Compositional dependence of optical band gap and refractive index in lead and bismuth borate glasses

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mallur, Saisudha B.; Czarnecki, Tyler; Adhikari, Ashish

2015-08-15

Highlights: • Refractive indices increase with increasing PbO/Bi{sub 2}O{sub 3} content. • Optical band gap arises due to direct forbidden transition. • Optical band gaps decrease with increasing PbO/Bi{sub 2}O{sub 3} content. • New empirical relation between the optical band gap and the refractive index. - Abstract: We prepared a series of lead and bismuth borate glasses by varying PbO/Bi{sub 2}O{sub 3} content and studied refractive index and optical band gap as a function of glass composition. Refractive indices were measured very accurately using a Brewster’s angle set up while the optical band gaps were determined by analyzing the opticalmore » absorption edge using the Mott–Davis model. Using the Lorentz–Lorentz method and the effective medium theory, we calculated the refractive indices and then compared them with the measured values. Bismuth borate glasses show better agreement between the calculated values of the refractive index and experimental values. We used a differential method based on Mott–Davis model to obtain the type of transition and optical band gap (E{sub opt}) which in turn was compared with the value of E{sub opt} obtained using the extinction coefficient. Our analysis shows that in both lead and bismuth borate glasses, the optical band gap arises due to direct forbidden transition. With increasing PbO/Bi{sub 2}O{sub 3} content, the absorption edge shifts toward longer wavelengths and the optical band gap decreases. This behavior can be explained in terms of changes to the Pb−O/Bi−O chemical bonds with glass composition. We obtained a new empirical relation between the optical band gap and the refractive index which can be used to accurately determine the electronic oxide polarizability in lead and bismuth oxide glasses.« less

Dosimetric properties of dysprosium doped lithium borate glass irradiated by 6 MV photons

NASA Astrophysics Data System (ADS)

Ab Rasid, A.; Wagiran, H.; Hashim, S.; Ibrahim, Z.; Ali, H.

2015-07-01

Undoped and dysprosium doped lithium borate glass system with empirical formula (70-x) B2O3-30 Li2O-(x) Dy2O3 (x=0.1, 0.3, 0.5, 0.7, 1.0 mol%) were prepared using the melt-quenching technique. The dosimetric measurements were performed by irradiating the samples to 6 MV photon beam using linear accelerator (LINAC) over a dose range of 0.5-5.0 Gy. The glass series of dysprosium doped lithium borate glass produced the best thermoluminescence (TL) glow curve with the highest intensity peak from sample with 1.0 mol% Dy2O3 concentration. Minimum detectable dose was detected at 2.24 mGy, good linearity of regression coefficient, high reproducibility and high sensitivity compared to the undoped glass are from 1.0 mol% dysprosium doped lithium borate glass. The results indicated that the series of dysprosium doped lithium glasses have a great potential to be considered as a thermoluminescence dosimetry (TLD).

The preparation and characterization of a lithium borate glass prepared by the gel technique

NASA Technical Reports Server (NTRS)

Weinberg, M. C.; Neilson, G. F.; Smith, G. L.; Dunn, B.; Moore, G. S.; Mackenzie, J. D.

1985-01-01

The preparation of an amorphous lithium borate gel by the metal organic procedure is described. In addition, a preliminary evaluation of the behavior of the gel upon heating is given. In particular the crystallization tendency of the gel is studied with the aid of DTA and X-ray diffraction, and the structural changes in the gel are monitored with the aid of IR spectroscopy. The glass produced from the lithium borate gel is compared to both the gel precursor material and a glass of similar composition prepared by conventional techniques. Specifically, the relevant water contents, crystallization behavior, and structural features are contrasted.

Bismuth oxyfluoride @ CMK-3 nanocomposite as cathode for lithium ion batteries

NASA Astrophysics Data System (ADS)

Ni, Dan; Sun, Wang; Xie, Liqiang; Fan, Qinghua; Wang, Zhenhua; Sun, Kening

2018-01-01

Bismuth oxyfluoride impregnated CMK-3 nanocomposite is synthesized by a facile nanocasting approach. Mesoporous carbon CMK-3 can suppress the aggregation and growth of bismuth oxyfluoride particles and offer rapid electron and Li ion passageways. Bismuth oxyfluoride nanoparticles are embedded in the mesoporous channels with particle size less than 20 nm. The bismuth oxyfluoride@CMK-3 nanocomposite maintains 148 mA h g-1 after 40 cycles with the capacity from both the bismuth oxyfluoride and the functional groups on the mesoporous carbon. The hybrid with confined bismuth oxyfluoride nanoparticles, conductive carbon network, and oxygen functional groups on the carbon matrix exhibits higher capacity and cycling stability than bulk bismuth oxyfluoride particles when used as lithium ion batteries cathode.

Structural investigation and optical properties of xMnO2-25Li2O-5Na2O-15Bi2O3-(55-x)B2O3 glasses

NASA Astrophysics Data System (ADS)

Kulkarni, Shilpa; Jali, V. M.

2018-02-01

This paper deals with the new mixed system of glass compositions Lithium sodium bismuth borate glasses doped with transition metal oxide. The technique used to prepare a sample is by melt quenching. The XRD profile pattern confirmed the amorphous phase of the present glass system. The network structure is based on BO3, BO4 units and BiO6 octahedral units. No boroxyl rings observed in the glass structure. The addition of MnO2 in small amount does not account for major structural changes. Optical band gap lies in the range 1.89 to 0.96 eV. Density, molar volume, oxygen packing density, Tg, direct optical band gap and refractive index show anomalous behavior.

Electrical Characteristics of MnO2 Doped Bismuth Borate Glass Systems

NASA Astrophysics Data System (ADS)

Nissar, Umair; Ahmad, Javed; Rana, Anwar Manzoor; Bukhari, S. H.; Jamil, M. T.; Khan, J. Alam; Shakeel, R.; Nadeem, M. Y.

2018-02-01

Transparent glasses have a large number of applications in the industry of electronics as well as optical devices. xMnO2-(25- x) Bi2O3-75H3BO3 (0 ≤ x ≤ 1.5 mol.%) transparent glasses have been prepared via melt-quench technique and characterized using dc electrical measurements, and by analyzing x-ray diffraction and Fourier transform infrared (FTIR) spectra. These characteristics were examined to understand the role of modifier oxides, i.e., Bi2O3 and MnO2 in the B2O3 glass network. Adding MnO2 into a glass network causes structural changes, which are responsible for any variations in electrical characteristics of bismuth borate glasses. Manganese bismuth borate glasses (MBBG) show Ohmic conduction at low fields; however, glasses with higher manganese content seem to conduct through bulk limited Poole-Frenkel mechanism. FTIR spectroscopy analyses depict the presence of BO3 and BO4 groups along with B-O-B and Bi-O-Bi bonding vibrations. Glasses with higher MnO2 content also show Mn-O bond vibrations. The reduction of BO4 groups and increase of BO3 units lead to the formation of non-bridging oxygens (NBOs) which are responsible for the variations in the electrical properties of these glasses.

Structural and Luminescent property of Holmium doped Borate Glasses

NASA Astrophysics Data System (ADS)

Usharani, V. L.; Eraiah, B.

2018-02-01

Holmium doped Lithium Lead Borate glasses of different compositions were prepared by melt quenching technique. Fourier transform infrared investigations on lithium lead borate glasses have been made to study the local order and vibrations of atoms in the glass network and it contains mainly BO3 and BO4 structural units. Photoluminescence techniques were employed to investigate the luminescent property of these glasses excited at 451nm. Blue emission have been observed from the transition 495 (5F3 → 5I8).

Content and distribution of arsenic, bismuth, lithium and selenium in mineral and synthetic fertilizers and their contribution to soil

DOE Office of Scientific and Technical Information (OSTI.GOV)

Senesi, N.; Polemio, M.; Lorusso, L.

1979-01-01

Concentrations of arsenic, bismuth, lithium and selenium were determined by atomic absorption spectrophotometry in 32 samples of commercial fertilizers from various manufacturers and distributors. Arsenic and lithium were detected in all investigated samples, bismuth in 50% of samples and selenium only in two samples. Arsenic content ranged from 2 to 321 ppM; lithium varied from 5 to 0.1 ppM; bismuth was always lower than 0.5 ppM; selenium was detectable at the levels of 10 and 13 ppM. Fertilizers made from rock phosphates contained trace element amounts generally higher than those derived from rock carbonates, synthetic nitrogen fertilizers and potassium sulphate.more » Additions of trace elements from fertilizers applied at common rates to cultivated soils are tabulated and discussed on the basis of the natural soil reserves and toxicity levels for plants. Whereas applications of bismuth resulted always very low to influence the usual soil content and plant uptakes and selenium was only rarely present in fertilizers, lithium and moreover arsenic additions by fertilizers could influence the trace element status in soil, overcoming occasionally the toxicity levels for more sensitive crops.« less

Comparative study on lithium borates as corrosion inhibitors of aluminum current collector in lithium bis(fluorosulfonyl)imide electrolytes

NASA Astrophysics Data System (ADS)

Park, Kisung; Yu, Sunghun; Lee, Chulhaeng; Lee, Hochun

2015-11-01

Lithium bis(fluorosulfonyl)imide (LiFSI) is a promising salt that can possibly overcome the limitations of lithium hexafluorophosphate (LiPF6) in current Li-ion batteries (LIBs). Aluminum (Al) corrosion issue, however, is a major bottleneck for the wide use of LiFSI. This study investigates lithium borate salts as Al corrosion inhibitors in LiFSI electrolytes. Through a systematic comparison among lithium tetrafluoroborate (LiBF4), lithium bis(oxalato)borate (LiBOB), and lithium difluoro(oxalato)borate (LiDFOB), and LiPF6, the inhibition ability of the additives is revealed to be in the following order: LiDFOB > LiBF4 ≈ LiPF6 > LiBOB. In particular, the inhibition effect of LiDFOB is outstanding; the anodic behavior of Al in 0.8 M LiFSI + 0.2 M LiDFOB ethylene carbonate (EC)-based electrolyte is comparable to that of corrosion-free 1 M LiPF6 solution. The superior inhibition ability of LiDFOB is attributed to the formation of a passive layer composed of Al-F, Al2O3, and B-O species, as evidenced by X-ray photoelectron spectroscopy (XPS) measurements. A LiCoO2/graphite cell with 0.8 M LiFSI + 0.2 M LiDFOB electrolyte exhibits a rate capability comparable to a cell with 1 M LiPF6 solution, whereas a cell with 0.8 M LiFSI solution without LiDFOB suffers from poor power performance resulting from severe Al corrosion.

Bismuth- and lithium-loaded plastic scintillators for gamma and neutron detection

NASA Astrophysics Data System (ADS)

Cherepy, Nerine J.; Sanner, Robert D.; Beck, Patrick R.; Swanberg, Erik L.; Tillotson, Thomas M.; Payne, Stephen A.; Hurlbut, Charles R.

2015-04-01

Transparent plastic scintillators based on polyvinyltoluene (PVT) have been fabricated with high loading of bismuth carboxylates for gamma spectroscopy, and with lithium carboxylates for neutron detection. When activated with a combination of standard fluors, 2,5-diphenyloxazole (PPO) and tetraphenylbutadiene (TPB), gamma light yields with 15 wt% bismuth tripivalate of 5000 Ph/MeV are measured. A PVT plastic formulation including 30 wt% lithium pivalate and 30 wt% PPO offers both pulse shape discrimination, and a neutron capture peak at 400 keVee. In another configuration, a bismuth-loaded PVT plastic is coated with ZnS(6Li) paint, permitting simultaneous gamma and neutron detection via pulse shape discrimination with a figure-of-merit of 3.8, while offering gamma spectroscopy with energy resolution of R(662 keV)=15%.

Effect of the adsorption of lithium and borate species on the zeta potential of particles of cobalt ferrite, nickel ferrite, and magnetite.

PubMed

Barale, M; Lefèvre, G; Carrette, F; Catalette, H; Fédoroff, M; Cote, G

2008-12-01

Zetametric measurements on suspensions of oxide particles (cobalt ferrite, nickel ferrite, and magnetite) representative of corrosion products from primary circuits of pressurized water reactors were performed at 25 and 70 degrees C in the presence of lithium and borate species. No effect of lithium ions was observed. Borate species cause a decrease of the isoelectric point (IEP), attributed to the sorption of borate as a negative complex MOB(OH)3(-). A predictive model based on thermodynamic calculations (2-pK and diffuse layer models) of the surface acidity constants from the data of acid-base titrations combined with an empirical relationship between the surface potential Psi 0 and the zeta potential determined by zetametry was developed. A whole set of parameters valid at 25 degrees C, in a range of ionic strength between 10(-4) and 10(-2) molL(-1) and in a range of pH between 4 and 8, was determined for this model. Increase of temperature to 70 degrees C in the presence of borate results in a decrease of IEP for cobalt ferrite and an increase of the IEP for nickel ferrite.

Optical and physical properties of samarium doped lithium diborate glasses

NASA Astrophysics Data System (ADS)

Hanumantharaju, N.; Sardarpasha, K. R.; Gowda, V. C. Veeranna

2018-05-01

Sm3+ doped lithium di-borate glasses with composition 30Li2O-60B2O3-(10-x) PbO, (where 0 < x < 2 mole. %) were prepared by melt quenching method. The addition of modifier oxide to vitreous B2O3 modifies the glass network by converting three coordinated trigonal boron units (BO3) to weaker anionic four coordinated tetrahedral borons (BO4). The decrease in density and increase in molar volume with samarium ion content indicates the openness of the glass structure. The gradual increase in average separation of boron-boron atoms with VmB clearly indicates deterioration of borate glass network, which in turn leads to decrease in the oxygen packing density. The replacements of Sm2O3 for PbO depolymerise the chain structure and that would increase the concentration of non-bridging oxygens. The marginal increase of optical band gap energy after 1.0 mol.% of Sm2O3 is explained by considering the structural modification in lead-borate. The influence of Sm3+ ion on physical and optical properties in lithium-lead-borate glasses is investigated and the results were discussed in view of the structure of borate glass network.

Electromagnetic Pumps for Liquid Metal-Fed Electric Thrusters

NASA Technical Reports Server (NTRS)

Polzin, Kurt A.; Markusic, Thomas E.

2007-01-01

Prototype designs of two separate pumps for use in electric propulsion systems with liquid lithium and bismuth propellants are presented. Both pumps are required to operate at elevated temperatures, and the lithium pump must additionally withstand the corrosive nature of the propellant. Compatibility of the pump materials and seals with lithium and bismuth were demonstrated through proof-of-concept experiments followed by post-experiment visual inspections. The pressure rise produced by the bismuth pump was found to be linear with input current and ranged from 0-9 kPa for corresponding input current levels of 0-30 A, showing good quantitative agreement with theoretical analysis.

Dietary intake of barium, bismuth, chromium, lithium, and strontium in a Spanish population (Canary Islands, Spain).

PubMed

González-Weller, Dailos; Rubio, Carmen; Gutiérrez, Ángel José; González, Gara Luis; Caballero Mesa, José María; Revert Gironés, Consuelo; Burgos Ojeda, Antonio; Hardisson, Arturo

2013-12-01

The aim of this study was to analyze barium, bismuth, chromium, lithium, and strontium contents in food and beverages consumed by the population of the Canary Islands (Spain) as well as determine dietary intake of these metals in the archipelago as a whole and in its individual islands. To this end, 440 samples were analyzed by ICP-OES and GFAAS. Barium concentrations ranged from 5.210 ± 2.117 mg/kg in nuts to 0.035 ± 0.043 mg/L in water. Viscera exhibited the highest levels of bismuth (38.07 ± 36.80 mg/kg). The cold meat and sausages group stood out for its high chromium concentrations (0.494 ± 0.257 mg/kg). The highest concentration of lithium and strontium came out in nuts (8.761 ± 5.368 mg/kg and 9.759 ± 5.181 mg/kg, respectively). The total intakes of barium, bismuth, chromium, lithium, and strontium were 0.685, 1.274, 0.087, 3.674, and 1.923 mg/day, respectively. Cereals turned out to contribute most to the dietary intake of barium, bismuth, chromium, and lithium in the Canary Islands, while fruit contributes most to the strontium intake. We also performed a metal intake study by age and sex of the population and compared the outcome with data from other regions, both national and international.

Bismuth- and lithium-loaded plastic scintillators for gamma and neutron detection

DOE PAGES

Cherepy, Nerine J.; Sanner, Robert D.; Beck, Patrick R.; ...

2015-01-09

In this paper, transparent plastic scintillators based on polyvinyltoluene (PVT) have been fabricated with high loading of bismuth carboxylates for gamma spectroscopy, and with lithium carboxylates for neutron detection. When activated with a combination of standard fluors, 2,5-diphenyloxazole (PPO) and tetraphenylbutadiene (TPB), gamma light yields with 15 wt% bismuth tripivalate of 5000 Ph/MeV are measured. A PVT plastic formulation including 30 wt% lithium pivalate and 30 wt% PPO offers both pulse shape discrimination, and a neutron capture peak at ~400 keVee. Finally, in another configuration, a bismuth-loaded PVT plastic is coated with ZnS( 6Li) paint, permitting simultaneous gamma and neutronmore » detection via pulse shape discrimination with a figure-of-merit of 3.8, while offering gamma spectroscopy with energy resolution of R(662 keV)=15%.« less

Investigation of the Decomposition Mechanism of Lithium Bis(oxalate)borate (LiBOB) Salt in the Electrolyte of an Aprotic Li-O 2 Battery

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lau, Kah Chun; Lu, Jun; Low, John

2014-03-13

The stability of the lithium bis(oxalate) borate (LiBOB) salt against lithium peroxide (Li2O2) in an aprotic Li-O2 cell is investigated. From theoretical and experimental findings, we find that the chemical decomposition of LiBOB in electrolytes leads to the formation lithium oxalate during discharge of a Li-O2 cell. According to DFT calculations, the formation of lithium oxalate as the reaction product is exothermic, and therefore is thermodynamically feasible. This reaction seems to be independent of solvents used in the Li-O2 cell, and therefore LiBOB is probably not suitable to be used as the salt in Li-O2 cell electrolytes.

Electromagnetic Pumps for Conductive-Propellant Feed Systems

NASA Technical Reports Server (NTRS)

Markusic, Thomas E.; Polzin, Kurt A.; Dehoyos, Amado

2005-01-01

Prototype electromagnetic pumps for use with lithium and bismuth propellants were constructed and tested. Such pumps may be used to pressurize future electric propulsion liquid metal feed systems, with the primary advantages being the compactness and simplicity versus alternative pressurization technologies. Design details for two different pumps are described: the first was designed to withstand (highly corrosive) lithium propellant, and t he second was designed to tolerate the high temperature required to pump liquid bismuth. Both qualitative and quantitative test results are presented. Open-loop tests demonstrated the capability of each device to electromagnetically pump its design propellant (lithium or bismuth). A second set of tests accurately quantified the pump pressure developed as a function of current. These experiments, which utilized a more easily handled material (gallium), demonstrated continuously-adjustable pump pressure levels ranging from 0-100 Torr for corresponding input current levels of 0-75 A. While the analysis and testing in this study specifically targeted lithium and bismuth propellants, the underlying design principles should be useful in implementing liquid metal pumps in any conductive-propellant feed system.

Crystallization of lithium borate glasses

NASA Technical Reports Server (NTRS)

Goktas, A. A.; Neilson, G. F.; Weinberg, M. C.

1992-01-01

The glass-forming ability and crystallization behavior of lithium borate compositions, in the diborate-to-metaborate-range, were studied. In particular, the nature and sequence of formation of crystalline phases and the tendency toward devitrification were investigated as functions of temperature, thermal history and batch composition. It was found that the sequence of crystalline phase formation was sensitive to all of the three latter factors, and it was observed that under certain conditions metastable defect structures of the metaborate can appear.

Investigation of the Decomposition Mechanism of Lithium Bis(oxalate)borate (LiBOB) Salt in the Electrolyte of an Aprotic Li–O 2 Battery

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lau, Kah Chun; Lu, Jun; Low, John

2014-03-13

The stability of the lithium bis(oxalate) borate (LiBOB) salt against lithium peroxide (Li 2O 2) formation in an aprotic Li–O 2 (Li–air) battery is investigated. From theoretical and experimental findings, we find that the chemical decomposition of LiBOB in electrolytes leads to the formation lithium oxalate during the discharge of a Li–O 2 cell. According to density functional theory (DFT) calculations, the formation of lithium oxalate as the reaction product is exothermic and therefore is thermodynamically feasible. This reaction seems to be independent of solvents used in the Li–O 2 cell, and therefore LiBOB is probably not suitable to bemore » used as the salt in Li–O 2 cell electrolytes.« less

Record fifth-harmonic-generation efficiency producing 211 nm, joule-level pulses using cesium lithium borate

DOE PAGES

Begishev, I. A.; Bromage, J.; Yang, S. T.; ...

2018-05-16

The fifth harmonic of a pulsed Nd:YLF laser has been realized in a cascade of nonlinear crystals with a record efficiency of 30%. Cesium lithium borate is used in a Type-I configuration for sum-frequency mixing of 1053 nm and 266 nm, producing 211-nm pulses. Flattopped beam profiles and pulse shapes optimize efficiency. Furthermore, energies of the fifth harmonic up to 335 mJ in 2.4 ns pulses were demonstrated.

Record fifth-harmonic-generation efficiency producing 211  nm, joule-level pulses using cesium lithium borate

DOE PAGES

Begishev, I. A.; Bromage, J.; Yang, S. T.; ...

2018-01-01

The fifth harmonic of a pulsed Nd:YLF laser has been realized in a cascade of nonlinear crystals with a record efficiency of 30%. Cesium lithium borate is used in a Type-I configuration for sum-frequency mixing of 1053 nm and 266 nm, producing 211-nm pulses. Flattopped beam profiles and pulse shapes optimize efficiency. Energies of the fifth harmonic up to 335 mJ in 2.4 ns pulses were demonstrated.

Record fifth-harmonic-generation efficiency producing 211 nm, joule-level pulses using cesium lithium borate

DOE Office of Scientific and Technical Information (OSTI.GOV)

Begishev, I. A.; Bromage, J.; Yang, S. T.

The fifth harmonic of a pulsed Nd:YLF laser has been realized in a cascade of nonlinear crystals with a record efficiency of 30%. Cesium lithium borate is used in a Type-I configuration for sum-frequency mixing of 1053 nm and 266 nm, producing 211-nm pulses. Flattopped beam profiles and pulse shapes optimize efficiency. Furthermore, energies of the fifth harmonic up to 335 mJ in 2.4 ns pulses were demonstrated.

Li3PO4 Matrix Enables a Long Cycle Life and High Energy Efficiency Bismuth-Based Battery.

PubMed

Sun, Chuan-Fu; Hu, Junkai; Wang, Peng; Cheng, Xi-Yuan; Lee, Sang Bok; Wang, YuHuang

2016-09-14

Bismuth is a lithium-ion battery anode material that can operate at an equilibrium potential higher than graphite and provide a capacity twice as high as that of Li4Ti5O12, making it intrinsically free from lithium plating that may cause catastrophic battery failure. However, the potential of bismuth is hampered by its inferior cyclability (limited to tens of cycles). Here, we propose an "ion conductive solid-state matrix" approach to address this issue. By homogeneously confining bismuth nanoparticles in a solid-state γ-Li3PO4 matrix that is electrochemically formed in situ, the resulting composite anode exhibits a reversible capacity of 280 mA hours per gram (mA h/g) at a rate of 100 mA/g and a record cyclability among bismuth-based anodes up to 500 cycles with a capacity decay rate of merely 0.071% per cycle. We further show that full-cell batteries fabricated from this composite anode and commercial LiFePO4 cathode deliver a stable cell voltage of ∼2.5 V and remarkable energy efficiency up to 86.3%, on par with practical batteries (80-90%). This work paves a way for harnessing bismuth-based battery chemistry for the design of high capacity, safer lithium-ion batteries to meet demanding applications such as electric vehicles.

Structural studies of lead lithium borate glasses doped with silver oxide.

PubMed

Coelho, João; Freire, Cristina; Hussain, N Sooraj

2012-02-01

Silver oxide doped lead lithium borate (LLB) glasses have been prepared and characterized. Structural and composition characterization were accessed by XRD, FTIR, Raman, SEM and EDS. Results from FTIR and Raman spectra indicate that Ag(2)O acts as a network modifier even at small quantities by converting three coordinated to four coordinated boron atoms. Other physical properties, such as density, molar volume and optical basicity are also evaluated. Furthermore, they are also affected by the silver oxide composition. Copyright © 2011 Elsevier B.V. All rights reserved.

Structural investigation of Zn doped sodium bismuth borate glasses

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bhatia, V., E-mail: vijetabhatia0712@gmail.com; Kumar, D.; Singh, D.

2016-05-06

A series of Bismuth Borate Oxide Glass samples with composition x(ZnO):(15-x)Na{sub 2}O:15Bi{sub 2}O{sub 3}:70B{sub 2}O{sub 3} (variation in x is from 6 to 12 mole %) have been prepared by conventional melt quenching technique. All the chemicals used were of Analytical Grade. In order to verify the amorphous nature of the prepared samples the X-Ray Diffraction (XRD) was done. The physical and structural properties have been explored by using the techniques such as density, molar volume and FTIR in order to understand the effect of alkali and transition metal ions on the structure of these glasses. The results obtained bymore » these techniques are in good agreement to one another and with literature as well. With the increase in the content of ZnO, the increase in density and some variations in structural coordination (ratio of BO{sub 3} & BO{sub 4} structural units) have been observed.« less

Low loss photonic components in high index bismuth borate glass by femtosecond laser direct writing.

PubMed

Yang, Weijia; Corbari, Costantino; Kazansky, Peter G; Sakaguchi, Koichi; Carvalho, Isabel C S

2008-09-29

Single mode, low loss waveguides were fabricated in high index bismuth borate glass by femtosecond laser direct writing. A specific set of writing parameters leading to waveguides perfectly mode matched to standard single-mode fibers at 1.55 microm with an overall insertion loss of approximately 1 dB and with propagation loss below 0.2 dB/cm was identified. Photonic components such as Y-splitters and directional couplers were also demonstrated. A close agreement between their performances and theoretical predictions based upon the characterization of the waveguide properties is shown. Finally, the nonlinear refractive index of the waveguides has been measured to be 6.6 x 10(-15) cm(2)/W by analyzing self-phase modulation of the propagating femtosecond laser pulse at the wavelength of 1.46 microm. Broadening of the transmitted light source as large as 500 nm was demonstrated through a waveguide with the length of 1.8 cm.

Physical and optical property studies on Bi3+ ion containing vanadium sodium borate glasses

NASA Astrophysics Data System (ADS)

Venkatesh, G.; Meera, B. N.; Eraiah, B.

2018-04-01

xBi2O3-(15-x)V2O5-45B2O3-40Na2O glasses have been prepared using melt quenching technique. Amorphous nature of the glasses is verified using powder XRD. Densities and molar volume have been determined as a function of bismuth content and interestingly both increases as a function of bismuth content. Further oxygen packing density (OPD) is found to decrease with bismuth content. The increase in the molar volume as a function of bismuth content may be due to structural changes in the glass network. The optical properties performed from the optical absorption spectra were recorded in the wavelength range 200-1100 nm using UV-Visible spectrophotometer. The theoretical optical basicity of the oxides have also been estimated. The calculated energy band gap values increases with increase in Bi2O3 content.

Lithium-tellurium bimetallic cell has increased voltage

NASA Technical Reports Server (NTRS)

Cairns, E. J.; Rogers, G. L.; Shimotake, H.

1968-01-01

Lithium-tellurium secondary cell with a fused lithium halide electrolyte, tested in the temperature range 467 degrees to 500 degrees C, showed improvement over the sodium bismuth cell. The voltage of this bimetallic cell was increased by using the more electropositive anode material, lithium, and the more electronegative cathode material, tellurium.

Modulation of solid electrolyte interphase of lithium-ion batteries by LiDFOB and LiBOB electrolyte additives

NASA Astrophysics Data System (ADS)

Huang, Shiqiang; Wang, Shuwei; Hu, Guohong; Cheong, Ling-Zhi; Shen, Cai

2018-05-01

Solid-electrolyte interphase (SEI) layer is an organic-inorganic composite layer that allows Li+ transport across but blocks electron flow across and prevents solvent diffusing to electrode surface. Morphology, thickness, mechanical and chemical properties of SEI are important for safety and cycling performance of lithium-ion batteries. Herein, we employ a combination of in-situ AFM and XPS to investigate the effects of two electrolyte additives namely lithium difluoro(oxalate)borate (LiDFOB) and lithium bis(oxalato)borate (LiBOB) on SEI layer. LiDFOB is found to result in a thin but hard SEI layer containing more inorganic species (LiF and LiCO3); meanwhile LiBOB promotes formation of a thick but soft SEI layer containing more organic species such as ROCO2Li. Findings from present study will help development of electrolyte additives that promote formation of good SEI layer.

Effect of mixed transition metal ions on DC conductivity in lithium bismuth borate glasses

NASA Astrophysics Data System (ADS)

Khasa, S.; Yadav, Arti; Dahiya, M. S.; Seema, Ashima, Agarwal, A.

2015-06-01

The DC conductivities of glasses having composition x(2NiO.V2O5).(30-x)Li2O.20Bi2O3.50B2O3 (with x=0, 2, 5, 7 and 10, i.e. NVLBB glasses) and glass samples having composition 7NiO.23 Li2O.20Bi2O3.50B2O3 and 7V2O5.23Li2O.20Bi2O3.50B2O3 (NLBB and VLBB respectively) are investigated as a function of temperature. Conductivity for glasses containing higher percentage of lithium ions is predominantly ionic and in glasses containing higher percentage of transition metal (TM) ions is predominantly electronic. The observed increase in conductivity with x and peak-like behavior at x=7 in NVLBB glasses due to competitive transport of small polaron contributing to a significant structural change in NVLBB glasses. Variation of molar volume and density was also observed with x. In NVLBB glasses, as x increases density increases except a slight decrease at x=7. Also density increases in NLBB whereas in case of VLBB it decreases in comparison to NVLBB1 glass composition. Mott's small polaron hopping (SPH) model has been applied to analyze the high temperature conductivity data and activation energy.

LiBi{sub 3}S{sub 5}—A lithium bismuth sulfide with strong cation disorder

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nakhal, Suliman; Wiedemann, Dennis, E-mail: dennis.wiedemann@chem.tu-berlin.de; Stanje, Bernhard

Among chalcogenide semiconductors for thermoelectric applications, alkali-metal bismuth compounds occur in many complex compositions favorable for high performance. Although LiBi{sub 3}S{sub 5} had been announced in 1977, the potential 1D lithium-ion conductor has hitherto eluded selective synthesis and structure determination. In this study, we present a solid-state route to phase-pure LiBi{sub 3}S{sub 5} powder starting from LiBiS{sub 2} and Bi{sub 2}S{sub 3}. Neutron diffractograms and lithium NMR spectra reveal its crystal structure to be a cation-disordered variety of the AgBi{sub 3}S{sub 5} type (synthetic pavonite; monoclinic, C2/m). Topological analyses and lithium NMR relaxometry suggest that correlated lithium-ion diffusion with activationmore » energies up to 0.66(2) eV occurs along the channels in b direction including tetrahedral voids. Because of cation disorder, immobile bismuth(III) ions clog these pathways, making LiBi{sub 3}S{sub 5} a moderate to poor ionic conductor. The synthesis route reported is nonetheless promising for new lithium bismuth sulfides with, possibly ordered, structure types of the pavonite homologous series. - Graphical abstract: Phase-pure LiBi{sub 3}S{sub 5} has been synthesized and shown to crystallize in cation-disordered variety of the AgBi{sub 3}S{sub 5} type (synthetic pavonite, C2/m) using neutron diffractometry. Topological analyses and NMR relaxometry suggest that immobile Bi{sup 3+} ions clog migration channels along b, making the material a poor lithium conductor. Display Omitted - Highlights: • Phase-pure LiBi{sub 3}S{sub 5} has been synthesized using a promising solid-state route. • LiBi{sub 3}S{sub 5} crystallizes in a cation-disordered variant of the AgBi{sub 3}S{sub 5} type. • Topological analyses suggest lithium diffusion in channels along b. • NMR relaxometry finds activation energies of diffusion as high as 0.66(2) eV. • Because of disorder, LiBi{sub 3}S{sub 5} is a moderate to poor lithium-ion conductor.« less

Lithium tri borate (LiB3O5) embedded polymer electret for mechanical sensing application

NASA Astrophysics Data System (ADS)

Murugan, S.; Praveen, E.; Prasad, M. V. N.; Jayakumar, K.

2017-05-01

Lithium tri borate (LiB3O5) particles were synthesized by precipitation assisted high temperature solid state reaction. The particles were embedded in chitosan polymer and used as an electret. This electret was characterized for the suitability as a sensing element in vibration accelerometer. It is observed that LiB3O5 embedded electret exhibiting piezoelectric property. The electret is also giving an isolation of > 999 MΩ at 100 Vdc, 250 Vdc, 500 Vdc and 1kVdc confirms compatible for intrinsically safe sensing alternative in vibration accelerometer.

Analysis of secondary cells with lithium anodes and immobilized fused-salt electrolytes

NASA Technical Reports Server (NTRS)

Cairns, E. J.; Rogers, G. L.; Shimotake, H.

1969-01-01

Secondary cells with liquid lithium anodes, liquid bismuth or tellurium cathodes, and fused lithium halide electrolytes immobilized as rigid pastes operate between 380 and 485 degrees. Applications include power sources in space, military vehicle propulsion and special commercial vehicle propulsion.

Structure and luminescence properties of Dy 2O 3 doped bismuth-borate glasses

DOE PAGES

Mugoni, Consuelo; Gatto, C.; Pla-Dalmau, A.; ...

2017-07-05

In this study heavy bismuth-borate glasses were studied as host matrices of Dy 2O 3 rare earth, for potential application as scintillator materials in high energy physics experiments and in general radiation detection systems. Glass matrices were prepared from 20BaO-xBi 2O 3-(80-x)B 2O 3 (x = 20, 30, 40 mol%) ternary systems and synthesized by the melt-quenching method at different temperatures in order to obtain high density and high transparency in the UV/Vis range. Particularly, the glass manifesting the higher transparency and with sufficiently high density was doped with Dy 2O 3 (2.5 and 5 mol%) in order to inducemore » the luminescence characteristics. The effects of Bi 2O 3 and Dy 2O 3 on density, thermal behaviour, transmission as well as luminescence properties under UV excitation, were investigated. The experimental results show that the synthesized glasses can be considered promising candidate materials as dense scintillators, due to the Dy 3 + centres emission.« less

Crystal nucleation in lithium borate glass

NASA Technical Reports Server (NTRS)

Smith, Gary L.; Neilson, George F.; Weinberg, Michael C.

1988-01-01

Crystal nucleation measurements were made on three lithium borate compositions in the vicinity of Li2O-2Br2O3. All nucleation measurements were performed at 500 C. Certain aspects of the nucleation behavior indicated (tentatively) that it proceeded by a homogeneous mechanism. The steady state nucleation rate was observed to have the largest value when the Li2O concentration was slightly in excess of the diborate composition. The change in nucleation rate with composition is controlled by the variation of viscosity as well as the change in free energy with composition. The variation of nucleation rate is explained qualitatively in these terms.

A Stable Fluorinated and Alkylated Lithium Malonatoborate Salt for Lithium Ion Battery Application

DOE PAGES

Wan, Shun; Jiang, Xueguang; Guo, Bingkun; ...

2015-04-27

A new fluorinated and alkylated lithium malonatoborate salt, lithium bis(2-methyl-2-fluoromalonato)borate (LiBMFMB), has been synthesized for lithium ion battery application. A 0.8 M LiBMFMB solution is obtained in a mixture of ethylene carbonate (EC) and ethyl methyl carbonate (EMC) (1:2 by wt.). The new LiBMFMB based electrolyte exhibits good cycling stability and rate capability in LiNi0.5Mn1.5O4 and graphite based half-cells.

Study of the response of a lithium yttrium borate scintillator based neutron rem counter by Monte Carlo radiation transport simulations

NASA Astrophysics Data System (ADS)

Sunil, C.; Tyagi, Mohit; Biju, K.; Shanbhag, A. A.; Bandyopadhyay, T.

2015-12-01

The scarcity and the high cost of 3He has spurred the use of various detectors for neutron monitoring. A new lithium yttrium borate scintillator developed in BARC has been studied for its use in a neutron rem counter. The scintillator is made of natural lithium and boron, and the yield of reaction products that will generate a signal in a real time detector has been studied by FLUKA Monte Carlo radiation transport code. A 2 cm lead introduced to enhance the gamma rejection shows no appreciable change in the shape of the fluence response or in the yield of reaction products. The fluence response when normalized at the average energy of an Am-Be neutron source shows promise of being used as rem counter.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cherepy, Nerine J.; Sanner, Robert D.; Beck, Patrick R.

In this paper, transparent plastic scintillators based on polyvinyltoluene (PVT) have been fabricated with high loading of bismuth carboxylates for gamma spectroscopy, and with lithium carboxylates for neutron detection. When activated with a combination of standard fluors, 2,5-diphenyloxazole (PPO) and tetraphenylbutadiene (TPB), gamma light yields with 15 wt% bismuth tripivalate of 5000 Ph/MeV are measured. A PVT plastic formulation including 30 wt% lithium pivalate and 30 wt% PPO offers both pulse shape discrimination, and a neutron capture peak at ~400 keVee. Finally, in another configuration, a bismuth-loaded PVT plastic is coated with ZnS( 6Li) paint, permitting simultaneous gamma and neutronmore » detection via pulse shape discrimination with a figure-of-merit of 3.8, while offering gamma spectroscopy with energy resolution of R(662 keV)=15%.« less

Thermoluminescent properties of rare earth doped lithium strontium borate phosphors

NASA Astrophysics Data System (ADS)

Jakathamani, S.; Annalakshmi, O.; Jose, M. T.

2018-04-01

Thermoluminescence (TL) of borates is remarkable in the field of radiation dosimetry because they can detect both neutron and gamma radiations. Usually, the TL efficiency of pure borates is low and hence dopants have to be added to increase their TL output. Their sensitivity and thermal stability vary widely and depend strongly on the preparation method. In this study polycrystalline powders of different rare earth doped thermoluminescent phosphors of Lithium Strontium borate (LSB) were synthesized by solid state sintering technique. Among the different rare earth dopants, the phosphor doped with cerium was found to have a simple glow curve structure with a dosimetric peak at around 265°C for a heating rate of 5°C/s. In order to study the effect of dopant on the TL characteristics, LSB phosphor with different concentrations of Ce dopant was synthesized and the TL intensity was found to be maximum for a dopant concentration of 0.7 mol%. All other important dosimetric characteristics like dose response and fading were carried out for the LSB:Ce (0.7 mol%) phosphor. Kinetic parameters like trap depth and frequency factor were determined using Peak shape method from Chen's equation.

Growth and Evaluation of Nonlinear Optical Crystals for Laser Applications: Lithium Borate, Barium Borate and Silver Gallium Selenide.

DTIC Science & Technology

1994-12-08

communication 2. S. A. Kutovi, V. V. Laptev and S. Yu. Matsnev, " Lanthanum scandoborate as a new highly efficient active medium of solid state lasers," Sov. J...34Noncritical detection of tunable C02 laser radiation into green by upconversion in silver thio- gallate ," Applied Physics B53, 19 (1991). 3. N.-H

The structural studies of vanadium substituted lithium-bismuth-boro-tellurite glass

NASA Astrophysics Data System (ADS)

Madhu, A.; Eraiah, B.

2018-05-01

The structural studies of vanadium substituted lithium-bismuth-boro-tellurite glass is successfully prepared and certain analysis like XRD,FTIR,DTA/TGA with density, molar volume are done. The amorphous phase has been identified based on X-ray diffraction analysis. The vanadium oxide plays the role as a glass-modifier and influences on BO3 ↔ BO4 conversion. The observed nonlinear variation in Tg with vanadium oxide increase, it reflects structural changes. The nonlinear variation of density and molar volume can be attributed to vanadium oxide incorporation have increased the number of Non-bridging oxygen (NBO'S).

High performance Aurivillius phase sodium-potassium bismuth titanate lead-free piezoelectric ceramics with lithium and cerium modification

NASA Astrophysics Data System (ADS)

Wang, Chun-Ming; Wang, Jin-Feng

2006-11-01

The piezoelectric properties of the lithium and cerium modified A-site vacancies sodium-potassium bismuth titanate (NKBT) lead-free piezoceramics are investigated. The piezoelectric activity of NKBT ceramics is significantly improved by the modification of lithium and cerium. The Curie temperature TC, piezoelectric coefficient d33, and mechanical quality factor Qm for the NKBT ceramics modified with 0.10mol% (LiCe) are found to be 660°C, 25pC/N, and 3135, respectively. The Curie temperature gradually decreases from 675to650°C with the increase of (LiCe) modification. The dielectric spectroscopy shows that all the samples possess stable piezoelectric properties, demonstrating that the (LiCe) modified NKBT-based ceramics are the promising candidates for high temperature applications.

Separation of Californium from other Actinides

DOEpatents

Mailen, J C; Ferris, L M

1973-09-25

A method is provided for separating californium from a fused fluoride composition containing californium and at least one element selected from the group consisting of plutonium, americium, curium, uranium, thorium, and protactinium which comprises contacting said fluoride composition with a liquid bismuth phase containing sufficient lithium or thorium to effect transfer of said actinides to the bismuth phase and then contacting the liquid bismuth phase with molten LiCl to effect selective transfer of californium to the chloride phase.

Effect of Bi2O3 on spectroscopic and structural properties of Er3+ doped cadmium bismuth borate glasses.

PubMed

Sanghi, S; Pal, I; Agarwal, A; Aggarwal, M P

2011-12-01

Glasses with composition 20CdO·xBi(2)O(3)·(79.5-x)B(2)O(3) (15≤x≤35, x in mol%) containing 0.5 mol% of Er(3+) ions were prepared by melt-quench technique (1150°C in air). The amorphous nature of the glasses was confirmed by X-ray diffraction. The spectroscopic properties of the glasses were investigated using optical absorption spectra and fluorescence spectra. The phenomenological Judd-Ofelt intensity parameters Ω(λ) (λ=2, 4, 6) were determined from the spectral intensities of absorption bands in order to calculate the radiative transition probability (A(R)), radiative life time (τ(R)), branching ratios (β(R)) for various excited luminescent states. Using the near infrared emission spectra, full width at half maxima (FWHM), stimulated emission cross-section (σ(e)) and figure of merit (FOM) were evaluated and compared with other hosts. Especially, the numerical values of these parameters indicate that the emission transition (4)I(13/2)→(4)I(15/2) at 1.506 μm in Er(3+)-doped cadmium bismuth borate glasses may be useful in optical communication. Copyright © 2011 Elsevier B.V. All rights reserved.

METHOD OF SEPARATING FISSION PRODUCTS FROM FUSED BISMUTH-CONTAINING URANIUM

DOEpatents

Wiswall, R.H.

1958-06-24

A process is described for removing metal selectively from liquid metal compositions. The method effects separation of flssion product metals selectively from dilute solution in fused bismuth, which contains uraniunn in solution without removal of more than 1% of the uranium. The process comprises contacting the fused bismuth with a fused salt composition consisting of sodium, potassium and lithium chlorides, adding to fused bismuth and molten salt a quantity of bismuth chloride which is stoichiometrically required to convert the flssion product metals to be removed to their chlorides which are more stable in the fused salt than in the molten metal and are, therefore, preferentially taken up in the fused salt phase.

Investigation of a novel ternary electrolyte based on dimethyl sulfite and lithium difluoromono(oxalato)borate for lithium ion batteries

NASA Astrophysics Data System (ADS)

Chen, Renjie; Zhu, Lu; Wu, Feng; Li, Li; Zhang, Rong; Chen, Shi

2014-01-01

Lithium difluoromono(oxalato)borate (LiODFB) has been used as a novel lithium salt for battery in recent studies. In this study, a series of novel electrolytes has been prepared by adding 30 vol% dimethyl sulfite (DMS) or dimethyl carbonate (DMC) as co-solvent into an ethylene carbonate (EC)/ethyl methyl carbonate (EMC) + LiX mixture, in which the LiX could be LiClO4, LiODFB, LiBOB, LiTFSI, or LiCF3SO3. These ternary electrolytes have been investigated for use in lithium ion batteries. FT-IR spectroscopy analysis shows that characteristic functional groups (-CO3, -SO3) undergo red-shift or blue-shift with the addition of different lithium salts. The LiODFB-EC/EMC/DMS electrolyte exhibits high ionic conductivity, which is mainly because of the low melting point of DMS, and LiODFB possessing high solubility. The Li/MCMB cells containing this novel electrolyte exhibit high capacities, good cycling performance, and excellent rate performance. These performances are probably because both LiODFB and DMS can assist in the formation of SEI films by reductive decomposition. Additionally, the discharge capacity of Li/LiCoO2 half cell containing LiODFB-EC/EMC/DMS electrolyte is 130.9 mAh g-1 after 50 cycles, and it is very comparable with the standard-commercial electrolyte. The results show that this study produces a promising electrolyte candidate for lithium ion batteries.

Effect of silver nanoparticles on the fluorescence of Pb2+ and compositional dependence of Sm3+ fluorescence in borate glasses

NASA Astrophysics Data System (ADS)

Olumoroti, Akinloluwa T.

Borate glasses have been widely studied due to their good optical and mechanical properties. Lead and bismuth (PbO/Bi2O 3:B2O3) borate glasses belong to a family of heavy metal oxide (HMO) glasses which are well known to be chemically durable, stable against atmospheric moisture, have low melting temperatures and good corrosion resistance. The first part of this work deals with lead borate glasses with silver nanoparticles (NPs) introduced into the glass matrix. Transmission electron microscopy characterization is done to verify the nucleation of NPs. Fluorescence and optical absorption experiments are then carried out after different heat treatment duration to investigate the influence of silver NPs on the optical properties of lead (Pb2+) by comparing with a glass sample without silver NPs. Optical absorption experiments show that a well-defined surface plasmon resonance (SPR) peak due to Ag NPs can be observed only for samples that were annealed for 36 hrs. Pb2+ fluorescence spectra reveal that the presence of silver NPs creates new emission centers for Pb2+ ions by altering their chemical environment. The second part of the work involves the use of samarium (a rare earth ion) as a dopant in lead and bismuth borate glasses. The concentration of samarium (Sm3+) is fixed and the base glass composition is varied. The goal is to investigate the compositional dependence of optical properties of samarium in the base glass (PbO/Bi2O3:B 2O3). Optical absorption spectra have been collected and the oscillator strength of each transition - including the hypersensitive - is obtained. The Optical absorption edge is found to shift toward lower energies with increasing PbO/Bi2O3 concentration. Both the oscillator strength and the peak position of the hypersensitive transition show significant variation with glass composition. Strong interaction between Sm3+ ions and Pb2+/Bi3+ ions can also be seen from the variations in the fluorescence emission properties of Sm3+ as a function of base glass composition. Studying the variation of these optical properties will help to create the optimum rare-earth ion-host configuration for possible technological applications. This is the thrust of our future investigations of these glass systems. Keywords: Borate glasses, nanoparticles, fluorescence, transmission electron microscopy, optical absorption, surface plasmon resonance, rare-earth (RE) ions, oscillator strength, hypersensitive transition (HST).

Effect of combinations of additives on the performance of lithium ion batteries

NASA Astrophysics Data System (ADS)

Santee, Stuart; Xiao, Ang; Yang, Li; Gnanaraj, Joe; Lucht, Brett L.

Commercial lithium-ion batteries have excellent performance at room temperature for a few years. However, the calendar life and thermal stability (>50 °C) need to be improved for many applications, including electric vehicles. We have conducted an investigation of the effect of thermal stabilizing additives, including dimethyl acetamide, vinylene carbonate, and lithium bis(oxalato) borate, on the performance of lithium ion batteries stored at 70 °C for one month. The reactions of the lithium hexafluorophosphate/carbonate electrolyte, with and without electrolyte additives, with the surface of the electrodes after initial formation cycling have been analyzed via a combination of IR-ATR and XPS.

Hydrothermal Crystal Growth of Lithium Tetraborate and Lithium Gamma-Metaborate

DTIC Science & Technology

2014-03-27

could be atomic nuclei, the center of mass of some complex—those details are immaterial. Both the rectangle and lozenge form potential cross-sections...HR y d L Figure 10. The red lines are the various contours of solution of 9, using a = 10 Bohr radii and the mass of coefficients on the LHS forced to...absorptivity is significantly below that of the transition metals or the actinides [9]. The lithium borate crystals are therefore a strong candidate for

Transition and post-transition metal ions in borate glasses: Borate ligand speciation, cluster formation, and their effect on glass transition and mechanical properties.

PubMed

Möncke, D; Kamitsos, E I; Palles, D; Limbach, R; Winterstein-Beckmann, A; Honma, T; Yao, Z; Rouxel, T; Wondraczek, L

2016-09-28

A series of transition and post-transition metal ion (Mn, Cu, Zn, Pb, Bi) binary borate glasses was studied with special consideration of the cations impact on the borate structure, the cations cross-linking capacity, and more generally, structure-property correlations. Infrared (IR) and Raman spectroscopies were used for the structural characterization. These complementary techniques are sensitive to the short-range order as in the differentiation of tetrahedral and trigonal borate units or regarding the number of non-bridging oxygen ions per unit. Moreover, vibrational spectroscopy is also sensitive to the intermediate-range order and to the presence of superstructural units, such as rings and chains, or the combination of rings. In order to clarify band assignments for the various borate entities, examples are given from pure vitreous B 2 O 3 to meta-, pyro-, ortho-, and even overmodified borate glass compositions. For binary metaborate glasses, the impact of the modifier cation on the borate speciation is shown. High field strength cations such as Zn 2+ enhance the disproportionation of metaborate to polyborate and pyroborate units. Pb 2+ and Bi 3+ induce cluster formation, resulting in PbO n - and BiO n -pseudophases. Both lead and bismuth borate glasses show also a tendency to stabilize very large superstructural units in the form of diborate polyanions. Far-IR spectra reflect on the bonding states of modifier cations in glasses. The frequency of the measured cation-site vibration band was used to obtain the average force constant for the metal-oxygen bonding, F M-O . A linear correlation between glass transition temperature (T g ) and F M-O was shown for the metaborate glass series. The mechanical properties of the glasses also correlate with the force constant F M-O , though for cations of similar force constant the fraction of tetrahedral borate units (N 4 ) strongly affects the thermal and mechanical properties. For paramagnetic Cu- and Mn-borate glasses, N 4 was determined from the IR spectra after deducing the relative absorption coefficient of boron tetrahedral versus boron trigonal units, α = α 4 /α 3 , using NMR literature data of the diamagnetic glasses.

Optical studies of Sm³⁺ ions doped zinc alumino bismuth borate glasses.

PubMed

Swapna, K; Mahamuda, Sk; Srinivasa Rao, A; Shakya, S; Sasikala, T; Haranath, D; Vijaya Prakash, G

2014-05-05

Zinc Alumino Bismuth Borate (ZnAlBiB) glasses doped with different concentrations of samarium (Sm(3+)) ions were prepared by using melt quenching technique and characterized for their lasing potentialities in visible region by using the techniques such as optical absorption, emission and emission decay measurements. Radiative properties for various fluorescent levels of Sm(3+) ions were estimated from absorption spectral information using Judd-Ofelt (JO) analysis. The emission spectra and con-focal photoluminescence images obtained by 410 nm laser excitation demonstrates very distinct and intense orange-red emission for all the doped glasses. The suitable concentration of Sm(3+) ions in these glasses to act as an efficient lasing material has been discussed by measuring the emission cross-section and branching ratios for the emission transitions. The quantum efficiencies were also been estimated from emission decay measurements recorded for the (4)G5/2 level of Sm(3+) ions. From the measured emission cross-sections, branching ratios, strong photoluminescence features and CIE chromaticity coordinates, it was found that 1 mol% of Sm(3+) ions doped ZnAlBiB glasses are most suitable for the development of visible orange-red lasers. Copyright © 2014 Elsevier B.V. All rights reserved.

Bismuth- and lithium-loaded plastic scintillators for gamma and neutron detection (Conference Presentation)

NASA Astrophysics Data System (ADS)

Martinez, H. Paul; Cherepy, Nerine J.; Sanner, Robert D.; Beck, Patrick R.; Swanberg, Eric L.; Payne, Stephen A.

2016-09-01

Plastic scintillators are widely deployed for ionizing radiation detection, as they can be fabricated in large sizes, for high detection efficiency. However commercial plastics are limited in use for gamma spectroscopy, since their photopeak is too weak, due to low Z, and they are also limited in use for neutron detection, since proton recoils are indistinguishable from other ionizing radiation absorption events in standard plastics. We are working on scale up and production of transparent plastic scintillators based on polystyrene (PS) with high loading of bismuth metallorganics for gamma spectroscopy, and with lithium metallorganics for neutron detection. When activated with standard organic fluors, PS scintillators containing 8 wt% bismuth provide energy resolution of 11% at 662 keV. A PS plastic formulation including 1.3 wt% lithium-6 provides a neutron capture peak at 525 keVee, with 11% resolution for the capture peak and 90% efficiency for thermal neutron capture in 2mm thickness. Acknowledgements This work was performed under the auspices of the U.S. DOE by Lawrence Livermore National Laboratory under Contract DE-AC52-07NA27344, and has been supported by the US DOE National Nuclear Security Administration, Defense Nuclear Nonproliferation Research and Development under Contract No. DE-AC03-76SF00098

Physical and optical absorption studies of Fe{sup 3+} - ions doped lithium borate glasses containing certain alkaline earths

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bhogi, Ashok; Kumar, R. Vijaya; Kistaiah, P., E-mail: pkistaiah@yahoo.com

Iron ion doped lithium borate glasses with the composition 15RO-25Li{sub 2}O-59B{sub 2}O{sub 3}-1Fe{sub 2}O{sub 3} (where R= Ca, Sr and Ba) have been prepared by the conventional melt quenching technique and characterized to investigate the physical and optical properties using XRD, density, molar volume and UV-Visible spectroscopy. The optical absorption spectra exhibit a band at around 460 nm which is assigned to {sup 6}A{sub 1g}(S) → 4E{sub g} (G) of Fe{sup 3+} ions with distorted octahedral symmetry. From ultraviolet absorption edges, the optical band gap and Urbach energies have been evaluated. The effect of alkaline earths on these properties ismore » discussed.« less

Evaluating electrolyte additives for lithium-ion cells: A new Figure of Merit approach

NASA Astrophysics Data System (ADS)

Tornheim, Adam; Peebles, Cameron; Gilbert, James A.; Sahore, Ritu; Garcia, Juan C.; Bareño, Javier; Iddir, Hakim; Liao, Chen; Abraham, Daniel P.

2017-10-01

Electrolyte additives are known to improve the performance of lithium-ion cells. In this work we examine the performance of Li1.03Ni0.5Mn0.3Co0.3O2-graphite (NMC532/Gr) cells containing combinations of lithium bis(oxalate)borate (LiBOB), vinylene carbonate (VC), trivinylcyclotriboroxane (tVCBO), prop-1-ene-1,3-sultone (PES), phenyl boronic acid ethylene glycol ester (PBE), tris(trimethylsilyl) phosphite (TMSPi), triethyl phosphite (TEPi), and lithium difluoro(oxalate)borate (LiDFOB) added to our baseline (1.2 M LiPF6 in EC:EMC, 3:7 w/w) electrolyte. In order to rank performance of the various electrolytes, we developed two separate figures of merit (FOM), which are based on the energy retention and power retention of the cells. Using these two metrics in conjunction, we show that only one of the fifteen electrolyte formulations tested significantly outperforms the baseline electrolyte: this electrolyte contains the 0.25 wt% tVCBO + 1 wt% TMSPi additive mix. Little correlation was observed between the FOMs for energy retention and power retention, which indicates that the mechanisms that govern these performance parameters are likely independent of each other. Our FOM approach has general applicability and can be used to develop electrolyte and electrode formulations that prolong the life of lithium-ion batteries.

Evaluating electrolyte additives for lithium-ion cells: A new Figure of Merit approach

DOE PAGES

Tornheim, Adam; Peebles, Cameron; Gilbert, James A.; ...

2017-09-01

Electrolyte additives are known to improve the performance of lithium-ion cells. In this work we examine the performance of Li 1.03Ni 0.5Mn 0.3Co 0.3O 2-graphite (NMC532/Gr) cells containing combinations of lithium bis(oxalate)borate (LiBOB), vinylene carbonate (VC), trivinylcyclotriboroxane (tVCBO), prop-1-ene-1,3-sultone (PES), phenyl boronic acid ethylene glycol ester (PBE), tris(trimethylsilyl) phosphite (TMSPi), triethylphosphite (TEPi), and lithium difluoro(oxalate)borate (LiDFOB) added to our baseline (1.2M LiPF 6 in EC:EMC, 3:7 w/w) electrolyte. In order to rank performance of the various electrolytes, we developed two separate figures of merit (FOM), which are based on the energy retention and power retention of the cells. Using thesemore » two metrics in conjunction, we show that only one of the fifteen electrolyte formulations tested significantly outperforms the baseline electrolyte: this electrolyte contains the 0.25 wt% tVCBO + 1 wt% TMSPi additive mix. Little correlation was observed between the FOMs for energy retention and power retention, which indicates that the mechanisms that govern these performance parameters are likely independent of each other. In conclusion, our FOM approach has general applicability and can be used to develop electrolyte and electrode formulations that prolong the life of lithium-ion batteries.« less

Evaluating electrolyte additives for lithium-ion cells: A new Figure of Merit approach

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tornheim, Adam; Peebles, Cameron; Gilbert, James A.

Electrolyte additives are known to improve the performance of lithium-ion cells. In this work we examine the performance of Li 1.03Ni 0.5Mn 0.3Co 0.3O 2-graphite (NMC532/Gr) cells containing combinations of lithium bis(oxalate)borate (LiBOB), vinylene carbonate (VC), trivinylcyclotriboroxane (tVCBO), prop-1-ene-1,3-sultone (PES), phenyl boronic acid ethylene glycol ester (PBE), tris(trimethylsilyl) phosphite (TMSPi), triethylphosphite (TEPi), and lithium difluoro(oxalate)borate (LiDFOB) added to our baseline (1.2M LiPF 6 in EC:EMC, 3:7 w/w) electrolyte. In order to rank performance of the various electrolytes, we developed two separate figures of merit (FOM), which are based on the energy retention and power retention of the cells. Using thesemore » two metrics in conjunction, we show that only one of the fifteen electrolyte formulations tested significantly outperforms the baseline electrolyte: this electrolyte contains the 0.25 wt% tVCBO + 1 wt% TMSPi additive mix. Little correlation was observed between the FOMs for energy retention and power retention, which indicates that the mechanisms that govern these performance parameters are likely independent of each other. In conclusion, our FOM approach has general applicability and can be used to develop electrolyte and electrode formulations that prolong the life of lithium-ion batteries.« less

Tetraarylborate polymer networks as single-ion conducting solid electrolytes

DOE PAGES

Van Humbeck, Jeffrey F.; Aubrey, Michael L.; Alsbaiee, Alaaeddin; ...

2015-06-23

A new family of solid polymer electrolytes based upon anionic tetrakis(phenyl)borate tetrahedral nodes and linear bis-alkyne linkers is reported. Sonogashira polymerizations using tetrakis(4-iodophenyl)borate, tetrakis(4-iodo-2,3,5,6-tetrafluorophenyl)borate and tetrakis(4-bromo-2,3,5,6-tetrafluorophenyl)borate delivered highly cross-linked polymer networks with both 1,4-diethynylbeznene and a tri(ethylene glycol) substituted derivative. Promising initial conductivity metrics have been observed, including high room temperature conductivities (up to 2.7 × 10 -4 S cm -1), moderate activation energies (0.25–0.28 eV), and high lithium ion transport numbers (up to t Li+ = 0.93). Initial investigations into the effects of important materials parameters such as bulk morphology, porosity, fluorination, and other chemical modification, provide starting designmore » parameters for further development of this new class of solid electrolytes.« less

Active Mechanism of the Interphase Film-Forming Process for an Electrolyte Based on a Sulfolane Solvent and a Chelato-Borate Complexe.

PubMed

Li, Chunlei; Wang, Peng; Li, Shiyou; Zhao, Dongni; Zhao, Qiuping; Liu, Haining; Cui, Xiao-Ling

2018-06-14

Electrolytes based on sulfolane (SL) solvents and lithium bis(oxalato)borate (LiBOB) chelato-borate complexes have been reported many times for use in advanced lithium-ion batteries due to their many advantages. This study aims to clarify the active mechanism of the interphase film-forming process to optimize the properties of these batteries by experimental analysis and theoretical calculations. The results indicate that the self-repairing film-forming process during the first cycle is divided into three stages: the initial film formation with an electric field force of ~1.80 V, the further growth of the preformation solid electrolyte interface (SEI) film at ~1.73 V, and the final formation of a complete SEI film at a potential below 0.7 V. Additionally, we can deduce that the decomposition of LiBOB and SL occurs throughout nearly the entire process of the formation of the SEI film. The decomposition product of BOB- anions tends to form films with an irregular structure, while the decomposition product of SL is in favor of the formation of a uniform SEI film.

Optical constants, single-oscillator modal and refractive index dispersion analysis of lithium zinc bismuth borate glasses doped with Eu{sup 3+} ions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Boda, Ramesh; Srinivas, G.; Komaraiah, D.

2016-05-06

The glasses of composition xLi{sub 2}O-15ZnO- 20Bi{sub 2}O{sub 3}- (64 - x) B{sub 2}O{sub 3}- 1EuO (ZLB) (where x=0, 5, 10, 15, 20 mole %) prepared by melt-quenching technique. The amorphous nature of the prepared glasses was confirmed by XRD spectra. The UV-Vis optical absorption spectrum was recorded in the wave length range of 200-1000 nm. It is observed that the optical band gap is inversely changing with Urbach energy. The optical constants such as G (a constant proportional to the second-order deformation potential) and E{sub f} (a constant that depends on local coordination and is called as free energy ofmore » the glass system). The most significant result of the present work is the refractive index dispersion curves of the ZLB glasses obey the single-oscillator model and oscillator parameters (E{sub o}, E{sub d}) changed with the Li{sub 2}O content. the absorption edge, band gap and Urbach energy is changing nonlinearly with increasing content of Li{sub 2}O, which can be used to calculate the optical, physical, and other constants.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kumada, Nobuhiro, E-mail: kumada@yamanashi.ac.jp; Nakamura, Ayumi; Miura, Akira

A new lithium copper bismuth oxide, LiCuBiO{sub 4} was prepared by hydrothermal reaction using NaBiO{sub 3}0.1*4H{sub 2}O. The crystal structural model of this compound was refined by using synchrotron X-ray powder diffraction data. This bismuthate has the LiCuSbO{sub 4} related structure with the orthorhombic cell (Space group: Pnma) of a=10.9096(9), b=5.8113(5) and c=5.0073(4) Å, and the final R-factors were R{sub wp}=4.84 and R{sub p}=3.58%. This compound is the first example of a lithium copper bismuthate containing Bi{sup 5+}. An antiferromagnetic ordering of Cu{sup 2+} moment was observed at 6 K. - Graphical abstract: In the crystal structure of LiCuBiO{sub 4}more » all metal atoms are coordinated octahedrally by six O atoms and LiO{sub 6} and CuO{sub 6} octahedra form the one-dimensional chains by edge-sharing along the b-axis. The LiO{sub 6} and CuO{sub 6} chains form the layer by face-sharing in the bc plane. The Bi atoms are placed in that interlayer and BiO{sub 6} octahedra are edge-sharing with LiO{sub 6} and CuO{sub 6} octahedra. - Highlights: • A new lithium copper bismuth oxide, LiCuBiO{sub 4} is prepared by hydrothermal reaction. • The crystal structure of LiCuBiO{sub 4} is closely related with that of LiCuSbO{sub 4}. • This new compound exhibits an antiferromagnetic ordering of Cu{sup 2+} moment at 6 K.« less

Optical absorption of Er3+ doped lithium lead borate glasses

NASA Astrophysics Data System (ADS)

Usharani, V. L.; Eraiah, B.

2018-05-01

A new glass system Lithium lead borate doped with erbium trioxide were perpared using conventional melt quenching method. The amorphous nature of the glass samples were confirmed by XRD spectrum. The density of these glass were measured using Archmides principle, the values lie in the range from 4.27 to 4.76 g/cm-3. The corresponding molar volumes are calculated and the values are in the range of 23.81 to 26.17 cm-3. Absorption spectra were recorded in the wavelength range of 200nm to 1100nm, for the prepared glass samples. The optical direct and indirect energy band gaps were measured, the values are in the range of 2.875 to 3.254 eV and 2.25 to 2.81 eV respectively. Photoluminescence technique was employed to study the luminescent property of the prepared glasses excited at 380nm, emission spectra were recorded and analyzed.

Effect of electrolyte composition on initial cycling and impedance characteristics of lithium-ion cells

NASA Astrophysics Data System (ADS)

Abraham, D. P.; Furczon, M. M.; Kang, S.-H.; Dees, D. W.; Jansen, A. N.

Hybrid-electric vehicles require lithium-battery electrolytes that form stable, low impedance passivation layers to protect the electrodes, while allowing rapid lithium-ion transport under high current charge/discharge pulses. In this article, we describe data acquired on cells containing LiNi 0.8Co 0.15Al 0.05O 2-based positive electrodes, graphite-based negative electrodes, and electrolytes with lithium hexafluorophosphate (LiPF 6), lithium tetrafluoroborate (LiBF 4), lithium bis(oxalato)borate (LiBOB) and lithium difluoro(oxalato) borate (LiF 2OB) salts. The impedance data were collected in cells containing a Li-Sn reference electrode to determine effect of electrolyte composition and testing temperature on individual electrode impedance. The full cell impedance data showed the following trend: LiBOB > LiBF 4 > LiF 2OB > LiPF 6. The negative electrode impedance showed a trend similar to that of the full cell; this electrode was the main contributor to impedance in the LiBOB and LiBF 4 cells. The positive electrode impedance values for the LiBF 4, LiF 2OB, and LiPF 6 cells were comparable; the values were somewhat higher for the LiBOB cell. Cycling and impedance data were also obtained for cells containing additions of LiBF 4, LiBOB, LiF 2OB, and vinylene carbonate (VC) to the EC:EMC (3:7 by wt.) + 1.2 M LiPF 6 electrolyte. Our data indicate that the composition and morphology of the graphite SEI formed during the first lithiation cycle is an important determinant of the negative electrode impedance, and hence full cell impedance.

Ho3+-doped strontium-aluminium-bismuth-borate glasses for green light emission.

PubMed

Rajesh, D; Dhamodhara Naidu, M; Ratnakaram, Y C; Balakrishna, A

2014-11-01

Strontium-aluminium-bismuth-borate glasses (SAlBiB) doped with different concentrations of Ho(3+) were prepared using conventional melt quenching technique and their structural and optical properties investigated. X-ray diffraction and scanning electron microscopy analysis were used to study the structural properties. Optical properties were studied by measuring the optical absorption and visible luminescence spectra. The Judd-Ofelt (J-O) theory was applied to evaluate J-O intensity parameters, Ω(λ) (λ = 2, 4 and 6). Using J-O intensity parameters, radiative properties such as spontaneous transition probabilities (A(R)), branching ratios (β(R)) and radiative lifetimes (τ(R)) were determined. From the emission spectra, a strong green emission nearly at 549 nm corresponding to the transition, (5)S2 ((5)F4)→(5)I(8) was observed. Emission peak positions (λ(P)), effective bandwidths (Δλ(eff)) and stimulated emission cross-sections (σ(p)) were calculated for the observed emission transitions, (5)F3 →(5)I(8), (5)S2((5)F4)→(5)I(8) and (5)F5 →(5)I(8) of Ho(3+) in all the glass matrices. Chromaticity color coordinates were calculated using the emission spectra. The experimental results suggest that SAlBiB glass matrix with 1.5 mol% of Ho(3+) has better emission properties. Copyright © 2014 John Wiley & Sons, Ltd.

The effect of MgO on the optical properties of lithium sodium borate doped with Cu+ ions

NASA Astrophysics Data System (ADS)

Alajerami, Yasser Saleh Mustafa; Hashim, Suhairul; Hassan, Wan Muhamad Saridan Wan; Ramli, Ahmad Termizi; Saleh, Muneer Aziz

2013-04-01

The current work presented the photoluminescence (PL) properties of a new glass system, which are reported for the first time. Based on the attractive properties of borate glass, a mixture of boric acid (70-x mol %) modified with lithium (20 mol %) and sodium carbonate (10 mol %) was prepared. The current study illustrated the effect of dopant and co-dopant techniques on the lithium sodium borate (LNB). Firstly, 0.1 mol % of copper ions doped with LNB was excited at 610 nm. The emission spectrum showed two prominent peaks in the violet region (403 and 440 nm). Then, we remarked the effect of adding different concentration of MgO on the optical properties of LNB. The results showed the great effect of magnesium oxide on the PL intensities (enhanced more than two times). Moreover, an obvious shifting has been defined toward the blue region (440 → 475 nm). The up-conversion optical properties were observed in all emission spectra. This enhancement is contributed to the energy transfer from MgO ions to monovalent Cu+ ion. It is well known that magnesium oxide alone generates weak emission intensity, but during this increment the MgO act as an activator (co-doped) for Cu+ ions. Finally, energy band gap, density, ion concentration, molar volume, Polaron radius and inter-nuclear distance all were measured for the current samples. The current samples were subjected to XRD for amorphous confirmation and IR for glass characterization before and after dopants addition. Finally, some of significant physical and optical parameters were also calculated.

Variation of photoluminescence features in Pr{sup 3+} doped lithium-fluoro-borate glass by changing different modifier oxides (MgO, CaO, CdO and PbO)-Judd-Ofelt theory application

DOE Office of Scientific and Technical Information (OSTI.GOV)

Balakrishna, A.; Rajesh, D.; Babu, S.

2015-06-24

Pr{sup 3+} (1.0 mol%) doped different modifier oxide based six lithium-fluoro-borate glasses with chemical composition of 49Li{sub 2}B{sub 4}O{sub 7}-20BaF{sub 2}-10NaF-20MO (where M= Mg, Ca, Cd and Pb), 49Li{sub 2}B{sub 4}O{sub 7}-20BaF{sub 2}-10NaF-10MgO-10CaO and 49Li{sub 2}B{sub 4}O{sub 7}-20BaF{sub 2}-10NaF-10CdO-10PbO were prepared by conventional melt quenching technique. Judd-Ofelt theory has been applied for evaluating the Judd-Ofelt intensity parameters for Pr{sup 3+} ion in these glass compositions and are in turn to used to predict radiative properties such as radiative transition probabilities (A{sub T}), branching ratios (β) and stimulated emission cross-section (σ{sub P}). Stimulated emission cross-section (σ{sub p}) of prominent emission transitions,more » {sup 3}P{sub 0}→{sup 3}H{sub 4} and {sup 1}D{sub 2}→{sup 3}H{sub 4} of Pr{sup 3+} ion in all lithium-fluoro-borate glasses were calculated. Among all the emission transitions, {sup 3}P{sub 0}→{sup 3}H{sub 4} posseses higher branching ratio and stimulated emission cross-section in Mg-Ca glass, which leads to the best laser excitation at 487 nm wavelength.« less

Optical and vibrational spectroscopy of Ba0.85Ca0.15Zr0.1Ti0.9O3 modified lithium borate glass ceramics

NASA Astrophysics Data System (ADS)

Viswanath, Pamarti; Prashanth, Sadhu Sai Pavan; Molli, Muralikrishna; Wicram, Jaschin Prem; Sai Muthukumar, V.

2018-04-01

Glass ceramics are excellent replacement for single crystalline materials which are expensive and difficult to fabricate. In this context, we have attempted to fabricate glass nanocomposites comprising of Lithium Borate glass matrix embedded with lead free ferroelectric Ba0.85Ca0.15Zr0.1Ti0.9O3 (BCZT). Both of these functional materials are known to exhibit excellent ferroelectric behavior and are currently explored for various device applications. We have prepared these novel glass nanocomposite using melt-quenching techniquein various chemical composition involving different molar ratio. x(Ba0.85Ca0.15Zr0.1Ti0.9O3)-(1-x)(Li2O.2B2O3) where (x=0.1,0.2,0.3,0.4). The as-quenched samples exhibited amorphous nature as revealed by X-ray Diffraction studies. With the increase in BCZT content we have observed significant alteration in optical bandgap and Urbach energy. The tailoring of optical properties by tuning the structure was probed by Raman vibrational spectroscopy which confirmed the dominant role played by BCZT as a network modifier in these borate glasses. Concomitantly, these glass nanocomposites were found to be excellent UV absorbers.

Lithium-ion conducting electrolyte salts for lithium batteries.

PubMed

Aravindan, Vanchiappan; Gnanaraj, Joe; Madhavi, Srinivasan; Liu, Hua-Kun

2011-12-16

This paper presents an overview of the various types of lithium salts used to conduct Li(+) ions in electrolyte solutions for lithium rechargeable batteries. More emphasis is paid towards lithium salts and their ionic conductivity in conventional solutions, solid-electrolyte interface (SEI) formation towards carbonaceous anodes and the effect of anions on the aluminium current collector. The physicochemical and functional parameters relevant to electrochemical properties, that is, electrochemical stabilities, are also presented. The new types of lithium salts, such as the bis(oxalato)borate (LiBOB), oxalyldifluoroborate (LiODFB) and fluoroalkylphosphate (LiFAP), are described in detail with their appropriate synthesis procedures, possible decomposition mechanism for SEI formation and prospect of using them in future generation lithium-ion batteries. Finally, the state-of-the-art of the system is given and some interesting strategies for the future developments are illustrated. Copyright © 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

In vitro and in vivo dissolution behavior of a dysprosium lithium borate glass designed for the radiation synovectomy treatment of rheumatoid arthritis.

PubMed

Conzone, Samuel D; Brown, Roger F; Day, Delbert E; Ehrhardt, Gary J

2002-05-01

Dysprosium lithium borate (DyLB) glass microspheres were investigated for use in the radiation synovectomy treatment of rheumatoid arthritis. In vitro testing focused on weight loss and cation dissolution from glass microspheres immersed in simulated synovial fluid (SSF) at 37 degrees C for up to 64 days. In vivo testing was performed by injecting glass microspheres into the stifle joints of Sprague-Dawley rats and monitoring the biodegradability of the microspheres and the tissue response within the joints. The DyLB microspheres reacted nonuniformly in SSF with the majority of lithium and boron being dissolved, whereas nearly all of the dysprosium (>99.7%) remained in the reacted microspheres. Because the DyLB glasses released negligible amounts of dysprosium while reacting with SSF, they are considered safe for radiation synovectomy from the standpoint of unwanted radiation release from the joint capsule. Furthermore, the DyLB microspheres fragmented, degraded, and reacted with body fluids while in the joints of rats without histologic evidence of joint damage. Copyright 2002 Wiley Periodicals, Inc. J Biomed Mater Res 60: 260--268, 2002; DOI 10.1002/jbm.10047

Photorefraction in the ultraviolet: Materials and effects

NASA Astrophysics Data System (ADS)

Laeri, F.; Jungen, R.; Angelow, G.; Vietze, U.; Engel, T.; Würtz, M.; Hilgenberg, D.

1995-10-01

Doped as well as nominally pure crystals of Lithium Niobate (LiNbO3), ι-Arginine Phosphate (LAP), Lithium Iodate (LiIO3), Potassium Dihydrogen Phosphate (KDP), Lithium Formate (LFM), Beta-Barium Borate (BBO), and lithium tetra borate were grown and investigated for photorefractive effects at ultraviolet wavelengths down to 333 nm. In nominally undoped LiNbO3 crystals strong beam coupling effects were observed. In contrast to the visible we revealed a diffusion-dominated charge transport mechanism based on holes, and a low photovoltaic field in the order of 550 V/cm. With such a crystal we investigated the modulation transfer function of a lensless image projection system based on a phase conjugation scheme. A spatial frequency response beyond 2800 line pairs per millimeter was observed. Photorefractive beam coupling was also obtained in LiIO3. Light-induced scattering was detected in iron-doped LiIO3 whereas as-grown LAP material did not exhibit any observable photorefractive effects. However, 100 kV X-ray irradiation seems to induce material defects which can lead to weak light-induced scattering at 351 nm. In all other above-mentioned materials, doped as well as undoped, light-induced scattering could not be observed. On the other hand, this is appreciated in all the applications where the crystals are used as nonlinear material for optical frequency conversion.

Calibration of the borated ion chamber at NIST reactor thermal column.

PubMed

Wang, Z; Hertel, N E; Lennox, A

2007-01-01

In boron neutron capture therapy and boron neutron capture enhanced fast neutron therapy, the absorbed dose of tissue due to the boron neutron capture reaction is difficult to measure directly. This dose can be computed from the measured thermal neutron fluence rate and the (10)B concentration at the site of interest. A borated tissue-equivalent (TE) ion chamber can be used to directly measure the boron dose in a phantom under irradiation by a neutron beam. Fermilab has two Exradin 0.5 cm(3) Spokas thimble TE ion chambers, one loaded with boron, available for such measurements. At the Fermilab Neutron Therapy Facility, these ion chambers are generally used with air as the filling gas. Since alpha particles and lithium ions from the (10)B(n,alpha)(7)Li reactions have very short ranges in air, the Bragg-Gray principle may not be satisfied for the borated TE ion chamber. A calibration method is described in this paper for the determination of boron capture dose using paired ion chambers. The two TE ion chambers were calibrated in the thermal column of the National Institute of Standards and Technology (NIST) research reactor. The borated TE ion chamber is loaded with 1,000 ppm of natural boron (184 ppm of (10)B). The NIST thermal column has a cadmium ratio of greater than 400 as determined by gold activation. The thermal neutron fluence rate during the calibration was determined using a NIST fission chamber to an accuracy of 5.1%. The chambers were calibrated at two different thermal neutron fluence rates: 5.11 x 10(6) and 4.46 x 10(7)n cm(-2) s(-1). The non-borated ion chamber reading was used to subtract collected charge not due to boron neutron capture reactions. An optically thick lithium slab was used to attenuate the thermal neutrons from the neutron beam port so the responses of the chambers could be corrected for fast neutrons and gamma rays in the beam. The calibration factor of the borated ion chamber was determined to be 1.83 x 10(9) +/- 5.5% (+/- 1sigma) n cm(-2) per nC at standard temperature and pressure condition.

A novel electrolyte salt additive for lithium-ion batteries with voltages greater than 4.7 V

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Yunchao; Wan, Shun; Veith, Gabriel M.

2016-11-07

Here, lithium bis(2-methyl-2-fluoromalonato)borate (LiBMFMB), as an additive in conventional electrolyte for LiNi 0.5Mn 1.5O 4, exhibits improved coulombic efficiencies and cycling stability. Cyclic voltammograms indicate the cells with additive form good SEIs during the first cycle whereas no additive cell needs more cycles to form a functional SEI. XPS reveals LiBMFMB could reduce the decomposition of LiPF 6 salt and solvents, resulting in thinner SEI.

Improving the Performance at Elevated Temperature of High Voltage Graphite/LiNi 0.5Mn 1.5O 4 Cells with Added Lithium Catechol Dimethyl Borate

DOE PAGES

Dong, Yingnan; Demeaux, Julien; Zhang, Yuzi; ...

2016-12-13

Performance of LiNi 0.5Mn 1.5O 4/graphite cells cycled to 4.8 V at 55°C with the 1.2 M LiPF 6 in EC/EMC (3/7, STD electrolyte) with and without added lithium catechol dimethyl borate (LiCDMB) has been investigated. The incorporation of 0.5 wt% LiCDMB to the STD electrolyte results in an improved capacity retention and coulombic efficiency upon cycling at 55°C. Ex-situ analysis of the electrode surfaces via a combination of SEM, TEM, and XPS reveals that oxidation of LiCDMB at high potential results in the deposition of a passivation layer on the electrode surface, preventing transition metal ion dissolution from themore » cathode and subsequent deposition on the anode. NMR investigations of the bulk electrolyte stored at 85°C reveals that added LiCDMB prevents the thermal decomposition of LiPF 6.« less

Surface layer formation of LiCoO2 thin film electrodes in non-aqueous electrolyte containing lithium bis(oxalate)borate

NASA Astrophysics Data System (ADS)

Matsui, Masaki; Dokko, Kaoru; Akita, Yasuhiro; Munakata, Hirokazu; Kanamura, Kiyoshi

2012-07-01

Surface layer formation processes on a LiCoO2 thin film electrode in a non-aqueous electrolyte containing lithium bis(oxalate)borate (LiBOB) were investigated using in situ FTIR spectroscopy and X-ray photoelectron spectroscopy (XPS). The in situ FTIR spectra of the electrolyte solution containing LiBOB showed that the adsorption of BOB anions on the electrode surface occurred during the charge process of the LiCoO2 thin film electrode above 4.0 V. XPS analysis for the LiCoO2 thin film electrode charged in an electrolyte containing LiBOB suggested that the adsorbed BOB anions on the electrode surface prevent the continuous decomposition of hexafluorophosphate (PF6) anions resulting in the formation of a very thin surface layer containing organic species, while the LiCoO2 charged in a LiPF6 solution had a relatively thick surface layer containing organic species and inorganic species.

Improving the Performance at Elevated Temperature of High Voltage Graphite/LiNi 0.5Mn 1.5O 4 Cells with Added Lithium Catechol Dimethyl Borate

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dong, Yingnan; Demeaux, Julien; Zhang, Yuzi

Performance of LiNi 0.5Mn 1.5O 4/graphite cells cycled to 4.8 V at 55°C with the 1.2 M LiPF 6 in EC/EMC (3/7, STD electrolyte) with and without added lithium catechol dimethyl borate (LiCDMB) has been investigated. The incorporation of 0.5 wt% LiCDMB to the STD electrolyte results in an improved capacity retention and coulombic efficiency upon cycling at 55°C. Ex-situ analysis of the electrode surfaces via a combination of SEM, TEM, and XPS reveals that oxidation of LiCDMB at high potential results in the deposition of a passivation layer on the electrode surface, preventing transition metal ion dissolution from themore » cathode and subsequent deposition on the anode. NMR investigations of the bulk electrolyte stored at 85°C reveals that added LiCDMB prevents the thermal decomposition of LiPF 6.« less

Insight into self-discharge of layered lithium-rich oxide cathode in carbonate-based electrolytes with and without additive

NASA Astrophysics Data System (ADS)

Li, Jianhui; Xing, Lidan; Zhang, Liping; Yu, Le; Fan, Weizhen; Xu, Mengqing; Li, Weishan

2016-08-01

Self-discharge behavior of layered lithium-rich oxide as cathode of lithium ion battery in a carbonated-based electrolyte is understood, and a simple boron-containing compound, trimethyl borate (TMB), is used as an electrolyte additive to suppress this self-discharge. It is found that layered lithium-rich oxide charged under 4.8 V in additive-free electrolyte suffers severe self-discharge and TMB is an effective electrolyte additive for self-discharge suppression. Physical characterizations from XRD, SEM, TEM, XPS and ICP-MS demonstrate that the crystal structure of the layered lithium-rich oxide collapses due to the chemical interaction between the charged oxide and electrolyte. When TMB is applied, the structural integrity of the oxide is maintained due to the protective cathode film generated from the preferential oxidation of TMB.

Thermodynamics of Pb17Li-bismuth interactions

NASA Astrophysics Data System (ADS)

Hubberstey, Peter; Sample, Tony

1994-09-01

Thermodynamic calculations of the PbBiLi ternary system have been completed to rationalise the formation of solid Li 3Bi on reaction of liquid Pb17Li with bismuth. At 723 K, the bismuth activity in equilibrium with liquid Pi17Li and solid Li 3Bi is calculated to be 9.50 × 10 -4; this can be correlated to a solubility of 2.09 × 10 -1 mol% Bi(2520 wppm). The corresponding bismuth activity in equilibrium with liquid Pb17Li and solid LiBi is 5.04 × 10 -2 (an extrapolated value as LiBi decomposes peritectically at 688 K). The minimum lithium content of PbLi alloys required to react with unit activity bismuth to form Li 3Bi at 723 K is calculated to be ˜ 1.8 mol% Li. The dominance of Li 3Bi in the PbBiLi system is attributed to its extreme stability as evidenced by both its high melting point (1418 K) and free energy of formation [ ΔGf0(Li 3Bi, c 723 K) = 212.8 kJ mol -1].

Lithium Gadolinium Borate in Plastic Scintillator as an Antineutrino Detection Material

DTIC Science & Technology

2010-06-01

advancement of fundamental particle physics, development of the standard model of particle physics and our understanding many cosmological processes...MeVee). Where the light produced by by a 1MeV electron is 1 MeVee by definition , but a heavy charged particle would have a kinetic energy of several

Glass microspheres for medical applications

NASA Astrophysics Data System (ADS)

Conzone, Samuel David

Radioactive dysprosium lithium borate glass microspheres have been developed as biodegradable radiation delivery vehicles for the radiation synovectomy treatment of rheumatoid arthritis. Once injected into a diseased joint, the microspheres deliver a potent dose of radiation to the diseased tissue, while a non-uniform chemical reaction converts the glass into an amorphous, porous, hydrated dysprosium phosphate reaction product. The non-radioactive, lithium-borate component is dissolved from the glass (up to 94% weight loss), while the radioactive 165Dy reacts with phosphate anions in the body fluids, and becomes "chemically" trapped in a solid, dysprosium phosphate reaction product that has the same size as the un-reacted glass microsphere. Ethylene diamine tetraacetate (EDTA) chelation therapy can be used to dissolve the dysprosium phosphate reaction product after the radiation delivery has subsided. The dysprosium phosphate reaction product, which formed in vivo in the joint of a Sprague-Dawley rat, was dissolved by EDTA chelation therapy in <1 week, without causing any detectable joint damage. The combination of dysprosium lithium borate glass microspheres and EDTA chelation therapy provides an unique "tool" for the medical community, which can deliver a large dose (>100 Gy) of localized beta radiation to a treatment site within the body, followed by complete biodegradability. The non-uniform reaction process is a desirable characteristic for a biodegradable radiation delivery vehicle, but it is also a novel material synthesis technique that can convert a glass to a highly porous materials with widely varying chemical composition by simple, low-temperature, glass/solution reaction. The reaction product formed by nonuniform reaction occupies the same volume as the un-reacted glass, and after drying for 1 h at 300°C, has a specific surface area of ≈200 m2/g, a pore size of ≈30 nm, and a nominal crushing strength of ≈10 MPa. Finally, rhenium glass microspheres, composed of micron-sized, metallic rhenium particles dispersed within a magnesium alumino borate glass matrix were produced by sintering ReO2 powder and glass frit at 1050°C. A 50 mg injection of radioactive rhenium glass microspheres containing 3.7 GBq of 186Re and 8.5 GBq of 188Re could be used to deliver a 100 Gy dose to a cancerous tumor, while limiting the total body dose caused by rhenium dissolution to approximately 1 mGy.

Preparation and Elastic Moduli of Germanate Glass Containing Lead and Bismuth

PubMed Central

Sidek, Hj A. A.; Bahari, Hamid R.; Halimah, Mohamed K.; Yunus, Wan M. M.

2012-01-01

This paper reports the rapid melt quenching technique preparation for the new family of bismuth-lead germanate glass (BPG) systems in the form of (GeO2)60–(PbO)40−x–(½Bi2O3)x where x = 0 to 40 mol%. Their densities with respect of Bi2O3 concentration were determined using Archimedes’ method with acetone as a floatation medium. The current experimental data are compared with those of bismuth lead borate (B2O3)20–(PbO)80−x–(Bi2O3)x. The elastic properties of BPG were studied using the ultrasonic pulse-echo technique where both longitudinal and transverse sound wave velocities have been measured in each glass samples at a frequency of 15 MHz and at room temperature. Experimental data shows that all the physical parameters of BPG including density and molar volume, both longitudinal and transverse velocities increase linearly with increasing of Bi2O3 content in the germanate glass network. Their elastic moduli such as longitudinal, shear and Young’s also increase linearly with addition of Bi2O3 but the bulk modulus did not. The Poisson’s ratio and fractal dimensionality are also found to vary linearly with the Bi2O3 concentration. PMID:22606000

Preparation and elastic moduli of germanate glass containing lead and bismuth.

PubMed

Sidek, Hj A A; Bahari, Hamid R; Halimah, Mohamed K; Yunus, Wan M M

2012-01-01

This paper reports the rapid melt quenching technique preparation for the new family of bismuth-lead germanate glass (BPG) systems in the form of (GeO(2))(60)-(PbO)(40-) (x)-(½Bi(2)O(3))(x) where x = 0 to 40 mol%. Their densities with respect of Bi(2)O(3) concentration were determined using Archimedes' method with acetone as a floatation medium. The current experimental data are compared with those of bismuth lead borate (B(2)O(3))(20)-(PbO)(80-) (x)-(Bi(2)O(3))(x). The elastic properties of BPG were studied using the ultrasonic pulse-echo technique where both longitudinal and transverse sound wave velocities have been measured in each glass samples at a frequency of 15 MHz and at room temperature. Experimental data shows that all the physical parameters of BPG including density and molar volume, both longitudinal and transverse velocities increase linearly with increasing of Bi(2)O(3) content in the germanate glass network. Their elastic moduli such as longitudinal, shear and Young's also increase linearly with addition of Bi(2)O(3) but the bulk modulus did not. The Poisson's ratio and fractal dimensionality are also found to vary linearly with the Bi(2)O(3) concentration.

EPR and impedance spectroscopic investigations on lithium bismuth borate glasses containing nickel and vanadium ions

NASA Astrophysics Data System (ADS)

Yadav, Arti; Khasa, Satish; Hooda, Ashima; Dahiya, Manjeet S.; Agarwal, Ashish; Chand, Prem

2016-03-01

Glasses having composition 7NiO • 23Li2O • 20Bi2O3 • 50B2O3, 7V2O5 • 23Li2O • 20Bi2O3 • 50B2O3 and x(2NiO • V2O5) • (30 - x)Li2O • 50B2O3 • 20Bi2O3 (with x = 0, 2, 5, 7 & 10 mol%) prepared through melt-quench route are explored by analyzing density, impedance spectroscopy and electron paramagnetic resonance (EPR). It is found that both density and molar volume increase with an increase in substitution of 2NiO • V2O5 in the base glass matrix. Different dielectric parameters viz. dielectric loss (ε), electrical modulus (M), loss tangent (tanδ) etc. are evaluated and their variations with frequency and temperature are analyzed which reveals that these glasses exhibit a non-Debye relaxation behavior. A phenomenal description of the capacitive behavior is obtained by considering the circuitry as a parallel combination of bulk resistance (Rb) and constant phase element (CPE). The conduction mechanism is found to follow Quantum Mechanical Tunneling (QMT) model. Spin Hamiltonian Parameters (SHPs) and covalency rates are calculated from the EPR spectra of vanadyl ion. The observed EPR spectra confirmed that V4 + ion exists as vanadyl ion in the octahedral coordination with tetragonal compression.

Physical, structural and luminescence investigation of Eu3+-doped lithium-gadolinium bismuth-borate glasses for LEDs

NASA Astrophysics Data System (ADS)

Zaman, F.; Rooh, G.; Srisittipokakun, N.; Wongdeeying, C.; Kim, H. J.; Kaewkhao, J.

2018-06-01

The aim of the current report is to fabricate Eu3+-doped glasses with the chemical composition of 50Li2O-15Gd2O3-5Bi2O3-(30-x)B2O3-xEu2O3 (where x = 0.5, 1.0, 1.5, 2.0 and 2.5 mol%), with the help of conventional melt quenching technique. The fabricated glasses have been studied with help of physical, structural and luminescence properties for application of LEDs. The structural properties were investigated by XRD and FTIR spectra. Physical properties have been measured. Direct and indirect optical energy band gap (Eg) have been calculated and found to be increasing with Eu2O3 concentration. Luminescence spectra have been observed from photo and radioluminescence spectra and found in good agreement with each other, however the concentration quenching was not determined for the samples. The high-covalence and asymmetric nature was confirmed from Photoluminescence emission and RL emission transition as well as from the higher values of luminescence intensity ratio. The JO parameters have been found for the better performance of lasing materials. The lifetime's data have been found to be decreasing from 1.64 to 1.50 ms, which is the confirmation of energy transfer in Eu3+ ions through cross relaxations. From the calculated properties it has been suggested that the present glass samples might be good for red-light emitting devices.

Fluorescence properties of Eu3+ ions doped borate and fluoroborate glasses containing lithium, zinc and lead.

PubMed

Venkatramu, V; Babu, P; Jayasankar, C K

2006-02-01

The influence of glass composition on the fluorescence properties of Eu3+ ions doped borate and fluoroborate glasses modified with Li+, Zn2+ and Pb2+ cations have been investigated. The magnitude of splittings of 7F1 levels are analyzed using crystal-field (CF) analysis. The relative intensities of 5D0 --> 7F2 to 5D0 --> 7F1 transitions, crystal-field strength parameters and decay times of the 5D0 level have been determined and are found to be lower for Pb based glasses than those of Zn/Li based glasses. The lifetimes of 5D0 level are found to increase when borate glasses are modified with pure fluorides than with oxides and oxyfluorides. The fluorescence decay of 5D0 level fits perfect single exponential in the Eu3+:glass systems studied which indicates the absence of energy transfer between Eu3+ ions in these glasses.

Ionic Borate-Based Covalent Organic Frameworks: Lightweight Porous Materials for Lithium-Stable Solid State Electrolytes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Black, Hayden T.; Harrison, Katharine Lee

2016-10-01

The synthesis and characterization of the first polyelectrolyte of intrinsic microporosity (PEIM) is described. The novel material was synthesized via reaction between the nitrile group in the polymer backbone and n-butyl lithium, effectively anchoring an imine anion to the porous framework while introducing a mobile lithium counterion. The PEIM was characterized by 13C, 1H, and 7Li NMR experiments, revealing quantitative conversion of the nitrile functionality to the anionic imine. Variable temperature 7Li NMR analysis of the dry PEIM and the electrolyteswollen PEIM revealed that lithium ion transport within the dry PEIM was largely due to interchain hopping of the Limore » + ions, and that the mobility of polymer associated Li + was reduced after swelling in electrolyte solution. Meanwhile, the swollen PEIM supported efficient transport of dissolved Li + within the expanded pores. These results are discussed in the context of developing novel solid or solid-like lithium ion electrolytes using the new PEIM material.« less

Solid polymeric electrolytes for lithium batteries

DOEpatents

Angell, Charles A.; Xu, Wu; Sun, Xiaoguang

2006-03-14

Novel conductive polyanionic polymers and methods for their preparion are provided. The polyanionic polymers comprise repeating units of weakly-coordinating anionic groups chemically linked to polymer chains. The polymer chains in turn comprise repeating spacer groups. Spacer groups can be chosen to be of length and structure to impart desired electrochemical and physical properties to the polymers. Preferred embodiments are prepared from precursor polymers comprising the Lewis acid borate tri-coordinated to a selected ligand and repeating spacer groups to form repeating polymer chain units. These precursor polymers are reacted with a chosen Lewis base to form a polyanionic polymer comprising weakly coordinating anionic groups spaced at chosen intervals along the polymer chain. The polyanionic polymers exhibit high conductivity and physical properties which make them suitable as solid polymeric electrolytes in lithium batteries, especially secondary lithium batteries.

Neutronics and activation analysis of lithium-based ternary alloys in IFE blankets

DOE PAGES

Jolodosky, Alejandra; Kramer, Kevin; Meier, Wayne; ...

2016-04-09

Here we report that an attractive feature of using liquid lithium as the breeder and coolant in fusion blankets is that it has very high tritium solubility and results in very low levels of tritium permeation throughout the facility infrastructure. However, lithium metal vigorously reacts with air and water and presents plant safety concerns. The Lawrence Livermore National Laboratory is carrying an effort to develop a lithium-based alloy that maintains the beneficial properties of lithium (e.g. high tritium breeding and solubility) and at the same time reduces overall flammability concerns. This study evaluates the neutronics performance of lithium-based alloys inmore » the blanket of an inertial fusion energy chamber in order to inform such development. 3-D Monte Carlo calculations were performed to evaluate two main neutronics performance parameters for the blanket: tritium breeding ratio (TBR), and the fusion energy multiplication factor (EMF). It was found that elements that exhibit low absorption cross sections and higher q-values such as lead, tin, and strontium, perform well with those that have high neutron multiplication such as lead and bismuth. These elements meet TBR constrains ranging from 1.02 to 1.1. However, most alloys do not reach EMFs greater than 1.15. Additionally, it was found that enriching lithium significantly increases the TBR and decreases the minimum lithium concentration by more than 60%. The amount of enrichment depends on how much total lithium is in the alloy to begin with. Alloys that performed well in the TBR and EMF calculations were considered for activation analysis. Activation simulations were executed with 50 years of irradiation and 300 years of cooling. It was discovered that bismuth is a poor choice due to achieving the highest decay heat, contact dose rates, and accident doses. In addition, it does not meet the waste disposal ratings (WDR). Some of the activation results for alloys with tin, zinc, and gallium were in the higher end and should be considered secondary to elements such as strontium and barium that had overall better results. The results of this study along with other considerations such as thermodynamics, and chemical reactivity will help down select a preferred lithium ternary alloy.« less

High precision hyperfine measurements in Bismuth challenge bound-state strong-field QED

NASA Astrophysics Data System (ADS)

Ullmann, Johannes; Andelkovic, Zoran; Brandau, Carsten; Dax, Andreas; Geithner, Wolfgang; Geppert, Christopher; Gorges, Christian; Hammen, Michael; Hannen, Volker; Kaufmann, Simon; König, Kristian; Litvinov, Yuri A.; Lochmann, Matthias; Maaß, Bernhard; Meisner, Johann; Murböck, Tobias; Sánchez, Rodolfo; Schmidt, Matthias; Schmidt, Stefan; Steck, Markus; Stöhlker, Thomas; Thompson, Richard C.; Trageser, Christian; Vollbrecht, Jonas; Weinheimer, Christian; Nörtershäuser, Wilfried

2017-05-01

Electrons bound in highly charged heavy ions such as hydrogen-like bismuth 209Bi82+ experience electromagnetic fields that are a million times stronger than in light atoms. Measuring the wavelength of light emitted and absorbed by these ions is therefore a sensitive testing ground for quantum electrodynamical (QED) effects and especially the electron-nucleus interaction under such extreme conditions. However, insufficient knowledge of the nuclear structure has prevented a rigorous test of strong-field QED. Here we present a measurement of the so-called specific difference between the hyperfine splittings in hydrogen-like and lithium-like bismuth 209Bi82+,80+ with a precision that is improved by more than an order of magnitude. Even though this quantity is believed to be largely insensitive to nuclear structure and therefore the most decisive test of QED in the strong magnetic field regime, we find a 7-σ discrepancy compared with the theoretical prediction.

High precision hyperfine measurements in Bismuth challenge bound-state strong-field QED.

PubMed

Ullmann, Johannes; Andelkovic, Zoran; Brandau, Carsten; Dax, Andreas; Geithner, Wolfgang; Geppert, Christopher; Gorges, Christian; Hammen, Michael; Hannen, Volker; Kaufmann, Simon; König, Kristian; Litvinov, Yuri A; Lochmann, Matthias; Maaß, Bernhard; Meisner, Johann; Murböck, Tobias; Sánchez, Rodolfo; Schmidt, Matthias; Schmidt, Stefan; Steck, Markus; Stöhlker, Thomas; Thompson, Richard C; Trageser, Christian; Vollbrecht, Jonas; Weinheimer, Christian; Nörtershäuser, Wilfried

2017-05-16

Electrons bound in highly charged heavy ions such as hydrogen-like bismuth 209 Bi 82+ experience electromagnetic fields that are a million times stronger than in light atoms. Measuring the wavelength of light emitted and absorbed by these ions is therefore a sensitive testing ground for quantum electrodynamical (QED) effects and especially the electron-nucleus interaction under such extreme conditions. However, insufficient knowledge of the nuclear structure has prevented a rigorous test of strong-field QED. Here we present a measurement of the so-called specific difference between the hyperfine splittings in hydrogen-like and lithium-like bismuth 209 Bi 82+,80+ with a precision that is improved by more than an order of magnitude. Even though this quantity is believed to be largely insensitive to nuclear structure and therefore the most decisive test of QED in the strong magnetic field regime, we find a 7-σ discrepancy compared with the theoretical prediction.

High precision hyperfine measurements in Bismuth challenge bound-state strong-field QED

PubMed Central

Ullmann, Johannes; Andelkovic, Zoran; Brandau, Carsten; Dax, Andreas; Geithner, Wolfgang; Geppert, Christopher; Gorges, Christian; Hammen, Michael; Hannen, Volker; Kaufmann, Simon; König, Kristian; Litvinov, Yuri A.; Lochmann, Matthias; Maaß, Bernhard; Meisner, Johann; Murböck, Tobias; Sánchez, Rodolfo; Schmidt, Matthias; Schmidt, Stefan; Steck, Markus; Stöhlker, Thomas; Thompson, Richard C.; Trageser, Christian; Vollbrecht, Jonas; Weinheimer, Christian; Nörtershäuser, Wilfried

2017-01-01

Electrons bound in highly charged heavy ions such as hydrogen-like bismuth 209Bi82+ experience electromagnetic fields that are a million times stronger than in light atoms. Measuring the wavelength of light emitted and absorbed by these ions is therefore a sensitive testing ground for quantum electrodynamical (QED) effects and especially the electron–nucleus interaction under such extreme conditions. However, insufficient knowledge of the nuclear structure has prevented a rigorous test of strong-field QED. Here we present a measurement of the so-called specific difference between the hyperfine splittings in hydrogen-like and lithium-like bismuth 209Bi82+,80+ with a precision that is improved by more than an order of magnitude. Even though this quantity is believed to be largely insensitive to nuclear structure and therefore the most decisive test of QED in the strong magnetic field regime, we find a 7-σ discrepancy compared with the theoretical prediction. PMID:28508892

Structural and optical properties of lithium sodium borate glasses doped with Sm3+ ions

NASA Astrophysics Data System (ADS)

Dawaud, R. S. E. S.; Hashim, S.; Alajerami, Y. S. M.; Mhareb, M. H. A.; Maqableh, M. M.; Tamchek, N.

2014-07-01

Absorption and emission spectra of Sm3+ doped lithium sodium borate (LNB) have been reported. The samples were prepared by the melt-quenching technique and characterized by X-ray diffraction (XRD), diffraction thermal analysis (DTA), Fourier transforms infrared (FTIR) spectroscopy and field emission scanning electron microscopy (FESEM). From the thermo-grams spectrum, glass transition (Tg), crystallization (Tc) and melting temperatures (Tm) have been evaluated. Direct and indirect optical band gaps have been calculated based on the glasses UV absorption spectra. These glasses have shown strong nine absorption bands with hypersensitive transition at 1221 nm (6H5/2→4H3/2) and five emission bands for the transition at 4I7/2→6H13/2 (green color), 4I7/2→6H7/2 (orange color), 4I7/2→6H9/2 (orange color), 4I7/2→6H11/2 (red color) and 4I7/2→6H13/2 (red color) with performing an excitation of 400 nm. The oscillator strengths, refractive index, ions concentration, polaron radius and other parameters have been calculated for each dopant.

Thermoluminescence properties of lithium magnesium borate glasses system doped with dysprosium oxide.

PubMed

Mhareb, M H A; Hashim, S; Ghoshal, S K; Alajerami, Y S M; Saleh, M A; Razak, N A B; Azizan, S A B

2015-12-01

We report the impact of dysprosium (Dy(3+)) dopant and magnesium oxide (MgO) modifier on the thermoluminescent properties of lithium borate (LB) glass via two procedures. The thermoluminescence (TL) glow curves reveal a single prominent peak at 190 °C for 0.5 mol% of Dy(3+). An increase in MgO contents by 10 mol% enhances the TL intensity by a factor of 1.5 times without causing any shift in the maximum temperature. This enhancement is attributed to the occurrence of extra electron traps created via magnesium and the energy transfer to trivalent Dy(3+) ions. Good linearity in the range of 0.01-4 Gy with a linear correlation coefficient of 0.998, fading as low as 21% over a period of 3 months, excellent reproducibility without oven annealing and tissue equivalent effective atomic numbers ~8.71 are achieved. The trap parameters, including geometric factor (μg), activation energy (E) and frequency factor (s) associated with LMB:Dy are also determined. These favorable TL characteristics of prepared glasses may contribute towards the development of Li2O-MgO-B2O3 radiation dosimeters. Copyright © 2015 John Wiley & Sons, Ltd.

Taichi-inspired rigid-flexible coupling cellulose-supported solid polymer electrolyte for high-performance lithium batteries

PubMed Central

Zhang, Jianjun; Yue, Liping; Hu, Pu; Liu, Zhihong; Qin, Bingsheng; Zhang, Bo; Wang, Qingfu; Ding, Guoliang; Zhang, Chuanjian; Zhou, Xinhong; Yao, Jianhua; Cui, Guanglei; Chen, Liquan

2014-01-01

Inspired by Taichi, we proposed rigid-flexible coupling concept and herein developed a highly promising solid polymer electrolyte comprised of poly (ethylene oxide), poly (cyano acrylate), lithium bis(oxalate)borate and robust cellulose nonwoven. Our investigation revealed that this new class solid polymer electrolyte possessed comprehensive properties in high mechanical integrity strength, sufficient ionic conductivity (3 × 10−4 S cm−1) at 60°C and improved dimensional thermostability (up to 160°C). In addition, the lithium iron phosphate (LiFePO4)/lithium (Li) cell using such solid polymer electrolyte displayed superior rate capacity (up to 6 C) and stable cycle performance at 80°C. Furthermore, the LiFePO4/Li battery could also operate very well even at an elevated temperature of 160°C, thus improving enhanced safety performance of lithium batteries. The use of this solid polymer electrolyte mitigates the safety risk and widens the operation temperature range of lithium batteries. Thus, this fascinating study demonstrates a proof of concept of the use of rigid-flexible coupling solid polymer electrolyte toward practical lithium battery applications with improved reliability and safety. PMID:25183416

Multimodal emissions from Tb{sup 3+}/Yb{sup 3+} co-doped lithium borate glass: Upconversion, downshifting and quantum cutting

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bahadur, A.; Yadav, R.S.; Yadav, R.V.

This paper reports the optical properties of Tb{sup 3+}/Yb{sup 3+} co-doped lithium borate (LB) glass prepared by melt quench method. The absorption spectrum of the Yb{sup 3+} doped LB glass contains intense NIR band centered at 976 nm due to {sup 2}F{sub 7/2}→{sup 2}F{sub 5/2} transition. The emission spectra of the prepared glasses have been monitored on excitation with 266, 355 and 976 nm. The Yb{sup 3+} doped glass emits a broad NIR band centered at 976 nm whereas the Tb{sup 3+} doped glass gives off visible bands on excitations with 266 and 355 nm. When the Tb{sup 3+} andmore » Yb{sup 3+} ions are co-doped together, the emission intensity in the visible region decreases whereas it increases in the NIR region significantly. The increase in the emission intensity in the NIR region is due to efficient cooperative energy transfer (CET) from Tb{sup 3+} to Yb{sup 3+} ions. The quantum cutting efficiency for Tb{sup 3+}/Yb{sup 3+} co-doped glass has been calculated and compared for 266 and 355 nm excitations. The quantum cutting efficiency is larger for 355 nm excitation (137%). The Tb{sup 3+}/Yb{sup 3+} co-doped LB glass also emits upconverted visible bands on excitation with 976 nm. The mechanisms involved in the energy transfer have been discussed using schematic energy level diagram. The Tb{sup 3+}/Yb{sup 3+} co-doped LB glass may be used in the optical devices and in solar cell for solar spectral conversion and behaves as a multi-modal photo-luminescent material. - Graphical abstract: The Tb{sup 3+}/Yb{sup 3+} co-doped lithium borate (LB) glass prepared by melt quench method emits upconverted visible emissions through upconversion CET from Yb{sup 3+} to Tb{sup 3+} ions and quantum cutting emissions through downconversion CET from Tb{sup 3+} to Yb{sup 3+} ions. Therefore, the Tb{sup 3+}/Yb{sup 3+} co-doped LB glass may find applications in optical devices and solar cell and behaves as a multi-modal photo-luminescent material. - Highlights: • The Tb{sup 3+}/Yb{sup 3+} co-doped lithium borate (LB) glass prepared by melt quench method. • The Tb{sup 3+}/Yb{sup 3+} co-doped glass gives QC emissions upon 266 and 355 nm excitations. • The Tb{sup 3+}/Yb{sup 3+} co-doped glass also emits intense green color on excitation with 976 nm. • The quantum cutting efficiency is larger for 355 nm excitation (137%). • The Tb{sup 3+}/Yb{sup 3+} co-doped glass may be used in solar cell and display devices.« less

XRD and FTIR studies the effect of heat treatment and doping the transition metal oxide on LiNbO3 and LiNb3O8 nano-crystallite phases in lithium borate glass system.

PubMed

Kashif, Ismail; Soliman, Ashia A; Sakr, Elham M; Ratep, Asmaa

2013-09-01

Glasses of various compositions in the system 90 Li2B4O7-10 Nb2O5 mixed with T.M ions (where T.M is the transition metal) were prepared by quenching technique. Heat-treatment of the parent glasses was performed at 540, 570 and 620 °C, for 5 and 16 h. The glass structure evolution during the controlled crystallization was examined by XRD and FT-IR spectroscopy analysis. The crystalline phases present in the glass ceramics were identified via X-ray diffraction as a function of heat treatment. The FT-IR data propose for these glasses and heat-treated glass network structures mainly built by: di-, tri-, tetra-, penta-and ortho-borate groups. It was found that the quantitative evolution of these various borate species in the glass structures is influenced by the transition metal. A detailed discussion relating to the N4 evolution with the T.M content was made. Copyright © 2013 Elsevier B.V. All rights reserved.

Electrolytes for Low Impedance, Wide Operating Temperature Range Lithium-Ion Battery Module

NASA Technical Reports Server (NTRS)

Hallac, Boutros (Inventor); Krause, Frederick C. (Inventor); Jiang, Junwei (Inventor); Smart, Marshall C. (Inventor); Metz, Bernhard M. (Inventor); Bugga, Ratnakumar V. (Inventor)

2018-01-01

A lithium ion battery cell includes a housing, a cathode disposed within the housing, wherein the cathode comprises a cathode active material, an anode disposed within the housing, wherein the anode comprises an anode active material, and an electrolyte disposed within the housing and in contact with the cathode and anode. The electrolyte consists essentially of a solvent mixture, a lithium salt in a concentration ranging from approximately 1.0 molar (M) to approximately 1.6 M, and an additive mixture. The solvent mixture includes a cyclic carbonate, an non-cyclic carbonate, and a linear ester. The additive mixture consists essentially of lithium difluoro(oxalato)borate (LiDFOB) in an amount ranging from approximately 0.5 weight percent to approximately 2.0 weight percent based on the weight of the electrolyte, and vinylene carbonate (VC) in an amount ranging from approximately 0.5 weight percent to approximately 2.0 weight percent based on the weight of the electrolyte.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Azimi, Nasim; Xue, Zheng; Hu, Libo

Lithium difluoro(oxalato) borate (LiDFOB) was investigated as an electrolyte additive for the Li-S battery. This additive was identified to be an efficient electrolyte additive to suppress the polysulfide shuttling effect existing in the conventional Li-S chemistry. To detect the positive impact of the new additive, oligo (ethylene glycol) functionalized silane was employed as the electrolyte solvent due to its high solvation capability with the lithium polysulfides. The electrochemical results and the SEM data of Li-S battery using the new electrolyte confirmed the role of the LiDFOB as a critical component to eliminate the shuttling of the dissolved polysulfides thus enablingmore » a high coulombic efficiency. (C) 2014 Elsevier Ltd. All rights reserved.« less

Mixed polyanion glass cathodes: Effect of polyanion content

DOE PAGES

Kercher, Andrew K.; Kolopus, James A.; Sacci, Robert L.; ...

2017-02-18

Mixed polyanion glass cathodes in lithium-ion batteries have very high capacities (200-500 mAh/g), but currently these materials have fundamental problems with 1 st-cycle irreversible loss, cycling efficiency, and capacity fade. It is well established that polyanion substitutions into glasses can dramatically affect their physical properties, but the effect of polyanion content on the electrochemical performance has not been previously established. The proper amount of lithium and borate substitution in copper phosphate/vanadate glasses was shown to nearly eliminate 1 st-cycle irreversible loss and improve cycling efficiency. As a result, Raman and IR spectroscopy were used to identify polyanions that correlated withmore » electrochemical performance changes.« less

Comments on "Optical properties of borate crystals in the terahertz domain"

NASA Astrophysics Data System (ADS)

Svetlichnyi, V. A.; Naftaly, M.; Molloy, J. F.; Andreev, Yu. M.; Kokh, K. A.; Lanskii, G. V.; Kononova, N. G.; Kokh, A. E.

2016-04-01

We comment on the recent paper by V.D. Antsygin et al. [Opt. Commun. 309 (2013) 333-337], in which for the first time dispersions of refractive indices nx,z in lithium triborate (LBO) were presented for the THz domain. Their claim of "nx>nz", based on measurements by THz time-domain spectroscopy (TDS), is contrary to the well-known relationship for the maximum transparency region.

Capacity extended bismuth-antimony cathode for high-performance liquid metal battery

NASA Astrophysics Data System (ADS)

Dai, Tao; Zhao, Yue; Ning, Xiao-Hui; Lakshmi Narayan, R.; Li, Ju; Shan, Zhi-wei

2018-03-01

Li-Bi based liquid metal batteries (LMBs) have attracted interest due to their potential for solving grid scale energy storage problems. In this study, the feasibility of replacing the bismuth cathode with a bismuth-antimony alloy cathode in lithium based LMBs is investigated. The influence of the Bi:Sb ratio on voltage characteristics is evaluated via the constant current discharge method and electrochemical titration. On observing the cross section of the electrode at various stages of discharge, it is determined that both Sb and Bi form solid intermetallics with Li on the cathode. Additionally, the addition of Bi not only reduces the melting temperature of the Bi:Sb intermetallic but also actively contributes to the electrode capacity. Thereafter, a Li|LiCl-LiF|Sb-Bi liquid metal battery with 3 A h nameplate capacity, assembled and cycled at 1 C rate, is found to possess a stable capacity for over 160 cycles. The overall performance of this battery is discussed in the context of cost effectiveness, energy and coulombic efficiencies.

PROCESS FOR THE RECOVERY OF PLUTONIUM

DOEpatents

Ritter, D.M.

1959-01-13

An improvement is presented in the process for recovery and decontamination of plutonium. The carrier precipitate containing plutonium is dissolved and treated with an oxidizing agent to place the plutonium in a hexavalent oxidation state. A lanthanum fluoride precipitate is then formed in and removed from the solution to carry undesired fission products. The fluoride ions in the reniaining solution are complexed by addition of a borate sueh as boric acid, sodium metaborate or the like. The plutonium is then reduced and carried from the solution by the formation of a bismuth phosphate precipitate. This process effects a better separation from unwanted flssion products along with conccntration of the plutonium by using a smaller amount of carrier.

Evaluation of High-Power Solar Electric Propulsion using Advanced Ion, Hall, MPD, and PIT Thrusters for Lunar and Mars Cargo Missions

NASA Technical Reports Server (NTRS)

Frisbee, Robert H.

2006-01-01

This paper presents the results of mission analyses that expose the advantages and disadvantages of high-power (MWe-class) Solar Electric Propulsion (SEP) for Lunar and Mars Cargo missions that would support human exploration of the Moon and Mars. In these analyses, we consider SEP systems using advanced Ion thrusters (the Xenon [Xe] propellant Herakles), Hall thrusters (the Bismuth [Bi] propellant Very High Isp Thruster with Anode Layer [VHITAL], magnetoplasmadynamic (MPD) thrusters (the Lithium [Li] propellant Advanced Lithium-Fed, Applied-field Lorentz Force Accelerator (ALFA2), and pulsed inductive thruster (PIT) (the Ammonia [NH3] propellant Nuclear-PIT [NuPIT]). The analyses include comparison of the advanced-technology propulsion systems (VHITAL, ALFA2, and NuPIT) relative to state-of-theart Ion (Herakles) propulsion systems and quantify the unique benefits of the various technology options such as high power-per-thruster (and/or high power-per-thruster packaging volume), high specific impulse (Isp), high-efficiency, and tankage mass (e.g., low tankage mass due to the high density of bismuth propellant). This work is based on similar analyses for Nuclear Electric Propulsion (NEP) systems.

Order–Disorder Transitions and Superionic Conductivity in the Sodium nido -Undeca(carba)borates

DOE PAGES

Tang, Wan Si; Dimitrievska, Mirjana; Stavila, Vitalie; ...

2017-11-20

The salt compounds NaB 11H 14, Na-7-CB10H13, Li-7-CB 10H 13, Na-7,8-C 2B 9H 12, and Na-7,9-C 2B 9H 12 all contain geometrically similar, monocharged, nido-undeca(carba)borate anions (i.e., truncated icosohedral-shaped clusters constructed of only 11 instead of 12 {B-H} + {C-H} vertices and an additional number of compensating bridging and/or terminal H atoms). We used first-principles calculations, X-ray powder diffraction, differential scanning calorimetry, neutron vibrational spectroscopy, neutron elastic-scattering fixed-window scans, quasielastic neutron scattering, and electrochemical impedance measurements to investigate their structures, bonding potentials, phase-transition behaviors, anion orientational mobilities, and ionic conductivities compared to those of their closo-poly(carba)borate cousins. All exhibited order-disordermore » phase transitions somewhere between room temperature and 375 K. All disordered phases appear to possess highly reorientationally mobile anions (> ~10 10 jumps s -1 above 300 K) and cation-vacancy-rich, close-packed or body-center-cubic-packed structures [like previously investigated closo-poly(carba)borates]. Moreover, all disordered phases display superionic conductivities but with generally somewhat lower values compared to those for the related sodium and lithium salts with similar monocharged 1-CB 9H 10- and CB 11H 12- closo-carbaborate anions. This study significantly expands the known toolkit of solid-state, poly(carba)borate-based salts capable of superionic conductivities and provides valuable insights into the effect of crystal lattice, unit cell volume, number of carbon atoms incorporated into the anion, and charge polarization on ionic conductivity.« less

The Evaluation of Triphenyl Phosphate as a Flame Retardant Additive to Improve the Safety of Lithium-Ion Battery Electrolytes

NASA Technical Reports Server (NTRS)

Smart, M. C.; Krause, F. C.; Hwang, C.; West, W. C.; Soler, J.; Prakash, G. K. S.; Ratnakumar, B. V.

2011-01-01

With the intent of improving the safety characteristics of lithium ion cells, electrolytes containing flame retardant additives have been investigated. A number of triphenyl phosphate-containing electrolytes were evaluated in both coin cells and experimental three electrode lithium-ion cells (containing reference electrodes). A number of chemistries were investigated, including MCMB carbon/LiNi(0.8)Co(0.2)O2 (NCO), graphite/LiNi(0.8)Co(0.15)Al(0.05)O2 (NCA), Li/Li(Li(0.17)Ni(0.25)Mn(0.58))O2, Li/LiNiMnCoO2 (NMC) and graphite/LiNiMnCoO2 (NMC), to study the effect that different electrolyte compositions have upon performance. A wide range of TPP-containing electrolytes were demonstrated to have good compatibility with the C/NCO, C/NCA, and Li/NMC systems, however, poor performance was initially observed with the high voltage C/NMC system. This necessitated the development of improved electrolytes with stabilizing additives, leading to formulations containing lithium bis(oxalato)borate (LiBOB) that displayed substantially improved performance.

Quantitative determination of copper in a glass matrix using double pulse laser induced breakdown and electron paramagnetic resonance spectroscopic techniques.

PubMed

Khalil, Ahmed A I; Morsy, Mohamed A

2016-07-01

A series of lithium-lead-borate glasses of a variable copper oxide loading were quantitatively analyzed in this work using two distinct spectroscopic techniques, namely double pulse laser induced breakdown spectroscopy (DP-LIBS) and electron paramagnetic resonance (EPR). DP-LIBS results measured upon a combined nanosecond lasers irradiation running at 266nm and 1064nm pulses of a collinear configuration directed to the surface of borate glass samples with a known composition. This arrangement was employed to predict the electron's temperature (Te) and density (Ne) of the excited plasma from the recorded spectra. The intensity of elements' responses using this scheme is higher than that of single-pulse laser induced breakdown spectroscopy (SP-LIBS) setup under the same experimental conditions. On the other hand, the EPR data shows typical Cu (II) EPR-signals in the borate glass system that is networked at a distorted tetragonal Borate-arrangement. The signal intensity of the Cu (II) peak at g⊥=2.0596 has been used to quantify the Cu-content accurately in the glass matrix. Both techniques produced linear calibration curves of Cu-metals in glasses with excellent linear regression coefficient (R(2)) values. This study establishes a good correlation between DP-LIBS analysis of glass and the results obtained using EPR spectroscopy. The proposed protocols prove the great advantage of DP-LIBS system for the detection of a trace copper on the surface of glasses. Copyright © 2016 Elsevier B.V. All rights reserved.

Optically stimulated luminescence of borate glasses containing magnesia, quicklime, lithium and potassium carbonates

NASA Astrophysics Data System (ADS)

Valença, J. V. B.; Silveira, I. S.; Silva, A. C. A.; Dantas, N. O.; Antonio, P. L.; Caldas, L. V. E.; d'Errico, F.; Souza, S. O.

2017-11-01

The OSL characteristics of three different borate glass matrices containing magnesia (LMB), quicklime (LCB) or potassium carbonate (LKB) were examined. Five different formulations for each composition were produced using a melt-quenching method and analyzed in terms of both dose-response curves and OSL shape decay. The samples were irradiated using a 90Sr/90Y beta source with doses up to 30 Gy. Dose-response curves were plotted using the initial OSL intensity as the chosen parameter. The OSL analysis showed that LKB glasses are the most sensitive to beta irradiation. For the most sensitive LKB composition, the irradiation process was also done using a 60Co gamma source in a dose range from 200 to 800 Gy. In all cases, no saturation was observed. A fitting process using a three-term exponential function was performed for the most sensitive formulations of each composition, which suggested a similar behavior in the OSL decay.

High-power, continuous-wave, solid-state, single-frequency, tunable source for the ultraviolet.

PubMed

Aadhi, A; Apurv Chaitanya, N; Singh, R P; Samanta, G K

2014-06-15

We report the development of a compact, high-power, continuous-wave, single-frequency, ultraviolet (UV) source with extended wavelength tunability. The device is based on single-pass, intracavity, second-harmonic-generation (SHG) of the signal radiation of a singly resonant optical parametric oscillator (SRO) working in the visible and near-IR wavelength range. The SRO is pumped in the green with a 25-mm-long, multigrating, MgO doped periodically poled stoichiometric lithium tantalate (MgO:sPPLT) as nonlinear crystal. Using three grating periods, 8.5, 9.0, and 9.5 μm of the MgO:sPPLT crystal and a single set of cavity mirrors, the SRO can be tuned continuously across 710.7-836.3 nm in the signal and corresponding idler across 2115.8-1462.1 nm with maximum idler power of 1.9 W and maximum out-coupled signal power of 254 mW. By frequency-doubling the intracavity signal with a 5-mm-long bismuth borate (BIBO) crystal, we can further tune the SRO continuously over 62.8 nm across 355.4-418.2 nm in the UV with maximum single-frequency UV power, as much as 770 mW at 398.28 nm in a Gaussian beam profile. The UV radiation has an instantaneous line-width of ∼14.5  MHz and peak-peak frequency stability of 151 MHz over 100 s. More than 95% of the tuning range provides UV power >260  mW. Access to lower UV wavelengths can in principle be realized by operating the SRO in the visible using shorter grating periods.

Effect of SiO2 addition and gamma irradiation on the lithium borate glasses

NASA Astrophysics Data System (ADS)

Raut, A. P.; Deshpande, V. K.

2018-01-01

The physical properties like density, glass transition temperature (Tg), and ionic conductivity of lithium borate (LB) glasses with SiO2 addition were measured before and after gamma irradiation. Remarkable changes in properties have been obtained in the physical properties of LB glasses with SiO2 addition and after gamma irradiation. The increase in density and glass transition temperature of LB glasses with SiO2 addition has been explained with the help of increase in density of cross linking due to SiO4 tetrahedra formation. The increase in ionic conductivity with SiO2 addition was explained with the help of ‘mixed glass former effect’. The increase in density and Tg of LB glasses with SiO2 addition after gamma irradiation has been attributed to fragmentation of bigger ring structure into smaller rings, which increases the density of cross linking and hence compaction. The exposure of gamma irradiation has lead to decrease in ionic conductivity of LB glasses with SiO2 addition. The atomic displacement caused by gamma irradiation resulted in filling of interstices and decrease in trapping sites. This explains the obtained decrease in ionic conductivity after gamma irradiation of glasses. The obtained results of effect of SiO2 addition and gamma irradiation on the density, Tg and ionic conductivity has been supported by FTIR results.

Impact of Nd3+ ions on physical and optical properties of Lithium Magnesium Borate glass

NASA Astrophysics Data System (ADS)

Mhareb, M. H. A.; Hashim, S.; Ghoshal, S. K.; Alajerami, Y. S. M.; Saleh, M. A.; Dawaud, R. S.; Razak, N. A. B.; Azizan, S. A. B.

2014-11-01

Enhancing the up-conversion efficiency of borate glass via optimized doping of rare earth ions is an ever-ending quest in lasing glass. Neodymium (Nd3+) doped Lithium Magnesium Borate (LMB) glasses are prepared using the melt-quenching method. X-ray diffraction (XRD), Fourier transformed infrared (FTIR), UV-Vis-NIR absorption and Photoluminescence (PL) spectroscopic characterizations are made to examine the influence of Nd3+ concentration on physical properties and optical properties. Nd3+ contents dependent density, molar volume, refractive index, ion concentration, Polaron radius, inter nuclear distance, field strength, energy band gap and oscillator strength are calculated. XRD patterns confirm the amorphous nature of all glasses and the FTIR spectra reveal the presence of BO3 and BO4 functional groups. UV-Vis-IR spectra exhibit ten prominent bands centered at 871, 799, 741, 677, 625, 580, 522, 468, 426, 349 nm corresponding to the transitions from the ground state to 4F3/2, (4F5/2 + 2H9/2), (4F7/2 + 4S3/2), 4F9/2, 2H11/2, (4G5/2 + 2G7/2), (2K13/2 + 4G7/2 + 4G9/2), (2G9/2 + 2D3/2 + 2P3/2), (2P1/2 + 2D5/2), (4D3/2 + 4D5/2) excited states, respectively. A hyper-sensitive transition related to (4G5/2 + 2G7/2) level is evidenced at 580 nm. The room temperature up-conversion emission spectra at 800 nm excitation displays three peaks centered at 660, 610 and 540 nm. Glass with 0.5 mol% of Nd3+ showing an emission enhancement by a factor to two is attributed to the energy transfer between Mg2+ and Nd3+ ions. Our results suggest that these glasses can be nominated for solid state lasers and other photonic devices.

X-ray Raman spectroscopy of lithium-ion battery electrolyte solutions in a flow cell.

PubMed

Ketenoglu, Didem; Spiekermann, Georg; Harder, Manuel; Oz, Erdinc; Koz, Cevriye; Yagci, Mehmet C; Yilmaz, Eda; Yin, Zhong; Sahle, Christoph J; Detlefs, Blanka; Yavaş, Hasan

2018-03-01

The effects of varying LiPF 6 salt concentration and the presence of lithium bis(oxalate)borate additive on the electronic structure of commonly used lithium-ion battery electrolyte solvents (ethylene carbonate-dimethyl carbonate and propylene carbonate) have been investigated. X-ray Raman scattering spectroscopy (a non-resonant inelastic X-ray scattering method) was utilized together with a closed-circle flow cell. Carbon and oxygen K-edges provide characteristic information on the electronic structure of the electrolyte solutions, which are sensitive to local chemistry. Higher Li + ion concentration in the solvent manifests itself as a blue-shift of both the π* feature in the carbon edge and the carbonyl π* feature in the oxygen edge. While these oxygen K-edge results agree with previous soft X-ray absorption studies on LiBF 4 salt concentration in propylene carbonate, carbon K-edge spectra reveal a shift in energy, which can be explained with differing ionic conductivities of the electrolyte solutions.

Preparation of Ni3B2O6 nanosheet-based flowerlike architecture by a precursor method and its electrochemical properties in lithium-ion battery

NASA Astrophysics Data System (ADS)

Liang, Pan; Du, Lu; Wang, Xia; Liu, Zhi-Hong

2014-11-01

A novel flower-like nickel borate of Ni3B2O6 nanostructure was prepared through a hydrothermal treatment and sequential thermal decomposition of precursor without employing any template or surfactant. All the samples were characterized by XRD, IR, XPS, TG-DTA, nitrogen adsorption, SEM and TEM. The flower-like Ni3B2O6 nanostructure was self-assembled by nanosheets with the thickness of about 40 nm. The electrochemical properties in lithium-ion battery of flower-like Ni3B2O6 nanostructure were studied by the cyclic voltammetry, galvanostatic cycling test, and electrochemical impedance spectroscopy, which showed it had a high initial discharge capacity and a good reversibility.

RARE-EARTH METAL FISSION PRODUCTS FROM LIQUID U-Bi

DOEpatents

Wiswall, R.H.

1960-05-10

Fission product metals can be removed from solution in liquid bismuth without removal of an appreciable quantity of uranium by contacting the liquid metal solution with fused halides, as for example, the halides of sodium, potassium, and lithium and by adding to the contacted phases a quantity of a halide which is unstable relative to the halides of the fission products, a specific unstable halide being MgCl/sub 3/.

Electromagnetic Pumps for Conductive-Propellant Feed Systems

NASA Technical Reports Server (NTRS)

Markusic, T. E.; Polzin, K. A.

2005-01-01

There has been a recent, renewed interest in high-power electric thrusters for application in nuclear-electric propulsion systems. Two of the most promising thrusters utilize liquid metal propellants: the lithium-fed magnetoplasmadynamic thruster and the bismuth-fed Hall thruster. An important element of part of the maturation of these thrusters will be the development of compact, reliable conductive-propellant feed system components. In the present paper we provide design considerations and experimental calibration data for electromagnetic (EM) pumps. The role of an electromagnetic pump in a liquid metal feed system is to establish a pressure gradient between the propellant reservoir and the thruster - to establish the requisite mass flow rate. While EM pumps have previously been used to a limited extent in nuclear reactor cooling loops, they have never been implemented in electric propulsion (EP) systems. The potential benefit of using EM pumps for EP are reliability (no moving parts) and the ability to precisely meter the propellant flow rate. We have constructed and tested EM pumps that use gallium, lithium, and bismuth propellants. Design details, test results (pressure developed versus current), and material compatibility issues are reported. It is concluded that EM pumps are a viable technology for application in both laboratory and flight EP conductive-propellant feed systems.

A new anion receptor for improving the interface between lithium- and manganese-rich layered oxide cathode and the electrolyte

DOE PAGES

Ma, Yulin; Zhou, Yan; Du, Chunyu; ...

2017-02-15

Surface degradation on cycled lithium-ion battery cathode particles is governed not only by intrinsic thermodynamic properties of the material but also, oftentimes more predominantly, by the side reactions with the electrolytic solution. A superior electrolyte inhibits these undesired side reactions on the cathode and at the electrolyte interface, which consequently minimizes the deterioration of the cathode surface. The present study investigates a new boron-based anion receptor, tris(2,2,2-trifluoroethyl)borate (TTFEB), as an electrolyte additive in cells containing a lithium- and manganese-rich layered oxide cathode, Li 1.16Ni 0.2Co 0.1Mn 0.54O 2. Our electrochemical studies demonstrate that the cycling performance and Coulombic efficiency aremore » significantly improved because of the additive, in particular, under elevated temperature conditions. Spectroscopic analyses revealed that the addition of 0.5 wt % TTFEB is capable of reducing the content of lithium-containing inorganic species within the cathode-electrolyte interphase layer and minimizing the reduction of tetravalent Mn4+ at the cathode surface. Furthermore, our work introduces a novel additive highly effective in improving lithium-ion battery performance, highlights the importance in preserving the surface properties of cathode materials, and provides new insights on the working mechanism of electrolyte additives.« less

XRD and FTIR analysis heat treated lithium bismo-borate glasses doped with 1.0 mol% copper ferrite

NASA Astrophysics Data System (ADS)

Yadav, Arti; Narwal, P.; Dahiya, Manjeet S.; Dahiya, T.; Agarwal, A.; Khasa, S.

2018-05-01

Glasses of compositions of 20Li20 • xBi2O3• (79-x)B2O3 + (1.0 mol%) CuFe2O4, with 0 ≤ x ≤ 40 were prepared by melt-quench technique. To obtain the glass-ceramics the controlled heat treatment were given to the prepared glasses. Two nano crystalline phases, i.e., Li2B4O7 and LiB3O5 were observed from X-ray diffraction patterns of the prepared glass- ceramic samples. We investigated the change in coordination number of network formers B2O3 and Bi2O3 and network modifiers Bi2O3, Li2O and CuFe2O4. Crystallites size (lies in range ˜47-50nm) and lattice strain (ɛ) were calculated for major phases for all prepared samples. FT-IR study revealed the de-polymerization of borate groups that change with heat treatment and Bi2O3 content. Deconvolution of IR absorption spectra resolves the overlapped and hidden peaks in IR spectra. Sharp and more intense FTIR peaks confirm the vibrations due to crystallites Li2B4O7 and LiB3O5 and change in coordination of network forming borate units.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tang, Wan Si; Dimitrievska, Mirjana; Stavila, Vitalie

The salt compounds NaB 11H 14, Na-7-CB10H13, Li-7-CB 10H 13, Na-7,8-C 2B 9H 12, and Na-7,9-C 2B 9H 12 all contain geometrically similar, monocharged, nido-undeca(carba)borate anions (i.e., truncated icosohedral-shaped clusters constructed of only 11 instead of 12 {B-H} + {C-H} vertices and an additional number of compensating bridging and/or terminal H atoms). We used first-principles calculations, X-ray powder diffraction, differential scanning calorimetry, neutron vibrational spectroscopy, neutron elastic-scattering fixed-window scans, quasielastic neutron scattering, and electrochemical impedance measurements to investigate their structures, bonding potentials, phase-transition behaviors, anion orientational mobilities, and ionic conductivities compared to those of their closo-poly(carba)borate cousins. All exhibited order-disordermore » phase transitions somewhere between room temperature and 375 K. All disordered phases appear to possess highly reorientationally mobile anions (> ~10 10 jumps s -1 above 300 K) and cation-vacancy-rich, close-packed or body-center-cubic-packed structures [like previously investigated closo-poly(carba)borates]. Moreover, all disordered phases display superionic conductivities but with generally somewhat lower values compared to those for the related sodium and lithium salts with similar monocharged 1-CB 9H 10- and CB 11H 12- closo-carbaborate anions. This study significantly expands the known toolkit of solid-state, poly(carba)borate-based salts capable of superionic conductivities and provides valuable insights into the effect of crystal lattice, unit cell volume, number of carbon atoms incorporated into the anion, and charge polarization on ionic conductivity.« less

High temperature ultrasonic transducers for the generation of guided waves for non-destructive evaluation of pipes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sinding, K.; Searfass, C.; Malarich, N.

2014-02-18

Applications for non-destructive evaluation and structural health monitoring of steam generators require ultrasonic transducers capable of withstanding the high temperatures of the pipes and heat exchangers. These applications require a strong coupling of the transducer to the heat exchanger’s complex geometry at the elevated temperatures. Our objective is to use spray-on piezo-electrics for depositing comb transducers onto the curved surfaces. This paper shows results for composite transducers such as lead zirconate titanate/ bismuth titanate and bismuth titanate/ lithium niobate. The comb transducers were prepared by precision laser ablation. The feasibility of producing second harmonic waves in rods with these spay-onmore » comb transducers was demonstrated and paves the way toward measuring material degradation early-on before crack initiation occurs.« less

Spectroscopic investigations of Nd3+ doped Lithium Lead Alumino Borate glasses for 1.06 μm laser applications

NASA Astrophysics Data System (ADS)

Deopa, Nisha; Rao, A. S.; Gupta, Mohini; Vijaya Prakash, G.

2018-01-01

Neodymium doped lithium lead alumino borate glasses were synthesized with the molar composition 10Li2Osbnd 10PbOsbnd (10-x) Al2O3sbnd 70B2O3sbnd x Nd2O3 (where, x = 0.1, 0.5, 1.0, 1.5, 2.0 and 2.5 mol %) via conventional melt quenching technique to understand their lasing potentialities using the absorption, emission and photoluminescence decay spectral measurements. The oscillator strengths measured from the absorption spectra were used to estimate the Judd-Ofelt intensity parameters using least square fitting procedure. The emission spectra recorded for the as-prepared glasses under investigation exhibit two emission transitions 4F3/2 → 4I11/2 (1063 nm) and 4F3/2 → 4I9/2 (1350 nm) for which radiative parameters have been evaluated. The emission intensity increases with increase in Nd3+ ion concentration up to 1 mol % and beyond concentration quenching took place. The decay profile shows single exponential nature for lower Nd3+ ion concentration and non-exponential for higher concentration. To elucidate the nature of energy transfer process, the non-exponential decay curves were well fitted to Inokuti-Hirayama model. The relatively higher values of emission cross-sections, branching ratios and quantum efficiency values obtained for 1.0 mol% of Nd3+ ions in LiPbAlB glass suggests it's aptness in generating lasing action at 1063 nm in NIR region.

Bismuth chalcogenide compounds Bi 2 × 3 (X=O, S, Se): Applications in electrochemical energy storage

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ni, Jiangfeng; Bi, Xuanxuan; Jiang, Yu

2017-04-01

Bismuth chalcogenides Bi2×3 (X=O, S, Se) represent a unique type of materials in diverse polymorphs and configurations. Multiple intrinsic features of Bi2×3 such as narrow bandgap, ion conductivity, and environmental friendliness, have render them attractive materials for a wide array of energy applications. In particular, their rich structural voids and the alloying capability of Bi enable the chalcogenides to be alternative electrodes for energy storage such as hydrogen (H), lithium (Li), sodium (Na) storage and supercapacitors. However, the low conductivity and poor electrochemical cycling are two key challenges for the practical utilization of Bi2×3 electrodes. Great efforts have been devotedmore » to mitigate these challenges and remarkable progresses have been achieved, mainly taking profit of nanotechnology and material compositing engineering. In this short review, we summarize state-of-the-art research advances in the rational design of diverse Bi2×3 electrodes and their electrochemical energy storage performance for H, Li, and Na and supercapacitors. We also highlight the key technical issues at present and provide insights for the future development of bismuth based materials in electrochemical energy storage devices.« less

Physical, structural and optical characterizations of borate modified bismuth-silicate-tellurite glasses

NASA Astrophysics Data System (ADS)

Berwal, Neelam; Kundu, R. S.; Nanda, Kirti; Punia, R.; Kishore, N.

2015-10-01

Quaternary bismuthate glasses with compositions xB2O3-(80 - x) Bi2O3-15SiO2-5TeO2 have been prepared by melt-quench technique. X-ray diffraction studies were performed to ascertain the amorphous nature of samples. The density, molar volume and crystalline volume decrease with increase in B2O3 content whereas the glass transition temperature shows the reverse trend. The Raman and FTIR spectra of the studied glasses indicate that B2O3 has been found to exist in the form of BO3 trigonal and BO4 tetrahedral structural units and vibrations corresponding to these structural units increase with increase in B2O3 content. SiO2 is present in the form of SiO4 tetrahedral structural units and TeO2 in the form of TeO3 structural units. Bismuth plays the role of network modifier [BiO6 octahedra] as well as network former [BiO3 pyramids] for all the glass compositions. The optical band gap energy has been calculated from the fitting of both Mott and Davis's model and Hydrogenic excitonic model with the experimentally observed absorption spectra. A good fitting of experimental data with HEM indicates the excitonic formation in the studies glass system. The values of optical band gap energy show nonlinear behavior due to the structural changes that take place in the present glass samples. The Urbach energy calculated using Urbach empirical formula for studied glass samples suggest the possibility of reduction in defect concentrations. The metallization criterion of the presently studied samples suggests that the prepared glasses may be potential candidates for nonlinear optical applications.

Oligo(ethylene glycol)-functionalized disiloxanes as electrolytes for lithium-ion batteries

NASA Astrophysics Data System (ADS)

Zhang, Zhengcheng; Dong, Jian; West, Robert; Amine, Khalil

Functionalized disiloxane compounds were synthesized by attaching oligo(ethylene glycol) chains, -(CH 2CH 2O)- n, n = 2-7, via hydrosilation, dehydrocoupling, and nucleophilic substitution reactions and were examined as non-aqueous electrolyte solvents in lithium-ion cells. The compounds were fully characterized by 1H, 13C, and 29Si nuclear magnetic resonance (NMR) spectroscopy. Upon doping with lithium bis(oxalato)borate (LiBOB) or LiPF 6, the disiloxane electrolytes showed conductivities up to 6.2 × 10 -4 S cm -1 at room temperature. The thermal behavior of the electrolytes was studied by differential scanning calorimetry, which revealed very low glass transition temperatures before and after LiBOB doping and much higher thermal stability compared to organic carbonate electrolytes. Cyclic voltammetry measurements showed that disiloxane-based electrolytes with 0.8 M LiBOB salt concentration are stable to 4.7 V. The LiBOB/disiloxane combinations were found to be good electrolytes for lithium-ion cells; unlike LiPF 6, LiBOB can provide a good passivation film on the graphite anode. The LiPF 6/disiloxane electrolyte was enabled in lithium-ion cells by adding 1 wt% vinyl ethylene carbonate (VEC). Full cell performance tests with LiNi 0.80Co 0.15Al 0.05O 2 as the cathode and mesocarbon microbead (MCMB) graphite as the anode show stable cyclability. The results demonstrate that disiloxane-based electrolytes have considerable potential as electrolytes for use in lithium-ion batteries.

Chemical stability of Lithium 2-trifluoromethyl-4,5-dicyanoimidazolide, an electrolyte salt for Li-ion cells

DOE PAGES

Shkrob, Ilya A.; Pupek, Krzysztof Z.; Gilbert, James A.; ...

2016-12-01

Lithium hexafluorophosphate (LiPF 6) is ubiquitous in commercial lithium-ion batteries, but it is hydrolytically unstable and corrosive on electrode surfaces. Using a more stable salt would confer multiple benefits for high-voltage operation, but many such electrolyte systems facilitate anodic dissolution and pitting corrosion of aluminum current collectors that negate their advantages. Lithium 2-trifluoromethyl-4,5-dicyanoimidazolide (LiTDI) is a new salt that was designed specifically for high-voltage cells. In this study we demonstrate that in carbonate electrolytes, LiTDI prevents anodic dissolution of Al current collectors, which places it into a select group of corrosion inhibitors. However, we also demonstrate that LiTDI becomes reducedmore » on lithiated graphite, undergoing sequential defluorination and yielding a thick and resistive solid-electrolyte interphase (SEI), which increases impedance and lowers electrode capacity. The mechanistic causes for this behavior are examined using computational chemistry methods in the light of recent spectroscopic studies. Here, we demonstrate that LiTDI reduction can be prevented by certain electrolyte additives, which include fluoroethylene carbonate, vinylene carbonate and lithium bis(oxalato)borate. This beneficial action is due to preferential reduction of these additives over LiTDI at a higher potential vs. Li/Li +, so the resulting SEI can prevent the direct reduction of LiTDI at lower potentials on the graphite electrode.« less

Preparation and properties of porous microspheres made from borate glass.

PubMed

Conzone, Samuel D; Day, Delbert E

2009-02-01

Dysprosium lithium-borate glass microspheres and particles, ranging from 45 to 150 microm in diameter, were reacted with a 0.25 M phosphate solution at 37 degrees C, whose pH was either 3 or 8.8. The glass reacted nonuniformly and was converted into a porous, amorphous, hydrated, dysprosium phosphate reaction product. The amorphous product had the same volume and shape (pseudomorphic) as the unreacted glass, and could be dried without cracking. After heating at 300 degrees C for 1 h, the amorphous reaction product had a specific surface area of approximately 200 m(2)/g, a pore size of approximately 30 nm, and nominal crushing strength of approximately 10 MPa. When the reaction product was heated to 600 degrees C for 15 min, the specific surface area decreased to approximately 90 m(2)/g and the nominal crushing strength increased to 35 MPa. Heating above 615 degrees C converted the amorphous dysprosium phosphate product into crystalline DyPO(4), which contained open porosity until heated above 800 degrees C for 15 min. Highly porous materials of different chemical composition can be prepared by chemically reacting a borate-based glass with an aqueous solution at low-temperature (<100 degrees C). These highly porous materials are easy to process, and are considered candidates for controlled drug delivery, catalysis, chromatographic separation, filtration, and as bioactive materials.

Using neutrons, X-rays and nuclear magnetism to determine the role of transition metal oxide inclusions on both glass structure and stability in automotive glass enamels.

PubMed

Bowron, Daniel T; Booth, Jonathan; Barrow, Nathan S; Sutton, Patricia; Johnson, Simon R

2018-05-23

Low levels of transition metal oxides in alkali borosilicate glass systems can drastically influence crystallisation and phase separation properties. We investigated the non-monotonic effect of manganese doping on suppressing crystallisation, and the influence on optical properties by iron oxide doping, in terms of local atomic structure. Structural models based on empirical potential structure refinement were generated from neutron and X-ray scattering data, and compared against multinuclear solid-state NMR. This revealed that a 2.5% manganese doping had a disruptive effect on the entire glass network, supressing crystallisation of an undesired bismuth silicate phase, and that iron species preferentially locate near borate tetrahedra. Preventing phase separation and controlling crystallisation behaviour of glass are critical to the ultimate properties of automotive glass enamels.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shkrob, Ilya A.; Pupek, Krzysztof Z.; Gilbert, James A.

Lithium hexafluorophosphate (LiPF 6) is ubiquitous in commercial lithium-ion batteries, but it is hydrolytically unstable and corrosive on electrode surfaces. Using a more stable salt would confer multiple benefits for high-voltage operation, but many such electrolyte systems facilitate anodic dissolution and pitting corrosion of aluminum current collectors that negate their advantages. Lithium 2-trifluoromethyl-4,5-dicyanoimidazolide (LiTDI) is a new salt that was designed specifically for high-voltage cells. In this study we demonstrate that in carbonate electrolytes, LiTDI prevents anodic dissolution of Al current collectors, which places it into a select group of corrosion inhibitors. However, we also demonstrate that LiTDI becomes reducedmore » on lithiated graphite, undergoing sequential defluorination and yielding a thick and resistive solid-electrolyte interphase (SEI), which increases impedance and lowers electrode capacity. The mechanistic causes for this behavior are examined using computational chemistry methods in the light of recent spectroscopic studies. Here, we demonstrate that LiTDI reduction can be prevented by certain electrolyte additives, which include fluoroethylene carbonate, vinylene carbonate and lithium bis(oxalato)borate. This beneficial action is due to preferential reduction of these additives over LiTDI at a higher potential vs. Li/Li +, so the resulting SEI can prevent the direct reduction of LiTDI at lower potentials on the graphite electrode.« less

Mechanistic Study of Electrolyte Additives to Stabilize High-Voltage Cathode-Electrolyte Interface in Lithium-Ion Batteries.

PubMed

Gao, Han; Maglia, Filippo; Lamp, Peter; Amine, Khalil; Chen, Zonghai

2017-12-27

Current developments of electrolyte additives to stabilize electrode-electrolyte interface in lithium-ion batteries highly rely on a trial-and-error search, which involves repetitive testing and intensive amount of resources. The lack of understandings on the fundamental protection mechanisms of the additives significantly increases the difficulty for the transformational development of new additives. In this study, we investigated two types of individual protection routes to build a robust cathode-electrolyte interphase at high potentials: (i) a direct reduction in the catalytic decomposition of the electrolyte solvent; and (ii) formation of a "corrosion inhibitor film" that prevents severely attack and passivation from protons that generated from the solvent oxidation, even the decomposition of solvent cannot be mitigated. Effect of two exemplary electrolyte additives, lithium difluoro(oxalato)borate (LiDFOB) and 3-hexylthiophene (3HT), on LiNi 0.6 Mn 0.2 Co 0.2 O 2 (NMC 622) cathode were investigated to validate our hypothesis. It is demonstrated that understandings of both electrolyte additives and solvent are essential and careful balance between the cathode protection mechanism of additives and their side effects is critical to obtain optimum results. More importantly, this study opens up new directions of rational design of functional electrolyte additives for the next-generation high-energy-density lithium-ion chemistries.

Polyfluorinated boron cluster based salts: A new electrolyte for application in nonaqueous asymmetric AC/Li 4Ti 5O 12 supercapacitors

NASA Astrophysics Data System (ADS)

Ionica-Bousquet, C. M.; Muñoz-Rojas, D.; Casteel, W. J.; Pearlstein, R. M.; Kumar, G. Girish; Pez, G. P.; Palacín, M. R.

Solutions of novel fluorinated lithium dodecaborate (Li 2B 12F xH 12- x) salts have been evaluated as electrolytes in nonaqueous asymmetric supercapacitors with Li 4Ti 5O 12 as negative electrode, and activated carbon (AC) as positive electrode. The results obtained with these new electrolytes were compared with those obtained with cells built using standard 1 M LiPF 6 dissolved in ethylene carbonate and dimethyl carbonate (EC:DMC; 1:1, v/v) as electrolyte. The specific energy, rate capability, and cycling performances of nonaqueous asymmetric cells based on these new electrolyte salts were studied. Cells assembled using the new fluoroborate salts show excellent reversibility, coulombic efficiency, rate capability and improved cyclability when compared with the standard electrolyte. These features confirm the suitability of lithium-fluoro-borate based salts to be used in nonaqueous asymmetric supercapacitors.

Four-time 7Li stimulated-echo spectroscopy for the study of dynamic heterogeneities: Application to lithium borate glass.

PubMed

Storek, M; Tilly, J F; Jeffrey, K R; Böhmer, R

2017-09-01

To study the nature of the nonexponential ionic hopping in solids a pulse sequence was developed that yields four-time stimulated-echo functions of previously inaccessible spin-3/2-nuclei such as 7 Li. It exploits combined Zeeman and octupolar order as longitudinal carrier state. Higher-order correlation functions were successfully generated for natural-abundance and isotopically-enriched lithium diborate glasses. Four-time 7 Li measurements are presented and compared with two-time correlation functions. The results are discussed with reference to approaches devised to quantify the degree of nonexponentiality in glass forming systems and evidence for the occurrence of dynamic heterogeneities and dynamic exchange were found. Additional experiments using the 6 Li species illustrate the challenge posed by subensemble selection when the dipolar interactions are not very much smaller than the quadrupolar ones. Copyright © 2017 Elsevier Inc. All rights reserved.

Diffraction imaging (topography) with monochromatic synchrotron radiation

NASA Technical Reports Server (NTRS)

Steiner, Bruce; Kuriyama, Masao; Dobbyn, Ronald C.; Laor, Uri

1988-01-01

Structural information of special interest to crystal growers and device physicists is now available from high resolution monochromatic synchrotron diffraction imaging (topography). In the review, the importance of superior resolution in momentum transfer and in space is described, and illustrations are taken from a variety of crystals: gallium arsenide, cadmium telluride, mercuric iodide, bismuth silicon oxide, and lithium niobate. The identification and understanding of local variations in crystal growth processes are shown. Finally, new experimental opportunities now available for exploitation are indicated.

X-Ray Absorption Spectroscopy Studies of the Atomic Structure of Zirconium-Doped Lithium Silicate Glasses and Glass-Ceramics, Zirconium-Doped Lithium Borate Glasses, and Vitreous Rare-Earth Phosphates

NASA Astrophysics Data System (ADS)

Yoo, Changhyeon

In the first part of this work, the atomic-scale structure around rare-earth (RE = Pr, Nd, Eu, Dy, and Er) cations (RE3+) in rare-earth sodium ultraphosphate (REUP) glasses were investigated using RE LIII -edge (RE = Nd, Er, Dy, and Eu) and K-edge (RE = Pr and Dy) Extended X-ray Absorption Fine Structure (EXAFS) spectroscopy. (RE2O 3)x(Na2O)y(P2O5) 1-x-y glasses in the compositional range 0 ≤ x ≤ 0.14 and 0.3 ≤ x + y ≤ 0.4 were studied. For the nearest oxygen shell, the RE-oxygen (RE-O) coordination number decreases from 10.8 to 6.5 with increasing RE content for Pr-, Nd-, Dy-, and Er-doped sodium ultraphosphate glasses. For Eu-doped samples, the Eu-O coordination number was between 7.5 and 8.8. Also, the RE-O mean distance ranges were between 2.43-2.45 A, 2.40-2.43 A, 2.36-2.38 A, 2.30-2.35 A, and 2.28-2.30 A for Pr-, Nd-, Eu-, Dy-, and Er-doped samples, respectively. In the second part, a series of Zr-doped (3-10 mol%) lithium silicate (ZRLS) glass-ceramics and their parent glasses and a series of Zr-doped (2-6 mol% ZrO2) lithium borate (ZRLB) glasses were investigated using Zr K-edge EXAFS and X-ray Absorption Near Edge Structure (XANES) spectroscopy. Immediate coordination environments of all ZRLS glasses are remarkably similar for different compositions. For the nearest oxygen shell, the Zr-O coordination number ranges were between 6.1 and 6.3 for nucleated and crystallized samples, respectively. Also, the Zr-O mean distance remains similar around 2.10 A. For these glasses, the composition dependence of structural parameters was small. Small changes in the coordination environment were observed for ZRLS glass-ceramics after thermal treatments. In contrast, Zr coordination environment in ZRLB glasses appear to depend appreciably on the Zr concentration. For the nearest oxygen shell, the Zr-O coordination number increased from 6.1 to 6.8 and the Zr-O distance decreased from 2.18 A to 2.14 A with decreasing ZrO2 content.

Solid state neutron detector and method for use

DOEpatents

Doty, F. Patrick; Zwieback, Ilya; Ruderman, Warren

2002-01-01

Crystals of lithium tetraborate or alpha-barium borate had been found to be neutron detecting materials. The crystals are prepared using known crystal growing techniques, wherein the process does not include the common practice of using a fluxing agent, such as sodium oxide or sodium fluoride, to reduce the melting temperature of the crystalline compound. Crystals prepared by this method can be sliced into thin single or polycrystalline wafers, or ground to a powder and prepared as a sintered compact or a print paste, and then configured with appropriate electronic hardware, in order to function as neutron detectors.

Effect of different conventional melt quenching technique on purity of lithium niobate (LiNbO3) nano crystal phase formed in lithium borate glass

NASA Astrophysics Data System (ADS)

Kashif, Ismail; Soliman, Ashia A.; Sakr, Elham M.; Ratep, Asmaa

2012-01-01

The glass system (45Li2O + 45B2O3 + 10Nb2O5) was fabricated by the conventional melt quenching technique poured in water, at air, between two hot plates and droplets at the cooled surface. The glass and glass ceramics were studied by differential thermal analysis (DTA) and X-ray diffraction (XRD). The as quenched samples poured in water and between two hot plates were amorphous. The samples poured at air and on cooled surface were crystalline as established via X-ray powder diffraction (XRD) studies. Differential thermal analysis was measured. The glass transition temperature (Tg) and the crystallization temperatures were calculated. Lithium niobate (LiNbO3) was the main phase in glass ceramic poured at air, droplets at the cooled surface and the heat treated glass sample at 500, 540 and 580 °C in addition to traces from LiNb3O8. Crystallite size of the main phases determined from the X-ray diffraction peaks is in the range of <100 nm. The fraction of crystalline (LiNbO3) phase decreases with increase in the heat treatment temperature.

Spectroscopic studies of Sm3+ ions activated lithium lead alumino borate glasses for visible luminescent device applications

NASA Astrophysics Data System (ADS)

Deopa, Nisha; Rao, A. S.

2017-10-01

Photoluminescence (PL) characterization of Lithium Lead Alumino Borate (LiPbAlB) glasses doped with Sm3+ ions at varying concentrations have been studied by using absorption, excitation, emission, time resolved and confocal image measurements. From the absorption spectra, Judd-Ofelt (J-O) intensity parameters were evaluated and in turn used to estimate various radiative parameters for the fluorescent levels of Sm3+ ion doped LiPbAlB glasses. The PL spectra of Sm3+ ions exhibit three emission bands corresponding to the transitions 4G5/2 → 6H5/2, 6H7/2 and 6H9/2, for which the emission cross-sections and branching ratios were evaluated to know the potentialities of these materials as visible luminescent devices. The decay spectral profiles measured for 4G5/2 → 6H7/2 transition level were used to estimate quantum efficiency of the as-prepared glasses. The non-exponential decay curves observed for higher Sm3+ ion concentrations were well fitted to Inokuti-Hirayama model to understand the predominant energy transfer mechanism involved in the as-prepared glasses. CIE chromaticity coordinates and correlated color temperatures (CCT) were evaluated to understand the utility of the titled glasses in cool white light generation. The confocal images captured under 405 nm CW laser excitation show intense reddish-orange color. From the evaluated radiative parameters, emission cross-sections, quantum efficiency, CIE co-ordinates, CCT temperatures and confocal images, it was observed that LiPbAlB glass with 0.5 mol% Sm3+ ions are more suitable for w-LEDs and reddish-orange luminescent device applications.

Effect of pyrophosphate ions on the conversion of calcium-lithium-borate glass to hydroxyapatite in aqueous phosphate solution.

PubMed

Fu, Hailuo; Rahaman, Mohamed N; Day, Delbert E; Huang, Wenhai

2010-10-01

The conversion of glass to a hydroxyapatite (HA) material in an aqueous phosphate solution is used as an indication of the bioactive potential of the glass, as well as a low temperature route for preparing biologically useful materials. In this work, the effect of varying concentrations of pyrophosphate ions in the phosphate solution on the conversion of a calcium-lithium-borate glass to HA was investigated. Particles of the glass (150-355 μm) were immersed for up to 28 days in 0.25 M K(2)HPO(4) solution containing 0-0.1 M K(4)P(2)O(7). The kinetics of degradation of the glass particles and their conversion to HA were monitored by measuring the weight loss of the particles and the ionic concentration of the solution. The structure and composition of the conversion products were analyzed using X-ray diffraction, scanning electron microscopy, and Fourier transform infrared spectroscopy. For K(4)P(2)O(7) concentrations of up to 0.01 M, the glass particles converted to HA, but the time for complete conversion increased from 2 days (no K(4)P(2)O(7)) to 10 days (0.01 M K(4)P(2)O(7)). When the K(4)P(2)O(7) concentration was increased to 0.1 M, the product consisted of an amorphous calcium phosphate material, which eventually crystallized to a pyrophosphate product (predominantly K(2)CaP(2)O(7) and Ca(2)P(2)O(7)). The consequences of the results for the formation of HA materials and devices by the glass conversion route are discussed.

Infrared and Raman spectroscopic studies on alkali borate glasses: evidence of mixed alkali effect.

PubMed

Padmaja, G; Kistaiah, P

2009-03-19

A lithium-potassium-borate glass system containing manganese and iron cations has been thoroughly investigated in order to obtain information about the mixed alkali effect and the structural role of both the manganese and iron in such glass hosts. Mixed alkali borate glasses of the (30 - x)Li(2)O - xK(2)O - 10CdO/ZnO - 59B(2)O(3) (x = 0, 10, 15, 20, and 30) doped with 1MnO(2)/1Fe(2)O(3) system were prepared by a melt quench technique. The amorphous phase of the prepared glass samples was confirmed from their X-ray diffraction. The spectroscopic properties of glass samples were studied using infrared (IR) and Raman spectroscopic techniques. The density of all the prepared glasses was measured using Archimedes principle. Molar volumes were estimated from the density data. IR spectra of these glasses revealed a dramatic variation of three- and four-coordinated boron structures as a function of mixed alkali concentration. The vibrations due to Li-O, K-O, and MnO(4)/FeO(4) arrangements are consistent in all the compositions and show a nonlinear variation in the intensity with alkali content. Raman spectra of different alkali combinations with CdO and ZnO present drastic changes in the intensity of various Raman bands. The observation of disappearance and reappearance of IR and Raman bands as a function of various alkali concentrations is an important result pertaining to the mixed alkali effect in borate glasses. Acting as complementary spectroscopic techniques, both types of measurements, IR and Raman, revealed that the network structure of the studied glasses is mainly based on BO(3) and BO(4) units placed in different structural groups, the BO(3) units being dominant. The measured IR and Raman spectra of different glasses are used to clarify the optical properties of the present glasses correlating them with their structure and composition.

Enhanced charging capability of lithium metal batteries based on lithium bis(trifluoromethanesulfonyl)imide-lithium bis(oxalato)borate dual-salt electrolytes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xiang, Hongfa; Shi, Pengcheng; Bhattacharya, Priyanka

2016-06-01

Rechargeable lithium (Li) metal batteries with conventional LiPF6-carbonate electrolytes have been reported to fail quickly at charging current densities of about 1.0 mA cm-2 and above. In this work, we demonstrate the rapid charging capability of the Li||LiNi0.8Co0.15Al0.05O2 (NCA) cells enabled by a dual-salt electrolyte of LiTFSI-LiBOB in a carbonate solvent mixture. It is found that the thickness of solid electrolyte interphase (SEI) layer on Li metal anode largely increases with increasing charging current density. However, the cells using the LiTFSI-LiBOB dual-salt electrolyte significantly outperforms those using the LiPF6 electrolyte at high charging current densities. At the charging current densitymore » of 1.50 mA cm-2, the Li||NCA cells with the dual-salt electrolyte can still deliver a discharge capacity of 131 mAh g-1 and a capacity retention of 80% after 100 cycles, while those with the LiPF6 electrolyte start to show fast capacity fading after the 30th cycle and only exhibit a low capacity of 25 mAh g-1 and a low retention of 15% after 100 cycles. The reasons for the good chargeability and cycling stability of the cells using LiTFSI-LiBOB dual-salt electrolyte can be attributed to the good film-formation ability of the electrolyte on lithium metal anode and the highly conductive nature of the sulfur-rich interphase layer.« less

Single crystal substrates for surface acoustic wave devices

NASA Astrophysics Data System (ADS)

Barsch, G. R.; Spear, K. E.

1981-01-01

In order to search for new temperature compensated materials for surface acoustic wave (SAW) devices with low ultrasonic attenuation and high electromechanical coupling, the following experimental and theoretical investigations were carried out: (1) Crystal growth research centered around: designing, constructing, and writing the software for a computer controlled constant-diameter attachment for our Czochralski crystal pullers; a major experimental effort on the growth of lead potassium niobate (PKN); Pb2KNb5O15, and lead bismuth niobate (PBN) PbBi2Nb2O9, and a minor experimental effort on the growth of lithium metasilicate, Li2SiO3; and bismuth molybdate, Bi2MoO6. (2) The dielectric constants and the associated loss tangents of alpha-berlinite were measured at eleven frequencies from 100 to 10,000 Hz between -150 and 200 C. The temperature dependence of the dielectric constants and the relaxation behavior are similar to the results obtained earlier, but the absolute values are 20 to 30 percent smaller than reported previously. (3) The temperature dependence of the two shear modes propagating in (001) has been measured from 10 to 315K for Bi4Ti3O12. A monotonical decrease of the associated shear moduli has been found. (4) Considerable effort was devoted to specimen preparation of lead bismuth niobate which was hampered by the easy cleavage of this material perpendicular to 001 .

Electrochemical behavior of Al in a non-aqueous alkyl carbonate solution containing LiBOB salt

NASA Astrophysics Data System (ADS)

Myung, Seung-Taek; Natsui, Hiroshi; Sun, Yang-Kook; Yashiro, Hitoshi

Aluminum was studied as a current collector for rechargeable lithium batteries to understand electrochemical and passivation behavior. Electrochemical polarization tests, in situ scratch polarization tests and time-of-flight secondary ion mass spectroscopy (ToF-SIMS) analysis in lithium bis-oxalato borate (LiBOB)-containing alkyl carbonate solution were conducted. The Al foil did not follow the alloy and de-alloy process with the LiBOB salt in electrolyte at 0 V vs. Li/Li + in the cathodic sweep. During the anodic scan to the noble direction, the absence of an oxidation peak up to 3 V vs. Li/Li + indicated that the air-formed oxide layer of Al was not reduced to metal. Oxide-free Al surfaces made by the in situ scratch test during the electrochemical polarization resulted in abrupt alloy formation with Li at 0 V vs. Li/Li +, but the newly formed surface formed passive films at higher potential with oxygen, namely, Al-O compound, as confirmed by ToF-SIMS.

Stabilizing Superionic-Conducting Structures via Mixed-Anion Solid Solutions of Monocarba- closo -borate Salts

DOE PAGES

Tang, Wan Si; Yoshida, Koji; Soloninin, Alexei V.; ...

2016-09-01

Solid lithium and sodium closo-polyborate-based salts are capable of superionic conductivities surpassing even liquid electrolytes, but often only at above-ambient temperatures where their entropically driven disordered phases become stabilized. Here we show by X-ray diffraction, quasielastic neutron scattering, differential scanning calorimetry, NMR, and AC impedance measurements that by introducing 'geometric frustration' via the mixing of two different closo-polyborate anions, namely, 1-CB 9H 10- and CB 11H 12-, to form solid-solution anion-alloy salts of lithium or sodium, we can successfully suppress the formation of possible ordered phases in favor of disordered, fast-ion-conducting alloy phases over a broad temperature range from subambientmore » to high temperatures. Finally, this result exemplifies an important advancement for further improving on the remarkable conductive properties generally displayed by this class of materials and represents a practical strategy for creating tailored, ambient-temperature, solid, superionic conductors for a variety of upcoming all-solid-state energy devices of the future.« less

A new solution chemical method to make low dimensional thermoelectric materials

NASA Astrophysics Data System (ADS)

Ding, Zhongfen

2001-11-01

Bismuth telluride and its alloys are currently the best thermoelectric materials known at room temperature and are therefore used for portable solid-state refrigeration. If the thermal electric figure of merit ZT could be improved by a factor of about 3, quiet and rugged solid-state devices could eventually replace conventional compressor based cooling systems. In order to test a theory that improved one-dimensional or two-dimensional materials could enhance ZT due to lower thermal conductivity, we are developing solution processing methods to make low dimensional materials. Bismuth telluride and its p-type and n-type alloys have layered structures consisting of 5 atom thick Te-Bi-Te-Bi-Te sheets, each sheet about 10 A thick. Lithium ions are intercalated into the layered materials using liquid ammonia. The lithium-intercalated materials are then exfoliated in water to form colloidal suspensions with narrow particle size distributions and are stable for more than 24 hours. The layers are then deposited on substrates, which after annealing at low temperatures, form highly c-axis oriented thin films. The exfoliated layers can potentially be restacked with other ions or layered materials in between the sheets to form novel structures. The restacked layers when treated with nitric acid and sonication form high yield nanorod structured materials. This new intercalation and exfoliation followed by sonication method could potentially be used for many other layered materials to make nanorod structured materials. The low dimensional materials are characterized by powder X-ray diffraction, atomic force microscopy (AFM), transmission electron microscopy (TEM), scanning electron microscopy (SEM), inductively coupled plasma (ICP) and dynamic light scattering.

Atom probe tomography of lithium-doped network glasses.

PubMed

Greiwe, Gerd-Hendrik; Balogh, Zoltan; Schmitz, Guido

2014-06-01

Li-doped silicate and borate glasses are electronically insulating, but provide considerable ionic conductivity. Under measurement conditions of laser-assisted atom probe tomography, mobile Li ions are redistributed in response to high electric fields. In consequence, the direct interpretation of measured composition profiles is prevented. It is demonstrated that composition profiles are nevertheless well understood by a complex model taking into account the electronic structure of dielectric materials, ionic mobility and field screening. Quantitative data on band bending and field penetration during measurement are derived which are important in understanding laser-assisted atom probe tomography of dielectric materials. Copyright © 2014 Elsevier B.V. All rights reserved.

Efficient second to ninth harmonic generation using megawatt peak power microchip laser.

PubMed

Bhandari, R; Tsuji, N; Suzuki, T; Nishifuji, M; Taira, T

2013-11-18

We report the design and use of a megawatt peak power Nd:YAG/Cr4+:YAG microchip laser for efficient second to ninth harmonic generation. We show that the sub-nanosecond pulse width region, between 100 ps and 1 ns, is ideally suited for efficient wavelength conversion. Using this feature, we report 85% second harmonic generation efficiency using lithium triborate (LBO), 60% fourth harmonic generation efficiency usingß-barium borate, and 44% IR to UV third harmonic generation efficiency using Type I and Type II LBO. Finally, we report the first demonstration of 118 nm VUV generation in xenon gas using a microchip laser.

Synthesis and optical properties of polycrystalline Li2Al2B2O7 (LABO)

NASA Astrophysics Data System (ADS)

Dagdale, S. R.; Muley, G. G.

2016-05-01

A polycrystalline lithium aluminum borate (Li2Al2B2O7, LABO) has been synthesized by using simple solid-state technique. The obtained LABO polycrystalline was characterized by powder X-ray diffraction; Fourier transform infrared (FT-IR) spectroscopy and second harmonic generation (SHG) efficiency measurement. The functional groups were identified using the FT-IR spectroscopic data. The SHG efficiency of the polycrystalline material was obtained by the classic Kurtz powder technique using a fundamental wavelength 1064 nm of Nd:YAG laser and it is found to be 1.4 times that of potassium dihydrogen phosphate (KDP).

Lithium Sensitivity of Store Operated Ca2+ Entry and Survival of Fibroblasts Isolated from Chorea-Acanthocytosis Patients.

PubMed

Pelzl, Lisann; Elsir, Bhaeldin; Sahu, Itishri; Bissinger, Rosi; Singh, Yogesh; Sukkar, Basma; Honisch, Sabina; Schoels, Ludger; Jemaà, Mohamed; Lang, Elisabeth; Storch, Alexander; Hermann, Andreas; Stournaras, Christos; Lang, Florian

2017-01-01

The widely expressed protein chorein fosters activation of the phosphoinositide 3 kinase (PI3K) pathway thus supporting cell survival. Loss of function mutations of the chorein encoding gene VPS13A (vacuolar protein sorting-associated protein 13A) causes chorea-acanthocytosis (ChAc), a neurodegenerative disorder paralleled by deformations of erythrocytes. In mice, genetic knockout of chorein leads to enhanced neuronal apoptosis. PI3K dependent signalling upregulates Orai1, a pore forming channel protein accomplishing store operated Ca2+ entry (SOCE). Increased Orai1 expression and SOCE have been shown to confer survival of tumor cells. SOCE could be up-regulated by lithium. The present study explored, whether SOCE and/or apoptosis are altered in ChAc fibroblasts and could be modified by lithium treatment. Fibroblasts were isolated from ChAc patients and age-matched healthy volunteers. Cytosolic Ca2+ activity ([Ca2+]i) was estimated from Fura-2-fluorescence, SOCE from increase of [Ca2+]i following Ca2+ re-addition after Ca2+-store depletion with sarcoendoplasmatic Ca2+-ATPase (SERCA) inhibitor thapsigargin (1 µM), and apoptosis from annexin-V/propidium iodide staining quantified in flow cytometry. SOCE was significantly smaller in ChAc fibroblasts than in control fibroblasts. Lithium (2 mM, 24 hours) significantly increased and Orai1 blocker 2-Aminoethoxydiphenyl Borate (2-APB, 50 µM, 24 hours) significantly decreased SOCE. Annexin-V-binding and propidium iodide staining were significantly higher in ChAc fibroblasts than in control fibroblasts. In ChAc fibroblasts annexin-V-binding and propidium iodide staining were significantly decreased by lithium treatment, significantly increased by 2-APB and virtually lithium insensitive in the presence of 2-APB. In ChAc fibroblasts, downregulation of SOCE contributes to enhanced susceptibility to apoptosis. Both, decreased SOCE and enhanced apoptosis of ChAc fibroblasts can be reversed by lithium treatment. © 2017 The Author(s). Published by S. Karger AG, Basel.

Determination of elemental content off rocks by laser ablation inductively coupled plasma mass spectrometry

USGS Publications Warehouse

Lichte, F.E.

1995-01-01

A new method of analysis for rocks and soils is presented using laser ablation inductively coupled plasma mass spectrometry. It is based on a lithium borate fusion and the free-running mode of a Nd/YAG laser. An Ar/N2 sample gas improves sensitivity 7 ?? for most elements. Sixty-three elements are characterized for the fusion, and 49 elements can be quantified. Internal standards and isotopic spikes ensure accurate results. Limits of detection are 0.01 ??g/g for many trace elements. Accuracy approaches 5% for all elements. A new quality assurance procedure is presented that uses fundamental parameters to test relative response factors for the calibration.

Impedance spectroscopic characterization of Sm2O3 containing lithium borate glasses.

PubMed

Ramteke, D D; Gedam, R S

2014-12-10

27.5 Li2O-(72.5-X) B2O3-X Sm2O3 (X=0.5, 1, 1.5 and 2) were prepared by conventional melt quench technique. Impedance spectroscopy (IS) is used to study the electrical properties of these prepared glasses. Modulus formalism is introduced to study relaxation behaviour of these glasses. Scaling model shows the good overlap of data on single master curve which suggests that conduction mechanism in these glasses is compositional dependent. Variation of dielectric constant and dielectric loss with the addition of Sm2O3 and frequency are discussed here. Copyright © 2014 Elsevier B.V. All rights reserved.

Bio-inspired spider-web-like membranes with a hierarchical structure for high performance lithium/sodium ion battery electrodes: the case of 3D freestanding and binder-free bismuth/CNF anodes.

PubMed

Jin, Yuqiang; Yuan, Haocheng; Lan, Jin-Le; Yu, Yunhua; Lin, Yuan-Hua; Yang, Xiaoping

2017-09-14

High gravimetric energy density and volumetric energy density energy storage devices are highly desirable due to the rapid development of electric vehicles, and portable and wearable electronic equipment. Electrospinning is a promising technology for preparing freestanding electrodes with high gravimetric and volumetric energy density. However, the energy density of the traditional electrospun electrodes is restricted by the low mass loading of active materials (e.g. 20%-30 wt%). Herein, a biomimetic strategy inspired by the phenomenon of the sticky spider web is demonstrated as a high performance anode, which simultaneously improves the gravimetric and volumetric energy density. Freestanding carbon nanofiber (CNF) membranes containing over 50 wt% of bismuth were prepared by electrospinning and subsequent thermal treatment. Membranes consisting of CNF network structures bonded tightly with active Bi cluster materials, resulting in excellent mechanical protection and a fast charge transport path, which are difficult to achieve simultaneously. The composite membrane delivers high reversible capacity (483 mA h g -1 at 100 mA g -1 after 200 cycles) and high rate performance (242 mA h g -1 at 1 A g -1 ) as a lithium-ion battery anode. For use as a sodium ion battery, the composite membrane also shows a high reversible specific capacity of 346 mA h g -1 and outstanding cycling performance (186 mA h g -1 at 50 mA g -1 after 100 cycles). This work offers a simple, low cost and eco-friendly method for fabricating free-standing and binder-free composite electrodes with high loading used in LIBs and SIBs.

The effect of Li2CO3 substitution on synthesis of LiBOB compounds as salt of electrolyte battery lithium ion

NASA Astrophysics Data System (ADS)

Lestariningsih, Titik; Wigayati, Etty Marty; Sabrina, Qolby; Prihandoko, Bambang; Priyono, Slamet

2018-04-01

Development of the synthesis of LiB(C2O4)2 compounds continues to evolve along with the need for electrolyte salts to support the research of the manufacture of lithium ion batteries. A study had been conducted on the effect of Li2CO3 substitution on the synthesis of LiB(C2O4)2 or LiBOB compounds. LiBOB was a major candidate to replace LiPF6 as a highly toxic lithium battery electrolyte and harmful to human health. Synthesis of Lithium bis(oxalato) borate used powder metallurgy method. The raw materials used are H2C2O4.2H2O, Li2CO3 or LiOH and H2BO3 from Merck Germany products. The materials are mixed with 2: 1: 1 mol ratio until homogeneous. The synthesis of LiBOB refers to previous research, where the heating process was done gradually. The first stage heating is carried out at 120°C for 4 hours, then the next stage heating is carried out at 240°C for 7 hours. The sample variation in this study was to distinguish the lithium source from Li2CO3 and LiOH. Characterization was done by XRD to know the phase formed, FTIR to confirm that functional group of LiB(C2O4)2 compound, SEM to know the morphological structure, and TG/DTA to know the thermal properties. The results of the analysis shows that LiBOB synthesis using Lithium source from Li2CO3 has succeeded to form LiBOB compound with more LiBOB phase composition is 59.1% and 40.9% LiBOB hydrate phase, SEM morphology shows powder consist of elongated round particle porous and similar to LiBOB commercial and show higher thermal stability.

Radiation effects and defects in lithium borate crystals

NASA Astrophysics Data System (ADS)

Ogorodnikov, Igor N.; Poryvay, Nikita E.; Pustovarov, Vladimir A.

2010-11-01

The paper presents the results of a study of the formation and decay of lattice defects in wide band-gap optical crystals of LiB3O5 (LBO), Li2B4O7 (LTB) and Li6Gd(BO3)3 (LGBO) with a sublattice of mobile lithium cations. By means of thermoluminescence techniques, and luminescent and absorption optical spectroscopy with a nanosecond time resolution under excitation with an electron beam, it was revealed that the optical absorption in these crystals in the visible and ultraviolet spectral ranges is produced by optical hole-transitions from the local defect level to the valence band states. The valence band density of the states determines mainly the optical absorption spectral profile, and the relaxation kinetics is rated by the interdefect non-radiative tunnel recombination between the trapped-hole center and the Li0 trapped-electron centers. At 290 K, the Li0 centers are subject to thermally stimulated migration. Based on experimental results, the overall picture of thermally stimulated recombination processes with the participation of shallow traps was established for these crystals.

Transport properties of lithium ions doped vanado-bismuth-tellurite glasses

NASA Astrophysics Data System (ADS)

Keshavamurthy, K.; Eraiah, B.

2016-05-01

The glasses of composition (65-x)V2O5-xLi2O-20TeO2-15Bi2O3 (x = 15 and 25 mol%) were prepared by conventional melt quenching method and their electrical conductivity and dielectric measurements have been carried out in the frequency range 40Hz to 6MHz over a temperature 373 to 473 K. The conductivity values increased with both Li2O concentration and temperature. Interestingly, the dielectric response showed the existence of a negative capacitance effect in the present glass system and concluded that this effect arose from the presence of external inductive reactance.

Graphene sheets stabilized on genetically engineered M13 viral templates as conducting frameworks for hybrid energy-storage materials.

PubMed

Oh, Dahyun; Dang, Xiangnan; Yi, Hyunjung; Allen, Mark A; Xu, Kang; Lee, Yun Jung; Belcher, Angela M

2012-04-10

Utilization of the material-specific peptide-substrate interactions of M13 virus broadens colloidal stability window of graphene. The homogeneous distribution of graphene is maintained in weak acids and increased ionic strengths by complexing with virus. This graphene/virus conducting template is utilized in the synthesis of energy-storage materials to increase the conductivity of the composite electrode. Successful formation of the hybrid biological template is demonstrated by the mineralization of bismuth oxyfluoride as a cathode material for lithium-ion batteries, with increased loading and improved electronic conductivity. Copyright © 2012 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Mechanistic Study of Electrolyte Additives to Stabilize High-Voltage Cathode–Electrolyte Interface in Lithium-Ion Batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gao, Han; Maglia, Filippo; Lamp, Peter

Current developments of electrolyte additives to stabilize electrode-electrolyte interface in Li-ion batteries highly rely on a trial-and-error search, which involves repetitive testing and intensive amount of resources. The lack of understandings on the fundamental protection mechanisms of the additives significantly increases the difficulty for the transformational development of new additives. In this study, we investigated two types of individual protection routes to build a robust cathode-electrolyte interphase at high potentials: (i) a direct reduction in the catalytic decomposition of the electrolyte solvent; and (ii) formation of a “corrosion inhibitor film” that prevents severely attack and passivation from protons that generatedmore » from the solvent oxidation, even the decomposition of solvent cannot not mitigated. Effect of three exemplary electrolyte additives: (i) lithium difluoro(oxalato)borate (LiDFOB); (ii) 3-hexylthiophene (3HT); and (iii) tris(hexafluoro-iso-propyl)phosphate (HFiP), on LiNi0.6Mn0.2Co0.2O2 (NMC 622) cathode were investigated to validate our hypothesis. It is demonstrated that understandings of both electrolyte additives and solvent are essential and careful balance between the cathode protection mechanism of additives and their side effects is critical to obtain optimum results. More importantly, this study opens up new directions of rational design of functional electrolyte additives for the next generation high-energy density lithium-ion chemistries.« less

Ion dynamics in a new class of materials: nanoglassy lithium alumosilicates

NASA Astrophysics Data System (ADS)

Stanje, B.; Bottke, P.; Breuer, S.; Hanzu, I.; Heitjans, P.; Wilkening, M.

2018-03-01

In many cases nanocrystalline materials, prepared through high-energy ball milling, reveal enhanced ion dynamics when compared to the situation in the coarse-grained analogues. This effect, which has particularly been seen for lithium alumosilicates, has been ascribed to structural disorder, i.e., the introduction of defect sites during mechanical treatment. Much less is, however, known about ion transport in nanostructured amorphous materials, e.g., nanoglassy compounds, which are regarded as a new class of functional materials. Following earlier studies on nanoglassy lithium alumosilicates and borates, here we studied ion dynamics in nanoglassy petalite LiAlSi4O10. While conductivity spectroscopy unequivocally reveals that long-range ion dynamics in nanoglassy LiAlSi4O10 decreases upon milling, local dynamics, sensed by 7Li nuclear magnetic resonance (NMR) spin-lattice relaxation, points to enhanced Li ion mobility compared to the non-treated glass. Most likely, as for nanocrystalline ceramics also for nanoglassy samples a heterogeneous structure, consisting of bulk and interfacial regions, is formed. For LiAlSi4O10 these interfacial regions, characterized by a higher degree of free volume, might act as hosts for spins experiencing fast longitudinal NMR relaxation. Obviously, these regions do not form a through-going network, which would allow the ions to move over long distances as quickly as in the unmilled glass.

Synthesis and evaluation of borates derived from boric acid and diols for the protection of wood against fungal decay and thermal degradation

Treesearch

George C. Chen

2004-01-01

N,N-dimethyl amino carbinol catechol borate(1). N,N-dimethyl amino carbinol-4-methyl catechol borate(2), N,N-dimethyl amino carbinol-4-t- butyl catechol borate(3). N,N-dimethyl amino carbinol-2,3-naphthyl borate 4) were synthesized by refluxing boric acid and diol in DMF(N,N-dimethyl formamide). The borates were characterized by NMR. Wood impregnated with borate 1,2 or...

Mineralogy and sedimentology of the Miocene Göcenoluk borate deposit, Kırka district, western Anatolia, Turkey

NASA Astrophysics Data System (ADS)

García-Veigas, Javier; Helvacı, Cahit

2013-05-01

The Miocene boratiferous district of Kırka, in western Anatolia (Turkey), is the most important Na-borate (borax) resource in the world. Two separate deposits in the Kırka district are located near the villages of Sarıkaya and Göcenoluk (Eskişehir Province). Borax is intensively exploited in open-pit mines in the Sarıkaya deposit while only small quarries of colemanite are known in the Göcenoluk deposit. Recent exploratory drilling in the Göcenoluk area intersected a thick succession of dolostones, tuffs and three borate-bearing units (Lower, Intermediate and Upper Borate Units). In them, the most abundant borate mineral is ulexite (Ca-Na-borate) passing at depth to probertite. Borax (Na-borate) is only present in the Intermediate Borate Unit. Minor amounts of colemanite (Ca-borate) and hydroboracite (Ca-Mg-borate) occur at the base, and/or top, of each mineralized unit. Pyroclastic layers within the borate units show intense alteration by alkaline, boron-bearing waters and formation of diagenetic clay minerals (smectites), zeolites (analcime) and borosilicates (searlesite). The Göcenoluk succession is interpreted as a shallow, ephemeral, alkaline lake deposit in which carbonates formed as stromatolites and travertines. Borate precipitation in the Göcenoluk area took place interstitially within muddy and carbonate sediments in a lateral progression from marginal Ca-borates towards Na-Ca-borates and rarely to Na-borates in the center of the lake. Authigenic silicate mineral distribution shows parallel changes toward the center of the lake that reflect increasing pH gradient.

Bismuth Nanoparticles Embedded in Carbon Spheres as Anode Materials for Sodium/Lithium-Ion Batteries.

PubMed

Yang, Fuhua; Yu, Fan; Zhang, Zhian; Zhang, Kai; Lai, Yanqing; Li, Jie

2016-02-12

Sodium-ion batteries (SIBs) are regarded as an attractive alternative to lithium-ion batteries (LIBs) for large-scale commercial applications, because of the abundant terrestrial reserves of sodium. Exporting suitable anode materials is the key to the development of SIBs and LIBs. In this contribution, we report on the fabrication of Bi@C microspheres using aerosol spray pyrolysis technique. When used as SIBs anode materials, the Bi@C microsphere delivered a high capacity of 123.5 mAh g(-1) after 100 cycles at 100 mA g(-1) . The rate performance is also impressive (specific capacities of 299, 252, 192, 141, and 90 mAh g(-1) are obtained under current densities of 0.1, 0.2, 0.5, 1, and 2 A g(-1) , respectively). Furthermore, the Bi@C microsphere also proved to be suitable LIB anode materials. The excellent electrochemical performance for both SIBs and LIBs can attributed to the Bi@C microsphere structure with Bi nanoparticles uniformly dispersed in carbon spheres. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Electrolytes with Improved Safety Developed for High Specific Energy Li-Ion Cells with Si-Based Anodes

NASA Technical Reports Server (NTRS)

Smart, M. C.; Krause, F. C.; Hwang, C.; Soler, J.; West, W. C.; Ratnakumar, B. V.; Prakash, G. K. S.

2012-01-01

A number of electrolyte formulations that have improved safety characteristics have been developed for use with high capacity silicon-based anodes. To improve the compatibility with Si-based anodes, a number of technical approaches have been employed, including: (1) the use of mono-fluoroethylene carbonate (FEC) in conjunction with, or in lieu of, ethylene carbonate (EC), (2) the use of high proportions of fluorinated co-solvents, (3) the use of vinylene carbonate (VC) to stabilize the Si/C electrode, and (4) the use of lithium bis(oxalato)borate (LiBOB) to improve the compatibility of the electrolyte when Si/C electrodes are used in conjunction with high voltage cathodes. Candidate electrolytes were studied in Li/Si-C and Si-C/ Li(MnNiCo)O2 (NMC) coin cells, as well as in larger Si-C/NMC three-electrode cells equipped with lithium reference electrodes. In summary, many electrolytes that contain triphenyl phosphate (TPP), which is used as a flame retardant additive up to concentrations of 15 volume percent, and possess FEC as a co-solvent have been demonstrated to outperform the all-carbonate baseline electrolytes when evaluated in Si-C/ Li(MnNiCo)O2 cells.

Structural study and DC conductivity of vanadyl doped zinc lithium borate glasses

NASA Astrophysics Data System (ADS)

Seema, Khasa, S.; Dahiya, M. S.; Yadav, Arti; Agarwal, A.; Dahiya, S.

2015-06-01

Glasses with composition xZnOṡ(30 - x)ṡLi2Oṡ70B2O3 containing 2 mol% of V2O5 (x = 0, 2, 5, 7 and 10) were prepared by standard melt-quench technique. The amorphous nature of the glass samples was confirmed by using x-ray diffraction. The structural changes in these glasses have been investigated by employing IR spectroscopy in the mid-IR range. The infrared spectroscopic analysis confirms the presence of both triangular and tetraheldral coordinated boron units and absence of boroxol ring. It also shows that metal-oxide vibrations are present which are due to the bonding of lithium and zinc ions with oxygen. The dc conductivity was measured in the temperature range 353-523 K. The dc conductivity results show that conductivity decreases and activation energy increases when Li2O is replaced by ZnO, keeping the concentration of B2O3 constant. Decrease in conductivity and increase in activation energy shows that addition of ZnO to the glass matrix shows a "blocking effect" on the overall mobility of alkali ions, but at higher concentration the hopping effect was also observed.

Simultaneous Stabilization of LiNi0.76Mn0.14Co0.10O2 Cathode and Lithium Metal Anode by LiBOB Additive.

PubMed

Zhao, Wengao; Zou, Lianfeng; Zheng, Jianming; Jia, Haiping; Song, Junhua; Engelhard, Mark H; Wang, Chongmin; Xu, Wu; Yang, Yong; Zhang, Ji-Guang

2018-05-01

The long-term cycling performance, rate capability, and voltage stability of lithium (Li) metal batteries with LiNi0.76Mn0.14Co0.10O2 (NMC76) cathodes is greatly enhanced by lithium bis(oxalato)borate (LiBOB) additive in the LiPF6-based electrolyte. With 2% LiBOB in the electrolyte, a Li||NMC76 cell is able to achieve a high capacity retention of 96.8% after 200 cycles at C/3 rate (1C = 200 mA g-1), which is the best result reported for a Ni-rich NMC cathode coupled with Li metal anode. The significantly enhanced electrochemical performance can be ascribed to the stabilization of both the NMC76-cathode/electrolyte and Li-metal-anode/electrolyte interfaces. LiBOB-containing electrolyte not only facilitates the formation of a more compact solid electrolyte interphase on the Li metal surface, it also forms a enhanced cathode electrolyte interface layer, which efficiently prevents the corrosion of the cathode interface and mitigates the formation of disordered rock-salt phase after cycling. The fundamental findings of this work highlight the importance of recognizing the dual effects of electrolyte additives in simultaneously stabilizing both cathode and anode interfaces, so as to enhance the long-term cycle life of high-energy-density battery systems. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Mg- and K-bearing borates and associated evaporites at Eagle Borax spring, Death Valley, California: A spectroscopic exploration

USGS Publications Warehouse

Crowley, J.K.

1996-01-01

Efflorescent crusts at the Eagle Borax spring in Death Valley, California, contain an array of rare Mg and K borate minerals, several of which are only known from one or two other localities. The Mg- and/or K-bearing borates include aristarainite, hydroboracite, kaliborite, mcallisterite, pinnoite, rivadavite, and santite. Ulexite and probertite also occur in the area, although their distribution is different from that of the Mg and K borates. Other evaporite minerals in the spring vicinity include halite, thenardite, eugsterite, gypsum-anhydrite, hexahydrite, and bloedite. Whereas the first five of these minerals are found throughout Death Valley, the last two Mg sulfates are more restricted in occurrence and are indicative of Mg-enriched ground water. Mineral associations observed at the Eagle Borax spring, and at many other borate deposits worldwide, can be explained by the chemical fractionation of borate-precipitating waters during the course of evaporative concentration. The Mg sulfate and Mg borate minerals in the Eagle Borax efflorescent crusts point to the fractionation of Ca by the operation of a chemical divide involving Ca carbonate and Na-Ca borate precipitation in the subsurface sediments. At many other borate mining localities, the occurrence of ulexite in both Na borate (borax-kernite) and Ca borate (ulexite-colemanite) deposits similarly reflects ulexite's coprecipitation with Ca carbonate at an early concentration stage. Such ulexite may perhaps be converted to colemanite by later reaction with the coexisting Ca carbonate - the latter providing the additional Ca2+ ions needed for the conversion. Mg and Ca-Mg borates are the expected late-stage concentration products of waters forming ulexite-colemanite deposits and are therefore most likely to occur in the marginal zones or nearby mud facies of ulexite-colemanite orebodies. Under some circumstances, Mg and Ca-Mg borates might provide a useful prospecting guide for ulexite-colemanite deposits, although the high solubility of Mg borate minerals may prevent their formation in lacustrine settings and certainly inhibits their geologic preservation. The occurrence of Mg borates in borax-kernite deposits is also related to fractionation processes and points to the operation of an Mg borate chemical divide, characterized by Mg borate precipitation ahead of Mg carbonate. All of these considerations imply that Mg is a significant chemical component of many borate-depositing ground waters, even though Mg borate minerals may not be strongly evident in borate orebodies. The Eagle Borax spring borates and other evaporite minerals were studied using spectroscopic and X-ray powder diffraction methods, which were found to be highly complementary. Spectral reflectance measurements provide a sensitive means for detecting borates present in mixtures with other evaporites and can be used to screen samples rapidly for X-ray diffraction analysis. The apparently limited occurrence of Mg and K borate minerals compared to Ca and Na borates may stem partly from the inefficiency of X-ray diffraction methods for delineating the mineralogy of large and complex deposits. Spectral reflectance measurements can be made in the laboratory, in the field, on the mine face, and even remotely. Reflectance data should have an important role in studies of existing deposit mineralogy and related chemical fractionation processes, and perhaps in the discovery of new borate mineral resources.

Role of oxygen on the optical properties of borate glass doped with ZnO

DOE Office of Scientific and Technical Information (OSTI.GOV)

Abdel-Baki, Manal; El-Diasty, Fouad, E-mail: fdiasty@yahoo.com

2011-10-15

Lithium tungsten borate glass (0.56-x)B{sub 2}O{sub 3}-0.4Li{sub 2}O-xZnO-0.04WO{sub 3} (0{<=}x{<=}0.1 mol%) is prepared by the melt quenching technique for photonic applications. Small relative values of ZnO are used to improve the glass optical dispersion and to probe as well the role of oxygen electronic polarizability on its optical characteristics. The spectroscopic properties of the glass are determined in a wide spectrum range (200-2500 nm) using a Fresnel-based spectrophotometric technique. Based on the Lorentz-Lorenz theory, as ZnO content increases on the expense of B{sub 2}O{sub 3} the glass molar polarizability increased due to an enhanced unshared oxide ion 2p electron density,more » which increases ionicity of the chemical bonds of glass. The role of oxide ion polarizability is explained in accordance with advanced measures and theories such as optical basicity, O 1s binding energy, the outer most cation binding energy in Yamashita-Kurosawa's interionic interaction parameter and Sun's average single bond strength. FT-IR measurements confirm an increase in bridging oxygen bonds, as a result of replacement of ZnO by B{sub 2}O{sub 3}, which increase the UV glass transmission window and transmittance. - Graphical abstract: O1s, Yamashita-Kurosawa's parameter and average single bond strength of charge overlapping between electronic shells are used to explain enhanced oxide ion 2p electron density, which increases refractive index of glasses. Highlights: > New borate glass for photonic application is prepared. > The dispersion property of the glass is effectively controlled using small amounts of ZnO. > ZnO is used to probe the glass structure and investigate the role of oxygen on the obtained optical properties of the glasses. > Modern theories are used to explain enhanced unshared oxide ion 2p electron density, which increases ionicity of chemical bonds of the glass.« less

Radiological properties of plastics and TLD materials its application in radiation dosimetry

NASA Astrophysics Data System (ADS)

Jabaseelan Samuel, E. James; Srinivasan, K.; Poopathi, V.

2017-05-01

In the current study, we evaluated the tissue equivalency of nine different commonly used thermoluminescence compounds and six plastic materials over the photon energy range of 15 KeV to 20 MeV. Our result confirmed that the ratio of number of electrons per gram, electron density of the entire TLD compounds and plastic materials to ICRU-44 soft tissue was lesser than unity, except in the case of polypropylene plastics. The effective atomic number ratio of all the plastic materials was also <1 excluding Poly-vinyl-chloride, and for TLD lithium borate material, it was <1 others which showed the deviation with respect to photon energy. Mass attenuation coefficient (µ/ϼ), mass absorption coefficient (µen/ρ) was calculated and the results are discussed in this paper.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Abdel-Baki, Manal; Abdel-Wahab, Fathy A.; El-Diasty, Fouad

Lithium tungsten borate glass of the composition (0.56-x)B{sub 2}O{sub 3}-0.4Li{sub 2}O-xZnO-0.04WO{sub 3} (0 {<=}x{<=} 0.1 mol. %) is prepared for photonics applications. The glass is doped with ZnO to tune the glass absorption characteristics in a wide spectrum range (200-2500 nm). Chemical bond approach, including chemical structure, electronegativity, bond ionicity, nearest-neighbor coordination, and other chemical bonding aspect, is used to analyze and to explain the obtained glass properties such as: transmittance, absorption, electronic structure parameters (bandgap, Fermi level, and Urbach exciton-phonon coupling), Wannier free excitons excitation (applying Elliott's model), and two-photon absorption coefficient as a result of replacement of B{submore » 2}O{sub 3} by ZnO.« less

Fabrication of large-scale single-crystal bismuth telluride (Bi2Te3) nanosheet arrays by a single-step electrolysis process

NASA Astrophysics Data System (ADS)

Tsai, Hung-Wei; Wang, Tsang-Hsiu; Chan, Tsung-Cheng; Chen, Pei-Ju; Chung, Chih-Chun; Yaghoubi, Alireza; Liao, Chien-Neng; Diau, Eric Wei-Guang; Chueh, Yu-Lun

2014-06-01

Nanolizing of thermoelectric materials is one approach to reduce the thermal conductivity and hence enhance the figure of merit. Bismuth telluride (Bi2Te3)-based materials have excellent figure of merit at room temperature. For device applications, precise control and rapid fabrication for the nanostructure of thermoelectric materials are essential issues. In the present study, we demonstrate a one-step electrolysis process to directly form Bi2Te3 nanosheet arrays (NSAs) on the surface of bulk Bi2Te3 with controllable spacing distance and depth by tuning the applied bias and duration. The single sheet of NSAs reveals that the average thickness and electrical resistivity of single crystalline Bi2Te3 in composition are 399.8 nm and 137.34 μΩ m, respectively. The formation mechanism of NSAs has been proposed. A 1.12% efficiency of quantum dot-sensitized solar cells with Bi2Te3 NSAs for counter electrode has been demonstrated, indicating that Bi2Te3 NSAs from top-down processing with a high ratio of surface area to volume are a promising candidate for possible applications such as thermoelectrics, dye-sensitized solar cells (DSSCs), and lithium-ion batteries.Nanolizing of thermoelectric materials is one approach to reduce the thermal conductivity and hence enhance the figure of merit. Bismuth telluride (Bi2Te3)-based materials have excellent figure of merit at room temperature. For device applications, precise control and rapid fabrication for the nanostructure of thermoelectric materials are essential issues. In the present study, we demonstrate a one-step electrolysis process to directly form Bi2Te3 nanosheet arrays (NSAs) on the surface of bulk Bi2Te3 with controllable spacing distance and depth by tuning the applied bias and duration. The single sheet of NSAs reveals that the average thickness and electrical resistivity of single crystalline Bi2Te3 in composition are 399.8 nm and 137.34 μΩ m, respectively. The formation mechanism of NSAs has been proposed. A 1.12% efficiency of quantum dot-sensitized solar cells with Bi2Te3 NSAs for counter electrode has been demonstrated, indicating that Bi2Te3 NSAs from top-down processing with a high ratio of surface area to volume are a promising candidate for possible applications such as thermoelectrics, dye-sensitized solar cells (DSSCs), and lithium-ion batteries. Electronic supplementary information (ESI) available. See DOI: 10.1039/c4nr00184b

Penetration of boron from topically applied borate solutions

Treesearch

Stan T. Lebow; Patricia K. Lebow; Steven A. Halverson

2010-01-01

Borate penetration relies on diffusion when borate and glycol-borate preservatives are applied to the surface of wood. This study evaluated the extent of borate penetration in framing lumber as a function of preservative formulation, wood moisture content, and diffusion time after treatment. In Phase I of the study, end-matched specimens were conditioned to target...

High temperature ultrasonic transducers for imaging and measurements in a liquid Pb/Bi eutectic alloy.

PubMed

Kazys, Rymantas; Voleisis, Algirdas; Sliteris, Reimondas; Mazeika, Liudas; Van Nieuwenhove, Rudi; Kupschus, Peter; Abderrahim, Hamid Aït

2005-04-01

In some nuclear reactors or accelerator-driven systems (ADS) the core is intended to be cooled by means of a heavy liquid metal, for example, lead-bismuth (Pb/Bi) eutectic alloy. For safety and licensing reasons, an imaging method of the interior of ADS, based on application of ultrasonic waves, has thus to be developed. This paper is devoted to description of developed various ultrasonic transducers suitable for long term imaging and measurements in the liquid Pb/Bi alloy. The results of comparative experimental investigations of the developed transducers of different designs in a liquid Pb/Bi alloy up to 450 degrees C are presented. Prototypes with different high temperature piezoelectric materials were investigated: PZT, bismuth titanate (Bi4Ti3O12), lithium niobate (LiNbO3), gallium orthophosphate (GaPO4) and aluminum nitride (A1N). For acoustic coupling with the metal alloy, it was proposed to coat the active surface of the transducers by diamond like carbon (DLC). The radiation robustness was assessed by exposing the transducers to high gamma dose rates in one of the irradiation facilities at SCK x CEN. The experimental results proved that the developed transducers are suitable for long-term operation in harsh conditions.

Bright up-conversion white light emission from Er3+ doped lithium fluoro zinc borate glasses for photonic applications

NASA Astrophysics Data System (ADS)

Vijayalakshmi, L.; Naveen Kumar, K.; Rao, K. Srinivasa; Hwang, Pyung

2018-03-01

Various concentrations of Er3+ (0.3, 0.5, 1.0 and 1.5 mol %) doped lithium fluoro zinc borate glasses were synthesized by a traditional melt quenching method. XRD, FTIR and FESEM have been employed to analyze the structural, compositional and morphological analysis respectively. Judd-Ofelt theory has been employed to analyze the intensity parameters (Ωλ, λ = 2, 4 and 6) which can be used to estimate the radiative properties of fluorescent levels of Er3+. We have been observed a strong NIR emission peak at 1.53 μm (4I13/2 → 4I15/2) under the excitation of 980 nm from Er3+: LBZ glasses. Nevertheless, the NIR emission is remarkably enhanced by increasing the Er3+ ions concentration until the optimized concentration of 0.5 mol%. The lifetime of the excited level of 4I13/2 in the NIR emission transition is evaluated and it is found to be1.22 ms from the decay analysis of 0.5 mol% Er3+: LBZ glass. Apart from the NIR emission, a bright up-conversion green emission is observed at 544 nm (4S3/2 → 4I15/2) along with an intense red emission at 659 nm (4F9/2 → 4I15/2) and a weak blue emission (2H9/2 → 4I15/2) under the excitation of 980 nm. Up-conversion emission features were significantly enhanced with increasing the Er3+ concentration up to 1.0 mol%. The combination of the obtained up-conversion emission colors of green, red and blue could generate white light emission. The cool white-light emission from the optimized glass sample has been confirmed from the Commission International de I'Echairage (CIE) 1931 chromaticity diagram analysis and their correlated color temperature (CCT) values. Based on the NIR and up-conversion emission features, Er3+: LBZ glasses could be suggested as promising candidates for optical amplifiers, optical telecommunication windows and white light photonic applications.

Enhanced Electrochemical Performances of Bi2O3/rGO Nanocomposite via Chemical Bonding as Anode Materials for Lithium Ion Batteries.

PubMed

Deng, Zhuo; Liu, Tingting; Chen, Tao; Jiang, Jiaxiang; Yang, Wanli; Guo, Jun; Zhao, Jianqing; Wang, Haibo; Gao, Lijun

2017-04-12

Bismuth oxide/reduced graphene oxide (termed Bi 2 O 3 @rGO) nanocomposite has been facilely prepared by a solvothermal method via introducing chemical bonding that has been demonstrated by Raman and X-ray photoelectron spectroscopy spectra. Tremendous single-crystal Bi 2 O 3 nanoparticles with an average size of ∼5 nm are anchored and uniformly dispersed on rGO sheets. Such a nanostructure results in enhanced electrochemical reversibility and cycling stability of Bi 2 O 3 @rGO composite materials as anodes for lithium ion batteries in comparison with agglomerated bare Bi 2 O 3 nanoparticles. The Bi 2 O 3 @rGO anode material can deliver a high initial capacity of ∼900 mAh/g at 0.1C and shows excellent rate capability of ∼270 mAh/g at 10C rates (1C = 600 mA/g). After 100 electrochemical cycles at 1C, the Bi 2 O 3 @rGO anode material retains a capacity of 347.3 mAh/g with corresponding capacity retention of 79%, which is significantly better than that of bare Bi 2 O 3 material. The lithium ion diffusion coefficient during lithiation-delithiation of Bi 2 O 3 @rGO nanocomposite has been evaluated to be around ∼10 -15 -10 -16 cm 2 /S. This work demonstrates the effects of chemical bonding between Bi 2 O 3 nanoparticles and rGO substrate on enhanced electrochemical performances of Bi 2 O 3 @rGO nanocomposite, which can be used as a promising anode alterative for superior lithium ion batteries.

Deep-ocean ferromanganese crusts and nodules

USGS Publications Warehouse

Hein, James R.; Koschinsky, Andrea

2014-01-01

Ferromanganese crusts and nodules may provide a future resource for a large variety of metals, including many that are essential for emerging high- and green-technology applications. A brief review of nodules and crusts provides a setting for a discussion on the latest (past 10 years) research related to the geochemistry of sequestration of metals from seawater. Special attention is given to cobalt, nickel, titanium, rare earth elements and yttrium, bismuth, platinum, tungsten, tantalum, hafnium, tellurium, molybdenum, niobium, zirconium, and lithium. Sequestration from seawater by sorption, surface oxidation, substitution, and precipitation of discrete phases is discussed. Mechanisms of metal enrichment reflect modes of formation of the crusts and nodules, such as hydrogenetic (from seawater), diagenetic (from porewaters), and mixed diagenetic–hydrogenetic processes.

Amount of leachant and water absorption levels of wood treated with borates and water repellents.

PubMed

Baysal, Ergun; Sonmez, Abdullah; Colak, Mehmet; Toker, Hilmi

2006-12-01

Wood protection efficacy of borates against biological agents, flame retardancy, and suitability to the environment is well known. Since borates can be applied to timber as water based solutions, they are preferred economically as well. Even though they are highly mobile in wood, boron compounds are widely used in timber preservation. Borates migrate in liquid and increase the hygroscopicity of wood in damp conditions. This study deals with the physical restriction of water access in wood by impregnating water repellent agents into wood to limit amount of leachant and water absorption levels of wood after boron treatment. Borates were incorporated with polyethylene glycol-400 (PEG-400) their bulking effect in wood was considered. Results indicated that the amount of leachates from wood treated with borates in PEG-400 was remarkably higher compared to those of wood treated with the aqueous solutions of borates. Water absorption (WA) levels of wood treated with aqueous solutions of borates were higher than those of their treated samples with the solutions in PEG-400. Secondary treatments of wood with the water repellent (WR) chemicals following borate impregnation reduced the leaching of chemicals from wood in water and also WA of the specimens were less than those of the wood treated with only borates from aqueous and PEG solutions. Styrene (St) was the most effective monomer among the other agents used in terms of immobility effect on borates and WA.

Borates

USGS Publications Warehouse

Crangle, R.D.

2013-01-01

Four minerals represent 90 percent of the borates used by industry worldwide — the sodium borates (tincal and kernite), calcium borate (colemanite) and the sodium-calcium borate (ulexite). Borax is a white crystalline substance, chemically known as sodium tetraborate decahydrate, and is found naturally as the mineral tincal. Boric acid is a colorless crystalline solid sold in technical, national formulary and special quality grades as granules or powder and marketed most often as anhydrous boric acid. Deposits of borates are associated with volcanic activity and arid climates, with the largest economically viable deposits located in the Mojave Desert of the United States near Boron, CA, the Alpide belt in southern Asia and the Andean belt of South America.

Synthesis and optical properties of antimony oxide glasses doped with holmium trioxide

DOE Office of Scientific and Technical Information (OSTI.GOV)

Raghunatha, S.; Eraiah, B., E-mail: eraiah@rediffmail.com

2016-05-06

Holmium doped lithium-antimony-lead borate glasses having 1 mol% AgNO{sub 3} with composition 50B{sub 2}O{sub 3}-20PbO-25Sb{sub 2}O{sub 3}-5Li{sub 2}O have been prepared using single step melt quenching technique. The XRD spectrum confirms amorphous nature of glasses. The optical absorbance studies were carried out on these glasses. The optical direct band gap energies were found to be in the range of 3.10 eV to 3.31 eV and indirect band gap energies were found to be in the range of 2.28 eV to 3.00 eV. The refractive indexes have been calculated by using Lorentz-Lorenz formula and the calculated values in the range ofmore » 2.31 to 2.37.« less

A novel mixed-metal borate with large [B12O18(OH)6]6- motif: Synthesis, structure and property

NASA Astrophysics Data System (ADS)

Wei, Li; Pan, Jie; Xue, Zhen-Zhen; Wang, Guo-Ming; Wang, Ying-Xia

2018-01-01

A new mixed-metal polyborate, Na5Li[B12O18(OH)6]·2H2O (1), has been synthesized using solvothermal method and characterized by IR spectroscopy, thermogravimetric analysis, UV-Vis spectroscopy, powder and single-crystal X-ray diffraction, respectively. It crystallizes in the trigonal space group R-3c (No. 167) with unit cell parameters of a = b = 9.6767(6) Å, c = 36.358(5) Å, and Z = 6. Its structure features unprecedented 3D framework constructed from novel honeycomb-shaped inorganic Na-O sheets with unique 12-MR sodium rings and supramolecular polyborate 2D layers of lithium-centered [B12O18(OH)6]6-. UV-Vis spectral characterization indicates that compound 1 is a wide-band-gap semiconductor.

40 CFR 721.10631 - Mixed metal borate (generic).

Code of Federal Regulations, 2013 CFR

2013-07-01

... 40 Protection of Environment 32 2013-07-01 2013-07-01 false Mixed metal borate (generic). 721... Substances § 721.10631 Mixed metal borate (generic). (a) Chemical substance and significant new uses subject to reporting. (1) The chemical substance identified generically as mixed metal borate (PMN P-12-64...

40 CFR 721.10631 - Mixed metal borate (generic).

Code of Federal Regulations, 2014 CFR

2014-07-01

... 40 Protection of Environment 31 2014-07-01 2014-07-01 false Mixed metal borate (generic). 721... Substances § 721.10631 Mixed metal borate (generic). (a) Chemical substance and significant new uses subject to reporting. (1) The chemical substance identified generically as mixed metal borate (PMN P-12-64...

Near-IR, blue, and UV generation by frequency conversion of a Tm:YAP laser

NASA Astrophysics Data System (ADS)

Cole, Brian; Goldberg, Lew; Chinn, Steve

2018-02-01

We describe generation of near-infrared (944nm, 970nm), blue (472nm, 485nm), and UV (236 nm) light by frequency up-conversion of 2 μm output of a compact and efficient passively Q-switched Tm:YAP laser. The Tm:YAP laser source was near diffraction limited with maximum Q-switched pulse peak power of 190 kW. For second harmonic generation (SHG) of NIR, both periodically poled lithium niobate (PPLN) and lithium tri-borate (LBO) were evaluated, with 58% conversion efficiency and 3.1 W of 970 nm power achieved with PPLN. The PPLN 970nm emission was frequency doubled in 20mm long type I LBO, generating 1.1 W at 485nm with a conversion efficiency of 34%. With LBO used for frequency doubling of 2.3 W of 1888 nm Tm:YAP output to 944nm, 860mW was generated, with 37% conversion efficiency. Using a second LBO crystal to generate the 4th harmonic, 545mW of 472nm power was generated, corresponding to 64% conversion efficiency. To generate the 8th harmonic of Tm:YAP laser emission, the 472nm output of the second LBO was frequency doubled in a 7mm long BBO crystal, generating 110 mW at 236nm, corresponding to 21% conversion efficiency.

21 CFR 872.3400 - Karaya and sodium borate with or without acacia denture adhesive.

Code of Federal Regulations, 2010 CFR

2010-04-01

... denture adhesive. 872.3400 Section 872.3400 Food and Drugs FOOD AND DRUG ADMINISTRATION, DEPARTMENT OF... and sodium borate with or without acacia denture adhesive. (a) Identification. A karaya and sodium borate with or without acacia denture adhesive is a device composed of karaya and sodium borate with or...

Polarized localization and borate-dependent degradation of the Arabidopsis borate transporter BOR1 in tobacco BY-2 cells

PubMed Central

Matsuoka, Ken

2013-01-01

In Arabidopsis the borate transporter BOR1, which is located in the plasma membrane, is degraded in the presence of excess boron by an endocytosis-mediated mechanism. A similar mechanism was suggested in rice as excess boron decreased rice borate transporter levels, although in this case whether the decrease was dependent on an increase in degradation or a decrease in protein synthesis was not elucidated. To address whether the borate-dependent degradation mechanism is conserved among plant cells, we analyzed the fate of GFP-tagged BOR1 (BOR1-GFP) in transformed tobacco BY-2 cells. Cells expressing BOR1-GFP displayed GFP fluorescence at the plasma membrane, especially at the membrane between two attached cells. The plasma membrane signal was abolished when cells were incubated in medium with a high concentration of borate (3 to 5 mM). This decrease in BOR1-GFP signal was mediated by a specific degradation of the protein after internalization by endocytosis from the plasma membrane. Pharmacological analysis indicated that the decrease in BOR1-GFP largely depends on the increase in degradation rate and that the degradation was mediated by a tyrosine-motif and the actin cytoskeleton. Tyr mutants of BOR1-GFP, which has been shown to inhibit borate-dependent degradation in Arabidopsis root cells, did not show borate-dependent endocytosis in tobacco BY-2 cells. These findings indicate that the borate-dependent degradation machinery of the borate transporter is conserved among plant species. PMID:24715955

Polarized localization and borate-dependent degradation of the Arabidopsis borate transporter BOR1 in tobacco BY-2 cells.

PubMed

Yamauchi, Noboru; Gosho, Tadashi; Asatuma, Satoru; Toyooka, Kiminori; Fujiwara, Toru; Matsuoka, Ken

2013-01-01

In Arabidopsis the borate transporter BOR1, which is located in the plasma membrane, is degraded in the presence of excess boron by an endocytosis-mediated mechanism. A similar mechanism was suggested in rice as excess boron decreased rice borate transporter levels, although in this case whether the decrease was dependent on an increase in degradation or a decrease in protein synthesis was not elucidated. To address whether the borate-dependent degradation mechanism is conserved among plant cells, we analyzed the fate of GFP-tagged BOR1 (BOR1-GFP) in transformed tobacco BY-2 cells. Cells expressing BOR1-GFP displayed GFP fluorescence at the plasma membrane, especially at the membrane between two attached cells. The plasma membrane signal was abolished when cells were incubated in medium with a high concentration of borate (3 to 5 mM). This decrease in BOR1-GFP signal was mediated by a specific degradation of the protein after internalization by endocytosis from the plasma membrane. Pharmacological analysis indicated that the decrease in BOR1-GFP largely depends on the increase in degradation rate and that the degradation was mediated by a tyrosine-motif and the actin cytoskeleton. Tyr mutants of BOR1-GFP, which has been shown to inhibit borate-dependent degradation in Arabidopsis root cells, did not show borate-dependent endocytosis in tobacco BY-2 cells. These findings indicate that the borate-dependent degradation machinery of the borate transporter is conserved among plant species.

Uranium(iii) complexes supported by hydrobis(mercaptoimidazolyl)borates: synthesis and oxidation chemistry.

PubMed

Maria, Leonor; Santos, Isabel C; Santos, Isabel

2018-05-23

The reaction of [UI3(thf)4] with the sodium or lithium salts of hydrobis(2-mercapto-1-methylimidazolyl)borate ligands ([H(R)B(timMe)2]-) in a 1 : 2 ratio, in tetrahydrofuran, gave the U(iii) complexes [UI{κ3-H,S,S'-H(R)B(timMe)2}2(thf)2] (R = H (1), Ph (2)) in good yields. Crystals of [UI{κ3-H,S,S'-H(Ph)B(timMe)2}2(thf)2] (2) were obtained by recrystallization from a tetrahydrofuran/acetonitrile solution, and the ion-separated uranium complex [U{κ3-H,S,S'-H(Ph)B(timMe)2}2(CH3CN)3][I] (3-I) was obtained by dissolution of 2 in acetonitrile followed by recrystallization. One-electron oxidation of 2 with AgBPh4 or I2 resulted in the formation of the cationic U(iv) complexes [U{κ3-H,S,S'-H(Ph)B(timMe)2}3][X] (X = BPh4 (6-BPh4), I (6-I)), due to a ligand redistribution process. These complexes are the first examples of homoleptic poly(azolyl)borate U(iv) complexes. Treatment of complex 2 with azobenzene led to the isolation of crystals of the U(iv) compound [UI{κ3-H(Ph)B(timMe)2}2(κ2-timMe)] (7). Treatment of 2 with pyridine-N oxide (pyNO) led to the formation of the uranyl complex [UO2{κ2-S,S'-H(Ph)B(timMe)2}2] (8) and of complex 6-I, while from the reaction of [U{κ3-H(Ph)B(timMe)2}2(thf)3][BPh4] (5) with pyNO, the oxo-bridged U(iv) complex [{U{κ3-H(Ph)B(timMe)2}2(pyNO)}2(μ-O)][BPh4]2 (9) was also obtained. In the U(iii) and U(iv) complexes, the bis(azolyl)borate ligands bind to the uranium center in a κ3-H,S,S' coordination mode, while in the U(vi) complex the ligands bind to the metal in a κ2-S,S' mode. The presence of UH-B interactions in the solid-state, for the nine-coordinate complexes 1, 2, 3, 6 and 7 and for the eight-coordinate complex 9, was supported by IR spectroscopy and/or X-ray diffraction analysis.

X-ray diffraction, crystal structure, and spectral features of the optical susceptibilities of single crystals of the ternary borate oxide lead bismuth tetraoxide, PbBiBO4.

PubMed

Reshak, Ali Hussain; Kityk, I V; Auluck, S; Chen, Xuean

2009-05-14

The all-electron full-potential linearized augmented plane-wave method has been used for an ab initio theoretical study of the band structure, the spectral features of the optical susceptibilities, the density of states, and the electron charge density for PbBiBO4. Our calculations show that the valence-band maximum (VBM) and conduction-band minimum (CBM) are located at the center of the Brillouin zone, resulting in a direct energy gap of about 3.2 eV. We have synthesized the PbBiBO4 crystal by employing a conventional solid-state reaction method. The theoretical calculations in this work are based on the structure built from our measured atomic parameters. We should emphasize that the observed experimental X-ray diffraction (XRD) pattern is in good agreement with the theoretical one, confirming that our structural model is valid. Our calculated bond lengths show excellent agreement with the experimental data. This agreement is attributed to our use of full-potential calculations. The spectral features of the optical susceptibilities show a small positive uniaxial anisotropy.

Synthesis and characterization of cathode, anode and electrolyte materials for rechargeable lithium batteries

NASA Astrophysics Data System (ADS)

Yang, Shoufeng

Two new classes of cathode materials were studied: iron phosphate/sulfate materials and layered manganese oxides, both of which are low cost and had shown some potential. The first class of materials have poor conductivity and cyclability. I studied a number of methods for increasing the conductivity, and determined that grinding the material with carbon black was as effective as special in-situ coatings. The optimum carbon loading was determined to be between 6 and 15 wt%. Too much carbon reduces the volumetric energy density, whereas too little significantly increased cell polarization (reduced the rate of reaction). The kinetic and thermodynamic stability of LiFePO 4 was also studied and it was determined that over discharge protection will be needed as irreversible Li3PO4 can be formed at low potentials. A novel hydrothermal synthesis method was developed, but the significant level of Fe on the Li site reduces the reaction rate too much. In the case of the layered manganese oxide, cation substitution with Co and Ni is found to be effective in avoiding Jahn-Teller effects and improving electrochemistry. A wide range of tin compounds have been suggested as lithium storage media for advanced anode materials, as tin can store over 4 Li per Sn atom. Lithium hexafluorophosphate, LiPF6, is presently the salt of choice for LiCoO2 batteries, but it is expensive and dissolves some manganese compounds. The lithium bis(oxolato)borate (BOB) salt was recently reported, and I made a study of its use in cells with the LiFePO4 cathode and the tin anode. During its synthesis, it became clear that LiBOB is very reactive with many solvents, and these complexes were characterized to better understand this new material. In LiBOB the lithium is five coordinated, an unstable configuration for the lithium ion so that water and many other solvents rapidly react to make a six coordination. Only in the case of ethylene carbonate was the lithium found to be four coordinated. The LiBOB based electrolyte has a lower ionic conductivity than LiPF6, thus providing a poorer performance, while the capacity retention is improved. Further improvement of conductivity is still needed. Improved LiFePO4 cathode materials have been formed, the behavior of pure tin in the form of foil has been determined and will serve as the base case for future studies of tin based anodes, and the structure and electrochemical behavior of the new LIBOB electrolyte salt has been determined. (Abstract shortened by UMI.)

Effective binding of perhalogenated closo-borates to serum albumins revealed by spectroscopic and ITC studies

NASA Astrophysics Data System (ADS)

Kuperman, Marina V.; Losytskyy, Mykhaylo Yu.; Bykov, Alexander Yu.; Yarmoluk, Sergiy M.; Zhizhin, Konstantin Yu.; Kuznetsov, Nikolay T.; Varzatskii, Oleg A.; Gumienna-Kontecka, Elzbieta; Kovalska, Vladyslava B.

2017-08-01

The interactions of boron cluster compounds closo-borates with biomolecules are widely studied due to their efficiency as agents for boron neutron capture therapy of cancer. In present work the binding abilities of anionic halogen closo-borates [B10Hal10]2- (Hal = Cl, Br, I) and [B12Hal12]2- (Hal = Cl, I) towards bovine and human serum albumins were investigated by spectroscopic and isothermal titration calorimetry (ITC) methods. The protein fluorescence quenching method and ITC studies confirmed the complex formation. The degree of protein fluorescence quenching increased from chlorine to iodine boron derivatives that is attributed to external heavy atom effect. The ITC data point on the existence in the protein structure of two types of binding sites: with higher and lower affinity to closo-borates. Albumin-closo-borate complex binding ratio, n (4-5 anions per protein molecule) is higher than for the parent hydrogen closo-borates (2 anions per protein molecule). Binding constants estimated by fluorescent and ITC methods indicate higher affinity of halogen closo-borates to albumins (K in the range of 104-106 M-1) comparing to that of the hydrogen closo-borate (K about 103 M-1). Due to their high affinity and high binding ratio to albumins halogen closo-borates are proposed for further studies as agents for boron neutron capture therapy.

303 nm continuous wave ultraviolet laser generated by intracavity frequency-doubling of diode-pumped Pr3+:LiYF4 laser

NASA Astrophysics Data System (ADS)

Zhu, Pengfei; Zhang, Chaomin; Zhu, Kun; Ping, Yunxia; Song, Pei; Sun, Xiaohui; Wang, Fuxin; Yao, Yi

2018-03-01

We demonstrate an efficient and compact ultraviolet laser at 303 nm generated by intracavity frequency doubling of a continuous wave (CW) laser diode-pumped Pr3+:YLiF4 laser at 607 nm. A cesium lithium borate (CLBO) crystal, cut for critical type I phase matching at room temperature, is used for second-harmonic generation (SHG) of the fundamental laser. By using an InGaN laser diode array emitting at 444.3 nm with a maximum incident power of 10 W, as high as 68 mW of CW output power at 303 nm is achieved. The output power stability in 4 h is better than 2.85%. To the best of our knowledge, this is high efficient UV laser generated by frequency doubling of an InGaN laser diode array pumped Pr3+:YLiF4 laser.

Understanding fifth-harmonic generation in CLBO

NASA Astrophysics Data System (ADS)

Patankar, S.; Yang, S. T.; Moody, J. D.; Bayramian, A. J.; Swadling, G. F.; Barker, D.; Datte, P.; Mennerat, G.; Norton, M.; Carr, C. W.; Begishev, I. A.; Bromage, J.; Ross, J. S.

2018-02-01

We report on results of fifth harmonic generation in Cesium Lithium Borate (CLBO) using a three-crystal cascaded frequency conversion scheme designed to study the energy balance of the final sum frequency generation stage. The experimental setup independently combines the first and fourth harmonic of a Nd:Glass laser in a 5mm thick CLBO crystal. Energy balance between the incoming and output energy is close to unity when the CLBO is out of phase matching and approximately 80% when the crystal is in phase matching. A detailed analysis of the residual fundamental and fourth harmonic energy indicates 5th harmonic light is being generated but only 26% is unaccounted for. We attribute the missing light to linear transmission loss in the CLBO oven. The ratio of the output to input energy is unity when the missing 5th harmonic is incorporated into the calculations. Two-dimensional plane wave mixing simulations show agreement with the results at lower intensities.

Ternary borate-nucleoside complex stabilization by Ribonuclease A demonstrates phosphate mimicry

PubMed Central

Gabel, Scott A.; London, Robert E.

2010-01-01

Phosphate esters play a central role in cellular energetics, biochemical activation, signal transduction and conformational switching. The structural homology of the borate anion with phosphate, combined with its ability to spontaneously esterify hydroxyl groups, suggested that phosphate-ester recognition sites on proteins might exhibit significant affinity for non-enzymatically formed borate esters. 11B NMR studies and activity measurements on ribonuclease A in the presence of borate and several cytidine analogs demonstrate the formation of a stable ternary RNase A•3′-deoxycytidine-2′-borate ternary complex that mimics the complex formed between RNase A and a 2′-cytidine monophosphate (2′-CMP) inhibitor. Alternatively, no slowly exchanging borate resonance is observed for a ternary RNase A, borate, 2′-deoxycytidine mixture, demonstrating the critical importance of the 2′-hydroxyl group for complex formation. Titration of the ternary complex with 2′-CMP shows that it can displace the bound borate ester with a binding constant that is close to the reported inhibition constant of RNase A by 2′CMP. RNase A binding of a cyclic cytidine-2′,3′-borate ester, which is a structural homolog of the cytidine-2′,3′-cyclic phosphate substrate, could also be demonstrated. The apparent dissociation constant for the cytidine-2′,3′-borate•RNase A complex is 0.8 mM, which compares with a Michaelis constant of 11 mM for cCMP at pH 7, indicating considerably stronger binding. However, the value is 1000-fold larger than the reported dissociation constant of the RNase A complex with uridine-vanadate. These results are consistent with recent reports suggesting that in situ formation of borate esters that mimic the corresponding phosphate esters support enzyme catalysis. PMID:17957392

A crystal-chemical classification of borate structures with emphasis on hydrated borates

USGS Publications Warehouse

Christ, C.L.; Clark, J.R.

1977-01-01

The rules governing formation of hydrated borate polyanions that were proposed by C.L. Christ in 1960 are critically reviewed and new rules added on the basis of recent crystal structure determinations. Principles and classifications previously published by others are also critically reviewed briefly. The fundamental building blocks from which borate polyanions can be constructed are defined on the basis of the number n of boron atoms, and the fully hydrated polyanions are illustrated. Known structures are grouped accordingly, and a shorthand notation using n and symbols ?? = triangle, T = tetrahedron is introduced so that the polyanions can be easily characterized. For example, 3:??+2T describes [B3O3(OH)5]2-. Correct structural formulas are assigned borates with known structures whereas borates of unknown structure are grouped separately. ?? 1977 Springer-Verlag.

Simultaneous immobilization of borate, arsenate, and silicate from geothermal water derived from mining activity by co-precipitation with hydroxyapatite.

PubMed

Sasaki, Keiko; Hayashi, Yoshikazu; Toshiyuki, Kenta; Guo, Binglin

2018-09-01

The treatment of the geothermal water discharged through mining activity is a critical issue because the rate of discharge is 12,000 m 3 per day and the discharge contains high concentrations of borate (>20 mg/L) and arsenate (ca. 0.4 mg/L) as well as silicate and carbonate. The simultaneous reduction of borate and arsenate concentrations to acceptable levels was successfully performed by co-precipitation with hydroxyapatite (HAp). Although the coexisting high concentrations of carbonate act as a disturbing element, the co-precipitation equilibrium of borate was shifted to lower values by adjusting the P/Ca molar ratio, and the removal rate of borate was accelerated by using Al 3+ additives, resulting in the efficient reduction of borate within 1 h. The initially immobilized boron in HAp is in the tetragonal form, which probably occupies the hydroxyl sites in HAp, gradually transforming into the trigonal form in the solid state, as interpreted by 1 H NMR and 11 B-NMR. The coexisting silicate was also immobilized in an ellestadite form, as confirmed by 29 Si-NMR measurements. Arsenate and silicate were immobilized before borate in geothermal water. A dissolution assay of borate in the solid residues after co-precipitation with HAp verified the acceptable stability of borate, which is independent of the amount of added Al 3+ . Copyright © 2018 Elsevier Ltd. All rights reserved.

Improved Wide Operating Temperature Range of Li-Ion Cells

NASA Technical Reports Server (NTRS)

Smart, Marshall C.; Bugga, Ratnakumar V.

2013-01-01

Future NASA missions aimed at exploring the Moon, Mars, and the outer planets require rechargeable batteries that can operate over a wide temperature range (-60 to +60 C) to satisfy the requirements of various applications including landers, rovers, penetrators, CEV, CLV, etc. This work addresses the need for robust rechargeable batteries that can operate well over a wide temperature range. The Department of Energy (DoE) has identified a number of technical barriers associated with the development of Liion rechargeable batteries for PHEVs. For this reason, DoE has interest in the development of advanced electrolytes that will improve performance over a wide range of temperatures, and lead to long life characteristics (5,000 cycles over a 10-year life span). There is also interest in improving the high-voltage stability of these candidate electrolyte systems to enable the operation of up to 5 V with high specific energy cathode materials. Currently, the state-of-the-art lithium-ion system has been demonstrated to operate over a wide range of temperatures (-40 to +40 C); however, the rate capability at the lower temperatures is very poor. In addition, the low-temperature performance typically deteriorates rapidly upon being exposed to high temperatures. A number of electrolyte formulations were developed that incorporate the use of electrolyte additives to improve the high-temperature resilience, low-temperature power capability, and life characteristics of methyl propionate (MP)-based electrolyte solutions. These electrolyte additives include mono-fluoroethylene carbonate (FEC), lithium oxalate, vinylene carbonate (VC), and lithium bis(oxalate borate) (LiBOB), which have previously been shown to result in improved high-temperature resilience of all carbonate-based electrolytes. These MP-based electrolytes with additives have been shown to have improved performance in experiments with MCMB-LiNiCoAlO2 cells.

Borates

USGS Publications Warehouse

Angulo, M.A.

2011-01-01

The article discusses the latest developments in the borates industry, particularly in the U.S., as of June 2011. It claims that the biggest economically feasible deposits of borates are seen in the U.S.' Mojave Desert, the Alpide belt in southern Asia and the Andean belt of South America. Turkish state-owned mining firm Eti Maden AS reported that borates were mainly used in the manufacture of glass, ceramics, fertilizer and detergent in 2009.

Synthesis and evaluation of aminoborates derived from boric acid and diols for protecting wood against fungal and thermal degradation

Treesearch

George C. Chen

2008-01-01

N-methyl amino catechol borate (1), N-methyl amino-4-methyl catechol borate (2), N-methyl amino-4-t-butyl catechol borate (3), and N-methyl amino-2, 3-naphthyl borate (4) were synthesized by reflux of boric acid with a diol in solvent N,N-dimethyl formamide. The aminoborates were characterized by proton nuclear magnetic resonance spectroscopy, FTIR spectroscopy and...

Recent advances in rare earth doped alkali-alkaline earth borates for solid state lighting applications

NASA Astrophysics Data System (ADS)

Verma, Shefali; Verma, Kartikey; Kumar, Deepak; Chaudhary, Babulal; Som, Sudipta; Sharma, Vishal; Kumar, Vijay; Swart, Hendrik C.

2018-04-01

As a novel class of inorganic phosphor, the alkali-alkaline earth borate phosphors have gained huge attention due to their charming applications in solid-state lighting (SSL) and display devices. The current research drive shows that phosphors based on the alkali-alkaline earth borates have transformed the science and technology due to their high transparency over a broad spectral range, their flexibility in structure and durability for mechanical and high-laser applications. Recent advances in various aspects of rare-earth (RE) doped borate based phosphors and their utilizations in SSL and light emitting diodes are summarized in this review article. Moreover, the present status and upcoming scenario of RE-doped borate phosphors were reviewed in general along with the proper credential from the existing literature. It is believed that this review is a sole compilation of crucial information about the RE-doped borate phosphors in a single platform.

Radiopacifier Particle Size Impacts the Physical Properties of Tricalcium Silicate–based Cements

PubMed Central

Saghiri, Mohammad Ali; Gutmann, James L.; Orangi, Jafar; Asatourian, Armen; Sheibani, Nader

2016-01-01

Introduction The aim of this study was to evaluate the impact of radiopaque additive, bismuth oxide, particle size on the physical properties, and radiopacity of tricalcium silicate–based cements. Methods Six types of tricalcium silicate cement (CSC) including CSC without bismuth oxide, CSC + 10% (wt%) regular bismuth oxide (particle size 10 μm), CSC + 20% regular bismuth oxide (simulating white mineral trioxide aggregate [WMTA]) as a control, CSC + 10% nano bismuth oxide (particle size 50–80 nm), CSC + 20% nano-size bismuth oxide, and nano WMTA (a nano modification of WMTA comprising nanoparticles in the range of 40–100 nm) were prepared. Twenty-four samples from each group were divided into 4 groups and subjected to push-out, surface microhardness, radiopacity, and compressive strength tests. Data were analyzed by 1-way analysis of variance with the post hoc Tukey test. Results The push-out and compressive strength of CSC without bismuth oxide and CSC with 10% and 20% nano bismuth oxide were significantly higher than CSC with 10% or 20% regular bismuth oxide (P < .05). The surface micro-hardness of CSC without bismuth oxide and CSC with 10% regular bismuth oxide had the lowest values (P < .05). The lowest radiopacity values were seen in CSC without bismuth oxide and CSC with 10% nano bismuth oxide (P < .05). Nano WMTA samples showed the highest values for all tested properties (P < .05) except for radiopacity. Conclusions The addition of 20% nano bismuth oxide enhanced the physical properties of CSC without any significant changes in radiopacity. Regular particle-size bismuth oxide reduced the physical properties of CSC material for tested parameters. PMID:25492489

Tris-borate is a poor counterion for RNA: a cautionary tale for RNA folding studies

PubMed Central

Buchmueller, Karen L.; Weeks, Kevin M.

2004-01-01

Native polyacrylamide gel electrophoresis is a powerful approach for visualizing RNA folding states and folding intermediates. Tris-borate has a high-buffering capacity and is therefore widely used in electrophoresis-based investigations of RNA structure and folding. However, the effectiveness of Tris-borate as a counterion for RNA has not been systematically investigated. In a recirculated Hepes/KCl buffer, the catalytic core of the bI5 group I intron RNA undergoes a conformational collapse characterized by a bulk transition midpoint, or Mg1/2, of ∼3 mM, consistent with extensive independent biochemical experiments. In contrast, in Tris-borate, RNA collapse has a much smaller apparent Mg1/2, equal to 0.1 mM, because in this buffer the RNA undergoes a different, large amplitude, folding transition at low Mg2+ concentrations. Analysis of structural neighbors using a short-lived, RNA-tethered, photocrosslinker indicates that the global RNA structure eventually converges in the two buffer systems, as the divalent ion concentration approaches ∼1 mM Mg2+. The weak capacity of Tris-borate to stabilize RNA folding may reflect relatively unfavorable interactions between the bulky Tris-borate ion and RNA or partial coordination of RNA functional groups by borate. Under some conditions, Tris-borate is a poor counterion for RNA and its use merits careful evaluation in RNA folding studies. PMID:15601995

Waveguide structures in anisotropic nonlinear crystals

NASA Astrophysics Data System (ADS)

Li, Da; Hong, Pengda; Meissner, Helmuth E.

2017-02-01

We report on the design and manufacturing parameters of waveguiding structures of anisotropic nonlinear crystals that are employed for harmonic conversions, using Adhesive-Free Bonding (AFB®). This technology enables a full range of predetermined refractive index differences that are essential for the design of single mode or low-mode propagation with high efficiency in anisotropic nonlinear crystals which in turn results in compact frequency conversion systems. Examples of nonlinear optical waveguides include periodically bonded walk-off corrected nonlinear optical waveguides and periodically poled waveguide components, such as lithium triborate (LBO), beta barium borate (β-BBO), lithium niobate (LN), potassium titanyl phosphate (KTP), zinc germanium phosphide (ZGP) and silver selenogallate (AGSE). Simulation of planar LN waveguide shows that when the electric field vector E lies in the k-c plane, the power flow is directed precisely along the propagation direction, demonstrating waveguiding effect in the planar waveguide. Employment of anisotropic nonlinear optical waveguides, for example in combination with AFB® crystalline fiber waveguides (CFW), provides access to the design of a number of novel high power and high efficiency light sources spanning the range of wavelengths from deep ultraviolet (as short as 200 nm) to mid-infrared (as long as about 18 μm). To our knowledge, the technique is the only generally applicable one because most often there are no compatible cladding crystals available to nonlinear optical cores, especially not with an engineer-able refractive index difference and large mode area.

Microwave synthesis and electrochemical properties of lithium manganese borate as cathode for lithium ion batteries

NASA Astrophysics Data System (ADS)

Ma, Ting; Muslim, Arzugul; Su, Zhi

2015-05-01

Nano structured LiMnBO3/C cathode materials are synthesized by a fast microwave solid-state reaction method using MnCO3, Li2CO3, H3BO3 and glucose as starting materials for the first time. The crystal structure, morphology and electrochemical properties of LiMnBO3/C composites are characterized by X-ray diffraction (XRD), raman spectroscopy (Ramon), scanning electron microscopy (SEM), transmission electron microscopy (TEM), cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS) and charge-discharge tests. The result shows that not only monoclinic LiMnBO3/C but also hexagonal LiMnBO3/C cathode materials can be successfully synthesized by microwave solid-state method with power of 240 W in different time. Compared with h-LiMnBO3/C and mixed phase LiMnBO3/C, m-LiMnBO3/C displays lower charge-transfer resistance and the Warburg impedance, so it reveals a higher first discharge capacity of 156.3 mAh g-1 at 0.05 C within 1.8V-4.6 V, The value increases up to 173.2 mAh g-1 caused by the activation process. Even after 50 cycles, the discharge capacity of m-LiMnBO3/C still remains at 148.2 mAh g-1.

Bismuth Subgallate Toxicity in the Age of Online Supplement Use.

PubMed

Sampognaro, Paul; Vo, Kathy T; Richie, Megan; Blanc, Paul D; Keenan, Kevin

2017-11-01

Bismuth salts have been used to treat gastroenterological disorders and are readily available over-the-counter and via the internet. Even though generally considered safe, bismuth compounds can cause a syndrome of subacute, progressive encephalopathy when taken in large quantities. We present the case of woman who developed progressive encephalopathy, aphasia, myoclonus, and gait instability after chronically ingesting large amounts of bismuth subgallate purchased from a major online marketing website to control symptoms of irritable bowel syndrome. After extensive neurological work-up, elevated bismuth levels in her blood, urine, and cerebrospinal fluid confirmed the diagnosis of bismuth-related neurotoxicity. She improved slowly following cessation of exposure. This case highlights bismuth subgallate as a neurotoxic bismuth formulation and reminds providers of the potential for safety misconceptions of positively reviewed online supplements.

Self-assembled 3D zinc borate florets via surfactant assisted synthesis under moderate pressures: Process temperature dependent morphology study

NASA Astrophysics Data System (ADS)

Mahajan, Dhiraj S.; Deshpande, Tushar; Bari, Mahendra L.; Patil, Ujwal D.; Narkhede, Jitendra S.

2018-04-01

In the present study, we prepared zinc borates using aqueous phase synthesis under moderate pressures (MP) (<150 psi) with ethanol as a co-solvent in the presence of a quaternary ammonium surfactant-Cetyltrimethylammonium bromide (CTAB). 3D morphologies of self-assembled zinc borate (Zn(H2O)B2O4 · 0.12 H2O, Zn3B6O12 · 3.5H2O, ZnB2O4) resembling flower-like structures were obtained by varying temperature under moderate pressure conditions. Synthesized zinc borates’ florets were morphologically characterized by Field Emission Scanning Electron Microscopy. The x-ray diffractions of borate species reveal rhombohydra, monoclinic and cubic phases of zinc borate crystals as a function of process temperature. Additionally, thermal analysis confirms excellent dehydration/degradation behavior for the zinc borate crystals synthesized at moderate pressures and elevated temperatures and could be utilized as potential flame retardant fillers in the polymer matrices.

Bioactive borate glass coatings for titanium alloys.

PubMed

Peddi, Laxmikanth; Brow, Richard K; Brown, Roger F

2008-09-01

Bioactive borate glass coatings have been developed for titanium and titanium alloys. Glasses from the Na(2)O-CaO-B(2)O(3) system, modified by additions of SiO(2), Al(2)O(3), and P(2)O(5), were characterized and compositions with thermal expansion matches to titanium were identified. Infrared and X-ray diffraction analyses indicate that a hydroxyapatite surface layer forms on the borate glasses after exposure to a simulated body fluid for 2 weeks at 37 degrees C; similar layers form on 45S5 Bioglass((R)) exposed to the same conditions. Assays with MC3T3-E1 pre-osteoblastic cells show the borate glasses exhibit in vitro biocompatibility similar to that of the 45S5 Bioglass((R)). An enameling technique was developed to form adherent borate glass coatings on Ti6Al4V alloy, with adhesive strengths of 36 +/- 2 MPa on polished substrates. The results show these new borate glasses to be promising candidates for forming bioactive coatings on titanium substrates.

Spectroscopic Characterization of Extracellular Polymeric Substances from Escherichia coli and Serratia marcescens: Suppression using Sub-Inhibitory Concentrations of Bismuth Thiols

DOE Office of Scientific and Technical Information (OSTI.GOV)

Badireddy, Appala R.; Korpol, Bhoom Reddy; Chellam, Shankararaman

2008-10-21

Free and capsular EPS produced by Escherichia coli and Serratia marcescens were characterized in detail using Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), and Auger electron spectroscopy (AES). Total EPS production decreased upon treatment with sub-inhibitory concentrations of lipophilic bismuth thiols (bismuth dimercaptopropanol, BisBAL; bismuth ethanedithiol, BisEDT; and bismuth pyrithione, BisPYR), BisBAL being most effective. Bismuth thiols also influenced acetylation and carboxylation of polysaccharides in EPS from S. marcescens. Extensive homology between EPS samples in the presence and absence of bismuth was observed with proteins, polysaccharides, and nucleic acids varying predominantly only in the total amount expressed. Secondmore » derivative analysis of the amide I region of FTIR spectra revealed decreases in protein secondary structures in the presence of bismuth thiols. Hence, anti-fouling properties of bismuth thiols appear to originate in their ability to suppress O-acetylation and protein secondary structures in addition to total EPS secretion.« less

SEPARATION OF PLUTONIUM HYDROXIDE FROM BISMUTH HYDROXIDE

DOEpatents

Watt, G.W.

1958-08-19

An tmproved method is described for separating plutonium hydroxide from bismuth hydroxide. The end product of the bismuth phosphate processes for the separation amd concentration of plutonium is a inixture of bismuth hydroxide amd plutonium hydroxide. It has been found that these compounds can be advantageously separated by treatment with a reducing agent having a potential sufficient to reduce bismuth hydroxide to metalltc bisinuth but not sufficient to reduce the plutonium present. The resulting mixture of metallic bismuth and plutonium hydroxide can then be separated by treatment with a material which will dissolve plutonium hydroxide but not metallic bismuth. Sodiunn stannite is mentioned as a preferred reducing agent, and dilute nitric acid may be used as the separatory solvent.

METHOD OF MAKING UO$sub 2$-Bi SLURRIES

DOEpatents

Hahn, H.T.

1960-05-24

A process is given of preparing an easily dispersible slurry of uranium dioxide in bismuth. A mixture of bismuth oxide, uranium, and bismuth are heated in a capsule to a temperature over the melting point of bismuth oxide. The amount of bismuth oxide used is less than that stoichiometrically required because the oxygen in the capsule also enters into the reaction.

40 CFR 180.1121 - Boric acid and its salts, borax (sodium borate decahydrate), disodium octaborate tetrahydrate...

Code of Federal Regulations, 2014 CFR

2014-07-01

... 40 Protection of Environment 24 2014-07-01 2014-07-01 false Boric acid and its salts, borax... salts, borax (sodium borate decahydrate), disodium octaborate tetrahydrate, boric oxide (boric anhydride... its salts, borax (sodium borate decahydrate), disodium octaborate tetrahydrate, boric oxide (boric...

40 CFR 180.1121 - Boric acid and its salts, borax (sodium borate decahydrate), disodium octaborate tetrahydrate...

Code of Federal Regulations, 2011 CFR

2011-07-01

... 40 Protection of Environment 24 2011-07-01 2011-07-01 false Boric acid and its salts, borax... salts, borax (sodium borate decahydrate), disodium octaborate tetrahydrate, boric oxide (boric anhydride... its salts, borax (sodium borate decahydrate), disodium octaborate tetrahydrate, boric oxide (boric...

40 CFR 180.1121 - Boric acid and its salts, borax (sodium borate decahydrate), disodium octaborate tetrahydrate...

Code of Federal Regulations, 2012 CFR

2012-07-01

... 40 Protection of Environment 25 2012-07-01 2012-07-01 false Boric acid and its salts, borax... salts, borax (sodium borate decahydrate), disodium octaborate tetrahydrate, boric oxide (boric anhydride... its salts, borax (sodium borate decahydrate), disodium octaborate tetrahydrate, boric oxide (boric...

40 CFR 180.1121 - Boric acid and its salts, borax (sodium borate decahydrate), disodium octaborate tetrahydrate...

Code of Federal Regulations, 2013 CFR

2013-07-01

... 40 Protection of Environment 25 2013-07-01 2013-07-01 false Boric acid and its salts, borax... salts, borax (sodium borate decahydrate), disodium octaborate tetrahydrate, boric oxide (boric anhydride... its salts, borax (sodium borate decahydrate), disodium octaborate tetrahydrate, boric oxide (boric...

76 FR 74831 - Aging Management of Stainless Steel Structures and Components in Treated Borated Water

Federal Register 2010, 2011, 2012, 2013, 2014

2011-12-01

... exposed to treated borated water. In response to a request from the Nuclear Energy Institute (NEI), the... NUCLEAR REGULATORY COMMISSION [NRC-2011-0256] Aging Management of Stainless Steel Structures and Components in Treated Borated Water AGENCY: Nuclear Regulatory Commission. ACTION: Draft interim staff...

Structure and luminescence spectra of lutetium and yttrium borates synthesized from ammonium nitrate melt

NASA Astrophysics Data System (ADS)

Klassen, Nikolay V.; Shmurak, Semion Z.; Shmyt'ko, Ivan M.; Strukova, Galina K.; Derenzo, Stephen E.; Weber, Marvin J.

2005-01-01

Lutetium and yttrium borates doped with europium, terbium, gadolinium, etc. have been synthesized by dissolving initial oxides and nitrates in ammonium nitrate melt and thermal decomposition of the solvent. Annealings in the range of 500-1100°C modified the dimensions of the grains from 2 to 3 nm to more than 100 nm. Significant dependence of the structure of lutetium borate on slight doping with rare earth ions has been found: terbium makes high-temperature vaterite phase preferential at room temperature, whereas europium stabilizes low-temperature calcite phase. Influence of the structure of the borates on the pattern of the luminescence spectra of europium dopant was observed. Possibilities for manufacturing of scintillating lutetium borate ceramics by means of this method of synthesis are discussed.

Angiogenic effects of borate glass microfibers in a rodent model.

PubMed

Lin, Yinan; Brown, Roger F; Jung, Steven B; Day, Delbert E

2014-12-01

The primary objective of this research was to evaluate the use of bioactive borate-based glass microfibers for angiogenesis in soft tissue repair applications. The effect of these fibers on growth of capillaries and small blood vessels was compared to that of 45S5 silica glass microfibers and sham implant controls. Compressed mats of three types of glass microfibers were implanted subcutaneously in rats and tissues surrounding the implant sites histologically evaluated 2-4 weeks post surgery. Bioactive borate glass 13-93B3 supplemented with 0.4 wt % copper promoted extensive angiogenesis as compared to silica glass microfibers and sham control tissues. The angiogenic responses suggest the copper-containing 13-93B3 microfibers may be effective for treating chronic soft tissue wounds. A second objective was to assess the possible systemic cytotoxicity of dissolved borate ions and other materials released from implanted borate glass microfibers. Cytotoxicity was assessed via histological evaluation of kidney tissue collected from animals 4 weeks after subcutaneously implanting high amounts of the borate glass microfibers. The evaluation of the kidney tissue from these animals showed no evidence of chronic histopathological changes in the kidney. The overall results indicate the borate glass microfibers are safe and effective for soft tissue applications. © 2014 Wiley Periodicals, Inc.

Optical properties of Nd3+ doped bismuth zinc borate glasses

NASA Astrophysics Data System (ADS)

Shanmugavelu, B.; Venkatramu, V.; Ravi Kanth Kumar, V. V.

2014-03-01

Glasses with compositions of (100-x) (Bi2ZnOB2O6) - x Nd2O3 (where x = 0.1, 0.3, 0.5, 1 and 2 mol%) were prepared by melt quenching method and characterized through optical absorption, emission and decay curve measurements. Optical absorption spectra have been analyzed using Judd-Ofelt theory. The emission spectra exhibit three peaks at 919, 1063 and 1337 nm corresponding to 4F3/2 to 4I9/2, 4I11/2 and 4I13/2 transitions in the near infrared region. The emission intensity of the 4F3/2 to 4I11/2 transition increases with increase of Nd3+ concentration up to 1 mol% and then concentration quenching is observed for 2 mol% of Nd3+ concentration. The lifetimes for the 4F3/2 level are found to decrease with increase in Nd2O3 concentration in the glasses. The decay curves of the glass up to 0.3 mol% of Nd3+ exhibit single exponential nature and thereafter the curves become nonexponential nature (0.5, 1 and 2 mol%). The nonexponential curve has been fitted to the Inokuti-Hirayama model to understand the nature of energy transfer process.

Optical properties of Nd3+ doped bismuth zinc borate glasses.

PubMed

Shanmugavelu, B; Venkatramu, V; Ravi Kanth Kumar, V V

2014-03-25

Glasses with compositions of (100-x) (Bi2ZnOB2O6) -x Nd2O3 (where x=0.1, 0.3, 0.5, 1 and 2 mol%) were prepared by melt quenching method and characterized through optical absorption, emission and decay curve measurements. Optical absorption spectra have been analyzed using Judd-Ofelt theory. The emission spectra exhibit three peaks at 919, 1063 and 1337 nm corresponding to (4)F3/2 to (4)I9/2, (4)I11/2 and (4)I13/2 transitions in the near infrared region. The emission intensity of the (4)F3/2 to (4)I11/2 transition increases with increase of Nd(3+) concentration up to 1 mol% and then concentration quenching is observed for 2 mol% of Nd(3+) concentration. The lifetimes for the (4)F3/2 level are found to decrease with increase in Nd2O3 concentration in the glasses. The decay curves of the glass up to 0.3 mol% of Nd(3+) exhibit single exponential nature and thereafter the curves become nonexponential nature (0.5, 1 and 2 mol%). The nonexponential curve has been fitted to the Inokuti-Hirayama model to understand the nature of energy transfer process. Copyright © 2013 Elsevier B.V. All rights reserved.

Method for producing a borohydride

DOEpatents

Kong, Peter C [Idaho Falls, ID

2008-09-02

A method for producing a borohydride is described and which includes the steps of providing a source of borate; providing a material which chemically reduces the source of the borate to produce a borohydride; and reacting the source of borate and the material by supplying heat at a temperature which substantially effects the production of the borohydride.

Method for producing a borohydride

DOEpatents

Kong, Peter C.

2010-06-22

A method for producing a borohydride is described that includes the steps of providing a source of borate; providing a material that chemically reduces the source of the borate to produce a borohydride; and reacting the source of the borate and the material by supplying heat at a temperature that substantially effects the production of the borohydride.

Bismuth-doped optical fibres: A new breakthrough in near-IR lasing media

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dianov, Evgenii M

Recent results demonstrate that bismuth-doped optical fibres have considerable potential as near-IR active lasing media. This paper examines bismuth-doped fibres intended for the fabrication of fibre lasers and optical amplifiers and reviews recent results on the luminescence properties of various types of bismuth-doped fibres and the performance of bismuth-doped fibre lasers and optical amplifiers for the spectral range 1150 - 1550 nm. Problems are discussed that have yet to be solved in order to improve the efficiency of the bismuth lasers and optical amplifiers. (optical fibres, lasers and amplifiers. properties and applications)

First Observations of Boron on Mars and Implications for Gale Crater Geochemistry

NASA Astrophysics Data System (ADS)

Gasda, P. J.; Haldeman, E. B.; Wiens, R. C.; Rapin, W.; Frydenvang, J.; Maurice, S.; Clegg, S. M.; Delapp, D.; Sanford, V.; McInroy, R.

2016-12-01

Borates are potentially important precursor materials for the origin of life on Earth. It has been shown that borates are required to stabilize ribose, a component of RNA, when produced by the formose reaction, a prebiotically plausible mechanism to produce ribose from formaldehyde. Evaporites, including borates, also shed light on the history of aqueous activity on Mars. The ChemCam instrument onboard the NASA Curiosity rover provides quantitative elemental compositions of targets in Gale Crater, Mars, using laser-induced breakdown spectroscopy (LIBS). Laboratory observations of Fe-free targets indicate that a LIBS emission line is visible with as little as 10 ppm B. We have observed B lines in 23 calcium sulfate veins in Gale Crater: 3 in Yellowknife Bay and 20 in the Murray lacustrine mudstone and the Stimson eolian sandstone units since sol 727, as Curiosity arrived at the base of Mt. Sharp, a 5 km sedimentary mound in the center of Gale Crater. To calibrate these observations, samples composed of borates diluted with Hawaiian basalt have been analyzed using the LANL ChemCam engineering model. Preliminary results show that the Gale Crater veins have between 10-100 ppm B. One possible explanation for borates in veins is that Gale Lake evaporated, depositing evaporites, including borates. Later, Gale Crater was partially buried and its lacustrine and overlying eolian units were lithified and fractured. Water flowed through the evaporite-rich layers, partially dissolving them. Fluid moved through the fractures, re-precipitating the borates and sulfates as veins. ChemCam cannot directly determine mineralogy, but B is likely present as borax as the dominate borate phase in these veins, based on previous estimates of vein fluid temperature. Borates forming in this environment tend to precipitate from mildly alkaline fluids. The fluid temperature and pH implies these veins were potentially habitable environments.

Improved synthesis of fine zinc borate particles using seed crystals

NASA Astrophysics Data System (ADS)

Gürhan, Deniz; Çakal, Gaye Ö.; Eroğlu, İnci; Özkar, Saim

2009-03-01

Zinc borate is a flame retardant additive used in polymers, wood applications and textile products. There are different types of zinc borate having different chemical compositions and structures. In this study, the production of zinc borate having the molecular formula of 2ZnO·3B 2O 3·3.5H 2O was reexamined by studying the effects of reaction parameters on the properties of product as well as the reaction kinetics. Production of zinc borate from the reaction of boric acid and zinc oxide in the presence of seed crystals was performed in a continuously stirred, temperature-controlled batch reactor having a volume of 1.5 L. Samples taken in regular time intervals during the experiments were analyzed for the concentration of zinc oxide and boron oxide in the solid as well as for the conversion of zinc oxide to zinc borate versus time. The zinc borate production reaction was fit to the logistic model. The reaction rate, reaction completion time, composition and particle size distribution of zinc borate product were determined by varying the following parameters: the boric acid to zinc oxide ratio (H 3BO 3:ZnO=3:1, 3.5:1, 5:1 and 7:1), the particle size of zinc oxide (10 and 25 μm), stirring rate (275, 400, 800 and 1600 rpm), temperature (75, 85 and 95 °C) and the size of seed crystals (10 and 2 μm). The products were also analyzed for particle size distribution. The experimental results showed that the reaction rate increases with the increase in H 3BO 3:ZnO ratio, particle size of zinc oxide, stirring rate and temperature. Concomitantly, the reaction completion time is decreased by increasing the H 3BO 3:ZnO ratio, stirring rate and temperature. The average particle sizes of the zinc borate products are in the range 4.3-16.6 μm (wet dispersion analysis).

Chemical structure of bismuth compounds determines their gastric ulcer healing efficacy and anti-Helicobacter pylori activity.

PubMed

Sandha, G S; LeBlanc, R; Van Zanten, S J; Sitland, T D; Agocs, L; Burford, N; Best, L; Mahoney, D; Hoffman, P; Leddin, D J

1998-12-01

The recognition of the role of Helicobacter pylori in the pathogenesis of peptic ulcer disease has led to renewed interest in bismuth pharmacology since bismuth compounds have both anti-Helicobacter pylori and ulcer healing properties. The precise chemical structure of current bismuth compounds is not known. This has hindered the development of new and potentially more efficacious formulations. We have created two new compounds, 2-chloro-1,3-dithia-2-bismolane (CDTB) and 1,2-[bis(1,3-dithia-2-bismolane)thio]ethane (BTBT), with known structure. In a rat model of gastric ulceration, BTBT was comparable to, and CDTB was significantly less effective than colloidal bismuth subcitrate in healing cryoprobe-induced ulcers. However, both BTBT and CDTB inhibited H. pylori growth in vitro at concentrations <1/10 that of colloidal bismuth subcitrate. The effects on ulcer healing are not mediated by suppression of acid secretion, pepsin inhibition, or prostaglandin production. Since all treated animals received the same amount of elemental bismuth, it appears that the efficacy of bismuth compounds varies with compound structure and is not simply dependent on the delivery of bismuth ion. Because the structure of the novel compounds is known, our understanding of the relationship of bismuth compound structure and to biologic activity will increase. In the future it may be possible to design other novel bismuth compounds with more potent anti-H. pylori and ulcer healing effects.

Mineral resource of the month: bismuth

USGS Publications Warehouse

Carlin, James F.

2006-01-01

Bismuth compounds are most known for their soothing effects on the stomach, wounds and sores. These properties make the compounds an essential part of many medicinal and cosmetic preparations, which until 1930 accounted for about 90 percent of the bismuth used. The subsequent development of low-melting alloys and chemical catalysts containing bismuth, as well as its use as an additive to casting alloys, has resulted in a wider variety of industrial applications for bismuth.

Effect of bismuth subcitrate on amphibian gastroduodenal bicarbonate secretion.

PubMed Central

Shorrock, C J; Crampton, J R; Gibbons, L C; Rees, W D

1989-01-01

The ulcer healing and cytoprotective properties of colloidal bismuth (De-Nol) are well established although its mode of action is unclear. We have examined the action of bismuth subcitrate, the active ingredient of De-Nol, on gastroduodenal bicarbonate secretion by isolated amphibian mucosa. Addition of bismuth subcitrate (10(-6) to 10(-4) M) to the luminal solution produced a dose dependent increase in bicarbonate secretion from both gastric and duodenal mucosae without a change in transmucosal potential difference. The magnitude of this stimulation was greater for gastric than duodenal mucosae at all dose ranges. A second bismuth salt, bismuth oxynitrate, produced similar increases in bicarbonate secretion from gastric mucosae. Pretreatment of gastric mucosa with the cyclooxygenase inhibitor, indomethacin (10(-5) and 10(-4) M), did not abolish the secretory response to bismuth subcitrate. Similar treatment with the chloride transport inhibitor, 4-acetamido-4'-isothiocyanatostilbene-2,2'-disulfonic acid (SITS) (10(-3) M) prevented the secretory response to bismuth subcitrate. PMID:2788112

40 CFR 721.1880 - Borate(1-), tris(acetato-.kappa.O)hydro-, sodium, (T-4)-.

Code of Federal Regulations, 2010 CFR

2010-07-01

...)hydro-, sodium, (T-4)-. 721.1880 Section 721.1880 Protection of Environment ENVIRONMENTAL PROTECTION... New Uses for Specific Chemical Substances § 721.1880 Borate(1-), tris(acetato-.kappa.O)hydro-, sodium... substance identified as borate(1-), tris(acetato-.kappa.O)hydro-, sodium, (T-4)- (PMN P-00-0922; CAS No...

40 CFR 721.1880 - Borate(1-), tris(acetato-.kappa.O)hydro-, sodium, (T-4)-.

Code of Federal Regulations, 2011 CFR

2011-07-01

...)hydro-, sodium, (T-4)-. 721.1880 Section 721.1880 Protection of Environment ENVIRONMENTAL PROTECTION... New Uses for Specific Chemical Substances § 721.1880 Borate(1-), tris(acetato-.kappa.O)hydro-, sodium... substance identified as borate(1-), tris(acetato-.kappa.O)hydro-, sodium, (T-4)- (PMN P-00-0922; CAS No...

40 CFR 180.1121 - Boric acid and its salts, borax (sodium borate decahydrate), disodium octaborate tetrahydrate...

Code of Federal Regulations, 2010 CFR

2010-07-01

... 40 Protection of Environment 23 2010-07-01 2010-07-01 false Boric acid and its salts, borax (sodium borate decahydrate), disodium octaborate tetrahydrate, boric oxide (boric anhydride), sodium borate and sodium metaborate; exemptions from the requirement of a tolerance. 180.1121 Section 180.1121 Protection of Environment ENVIRONMENTAL PROTECTION...

PROCESS OF COATING METALS WITH BISMUTH OR BISMUTH-BASE ALLOYS

DOEpatents

Beach, J.G.

1958-01-28

A method is described for producing coatings of bismuth or bismuth alloys on a metal base. This is accomplished by electrodepositing the bismuth from an aqueous solution of BiCl/sub 3/, and by making the metal base alternately the cathode and the anode, the cathode periods being twice as long as the anode periods. In one embodiment a nickel coating is first electrodeposited in a known way, and this nickel plated piece is tae base upon which tae bismuth is deposited by the process of this patent. The coated piece is then heat treated to produce a homogeneous Ni--Bi alloy by diffusion.

Li{sub 2}Sr{sub 4}B{sub 12}O{sub 23}: A new alkali and alkaline-earth metal mixed borate with [B{sub 10}O{sub 18}]{sup 6-} network and isolated [B{sub 2}O{sub 5}]{sup 4-} unit

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang Min; Graduate University of Chinese Academy of Sciences, Beijing 100049; Pan Shilie, E-mail: slpan@ms.xjb.ac.cn

2012-06-15

A novel ternary lithium strontium borate Li{sub 2}Sr{sub 4}B{sub 12}O{sub 23} crystal with size up to 20 mm Multiplication-Sign 10 mm Multiplication-Sign 4 mm has been grown via the top-seeded solution growth method below 730 Degree-Sign C. Single-crystal XRD analyses showed that Li{sub 2}Sr{sub 4}B{sub 12}O{sub 23} crystallizes in the monoclinic space group P2{sub 1}/c with a=6.4664(4) A, b=8.4878(4) A, c=15.3337(8) A, {beta}=102.02(3) Degree-Sign , Z=2. The crystal structure is composed of [B{sub 10}O{sub 18}]{sup 6-} network and isolated [B{sub 2}O{sub 5}]{sup 4-} unit. The IR spectrum further confirmed the presence of both BO{sub 3} and BO{sub 4} groups. TG-DSCmore » and Transmission spectrum were reported. Band structures and density of states were calculated. - Graphical abstract: A new phase, Li{sub 2}Sr{sub 4}B{sub 12}O{sub 23}, has been discovered in the ternary M{sub 2}O-M Prime O-B{sub 2}O{sub 3} (M=alkali-metal, M Prime =alkalineearth metal) system. The crystal structure consists of [B{sub 10}O{sub 18}]{sup 6-} network and isolated [B{sub 2}O{sub 5}]{sup 4-} unit. Highlights: Black-Right-Pointing-Pointer Li{sub 2}Sr{sub 4}B{sub 12}O{sub 23} is a a novel borate discovered in the M{sub 2}O-M Prime O-B{sub 2}O{sub 3} (M=alkali-metal, M Prime =alkaline-earth metal) system. Black-Right-Pointing-Pointer Li{sub 2}Sr{sub 4}B{sub 12}O{sub 23} crystal structure has a three-dimensional crystal structure with [B{sub 10}O{sub 18}]{sup 6-} network and isolated [B{sub 2}O{sub 5}]{sup 4-} unit. Black-Right-Pointing-Pointer Sr{sub 1} and Sr{sub 2} are located in two different channels constructed by {sup 3}{sub {infinity}}[B{sub 10}O{sub 18}] network.« less

Influence of sodium borate on the early age hydration of calcium sulfoaluminate cement

DOE Office of Scientific and Technical Information (OSTI.GOV)

Champenois, Jean-Baptiste; Dhoury, Mélanie; Cau Dit Coumes, Céline, E-mail: celine.cau-dit-coumes@cea.fr

Calcium sulfoaluminate (CSA) cements are potential candidates for the conditioning of radioactive wastes with high sodium borate concentrations. This work thus investigates early age hydration of two CSA cements with different gypsum contents (0 to 20%) as a function of the mixing solution composition (borate and NaOH concentrations). Gypsum plays a key role in controlling the reactivity of cement. When the mixing solution is pure water, increasing the gypsum concentration accelerates cement hydration. However, the reverse is observed when the mixing solution contains sodium borate. Until gypsum exhaustion, the pore solution pH remains constant at ~ 10.8, and a poorlymore » crystallized borate compound (ulexite) precipitates. A correlation is established between this transient precipitation and the hydration delay. Decreasing the gypsum content in the binder, or increasing the sodium content in the mixing solution, are two ways of reducing the stability of ulexite, thus decreasing the hydration delay.« less

Preservation of tissue specimens during transport to mycobacteriology laboratories.

PubMed Central

Richards, W D; Wright, H S

1983-01-01

Chloramine-T and sodium borate solutions were evaluated for their effectiveness in preserving Mycobacterium bovis and controlling the growth of non-mycobacterial contaminants on tissue specimens during transport to laboratories. The number of culturable M. bovis cells in suspension was reduced by 5.1 log10 upon exposure to chloramine-T solution and by less than 1 log10 upon exposure to sodium borate solution for 7 days. Reinoculation of laboratory media (because of overgrowth by non-mycobacterial contaminants) was required for 52.6% of 190 routine bovine tissue specimens shipped refrigerated in chloramine-T solution and for 6.1% of 520 specimens shipped unrefrigerated in sodium borate solution. M. bovis was isolated from bovine tissue stored in sodium borate solution at 23 degrees C for 17 weeks and at 4 degrees C for 25 weeks. Unrefrigerated sodium borate solution has been used successfully to ship tissue specimens to our laboratory for the past 11 years. PMID:6341397

Femtosecond laser-induced refractive index modification in multicomponent glasses

NASA Astrophysics Data System (ADS)

Bhardwaj, V. R.; Simova, E.; Corkum, P. B.; Rayner, D. M.; Hnatovsky, C.; Taylor, R. S.; Schreder, B.; Kluge, M.; Zimmer, J.

2005-04-01

We present a comprehensive study on femtosecond laser-induced refractive index modification in a wide variety of multicomponent glasses grouped as borosilicate, aluminum-silicate, and heavy-metal oxide glasses along with lanthanum-borate and sodium-phosphate glasses. By using high-spatial resolution refractive index profiling techniques, we demonstrate that under a wide range of writing conditions the refractive index modification in multicomponent glasses can be positive, negative, or nonuniform, and exhibits a strong dependence on the glass composition. With the exception of some aluminum-silicate glasses all other glasses exhibited a negative/nonuniform index change. We also demonstrate direct writing of waveguides in photosensitive Foturan® glass with a femtosecond laser without initiating crystallization by thermal treatment. Upon ceramization of lithium-aluminum-silicate glasses such as Foturan®, Zerodur®, and Robax® we observe switching of laser-induced refractive index change from being positive to negative. The measured transmission losses in the waveguides at 1550nm agree with the index profile measurements in alkali-free aluminum-silicate glasses.

TL and EPR studies of Cu, Ag and P doped Li2B4O7 phosphor

NASA Astrophysics Data System (ADS)

Can, N.; Karali, T.; Townsend, P. D.; Yildiz, F.

2006-05-01

Key characteristics of a newly prepared tissue-equivalent, highly sensitive thermoluminescence dosimeter, Li2B4O7:Cu,Ag,P, are presented. The material was developed at the Institute of Nuclear Sciences, Belgrade, in the form of sintered pellets. A new preparation procedure has greatly increased the sensitivity of the basic copper activated lithium borate and the glow curve of Li2B4O7 : Cu,Ag,P consists of a well-defined main dosimetric peak situated at about 460-465 K with a sensitivity which is about four to five times higher than that of LiF : Mg,Ti (TLD-100). The exceptionally good response features of Li2B4O7 : Cu,Ag,P are attributed to the incorporation of Cu as a dopant. Both low and high temperature emission spectra are presented and the origins of the various emission bands are considered. Additional data are provided from electron paramagnetic resonance measurements.

Synthesis and optical property of holmium doped Lithium lead borate glasses

NASA Astrophysics Data System (ADS)

Usharani, V. L.; Eraiah, B.

2017-05-01

The new glass system 60B2O3-30PbO-(10-x)Li2O-xHo2O3 (where x =0, 0.1, 0.3 and 0.5 mol%) were prepared by conventional melt quenching method. The XRD spectrum confirms the amorphous nature of the sample. The density of these glasses is measured by using Archimedes principle, the values range from 4.23 g/cm-3 to 4.34 g/cm-3 and the corresponding molar volumes are calculated. The optical absorbance studies were carried out on these glasses in the wavelength range of 200nm to 1100nm. The measured optical direct band gap energies were in the range of 3.072eV to 3.259eV and the optical indirect band gap energies in the range of 2.658eV to 2.846eV. The refractive indices of these glasses were measured by using Abbe refractometer and the corresponding polarizabilities of oxide ions are calculated by using Lorentz-Lorentz relations.

40 CFR 471.10 - Applicability; description of the lead-tin-bismuth forming subcategory.

Code of Federal Regulations, 2014 CFR

2014-07-01

...-tin-bismuth forming subcategory. 471.10 Section 471.10 Protection of Environment ENVIRONMENTAL... METAL POWDERS POINT SOURCE CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.10 Applicability; description of the lead-tin-bismuth forming subcategory. This subpart applies to discharges of pollutants to...

40 CFR 471.10 - Applicability; description of the lead-tin-bismuth forming subcategory.

Code of Federal Regulations, 2012 CFR

2012-07-01

...-tin-bismuth forming subcategory. 471.10 Section 471.10 Protection of Environment ENVIRONMENTAL... METAL POWDERS POINT SOURCE CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.10 Applicability; description of the lead-tin-bismuth forming subcategory. This subpart applies to discharges of pollutants to...

40 CFR 471.10 - Applicability; description of the lead-tin-bismuth forming subcategory.

Code of Federal Regulations, 2011 CFR

2011-07-01

...-tin-bismuth forming subcategory. 471.10 Section 471.10 Protection of Environment ENVIRONMENTAL... POINT SOURCE CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.10 Applicability; description of the lead-tin-bismuth forming subcategory. This subpart applies to discharges of pollutants to waters of the...

40 CFR 471.10 - Applicability; description of the lead-tin-bismuth forming subcategory.

Code of Federal Regulations, 2013 CFR

2013-07-01

...-tin-bismuth forming subcategory. 471.10 Section 471.10 Protection of Environment ENVIRONMENTAL... METAL POWDERS POINT SOURCE CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.10 Applicability; description of the lead-tin-bismuth forming subcategory. This subpart applies to discharges of pollutants to...

40 CFR 471.10 - Applicability; description of the lead-tin-bismuth forming subcategory.

Code of Federal Regulations, 2010 CFR

2010-07-01

...-tin-bismuth forming subcategory. 471.10 Section 471.10 Protection of Environment ENVIRONMENTAL... POINT SOURCE CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.10 Applicability; description of the lead-tin-bismuth forming subcategory. This subpart applies to discharges of pollutants to waters of the...

Wide Operating Temperature Range Electrolytes for High Voltage and High Specific Energy Li-Ion Cells

NASA Technical Reports Server (NTRS)

Smart, M. C.; Hwang, C.; Krause, F. C.; Soler, J.; West, W. C.; Ratnakumar, B. V.; Amine, K.

2012-01-01

A number of electrolyte formulations that have been designed to operate over a wide temperature range have been investigated in conjunction with layered-layered metal oxide cathode materials developed at Argonne. In this study, we have evaluated a number of electrolytes in Li-ion cells consisting of Conoco Phillips A12 graphite anodes and Toda HE5050 Li(1.2)Ni(0.15)Co(0.10)Mn(0.55)O2 cathodes. The electrolytes studied consisted of LiPF6 in carbonate-based electrolytes that contain ester co-solvents with various solid electrolyte interphase (SEI) promoting additives, many of which have been demonstrated to perform well in 4V systems. More specifically, we have investigated the performance of a number of methyl butyrate (MB) containing electrolytes (i.e., LiPF6 in ethylene carbonate (EC) + ethyl methyl carbonate (EMC) + MB (20:20:60 v/v %) that contain various additives, including vinylene carbonate, lithium oxalate, and lithium bis(oxalato)borate (LiBOB). When these systems were evaluated at various rates at low temperatures, the methyl butyrate-based electrolytes resulted in improved rate capability compared to cells with all carbonate-based formulations. It was also ascertained that the slow cathode kinetics govern the generally poor rate capability at low temperature in contrast to traditionally used LiNi(0.80)Co(0.15)Al(0.05)O2-based systems, rather than being influenced strongly by the electrolyte type.

Hydrothermal synthesis of Ni 2FeBO 5 in near-supercritical PWR coolant and possible effects of neutron-induced 10B fission in fuel crud

NASA Astrophysics Data System (ADS)

Sawicki, Jerzy A.

2011-08-01

The hydrothermal synthesis of a nickel-iron oxyborate, Ni 2FeBO 5, known as bonaccordite, was investigated at pressures and temperatures that might occur at the surface of high-power fuel rods in PWR cores and in supercritical water reactors, especially during localized departures from nucleate boiling and dry-outs. The tests were performed using aqueous mixtures of nickel and iron oxides with boric acid or boron oxide, and as a function of lithium hydroxide addition, temperature and time of heating. At subcritical temperatures nickel ferrite NiFe 2O 4 was always the primary reaction product. High yield of Ni 2FeBO 5 synthesis started near critical water temperature and was strongly promoted by additions of LiOH up to Li/Fe and Li/B molar ratios in a range 0.1-1. The synthesis of bonaccordite was also promoted by other alkalis such as NaOH and KOH. The bonaccordite particles were likely formed by dissolution and re-crystallization by means of an intermediate nickel ferrite phase. It is postulated that the formation of Ni 2FeBO 5 in deposits of borated nickel and iron oxides on PWR fuel cladding can be accelerated by lithium produced in thermal neutron capture 10B(n,α) 7Li reactions. The process may also be aided in the reactor core by kinetic energy of α-particles and 7Li ions dissipated in the crud layer.

Laboratory evaluation of borate:amine:copper derivatives In wood for fungal decay protection

Treesearch

George Chen

2011-01-01

This study aimed to evaluate borate:amine:copper derivatives in wood for fungal decay protection as well as the permanence of copper and boron in wood. Each of four derivatives of borate:amine:copper prevented fungal decay in wood. Disodium tetraborate decahydrate (borax):amine:copper derivatives with 0.61-0.63% retention after water leaching prevented decay by...

Corrosion studies of titanium in borated water for TPX

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wilson, D.F.; Pawel, S.J.; DeVan, J.H.

1995-12-31

Corrosion testing was performed to demonstrate the compatibility of the titanium vacuum vessel with borated water. Borated water is proposed to fill the annulus of the double wall vacuum vessel to provide effective radiation shielding. Borating the water with 110 grams of boric acid per liter is sufficient to reduce the nuclear heating in the Toroidal Field Coil set and limit the activation of components external to the vacuum vessel. Constant extension rate tensile (CERT) and electrochemical potentiodynamic tests were performed. Results of the CERT tests confirm that stress corrosion cracking is not significant for Ti-6Al4V or Ti-3AI-2.5V. Welded andmore » unwelded specimens were tested in air and in borated water at 150{degree}C. Strength, elongation, and time to failure were nearly identical for all test conditions, and all the samples exhibited ductile failure. Potentiodynamic tests on Ti-6A1-4V and Ti in borated water as a function of temperature showed low corrosion rates over a wide passive potential range. Further, this passivity appeared stable to anodic potentials substantially greater than those expected from MHD effects.« less

Effect of modifying agents on the hydrophobicity and yield of zinc borate synthesized by zinc oxide

NASA Astrophysics Data System (ADS)

Acarali, Nil Baran; Bardakci, Melek; Tugrul, Nurcan; Derun, Emek Moroydor; Piskin, Sabriye

2013-06-01

The aim of this study was to synthesize zinc borate using zinc oxide, reference boric acid, and reference zinc borate (reference ZB) as the seed, and to investigate the effects of modifying agents and reaction parameters on the hydrophobicity and yield, respectively. The reaction parameters include reaction time (1-5 h), reactant ratio (H3BO3/ZnO by mass: 2-5), seed ratio (seed crystal/(H3BO3+ZnO) by mass: 0-2wt%), reaction temperature (50-120°C), cooling temperature (10-80°C), and stirring rate (400-700 r/min); the modifying agents involve propylene glycol (PG, 0-6wt%), kerosene (1wt%-6wt%), and oleic acid (OA, 1wt%-6wt%) with solvents (isopropyl alcohol (IPA), ethanol, and methanol). The results of reaction yield obtained from either magnetically or mechanically stirred systems were compared. Zinc borate produced was characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), and contact angle tests to identify the hydrophobicity. In conclusion, zinc borate is synthesized successfully under the optimized reaction conditions, and the different modifying agents with various solvents affect the hydrophobicity of zinc borate.

Novel method for early investigation of bioactivity in different borate bio-glasses

NASA Astrophysics Data System (ADS)

Abdelghany, A. M.

Some ternary borate glasses were prepared and corrosion behavior of such ternary borate glasses after immersion in aqueous dilute phosphate solution was studied using different immersion times. Fourier transform infrared (FTIR) absorption spectral measurements were done before and after immersion in the mentioned solution for extended times up to 2 days to justify the appearance of the characteristic FTIR bands due to calcium phosphate (hydroxyapatite (HA)) which is considered as the potential indication of bioactivity. Experimental IR data confirm the beginning of the appearance of FTIR bands at about 580 and 620 cm-1 after 3 days and the complete resolution with its characteristic split form after 1 week and more. Deconvolution analysis technique (DAT) of the FTIR spectrum was employed to investigate the bioactivity of such ternary borate system after a short period of immersion. The corrosion behavior of such glasses is explained in relation to a suggested hydrolysis followed by direct dissolution mechanism. The ease of dissolution of all the borate glasses constituents explains the formation of calcium phosphate and conversion to crystalline hydroxyapatite within the borate glass matrix. X-ray diffraction may be used to retrace the structural changes and degree of crystallinity of the prepared glasses.

Development of Natural Anthocyanin Dye-Doped Silica Nanoparticles for pH and Borate-Sensing Applications

NASA Astrophysics Data System (ADS)

Ha, Chu T.; Lien, Nghiem T. Ha; Anh, Nguyen D.; Lam, Nguyen L.

2017-12-01

Anthocyanin belongs to a large group of phenolic compounds called flavonoids. It is found primarily in fruits, flowers, roots and other parts of higher plants. Within the black carrot, it has been found that the cyanidin component 1,2 diol was the major anthocyanine. Since the terminal thiols potentially display chemical interactions with borate additives, anthocyanin from the black carrot can act as a sensing material for detecting borate in the environment. As a natural dye, anthocyanin responds to pH change of the medium. Here, we present an application of black carrot dyes for pH sensing and for the detection of borate additives within meats. The dyes were encapsulated within a mesoporous silica (SiO2) matrix in order to prevent the sensing materials from dissolution into the aqueous medium. The encapsulation was done in situ during preparation of silica nanoparticles (size from 100 nm to 500 nm) following an advanced Stöber method. These anthocyanin-encapsulated silica nanoparticles show a clear color change from green in an aqueous solution free of borate to GRAY-red in the presence of borate additive and red (pH 2) to green (pH 10).

A medium range order structural connection to the configurational heat capacity of borate-silicate mixed glasses.

PubMed

Liu, Hao; Smedskjaer, Morten M; Tao, Haizheng; Jensen, Lars R; Zhao, Xiujian; Yue, Yuanzheng

2016-04-28

It has been reported that the configurational heat capacity (C(p,conf)) first increases and then becomes saturated with increasing B2O3/SiO2 ratio in borate-silicate mixed glasses. Through Raman spectroscopy measurements, we have, in this work, found an implication for the intermediate range order (IRO) structural connection to the composition dependence of the C(p,conf) of borate-silicate mixed glasses. In the silica-rich compositions, the C(p,conf) rapidly increases with increasing B2O3 content. This is attributed to the increase of the content of the B-O-Si network units ([B2Si2O8](2-)) and 6-membered borate rings with 1 or 2 B(4). In the boron-rich compositions, the C(p,conf) is almost constant, independent of the increase in the B2O3/SiO2 ratio. This is likely attributed to the counteraction between the decrease of the fraction of two types of metaborate groups and the increase of the fraction of other borate superstructural units (particularly 6-membered borate rings). The overall results suggest that the glasses containing more types of superstructural units have a larger C(p,conf).

BISMUTH PHOSPHATE CARRIER PROCESS FOR Pu RECOVERY

DOEpatents

Finzel, T.G.

1959-02-01

An improvement in the bismuth phosphate carrier precipitation process for recovering plutonium is described. It has been found that a more granular and more easily filterable carrier precipitiite is formed if the addition of the bismuth and phosphate ions is effected by first adding 9/10 of the bismuth ions necessary, then slowly adding all of the source of the phosphate ions to be incorporated in the precipitate, while digesting at 75 C and afterwards incorporating the remainder of the total bismuth ions necessary

Borate minerals and origin of the RNA world.

PubMed

Grew, Edward S; Bada, Jeffrey L; Hazen, Robert M

2011-08-01

The RNA World is generally thought to have been an important link between purely prebiotic (>3.7 Ga) chemistry and modern DNA/protein biochemistry. One concern about the RNA World hypothesis is the geochemical stability of ribose, the sugar moiety of RNA. Prebiotic stabilization of ribose by solutions associated with borate minerals, notably colemanite, ulexite, and kernite, has been proposed as one resolution to this difficulty. However, a critical unresolved issue is whether borate minerals existed in sufficient quantities on the primitive Earth, especially in the period when prebiotic synthesis processes leading to RNA took place. Although the oldest reported colemanite and ulexite are 330 Ma, and the oldest reported kernite, 19 Ma, boron isotope data and geologic context are consistent with an evaporitic borate precursor to 2400-2100 Ma borate deposits in the Liaoning and Jilin Provinces, China, as well as to tourmaline-group minerals at 3300-3450 Ma in the Barberton belt, South Africa. The oldest boron minerals for which the age of crystallization could be determined are the metamorphic tourmaline species schorl and dravite in the Isua complex (metamorphism between ca. 3650 and ca. 3600 Ma). Whether borates such as colemanite, ulexite and kernite were present in the Hadean (>4000 Ma) at the critical juncture when prebiotic molecules such as ribose required stabilization depends on whether a granitic continental crust had yet differentiated, because in its absence we see no means for boron to be sufficiently concentrated for borates to be precipitated.

Bursting at the Seams: Rippled Monolayer Bismuth on NbSe 2

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fang, Alan; Adamo, Carolina; Jia, Shuang

Bismuth, one of the heaviest semimetals in nature, ignited the interest of the materials-physics community for its potential impact on topological quantum-material systems that utilize its strong spin-orbit coupling (SOC) and unique orbital hybridization. In particular, recent theoretical predictions of unique topological and superconducting properties of thin bismuth films and interfaces prompted intense research on the growth of sub- to a few monolayers of bismuth on different substrates. Similar to bulk rhombohedral bismuth, the initial growth of bismuth films on most substrates results in buckled bilayers that either grow in the (111) or (110) directions, with a lattice constant closemore » to that of bulk Bi. By contrast, in this paper we show a new growth pattern for bismuth monolayers on NbSe 2. We find that the initial growth of Bi can form a strongly bonded commensurate layer, resulting in a compressively strained two-dimensional triangular lattice. A unique pattern of 1D ripples and domain walls is observed. The single layer of bismuth also introduces strong marks on the electronic properties at the surface.« less

Bursting at the Seams: Rippled Monolayer Bismuth on NbSe 2

DOE PAGES

Fang, Alan; Adamo, Carolina; Jia, Shuang; ...

2018-04-13

Bismuth, one of the heaviest semimetals in nature, ignited the interest of the materials-physics community for its potential impact on topological quantum-material systems that utilize its strong spin-orbit coupling (SOC) and unique orbital hybridization. In particular, recent theoretical predictions of unique topological and superconducting properties of thin bismuth films and interfaces prompted intense research on the growth of sub- to a few monolayers of bismuth on different substrates. Similar to bulk rhombohedral bismuth, the initial growth of bismuth films on most substrates results in buckled bilayers that either grow in the (111) or (110) directions, with a lattice constant closemore » to that of bulk Bi. By contrast, in this paper we show a new growth pattern for bismuth monolayers on NbSe 2. We find that the initial growth of Bi can form a strongly bonded commensurate layer, resulting in a compressively strained two-dimensional triangular lattice. A unique pattern of 1D ripples and domain walls is observed. The single layer of bismuth also introduces strong marks on the electronic properties at the surface.« less

Bioavailability and chronic toxicity of bismuth citrate to earthworm Eisenia andrei exposed to natural sandy soil.

PubMed

Omouri, Zohra; Hawari, Jalal; Fournier, Michel; Robidoux, Pierre Yves

2018-01-01

The present study describes bioavailability and chronic effects of bismuth to earthworms Eisenia andrei using OECD reproduction test. Adult earthworms were exposed to natural sandy soil contaminated artificially by bismuth citrate. Average total concentrations of bismuth in soil recovered by HNO 3 digestion ranged from 75 to 289mg/kg. Results indicate that bismuth decreased significantly all reproduction parameters of Eisenia andrei at concentrations ≥ 116mg/kg. However, number of hatched cocoons and number of juveniles seem to be more sensitive than total number of cocoons, as determined by IC 50 ; i.e., 182, 123 and > 289mg/kg, respectively. Bismuth did not affect Eisenia andrei growth and survival, and had little effect on phagocytic efficiency of coelomocytes. The low immunotoxicity effect might be explained by the involvement of other mechanisms i.e. bismuth sequestered by metal-binding compounds. After 28 days of exposure bismuth concentrations in earthworms tissue increased with increasing bismuth concentrations in soil reaching a stationary state of 21.37mg/kg dry tissue for 243mg Bi/kg dry soil total content. Data indicate also that after 56 days of incubation the average fractions of bismuth available extracted by KNO 3 aqueous solution in soil without earthworms varied from 0.0051 to 0.0229mg/kg, while in soil with earthworms bismuth concentration ranged between 0.310-1.347mg/kg dry soil. We presume that mucus and chelating agents produced by earthworms and by soil or/and earthworm gut microorganisms could explain this enhancement, as well as the role of dermal and ingestion routes of earthworms uptake to soil contaminant. Copyright © 2017 Elsevier Inc. All rights reserved.

Laboratory evaluation of borate/amine/zinc formulations for fungal decay protection

Treesearch

George C. Chen; Rebecca E. Ibach

2010-01-01

The goals of this study were to evaluate borate/amine/zinc formulations in wood for fungal decay protection as well as the permanence of zinc and boron in wood. Wood treated with each of four formulations of borate/amine/zinc prevented or decreased fungal degradation after a 12-week AWPA Standard soil-block test. For non-leached specimens, wood treated with borax/amine...

A mechanistic study of the interaction of water-soluble borate glass with apatite-bound heterocyclic nitrogen-containing bisphosphonates.

PubMed

Pramanik, Chandrani; Sood, Parveen; Niu, Li-Na; Yuan, He; Ghoshal, Sushanta; Henderson, Walter; Liu, Yaodong; Jang, Seung Soon; Kumar, Satish; Pashley, David H; Tay, Franklin R

2016-02-01

Long-term oral and intravenous use of nitrogen-containing bisphosphonates (N-BPs) is associated with osteonecrosis of the jaw. Although N-BPs bind strongly to bone surfaces via non-covalent bonds, it is possible for extrinsic ions to dissociate bound N-BPs from mineralized bone by competitive desorption. Here, we investigate the effects and mechanism of using an ionic cocktail derived from borate bioactive glass for sequestration of heterocyclic N-BPs bound to apatite. By employing solid-state and solution-state analytical techniques, we confirmed that sequestration of N-BPs from bisphosphonate-bound apatite occurs in the presence of the borate-containing ionic cocktail. Simulations by density functional theory computations indicate that magnesium cation and borate anion are well within the extent of the risedronate or zoledronate anion to form precipitate complexes. The sequestration mechanism is due to the borate anion competing with bisphosphonates for similar electron-deficient sites on the apatite surface for binding. Thus, application of the borate-containing ionic cocktail represents a new topical lavage approach for removing apatite-bound heterocyclic N-BPs from exposed necrotic bone in bisphosphonate-related osteonecrosis of the jaw. Long-term oral consumption and injections of nitrogen-containing bisphosphonates (N-BPs) may result in death of the jaw bone when there is traumatic injury to the bone tissues. To date, there is no effective treatment for such a condition. This work reported the use of an ionic cocktail derived from water-soluble borate glass microfibers to displace the most potent type of N-BPs that are bound strongly to the mineral component on bone surfaces. The mechanism responsible for such an effect has been identified to be cation-mediated complexation of borate anions with negatively-charged N-BPs, allowing them to be released from the mineral surface. This borate-containing cocktail may be developed into a novel topical rinse for removing mineral-bound N-BPs from exposed dead bone. Copyright © 2015 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Gravimetric Analysis of Bismuth in Bismuth Subsalicylate Tablets: A Versatile Quantitative Experiment for Undergraduate Laboratories

ERIC Educational Resources Information Center

Davis, Eric; Cheung, Ken; Pauls, Steve; Dick, Jonathan; Roth, Elijah; Zalewski, Nicole; Veldhuizen, Christopher; Coeler, Joel

2015-01-01

In this laboratory experiment, lower- and upper-division students dissolved bismuth subsalicylate tablets in acid and precipitated the resultant Bi[superscript 3+] in solution with sodium phosphate for a gravimetric determination of bismuth subsalicylate in the tablets. With a labeled concentration of 262 mg/tablet, the combined data from three…

Hydrothermal synthesis of bismuth germanium oxide

DOEpatents

Boyle, Timothy J.

2016-12-13

A method for the hydrothermal synthesis of bismuth germanium oxide comprises dissolving a bismuth precursor (e.g., bismuth nitrate pentahydrate) and a germanium precursor (e.g., germanium dioxide) in water and heating the aqueous solution to an elevated reaction temperature for a length of time sufficient to produce the eulytite phase of bismuth germanium oxide (E-BGO) with high yield. The E-BGO produced can be used as a scintillator material. For example, the air stability and radioluminescence response suggest that the E-BGO can be employed for medical applications.

Bismuth, Metronidazole, and Tetracycline

MedlinePlus

Helidac® (as a kit containing Bismuth Subsalicylate, Metronidazole, Tetracycline) ... Bismuth, metronidazole, and tetracycline is used along with other ulcer medications to treat duodenal ulcers. It is in a ...

Low-energy collisionally activated dissociation of pentose-borate complexes

NASA Astrophysics Data System (ADS)

Pepi, Federico; Garzoli, Stefania; Tata, Alessandra; Giacomello, Pierluigi

2010-01-01

Pentose-borate 1:1 complexes were generated in the ESI source of a triple quadrupole and ion trap mass spectrometer by electrospray ionization of Na2B4O7 and pentose (arabinose, lyxose, ribose, xylose) 2:1 solution in CH3CN/H2O. The study of their low-energy collisionally activated dissociation (CAD) demonstrated that ribose and lyxose are preferentially complexed at the C2-C3 cis-diol function whereas arabinose and xylose are esterified at the C1-C2 hydroxyl groups. No evidence was found of the stronger affinity for ribose to borate. The ribose probiotic rule can be explained by considering its peculiar capability, among the investigated pentoses, to almost totally complex the borate anion at the C2-C3 hydroxyl group, thus enabling the subsequent stages of nucleotide assembly, such as phosphorylation and linkage to the nucleobases. Finally, the differences observed in the pentose-borate complex CAD spectra can be used for the mass spectrometric discrimination of isomeric pentoses in complex mixtures.

Study on Microstructure and Electrochemical Corrosion Behavior of PEO Coatings Formed on Aluminum Alloy

NASA Astrophysics Data System (ADS)

Xiang, N.; Song, R. G.; Li, H.; Wang, C.; Mao, Q. Z.; Xiong, Y.

2015-12-01

Plasma electrolytic oxidation (PEO) treated 6063 aluminum alloy was applied in a silicate- and borate-based alkaline solution. The microstructure and electrochemical corrosion behavior were studied by scanning electron microscopy, electrochemical impedance spectroscopy (EIS), and potentiodynamic polarization techniques. The results showed that the silicate-based PEO coating was of a denser structure compared with that of borate-based PEO coating. In addition, the silicate-based PEO coating was composed of more phased (Al9Si) than borate-based PEO coating. The results of corrosion test indicated that the silicate-based PEO coating provided a superior protection to 6063 aluminum alloy substrate, while borate-based PEO coating with a porous structure showed an inferior conservancy against corrosive electrolyte. Furthermore, the EIS tests proved that both coatings were capable to resist the aggressive erosion in 0.5 M NaCl solution after 72 h of immersion. However, the borate-based PEO coating could not provide sufficient protection to the substrate after 72-h immersion in 1 M NaCl solution.

Synthesis of hydrophobic zinc borate nanoflakes and its effect on flame retardant properties of polyethylene

NASA Astrophysics Data System (ADS)

Li, Shengli; Long, Beihong; Wang, Zichen; Tian, Yumei; Zheng, Yunhui; Zhang, Qian

2010-04-01

Zinc borate (2ZnO·3B 2O 3·3.5H 2O) has relatively high dehydration on-set temperature which property permits processing in a wide range of polymer system. But zinc borate particles are hardly dispersed in a polymer matrix so that they prevent their using in industry. To address this problem, we synthesized hydrophobic zinc borate (2ZnO·3B 2O 3·3.5H 2O) nanoflakes by employing solid-liquid reaction of zinc oxide (ZnO) and boric acid (H 3BO 3) in the presence of oleic acid. This method does not bring pollution. By conducting morphological and microscopic analyses, we found that this compound displayed nanoflake morphology with particle size of around 100-200 nm, thickness less than 100 nm and there were uniform mesopores with the diameter about 10 nm within the particles. Furthermore, our products had an effect on flame retardant of polyethylene, especially when the zinc borate was modified by oleic acid.

Boron

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cozen, L.F.

1991-05-01

This paper reports that borate minerals and refined borates are used extensively for the manufacture of vitreous materials such as insulation and textile fiberglasses, borosilicate glass, and porcelain enamels and frits. In North America, these applications are estimated to account for over 54% of the borate consumption. Other substantial uses are in soaps and detergents, metallurgy, fire retardants, industrial biocides, agriculture, and various miscellaneous applications. Reported domestic borate consumption in 1990 was estimated by the U.S. Bureau of Mines to be 320 000 metric tons B{sub 2}O{sub 3} versus 354 000 metric tons B{sub 2}O{sub 3} in 1989. Consumption ismore » projected to remain essentially static in 1991. Imports were estimated by the Bureau to be 50 000 metric tons B{sub 2}O{sub 3} in 1990. Exports of boric acid and refined borates were approximately 650 000 metric tons of product, a 15 000 metric ton increase from the 1989 level. This increase partially offsets the drop in the 1990 consumption level.« less

Thermodynamics Calculation and Experimental Study on Separation of Bismuth from a Bismuth Glance Concentrate Through a Low-Temperature Molten Salt Smelting Process

NASA Astrophysics Data System (ADS)

Yang, Jian-Guang; He, De-Wen; Tang, Chao-Bo; Chen, Yong-Ming; Sun, Ya-Hui; Tang, Mo-Tang

2011-08-01

The main purpose of this study is to characterize and separate bismuth from a bismuth glance concentrate through a low-temperature, sulfur-fixing smelting process. This article reports on a study conducted on the optimization of process parameters, such as Na2CO3 and zinc oxide wt pct in charging, smelting temperature, smelting duration on the bismuth yield, resultant crude bismuth grade, and sulfur-fixing rate. A maximum bismuth recovery of 97.31 pct, crude bismuth grade of 96.93 pct, and 98.23 pct sulfur-fixing rate are obtained when a charge (containing 63.50 wt pct of Na2CO3 and 22.50 wt pct of bismuth glance, as well as 5 pct in excess of the stoichiometric requirement of zinc oxide dosage) is smelted at 1000 K (727 °C) for 150 minutes. This smelting operation is free from atmospheric pollution because zinc oxide is used as the sulfur-fixing agent, which can capture sulfur from bismuth sulfide and form the more thermodynamic-stable compound, zinc sulfide. The solid residue is subjected to a mineral dressing operation to obtain suspension, which is filtered to produce a cake, representing the solid particles of zinc sulfide. Based on the results of the chemical content analysis of the as-resultant zinc sulfide, more than 93 pct zinc sulfide can be recovered, and the recovered zinc sulfide grade can reach 60.20 pct. This material can be sold as zinc sulfide concentrate or roasted to be regenerated as zinc oxide.

In vitro stimulation of vascular endothelial growth factor by borate-based glass fibers under dynamic flow conditions.

PubMed

Chen, Sisi; Yang, Qingbo; Brow, Richard K; Liu, Kun; Brow, Katherine A; Ma, Yinfa; Shi, Honglan

2017-04-01

Bioactive borate glass has been recognized to have both hard and soft tissue repair and regeneration capabilities through stimulating both osteogenesis and angiogenesis. However, the underlying biochemical and cellular mechanisms remain unclear. In this study, dynamic flow culturing modules were designed to simulate the micro-environment near the vascular depletion and hyperplasia area in wound-healing regions, thus to better investigate the mechanisms underlying the biocompatibility and functionality of borate-based glass materials. Glass fibers were dosed either upstream or in contact with the pre-seeded cells in the dynamic flow module. Two types of borate glasses, doped with (1605) or without (13-93B3) CuO and ZnO, were studied along with the silicate-based glass, 45S5. Substantial fiber dissolution in cell culture medium was observed, leading to the release of ions (boron, sodium and potassium) and the deposition of a calcium phosphate phase. Different levels of vascular endothelial growth factor secretion were observed from cells exposed to these three glass fibers, and the copper/zinc containing borate 1605 fibers exhibited the most positive influence. These results indicate that dynamic studies of in vitro bioactivity provide useful information to understand the in vivo response to bioactive borate glasses. Copyright © 2016 Elsevier B.V. All rights reserved.

Novel method for early investigation of bioactivity in different borate bio-glasses.

PubMed

Abdelghany, A M

2013-01-01

Some ternary borate glasses were prepared and corrosion behavior of such ternary borate glasses after immersion in aqueous dilute phosphate solution was studied using different immersion times. Fourier transform infrared (FTIR) absorption spectral measurements were done before and after immersion in the mentioned solution for extended times up to 2 days to justify the appearance of the characteristic FTIR bands due to calcium phosphate (hydroxyapatite (HA)) which is considered as the potential indication of bioactivity. Experimental IR data confirm the beginning of the appearance of FTIR bands at about 580 and 620 cm(-1) after 3 days and the complete resolution with its characteristic split form after 1 week and more. Deconvolution analysis technique (DAT) of the FTIR spectrum was employed to investigate the bioactivity of such ternary borate system after a short period of immersion. The corrosion behavior of such glasses is explained in relation to a suggested hydrolysis followed by direct dissolution mechanism. The ease of dissolution of all the borate glasses constituents explains the formation of calcium phosphate and conversion to crystalline hydroxyapatite within the borate glass matrix. X-ray diffraction may be used to retrace the structural changes and degree of crystallinity of the prepared glasses. Copyright © 2012 Elsevier B.V. All rights reserved.

Facile formation of metallic bismuth/bismuth oxide heterojunction on porous carbon with enhanced photocatalytic activity.

PubMed

Zhang, Liping; Ghimire, Pramila; Phuriragpitikhon, Jenjira; Jiang, Baojiang; Gonçalves, Alexandre A S; Jaroniec, Mietek

2018-03-01

Bismuth/bismuth oxide heterojunction on porous carbon (Bi 0 /Bi 2 O 3 @C) was successfully prepared by a surfactant-assisted sol-gel method. This composite photocatalyst was fabricated by depositing Bi 2 O 3 and metallic bismuth nanoparticles (NPs) on porous carbon sheets. Bi NPs were created by in-situ reduction of Bi 2 O 3 with amorphous carbon. During the synthesis, bismuth and carbon precursors were mixed in different ratios, resulting in distinct amounts of metallic bismuth in the composites. The composites showed large specific surface area and pore volume as well as strong light absorption ability due to the existing carbon. In addition, the plasmonic bismuth NPs were found to behave as a noble metal, which is able to generate hot charge carriers under visible light irradiation. Photocatalytic performance of the Bi 0 /Bi 2 O 3 @C composites was investigated by degradation of methylene blue. It turned out that the composites showed much higher efficiency as compared to bare Bi 2 O 3 , which may be attributed to the synergistic effects of porous structures, improved optical absorption, and surface plasmon resonance. Copyright © 2017 Elsevier Inc. All rights reserved.

Glutathione and multidrug resistance protein transporter mediate a self-propelled disposal of bismuth in human cells

PubMed Central

Hong, Yifan; Lai, Yau-Tsz; Chan, Godfrey Chi-Fung; Sun, Hongzhe

2015-01-01

Glutathione and multidrug resistance protein (MRP) play an important role on the metabolism of a variety of drugs. Bismuth drugs have been used to treat gastrointestinal disorder and Helicobacter pylori infection for decades without exerting acute toxicity. They were found to interact with a wide variety of biomolecules, but the major metabolic pathway remains unknown. For the first time (to our knowledge), we systematically and quantitatively studied the metabolism of bismuth in human cells. Our data demonstrated that over 90% of bismuth was passively absorbed, conjugated to glutathione, and transported into vesicles by MRP transporter. Mathematical modeling of the system reveals an interesting phenomenon. Passively absorbed bismuth consumes intracellular glutathione, which therefore activates de novo biosynthesis of glutathione. Reciprocally, sequestration by glutathione facilitates the passive uptake of bismuth and thus completes a self-sustaining positive feedback circle. This mechanism robustly removes bismuth from both intra- and extracellular space, protecting critical systems of human body from acute toxicity. It elucidates the selectivity of bismuth drugs between human and pathogens that lack of glutathione, such as Helicobacter pylori, opening new horizons for further drug development. PMID:25737551

Intense 2.7 µm emission and structural origin in Er3+-doped bismuthate (Bi2O3-GeO2-Ga2O3-Na2O) glass.

PubMed

Guo, Yanyan; Li, Ming; Hu, Lili; Zhang, Junjie

2012-01-15

The 2.7 μm emission properties in Er3+-doped bismuthate (Bi2O3-GeO2-Ga2O3-Na2O) glass were investigated in the present Letter. An intense 2.7 μm emission in Er3+-doped bismuthate glass was observed. It is found that Er3+-doped bismuthate glass possesses high spontaneous transition probability A (65.26 s(-1)) and large 2.7 μm emission cross section σ(em) (9.53×10(-21) cm2) corresponding to the stimulated emission of Er3+:4I11/2→4I13/2 transition. The emission characteristic and energy transfer process upon excitation of a conventional 980 nm laser diode in bismuthate glass were analyzed. Additionally, the structure of bismuthate glass was analyzed by the Raman spectrum. The advantageous spectroscopic characteristics of Er3+ single-doped bismuthate glass together with the prominent thermal property indicate that bismuthate glass might become an attractive host for developing solid-state lasers around 2.7 μm.

Borate protection of softwood from Coptotermes acinaciformis (Isoptera: Rhinotermitidae) damage: variation in protection thresholds explained.

PubMed

Peters, Brenton C; Fitzgerald, Christopher J

2006-10-01

Laboratory and field data reported in the literature are confusing with regard to "adequate" protection thresholds for borate timber preservatives. The confusion is compounded by differences in termite species, timber species and test methodology. Laboratory data indicate a borate retention of 0.5% mass/mass (m/m) boric acid equivalent (BAE) would cause > 90% termite mortality and restrict mass loss in test specimens to < or = 5%. Field data generally suggest that borate retentions appreciably > 0.5% m/m BAE are required. We report two field experiments with varying amounts of untreated feeder material in which Coptotermes acinaciformis (Froggatt) (Isoptera: Rhinotermitidae) responses to borate-treated radiata (Monterey) pine, Pinus radiata D. Don, were measured. The apparently conflicting results between laboratory and field data are explained by the presence or absence of untreated feeder material in the test environment. In the absence of untreated feeder material, wood containing 0.5% BAE provided adequate protection from Coptotermes sp., whereas in the presence of untreated feeder material, increased retentions were required. Furthermore, the retentions required increased with increased amounts of susceptible material present. Some termites, Nasutitermes sp. and Mastotermes darwiniensis Froggatt, for example, are borate-tolerant and borate timber preservatives are not a viable management option with these species. The lack of uniform standards for termite test methodology and assessment criteria for efficacy across the world is recognized as a difficulty with research into the performance of timber preservatives with termites. The many variables in laboratory and field assays make "prescriptive" standards difficult to recommend. The use of "performance" standards to define efficacy criteria ("adequate" protection) is discussed.

Zerovalent bismuth nanoparticles inhibit Streptococcus mutans growth and formation of biofilm

PubMed Central

Hernandez-Delgadillo, Rene; Velasco-Arias, Donaji; Diaz, David; Arevalo-Niño, Katiushka; Garza-Enriquez, Marianela; De la Garza-Ramos, Myriam A; Cabral-Romero, Claudio

2012-01-01

Background and methods Despite continuous efforts, the increasing prevalence of resistance among pathogenic bacteria to common antibiotics has become one of the most significant concerns in modern medicine. Nanostructured materials are used in many fields, including biological sciences and medicine. While some bismuth derivatives has been used in medicine to treat vomiting, nausea, diarrhea, and stomach pain, the biocidal activity of zerovalent bismuth nanoparticles has not yet been studied. The objective of this investigation was to analyze the antimicrobial activity of bismuth nanoparticles against oral bacteria and their antibiofilm capabilities. Results Our results showed that stable colloidal bismuth nanoparticles had 69% antimicrobial activity against Streptococcus mutans growth and achieved complete inhibition of biofilm formation. These results are similar to those obtained with chlorhexidine, the most commonly used oral antiseptic agent. The minimal inhibitory concentration of bismuth nanoparticles that interfered with S. mutans growth was 0.5 mM. Conclusion These results suggest that zerovalent bismuth nanoparticles could be an interesting antimicrobial agent to be incorporated into an oral antiseptic preparation. PMID:22619547

Low-energy vibrational dynamics of cesium borate glasses.

PubMed

Crupi, C; D'Angelo, G; Vasi, C

2012-06-07

Low-temperature specific heat and inelastic light scattering experiments have been performed on a series of cesium borate glasses and on a cesium borate crystal. Raman measurements on the crystalline sample have revealed the existence of cesium rattling modes in the same frequency region where glasses exhibit the boson peak (BP). These localized modes are supposed to overlap with the BP in cesium borate glasses affecting its magnitude. Their influence on the low frequency vibrational dynamics in glassy samples has been considered, and their contribution to the specific heat has been estimated. Evidence for a relation between the changes of the BP induced by the increased amount of metallic oxide and the variations of the elastic medium has been provided.

The Effects of Bismuth Oxide on Microstructures and Magnetic Properties of Mn-Mg-Al Ferrites

NASA Astrophysics Data System (ADS)

Nekouee, Kh. A.; Rahimi, A. H.; Haghighi, M. Alineghad; Ehsani, N.

2018-04-01

In the present paper, the effects of bismuth oxide as an additive on microstructure and magnetic properties of Mg0.9Mn0.1Al0.4Fe1.6O4 were investigated. Mg-Mn-Al ferrite powders were prepared by the conventional solid state synthesis method. Two different amounts of bismuth oxide (2.5 wt.% and 5 wt.%) were utilized as the sintering aid and their microstructure and physical properties were compared to those of the sample without additives. X-ray diffraction (XRD) analysis indicated that crystal lattice distortion due to the microstructural constraints as the result from incorporation of bismuth oxide into the microstructure was developed by adding bismuth oxide. XRD Rietveld refinement was used to define the cation distribution and to refine the lattice parameter and oxygen parameter for the sample without bismuth oxide as (Mg0.16Mn0.02Al0.15Fe0.77)A(Mg0.74Mn0.08Al0.25Fe0.83)BO4 and 8.3308 Å and 0.2542, respectively. Microstructure studies show that a bismuth rich liquid phase forms during the sintering at 1250°C, which enhances the densification of sintered bodies up to 13% (a relative density of 93%). Magnetization of sintered samples were increased from 21.1 emu/g to 26.2 emu/g upon addition of 2.5 wt.% bismuth oxide and then decreased to 24.9 emu/g when 5 wt.% bismuth oxide was added.

Bismuth oxide aqueous colloidal nanoparticles inhibit Candida albicans growth and biofilm formation

PubMed Central

Hernandez-Delgadillo, Rene; Velasco-Arias, Donaji; Martinez-Sanmiguel, Juan Jose; Diaz, David; Zumeta-Dube, Inti; Arevalo-Niño, Katiushka; Cabral-Romero, Claudio

2013-01-01

Multiresistance among microorganisms to common antimicrobials has become one of the most significant concerns in modern medicine. Nanomaterials are a new alternative to successfully treat the multiresistant microorganisms. Nanostructured materials are used in many fields, including biological sciences and medicine. Recently, it was demonstrated that the bactericidal activity of zero-valent bismuth colloidal nanoparticles inhibited the growth of Streptococcus mutans; however the antimycotic potential of bismuth nanostructured derivatives has not yet been studied. The main objective of this investigation was to analyze the fungicidal activity of bismuth oxide nanoparticles against Candida albicans, and their antibiofilm capabilities. Our results showed that aqueous colloidal bismuth oxide nanoparticles displayed antimicrobial activity against C. albicans growth (reducing colony size by 85%) and a complete inhibition of biofilm formation. These results are better than those obtained with chlorhexidine, nystatin, and terbinafine, the most effective oral antiseptic and commercial antifungal agents. In this work, we also compared the antimycotic activities of bulk bismuth oxide and bismuth nitrate, the precursor metallic salt. These results suggest that bismuth oxide colloidal nanoparticles could be a very interesting candidate as a fungicidal agent to be incorporated into an oral antiseptic. Additionally, we determined the minimum inhibitory concentration for the synthesized aqueous colloidal Bi2O3 nanoparticles. PMID:23637533

Evaluation to the effect of B2O3-La2O3-SrO-Na2O-Al2O3 bonding agent on Ti6Al4V-porcelain bonding.

PubMed

Zhao, C Q; Wu, S Q; Lu, Y J; Gan, Y L; Guo, S; Lin, J J; Huang, T T; Lin, J X

2016-10-01

Low-fusing bonding agents have been widely applied in Ti-ceramics restorations. As an important category, borate bonding agents have great potentials in increasing Ti-porcelain bonding. The purpose of this study is to evaluate the effect of borate bonding agent with addition of Na2O and Al2O3 on Ti6Al4V-porcelain bonding. The thermal properties of borate bonding agent, such as glass transition temperature (Tg) and crystallization peak temperature (Tp), were investigated to establish the sintering process. And the coefficient of thermal expansion (CTE) was to evaluate the matching effect of porcelain to Ti6Al4V. The bond strength was analyzed by the three point bending test. The microscopic morphology of the borate bonding agent surface after sintering, the interface of Ti-borate bonding agent-porcelain, and the fracture mode after porcelains fracture, were studied to assess the influence of borate bonding agent on Ti6Al4V-ceramics. With the addition of Na2O and Al2O3, the porcelain residues were observed increased indication on the Ti6Al4V surface after porcelain fracture and the bond strength was acquired the maximum (49.45MPa) in the bonding agent composition of 75.70B2O3-5.92La2O3-11.84SrO-4.67Na2O-1.87Al2O3. Those results suggest that borate bonding agent is an effective way to improve the Ti6Al4V-ceramics bond strength. And the addition of Na2O and Al2O3 strengthen this effect. Copyright © 2016 Elsevier Ltd. All rights reserved.

The Mechanism of Boron Mobility in Wheat and Canola Phloem1[C][OA

PubMed Central

Stangoulis, James; Tate, Max; Graham, Robin; Bucknall, Martin; Palmer, Lachlan; Boughton, Berin; Reid, Robert

2010-01-01

Low-molecular-weight borate complexes were isolated from canola (Brassica napus) and wheat (Triticum aestivum) phloem exudates, as well as the cytoplasm of the fresh-water alga Chara corallina, and identified using matrix-assisted laser desorption/ionization time-of-flight mass spectrometry. Phloem exudate was collected from field-grown canola inflorescence stalks by shallow incision, while wheat phloem exudate was collected by aphid stylectomy. Chara cytoplasm was collected by careful manual separation of the cell wall, vacuole, and cytosolic compartments. Matrix-assisted laser desorption/ionization time-of-flight mass spectrometry showed the presence of isotopic borate complexes, at mass-to-charge ratio of 690.22/691.22 in the canola and wheat phloem and at 300.11/301.11 in canola phloem and Chara cytoplasm. Using reference compounds, the borate complexes with mass-to-charge ratio 690.22/691.22 was identified as a bis-sucrose (Suc) borate complex in which the 4,6-hydroxyl pairs from the two α-glucopyranoside moieties formed an [L2B]−1 complex. Further investigation using liquid chromatography electrospray ionization triple quadrupole mass spectrometry analysis confirmed the presence of the bis-Suc borate complex in wheat phloem with a concentration up to 220 μm. The 300.11/301.11 complex was putatively identified as a bis-N-acetyl-serine borate complex but its concentration was below the detection limits of the liquid chromatography electrospray ionization triple quadrupole mass spectrometer so could not be quantified. The presence of borate complexes in the phloem provides a mechanistic explanation for the observed phloem boron mobility in canola and wheat and other species that transport Suc as their primary photoassimilate. PMID:20413647

Geochemical characteristics of The Emet (Espey-Hisarcik) borate deposits, Kütahya, Turkey

NASA Astrophysics Data System (ADS)

Koçak, İ.; Koç, Ş.

2018-06-01

Nearly 72% world's borate reserves are in western part of Turkey. The Emet (Kütahya) deposit is one of these deposits. The Emet borate deposit, like other deposits in western Anatolia, was deposited in Miocene lacustrine environment whose formation coincides with volcanic activity started in Paleogene and lasted to the beginning of Quaternary. The borate ore displaying lenticular structure is alternated with claystone, marl, tuff and thin bedded limestone. The mineral paragenesis is composed of colemanite, hydroboracite, Veatchite, dolomite, calcite, montmorillonite and illite. The Emet borate deposit has been the subject of various geologic and mineralogical studies. In the present study major and trace element contents of 60 borate samples from this deposit are discussed. Among the trace elements, significant enrichment was found in As, Se, Sr, Cs, Sb and Li. Element correlations indicate volcanic source for boron (exhalations and hydrothermal solutions) whilst other elements are found to be derived from a terrestrial source. According to REE data, high Ce concentrations and anomalies are generally indicative of oxygenated depositional environment whilst low Ce contents facilitated the lake waters to be low oxygenated as a result of H2S-rich hydrothermal solutions. The weak negative anomaly detected only in the Hisarcık region is attributed to lacking of Eu contribution to the lake due to insufficient alteration on the continent.

Structural, electronic, vibrational and optical properties of Bin clusters

NASA Astrophysics Data System (ADS)

Liang, Dan; Shen, Wanting; Zhang, Chunfang; Lu, Pengfei; Wang, Shumin

2017-10-01

The neutral, anionic and cationic bismuth clusters with the size n up to 14 are investigated by using B3LYP functional within the regime of density functional theory and the LAN2DZ basis set. By analysis of the geometries of the Bin (n = 2-14) clusters, where cationic and anionic bismuth clusters are largely similar to those of neutral ones, a periodic effect by adding units with one to four atoms into smaller cluster to form larger cluster is drawn for the stable structures of bismuth clusters. An even-odd alteration is shown for the properties of the clusters, such as the calculated binding energies and dissociation energies, as well as frontier orbital energies, electron affinities, ionization energies. All the properties indicate that the Bi4 cluster is the most possible existence in bismuth-containing materials, which supports the most recent experiment. The orbital compositions, infrared and Raman activities and the ultraviolet absorption of the most possible tetramer bismuth cluster are given in detail to reveal the periodic tendency of adding bismuth atoms and the stability of tetramer bismuth cluster.

Extreme Pressure Synergistic Mechanism of Bismuth Naphthenate and Sulfurized Isobutene Additives

NASA Astrophysics Data System (ADS)

Xu, Xin; Hu, Jianqiang; Yang, Shizhao; Xie, Feng; Guo, Li

A four-ball tester was used to evaluate the tribological performances of bismuth naphthenate (BiNap), sulfurized isobutene (VSB), and their combinations. The results show that the antiwear properties of BiNap and VSB are not very visible, but they possess good extreme pressure (EP) properties, particularly sulfur containing bismuth additives. Synergistic EP properties of BiNap with various sulfur-containing additives were investigated. The results indicate that BiNap exhibits good EP synergism with sulfur-containing additives. The surface analytical tools, such as X-ray photoelectron spectrometer (XPS) scanning electron microscope (SEM) and energy dispersive X-ray (EDX), were used to investigate the topography, composition contents, and depth profile of some typical elements on the rubbing surface. Smooth topography of wear scar further confirms that the additive showed good EP capacities, and XPS and EDX analyzes indicate that tribochemical mixed protective films composed of bismuth, bismuth oxides, sulfides, and sulfates are formed on the rubbing surface, which improves the tribological properties of lubricants. In particular, a large number of bismuth atoms and bismuth sulfides play an important role in improving the EP properties of oils.

Strontium borate glass: potential biomaterial for bone regeneration

PubMed Central

Pan, H. B.; Zhao, X. L.; Zhang, X.; Zhang, K. B.; Li, L. C.; Li, Z. Y.; Lam, W. M.; Lu, W. W.; Wang, D. P.; Huang, W. H.; Lin, K. L.; Chang, J.

2010-01-01

Boron plays important roles in many life processes including embryogenesis, bone growth and maintenance, immune function and psychomotor skills. Thus, the delivery of boron by the degradation of borate glass is of special interest in biomedical applications. However, the cytotoxicity of borate glass which arises with the rapid release of boron has to be carefully considered. In this study, it was found that the incorporation of strontium into borate glass can not only moderate the rapid release of boron, but also induce the adhesion of osteoblast-like cells, SaOS-2, thus significantly increasing the cyto-compatibility of borate glass. The formation of multilayers of apatite with porous structure indicates that complete degradation is optimistic, and the spread of SaOS-2 covered by apatite to form a sandwich structure may induce bone-like tissue formation at earlier stages. Therefore, such novel strontium-incorporated borosilicate may act as a new generation of biomaterial for bone regeneration, which not only renders boron as a nutritious element for bone health, but also delivers strontium to stimulate formation of new bones. PMID:20031984

Is Boron a Prebiotic Element? A Mini-review of the Essentiality of Boron for the Appearance of Life on Earth

NASA Astrophysics Data System (ADS)

Scorei, Romulus

2012-02-01

Boron is probably a prebiotic element with special importance in the so-called "sugars world". Boron is not present on Earth in its elemental form. It is found only in compounds, e.g., borax, boric acid, kernite, ulexite, colemanite and other borates. Volcanic spring waters sometimes contain boron-based acids (e.g., boric, metaboric, tetraboric and pyroboric acid). Borates influence the formation of ribofuranose from formaldehyde that feeds the "prebiotic metabolic cycle". The importance of boron in the living world is strongly related to its implications in the prebiotic origins of genetic material; consequently, we believe that throughout the evolution of life, the primary role of boron has been to provide thermal and chemical stability in hostile environments. The complexation of boric acid and borates with organic cis-diols remains the most probable chemical mechanism for the role of this element in the evolution of the living world. Because borates can stabilize ribose and form borate ester nucleotides, boron may have provided an essential contribution to the "pre-RNA world".

Synthesis and characterization of cerium- and gallium-containing borate bioactive glass scaffolds for bone tissue engineering.

PubMed

Deliormanlı, Aylin M

2015-02-01

Bioactive glasses are widely used in biomedical applications due to their ability to bond to bone and even to soft tissues. In this study, borate based (13-93B3) bioactive glass powders containing up to 5 wt% Ce2O3 and Ga2O3 were prepared by the melt quench technique. Cerium (Ce+3) and gallium (Ga+3) were chosen because of their low toxicity associated with bacteriostatic properties. Bioactive glass scaffolds were fabricated using the polymer foam replication method. In vitro degradation and bioactivity of the scaffolds were evaluated in SBF under static conditions. Results revealed that the cerium- and gallium-containing borate glasses have much lower degradation rates compared to the bare borate glass 13-93B3. In spite of the increased chemical durability, substituted glasses exhibited a good in vitro bioactive response except when the Ce2O3 content was 5 wt%. Taking into account the high in vitro hydroxyapatite forming ability, borate glass scaffolds containing Ce+3 and Ga+3 therapeutic ions are promising candidates for bone tissue engineering applications.

Strontium borate glass: potential biomaterial for bone regeneration.

PubMed

Pan, H B; Zhao, X L; Zhang, X; Zhang, K B; Li, L C; Li, Z Y; Lam, W M; Lu, W W; Wang, D P; Huang, W H; Lin, K L; Chang, J

2010-07-06

Boron plays important roles in many life processes including embryogenesis, bone growth and maintenance, immune function and psychomotor skills. Thus, the delivery of boron by the degradation of borate glass is of special interest in biomedical applications. However, the cytotoxicity of borate glass which arises with the rapid release of boron has to be carefully considered. In this study, it was found that the incorporation of strontium into borate glass can not only moderate the rapid release of boron, but also induce the adhesion of osteoblast-like cells, SaOS-2, thus significantly increasing the cyto-compatibility of borate glass. The formation of multilayers of apatite with porous structure indicates that complete degradation is optimistic, and the spread of SaOS-2 covered by apatite to form a sandwich structure may induce bone-like tissue formation at earlier stages. Therefore, such novel strontium-incorporated borosilicate may act as a new generation of biomaterial for bone regeneration, which not only renders boron as a nutritious element for bone health, but also delivers strontium to stimulate formation of new bones.

Secondary relaxations in supercooled and glassy sucrose-borate aqueous solutions.

PubMed

Longinotti, M Paula; Corti, Horacio R; Pablo, Juan J de

2008-10-13

The dielectric relaxation spectra of concentrated aqueous solutions of sucrose-borate mixtures have been measured in the supercooled and glassy regions in the frequency range of 40Hz to 2MHz. The secondary (beta) relaxation process was analyzed in the temperature range 183-233K at water contents between 20 and 30wt%. The relaxation times were obtained, and the activation energy of that process was calculated. In order to assess the effect of borate on the relaxation of disaccharide-water mixtures, we also studied the dielectric behavior of sucrose aqueous solutions in the same range of temperatures and water contents. Our findings support the view that, beyond a water content of approximately 20wt%, the secondary relaxation of water-sucrose and water-sucrose-borate mixtures adopts a universal character that can be explained in terms of a simple exponential function of the temperature scaled by the glass transition temperature (T(g)). The behavior observed for water-sucrose and water-sucrose-borate mixtures is compared with previous results obtained in other water-carbohydrate systems.

The molecular structure of the borate mineral rhodizite (K, Cs)Al4Be4(B, Be)12O28 - A vibrational spectroscopic study

NASA Astrophysics Data System (ADS)

Frost, Ray L.; López, Andrés; Xi, Yunfei; Scholz, Ricardo; Souza, Larissa; Lana, Cristiano

2014-07-01

We have studied the borate mineral rhodizite (K, Cs)Al4Be4(B, Be)12O28 using a combination of DEM with EDX and vibrational spectroscopic techniques. The mineral occurs as colorless, gray, yellow to white crystals in the triclinic crystal system. The studied sample is from the Antandrokomby Mine, Sahatany valley, Madagascar. The mineral is prized as a semi-precious jewel. Semi-quantitative chemical composition shows a Al, Ca, borate with minor amounts of K, Mg and Cs. The mineral has a characteristic borate Raman spectrum and bands are assigned to the stretching and bending modes of B, Be and Al. No Raman bands in the OH stretching region were observed.

Eliminating the non-Gaussian spectral response of X-ray absorbers for transition-edge sensors

NASA Astrophysics Data System (ADS)

Yan, Daikang; Divan, Ralu; Gades, Lisa M.; Kenesei, Peter; Madden, Timothy J.; Miceli, Antonino; Park, Jun-Sang; Patel, Umeshkumar M.; Quaranta, Orlando; Sharma, Hemant; Bennett, Douglas A.; Doriese, William B.; Fowler, Joseph W.; Gard, Johnathon D.; Hays-Wehle, James P.; Morgan, Kelsey M.; Schmidt, Daniel R.; Swetz, Daniel S.; Ullom, Joel N.

2017-11-01

Transition-edge sensors (TESs) as microcalorimeters for high-energy-resolution X-ray spectroscopy are often fabricated with an absorber made of materials with high Z (for X-ray stopping power) and low heat capacity (for high resolving power). Bismuth represents one of the most compelling options. TESs with evaporated bismuth absorbers have shown spectra with undesirable and unexplained low-energy tails. We have developed TESs with electroplated bismuth absorbers over a gold layer that are not afflicted by this problem and that retain the other positive aspects of this material. To better understand these phenomena, we have studied a series of TESs with gold, gold/evaporated bismuth, and gold/electroplated bismuth absorbers, fabricated on the same die with identical thermal coupling. We show that the bismuth morphology is linked to the spectral response of X-ray TES microcalorimeters.

Eliminating the non-Gaussian spectral response of X-ray absorbers for transition-edge sensors

DOE PAGES

Divan, Ralu; Gades, Lisa M.; Kenesei, Peter; ...

2017-11-08

Transition-edge sensors (TESs) as microcalorimeters for high-energy-resolution X-ray spectroscopy are often fabricated with an absorber made of materials with high Z (for X-ray stopping power) and low heat capacity (for high resolving power). Bismuth represents one of the most compelling options. TESs with evaporated bismuth absorbers have shown spectra with undesirable and unexplained low-energy tails. We have developed TESs with electroplated bismuth absorbers over a gold layer that are not afflicted by this problem and that retain the other positive aspects of this material. To better understand these phenomena, we have studied a series of TESs with gold, gold/evaporated bismuth,more » and gold/electroplated bismuth absorbers, fabricated on the same die with identical thermal coupling. Lastly, we show that the bismuth morphology is linked to the spectral response of X-ray TES microcalorimeters.« less

Eliminating the non-Gaussian spectral response of X-ray absorbers for transition-edge sensors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Divan, Ralu; Gades, Lisa M.; Kenesei, Peter

Transition-edge sensors (TESs) as microcalorimeters for high-energy-resolution X-ray spectroscopy are often fabricated with an absorber made of materials with high Z (for X-ray stopping power) and low heat capacity (for high resolving power). Bismuth represents one of the most compelling options. TESs with evaporated bismuth absorbers have shown spectra with undesirable and unexplained low-energy tails. We have developed TESs with electroplated bismuth absorbers over a gold layer that are not afflicted by this problem and that retain the other positive aspects of this material. To better understand these phenomena, we have studied a series of TESs with gold, gold/evaporated bismuth,more » and gold/electroplated bismuth absorbers, fabricated on the same die with identical thermal coupling. Lastly, we show that the bismuth morphology is linked to the spectral response of X-ray TES microcalorimeters.« less

Localization and Related Phenomena in Multiply Connected Nanostructured Inverse Opal Bismuth

NASA Astrophysics Data System (ADS)

Bleiweiss, Michael; Saygi, Salih; Amirzadeh, Jafar; Datta, Timir; Lungu, Anca; Yin, Ming; Palm, Eric; Brandt, Bruce; Iqbal, Zafar

2001-03-01

The nanostructures were fabricated by pressure infiltration of bismuth into porous artificial opal and were characterized using SEM, EDX and XRD. These structures form a regular three-dimensional network in which the bismuth regions percolate in all directions between the close packed spheres of SiO_2. The sizes of the conducting regions are of the order of tens of nanometers. The static magnetic properties of both bismuth inverse opal and bulk bismuth were studied using a SQUID magnetometer. Transport measurements, including Hall, were done using standard ac four and six probe techniques in fields up to 17 T* and temperatures between 4.2 and 150 K. The results of these measurements, including the observation of localization phenomena, will be discussed. Comparisons will be made with published results on bismuth nanowires. *Performed at the National High Magnetic Field Lab (NHMFL) FSU, Tallahassee, FL. Partially supported by a grant from NASA.

Hydrothermal synthesis of nanocubes of sillenite type compounds for photovoltaic applications and solar energy conversion of carbon dioxide to fuels

DOEpatents

Subramanian, Vaidyanathan; Murugesan, Sankaran

2014-04-29

The present invention relates to formation of nanocubes of sillenite type compounds, such as bismuth titanate, i.e., Bi.sub.12TiO.sub.20, nanocubes, via a hydrothermal synthesis process, with the resulting compound(s) having multifunctional properties such as being useful in solar energy conversion, environmental remediation, and/or energy storage, for example. In one embodiment, a hydrothermal method is disclosed that transforms nanoparticles of TiO.sub.2 to bismuth titanate, i.e., Bi.sub.12TiO.sub.20, nanocubes, optionally loaded with palladium nanoparticles. The method includes reacting titanium dioxide nanotubes with a bismuth salt in an acidic bath at a temperature sufficient and for a time sufficient to form bismuth titanate crystals, which are subsequently annealed to form bismuth titanate nanocubes. After annealing, the bismuth titanate nanocubes may be optionally loaded with nano-sized metal particles, e.g., nanosized palladium particles.

Recent Advances in Bismuth-Based Nanomaterials for Photoelectrochemical Water Splitting.

PubMed

Bhat, Swetha S M; Jang, Ho Won

2017-08-10

In recent years, bismuth-based nanomaterials have drawn considerable interest as potential candidates for photoelectrochemical (PEC) water splitting owing to their narrow band gaps, nontoxicity, and low costs. The unique electronic structure of bismuth-based materials with a well-dispersed valence band comprising Bi 6s and O 2p orbitals offers a suitable band gap to harvest visible light. This Review presents significant advancements in exploiting bismuth-based nanomaterials for solar water splitting. An overview of the different strategies employed and the new ideas adopted to improve the PEC performance of bismuth-based nanomaterials are discussed. Morphology control, the construction of heterojunctions, doping, and co-catalyst loading are several approaches that are implemented to improve the efficiency of solar water splitting. Key issues are identified and guidelines are suggested to rationalize the design of efficient bismuth-based materials for sunlight-driven water splitting. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

I Situ Surface X-Ray Diffraction Studies of Electrochemically Deposited Monolayers

NASA Astrophysics Data System (ADS)

Yee, Dennis

1995-01-01

In situ x-ray diffraction has been used to determine the detailed atomic structure of electrochemically deposited lead, thallium, and bismuth monolayers on the silver (111) electrode surface. A review of our previously published lead and thallium monolayer results and the first in situ surface x-ray crystallographic study of the bismuth monolayer structure is presented. The crystallographic analysis of the bismuth Bragg rod intensities and the interference between the bismuth Bragg rod and silver crystal truncation rod scattering were used to determine the detailed atomic structure of the bismuth on silver (111) system at the liquid-solid interface. Our previous in situ x-ray diffraction studies showed that the bismuth monolayer lattice is rectangular and uniaxially incommensurate with the underlying hexagonal silver surface. A crystallographic analysis of the measured structure factor magnitudes reveals that the monolayer forms chains of atoms on the silver surface, similar to the bulk Bi(110)_{rh} plane, with a near neighbor distance of 3.12 +/- 0.01 A and a bond angle of 93 +/- 1^circ, consistent with the bulk Bi(110) _{rh} plane values. The crystallographic refinement also shows that the bismuth monolayer atoms are anisotropically disordered with a rms disorder of 0.25 +/- 0.03 A in the incommensurate direction and 0.09 +/- 0.03 A rms in the commnensurate direction. The interference between the Bi(20) Bragg rod and the Ag(10L)_ {h} crystal truncation rod scattering reveals that one set of bismuth atoms is registered near the bridge sites of the silver (111) surface while another set is registered near the 3-fold hollow sites. In addition, the Bi-Ag d-spacing (3.1 +/- 0.1 A) is found to be consistent with the bulk bismuth near neighbor distance. The bismuth z-direction rms disorder (1.01 +/- 0.08 A) is found to be dominated by the roughness of the underlying silver (sigma_{Ag} = 0.9 +/- 0.1 A rms). Using the estimated bismuth-bismuth spring constant of 1.41 +/- 0.07 eV/A^2 from our measured bismuth two-dimensional compressibility, two simple models are used to try and understand the origin of the anisotropic disorder. A simple two-dimensional isotropic thermal fluctuation model shows that thermal fluctuations are not large enough to account for all of the measured excess disorder in the incommensurate direction. A simple one-dimensional Frenkel-Kontorova model shows that the substrate-induced disorder can account for the anisotropic disorder, assuming a substrate sinusoidal potential strength of 0.35 +/- 0.02 eV.

Microwave-induced Bismuth Salts-mediated Synthesis of Molecules of Medicinal Interests.

PubMed

Bandyopadhyay, Debasish; Chavez, Ashlee; Banik, Bimal K

2017-01-01

Bismuth salts-mediated reactions have become a powerful tool for the synthesis of diverse medicinally-significant compounds because of their low-toxicity (non-toxic) and Lewis acidic capacity. In fact, LD50 of bismuth nitrate is lower than table salt. On the other hand, microwave-induced chemical synthesis is considered as a major greener route in modern chemistry. A total of 139 publications (including a few authentic web links) have been reviewed mainly to discuss bismuth salts-induced electrophilic aromatic substitution, protection-deprotection chemistry of carbonyl compounds, enamination, oxidation, carbohydrate chemistry, hydrolysis, addition-elimination route, Paal-Knorr reaction, Clauson-kaas synthesis, Michael addition, aza-Michael addition, Hantzsch reaction, Biginelli reaction, Ferrier rearrangement, Pechmann condensation, Diels-Alder and aza-Diels- Alder reactions, as well as effects of microwave irradiation in a wide range of chemical transformations. Bismuth salts-mediated reactions are developed for the synthesis of diverse organic molecules of medicinal significance. Reactions conducted with bismuth salts are environmentally benign, economical, rapid and high yielding. Microwave irradiation has accelerated these reactions significantly. It is believed that bismuth salts released corresponding acids in the media during the reaction. However, a coordination of bismuth salt to the electronegative atom is also observed in the NMR study. Bismuth has much less control (less attractive forces) over anions (for example, halides, nitrate, sulfate and triflates) compared to alkali metals. Therefore, it forms weak bond with electronegative atoms more readily and facilitates the reactions significantly. Many products obtained via bismuth salts-mediated reactions are medicinally active or intermediate for the synthesis of biologically active molecules including antifungal, anti-parasitic, anticancer and antibacterial agents, as well as agents to prevent Leishmaniosis and Chagas' diseases. Bismuth salts are able to (i) generate mineral acids in the reaction media and (ii) coordinate with electronegative atoms to facilitate the reaction. When the reagents and the catalyst (bismuth salt) are subjected to microwave irradiation, microwave passes through the (glass) walls of the reaction vessel and heat only the reactants avoiding local overheating at the wall of the vessel. Accordingly, the possibility of side reaction and subsequent by-product formation are reduced abruptly which in turn increases the yield of the desired product. The extreme rapidity with excellent yield of the product can be rationalized as a synergistic effect of the bismuth salts and microwave irradiation. Copyright© Bentham Science Publishers; For any queries, please email at epub@benthamscience.org.

Reactive magnetron sputtering deposition of bismuth tungstate onto titania nanoparticles for enhancing visible light photocatalytic activity

NASA Astrophysics Data System (ADS)

Ratova, Marina; Kelly, Peter J.; West, Glen T.; Tosheva, Lubomira; Edge, Michele

2017-01-01

Titanium dioxide - bismuth tungstate composite materials were prepared by pulsed DC reactive magnetron sputtering of bismuth and tungsten metallic targets in argon/oxygen atmosphere onto anatase and rutile titania nanoparticles. The use of an oscillating bowl placed beneath the two magnetrons arranged in a co-planar closed field configuration enabled the deposition of bismuth tungstate onto loose powders, rather than a solid substrate. The atomic ratio of the bismuth/tungsten coatings was controlled by varying the power applied to each target. The effect of the bismuth tungstate coatings on the phase, optical and photocatalytic properties of titania was investigated by X-ray diffraction, energy-dispersive X-ray spectroscopy (EDX), Brunauer-Emmett-Teller (BET) surface area measurements, transmission electron microscopy (TEM), UV-vis diffuse reflectance spectroscopy and an acetone degradation test. The latter involved measurements of the rate of CO2 evolution under visible light irradiation of the photocatalysts, which indicated that the deposition of bismuth tungstate resulted in a significant enhancement of visible light activity, for both anatase and rutile titania particles. The best results were achieved for coatings with a bismuth to tungsten atomic ratio of 2:1. In addition, the mechanism by which the photocatalytic activity of the TiO2 nanoparticles was enhanced by compounding it with bismuth tungstate was studied by microwave cavity perturbation. The results of these tests confirmed that such enhancement of the photocatalytic properties is due to more efficient photogenerated charge carrier separation, as well as to the contribution of the intrinsic photocatalytic properties of Bi2WO6.

Mineral resource of the month: boron

USGS Publications Warehouse

Crangle, Robert D.

2012-01-01

The article offers information on the mineral, boron. Boron compounds, particularly borates, have more commercial applications than its elemental relative which is a metalloid. Making up the 90% of the borates that are used worldwide are colemanite, kernite, tincal, and ulexite. The main borate deposits are located in the Mojave Desert of the U.S., the Tethyan belt in southern Asia, and the Andean belt of South America. Underground and surface mining are being used in gathering boron compounds. INSETS: Fun facts;Boron production and consumption.

Bismuth-induced Raman modes in GaP 1– xBi x

DOE PAGES

Christian, Theresa M.; Fluegel, Brian; Beaton, Daniel A.; ...

2016-09-02

Here, dilute bismide semiconductor alloys are a promising material platform for optoelectronic devices due to drastic impacts of bismuth on the electronic structure of the alloy. At the same time, the details of bismuth incorporation in the lattice are not fully understood. In this work, we conduct Raman scattering spectroscopy on GaP 1- xBi x epilayers grown by molecular beam epitaxy (MBE) and identify several bismuth-related Raman features including gap vibration modes at 296, 303, and 314 cm -1. This study paves the way for more detailed analysis of the local symmetry at bismuth incorporation sites in the dilute bismidemore » alloy regime.« less

Investigation on gas sensing properties of Ag doped BiFeO3

NASA Astrophysics Data System (ADS)

Bagwaiya, Toshi; Khade, Poonam; Reshi, Hilal Ahmad; Bhattacharya, Shovit; Shelke, Vilas; Kaur, Manmeet; Debnath, A. K.; Muthe, K. P.; Gadkari, S. C.

2018-04-01

Bismuth ferrite (BFO) and Ag substituted Bismuth ferrite with perovskite structure have been synthesized using sol-gel method and investigated for their gas sensing properties. Single phase and rhombohedral crystal structure of the samples were confirmed from XRD pattern. Oxidation state of the elements is confirmed using X-Ray Photoelectron Spectroscopy (XPS). Since Ag substituted Bismuth ferrite exhibited pronounced response to H2S gas as compared to other gases, H2S gas sensing properties of Bismuth ferrite (BFO) and Ag substituted Bismuth ferrite were investigated in detail. Bi0.9Ag0.1FeO3 (BAFO) exhibits enhanced sensitivity, quick response and selectivity towards H2S as compared to BFO.

High-pressure synthesis and characterization of the first cerium fluoride borate CeB{sub 2}O{sub 4}F

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hinteregger, Ernst; Wurst, Klaus; Tribus, Martina

2013-08-15

CeB{sub 2}O{sub 4}F is the first cerium fluoride borate, which is exclusively built up of one-dimensional, infinite chains of condensed trigonal-planar [BO{sub 3}]{sup 3−} groups. This new cerium fluoride borate was synthesized under high-pressure/high-temperature conditions of 0.9 GPa and 1450 °C in a Walker-type multianvil apparatus. The compound crystallizes in the orthorhombic space group Pbca (No. 61) with eight formula units and the lattice parameters a=821.63(5), b=1257.50(9), c=726.71(6) pm, V=750.84(9) Å{sup 3}, R{sub 1}=0.0698, and wR{sub 2}=0.0682 (all data). The structure exhibits a 9+1 coordinated cerium ion, one three-fold coordinated fluoride ion and a one-dimensional chain of [BO{sub 3}]{sup 3−}more » groups. Furthermore, IR spectroscopy, Electron Micro Probe Analysis and temperature-dependent X-ray powder diffraction measurements were performed. - Graphical abstract: A new rare-earth fluoride borate CeB{sub 2}O{sub 4}F could be synthesized under high-pressure/high-temperature conditions of 0.9 °GPa and 1450 °Cin a Walker-type multianvil apparatus. The crystal structure represents a new structure type in the class of rare-earth fluoride borates. The structure exhibits a 9+1 coordinated cerium ion, one three-fold coordinated fluoride ion and a one-dimensional chain of [BO{sub 3}]{sup 3−} groups. A closer view on the ac-plane shows an interesting wave-like modulation of the borate chains. Highlights: • CeB{sub 2}O{sub 4}F is the first fluoride borate exclusively built up of one-dimensional, infinite chains of condensed trigonal-planar [BO{sub 3}]{sup 3−} groups. • CeB{sub 2}O{sub 4}F is the first cerium fluoride borate. • High-pressure conditions were necessary to synthesize CeB{sub 2}O{sub 4}F.« less

Structural Dynamics and Evolution of Bismuth Electrodes during Electrochemical Reduction of CO 2 in Imidazolium-Based Ionic Liquid Solutions

DOE PAGES

Medina-Ramos, Jonnathan; Lee, Sang Soo; Fister, Timothy T.; ...

2017-09-12

Real-time changes in the composition and structure of bismuth electrodes used for catalytic conversion of CO 2 into CO were examined via X-ray absorption spectroscopy (including XANES and EXAFS), electrochemical quartz crystal microbalance (EQCM) and in situ X-ray reflectivity (XR). Measurements were performed with bismuth electrodes immersed in acetonitrile (MeCN) solutions containing a 1-butyl-3-methylimidazolium ([BMIM] +) ionic liquid promoter or electrochemically inactive tetrabutylammonium supporting electrolytes (TBAPF 6 or TBAOTf). Altogether, these measurements show that bismuth electrodes are originally a mixture of bismuth oxides (including Bi 2O 3) and metallic bismuth (Bi 0), and that the reduction of oxidized bismuth speciesmore » to Bi 0 is fully achieved under potentials at which CO 2 activation takes place. Furthermore, EQCM measurements conducted during cyclic voltammetry revealed that a bismuth-coated quartz crystal exhibits significant shifts in resistance (ΔR) prior to the onset of CO 2 reduction near -1.75 V vs. Ag/AgCl and pronounced hysteresis in frequency (Δf) and ΔR, which suggests significant changes in roughness or viscosity at the Bi/[BMIM] + solution interface. In situ XR performed on rhombohedral Bi (001) oriented films indicates extensive restructuring of the bismuth film cathodes takes place upon polarization to potentials more negative than -1.6 V vs. Ag/AgCl, which is characterized by a decrease of the Bi (001) Bragg peak intensity of ≥50% in [BMIM]OTf solutions in the presence and absence of CO 2. Over 90% of the reflectivity is recovered during the anodic half-scan, suggesting that the structural changes are mostly reversible. By contrast, such a phenomenon is not observed for thin Bi (001) oriented films in solutions of tetrabutylammonium salts that do not promote CO 2 reduction. In conclusion, these results highlight that Bi electrodes undergo significant potential-dependent chemical and structural transformations in the presence of [BMIM] + based electrolytes, including the reduction of bismuth oxide to bismuth metal, changes in roughness and near-surface viscosity.« less

Enhancement of bismuth antibacterial activity with lipophilic thiol chelators.

PubMed Central

Domenico, P; Salo, R J; Novick, S G; Schoch, P E; Van Horn, K; Cunha, B A

1997-01-01

The antibacterial properties of bismuth are greatly enhanced when bismuth is combined with certain lipophilic thiol compounds. Antibacterial activity was enhanced from 25- to 300-fold by the following seven different thiols, in order of decreasing synergy: 1,3-propanedithiol, dimercaprol (BAL), dithiothreitol, 3-mercapto-2-butanol, beta-mercaptoethanol, 1-monothioglycerol, and mercaptoethylamine. The dithiols produced the greatest synergy with bismuth at optimum bismuth-thiol molar ratios of from 3:1 to 1:1. The monothiols were generally not as synergistic and required molar ratios of from 1:1 to 1:4 for optimum antibacterial activity. The most-active mono- or dithiols were also the most soluble in butanol. The intensity of the yellow formed by bismuth-thiol complexes reflected the degree of chelation and correlated with antibacterial potency at high molar ratios. The bismuth-BAL compound (BisBAL) was active against most bacteria, as assessed by broth dilution, agar diffusion, and agar dilution analyses. Staphylococci (MIC, 5 to 7 microM Bi3+) and Helicobacter pylori (MIC, 2.2 microM) were among the most sensitive bacteria. Gram-negative bacteria were sensitive (MIC, < 17 microM). Enterococci were relatively resistant (MIC, 63 microM Bi3+). The MIC range for anaerobes was 15 to 100 microM Bi3+, except for Clostridium difficile (MIC, 7.5 microM). Bactericidal activity averaged 29% above the MIC. Bactericidal activity increased with increasing pH and/or increasing temperature. Bismuth-thiol solubility, stability, and antibacterial activity depended on pH and the bismuth-thiol molar ratio. BisBAL was stable but ineffective against Escherichia coli at pH 4. Activity and instability (reactivity) increased with increasing alkalinity. BisBAL was acid soluble at a molar ratio of greater than 3:2 and alkaline soluble at a molar ratio of less than 2:3. In conclusion, certain lipophilic thiol compounds enhanced bismuth antibacterial activity against a broad spectrum of bacteria. The activity, solubility, and stability of BisBAL were strongly dependent on the pH, temperature, and molar ratio. Chelation of bismuth with certain thiol agents enhanced the solubility and lipophilicity of this cationic heavy metal, thereby significantly enhancing its potency and versatility as an antibacterial agent. PMID:9257744

21 CFR 73.2162 - Bismuth oxychloride.

Code of Federal Regulations, 2010 CFR

2010-04-01

... amounts consistent with good manufacturing practice. (c) Labeling. The color additive and any mixture... COLOR ADDITIVES EXEMPT FROM CERTIFICATION Cosmetics § 73.2162 Bismuth oxychloride. (a) Identity and specifications. (1) The color additive bismuth oxychloride shall conform in identity and specifications to the...

Piezo-generated charge mapping revealed through direct piezoelectric force microscopy.

PubMed

Gomez, A; Gich, M; Carretero-Genevrier, A; Puig, T; Obradors, X

2017-10-24

While piezoelectric and ferroelectric materials play a key role in many everyday applications, there are still a number of open questions related to their physics. To enhance our understanding of piezoelectrics and ferroelectrics, nanoscale characterization is essential. Here, we develop an atomic force microscopy based mode that obtains a direct quantitative analysis of the piezoelectric coefficient d 33 . We report nanoscale images of piezogenerated charge in a thick single crystal of periodically poled lithium niobate (PPLN), a bismuth ferrite (BiFO 3 ) thin film, and lead zirconate titanate (PZT) by applying a force and recording the current produced by these materials. The quantification of d 33 coefficients for PPLN (14 ± 3 pC per N) and BFO (43 ± 6 pC per N) is in agreement with the values reported in the literature. Even stronger evidence of the reliability of the method is provided by an equally accurate measurement of the significantly larger d 33 of PZT.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Medina-Ramos, Jonnathan; Lee, Sang Soo; Fister, Timothy T.

Real-time changes in the composition and structure of bismuth electrodes used for catalytic conversion of CO 2 into CO were examined via X-ray absorption spectroscopy (including XANES and EXAFS), electrochemical quartz crystal microbalance (EQCM) and in situ X-ray reflectivity (XR). Measurements were performed with bismuth electrodes immersed in acetonitrile (MeCN) solutions containing a 1-butyl-3-methylimidazolium ([BMIM] +) ionic liquid promoter or electrochemically inactive tetrabutylammonium supporting electrolytes (TBAPF 6 or TBAOTf). Altogether, these measurements show that bismuth electrodes are originally a mixture of bismuth oxides (including Bi 2O 3) and metallic bismuth (Bi 0), and that the reduction of oxidized bismuth speciesmore » to Bi 0 is fully achieved under potentials at which CO 2 activation takes place. Furthermore, EQCM measurements conducted during cyclic voltammetry revealed that a bismuth-coated quartz crystal exhibits significant shifts in resistance (ΔR) prior to the onset of CO 2 reduction near -1.75 V vs. Ag/AgCl and pronounced hysteresis in frequency (Δf) and ΔR, which suggests significant changes in roughness or viscosity at the Bi/[BMIM] + solution interface. In situ XR performed on rhombohedral Bi (001) oriented films indicates extensive restructuring of the bismuth film cathodes takes place upon polarization to potentials more negative than -1.6 V vs. Ag/AgCl, which is characterized by a decrease of the Bi (001) Bragg peak intensity of ≥50% in [BMIM]OTf solutions in the presence and absence of CO 2. Over 90% of the reflectivity is recovered during the anodic half-scan, suggesting that the structural changes are mostly reversible. By contrast, such a phenomenon is not observed for thin Bi (001) oriented films in solutions of tetrabutylammonium salts that do not promote CO 2 reduction. In conclusion, these results highlight that Bi electrodes undergo significant potential-dependent chemical and structural transformations in the presence of [BMIM] + based electrolytes, including the reduction of bismuth oxide to bismuth metal, changes in roughness and near-surface viscosity.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Medina-Ramos, Jonnathan; Lee, Sang Soo; Fister, Timothy T.

Real-time changes in the composition and structure of bismuth electrodes used for catalytic conversion of CO2 into CO were examined via X-ray absorption spectroscopy (including XANES and EXAFS), electrochemical quartz crystal microbalance (EQCM), and in situ X-ray reflectivity (XR). Measurements were performed with bismuth electrodes immersed in acetonitrile (MeCN) solutions containing a 1-butyl-3-methylimidazolium ([BMIM]+) ionic liquid promoter or electrochemically inactive tetrabutylammonium supporting electrolytes (TBAPF6 and TBAOTf). Altogether, these measurements show that bismuth electrodes are originally a mixture of bismuth oxides (including Bi2O3) and metallic bismuth (Bi0) and that the reduction of oxidized bismuth species to Bi0 is fully achieved undermore » potentials at which CO2 activation takes place. Furthermore, EQCM measurements conducted during cyclic voltammetry revealed that a bismuth-coated quartz crystal exhibits significant shifts in resistance (ΔR) prior to the onset of CO2 reduction near -1.75 V vs Ag/AgCl and pronounced hysteresis in frequency (Δf) and ΔR, which suggests significant changes in roughness or viscosity at the Bi/[BMIM]+ solution interface. In situ XR performed on rhombohedral Bi (001) oriented films indicates that extensive restructuring of the bismuth film cathodes takes place upon polarization to potentials more negative than -1.6 V vs Ag/AgCl, which is characterized by a decrease of the Bi (001) Bragg peak intensity of ≥50% in [BMIM]OTf solutions in the presence and absence of CO2. Over 90% of the reflectivity is recovered during the anodic half-scan, suggesting that the structural changes are mostly reversible. In contrast, such a phenomenon is not observed for thin Bi (001) oriented films in solutions of tetrabutylammonium salts that do not promote CO2 reduction. Overall, these results highlight that Bi electrodes undergo significant potential-dependent chemical and structural transformations in the presence of [BMIM]+-based electrolytes, including the reduction of bismuth oxide to bismuth metal and changes in roughness and near-surface viscosity.« less

Natural circulation in a liquid metal one-dimensional loop

NASA Astrophysics Data System (ADS)

Tarantino, M.; De Grandis, S.; Benamati, G.; Oriolo, F.

2008-06-01

A wide use of pure lead, as well as its alloys (such as lead-bismuth, lead-lithium), is foreseen in several nuclear-related fields: it is studied as coolant in critical and sub-critical nuclear reactors, as spallation target for neutron generation in several applications and for tritium generation in fusion systems. In this framework, a new facility named NAtural CIrculation Experiment (NACIE), has been designed at ENEA-Brasimone Research Centre. NACIE is a rectangular loop, made by stainless steel pipes. It consists mainly of a cold and hot leg and an expansion tank installed on the top of the loop. A fuel bundle simulator, made by three electrical heaters placed in a triangular lattice, is located in the lower part of the cold leg, while a tube in tube heat exchanger is installed in the upper part of the hot leg. The adopted secondary fluid is THT oil, while the foreseen primary fluid for the tests is lead-bismuth in eutectic composition (LBE). The aim of the facility is to carry out experimental tests of natural circulation and collect data on the heat transfer coefficient (HTC) for heavy liquid metal flowing through rod bundles. The paper is focused on the preliminary estimation of the LBE flow rate along the loop. An analytical methodology has been applied, solving the continuity, momentum and energy transport equations under appropriate hypothesis. Moreover numerical simulations have been performed. The FLUENT 6.2 CFD code has been utilized for the numerical simulations. The main results carried out from the pre-tests simulations are illustrated in the paper, and a comparison with the theoretical estimations is done.

Separation of bismuth from gram amounts of thallium and silver by cation-exchange chromatography in nitric acid.

PubMed

Meintjies, E; Strelow, F W; Victor, A H

1987-04-01

Traces and small amounts of bismuth can be separated from gram amounts of thallium and silver by successively eluting these elements with 0.3M and 0.6M nitric acid from a column containing 13 ml (3 g) of AG50W-X4, a cation-exchanger (100-200 mesh particle size) with low cross-linking. Bismuth is retained and can be eluted with 0.2M hydrobromic acid containing 20% v/v acetone, leaving many other trace elements absorbed. Elution of thallium is quite sharp, but silver shows a small amount of tailing (less than 1 gmg/ml silver in the eluate) when gram amounts are present, between 20 and 80 mug of silver appearing in the bismuth fraction. Relevant elution curves and results for the analysis of synthetic mixtures containing between 50 mug and 10 mg of bismuth and up to more than 1 g of thallium and silver are presented, as well as results for bismuth in a sample of thallium metal and in Merck thallium(I) carbonate. As little as 0.01 ppm of bismuth can be determined when the separation is combined with electrothermal atomic-absorption spectrometry.

Evaluation of the strength and radiopacity of Portland cement with varying additions of bismuth oxide.

PubMed

Saliba, E; Abbassi-Ghadi, S; Vowles, R; Camilleri, J; Hooper, S; Camilleri, J

2009-04-01

To study the effect of addition of various proportions of bismuth oxide on compressive strength and radiopacity of Portland cement. The compressive strength of white Portland cement and cement replaced with 10, 15, 20, 25 and 30% bismuth oxide was evaluated by testing cylinders 6 mm in diameter and 12 mm high. Twelve cylinders were tested for each material under study. The radiopacity of the cements tested was evaluated using an aluminium step-wedge and densitometer. The optical density was compared with the relevant thickness of aluminium (Al). Statistical analysis was performed using Analysis of Variance (ANOVA) with P = 0.05 and Tukey test to perform multiple comparison tests. Various additions of bismuth oxide had no significant effect on the strength of the material when compared with the unmodified Portland cement (P > 0.05). The radiopacity of the cements tested ranged from 2.02 mm Al for Portland cement to 9.79 mm Al for the highest bismuth replacement. Addition of bismuth oxide did not affect the compressive strength of Portland cement. All the bismuth oxide cement mixtures had radio-opacities higher than 3 mm thickness of aluminium.

Study of the structure, dielectric and ferroelectric behavior of BaBi4+δTi4O15 ceramics

NASA Astrophysics Data System (ADS)

Khokhar, Anita; Goyal, Parveen K.; Thakur, O. P.; Sreenivas, K.

2016-05-01

The structure and ferroelectric properties of excess bismuth doped barium bismuth titanate BaBi4+δTi4O15 (δ = 2 - 10 wt.%)) ceramics prepared by solid-state reaction method have been investigated. X-ray diffraction (XRD) confirms the formation of a single phase material with a change in the orthorhombic distortion with varying excess of bismuth content. There is no change in the phase transition temperature (Tm) while the relaxor behaviour has been modified significantly with excess of bismuth doping. Saturated hysteresis loops with high remnant polarization (Pr ~ 12.5 µC/cm2), low coercive fields (Ec ~ 26 kV/cm) are measured and a high piezoelectric coefficient (d33 ~ 29 pC/N) is achieved in poled BaBi4Ti4O15 ceramics prepared with up to 8 wt.% of excess bismuth oxide. The improvement in the ferroelectric properties with increase in the excess bismuth content in BaBi4Ti4O15 ceramics has been explained in terms of changing oxygen vacancy concentration and structural relaxation. Tunable ferroelectric materials can be obtained by manipulating the doping amount of excess bismuth.

Adverse events with bismuth salts for Helicobacter pylori eradication: Systematic review and meta-analysis

PubMed Central

Ford, Alexander C; Malfertheiner, Peter; Giguère, Monique; Santana, José; Khan, Mostafizur; Moayyedi, Paul

2008-01-01

AIM: To assess the safety of bismuth used in Helicobacter pylori (H pylori) eradication therapy regimens. METHODS: We conducted a systematic review and meta-analysis. MEDLINE and EMBASE were searched (up to October 2007) to identify randomised controlled trials comparing bismuth with placebo or no treatment, or bismuth salts in combination with antibiotics as part of eradication therapy with the same dose and duration of antibiotics alone or, in combination, with acid suppression. Total numbers of adverse events were recorded. Data were pooled and expressed as relative risks with 95% confidence intervals (CI). RESULTS: We identified 35 randomised controlled trials containing 4763 patients. There were no serious adverse events occurring with bismuth therapy. There was no statistically significant difference detected in total adverse events with bismuth [relative risk (RR) = 1.01; 95% CI: 0.87-1.16], specific individual adverse events, with the exception of dark stools (RR = 5.06; 95% CI: 1.59-16.12), or adverse events leading to withdrawal of therapy (RR = 0.86; 95% CI: 0.54-1.37). CONCLUSION: Bismuth for the treatment of H pylori is safe and well-tolerated. The only adverse event occurring significantly more commonly was dark stools. PMID:19109870

A novel structure photonic crystal fiber based on bismuth-oxide for optical parametric amplification

NASA Astrophysics Data System (ADS)

Jin, Cang; Yuan, Jinhui; Yu, Chongxiu

2010-11-01

The heavy metal oxide glasses containing bismuth such as bismuth sesquioxide show unique high refractive index. In addition, the bismuth-oxide based glass does not include toxic elements such as Pb, As, Se, Te, and exhibits well chemical, mechanical and thermal stability. Hence, it is used to fabricate high nonlinear fiber for nonlinear optical application. Although the bismuth-oxide based high nonlinear fiber can be fusion-spliced to conventional silica fibers and have above advantages, yet it suffers from large group velocity dispersion because of material chromatic dispersion which restricts its utility. In regard to this, the micro-structure was introduced to adjust the dispersion of bismuth-oxide high nonlinear fiber in the 1550nm wave-band. In this paper, a hexagonal solid-core micro-structure is developed to balance its dispersion and nonlinearity. Our simulation and calculation results show that the bismuth-oxide based photonic crystal fiber has near zero dispersion around 1550nm where the optical parametric amplification suitable wavelength is. Its dispersion slop in the communication wavelength range is also relatively flat. Moreover, both nonlinear coefficient and model filed distribution were simulated, respectively.

Green colorants based on energetic azole borates.

PubMed

Glück, Johann; Klapötke, Thomas M; Rusan, Magdalena; Stierstorfer, Jörg

2014-11-24

The investigation of green-burning boron-based compounds as colorants in pyrotechnic formulations as alternative for barium nitrate, which is a hazard to health and to the environment, is reported. Metal-free and nitrogen-rich dihydrobis(5-aminotetrazolyl)borate salts and dihydrobis(1,3,4-triazolyl)borate salts have been synthesized and characterized by NMR spectroscopy, elemental analysis, mass spectrometry, and vibrational spectroscopy. Their thermal and energetic properties have been determined as well. Several pyrotechnic compositions using selected azolyl borate salts as green colorants were investigated. Formulations with ammonium dinitramide and ammonium nitrate as oxidizers and boron and magnesium as fuels were tested. The burn time, dominant wavelength, spectral purity, luminous intensity, and luminous efficiency as well as the thermal and energetic properties of these compositions were measured. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

The molecular structure of the borate mineral rhodizite (K, Cs)Al4Be4(B, Be)12O28--a vibrational spectroscopic study.

PubMed

Frost, Ray L; López, Andrés; Xi, Yunfei; Scholz, Ricardo; Souza, Larissa; Lana, Cristiano

2014-07-15

We have studied the borate mineral rhodizite (K, Cs)Al4Be4(B, Be)12O28 using a combination of DEM with EDX and vibrational spectroscopic techniques. The mineral occurs as colorless, gray, yellow to white crystals in the triclinic crystal system. The studied sample is from the Antandrokomby Mine, Sahatany valley, Madagascar. The mineral is prized as a semi-precious jewel. Semi-quantitative chemical composition shows a Al, Ca, borate with minor amounts of K, Mg and Cs. The mineral has a characteristic borate Raman spectrum and bands are assigned to the stretching and bending modes of B, Be and Al. No Raman bands in the OH stretching region were observed. Copyright © 2014 Elsevier B.V. All rights reserved.

Thermally reversible gels in electrophoresis. I - Matrix characterization

NASA Technical Reports Server (NTRS)

Righetti, Pier Giorgio; Snyder, Robert S.

1988-01-01

Two series of thermally reversible hydrogen-bonded gels have been characterized: (5 pct) PVA-(4 pct) PEG and (5 pct) PVA-(0.04 pct) borate gels. They both have extremely low melting points (16-17 C) and could be of potential interest for recovery of proteins after preparative electrophoresis. The PVA-borate gels can be exploited in the pH range 7-11 by progressively increasing the borate content in the pH interval 8 to 7 and concomitantly decreasing the borate levels in the pH zone 8 to 11. It is hypothesized that the low melting point of these gels is due to the fact that they are sparingly and sparsely hydrogen bonded along the PVA chain: on the average, 1 OH group out of 3 or 4 OH groups in the PVA polymer should be engaged in H-bond formation.

METHOD OF PREPARING URANIUM, THORIUM, OR PLUTONIUM OXIDES IN LIQUID BISMUTH

DOEpatents

Davidson, J.K.; Robb, W.L.; Salmon, O.N.

1960-11-22

A method is given for forming compositions, as well as the compositions themselves, employing uranium hydride in a liquid bismuth composition to increase the solubility of uranium, plutonium and thorium oxides in the liquid bismuth. The finely divided oxide of uranium, plutonium. or thorium is mixed with the liquid bismuth and uranium hydride, the hydride being present in an amount equal to about 3 at. %, heated to about 5OO deg C, agitated and thereafter cooled and excess resultant hydrogen removed therefrom.

Process for removal of mineral particulates from coal-derived liquids

DOEpatents

McDowell, William J.

1980-01-01

Suspended mineral solids are separated from a coal-derived liquid containing the solids by a process comprising the steps of: (a) contacting said coal-derived liquid containing solids with a molten additive having a melting point of 100.degree.-500.degree. C. in an amount of up to 50 wt. % with respect to said coal-derived liquid containing solids, said solids present in an amount effective to increase the particle size of said mineral solids and comprising material or mixtures of material selected from the group of alkali metal hydroxides and inorganic salts having antimony, tin, lithium, sodium, potassium, magnesium, calcium, beryllium, aluminum, zinc, molybdenum, cobalt, nickel, ruthenium, rhodium or iron cations and chloride, iodide, bromide, sulfate, phosphate, borate, carbonate, sulfite, or silicate anions; and (b) maintaining said coal-derived liquid in contact with said molten additive for sufficient time to permit said mineral matter to agglomerate, thereby increasing the mean particle size of said mineral solids; and (c) recovering a coal-derived liquid product having reduced mineral solids content. The process can be carried out with less than 5 wt. % additive and in the absence of hydrogen pressure.

Effect of Variable Oxidation States of Vanadium on the Structural, Optical, and Dielectric Properties of B2O3-Li2O-ZnO-V2O5 Glasses.

PubMed

Arya, S K; Danewalia, S S; Arora, Manju; Singh, K

2016-12-01

In the present study, the effect of variable vanadium oxidation states on the structural, optical, and dielectric properties of vanadium oxide containing lithium borate glasses has been investigated. Electron paramagnetic resonance studies indicate that vanadium in these glasses is mostly in the V 4+ state, having a tetragonal symmetry. As the glass composition of V 2 O 5 increases, tetragonality also increases at the cost of octahedral symmetry. The photoluminescence (PL) spectra of these glasses are dominated by zinc oxide transition, whereas the peaks pertaining to the vanadyl group are not visible in the PL spectra. The optical absorption spectra show a single wide absorption band, which is attributed to V 4+ ions in these glasses. The ac conductivity of the glasses increases with an increase in vanadium content. The highest electrical conductivity observed is ∼10 -5 S cm -1 at 250 °C for the glass with 2.5 mol % V 2 O 5 . Electrical conductivity is dominated by electron conduction, as indicated by the activation energy calculation.

Analysis of barium and strontium in sediments by dc plasma emission spectrometry

USGS Publications Warehouse

Bowker, P.C.; Manheim, F. T.

1982-01-01

The dc plasma are is suited to analysis of barium and strontium in a wide range of sedimentary rock matrices, from sands, shales, and carbonates, to ferromanganese nodules. Samples containing 10 ppm to more than 3000 ppm barium and strontium were studied. Both alkali (3500 ppm lithium borate, from a preliminary fusion) and lanthanum salts (1%) in the final solution are needed to achieve freedom from systematic effects due to extreme variation in matrix. In the absence of La, neither Li, Na, K, nor Cs totally eliminated effects of Al and other constituents on emission. Silica addition to the fusion helps achieve proper flux viscosity to aid removal of fused beads from graphite crucibles. The effect of refractory-substance formers such as aluminum with calcium can be reduced or removed by selection of a portion of the are for emission measurement. However, it was decided not to pursue this approach because of loss in analytical sensitivity and need for greater precision in optical adjustment. Analysis of standard rock samples showed generally satisfactory agreement with precision methods of analysis, and some new standard rock data are reported.

Low-energy neutron detector based upon lithium lanthanide borate scintillators

DOEpatents

Czirr, John B.

1998-01-01

An apparatus for detecting neutrons includes a cerium activated scintillation crystal containing .sup.10 B, with the scintillation crystal emitting light in response to .alpha. particles emitted from the .sup.10 B(n,.alpha.)Li* reaction. The apparatus also includes a gamma scintillator positioned adjacent the crystal and which generates light in response to gamma rays emitted from the decay of Li*. The apparatus further includes a first and a second light-to-electronic signal converter each positioned to respectively receive light from the crystal and the gamma scintillator, and each respectively outputting first and second electronic signals representative of .alpha. particles from the .sup.10 B(n,.alpha.)Li* reaction and gamma rays from the .sup.10 B(n,.alpha.)Li* reaction. The apparatus includes a coincidence circuit connected to receive the first and second signals and which generates a coincidence signal when the first and second signals coincide. The apparatus also includes a data analyzer for receiving an additional signal from at least one of the first and second converters, and for operating in response to the coincidence signal.

Chemical characterization of solid polymer electrolyte membrane surfaces in LiFePO4 half-cells

NASA Astrophysics Data System (ADS)

Kyu, Thein; He, Ruixuan; Peng, Fang; Dunn, William E.; Kyu's Group Team, Dr.

High temperature (60 °C) capacity retention of succinonitrile plasticized solid polymer electrolyte membrane (PEM) in a LiFePO4 half-cell was investigated with or without lithium bis(oxalato)borate (LiBOB) modification. Various symmetric cells and half-cells were studied under different thermal and electrochemical conditions. At room temperature cycling, the unmodified PEM in the half-cell appeared stable up to 50 cycles tested. Upon cycling at 60 °C, the capacity decays rapidly and concurrently the cell resistance increased. The chemical compositions of the solid PEM surfaces on both cathode and anode sides were analyzed. New IR bands (including those belonged to amide) were discerned on the unmodified PEM surface of the Li electrode side at 60 °C suggestive of side reaction, but no new bands develop during room temperature cycling. To our astonishment, the side reaction was effectively suppressed upon LiBOB addition (0.4 wt%) into the PEM, contributing to increased high temperature capacity retention at 60°C. Plausible mechanisms of capacity fading and improved cycling performance due to LiBOB modification are discussed.

Radiochemical determination of 241Am and Pu(alpha) in environmental materials.

PubMed

Warwick, P E; Croudace, I W; Oh, J S

2001-07-15

Americium-241 and plutonium determinations will become of greater importance over the coming decades as 137Cs and 241Pu decay. The impact of 137Cs on environmental chronology has been great, but its potency is waning as it decays and diffuses. Having 241Am and Pu as unequivocal markers for the 1963 weapon fallout maximum is important for short time scale environmental work, but a fast and reliable procedure is required for their separation. The developed method described here begins by digesting samples using a lithium borate fusion although an aqua regia leachate is also effective in many instances. Isolation of the Am and Pu is then achieved using a combination of extraction chromatography and conventional anion exchange chromatography. The whole procedure has been optimized, validated, and assessed for safety. The straightforwardness of this technique permits the analysis of large numbers of samples and makes 241Am-based techniques for high-resolution sediment accumulation rate studies attractive. In addition, the technique can be employed for the sequential measurement of Pu and Am in environmental surveillance programs, potentially reducing analytical costs and turnround times.

Point defect disorder in high-temperature solution grown Sr6Tb0.94Fe1.06(BO3)6 single crystals

NASA Astrophysics Data System (ADS)

Velázquez, M.; Péchev, S.; Duttine, M.; Wattiaux, A.; Labrugère, C.; Veber, Ph.; Buffière, S.; Denux, D.

2018-08-01

New Sr6Tb0.94Fe1.06(BO3)6 single crystals were obtained from lithium borate high-temperature solution growth under controlled atmosphere. Their average crystal structure was found to adopt the trigonal R-3 space group with lattice parameters a = 12.2164 Å and c = 9.1934 Å. A combined multiscale characterization approach, involving diffuse reflectance, X-ray photoelectron (XPS) and Mössbauer spectroscopies, was undertaken to establish the exact nature of the point defect disorder in this crystal structure. The FeTb× antisite disorder in the Sr6Tb0.94Fe1.06(BO3)6 single crystals is different from the kind of point defect disorder known to exist in the powder phase material counterpart. The absence of Tb4+ cations in the crystal lattice was established by XPS, and that of any phase transition down to 4 K was checked by specific heat measurements. The magnetic susceptibility curve was found to follow a Curie-Weiss behaviour in the 4-354 K temperature range.

21 CFR 73.1162 - Bismuth oxychloride.

Code of Federal Regulations, 2010 CFR

2010-04-01

... COLOR ADDITIVES EXEMPT FROM CERTIFICATION Drugs § 73.1162 Bismuth oxychloride. (a) Identity. (1) The color additive bismuth oxychloride is a synthetically prepared white or nearly white amorphous or finely crystalline, odorless powder consisting principally of BiOCl. (2) Color additive mixtures for drug use made...

Bismuth doping effect on crystal structure and photodegradation activity of Bi-TiO2 nanoparticles

NASA Astrophysics Data System (ADS)

Wu, Ming-Chung; Chang, Yin-Hsuan; Lin, Ting-Han

2017-04-01

The bismuth precursor is adopted as dopant to synthesize bismuth doped titanium dioxide nanoparticles (Bi-TiO2 NPs) with sol-gel method following by the thermal annealing treatment. We systematically developed a series of Bi-TiO2 NPs at several calcination temperatures and discovered the corresponding crystal structure by varying the bismuth doping concentration. At a certain 650 °C calcination temperature, the crystal structure of bismuth titanate (Bi2Ti2O7) is formed when the bismuth doping concentration is as high as 10.0 mol %. The photocatalytic activity of Bi-TiO2 NPs is increased by varying the doping concentration at the particular calcination temperature. By the definition X-ray diffraction (XRD) structural identification, a phase diagram of Bi-TiO2 NPs in doping concentration versus calcination temperature is provided. It can be useful for further study in the crystal structure engineering and the development of photocatalyst.

Ultrasonication of Bismuth Telluride Nanocrystals Fabricated by Solvothermal Method

NASA Technical Reports Server (NTRS)

Chu, Sang-Hyon; Choi, Sang H.; Kim, Jae-Woo; King, Glen C.; Elliott, James R.

2006-01-01

The objective of this study is to evaluate the effect of ultrasonication on bismuth telluride nanocrystals prepared by solvothermal method. In this study, a low dimensional nanocrystal of bismuth telluride (Bi2Te3) was synthesized by a solvothermal process in an autoclave at 180 C and 200 psi. During the solvothermal reaction, organic surfactants effectively prevented unwanted aggregation of nanocrystals in a selected solvent while controlling the shape of the nanocrystal. The atomic ratio of bismuth and tellurium was determined by energy dispersive spectroscopy (EDS). The cavitational energy created by the ultrasonic probe was varied by the ultrasonication process time, while power amplitude remained constant. The nanocrystal size and its size distribution were measured by field emission scanning electron microscopy (FESEM) and a dynamic light scattering system. When the ultrasonication time increased, the average size of bismuth telluride nanocrystal gradually increased due to the direct collision of nanocrystals. The polydispersity of the nanocrystals showed a minimum when the ultrasonication was applied for 5 min. Keywords: bismuth telluride, nanocrystal, low-dimensional, ultrasonication, solvothermal

Adaptive statistical iterative reconstruction and bismuth shielding for evaluation of dose reduction to the eye and image quality during head CT

NASA Astrophysics Data System (ADS)

Kim, Myeong Seong; Choi, Jiwon; Kim, Sun Young; Kweon, Dae Cheol

2014-03-01

There is a concern regarding the adverse effects of increasing radiation doses due to repeated computed tomography (CT) scans, especially in radiosensitive organs and portions thereof, such as the lenses of the eyes. Bismuth shielding with an adaptive statistical iterative reconstruction (ASIR) algorithm was recently introduced in our clinic as a method to reduce the absorbed radiation dose. This technique was applied to the lens of the eye during CT scans. The purpose of this study was to evaluate the reduction in the absorbed radiation dose and to determine the noise level when using bismuth shielding and the ASIR algorithm with the GE DC 750 HD 64-channel CT scanner for CT of the head of a humanoid phantom. With the use of bismuth shielding, the noise level was higher in the beam-hardening artifact areas than in the revealed artifact areas. However, with the use of ASIR, the noise level was lower than that with the use of bismuth alone; it was also lower in the artifact areas. The reduction in the radiation dose with the use of bismuth was greatest at the surface of the phantom to a limited depth. In conclusion, it is possible to reduce the radiation level and slightly decrease the bismuth-induced noise level by using a combination of ASIR as an algorithm process and bismuth as an in-plane hardware-type shielding method.

Zirconocene mediated acetylboron chemistry.

PubMed

Jian, Zhongbao; Daniliuc, Constantin G; Kehr, Gerald; Erker, Gerhard

2018-05-31

The methyl zirconocene complex Cp*2Zr(Me)OMes reacts with H3C-B(C6F5)2 and CO to give the respective acetyl(methyl)borate Zr complex. Cp*2Zr(H)OMes reacts with H3C-B(C6F5)2 and CO to give the respective acetyl(hydrido)borate Zr product, admixed with a minor amount of the formyl(methyl)borate Zr complex isomer. Prolonged exposure to CO under close to ambient conditions results in the uptake of another CO equivalent to yield the corresponding borata-β-lactone zirconocene product.

The effects of borate minerals on the synthesis of nucleic acid bases, amino acids and biogenic carboxylic acids from formamide.

PubMed

Saladino, Raffaele; Barontini, Maurizio; Cossetti, Cristina; Di Mauro, Ernesto; Crestini, Claudia

2011-08-01

The thermal condensation of formamide in the presence of mineral borates is reported. The products afforded are precursors of nucleic acids, amino acids derivatives and carboxylic acids. The efficiency and the selectivity of the reaction was studied in relation to the elemental composition of the 18 minerals analyzed. The possibility of synthesizing at the same time building blocks of both genetic and metabolic apparatuses, along with the production of amino acids, highlights the interest of the formamide/borate system in prebiotic chemistry.

40 CFR 471.13 - New source performance standards (NSPS).

Code of Federal Regulations, 2011 CFR

2011-07-01

... GUIDELINES AND STANDARDS NONFERROUS METALS FORMING AND METAL POWDERS POINT SOURCE CATEGORY Lead-Tin-Bismuth...-tin-bismuth forming operations' process wastewater shall not exceed the following values: (a) Rolling... monthly average mg/off-kg (pounds per million off-pounds) of lead-tin-bismuth rolled with emulsions...

40 CFR 471.13 - New source performance standards (NSPS).

Code of Federal Regulations, 2010 CFR

2010-07-01

... GUIDELINES AND STANDARDS NONFERROUS METALS FORMING AND METAL POWDERS POINT SOURCE CATEGORY Lead-Tin-Bismuth...-tin-bismuth forming operations' process wastewater shall not exceed the following values: (a) Rolling... monthly average mg/off-kg (pounds per million off-pounds) of lead-tin-bismuth rolled with emulsions...

Chemical composition and mineralogy of borate from Rio Grande deposit, Uyuni (Bolivia) as raw materials for industrial applications

NASA Astrophysics Data System (ADS)

Guillen Vargas, Julio; Arancibia, Jony Roger Hans; Alfonso, Pura; Garcia-Valles, Maite; Parcerisa, David; Martinez, Salvador

2014-05-01

Bolivia has large tailings as a result of the historic and present-day Sn mining activity developed extensively in that country. Tailings produced in these mining activities have an appropriate composition to reprocess them and make silicate glass and glass-ceramics, obtaining the valorization of wastes and reducing the visual and chemical impact. Reprocessing the wastes to make glass and glass-ceramics prevents the leaching of heavy metals from those wastes because they are retained in the structure of the glass. Furthermore, an option to increase the economic value of these glasses is the introduction of boron and other additives to produce borosilicate glass. In this study a characterization of the Rio Grande borate deposit for its use in the manufacture of borosilicate glass is presented. Mineralogy was determined by X-ray diffraction (XRD), and Fourier transforms infrared spectroscopy (FTIR); textures were observed by scanning electron microscopy (SEM) and chemical composition was determined by inductively coupled plasma mass spectrometry (ICP-MS). The Rio Grande borate deposit is located in an area of about 50 km2 close to the south of the Salar of Uyuni, in the Río Grande de Lípez Delta. Borates occur in the contact between fluvio-deltaic and lacustrine sediments from water raising the surface by capillarity. The borates crop out in an extent area but towards the west they are covered by fluvio-deltaic sediments, which can be up to 2 m thick. These borates occur as lenses 50-100 m in diameter and layers up to 1 m thick. They usually form brittle nodules with a cotton-ball texture. Chemical composition of the Rio Grande borates is CaO, 11.82-13.83 wt%; Na2O, 13.50-19.35 wt%; K2O, 0.05- 1.04 wt%; MgO, 0.42-1.46 wt%; B2O3, 36.21-42.60 wt%; SiO2, up to 0.53 wt% and SO2, up to 0.60 wt%. Trace elements are low: Sr content is between 151-786 ppm, Al 12-676 ppm, Mn between 1-17 ppm, As 2-10 ppm and Fe between 9-376 ppm. The most abundant borate mineral in this deposit is ulexite (NaCaB5.5H20), halite can reach up to 17 wt% and gypsum up to 1.2 wt.%. Calcite occurs in minor contents. Ulexite exhibits a fibrous morphology with fibers oriented parallel each other. Purity of borates from the Rio Grande deposits makes them suitable for the most restrictive applications. Chemistry of these borates is in accordance with the necessary composition for obtaining borosilicate glasses. Acknowledgements: This work was partly financed by the project AECID: A3/042750/11, and the SGR 2009SGR-00444.

Supramolecular assembly of borate with quaternary ammonium: Crystal structure and tunable luminescent properties

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liang, Jie; Wang, Yong-gang; Wang, Ying-xia, E-mail: wangyx@pku.edu.cn

2013-04-15

A new borate [C{sub 6}H{sub 16}N][B{sub 5}O{sub 6}(OH){sub 4}] (1) is synthesized hydrothermally by the reaction of isopropyltrimethylammonium hydroxide with boric acid. It crystallizes in the triclinic space group P-1 with the parameters a=9.1578(10) Å, b=9.372(9) Å, c=9.9812(10) Å, α=66.508(2)°, β=74.751(2)°, γ=81.893(2)°. The [B{sub 5}O{sub 6}(OH){sub 4}]{sup −} anions are interlinked via hydrogen bonding forming a 3D supramolecular network containing large cavities, where reside the (CH{sub 3}){sub 3}(i-C{sub 3}H{sub 7}) N{sup +} cations. This borate shows tunable luminescent properties with temperature, heating-treatment, exciting-light, and solvents. The fluorescent intensity of 1 enhances 6-fold with decreasing the temperature from 25 K tomore » 78 K. By treatment under different temperatures, the luminescence of 1 shifted from blue to white and the sample treated at 230 °C emits bright white light to naked eyes. The hybrid borate can disperse in different solvents, and shows a red-shifted and intense emission in polar solvents. - Graphical abstract: The new quaternary ammonium borate [C{sub 6}H{sub 17}N][B{sub 5}O{sub 6}(OH){sub 4}] contains a 3D supramolecular network formed by hydrogen bond linked [B{sub 5}O{sub 6}(OH){sub 4}]{sup −} anions and shows tunable luminescent properties with temperature, excitation light, and solvents. Highlights: ► A novel quaternary ammonium borate was synthesized. ► It possesses a supramolecular network fomed by H-bonded [B{sub 5}O{sub 6}(OH){sub 4}]{sup −} anions. ► This borate shows tunable luminescent properties with temperature, heating treatment, excitation light, and solvents.« less

Impact of vanadium ions in barium borate glass

NASA Astrophysics Data System (ADS)

Abdelghany, A. M.; Hammad, Ahmed H.

2015-02-01

Combined optical and infrared spectral measurements of prepared barium borate glasses containing different concentrations of V2O5 were carried out. Vanadium containing glasses exhibit extended UV-visible (UV/Vis.) bands when compared with base binary borate glass. UV/Vis. spectrum shows the presence of an unsymmetrical strong UV broad band centered at 214 nm attributed to the presence of unavoidable trace iron impurities within the raw materials used for the preparation of such glass. The calculated direct and indirect optical band gaps are found to decrease with increasing the vanadium content (2.9:137 for indirect and 3.99:2.01 for direct transition). This change was discussed in terms of structural changes in the glass network. Infrared absorption spectra of the glasses reveal the appearance of both triangular and tetrahedral borate units. Electron spin resonance analyses indicate the presence of unpaired species in sufficient quantity to be identified and to confirm the spectral data.

Effect of Borates and Silicates on Wearing Properties of Mao Coatings

NASA Astrophysics Data System (ADS)

Zhang, Yu; Zhao, Yan-Wei; Xiang, Nan; Song, Ren-Guo

In the present study, microarc oxidation (MAO) coatings were formed on ZL101A aluminum alloy in an electrolytic bath containing 3g/L KOH + 2g/L Na2WO4+ 4g/L KF. The morphology and wearing behavior were investigated. In both electrolytes, the additives were borates (Na2B4O718g/L) and silicates (Na2SiO3 18g/L), respectively. It was found that the coating formed in borates-containing electrolyte was of compact and smooth structure than that of the one formed in silicates-containing electrolyte at the optimum treatment time. It was found that all the coatings were composed of á-Al2O3 and ã-Al2O3. The microhardness and wear tests proved that the coating formed in borates-containing electrolyte was having better mechanical properties than those of the coating formed in silicates-containing electrolyte.

21 CFR 73.1162 - Bismuth oxychloride.

Code of Federal Regulations, 2013 CFR

2013-04-01

... 21 Food and Drugs 1 2013-04-01 2013-04-01 false Bismuth oxychloride. 73.1162 Section 73.1162 Food and Drugs FOOD AND DRUG ADMINISTRATION, DEPARTMENT OF HEALTH AND HUMAN SERVICES GENERAL LISTING OF COLOR ADDITIVES EXEMPT FROM CERTIFICATION Drugs § 73.1162 Bismuth oxychloride. (a) Identity. (1) The...

21 CFR 73.1162 - Bismuth oxychloride.

Code of Federal Regulations, 2012 CFR

2012-04-01

... 21 Food and Drugs 1 2012-04-01 2012-04-01 false Bismuth oxychloride. 73.1162 Section 73.1162 Food and Drugs FOOD AND DRUG ADMINISTRATION, DEPARTMENT OF HEALTH AND HUMAN SERVICES GENERAL LISTING OF COLOR ADDITIVES EXEMPT FROM CERTIFICATION Drugs § 73.1162 Bismuth oxychloride. (a) Identity. (1) The...

21 CFR 73.1162 - Bismuth oxychloride.

Code of Federal Regulations, 2014 CFR

2014-04-01

... 21 Food and Drugs 1 2014-04-01 2014-04-01 false Bismuth oxychloride. 73.1162 Section 73.1162 Food and Drugs FOOD AND DRUG ADMINISTRATION, DEPARTMENT OF HEALTH AND HUMAN SERVICES GENERAL LISTING OF COLOR ADDITIVES EXEMPT FROM CERTIFICATION Drugs § 73.1162 Bismuth oxychloride. (a) Identity. (1) The...

40 CFR 471.14 - Pretreatment standards for existing sources (PSES).

Code of Federal Regulations, 2012 CFR

2012-07-01

... CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.14 Pretreatment standards for existing sources (PSES... in lead-tin-bismuth forming process wastewater introduced into a POTW shall not exceed the following... Maximum for monthly average mg/off-kg (pounds per million off-pounds) of lead-tin-bismuth rolled with...

40 CFR 471.14 - Pretreatment standards for existing sources (PSES).

Code of Federal Regulations, 2011 CFR

2011-07-01

...-Tin-Bismuth Forming Subcategory § 471.14 Pretreatment standards for existing sources (PSES). Except as...-tin-bismuth forming process wastewater introduced into a POTW shall not exceed the following values... Maximum for monthly average mg/off-kg (pounds per million off-pounds) of lead-tin-bismuth rolled with...

40 CFR 471.13 - New source performance standards (NSPS).

Code of Federal Regulations, 2013 CFR

2013-07-01

...-Tin-Bismuth Forming Subcategory § 471.13 New source performance standards (NSPS). Any new source... pollutants in the lead-tin-bismuth forming operations' process wastewater shall not exceed the following... Maximum for monthly average mg/off-kg (pounds per million off-pounds) of lead-tin-bismuth rolled with...

40 CFR 471.14 - Pretreatment standards for existing sources (PSES).

Code of Federal Regulations, 2014 CFR

2014-07-01

... CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.14 Pretreatment standards for existing sources (PSES... in lead-tin-bismuth forming process wastewater introduced into a POTW shall not exceed the following... Maximum for monthly average mg/off-kg (pounds per million off-pounds) of lead-tin-bismuth rolled with...

40 CFR 471.13 - New source performance standards (NSPS).

Code of Federal Regulations, 2014 CFR

2014-07-01

...-Tin-Bismuth Forming Subcategory § 471.13 New source performance standards (NSPS). Any new source... pollutants in the lead-tin-bismuth forming operations' process wastewater shall not exceed the following... Maximum for monthly average mg/off-kg (pounds per million off-pounds) of lead-tin-bismuth rolled with...

40 CFR 471.13 - New source performance standards (NSPS).

Code of Federal Regulations, 2012 CFR

2012-07-01

...-Tin-Bismuth Forming Subcategory § 471.13 New source performance standards (NSPS). Any new source... pollutants in the lead-tin-bismuth forming operations' process wastewater shall not exceed the following... Maximum for monthly average mg/off-kg (pounds per million off-pounds) of lead-tin-bismuth rolled with...

40 CFR 471.14 - Pretreatment standards for existing sources (PSES).

Code of Federal Regulations, 2010 CFR

2010-07-01

...-Tin-Bismuth Forming Subcategory § 471.14 Pretreatment standards for existing sources (PSES). Except as...-tin-bismuth forming process wastewater introduced into a POTW shall not exceed the following values... Maximum for monthly average mg/off-kg (pounds per million off-pounds) of lead-tin-bismuth rolled with...

40 CFR 471.14 - Pretreatment standards for existing sources (PSES).

Code of Federal Regulations, 2013 CFR

2013-07-01

... CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.14 Pretreatment standards for existing sources (PSES... in lead-tin-bismuth forming process wastewater introduced into a POTW shall not exceed the following... Maximum for monthly average mg/off-kg (pounds per million off-pounds) of lead-tin-bismuth rolled with...

Myoclonic encephalopathy due to bismuth salts: treatment with dimercaprol and analysis of CSF transmitters.

PubMed

Molina, J A; Calandre, L; Bermejo, F

1989-03-01

Two cases of myoclonic encephalopathy due to bismuth salts intoxication are reported. In both, treatment with dimercaprol led to clinical recovery. This therapy was shown to enhance bismuth clearance. We also present data on the CSF metabolites dopamine, norepinephrine and serotonin of one patient.

PRODUCTION OF PLUTONIUM FLUORIDE FROM BISMUTH PHOSPHATE PRECIPITATE CONTAINING PLUTONIUM VALUES

DOEpatents

Brown, H.S.; Bohlmann, E.G.

1961-05-01

A process is given for separating plutonium from fission products present on a bismuth phosphate carrier. The dried carrier is first treated with hydrogen fluoride at between 500 and 600 deg C whereby some fission product fluorides volatilize away from plutonium tetrafluoride, and nonvolatile fission product fluorides are formed then with anhydrous fluorine at between 400 and 500 deg C. Bismuth and plutonium distill in the form of volatile fluorides away from the nonvolatile fission product fluorides. The bismuth and plutonium fluorides are condensed at below 290 deg C.

Multi-elemental bio-imaging of rat tissue from a study investigating the bioavailability of bismuth from shotgun pellets.

PubMed

Urgast, Dagmar S; Ellingsen, Dag G; Berlinger, Balázs; Eilertsen, Einar; Friisk, Grete; Skaug, Vidar; Thomassen, Yngvar; Beattie, John H; Kwun, In-Sook; Feldmann, Jörg

2012-07-01

In recent years, bismuth has been promoted as a "green element" and is used as a substitute for the toxic lead in ammunition and other applications. However, the bioavailability and toxicity of bismuth is still not very well described. Following a hunting accident with bismuth-containing shots, a bioavailability study of bismuth from metal pellets inoculated into rat limb muscles was carried out. Bismuth could be found in urine and blood of the animals. Bio-imaging using laser ablation ICP-MS of thin sections of the tissue around the metal implant was carried out to find out more about the distribution of the metal diffusing into the tissue. Two laser ablation systems with different ablation cell designs were compared regarding their analytical performance. Low concentrations of bismuth showing a non-symmetrical pattern were detected in the tissue surrounding the metal implant. This was partly an artefact from cutting the thin sections but also bio-mobilisation of the metals of the implant could be seen. An accumulation of zinc around the implant was interpreted as a marker of inflammation. Challenges regarding sample preparation for laser ablation and bio-imaging of samples of diverse composition became apparent during the analysis.

Enhanced detection of quantum dots labeled protein by simultaneous bismuth electrodeposition into microfluidic channel.

PubMed

Medina-Sánchez, Mariana; Miserere, Sandrine; Cadevall, Miquell; Merkoçi, Arben

2016-02-01

In this study, we propose an electrochemical immunoassay into a disposable microfluidic platform, using quantum dots (QDs) as labels and their enhanced detection using bismuth as an alternative to mercury electrodes. CdSe@ZnS QDs were used to tag human IgG as a model protein and detected through highly sensitive stripping voltammetry of the dissolved metallic component (cadmium in our case). The modification of the screen printed carbon electrodes (SPCEs) was done by a simple electrodeposition of bismuth that was previously mixed with the sample containing QDs. A magneto-immunosandwich assay was performed using a micromixer. A magnet placed at its outlet in order to capture the magnetic beads used as solid support for the immunoassay. SPCEs were integrated at the end of the channel as detector. Different parameters such as bismuth concentration, flow rate, and incubation times, were optimized. The LOD for HIgG in presence of bismuth was 3.5 ng/mL with a RSD of 13.2%. This LOD was about 3.3-fold lower than the one obtained without bismuth. Furthermore, the sensitivity of the system was increased 100-fold respect to experiments carried out with classical screen-printed electrodes, both in presence of bismuth. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Viability of Bismuth as a Green Substitute for Lead in Jacketed .357 Magnum Revolver Bullets

NASA Astrophysics Data System (ADS)

Jenkins, Joel

In seeking to develop environmentally friendly lead-free non-toxic bullets, the research ballistically evaluated the performance of copper-jacketed handgun bullets containing a pure bismuth core. The lead was first removed from 140 grain Hornady(TM) XTPRTM bullets of 38 caliber (.357 diameter) by melting. The empty jackets were then refilled with pure bismuth, including the forming of a correctly sized hollow-point cavity. Due to the lower density of bismuth as compared to lead, the bismuth-cored bullets consistently weighed 125 gains. Conveniently this allowed direct comparison to commercially available 125 grain Hornady(TM) XTPRTM lead-cored bullets of 38 caliber. Both bismuth-cored and lead-cored versions of the 125 grain bullets had identical nose dimensions and jacket material, the only dimensional difference being the bullet length below the cannelure. Shooting took place at an outdoor range using a 357 Magnum Ruger(TM) SP101RTM revolver with 3" barrel as the test weapon. FBI protocols were followed when firing through clothing, wallboard, plywood, steel plates and laminated glass. Wound paths and bullets were captured in ballistic gelatin, with data collected for velocity, penetration, expansion, and weight retention. Bismuth compared favorably with lead in all but the laminated glass test, where it under penetrated due to jacket separation.

Magnesium and zinc borate enhance osteoblastic differentiation of stem cells from human exfoliated deciduous teeth in vitro.

PubMed

Liu, Yao-Jen; Su, Wen-Ta; Chen, Po-Hung

2018-01-01

Various biocompatible and biodegradable scaffolds blended with biochemical signal molecules with adequate osteoinductive and osteoconductive properties have attracted significant interest in hard tissue engineering regeneration. We evaluated the distinct effects of magnesium borate, zinc borate, and boric acid blended into chitosan scaffold for osteogenic differentiation of stem cells from exfoliated deciduous teeth. Stem cells from exfoliated deciduous teeth cells are a potential source of functional osteoblasts for applications in bone tissue engineering, but the efficiency of osteoblastic differentiation is low, thereby significantly limiting their clinical applications. Divalent metal borates have potential function in bone remodeling because they can simulate bone formation and decrease bone resorption. These magnesium, zinc, and B ions can gradually be released into the culture medium from the scaffold and induce advanced osteoblastic differentiation from stem cells from exfoliated deciduous teeth. Stem cells from exfoliated deciduous teeth with magnesium borate or zinc borate as inducer demonstrated more osteoblastic differentiation after 21 days of culture. Differentiated cells exhibited activity of alkaline phosphatase, bone-related gene expression of collagen type I, runt-related transcription factor 2, osteopontin, osteocalcin, vascular endothelial growth factor, and angiopoietin-1, as noted via real-time polymerase chain reaction analysis, as well as significant deposits of calcium minerals. Divalent mental magnesium and zinc and nonmetal boron can be an effective inducer of osteogenesis for stem cells from exfoliated deciduous teeth. This experiment might provide useful inducers for osteoblastic differentiation of stem cells from exfoliated deciduous teeth for tissue engineering and bone repair.

Effect of zinc-borate glass addition on the thermal properties of the cordierite/Al2O3 composites containing nano-sized spinel crystal.

PubMed

Jo, Sinae; Kang, Seunggu

2013-11-01

Low-melting zinc-borate glass was added to the cordierite/Al2O3 composite in order to improve the sintering facility of Al2O3 and formation of nano-sized spinel crystal of high thermal conductivity. Increasing the ZnO/B2O3 ratio in the zinc-borate glass increased the ZnAl2O4 spinel and decreased the Al4B2O9 crystal peak intensities in X-ray diffraction pattern. The XRD peak intensities of the ZnAl2O4 spinel and Al4B2O9 crystals in the specimen containing 10 wt% zinc-borate glass (10G series) are higher than that of the specimen containing 5 wt% zinc-borate glass (5G series). The microstructures of most 10G series specimens had the flower-shaped crystal which was composed of 50 nm wide and 250 nm long needle-like crystals and identified as ZnAl2O4 spinel phase. The thermal conductivity of the 10G series specimen was higher than that of the 5G series in any ZnO/B2O3 ratio due to the formation of plenty of nano-sized ZnAl2O4 spinel of high thermal conductivity. Particularly, the thermal conductivity of the cordierite/Al2O3 composite containing 10 wt% zinc-borate glass of ZnO/B2O3 weight ratio = 1.5 was 3.8 W/Km which is much higher than that of the published value (3.0 W/Km).

Hydrothermal synthesis and structural analysis of new mixed oxyanion borates: Ba{sub 11}B{sub 26}O{sub 44}(PO{sub 4}){sub 2}(OH){sub 6}, Li{sub 9}BaB{sub 15}O{sub 27}(CO{sub 3}) and Ba{sub 3}Si{sub 2}B{sub 6}O{sub 16}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Heyward, Carla, E-mail: cheywar@clemson.edu; McMillen, Colin D., E-mail: cmcmill@clemson.edu; Kolis, Joseph, E-mail: kjoseph@clemson.edu

2013-07-15

Several new borate compounds, Ba{sub 11}B{sub 26}O{sub 44}(PO{sub 4}){sub 2}(OH){sub 6} (1), Li{sub 9}BaB{sub 15}O{sub 27}(CO{sub 3}) (2), and Ba{sub 3}Si{sub 2}B{sub 6}O{sub 16} (3) were synthesized containing other hetero-oxyanion building blocks in addition to the borate frameworks. They were all prepared under hydrothermal conditions and characterized by single crystal and powder X-ray diffraction, and IR spectroscopy. Crystal data: For 1; space group P2{sub 1}/c, a=6.8909 (14) Å, b=13.629 (3) Å, c=25.851 (5) Å, β=90.04 (3)°; For 2; space group P-31c, a=8.8599 (13) Å, c=15.148 (3) Å; For 3; space group P-1, a=5.0414 (10) Å, b=7.5602 (15) Å, c=8.5374 (17)more » Å, α=77.15 (3)°, β=77.84 (3)°, γ=87.41 (3)° for 3. Compounds 1 and 2 contain isolated oxyanions [PO{sub 4}]{sup 3−} and [CO{sub 3}]{sup 2−} respectively, sitting in channels created by the borate framework, while structure 3 has the [SiO{sub 4}]{sup 4−} groups directly bonded to the borate groups creating a B–O–Si framework. - Highlights: • Hydrothermal syntheses of three new mixed oxyanion borates are presented. • Ba{sub 11}B{sub 26}O{sub 44}(PO{sub 4}){sub 2}(OH){sub 6} contains isolated [PO{sub 4}]{sup 3−} in voids of the borate framework. • Li{sub 9}BaB{sub 15}O{sub 27}(CO{sub 3}) contains isolated [CO{sub 3}]{sup 2−} in channels created by the framework. • Ba{sub 3}Si{sub 2}B{sub 6}O{sub 16} has direct bonding of [SiO{sub 4}]{sup 4−} and borates creating a B–O–Si framework.« less

Corneal epithelial cell biocompatibility to silicone hydrogel and conventional hydrogel contact lens packaging solutions

PubMed Central

Tanti, N.C.; Jones, L.; Sheardown, H.

2010-01-01

Purpose Although all contact lenses (CLs) are applied initially to the eye directly from a packaging solution, little is known about the effects of these solutions on human corneal epithelial cells (HCECs). Due to the porous nature of CL materials, they have the potential to sorb components of the packaging solution during storage, which could then be subsequently released upon insertion of the CL on the eye. The purpose of this study was to investigate the effect of various packaging solutions on HCECs, using an in vitro model. Methods An in vitro assay was developed whereby various silicone hydrogels and conventional, poly-2-hydroxyethylmethacrylate  (polyHEMA)-based lens materials were removed directly from their packaging and then incubated for up to 24 h with HCECs. The effect of the retained and released packaging solution components on HCECs was assessed by measuring cell viability, adhesion phenotype, and apoptosis. Results Incubation of HCECs with CLs stored in borate-buffered packaging solutions resulted in a significant reduction in cell viability. Adherent cells incubated with these CLs also exhibited reduced levels of β1 and α3 integrin. Soaking borate-buffered packaged CLs in PBS before cell incubation resolved viability and integrin expression in all cases, with the exception of galyfilcon A and balafilcon A, from which a 20% reduction in cell viability was still observed. In comparison, CLs stored in phosphate-buffered packaging solutions had cellular viability and expression of integrins similar to control cells (cells incubated in the absence of a lens). When incubated with cells at a 10% concentration in serum-free medium, borate-buffered packaging solutions and borate-containing saline (Unisol 4) significantly reduced cell viability and integrin expression. Neither caspase activation nor annexin V binding was observed on cells following exposure to borate buffer solution. However, a significant decrease in reactive oxygen species was observed at 24 h. These latter results suggest that in vitro exposure to low concentration of borate/boric acid results in cell dysfunction, leading to necrosis rather than apoptosis. Conclusions Borate-buffered packaging solutions were shown to adversely affect the viability and integrin expression of HCECs in vitro. When used in ophthalmic packaging solutions, the antimicrobial properties of borate buffer may be outweighed by its relatively cytotoxic effects on cells. PMID:20169012

Corneal epithelial cell biocompatibility to silicone hydrogel and conventional hydrogel contact lens packaging solutions.

PubMed

Gorbet, M B; Tanti, N C; Jones, L; Sheardown, H

2010-02-19

Although all contact lenses (CLs) are applied initially to the eye directly from a packaging solution, little is known about the effects of these solutions on human corneal epithelial cells (HCECs). Due to the porous nature of CL materials, they have the potential to sorb components of the packaging solution during storage, which could then be subsequently released upon insertion of the CL on the eye. The purpose of this study was to investigate the effect of various packaging solutions on HCECs, using an in vitro model. An in vitro assay was developed whereby various silicone hydrogels and conventional, poly-2-hydroxyethylmethacrylate (polyHEMA)-based lens materials were removed directly from their packaging and then incubated for up to 24 h with HCECs. The effect of the retained and released packaging solution components on HCECs was assessed by measuring cell viability, adhesion phenotype, and apoptosis. Incubation of HCECs with CLs stored in borate-buffered packaging solutions resulted in a significant reduction in cell viability. Adherent cells incubated with these CLs also exhibited reduced levels of beta(1) and alpha(3) integrin. Soaking borate-buffered packaged CLs in PBS before cell incubation resolved viability and integrin expression in all cases, with the exception of galyfilcon A and balafilcon A, from which a 20% reduction in cell viability was still observed. In comparison, CLs stored in phosphate-buffered packaging solutions had cellular viability and expression of integrins similar to control cells (cells incubated in the absence of a lens). When incubated with cells at a 10% concentration in serum-free medium, borate-buffered packaging solutions and borate-containing saline (Unisol 4) significantly reduced cell viability and integrin expression. Neither caspase activation nor annexin V binding was observed on cells following exposure to borate buffer solution. However, a significant decrease in reactive oxygen species was observed at 24 h. These latter results suggest that in vitro exposure to low concentration of borate/boric acid results in cell dysfunction, leading to necrosis rather than apoptosis. Borate-buffered packaging solutions were shown to adversely affect the viability and integrin expression of HCECs in vitro. When used in ophthalmic packaging solutions, the antimicrobial properties of borate buffer may be outweighed by its relatively cytotoxic effects on cells.

[Geochemical distribution of dissolved bismuth in the Yellow Sea and East China Sea].

PubMed

Wu, Xiao-Dan; Song, Jin-Ming; Wu, Bin; Li, Xue-Gang

2014-01-01

Occurrence level, geochemical distribution of dissolved bismuth and its coupling relationship to eco-environment were investigated in the Yellow Sea and East China Sea to explore the source and influencing factors. The results showed that the concentration of dissolved bismuth was within the range of 0-0. 029 microg x L(-1) at the surface and 0.001-0.189 microg x L(-1) at the bottom, with the averages of 0.008 and 0.016 microg x L(-1), respectively. Horizontally, low value of dissolved bismuth exhibited the bidirectional extension feature, indicating that it could trace the path of Changjiang Diluted Water. High value of dissolved bismuth was observed where the Subei Costal Current and Yellow Sea Warm Current flowed and the Changjiang Diluted Water and Zhejiang-Fujian Coastal Current met, suggesting that it was controlled by the cycle of current system. Vertically, the coastal water was fully mixed by water convection and eddy mixing, and was divided from the stratified water by strong tidal front, which blocked the transport of dissolved bismuth to the open sea. Thus, the concentration in front area was significantly higher than that in the open sea. Diurnal variation of dissolved bismuth was related to the hydrodynamic conditions (tide, suspension and thermocline) instead of the environmental factors (temperature and salinity). Positive relationship to SPM (suspended particulate matter) clarified that bismuth was prone to release from solid phase to liquid phase. Furthermore, conditions with temperature ranging 22-27 degrees C, salinity ranging 28-31 and pH ranging 7.9-8.1 were shown to be optimal for the release process.

40 CFR 471.15 - Pretreatment standards for new sources (PSNS).

Code of Federal Regulations, 2013 CFR

2013-07-01

... CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.15 Pretreatment standards for new sources (PSNS... pretreatment standards for new sources. The mass of wastewater pollutants in lead-tin-bismuth forming process... (pounds per million off-pounds) of lead-tin-bismuth rolled with emulsions Antimony 0.067 0.030 Lead 0.010...

40 CFR 471.15 - Pretreatment standards for new sources (PSNS).

Code of Federal Regulations, 2014 CFR

2014-07-01

... CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.15 Pretreatment standards for new sources (PSNS... pretreatment standards for new sources. The mass of wastewater pollutants in lead-tin-bismuth forming process... (pounds per million off-pounds) of lead-tin-bismuth rolled with emulsions Antimony 0.067 0.030 Lead 0.010...

40 CFR 471.15 - Pretreatment standards for new sources (PSNS).

Code of Federal Regulations, 2010 CFR

2010-07-01

...-Tin-Bismuth Forming Subcategory § 471.15 Pretreatment standards for new sources (PSNS). Except as... standards for new sources. The mass of wastewater pollutants in lead-tin-bismuth forming process wastewater... million off-pounds) of lead-tin-bismuth rolled with emulsions Antimony 0.067 0.030 Lead 0.010 0.005 (b...

40 CFR 471.15 - Pretreatment standards for new sources (PSNS).

Code of Federal Regulations, 2012 CFR

2012-07-01

... CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.15 Pretreatment standards for new sources (PSNS... pretreatment standards for new sources. The mass of wastewater pollutants in lead-tin-bismuth forming process... (pounds per million off-pounds) of lead-tin-bismuth rolled with emulsions Antimony 0.067 0.030 Lead 0.010...

40 CFR 471.15 - Pretreatment standards for new sources (PSNS).

Code of Federal Regulations, 2011 CFR

2011-07-01

...-Tin-Bismuth Forming Subcategory § 471.15 Pretreatment standards for new sources (PSNS). Except as... standards for new sources. The mass of wastewater pollutants in lead-tin-bismuth forming process wastewater... million off-pounds) of lead-tin-bismuth rolled with emulsions Antimony 0.067 0.030 Lead 0.010 0.005 (b...

75 FR 14491 - Listing of Color Additives Exempt From Certification; Bismuth Citrate

Federal Register 2010, 2011, 2012, 2013, 2014

2010-03-26

... DEPARTMENT OF HEALTH AND HUMAN SERVICES Food and Drug Administration 21 CFR Part 73 [Docket No. FDA-2008-C-0098] Listing of Color Additives Exempt From Certification; Bismuth Citrate AGENCY: Food... amending the color additive regulations to increase the permitted use level of bismuth citrate as a color...

Method of Creating Micro-scale Silver Telluride Grains Covered with Bismuth Nanoparticles

NASA Technical Reports Server (NTRS)

Park, Yeonjoon (Inventor); Lee, Kunik (Inventor); Kim, Hyun-Jung (Inventor); Choi, Sang Hyouk (Inventor); King, Glen C. (Inventor)

2014-01-01

Provided is a method of enhancing thermoelectric performance by surrounding crystalline semiconductors with nanoparticles by contacting a bismuth telluride material with a silver salt under a substantially inert atmosphere and a temperature approximately near the silver salt decomposition temperature; and recovering a metallic bismuth decorated material comprising silver telluride crystal grains.

The cytotoxicity of organobismuth compounds with certain molecular structures can be diminished by replacing the bismuth atom with an antimony atom in the molecules.

PubMed

Kohri, Kumiko; Yoshida, Eiko; Yasuike, Shuji; Fujie, Tomoya; Yamamoto, Chika; Kaji, Toshiyuki

2015-06-01

Organic-inorganic hybrid molecules, which are composed of an organic structure and metal(s), are indispensable for synthetic chemical reactions; however, their toxicity has been incompletely understood. In the present study, we discovered two cytotoxic organobismuth compounds whose cytotoxicity diminished upon replacement of the intramolecular bismuth atom with an antimony atom. The intracellular accumulation of the organobismuth compounds was much higher than that of the organoantimony compounds with the corresponding organic structures. We also showed that both the organic structure and bismuth atom are required for certain organobismuth compounds to exert their cytotoxic effect, suggesting that the cytotoxicity of such a compound is a result of an interaction between the organic structure and the bismuth atom. The present data suggest that organobismuth compounds with certain molecular structures exhibit cytotoxicity via an interaction between the molecular structure and the bismuth atom, and this cytotoxicity can be diminished by replacing the bismuth atom with an antimony atom, resulting in lower intracellular accumulation.

Passive safety injection system using borated water

DOEpatents

Conway, Lawrence E.; Schulz, Terry L.

1993-01-01

A passive safety injection system relies on differences in water density to induce natural circulatory flow patterns which help maintain prescribed concentrations of boric acid in borated water, and prevents boron from accumulating in the reactor vessel and possibly preventing heat transfer.

Boric Acid Corrosion of Concrete Rebar

NASA Astrophysics Data System (ADS)

Pabalan, R. T.; Yang, L.; Chiang, K.–T.

2013-07-01

Borated water leakage through spent fuel pools (SFPs) at pressurized water reactors is a concern because it could cause corrosion of reinforcement steel in the concrete structure and compromise the integrity of the structure. Because corrosion rate of carbon steel in concrete in the presence of boric acid is lacking in published literature and available data are equivocal on the effect of boric acid on rebar corrosion, corrosion rate measurements were conducted in this study using several test methods. Rebar corrosion rates were measured in (i) borated water flowing in a simulated concrete crack, (ii) borated water flowing over a concrete surface, (iii) borated water that has reacted with concrete, and (iv) 2,400 ppm boric acid solutions with pH adjusted to a range of 6.0 to 7.7. The corrosion rates were measured using coupled multielectrode array sensor (CMAS) and linear polarization resistance (LPR) probes, both made using carbon steel. The results indicate that rebar corrosion rates are low (~1 μm/yr or less)when the solution pH is ~7.1 or higher. Below pH ~7.1, the corrosion rate increases with decreasing pH and can reach ~100 μm/yr in solutions with pH less than ~6.7. The threshold pH for carbon steel corrosion in borated solution is between 6.8 and 7.3.

Geochemical characteristics of Kırka (Sarıkaya) borate deposit, northwestern Anatolia, Turkey

NASA Astrophysics Data System (ADS)

Koçak, İ.; Koç, Ş.

2016-02-01

The Kırka borate deposit was deposited in a Miocene lacustrine basin which is closely associated with volcanic activity which lasted from Paleogene to the beginning of Quaternary. Borate mineralization alternates with claystone, mudstone, tuff and fine-layered limestone and mostly shows a lenticular structure. The mineral paragenesis is composed of borax, tincalconite, ulexite, kurnakovite, probertite, tunellite, colemanite, dolomite, smectite group minerals, illite and some firstly reported minerals for the Kırka deposit including hydrochloroborite, brianroulstonite, hilgardite-4M and searlesite minerals. In comparison to average values of earth crust, concentrations of Cs, Sr, Li, As and Se were significantly enriched with respective rates of 21, 15, 14, 3 and 188 folds. Regarding KY, KS1 and KS2 locations, there are differences in both element abundances and their geochemical tendencies which are attributed to variations in discharge regime and physico-chemical conditions of the depositional environment. Independent behaviour of B2O3 might indicate that boron is not associated with clays and carbonates and, therefore, most part of boron must be derived from volcanic activity (hydrothermal solutions, gases). REE data indicate that the Kırka borate deposit was formed in a sedimentary environment where highly alkaline (high pH) hydrothermal solutions also took part in borate precipitation process.

Treatment of cells with alkaline borate buffer extends the capability of interphase FISH mapping.

PubMed

Yokota, H; van den Engh, G; Mostert, M; Trask, B J

1995-01-20

Interphase fluorescence in situ hybridization (FISH) has been shown to be a means to map DNA sequences relative to each other in the 100 kb to 1-2 Mb genomic-separation range. At distances below 0.1 Mb, probe sites are infrequently resolved in interphase chromatin. In the 0.1- to 1-Mb range, interphase chromatin can be modeled as a freely flexible chain. The mean square interphase distance between two probes is proportional to the genomic separation between the probes on the linear DNA molecule. Above 1-2 Mb, the relationship between interphase distance and genomic separation changes abruptly and appears to level off. We have used alkaline-borate treatment to expand the capability of interphase FISH mapping. We show here that alkaline-borate treatment increases nuclear diameter, the interphase distance between probes on homologous chromosomes, and the distance between probes on the same chromosome. We also show that the mean square distance between hybridization sites in borate-treated nuclei is proportional to genomic separation up to 4 Mb. Thus, alkaline-borate treatment enhances the capability of interphase FISH mapping by increasing the absolute distance between probes and extending the range of the simple relationship between interphase distance and genomic separation.

Treatment of cells with alkaline borate buffer extends the capability of interphase FISH mapping

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yokota, H.; Van Den Engh, G.; Mostert, M.

1995-01-20

Interphase fluorescence in situ hybridization (FISH) has been shown to be a means to map DNA sequences relative to each other in the 100 kb to 1-2 Mb genomic-separation range. At distances below 0.1 Mb, probe sites are infrequently resolved in interphase chromatin. In the 0.1- to 1-Mb range, interphase chromatin can be modeled as a freely flexible chain. The mean square interphase distance between two probes is proportional to the genomic separation between the probes on the linear DNA molecule. Above 1-2 Mb, the relationship between interphase distance and genomic separation changes abruptly and appears to level off. Wemore » have used alkaline-borate treatment to expand the capability of interphase FISH mapping. We show here that alkaline-borate treatment increases nuclear diameter, the interphase distance between probes on homologous chromosomes, and the distance between probes on the same chromosome. We also show that the mean square distance between hybridization sites in borate-treated nuclei is proportional to genomic separation up to 4 Mb. Thus, alkaline-borate treatment enhances the capability of interphase FISH mapping by increasing the absolute distance between probes and extending the range of the simple relationship between interphase distance and genomic separation. 31 refs., 5 figs.« less

A novel injectable borate bioactive glass cement for local delivery of vancomycin to cure osteomyelitis and regenerate bone.

PubMed

Cui, Xu; Zhao, Cunju; Gu, Yifei; Li, Le; Wang, Hui; Huang, Wenhai; Zhou, Nai; Wang, Deping; Zhu, Yi; Xu, Jun; Luo, Shihua; Zhang, Changqing; Rahaman, Mohamed N

2014-03-01

Osteomyelitis (bone infection) is often difficult to cure. The commonly-used treatment of surgical debridement to remove the infected bone combined with prolonged systemic and local antibiotic treatment has limitations. In the present study, an injectable borate bioactive glass cement was developed as a carrier for the antibiotic vancomycin, characterized in vitro, and evaluated for its capacity to cure osteomyelitis in a rabbit tibial model. The cement (initial setting time = 5.8 ± 0.6 min; compressive strength = 25.6 ± 0.3 MPa) released vancomycin over ~25 days in phosphate-buffered saline, during which time the borate glass converted to hydroxyapatite (HA). When implanted in rabbit tibial defects infected with methicillin-resistant Staphylococcus aureus (MRSA)-induced osteomyelitis, the vancomycin-loaded cement converted to HA and supported new bone formation in the defects within 8 weeks. Osteomyelitis was cured in 87 % of the defects implanted with the vancomycin-loaded borate glass cement, compared to 71 % for the defects implanted with vancomycin-loaded calcium sulfate cement. The injectable borate bioactive glass cement developed in this study is a promising treatment for curing osteomyelitis and for regenerating bone in the defects following cure of the infection.

In vitro bioactivity, cytocompatibility, and antibiotic release profile of gentamicin sulfate-loaded borate bioactive glass/chitosan composites.

PubMed

Cui, Xu; Gu, Yifei; Li, Le; Wang, Hui; Xie, Zhongping; Luo, Shihua; Zhou, Nai; Huang, Wenhai; Rahaman, Mohamed N

2013-10-01

Borate bioactive glass-based composites have been attracting interest recently as an osteoconductive carrier material for local antibiotic delivery. In the present study, composites composed of borate bioactive glass particles bonded with a chitosan matrix were prepared and evaluated in vitro as a carrier for gentamicin sulfate. The bioactivity, degradation, drug release profile, and compressive strength of the composite carrier system were studied as a function of immersion time in phosphate-buffered saline at 37 °C. The cytocompatibility of the gentamicin sulfate-loaded composite carrier was evaluated using assays of cell proliferation and alkaline phosphatase activity of osteogenic MC3T3-E1 cells. Sustained release of gentamicin sulfate occurred over ~28 days in PBS, while the bioactive glass converted continuously to hydroxyapatite. The compressive strength of the composite loaded with gentamicin sulfate decreased from the as-fabricated value of 24 ± 3 MPa to ~8 MPa after immersion for 14 days in PBS. Extracts of the soluble ionic products of the borate glass/chitosan composites enhanced the proliferation and alkaline phosphatase activity of MC3T3-E1 cells. These results indicate that the gentamicin sulfate-loaded composite composed of chitosan-bonded borate bioactive glass particles could be useful clinically as an osteoconductive carrier material for treating bone infection.

Synthesis and study on the luminescence properties of cadmium borate phosphors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Annalakshmi, O.; Jose, M.T., E-mail: mtjosein@yahoo.co.in; Venkatraman, B.

2014-02-01

Highlights: • Cadmium borate synthesized by solid state sintering technique. • Neutron sensitivity of the material ten times that of TLD-600. • Gamma sensitivity is found to be twice that of TLD-100. • Gamma response is linear from 0.1 to 10{sup 3} mGy. - Abstract: Cadmium borate compound prepared through wet chemical reaction from the starting chemicals followed by high temperature solid state synthesis below the melting point to get the final TL phosphor powder. Phase purity and bond details of cadmium borate crystals are characterized using X-ray diffraction technique and infrared spectroscopy. Feasibility of these materials for radiation dosimetrymore » applications was studied after gamma and neutron irradiation. Gamma irradiation of undoped phosphors show a single peak around 185 °C whereas doping with gadolinium and silver, new more intense peak observed at 290 °C. Irradiation to thermal neutrons revealed single peak around 170 °C for all the phosphors. TL emission spectra and photoluminescence (PL) studies were also carried out on the phosphors. These borate materials are found to be highly sensitive to neutrons and hence can be used for neutron detection. Neutron sensitivity of the material is about ten times that of TLD-600.« less

Helicobacter pylori second-line rescue therapy with levofloxacin- and bismuth-containing quadruple therapy, after failure of standard triple or non-bismuth quadruple treatments.

PubMed

Gisbert, J P; Romano, M; Gravina, A G; Solís-Muñoz, P; Bermejo, F; Molina-Infante, J; Castro-Fernández, M; Ortuño, J; Lucendo, A J; Herranz, M; Modolell, I; Del Castillo, F; Gómez, J; Barrio, J; Velayos, B; Gómez, B; Domínguez, J L; Miranda, A; Martorano, M; Algaba, A; Pabón, M; Angueira, T; Fernández-Salazar, L; Federico, A; Marín, A C; McNicholl, A G

2015-04-01

The most commonly used second-line Helicobacter pylori eradication regimens are bismuth-containing quadruple therapy and levofloxacin-containing triple therapy, both offering suboptimal results. Combining bismuth and levofloxacin may enhance the efficacy of rescue eradication regimens. To evaluate the efficacy and tolerability of a second-line quadruple regimen containing levofloxacin and bismuth in patients whose previous H. pylori eradication treatment failed. This was a prospective multicenter study including patients in whom a standard triple therapy (PPI-clarithromycin-amoxicillin) or a non-bismuth quadruple therapy (PPI-clarithromycin-amoxicillin-metronidazole, either sequential or concomitant) had failed. Esomeprazole (40 mg b.d.), amoxicillin (1 g b.d.), levofloxacin (500 mg o.d.) and bismuth (240 mg b.d.) was prescribed for 14 days. Eradication was confirmed by (13) C-urea breath test. Compliance was determined through questioning and recovery of empty medication envelopes. Incidence of adverse effects was evaluated by questionnaires. 200 patients were included consecutively (mean age 47 years, 67% women, 13% ulcer). Previous failed therapy included: standard clarithromycin triple therapy (131 patients), sequential (32) and concomitant (37). A total of 96% took all medications correctly. Per-protocol and intention-to-treat eradication rates were 91.1% (95%CI = 87-95%) and 90% (95%CI = 86-94%). Cure rates were similar regardless of previous (failed) treatment or country of origin. Adverse effects were reported in 46% of patients, most commonly nausea (17%) and diarrhoea (16%); 3% were intense but none was serious. Fourteen-day bismuth- and levofloxacin-containing quadruple therapy is an effective (≥90% cure rate), simple and safe second-line strategy in patients whose previous standard triple or non-bismuth quadruple (sequential or concomitant) therapies have failed. © 2015 John Wiley & Sons Ltd.

Effect of absorption recovery in bismuth-doped silica glass at 1450 nm on soliton grouping in fiber laser

PubMed Central

Gumenyuk, R.; Melkumov, M. A.; Khopin, V. F.; Dianov, E. M.; Okhotnikov, O. G.

2014-01-01

Saturable absorption in bismuth-doped glasses was found to have a noticeable influence on soliton interaction and group formation. This phenomenon, observed in 1450 nm mode-locked bismuth-doped fiber laser, shows the distinct feature of the multiple pulse regime, which appears as a stationary pulse group whose length can be spread over the whole cavity length by variation of the pump power and polarization. Pulse positioning within the ensemble depends on the saturation fluence and the relatively fast recovery dynamics of bismuth fiber. PMID:25391808

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jena, Puru; Kandalam, Anil K.; Christian, Theresa M.

Gallium phosphide bismide (GaP1-xBix) epilayers with bismuth fractions from 0.9% to 3.2%, as calculated from lattice parameter measurements, were studied with Rutherford backscattering spectrometry (RBS) to directly measure bismuth incorporation. The total bismuth fractions found by RBS were higher than expected from the lattice parameter calculations. Furthermore, in one analyzed sample grown by molecular beam epitaxy at 300 degrees C, 55% of incorporated bismuth was found to occupy interstitial sites. We discuss implications of this high interstitial incorporation fraction and its possible relationship to x-ray diffraction and photoluminescence measurements of GaP0.99Bi0.01.

Study of the structure, dielectric and ferroelectric behavior of BaBi{sub 4+δ}Ti{sub 4}O{sub 15} ceramics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Khokhar, Anita, E-mail: mails4anita@gmail.com, E-mail: goyalphy@gmail.com; Goyal, Parveen K., E-mail: mails4anita@gmail.com, E-mail: goyalphy@gmail.com; Sreenivas, K.

2016-05-23

The structure and ferroelectric properties of excess bismuth doped barium bismuth titanate BaBi{sub 4+δ}Ti{sub 4}O{sub 15} (δ = 2 - 10 wt.%)) ceramics prepared by solid-state reaction method have been investigated. X-ray diffraction (XRD) confirms the formation of a single phase material with a change in the orthorhombic distortion with varying excess of bismuth content. There is no change in the phase transition temperature (T{sub m}) while the relaxor behaviour has been modified significantly with excess of bismuth doping. Saturated hysteresis loops with high remnant polarization (P{sub r} ~ 12.5  µC/cm{sup 2}), low coercive fields (E{sub c} ~ 26 kV/cm) aremore » measured and a high piezoelectric coefficient (d{sub 33} ~ 29 pC/N) is achieved in poled BaBi{sub 4}Ti{sub 4}O{sub 15} ceramics prepared with up to 8 wt.% of excess bismuth oxide. The improvement in the ferroelectric properties with increase in the excess bismuth content in BaBi{sub 4}Ti{sub 4}O{sub 15} ceramics has been explained in terms of changing oxygen vacancy concentration and structural relaxation. Tunable ferroelectric materials can be obtained by manipulating the doping amount of excess bismuth.« less

The efficacy of ranitidine bismuth citrate, amoxicillin and doxycycline or tetracycline regimens as a first line treatment for Helicobacter pylori eradication.

PubMed

Akyildiz, Murat; Akay, Sinan; Musoglu, Ahmet; Tuncyurek, Muge; Aydin, Ahmet

2009-01-01

The eradication rates of Helicobacter pylori (H. pylori) clearly decreased with standard PPI-based triple therapies. To assess the efficacy of two different triple therapies consisting of ranitidine bismuth citrate-amoxicillin-doxycycline and ranitidine bismuth citrate-amoxicillin-tetracycline combinations as a first line treatment option. One hundred and fifteen consecutive dyspeptic patients in whom H. pylori infection was diagnosed for the first time were enrolled in this study. The patients were randomized into two groups. Group 1 (n=57) was assigned to receive a 14-day triple therapy consisting of ranitidine bismuth citrate 400 mg (b.i.d.), amoxicillin 1 g (b.i.d) and doxycycline 100 mg (b.i.d.). Group 2 (n=58) was assigned to receive a 14-day triple therapy consisting of ranitidine bismuth citrate 400 mg (b.i.d.), amoxicillin 1 g (b.i.d.) and tetracycline 500 mg (q.i.d.). The eradication was achieved in 45.7% (21/46) and 40.8% (20/49) of the patients in group 1 and group 2, according to per protocol analysis. The intention-to-treat eradication rates were 36.8% (21/57) and 34.5% (20/58) in group 1 and group 2, respectively. Two-week therapy with neither ranitidine bismuth citrate-amoxicillin-doxycycline nor ranitidine bismuth citrate-amoxicillin-tetracycline is adequately effective for H. pylori eradication as a first line therapy.

Investigation of radiological properties of some shielding materials on charged and uncharged radiation interaction for neutron generator

NASA Astrophysics Data System (ADS)

Büyükyıldız, Mehmet

2017-04-01

Radiation interaction parameters such as total stopping power, projected range (longitudinal and lateral) straggling, mass attenuation coefficient, effective atomic number (Zeff) and electron density (Neff) of some shielding materials were investigated for photon and heavy charged particle interactions. The ranges, stragglings and mass attenuation coefficients were calculated for the high-density polyethylene(HDPE), borated polyethylene (BPE), brick (common silica), concrete (regular), wood, water, stainless steel (304), aluminum (alloy 6061-O), lead and bismuth using SRIM Monte Carlo software and WinXCom program. In addition, effective atomic numbers (Zeff) and electron densities (Neff) of HDPE, BPE, brick (common silica), concrete (regular), wood, water, stainless steel (304) and aluminum (alloy 6061-O) were calculated in the energy region 10 keV-100 MeV using mass stopping powers and mass attenuation coefficients. Two different methods namely direct and interpolation procedures were used to calculate Zeff for comparison and significant differences were determined between the methods. Variations of the ranges, longitudinal and lateral stragglings of water, concrete and stainless steel (304) were compared with each other in the continuous kinetic energy region and discussed with respect to their Zeffs. Moreover, energy absorption buildup factors (EABF) and exposure buildup factors (EBF) of the materials were determined for gamma rays as well and were compared with each other for different photon energies and different mfps in the photon energy region 0.015-15 MeV.

Optical and Physical Investigations of Lanthanum Bismuth Borate glasses doped with Ho2O3

NASA Astrophysics Data System (ADS)

Ramesh, P.; Jagannath, G.; Eraiah, B.; Kokila, M. K.

2018-02-01

Holmium doped 10La2O3-15Bi2O3-(75-x) B2O3 (Ho3+: LBB) glasses have been prepared by melt quench technique and the impact of holmium ions concentration on optical and physical properties of present glasses have been examined. Ho3+ dependent density, molar volume, refractive index, rare earth ion concentration, polaron radius, inter ionic distance, field strength and energy band gap are calculated and tabulated. Amorphous nature of the all glasses has been confirmed by XRD patterns. The room temperature (RT) Uv-Vis absorption spectrum doped with 1 mol% of Ho2O3 exhibit eight prominent bands centred at 895, 641, 537, 486, 472, 467, 451 and 416 due to transition between ground state to various excited states. The results show that, the density is increases and molar volume of the glasses is decreases with an increase in Ho2O3 concentration and consequently generate more non-bridging oxygen (NBOs) in the glass matrix. The Urbach energy is increases with holmium concentration which exemplifies the degree of disorder present in the LBB glasses. The considerable increase in field strength observed in present glasses is attributed to occurrence of strong bridge between Ho3+ and B- ions and this strong bridge is possibly due to the displacement between Ho3+ and oxygen atoms which are generated from the conversion BO3-BO4 units.

Crystal growth, crystal structure of new polymorphic modification, β-Bi 2B 8O 15 and thermal expansion of α-Bi 2B 8O 15

NASA Astrophysics Data System (ADS)

Bubnova, R. S.; Alexandrova, J. V.; Krivovichev, S. V.; Filatov, S. K.; Egorysheva, A. V.

2010-02-01

Single crystals of α- and β-polymorphs of Bi 2B 8O 15 were grown by Czochralski method from a charge of the stoichiometric composition. The crystal structure of β-Bi 2B 8O 15 was solved by direct methods from a twinned crystal and refined to R1=0.081 (w R=0.198) on the basis of 1584 unique observed reflections ( I>2 σ( I)). The compound is triclinic, space group P1¯, a=4.3159(8), b=6. 4604(12), c=22.485(4) Å, α=87.094(15)°, β=86.538(15)°, γ=74.420(14)°, V=602.40(19) Å 3, Z=2. The B-O layered anion of β-Bi 2B 8O 15 is topologically identical to the anion of α-Bi 2B 8O 15 but the orientation of neighboring layers is different. Thermal expansion of α-Bi 2B 8O 15 has been investigated by X-ray powder diffraction in air in temperature range from 20 to 700 °C. It is strongly anisotropic, which can be explained by the hinge mechanism applied to chains of Bi-O polyhedra. While the anisotropy of thermal expansion is rather high, the volume thermal expansion coefficient α V=40×10 6 °C -1 for α-Bi 2B 8O 15 is close to those of other bismuth borates.

Influence of CuO content on the structure of lithium fluoroborate glasses: Spectral and gamma irradiation studies.

PubMed

Abdelghany, A M; ElBatal, H A; EzzElDin, F M

2015-10-05

Glasses of lithium fluoroborate of the composition LiF 15%-B2O3 85% with increasing CuO as added dopant were prepared and characterized by combined optical and FTIR spectroscopy before and after gamma irradiation. The optical spectrum of the undoped glass reveals strong UV absorption with two distinct peaks at about 235 and 310 nm and with no visible bands. This strong UV absorption is related to the presence of unavoidable trace iron impurity (Fe(3+)) within the materials used for the preparation of this glass. After irradiation, the spectrum of the undoped glass shows a decrease of the intensity of the UV bands together with the resolution of an induced visible broad band centered at about 520 nm. The CuO doped glasses reveal the same UV absorption beside a very broad visible band centered at 780 nm and this band shows extension and splitting to several component peaks with higher CuO contents. Upon gamma irradiation, the spectra of all CuO-doped glasses reveal pronounced decrease of their intensities. The response of irradiation on the studied glasses is correlated with suggested photochemical reactions together with some shielding effect of the copper ions. The observed visible band is related to the presence of copper as distorted octahedral Cu(2+) ions. Infrared absorption spectra of the prepared glasses show repetitive characteristic triangular and tetrahedral borate units similar to that published from alkali or alkaline earth oxides B2O3 glasses. A suggested formation of (BO3/2F) tetrahedral units is advanced through action of LiF on B2O3 and these suggested units showing the same position and number as BO4 tetrahedra. Copyright © 2015 Elsevier B.V. All rights reserved.

Unusual stoichiometry control in the atomic layer deposition of manganese borate films from manganese bis(tris(pyrazolyl)borate) and ozone

DOE Office of Scientific and Technical Information (OSTI.GOV)

Klesko, Joseph P.; Bellow, James A.; Saly, Mark J.

The atomic layer deposition (ALD) of films with the approximate compositions Mn{sub 3}(BO{sub 3}){sub 2} and CoB{sub 2}O{sub 4} is described using MnTp{sub 2} or CoTp{sub 2} [Tp = tris(pyrazolyl)borate] with ozone. The solid state decomposition temperatures of MnTp{sub 2} and CoTp{sub 2} are ∼370 and ∼340 °C, respectively. Preparative-scale sublimations of MnTp{sub 2} and CoTp{sub 2} at 210 °C/0.05 Torr afforded >99% recoveries with <0.1% nonvolatile residues. Self-limited ALD growth was demonstrated at 325 °C for MnTp{sub 2} or CoTp{sub 2} with ozone as the coreactant. The growth rate for the manganese borate process was 0.19 Å/cycle within the ALD window of 300–350 °C. The growth ratemore » for the cobalt borate process was 0.39–0.42 Å/cycle at 325 °C. X-ray diffraction of the as-deposited films indicated that they were amorphous. Atomic force microscopy of 35–36 nm thick manganese borate films grown within the 300–350 °C ALD window showed root mean square surface roughnesses of 0.4–0.6 nm. Film stoichiometries were assessed by x-ray photoelectron spectroscopy and time of flight-elastic recoil detection analysis. The differing film stoichiometries obtained from the very similar precursors MnTp{sub 2} and CoTp{sub 2} are proposed to arise from the oxidizing ability of the intermediate high valent manganese oxide layers and lack thereof for cobalt.« less

Optical absorption and photoluminescence properties of Er3+ doped mixed alkali borate glasses.

PubMed

Ratnakaram, Y C; Kumar, A Vijaya; Naidu, D Tirupathi; Rao, J L

2005-07-01

An investigations of the optical absorption and fluorescence spectra of 0.2 mol% Er2O3 in mixed alkali borate glasses of the type 67.8B2O3 x xLi2O(32-x)Na2O, 67.8B2O3 x xLi2O(32-x)K2O and 67.8B2O3 x xNa2O(32-x)K2O (where x = 8, 12, 16, 20 and 24) are presented. The glasses were obtained by quenching melts consisting of H3BO3, Li2CO3, Na2CO3, K2CO3 and Er2O3 (950-1100 degrees C, 1.5-2 h) between two brass plates. Spectroscopic parameters like Racah (E1, E2 and E3), spin-orbit (xi(4f)) and configuration interaction (alpha) parameters are deduced as function of x. Using Judd-Ofelt theory, Judd-Ofelt intensity parameters (omega2, omega4 and omega6) are obtained. Radiative and non-radiative transition rates (A(T) and W(MPR)), radiative lifetimes (tauR), branching ratios (beta) and integrated absorption cross-sections (sigma) have been computed for certain excited states of Er3+ in these mixed alkali borate glasses. Emission spectra have been studied for all the three Er3+ doped mixed alkali borate glasses. The present paper throws light on the trends observed in the intensity parameters, radiative lifetimes, branching ratios and emission cross-sections as a function of x in these borate glasses, keeping in view the effect of mixed alkalies in borate glasses.

Synthesis of cross-linked chitosan modified with the glycine moiety for the collection/concentration of bismuth in aquatic samples for ICP-MS determination.

PubMed

Oshita, Koji; Noguchi, Osamu; Oshima, Mitsuko; Motomizu, Shoji

2007-10-01

A chelating resin, cross-linked chitosan modified with the glycine moiety (glycine-type chitosan resin), was developed for the collection and concentration of bismuth in aquatic samples for ICP-MS measurements. The adsorption behavior of bismuth and 55 elements on glycine-type chitosan resin was systematically examined by passing a sample solution containing 56 elements through a mini-column packed with the resin (wet volume; 1 ml). After eluting the elements adsorbed on the resin with nitric acid, the eluates were measured by ICP-MS. The glycine-type chitosan resin could adsorb several cations by a chelating mechanism and several oxoanions by an anion-exchange mechanism. Especially, the resin could adsorb almost 100% Bi(III) over a wide pH region from pH 2 to 6. Bismuth could be strongly adsorbed at pH 3, and eluted quantitatively with 10 ml of 3 M nitric acid. A column pretreatment method with the glycine-type chitosan resin was used prior to removal of high concentrations of matrices in a seawater sample and the preconcentration of trace bismuth in river water samples for ICP-MS measurements. The column pretreatment method was also applied to the determination of bismuth in real samples by ICP-MS. The LOD of bismuth was 0.1 pg ml(-1) by 10-fold column preconcentration for ICP-MS measurements. The analytical results for bismuth in sea and river water samples by ICP-MS were 22.9 +/- 0.5 pg ml(-1) (RSD, 2.2%) and 2.08 +/- 0.05 pg ml(-1) (RSD, 2.4%), respectively.

Electronic bandstructure of semiconductor dilute bismide structures

NASA Astrophysics Data System (ADS)

Erucar, T.; Nutku, F.; Donmez, O.; Erol, A.

2017-02-01

In this work electronic band structure of dilute bismide GaAs/GaAs1-xBix quantum well structures with 1.8% and 3.75% bismuth compositions have been investigated both experimentally and theoretically. Photoluminescence (PL) measurements reveal that effective bandgap of the samples decreases approximately 65 meV per bismuth concentration. Temperature dependence of the effective bandgap is obtained to be higher for the sample with higher bismuth concentration. Moreover, both asymmetric characteristic at the low energy tail of the PL and full width at half maximum (FWHM) of PL peak increase with increasing bismuth composition as a result of increased Bi related defects located above valence band (VB). In order to explain composition dependence of the effective bandgap quantitatively, valence band anti-crossing (VBAC) model is used. Bismuth composition and temperature dependence of effective bandgap in a quantum well structure is modeled by solving Schrödinger equation and compared with experimental PL data.

Element Distribution in the Oxygen-Rich Side-Blow Bath Smelting of a Low-Grade Bismuth-Lead Concentrate

NASA Astrophysics Data System (ADS)

Yang, Tianzu; Xiao, Hui; Chen, Lin; Chen, Wei; Liu, Weifeng; Zhang, Duchao

2018-03-01

Oxygen-rich side-blow bath smelting (OSBS) technology offers an efficient method for processing complex bismuth-lead concentrates; however, the element distributions in the process remain unclear. This work determined the distributions of elements, i.e., bismuth, lead, silver, copper, arsenic and antimony, in an industrial-scale OSBS process. The feed, oxidized slag and final products were collected from the respective sampling points and analyzed. For the oxidative smelting process, 65% of bismuth and 76% of silver in the concentrate report to the metal alloy, whereas less lead reports to the metal ( 31%) than the oxidized slag ( 44%). Approximately 50% of copper enters the matte, while more than 63% of arsenic and antimony report to the slag. For the reductive smelting process, less than 4.5% of bismuth, lead, silver and copper in the oxidized slag enter the reduced slag, indicating high recoveries of these metal values.

Element Distribution in the Oxygen-Rich Side-Blow Bath Smelting of a Low-Grade Bismuth-Lead Concentrate

NASA Astrophysics Data System (ADS)

Yang, Tianzu; Xiao, Hui; Chen, Lin; Chen, Wei; Liu, Weifeng; Zhang, Duchao

2018-06-01

Oxygen-rich side-blow bath smelting (OSBS) technology offers an efficient method for processing complex bismuth-lead concentrates; however, the element distributions in the process remain unclear. This work determined the distributions of elements, i.e., bismuth, lead, silver, copper, arsenic and antimony, in an industrial-scale OSBS process. The feed, oxidized slag and final products were collected from the respective sampling points and analyzed. For the oxidative smelting process, 65% of bismuth and 76% of silver in the concentrate report to the metal alloy, whereas less lead reports to the metal ( 31%) than the oxidized slag ( 44%). Approximately 50% of copper enters the matte, while more than 63% of arsenic and antimony report to the slag. For the reductive smelting process, less than 4.5% of bismuth, lead, silver and copper in the oxidized slag enter the reduced slag, indicating high recoveries of these metal values.

Studies on Ionic Conductivity and Electrochemical Stability of Plasticized Photopolymerized Polymer Electrolyte Membranes for Solid State Lithium Ion Batteries

NASA Astrophysics Data System (ADS)

He, Ruixuan

In pursuit of safer and more flexible solid-state lithium ion batteries, solid polymer electrolytes have emerged as a promising candidate. The present dissertation entails exploration of solid plasticized, photopolymerized (i.e. ultraviolent-cured) polymer electrolyte membranes (PEM) for fulfilling the critical requirements of electrolytes, such as high ionic conductivity and good thermal and electrochemical stability, among others. Electrochemical performance of PEMs containing lithium ion half-cells was also investigated at different two temperatures. Phase diagram approach was adopted to guide the fabrication of two types of plasticized PEMs. Prepolymer poly (ethylene glycol) diacrylate (PEGDA) was used as a matrix for building an ionic conductive and mechanically sturdy network. Lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) was incorporated as a source of lithium ions, while a solid plasticizer succinonitrile (SCN) and a liquid plasticizer tetraethylene glycol dimethyl ether (TEGDME) were incorporated in the respective systems. The important role of plasticizer on the enhancement of ionic conductivity (sigma) to the superionic conductive level (10-3 S/cm) was revealed in both systems. It is worth noting that photopolymerization induced crystallization (PIC) occurred during UV-curing in the SCN-rich region of the ternary PEGDA/LiTFSI/SCN ternary mixtures. The PEM thus formed contained a plastic crystal phase, which showed lower σ relative to their amorphous PEGDA/LiTFSI/TEGDME counterpart. Comparisons on other thermal and electrochemical properties of the two types of PEMs are presented in Chapter IV. For the PEGDA/LiTFSI/SCN PEMs, fundamental study was carried out to clarify the relationship between σ and glass transition temperature (T g). In lithium salt/polymer binary PEMs, increase in Tg and reduction in σ were observed; these may be attributed to ion-dipole complexation between dissociated lithium cations and ether oxygen upon salt addition. Notably, above the threshold salt concentration of 7 mol %, dual loss tangent peaks were observed in dynamic mechanical studies. These might be ascribed to segmental relaxations of ion-dipole complexed networks and that of polymer chains surrounding the undissociated lithium salt acting like "fillers". Upon SCN incorporation, these two peaks merged into one that was further suppressed below the Tg of the pure network, whereas σ improved to the superionic conductor level. The role of SCN on the σ enhancement as both plasticizer for the polymer network and ionizer for the salt is discussed in Chapter V. In order to improve the mechanical toughness of the highly conductive PEGDA/LiTFSI/SCN PEM, effects of prepolymer molecular weight on mechanical and electrochemical properties of PEMs were further investigated. By increasing molecular weight of PEGDA from 700 to 6000 g/mol, toughness and elongation at break were enhanced as expected. Interestingly, improved ionic conductivity was achieved simultaneously. The dual improvement may be attributed to the less chemical crosslinked points and the more flexible chain motion in the looser network of PEGDA6000-PEM relative to its PEGDA700 counterpart. Subsequently, high thermal stability and electrochemical stability of both types of PEMs, as well as the satisfactory room temperature charge/discharge cycling performance of PEM containing lithium ion half-cells were observed. The pertinent information is documented in Chapter VI. Finally, the investigation of the charge/discharge cycling performance of solid-state LiFePO4 half-cells at an elevated temperature of 60°C is discussed in Chapter VII. In the half-cells, particularly, SCN plasticized PEMs with and without electrolyte modifier lithium bis(oxalato)borate (LiBOB) were respectively employed. Rapid decline of capacity and increase of cell resistance were found in the unmodified PEM containing cell; however, these deteriorations were greatly suppressed upon LiBOB modification. Electrochemical and thermal compatibility of PEMs towards different electrodes were examined in several symmetric cells and half-cells. Detailed characterization on LiFePO 4 electrodes and PEMs retrieved from these cells implied that the observed battery failure might be triggered by an amide-forming side reaction that took place at the interface of a SCN plasticized PEM and a lithium electrode at high temperature. Of particular importance is the fact that this detrimental side reaction was effectively suppressed upon LiBOB electrolyte modifier addition. Plausible mechanisms are discussed.

Impact of vanadium ions in barium borate glass.

PubMed

Abdelghany, A M; Hammad, Ahmed H

2015-02-25

Combined optical and infrared spectral measurements of prepared barium borate glasses containing different concentrations of V2O5 were carried out. Vanadium containing glasses exhibit extended UV-visible (UV/Vis.) bands when compared with base binary borate glass. UV/Vis. spectrum shows the presence of an unsymmetrical strong UV broad band centered at 214 nm attributed to the presence of unavoidable trace iron impurities within the raw materials used for the preparation of such glass. The calculated direct and indirect optical band gaps are found to decrease with increasing the vanadium content (2.9:137 for indirect and 3.99:2.01 for direct transition). This change was discussed in terms of structural changes in the glass network. Infrared absorption spectra of the glasses reveal the appearance of both triangular and tetrahedral borate units. Electron spin resonance analyses indicate the presence of unpaired species in sufficient quantity to be identified and to confirm the spectral data. Copyright © 2014 Elsevier B.V. All rights reserved.

Reliability of Monte Carlo simulations in modeling neutron yields from a shielded fission source

NASA Astrophysics Data System (ADS)

McArthur, Matthew S.; Rees, Lawrence B.; Czirr, J. Bart

2016-08-01

Using the combination of a neutron-sensitive 6Li glass scintillator detector with a neutron-insensitive 7Li glass scintillator detector, we are able to make an accurate measurement of the capture rate of fission neutrons on 6Li. We used this detector with a 252Cf neutron source to measure the effects of both non-borated polyethylene and 5% borated polyethylene shielding on detection rates over a range of shielding thicknesses. Both of these measurements were compared with MCNP calculations to determine how well the calculations reproduced the measurements. When the source is highly shielded, the number of interactions experienced by each neutron prior to arriving at the detector is large, so it is important to compare Monte Carlo modeling with actual experimental measurements. MCNP reproduces the data fairly well, but it does generally underestimate detector efficiency both with and without polyethylene shielding. For non-borated polyethylene it underestimates the measured value by an average of 8%. This increases to an average of 11% for borated polyethylene.

Borate cross-linking chitosan/graphene oxide films: Toward the simultaneous enhancement of gases barrier and mechanical properties

NASA Astrophysics Data System (ADS)

Yan, Ning; Capezzuto, Filomena; Buonocore, Giovanna G.; Tescione, Fabiana; Lavorgna, Marino; Xia, Hesheng; Ambrosio, Luigi

2015-12-01

Borate adducts, originated from hydrolysis of sodium tetraborate decahydrate (borax), have been used to crosslink chitosan (CS) and graphene oxide (GO) nanosheets for the production of innovative composite sustainable materials. CS/GO film consisting of 10wt% borax and 1wt% GO exhibits a significant improvement of both toughness and oxygen barrier properties in comparison to pristine chitosan. In particular the tensile strength increases by about 100% and 150% after thermal annealing of samples at 90°C for 50min whereas the oxygen permeability reduces of about 90% compared to pristine chitosan. The enhancement of both mechanical and barrier properties is ascribed to the formation of a resistant network due to the chemical crosslinking, including borate orthoester bonds and hydroxyl moieties complexes, formed among borate ions, chitosan, and GO nanoplatelets. The crosslinked graphene-based chitosan material with its enhanced mechanical and barrier properties may significantly broad the range of applications of chitosan based-materials which presently are very limited and addressed only to packaging.

D-Tagatose production in the presence of borate by resting Lactococcus lactis cells harboring Bifidobacterium longum L-arabinose isomerase.

PubMed

Salonen, Noora; Salonen, Kalle; Leisola, Matti; Nyyssölä, Antti

2013-04-01

Bifidobacterium longum NRRL B-41409 L-arabinose isomerase (L-AI) was overexpressed in Lactococcus lactis using a phosphate depletion inducible expression system. The resting L. lactis cells harboring the B. longum L-AI were used for production of D-tagatose from D-galactose in the presence of borate buffer. Multivariable analysis suggested that high pH, temperature and borate concentration favoured the conversion of D-galactose to D-tagatose. Almost quantitative conversion (92 %) was achieved at 20 g L⁻¹ substrate and at 37.5 °C after 5 days. The D-tagatose production rate of 185 g L⁻¹ day ⁻¹ was obtained at 300 g L⁻¹ galactose, at 1.15 M borate, and at 41 °C during 10 days when the production medium was changed every 24 h. There was no significant loss in productivity during ten sequential 24 h batches. The initial D-tagatose production rate was 290 g L⁻¹ day⁻¹ under these conditions.

Vibrational spectroscopy of the borate mineral kotoite Mg₃(BO₃)₂.

PubMed

Frost, Ray L; Xi, Yunfei

2013-02-15

Vibrational spectroscopy has been used to assess the structure of kotoite a borate mineral of magnesium which is isostructural with jimboite. The mineral is orthorhombic with point group: 2/m 2/m 2/m. The mineral has the potential as a new memory insulator material. The mineral has been characterised by a combination of Raman and infrared spectroscopy. The Raman spectrum is dominated by a very intense band at 835 cm(-1), assigned to the symmetric stretching mode of tetrahedral boron. Raman bands at 919, 985 and 1015 cm(-1) are attributed to the antisymmetric stretching modes of tetrahedral boron. Kotoite is strictly an hydrous borate mineral. An intense Raman band observed at 3559 cm(-1) is attributed to the stretching vibration of hydroxyl units, more likely to be associated with the borate mineral hydroxyborate. The lack of observation of water bending modes proves the absence of water in the kotoite structure. Copyright © 2012 Elsevier B.V. All rights reserved.

New insight in the nature of surface magnetic anisotropy in iron borate

NASA Astrophysics Data System (ADS)

Strugatsky, M.; Seleznyova, K.; Zubov, V.; Kliava, J.

2018-02-01

The theory of surface magnetism of iron borate, FeBO3, has been extended by taking into consideration a crystal field contribution to the surface magnetic anisotropy energy. For this purpose, a model of distortion of the six-fold oxygen environment of iron ions in the near-surface layer of iron borate has been put forward. The spin Hamiltonian parameters for isolated Fe3+ ions in the distorted environment of the near-surface layer have been calculated using the Newman's superposition model. The crystal field contribution to the surface magnetic anisotropy energy has been calculated in the framework of the perturbation theory. The model developed allows concluding that the distortions of the iron environment produce a significant crystal field contribution to the surface magnetic anisotropy constant. The results of experimental studies of the surface magnetic anisotropy in iron borate can be described assuming the existence of relative contractions in the near-surface layer of the order of 1 %.

40 CFR 471.11 - Effluent limitations representing the degree of effluent reduction attainable by the application...

Code of Federal Regulations, 2013 CFR

2013-07-01

... SOURCE CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.11 Effluent limitations representing the... lead-tin-bismuth rolled with emulsions Antimony 0.068 0.030 Lead 0.010 0.005 Oil and grease 0.468 0.281... mg/off-kg (pounds per million off-pound) of lead-tin-bismuth rolled with soap solutions Antimony 0...

40 CFR 471.11 - Effluent limitations representing the degree of effluent reduction attainable by the application...

Code of Federal Regulations, 2012 CFR

2012-07-01

... SOURCE CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.11 Effluent limitations representing the... lead-tin-bismuth rolled with emulsions Antimony 0.068 0.030 Lead 0.010 0.005 Oil and grease 0.468 0.281... mg/off-kg (pounds per million off-pound) of lead-tin-bismuth rolled with soap solutions Antimony 0...

40 CFR 471.12 - Effluent limitations representing the degree of effluent reduction attainable by the application...

Code of Federal Regulations, 2014 CFR

2014-07-01

... CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.12 Effluent limitations representing the degree of... average mg/off-kg (pounds per million off-pounds) of lead-tin-bismuth rolled with emulsion Antimony 0.067... lead-tin-bismuth rolled with soap solutions Antimony 0.120 0.055 Lead 0.018 0.009 (c) Drawing spent...

40 CFR 471.11 - Effluent limitations representing the degree of effluent reduction attainable by the application...

Code of Federal Regulations, 2014 CFR

2014-07-01

... SOURCE CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.11 Effluent limitations representing the... lead-tin-bismuth rolled with emulsions Antimony 0.068 0.030 Lead 0.010 0.005 Oil and grease 0.468 0.281... mg/off-kg (pounds per million off-pound) of lead-tin-bismuth rolled with soap solutions Antimony 0...

40 CFR 471.12 - Effluent limitations representing the degree of effluent reduction attainable by the application...

Code of Federal Regulations, 2012 CFR

2012-07-01

... CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.12 Effluent limitations representing the degree of... average mg/off-kg (pounds per million off-pounds) of lead-tin-bismuth rolled with emulsion Antimony 0.067... lead-tin-bismuth rolled with soap solutions Antimony 0.120 0.055 Lead 0.018 0.009 (c) Drawing spent...

40 CFR 471.12 - Effluent limitations representing the degree of effluent reduction attainable by the application...

Code of Federal Regulations, 2011 CFR

2011-07-01

...-Tin-Bismuth Forming Subcategory § 471.12 Effluent limitations representing the degree of effluent... average mg/off-kg (pounds per million off-pounds) of lead-tin-bismuth rolled with emulsion Antimony 0.067... lead-tin-bismuth rolled with soap solutions Antimony 0.120 0.055 Lead 0.018 0.009 (c) Drawing spent...

40 CFR 471.12 - Effluent limitations representing the degree of effluent reduction attainable by the application...

Code of Federal Regulations, 2010 CFR

2010-07-01

...-Tin-Bismuth Forming Subcategory § 471.12 Effluent limitations representing the degree of effluent... average mg/off-kg (pounds per million off-pounds) of lead-tin-bismuth rolled with emulsion Antimony 0.067... lead-tin-bismuth rolled with soap solutions Antimony 0.120 0.055 Lead 0.018 0.009 (c) Drawing spent...

40 CFR 471.12 - Effluent limitations representing the degree of effluent reduction attainable by the application...

Code of Federal Regulations, 2013 CFR

2013-07-01

... CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.12 Effluent limitations representing the degree of... average mg/off-kg (pounds per million off-pounds) of lead-tin-bismuth rolled with emulsion Antimony 0.067... lead-tin-bismuth rolled with soap solutions Antimony 0.120 0.055 Lead 0.018 0.009 (c) Drawing spent...

Build-up enhancement of photoluminescence from phenylazomethine bismuth dendrimer using Bi(OTf)3

NASA Astrophysics Data System (ADS)

Kambe, Tetsuya; Imaoka, Shotaro; Imaoka, Takane; Yamamoto, Kimihisa

2018-05-01

Metal assembly to a dendrimer can provide various functionalities based on the branched structure. Here, we researched assembly phenomena of bismuth salts in the phenylazomethine dendrimer and achieved enhancement of emission intensity per metal unit by using Bi(OTf)3. This enhancement suggested increasing of Bi-N coordination bonds derived from the bismuth units in the dendrimer.

Computational chemistry calculations of stability for bismuth nanotubes, fullerene-like structures and hydrogen-containing nanostructures.

PubMed

Kharissova, Oxana V; Osorio, Mario; Vázquez, Mario Sánchez; Kharisov, Boris I

2012-08-01

Using molecular mechanics (MM+), semi-empirical (PM6) and density functional theory (DFT) (B3LYP) methods we characterized bismuth nanotubes. In addition, we predicted the bismuth clusters {Bi(20)(C(5V)), Bi(24)(C(6v)), Bi(28)(C(1)), B(32)(D(3H)), Bi(60)(C(I))} and calculated their conductor properties.

Increased InAs quantum dot size and density using bismuth as a surfactant

NASA Astrophysics Data System (ADS)

Dasika, Vaishno D.; Krivoy, E. M.; Nair, H. P.; Maddox, S. J.; Park, K. W.; Jung, D.; Lee, M. L.; Yu, E. T.; Bank, S. R.

2014-12-01

We have investigated the growth of self-assembled InAs quantum dots using bismuth as a surfactant to control the dot size and density. We find that the bismuth surfactant increases the quantum dot density, size, and uniformity, enabling the extension of the emission wavelength with increasing InAs deposition without a concomitant reduction in dot density. We show that these effects are due to bismuth acting as a reactive surfactant to kinetically suppress the surface adatom mobility. This mechanism for controlling quantum dot density and size has the potential to extend the operating wavelength and enhance the performance of various optoelectronic devices.

Composition for radiation shielding

DOEpatents

Kronberg, J.W.

1994-08-02

A composition for use as a radiation shield is disclosed. The shield has a depleted uranium core for absorbing gamma rays and a bismuth coating for preventing chemical corrosion and absorbing gamma rays. Alternatively, a sheet of gadolinium may be positioned between the uranium core and the bismuth coating for absorbing neutrons. The composition is preferably in the form of a container for storing materials that emit radiation such as gamma rays and neutrons. The container is preferably formed by casting bismuth around a pre-formed uranium container having a gadolinium sheeting, and allowing the bismuth to cool. The resulting container is a structurally sound, corrosion-resistant, radiation-absorbing container. 2 figs.

Topological Insulator State in Thin Bismuth Films Subjected to Plane Tensile Strain

NASA Astrophysics Data System (ADS)

Demidov, E. V.; Grabov, V. M.; Komarov, V. A.; Kablukova, N. S.; Krushel'nitskii, A. N.

2018-03-01

The results of experimental examination of galvanomagnetic properties of thin bismuth films subjected to plane tensile strain resulting from the difference in thermal expansion coefficients of the substrate material and bismuth are presented. The resistivity, the magnetoresistance, and the Hall coefficient were studied at temperatures ranging from 5 to 300 K in magnetic fields as strong as 0.65 T. Carrier densities were calculated. A considerable increase in carrier density in films thinner than 30 nm was observed. This suggests that surface states are more prominent in thin bismuth films on mica substrates, while the films themselves may exhibit the properties of a topological insulator.

Oxidation mechanism of formic acid on the bismuth adatom-modified Pt(111) surface.

PubMed

Perales-Rondón, Juan Victor; Ferre-Vilaplana, Adolfo; Feliu, Juan M; Herrero, Enrique

2014-09-24

In order to improve catalytic processes, elucidation of reaction mechanisms is essential. Here, supported by a combination of experimental and computational results, the oxidation mechanism of formic acid on Pt(111) electrodes modified by the incorporation of bismuth adatoms is revealed. In the proposed model, formic acid is first physisorbed on bismuth and then deprotonated and chemisorbed in formate form, also on bismuth, from which configuration the C-H bond is cleaved, on a neighbor Pt site, yielding CO2. It was found computationally that the activation energy for the C-H bond cleavage step is negligible, which was also verified experimentally.

Composition for radiation shielding

DOEpatents

Kronberg, James W.

1994-01-01

A composition for use as a radiation shield. The shield has a depleted urum core for absorbing gamma rays and a bismuth coating for preventing chemical corrosion and absorbing gamma rays. Alternatively, a sheet of gadolinium may be positioned between the uranium core and the bismuth coating for absorbing neutrons. The composition is preferably in the form of a container for storing materials that emit radiation such as gamma rays and neutrons. The container is preferably formed by casting bismuth around a pre-formed uranium container having a gadolinium sheeting, and allowing the bismuth to cool. The resulting container is a structurally sound, corrosion-resistant, radiation-absorbing container.

Bismuth oxyhalide nanomaterials: layered structures meet photocatalysis

NASA Astrophysics Data System (ADS)

Li, Jie; Yu, Ying; Zhang, Lizhi

2014-07-01

In recent years, layered bismuth oxyhalide nanomaterials have received more and more interest as promising photocatalysts because their unique layered structures endow them with fascinating physicochemical properties; thus, they have great potential photocatalytic applications for environment remediation and energy harvesting. In this article, we explore the synthesis strategies and growth mechanisms of layered bismuth oxyhalide nanomaterials, and propose design principles of tailoring a layered configuration to control the nanoarchitectures for high efficient photocatalysis. Subsequently, we focus on their layered structure dependent properties, including pH-related crystal facet exposure and phase transformation, facet-dependent photoactivity and molecular oxygen activation pathways, so as to clarify the origin of the layered structure dependent photoreactivity. Furthermore, we summarize various strategies for modulating the composition and arrangement of layered structures to enhance the photoactivity of nanostructured bismuth oxyhalides via internal electric field tuning, dehalogenation effect, surface functionalization, doping, plasmon modification, and heterojunction construction, which may offer efficient guidance for the design and construction of high-performance bismuth oxyhalide-based photocatalysis systems. Finally, we highlight some crucial issues in engineering the layered-structure mediated properties of bismuth oxyhalide photocatalysts and provide tentative suggestions for future research on increasing their photocatalytic performance.

Investigation of passive films formed on the surface of alloy 690 in borate buffer solution

NASA Astrophysics Data System (ADS)

Jinlong, Lv; Tongxiang, Liang; Chen, Wang; Wenli, Guo

2015-10-01

The passive film formed on the surface of the alloy 690 in borate buffer solution was studied by potentiodynamic curves and electrochemical impedance spectroscopy. With the increasing of the passivation potential, the corrosion resistance of the alloy 690 reduced. Moreover, the corrosion resistance of the passive film was the lowest in the vicinity of 0.6 VSCE. These results were supported by XPS and Mott-Schottky analyses. The corrosion resistance of the alloy 690 increased with the increasing of passivated potential in borate buffer solution with chloride ion. The chloride ion decreased corrosion resistance of the alloy 690 according to point defect model.

[Investigations of the efficacy and bio-availability of different pilocarpine eye drops].

PubMed

Tapasztó, I; Boross, F

1982-01-01

The efficacy of three pilocarpine preparations in different concentrations (pilocarpine borate 0.5%, 1%, 2%; pilocarpine hydrochloride 0.5%, 1%, 2%; pilocarpine nitrate 1%, 2%) was investigated in 57 glaucomatous patients. Pilocarpine borate reduced intraocular pressure more effectively than either of the other pilocarpine solutions. The 2% concentration had a particularly prolonged effect. This finding corresponded well with pilocarpine levels in the aqueous humour of rabbits, as determined by spectrophotometric analysis. Pilocarpine borate 2% revealed an almost two-fold amount of drug compared to the 2% hydrochloride and nitrate solutions, and a detectable pilocarpine level was present for a longer period as well.

A method for determining the composition of methanol-trimethyl borate mixtures

NASA Technical Reports Server (NTRS)

Kaye, Samuel; Sordyl, Frank

1955-01-01

A study of mixtures of pure methanol and trimethyl borate showed that the composition can be accurately obtained by a simple density determination. The refractive-index determination gives the composition with much less accuracy. The potentiometric titration of boric acid is also discussed.

INFLUENCE OF BORATE BUFFERS ON THE ELECTROPHORETIC BEHAVIOR OF HUMIC SUBSTANCES IN CAPILLARY ZONE ELECTROPHORESIS

EPA Science Inventory

The influence of tetrahydroxyborate ions on the electrophoretic mobility of humic acids was evaluated by capillary electrophoresis (CE). Depending on the molarity of borate ions in the separation buffer, the humic acids exhibit electropherograms with sharp peaks consistently exte...

Hydrothermal synthesis and structural analysis of new mixed oxyanion borates: Ba11B26O44(PO4)2(OH)6, Li9BaB15O27(CO3) and Ba3Si2B6O16

NASA Astrophysics Data System (ADS)

Heyward, Carla; McMillen, Colin D.; Kolis, Joseph

2013-07-01

Several new borate compounds, Ba11B26O44(PO4)2(OH)6 (1), Li9BaB15O27(CO3) (2), and Ba3Si2B6O16 (3) were synthesized containing other hetero-oxyanion building blocks in addition to the borate frameworks. They were all prepared under hydrothermal conditions and characterized by single crystal and powder X-ray diffraction, and IR spectroscopy. Crystal data: For 1; space group P21/c, a=6.8909 (14) Å, b=13.629 (3) Å, c=25.851 (5) Å, β=90.04 (3)°; For 2; space group P-31c, a=8.8599 (13) Å, c=15.148 (3) Å; For 3; space group P-1, a=5.0414 (10) Å, b=7.5602 (15) Å, c=8.5374 (17) Å, α=77.15 (3)°, β=77.84 (3)°, γ=87.41 (3)° for 3. Compounds 1 and 2 contain isolated oxyanions [PO4]3- and [CO3]2- respectively, sitting in channels created by the borate framework, while structure 3 has the [SiO4]4- groups directly bonded to the borate groups creating a B-O-Si framework.

Effects of chronic Akt/mTOR inhibition by rapamycin on mechanical overload-induced hypertrophy and myosin heavy chain transition in masseter muscle.

PubMed

Umeki, Daisuke; Ohnuki, Yoshiki; Mototani, Yasumasa; Shiozawa, Kouichi; Fujita, Takayuki; Nakamura, Yoshiki; Saeki, Yasutake; Okumura, Satoshi

2013-01-01

To examine the effects of the Akt/mammalian target of rapamycin (mTOR) pathway on masseter muscle hypertrophy and myosin heavy chain (MHC) transition in response to mechanical overload, we analyzed the effects of bite-opening (BO) on the hypertrophy and MHC composition of masseter muscle of BO-rats treated or not treated with rapamycin (RAPA), a selective mTOR inhibitor. The masseter muscle weight in BO-rats was significantly greater than that in controls, and this increase was attenuated by RAPA treatment. Expression of slow-twitch MHC isoforms was significantly increased in BO-rats with/without RAPA treatment, compared with controls, but the magnitude of the increase was much smaller in RAPA-treated BO-rats. Phosphorylation of p44/42 MAPK (ERK1/2), which preserves fast-twitch MHC isoforms in skeletal muscle, was significantly decreased in BO-rats, but the decrease was abrogated by RAPA treatment. Calcineurin signaling is known to be important for masseter muscle hypertrophy and fast-to-slow MHC isoform transition, but expression of known calcineurin activity modulators was unaffected by RAPA treatment. Taken together, these results indicate that the Akt/mTOR pathway is involved in both development of masseter muscle hypertrophy and fast-to-slow MHC isoform transition in response to mechanical overload with inhibition of the ERK1/2 pathway and operates independently of the calcineurin pathway.

Degradable borate glass polyalkenoate cements.

PubMed

Shen, L; Coughlan, A; Towler, M; Hall, M

2014-04-01

Glass polyalkenoate cements (GPCs) containing aluminum-free borate glasses having the general composition Ag2O-Na2O-CaO-SrO-ZnO-TiO2-B2O3 were evaluated in this work. An initial screening study of sixteen compositions was used to identify regions of glass formation and cement compositions with promising rheological properties. The results of the screening study were used to develop four model borate glass compositions for further study. A second round of rheological experiments was used to identify a preferred GPC formulation for each model glass composition. The model borate glasses containing higher levels of TiO2 (7.5 mol %) tended to have longer working times and shorter setting times. Dissolution behavior of the four model GPC formulations was evaluated by measuring ion release profiles as a function of time. All four GPC formulations showed evidence of incongruent dissolution behavior when considering the relative release profiles of sodium and boron, although the exact dissolution profile of the glass was presumably obscured by the polymeric cement matrix. Compression testing was undertaken to evaluate cement strength over time during immersion in water. The cements containing the borate glass with 7.5 mol % TiO2 had the highest initial compressive strength, ranging between 20 and 30 MPa. No beneficial aging effect was observed-instead, the strength of all four model GPC formulations was found to degrade with time.

Thermal-stability studies of electrode materials for lithium-ion batteries

NASA Astrophysics Data System (ADS)

Jiang, Junwei

2005-07-01

The thermal stability of lithium-ion batteries has recently attracted attention for two major reasons. (1) Attempts to make large-size cells used in power tools, E-bikes and EVs. Large cells have lower surface area to volume ratios and hence heat dissipation is more problematic than 18650-size cells. Safety problems, therefore, for large cells are more serious. (2) Next generation high-capacity electrodes will increase the energy density of lithium-ion cells meaning even an 18650-size cell may face safety concerns. This thesis presents studies of the thermal stability of electrode materials in electrolytes to understand their reactivity. A search for new positive electrode materials with high thermal stability was made. The thermal stability of two common electrode materials (Li0.81 C6 and Li0.5CoO2) in lithium-ion cells was studied by Accelerating Rate Calorimeter (ARC). Li0.81C 6 has much lower reactivity with lithium bis(oxalato)borate (LiBOB) electrolyte compared to LiPF6 electrolyte. It is not the case, however, for Li0.5CoO2. Oven tests of full LiCoO 2/C 18650-size cells with LiBOB or LiPF6 electrolytes, confirmed the ARC results. ARC was then used to study the reactivity of existing electrode materials. The thermal stability of a negative electrode material was found to increase with the binding energy of Li atoms hosted in the material. Li0.5VO 2 (B) has a higher lithium binding energy (2.45 eV vs. Li) than Li 0.81C6 (0.1 eV vs. Li) and Li7Ti5O 12 (1.55 eV) and it shows the highest thermal stability in EC/DEC among the three materials. The reactivity of two existing positive electrode materials, LiMn2O4 and LiFePO4, was studied. Cell systems expected to be highly tolerant to thermal abuse were suggested: LiFePO 4/C or Li4Ti5O12 in LiBOB electrolytes. The system, x Li[Ni1/2Mn1/2]O2 • y LiCoO2 • z Li[Li1/3Mn2/3]O2 (x + y + z = 1), was explored for new positive electrode materials with large capacity and high thermal stability. Li[(Ni0.5Mn0.5) xCo1-x]O2 (0.4 ≤ x ≤ 0.7) samples have excellent electrochemical properties and thermal stability and are being commercialized by industry. Li[(Ni0.5Mn0.5)xCo y(Li1/3Mn2/3)z]O2 (1/12 ≤ y ≤ 1/4, 1/6 ≤ z ≤ 1/3) samples have high specific capacity (200 mA h g-1), excellent cycling performance, and are safer than LiCoO2. The materials are suggested for energy cells used in cell phones, laptops, and so on.

40 CFR 471.11 - Effluent limitations representing the degree of effluent reduction attainable by the application...

Code of Federal Regulations, 2010 CFR

2010-07-01

... CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.11 Effluent limitations representing the degree of... lead-tin-bismuth rolled with emulsions Antimony 0.068 0.030 Lead 0.010 0.005 Oil and grease 0.468 0.281... mg/off-kg (pounds per million off-pound) of lead-tin-bismuth rolled with soap solutions Antimony 0...

40 CFR 471.11 - Effluent limitations representing the degree of effluent reduction attainable by the application...

Code of Federal Regulations, 2011 CFR

2011-07-01

... CATEGORY Lead-Tin-Bismuth Forming Subcategory § 471.11 Effluent limitations representing the degree of... lead-tin-bismuth rolled with emulsions Antimony 0.068 0.030 Lead 0.010 0.005 Oil and grease 0.468 0.281... mg/off-kg (pounds per million off-pound) of lead-tin-bismuth rolled with soap solutions Antimony 0...

Heat-Pipe Bismuth Laser; Examination of Laser Action at 4722A in Bismuth Vapor

DTIC Science & Technology

1976-11-01

11, 15(1975). of Type 6p 3 -6p 2 7s in the Bismuth Atomic Spectrum in Intermediate Coupling," Acta Physica Polonica A47, 231(1975). 19. A.N. Nesmeyanov...Calculated Transit n Probabilities and Lifetimes for the First Excited Configuration np (n+l)s in the Neutral As, Sb and Bi Atoms, " Physica Scripta

Using quality control to limit bismuth in copper cathodes

NASA Astrophysics Data System (ADS)

Serrano, John R.; Berger, Dennis; Bridges, Bill

1994-10-01

This article describes quality-control work at Phelps Dodge, undertaken as part of ISO 9003 certification, to better identify and prevent the contamination of copper cathodes by bismuth. It also overviews the implementation of a production control system as well as associated training designed to minimize the possibility of bismuth-contaminated copper progressing beyond the cathode stage to other areas of manufacturing or distribution.

77 FR 27815 - Aging Management of Stainless Steel Structures and Components in Treated Borated Water

Federal Register 2010, 2011, 2012, 2013, 2014

2012-05-11

... NUCLEAR REGULATORY COMMISSION [NRC-2011-0256] Aging Management of Stainless Steel Structures and... Guidance (LR-ISG), LR-ISG-2011-01, ``Aging Management of Stainless Steel Structures and Components in...) Report for the aging management of stainless steel structures and components exposed to treated borated...

76 FR 69292 - Aging Management of Stainless Steel Structures and Components in Treated Borated Water

Federal Register 2010, 2011, 2012, 2013, 2014

2011-11-08

... NUCLEAR REGULATORY COMMISSION [NRC-2011-0256] Aging Management of Stainless Steel Structures and... Stainless Steel Structures and Components in Treated Borated Water.'' This LR-ISG revises the guidance in...) and Generic Aging Lessons Learned (GALL) Report for the aging management of stainless steel structures...

77 FR 74883 - Aging Management of Stainless Steel Structures and Components in Treated Borated Water; Revision 1

Federal Register 2010, 2011, 2012, 2013, 2014

2012-12-18

... NUCLEAR REGULATORY COMMISSION [NRC-2011-0256] Aging Management of Stainless Steel Structures and..., ``Aging Management of Stainless Steel Structures and Components in Treated Borated Water,'' which was... Staff Guidance LR-ISG-2011-01, ``Aging Management of Stainless Steel Structures and Components in...

Could borate have played a role in the RNA World?

NASA Astrophysics Data System (ADS)

Grew, E. S.; Bada, J. L.; Hazen, R. M.

2012-12-01

Two scenarios have been proposed for boron to play a critical role in the stabilization of ribose and other sugars in the ribonucleic acid (RNA) World, >3.8 Ga ago. One scenario envisages oligomeric RNA being synthesized in subaerial intermountane desert valleys in which groundwater was enriched in borate from breakdown of tourmaline (Benner et al. 2012 doi: 10.1021/ar200332w). In the alternative scenario, borates are enriched in hydrothermal environments (<150°C) in oceanic crust where ferromagnesian minerals are altered to brucite, serpentine and other minerals that can extract borate from the circulating seawater (Holm et al. 2006 doi:10.1186/1467-4866-7-7). Both scenarios presume that (1) B concentrations in non-marine water or sea water were about the same at >3.8 Ma as they are today and (2) plate tectonics was the prevailing regime. The postulated non-marine borate deposits would have been associated with continental collision and subduction with volcanism releasing B, whereas in the second scenario, ocean floor caught up in an early phase of subduction is considered a favorable site for borate formation. Because borate deposits are typically ephemeral and poorly preserved, the lack of evidence in the geologic record for these scenarios does not invalidate them. For example, the oldest reported non-marine borate deposits analogous to the type postulated in first scenario are only 20 Ma, but metamorphosed borates of Precambrian age have been interpreted to have non-marine evaporite precursors, the oldest being 2.4-2.1 Ga in the Liaoning-Jilin area, China. The first B minerals so far reported in the geologic record are metamorphic dravite-schorl tourmalines in the 3.7-3.8 Ga Isua supracrustal belt (southern West Greenland), where there is good evidence for seafloor spreading and subduction. The precursors to the Isua tourmalines are reported to include B-bearing marine clay minerals and detrital tourmaline. The relatively high Li contents in zircon from Jack Hills, Australia, have been cited as evidence for the presence of granitic (s. l.) "protocontinental" crust by 4.3 Ga (Ushikuba et al. 2008 doi:10.1016/j.epsl.2008.05.032; Valley et al. 2010 Rec Geol Surv W Aust, 5-7), but the existence of conventional plate tectonics prior to 3.8 Ga remains controversial. Chaussidon & Appel (1997 Chem Geol 136, 171-180) concluded that boron isotope compositions (δ11B) of tourmaline from Isua volcaniclastic rocks provide no evidence for changes of δ11B in the mantle or continental crust between now and 3.8 Ga, whereas the very light B (δ11B = -20‰) in tourmaline from Isua metachert could indicate that seawater δ11B was at least 10‰ less at 3.8 Ga than now and that there was proportionally less B in sediments at 3.8 Ga, i.e., fractionation of B between depleted mantle, oceans, continental crust and oceanic crust was still in progress (Chaussidon & Albarède 1992, EPSL 108, 229-241). If fractionation and outgassing of boron had not proceeded very far during the RNA World, neither of the proposed scenarios of borate enrichment is plausible, particularly in the absence of a conventional plate tectonics regime.

Radiation dose reduction to the breast in thoracic CT: Comparison of bismuth shielding, organ-based tube current modulation, and use of a globally decreased tube current

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang Jia; Duan Xinhui; Christner, Jodie A.

2011-11-15

Purpose: The purpose of this work was to evaluate dose performance and image quality in thoracic CT using three techniques to reduce dose to the breast: bismuth shielding, organ-based tube current modulation (TCM) and global tube current reduction. Methods: Semi-anthropomorphic thorax phantoms of four different sizes (15, 30, 35, and 40 cm lateral width) were used for dose measurement and image quality assessment. Four scans were performed on each phantom using 100 or 120 kV with a clinical CT scanner: (1) reference scan; (2) scan with bismuth breast shield of an appropriate thickness; (3) scan with organ-based TCM; and (4)more » scan with a global reduction in tube current chosen to match the dose reduction from bismuth shielding. Dose to the breast was measured with an ion chamber on the surface of the phantom. Image quality was evaluated by measuring the mean and standard deviation of CT numbers within the lung and heart regions. Results: Compared to the reference scan, dose to the breast region was decreased by about 21% for the 15-cm phantom with a pediatric (2-ply) shield and by about 37% for the 30, 35, and 40-cm phantoms with adult (4-ply) shields. Organ-based TCM decreased the dose by 12% for the 15-cm phantom, and 34-39% for the 30, 35, and 40-cm phantoms. Global lowering of the tube current reduced breast dose by 23% for the 15-cm phantom and 39% for the 30, 35, and 40-cm phantoms. In phantoms of all four sizes, image noise was increased in both the lung and heart regions with bismuth shielding. No significant increase in noise was observed with organ-based TCM. Decreasing tube current globally led to similar noise increases as bismuth shielding. Streak and beam hardening artifacts, and a resulting artifactual increase in CT numbers, were observed for scans with bismuth shields, but not for organ-based TCM or global tube current reduction. Conclusions: Organ-based TCM produces dose reduction to the breast similar to that achieved with bismuth shielding for both pediatric and adult phantoms. However, organ-based TCM does not affect image noise or CT number accuracy, both of which are adversely affected by bismuth shielding. Alternatively, globally decreasing the tube current can produce the same dose reduction to the breast as bismuth shielding, with a similar noise increase, yet without the streak artifacts and CT number errors caused by the bismuth shields. Moreover, globally decreasing the tube current reduces the dose to all tissues scanned, not simply to the breast.« less

Disturbed oxidative metabolism in organic brain syndrome caused by bismuth in skin creams.

PubMed

Krüger, G; Thomas, D J; Weinhardt, F; Hoyer, S

1976-09-04

Two patients are described with an organic brain syndrome thought to be due to bismuth (Bi) absorbed from a skin cream. Both patients had intellectual impairment and memory loss punctuated by periods of confusion, tremulousness, clumsiness, difficulty in walking, and myoclonic jerks. A similar clinical picture has been reported from Australia and France in patients taking insoluble bismuth salts by mouth. Bi was found in cerebral venous blood in both patients and in the cerebrospinal fluid in one. It is suggested that bismuth can cross the blood/brain barrier and disturb oxidative cerebral metabolism, because increased lactate production was found with decreased consumption of oxygen and glucose and lowered cerebral blood-flow.

Dual-modality, fluorescent, PLGA encapsulated bismuth nanoparticles for molecular and cellular fluorescence imaging and computed tomography

NASA Astrophysics Data System (ADS)

Swy, Eric R.; Schwartz-Duval, Aaron S.; Shuboni, Dorela D.; Latourette, Matthew T.; Mallet, Christiane L.; Parys, Maciej; Cormode, David P.; Shapiro, Erik M.

2014-10-01

Reports of molecular and cellular imaging using computed tomography (CT) are rapidly increasing. Many of these reports use gold nanoparticles. Bismuth has similar CT contrast properties to gold while being approximately 1000-fold less expensive. Herein we report the design, fabrication, characterization, and CT and fluorescence imaging properties of a novel, dual modality, fluorescent, polymer encapsulated bismuth nanoparticle construct for computed tomography and fluorescence imaging. We also report on cellular internalization and preliminary in vitro and in vivo toxicity effects of these constructs. 40 nm bismuth(0) nanocrystals were synthesized and encapsulated within 120 nm Poly(dl-lactic-co-glycolic acid) (PLGA) nanoparticles by oil-in-water emulsion methodologies. Coumarin-6 was co-encapsulated to impart fluorescence. High encapsulation efficiency was achieved ~70% bismuth w/w. Particles were shown to internalize within cells following incubation in culture. Bismuth nanocrystals and PLGA encapsulated bismuth nanoparticles exhibited >90% and >70% degradation, respectively, within 24 hours in acidic, lysosomal environment mimicking media and both remained nearly 100% stable in cytosolic/extracellular fluid mimicking media. μCT and clinical CT imaging was performed at multiple X-ray tube voltages to measure concentration dependent attenuation rates as well as to establish the ability to detect the nanoparticles in an ex vivo biological sample. Dual fluorescence and CT imaging is demonstrated as well. In vivo toxicity studies in rats revealed neither clinically apparent side effects nor major alterations in serum chemistry and hematology parameters. Calculations on minimal detection requirements for in vivo targeted imaging using these nanoparticles are presented. Indeed, our results indicate that these nanoparticles may serve as a platform for sensitive and specific targeted molecular CT and fluorescence imaging.Reports of molecular and cellular imaging using computed tomography (CT) are rapidly increasing. Many of these reports use gold nanoparticles. Bismuth has similar CT contrast properties to gold while being approximately 1000-fold less expensive. Herein we report the design, fabrication, characterization, and CT and fluorescence imaging properties of a novel, dual modality, fluorescent, polymer encapsulated bismuth nanoparticle construct for computed tomography and fluorescence imaging. We also report on cellular internalization and preliminary in vitro and in vivo toxicity effects of these constructs. 40 nm bismuth(0) nanocrystals were synthesized and encapsulated within 120 nm Poly(dl-lactic-co-glycolic acid) (PLGA) nanoparticles by oil-in-water emulsion methodologies. Coumarin-6 was co-encapsulated to impart fluorescence. High encapsulation efficiency was achieved ~70% bismuth w/w. Particles were shown to internalize within cells following incubation in culture. Bismuth nanocrystals and PLGA encapsulated bismuth nanoparticles exhibited >90% and >70% degradation, respectively, within 24 hours in acidic, lysosomal environment mimicking media and both remained nearly 100% stable in cytosolic/extracellular fluid mimicking media. μCT and clinical CT imaging was performed at multiple X-ray tube voltages to measure concentration dependent attenuation rates as well as to establish the ability to detect the nanoparticles in an ex vivo biological sample. Dual fluorescence and CT imaging is demonstrated as well. In vivo toxicity studies in rats revealed neither clinically apparent side effects nor major alterations in serum chemistry and hematology parameters. Calculations on minimal detection requirements for in vivo targeted imaging using these nanoparticles are presented. Indeed, our results indicate that these nanoparticles may serve as a platform for sensitive and specific targeted molecular CT and fluorescence imaging. Electronic supplementary information (ESI) available. See DOI: 10.1039/c4nr01405g

Group III-nitride thin films grown using MBE and bismuth

DOEpatents

Kisielowski, Christian K.; Rubin, Michael

2002-01-01

The present invention comprises growing gallium nitride films in the presence of bismuth using MBE at temperatures of about 1000 K or less. The present invention further comprises the gallium nitride films fabricated using the inventive fabrication method. The inventive films may be doped with magnesium or other dopants. The gallium nitride films were grown on sapphire substrates using a hollow anode Constricted Glow Discharge nitrogen plasma source. When bismuth was used as a surfactant, two-dimensional gallium nitride crystal sizes ranging between 10 .mu.m and 20 .mu.m were observed. This is 20 to 40 times larger than crystal sizes observed when GaN films were grown under similar circumstances but without bismuth. It is thought that the observed increase in crystal size is due bismuth inducing an increased surface diffusion coefficient for gallium. The calculated value of 4.7.times.10.sup.-7 cm.sup.2 /sec. reveals a virtual substrate temperature of 1258 K which is 260 degrees higher than the actual one.

Group III-nitride thin films grown using MBE and bismuth

DOEpatents

Kisielowski, Christian K.; Rubin, Michael

2000-01-01

The present invention comprises growing gallium nitride films in the presence of bismuth using MBE at temperatures of about 1000 K or less. The present invention further comprises the gallium nitride films fabricated using the inventive fabrication method. The inventive films may be doped with magnesium or other dopants. The gallium nitride films were grown on sapphire substrates using a hollow anode Constricted Glow Discharge nitrogen plasma source. When bismuth was used as a surfactant, two-dimensional gallium nitride crystal sizes ranging between 10 .mu.m and 20 .mu.m were observed. This is 20 to 40 times larger than crystal sizes observed when GaN films were grown under similar circumstances but without bismuth. It is thought that the observed increase in crystal size is due bismuth inducing an increased surface diffusion coefficient for gallium. The calculated value of 4.7.times.10.sup.-7 cm.sup.2 /sec. reveals a virtual substrate temperature of 1258 K which is 260 degrees higher than the actual one.

Contrasting role of antimony and bismuth dopants on the thermoelectric performance of lead selenide

DOE PAGES

Lee, Yeseul; Lo, Shih -Han; Chen, Changqiang; ...

2014-05-02

Increasing the conversion efficiency of thermoelectric materials is a key scientific driver behind a worldwide effort to enable heat to electricity power generation at competitive cost. Here we report an increased performance for antimony-doped lead selenide with a thermoelectric figure of merit of ~1.5 at 800 K. This is in sharp contrast to bismuth doped lead selenide, which reaches a figure of merit of <1. Substituting antimony or bismuth for lead achieves maximum power factors between ~23–27μW cm –1 K –2 at temperatures above 400 K. The addition of small amounts (~0.25 mol%) of antimony generates extensive nanoscale precipitates, whereasmore » comparable amounts of bismuth results in very few or no precipitates. The antimony-rich precipitates are endotaxial in lead selenide, and appear remarkably effective in reducing the lattice thermal conductivity. As a result, the corresponding bismuth-containing samples exhibit smaller reduction in lattice thermal conductivity.« less

Movement of elements into the atmosphere from coniferous trees in subalpine forests of colorado and Idaho

USGS Publications Warehouse

Curtin, G.C.; King, H.D.; Mosier, E.L.

1974-01-01

Exudates from conifer trees, presumably consisting largely of volatile materials, were sampled at 19 subalpine localitites in Colorado and Idaho where anomalous amounts of several metals were determined in vegetation and mull during previous geochemical testing. The trees sampled were lodgepole pine (Pinus contorta), Engelmann spruce (Picea engelmannii) and Douglas fir (Pseudotsuga menziesii). The condensed exudates were passed through No. 40 Whatman filters, and through 5-micron, 0.45-micron, and 0.05-micron average-pore-diameter membrane filters, evaporated to dryness, and each residue was ashed and analyzed by a semiquantitative spectrographic method. The ashed residues of the exudates contain lithium, beryllium, boron, sodium, magnesium, titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, gallium, arsenic, strontium, yttrium, zirconium, molybdenum, silver, lead, bismuth, cadmium, tin, antimony, barium, and lanthanum. The presence of these elements suggests that volatile exudates from vegetation are a medium for the transport of elements in the biogeochemical cycle in subalpine environments. Thus, air sampling and analysis of aerosols derived from volatile exudates may be a useful tool in geochemical exploration. ?? 1974.

Targeted nanoparticles for enhanced X-ray radiation killing of multidrug-resistant bacteria.

PubMed

Luo, Yang; Hossain, Mainul; Wang, Chaoming; Qiao, Yong; An, Jincui; Ma, Liyuan; Su, Ming

2013-01-21

This paper describes a nanoparticle enhanced X-ray irradiation based strategy that can be used to kill multidrug resistant (MDR) bacteria. In the proof-of-concept experiment using MDR Pseudomonas aeruginosa (P. aeruginosa) as an example, polyclonal antibody modified bismuth nanoparticles are introduced into bacterial culture to specifically target P. aeruginosa. After washing off uncombined bismuth nanoparticles, the bacteria are irradiated with X-rays, using a setup that mimics a deeply buried wound in humans. Results show that up to 90% of MDR P. aeruginosa are killed in the presence of 200 μg ml(-1) bismuth nanoparticles, whereas only ∼6% are killed in the absence of bismuth nanoparticles when exposed to 40 kVp X-rays for 10 min. The 200 μg ml(-1) bismuth nanoparticles enhance localized X-ray dose by 35 times higher than the control with no nanoparticles. In addition, no significant harmful effects on human cells (HeLa and MG-63 cells) have been observed with 200 μg ml(-1) bismuth nanoparticles and 10 min 40 kVp X-ray irradiation exposures, rendering the potential for future clinical use. Since X-rays can easily penetrate human tissues, this bactericidal strategy has the potential to be used in effectively killing deeply buried MDR bacteria in vivo.

CONCENTRATION AND DECONTAMINATION OF SOLUTIONS CONTAINING PLUTONIUM VALUES BY BISMUTH PHOSPHATE CARRIER PRECIPITATION METHODS

DOEpatents

Seaborg, G.T.; Thompson, S.G.

1960-08-23

A process is given for isolating plutonium present in the tetravalent state in an aqueous solution together with fission products. First, the plutonium and fission products are coprecipitated on a bismuth phosphate carrier. The precipitate obtained is dissolved, and the plutonium in the solution is oxidized to the hexavalent state (with ceric nitrate, potassium dichromate, Pb/ sub 3/O/sub 4/, sodium bismuthate and/or potassium dichromate). Thereafter a carrier for fission products is added (bismuth phosphate, lanthanum fluoride, ceric phosphate, bismuth oxalate, thorium iodate, or thorium oxalate), and the fission-product precipitation can be repeated with one other of these carriers. After removal of the fission-product-containing precipitate or precipitates. the plutonium in the supernatant is reduced to the tetravalent state (with sulfur dioxide, hydrogen peroxide. or sodium nitrate), and a carrier for tetravalent plutonium is added (lanthanum fluoride, lanthanum hydroxide, lanthanum phosphate, ceric phosphate, thorium iodate, thorium oxalate, bismuth oxalate, or niobium pentoxide). The plutonium-containing precipitate is then dissolved in a relatively small volume of liquid so as to obtain a concentrated solution. Prior to dissolution, the bismuth phosphate precipitates first formed can be metathesized with a mixture of sodium hydroxide and potassium carbonate and plutonium-containing lanthanum fluorides with alkali-metal hydroxide. In the solutions formed from a plutonium-containing lanthanum fluoride carrier the plutonium can be selectively precipitated with a peroxide after the pH was adjusted preferably to a value of between 1 and 2. Various combinations of second, third, and fourth carriers are discussed.

Assessment of color stability of white mineral trioxide aggregate angelus and bismuth oxide in contact with tooth structure.

PubMed

Marciano, Marina Angélica; Costa, Reginaldo Mendonça; Camilleri, Josette; Mondelli, Rafael Francisco Lia; Guimarães, Bruno Martini; Duarte, Marco Antonio Hungaro

2014-08-01

Dental discoloration with use of materials containing bismuth oxide has been reported. It is postulated that the discoloration is a result of chemical interaction of bismuth oxide with dentin. The aim of the study was to analyze dental color alteration and the chemical interaction of bismuth oxide with the main components present in composite (methacrylate) and in dentin (collagen). Fifty bovine teeth were prepared and filled with white mineral trioxide aggregate (MTA) Angelus, Portland cement (PC) with 20% zirconium oxide, or PC with 20% calcium tungstate and then sealed with composite. Triple antibiotic paste and unfilled samples were the positive and negative controls, respectively. The specimens were stored in separate flasks immersed in tap water at 37°C with ambient light blocked out. The color assessment was performed with a spectrophotometer at different intervals, namely before filling and 24 hours, 15 days, and 30 days after filling. The color change and the luminosity were calculated. The statistical analysis was performed by using nonparametric Kruskal-Wallis and Dunn tests (P < .05). The interaction of the bismuth oxide, zirconium oxide, and calcium tungstate with collagen and methacrylate was assessed by placing the materials in contact, followed by color assessment. The analysis of color change values showed that all the materials presented color alteration after the evaluated periods. Statistically higher luminosity was verified for PC/20% zirconium oxide in comparison with white MTA Angelus (P < .05). The teeth filled with white MTA Angelus demonstrated a grayish discoloration with evident dentin staining. Bismuth oxide exhibited a color change when in contact with collagen. The color of white MTA Angelus was altered in contact with dental structures. Collagen, which is present in dentin matrix, reacted with bismuth oxide, resulting in a grayish discoloration. The use of an alternative radiopacifier to replace bismuth in white MTA is indicated. Copyright © 2014 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

Boiling water neutronic reactor incorporating a process inherent safety design

DOEpatents

Forsberg, Charles W.

1987-01-01

A boiling-water reactor core is positioned within a prestressed concrete reactor vessel of a size which will hold a supply of coolant water sufficient to submerge and cool the reactor core by boiling for a period of at least one week after shutdown. Separate volumes of hot, clean (non-borated) water for cooling during normal operation and cool highly borated water for emergency cooling and reactor shutdown are separated by an insulated wall during normal reactor operation with contact between the two water volumes being maintained at interfaces near the top and bottom ends of the reactor vessel. Means are provided for balancing the pressure of the two volumes at the lower interface zone during normal operation to prevent entry of the cool borated water into the reactor core region, for detecting the onset of excessive power to coolant flow conditions in the reactor core and for detecting low water levels of reactor coolant. Cool borated water is permitted to flow into the reactor core when low reactor coolant levels or excessive power to coolant flow conditions are encountered.

Preparation and characterization of magnesium borate for special glass

NASA Astrophysics Data System (ADS)

Dou, Lishuang; Zhong, Jianchu; Wang, Hongzhi

2010-05-01

Magnesium borate with a variety of B2O3/MgO molar ratios, which can be applied for special glass, has been prepared through the reaction of light-burned magnesia with boric acid by a hydrothermal method. The effects of the B2O3/MgO molar ratio of raw materials, reaction time, temperature and liquid to solid ratio (ml g-1) on the synthetic product are investigated. The XRD and TG-DTG analyses indicate that the prepared magnesium borate is a mixture of magnesium hexaborate hydrate and ascharite. The results show that high B2O3/MgO molar ratios of raw materials and low reaction liquid-solid ratios favour the product with a high B2O3/MgO molar ratio and vice versa. There exists free MgO in the product when the reaction temperature is below 140 °C or the reaction time is not enough, because of the incomplete reaction of magnesium oxide with boric acid. The process of fractional crystallization for the magnesium borate mixture is also discussed.

Advanced shield development for a fission surface power system for the lunar surface

DOE Office of Scientific and Technical Information (OSTI.GOV)

A. E. Craft; I. J. Silver; C. M. Clark

A nuclear reactor power system such as the affordable fission surface power system enables a potential outpostonthemoon.Aradiation shieldmustbe included in the reactor system to reduce the otherwise excessive dose to the astronauts and other vital system components. The radiation shield is typically the most massive component of a space reactor system, and thus must be optimized to reduce mass asmuchas possible while still providing the required protection.Various shield options for an on-lander reactor system are examined for outpost distances of 400m and 1 kmfromthe reactor. Also investigated is the resulting mass savings from the use of a high performance cermetmore » fuel. A thermal analysis is performed to determine the thermal behaviours of radiation shields using borated water. For an outpost located 1000m from the core, a tetramethylammonium borohydride shield is the lightest (5148.4 kg), followed by a trilayer shield (boron carbide–tungsten–borated water; 5832.3 kg), and finally a borated water shield (6020.7 kg). In all of the final design cases, the temperature of the borated water remains below 400 K.« less

Silica-Based and Borate-Based, Titania-Containing Bioactive Coatings Characterization: Critical Strain Energy Release Rate, Residual Stresses, Hardness, and Thermal Expansion.

PubMed

Rodriguez, Omar; Matinmanesh, Ali; Phull, Sunjeev; Schemitsch, Emil H; Zalzal, Paul; Clarkin, Owen M; Papini, Marcello; Towler, Mark R

2016-12-01

Silica-based and borate-based glass series, with increasing amounts of TiO₂ incorporated, are characterized in terms of their mechanical properties relevant to their use as metallic coating materials. It is observed that borate-based glasses exhibit CTE (Coefficient of Thermal Expansion) closer to the substrate's (Ti6Al4V) CTE, translating into higher mode I critical strain energy release rates of glasses and compressive residual stresses and strains at the coating/substrate interface, outperforming the silica-based glasses counterparts. An increase in the content of TiO₂ in the glasses results in an increase in the mode I critical strain energy release rate for both the bulk glass and for the coating/substrate system, proving that the addition of TiO₂ to the glass structure enhances its toughness, while decreasing its bulk hardness. Borate-based glass BRT3, with 15 mol % TiO₂ incorporated, exhibits superior properties overall compared to the other proposed glasses in this work, as well as 45S5 Bioglass ® and Pyrex.

Silica-Based and Borate-Based, Titania-Containing Bioactive Coatings Characterization: Critical Strain Energy Release Rate, Residual Stresses, Hardness, and Thermal Expansion

PubMed Central

Rodriguez, Omar; Matinmanesh, Ali; Phull, Sunjeev; Schemitsch, Emil H.; Zalzal, Paul; Clarkin, Owen M.; Papini, Marcello; Towler, Mark R.

2016-01-01

Silica-based and borate-based glass series, with increasing amounts of TiO2 incorporated, are characterized in terms of their mechanical properties relevant to their use as metallic coating materials. It is observed that borate-based glasses exhibit CTE (Coefficient of Thermal Expansion) closer to the substrate’s (Ti6Al4V) CTE, translating into higher mode I critical strain energy release rates of glasses and compressive residual stresses and strains at the coating/substrate interface, outperforming the silica-based glasses counterparts. An increase in the content of TiO2 in the glasses results in an increase in the mode I critical strain energy release rate for both the bulk glass and for the coating/substrate system, proving that the addition of TiO2 to the glass structure enhances its toughness, while decreasing its bulk hardness. Borate-based glass BRT3, with 15 mol % TiO2 incorporated, exhibits superior properties overall compared to the other proposed glasses in this work, as well as 45S5 Bioglass® and Pyrex. PMID:27916951

A comparative study of Si-containing electrolyte additives for lithium ion battery: Which one is better and why is it better

NASA Astrophysics Data System (ADS)

Wang, Kang; Xing, Lidan; Zhu, Yunmin; Zheng, Xiongwen; Cai, Dandan; Li, Weishan

2017-02-01

Influence of two Si-containing electrolyte additives, tris(trimethylsilyl)borate (TMSB) and tris(trimethylsilyl)phosphate (TMSP), on the cyclic stability of high voltage LiNi0.5Mn1.5O4 electrode has been systematically studied in this work. The capacity retention of LiNi0.5Mn1.5O4 cycling in STD (1M LiPF6/EC: EMC = 3:7), TMSB- and TMSP-containing electrolytes is 23%, 85% and 71% after 600 cycles at 1C rate, respectively, revealing that the ability of TMSB on improving the cyclic performance of LiNi0.5Mn1.5O4 is superior to that of TMSP. Experimental and theoretical characterizations show that the preferential reaction of both TMSB and TMSP generates thin and uniform film on LiNi0.5Mn1.5O4 surface, which effectively suppress the continuous oxidation reaction of electrolyte. While the film generated from TMSB, which contains B and Si-rich compounds, shows better ability on restraining the growth of interfacial resistance during cycling, resulting in better cyclic stability of LiNi0.5Mn1.5O4 than that of TMSP.

Observation of a different birefringence order at optical and THz frequencies in LBO crystal

NASA Astrophysics Data System (ADS)

Andreev, Yu. M.; Kokh, A. E.; Kokh, K. A.; Lanskii, G. V.; Litvinenko, K.; Mamrashev, A. A.; Molloy, J. F.; Murdin, B.; Naftaly, M.; Nikolaev, N. A.; Svetlichnyi, V. A.

2017-04-01

THz optical properties of lithium borate (LBO) crystals were measured using time-domain spectroscopy (TDS). The LBO crystal samples were of high optical quality and were cut and polished along the 〈100〉, 〈010〉 and 〈001〉 axes. Two independent measurements were performed in order to confirm the reproducibility and consistency of results. The contradictions in the previously published data on the THz optical properties of LBO were clarified. It was shown that the birefringence order at THz frequencies is nz

Effects of TiO2 and ZrO2 nanofillers in LiBOB based PVdF/PVC composite polymer electrolytes (CPE)

NASA Astrophysics Data System (ADS)

Aravindan, V.; Vickraman, P.

2007-11-01

A novel type of lithium bis(oxalato)borate (LiBOB) synthesized by the solid-state reaction method has been presented. LiBOB composite polymer electrolytes (CPE) prepared with dispersions of TIO2/ZrO2with various concentrations into the host blend matrices of poly(vinylidenefluoride) (PVdF)-poly(vinylchloride) (PVC) are investigated by scanning electron microscopy, x-ray diffraction (XRD) and ac impedance measurements. The plasticizing agent selected for the present study is a mixture of ethylene carbonate (EC) and diethyl carbonate (DEC) for the phase separated morphology of the studied polymers. The impedance studies on CPE membranes identify that membranes, with 2.5 wt% of fillers, have enhanced conductivities of 5.43 × 10-4 S cm-1 and 4.38 × 10-4 S cm-1, respectively, for TiO2 and ZrO2 at ambient temperature. The XRD investigations confirm that the membranes with filler levels exceeding the limit of 2.5 wt% show a gradual increase in the degree of crystallinity, rendering them less conducting. The activation energy calculations also highlight variations in conductivities of all the membranes.

Dosimetric characteristics of LKB:Cu,P solid TL detector

NASA Astrophysics Data System (ADS)

Hashim, S.; Alajerami, Y. S. M.; Ghoshal, S. K.; Saleh, M. A.; Saripan, M. I.; Kadir, A. B. A.; Bradley, D. A.; Alzimami, K.

2014-11-01

The dosimetric characteristics of newly developed borate glass dosimeter modified with lithium and potassium carbonate (LKB) and co-doped with CuO and NH4H2PO4 are reported. Broad peaks in the absence of any sharp peak confirms the amorphous nature of the prepared glass. A simple glow curve of Cu doped sample is observed with a single prominent peak (Tm) at 220 °C. The TL intensity response shows an enhancement of ~100 times due to the addition of CuO (0.1 mol%) to LKB compound. A further enhancement of the intensity by a factor of 3 from the addition of 0.25 mol% NH4H2PO4 as a co-dopant impurity is attributed to the creation of extra electron traps with consequent increase in energy transfer of radiation recombination centers. The TL yield performance of LKB:Cu,P with Zeff ≈8.92 is approximately seventeen times less sensitive compared to LiF:Mg,Ti (TLD-100). The proposed dosimeter shows good linearity up to 103 Gy, minimal fading and photon energy independence. These attractive features offered by our dosimeter is expected to pave the way towards dosimetric applications.

Reactivity of cyclopentadienyl transition metal(ii) complexes with borate ligands: structural characterization of the toluene-activated molybdenum complex [Cp*Mo(CO)2(η3-CH2C6H5)].

PubMed

Ramalakshmi, Rongala; Maheswari, K; Sharmila, Dudekula; Paul, Anamika; Roisnel, Thierry; Halet, Jean-François; Ghosh, Sundargopal

2016-10-18

Reactions of cyclopentadienyl transition-metal halide complexes [Cp*Mo(CO) 3 Cl], 1, and [CpFe(CO) 2 I], 2, (Cp = C 5 H 5 ; Cp* = η 5 -C 5 Me 5 ) with borate ligands are reported. Treatment of 1 with [NaBt 2 ] (Bt 2 = dihydrobis(2-mercapto-benzothiazolyl)borate) in toluene yielded [Cp*Mo(CO) 2 (C 7 H 4 S 2 N)], 3, and [Cp*Mo(CO) 2 (η 3 -CH 2 C 6 H 5 )], 4, with a selective binding of toluene through C-H activation followed by orthometallation. Note that compound 4 is a structurally characterized toluene-activated molecule in which the metal is in η 3 -coordination mode. Under similar reaction conditions, [NaPy 2 ] (Py 2 = dihydrobis(2-mercaptopyridyl)borate) produced only the mercaptopyridyl molybdenum complex [Cp*Mo(CO) 2 (C 5 H 4 SN)], 5, in good yield. On the other hand, when compound 2 was treated individually with [NaBt] (Bt = trihydro(2-mercapto-benzothiazolyl)borate) and [NaPy 2 ] in THF, formation of the η 1 -coordinated complexes [CpFe(CO) 2 (C 7 H 4 S 2 N)], 6, and [CpFe(CO) 2 (C 5 H 4 SN)], 7, was observed. The solid-state molecular structures of compounds 3, 4, 6, and 7 have been established by single-crystal X-ray crystallographic analyses.

Comparative study of A-site order in the lead-free bismuth titanates M{sub 1/2}Bi{sub 1/2}TiO{sub 3} (M=Li, Na, K, Rb, Cs, Ag, Tl) from first-principles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gröting, Melanie, E-mail: groeting@mm.tu-darmstadt.de; Albe, Karsten, E-mail: albe@mm.tu-darmstadt.de

2014-05-01

We investigate the possibility of enhancing chemical order in the relaxor ferroelectric Na{sub 1/2}Bi{sub 1/2}TiO{sub 3} upon substitution of Na{sup +} by other monovalent cations M{sup +} using total energy calculations based on density functional theory. All chemically available monovalent cations M{sup +}, which are Li, Na, Ag, K, Tl, Rb and Cs, are considered and an analysis of the structurally relaxed structures in terms of symmetry-adapted distortion modes is given in order to quantify the chemically induced structural distortions. We demonstrate that the replacement of Na{sup +} by other monovalent cations can hardly alter the tendency of chemical ordermore » with respect to Na{sub 1/2}Bi{sub 1/2}TiO{sub 3}. Only Tl{sub 1/2}Bi{sub 1/2}TiO{sub 3} and Ag{sub 1/2}Bi{sub 1/2}TiO{sub 3} show enhanced tendency for chemical ordering. Both heavy metals behave similar to the light alkali metals in terms of structural relaxations and relative stabilities of the ordered configurations. Although a comparison of the Goldschmidt factors of components (M TiO{sub 3}){sup −} reveals for Tl a value above the upper stability limit for perovskites, the additional lone-pair effect of Tl{sup +} stabilizes the ordered structure. - Graphical abstract: Amplitudes of chemically induced distortion modes in different ordered perovskites M{sub 1/2}Bi{sub 1/2}TiO{sub 3} and visualisation of atomic displacements associated with distortion mode X{sup +}{sub 1} in the 001-ordered compounds Li{sub 1/2}Bi{sub 1/2}TiO{sub 3} and Cs{sub 1/2}Bi{sub 1/2}TiO{sub 3}. Due to a substantial size mismatch between bismuth (green) and caesium (dark blue), incorporation of the latter leads to enhanced displacements of oxygen atoms (red) and suppresses displacements of titanium (silver) as compared to lithium (light blue) or other smaller monovalent cations. - Highlights: • Lead-free A-site mixed bismuth titanates M{sub 1/2}Bi{sub 1/2}TiO{sub 3} are studied by first-principles calculations. • Investigation of chemical ordering tendency for M=Li, Na, K, Rb, Cs, Ag, and Tl. • Group theoretical analysis of different ordered structures. • Ag and Tl compounds are the most promising candidates for study of chemical order dependent ferroelectric properties.« less

Acute Esophageal Necrosis: A Case of Black Esophagus Associated with Bismuth Subsalicylate Ingestion

PubMed Central

Mankal, Pavan; Judeh, Hani; Kim, Sang

2014-01-01

We present a case of acute esophageal necrosis (AEN) likely caused by chronic use of bismuth subsalicylate, an active ingredient in over-the-counter Pepto-Bismol®, which contains 220 g of salicylic acid in each 30 mL quantity. While aspirin is known to cause gastritis and gastric ulcers, this is the first case, to our knowledge, reporting AEN after chronic bismuth subsalicylate use. PMID:26157851

URANIUM BISMUTHIDE DISPERSION IN MOLTEN METAL

DOEpatents

Teitel, R.J.

1959-10-27

The formation of intermetallic bismuth compounds of thorium or uranium dispersed in a liquid media containing bismuth and lead is described. A bismuthide of uranium dispersed in a liquid metal medium is formed by dissolving uranium in composition of lead and bismuth containing less than 80% lead and lowering the temperature of the composition to a temperature below the point at which the solubility of uranium is exceeded and above the melting point of the composition.

PURIFICATION OF PLUTONIUM USING A CERIUM PRECIPITATE AS A CARRIER FOR FISSION PRODUCTS

DOEpatents

Faris, B.F.; Olson, C.M.

1961-07-01

Bismuth phosphate carrier precipitation processes are described for the separation of plutonium from fission products wherein in at least one step bismuth phosphate is precipitated in the presence of hexavalent plutonium thereby carrying a portion of the fission products from soluble plu tonium values. In this step, a cerium phosphate precipitate is formed in conjunction with the bismuth phosphate precipitate, thereby increasing the amount of fission products removed from solution.

Bismuth interstitial impurities and the optical properties of GaP 1- x - yBi xN y

DOE Office of Scientific and Technical Information (OSTI.GOV)

Christian, Theresa M.; Beaton, Daniel A.; Perkins, John D.

Two distinctive regimes of behavior are observed from GaP 1-x-y Bi x N y alloys with x < 2.4%, y < 3.4% grown by molecular beam epitaxy. These regimes are correlated with abundant bismuth interstitial impurities that are encouraged or suppressed according to the sample growth temperature, with up to 55% of incorporated bismuth located interstitially. When bismuth interstitials are present, radiative recombination arises at near-band-edge localized states rather than from impurity bands and deep state luminescence. Finally, this change demonstrates a novel strategy for controlling luminescence in isoelectronic semiconductor alloys and is attributed to a disruption of carrier transfermore » processes.« less

Preparation of bismuth titanate/calcium alginate composite bead and its photocatalytic degradation of dye pollutants

NASA Astrophysics Data System (ADS)

Gan, Huihui; Dong, Nanyang; Lu, Linxiao; Fu, Yan; Zhang, Huining; Qian, Yongxin; Zhang, Kefeng; Jin, Huixia

2017-08-01

In this study, the bismuth titanate/calcium alginate composite bead was synthesized by immobilizing bismuth titanate Bi4Ti3O12 particles into 1.5% sodium alginate (SA) matrix. The Bi4Ti3O12 particles were characterized by X-ray diffraction (XRD). The photocatalytic activity for the degradation of dye Rhodamine B in solution by as-prepared bismuth titanate/calcium alginate composite bead was investigated. The as-prepared composite beads CA/BTO-700 exhibited best photocatalytic efficiency for the degradation of RhB compared with CA/BTO-800 and CA/BTO-900 under simulated solar light. After 4 cycles in photocatalytic degradation of RhB, the degradation rate of the CA/BTO-700 nearly remained unchanged.

Bismuth interstitial impurities and the optical properties of GaP 1- x - yBi xN y

DOE PAGES

Christian, Theresa M.; Beaton, Daniel A.; Perkins, John D.; ...

2017-10-10

Two distinctive regimes of behavior are observed from GaP 1-x-y Bi x N y alloys with x < 2.4%, y < 3.4% grown by molecular beam epitaxy. These regimes are correlated with abundant bismuth interstitial impurities that are encouraged or suppressed according to the sample growth temperature, with up to 55% of incorporated bismuth located interstitially. When bismuth interstitials are present, radiative recombination arises at near-band-edge localized states rather than from impurity bands and deep state luminescence. Finally, this change demonstrates a novel strategy for controlling luminescence in isoelectronic semiconductor alloys and is attributed to a disruption of carrier transfermore » processes.« less

Relationship between Eu{sup 3+} reduction and glass polymeric structure in Al{sub 2}O{sub 3}-modified borate glasses under air atmosphere

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jiao, Qing; Yu, Xue; Xu, Xuhui

2013-06-15

The reduction of Eu{sup 3+} to Eu{sup 2+} is realized efficiently in Eu{sub 2}O{sub 3}-doped borate glasses prepared under air condition by melting-quenching method. Luminescent spectra show an increasing tendency of Eu{sup 2+} emission with increasing Al{sub 2}O{sub 3} concentration in B{sub 2}O{sub 3}–Na{sub 2}O glasses. It is interesting that significant enhancement appeared of Eu{sup 2+} luminescence in the Al{sub 2}O{sub 3}-rich sample comparing to the samples of Al{sub 2}O{sub 3} less than 6 mol%. FTIR and Raman scattering measurements indicated that some new vibration modes assigned to the low-polymerized structure groups decomposed from the slight Al{sub 2}O{sub 3} dopantmore » samples. These results demonstrated that the polymerization of the glass structure decreased with increasing incorporation of Al{sub 2}O{sub 3} into the borate glasses, linking to the efficiency of Eu{sup 3+} self-reduction in air at high temperature. - graphical abstract: A novel europium valence reduction phenomenon occurred in Al{sub 2}O{sub 3} modified borate glasses, FTIR and Raman measurements revealed that high polymeric groups were destroyed to low polymery structures with Al{sub 2}O{sub 3} addition. - Highlights: • The efficient reduction of Eu{sup 3+} to Eu{sup 2+} is observed in the B{sub 2}O{sub 3}–Na{sub 2}O glasses. • Eu{sup 2+} luminescence is significant enhanced in the Al{sub 2}O{sub 3}-rich glasses. • The introduction of Al{sub 2}O{sub 3} changed the network structure of the borate glasses. • High polymeric borate groups in the glass matrix may be destroyed to the lower ones.« less

Borate cross-linked graphene oxide-chitosan as robust and high gas barrier films

NASA Astrophysics Data System (ADS)

Yan, Ning; Capezzuto, Filomena; Lavorgna, Marino; Buonocore, Giovanna G.; Tescione, Fabiana; Xia, Hesheng; Ambrosio, Luigi

2016-05-01

Chitosan (CS) is one of the most promising polymers due to its biocompatibility, biodegradability, and natural abundance. However, its poor mechanical and barrier properties make it difficult to satisfy a wide range of applications. Herein, borate ions, originating from the hydrolysis of sodium tetraborate decahydrate (borax), have been used to crosslink chitosan and graphene oxide (GO) nanocomposites. Chitosan films consisting of 1.0 wt% boron and 1.0 wt% GO exhibit a significant improvement in both the toughness and oxygen barrier properties compared to pristine chitosan. In particular the tensile strength of the samples after thermal treatment increases by ~160% compared to pristine chitosan, whereas their oxygen permeability reduces by ~90%. This is ascribed to the chemical crosslinking between chitosan and GO nanoplatelets through borate ions, as well as the formation of a layered morphology with graphene nanoplatelets oriented parallel to the sample surface. The exceptional robust and high gas barrier film has promising application in the packaging industry. The borate-crosslinking chemistry represents the potential strategy for improving properties of other polymer nanocomposites.Chitosan (CS) is one of the most promising polymers due to its biocompatibility, biodegradability, and natural abundance. However, its poor mechanical and barrier properties make it difficult to satisfy a wide range of applications. Herein, borate ions, originating from the hydrolysis of sodium tetraborate decahydrate (borax), have been used to crosslink chitosan and graphene oxide (GO) nanocomposites. Chitosan films consisting of 1.0 wt% boron and 1.0 wt% GO exhibit a significant improvement in both the toughness and oxygen barrier properties compared to pristine chitosan. In particular the tensile strength of the samples after thermal treatment increases by ~160% compared to pristine chitosan, whereas their oxygen permeability reduces by ~90%. This is ascribed to the chemical crosslinking between chitosan and GO nanoplatelets through borate ions, as well as the formation of a layered morphology with graphene nanoplatelets oriented parallel to the sample surface. The exceptional robust and high gas barrier film has promising application in the packaging industry. The borate-crosslinking chemistry represents the potential strategy for improving properties of other polymer nanocomposites. Electronic supplementary information (ESI) available: Detailed characterization methods and survey XPS spectra. See DOI: 10.1039/c6nr00377j

Bismuth-based electrochemical stripping analysis

DOEpatents

Wang, Joseph

2004-01-27

Method and apparatus for trace metal detection and analysis using bismuth-coated electrodes and electrochemical stripping analysis. Both anodic stripping voltammetry and adsorptive stripping analysis may be employed.

Bismuth Nephrotoxicity: Report of a Case

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gryboski, Joyce D.; Gotoff, Samuel P.

1961-12-28

A case of renal poisoning by bismuth thioglycolate is reported which demonstrates the nephrotoxicity of bismuth compounds in the pediatric age group. For treatment of warts the patient received a relatively small amount of bismuth thioglycollate (1.3 mg/kg body wt), and although the symptomatology was mild, the degree of azotemia was severe. Evidence of both tubular and glomerular damage was present, the former reflected by fixed urinary specific gravity and minimal glycosuria in the presence of a normal blood sugar, and the latter by azotemia and mild proteinuria. Backward diffusion of creatinine through damaged tubular epithelium probably contributed to themore » observed elevated plasma creatinine value, and the presence of a high anion content of serum probably represented retained phosphate, sulfate, and organic acids. The observed maculopapular rash probably corresponded to the socalled erythema of the ninth day, described previously as a rare manifestation of bismuth toxicity. The therapy employed was that for acute renal failure, but chelating agents, which are potential nephrotoxins, were not employed because of the known rapid excretion of bismuth thioglycollate. Rehydration was carried out, and electrolyte and protein intake was limited until diuresis was well established and the blood urea nitrogen had begun to fall. To avoid hyperkalemia, potassium restriction was carried out. Normal renal function was restored within a month after the onset of renal injury. It is suggested that the degree of sensitivity to the metal was related to the age of the patient and to the structural maturity of the kidney, for all cases of bismuth nephropathy reported the past 15 yr have occurred in the pediatric age group, children less than 3 yr being the most severely affected.« less

Bismuth Passivation Technique for High-Resolution X-Ray Detectors

NASA Technical Reports Server (NTRS)

Chervenak, James; Hess, Larry

2013-01-01

The Athena-plus team requires X-ray sensors with energy resolution of better than one part in 3,000 at 6 keV X-rays. While bismuth is an excellent material for high X-ray stopping power and low heat capacity (for large signal when an X-ray is stopped by the absorber), oxidation of the bismuth surface can lead to electron traps and other effects that degrade the energy resolution. Bismuth oxide reduction and nitride passivation techniques analogous to those used in indium passivation are being applied in a new technique. The technique will enable improved energy resolution and resistance to aging in bismuth-absorber-coupled X-ray sensors. Elemental bismuth is lithographically integrated into X-ray detector circuits. It encounters several steps where the Bi oxidizes. The technology discussed here will remove oxide from the surface of the Bi and replace it with nitridized surface. Removal of the native oxide and passivating to prevent the growth of the oxide will improve detector performance and insulate the detector against future degradation from oxide growth. Placing the Bi coated sensor in a vacuum system, a reduction chemistry in a plasma (nitrogen/hydrogen (N2/H2) + argon) is used to remove the oxide and promote nitridization of the cleaned Bi surface. Once passivated, the Bi will perform as a better X-ray thermalizer since energy will not be trapped in the bismuth oxides on the surface. A simple additional step, which can be added at various stages of the current fabrication process, can then be applied to encapsulate the Bi film. After plasma passivation, the Bi can be capped with a non-diffusive layer of metal or dielectric. A non-superconducting layer is required such as tungsten or tungsten nitride (WNx).

Liquid Bismuth Feed System for Electric Propulsion

NASA Technical Reports Server (NTRS)

Markusic, T. E.; Polzin, K. A.; Stanojev, B. J.

2006-01-01

Operation of Hall thrusters with bismuth propellant has been shown to be a promising path toward high-power, high-performance, long-lifetime electric propulsion for spaceflight missions. For example, the VHITAL project aims td accurately, experimentally assess the performance characteristics of 10 kW-class bismuth-fed Hall thrusters - in order to validate earlier results and resuscitate a promising technology that has been relatively dormant for about two decades. A critical element of these tests will be the precise metering of propellant to the thruster, since performance cannot be accurately assessed without an accurate accounting of mass flow rate. Earlier work used a pre/post-test propellant weighing scheme that did not provide any real-time measurement of mass flow rate while the thruster was firing, and makes subsequent performance calculations difficult. The motivation of the present work was to develop a precision liquid bismuth Propellant Management System (PMS) that provides real-time propellant mass flow rate measurement and control, enabling accurate thruster performance measurements. Additionally, our approach emphasizes the development of new liquid metal flow control components and, hence, will establish a basis for the future development of components for application in spaceflight. The design of various critical components in a bismuth PMS are described - reservoir, electromagnetic pump, hotspot flow sensor, and automated control system. Particular emphasis is given to material selection and high-temperature sealing techniques. Open loop calibration test results are reported, which validate the systems capability to deliver bismuth at mass flow rates ranging from 10 to 100 mg/sec with an uncertainty of less than +/- 5%. Results of integrated vaporizer/liquid PMS tests demonstrate all of the necessary elements of a complete bismuth feed system for electric propulsion.

Dual-modality, fluorescent, PLGA encapsulated bismuth nanoparticles for molecular and cellular fluorescence imaging and computed tomography.

PubMed

Swy, Eric R; Schwartz-Duval, Aaron S; Shuboni, Dorela D; Latourette, Matthew T; Mallet, Christiane L; Parys, Maciej; Cormode, David P; Shapiro, Erik M

2014-11-07

Reports of molecular and cellular imaging using computed tomography (CT) are rapidly increasing. Many of these reports use gold nanoparticles. Bismuth has similar CT contrast properties to gold while being approximately 1000-fold less expensive. Herein we report the design, fabrication, characterization, and CT and fluorescence imaging properties of a novel, dual modality, fluorescent, polymer encapsulated bismuth nanoparticle construct for computed tomography and fluorescence imaging. We also report on cellular internalization and preliminary in vitro and in vivo toxicity effects of these constructs. 40 nm bismuth(0) nanocrystals were synthesized and encapsulated within 120 nm Poly(dl-lactic-co-glycolic acid) (PLGA) nanoparticles by oil-in-water emulsion methodologies. Coumarin-6 was co-encapsulated to impart fluorescence. High encapsulation efficiency was achieved ∼70% bismuth w/w. Particles were shown to internalize within cells following incubation in culture. Bismuth nanocrystals and PLGA encapsulated bismuth nanoparticles exhibited >90% and >70% degradation, respectively, within 24 hours in acidic, lysosomal environment mimicking media and both remained nearly 100% stable in cytosolic/extracellular fluid mimicking media. μCT and clinical CT imaging was performed at multiple X-ray tube voltages to measure concentration dependent attenuation rates as well as to establish the ability to detect the nanoparticles in an ex vivo biological sample. Dual fluorescence and CT imaging is demonstrated as well. In vivo toxicity studies in rats revealed neither clinically apparent side effects nor major alterations in serum chemistry and hematology parameters. Calculations on minimal detection requirements for in vivo targeted imaging using these nanoparticles are presented. Indeed, our results indicate that these nanoparticles may serve as a platform for sensitive and specific targeted molecular CT and fluorescence imaging.

Spectroscopic properties of some borate glasses containg uranium

NASA Astrophysics Data System (ADS)

Culea, E.; Milea, I.; Bratu, I.

1993-03-01

Spectroscopic properties of some borate glasses containing 1-5%UO 3 have been studied in the fields of 700-1200 cm -1 and 10,000-30,000 cm -1 Absorption bands specific for U 6+ and U 4+ ions were observed. The increase of the melting time produces the reduction of U 6+ ions to U 4+.

CADMIUM-RARE EARTH BORATE GLASS AS REACTOR CONTROL MATERIAL

DOEpatents

Ploetz, G.L.; Ray, W.E.

1958-11-01

A reactor control rod fabricated from a cadmiumrare earth-borate glass is presented. The rare earth component of this glass is selected from among those rare earths having large neutron capture cross sections, such as samarium, gadolinium or europium. Partlcles of this glass are then dispersed in a metal matrix by standard powder metallurgy techniques.

N-Alkyl-N-methylpyrrolidinium Difluoro(oxalato)borate Ionic Liquids: Physical/Electrochemical Properties and Al Corrosion

DTIC Science & Technology

2013-01-01

U.S. Army Research Laboratory, Adelphi, MD 20783, USA The synthesis and physical properties of difluoro(oxalato) borate (DFOB-)-based ionic...have a melting point (Tm) of -5°C and 31°C, respectively, whereas the PY15DFOB salt does not crystallize. Instead, this salt has a glass transition

Infrared-to-visible conversion luminescence of Er 3+ ions in lead borate transparent glass-ceramics

NASA Astrophysics Data System (ADS)

Pisarski, Wojciech A.; Pisarska, Joanna; Lisiecki, Radosław; Grobelny, Łukasz; Dominiak-Dzik, Grażyna; Ryba-Romanowski, Witold

2009-10-01

Transparent glass-ceramics were successfully prepared during controlled heat treatment of lead borate glasses. The PbF 2 particles were dispersed into a borate glass matrix which was evidenced by X-ray diffraction analysis. The phase identification revealed that crystalline peaks can be related to the orthorhombic PbF 2 phase. Green up-conversion luminescence due to the 4S 3/2- 4I 15/2 transition of Er 3+ ions was registered. In comparison to the precursor glass the luminescence intensity was considerably higher, whereas the luminescence linewidth slightly decreased in the studied oxyfluoride transparent glass-ceramics. It indicated that a part of the trivalent erbium was incorporated into the PbF 2 crystalline phase.

Framework influence of erbium doped oxyfluoride glasses on their optical properties

NASA Astrophysics Data System (ADS)

Środa, Marcin; Cholewa-Kowalska, Katarzyna; Różański, Marek; Nocuń, Marek

2011-01-01

Glasses of different matrix (phosphate, borate, silicate and lead-silicate) were studied for their optical properties. The effect of Er dopant on transmittance and luminescence properties was presented. The significant “red shift” and “blue shift” of UV edge absorption were discussed based on the changes in the framework of the borate and phosphate glasses, respectively. It was showed that the integral intensity of the two main optical absorption transitions monotonically increases with the order: phosphate < borate < silicate < lead-silicate. Ellipsometric measurement was applied to obtain the refractive index of the glasses. The correlation between the shift of edge absorption and the change of refractive index was presented. Effect of glassy matrix on luminescence of Er3+ was discussed.

PLUTONIUM CARRIER METATHESIS WITH ORGANIC REAGENT

DOEpatents

Thompson, S.G.

1958-07-01

A method is described for converting a plutonium containing bismuth phosphate carrier precipitate Into a compositton more readily soluble in acid. The method consists of dissolving the bismuth phosphate precipitate in an aqueous solution of alkali metal hydroxide, and adding one of a certaia group of organic compounds, e.g., polyhydric alcohols or a-hydrorycarboxylic acids. The mixture is then heated causiing formation of a bismuth hydroxide precipitate containing plutonium which may be readily dissolved in nitric acid for further processing.

OPTICAL FIBRES AND FIBREOPTIC SENSORS: Bismuth-ring-doped fibres

NASA Astrophysics Data System (ADS)

Zlenko, Aleksandr S.; Akhmetshin, Ural G.; Dvoirin, Vladislav V.; Bogatyrev, Vladimir A.; Firstov, Sergei V.

2009-11-01

A new process for bismuth doping of optical fibres is proposed in which the dopant is introduced into a thin layer surrounding the fibre core. This enables bismuth stabilisation in the silica glass, with no limitations on the core composition. In particular, the GeO2 content of the fibre core in this study is 16 mol %. Spectroscopic characterisation of such fibres and optical gain measurements suggest that the proposed approach has considerable potential for laser applications.

Piezoelectric and Electrostrictive Materials for Transducer Applications. Volume 1.

DTIC Science & Technology

1988-03-01

3 Composites for Hydrophone Applications ...................... 2 2.3.1 Lead Bismuth Titanate Ferrate Compositions ................. 2 2.3.2...external variables are considered. 2.3 0:3 Composites for Hydrophone Applications 2.3.1 Lead Bismuth Titanate Ferrate Compositions the-"Following up...34" Even for doped samples however, the best results were obtained at the 50% bismuth ferrate composition. 0.. W* . - ’ w-w~-,wn~ , 7WI W W PP7W-w7WnM

Effect of bismuth doping on the structural and magnetic properties of zinc-ferrite nanoparticles prepared by a microwave combustion method

NASA Astrophysics Data System (ADS)

Shoushtari, Morteza Zargar; Emami, Akram; Ghahfarokhi, Seyed Ebrahim Mosavi

2016-12-01

In this study, we examine the bismuth doping effect on the structural, magnetic and microstructural properties of zinc-ferrite nanoparticles (ZnFe2-xBixO4 with x=0.0, 0.02, 0.04, 0.06, 0.1, 0.15) which have been prepared by a microwave combustion method. The structural, morphological and electromagnetic properties and also Curie temperature of the samples were examined by x-ray powder diffraction (XRD), field emission scanning electron microscope (FESEM), vibrating sample magnetometer (VSM), and LCR meter, respectively. In order to measure the energy band gap, the FTIR spectra of the samples were also considered. The XRD patterns of the samples revealed that all of them are ZnFe2O4 structure and no additional peak was observed in their patterns. This implied that the samples were single-phase up to bismuth solubility of 0.15 in Zinc-Ferrite. The results of XRD patterns also showed that the value lattice parameter increases with increasing the bismuth doping. The FESEM results revealed an ascending trend in the size of the nanoparticles. Also considering the VSM results characterized that an increasing the bismuth doping leads to lower the saturation magnetization. The Curie temperatures of the samples were reduced as a result of increasing the amount of bismuth.

Ranitidine bismuth citrate and ranitidine do not affect gastric emptying of a radio-labelled liquid meal.

PubMed Central

Parikh, R; Sweetland, J; Forster, E R; Bedding, A W; Farr, S J; Smith, J T

1994-01-01

Ranitidine bismuth citrate, a new chemical entity which is a salt complex of ranitidine and bismuth citrate, is being developed for the treatment of relapse of benign gastric and duodenal ulcer and eradication of Helicobacter pylori. The aim of the present study was to establish whether ranitidine bismuth citrate (800 mg) or ranitidine hydrochloride (300 mg) have any effect on gastric emptying of a liquid meal using gamma scintigraphy. On three separate occasions, each of twelve subjects received a single oral tablet of 800 mg ranitidine bismuth citrate, 300 mg ranitidine hydrochloride or placebo in random order. Thirty minutes after dosing each subject was given 375 ml of 99mTc-DTPA (diethylene triaminepentaacetic acid) labelled Clinifeed-ISO. The primary endpoint was the time to 50% gastric emptying (t50%). The proportion of the meal remaining was summarised by weighted mean proportion of the meal remaining in the stomach over 0-60 min and 0-180 min, separately. No differences were observed for t50%, weighted mean 0-60 min, and weighted mean 0-180 min between any two treatments. In man, we have detected no significant effect of single oral doses of ranitidine bismuth citrate 800 mg or ranitidine hydrochloride 300 mg on the rate of gastric emptying of a liquid meal when compared with placebo. PMID:7888296

How reliable are environmental data on 'orphan' elements? The case of bismuth concentrations in surface waters.

PubMed

Filella, Montserrat

2010-01-01

Like all elements of the periodic table, bismuth is ubiquitously distributed throughout the environment as a result of natural processes and human activities. It is present as Bi(III) in environmental, biological and geochemical samples. Although bismuth and its compounds are considered to be non-toxic to humans, its increasing use as a replacement for lead has highlighted how little is known about its environmental and ecotoxicological behaviour. In this first critical review paper on the existing information on bismuth occurrence in natural waters, 125 papers on fresh and marine waters have been collated. Although the initial objective of this study was to establish the range of the typical concentrations of total dissolved bismuth in natural waters, this proved impossible to achieve due to the wide, and hitherto unexplained, dispersion of published data. Since analytical limitations might be one of the reasons underlying value dispersion, new analytical methods published since 2000--intended to be applied to natural waters--have also been reviewed. Disappointingly, the detection limits of the bulk of them are well above those required; they are thus of limited usefulness. Analysis of the existing information on bismuth in secondary references (i.e., books, review chapters) and on its chemical speciation in seawater revealed that the uncritical reproduction of old data is a widespread practice.

Bismuth-Silicon and Bismuth-Polyurethane Composite Shields for Breast Protection in Chest Computed Tomography Examinations

PubMed Central

Mehnati, Parinaz; Arash, Mehran; Akhlaghi, Parisa

2018-01-01

The article aims at constructing protective composite shields for breasts in chest computed tomography and investigating the effects of applying these new bismuth composites on dose and image quality. Polyurethane and silicon with 5% of bismuth were fabricated as a protective shield. At first, their efficiency in attenuating the X-ray beam was investigated by calculating the total attenuation coefficients at diagnostic energy range. Then, a physical chest phantom was scanned without and with these shields at tube voltage of 120 kVp, and image parameters together with dose values were studied. The results showed that these two shields have great effects on attenuating the X-ray beam, especially for lower energies (<40 kV), and in average, the attenuation coefficients of bismuth-polyurethane composite are higher in this energy range. The maximum relative differences between the average Hounsfield units (HUs) and noises of images without and with shield for both composites in 13 regions of interest were 4.5% and 15.7%, respectively. Moreover, primary investigation confirmed the ability of both shields (especially polyurethane-bismuth composite) in dose reduction. Comparing these two composites regarding the amount of dose reduction, the changes in HU and noise, and attenuation coefficients in diagnostic energy range, it seems that polyurethane composite is more useful for dose reduction, especially for higher tube voltages. PMID:29628636

Absorber Materials for Transition-Edge Sensor X-ray Microcalorimeters

NASA Technical Reports Server (NTRS)

Brown, Ari-David; Bandler, Simon; Brekosky, Regis; Chervenak, James; Figueroa-Feliciano, Enectali; Finkbeiner, Fred; Sadleir, Jack; Iyomoto, Naoko; Kelley, Richard; Kilbourne, Caroline;

Pairing from dynamically screened Coulomb repulsion in bismuth

NASA Astrophysics Data System (ADS)

Ruhman, Jonathan; Lee, Patrick A.

2017-12-01

Recently, Prakash et al. have discovered bulk superconductivity in single crystals of bismuth, which is a semimetal with extremely low carrier density. At such low density, we argue that conventional electron-phonon coupling is too weak to be responsible for the binding of electrons into Cooper pairs. We study a dynamically screened Coulomb interaction with effective attraction generated on the scale of the collective plasma modes. We model the electronic states in bismuth to include three Dirac pockets with high velocity and one hole pocket with a significantly smaller velocity. We find a weak-coupling instability, which is greatly enhanced by the presence of the hole pocket. Therefore we argue that bismuth is the first material to exhibit superconductivity driven by retardation effects of Coulomb repulsion alone. By using realistic parameters for bismuth we find that the acoustic plasma mode does not play the central role in pairing. We also discuss a matrix element effect, resulting from the Dirac nature of the conduction band, which may affect Tc in the s -wave channel without breaking time-reversal symmetry.

POLONIUM SEPARATION PROCESS

DOEpatents

Karraker, D.G.

1959-07-14

A liquid-liquid extraction process is presented for the recovery of polonium from lead and bismuth. According to the invention an acidic aqueous chloride phase containing the polonium, lead, and bismuth values is contacted with a tributyl phosphate ether phase. The polonium preferentially enters the organic phase which is then separated and washed with an aqueous hydrochloric solution to remove any lead or bismuth which may also have been extracted. The now highly purified polonium in the organic phase may be transferred to an aqueous solution by extraction with aqueous nitric acid.

METHOD FOR REMOVING CONTAMINATION FROM PRECIPITATES

DOEpatents

Stahl, G.W.

1959-01-01

An improvement in the bismuth phosphate carrier precipitation process is presented for the recovery and purification of plutonium. When plutonium, in the tetravalent state, is carried on a bismuth phosphate precipitate, amounts of centain of the fission products are carried along with the plutonium. The improvement consists in washing such fission product contaminated preeipitates with an aqueous solution of ammonium hydrogen fluoride. since this solution has been found to be uniquely effective in washing fission production contamination from the bismuth phosphate precipitate.

Experimental Study and Reactive Transport Modeling of Boric Acid Leaching of Concrete

NASA Astrophysics Data System (ADS)

Pabalan, R. T.; Chiang, K.-T. K.

2013-07-01

Borated water leakage through spent fuel pools (SFPs) at pressurized water reactors is a concern because it could cause corrosion of reinforcement steel in the concrete structure, compromise the integrity of the structure, or cause unmonitored releases of contaminated water to the environment. Experimental data indicate that pH is a critical parameter that determines the corrosion susceptibility of rebar in borated water and the degree of concrete degradation by boric acid leaching. In this study, reactive transport modeling of concrete leaching by borated water was performed to provide information on the solution pH in the concrete crack or matrix and the degree of concrete degradation at different locations of an SFP concrete structure exposed to borated water. Simulations up to 100 years were performed using different boric acid concentrations, crack apertures, and solution flow rates. Concrete cylinders were immersed in boric acid solutions for several months and the mineralogical changes and boric acid penetration in the concrete cylinder were evaluated as a function of time. The depths of concrete leaching by boric acid solution derived from the reactive transport simulations were compared with the measured boric acid penetration depth.

Dosimetric properties of dysprosium doped calcium magnesium borate glass subjected to Co-60 gamma ray

DOE Office of Scientific and Technical Information (OSTI.GOV)

Omar, R. S., E-mail: ratnasuffhiyanni@gmail.com; Wagiran, H., E-mail: husin@utm.my; Saeed, M. A.

Thermoluminescence (TL) dosimetric properties of dysprosium doped calcium magnesium borate (CMB:Dy) glass are presented. This study is deemed to understand the application of calcium as the modifier in magnesium borate glass with the presence of dysprosium as the activator to be performed as TL dosimeter (TLD). The study provides fundamental knowledge of a glass system that may lead to perform new TL glass dosimetry application in future research. Calcium magnesium borate glass systems of (70-y) B{sub 2}O{sub 3} − 20 CaO – 10 MgO-(y) Dy{sub 2}O{sub 3} with 0.05  mol % ≤ y ≤ 0.7  mol % of dyprosium weremore » prepared by melt-quenching technique. The amorphous structure and TL properties of the prepared samples were determined using powder X-ray diffraction (XRD) and TL reader; model Harshaw 4500 respectively. The samples were irradiated to Co-60 gamma source at a dose of 50 Gy. Dosimetric properties such as annealing procedure, time temperature profile (TTP) setting, optimization of Dy{sub 2}O{sub 3} concentration of 0.5 mol % were determined for thermoluminescence dosimeter (TLD) reader used.« less

Evaluation of borate bioactive glass scaffolds with different pore sizes in a rat subcutaneous implantation model.

PubMed

Deliormanli, Aylin M; Liu, Xin; Rahaman, Mohamed N

2014-01-01

Borate bioactive glass has been shown to convert faster and more completely to hydroxyapatite and enhance new bone formation in vivo when compared to silicate bioactive glass (such as 45S5 and 13-93 bioactive glass). In this work, the effects of the borate glass microstructure on its conversion to hydroxyapatite (HA) in vitro and its ability to support tissue ingrowth in a rat subcutaneous implantation model were investigated. Bioactive borate glass scaffolds, designated 13-93B3, with a grid-like microstructure and pore widths of 300, 600, and 900 µm were prepared by a robocasting technique. The scaffolds were implanted subcutaneously for 4 weeks in Sprague Dawley rats. Silicate 13-93 glass scaffolds with the same microstructure were used as the control. The conversion of the scaffolds to HA was studied as a function of immersion time in a simulated body fluid. Histology and scanning electron microscopy were used to evaluate conversion of the bioactive glass implants to hydroxyapatite, as well as tissue ingrowth and blood vessel formation in the implants. The pore size of the scaffolds was found to have little effect on tissue infiltration and angiogenesis after the 4-week implantation.

Titanium addition influences antibacterial activity of bioactive glass coatings on metallic implants.

PubMed

Rodriguez, Omar; Stone, Wendy; Schemitsch, Emil H; Zalzal, Paul; Waldman, Stephen; Papini, Marcello; Towler, Mark R

2017-10-01

In an attempt to combat the possibility of bacterial infection and insufficient bone growth around metallic, surgical implants, bioactive glasses may be employed as coatings. In this work, silica-based and borate-based glass series were synthesized for this purpose and subsequently characterized in terms of antibacterial behavior, solubility and cytotoxicity. Borate-based glasses were found to exhibit significantly superior antibacterial properties and increased solubility compared to their silica-based counterparts, with BRT0 and BRT3 (borate-based glasses with 0 and 15 mol% of titanium dioxide incorporated, respectively) outperforming the remainder of the glasses, both borate and silicate based, in these respects. Atomic Absorption Spectroscopy confirmed the release of zinc ions (Zn 2+ ), which has been linked to the antibacterial abilities of glasses SRT0, BRT0 and BRT3, with inhibition effectively achieved at concentrations lower than 0.7 ppm. In vitro cytotoxicity studies using MC3T3-E1 osteoblasts confirmed that cell proliferation was affected by all glasses in this study, with decreased proliferation attributed to a faster release of sodium ions over calcium ions in both glass series, factor known to slow cell proliferation in vitro .

University of Maryland MRSEC - News: Featured

Science.gov Websites

state at surface of bismuth selenide Completed device MRSEC research, published in NanoLetters ASAP in and M. S. Fuhrer, "Insulating behavior in ultrathin bismuth selenide field effect transistors

Uranium Hydridoborates: Synthesis, Magnetism, and X-ray/Neutron Diffraction Structures.

PubMed

Braunschweig, H; Gackstatter, A; Kupfer, T; Radacki, K; Franke, S; Meyer, K; Fucke, K; Lemée-Cailleau, M-H

2015-08-17

While uranium hydridoborate complexes containing the [BH4](-) moiety have been well-known in the literature for many years, species with functionalized borate centers remained considerably rare. We were now able to prepare several uranium hydridoborates (1-4) with amino-substituted borate moieties with high selectivity by smooth reaction of [Cp*2UMe2] (Cp* = C5Me5) and [Cp'2UMe2] (Cp' = 1,2,4-tBu3C5H2) with the aminoborane H2BN(SiMe3)2. A combination of nuclear magnetic resonance spectroscopy, deuteration experiments, magnetic SQUID measurements, and X-ray/neutron diffraction studies was used to verify the anticipated molecular structures and oxidation states of 1-4 and helped to establish a linear tridentate coordination mode of the borate anions.

Investigation of Mechanistic Pathway for Trimethyl Borate Mediated Amidation of (R)-Mandelic Acid for the Synthesis of Mirabegron, an Antimuscarinic Agent.

PubMed

Deshmukh, Dattatray G; Bangal, Mukund N; Patekar, Mukunda R; Medhane, Vijay J; Mathad, Vijayavitthal Thippannachar

2018-03-01

The present work describes investigation of mechanistic pathway for trimethyl borate mediated amidation of (R)-mandelic acid (3) with 4-nitophenylethylamine (2) to provide (R)-2-hydroxy-N-[2-(4-nitrophenyl)ethyl]-2-phenylacetamide (4) during mirabegron synthesis. Plausible reaction mechanism is proposed by isolating and elucidating the active α-hydroxy ester intermediate 16 from the reaction mass. Trimethyl borate mediated approach proved to be selective in providing 4 without disturbing α-hydroxyl group and stereochemistry of the chiral center, and is also a greener, more economic and production friendly over the reported methods. The developed approach is rapid and efficient for the preparation of 4 with an overall yield of 85-87% and around 99.0% purity by HPLC at scale.

FTIR of binary lead borate glass: Structural investigation

NASA Astrophysics Data System (ADS)

Othman, H. A.; Elkholy, H. S.; Hager, I. Z.

2016-02-01

The glass samples were prepared according to the following formula: (100-x) B2O3 - x PbO, where x = 20-80 mol% by melt quenching method. The density of the prepared samples was measured and molar volume was calculated. IR spectra were measured for the prepared samples to investigate the glass structure. The IR spectra were deconvoluted using curves of Gaussian shape at approximately the same frequencies. The deconvoluted data were used to study the effect of PbO content on all the structural borate groups. Some structural parameters such as density, packing density, bond length and bond force constant were theoretically calculated and were compared to the obtained experimental results. Deviation between the experimental and theoretically calculated parameters reflects the dual role of PbO content on the network of borate glass.

Visible luminescence of dysprosium ions in oxyhalide lead borate glasses.

PubMed

Pisarska, Joanna; Żur, Lidia; Pisarski, Wojciech A

2011-08-15

Visible luminescence of Dy(3+) ions in oxyhalide lead borate glasses was examined. Luminescence spectra show two intense bands at 480 nm and 573 nm due to (4)F(9/2)→(6)H(15/2) (blue) and (4)F(9/2)→(6)H(13/2) (yellow) transitions of Dy(3+). Luminescence decays from (4)F(9/2) state and yellow-to-blue luminescence intensity ratios (Y/B) were analysed with PbX(2) (X=F, Cl) content. An introduction of PbX(2) to the borate glass results in the increasing of (4)F(9/2) lifetime and the decreasing of yellow-to-blue luminescence intensity ratio, which is due to reduction of covalency between Dy(3+) and O(2-)/X(-) ions. Copyright © 2010 Elsevier B.V. All rights reserved.

PROCESS USING BISMUTH PHOSPHATE AS A CARRIER PRECIPITATE FOR FISSION PRODUCTS AND PLUTONIUM VALUES

DOEpatents

Finzel, T.G.

1959-03-10

A process is described for separating plutonium from fission products carried therewith when plutonium in the reduced oxidation state is removed from a nitric acid solution of irradiated uranium by means of bismuth phosphate as a carrier precipitate. The bismuth phosphate carrier precipitate is dissolved by treatment with nitric acid and the plutonium therein is oxidized to the hexavalent oxidation state by means of potassium dichromate. Separation of the plutonium from the fission products is accomplished by again precipitating bismuth phosphate and removing the precipitate which now carries the fission products and a small percentage of the plutonium present. The amount of plutonium carried in this last step may be minimized by addition of sodium fluoride, so as to make the solution 0.03N in NaF, prior to the oxidation and prccipitation step.

Isotopic generator for bismuth-212 and lead-212 based on radium

DOEpatents

Hines, J.J.; Atcher, R.W.; Friedman, A.M.

1985-01-30

Disclosed are method and apparatus for providing radionuclides of bismuth-212 and lead-212. Thorium-228 and carrier solution starting material is input to a radiologically contained portion of an isotopic generator system, and radium-224 is separated from thorium-228 which is retained by a strongly basic anion exchange column. The separated radium-224 is transferred to an accessible, strongly acidic cationic exchange column. The cationic column retains the radium-224, and natural radioactive decay generates bismuth-212 and lead-212. The cationic exchange column can also be separated from the contained portion of the system and utilized without the extraordinary safety measures necessary in the contained portion. Furthermore, the cationic exchange column provides over a relatively long time period the short lived lead-212 and bismuth-212 radionuclides which are useful for a variety of medical therapies.

Simultaneous quantitative analysis of arsenic, bismuth, selenium, and tellurium in soil samples using multi-channel hydride-generation atomic fluorescence spectrometry.

PubMed

Wang, Fang; Zhang, Gai

2011-03-01

The basic principles and the application of hydride-generation multi-channel atomic fluorescence spectrometry (HG-MC-AFS) in soil analysis are described. It is generally understood that only one or two elements can be simultaneously detected by commonly used one- or two-channel HG-AFS. In this work, a new sample-sensitive and effective method for the analysis of arsenic, bismuth, tellurium, and selenium in soil samples by simultaneous detection using HG-MC-AFS was developed. The method detection limits for arsenic, bismuth, tellurium, and selenium are 0.19 μg/g, 0.10 μg/g, 0.11 μg/g, and 0.08 μg/g, respectively. This method was successfully applied to the simultaneous determination of arsenic, bismuth, tellurium, and selenium in soil samples.

Isotopic generator for bismuth-212 and lead-212 from radium

DOEpatents

Atcher, Robert W.; Friedman, Arnold M.; Hines, John

1987-01-01

A method and apparatus for providing radionuclides of bismuth-212 and lead-212. Thorium-228 and carrier solution starting material is input to a radiologically contained portion of an isotopic generator system, and radium-224 is separated from thorium-228 which is retained by a strongly basic anion exchange column. The separated radium-224 is transferred to an accessible, strongly acidic cationic exchange column. The cationic column retains the radium-224, and natural radioactive decay generates bismuth-212 and lead-212. The cationic exchange column can also be separated from the contained portion of the system and utilized without the extraordinary safety measures necessary in the contained portion. Furthermore, the cationic exchange column provides over a relatively long time period the short lived lead-212 and bismuth-212 radionuclides which are useful for a variety of medical therapies.