PubMed

Nunamaker, Elizabeth A; Otto, Kevin J; Artwohl, James E; Fortman, Jeffrey D

2013-01-01

Providing high-quality, uncontaminated drinking water is an essential component of rodent husbandry. Acidification of drinking water is a common technique to control microbial growth but is not a benign treatment. In addition to its potential biologic effects, acidified water might interact with the water-delivery system, leading to the leaching of heavy metals into the drinking water. The goal of the current study was to evaluate the effects of water acidification and autoclaving on water-bottle assemblies. The individual components of the system (stainless-steel sipper tubes, rubber stoppers, neoprene stoppers, and polysulfone water bottles) were acid-digested and analyzed for cadmium, chromium, copper, iron, lead, magnesium, manganese, selenium, and zinc to quantify the metal composition of each material. In addition the amounts of these metals that leached into tap and acidified water with and without autoclaving were quantified after 1 wk of contact time. On a weight basis, sipper tubes contained the largest quantities of all metals except magnesium and zinc, which were greatest in the neoprene stoppers. Except for cadmium and selenium, all metals had leached into the water after 1 wk, especially under the acidified condition. The quantities of copper, lead, and zinc that leached into the drinking water were the most noteworthy, because the resulting concentrations had the potential to confound animal experiments. On the basis of these findings, we suggest that water-quality monitoring programs include heavy metal analysis at the level of water delivery to animals.

Lanthanide-alkali double sulfate precipitation from strong sulfuric acid NiMH battery waste leachate.

PubMed

Porvali, Antti; Wilson, Benjamin P; Lundström, Mari

2018-01-01

In NiMH battery leaching, rare earth element (REE) precipitation from sulfate media is often reported as being a result of increasing pH of the pregnant leach solution (PLS). Here we demonstrate that this precipitation is a phenomenon that depends on both Na + and SO 4 2- concentrations and not solely on pH. A two-stage leaching for industrially crushed NiMH waste is performed: The first stage consists of H 2 SO 4 leaching (2 M H 2 SO 4 , L/S = 10.4, V = 104 ml, T = 30 °C) and the second stage of H 2 O leaching (V = 100 ml, T = 25 °C). Moreover, precipitation experiments are separately performed as a function of added Na 2 SO 4 and H 2 SO 4 . During the precipitation, higher than stoichiometric quantities of Na to REE are utilized and this increase in both precipitation reagent concentrations results in an improved double sulfate precipitation efficiency. The best REE precipitation efficiencies (98-99%) - achieved by increasing concentrations of H 2 SO 4 and Na 2 SO 4 by 1.59 M and 0.35 M, respectively - results in a 21.8 times Na (as Na 2 SO 4 ) and 58.3 times SO 4 change in stoichiometric ratio to REE. Results strongly indicate a straightforward approach for REE recovery from NiMH battery waste without the need to increase the pH of PLS. Copyright © 2017 The Authors. Published by Elsevier Ltd.. All rights reserved.

Investigation of water-soluble organic matter extracted from shales during leaching experiments

NASA Astrophysics Data System (ADS)

Zhu, Yaling; Vieth-Hillebrand, Andrea; Wilke, Franziska D. H.; Horsfield, Brian

2017-04-01

The huge volumes and unknown composition of flowback and produced waters cause major public concerns about the environmental and social compatibility of hydraulic fracturing and the exploitation of gas from unconventional reservoirs. Flowback and produced waters contain not only residues of fracking additives but also chemical species that are dissolved from the shales themselves during fluid-rock interaction. Knowledge of the composition, size and structure of dissolved organic carbon (DOC) as well as the main controls on the release of DOC are a prerequisite for a better understanding of these interactions and its effects on composition of flowback and produced water. Black shales from four different geological settings and covering a maturity range Ro = 0.3-2.6% were extracted with deionized water. The DOC yields were found to decrease rapidly with increasing diagenesis and remain low throughout catagenesis. Four DOC fractions have been qualitatively and quantitatively characterized using size-exclusion chromatography. The concentrations of individual low molecular weight organic acids (LMWOA) decrease with increasing maturity of the samples except for acetate extracted from the overmature Posidonia shale, which was influenced by hydrothermal brines. The oxygen content of the shale organic matter also shows a significant influence on the release of organic acids, which is indicated by the positive trend between oxygen index (OI) and the concentrations of formate and acetate. Based on our experiments, both the properties of the organic matter source and the thermal maturation progress of the shale organic matter significantly influence the amount and quality of extracted organic compounds during the leaching experiments.

Sodic soil properties and sunflower growth as affected by byproducts of flue gas desulfurization.

PubMed

Wang, Jinman; Bai, Zhongke; Yang, Peiling

2012-01-01

The main component of the byproducts of flue gas desulfurization (BFGD) is CaSO(4), which can be used to improve sodic soils. The effects of BFGD on sodic soil properties and sunflower growth were studied in a pot experiment. The experiment consisted of eight treatments, at four BFGD rates (0, 7.5, 15 and 22.5 t ha(-1)) and two leaching levels (750 and 1200 m(3) ha(-1)). The germination rate and yield of the sunflower increased, and the exchangeable sodium percentage (ESP), pH and total dissolved salts (TDS) in the soils decreased after the byproducts were applied. Excessive BFGD also affected sunflower germination and growth, and leaching improved reclamation efficiency. The physical and chemical properties of the reclaimed soils were best when the byproducts were applied at 7.5 t ha(-1) and water was supplied at 1200 m(3)·ha(-1). Under these conditions, the soil pH, ESP, and TDS decreased from 9.2, 63.5 and 0.65% to 7.8, 2.8 and 0.06%, and the germination rate and yield per sunflower reached 90% and 36.4 g, respectively. Salinity should be controlled by leaching when sodic soils are reclaimed with BFGD as sunflower growth is very sensitive to salinity during its seedling stage.

Evaluation of gold and silver leaching from printed circuit board of cellphones.

PubMed

Petter, P M H; Veit, H M; Bernardes, A M

2014-02-01

Electronic waste has been increasing proportionally with the technology. So, nowadays, it is necessary to consider the useful life, recycling, and final disposal of these equipment. Metals, such as Au, Ag, Cu, Sn and Ni can be found in the printed circuit boards (PCB). According to this, the aims of this work is to characterize the PCBs of mobile phones with aqua regia; obtaining "reference" values of leaching, to gold and silver, with cyanide and nitric acid, respectively; and study the process of leaching of these metals in alternative leaching with sodium thiosulfate and ammonium thiosulfate. The metals were characterized by digesting the sample with aqua regia for 1 and 2h at 60°C and 80°C. The leaching of Au with a commercial reagent (cyanide) and the Ag with HNO3were made. The leaching of Au and Ag with alternative reagents: Na2S2O3, and (NH4)2S2O3 in 0.1M concentration with the addition of CuSO4, NH4OH, and H2O2, was also studied. The results show that the digestion with aqua regia was efficient to characterize the metals present in the PCBs of mobile phones. However, the best method to solubilize silver was by digesting the sample with nitric acid. The leaching process using sodium thiosulfate was more efficient when an additional concentration of 0.015 and 0.030 M of the CuSO4 was added. Copyright © 2013 Elsevier Ltd. All rights reserved.

Quantifying long-term responses of crop yield and nitrate leaching in an intensive farmland using agro-eco-environmental model.

PubMed

Sun, Mei; Huo, Zailin; Zheng, Yanxia; Dai, Xiaoqin; Feng, Shaoyuan; Mao, Xiaomin

2018-02-01

Quantitatively ascertaining and analyzing long-term responses of crop yield and nitrate leaching on varying irrigation and fertilization treatments are focal points for guaranteeing crop yield and reducing nitrogen loss. The calibrated agricultural-hydrological RZWQM2 model was used to explore the long-term (2003-2013) transport processes of water and nitrogen and the nitrate leaching amount into groundwater in summer maize and winter wheat rotation field in typical intensive plant area in the North China Plain, Daxing district of Beijing. Simulation results showed that application rates of irrigation and nitrogen fertilizer have couple effects on crop yields and nitrogen leaching of root zone. When both the irrigation and fertilizer for summer maize and winter wheat were 400mm and 400kgNha -1 , respectively, nitrate leaching into groundwater accounted for 47.9% of application amount of nitrogen fertilizer. When application amount of irrigation is 200mm and fertilization is 200kgNha -1 , NUPE (nitrogen uptake efficiency), NUE (nitrogen use efficiency), NPFP (nitrogen partial factor productivity), and W pi (irrigation water productive efficiency) were in general higher than that under other irrigation and fertilization condition (irrigation from 104-400mm, fertilizer 104-400kgNha -1 ). Irrigation bigger than 200mm could shorten the response time of nitrate leaching in deeper soil layer in different irrigation treatment. Copyright © 2017 Elsevier B.V. All rights reserved.

Nanosized zero-valent iron as Fenton-like reagent for ultrasonic-assisted leaching of zinc from blast furnace sludge.

PubMed

Mikhailov, Ivan; Komarov, Sergey; Levina, Vera; Gusev, Alexander; Issi, Jean-Paul; Kuznetsov, Denis

2017-01-05

Ultrasonic-assisted sulphuric acid leaching combined with a Fenton-like process, utilizing nanoscale zero-valent iron (nZVI), was investigated to enhance the leaching of zinc from the blast furnace sludge (BFS). The leaching of iron (Fe) and zinc (Zn) from the sludge was investigated using Milli-Q water/BFS ratio of 10 and varying the concentration of hydrogen peroxide, sulphuric acid, the temperature, the input energy for ultrasound irradiation, and the presence or absence of nZVI as a Fenton reagent. The results showed that with 1g/l addition of nZVI and 0.05M of hydrogen peroxide, the kinetic rate of Zn leaching increased with a maximum dissolution degree of 80.2%, after 5min treatment. In the absence of nZVI, the maximum dissolution degree of Zn was 99.2%, after 15min treatment with 0.1M of hydrogen peroxide. The rate of Zn leaching at several concentrations of hydrogen peroxide is accelerated in the presence of nZVI although a reduction in efficiency was observed. The loss of Fe was no more than 3%. On the basis of these results, the possible route for BFS recycling has been proposed (BFS slurry mixed with sulphuric acid and hydrogen peroxide is recirculated under ultrasonic irradiation then separated). Copyright © 2016 Elsevier B.V. All rights reserved.

EDTA and HCl leaching of calcareous and acidic soils polluted with potentially toxic metals: remediation efficiency and soil impact.

PubMed

Udovic, Metka; Lestan, Domen

2012-07-01

The environmental risk of potentially toxic metals (PTMs) in soil can be diminished by their removal. Among the available remediation techniques, soil leaching with various solutions is one of the most effective but data about the impact on soil chemical and biological properties are still scarce. We studied the effect of two common leaching agents, hydrochloric acid (HCl) and a chelating agent (EDTA) on Pb, Zn, Cd removal and accessibility and on physico-chemical and biological properties in one calcareous, pH neutral soil and one non-calcareous acidic soil. EDTA was a more efficient leachant compared to HCl: up to 133-times lower chelant concentration was needed for the same percentage (35%) of Pb removal. EDTA and HCl concentrations with similar PTM removal efficiency decreased PTM accessibility in both soils but had different impacts on soil properties. As expected, HCl significantly dissolved carbonates from calcareous soil, while EDTA leaching increased the pH of the acidic soil. Enzyme activity assays showed that leaching with HCl had a distinctly negative impact on soil microbial and enzyme activity, while leaching with EDTA had less impact. Our results emphasize the importance of considering the ecological impact of remediation processes on soil in addition to the capacity for PTM removal. Copyright © 2012 Elsevier Ltd. All rights reserved.

Sulfur dioxide leaching of spent zinc-carbon-battery scrap

NASA Astrophysics Data System (ADS)

Avraamides, J.; Senanayake, G.; Clegg, R.

Zinc-carbon batteries, which contain around 20% zinc, 35% manganese oxides and 10% steel, are currently disposed after use as land fill or reprocessed to recover metals or oxides. Crushed material is subjected to magnetic separation followed by hydrometallurgical treatment of the non-magnetic material to recover zinc metal and manganese oxides. The leaching with 2 M sulfuric acid in the presence of hydrogen peroxide recovers 93% Zn and 82% Mn at 25 °C. Alkaline leaching with 6 M NaOH recovers 80% zinc. The present study shows that over 90% zinc and manganese can be leached in 20-30 min at 30 °C using 0.1-1.0 M sulfuric acid in the presence of sulfur dioxide. The iron extraction is sensitive to both acid concentration and sulfur dioxide flow rate. The effect of reagent concentration and particle size on the extraction of zinc, manganese and iron are reported. It is shown that the iron and manganese leaching follow a shrinking core kinetic model due to the formation of insoluble metal salts/oxides on the solid surface. This is supported by (i) the decrease in iron and manganese extraction from synthetic Fe(III)-Mn(IV)-Zn(II) oxide mixtures with increase in acid concentration from 1 M to 2 M, and (ii) the low iron dissolution and re-precipitation of dissolved manganese and zinc during prolonged leaching of battery scrap with low sulfur dioxide.