49 CFR 178.347-2 - Material and thickness of material.

Code of Federal Regulations, 2014 CFR

2014-10-01

... Baffles When Used as Tank Reinforcement) Using Mild Steel (MS), High Strength Low Alloy Steel (HSLA), Austenitic Stainless Steel (SS), or Aluminum (AL)—Expressed in Decimals of an Inch After Forming Volume... (MS), High Strength Low Alloy Steel (HSLA), Austenitic Stainless Steel (SS), or Aluminum (AL...

49 CFR 178.347-2 - Material and thickness of material.

Code of Federal Regulations, 2012 CFR

2012-10-01

... Baffles When Used as Tank Reinforcement) Using Mild Steel (MS), High Strength Low Alloy Steel (HSLA), Austenitic Stainless Steel (SS), or Aluminum (AL)—Expressed in Decimals of an Inch After Forming Volume... (MS), High Strength Low Alloy Steel (HSLA), Austenitic Stainless Steel (SS), or Aluminum (AL...

49 CFR 178.347-2 - Material and thickness of material.

Code of Federal Regulations, 2011 CFR

2011-10-01

... Baffles When Used as Tank Reinforcement) Using Mild Steel (MS), High Strength Low Alloy Steel (HSLA), Austenitic Stainless Steel (SS), or Aluminum (AL)—Expressed in Decimals of an Inch After Forming Volume... (MS), High Strength Low Alloy Steel (HSLA), Austenitic Stainless Steel (SS), or Aluminum (AL...

49 CFR 178.347-2 - Material and thickness of material.

Code of Federal Regulations, 2013 CFR

2013-10-01

... Baffles When Used as Tank Reinforcement) Using Mild Steel (MS), High Strength Low Alloy Steel (HSLA), Austenitic Stainless Steel (SS), or Aluminum (AL)—Expressed in Decimals of an Inch After Forming Volume... (MS), High Strength Low Alloy Steel (HSLA), Austenitic Stainless Steel (SS), or Aluminum (AL...

49 CFR 178.346-2 - Material and thickness of material.

Code of Federal Regulations, 2010 CFR

2010-10-01

... Bulkheads and Baffles When Used as Tank Reinforcement) Using Mild Steel (MS), High Strength Low Alloy Steel (HSLA), Austenitic Stainless Steel (SS), or Aluminum (AL)—Expressed in Decimals of an Inch After Forming... Thickness of Shell Using Mild Steel (MS), High Strength Low Alloy Steel (HSLA), Austenitic Stainless Steel...

Microdomain Yield Behaviour in an Ultra-High Strength Low Alloy Steel for Marine Use with Low Sensitivity of SCC

NASA Astrophysics Data System (ADS)

Yin, Jiang; Tao, Anxiang; Xu, Pingguang; Ping, Dehai

The present paper involves a fundamental research on microdomain yield behavior of an ultrahigh strength low alloy steel with high temperature tempered bainite. The smooth cylinder specimen was took from deep water mooring chain links from the steel with the chemical composition of 0.23C-0.25Si -0.70Mn-3.55 (Cr+Ni+Mo) -0.13 (V+Nb+Ti) (mass %) ,which was quenched from 1253K and then tempered at 873K Its macroscopic yield strength is 1120MPa and the tensile strength is 1250MPa In-situ neutron diffraction measurements of loading tension have suggested that a good linear elastic deformation can be kept up to 500MPa stress, and then (200) priority non-linear elastic strain, that is the yield of crystal lattice occur at 700MPa and the (110) non-linear elastic strain was found at 800MPa. The (200) and (110) nonlinear elastic strain increases gradually when the stress was further increased, however, the (211) kept its linear elastic deformation stage as before. The sub-microstructural analysis carried out using TEM and additional determine the nature and quantitative analysis has revealed that there are three kinds of alloy carbides: (1) θ-M3C cementites with an average particle size of less than 50 nm which inside laths and lath boundaries; (2) ɛ-M2C formed uniformly within the ferrites with a length of less than 200 nm and width of less than 20 nm; (3) ultra-fine high density MC cohered with matrix α-Fe and its particle size is about 2 nm. The whole microdomain yield behaviour of the material was possibly influenced by the fcc-MC with high density. The results of CLT (constant load), SSRT (slow strain rate) and KIscc test of the present chain in seawater solution indicate, that threshold value of SCC (stress corrosion cracking) stress exceed 0.8 tensile strength and the chain's KIscc value is double of KIscc value of 4340 steel type parts. MC not only form strong hydrogen trap, but also slow down microdomain yield likely by means of increasing yield strength of crystal lattice, thus reduce SCC sensibility of the steel.

Stress Corrosion Cracking and Hydrogen Embrittlement of Thick Section High Strength Low Alloy Steel

DTIC Science & Technology

1986-06-01

copper and especially molybdenum. Dual phase HSLA steels are comprised of islands of martensite or bainite in a ferrite matrix. The... Copper Steels", TransactionN AIME, Volume 105, pp. 133-166, 1933. 60. Creswick, W. E., "Commercial Development of a Rimmed Low Alloy Precipitation ... precipitates all serve to minimize the aggregate effects of hydrogen. 82 - ------- ------ - 3. MATERIAL 3.1 bSLA STEELS High strength low alloy

Influence of Carbide Modifications on the Mechanical Properties of Ultra-High-Strength Stainless Steels

NASA Astrophysics Data System (ADS)

Seo, Joo-Young; Park, Soo-Keun; Kwon, Hoon; Cho, Ki-Sub

2017-10-01

The mechanical properties of ultra-high-strength secondary hardened stainless steels with varying Co, V, and C contents have been studied. A reduced-Co alloy based on the chemical composition of Ferrium S53 was made by increasing the V and C content. This changed the M2C-strengthened microstructure to a MC plus M2C-strengthened microstructure, and no deteriorative effects were observed for peak-aged and over-aged samples despite the large reduction in Co content from 14 to 7 wt pct. The mechanical properties according to alloying modification were associated with carbide precipitation kinetics, which was clearly outlined by combining analytical tools including small-angle neutron scattering (SANS) as well as an analytical TEM with computational simulation.

A high-strength silicide phase in a stainless steel alloy designed for wear-resistant applications.

PubMed

Bowden, D; Krysiak, Y; Palatinus, L; Tsivoulas, D; Plana-Ruiz, S; Sarakinou, E; Kolb, U; Stewart, D; Preuss, M

2018-04-10

Hardfacing alloys provide strong, wear-resistant and corrosion-resistant coatings for extreme environments such as those within nuclear reactors. Here, we report an ultra-high-strength Fe-Cr-Ni silicide phase, named π-ferrosilicide, within a hardfacing Fe-based alloy. Electron diffraction tomography has allowed the determination of the atomic structure of this phase. Nanohardness testing indicates that the π-ferrosilicide phase is up to 2.5 times harder than the surrounding austenite and ferrite phases. The compressive strength of the π-ferrosilicide phase is exceptionally high and does not yield despite loading in excess of 1.6 GPa. Such a high-strength silicide phase could not only provide a new type of strong, wear-resistant and corrosion-resistant Fe-based coating, replacing more costly and hazardous Co-based alloys for nuclear applications, but also lead to the development of a new class of high-performance silicide-strengthened stainless steels, no longer reliant on carbon for strengthening.

Novel 1.5 GPa-strength with 50%-ductility by transformation-induced plasticity of non-recrystallized austenite in duplex steels.

PubMed

Sohn, Seok Su; Song, Hyejin; Jo, Min Chul; Song, Taejin; Kim, Hyoung Seop; Lee, Sunghak

2017-04-28

Needs for steel designs of ultra-high strength and excellent ductility have been an important issue in worldwide automotive industries to achieve energy conservation, improvement of safety, and crashworthiness qualities. Because of various drawbacks in existing 1.5-GPa-grade steels, new development of formable cold-rolled ultra-high-strength steels is essentially needed. Here we show a plausible method to achieve ultra-high strengths of 1.0~1.5 GPa together with excellent ductility above 50% by actively utilizing non-recrystallization region and TRansformation-Induced Plasticity (TRIP) mechanism in a cold-rolled and annealed Fe-Mn-Al-C-based steel. We adopt a duplex microstructure composed of austenite and ultra-fine ferrite in order to overcome low-yield-strength characteristics of austenite. Persistent elongation up to 50% as well as ultra-high yield strength over 1.4 GPa are attributed to well-balanced mechanical stability of non-crystallized austenite with critical strain for TRIP. Our results demonstrate how the non-recrystallized austenite can be a metamorphosis in 1.5-GPa-grade steel sheet design.

Quenching and Partitioning Process Development to Replace Hot Stamping of High Strength Automotive Steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

De Moor, Emmanuel

The present project investigated Quenching and Partitioning (Q&P) to process cold rolled steels to develop high strength sheet steels that exhibit superior ductility compared to available grades with the intent to allow forming of high strength parts at room temperature to provide an alternative to hot stamping of parts. Hot stamping of boron alloyed steel is the current technology to manufacture thinner gauge sections in automotive structures to guarantee anti-intrusion during collisions whilst improving fuel efficiency by decreasing vehicle weight. Hot stamping involves reheating steel to 900 °C or higher followed by deformation and quenching in the die to producemore » ultra-high strength materials. Hot stamping requires significant energy to reheat the steel and is less productive than traditional room temperature stamping operations. Stamping at elevated temperature was developed due to the lack of available steels with strength levels of interest possessing sufficient ductility enabling traditional room temperature forming. This process is seeing growing demand within the automotive industry and, given the reheating step in this operation, increased energy consumption during part manufacturing results. The present research program focused on the development of steel grades via Q&P processing that exhibit high strength and formability enabling room temperature forming to replace hot stamping. The main project objective consisted of developing sheet steels exhibiting minimum ultimate tensile strength levels of 1200 MPa in combination with minimum tensile elongation levels of 15 pct using Q&P processing through judicious alloy design and heat treating parameter definition. In addition, detailed microstructural characterization and study of properties, processing and microstructure interrelationships were pursued to develop strategies to further enhance tensile properties. In order to accomplish these objectives, alloy design was conducted towards achieving the target properties. Twelve alloys were designed and laboratory produced involving melting, alloying, casting, hot rolling, and cold rolling to obtain sheet steels of approximately 1 mm thickness. Q&P processing of the samples was then conducted. Target properties were achieved and substantially exceeded demonstrating success in the developed and employed alloy design approaches. The best combinations of tensile properties were found at approximately 1550 MPa with a total elongation in excess of 20 pct clearly showing the potential for replacement of hot stamping to produce advanced high strength steels.« less

Brittle intermetallic compound makes ultrastrong low-density steel with large ductility.

PubMed

Kim, Sang-Heon; Kim, Hansoo; Kim, Nack J

2015-02-05

Although steel has been the workhorse of the automotive industry since the 1920s, the share by weight of steel and iron in an average light vehicle is now gradually decreasing, from 68.1 per cent in 1995 to 60.1 per cent in 2011 (refs 1, 2). This has been driven by the low strength-to-weight ratio (specific strength) of iron and steel, and the desire to improve such mechanical properties with other materials. Recently, high-aluminium low-density steels have been actively studied as a means of increasing the specific strength of an alloy by reducing its density. But with increasing aluminium content a problem is encountered: brittle intermetallic compounds can form in the resulting alloys, leading to poor ductility. Here we show that an FeAl-type brittle but hard intermetallic compound (B2) can be effectively used as a strengthening second phase in high-aluminium low-density steel, while alleviating its harmful effect on ductility by controlling its morphology and dispersion. The specific tensile strength and ductility of the developed steel improve on those of the lightest and strongest metallic materials known, titanium alloys. We found that alloying of nickel catalyses the precipitation of nanometre-sized B2 particles in the face-centred cubic matrix of high-aluminium low-density steel during heat treatment of cold-rolled sheet steel. Our results demonstrate how intermetallic compounds can be harnessed in the alloy design of lightweight steels for structural applications and others.

On the Processing of Martensitic Steels in Continuous Galvanizing Lines: Part II

NASA Astrophysics Data System (ADS)

Song, Taejin; Kwak, Jaihyun; de Cooman, B. C.

2012-01-01

The conventional continuous hot-dip galvanizing (GI) and galvannealing (GA) processes can be applied to untransformed austenite to produce Zn and Zn-alloy coated low-carbon ultra-high-strength martensitic steel provided specific alloying additions are made. The most suitable austenite decomposition behavior results from the combined addition of boron, Cr, and Mo, which results in a pronounced transformation bay during isothermal transformation. The occurrence of this transformation bay implies a considerable retardation of the austenite decomposition in the temperature range below the bay, which is close to the stages in the continuous galvanizing line (CGL) thermal cycle related to the GI and GA processes. After the GI and GA processes, a small amount of granular bainite, which consists of bainitic ferrite and discrete islands of martensite/austenite (M/A) constituents embedded in martensite matrix, is present in the microstructure. The ultimate tensile strength (UTS) of the steel after the GI and GA cycle was over 1300 MPa, and the stress-strain curve was continuous without any yielding phenomena.

Estimation of Atmospheric Corrosion of High-Strength, Low-Alloy Steels

DOT National Transportation Integrated Search

1997-05-01

This data analysis was undertaken to investigate the weatherability of steels whose compositions do not fall in the range of ASTM Standard G101, Estimating the Atmospheric Corrosion Resistance of Low-Alloy Steels.

Enhancement of Impact Toughness by Delamination Fracture in a Low-Alloy High-Strength Steel with Al Alloying

NASA Astrophysics Data System (ADS)

Sun, Junjie; Jiang, Tao; Liu, Hongji; Guo, Shengwu; Liu, Yongning

2016-12-01

The effect of delamination toughening of martensitic steel was investigated both at room and low temperatures [253 K and 233 K (-20 °C and -40 °C)]. Two low-alloy martensitic steels with and without Al alloying were both prepared. Layered structure with white band and black matrix was observed in Al alloyed steel, while a homogeneous microstructure was displayed in the steel without Al. Both steels achieved high strength (tensile strength over 1600 MPa) and good ductility (elongation over 11 pct), but they displayed stark contrasts on impact fracture mode and Charpy impact energy. Delamination fracture occurred in Al alloyed steel and the impact energies were significantly increased both at room temperature (from 75 to 138 J, i.e., nearly improved up to 2 times) and low temperatures [from 47.9 to 71.3 J at 233 K (-40 °C)] compared with the one without Al. Alloying with Al promotes the segregation of Cr, Mn, Si and C elements to form a network structure, which is martensite with higher carbon content and higher hardness than that of the matrix. And this network structure evolved into a band structure during the hot rolling process. The difference of yield stress between the band structure and the matrix gives rise to a delamination fracture during the impact test, which increases the toughness greatly.

Cyclic Strain Resistance, Stress Response, Fatigue Life, and Fracture Behavior of High Strength Low Alloy Steel 300 M

NASA Astrophysics Data System (ADS)

Manigandan, K.; Srivatsan, T. S.; Tammana, Deepthi; Poorgangi, Behrang; Vasudevan, Vijay K.

2014-05-01

The focus of this technical manuscript is a record of the specific role of microstructure and test specimen orientation on cyclic stress response, cyclic strain resistance, and cyclic stress versus strain response, deformation and fracture behavior of alloy steel 300 M. The cyclic strain amplitude-controlled fatigue properties of this ultra-high strength alloy steel revealed a linear trend for the variation of log elastic strain amplitude with log reversals-to-failure, and log plastic strain amplitude with log reversals-to-failure for both longitudinal and transverse orientations. Test specimens of the longitudinal orientation showed only a marginal improvement over the transverse orientation at equivalent values of plastic strain amplitude. Cyclic stress response revealed a combination of initial hardening for the first few cycles followed by gradual softening for a large portion of fatigue life before culminating in rapid softening prior to catastrophic failure by fracture. Fracture characteristics of test specimens of this alloy steel were different at both the macroscopic and fine microscopic levels over the entire range of cyclic strain amplitudes examined. Both macroscopic and fine microscopic observations revealed fracture to be a combination of both brittle and ductile mechanisms. The underlying mechanisms governing stress response, deformation characteristics, fatigue life, and final fracture behavior are presented and discussed in light of the competing and mutually interactive influences of test specimen orientation, intrinsic microstructural effects, deformation characteristics of the microstructural constituents, cyclic strain amplitude, and response stress.

Increasing the Cryogenic Toughness of Steels

NASA Technical Reports Server (NTRS)

Rush, H. F.

1986-01-01

Grain-refining heat treatments increase toughness without substantial strength loss. Five alloys selected for study, all at or near technological limit. Results showed clearly grain sizes of these alloys refined by such heat treatments and grain refinement results in large improvement in toughness without substantial loss in strength. Best improvements seen in HP-9-4-20 Steel, at low-strength end of technological limit, and in Maraging 200, at high-strength end. These alloys, in grain refined condition, considered for model applications in high-Reynolds-number cryogenic wind tunnels.

Ultrahigh Charpy impact toughness (~450J) achieved in high strength ferrite/martensite laminated steels

PubMed Central

Cao, Wenquan; Zhang, Mingda; Huang, Chongxiang; Xiao, Shuyang; Dong, Han; Weng, Yuqing

2017-01-01

Strength and toughness are a couple of paradox as similar as strength-ductility trade-off in homogenous materials, body-centered-cubic steels in particular. Here we report a simple way to get ultrahigh toughness without sacrificing strength. By simple alloying design and hot rolling the 5Mn3Al steels in ferrite/austenite dual phase temperature region, we obtain a series of ferrite/martensite laminated steels that show up-to 400–450J Charpy V-notch impact energy combined with a tensile strength as high as 1.0–1.2 GPa at room temperature, which is nearly 3–5 times higher than that of conventional low alloy steels at similar strength level. This remarkably enhanced toughness is mainly attributed to the delamination between ferrite and martensite lamellae. The current finding gives us a promising way to produce high strength steel with ultrahigh impact toughness by simple alloying design and hot rolling in industry. PMID:28150692

Ultrahigh Charpy impact toughness (~450J) achieved in high strength ferrite/martensite laminated steels

NASA Astrophysics Data System (ADS)

Cao, Wenquan; Zhang, Mingda; Huang, Chongxiang; Xiao, Shuyang; Dong, Han; Weng, Yuqing

2017-02-01

Strength and toughness are a couple of paradox as similar as strength-ductility trade-off in homogenous materials, body-centered-cubic steels in particular. Here we report a simple way to get ultrahigh toughness without sacrificing strength. By simple alloying design and hot rolling the 5Mn3Al steels in ferrite/austenite dual phase temperature region, we obtain a series of ferrite/martensite laminated steels that show up-to 400-450J Charpy V-notch impact energy combined with a tensile strength as high as 1.0-1.2 GPa at room temperature, which is nearly 3-5 times higher than that of conventional low alloy steels at similar strength level. This remarkably enhanced toughness is mainly attributed to the delamination between ferrite and martensite lamellae. The current finding gives us a promising way to produce high strength steel with ultrahigh impact toughness by simple alloying design and hot rolling in industry.

Factors affecting the strength of multipass low-alloy steel weld metal

NASA Technical Reports Server (NTRS)

Krantz, B. M.

1972-01-01

The mechanical properties of multipass high-strength steel weld metals depend upon several factors, among the most important being: (1) The interaction between the alloy composition and weld metal cooling rate which determines the as-deposited microstructure; and (2) the thermal effects of subsequent passes on each underlying pass which alter the original microstructure. The bulk properties of a multipass weld are therefore governed by both the initial microstructure of each weld pass and its subsequent thermal history. Data obtained for a high strength low alloy steel weld metal confirmed that a simple correlation exists between mechanical properties and welding conditions if the latter are in turn correlated as weld cooling rate.

Resistance of Some Steels to Stress Corrosion Cracking

NASA Technical Reports Server (NTRS)

Humphries, T. S.; Nelson, E. E.

1982-01-01

Evaluations of stress-corrosion cracking resistance of five high-strength low-alloy steels described in report now available. Steels were heat-treated to various tensile strengths and found to be highly resistant to stress-corrosion cracking.

Welding of High-Strength Steels for Aircraft and Missile Applications

DTIC Science & Technology

1959-10-12

40 PRECIPITATION -HARDENING STAINLESS STEELS ...... .............. .. 40 Single-Treatment Martensitic Steelse ...metal. A survey of the procedures currently being used is presented. Low - Alloy Martensitic Steels AISI 4340, AMS 6434, XZOO, 300M, and 17-Z2AS all are...in roughly decreasing order of industry-wide interest: low - alloy martensitic steels , hot-work die steels , martensitic stainless steels , and

Development of Low Alloy Ti-B Steels for High Temperature Service Applications

DTIC Science & Technology

1952-04-01

Ti-B steels . Ordinarily, martensite or a hardened acicular ferrite structure in steel is associated with extremely low creep strength. However, the...12000 F. The ability of the Ti-B sheet steels to suppress the ferrite transformation to the martensite or lower bainite temperature range upon air...APPROVED FOR PUBLIC mEESX_ DISTRIBUTION UNjfljarT, • WJADC TECHNICAL REPORT 52-77 DEVELOPMENT OF LOW ALLOY Ti-B STEELS FOR HIGH TEMPERATURE SERVICE

Spray Deposition: A Fundamental Study of Droplet Impingement, Spreading and Consolidation

DTIC Science & Technology

1989-12-01

low alloy (HSLA) steel. Preforms of HSLA-100, a low carbon bainitic, copper precipitation strengthened HSLA steel...manufacturing process. Specifically, HSLA-100, a copper precipitation strengthened high-strength, low - alloy steel was spray cast via the Osprey’ m process...by spray casting. Preforms of HSLA-100, a low carbon bainitic, copper precipitation strengthened steel, were spray cast under differing conditions

Advanced Gear Alloys for Ultra High Strength Applications

NASA Technical Reports Server (NTRS)

Shen, Tony; Krantz, Timothy; Sebastian, Jason

2011-01-01

Single tooth bending fatigue (STBF) test data of UHS Ferrium C61 and C64 alloys are presented in comparison with historical test data of conventional gear steels (9310 and Pyrowear 53) with comparable statistical analysis methods. Pitting and scoring tests of C61 and C64 are works in progress. Boeing statistical analysis of STBF test data for the four gear steels (C61, C64, 9310 and Pyrowear 53) indicates that the UHS grades exhibit increases in fatigue strength in the low cycle fatigue (LCF) regime. In the high cycle fatigue (HCF) regime, the UHS steels exhibit better mean fatigue strength endurance limit behavior (particularly as compared to Pyrowear 53). However, due to considerable scatter in the UHS test data, the anticipated overall benefits of the UHS grades in bending fatigue have not been fully demonstrated. Based on all the test data and on Boeing s analysis, C61 has been selected by Boeing as the gear steel for the final ERDS demonstrator test gearboxes. In terms of potential follow-up work, detailed physics-based, micromechanical analysis and modeling of the fatigue data would allow for a better understanding of the causes of the experimental scatter, and of the transition from high-stress LCF (surface-dominated) to low-stress HCF (subsurface-dominated) fatigue failure. Additional STBF test data and failure analysis work, particularly in the HCF regime and around the endurance limit stress, could allow for better statistical confidence and could reduce the observed effects of experimental test scatter. Finally, the need for further optimization of the residual compressive stress profiles of the UHS steels (resulting from carburization and peening) is noted, particularly for the case of the higher hardness C64 material.

Influence of Hot Plastic Deformation in γ and (γ + α) Area on the Structure and Mechanical Properties of High-Strength Low-Alloy (HSLA) Steel.

PubMed

Sas, Jan; Kvačkaj, Tibor; Milkovič, Ondrej; Zemko, Michal

2016-11-30

The main goal of this study was to develop a new processing technology for a high-strength low-alloy (HSLA) steel in order to maximize the mechanical properties attainable at its low alloy levels. Samples of the steel were processed using thermal deformation schedules carried out in single-phase (γ) and dual-phase (γ + α) regions. The samples were rolled at unconventional finishing temperatures, their final mechanical properties were measured, and their strength and plasticity behavior was analyzed. The resulting microstructures were observed using optical and transmission electron microscopy (TEM). They consisted of martensite, ferrite and (NbV)CN precipitates. The study also explored the process of ferrite formation and its influence on the mechanical properties of the material.

Influences of Thermomechanical Processing on the Microstructure and Mechanical Properties of a HSLA Steel

NASA Astrophysics Data System (ADS)

Zhao, Yu; Xu, Songsong; Zou, Yun; Li, Jinhui; Zhang, Z. W.

High strength low alloy (HSLA) steels with high strength, high toughness, good corrosion resistance and weldability, can be widely used in shipbuilding, automobile, construction, bridging industry, etc. The microstructure evolution and mechanical properties can be influenced by thermomechanical processing. In this study, themomechanical processing is optimized to control the matrix microstructure and nano-scale precipitates in the matrix simultaneously. It is found that the low-temperature toughness and ductility of the steels are significantly the matrix microstructure during enhancing the strength by introducing the nano-scale precipitates. The effects of alloying elements on the microstructure evolution and nano-scale precipitation are also discussed.

Correlation of the thermodynamic calculation and the experimental observation of Ni-Mo-Cr low alloy steel changing Ni, Mo, and Cr contents

NASA Astrophysics Data System (ADS)

Park, Sang-Gyu; Kim, Min-Chul; Lee, Bong-Sang; Wee, Dang-Moon

2010-12-01

SA508 Gr.4N Ni-Mo-Cr low alloy steel has improved fracture toughness and strength compared to commercial low alloy steels such as SA508 Gr.3 Mn-Mo-Ni low alloy steel, which has less than 1% Ni. Higher strength and fracture toughness of low alloy steels can be achieved by increasing the Ni and Cr contents. In this study, the effects of the alloying elements of Ni and Cr on the microstructural characteristics and mechanical properties of SA508 Gr.4N Ni-Mo-Cr low alloy steel are evaluated. Changes in the stable phases of SA508 Gr.4N low alloy steel with these alloying elements were evaluated using thermodynamic calculation software. These values were then compared with the observed microstructural results. Additionally, tensile tests and Charpy impact test were carried out to evaluate the mechanical properties. The thermodynamic calculations show that Ni mainly affects the change of the matrix phase of γ and α rather than the carbide phase. Contrary to the Ni effect, Cr and Mo primarily affect the precipitation behavior of the carbide phases of Cr 23C 6, Cr 7C 3 and Mo 2C. In the microscopic observations, the lath martensitic structure becomes finer as the Ni content increases without affecting the carbides. When the Cr content decreases, the Cr carbide becomes unstable and carbide coarsening occurs. Carbide Mo 2C in the form of fine needles were observed in the high-Mo alloy. Greater strength was obtained after additions of Ni and Mo and the transition properties were improved as the Ni and Cr contents increased. These results were correlated with the thermodynamic calculation results.

The Mechanical Property of Batch Annealed High Strength Low Alloy Steel HC260LA

NASA Astrophysics Data System (ADS)

Yang, Xiaojiang; Xia, Mingsheng; Zhang, Hongbo; Han, Bin; Li, Guilan

Cold rolled high strength low alloy steel is widely applied in the automotive parts due to its excellent formability and weldability. In this paper, the steel grade HC260LA according to European Norm was developed with batch annealing process. With commercial C-Mn mild steel as a benchmark, three different groups of chemistry namely C-Mn-Si, C-Mn-Nb-Ti and C-Mn-Nb were compared in terms of yield-tensile strength (Y/T) ratio. Microstructure and mechanical properties were characterized as well. Based on industrial production results, chemistry and detailed process parameters for batch annealing were identified. In the end the optimal Y/T ratio was proposed for this steel grade under batch annealing process.

Creep Strength of Dissimilar Welded Joints Using High B-9Cr Steel for Advanced USC Boiler

NASA Astrophysics Data System (ADS)

Tabuchi, Masaaki; Hongo, Hiromichi; Abe, Fujio

2014-10-01

The commercialization of a 973 K (700 °C) class pulverized coal power system, advanced ultra-supercritical (A-USC) pressure power generation, is the target of an ongoing research project initiated in Japan in 2008. In the A-USC boiler, Ni or Ni-Fe base alloys are used for high-temperature parts at 923 K to 973 K (650 °C to 700 °C), and advanced high-Cr ferritic steels are planned to be used at temperatures lower than 923 K (650 °C). In the dissimilar welds between Ni base alloys and high-Cr ferritic steels, Type IV failure in the heat-affected zone (HAZ) is a concern. Thus, the high B-9Cr steel developed at the National Institute for Materials Science, which has improved creep strength in weldments, is a candidate material for the Japanese A-USC boiler. In the present study, creep tests were conducted on the dissimilar welded joints between Ni base alloys and high B-9Cr steels. Microstructures and creep damage in the dissimilar welded joints were investigated. In the HAZ of the high B-9Cr steels, fine-grained microstructures were not formed and the grain size of the base metal was retained. Consequently, the creep rupture life of the dissimilar welded joints using high B-9Cr steel was 5 to 10 times longer than that of the conventional 9Cr steel welded joints at 923 K (650 °C).

Effect of Temperature and Dynamic Loading on the Mechanical Properties of Copper-Alloyed High-Strength Interstitial-Free Steel

NASA Astrophysics Data System (ADS)

Rana, R.; Singh, S. B.; Bleck, W.; Mohanty, O. N.

2009-04-01

Crash resistance and formability relevant mechanical properties of a copper-alloyed interstitial-free (IF) steel processed under various conditions of batch annealing (BA), continuous annealing (CA), and postcontinuous annealing aging have been studied in a wide range of strain rate (3.33 × 10-4 to 200 s-1) and temperature (-100 °C to +20 °C). These properties have been compared with similarly processed traditional mild and high-strength IF steels. Assessment of various parameters such as strength, elongation, strain rate sensitivity of stress, strain-hardening capacity, temperature sensitivity of stress, activation volume, and specific energy absorption of all these steels implies that copper-alloyed IF steel is soft and formable in CA condition. It can be made stronger and more crash resistant than the conventional mild- or high-strength IF steels when aged to peak strength after CA. Room-temperature strain rate sensitivity of stress of the investigated steels exhibits a two-stage behavior. Copper in solution in ferrite causes solid solution softening at low temperatures (≤20 °C) and at high strain rates (200 s-1).

Assessment of Electron Beam Welding in Shipyard Construction,

DTIC Science & Technology

1985-12-01

electrical grade transformer oil which acts as a heat sink for the electrical components. The main high voltage power source converts the three phase I ne...tensile strength material in the range of 80 100 KSI (HY8O 10o0) *’*’ and 3) high strength low alloy material (A710 Gr. A with sulfur 0.0l0 maximum...Carbon Steel Structural Grade HSLA Steel Grade A710: 1) Carbon Steels (2-3") 2) Aluminum * - Grade E633: 3) Low Alloy HY 80, HY 100: -"Aluminum, Titanium

Fracture Characteristics of Two High-Strength, Low-Alloy and Two Stainless Steels

DTIC Science & Technology

1977-01-01

conditions. The effects of hydrogen. and temper. embrittlement on the materials’ behavior when fractured under tensile and fatigue fonditions were... effects of hydrogen- and tomper-embrittlement have a bet, crystal structure, this plane has the type on the materials’ behavior when fractured under...A. Troiano, "The Role of lydrogen and Other Intersiftials high-strength, low-alloy structural steels generally used in the Mechanical Behavior ot

Tailoring microstructure of Mg–Zn–Y alloys with quasicrystal and related phases for high mechanical strength

PubMed Central

Singh, Alok

2014-01-01

The occurrence of a stable icosahedral (i-) phase, which is quasicrystalline with an icosahedral (fivefold) symmetry, on the equilibrium phase diagram of Mg–Zn–RE (RE = Y, Gd, Tb, Dy, Ho or Er) alloys opened up an interesting possibility of developing a new series of magnesium alloys for structural applications. Alloys based on the i-phase have been studied for the past 14 years. Ultra-high strengths combined with good ductility have been shown. Here we show two strategies for tailoring microstructures for very high strengths in Mg–Zn–Y alloys. One of them involves strengthening by a fine distribution of rod-like precipitates, where the matrix grain size is not critical. The alloy is solutionized at a high temperature of 480 °C to dissolve a large part of the i-phase, followed by a high temperature extrusion (∼430 °C) and a low temperature ageing to reprecipitate phases with fine size distribution. At first, phase transformations involved in this procedure are described. The closeness of the structure of the precipitates to the i-phase is brought out. By this procedure, tensile yield strengths of over 370 MPa are obtained in grain sizes of 20 μm. In another strategy, the alloys are chill cast and then extruded at low temperatures of about 250 °C. Ultra-fine grains are produced by enhanced recrystallization due to presence of the i-phase. At the same time nano-sized precipitates are precipitated dynamically during extrusion from the supersaturated matrix. Ultra-high tensile strengths of up to 400 MPa are obtained in combination with ductility of 12 to 16%. Analysis of the microstructure shows that strengthening by the i-phase occurs by enhanced recrystallization during extrusion. It produces ultra-fine grain sizes to give very high strengths, and moderate texture for good ductility. Fine distribution of the i-phase and precipitates contribute to strengthening and provide microstructre stability. Ultra-high strength over a very wide range of grain sizes is thus demonstrated, by utilizing different strengthening effects. PMID:27877701

Development of Fine-Grained, Low-Carbon Bainitic Steels with High Strength and Toughness Produced Through the Conventional Hot-Rolling and Air-Cooling

NASA Astrophysics Data System (ADS)

Dhua, Sanjay Kumar; Sarkar, Partha Pratim; Saxena, Atul; Jha, Bimal Kumar

2016-12-01

Low-carbon bainitic steels have created enormous interest among scientists across the world in the past few decades because of their high strength, toughness, and weldability replacing the conventional quenched and tempered medium-carbon steels. Three experimental steels with varying alloy additions were made in a 100-kg laboratory induction furnace and cast into 100-mm-diameter cylindrical ingots. These ingots were hot-rolled and air-cooled to 6-mm plates in an experimental rolling mill with selected thermomechanical parameters. Steels processed through this process provided an ultrafine low-carbon bainitic microstructure with maximum yield strength (YS) and ultimate tensile strength (UTS) 575 and 705 MPa, respectively. The Charpy impact toughness of the experimental steels was excellent, and at 253 K (-20 °C), it varied from 114 to 170 Joules. Cu-B-added steel was found to give an optimum combination of strength, YS-575 MPa, and toughness, 114 J at 253 K (-20 °C). Thus, fine-grained, low-carbon bainitic steels could be developed with a proper combination of alloying elements and thermomechanical parameters even by air-cooling.

Effect of alloy composition on high-temperature bending fatigue strength of ferritic stainless steels

NASA Astrophysics Data System (ADS)

Ahn, Yong-Sik; Song, Jeon-Young

2011-12-01

Exhaust manifolds are subjected to an environment in which heating and cooling cycles occur due to the running pattern of automotive engines. This temperature profile results in the repeated bending stress of exhaust pipes. Therefore, among high-temperature characteristics, the bending fatigue strength is an important factor that affects the lifespan of exhaust manifolds. Here, we report on the effect of the alloy composition, namely the weight fraction of the elements Cr, Mo, Nb, and Ti, on the high-temperature bending fatigue strength of the ferritic stainless steel used in exhaust manifolds. Little difference in the tensile strength and bending fatigue strength of the different composition steels was observed below 600 °C, with the exception of the low-Cr steel. However, steels with high Cr, Mo, or Nb fractions showed considerably larger bending fatigue strength at temperatures of 800 °C. After heating, the precipitates from the specimens were extracted electrolytically and analyzed using scanning electron microscopy energy dispersive spectrometry and transmission electron microscopy. Alloying with Cr and Mo was found to increase the bending fatigue strength due to the substitutional solid solution effect, while alloying with Nb enhanced the strength by forming fine intermetallic compounds, including NbC and Fe2Nb.

49 CFR 195.112 - New pipe.

Code of Federal Regulations, 2013 CFR

2013-10-01

... with the following: (a) The pipe must be made of steel of the carbon, low alloy-high strength, or alloy... sets forth the chemical requirements for the pipe steel and mechanical tests for the pipe to provide... made, the specified minimum yield strength or grade, and the pipe size. The marking must be applied in...

49 CFR 195.112 - New pipe.

Code of Federal Regulations, 2012 CFR

2012-10-01

... with the following: (a) The pipe must be made of steel of the carbon, low alloy-high strength, or alloy... sets forth the chemical requirements for the pipe steel and mechanical tests for the pipe to provide... made, the specified minimum yield strength or grade, and the pipe size. The marking must be applied in...

49 CFR 195.112 - New pipe.

Code of Federal Regulations, 2014 CFR

2014-10-01

... with the following: (a) The pipe must be made of steel of the carbon, low alloy-high strength, or alloy... sets forth the chemical requirements for the pipe steel and mechanical tests for the pipe to provide... made, the specified minimum yield strength or grade, and the pipe size. The marking must be applied in...

49 CFR 195.112 - New pipe.

Code of Federal Regulations, 2011 CFR

2011-10-01

... with the following: (a) The pipe must be made of steel of the carbon, low alloy-high strength, or alloy... sets forth the chemical requirements for the pipe steel and mechanical tests for the pipe to provide... made, the specified minimum yield strength or grade, and the pipe size. The marking must be applied in...

49 CFR 195.112 - New pipe.

Code of Federal Regulations, 2010 CFR

2010-10-01

... with the following: (a) The pipe must be made of steel of the carbon, low alloy-high strength, or alloy... sets forth the chemical requirements for the pipe steel and mechanical tests for the pipe to provide... made, the specified minimum yield strength or grade, and the pipe size. The marking must be applied in...

Study of the Impact of Heat Treatment Modes on Formation of Microstructure and a Given Set of Mechanical Properties of High-Strength Flat Products with Guaranteed Hardness (400 to 450 HB) from Low-Alloyed Steel

NASA Astrophysics Data System (ADS)

Matrosov, M. Yu; Martynov, P. G.; Goroshko, T. V.; Zvereva, M. I.; Mitrofanov, A. V.; Barabash, K. Yu

2017-12-01

The results of the study of influence of heat treatment modes on microstructure, size and shape of grains, mechanical properties of high-strength flat products from low-alloyed C-Mn-Cr-Si-Mo steel microalloyed by boron are presented. Heat treatment modes, which provide a combination of high impact viscosity at negative temperatures and guaranteed hardness, are determined.

Superplasticity in a lean Fe-Mn-Al steel.

PubMed

Han, Jeongho; Kang, Seok-Hyeon; Lee, Seung-Joon; Kawasaki, Megumi; Lee, Han-Joo; Ponge, Dirk; Raabe, Dierk; Lee, Young-Kook

2017-09-29

Superplastic alloys exhibit extremely high ductility (>300%) without cracks when tensile-strained at temperatures above half of their melting point. Superplasticity, which resembles the flow behavior of honey, is caused by grain boundary sliding in metals. Although several non-ferrous and ferrous superplastic alloys are reported, their practical applications are limited due to high material cost, low strength after forming, high deformation temperature, and complicated fabrication process. Here we introduce a new compositionally lean (Fe-6.6Mn-2.3Al, wt.%) superplastic medium Mn steel that resolves these limitations. The medium Mn steel is characterized by ultrafine grains, low material costs, simple fabrication, i.e., conventional hot and cold rolling, low deformation temperature (ca. 650 °C) and superior ductility above 1300% at 850 °C. We suggest that this ultrafine-grained medium Mn steel may accelerate the commercialization of superplastic ferrous alloys.Research in new alloy compositions and treatments may allow the increased strength of mass-produced, intricately shaped parts. Here authors introduce a superplastic medium manganese steel which has an inexpensive lean chemical composition and which is suited for conventional manufacturing processes.

Laser beam welding of new ultra-high strength and supra-ductile steels

NASA Astrophysics Data System (ADS)

Dahmen, Martin

2015-03-01

Ultra-high strength and supra-ductile are entering fields of new applications. Those materials are excellent candidates for modern light-weight construction and functional integration. As ultra-high strength steels the stainless martensitic grade 1.4034 and the bainitic steel UNS 53835 are investigated. For the supra-ductile steels stand two high austenitic steels with 18 and 28 % manganese. As there are no processing windows an approach from the metallurgical base on is required. Adjusting the weld microstructure the Q+P and the QT steels require weld heat treatment. The HSD steel is weldable without. Due to their applications the ultra-high strength steels are welded in as-rolled and strengthened condition. Also the reaction of the weld on hot stamping is reflected for the martensitic grades. The supra-ductile steels are welded as solution annealed and work hardened by 50%. The results show the general suitability for laser beam welding.

Fracture Behavior of Ultra-Low-Carbon Steel Plate and Heat-Affected-Zone.

DTIC Science & Technology

1990-12-01

ferrite . This effect on the transformation kinetics of steel is shown in Fig. 2. This alloying addition, however, has experienced...V-notch ITT of -76’F (-600C). The design philo.ophy used for this alloy required that the steel be low carbon with a nearly 100% acicular ferrite ...line pipe fitting steel by International Nickel Company and was called IN 787. It is a low carbon-manganese steel strengthened with a fine precipitate

Characterization of welded HP 9-4-30 steel for the advanced solid rocket motor

NASA Technical Reports Server (NTRS)

Watt, George William

1990-01-01

Solid rocket motor case materials must be high-strength, high-toughness, weldable alloys. The Advanced Solid Rocket Motor (ASRM) cases currently being developed will be made from a 9Ni-4Co quench and temper steel called HP 9-4-30. These ultra high-strength steels must be carefully processed to give a very clean material and a fine grained microstructure, which insures excellent ductility and toughness. The HP 9-4-30 steels are vacuum arc remelted and carbon deoxidized to give the cleanliness required. The ASRM case material will be formed into rings and then welded together to form the case segments. Welding is the desired joining technique because it results in a lower weight than other joining techniques. The mechanical and corrosion properties of the weld region material were fully studied.

Investigation of the plastic fracture of high strength steels

NASA Technical Reports Server (NTRS)

Cox, T. B.; Low, J. R., Jr.

1972-01-01

An investigation of the plastic fracture process to improve tensile strength in high strength steels is presented. Two generic types of steels are considered: a quenched and tempered grade and a maraging grade, in order to compare two different matrix microstructures. Each type of steel was studied in commercial grade purity and in special melted high purity form, low in residual and impurity elements. The specific alloys dealt with include AISI 4340 and 18 Ni, 200 grade maraging steel, both heat treated to the same yield strength level of approximately 200 ksi.

High Resolution Orientation Imaging Microscopy

DTIC Science & Technology

2012-05-02

Structure of In-Situ Deformations of Steel , TMS, San Diego, 2011 13. Jay Basinger, David Fullwood, Brent Adams, EBSD Detail Extraction for Greater Spatial...Its use has contributed to the development of new steels , aluminum alloys, high TC superconductors, electronic materials, lead-free solders, optical...Resolution The simulated pattern method has been used to recover lattice tetragonality in high-strength low- alloy steels . Since the level of

Low-carbon martensitic steels. Alloying and properties

NASA Astrophysics Data System (ADS)

Kleiner, L. M.; Shatsov, A. A.; Larinin, D. M.

2011-03-01

Requirements on the structure of a steel with structural strength and a set of characteristics higher than those of medium-carbon steels with a structure of tempered sorbite are formulated. Principles for choosing compositions for process-adaptable low-carbon martensitic steels are presented. The combination of carbon and alloying elements providing high stability of austenite in the ranges of normal and intermediate transformations is determined, which makes it possible to obtain lath martensite in slow cooling.

Self-Pierce Riveting Through 3 Sheet Metal Combinations

DOE Office of Scientific and Technical Information (OSTI.GOV)

Andersson, Roger; Jonason, Paul; Pettersson, Tommy

2011-05-04

One way to reduce the CO{sub 2} emissions in automotives is to reduce the weight of the Body-In-White. One easy to achieve the weight reduction is to replace steel sheet materials with Al alloys, which is 3 times lighter. One issue is the joining process, especially with combinations between steel grades and AL alloys. Example of combination of mixed material combinations (Al-steel) might be found in the door structure. The reason is because of the AL alloys worthier crash performance so the automotive manufacturer might want to use crash impact beams made by high strength steels in a AL intensivemore » door structure. The joining process between aluminum and steel are problematic due it's not possible to use traditional spot-welding technologies due to the materials total difference in microstructure characteristics as well thermal properties. To overcome this issue then mechanical as well adhesion joining are frequently used. This paper describes a development process and subsequently analysis of a self-pierce rivet (SPR) process between 3 sheet metal combinations. The multi-material combinations in this study were a combination of ultra high strength steels sheets (DP1000) and a Al-alloy (AA 6014). The analysis of the SPR process, in sense of mechanical strengths, has been done by peel- and shear tests. To reduce the amount of future physical tests a virtual FE-model has been developed for the process. This FE model of the process has been subsequently used to analyze the mechanical strength during plastic deformation. By using inverse analysis a correct contact algorithm has been evaluated that would predict the binding force between the rivet and sheet under a deformation process. With this new virtual model it will not only possible to analyze and develop the SPR process but also to achieve the final strength of the joint.« less

The influence of the corrosion product layer generated on the high strength low-alloy steels welded by underwater wet welding with stainless steel electrodes in seawater

NASA Astrophysics Data System (ADS)

Bai, Qiang; Zou, Yan; Kong, Xiangfeng; Gao, Yang; Dong, Sheng; Zhang, Wei

2017-02-01

The high strength low-alloy steels are welded by underwater wet welding with stainless steel electrodes. The micro-structural and electrochemical corrosion study of base metal (BM), weld zone (WZ) and heat affected zone (HAZ) are carried out to understand the influence of the corrosion product layer generated on the high strength low-alloy steels welded by underwater wet welding with stainless steel electrodes, methods used including, potentiodynamic polarization, electrochemical impedance spectroscopy (EIS) and scanning electron microscope (SEM). The results indicate that the WZ acts as a cathode and there is no corrosion product on it throughout the immersion period in seawater. The HAZ and BM acts as anodes. The corrosion rates of the HAZ and BM change with the immersion time increasing. In the initial immersion period, the HAZ has the highest corrosion rate because it has a coarse tempered martensite structure and the BM exhibites a microstructure with very fine grains of ferrite and pearlite. After a period of immersion, the BM has the highest corrosion rate. The reason is that the corrosion product layer on the HAZ is dense and has a better protective property while that on the BM is loose and can not inhibit the diffusion of oxygen.

Evaluation of the stress corrosion cracking resistance of several high strength low alloy steels

NASA Technical Reports Server (NTRS)

Humphries, T. S.; Nelson, E. E.

1980-01-01

The stress corrosion cracking resistance was studied for high strength alloy steels 4130, 4340, for H-11 at selected strength levels, and for D6AC and HY140 at a single strength. Round tensile and C-ring type specimens were stressed up to 100 percent of their yield strengths and exposed to alternate immersion in salt water, salt spray, the atmosphere at Marshall Space Flight Center, and the seacoast at Kennedy Space Center. Under the test conditions, 4130 and 4340 steels heat treated to a tensile strength of 1240 MPa (180 ksi), H-11 and D6AC heat treated to a tensile strength of 1450 MPa (210 ksi), and HY140 (1020 MPa, 148 ksi) are resistant to stress corrosion cracking because failures were not encountered at stress levels up to 75 percent of their yield strengths. A maximum exposure period of one month for alternate immersion in salt water or salt spray and three months for seacoast is indicated for alloy steel to avoid false indications of stress corrosion cracking because of failure resulting from severe pitting.

Influence of Al content on the corrosion resistance of micro-alloyed hot rolled steel as a function of grain size

NASA Astrophysics Data System (ADS)

Qaban, Abdullah; Naher, Sumsun

2018-05-01

High-strength low-alloy steel (HSLA) has been widely used in many applications involving automobiles, aerospace, construction, and oil and gas pipelines due to their enhanced mechanical and chemical properties. One of the most critical elements used to improve these properties is Aluminium. This work will explore the effect of Al content on the corrosion behaviour of hot rolled high-strength low-alloy steel as a function of grain size. The method of investigation employed was weight loss technique. It was obvious that the increase in Al content enhanced corrosion resistance through refinement of grain size obtained through AlN precipitation by pinning grain boundaries and hindering their growth during solidification which was found to be beneficial in reducing corrosion rate.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tanaka, T.; Kameyama, M.; Urabe, Y.

At present, cast duplex stainless steel has been used for the primary coolant piping of PWRs in Japan and joints of dissimilar material have been applied for welding to reactor vessels and steam generators. For the primary coolant piping of the next APWR plants, application of low alloy steel that results in designing main loops with the same material is being studied. It means that there is no need to weld low alloy steel with stainless steel and that makes it possible to reduce the welding length. Attenuation of Ultra Sonic Wave Intensity is lower for low alloy steel thanmore » for stainless steel and they have advantageous inspection characteristics. In addition to that, the thermal expansion rate is smaller for low alloy steel than for stainless steel. In consideration of the above features of low alloy steel, the overall reliability of primary coolant piping is expected to be improved. Therefore, for the evaluation of crack stability of low alloy steel piping to be applied for primary loops, elastic-plastic future mechanics analysis was performed by means of a three-dimensioned FEM. The evaluation results for the low alloy steel pipings show that cracks will not grow into unstable fractures under maximum design load conditions, even when such a circumferential crack is assumed to be 6 times the size of the wall thickness.« less

Effect of Q&P heat treatment on fine microstructure and mechanical properties of a low-alloy medium-carbon steel

NASA Astrophysics Data System (ADS)

Jafari, Rahim; Kheirandish, Shahram; Mirdamadi, Shamsoddin

2018-01-01

The current research investigates the effect of ultrafine microstructure resulted from Quench and Partitioning (Q&P) process on obtaining ultra-high strengths in a low-alloy steel with 4wt.% carbon. The purpose of Q&P heat treatment is to enrich the austenite with carbon by partitioning of carbon from supersaturated martensite to austenite, in order to stabilize it to the room temperature. The microstructure, consequently, is consists of martensite, retained austenite and in some conditions bainite. Two-step Q&P heat treatment with quench and partitioning temperatures equal to 120°C and 300°C respectively were applied to the samples at different times. Mechanical behavior was studied by tensile test. The microstructure of the samples was observed using SEM, and TEM and to quantify the amount of retained austenite X-ray diffraction was used. The retained austenite grain size was estimated to be about 0.5 µm and the highest amount of retained austenite obtained was 10 vol%. All samples showed a yield strength and a tensile strength of above 900MPa and 1500MP respectively. The yield strength increased with increase in partitioning time, whereas tensile strength showed an inverse behavior. The elongation in samples varied from 5% to 9% which seemed to not have a direct connection with the amount of retained austenite, but instead it was related to the ferritic structures formed during partitioning such as coalesced martensite, bainite and tempered martensite.

The Bendability of Ultra High strength Steels

NASA Astrophysics Data System (ADS)

Hazra, S. K.; Efthymiadis, P.; Alamoudi, A.; Kumar, R. L. V.; Shollock, B.; Dashwood, R.

2016-08-01

Automotive manufacturers have been reducing the weight of their vehicles to meet increasingly stringent environmental legislation that reflects public demand. A strategy is to use higher strength materials for parts with reduced cross-sections. However, such materials are less formable than traditional grades. The frequent result is increased processing and piece costs. 3D roll forming is a novel and flexible process: it is estimated that a quarter of the structure of a vehicle can be made with a single set of tooling. Unlike stamping, this process requires material with low work hardening rates. In this paper, we present results of ultra high strength steels that have low elongation in a tension but display high formability in bending through the suppression of the necking response.

Corrosion and Fatigue Behavior of High-Strength Steel Treated with a Zn-Alloy Thermo-diffusion Coating

NASA Astrophysics Data System (ADS)

Mulligan, C. P.; Vigilante, G. N.; Cannon, J. J.

2017-11-01

High and low cycle fatigue tests were conducted on high-strength steel using four-point bending. The materials tested were ASTM A723 steel in the as-machined condition, grit-blasted condition, MIL-DTL-16232 heavy manganese phosphate-coated condition, and ASTM A1059 Zn-alloy thermo-diffusion coated (Zn-TDC). The ASTM A723 steel base material exhibits a yield strength of 1000 MPa. The effects of the surface treatments versus uncoated steel were examined. The fatigue life of the Zn-TDC specimens was generally reduced on as-coated specimens versus uncoated or phosphate-coated specimens. Several mechanisms are examined including the role of compressive residual stress relief with the Zn-TDC process as well as fatigue crack initiation from the hardened Zn-Fe alloy surface layer produced in the gas-metal reaction. Additionally, the effects of corrosion pitting on the fatigue life of coated specimens are explored as the Zn-TDC specimens exhibit significantly improved corrosion resistance over phosphate-coated and oiled specimens.

A Study of the Microstructural Basis for the Strength and Toughness Properties of Overaged HSLA-100 Steel

DTIC Science & Technology

1991-06-01

series, though, HSLA steels possess excellent weld characteristics. These low carbon martensite /bainite alloys have lower carbon levels resulting in...Ref l:p. 31 [Ref 3:p. 64]. HSLA-100 is a solution treated, quenched and aged, low carbon, copper precipitation strengthened steel designed to meet the...and aged, highly weldable, low carbon, copper precipitation strengthened steel designed to achieve a yield strength of 690 MPa. The chemical composition

High-Cycle Fatigue of High-Strength Low Alloy Steel Q345 Subjected to Immersion Corrosion for Mining Wheel Applications

NASA Astrophysics Data System (ADS)

Dicecco, Sante; Altenhof, William; Hu, Henry; Banting, Richard

2017-04-01

In an effort to better understand the impact of material degradation on the fatigue life of mining wheels made of a high-strength low alloy carbon steel (Q345), this study seeks to evaluate the effect of surface corrosion on the high-cycle fatigue behavior of the Q345 alloy. The fatigue behavior of the polished and corroded alloy was investigated. Following exposure to a 3.5 wt.% NaCl saltwater solution, polished and corroded fatigue specimens were tested using an R.R. Moore rotating-bending fatigue apparatus. Microstructural analyses via both optical microscopy and scanning electron microscopy (SEM) revealed that one major phase, α-iron phase, ferrite, and one minor phase, colony pearlite, existed in the extracted Q345 alloy. The results of the fatigue testing showed that the polished and corroded specimens had an endurance strength of approximately 295 and 222 MPa, respectively, at 5,000,000 cycles. The corroded surface condition resulted in a decrease in the fatigue strength of the Q345 alloy by 24.6%. Scanning electron microscope fractography indicated that failure modes for polished and corroded fatigue specimens were consistent in the high-cycle low loading fatigue regime. Conversely, SEM fractography of low-cycle high-loading fatigue specimens found considerable differences in fracture surfaces between the corroded and polished fatigue specimens.

Industrial based volume manufacturing of lightweight aluminium alloy panel components with high-strength and complex-shape for car body and chassis structures

NASA Astrophysics Data System (ADS)

Anyasodor, Gerald; Koroschetz, Christian

2017-09-01

To achieve the high volume manufacture of lightweight passenger cars at economic cost as required in the automotive industry, low density materials and new process route will be needed. While high strength aluminium alloy grades: AA7075 and AA6082 may provide the alternative material solution, hot stamping process used for high-strength and ultrahigh strength steels such as boron steel 22mnb5 can enable the volume manufacture of panel components with high-strength and complex-shape for car body and chassis structures. These aluminium alloy grades can be used to manufacture panel components with possible yield strengths ≥ 500 MPa. Due to the differences in material behaviors, hot stamping process of 22mnb5 cannot be directly applied to high strength aluminium alloy grades. Despite recorded successes in laboratories, researches and niche hot forming processes of high strength aluminium alloy grades, not much have been achieved for adequate and efficient volume manufacturing system applicable in the automotive industry. Due to lack of such system and based on expert knowledge in hot stamping production-line, AP&T presents in this paper a hot stamping processing route for high strength aluminium alloys been suitable for production-line development and volume manufacturing.

A comparative assessment of the fracture toughness behavior of ferritic-martensitic steels and nanostructured ferritic alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Byun, Thak Sang; Hoelzer, David T.; Kim, Jeoung Han

The Fe-Cr alloys with ultrafine microstructures are primary candidate materials for advanced nuclear reactor components because of their excellent high temperature strength and high resistance to radiation-induced damage such as embrittlement and swelling. Mainly two types of Fe-Cr alloys have been developed for the high temperature reactor applications: the quenched and tempered ferritic-martensitic (FM) steels hardened primarily by ultrafine laths and carbonitrides and the powder metallurgy-based nanostructured ferritic alloys (NFAs) by nanograin structure and nanoclusters. This paper aims at elucidating the differences and similarities in the temperature and strength dependences of fracture toughness in the Fe-Cr alloys to provide amore » comparative assessment of their high-temperature structural performance. The K JQ versus yield stress plots confirmed that the fracture toughness was inversely proportional to yield strength. It was found, however, that the toughness data for some NFAs were outside the band of the integrated dataset at given strength level, which indicates either a significant improvement or deterioration in mechanical properties due to fundamental changes in deformation and fracture mechanisms. When compared to the behavior of NFAs, the FM steels have shown much less strength dependence and formed narrow fracture toughness data bands at a significantly lower strength region. It appeared that at high temperatures ≥600 °C the NFAs cannot retain the nanostructure advantage of high strength and high toughness either by high-temperature embrittlement or by excessive loss of strength. Finally, irradiation studies have revealed, however, that the NFAs have much stronger radiation resistance than tempered martensitic steels, such as lower radiation-induced swelling, finer helium bubble formation, lower irradiation creep rate and reduced low temperature embrittlement.« less

A comparative assessment of the fracture toughness behavior of ferritic-martensitic steels and nanostructured ferritic alloys

DOE PAGES

Byun, Thak Sang; Hoelzer, David T.; Kim, Jeoung Han; ...

2016-12-07

The Fe-Cr alloys with ultrafine microstructures are primary candidate materials for advanced nuclear reactor components because of their excellent high temperature strength and high resistance to radiation-induced damage such as embrittlement and swelling. Mainly two types of Fe-Cr alloys have been developed for the high temperature reactor applications: the quenched and tempered ferritic-martensitic (FM) steels hardened primarily by ultrafine laths and carbonitrides and the powder metallurgy-based nanostructured ferritic alloys (NFAs) by nanograin structure and nanoclusters. This paper aims at elucidating the differences and similarities in the temperature and strength dependences of fracture toughness in the Fe-Cr alloys to provide amore » comparative assessment of their high-temperature structural performance. The K JQ versus yield stress plots confirmed that the fracture toughness was inversely proportional to yield strength. It was found, however, that the toughness data for some NFAs were outside the band of the integrated dataset at given strength level, which indicates either a significant improvement or deterioration in mechanical properties due to fundamental changes in deformation and fracture mechanisms. When compared to the behavior of NFAs, the FM steels have shown much less strength dependence and formed narrow fracture toughness data bands at a significantly lower strength region. It appeared that at high temperatures ≥600 °C the NFAs cannot retain the nanostructure advantage of high strength and high toughness either by high-temperature embrittlement or by excessive loss of strength. Finally, irradiation studies have revealed, however, that the NFAs have much stronger radiation resistance than tempered martensitic steels, such as lower radiation-induced swelling, finer helium bubble formation, lower irradiation creep rate and reduced low temperature embrittlement.« less

A comparative assessment of the fracture toughness behavior of ferritic-martensitic steels and nanostructured ferritic alloys

NASA Astrophysics Data System (ADS)

Byun, Thak Sang; Hoelzer, David T.; Kim, Jeoung Han; Maloy, Stuart A.

2017-02-01

The Fe-Cr alloys with ultrafine microstructures are primary candidate materials for advanced nuclear reactor components because of their excellent high temperature strength and high resistance to radiation-induced damage such as embrittlement and swelling. Mainly two types of Fe-Cr alloys have been developed for the high temperature reactor applications: the quenched and tempered ferritic-martensitic (FM) steels hardened primarily by ultrafine laths and carbonitrides and the powder metallurgy-based nanostructured ferritic alloys (NFAs) by nanograin structure and nanoclusters. This study aims at elucidating the differences and similarities in the temperature and strength dependences of fracture toughness in the Fe-Cr alloys to provide a comparative assessment of their high-temperature structural performance. The KJQ versus yield stress plots confirmed that the fracture toughness was inversely proportional to yield strength. It was found, however, that the toughness data for some NFAs were outside the band of the integrated dataset at given strength level, which indicates either a significant improvement or deterioration in mechanical properties due to fundamental changes in deformation and fracture mechanisms. When compared to the behavior of NFAs, the FM steels have shown much less strength dependence and formed narrow fracture toughness data bands at a significantly lower strength region. It appeared that at high temperatures ≥600 °C the NFAs cannot retain the nanostructure advantage of high strength and high toughness either by high-temperature embrittlement or by excessive loss of strength. Irradiation studies have revealed, however, that the NFAs have much stronger radiation resistance than tempered martensitic steels, such as lower radiation-induced swelling, finer helium bubble formation, lower irradiation creep rate and reduced low temperature embrittlement.

Study on Phase Stability of New Ni Based Superalloy Less 1 Designed to Low the ETA and Sigma Phase Fraction at 700 °C

NASA Astrophysics Data System (ADS)

Youn, Jeong Il; Shin, Yong Kwan; Kang, Byung Il; Kim, Young Jig; Suk, Jhin Ik; Ryu, Seok Hyeon

The alloys required for fossil power plants are altered from stainless steel that has been used below 600 °C to Ni-based alloy that can operate over 700 °C for advanced ultra super critical (A-USC) steam turbine. The IN 740 alloy is proposed for improved rupture strength and corrosion resistance at high temperature. However, previous studies with experiments and simulations on stable phases at over 700 °C have indicated the formation of the eta phase with the wasting of the gamma prime phase, which is the most important reinforced phase in precipitation hardened Ni alloys. This results in the formation of precipitation free zones to decrease the strength. LESS 1 alloy designed through some modifications of IN 740 was suggested in this study. LESS 1 showed the phase stability more than IN 740 due to the optimum composition of Cr, Mo, Ti and Al. The experimental results established that a needle-shaped eta phase was formed in the grain boundary and it grew to intra-grain, and a precipitation free zone was also observed in IN 740, but these defects were entirely controlled in LESS 1.

Experimental investigation of the effect of surface markings on the mechanical integrity of weathering bridge steels : [summary].

DOT National Transportation Integrated Search

2014-11-01

High-strength low-alloy steel (HSLA) weathering : steels are the conventional choice for fracture-critical members in bridge construction. HSLA : weathering steels offer superior corrosion : resistance, important in Floridas humid and : coastal en...

Metallurgy: A compilation

NASA Technical Reports Server (NTRS)

1973-01-01

A technology utilization program is presented for the dissemination of information on technological developments which have potential utility outside the aerospace and nuclear communities. Discussion is restricted to the effects of hydrogen on a variety of metal alloys, and the mechanical properties of some recently developed alloys. Hydrogen at both low and high pressure is shown to have adverse effects on alloys such as ultrahigh-strength steels, irradiated steels, columbium, inconel alloys, titanium alloys, and certain stainless steels. The mechanical and physical properties of a wide range of alloys, their performance at elevated temperatures, and some of the processes involved in their development are also considered.

An investigation of laser cutting quality of 22MnB5 ultra high strength steel using response surface methodology

NASA Astrophysics Data System (ADS)

Tahir, Abdul Fattah Mohd; Aqida, Syarifah Nur

2017-07-01

In hot press forming, changes of mechanical properties in boron steel blanks have been a setback in trimming the final shape components. This paper presents investigation of kerf width and heat affected zone (HAZ) of ultra high strength 22MnB5 steel cutting. Sample cutting was conducted using a 4 kW Carbon Dioxide (CO2) laser machine with 10.6 μm wavelength with the laser spot size of 0.2 mm. A response surface methodology (RSM) using three level Box-Behnken design of experiment was developed with three factors of peak power, cutting speed and duty cycle. The parameters were optimised for minimum kerf width and HAZ formation. Optical evaluation using MITUTOYO TM 505 were conducted to measure the kerf width and HAZ region. From the findings, laser duty cycle was crucial to determine cutting quality of ultra-high strength steel; followed by cutting speed and laser power. Meanwhile, low power intensity with continuous wave contributes the narrowest kerf width formation and least HAZ region.

Effect of Multistage Heat Treatment on Microstructure and Mechanical Properties of High-Strength Low-Alloy Steel

NASA Astrophysics Data System (ADS)

Liu, Qingdong; Wen, Haiming; Zhang, Han; Gu, Jianfeng; Li, Chuanwei; Lavernia, Enrique J.

2016-05-01

The influence of Cu-rich precipitates (CRPs) and reverted austenite (RA) on the strength and impact toughness of a Cu-containing 3.5 wt pct Ni high-strength low-alloy (HSLA) steel after various heat treatments involving quenching (Q), lamellarization (L), and tempering (T) is studied using electron back-scatter diffraction, transmission electron microscopy, and atom probe tomography. The QT sample exhibits high strength but low impact toughness, whereas the QL samples mostly possess improved impact toughness but moderate strength, but the QLT samples again have degraded impact toughness due to additional tempering. The dispersion of nanoscale CRPs, which are formed during tempering, is responsible for the enhanced strength but simultaneously leads to the degraded impact toughness. The RA formed during lamellarization contributes to the improved impact toughness. Based on the present study, new heat treatment schedules are proposed to balance strength and impact toughness by optimizing the precipitation of CRPs and RA.

Mechanical properties of Fe -10Ni -7Mn martensitic steel subjected to severe plastic deformation via cold rolling and wire drawing

NASA Astrophysics Data System (ADS)

Ghasemi-Nanesa, H.; Nili-Ahmadabadi, M.; Shirazi, H.

2010-07-01

Fe-Ni-Mn martensitic steels are one of the major groups of ultra-high strength steels that have good mechanical properties and ductility in as annealed condition but they suffer from severe inter-granular embitterment after aging. In this paper, the effect of heavy shaped cold rolling and wire drawing on the mechanical properties of Fe-Ni-Mn steel was investigated. This process could provide a large strain deformation in this alloy. The total strain was epsilon ~7. Aging behavior and tensile properties of Fe-10Ni-7Mn were studied after aging at 753 K. The results showed that the ultimate tensile strength and ductility after cold rolling, wire drawing and aging increased up to 2540 MPa and 7.1 %, respectively, while the conventional steels show a premature fracture stress of 830 MPa with about zero ductility after aging.

The Composition and Temperature Effects on the Ultra High Strength Stainless Steel Design

NASA Astrophysics Data System (ADS)

Xu, W.; Del Castillo, P. E. J. Rivera Díaz; van der Zwaag, S.

Alloy composition and heat treatment are of paramount importance to determining alloy properties. Their control is of great importance for new alloy design and industrial fabrication control. A base alloy utilizing MX carbide is designed through a theory guided computational approach coupling a genetic algorithm with optimization criteria based on thermodynamic, kinetic and mechanical principles. The combined effects of 11 alloying elements (Al, C, Co, Cr, Cu, Mo, Nb, Ni, Si, Ti and V) are investigated in terms of the composition optimization criteria: the martensite start (Ms) temperature, the suppression of undesirable phases, the Cr concentration in the matrix and the potency of the precipitation strengthening contribution. The results show the concentration sensitivities of each component and also point out new potential composition domains for further strength increase. The aging temperature effect is studied and the aging temperature industrially followed is recovered.

46 CFR 54.25-10 - Low temperature operation-ferritic steels (replaces UCS-65 through UCS-67).

Code of Federal Regulations, 2013 CFR

2013-10-01

... the following additional requirements: Note: For high alloy steels refer to § 54.25-15. For heat... tempered steels. The ultimate and yield strengths shall be as shown in the applicable specification and... 46 Shipping 2 2013-10-01 2013-10-01 false Low temperature operation-ferritic steels (replaces UCS...

46 CFR 54.25-10 - Low temperature operation-ferritic steels (replaces UCS-65 through UCS-67).

Code of Federal Regulations, 2014 CFR

2014-10-01

... the following additional requirements: Note: For high alloy steels refer to § 54.25-15. For heat... tempered steels. The ultimate and yield strengths shall be as shown in the applicable specification and... 46 Shipping 2 2014-10-01 2014-10-01 false Low temperature operation-ferritic steels (replaces UCS...

46 CFR 54.25-10 - Low temperature operation-ferritic steels (replaces UCS-65 through UCS-67).

Code of Federal Regulations, 2012 CFR

2012-10-01

... the following additional requirements: Note: For high alloy steels refer to § 54.25-15. For heat... tempered steels. The ultimate and yield strengths shall be as shown in the applicable specification and... 46 Shipping 2 2012-10-01 2012-10-01 false Low temperature operation-ferritic steels (replaces UCS...

Aircraft landing dynamics facility carriage weld test program

NASA Technical Reports Server (NTRS)

Lawson, A. G.

1984-01-01

A welded tubular structure constructed of low alloy high strength quenched and tempered steel was tested. The consistency of the mechanical strengths and chemical composition and the degree of difficulty of obtaining full strength welds with these steels is characterized. The results of constructing and testing two typical connections which are used in the structure design are reported.

Grain refinement of high strength steels to improve cryogenic toughness

NASA Technical Reports Server (NTRS)

Rush, H. F.

1985-01-01

Grain-refining techniques using multistep heat treatments to reduce the grain size of five commercial high-strength steels were investigated. The goal of this investigation was to improve the low-temperature toughness as measured by Charpy V-notch impact test without a significant loss in tensile strength. The grain size of four of five alloys investigated was successfully reduced up to 1/10 of original size or smaller with increases in Charpy impact energy of 50 to 180 percent at -320 F. Tensile properties were reduced from 0 to 25 percent for the various alloys tested. An unexpected but highly beneficial side effect from grain refining was improved machinability.

Improvement of corrosion resistance of low-alloy steels by resurfacing using multifunction cavitation in water

NASA Astrophysics Data System (ADS)

Ijiri, Masataka; Yoshimura, Toshihiko

2018-02-01

Low-alloy steels are based on carbon steel in combination with several percent or less (in many cases, 1 mass%) alloying elements, and they offer improved resistance to corrosion at a cost slightly higher than that of carbon steel. However, these materials do not exhibit the same corrosion resistance as stainless steel. The authors have previously developed a novel multifunction cavitation (MFC) technique, which combines ultrasonic cavitation with water jet cavitation. In this study, MFC was used to modify the surface of Cr-Mo steel (SCM435) and Ni-Cr-Mo steel (SNCM630). MFC was found to improve the residual stress value of the material as the result of surface modification while also imparting high strength and superior corrosion resistance.

Naval Structural Materials: Requirements, Issues, and Opportunities.

DTIC Science & Technology

1981-04-10

because of the alloy’s relatively good corrosion resistance at high strength levels. The data 0 of Fig. 5 show the effects of electrochemical potential...STRENGTH,a-y (ksi) Fig. 5 Stress corrosion cracking data for high strength stainless steel (17-4PH) of different yield strengths under four electrochemical ... behavior . In contrast to the previously discussed results for low-carbon steel , heat treatment has only a small effect on the fatigue behavior of either

Factors Affecting the Strength and Toughness of Ultra-Low Carbon Steel Weld Metal

DTIC Science & Technology

1999-12-01

ferrite or martensite due to its strength and toughness, respectively. Ferrite with non-aligned second phase is associated with ferrite completely...with interphase carbides and pearlite. It forms at high temperatures and slow cooling rates than ferrite with secondary phase or martensite . It is...therefore termed a diffusionless transformation . In low carbon steels, the transformation occurs from fccy (austenite) to beta’ ( martensite ),

Microstructural design in low alloy steels

NASA Technical Reports Server (NTRS)

Honeycombe, R. W. K.

1982-01-01

The evolution of microalloyed steels from plain carbon steels is examined with emphasis on grain size control by use of Nb, Ti and V additions and by the application of controlled rolling. The structural changes during controlled rolling are described as well as the influence of alloying elements on these changes, and on the final microstructure. The achievement of high strength and toughness is discussed including the role of inclusions.

Study of austenitic stainless steel welded with low alloy steel filler metal. [tensile and impact strength tests

NASA Technical Reports Server (NTRS)

Burns, F. A.; Dyke, R. A., Jr.

1979-01-01

The tensile and impact strength properties of 316L stainless steel plate welded with low alloy steel filler metal were determined. Tests were conducted at room temperature and -100 F on standard test specimens machined from as-welded panels of various chemical compositions. No significant differences were found as the result of variations in percentage chemical composition on the impact and tensile test results. The weldments containing lower chromium and nickel as the result of dilution of parent metal from the use of the low alloy steel filler metal corroded more severely in a marine environment. The use of a protective finish, i.e., a nitrile-based paint containing aluminum powder, prevented the corrosive attack.

Ultrastrong steel via minimal lattice misfit and high-density nanoprecipitation

NASA Astrophysics Data System (ADS)

Jiang, Suihe; Wang, Hui; Wu, Yuan; Liu, Xiongjun; Chen, Honghong; Yao, Mengji; Gault, Baptiste; Ponge, Dirk; Raabe, Dierk; Hirata, Akihiko; Chen, Mingwei; Wang, Yandong; Lu, Zhaoping

2017-04-01

Next-generation high-performance structural materials are required for lightweight design strategies and advanced energy applications. Maraging steels, combining a martensite matrix with nanoprecipitates, are a class of high-strength materials with the potential for matching these demands. Their outstanding strength originates from semi-coherent precipitates, which unavoidably exhibit a heterogeneous distribution that creates large coherency strains, which in turn may promote crack initiation under load. Here we report a counterintuitive strategy for the design of ultrastrong steel alloys by high-density nanoprecipitation with minimal lattice misfit. We found that these highly dispersed, fully coherent precipitates (that is, the crystal lattice of the precipitates is almost the same as that of the surrounding matrix), showing very low lattice misfit with the matrix and high anti-phase boundary energy, strengthen alloys without sacrificing ductility. Such low lattice misfit (0.03 ± 0.04 per cent) decreases the nucleation barrier for precipitation, thus enabling and stabilizing nanoprecipitates with an extremely high number density (more than 1024 per cubic metre) and small size (about 2.7 ± 0.2 nanometres). The minimized elastic misfit strain around the particles does not contribute much to the dislocation interaction, which is typically needed for strength increase. Instead, our strengthening mechanism exploits the chemical ordering effect that creates backstresses (the forces opposing deformation) when precipitates are cut by dislocations. We create a class of steels, strengthened by Ni(Al,Fe) precipitates, with a strength of up to 2.2 gigapascals and good ductility (about 8.2 per cent). The chemical composition of the precipitates enables a substantial reduction in cost compared to conventional maraging steels owing to the replacement of the essential but high-cost alloying elements cobalt and titanium with inexpensive and lightweight aluminium. Strengthening of this class of steel alloy is based on minimal lattice misfit to achieve maximal precipitate dispersion and high cutting stress (the stress required for dislocations to cut through coherent precipitates and thus produce plastic deformation), and we envisage that this lattice misfit design concept may be applied to many other metallic alloys.

Ultrastrong steel via minimal lattice misfit and high-density nanoprecipitation.

PubMed

Jiang, Suihe; Wang, Hui; Wu, Yuan; Liu, Xiongjun; Chen, Honghong; Yao, Mengji; Gault, Baptiste; Ponge, Dirk; Raabe, Dierk; Hirata, Akihiko; Chen, Mingwei; Wang, Yandong; Lu, Zhaoping

2017-04-27

Next-generation high-performance structural materials are required for lightweight design strategies and advanced energy applications. Maraging steels, combining a martensite matrix with nanoprecipitates, are a class of high-strength materials with the potential for matching these demands. Their outstanding strength originates from semi-coherent precipitates, which unavoidably exhibit a heterogeneous distribution that creates large coherency strains, which in turn may promote crack initiation under load. Here we report a counterintuitive strategy for the design of ultrastrong steel alloys by high-density nanoprecipitation with minimal lattice misfit. We found that these highly dispersed, fully coherent precipitates (that is, the crystal lattice of the precipitates is almost the same as that of the surrounding matrix), showing very low lattice misfit with the matrix and high anti-phase boundary energy, strengthen alloys without sacrificing ductility. Such low lattice misfit (0.03 ± 0.04 per cent) decreases the nucleation barrier for precipitation, thus enabling and stabilizing nanoprecipitates with an extremely high number density (more than 10 24 per cubic metre) and small size (about 2.7 ± 0.2 nanometres). The minimized elastic misfit strain around the particles does not contribute much to the dislocation interaction, which is typically needed for strength increase. Instead, our strengthening mechanism exploits the chemical ordering effect that creates backstresses (the forces opposing deformation) when precipitates are cut by dislocations. We create a class of steels, strengthened by Ni(Al,Fe) precipitates, with a strength of up to 2.2 gigapascals and good ductility (about 8.2 per cent). The chemical composition of the precipitates enables a substantial reduction in cost compared to conventional maraging steels owing to the replacement of the essential but high-cost alloying elements cobalt and titanium with inexpensive and lightweight aluminium. Strengthening of this class of steel alloy is based on minimal lattice misfit to achieve maximal precipitate dispersion and high cutting stress (the stress required for dislocations to cut through coherent precipitates and thus produce plastic deformation), and we envisage that this lattice misfit design concept may be applied to many other metallic alloys.

Advances in Low Carbon, High Strength Ferrous Alloys

DTIC Science & Technology

1993-04-01

35 TABLES 1. Specified chemical compositions and mechanical properties for GMAW/SAW/ GTAW wire electrodes, MIL-XXXS type, for welding...minimum service temperature of +300 F. The chromium and molybdenum additions improved hardenability and promoted the formation of mar- tensite in thick...alloying ele- ments ( chromium , nickel and molybdenum) are required, especially for thick sections. Production of high strength steel plate for military

Electroforming of optical tooling in high-strength Ni-Co alloy

NASA Astrophysics Data System (ADS)

Stein, Berl

2003-05-01

Plastic optics are often mass produced by injection, compression or injection-compression molding. Optical quality molds can be directly machined in appropriate materials (tool steels, electroless nickel, aluminum, etc.), but much greater cost efficiency can be achieved with electroformed modl inserts. Traditionally, electroforming of optical quality mold inserts has been carried out in nickel, a material much softer than tool steels which, when hardened to 45 - 50 HRc usually exhibit high wear resistance and long service life (hundreds of thousands of impressions per mold). Because of their low hardness (< 20 HRc), nickel molds can produce only tens of thousands of parts before they are scrapped due to wear or accidental damage. This drawback prevented their wider usage in general plastic and optical mold making. Recently, NiCoForm has developed a proprietary Ni-CO electroforming bath combining the high strength and wear resistance of the alloy with the low stress and high replication fidelity typical of pure nickel electroforming. This paper will outline the approach to electroforming of optical quality tooling in low stress, high strength Ni-Co alloy and present several examples of electroformed NiColoy mold inserts.

Grain-refining heat treatments to improve cryogenic toughness of high-strength steels

NASA Technical Reports Server (NTRS)

Rush, H. F.

1984-01-01

The development of two high Reynolds number wind tunnels at NASA Langley Research Center which operate at cryogenic temperatures with high dynamic pressures has imposed severe requirements on materials for model construction. Existing commercial high strength steels lack sufficient toughness to permit their safe use at temperatures approaching that of liquid nitrogen (-320 F). Therefore, a program to improve the cryogenic toughness of commercial high strength steels was conducted. Significant improvement in the cryogenic toughness of commercial high strength martensitic and maraging steels was demonstrated through the use of grain refining heat treatments. Charpy impact strength at -320 F was increased by 50 to 180 percent for the various alloys without significant loss in tensile strength. The grain sizes of the 9 percent Ni-Co alloys and 200 grade maraging steels were reduced to 1/10 of the original size or smaller, with the added benefit of improved machinability. This grain refining technique should permit these alloys with ultimate strengths of 220 to 270 ksi to receive consideration for cryogenic service.

Micromechanisms of Fracture and Crack Arrest in Two High Strength Steels.

DTIC Science & Technology

1987-02-01

martensitic RY-80, and low -carbon, copper precipitation -hardened ferritic alloy ASTM A710 Gr. A Cl. 3...enriched clusters which subsequently transform into epsilon- phase copper particles near peak hardness [Hornbogen, 1964; Goodman, et al. 1973a; Krishnadev...3-Ni te 1 and a copper precipitat Ion strengthened low carbon ferritic steel( KMIN’ATWOdr>A- ..-3 possessing similar yield \\strengths was

Performance Steel Castings

DTIC Science & Technology

2012-09-30

Development of Sand Properties 103 Advanced Modeling Dataset.. 105 High Strength Low Alloy (HSLA) Steels 107 Steel Casting and Engineering Support...to achieve the performance goals required for new systems. The dramatic reduction in weight and increase in capability will require high performance...for improved weapon system reliability. SFSA developed innovative casting design and manufacturing processes for high performance parts. SFSA is

High-Strength Aluminum Casting Alloy for High-Temperature Applications (MSFC Center Director's Discretionary Fund Final Project No. 97-10)

NASA Technical Reports Server (NTRS)

Lee, J. A.

1998-01-01

A new aluminum-silicon alloy has been successfully developed at Marshall Space Flight Center that has a significant improvement in tensile strength at elevated temperatures (550 to 700 F). For instance, the new alloy shows in average tensile strength of at least 90 percent higher than the current 390 aluminum piston alloy tested at 500 F. Compared to conventional aluminum alloys, automotive engines using the new piston alloy will have improved gas mileage, and may produce less air pollution in order to meet the future U.S. automotive legislative requirements for low hydrocarbon emissions. The projected cost for this alloy is less than $0.95/lb, and it readily allows the automotive components to be cast at a high production volume with a low, fully accounted cost. It is economically produced by pouring molten metal directly into conventional permanent steel molds or die casting.

77 FR 69790 - Certain Hot-Rolled Carbon Steel Flat Products From the People's Republic of China: Final Results...

Federal Register 2010, 2011, 2012, 2013, 2014

2012-11-21

... fully stabilized; high strength low alloy; and the substrate for motor lamination steel may also enter... Steel Flat Products From the People's Republic of China: Final Results and Final No Shipments... antidumping duty order on certain hot- rolled carbon steel flat products (``hot-rolled steel'') from the...

49 CFR 179.220-7 - Materials.

Code of Federal Regulations, 2013 CFR

2013-10-01

... indicated minimum tensile strength and elongation in the welded condition. (b) Carbon steel plate: The...) High alloy steel plate: High alloy steel plate must comply with one of the following specifications... Minimum tensile strength (p.s.i.) welded condition 1 Minimum elongation in 2 inches (percent) weld metal...

49 CFR 179.220-7 - Materials.

Code of Federal Regulations, 2012 CFR

2012-10-01

... indicated minimum tensile strength and elongation in the welded condition. (b) Carbon steel plate: The...) High alloy steel plate: High alloy steel plate must comply with one of the following specifications... Minimum tensile strength (p.s.i.) welded condition 1 Minimum elongation in 2 inches (percent) weld metal...

49 CFR 179.220-7 - Materials.

Code of Federal Regulations, 2011 CFR

2011-10-01

... indicated minimum tensile strength and elongation in the welded condition. (b) Carbon steel plate: The...) High alloy steel plate: High alloy steel plate must comply with one of the following specifications... Minimum tensile strength (p.s.i.) welded condition 1 Minimum elongation in 2 inches (percent) weld metal...

49 CFR 179.220-7 - Materials.

Code of Federal Regulations, 2014 CFR

2014-10-01

... indicated minimum tensile strength and elongation in the welded condition. (b) Carbon steel plate: The...) High alloy steel plate: High alloy steel plate must comply with one of the following specifications... Minimum tensile strength (p.s.i.) welded condition 1 Minimum elongation in 2 inches (percent) weld metal...

Stiff, light, strong and ductile: nano-structured High Modulus Steel.

PubMed

Springer, H; Baron, C; Szczepaniak, A; Uhlenwinkel, V; Raabe, D

2017-06-05

Structural material development for lightweight applications aims at improving the key parameters strength, stiffness and ductility at low density, but these properties are typically mutually exclusive. Here we present how we overcome this trade-off with a new class of nano-structured steel - TiB 2 composites synthesised in-situ via bulk metallurgical spray-forming. Owing to the nano-sized dispersion of the TiB 2 particles of extreme stiffness and low density - obtained by the in-situ formation with rapid solidification kinetics - the new material has the mechanical performance of advanced high strength steels, and a 25% higher stiffness/density ratio than any of the currently used high strength steels, aluminium, magnesium and titanium alloys. This renders this High Modulus Steel the first density-reduced, high stiffness, high strength and yet ductile material which can be produced on an industrial scale. Also ideally suited for 3D printing technology, this material addresses all key requirements for high performance and cost effective lightweight design.

Effect of Stress Relief Annealing on Microstructure & Mechanical Properties of Welded Joints Between Low Alloy Carbon Steel and Stainless Steel

NASA Astrophysics Data System (ADS)

Nivas, R.; Das, G.; Das, S. K.; Mahato, B.; Kumar, S.; Sivaprasad, K.; Singh, P. K.; Ghosh, M.

2017-01-01

Two types of welded joints were prepared using low alloy carbon steel and austenitic stainless steel as base materials. In one variety, buttering material and weld metal were Inconel 82. In another type, buttering material and weld metal were Inconel 182. In case of Inconel 82, method of welding was GTAW. For Inconel 182, welding was done by SMAW technique. For one set of each joints after buttering, stress relief annealing was done at 923 K (650 °C) for 90 minutes before further joining with weld metal. Microstructural investigation and sub-size in situ tensile testing in scanning electron microscope were carried out for buttered-welded and buttered-stress relieved-welded specimens. Adjacent to fusion boundary, heat-affected zone of low alloy steel consisted of ferrite-pearlite phase combination. Immediately after fusion boundary in low alloy steel side, there was increase in matrix grain size. Same trend was observed in the region of austenitic stainless steel that was close to fusion boundary between weld metal-stainless steel. Close to interface between low alloy steel-buttering material, the region contained martensite, Type-I boundary and Type-II boundary. Peak hardness was obtained close to fusion boundary between low alloy steel and buttering material. In this respect, a minimum hardness was observed within buttering material. The peak hardness was shifted toward buttering material after stress relief annealing. During tensile testing no deformation occurred within low alloy steel and failure was completely through buttering material. Crack initiated near fusion boundary between low alloy steel-buttering material for welded specimens and the same shifted away from fusion boundary for stress relieved annealed specimens. This observation was at par with the characteristics of microhardness profile. In as welded condition, joints fabricated with Inconel 82 exhibited superior bond strength than the weld produced with Inconel 182. Stress relief annealing reduced the strength of transition joints and the reduction was maximum for specimen welded with Inconel 82.

High-Strength Nanotwinned Al Alloys with 9R Phase.

PubMed

Li, Qiang; Xue, Sichuang; Wang, Jian; Shao, Shuai; Kwong, Anthony H; Giwa, Adenike; Fan, Zhe; Liu, Yue; Qi, Zhimin; Ding, Jie; Wang, Han; Greer, Julia R; Wang, Haiyan; Zhang, Xinghang

2018-03-01

Light-weight aluminum (Al) alloys have widespread applications. However, most Al alloys have inherently low mechanical strength. Nanotwins can induce high strength and ductility in metallic materials. Yet, introducing high-density growth twins into Al remains difficult due to its ultrahigh stacking-fault energy. In this study, it is shown that incorporating merely several atomic percent of Fe solutes into Al enables the formation of nanotwinned (nt) columnar grains with high-density 9R phase in Al(Fe) solid solutions. The nt Al-Fe alloy coatings reach a maximum hardness of ≈5.5 GPa, one of the strongest binary Al alloys ever created. In situ uniaxial compressions show that the nt Al-Fe alloys populated with 9R phase have flow stress exceeding 1.5 GPa, comparable to high-strength steels. Molecular dynamics simulations reveal that high strength and hardening ability of Al-Fe alloys arise mainly from the high-density 9R phase and nanoscale grain sizes. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Additively manufactured hierarchical stainless steels with high strength and ductility.

PubMed

Wang, Y Morris; Voisin, Thomas; McKeown, Joseph T; Ye, Jianchao; Calta, Nicholas P; Li, Zan; Zeng, Zhi; Zhang, Yin; Chen, Wen; Roehling, Tien Tran; Ott, Ryan T; Santala, Melissa K; Depond, Philip J; Matthews, Manyalibo J; Hamza, Alex V; Zhu, Ting

2018-01-01

Many traditional approaches for strengthening steels typically come at the expense of useful ductility, a dilemma known as strength-ductility trade-off. New metallurgical processing might offer the possibility of overcoming this. Here we report that austenitic 316L stainless steels additively manufactured via a laser powder-bed-fusion technique exhibit a combination of yield strength and tensile ductility that surpasses that of conventional 316L steels. High strength is attributed to solidification-enabled cellular structures, low-angle grain boundaries, and dislocations formed during manufacturing, while high uniform elongation correlates to a steady and progressive work-hardening mechanism regulated by a hierarchically heterogeneous microstructure, with length scales spanning nearly six orders of magnitude. In addition, solute segregation along cellular walls and low-angle grain boundaries can enhance dislocation pinning and promote twinning. This work demonstrates the potential of additive manufacturing to create alloys with unique microstructures and high performance for structural applications.

Additively manufactured hierarchical stainless steels with high strength and ductility

NASA Astrophysics Data System (ADS)

Wang, Y. Morris; Voisin, Thomas; McKeown, Joseph T.; Ye, Jianchao; Calta, Nicholas P.; Li, Zan; Zeng, Zhi; Zhang, Yin; Chen, Wen; Roehling, Tien Tran; Ott, Ryan T.; Santala, Melissa K.; Depond, Philip J.; Matthews, Manyalibo J.; Hamza, Alex V.; Zhu, Ting

2018-01-01

Many traditional approaches for strengthening steels typically come at the expense of useful ductility, a dilemma known as strength-ductility trade-off. New metallurgical processing might offer the possibility of overcoming this. Here we report that austenitic 316L stainless steels additively manufactured via a laser powder-bed-fusion technique exhibit a combination of yield strength and tensile ductility that surpasses that of conventional 316L steels. High strength is attributed to solidification-enabled cellular structures, low-angle grain boundaries, and dislocations formed during manufacturing, while high uniform elongation correlates to a steady and progressive work-hardening mechanism regulated by a hierarchically heterogeneous microstructure, with length scales spanning nearly six orders of magnitude. In addition, solute segregation along cellular walls and low-angle grain boundaries can enhance dislocation pinning and promote twinning. This work demonstrates the potential of additive manufacturing to create alloys with unique microstructures and high performance for structural applications.

Improvement of formability of high strength steel sheets in shrink flanging

NASA Astrophysics Data System (ADS)

Hamedon, Z.; Abe, Y.; Mori, K.

2016-02-01

In the shrinkage flanging, the wrinkling tends to occur due to compressive stress. The wrinkling will cause a difficulty in assembling parts, and severe wrinkling may leads to rupture of parts. The shrinkage flange of the ultra-high strength steel sheets not only defects the product by the occurrence of the wrinkling but also causes seizure and wear of the dies and shortens the life of dies. In the present study, a shape of a punch having gradual contact was optimized in order to prevent the wrinkling in shrinkage flanging of ultra-high strength steel sheets. The sheet was gradually bent from the corner of the sheet to reduce the compressive stress. The wrinkling in the shrink flanging of the ultra-high strength steel sheets was prevented by the punch having gradual contact. It was found that the punch having gradual contact is effective in preventing the occurrence of wrinkling in the shrinkage flanging.

Effects of Rolling and Cooling Conditions on Microstructure and Tensile and Charpy Impact Properties of Ultra-Low-Carbon High-Strength Bainitic Steels

NASA Astrophysics Data System (ADS)

Sung, Hyo Kyung; Shin, Sang Yong; Hwang, Byoungchul; Lee, Chang Gil; Kim, Nack J.; Lee, Sunghak

2011-07-01

Six ultra-low-carbon high-strength bainitic steel plates were fabricated by controlling rolling and cooling conditions, and effects of bainitic microstructure on tensile and Charpy impact properties were investigated. The microstructural evolution was more critically affected by start cooling temperature and cooling rate than by finish rolling temperature. Bainitic microstructures such as granular bainites (GBs) and bainitic ferrites (BFs) were well developed as the start cooling temperature decreased or the cooling rate increased. When the steels cooled from 973 K or 873 K (700 °C or 600 °C) were compared under the same cooling rate of 10 K/s (10 °C/s), the steels cooled from 973 K (700 °C) consisted mainly of coarse GBs, while the steels cooled from 873 K (600 °C) contained a considerable amount of BFs having high strength, thereby resulting in the higher strength but the lower ductility and upper shelf energy (USE). When the steels cooled from 673 K (400 °C) at a cooling rate of 10 K/s (10 °C/s) or 0.1 K/s (0.1 °C/s) were compared under the same start cooling temperature of 873 K (600 °C), the fast cooled specimens were composed mainly of coarse GBs or BFs, while the slowly cooled specimens were composed mainly of acicular ferrites (AFs). Since AFs had small effective grain size and contained secondary phases finely distributed at grain boundaries, the slowly cooled specimens had a good combination of strength, ductility, and USE, together with very low energy transition temperature (ETT).

Computational Modeling Develops Ultra-Hard Steel

NASA Technical Reports Server (NTRS)

2007-01-01

Glenn Research Center's Mechanical Components Branch developed a spiral bevel or face gear test rig for testing thermal behavior, surface fatigue, strain, vibration, and noise; a full-scale, 500-horsepower helicopter main-rotor transmission testing stand; a gear rig that allows fundamental studies of the dynamic behavior of gear systems and gear noise; and a high-speed helical gear test for analyzing thermal behavior for rotorcraft. The test rig provides accelerated fatigue life testing for standard spur gears at speeds of up to 10,000 rotations per minute. The test rig enables engineers to investigate the effects of materials, heat treat, shot peen, lubricants, and other factors on the gear's performance. QuesTek Innovations LLC, based in Evanston, Illinois, recently developed a carburized, martensitic gear steel with an ultra-hard case using its computational design methodology, but needed to verify surface fatigue, lifecycle performance, and overall reliability. The Battelle Memorial Institute introduced the company to researchers at Glenn's Mechanical Components Branch and facilitated a partnership allowing researchers at the NASA Center to conduct spur gear fatigue testing for the company. Testing revealed that QuesTek's gear steel outperforms the current state-of-the-art alloys used for aviation gears in contact fatigue by almost 300 percent. With the confidence and credibility provided by the NASA testing, QuesTek is commercializing two new steel alloys. Uses for this new class of steel are limitless in areas that demand exceptional strength for high throughput applications.

Microstructural evolution and mechanical properties of a low alloy high strength Ni-Cr-Mo-V steel during heat treatment process

NASA Astrophysics Data System (ADS)

Wu, C.; Han, S.

2018-05-01

In order to obtain an optimal heat treatment for a low alloy high strength Ni-Cr-Mo-V steel, the microstructural evolution and mechanical properties of the material were studied. For this purpose, a series of quenching and temper experiments were carried out. The results showed that the effects of tempering temperature, time, original microstructure on the microstructural evolution and final properties were significant. The martensite can be completely transformed into the tempered lath structure. The width and length of the lath became wider and shorter, respectively with increasing temperature and time. The amount and size of the precipitates increased with temperature and time. The yield strength (YS), ultimate tensile strength (UTS) and hardness decreased with temperature and time, but the reduction in area (Z), elongation (E) and impact toughness displayed an opposite trend, which was related to the morphological evolution of the lath tempered structure.

Ultra-high temperature tensile properties of ODS steel claddings under severe accident conditions

NASA Astrophysics Data System (ADS)

Yano, Y.; Tanno, T.; Oka, H.; Ohtsuka, S.; Inoue, T.; Kato, S.; Furukawa, T.; Uwaba, T.; Kaito, T.; Ukai, S.; Oono, N.; Kimura, A.; Hayashi, S.; Torimaru, T.

2017-04-01

Ultra-high temperature ring tensile tests were performed to investigate the tensile behavior of oxide dispersion strengthened (ODS) steel claddings and wrapper materials under severe accident conditions with temperatures ranging from room temperature to 1400 °C which is close to the melting point of core materials. The experimental results showed that the tensile strength of 9Cr-ODS steel claddings was highest in the core materials at ultra-high temperatures of 900-1200 °C, but there was significant degradation in the tensile strength of 9Cr-ODS steel claddings above 1200 °C. This degradation was attributed to grain boundary sliding deformation with γ/δ transformation, which is associated with reduced ductility. By contrast, the tensile strength of recrystallized 12Cr-ODS and FeCrAl-ODS steel claddings retained its high value above 1200 °C, unlike the other tested materials.

The Development and Microstructure Analysis of High Strength Steel Plate NVE36 for Large Heat Input Welding

NASA Astrophysics Data System (ADS)

Peng, Zhang; Liangfa, Xie; Ming, Wei; Jianli, Li

In the shipbuilding industry, the welding efficiency of the ship plate not only has a great effect on the construction cost of the ship, but also affects the construction speed and determines the delivery cycle. The steel plate used for large heat input welding was developed sufficiently. In this paper, the composition of the steel with a small amount of Nb, Ti and large amount of Mn had been designed in micro-alloyed route. The content of C and the carbon equivalent were also designed to a low level. The technology of oxide metallurgy was used during the smelting process of the steel. The rolling technology of TMCP was controlled at a low rolling temperature and ultra-fast cooling technology was used, for the purpose of controlling the transformation of the microstructure. The microstructure of the steel plate was controlled to be the mixed microstructure of low carbon bainite and ferrite. Large amount of oxide particles dispersed in the microstructure of steel, which had a positive effects on the mechanical property and welding performance of the steel. The mechanical property of the steel plate was excellent and the value of longitudinal Akv at -60 °C is more than 200 J. The toughness of WM and HAZ were excellent after the steel plate was welded with a large heat input of 100-250 kJ/cm. The steel plate processed by mentioned above can meet the requirement of large heat input welding.

49 CFR 179.200-7 - Materials.

Code of Federal Regulations, 2011 CFR

2011-10-01

...) High alloy steel plate: High alloy steel plate must comply with one of the following specifications... 30 1 Maximum stresses to be used in calculations. 2 High alloy steel materials used to fabricate tank... specifications with the indicated minimum tensile strength and elongation in the welded condition. (b) Carbon...

49 CFR 179.200-7 - Materials.

Code of Federal Regulations, 2013 CFR

2013-10-01

...) High alloy steel plate: High alloy steel plate must comply with one of the following specifications... 30 1 Maximum stresses to be used in calculations. 2 High alloy steel materials used to fabricate tank... specifications with the indicated minimum tensile strength and elongation in the welded condition. (b) Carbon...

49 CFR 179.200-7 - Materials.

Code of Federal Regulations, 2014 CFR

2014-10-01

...) High alloy steel plate: High alloy steel plate must comply with one of the following specifications... 30 1 Maximum stresses to be used in calculations. 2 High alloy steel materials used to fabricate tank... specifications with the indicated minimum tensile strength and elongation in the welded condition. (b) Carbon...

49 CFR 179.200-7 - Materials.

Code of Federal Regulations, 2012 CFR

2012-10-01

...) High alloy steel plate: High alloy steel plate must comply with one of the following specifications... 30 1 Maximum stresses to be used in calculations. 2 High alloy steel materials used to fabricate tank... specifications with the indicated minimum tensile strength and elongation in the welded condition. (b) Carbon...

High Strength Steel Welding Research

DTIC Science & Technology

2005-05-27

E.S.K. Menon, and M.G. Hall, "Sympathetic Nucleation: An Overview," Materials Science and Engineering B, Solid State Materials for Advanced Technology ...GTAW of Titanium Using Flux-cored Wire with Magnesium Fluoride Kook-soo Bang’, Greg Chirieleison 2, and Stephen Liu 2 1 Division of Advanced Materials...O CHAPTER I O INTRODUCTION * The application of advanced high strength low alloy (HSLA) steels has been * limited by the availability of suitable

Improvement of mechanical strength of sintered Mo alloyed steel by optimization of sintering and cold-forging processes with densification

NASA Astrophysics Data System (ADS)

Kamakoshi, Y.; Shohji, I.; Inoue, Y.; Fukuda, S.

2017-10-01

Powder metallurgy (P/M) materials have been expected to be spread in automotive industry. Generally, since sintered materials using P/M ones contain many pores and voids, mechanical properties of them are inferior to those of conventional wrought materials. To improve mechanical properties of the sintered materials, densification is effective. The aim of this study is to improve mechanical strength of sintered Mo-alloyed steel by optimizing conditions in sintering and cold-forging processes. Mo-alloyed steel powder was compacted. Then, pre-sintering (PS) using a vacuum sintering furnace was conducted. Subsequently, coldforging (CF) by a backward extrusion method was conducted to the pre-sintered specimen. Moreover, the cold-forged specimen was heat treated by carburizing, tempering and quenching (CQT). Afterwards, mechanical properties were investigated. As a result, it was found that the density of the PS specimen is required to be more than 7.4 Mg/m3 to strengthen the specimen by heat treatment after CF. Furthermore, density and the microstructure of the PS specimen are most important factors to make the high density and strength material by CF. At the CF load of 1200 kN, the maximum density ratio reached approximately 99% by the use of the PS specimen with proper density and microstructure. At the CF load of 900 kN, although density ratio was high like more than 97.8%, transverse rupture strength decreased sharply. Since densification caused high shear stress and stress concentration in the surface layer, microcracks occurred by the damages of inter-particle sintered connection of the surface layer. On the contrary, in case of the CF load of 1200 kN, ultra-densification of the surface layer occurred by a sufficient plastic flow. Such sufficient compressed specimens regenerated the sintered connections by high temperature heat treatment and thus the high strength densified material was obtained. These processes can be applicable to near net shape manufacturing without surface machining.

Development of weldable, corrosion-resistant iron-aluminide (FeAl) alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Maziasz, P.J.; Goodwin, G.M.; Wang, X.L.

1997-04-01

A boron-microalloyed FeAl alloy (Fe-36Al-0.2Mo-0.05Zr-0.13C, at.%, with 100-400 appm B) with improved weldability and mechanical properties was developed in FY 1994. A new scale-up and industry technology development phase for this work began in FY 1995, pursuing two parallel paths. One path was developing monolithic FeAl component and application technology, and the other was developing coating/cladding technology for alloy steels, stainless steels and other Fe-Cr-Ni alloys. In FY 1995, it was found that cast FeAl alloys had good strength at 700-750{degrees}C, and some (2.5%) ductility in air at room-temperature. Hot-extruded FeAl with refined grain size was found to have ductilitymore » and to also have good impact-toughness at room-temperature. Further, it was discovered that powder-metallurgy (P/M) FeAl, consolidated by direct hot-extrusion at 950-1000{degrees}C to have an ultra fine-grained microstructure, had the highest ductility, strength and impact-toughness ever seen in such intermetallic alloys.« less

49 CFR 180.407 - Requirements for test and inspection of specification cargo tanks.

Code of Federal Regulations, 2014 CFR

2014-10-01

... constructed of mild steel or high-strength, low-alloy steel, that create air cavities adjacent to the tank...) Equipment must consist of: (A) A high frequency spark tester capable of producing sufficient voltage to...; and (C) A steel calibration coupon 30.5 cm × 30.5 cm (12 inches × 12 inches) covered with the same...

49 CFR 180.407 - Requirements for test and inspection of specification cargo tanks.

Code of Federal Regulations, 2012 CFR

2012-10-01

... constructed of mild steel or high-strength, low-alloy steel, that create air cavities adjacent to the tank...) Equipment must consist of: (A) A high frequency spark tester capable of producing sufficient voltage to...; and (C) A steel calibration coupon 30.5 cm × 30.5 cm (12 inches × 12 inches) covered with the same...

49 CFR 180.407 - Requirements for test and inspection of specification cargo tanks.

Code of Federal Regulations, 2011 CFR

2011-10-01

... constructed of mild steel or high-strength, low-alloy steel, that create air cavities adjacent to the tank...) Equipment must consist of: (A) A high frequency spark tester capable of producing sufficient voltage to...; and (C) A steel calibration coupon 30.5 cm × 30.5 cm (12 inches × 12 inches) covered with the same...

Damage Tolerant Design Handbook. A Compilation of Fracture and Crack- Growth Data for High-Strength Alloys. Volume 4

DTIC Science & Technology

1983-12-01

DAMAGTE (aduiTOLEATDSG ANBO.A TYPE OF REPORT 6 PERIOD COVERED DAMAE TLERAT DSIG HANBOO. ACOMPILATION OF FRACTURE AND CRACK GROWTH...4 Volumes (No copies furnished by DTIC) 13 KEY WORDS (Conitnue ate reverse side it necessa.ry and idenn’fy by. black flueoebr) * Fracture (Mechanics...Handbooks, *Titanium Alloys, *Nickel Alloys, *Stainless Steel, *Aluminum Alloys, High Strength Alloys, Structural Steel, Fracture Toughness, Damage

Development of Low Carbon Niobium Bearing High Strength F-B Dual Phase Steel with High Hole Expansion Property

NASA Astrophysics Data System (ADS)

Zhang, Lin; Xia, Ming-sheng; Xiong, Zi-liu; Du, Yan-bing; Qiao, Zhi-ming; Zhang, Hong-bo

In the study a low carbon niobium bearing high strength F-B dual phase automobile steel with high hole expansion property has been investigated. Steels of different chemical composition have been investigated by simulation experiments of controlled rolling and cooling process to study the influences of chemical elements, especially for C,Nb and Ti, and cooling pattern on the mechanical properties, flangeability and microstructure of strips. So-called 3-stages cooling pattern was adopted in simulation experiments, combining ultra fast cooling in first stage, air cooling in middle stage and fast cooling in the last stage, and at the end of run-out table the temperature of rolled pieces drop to below Bs point. Optical microstructure and SEM morphology have been observed. Results indicate that it is possible to obtain dual phase microstructure of polygonal ferrite plus bainite in adopting 3-stages cooling pattern. The low temperature coiling method using 3-step controlled cooling pattern after hot rolling is effective to produce low carbon Nb bearing steel with high balance of strength-ductility-flangeability, in addition, higher carbon content of steel tend to be detrimental to flangeability of steel, due to much carbide precipitation at ferrite boundary. Based on the results of simulation experiments mill trial has been carried out and hot rolled high strength steel with tensile strength higher as 600Mpa and hole expansion ratio higher as 100% has been developed successfully.

Retraction Note to: Ultra-High Strength and Ductile Lamellar-Structured Powder Metallurgy Binary Ti-Ta Alloys

NASA Astrophysics Data System (ADS)

Liu, Yong; Xu, Shenghang; Wang, Xin; Li, Kaiyang; Liu, Bin; Wu, Hong; Tang, Huiping

2018-05-01

The editors and authors have retracted the article, "Ultra-High Strength and Ductile Lamellar-Structured Powder Metallurgy Binary Ti-Ta Alloys" by Yong Liu, Shenghang Xu, Xin Wang, Kaiyang Li, Bin Liu, Hong Wu, and Huiping Tang (https://doi.org/10.1007/s11837-015-1801-1).

An Introduction to Navy Corrosion Problems. A Guideline for Designers and Engineers of Naval Ordnance and Hardware.

DTIC Science & Technology

1986-03-31

titanium, stainless steel , and copper alloys . During SCC, the alloy surface remains essentially unattacked while insidious crack propagation through...strength steels Water I High strength aluminum Chloride solutions, Appears to be due I alloys organic solvents moisture Copper alloys - Ammoniacal solutions... Precipitation hardened martensitic stainless steels , above 1240 MPa, have exhibited cracking in salt-spray and when fully immersed in aqueous media (23

Creep Response and Deformation Processes in Nanocluster Strengthened Ferritic Steels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hayashi, Taisuke; Sarosi, P. M.; Schneibel, Joachim H

2008-01-01

There is increasing demand for oxide-dispersion-strengthened ferritic alloys that possess both high-temperature strength and irradiation resistance. Improvement of the high-temperature properties requires an understanding of the operative deformation mechanisms. In this study, the microstructures and creep properties of the oxide-dispersion-strengthened alloy 14YWT have been evaluated as a function of annealing at 1000 C for 1 hour up to 32 days. The ultra-fine initial grain size (approx. 100nm) is stable after the shortest annealing time, and even after subsequent creep at 800 C. Longer annealing periods lead to anomalous grain growth that is further enhanced following creep. Remarkably, the minimum creepmore » rate is relatively insensitive to this dramatic grain-coarsening. The creep strength is attributed to highly stable, Ti-rich nanoclusters that appear to pin the initial primary grains, and present strong obstacles to dislocation motion in the large, anomalously grown grains.« less

Microstructure and properties of thermomechanically strengthened reinforcement bars: A comparative assessment of plain-carbon and low-alloy steel grades

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ray, A.; Mukerjee, D.; Sen, S.K.

1997-06-01

An extensive investigation has been carried out to study structure-property characteristics and corrosion behavior in three varieties of thermomechanically treated (TMT) reinforcement bars (rebars) produced in an integrated steel plant under the Steel Authority of India Limited. Three experimental steel heats--one of plain-carbon and two of low-alloy chemistry--were chosen for the study. Of the two low-alloy heats, one was copper-bearing and the other contained both copper and chromium for improved corrosion resistance. Hot-rolled bars for each specific chemistry were subjected to in-line thermomechanical treatment, where quenching parameters were altered to achieve different yield strength levels. All the TMT rebars, regardlessmore » of chemistry and strength level, exhibited a composite microstructure consisting of ferrite-pearlite at the core and tempered martensite at the rim. Although a tendency toward formation of Widmanstaetten ferrite was evident in bars of 500 and 550 MPa yield strength levels, no adverse effect on their strength and ductility was observed. From the standpoint of mechanical properties, the rebars not only conformed to minimum yield strength requirements, but also exhibited high elongation values (21 to 28%) and excellent bendability. Corrosion studies of both TMT and cold-twisted and deformed (CTD) rebars subjected to different laboratory tests indicated that corrosion resistance increased in this order: CTD, plain-carbon TMT, copper-bearing TMT, and copper/chromium-bearing TMT.« less

Developing radiopure copper alloys for high strength low background applications

NASA Astrophysics Data System (ADS)

Suriano, A. M.; Howard, S. M.; Christofferson, C. D.; Arnquist, I. J.; Hoppe, E. W.

2018-01-01

High purity copper continues to play an important role for ultra-low-background detectors. Measurements of rare nuclear decays, e.g. neutrinoless double-beta decay, and searches for dark matter can require construction materials that have high thermal and electrical conductivity with bulk radiopurity less than one micro-Becquerel per kilogram. However, experiments currently using components constructed of radiopure electroformed copper struggle with design of structural and mechanical parts due to the physical properties of pure copper. A higher strength material which possesses many of the favorable attributes of copper yet remains radiopure is desired. A number of copper alloying candidates which may provide improved mechanical performance and adequate radiopurity were considered. Development of an electrodeposited copper-chrome alloy from additive-free electrolyte systems is discussed. The resulting material is shown to possess high strength and meets the aforementioned radiopurity goals.

Development and application of super heavy gauge high-strength structural steel for high-rise buildings

NASA Astrophysics Data System (ADS)

Gu, Linhao Gu; Lu, Shiping; Liu, Chunming; Liu, Jingang; Zhang, Suyuan; Chu, Rensheng; Ma, Changwen

2017-09-01

This paper presents development of 130mm S460G1-Z35 by using low carbon Nb-Ni-Mo-V-Ti micro-alloying design and two-stage rolling, quenching and tempering process. For the super heavy gauge high-strength structural steel, the yield strength is higher than 450MPa, the tensile strength is higher than 550MPa, the elongation is greater than 20%, the low temperature(-40) impact energy value is not less than 250J, the z-direction section shrinkage is more than 65%, and the welding performance is good. The plate are successfully applied to the engineering construction of the city of dreams in Macau.

Experimental investigation of the effect of surface markings on the mechanical integrity of weathering bridge steels.

DOT National Transportation Integrated Search

2014-11-01

High-strength low-alloy (HSLA) weathering steels are the conventional material used for non-redundant fracture-critical members in bridge construction. Guidelines have been put in place by state : Departments of Transportation (DOTs) to prevent mater...

Control of Hydrogen Environment Embrittlement of Ultra-High Strength Steel for Naval Application

DTIC Science & Technology

2005-07-01

load cracking behavior of maraging steels in hydrogen. Corrosion , 29, 1973, 299-304. D.A. Jones, A.F. Jankowski and G.A. Davidson, "Diffusion of...short crack case. This behavior is relevant to small surface cracks in coated UHSS components such as a landing gear. IV.B. Effect of Steel Composition ...PRESSURE (k N /m 2) Figure 26. The effect of H2 pressure on the HEAC growth rate for a ultra-high strength 18Ni Maraging steel stressed in a highly

Low Cost Al-Si Casting Alloy As In-Situ Composite for High Temperature Applications

NASA Technical Reports Server (NTRS)

Lee, Jonathan A.

2000-01-01

A new aluminum-silicon (Al-Si) alloy has been successfully developed at NASA- Marshall Space Flight Center (MSFC) that has significant improvement in tensile and fatigue strength at elevated temperatures (500 F-700 F). The alloy offers a number of benefits such as light weight, high hardness, low thermal expansion and high surface wear resistance. In hypereutectic form, this alloy is considered as an in-situ Al-Si composite with tensile strength of about 90% higher than the auto industry 390 alloy at 600 F. This composite is very economically produced by using either conventional permanent steel molds or die casting. The projected material cost is less than $0.90 per pound, and automotive components such as pistons can be cast for high production rate using conventional casting techniques with a low and fully accounted cost. Key Words: Metal matrix composites, In-situ composite, aluminum-silicon alloy, hypereutectic alloy, permanent mold casting, die casting.

Additively manufactured hierarchical stainless steels with high strength and ductility

DOE PAGES

Wang, Y. Morris; Voisin, Thomas; McKeown, Joseph T.; ...

2017-10-30

Many traditional approaches for strengthening steels typically come at the expense of useful ductility, a dilemma known as strength–ductility trade-off. New metallurgical processing might offer the possibility of overcoming this. Here we report that austenitic 316L stainless steels additively manufactured via a laser powder-bed-fusion technique exhibit a combination of yield strength and tensile ductility that surpasses that of conventional 316L steels. High strength is attributed to solidification-enabled cellular structures, low-angle grain boundaries, and dislocations formed during manufacturing, while high uniform elongation correlates to a steady and progressive work-hardening mechanism regulated by a hierarchically heterogeneous microstructure, with length scales spanning nearlymore » six orders of magnitude. In addition, solute segregation along cellular walls and low-angle grain boundaries can enhance dislocation pinning and promote twinning. This work demonstrates the potential of additive manufacturing to create alloys with unique microstructures and high performance for structural applications.« less

Additively manufactured hierarchical stainless steels with high strength and ductility

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Y. Morris; Voisin, Thomas; McKeown, Joseph T.

Many traditional approaches for strengthening steels typically come at the expense of useful ductility, a dilemma known as strength–ductility trade-off. New metallurgical processing might offer the possibility of overcoming this. Here we report that austenitic 316L stainless steels additively manufactured via a laser powder-bed-fusion technique exhibit a combination of yield strength and tensile ductility that surpasses that of conventional 316L steels. High strength is attributed to solidification-enabled cellular structures, low-angle grain boundaries, and dislocations formed during manufacturing, while high uniform elongation correlates to a steady and progressive work-hardening mechanism regulated by a hierarchically heterogeneous microstructure, with length scales spanning nearlymore » six orders of magnitude. In addition, solute segregation along cellular walls and low-angle grain boundaries can enhance dislocation pinning and promote twinning. This work demonstrates the potential of additive manufacturing to create alloys with unique microstructures and high performance for structural applications.« less

Collected Engineering Data Sheets (Air Force Data Sheet Program)

DTIC Science & Technology

1978-12-01

alloy is a martensitic precipitation hardenable stainless steel developed by the Armco Steel Corporation. It can be heat treated to high strength levels...I12 HP 9-4-25 The HP 9-4-25 alloy is a nickel-cobalt quenched and tempered martensitic steel possessing excellent toughness at yield strength levels up...H900) Bar (ESR) Material Description This alloy is one of the family of precipitation hardening stainless steels which have found wide usage in

Microstructure Evolution and Mechanical Properties of Underwater Dry and Local Dry Cavity Welded Joints of 690 MPa Grade High Strength Steel

PubMed Central

Sun, Kun; Cui, Shuwan; Zeng, Min; Yi, Jianglong; Shen, Xiaoqin; Yi, Yaoyong

2018-01-01

Q690E high strength low alloy (HSLA) steel plays an important role in offshore structures. In addition, underwater local cavity welding (ULCW) technique was widely used to repair important offshore constructions. However, the high cooling rate of ULCW joints results in bad welding quality compared with underwater dry welding (UDW) joints. Q690E high strength low alloy steels were welded by multi-pass UDW and ULCW techniques, to study the microstructural evolution and mechanical properties of underwater welded joints. The microstructure and fracture morphology of welded joints were observed by scanning electron microscope and optical microscope. The elemental distribution in the microstructure was determined with an Electron Probe Microanalyzer. The results indicated that the microstructure of both two welded joints was similar. However, martensite and martensite-austenite components were significantly different with different underwater welding methods such that the micro-hardness of the HAZ and FZ in the ULCW specimen was higher than that of the corresponding regions in UDW joint. The yield strength and ultimate tensile strength of the ULCW specimen are 109 MPa lower and 77 MPa lower, respectively, than those of the UDW joint. The impact toughness of the UDW joint was superior to those of the ULCW joint. PMID:29361743

Microstructure Evolution and Mechanical Properties of Underwater Dry and Local Dry Cavity Welded Joints of 690 MPa Grade High Strength Steel.

PubMed

Shi, Yonghua; Sun, Kun; Cui, Shuwan; Zeng, Min; Yi, Jianglong; Shen, Xiaoqin; Yi, Yaoyong

2018-01-22

Q690E high strength low alloy (HSLA) steel plays an important role in offshore structures. In addition, underwater local cavity welding (ULCW) technique was widely used to repair important offshore constructions. However, the high cooling rate of ULCW joints results in bad welding quality compared with underwater dry welding (UDW) joints. Q690E high strength low alloy steels were welded by multi-pass UDW and ULCW techniques, to study the microstructural evolution and mechanical properties of underwater welded joints. The microstructure and fracture morphology of welded joints were observed by scanning electron microscope and optical microscope. The elemental distribution in the microstructure was determined with an Electron Probe Microanalyzer. The results indicated that the microstructure of both two welded joints was similar. However, martensite and martensite-austenite components were significantly different with different underwater welding methods such that the micro-hardness of the HAZ and FZ in the ULCW specimen was higher than that of the corresponding regions in UDW joint. The yield strength and ultimate tensile strength of the ULCW specimen are 109 MPa lower and 77 MPa lower, respectively, than those of the UDW joint. The impact toughness of the UDW joint was superior to those of the ULCW joint.

Prospects of increasing the strength of aluminum by reinforcing it with stainless steel wire (a review)

NASA Technical Reports Server (NTRS)

Botvina, L. R.; Ivanova, V. S.; Kopev, I. M.

1982-01-01

The theoretical and experimental strength of aluminum reinforced with stainless steel wire is analyzed. Various methods of producing the composite material and it's static and cyclical strengths are considered. The reinforcement of aluminum with stainless steel wire was accomplished from the perspective of increasing the specific strength of aluminum and it's alloys, increasing the strength of the material with respect to high and low temperatures, as well as increasing the cyclical strength. The production of the composite aluminum-stainless steel wire material with approximated or calculated strengthening is possible by any of the considered methods. The selection of the proper production technology depends on precise details and conditions of application of the material.

Factors that determine the level of the yield strength and the return of the yield-point elongation in low-alloy ferrite-martensite steels

NASA Astrophysics Data System (ADS)

Fonstein, N.; Kapustin, M.; Pottore, N.; Gupta, I.; Yakubovsky, O.

2007-09-01

The results of laboratory investigations of dual-phase steels with different contents of carbon and alloying elements after the controlled cooling from the two-phase field and the final low-temperature tempering are presented. It is shown that the ratio of the yield strength to the tensile strength of dual-phase steels, just as the return of the yield-point elongation, depends on the volume fraction of martensite, temperature of the martensite transformation of the austenite component, quenching stresses, concentration of carbon in ferrite, and the temperature of the final tempering.

High strength, tough alloy steel

DOEpatents

Thomas, Gareth; Rao, Bangaru V. N.

1979-01-01

A high strength, tough alloy steel is formed by heating the steel to a temperature in the austenite range (1000.degree.-1100.degree. C.) to form a homogeneous austenite phase and then cooling the steel to form a microstructure of uniformly dispersed dislocated martensite separated by continuous thin boundary films of stabilized retained austenite. The steel includes 0.2-0.35 weight % carbon, at least 1% and preferably 3-4.5% chromium, and at least one other substitutional alloying element, preferably manganese or nickel. The austenite film is stable to subsequent heat treatment as by tempering (below 300.degree. C.) and reforms to a stable film after austenite grain refinement.

High-Strength Low-Alloy Steel Strengthened by Multiply Nanoscale Microstructures

NASA Astrophysics Data System (ADS)

Shen, Y. F.; Zuo, L.

Recently, we have being focused on improving the strength without sacrificing ductility of High-strength low-alloy (HSLA) steels by designing nanostructures. Several developments have been obtained, summarized as the following three parts: (a) Depressively nanoscale precipitates: A ferritic steel with finely dispersed precipitates reveals a yield strength of 760 MPa, approximately three times higher than that of conventional Ti-bearing high strength hot-rolled sheet steels, and its ultimate tensile strength reaches 850 MPa with an elongation-to-failure value of 18%. The finely dispersed TiC precipitates in the matrix provide matrix strengthening. The estimated magnitude of precipitation strengthening is around 458 MPa. The effects of the particle size, particle distribution and intrinsic particle strength have been investigated through dislocation dynamics (DD) simulations. The DD results show that strengthening is not only a function of the density of the nano-scale precipitates but also of their size. (b) Ultrafinely ferritic plate: An interstitial-free (IF) steel sheet with a cold-rolling reduction of 75% shows a high tensile strength (710MPa) while preserving a considerable plastic strain (13%). The ductility recovery with increasing the rolling reduction up to 75% is related with the decreasing both in lamellar spacings and cell blocks sizes. (c) Parallel nano-laminated austenite: A composite microstructure consisting of ferrite, bainitic ferrite (BF) laths and retained austenite (RA) platelets has been found for the steel with a chemical composition of 0.19C-0.30Si-1.76Mn-1.52Al (in mass fraction), processed with annealing and bainitic holding. The sample annealed at 820oC (for 120s) and partitioned at 400oC (for 300s) has the best combination of ultimate tensile strength (UTS, 682 MPa) and elongation to failure ( 70%) with about 26% of BF plates 16% RA in its microstructure.

High-Strength Low-Alloy (HSLA) Mg-Zn-Ca Alloys with Excellent Biodegradation Performance

NASA Astrophysics Data System (ADS)

Hofstetter, J.; Becker, M.; Martinelli, E.; Weinberg, A. M.; Mingler, B.; Kilian, H.; Pogatscher, S.; Uggowitzer, P. J.; Löffler, J. F.

2014-04-01

This article deals with the development of fine-grained high-strength low-alloy (HSLA) magnesium alloys intended for use as biodegradable implant material. The alloys contain solely low amounts of Zn and Ca as alloying elements. We illustrate the development path starting from the high-Zn-containing ZX50 (MgZn5Ca0.25) alloy with conventional purity, to an ultrahigh-purity ZX50 modification, and further to the ultrahigh-purity Zn-lean alloy ZX10 (MgZn1Ca0.3). It is shown that alloys with high Zn-content are prone to biocorrosion in various environments, most probably because of the presence of the intermetallic phase Mg6Zn3Ca2. A reduction of the Zn content results in (Mg,Zn)2Ca phase formation. This phase is less noble than the Mg-matrix and therefore, in contrast to Mg6Zn3Ca2, does not act as cathodic site. A fine-grained microstructure is achieved by the controlled formation of fine and homogeneously distributed (Mg,Zn)2Ca precipitates, which influence dynamic recrystallization and grain growth during hot forming. Such design scheme is comparable to that of HSLA steels, where low amounts of alloying elements are intended to produce a very fine dispersion of particles to increase the material's strength by refining the grain size. Consequently our new, ultrapure ZX10 alloy exhibits high strength (yield strength R p = 240 MPa, ultimate tensile strength R m = 255 MPa) and simultaneously high ductility (elongation to fracture A = 27%), as well as low mechanical anisotropy. Because of the anodic nature of the (Mg,Zn)2Ca particles used in the HSLA concept, the in vivo degradation in a rat femur implantation study is very slow and homogeneous without clinically observable hydrogen evolution, making the ZX10 alloy a promising material for biodegradable implants.

Bond behavior of reinforcing steel in ultra-high performance concrete.

DOT National Transportation Integrated Search

2014-10-01

Ultra-High Performance Concrete (UHPC) is a relatively new class of advanced cementitious composite : materials, which exhibits high compressive [above 21.7 ksi (150 MPa)] and tensile [above 0.72 ksi (5 MPa)] : strengths. The discrete steel fiber rei...

High Strength and Wear Resistant Aluminum Alloy for High Temperature Applications

NASA Technical Reports Server (NTRS)

Lee, Jonathan A.; Munafo, Paul M. (Technical Monitor)

2002-01-01

In this paper, a new high strength and wear resistant aluminum cast alloy invented by NASA-MSFC for high temperature applications will be presented. Developed to meet U.S. automotive legislation requiring low-exhaust emission, the novel NASA 398 aluminum-silicon alloy offers dramatic improvement in tensile and fatigue strengths at elevated temperatures (500 F-800 F), enabling new pistons to utilize less material, which can lead to reducing part weight and cost as well as improving performance. NASA 398 alloy also offers greater wear resistance, surface hardness, dimensional stability, and lower thermal expansion compared to conventional aluminum alloys for several commercial and automotive applications. The new alloy can be produced economically using permanent steel molds from conventional gravity casting or sand casting. The technology was developed to stimulate the development of commercial aluminum casting products from NASA-developed technology by offering companies the opportunity to license this technology.

Relationship Between Solidification Microstructure and Hot Cracking Susceptibility for Continuous Casting of Low-Carbon and High-Strength Low-Alloyed Steels: A Phase-Field Study

NASA Astrophysics Data System (ADS)

Böttger, B.; Apel, M.; Santillana, B.; Eskin, D. G.

2013-08-01

Hot cracking is one of the major defects in continuous casting of steels, frequently limiting the productivity. To understand the factors leading to this defect, microstructure formation is simulated for a low-carbon and two high-strength low-alloyed steels. 2D simulation of the initial stage of solidification is performed in a moving slice of the slab using proprietary multiphase-field software and taking into account all elements which are expected to have a relevant effect on the mechanical properties and structure formation during solidification. To account for the correct thermodynamic and kinetic properties of the multicomponent alloy grades, the simulation software is online coupled to commercial thermodynamic and mobility databases. A moving-frame boundary condition allows traveling through the entire solidification history starting from the slab surface, and tracking the morphology changes during growth of the shell. From the simulation results, significant microstructure differences between the steel grades are quantitatively evaluated and correlated with their hot cracking behavior according to the Rappaz-Drezet-Gremaud (RDG) hot cracking criterion. The possible role of the microalloying elements in hot cracking, in particular of traces of Ti, is analyzed. With the assumption that TiN precipitates trigger coalescence of the primary dendrites, quantitative evaluation of the critical strain rates leads to a full agreement with the observed hot cracking behavior.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Clark, Williams; Zhao, Ji-Cheng

Cost effective and high performance alloys that are capable of operating at 760 °C or higher for extended periods of time under a very aggressive environment are critically required for the design and development of advanced ultrasupercritical (AUSC) boilers and steam turbines. Finely dispersed Laves phase precipitates have been shown by Takeyama and co-workers to be a viable strengthening mechanism in high temperature austenitic steels. There is currently no straightforward theory that can predict what other intermetallic phases can serve as potent precipitation-strengthening phases for steels; thus we employed a highly effective dual-anneal diffusion multiple (DADM) approach to screen formore » viable strengthening precipitates over a wide range of compositions. From the Fe-Co-Cr-Ni-Mo DADMs, the Fe-Cr-Mo based Chi phase was identified as a new strengthening phase for high temperature ferritic steels; and from the Fe-Mn-Cr-Nb-Ni-Mo-FeAl DADMs, the Laves phase was identified as a viable strengthening precipitate in Fe-Mn and Fe-Ni based austenitic steels. After identification of viable strengthening phases from the DADMs that covered compositions in the basic ternary and quaternary systems, we employed computation thermodynamics to perform multicomponent alloy design and optimization. For the new the Chi-phase strengthened steels, we performed thermodynamic calculations to vary the volume fraction of the Chi phase and introduced Nb and carbon to promote the formation of stable carbides for grain size control during solution heat treatment. For the Fe-Ni-Mn based austenitic steels, we performed extensive parametric optimization of compositions in order to reduce the expensive Ni content, add Cr and Al for oxidation resistance, and balance the alloying contents (Ni, Mn, Cr, Al, Mo) to suppress the ferritic phase and promote the austenitic matrix phase. Four steels (two ferritic + two austenitic) were designed and tested. The two Chi-phase strengthened ferritic steels exhibited excellent oxidation resistance and good creep-rupture strength at moderate temperatures, considering their ferritic matrix that usually results in lower creep resistance than austenitic steels. These steels showed brittleness and sample-to-sample variability in ductility. The low ductility might be due to the macro segregation during solidification or the significant grain growth during the solution heat treatments. We believe there is no inherent brittleness based on the chemistry of the steels. The creep-rupture performance of the steels is comparable to the 9Cr steels. Due to their ferritic matrix, the new Chi-phase strengthened ferritic steels may not be suited for the 760 °C AUSC applications, but they are very good candidates for intermediate temperature applications due to their outstanding oxidation resistance and high strength. Further study is required to find the source of low and highly variable ductility. We believe the compositions of the Chi-phase strengthened steels are not inherently brittle. The Chi-phase strengthened ferritic steels may also be excellent candidates for intermediate-temperature and room-temperature cast stainless steels, thus we highly recommend further investigations. The two Mn-containing austenitic steels based on the Laves phase showed good ductility, excellent oxidation resistance (slightly inferior to the two ferritic steels) at high temperatures and moderate creep strength. The creep-strength of the two austenitic steels based on the Larson-Miller parameters is higher than that of the traditional 316 stainless steels, but lower than the alumina-forming alloys (AFAs) developed at Oak Ridge National Laboratories. We do not recommend high priority in further studying these compositions unless higher Cr alloys are required for hot-corrosion resistance.« less

High dislocation density-induced large ductility in deformed and partitioned steels

NASA Astrophysics Data System (ADS)

He, B. B.; Hu, B.; Yen, H. W.; Cheng, G. J.; Wang, Z. K.; Luo, H. W.; Huang, M. X.

2017-09-01

A wide variety of industrial applications require materials with high strength and ductility. Unfortunately, the strategies for increasing material strength, such as processing to create line defects (dislocations), tend to decrease ductility. We developed a strategy to circumvent this in inexpensive, medium manganese steel. Cold rolling followed by low-temperature tempering developed steel with metastable austenite grains embedded in a highly dislocated martensite matrix. This deformed and partitioned (D and P) process produced dislocation hardening but retained high ductility, both through the glide of intensive mobile dislocations and by allowing us to control martensitic transformation. The D and P strategy should apply to any other alloy with deformation-induced martensitic transformation and provides a pathway for the development of high-strength, high-ductility materials.

Mineral Resource of the Month: Niobium

USGS Publications Warehouse

Papp, John F.

2014-01-01

Niobium, also called columbium, is a transition metal with a very high melting point. It is in greatest demand in industrialized countries, like the United States, because of its defense-related uses in the aerospace, energy and transportation industries. Niobium is used mostly to make high-strength, low-alloy (HSLA) steel and stainless steel. HSLA steels are used in large-diameter pipes for oil and natural gas pipelines and automobile wheels.

Effect of Curing Period on Properties of Steel and Polypropylene Fibre Reinforced Ultra-High Performance Concrete

NASA Astrophysics Data System (ADS)

Smarzewski, Piotr

2017-10-01

This study has investigated the effect of curing period on the mechanical properties of straight polypropylene and hooked-end steel fibre reinforced ultra-high performance concrete (UHPC). Various physical properties are evaluated, i.e. absorbability, apparent density and open porosity. Compressive strength, tensile splitting strength, flexural strength and modulus of elasticity were determined at 28, 56 and 730 days. Comparative strength development of fibre reinforced mixes at 0.5%, 1%, 1.5% and 2% by volume fractions in relation to the mix without fibres was observed. Good correlations between the compressive strength and the modulus of elasticity are established. Steel and polypropylene fibres significantly increased the compressive strength, tensile splitting strength, flexural strength and modulus of elasticity of UHPC after two years curing period when fibre content volume was at least 1%. It seems that steel fibre reinforced UHPC has better properties than the polypropylene fibre reinforced UHPC.

Influence of Microstructure on the Fatigue Crack Growth of A516 in Hydrogen

NASA Technical Reports Server (NTRS)

Wachob, Harry F.; Nelson, Howard G.

1980-01-01

Some day hydrogen may be used as a viable energy storage and transport medium within the United States. Hydrogen gas may be used to dilute and extend our present methane supply as a blend or may even be used in its pure elemental form as a primary fuel. Independent of the methods of production, storage, and distribution, the interaction of hydrogen with its containment material will play an integral role in the success of a hydrogen energy program. Presently, the selection of hydrogen containment materials can be made such that the material will remain reasonably free from environmental degradation; however, costly alloying additions are required. Unfortunately, high alloy steels are economically prohibitive when large-scale hydrogen energy storage, transmission, and conversion systems are desired. Therefore, in order to implement such hydrogen energy systems in the future, existing low-cost materials must be improved via mechanical, thermal, or thermo-mechanical processing methods or new low-cost materials which are compatible with hydrogen must be developed. Originally, low strength, low alloy steels at room temperature were thought to be immune to hydrogen gas embrittlement, since no sustained load crack growth is observed. However, results of Clark in HY8O and Nelson in SAE 1020 have shown that the fatigue crack growth rate can be greatly accelerated in the presence of hydrogen gas. In recent results reported by Louthan and Mucci, the smooth bar fatigue life of an A1068 pipeline steel was reduced up to a factor of ten when the tests were performed in a 13.8 MPa hydrogen environment. These results suggest that the selection of material for structures designed to operate in hydrogen under cyclic loads must include consideration of hydrogen/metal fatigue interaction. Although the hydrogen/metal fatigue interaction can be severe in low strength low alloy steels, the degree of degradation may be altered by the underlying ferrous microstructure. At present, no correlation between microstructure and degree of hydrogen susceptibility exists for low strength steels. However, in high strength steels, susceptibility to hydrogen embrittlement has been shown to be strongly sensitive to the metallurgical microstructure. In addition, compositional effects and grain size can 703 Some day hydrogen may be used as a viable energy storage and transport medium within the United States. Hydrogen gas may be used to dilute and extend our present methane supply as a blend or may even be used in its pure elemental form as a primary fuel. Independent of the methods of production, storage, and distribution, the interaction of hydrogen with its containment material will play an integral role in the success of a hydrogen energy program. Presently, the selection of hydrogen containment materials can be made such that the material will remain reasonably free from environmental degradation; however, costly alloying additions are required. Unfortunately, high alloy steels are economically prohibitive when large-scale hydrogen energy storage, transmission, and conversion systems are desired. Therefore, in order to implement such hydrogen energy systems in the future, existing low-cost materials must be improved via mechanical, thermal, or thermo-mechanical processing methods or new low-cost materials which are compatible with hydrogen must be developed.

Development in high-grade dual phase steels with low C and Si design

NASA Astrophysics Data System (ADS)

Zhu, Guo-hui; Zhang, Xue-hui; Mao, Wei-min

2009-12-01

Cold rolled dual phase steels with low C and Si addition were investigated in terms of combination of composition and processing in order to improve mechanical properties and workability including welding and galvanizing. Mo and Cr could be used as alloying elements to partially replace C and Si to assure enough hardening ability of the steels and also give solute-hardening. Mo addition is more effective than Cr addition in terms of obtaining the required volume fraction of martensite and mechanical strength. The ferrite grain was effectively refined by addition of Nb microalloying, which gives optimized mechanical properties. The experimental results show that it is possible to obtain the required mechanical properties of high grade 800 MPa dual phase steel, i.e., tensile strength > 780 MPa, elongation > 15%, and yield/tensile strength ratio < 0.6 in the condition of low carbon (C < 0.11 wt.%) and low silicon design (Si < 0.05 wt.%) through adequate combination of composition and processing.

Understanding the Interaction between a Steel Microstructure and Hydrogen

PubMed Central

Depover, Tom; Laureys, Aurélie; Wallaert, Elien

2018-01-01

The present work provides an overview of the work on the interaction between hydrogen (H) and the steel’s microstructure. Different techniques are used to evaluate the H-induced damage phenomena. The impact of H charging on multiphase high-strength steels, i.e., high-strength low-alloy (HSLA), transformation-induced plasticity (TRIP) and dual phase (DP) is first studied. The highest hydrogen embrittlement resistance is obtained for HSLA steel due to the presence of Ti- and Nb-based precipitates. Generic Fe-C lab-cast alloys consisting of a single phase, i.e., ferrite, bainite, pearlite or martensite, and with carbon contents of approximately 0, 0.2 and 0.4 wt %, are further considered to simplify the microstructure. Finally, the addition of carbides is investigated in lab-cast Fe-C-X alloys by adding a ternary carbide forming element to the Fe-C alloys. To understand the H/material interaction, a comparison of the available H trapping sites, the H pick-up level and the H diffusivity with the H-induced mechanical degradation or H-induced cracking is correlated with a thorough microstructural analysis. PMID:29710803

Influence of nitrogen as grain refiner in low carbon and microalloyed steels

NASA Astrophysics Data System (ADS)

Hasan, B. M.; Sathyamurthy, P.

2018-02-01

Microalloyed steel is replacing using of low alloy steel in automotive industry. Microalloying elements like vanadium, niobium and titanium are used to enhance the steel property. The current work is focused on using nitrogen as a strengthening element in existing steel grade. Nitrogen in free form acts as solid solution strengthener and in combined form as precipitates acts as grain refiner for enhancing strength. The problem of grain coarsening at high temperature in case carburizing steel was avoided by increasing nitrogen level from 60ppm to 200ppm. Grain size of ASTM no 10 is obtained at carburizing temperature of 950 °C by increasing nitrogen content from grain size no 6 with lower nitrogen. Mostly crankshaft is made from Cr-Mo alloyed steel. At JSW, nitrogen in the level of 130-200ppm is added to medium carbon steel to meet property requirement for crankshaft application

Welding of HSLA-100 steel using ultra low carbon bainitic weld metal to eliminate preheating

DOE Office of Scientific and Technical Information (OSTI.GOV)

Devletian, J.H.; Singh, D.; Wood, W.E.

1996-12-31

Advanced high strength steels such as the Navy`s HSLA-100 and HSLA-80 contain sufficiently low carbon levels to be weldable without preheating. Unfortunately, commercial filler metals specifically designed to weld these steels without costly preheating have not yet been developed. The objective of this paper is to show that the Navy`s advanced steels can be welded by gas metal-arc (GMAW) and gas tungsten-arc welding (GTAW) without preheating by using filler metal compositions that produce weld metal with an ultra-low carbon bainitic (ULCB) microstructure. Filler metals were fabricated from vacuum induction melted (VIM) ingots containing ultra-low levels of C, O and N.more » HSLA-100 plate and plate from the VIM ingots were welded by both GMAW and GTAW with Ar-5% CO{sub 2} shielding gas using welding conditions to achieve cooling times from 800 to 500 C (t{sub 8-5}) from 35 to 14 sec. Weld metal tensile, hardness and CVN impact toughness testing as well as microstructural studies using transmission electron microscopy were conducted. The ULCB weld metal was relatively insensitive to cooling rate, resulting in good strength and toughness values over a wide range of t{sub 8-5} cooling times. Filler metal compositions which met the mechanical property requirements for HSLA-100, HSLA-80 and HSLA-65 weld metal were developed.« less

Creep modeling for life evaluation and strengthening mechanism of tungsten alloyed 9-12% Cr steels

NASA Astrophysics Data System (ADS)

Park, Kyu-Seop; Bae, Dong-Sik; Lee, Sung-Keun; Lee, Goo-Hyun; Kim, Jung-Ho; Endo, Takao

2006-10-01

Recently, high strength tungsten (W) alloyed steels have been developed for use in power plants with higher steam conditions for environmental reasons as well as the improvement of thermal efficiency resulting in lower fuel costs. In order to establish a creep modeling of high strength martensitic steel and to understand the basic role of W in tungsten alloyed 9-12Cr steels, conventional martensitic steels (X20CrMoV121, X20CrMoWV121, and Mod9Cr-1Mo) and tungsten alloyed steels (NF616 and HCM12A) were employed for creep tests and creep behavior analyses by the Ω method. The proposed creep model, which takes into account both primary and tertiary creep, satisfactorily described the creep curves and accurately predicted creep life, as martensitic steel undergoes a relatively large amount of primary creep, up to nearly 30%, over its normal life. The tungsten alloyed steels exhibited a smaller minimum creep rate and a larger stress exponent compared to the conventional steels. In addition, in tungsten alloyed steel, the Ω value features strong stress dependence such that creep life is prolonged at lower stresses due to high Ω values. The importance of the Ω value from the standpoint of creep strengthening in primary and tertiary creep is discussed.

Method of making high strength, tough alloy steel

DOEpatents

Thomas, Gareth; Rao, Bangaru V. N.

1979-01-01

A high strength, tough alloy steel, particularly suitable for the mining industry, is formed by heating the steel to a temperature in the austenite range (1000.degree.-1100.degree. C.) to form a homogeneous austenite phase and then cooling the steel to form a microstructure of uniformly dispersed dislocated martensite separated by continuous thin boundary films of stabilized retained austenite. The steel includes 0.2-0.35 weight % carbon, at least 1% and preferably 3-4.5% chromium, and at least one other subsitutional alloying element, preferably manganese or nickel. The austenite film is stable to subsequent heat treatment as by tempering (below 300.degree. C.) and reforms to a stable film after austenite grain refinement.

An Atom Probe Tomographic Investigation of High-Strength, High-Toughness Precipitation Strengthened Steels for Naval Applications

NASA Astrophysics Data System (ADS)

Hunter, Allen H.

Novel high-strength high-toughness alloys strengthened by precipitation are investigated for use in naval applications. The mechanical properties of an experimental steel alloy, NUCu-140, are evaluated and are not suitable for the naval requirements due to poor impact toughness at -40°C. An investigation is conducted to determine optimum processing conditions to restore toughness. A detailed aging study is conducted at 450, 500, and 550°C to determine the evolution of the microstructure and mechanical properties. A combination of transmission electron microscopy (TEM), synchrotron X-ray Diffraction (XRD), and Local electrode atom probe (LEAP) tomography are used to measure the evolution of the Cu precipitates, austenite, NbC, and cementite phases during aging. The evolution of the Cu precipitates significantly affects the yield strength of the steel, but low temperature toughness is controlled by the cementite precipitates. Extended aging is effective at improving the impact toughness but the yield strength is also decreased due to coarsening of the Cu precipitates. To provide a foundation for successful welding of NUCu-140 steel, an investigation of the effects of gas metal arc welding (GMAW) are performed. The microstructures in the base metal (BM), heat affected zone (HAZ), and fusion zone (FZ) of a GMAW sample are analyzed to determine the effects of the welding thermal cycle. Weld simulation samples with known thermal histories are prepared and analyzed by XRD and LEAP tomography. A significant loss in microhardness is observed as a result of dissolution of the Cu precipitates after the weld thermal cycle. The cooling time is too rapid to allow significant precipitation of Cu. In addition to the NUCu-140 alloy, a production HSLA-115 steel alloy is investigated using TEM, XRD, and LEAP tomography. The strength of the HSLA-115 is found to be derived primarily from Cu precipitates. The volume fractions of cementite, austenite, and NbC are measured by XRD. Austenite precipitates are observed at martensite lath boundaries using TEM.

Strength of "Light" Ferritic and Austenitic Steels Based on the Fe - Mn - Al - C System

NASA Astrophysics Data System (ADS)

Kaputkina, L. M.; Svyazhin, A. G.; Smarygina, I. V.; Kindop, V. E.

2017-01-01

The phase composition, the hardness, the mechanical properties at room temperature, and the resistance to hot (950 - 1000°C) and warm (550°C) deformation are studied for cast deformable "light" ferritic and austenitic steels of the Fe - (12 - 25)% Mn - (0 - 15)% Al - (0 - 2)% C system alloyed additionally with about 5% Ni. The high-aluminum high-manganese low-carbon and carbonless ferritic steels at a temperature of about 0.5 T melt have a specific strength close to that of the austenitic steels and may be used as weldable scale-resistant and wear-resistant materials. The high-carbon Fe - (20 - 24)% Mn - (5 - 9)% Al - 5% Ni - 1.5% C austenitic steels may be applied as light high-strength materials operating at cryogenic temperatures after a solution treatment and as scale- and heat-resistant materials in an aged condition.

49 CFR 179.220-7 - Materials.

Code of Federal Regulations, 2010 CFR

2010-10-01

...) High alloy steel plate: High alloy steel plate must comply with one of the following specifications... and with the indicated minimum tensile strength and elongation in the welded condition. (b) Carbon steel plate: The maximum allowable carbon content must be 0.31 percent when the individual specification...

COMMERCIAL SUPERSONIC TRANSPORT PROGRAM. PHASE II-C REPORT. HIGH STRENGTH STEEL EVALUATION FOR SUPERSONIC AIRCRAFT.

DTIC Science & Technology

JET TRANSPORT AIRCRAFT, *AIRFRAMES, SUPERSONIC AIRCRAFT, STEEL , STRUCTURAL PROPERTIES, FRACTURE(MECHANICS), FATIGUE(MECHANICS), STRESS CORROSION...MICROPHOTOGRAPHY, HIGH TEMPERATURE, NICKEL ALLOYS, COBALT ALLOYS, CARBON, BAINITE , COMMERCIAL AIRCRAFT.

The Effect of Welding Process on the Microstructure of HY-130 Steel Weldments

DTIC Science & Technology

1988-12-01

low -carbon, high-strength, low - alloy (HSLA) steels (C below 0.07 per- cent), the weld metal changed from coarse polygonal ferrite to...17. Ricks. R. A., Barritte, G. S., and Howell, P. R., "The Influence of Second Phase Particles on Diffusional Phase Transformations in Steels ... phase , austenite, may transform to mar- tensite on rapid cooling. The martensite has the exact same composi- tion as the austenite (up to two

Delamination Fracture Related to Tempering in a High-Strength Low-Alloy Steel

NASA Astrophysics Data System (ADS)

Yan, Wei; Sha, Wei; Zhu, Lin; Wang, Wei; Shan, Yi-Yin; Yang, Ke

2010-01-01

The delamination or splitting of mechanical test specimens of rolled steel plate is a phenomenon that has been studied for many years. In the present study, splitting during fracture of tensile and Charpy V-notch (CVN) test specimens is examined in a high-strength low-alloy plate steel. It is shown that delamination did not occur in test specimens from plate in the as-rolled condition, but was severe in material tempered in the temperature range 500 °C to 650 °C. Minor splitting was seen after heating to 200 °C, 400 °C, and 700 °C. Samples that had been triple quenched and tempered to produce a fine equiaxed grain size also did not exhibit splitting. Microstructural and preferred orientation studies are presented and are discussed as they relate to the splitting phenomenon. It is concluded that the elongated as-rolled grains and grain boundary embrittlement resulting from precipitates (carbides and nitrides) formed during reheating were responsible for the delamination.

46 CFR 54.25-15 - Low temperature operation-high alloy steels (modifies UHA-23(b) and UHA-51).

Code of Federal Regulations, 2010 CFR

2010-10-01

... 46 Shipping 2 2010-10-01 2010-10-01 false Low temperature operation-high alloy steels (modifies... (CONTINUED) MARINE ENGINEERING PRESSURE VESSELS Construction With Carbon, Alloy, and Heat Treated Steels § 54.25-15 Low temperature operation—high alloy steels (modifies UHA-23(b) and UHA-51). (a) Toughness...

46 CFR 54.25-15 - Low temperature operation-high alloy steels (modifies UHA-23(b) and UHA-51).

Code of Federal Regulations, 2012 CFR

2012-10-01

... 46 Shipping 2 2012-10-01 2012-10-01 false Low temperature operation-high alloy steels (modifies... (CONTINUED) MARINE ENGINEERING PRESSURE VESSELS Construction With Carbon, Alloy, and Heat Treated Steels § 54.25-15 Low temperature operation—high alloy steels (modifies UHA-23(b) and UHA-51). (a) Toughness...

46 CFR 54.25-15 - Low temperature operation-high alloy steels (modifies UHA-23(b) and UHA-51).

Code of Federal Regulations, 2014 CFR

2014-10-01

... 46 Shipping 2 2014-10-01 2014-10-01 false Low temperature operation-high alloy steels (modifies... (CONTINUED) MARINE ENGINEERING PRESSURE VESSELS Construction With Carbon, Alloy, and Heat Treated Steels § 54.25-15 Low temperature operation—high alloy steels (modifies UHA-23(b) and UHA-51). (a) Toughness...

46 CFR 54.25-15 - Low temperature operation-high alloy steels (modifies UHA-23(b) and UHA-51).

Code of Federal Regulations, 2013 CFR

2013-10-01

... 46 Shipping 2 2013-10-01 2013-10-01 false Low temperature operation-high alloy steels (modifies... (CONTINUED) MARINE ENGINEERING PRESSURE VESSELS Construction With Carbon, Alloy, and Heat Treated Steels § 54.25-15 Low temperature operation—high alloy steels (modifies UHA-23(b) and UHA-51). (a) Toughness...

46 CFR 54.25-15 - Low temperature operation-high alloy steels (modifies UHA-23(b) and UHA-51).

Code of Federal Regulations, 2011 CFR

2011-10-01

... 46 Shipping 2 2011-10-01 2011-10-01 false Low temperature operation-high alloy steels (modifies... (CONTINUED) MARINE ENGINEERING PRESSURE VESSELS Construction With Carbon, Alloy, and Heat Treated Steels § 54.25-15 Low temperature operation—high alloy steels (modifies UHA-23(b) and UHA-51). (a) Toughness...

Effect of Cooling Rate on Phase Transformations in a High-Strength Low-Alloy Steel Studied from the Liquid Phase

NASA Astrophysics Data System (ADS)

Dorin, Thomas; Stanford, Nicole; Taylor, Adam; Hodgson, Peter

2015-12-01

The phase transformation and precipitation in a high-strength low-alloy steel have been studied over a large range of cooling rates, and a continuous cooling transformation (CCT) diagram has been produced. These experiments are unique because the measurements were made from samples cooled directly from the melt, rather than in homogenized and re-heated billets. The purpose of this experimental design was to examine conditions pertinent to direct strip casting. At the highest cooling rates which simulate strip casting, the microstructure was fully bainitic with small regions of pearlite. At lower cooling rates, the fraction of polygonal ferrite increased and the pearlite regions became larger. The CCT diagram and the microstructural analysis showed that the precipitation of NbC is suppressed at high cooling rates, and is likely to be incomplete at intermediate cooling rates.

Hydrogen Assisted Cracking of High Strength Alloys

DTIC Science & Technology

2003-08-01

maraging steels (Dautovich and Floreen, 1973, 1977; Gerberich et al., 1988; Yamaguchi, et al., 1997). This behavior is typically described by a...transgranular. A similar maximum in IG cracking susceptibility near the free corrosion potential was reported for 18Ni Maraging steel in neutral NaCl... steel in 133 kPa pure H2 parallels the behavior of AISI 4340 and the 18 Ni maraging steels , particularly in terms of a low temperature activation

Hydrogen assisted cracking and CO2 corrosion behaviors of low-alloy steel with high strength used for armor layer of flexible pipe

NASA Astrophysics Data System (ADS)

Liu, Zhenguang; Gao, Xiuhua; Du, Linxiu; Li, Jianping; Zhou, Xiaowei; Wang, Xiaonan; Wang, Yuxin; Liu, Chuan; Xu, Guoxiang; Misra, R. D. K.

2018-05-01

In this study, hydrogen induced cracking (HIC), sulfide stress corrosion cracking (SSCC) and hydrogen embrittlement (HE) were carried out to study hydrogen assisted cracking behavior (HIC, SSCC and HE) of high strength pipeline steel used for armor layer of flexible pipe in ocean. The CO2 corrosion behavior of designed steel with high strength was studied by using immersion experiment. The experimental results demonstrate that the corrosion resistance of designed steel with tempered martensite to HIC, SSCC and HE is excellent according to specific standards, which contributes to the low concentration of dislocation and vacancies previously formed in cold rolling process. The corrosion mechanism of hydrogen induced cracking of designed steel, which involves in producing process, microstructure and cracking behavior, is proposed. The designed steel with tempered martensite shows excellent corrosion resistance to CO2 corrosion. Cr-rich compound was first formed on the coupon surface exposed to CO2-saturated brine condition and chlorine, one of the corrosion ions in solution, was rich in the inner layer of corrosion products.

Stress corrosion cracking of several high strength ferrous and nickel alloys

NASA Technical Reports Server (NTRS)

Nelson, E. E.

1971-01-01

The stress corrosion cracking resistance of several high strength ferrous and nickel base alloys has been determined in a sodium chloride solution. Results indicate that under these test conditions Multiphase MP35N, Unitemp L605, Inconel 718, Carpenter 20Cb and 20Cb-3 are highly resistant to stress corrosion cracking. AISI 410 and 431 stainless steels, 18 Ni maraging steel (250 grade) and AISI 4130 steel are susceptible to stress corrosion cracking under some conditions.

Reinforcing aluminum alloys with high strength fibers

NASA Technical Reports Server (NTRS)

Kolpashnikov, A. I.; Manuylov, V. F.; Chukhin, B. D.; Shiryayev, Y. V.; Shurygin, A. S.

1982-01-01

A study is made of the possibility of reinforcing aluminum and aluminum based alloys with fibers made of high strength steel wire. The method of introducing the fibers is described in detail. Additional strengthening by reinforcement of the high alloy system Al - An - Mg was investigated.

Evaluation of advanced austenitic alloys relative to alloy design criteria for steam service

DOE Office of Scientific and Technical Information (OSTI.GOV)

Swindeman, R.W.; Maziasz, P.J.; Bolling, E.

1990-05-01

The results are summarized for a 6-year activity on advanced austenitic stainless steels for heat recovery systems. Commercial, near-commercial, and developmental alloys were evaluated relative to criteria for metallurgical stability, fabricability, weldability, and mechanical strength. Fireside and steamside corrosion were also considered, but no test data were collected. Lean stainless steel alloys that were given special attention in the study were type 316 stainless steel, fine-grained type 347 stainless steel, 17-14CuMo stainless steel, Esshete 1250, Sumitomo ST3Cu{reg sign} stainless steel, and a group of alloys identified as HT-UPS (high-temperature, ultrafine-precipitation strengthened) steels that were basically 14Cr--16Ni--Mo steels modified by variousmore » additions of MC-forming elements. It was found that, by solution treating the MC-forming alloys to temperatures above 1150{degree}C and subsequently cold or warm working, excellent metallurgical stability and creep strength could be achieved. Test data to beyond 35,000 h were collected. The ability to clad the steels for improved fireside corrosion resistance was demonstrated. Weldability of the alloys was of concern, and hot cracking was found to be a problem in the HT-UPS alloys. By reducing the phosphorous content and selecting either CRE 16-8-2 stainless steel or alloy 556 filler metal, weldments were produced that had excellent strength and ductility. The major issues related to the development of the advanced alloys were identified and ways to resolve the issues suggested. 89 refs., 45 figs., 8 tabs.« less

EBSD characterization of low temperature deformation mechanisms in modern alloys

NASA Astrophysics Data System (ADS)

Kozmel, Thomas S., II

For structural applications, grain refinement has been shown to enhance mechanical properties such as strength, fatigue resistance, and fracture toughness. Through control of the thermos-mechanical processing parameters, dynamic recrystallization mechanisms were used to produce microstructures consisting of sub-micron grains in 9310 steel, 4140 steel, and Ti-6Al-4V. In both 9310 and 4140 steel, the distribution of carbides throughout the microstructure affected the ability of the material to dynamically recrystallize and determined the size of the dynamically recrystallized grains. Processing the materials at lower temperatures and higher strain rates resulted in finer dynamically recrystallized grains. Microstructural process models that can be used to estimate the resulting microstructure based on the processing parameters were developed for both 9310 and 4140 steel. Heat treatment studies performed on 9310 steel showed that the sub-micron grain size obtained during deformation could not be retained due to the low equilibrium volume fraction of carbides. Commercially available aluminum alloys were investigated to explain their high strain rate deformation behavior. Alloys such as 2139, 2519, 5083, and 7039 exhibit strain softening after an ultimate strength is reached, followed by a rapid degradation of mechanical properties after a critical strain level has been reached. Microstructural analysis showed that the formation of shear bands typically preceded this rapid degradation in properties. Shear band boundary misorientations increased as a function of equivalent strain in all cases. Precipitation behavior was found to greatly influence the microstructural response of the alloys. Additionally, precipitation strengthened alloys were found to exhibit similar flow stress behavior, whereas solid solution strengthened alloys exhibited lower flow stresses but higher ductility during dynamic loading. Schmid factor maps demonstrated that shear band formation behavior was influenced by texturing in these alloys.

Physical, mechanical, and flexural properties of 3 orthodontic wires: an in-vitro study.

PubMed

Juvvadi, Shubhaker Rao; Kailasam, Vignesh; Padmanabhan, Sridevi; Chitharanjan, Arun B

2010-11-01

Understanding the biologic requirements of orthodontic patients requires proper characterization studies of new archwire alloys. The aims of this study were to evaluate properties of wires made of 2 new materials and to compare their properties with those of stainless steel. The sample consisted of 30 straight lengths of 3 types of wires: stainless steel, titanium-molybdenum alloy, and beta-titanium alloy. Eight properties were evaluated: wire dimension, edge bevel, composition, surface characteristics, frictional characteristics, ultimate tensile strength (UTS), modulus of elasticity (E), yield strength (YS), and load deflection characteristics. A toolmaker's microscope was used to measure the edge bevel, and x-ray fluorescence was used for composition analysis. Surface profilometry and scanning electron microscopy were used for surface evaluation. A universal testing machine was used to evaluate frictional characteristics, tensile strength, and 3-point bending. Stainless steel was the smoothest wire; it had the lowest friction and spring-back values and high values for stiffness, E, YS, and UTS. The titanium-molybdenum alloy was the roughest wire; it had high friction and intermediate spring-back, stiffness, and UTS values. The beta-titanium alloy was intermediate for smoothness, friction, and UTS but had the highest spring-back. The beta-titanium alloy with increased UTS and YS had a low E value, suggesting that it would have greater resistance to fracture, thereby overcoming a major disadvantage of titanium-molybdenum alloy wires. The beta-titanium alloy wire would also deliver gentler forces. Copyright © 2010 American Association of Orthodontists. Published by Mosby, Inc. All rights reserved.

Microstructural and Mechanical Properties of Hot Roll Bonded Titanium Alloy/Low Carbon Steel Plate

NASA Astrophysics Data System (ADS)

Yu, Chao; Qi, Zi-chen; Yu, Hui; Xu, Cheng; Xiao, Hong

2018-03-01

In this paper, a titanium alloy and low carbon steel were bonded via hot rolling in a vacuum, and the effect of roll bonding temperature and reduction ratio on the microstructural and mechanical properties of the plate was studied. When the bonding temperature was between 850 and 1050 °C, the shear strength of the interface increased with an increasing reduction ratio from 18 to 70%. At a bonding temperature of 950 °C and at a rolling reduction ratio of 70%, the best bonding strength was obtained, and a shear fracture occurred on the low carbon steel matrix. At 1050 °C, brittle compounds, i.e., TiC, FeTi, and Fe2Ti, formed at the interface, which decreased the bonding strength. The large reduction ratio can break up compounds at the interface and extrude fresh metal for bonding, thereby increasing the bonding strength.

Aluminum/steel wire composite plates exhibit high tensile strength

NASA Technical Reports Server (NTRS)

1966-01-01

Composite plate of fine steel wires imbedded in an aluminum alloy matrix results in a lightweight material with high tensile strength. Plates have been prepared having the strength of titanium with only 85 percent of its density.

Effect of steel structure and defects on reliability of parts of impact mechanisms

NASA Astrophysics Data System (ADS)

Popelyukh, AI; Repin, AA; Alekseev, SE

2018-03-01

The paper discusses selection of materials suitable for manufacturing critical parts of impact mechanisms. It is shown that in order to extend life of parts exposed to high dynamic loading, it is expedient to use medium- and high-carbon alloy-treated steels featuring low impurity with nonmetallic inclusions and high hardening characteristics. Application of thermally untreated parts is undesirable as steel having ferrite–pearlite structure possesses low fatigue strength. Aimed to ensure high reliability of parts with a hardness of 42–55 HRC, steel should be reinforced by thermal treatement with the formation of multicomponent martensite–bainite structure. High-quality production should include defectoscopy and incoming material control.

Application of the Materials-by-Design Methodology to Redesign a New Grade of the High-Strength Low-Alloy Class of Steels with Improved Mechanical Properties and Processability

NASA Astrophysics Data System (ADS)

Grujicic, M.; Snipes, J. S.; Ramaswami, S.

2016-01-01

An alternative to the traditional trial-and-error empirical approach for the development of new materials is the so-called materials-by-design approach. Within the latter approach, a material is treated as a complex system and its design and optimization is carried out by employing computer-aided engineering analyses, predictive tools, and available material databases. In the present work, the materials-by-design approach is utilized to redesign a grade of high-strength low-alloy (HSLA) class of steels with improved mechanical properties (primarily strength and fracture toughness), processability (e.g., castability, hot formability, and weldability), and corrosion resistance. Toward that end, a number of material thermodynamics, kinetics of phase transformations, and physics of deformation and fracture computational models and databases have been developed/assembled and utilized within a multi-disciplinary, two-level material-by-design optimization scheme. To validate the models, their prediction is compared against the experimental results for the related steel HSLA100. Then the optimization procedure is employed to determine the optimal chemical composition and the tempering schedule for a newly designed grade of the HSLA class of steels with enhanced mechanical properties, processability, and corrosion resistance.

Microstructural evolution during aging of an Al-Cu-Li-Ag-Mg-Zr alloy

NASA Technical Reports Server (NTRS)

Kumar, K. S.; Brown, S. A.; Pickens, Joseph R.

1991-01-01

Alloys in the Al-Cu-Li Ag-Mg subsystem were developed that exhibit desirable combinations of strength and ductility. These Weldalite (trademark) alloys, are unique for Al-Cu-Li alloys in that with or without a prior cold stretching operation, they obtain excellent strength-ductility combinations upon natural and artificial aging. This is significant because it enables complex, near-net shape products such as forgings and super plastically formed parts to be heat treated to ultra-high strengths. On the other hand, commercial extrusions, rolled plates and sheets of other Al-Cu-Li alloys are typically subjected to a cold stretching operation before artificial aging to the highest strength tempers to introduce dislocations that provide low-energy nucleation sites for strengthening precipitates such as the T(sub 1) phase. The variation in yield strength (YS) with Li content in the near-peak aged condition for these Weldalite (trademark) alloys and the associated microstructures were examined, and the results are discussed.

76 FR 52379 - Buy America Waiver Notification

Federal Register 2010, 2011, 2012, 2013, 2014

2011-08-22

... 0.008 steel fiber with ultimate tensile strength of 290ksi for experimental use in Ultra High... for \\1/2\\'' x 0.008 steel fiber with ultimate tensile strength of 290ksi for experimental use in UHPC... there are no domestic manufacturers of \\1/2\\'' x 0.008 steel fiber with ultimate tensile strength of...

Microalloyed HSLA (High Strength Low Alloy) Steels: Proceedings of Microalloying 󈨜 Held in Conjunction with the 1988 World Materials Congress, Chicago, Illinois, USA, 24-30 September 1988

DTIC Science & Technology

1988-01-01

steels. The high quality linepipe steels are During the last few years, a large scale conducted. During the last few years, API X52 of efforts has been...with satisfied results. mass production of API X52 steels in production line will be demonstrated. The mass production of line pipe steels in the plate...mill of China Steel Corporation has also been conducted. More than eighty Procedures thousand tons of API X52 has been manufactured during the last 2

Mechanical properties and microstructure of copper alloys and copper alloy-stainless steel laminates for fusion reactor high heat flux applications

NASA Astrophysics Data System (ADS)

Leedy, Kevin Daniel

A select group of copper alloys and bonded copper alloy-stainless steel panels are under consideration for heat sink applications in first wall and divertor structures of a planned thermonuclear fusion reactor. Because these materials must retain high strengths and withstand high heat fluxes, their material properties and microstructures must be well understood. Candidate copper alloys include precipitate strengthened CuNiBe and CuCrZr and dispersion strengthened Cu-Alsb2Osb3 (CuAl25). In this study, uniaxial mechanical fatigue tests were conducted on bulk copper alloy materials at temperatures up to 500sp°C in air and vacuum environments. Based on standardized mechanical properties measurement techniques, a series of tests were also implemented to characterize copper alloy-316L stainless steel joints produced by hot isostatic pressing or by explosive bonding. The correlation between mechanical properties and the microstructure of fatigued copper alloys and the interface of copper alloy-stainless steel laminates was examined. Commercial grades of these alloys were used to maintain a degree of standardization in the materials testing. The commercial alloys used were OMG Americas Glidcop CuAl25 and CuAl15; Brush Wellman Hycon 3HP and Trefimetaux CuNiBe; and Kabelmetal Elbrodur and Trefimetaux CuCrZr. CuAl25 and CuNiBe alloys possessed the best combination of fatigue resistance and microstructural stability. The CuAl25 alloy showed only minimal microstructural changes following fatigue while the CuNiBe alloy consistently exhibited the highest fatigue strength. Transmission electron microscopy observations revealed that small matrix grain sizes and high densities of submicron strengthening phases promoted homogeneous slip deformation in the copper alloys. Thus, highly organized fatigue dislocation structure formation, as commonly found in oxygen-free high conductivity Cu, was inhibited. A solid plate of CuAl25 alloy hot isostatically pressed to a 316L stainless steel plate showed the best overall mechanical properties of the studied bi-metallic bonded panels. Bond properties were nominally inferior to constituent bulk material properties and fracture toughness values, in particular, were quite low for all bonded laminates. Delamination near the copper alloy-stainless steel interface was the dominate failure mode in the bi-metallic panels. The joining processes caused microstructural alterations in the bond interfacial regions including: microporosity, new precipitate formation, existing precipitate morphology changes and interdiffusion of constituent elements.

Large Scale Screening of Low Cost Ferritic Steel Designs For Advanced Ultra Supercritical Boiler Using First Principles Methods

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ouyang, Lizhi

Advanced Ultra Supercritical Boiler (AUSC) requires materials that can operate in corrosive environment at temperature and pressure as high as 760°C (or 1400°F) and 5000psi, respectively, while at the same time maintain good ductility at low temperature. We develop automated simulation software tools to enable fast large scale screening studies of candidate designs. While direct evaluation of creep rupture strength and ductility are currently not feasible, properties such as energy, elastic constants, surface energy, interface energy, and stack fault energy can be used to assess their relative ductility and creeping strength. We implemented software to automate the complex calculations tomore » minimize human inputs in the tedious screening studies which involve model structures generation, settings for first principles calculations, results analysis and reporting. The software developed in the project and library of computed mechanical properties of phases found in ferritic steels, many are complex solid solutions estimated for the first time, will certainly help the development of low cost ferritic steel for AUSC.« less

Influence of Short Austenitization Treatments on the Mechanical Properties of Low-Alloy Steels for Hot Forming Applications

NASA Astrophysics Data System (ADS)

Holzweissig, Martin Joachim; Lackmann, Jan; Konrad, Stefan; Schaper, Mirko; Niendorf, Thomas

2015-07-01

The current work elucidates an improvement of the mechanical properties of tool-quenched low-alloy steel by employing extremely short austenitization durations utilizing a press heating arrangement. Specifically, the influence of different austenitization treatments—involving austenitization durations ranging from three to 15 seconds—on the mechanical properties of low-alloy steel in comparison to an industrial standard furnace process was examined. A thorough set of experiments was conducted to investigate the role of different austenitization durations and temperatures on the resulting mechanical properties such as hardness, bending angle, tensile strength, and strain at fracture. The most important finding is that the hardness, the bending angle as well as the tensile strength increase with shortened austenitization durations. Furthermore, the ductility of the steels exhibits almost no difference following the short austenitization durations and the standard furnace process. The enhancement of the mechanical properties imposed by the short heat treatments investigated, is related to a refinement of microstructural features as compared to the standard furnace process.

Evaluation of a Diffusion/Trapping Model for Hydrogen Ingress in High- Strength Alloys

DTIC Science & Technology

1992-10-01

high-strength steels [3-5], precipitation -hardened and work-hardened nickel-base alloys [3-61, and titanium [71 and was shown to be effective in...other two alloys, Ti-13-11-3 was tested in the unaged and age- conditions to establish the role of the secondary (x phase precipitated during aging... maraging steel , so it probably takes the form of reversible trapping [5,29]. Hence, grain boundaries are considered to be the most likely sites for

Retention of ductility in high-strength steels

NASA Technical Reports Server (NTRS)

Parker, E. R.; Zackay, V. F.

1969-01-01

To produce high strength alloy steel with retention of ductility, include tempering, cooling and subsequent tempering. Five parameters for optimum results are pretempering temperature, amount of strain, strain rate, temperature during strain, and retempering temperature.

Influence of minor combined addition of Cr and Pr on microstructure, mechanical properties and corrosion behaviors of an ultrahigh strength Al-Zn-Mg-Cu-Zr alloy.

PubMed

Wang, Ming; Huang, Lanping; Chen, Kanghua; Liu, Wensheng

2018-01-01

This work focuses on controlling grain boundary structure in an ultra-high strength Al-8.6Zn-2.5Mg-2.2Cu-0.16Zr (wt.%) alloy by the combined addition of trace Cr (0.1wt.%) and Pr (0.14wt.%), and evaluating mechanical properties and localized corrosion behaviors of the alloy in the peak aged condition. The introduction of trace Cr and Pr leads to the formation of nanoscale Cr, Pr-containing Al 3 Zr and Zr-containing PrCr 2 Al 20 dispersoids which can obviously inhibit the recrystallization and sub-grain growth of the super-high strength Al-Zn-Mg-Cu alloys, and retain the deformation-recovery microstructure dominated by low-angle grain boundaries. The nearly ellipsoidal dispersoids with a size of 10-35nm are discretely distributed and precipitate free zones are hardly formed in low-angle grain boundaries. This new alloy composition exhibits better combined properties, higher resistance to stress corrosion, exfoliation corrosion and inter-granular corrosion with the undamaged strength, ductility and fracture toughness. Copyright © 2017 Elsevier Ltd. All rights reserved.

Demonstration of Ultra High-Strength Nanocrystalline Copper Alloys for Military Applications

DTIC Science & Technology

2012-01-22

Powder Processing vi Acknowledgements The development of these Cu -Ta alloys was accomplished with assistance from the following...nanostructured Cu -Ta based alloy powders with a unique ability to retain their ultrahigh strength properties to temperatures nearing the melting point of the Cu ...nanostructured Cu -Ta based alloy powders with the unique ability to retain their ultrahigh strength properties to temperatures

The use of Spark Plasma Sintering method for high-rate diffusion welding of high-strength UFG titanium alloys

NASA Astrophysics Data System (ADS)

Nokhrin, A. V.; Chuvil'deev, V. N.; Boldin, M. S.; Piskunov, A. V.; Kozlova, N. A.; Chegurov, M. K.; Popov, A. A.; Lantcev, E. A.; Kopylov, V. I.; Tabachkova, N. Yu

2017-07-01

The article provides an example of applying the technology of spark plasma sintering (SPS) to ensure high-rate diffusion welding of high-strength ultra-fine-grained UFG titanium alloys. Weld seams produced from Ti-5Al-2V UFG titanium alloy and obtained through SPS are characterized by high density, hardness and corrosion resistance.

The development of ultrahigh strength low alloy cast steels with increased toughness

NASA Astrophysics Data System (ADS)

Lynch, Paul C.

This work describes the initial work on the development of the next generation of ultrahigh strength low alloy (UHSLA) cast steels. These UHSLA cast steels have both ultrahigh strength levels and good impact toughness. The influence of heat treatment, secondary processing using hot isostatic processing (HIP), and chemical composition on the microstructure and properties of UHSLA cast steels have been evaluated. The extent of microsegregation reduction expected during the heat treatment of UHSLA cast steels has also been estimated by diffusion modeling. This new family of UHSLA cast steels is similar in composition and properties to UHSLA wrought steels. However, the heat treatment and secondary processing of the UHSLA cast steels is used to develop microstructures and properties typically developed through thermomechanical processing and heat treatment for wrought UHSLA steels. Two martensitic UHSLA steels, 4340+ (silicon modified 4340) and ES-1 were investigated for this study. For the 4340+ alloy, heat treatment variables evaluated include homogenization temperature and time, tempering temperature, and austempering temperature and time. For the ES-1 alloy, heat treatment variables evaluated include homogenization temperature and time, austenization temperature, cryogenic treatment, and tempering temperature. The effect of high temperature hot isostatic processing (HIP) on the 4340+ and ES- 1 alloys was also investigated. Tensile properties, charpy v-notch impact toughness (CVN), microstructures, and fractographs have all been characterized after heat treatment. The effects of HIP on microporosity reduction in the ES-1 alloy were also investigated. The experiments carried out on the investment cast 4340+ alloy have shown that increasing the homogenization temperature can increase CVN without changing the ultimate tensile strength (UTS) or yield strength (YS) of the cast material. By replacing the homogenization step in the conventional heat treatment process with a high temperature HIP treatment, both the CVN and ductility of the alloy was found to increase while maintaining comparable ultimate tensile strength (UTS) and yield strength (YS) levels as compared to the original homogenization treatment. Austempering the (IC) 4340+ material led to a significant increase in CVN and ductility at the expense of UTS and yield strength as the primarily martensitic microstructure was converted to a mixed martensitic-bainitic structure. An initial heat of induction melted, aluminum deoxidized investment cast ES-1 with 0.06 wt % of aluminum showed that the average -40°F and +72°F impact toughness, % elongation, and UTS and YS of the fully heat treated investment cast + HIP ES-1 material lagged significantly behind that of the vacuum degassed cast + HIP ES-1 ingot material. Even though the % elongation and impact toughness of the investment cast ES-1 material changed between heat treatment conditions, the average UTS and YS values remained relatively unchanged throughout the heat treatments for the investment cast study. Etched micrographs of the investment cast ES-1 material showed evidence of significant differences in microsegregation reduction between the samples homogenized at 2125°F for 4 hours and those not homogenized at 2125°F for 4 hours. SEM fracture surface work performed on the investment cast material clearly showed that the induction melted investment and aluminum killed cast material contained significant amounts of MnS and Al2O3 inclusions that were not discovered in the vacuum degassed cast ingot material. Lastly, the results of a third heat of induction melted, aluminum deoxidized investment cast ES-1 material possessing just 0.01wt% of aluminum showed that the decrease in aluminum content from the first experimental heat did not improve the mechanical properties of the investment cast material. (Abstract shortened by UMI.)

78 FR 63563 - Buy America Waiver Notification

Federal Register 2010, 2011, 2012, 2013, 2014

2013-10-24

.... steel fibers with ultimate tensile strength of 290 ksi. in Ultra High Performance Concrete (UHPC) at the... appropriate to use UHPC 0.5 in. x 0.008 in. steel fibers with ultimate tensile strength 290 ksi. on Federal... for the use of non-domestic UHPC 0.5 in. x 0.008 in. steel fibers with ultimate tensile strength of...

One-Step Quenching and Partitioning Heat Treatment of Medium Carbon Low Alloy Steel

NASA Astrophysics Data System (ADS)

Tariq, Fawad; Baloch, Rasheed Ahmed

2014-05-01

This paper presents the results of novel one-step quenching and partitioning (Q&P) heat treatment conducted on medium carbon low alloy steel sheet. Samples were austenitised at 1193 K followed by interrupted quenching at 473 K for different partitioning times and finally they were quenched in water. Dilatometry was employed for selection of treatment temperatures. Optical and scanning electron microscopy was carried out to examine the microstructural changes. Volume fraction of retained austenite was measured by x-ray diffraction technique. Resulting microstructures were correlated with the mechanical properties such hardness, tensile strength, elongation, impact absorbed energy, etc. The notch tensile and fracture toughness properties of Q&P steels are still lacking therefore notch tensile strength and plain strain fracture toughness tests were conducted and results are reported here. Results of Q&P treatments were also compared with the properties obtained by conventional Quenching and Tempering (Q&T) and normalizing treatments. Optimum strength-ductility balance of about 2000 MPa tensile strength with 11% elongation was achieved in samples quenched at 473 K and isothermally partitioned for 100 s. Higher ductility of Q&P steel was attributed to the presence of 6.8% film-type interlath retained austenite. Fine-grained martensitic structure with high density of interphase boundaries imparted ultrahigh strength. It was further noted that the impact toughness, notch tensile strength and fracture toughness of 1000 s partitioned samples was higher than 100 s partitioned samples. Possible reasons for high toughness are synergetic effect of recovery of dislocations, partial loss of martensite tetragonality and precipitation of fine transition carbides.

A Modified Constitutive Model for Tensile Flow Behaviors of BR1500HS Ultra-High-Strength Steel at Medium and Low Temperature Regions

NASA Astrophysics Data System (ADS)

Zhao, Jun; Quan, Guo-Zheng; Pan, Jia; Wang, Xuan; Wu, Dong-Sen; Xia, Yu-Feng

2018-01-01

Constitutive model of materials is one of the most requisite mathematical model in the finite element analysis, which describes the relationships of flow behaviors with strain, strain rate and temperature. In order to construct such constitutive relationships of ultra-high-strength BR1500HS steel at medium and low temperature regions, the true stress-strain data over a wide temperature range of 293-873 K and strain rate range of 0.01-10 s-1 were collected from a series of isothermal uniaxial tensile tests. The experimental results show that stress-strain relationships are highly non-linear and susceptible to three parameters involving temperature, strain and strain rate. By considering the impacts of strain rate and temperature on strain hardening, a modified constitutive model based on Johnson-Cook model was proposed to characterize flow behaviors in medium and low temperature ranges. The predictability of the improved model was also evaluated by the relative error (W(%)), correlation coefficient (R) and average absolute relative error (AARE). The R-value and AARE-value for modified constitutive model at medium and low temperature regions are 0.9915 & 1.56 % and 0.9570 & 5.39 %, respectively, which indicates that the modified constitutive model can precisely estimate the flow behaviors for BR1500HS steel in the medium and low temperature regions.

Alternatives to steel grid decks - phase II.

DOT National Transportation Integrated Search

2012-09-01

The primary objective of this research project was to investigate alternatives to open grid steel decks for movable bridges. Three alternative deck systems, including aluminum deck, ultra-high performance concrete (UHPC)-high-strength steel (HSS) dec...

Low activation ferritic alloys

DOEpatents

Gelles, David S.; Ghoniem, Nasr M.; Powell, Roger W.

1986-01-01

Low activation ferritic alloys, specifically bainitic and martensitic stainless steels, are described for use in the production of structural components for nuclear fusion reactors. They are designed specifically to achieve low activation characteristics suitable for efficient waste disposal. The alloys essentially exclude molybdenum, nickel, nitrogen and niobium. Strength is achieved by substituting vanadium, tungsten, and/or tantalum in place of the usual molybdenum content in such alloys.

Low activation ferritic alloys

DOEpatents

Gelles, D.S.; Ghoniem, N.M.; Powell, R.W.

1985-02-07

Low activation ferritic alloys, specifically bainitic and martensitic stainless steels, are described for use in the production of structural components for nuclear fusion reactors. They are designed specifically to achieve low activation characteristics suitable for efficient waste disposal. The alloys essentially exclude molybdenum, nickel, nitrogen and niobium. Strength is achieved by substituting vanadium, tungsten, and/or tantalum in place of the usual molybdenum content in such alloys.

Interfacial Characterization of Dissimilar Joints Between Al/Mg/Al-Trilayered Clad Sheet to High-Strength Low-Alloy Steel

NASA Astrophysics Data System (ADS)

Macwan, A.; Jiang, X. Q.; Chen, D. L.

2015-07-01

Magnesium (Mg) alloys are increasingly used in the automotive and aerospace sectors to reduce vehicle weight. Al/Mg/Al tri-layered clad sheets are deemed as a promising alternative to improve the corrosion resistance and formability of Mg alloys. The structural application of Al/Mg/Al tri-layered clad sheets inevitably involves welding and joining in the multi-material vehicle body manufacturing. This study aimed to characterize the bonding interface microstructure of the Al/Mg/Al-clad sheet to high-strength low-alloy steel with and without Zn coating using ultrasonic spot welding at different levels of welding energy. It was observed that the presence of Zn coating improved the bonding at the interface due to the formation of Al-Zn eutectic structure via enhanced diffusion. At a higher level of welding energy, characteristic flow patterns of Zn into Al-clad layer were observed with an extensive penetration mainly along some high angle grain boundaries. The dissimilar joints without Zn coating made at a high welding energy of 800 J failed partially from the Al/Fe weld interface and partially from the Al/Mg clad interface, while the joints with Zn coating failed from the Al/Mg clad interface due to the presence of brittle Al12Mg17 phase.

Influence of Cyclic Straining on Fatigue, Deformation, and Fracture Behavior of High-Strength Alloy Steel

NASA Astrophysics Data System (ADS)

Manigandan, K.; Srivatsan, T. S.; Vasudevan, V. K.; Tammana, D.; Poorganji, B.

2016-01-01

In this paper, the results of a study on microstructural influences on mechanical behavior of the high-strength alloy steel Tenax™ 310 are presented and discussed. Under the influence of fully reversed strain cycling, the stress response of this alloy steel revealed softening from the onset of deformation. Cyclic strain resistance exhibited a linear trend for the variation of both elastic strain amplitude with reversals-to-failure, and plastic strain amplitude with reversals-to-failure. Fracture morphology was essentially the same at the macroscopic level over the entire range of cyclic strain amplitudes examined. However, at the fine microscopic level, this high-strength alloy steel revealed fracture to be mixed-mode with features reminiscent of "locally" ductile and brittle mechanisms. The macroscopic mechanisms governing stress response at the fine microscopic level, resultant fatigue life, and final fracture behavior are presented and discussed in light of the mutually interactive influences of intrinsic microstructural effects, deformation characteristics of the microstructural constituents during fully reversed strain cycling, cyclic strain amplitude, and resultant response stress.

High strength and high toughness steel

DOEpatents

Parker, Earl R.; Zackay, Victor F.

1979-01-01

A structural steel which possess both high strength and high toughness and has particular application of cryogenic uses. The steel is produced by the utilization of thermally induced phase transformation following heating in a three-phase field in iron-rich alloys of the Fe-Ni-Ti system, with a preferred composition of 12% nickel, 0.5% titanium, the remainder being iron.

Shape effect of ultrafine-grained structure on static fracture toughness in low-alloy steel.

PubMed

Inoue, Tadanobu; Kimura, Yuuji; Ochiai, Shojiro

2012-06-01

A 0.4C-2Si-1Cr-1Mo steel with an ultrafine elongated grain (UFEG) structure and an ultrafine equiaxed grain (UFG) structure was fabricated by multipass caliber rolling at 773 K and subsequent annealing at 973 K. A static three-point bending test was conducted at ambient temperature and at 77 K. The strength-toughness balance of the developed steels was markedly better than that of conventionally quenched and tempered steel with a martensitic structure. In particular, the static fracture toughness of the UFEG steel, having a yield strength of 1.86 GPa at ambient temperature, was improved by more than 40 times compared with conventional steel having a yield strength of 1.51 GPa. Furthermore, even at 77 K, the fracture toughness of the UFEG steel was about eight times higher than that of the conventional and UFG steels, despite the high strength of the UFEG steel (2.26 GPa). The UFG steel exhibited brittle fracture behavior at 77 K, as did the conventional steel, and no dimple structure was observed on the fracture surface. Therefore, it is difficult to improve the low-temperature toughness of the UFG steel by grain refinement only. The shape of crystal grains plays an important role in delamination toughening, as do their refinement and orientation.

Galvanizing and Galvannealing Behavior of CMnSiCr Dual-Phase Steels

NASA Astrophysics Data System (ADS)

Lin, Ko-Chun; Chu, Peng-Wei; Lin, Chao-Sung; Chen, Hon-Bor

2013-06-01

Alloying elements, such as Mn, Mo, Si, and Cr, are commonly used to enhance the strength of advanced high-strength steels. Those elements also play an important role in the hot-dip galvanizing (GI) and galvannealing (GA) process. In this study, two kinds of CMnSiCr dual-phase steels were galvanized and galvannealed using a hot-dip simulator to investigate the effect of the alloying elements on the microstructure of the GI and GA coatings. The results showed that the dual-phase steels had good galvanizability because no bare spots were observed and the Fe-Zn phases were readily formed at the interface. However, the alloying reaction during the GA process was significantly hindered. XPS analysis showed that external oxidation occurred under an extremely low dew point [213 K to 203 K (-60 °C to -70 °C)] atmosphere during the annealing prior to hot dipping. However, most of the oxides were reduced during the GI process. After the GI process, the Al was present as solid solutes in the Fe-Zn phase, suggesting that the Fe-Zn phase was formed from the transformation of the Fe-Al inhibition alloy. Meanwhile, the solubility of Si in the ζ phase was extremely low. With continued GA reaction, the ζ phase transformed into the δ phase, which contained approximately 1.0 at.pct Si. The Si also diffused into the Zn layer during the GA reaction. Hence, the ζ phase did not homogeneously nucleate at the steel substrate/Zn coating interface, but was found at the area away from the interface. Therefore, the Fe-Zn phases on the CMnSiCr dual-phase steels were relatively non-uniform compared to those on interstitial-free steel.

Fundamental Studies of Phase Transformations and Mechanical Properties in the Heat Affected Zone of 10 wt% Nickel Steel

NASA Astrophysics Data System (ADS)

Barrick, Erin J.

United States naval applications require the use of steels with high strength and resistance to fracture at low temperatures to provide good ballistic properties. In recent years, 10 wt% Ni steel has been developed with strength and toughness values exceeding those of steels currently used, and is now being considered as a candidate material to replace existing high-strength, low alloy steels. This steel has excellent toughness from the mechanically induced transformation of interlath austenite films to martensite. These austenite films are formed via a carefully developed quenching, lamellarizing, and tempering heat treatment. However, before 10 wt% Ni steel can be implemented for full-scale applications, the effects of the rapid heating and cooling rates associated with welding thermal cycles on phase transformations and mechanical properties must be understood. In this research, a fundamental understanding of phase transformations and mechanical properties in the heat-affected zone of fusion welds in 10 wt% Ni steel was developed through heating and cooling rate dilatometry experiments, gas tungsten arc welding, and simulation of gas metal arc welding. First, an investigation into the effects of heating and cooling rate on the phase transformations in 10 wt% Ni steel was performed. The Ac1 and Ac3 temperatures during heating were determined as a function of heating rate, and sluggish transformation during fast heating rates manifested itself as a high Ac3 temperature of 1050°C as opposed to a temperature of 850°C at slow heating rates. A continuous cooling transformation diagram produced for 10 wt% Ni steel reveals that martensite will form over a very wide range of cooling rates, which reflects a very high hardenability of this alloy. This is significant because the range of cooling rates for which the diagram was constructed over easily covers the range associated with fusion welding, so there would not be the need for precise control over the weld processing conditions. The microstructures observed in a single pass gas tungsten arc weld were rationalized with the observations from the heating and cooling rate experiments. The microhardness of gas tungsten arc weld is highest in the intercritical heat affected zone, which is unexpected based on the usual behavior of quench and tempered steels. The hardness of the heat affected zone is always higher than the base metal which is a promising outcome. Having understood the overall effects of heating and cooling on the phase transformations in 10 wt% Ni steel, the microstructure and mechanical property evolution through the heat affected zone was investigated. A Gleeble 3500 thermo-mechanical simulator was used to replicate microstructures observed in the gas-tungsten arc weld, and the microstructural factors influencing the strength and toughness in the simulated heat affected zone samples were correlated to mechanical property results. The strength is the highest in the intercritical heat-affected zone, mostly attributed to microstructural refinement. With increasing peak temperature of the thermal cycle, the volume fraction of retained austenite decreases. The local atom probe tomography results suggest this is due to the destabilization of the austenite brought on by the diffusion of Ni out of the austenite. There is a local low toughness region in the intercritical heat-affected zone, corresponding to a low retained austenite content. However, the retained austenite is similarly low in higher peak temperature regions but the toughness is high. This suggests that while 10 wt% Ni steel is a TRIP-assisted steel and thus obtains high toughness from the plasticity-induced martensite to austenite transformation, the toughness of the steel is also based on other microstructural factors. Overall, the results presented in this work have established, for the first time, the effects of rapid heating and cooling on the phase transformations and mechanical properties in 10 wt% Ni steel, and have started to identify the microstructural features influencing the strength and toughness of this alloy.

Oxidation resistant high creep strength austenitic stainless steel

DOEpatents

Brady, Michael P.; Pint, Bruce A.; Liu, Chain-Tsuan; Maziasz, Philip J.; Yamamoto, Yukinori; Lu, Zhao P.

2010-06-29

An austenitic stainless steel displaying high temperature oxidation and creep resistance has a composition that includes in weight percent 15 to 21 Ni, 10 to 15 Cr, 2 to 3.5 Al, 0.1 to 1 Nb, and 0.05 to 0.15 C, and that is free of or has very low levels of N, Ti and V. The alloy forms an external continuous alumina protective scale to provide a high oxidation resistance at temperatures of 700 to 800.degree. C. and forms NbC nanocarbides and a stable essentially single phase fcc austenitic matrix microstructure to give high strength and high creep resistance at these temperatures.

Metallurgical/Alloy Optimization of High Strength and Wear Resistant Structural Quench and Tempered Steels

NASA Astrophysics Data System (ADS)

Stalheim, Douglas G.; Peimao, Fu; Linhao, Gu; Yongqing, Zhang

Structural steels with yield strength requirements greater or equal to 690 MPa can be produced through controlled recrystallization hot rolling coupled with precipitation strengthening or purposeful heat treatment through quench and tempering (Q&T). High strength structural steel and wear/abrasion resistant requirements greater or equal to 360 Brinell hardness (BHN) are produced by the development of microstructures of tempered lower bainite and/or martensite through the Q&T process. While these Q&T microstructures can produce very high strengths and hardness levels making them ideal for 690 MPa plus yield strength or wear/abrasion resistant applications, they lack toughness/ductility and hence are very brittle and prone to cracking. While tempering the microstructures helps in improving the toughness/ductility and reducing the brittleness, strength and hardness can be sacrificed. In addition, these steels typically consist of alloy designs containing boron with carbon equivalents (CE) greater than 0.50 to achieve the desired microstructures. The higher CE has a negative influence on weldability.

Characterization of ultrafine grained Cu-Ni-Si alloys by electron backscatter diffraction

NASA Astrophysics Data System (ADS)

Altenberger, I.; Kuhn, H. A.; Gholami, M.; Mhaede, M.; Wagner, L.

2014-08-01

A combination of rotary swaging and optimized precipitation hardening was applied to generate ultra fine grained (UFG) microstructures in low alloyed high performance Cu-based alloy CuNi3Si1Mg. As a result, ultrafine grained (UFG) microstructures with nanoscopically small Ni2Si-precipitates exhibiting high strength, ductility and electrical conductivity can be obtained. Grain boundary pinning by nano-precipitates enhances the thermal stability. Electron channeling contrast imaging (ECCI) and especially electron backscattering diffraction (EBSD) are predestined to characterize the evolving microstructures due to excellent resolution and vast crystallographic information. The following study summarizes the microstructure after different processing steps and points out the consequences for the most important mechanical and physical properties such as strength, ductility and conductivity.

A Study of the Efficiency of High-strength, Steel, Cellular-core Sandwich Plates in Compression

NASA Technical Reports Server (NTRS)

Johnson, Aldie E , Jr; Semonian, Joseph W

1956-01-01

Structural efficiency curves are presented for high-strength, stainless-steel, cellular-core sandwich plates of various proportions subjected to compressive end loads for temperatures of 80 F and 600 F. Optimum proportions of sandwich plates for any value of the compressive loading intensity can be determined from the curves. The efficiency of steel sandwich plates of optimum proportions is compared with the efficiency of solid plates of high-strength steel and aluminum and titanium alloys at the two temperatures.

Latest Development and Application of Nb-Bearing High Strength Pipeline Steels

NASA Astrophysics Data System (ADS)

Zhang, Yongqing; Shang, Chengjia; Guo, Aimin; Zheng, Lei; Niu, Tao; Han, Xiulin

In order to solve the pollution problem emerging in China recently, China's central government is making great efforts to raise the percentage of natural gas consumption in the China's primary energy mix, which needs to construct big pipelines to transport natural gas from the nation's resource-rich western regions to the energy-starved east, as well as import from the Central Asia and Russia. With this mainstream trend, high strength, high toughness, heavy gauge, and large diameter pipeline steels are needed to improve the transportation efficiency. This paper describes the latest progresses in Nb-bearing high strength pipeline steels with regard to metallurgical design, development and application, including X80 coil with a thickness up to 22.0mm, X80 plate with a diameter as much as 1422mm, X80 plate with low-temperature requirements and low-Mn sour service X65 for harsh sour service environments. Moreover, based on widely accepted TMCP and HTP practices with low carbon and Nb micro-alloying design, this paper also investigated some new metallurgical phenomena based on powerful rolling mills and heavy ACC equipment.

The development of high strength corrosion resistant precipitation hardening cast steels

NASA Astrophysics Data System (ADS)

Abrahams, Rachel A.

Precipitation Hardened Cast Stainless Steels (PHCSS) are a corrosion resistant class of materials which derive their properties from secondary aging after a normalizing heat treatment step. While PHCSS materials are available in austenitic and semi-austenitic forms, the martensitic PHCSS are most widely used due to a combination of high strength, good toughness, and corrosion resistance. If higher strength levels can be achieved in these alloys, these materials can be used as a lower-cost alternative to titanium for high specific strength applications where corrosion resistance is a factor. Although wrought precipitation hardened materials have been in use and specified for more than half a century, the specification and use of PHCSS has only been recent. The effects of composition and processing on performance have received little attention in the cast steel literature. The work presented in these investigations is concerned with the experimental study and modeling of microstructural development in cast martensitic precipitation hardened steels at high strength levels. Particular attention is focused on improving the performance of the high strength CB7Cu alloy by control of detrimental secondary phases, notably delta ferrite and retained austenite, which is detrimental to strength, but potentially beneficial in terms of fracture and impact toughness. The relationship between age processing and mechanical properties is also investigated, and a new age hardening model based on simultaneous precipitation hardening and tempering has been modified for use with these steels. Because the CB7Cu system has limited strength even with improved processing, a higher strength prototype Fe-Ni-Cr-Mo-Ti system has been designed and adapted for use in casting. This prototype is expected to develop high strengths matching or exceed that of cast Ti-6Al-4V alloys. Traditional multicomponent constitution phase diagrams widely used for phase estimation in conventional stainless steels, give poor estimates of secondary phases in PHCSS. No measureable retained austenite was observed in any of the CB7Cu-1 steels studied, in spite of the fact that austenite is predicted by the constitution diagrams. A designed experiment using computationally derived phase equilibrium diagrams and actual experimental tests on CB7Cu of different compositions suggests that the ferrite phase is less stable than the constitution diagrams for austenitic stainless steels suggest. Delta ferrite was also more stable in slower-cooled sand cast material as compared to thin, fast-cooled investment cast material. High temperature solutionizing treatments were effective in dissolving delta ferrite at temperatures above 1900°F (˜1040°C). Delta ferrite dissolution was found to proceed at high rates during initial dissolution, and then was found to slow after 1 hour. Diffusion during the later stages is well-predicted by classical diffusion models. Repeated solution treatments were found to modestly increase both ductility and strength, likely due to subgrain refinement through austenite regrowth. Multistaged aging provided superior strength and toughness increases over similarly peak-aged and near peak-aged material aged at a single temperature. Peak-aged material fractography suggested that low energy quasi-cleavage fracture was likely due to age precipitate embrittlement along with some nucleation of MnS particulates at prior austenite grain boundaries. Yield strengths approaching 190 ksi (1310MPa) can be achieved in CB7Cu-1 if appropriate best-practices "+" processing techniques are used. This includes hot isostatic processing to reduce solidification segregation and heal microporosity, high temperature homogenization for effective age hardening and ferrite reduction, double-cycle solutionizing for structure refinement, and multistaged age strengthening for finer precipitate control. The experimental prototype 11-11PH (Fe-Ni-Cr-Ti-Mo) casting alloys was cast and was found to be delta-ferrite free in the as-cast condition. In this material, proper quench processing to eliminate excessive retained austenite was found to be most influential in terms of high strengths. It was also found that cooling below 0°C provided the best combination of strength and toughness, with the specific strength of the material exceeding that of cast Ti-6Al-4V material. Fractography studies suggest that titanium carbonitride and titanium carbon-nitride-sulfide inclusions limit the toughness of cast materials due to long exposures to ideal growth conditions during initial cooling. OIM studies also suggest that the retained austenite in properly processed 11-11PH alloy takes on an interlath structure, which likely contributes to toughness of the alloy, even at high-strength, peak aged conditions. Yield strengths approaching 235 ksi (1620 MPa) were achieved during initial heat treatment trials. It is expected that further improvements in properties can be achieved with continued improvement of processing for this new cast alloy system.

The influence of high heat input and inclusions control for rare earth on welding in low alloy high strength steel

NASA Astrophysics Data System (ADS)

Chu, Rensheng; Mu, Shukun; Liu, Jingang; Li, Zhanjun

2017-09-01

In the current paper, it is analyzed for the influence of high heat input and inclusions control for rare earth on welding in low alloy high strength steel. It is observed for the structure for different heat input of the coarse-grained area. It is finest for the coarse grain with the high heat input of 200 kJ / cm and the coarse grain area with 400 kJ / cm is the largest. The performance with the heat input of 200 kJ / cm for -20 °C V-shaped notch oscillatory power is better than the heat input of 400 kJ / cm. The grain structure is the ferrite and bainite for different holding time. The grain structure for 5s holding time has a grain size of 82.9 μm with heat input of 200 kJ/cm and grain size of 97.9 μm for 10s holding time. For the inclusions for HSLA steel with adding rare earth, they are Al2O3-CaS inclusions in the Al2O3-CaS-CaO ternary phase diagram. At the same time, it can not be found for low melting calcium aluminate inclusions compared to the inclusions for the HSLA steel without rare earth. Most of the size for the inclusions is between 1 ~ 10μm. The overall grain structure is smaller and the welding performance is more excellent for adding rare earth.

High Temperature Strengthening in 12Cr-W-Mo Steels by Controlling the Formation of Delta Ferrite

NASA Astrophysics Data System (ADS)

Wang, Shushen; Chang, Li; Lin, Deye; Chen, Xiaohua; Hui, Xidong

2014-09-01

Novel 12Cr-W-Mo-Co heat resistance steels (HRSs) with excellent mechanical properties have been developed for ultra-supercritical (USC) applications above 923 K (650 °C). The thermal analysis of the present steels indicates that the remelting temperature of secondary phases is increased by Co alloying, resulting in the improvement of microstructural stability. Delta ferrite in these HRSs is completely suppressed as the content of Co is increased up to 5 pct. The room temperature tensile strength (TS), yield strength (YS), and the elongation (EL) of the HRS with 5 pct Co reach 887.9, 652.6 MPa, and 21.07 pct, respectively. At 948 K (675 °C), the TS and YS of the HRS with 5 pct Co attain 360 and 290 MPa, respectively, which are higher than those of T/P122 steel by 27.4 and 22.1 pct, respectively. TEM study of the microstructure confirmed that the strengthening effects for these 12Cr-W-Mo-Co HRSs are attributed to the suppression of delta ferrite, the formation of fine martensitic laths with substructure, dislocation networks and walls, and the precipitation of second nanoscale phases.

Brazing process provides high-strength bond between aluminum and stainless steel

NASA Technical Reports Server (NTRS)

Huschke, E. G., Jr.; Nord, D. B.

1966-01-01

Brazing process uses vapor-deposited titanium and an aluminum-zirconium-silicon alloy to prevent formation of brittle intermetallic compounds in stainless steel and aluminum bonding. Joints formed by this process maintain their high strength, corrosion resistance, and hermetic sealing properties.

Microstructural Developments Leading to New Advanced High Strength Sheet Steels: A Historical Assessment of Critical Metallographic Observations

DOE Office of Scientific and Technical Information (OSTI.GOV)

Matlock, David K; Thomas, Larrin S; Taylor, Mark D

In the past 30+ years significant advancements have been made in the development of higher strength sheet steels with improved combinations of strength and ductility that have enabled important product improvements leading to safer, lighter weight, and more fuel efficient automobiles and in other applications. Properties of the primarily low carbon, low alloy steels are derived through careful control of time-temperature processing histories designed to produce multiphase ferritic based microstructures that include martensite and other constituents including retained austenite. The basis for these developments stems from the early work on dual-phase steels which was the subject of much interest. Inmore » response to industry needs, dual-phase steels have evolved as a unique class of advanced high strength sheet steels (AHSS) in which the thermal and mechanical processing histories have been specifically designed to produce constituent combinations for the purpose of simultaneously controlling strength and deformation behavior, i.e. stress-strain curve shapes. Improvements continue as enhanced dual-phase steels have recently been produced with finer microstructures, higher strengths, and better overall formability. Today, dual phase steels are the primary AHSS products used in vehicle manufacture, and several companies have indicated that the steels will remain as important design materials well into the future. In this presentation, fundamental results from the early work on dual-phase steels will be reviewed and assessed in light of recent steel developments. Specific contributions from industry/university cooperative research leading to product improvements will be highlighted. The historical perspective provided in the evolution of dual-phase steels represents a case-study that provides important framework and lessons to be incorporated in next generation AHSS products.« less

Development of cast alumina-forming austenitic stainless steels

DOE PAGES

Muralidharan, G.; Yamamoto, Y.; Brady, M. P.; ...

2016-09-06

Cast Fe-Ni-Cr chromia-forming austenitic stainless steels with Ni levels up to 45 wt. % are used at high temperatures in a wide range of industrial applications that demand microstructural stability, corrosion resistance, and creep strength. Although alumina scales offer better corrosion protection at these temperatures, designing cast austenitic alloys that form a stable alumina scale and achieve creep strength comparable to existing cast chromia-forming alloys is challenging. This work outlines the development of cast Fe-Ni-Cr-Al austenitic stainless steels containing about 25 wt. % Ni with good creep strength and the ability to form a protective alumina scale for use atmore » temperatures up to 800 C - 850 C in H 2O-, S-, and C- containing environments. Creep properties of the best alloy were comparable to that of HK-type cast chromia-forming alloy along with improved oxidation resistance typical of alumina-forming alloys. Lastly, challenges in the design of cast alloys and a potential path to increasing the temperature capability are discussed.« less

Development of Cast Alumina-Forming Austenitic Stainless Steels

NASA Astrophysics Data System (ADS)

Muralidharan, G.; Yamamoto, Y.; Brady, M. P.; Walker, L. R.; Meyer, H. M., III; Leonard, D. N.

2016-11-01

Cast Fe-Ni-Cr chromia-forming austenitic stainless steels with Ni levels up to 45 wt.% are used at high temperatures in a wide range of industrial applications that demand microstructural stability, corrosion resistance, and creep strength. Although alumina scales offer better corrosion protection at these temperatures, designing cast austenitic alloys that form a stable alumina scale and achieve creep strength comparable to existing cast chromia-forming alloys is challenging. This work outlines the development of cast Fe-Ni-Cr-Al austenitic stainless steels containing about 25 wt.% Ni with good creep strength and the ability to form a protective alumina scale for use at temperatures up to 800-850°C in H2O-, S-, and C-containing environments. Creep properties of the best alloy were comparable to that of HK-type cast chromia-forming alloys along with improved oxidation resistance typical of alumina-forming alloys. Challenges in the design of cast alloys and a potential path to increasing the temperature capability are discussed.

Effect of single and double austenitization treatments on the microstructure and mechanical properties of 16Cr-2Ni steel

NASA Astrophysics Data System (ADS)

Balan, K. P.; Reddy, A. Venugopal; Sarma, D. S.

1999-06-01

Double austenitization (DA) treatment is found to yield the best combination of strength and toughness in both low-temperature as well as high-temperature tempered conditions as compared to single austenitization (SA) treatments. Obtaining the advantages of double austenitization (DA) to permit dissolution of alloy carbides without significant grain coarsening was attempted in AISI 431 type martensitic stainless steel. Structure-property correlation after low-temperature tempering (200 °C) as well as high-temperature double tempering (650+600 °C) was carried out for three austenitization treatments through SA at 1000 °C, SA at 1070 °C, and DA at 1070+1000 °C. While the increase in strength after DA treatment and low-temperature tempering at 200 °C is due to the increased amount of carbon in solution as a result of dissolution of alloy carbides during first austenitization, the increased toughness is attributable to the increased quantity of retained austenite. After double tempering (650+600 °C), strength and toughness are mainly found to depend on the precipitation and distribution of carbides in the microstructure and the grain size effect.

Influence of the thermodynamic parameters on the temper embrittlement of SA508 Gr.4N Ni-Cr-Mo low alloy steel with variation of Ni, Cr and Mn contents

NASA Astrophysics Data System (ADS)

Park, Sang-Gyu; Lee, Ki-Hyoung; Min, Ki-Deuk; Kim, Min-Chul; Lee, Bong-Sang

2012-07-01

It is well known that SA508 Gr.4N low alloy steel offers improved fracture toughness and strength compared to commercial low alloy steels such as SA508 Gr.3 Mn-Mo-Ni low alloy steel. In this study, the effects of Cr, Mn, and Ni on temper embrittlement in SA508 Gr.4N low alloy steel were evaluated from the viewpoint of thermodynamic parameters such as P diffusivity and C activity. The changes of the ductile-brittle transition temperatures before and after aging were correlated with varying alloying element content, and the diffusivity of P and the activity of C were calculated and correlated with the transition behaviors. The addition of Ni, Cr, and Mn reduce the resistance to temper embrittlement, showing increased Transition-Temperature Shift (TTS) and an increased fraction of intergranular fracture. Although the diffusivity of P is changed by the addition of alloying elements, it does not considerably affect the temper embrittlement. The Mn and Cr content in the matrix significantly reduce the C activity, with showing an inversely proportional relationship to TTS. The change of susceptibility to temper embrittlement caused by Cr and Mn addition could be explained by the variation of C activity. Unlike Cr and Mn, Ni has little effect on the temper embrittlement and C activity.

Determination of the continuous cooling transformation diagram of a high strength low alloyed steel

NASA Astrophysics Data System (ADS)

Kang, Hun Chul; Park, Bong June; Jang, Ji Hun; Jang, Kwang Soon; Lee, Kyung Jong

2016-11-01

The continuous cooling transformation diagram of a high strength low alloyed steel was determined by a dilatometer and microscopic analysis (OM, SEM) as well as thermodynamic analysis. As expected, Widmanstätten ferrite, bainite and martensite coexisted for most cooling rates, which made it difficult to determine the transformation kinetics of individual phases. However, peaks were clearly observed in the dilatometric {d( {LVDT} )}/{dT} curves. By overlapping the {d( {LVDT} )}/{dT} curves, which were determined using various cooling rates, peaks were separated and the peak rate temperatures, as well as the temperature at the start of transformation (5%) and the end of transformation (95%) of an individual phase, were determined. A SEM analysis was also conducted to identify which phase existed and to quantify the volume fraction of each phase. It was confirmed that the additional {d( {LVDT} )}/{dT} curve analysis described the transformation behavior more precisely than the conventional continuous cooling transformation diagram, as determined by the volume measured from the microstructure analysis.

Prediction of Microstructure in High-Strength Ductile Forging Parts

NASA Astrophysics Data System (ADS)

Urban, M.; Keul, C.; Back, A.; Bleck, W.; Hirt, G.

2010-06-01

Governmental, environmental and economic demands call for lighter, stiffer and at the same time cheaper products in the vehicle industry. Especially safety relevant parts have to be stiff and at the same time ductile. The strategy of this project was to improve the mechanical properties of forging steel alloys by employing a high-strength and ductile bainitic microstructure in the parts while maintaining cost effective process chains to reach these goals for high stressed forged parts. Therefore, a new steel alloy combined with an optimized process chain has been developed. To optimize the process chain with a minimum of expensive experiments, a numerical approach was developed to predict the microstructure of the steel alloy after the process chain based on FEM simulations of the forging and cooling combined with deformation-time-temperature-transformation-diagrams.

Development of Creep-Resistant, Alumina-Forming Ferrous Alloys for High-Temperature Structural Use

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yamamoto, Yukinori; Brady, Michael P.; Muralidharan, Govindarajan

This paper overviews recent advances in developing novel alloy design concepts of creep-resistant, alumina-forming Fe-base alloys, including both ferritic and austenitic steels, for high-temperature structural applications in fossil-fired power generation systems. Protective, external alumina-scales offer improved oxidation resistance compared to chromia-scales in steam-containing environments at elevated temperatures. Alloy design utilizes computational thermodynamic tools with compositional guidelines based on experimental results accumulated in the last decade, along with design and control of the second-phase precipitates to maximize high-temperature strengths. The alloys developed to date, including ferritic (Fe-Cr-Al-Nb-W base) and austenitic (Fe-Cr-Ni-Al-Nb base) alloys, successfully incorporated the balanced properties of steam/water vapor-oxidationmore » and/or ash-corrosion resistance and improved creep strength. Development of cast alumina-forming austenitic (AFA) stainless steel alloys is also in progress with successful improvement of higher temperature capability targeting up to ~1100°C. Current alloy design approach and developmental efforts with guidance of computational tools were found to be beneficial for further development of the new heat resistant steel alloys for various extreme environments.« less

High Yield Strength Cast Steel With Improved Weldability

DTIC Science & Technology

1991-05-01

Transformation ( CCT ) diagram presented in Figure 25. It is clear that these low carbon steels generally will produce martensite and~or bainite over a very wide...microstructure. The CCT diagram developed from the Gleeble evaluations appears to indicate a martensite start (MJ temperature of approximately 800° F...Regardless of the exact identity of the transformation products, the CCT diagram contains the features desired for the experimental alloy system

Effects of Residual Impurities on Hydrogen Assisted Cracking in High Strength Steels. Part II.

DTIC Science & Technology

1982-06-01

source of hydrogen is the corrosion reaction of steel with aqueous hydrogen sulfide solutions encountered either in the production of crude oil and...autoradiography technique, it has been shown that in Armco iron and in maraging steel of hydrogen is trapped at prior austenite grain boundaries. Tritium...also play a deleterious role in hydrogen-induced cracking. In these ultra-high strength steels , the crack-tip stress level and the concomitant stress

High temperature alloy

NASA Technical Reports Server (NTRS)

Frank, R. G.; Semmel, J. W., Jr.

1968-01-01

Molybdenum is substituted for tungsten on an atomic basis in a cobalt-based alloy, S-1, thus enabling the alloy to be formed into various mill products, such as tubing and steels. The alloy is weldable, has good high temperature strength and is not subject to embrittlement produced by high temperature aging.

Convection in containerless processing.

PubMed

Hyers, Robert W; Matson, Douglas M; Kelton, Kenneth F; Rogers, Jan R

2004-11-01

Different containerless processing techniques have different strengths and weaknesses. Applying more than one technique allows various parts of a problem to be solved separately. For two research projects, one on phase selection in steels and the other on nucleation and growth of quasicrystals, a combination of experiments using electrostatic levitation (ESL) and electromagnetic levitation (EML) is appropriate. In both experiments, convection is an important variable. The convective conditions achievable with each method are compared for two very different materials: a low-viscosity, high-temperature stainless steel, and a high-viscosity, low-temperature quasicrystal-forming alloy. It is clear that the techniques are complementary when convection is a parameter to be explored in the experiments. For a number of reasons, including the sample size, temperature, and reactivity, direct measurement of the convective velocity is not feasible. Therefore, we must rely on computation techniques to estimate convection in these experiments. These models are an essential part of almost any microgravity investigation. The methods employed and results obtained for the projects levitation observation of dendrite evolution in steel ternary alloy rapid solidification (LODESTARS) and quasicrystalline undercooled alloys for space investigation (QUASI) are explained.

Comparison of microstructure and mechanical properties of ultra-narrow gap laser and gas-metal-arc welded S960 high strength steel

NASA Astrophysics Data System (ADS)

Guo, Wei; Li, Lin; Dong, Shiyun; Crowther, Dave; Thompson, Alan

2017-04-01

The microstructural characteristics and mechanical properties, including micro-hardness, tensile properties, three-point bending properties and Charpy impact toughness at different test temperatures of 8 mm thick S960 high strength steel plates were investigated following their joining by multi-pass ultra-narrow gap laser welding (NGLW) and gas metal arc welding (GMAW) techniques. It was found that the microstructure in the fusion zone (FZ) for the ultra-NGLW joint was predominantly martensite mixed with some tempered martensite, while the FZ for the GMAW joint was mainly consisted of ferrite with some martensite. The strength of the ultra-NGLW specimens was comparable to that of the base material (BM), with all welded specimens failed in the BM in the tensile tests. The tensile strength of the GMAW specimens was reduced approximately by 100 MPa when compared with the base material by a broad and soft heat affected zone (HAZ) with failure located in the soft HAZ. Both the ultra-NGLW and GMAW specimens performed well in three-point bending tests. The GMAW joints exhibited better impact toughness than the ultra-NGLW joints.

Principles of TRIP Steel Optimization for Passive Damping Applications

NASA Astrophysics Data System (ADS)

Fraley, George Jay

Globally many historic structures of cultural significance which do not have systems to mitigate seismic damage are located in areas with heavy seismic activity. Efforts have been undertaken to develop strategies to retrofit such structures, however any intervention must be limited in size for aesthetic reasons. To contribute to this effort, ArcelorMittal aims to create steel-based solutions for passive energy dissipation through plastic deformation during cyclic loading. High-strength TRansformation-Induced Plasticity (TRIP) steels are proposed as an excellent candidate material for this application, due to the extreme combination of high strength and large ductility they are well-known to exhibit. To evaluate high-strength TRIP steels for passive damping applications, isothermal, fully-reversed, displacement-controlled Ultra-Low Cycle Fatigue (ULCF) experiments (Nf < 100) were conducted on two tempering conditions of austenitic BlastAlloy (BA) TRIP 180. One tempering condition resulted in a Mssigma temperature of 27 °C and stress-assisted martensitic nucleation, and the other a Mssigma temperature of -8 °C and strain-induced martensitic nucleation at room temperature. The higher austenite stability condition (Ms sigma = -8 °C) was found to have approximately twice the fatigue life and a lower rate of cyclic hardening at fixed displacement amplitudes for low to intermediate levels of plastic strain range (2-10%) compared to the lower stability austenite condition (Mssigma = 27 °C). However, at higher levels of plastic straining (10-16% strain range) the fatigue lives and strain hardening behavior converged for the two stabilities, indicating a likely exhaustion of transformation during the first few cycles. ULCF life behavior for the high-stability austenite condition compared favorably with literature values for structural stainless steel 316, despite having a yield strength approximately four times larger. For a similar number of cycles to failure the high stability condition dissipated 2.4 times more energy than stainless steel 316 upon initial cycling. The stress-strain hysteresis curves and fatigue life data generated can be input into computational models of passive damping devices for initial concurrent material/device design iterations. Evidence of shear lips, large primary inclusions serving as fracture-initiation sites, and highly dimpled fracture surfaces confirmed for all failed specimens that ductile fracture mechanisms contribute to failure under ULCF conditions. For specimens failing in 10-11 cycles large protrusions aligned along the transverse direction were found, indicating that intergranular fracture may also be playing a role in ULCF failures for this alloy. To explore lower cost alternatives to fully-austenitic TRIP steels for passive-damping devices, austenite precipitation and its effect on uniaxial-tension mechanical properties in martensitic steels was investigated. Isothermal dilatometry measurements on martensitic BlastAlloy (BA) 160 confirmed that significant phase fractions of interlath austenite could be precipitated, which was previously not confirmed. A two-step tempering treatment of 650 °C for 2 hours followed by 500 °C for 4 hours resulting in an estimated austenite content of 11.0 +/- 2.1% by volume was found to yield highly unstable austenite with no significant increase in uniform ductility when compared to non-transforming conditions. Subsequent dilatometry investigations on a 10 wt% Ni plate steel demonstrated faster rate kinetics of austenite precipitation. Characterization of a single step temper of 640 °C for 30 minutes of this steel, with an estimated austenite content of 21.4 +/- 2.1% by volume, found a measureable Ms sigma temperature of 75 °C. Uniaxial tension tests above Mssigma showed a transition from stress-assisted to strain-induced nucleation, resulting in a significant increase in fracture ductility, however with no simultaneous increase in uniform ductility. Local Electrode Atom Probe tomography investigations found interlath austenite films to be enriched with roughly 18.2 at% Ni. Such compositional data along with measured austenite stabilities and precipitation rate kinetics can be used in future design iterations of martensitic steels. Given the confirmed relationship between ULCF life and ductility once a significant increase in uniform ductility for this class of steels is achieved ULCF studies can be performed to assess their appropriateness for passive damping applications.

Shape effect of ultrafine-grained structure on static fracture toughness in low-alloy steel

PubMed Central

Inoue, Tadanobu; Kimura, Yuuji; Ochiai, Shojiro

2012-01-01

A 0.4C-2Si-1Cr-1Mo steel with an ultrafine elongated grain (UFEG) structure and an ultrafine equiaxed grain (UFG) structure was fabricated by multipass caliber rolling at 773 K and subsequent annealing at 973 K. A static three-point bending test was conducted at ambient temperature and at 77 K. The strength–toughness balance of the developed steels was markedly better than that of conventionally quenched and tempered steel with a martensitic structure. In particular, the static fracture toughness of the UFEG steel, having a yield strength of 1.86 GPa at ambient temperature, was improved by more than 40 times compared with conventional steel having a yield strength of 1.51 GPa. Furthermore, even at 77 K, the fracture toughness of the UFEG steel was about eight times higher than that of the conventional and UFG steels, despite the high strength of the UFEG steel (2.26 GPa). The UFG steel exhibited brittle fracture behavior at 77 K, as did the conventional steel, and no dimple structure was observed on the fracture surface. Therefore, it is difficult to improve the low-temperature toughness of the UFG steel by grain refinement only. The shape of crystal grains plays an important role in delamination toughening, as do their refinement and orientation. PMID:27877493

Carbon Equivalence and Weldability of Microalloyed Steels

DTIC Science & Technology

1989-10-25

phase particles [191. The particles have been identified as retained austcnite or retained austenite- martensite . The copper precipitates ...the strengthening mc’hani;m;,, utilized in three of the four mechanisms described above do not utilize a low tcn perature phase transformation ... low carbon alloy st,-el and derives its strength from a tempered martensite structure. The set of low carbon steels include five Navy HSLA steels

Contributions of Cu-rich clusters, dislocation loops and nanovoids to the irradiation-induced hardening of Cu-bearing low-Ni reactor pressure vessel steels

NASA Astrophysics Data System (ADS)

Bergner, F.; Gillemot, F.; Hernández-Mayoral, M.; Serrano, M.; Török, G.; Ulbricht, A.; Altstadt, E.

2015-06-01

Dislocation loops, nanovoids and Cu-rich clusters (CRPs) are known to represent obstacles for dislocation glide in neutron-irradiated reactor pressure vessel (RPV) steels, but a consistent experimental determination of the respective obstacle strengths is still missing. A set of Cu-bearing low-Ni RPV steels and model alloys was characterized by means of SANS and TEM in order to specify mean size and number density of loops, nanovoids and CRPs. The obstacle strengths of these families were estimated by solving an over-determined set of linear equations. We have found that nanovoids are stronger than loops and loops are stronger than CRPs. Nevertheless, CRPs contribute most to irradiation hardening because of their high number density. Nanovoids were only observed for neutron fluences beyond typical end-of-life conditions of RPVs. The estimates of the obstacle strength are critically compared with reported literature data.

Friction Stir Spot Welding of Advanced High Strength Steels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hovanski, Yuri; Grant, Glenn J.; Santella, M. L.

Friction stir spot welding techniques were developed to successfully join several advanced high strength steels. Two distinct tool materials were evaluated to determine the effect of tool materials on the process parameters and joint properties. Welds were characterized primarily via lap shear, microhardness, and optical microscopy. Friction stir spot welds were compared to the resistance spot welds in similar strength alloys by using the AWS standard for resistance spot welding high strength steels. As further comparison, a primitive cost comparison between the two joining processes was developed, which included an evaluation of the future cost prospects of friction stir spotmore » welding in advanced high strength steels.« less

The influence of deformation-induced residual stresses on the post-forming tensile stress/strain behavior of dual-phase steels

NASA Astrophysics Data System (ADS)

Hance, Brandon Michael

It was hypothesized that, in dual-phase (DP) steels, strain partitioning between ferrite (alpha) and martensite (alpha') during deformation results in a distribution of post-deformation residual stresses that, in turn, affects the subsequent strength, work hardening behavior and formability when the strain path is changed. The post-forming deformation-induced residual stress state was expected to depend upon the microstructure, the amount of strain and the prestrain path. The primary objective of this research program was to understand the influence of deformation-induced residual stresses on the post-forming tensile stress/strain behavior of DP steels. Three commercially produced sheet steels were considered in this analysis: (1) a DP steel with approximately 15 vol. % martensite, (2) a conventional high-strength, low-alloy (HSLA) steel, and (3) a conventional, ultra-low-carbon interstitial-free (IF) steel. Samples of each steel were subjected to various prestrain levels in various plane-stress forming modes, including uniaxial tension, plane strain and balanced biaxial stretching. Neutron diffraction experiments confirmed the presence of large post-forming deformation-induced residual stresses in the ferrite phase of the DP steel. The deformation-alphainduced residual stress state varied systematically with the prestrain mode, where the principal residual stress components are proportional to the principal strain components of the prestrain mode, but opposite in sign. For the first time, and by direct experimental correlation, it was shown that deformation-induced residual stresses greatly affect the post-forming tensile stress/strain behavior of DP steels. As previously reported in the literature, the formability (residual tensile ductility) of the IF steel and the HSLA steel was adversely affected by strain path changes. The DP steel presents a formability advantage over the conventional IF and HSLA steels, and is expected to be particularly well suited for complex forming operations that involve abrupt strain path changes. Deformation-induced residual stresses were measured in the IF steel and the HSLA steel; however, the magnitudes of which are such that post-forming tensile stress/strain behavior was not significantly affected. Considering the vast differences in mechanical properties, microstructure, and composition, the IF steel and the HSLA steel showed remarkably similar post-forming tensile stress/strain behavior for all prestrain modes considered.

Design for Fe-high Mn alloy with an improved combination of strength and ductility.

PubMed

Lee, Seung-Joon; Han, Jeongho; Lee, Sukjin; Kang, Seok-Hyeon; Lee, Sang-Min; Lee, Young-Kook

2017-06-15

Recently, Fe-Mn twinning-induced plasticity steels with an austenite phase have been the course of great interest due to their excellent combination of tensile strength and ductility, which carbon steels have never been able to attain. Nevertheless, twinning-induced plasticity steels also exhibit a trade-off between strength and ductility, a longstanding dilemma for physical metallurgists, when fabricated based on the two alloy design parameters of stacking fault energy and grain size. Therefore, we investigated the tensile properties of three Fe-Mn austenitic steels with similar stacking fault energy and grain size, but different carbon concentrations. Surprisingly, when carbon concentration increased, both strength and ductility significantly improved. This indicates that the addition of carbon resulted in a proportionality between strength and ductility, instead of a trade-off between those characteristics. This new design parameter, C concentration, should be considered as a design parameter to endow Fe-Mn twinning-induced plasticity steel with a better combination of strength and ductility.

The strain-rate sensitivity of high-strength high-toughness steels.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dilmore, M.F.; Crenshaw, Thomas B.; Boyce, Brad Lee

2006-01-01

The present study examines the strain-rate sensitivity of four high strength, high-toughness alloys at strain rates ranging from 0.0002 s-1 to 200 s-1: Aermet 100, a modified 4340, modified HP9-4-20, and a recently developed Eglin AFB steel alloy, ES-1c. A refined dynamic servohydraulic method was used to perform tensile tests over this entire range. Each of these alloys exhibit only modest strain-rate sensitivity. Specifically, the strain-rate sensitivity exponent m, is found to be in the range of 0.004-0.007 depending on the alloy. This corresponds to a {approx}10% increase in the yield strength over the 7-orders of magnitude change in strain-rate.more » Interestingly, while three of the alloys showed a concominant {approx}3-10% drop in their ductility with increasing strain-rate, the ES1-c alloy actually exhibited a 25% increase in ductility with increasing strain-rate. Fractography suggests the possibility that at higher strain-rates ES-1c evolves towards a more ductile dimple fracture mode associated with microvoid coalescence.« less

New-type steel plate with ultra high crack-arrestability

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ishikawa, T.; Nomiyama, Y.; Hagiwara, Y.

1995-12-31

A new-type steel plate has been developed by controlling the microstructure of the surface layers. The surface layer consists of ultra fine grain ferrite microstructure, which provides excellent fracture toughness even at cryogenic temperature. When an unstable brittle crack propagates in the developed steel plate, shear-lips can be easily formed due to the surface layers with ultra fine grain microstructure. Since unstable running crack behavior is strongly affected by side-ligaments (shear-lips), which are associated with extensive plastic deformation, enhanced formation of the shear-lips can improve crack arrestability. This paper describes the developed steel plates of HT500MPa tensile strength class formore » shipbuilding use. Fracture mechanics investigations using large-scale fracture testings (including ultrawide duplex ESSO tests) clarified that the developed steel plates have ultra high crack-arrestability. It was also confirmed that the plates possess sufficient properties, including weldability and workability, for ship building use.« less

The effect of microstructure and strength on the fracture toughness of an 18 ni, 300 grade maraging steel

NASA Technical Reports Server (NTRS)

Psioda, J. A.; Low, J. R., Jr.

1974-01-01

Methods for increasing the strength of maraging steels are discussed. An investigation was conducted to systematically vary the strength of 18 weight percent nickel, 300 grade maraging steel, to isolate any attending microstructural changes, and to study the effects of these changes on the fracture toughness of the alloy. A study aimed at determining the aging behavior of the program alloy was carried out to provide data by which to estimate yield strength. The effects of various alloying materials on the strength of the maraging steel are examined. The mechanical properties of the 300 grade maraging steel were determined by tension tests, fatigue precracked Charpy impact tests, and plane strain fracture toughness tests.

Experience of high-nitrogenous steel powder application in repairs and surface hardening of responsible parts for power equipment by plasma spraying

NASA Astrophysics Data System (ADS)

Kolpakov, A. S.; Kardonina, N. I.

2016-02-01

The questions of the application of novel diffusion-alloying high-nitrogenous steel powders for repair and surface hardening of responsible parts of power equipment by plasma spraying are considered. The appropriateness of the method for operative repair of equipment and increasing its service life is justified. General data on the structure, properties, and manufacture of nitrogen-, aluminum-, and chromium-containing steel powders that are economically alloyed using diffusion are described. It is noted that the nitrogen release during the decomposition of iron nitrides, when heating, protects the powder particles from oxidation in the plasma jet. It is shown that the coating retains 50% of nitrogen that is contained in the powder. Plasma spraying modes for diffusion-alloying high-nitrogenous steel powders are given. The service properties of plasma coatings based on these powders are analyzed. It is shown that the high-nitrogenous steel powders to a nitrogen content of 8.9 wt % provide the necessary wear resistance and hardness of the coating and the strength of its adhesion to the substrate and corrosion resistance to typical aggressive media. It is noted that increasing the coating porosity promotes stress relaxation and increases its thickness being limited with respect to delamination conditions in comparison with dense coatings on retention of the low defectiveness of the interface and high adhesion to the substrate. The examples of the application of high-nitrogenous steel powders in power engineering during equipment repairs by service companies and overhaul subdivisions of heat power plants are given. It is noted that the plasma spraying of diffusion-alloyed high-nitrogenous steel powders is a unique opportunity to restore nitrided steel products.

Spectral emissivity of candidate alloys for very high temperature reactors in high temperature air environment

NASA Astrophysics Data System (ADS)

Cao, G.; Weber, S. J.; Martin, S. O.; Sridharan, K.; Anderson, M. H.; Allen, T. R.

2013-10-01

Emissivity measurements for candidate alloys for very high temperature reactors were carried out in a custom-built experimental facility, capable of both efficient and reliable measurements of spectral emissivities of multiple samples at high temperatures. The alloys studied include 304 and 316 austenitic stainless steels, Alloy 617, and SA508 ferritic steel. The oxidation of alloys plays an important role in dictating emissivity values. The higher chromium content of 304 and 316 austenitic stainless steels, and Alloy 617 results in an oxide layer only of sub-micron thickness even at 700 °C and consequently the emissivity of these alloys remains low. In contrast, the low alloy SA508 ferritic steel which contains no chromium develops a thicker oxide layer, and consequently exhibits higher emissivity values.

Effect of Heat-Affected Zone on Spot Weldability in Automotive Ultra High Strength Steel Sheet

NASA Astrophysics Data System (ADS)

Nagasaka, Akihiko; Naito, Junya; Chinzei, Shota; Hojo, Tomohiko; Horiguchi, Katsumi; Shimizu, Yuki; Furusawa, Takuro; Kitahara, Yu

Effect of heat-affected zone (HAZ) on spot weldability in automotive hot stamping (HS) steel sheet was investigated for automotive applications. Tensile test was performed on a tensile testing machine at a crosshead speed of 3 mm/min, using spot welded test specimen (Parallel length: 60 mm, Width: 20 mm, Thickness: 1.4 mm, Tab: 20×20 mm). The spot welding test was carried out using spot welded test specimen with welding current (I) of 6.3 kA to 9.5 kA. Hardness was measured with the dynamic ultra micro Vickers hardness tester. In HS steel, has very high strength of 1 500 MPa, tensile strength (TS) and total elongation (TEl) of the spot welded test specimen of HS steel were lower than those of base metal test specimen. The spot welded test specimen broke in the weld. The Vickers hardnesses (HVs) of base metal and fusion zone of hot stamping steel were around HV500. In addition, the hardness of HAZ was under HV300. The difference of hardness between fusion zone and HAZ was around HV200. The hardness distribution acted as a notch. On the other hand, in dual phase (DP) steel, has low strength of 590 MPa, the TS of spot welded test specimen of DP steel was the same as the base metal test specimen because of the breaking of base metal. The TEl of the spot welded test specimen of DP steel was smaller than that of base metal test specimen. In the spot welded test specimen of DP steel, the hardness of base metal was around HV200 and the fusion zone was around HV500. The hardness distribution did not act as a notch. The difference in hardness between base metal and HAZ acted on a crack initiation at HAZ softening.

Stress-Corrosion Cracking in High Strength Steels and in Titanium and Aluminum Alloys

DTIC Science & Technology

1972-01-01

EFFECTS 01: STRESS) 155 Table 2. Mechanical, Fracture, and Stress Corrosion Properties for Plates of Several Aluminum Alloys --Continued 4f’l14...One of the most effective SCC preventives for high strength aluminum alloys is surface working by shot peening, particularl) when used in combination...Aluminaut uses aluminum alloy anodes to supplement the protection of the pressure hull offered by several layers of polyurethane coating 175). 100 A

Characterization of the behavior under impact loading of a maraging steel strengthened by nano-precipitates

NASA Astrophysics Data System (ADS)

Lach, E.; Redjaïmia, A.; Leitner, H.; Clemens, H.

2006-08-01

Nanometer-sized precipitates are responsible for the high strength of steel alloys well known as maraging steels. The term maraging relates to aging reactions in very low-carbon martensitic steels. Due to precipitation hardening 0.2% yield stress values of up to 2.4 GPa can be achieved. The class of stainless maraging steels exhibits an excellent combination of very high strength and hardness, ductility and toughness, combined with good corrosion resistance. In many applications like crash worthiness or ballistic protection the materials are loaded at high strain-rates. The most important characteristic of material behavior under dynamic load is the dynamic yield stress. In this work compression tests had been conducted at strain-rates in the order of 5 x 10 - 3 s - 1 up to 3 x 103 s - 1 to study the materials behaviour. Additionally high dynamic compression tests had been performed in the temperature range from -40circC up to 300circC.

Partial-Isothermally-Treated Low Alloy Ultrahigh Strength Steel with Martensitic/Bainitic Microstructure

NASA Astrophysics Data System (ADS)

Luo, Quanshun; Kitchen, Matthew; Patel, Vinay; Filleul, Martin; Owens, Dave

We introduce a new strengthening heat treatment of a Ni-Cr-Mo-V alloyed spring steel by partial isothermal salt-bath and subsequent air-cooling and tempering. Detailed isothermal treatments were made at temperatures below or above the Ms point (230°C). The salt bath time was controlled between 10 and 80 minutes. Through the new treatment, the candidate steel developed ultrahigh tensile strength 2,100 MPa, yield strength 1,800 MPa, elongation 8-10 %, hardness 580-710 HV, and V-notch Charpy toughness 10-12 J. Optical and electron microscopic observations and X-ray diffraction revealed multi-phase microstructures of bainitic/martensitic ferrites, fine carbide precipitates and retained austenite. Carbon partitioning during the bainitic/martensitic transformation was investigated for its remarkable influence on the strengthening mechanism.

Microstructure design of low alloy transformation-induced plasticity assisted steels

NASA Astrophysics Data System (ADS)

Zhu, Ruixian

The microstructure of low alloy Transformation Induced Plasticity (TRIP) assisted steels has been systematically varied through the combination of computational and experimental methodologies in order to enhance the mechanical performance and to fulfill the requirement of the next generation Advanced High Strength Steels (AHSS). The roles of microstructural parameters, such as phase constitutions, phase stability, and volume fractions on the strength-ductility combination have been revealed. Two model alloy compositions (i.e. Fe-1.5Mn-1.5Si-0.3C, and Fe-3Mn-1Si-0.3C in wt%, nominal composition) were studied. Multiphase microstructures including ferrite, bainite, retained austenite and martensite were obtained through conventional two step heat treatment (i.e. intercritical annealing-IA, and bainitic isothermal transformation-BIT). The effect of phase constitution on the mechanical properties was first characterized experimentally via systematically varying the volume fractions of these phases through computational thermodynamics. It was found that martensite was the main phase to deteriorate ductility, meanwhile the C/VA ratio (i.e. carbon content over the volume fraction of austenite) could be another indicator for the ductility of the multiphase microstructure. Following the microstructural characterization of the multiphase alloys, two microstructural design criteria (i.e. maximizing ferrite and austenite, suppressing athermal martensite) were proposed in order to optimize the corresponding mechanical performance. The volume fraction of ferrite was maximized during the IA with the help of computational thermodyanmics. On the other hand, it turned out theoretically that the martensite suppression could not be avoided on the low Mn contained alloy (i.e. Fe- 1.5Mn-1.5Si-0.3C). Nevertheless, the achieved combination of strength (~1300MPa true strength) and ductility (˜23% uniform elongation) on the low Mn alloy following the proposed design criteria fulfilled the requirement of the next generation AHSS. To further optimize the microstructure such that the designed criteria can be fully satisfied, further efforts have been made on two aspects: heat treatment and alloy addition. A multi-step BIT treatment was designed and successfully reduced the martensite content on the Fe-1.5Mn-1.5Si-0.3C alloy. Microstructure analysis showed a significant reduction on the volume fraction of martensite after the multi-step BIT as compared to the single BIT step. It was also found that, a slow cooling rate between the two BIT treatments resulted in a better combination of strength and ductility than rapid cooling or conventional one step BIT. Moreover, the athermal martensite formation can be fully suppressed by increasing the Mn content (Fe-3Mn-1Si-0.3C) and through carefully designed heat treatments. The athermal martensite-free alloy provided consistently better ductility than the martensite containing alloy. Finally, a microstructure based semi-empirical constitutive model has been developed to predict the monotonic tensile behavior of the multiphase TRIP assisted steels. The stress rule of mixture and isowork assumption for individual phases was presumed. Mecking-Kocks model was utilized to simulate the flow behavior of ferrite, bainitic ferrite and untransformed retained austenite. The kinetics of strain induced martensitic transformation was modeled following the Olson-Cohen method. The developed model has results in good agreements with the experimental results for both TRIP steels studied with same model parameters.

Repair of steel beam/girder ends with ultra high-strength concrete - phase II.

DOT National Transportation Integrated Search

2016-01-01

A novel repair method has been developed at the University of Connecticut for corroded steel bridge girder : ends. The repair method consists of encasing the corroded steel area with UHPC. The UHPC panel is bonded : to the steel girder using headed s...

Metallurgical and mechanical properties of laser welded high strength low alloy steel

PubMed Central

Oyyaravelu, Ramachandran; Kuppan, Palaniyandi; Arivazhagan, Natarajan

2016-01-01

The study aimed at investigating the microstructure and mechanical properties of Neodymium-Doped Yttrium Aluminum Garnet (Nd:YAG) laser welded high strength low alloy (HSLA) SA516 grade 70 boiler steel. The weld joint for a 4 mm thick plate was successfully produced using minimum laser power of 2 kW by employing a single pass without any weld preheat treatment. The micrographs revealed the presence of martensite phase in the weld fusion zone which could be due to faster cooling rate of the laser weldment. A good correlation was found between the microstructural features of the weld joints and their mechanical properties. The highest hardness was found to be in the fusion zone of cap region due to formation of martensite and also enrichment of carbon. The hardness results also showed a narrow soft zone at the heat affected zone (HAZ) adjacent to the weld interface, which has no effect on the weld tensile strength. The yield strength and ultimate tensile strength of the welded joints were 338 MPa and 549 MPa, respectively, which were higher than the candidate metal. These tensile results suggested that the laser welding process had improved the weld strength even without any weld preheat treatment and also the fractography of the tensile fractured samples showed the ductile mode of failure. PMID:27222751

Irradiation-assisted stress corrosion cracking of model austenitic stainless steel.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chung, H. M.; Ruther, W. E.; Strain, R. V.

1999-10-26

Slow-strain-rate tensile (SSRT) tests were conducted on model austenitic stainless steel (SS) alloys that were irradiated at 289 C in He. After irradiation to {approx}0.3 x 10{sup 21} n {center_dot} cm{sup 2} and {approx} 0.9 x 10{sup 21} n {center_dot} cm{sup -2} (E > 1 MeV), significant heat-to-heat variations in the degree of intergranular and transgranular stress corrosion cracking (IGSCC and TGSCC) were observed. At {approx}0.3 x 10{sup 21} n {center_dot} cm{sup -2}, a high-purity heat of Type 316L SS that contains a very low concentration of Si exhibited the highest susceptibility to IGSCC. In unirradiated state, Types 304 andmore » 304L SS did not exhibit a systematic effect of Si content on alloy strength. However, at {approx}0.3 x 10{sup 21} n {center_dot} cm{sup -2}, yield and maximum strengths decreased significantly as Si content was increased to >0.9 wt.%. Among alloys that contain low concentrations of C and N, ductility and resistance to TGSCC and IGSCC were significantly greater for alloys with >0.9 wt.% Si than for alloys with <0.47 wt.% Si. Initial data at {approx}0.9 x 10{sup 21} n {center_dot} cm{sup -2} were also consistent with the beneficial effect of high Si content. This indicates that to delay onset of and reduce susceptibility to irradiation-assisted stress corrosion cracking (IASCC), at least at low fluence levels, it is helpful to ensure a certain minimum concentration of Si. High concentrations of Cr were also beneficial; alloys that contain <15.5 wt.% Cr exhibited greater susceptibility to IASCC than alloys with {approx}18 wt.% Cr, whereas an alloy that contains >21 wt.% Cr exhibited less susceptibility than the lower-Cr alloys under similar conditions.« less

Molybdenum-A Key Component of Metal Alloys

USGS Publications Warehouse

Kropschot, S.J.

2010-01-01

Molybdenum, whose chemical symbol is Mo, was first recognized as an element in 1778. Until that time, the mineral molybdenite-the most important source of molybdenum-was believed to be a lead mineral because of its metallic gray color, greasy feel, and softness. In the late 19th century, French metallurgists discovered that molybdenum, when alloyed (mixed) with steel in small quantities, creates a substance that is remarkably tougher than steel alone and is highly resistant to heat. The alloy was found to be ideal for making tools and armor plate. Today, the most common use of molybdenum is as an alloying agent in stainless steel, alloy steels, and superalloys to enhance hardness, strength, and resistance to corrosion.

Effect of Copper and Silicon on Al-5%Zn Alloy as a Candidate Low Voltage Sacrificial Anode

NASA Astrophysics Data System (ADS)

Pratesa, Yudha; Ferdian, Deni; Togina, Inez

2017-05-01

One common method used for corrosion protection is a sacrificial anode. Sacrificial anodes that usually employed in the marine environment are an aluminum alloy sacrificial anode, especially Al-Zn-In. However, the electronegativity of these alloys can cause corrosion overprotection and stress cracking (SCC) on a high-strength steel. Therefore, there is a development of the sacrificial anode aluminum low voltage to reduce the risk of overprotection. The addition of alloying elements such as Cu, Si, and Ge will minimize the possibility of overprotection. This study was conducted to analyze the effect of silicon and copper addition in Al-5Zn. The experiment started from casting the sacrificial anode aluminum uses electrical resistance furnace in a graphite crucible in 800°C. The results alloy was analyzed using Optical emission spectroscopy (OES), Differential scanning calorimetry, electrochemical impedance spectroscopy, and metallography. Aluminum alloy with the addition of a copper alloy is the most suitable and efficient to serve as a low-voltage sacrificial anode aluminum. Charge transfer resistivity of copper is smaller than silicon which indicates that the charge transfer between the metal and the electrolyte is easier t to occur. Also, the current potential values in coupling with steel are also in the criteria range of low-voltage aluminum sacrificial anodes.

Effect of alloying elements and coiling temperature on the recrystallization behavior and the bainitic transformation in TRIP steels

NASA Astrophysics Data System (ADS)

Han, Seongho; Seong, Hwangoo; Ahn, Yeonsang; Garcia, C. I.; DeArdo, A. J.; Kim, Inbae

2009-08-01

The effects of alloying elements and coiling temperature on recrystallization behavior and bainitic transformation were investigated based on 0.07C-Mn-Cr-Nb steel with a low carbon equivalent. Based on the ferrite recrystallization behavior, the proper intercritical annealing temperature of all studied steels was suggested to produce TRIP steel with good strength and elongation balance. All steels coiled at 550 °C showed much faster ferrite recrystallization behavior than steels coiled at 700 °C. In addition to the coiling temperature, the effect of increasing carbon content on the ferrite recrystallization was minor at a coiling temperature of 550 °C, but much more prominent at a coiling temperature of 700 °C. The highest Mo added steel showed the best strength and elongation balance, and the highest carbon and Mo added steel showed the highest tensile strength at a coiling temperature of 550 °C. The steel containing a higher amount of elemental Al (0.7 wt.% Al) exhibited much better elongation than the lower Al added steel (0.04 wt.% Al) in TS 780 MPa grade, about 24 % and 19 %, respectively.

Microstructure control for high strength 9Cr ferritic-martensitic steels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tan, Lizhen; Hoelzer, David T; Busby, Jeremy T

2012-01-01

Ferritic-martensitic (F-M) steels with 9 wt.%Cr are important structural materials for use in advanced nuclear reactors. Alloying composition adjustment, guided by computational thermodynamics, and thermomechanical treatment (TMT) were employed to develop high strength 9Cr F-M steels. Samples of four heats with controlled compositions were subjected to normalization and tempering (N&T) and TMT, respectively. Their mechanical properties were assessed by Vickers hardness and tensile testing. Ta-alloying showed significant strengthening effect. The TMT samples showed strength superior to the N&T samples with similar ductility. All the samples showed greater strength than NF616, which was either comparable to or greater than the literaturemore » data of the PM2000 oxide-dispersion-strengthened (ODS) steel at temperatures up to 650 C without noticeable reduction in ductility. A variety of microstructural analyses together with computational thermodynamics provided rational interpretations on the strength enhancement. Creep tests are being initiated because the increased yield strength of the TMT samples is not able to deduce their long-term creep behavior.« less

Characterization of Mechanical Properties and Residual Stress in API 5L X80 Steel Welded Joints

NASA Astrophysics Data System (ADS)

de Sousa Lins, Amilton; de Souza, Luís Felipe Guimarães; Fonseca, Maria Cindra

2018-01-01

The use of high-strength and low-alloy steels, high design factors and increasingly stringent safety requirements have increased the operating pressure levels and, consequently, the need for further studies to avoid and prevent premature pipe failure. To evaluate the possibility of improving productivity in manual arc welding of this type of steel, this work characterizes the mechanical properties and residual stresses in API 5L X80 steel welded joints using the SMAW and FCAW processes. The residual stresses were analyzed using x-ray diffraction with the sin2 ψ method at the top and root of the welded joints in the longitudinal and transverse directions of the weld bead. The mechanical properties of the welded joints by both processes were characterized in terms of tensile strength, impact toughness and Vickers microhardness in the welded and shot peening conditions. A predominantly compressive residual stress was found, and shot peening increased the tensile strength and impact toughness in both welded joints.

Effect of nitrogen on iron-manganese-based shape memory alloys

NASA Astrophysics Data System (ADS)

Ariapour, Azita

Shape memory effect is due to a reversible martensitic transformation. The major drawback in case of Fe-Mn-based shape memory alloys is their inferior shape memory effect compared to Ni-Ti and Cu-based shape memory alloys and their low strength and corrosion resistance compared to steel alloys. It is known that by increasing the alloy strength the shape memory effect can be improved. Nitrogen in solid solution can increase the strength of steels to a greater extent than other major alloying elements. However, its effect on shape memory effect of Fe-Mn-based alloys is ambiguous. In this work first we investigated the effect of nitrogen addition in solid solution on both shape memory effect (SME) and strength of a Fe-Mn-Cr-Ni-Si shape memory alloy (SMA). It was found that interstitial nitrogen suppressed the shape memory effect in these alloys. As an example addition of 0.24 wt % nitrogen in solid solution to the alloy system suppressed the SME by ˜80% and increased the strength by 20%. A reduction of martensitic phase formation was found to be the dominant factor in suppression of the SME. This was related, experimentally and theoretically to stacking fault energy of the alloy as well as the driving force and friction force during the transformation. The second approach was doping the alloy with both 0.36 wt% of nitrogen and 0.36 wt% of niobium. Niobium has great affinity for nitrogen and thus NbN dispersed particles can be produced in the alloy following hot rolling. Then particles prevent growth of the alloy and increase the strength of the alloy due to reduced grain size, and precipitation hardening. The improvement of SME in this alloy compared to the interstitial containing alloys was due to the large removal of the nitrogen from solid solution. In case of all the alloys studied in this work, the presence of nitrogen in solid solution improved the corrosion resistance of the alloy. This suggests that nitrogen can replace nickel in the alloy. One of the proposed applications for high strength Fe-Mn-based alloys is as tendon rods in prestressed concrete. The advantage of M alloys in this application is the possibility of producing curved structural prestressed concrete.

Processing of Advanced Cast Alloys for A-USC Steam Turbine Applications

NASA Astrophysics Data System (ADS)

Jablonski, Paul D.; Hawk, Jeffery A.; Cowen, Christopher J.; Maziasz, Philip J.

2012-02-01

The high-temperature components within conventional supercritical coal-fired power plants are manufactured from ferritic/martensitic steels. To reduce greenhouse-gas emissions, the efficiency of pulverized coal steam power plants must be increased to as high a temperature and pressure as feasible. The proposed steam temperature in the DOE/NETL Advanced Ultra Supercritical power plant is high enough (760°C) that ferritic/martensitic steels will not work for the majority of high-temperature components in the turbine or for pipes and tubes in the boiler due to temperature limitations of this class of materials. Thus, Ni-based superalloys are being considered for many of these components. Off-the-shelf forged nickel alloys have shown good promise at these temperatures, but further improvements can be made through experimentation within the nominal chemistry range as well as through thermomechanical processing and subsequent heat treatment. However, cast nickel-based superalloys, which possess high strength, creep resistance, and weldability, are typically not available, particularly those with good ductility and toughness that are weldable in thick sections. To address those issues related to thick casting for turbine casings, for example, cast analogs of selected wrought nickel-based superalloys such as alloy 263, Haynes 282, and Nimonic 105 have been produced. Alloy design criteria, melt processing experiences, and heat treatment are discussed with respect to the as-processed and heat-treated microstructures and selected mechanical properties. The discussion concludes with the prospects for full-scale development of a thick section casting for a steam turbine valve chest or rotor casing.

Low temperature mechanical properties, fractographic and metallographic evaluation of several alloy steels

NASA Technical Reports Server (NTRS)

Montano, J. W.

1973-01-01

The mechanical properties are presented of alloy steels, 4130, 4140, 4340, 6150, and 8740. Test specimens were manufactured from approximately 1.00 inch (2.54 cm) diameter bar stock which had been heat treated to two different hardness levels. The following mechanical tests were performed at temperatures of 80 F (+26.7 C), 0 F (-17.8 C), -100 F (-73 C), and -200 F (-129 C): (1) tensile test (Ultimate, yield, modulus, elongation, and reduction of area), (2) notched tensile test, (3) charpy V-notched impact test (impact energy), and (4) double shear strength test (ultimate and yield). The test data indicate excellent tensile strength, notched/unnotched tensile ratios, ductility, impact, and shear properties at all test temperatures, except at -200 F (-129 C) where the impact strength of the higher strength group of alloy steels, 4130 (Rc-37) and 4140 (Rc-44) decreased to approximately 9 ft. lbs. (12 joules) and 6 ft. lbs. (8 joules), respectively. Chemical, metallographic, and fractographic analyses were also performed to evaluate microstructure, microhardness and the effect of decrease in temperature on the ductile to brittle failure transition.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tan, Xiao-Dong; Xu, Yun-Bo, E-mail: yunbo_xu@126.com; Yang, Xiao-Long

Microstructures composed of lath martensite and retained austenite with volume fraction between 8.0 vol.% and 12.0 vol.% were obtained in a low-C low-Si Al-free steel through hot-rolling direct quenching and dynamical partitioning (HDQ&DP) processes. The austenite stabilization mechanism in the low-C low-Si Al-free steel under the special dynamical partitioning processes is investigated by analyzing the carbon partition behavior from martensite to austenite and the carbide precipitation-coarsening behavior in martensite laths combining with the possible hot rolling deformation inheritance. Results show that the satisfying retained austenite amount in currently studied low-Si Al-free HDQ&DP steel is caused by the high-efficiency carbon enrichmentmore » in the 30–80 nm thick regions of austenite near the interfaces in the hot-rolled ultra-fast cooled structure and the avoidance of serious carbides coarsening during the continuous cooling procedures. The excellent strength-elongation product reaching up to 26,000 MPa% shows that the involved HDQ&DP process is a promising method to develop a new generation of advanced high strength steel. - Highlights: • HDQ&DP processes were applied to a low-C low-Si Al-free steel. • Effective partitioning time during the continuous cooling processes is 1–220 s. • Retained austenite with volume fraction between 8.0 vol. % and 12.0 vol. % has been obtained. • The special austenite stabilization mechanism has been expounded.« less

Development of Press Hardening Steel with High Resistance to Hydrogen Embrittlement

NASA Astrophysics Data System (ADS)

Bian, Jian; Mohrbacher, Hardy; Lu, Hongzhou; Wang, Wenjun

Press hardening has become the state-of-art technology in the car body manufacturing to enhance safety standard and to reduce CO2 emission of new vehicles. However the delayed cracking due to hydrogen embrittlement remains to be a critical issue. Generally press hardening steel is susceptible to hydrogen embrittlement due to ultra-high strength and martensitic microstructure. The hydrogen charging tests clearly demonstrate that only a few ppm of diffusible hydrogen is sufficient to cause such embrittlement. Currently the hydrogen embrittlement cannot be detected in the press hardened components and the embitteled components could collapse in the crash situation with fatal consequences arisen through dramatic loss in both strength and ductility. This paper introduces a new metallurgical solution to increase the resistance to hydrogen embrittlement of conventional press hardening steel based on 22MnB5 by Nb microalloying. In the hydrogen embrittlement and permeation tests the impact of Nb microalloying on the hydrogen embrittlement behavior was investigated under different hydrogen charging conditions and constant load. The test results revealed that Nb addition increases the resistance to hydrogen embrittlement due to reduced hydrogen diffusivity. The focus of this paper is to investigate the precipitation behavior of microalloying elements by using TEM and STEM and to find out the mechanisms leading to higher performance against hydrogen embrittlement of Nb alloyed steels.

Ultra-High Efficiency / Low Hydrogen Embrittlement Nanostructured Zn-Based Electrodeposits as Environmentally Benign Cd-Replacement Coatings for High Strength Steel Fasteners

DTIC Science & Technology

2011-04-01

forma The prese corrosion coating) w conversio converted not develo before and a : Example un ted Zn-Ni ac : Example s Zn-Ni alkalin nt of scribing...Protection Agency, 1998. Retrieved from web July 30th 2009. Available online at www.epa.gov/ iris /subst/0141.htm. 3 M. Bielawski, Surface and

Effect of microstructure on static and dynamic mechanical properties of high strength steels

NASA Astrophysics Data System (ADS)

Qu, Jinbo

The high speed deformation behavior of a commercially available dual phase (DP) steel was studied by means of split Hopkinson bar apparatus in shear punch (25m/s) and tension (1000s-1) modes with an emphasis on the influence of microstructure. The cold rolled sheet material was subjected to a variety of heat treatment conditions to produce several different microstructures, namely ferrite plus pearlite, ferrite plus bainite and/or acicular ferrite, ferrite plus bainite and martensite, and ferrite plus different fractions of martensite. Static properties (0.01mm/s for shear punch and 0.001s -1 for tension) of all the microstructures were also measured by an MTS hydraulic machine and compared to the dynamic properties. The effects of low temperature tempering and bake hardening were investigated for some ferrite plus martensite microstructures. In addition, two other materials, composition designed as high strength low alloy (HSLA) steel and transformation induced plasticity (TRIP) steel, were heat treated and tested to study the effect of alloy chemistry on the microstructure and property relationship. A strong effect of microstructure on both static and dynamic properties and on the relationship between static and dynamic properties was observed. According to the variation of dynamic factor with static strength, three groups of microstructures with three distinct behaviors were identified, i.e. classic dual phase (ferrite plus less than 50% martensite), martensite-matrix dual phase (ferrite plus more than 50% martensite), and non-dual phase (ferrite plus non-martensite). Under the same static strength level, the dual phase microstructure was found to absorb more dynamic energy than other microstructures. It was also observed that the general dependence of microstructure on static and dynamic property relationship was not strongly influenced by chemical composition, except the ferrite plus martensite microstructures generated by the TRIP chemistry, which exhibited much better dynamic factor values. This may suggest that solid solution strengthening should be more utilized in the design of crashworthy dual phase steels.

Development of new ferritic steels as cladding material for metallic fuel fast breeder reactor

NASA Astrophysics Data System (ADS)

Tokiwai, Moriyasu; Horie, Masaaki; Kako, Kenji; Fujiwara, Masayuki

1993-09-01

The excellent thermal, chemical and neutronic properties of metallic fuel (U-Pu-Zr alloy) will lead to drastic improvements in fast reactor safety and the related fuel cycle economy. Some new high molybdenum 12Cr ferritic stainless steel candidate cladding alloys have been designed to achieve the mechanical properties required for high performance metallic fuel elements. These candidate claddings were irradiated by ion bombardment and tested to determine their strength and creep rupture properties. A 12Cr-8Mo and a 12Cr-8Mo-0.1Y 2O 3 steel were fabricated into cladding via a powder metallurgy process and by a mechanical alloying process, respectively. These claddings had two and three times the creep rupture strength (pressurized at 650°C for 10000 h) of a conventional 12Cr ferritic steel (HT-9). These two steels also showed no void formation up to 350 dpa by Ni 3+ irradiation. A zircaloy-2 lined steel cladding tube has also been fabricated for the purpose of reducing fuel-cladding interdiffusion and chemical interaction.

Cr-W-V bainitic/ferritic steel with improved strength and toughness and method of making

DOEpatents

Klueh, R.L.; Maziasz, P.J.

1994-03-08

This work describes a high strength, high toughness bainitic/ferritic steel alloy comprising about 2.75% to 4.0% chromium, about 2.0% to 3.5% tungsten, about 0.10% to 0.30% vanadium, and about 0.1% to 0.15% carbon with the balance iron, wherein the percentages are by total weight of the composition, wherein the alloy having been heated to an austenitizing temperature and then cooled at a rate sufficient to produce carbide-free acicular bainite. 15 figures.

Hydrogen adsorption and diffusion, and subcritical-crack growth in high-strength steels and nickel base alloys

NASA Technical Reports Server (NTRS)

Wei, R. P.; Klier, K.; Simmons, G. W.

1974-01-01

Coordinated studies of the kinetics of crack growth and of hydrogen adsorption and diffusion were initiated to develop information that is needed for a clearer determination of the rate controlling process and possible mechanism for hydrogen enhanced crack growth, and for estimating behavior over a range of temperatures and pressures. Inconel 718 alloy and 18Ni(200) maraging steel were selected for these studies. 18Ni(250) maraging steel, 316 stainless steel, and iron single crystal of (111) orientation were also included in the chemistry studies. Crack growth data on 18Ni(250) maraging steel from another program are included for comparison. No sustained-load crack growth was observed for the Inconel 718 alloy in gaseous hydrogen. Gaseous hydrogen assisted crack growth in the 18Ni maraging steels were characterized by K-independent (Stage 2) extension over a wide range of hydrogen pressures (86 to 2000 torr or 12 kN/m2 to 266 kN/m2) and test temperatures (-60 C to +100 C). The higher strength 18Ni(250) maraging steel was more susceptible than the lower strength 200 grade. A transition temperature was observed, above which crack growth rates became diminishingly small.

Simulated Single Tooth Bending of High Temperature Alloys

NASA Technical Reports Server (NTRS)

Handschuh, Robert, F.; Burke, Christopher

2012-01-01

Future unmanned space missions will require mechanisms to operate at extreme conditions in order to be successful. In some of these mechanisms, very high gear reductions will be needed to permit very small motors to drive other components at low rotational speed with high output torque. Therefore gearing components are required that can meet the mission requirements. In mechanisms such as this, bending fatigue strength capacity of the gears is very important. The bending fatigue capacity of a high temperature, nickel-based alloy, typically used for turbine disks in gas turbine engines and two tool steel materials with high vanadium content, were compared to that of a typical aerospace alloy-AISI 9310. Test specimens were fabricated by electro-discharge machining without post machining processing. Tests were run at 24 and at 490 C. As test temperature increased from 24 to 490 C the bending fatigue strength was reduced by a factor of five.

Hydrogen adsorption and diffusion, and subcritical-crack growth in high strength steels and nickel base alloys

NASA Technical Reports Server (NTRS)

Wei, R. P.; Klier, K.; Simmons, G. W.; Chornet, E.

1973-01-01

Embrittlement, or the enhancement of crack growth by gaseous hydrogen in high strength alloys, is of primary interest in selecting alloys for various components in the space shuttle. Embrittlement is known to occur at hydrogen gas pressures ranging from fractions to several hundred atmospheres, and is most severe in the case of martensitic high strength steels. Kinetic information on subcritical crack growth in gaseous hydrogen is sparse at this time. Corroborative information on hydrogen adsorption and diffusion is inadequate to permit a clear determination of the rate controlling process and possible mechanism in hydrogen enhanced crack growth, and for estimating behavior over a range of temperatures and pressures. Therefore, coordinated studies of the kinetics of crack growth, and adsorption and diffusion of hydrogen, using identical materials, have been initiated. Comparable conditions of temperature and pressure will be used in the chemical and mechanical experiments. Inconel 718 alloy and 18Ni(200) maraging steel have been selected for these studies. Results from these studies are expected to provide not only a better understanding of the gaseous hydrogen embrittlement phenomenon itself, but also fundamental information on hydrogen adsorption and diffusion, and crack growth information that can be used directly for design.

Structural efficiencies of various aluminum, titanium, and steel alloys at elevated temperatures

NASA Technical Reports Server (NTRS)

Heimerl, George J; Hughes, Philip J

1953-01-01

Efficient temperature ranges are indicated for two high-strength aluminum alloys, two titanium alloys, and three steels for some short-time compression-loading applications at elevated temperatures. Only the effects of constant temperatures and short exposure to temperature are considered, and creep is assumed not to be a factor. The structural efficiency analysis is based upon preliminary results of short-time elevated-temperature compressive stress-strain tests of the materials. The analysis covers strength under uniaxial compression, elastic stiffness, column buckling, and the buckling of long plates in compression or in shear.

Braze alloy process and strength characterization studies for 18 nickel grade 200 maraging steel with application to wind tunnel models

NASA Technical Reports Server (NTRS)

Bradshaw, James F.; Sandefur, Paul G., Jr.; Young, Clarence P., Jr.

1991-01-01

A comprehensive study of braze alloy selection process and strength characterization with application to wind tunnel models is presented. The applications for this study include the installation of stainless steel pressure tubing in model airfoil sections make of 18 Ni 200 grade maraging steel and the joining of wing structural components by brazing. Acceptable braze alloys for these applications are identified along with process, thermal braze cycle data, and thermal management procedures. Shear specimens are used to evaluate comparative shear strength properties for the various alloys at both room and cryogenic (-300 F) temperatures and include the effects of electroless nickel plating. Nickel plating was found to significantly enhance both the wetability and strength properties for the various braze alloys studied. The data are provided for use in selecting braze alloys for use with 18 Ni grade 200 steel in the design of wind tunnel models to be tested in an ambient or cryogenic environment.

Hydrogen Environment Assisted Cracking of Modern Ultra-High Strength Martensitic Steels

NASA Astrophysics Data System (ADS)

Pioszak, Greger L.; Gangloff, Richard P.

2017-09-01

Martensitic steels (Aermet®100, Ferrium®M54™, Ferrium®S53®, and experimental CrNiMoWV at ultra-high yield strength of 1550 to 1725 MPa) similarly resist hydrogen environment assisted cracking (HEAC) in aqueous NaCl. Cracking is transgranular, ascribed to increased steel purity and rare earth addition compared to intergranular HEAC in highly susceptible 300M. Nano-scale precipitates ((Mo,Cr)2C and (W,V)C) reduce H diffusivity and the K-independent Stage II growth rate by 2 to 3 orders of magnitude compared to 300M. However, threshold K TH is similarly low (8 to 15 MPa√m) for each steel at highly cathodic and open circuit potentials. Transgranular HEAC likely occurs along martensite packet and {110}α'-block interfaces, speculatively governed by localized plasticity and H decohesion. Martensitic transformation produces coincident site lattice interfaces; however, a connected random boundary network persists in 3D to negate interface engineering. The modern steels are near-immune to HEAC when mildly cathodically polarized, attributed to minimal crack tip H production and uptake. Neither reduced Co and Ni in M54 and CrNiMoWV nor increased Cr in S53 broadly degrade HEAC resistance compared to baseline AM100. The latter suggests that crack passivity dominates acidification to widen the polarization window for HEAC resistance. Decohesion models predict the applied potential dependencies of K TH and d a/d t II with a single-adjustable parameter, affirming the importance of steel purity and trap sensitive H diffusivity.

Multifunctional CNT-polymer composites for ultra-tough structural supercapacitors and desalination devices.

PubMed

Benson, Jim; Kovalenko, Igor; Boukhalfa, Sofiane; Lashmore, David; Sanghadasa, Mohan; Yushin, Gleb

2013-12-03

Pulsed electrodeposition of polyaniline (PANI) allows the fabrication of flexible, electrically conductive, nonwoven PANI-carbon nanotube (PANI-CNT) composite fabrics. They possess specific tensile strength and a modulus of toughness higher than that of aluminum matrix composites, titanium and aluminum alloys, steels, and many other structural materials. Electrochemical tests show that these nanocomposites additionally offer excellent cycle stability and ion electro-sorption and storage properties. © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Environmental crack-growth behavior of high strength pressure vessel alloys

NASA Technical Reports Server (NTRS)

Forman, R. G.

1975-01-01

Results of sustained-load environmental crack growth threshold tests performed on six spacecraft pressure vessel alloys are presented. The alloys were Inconel 718, 6Al-4V titanium, A-286 steel, AM-350 stainless steel, cryoformed AISI 301 stainless steel; and cryoformed AISI 304L steel. The test environments for the program were air, pressurized gases of hydrogen, oxygen, nitrogen, and carbon dioxide, and liquid environments of distilled water, sea water, nitrogen tetroxide, hydrazine, aerozine 50, monomethyl hydrazine, and hydrogen peroxide. Surface flaw type specimens were used with flaws located in both base metal and weld metal.

Study of retained austenite and nano-scale precipitation and their effects on properties of a low alloyed multi-phase steel by the two-step intercritical treatment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xie, Z.J.; Han, G., E-mail: hangang@mater.ustb.edu.cn; Zhou, W.H.

2016-03-15

Microstructure evolution and properties were studied in a low carbon low alloyed hot-rolled bainitic steel by annealing and annealing plus tempering. Microstructure of the hot-rolled steel consists of lath bainite and martensite. By annealing at 720 °C for 30 min and water quenching, multi-phase microstructure consisting of intercritical ferrite, tempered bainite/martensite, retained austenite and fresh martensite was obtained. With increasing annealing temperature to 760 °C, microstructure of the steel consisted of intercritical ferrite, fresh martensite without retained austenite. After the second step of tempering at 680 °C for samples annealed both at 720 °C and 760 °C, ~ 8–9% volumemore » fraction of retained austenite was obtained in the multi-phase microstructure. Moreover, fine precipitates of VC with size smaller than 10 nm and copper precipitates with size of ~ 10–50 nm were obtained after tempering. Results from scanning transmission electron microscopy (STEM) give evidence to support that the partitioning of Mn, Ni and Cu is of significance for retained austenite stabilization. Due to the combined contribution of multiphase microstructure, the transformation-induced-plasticity effect of retained austenite and strengthening effect of nanometer-sized precipitates, yield strength greater than 800 MPa, yield to tensile ratio of 0.9, uniform elongation of ~ 9% and good low temperature impact toughness of 147 J at − 40 °C were achieved. - Highlights: • Stable retained austenite was produced in a low alloyed steel. • Partition of Mn, Ni and Cu was confirmed by STEM for austenite stabilization. • Nano-sized VC and Cu precipitates were achieved by second tempering. • High strength–high toughness with low Y/T ratio was obtained.« less

Application technologies for effective utilization of advanced high strength steel sheets

DOE Office of Scientific and Technical Information (OSTI.GOV)

Suehiro, Masayoshi, E-mail: suehiro.kp5.masayoshi@jp.nssmc.com

Recently, application of high strength steel sheets for automobiles has increased in order to meet a demand of light weighting of automobiles to reduce a carbon footprint while satisfying collision safety. The formability of steel sheets generally decreases with the increase in strength. Fracture and wrinkles tend to occur easily during forming. The springback phenomenon is also one of the issues which we should cope with, because it makes it difficult to obtain the desired shape after forming. Advanced high strength steel sheets with high formability have been developed in order to overcome these issues, and at the same timemore » application technologies have been developed for their effective utilization. These sheets are normally used for cold forming. As a different type of forming, hot forming technique has been developed in order to produce parts with ultra high strength. In this report, technologies developed at NSSMC in this field will be introduced.« less

Corrosion fatigue of high strength fastener materials in seawater

NASA Technical Reports Server (NTRS)

Tipton, D. G.

1983-01-01

Environmental effects which significantly reduce the fatigue life of metals are discussed. Corrosion fatigue is a major concern in the engineering application of high strength fasteners in marine environments. The corrosion fatigue failure of an AISI 41L4O high strength steel blade to hub attachment bolt at the MOD-OA 200 kW wind turbine generator was investigated. The reduction of fatigue strength of AISI 41L4O in marine environments and to obtain similar corrosion fatigue data for candidate replacement materials was studied. The AISI 4140, PH 13-8Mo stainless steel, alloy 718 and alloy MP-35N were tested in axial fatigue at a frequency of 20 Hz in dry air and natural seawater. The fatigue data are fitted by regression equations to allow determination of fatigue strength for a given number of cycles to failure.

Corrosion fatigue of high strength fastener materials in seawater

NASA Astrophysics Data System (ADS)

Tipton, D. G.

1983-12-01

Environmental effects which significantly reduce the fatigue life of metals are discussed. Corrosion fatigue is a major concern in the engineering application of high strength fasteners in marine environments. The corrosion fatigue failure of an AISI 41L4O high strength steel blade to hub attachment bolt at the MOD-OA 200 kW wind turbine generator was investigated. The reduction of fatigue strength of AISI 41L4O in marine environments and to obtain similar corrosion fatigue data for candidate replacement materials was studied. The AISI 4140, PH 13-8Mo stainless steel, alloy 718 and alloy MP-35N were tested in axial fatigue at a frequency of 20 Hz in dry air and natural seawater. The fatigue data are fitted by regression equations to allow determination of fatigue strength for a given number of cycles to failure.

Development of a Modulated-Microstructure Heat Treatable Steel

DTIC Science & Technology

1975-07-10

IV. Heat Treatment V. Results and Discussion V. 1 Properties of the Soft Layer Alloy, PS4 V. 2 Properties of High Speed Steel (REX 71) V. 3...the High Strength System. Fig. 6 Hardness of Tempered PS4 Alloy. Cast alloy hardened by austenitizing, at 2175^ quenched, and reheating three times...at 1000oF and then cooling in liquid nitrogen to form martensite. Fig. 7A Metallographic Section Through Impact Fracture of PS4 Tempered at 300oF

Liquid Zn assisted embrittlement of advanced high strength steels with different microstructures

NASA Astrophysics Data System (ADS)

Jung, Geunsu; Woo, In Soo; Suh, Dong Woo; Kim, Sung-Joon

2016-03-01

In the present study, liquid metal embrittlement (LME) phenomenon during high temperature deformation was investigated for 3 grades of Zn-coated high strength automotive steel sheets consisting of different phases. Hot tensile tests were conducted for each alloy to compare their LME sensitivities at temperature ranges between 600 and 900 °C with different strain rates. The results suggest that Zn embrittles all the Fe-alloy system regardless of constituent phases of the steel. As hot tensile temperature and strain rate increase, LME sensitivity increases in every alloy. Furthermore, it is observed that the critical strain, which is experimentally thought to be 0.4% of strain at temperatures over 700 °C, is needed for LME to occur. It is observed via TEM work that Zn diffuses along grain boundaries of the substrate alloy when the specimen is strained at high temperatures. When the specimen is exposed to the strain more than 0.4% at over 700 °C, the segregation level of Zn at grain boundaries seems to become critical, leading to occurrence of LME cracks.

On the Specific Role of Microstructure in Governing Cyclic Fatigue, Deformation, and Fracture Behavior of a High-Strength Alloy Steel

NASA Astrophysics Data System (ADS)

Manigandan, K.; Srivatsan, T. S.

2015-06-01

In this paper, the results of an experimental study that focused on evaluating the conjoint influence of microstructure and test specimen orientation on fully reversed strain-controlled fatigue behavior of the high alloy steel X2M are presented and discussed. The cyclic stress response of this high-strength alloy steel revealed initial hardening during the first few cycles followed by gradual softening for most of fatigue life. Cyclic strain resistance exhibited a linear trend for the variation of elastic strain amplitude with reversals to failure, and plastic strain amplitude with reversals to failure. Fracture morphology was the same at the macroscopic level over the entire range of cyclic strain amplitudes examined. However, at the fine microscopic level, the alloy steel revealed fracture to be essentially ductile with features reminiscent of predominantly "locally" ductile and isolated brittle mechanisms. The mechanisms governing stress response at the fine microscopic level, fatigue life, and final fracture behavior are presented and discussed in light of the mutually interactive influences of intrinsic microstructural effects, deformation characteristics of the microstructural constituents during fully reversed strain cycling, cyclic strain amplitude, and resultant response stress.

Structure and properties during aging of an ultra-high strength Al-Cu-Li-Ag-Mg alloy

NASA Technical Reports Server (NTRS)

Gayle, Frank W.; Heubaum, Frank H.; Pickens, Joseph R.

1990-01-01

The structure and properties of the strengthening phases formed during aging in an Al-Cu-Li-Ag-Mg alloy (Weldalite 049) were elulcidated, by following the development of the microstructure by means of TEM. The results of observations showed that the Weldalite 049 alloy has a series of unusual and technologically useful combinations of mechanical properties in different aging conditions, such as natural aging without prior cold work to produce high strengths, a reversion temper of lower yield strength and unusually high ductility, a room temperature reaging of the reversion temper eventually leading to the original T4 hardness, and ultrahigh-strength T6 properties.

The effect of cobalt and carbon the microstructure and mechanical properties of martensitic precipitation strengthened stainless steels

NASA Astrophysics Data System (ADS)

Komolwit, Piyamanee

The effects of cobalt additions on the mechanical properties and strengthening mechanisms of a martensitic precipitation strengthening stainless steel whose composition is (in wt. %) 0.005C/12Cr/5Mo/1.5Ni has been investigated for cobalt levels of 9, 12, 15, 18, and 21 wt. %. Hardness, yield strength and ultimate tensile strength increase as the cobalt content increases, while the Charpy impact energy decreases as tempering temperature increases. At the peak strength of the 21 wt. % cobalt alloy, which is after tempering at 550°C, the yield strength is 1772 MPa, the ultimate tensile strength is 1916 MPa, and the hardness is 55 HRC. The martensite start temperature decreases as cobalt content increases. In this alloys there is no retained austenite after austenitizing, oil quenching and then refrigerating in liquid nitrogen prior to tempering. These alloys contain no reverted austenite except for the 21 wt. % cobalt alloy after tempering at 600°C. Optical micrographs show lath martensite as the matrix for all alloys. Increasing cobalt content has little effect on prior austenite grain size. Transmission electron micrographs show a substructure of lath martensite and a b.c.c. matrix for all alloys after tempering at 525°C. Precipitates were observed in dark field images at all cobalt levels and were seen in bright field images of 21 wt. % cobalt alloy. One of the precipitates was identified as omega phase with a trigonal structure with lattice parameter of a = b = 4.1 A, c = 2.51 A with c/a = 0.612. The particle size appears to be 17 nanometers in diameter and they were found only in the foils of 21 wt. % cobalt alloy. The second precipitate type was identified as a monoclinic phase with a monoclinic structure with lattice parameters of a = 5.464 A, b = 2.843 A, c = 3.178 A, and alpha = gamma = 90° and beta = 63.4°. The monoclinic phase particles appear to significantly contribute to the strength of these alloys, with particles size and volume fraction increasing with increasing cobalt content for the same condition. Limited observation on the effects of carbon additions to a 12Cr/12Co/5Mo/4.5Ni martensitic precipitation strengthening stainless steel has been made for carbon levels of 0.005 wt. %, 0.025 wt. % and 0.05 wt. %. A small addition of chromium, one weight percent, to a 0.005C/12Co/5Mo/5Ni martensitic precipitation strengthening stainless steel was found to increase hardness, strength, Charpy impact energy, and ductility. Results on the effects of cobalt, carbon and chromium additions helped in the selection of modified alloys which were used to investigate the effects of composition and heat treatment on strength and toughness. The first set of modified alloys are referred to as the low carbon modified alloys. These alloys have a better Charpy impact energy than the alloys used to investigate the effect of cobalt on strength and the hardness and strength of these alloys are similar to those of alloys used to investigate the effects of cobalt on strength. Fractographs of these alloys show quasi-cleavage fracture, the presence of ductile fracture increases with increasing cobalt content. The martensite start temperature is lowered by the chromium additions and results in the existence of retained austenite even after refrigeration after austenitizing. Refrigeration prior to tempering is not necessary for these alloys to achieve a high yield strength and good Charpy impact energy. The second set of modified alloys are referred to as the carbon-titanium modified alloys. These alloys differ from the first set of modified alloys in that these alloys contain small additions of carbon and titanium and have lower cobalt levels. Lower cobalt levels were required because carbon lowers the martensite start temperature. These alloys have improved Charpy impact energy and ductility. The carbon addition lowers the martensite start temperature and the martensite start temperature of these alloys is sufficiently low that they contain retain austenite even after refrigeration after austenitizing. Refrigeration prior to tempering is necessity for the alloys to maintain their yield strength and hardness. The effects of austenitizing temperature, cooling rate after austenitization, refrigeration and double austenitization on the mechanical properties of the modified alloys were investigated. Lowering the austenitization temperature decreases the Charpy impact energy and hardness of these alloys. (Abstract shortened by UMI.)

The Effect of Niobium Microalloying on Processing and Application Properties of Dual Phase Steel

NASA Astrophysics Data System (ADS)

Mohrbacher, Hardy

Dual phase steel is widely used in today's car body manufacturing. Its characteristics of high n-value and good elongation (A80) are the basis of good press formability. However, practical experience has shown unexpected failure in forming operations where tight bending, stretch flanging or hole expansion are predominant. The inhomogeneous microstructure of soft ferrite and hard martensite in combination with highly localized straining is the origin of these problems. Furthermore, weldability and delayed cracking have been experienced to cause problems in ultra-high strength DP steel. Refinement and homogenization of the two-phase microstructure as well as lowering of the carbon content have been identified as remedies to the mentioned problems. However, mill processing of DP steel with reduced carbon content is more difficult especially for the higher strength levels. Niobium microalloying proved to be very effective in increasing the processing window of low-carbon DP steels besides of its natural effect of refining the microstructure. Meanwhile the production of niobium microalloyed DP steel has been established in several markets including China. The paper details the fundamentals, demonstrates respective production concepts and presents examples of application of Nb-microalloyed DP steels.

Simulation of Microdamage and Evaluation of Remaining Life of Steam Conduit Components from New-Generation Refractory Steel 10Kh9MF-Sh

NASA Astrophysics Data System (ADS)

Gladshtein, V. I.

2018-03-01

The effects of microdamage on the remaining life of high-temperature components of steam conduits from high-chromium steel 10Kh9MF-Sh and low-alloy steel 12Kh1M1F are compared. To simulate the microdamage, specimens with a circular notch and different relative diameters are fabricated. Specimens with a notch simulating the highest degree of microdamage and smooth specimens are tested for long-term strength. The coefficient of the remaining life of a conduit is computed for the range of relative damage presenting practical interest.

High Strength and Thermally Stable Nanostructured Magnesium Alloys and Nanocomposites

NASA Astrophysics Data System (ADS)

Chang, Yuan-Wei

Magnesium and its alloys are currently in the spotlight of global research because of the need to limit energy consumption and reduce the environmental impact. In particular, their low densities compared to other structural metals make them a very attractive alternative in the automobile and aerospace industries. However, their low strength compared to other structural materials (e.g. Al and steels) has limited their widespread application. This dissertation presents the results of developing and investigation of a high strength nanostructured magnesium-aluminum alloy and composite. The nanostructured magnesium alloy is prepared by cryomilling and consolidated by spark-plasma-sintering. Focused ion beam is used to prepare micropillars with different diameters ranging from 1.5 to 8 mum and micro-compression test is conducted by nanoindenter in order to evaluate the mechanical properties. The yield strength obtained in the present study is around three times higher than conventional magnesium alloys (120 MPa vs. 370 MPa). The yield strength of the nanostructured magnesium alloy is further improved through hot extrusion, resulting in a yield strength of 550 MPa and an ultimate strength of 580 MPa. The nanostructured magnesium alloy exhibits a strong size-dependence, and a significant improvement in strength is observed when the pillar diameter is reduced to below 3.5 mum. The deformation mechanisms of the compressed pillars were characterized using transmission electron microscopy. The size-induced strengthening is attributed to a less number of dislocation sources along with a higher activity of non-basal deformation mechanisms. We have also developed a high strength and thermally stable nanostructured magnesium composite by adding diamantane. A yield strength of 500 MPa is achieved, moreover, excellent thermal stability is demonstrated in the magnesium alloy containing diamantanes. The strength and grain size are thermally stable after annealing at 400°C for 100 hours. In contrast, the yield strength of the alloy without diamantanes decreases significantly after annealing due to severe grain growth. These results suggest that diamantanes are pinning the grain boundaries and inhibiting grain growth at elevated temperatures. Finally, molecular dynamics simulations and finite element analysis are used to explore the deformation mechanisms of magnesium with different grain sizes at atomic resolutions and correct tapering effect on micro-compression test, respectively. The results in the dissertation show that nanostructured Mg-Al alloy and Mg-Al-Diamantane composite are promising materials for aerospace and automobile industries.

The Quantitative Microstructural Characterization of Multipass TIG Ultra Low Carbon Bainitic Steel Weldments and Correlation with Mechanical Properties

DTIC Science & Technology

1993-09-01

in TIG weldments. The alloying elements used in ULCB steels are; Carbon (C), Manganese (Mn), Molybdenum (Mo), Nickel (Ni), Niobium (Nb), Chromium (Cr...process. 7 C. WELDING PROCESSES 1. Tungsten Inert Gas (TIG) Welding Tungsten Inert Gas (TIG) Welding (or Gas Tungsten Arc Welding ( GTAW )), produces... chromium (Cr), molybdenum (Mo), and sometimes vanadium (V). Reheat cracking occurs in the HAZ during postweld stress relieving, especially in thick

Statistical Analysis on the Mechanical Properties of Magnesium Alloys

PubMed Central

Liu, Ruoyu; Jiang, Xianquan; Zhang, Hongju; Zhang, Dingfei; Wang, Jingfeng; Pan, Fusheng

2017-01-01

Knowledge of statistical characteristics of mechanical properties is very important for the practical application of structural materials. Unfortunately, the scatter characteristics of magnesium alloys for mechanical performance remain poorly understood until now. In this study, the mechanical reliability of magnesium alloys is systematically estimated using Weibull statistical analysis. Interestingly, the Weibull modulus, m, of strength for magnesium alloys is as high as that for aluminum and steels, confirming the very high reliability of magnesium alloys. The high predictability in the tensile strength of magnesium alloys represents the capability of preventing catastrophic premature failure during service, which is essential for safety and reliability assessment. PMID:29113116

Quantitative observations of hydrogen-induced, slow crack growth in a low alloy steel

NASA Technical Reports Server (NTRS)

Nelson, H. G.; Williams, D. P.

1973-01-01

Hydrogen-induced slow crack growth, da/dt, was studied in AISI-SAE 4130 low alloy steel in gaseous hydrogen and distilled water environments as a function of applied stress intensity, K, at various temperatures, hydrogen pressures, and alloy strength levels. At low values of K, da/dt was found to exhibit a strong exponential K dependence (Stage 1 growth) in both hydrogen and water. At intermediate values of K, da/dt exhibited a small but finite K dependence (Stage 2), with the Stage 2 slope being greater in hydrogen than in water. In hydrogen, at a constant K, (da/dt) sub 2 varied inversely with alloy strength level and varied essentially in the same complex manner with temperature and hydrogen pressure as noted previously. The results of this study provide support for most of the qualitative predictions of the lattice decohesion theory as recently modified by Oriani. The lack of quantitative agreement between data and theory and the inability of theory to explain the observed pressure dependence of slow crack growth are mentioned and possible rationalizations to account for these differences are presented.

Microstructural, mechanical and tribological investigation of 30CrMnSiNi2A ultra-high strength steel under various tempering temperatures

NASA Astrophysics Data System (ADS)

Arslan Hafeez, Muhammad; Farooq, Ameeq

2018-01-01

The aim of the research was to investigate the variation in microstructural, mechanical and tribological characteristics of 30CrMnSiNi2A ultra-high strength steel as a function of tempering temperatures. Steel was quenched at 880 °C and tempered at five different tempering temperatures ranging from 250 °C to 650 °C. Optical microscopy and pin on disc tribometer was used to evaluate the microstructural and wear properties. Results show that characteristics of 30CrMnSiNi2A are highly sensitive to tempering temperatures. Lathe and plate shaped martensite obtained by quenching transform first into ε-carbide, second cementite, third coarsened and spheroidized cementite and finally into recovered ferrite and austenite. Hardness, tensile and yield strengths decreased while elongation increased with tempering temperatures. On the other hand, wear rate first markedly decreased and then increased. Optimum amalgamation of characteristics was achieved at 350 °C.

The influence of Cr content on the mechanical properties of ODS ferritic steels

NASA Astrophysics Data System (ADS)

Li, Shaofu; Zhou, Zhangjian; Jang, Jinsung; Wang, Man; Hu, Helong; Sun, Hongying; Zou, Lei; Zhang, Guangming; Zhang, Liwei

2014-12-01

The present investigation aimed at researching the mechanical properties of the oxide dispersion strengthened (ODS) ferritic steels with different Cr content, which were fabricated through a consolidation of mechanical alloyed (MA) powders of 0.35 wt.% nano Y2O3 dispersed Fe-12.0Cr-0.5Ti-1.0W (alloy A), Fe-16.0Cr-0.5Ti-1.0W (alloy B), and Fe-18.0Cr-0.5Ti-1.0W (alloy C) alloys (all in wt.%) by hot isostatic pressing (HIP) with 100 MPa pressure at 1150 °C for 3 h. The mechanical properties, including the tensile strength, hardness, and impact fracture toughness were tested by universal testers, while Young's modulus was determined by ultrasonic wave non-destructive tester. It was found that the relationship between Cr content and the strength of ODS ferritic steels was not a proportional relationship. However, too high a Cr content will cause the precipitation of Cr-enriched segregation phase, which is detrimental to the ductility of ODS ferritic steels.

Precipitate design for creep strengthening of 9% Cr tempered martensitic steel for ultra-supercritical power plants

PubMed Central

Abe, Fujio

2008-01-01

It is crucial for the carbon concentration of 9% Cr steel to be reduced to a very low level, so as to promote the formation of MX nitrides rich in vanadium as very fine and thermally stable particles to enable prolonged periods of exposure at elevated temperatures and also to eliminate Cr-rich carbides M23C6. Sub-boundary hardening, which is inversely proportional to the width of laths and blocks, is shown to be the most important strengthening mechanism for creep and is enhanced by the fine dispersion of precipitates along boundaries. The suppression of particle coarsening during creep and the maintenance of a homogeneous distribution of M23C6 carbides near prior austenite grain boundaries, which precipitate during tempering and are less fine, are effective for preventing the long-term degradation of creep strength and for improving long-term creep strength. This can be achieved by the addition of boron. The steels considered in this paper exhibit higher creep strength at 650 °C than existing high-strength steels used for thick section boiler components. PMID:27877920

Systems design of transformation toughened blast-resistant naval hull steels

NASA Astrophysics Data System (ADS)

Saha, Arup

A systems approach to computational materials design has demonstrated a new class of ultratough, weldable secondary hardened plate steels combining new levels of strength and toughness while meeting processability requirements. A first prototype alloy has achieved property goals motivated by projected naval hull applications requiring extreme fracture toughness (Cv > 85 ft-lbs (115 J) corresponding to KId > 200 ksi.in1/2 (220 MPa.m1/2)) at strength levels of 150--180 ksi (1034--1241 MPa) yield strength in weldable, formable plate steels. A theoretical design concept was explored integrating the mechanism of precipitated nickel-stabilized dispersed austenite for transformation toughening in an alloy strengthened by combined precipitation of M2C carbides and BCC copper both at an optimal ˜3nm particle size for efficient strengthening. This concept was adapted to plate steel design by employing a mixed bainitic/martensitic matrix microstructure produced by air-cooling after solution-treatment and constraining the composition to low carbon content for weldability. With optimized levels of copper and M2C carbide formers based on a quantitative strength model, a required alloy nickel content of 6.5 wt% was predicted for optimal austenite stability for transformation toughening at the desired strength level of 160 ksi (1100 MPa) yield strength. A relatively high Cu level of 3.65 wt% was employed to allow a carbon limit of 0.05 wt% for good weldability. Hardness and tensile tests conducted on the designed prototype confirmed predicted precipitation strengthening behavior in quench and tempered material. Multi-step tempering conditions were employed to achieve the optimal austenite stability resulting in significant increase of impact toughness to 130 ft-lb (176 J) at a strength level of 160 ksi (1100 MPa). Comparison with the baseline toughness-strength combination determined by isochronal tempering studies indicates a transformation toughening increment of 60% in Charpy energy. Predicted Cu particle number densities and the heterogeneous nucleation of optimal stability high Ni 5 nm austenite on nanometer-scale copper precipitates in the multi-step tempered samples was confirmed using three-dimensional atom probe microscopy. Charpy impact tests and fractography demonstrate ductile fracture with C v > 90 ft-lbs (122 J) down to -40°C, with a substantial toughness peak at 25°C consistent with designed transformation toughening behavior. The properties demonstrated in this first prototype represent a substantial advance over existing naval hull steels.

Fatigue Properties of the Ultra-High Strength Steel TM210A

PubMed Central

Kang, Xia; Zhao, Gui-ping

2017-01-01

This paper presents the results of an experiment to investigate the high cycle fatigue properties of the ultra-high strength steel TM210A. A constant amplitude rotating bending fatigue experiment was performed at room temperature at stress ratio R = −1. In order to evaluate the notch effect, the fatigue experiment was carried out upon two sets of specimens, smooth and notched, respectively. In the experiment, the rotating bending fatigue life was tested using the group method, and the rotating bending fatigue limit was tested using the staircase method at 1 × 107 cycles. A double weighted least square method was then used to fit the stress-life (S–N) curve. The S–N curves of the two sets of specimens were obtained and the morphologies of the fractures of the two sets of specimens were observed with scanning electron microscopy (SEM). The results showed that the fatigue limit of the smooth specimen for rotating bending fatigue was 615 MPa; the ratio of the fatigue limit to tensile strength was 0.29, and the cracks initiated at the surface of the smooth specimen; while the fatigue limit of the notched specimen for rotating bending fatigue was 363 MPa, and the cracks initiated at the edge of the notch. The fatigue notch sensitivity index of the ultra-high strength maraging steel TM210A was 0.69. PMID:28891934

Study of Near-Threshold Fatigue Crack Propagation in Pipeline Steels in High Pressure Environments

NASA Technical Reports Server (NTRS)

Mitchell, M.

1981-01-01

Near threshold fatigue crack propagation in pipeline steels in high pressure environments was studied. The objective was to determine the level of threshold stress intensity for fatigue crack growth rate behavior in a high strength low alloy X60 pipeline-type steel. Complete results have been generated for gaseous hydrogen at ambient pressure, laboratory air at ambient pressure and approximately 60% relative humidity as well as vacuum of 0.000067 Pa ( 0.0000005 torr) at R-ratios = K(min)/K(max) of 0.1, 0.5, and 0.8. Fatigue crack growth rate behavior in gaseous hydrogen, methane, and methane plus 10 percent hydrogen at 6.89 MPa (100 psi) was determined.

Achieving large linear elasticity and high strength in bulk nanocompsite via synergistic effect

DOE PAGES

Hao, Shijie; Cui, Lishan; Guo, Fangmin; ...

2015-03-09

Elastic strain in bulk metallic materials is usually limited to only a fraction of 1%. Developing bulk metallic materials showing large linear elasticity and high strength has proven to be difficult. Here, based on the synergistic effect between nanowires and orientated martensite NiTi shape memory alloy, we developed an in-situ Nb nanowires-orientated martensitic NiTi matrix composite showing an ultra-large linear elastic strain of 4% and an ultrahigh yield strength of 1.8 GPa. This material also has a high mechanical energy storage efficiency of 96% and a high energy storage density of 36 J/cm 3 that is almost one order ofmore » larger than that of spring steel. It is demonstrated that the synergistic effect allows the exceptional mechanical properties of nanowires to be harvested at macro scale and the mechanical properties of matrix to be greatly improved, resulting in these superior properties. This research provides new avenues for developing advanced composites with superior properties by using effective synergistic effect between components.« less

Forming of AHSS using Servo-Presses

NASA Astrophysics Data System (ADS)

Groseclose, Adam Richard

Stamping of Advanced High Strength Steel (AHSS) alloys poses several challenges due to the material's higher strength and low formability compared to conventional steels and other problems such as (a) inconsistency of incoming material properties, (b) ductile fracture during forming, (c) higher contact pressure and temperature rise during forming, (d) higher die wear leading to reduced tool life, (e) higher forming load/press capacity, and (f) large springback leading to dimensional inaccuracy in the formed part. [Palaniswamy et. al., 2007]. The use of AHSS has been increasing steadily in automotive stamping. New AHSS alloys (TRIP, TWIP) may replace some of the Hot Stamping applications. Stamping of AHSS alloys, especially higher strength materials, 780 MPa and higher, present new challenges in obtaining good part definition (corner and fillet radii), formability (fracture and resulting scrap) and in reducing springback. Servo-drive presses, having the capability to have infinitely variable and adjustable ram speed and dwell at BDC, offer a potential improvement in quality, part definition, and springback reduction especially when the infinitely adjustable slide motion is used in combination with a CNC hydraulic cushion. Thus, it is desirable to establish a scientific/engineering basis for improving the stamping conditions in forming AHSS using a servo-drive press.

Self-Pierce Riveting of Three Aluminium Alloy and Mild Steel Sheets

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mori, K.; Abe, Y.; Sakai, S.

2010-06-15

Three aluminium alloy and steel sheets were joined with a self-piercing rivet. Self-pierce riveting has the function of joining steel and aluminium alloys having very different melting points due to plastic joining. The requisites for joining the three sheets are the driving of the rivet leg through the middle sheet, the flaring of the rivet leg in the lower sheet and the prevention of the fracture of the lower sheet. The joinability for various combinations of the three sheets was determined. When the rivet leg is small, no driving through the middle sheet occurs, the lower sheet ruptures for amore » large rivet leg. In addition, 980 MPa high strength steel, mild steel and aluminium alloy sheets were joined by the self-pierce riveting.« less

High Integrity Castings: Proceedings of the Conference on Advances in High Integrity Castings Held in Conjunction with the 1988 World Materials Congress, Chicago, Illinois, USA, 24-30 September 1988

DTIC Science & Technology

1988-01-01

above design requirements. The The first cast parts used in this higher strength standard chemistry parts application were of the Extra Low...present work was to study the use of beta THE HIGH COST OF TITANIUM alloys can limit their titanium alloys in the cast form. Beta or use to applications ...refractory as was is intended to achieve a pouring stream su- used with the nozzles for steel applications . perior to conventional nozzle designs , and this

A high-specific-strength and corrosion-resistant magnesium alloy

NASA Astrophysics Data System (ADS)

Xu, Wanqiang; Birbilis, Nick; Sha, Gang; Wang, Yu; Daniels, John E.; Xiao, Yang; Ferry, Michael

2015-12-01

Ultra-lightweight alloys with high strength, ductility and corrosion resistance are desirable for applications in the automotive, aerospace, defence, biomedical, sporting and electronic goods sectors. Ductility and corrosion resistance are generally inversely correlated with strength, making it difficult to optimize all three simultaneously. Here we design an ultralow density (1.4 g cm-3) Mg-Li-based alloy that is strong, ductile, and more corrosion resistant than Mg-based alloys reported so far. The alloy is Li-rich and a solute nanostructure within a body-centred cubic matrix is achieved by a series of extrusion, heat-treatment and rolling processes. Corrosion resistance from the environment is believed to occur by a uniform lithium carbonate film in which surface coverage is much greater than in traditional hexagonal close-packed Mg-based alloys, explaining the superior corrosion resistance of the alloy.

A high-specific-strength and corrosion-resistant magnesium alloy.

PubMed

Xu, Wanqiang; Birbilis, Nick; Sha, Gang; Wang, Yu; Daniels, John E; Xiao, Yang; Ferry, Michael

2015-12-01

Ultra-lightweight alloys with high strength, ductility and corrosion resistance are desirable for applications in the automotive, aerospace, defence, biomedical, sporting and electronic goods sectors. Ductility and corrosion resistance are generally inversely correlated with strength, making it difficult to optimize all three simultaneously. Here we design an ultralow density (1.4 g cm(-3)) Mg-Li-based alloy that is strong, ductile, and more corrosion resistant than Mg-based alloys reported so far. The alloy is Li-rich and a solute nanostructure within a body-centred cubic matrix is achieved by a series of extrusion, heat-treatment and rolling processes. Corrosion resistance from the environment is believed to occur by a uniform lithium carbonate film in which surface coverage is much greater than in traditional hexagonal close-packed Mg-based alloys, explaining the superior corrosion resistance of the alloy.

Analysis of Bolted and Bonded Composite

DTIC Science & Technology

1992-09-01

pp. 1067-1079. 2-73. Askins, D. R. and D. R. Byrge, "Evaluation of 350°F Curing Adhesive Systems on Phosphoricn Acid Anodized Aluminum Substrates...Acceptable Aluminum Not compatible Cadmium Not compatible Chrom. plate Adequate with A286, PHI 3-8MO INCO 600 (Cobalt alloys) Good Low alloy steel Not... aluminum . Their tensile moduli are 30, 16 and 10 msi, respectively. The range for tensile strengths of steel and titanium bolts is approximately 220 to

Numerical simulation of temperature field, microstructure evolution and mechanical properties of HSS during hot stamping

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shi, Dongyong; Liu, Wenquan; Ying, Liang, E-mail: pinghu@dlut.edu.cn

The hot stamping of boron steels is widely used to produce ultra high strength automobile components without any spring back. The ultra high strength of final products is attributed to the fully martensitic microstructure that is obtained through the simultaneous forming and quenching of the hot blanks after austenization. In the present study, a mathematical model incorporating both heat transfer and the transformation of austenite is presented. A FORTRAN program based on finite element technique has been developed which permits the temperature distribution and microstructure evolution of high strength steel during hot stamping process. Two empirical diffusion-dependent transformation models undermore » isothermal conditions were employed respectively, and the prediction capability on mechanical properties of the models were compared with the hot stamping experiment of an automobile B-pillar part.« less

Research and Development of Ultra-High Strength X100 Welded Pipe

NASA Astrophysics Data System (ADS)

Chuanguo, Zhang; Lei, Zheng; Ping, Hu; Bei, Zhang; Kougen, Wu; Weifeng, Huang

Ultra-high strength X100 welded pipe can be used in the construction of long distance oil and gas pipeline to improve transmission capacity and reduce operation cost. By using the way of thermo-simulation and pilot rolling, the CCT (Continuous Cooling Transformation) diagram and the relationship between ACC (Accelerated Cooling) parameters, microstructure and mechanical properties were studied for the designed X100 pipeline steel with low carbon, high manganese and niobium micro-alloyed composition in lab. The analysis of CCT diagram indicates that the suitable hardness and microstructure can be obtained in the cooling rate of 20 80°C/sec. The pilot rolling results show that the ACC cooling start temperature below Ar3 phase transformation point is beneficial to increase uniform elongation, and the cooling stop temperature of 150 350°C is helpful to obtain high strength and toughness combination. Based on the research conclusions, the X100 plate and UOE pipe with dimension in O.D.1219×W.T.14.8mm, O.D.1219×W.T.17.8mm, designed for the natural gas transmission pipeline, were trial produced. The manufactured pipe body impact absorbed energy at -10°C is over 250J. The DWTT shear area ratio at 0°C is over 85%. The transverse strength meets the X100 grade requirement, and uniform elongation is over 4%. The X100 plate and UOE pipe with dimension in O.D.711×W.T.20.0mm, O.D.711×W.T.12.5mm, designed for an offshore engineering, were also trial produced. The average impact absorbed energy of pipe body at -30°C is over 200J. The average impact absorbed energy of HAZ (Heat-affected zone) and WM (Welded Seam) at -30°C is over 100J. And the good pipe shapes were obtained

Processing and Characterization of High Strength, High Ductility Hadfield Steel

DTIC Science & Technology

1990-04-01

precipitation in high carbon content Hadfield steel resulting in the introduction of a grain boundary void nucleation softening mechanism leading to plastic...hardening, in comparison to the thin twin spacing of Fe-Ni martensite and inferred that carbon may have an important role in contributing to Hadfield steel ...approaches to strengthening from alloying or precipitation mechanisms are introduced, the deformation mechanisms responsible for Hadfield steel

The Science of Cost-Effective Materials Design - A Study in the Development of a High Strength, Impact Resistant Steel

NASA Astrophysics Data System (ADS)

Abrahams, Rachel

2017-06-01

Intermediate alloy steels are widely used in applications where both high strength and toughness are required for extreme/dynamic loading environments. Steels containing greater than 10% Ni-Co-Mo are amongst the highest strength martensitic steels, due to their high levels of solution strengthening, and preservation of toughness through nano-scaled secondary hardening, semi-coherent hcp-M2 C carbides. While these steels have high yield strengths (σy 0.2 % >1200 MPa) with high impact toughness values (CVN@-40 >30J), they are often cost-prohibitive due to the material and processing cost of nickel and cobalt. Early stage-I steels such as ES-1 (Eglin Steel) were developed in response to the high cost of nickel-cobalt steels and performed well in extreme shock environments due to the presence of analogous nano-scaled hcp-Fe2.4 C epsilon carbides. Unfortunately, the persistence of W-bearing carbides limited the use of ES-1 to relatively thin sections. In this study, we discuss the background and accelerated development cycle of AF96, an alternative Cr-Mo-Ni-Si stage-I temper steel using low-cost heuristic and Integrated Computational Materials Engineering (ICME)-assisted methods. The microstructure of AF96 was tailored to mimic that of ES-1, while reducing stability of detrimental phases and improving ease of processing in industrial environments. AF96 is amenable to casting and forging, deeply hardenable, and scalable to 100,000 kg melt quantities. When produced at the industrial scale, it was found that AF96 exhibits near-statistically identical mechanical properties to ES-1 at 50% of the cost.

Experimental evaluation of tool wear throughout a continuous stroke blanking process of quenched 22MnB5 ultra-high-strength steel

NASA Astrophysics Data System (ADS)

Vogt, S.; Neumayer, F. F.; Serkyov, I.; Jesner, G.; Kelsch, R.; Geile, M.; Sommer, A.; Golle, R.; Volk, W.

2017-09-01

Steel is the most common material used in vehicles’ chassis, which makes its research an important topic for the automotive industry. Recently developed ultra-high-strength steels (UHSS) provide extreme tensile strength up to 1,500 MPa and combine great crashworthiness with good weight reduction potential. However, in order to reach the final shape of sheet metal parts additional cutting steps such as trimming and piercing are often required. The final trimming of quenched metal sheets presents a huge challenge to a conventional process, mainly because of the required extreme cutting force. The high cutting impact, due to the materials’ brittleness, causes excessive tool wear or even sudden tool failure. Therefore, a laser is commonly used for the cutting process, which is time and energy consuming. The purpose of this paper is to demonstrate the capability of a conventional blanking tool design in a continuous stroke piercing process using boron steel 22MnB5 sheets. Two different types of tool steel were tested for their suitability as active cutting elements: electro-slag remelted (ESR) cold work tool steel Bohler K340 ISODUR and powder-metallurgic (PM) high speed steel Bohler S390 MICROCLEAN. A FEM study provided information about an optimized punch design, which withstands buckling under high cutting forces. The wear behaviour of the process was assessed by the tool wear of the active cutting elements as well as the quality of cut surfaces.

Orientation dependence of microfracture behavior in a dual-phase high-strength low-alloy steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Suh, D.; Lee, S.; Kim, N.J.

1997-02-01

In selecting the processing conditions and evaluating the reliability of structural materials, microscopic observations and identification of the fracture mechanisms in local cracking behavior are required. An important instance in the failure of the local brittle zone (LBZ) in the welding zone. The LBZ, which is very brittle, is the coarse-grained heat-affected zone near the fusion line, a zone known to be critical to the fracture toughness of welded parts. Thus, maintaining stable fracture resistance by predicting the microfracture behavior is important when using high-strength low-alloy (HSLA) steels in offshore structural steel welds. Depending on the thermal cycles involved duringmore » welding, the ferrite/martensite structure can have various morphologies of martensite particles, for example, fibrous and blocky martensite. In summary, in situ SEM fracture tests reveal that in the L-oriented IQ DCB specimen, a microcrack tends to propagate relatively uniformly throughout the ferrite and well-distributed fine fibrous martensite, yielding good elongation with high strength level. Also, the IQ structure in the T orientation shows similar microfracture behavior. On the other hand, in the SQ structure, where blocky-type martensite is mixed with ferrite, strain is localized into shear bands mostly in the ferrite region, and a local microcrack propagates along the strain-localized band formed in the ferrite, resulting in the SQ structure in the T orientation, where the ferrite-martensite bands are parallel to the notch direction, the martensite cannot act as an efficient barrier to microcrack advance, and thus the tensile ductility is decreased.« less

Laser beam joining of material combinations for automotive applications

NASA Astrophysics Data System (ADS)

Schubert, Emil; Zerner, Ingo; Sepold, Gerd

1997-08-01

An ideal material for automotive applications would combine the following properties: high corrosion resistance, high strength, high stiffness and not at least a low material price. Today a single material is not able to meet all these requirements. Therefore, in the future different materials will be placed where they meet the requirements best. The result of this consideration is a car body with many different alloys and metals, which have to be joined to one another. BIAS is working on the development of laser based joining technologies for different material combinations, especially for thin sheets used in automotive applications. One result of the research is a joining technology for an aluminum-steel-joint. Using a Nd:YAG laser the problem of brittle intermetallic phases between these materials was overcome. Using suitable temperature-time cycles, elected by a FEM-simulation, the thickness of intermetallic phases was kept below 10 micrometers . This technology was also applied to coated steels, which were joined with different aluminum alloys. Further it is demonstrated that titanium alloys, e.g. used for racing cars, can also be joined with aluminum alloys.

Comparison of Fatigue Properties and Fatigue Crack Growth Rates of Various Implantable Metals

PubMed Central

Okazaki, Yoshimitsu

2012-01-01

The fatigue strength, effects of a notch on the fatigue strength, and fatigue crack growth rate of Ti-15Zr-4Nb-4Ta alloy were compared with those of other implantable metals. Zr, Nb, and Ta are important alloying elements for Ti alloys for attaining superior long-term corrosion resistance and biocompatibility. The highly biocompatible Ti-15Zr-4Nb-4Ta alloy exhibited an excellent balance between strength and ductility. Its notched tensile strength was much higher than that of a smooth specimen. The strength of 20% cold-worked commercially pure (C.P.) grade 4 Ti was close to that of Ti alloy. The tension-to-tension fatigue strength of an annealed Ti-15Zr-4Nb-4Ta rod at 107 cycles was approximately 740 MPa. The fatigue strength of this alloy was much improved by aging treatment after solution treatment. The fatigue strengths of C.P. grade 4 Ti and stainless steel were markedly improved by 20% cold working. The fatigue strength of Co-Cr-Mo alloy was markedly increased by hot forging. The notch fatigue strengths of 20% cold-worked C.P. grade 4 Ti, and annealed and aged Ti-15Zr-4Nb-4Ta, and annealed Ti-6Al-4V alloys were less than those of the smooth specimens. The fatigue crack growth rate of Ti-15Zr-4Nb-4Ta was the same as that of Ti-6Al-4V. The fatigue crack growth rate in 0.9% NaCl was the same as that in air. Stainless steel and Co-Cr-Mo-Ni-Fe alloy had a larger stress-intensity factor range (ΔK) than Ti alloy.

Research Results Of Stress-Strain State Of Cutting Tool When Aviation Materials Turning

NASA Astrophysics Data System (ADS)

Serebrennikova, A. G.; Nikolaeva, E. P.; Savilov, A. V.; Timofeev, S. A.; Pyatykh, A. S.

2018-01-01

Titanium alloys and stainless steels are hard-to-machine of all the machining types. Cutting edge state of turning tool after machining titanium and high-strength aluminium alloys and corrosion-resistant high-alloy steel has been studied. Cutting forces and chip contact arears with the rake surface of cutter has been measured. The relationship of cutting forces and residual stresses are shown. Cutting forces and residual stresses vs value of cutting tool rake angle relation were obtained. Measurements of residual stresses were performed by x-ray diffraction.

Development of a High-Strength Ultrafine-Grained Ferritic Steel Nanocomposite

NASA Astrophysics Data System (ADS)

Rahmanifard, Roohollah; Farhangi, Hasan; Novinrooz, Abdul Javad; Moniri, Samira

2013-02-01

This article describes the microstructural and mechanical properties of 12YWT oxide-dispersion-strengthened (ODS)-ferritic steel nanocomposite. According to the annealing results obtained from X-ray diffraction line profile analysis on mechanically alloyed powders milled for 80 hours, the hot extrusion at 1123 K (850 °C) resulted in a nearly equiaxed ultrafine structure with an ultimate tensile strength of 1470 MPa, yield strength of 1390 MPa, and total elongation of 13 pct at room temperature comparable with high-strength 14YWT ODS steel. Maximum total elongation was found at 973 K (600 °C) where fractography of the tensile specimen showed a fully ductile dimple feature compared with the splitting cracks and very fine dimpled structure observed at room temperature. The presence of very small particles on the wall of dimples at 1073 K (800 °C) with nearly chemical composition of the matrix alloy was attributed to the activation of the boundaries decohesion mechanism as a result of diffusion of solute atoms. The results of Charpy impact test also indicated significant improvement of transition temperature with respect to predecessor 12YWT because of the decreased grain size and more homogeneity of grain size distribution. Hence, this alloy represented a good compromise between the strength and Charpy impact properties.

Optimum Design and Development of High Strength and Toughness Welding Wire for Pipeline Steel

NASA Astrophysics Data System (ADS)

Chen, Cuixin; Xue, Haitao; Yin, Fuxing; Peng, Huifen; Zhi, Lei; Wang, Sixu

Pipeline steel with higher strength(>800MPa) has been gradually used in recent years, so how to achieve good match of base metal and weld deposit is very important for its practical application. Based on the alloy system of 0.02-0.04%C, 2.0%Mn and 0.5%Si, four different kinds of welding wires were designed and produced. The effects of alloy elements on phase transformation and mechanical properties were analyzed. Experimental results show that the designed steels with the addition of 2-4% Ni+Cr+Mo and <0.2% Nb+V+Ti have high strength (>800MPa) and good elongation (>15%). The microstructure of deposits metal is mainly composed of granular bainite and M-A constituents with the mean size of 0.2-07μm are dispersed on ferritic matrix. The deposited metals have good match of strength (>800MPa) and impact toughness (>130J) which well meet the requirement of pipeline welding.

Comprehensive Understanding of Ductility Loss Mechanisms in Various Steels with External and Internal Hydrogen

NASA Astrophysics Data System (ADS)

Takakuwa, Osamu; Yamabe, Junichiro; Matsunaga, Hisao; Furuya, Yoshiyuki; Matsuoka, Saburo

2017-11-01

Hydrogen-induced ductility loss and related fracture morphologies are comprehensively discussed in consideration of the hydrogen distribution in a specimen with external and internal hydrogen by using 300-series austenitic stainless steels (Types 304, 316, 316L), high-strength austenitic stainless steels (HP160, XM-19), precipitation-hardened iron-based super alloy (A286), low-alloy Cr-Mo steel (JIS-SCM435), and low-carbon steel (JIS-SM490B). External hydrogen is realized by a non-charged specimen tested in high-pressure gaseous hydrogen, and internal hydrogen is realized by a hydrogen-charged specimen tested in air or inert gas. Fracture morphologies obtained by slow-strain-rate tensile tests (SSRT) of the materials with external or internal hydrogen could be comprehensively categorized into five types: hydrogen-induced successive crack growth, ordinary void formation, small-sized void formation related to the void sheet, large-sized void formation, and facet formation. The mechanisms of hydrogen embrittlement are broadly classified into hydrogen-enhanced decohesion (HEDE) and hydrogen-enhanced localized plasticity (HELP). In the HEDE model, hydrogen weakens interatomic bonds, whereas in the HELP model, hydrogen enhances localized slip deformations. Although various fracture morphologies are produced by external or internal hydrogen, these morphologies can be explained by the HELP model rather than by the HEDE model.

Wrought Cr--W--V bainitic/ferritic steel compositions

DOEpatents

Klueh, Ronald L.; Maziasz, Philip J.; Sikka, Vinod Kumar; Santella, Michael L.; Babu, Sudarsanam Suresh; Jawad, Maan H.

2006-07-11

A high-strength, high-toughness steel alloy includes, generally, about 2.5% to about 4% chromium, about 1.5% to about 3.5% tungsten, about 0.1% to about 0.5% vanadium, and about 0.05% to 0.25% carbon with the balance iron, wherein the percentages are by total weight of the composition, wherein the alloy is heated to an austenitizing temperature and then cooled to produce an austenite transformation product.

Development of High Heat Input Welding Offshore Steel as Normalized Condition

NASA Astrophysics Data System (ADS)

Deng, Wei; Qin, Xiaomei

The heavy plate used for offshore structure is one of the important strategic products. In recent years, there is an increasing demand for heavy shipbuilding steel plate with excellent weldability in high heat input welding. During the thermal cycle, the microstructure of the heat affected zone (HAZ) of plates was damaged, and this markedly reduced toughness of HAZ. So, how to improve the toughness of HAZ has been a key subject in the fields of steel research. Oxide metallurgy is considered as an effective way to improve toughness of HAZ, because it could be used to retard grain growth by fine particles, which are stable at the high temperature.The high strength steel plate, which satisfies the low temperature specification, has been applied to offshore structure. Excellent properties of the plates and welded joints were obtained by oxide metallurgy technology, latest controlled rolling and accelerated cooling technology using Ultra-Fast Cooling (an on-line accelerated cooling system). The 355MPa-grade high strength steel plates with normalizing condition were obtained, and the steels have excellent weldability with heat input energy of 79 287kJ/cm, and the nil ductility transition (NDT) temperature was -70°C, which can satisfy the construction of offshore structure in cold regions.

An experimental study on fatigue performance of cryogenic metallic materials for IMO type B tank

NASA Astrophysics Data System (ADS)

Lee, Jin-Sung; You, Won-Hyo; Yoo, Chang-Hyuk; Kim, Kyung-Su; Kim, Yooil

2013-12-01

Three materials SUS304, 9% Ni steel and Al 5083-O alloy, which are considered possible candidate for International Maritime Organization (IMO) type B Cargo Containment System, were studied. Monotonic tensile, fatigue, fatigue crack growth rate and Crack Tip Opening Displacement tests were carried out at room, intermediate low (-100 °C) and cryogenic (-163 °C) temperatures. The initial yield and tensile strengths of all materials tended to increase with decreasing temperature, whereas the change in elastic modulus was not as remarkable. The largest and smallest improvement ratio of the initial yield strengths due to a temperature reduction were observed in the SUS304 and Al 5083- O alloy, respectively. The fatigue strengths of the three materials increased with decreasing temperature. The largest increase in fatigue strength was observed in the Al 5083-O alloy, whereas the 9% Ni steel sample showed the smallest increase. In the fatigue crack growth rate test, SUS304 and Al 5083-O alloy showed a decrease in the crack propagation rate, due to decrease in temperature, but no visible improvement in da/dN was observed in the case of 9% Ni steel. In the Crack Tip Opening Displacement (CTOD) test, CTOD values were converted to critical crack length for the comparison with different thickness specimens. The critical crack length tended to decrease in the case of SUS304 and increase for the Al 5083-O alloy with decreasing temperature. In case of 9% Ni steel, change of critical crack length was not observed due to temperature decrease. In addition, the changing material properties according to the temperature of the LNG tank were analyzed according to the international code for the construction and equipment of ships carrying liquefied gases in bulk (IGC code) and the rules of classifications.

Structure and properties of corrosion and wear resistant Cr-Mn-N steels

NASA Astrophysics Data System (ADS)

Lenel, U. R.; Knott, B. R.

1987-06-01

Steels containing about 12 pct Cr, 10 pct Mn, and 0.2 pct N have been shown to have an unstable austenitic microstructure and have good ductility, extreme work hardening, high fracture strength, excellent toughness, good wear resistance, and moderate corrosion resistance. A series of alloys containing 9.5 to 12.8 pct Cr, 5.0 to 10.4 pct Mn, 0.16 to 0.32 pct N, 0.05 pct C, and residual elements typical of stainless steels was investigated by microstructural examination and mechanical, abrasion, and corrosion testing. Microstructures ranged from martensite to unstable austenite. The unstable austenitic steels transformed to α martensite on deformation and displayed very high work hardening, exceeding that of Hadfield’s manganese steels. Fracture strengths similar to high carbon martensitic stainless steels were obtained while ductility and toughness values were high, similar to austenitic stainless steels. Resistance to abrasive wear exceeded that of commercial abrasion resistant steels and other stainless steels. Corrosion resistance was similar to that of other 12 pct Cr steels. Properties were not much affected by minor compositional variations or rolled-in nitrogen porosity. In 12 pct Cr-10 pct Mn alloys, ingot porosity was avoided when nitrogen levels were below 0.19 pet, and austenitic microstructures were obtained when nitrogen levels exceeded 0.14 pct.

A New Vacuum Brazing Route for Niobium-316L Stainless Steel Transition Joints for Superconducting RF Cavities

NASA Astrophysics Data System (ADS)

Kumar, Abhay; Ganesh, P.; Kaul, R.; Bhatnagar, V. K.; Yedle, K.; Ram Sankar, P.; Sindal, B. K.; Kumar, K. V. A. N. P. S.; Singh, M. K.; Rai, S. K.; Bose, A.; Veerbhadraiah, T.; Ramteke, S.; Sridhar, R.; Mundra, G.; Joshi, S. C.; Kukreja, L. M.

2015-02-01

The paper describes a new approach for vacuum brazing of niobium-316L stainless steel transition joints for application in superconducting radiofrequency cavities. The study exploited good wettability of titanium-activated silver-base brazing alloy (CuSil-ABA®), along with nickel as a diffusion barrier, to suppress brittle Fe-Nb intermetallic formation, which is well reported during the established vacuum brazing practice using pure copper filler. The brazed specimens displayed no brittle intermetallic layers on any of its interfaces, but instead carried well-distributed intermetallic particles in the ductile matrix. The transition joints displayed room temperature tensile and shear strengths of 122-143 MPa and 80-113 MPa, respectively. The joints not only exhibited required hermeticity (helium leak rate <1.1 × 10-10 mbar l/s) for service in ultra-high vacuum but also withstood twelve hour degassing heat treatment at 873 K (suppresses Q-disease in niobium cavities), without any noticeable degradation in the microstructure and the hermeticity. The joints retained their leak tightness even after undergoing ten thermal cycles between the room temperature and the liquid nitrogen temperature, thereby establishing their ability to withstand service-induced low cycle fatigue conditions. The study proposes a new lower temperature brazing route to form niobium-316L stainless steel transition joints, with improved microstructural characteristics and acceptable hermeticity and mechanical properties.

Dynamic strength properties of the surface of an ultra-fine-grained aluminum alloy under conditions of high-speed erosion

NASA Astrophysics Data System (ADS)

Kazarinov, N. A.; Evstifeev, A. D.; Petrov, Yu. V.; Lashkov, V. A.

2016-05-01

The influence of severe plastic deformation on the material surface is investigated under highspeed erosion conditions. The AD1 aluminum alloy was tested with the structure changed by severe plastic torsional deformation.

Advanced characterization techniques in understanding the roles of nickel in enhancing strength and toughness of submerged arc welding high strength low alloy steel multiple pass welds in the as-welded condition

NASA Astrophysics Data System (ADS)

Sham, Kin-Ling

Striving for higher strength along with higher toughness is a constant goal in material properties. Even though nickel is known as an effective alloying element in improving the resistance of a steel to impact fracture, it is not fully understood how nickel enhances toughness. It was the goal of this work to assist and further the understanding of how nickel enhanced toughness and maintained strength in particular for high strength low alloy (HSLA) steel submerged arc welding multiple pass welds in the as-welded condition. Using advanced analytical techniques such as electron backscatter diffraction, x-ray diffraction, electron microprobe, differential scanning calorimetry, and thermodynamic modeling software, the effect of nickel was studied with nickel varying from one to five wt. pct. in increments of one wt. pct. in a specific HSLA steel submerged arc welding multiple pass weldment. The test matrix of five different nickel compositions in the as-welded and stress-relieved condition was to meet the targeted mechanical properties with a yield strength greater than or equal to 85 ksi, a ultimate tensile strength greater than or equal to 105 ksi, and a nil ductility temperature less than or equal to -140 degrees F. Mechanical testing demonstrated that nickel content of three wt. pct and greater in the as-welded condition fulfilled the targeted mechanical properties. Therefore, one, three, and five wt. pct. nickel in the as-welded condition was further studied to determine the effect of nickel on primary solidification mode, nickel solute segregation, dendrite thickness, phase transformation temperatures, effective ferrite grain size, dislocation density and strain, grain misorientation distribution, and precipitates. From one to five wt. pct nickel content in the as-welded condition, the primary solidification was shown to change from primary delta-ferrite to primary austenite. The nickel partitioning coefficient increased and dendrite/cellular thickness was refined. Austenite decomposition temperatures into different ferrite products were also suppressed to refine the effective ferrite grain size with increasing nickel. Finally, dislocation density and strain increased and a more preferred orientation behavior was observed. At five wt. pct nickel, a precipitate in the form of MnNi3 or FeNi3 was observed. Its presence in both inter and intragranular regions enhanced strength and toughness by limiting the ferrite grain size and precipitation strengthening.

Continuous cooling transformations and microstructures in a low-carbon, high-strength low-alloy plate steel

NASA Astrophysics Data System (ADS)

Thompson, S. W.; Vin, D. J., Col; Krauss, G.

1990-06-01

A continuous-cooling-transformation (CCT) diagram was determined for a high-strength low-alloy plate steel containing (in weight percent) 0.06 C, 1.45 Mn, 1.25 Cu, 0.97 Ni, 0.72 Cr, and 0.42 Mo. Dilatometric measurements were supplemented by microhardness testing, light microscopy, and transmission electron microscopy. The CCT diagram showed significant suppression of polygonal ferrite formation and a prominent transformation region, normally attributed to bainite formation, at temperatures intermediate to those of polygonal ferrite and martensite formation. In the intermediate region, ferrite formation in groups of similarly oriented crystals about 1 μm in size and containing a high density of dislocations dominated the transformation of austenite during continuous cooling. The ferrite grains assumed two morphologies, elongated or acicular and equiaxed or granular, leading to the terms “acicular ferrite” and “granular ferrite,” respectively, to describe these structures. Austenite regions, some transformed to martensite, were enriched in carbon and retained at interfaces between ferrite grains. Coarse interfacial ledges and the nonacicular morphology of the granular ferrite grains provided evidence for a phase transformation mechanism involving reconstructive diffusion of substitutional atoms. At slow cooling rates, polygonal ferrite and Widmanstätten ferrite formed. These latter structures contained low dislocation densities and e-copper precipitates formed by an interphase transformation mechanism.

Materials studies for magnetic fusion energy applications at low temperatures, 7

NASA Astrophysics Data System (ADS)

Reed, R. P.; Simon, N. J.

1984-05-01

Work leading toward development of strong, tough structural alloys for use in superconducting magnets of magnetic fusion power plants is reported. Low temperature studies were conducted to assess the quantitative dependence of the yield strength, density, and elastic constants of AISI 304 stainless steels upon carbon and nitrogen concentration. Tensile property measurements of developmental austenitic steels confirmed the dependence of yield strength upon temperature. Evidence is presented to show that the flow strength and austenite stability of stainless steels are not significantly affected by 8-T fields at 4 K. Instrumentation developed for low temperature testing included a computer assisted apparatus used to measure threshold fatigue. Low temperature welding research involved an investigation of the weld reinforcement effect on the weld joint strength and measurements of the 4 K fracture toughness of magnesium-chromium steel weldments and electroodes. In the area of non-metallics, a standardized test specimen was devised to aid in screening radiation-resistant composites for magnet insulation. Mechanical properties of concrete mortar and polyurethane foam at 4 K are reported.

Deformation Behavior of Ultra-Strong and Ductile Mg-Gd-Y-Zn-Zr Alloy with Bimodal Microstructure

NASA Astrophysics Data System (ADS)

Xu, C.; Fan, G. H.; Nakata, T.; Liang, X.; Chi, Y. Q.; Qiao, X. G.; Cao, G. J.; Zhang, T. T.; Huang, M.; Miao, K. S.; Zheng, M. Y.; Kamado, S.; Xie, H. L.

2018-02-01

An ultra-strong and ductile Mg-8.2Gd-3.8Y-1Zn-0.4Zr (wt pct) alloy was developed by using hot extrusion to modify the microstructure via forced-air cooling and an artificial aging treatment. A superior strength-ductility balance was obtained that had a tensile yield strength of 466 MPa and an elongation to failure of 14.5 pct. The local strain evolution during the in situ testing of the ultra-strong and ductile alloy was quantitatively analyzed with high-resolution electron backscattered diffraction and digital image correlation. The fracture behavior during the tensile test was characterized by synchrotron X-ray tomography along with SEM and STEM observations. The alloy showed a bimodal microstructure, consisting of dynamically recrystallized (DRXed) grains with random orientations and elongated hot-worked grains with < { 10{\\bar{1}}0} > parallel to the extrusion direction. The DRXed grains were deformed by the basal <;a> slip and the hot-worked grains were deformed by the prismatic slip dominantly. The strain evolution analysis indicated that the multilayered structure relaxed the strain localization via strain transfer from the DRXed to the hot-worked regions, which led to the high ductility of the alloy. Precipitation of the γ' on basal planes and the β' phases on the prismatic planes of the α-Mg generated closed volumes, which enhanced the strength by pinning dislocations effectively, and contributed to the high ductility by impeding the propagation of micro-cracks inside the grains. The deformation incompatibility between the hot-worked grains and the arched block-shaped long-period stacking ordered (LPSO) phases induced the crack initiation and propagation, which fractured the alloy.

Influence of Tension-Compression Asymmetry on the Mechanical Behavior of AZ31B Magnesium Alloy Sheets in Bending

NASA Astrophysics Data System (ADS)

Zhou, Ping; Beeh, Elmar; Friedrich, Horst E.

2016-03-01

Magnesium alloys are promising materials for lightweight design in the automotive industry due to their high strength-to-mass ratio. This study aims to study the influence of tension-compression asymmetry on the radius of curvature and energy absorption capacity of AZ31B-O magnesium alloy sheets in bending. The mechanical properties were characterized using tension, compression, and three-point bending tests. The material exhibits significant tension-compression asymmetry in terms of strength and strain hardening rate due to extension twinning in compression. The compressive yield strength is much lower than the tensile yield strength, while the strain hardening rate is much higher in compression. Furthermore, the tension-compression asymmetry in terms of r value (Lankford value) was also observed. The r value in tension is much higher than that in compression. The bending results indicate that the AZ31B-O sheet can outperform steel and aluminum sheets in terms of specific energy absorption in bending mainly due to its low density. In addition, the AZ31B-O sheet was deformed with a larger radius of curvature than the steel and aluminum sheets, which brings a benefit to energy absorption capacity. Finally, finite element simulation for three-point bending was performed using LS-DYNA and the results confirmed that the larger radius of curvature of a magnesium specimen is mainly attributed to the high strain hardening rate in compression.

Evaluation of a Diffusion/Trapping Model for Hydrogen Ingress in High Strength Alloys

DTIC Science & Technology

1989-11-17

been extended to a group of precipitation -hardened nickel-containing alloys (Inconel 718, Incoloy 925, and 18Ni maraging steel ) and titanium (pure and...possibly Ni 3Ti or FeTi, precipitated during age hardening of the maraging steel . 2 1 The energy of hydrogen interaction with the interrmetallic particles...102, Part 1 (1972); Ref 105 in "The Stress Corrosion and Hydrogen Embrittlement Behavior of Maraging Steels ", Proceedings of the Conference on the

Effects of gap width on droplet transfer behavior in ultra-narrow gap laser welding of high strength aluminum alloys

NASA Astrophysics Data System (ADS)

Song, Chaoqun; Dong, Shiyun; Yan, Shixing; He, Jiawu; Xu, Binshi; He, Peng

2017-10-01

Ultra-narrow gap laser welding is a novel method for thick high strength aluminum alloy plate for its lower heat input, less deformation and higher efficiency. To obtain a perfect welding quality, it is vital to control the more complex droplet transfer behavior under the influence of ultra-narrow gap groove. This paper reports the effects of gap width of groove on droplet transfer behavior in ultra-narrow gap laser welding of 7A52 aluminum alloy plates by a high speed camera, using an ER 5356 filler wire. The results showed that the gap width had directly effects on droplet transfer mode and droplet shape. The droplet transfer modes were, in order, both-sidewall transfer, single-sidewall transfer, globular droplet transfer and bridging transfer, with different droplet shape and transition period, as the gap width increased from 2 mm to 3.5mm. The effect of gap width on lack of fusion was also studied to analyze the cause for lack of fusion at the bottom and on the sidewall of groove. Finally, with a 2.5 mm U-type parallel groove, a single-pass joint with no lack of fusion and other macro welding defects was successfully obtained in a single-sidewall transfer mode.

Controlled rolling process for dual phase steels and application to rod, wire, sheet and other shapes

DOEpatents

Thomas, G.; Ahn, J.H.; Kim, N.J.

1986-10-28

An improved, energy efficient, hot rolling method for direct production of cold formable dual-phase steel is provided. The steel is heated to completely austenitize it and then continuously hot rolled and cooled down into the ferrite-austenite two phase region to a temperature which is just below the effective Ar[sub 3] temperature. The hot rolled steel is then rapidly quenched to provide an alloy containing strong, tough lath martensite (fibers) in a ductile soft ferrite matrix. The method is particularly useful for providing rods in which form the alloy is capable of being drawn into high strength wire or the like in a cold drawing operation without any intermediate annealing or patenting, and has excellent strength, ductility and fatigue characteristics. 3 figs.

Controlled rolling process for dual phase steels and application to rod, wire, sheet and other shapes

DOEpatents

Thomas, Gareth; Ahn, Jae-Hwan; Kim, Nack-Joon

1986-01-01

An improved, energy efficient, hot rolling method for direct production of cold formable dual-phase steel is provided. The steel is heated to completely austenitize it and then continuously hot rolled and cooled down into the ferrite-austenite two phase region to a temperature which is just below the effective Ar.sub.3 temperature. The hot rolled steel is then rapidly quenched to provide an alloy containing strong, tough lath martensite (fibers) in a ductile soft ferrite matrix. The method is particularly useful for providing rods in which form the alloy is capable of being drawn into high strength wire or the like in a cold drawing operation without any intermediate annealing or patenting, and has excellent strength, ductility and fatigue characteristics.

Improved the microstructures and properties of M3:2 high-speed steel by spray forming and niobium alloying

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lu, L.; Hou, L.G., E-mail: lghou@skl.ustb.edu.cn; Zhang, J.X.

The microstructures and properties of spray formed (SF) high-speed steels (HSSs) with or without niobium (Nb) addition were studied. Particular emphasis was placed on the effect of Nb on the solidification microstructures, decomposition of M{sub 2}C carbides, thermal stability and mechanical properties. The results show that spray forming can refine the cell size of eutectic carbides due to the rapid cooling effect during atomization. With Nb addition, further refinement of the eutectic carbides and primary austenite grains are obtained. Moreover, the Nb addition can accelerate the decomposition of M{sub 2}C carbides and increase the thermal stability of high-speed steel, andmore » also can improve the hardness and bending strength with slightly decrease the impact toughness. The high-speed steel made by spray forming and Nb alloying can give a better tool performance compared with powder metallurgy M3:2 and commercial AISI M2 high-speed steels. - Highlights: • Spray forming can effectively refine the microstructure of M3:2 steel. • Niobium accelerates the decomposition of M{sub 2}C carbides. • Niobium increases the hardness and bending strength of spray formed M3:2 steel. • Spray-formed niobium-containing M3:2 steel has the best tool performance.« less

Development of new generation reduced activation ferritic-martenstic steels for advanced fusion reactors

DOE PAGES

Tan, Lizhen; Snead, Lance Lewis; Katoh, Yutai

2016-05-26

International development of reduced activation ferritic-martensitic (RAFM) steels has focused on 9 wt percentage Cr, which primarily contain M 23C 6 (M = Cr-rich) and small amounts of MX (M = Ta/V, X = C/N) precipitates, not adequate to maintain strength and creep resistance above ~500 °C. To enable applications at higher temperatures for better thermal efficiency of fusion reactors, computational alloy thermodynamics coupled with strength modeling have been employed to explore a new generation RAFM steels. The new alloys are designed to significantly increase the amount of MX nanoprecipitates, which are manufacturable through standard and scalable industrial steelmaking methods.more » Preliminary experimental results of the developed new alloys demonstrated noticeably increased amount of MX, favoring significantly improved strength, creep resistance, and Charpy impact toughness as compared to current RAFM steels. Furthermore, the strength and creep resistance were comparable or approaching to the lower bound of, but impact toughness was noticeably superior to 9–20Cr oxide dispersion-strengthened ferritic alloys.« less

The improvement of cryogenic mechanical properties of Fe-12 Mn and Fe-8 Mn alloy steels through thermal/mechanical treatments

NASA Technical Reports Server (NTRS)

Hwang, S. K.; Morris, J. W., Jr.

1979-01-01

An investigation has been made to improve the low temperature mechanical properties of Fe-8Mn and Fe-12Mn-0.2 Ti alloy steels. A reversion annealing heat treatment in the two-phase (alpha + gamma) region following cold working has been identified as an effective treatment. In an Fe-12Mn-0.2Ti alloy a promising combination of low temperature (-196 C) fracture toughness and yield strength was obtained by this method. The improvement of properties was attributed to the refinement of grain size and to the introduction of a uniform distribution of retained austenite (gamma). It was also shown that an Fe-8Mn steel could be grain-refined by a purely thermal treatment because of its dislocated alpha-prime martensitic structure and absence of epsilon martensite. As a result, a significant reduction of ductile to brittle transition temperature was obtained.

High-temperature steam oxidation testing of select advanced replacement alloys for potential core internals

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tan, Lizhen; Pint, Bruce A.

2017-05-19

Coupons from a total of fourteen commercial and custom fabricated alloys were exposed to 1 bar full steam with ~10 ppb oxygen content at 600 and 650°C. The coupons were weighed at 500-h intervals with a total exposure time of 5,000 h. The fourteen alloys are candidate alloys selected under the ARRM program, which include three ferritic steels (Grade 92, 439, and 14YWT), three austenitic stainless steels (316L, 310, and 800), seven Ni-base superalloys (X750, 725, C22, 690, 625, 625 direct-aging, and 625- plus), and one Zr-alloy (Zr–2.5Nb). Among the alloys, 316L and X750 are served as reference alloys formore » low- and high-strength alloys, respectively. The candidate Ni-base superalloy 718 was procured too late to be included in the tests. The corrosion rates of the candidate alloys can be approximately interpreted by their Cr, Ni and Fe content. The corrosion rate was significantly reduced with increasing Cr content and when Ni content is above ~15 wt%, but not much further reduced when Fe content is less than ~55 wt%. Simplified thermodynamics analyses of the alloy oxidation provided reasonable indications for the constituents of oxide scales formed on the alloys and explanations for the porosity and exfoliation phenomena because of the nature of specific types of oxides.« less

Latest Development and Application of High Strength and Heavy Gauge Pipeline Steel in China

NASA Astrophysics Data System (ADS)

Yongqing, Zhang; Aimin, Guo; Chengjia, Shang; Qingyou, Liu; Gray, J. Malcolm; Barbaro, Frank

Over the past twenty years, significant advances have been made in the field of microalloying and associated application, among which one of the most successful application cases is HTP practice for heavy gauge, high strength pipeline steels. Combined the strengthening effects of TMCP and retardation effects of austenite recrystallization with increasing Nb in austenite region, HTP conception with low carbon and high niobium alloy design has been successfully applied to develop X80 coil with a thickness of 18.4mm used for China's Second West-East pipeline. During this process, big efforts were made to further develop and enrich the application of microalloying technology, and at the same time the strengthening effects of Nb have been completely unfolded and fully utilized with improved metallurgical quality and quantitative analysis of microstructure. In this paper, the existing status and strengthening effect of Nb during reheating, rolling, cooling and welding have been analyzed and characterized based on mass production samples and laboratory analysis. As confirmed, grain refinement remains the most basic strengthening measure to reduce the microstructure gradient along the thickness, which in turn enlarges the processing window to improve upon low temperature toughness, and finally make it possible to develop heavy gauge, high strength pipeline steels with more challenging fracture toughness requirements.

An assessment of alternative diesel fuels: microbiological contamination and corrosion under storage conditions.

PubMed

Lee, Jason S; Ray, Richard I; Little, Brenda J

2010-08-01

Experiments were designed to evaluate the nature and extent of microbial contamination and the potential for microbiologically influenced corrosion of alloys exposed in a conventional high sulfur diesel (L100) and alternative fuels, including 100% biodiesel (B100), ultra-low sulfur diesel (ULSD) and blends of ULSD and B100 (B5 and B20). In experiments with additions of distilled water, all fuels supported biofilm formation. Changes in the water pH did not correlate with observations related to corrosion. In all exposures, aluminum 5052 was susceptible to pitting while stainless steel 304L exhibited passive behavior. Carbon steel exhibited uniform corrosion in ULSD and L100, and passive behavior in B5, B20, and B100.

Surface Modification of Micro-Alloyed High-Strength Low-Alloy Steel by Controlled TIG Arcing Process

NASA Astrophysics Data System (ADS)

Ghosh, P. K.; Kumar, Ravindra

2015-02-01

Surface modification of micro-alloyed HSLA steel plate has been carried out by autogenous conventional and pulse current tungsten inert gas arcing (TIGA) processes at different welding parameters while the energy input was kept constant. At a given energy input the influence of pulse parameters on the characteristics of surface modification has been studied in case of employing single and multi-run procedure. The role of pulse parameters has been studied by considering their summarized influence defined by a factor Φ. The variation in Φ and pulse frequency has been found to significantly affect the thermal behavior of fusion and accordingly the width and penetration of the modified region along with its microstructure, hardness and wear characteristics. It is found that pulsed TIGA is relatively more advantageous over the conventional TIGA process, as it leads to higher hardness, improved wear resistance, and a better control over surface characteristics.

Microstructure of warm rolling and pearlitic transformation of ultrafine-grained GCr15 steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sun, Jun-Jie; Lian, Fu-Liang; Liu, Hong-Ji

2014-09-15

Pearlitic transformation mechanisms have been investigated in ultra-fine grained GCr15 steel. The ultrafine-grained steel, whose grain size was less than 1 μm, was prepared by thermo-mechanical treatment at 873 K and then annealing at 923 K for 2 h. Pearlitic transformation was conducted by reheating the ultra-fine grained samples at 1073 K and 1123 K for different periods of time and then cooling in air. Scanning electron microscope observation shows that normal lamellar pearlite, instead of granular cementite and ferrite, cannot be formed when the grain size is approximately less than 4(± 0.6) μm, which yields a critical grain sizemore » for normal lamellar pearlitic transformations in this chromium alloyed steel. The result confirms that grain size has a great influence on pearlitic transformation by increasing the diffusion rate of carbon atoms in the ultra-fine grained steel, and the addition of chromium element doesn't change this pearlitic phase transformation rule. Meanwhile, the grain growth rate is reduced by chromium alloying, which is beneficial to form fine grains during austenitizing, thus it facilitating pearlitic transformation by divorced eutectoid transformation. Moreover, chromium element can form a relatively high gradient in the frontier of the undissolved carbide, which promotes carbide formation in the frontier of the undissolved carbide, i.e., chromium promotes divorced eutectoid transformation. - Highlights: • Ultrafine-grained GCr15 steel was obtained by warm rolling and annealing technology. • Reduction of grain size makes pearlite morphology from lamellar to granular. • Adding Cr does not change normal pearlitic phase transformation rule in UFG steel. • Cr carbide resists grain growth and facilitates pearlitic transformation by DET.« less

Microstructure and Mechanical Properties of High Copper HSLA-100 Steel in 2-inch Plate Form

DTIC Science & Technology

1992-06-01

2. HSLA-100 Steel Continuous Cooling Transformation Diagram [Ref. 13:p. 262] One of the most desirable characteristics of the low -carbon, copper ...none V mild v.strong v. strong V. strong moderate The use of copper as an alloying element in low carbon HSLA steel has resulted in the following...HY-130 steel . In research presently being done, it has been determined that the high copper alloy has a highly dislocated martensitic /bainitic

Ultra-high temperature isothermal furnace liners (IFLS) for copper freeze point cells

NASA Astrophysics Data System (ADS)

Dussinger, P. M.; Tavener, J. P.

2013-09-01

Primary Laboratories use large fixed-point cells in deep calibration furnaces utilizing heat pipes to achieve temperature uniformity. This combination of furnace, heat pipe, and cell gives the smallest of uncertainties. The heat pipe, also known as an isothermal furnace liner (IFL), has typically been manufactured with Alloy 600/601 as the envelope material since the introduction of high temperature IFLs over 40 years ago. Alloy 600/601 is a widely available high temperature material, which is compatible with Cesium, Potassium, and Sodium and has adequate oxidation resistance and reasonable high temperature strength. Advanced Cooling Technologies, Inc. (ACT) Alloy 600/Sodium IFLs are rated to 1100°C for approximately 1000 hours of operation (based on creep strength). Laboratories interested in performing calibrations and studies around the copper freezing point (1084.62°C) were frustrated by the 1000 hours at 1100°C limitation and the fact that expensive freeze-point cells were getting stuck and/or crushed inside the IFL. Because of this growing frustration/need, ACT developed an Ultra High Temperature IFL to take advantage of the exceptional high temperature strength properties of Haynes 230.

Intercritical heat treatments in ductile iron and steel

NASA Astrophysics Data System (ADS)

Aristizabal, Ricardo E.

Materials such as dual phase (DP) steels, transformation induced plasticity (TRIP) steels and dual phase ductile irons are produced by intercritical heat treatments. These materials can provide significant weight savings in the automotive industry. The goal of this dissertation is to study intercritical heat treatments in ductile iron and steel to optimize the production parameters. Three different aspects were addressed. First, common steels were intercritically austenitized and austempered (intercritically austempered) under a variety conditions. The results showed that common grade steels that were intercritically austempered exhibited tensile properties in the same range as DP and TRIP steels. The second study consisted of determining the effect of heat treatment conditions on the tensile properties of intercritically austenitized, quenched and tempered ductile iron (IAQ&TDI). The results showed that (1) ultimate tensile strength (UTS) and yield strength (YS) were determined by the volume fraction of martensite, (2) tempering improved the elongation 1.7-2.5 times with only a slight decrease in strength, (3) the carbon in austenite formed during the intercritical heat treatment of ductile iron with a ferritic-pearlitic matrix came from the carbon available in the matrix and that carbon diffusion from the graphite nodules was restricted, and (4) limited segregation of substitutional elements occurred during intercritical austenitizing. Finally, intercritically austempered ductile iron (IADI) alloyed with different amounts of manganese and nickel was produced. Tensile properties and microstructure were determined. Also, the stability of the austenite during deformation and the lattice strains of the ferrite and the austenite phases were determined using x-ray diffraction (XRD) and neutron diffraction. The results indicated that: 1) high manganese concentrations produced materials with large blocky, low carbon austenite particles at the intercellular boundaries which decreased the elongation of the materials and transformed to martensite during deformation at low strains. 2) Nickel and nickel-manganese alloys formed a combination of blocky and plate-like austenite particles, which were more stable during deformation and either transformed to martensite after yielding or did not transform at all.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kamiya, Junichiro, E-mail: kamiya.junichiro@jaea.go.jp; Hikichi, Yusuke; Kinsho, Michikazu

For the vacuum systems of high-intensity beam accelerators, low radioactivation materials with good vacuum characteristics and high mechanical strength are required. The titanium alloy Ti-6Al-4V was investigated as a potential low activation vacuum material with high mechanical strength for the fabrication of vacuum components, particularly the flanges of beam pipes, in the J-PARC 3 GeV synchrotron. The dose rate of Ti-6Al-4V when irradiated by a 400 MeV proton was observed to decrease more rapidly than that of stainless steel. Furthermore, the generated radioactive isotopes were nuclides with relatively short half-lives. The outgassing rate per unit area of Ti-6Al-4V was approximately 10{sup −8 }Pamore » m{sup 3}/s m{sup 2} after pumping for 100 h, which is the same as the typical value for stainless steel. Additionally, the hydrogen concentration in bulk Ti-6Al-4V was reduced to approximately 1 ppm by vacuum firing at 700 °C for 9 h; the mechanical strength was not reduced by this process. These results indicate that Ti-6Al-4V is a good candidate for use as a low activation vacuum material with high mechanical strength.« less

Design of Fully Austenitic Medium Manganese Steels

NASA Astrophysics Data System (ADS)

Luan, G.; Volkova, O.; Mola, J.

2018-06-01

Due to their higher ferrite potential compared to high Mn twinning-induced plasticity (TWIP) steels, medium Mn steels usually exhibit austenitic-ferritic microstructures, which makes them suitable for third-generation advanced high-strength steel applications. Nevertheless, the strain hardening characteristics of medium Mn steels are inferior to those of fully austenitic high Mn steels. The present work introduces alloy design strategies to obtain fully austenitic medium Mn steels capable of the TWIP effect. To achieve a fully austenitic microstructure, the martensite start temperature is reduced by raising the C concentration to above 1 mass-%, which in turn facilitates the formation of cementite. The formation of cementite during cooling from austenitization temperature is counteracted by alloying with Al. Microstructural examination of slowly-cooled Fe‑Mn‑Al‑C and Fe‑Mn‑C steels indicated that Al changes the morphology of intergranular cementite from plate-shaped to equiaxed.

Castable Amorphous Metal Mirrors and Mirror Assemblies

NASA Technical Reports Server (NTRS)

Hofmann, Douglas C.; Davis, Gregory L.; Agnes, Gregory S.; Shapiro, Andrew A.

2013-01-01

A revolutionary way to produce a mirror and mirror assembly is to cast the entire part at once from a metal alloy that combines all of the desired features into the final part: optical smoothness, curvature, flexures, tabs, isogrids, low CTE, and toughness. In this work, it has been demonstrated that castable mirrors are possible using bulk metallic glasses (BMGs, also called amorphous metals) and BMG matrix composites (BMGMCs). These novel alloys have all of the desired mechanical and thermal properties to fabricate an entire mirror assembly without machining, bonding, brazing, welding, or epoxy. BMGs are multi-component metal alloys that have been cooled in such a manner as to avoid crystallization leading to an amorphous (non-crystalline) microstructure. This lack of crystal structure and the fact that these alloys are glasses, leads to a wide assortment of mechanical and thermal properties that are unlike those observed in crystalline metals. Among these are high yield strength, carbide-like hardness, low melting temperatures (making them castable like aluminum), a thermoplastic processing region (for improving smoothness), low stiffness, high strength-to-weight ratios, relatively low CTE, density similar to titanium alloys, high elasticity and ultra-smooth cast parts (as low as 0.2-nm surface roughness has been demonstrated in cast BMGs). BMGMCs are composite alloys that consist of a BMG matrix with crystalline dendrites embedded throughout. BMGMCs are used to overcome the typically brittle failure observed in monolithic BMGs by adding a soft phase that arrests the formation of cracks in the BMG matrix. In some cases, BMGMCs offer superior castability, toughness, and fatigue resistance, if not as good a surface finish as BMGs. This work has demonstrated that BMGs and BMGMCs can be cast into prototype mirrors and mirror assemblies without difficulty.

Experimental and theoretical research of the interaction between high-strength supercavitation impactors and monolithic barriers in water

NASA Astrophysics Data System (ADS)

Ishchenko, A. N.; Afanas'eva, S. A.; Burkin, V. V.; Diachkovskii, A. S.; Zykova, A. I.; Khabibullin, M. V.; Chupashev, A. V.; Yugov, N. T.

2017-09-01

The article describes experimental and theoretical research of the interaction between supercavitating impactors and underwater aluminum alloy and steel barriers. Strong alloys are used for making impactors. An experimental research technique based on a high-velocity hydro-ballistic complex was developed. Mathematical simulation of the collision the impactor and barrier is based on the continuum mechanics inclusive of the deformation and destruction of interacting bodies. Calculated and experimental data on the ultimate penetration thickness of barriers made of aluminum alloy D16T and steel for the developed supercavitating impactor are obtained.

Mechanical, Corrosion, and Fatigue Properties of 15-5 PH, Inconel 718, and Rene 41 Weldments

DTIC Science & Technology

1975-05-01

TUCUMvARI (PGH 2) It was originally developed for high - temperature use by Armco Steel Corporation. 2 High strength is obtained by the precipitation...Rene 41 was developed by General Electric Company as a high - temperature turbine alloy. It is a nickel-base alloy, high in chromium, cobalt, and... molybdenum . Its high strength comes from the precipitation of a gamma-prime phase consisting of Ni3AI and Ni5Ti, and from the solid solution effects of

Corrosion Characterization in Nickel Plated 110 ksi Low Alloy Steel and Incoloy 925: An Experimental Case Study

NASA Astrophysics Data System (ADS)

Thomas, Kiran; Vincent, S.; Barbadikar, Dipika; Kumar, Shresh; Anwar, Rebin; Fernandes, Nevil

2018-04-01

Incoloy 925 is an age hardenable Nickel-Iron-Chromium alloy with the addition of Molybdenum, Copper, Titanium and Aluminium used in many applications in oil and gas industry. Nickel alloys are preferred mostly in corrosive environments where there is high concentration of H2S, CO2, chlorides and free Sulphur as sufficient nickel content provides protection against chloride-ion stress-corrosion cracking. But unfortunately, Nickel alloys are very expensive. Plating an alloy steel part with nickel would cost much lesser than a part make of nickel alloy for large quantities. A brief study will be carried out to compare the performance of nickel plated alloy steel with that of an Incoloy 925 part by conducting corrosion tests. Tests will be carried out using different coating thicknesses of Nickel on low alloy steel in 0.1 M NaCl solution and results will be verified. From the test results we can confirm that Nickel plated low alloy steel is found to exhibit fairly good corrosion in comparison with Incoloy 925 and thus can be an excellent candidate to replace Incoloy materials.

A review on nickel-free nitrogen containing austenitic stainless steels for biomedical applications.

PubMed

Talha, Mohd; Behera, C K; Sinha, O P

2013-10-01

The field of biomaterials has become a vital area, as these materials can enhance the quality and longevity of human life. Metallic materials are often used as biomaterials to replace structural components of the human body. Stainless steels, cobalt-chromium alloys, commercially pure titanium and its alloys are typical metallic biomaterials that are being used for implant devices. Stainless steels have been widely used as biomaterials because of their very low cost as compared to other metallic materials, good mechanical and corrosion resistant properties and adequate biocompatibility. However, the adverse effects of nickel ions being released into the human body have promoted the development of "nickel-free nitrogen containing austenitic stainless steels" for medical applications. Nitrogen not only replaces nickel for austenitic structure stability but also much improves steel properties. Here we review the harmful effects associated with nickel and emphatically the advantages of nitrogen in stainless steel, as well as the development of nickel-free nitrogen containing stainless steels for medical applications. By combining the benefits of stable austenitic structure, high strength, better corrosion and wear resistance and superior biocompatibility in comparison to the currently used austenitic stainless steel (e.g. 316L), the newly developed nickel-free high nitrogen austenitic stainless steel is a reliable substitute for the conventionally used medical stainless steels. Copyright © 2013 Elsevier B.V. All rights reserved.

Ballistic Analysis of New Military Grade Magnesium Alloys for Armor Applications

NASA Astrophysics Data System (ADS)

Jones, Tyrone L.; Kondoh, Katsuyoshi

Since 2006, the U.S. Army has been evaluating magnesium (Mg) alloys for ballistic structural applications. While Mg-alloys have been used in military structural applications since WWII, very little research has been done to improve its mediocre ballistic performance. The Army's need for ultra-lightweight armor systems has led to research and development of high strength, high ductility Mg-alloys. The U.S. Army Research Laboratory contracted through International Technology Center-Pacific Contract Number FA-5209-09-P-0158 with the Joining and Welding Research Instituteof Osaka University to develop the next generation of high strength, high ductility Mg-alloys using a novel Spinning Water Atomization Process for rapid solidification. New alloys AMX602 and ZAXE1711 in extruded bar form were characterized for microstructure, mechanical, and ballistic response. Significant increases in ballistic performance were evident when compared to the baseline alloy AZ31B.

Design of Fatigue Resistant Heusler-strengthened PdTi-based Shape Memory Alloys for Biomedical Applications

NASA Astrophysics Data System (ADS)

Frankel, Dana J.

The development of non-surgical transcatheter aortic valve implantation (TAVI) techniques, which utilize collapsible artificial heart valves with shape memory alloy (SMA)-based frames, pushes performance requirements for biomedical SMAs beyond those for well-established vascular stent applications. Fatigue life for these devices must extend into the ultra-high cycle fatigue (UHCF) regime (>600M cycles) with zero probability of failure predicted at applied strain levels. High rates of Ni-hypersensitivity raise biocompatibility concerns, driving the development of low-Ni and Ni-free SMAs. This work focuses on the development of biocompatible, precipitation-strengthened, fatigue-resistant PdTi-based SMAs for biomedical applications. Functional and structural fatigue are both manifestations of cyclic instability resulting in accumulation of slip and eventual structural damage. While functional fatigue is easily experimentally evaluated, structural fatigue is more difficult to measure without the proper equipment. Therefore, in this work a theoretical approach using a model well validated in steels is utilized to investigate structural fatigue behavior in NiTi in the UHCF regime, while low cycle functional fatigue is evaluated in order to monitor the core phenomena of the cyclic instability. Results from fatigue simulations modeling crack nucleation at non-metallic inclusions in commercial NiTi underscore the importance of increasing yield strength for UHCF performance. Controlled precipitation of nanoscale, low-misfit, L21 Heusler aluminides can provide effective strengthening. Phase relations, precipitation kinetics, transformation temperature, transformation strain, cyclic stability, and mechanical properties are characterized in both Ni-free (Pd,Fe)(Ti,Al) and low-Ni high-strength "hybrid" (Pd,Ni)(Ti,Zr,Al) systems. Atom probe tomography is employed to measure phase compositions and particle sizes used to calibrate LSW models for coarsening kinetics and Gibbs-Thompson models for composition trajectories for systems under evolving unstable equilibrium. Mechanical and thermal cyclic stability are investigated using compression testing and differential scanning calorimetry. Mechanical properties are characterized using room temperature and high temperature Vickers microhardness as well as nanoindentation. A superelastic Ni-free (Pd,Fe)(Ti,Al) alloy with near-ambient transformation temperatures, low hysteresis, a highly stable cyclic response, and reversible transformation strains of 3.2% was designed. Due to Pd softening, the addition of Zr is considered to improve strength in a low-Ni "hybrid" (Pd,Ni)(Ti,Zr,Al) alloy. Aging studies at 600°C result in unusually fast coarsening kinetics, while low-temperature aging studies at 500-530°C reveal the presence of a Zr-rich phase in association with the matrix and Heusler phase. A strengthening study on a nontransforming hybrid prototype shows lower than expected precipitation strengthening at 600°C but significant strengthening when aged at 500°C due to the Zr-rich phase. Transformation temperatures, transformation strain, and cyclic stability are characterized in a set of transforming hybrid prototypes.

Corrosion fatigue of high strength fastener materials in seawater. Final report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tipton, D.G.

1983-12-01

Environmental effects can significantly reduce the fatigue life of metals. As such, corrosion fatigue is a major concern in the engineering application of high strength fasteners in marine environments. The corrosion fatigue failure of an AISI 41L40 high strength steel blade-to-hub attachment bolt at the MOD-0A 200 kW wind turbine generator in Oahu, Hawaii prompted the current test program. Tests were undertaken to confirm the dramatic reduction of fatigue strength of AISI 41L40 in marine environments and to obtain similar corrosion fatigue data for candidate replacement materials. AISI 41L40, AISI 4140, PH 13-8Mo stainless steel, alloy 718 and alloy MP-35Nmore » were tested in axial fatigue at a frequency of 20 Hz in dry air and natural seawater. The fatigue data were fitted by regression equations to allow determination of fatigue strength for a given number of cycles to failure.« less

Validation of the role of bulk charging of hydrogen in the corrosion fatigue cracking of a low alloy steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Griffiths, A.J.; Hutchings, R.B.; Turnbull, A.

1993-09-01

The enhanced corrosion fatigue crack growth rates of low alloy steels cathodically protected in marine environments results from absorbed hydrogen atoms. Hydrogen atoms are generated at the crack tip, crack walls and the external surface of the specimen (bulk charging). In previous work, Turnbull and Saenz de Santa Maria developed a model to predict the rate of generation of hydrogen atoms at the tips of fatigue cracks for steels cathodically polarized in marine environments. The main prediction from this work was that the external surface of the specimen can be the dominant source of hydrogen atoms at potentials more negativemore » than about [minus]900 mV (SCE), at a cyclic frequency of 0.1 Hz and a stress ratio of 0.5. The relative importance of bulk charging depends on the specific test conditions and is influenced by the applied potential, bulk chemistry, cyclic frequency, specimen thickness, temperature and use of coatings. Since laboratory test times are usually short in relation to the time required for hydrogen transport measured crack growth rates may be lower than those occurring in practice, for which there is sufficient time for full hydrogen charging. The purpose of this study is to verify experimentally the importance of bulk charging. Since the sensitivity of cracking to variations in hydrogen concentration will be material dependent a high strength steel was selected in this initial study because of its sensitivity to hydrogen. This will enable validation of the basic premise that bulk charging can be important, prior to more extensive studies using lower strength alloys.« less

Influence of Filler Alloy Composition and Process Parameters on the Intermetallic Layer Thickness in Single-Sided Cold Metal Transfer Welding of Aluminum-Steel Blanks

NASA Astrophysics Data System (ADS)

Silvayeh, Zahra; Vallant, Rudolf; Sommitsch, Christof; Götzinger, Bruno; Karner, Werner; Hartmann, Matthias

2017-11-01

Hybrid components made of aluminum alloys and high-strength steels are typically used in automotive lightweight applications. Dissimilar joining of these materials is quite challenging; however, it is mandatory in order to produce multimaterial car body structures. Since especially welding of tailored blanks is of utmost interest, single-sided Cold Metal Transfer butt welding of thin sheets of aluminum alloy EN AW 6014 T4 and galvanized dual-phase steel HCT 450 X + ZE 75/75 was experimentally investigated in this study. The influence of different filler alloy compositions and welding process parameters on the thickness of the intermetallic layer, which forms between the weld seam and the steel sheet, was studied. The microstructures of the weld seam and of the intermetallic layer were characterized using conventional optical light microscopy and scanning electron microscopy. The results reveal that increasing the heat input and decreasing the cooling intensity tend to increase the layer thickness. The silicon content of the filler alloy has the strongest influence on the thickness of the intermetallic layer, whereas the magnesium and scandium contents of the filler alloy influence the cracking tendency. The layer thickness is not uniform and shows spatial variations along the bonding interface. The thinnest intermetallic layer (mean thickness < 4 µm) is obtained using the silicon-rich filler Al-3Si-1Mn, but the layer is more than twice as thick when different low-silicon fillers are used.

Irradiation creep of dispersion strengthened copper alloy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pokrovsky, A.S.; Barabash, V.R.; Fabritsiev, S.A.

1997-04-01

Dispersion strengthened copper alloys are under consideration as reference materials for the ITER plasma facing components. Irradiation creep is one of the parameters which must be assessed because of its importance for the lifetime prediction of these components. In this study the irradiation creep of a dispersion strengthened copper (DS) alloy has been investigated. The alloy selected for evaluation, MAGT-0.2, which contains 0.2 wt.% Al{sub 2}O{sub 3}, is very similar to the GlidCop{trademark} alloy referred to as Al20. Irradiation creep was investigated using HE pressurized tubes. The tubes were machined from rod stock, then stainless steel caps were brazed ontomore » the end of each tube. The creep specimens were pressurized by use of ultra-pure He and the stainless steel caps subsequently sealed by laser welding. These specimens were irradiated in reactor water in the core position of the SM-2 reactors to a fluence level of 4.5-7.1 x 10{sup 21} n/cm{sup 2} (E>0.1 MeV), which corresponds to {approx}3-5 dpa. The irradiation temperature ranged from 60-90{degrees}C, which yielded calculated hoop stresses from 39-117 MPa. A mechanical micrometer system was used to measure the outer diameter of the specimens before and after irradiation, with an accuracy of {+-}0.001 mm. The irradiation creep was calculated based on the change in the diameter. Comparison of pre- and post-irradiation diameter measurements indicates that irradiation induced creep is indeed observed in this alloy at low temperatures, with a creep rate as high as {approx}2 x 10{sup {minus}9}s{sup {minus}1}. These results are compared with available data for irradiation creep for stainless steels, pure copper, and for thermal creep of copper alloys.« less

Impact of high-pressure coolant supply on chip formation in milling

NASA Astrophysics Data System (ADS)

Klocke, F.; Döbbeler, B.; Lakner, T.

2017-10-01

Machining of titanium alloys is considered as difficult, because of their high temperature strength, low thermal conductivity and low E-modulus, which contributes to high mechanical loads and high temperatures in the contact zone between tool and workpiece. The generated heat in the cutting zone can be dissipated only in a low extent. When cutting steel materials, up to 75% of the process heat is transported away by the chips, contrary to only 25% when machining titanium alloys. As a result, the cutting tool heats up, which leads to high tool wear. Therefore, machining of titanium alloys is only possible with relatively low cutting speeds. This leads to low levels of productivity for milling processes with titanium alloys. One way to increase productivity is to use more cutting edges in tools with the same diameter. However, the limiting factor of adding more cutting edges to a milling tool is the minimum size of the chip spaces, which are sufficient for a stable chip evacuation. This paper presents experimental results on the chip formation and chip size influenced by high-pressure coolant supply, which can lead to smaller chips and to smaller sizes of the chip spaces, respectively. Both influences, the pressure of the supplied coolant and the volumetric flow rate were individually examined. Alpha-beta annealed titanium TiAl6V4 was examined in relation to the reference material quenched and tempered steel 42CrMo4+QT (AISI 4140+QT). The work shows that with proper chip control due to high-pressure coolant supply in milling, the number of cutting edges on the same diameter tool can be increased, which leads to improved productivity.

TAZ-8A Alloy Increases The Thermal Endurance Of Steel

NASA Technical Reports Server (NTRS)

Waters, William J.

1990-01-01

TAZ-8A exhibits high strength at temperatures as high as 1,400 degrees F (760 degrees C) and resistance to oxidation; also exhibits excellent cyclic shock resistance between 600 and 2,000 degrees F (316 and 1,093 degrees C) and superplasticity at 1,800 degrees F (982 degrees C). Converts into fine powder and then flame-, plasma-, arc-, or wire-sprayed onto inexpensive steel substrate. Surface treatment with this alloy prolongs service life and reduces costs.

Effects of microalloying on hot-rolled and cold-rolled Q&P steels

NASA Astrophysics Data System (ADS)

Azevedo de Araujo, Ana Luiza

Third generation advanced high strength steels (AHSS) have been a major focus in steel development over the last decade. The premise of these types of steel is based on the potential to obtain excellent combinations of strength and ductility with low-alloy compositions by forming mixed microstructures containing retained austenite (RA). The development of heat treatments able to achieve the desired structures and properties, such as quenching and partitioning (Q&P) steels, is driven by new requirements to increase vehicle fuel economy by reducing overall weight while maintaining safety and crashworthiness. Microalloying additions of niobium (Nb) and vanadium (V) in sheet products are known to provide strengthening via grain refinement and precipitation hardening and may influence RA volume fraction and transformation behavior. Additions of microalloying elements in Q&P steels have not been extensively studied to date, however. The objective of the present study was to begin to understand the potential roles of Nb and V in hot-rolled and cold-rolled Q&P steel. For that, a common Q&P steel composition was selected as a Base alloy with 0.2C-1.5Si-2.0Mn (wt. %). Two alloys with an addition of Nb (0.02 and 0.04 wt. %) and one with an addition of V (0.06 wt. %) to the Base alloy were investigated. Both hot-rolled and cold-rolled/annealed Q&P simulations were conducted. In the hot-rolled Q&P study, thermomechanical processing was simulated via hot torsion testing in a GleebleRTM 3500, and four coiling temperatures (CT) were chosen. Microstructural evaluation (including RA measurements via electron backscattered diffraction - EBSD) and hardness measurements were performed for all alloys and coiling conditions. The analysis showed that Nb additions led to overall refinement of the prior microstructure. Maximum RA fractions were measured at the 375 °C CT, and microalloying was associated with increased RA in this condition when compared to the Base alloy. A change in austenite morphology from lath-like to blocky with increasing CT was observed. Hardness generally increased with decreasing CT, consistent with the increased fraction of harder phases in the microstructure. For the cold-rolled Q&P study, several combinations of quenching temperature (QT), partitioning temperature (PT), and partitioning time (t p) were examined using heat treatments in salt baths. Uniaxial tensile tests and RA measurements via x-ray diffraction (XRD) were performed for all alloys and heat treatment conditions. Scanning electron microscope (SEM) imaging and EBSD were conducted for a few select conditions. In terms of microstructure, Nb promoted an extensive refinement of the prior austenite grain size. Additions of V and Nb also seemed to affect the morphology of the microstructural constituents. It was observed that V generally increased austenite fractions at lower t p's, and the Nb-containing alloys had greater austenite fractions in most instances when compared to the Base alloy. Carbon content in austenite was usually increased or maintained with additions of Nb and V. In terms of mechanical properties, V slightly improved strength and elongation when compared to the Base alloy for most conditions. Niobium additions were somewhat more effective in improving ductility.

Investigation of the Phase Formation of AlSi-Coatings for Hot Stamping of Boron Alloyed Steel

NASA Astrophysics Data System (ADS)

Veit, R.; Hofmann, H.; Kolleck, R.; Sikora, S.

2011-01-01

Hot stamping of boron alloyed steel is gaining more and more importance for the production of high strength automotive body parts. Within hot stamping of quenchenable steels the blank is heated up to austenitization temperature, transferred to the tool, formed rapidly and quenched in the cooled tool. To avoid scale formation during the heating process of the blank, the sheet metal can be coated with an aluminium-silicum alloy. The meltimg temperature of this coating is below the austenitization temperature of the base material. This means, that a diffusion process between base material and coating has to take place during heating, leading to a higher melting temperature of the coating. In conventional heating devices, like roller hearth furnaces, the diffusion process is reached by relatively low heating rates. New technologies, like induction heating, reach very high heating rates and offer great potentials for the application in hot stamping. Till now it is not proofed, that this technology can be used with aluminum-silicon coated materials. This paper will present the results of comparative heating tests with a conventional furnace and an induction heating device. For different time/temperature-conditions the phase formation within the coating will be described.

Repair of steel beam/girder ends with ultra high strength concrete (phase I) : final report.

DOT National Transportation Integrated Search

2015-06-06

The end corrosion in steel girders at the bearings due to joint leakage is a : significant problem in many of the old bridges around the nation. This critical : damage impairs the shear and bearing capacities of girders. Research has been : conducted...

On the Bonding Strength of Fe-Based Self-Fluxing Alloy Coating Deposited by Different Methods on the Steel Substrate

NASA Astrophysics Data System (ADS)

Feldshtein, E.; Kardapolava, M.; Dyachenko, O.

2018-05-01

In the present paper, the bonding strength of Fe-based self-fluxing alloy coating deposited by plasma spraying, gluing and laser remelting and alloying on the steel substrate have been investigated. When flame melting, a globular structure is formed. Against the background of the solid solution carbide-boride phases are clearly distinguishable, between which the Fe-Fe2B and Fe-FeB eutectic colonies are situated. Laser remelting leads to the formation of metastable structures, reinforced with dendrites, consisting of alloyed Fe-α and Fe-γ. At the low laser beam speeds the coating is melted completely with the formation of a cast structure with the dendrites. When the laser beam speed is increased, the dendritic structure gets fragmented. Structures of coatings alloyed with B4C and remelted by the laser beam vary with the increase of the spot speed. The bonding strength of coating without subsequent remelting decreases by 4-5 times in comparison with remelted. The bonding strength of the reinforced glue coating has adhesive and adhesive-cohesive character. When the load increases in the coating, microcracks develop, which gradually spread to the center of the bonding surface. For plasma coatings after laser remelting without additional alloying, the maximum bonding strength is observed with the minimum laser beam speed. With increasing the laser beam speed it decreases almost 1.5 times. In glue coatings reinforced with B4C particulates by laser remelting, the bonding strength is lower by 1.2-1.4 times in comparison with plasma coating.

Development of Custom 465® Corrosion-Resisting Steel for Landing Gear Applications

NASA Astrophysics Data System (ADS)

Daymond, Benjamin T.; Binot, Nicolas; Schmidt, Michael L.; Preston, Steve; Collins, Richard; Shepherd, Alan

2016-04-01

Existing high-strength low-alloy steels have been in place on landing gear for many years owing to their superior strength and cost performance. However, there have been major advances in improving the strength of high-performance corrosion-resisting steels. These materials have superior environmental robustness and remove the need for harmful protective coatings such as chromates and cadmium now on the list for removal under REACH legislation. A UK government-funded collaborative project is underway targeting a refined specification Custom 465® precipitation hardened stainless steel to replace the current material on Airbus A320 family aircraft main landing gear, a main fitting component developed by Messier-Bugatti-Dowty. This is a collaborative project between Airbus, Messier-Bugatti-Dowty, and Carpenter Technology Corporation. An extensive series of coupon tests on four production Heats of the material have been conducted, to obtain a full range of mechanical, fatigue, and corrosion properties. Custom 465® is an excellent replacement to the current material, with comparable tensile strength and fracture toughness, better ductility, and very good general corrosion and stress corrosion cracking resistance. Fatigue performance is the only significant area of deficit with respect to incumbent materials, fatigue initiation being often related to carbo-titanium-nitride particles and cleavage zones.

Effect of a prior stretch on the aging response of an Al-Cu-Li-Ag-Mg-Zr alloy

NASA Technical Reports Server (NTRS)

Kumar, K. S.; Brown, S. A.; Pickens, Joseph R.

1991-01-01

Recently, a family of Al-Cu-Li alloys containing minor amounts of Ag, Mg, and Zr and having desirable combinations of strength and toughness were developed. The Weldalite (trademark) alloys exhibit a unique characteristic in that with or without a prior stretch, they obtain significant strength-ductility combinations upon natural and artificial aging. The ultra-high strength (approximately 690 MPa yield strength) in the peak-aged tempers (T6 and T8) were primarily attributed to the extremely fine T(sub 1) (Al2CuLi) or T(sub 1)-type precipitates that occur in these alloys during artificial aging, whereas the significant natural aging response observed is attributed to strengthening from delta prime (Al3Li) and GP zones. In recent work, the aging behavior of an Al-Cu-Li-Ag-Mg alloy without a prior stretch was followed microstructurally from the T4 to the T6 condition. Commercial extrusions, rolled plates, and sheets of Al-Cu-Li alloys are typically subjected to a stretching operation before artificial aging to straighten the extrusions and, more importantly, introduce dislocations to simulate precipitation of strengthening phases such as T(sub 1) by providing relatively low-energy nucleation sites. The goals of this study are to examine the microstructure that evolves during aging of an alloy that was stretch after solution treatment and to compare the observations with those for the unstretched alloy.

Larson-Miller Constant of Heat-Resistant Steel

NASA Astrophysics Data System (ADS)

Tamura, Manabu; Abe, Fujio; Shiba, Kiyoyuki; Sakasegawa, Hideo; Tanigawa, Hiroyasu

2013-06-01

Long-term rupture data for 79 types of heat-resistant steels including carbon steel, low-alloy steel, high-alloy steel, austenitic stainless steel, and superalloy were analyzed, and a constant for the Larson-Miller (LM) parameter was obtained in the current study for each material. The calculated LM constant, C, is approximately 20 for heat-resistant steels and alloys except for high-alloy martensitic steels with high creep resistance, for which C ≈ 30 . The apparent activation energy was also calculated, and the LM constant was found to be proportional to the apparent activation energy with a high correlation coefficient, which suggests that the LM constant is a material constant possessing intrinsic physical meaning. The contribution of the entropy change to the LM constant is not small, especially for several martensitic steels with large values of C. Deformation of such martensitic steels should accompany a large entropy change of 10 times the gas constant at least, besides the entropy change due to self-diffusion.

Hydrogen environment embrittlement of metals

NASA Technical Reports Server (NTRS)

Jewett, R. P.; Walter, R. J.; Chandler, W. T.; Frohmberg, R. P.

1973-01-01

Hydrogen environment embrittlement refers to metals stressed while exposed to a hydrogen atmosphere. Tested in air, even after exposure to hydrogen under pressure, this effect is not observed on similar specimens. Much high purity hydrogen is prepared by evaporation of liquid hydrogen, and thus has low levels for potential impurities which could otherwise inhibit or poison the absorbent reactions that are involved. High strength steels and nickel-base allows are rated as showing extreme embrittlement; aluminum alloys and the austenitic stainless steels, as well as copper, have negligible susceptibility to this phenomenon. The cracking that occurs appears to be a surface phenomenon, is unlike that of internal hydrogen embrittlement.

Electroless nickel plating on stainless steels and aluminum

NASA Technical Reports Server (NTRS)

1966-01-01

Procedures for applying an adherent electroless nickel plating on 303 SE, 304, and 17-7 PH stainless steels, and 7075 aluminum alloy was developed. When heat treated, the electroless nickel plating provides a hard surface coating on a high strength, corrosion resistant substrate.

Design of Reforma 509 with High Strength Steel

NASA Astrophysics Data System (ADS)

Smith, Stuart; Whitby, William; Easton, Marc

Reforma 509 is a high-rise building located in the heart of the Central Business District of Mexico City. The building is comprised of office, hotel, residential and parking and forms part of a cluster of tall buildings in the area. If completed today, Reforma 509 would be the tallest building in Mexico, at 238m. All of the building's gravity and lateral (wind and seismic) loads are carried by an architecturally expressed perimeter frame that is formed from highly efficient Steel Reinforced Concrete (SRC) columns coupled together by steel tube perimeter bracing. This paper investigates the implications of substituting a grade 50 (fy=345 MPa) carbon steel with a higher strength micro-alloyed grade 70 (fy=480 MPa) steel in the design of Reforma 509.

Superior Ballistic Impact Resistance Achieved by the Co-Base Alloy Haynes 25

NASA Technical Reports Server (NTRS)

Hebsur, Mohan G.; Noebe, Ronald D.; Revilock, Duane M.

2003-01-01

The fan case in a jet engine is required to contain a fan blade in the rare event of a blade loss during operation. Because of its function, the fan case is the largest structural component in high-bypass-ratio turbofan engines used in commercial aircraft. Therefore, the use of lighter and stronger materials would be advantageous in most engines and is practically a necessity in the latest generation of high-bypass engines. Small panels, 7 in. wide by 7 in. long, of a number of metallic alloys were impact tested at room temperature with a 0.50-caliber blunt-nose titanium alloy projectile at the NASA Glenn Research Center (ref. 1). These metallic systems included several high-strength aluminum (Al) alloys, Al-based laminates, aluminum metal matrix composites (Al-MMCs), nickel-base superalloys (Inconel 718 and 625), several titanium (Ti) alloys in different heat treated conditions, 304L stainless steel, a stainless-steel-based laminate, and a high strength steel (Nitronic 60). It was determined that a simple Co-base alloy (Haynes 25) had the best impact resistance on an areal weight basis. Haynes 25 was at least 10 percent better than IMI 550, the best titanium alloy tested to date, and it was far superior to other metals, especially at higher impact velocities (greater than 1100 ft/sec). Because this material could be ideal for fan containment applications in supersonic aircraft as a replacement for titanium, impact tests were also conducted at 371 oC and compared with results from alloys tested at elevated temperature under previous programs (i.e., Inconel 718, Ti-6242, M-152, Timetal 21S, and Aeromet 100). Although cobalt-base alloys are used in some high-temperature engine applications, to our knowledge they are not used in any containment systems. Advantages of cobalt over titanium include lower cost, easier processing, better high-temperature strength, and no fire hazard if tip rub occurs. Future plans include testing of lightweight sandwich panels with Haynes 25 as a core material in the form of a foam or lattice block structure and scaling up the current tests by using blade-simulating projectiles impacting large plates and half rings.

A study of microstructure, quasi-static response, fatigue, deformation and fracture behavior of high strength alloy steels

NASA Astrophysics Data System (ADS)

Kannan, Manigandan

The history of steel dates back to the 17th century and has been instrumental in the betterment of every aspect of our lives ever since, from the pin that holds the paper together to the Automobile that takes us to our destination steel touches everyone every day. Path breaking improvements in manufacturing techniques, access to advanced machinery and understanding of factors like heat treatment, corrosion resistance have aided in the advancement in the properties of steel in the last few years. In this dissertation document, the results of a study aimed at the influence of alloy chemistry, processing and influence of the quasi static and fatigue behavior of seven alloy steels is discussed. The microstructure of the as-received steel was examined and characterized for the nature and morphology of the grains and the presence of other intrinsic features in the microstructure. The tensile, cyclic fatigue and bending fatigue tests were done on a fully automated closed-loop servo-hydraulic test machine at room temperature. The failed samples of high strength steels were examined in a scanning electron microscope for understanding the fracture behavior, especially the nature of loading be it quasi static, cyclic fatigue or bending fatigue . The quasi static and cyclic fatigue fracture behavior of the steels examined coupled with various factors contributing to failure are briefly discussed in light of the conjoint and mutually interactive influences of intrinsic microstructural effects, nature of loading, and stress (load)-deformation-microstructural interactions.

Effects of Zr Addition on Strengthening Mechanisms of Al-Alloyed High-Cr ODS Steels.

PubMed

Ren, Jian; Yu, Liming; Liu, Yongchang; Liu, Chenxi; Li, Huijun; Wu, Jiefeng

2018-01-12

Oxide dispersion strengthened (ODS) steels with different contents of zirconium (denoted as 16Cr ODS, 16Cr-0.3Zr ODS and 16Cr-0.6Zr ODS) were fabricated to investigate the effects of Zr on strengthening mechanism of Al-alloyed 16Cr ODS steel. Electron backscatter diffraction (EBSD) results show that the mean grain size of ODS steels could be decreased by Zr addition. Transmission electron microscope (TEM) results indicate that Zr addition could increase the number density but decrease the mean diameter and inter-particle spacing of oxide particles. Furthermore, it is also found that in addition to Y-Al-O nanoparticles, Y-Zr-O oxides with finer size were observed in 16Cr-0.3Zr ODS and 16Cr-0.6Zr ODS steels. These changes in microstructure significantly increase the yield strength (YS) and ultimate tensile strength (UTS) of ODS steels through mechanisms of grain boundary strengthening and dispersion strengthening.

Effects of Zr Addition on Strengthening Mechanisms of Al-Alloyed High-Cr ODS Steels

PubMed Central

Ren, Jian; Yu, Liming; Liu, Yongchang; Liu, Chenxi; Li, Huijun; Wu, Jiefeng

2018-01-01

Oxide dispersion strengthened (ODS) steels with different contents of zirconium (denoted as 16Cr ODS, 16Cr-0.3Zr ODS and 16Cr-0.6Zr ODS) were fabricated to investigate the effects of Zr on strengthening mechanism of Al-alloyed 16Cr ODS steel. Electron backscatter diffraction (EBSD) results show that the mean grain size of ODS steels could be decreased by Zr addition. Transmission electron microscope (TEM) results indicate that Zr addition could increase the number density but decrease the mean diameter and inter-particle spacing of oxide particles. Furthermore, it is also found that in addition to Y-Al-O nanoparticles, Y-Zr-O oxides with finer size were observed in 16Cr-0.3Zr ODS and 16Cr-0.6Zr ODS steels. These changes in microstructure significantly increase the yield strength (YS) and ultimate tensile strength (UTS) of ODS steels through mechanisms of grain boundary strengthening and dispersion strengthening. PMID:29329260

Effect of Ultra-Fast Cooling on Microstructure and Properties of High Strength Steel for Shipbuilding

NASA Astrophysics Data System (ADS)

Zhou, Cheng; Ye, Qibin; Yan, Ling

The effect of ultra-fast cooling(UFC) and conventional accelerated cooling(AcC) on the mechanical properties and microstructure of controlled rolled AH32 grade steel plates on industrial scale were compared using tensile test, Charpy impact test, welding thermal simulation, and microscopic analysis. The results show that the properties of the plate produced by UFC are improved considerably comparing to that by AcC. The yield strength is increased with 54 MPa without deterioration in the ductility and the impact energy is improved to more than 260 J at -60 °C with much lower ductile-to-brittle transition temperature(DBTT). The ferrite grain size is refined to ASTM No. 11.5 in the UFC steel with uniform microstructure throughout the thickness direction, while that of the AcC steel is ASTM No. 9.5. The analysis of nucleation kinetics of α-ferrite indicates that the microstructure is refined due to the increased nucleation rate of α-ferrite by much lower γ→α transition temperature through the UFC process. The Hall-Petch effect is quantified for the improvement of the strength and toughness of the UFC steel attributed to the grain refinement.

Mechanical properties of low-alloy-steels with bainitic microstructures and varying carbon content

NASA Astrophysics Data System (ADS)

Weber, A.; Klarner, J.; Vogl, T.; Schöngrundner, R.; Sam, G.; Buchmayr, B.

2016-03-01

Materials used in the oilfield industry are subjected to special conditions. These requirements for seamless steel tubes are between the priorities of strength, toughness and sour gas resistance. Steels with bainitic microstructure provide a great opportunity for those harsh environmental conditions. With different morphologies of bainite, like carbide free, upper or lower bainite, the interaction of high tensile strength and elongation is assumed to be better than with tempered martensite. To form carbide free bainite two ways of processing are proposed, isothermal holding with accurate time control or controlled continuous cooling. Both require knowledge of time-temperature transformation behaviour, which can be reached through a detailed alloying concept, focused on the influence of silicon to supress the carbide nucleation and chromium to stabilize the austenite fraction. The present work is based on three alloys with varying silicon and chromium contents. The carbide free microstructure is obtained by a continuous cooling path. Additionally different heat treatments were done to compare the inherent performance of the bainitic morphologies. The bainitic structures were characterized metallographically for their microstructure and the primary phase by means of transmission electron microscopy. The mechanical properties of carbide-free structures were analysed with quasi-static tensile tests and Charpy impact tests. Moreover, investigations about hydrogen embrittlement were done with focus on the effect of retained austenite. The results were ranked and compared qualitatively.

Influence of Ti addition on fracture behaviour of HSLA steel using TIG melting technique

NASA Astrophysics Data System (ADS)

Musa, M. H. A.; Maleque, M. A.; Ali, M. Y.

2017-03-01

The welding process is a critical stage in the production of structural parts and the microstructure and mechanical properties of the welded joints must be appropriate in order to guarantee the reliability and durability of the components. The fracture toughness behaviour, which accounts for the residual strength of the component in the presence of flaws or cracks, is one of the most important properties to be evaluated in terms of microstructure and mechanical properties. In this present study, the surface of high strength low alloy (HSLA) steel was surface modified with the preplacement of pure Titanium (Ti) powder using a tungsten inert gas (TIG) arc heat source, at 100 ampere current with a voltage 30 V and a constant traversing speed of 1.0 mm/s using Argon shielded gas. The effect of preplaced Ti powder on the strength and toughness properties of the modified HSLA steel surface was investigated. The results indicated that the tensile and yield strength of HSLA steel decreased by ∼12% and ∼14%, respectively. While the impact toughness increased by ∼33% and the ductility decreased by ∼50%. The fractography analysis results by scanning electron microscopy (SEM) were also presented in this paper.

Mechanical and degradation property improvement in a biocompatible Mg-Ca-Sr alloy by thermomechanical processing

DOE PAGES

Henderson, Hunter B.; Ramaswamy, Vidhya; Wilson-Heid, Alexander E.; ...

2018-02-03

Magnesium-based alloys have attracted interest as a potential material to comprise biomedical implants that are simultaneously high-strength and temporary, able to provide stabilization before degrading safely and able to be excreted by the human body. Many alloy systems have been evaluated, but this work reports on improved properties through hot extrusion of one promising alloy: Mg-1.0 wt% Ca-0.5 wt%Sr. This alloy has previously demonstrated promising toxicity and degradation properties in the as-cast and rolled conditions. In the current study extrusion causes a dramatic improvement in the mechanical properties in tension and compression, as well as a low in vitro degradationmore » rate. Microstructure (texture, second phase distribution, and grain size), bulk mechanical properties, flow behavior, degradation in simulated body fluid, and effect on osteoblast cyctotoxicity are evaluated and correlated to extrusion temperature. In conclusion, maximum yield strength of 300 MPa (above that of annealed 316 stainless steel) with 10% elongation is observed, making this alloy competitive with existing implant materials.« less

Mechanical and degradation property improvement in a biocompatible Mg-Ca-Sr alloy by thermomechanical processing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Henderson, Hunter B.; Ramaswamy, Vidhya; Wilson-Heid, Alexander E.

Magnesium-based alloys have attracted interest as a potential material to comprise biomedical implants that are simultaneously high-strength and temporary, able to provide stabilization before degrading safely and able to be excreted by the human body. Many alloy systems have been evaluated, but this work reports on improved properties through hot extrusion of one promising alloy: Mg-1.0 wt% Ca-0.5 wt%Sr. This alloy has previously demonstrated promising toxicity and degradation properties in the as-cast and rolled conditions. In the current study extrusion causes a dramatic improvement in the mechanical properties in tension and compression, as well as a low in vitro degradationmore » rate. Microstructure (texture, second phase distribution, and grain size), bulk mechanical properties, flow behavior, degradation in simulated body fluid, and effect on osteoblast cyctotoxicity are evaluated and correlated to extrusion temperature. In conclusion, maximum yield strength of 300 MPa (above that of annealed 316 stainless steel) with 10% elongation is observed, making this alloy competitive with existing implant materials.« less

Mechanical and degradation property improvement in a biocompatible Mg-Ca-Sr alloy by thermomechanical processing.

PubMed

Henderson, Hunter B; Ramaswamy, Vidhya; Wilson-Heid, Alexander E; Kesler, Michael S; Allen, Josephine B; Manuel, Michele V

2018-04-01

Magnesium-based alloys have attracted interest as a potential material to comprise biomedical implants that are simultaneously high-strength and temporary, able to provide stabilization before degrading safely and able to be excreted by the human body. Many alloy systems have been evaluated, but this work reports on improved properties through hot extrusion of one promising alloy: Mg-1.0 wt% Ca-0.5 wt%Sr. This alloy has previously demonstrated promising toxicity and degradation properties in the as-cast and rolled conditions. In the current study extrusion causes a dramatic improvement in the mechanical properties in tension and compression, as well as a low in vitro degradation rate. Microstructure (texture, second phase distribution, and grain size), bulk mechanical properties, flow behavior, degradation in simulated body fluid, and effect on osteoblast cyctotoxicity are evaluated and correlated to extrusion temperature. Maximum yield strength of 300 MPa (above that of annealed 316 stainless steel) with 10% elongation is observed, making this alloy competitive with existing implant materials. Copyright © 2018 The Author(s). Published by Elsevier Ltd.. All rights reserved.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Field, Kevin G.; Univ. of Wisconsin, Madison, WI; Miller, Brandon D.

Ferritic/Martensitic (F/M) steels with high Cr content posses the high temperature strength and low swelling rates required for advanced nuclear reactor designs. Radiation induced segregation (RIS) occurs in F/M steels due to solute atoms preferentially coupling to point defect fluxes which migrate to defect sinks, such as grain boundaries (GBs). The RIS response of F/M steels and austenitic steels has been shown to be dependent on the local structure of GBs where low energy structures have suppressed RIS responses. This relationship between local GB structure and RIS has been demonstrated primarily in ion-irradiated specimens. A 9 wt.% Cr model alloymore » steel was irradiated to 3 dpa using neutrons at the Advanced Test Reactor (ATR) to determine the effect of a neutron radiation environment on the RIS response at different GB structures. This investigation found the relationship between GB structure and RIS is also active for F/M steels irradiated using neutrons. The data generated from the neutron irradiation is also compared to RIS data generated using proton irradiations on the same heat of model alloy.« less

Effect of process parameters on formability of laser melting deposited 12CrNi2 alloy steel

NASA Astrophysics Data System (ADS)

Peng, Qian; Dong, Shiyun; Kang, Xueliang; Yan, Shixing; Men, Ping

2018-03-01

As a new rapid prototyping technology, the laser melting deposition technology not only has the advantages of fast forming, high efficiency, but also free control in the design and production chain. Therefore, it has drawn extensive attention from community.With the continuous improvement of steel performance requirements, high performance low-carbon alloy steel is gradually integrated into high-tech fields such as aerospace, high-speed train and armored equipment.However, it is necessary to further explore and optimize the difficult process of laser melting deposited alloy steel parts to achieve the performance and shape control.This article took the orthogonal experiment on alloy steel powder by laser melting deposition ,and revealed the influence rule of the laser power, scanning speed, powder gas flow on the quality of the sample than the dilution rate, surface morphology and microstructure analysis were carried out.Finally, under the optimum technological parameters, the Excellent surface quality of the alloy steel forming part with high density, no pore and cracks was obtained.

Evaluation of Fatigue Strength Improvement by CFRP Laminates and Shot Peening onto the Tension Flanges Joining Corrugated Steel Webs

PubMed Central

Wang, Zhi-Yu; Wang, Qing-Yuan; Liu, Yong-Jie

2015-01-01

Corrugated steel web with inherent high out-of-plane stiffness has a promising application in configuring large span highway bridge girders. Due to the irregularity of the configuration details, the local stress concentration poses a major fatigue problem for the welded flange plates of high strength low alloy structural steels. In this work, the methods of applying CFRP laminate and shot peening onto the surfaces of the tension flanges were employed with the purpose of improving the fatigue strength of such configuration details. The effectiveness of this method in the improvement of fatigue strength has been examined experimentally. Test results show that the shot peening significantly increases hardness and roughness in contrast to these without treatment. Also, it has beneficial effects on the fatigue strength enhancement when compared against the test data of the joints with CFRP strengthening. The stiffness degradation during the loading progress is compared with each treatment. Incorporating the stress acting on the constituent parts of the CFRP laminates, a discussion is made regarding the mechanism of the retrofit and related influencing factors such as corrosion and economic cost. This work could enhance the understanding of the CFRP and shot peening in repairing such welded details and shed light on the reinforcement design of welded joints between corrugated steel webs and flange plates. PMID:28793509

A New Paradigm for Designing High-Fracture-Energy Steels

NASA Astrophysics Data System (ADS)

Fine, M. E.; Vaynman, S.; Isheim, D.; Chung, Y.-W.; Bhat, S. P.; Hahin, C. H.

2010-12-01

The steels used for structural and other applications ideally should have both high strength and high toughness. Most high-strength steels contain substantial carbon content that gives poor weldability and toughness. A theoretical study is presented that was inspired by the early work of Weertman on the effect that single or clusters of solute atoms with slightly different atom sizes have on dislocation configurations in metals. This is of particular interest for metals with high Peierls stress. Misfit centers that are coherent and coplanar in body-centered cubic (bcc) metals can provide sufficient twisting of nearby screw dislocations to reduce the Peierls stress locally and to give improved dislocation mobility and hence better toughness at low temperatures. Therefore, the theory predicts that such nanoscale misfit centers in low-carbon steels can give both precipitation hardening and improved ductility and fracture toughness. To explore the validity of this theory, we measured the Charpy impact fracture energy as a function of temperature for a series of low-carbon Cu-precipitation-strengthened steels. Results show that an addition of 0.94 to 1.49 wt pct Cu and other accompanying elements results in steels with high Charpy impact energies down to cryogenic temperatures (198 K [-75 °C]) with no distinct ductile-to-brittle transition. The addition of 0.1 wt pct Ti results in an additional increase in impact toughness, with Charpy impact fracture energies ranging from 358 J (machine limit) at 248 K (-25 °C) to almost 200 J at 198 K (-75 °C). Extending this concept of using coherent and coplanar misfit centers to decrease the Peierls stress locally to other than bcc iron-based systems suggests an intriguing possibility of developing ductile hexagonal close-packed alloys and intermetallics.

Stress corrosion evaluation of HP 9Ni-4Co-0.20C steel

NASA Technical Reports Server (NTRS)

Torres, Pablo D.

1993-01-01

A stress corrosion cracking (SCC) evaluation was undertaken on HP 9Ni-4Co-0.20C steel in support of the Advanced Solid Rocket Motor (ASRM) program. This alloy was tested in plate, bar, and ring forging forms. Several heat treating procedures yielded ultimate tensile strengths ranging from 1,407 to 1,489 MPa (204 to 216 ksi). The test environments were high humidity, alternate immersion in 3.5-percent NaCl, and 5-percent salt spray. Stress levels ranged from 25 to 90 percent of the yield strengths. The majority of the tests were conducted for 90 days. Even though the specimens rusted significantly in salt spray and alternate immersion, no failures occurred. Therefore, it can be concluded that this alloy, in the forms and at the strength levels tested, is highly resistant to SCC in salt and high humidity environments.

High yttria ferritic ODS steels through powder forging

NASA Astrophysics Data System (ADS)

Kumar, Deepak; Prakash, Ujjwal; Dabhade, Vikram V.; Laha, K.; Sakthivel, T.

2017-05-01

Oxide dispersion strengthened (ODS) steels are being developed for future nuclear reactors. ODS Fe-18%Cr-2%W-0.2%Ti steels with 0, 0.35, 0.5, 1 and 1.5% Y2O3 (all compositions in weight%) dispersion were fabricated by mechanical alloying of elemental powders. The powders were placed in a mild steel can and forged in a stream of hydrogen gas at 1473 K. The steels were forged again to final density. The strength of ODS steel increased with yttria content. Though this was accompanied by a decrease in tensile elongation, all the steels showed significant ductility. The ductility in high yttria alloys may be attributed to improved inter-particle bonding between milled powders due to reduction of surface oxides by hydrogen. This may permit development of ODS steels with yttria contents higher than the conventional limit of 0.5%. It is suggested that powder forging is a promising route to fabricate ODS steels with high yttria contents and improved ductility.

The effect of aluminum alloying on strength properties and deformation mechanisms of the <123> Hadfield steel single crystals

NASA Astrophysics Data System (ADS)

Astafurova, E. G.; Tukeev, M. S.; Chumlyakov, Yu. I.

2007-10-01

The role of aluminum alloying on strength properties and deformation mechanisms (slip, twinning) of <123> single crystals of Hadfield steel under tensile loading at T = 300 K is demonstrated. It is found out that aluminum alloying suppresses twinning deformation in the <123> single crystals and, during slip, results in a dislocation structure change from a uniform dislocation distribution to a planar dislocation structure.

Effects of annealing conditions on microstructure and mechanical properties of low carbon, manganese transformation-induced plasticity steel

NASA Astrophysics Data System (ADS)

Jang, Jae-Myeong; Kim, Sung-Joon; Kang, Nam Hyun; Cho, Kyung-Mox; Suh, Dong-Woo

2009-12-01

The effects of annealing conditions on microstructural evolution and mechanical properties have been investigated in low carbon, manganese TRIP (Mn TRIP) steel based on a 0.12C-6Mn-0.5Si-3Al alloy system. The microstructure of cold-rolled sheet subjected to annealing at 760 °C to 800 °C for 30 s to 1800 s consists of a recrystallized ferrite matrix and fine-grained austenite with a phase fraction of 25 % to 35 %. Variation of the annealing conditions remarkably influenced the characteristics of constituent phases and thus affected the tensile strength and elongation. Optimization of microstructural parameters such as grain size and fraction of constituent phases, which control the yield strength, overall work hardening, and the kinetics of strain-induced martensite formation, is thus critical for obtaining an exceptional mechanical balance of the alloy.

76 FR 60582 - Buy America Waiver Notification

Federal Register 2010, 2011, 2012, 2013, 2014

2011-09-29

... 1/ 2'' x 0.008 steel fiber with ultimate tensile strength of 290ksi for experimental use in Ultra... 0.008 steel fiber with ultimate tensile strength of 290ksi for experimental use in UHPC in Iowa. In... potential domestic manufacturers for 1/2'' x 0.008 steel fiber with ultimate tensile strength of 290ksi for...

Observation of the TWIP + TRIP Plasticity-Enhancement Mechanism in Al-Added 6 Wt Pct Medium Mn Steel

NASA Astrophysics Data System (ADS)

Lee, Seawoong; Lee, Kyooyoung; De Cooman, Bruno C.

2015-06-01

The intercritically annealed Fe-0.15 pctC-6.0 pctMn-1.5 pctSi-3.0 pctAl and Fe-0.30 pctC-6.0 pctMn-1.5 pctSi-3.0 pctAl medium Mn steels were found to have improved mechanical properties due to the TWIP and TRIP plasticity-enhancing mechanisms being activated in succession during tensile deformation. The increase of the C content from 0.15 to 0.30 pct resulted in ultra-high strength properties and a strength-ductility balance of approximately 65,000 MPa-pct, i.e., equivalent to the strength-ductility balance of high Mn TWIP steel with a fully austenitic microstructure.

Finite element modelling of chain-die forming for ultra-high strength steel

NASA Astrophysics Data System (ADS)

Majji, Raju; Xiang, Yang; Ding, Scott; Yang, Chunhui

2017-10-01

There has been a high demand for weight reduction in automotive vehicles while maintaining passenger safety. A potential steel material to achieve this is Ultra High Strength Steel (UHSS). As a high strength material, it is difficult to be formed with desired profiles using traditional sheet metal forming processes such as Cold Roll Forming. To overcome this problem, a potentially alternative solution is Chain-die Forming (CDF), recently developed. The basic principal of the CDF is to fully combine roll forming and bending processes. The main advantage of this process is the elongated deformation length that significantly increases effective roll radius. This study focuses on identifying issues with the CDF by using CAD modelling, Motion Analysis and Finite Element Analysis (FEA) to devise solutions and construct a more reliable process in an optimal design sense. Some attempts on finite element modelling and simulation of the CDF were conducted using relatively simple models in literature and the research was still not sufficient enough for optimal design of a typical CDF for UHSS. Therefore two numerical models of Chain-die Forming process are developed in this study, including a) one having a set of rolls similar to roll forming but with a large radius, i.e., 20 meters; and b) the other one with dies and punch segments similar to a typical CDF machine. As a case study, to form a 60° channel with single pass was conducted using these two devised models for a comparison. The obtained numerical results clearly show the CDF could generate less residual stress, low strain and small springback of a single pass for the 60° UHSS channel. The design analysis procedure proposed in this study could greatly help the mechanical designers to devise a cost-effective and reliable CDF process for forming UHSS.

Selective role of bainitic lath boundary in influencing slip systems and consequent deformation mechanisms and delamination in high-strength low-alloy steel

NASA Astrophysics Data System (ADS)

Liu, S.; Li, X.; Guo, H.; Yang, S.; Wang, X.; Shang, C.; Misra, R. D. K.

2018-04-01

We elucidate here the deformation behaviour and delamination phenomenon in a high-strength low-alloy bainitic steel, in terms of microstructure, texture and stress evolution during deformation via in situ electron back-scattered diffraction and electron microscopy. Furthermore, the selective role of bainitic lath boundary on slip systems was studied in terms of dislocation pile-up and grain boundary energy models. During tensile deformation, the texture evolution was concentrated at {1 1 0}<1 1 1> and the laths were turn parallel to loading direction. The determining role of lath on the deformation behaviour is governed by length/thickness (l/t) ratio. When l/t > 28, the strain accommodates along the bainite lath rather than along the normal direction. The delamination crack initiated normal to (0 1 1) plane, and become inclined to (0 1 1) plane with continued strain along (0 1 1) plane and lath plane. This indicated that the delamination is not brittle process but plastic process. The lack of dimples at the delaminated surface is because of lack of strain normal to the direction of lath. The delaminated (0 1 1) planes were associated with cleavage along the (1 0 0) plane.

Grain boundary engineering for structure materials of nuclear reactors

NASA Astrophysics Data System (ADS)

Tan, L.; Allen, T. R.; Busby, J. T.

2013-10-01

Grain boundary engineering (GBE), primarily implemented by thermomechanical processing, is an effective and economical method of enhancing the properties of polycrystalline materials. Among the factors affecting grain boundary character distribution, literature data showed definitive effect of grain size and texture. GBE is more effective for austenitic stainless steels and Ni-base alloys compared to other structural materials of nuclear reactors, such as refractory metals, ferritic and ferritic-martensitic steels, and Zr alloys. GBE has shown beneficial effects on improving the strength, creep strength, and resistance to stress corrosion cracking and oxidation of austenitic stainless steels and Ni-base alloys.

Development of Ag-Pd-Au-Cu alloy for multiple dental applications. Part 1. Effects of Pd and Cu contents, and addition of Ga or Sn on physical properties and bond with ultra-low fusing ceramic.

PubMed

Goto, S; Miyagawa, Y; Ogura, H

2000-09-01

Ag-Pd-Au-Cu quaternary alloys consisting of 30-50% Ag, 20-40% Pd, 10-20% Cu and 20% Au (mother alloys) were prepared. Then 5% Sn or 5% Ga was added to the mother alloy compositions, and another two alloy systems (Sn-added alloys and Ga-added alloys) were also prepared. The bond between the prepared alloys and an ultra-low fusing ceramic as well as their physical properties such as the solidus point, liquidus point and the coefficient of thermal expansion were evaluated. The solidus point and liquidus point of the prepared alloys ranged from 802 degrees C to 1142 degrees C and from 931 degrees C to 1223 degrees C, respectively. The coefficient of thermal expansion ranged from 14.6 to 17.1 x 10(-6)/degrees C for the Sn- and Ga-added alloys. In most cases, the Pd and Cu contents significantly influenced the solidus point, liquidus point and coefficient of thermal expansion. All Sn- and Ga-added alloys showed high area fractions of retained ceramic (92.1-100%), while the mother alloy showed relatively low area fractions (82.3%) with a high standard deviation (20.5%). Based on the evaluated properties, six Sn-added alloys and four Ga-added alloys among the prepared alloys were suitable for the application of the tested ultra-low fusing ceramic.

Process for making a martensitic steel alloy fuel cladding product

DOEpatents

Johnson, Gerald D.; Lobsinger, Ralph J.; Hamilton, Margaret L.; Gelles, David S.

1990-01-01

This is a very narrowly defined martensitic steel alloy fuel cladding material for liquid metal cooled reactors, and a process for making such a martensitic steel alloy material. The alloy contains about 10.6 wt. % chromium, about 1.5 wt. % molybdenum, about 0.85 wt. % manganese, about 0.2 wt. % niobium, about 0.37 wt. % silicon, about 0.2 wt. % carbon, about 0.2 wt. % vanadium, 0.05 maximum wt. % nickel, about 0.015 wt. % nitrogen, about 0.015 wt. % sulfur, about 0.05 wt. % copper, about 0.007 wt. % boron, about 0.007 wt. % phosphorous, and with the remainder being essentially iron. The process utilizes preparing such an alloy and homogenizing said alloy at about 1000.degree. C. for 16 hours; annealing said homogenized alloy at 1150.degree. C. for 15 minutes; and tempering said annealed alloy at 700.degree. C. for 2 hours. The material exhibits good high temperature strength (especially long stress rupture life) at elevated temperature (500.degree.-760.degree. C.).

Overview of Strategies for High-Temperature Creep and Oxidation Resistance of Alumina-Forming Austenitic Stainless Steels

NASA Astrophysics Data System (ADS)

Yamamoto, Y.; Brady, M. P.; Santella, M. L.; Bei, H.; Maziasz, P. J.; Pint, B. A.

2011-04-01

A family of creep-resistant, alumina-forming austenitic (AFA) stainless steel alloys is under development for structural use in fossil energy conversion and combustion system applications. The AFA alloys developed to date exhibit comparable creep-rupture lives to state-of-the-art advanced austenitic alloys, and superior oxidation resistance in the ~923 K to 1173 K (650 °C to 900 °C) temperature range due to the formation of a protective Al2O3 scale rather than the Cr2O3 scales that form on conventional stainless steel alloys. This article overviews the alloy design approaches used to obtain high-temperature creep strength in AFA alloys via considerations of phase equilibrium from thermodynamic calculations as well as microstructure characterization. Strengthening precipitates under evaluation include MC-type carbides or intermetallic phases such as NiAl-B2, Fe2(Mo,Nb)-Laves, Ni3Al-L12, etc. in the austenitic single-phase matrix. Creep, tensile, and oxidation properties of the AFA alloys are discussed relative to compositional and microstructural factors.

Experimental Investigation of Mechanical Properties of Welded Corten Steel A588 Grade Plate Using ER70S - 6 Filler Material for Construction Application

NASA Astrophysics Data System (ADS)

Deepak, J. R.; Bupesh Raja, V. K.; Janardhan Guptha, Mittapalli; Durga Prasad, Palaparthi Hari; Sriram, V.

2017-05-01

ASTM A588 Grade A steel plate is a high strength, low alloy structural steel with 0.19 % of carbon content. When exposed to the atmosphere, A588 Grade A is suitable for construction in the bare (paint - free) condition. The main problems are lack of fusion, lack of penetration and corrosion on heat affected zone. In this research work Corten ASTM A588 Grade steel of 3mm thickness is electroplated with copper and then both raw and copper electroplated are welded by GMAW welding process with ER70S-6 as a filler material. The welded ASTM A588 is cut according to ASTM size for further testing of mechanical properties. Considering its welding strength after the process of electroplating, this research clearly states the metal can be utilized for better results in any given field. Here both the tensile and hardness are higher in copper electroplated welded when compare to raw welded.

Microstructure and Mechanical Properties of Friction Stir Welded Aluminum Alloy/Stainless Steel Lap Joints

NASA Astrophysics Data System (ADS)

Ogura, Tomo; Nishida, Taichi; Nishida, Hidehito; Yoshikawa, Syuhei; Yoshida, Takumi; Omichi, Noriko; Fujimoto, Mitsuo; Hirose, Akio

The mechanical properties and interfacial microstructure of an aluminum alloy/stainless steel dissimilar lap joint using friction stir welding (FSW) were characterized. In an FSWed A3003 aluminum alloy-SUS304 steel lap joint, the strength on the advancing side was larger than that at the retreating side. TEM observation indicated that a sound joint can be obtained from the stage of the formation of the amorphous layer owing to the mechanical alloying effects before the formation of intermetallic compounds. This lap joining technique was also successfully applied to A6061-T6 aluminum alloy-grooved SUS304 plates. The maximum tensile strength of the lap joint was approximately the same as that of the base alloy, however, the proof stress of the joint decreased with the dissolution of the β″ phase in the A6061 aluminium alloy, which is caused by the generation of heat during friction stir welding.

Structural studies with the use of XRD and Mössbauer spectroscopy of new high Manganese steels

NASA Astrophysics Data System (ADS)

Jablonska, Magdalena Barbara

2014-04-01

New high-strength austenitic and austenitic-ferritic manganese steels represent a significant potential in applications for structural components in the automotive and railway industry due to the excellent combination of high mechanical properties and good plasticity. They belong to the group of steels called AHSS (Advanced High Strength Steels) and UHSS (Ultra High Strength Steels). Application of this combination of properties allows a reduction in the weight of vehicles by the use of reduced cross-section components, and thus to reduce fuel consumption. The development and implementation of industrial production of such interesting and promising steel and its use as construction material requires an improvement of their casting properties and susceptibility to deformation in plastic working conditions. In this work, XRD, Transmission Mössbauer Spectroscopy and Conversion Electron Mössbauer Spectroscopy were employed in a study of the new high-manganese steels with a austenite and austenite-ferrite structure. The influence of the plastic deformation parameters on the changes in the structure, distribution of ferrite and disclosure of the presence of carbides was determined. The analysis of phase transformations in various times using CEMS method made possible to reveal their fine details.

An assessment of ultra fine grained 316L stainless steel for implant applications.

PubMed

Muley, Sachin Vijay; Vidvans, Amey N; Chaudhari, Gajanan P; Udainiya, Sumit

2016-01-01

Ultra fine-grained metals obtained by severe plastic deformation exhibit higher specific strength that is useful for many applications and show promise for use as body implants. This work studied the microstructural evolution, mechanical and sliding wear behavior and corrosion behavior of 316L stainless steel warm multi axially forged at 600°C. Microstructural evolution studied using electron backscatter diffraction technique and transmission electron microscopy confirmed the formation of ultra fine-grained structure. Average grain size reduced from 30μm to 0.86μm after nine strain steps. A combination of Hall-Petch strengthening and strain hardening increased the hardness. Improved sliding wear resistance is attributed to a transition from micro cutting to wedge-forming mode of abrasive wear. Load-bearing orthopedic implants often fail from pitting initiated corrosion fatigue. Potentiodynamic tests, cyclic polarization, and FeCl3 immersion tests revealed enhanced pitting resistance of forged steel that is confirmed by Mott-Schottky analysis. This is ascribed to an increase in the grain boundary volume, and homogenization of pit inducing impurities and non-metallic phases due to severe deformation, which influenced the passive film properties. These model studies on 316L steel demonstrate that severely deformed ultra fine-grained metals have potential to deliver improved implant performance. This model study on 316L steel demonstrates that severely deformed ultra fine-grained (UFG) metals have potential to deliver improved load-bearing implant performance. It is as interesting as is unclear as to how such severely deformed UFG material behaves electrochemically in the corrosive body fluids. This work is on studying the inter-relationship between structure, and mechanical, wear, and corrosion behavior of warm multiaxially forged (MAFed) UFG 316L stainless steel. Warm MAF is a bulk processing method capable of yielding large volume of UFG material and is an easily readily adaptable technique in industry. It can be a promising alternative to the expensive metallic alloys available for implant applications. Copyright © 2015 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Nanometric Scale Investigation of Phase Transformations in Advanced Steels for Automotive Application

NASA Astrophysics Data System (ADS)

Drillet, Josée; Valle, Nathalie; Iung, Thierry

2012-12-01

The current trend toward producing lighter vehicles in the automotive industry is driven by the need to conform to the new exhaust emission control regulations. This objective presents a challenge to steel manufacturers. The difficulty lies in designing new alloys with an optimum strength/formability/cost balance for the various components. Here, the key to success lies in controlling the steel microstructure and especially the phase transformations at the smallest possible scale. Among the different alloying elements, light elements such as carbon and boron are of prime importance due to their major effects on the kinetics of phase transformations. Characterization tools combining high spatial and analytical resolution such as secondary ion mass spectrometry (SIMS) and field emission gun-transmission electron microscopy (TEM) were used. In this article, the examples presented are as follows. (1) Boron segregation and precipitation effects to control hardenability in martensitic steels. (2) Local carbon distribution in advanced high-strength steels, with a specific emphasis on martensite tempering. Links have been established between the boron and carbon distribution and the formability.

Fabrication, characterization, and irradiation of an austenitic oxide dispersion strengthened steel suited for next generation nuclear applications

NASA Astrophysics Data System (ADS)

Brooks, Adam J.

As nuclear energy systems become more advanced, the materials encompassing them need to perform at higher temperatures for longer periods of time. In this Master's thesis we experiment with an oxide dispersion strengthened (ODS) austenitic steel that has been recently developed. ODS materials have a small concentration of nano oxide particles dispersed in their matrix, and typically have higher strength and better extreme temperature creep resistance characteristics than ordinary steels. However, no ODS materials have ever been installed in a commercial power reactor to date. Being a newer research material, there are many unanswered phenomena that need to be addressed regarding the performance under irradiation. Furthermore, due to the ODS material traditionally needing to follow a powder metallurgy fabrication route, there are many processing parameters that need to be optimized before achieving a nuclear grade material specification. In this Master's thesis we explore the development of a novel ODS processing technology conducted in Beijing, China, to produce solutionized bulk ODS samples with 97% theoretical density. This is done using relatively low temperatures and ultra high pressure (UHP) equipment, to compact the mechanically alloyed (MA) steel powder into bulk samples without any thermal phase change influence or oxide precipitation. By having solutionized bulk ODS samples, transmission electron microscopy (TEM) observation of nano oxide precipitation within the steel material can be studied by applying post heat treatments. These types of samples will be very useful to the science and engineering community, to answer questions regarding material powder compacting, oxide synthesis, and performance. Subsequent analysis performed at Queen's University included X-ray diffraction (XRD) and inductively coupled plasma optical emission spectrometry (ICP-OES). Additional TEM in-situ 1MeV Kr2+ irradiation experiments coupled with energy dispersive X-ray (EDX) techniques, were also performed on large (200nm+) non-stoichiometric oxides embedded within the austenite steel grains, in an attempt to quantify the elemental compositional changes during high temperature (520°C) heavy ion irradiation.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tan, Lizhen; Snead, Lance Lewis; Katoh, Yutai

International development of reduced activation ferritic-martensitic (RAFM) steels has focused on 9 wt percentage Cr, which primarily contain M 23C 6 (M = Cr-rich) and small amounts of MX (M = Ta/V, X = C/N) precipitates, not adequate to maintain strength and creep resistance above ~500 °C. To enable applications at higher temperatures for better thermal efficiency of fusion reactors, computational alloy thermodynamics coupled with strength modeling have been employed to explore a new generation RAFM steels. The new alloys are designed to significantly increase the amount of MX nanoprecipitates, which are manufacturable through standard and scalable industrial steelmaking methods.more » Preliminary experimental results of the developed new alloys demonstrated noticeably increased amount of MX, favoring significantly improved strength, creep resistance, and Charpy impact toughness as compared to current RAFM steels. Furthermore, the strength and creep resistance were comparable or approaching to the lower bound of, but impact toughness was noticeably superior to 9–20Cr oxide dispersion-strengthened ferritic alloys.« less

High-rate tensile properties of Si-reduced TRIP sheet steels

NASA Astrophysics Data System (ADS)

Choi, Ildong; Park, Yeongdo; Son, Dongmin; Kim, Sung-Joon; Moon, Manbeen

2010-02-01

There have been efforts to develop Si-reduced TRIP steels to improve the wettability of Zn coatings, since the conventional CMnSi-TRIP steels suffer from poor galvanizability. In addition, for the development of potential applications of Si-reduced TRIP steels in vehicle crash management, a better understanding of high strain rate properties is required. In the present study, the effects of alloying elements, such as Cu, Al, Si, and P, on the high-rate tensile properties of Si-reduced TRIP sheet steels were investigated. Tensile tests were performed with a servo-hydraulic tensile testing machine at strain rates ranging from 10-2 to 6 × 102 s-1, and the ultimate tensile strength, elongation, strain rate sensitivity, and absorbed energy were evaluated. The retained austenite volume fractions and carbon content of the specimens were measured using neutron diffraction. The UTS was increased with Cu, Al, Si, and P alloying throughout the strain rate range, and the alloying effect on UTS was considerable with Cu and P. The effects of alloying on the microstructure were not significant. All the steels tested in this study exhibited positive strain rate sensitivity, and the m value at strain rates higher than 10 s-1 was at least two times higher than that at lower strain rates.

Experimental Validation for Hot Stamping Process by Using Taguchi Method

NASA Astrophysics Data System (ADS)

Fawzi Zamri, Mohd; Lim, Syh Kai; Razlan Yusoff, Ahmad

2016-02-01

Due to the demand for reduction in gas emissions, energy saving and producing safer vehicles has driven the development of Ultra High Strength Steel (UHSS) material. To strengthen UHSS material such as boron steel, it needed to undergo a process of hot stamping for heating at certain temperature and time. In this paper, Taguchi method is applied to determine the appropriate parameter of thickness, heating temperature and heating time to achieve optimum strength of boron steel. The experiment is conducted by using flat square shape of hot stamping tool with tensile dog bone as a blank product. Then, the value of tensile strength and hardness is measured as response. The results showed that the lower thickness, higher heating temperature and heating time give the higher strength and hardness for the final product. In conclusion, boron steel blank are able to achieve up to 1200 MPa tensile strength and 650 HV of hardness.

Miniature High-Force, Long-Stroke SMA Linear Actuators

NASA Technical Reports Server (NTRS)

Cummin, Mark A.; Donakowski, William; Cohen, Howard

2008-01-01

Improved long-stroke shape-memory-alloy (SMA) linear actuators are being developed to exert significantly higher forces and operate at higher activation temperatures than do prior SMA actuators. In these actuators, long linear strokes are achieved through the principle of displacement multiplication, according to which there are multiple stages, each intermediate stage being connected by straight SMA wire segments to the next stage so that relative motions of stages are additive toward the final stage, which is the output stage. Prior SMA actuators typically include polymer housings or shells, steel or aluminum stages, and polymer pads between successive stages of displacement-multiplication assemblies. Typical output forces of prior SMA actuators range from 10 to 20 N, and typical strokes range from 0.5 to 1.5 cm. An important disadvantage of prior SMA wire actuators is relatively low cycle speed, which is related to actuation temperature as follows: The SMA wires in prior SMA actuators are typically made of a durable nickel/titanium alloy that has a shape-memory activation temperature of 80 C. An SMA wire can be heated quickly from below to above its activation temperature to obtain a stroke in one direction, but must then be allowed to cool to somewhat below its activation temperature (typically, less than or equal to 60 C in the case of an activation temperature of 80 C) to obtain a stroke in the opposite direction (return stroke). At typical ambient temperatures, cooling times are of the order of several seconds. Cooling times thus limit cycle speeds. Wires made of SMA alloys having significantly higher activation temperatures [denoted ultra-high-temperature (UHT) SMA alloys] cool to the required lower return-stroke temperatures more rapidly, making it possible to increase cycle speeds. The present development is motivated by a need, in some applications (especially aeronautical and space-flight applications) for SMA actuators that exert higher forces, operate at greater cycle speeds, and have stronger housings that can withstand greater externally applied forces and impacts. The main novel features of the improved SMA actuators are the following: 1) The ends of the wires are anchored in compact crimps made from short steel tubes. Each wire end is inserted in a tube, the tube is flattened between planar jaws to make the tube grip the wire, the tube is compressed to a slight U-cross-section deformation to strengthen the grip, then the crimp is welded onto one of the actuator stages. The pull strength of a typical crimp is about 125 N -- comparable to the strength of the SMA wire and greater than the typical pull strengths of wire-end anchors in prior SMA actuators. Greater pull strength is one of the keys to achievement of higher actuation force; 2) For greater strength and resistance to impacts, housings are milled from aluminum instead of being made from polymers. Each housing is made from two pieces in a clamshell configuration. The pieces are anodized to reduce sliding friction; 3) Stages are made stronger (to bear greater compression loads without excessive flexing) by making them from steel sheets thicker than those used in prior SMA actuators. The stages contain recessed pockets to accommodate the crimps. Recessing the pockets helps to keep overall dimensions as small as possible; and, 4) UHT SMA wires are used to satisfy the higher-speed/higher-temperature requirement.

Modern high-strength steels for heavily loaded gearing (a review of engineering patents)

NASA Astrophysics Data System (ADS)

Voronenko, B. I.

1996-08-01

In order to increase the service life of machines the life of their parts should be increased. For example, in machine tool and lifting-and-transport manufacture the maintenance cost of the equipment over the duration of its operation often exceeds the cost of the new equipment by a factor of 10-20. This imposes strict requirements on structural materials for heavily loaded gearings, including the development of high-strength, wear-resistant, manufacture-adaptable, and economically alloyed steels.

Constitutive modeling of the mechanical behavior of high strength ferritic steels for static and dynamic applications

NASA Astrophysics Data System (ADS)

Abed, Farid H.

2010-11-01

A constitutive relation is presented in this paper to describe the plastic behavior of ferritic steel over a broad range of temperatures and strain rates. The thermo-mechanical behavior of high strength low alloy (HSLA-65) and DH-63 naval structural steels is considered in this study at strains over 40%. The temperatures and strain rates are considered in the range where dynamic strain aging is not effective. The concept of thermal activation analysis as well as the dislocation interaction mechanism is used in developing the flow model for both the isothermal and adiabatic viscoplastic deformation. The flow stresses of the two steels are very sensitive to temperature and strain rate, the yield stresses increase with decreasing temperatures and increasing strain rates. That is, the thermal flow stress is mainly captured by the yield stresses while the hardening stresses are totally pertained to the athermal component of the flow stress. The proposed constitutive model predicts results that compare very well with the measured ones at initial temperature range of 77 K to 1000 K and strain rates between 0.001 s-1 and 8500 s-1 for both steels.

Niobium Application, Metallurgy and Global Trends in Pressure Vessel Steels

NASA Astrophysics Data System (ADS)

Jansto, Steven G.

Niobium-containing high strength steel materials have been developed for a variety of pressure vessel applications. Through the application of these Nb-bearing steels in demanding applications, the designer and end user experience improved toughness at low temperature, excellent fatigue resistance and fracture toughness and excellent weldability. These enhancements provide structural engineers the opportunity to further improve the pressure vessel design and performance. The Nb-microalloy alloy designs also result in reduced operational production cost at the steel operation, thereby embracing the value-added attribute Nb provides to both the producer and the end user throughout the supply chain. For example, through the adoption of these Nb-containing structural materials, several design-manufacturing companies are considering improved designs which offer improved manufacturability, lower overall cost and better life cycle performance.

Fracture-tough, corrosion-resistant bearing steels

NASA Technical Reports Server (NTRS)

Olson, Gregory B.

1990-01-01

The fundamental principles allowing design of stainless bearing steels with enhanced toughness and stress corrosion resistance has involved both investigation of basic phenomena in model alloys and evaluation of a prototype bearing steel based on a conceptual design exercise. Progress in model studies has included a scanning Auger microprobe (SAM) study of the kinetics of interfacial segregation of embrittling impurities which compete with the kinetics of alloy carbide precipitation in secondary hardening steels. These results can define minimum allowable carbide precipitation rates and/or maximum allowable free impurity contents in these ultrahigh strength steels. Characterization of the prototype bearing steel designed to combine precipitated austenite transformation toughening with secondary hardening shows good agreement between predicted and observed solution treatment response including the nature of the high temperature carbides. An approximate equilibrium constraint applied in the preliminary design calculations to maintain a high martensitic temperature proved inadequate, and the solution treated alloy remained fully austenitic down to liquid nitrogen temperature rather than transforming above 200 C. The alloy can be martensitically transformed by cryogenic deformation, and material so processed will be studied further to test predicted carbide and austenite precipitation behavior. A mechanistically-based martensitic kinetic model was developed and parameters are being evaluated from available kinetic data to allow precise control of martensitic temperatures of high alloy steels in future designs. Preliminary calculations incorporating the prototype stability results suggest that the transformation-toughened secondary-hardening martensitic-stainless design concept is still viable, but may require lowering Cr content to 9 wt. pct. and adding 0.5 to 1.0 wt. pct. Al. An alternative design approach based on strain-induced martensitic transformation during cryogenic forming, thus removing the high martensitic constraint, may permit alloy compositions offering higher fracture roughness.

Metallurgical and Mechanical Evaluation of 4340 Steel Produced by Direct Metal Laser Sintering

NASA Astrophysics Data System (ADS)

Jelis, Elias; Clemente, Matthew; Kerwien, Stacey; Ravindra, Nuggehalli M.; Hespos, Michael R.

2015-03-01

Direct metal laser sintering (DMLS) was used to produce high-strength low-alloy 4340 steel specimens. Mechanical and metallurgical analyses were performed on the specimens to determine the samples with the highest strengths and the least porosity. The optimal process parameters were thus defined based on the corresponding experimental conditions. Additionally, the effects of fabricating specimens with both virgin and recycled powders were studied. Scanning electron microscopy and electron-dispersive spectroscopy were performed on both types of powders to determine the starting morphology and composition. The initial tensile results are promising, suggesting that DMLS can produce specimens equal in strength to wrought materials. However, there is evidence of cracking on several of the heat-treated tensile specimens that is unexplained. Several theories point to disturbances in the build chamber environment that went undetected while the specimens were being fabricated.

Materials and processes for aircraft environmental controls in the 1990's

NASA Astrophysics Data System (ADS)

Delgrosso, E. J.; Zajac, T.; Tseka, J.

1980-10-01

Changes in materials and processes expected to be used in aircraft environmental control systems (ECS) in the 1990s are analyzed, and a forecast is presented. Results of the study show that the most advanced development would be in the use of a cast high strength alloy steel, i.e., a steel with below 8% alloy content, and a 225 KSI annealed tensile strength. To assure complete densification and enhancement of properties, the casting would be HIP, and modification of its surface chemistry could be achieved through ion implantation. As candidate methods for imparting surface protection, laser glazing and chemical vapor deposition are mentioned. The anticipated changes in the materials and techniques used for construction of ECS components are: the development of rapid solidification rate powders for the production of some alloy systems such as Al-Mg-Li, bearing alloy CRB-7, and titanium alloys, 'near-net-shape' processing, and the use of advanced fiber-reinforced plastics.

Effect of welding process on the microstructure and properties of dissimilar weld joints between low alloy steel and duplex stainless steel

NASA Astrophysics Data System (ADS)

Wang, Jing; Lu, Min-xu; Zhang, Lei; Chang, Wei; Xu, Li-ning; Hu, Li-hua

2012-06-01

To obtain high-quality dissimilar weld joints, the processes of metal inert gas (MIG) welding and tungsten inert gas (TIG) welding for duplex stainless steel (DSS) and low alloy steel were compared in this paper. The microstructure and corrosion morphology of dissimilar weld joints were observed by scanning electron microscopy (SEM); the chemical compositions in different zones were detected by energy-dispersive spectroscopy (EDS); the mechanical properties were measured by microhardness test, tensile test, and impact test; the corrosion behavior was evaluated by polarization curves. Obvious concentration gradients of Ni and Cr exist between the fusion boundary and the type II boundary, where the hardness is much higher. The impact toughness of weld metal by MIG welding is higher than that by TIG welding. The corrosion current density of TIG weld metal is higher than that of MIG weld metal in a 3.5wt% NaCl solution. Galvanic corrosion happens between low alloy steel and weld metal, revealing the weakness of low alloy steel in industrial service. The quality of joints produced by MIG welding is better than that by TIG welding in mechanical performance and corrosion resistance. MIG welding with the filler metal ER2009 is the suitable welding process for dissimilar metals jointing between UNS S31803 duplex stainless steel and low alloy steel in practical application.

Wear Behavior of an Ultra-High-Strength Eutectoid Steel

NASA Astrophysics Data System (ADS)

Mishra, Alok; Maity, Joydeep

2018-02-01

Wear behavior of an ultra-high-strength AISI 1080 steel developed through incomplete austenitization-based combined cyclic heat treatment is investigated in comparison with annealed and conventional hardened and tempered conditions against an alumina disk (sliding speed = 1 m s-1) using a pin-on-disk tribometer at a load range of 7.35-14.7 N. On a gross scale, the mechanism of surface damage involves adhesive wear coupled with abrasive wear (microcutting effects in particular) at lower loads. At higher loads, mainly the abrasive wear (both microcutting and microploughing mechanisms) and evolution of adherent oxide are observed. Besides, microhardness of matrix increases with load indicating substantial strain hardening during wear test. The rate of overall wear is found to increase with load. As-received annealed steel with the lowest initial hardness suffers from severe abrasive wear, thereby exhibiting the highest wear loss. Such a severe wear loss is not observed in conventional hardened and tempered and combined cyclic heat treatment conditions. Combined cyclic heat-treated steel exhibits the greatest wear resistance (lowest wear loss) due to its initial high hardness and evolution of hard abrasion-resistant tribolayer during wear test at higher load.

Combined Intercritical Annealing and Q&P Processing of Medium Mn Steel

NASA Astrophysics Data System (ADS)

De Cooman, Bruno C.; Lee, Seon Jong; Shin, Sunmi; Seo, Eun Jung; Speer, John G.

2017-01-01

The microstructure and mechanical properties of intercritically annealed medium Mn steel are dependent on the selection of the intercritical annealing (IA) temperature. While the yield strength (YS) decreases with increasing IA temperature, the ultimate tensile strength increases with increasing IA temperature. Strain aging phenomena, both static and dynamic, are also often observed. The present contribution shows that, by combining IA with the quench and partitioning processing of the intercritical austenite, it is possible to obtain non-aging mechanical properties which combine a high YS with an ultra-high tensile strength. These properties are particularly suitable for automotive parts related to passenger safety.

On the Processing of Martensitic Steels in Continuous Galvanizing Lines: Part 1

NASA Astrophysics Data System (ADS)

Song, Taejin; Kwak, Jaihyun; de Cooman, B. C.

2012-01-01

Whereas low-carbon (<0.2 mass pct) martensitic grades can be produced easily in continuous annealing processing lines equipped with the required cooling capacity, the thermal cycles in continuous galvanizing lines make it difficult to produce hot-dip Zn or Zn-alloy coated high-strength martensitic grades. This is because of the tempering processes occurring during dipping of the strip in the liquid Zn bath and, in the case of galvannealed sheet steel, the short thermal treatment required to achieve the alloying between the Zn and the steel. These short additional thermal treatments last less than 30 seconds but severely degrade the mechanical properties. Using a combination of internal friction, X-ray diffraction, and transmission electron microscopy, it is shown that the ultrafine-grained lath microstructure allows for a rapid dislocation recovery and carbide formation during the galvanizing processes. In addition, the effective dislocation pinning occurring during the galvannealing process results in strain localization and the suppression of strain hardening.

Magnesium for Crashworthy Components

NASA Astrophysics Data System (ADS)

Abbott, T.; Easton, M.; Schmidt, R.

Most applications of magnesium in automobiles are for nonstructural components. However, the light weight properties of magnesium make it attractive in structural applications where energy absorption in a crash is critical. Because most deformation in a crash occurs as bending rather than simple tension or compression, the advantages of magnesium are greater than anticipated simply from tensile strength to weight ratios. The increased thickness possible with magnesium strongly influences bending behavior and theoretical calculations suggest almost an order of magnitude greater energy absorption with magnesium compared to the same weight of steel. The strain rate sensitivity of steel is of concern for energy absorption. Mild steels exhibit a distinct yield point which increases with strain rate. At strain rates typical of vehicle impact, this can result in strain localization and poor energy absorption. Magnesium alloys with relatively low aluminum contents exhibit strain rate sensitivity, however, this is manifest as an increase in work hardening and tensile / yield ratio. This behavior suggests that the performance of magnesium alloys in terms of energy absorption actually improves at high strain rates.

A mechanical property and stress corrosion evaluation of Custom 455 stainless steel alloy

NASA Technical Reports Server (NTRS)

Montano, J. W.

1972-01-01

The mechanical and stress corrosion properties are presented of vacuum melted Custom 455 stainless steel alloy bar (1.0-inch diameter) and sheet (0.083-inch thick) material aged at 950 F, 1000 F, and 1050 F. Low temperature mechanical properties were determined at temperatures of 80 F, 0 F, -100 F, and -200 F. For all three aging treatments, the ultimate tensile and 0.2 percent offset yield strengths increased with decreasing test temperatures while the elongation held fairly constant down to -100 F and decreased at -200 F. Reduction in Area decreased moderately with decreasing temperature for the longitudinal round (0.250-inch diameter) specimens. Notched tensile strength and charpy V-notched impact strength decreased with decreasing test temperature. For all three aging treatments, no failures were observed in the unstressed specimens or the specimens stressed to 50, 75, and 100 percent of their yield strengths for 180 days of alternate immersion testing in a 3.5 percent NaCl solution. As indicated by the results of tensile tests performed after alternate immersion testing, the mechanical properties of Custom 455 alloy were not affected by stress or exposure under the conditions of the evaluation.

Low temperature physical properties of Co-35Ni-20Cr-10Mo alloy MP35N®

NASA Astrophysics Data System (ADS)

Lu, J.; Toplosky, V. J.; Goddard, R. E.; Han, K.

2017-09-01

Multiphase Co-35Ni-20Cr-10Mo alloy MP35N® is a high strength alloy with excellent corrosion resistance. Its applications span chemical, medical, and food processing industries. Thanks to its high modulus and high strength, it found applications in reinforcement of ultra-high field pulsed magnets. Recently, it has also been considered for reinforcement in superconducting wires used in ultra-high field superconducting magnets. For these applications, accurate measurement of its physical properties at cryogenic temperatures is very important. In this paper, physical properties including electrical resistivity, specific heat, thermal conductivity, and magnetization of as-received and aged samples are measured from 2 to 300 K. The electrical resistivity of the aged sample is slightly higher than the as-received sample, both showing a weak linear temperature dependence in the entire range of 2-300 K. The measured specific heat Cp of 430 J/kg-K at 295 K agrees with a theoretical prediction, but is significantly smaller than the values in the literature. The thermal conductivity between 2 and 300 K is in good agreement with the literature which is only available above 77 K. Magnetic property of MP35N® changes significantly with aging. The as-received sample exhibits Curie paramagnetism with a Curie constant C = 0.175 K. While the aged sample contains small amounts of a ferromagnetic phase even at room temperature. The measured MP35N® properties will be useful for the engineering design of pulsed magnets and superconducting magnets using MP35N® as reinforcement.

Approaches for springback reduction when forming ultra high-strength sheet metals

NASA Astrophysics Data System (ADS)

Radonjic, R.; Liewald, M.

2016-11-01

Nowadays, the automotive industry is challenged constantly by increasing environmental regulations and the continuous enhancement of standards with regard to passenger's safety (NCAP, Part 1). In order to fulfil the aforementioned requirements, the use of ultra high-strength steels in research and industrial applications is of high interest. When forming such materials, the main problem results from the large amount of springback which occurs after the release of the part. This paper shows the applicability of several approaches for the reduction of springback amount by forming of one hat channel shaped component. A novel approach for springack reduction which is based on forming with an alternating blank draw-in is presented as well. In this investigation an ultra high-strength steel of the grade DP 980 was used. The part's measurements were taken at significant cross-sections in order to provide a qualitative comparison between the reference geometry and the part's released shape. The obtained results were analysed and used in order to quantify the success of particular approaches for springback reduction. When taking a curved hat channel shaped component as an example, the results achieved in the investigations showed that it is possible to reduce part shape deviations significantly when using DP 980 as workpiece material.

An in situ USAXS-SAXS-WAXS study of precipitate size distribution evolution in a model Ni-based alloy.

PubMed

Andrews, Ross N; Serio, Joseph; Muralidharan, Govindarajan; Ilavsky, Jan

2017-06-01

Intermetallic γ' precipitates typically strengthen nickel-based superalloys. The shape, size and spatial distribution of strengthening precipitates critically influence alloy strength, while their temporal evolution characteristics determine the high-temperature alloy stability. Combined ultra-small-, small- and wide-angle X-ray scattering (USAXS-SAXS-WAXS) analysis can be used to evaluate the temporal evolution of an alloy's precipitate size distribution (PSD) and phase structure during in situ heat treatment. Analysis of PSDs from USAXS-SAXS data employs either least-squares fitting of a preordained PSD model or a maximum entropy (MaxEnt) approach, the latter avoiding a priori definition of a functional form of the PSD. However, strong low- q scattering from grain boundaries and/or structure factor effects inhibit MaxEnt analysis of typical alloys. This work describes the extension of Bayesian-MaxEnt analysis methods to data exhibiting structure factor effects and low- q power law slopes and demonstrates their use in an in situ study of precipitate size evolution during heat treatment of a model Ni-Al-Si alloy.

An in situ USAXS–SAXS–WAXS study of precipitate size distribution evolution in a model Ni-based alloy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Andrews, Ross N.; Serio, Joseph A.; Muralidharan, Govindarajan

Intermetallic γ' precipitates typically strengthen nickel-based superalloys. The shape, size and spatial distribution of strengthening precipitates critically influence alloy strength, while their temporal evolution characteristics determine the high-temperature alloy stability. Combined ultra-small-, small- and wide-angle X-ray scattering (USAXS–SAXS–WAXS) analysis can be used to evaluate the temporal evolution of an alloy's precipitate size distribution (PSD) and phase structure duringin situheat treatment. Analysis of PSDs from USAXS–SAXS data employs either least-squares fitting of a preordained PSD model or a maximum entropy (MaxEnt) approach, the latter avoidinga prioridefinition of a functional form of the PSD. However, strong low-qscattering from grain boundaries and/or structuremore » factor effects inhibit MaxEnt analysis of typical alloys. Lastly, this work describes the extension of Bayesian–MaxEnt analysis methods to data exhibiting structure factor effects and low-qpower law slopes and demonstrates their use in anin situstudy of precipitate size evolution during heat treatment of a model Ni–Al–Si alloy.« less

An in situ USAXS–SAXS–WAXS study of precipitate size distribution evolution in a model Ni-based alloy

DOE PAGES

Andrews, Ross N.; Serio, Joseph A.; Muralidharan, Govindarajan; ...

2017-05-30

Intermetallic γ' precipitates typically strengthen nickel-based superalloys. The shape, size and spatial distribution of strengthening precipitates critically influence alloy strength, while their temporal evolution characteristics determine the high-temperature alloy stability. Combined ultra-small-, small- and wide-angle X-ray scattering (USAXS–SAXS–WAXS) analysis can be used to evaluate the temporal evolution of an alloy's precipitate size distribution (PSD) and phase structure duringin situheat treatment. Analysis of PSDs from USAXS–SAXS data employs either least-squares fitting of a preordained PSD model or a maximum entropy (MaxEnt) approach, the latter avoidinga prioridefinition of a functional form of the PSD. However, strong low-qscattering from grain boundaries and/or structuremore » factor effects inhibit MaxEnt analysis of typical alloys. Lastly, this work describes the extension of Bayesian–MaxEnt analysis methods to data exhibiting structure factor effects and low-qpower law slopes and demonstrates their use in anin situstudy of precipitate size evolution during heat treatment of a model Ni–Al–Si alloy.« less

HP9-4-.30 weld properties and microstructure

NASA Technical Reports Server (NTRS)

Watt, George W.

1991-01-01

HP9-4-.30, ultra high strength steel, the case material for the Advanced Solid Rocket Motor (ASRM), must exhibit acceptable strength, ductility, toughness, and stress corrosion cracking (SCC) resistance after welding and a local post weld heat treatment (PWHT). Testing, to date, shows that the base metal (BM) properties are more than adequate for the anticipated launch loads. Tensile tests of test specimens taken transverse to the weld show that the weld metal overmatches the BM even in the PWHT condition. However, that is still some question about the toughness and SCC resistance of the weld metal in the as welded and post weld heat treated condition. To help clarify the as welded and post weld heat treated mechanical behavior of the alloy, subsize tensile specimens from the BM, the fusion zone (FZ) with and without PWHT, and the heat affected zone (HAZ) with and without PWHT were tested to failure and the fracture surfaces subsequently examined with a scanning electron microscope. Results are given and briefly discussed.

Tensile and Fatigue Properties of Single and Multiple Dissimilar Welded Joints of DP980 and HSLA

NASA Astrophysics Data System (ADS)

Cui, Q. L.; Parkes, D.; Westerbaan, D.; Nayak, S. S.; Zhou, Y.; Saha, D. C.; Liu, D.; Goodwin, F.; Bhole, S.; Chen, D. L.

2017-02-01

The present study focused on single and multiple dissimilar joints between DP980 and high-strength low-alloy (HSLA) galvanized steels. The tensile properties of the dissimilar joint between the strong DP980 and the relatively soft HSLA reflected only the properties of HSLA with plastic deformation, and final fracture took place entirely in HSLA. The fatigue properties of the dissimilar joints were more intriguing, with the strong DP980 outperforming at high stress amplitude and the ductile HSLA outperforming at low stress amplitude. For different load amplitudes, fatigue failure occurred in different materials and at different locations. The fatigue strength of DP980 was more negatively impaired by weld defects than that of HSLA.

Crack Resistance of Welded Joints of Pipe Steels of Strength Class K60 of Different Alloying Systems

NASA Astrophysics Data System (ADS)

Tabatchikova, T. I.; Tereshchenko, N. A.; Yakovleva, I. L.; Makovetskii, A. N.; Shander, S. V.

2018-03-01

The crack resistance of welded joints of pipe steels of strength class K60 and different alloying systems is studied. The parameter of the crack tip opening displacement (CTOD) is shown to be dependent on the size of the austenite grains and on the morphology of bainite in the superheated region of the heat-affected zone of the weld. The crack resistance is shown to be controllable due to optimization of the alloying system.

Development of high strength ferritic steel for interconnect application in SOFCs

NASA Astrophysics Data System (ADS)

Froitzheim, J.; Meier, G. H.; Niewolak, L.; Ennis, P. J.; Hattendorf, H.; Singheiser, L.; Quadakkers, W. J.

High-Cr ferritic model steels containing various additions of the refractory elements Nb and/or W were studied with respect to oxidation behaviour (hot) tensile properties, creep behaviour and high-temperature electrical conductivity of the surface oxide scales. Whereas W additions of around 2 wt.% had hardly any effect on the oxidation rates at 800 and 900 °C, Nb additions of 1% led to a substantially enhanced growth rate of the protective surface oxide scale. It was found that this adverse effect can be alleviated by suitable Si additions. This is related to the incorporation of Si and Nb into Laves phase precipitates which also contribute to increased creep and hot tensile strength. The dispersion of Laves phase precipitates was greatly refined by combined additions of Nb and W. The high-temperature electrical conductivity of the surface oxide scales was similar to that of the Nb/W-free alloys. Thus the combined additions of Nb, W and Si resulted in an alloy with oxidation resistance, ASR contribution and thermal expansion comparable to the commercial alloy Crofer 22 APU, but with creep strength far greater than that of Crofer 22 APU.

Development of Highly Ductile Spheroidized Steel from High C (0.61 wt.% C) Low-Alloy Steel

NASA Astrophysics Data System (ADS)

Monia, S.; Varshney, A.; Gouthama; Sangal, S.; Kundu, S.; Samanta, S.; Mondal, K.

2015-11-01

This research aims to develop a multiphase steel combining spheroidal cementite and bainite in ductile ferrite matrix possessing an optimal balance of reasonably high strength and excellent ductility. A high carbon (0.61 wt.%) high silicon (1.71 wt.%) EN45 spring steel was annealed to obtain ferrite pearlite microstructure. The samples were given 5 and 10% cold rolling followed by holding at temperature below Ac1 for about 3 h. The samples were then held in intercritical range at 770 °C temperature for different durations ranging from 5 to 20 min for partial re-austenitization followed by quenching in a salt bath maintained at 350 °C and holding for 10 min to get bainite. The samples were finally water quenched. Characterizations of the samples with the help of optical microscopy, x-ray diffraction, scanning electron microscopy, and atomic force microscopy were carried out. Optimal heat-treatment conditions were found out after correlating with tensile properties. The best combination of high tensile strength (~800 MPa) with very high elongation (~29%) was obtained. Effects of cold-rolled strain and holding time in the intercritical region on the mechanical properties and microstructural changes were studied. Finally, structural property correlation is established.

Isothermal Treatment Effects on Precipitates and Tensile Properties of an HSLA Steel

NASA Astrophysics Data System (ADS)

Kim, J.-E.; Seol, J.-B.; Choi, W.-M.; Lee, B.-J.; Park, C.-G.

2018-05-01

The relationships between tensile properties and precipitates of a high-strength low-alloy steel depending on the isothermal conditions were investigated. While the isothermally treated steel at 300-500 °C for 1 and 24 h had no significant difference, the steel treated at 500 for 336 h, denoted as 500-336 h, not only showed a decrease in tensile stress but also exhibited a highly increased elongation. Transmission electron microscopy and atom probe tomography were utilized to evaluate the precipitates distribution. The results showed that, in the case of 500-336 h sample, the fraction of precipitates with a radius over 10 nm is the highest and that of a few nano-sized precipitates is the lowest among all samples. It can be explained that the coarsening of originally nano-sized precipitates, occurred by diffusion of dissolved carbon in 500-336 h, mainly affects the tensile behavior.

Effect of Alloying on the Strength Properties and the Hardening Mechanisms of Nitrogen-Bearing Austenitic Steels after Hot Deformation and Annealing

NASA Astrophysics Data System (ADS)

Bannykh, I. O.

2017-11-01

The main mechanisms of hardening nitrogen-bearing austenitic steels that operate under various thermomechanical treatment conditions at various steel compositions are considered. The strength properties of the steels are shown to depend on the content of interstitial elements, namely, carbon and nitrogen, and the influence of these elements on the stacking fault energy is estimated. The ratios of the main alloying elements that favor an increase or a decrease in the stacking fault energy are found to achieve the desirable level of strain hardening provided that an austenitic structure of steel is retained.

Effects of combined silicon and molybdenum alloying on the size and evolution of microalloy precipitates in HSLA steels containing niobium and titanium

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pavlina, Erik J., E-mail: e.pavlina@deakin.edu.au; Van Tyne, C.J.; Speer, J.G.

2015-04-15

The effects of combined silicon and molybdenum alloying additions on microalloy precipitate formation in austenite after single- and double-step deformations below the austenite no-recrystallization temperature were examined in high-strength low-alloy (HSLA) steels microalloyed with titanium and niobium. The precipitation sequence in austenite was evaluated following an interrupted thermomechanical processing simulation using transmission electron microscopy. Large (~ 105 nm), cuboidal titanium-rich nitride precipitates showed no evolution in size during reheating and simulated thermomechanical processing. The average size and size distribution of these precipitates were also not affected by the combined silicon and molybdenum additions or by deformation. Relatively fine (< 20more » nm), irregular-shaped niobium-rich carbonitride precipitates formed in austenite during isothermal holding at 1173 K. Based upon analysis that incorporated precipitate growth and coarsening models, the combined silicon and molybdenum additions were considered to increase the diffusivity of niobium in austenite by over 30% and result in coarser precipitates at 1173 K compared to the lower alloyed steel. Deformation decreased the size of the niobium-rich carbonitride precipitates that formed in austenite. - Highlights: • We examine combined Si and Mo additions on microalloy precipitation in austenite. • Precipitate size tends to decrease with increasing deformation steps. • Combined Si and Mo alloying additions increase the diffusivity of Nb in austenite.« less

Graded High-Strength Spring-Steels by a Special Inductive Heat T reatment

NASA Astrophysics Data System (ADS)

Tump, A.; Brandt, R.

2016-03-01

A method for effective lightweight design is the use of materials with high specific strength. As materials e.g. titanium are very expensive, steel is still the most important material for manufacturing automotive components. Steel is cost efficient, easy to recycle and its tensile strength easily exceeds 2,000 MPa by means of modern QT-technology (Quenched and Tempered). Therefore, lightweight design is still feasible in spite of the high density of steel. However, a further increase of tensile strength is limited, especially due to an increasing notch sensitivity and exposure to a corrosive environment. One solution is a special QT-process for steel, which creates a hardness gradient from the surface to the core of the material. This type of tailored material possesses a softer layer, which improves material properties such as fracture toughness and notch sensitivity. This leads to a better resistance to stress corrosion cracking and corrosion fatigue. Due to this optimization, a weight reduction is feasible without the use of expensive alloying elements. To understand the damage mechanism a comprehensive testing procedure was performed on homogeneous and gradient steels. Some results regarding the fracture mechanic behavior of such steels will be discussed.

Investigation of attenuation coefficients of some stainless steel and aluminum alloys

NASA Astrophysics Data System (ADS)

Caner, Zafer; Tufan, Mustafa ćaǧatay

2018-02-01

In this study, attenuation coefficients of two different stainless steel alloys (AISI 304 and AISI 310), which have a wide range of applications from home appliances to the automotive sector, and two different aluminum alloys (6013 and 5083), which have a high mechanical strength and a light weight structure and are used in many fields from aviation to military vehicles, has been determined. For this purpose, we used gamma spectrometer system with NaI(Tl) detector. In our measurements, we used Eu-152, Ra-226 and Co-60 as gamma ray sources. To narrow the beam of gamma rays, we designed the new steel based collimator. We also investigated the effect of using collimator. Obtained results were compared with the NIST XCOM values.

The Delayed Fracture of Aluminum Alloys, End of Year Report.

DTIC Science & Technology

1982-03-01

Corrosion Cracking of Maraging Steel ," Corrosion NACE, 1971, vol. 27, no. 10, pp. 429-433. 17. J.C.M. Li, R.A. Oriani, and L.S. Darken: "The...Park, OH, 1974, p. 274. 32. M.V. Hyatt and M.O. Speidel: Chapter 4 of Stress- Corrosion Cracking in High Strength Steels and in Titanium and Aluminum...reverse side it necessary and identify by block number) Aluminum alloys, stress corrosion cracking, oxide film, Auger electron spectroscopy, Mode I

Heat and corrosion resistant cast CF8C stainless steel with improved high temperature strength and ductility

DOEpatents

Maziasz, Philip J.; McGreevy, Tim; Pollard, Michael James; Siebenaler, Chad W.; Swindeman, Robert W.

2006-12-26

A CF8C type stainless steel alloy and articles formed therefrom containing about 18.0 weight percent to about 22.0 weight percent chromium and 11.0 weight percent to about 14.0 weight percent nickel; from about 0.05 weight percent to about 0.15 weight percent carbon; from about 2.0 weight percent to about 10.0 weight percent manganese; and from about 0.3 weight percent to about 1.5 weight percent niobium. The present alloys further include less than 0.15 weight percent sulfur which provides high temperature strength both in the matrix and at the grain boundaries without reducing ductility due to cracking along boundaries with continuous or nearly-continuous carbides. The disclosed alloys also have increased nitrogen solubility thereby enhancing strength at all temperatures because nitride precipitates or nitrogen porosity during casting are not observed. The solubility of nitrogen is dramatically enhanced by the presence of manganese, which also retains or improves the solubility of carbon thereby providing additional solid solution strengthening due to the presence of manganese and nitrogen, and combined carbon.

Heat and corrosion resistant cast CF8C stainless steel with improved high temperature strength and ductility

DOEpatents

Maziasz, Philip J.; McGreevy, Tim; Pollard, Michael James; Siebenaler, Chad W.; Swindeman, Robert W.

2010-08-17

A CF8C type stainless steel alloy and articles formed therefrom containing about 18.0 weight percent to about 22.0 weight percent chromium and 11.0 weight percent to about 14.0 weight percent nickel; from about 0.05 weight percent to about 0.15 weight percent carbon; from about 2.0 weight percent to about 10.0 weight percent manganese; and from about 0.3 weight percent to about 1.5 weight percent niobium. The present alloys further include less than 0.15 weight percent sulfur which provides high temperature strength both in the matrix and at the grain boundaries without reducing ductility due to cracking along boundaries with continuous or nearly-continuous carbides. The disclosed alloys also have increased nitrogen solubility thereby enhancing strength at all temperatures because nitride precipitates or nitrogen porosity during casting are not observed. The solubility of nitrogen is dramatically enhanced by the presence of manganese, which also retains or improves the solubility of carbon thereby providing additional solid solution strengthening due to the presence of manganese and nitrogen, and combined carbon.

The Effects of Casting Porosity on the Tensile Behavior of Investment Cast 17-4PH Stainless Steel

NASA Astrophysics Data System (ADS)

Susan, D. F.; Crenshaw, T. B.; Gearhart, J. S.

2015-08-01

The effect of casting porosity on the mechanical behavior of investment cast 17-4PH stainless steel was studied as well as the effect of heat treatment on the alloy's sensitivity to casting defects. Interdendritic porosity, formed during solidification and shrinkage of the alloy, reduces the yield strength and ultimate tensile strength roughly in proportion to the reduction in load bearing cross-section. The effects of casting porosity on ductility (% strain, % reduction in area) are more severe, in agreement with research on other alloy systems. In this study, 10% porosity reduced the ductility of 17-4PH stainless steel by almost 80% for the high-strength H925 condition. Tensile testing at -10°C (263 K) further reduces the alloy ductility with and without pores present. In the lower strength H1100 condition, the ductility is higher than the H925 condition, as expected, and somewhat less sensitive to porosity. By measuring the area % porosity on the fracture surface of tensile specimens, the trend in failure strain versus area % porosity was obtained and analyzed using two methods: an empirical approach to determine an index of defect susceptibility with a logarithmic fit and an analytical approach based on the constitutive stress-strain behavior and critical strain concentration in the vicinity of the casting voids. The applicability of the second method depends on the amount of non-uniform strain (necking) and, as such, the softer H1100 material did not correlate well to the model. The behavior of 17-4PH was compared to previous work on cast Al alloys, Mg alloys, and other cast materials.

Dissimilar Impact Welding of 6111-T4, 5052-H32 Aluminum Alloys to 22MnB5, DP980 Steels and the Structure-Property Relationship of a Strongly Bonded Interface

NASA Astrophysics Data System (ADS)

Liu, Bert; Vivek, Anupam; Presley, Michael; Daehn, Glenn S.

2018-03-01

The ability to weld high-strength aluminum to high-strength steel is highly desired for vehicle lightweighting but difficult to attain by conventional means. In this work, vaporizing foil actuator welding was used to successfully weld four Al/Fe combinations consisting of high-strength alloys: AA5052-H32, AA6111-T4, DP980, and 22MnB5. Flyer velocities up to 727 m/s were reached using 10 kJ input energy. In lap-shear testing, samples primarily failed in base aluminum near the aluminum's native strength, showing that the welds were stronger than a base metal and that the base metal was not significantly weakened by the welding process. A particularly strong weld area was studied by transmission electron microscopy to shed light on the microstructural features of strong impact welds. It was found to be characterized by a continuously bonded, fully crystalline interface, extremely fine (nanoscale) grains, mesoscopic as well as microscopic wavy features, and lack of large continuous intermetallic compounds.

Metastable high-entropy dual-phase alloys overcome the strength-ductility trade-off.

PubMed

Li, Zhiming; Pradeep, Konda Gokuldoss; Deng, Yun; Raabe, Dierk; Tasan, Cemal Cem

2016-06-09

Metals have been mankind's most essential materials for thousands of years; however, their use is affected by ecological and economical concerns. Alloys with higher strength and ductility could alleviate some of these concerns by reducing weight and improving energy efficiency. However, most metallurgical mechanisms for increasing strength lead to ductility loss, an effect referred to as the strength-ductility trade-off. Here we present a metastability-engineering strategy in which we design nanostructured, bulk high-entropy alloys with multiple compositionally equivalent high-entropy phases. High-entropy alloys were originally proposed to benefit from phase stabilization through entropy maximization. Yet here, motivated by recent work that relaxes the strict restrictions on high-entropy alloy compositions by demonstrating the weakness of this connection, the concept is overturned. We decrease phase stability to achieve two key benefits: interface hardening due to a dual-phase microstructure (resulting from reduced thermal stability of the high-temperature phase); and transformation-induced hardening (resulting from the reduced mechanical stability of the room-temperature phase). This combines the best of two worlds: extensive hardening due to the decreased phase stability known from advanced steels and massive solid-solution strengthening of high-entropy alloys. In our transformation-induced plasticity-assisted, dual-phase high-entropy alloy (TRIP-DP-HEA), these two contributions lead respectively to enhanced trans-grain and inter-grain slip resistance, and hence, increased strength. Moreover, the increased strain hardening capacity that is enabled by dislocation hardening of the stable phase and transformation-induced hardening of the metastable phase produces increased ductility. This combined increase in strength and ductility distinguishes the TRIP-DP-HEA alloy from other recently developed structural materials. This metastability-engineering strategy should thus usefully guide design in the near-infinite compositional space of high-entropy alloys.

Metastable high-entropy dual-phase alloys overcome the strength-ductility trade-off

NASA Astrophysics Data System (ADS)

Li, Zhiming; Pradeep, Konda Gokuldoss; Deng, Yun; Raabe, Dierk; Tasan, Cemal Cem

2016-06-01

Metals have been mankind’s most essential materials for thousands of years; however, their use is affected by ecological and economical concerns. Alloys with higher strength and ductility could alleviate some of these concerns by reducing weight and improving energy efficiency. However, most metallurgical mechanisms for increasing strength lead to ductility loss, an effect referred to as the strength-ductility trade-off. Here we present a metastability-engineering strategy in which we design nanostructured, bulk high-entropy alloys with multiple compositionally equivalent high-entropy phases. High-entropy alloys were originally proposed to benefit from phase stabilization through entropy maximization. Yet here, motivated by recent work that relaxes the strict restrictions on high-entropy alloy compositions by demonstrating the weakness of this connection, the concept is overturned. We decrease phase stability to achieve two key benefits: interface hardening due to a dual-phase microstructure (resulting from reduced thermal stability of the high-temperature phase); and transformation-induced hardening (resulting from the reduced mechanical stability of the room-temperature phase). This combines the best of two worlds: extensive hardening due to the decreased phase stability known from advanced steels and massive solid-solution strengthening of high-entropy alloys. In our transformation-induced plasticity-assisted, dual-phase high-entropy alloy (TRIP-DP-HEA), these two contributions lead respectively to enhanced trans-grain and inter-grain slip resistance, and hence, increased strength. Moreover, the increased strain hardening capacity that is enabled by dislocation hardening of the stable phase and transformation-induced hardening of the metastable phase produces increased ductility. This combined increase in strength and ductility distinguishes the TRIP-DP-HEA alloy from other recently developed structural materials. This metastability-engineering strategy should thus usefully guide design in the near-infinite compositional space of high-entropy alloys.

Enhancing steel properties through in situ formation of ultrahard ceramic surface

PubMed Central

Pahlevani, Farshid; Kumar, Rahul; Gorjizadeh, Narjes; Hossain, Rumana; Cholake, Sagar T; Privat, Karen; Sahajwalla, Veena

2016-01-01

Abrasion and corrosion resistant steel has attracted considerable interest for industrial application as a means of minimising the costs associated with product/component failures and/or short replacement cycles. These classes of steels contain alloying elements that increase their resistance to abrasion and corrosion. Their benefits, however, currently come at a potentially prohibitive cost; such high performance steel products are both more technically challenging and more expensive to produce. Although these methods have proven effective in improving the performance of more expensive, high-grade steel components, they are not economically viable for relatively low cost steel products. New options are needed. In this study, a complex industrial waste stream has been transformed in situ via precisely controlled high temperature reactions to produce an ultrahard ceramic surface on steel. This innovative ultrahard ceramic surface increases both the hardness and compressive strength of the steel. Furthermore, by modifying the composition of the waste input and the processing parameters, the ceramic surface can be effectively customised to match the intended application of the steel. This economical new approach marries industry demands for more cost-effective, durable steel products with global imperatives to address resource depletion and environmental degradation through the recovery of resources from waste. PMID:27929096

Enhancing steel properties through in situ formation of ultrahard ceramic surface.

PubMed

Pahlevani, Farshid; Kumar, Rahul; Gorjizadeh, Narjes; Hossain, Rumana; Cholake, Sagar T; Privat, Karen; Sahajwalla, Veena

2016-12-08

Abrasion and corrosion resistant steel has attracted considerable interest for industrial application as a means of minimising the costs associated with product/component failures and/or short replacement cycles. These classes of steels contain alloying elements that increase their resistance to abrasion and corrosion. Their benefits, however, currently come at a potentially prohibitive cost; such high performance steel products are both more technically challenging and more expensive to produce. Although these methods have proven effective in improving the performance of more expensive, high-grade steel components, they are not economically viable for relatively low cost steel products. New options are needed. In this study, a complex industrial waste stream has been transformed in situ via precisely controlled high temperature reactions to produce an ultrahard ceramic surface on steel. This innovative ultrahard ceramic surface increases both the hardness and compressive strength of the steel. Furthermore, by modifying the composition of the waste input and the processing parameters, the ceramic surface can be effectively customised to match the intended application of the steel. This economical new approach marries industry demands for more cost-effective, durable steel products with global imperatives to address resource depletion and environmental degradation through the recovery of resources from waste.

High damping Al-Fe-Mo-Si/Zn-Al composites produced by rapidly solidified powder metallurgy process

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, P.Y.; Dai, S.L.; Chai, S.C.

2000-05-10

The metallic materials commonly used in aircraft and aerospace fields, such as aluminum and titanium alloys, steels, etc., show extremely low damping capacity (usually of the order of or less than 10{sup {minus}3}). Thus, some problems related to vibration may emerge and influence the reliability, safety and life of airplanes, satellites, etc. It has been reported that almost two thirds of errors for rockets and satellites are related to vibration and noise. One effective way to solve these vibration-related problems is to adopt high damping metallic materials. Conventional high damping alloys exhibit damping capacity above 10{sup {minus}2}, however, their densitiesmore » are usually great than 5 x 10{sup 3} kg m{sup {minus}3}, or their strengths are less than 200 MPa (for alloys based on dislocation damping), making them impossible to be applied to aircraft and aerospace areas. Recently, some low-density high-damping metal/metal composites based on aluminum and high damping alloys have been developed in Beijing Institute of Aeronautical Materials (BIAM) by the rapidly solidified power metallurgy process. This paper aims to report the properties of the composites based on a high temperature Al-Fe-Mo-Si alloy and a high damping Zn-Al alloy, and compare them with that of 2618-T61 alloy produced by the ingot metallurgy process.« less

Welding Residual Stress Analysis and Fatigue Strength Assessment at Elevated Temperature for Multi-pass Dissimilar Material Weld Between Alloy 617 and P92 Steel

NASA Astrophysics Data System (ADS)

Lee, Juhwa; Hwang, Jeongho; Bae, Dongho

2018-03-01

In this paper, welding residual stress analysis and fatigue strength assessment were performed at elevated temperature for multi-pass dissimilar material weld between Alloy 617 and P92 steel, which are used in thermal power plant. Multi-pass welding between Alloy 617 and P92 steel was performed under optimized welding condition determined from repeated pre-test welding. In particular, for improving dissimilar material weld-ability, the buttering welding technique was applied on the P92 steel side before multi-pass welding. Welding residual stress distribution at the dissimilar material weld joint was numerically analyzed by using the finite element method, and compared with experimental results which were obtained by the hole-drilling method. Additionally, fatigue strength of dissimilar material weld joint was assessed at the room temperature (R.T), 300, 500, and 700 °C. In finite element analysis results, numerical peak values; longitudinal (410 MPa), transverse (345 MPa) were higher than those of experiments; longitudinal (298 MPa), transverse (245 MPa). There are quantitatively big differences between numerical and experimental results, due to some assumption about the thermal conductivity, specific heat, effects of enforced convection of the molten pool, dilution, and volume change during phase transformation caused by actual shield gas. The low fatigue limit at R.T, 300 °C, 500 °C and 700 °C was assessed to be 368, 276, 173 and 137 MPa respectively.

Welding Residual Stress Analysis and Fatigue Strength Assessment at Elevated Temperature for Multi-pass Dissimilar Material Weld Between Alloy 617 and P92 Steel

NASA Astrophysics Data System (ADS)

Lee, Juhwa; Hwang, Jeongho; Bae, Dongho

2018-07-01

In this paper, welding residual stress analysis and fatigue strength assessment were performed at elevated temperature for multi-pass dissimilar material weld between Alloy 617 and P92 steel, which are used in thermal power plant. Multi-pass welding between Alloy 617 and P92 steel was performed under optimized welding condition determined from repeated pre-test welding. In particular, for improving dissimilar material weld-ability, the buttering welding technique was applied on the P92 steel side before multi-pass welding. Welding residual stress distribution at the dissimilar material weld joint was numerically analyzed by using the finite element method, and compared with experimental results which were obtained by the hole-drilling method. Additionally, fatigue strength of dissimilar material weld joint was assessed at the room temperature (R.T), 300, 500, and 700 °C. In finite element analysis results, numerical peak values; longitudinal (410 MPa), transverse (345 MPa) were higher than those of experiments; longitudinal (298 MPa), transverse (245 MPa). There are quantitatively big differences between numerical and experimental results, due to some assumption about the thermal conductivity, specific heat, effects of enforced convection of the molten pool, dilution, and volume change during phase transformation caused by actual shield gas. The low fatigue limit at R.T, 300 °C, 500 °C and 700 °C was assessed to be 368, 276, 173 and 137 MPa respectively.

Characteristics of HY-180 and Ti-100 for Welded High Strength Structures

DTIC Science & Technology

1974-12-01

materials in welded structures are reported. The 10Ni-8Co-2Cr-lMo steel arid the Ti- 6Al -2Cb-lTa-0. 8Mo titanium alloy were selected as candidate...only li- 6Al -iCb-na-0.»Mo (Ti-6-2-1-1) and’Ii- 6Al - 4V are competitive with 10Ni-8Co-2Cr-lMo steel on a strength-weight basis, while possessing ade...Ti- 6Al -2Cb-lTa-0. 8Mo has better toughness in plate form, based upon dynamic tear properties. There- fore the Ti- 6Al -2Cb-lTa-0.8Mo titanium alloy

The electrochemical Evaluation of a Zr-Based Bulk Metallic Glass in a Phosphate-Buffered Saline Electrolyte

DOE Office of Scientific and Technical Information (OSTI.GOV)

Morrison, M. L.; Buchanan, R. A.; Leon, R. V.

2005-01-01

Bulk metallic glasses (BMGs) represent an emerging class of materials with an amorphous structure and a unique combination of properties. The objectives of this investigation were to define the electrochemical behavior of a specific Zr-based BMG alloy in a physiologically relevant environment and to compare these properties to standard, crystalline biomaterials as well as other Zr-based BMG compositions. Cyclic-anodic-polarization studies were conducted with a Zr{sub 52.5}Cu{sub 17.9}Ni{sub 14.6}Al{sub 10.0}Ti{sub 5.0} (at %) BMG in a phosphate-buffered saline electrolyte with a physiologically relevant oxygen content at 37 C. The results were compared to three common, crystalline biomaterials: CoCrMo, 316L stainless steel,more » and Ti-6Al-4V. The BMG alloy was found to have a lower corrosion penetration rate (CPR), as compared to the 316L stainless steel, and an equivalent CPR, as compared to the CoCrMo and Ti-6Al-4V alloys. Furthermore, the BMG alloy demonstrated better localized corrosion resistance than the 316L stainless steel. However, the localized corrosion resistance of the BMG alloy was not as high as those of the CoCrMo and Ti-6Al-4V alloys in the tested environment. The excellent electrochemical properties demonstrated by the BMG alloy are combined with a low modulus and unparalleled strength. This unique combination of properties dramatically demonstrates the potential for amorphous alloys as a new generation of biomaterials.« less

Fe-Mn(Al, Si) TWIP steel - strengthening characteristics and weldability

NASA Astrophysics Data System (ADS)

Podany, P.; Koukolikova, M.; Kubina, T.; Prochazka, R.; Franc, A.

2017-02-01

Twinning Induced Plasticity steel, or TWIP steel, has had increased interest in recent years from various industry sectors. This is due to it being lightweight, strong, and ductile; which are all properties that are useful in the automotive and aerospace industries. These steels potentially can offer lighter weight vehicles and parts with increased strength and other mechanical properties. This combination could offer greater fuel efficiency and performance while at the same time improving the safety features of the vehicle. This steel is characterised by being a high alloy steel, specifically having a high manganese content. It also has a fully austenitic microstructure at room temperature, which is a unique characteristic. But, for TWIP steel to be useful in various industrial sectors, it must have good weldability. This paper deals with the description of the strengthening due to the cold rolling on experimental heats of manganese steel with TRIP/TWIP effect. Impacts on microstructure, yield strength and tensile strength are described. Also, the weldability of experimental TWIP steel by studying the properties of weld joints after laser welding is described.

The corrosion performance of high chromium stainless steels and titanium alloys at a reverse osmosis plant in Arabian Gulf seawater

DOE Office of Scientific and Technical Information (OSTI.GOV)

Al-Odwani, A.; Al-Tabatabaei, M.; Carew, J.

1997-08-01

Electrochemical impedance spectroscopy (EIS) was used to evaluate the corrosion performance of four high chromium stainless steels and Grade 2 titanium in flowing Arabian Gulf natural seawater. The EIS provided information concerning the changes to the interfacial impedance as a function of exposure time for these alloys. The impedance spectra for all the alloys showed slight changes at the low frequency region over the exposure period. The open-circuit potentials (OCP) of these alloys were also monitored as a function of exposure time. The stainless steel alloys exhibited slight fluctuation in potential around the initial exposure potential. However, Grade 2 titaniummore » initial potential was more active and then gradually shifted towards the noble direction. The linear polarization resistance (LPR) method indicated that Grade 2 titanium exhibited the lowest corrosion rate with respect to the stainless steel alloys. The results of the EIS analysis and OCP indicated that Grade 2 titanium performed better than the four high chromium stainless steel alloys.« less

The effects of Ni, Mo, Ti and Si on the mechanical properties of Cr free Mn steel (Fe-25Mn-5Al-2C)

NASA Technical Reports Server (NTRS)

Schuon, S. R.

1982-01-01

The FeMnAlC alloys may hold potential as Cr-free replacements for high strategic material iron base superalloys, but little is known about their intermediate temperature (650 C to 870 C) mechanical properties. The effects of alloying elements on the mechanical properties of model FeMnAlC alloys were studied. Results showed that modified FeMnAlC alloys had promising short term, intermediate temperature properties but had relatively poor stress rupture lives at 172 MPa and 788 C. Room temperature and 788 C tensile strength of FeMnAlC alloys were better than common cast stainless steels. Changes in room temperature tensile and 788 C tensile strength and ductility, and 788 C stress rupture life were correlated with changes in Ni, Mo, Ti, and Si levels due to alloying effects on interstitial carbon levels and carbide morphology. Fe-25Mn-5Al-2C had a very poor stress rupture life at 172 MPa and 788 C. Addition of carbide-forming elements improved the stress rupture life.

Hydrogen Environment Assisted Cracking of Ultra-High Strength AetMet(Trademark) 100 Steel

DTIC Science & Technology

2006-01-01

landing gear. LV.B. Effect of Steel Composition on Intergranular HEAC Instances of intergranular HEAC and IiHAC in AerMetTm 100 were rarely observed in the...fit the H concentration effect with that of the other elements. While the Maraging and Custom 465TM steels are relatively pure, the H concentration...to -0.9 VsCE and increased cracking at more anodic and more cathodic potentials 471 . Similar effects were noted for HEAC of 18Ni Maraging steel , with

Microstructural-Scale Model for Surfaces Spreading of Intergranular Corrosion in Sensitized Stainless Steels and Aluminum-Magnesium (AA5XXX) Alloys

NASA Astrophysics Data System (ADS)

Jain, Swati

Components from AA5XXX (Al-Mg alloys with more than 3 wt% Mg) alloys are X attractive due to availability of low cost, high strength to weight ratio and good weldability. Therefore, these alloys have potential applications in Naval ships. However, these alloys become susceptible to IGC (intergranular corrosion) due to beta-phase precipitation due to improper heat treatment or inadvertent thermal exposure. Stainless steels may also become susceptible due to carbide precipitation and chromium depletion on grain boundaries. IGC susceptibility depends on the interplay between the metallurgical conditions, electrochemical conditions, and chemical conditions. Specific combinations cause IGC while others do not. The objective of this study is to investigate the conditions which bring about surface spreading of IGC in these alloy classes. To accomplish this goal, a microstructure scale model was developed with experimental inputs to understand the 2-D IGC spreading in stainless steels and AA5XXX alloys. The conditions strongly affecting IGC spreading were elucidated. Upon natural and artificial aging, the stainless steels become susceptible to intergranular corrosion because of chromium depletion in the grain boundaries. After aging Al-Mg (AA5XXX) alloys show susceptibility due to the precipitation of the beta-phase (Al3Mg7) in the grain boundaries. Chromium depleted grain boundaries in stainless steels are anodically more active as compared to the interior of the grains. (3-phase rich grain boundaries have lower OCP (open circuit potential) and pitting potentials as compared to the Al-Mg solid solutions. A new approach to modeling the IGC surface spreading in polycrystalline materials that is presented. This model is the first to couple several factors into one granular scale model that illustrates the way in which they interact and IGC occurs. It sheds new information on conditions which cause IGC spreading in two alloy classes and describes a new theory for the critical potential associated with IGC. The outcomes from this contribute to ways to advance the goal of corrosion resistant computational design of alloys, guiding mitigation strategies for suppressing IGC in existing alloys, and to damage prognosis aimed at predicting damage and structural integrity.

Selection And Evaluation Of An Alloy For Nozzle Application

NASA Technical Reports Server (NTRS)

Pandey, A. B.; Shah, S.; Shadoan, M.; Lyles, Garry (Technical Monitor)

2003-01-01

The present work includes results on material characterization conducted under COBRA Hydrogen Cooled Nozzle Program and was funded by NASA MSFC. The nozzle requires a material that has high strength at ambient and high (up to l200 F) temperatures in air and hydrogen. Presently, a precipitation hardened steel; A-286 is used in nozzles for Space Shuttle Engines. The A-286 alloy has limited hydrogen compatibility and weldability. The present work focused on selection and characterization of JBK-75 alloy that has significantly higher capability in hydrogen and weldability in addition to other attributes. The alloy was evaluated at different temperatures and environments. Tungsten Inert Gas (TIG) and Electron Beam welding techniques were used to evaluate the weldability of material. Brazing was also conducted on the alloy and evaluated. The characterization of base JBK-75 alloy, welded and brazed alloy included tensile properties, low cycle fatigue and crack growth resistance at different temperatures in air and hydrogen environments. The results indicated that JBK-75 has excellent tensile and fatigue properties in air and hydrogen. The welded and brazed alloy also showed very good properties.

Mechanical Properties and Microstructural Evolution of Welded Eglin Steel

NASA Astrophysics Data System (ADS)

Leister, Brett M.

Eglin steel is a new ultra-high strength steel that has been developed at Eglin Air Force Base in the early 2000s. This steel could be subjected to a variety of processing steps during fabrication, each with its own thermal history. This article presents a continuous cooling transformation diagram developed for Eglin steel to be used as a guideline during processing. Dilatometry techniques performed on a Gleeble thermo-mechanical simulator were combined with microhardness results and microstructural characterization to develop the diagram. The results show that four distinct microstructures form within Eglin steel depending on the cooling rate. At cooling rates above about 1 °C/s, a predominately martensitic microstructure is formed with hardness of ˜520 HV. Intermediate cooling rates of 1 °C/s to 0.2 °C/s produce a mixed martensitic/bainitic microstructure with a hardness that ranges from 520 - 420 HV. Slower cooling rates of 0.1 °C/s to 0.03 °C/s lead to the formation of a bainitic microstructure with a hardness of ˜420 HV. The slowest cooling rate of 0.01 °C/s formed a bainitic microstructure with pearlite at the prior austenite grain boundaries. A comprehensive study was performed to correlate the mechanical properties and the microstructural evolution in the heat affected zone of thermally simulated Eglin steel. A Gleeble 3500 thermo-mechanical simulator was used to resistively heat samples of wrought Eglin steel according to calculated thermal cycles with different peak temperatures at a heat input of 1500 J/mm. These samples underwent mechanical testing to determine strength and toughness, in both the `as-simulated' condition and also following post-weld heat treatments. Mechanical testing has shown that the inter-critical heat affected zone (HAZ) has the lowest strength following thermal simulation, and the fine-grain and coarse-grain heat affected zone having an increased strength when compared to the inter-critical HAZ. The toughness of the heat affected zone in the as-simulated condition is lower than that of the base metal. Post-weld heat treatments (PWHT) have been shown to increase the toughness of the HAZ, but at the expense of strength. In addition, certain combinations of PWHTs within specific HAZ regions have exhibited low toughness caused by tempered martensite embrittlement or intergranular failure. Synchrotron X-ray diffraction data has shown that Eglin steel has retained austenite in the fine-grain HAZ in the as-simulated condition. In addition, alloy carbides (M23C 6, M2C, M7C3) have been observed in the diffraction spectra for the fine-grain and coarse-grain HAZ following a PWHT of 700 °C / 4 hours. A first attempt at thermodynamic modeling has been undertaken using MatCalc to try to predict the evolution of carbides in the HAZ following thermal cycling and PWHT.

A Preliminary Report on the Strength and Metallography of a Bimetallic Friction Stir Weld Joint Between AA6061 and MIL-DTL-46100E High Hardness Steel Armor

DTIC Science & Technology

2012-11-26

alloy and High Hardness steel armor (MIL- STD-46100) were successfully joined by the friction stir welding (FSW) process using a tungsten- rhenium ...tungsten- rhenium stir tool. Process parameter variation experiments, which included inductive pre-heating, tool design geometry, plunge and traverse

9 Cr-- 1 Mo steel material for high temperature application

DOEpatents

Jablonski, Paul D; Alman, David; Dogan, Omer; Holcomb, Gordon; Cowen, Christopher

2012-11-27

One or more embodiments relates to a high-temperature, titanium alloyed, 9 Cr-1 Mo steel exhibiting improved creep strength and oxidation resistance at service temperatures up to 650.degree. C. The 9 Cr-1 Mo steel has a tempered martensite microstructure and is comprised of both large (0.5-3 .mu.m) primary titanium carbides and small (5-50 nm) secondary titanium carbides in a ratio of. from about 1:1.5 to about 1.5:1. The 9 Cr-1 Mo steel may be fabricated using exemplary austenizing, rapid cooling, and tempering steps without subsequent hot working requirements. The 9 Cr-1 Mo steel exhibits improvements in total mass gain, yield strength, and time-to-rupture over ASTM P91 and ASTM P92 at the temperature and time conditions examined.

Effect of cyclic treatment on the formation of a fragmented structure in a sparingly alloyed martensitic steel

NASA Astrophysics Data System (ADS)

Tabatchikova, T. I.; Yakovleva, I. L.; Delgado Reina, S. Yu.; Plokhikh, A. I.

2016-11-01

Methods of metallography and transmission electron microscopy were used to study the structure of a high-alloy low-carbon steel of martensitic VKS-10 class subjected to cyclic treatment according to different regimes. It has been found that the warm deformation in the α state at 700°C causes the fragmentation of the structure; however, the decomposition of the α solid solution and the precipitation of coarse carbides leads to a significant decrease in the strength. It has been shown that 12 cycles of treatment, including austenitizing at 1000°C, rolling at 700°C, and subsequent γ → α transformation during rapid cooling do not lead to a noticeable fragmentation of the structure. It has been found that the deformation of the overcooled austenite by rolling carried out using 12 cycles in the range of temperatures of 700-500°C and subsequent γ → α transformation lead to the formation of a fragmented structure with a large fraction of fine grains with a size less than 0.5 μm. This treatment and the subsequent tempering at 530°C for 1 h allow us to increase the strength and hardness of the VKS-10 steel at an insignificant decrease in the plasticity.

High hardness and superlative oxidation resistance in a pseudo-icosahehdral Cr-Al binary

NASA Astrophysics Data System (ADS)

Simonson, J. W.; Rosa, R.; Antonacci, A. K.; He, H.; Bender, A. D.; Pabla, J.; Adrip, W.; McNally, D. E.; Zebro, A.; Kamenov, P.; Geschwind, G.; Ghose, S.; Dooryhee, E.; Ibrahim, A.; Aronson, M. C.

Improving the efficiency of fossil fuel plants is a practical option for decreasing carbon dioxide emissions from electrical power generation. Present limits on the operating temperatures of exposed steel components, however, restrict steam temperatures and therefore energy efficiency. Even as a new generation of creep-resistant, high strength steels retain long term structural stability to temperatures as high as ~ 973 K, the low Cr-content of these alloys hinders their oxidation resistance, necessitating the development of new corrosion resistant coatings. We report here the nearly ideal properties of potential coating material Cr55Al229, which exhibits high hardness at room temperature as well as low thermal conductivity and superlative oxidation resistance at 973 K, with an oxidation rate at least three times smaller than those of benchmark materials. These properties originate from a pseudo-icosahedral crystal structure, suggesting new criteria for future research.

Ability of the total strain version of strainrange partitioning to characterize thermomechanical fatigue behavior

NASA Technical Reports Server (NTRS)

Saltsman, James F.; Halford, Gary R.

1994-01-01

Strainrange partitioning (SRP) was originally developed on an inelastic strain basis for isothermal fatigue in the high-strain regime where the inelastic strainrange could be determined accurately. However, most power-generating equipment operates in the regime where the inelastic strains are small and difficult to determine with any degree of accuracy. This shortcoming led to the development of the total strain version of SRP (TS-SRP). Power-generating equipment seldom operates under isothermal conditions, and isothermal life prediction methods cannot be depended on to predict the lives of anisothermal cycles. To overcome this shortcoming, a method was proposed for extending TS-SRP to characterize anisothermal fatigue behavior and to predict the lives of thermomechanical fatigue (TMF) cycles using apppropriate anisothermal data. The viability of this method, referred to as TMF/TS-SRP, was demonstrated using TMF data for two high-temperature aerospace alloys. In this report, data from the literature are used to examine the ability of TMF/TS-SRP to characterize the failure and flow behavior of three low-strength, high-ductility alloys widely used for ground-based power-generating equipment. The three alloys are type 304 stainless steel, 1Cr-1Mo-0.25V steel, and 2.25Cr-1Mo steel. Because of the limited nature of the data, it was possible to evaluate the characterization, but not the predictive capability of TMF/TS-SRP.

Noncyanide Stripper Placement Program. Phase 1

DTIC Science & Technology

1989-05-01

bronze (brazing material ) from low-alloy steels , heat and corrosion resistant...STRIPPERS AND BASIS MATERIALS FROM WHICH THE COATINGS ARE REMOVED (FROM T.O.42C2-1-7) Surface Coating Basis Material Brass Low-Alloy Steels Bronze Low...braze materials , low alloy steels , and heat and corrosion resistant steels . Additional tests were performed on three masking materials routinely

Study of Creep of Alumina-Forming Austenitic Stainless Steel for High-Temperature Energy Applications

NASA Astrophysics Data System (ADS)

Afonina, Natalie Petrovna

To withstand the high temperature (>700°C) and pressure demands of steam turbines and boilers used for energy applications, metal alloys must be economically viable and have the necessary material properties, such as high-temperature creep strength, oxidation and corrosion resistance, to withstand such conditions. One promising class of alloys potentially capable of withstanding the rigors of aggressive environments, are alumina-forming austenitic stainless steels (AFAs) alloyed with aluminum to improve corrosion and oxidation resistance. The effect of aging on the microstructure, high temperature constant-stress creep behavior and mechanical properties of the AFA-type alloy Fe-20Cr-30Ni-2Nb-5Al (at.%) were investigated in this study. The alloy's microstructural evolution with increased aging time was observed prior to creep testing. As aging time increased, the alloy exhibited increasing quantities of fine Fe2Nb Laves phase dispersions, with a precipitate-free zone appearing in samples with higher aging times. The presence of the L1 2 phase gamma'-Ni3Al precipitate was detected in the alloy's matrix at 760°C. A constant-stress creep rig was designed, built and its operation validated. Constant-stress creep tests were performed at 760°C and 35MPa, and the effects of different aging conditions on creep rate were investigated. Specimens aged for 240 h exhibited the highest creep rate by a factor of 5, with the homogenized sample having the second highest rate. Samples aged for 2.4 h and 24 h exhibited similar low secondary creep rates. Creep tests conducted at 700oC exhibited a significantly lower creep rate compared to those at 760oC. Microstructural analysis was performed on crept samples to explore high temperature straining properties. The quantity and size of Fe2Nb Laves phase and NiAl particles increased in the matrix and on grain boundaries with longer aging time. High temperature tensile tests were performed and compared to room temperature results. The high temperature results were significantly lower when compared to room temperature values. Higher creep rates were correlated with lower yield strengths.

Carburizing treatment of low alloy steels: Effect of technological parameters

NASA Astrophysics Data System (ADS)

Benarioua, Younes

2018-05-01

The surface areas of the parts subjected to mechanical loads influence to a great extent the resistance to wear and fatigue. In majority of cases, producing of a hard superficial layer on a tough substrate is conducive to an increased resistance to mechanical wear and fatigue. Cementation treatment of low alloy steels which bonds superficial martensitic layer of high hardness and lateral compressive to a core of lower hardness and greater toughness is an example of a good solution of the problem. The high hardness of the martensitic layer is due to an increased concentration of interstitial carbon atoms in the austenite before quenching. The lower hardness of the core after quenching is due to the presence of ferrite and pearlite components which appear if the cooling rate after austenitization becomes lower than the critical on. The objective of the present study was to obtain a cemented surface layer on low alloy steel by means of pack carburizing treatment. Different steel grades, austenitization temperatures as well as different soaking times were used as parameters of the pack carburizing treatment. During this treatment, carbon atoms from the pack powder diffuse toward the steels surface and form compounds of iron carbides. The effect of carburizing parameters on the transformation rate of low carbon surface layer of the low alloy steel to the cemented one was investigated by several analytical techniques.

Proving the viability of manufacturing of multi-layer steel/vanadium alloy/steel composite tubes by numerical simulations and experiment

NASA Astrophysics Data System (ADS)

Nechaykina, T.; Nikulin, S.; Rozhnov, A.; Molotnikov, A.; Zavodchikov, S.; Estrin, Y.

2018-05-01

Vanadium alloys are promising structural materials for fuel cladding tubes for fast-neutron reactors. However, high solubility of oxygen and nitrogen in vanadium alloys at operating temperatures of 700 °C limits their application. In this work, we present a novel composite structure consisting of vanadium alloy V-4Ti-4Cr (provides high long-term strength of the material) and stainless steel Fe-0.2C-13Cr (as a corrosion resistant protective layer). It is produced by co-extrusion of these materials forming a three-layered tube. Finite element simulations were utilised to explore the influence of the various co-extrusion parameters on manufacturability of multi-layered tubes. Experimental verification of the numerical modelling was performed using co-extrusion with the process parameters suggested by the numerical simulations. Scanning electron microscopy and microhardness measurements revealed a defect-free diffusion layer at the interfaces between both materials indicating a good quality bonding for these co-extrusion conditions.

Steel Alloy Hot Roll Simulations and Through-Thickness Variation Using Dislocation Density-Based Modeling

NASA Astrophysics Data System (ADS)

Jansen Van Rensburg, G. J.; Kok, S.; Wilke, D. N.

2017-10-01

Different roll pass reduction schedules have different effects on the through-thickness properties of hot-rolled metal slabs. In order to assess or improve a reduction schedule using the finite element method, a material model is required that captures the relevant deformation mechanisms and physics. The model should also report relevant field quantities to assess variations in material state through the thickness of a simulated rolled metal slab. In this paper, a dislocation density-based material model with recrystallization is presented and calibrated on the material response of a high-strength low-alloy steel. The model has the ability to replicate and predict material response to a fair degree thanks to the physically motivated mechanisms it is built on. An example study is also presented to illustrate the possible effect different reduction schedules could have on the through-thickness material state and the ability to assess these effects based on finite element simulations.

A Multiscale Meshfree Approach for Modeling Fragment Penetration into Ultra High-Strength Concrete

DTIC Science & Technology

2011-09-01

velocity history................................................................................ 62  Figure 53. Yield stress versus strain rate for steel ...Spherical steel projectile properties. ....................................................................................... 54  Table 3. J2 material...10000E  , Poisson’s ratio 0v  , and density 1  . Here the Poisson’s effect is purposely removed for the wave to propagate only in the axial

Influence of cryogenic treatment on microstructure and mechanical properties of high strength AISI D2 tool steel =

NASA Astrophysics Data System (ADS)

Ghasemi Nanesa, Hadi

Cryogenic treatment, known as treating materials at sub-zero temperatures, has been added to conventional heat treatment cycle of high alloyed steels where martensitic transformation is incomplete after quenching to room temperature. Incomplete martensitic transformation occurs due to the effect of high content of alloying elements on pushing down martensite start and finish temperatures to very low values, specifically, on tool steels. In spite of obtaining significant improvements in mechanical and wear properties after cryogenic treatment, there is no cohesive picture about what exactly modifies the microstructure of tool steels during cryogenic treatment and therefore divergent opinions on the influence of process parameters are still reported. For example, the suggested time length for cryogenic treatment starts from few seconds to several days indicating the lack of understanding about micromechanisms responsible for microstructural evolution while holding at cryogenic temperatures. In this regard, the main objective of this project is to develop a better understanding on the fundamental micromechanisms operating during cryogenic treatment. To attain this objective, the following milestones are pursued. - To study the conventional cryogenic treatment and finding challenges. - To identify and characterize the optimum starting microstructure before cryogenic treatment. - To determine the important processing parameters those control the evolution of microstructure and hardness. - To investigate the interaction between carbide precipitation and martensitic transformation in the AISI D2 steel. - To propose an optimal cryogenic treatment for AISI D2 steel.

Cracking Tendancies of Restrained Welds in High Strength Low Alloy Steels under Hyperbaric Conditions.

DTIC Science & Technology

1987-06-01

refinement of NICUAGE by addition of Chromium and Molybdenum with prescribed heat ’I. 24 [I.% treatments to even further lower the DBTT to -115 degrees F...sulpher a., reduces hi temp transformation products " provides solid solution strengthening copper - precipitation strengthening O chromium - optimize...contractors and oil companies include GTAW , GMAW, FCAW, and SMAW. My sense was -, that the most popular technique was the GTAW root pass * followed by the

An in situ USAXS–SAXS–WAXS study of precipitate size distribution evolution in a model Ni-based alloy1

PubMed Central

Andrews, Ross N.; Serio, Joseph; Muralidharan, Govindarajan; Ilavsky, Jan

2017-01-01

Intermetallic γ′ precipitates typically strengthen nickel-based superalloys. The shape, size and spatial distribution of strengthening precipitates critically influence alloy strength, while their temporal evolution characteristics determine the high-temperature alloy stability. Combined ultra-small-, small- and wide-angle X-ray scattering (USAXS–SAXS–WAXS) analysis can be used to evaluate the temporal evolution of an alloy’s precipitate size distribution (PSD) and phase structure during in situ heat treatment. Analysis of PSDs from USAXS–SAXS data employs either least-squares fitting of a preordained PSD model or a maximum entropy (MaxEnt) approach, the latter avoiding a priori definition of a functional form of the PSD. However, strong low-q scattering from grain boundaries and/or structure factor effects inhibit MaxEnt analysis of typical alloys. This work describes the extension of Bayesian–MaxEnt analysis methods to data exhibiting structure factor effects and low-q power law slopes and demonstrates their use in an in situ study of precipitate size evolution during heat treatment of a model Ni–Al–Si alloy. PMID:28656039

A Study of the Effect of Interrupted Quenches on a Thermomechanically Processed High Carbon Steel.

DTIC Science & Technology

1982-10-01

Martensite And Austenite Phases In Steel Using Copper Radiation ---------------------------- 38 4° J !7...34A General Equa- tion Prescribing the Extent of the Austenite- Martensite Transformation in Pure Iron-Carbon Alloys and Plain Carbon Steels ," Acta Met...relatively low temperatures, resulting in incomplete disso- lution of alloy carbides, predominantly Fe-Cr complexes. In some instances 52100 steel is

Solubility of Nitrogen in Superaustenitic Stainless Steels During Air Induction Melting

NASA Astrophysics Data System (ADS)

Chandrasekar, A.; Anburaj, J.; Narayanan, R.; Balusamy, V.; Mohamed Nazirudeen, S. S.

2013-04-01

The amount of nitrogen contained in super austenitic stainless steels (SASS) influences their properties significantly. The effect of maximum amount of nitrogen in the highly alloyed Cr and Ni SASS containing further additions of Mo and Mn is studied. The calculated nitrogen contents of the experimental alloys are compared with the actual nitrogen contents obtained in the alloys produced using induction melting furnace. The actual nitrogen content of the alloys is always lower than the calculated value, and this discrepancy is due to the presence of positive interaction parameters of Ni, Cu, and Si in the alloy. However, the yield of nitrogen in the liquid SASS is improved significantly with additions of Mn and Mo contents. The construction of multicomponent phase diagrams for SASS is demonstrated using Thermo-Calc software. SASS containing more nitrogen exhibited a very high strength without loss of toughness.

Effect of aluminizing of Cr-containing ferritic alloys on the seal strength of a novel high-temperature solid oxide fuel cell sealing glass

NASA Astrophysics Data System (ADS)

Chou, Yeong-Shyung; Stevenson, Jeffry W.; Singh, Prabhakar

A novel high-temperature alkaline earth silicate sealing glass was developed for solid oxide fuel cell (SOFC) applications. The glass was used to join two metallic coupons of Cr-containing ferritic stainless steel for seal strength evaluation. In previous work, SrCrO 4 was found to form along the glass/steel interface, which led to severe strength degradation. In the present study, aluminization of the steel surface was investigated as a remedy to minimize or prevent the strontium chromate formation. Three different processes for aluminization were evaluated with Crofer22APU stainless steel: pack cementation, vapor-phase deposition, and aerosol spraying. It was found that pack cementation resulted in a rough surface with occasional cracks in the Al-diffused region. Vapor-phase deposition yielded a smoother surface, but the resulting high Al content increased the coefficient of thermal expansion (CTE), resulting in the failure of joined coupons. Aerosol spraying of an Al-containing salt resulted in the formation of a thin aluminum oxide layer without any surface damage. The room temperature seal strength was evaluated in the as-fired state and in environmentally aged conditions. In contrast to earlier results with uncoated Crofer22APU, the aluminized samples showed no strength degradation even for samples aged in air. Interfacial and chemical compatibility was also investigated. The results showed aluminization to be a viable candidate approach to minimize undesirable chromate formation between alkaline earth silicate sealing glass and Cr-containing interconnect alloys for SOFC applications.

Heat-Resistant Alloys for Ordnance Materiel and Aircraft and Naval Engine Parts (N-102): Part 1 - Heat Resistant Alloys of the 21%Cr:9%Ni Type

DTIC Science & Technology

1945-06-29

10.555Ni Alloy 22 Sigma and Ferrite In 22.3#r:7.7*Ni Alloy 23 Ferrite Mosaic In 22.3#r:7.7#Ni Alloy 24 Precipitated Carbides In 21.2*Cr:8.7*Ni... ferritic steels and heat resistant cast irons are widely applied. Where plasticity is essential,steels must be used. The irons exhibit some...ductility above 900°F, but they are seldom able to survive sudden thermal or mechanical stresses that exceed their elastic strength. Ferritic steels, of

Creep and microstructural processes in a low-alloy 2.25%Cr1.6%W steel (ASTM Grade 23)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kucharova, K.; Sklenicka, V., E-mail: sklen@ipm.cz; CEITEC — IPM, Institute of Physics of Materials, Academy of Sciences of the Czech Republic, CZ-616 62 Brno

2015-11-15

A low-alloy 2.25%Cr1%Mo steel (ASTM Grade 22) has been greatly improved by the substitution of almost all of the 1%Mo by 1.6%W. The improved material has been standardized as P/T23 steel (Fe–2.25Cr–1.6W–0.25V–0.05Nb–0.07C). The present investigation was conducted on T23 steel in an effort to obtain a more complete description and understanding of the role of the microstructural evolution and deformation processes in high-temperature creep. Constant load tensile creep tests were carried out in an argon atmosphere in the temperature range 500–650 °C at stresses ranging from 50 to 400 MPa. It was found that the diffusion in the matrix latticemore » is the creep-rate controlling process. The results of an extensive transmission electron microscopy (TEM) analysis programme to investigate microstructure evolution as a function of temperature are described and compared with the thermodynamic calculations using the software package Thermo-Calc. The significant creep-strength drop of T23 steel after long-term creep exposures can be explained by the decrease in dislocation hardening, precipitation hardening and solid solution hardening due to the instability of the microstructure at high temperature. - Highlights: • The constant load creep tests of T23 steel were carried out at 500–650 °C. • The stress exponents of the creep rate correspond to power law (dislocation) creep. • Diffusion in the matrix lattice is the creep-rate controlling process. • The microstructure instability is the main creep degradation process in T23 steel.« less

Anomolous Fatigue Crack Growth Phenomena in High-Strength Steel

NASA Technical Reports Server (NTRS)

Forth, Scott C.; James, Mark A.; Johnston, William M., Jr.; Newman, James C., Jr.

2004-01-01

The growth of a fatigue crack through a material is the result of a complex interaction between the applied loading, component geometry, three-dimensional constraint, load history, environment, material microstructure and several other factors. Previous studies have developed experimental and computational methods to relate the fatigue crack growth rate to many of the above conditions, with the intent of discovering some fundamental material response, i.e. crack growth rate as a function of something. Currently, the technical community uses the stress intensity factor solution as a simplistic means to relate fatigue crack growth rate to loading, geometry and all other variables. The stress intensity factor solution is a very simple linear-elastic representation of the continuum mechanics portion of crack growth. In this paper, the authors present fatigue crack growth rate data for two different high strength steel alloys generated using standard methods. The steels exhibit behaviour that appears unexplainable, compared to an aluminium alloy presented as a baseline for comparison, using the stress intensity factor solution.

Effect of SMAT on microstructural and mechanical properties of AA2024

NASA Astrophysics Data System (ADS)

Tadge, Prashant; Sasikumar, C.

2016-05-01

In recent days surface mechanical attrition treatment (SMAT) had attracted the attention of researchers as it produces a nano-crystalline surface with improved mechanical properties. In the present study Al-4%Cu alloy used in automobile and aerospace application is subjected to surface mechanical attrition treatment using steel shots. The microstructural changes introduced on the surface of the Al alloy was investigated using Scanning Electron Microscopy (SEM). The secondary phases formed during the SMAT process is been investigated using EDX and XRD analysis. The effects of SMAT on the mechanical properties were analyzed using a tensile testing. The SMA treatment had resulted in severe plastic deformation of the surface, thereby yielded a nanocrystalline surface with a grain size of 30 to 50 nm. Further, it is also found that the SMAT produced ultra nanocrystalline particles of Cu2Al dispersed uniformly into α-Al matrix. These microstructural changes had resulted in considerable change in the mechanical properties of these alloys. The tensile strength of these alloys had increased from ˜212 MPa to 303 MPa while the fracture toughness increased up to 28% in 10 minutes of SMAT.

The production of fine grained magnesium alloys through thermomechanical processing for the optimization of microstructural and mechanical properties

NASA Astrophysics Data System (ADS)

Young, John Paul

The low density and high strength to weight ratio of magnesium alloys makes them ideal candidates to replace many of the heavier steel and aluminum alloys currently used in the automotive and other industries. Although cast magnesium alloys components have a long history of use in the automotive industry, the integration of wrought magnesium alloys components has been hindered by a number of factors. Grain refinement through thermomechanical processing offers a possible solution to many of the inherent problems associated with magnesium alloys. This work explores the development of several thermomechanical processing techniques and investigates their impact on the microstructural and mechanical properties of magnesium alloys. In addition to traditional thermomechanical processing, this work includes the development of new severe plastic deformation techniques for the production of fine grain magnesium plate and pipe and develops a procedure by which the thermal microstructural stability of severely plastically deformed microstructures can be assessed.

Non-Magnetic, Tough, Corrosion- and Wear-Resistant Knives From Bulk Metallic Glasses and Composites

NASA Technical Reports Server (NTRS)

Hoffman, Douglas C.; Potter, Benjamin

2013-01-01

Quality knives are typically fabricated from high-strength steel alloys. Depending on the application, there are different requirements for mechanical and physical properties that cause problems for steel alloys. For example, diver's knives are generally used in salt water, which causes rust in steel knives. Titanium diver's knives are a popular alternative due to their salt water corrosion resistance, but are too soft to maintain a sharp cutting edge. Steel knives are also magnetic, which is undesirable for military applications where the knives are used as a tactical tool for diffusing magnetic mines. Steel is also significantly denser than titanium (8 g/cu cm vs. 4.5 g/cu cm), which results in heavier knives for the same size. Steel is hard and wear-resistant, compared with titanium, and can keep a sharp edge during service. A major drawback of both steel and titanium knives is that they must be ground or machined into the final knife shape from a billet. Since most knives have a mirrored surface and a complex shape, manufacturing them is complex. It would be more desirable if the knife could be cast into a net or near-net shape in a single step. The solution to the deficiencies of titanium, steel, and ceramic knives is to fabricate them using bulk metallic glasses (or composites). These alloys can be cast into net or near-net shaped knives with a combination of properties that exceed both titanium and steel. A commercially viable BMG (bulk metallic glass) or composite knife is one that exhibits one or all of the following properties: It is based on titanium, has a self-sharpening edge, can retain an edge during service, is hard, is non-magnetic, is corrosion-resistant against a variety of corrosive environments, is tough (to allow for prying), can be cast into a net-shape with a mirror finish and a complex shape, has excellent wear resistance, and is low-density. These properties can be achieved in BMG and composites through alloy chemistry and processing. For each desired property for knife fabrication and performance, there is an alloy development strategy that optimizes behavior. Although BMG knives have been demonstrated as far back as 1995, they never found commercial success because they had to be ground (which presented problems because the alloys contained beryllium), they weren't low cost (because they weren't cast to a net-shape), they were brittle (because they were made with a low-quality commercial material), and they had extremely poor corrosion resistance (because corrosion was not well-understood in these materials). Ultimately, these shortcomings prevented the widespread commercialization. In the current work, the inventors have applied more than a decade of research on BMGs from Caltech and JPL to develop a better understanding of how to make BMG knives that exhibit an optimal combination of properties, processing and cost. Alloys have been developed based in titanium (and other metals), that exhibit high toughness, high hardness, excellent corrosion resistance, no ferromagnetism, edge-retaining selfsharpening, and the ability to be cast like a plastic using commercially available casting techniques (currently used by commercial companies such as Liquidmetal Technologies and Visser Precision Casting). The inventors argue that depending on the application (diving, military, tactical, utility, etc.) there is an optimal combination of design and alloy composition. Moreover, with new casting technologies not available at the inception of these materials, net-shaped knives can be cast into complex shapes that require no aftermarket forming, except for sharpening using water-cooled polishing wheel. These combinations of discoveries seek to make low-cost BMG knives commercially viable products that have no equal among metal or ceramic knives. Current work at JPL focuses on net-shape casting of these alloys and testing their mechanical properties versus commercially available knives to demonstrate their benefits.

Tribological characterisation of Zr-based bulk metallic glass in simulated physiological media

NASA Astrophysics Data System (ADS)

Chen, Q.; Chan, K. C.; Liu, L.

2011-10-01

Due to their excellent wear resistant properties and high strength, as well as a low Young's modulus, Zr-based bulk metallic glasses (BMGs) are potentially suitable biomaterials for low-friction arthroplasty. The wear characteristics of the Zr60.14Cu22.31Fe4.85Al9.7Ag3 bulk amorphous alloy against ultra-high-molecular-weight polyethylene (UHMWPE) compared to a CoCrMo/UHMWPE combination were investigated in two different wear screening test devices, reciprocating and unidirectional. Hank's solution and sterile calf bovine serum were selected as the lubricant fluid media. It was found that different fluid media had insignificant effect on polyethylene wear against BMG counterfaces. The wear behaviour obtained on both test devices demonstrated that Zr-based BMG achieved UHMWPE counterface wear rates superior to conventional cast CoCrMo alloy, where the wear rate of UHMWPE is decreased by over 20 times. The tribological performance of these joints is superior to that of conventional metal-on-polymer designs. Contact angle measurements suggested that the advantage of BMG over a CoCrMo alloy counterface is attributed to its highly hydrophilic surfaces.

How to Choose between the Implant Materials Steel and Titanium in Orthopedic Trauma Surgery: Part 2 - Biological Aspects.

PubMed

Perren, S M; Regazzoni, P; Fernandez, A A

2017-01-01

BIOLOGICAL ASPECTS OF STEEL AND TITANIUM AS IMPLANT MATERIAL IN ORTHOPEDIC TRAUMA SURGERY The following case from the ICUC database, where a titanium plate was implanted into a flourishing infection, represents the clinical experience leading to preferring titanium over steel. (Fig. 1) (6). Current opinions regarding biological aspects of implant function. The "street" opinions regarding the biological aspects of the use of steel versus titanium as a surgical trauma implant material differ widely. Statements of opinion leaders range from "I do not see any difference in the biological behavior between steel and titanium in clinical application" to "I successfully use titanium implants in infected areas in a situation where steel would act as foreign body "sustaining" infection." Furthermore, some comments imply that clinical proof for the superiority of titanium in human application is lacking. The following tries to clarify the issues addressing the different aspects more through a practical clinical approach than a purely scientific one, this includes simplifications. Today's overall biocompatibility of implant materials is acceptable but: As the vast majority of secondary surgeries are elective procedures this allows the selection of implant materials with optimal infection resistance. The different biological reactions of stainless steel and titanium are important for this segment of clinical pathologies. Biological tole - rance (18) depends on the toxicity and on the amount of soluble implant material released. Release, diffusion and washout through blood circulation determine the local concentration of the corrosion products. Alloying components of steel, especially nickel and chromium, are less than optimal in respect to tissue tolerance and allergenicity. Titanium as a pure metal provides excellent biological tolerance (3, 4, 16). Better strength was obtained by titanium alloys like TiAl6V4. The latter found limited application as surgical implants. It contains Vanadium (9). Today's high strength titanium alloys contain well tolerated alloying components1 like Zr, Nb, Mo and Ta (ISO 5832-14) (7, 15). The corrosion rate of surgical implants is kept low by the passive layer formed when immerged in body fluids (13, 14). The passive layer may be locally destroyed, for instance, by mechanical fretting or by local corrosion conditions like in pitting; it is renewed by an electrochemical corrosion process which releases alloying components like Ni and Cr (Fig. 2) (10). The amount of soluble component may vary markedly depending on the local electrochemical conditions (see below).

Coupled gamma/alpha phase transformations in low-carbon steels

NASA Astrophysics Data System (ADS)

Mizutani, Yasushi

Since steels have been the most prevalently utilized materials for many years, the desire for steels with low alloying components with a well-balanced combination of high strength and toughness is increasing. Low carbon steels consisting of bainitic microstructures are ideally suited to meeting such technological and economic requirements. Thus it is extremely important to fully clarify the mechanism of bainite formation in order to produce this type of engineering steel by optimized alloy and process design. This research focuses on understanding the mechanism of coupled displacive/diffusional gamma/alpha transformation in low-carbon steels including bainitic and martensitic transformation, and establishing a more comprehensive and physically rational computational model for predictive control of coupled gamma/alpha transformation phenomena. Models for coupled gamma/alpha phase transformation proposed in this study are based on a mechanistic and unified theory and the following assumptions: (1) The energy dissipation due to interface motion can be linearly combined with the energy dissipation due to carbon diffusion. (2) The carbon concentrations at the interface in both gamma and alpha phases are constrained by an interface solute trapping law. (3) Interface motion during nucleation is also governed by the carbon diffusion field velocity. (4) The response function of glissile interface motion can be expressed in the form of thermally activated dislocation glide. In contrast to the conventional semi-empirical models of the previous literature, the computational model proposed in this study is demonstrated to successfully provide a comprehensive and quantitative prediction of the effects of temperature, composition, microstructure, and the interactions among them. This includes the effects of substitutional solutes, morphology of the parent gamma phase, density of nucleation sites, temperature dependent variation of flow stress of matrix, and dynamic recovery of forest dislocations on the kinetics of coupled gamma/alpha phase transformation.

Dynamic strength properties and alpha-phase shock Hugoniot of iron and steel

NASA Astrophysics Data System (ADS)

Thomas, S. A.; Hawkins, M. C.; Matthes, M. K.; Gray, G. T.; Hixson, R. S.

2018-05-01

The properties of iron and steel are of considerable interest scientifically to the dynamic materials properties' community, as well as to a broader audience, for many applications. This is true in part because of the existence of a solid-solid phase (α-ɛ) transition at relatively modest stress (13 GPa). Because of this, there is a significant amount of data on iron and steel alloy shock compression properties at stresses above 13 GPa, but much less fundamental data under stress conditions lower than that, where the metals are in the α-phase. New data have been obtained under relatively low stress (below 10 GPa) conditions in which samples are subjected to low-velocity symmetric impact on the order of 0.2 to 0.4 km/s. We used well-developed flyer plate impact methods combined with velocity interferometry to measure wave speeds and strength properties in compression and tension. The shock α-phase Hugoniot data reported here are compared with literature values. A comparison of spall strength and Hugoniot elastic limit is made between different types of steel studied and for pure iron.

A comparative study of the in vitro corrosion behavior and cytotoxicity of a superferritic stainless steel, a Ti-13Nb-13Zr alloy, and an austenitic stainless steel in Hank's solution.

PubMed

Assis, S L; Rogero, S O; Antunes, R A; Padilha, A F; Costa, I

2005-04-01

In this study, the in vitro corrosion resistance of a superferritic stainless steel in naturally aerated Hank's solution at 37 degrees C has been determined to evaluate the steel for use as a biomaterial. The potentiodynamic polarization method and electrochemical impedance spectroscopy (EIS) were used to determine the corrosion resistance. The polarization results showed very low current densities at the corrosion potential and electrochemical behavior typical of passive metals. At potentials above 0.75 V (SCE), and up to that of the oxygen evolution reaction, the superferritic steel exhibited transpassive behavior followed by secondary passivation. The superferritic stainless steel exhibited high pitting resistance in Hank's solution. This steel did not reveal pits even after polarization to 3000 mV (SCE). The EIS results indicated high impedance values at low frequencies, supporting the results obtained from the polarization measurements. The results obtained for the superferritic steel have been compared with those of the Ti-13Nb-13Zr alloy and an austenitic stainless steel, as Ti alloys are well known for their high corrosion resistance and biocompatibility, and the austenitic stainless steel is widely used as an implant material. The cytotoxicity tests indicated that the superferritic steel, the austenitic steel, and the Ti-13Nb-13Zr alloy were not toxic. Based on corrosion resistance and cytotoxicity results, the superferritic stainless steel can be considered as a potential biomaterial. (c) 2005 Wiley Periodicals, Inc.

Microstructural Evolution of Thor™ 115 Creep-Strength Enhanced Ferritic Steel

NASA Astrophysics Data System (ADS)

Ortolani, Matteo; D'Incau, Mirco; Ciancio, Regina; Scardi, Paolo

2017-12-01

A new ferritic steel branded as Thor™ 115 has been developed to enhance high-temperature resistance. The steel design combines an improved oxidation resistance with long-term microstructural stability. The new alloy, cast to different product forms such as plates and tubes, was extensively tested to assess the high-temperature time-dependent mechanical behavior (creep). The main strengthening mechanism is precipitation hardening by finely dispersed carbide and nitride phases. Information on the evolution of secondary phases and time-temperature-precipitation behavior of the alloy, essential to ensure long-term property stability, was obtained by scanning transmission electron microscopy with energy dispersive spectroscopy, and by X-ray Powder Diffraction on specimens aged up to 50,000 hours. A thermodynamic modeling supports presentation and evaluation of the experimental results. The evolution of precipitates in the new alloy confirms the retention of the strengthening by secondary phases, even after long-term exposure at high temperature. The deleterious conversion of nitrides into Z phase is shown to be in line with, or even slower than that of the comparable ASME grade 91 steel.

Excellent mechanical properties and resistance to cavitation erosion for an ultra-low carbon CrMnN stainless steel through quenching and partitioning treatment

NASA Astrophysics Data System (ADS)

Zhou, Ze-an; Fu, Wan-tang; Zhu, Zhe; Li, Bin; Shi, Zhong-ping; Sun, Shu-hua

2018-05-01

The retained austenite content (RAC), the mechanical properties, and the resistance to cavitation erosion (CE) of the 00Cr13Mn8MoN steel after quenching and partitioning (Q&P) processing were investigated. The results show that the Q&P process affected the RAC, which reached the maximum value after partitioning at 400°C for 10 min. The tensile strength of the steel slightly decreased with increasing partitioning temperature and time. However, the elongation and product of strength and elongation first increased and then decreased. The sample partitioned at 400°C for 10 min exhibited the optimal property: a strength-ductility of 23.8 GPa·%. The resistance to CE for the 00Cr13Mn8MoN steel treated by the Q&P process was improved due to work hardening, spalling, and cavitation-induced martensitic transformation of the retained austenite.

Influence of V-N Microalloying on the High-Temperature Mechanical Behavior and Net Crack Defect of High Strength Weathering Steel

NASA Astrophysics Data System (ADS)

Qing, Jiasheng; Wang, Lei; Dou, Kun; Wang, Bao; Liu, Qing

2016-06-01

The influence of V-N microalloying on the high-temperature mechanical behavior of high strength weathering steel is discussed through thermomechanical simulation experiment. The difference of tensile strength caused by variation of [%V][%N] appears after proeutectoid phase change, and the higher level of [%V][%N] is, the stronger the tensile strength tends to be. The ductility trough apparently becomes deeper and wider with the increase of [%V][%N]. When the level of [%V][%N] reaches to 1.7 × 10-3, high strength weathering steel shows almost similar reduction of area to 0.03% Nb-containing steel in the temperature range of 800-900°, however, the ductility trough at the low-temperature stage is wider than that of Nb-containing steel. Moreover, the net crack defect of bloom is optimized through the stable control of N content in low range under the precondition of high strength weathering steel with sufficient strength.

Heat treated 9 Cr-1 Mo steel material for high temperature application

DOEpatents

Jablonski, Paul D.; Alman, David; Dogan, Omer; Holcomb, Gordon; Cowen, Christopher

2012-08-21

The invention relates to a composition and heat treatment for a high-temperature, titanium alloyed, 9 Cr-1 Mo steel exhibiting improved creep strength and oxidation resistance at service temperatures up to 650.degree. C. The novel combination of composition and heat treatment produces a heat treated material containing both large primary titanium carbides and small secondary titanium carbides. The primary titanium carbides contribute to creep strength while the secondary titanium carbides act to maintain a higher level of chromium in the finished steel for increased oxidation resistance, and strengthen the steel by impeding the movement of dislocations through the crystal structure. The heat treated material provides improved performance at comparable cost to commonly used high-temperature steels such as ASTM P91 and ASTM P92, and requires heat treatment consisting solely of austenization, rapid cooling, tempering, and final cooling, avoiding the need for any hot-working in the austenite temperature range.

Effect of the carbide phase on the tribological properties of high-manganese antiferromagnetic austenitic steels alloyed with vanadium and molybdenum

NASA Astrophysics Data System (ADS)

Korshunov, L. G.; Kositsina, I. I.; Sagaradze, V. V.; Chernenko, N. L.

2011-07-01

Effect of special carbides (VC, M 6C, Mo2C) on the wear resistance and friction coefficient of austenitic stable ( M s below -196°C) antiferromagnetic ( T N = 40-60°C) steels 80G20F2, 80G20M2, and 80G20F2M2 has been studied. The structure and the effective strength (microhardness H surf, shear resistance τ) of the surface layer of these steels have been studied using optical and electron microscopy. It has been shown that the presence of coarse particles of primary special carbides in the steels 80G20F2, 80G20M2, and 80G20F2M2 quenched from 1150°C decreases the effective strength and the resistance to adhesive and abrasive wear of these materials. This is caused by the negative effect of carbide particles on the toughness of steels and by a decrease in the carbon content in austenite due to a partial binding of carbon into the above-mentioned carbides. The aging of quenched steels under conditions providing the maximum hardness (650°C for 10 h) exerts a substantial positive effect on the parameters of the effective strength ( H surf, τ) of the surface layer and, correspondingly, on the resistance of steels to various types of wear (abrasive, adhesive, and caused by the boundary friction). The maximum positive effect of aging on the wear resistance is observed upon adhesive wear of the steels under consideration. Upon friction with enhanced sliding velocities (to 4 m/s) under conditions of intense (to 500-600°C) friction-induced heating, the 80G20F2, 80G20M2, and, especially, 80G20F2M2 steels subjected to quenching and aging substantially exceed the 110G13 (Hadfield) steel in their tribological properties. This is due to the presence in these steels of a favorable combination of high effective strength and friction heat resistance of the surface layer, which result from the presence of a large amount of special carbides in these steels and from a high degree of alloying of the matrix of these steels by vanadium and molybdenum. In the process of friction, there are formed nanocrystalline austenitic structures possessing high effective strength and wear resistance on the wear surface of these steels.

Reaction of Unalloyed and Cr-Mo Alloyed Steels with Nitrogen from the Sintering Atmosphere

NASA Astrophysics Data System (ADS)

Dlapka, Magdalena; Gierl-Mayer, Christian; Calderon, Raquel de Oro; Danninger, Herbert; Bengtsson, Sven; Dudrova, Eva

2016-12-01

Nitrogen is usually regarded as an inert sintering atmosphere for PM steels; however, this cannot be taken for granted in particular for steels alloyed with nitride forming elements. Among those elements, chromium has become more and more important as an alloying element in sintered low alloy structural steels in the last decade due to the moderate alloying cost and the excellent mechanical properties obtainable, in particular when sinter hardening is applied. The high affinity of Cr to oxygen and the possible ways to overcome related problems have been the subject of numerous studies, while the fact that chromium is also a fairly strong nitride forming element has largely been neglected at least for low alloy steel grades, although frequently used materials like steels from Cr and Cr-Mo prealloyed powders are commonly sintered in atmospheres consisting mainly of nitrogen. In the present study, nitrogen pickup during sintering at different temperatures and for varying times has been studied for Cr-Mo prealloyed steel grades as well as for unalloyed carbon steel. Also the effect of the cooling rate and its influence on the properties, of the microstructure and the composition have been investigated. It showed that the main nitrogen uptake occurs not during isothermal sintering but rather during cooling. It could be demonstrated that a critical temperature range exists within which the investigated CrM-based steel is particularly sensitive to nitrogen pickup.

Effect of Al and Mg Contents on Wettability and Reactivity of Molten Zn-Al-Mg Alloys on Steel Sheets Covered with MnO and SiO2 Layers

NASA Astrophysics Data System (ADS)

Huh, Joo-Youl; Hwang, Min-Je; Shim, Seung-Woo; Kim, Tae-Chul; Kim, Jong-Sang

2018-05-01

The reactive wetting behaviors of molten Zn-Al-Mg alloys on MnO- and amorphous (a-) SiO2-covered steel sheets were investigated by the sessile drop method, as a function of the Al and Mg contents in the alloys. The sessile drop tests were carried out at 460 °C and the variation in the contact angles (θc) of alloys containing 0.2-2.5 wt% Al and 0-3.0 wt% Mg was monitored for 20 s. For all the alloys, the MnO-covered steel substrate exhibited reactive wetting whereas the a-SiO2-covered steel exhibited nonreactive, nonwetting (θc > 90°) behavior. The MnO layer was rapidly removed by Al and Mg contained in the alloys. The wetting of the MnO-covered steel sheet significantly improved upon increasing the Mg content but decreased upon increasing the Al content, indicating that the surface tension of the alloy droplet is the main factor controlling its wettability. Although the reactions of Al and Mg in molten alloys with the a-SiO2 layer were found to be sluggish, the wettability of Zn-Al-Mg alloys on the a-SiO2 layer improved upon increasing the Al and Mg contents. These results suggest that the wetting of advanced high-strength steel sheets, the surface oxide layer of which consists of a mixture of MnO and SiO2, with Zn-Al-Mg alloys could be most effectively improved by increasing the Mg content of the alloys.

Effects of alloying and processing modifications on precipitation and strength in 9%Cr ferritic/martensitic steels for fast reactor cladding

NASA Astrophysics Data System (ADS)

Tippey, Kristin E.

P92 was modified with respect to alloying and processing in the attempt to enhance high-temperature microstructural stability and mechanical properties. Alloying effects were modeled in ThermoCalcRTM and analyzed with reference to literature. ThermoCalcRTM modeling was conducted to design two low-carbon P92-like low-carbon alloys with austenite stabilized by alternative alloying; full conversion to austenite allows for a fully martensitic structure. Goals included avoidance of Z-phase, decrease of M23C6 phase fraction and maintained or increased MX phase fraction. Fine carbonitride precipitation was optimized by selecting alloying compositions such that all V and Nb could be solutionized at temperatures outside the delta-ferrite phase field. A low-carbon alloy (LC) and a low-carbon-zero-niobium alloy (0Nb) were identified and fabricated. This low-carbon approach stems from the increased creep resistance reported in several low-carbon alloys, presumably from reduced M23C6 precipitation and maintained MX precipitation [1], although these low-carbon alloys also contained additional tungsten (W) and cobalt (Co) compared to the base P92 alloy. The synergistic effect of Co and W on the microstructure and mechanical properties are difficult to deconvolute. Higher solutionizing temperatures allow more V and Nb into solution and increase prior austenite grain size; however, at sufficiently high temperatures delta-ferrite forms. Optimal solutionizing temperatures to maximize V and Nb in solution, while avoiding the onset of the delta ferrite phase field, were analyzed in ThermoCalcRTM. Optical microscopy showed ThermoCalc RTM predicted higher delta-ferrite onset temperatures of 20 °C in P92 alloys to nearly 50 °C in the designed alloys of the critical temperature. Identifying the balance where maximum fine precipitation is achieved and delta-ferrite avoided is a key factor in the design of an acceptable P92-like alloy for Generation IV reactor cladding. Processing was further modified utilizing thermomechanical processing (TMP) simulations with the GleebleRTM 3500. Hardness increased substantially in thermomechanically processed alloys, with increased hardness strongly correlating to decreased TMP temperature. The most significant difference between low- and high-temperature thermomechanically processed specimens was an increase in crystallite size at the higher temperature. The fundamental reason for higher strength in the TMP conditions is higher dislocation density, as precipitate volume fraction was not specifically improved in TMP conditions. Thermal stability of the base P92 and of the experimental alloys was analyzed by aging the alloys for times ranging from 500 to 10,000 h at 550, 600, 650, and 700 °C. Results suggest the hardness and thermal stability of LC is greater than that of 0Nb at lower aging temperatures and shorter times, with 0Nb surpassing LC microhardness at 10,000 h at 650 °C and for most conditions aged at 700 °C. Small- and wide-angle x-ray scattering (SAXS/WAXS) was conducted at Argonne National Laboratory (ANL). Atom probe tomography (APT) and scanning transmission electron microscopy high-angle annular dark field (STEM-HAADF) in conjunction with EDS were used to elucidate x-ray findings. These microstructural characteristics were then correlated with mechanical properties, including Vickers microhardness testing, elevated-temperature tensile testing, and creep rupture testing. The designed alloys exhibited less stable microstructures leading to less favorable mechanical potencies, as compared to the base P92 alloy. It is posited that factors other than inclination towards MX over M23C6 precipitation are important in generating thermal stability and high-temperature strength, i.e. perhaps the solid solution or diffusion controlling effects of Co in the low-carbon variation of Taneike's alloys [1] delay martensite recovery. The refined thermal profiles, however, put both P92 and LC creep strengths beyond those found in literature.

Modified heat treatment for lower temperature improvement of the mechanical properties of two ultrahigh strength low alloy steels

NASA Astrophysics Data System (ADS)

Tomita, Yoshiyuki; Okabayashi, Kunio

1985-01-01

In the previous papers, a new heat treatment for improving the lower temperature mechanical propertise of the ultrahigh strength low alloy steels was suggested by the authors which produces a mixed structure of 25 vol pct lower bainite and 75 vol pct martensite through isothermal transformation at 593 K for a short time followed by water quenching (after austenitization at 1133 K). In this paper, two commercial Japanese ultrahigh strength steels, 0.40 pct C-Ni-Cr-Mo (AISI 4340 type) and 0.40 pct C-Cr-Mo (AISI 4140 type), have been studied to determine the effect of the modified heat treatment, coupled above new heat treatment with γ ⇆ α' repctitive heat treatment, on the mechanical properties from ambient temperature (287 K) to 123 K. The results obtained for various test temperatures have been compared with those for the new heat treatment reported previously and the conventional 1133 K direct water quenching treatment. The incorporation of intermediate four cyclic γ ⇆ α' repctitive heat treatment steps (after the initial austenitization at 1133 K and oil quenching) into the new heat treatment reported previously, as compared with the conventional 1133 K direct water quenching treatment, significantly improved 0.2 pct proof stress as well as notch toughness of the 0.40 pct C-Ni-Cr-Mo ultrahigh strength steel at similar fracture ductility levels from 287 to 123 K. Also, this heat treatment, as compared with the conventional 1133 K direct water quenching treatment, significantly improved both 0.2 pct proof stress and notch toughness of the 0.40 pct C-Cr-Mo ultrahigh strength steel with increased fracture ductility at 203 K and above. The microstructure consists of mixed areas of ultrafine grained martensite, within which is the refined blocky, highly dislocated structure, and the second phase lower bainite (about 15 vol pct), which appears in acicular form and partitions prior austenite grains. This newly developed heat treatment makes it possible to modify the new heat treatment reported previously so as to raise 0.2 pct proof stress to a higher level and keep notch toughness at the same level. The improvement in the mechanical properties is discussed in terms of metallographic observations and the modified law of mixtures and so forth.

Research on mechanical properties of silver-bearing antibacterial duplex stainless steel

NASA Astrophysics Data System (ADS)

Liu, Dong; Xiang, Hongliang

2017-04-01

In this paper, silver-bearing antibacterial duplex stainless steels were prepared by adding Ag or Cu-Ag alloy particles. The microstructure, mechanical properties and fracture morphology were investigated in detail by OM, ESEM and tensile testing machine. Tensile tests indicate that the tensile fractures of Ag-bearing antibacterial duplex stainless steel and CD4MCu have the typical ductile character and toughening nests are isometric. After the solution treatment at 1050 ℃, for the material prepared by adding 150-300 µm Cu-Ag master alloy after the solution treatment at 1050 ℃, its plasticity is superior to that of CD4MCu, the strength and hardness are equivalent. But for the material prepared by adding pure Ag alloy particles, its plasticity, strength and hardness are less than that of CD4MCu. When the solution temperature rises, the plastic, strength and hardness of the material prepared by adding 150-300 µm Cu-Ag decrease.

Martensitic transformations, structure, and strengthness of processed high-nitrogen and high-carbon ferrous alloys

NASA Astrophysics Data System (ADS)

Kaputkina, L. M.; Prokoshkina, V. G.

2003-10-01

Structures and properties of metastable austenitic alloys Fe-18Cr-16Ni-I2Mn-(0.17 to 0. 50)N, Fe-18Cr-12Mn-(0.48 to 1.12)N, Fe-18Cr-(0.1 to 1.18)N, and Fe-(12 to 20)Ni-(0.6 to 1.3)C, Fe-(6 to 8)Mn-(0.6 to 1.0)C, Fe-(5 to 6)Cr-(4 to 5)Mn-(0.6 to 0.8)C, Fe-6Cr-(1.0 to 1.3)C resulting from martensitic transformations under cooling and cold deformation (CD), as well as following tempering processes, were studied by magnetometry, X-ray and electron microscopy analyses, hardness measurements and mechanical properties tests. Martensite with a b.c.t. lattice was formed in all alloys with M_s{>}-196^circC during cooling. Under CD transformations of γ{to}α, γ{to}\\varepsilon{to}α, or γ{to}\\varepsilon types were realized depending on the alloy composition. Carbon increased but nitrogen decreased stacking fault energy. Thus carbon assists α-martensite formation but nitrogen promotese. As CD level and/or concentration of carbon and nitrogen increase residual stresses resulting from the CD also increase. The martensitic transformation during CD can decrease the residual stresses. Kinetic of tempering of b.c.t. thermal martensite differs from those of CD-induced martensite. In the second case, deformation aging, texture, and residual stresses are more visible. The maximal strengthening under CD takes place in (Mn+N)-steels. (Cr+N) and (Cr+Mn+N)-steels are high-strength, non-magnetic and corrosion resistant and are easily hardened by a low level of plastic deformation.

Solid State Joining of Magnesium to Steel

NASA Astrophysics Data System (ADS)

Jana, Saumyadeep; Hovanski, Yuri; Pilli, Siva P.; Field, David P.; Yu, Hao; Pan, Tsung-Yu; Santella, M. L.

Friction stir welding and ultrasonic welding techniques were applied to join automotive magnesium alloys to steel sheet. The effect of tooling and process parameters on the post-weld microstructure, texture and mechanical properties was investigated. Static and dynamic loading were utilized to investigate the joint strength of both cast and wrought magnesium alloys including their susceptibility and degradation under corrosive media. The conditions required to produce joint strengths in excess of 75% of the base metal strength were determined, and the effects of surface coatings, tooling and weld parameters on weld properties are presented.

Controlling the mechanical properties of carbon steel by thermomechanical treatment

NASA Astrophysics Data System (ADS)

Balavar, Mohsen; Mirzadeh, Hamed

2018-01-01

The effect of thermomechanical processing and heat treatment on the microstructure and mechanical properties of low carbon steel was studied. It was revealed that the dual phase ferritic-martensitic microstructure shows a good combination of tensile strength and ductility along with superior work hardening response. On the other hand, the bimodal-sized structure containing ultrafine grained (UFG) and micron-sized ferrite phase can be easily produced by cold rolling and annealing of the dual phase starting microstructure. This steel showed high yield stress, tensile strength, and ductility, but poor work hardening ability. The full annealed ferritic-pearlitic sheet with banded morphology exhibited low strength and high total elongation with the appearance of the yield point phenomenon. The martensitic steels, however, had high tensile strength and low ductility. By comparing the tensile properties of these steels, it was shown that it is possible to control the mechanical properties of low carbon steel by simple processing routes.

The effect of microstructure and strength on the fracture toughness of an 18 Ni, 300 grade maraging steel

NASA Technical Reports Server (NTRS)

Psioda, J. A.; Low, J. R., Jr.

1975-01-01

A 300 grade maraging steel was chosen as a vehicle by which to understand the inverse relationship between strength and toughness in high strength alloys such as the 18 Ni maraging steels. The 18 Ni, 300 grade maraging material was a commercial grade consumable-electrode, vacuum arc remelted heat obtained in the form of forged and annealed plate. The matrix contained a population of second-phase impurity inclusions which was a product of the casting and hot working processes. These inclusions did not change with subsequent precipitation hardening. Changes in microstructure resulting in strength increases were brought about by variations in aging temperature and time. Maximum strength was attained in the 300 grade maraging steel by aging at 427 C (800 F) for 100 hours. Tensile, fatigue precracked Charpy impact, and plane-strain fracture toughness tests were performed at room temperature, 20 C (68 F). With increasing strength the fracture toughness decreases as smaller and smaller inclusions act as sites for void initiation.

Exceptional damage-tolerance of a medium-entropy alloy CrCoNi at cryogenic temperatures

DOE PAGES

Gludovatz, Bernd; Hohenwarter, Anton; Thurston, Keli V. S.; ...

2016-02-02

The high-entropy alloys are an intriguing new class of metallic materials that derive their properties not from a single dominant constituent, such as iron in steels, nor from the presence of a second phase, such as in nickel-base superalloys, but rather comprise multi-element systems that crystallize as a single phase, despite containing high concentrations (~20 at.%) of five or more elements with different crystal structures. Indeed, we have recently reported on one such single-phase high-entropy alloy, NiCoCrFeMn, which displays exceptional strength and toughness at cryogenic temperatures. Here which displays unprecedented strength-toughness properties that exceed those of all high-entropy alloys andmore » most multi-phase alloys. With roomtemperature tensile strengths of almost 1 GPa and KJIc fracture-toughness values above 200 MPa.m 1/2 (with crack-growth toughnesses exceeding 300 MPa.m 1/2), the strength, ductility and toughness of the NiCoCr alloy actually improve at cryogenic temperatures to unprecedented levels of strengths above 1.3 GPa, failure strains up to 90% and K JIc values of 275 MPa.m 1/2 (with crackgrowth toughnesses above 400 MPa.m 1/2). These properties appear to result from continuous steady strain hardening, which acts to suppress plastic instability, resulting from pronounced dislocation activity and deformation-induced nano-twinning.« less

76 FR 14108 - Notice of Issuance of Regulatory Guide

Federal Register 2010, 2011, 2012, 2013, 2014

2011-03-15

..., Revision 1, ``Control of Preheat Temperature for Welding of Low-Alloy Steel.'' FOR FURTHER INFORMATION... for Welding of Low-Alloy Steel,'' was issued with a temporary identification as Draft Regulatory Guide... implementing regulatory requirements related to the control of welding for low-alloy steel components during...

Effect of Heat Treatment on the Impact Toughness of `High-Chromium Cast Iron - Low Alloy Steel' Bimetal Components

NASA Astrophysics Data System (ADS)

Özdemir, Z.

2017-03-01

A bimetallic `low-alloy steel - high-chromium cast iron' composite obtained by successive sand casting is studied and shown to have good cohesion on the interface and no casting defects. The hardness and the impact toughness of the bimetal increase simultaneously. The microstructure is more homogeneous after diffusion annealing at 1040°C, rapid cooling, and 3-h tempering at 270°C.