Effects of thermal and mechanical fatigue on the flexural strength of G40-600/PMR-15 cross-ply laminates

NASA Technical Reports Server (NTRS)

Roberts, Gary D.; Ho, Barry Ping Hsiao; Wallace, John F.

1993-01-01

The effects of thermal and mechanical fatigue on the flexural strength of G40-600/PMR-15 cross-ply laminates with ply orientation of (0(2),90(2))2S and (90(2),0(2))2S are examined. The relative importance of shear and tensile stresses is examined by varying the span-to-depth ratios of flexural test specimens from 8 to 45. Acoustic emission signals are measured during the flexural tests in order to monitor the initiation and growth of damage. Optical microscopy is used to examine specimens for resin cracking, delamination, and fiber breaks after testing. Transverse matrix cracks and delaminations occur in all specimens, regardless of ply orientation, span-to-depth ratio, or previous exposure of specimens to thermal and mechanical fatigue. A small amount of fiber tensile fracture occurs in the outer 0 deg ply of specimens with high span-to-depth ratios. Because of the complex failure modes, the flexural test results represent the 'apparent' strengths rather than the true flexural or shear strengths for these cross-ply laminates. Thermal cycling of specimens prior to flexural testing does not reduce the apparent flexural strength or change the mode of failure. However, fewer acoustic events are recorded at all strains during flexural testing of specimens exposed to prior thermal cycling. High temperature thermal cycling (32 to 260 C, 100 cycles) causes a greater reduction in acoustic events than low temperature thermal cycling (-85 to +85 C, 500 cycles). Mechanical cycling (0 to 50 percent of the flexural strength, 100 cycles) has a similar effect, except that acoustic events are reduced only at strains less than the maximum strain applied during flexural fatigue.

On the design of innovative heterogeneous tests using a shape optimization approach

NASA Astrophysics Data System (ADS)

Aquino, J.; Campos, A. Andrade; Souto, N.; Thuillier, S.

2018-05-01

The development of full-field measurement methods enabled a new trend of mechanical tests. By providing the inhomogeneous strain field from the tests, these techniques are being widely used in sheet metal identification strategies, through heterogeneous mechanical tests. In this work, a heterogeneous mechanical test with an innovative tool/specimen shape, capable of producing rich heterogeneous strain paths providing extensive information on material behavior, is aimed. The specimen is found using a shape optimization process where a dedicated indicator that evaluates the richness of strain information is used. The methodology and results here presented are extended to non-specimen geometry dependence and to the non-dependence of the geometry parametrization through the use of the Ritz method for boundary value problems. Different curve models, such as Splines, B-Splines and NURBS, are used and C1 continuity throughout the specimen is guaranteed. Moreover, various optimization methods are used, deterministic and stochastic, in order to find the method or a combination of methods able to effectively minimize the cost function.

MICROSTRUCTURAL AND MECHANICAL CHARACTERIZATION OF 2-D AND 3-D SiC/SiNC CERAMIC MATRIX COMPOSITES

DTIC Science & Technology

2018-02-23

48 5.2 Residual Strength of Test Specimens Reaching Run -Out ...........................................48 5.3 Fracture...46 Table 10. Residual Strength Tension Test Results for Creep Rupture Specimens Reaching Run - Out...Residual Strength Tension Test Results for Fatigue Specimens Reaching Run -Out . 49 vii Distribution Statement A. Approved for public release

Environment-Assisted Cracking in Custom 465 Stainless Steel

NASA Astrophysics Data System (ADS)

Lee, E. U.; Goswami, R.; Jones, M.; Vasudevan, A. K.

2011-02-01

The influence of cold work and aging on the environment-assisted cracking (EAC) behavior and mechanical properties of Custom 465 stainless steel (SS) was studied. Four sets of specimens were made and tested. All specimens were initially solution annealed, rapidly cooled, and refrigerated (SAR condition). The first specimen set was steel in the SAR condition. The second specimen set was aged to the H1000 condition. The third specimen set was 60 pct cold worked, and the fourth specimen set was 60 pct cold worked and aged at temperatures ranging from 755 K to 825 K (482 °C to 552 °C) for 4 hours in air. The specimens were subsequently subjected to EAC and mechanical testing. The EAC testing was conducted, using the rising step load (RSL) technique, in aqueous solutions of NaCl of pH 7.3 with concentrations ranging from 0.0035 to 3.5 pct at room temperature. The microstructure, dislocation substructure, and crack paths, resulting from the cold work, aging, or subsequent EAC testing, were examined by optical microscopy, transmission electron microscopy (TEM), and scanning electron microscopy (SEM). The aging of the cold-worked specimens induced carbide precipitation within the martensite lath, but not at the lath or packet boundaries. In the aged specimens, as aging temperature rose, the threshold stress intensity for EAC (KIEAC), elongation, and fracture toughness increased, but the strength and hardness decreased. The KIEAC also decreased with increasing yield strength and NaCl concentration. In the SAR and H1000 specimens, the EAC propagated along the prior austenite grain boundary, while in the cold-worked and cold-worked and aged specimens, the EAC propagated along the martensite lath, and its packet and prior austenite grain boundaries. The controlling mechanism for the observed EAC was identified to be hydrogen embrittlement.

Apparatus for pre-stress-straining rod-type specimens in tension for in-situ passive fracture testing

DOEpatents

Wang, John Jy-an [Oak Ridge, TN; Liu, Ken C [Oak Ridge, TN; Feng, Zhili [Knoxville, TN

2013-07-31

A stress-strain testing apparatus imposes a stress-strain on a specimen while disposed in a controlled environment. Each end of the specimen is fastened to an end cap and a strain gage is attached to the specimen. An adjusting mechanism and a compression element are disposed between the end caps forming a frame for applying forces to the end caps and thereby stress-straining the specimen. The adjusting mechanism may be extended or retracted to increase or decrease the imposed stress-strain on the specimen, and the stress-strain is measured by the strain gage on the specimen while the apparatus is exposed to an environment such as high pressure hydrogen. Strain gages may be placed on the frame to measure stress-strains in the frame that may be caused by the environment.

Interrelationship of mechanical and corrosion-mechanical characteristics of type 12KhN4MF steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Voronin, V.P.; Goncharov, A.F.; Maslov, V.A.

1985-11-01

Investigations presented include a comparative evaluation of the corrosionmechanical characteristics of specimens of high-strength chrome-nickelmolybdenum steel taking into consideration the different methods of melting of the original metal. A comparison of the corrosion-mechanical test results obtained with the results of acceptance tests are presented. A study of the fracture surfaces and the specimen material with the use of fractographic, macroscopic, and microscopic analyses is given. The systematization of the corrosion-mechanical test results with the use of methods of mathematical statistics are presented.

Thermal insulation testing method and apparatus

NASA Technical Reports Server (NTRS)

Fesmire, James E. (Inventor); Augustynowicz, Stanislaw D. (Inventor)

2004-01-01

A test apparatus and method of its use for evaluating various performance aspects of a test specimen is disclosed. A chamber within a housing contains a cold mass tank with a contact surface in contact with a first surface of a test specimen. The first surface of the test specimen is spaced from the second surface of the test specimen by a thickness. The second surface of the test specimen is maintained at a desired warm temperature. The first surface is maintained at a constant temperature by a liquid disposed within the cold mass tank. A boil-off flow rate of the gas is monitored and provided to a processor along with the temperature of the first and second surfaces of the test specimen. The processor calculates thermal insulation values of the test specimen including comparative values for heat flux and apparent thermal conductivity (k-value). The test specimen may be placed in any vacuum pressure level ranging from about 0.01 millitorr to 1,000,000 millitorr with different residual gases as desired. The test specimen may be placed under a mechanical load with the cold mass tank and another factors may be imposed upon the test specimen so as to simulate the actual use conditions.

Thermal Insulation Testing Method and Apparatus

NASA Technical Reports Server (NTRS)

Fesmire, James E. (Inventor); Augustynowicz, Stanislaw D. (Inventor)

2004-01-01

A test apparatus and method of its use for evaluating various performance aspects of a test specimen is disclosed. A chamber within a housing contains a cold mass tank with a contact surface in contact with a first surface of a test specimen. The first surface of the test specimen is spaced from the second surface of the test specimen by a thickness. The second surface of the test specimen is maintained at a a constant temperature by a liquid disposed within the cold mass tank. A boil-off flow rate of the gas is monitored and provided to a processor along with the temperature of the first and second surfaces of the test specimen. The processor calculates thermal insulation values of the test specimen including comparative values for heat flux and apparent thermal conductivity k-value). The test specimen may be placed in any vacuum pressure level ranging from about 0.01 millitorr to 1,000,000 millitorr with different residual gases as desired. The test specimen may be placed under a mechanical load with the cold mass tank and another factors may be imposed upon the test specimen so as to simulate the actual use conditions.

Mechanical characteristics of a tool steel layer deposited by using direct energy deposition

NASA Astrophysics Data System (ADS)

Baek, Gyeong Yun; Shin, Gwang Yong; Lee, Eun Mi; Shim, Do Sik; Lee, Ki Yong; Yoon, Hi-Seak; Kim, Myoung Ho

2017-07-01

This study focuses on the mechanical characteristics of layered tool steel deposited using direct energy deposition (DED) technology. In the DED technique, a laser beam bonds injected metal powder and a thin layer of substrate via melting. In this study, AISI D2 substrate was hardfaced with AISI H13 and M2 metal powders for mechanical testing. The mechanical and metallurgical characteristics of each specimen were investigated via microstructure observation and hardness, wear, and impact tests. The obtained characteristics were compared with those of heat-treated tool steel. The microstructures of the H13- and M2-deposited specimens show fine cellular-dendrite solidification structures due to melting and subsequent rapid cooling. Moreover, the cellular grains of the deposited M2 layer were smaller than those of the H13 structure. The hardness and wear resistance were most improved in the M2-deposited specimen, yet the H13-deposited specimen had higher fracture toughness than the M2-deposited specimen and heat-treated D2.

Study on mechanical properties of steel honeycomb panel three-point bending specimen under in-plane and out-plane transverse dynamic impact load

NASA Astrophysics Data System (ADS)

Zou, Guangping; Chang, Zhongliang; Xia, Xingyou; Zhang, Xueyi

2010-03-01

The metal honeycomb material has high strength and high stiffness, as a high-performance sandwich panel, it is an ideal lightweight structural material, and widely used in aviation, aerospace, shipbuilding and other fields. In this paper, the improved SHPB instrument is used for testing the in-plane and out-plane mechanical properties of the steel honeycomb panel three-point bending specimen, and also compare the results with the static in-plane and out-plane three-point bending experiments results which is tested by the INSTRON 4505 electronic universal testing machine, and then study the mechanical properties of the steel honeycomb panel three-point bending specimen under transverse dynamic impact load. From the results it can be see that, for the out-plane three point bending experiment, L direction mechanical properties is better than the W direction, and the honeycomb core play an important role during the specimen deformation, while for the in-plane three point bending experiment, the honeycomb core mechanical role is not distinctness.

Hypervelocity penetration against mechanical properties of target materials

NASA Astrophysics Data System (ADS)

Kamarudin, Khairul Hasni; Abdullah, Mohamad Faizal; Zaidi, Ahmad Mujahid Ahmad; Nor, Norazman M.; Ismail, Ariffin; Yusof, Mohammed Alias; Hilmi, Ahmad Humaizi

2018-02-01

This paper study the mechanical properties behavior of metal plates against hypervelocity penetration caused by shaped charge. Five different materials were used as target specimen fabricated from welded stacks of material plates, namely Rolled Homogeneous Armor (RHA), Hardox-500, mild steel, aluminum and brass. Specimens had undergone an initial monolithic test consist of tensile tests and microstructure observations, followed by series of hydrodynamics penetration blast tests using shape charge mechanism. Results from blast test shows that the least penetrated specimen is RHA (58mm) followed by Hardox-500 (92 mm), mild steel (110 mm), Brass (155 mm) and aluminum 238 mm). Comparing these with the specimen yield strength from the tensile test results shows that Hardox-500 has higher yield strength (Sy) followed by RHA, mild steel, brass and aluminum, which are 1370 MPa, 1320 MPa, 280,221 respectively, which are not inversely proportional to the penetration. However, the ultimate tensile strength (Sut) where the RHA were the highest followed by Hardox-500, mild steel, brass and aluminum, were inversely proportional with the depth of penetration. The penetration results also show consistence relation with energy absorption.

Apparent-Strain Correction for Combined Thermal and Mechanical Testing

NASA Technical Reports Server (NTRS)

Johnson, Theodore F.; O'Neil, Teresa L.

2007-01-01

Combined thermal and mechanical testing requires that the total strain be corrected for the coefficient of thermal expansion mismatch between the strain gage and the specimen or apparent strain when the temperature varies while a mechanical load is being applied. Collecting data for an apparent strain test becomes problematic as the specimen size increases. If the test specimen cannot be placed in a variable temperature test chamber to generate apparent strain data with no mechanical loads, coupons can be used to generate the required data. The coupons, however, must have the same strain gage type, coefficient of thermal expansion, and constraints as the specimen to be useful. Obtaining apparent-strain data at temperatures lower than -320 F is challenging due to the difficulty to maintain steady-state and uniform temperatures on a given specimen. Equations to correct for apparent strain in a real-time fashion and data from apparent-strain tests for composite and metallic specimens over a temperature range from -450 F to +250 F are presented in this paper. Three approaches to extrapolate apparent-strain data from -320 F to -430 F are presented and compared to the measured apparent-strain data. The first two approaches use a subset of the apparent-strain curves between -320 F and 100 F to extrapolate to -430 F, while the third approach extrapolates the apparent-strain curve over the temperature range of -320 F to +250 F to -430 F. The first two approaches are superior to the third approach but the use of either of the first two approaches is contingent upon the degree of non-linearity of the apparent-strain curve.

Specimen's plane misaligned installation solution based on charge fluctuation inside SEM

NASA Astrophysics Data System (ADS)

Lu, Haojian; Liu, Yanting; Yang, Yuanyuan; Wang, Panbing; Shen, Yajing

2018-04-01

Precise specimen's installation is a sticking point to ensure the characterization accuracy of the in-situ material property test. Although it is common knowledge that specimen's plane misaligned installation (PMI) would cause extra force loading during mechanical testing, there are few effective solutions available to deal with it at the current stage, especially during the in-situ scanning electron microscopy (SEM) test. Taking into consideration the charge fluctuation phenomenon under SEM, this paper proposes a highlight area variation (HAV) method for specimen deformation judgment, i.e., the specimen deformation is defined when the highlight area changes greater than 20% of the initial value of the specimen surface. Three types of specimens with different resistivities, i.e., human hair (electrical resistivity ˜3 × 1012 Ω cm), optical fiber (electrical resistivity ˜1017 Ω cm), and magnetic wire (electrical resistivity ˜2 × 10-5 Ω cm), are chosen to verify the effectiveness of the HAV method. Furthermore, combined with the developed robot-aided alignment system, the specimen's PMI problem can also be solved. In the demonstration, the human hair specimen is installed across two specimen stages and its in-situ twisting (in 360°) test is implemented. The results clearly indicate that the HAV method and the robot-aided alignment system are practical and reliable, and the specimen can be aligned on the same plane and installed precisely with accuracy up to 3 μm. This method will benefit the in-situ SEM material mechanical property test and has a significant impact in fundamental material research.

Ten Deg Off-Axis Test for Shear Properties in Fiber Composites

NASA Technical Reports Server (NTRS)

Chamis, C. C.; Sinclair, J. H.

1977-01-01

A combined theoretical and experimental investigation was conducted to assess the suitability of the 10 deg off-axis tensile test specimen for the intralaminar shear characterization of unidirectional composites. Composite mechanics, a combined-stress failure criterion, and a finite variation across the specimen width and the relative stress and strain magnitudes at the 10 deg plane. Strain gages were used to measure the strain variation across the specimen width at specimen midlength and near the end tabs. Specimens from Mod-I/epoxy, T-300/epoxy, and S-glass/epoxy were used in the experimental program. It was found that the 10 deg off-axis tensile test specimen is suitable for intralaminar shear characterization, and it is recommended that it should be considered as a possible standard test specimen for such a characterization.

New test structures and techniques for measurement of mechanical properties of MEMS materials

NASA Astrophysics Data System (ADS)

Sharpe, William N., Jr.; Yuan, Bin; Vaidyanathan, Ranji; Edwards, Richard L.

1996-09-01

This paper presents techniques and procedures for addressing the three major problems of mechanical testing of the thin films used in surface micromachined microelectromechanical systems--specimen handling, friction, and strain measurement. The polysilicon tensile specimens are fabricated with two supporting side strips on silicon wafers at the Microelectronic Center of North Carolina. The tensile specimen is released by etching away the wafer, and the two support strips are cut after the specimen is glued in the test machine. Friction is reduced by a linear air bearing in the load train, and strain is measured with a noncontacting technique based on laser interferometry between two gold lines on the tensile specimen. The Young's modulus of polysilicon is 170 +/- 7 GPa and the strength is 1.21 +/- 0.16 GPa from a series of 29 tests. preliminary measurements have been made of Poisson's ratio and the fatigue behavior, and an attempt is underway to measure the fracture toughness.

Design and fabrication of a micron scale free-standing specimen for uniaxial micro-tensile tests

NASA Astrophysics Data System (ADS)

Tang, Jun; Wang, Hong; Li, Shi Chen; Liu, Rui; Mao, Sheng Ping; Li, Xue Ping; Zhang, Cong Chun; Ding, Guifu

2009-10-01

This paper presents a novel design and fabrication of test chips with a nickel free-standing specimen for the micro uniaxial tensile test. To fabricate test chips on the quartz substrate significantly reduces the fabrication time, minimizes the number of steps and eliminates the effect of the wet anisotropic etching process on mechanical properties. The test chip can be gripped tightly to the test machine and aligned accurately in the pulling direction; furthermore, the approximately straight design of the specimen rather than the traditional dog-bone structure enables the strain be directly measured by a displacement sensor. Both finite-element method (FEM) analysis and experimental results indicate the reliability of the new design. The test chip can also be extended to other materials. The experimental measured Young's modulus of a thin nickel film and the ultimate tensile strength are approximately 94.5 Gpa and 1.76 Gpa, respectively. The results were substantially supported by the experiment on larger gauge specimens by a commercial dynamic mechanical analysis (DMA) instrument. These specimens were electroplated under the same conditions. The low Young's modulus and the high ultimate tensile strength might be explained by the fine grain in the electroplated structure.

Force Limit System

NASA Technical Reports Server (NTRS)

Pawlik, Ralph; Krause, David; Bremenour, Frank

2011-01-01

The Force Limit System (FLS) was developed to protect test specimens from inadvertent overload. The load limit value is fully adjustable by the operator and works independently of the test system control as a mechanical (non-electrical) device. When a test specimen is loaded via an electromechanical or hydraulic test system, a chance of an overload condition exists. An overload applied to a specimen could result in irreparable damage to the specimen and/or fixturing. The FLS restricts the maximum load that an actuator can apply to a test specimen. When testing limited-run test articles or using very expensive fixtures, the use of such a device is highly recommended. Test setups typically use electronic peak protection, which can be the source of overload due to malfunctioning components or the inability to react quickly enough to load spikes. The FLS works independently of the electronic overload protection.

Role of age and injury mechanism on cervical spine injury tolerance from head contact loading.

PubMed

Yoganandan, Narayan; Chirvi, Sajal; Voo, Liming; Pintar, Frank A; Banerjee, Anjishnu

2018-02-17

The objective of this study was to determine the influence of age and injury mechanism on cervical spine tolerance to injury from head contact loading using survival analysis. This study analyzed data from previously conducted experiments using post mortem human subjects (PMHS). Group A tests used the upright intact head-cervical column experimental model. The inferior end of the specimen was fixed, the head was balanced by a mechanical system, and natural lordosis was removed. Specimens were placed on a testing device via a load cell. The piston applied loading at the vertex region. Spinal injuries were identified using medical images. Group B tests used the inverted head-cervical column experimental model. In one study, head-T1 specimens were fixed distally, and C7-T1 joints were oriented anteriorly, preserving lordosis. Torso mass of 16 kg was added to the specimen. In another inverted head-cervical column study, occiput-T2 columns were obtained, an artificial head was attached, T1-T2 was fixed, C4-C5 disc was maintained horizontal in the lordosis posture, and C7-T1 was unconstrained. The specimens were attached to the drop test carriage carrying a torso mass of 15 kg. A load cell at the inferior end measured neck loads in both studies. Axial neck force and age were used as the primary response variable and covariate to derive injury probability curves using survival analysis. Group A tests showed that age is a significant (P < .05) and negative covariate; that is, increasing age resulted in decreasing force for the same risk. Injuries were mainly vertebral body fractures and concentrated at one level, mid-to-lower cervical spine, and were attributed to compression-related mechanisms. However, age was not a significant covariate for the combined data from group B tests. Both group B tests produced many soft tissue injuries, at all levels, from C1 to T1. The injury mechanism was attributed to mainly extension. Multiple and noncontiguous injuries occurred. Injury probability curves, ±95% confidence intervals, and normalized confidence interval sizes representing the quality of the mean curve are given for different data sets. For compression-related injuries, specimen age should be used as a covariate or individual specimen data may be prescaled to derive risk curves. For distraction- or extension-related injuries, however, specimen age need not be used as a covariate in the statistical analysis. The findings from these tests and survival analysis indicate that the age factor modulates human cervical spine tolerance to impact injury.

Determining mechanical behavior of solid materials using miniature specimens

DOEpatents

Manahan, Michael P.; Argon, Ali S.; Harling, Otto K.

1986-01-01

A Miniaturized Bend Test (MBT) capable of extracting and determining mechanical behavior information from specimens only so large as to have at least a volume or smallest dimension sufficient to satisfy continuum behavior in all directions. The mechanical behavior of the material is determined from the measurements taken during the bending of the specimen and is processed according to the principles of linear or nonlinear material mechanics or both. In a preferred embodiment the determination is carried out by a code which is constructed according to the finite element method, and the specimen used for the determinations is a miniature disk simply supported for central loading at the axis on the center of the disk.

A method for predicting the fatigue life of pre-corroded 2024-T3 aluminum from breaking load tests

NASA Astrophysics Data System (ADS)

Gruenberg, Karl Martin

Characterization of material properties is necessary for design purposes and has been a topic of research for many years. Over the last several decades, much progress has been made in identifying metrics to describe fracture mechanics properties and developing procedures to measure the appropriate values. However, in the context of design, there has not been as much success in quantifying the susceptibility of a material to corrosion damage and its subsequent impact on material behavior in the framework of fracture mechanics. A natural next step in understanding the effects of corrosion damage was to develop a link between standard material test procedures and fatigue life in the presence of corrosion. Simply stated, the goal of this investigation was to formulate a cheaper and quicker method for assessing the consequences of corrosion on remaining fatigue life. For this study, breaking load specimens and fatigue specimens of a single nominal gage (0.063″) of aluminum alloy 2024-T3 were exposed to three levels of corrosion. The breaking load specimens were taken from three different material lots, and the fatigue tests were carried out at three stress levels. All failed specimens, both breaking load and fatigue specimens, were examined to characterize the damage state(s) and failure mechanism(s). Correlations between breaking load results and fatigue life results in the presence of corrosion damage were developed using a fracture mechanics foundation and the observed mechanisms of failure. Where breaking load tests showed a decrease in strength due to increased corrosion exposure, the corresponding set of fatigue tests showed a decrease in life. And where breaking load tests from different specimen orientations exhibited similar levels of strength, the corresponding set of fatigue specimens showed similar lives. The spread from shortest to longest fatigue lives among the different corrosion conditions decreased at the higher stress levels. Life predictions based on breaking load data were generally shorter than the experimental lives by an average of 20%. The life prediction methodology developed from this investigation is a very valuable tool for the purpose of assessing material substitution for aircraft designers, alloy differentiation for manufacturers, or inspection intervals and aircraft retirement schedules for aircraft in service.

Laboratory Characterization of Solid Grade SW Brick

DTIC Science & Technology

2007-08-01

Society for Testing and Materials (ASTM) D 2216 (ASTM 2002e). Based on the appropriate values of posttest water content, wet density, and an assumed...strain path (UX/SP) tests. In addition to the mechanical property tests, nondestructive pulse-velocity measurements were performed on each specimen...Figure 3. Spring-arm lateral deformeter mounted on test specimen

An experimental study on fracture mechanical behavior of rock-like materials containing two unparallel fissures under uniaxial compression

NASA Astrophysics Data System (ADS)

Huang, Yan-Hua; Yang, Sheng-Qi; Tian, Wen-Ling; Zeng, Wei; Yu, Li-Yuan

2016-06-01

Strength and deformability characteristics of rock with pre-existing fissures are governed by cracking behavior. To further research the effects of pre-existing fissures on the mechanical properties and crack coalescence process, a series of uniaxial compression tests were carried out for rock-like material with two unparallel fissures. In the present study, cement, quartz sand, and water were used to fabricate a kind of brittle rock-like material cylindrical model specimen. The mechanical properties of rock-like material specimen used in this research were all in good agreement with the brittle rock materials. Two unparallel fissures (a horizontal fissure and an inclined fissure) were created by inserting steel during molding the model specimen. Then all the pre-fissured rock-like specimens were tested under uniaxial compression by a rock mechanics servo-controlled testing system. The peak strength and Young's modulus of pre-fissured specimen all first decreased and then increased when the fissure angle increased from 0° to 75°. In order to investigate the crack initiation, propagation and coalescence process, photographic monitoring was adopted to capture images during the entire deformation process. Moreover, acoustic emission (AE) monitoring technique was also used to obtain the AE evolution characteristic of pre-fissured specimen. The relationship between axial stress, AE events, and the crack coalescence process was set up: when a new crack was initiated or a crack coalescence occurred, the corresponding axial stress dropped in the axial stress-time curve and a big AE event could be observed simultaneously. Finally, the mechanism of crack propagation under microscopic observation was discussed. These experimental results are expected to increase the understanding of the strength failure behavior and the cracking mechanism of rock containing unparallel fissures.

Mechanical properties of turbine blade alloys in hydrogen at elevated temperatures

NASA Technical Reports Server (NTRS)

Deluca, D. P.

1981-01-01

The mechanical properties of single crystal turbine blade alloys in a gaseous hydrogen environment were determined. These alloys are proposed for use in space propulsion systems in pure or partial high pressure hydrogen environments at elevated temperatures. Mechanical property tests included: tensile, creep, low fatigue (LCF), and crack growth. Specimens were in both transverse and longitudinal directions relative to the casting solidification direction. Testing was conducted on solid specimens exposed to externally pressurized environments of gaseous hydrogen and hydrogen-enriched steam.

16 CFR 1610.2 - Definitions.

Code of Federal Regulations, 2011 CFR

2011-01-01

... mechanism of the test apparatus. (c) Dry cleaning means the cleaning of samples in a commercial dry cleaning... 1 second during which the ignition flame is applied to the test specimen. (g) Ignition means that there is a self-sustaining flame on the specimen after the test flame is removed. (h) Interlining means...

16 CFR 1610.2 - Definitions.

Code of Federal Regulations, 2012 CFR

2012-01-01

... mechanism of the test apparatus. (c) Dry cleaning means the cleaning of samples in a commercial dry cleaning... 1 second during which the ignition flame is applied to the test specimen. (g) Ignition means that there is a self-sustaining flame on the specimen after the test flame is removed. (h) Interlining means...

16 CFR § 1610.2 - Definitions.

Code of Federal Regulations, 2013 CFR

2013-01-01

... mechanism of the test apparatus. (c) Dry cleaning means the cleaning of samples in a commercial dry cleaning... 1 second during which the ignition flame is applied to the test specimen. (g) Ignition means that there is a self-sustaining flame on the specimen after the test flame is removed. (h) Interlining means...

16 CFR 1610.2 - Definitions.

Code of Federal Regulations, 2014 CFR

2014-01-01

... mechanism of the test apparatus. (c) Dry cleaning means the cleaning of samples in a commercial dry cleaning... 1 second during which the ignition flame is applied to the test specimen. (g) Ignition means that there is a self-sustaining flame on the specimen after the test flame is removed. (h) Interlining means...

Characterization of fatigue behavior of 2-D woven fabric reinforced ceramic matrix composite at elevated temperature. Final report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Groner, D.J.

This study investigated the fatigue behavior and associated damage mechanisms in notched and unnotched enhanced SiC/SiC ceramic matrix composite specimens at 1100 deg C. Stiffness degradation, strain variation, and hysteresis were evaluated to characterize material behavior. Microscopic examination was performed to characterize damage mechanisms. During high cycle/low stress fatigue tests, far less fiber/matrix interface debond was evident than in low cycle/high stress fatigue tests. Notched specimens exhibited minimal stress concentration during monotonic tensile testing and minimal notch sensitivity during fatigue testing. Damage mechanisms were also similar to unnotched.

Effect of different aging methods on the mechanical behavior of multi-layered ceramic structures.

PubMed

Borba, Márcia; de Araújo, Maico D; Fukushima, Karen A; Yoshimura, Humberto N; Griggs, Jason A; Della Bona, Álvaro; Cesar, Paulo F

2016-12-01

To evaluate the effect of two aging methods (mechanical cycling and autoclave) on the mechanical behavior of veneer and framework ceramic specimens with different configurations (monolithic, two and three-layers). Three ceramics used as framework for fixed dental prostheses (YZ-Vita In-Ceram YZ; IZ-Vita In-Ceram Zirconia; AL-Vita In-Ceram AL) and two veneering porcelains (VM7 and VM9) were studied. Bar-shaped specimens were produced in three different designs: monolithic, two layers (porcelain-framework) and three layers (porcelain-framework-porcelain). Specimens were tested for three-point flexural strength at 1MPa/s in 37°C artificial saliva. Three different experimental conditions were evaluated (n=10): control; mechanical cycling (2Hz, 37°C artificial saliva); and autoclave aging (134°C, 2 bars, 5h). Bi-layered specimens were tested in both conditions: with porcelain or framework ceramic under tension. Fracture surfaces were analyzed using stereomicroscope and scanning electron microscopy. Results were statistically analyzed using Kruskal-Wallis and Student-Newman-Keuls tests. Only for AL group, mechanical cycling and autoclave aging significantly decreased the flexural strength values in comparison to the control (p<0.01). YZ, AL, VM7 and VM9 monolithic groups showed no strength degradation. For multi-layered specimens, when the porcelain layer was tested in tension (bi and tri-layers), the aging methods evaluated also had no effect on strength (p≥0.05). Total and partial failure modes were identified. Mechanical cycling and autoclave aging protocols had no effect on the flexural strength values and failure behavior of YZ and IZ ceramic structures. Yet, AL monolithic structures showed a significant decrease in flexural strength with any of the aging methods. Copyright © 2016. Published by Elsevier Ltd.

Long-Term Isothermal Aging Effects on Carbon Fabric-Reinforced PMR-15 Composites: Compression Strength

NASA Technical Reports Server (NTRS)

Bowles, Kenneth J.; Roberts, Gary D.; Kamvouris, John E.

1996-01-01

A study was conducted to determine the effects of long-term isothermal thermo-oxidative aging on the compressive properties of T-650-35 fabric reinforced PMR-15 composites. The temperatures that were studied were 204, 260, 288, 316, and 343 C. Specimens of different geometries were evaluated. Cut edge-to-surface ratios of 0.03 to 0.89 were fabricated and aged. Aging times extended to a period in excess of 15,000 hours for the lower temperature runs. The unaged and aged specimens were tested in compression in accordance with ASTM D-695. Both thin and thick (plasma) specimens were tested. Three specimens were tested at each time/temperature/geometry condition. The failure modes appeared to be initiated by fiber kinking with longitudinal, interlaminar splitting. In general, it appears that the thermo-oxidative degradation of the compression strength of the composite material may occur by both thermal (time-dependent) and oxidative (weight-loss) mechanisms. Both mechanisms appear to be specimen-thickness dependent.

Ten deg off-axis tensile test for intralaminar shear characterization of fiber composites

NASA Technical Reports Server (NTRS)

Chamis, C. C.; Sinclair, J. H.

1976-01-01

A combined theoretical and experimental investigation was conducted to assess the suitability of the 10 deg off-axis tensile test specimen for the intralaminar shear characterization of unidirectional composites. Composite mechanics, a combined-stress failure criterion, and a finite element analysis were used to determine theoretically the stress-strain variation across the specimen width and the relative stress and strain magnitudes at the 10 deg plane. Strain gages were used to measure the strain variation across the specimen width at specimen midlength and near the end tabs. Specimens from Mod-I/epoxy, T-300/epoxy, and S-glass/epoxy were used in the experimental program. It was found that the 10 deg off-axis tensile test specimen is suitable for intralaminar shear characterization and it is recommended that it should be considered as a possible standard test specimen for such a characterization.

Controlled shear/tension fixture

DOEpatents

Hsueh, Chun-Hway [Knoxville, TN; Liu, Chain-tsuan [Knoxville, TN; George, Easo P [Knoxville, TN

2012-07-24

A test fixture for simultaneously testing two material test samples is provided. The fixture provides substantially equal shear and tensile stresses in each test specimens. By gradually applying a load force to the fixture only one of the two specimens fractures. Upon fracture of the one specimen, the fixture and the load train lose contact and the second specimen is preserved in a state of upset just prior to fracture. Particular advantages of the fixture are (1) to control the tensile to shear load on the specimen for understanding the effect of these stresses on the deformation behavior of advanced materials, (2) to control the location of fracture for accessing localized material properties including the variation of the mechanical properties and residual stresses across the thickness of advanced materials, (3) to yield a fractured specimen for strength measurement and an unfractured specimen for examining the microstructure just prior to fracture.

Effect of cyclic fatigue on the fracture toughness of Polyoxymethylene

NASA Astrophysics Data System (ADS)

Ramoa, B.; Berer, M.; Schwaiger, M.; Pinter, G.

2017-05-01

Polymers are used in a wide range of applications and their properties are dependent upon the morphological development during processing and the specimen configuration which in turn define the mechanical properties. In this context fatigue and monotonic testing are part of the standard procedure to assess relevant mechanical and material parameters to ensure a better part design. The present work addresses the performance issues of a real component made of Polyoxymethylene (POM) which is subjected to cyclic loads from intermediate levels to high peak values inside a damping mechanism. For this linear elastic fracture mechanics concepts were used to characterize the behavior of a POM homopolymer resin used in this application. Injection molded compact tension specimens, with sharp and blunt notches, were tested under a combination of cyclic and monotonic loads and the fracture surfaces were examined. The critical stress intensity factor obtained by monotonic tests was evaluated as a function of the cycle number, where an increase after the first 1000 cycles followed by a continuous decrease with higher numbers of cycles was observed. A variation of approximately 50% and 70% were obtained along the duration of the tests for the sharp and blunt notch specimens, respectively. In light of the obtained results, a discussion is presented considering the dynamic specimen compliance and the structural features observed on the fracture surfaces in combination with the fracture mechanical response.

Influence of additional coupling agent on the mechanical properties of polyester–agave cantala roxb based composites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ubaidillah, E-mail: ubaidillah@uns.ac.id; Malaysia-Japan International Institute of Technology, Universiti Teknologi Malaysia, Jalan Sultan Yahya Petra, Kuala Lumpur; Raharjo, Wijang W.

The mechanical and morphological properties of the unsaturated polyester resins (UPRs)-agave cantala roxb based composite are investigated in this paper. The cantala fiber woven in 3D angle interlock was utilized as the composite reinforcement. Surface grafting of the cantala fiber through chemical treatment was performed by introducing silane coupling agent to improving the compatibility with the polymer matrix. The fabrication of the composite specimens was conducted using vacuum bagging technique. The effect of additional coupling agent to the morphological appearance of surface fracture was observed using scanning electron microscopy. Meanwhile, the influence of additional silane to the mechanical properties wasmore » examined using tensile, bending and impact test. The photograph of surface fracture on the treated specimens showed the residual matrix left on the fibers in which the phenomenon was not found in the untreated specimens. Based on mechanical tests, the treated specimens were successfully increased their mechanical properties by 55%, 9.67%, and 92.4% for tensile strength, flexural strength, and impact strength, respectively, at 1.5% silane coupling agent.« less

Characterization of Mechanical Properties of Nuclear Graphite Using Subsize Specimens and Reusing Tested Specimens

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ji Hyun, Yoon; Byun, Thak Sang; Strizak, Joe P

2011-01-01

The mechanical properties of NBG-18 nuclear grade graphite have been characterized using small specimen test techniques and statistical treatment on the test results. New fracture strength and toughness test techniques were developed to use subsize cylindrical specimens with glued heads and to reuse their broken halves. Three sets of subsize cylindrical specimens with the different diameters of 4 mm, 8 mm, and 12 mm were tested to obtain tensile fracture strength. The longer piece of the broken halves was cracked from side surfaces and tested under three-point bend loading to obtain fracture toughness. Both the strength and fracture toughness datamore » were analyzed using Weibull distribution models focusing on size effect. The mean fracture strength decreased from 22.9 MPa to 21.5 MPa as the diameter increased from 4 mm to 12 mm, and the mean strength of 15.9 mm diameter standard specimen, 20.9 MPa, was on the extended trend line. These fracture strength data indicate that in the given diameter range the size effect is not significant and much smaller than that predicted by the Weibull statistics-based model. Further, no noticeable size effect existed in the fracture toughness data, whose mean values were in a narrow range of 1.21 1.26 MPa. The Weibull moduli measured for fracture strength and fracture toughness datasets were around 10. It is therefore believed that the small or negligible size effect enables to use the subsize specimens and that the new fracture toughness test method to reuse the broken specimens to help minimize irradiation space and radioactive waste.« less

Determining mechanical behavior of solid materials using miniature specimens

DOEpatents

Manahan, M.P.; Argon, A.S.; Harling, O.K.

1986-02-04

A Miniaturized Bend Test (MBT) capable of extracting and determining mechanical behavior information from specimens only so large as to have at least a volume or smallest dimension sufficient to satisfy continuum behavior in all directions is disclosed. The mechanical behavior of the material is determined from the measurements taken during the bending of the specimen and is processed according to the principles of linear or nonlinear material mechanics or both. In a preferred embodiment the determination is carried out by a code which is constructed according to the finite element method, and the specimen used for the determinations is a miniature disk simply supported for central loading at the axis on the center of the disk. 51 figs.

Effect of Boundary Condition on the Shear Behaviour of Rock Joints in the Direct Shear Test

NASA Astrophysics Data System (ADS)

Bahaaddini, M.

2017-05-01

The common method for determination of the mechanical properties of the rock joints is the direct shear test. This paper aims to study the effect of boundary condition on the results of direct shear tests. Experimental studies undertaken in this research showed that the peak shear strength is mostly overestimated. This problem is more pronounced for steep asperities and under high normal stresses. Investigation of the failure mode of these samples showed that tensile cracks are generated at the boundary of sample close to the specimen holders and propagated inside the intact materials. In order to discover the reason of observed failure mechanism in experiments, the direct shear test was simulated using PFC2D. Results of numerical models showed that the gap zone size between the upper and lower specimen holders has a significant effect on the shear mechanism. For the high gap size, stresses concentrate at the vicinity of the tips of specimen holders and result in generation and propagation of tensile cracks inside the intact material. However, by reducing the gap size, stresses are concentrated on asperities, and damage of specimen at its boundary is not observed. Results of this paper show that understanding the shear mechanism of rock joints is an essential step prior to interpreting the results of direct shear tests.

Characterization of Heat Treated Titanium-Based Implants by Nondestructive Eddy Current and Ultrasonic Tests

NASA Astrophysics Data System (ADS)

Mutlu, Ilven; Ekinci, Sinasi; Oktay, Enver

2014-06-01

This study presents nondestructive characterization of microstructure and mechanical properties of heat treated Ti, Ti-Cu, and Ti-6Al-4V titanium-based alloys and 17-4 PH stainless steel alloy for biomedical implant applications. Ti, Ti-Cu, and 17-4 PH stainless steel based implants were produced by powder metallurgy. Ti-6Al-4V alloy was investigated as bulk wrought specimens. Effects of sintering temperature, aging, and grain size on mechanical properties were investigated by nondestructive and destructive tests comparatively. Ultrasonic velocity in specimens was measured by using pulse-echo and transmission methods. Electrical conductivity of specimens was determined by eddy current tests. Determination of Young's modulus and strength is important in biomedical implants. Young's modulus of specimens was calculated by using ultrasonic velocities. Calculated Young's modulus values were compared and correlated with experimental values.

Test and Analysis of Composite Hat Stringer Pull-off Test Specimens

NASA Technical Reports Server (NTRS)

Li, Jian; OBrien, T. Kevin; Rousseau, Carl Q.

1996-01-01

Hat stringer pull-off tests were performed to evaluate the delamination failure mechanisms in the flange region for a rod-reinforced hat stringer section. A special test fixture was used to pull the hat off the stringer while reacting the pull-off load through roller supports at both stringer flanges. Microscopic examinations of the failed specimens revealed that failure occurred at the ply termination in the flange area where the flange of the stiffener is built up by adding 45/-45 tape plies on the top surface. Test results indicated that the as-manufactured microstructure in the flange region has a strong influence on the delamination initiation and the associated pull-off loads. Finite element models were created for each specimen with a detailed mesh based on micrographs of the critical location. A fracture mechanics approach and a mixed mode delamination criterion were used to predict the onset of delamination and the pull-off load. By modeling the critical local details of each specimen from micrographs, the model was able to accurately predict the hat stringer pull-off loads and replicate the variability in the test results.

A mechanical property and stress corrosion evaluation of 431 stainless steel alloy

NASA Technical Reports Server (NTRS)

Montano, J. W.

1973-01-01

The mechanical properties of type 431 stainless steel in two conditions: annealed bar and hardened and tempered bar are presented. Test specimens, manufactured from approximately 1.0 inch (2.54 cm) diameter bar stock, were tested at temperatures of 80 F (+26.7 C), 0 F (-17.8 C), -100 F (-73 C), and -200 F (-129 C). The test data indicated excellent tensile strength, notched/unnotched tensile ratio, ductility, shear, and impact properties at all testing temperatures. Results of the alternate immersion stress corrosion tests on stressed and unstressed longitudinal tensile specimens 0.1250 inch (0.3175 cm) diameter and transverse C-ring specimens, machined from 1.0 inch (2.54 cm) diameter bar stock, indicated that the material is not susceptible to stress corrosion cracking when tested in a 3.5 percent NaCl solution for 180 days.

Device for measuring hole elongation in a bolted joint

NASA Technical Reports Server (NTRS)

Wichorek, Gregory R. (Inventor)

1987-01-01

A device to determine the operable failure mode of mechanically fastened lightweight composite joints by measuring the hole elongation of a bolted joint is disclosed. The double-lap joint test apparatus comprises a stud, a test specimen having a hole, two load transfer plates, and linear displacement measuring instruments. The test specimen is sandwiched between the two load transfer plates and clamped together with the stud. Spacer washers are placed between the test specimen and each load transfer plate to provide a known, controllable area for the determination of clamping forces around the hole of the specimen attributable to bolt torque. The spacer washers also provide a gap for the mounting of reference angles on each side of the test specimen. Under tensile loading, elongation of the hole of the test specimen causes the stud to move away from the reference angles. This displacement is measured by the voltage output of two linear displacement measuring instruments that are attached to the stud and remain in contact with the reference angles throughout the tensile loading. The present invention obviates previous problems in obtaining specimen deformation measurements by monitoring the reference angles to the test specimen and the linear displacement measuring instruments to the stud.

In Situ Microstructural Control and Mechanical Testing Inside the Transmission Electron Microscope at Elevated Temperatures

NASA Astrophysics Data System (ADS)

Wang, Baoming; Haque, M. A.

2015-08-01

With atomic-scale imaging and analytical capabilities such as electron diffraction and energy-loss spectroscopy, the transmission electron microscope has allowed access to the internal microstructure of materials like no other microscopy. It has been mostly a passive or post-mortem analysis tool, but that trend is changing with in situ straining, heating and electrical biasing. In this study, we design and demonstrate a multi-functional microchip that integrates actuators, sensors, heaters and electrodes with freestanding electron transparent specimens. In addition to mechanical testing at elevated temperatures, the chip can actively control microstructures (grain growth and phase change) of the specimen material. Using nano-crystalline aluminum, nickel and zirconium as specimen materials, we demonstrate these novel capabilities inside the microscope. Our approach of active microstructural control and quantitative testing with real-time visualization can influence mechanistic modeling by providing direct and accurate evidence of the fundamental mechanisms behind materials behavior.

A preliminary mechanical property and stress corrosion evaluation of VIM-VAR work strengthened and direct aged Inconel 718 bar material

NASA Technical Reports Server (NTRS)

Montano, J. W.

1987-01-01

This report presents a preliminary mechanical property and stress corrosion evaluation of double melted (vacuum induction melted (VIM), and vacuum arc remelted (VAR)), solution treated, work strengthened and direct aged Inconel 718 alloy bar (5.50 in. (13.97 cm) diameter). Two sets of tensile specimens, one direct single aged and the other direct double aged, were tested at ambient temperature in both the longitudinal and transverse directions. Longitudinal tensile and yield strengths in excess of 200 ksi (1378.96 MPa) and 168 ksi (1158.33 MPa), respectively, were realized at ambient temperature, for the direct double aged specimen. No failures occurred in the single or double edged longitudinal and transverse tensile specimens stressed to 75 and 100 percent of their respective yield strengths and exposed to a salt fog environment for 180 days. Tensile tests performed after the stress corrosion test showed no mechanical property degradation.

Results of Mechanical Testing for Pyroceram(tm) Glass-Ceramic

NASA Technical Reports Server (NTRS)

Choi, Sung R.; Gyekenyesi, John P.

2003-01-01

Mechanical testing for Pyroceram (trademark) 9606 glass-ceramic fabricated by Corning was conducted to determine mechanical properties of the material including slow crack growth.Valid testing was not achieved in tension, compression, and shear testing due to inappropriate test specimen configurations provided and primarily due to the existence of fortified layer( in tension).

Transpiring Cooling of a Scram-Jet Engine Combustion Chamber

NASA Technical Reports Server (NTRS)

Choi, Sang H.; Scotti, Stephen J.; Song, Kyo D.; Ries,Heidi

1997-01-01

The peak cold-wall heating rate generated in a combustion chamber of a scram-jet engine can exceed 2000 Btu/sq ft sec (approx. 2344 W/sq cm). Therefore, a very effective heat dissipation mechanism is required to sustain such a high heating load. This research focused on the transpiration cooling mechanism that appears to be a promising approach to remove a large amount of heat from the engine wall. The transpiration cooling mechanism has two aspects. First, initial computations suggest that there is a reduction, as much as 75%, in the heat flux incident on the combustion chamber wall due to the transpirant modifying the combustor boundary layer. Secondly, the heat reaching the combustor wall is removed from the structure in a very effective manner by the transpirant. It is the second of these two mechanisms that is investigated experimentally in the subject paper. A transpiration cooling experiment using a radiant heating method, that provided a heat flux as high as 200 Btu/sq ft sec ( approx. 234 W/sq cm) on the surface of a specimen, was performed. The experiment utilized an arc-lamp facility (60-kW radiant power output) to provide a uniform heat flux to a test specimen. For safety reasons, helium gas was used as the transpirant in the experiments. The specimens were 1.9-cm diameter sintered, powdered-stainless-steel tubes of various porosities and a 2.54cm square tube with perforated multi-layered walls. A 15-cm portion of each specimen was heated. The cooling effectivenes and efficiencies by transpiration for each specimen were obtained using the experimental results. During the testing, various test specimens displayed a choking phenomenon in which the transpirant flow was limited as the heat flux was increased. The paper includes a preliminary analysis of the transpiration cooling mechanism and a scaling conversion study that translates the results from helium tests into the case when a hydrogen medium is used.

A mechanical property and stress corrosion evaluation of Custom 455 stainless steel alloy

NASA Technical Reports Server (NTRS)

Montano, J. W.

1972-01-01

The mechanical and stress corrosion properties are presented of vacuum melted Custom 455 stainless steel alloy bar (1.0-inch diameter) and sheet (0.083-inch thick) material aged at 950 F, 1000 F, and 1050 F. Low temperature mechanical properties were determined at temperatures of 80 F, 0 F, -100 F, and -200 F. For all three aging treatments, the ultimate tensile and 0.2 percent offset yield strengths increased with decreasing test temperatures while the elongation held fairly constant down to -100 F and decreased at -200 F. Reduction in Area decreased moderately with decreasing temperature for the longitudinal round (0.250-inch diameter) specimens. Notched tensile strength and charpy V-notched impact strength decreased with decreasing test temperature. For all three aging treatments, no failures were observed in the unstressed specimens or the specimens stressed to 50, 75, and 100 percent of their yield strengths for 180 days of alternate immersion testing in a 3.5 percent NaCl solution. As indicated by the results of tensile tests performed after alternate immersion testing, the mechanical properties of Custom 455 alloy were not affected by stress or exposure under the conditions of the evaluation.

Design, Fabrication and Test of Multi-Fiber Laminates

NASA Technical Reports Server (NTRS)

Pike, R. A.; Novak, R. C.

1975-01-01

Unidirectional and angleply multifiber laminates were tested for improved impact strength and other mechanical properties. The effects of several variables on the mechanical properties of epoxy matrix materials were described. These include fiber type (HMS and AS graphites, glass, and Kevlar 49), ratio of primary to hybridizing fiber and hybrid configuration. It is demonstrated that AS graphite/S glass in an intraply configuration results in the best combination of static and Charpy impact properties as well as superior ballistic impact resistance. Pendulum impact tests which were conducted on thin specimens are shown to produce different ranking of materials than tests conducted on standard thickness Charpy specimens. It is shown that the thin specimen results are in better agreement with the ballistic impact data. Additional static test data are reported as a function of temperature for the seven best hybrid configurations having epoxy, polyimide (PMR-15) and polyphenylquinoxaline resins as the matrix.

AGC-2 Specimen Post Irradiation Data Package Report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Windes, William Enoch; Swank, W. David; Rohrbaugh, David T.

This report documents results of the post-irradiation examination material property testing of the creep, control, and piggyback specimens from the irradiation creep capsule Advanced Graphite Creep (AGC)-2 are reported. This is the second of a series of six irradiation test trains planned as part of the AGC experiment to fully characterize the neutron irradiation effects and radiation creep behavior of current nuclear graphite grades. The AGC-2 capsule was irradiated in the Idaho National Laboratory Advanced Test Reactor at a nominal temperature of 600°C and to a peak dose of 5 dpa (displacements per atom). One-half of the creep specimens weremore » subjected to mechanical stresses (an applied stress of either 13.8, 17.2, or 20.7 MPa) to induce irradiation creep. All post-irradiation testing and measurement results are reported with the exception of the irradiation mechanical strength testing, which is the last destructive testing stage of the irradiation testing program. Material property tests were conducted on specimens from 15 nuclear graphite grades using a similar loading configuration as the first AGC capsule (AGC-1) to provide easy comparison between the two capsules. However, AGC-2 contained an increased number of specimens (i.e., 487 total specimens irradiated) and replaced specimens of the minor grade 2020 with the newer grade 2114. The data reported include specimen dimensions for both stressed and unstressed specimens to establish the irradiation creep rates, mass and volume data necessary to derive density, elastic constants (Young’s modulus, shear modulus, and Poisson’s ratio) from ultrasonic time-of-flight velocity measurements, Young’s modulus from the fundamental frequency of vibration, electrical resistivity, and thermal diffusivity and thermal expansion data from 100–500°C. No data outliers were determined after all measurements were completed. A brief statistical analysis was performed on the irradiated data and a limited comparison between pre- and post-irradiation properties is presented. A more complete evaluation of trends in the material property changes, as well as irradiation-induced creep due to irradiation, temperature, and applied load on specimens will be discussed in later AGC-2 post-irradiation examination analysis reports.« less

Prediction of fracture load and stiffness of the proximal femur by CT-based specimen specific finite element analysis: cadaveric validation study.

PubMed

Miura, Michiaki; Nakamura, Junichi; Matsuura, Yusuke; Wako, Yasushi; Suzuki, Takane; Hagiwara, Shigeo; Orita, Sumihisa; Inage, Kazuhide; Kawarai, Yuya; Sugano, Masahiko; Nawata, Kento; Ohtori, Seiji

2017-12-16

Finite element analysis (FEA) of the proximal femur has been previously validated with large mesh size, but these were insufficient to simulate the model with small implants in recent studies. This study aimed to validate the proximal femoral computed tomography (CT)-based specimen-specific FEA model with smaller mesh size using fresh frozen cadavers. Twenty proximal femora from 10 cadavers (mean age, 87.1 years) were examined. CT was performed on all specimens with a calibration phantom. Nonlinear FEA prediction with stance configuration was performed using Mechanical Finder (mesh,1.5 mm tetrahedral elements; shell thickness, 0.2 mm; Poisson's coefficient, 0.3), in comparison with mechanical testing. Force was applied at a fixed vertical displacement rate, and the magnitude of the applied load and displacement were continuously recorded. The fracture load and stiffness were calculated from force-displacement curve, and the correlation between mechanical testing and FEA prediction was examined. A pilot study with one femur revealed that the equations proposed by Keller for vertebra were the most reproducible for calculating Young's modulus and the yield stress of elements of the proximal femur. There was a good linear correlation between fracture loads of mechanical testing and FEA prediction (R 2 = 0.6187) and between the stiffness of mechanical testing and FEA prediction (R 2 = 0.5499). There was a good linear correlation between fracture load and stiffness (R 2 = 0.6345) in mechanical testing and an excellent correlation between these (R 2 = 0.9240) in FEA prediction. CT-based specimen-specific FEA model of the proximal femur with small element size was validated using fresh frozen cadavers. The equations proposed by Keller for vertebra were found to be the most reproducible for the proximal femur in elderly people.

Effects of asphalt rejuvenator on thermal and mechanical properties on oxidized hot mixed asphalt pavements

NASA Astrophysics Data System (ADS)

Farace, Nicholas A.; Buttlar, William G.; Reis, Henrique

2016-04-01

The utilization of asphalt rejuvenator, and its effectiveness for restoring thermal and mechanical properties was investigated via Disk-shaped Compact Tension (DC(T)) and acoustic emission (AE) testing for determining mechanical properties and embrittlement temperatures of the mixtures. During the DC(T) testing the fracture energies and peak loads were used to measure the resistance of the rejuvenated asphalt to low temperature cracking. The AE testing monitored the acoustic emission activity while the specimens were cooled from room temperature to -40 °C to estimate the temperature at which thermal cracking began (i.e. the embrittlement temperature). First, a baseline response was obtained by obtaining the mechanical and thermal response of virgin HMA samples and HMA samples that had been exposed to oxidative aging for 36 hours at 135°C. The results showed the virgin samples had much higher peak loads and fracture energies than the 36 hours aged samples. Acoustic Emission showed similar results with the virgin samples having embrittlement temperatures 10 °C cooler than the 36 hours aged specimens. Then, overaged for 36 hours specimens were treated different amounts of rejuvenator (10%, 15%, and 20% by weight of binder content) and left to dwell for increased amount of time periods varying from one to eight weeks. It was observed that the AE results showed an improvement of embrittlement temperature with increasing with the dwell times. The 8 weeks specimens had cooler embrittlement temperatures than the virgin specimens. Finally, the low temperature effects on fracture energy and peak load of the rejuvenated asphalt was investigated. Rejuvenator was applied (10% by weight of binder) to specimens aged 36 hours at 135 °C, and the dwell time was varied from 1 to 4 weeks. The results showed that the peak loads were restored to levels of the virgin specimens, and the fracture energies improved to levels beyond that of the virgin specimens. The results also showed a general trend of improvement for the AE testing of the embrittlement temperature.

Structure and mechanical properties of Cresco-Ti laser-welded joints and stress analyses using finite element models of fixed distal extension and fixed partial prosthetic designs.

PubMed

Uysal, Hakan; Kurtoglu, Cem; Gurbuz, Riza; Tutuncu, Naki

2005-03-01

The Cresco-Ti System uses a laser-welded process that provides an efficient technique to achieve passive fit frameworks. However, mechanical behavior of the laser-welded joint under biomechanical stress factors has not been demonstrated. This study describes the effect of Cresco-Ti laser-welding conditions on the material properties of the welded specimen and analyzes stresses on the weld joint through 3-dimensional finite element models (3-D FEM) of implant-supported fixed dentures with cantilever extensions and fixed partial denture designs. Twenty Grade III (ASTM B348) commercially pure titanium specimens were machine-milled to the dimensions described in the EN10002-1 tensile test standard and divided into test (n = 10) and control (n = 10) groups. The test specimens were sectioned and laser-welded. All specimens were subjected to tensile testing to determine yield strength (YS), ultimate tensile strength (UTS), and percent elongation (PE). The Knoop micro-indentation test was performed to determine the hardness of all specimens. On welded specimens, the hardness test was performed at the welded surface. Data were analyzed with the Mann-Whitney U test and Student's t test (alpha=.05). Fracture surfaces were examined by scanning electron microscopy to characterize the mode of fracture and identify defects due to welding. Three-dimensional FEMs were created that simulated a fixed denture with cantilever extensions supported by 5 implants (M1) and a fixed partial denture supported by 2 implants (M2), 1 of which was angled 30 degrees mesio-axially. An oblique load of 400 N with 15 degrees lingual-axial inclinations was applied to both models at various locations. Test specimens fractured between the weld and the parent material. No porosities were observed on the fractured surfaces. Mean values for YS, UTS, PE, and Knoop hardness were 428 +/- 88 MPa, 574 +/- 113 MPa, 11.2 +/- 0.4%, 270 +/- 17 KHN, respectively, for the control group and 642 +/- 2 MPa, 772 +/- 72 MPa, 4.8 +/- 0.7%, 353 +/- 23 KHN, respectively, for the test group. The differences between the groups were significant for all mechanical properties ( P <.05). For both models, the FEA revealed that maximum principal stresses were concentrated at the framework-weld junction but did not exceed the UTS of the weld joint. Within the constraints of the finite element models, mechanical failure of the welded joint between the support and the framework may not be expected under biomechanical conditions simulated in this study.

Mechanical Property Characterization and Modeling of Structural Materials.

DTIC Science & Technology

1982-02-01

ELEMENT ANALYSIS OF TEST SPECIMENS 69 a. Ring and Partial Ring Geometries 69 b. Keyhole and Wide-Notch Specimens 72 c. Three-Dimensional Results for...Figure 12. 45 16 Keyhole Specimen for Short-Crack Investigation (Dimensions in Inches). 47 17 Fatigue-Crack-Growth Rate for a Long Crack in 7075-T651...spacings. A modified keyhole specimen, 1/4-in. thick (shown in Fig. 16 ), was chosen for the investigation. The elongated specimen geometry was

ADAPTATION OF CRACK GROWTH DETECTION TECHNIQUES TO US MATERIAL TEST REACTORS

DOE Office of Scientific and Technical Information (OSTI.GOV)

A. Joseph Palmer; Sebastien P. Teysseyre; Kurt L. Davis

2015-04-01

A key component in evaluating the ability of Light Water Reactors to operate beyond 60 years is characterizing the degradation of materials exposed to radiation and various water chemistries. Of particular concern is the response of reactor materials to Irradiation Assisted Stress Corrosion Cracking (IASCC). Some test reactors outside the United States, such as the Halden Boiling Water Reactor (HBWR), have developed techniques to measure crack growth propagation during irradiation. The basic approach is to use a custom-designed compact loading mechanism to stress the specimen during irradiation, while the crack in the specimen is monitored in-situ using the Direct Currentmore » Potential Drop (DCPD) method. In 2012 the US Department of Energy commissioned the Idaho National Laboratory and the MIT Nuclear Reactor Laboratory (MIT NRL) to take the basic concepts developed at the HBWR and adapt them to a test rig capable of conducting in-pile IASCC tests in US Material Test Reactors. The first two and half years of the project consisted of designing and testing the loader mechanism, testing individual components of the in-pile rig and electronic support equipment, and autoclave testing of the rig design prior to insertion in the MIT Reactor. The load was applied to the specimen by means of a scissor like mechanism, actuated by a miniature metal bellows driven by pneumatic pressure and sized to fit within the small in-core irradiation volume. In addition to the loader design, technical challenges included developing robust connections to the specimen for the applied current and voltage measurements, appropriate ceramic insulating materials that can endure the LWR environment, dealing with the high electromagnetic noise environment of a reactor core at full power, and accommodating material property changes in the specimen, due primarily to fast neutron damage, which change the specimen resistance without additional crack growth. The project culminated with an in-pile demonstration at the MIT Reactor. The test rig and associated support equipment were used to apply loads to a representative Compact Tensile specimen during one MITR operating cycle, while measuring crack growth using the DCPD method. Although the test period was short (approximately 70 days), and the accumulated neutron dose relatively small, successful operation of the test rig was demonstrated. The specimen was cycled more than 8000 times (more than would be typical for a long term IASCC test), which was sufficient to propagate a crack of over 2 mm.« less

Effect of extraoral aging conditions on mechanical properties of maxillofacial silicone elastomer.

PubMed

Hatamleh, Muhanad M; Polyzois, Gregory L; Silikas, Nick; Watts, David C

2011-08-01

The purpose of this study was to investigate the effect of extraoral human and environmental conditions on the mechanical properties (tensile strength and modulus, elongation, tear strength hardness) of maxillofacial silicone elastomer. Specimens were fabricated using TechSil-S25 silicone elastomer (Technovent Ltd, Leeds, UK). Eight groups were prepared (21 specimens in each group; eight tensile, eight tear, five hardness) and conditioned differently as follows (groups 1 through 8): Dry storage for 24 hours; dry storage in dark for 6 months; storage in simulated sebum solution for 6 months; storage in simulated acidic perspiration for 6 months; accelerated artificial daylight aging under controlled moisture for 360 hours; outdoor weathering for 6 months; storage in antimicrobial silicone-cleaning solution for 30 hours; and mixed conditioning of sebum storage and light aging for 360 hours. The conditioning period selected simulated a prosthesis being in service for up to 12 months. Tensile and tear test specimens were fabricated and tested according to the International Standards Organization (ISO) standards no. 37 and 34, respectively. Shore A hardness test specimens were fabricated and tested according to the American Standards for Testing and Materials (ASTM) D 2240. Data were analyzed with one-way ANOVA, Bonferroni, and Dunnett's T3 post hoc tests (p < 0.05). Weibull analysis was also used for tensile strength and tear strength. Statistically significant differences were evident among all properties tested. Mixed conditioning of simulated sebum storage under accelerated artificial daylight aging significantly degraded mechanical properties of the silicone (p < 0.05). Mechanical properties of maxillofacial elastomers are adversely affected by human and environmental factors. Mixed aging of storage in simulated sebum under accelerated daylight aging was the most degrading regime. Accelerated aging of silicone specimens in simulated sebum under artificial daylight for 12 months of simulated clinical service greatly affected functional properties of silicone elastomer; however, in real practice, the effect is modest, since sebum concentration is lower, and daylight is less concentrated. © 2011 by The American College of Prosthodontists.

Effect of temperature, microstructure, and stress state on the low cycle fatigue behavior of Waspaloy

NASA Technical Reports Server (NTRS)

Stahl, D. R.; Antolovich, S. D.; Mirdamadi, M.; Zamrik, S. Y.

1988-01-01

Specimens of Waspaloy of two different microstructures were tested in uniaxial and torsional low-cycle fatigue at 24 and 649 C. For all specimens, deformation and failure mechanisms are found to be independent of stress state at 24 C; in both microstructures, failure is associated with the formation of shear cracks. At 649 C, deformation and failure mechanisms for the fine-grain large gamma-prime specimens are independent of stress state, and the mechanisms are similar to those observed at 24 C. For the coarse-grain small gamma-prime specimens, however, failure occurs on principal planes in torsion and on shear plane in uniaxial tension. The results are interpreted in terms of deformation mode and microstructural instability.

Energy monitoring and analysis during deformation of bedded-sandstone: use of acoustic emission.

PubMed

Wasantha, P L P; Ranjith, P G; Shao, S S

2014-01-01

This paper investigates the mechanical behaviour and energy releasing characteristics of bedded-sandstone with bedding layers in different orientations, under uniaxial compression. Cylindrical sandstone specimens (54 mm diameter and 108 mm height) with bedding layers inclined at angles of 10°, 20°, 35°, 55°, and 83° to the minor principal stress direction, were produced to perform a series of Uniaxial Compressive Strength (UCS) tests. One of the two identical sample sets was fully-saturated with water before testing and the other set was tested under dry conditions. An acoustic emission system was employed in all the testing to monitor the acoustic energy release during the whole deformation process of specimens. From the test results, the critical joint orientation was observed as 55° for both dry and saturated samples and the peak-strength losses due to water were 15.56%, 20.06%, 13.5%, 13.2%, and 13.52% for the bedding orientations 10°, 20°, 35°, 55°, and 83°, respectively. The failure mechanisms for the specimens with bedding layers in 10°, 20° orientations showed splitting type failure, while the specimens with bedding layers in 55°, 83° orientations were failed by sliding along a weaker bedding layer. The failure mechanism for the specimens with bedding layers in 35° orientation showed a mixed failure mode of both splitting and sliding types. Analysis of the acoustic energy, captured from the acoustic emission detection system, revealed that the acoustic energy release is considerably higher in dry specimens than that of the saturated specimens at any bedding orientation. In addition, higher energy release was observed for specimens with bedding layers oriented in shallow angles (which were undergoing splitting type failures), whereas specimens with steeply oriented bedding layers (which were undergoing sliding type failures) showed a comparatively less energy release under both dry and saturated conditions. Moreover, a considerable amount of energy dissipation before the ultimate failure was observed for specimens with bedding layers oriented in shallow angles under both dry and saturated conditions. These results confirm that when rock having bedding layers inclined in shallow angles the failures could be more violent and devastative than the failures of rock with steeply oriented bedding layers. Copyright © 2013 Elsevier B.V. All rights reserved.

SLM processing-microstructure-mechanical property correlation in an aluminum alloy produced by additive manufacturing

NASA Astrophysics Data System (ADS)

Alejos, Martin Fernando

Additive manufacturing has become a highly researched topic in recent years all over the world. The current research evaluates the merits of additive manufacturing based on the mechanical, microstructural, and fracture properties of additive manufactured AlSi10Mg test specimens. The additive manufactured build plates consisted of tensile and fatigue test specimens. They were printed in the 0°, 30°, 60°, and 90° orientations relative to the build platform. Tensile and dynamic fatigue tests were conducted followed by microstructural characterization and fracture analysis. A wrought 6061 T6 aluminum alloy was also tested for comparison. Tensile tests revealed similar ultimate tensile strengths for all aluminum tensile specimens (350-380 MPa). Fatigue strength was greatest for wrought 6061 T6 aluminum (175 MPa). The fatigue behavior was a strong function of build orientation for the additive manufactured specimens. The 0°, 30°, and 60° orientations had fatigue strengths close to 104 MPa while the 90° orientation had a fatigue strength of 125 MPa. All test specimens failed primarily in a ductile manner. The effect of laser power, hatch spacing, and scan speed were also studied using microstructural analysis. Increasing laser power decreased grain size and void size. Increasing scan speed led to the formation of columnar grains. Increasing hatch spacing decreased grain size and the amount of voids present in the microstructure.

Tensile strength of various nylon PA6 specimen modes

NASA Astrophysics Data System (ADS)

Raz, Karel; Zahalka, Martin

2017-05-01

This article explores the influence of production technique on the strength of nylon parts. Identical specimens were manufactured by various techniques. The material of specimens was nylon PA6. 3D printing and injection molding were used, with various orientations of printed layers, and various orientations of specimens in the working space of the 3D printer. The variants are described in detail. A special mold was used for the injection molding process in order to make specimens with and without a weld line. The effect of this weld line was evaluated. All specimens were tested using the standard tensile test configuration. The strength was compared. It was found that the same plastic material has very different mechanical properties depending on the production process.

Characterizing Sintered Nano-Hydroxyapatite Sol-Gel Coating Deposited on a Biomedical Ti-Zr-Nb Alloy

NASA Astrophysics Data System (ADS)

Jafari, Hassan; Hessam, Hamid; Shahri, Seyed Morteza Ghaffari; Assadian, Mahtab; Shairazifard, Shahin Hamtaie Pour; Idris, Mohd Hasbullah

2016-03-01

In this study, sol-gel dip-coating method was used to coat nano-hydroxyapatite on specimens of Ti-14Zr-13Nb alloy for orthopedic applications. The coated specimens were sintered at three different temperatures and time spans to evaluate the impact of sintering process on microstructure, mechanical, bio-corrosion, and bioactivity properties of the coating. Field-emission scanning electron microscopy and x-ray diffraction were used to analyze the coating microstructure. Coating adhesion and mechanical performance were also investigated by scratch testing. Besides, electrochemical corrosion and immersion tests were performed in simulated body fluid to examine the sintering effect on corrosion performance and bioactivity of the coatings, respectively. The evaluations of coated specimens displayed that sintering at elevated temperatures leads to higher surface integrity and improves crystallinity of the nano-hydroxyapatite to approximately 89% which brings about distinctively enhanced mechanical properties. Similarly, it improved the corrosion rate for about 17 times through sintering at 700 °C. Immersion test proved that the coating increased the bioactivity resulted from the dissolution of calcium phosphates into the corresponding environment. It is noticeable that sintering the dip-coated specimens in the nano-hydroxyapatite improves corrosion performance and maintains bioactive behaviors as well.

Mechanical testing of advanced coating system, volume 1

NASA Technical Reports Server (NTRS)

Cruse, T. A.; Nagy, A.; Popelar, C. F.

1990-01-01

The Electron Beam Physical Vapor Deposition (EBPVD) coating material has a highly columnar microstructure, and as a result it was expected to have very low tensile strength. To be able to fabricate the required compression and tensile specimens, a substrate was required to provide structural integrity for the specimens. Substrate and coating dimensions were adjusted to provide sufficient sensitivity to resolve the projected loads carried by the EBPVD coating. The use of two distinctively different strain transducer systems, for tension and compression loadings, mandated two vastly different specimen geometries. Compression specimen and tensile specimen geometries are given. Both compression and tensile test setups are described. Data reduction mathematical models are given and discussed in detail as is the interpretation of the results. Creep test data is also given and discussed.

Effects of Post-Weld Heat Treatment on the Mechanical Properties of Similar- and Dissimilar-Alloy Friction Stir Welded Blanks

NASA Astrophysics Data System (ADS)

Zadpoor, Amir Abbas; Sinke, Jos

2011-01-01

Friction stir welding is a solid state joining process with relatively low welding temperatures. Nevertheless, the mechanical properties of friction stir welded blanks are degraded after welding. Indeed, both strength and ductility of the welds are decreased after welding. Often, the resulting friction stir welded blanks need to be formed to their final structural shape. Therefore, the formability of friction stir welded blanks is of primary importance in the manufacturing of structural parts. This paper studies how the mechanical properties and particularly formability of friction stir welded blanks can be improved by applying a post weld heat treatment. Two aluminum alloys from 2000 and 7000 series, namely 2024-T3 and 7075-T6, are selected for the study. The sheet thickness of both materials is 2,0 mm. The selected alloys are welded in three configurations: 2024-T3 and 2024-T3, 7075-T6 and 7075-T6, and 2024-T3 and 7075-T6. The resulting welds are naturally aged for a few months. Three sets of standard dog bone shape tensile test specimens are then machined from the welds. The first set of the specimens is tested without any heat treatment. The second set of the specimens is solution heat treated and quenched before testing. The third set of the specimens is solution heat treated, quenched, and naturally aged for a week before testing. The mechanical properties of the three different sets of specimens are compared with each other. It is shown that careful selection of post weld heat-treatment can greatly improve the formability of friction stir welded blanks.

Influence of precracked specimen configuration and starting stress intensity on the stress corrosion cracking of 4340 steel

NASA Technical Reports Server (NTRS)

Lisagor, W. B.

1984-01-01

Since the pioneer work of Brown (1966), precracked specimens and related fracture mechanics analyses have been extensively used to study stress corrosion cracking. Certain questions arose in connection with initial attempts to prepare standardized recommended practices by ASTM Committee G-1 on Corrosion of Metals. These questions were related to adequacy of test control as it pertains to acceptable limits of variability, and to validity of expressions for stress intensity and crack-surface displacements for both specimen configurations. An interlaboratory test program, was, therefore, planned with the objective to examine the validity of KIscc testing for selected specimen configurations, materials,and environmental systems. The results reported in the present paper include details of a single laboratory test program. The program was conducted to determine if the threshold value of stress intensity for onset and arrest of stress corrosion cracking was independent for the two specimen configurations examined.

The stress-corrosion behavior of Al-Li-Cu alloys: A comparison of test methods

NASA Technical Reports Server (NTRS)

Rizzo, P. P.; Galvin, R. P.; Nelson, H. G.

1982-01-01

Two powder metallurgy processed (Al-Li-Cu) alloys with and without Mg addition were studied in aqueous 3.5% NaCl solution during the alternate immersion testing of tuning fork specimens, slow crack growth tests using fracture mechanics specimens, and the slow strain rate testing of straining electrode specimens. Scanning electron microscopy and optical metallography were used to demonstrate the character of the interaction between the Al-Li-Cu alloys and the selected environment. Both alloys are susceptible to SC in an aqueous 3.5% NaCl solution under the right electrochemical and microstructural conditions. Each test method yields important information on the character of the SC behavior. Under all conditions investigated, second phase particles strung out in rows along the extrusion direction in the alloys were rapidly attacked, and played principal role in the SC process. With time, larger pits developed from these rows of smaller pits and under certain electrochemical conditions surface cracks initiated from the larger pits and contributed directly to the fracture process. Evidence to support slow crack growth was observed in both the slow strain rate tests and the sustained immersion tests of precracked fracture mechanics specimens. The possible role of H2 in the stress corrosion cracking process is suggested.

Intra-Laminar Fracture Toughness of Glass Fiber Reinforced Polymer By Using Theory, Experimentation and FEA

NASA Astrophysics Data System (ADS)

Firojkhan, Pathan; Tanpure, Kshitijit; Dawale, Ajinkya; Patil, Shital

2018-04-01

Fiber reinforced polymer (FRP) composites are widely use in aerospace, marine, auto-mobile and civil engineering applications because of their high strength-to-weight and stiffness-to-weight ratios, corrosion resistance and potentially high durability. The purpose of this research is to experimentally investigate the mechanical and fracture properties of glass-fiber reinforced polyester composite material, 450 g/m 2 randomly distributed glass-fiber mat also known as woven strand mat with polyester resin as a matrix. The samples have been produced by the conventional hand layup process and the specimens were prepared as per the ASTM standards. The tensile test was performed on the composite specimens using Universal testing machine (UTM) which are used for the finite element simulation of composite Layered fracture model. The mechanical properties were evaluated from the stress vs. strain curve obtained from the test result. Later, fracture tests were performed on the CT specimen. In case of CT specimen the load vs. Displacement plot obtained from the experimental results was used to determine the fracture properties of the composite. The failure load of CT specimen using FEA is simulated which gives the Stress intensity factor by using FEA. Good agreement between the FEA and experimental results was observed.

Laser-heated rotating specimen autoignition test

NASA Technical Reports Server (NTRS)

Au, A. C.

1988-01-01

Specimens of 440 C steel were rotated in a chamber pressurized with oxygen gas and heated with a 5-kW CO2 laser to determine the temperature required for autoignition to occur. Tests included exposures of static and rotating (25,000 rpm) specimens in oxygen pressurized to 5.51 MPa, and with focused laser fluences of more than 3.5 billion W/sq m. Specimen surface temperatures were monitored with a scanning infrared camera. Temperature measurement difficulties were experienced due to a problem with internal reflection inside the test chamber; however, posttest specimen examinations confirmed that surface melt (1371 C) was achieved in several tests. No sustained combustion was initiated in any rotating specimen. One static specimen was ignited. Results indicated that conditions necessary for autoignition of 440 C steel are more dependent on specimen geometry and available heat removal mechanisms. Sustained combustion occurred in the ignited static specimen with an estimated 130 C/sec cooling rate due to conduction. The rotating specimens could not sustain combustion due to a greater conductive/convective cooling rate of about 4000 C/sec and ejection of molten material. These results were applied to the Space Shuttle Main Engine (SSME) oxygen turbopump bearings to conclude that the LOX-cooled 440 C steel bearings cannot sustain combustion initiated by skidding friction.

Noncontacting-optical-strain device

NASA Technical Reports Server (NTRS)

Silver, R. H.

1970-01-01

Noncontacting-strain-measuring gauge and extensometer remotely measures the mechanical displacement along the entire length of a test specimen. Measurement is accomplished by continuous scanning of a reflected light from reflective bench markings or stripes previously affixed to the specimen.

Mechanical properties of woven glass fiber-reinforced composites.

PubMed

Kanie, Takahito; Arikawa, Hiroyuki; Fujii, Koichi; Ban, Seiji

2006-06-01

The aim of this investigation was to measure the flexural and compressive strengths and the corresponding moduli of cylindrical composite specimens reinforced with woven glass fiber. Test specimens were made by light-curing urethane dimethacrylate oligomer with woven glass fiber of 0.18-mm standard thickness. Tests were conducted using four reinforcement methods and two specimen diameters. Flexural strength and modulus of woven glass fiber-reinforced specimens were significantly greater than those without woven glass fiber (p < 0.01). Likewise, compressive strength of reinforced specimens was significantly greater than those without woven glass fiber (p < 0.01), except for specimens reinforced with woven glass fiber oriented at a tilt direction in the texture (p > 0.05). In terms of comparison between the two specimen diameters, no statistically significant differences in flexural strength and compressive strength (p > 0.05) were observed.

Mechanical Testing of Silicon Carbide on MISSE-7

DTIC Science & Technology

2012-07-15

JS) ii Abstract Silicon carbide ( SiC ) mechanical test specimens were included on the second Optical and Reflector Materials Experiment (ORMatE II...2. Vendor 2 EFS Weibull Results (normalized to Extra Disks Weibull parameters) 12 1. Introduction Silicon carbide ( SiC ) mechanical test...AEROSPACE REPORT NO ATR-2012(8921)-5 Mechanical Testing of Silicon Carbide on MISSE-7 Jul> 15. 2012 David B. Witkin Space Materials Laboratory

Interlaboratory round robin study on axial tensile properties of SiC-SiC CMC tubular test specimens [Interlaboratory round robin study on axial tensile properties of SiC/SiC tubes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Singh, Gyanender P.; Gonczy, Steve T.; Deck, Christian P.

An interlaboratory round robin study was conducted on the tensile strength of SiC–SiC ceramic matrix composite (CMC) tubular test specimens at room temperature with the objective of expanding the database of mechanical properties of nuclear grade SiC–SiC and establishing the precision and bias statement for standard test method ASTM C1773. The mechanical properties statistics from the round robin study and the precision statistics and precision statement are presented herein. The data show reasonable consistency across the laboratories, indicating that the current C1773–13 ASTM standard is adequate for testing ceramic fiber reinforced ceramic matrix composite tubular test specimen. Furthermore, it wasmore » found that the distribution of ultimate tensile strength data was best described with a two–parameter Weibull distribution, while a lognormal distribution provided a good description of the distribution of proportional limit stress data.« less

Interlaboratory round robin study on axial tensile properties of SiC-SiC CMC tubular test specimens [Interlaboratory round robin study on axial tensile properties of SiC/SiC tubes

DOE PAGES

Singh, Gyanender P.; Gonczy, Steve T.; Deck, Christian P.; ...

2018-04-19

An interlaboratory round robin study was conducted on the tensile strength of SiC–SiC ceramic matrix composite (CMC) tubular test specimens at room temperature with the objective of expanding the database of mechanical properties of nuclear grade SiC–SiC and establishing the precision and bias statement for standard test method ASTM C1773. The mechanical properties statistics from the round robin study and the precision statistics and precision statement are presented herein. The data show reasonable consistency across the laboratories, indicating that the current C1773–13 ASTM standard is adequate for testing ceramic fiber reinforced ceramic matrix composite tubular test specimen. Furthermore, it wasmore » found that the distribution of ultimate tensile strength data was best described with a two–parameter Weibull distribution, while a lognormal distribution provided a good description of the distribution of proportional limit stress data.« less

Production of ultrafine grained aluminum by cyclic severe plastic deformation at ambient temperature

NASA Astrophysics Data System (ADS)

Bereczki, P.; Szombathelyi, V.; Krallics, G.

2014-08-01

In the present study the possibilities of grain refinement was investigated by applying large-scale of cyclic plastic deformation to aluminum at ambient temperature. The specimens are processed by multiaxial forging, which is one of the severe plastic deformation techniques. The aim of the experiments with the aluminum alloy 6082M was the determination of the equivalent stress and strain by multiaxial forging and the investigation of evolution of mechanical properties in relation with the accumulated deformation in the specimen. The mechanical properties of raw material was determined by plane strain compression test as well as by hardness measurements. The forming experiments were carried out on Gleeble 3800 physical simulator with MaxStrain System. The mechanical properties of the forged specimens were investigated by micro hardness measurements and tensile tests. A mechanical model, based on the principle of virtual velocities was developed to calculate the flow curves using the measured dimensional changes of the specimen and the measured force. With respect to the evolution of these curves, the cyclic growth of the flow stress can be observed at every characteristic points of the calculated flow curves. In accordance with this tendency, the evolution of the hardness along the middle cross section of the deformed volume has also a nonmonotonous characteristic and the magnitudes of these values are much smaller than by the specimen after plane strain compression test. This difference between the flow stresses respect to the monotonic and non-monotonic deformation can be also observed. The formed microstructure, after a 10-passes multiaxial forging process, consists of mainly equiaxial grains in the submicron grain scale.

i RadMat: A thermo-mechanical testing system for in situ high-energy X-ray characterization of radioactive specimens

DOE PAGES

Zhang, Xuan; Xu, Chi; Wang, Leyun; ...

2017-01-27

Here, we present an in situ Radiated Materials (iRadMat) experimental module designed to interface with a servo-hydraulic load frame for X-ray measurements at beamline 1-ID at the Advanced Photon Source. This new capability allows in situ studies of radioactive specimens subject to thermo-mechanical loading using a suite of high-energy X-ray scattering and imaging techniques. The iRadMat is a radiation-shielded vacuum heating system with the sample rotation-under-load capability. We describe the design features and performances of the iRadMat and present a dataset from a 300 °C uniaxial tensile test of a neutron-irradiated pure Fe specimen to demonstrate its capabilities.

Effect of weld line positions on the tensile deformation of two-component metal injection moulding

NASA Astrophysics Data System (ADS)

Manonukul, Anchalee; Songkuea, Sukrit; Moonchaleanporn, Pongporn; Tange, Makiko

2017-12-01

Knowledge of the mechanical properties of two-component parts is critical for engineering functionally graded components. In this study, mono- and two-component tensile test specimens were metal injection moulded. Three different weld line positions were generated in the two-component specimens. Linear shrinkage of the two-component specimens was greater than that of the mono-component specimens because the incompatibility of sintering shrinkage of both materials causes biaxial stresses and enhances sintering. The mechanical properties of 316L stainless steel were affected by the addition of a coloured pigment used to identify the weld line position after injection moulding. For the two-component specimens, the yield stress and ultimate tensile stress were similar to those of 316L stainless steel. Because 316L and 630 (also known as 17-4PH) stainless steels were well-sintered at the interface, the mechanical properties of the weaker material (316L stainless steel) were dominant. However, the elongations of the two-component specimens were lower than those of the mono-component specimens. An interfacial zone with a microstructure that differed from those of the mono-material specimens was observed; its different microstructure was attributed to the gradual diffusion of nickel and copper.

Fracture mechanics data for 2024-T861 and 2124-T851 aluminum

NASA Technical Reports Server (NTRS)

Pionke, L. J.; Linback, R. K.

1974-01-01

The fracture toughness and fatigue flaw growth characteristics of 2024-T861 and 2124-T851 aluminum were evaluated under plane stress conditions. Center cracked tension specimens were employed to evaluate these properties under a number of different test conditions which included variations in specimen thickness, specimen orientation, test environment, and initial flaw size. The effect of buckling was also investigated for all tests of thin gage specimens, and the effect of frequency and stress ratio was evaluated for the cyclic tests. Fracture toughness test results were analyzed and presented in terms of fracture resistance curves; fatigue flaw growth data was analyzed using empirical rate models. The results of the study indicate that both fracture toughness and resistance to fatigue crack growth improve with increasing temperature and decreasing thickness. The presence of buckling during testing of thin gage panels was found to degrade the resistance to fatigue flaw growth only at elevated temperatures.

Damage mechanisms in bithermal and thermomechanical fatigue of Haynes 188

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; Halford, Gary R.

1992-01-01

Post failure fractographic and metallographic studies were conducted on Haynes 188 specimens fatigued under bithermal and thermomechanical loading conditions between 316 and 760 C. Bithermal fatigue specimens examined included those tested under high strain rate in-phase and out-phase, tensile creep in-phase, and compressive creep out-of-phase loading conditions. Specimens tested under in-phase and out-of-phase thermomechanical fatigue were also examined. The nature of failure mode (transgrandular versus intergranular), the topography of the fracture surface, and the roles of oxidation and metallurgical changes were studied for each type of bithermal and thermomechanical test.

Strain controlled cyclic tests on miniaturized specimens

NASA Astrophysics Data System (ADS)

Procházka, R.; Džugan, J.

2017-02-01

The paper is dealing with strain controlled cyclic tests using a non-contact strain measurement based on digital image correlation techniques on proportional sizes of conventional specimens. The cyclic behaviour of 34CrNiMo6 high-strength steel was investigated on miniaturized round specimens with diameter of 2mm that were compared with specimens in accordance with ASTM E606 standards. The cycle asymmetry coefficient was R= -1. This application is intended to be used for life time assessment of in service components in future work which enables to carried out a group of mechanical tests from a limited amount of the experimental material. The attention was paid to confirm the suitability of the proposed size miniaturization geometry, testing set up and procedure. The test results obtained enabled to construct Manson-Coffin curves and assess fatigue parameters. The purpose of this study is to present differences between cyclic curves and cyclic parameters which have been evaluated based on conventional and miniaturized specimens.

Mechanical Properties of a Unidirectional Basalt-Fiber-Reinforced Plastic Under a Loading Simulating Operation Conditions

NASA Astrophysics Data System (ADS)

Lobanov, D. S.; Slovikov, S. V.

2017-01-01

The results of experimental investigations of unidirectional composites based on basalt fibers and different marks of epoxy resins are presented. Uniaxial tensile tests were carried out using a specimen fixation technique simulating the operation conditions of structures. The mechanical properties of the basalt-fiber-reinforced plastics (BFRPs) were determined. The diagrams of loading and deformation of BFRP specimens were obtain. The formulations of the composites with the highest mechanical properties were revealed.

Experimental Investigation of Mechanical Behavior of an Oxide/Oxide Ceramic Composite in Interlaminar Shear and under Combined Tension-Torsion Loading

DTIC Science & Technology

2014-03-27

testing machine was warmed up for at least 30 min using a cyclic command with a sine waveform in displacement control . Gripping sections of each test...the test specimen was inserted into the susceptor. Then the testing machine is placed in displacement control and the top portion of the specimen...the MTS software also triggered the operation of the high speed cameras. 31 The testing system was placed in displacement /rotation control and the

The stress corrosion resistance and the cryogenic temperature mechanical properties of hot rolled Nitronic 32 bar material

NASA Technical Reports Server (NTRS)

Montano, J. W. L.

1977-01-01

The ambient and cryogenic temperature mechanical properties and the ambient temperature stress corrosion properties of hot rolled and centerless ground Nitronic 32 stainless steel bar material are presented. The mechanical properties of longitudinal specimens were evaluated at test temperatures from ambient to liquid hydrogen. The tensile test data indicated increasing smooth tensile strength with decreasing temperature to liquid hydrogen temperature. However, below -200 F (-129.0 C) the notched tensile strength decreased slightly and below -320 F (-196.0 C) the decrease was significant. The elongation and reduction of area decreased drastically at temperatures below -200 F (-129.0 C). The Charpy V-notched impact energy decreased steadily with decreasing test temperature. Stress corrosion tests were performed on longitudinal tensile specimens stressed to 0, 75, and 90 percent of the 0.2 percent yield strength and on transverse 'C'-ring specimens stressed to 75 and 90 percent of the yield strength and exposed to: alternate immersion in a 3.5 percent NaCl bath, humidity cabinet environment, and a 5 percent salt spray atmosphere. The longitudinal tensile specimens experienced no corrosive attack; however, the 'C'-rings exposed to the alternate immersion and to the salt spray experienced some shallow etching and pitting, respectively. Small cracks appeared in two of the 'C'-rings after one month exposure to the salt spray.

Failure mechanism of resistance-spot-welded specimens impacted on base material by bullets

NASA Astrophysics Data System (ADS)

Fan, Chunlei; Ma, Bohan; Chen, Danian; Wang, Huanran; Ma, Dongfang

2018-01-01

The tests of bullet impact on the base material (BM) of a simple specimen with a single resistance-spot-welded (RSW) nugget of TRIP800 steel are performed to investigate the response of the RSW specimen to the ballistic debris impact on the RSW specimen. A one-stage gas gun is used to fire the bullets while a laser velocity interferometer system for any reflector (VISAR) is used to measure the velocity histories of the free surfaces of the RSW specimen. The recovered RSW specimens are examined with the three-dimensional super depth digital microscope (SDDM) and the scanning electro microscope (SEM). For the tests of small multiple-bullet impact, it is revealed that the wave train of the VISAR measured results and the detachment of the base material interfaces in the recovered RSW specimens are directly related to the reflection and refraction of the curved stress waves incoming to the interfaces and the free surfaces in the RSW specimens. The detachment of BM interfaces can lead to the impact failure of the RSW joints for the larger multiple-bullet impact at higher velocity, the mechanism of which is different from the case for normal incidence (spalling). For the tests of single large bullet impact, it is brought to light experimentally that the plastic strain concentration at the "notch tip" spurs either the crack near the RSW joint or the split of the nugget. The numerical simulation shows up the process of splitting the nugget: a crack initiates at the "notch tip", propagates across the nugget interface and splits the nugget into two parts. It is indicated that the interaction between the stress waves and many interfaces/free surfaces in the RSW specimen under ballistic impact causes variable local stress triaxialities and stress Lode angles, which affects the deformation and fracture mechanism of the RSW specimen including stretching and shearing failure. It is shown that the impact failure of the RSW joints is a mixture of brittle fracture and ductile fracture while the fracture or perforation of the BM is ductile.

Fatigue Behavior of Porous Ti-6Al-4V Made by Laser-Engineered Net Shaping.

PubMed

Razavi, Seyed Mohammad Javad; Bordonaro, Giancarlo G; Ferro, Paolo; Torgersen, Jan; Berto, Filippo

2018-02-12

The fatigue behavior and fracture mechanisms of additively manufactured Ti-6Al-4V specimens are investigated in this study. Three sets of testing samples were fabricated for the assessment of fatigue life. The first batch of samples was built by using Laser-Engineered Net Shaping (LENS) technology, a Direct Energy Deposition (DED) method. Internal voids and defects were induced in a second batch of samples by changing LENS machine processing parameters. Fatigue performance of these samples is compared to the wrought Ti-6Al-4V samples. The effects of machine-induced porosity are assessed on mechanical properties and results are presented in the form of SN curves for the three sets of samples. Fracture mechanisms are examined by using Scanning Electron Microscopy (SEM) to characterize the morphological characteristics of the failure surface. Different fracture surface morphologies are observed for porous and non-porous specimens due to the combination of head write speed and laser power. Formation of defects such as pores, unmelted regions, and gas entrapments affect the failure mechanisms in porous specimens. Non-porous specimens exhibit fatigue properties comparable with that of the wrought specimens, but porous specimens are found to show a tremendous reduced fatigue strength.

Thermal-Mechanical Fatigue Testing of a Titanium-Aluminide Alloy.

DTIC Science & Technology

1987-12-01

DIMSTRIBUTION STA Approved for pubi robing e% dQ *- AFIT/GAB/AA/87D-18 THERMAL-MECHANICAL FATIGUE TESTING OF A TITANIUM - ALUMINIDE ALLOY THESIS John J...THERMAL-MECHANICAL FATIGUE TESTING OF A TITANIUM - ALUMINIDE ALLOY THESIS Presented to the Faculty of the School of Engineering of the Air Force Institute...develop a Thermal-Mechanical Fatigue (TMF) testing system for titanium - aluminide compact tension specimens. I could not have accomplished this without the

Resistance of polyamide-6 against long time effects of various media at various temperatures

NASA Technical Reports Server (NTRS)

Debski, W.; Przylecka, M.

1988-01-01

During the first phase of tempering of polyamide-6, there are temporary changes which are apparently related to the lamella structure of the material. Test specimens at high temperature show that the mechanical properties of polyamide-6 are changed permanently, and mostly at 80 C. From the results of density tests and X-ray analysis, it follows that these changes depend on environmental influences and differ in gaseous and liquid media. The results of the test specimens of the mechanical properties as a function of temperature and the medium give information about the practical applications of polyamide-6.

A mechanical system for tensile testing of supported films at the nanoscale.

PubMed

Pantano, Maria F; Speranza, G; Galiotis, Costas; Pugno, Nicola M

2018-06-27

Standard tensile tests of materials are usually performed on freestanding specimens. However, such requirement is difficult to implement when the materials of interest are of nanoscopic dimensions due to problems related to their handling and manipulation. In the present paper, a new device is presented for tensile testing of thin nanomaterials, which allows tests to be carried out on specimens initially deposited onto a macroscopic pre-notched substrate. On loading, however, no substrate effects are introduced, allowing the films to be freely stretched. The results obtained from a variety of thin metal or polymeric films are very promising for the further development of this technique as a standard method for nanomaterial mechanical testing. © 2018 IOP Publishing Ltd.

Investigation of the relations between resin and advanced composite mechanical properties. Volume 2: Appendices

NASA Technical Reports Server (NTRS)

Zimmerman, R. S.; Adams, D. F.; Walrath, D. E.

1984-01-01

One untoughened epoxy baseline resin and three toughened epoxy resin systems were evaluated. The Hercules 3502, 2220-1, and 2220-3, and Ciba-Geigy Fibredux 914 resin systems were supplied in the uncured state by NASA-Langley and cast into thin flat specimens and round dogbone specimens. Tensile and torsional shear measurements were performed at three temperatures and two moisture conditions. Coefficients of thermal expansion and moisture expansion were also measured. Extensive scanning electron microscopic examination of fracture surfaces was performed to permit the correlation of observed failure modes with the environmental conditions under which the various specimens were tested. A micromechanics analysis was used to predict the unidirectional composite response under the various test conditions, incorporating the neat resin experimental results as the required input data. The mechanical and physical test results, the scanning electron microscope observations, and the analytical predictions were then correlated.

Investigation of the relations between neat resin and advanced composite mechanical properties. Volume 1: Results

NASA Technical Reports Server (NTRS)

Zimmerman, R. S.; Adams, D. F.; Walrath, D. E.

1984-01-01

A detailed evaluation of one untoughened epoxy baseline resin and three toughened epoxy resin systems was performed. The Hercules 3502, 2220-1, and 2220-3, and Ciba-Geigy Fibredux 914 resin systems were supplied in the uncured state by NASA-Langley and cast into thin flat specimens and round dogbone specimens. Tensile and torsional shear measurements were performed at three temperatures and two moisture conditions. Coefficients of thermal expansion and moisture expansion were also measured. Extensive scanning electron microscopic examination of fracture surfaces was performed, to permit the correlation of observed failure modes with the environmental conditions under which the various specimens were tested. A micromechanics analysis was used to predict the unidirectional composite response under the various test conditions, using the neat resin experimental results as the required input data. Mechanical and physical test results, the scanning electron microscope observations, and the analytical predictions were then correlated.

Effect of soot on oil properties and wear of engine components

NASA Astrophysics Data System (ADS)

Green, D. A.; Lewis, R.

2007-09-01

The objective of the work outlined in this paper was to increase the understanding of the wear mechanisms that occur within a soot contaminated contact zone, to help in future development of a predictive wear model to assist in the automotive engine valve train design process. The paper builds on previous work by the author, through testing of different lubricants and increased levels of soot contamination. Wear testing has been carried out using specimens operating under realistic engine conditions, using a reciprocating test-rig specifically designed for this application, where a steel disc is held in a heated bath of oil and a steel ball is attached to a reciprocating arm (replicating a sliding elephant's foot valve train contact). Detailed analysis of the test specimens has been performed using scanning electron microscopy to identify wear features relating to the proposed wear mechanisms. Analysis of worn engine components from durability engine tests has also been carried out for a comparison between specimen tests and engine testing. To assist the understanding of the wear test results obtained, the physical properties of contaminated lubricants were investigated, through viscosity, traction and friction measurements. The results have revealed how varying lubrication conditions change the wear rate of engine components and determine the wear mechanism that dominates in specific situations. Testing has also shown the positive effects of advanced engine lubricants to reduce the amount of wear produced with soot present.

The influence of micro-scale dimples and nano-sized grains on the fretting characteristics generated by laser pulses.

PubMed

Amanov, Auezhan; Watabe, Tsukasa; Sasaki, Shinya

2013-12-01

The tribological characteristics of micro-scale dimpled Cu-based alloy specimen generated using a laser surface texturing (LST) were assessed and compared with that of the untextured specimen. The objective of this study is to improve the tribological characteristics of internal combustion engine (ICE) bearings and bushings made of Cu-based alloy by generating micro-scale dimples using an LST. Fretting wear tests were performed by sliding a hardened SAE52100 steel ball against the untextured and LSTed specimens at a normal load of 5 N under oil-lubricated conditions. The friction force and relative movement between the specimens were measured simultaneously during the fretting tests. The test results showed that the LSTed specimens showed a reduction in friction coefficient and an enhancement in fretting wear resistance compared to that of the untextured specimen. The friction coefficient and fretting wear volume increased with increasing frequency for both untextured and LSTed specimens. The improved tribological properties of the LSTed specimen may be attributed to the micro-scale dimples, refined grain size and high lattice strain. In addition, a model for the nanocrystallization mechanism of the LSTed specimen was proposed.

Estimating Trabecular Bone Mechanical Properties From Non-Invasive Imaging

NASA Technical Reports Server (NTRS)

Hogan, Harry A.; Webster, Laurie

1997-01-01

An important component in developing countermeasures for maintaining musculoskeletal integrity during long-term space flight is an effective and meaningful method of monitoring skeletal condition. Magnetic resonance imaging (MRI) is an attractive non-invasive approach because it avoids the exposure to radiation associated with X-ray based imaging and also provides measures related to bone microstructure rather than just density. The purpose of the research for the 1996 Summer Faculty Fellowship period was to extend the usefulness of the MRI data to estimate the mechanical properties of trabecular bone. The main mechanical properties of interest are the elastic modulus and ultimate strength. Correlations are being investigated between these and fractal analysis parameters, MRI relaxation times, apparent densities, and bone mineral densities. Bone specimens from both human and equine donors have been studied initially to ensure high-quality MR images. Specimens were prepared and scanned from human proximal tibia bones as well as the equine distal radius. The quality of the images from the human bone appeared compromised due to freezing artifact, so only equine bone was included in subsequent procedures since these specimens could be acquired and imaged fresh before being frozen. MRI scans were made spanning a 3.6 cm length on each of 5 equine distal radius specimens. The images were then sent to Dr. Raj Acharya of the State University of New York at Buffalo for fractal analysis. Each piece was cut into 3 slabs approximately 1.2 cm thick and high-resolution contact radiographs were made to provide images for comparing fractal analysis with MR images. Dual energy X-ray absorptiometry (DEXA) scans were also made of each slab for subsequent bone mineral density determination. Slabs were cut into cubes for mechanical using a slow-speed diamond blade wafering saw (Buehler Isomet). The dimensions and wet weights of each cube specimen were measured and recorded. Wet weights were also recorded. Each specimen was labeled and marked to denote anatomic orientations, i.e. superior/inferior (S/I), media/lateral (M/L), and anterior/posterior (A/P). The actual locations of each cube cut were documented and images distributed to define ROI locations for other analyses (to Raj Acharya for fractal analysis, to Jon Richardson at Baylor College of Medicine for DEXA, and to Chen Lin at Baylor College of Medicine for T2* MRI analysis). Quasistatic mechanical testing consisted of compressive loading in all three mutually perpendicular anatomic directions. Cyclic loading was applied for 10 cycles to precondition the specimen and results calculated for the eleventh. For one of three directions tested on each specimen, the 10 cycles were followed with loading to failure. Testing is currently proceeding and once completed the results will be correlated with data from the other analyses. One of the main points of interest is the relationship between fractal dimension and mechanical properties. Throughout preparation and testing all specimens were maintained hydrated with physiological saline and stored frozen when not being used.

Methodology for Mechanical Property Testing on Fuel Cladding Using an Expanded Plug Wedge Test

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Jy-An John; Jiang, Hao

To determine the tensile properties of irradiated fuel cladding in a hot cell, a simple test was developed at ORNL and is described fully in US Patent Application 20060070455, Expanded plug method for developing circumferential mechanical properties of tubular materials. This method is designed for testing fuel rod cladding ductility in a hot cell utilizing an expandable plug to stretch a small ring of irradiated cladding material. The specimen strain is determined using the measured diametrical expansion of the ring. This method removes many complexities associated with specimen preparation and testing. The advantages are the simplicity of measuring the testmore » component assembly in the hot cell and the direct measurement of specimen strain. It was also found that cladding strength could be determined from the test results. The basic approach of this test method is to apply an axial compressive load to a cylindrical plug of polyurethane (or other materials) fitted inside a short ring of the test material to achieve radial expansion of the specimen. The diameter increase of the specimen is used to calculate the circumferential strain accrued during the test. The other two basic measurements are total applied load and amount of plug compression (extension). A simple procedure is used to convert the load circumferential strain data from the ring tests into material pseudo-stress-strain curves. However, several deficiencies exist in this expanded-plug loading ring test, which will impact accuracy of test results and introduce potential shear failure of the specimen due to inherited large axial compressive stress from the expansion plug test. First of all, the highly non-uniform stress and strain distribution resulted in the gage section of the clad. To ensure reliable testing and test repeatability, the potential for highly non-uniform stress distribution or displacement/strain deformation has to be eliminated at the gage section of the specimen. Second, significant compressive stresses were induced by clad bending deformation due to a clad bulging effect (or the barreling effect). The barreling effect caused very large localized shear stress in the clad and left testing material at a high risk of shear failure. The above combined effects will result in highly non-conservative predictions both in strength and ductility of the tested clad, and the associated mechanical properties as well. To overcome/mitigate the mentioned deficiencies associated with the current expansion plug test, systematic studies have been conducted. Through detailed parameter investigation on specific geometry designs, careful filtering of material for the expansion plug, as well as adding newly designed parts to the testing system, a method to reconcile the potential non-conservatism embedded in the expansion plug test system has been discovered. A modified expansion plug testing protocol has been developed based on the method. In order to closely resemble thin-wall theory, a general procedure was also developed to determine the hoop stress in the tested ring specimen. A scaling factor called -factor is defined to correlate the ring load P into hoop stress . , = . The generated stress-strain curve agrees very well with tensile test data in both the elastic and plastic regions.« less

Mechanical Properties of Aerogels

NASA Technical Reports Server (NTRS)

Parmenter, Kelly E.; Milstein, Frederick

1995-01-01

Aerogels are extremely low density solids that are characterized by a high porosity and pore sizes on the order of nanometers. Their low thermal conductivity and sometimes transparent appearance make them desirable for applications such as insulation in cryogenic vessels and between double paned glass in solar architecture. An understanding of the mechanical properties of aerogels is necessary before aerogels can be used in load bearing applications. In the present study, the mechanical behavior of various types of fiber-reinforced silica aerogels was investigated with hardness, compression, tension and shear tests. Particular attention was paid to the effects of processing parameters, testing conditions, storage environment, and age on the aerogels' mechanical response. The results indicate that the addition of fibers to the aerogel matrix generally resulted in softer, weaker materials with smaller elastic moduli. Furthermore, the testing environment significantly affected compression results. Tests in ethanol show an appreciable amount of scatter, and are not consistent with results for tests in air. In fact, the compression specimens appeared to crack and begin to dissolve upon exposure to the ethanol solution. This is consistent with the inherent hydrophobic nature of these aerogels. In addition, the aging process affected the aerogels' mechanical behavior by increasing their compressive strength and elastic moduli while decreasing their strain at fracture. However, desiccation of the specimens did not appreciably affect the mechanical properties, even though it reduced the aerogel density by removing trapped moisture. Finally, tension and shear test results indicate that the shear strength of the aerogels exceeds the tensile strength. This is consistent with the response of brittle materials. Future work should concentrate on mechanical testing at cryogenic temperatures, and should involve more extensive tensile tests. Moreover, before the mechanical response of reinforced aerogels can be fully understood, more tests of unreinforced aerogels are necessary. Unreinforced aerogels are of particular use because their birefringent nature allows for visual determination of stress fields during mechanical testing. The success of any future tests depends on the availability of a large supply of quality specimens with well-documented preparation and storage histories.

Characterization of irradiated AISI 316L stainless steel disks removed from the Spallation Neutron Source

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vevera, Bradley J; Hyres, James W; McClintock, David A

2014-01-01

Irradiated AISI 316L stainless steel disks were removed from the Spallation Neutron Source (SNS) for post-irradiation examination (PIE) to assess mechanical property changes due to radiation damage and erosion of the target vessel. Topics reviewed include high-resolution photography of the disk specimens, cleaning to remove mercury (Hg) residue and surface oxides, profile mapping of cavitation pits using high frequency ultrasonic testing (UT), high-resolution surface replication, and machining of test specimens using wire electrical discharge machining (EDM), tensile testing, Rockwell Superficial hardness testing, Vickers microhardness testing, scanning electron microscopy (SEM), and energy dispersive spectroscopy (EDS). The effectiveness of the cleaning proceduremore » was evident in the pre- and post-cleaning photography and permitted accurate placement of the test specimens on the disks. Due to the limited amount of material available and the unique geometry of the disks, machine fixturing and test specimen design were critical aspects of this work. Multiple designs were considered and refined during mock-up test runs on unirradiated disks. The techniques used to successfully machine and test the various specimens will be presented along with a summary of important findings from the laboratory examinations.« less

Enhanced mechanical properties of self-polymerized polydopamine-coated recycled PLA filament used in 3D printing

NASA Astrophysics Data System (ADS)

Zhao, Xing Guan; Hwang, Kyung-Jun; Lee, Dongoh; Kim, Taemin; Kim, Namsu

2018-05-01

Dopamine readily adsorbs onto almost all kinds of surfaces and develops cohesive strength through self-polymerization; hence, aqueous solutions of dopamine can be used as adhesives. These properties were used to prevent the degradation in the mechanical properties of recycled PLA fabricated by 3D printer. The mechanical properties of 3D printed PLA play a critical role in determining its applications. To reduce the manufacturing cost as well as environmental pollutants, recycling of 3D printed materials has attracted many attentions. However, recycling of polymeric materials causes the degradation of the mechanical properties. Our study is aimed at advancing the current knowledge on the adhesion behavior of polydopamine coatings on PLA pellets used in 3D printing process. Polydopamine was synthesized by oxidative polymerization and used to coat PLA specimens. The adhesion behavior and mechanical properties of the 3D printed specimens were evaluated by tensile tests. It was found that the mechanical properties of recycled specimen with polydopamine coating have been improved. Microstructural and chemical characterization of the coated specimens was carried out using FE-SEM, FTIR, and XPS analyses.

Computer-aided analysis for the Mechanics of Granular Materials (MGM) experiment, part 2

NASA Technical Reports Server (NTRS)

Parker, Joey K.

1987-01-01

Computer vision based analysis for the MGM experiment is continued and expanded into new areas. Volumetric strains of granular material triaxial test specimens have been measured from digitized images. A computer-assisted procedure is used to identify the edges of the specimen, and the edges are used in a 3-D model to estimate specimen volume. The results of this technique compare favorably to conventional measurements. A simplified model of the magnification caused by diffraction of light within the water of the test apparatus was also developed. This model yields good results when the distance between the camera and the test specimen is large compared to the specimen height. An algorithm for a more accurate 3-D magnification correction is also presented. The use of composite and RGB (red-green-blue) color cameras is discussed and potentially significant benefits from using an RGB camera are presented.

Mechanical Properties of Degraded PMR-15 Resin

NASA Technical Reports Server (NTRS)

Tsuji, Luis C.

2000-01-01

Thermo-oxidative aging produces a nonuniform degradation state in PMR-15 resin. A surface layer, usually attributed to oxidative degradation, forms. This surface layer has different properties from the inner material. A set of material tests was designed to separate the properties of the oxidized surface layer from the properties of interior material. Test specimens were aged at 316 C in either air or nitrogen, for durations of up to 800 hr. The thickness of the oxidized surface layer in air aged specimens, and the shrinkage and coefficient of thermal expansion (CTE) of nitrogen aged specimens were measured directly. The nitrogen-aged specimens were assumed to have the same properties as the interior material in the air-aged specimens. Four-point-bend tests were performed to determine modulus of both the oxidized surface layer and the interior material. Bimaterial strip specimens consisting of oxidized surface material and unoxidized interior material were constructed and used to determine surface layer shrinkage and CTE. Results confirm that the surface layer and core materials have substantially different properties.

Correlation of microstructure with dynamic deformation behavior and penetration performance of tungsten heavy alloys fabricated by mechanical alloying

NASA Astrophysics Data System (ADS)

Kim, Dong-Kuk; Lee, Sunghak; Ryu, Ho Jin; Hyunghong, Soon; Noh, Joon-Woong

2000-10-01

In this study, tungsten heavy alloy specimens were fabricated by mechanical alloying (MA), and their dynamic torsional properties and penetration performance were investigated. Dynamic torsional tests were conducted on the specimens fabricated with different sintering temperatures after MA, and then the test data were compared with those of a conventionally processed specimen. Refinement of tungsten particles was obtained after MA, but contiguity was seriously increased, thereby leading to low ductility and impact energy. Specimens in which both particle size and contiguity were simultaneously reduced by MA and two-step sintering and those having higher matrix fraction by partial MA were successfully fabricated. The dynamic test results indicated that the formation of adiabatic shear bands was expected because of the plastic localization at the central area of the gage section. Upon highspeed impact testing of these specimens, self-sharpening was promoted by the adiabatic shear band formation, but their penetration performance did not improve since much of kinetic energy of the penetrators was consumed for the microcrack formation due to interfacial debonding and cleavage fracture of tungsten particles. In order to improve penetration performance as well as to achieve selfsharpening by applying MA, conditions of MA and sintering process should be established so that alloy densification, particle refinement, and contiguity reduction can be simultaneously achieved.

Effect of Heat Exposure on the Fatigue Properties of AA7050 Friction Stir Welds

NASA Astrophysics Data System (ADS)

White, B. C.; Rodriguez, R. I.; Cisko, A.; Jordon, J. B.; Allison, P. G.; Rushing, T.; Garcia, L.

2018-05-01

This work examines the effect of heat exposure on the subsequent monotonic and fatigue properties of friction stir-welded AA7050. Mechanical characterization tests were conducted on friction stir-welded specimens as-welded (AW) and specimens heated to 315 °C in air for 20 min. Monotonic testing revealed high joint efficiencies of 98% (UTS) in the AW specimens and 60% in the heat-damaged (HD) specimens. Experimental results of strain-controlled fatigue testing revealed shorter fatigue lives for the HD coupons by nearly a factor of four, except for the highest strain amplitude tested. Postmortem fractography analysis found similar crack initiation or propagation behavior between the AW and HD specimens; however, the failure locations for the AW were predominantly in the heat-affected zone, while the HD specimens also failed in the stir zone. Microhardness measurements revealed a relatively uniform strength profile in the HD group, accounting for the variety of failure locations observed. The differences in both monotonic and cyclic properties observed between the AW and HD specimens support the conclusion that the heat damage (315 °C at 20 min) acts as an over-aging and a quasi-annealing treatment.

Clip gage attachment for frictionless measurement of displacement during high-temperature mechanical testing

DOEpatents

Alexander, David J.

1994-01-01

An attachment for placement between a test specimen and a remote clip gage extensometer providing improved fracture toughness tests of materials at elevated temperature. Using a cylindrical tube and axial rod in new relationship, the device transfers the displacement signal of the fracture toughness test specimen directly to a clip gage extensometer located outside the high temperature furnace. Virtually frictionless operation is assured by having the test specimen center one end of the rod in one end of the tube, while the clip gage extensometer arms center the other end of the rod in the other end of the tube. By providing positive control over both ends of both rod and tube, the attachment may be operated in orientations other than vertical.

A study of environmental characterization of conventional and advanced aluminum alloys for selection and design. Phase 2: The breaking load test method

NASA Technical Reports Server (NTRS)

Sprowls, D. O.; Bucci, R. J.; Ponchel, B. M.; Brazill, R. L.; Bretz, P. E.

1984-01-01

A technique is demonstrated for accelerated stress corrosion testing of high strength aluminum alloys. The method offers better precision and shorter exposure times than traditional pass fail procedures. The approach uses data from tension tests performed on replicate groups of smooth specimens after various lengths of exposure to static stress. The breaking strength measures degradation in the test specimen load carrying ability due to the environmental attack. Analysis of breaking load data by extreme value statistics enables the calculation of survival probabilities and a statistically defined threshold stress applicable to the specific test conditions. A fracture mechanics model is given which quantifies depth of attack in the stress corroded specimen by an effective flaw size calculated from the breaking stress and the material strength and fracture toughness properties. Comparisons are made with experimental results from three tempers of 7075 alloy plate tested by the breaking load method and by traditional tests of statistically loaded smooth tension bars and conventional precracked specimens.

Two-body wear rate of PEEK, CAD/CAM resin composite and PMMA: Effect of specimen geometries, antagonist materials and test set-up configuration.

PubMed

Wimmer, Timea; Huffmann, Anne Mildred Sophie; Eichberger, Marlis; Schmidlin, Patrick R; Stawarczyk, Bogna

2016-06-01

To test and compare the two-body wear rate of three CAD/CAM polymer materials and the influence of specimen geometry, antagonist material and test set-up configuration. Three CAD/CAM polymeric materials were assessed: a thermoplastic polyetheretherketone (PEEK), an experimental nanohybrid composite (COMP) and a PMMA-based material (PMMA). Crown-shaped and flat specimens were prepared from each material. The specimens underwent thermo-mechanical loading (50N, 5/55°C; 600,000 chewing cycles) opposed to human enamel and stainless steel antagonists. Half of the specimens of each group were loaded with a sliding movement of 0.7mm, the remaining half without. Thereby, 24 different test set-ups were investigated (n=12). Wear of the materials and antagonists was evaluated with a match-3D procedure. The topography of all surfaces was examined with scanning electron microscopy (SEM). Data were statistically evaluated with four-/one-way ANOVA followed by Scheffé post hoc test and unpaired t-test (p<0.05). All PEEK specimens showed significantly less material loss than COMP and PMMA specimens when loaded laterally. Within the axial loaded groups this was only true for the flat specimens tested with enamel antagonists. Crown specimens of these groups exhibited lower loss values than flat ones. Lateral force application led mostly to significantly higher material loss than the axial load application. On the antagonist side, no impact of CAD/CAM polymer material, antagonist material, force application and specimen geometry was found. Wear of PEEK was lower than that of the resin-based materials when lateral forces were applied, but showed comparable antagonist wear rates at the same time. Copyright © 2016 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Analysis of shear test method for composite laminates

NASA Technical Reports Server (NTRS)

Bergner, H. W., Jr.; Davis, J. G., Jr.; Herakovich, C. T.

1977-01-01

An elastic plane stress finite element analysis of the stress distributions in four flat test specimens for in-plane shear response of composite materials subjected to mechanical or thermal loads is presented. The shear test specimens investigated include: slotted coupon, cross beam, losipescu, and rail shear. Results are presented in the form of normalized shear contour plots for all three in-plane stess components. It is shown that the cross beam, losipescu, and rail shear specimens have stress distributions which are more than adequate for determining linear shear behavior of composite materials. Laminate properties, core effects, and fixture configurations are among the factors which were found to influence the stress distributions.

Impact damage resistance and residual property assessment of (0/+/-45/90)s SCS-6/Timetal 21S

NASA Technical Reports Server (NTRS)

Miller, Jennifer L.; Portanova, Marc A.; Johnson, W. Steven

1995-01-01

The impact damage resistance and residual mechanical properties of (0/ +/- 45/90)s SCS-6/Timetal 21S composites were evaluated. Both quasi-static indentation and drop-weight impact tests were used to investigate the impact behavior at two nominal energy levels (5.5 and 8.4 J) and determine the onset of internal damage. Through x-ray inspection, the extent of internal damage was characterized non-destructively. The composite strength and constant amplitude fatigue response were evaluated to assess the effects of the sustained damage. Scanning electron microscopy was used to characterize internal damage from impact in comparison to damage that occurs during mechanical loading alone. The effect of stacking sequence was examined by using specimens with the long dimension of the specimen both parallel (longitudinal) and perpendicular (transverse) to the 0 deg fiber direction. Damage in the form of longitudinal and transverse cracking occurred in all longitudinal specimens tested at energies greater than 6.3 J. Similar results occurred in the transverse specimens tested above 5.4 J. Initial load drop, characteristic of the onset of damage, occurred on average at 6.3 J in longitudinal specimens and at 5.0 J in transverse specimens. X-ray analysis showed broken fibers in the impacted region in specimens tested at the higher impact energies. At low impact energies, visible matrix cracking may occur, but broken fibers may not. Matrix cracking was noted along fiber swims and it appeared to depend on the surface quality of composite. At low impact energies, little damage has been incurred by the composite and the residual strength and residual life is not greatly reduced as compared to an undamaged composite. At higher impact energies, more damage occurred and a greater effect of the impact damage was observed.

Characterization of porous glass fiber-reinforced composite (FRC) implant structures: porosity and mechanical properties.

PubMed

Ylä-Soininmäki, Anne; Moritz, Niko; Lassila, Lippo V J; Peltola, Matti; Aro, Hannu T; Vallittu, Pekka K

2013-12-01

The aim of this study was to characterize the microstructure and mechanical properties of porous fiber-reinforced composites (FRC). Implants made of the FRC structures are intended for cranial applications. The FRC specimens were prepared by impregnating E-glass fiber sheet with non-resorbable bifunctional bis-phenyl glycidyl dimethacrylate and triethylene glycol dimethacrylate resin matrix. Four groups of porous FRC specimens were prepared with a different amount of resin matrix. Control group contained specimens of fibers, which were bound together with sizing only. Microstructure of the specimens was analyzed using a micro computed tomography (micro-CT) based method. Mechanical properties of the specimens were measured with a tensile test. The amount of resin matrix in the specimens had an effect on the microstructure. Total porosity was 59.5 % (median) in the group with the lowest resin content and 11.2 % (median) in the group with the highest resin content. In control group, total porosity was 94.2 % (median). Correlations with resin content were obtained for all micro-CT based parameters except TbPf. The tensile strength of the composites was 21.3 MPa (median) in the group with the highest resin content and 43.4 MPa (median) in the group with the highest resin content. The tensile strength in control group was 18.9 MPa (median). There were strong correlations between the tensile strength of the specimens and most of the micro-CT based parameters. This experiment suggests that porous FRC structures may have the potential for use in implants for cranial bone reconstructions, provided further relevant in vitro and in vivo tests are performed.

The correlation of low-velocity impact resistance of graphite-fiber-reinforced composites with matrix properties

NASA Technical Reports Server (NTRS)

Bowles, K. J.

1986-01-01

Summarized are basic studies that were conducted to correlate the impact resistance of graphite-fiber-reinforced composites with polymer matrix properties. Three crosslinked epoxy resins and a linear polysulfone were selected as composite matrices. As a group, these resins possess a significantly large range of mechanical properties. The mechanical properties of the resins and their respective composites were measured. Neat resin specimens and unidirectional and crossply composite specimens were impact tested with an instrumented dropweight tester. Impact resistances of the specimens were assessed on the basis of loading capability, energy absorption, and extent of damage.

The Effects of Shielded Metal Arc Welding (Smaw) Welding On The Mechanical Characteristics With Heating Treatment inn S45c Steel

NASA Astrophysics Data System (ADS)

Munawar; Abbas, Hammada; Yusran Aminy, Ahmad

2018-02-01

Steel material has been used mainly for making tooling, automotive components, other household needs, power generators to frame buildings and bridges. This study aimed (1) to analyze the mechanical Characteristics of S45C steel with and without heating treatments, and (2) to analyze the temperature of heating treatment which could result in the maximal strength of S45C steel after the welding process. The research was conducted in the laboratory of mechanical engineering study program, Departement of mechanical Engineering, Christian university of indonesia paulus, makassar. The method used materials, instruments, and the dimensions determination of specimen based on the proposed testing standard, Next, was to determine the mechanical caracteristics of the S45C steel wich had been welded and heated.The tensile specimens, the hardness specimen, the impact specimen, and microstructures of which,each of the 3 specimens was the specimens was the specimen without treatment, the spesimen with the welding wthout heating and the specimen of 150°C, 250° C, 300° C. The research results indicated that the treatment process of 150°C, 250°C and 300°C produced the changes of mechanic charateristics with the tensile strength of 42 kgf/mm2 when the temperature had reached 300°C, but at the temperature 300°C, the its toughness would decrease to Hi = 0.836 j/m2 and its hardness would increase to 40.83 at the temperature of 300°C. The value of the maximum strengs was reached at the heating temperature of 300°C for the tensile strength and the hardness, while at the temperature of 300°C its impact value would decrease.

Comparisons of nanoindentation, 3-point bending, and tension tests for orthodontic wires.

PubMed

Iijima, Masahiro; Muguruma, Takeshi; Brantley, William A; Mizoguchi, Itaru

2011-07-01

The purposes of this study were to obtain information about mechanical properties with the nanoindentation test for representative wire alloys and compare the results with conventional mechanical tests. Archwires having 0.016 × 0.022-in cross sections were obtained of 1 stainless steel, 1 cobalt-chromium-nickel, 1 beta-titanium alloy, and 2 nickel-titanium products. Specimens of as-received wires were subjected to nanoindentation testing along the external surfaces and over polished cross sections to obtain values of hardness and elastic modulus. Other specimens of as-received wires were subjected to Vickers hardness, 3-point bending, and tension tests. All testing was performed at 25°C. Differences were found in hardness and elastic modulus obtained with the nanoindentation test at the external and cross-sectioned surfaces and with the conventional mechanical-property tests. Mechanical properties obtained with the nanoindentation test generally varied with indentation depth. The 3 testing methods did not yield identical values of hardness and elastic modulus, although the order among the 5 wire products was the same. Variations in results for the nanoindentation and conventional mechanical property tests can be attributed to the different material volumes sampled, different work-hardening levels, and an oxide layer on the wire surface. Copyright © 2011 American Association of Orthodontists. Published by Mosby, Inc. All rights reserved.

A Tensile Specimen of Tailor Rolled Blanks with Equal Probability in Yield and Its Mechanical Behavior Analysis

PubMed Central

Zhang, Sijia; Liu, Xianghua; Liu, Lizhong

2018-01-01

In this paper, the microstructure and mechanical properties that distribute regulation along the rolling direction of tailor rolled blanks (TRB) were investigated. A tensile specimen with equal probability in yield (EYS) was first designed considering variation both in thickness and in material strength. The uniaxial tension test was carried out with a digital image correlation method to analyze the mechanical behaviors. The results showed that the strain distribution of EYS was homogeneous. From the results, it can be known that a new design philosophy for a TRB tensile specimen is reasonable and EYS is suitable to characterize the mechanical behavior of TRB. The true stress-strain curves of metal in different cross sections of TRB were calculated. On the basis of the true stress-strain curves, a material model of TRB was constructed and then implemented into finite element simulations of TRB uniaxial tensile tests. The strain distribution of numerical and experimental results was similar and the error between the elongation of the specimen after fracture obtained by experiment and FE ranged from 9.51% to 13.06%. Therefore, the simulation results match well with the experimental results and the material model has high accuracy and as well as practicability. PMID:29710772

Rolling Contact Fatigue Failure Mechanisms of Plasma-Nitrided Ductile Cast Iron

NASA Astrophysics Data System (ADS)

Wollmann, D.; Soares, G. P. P. P.; Grabarski, M. I.; Weigert, N. B.; Escobar, J. A.; Pintaude, G.; Neves, J. C. K.

2017-05-01

Rolling contact fatigue (RCF) of a nitrided ductile cast iron was investigated. Flat washers machined from a pearlitic ductile cast iron bar were quenched and tempered to maximum hardness, ground, polished and divided into four groups: (1) specimens tested as quenched and tempered; (2) specimens plasma-nitrided for 8 h at 400 °C; (3) specimens plasma-nitrided and submitted to a diffusion process for 16 h at 400 °C; and (4) specimens submitted to a second tempering for 24 h at 400 °C. Hardness profiles, phase analyses and residual stress measurements by x-ray diffraction, surface roughness and scanning electron microscopy were applied to characterize the surfaces at each step of this work. Ball-on-flat washer tests were conducted with a maximum contact pressure of 3.6 GPa, under flood lubrication with a SAE 90 API GL-5 oil at 50 °C. Test ending criterion was the occurrence of a spalling. Weibull analysis was used to characterize RCF's lifetime data. Plasma-nitrided specimens exhibited a shorter RCF lifetime than those just quenched and tempered. The effects of nitriding on the mechanical properties and microstructure of the ductile cast iron are discussed in order to explain the shorter endurance of nitrided samples.

Experimental validation of a new heterogeneous mechanical test design

NASA Astrophysics Data System (ADS)

Aquino, J.; Campos, A. Andrade; Souto, N.; Thuillier, S.

2018-05-01

Standard material parameters identification strategies generally use an extensive number of classical tests for collecting the required experimental data. However, a great effort has been made recently by the scientific and industrial communities to support this experimental database on heterogeneous tests. These tests can provide richer information on the material behavior allowing the identification of a more complete set of material parameters. This is a result of the recent development of full-field measurements techniques, like digital image correlation (DIC), that can capture the heterogeneous deformation fields on the specimen surface during the test. Recently, new specimen geometries were designed to enhance the richness of the strain field and capture supplementary strain states. The butterfly specimen is an example of these new geometries, designed through a numerical optimization procedure where an indicator capable of evaluating the heterogeneity and the richness of strain information. However, no experimental validation was yet performed. The aim of this work is to experimentally validate the heterogeneous butterfly mechanical test in the parameter identification framework. For this aim, DIC technique and a Finite Element Model Up-date inverse strategy are used together for the parameter identification of a DC04 steel, as well as the calculation of the indicator. The experimental tests are carried out in a universal testing machine with the ARAMIS measuring system to provide the strain states on the specimen surface. The identification strategy is accomplished with the data obtained from the experimental tests and the results are compared to a reference numerical solution.

Step-stress analysis for predicting dental ceramic reliability

PubMed Central

Borba, Márcia; Cesar, Paulo F.; Griggs, Jason A.; Bona, Álvaro Della

2013-01-01

Objective To test the hypothesis that step-stress analysis is effective to predict the reliability of an alumina-based dental ceramic (VITA In-Ceram AL blocks) subjected to a mechanical aging test. Methods Bar-shaped ceramic specimens were fabricated, polished to 1µm finish and divided into 3 groups (n=10): (1) step-stress accelerating test; (2) flexural strength- control; (3) flexural strength- mechanical aging. Specimens from group 1 were tested in an electromagnetic actuator (MTS Evolution) using a three-point flexure fixture (frequency: 2Hz; R=0.1) in 37°C water bath. Each specimen was subjected to an individual stress profile, and the number of cycles to failure was recorded. A cumulative damage model with an inverse power law lifetime-stress relation and Weibull lifetime distribution were used to fit the fatigue data. The data were used to predict the stress level and number of cycles for mechanical aging (group 3). Groups 2 and 3 were tested for three-point flexural strength (σ) in a universal testing machine with 1.0 s in 37°C water. Data were statistically analyzed using Mann-Whitney Rank Sum test. Results Step-stress data analysis showed that the profile most likely to weaken the specimens without causing fracture during aging (95% CI: 0–14% failures) was: 80 MPa stress amplitude and 105 cycles. The median σ values (MPa) for groups 2 (493±54) and 3 (423±103) were statistically different (p=0.009). Significance The aging profile determined by step-stress analysis was effective to reduce alumina ceramic strength as predicted by the reliability estimate, confirming the study hypothesis. PMID:23827018

Step-stress analysis for predicting dental ceramic reliability.

PubMed

Borba, Márcia; Cesar, Paulo F; Griggs, Jason A; Della Bona, Alvaro

2013-08-01

To test the hypothesis that step-stress analysis is effective to predict the reliability of an alumina-based dental ceramic (VITA In-Ceram AL blocks) subjected to a mechanical aging test. Bar-shaped ceramic specimens were fabricated, polished to 1μm finish and divided into 3 groups (n=10): (1) step-stress accelerating test; (2) flexural strength-control; (3) flexural strength-mechanical aging. Specimens from group 1 were tested in an electromagnetic actuator (MTS Evolution) using a three-point flexure fixture (frequency: 2Hz; R=0.1) in 37°C water bath. Each specimen was subjected to an individual stress profile, and the number of cycles to failure was recorded. A cumulative damage model with an inverse power law lifetime-stress relation and Weibull lifetime distribution were used to fit the fatigue data. The data were used to predict the stress level and number of cycles for mechanical aging (group 3). Groups 2 and 3 were tested for three-point flexural strength (σ) in a universal testing machine with 1.0MPa/s stress rate, in 37°C water. Data were statistically analyzed using Mann-Whitney Rank Sum test. Step-stress data analysis showed that the profile most likely to weaken the specimens without causing fracture during aging (95% CI: 0-14% failures) was: 80MPa stress amplitude and 10(5) cycles. The median σ values (MPa) for groups 2 (493±54) and 3 (423±103) were statistically different (p=0.009). The aging profile determined by step-stress analysis was effective to reduce alumina ceramic strength as predicted by the reliability estimate, confirming the study hypothesis. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Speckle-interferometric measurement system of 3D deformation to obtain thickness changes of thin specimen under tensile loads

NASA Astrophysics Data System (ADS)

Kowarsch, Robert; Zhang, Jiajun; Sguazzo, Carmen; Hartmann, Stefan; Rembe, Christian

2017-06-01

The analysis of materials and geometries in tensile tests and the extraction of mechanic parameters is an important field in solid mechanics. Especially the measurement of thickness changes is important to obtain accurate strain information of specimens under tensile loads. Current optical measurement methods comprising 3D digital image correlation enable thickness-change measurement only with nm-resolution. We present a phase-shifting electronic speckle-pattern interferometer in combination with speckle-correlation technique to measure the 3D deformation. The phase-shift for the interferometer is introduced by fast wavelength tuning of a visible diode laser by injection current. In a post-processing step, both measurements can be combined to reconstruct the 3D deformation. In this contribution, results of a 3Ddeformation measurement for a polymer membrane are presented. These measurements show sufficient resolution for the detection of 3D deformations of thin specimen in tensile test. In future work we address the thickness changes of thin specimen under tensile loads.

The influence of build parameters on the microstructure during electron beam melting of Titanium6Aluminum4Vanadium

NASA Astrophysics Data System (ADS)

Puebla, Karina

With the demand of devices to replace or improve areas, such as: electronic, biomedical and aerospace industries. Improvements in these areas of engineering have been in need due to the customer's needs for product properties requirements. The design of components must exhibit better material properties (mechanical or biocompatible) close to those of any given product. Rapid prototyping (RP) technologies that were originally designed to build prototypes may now be required to build functional end-use products. To carry out the transition, from RP to rapid manufacturing (RM), the available materials utilized in RP must provide the performance required for RM. The specific technology being used should be capable of producing reliable parts in regards to their mechanical properties. The research presented in this work investigated the effects of building parameters (build orientation and melt scan rate) on microstructure and the mechanical properties of test specimens fabricated via Electron Beam Melting (EBM) using Ti6Al4V. EBM, a rapid prototyping technology, has the potential to manufacture complex 3-dimensional end-use products layer-by-layer. In this work, a design of experiments approach was performed to determine the effects of build orientation and melt scan rate on both the microstructure and mechanical properties of test samples fabricated using EBM. Two randomized setups were designed to build two batches of 18 specimens. The experimental designs were carried out to determine the effect of different build parameters (build orientation and melt scan rate) in the mechanical properties of the fabricated specimens. The results demonstrated that EBM manufactured specimens built with different melt scan rates and build orientations have different microstructures and mechanical properties. Different melt scans produced variations in particle sintering resulting in dissimilar porosities and in mechanical properties (hardness and tensile testing). The mechanical properties decreased as the porosity increased for tensile testing and Rockwell C-scale (HR C), while Vickers hardness (HV) measurements increased and are related to the microstructure. The different build orientations of the specimens produced different mechanical properties since the orientation of the fabricated specimens impact the local heat transfer flow. This influenced the microstructure where the specimens oriented horizontally cooled more rapidly than those built vertically. Statistically significant differences in mechanical properties were found as an effect of melt scan rate. The statistical analyses that were done can help identify and classify fabrication parameters on mechanical properties for EBM-fabricated products. Optical images demonstrated the presence of alpha and beta phases, and alpha'-martensite with slight differences in microstructure. Dislocation substructures were observed in acicular alpha-plates from TEM images and alpha, beta, and alpha'-phase features. Mechanical and thermal treatment on Ti6Al4V can generate different microstructures promoting Ti6Al4V as an evolutionary alloy. Tailored mechanical properties of complex 3-dimensional end-use products can be achieved by modifying the building parameters of the EBM system. The EBM system can facilitate the process of manufacturing components by varying build parameters in order to obtain desirable physical and mechanical properties. Once the desired properties for Ti6Al4V are established, the fabrication process will lead to more successful end-use products.

Influence of gaseous hydrogen on the mechanical properties of high temperature alloys

NASA Technical Reports Server (NTRS)

1976-01-01

Tensile tests of six nickel-base and one cobalt-base alloy were conducted in 34.5 MN/sq m helium and hydrogen environments at temperatures from 297 K to 1,088 K. Mechanical properties tests of the nickel-base alloy MAR M-246 (Hf modified), in two cast conditions, were conducted in gaseous environments at temperatures from 297 K to 1,144 K and pressures from one atmosphere to 34.5 MN/sq m. The objective of this program was to obtain the mechanical properties of the various alloys proposed for use in space propulsion systems in a pure hydrogen environment at different temperatures and to compare with the mechanical properties in helium at the same conditions. All testing was conducted on solid specimens exposed to external gaseous pressure. Smooth and notched tensile properties were determined using ASTM tensile testing techniques, and creep-rupture life was determined using ASTM creep-rupture techniques. Low-cycle fatigue life was established by constant total strain and constant stress testing using smooth specimens and a closed-loop test machine.

Tensile testing apparatus

NASA Technical Reports Server (NTRS)

Blackburn, L. B.; Ellingsworth, J. R. (Inventor)

1985-01-01

An improved mechanical extensometer is described for use with a constant load creep test machine. The dead weight of the extensometer is counterbalanced by two pairs of weights connected through a pulley system and to rod extension and leading into the furnace where the test sample is undergoing elevated temperature (above 500 F.) tensile testing. Novel gripper surfaces, conical tip and flat surface are provided in each sampling engaging platens to reduce the grip pressure normally required for attachment of the extensometer to the specimen and reduce initial specimen bending normally associated with foil-gage metal testing.

Impact compressive and bending behaviour of rocks accompanied by electromagnetic phenomena.

PubMed

Kobayashi, Hidetoshi; Horikawa, Keitaro; Ogawa, Kinya; Watanabe, Keiko

2014-08-28

It is well known that electromagnetic phenomena are often observed preceding earthquakes. However, the mechanism by which these electromagnetic waves are generated during the fracture and deformation of rocks has not been fully identified. Therefore, in order to examine the relationship between the electromagnetic phenomena and the mechanical properties of rocks, uniaxial compression and three-point bending tests for two kinds of rocks with different quartz content, granite and gabbro, have been carried out at quasi-static and dynamic rates. Especially, in the bending tests, pre-cracked specimens of granite were also tested. Using a split Hopkinson pressure bar and a ferrite-core antenna in close proximity to the specimens, both the stress-strain (load-displacement) curve and simultaneous electromagnetic wave magnitude were measured. It was found that the dynamic compressive and bending strengths and the stress increase slope of both rocks were higher than those observed in static tests; therefore, there is a strain-rate dependence in their strength and stress increase rate. It was found from the tests using the pre-cracked bending specimens that the intensity of electromagnetic waves measured during crack extension increased almost proportionally to the increase of the maximum stress intensity factor of specimens. This tendency was observed in both the dynamic and quasi-static three-point bending tests for granite. © 2014 The Author(s) Published by the Royal Society. All rights reserved.

Load-bearing capacity of screw-retained CAD/CAM-produced titanium implant frameworks (I-Bridge®2) before and after cyclic mechanical loading.

PubMed

Dittmer, Marc Philipp; Nensa, Moritz; Stiesch, Meike; Kohorst, Philipp

2013-01-01

Implant-supported screw-retained fixed dental prostheses (FDPs) produced by CAD/ CAM have been introduced in recent years for the rehabilitation of partial or total endentulous jaws. However, there is a lack of data about the long-term mechanical characteristics. The aim of this study was to investigate the failure mode and the influence of extended cyclic mechanical loading on the load-bearing capacity of these frameworks. Ten five-unit FDP frameworks simulating a free-end situation in the mandibular jaw were manufactured according to the I-Bridge®2-concept (I-Bridge®2, Biomain AB, Helsingborg, Sweden) and each was screw-retained on three differently angulated Astra Tech implants (30º buccal angulation/0º angulation/30º lingual angulation). One half of the specimens was tested for static load-bearing capacity without any further treatment (control), whereas the other half underwent five million cycles of mechanical loading with 100 N as the upper load limit (test). All specimens were loaded until failure in a universal testing machine with an occlusal force applied at the pontics. Load-displacement curves were recorded and the failure mode was macro- and microscopically analyzed. The statistical analysis was performed using a t-test (p=0.05). All the specimens survived cyclic mechanical loading and no obvious failure could be observed. Due to the cyclic mechanical loading, the load-bearing capacity decreased from 8,496 N±196 N (control) to 7,592 N±901 N (test). The cyclic mechanical loading did not significantly influence the load-bearing capacity (p=0.060). The failure mode was almost identical in all specimens: large deformations of the framework at the implant connection area were obvious. The load-bearing capacity of the I-Bridge®2 frameworks is much higher than the clinically relevant occlusal forces, even with considerably angulated implants. However, the performance under functional loading in vivo depends on additional aspects. Further studies are needed to address these aspects.

Load-bearing capacity of screw-retained CAD/CAM-produced titanium implant frameworks (I-Bridge®2) before and after cyclic mechanical loading

PubMed Central

DITTMER, Marc Philipp; NENSA, Moritz; STIESCH, Meike; KOHORST, Philipp

2013-01-01

Implant-supported screw-retained fixed dental prostheses (FDPs) produced by CAD/ CAM have been introduced in recent years for the rehabilitation of partial or total endentulous jaws. However, there is a lack of data about the long-term mechanical characteristics. Objective The aim of this study was to investigate the failure mode and the influence of extended cyclic mechanical loading on the load-bearing capacity of these frameworks. Material and Methods Ten five-unit FDP frameworks simulating a free-end situation in the mandibular jaw were manufactured according to the I-Bridge®2-concept (I-Bridge®2, Biomain AB, Helsingborg, Sweden) and each was screw-retained on three differently angulated Astra Tech implants (30º buccal angulation/0º angulation/30º lingual angulation). One half of the specimens was tested for static load-bearing capacity without any further treatment (control), whereas the other half underwent five million cycles of mechanical loading with 100 N as the upper load limit (test). All specimens were loaded until failure in a universal testing machine with an occlusal force applied at the pontics. Load-displacement curves were recorded and the failure mode was macro- and microscopically analyzed. The statistical analysis was performed using a t-test (p=0.05). Results All the specimens survived cyclic mechanical loading and no obvious failure could be observed. Due to the cyclic mechanical loading, the load-bearing capacity decreased from 8,496 N±196 N (control) to 7,592 N±901 N (test). The cyclic mechanical loading did not significantly influence the load-bearing capacity (p=0.060). The failure mode was almost identical in all specimens: large deformations of the framework at the implant connection area were obvious. Conclusion The load-bearing capacity of the I-Bridge®2 frameworks is much higher than the clinically relevant occlusal forces, even with considerably angulated implants. However, the performance under functional loading in vivo depends on additional aspects. Further studies are needed to address these aspects. PMID:24037068

Performance of V-4Cr-4Ti material exposed to DIII-D tokamak environment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tsai, H.; Chung, H.M.; Smith, D.L.

1997-04-01

Test specimens made with the 832665 heat of V-4Cr-4Ti alloy were exposed in the DIII-D tokamak environment to support the installation of components made of a V-4Cr-4Ti alloy in the radiative divertor of the DIII-D. Some of the tests were conducted with the Divertor Materials Evaluation System (DiMES) to study the short-term effects of postvent bakeout, when concentrations of gaseous impurities in the DIII-D chamber are the highest. Other specimens were mounted next to the chamber wall behind the divertor baffle plate, to study the effects of longer-term exposures. By design, none of the specimens directly interacted with the plasma.more » Preliminary results from testing the exposed specimens indicate only minor degradation of mechanical properties. Additional testing and microstructural characterization are in progress.« less

A study of the effects of long-term exposure to fuels and fluids on the behavior of advanced composite materials

NASA Technical Reports Server (NTRS)

Tanimoto, E. Y.

1981-01-01

The periodic testing and evaluation of graphite/epoxy and Kevlar/epoxy material systems after subjecting test specimens to prolonged exposure to several laboratory-controlled environments deemed typical of normal aircraft operations is discussed. It is noted that specimen immersion in water or water-based fluids resulted in the greatest effect on the mechanical properties tested. Also, the environmental fluids showed a tendency to affect Kevlar/epoxy systems at an earlier exposure period than the graphite/epoxy systems. Results also indicate mechanical property strength retention generally being lower for the Kevlar/epoxy systems when compared to the corresponding graphite/epoxy systems in similar environments, after prolonged exposure.

Mechanical characterization and structural analysis of recycled fiber-reinforced-polymer resin-transfer-molded beams

NASA Astrophysics Data System (ADS)

Tan, Eugene Wie Loon

1999-09-01

The present investigation was focussed on the mechanical characterization and structural analysis of resin-transfer-molded beams containing recycled fiber-reinforced polymers. The beams were structurally reinforced with continuous unidirectional glass fibers. The reinforcing filler materials consisted entirely of recycled fiber-reinforced polymer wastes (trim and overspray). The principal resin was a 100-percent dicyclo-pentadiene unsaturated polyester specially formulated with very low viscosity for resin transfer molding. Variations of the resin transfer molding technique were employed to produce specimens for material characterization. The basic materials that constituted the structural beams, continuous-glass-fiber-reinforced, recycled-trim-filled and recycled-overspray-filled unsaturated polyesters, were fully characterized in axial and transverse compression and tension, and inplane and interlaminar shear, to ascertain their strengths, ultimate strains, elastic moduli and Poisson's ratios. Experimentally determined mechanical properties of the recycled-trim-filled and recycled-overspray-filled materials from the present investigation were superior to those of unsaturated polyester polymer concretes and Portland cement concretes. Mechanical testing and finite element analyses of flexure (1 x 1 x 20 in) and beam (2 x 4 x 40 in) specimens were conducted. These structurally-reinforced specimens were tested and analyzed in four-point, third-point flexure to determine their ultimate loads, maximum fiber stresses and mid-span deflections. The experimentally determined load capacities of these specimens were compared to those of equivalent steel-reinforced Portland cement concrete beams computed using reinforced concrete theory. Mechanics of materials beam theory was utilized to predict the ultimate loads and mid-span deflections of the flexure and beam specimens. However, these predictions proved to be severely inadequate. Finite element (fracture propagation) analyses of the flexure and beam specimens were also performed. These progressive failure analyses more closely approximated flexural behavior under actual testing conditions by reducing the elastic moduli of elements that were considered to have partially or totally failed. Individual element failures were predicted using the maximum stress, Tsai-Hill and Tsai-Wu failure criteria. Excellent predictions of flexural behavior were attributed to the progressive failure analyses combined with an appropriate failure criterion, and the reliable input material properties that were generated.

Mechanical properties of neat polymer matrix materials and their unidirectional carbon fiber-reinforced composites

NASA Technical Reports Server (NTRS)

Zimmerman, Richard S.; Adams, Donald F.

1988-01-01

The mechanical properties of two neat resin systems for use in carbon fiber epoxy composites were characterized. This included tensile and shear stiffness and strengths, coefficients of thermal and moisture expansion, and fracture toughness. Tests were conducted on specimens in the dry and moisture-saturated states, at temperatures of 23, 82 and 121 C. The neat resins tested were American Cyanamid 1806 and Union Carbide ERX-4901B(MPDA). Results were compared to previously tested neat resins. Four unidirectional carbon fiber reinforced composites were mechanically characterized. Axial and transverse tension and in-plane shear strengths and stiffness were measured, as well as transverse coefficients of thermal and moisture expansion. Tests were conducted on dry specimens only at 23 and 100 C. The materials tested were AS4/3502, AS6/5245-C, T300/BP907, and C6000/1806 unidirectional composites. Scanning electron microscopic examination of fracture surfaces was performed to permit the correlation of observed failure modes with the environmental test conditions.

Fatigue Behavior of Porous Ti-6Al-4V Made by Laser-Engineered Net Shaping

PubMed Central

Bordonaro, Giancarlo G.; Berto, Filippo

2018-01-01

The fatigue behavior and fracture mechanisms of additively manufactured Ti-6Al-4V specimens are investigated in this study. Three sets of testing samples were fabricated for the assessment of fatigue life. The first batch of samples was built by using Laser-Engineered Net Shaping (LENS) technology, a Direct Energy Deposition (DED) method. Internal voids and defects were induced in a second batch of samples by changing LENS machine processing parameters. Fatigue performance of these samples is compared to the wrought Ti-6Al-4V samples. The effects of machine-induced porosity are assessed on mechanical properties and results are presented in the form of SN curves for the three sets of samples. Fracture mechanisms are examined by using Scanning Electron Microscopy (SEM) to characterize the morphological characteristics of the failure surface. Different fracture surface morphologies are observed for porous and non-porous specimens due to the combination of head write speed and laser power. Formation of defects such as pores, unmelted regions, and gas entrapments affect the failure mechanisms in porous specimens. Non-porous specimens exhibit fatigue properties comparable with that of the wrought specimens, but porous specimens are found to show a tremendous reduced fatigue strength. PMID:29439510

Debonding characteristics of adhesively bonded woven Kevlar composites

NASA Technical Reports Server (NTRS)

Mall, S.; Johnson, W. S.

1988-01-01

The fatigue damage mechanism of an adhesively bonded joint between fabric reinforced composite adherends was investigated with cracked-lap-shear specimens. Two bonded systems were studied: fabric Kevlar 49/5208 epoxy adherends bonded together with either EC 3445 or FM-300 adhesive. For each bonded system, two specimen geometries were tested. In all specimens tested, fatigue damage occurred in the form of cyclic debonding; however, the woven Kevlar specimens gave significantly slower debond growth rates and higher fracture toughness than previously found in the nonwoven adherend specimens. The surfaces for the woven adherends were not smooth; rather, they had regular crests (high spots) and troughs (low spots) due to the weave pattern. Radiographs of the specimens and examination of their failure surfaces revealed that fiber bridging occurred between the crests of the two adherends in the debonded region. The observed improvements in debond growth resistance and static fracture toughness are attributed to this bridging.

Examining Mechanical Strength Characteristics of Selective Inhibition Sintered HDPE Specimens Using RSM and Desirability Approach

NASA Astrophysics Data System (ADS)

Rajamani, D.; Esakki, Balasubramanian

2017-09-01

Selective inhibition sintering (SIS) is a powder based additive manufacturing (AM) technique to produce functional parts with an inexpensive system compared with other AM processes. Mechanical properties of SIS fabricated parts are of high dependence on various process parameters importantly layer thickness, heat energy, heater feedrate, and printer feedrate. In this paper, examining the influence of these process parameters on evaluating mechanical properties such as tensile and flexural strength using Response Surface Methodology (RSM) is carried out. The test specimens are fabricated using high density polyethylene (HDPE) and mathematical models are developed to correlate the control factors to the respective experimental design response. Further, optimal SIS process parameters are determined using desirability approach to enhance the mechanical properties of HDPE specimens. Optimization studies reveal that, combination of high heat energy, low layer thickness, medium heater feedrate and printer feedrate yielded superior mechanical strength characteristics.

Clip gage attachment for frictionless measurement of displacement during high-temperature mechanical testing

DOEpatents

Alexander, D.J.

1994-01-04

An attachment for placement between a test specimen and a remote clip gage extensometer providing improved fracture toughness tests of materials at elevated temperature is described. Using a cylindrical tube and axial rod in new relationship, the device transfers the displacement signal of the fracture toughness test specimen directly to a clip gage extensometer located outside the high temperature furnace. Virtually frictionless operation is assured by having the test specimen center one end of the rod in one end of the tube, while the clip gage extensometer arms center the other end of the rod in the other end of the tube. By providing positive control over both ends of both rod and tube, the attachment may be operated in orientations other than vertical. 1 figure.

Influences of strain rate on yield strength aluminum alloys

NASA Astrophysics Data System (ADS)

Rizal, Samsul; Firdaus, Hamdani Teuku; Thaib, Razali; Homma, Hiroomi

2005-04-01

The simulation of aircraft has often been performing by implementing finite element code on supercomputers. The reliability an accuracy of simulation depends mainly on the material model as well as on structural model used in calculations. Consequently, an accurate knowledge of mechanical behavior of materials under impact loading is essential for safety performance evaluation of structure. Impact tension tests on specimens for aircrafts and automotive structural applications are conduct by means of the split Hopkinson bar apparatus. Small specimens having diameter 4 mm are use in the test. Tensile stress-strain relations at strain rates of 102 s-1 to over 103 s-1 are present and compared with those obtained at quasi-static strain rates. The limitations on the applicability of apparatus are also discusses. The other importance of the reference of strain, while studying void growth in elastic-viscoplastic material, is emphasized. In the present paper, a simplified plane-symmetrical two-dimensional finite element model for a SHPB with a plate specimen made of an elastic material is first established. The used of strain gage mounted at the specimens to be monitored strain during the course of impact test. Comparisons may then be made between the numerical predicted and experimentally observed of load and a specimen strain. This report also describes the apparatus and instrumentation, and also be discusses the advantages and limitations of experimental technique. Fractograph is taken by scanning electron microscope on the center of the specimens for judgment of the fracture mechanism and strain rates influences on the materials.

Characterization of plastic deformation in a disk bend test

NASA Astrophysics Data System (ADS)

Byun, T. S.; Lee, E. H.; Hunn, J. D.; Farrell, K.; Mansur, L. K.

2001-04-01

A disk bend test technique has been developed to study deformation mechanisms as well as mechanical properties. In the disk bend test, a transmission electron microscopy (TEM) disk size specimen of 3 mm diameter ×0.25 mm thick is clamped around its rim in a circular holder and indented with a tungsten carbide ball of 1 mm diameter on its back face. AISI 316LN austenitic stainless steel and 9Cr-2WVTa ferritic/martensitic steel were selected as test materials. A model was developed to determine the average plastic strain and surface plastic strain in the disk bend test. The deformation regimes of the plastic strain versus deflection curves corresponded to those of the load versus deflection curves. The stress state of the disk bend deformation was analyzed for the two test materials and compared with those of other mechanical tests such as uniaxial tensile, compact tension, and ball indentation tests. Slip line features at the deformed surface and the corresponding TEM microstructures were examined for both tensile and disk bend specimens. Differences and similarities in deformation between the disk bend and the tensile tests are described.

Investigation of interfacial fracture behavior on injection molded parts

NASA Astrophysics Data System (ADS)

Fischer, Matthieu; Ausias, Gilles; Kuehnert, Ines

2016-03-01

In this study the interfacial morphology of different polymers joined by various assembly injection molding (AIM) technologies were discussed. Melt streams were injected successively using tools with core-back or rotation techniques. To compare bulk specimen strength and weld line strength, the fracture behavior of different specimen scales and thin sections were investigated. An in-situ SEM tensile test and a new thin section testing device which is used in polarized (transmitted) light microscopy were used to observe specimen failure. The effects of processing on spherulitic structures were linked to bonding strength and mechanical properties.

High Temperature Mechanical Testing of a Cylindrical Weave Carbon-Carbon Composite.

DTIC Science & Technology

1985-07-01

umentation. 11. Photograph of the Calcination Furnace 46 and Automatic Controller/"Recorder. 12. Shear-Lao Specimen for both Axial 47 and Radial Fiber...Pull-out.S 13. Photograph of Displacement Frame Used to 48 Load Both the Pull-out Specimens and Axial Rupture Specimens. 14. Graph i te Loadi ng B1...tested in creep at 1800 C the spec imen shoted no el onga t i on w i th an ao a: I stre=ss of 11.4 ksi for 20 min. This was not surp r is i rg si nce Lu an

Double Cantilever Beam and End Notched Flexure Fracture Toughness Testing of Two Composite Materials

NASA Technical Reports Server (NTRS)

Kessler, Jeff A.; Adams, Donald F.

1993-01-01

Two different unidirectional composite materials were provided by NASA Langley Research Center and tested by the Composite Materials Research Group within the Department of Mechanical Engineering at the University of Wyoming. Double cantilever beam and end notched flexure tests were performed to measure the mode I (crack opening) and mode II (sliding or shear) interlaminar fracture toughness of the two materials. The two composites consisted of IM7 carbon fiber combined with either RP46 resin toughened with special formulation of LaRC IA resin, known as JJS1356; or PES chain extended thermoplastic resin known as JJS1361. Double Cantilever Beam Specimen Configuration and Test Methods As received from NASA, the test specimens were nominally 0.5 inch wide, 6 inches long, and 0.2 inch thick. A 1 inch long Kapton insert at the midplane of one end of the specimen (placed during laminate fabrication) facilitated crack initiation and extension. It was noted that the specimens provided were smaller than the nominal 1.5 inch wide, 9.0 inch long configuration specified. Similarly, the Kapton inserts were of greater length than those in the present specimens. Hence, the data below should not be compared directly to those generated with the referenced methods. No preconditioning was performed on the specimens prior to testing. In general, the methodology was used for the present work. Crack opening loads were introduced to the specimens via piano hinges attached to the main specimen faces at a single end of each specimen. Hinges were bolted to the specimens using the technique presented. The cracks were extended a small distance from the end of the Kapton insert prior to testing. Just before precracking, the sides of the specimens were coated with water-soluble typewriter correction fluid to aid in crack visualization. Scribe marks were then made in the coating at half-inch intervals.

Confocal arthroscopy-based patient-specific constitutive models of cartilaginous tissues - II: prediction of reaction force history of meniscal cartilage specimens.

PubMed

Taylor, Zeike A; Kirk, Thomas B; Miller, Karol

2007-10-01

The theoretical framework developed in a companion paper (Part I) is used to derive estimates of mechanical response of two meniscal cartilage specimens. The previously developed framework consisted of a constitutive model capable of incorporating confocal image-derived tissue microstructural data. In the present paper (Part II) fibre and matrix constitutive parameters are first estimated from mechanical testing of a batch of specimens similar to, but independent from those under consideration. Image analysis techniques which allow estimation of tissue microstructural parameters form confocal images are presented. The constitutive model and image-derived structural parameters are then used to predict the reaction force history of the two meniscal specimens subjected to partially confined compression. The predictions are made on the basis of the specimens' individual structural condition as assessed by confocal microscopy and involve no tuning of material parameters. Although the model does not reproduce all features of the experimental curves, as an unfitted estimate of mechanical response the prediction is quite accurate. In light of the obtained results it is judged that more general non-invasive estimation of tissue mechanical properties is possible using the developed framework.

Preliminary report on tests of tensile specimens with a part-through surface notch for a filament wound graphite/epoxy material

NASA Technical Reports Server (NTRS)

Harris, C. E.; Morris, D. H.

1985-01-01

The behavior of tensile coupons with surface notches of various semi-elliptical shapes were evaluated for specimens obtained from a filament wound graphite/epoxy cylinder. The quasi-static test results, in some instances, are inadequate for defining complete trend curves and the interpretive analysis is considered to be preliminary. Specimens with very shallow notches were observed to be notch insensitive and the unnotched strength from these specimens was determined to be 54.97 Ksi. The failure strain of the laminate was found to be 1.328%. Specimens with deeper notches were sensitive to notch depth, notch aspect ratio, and specimen width. Using the unnotched strength of 54.97 Ksi and Poe's general toughness parameter, the fracture toughness was estimated to be 27.2 Ksi square root of In. Isotropic linear elastic fracture mechanics together with the estimated fracture toughness correctly predicted the influence of notch depth, aspect ratio, and specimen finitewidth.

Fatigue Behavior of Crystalline-Reinforced Glass-Ceramics.

PubMed

Vicari, Carolina Barbosa; Magalhães, Bárbara de Oliveira; Griggs, Jason Alan; Borba, Márcia

2018-01-03

To evaluate the fatigue behavior of two crystalline-reinforced ceramics: leucite-reinforced (VL) and lithium disilicate-based (VD) glass-ceramics. Bar-shaped specimens (16 × 4 × 1.2 mm) were produced for each ceramic using prefabricated CAD/CAM blocks. For each group, 30 specimens were subjected to a three-point flexural strength test in a universal testing machine. For VL and VD, 36 and 41 specimens were subjected to a cyclic fatigue test, respectively. The cyclic fatigue test was performed with a pneumatic mechanical cycling machine (1 Hz; 37°C distilled water). Specimens were tested at two stress levels for each preset lifetime (10 3 and 10 4 cycles for VL; 10 4 and 10 5 cycles for VD) following the boundary technique. Fractography was performed with a scanning electron microscope. Data were analyzed with Weibull analysis. There were significant differences among groups for characteristic strength (σ 0 ) and Weibull modulus (m), as the confidence intervals did not overlap. The VD group presented the highest values of σ 0 , but the lowest Weibull modulus. Both groups showed a reduction of approximately 60% of the initial flexural strength (σ f ) after cycling for 10 4 cycles. For VD tested in fatigue, there was no degradation of σ f when the number of cycles was increased from 10 4 to 10 5 . The VL group showed an 18% decrease in σ f when the number of cycles increased from 10 3 to 10 4 . Flexural strength values estimated for a 5% probability of failure were 36 MPa for VL and 55 MPa for VD, after 10 4 cycles. Both glass-ceramics showed similar strength degradation (60%) after a lifetime of 10 4 cycles, despite their distinct mechanical properties. Mechanical cycling in humid conditions proved to be an important factor for the degradation of the mechanical properties of crystalline-reinforced glass-ceramics. © 2018 by the American College of Prosthodontists.

Comparison of microstructure and mechanical properties of ultra-narrow gap laser and gas-metal-arc welded S960 high strength steel

NASA Astrophysics Data System (ADS)

Guo, Wei; Li, Lin; Dong, Shiyun; Crowther, Dave; Thompson, Alan

2017-04-01

The microstructural characteristics and mechanical properties, including micro-hardness, tensile properties, three-point bending properties and Charpy impact toughness at different test temperatures of 8 mm thick S960 high strength steel plates were investigated following their joining by multi-pass ultra-narrow gap laser welding (NGLW) and gas metal arc welding (GMAW) techniques. It was found that the microstructure in the fusion zone (FZ) for the ultra-NGLW joint was predominantly martensite mixed with some tempered martensite, while the FZ for the GMAW joint was mainly consisted of ferrite with some martensite. The strength of the ultra-NGLW specimens was comparable to that of the base material (BM), with all welded specimens failed in the BM in the tensile tests. The tensile strength of the GMAW specimens was reduced approximately by 100 MPa when compared with the base material by a broad and soft heat affected zone (HAZ) with failure located in the soft HAZ. Both the ultra-NGLW and GMAW specimens performed well in three-point bending tests. The GMAW joints exhibited better impact toughness than the ultra-NGLW joints.

The influence of flame hardening process to aluminum 7075 series on the mechanical strength and micro structure

NASA Astrophysics Data System (ADS)

Koin, Sudibtia Titio; Triyono, Teguh; Surojo, Eko

2018-02-01

The 7075 series alloys are heat treatable wrought aluminum alloys based on the Al-Zn-Mg(-Cu) system. They are widely used in high-performance structural aerospace and transportation applications. Apart from compositional, casting and thermo-mechanical processing effects, the balance of properties is also significantly influenced by the way in which the materials are heat-treated. This paper describes the effect of flame hardening process to aluminum 7075 series on the increasing hardness, tensile strength, and evolution of microstructure. A test specimen had made by machining process and flame heating. Temperature of solution heat treatment is varied on 350 °C, 400 °C, 450 °C and 500 °C. After that process a test specimen would be quenched at nitrate-nitrite liquid during 45 minutes and artificial aging at 120°C until two days. The testing specimen consist of hardness and tensile strength according to ASTM. The result showed that specimen had precipitation on microstructure lead to an increase in aluminum properties. On the temperature 450°C solution heat treatment, the aluminum properties reached the highest value, namely, hardness of 129 HVN and tensile strength 570 MPa.

Magnesium alloys as body implants: fracture mechanism under dynamic and static loadings in a physiological environment.

PubMed

Choudhary, Lokesh; Raman, R K Singh

2012-02-01

It is essential that a metallic implant material possesses adequate resistance to cracking/fracture under the synergistic action of a corrosive physiological environment and mechanical loading (i.e. stress corrosion cracking (SCC)), before the implant can be put to actual use. This paper presents a critique of the fundamental issues with an assessment of SCC of a rapidly corroding material such as magnesium alloys, and describes an investigation into the mechanism of SCC of a magnesium alloy in a physiological environment. The SCC susceptibility of the alloy in a simulated human body fluid was established by slow strain rate tensile (SSRT) testing using smooth specimens under different electrochemical conditions for understanding the mechanism of SCC. However, to assess the life of the implant devices that often possess fine micro-cracks, SCC susceptibility of notched specimens was investigated by circumferential notch tensile (CNT) testing. CNT tests also produced important design data, i.e. threshold stress intensity for SCC (KISCC) and SCC crack growth rate. Fractographic features of SCC were examined using scanning electron microscopy. The SSRT and CNT results, together with fractographic evidence, confirmed the SCC susceptibility of both smooth and notched specimens of a magnesium alloy in the physiological environment. Copyright © 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Mechanical Properties of Calcium Fluoride-Based Composite Materials

PubMed Central

Kleczewska, Joanna; Pryliński, Mariusz; Podlewska, Magdalena; Sokołowski, Jerzy; Łapińska, Barbara

2016-01-01

Aim of the study was to evaluate mechanical properties of light-curing composite materials modified with the addition of calcium fluoride. The study used one experimental light-curing composite material (ECM) and one commercially available flowable light-curing composite material (FA) that were modified with 0.5–5.0 wt% anhydrous calcium fluoride. Morphology of the samples and uniformity of CaF2 distribution were analyzed using Scanning Electron Microscopy (SEM) and Energy Dispersive Spectroscopy (EDS). Mechanical properties were tested after 24-hour storage of specimens in dry or wet conditions. Stored dry ECM enriched with 0.5–1.0 wt% CaF2 showed higher tensile strength values, while water storage of all modified ECM specimens decreased their tensile strength. The highest Vickers hardness tested after dry storage was observed for 2.5 wt% CaF2 content in ECM. The addition of 2.0–5.0 wt% CaF2 to FA caused significant decrease in tensile strength after dry storage and overall tensile strength decrease of modified FA specimens after water storage. The content of 2.0 wt% CaF2 in FA resulted in the highest Vickers hardness tested after wet storage. Commercially available composite material (FA), unmodified with fluoride addition, demonstrated overall significantly higher mechanical properties. PMID:28004001

Aspects of fracture mechanics in cryogenic model design. Part 2: NTF materials

NASA Technical Reports Server (NTRS)

Newman, J. C., Jr.; Lisagor, W. B.

1983-01-01

Results of fatigue crack growth and fracture toughness tests conducted on three candidate materials are presented. Fatigue crack growth and fracture toughness tests were conducted on NITRONIC 40 at room temperature and -275 F. Fracture toughness tests were also conducted on Vascomax 200 and 250 maraging steel from room temperature to -320 F. NITRONIC 40 was used to make the Pathfinder 1 model. The fatigue crack growth rate tests were conducted at room temperature and -275 F on three-point notch bend specimens. The fracture toughness tests on the as received and stress relieved materials at -275 F were conducted on the center crack tension specimens. Toughness tests were also conducted on Vascomax CVM-200 and CVM-250 maraging steel from room temperature to -320 F using round and rectangular compact specimens.

Verification and application of the Iosipescu shear test method

NASA Technical Reports Server (NTRS)

Walrath, D. E.; Adams, D. F.

1984-01-01

Finite element models were used to study the effects of notch angle variations on the stress state within an Iosipescu shear test speciment. These analytical results were also studied to determine the feasibility of using strain gage rosettes and a modified extensometer to measure shear strains in this test specimen. Analytical results indicate that notch angle variations produced only small differences in simulated shear properties. Both strain gage rosettes and the modified extensometer were shown to be feasible shear strain transducers for the test method. The Iosipoescu shear test fixture was redesigned to incorporate several improvements. These improvements include accommodation of a 50 percent larger specimen for easier measurement of shear train, a clamping mechanism to relax strict tolerances on specimen width, and a self contained alignment tool for use during specimen installation. A set of in-plane and interlaminar shear properties were measured for three graphite fabric/epoxy composites of T300/934 composite material. The three weave patterns were Oxford, 5-harness satin, and 8-harness satin.

Combined meso-scale modeling and experimental investigation of the effect of mechanical damage on the transport properties of cementitious composites

NASA Astrophysics Data System (ADS)

Raghavan, Balaji; Niknezhad, Davood; Bernard, Fabrice; Kamali-Bernard, Siham

2016-09-01

The transport properties of cementitious composites such as concrete are important indicators of their durability, and are known to be heavily influenced by mechanical loading. In the current work, we use meso-scale hygro-mechanical modeling with a morphological 3D two phase mortar-aggregate model, in conjunction with experimentally obtained properties, to investigate the coupling between mechanical loading and damage and the permeability of the composite. The increase in permeability of a cylindrical test specimen at 28% aggregate fraction during a uniaxial displacement-controlled compression test at 85% of the peak load was measured using a gas permeameter. The mortar's mechanical behavior is assumed to follow the well-known compression damaged plasticity (CDP) model with isotropic damage, at varying thresholds, and obtained from different envelope curves. The damaged intrinsic permeability of the mortar evolves according to a logarithmic matching law with progressive loading. We fit the matching law parameters to the experimental result for the test specimen by inverse identification using our meso-scale model. We then subject a series of virtual composite specimens to quasi-static uniaxial compressive loading with varying boundary conditions to obtain the simulated damage and strain evolutions, and use the damage data and the previously identified parameters to determine the evolution of the macroscopic permeability tensor for the specimens, using a network model. We conduct a full parameter study by varying aggregate volume fraction, granulometric distribution, loading/boundary conditions and "matching law" parameters, as well as for different strain-damage thresholds and uniaxial loading envelope curves. Based on this study, we propose Avrami equation-based upper and lower bounds for the evolution of the damaged permeability of the composite.

On the dynamic behavior of mineralized tissues

NASA Astrophysics Data System (ADS)

Kulin, Robb Michael

Mineralized tissues, such as bone and antler, are complex hierarchical materials that have adapted over millennia to optimize strength and fracture resistance for their in vivo applications. As a structural support, skeletal bone primarily acts as a rigid framework that is resistant to fracture, and able to repair damage and adapt to sustained loads during its lifetime. Antler is typically deciduous and subjected to large bending moments and violent impacts during its annual cycle. To date, extensive characterization of the quasi-static mechanical properties of these materials has been performed. However, very little has been done to characterize their dynamic properties, despite the fact that the majority of failures in these materials occur under impact loads. Here, an in depth analysis of the dynamic mechanical behavior of these two materials is presented, using equine bone obtained post-mortem from donors ranging in age from 6 months to 28 years, and antler from the North American Elk. Specimens were tested under compressive strain rates of 10-3, 100, and 103 sec-1 in order to investigate their strain rate dependent compressive response. Fracture toughness experiments were performed using a four-point bending geometry on single and double-notch specimens in order to measure fracture toughness, as well as observe differences in crack propagation between dynamic (˜2x105 MPa˙m1/2/s) and quasi-static (˜0.25 MPa˙m1/2/s) loading rates. After testing, specimens were analyzed using a combination of optical, electron and confocal microscopy. Results indicated that the mechanical response of these materials is highly dependent on loading rate. Decreasing quasi-static fracture toughness is observed with age in bone specimens, while dynamic specimens show no age trends, yet universally decreased fracture toughness compared to those tested quasi-statically. For the first time, rising R-curve behavior in bone was also shown to exist under both quasi-static and dynamic loading. Antler demonstrated itself to be extremely resistant to impact loading, often requiring multiple impacts to fracture a specimen. Microscopy observations of deformation and crack propagation mechanisms indicate that differences in mechanical behavior between bone and antler, and at varying strain rates, are the result of subtle differences in bulk composition and active microstructural toughening mechanisms.

Tensile testing method for rare earth based bulk superconductors at liquid nitrogen temperature

NASA Astrophysics Data System (ADS)

Kasaba, K.; Katagiri, K.; Murakami, A.; Sato, G.; Sato, T.; Murakami, M.; Sakai, N.; Teshima, H.; Sawamura, M.

2005-10-01

Bending tests have been commonly carried out to investigate the mechanical properties of melt-processed rare earth based bulk superconductors. Tensile tests by using small specimen, however, are preferable to evaluate the detailed distribution of the mechanical properties and the intrinsic elastic modulus because no stress distributions exist in the cross-section. In this study, the tensile test method at low temperature by using specimens with the dimensions of 3 × 3 × 4 mm from Y123 and Gd123 bulks was examined. They were glued to Al alloy rods at 400 K by using epoxy resin. Tests were carried out at liquid nitrogen temperature (LNT) by using the immersion type jig. Although the bending strength in the direction perpendicular to the c-axis of the bulks at LNT is higher than that at room temperature (RT), the tensile strength at LNT was lower than that at RT. Many of specimens fractured near the interface between the specimen and the Al alloy rod at LNT. According to the finite element method analysis, it was shown that there was a peak thermal stress in the loading direction near the interface and it was significantly higher at LNT than that at RT. It was also shown that the replacement of the Al alloy rod to Ti rod of which the coefficient of thermal expansion is close to that of bulks significantly increased the tensile strength.

Experimental Observations for Determining the Maximum Torque Values to Apply to Composite Components Mechanically Joined With Fasteners (MSFC Center Director's Discretionary Fund Final Report, Proj. 03-13}

NASA Technical Reports Server (NTRS)

Thomas, F. P.

2006-01-01

Aerospace structures utilize innovative, lightweight composite materials for exploration activities. These structural components, due to various reasons including size limitations, manufacturing facilities, contractual obligations, or particular design requirements, will have to be joined. The common methodologies for joining composite components are the adhesively bonded and mechanically fastened joints and, in certain instances, both methods are simultaneously incorporated into the design. Guidelines and recommendations exist for engineers to develop design criteria and analyze and test composites. However, there are no guidelines or recommendations based on analysis or test data to specify a torque or torque range to apply to metallic mechanical fasteners used to join composite components. Utilizing the torque tension machine at NASA s Marshall Space Flight Center, an initial series of tests were conducted to determine the maximum torque that could be applied to a composite specimen. Acoustic emissions were used to nondestructively assess the specimens during the tests and thermographic imaging after the tests.

Comparison of mechanical characteristics of focused ion beam fabricated silicon nanowires

NASA Astrophysics Data System (ADS)

Ina, Ginnosuke; Fujii, Tatsuya; Kozeki, Takahiro; Miura, Eri; Inoue, Shozo; Namazu, Takahiro

2017-06-01

In this study, we investigate the effects of focused ion beam (FIB)-induced damage and specimen size on the mechanical properties of Si nanowires (NWs) by a microelectromechanical system (MEMS)-based tensile testing technique. By an FIB fabrication technique, three types of Si NWs, which are as-FIB-fabricated, annealed, and FIB-implanted NWs, are prepared. A sacrificial-oxidized NW is also prepared to compare the mechanical properties of these FIB-based NWs. The quasi-static uniaxial tensile tests of all the NWs are conducted by scanning electron microscopy (SEM). The fabrication process and specimen size dependences on Young’s modulus and fracture strength are observed. Annealing is effective for improving the Young’s modulus of the FIB-damaged Si. Transmission electron microscopy (TEM) suggests that the mechanism behind the process dependence on the mechanical characteristics is related to the crystallinity of the FIB-damaged portion.

Mechanical Behaviour of Bolted Joints Under Impact Rates of Loading

DTIC Science & Technology

2012-01-01

Joints in Glass Fibre / Epoxy Laminates. Composites, Volume 16. No 2. Kolsky, H. (1949). An Investigation of the Mechanical Properties of Materials at...and equations 2.1 and 2, Figures 2.3, 2.4, and 2.5 were constructed to determine optimal specimen properties for later testing of bolted joints of...9.5 l/d=11.5 UNCLASSIFIED UNCLASSIFIED 2.5 Discussion Ideal specimen properties are high total equilibrium times, low equilibrium start times and

Stress Wave Attenuation in Aluminum Alloy and Mild Steel Specimens Under SHPB Tensile Testing

NASA Astrophysics Data System (ADS)

Pothnis, J. R.; Ravikumar, G.; Arya, H.; Yerramalli, Chandra S.; Naik, N. K.

2018-02-01

Investigations on the effect of intensity of incident pressure wave applied through the striker bar on the specimen force histories and stress wave attenuation during split Hopkinson pressure bar (SHPB) tensile testing are presented. Details of the tensile SHPB along with Lagrangian x- t diagram of the setup are included. Studies were carried out on aluminum alloy 7075 T651 and IS 2062 mild steel. While testing specimens using the tensile SHPB setup, it was observed that the force calculated from the transmitter bar strain gauge was smaller than the force obtained from the incident bar strain gauge. This mismatch between the forces in the incident bar and the transmitter bar is explained on the basis of stress wave attenuation in the specimens. A methodology to obtain force histories using the strain gauges on the specimen during SHPB tensile testing is also presented. Further, scanning electron microscope images and photomicrographs are given. Correlation between the microstructure and mechanical properties is explained. Further, uncertainty analysis was conducted to ascertain the accuracy of the results.

Evaluation of suitable porosity for sintered porous {beta}-tricalcium phosphate as a bone substitute

DOE Office of Scientific and Technical Information (OSTI.GOV)

Park, Jin-Hong; Bae, Ji-Yong; Shim, Jaebum

2012-09-15

Structural and mechanical characterization is performed for sintered porous beta tricalcium phosphate ({beta}-TCP) to determine the appropriate porosity for use as a bone substitute. Four different types of porous {beta}-TCP specimen with different porosities are fabricated through a sintering process. For structural characterization, scanning electron microscopy and a Microfocus X-ray computed tomography system are used to investigate the pore openings on the specimen's surface, pore size, pore distribution, and pore interconnections. Compression tests of the specimens are performed, and mechanical properties such as the elastic modulus and compressive strength are obtained. Also, the geometric shape and volume of the {beta}-TCPmore » around the contact region of two pores, which need to be initially resolved after implantation in order to increase the size of the pore openings, are evaluated through simple calculations. The results show that porous {beta}-TCP with 42.1% porosity may be a suitable bone substitute candidate in terms of sustaining external loads, and inducing and cultivating bone cells. - Highlights: Black-Right-Pointing-Pointer Structural and mechanical characterization was performed for sintered porous {beta}-TCP specimens. Black-Right-Pointing-Pointer For structural characterization, SEM and Microfocus X-ray CT system were used. Black-Right-Pointing-Pointer For mechanical characterization, compression tests were performed. Black-Right-Pointing-Pointer Porous {beta}-TCP with 42.1% porosity may be a suitable bone substitute.« less

Modeling of fracture and durability of paste-bonded composite joints subjected to hygro-thermal-mechanical loading

NASA Astrophysics Data System (ADS)

Harris, David Lee

The objective of the research is to characterize the behavior of composite/composite joints with paste adhesive using both experimental testing and analytical modeling. In comparison with the conventional tape adhesive, joining composites using paste adhesive provides several advantages. The carbon fiber laminate material systems employed in this study included IM7 carbon fibers and 977-3 epoxy matrix assembled in prepreg tape, and AS4 carbon fibers and 977-3 epoxy matrix as a five-harness satin weave. The adhesive employed was EA 9394 epoxy. All laminates and test specimens were fabricated and inspected by Boeing using their standard propriety procedures. Three types of test specimens were used in the program. They were bonded double-lap shear (DLS), bonded double cantilever beam (DCB) and bonded interlaminar tension (ILT) specimens. A group of specimens were conditioned at elevated temperature and humidity in an environmental chamber at Boeing's facility and their moisture absorption recorded with time. Specimens were tested at room temperature dry and elevated temperatures. DCB and DLS specimens were tested in fatigue as well as static conditions. Two-dimensional finite element models of the three configurations were developed for determining stresses and strains using the ABAQUS finite element package code. Due to symmetry, only the one-half of the specimen needed to be considered thus reducing computational time. The effect of the test fixture is not taken into account instead equivalent distributed stresses are applied directly on the composite laminates. For each of the specimen, the distribution of Mises stress and the first strain invariant J1 are obtained to identify potential failure locations within a specimen.

Effect of Specimen Thickness on the Creep Response of a Single Crystal Superalloy (Preprint)

DTIC Science & Technology

2012-01-01

0.38mm. 3.1.2. Fractography Figure 5: SEM images of the sheet specimen of thickness 3.18mm creep tested at 760◦C/758MPa, (a) Specimen reconstructed after...with dotted rectangle in (b). To further explore the mechanism behind thickness debit effect, we performed stan- dard fractography using secondary...thickness 3.18mm ruptured after 210hours. 3.2.3. Fractography The SEM image of the reconstructed creep ruptured specimen of thickness 3.18mm is shown in

Elevated-Temperature Tensile-Testing of Foil-Gage Metals

NASA Technical Reports Server (NTRS)

Blackburn, L. B.; Ellingsworth, J. R.

1986-01-01

Automated system for measuring strain in metal foils at temperatures above 500 degrees F (260 degrees C) uses mechanical extensometer and displacement transducer. System includes counterbalance feature, which eliminates weight contribution of extensometer and reduces grip pressure required for attachment to specimen. Counterbalancing feature overcomes two major difficulties in using extensometers with foil-gage specimens: (1) Weight of extensometer and transducer represents significant fraction of total load applied to specimen and may actually damage it; and (2) grip pressure required for attachment of extensometer to specimens may induce bending stresses in foil-gage materials.

Relationship of mechanical characteristics and microstructural features to the time-dependent edge notch sensitivity of inconel 718 sheet

NASA Technical Reports Server (NTRS)

Wilson, D. J.

1971-01-01

Time-dependent notch sensitivity of Inconel 718 sheet was observed at 900 F to 1200 F (482 - 649 C). It occurred when edge-notched specimens were loaded below the yield strength and smooth specimen tests showed that small amounts of creep consumed large rupture life fractions. The severity of the notch sensitivity was reduced by decreasing the solution temperature, increasing the time and/or temperature of aging and increasing the test temperature to 1400 F (760 C). Elimination of time-dependent notch sensitivity correlated with a change in dislocation motion mechanism from shearing to by-passing precipitate particles.

Results of PBX 9501 and PBX 9502 Round-Robin Quasi-Static Tension Tests from JOWOG-9/39 Focused Exchange.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Thompson, D. G.

2002-01-01

A round-robin study was conducted with the participation of three laboratory facilities: Los Alamos National Laboratory (LANL), BWXT Pantex Plant (PX), and Lawrence Livermore National Laboratory (LLNL). The study involved the machining and quasi-static tension testing of two plastic-bonded high explosive (PBX) composites, PBX 9501 and PBX 9502. Nine tensile specimens for each type of PBX were to be machined at each of the three facilities; 3 of these specimens were to be sent to each of the participating materials testing facilities for tensile testing. The resultant data was analyzed to look for trends associated with specimen machining location and/ormore » trends associated with materials testing location. The analysis provides interesting insights into the variability and statistical nature of mechanical properties testing on PBX composites. Caution is warranted when results are compared/exchanged between testing facilities.« less

Effect of chemical disinfectant on the transverse strength of heat-polymerized acrylic resins subjected to mechanical and chemical polishing: an in vitro study.

PubMed

Sharan, Smitha; Kavitha, H R; Konde, Harish; Kalahasti, Deepthi

2012-05-01

To evaluate the effect of chemical disinfectant on the transverse strength of heat-polymerized acrylic resins subjected to mechanical and chemical polishing. A total of 256 rectangular specimens (65 * 10 * 3 mm) 128 per resin (Lucitone-199 and Acralyn-H) were fabricated. One side of each specimen was not polished and the other was either mechanically (n = 96) or chemically (n = 96) polished and immersed for 10, 30 and 60 minutes in 2% alkaline glutaraldehyde. Mechanically polished (n = 32) and chemically polished (n = 32) control specimens were immersed only in distilled water. The transverse strength (N/mm(2)) was tested for failure in a universal testing machine, at a crosshead speed of 5 mm/min. Data were statistically analyzed using 2-way ANOVA and Student t-test. chemical polishing resulted in significantly lower transverse strength values than mechanical polishing. Lucitone- 199 resin demonstrated the highest overall transverse strength for the materials tested. Heat-polymerized acrylic resins either mechanically or chemically polished, did not demonstrate significant changes in transverse strength during immersion in the disinfecting solution tested, regardless of time of immersion. Lucitone-199 resin demonstrated the highest overall transverse strength for the materials tested and significantly stronger than Acralyn-H with either type of polishing following immersion in 2% alkaline glutaraldehyde. There is a concern that immersion in chemical solutions often used for cleansing and disinfection of prostheses may undermine the strength and structure of denture base resins. In this study it was observed that, the transverse strength of samples of Lucitone-199 was higher than that of the samples of Acralyn-H. The chances of fracture of the denture made of Lucitone-199 are less than that of dentures made of Acralyn-H. The chemically polished dentures may be more prone to fracture than mechanically polished dentures.

Effect of opacifiers and UV absorbers on pigmented maxillofacial silicone elastomer, part 2: mechanical properties after artificial aging.

PubMed

Nguyen, Caroline Tram; Chambers, Mark S; Powers, John M; Kiat-Amnuay, Sudarat

2013-06-01

There are reports of dissatisfaction with color instability and reduced lifetime of extraoral maxillofacial prostheses. Previous studies showed that UV mineral-based light-protecting agent (LP) improved color stability of MDX4-4210/Type A silicone elastomer. However, effects of this agent and opacifiers on mechanical properties of the elastomer are unknown. The purpose of this study was to evaluate the effect of 2 commonly used opacifiers and LP, a new opacifier, when combined with pigments on the mechanical properties of MDX4-4210/Type A silicone elastomer before and after artificial aging. Two commonly used opacifiers, titanium white dry pigment (TW) and silicone intrinsic white (SW) and LP were each combined with MDX4-4210/type A. Artists' oil pigment was then combined with the LP and TW groups, and silicone intrinsic pigments were combined with the SW group with 5 colors (no pigment=control, red, yellow, blue, or a combination of the 3 pigments). Ten dumbbell-shaped and 10 trouser-shaped specimens of each opacifier + pigment mixture, plus a control group with no opacifier and no pigment, were made for a total of 320 specimens. Half of the specimens (n=5) were aged in a chamber at 450 kJ/m(2). Specimens were tested for hardness (ASTM D2240), tensile strength (ASTM D412), tear strength (ASTM D624), and percentage elongation in a universal testing machine. A 3-way ANOVA and the Fisher PLSD test were performed (α=.05) for each mechanical property. After accelerated aging, values of Shore A hardness were the lowest for LP with all 5 pigments and the control, followed by SW and TW (P<.001). After accelerated aging, tear strength, tensile strength, and elongation decreased significantly (P<.001) for LP, whereas changes for SW and TW varied depending on the pigment. The mechanical properties of specimens with the light-protecting opacifier were adversely affected after being subjected to artificial aging. SW and TW preserved the mechanical properties of silicone in this study. Copyright © 2013 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Fluoride release, recharge and mechanical property stability of various fluoride-containing resin composites.

PubMed

Naoum, S; Ellakwa, A; Martin, F; Swain, M

2011-01-01

To determine the fluoride release and recharge of three fluoride-containing resin composites when aged in deionized water (pH 6.5) and lactic acid (pH 4.0) and to assess mechanical properties of these composites following aging. Three fluoride-containing resin composites were analyzed in this study; a new giomer material named Beautifil II, Gradia Direct X, and Tetric EvoCeram. A glass ionomer cement, Fuji IX Extra, was also analyzed for comparison. Specimens were fabricated for two test groups: group 1 included 10 disc specimens initially aged 43 days in deionized water (five specimens) and lactic acid (five specimens). The fluoride release from these specimens was measured using a fluoride-specific electrode on nine specific test days during the aging period. Following 49 days of aging, each specimen was recharged in 5000 ppm neutral sodium fluoride solution for 5 minutes. Specimen recharge was then repeated on a weekly basis for 3 weeks. The subsequent fluoride rerelease was measured at 1, 3, and 7 days after each recharge episode. Group 2 included six disc specimens aged for 3 months in deionized water (three specimens) and lactic acid (three specimens). The hardness and elastic modulus of each specimen was measured using nano-indentation at intervals of 24 hours, 1 month, and 3 months after fabrication. Two-way factorial analysis of variance (ANOVA) and post-hoc (Tukey) testing was used to assess the influence of storage media (two levels) and composite type (three levels) on the fluoride release, fluoride rerelease, hardness, and elastic modulus of the assessed materials. The level of significance was set at p=0.05. All three composites demonstrated fluoride release and recharge when aged in both deionized water and lactic acid. The cumulative fluoride released from Beautifil II into both media was substantially greater than the fluoride released from Gradia Direct X and Tetric EvoCeram after 43 days aging and was significantly (p<0.05, ANOVA, Tukey test) greater during several analysis periods. Beautifil II demonstrated the greatest recharge ability of the three composites over the 3-week recharge period in both media. Fuji IX Extra demonstrated a significantly (p<0.05) greater fluoride release and recharge compared with the three resin composites. The elastic modulus and hardness of the three composites did not decrease significantly (p<0.05) with fluoride release or fluid uptake over the 3-month aging period, in either media. The three composites in the present study demonstrated fluoride release (Beautiful II > Gradia Direct X > Tetric EvoCeram) and fluoride recharge (Beautiful II > Gradia Direct X > Tetric EvoCeram). This capability raises the possibility of fluoride-containing composites exhibiting a lower incidence of recurrent caries than non fluoride–containing composites. The mechanical properties of each composite did not diminish with aging and fluoride release over the testing period.

Analysis of the Mechanical Behavior and Surface Rugosity of Different Dental Die Materials.

PubMed

Niekawa, Ciro T; Kreve, Simone; A'vila, Gisseli Bertozzi; Godoy, Gilmar Gil; Eduardo Vieira da Silva, J R; Dias, Sergio Candido

2017-01-01

This work evaluated the mechanical and surface behavior of different die materials. The studied materials are polyurethane resin Exakto-Form (Bredent), Gypsum type IV, Fuji Rock EP (Gc), and Durone (Dentsply). Two metallic matrices molded in polyvinyl siloxane provided 30 cylindrical test specimens for the diametral compression test and 30 hemispherical test specimens for the surface rugosity test. The cylindrical test specimens were submitted to tests of diametral compression strength using a DL2000 universal assay machine, with a load cell of 2000 Kgf and constant speed of 1 mm/min connected to the software. Kruskal-Wallis and Dunn's nonparametric tests were used to analyze the results. The hemispheres were submitted to the surface rugosity assay using a SJ201-P rugosimeter with a sensitivity of 300 μm, speed of 0.5 mm/s, and cut-off of 0.8 mm, and the readings were taken on the convex surface of the test specimens and metallic matrix. Results were analyzed using with Fisher's least significant differences test (LSD) and Dunnett's test. Kruskal-Wallis test showed significant difference between die materials for diametral compression strength ( P = 0.002). Dunn's test showed significantly higher values for modified polyurethane resin (Exakto-Form). The gypsum type IV, which did not significantly differ regarding diametral compression strength, showed 34.0% (Durone) and 42.7% (Fuji Rock) lower values in comparison to Exakto-Form. Within the parameters adopted in this study, it is possible to conclude that Exakto-Form polyurethane resin showed higher resistance to compression and was closer to the metallic matrix rugosity, and, along with the gypsum type IV Durone, showed better reproducibility of details relative to the Fuji Rock.

Laboratory Characterization of White Masonry Concrete

DTIC Science & Technology

2006-09-01

procedures given in American Society for Testing and Materials (ASTM) D 2216 (ASTM 2002e). Based on the appropriate values of posttest water content...properties of the material. All of the mechanical property tests were conducted quasi -statically with axial strain rates on the order of 10-4 to 10...mechanical property tests, nondestructive pulse-velocity measurements were performed on each specimen. The TXC tests exhibited a continuous increase

The fracture characteristic of three collinear cracks under true triaxial compression.

PubMed

Liu, Jianjun; Zhu, Zheming; Wang, Bo

2014-01-01

The mechanical behavior of multicracks under compression has become a very important project in the field of fracture mechanics and rock mechanics. In this paper, experimental and numerical studies on the fracture property of three collinear cracks under compression were implemented. The specimens were a square concrete plate, and the cracks were made by a very thin film. The tests were conducted by using true triaxial loading device. In the numerical study, the Abaqus code was employed. The effect of crack orientation and the confining stress on cracked specimen compressive strength were investigated. The results show that the critical stresses of cracked specimens change with crack inclination angles, and, as the angle is 45°, the critical stress is the lowest; the critical stresses increase with the confining stresses.

The Fracture Characteristic of Three Collinear Cracks under True Triaxial Compression

PubMed Central

Liu, Jianjun; Zhu, Zheming; Wang, Bo

2014-01-01

The mechanical behavior of multicracks under compression has become a very important project in the field of fracture mechanics and rock mechanics. In this paper, experimental and numerical studies on the fracture property of three collinear cracks under compression were implemented. The specimens were a square concrete plate, and the cracks were made by a very thin film. The tests were conducted by using true triaxial loading device. In the numerical study, the Abaqus code was employed. The effect of crack orientation and the confining stress on cracked specimen compressive strength were investigated. The results show that the critical stresses of cracked specimens change with crack inclination angles, and, as the angle is 45°, the critical stress is the lowest; the critical stresses increase with the confining stresses. PMID:24790569

The Development of Expansion Plug Wedge Test for Clad Tubing Structure Mechanical Property Evaluation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Jy-An John; Jiang, Hao

2016-01-12

To determine the tensile properties of irradiated fuel cladding in a hot cell, a simple test was developed at the Oak Ridge National Laboratory (ORNL) and is described fully in US Patent Application 20060070455, “Expanded plug method for developing circumferential mechanical properties of tubular materials.” This method is designed for testing fuel rod cladding ductility in a hot cell using an expandable plug to stretch a small ring of irradiated cladding material. The specimen strain is determined using the measured diametrical expansion of the ring. This method removes many complexities associated with specimen preparation and testing. The advantages are themore » simplicity of measuring the test component assembly in the hot cell and the direct measurement of the specimen’s strain. It was also found that cladding strength could be determined from the test results.« less

Mechanical Characterization of Mancos Shale

NASA Astrophysics Data System (ADS)

Broome, S.; Ingraham, M. D.; Dewers, T. A.

2015-12-01

A series of tests on Mancos shale have been undertaken to determine the failure surface and to characterize anisotropy. This work supports additional studies which are being performed on the same block of shale; fracture toughness, permeability, and chemical analysis. Mechanical tests are being conducted after specimens were conditioned for at least two weeks at 70% constant relative humidity conditions. Specimens are tested under drained conditions, with the constant relative humidity condition maintained on the downstream side of the specimen. The upstream is sealed. Anisotropy is determined through testing specimens that have been cored parallel and perpendicular to the bedding plane. Preliminary results show that when loaded parallel to bedding the shale is roughly 50% weaker. Test are run under constant mean stress conditions when possible (excepting indirect tension, unconfined compression, and hydrostatic). Tests are run in hydrostatic compaction to the desired mean stress, then differential stress is applied axially in displacement control to failure. The constant mean stress condition is maintained by decreasing the confining pressure by half of the increase in the axial stress. Results will be compared to typical failure criteria to investigate the effectiveness of capturing the behavior of the shale with traditional failure theory. Sandia National Laboratories is a multi-program laboratory managed and operated by Sandia Corporation, a wholly owned subsidiary of Lockheed Martin Corporation, for the U.S. Department of Energy's National Nuclear Security Administration under contract DE-AC04-94AL85000. SAND2015-6107 A.

Four-point Bend Testing of Irradiated Monolithic U-10Mo Fuel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rabin, B. H.; Lloyd, W. R.; Schulthess, J. L.

2015-03-01

This paper presents results of recently completed studies aimed at characterizing the mechanical properties of irradiated U-10Mo fuel in support of monolithic base fuel qualification. Mechanical properties were evaluated in four-point bending. Specimens were taken from fuel plates irradiated in the RERTR-12 and AFIP-6 Mk. II irradiation campaigns, and tests were conducted in the Hot Fuel Examination Facility (HFEF) at Idaho National Laboratory (INL). The monolithic fuel plates consist of a U-10Mo fuel meat covered with a Zr diffusion barrier layer fabricated by co-rolling, clad in 6061 Al using a hot isostatic press (HIP) bonding process. Specimens exhibited nominal (fresh)more » fuel meat thickness ranging from 0.25 mm to 0.64 mm, and fuel plate average burnup ranged from approximately 0.4 x 1021 fissions/cm 3 to 6.0 x 1021 fissions/cm 3. After sectioning the fuel plates, the 6061 Al cladding was removed by dissolution in concentrated NaOH. Pre- and post-dissolution dimensional inspections were conducted on test specimens to facilitate accurate analysis of bend test results. Four-point bend testing was conducted on the HFEF Remote Load Frame at a crosshead speed of 0.1 mm/min using custom-designed test fixtures and calibrated load cells. All specimens exhibited substantially linear elastic behavior and failed in a brittle manner. The influence of burnup on the observed slope of the stress-strain curve and the calculated fracture strength is discussed.« less

Method and apparatus for deflection measurements using eddy current effects

NASA Astrophysics Data System (ADS)

Chern, Engmin J.

1993-05-01

A method and apparatus for inserting and moving a sensing assembly with a mechanical positioning assembly to a desired remote location of a surface of a specimen under test and measuring angle and/or deflection by sensing the change in the impedance of at least one sensor coil located in a base plate which has a rotatable conductive plate pivotally mounted thereon so as to uncover the sensor coil(s) whose impedance changes as a function of deflection away from the center line of the base plate in response to the movement of the rotator plate when contacting the surface of the specimen under test is presented. The apparatus includes the combination of a system controller, a sensing assembly, an eddy current impedance measuring apparatus, and a mechanical positioning assembly driven by the impedance measuring apparatus to position the sensing assembly at a desired location of the specimen.

Method and apparatus for deflection measurements using eddy current effects

NASA Technical Reports Server (NTRS)

Chern, Engmin J. (Inventor)

1993-01-01

A method and apparatus for inserting and moving a sensing assembly with a mechanical positioning assembly to a desired remote location of a surface of a specimen under test and measuring angle and/or deflection by sensing the change in the impedance of at least one sensor coil located in a base plate which has a rotatable conductive plate pivotally mounted thereon so as to uncover the sensor coil(s) whose impedance changes as a function of deflection away from the center line of the base plate in response to the movement of the rotator plate when contacting the surface of the specimen under test is presented. The apparatus includes the combination of a system controller, a sensing assembly, an eddy current impedance measuring apparatus, and a mechanical positioning assembly driven by the impedance measuring apparatus to position the sensing assembly at a desired location of the specimen.

Mechanical Properties of Degraded PMR-15 Resin

NASA Technical Reports Server (NTRS)

Tsuji, Luis C.; McManus, Hugh L.; Bowles, Kenneth J.

1998-01-01

Thermo-oxidative aging produces a non-uniform degradation state in PMR-15 resin. A surface layer, usually attributed to oxidative degradation, forms. This surface layer has different properties from the inner material. A set of material tests was designed to separate the properties of the oxidized surface layer from the properties of interior material. Test specimens were aged at 316 C in either air or nitrogen, for durations of up to 800 hours. The thickness of the oxidized surface layer in air aged specimens, and the shrinkage and Coefficient of Thermal Expansion (CTE) of nitrogen aged specimens were measured directly. Four-point-bend tests were performed to determine modulus of both the oxidized surface layer and the interior material. Bimaterial strip specimens consisting of oxidized surface material and unoxidized interior material were constructed and used to determine surface layer shrinkage and CTE. Results confirm that the surface layer and core materials have substantially different properties.

Measurement of material mechanical properties in microforming

NASA Astrophysics Data System (ADS)

Yun, Wang; Xu, Zhenying; Hui, Huang; Zhou, Jianzhong

2006-02-01

As the rapid market need of micro-electro-mechanical systems engineering gives it the wide development and application ranging from mobile phones to medical apparatus, the need of metal micro-parts is increasing gradually. Microforming technology challenges the plastic processing technology. The findings have shown that if the grain size of the specimen remains constant, the flow stress changes with the increasing miniaturization, and also the necking elongation and the uniform elongation etc. It is impossible to get the specimen material properties in conventional tensile test machine, especially in the high precision demand. Therefore, one new measurement method for getting the specimen material-mechanical property with high precision is initiated. With this method, coupled with the high speed of Charge Coupled Device (CCD) camera and high precision of Coordinate Measuring Machine (CMM), the elongation and tensile strain in the gauge length are obtained. The elongation, yield stress and other mechanical properties can be calculated from the relationship between the images and CCD camera movement. This measuring method can be extended into other experiments, such as the alignment of the tool and specimen, micro-drawing process.

Piezoelectric Response of Ferroelectric Ceramics Under Mechanical Stress

DTIC Science & Technology

2015-09-17

dynamic response, and predict mechanical breakdown of electronic materials, numerous testing techniques such as very high-g machines , drop towers...James C. Hierholzer for building the custom test fixture, Michael D. Craft for his help with static capacitance measurements, Bryan J. Turner, Scott D...ISOLA 370HR Board Specimen Test Set-Up . . . . . . . . . . . . . . . . . . 59 3.3 Printed Circuit Board Electrical Layout

Mechanical Properties Analysis of 4340 Steel Specimen Heat Treated in Oven and Quenching in Three Different Fluids

NASA Astrophysics Data System (ADS)

Fakir, Rachid; Barka, Noureddine; Brousseau, Jean

2018-03-01

This paper proposes a statistical approach to analyze the mechanical properties of a standard test specimen, of cylindrical geometry and in steel 4340, with a diameter of 6 mm, heat-treated and quenched in three different fluids. Samples were evaluated in standard tensile test to access their characteristic quantities: hardness, modulus of elasticity, yield strength, tensile strength and ultimate deformation. The proposed approach is gradually being built (a) by a presentation of the experimental device, (b) a presentation of the experimental plan and the results of the mechanical tests, (c) anova analysis of variance and a representation of the output responses using the RSM response surface method, and (d) an analysis of the results and discussion. The feasibility and effectiveness of the proposed approach leads to a precise and reliable model capable of predicting the variation of mechanical properties, depending on the tempering temperature, the tempering time and the cooling capacity of the quenching medium.

Mechanical Characteristics of Submerged Arc Weldment in API Gas Pipeline Steel of Grade X65

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hashemi, S. H.; Mohammadyani, D.

The mechanical properties of submerged arc weldment (SAW) in gas transportation pipeline steel of grade API X65 (65 ksi yield strength) were investigated. This steel is produced by thermo mechanical control rolled (TMC), and is largely used in Iran gas piping systems and networks. The results from laboratory study on three different regions; i.e. base metal (BM), fusion zone (FZ) and heat affected zone (HAZ) were used to compare weldment mechanical characteristics with those specified by API 5L (revision 2004) standard code. Different laboratory experiments were conducted on test specimens taken from 48 inch outside diameter and 14.3 mm wallmore » thickness gas pipeline. The test results showed a gradient of microstructure and Vickers hardness data from the centerline of FZ towards the unaffected MB. Similarly, lower Charpy absorbed energy (compared to BM) was observed in the FZ impact specimens. Despite this, the API specifications were fulfilled in three tested zones, ensuring pipeline structural integrity under working conditions.« less

Effects of silvicultural practice and moisture content level on lobolly pine veneer mechanical properties

Treesearch

Todd F. Shupe; Chung-Yun Hse; Elvin T. Choong; Leslie H. Groom

1998-01-01

Loblolly pine veneer specimens were obtained from five silviculturally different stands. Clear specimens were cut parallel to the grain from full size veneer sheets and tests were done at either air-dry or ovendry conditions to determine differences in bending modulus of rupture (MORb), bending modulus of elasticity (MOEb...

Small scale mechanical characterization of thin foil materials via pin load microtesting

DOE PAGES

Wheeler, Robert; Pandey, Amit; Shyam, Amit; ...

2015-05-06

In situ scanning electron microscope (SEM) experiments, where small-scale mechanical tests are conducted on micro- and nanosized specimens, allow direct visualization of elastic and plastic responses over the entirety of the volume being deformed. This enables precise spatial and temporal correlation of slip events contributing to the plastic flow evidenced in a stress–strain curve. A new pin-loading methodology has been employed, in situ within the SEM, to conduct microtensile tests on thin polycrystalline metal foils. This approach can be tailored to a specific foil whose particular grain size may range from microns to tens of microns. Manufacture of the specializedmore » pin grip was accomplished via silicon photolithography-based processing followed by subsequent focused ion beam finishing. Microtensile specimen preparation was achieved by combining a stencil mask methodology employing broad ion beam sputtering along with focused ion beam milling in the study of several metallic foil materials. Finite-element analyses were performed to characterize the stress and strain distributions in the pin grip and micro-specimen under load. Furthermore, under appropriately conceived test conditions, uniaxial stress–strain responses measured within these foils by pin-load microtensile testing exhibit properties consistent with larger scale tests.« less

Influence of airborne-particle abrasion on mechanical properties and bond strength of carbon/epoxy and glass/bis-GMA fiber-reinforced resin posts.

PubMed

Soares, Carlos Jose; Santana, Fernanda Ribeiro; Pereira, Janaina Carla; Araujo, Tatiana Santos; Menezes, Murilo Souza

2008-06-01

Controversy exists concerning the use of fiber-reinforced posts to improve bond strength to resin cement because some precementation treatments can compromise the mechanical properties of the posts. The purpose of this study was to analyze the influence of airborne-particle abrasion on the mechanical properties and microtensile bond strength (MTBS) of carbon/epoxy and glass/bis-GMA fiber-reinforced resin posts. Flexural strength (delta(f)), flexural modulus (E(f)), and stiffness (S) were assessed using a 3-point bending test for glass fiber-reinforced and carbon fiber-reinforced resin posts submitted to airborne-particle abrasion (AB) with 50-microm Al(2)O(3), and for posts without any surface treatment (controls) (n=10). Forty glass fiber (GF) and 40 carbon fiber (CF) posts were submitted to 1 of 4 surface treatments (n=10) prior to MTBS testing: silane (S); silane and adhesive (SA); airborne-particle abrasion with 50-microm Al(2)O(3) and silane (ABS); airborne-particle abrasion, silane, and adhesive (ABSA). Two composite resin restorations (Filtek Z250) with rounded depressions in the lateral face were bilaterally fixed to the post with resin cement (RelyX ARC). Next, the specimen was sectioned with a precision saw running perpendicular to the bonded surface to obtain 10 bonded beam specimens with a cross-sectional area of 1 mm(2). Each beam specimen was tested in a mechanical testing machine (EMIC 2,000 DL), under stress, at a crosshead speed of 0.5 mm/min until failure. Data were analyzed by 2-way ANOVA followed by Tukey HSD test (alpha=.05). Failure patterns of tested specimens were analyzed using scanning electron microscopy (SEM). The 3-point bending test demonstrated significant differences among groups only for the post type factor for flexural strength, flexural modulus, and stiffness. The carbon fiber posts exhibited significantly higher mean flexural strength (P=.001), flexural modulus (P=.003), and stiffness (P=.001) values when compared with glass fiber posts, irrespective of surface treatment. An alteration in the superficial structure of the posts could be observed by SEM after airborne-particle abrasion. MTBS testing showed no significant effect for the surface treatment type; however, significant effects for post system factor and for interaction between the 2 factors were observed. For the carbon fiber post, the ABSA surface treatment resulted in values significantly lower than the S surface treatment. SEM analysis of MTBS-tested specimens demonstrated adhesive and cohesive failures. Airborne-particle abrasion did not influence the mechanical properties of the post; however, it produced undesirable surface changes, which could reduce the bond strength to resin cement. For the surface treatments studied, if silane is applied, the adhesive system and airborne-particle abrasion are not necessary.

Initial Mechanical Testing of Superalloy Lattice Block Structures Conducted

NASA Technical Reports Server (NTRS)

Krause, David L.; Whittenberger, J. Daniel

2002-01-01

The first mechanical tests of superalloy lattice block structures produced promising results for this exciting new lightweight material system. The testing was performed in-house at NASA Glenn Research Center's Structural Benchmark Test Facility, where small subelement-sized compression and beam specimens were loaded to observe elastic and plastic behavior, component strength levels, and fatigue resistance for hundreds of thousands of load cycles. Current lattice block construction produces a flat panel composed of thin ligaments arranged in a three-dimensional triangulated trusslike structure. Investment casting of lattice block panels has been developed and greatly expands opportunities for using this unique architecture in today's high-performance structures. In addition, advances made in NASA's Ultra-Efficient Engine Technology Program have extended the lattice block concept to superalloy materials. After a series of casting iterations, the nickel-based superalloy Inconel 718 (IN 718, Inco Alloys International, Inc., Huntington, WV) was successfully cast into lattice block panels; this combination offers light weight combined with high strength, high stiffness, and elevated-temperature durability. For tests to evaluate casting quality and configuration merit, small structural compression and bend test specimens were machined from the 5- by 12- by 0.5-in. panels. Linear elastic finite element analyses were completed for several specimen layouts to predict material stresses and deflections under proposed test conditions. The structural specimens were then subjected to room-temperature static and cyclic loads in Glenn's Life Prediction Branch's material test machine. Surprisingly, the test results exceeded analytical predictions: plastic strains greater than 5 percent were obtained, and fatigue lives did not depreciate relative to the base material. These assets were due to the formation of plastic hinges and the redundancies inherent in lattice block construction, which were not considered in the simplified computer models. The fatigue testing proved the value of redundancies since specimen strength was maintained even after the fracture of one or two ligaments. This ongoing test program is planned to continue through high-temperature testing. Also scheduled for testing are IN 718 lattice block panels with integral face sheets, as well as specimens cast from a higher temperature alloy. The initial testing suggests the value of this technology for large panels under low and moderate pressure loadings and for high-risk, damage-tolerant structures. Potential aeropropulsion uses for lattice blocks include turbine-engine actuated panels, exhaust nozzle flaps, and side panel structures.

Estimation of Mechanical Properties of Stainless Steel AISI 410 by Small-Punch Testing (Erickson Test)

NASA Astrophysics Data System (ADS)

Hassan, A.-P.

2014-07-01

The small-punch testing (SPT) method is used for determining the mechanical properties of AISI 410 (0.14% C, 12% Cr) stainless steel. A thin disc-shaped specimen with known mechanical properties is pressed with a small ball until the appearance of cracks in the former. The load - displacement curves are recorded. Computation of the yield strength and fracture energy by the curve obtained and by known formulas shows good convergence with the characteristics obtained by standard testing.

A Comparison of the Flexural and Impact Strengths and Flexural Modulus of CAD/CAM and Conventional Heat-Cured Polymethyl Methacrylate (PMMA).

PubMed

Al-Dwairi, Ziad N; Tahboub, Kawkab Y; Baba, Nadim Z; Goodacre, Charles J

2018-06-13

The introduction of computer-aided design/computer-aided manufacturing (CAD/CAM) technology to the field of removable prosthodontics has recently made it possible to fabricate complete dentures of prepolymerized polymethyl methacrylate (PMMA) blocks, which are claimed to be of better mechanical properties; however, no published reports that have evaluated mechanical properties of CAD/CAM PMMA. The purpose of this study was to compare flexural strength, impact strength, and flexural modulus of two brands of CAD/CAM PMMA and a conventional heat-cured PMMA. 45 rectangular specimens (65 mm × 10 mm × 3 mm) were fabricated (15 CAD/CAM AvaDent PMMA specimens from AvaDent, 15 CAD/CAM Tizian PMMA specimens from Shütz Dental, 15 conventional Meliodent PMMA specimens from Heraeus Kulzer) and stored in distilled water at (37  ± 1°C) for 7 days. Specimens (N = 15) in each group were subjected to the three-point bending test and impact strength test, employing the Charpy configuration on unnotched specimens. The morphology of the fractured specimens was studied under a scanning electron microscope (SEM). Statistical analysis was performed using one-way ANOVA and Tukey pairwise multiple comparisons with 95% confidence interval. The Schütz Dental specimens showed the highest mean flexural strength (130.67 MPa) and impact strength (29.56 kg/m 2 ). The highest mean flexural modulus was recorded in the AvaDent group (2519.6 MPa). The conventional heat-cured group showed the lowest mean flexural strength (93.33 MPa), impact strength (14.756 kg/m 2 ), and flexural modulus (2117.2 MPa). Differences in means of flexural properties between AvaDent and Schütz Dental specimens were not statistically significant (p > 0.05). As CAD/CAM PMMA specimens exhibited improved flexural strength, flexural modulus, and impact strength in comparison to the conventional heat-cured groups, CAD/CAM dentures are expected to be more durable. Different brands of CAD/CAM PMMA may have inherent variations in mechanical properties. © 2018 by the American College of Prosthodontists.

Damage mechanisms in PBT-GF30 under thermo-mechanical cyclic loading

NASA Astrophysics Data System (ADS)

Schaaf, A.; De Monte, M.; Hoffmann, C.; Vormwald, M.; Quaresimin, M.

2014-05-01

The scope of this paper is the investigation of damage mechanisms at microscopic scale on a short glass fiber reinforced polybutylene terephthalate (PBT-GF30) under thermo-mechanical cyclic loading. In addition the principal mechanisms are verified through micro mechanical FE models. In order to investigate the fatigue behavior of the material both isothermal strain controlled fatigue (ISCF) tests at three different temperatures and thermo-mechanical fatigue (TMF) tests were conducted on plain and notched specimens, manufactured by injection molding. The goal of the work is to determine the damage mechanisms occurring under TMF conditions and to compare them with the mechanisms occurring under ISCF. For this reason fracture surfaces of TMF and ISCF samples loaded at different temperature levels were analyzed using scanning electron microscopy. Furthermore, specimens that failed under TMF were examined on microsections revealing insight into both crack initiation and crack propagation. The findings of this investigation give valuable information about the main damage mechanisms of PBT-GF30 under TMF loading and serve as basis for the development of a TMF life estimation methodology.

Microwave processing of a dental ceramic used in computer-aided design/computer-aided manufacturing.

PubMed

Pendola, Martin; Saha, Subrata

2015-01-01

Because of their favorable mechanical properties and natural esthetics, ceramics are widely used in restorative dentistry. The conventional ceramic sintering process required for their use is usually slow, however, and the equipment has an elevated energy consumption. Sintering processes that use microwaves have several advantages compared to regular sintering: shorter processing times, lower energy consumption, and the capacity for volumetric heating. The objective of this study was to test the mechanical properties of a dental ceramic used in computer-aided design/computer-aided manufacturing (CAD/CAM) after the specimens were processed with microwave hybrid sintering. Density, hardness, and bending strength were measured. When ceramic specimens were sintered with microwaves, the processing times were reduced and protocols were simplified. Hardness was improved almost 20% compared to regular sintering, and flexural strength measurements suggested that specimens were approximately 50% stronger than specimens sintered in a conventional system. Microwave hybrid sintering may preserve or improve the mechanical properties of dental ceramics designed for CAD/CAM processing systems, reducing processing and waiting times.

Mechanical Behavior of Recycled Aggregate Concrete-Filled Steel Tubular Columns before and after Fire.

PubMed

Liu, Wenchao; Cao, Wanlin; Zhang, Jianwei; Wang, Ruwei; Ren, Lele

2017-03-09

Recycled aggregate concrete (RAC) is an environmentally friendly building material. This paper investigates the mechanical behavior of recycled aggregate concrete filled steel tube (RACFST) columns exposed to fire. Two groups of 12 columns were designed and tested, under axial compression, before and after fire, to evaluate the degradation of bearing capacity due to fire exposure. Six specimens were subjected to axial compression tests at room temperature and the other six specimens were subjected to axial compression tests after a fire exposure. The main parameters of the specimens include the wall thickness of the steel tube (steel content) and the type of concrete materials. Several parameters as obtained from the experimental results were compared and analyzed, including the load-bearing capacity, deformation capacity, and failure characteristics of the specimens. Meanwhile, rate of loss of bearing capacity of specimens exposed to fire were calculated based on the standards EC4 and CECS28:90. The results show that concrete material has a large influence on the rate of loss of bearing capacity in the case of a relatively lower steel ratio. While steel content has little effect on the rate of loss of bearing capacity of concrete-filled steel tube (CFST) columns after fire, it has a relatively large influence on the loss rate of bearing capacity of the RACFST columns. The loss of bearing capacity of the specimens from the experiment is more serious than that from the calculation. As the calculated values are less conservative, particular attention should be given to the application of recycled aggregate concrete in actual structures.

Mechanical Behavior of Recycled Aggregate Concrete-Filled Steel Tubular Columns before and after Fire

PubMed Central

Liu, Wenchao; Cao, Wanlin; Zhang, Jianwei; Wang, Ruwei; Ren, Lele

2017-01-01

Recycled aggregate concrete (RAC) is an environmentally friendly building material. This paper investigates the mechanical behavior of recycled aggregate concrete filled steel tube (RACFST) columns exposed to fire. Two groups of 12 columns were designed and tested, under axial compression, before and after fire, to evaluate the degradation of bearing capacity due to fire exposure. Six specimens were subjected to axial compression tests at room temperature and the other six specimens were subjected to axial compression tests after a fire exposure. The main parameters of the specimens include the wall thickness of the steel tube (steel content) and the type of concrete materials. Several parameters as obtained from the experimental results were compared and analyzed, including the load-bearing capacity, deformation capacity, and failure characteristics of the specimens. Meanwhile, rate of loss of bearing capacity of specimens exposed to fire were calculated based on the standards EC4 and CECS28:90. The results show that concrete material has a large influence on the rate of loss of bearing capacity in the case of a relatively lower steel ratio. While steel content has little effect on the rate of loss of bearing capacity of concrete-filled steel tube (CFST) columns after fire, it has a relatively large influence on the loss rate of bearing capacity of the RACFST columns. The loss of bearing capacity of the specimens from the experiment is more serious than that from the calculation. As the calculated values are less conservative, particular attention should be given to the application of recycled aggregate concrete in actual structures. PMID:28772634

Impact of Gastric Acid Induced Surface Changes on Mechanical Behavior and Optical Characteristics of Dental Ceramics.

PubMed

Kulkarni, Aditi; Rothrock, James; Thompson, Jeffery

2018-01-14

To test the impact of exposure to artificial gastric acid combined with toothbrush abrasion on the properties of dental ceramics. Earlier research has indicated that immersion in artificial gastric acid has caused increased surface roughness of dental ceramics; however, the combined effects of acid immersion and toothbrush abrasion and the impact of increased surface roughness on mechanical strength and optical properties have not been studied. Three commercially available ceramics were chosen for this study: feldspathic porcelain, lithium disilicate glass-ceramic, and monolithic zirconium oxide. The specimens (10 × 1 mm discs) were cut, thermally treated as required, and polished. Each material was divided into four groups (n = 8 per group): control (no exposure), acid only, brush only, acid + brush. The specimens were immersed in artificial gastric acid (50 ml of 0.2% [w/v] sodium chloride in 0.7% [v/v] hydrochloric acid mixed with 0.16 g of pepsin powder, pH = 2) for 2 minutes and rinsed with deionized water for 2 minutes. The procedure was repeated 6 times/day × 9 days, and specimens were stored in deionized water at 37°C. Toothbrush abrasion was performed using an ISO/ADA design brushing machine for 100 cycles/day × 9 days. The acid + brush group received both treatments. Specimens were examined under SEM and an optical microscope for morphological changes. Color and translucency were measured using spectrophotometer CIELAB coordinates (L*, a*, b*). Surface gloss was measured using a gloss meter. Surface roughness was measured using a stylus profilometer. Biaxial flexural strength was measured using a mechanical testing machine. The data were analyzed by one-way ANOVA followed by Tukey's HSD post hoc test (p < 0.05). Statistically significant changes were found for color, gloss, and surface roughness for porcelain and e.max specimens. No statistically significant changes were found for any properties of zirconia specimens. The acid treatment affected the surface roughness, color, and gloss of porcelain and e.max ceramics. The changes in translucency and mechanical strength for all materials were not statistically significant. Zirconia ceramic showed resistance to all treatments. © 2018 by the American College of Prosthodontists.

Photoelasticity and DIC as optical techniques for monitoring masonry specimens under mechanical loads

NASA Astrophysics Data System (ADS)

Colla, C.; Gabrielli, E.

2017-01-01

To evaluate the complex behaviour of masonry structures under mechanical loads, numerical models are developed and continuously implemented at diverse scales, whilst, from an experimental viewpoint, laboratory standard mechanical tests are usually carried out by instrumenting the specimens via traditional measuring devices. Extracted values collected in the few points where the tools were installed are assumed to represent the behaviour of the whole specimen but this may be quite optimistic or approximate. Optical monitoring techniques may help in overcoming some of these limitations by providing full-field visualization of mechanical parameters. Photoelasticity and the more recent DIC, employed to monitor masonry columns during compression tests are here presented and a lab case study is compared listing procedures, data acquisitions, advantages and limitations. It is shown that the information recorded by traditional measuring tools must be considered limited to the specific instrumented points. Instead, DIC in particular among the optical techniques, is proving both a very precise global and local picture of the masonry performance, opening new horizons towards a deeper knowledge of this complex construction material. The applicability of an innovative DIC procedure to cultural heritage constructions is also discussed.

Mechanical behavior of Kenaf/Epoxy corrugated sandwich structures

NASA Astrophysics Data System (ADS)

Bakhori, S.; Hassan, M. Z.; Daud, Y.; Sarip, S.; Rahman, N.; Ismail, Z.; Aziz, S. A.

2015-12-01

This study presents the response of kenaf/epoxy corrugated sandwich structure during quasi-static test. Force-displacements curves have been deducted to determine the deformation pattern and collapse behavior of the structure. Kenaf/epoxy sandwich structures skins fabricated by using hand layup technique and the corrugated core were moulded by using steel mould. Different thicknesses of corrugated core web with two sizes of kenaf fibers were used. The corrugated core is then bonded with the skins by using poly-epoxy resin and has been cut into different number of cells. The specimens then tested under tensile and compression at different constant speeds until the specimens fully crushed. Tensile tests data showed the structure can be considered brittle when it breaking point strain, ε less than 0.025. In compression test, the specimens fail due to dominated by stress concentration that initiated by prior cracks. Also, the specimens with more number of cells and thicker core web have higher strength and the ability to absorb higher energy.

In vitro validation of a novel mechanical model for testing the anchorage capacity of pedicle screws using physiological load application.

PubMed

Liebsch, Christian; Zimmermann, Julia; Graf, Nicolas; Schilling, Christoph; Wilke, Hans-Joachim; Kienle, Annette

2018-01-01

Biomechanical in vitro tests analysing screw loosening often include high standard deviations caused by high variabilities in bone mineral density and pedicle geometry, whereas standardized mechanical models made of PU foam often do not integrate anatomical or physiological boundary conditions. The purpose of this study was to develop a most realistic mechanical model for the standardized and reproducible testing of pedicle screws regarding the resistance against screw loosening and the holding force as well as to validate this model by in vitro experiments. The novel mechanical testing model represents all anatomical structures of a human vertebra and is consisting of PU foam to simulate cancellous bone, as well as a novel pedicle model made of short carbon fibre filled epoxy. Six monoaxial cannulated pedicle screws (Ø6.5 × 45mm) were tested using the mechanical testing model as well as human vertebra specimens by applying complex physiological cyclic loading (shear, tension, and bending; 5Hz testing frequency; sinusoidal pulsating forces) in a dynamic materials testing machine with stepwise increasing load after each 50.000 cycles (100.0N shear force + 20.0N per step, 51.0N tension force + 10.2N per step, 4.2Nm bending moment + 0.8Nm per step) until screw loosening was detected. The pedicle screw head was fixed on a firmly clamped rod while the load was applied in the vertebral body. For the in vitro experiments, six human lumbar vertebrae (L1-3, BMD 75.4 ± 4.0mg/cc HA, pedicle width 9.8 ± 0.6mm) were tested after implanting pedicle screws under X-ray control. Relative motions of pedicle screw, specimen fixture, and rod fixture were detected using an optical motion tracking system. Translational motions of the mechanical testing model experiments in the point of load introduction (0.9-2.2mm at 240N shear force) were reproducible within the variation range of the in vitro experiments (0.6-3.5mm at 240N shear force). Screw loosening occurred continuously in each case between 140N and 280N, while abrupt failures of the specimen were observed only in vitro. In the mechanical testing model, no translational motion was detected in the screw entry point, while in vitro, translational motions of up to 2.5mm in inferior direction were found, leading to a slight shift of the centre of rotation towards the screw tip. Translational motions of the screw tip of about 5mm in superior direction were observed both in vitro and in the mechanical testing model, while they were continuous in the mechanical testing model and rapidly increasing after screw loosening initiation in vitro. The overall pedicle screw loosening characteristics were qualitatively and quantitatively similar between the mechanical testing model and the human vertebral specimens as long as there was no translation of the screw at the screw entrance point. Therefore, the novel mechanical testing model represents a promising method for the standardized testing of pedicle screws regarding screw loosening for cases where the screw rotates around a point close to the screw entry point. Copyright © 2017 Elsevier Ltd. All rights reserved.

Corrosion and Fatigue Behavior of High-Strength Steel Treated with a Zn-Alloy Thermo-diffusion Coating

NASA Astrophysics Data System (ADS)

Mulligan, C. P.; Vigilante, G. N.; Cannon, J. J.

2017-11-01

High and low cycle fatigue tests were conducted on high-strength steel using four-point bending. The materials tested were ASTM A723 steel in the as-machined condition, grit-blasted condition, MIL-DTL-16232 heavy manganese phosphate-coated condition, and ASTM A1059 Zn-alloy thermo-diffusion coated (Zn-TDC). The ASTM A723 steel base material exhibits a yield strength of 1000 MPa. The effects of the surface treatments versus uncoated steel were examined. The fatigue life of the Zn-TDC specimens was generally reduced on as-coated specimens versus uncoated or phosphate-coated specimens. Several mechanisms are examined including the role of compressive residual stress relief with the Zn-TDC process as well as fatigue crack initiation from the hardened Zn-Fe alloy surface layer produced in the gas-metal reaction. Additionally, the effects of corrosion pitting on the fatigue life of coated specimens are explored as the Zn-TDC specimens exhibit significantly improved corrosion resistance over phosphate-coated and oiled specimens.

ZM-21 magnesium alloy corrosion properties and cryogenic to elevated temperature mechanical properties

NASA Technical Reports Server (NTRS)

Montana, J. W.; Nelson, E. E.

1972-01-01

The mechanical properties of bare ZM-21 magnesium alloy flat tensile specimens were determined for test temperatures of +400 F, +300 F, +200 F, +80 F, 0 F, -100 F, -200 F, and -320 F. The ultimate tensile and yield strengths of the material increased with decreasing temperature with a corresponding reduction in elongation values. Stress corrosion tests performed under: (1) MSFC atmospheric conditions; (2) 95% relative humidity; and (3) submerged in 100 ppm chloride solution for 8 weeks indicated that the alloy is not susceptible to stress corrosion. The corrosion tests indicated that the material is susceptible to attack by crevice corrosion in high humidity and chemical type attack by chloride solution. Atmospheric conditions at MSFC did not produce any adverse effects on the material, probably due to the rapid formation of a protective oxide coating. In both the mechanical properties and the stress corrosion evaluations the test specimens which were cut transverse to the rolling direction had superior properties when compared to the longitudinal properties.

Mechanical Testing of IN718 Lattice Block Structures

NASA Technical Reports Server (NTRS)

Krause, David L.; Whittenberger, John D.; Kantzos, Pete T.; Hebsur, Mohan G.

2002-01-01

Lattice block construction produces a flat, structurally rigid panel composed of thin ligaments of material arranged in a three-dimensional triangulated truss-like structure. Low-cost methods of producing cast metallic lattice block panels are now available that greatly expand opportunities for using this unique material system in today's high-performance structures. Additional advances are being made in NASA's Ultra Efficient Engine Technology (UEET) program to extend the lattice block concept to superalloy materials. Advantages offered by this combination include high strength, light weight, high stiffness, and elevated temperature capabilities. Recently under UEET, the nickel-based superalloy Inconel 718 (IN718) was investment cast into lattice block panels with great success. To evaluate casting quality and lattice block architecture merit, individual ligaments, and structural subelement specimens were extracted from the panels. Tensile tests, structural compression, and bending strength tests were performed on these specimens. Fatigue testing was also completed for several bend test specimens. This paper first presents metallurgical and optical microscopy analysis of the castings. This is followed by mechanical test results for the tensile ligament tests and the subelement compression and bending strength tests, as well as for the fatigue tests that were performed. These tests generally showed comparable properties to base IN718 with the same heat treatment, and they underscored the benefits offered by lattice block materials. These benefits might be extended with improved architecture such as face sheets.

Thermo-elastic-plastic analysis for elastic component under high temperature fatigue crack growth rate

NASA Astrophysics Data System (ADS)

Ali, Mohammed Ali Nasser

The research project presents a fundamental understanding of the fatigue crack growth mechanisms of AISI 420 martensitic stainless steel, based on the comparison analysis between the theoretical and numerical modelling, incorporating research findings under isothermal fatigue loading for solid cylindrical specimen and the theoretical modelling with the numerical simulation for tubular specimen when subjected to cyclic mechanical loading superimposed by cyclic thermal shock.The experimental part of this research programme studied the fatigue stress-life data for three types of surface conditions specimen and the isothermal stress-controlled fatigue testing at 300 °C - 600 °C temperature range. It is observed that the highest strength is obtained for the polished specimen, while the machined specimen shows lower strength, and the lowest strength is the notched specimen due to the high effect of the stress concentration. The material behaviour at room and high temperatures shows an initial hardening, followed by slow extension until fully plastic saturation then followed by crack initiation and growth eventually reaching the failure of the specimen, resulting from the dynamic strain ageing occurred from the transformation of austenitic microstructure to martensite and also, the nucleation of precipitation at grain boundaries and the incremental temperature increase the fatigue crack growth rate with stress intensity factor however, the crack growth rate at 600 °C test temperature is less than 500 °C because of the creep-fatigue taking place.The theoretical modelling presents the crack growth analysis and stress and strain intensity factor approaches analysed in two case studies based on the addition of thermo-elastic-plastic stresses to the experimental fatigue applied loading. Case study one estimates the thermal stresses superimposed sinusoidal cyclic mechanical stress results in solid cylinder under isothermal fatigue simulation. Case study two estimates the transient thermal stresses superimposed on cyclic mechanical loading results in hollow cylinder under thermal shock in heating case and down shock cooling case. The combination of stress and strain intensity factor theoretical calculations with the experimental output recorded data shows a similar behaviour with increasing temperature, and there is a fair correlation between the profiles at the beginning and then divergence with increasing the crack length. The transient influence of high temperature in case two, giving a very high thermal shock stress as a heating or cooling effects, shifting up the combined stress, when applied a cyclic mechanical load in fraction of seconds, and the reputations of these shocks, causing a fast failure under high thermal shock stress superimposed with mechanical loading.Finally, the numerical modelling analyses three cases studied were solved due to the types of loading and types of specimen geometry by using finite element models constructed through the ANSYS Workbench version 13.0. The first case is a low cyclic fatigue case for a solid cylinder specimen simulated by applying a cyclic mechanical loading. The second is an isothermal fatigue case for solid cylinder specimen simulated by supplying different constant temperatures on the outer surface with cyclic mechanical loading, where the two cases are similar to the experimental tests and the third case, is a thermo-mechanical fatigue for a hollow cylinder model by simulating a thermal up-shock generated due to transient heating on the outer surface of the model or down shock cooling on the inner surface with the cyclic mechanical loading. The results show a good agreement with the experimental data in terms of alternative stress and life in the first case. In case two results show the strain intensity factor is increases with increasing temperature similar to the theoretical solution due to the influence of the modulus of elasticity and the difference in life estimation with the experimental output record is related to the input data made of theoretical physical properties and the experimental stress-life data.

Mechanical and Morphological Effect of Plant Based Antimicrobial Solutions on Maxillofacial Silicone Elastomer.

PubMed

Tetteh, Sophia; Bibb, Richard J; Martin, Simon J

2018-05-30

The objective of this study was to determine the effect of plant based antimicrobial solutions specifically tea tree and Manuka oil on facial silicone elastomers. The purpose of this in vitro study was to evaluate the effect of disinfection with plant extract solution on mechanical properties and morphology on the silicone elastomer. Test specimens were subjected to disinfection using tea tree oil, Manuka oil and the staphylococcus epidermidis bacteria. Furthermore, a procedure duration was used in the disinfection process to simulate up to one year of usage. Over 500 test specimens were fabricated for all tests performed namely hardness, elongation, tensile, tear strength tests, visual inspection and lastly surface characterization using SEM. A repeated measures ANOVA revealed that hardness and elongation at break varied significantly over the time period, whereas this was not observed in the tear and tensile strength parameters of the test samples.

Improved techniques for thermomechanical testing in support of deformation modeling

NASA Technical Reports Server (NTRS)

Castelli, Michael G.; Ellis, John R.

1992-01-01

The feasibility of generating precise thermomechanical deformation data to support constitutive model development was investigated. Here, the requirement is for experimental data that is free from anomalies caused by less than ideal equipment and procedures. A series of exploratory tests conducted on Hastelloy X showed that generally accepted techniques for strain controlled tests were lacking in at least three areas. Specifically, problems were encountered with specimen stability, thermal strain compensation, and temperature/mechanical strain phasing. The source of these difficulties was identified and improved thermomechanical testing techniques to correct them were developed. These goals were achieved by developing improved procedures for measuring and controlling thermal gradients and by designing a specimen specifically for thermomechanical testing. In addition, innovative control strategies were developed to correctly proportion and phase the thermal and mechanical components of strain. Subsequently, the improved techniques were used to generate deformation data for Hastelloy X over the temperature range, 200 to 1000 C.

Impact-induced fracture mechanisms of immiscible PC/ABS (50/50) blends

NASA Astrophysics Data System (ADS)

Machmud, M. N.; Omiya, M.; Inoue, H.; Kishimoto, K.

2018-03-01

This paper presents a study on fracture mechanisms of polycarbonate (PC)/acrylonitrile-butadiene-styrene (ABS) (50/50) blends with different ABS types under a drop weight impact test (DWIT) using a circular sheet specimen. Formation of secondary crack indicated by a stress-whitening layer on the mid-plane of scattered specimens and secondary surface of fracture perpendicular to primary fracture surface were captured under scanning electron microscope (SEM). Although the both blends finally failed in brittle modes, SEM observation showed that their secondary fracture mechanisms were completely different. Observation through the thickness of the etched PC/ABS specimen samples using SEM also clearly showed that PC and ABS were immiscible. The immiscibility between PC and ABS was indicated by presence of their layer structures through the thickness of the blends. It was revealed that layer of ABS structure was influenced by size of rubber particle and this latter parameter then affected microstructure and fracture mechanisms of the blends. Impact-induced fracture mechanisms of the blends due to such microstructures are discussed in this paper. It was also pointed out that the secondary cracking was likely caused by interface delamination between PC and ABS layers in the core due to transverse shear stress generated during the impact test.

PSU/WES Interlaboratory Comparative Methodology Study of an Experimental Cementitious Repository Seal Material. Report 2. Final Results.

DTIC Science & Technology

1982-03-01

meter 25 11.0 Microstructure by SEM 11.1 Introduction In order to correlate observed physical and mechanical properties in cured grout samples, a...studied at the two laboratories has proper physical properties , phase composi- tions, and microstructures for the materials used and ages covered...Scanning Electron Microscope Resolution Test Specimen ( Al -W) D. B. Ballard Research Material 100 SEM Resolution Test Specimen (AI-W)., is an alloy of

Quantifying dynamic mechanical properties of human placenta tissue using optimization techniques with specimen-specific finite-element models.

PubMed

Hu, Jingwen; Klinich, Kathleen D; Miller, Carl S; Nazmi, Giseli; Pearlman, Mark D; Schneider, Lawrence W; Rupp, Jonathan D

2009-11-13

Motor-vehicle crashes are the leading cause of fetal deaths resulting from maternal trauma in the United States, and placental abruption is the most common cause of these deaths. To minimize this injury, new assessment tools, such as crash-test dummies and computational models of pregnant women, are needed to evaluate vehicle restraint systems with respect to reducing the risk of placental abruption. Developing these models requires accurate material properties for tissues in the pregnant abdomen under dynamic loading conditions that can occur in crashes. A method has been developed for determining dynamic material properties of human soft tissues that combines results from uniaxial tensile tests, specimen-specific finite-element models based on laser scans that accurately capture non-uniform tissue-specimen geometry, and optimization techniques. The current study applies this method to characterizing material properties of placental tissue. For 21 placenta specimens tested at a strain rate of 12/s, the mean failure strain is 0.472+/-0.097 and the mean failure stress is 34.80+/-12.62 kPa. A first-order Ogden material model with ground-state shear modulus (mu) of 23.97+/-5.52 kPa and exponent (alpha(1)) of 3.66+/-1.90 best fits the test results. The new method provides a nearly 40% error reduction (p<0.001) compared to traditional curve-fitting methods by considering detailed specimen geometry, loading conditions, and dynamic effects from high-speed loading. The proposed method can be applied to determine mechanical properties of other soft biological tissues.

Flexural strength and failure modes of layered ceramic structures.

PubMed

Borba, Márcia; de Araújo, Maico D; de Lima, Erick; Yoshimura, Humberto N; Cesar, Paulo F; Griggs, Jason A; Della Bona, Alvaro

2011-12-01

To evaluate the effect of the specimen design on the flexural strength (σ(f)) and failure mode of ceramic structures, testing the hypothesis that the ceramic material under tension controls the mechanical performance of the structure. Three ceramics used as framework materials for fixed partial dentures (YZ--Vita In-Ceram YZ; IZ--Vita In-Ceram Zirconia; AL--Vita In-Ceram AL) and two veneering porcelains (VM7 and VM9) were studied. Bar-shaped specimens were produced in three different designs (n=10): monolithic, two layers (porcelain-framework) and three layers (TRI) (porcelain-framework-porcelain). Specimens were tested for three-point flexural strength at 1MPa/s in 37°C artificial saliva. For bi-layered design, the specimens were tested in both conditions: with porcelain (PT) or framework ceramic (FT) layer under tension. Fracture surfaces were analyzed using stereomicroscope and scanning electron microscopy (SEM). Young's modulus (E) and Poisson's ratio (ν) were determined using ultrasonic pulse-echo method. Results were statistically analyzed by Kruskal-Wallis and Student-Newman-Keuls tests. Except for VM7 and VM9, significant differences were observed for E values among the materials. YZ showed the highest ν value followed by IZ and AL. YZ presented the highest σ(f). There was no statistical difference in the σ(f) value between IZ and IZ-FT and between AL and AL-FT. σ(f) values for YZ-PT, IZ-PT, IZ-TRI, AL-PT, AL-TRI were similar to the results obtained for VM7 and VM9. Two types of fracture mode were identified: total and partial failure. The mechanical performance of the specimens was determined by the material under tension during testing, confirming the study hypothesis. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Acoustic emission from trabecular bone during mechanical testing: the effect of osteoporosis and osteoarthritis.

PubMed

Leichter, I; Bivas, A; Margulies, J Y; Roman, I; Simkin, A

1990-01-01

This study examines the relation between the nature of acoustic emission signals emitted from cancellous bone under compression and the mechanical properties of the tissue. The examined bone specimens were taken from 12 normal, 31 osteoporotic and six osteoarthritic femoral heads. The mechanical behaviour of the osteoporotic bone specimens was found to be significantly different from that of the normal specimens both in the pre-yield and post-yield ranges. In the osteoarthritic bones only the elastic behaviour was significantly different. The rates of acoustic events before yield and beyond it were found to be significantly higher both in the osteoporotic and osteoarthritic bone specimens. The average peak amplitude of the signals was also significantly higher in the diseased bones. Stepwise regression analysis showed that a combination of the acoustic emission parameters could significantly predict some mechanical properties of the bone. The energy absorbed during compression and the ultimate compressive stress of the specimens could be estimated from the rate of pre-yield acoustic events, the average amplitude of the signals and the rate of post-yield events. However, the explanation power of the acoustic emission parameters was only moderate. The nature of acoustic emission signals was thus demonstrated to be a potential tool for assessing bone quality.

The Stress Corrosion Resistance and the Cryogenic Temperature Mechanical Behavior of 18-3 Mn (Nitronic 33) Stainless Steel Parent and Welded Material

NASA Technical Reports Server (NTRS)

Montano, J. W.

1976-01-01

The ambient and cryogenic temperature mechanical properties and the ambient temperature stress corrosion results of 18-3 Mn (Nitronic 33)stainless steel, longitudinal and transverse, as received and as welded (TIG) material specimens manufactured from 0.063 inch thick sheet material, were described. The tensile test results indicate an increase in ultimate tensile and yield strengths with decreasing temperature. The elongation remained fairly constant to -200 F, but below that temperature the elongation decreased to less than 6.0% at liquid hydrogen temperature. The notched tensile strength (NTS) for the parent metal increased with decreasing temperature to liquid nitrogen temperature. Below -320 F the NTS decreased rapidly. The notched/unnotched (N/U) tensile ratio of the parent material specimens remained above 0.9 from ambient to -200 F, and decreased to approximately 0.65 and 0.62, respectively, for the longitudinal and transverse directions at liquid hydrogen temperature. After 180 days of testing, only those specimens exposed to the salt spray indicated pitting and some degradation of mechanical properties.

Development of a multi-cycle shear-compression testing for the modeling of severe plastic deformation

NASA Astrophysics Data System (ADS)

Pesin, A.; Pustovoytov, D.; Lokotunina, N.

2017-12-01

The mechanism of severe plastic deformation comes from very significant shear strain. Shear-compression testing of materials is complicated by the fact that a state of large equivalent strain with dominant shear strain is not easily achievable. This paper presents the novel technique of laboratory simulation of severe plastic deformation by multi-cycle shear-compression testing at room temperature with equivalent strain e=1…5. The specimen consisted of a parallelepiped having an inclined gauge section created by two diametrically opposed semi-circular slots which were machined at 45°. Height of the specimen was 50 mm, section dimensions were 25×25 mm, gauge thickness was 5.0 mm and gauge width was 6.0 mm. The specimen provided dominant shear strain in an inclined gauge-section. The level of shear strain and equivalent strain was controlled through adjustment of the height reduction of the specimen, load application direction and number of cycles of shear-compression. Aluminium alloy Al-6.2Mg-0.7Mn was used as a material for specimen. FE simulation and analysis of the stress-strain state were performed. The microstructure of the specimen after multi-cycle shear-compression testing with equivalent strain e=1…5 was examined by optical and scanning electron microscope.

Effect of hydrogen on void initiation in tensile test of carbon steel JIS-S25C

NASA Astrophysics Data System (ADS)

Sugawa, S.; Tsutsumi, N.; Oda, K.

2018-06-01

In order to investigate the effect of hydrogen on tensile fracture mechanism of a carbon steel, tensile tests were conducted. Pre-strain specimens (0%, 5% and 10%) were used to study the effect of hydrogen content, since saturated hydrogen content in specimens increases in increasing dislocation density. The tensile strength and the yield stress of hydrogen specimens were almost the same as uncharged. In contrast, the reduction of area of hydrogen charged specimens was smaller than that of uncharged. To reveal the reasons of decrease of the reduction of area, the fracture surface and longitudinal cross section near the fracture surface were observed. On the fracture surface of uncharged specimens, only dimples were observed. On the other hand, dimples and flat fracture surface were observed on the fracture surface of hydrogen charged. On the longitudinal cross section of hydrogen charged specimens, many voids were observed compared to uncharged. From these observations, it is showed that hydrogen gives a rise to the increase of voids and the hydrogen charged specimens break without sufficient necking, thus hydrogen makes the reduction of area smaller.

Correlating Scatter in Fatigue Life with Fracture Mechanisms in Forged Ti-6242Si Alloy

NASA Astrophysics Data System (ADS)

Sinha, V.; Pilchak, A. L.; Jha, S. K.; Porter, W. J.; John, R.; Larsen, J. M.

2018-04-01

Unlike the quasi-static mechanical properties, such as strength and ductility, fatigue life can vary significantly (by an order of magnitude or more) for nominally identical material and test conditions in many materials, including Ti-alloys. This makes life prediction and management more challenging for components that are subjected to cyclic loading in service. The differences in fracture mechanisms can cause the scatter in fatigue life. In this study, the fatigue fracture mechanisms were investigated in a forged near- α titanium alloy, Ti-6Al-2Sn-4Zr-2Mo-0.1Si, which had been tested under a condition that resulted in life variations by more than an order of magnitude. The crack-initiation and small crack growth processes, including their contributions to fatigue life variability, were elucidated via quantitative characterization of fatigue fracture surfaces. Combining the results from quantitative tilt fractography and electron backscatter diffraction, crystallography of crack-initiating and neighboring facets on the fracture surface was determined. Cracks initiated on the surface for both the shortest and the longest life specimens. The facet plane in the crack-initiating grain was aligned with the basal plane of a primary α grain for both the specimens. The facet planes in grains neighboring the crack-initiating grain were also closely aligned with the basal plane for the shortest life specimen, whereas the facet planes in the neighboring grains were significantly misoriented from the basal plane for the longest life specimen. The difference in the extent of cracking along the basal plane can explain the difference in fatigue life of specimens at the opposite ends of scatter band.

Taylor Impact Tests and Simulations on PBX 9501

NASA Astrophysics Data System (ADS)

Clements, Brad; Thompson, Darla G.; Luscher, D. J.; Deluca, Racci

2011-06-01

Taylor impact tests have been conducted previously on plastic bonded explosives (PBXs) to characterize the stress state of these materials as they impact smooth and flat steel anvil surfaces at speeds of ~100m/s (i.e. Christopher, et al, 11th Detonation Symposium). In 2003, C. Liu and R. Ellis (unpublished, Los Alamos National Laboratory) performed Taylor tests on PBX 9501 up to speeds of 115 m/s, capturing impact images. In the work presented here, we have extended these tests to velocities of 200 m/s using a composite-lined gun barrel and no specimen sabot. Specimen images are used to validate the thermo-mechanical constitutive model ViscoSCRAM. ViscoSCRAM has been parameterized for PBX 9501 in uniaxial stress configurations. Simulating Taylor impact experiments tests the model in situations undergoing extreme damage. In addition, experimental variations to specimen confinement and friction are introduced in an attempt to establish ignition thresholds in this velocity regime.

An in vitro biomechanical comparison of two fixation methods for transverse osteotomies of the medial proximal forelimb sesamoid bones in horses.

PubMed

Wilson, D A; Keegan, K G; Carson, W L

1999-01-01

This study compared the mechanical properties of the normal intact suspensory apparatus and two methods of fixation for repair of transverse, midbody fractures of the proximal sesamoid bones of adult horses: transfixation wiring (TW) and screws placed in lag fashion (LS). An in vitro, paired study using equine cadaver limbs mounted in a loading apparatus was used to test the mechanical properties of TW and LS. Seventeen paired (13 repaired, 4 normal) equine cadaver limbs consisting of the suspensory apparatus third metacarpal bone, and first and second phalanges. The two methods of repair and normal intact specimens were evaluated in single cycle-to-failure loading. Yield failure was defined to occur at the first notable discontinuity (>50 N) in the load-displacement curve, the first visible failure as evident on the videotape, or a change in the slope of the moment-fetlock angle curve. Ultimate failure was defined to occur at the highest load resisted by the specimen. Corresponding resultant force and force per kg of body weight on the suspensory apparatus, fetlock joint moment, and angle of fetlock dorsiflexion were calculated by use of specimen dimensions and applied load. These were compared along with specimen stiffness, and ram displacement. Load on the suspensory apparatus, load on the suspensory apparatus per kg of body weight, moment, applied load, and angle of fetlock dorsiflexion at yield failure were significantly greater for the TW-repaired than for the LS-repaired specimens. A 3 to 5 mm gap was observed before yield failure in most TW-repaired osteotomies. Transfixation wiring provided greater strength to yield failure than screws placed in lag fashion in single cycle load-to-failure mechanical testing of repaired transverse osteotomized specimens of the medial proximal forelimb sesamoid bone.

The Effects of Fiber Orientation and Adhesives on Tensile Properties of Carbon Fiber Reinforced Polymer Matrix Composite with Embedded Nickel-Titanium Shape Memory Alloys

NASA Technical Reports Server (NTRS)

Quade, Derek J.; Jana, Sadhan C.; Morscher, Gregory N.; Kannan, Manigandan; McCorkle, Linda S.

2017-01-01

Nickel-titanium (NiTi) shape memory alloy (SMA) sections were embedded within carbon fiber reinforced polymer matrix composite (CFRPPMC) laminates and their tensile properties were evaluated with simultaneous monitoring of modal acoustic emissions. The test specimens were fabricated in three different layup configurations and two different thin film adhesives were applied to bond the SMA with the PMC. A trio of acoustic sensors were attached to the specimens during tensile testing to monitor the modal acoustic emission (AE) as the materials experienced mechanical failure. The values of ultimate tensile strengths, strains, and moduli were obtained. Cumulative AE energy of events and specimen failure location were determined. In conjunction, optical and scanning electron microscopy techniques were used to examine the break areas of the specimens. The analysis of AE data revealed failure locations within the specimens which were validated from the microscopic images. The placement of 90 deg plies in the outer ply gave the strongest acoustic signals during break as well as the cleanest break of the samples tested. Overlapping 0 deg ply layers surrounding the SMA was found to be the best scenario to prevent failure of the specimen itself.

Experimental study on mix proportion of fiber reinforced cementitious composites

NASA Astrophysics Data System (ADS)

Jia, Yi; Zhao, Renda; Liao, Ping; Li, Fuhai; Yuan, Yuan; Zhou, Shuang

2017-10-01

To study the mechanical property of fiber reinforced cementations composites influenced by the fiber length, quartz sand diameter, matrix of water cement ratio, volume fraction of fiber and magnesium acrylate solution. Several 40×40×160 mm standard test specimens, "8" specimens and long "8" specimens and 21 groups of fiber concrete specimens were fabricated. The flexural, compressive and uniaxial tensile strength were tested by using the bending resistance, compression resistance and electronic universal testing machine. The results show that flexural and compressive strength of fiber reinforced cementations composites increases along with the increase of quartz sand diameter, with the growth of the PVA fiber length increases; When the water-binder ratio is 0.25 and powder-binder ratio is 0.3, the PVA fiber content is 1.5% of the mass of cementations materials, there is a phenomenon of strain hardening; The addition of magnesium acrylate solution reduces the tensile strength of PVA fiber reinforced cementations composites, the tensile strength of the specimens in the curing age of 7d is decreased by about 21% and the specimens in curing age of 28d is decreased by more than 50%.

Compressive behavior of laminated neoprene bridge bearing pads under thermal aging condition

NASA Astrophysics Data System (ADS)

Jun, Xie; Zhang, Yannian; Shan, Chunhong

2017-10-01

The present study was conducted to obtain a better understanding of the variation rule of mechanical properties of laminated neoprene bridge bearing pads under thermal aging condition using compression tests. A total of 5 specimens were processed in a high-temperature chamber. After that, the specimens were tested subjected to axial load. The parameter mainly considered time of thermal aging processing for specimens. The results of compression tests show that the specimens after thermal aging processing are more probably brittle failure than the standard specimen. Moreover, the exposure of steel plate, cracks and other failure phenomena are more serious than the standard specimen. The compressive capacity, ultimate compressive strength, compressive elastic modulus of the laminated neoprene bridge bearing pads decreased dramatically with the increasing in the aging time of thermal aging processing. The attenuation trends of ultimate compressive strength, compressive elastic modulus of laminated neoprene bridge bearing pads under thermal aging condition accord with power function. The attenuation models are acquired by regressing data of experiment with the least square method. The attenuation models conform to reality well which shows that this model is applicable and has vast prospect in assessing the performance of laminated neoprene bridge bearing pads under thermal aging condition.

Designing a biomechanics investigation: choosing the right model.

PubMed

Olson, Steven A; Marsh, J Lawrence; Anderson, Donald D; Latta Pe, Loren L

2012-12-01

Physical testing is commonly performed to answer important biomechanical questions in the treatment of patients with fractures and other orthopaedic conditions. However, a variety of mistakes that are made in performing such investigations can severely limit their impact. The goal of this article is to discuss important aspects of study design to consider when planning for biomechanical investigations so that the studies can provide maximal benefit to the field. The best mechanical investigations begin with a good research question, one that comes out of patient care experience, is clearly defined, and can be stated concisely. The first practical issue to be considered is often choosing the type of physical specimens to be tested to address the research question. A related issue involves determining how many specimens will be needed to answer the posed mechanical question. Cadavers are generally still the closest to the actual clinical situation, but they are limited by interspecimen variability, which often requires a matched pair design that can address only one question. Simulated bone specimens limit variability and can replicate normal and osteoporotic bone. In planning the physical testing, the critical mechanical variables involved in answering the research question must be identified and due consideration given to deciding how best to measure them. Another important issue that arises relates to whether or not single static loadings will suffice in the testing (eg, to study construct stiffness) or whether cyclic dynamic testing is necessary (eg, to study late failure likely attributable to fatigue). To summarize, experimental design should be carefully planned before initiating mechanical testing. Sample size calculations should be performed to ensure adequate power and that clinically relevant differences can be detected. This pregame analysis can save significant time and cost and greatly increase the likelihood that the results will advance knowledge.

Acoustic emission: A useful tool for damage evaluation in composite materials

NASA Astrophysics Data System (ADS)

Mouzakis, Dionysios E.; Dimogianopoulos, Dimitrios G.

2018-02-01

High performance composites for aviation-related structures are prone to constant aging by environmental agents. Previous data from our work reported on the stiffening behaviour of glass fibre polyester composites used in the manufacturing of wind turbine blades. Airplanes from such composites are already on service nowadays. This justifies the detailed study of the exposure of high performance materials to environmental conditions such as varying temperature, humidity, ultraviolet radiation, in order to assess the impact of these important aging factors on their mechanical behaviour. The dramatic changes in the dynamic mechanical response of polymer matrix carbon fibre composites upon exposure to acceleration aging has been assessed in the present study. In order to assess the synergistic effect action of temperature and humidity on composites subjected to changes of temperature from -35 to +40 °C and humidity variations from <10% to 95% RH (non-condensing) specimens were stored in a climatic chamber for 60 days. Conditions were cycled, as if actual flight cycles of 3-4 hours per flight, were to be simulated. Dynamic mechanical analysis tests were performed in three point bending mode. Scanning of frequency and temperature were performed in order to determine both the viscoelastic response as well as the time-dependent behaviour of the aged materials. All tests were run both for aged and pristine materials for comparison purposes. Three point bending testing was performed in both static as well as in Dynamic mechanical analysis, for a range of temperatures and frequencies. Acoustic Emission damage detection was also performed during the three point bending test both in static and dynamic mode. The aged materials had gained in dynamic stiffness. In addition, that, the gain in the storage moduli, was accompanied by a decrease in the material damping ability, as determined by the tanδ parameter. In the final stages of the study, impact testing was performed on both pristine and aged specimens. The experimentally recorded force/time signals were utilized for concluding on the specimens' condition, by means of signal based damage detection methodologies. Effort was invested in utilizing signal analysis in order to get comparative aging-related information on the tested specimens in order to ultimately validate results of mechanical testing.

Thermomechanical Testing and Microstructural Development of Class L Steel Wheel Alloy

DOT National Transportation Integrated Search

1994-03-01

Macrostructure, microstructure, and quantitative metallographic analysis is conducted on Association of American Railroads Class L wheel steel specimens tested in a Gleeble 1500 under combined mechanical compression and resistance heating to temperat...

Calcified lesion modeling for excimer laser ablation

NASA Astrophysics Data System (ADS)

Scott, Holly A.; Archuleta, Andrew; Splinter, Robert

2009-06-01

Objective: Develop a representative calcium target model to evaluate penetration of calcified plaque lesions during atherectomy procedures using 308 nm Excimer laser ablation. Materials and Methods: An in-vitro model representing human calcified plaque was analyzed using Plaster-of-Paris and cement based composite materials as well as a fibrinogen model. The materials were tested for mechanical consistency. The most likely candidate(s) resulting from initial mechanical and chemical screening was submitted for ablation testing. The penetration rate of specific multi-fiber catheter designs and a single fiber probe was obtained and compared to that in human cadaver calcified plaque. The effects of lasing parameters and catheter tip design on penetration speed in a representative calcified model were verified against the results in human cadaver specimens. Results: In Plaster of Paris, the best penetration was obtained using the single fiber tip configuration operating at 100 Fluence, 120 Hz. Calcified human lesions are twice as hard, twice as elastic as and much more complex than Plaster of Paris. Penetration of human calcified specimens was highly inconsistent and varied significantly from specimen to specimen and within individual specimens. Conclusions: Although Plaster of Paris demonstrated predictable increases in penetration with higher energy density and repetition rate, it can not be considered a totally representative laser ablation model for calcified lesions. This is in part due to the more heterogeneous nature and higher density composition of cadaver intravascular human calcified occlusions. Further testing will require a more representative model of human calcified lesions.

Effects of the Heterogeneity in the Electron Beam Welded Joint on Mechanical Properties of Ti6Al4V Alloy

NASA Astrophysics Data System (ADS)

Liu, Jing; Gao, Xiao-Long; Zhang, Lin-Jie; Zhang, Jian-Xun

2015-01-01

The aim of this investigation was to evaluate the effect of microstructure heterogeneity on the tensile and low cycle fatigue properties of electron beam welded (EBW) Ti6Al4V sheets. To achieve this goal, the tensile and low cycle fatigue property in the EBW joints and base metal (BM) specimens is compared. During the tensile testing, digital image correlation technology was used to measure the plastic strain field evolution within the specimens. The experimental results showed that the tensile ductility and low cycle fatigue strength of EBW joints are lower than that of BM specimens, mainly because of the effect of microstructure heterogeneity of the welded joint. Moreover, the EBW joints exhibit the cyclic hardening behavior during low fatigue process, while BM specimens exhibit the cyclic softening behavior. Compared with the BM specimens with uniform microstructure, the heterogeneity of microstructure in the EBW joint is found to decrease the mechanical properties of welded joint.

A review of the effect of a/W ratio on fracture toughness (II) —experimental investigation in LEFM

NASA Astrophysics Data System (ADS)

Li, Qing-Fen; Fu, Yu-Dong; Xu, Xiao-Xue

2005-06-01

In part I of this series, experimental investigation in EPFM (elastic-plastic fracture mechanics) had been discussed. In this paper, experimental investigation in LEFM (linear elastic fracture mechanics) is given. Fracture toughness tests had been carried out on three different strength steels, using both through-cracked specimens with different a/W ratio and semi-elliptical cracked specimens with variable crack size and shape. Results show that the fracture toughness K IC increases with decreasing a/W when a/W<0.3 for three-point-bend specimens, and that for a/W>0.3, it is independent of a/W. Shallow crack specimens, both through-cracked and surface-cracked, gave markedly higher values than deeply notched specimens. However, the effect of crack shape on fracture toughness is negligible. Results also show that the LEFM approach to fracture is not tenable for design stresses where a c is often very small, far less than 2.5(K IC/σ y )2.

The effect of collagen crosslinking on the biphasic poroviscoelastic cartilage properties determined from a semi-automated microindentation protocol for stress relaxation.

PubMed

McGann, Megan E; Bonitsky, Craig M; Ovaert, Timothy C; Wagner, Diane R

2014-06-01

Given the important role of the collagenous structure in cartilage mechanics, there is considerable interest in the relationship between collagen crosslinking and the mechanical behavior of the cartilage matrix. While crosslink-induced alterations to the elastic modulus of cartilage have been described, changes to time-dependent behavior have not yet been determined. The objective of the study was to quantify changes to cartilage material properties, including viscoelastic coefficients, with crosslinking via indentation. To accomplish this, a semi-autonomous microindentation stress relaxation protocol was first developed, validated and then applied to cartilage specimens before and after crosslinking. The change in mechanical properties with crosslinking was analyzed both in the unloading portions of the test via the Oliver-Pharr method and in the holding portion with an inverse iterative finite element model that represented cartilage as a biphasic poroviscoelastic material. Although both techniques suggested a similar increase in equilibrium modulus in the crosslinked specimens as compared to the controls, distinct differences in the control specimens were apparent, suggesting that the two different techniques may be capturing different aspects of the material behavior. No differences in time-dependent properties were observed between the crosslinked and the control specimens. These results give further insight into the effects of crosslinking in cartilage mechanical behavior. Additionally, the microindentation stress relaxation protocol may enable increased automation for high-throughput testing. Copyright © 2014 Elsevier Ltd. All rights reserved.

Thermal barrier coating life prediction model development, phase 2

NASA Technical Reports Server (NTRS)

Meier, Susan Manning; Sheffler, Keith D.; Nissley, David M.

1991-01-01

The objective of this program was to generate a life prediction model for electron-beam-physical vapor deposited (EB-PVD) zirconia thermal barrier coating (TBC) on gas turbine engine components. Specific activities involved in development of the EB-PVD life prediction model included measurement of EB-PVD ceramic physical and mechanical properties and adherence strength, measurement of the thermally grown oxide (TGO) growth kinetics, generation of quantitative cyclic thermal spallation life data, and development of a spallation life prediction model. Life data useful for model development was obtained by exposing instrumented, EB-PVD ceramic coated cylindrical specimens in a jet fueled burner rig. Monotonic compression and tensile mechanical tests and physical property tests were conducted to obtain the EB-PVD ceramic behavior required for burner rig specimen analysis. As part of that effort, a nonlinear constitutive model was developed for the EB-PVD ceramic. Spallation failure of the EB-PVD TBC system consistently occurred at the TGO-metal interface. Calculated out-of-plane stresses were a small fraction of that required to statically fail the TGO. Thus, EB-PVD spallation was attributed to the interfacial cracking caused by in-plane TGO strains. Since TGO mechanical properties were not measured in this program, calculation of the burner rig specimen TGO in-plane strains was performed by using alumina properties. A life model based on maximum in-plane TGO tensile mechanical strain and TGO thickness correlated the burner rig specimen EB-PVD ceramic spallation lives within a factor of about plus or minus 2X.

Closed form expressions for crack mouth displacements and stress intensity factors for chevron notched short bar and short rod specimens based on experimental compliance measurements

NASA Technical Reports Server (NTRS)

Bubsey, R. T.; Orange, T. W.; Pierce, W. S.; Shannon, J. L., Jr.

1992-01-01

A set of equations are presented describing certain fracture mechanics parameters for chevron notch bar and rod specimens. They are developed by fitting compliance calibration data reported earlier. The equations present the various parameters in their most useful forms. The data encompass the entire range of the specimen geometries most commonly used. Their use will facilitate the testing and analysis of brittle metals, ceramics, and glasses.

Creep rupture testing of carbon fiber-reinforced epoxy composites

NASA Astrophysics Data System (ADS)

Burton, Kathryn Anne

Carbon fiber is becoming more prevalent in everyday life. As such, it is necessary to have a thorough understanding of, not solely general mechanical properties, but of long-term material behavior. Creep rupture testing of carbon fiber is very difficult due to high strength and low strain to rupture properties. Past efforts have included testing upon strands, single tows and overwrapped pressure vessels. In this study, 1 inch wide, [0°/90°]s laminated composite specimens were constructed from fabric supplied by T.D. Williamson Inc. Specimen fabrication methods and gripping techniques were investigated and a method was developed to collect long term creep rupture behavior data. An Instron 1321 servo-hydraulic material testing machine was used to execute static strength and short term creep rupture tests. A hanging dead-weight apparatus was designed to perform long-term creep rupture testing. The testing apparatus, specimens, and specimen grips functioned well. Collected data exhibited a power law distribution and therefore, a linear trend upon a log strength-log time plot. Statistical analysis indicated the material exhibited slow degradation behavior, similar to previous studies, and could maintain a 50 year carrying capacity at 62% of static strength, approximately 45.7 ksi.

Effect of G-Coat Plus on the mechanical properties of glass-ionomer cements.

PubMed

Bagheri, R; Taha, N A; Azar, M R; Burrow, M F

2013-12-01

Although various mechanical properties of tooth-coloured materials have been described, little data have been published on the effect of ageing and G-Coat Plus on the hardness and strength of the glass-ionomer cements (GICs). Specimens were prepared from one polyacid-modified resin composite (PAMRC; Freedom, SDI), one resin-modified glass-ionomer cement; (RM-GIC; Fuji II LC, GC), and one conventional glass-ionomer cement; (GIC; Fuji IX, GC). GIC and RM-GIC were tested both with and without applying G-Coat Plus (GC). Specimens were conditioned in 37 °C distilled water for either 24 hours, four and eight weeks. Half the specimens were subjected to a shear punch test using a universal testing machine; the remaining half was subjected to Vickers Hardness test. Data analysis showed that the hardness and shear punch values were material dependent. The hardness and shear punch of the PAMRC was the highest and GIC the lowest. Applying the G-Coat Plus was associated with a significant decrease in the hardness of the materials but increase in the shear punch strength after four and eight weeks. The mechanical properties of the restorative materials were affected by applying G-Coat Plus and distilled water immersion over time. The PAMRC was significantly stronger and harder than the RM-GIC or GIC. © 2013 Australian Dental Association.

Analysis on weathering characteristics of volcanic rocks in Dokdo, Korea based on accelerated weatehring experiments

NASA Astrophysics Data System (ADS)

Woo, Ik; Song, Won-Kyong; Kim, Bok-Chul; Kang, Jinseok

2010-05-01

Dokdo consists of small volcanic islands located in the southern part of the East Sea. Accelerated weathering tests was performed to examine the physico-mechanical characteristics of volcanic rocks in Dokdo. Rock core specimens of trachyandesite, andesitic dyke and ash tuff were prepared, and double soxhlet extractors(DSE) and peristatic pumps were used for accelerating the weathering processes. The DSE was designed to perform cyclic leaching tests for rock core specimen using distilled water at seventy degrees centigrade. The core specimens which are classified according to pre-test weathering grades placed in the lower part of the DSE, and periodically exposed to hot distilled water at every ninety minutes. On the other hand the peristatic pumps were utilized to induce leaching by distilled or brine water at normal temperature. The physico-mechanical property changes including rock surface appearance, microscopic structure and rock strength were analyzed with the results obtained from both experiments performed for 120 days. The conducted research in this study have shown that the methodologies of artificial weathering experiments have strong capability to understand the weathering characteristics of the rocks effectively.

Theoretical Analysis of Pore Pressure Diffusion in Some Basic Rock Mechanics Experiments

NASA Astrophysics Data System (ADS)

Braun, Philipp; Ghabezloo, Siavash; Delage, Pierre; Sulem, Jean; Conil, Nathalie

2018-05-01

Non-homogeneity of the pore pressure field in a specimen is an issue for characterization of the thermo-poromechanical behaviour of low-permeability geomaterials, as in the case of the Callovo-Oxfordian claystone ( k < 10-20 m2), a possible host rock for deep radioactive waste disposal in France. In tests with drained boundary conditions, excess pore pressure can result in significant errors in the measurement of material parameters. Analytical solutions are presented for the change in time of the pore pressure field in a specimen submitted to various loading paths and different rates. The pore pressure field in mechanical and thermal undrained tests is simulated with a 1D finite difference model taking into account the dead volume of the drainage system of the triaxial cell connected to the specimen. These solutions provide a simple and efficient tool for the estimation of the conditions that must hold for reliable determination of material parameters and for optimization of various test conditions to minimize the experimental duration, while keeping the measurement errors at an acceptable level.

Fabrication and Characterization of SMA Hybrid Composites

NASA Technical Reports Server (NTRS)

Turner, Travis L.; Lach, Cynthia L.; Cano, Robert J.

2001-01-01

Results from an effort to fabrication shape memory alloy hybrid composite (SMAHC) test specimens and characterize the material system are presented in this study. The SMAHC specimens are conventional composite structures with an embedded SMA constituent. The fabrication and characterization work was undertaken to better understand the mechanics of the material system, address fabrication issues cited in the literature, and provide specimens for experimental validation of a recently developed thermomechanical model for SMAHC structures. Processes and hardware developed for fabrication of the SMAHC specimens are described. Fabrication of a SMA14C laminate with quasi-isotropic lamination and ribbon-type Nitinol actuators embedded in the 0' layers is presented. Beam specimens are machined from the laminate and are the focus of recent work, but the processes and hardware are readily extensible to more practical structures. Results of thermomechanical property testing on the composite matrix and Nitinol ribbon are presented. Test results from the Nitinol include stress-strain behavior, modulus versus temperature. and constrained recovery stress versus temperature and thermal cycle. Complex thermomechanical behaviors of the Nitinol and composite matrix are demonstrated, which have significant implications for modeling of SMAHC structures.

Tensile and compressive stress-strain behavior of heat treated boron-aluminum

NASA Technical Reports Server (NTRS)

Kennedy, J. M.; Tenney, D. R.; Herakovich, C. T.

1978-01-01

An experimental study was conducted to assess the effects of heat treatment and cyclic mechanical loading on the tensile and compressive stress-strain behavior of six boron-aluminum composites having different laminate orientations and being subjected to different heat treatments. The heat treatments were as-fabricated, T6, and T6N consisting of T6 treatment followed by cryogenic quench in liquid nitrogen prior to testing. All laminates were tested in monotonic and cyclic compression, while the tensile-test data are taken from the literature for comparison purposes. It is shown that the linear elastic range of the T6- and T6N-condition specimens is larger than that of the as-fabricated specimens, and that cyclic loading in tension or compression strain hardens the specimens and extends the linear elastic range. For laminates containing 0-deg plies, the stress-strain behavior upon unloading is found to be nonlinear, whereas the other laminates exhibit a linear behavior upon unloading. Specimens in the T6 and T6N conditions show higher strain hardening than the as-fabricated specimens.

Heavy-section steel irradiation program. Progress report, April 1996--September 1996

DOE Office of Scientific and Technical Information (OSTI.GOV)

Corwin, W.R.

1997-09-01

The Heavy-Section Steel Irradiation Program was established to quantitatively assess the effects of neutron irradiation on the material behavior of typical reactor pressure vessel (RPV) steels. During this period, fracture mechanics testing of specimens of the irradiated low upper shelf (LUS) weld were completed and analyses performed. Heat treatment of five RPV plate materials was initiated to examine phosphorus segregation effects on the fracture toughness of the heat affected zone of welds. Initial results show that all five materials exhibited very large prior austenite grain sizes as a consequence of the initial heat treatment. Irradiated and annealed specimens of LUSmore » weld material were tested and analyzed. Four sets of Charpy V-notch (CVN) specimens were aged at various temperatures and tested to examine the reason for overrecovery of upper shelf energy that has been observed. Molecular dynamics cascade simulations were extended to 40 keV and have provided information representative of most of the fast neutron spectrum. Investigations of the correlation between microstructural changes and hardness changes in irradiated model alloys was also completed. Preliminary planning for test specimen machining for the Japan Power Development Reactor was completed. A database of Charpy impact and fracture toughness data for RPV materials that have been tested in the unirradiated and irradiated conditions is being assembled and analyzed. Weld metal appears to have similar CVN and fracture toughness transition temperature shifts, whereas the fracture toughness shifts are greater than CVN shifts for base metals. Draft subcontractor reports on precracked cylindrical tensile specimens were completed, reviewed, and are being revised. Testing on precracked CVN specimens, both quasi-static and dynamic, was evaluated. Additionally, testing of compact specimens was initiated as an experimental comparison of constraint limitations. 16 figs., 2 tabs.« less

On the mechanical characteristics of a self-setting calcium phosphate cement.

PubMed

Bimis, A; Canal, L P; Karalekas, D; Botsis, J

2017-04-01

To perform a mechanical characterization of a self-setting calcium phosphate cement in function of the immersion time in Ringer solution. Specimens of self-setting calcium phosphate cement were prepared from pure α-TCP powder. The residual strains developed during hardening stage were monitored using an embedded fiber Bragg grating sensor. Additionally, the evolution of the elastic modulus was obtained for the same time period by conducting low-load indentation tests. Micro-computed tomography as well as microscope-assisted inspections were employed to evaluate the porosity in the specimens. Moreover, diametral compression tests were conducted in wet and dried specimens to characterize the material strength. The volume of the estimated porosity and absorbed fluid mass, during the first few minutes of the material's exposure in a wet environment, coincide. The immersion in Ringer solution lead to a noticeable increase in the moduli values. The critical value of stresses obtained from the diametral compression tests were combined with the data from uniaxial compression tests, to suggest a Mohr-Coulomb failure criterion. This study presents different techniques to characterize a self-setting calcium phosphate cement and provides experimental data on porosity, mechanical properties and failure. The investigated material possessed an open porosity at its dried state with negligible residual strains and its Young's modulus, obtained from micro-indentation tests, increased with hardening time. The failure loci may be described by a Mohr-Coulomb criterion, characteristic of soil and rock materials. Copyright © 2017 Elsevier Ltd. All rights reserved.

Graphs of Soil Mechanics Tests in Orbit

NASA Technical Reports Server (NTRS)

1998-01-01

On STS-89, three Mechanics of Granular Materials (MGM) test cells were subjected to five cycles of compression and relief (left) and three were subjected to shorter displacement cycles that simulate motion during an earthquake (right). In the compression/relief tests, the sand particles rearranged themselves and slightly re-expanded the column during relief. In the short displacement tests, the specimen's resistance to compression decreases, even though the displacement remains the same. The specimens were cycled up to 100 times or until the resistive force was less than 1% that of the previous cycle. Sand and soil grains have faces that can cause friction as they roll and slide against each other, or even cause sticking and form small voids between grains. This complex behavior can cause soil to behave like a liquid under certain conditions such as earthquakes or when powders are handled in industrial processes. Mechanics of Granular Materials (MGM) experiments aboard the Space Shuttle use the microgravity of space to simulate this behavior under conditons that carnot be achieved in laboratory tests on Earth. MGM is shedding light on the behavior of fine-grain materials under low effective stresses. Applications include earthquake engineering, granular flow technologies (such as powder feed systems for pharmaceuticals and fertilizers), and terrestrial and planetary geology. Nine MGM specimens have flown on two Space Shuttle flights. Another three are scheduled to fly on STS-107. The principal investigator is Stein Sture of the University of Colorado at Boulder. Credit: NASA/Marshall Space Flight Center (MSFC)

Acoustic emission and acousto-ultrasonic signature analysis of failure mechanisms in carbon fiber reinforced polymer materials

NASA Astrophysics Data System (ADS)

Carey, Shawn Allen

Fiber reinforced polymer composite materials, particularly carbon (CFRPs), are being used for primary structural applications, particularly in the aerospace and naval industries. Advantages of CFRP materials, compared to traditional materials such as steel and aluminum, include: light weight, high strength to weight ratio, corrosion resistance, and long life expectancy. A concern with CFRPs is that despite quality control during fabrication, the material can contain many hidden internal flaws. These flaws in combination with unseen damage due to fatigue and low velocity impact have led to catastrophic failure of structures and components. Therefore a large amount of research has been conducted regarding nondestructive testing (NDT) and structural health monitoring (SHM) of CFRP materials. The principal objective of this research program was to develop methods to characterize failure mechanisms in CFRP materials used by the U.S. Army using acoustic emission (AE) and/or acousto-ultrasonic (AU) data. Failure mechanisms addressed include fiber breakage, matrix cracking, and delamination due to shear between layers. CFRP specimens were fabricated and tested in uniaxial tension to obtain AE and AU data. The specimens were designed with carbon fibers in different orientations to produce the different failure mechanisms. Some specimens were impacted with a blunt indenter prior to testing to simulate low-velocity impact. A signature analysis program was developed to characterize the AE data based on data examination using visual pattern recognition techniques. It was determined that it was important to characterize the AE event , using the location of the event as a parameter, rather than just the AE hit (signal recorded by an AE sensor). A back propagation neural network was also trained based on the results of the signature analysis program. Damage observed on the specimens visually with the aid of a scanning electron microscope agreed with the damage type assigned by the signature analysis program. The load level at which significant damage occurred in the specimens was evaluated using ASME Boiler and Pressure Vessel criteria. AU testing proved inconclusive for characterization of the damage due to common problems associated with AU testing such as: reproducibility difficulties due to degradation of the attachment of the sensors, damage not detected unless in the line of sight between sensors, and large intrinsic variation of the data.

Biomechanics of longitudinal arch support mechanisms in foot orthoses and their effect on plantar aponeurosis strain.

PubMed

Kogler, G F; Solomonidis, S E; Paul, J P

1996-07-01

OBJECTIVE: The purpose of this investigation was to quantify the longitudinal arch support properties of several types of foot orthosis. DESIGN: An in vitro method that simulated 'static stance' was used to determine arch support capabilities, with plantar aponeurosis strain implemented as the performance measure. BACKGROUND: A longitudinal arch support mechanism of an orthosis resists depression of the foot's arches by transferring a portion of the load to the medial structures of the foot. Since the plantar aponeurosis is in tension when the foot is loaded, a quantifiable decrease in strain should occur with an adequate orthotic arch control mechanism. METHODS: A differential variable reluctance transducer was surgically implanted in the plantar aponeurosis of cadaveric donor limb feet (n = 7). Each specimen was mounted in an electromechanical test machine which applied a load of up to 900 N axially to the tibia. The test schedule was divided into seven test conditions: specimen barefoot; specimen with shoe and specimen with shoe and five different orthoses. RESULTS: The University of California Biomechanics Laboratory Shoe Insert and two other foot orthoses significantly decreased the strain in the plantar aponeurosis compared to the barefoot control and were considered effective arch supports (P < 0.05). The functional foot orthosis, stock orthosis, and test shoe did not effectively reduce plantar aponeurosis strain. Significant variations of time required to achieve the specified load levels were recorded among the test conditions, indicating the relative cushioning properties of the shoe/orthosis systems. CONCLUSIONS: The patterns of plantar aponeurosis strain observed in cadaveric tests suggest that certain types of orthoses are more effective than others in the support of the foot's longitudinal arches. It is suggested that to support the longitudinal arches of the foot effectively the medial surface contours of the orthosis must stabilize the apical bony structure of the foot's arch. RELEVANCE: Reducing tension in the plantar aponeurosis is an important treatment objective for orthotic management of plantar fasciitis. Therefore it is of great clinical interest to know whether the longitudinal arch support mechanism of specific foot orthoses have benefits with respect to the loading of the plantar aponeurosis.

A stochastic visco-hyperelastic model of human placenta tissue for finite element crash simulations.

PubMed

Hu, Jingwen; Klinich, Kathleen D; Miller, Carl S; Rupp, Jonathan D; Nazmi, Giseli; Pearlman, Mark D; Schneider, Lawrence W

2011-03-01

Placental abruption is the most common cause of fetal deaths in motor-vehicle crashes, but studies on the mechanical properties of human placenta are rare. This study presents a new method of developing a stochastic visco-hyperelastic material model of human placenta tissue using a combination of uniaxial tensile testing, specimen-specific finite element (FE) modeling, and stochastic optimization techniques. In our previous study, uniaxial tensile tests of 21 placenta specimens have been performed using a strain rate of 12/s. In this study, additional uniaxial tensile tests were performed using strain rates of 1/s and 0.1/s on 25 placenta specimens. Response corridors for the three loading rates were developed based on the normalized data achieved by test reconstructions of each specimen using specimen-specific FE models. Material parameters of a visco-hyperelastic model and their associated standard deviations were tuned to match both the means and standard deviations of all three response corridors using a stochastic optimization method. The results show a very good agreement between the tested and simulated response corridors, indicating that stochastic analysis can improve estimation of variability in material model parameters. The proposed method can be applied to develop stochastic material models of other biological soft tissues.

Observation of Intralaminar Cracking in the Edge Crack Torsion Specimen

NASA Technical Reports Server (NTRS)

Czabaj, Michael W.; Ratcliffe, James G.; Davidson, Barry D.

2013-01-01

The edge crack torsion (ECT) test is evaluated to determine its suitability for measuring fracture toughness associated with mode III delamination growth onset. A series of ECT specimens with preimplanted inserts with different lengths is tested and examined using nondestructive and destructive techniques. Ultrasonic inspection of all tested specimens reveals that delamination growth occurs at one interface ply beneath the intended midplane interface. Sectioning and optical microscopy suggest that the observed delamination growth results from coalescence of angled intralaminar matrix cracks that form and extend across the midplane plies. The relative orientation of these cracks is approximately 45 deg with respect to the midplane, suggesting their formation is caused by resolved principal tensile stresses arising due to the global mode-III shear loading. Examination of ECT specimens tested to loads below the level corresponding to delamination growth onset reveals that initiation of intralaminar cracking approximately coincides with the onset of nonlinearity in the specimen's force-displacement response. The existence of intralaminar cracking prior to delamination growth onset and the resulting delamination extension at an unintended interface render the ECT test, in its current form, unsuitable for characterization of mode III delamination growth onset. The broader implications of the mechanisms observed in this study are also discussed with respect to the current understanding of shear-driven delamination in tape-laminate composites.

The effects of ultrasonic nanocrystal surface modification temperature on the mechanical properties and fretting wear resistance of Inconel 690 alloy

NASA Astrophysics Data System (ADS)

Amanov, A.; Umarov, R.

2018-05-01

In this study, a combination of local heat treatment (LHT) with (w/) and without (w/o) ultrasonic nanocrystal surface modification (UNSM) technique was applied to Inconel 690 alloy at room and high temperatures (RT and HT). The main purpose of this study is to investigate the influence of LHT w/ and w/o UNSM processing on the mechanical and fretting wear mitigation of Inconel 690 alloy. The surface roughness of the specimens was increased with increasing the LHT temperature w/ and w/o UNSM from RT to HT at 700 °C, while the surface hardness of the RT and HT at 300 °C specimens was increased and softening occurred at HT at 700 °C. The mechanical properties of the specimens were investigated using a tensile stress test. It was found that the stress-strain curve of the UNSM-treated at RT exhibited better mechanical characteristics in comparison with the as-received one. Moreover, the specimens treated at HT at 300 and 700 °C exhibited better results in terms of strain, but there was no significant difference in stress. The UNSM treated specimens at HT of 300 °C had better results in comparison with other specimens. In addition, the fretting wear resistance of those specimens was assessed using a ball-on-disk fretting wear tester at temperatures of 25 and 80 °C. The fretting wear resistance of Inconel 690 alloy was also increased by the combination of LHT + UNSM processing, which may be attributed to the increase in mechanical properties, increase in surface roughness, induced compressive residual stress and the presence of a nanostructured surface layer. Hence, Inconel 690 alloy with the increased mechanical properties and fretting wear resistance by the combination of LHT + UNSM processing could be beneficial for nuclear applications.

Strain compatibility tests for sprayed foam cryogenic insulation

NASA Technical Reports Server (NTRS)

Hill, W. L.; Kimberlin, D. O.

1970-01-01

Mechanical stress applied to foam-coated aluminum alloy specimens maintained at cryogenic temperature simulates actual use conditions of the foam insulation. The testing reveals defects in the polyurethane foam or in the foam to metal bond.

Superfluid helium leak sealant study

NASA Technical Reports Server (NTRS)

Vorreiter, J. W.

1981-01-01

Twenty-one leak specimens were fabricated in the ends of stainless steel and aluminum tubes. Eighteen of these tubes were coated with a copolymer material to seal the leak. The other three specimens were left uncoated and served as control specimens. All 21 tubes were cold shocked in liquid helium 50 times and then the leak rate was measured while the tubes were submerged in superfluid helium at 1.7 K. During the cold shocks two of the coated specimens were mechanically damaged and eliminated from the test program. Of the remaining 16 coated specimens one suffered a total coating failure and resulting high leak rate. Another three of the coated specimens suffered partial coating failures. The leak rates of the uncoated specimens were also measured and reported. The significance of various leak rates is discussed in view of the infrared astronomical satellite (IRAS) Dewar performance.

Application of neural networks in the acousto-ultrasonic evaluation of metal-matrix composite specimens

NASA Technical Reports Server (NTRS)

Cios, Krzysztof J.; Tjia, Robert E.; Vary, Alex; Kautz, Harold E.

1992-01-01

Acousto-ultrasonics (AU) is a nondestructive evaluation (NDE) technique that was devised for the testing of various types of composite materials. A study has been done to determine how effectively the AU technique may be applied to metal-matrix composites (MMCs). The authors use the results and data obtained from that study and apply neural networks to them, particularly in the assessment of mechanical property variations of a specimen from AU measurements. It is assumed that there is no information concerning the important features of the AU signal which relate to the mechanical properties of the specimen. Minimally processed AU measurements are used while relying on the network's ability to extract the significant features of the signal.

Automated Plasma Spray (APS) process feasibility study

NASA Technical Reports Server (NTRS)

Fetheroff, C. W.; Derkacs, T.; Matay, I. M.

1981-01-01

An automated plasma spray (APS) process was developed to apply two layer (NiCrAlY and ZrO2-12Y2O3) thermal barrier coatings to aircraft and stationary gas turbine engine blade airfoils. The APS process hardware consists of four subsystems: a mechanical positioning subsystem incorporating two interlaced six degree of freedom assemblies (one for coating deposition and one for coating thickness monitoring); a noncoherent optical metrology subsystem (for in process gaging of the coating thickness buildup at specified points on the specimen); a microprocessor based adaptive system controller (to achieve the desired overall thickness profile on the specimen); and commerical plasma spray equipment. Over fifty JT9D first stage aircraft turbine blade specimens, ten W501B utility turbine blade specimens and dozens of cylindrical specimens were coated with the APS process in preliminary checkout and evaluation studies. The best of the preliminary turbine blade specimens achieved an overall coating thickness uniformity of 53 micrometers (2.1 mils), much better than is achievable manually. Comparative evaluations of coating thickness uniformity for manually sprayed and APS coated specimens were performed. One of the preliminary turbine blade evaluation specimens was subjected to a torch test and metallographic evaluation. Some cylindrical specimens coated with the APS process survived up to 2000 cycles in subsequent burner rig testing.

Strain Rate Dependency of Bronze Metal Matrix Composite Mechanical Properties as a Function of Casting Technique

NASA Astrophysics Data System (ADS)

Brown, Lloyd; Joyce, Peter; Radice, Joshua; Gregorian, Dro; Gobble, Michael

2012-07-01

Strain rate dependency of mechanical properties of tungsten carbide (WC)-filled bronze castings fabricated by centrifugal and sedimentation-casting techniques are examined, in this study. Both casting techniques are an attempt to produce a functionally graded material with high wear resistance at a chosen surface. Potential applications of such materials include shaft bushings, electrical contact surfaces, and brake rotors. Knowledge of strain rate-dependent mechanical properties is recommended for predicting component response due to dynamic loading or impact events. A brief overview of the casting techniques for the materials considered in this study is followed by an explanation of the test matrix and testing techniques. Hardness testing, density measurement, and determination of the volume fraction of WC particles are performed throughout the castings using both image analysis and optical microscopy. The effects of particle filling on mechanical properties are first evaluated through a microhardness survey of the castings. The volume fraction of WC particles is validated using a thorough density survey and a rule-of-mixtures model. Split Hopkinson Pressure Bar (SHPB) testing of various volume fraction specimens is conducted to determine strain dependence of mechanical properties and to compare the process-property relationships between the two casting techniques. The baseline performances of C95400 bronze are provided for comparison. The results show that the addition of WC particles improves microhardness significantly for the centrifugally cast specimens, and, to a lesser extent, in the sedimentation-cast specimens, largely because the WC particles are more concentrated as a result of the centrifugal-casting process. Both metal matrix composites (MMCs) demonstrate strain rate dependency, with sedimentation casting having a greater, but variable, effects on material response. This difference is attributed to legacy effects from the casting process, namely, porosity and localized WC particle grouping.

Comparative studies on the mechanical properties of natural rubber and natural rubber filled with multi-walled carbon nanotubes

NASA Astrophysics Data System (ADS)

Ismail, R.; Ibrahim, A.; Rusop, M.; Adnan, A.

2018-05-01

The present article compares the mechanical properties of natural rubber (NR) and carbon nanotubes (CNTs) filled natural rubber composites. Four types of nanocomposite specimens are fabricated with different MWCNT loadings: 0 wt% (pure natural rubber), 1 wt%, 3 wt%, and 5 wt%. The specimens are tested for their mechanical properties. It is observed that the tensile strength, hardness and elongation break of CNTs filled rubber composites are remarkably higher than that of raw rubber indicating the inherent reinforcing potential of CNTs. Percentage of the elongation at break of rubber CNTs composites is lower than that of raw rubber.

Method for hygromechanical characterization of graphite/epoxy composite

NASA Technical Reports Server (NTRS)

Yaniv, Gershon; Peimanidis, Gus; Daniel, Isaac M.

1987-01-01

An experimental method is described for measuring hygroscopic swelling strains and mechanical strains of moisture-conditioned composite specimens. The method consists of embedding encapsulated strain gages in the midplane of the composite laminate; thus it does not interfere with normal moisture diffusion. It is particularly suited for measuring moisture swelling coefficients and for mechanical testing of moisture-conditioned specimens at high strain rates. Results obtained by the embedded gage method were shown to be more reliable and reproducible than those obtained by surface gages, dial gages, or extensometers.

1000541

NASA Image and Video Library

2010-04-13

TATHAN COFFEE (EM10 MATERIALS TEST ENGINEER, JACOBS ESTS GROUP/JTI) ADJUSTS A UNIQUE MECHANICAL TEST SETUP THAT MEASURES STRAIN ON A SINGLE SAMPLE, USING TWO DIFFERENT TECHNIQUES AT THE SAME TIME. THE TEST FIXTURE HOLDS A SPECIMEN THAT REPRESENTS A LIQUID OXYGEN (LOX) BEARING FROM THE J2-X ENGINE

Large strain cruciform biaxial testing for FLC detection

NASA Astrophysics Data System (ADS)

Güler, Baran; Efe, Mert

2017-10-01

Selection of proper test method, specimen design and analysis method are key issues for studying formability of sheet metals and detection of their forming limit curves (FLC). Materials with complex microstructures may need an additional micro-mechanical investigation and accurate modelling. Cruciform biaxial test stands as an alternative to standard tests as it achieves frictionless, in-plane, multi-axial stress states with a single sample geometry. In this study, we introduce a small-scale (less than 10 cm) cruciform sample allowing micro-mechanical investigation at stress states ranging from plane strain to equibiaxial. With successful specimen design and surface finish, large forming limit strains are obtained at the test region of the sample. The large forming limit strains obtained by experiments are compared to the values obtained from Marciniak-Kuczynski (M-K) local necking model and Cockroft-Latham damage model. This comparison shows that the experimental limiting strains are beyond the theoretical values, approaching to the fracture strain of the two test materials: Al-6061-T6 aluminum alloy and DC-04 high formability steel.

Comparison between the Strength Levels of Baseline Nuclear-Grade Graphite and Graphite Irradiated in AGC-2

DOE Office of Scientific and Technical Information (OSTI.GOV)

Carroll, Mark Christopher

2015-07-01

This report details the initial comparison of mechanical strength properties between the cylindrical nuclear-grade graphite specimens irradiated in the second Advanced Graphite Creep (AGC-2) experiment with the established baseline, or unirradiated, mechanical properties compiled in the Baseline Graphite Characterization program. The overall comparative analysis will describe the development of an appropriate test protocol for irradiated specimens, the execution of the mechanical tests on the AGC-2 sample population, and will further discuss the data in terms of developing an accurate irradiated property distribution in the limited amount of irradiated data by leveraging the considerably larger property datasets being captured in themore » Baseline Graphite Characterization program. Integrating information on the inherent variability in nuclear-grade graphite with more complete datasets is one of the goals of the VHTR Graphite Materials program. Between “sister” specimens, or specimens with the same geometry machined from the same sub-block of graphite from which the irradiated AGC specimens were extracted, and the Baseline datasets, a comprehensive body of data will exist that can provide both a direct and indirect indication of the full irradiated property distributions that can be expected of irradiated nuclear-grade graphite while in service in a VHTR system. While the most critical data will remain the actual irradiated property measurements, expansion of this data into accurate distributions based on the inherent variability in graphite properties will be a crucial step in qualifying graphite for nuclear use as a structural material in a VHTR environment.« less

An Experimental Investigation of Transverse Tension Fatigue Characterization of IM6/3501-6 Composite Materials Using a Three-Point Bend Test

NASA Technical Reports Server (NTRS)

Peck, Ann W.

1998-01-01

As composites are introduced into more complex structures with out-of-plane loadings, a better understanding is needed of the out-of-plane, matrix-dominated failure mechanisms. This work investigates the transverse tension fatigue characteristics of IM6/3501 composite materials. To test the 90 degree laminae, a three-point bend test was chosen, potentially minimizing handling and gripping issues associated with tension tests. A finite element analysis was performed of a particular specimen configuration to investigate the influence of specimen size on the stress distribution for a three-point bend test. Static testing of 50 specimens of 9 different sized configurations produced a mean transverse tensile strength of 61.3 Mpa (8.0 ksi). The smallest configuration (10.2 mm wide, Span-to-thickness ratio of 3) consistently exhibited transverse tensile failures. A volume scale effect was difficult to discern due to the large scatter of the data. Static testing of 10 different specimens taken from a second panel produced a mean transverse tensile strength of 82.7 Mpa (12.0 ksi). Weibull parameterization of the data was possible, but due to variability in raw material and/or manufacturing, more replicates are needed for greater confidence. Three-point flex fatigue testing of the smallest configuration was performed on 59 specimens at various levels of the mean static transverse tensile strength using an R ratio of 0.1 and a frequency of 20 Hz. A great deal of scatter was seen in the data. The majority of specimens failed near the center loading roller. To determine whether the scatter in the fatigue data is due to variability in raw material and/or the manufacturing process, additional testing should be performed on panels manufactured from different sources.

Strength degradation and lifetime prediction of dental zirconia ceramics under cyclic normal loading.

PubMed

Li, Wanzhong; Xu, Yingqiang; He, Huiming; Zhao, Haidan; Sun, Jian; Hou, Yue

2015-01-01

Clinical cases show that zirconia restoration could happen fracture by accident under overloading after using a period of time. The purpose of this study is to research mechanical behavior and predict lifetime of dental zirconia ceramics under cyclic normal contact loading with experiments. Cyclic normal contact loading test and three point bending test are carried on specimens made of two brands of dental zirconia ceramic to obtain flexure strength and damage degree after different number of loading cycles. By means of damage mechanics model, damage degree under different number of contact loading cycles are calculated according to flexure strength, and verified by SEM photographs of cross section morphology of zirconia ceramics specimen phenomenologically. Relation curve of damage degree and number of cycles is fitted by polynomial fitting, then the number of loading cycles can be concluded when the specimen is complete damage. Strength degradation of two brands dental zirconia ceramics are researched in vitro, and prediction method of contact fatigue lifetime is established.

Fatigue Failure Modes of the Grain Size Transition Zone in a Dual Microstructure Disk

NASA Technical Reports Server (NTRS)

Gabb, Timothy P.; Kantzos, Pete T.; Palsa, Bonnie; Telesman, Jack; Gayda, John; Sudbrack, Chantal K.

2012-01-01

Mechanical property requirements vary with location in nickel-based superalloy disks. In order to maximize the associated mechanical properties, heat treatment methods have been developed for producing tailored grain microstructures. In this study, fatigue failure modes of a grain size transition zone in a dual microstructure disk were evaluated. A specialized heat treatment method was applied to produce varying grain microstructure in the bore to rim portions of a powder metallurgy processed nickel-based superalloy disk. The transition in grain size was concentrated in a zone of the disk web, between the bore and rim. Specimens were extracted parallel and transversely across this transition zone, and multiple fatigue tests were performed at 427 C and 704 C. Grain size distributions were characterized in the specimens, and related to operative failure initiation modes. Mean fatigue life decreased with increasing maximum grain size, going out through the transition zone. The scatter in limited tests of replicates was comparable for failures of uniform gage specimens in all transition zone locations examined.

In Situ Electrosynthesis of Polymethyl Methacrylate Within Ceramic Launch Pad Materials

NASA Technical Reports Server (NTRS)

Acevedo, Raul; Cardenas, Henry

2012-01-01

Electrokinetic deposition of methylmethacrylate is used to mitigate corrosion in reinforced concrete. The methylmethacrylate (MMA) monomer deposits in the pores in the concrete where it is converted into its polymer, polymethylmethacrylate, thus creating a barrier that also enhances the mechanical properties of the concrete. Previous to the MMA treatment an Electrokinetic deposition is used to transport calcium, sodium and potassium hydroxide particles through the capillary pores of concrete directly to the concrete reinforcement. The intent is to use these compounds as a sacrificial electrode layer during the electrokinetic deposition of methylmethacrylate monomer. Cylindrical reinforced concrete specimens were subjected to electrokinetic treatment and the specimens were tested to characterize porosity reduction and tensile splitting strength showing an increase in the tensile strength. In addition, nine specimens treated electro-kinetically and in long-term atmospheric exposure testing at NASA's Kennedy Space Center, seaside atmospheric exposure test site were tested to determine their corrosion rate.

Effects of Internal and External Hydrogen on Inconel 718

NASA Technical Reports Server (NTRS)

Walter, R. J.; Frandsen, J. D.

1999-01-01

Internal hydrogen embrittlement (IHE) and hydrogen environment embrittlement (HEE) tensile and bend crack growth tests were performed on Inconel 718. For the IHE tests, the specimens were precharged to approximately 90 ppm hydrogen by exposure to 34.5 MPa H2 at 650 C. The HEE tests were performed in 34.5 MPa H2. Parameters evaluated were test temperature, strain rate for smooth and notch specimen geometries. The strain rate effect was very significant at ambient temperature for both IHE and HEE and decreased with increasing temperatures. For IHE, the strain rate effect was neglible at 260'C, and for HEE the strain rate effect was neglible at 400 C. At low temperatures, IHE was more severe than HEE, and at high temperatures HEE was more severe than IHE with a cross over temperature about 350 C. At 350 C, the equilibrium hydrogen concentration in Inconel 718 is about 50% lower than the hydrogen content of the precharged IHE specimens. Dislocation hydrogen sweeping of surface absorbed hydrogen was the likely transport mechanism for increasing the hydrogen concentration in the HEE tests sufficiently to produce the same degree of embrittlement as that of the more highly hydrogen charged IHE specimens. The main IHE fracture characteristic was formation of large, brittle flat facets, which decreased with increasing test temperature. The IHE fracture matrix surrounding the large facets ranged between brittle fine faceted to microvoid ductility depending upon strain rate, specimen geometry as well as temperature. The HEE fractures were characteristically fine featured, transgranular and brittle with a significant portion forming a "saw tooth" crystallographic pattern. Both IHE and HEE fractures were predominantly along the {1 1 1) slip and twin boundaries. With respect to embrittlement mechanism, it was postulated that dislocation hydrogen sweeping and hydrogen enhanced localized plasticity were active in HEE and IHE for concentrating hydrogen along (1 1 1) slip and twin planes. Final brittle failure occurred by hydrogen induced planer decohesion.

Effect of heat treatment on mechanical properties of age-hardenable gold alloy at intraoral temperature.

PubMed

Watanabe, I; Watanabe, E; Cai, Z; Okabe, T; Atsuta, M

2001-09-01

The aim of this study was to investigate the effect of various heat treatments on the mechanical properties of gold alloys capable of age-hardening at intraoral temperature. Dumbbell-shaped patterns (ISO 6871) were cast with three gold alloys (Sofard; NC Type-IV; Aurum Cast, NihombashiTokuriki Co.). The Sofard alloy is age-hardenable at intraoral temperature. The castings underwent various heat treatments [as-cast (AC); solution treatment (ST); high-temperature aging (HA); intraoral aging (IA)]. After these heat treatments, ultimate tensile strength (UTS), 0.2% offset yield strength (YS), and elongation (EL) were measured at a strain rate of 1.7x10(-4)/s. Fracture surfaces of the specimens after tensile testing were observed using SEM. Vickers hardness was also measured after heat treating. After IA, the hardness values of the Sofard alloy increased and reached values similar to the hardness of the Sofard specimens aged at high temperature (HA). The hardness values of the NC Type-IV and Aurum Cast specimens slightly increased after IA, but did not reach the values of the specimens after HA. All the Sofard, NC Type-IV and Aurum Cast specimens showed significantly (P<0.05) greater hardness values after HA, compared with the values after any other heat treatments (AC, ST and IA). The UTS and YS of the specimens indicated a tendency similar to the results obtained for hardness. The Sofard specimens with ST showed the greatest elongation compared to the corresponding NC Type-IV and Aurum Cast specimens. However, the elongation of the Sofard specimens was abruptly reduced after intraoral aging. Intraoral aging significantly improved the mechanical properties and hardness of the Sofard alloy.

Cyclic Strain Resistance, Stress Response, Fatigue Life, and Fracture Behavior of High Strength Low Alloy Steel 300 M

NASA Astrophysics Data System (ADS)

Manigandan, K.; Srivatsan, T. S.; Tammana, Deepthi; Poorgangi, Behrang; Vasudevan, Vijay K.

2014-05-01

The focus of this technical manuscript is a record of the specific role of microstructure and test specimen orientation on cyclic stress response, cyclic strain resistance, and cyclic stress versus strain response, deformation and fracture behavior of alloy steel 300 M. The cyclic strain amplitude-controlled fatigue properties of this ultra-high strength alloy steel revealed a linear trend for the variation of log elastic strain amplitude with log reversals-to-failure, and log plastic strain amplitude with log reversals-to-failure for both longitudinal and transverse orientations. Test specimens of the longitudinal orientation showed only a marginal improvement over the transverse orientation at equivalent values of plastic strain amplitude. Cyclic stress response revealed a combination of initial hardening for the first few cycles followed by gradual softening for a large portion of fatigue life before culminating in rapid softening prior to catastrophic failure by fracture. Fracture characteristics of test specimens of this alloy steel were different at both the macroscopic and fine microscopic levels over the entire range of cyclic strain amplitudes examined. Both macroscopic and fine microscopic observations revealed fracture to be a combination of both brittle and ductile mechanisms. The underlying mechanisms governing stress response, deformation characteristics, fatigue life, and final fracture behavior are presented and discussed in light of the competing and mutually interactive influences of test specimen orientation, intrinsic microstructural effects, deformation characteristics of the microstructural constituents, cyclic strain amplitude, and response stress.

Impact of Steel Fiber Size and Shape on the Mechanical Properties of Ultra-High Performance Concrete

DTIC Science & Technology

2015-08-01

32 Appendix B: DTT Specimens Pretest / Posttest ..................................................................................... 36 Appendix C...type and then subsequently compared to that material’s UCS. Figure 6 shows the splitting tensile testing set-up, both pretest and posttest . Figure...9 show the actual test configuration, pretest and posttest , respectively. This configuration utilized a chucking mechanism suited to the shape of

Numerical development of a new correlation between biaxial fracture strain and material fracture toughness for small punch test

NASA Astrophysics Data System (ADS)

Kumar, Pradeep; Dutta, B. K.; Chattopadhyay, J.

2017-04-01

The miniaturized specimens are used to determine mechanical properties of the materials, such as yield stress, ultimate stress, fracture toughness etc. Use of such specimens is essential whenever limited quantity of material is available for testing, such as aged/irradiated materials. The miniaturized small punch test (SPT) is a technique which is widely used to determine change in mechanical properties of the materials. Various empirical correlations are proposed in the literature to determine the value of fracture toughness (JIC) using this technique. bi-axial fracture strain is determined using SPT tests. This parameter is then used to determine JIC using available empirical correlations. The correlations between JIC and biaxial fracture strain quoted in the literature are based on experimental data acquired for large number of materials. There are number of such correlations available in the literature, which are generally not in agreement with each other. In the present work, an attempt has been made to determine the correlation between biaxial fracture strain (εqf) and crack initiation toughness (Ji) numerically. About one hundred materials are digitally generated by varying yield stress, ultimate stress, hardening coefficient and Gurson parameters. Such set of each material is then used to analyze a SPT specimen and a standard TPB specimen. Analysis of SPT specimen generated biaxial fracture strain (εqf) and analysis of TPB specimen generated value of Ji. A graph is then plotted between these two parameters for all the digitally generated materials. The best fit straight line determines the correlation. It has been also observed that it is possible to have variation in Ji for the same value of biaxial fracture strain (εqf) within a limit. Such variation in the value of Ji has been also ascertained using the graph. Experimental SPT data acquired earlier for three materials were then used to get Ji by using newly developed correlation. A reasonable comparison of calculated Ji with the values quoted in literature confirmed usefulness of the correlation.

Methodology to predict delayed failure due to slow crack growth in ceramic tubular components using data from simple specimens

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jadaan, O.M.; Tressler, R.E.

1993-04-01

The methodology to predict the lifetime of sintered [alpha]-silicon carbide (SASC) tubes subjected to slow crack growth (SCG) conditions involved the experimental determination of the SCG parameters of that material and the scaling analysis to project the stress rupture data from small specimens to large components. Dynamic fatigue testing, taking into account the effect of threshold stress intensity factor, of O-ring and compressed C-ring specimens was used to obtain the SCG parameters. These SCG parameters were in excellent agreement with those published in the literature and extracted from stress rupture tests of tensile and bend specimens. Two methods were usedmore » to predict the lifetimes of internally heated and pressurized SASC tubes. The first is a fracture mechanics approach that is well known in the literature. The second method used a scaling analysis in which the stress rupture distribution (lifetime) of any specimen configuration can be predicted from stress rupture data of another.« less

Scale effects in the response and failure of fiber reinforced composite laminates loaded in tension and in flexure

NASA Technical Reports Server (NTRS)

Jackson, Karen E.; Kellas, Sotiris; Morton, John

1992-01-01

The feasibility of using scale model testing for predicting the full-scale behavior of flat composite coupons loaded in tension and beam-columns loaded in flexure is examined. Classical laws of similitude are applied to fabricate and test replica model specimens to identify scaling effects in the load response, strength, and mode of failure. Experiments were performed on graphite-epoxy composite specimens having different laminate stacking sequences and a range of scaled sizes. From the experiments it was deduced that the elastic response of scaled composite specimens was independent of size. However, a significant scale effect in strength was observed. In addition, a transition in failure mode was observed among scaled specimens of certain laminate stacking sequences. A Weibull statistical model and a fracture mechanics based model were applied to predict the strength scale effect since standard failure criteria cannot account for the influence of absolute specimen size on strength.

Experimental and numerical study of the failure process and energy mechanisms of rock-like materials containing cross un-persistent joints under uniaxial compression.

PubMed

Cao, Rihong; Cao, Ping; Lin, Hang; Fan, Xiang

2017-01-01

Joints and fissures in natural rocks have a significant influence on the stability of the rock mass, and it is often necessary to evaluate strength failure and crack evolution behavior. In this paper, based on experimental tests and numerical simulation (PFC2D), the macro-mechanical behavior and energy mechanism of jointed rock-like specimens with cross non-persistent joints under uniaxial loading were investigated. The focus was to study the effect of joint dip angle α and intersection angle γ on the characteristic stress, the coalescence modes and the energy release of jointed rock-like specimens. For specimens with γ = 30° and 45°, the UCS (uniaxial compression strength), CIS (crack initiation stress) and CDiS (critical dilatancy stress) increase as α increases from 0° to 75°. When γ = 60° and 75°, the UCS, CIS and CDiS increase as α increases from 0° to 60° and decrease when α is over 60°. Both the inclination angle α and intersection angle γ have great influence on the failure pattern of pre-cracked specimens. With different α and γ, specimens exhibit 4 kinds of failure patterns. Both the experimental and numerical results show that the energy of a specimen has similar trends with characteristic stress as α increases.

Water sensitivity of the seismic properties of upper-mantle olivine

NASA Astrophysics Data System (ADS)

Cline, Christopher; David, Emmanuel; Faul, Ulrich; Berry, Andrew; Jackson, Ian

2017-04-01

The wave speeds and attenuation of seismic waves in the upper mantle are expected to be strongly influenced by the defect chemistry of olivine grain interiors and the associated chemical complexity of grain-boundary regions. Changes in chemical environment (oxygen fugacity and/or water fugacity) can impose different defect chemistries, including the creation and retention of hydrous defects, and therefore can directly influence anelastic relaxation involving stress-induced migration of lattice defects and/or grain-boundary sliding. Here we report the first low-frequency experimental study of the seismic properties of olivine under water-undersaturated conditions. Three synthetic sol-gel derived olivine (Fo90) specimens were fabricated by hot-pressing in welded Pt capsules with various concentrations of hydroxyl, chemically bound as doubly protonated Si vacancies, charge balanced by substitution of Ti on a neighboring M-site (i.e., the Ti-clinohumite-like defect). Hydroxyl contents, determined following the subsequent mechanical testing within Pt sleeves, increased systematically with the amount of added Ti-dopant. Added Ti concentrations ranged between 176 and 802 atom ppm Ti/Si, resulting in concentrations of bound hydrogen in the three samples ranging between 330 and 1150 atom ppm H/Si. Each hot-pressed specimen was precision ground and then sleeved in Pt for mechanical testing in forced torsional oscillation under water-undersaturated conditions. Forced-oscillation tests were conducted at seismic periods of 1 - 1000 s and 200 MPa confining pressure during slow staged cooling from 1200 to 25°C. Each Ti-doped specimen showed mechanical behavior of the high-temperature background type involving monotonically increasing dissipation and decreasing shear modulus with increasing oscillation period and increasing temperature. Comparison of the mechanical data acquired in these water-undersaturated conditions with a similarly tested, but dry, Ti-bearing specimen (enclosed within an Ni-Fe sleeve under more reducing conditions) shows a marked contrast. The OH-bearing specimens exhibit much lower shear moduli (by as much as 80%) and higher levels of dissipation (by as much as 0.5 log units in Q-1), but also limited sensitivity of the seismic properties to the total water content among the hydrated specimens in the series. These results indicate that the higher oxygen and water fugacities prevailing within Pt-sleeved specimens result in lower shear moduli and higher dissipation under water-undersaturated conditions - presumably attributable to contrasting defect populations and/or grain boundary chemistries. Clarification of the relative roles of grain-boundary sliding and any additional intragranular relaxation under increased fH2O and fO2 thus offers the prospect of an improved understanding of the seismological signature of more oxidized/hydrous portions of the Earth's upper mantle, such as subduction zone environments.

Using Digital Image Correlation to Characterize Local Strains on Vascular Tissue Specimens.

PubMed

Zhou, Boran; Ravindran, Suraj; Ferdous, Jahid; Kidane, Addis; Sutton, Michael A; Shazly, Tarek

2016-01-24

Characterization of the mechanical behavior of biological and engineered soft tissues is a central component of fundamental biomedical research and product development. Stress-strain relationships are typically obtained from mechanical testing data to enable comparative assessment among samples and in some cases identification of constitutive mechanical properties. However, errors may be introduced through the use of average strain measures, as significant heterogeneity in the strain field may result from geometrical non-uniformity of the sample and stress concentrations induced by mounting/gripping of soft tissues within the test system. When strain field heterogeneity is significant, accurate assessment of the sample mechanical response requires measurement of local strains. This study demonstrates a novel biomechanical testing protocol for calculating local surface strains using a mechanical testing device coupled with a high resolution camera and a digital image correlation technique. A series of sample surface images are acquired and then analyzed to quantify the local surface strain of a vascular tissue specimen subjected to ramped uniaxial loading. This approach can improve accuracy in experimental vascular biomechanics and has potential for broader use among other native soft tissues, engineered soft tissues, and soft hydrogel/polymeric materials. In the video, we demonstrate how to set up the system components and perform a complete experiment on native vascular tissue.

Dual Function Behavior of Carbon Fiber-Reinforced Polymer in Simulated Pore Solution.

PubMed

Zhu, Ji-Hua; Guo, Guanping; Wei, Liangliang; Zhu, Miaochang; Chen, Xianchuan

2016-02-06

The mechanical and electrochemical performance of carbon fiber-reinforced polymer (CFRP) were investigated regarding a novel improvement in the load-carrying capacity and durability of reinforced concrete structures by adopting CFRP as both a structural strengthener and an anode of the impressed current cathodic protection (ICCP) system. The mechanical and anode performance of CFRP were investigated in an aqueous pore solution in which the electrolytes were available to the anode in a cured concrete structure. Accelerated polarization tests were designed with different test durations and various levels of applied currents in accordance with the international standard. The CFRP specimens were mechanically characterized after polarization. The measured feeding voltage and potential during the test period indicates CFRP have stable anode performance in a simulated pore solution. Two failure modes were observed through tensile testing. The tensile properties of the post-polarization CFRP specimens declined with an increased charge density. The CFRP demonstrated success as a structural strengthener and ICCP anode. We propose a mathematic model predicting the tensile strengths of CFRP with varied impressed charge densities.

Dual Function Behavior of Carbon Fiber-Reinforced Polymer in Simulated Pore Solution

PubMed Central

Zhu, Ji-Hua; Guo, Guanping; Wei, Liangliang; Zhu, Miaochang; Chen, Xianchuan

2016-01-01

The mechanical and electrochemical performance of carbon fiber-reinforced polymer (CFRP) were investigated regarding a novel improvement in the load-carrying capacity and durability of reinforced concrete structures by adopting CFRP as both a structural strengthener and an anode of the impressed current cathodic protection (ICCP) system. The mechanical and anode performance of CFRP were investigated in an aqueous pore solution in which the electrolytes were available to the anode in a cured concrete structure. Accelerated polarization tests were designed with different test durations and various levels of applied currents in accordance with the international standard. The CFRP specimens were mechanically characterized after polarization. The measured feeding voltage and potential during the test period indicates CFRP have stable anode performance in a simulated pore solution. Two failure modes were observed through tensile testing. The tensile properties of the post-polarization CFRP specimens declined with an increased charge density. The CFRP demonstrated success as a structural strengthener and ICCP anode. We propose a mathematic model predicting the tensile strengths of CFRP with varied impressed charge densities. PMID:28787900

A Review of the Proposed KIsi Offset-Secant Method for Size-Insensitive Linear-Elastic Fracture Toughness Evaluation

NASA Technical Reports Server (NTRS)

James, Mark; Wells, Doug; Allen, Phillip; Wallin, Kim

2017-01-01

Recently proposed modifications to ASTM E399 would provide a new size-insensitive approach to analyzing the force-displacement test record. The proposed size-insensitive linear-elastic fracture toughness, KIsi, targets a consistent 0.5mm crack extension for all specimen sizes by using an offset secant that is a function of the specimen ligament length. The KIsi evaluation also removes the Pmax/PQ criterion and increases the allowable specimen deformation. These latter two changes allow more plasticity at the crack tip, prompting the review undertaken in this work to ensure the validity of this new interpretation of the force-displacement curve. This paper provides a brief review of the proposed KIsi methodology and summarizes a finite element study into the effects of increased crack tip plasticity on the method given the allowance for additional specimen deformation. The study has two primary points of investigation: the effect of crack tip plasticity on compliance change in the force-displacement record and the continued validity of linear-elastic fracture mechanics to describe the crack front conditions. The analytical study illustrates that linear-elastic fracture mechanics assumptions remain valid at the increased deformation limit; however, the influence of plasticity on the compliance change in the test record is problematic. A proposed revision to the validity criteria for the KIsi test method is briefly discussed.

Fiber-reinforced composite substructure: load-bearing capacity of an onlay restoration and flexural properties of the material.

PubMed

Garoushi, Sufyan K; Lassila, Lippo V J; Tezvergil, Arzu; Vallittu, Pekka K

2006-09-01

The aim of this study was to determine the static load-bearing capacity of composite resin onlay restorations made of particulate filler composite (PFC) with two different types of fiber-reinforced composite (FRC) substructures. In addition, flexural properties of the material combination and the effect of polymerization devices were tested. Specimens were prepared to simulate an onlay restoration, which consisted of 2 to 3 mm of FRC layer as a substructure (short random and continuous bidirectional fiber orientation) and a 1 mm surface layer of PFC. Control specimens were prepared from plain PFC. In Group A the specimens were incrementally polymerized only with a hand-light curing unit for 40 s, while in Group B the specimens were post-cured in a light-curing oven for 15 min before they were statically loaded with a steel ball. Bar-shaped test specimens were prepared to measure the flexural properties of material combination using a three-point bending test (ISO 10477). Analysis of variance (ANOVA) revealed all specimens with a FRC substructure have higher values of static load-bearing capacity and flexural properties than those obtained with plain PFC (p<0.001). The load-bearing capacity of all the specimens decreased after post-curing and water storage. Restorations made from a material combination of FRC and PFC showed better mechanical properties than those obtained with plain PFC.

Mechanical characterization of an additively manufactured Inconel 718 theta-shaped specimen

DOE PAGES

Cakmak, Ercan; Watkins, Thomas R.; Bunn, Jeffrey R.; ...

2015-11-20

Two sets of “theta”-shaped specimens were additively manufactured with Inconel 718 powders using an electron beam melting technique with two distinct scan strategies. Light optical microscopy, mechanical testing coupled with a digital image correlation (DIC) technique, finite element modeling, and neutron diffraction with in situ loading characterizations were conducted. The cross-members of the specimens were the focus. Light optical micrographs revealed that different microstructures were formed with different scan strategies. Ex situ mechanical testing revealed each build to be stable under load until ductility was observed on the cross-members before failure. The elastic moduli were determined by forming a correlationmore » between the elastic tensile stresses determined from FEM, and the elastic strains obtained from DIC. The lattice strains were mapped with neutron diffraction during in situ elastic loading; and a good correlation between the average axial lattice strains on the cross-member and those determined from the DIC analysis was found. Lastly, the spatially resolved stresses in the elastic deformation regime are derived from the lattice strains and increased with applied load, showing a consistent distribution along the cross-member.« less

Microstructure and Mechanical Properties of a Low Alloyed MnB Cast Steel

NASA Astrophysics Data System (ADS)

Luo, Kaishuang; Bai, Bingzhe

2010-08-01

The microstructure and mechanical properties of a low alloyed MnB cast steel designed for coupler castings of trucks were studied. The results show that the microstructure of the MnB cast steel after water quenching is lath martensite and a small amount of massive islands in the matrix of lath martensite. The average size of the martensite packets is about 10 μm in length. Carbides precipitated dispersively at the tempering temperature of 450 °C. The carbides are slender and fibrous, of which the microstructure was θ-phase (Fe, Mn)3C characterized by TEM. The MnB cast steel has good hardenability and tempering stability. Excellent combination of strength, ductility and low-temperature toughness were obtained after water-quenching and 450 °C tempering: Rm = 960-1040 MPa, ReL = 880-900 MPa, A = 19-21%, Z = 56-58%. Especially, the impact energy of the Charpy V-Notch (CVN) specimens reached 70-88 J at -40 °C. The fracture mechanism is transcrystalline fracture both for ambient temperature uniaxial tensile test specimens and for CVN impact test specimens broken at -40 °C, where the whole surfaces were manifested as voids and dimples.

Mechanical characterization of an additively manufactured Inconel 718 theta-shaped specimen

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cakmak, Ercan; Watkins, Thomas R.; Bunn, Jeffrey R.

Two sets of “theta”-shaped specimens were additively manufactured with Inconel 718 powders using an electron beam melting technique with two distinct scan strategies. Light optical microscopy, mechanical testing coupled with a digital image correlation (DIC) technique, finite element modeling, and neutron diffraction with in situ loading characterizations were conducted. The cross-members of the specimens were the focus. Light optical micrographs revealed that different microstructures were formed with different scan strategies. Ex situ mechanical testing revealed each build to be stable under load until ductility was observed on the cross-members before failure. The elastic moduli were determined by forming a correlationmore » between the elastic tensile stresses determined from FEM, and the elastic strains obtained from DIC. The lattice strains were mapped with neutron diffraction during in situ elastic loading; and a good correlation between the average axial lattice strains on the cross-member and those determined from the DIC analysis was found. Lastly, the spatially resolved stresses in the elastic deformation regime are derived from the lattice strains and increased with applied load, showing a consistent distribution along the cross-member.« less

Thermal-mechanical properties of a graphitic-nanofibers reinforced epoxy.

PubMed

Salehi-Khojin, Amin; Jana, Soumen; Zhong, Wei-Hong

2007-03-01

We previously developed a series of reactive graphitic nanofibers (r-GNFs) reinforced epoxy (nano-epoxy) as composite matrices, which have shown good wetting and adhesion properties with continuous fiber. In this work, the thermal-mechanical properties of the nano-epoxy system containing EponTM Resin 828 and Epi-cure Curing Agent W were characterized. Results from three-point bending tests showed that the flexural strength and flexural modulus of this system with 0.30 wt% of reactive nanofibers were increased by 16%, and 21% respectively, over pure epoxy. Fracture toughness increased by ca. 40% for specimens with 0.50 wt% of r-GNFs. By dynamic mechanical analysis (DMA) test, specimens with 0.30 wt% of r-GNFs showed a significant increase in storage modulus E' (by ca. 122%) and loss modulus E" (by ca. 111%) with respect to that of pure epoxy. Also thermo-dilatometry analysis (TDA) was used to measure dimensional change of specimens as a function of temperature, and then, coefficients of thermal expansion (CTE) before and after glass transition temperature (Tg) were obtained. Results implied that nano-epoxy materials had good dimensional stability and reduced CTE values when compared to those of pure epoxy.

Influence of Different Ceramic Systems on Marginal Misfit.

PubMed

Vargas, S P; Neves, A C C; Vitti, R; Amaral, M; Henrique, M N; Silva-Concílio, L R

2017-09-01

the aim of this study was to evaluate the marginal misfit at the interface between a ceramic coping and its abutment. Twenty-four specimens were made with solid abutments. The specimens were divided into 3 groups according to the ceramic system (n = 8): Lava (zirconia), IPS e.max Press (lithium disilicate), and IPS Empress Esthetic (leucite). All copings were cemented with resin luting agent (RelyX U200) and the marginal misfit were evaluated at 3 different times: initial, after cementation, and after mechanical cycling using a linear measuring microscope (Measuring Microscope STM-Olympus) at a magnification of 40x. All specimens were subjected to mechanical cycling (1 million cycles) by an universal testing machine (Instron 8800). The results were statistically analyzed using Analysis of Variance and Student's t-test (α = 0.05). all groups showed an increase in the marginal misfit after cementation. The lithium disilicate group demonstrated the lowest interacial gap values at each evaluation (p = 0.001). The zirconia and leucite groups showed similar interfacial gap values (initial, p = 0.244; and post cementation, p = 0.751). the cementation increase the marginal misfit, but the mechanical cycling did not influence the marginal misfit of the ceramics systems evaluated. Copyright© 2017 Dennis Barber Ltd.

Fracture mechanics correlation of boron/aluminum coupons containing stress risers

NASA Technical Reports Server (NTRS)

Adsit, N. R.; Waszczak, J. P.

1975-01-01

The mechanical behavior of boron/aluminum near stress risers has been studied and reported. This effort was directed toward defining the tensile behavior of both unidirectional and (0/ plus or minus 45) boron/aluminum using linear elastic fracture mechanics (LEFM). The material used was 5.6-mil boron in 6061 aluminum, consolidated using conventional diffusion bonding techniques. Mechanical properties are reported for both unidirectional and (0/ plus or minus 45) boron/aluminum, which serve as control data for the fracture mechanics predictions. Three different flawed specimen types were studied. In each case the series of specimens remained geometrically similar to eliminate variations in finite size correction factors. The fracture data from these tests were reduced using two techniques. They both used conventional LEFM methods, but the existence of a characteristic flaw was assumed in one case and not the other. Both the data and the physical behavior of the specimens support the characteristic flaw hypothesis. Cracks were observed growing slowly in the (0/ plus or minus 45) laminates, until a critical crack length was reached at which time catastrophic failure occurred.

Tribological and mechanical behaviours of rattan-fibre-reinforced friction materials under dry sliding conditions

NASA Astrophysics Data System (ADS)

Ma, Yunhai; Wu, Siyang; Tong, Jin; Zhao, Xiaolou; Zhuang, Jian; Liu, Yucheng; Qi, Hongyan

2018-03-01

This work was mainly aimed to study the physical, mechanical and tribological behaviours of the friction materials reinforced by different contents of rattan fibre. These friction materials were fabricated by a compression moulder and tested using a constant speed tester at different friction temperatures. It was found that the friction coefficients of the friction materials added with rattan fibre were relatively stable and no obvious fade was observed in comparison with specimen F-0 (containing 0 wt.% rattan fibres). The fade ratio of specimen F-5 (containing 5 wt.% rattan fibres) was 10.3% and its recovery ratio was 92.4%, indicating the excellent performances of fade resistance and recovery. And the specimen F-5 exhibited the lowest wear rate (0.541 × 10‑7 cm3(N · m)‑1 at 350 °C) among all tested specimens. The worn surface morphologies of the friction materials showed that the appropriate addition of rattan fibres effectively reduced abrasive wear and adhesion wear. The specimen F-5 had a smooth worn surface (Sa = 1.885 μm) with the superior fibre-matrix interfacial adhesion and a lot of secondary contact plateaus, which indicated the highest wear resistance property. The rattan-fibre-reinforced friction materials could be widely applied to automotive friction brake field according to their economic, environmental and social benefits.

Unusual plastic deformation and damage features in titanium: Experimental tests and constitutive modeling

NASA Astrophysics Data System (ADS)

Revil-Baudard, Benoit; Cazacu, Oana; Flater, Philip; Chandola, Nitin; Alves, J. L.

2016-03-01

In this paper, we present an experimental study on plastic deformation and damage of polycrystalline pure HCP Ti, as well as modeling of the observed behavior. Mechanical characterization data were conducted, which indicate that the material is orthotropic and displays tension-compression asymmetry. The ex-situ and in-situ X-ray tomography measurements conducted reveal that damage distribution and evolution in this HCP Ti material is markedly different than in a typical FCC material such as copper. Stewart and Cazacu (2011) anisotropic elastic/plastic damage model is used to describe the behavior. All the parameters involved in this model have a clear physical significance, being related to plastic properties, and are determined from very few simple mechanical tests. It is shown that this model predicts correctly the anisotropy in plastic deformation, and its strong influence on damage distribution and damage accumulation. Specifically, for a smooth axisymmetric specimen subject to uniaxial tension, damage initiates at the center of the specimen, and is diffuse; the level of damage close to failure being very low. On the other hand, for a notched specimen subject to the same loading the model predicts that damage initiates at the outer surface of the specimen, and further grows from the outer surface to the center of the specimen, which corroborates with the in-situ tomography data.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wereszczak, A.A.; Ferber, M.K.; Kirkland, T.P.

Several yttria-fluxed, hot-isostatically pressed (HIPed) silicon nitrides have been tensile creep tested at temperatures representative of gas turbine engines. Creep and oxidation assisted damage mechanisms concurrently evolve when these materials are tested at high temperatures and low stresses (i.e., long exposure times at temperature). Atmospheric creep testing results in creation of oxygen and yttrium gradients across the radial dimension. High concentrations of oxygen and yttrium coincide with dense populations of lenticular-shaped cavities near the surface of crept specimens. The center of the tensile specimens was devoid of oxygen or yttrium; in addition, lenticular cavities were rare. The gradient in lenticular-cavitymore » concentration is coincident with the oxygen and yttrium gradients. Stress corrosion cracking (SCC) also occurs in these HIPed silicon nitrides when they are subjected to stress at high temperatures in ambient air. The size of this damage zone increases when the temperature is higher and/or the applied stress is lower. Stress-corrosion cracking initiates at the surface of the tensile specimen and advances radially inwards. What nucleates SCC has not yet been identified, but it is believed to result from a stress-concentrator (e.g., machining damage) at the surface and its growth is a result of coalescence of microcracks and cavities. The higher concentration of oxygen and yttrium in the grain boundaries near the specimen`s surface lessens the local high temperature mechanical integrity; this is believed to be associated with the growth of the SCC zone. This SCC zone continues to grow in size during tensile loading until it reaches a critical size which causes fracture.« less

Design and application of a quasistatic crush test fixture for investigating scale effects in energy absorbing composite plates

NASA Astrophysics Data System (ADS)

Lavoie, J. Andre; Morton, John

1993-07-01

A crush test fixture for measuring energy absorption of flat plate specimens from an earlier study was redesigned to eliminate the problem of binding of the load transfer platen with the guide posts. Further modifications were to increase the stroke, and combine the two scaled text fixtures into one. This new crush text fixture was shown to produce load-displacement histories exhibiting well developed sustained crushing loads over long strokes. An experimental study was conducted on two material systems: AS4/3502 graphite/epoxy, and a hybrid AS4-Kevlar/3502 composite. The effect of geometric scaling of specimen size, the effect of ply level and sublaminate-level scaling of the stacking sequence of the full scale specimens, and the effect of trigger mechanism on the energy absorption capability were investigated. The new crush test fixture and flat plate specimens produced peak and sustained crushing loads that were lower than obtained with the old crush text fixture. The trigger mechanism used influenced the specific sustained crushing stress (SSCS). The results indicated that to avoid any reduction in the SSCS when scaling from the 1/2 scale to full scale specimen size, the sublaminate-level scaling approach should be used, in agreement with experiments on tubes. The use of Kevlar in place of the graphite 45 deg plies was not as effective a means for supporting and containing the 0 deg graphite plies for rushing of flat plates and resulted in a drop in the SSCS. This result did not correlate with that obtained for tubes.

Design and application of a quasistatic crush test fixture for investigating scale effects in energy absorbing composite plates. M.S. Thesis

NASA Technical Reports Server (NTRS)

Lavoie, J. Andre; Morton, John

1993-01-01

A crush test fixture for measuring energy absorption of flat plate specimens from an earlier study was redesigned to eliminate the problem of binding of the load transfer platen with the guide posts. Further modifications were to increase the stroke, and combine the two scaled text fixtures into one. This new crush text fixture was shown to produce load-displacement histories exhibiting well developed sustained crushing loads over long strokes. An experimental study was conducted on two material systems: AS4/3502 graphite/epoxy, and a hybrid AS4-Kevlar/3502 composite. The effect of geometric scaling of specimen size, the effect of ply level and sublaminate-level scaling of the stacking sequence of the full scale specimens, and the effect of trigger mechanism on the energy absorption capability were investigated. The new crush test fixture and flat plate specimens produced peak and sustained crushing loads that were lower than obtained with the old crush text fixture. The trigger mechanism used influenced the specific sustained crushing stress (SSCS). The results indicated that to avoid any reduction in the SSCS when scaling from the 1/2 scale to full scale specimen size, the sublaminate-level scaling approach should be used, in agreement with experiments on tubes. The use of Kevlar in place of the graphite 45 deg plies was not as effective a means for supporting and containing the 0 deg graphite plies for rushing of flat plates and resulted in a drop in the SSCS. This result did not correlate with that obtained for tubes.

Biomechanical comparison of the human cadaveric pelvis with a fourth generation composite model.

PubMed

Girardi, Brandon L; Attia, Tarik; Backstein, David; Safir, Oleg; Willett, Thomas L; Kuzyk, Paul R T

2016-02-29

The use of cadavers for orthopaedic biomechanics research is well established, but presents difficulties to researchers in terms of cost, biosafety, availability, and ease of use. High fidelity composite models of human bone have been developed for use in biomechanical studies. While several studies have utilized composite models of the human pelvis for testing orthopaedic reconstruction techniques, few biomechanical comparisons of the properties of cadaveric and composite pelves exist. The aim of this study was to compare the mechanical properties of cadaveric pelves to those of the 4th generation composite model. An Instron ElectroPuls E10000 mechanical testing machine was used to load specimens with orientation, boundary conditions and degrees of freedom that approximated those occurring during the single legged phase of walking, including hip abductor force. Each specimen was instrumented with strain gauge rosettes. Overall specimen stiffness and principal strains were calculated from the test data. Composite specimens showed significantly higher overall stiffness and slightly less overall variability between specimens (composite K=1448±54N/m, cadaver K=832±62N/m; p<0.0001). Strains measured at specific sites in the composite models and cadavers were similar (but did differ) only when the applied load was scaled to overall construct stiffness. This finding regarding strain distribution and the difference in overall stiffness must be accounted for when using these composite models for biomechanics research. Altering the cortical wall thickness or tuning the elastic moduli of the composite material may improve future generations of the composite model. Copyright © 2016 Elsevier Ltd. All rights reserved.

Shakedown Tests for Refurbished and Upgraded Frames and Initiation of Alloy 709 Creep Rupture Tests

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Hong; Moser, Jeremy L.; Hawkins, Charles S.

This report describes the shakedown tests conducted on the upgraded frames, and initiation of creep rupture tests on refurbished frames. SS316H, a reference material for Alloy 709, was used in shakedown tests, and the tests were conducted at 816 degree C under three stress levels to accumulate 1% creep strain. 1/4” gage diameter specimen design was used. The creep rupture tests on Alloy 709 were initiated at 600 degree C under 330 MPa to target 1,500 h rupture time. 12 specimens with 3/8” gage diameter were prepared from the materials with 6 heat treatment conditions, 2 from each. The requiredmore » mechanical load under 330MPa was calculated to be 5,286 lb for the 3/8” gage diameter specimen. Among the ART frames, 7 frames are equipped with 10,000 lb load cell including #5 to 8 and #88 to 90, and can be used. 7 tests were thus started in this stage of project, and remaining 5 will be continued whenever any of the 7 tests is completed.« less

The TDR Tuberculosis Specimen Bank: a resource for diagnostic test developers.

PubMed

Nathanson, C-M; Cuevas, L E; Cunningham, J; Perkins, M D; Peeling, R W; Guillerm, M; Moussy, F; Ramsay, A

2010-11-01

The Special Programme for Research and Training in Tropical Diseases established a specimen bank in 1999 to support the development and evaluation of new tuberculosis (TB) diagnostic tools. To provide a narrative of the bank's development and discuss lessons learned, the bank's limitations and potential future applications. Collection sites were selected in high- and low-prevalence settings. Patients with TB symptoms, consenting to participate and to undergo human immunodeficiency virus testing were enrolled and diagnosed. Serum, sputum, saliva and urine samples were collected and sent to the bank's repositories. The bank has stocked 41,437 samples from 2524 patients at 11 sites worldwide. Ninety-five requests for specimens have been reviewed and 67 sets have been approved. Approved applicants have received sets of 20 or 200 samples. The bank allowed an evaluation of 19 commercial lateral flow tests and showed that none of them had broad global utility for TB diagnosis. The establishment and development of the specimen bank have provided a wealth of experience. It is fulfilling a need to provide quality specimens, but the type and number of samples may not fulfil the demands of future end-users. Plans are underway to review the mechanisms of specimen collection and distribution to maximise their impact on product development.

The compressive mechanical properties of diabetic and non-diabetic plantar soft tissue.

PubMed

Pai, Shruti; Ledoux, William R

2010-06-18

Diabetic subjects are at an increased risk of developing plantar ulcers. Knowledge of the physiologic compressive properties of the plantar soft tissue is critical to understanding the possible mechanisms of ulcer formation and improving treatment options. The purpose of this study was to determine the compressive mechanical properties of the plantar soft tissue in both diabetic and non-diabetic specimens from six relevant locations beneath the foot, namely the hallux (big toe), first, third, and fifth metatarsal heads, lateral midfoot, and calcaneus (heel). Cylindrical specimens (1.905 cm diameter) from these locations were excised and separated from the skin and bone from 4 diabetic and 4 non-diabetic age-matched, elderly, fresh-frozen cadaveric feet. Specimens were then subjected to biomechanically realistic strains of approximately 50% in compression using triangle wave tests conducted at five frequencies ranging from 1 to 10 Hz to determine tissue modulus, energy loss, and strain rate dependence. Diabetic vs. non-diabetic results across all specimens, locations, and testing frequencies demonstrated altered mechanical properties with significantly increased modulus (1146.7 vs. 593.0 kPa) but no change in energy loss (68.5 vs. 67.9%). All tissue demonstrated strain rate dependence and tissue beneath the calcaneus was found to have decreased modulus and energy loss compared to other areas. The results of this study could be used to generate material properties for all areas of the plantar soft tissue in diabetic or non-diabetic feet, with implications for foot computational modeling efforts and potentially for pressure alleviating footwear that could reduce plantar ulcer incidence. Published by Elsevier Ltd.

The compressive mechanical properties of diabetic and non-diabetic plantar soft tissue

PubMed Central

Pai, Shruti; Ledoux, William R.

2010-01-01

Diabetic subjects are at an increased risk of developing plantar ulcers. Knowledge of the physiologic compressive properties of the plantar soft tissue is critical to understanding possible mechanisms of ulcer formation and improving treatment options. The purpose of this study was to determine the compressive mechanical properties of the plantar soft tissue in both diabetic and non-diabetic specimens from six relevant locations beneath the foot, namely the hallux (big toe), first, third, and fifth metatarsal heads, lateral midfoot, and calcaneus (heel). Cylindrical specimens (1.905cm diameter) from these locations were excised and separated from the skin and bone from 4 diabetic and 4 non-diabetic age-matched, elderly, fresh-frozen cadaveric feet. Specimens were then subjected to biomechanically realistic strains of ∼50% in compression using triangle wave tests conducted at five frequencies ranging from 1 to 10 Hz to determine tissue modulus, energy loss, and strain rate dependence. Diabetic vs. non-diabetic results across all specimens, locations, and testing frequencies demonstrated altered mechanical properties with significantly increased modulus (1146.7 vs. 593.0kPa) but no change in energy loss (68.5 vs. 67.9%). All tissue demonstrated strain rate dependence and tissue beneath the calcaneus was found to have decreased modulus and energy loss compared to other areas. The results of this study could be used to generate material properties for all areas of the plantar soft tissue in diabetic or non-diabetic feet, with implications for foot computational modeling efforts and potentially for pressure alleviating footwear that could reduce plantar ulcer incidence. PMID:20207359

Evaluation of flexural, diametral tensile, and shear bond strength of composite repairs.

PubMed

Imbery, T A; Gray, T; DeLatour, F; Boxx, C; Best, A M; Moon, P C

2014-01-01

Repairing composite restorations may be a more conservative treatment than replacing the entire restoration. The objective of this in vitro study was to determine the best repair method by measuring flexural, diametral tensile, and shear bond strength of repaired composites in which the surfaces were treated with chemical primers (Add & Bond or Silane Bond Enhancer), a bonding agent (Optibond Solo Plus [OBSP]), or mechanical retention with a bonding agent. Filtek Supreme Ultra shade B1B was placed in special molds to fabricate specimens that served to test the flexural, diametral tensile, or shear strength of the inherent resin substrate. The same molds were modified to make specimens for testing repair strength of the resin. Repairs were made immediately or after aging in deionized water at 37°C for seven days. All repair sites were finished with coarse Sof-Lex discs to simulate finishing new restorations or partially removing aged restorations. Repair surfaces were treated with one of the following: 1) phosphoric-acid etching and OBSP; 2) Add & Bond; 3) phosphoric-acid etching, Silane Bond Enhancer, and OBSP; or 4) quarter round bur, phosphoric-acid etching, and OBSP. Specimens were placed back in the original molds to fabricate specimens for diametral tensile or flexural testing or in an Ultradent jig to make specimens for shear bond testing. Composite resin in shade B5B was polymerized against the treated surfaces to make repairs. Two negative control groups for the three testing methods consisted of specimens in which repairs were made immediately or after aging without any surface treatments. Controls and experimental repairs were aged (water 37°C, 24 hours) before flexural, diametral tensile, or shear testing in an Instron Universal testing machine at a crosshead speed of 0.5 mm/min. Experimental flexural repair strengths ranged from 26.4% to 88.6% of the inherent substrate strength. Diametral tensile repair strengths ranged from 40% to 80% of the inherent substrate strength, and shear bond strength repairs ranged from 56% to 102%. Geometric means were statistically analyzed with two-way analysis of variance on their log-transformed values. Significant differences were determined using Tukey honestly significant difference (p<0.05). Depending on the mechanical property being tested, surface treatments produced different results. OBSP produced more consistent results than chemical primers.

Effects of Curing Temperature and Pressure on the Chemical, Physical, and Mechanical Properties of Portland Cement

NASA Astrophysics Data System (ADS)

Pang, Xueyu

This dissertation mainly focuses on studying the fundamental hydration kinetics and mechanisms of Portland cement as well as the effects of curing temperature and pressure on its various properties. An innovative test apparatus has been developed in this study to cure and test cement paste specimens under in-situ conditions, such as down-hole in oil wells with high temperature and high pressure. Two series of tests were performed using cement pastes prepared with four different classes of oilwell cement (namely Class A, C, G, and H cements). Specimens in groups of four were cured at temperatures ranging from ambient to 60 °C and pressures ranging from 0.69 to 51.7 MPa for a period of 48 or 72 hours. The density and w/c ratio of the specimens at the time of casting as well as at the end of the curing period were recorded. Total chemical shrinkage of the cement paste was measured continuously during the entire hydration period while tensile strength was obtained at the end of the curing period using both water pressure and splitting tension test methods. Due to capacity limitations of the test equipment, in-situ tensile strength was obtained for only one test series with a highest curing pressure of 13.1 MPa. Specimens from the other test series were depressurized before the tensile strength tests. Chemical shrinkage test is an important method of measuring cement hydration kinetics in that the normalized total chemical shrinkage is approximately equal to the degree of cement hydration. By studying the correlations between the chemical shrinkage and the non-evaporable water content of cement during hydration, a multi-linear model is first proposed to estimate the normalization factors for different types of cement under different curing conditions. Based on the hydration kinetics data obtained from chemical shrinkage test results, a new approach of modeling the effect of curing temperature and pressure on cement hydration kinetics is proposed. It is found that when a hydration kinetics curve is represented by an unknown function, the effect of curing condition on the curve can be modeled by incorporating a simple scale factor in this function. The relationship between this scale factor and curing condition is described by chemical kinetics laws. While the proposed new approach of modeling cement hydration kinetics has the advantage of being widely applicable to different types of cement, it only explains one influence factor of cement hydration (i.e. the curing condition). In order to take into account other influence factors and to further understand the fundamental mechanisms of cement hydration, a more complex particle-based numerical hydration model is developed by combining the two well-known cement hydration mechanisms, namely the nucleation and growth controlled mechanism and the diffusion controlled mechanism. The model is applied to experimental data of both C3S hydration in dilute suspensions and Class H cement paste hydration. Excellent agreement is observed between experimental and modeled results. Three rate-controlling parameters with clear physical meanings can be identified from the proposed model. Fitted model parameters are found to be in reasonable agreement with experimental observation. The dependencies of these parameters on particle size, cement composition, w/c ratio, and curing condition are also investigated. Finally, the importance of cement hydration kinetics is illustrated by showing their close correlations with the physical and mechanical properties. The various influence factors, including the curing temperature and pressure, of physical and mechanical property test results (particularly density and tensile strength) are evaluated. Potential damage mechanisms of cement paste specimens during depressurization are studied by analyzing the deformation behavior of the entire system consisting of the cement paste and pressurizing water.

Anisotropic Behaviour of Opalinus Clay Through Consolidated and Drained Triaxial Testing in Saturated Conditions

NASA Astrophysics Data System (ADS)

Favero, Valentina; Ferrari, Alessio; Laloui, Lyesse

2018-05-01

This paper investigates the anisotropic hydro-mechanical behaviour of Opalinus Clay shale, the host material currently being considered for the construction of a nuclear waste repository in Switzerland. Consolidated and drained triaxial tests on Opalinus Clay from the Mont Terri URL have been conducted in order to derive information on its strength and stiffness properties. Opalinus Clay specimens were tested both parallel to bedding (P-specimens) and perpendicular to bedding (S-specimens). The considered effective confining stress range (from 2 to 12 MPa) has been selected in order to reproduce possible in situ stress conditions for the repository. In this work, particular attention has been paid to the experimental procedure in order to ensure consolidated conditions and avoid generation of unwanted excess pore water pressure during drained shearing. The Skempton B parameter has been determined for all the tested specimens in order to ensure saturation. Both single-stage and multistage triaxial testing procedures were adopted in the experimental campaign. The results of the triaxial tests highlight an anisotropic elastic response of Opalinus Clay: S-specimens present a more compliant behaviour than P-specimens. The values of the Young modulus are found to increase with the increase in mean effective stress. The analysis of the peak and ultimate shear strength results reveals that the material behaves in a similar manner regardless of the considered direction of loading (P and S directions) with respect to the bedding orientation. Peak and ultimate failure envelopes for Opalinus Clay were derived for the investigated stress range.

Evaluation of five CAD/CAM materials by microstructural characterization and mechanical tests: a comparative in vitro study.

PubMed

Sonmez, Nesrin; Gultekin, Pinar; Turp, Volkan; Akgungor, Gokhan; Sen, Deniz; Mijiritsky, Eitan

2018-01-08

Polymer infiltrated ceramics and nano-ceramic resins are the new restorative materials which have been developed in order to enhance the adverse properties of glass-matrix ceramics and resin composites. The aim of the present in vitro study was to evaluate the characteristics of various CAD/CAM materials through mechanical, microstructural, and SEM analysis. Five test groups (n = 22) were formed by using the indicated CAD/CAM blocks: VITA Enamic (VITA Zahnfabrik), Lava Ultimate (3 M ESPE), IPS e.max CAD (Ivoclar Vivadent), IPS Empress CAD (Ivoclar Vivadent), and VITA Mark II (VITA Zahnfabrik). Two specimens from each test group were used for XRD and EDS analysis. Remaining samples were divided into two subgroups (n = 10). One subgroup specimens were thermocycled (5 °C to 55 °C, 30s, 10,000 cycles) whereas the other were not. All of the specimens were evaluated in terms of flexural strength, Vickers hardness, and fracture toughness. Results were statistically analyzed using two-way ANOVA, one-way ANOVA, Tukey's HSD, and Student's t tests (α = .05). Fractured specimens were evaluated using SEM. The highest Vickers microhardness value was found for VITA Mark II (p < .001), however flexural strength and fracture toughness results were lowest conversely (p < .05). IPS e.max CAD was found to have the highest flexural strength (p < .001). Fracture toughness of IPS e.max CAD was also higher than other tested block materials (p < .001). Lava Ultimate and VITA Enamic's mechanical properties were affected negatively from thermocycling (p < .05). Microhardness, flexural strength, and fracture toughness values of Lava Ultimate and VITA Enamic were found to be similar to VITA Mark II and IPS Empress CAD groups. It should be realised that simulated aging process seem to affect ceramic-polymer composite materials more significantly than glass ceramics.

Microstructure and mechanical properties of selective laser melted Ti6Al4V alloy

NASA Astrophysics Data System (ADS)

Losertová, M.; Kubeš, V.

2017-11-01

The present work was focused on the properties of porous Ti6Al4V specimens processed by selective laser melting (SLM) and tested in tension and compression before and after heat treatment. The SLM samples were annealed at 955 °C, water quenched and aged at 600 °C with following air cooling. The values of the mechanical tests showed that the samples exhibited high mechanical properties. The anisotropy of tensile and compressive strength was observed, which was related to the occurrence of voids. The plastic properties of specimens were improved by means of the heat treatment that led to the transformation of martensitic to lamellar structure composed of α + β phases. The microstructure of SLM samples were evaluated before and after the heat treatment. The brittle nature of failures of non-heat treated samples can be explained by synergy of martensite presence, microcracks and residual stresses produced by SLM.

Mechanics of Granular Materials (MGM) Test Cell

NASA Technical Reports Server (NTRS)

2004-01-01

Test cells comprise specimen sand contained in a latex membrane (with a grid pattern for CCD cameras) between metal end plates and housed in a water-filled Lexan jacket. Experiment flown on STS-79 and STS-89. Principal Investigator: Dr. Stein Sture.

Ropivacaine alters the mechanical properties of hamstring tendons: In vitro controlled mechanical testing of tendons from living donors.

PubMed

Ollivier, M; Sbihi, J; Sbihi, A; Pithioux, M; Parratte, S; Argenson, J-N

2017-11-01

Intraarticular or periarticular injection of ropivacaine (RI) is an element of current knee surgery practices. The goal of this study was to determine the effects of RI on the mechanical properties of hamstring tendons. We hypothesized that RI would have a detrimental effect on the mechanical properties of periarticular soft tissues METHODS: A tensile test to failure was performed on 120 hamstring tendon segments harvested during ACL reconstruction surgery in 120 patients. Two sets of tensile tests were done. The first evaluated the effect of RI itself on the mechanical properties of tendons: 30 samples were soaked for 1hour in a 2% RI solution and compared to 30 samples soaked in a saline solution (control group). The second evaluated the effect of RI concentration on the mechanical properties of hamstring tendons: 30 samples were soaked for 1hour in a 2% RI solution and 30 samples were soaked in a 7.5% RI solution. In the first test, 29 samples from each group were analyzed as two samples (one in each group) failed at the grip interface. The specimens exposed to 2% RI had lower ultimate tensile strength (Δ=4.4MPa, P=0.001), strain energy (Δ=13MPa, P=0.001) and Young's modulus (Δ=1.6MPa, P=0.02) than the specimens in the control group. There was no significant difference in the strain at failure between groups (Δ=5%, P=0.3). In the second test, one specimen from the 7.5% RI group failed during the preloading and was excluded. There was no significant difference in terms of the load at failure and ultimate tensile stress (Δ=0.45MPa, P=0.6) and strain energy (Δ=0.49MPa, P=0.49) between the two groups. There were significant differences in terms of elongation at failure (Δ=28%, P=0.0003) and Young's modulus (Δ=2.6MPa, P=0.005), with the specimens exposed to 7.5% RI undergoing greater deformation and having a lower Young's modulus. While local RI injections are widely performed in clinical practice, the results of this in vitro study point to short-term alterations of the mechanical properties of hamstring tendons. If these results hold in vivo, this could lead to weakness of the soft tissues exposed to this product, particularly the tendons and ligaments around the injection area. Experimental study. Level 1. Copyright © 2017 Elsevier Masson SAS. All rights reserved.

Tensile and Compressive Constitutive Response of 316 Stainless Steel at Elevated Temperatures

NASA Technical Reports Server (NTRS)

Manson, S. S.; Muralidharan, U.; Halford, G. R.

1983-01-01

Creep rate in compression is lower by factors of 2 to 10 than in tension if the microstructure of the two specimens is the same and are tested at equal temperatures and equal but opposite stresses. Such behavior is characteristic for monotonic creep and conditions involving cyclic creep. In the latter case creep rate in both tension and compression progressively increases from cycle to cycle, rendering questionable the possibility of expressing a time stabilized constitutive relationship. The difference in creep rates in tension and compression is considerably reduced if the tension specimen is first subjected to cycles of tensile creep (reversed by compressive plasticity), while the compression specimen is first subjected to cycles of compressive creep (reversed by tensile plasticity). In both cases, the test temperature is the same and the stresses are equal and opposite. Such reduction is a reflection of differences in microstructure of the specimens resulting from different prior mechanical history.

Characterization of mode 1 and mixed-mode failure of adhesive bonds between composite adherends

NASA Technical Reports Server (NTRS)

Mall, S.; Johnson, W. S.

1985-01-01

A combined experimental and analytical investigation of an adhesively bonded composite joint was conducted to characterize both the static and fatigue beyond growth mechanism under mode 1 and mixed-mode 1 and 2 loadings. Two bonded systems were studied: graphite/epoxy adherends bonded with EC 3445 and FM-300 adhesives. For each bonded system, two specimen types were tested: a double-cantilever-beam specimen for mode 1 loading and a cracked-lapshear specimen for mixed-mode 1 and 2 loading. In all specimens tested, failure occurred in the form of debond growth. Debonding always occurred in a cohesive manner with EC 3445 adhesive. The FM-300 adhesive debonded in a cohesive manner under mixed-mode 1 and 2 loading, but in a cohesive, adhesive, or combined cohesive and adhesive manner under mode 1 loading. Total strain-energy release rate appeared to be the driving parameter for debond growth under static and fatigue loadings.

Device for high spatial resolution chemical analysis of a sample and method of high spatial resolution chemical analysis

DOEpatents

Van Berkel, Gary J.

2015-10-06

A system and method for analyzing a chemical composition of a specimen are described. The system can include at least one pin; a sampling device configured to contact a liquid with a specimen on the at least one pin to form a testing solution; and a stepper mechanism configured to move the at least one pin and the sampling device relative to one another. The system can also include an analytical instrument for determining a chemical composition of the specimen from the testing solution. In particular, the systems and methods described herein enable chemical analysis of specimens, such as tissue, to be evaluated in a manner that the spatial-resolution is limited by the size of the pins used to obtain tissue samples, not the size of the sampling device used to solubilize the samples coupled to the pins.

Optimization of test parameters for quantitative stress measurements using the miniaturized disk-bend test

DOE Office of Scientific and Technical Information (OSTI.GOV)

Meyers, D.E.; Chen, F.C.; Zhang, J.

A recently-developed miniaturized disk-bend test (MDBT) has been successfully used to evaluate the mechanical properties of a variety of materials, using specimens 3 mm in diameter. The load is applied either by a solid ball (the ball-on ring (BOR) mode), or by a hollow cylinder (the ring-on-ring (ROR) mode). They authors have reproduced the yield stresses of ordered intermetallic compounds and the fracture toughness of several ceramics using analytical solutions to the equations of elasticity theory. Despite this success there are several curious features involved in the analysis of data; for example, in previous tests conducted in the BOR modemore » correct values of the yield stress were obtained using the equations appropriate to clamped specimens, whether or not hey were actually clamped in the test fixture. They show that this is ubiquitous to tests in the BOR mode, and does not arise because of frictional constraints at the supporting ring. They have also completed a thorough evaluation of testing in the ROR mode, in which the yield stresses of cold-rolled or annealed AISI type 302 stainless steel were measured using various combinations of specimen thickness and radii of the loading and supporting rings, and compared to those of tensile specimens machined from the same material. The most accurate and reproducible measurements of the yield strength were obtained for specific combinations of specimen thickness and geometry of the apparatus.« less

A Multiscale Material Testing System for In Situ Optical and Electron Microscopes and Its Application

PubMed Central

Ye, Xuan; Cui, Zhiguo; Fang, Huajun; Li, Xide

2017-01-01

We report a novel material testing system (MTS) that uses hierarchical designs for in-situ mechanical characterization of multiscale materials. This MTS is adaptable for use in optical microscopes (OMs) and scanning electron microscopes (SEMs). The system consists of a microscale material testing module (m-MTM) and a nanoscale material testing module (n-MTM). The MTS can measure mechanical properties of materials with characteristic lengths ranging from millimeters to tens of nanometers, while load capacity can vary from several hundred micronewtons to several nanonewtons. The m-MTM is integrated using piezoelectric motors and piezoelectric stacks/tubes to form coarse and fine testing modules, with specimen length from millimeters to several micrometers, and displacement distances of 12 mm with 0.2 µm resolution for coarse level and 8 µm with 1 nm resolution for fine level. The n-MTM is fabricated using microelectromechanical system technology to form active and passive components and realizes material testing for specimen lengths ranging from several hundred micrometers to tens of nanometers. The system’s capabilities are demonstrated by in-situ OM and SEM testing of the system’s performance and mechanical properties measurements of carbon fibers and metallic microwires. In-situ multiscale deformation tests of Bacillus subtilis filaments are also presented. PMID:28777341

Study of plastic strain localization mechanisms caused by nonequilibrium transitions in mesodefect ensembles under high-speed loading

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sokovikov, Mikhail, E-mail: sokovikov@icmm.ru; Chudinov, Vasiliy; Bilalov, Dmitry

2015-10-27

The behavior of specimens dynamically loaded during split Hopkinson (Kolsky) bar tests in a regime close to simple shear conditions was studied. The lateral surface of the specimens was investigated in-situ using a high-speed infrared camera CEDIP Silver 450M. The temperature field distribution obtained at different time allowed one to trace the evolution of plastic strain localization. The process of target perforation involving plug formation and ejection was examined using a high-speed infrared camera and a VISAR velocity measurement system. The microstructure of tested specimens was analyzed using an optical interferometer-profiler and a scanning electron microscope. The development of plasticmore » shear instability regions has been simulated numerically.« less

J and CTOD Estimation Equations for Shallow Cracks in Single Edge Notch Bend Specimens,

DTIC Science & Technology

1993-01-01

Landes, A. Saxena, and J.G. Merkle , eds., American Society for Testing and Materials, pp. 415-432,1989. [7] Kirk, M.T, and Dodds, R.H., "An Analytical...Specimen," Enn&eed fte:w Mechanics, Vol, 18, No. 1, pp. 83 -95, 1983. [11] Sorem, W.A., Dodds, R.H., and Rolfe , S.T., "Effects of Crack Depth on

Constitutive formulations for the mechanical investigation of colonic tissues.

PubMed

Carniel, Emanuele Luigi; Gramigna, Vera; Fontanella, Chiara Giulia; Stefanini, Cesare; Natali, Arturo N

2014-05-01

A constitutive framework is provided for the characterization of the mechanical behavior of colonic tissues, as a fundamental tool for the development of numerical models of the colonic structures. The constitutive analysis is performed by a multidisciplinary approach that requires the cooperation between experimental and computational competences. The preliminary investigation pertains to the review of the tissues histology. The complex structural configuration of the tissues and the specific distributions of fibrous elements entail the nonlinear mechanical behavior and the anisotropic response. The identification of the mechanical properties requires to perform mechanical tests according to different loading situations, as different loading directions. Because of the typical functionality of colon structures, the tissues mechanics is investigated by tensile tests, which are performed on taenia coli and haustra specimens from fresh pig colons. Accounting for the histological investigation and the results from the mechanical tests, a specific hyperelastic framework is provided within the theory of fiber-reinforced composite materials. Preliminary analytical formulations are defined to identify the constitutive parameters by the inverse analysis of the experimental tests. Finite element models of the specimens are developed accounting for the actual configuration of the colon structures to verify the quality of the results. The good agreement between experimental and numerical model results suggests the reliability of the constitutive formulations and parameters. Finally, the developed constitutive analysis makes it possible to identify the mechanical behavior and properties of the different colonic tissues. Copyright © 2013 Wiley Periodicals, Inc.

Properties of materials in high pressure hydrogen at room and elevated temperatures

NASA Technical Reports Server (NTRS)

Harris, J. A., Jr.

1972-01-01

Experimental efforts in this program for this period. Mechanical property tests of wrought and cast nickel-base alloys and one wrought cobalt-base alloy were conducted in 34.5 MN/sq m (5000-psig) helium and hydrogen or hydrogen mixtures. Comparison of test results was made to determine degradation of properties due to the hydrogen environments. All testing was conducted on solid specimens exposed to external gaseous pressure. Specific mechanical properties determined and the testing methods used are summarized.

Microstructural effects on the deformation and fracture of the alloy Ti-25Al-10Nb-3B-1Mo. Final report, 1 July 1988-15 December 1992

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ward, C.H.

1992-12-01

The effects of microstructure and temperature on tensile and fracture behavior were explored for the titanium aluminide alloy Ti-25Al-lONb-3V-lMo (atomic percent). Three microstructures were selected for this study in an attempt to determine the role of the individual microstructural constituents. the three microstructures studied were an alpha-2 + beta processed microstructure with a fine Widmanstaetten microstructure, a beta processed microstructure with a fine Widmanstaetten microstructure, and a beta processed microstructure with a coarse Widmanstaetten microstructure. Tensile testing of both round and flat specimens was conducted in vacuum at elevated temperature and in air at room and elevated temperatures. Extensive fractographymore » and specimen sectioning were used to study tensile deformation and the effects of environment on this alloy. Room temperature fracture toughness testing using compact tension specimens was conducted. Elevated temperature toughness testing was performed using J-bend bar specimens in an air environment. Again, extensive fractography and specimen sectioning were used to study the elevated temperature toughening mechanisms of this alloy.... Titanium, Titanium aluminide, Intermetallic, Fracture toughness, Tensile behavior, Fractography environmental interaction.« less

Rapid repair of severely earthquake-damaged bridge piers with flexural-shear failure mode

NASA Astrophysics Data System (ADS)

Sun, Zhiguo; Wang, Dongsheng; Du, Xiuli; Si, Bingjun

2011-12-01

An experimental study was conducted to investigate the feasibility of a proposed rapid repair technique for severely earthquake-damaged bridge piers with flexural-shear failure mode. Six circular pier specimens were first tested to severe damage in flexural-shear mode and repaired using early-strength concrete with high-fluidity and carbon fiber reinforced polymers (CFRP). After about four days, the repaired specimens were tested to failure again. The seismic behavior of the repaired specimens was evaluated and compared to the original specimens. Test results indicate that the proposed repair technique is highly effective. Both shear strength and lateral displacement of the repaired piers increased when compared to the original specimens, and the failure mechanism of the piers shifted from flexural-shear failure to ductile flexural failure. Finally, a simple design model based on the Seible formulation for post-earthquake repair design was compared to the experimental results. It is concluded that the design equation for bridge pier strengthening before an earthquake could be applicable to seismic repairs after an earthquake if the shear strength contribution of the spiral bars in the repaired piers is disregarded and 1.5 times more FRP sheets is provided.

Modernization of existing VVER-1000 surveillance programs

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kochkin, V.; Erak, D.; Makhotin, D.

2011-07-01

According to generally accepted world practice, evaluation of the reactor pressure vessel (RPV) material behavior during operation is carried out using tests of surveillance specimens. The main objective of the surveillance program consists in insurance of safe RPV operation during the design lifetime and lifetime-extension period. At present, the approaches of pressure vessels residual life validation based on the test results of their surveillance specimens have been developed and introduced in Russia and are under consideration in other countries where vodo-vodyanoi energetichesky reactors- (VVER-) 1000 are in operation. In this case, it is necessary to ensure leading irradiation of surveillancemore » specimens (as compared to the pressure vessel wall) and to provide uniformly irradiated specimen groups for mechanical testing. Standard surveillance program of VVER-1000 has several significant shortcomings and does not meet these requirements. Taking into account program of lifetime extension of VVER-1000 operating in Russia, it is necessary to carry out upgrading of the VVER-1000 surveillance program. This paper studies the conditions of a surveillance specimen's irradiation and upgrading of existing sets to provide monitoring and prognosis of RPV material properties for extension of the reactor's lifetime up to 60 years or more. (authors)« less

Investigation of flaw geometry and loading effects on plane strain fracture in metallic structures

NASA Technical Reports Server (NTRS)

Hall, L. R.; Finger, R. W.

1971-01-01

The effects on fracture and flaw growth of weld-induced residual stresses, combined bending and tension stresses, and stress fields adjacent to circular holes in 2219-T87 aluminum and 5AI-2.5Sn(ELI) titanium alloys were evaluated. Static fracture tests were conducted in liquid nitrogen; fatigue tests were performed in room air, liquid nitrogen, and liquid hydrogen. Evaluation of results was based on linear elastic fracture mechanics concepts and was directed to improving existing methods of estimating minimum fracture strength and fatigue lives for pressurized structure in spacecraft and booster systems. Effects of specimen design in plane-strain fracture toughness testing were investigated. Four different specimen types were tested in room air, liquid nitrogen and liquid hydrogen environments using the aluminum and titanium alloys. Interferometry and holograph were used to measure crack-opening displacements in surface-flawed plexiglass test specimens. Comparisons were made between stress intensities calculated using displacement measurements, and approximate analytical solutions.

Effect of Environment on Stress-Rupture Behavior of a Carbon Fiber-Reinforced Silicon Carbide (C/SiC) Ceramic Matrix Composite

NASA Technical Reports Server (NTRS)

Verrilli, Michael J.; Opila, Elizabeth J.; Calomino, Anthony; Kiser, J. Douglas

2002-01-01

Stress-rupture tests were conducted in air, vacuum, and steam-containing environments to identify the failure modes and degradation mechanisms of a carbon fiber-reinforced silicon carbide (C/SiC) composite at two temperatures, 600 and 1200 C. Stress-rupture lives in air and steam containing environments (50 - 80% steam with argon) are similar for a composite stress of 69 MPa at 1200 C. Lives of specimens tested in a 20% steam/argon environment were about twice as long. For tests conducted at 600 C, composite life in 20% steam/argon was 20 times longer than life in air. Thermogravimetric analysis of the carbon fibers was conducted under similar conditions to the stress-rupture tests. The oxidation rate of the fibers in the various environments correlated with the composite stress-rupture lives. Examination of the failed specimens indicated that oxidation of the carbon fibers was the primary damage mode for specimens tested in air and steam environments at both temperatures.

Mechanical property characterization of intraply hybrid composites

NASA Technical Reports Server (NTRS)

Chamis, C. C.; Lark, R. F.; Sinclair, J. H.

1979-01-01

An investigation was conducted to characterize the mechanical properties of intraply hybrids made from graphite fiber/epoxy matrix (primary composites) hybridized with varying amounts of secondary composites made from S-glass or Kevlar 49 fibers. The tests were conducted using thin laminates having the same thickness. The specimens for these tests were instrumented with strain gages to determine stress-strain behavior. Significant results are included.

Preliminary Analysis of the General Performance and Mechanical Behavior of Irradiated FeCrAl Base Alloys and Weldments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gussev, Maxim N.; Field, Kevin G.; Briggs, Samuel A.

The iron-based, iron-chromium-aluminum (FeCrAl) alloys are promising, robust materials for deployment in current and future nuclear power plants. This class of alloys demonstrates excellent performance in a range of environments and conditions, including high-temperature steam (>1000°C). Furthermore, these alloys have the potential to have prolonged survival under loss-of-coolant accident (LOCA) conditions compared to the more traditional cladding materials that are either Zr-based alloys or austenitic steels. However, one of the issues associated with FeCrAl alloys is cracking during welding. The present project investigates the possibility of mitigating welding-induced cracking via alloying and precise structure control of the weldments; in themore » frame work of the project, several advanced alloys were developed and are being investigated prior to and after neutron irradiation to provide insight into the radiation tolerance and mechanical performance of the weldments. The present report provides preliminary results on the post-irradiation characterization and mechanical tests performed during United States Fiscal Year (FY) 2016. Chapter 1 provides a general introduction, and Chapter 2 describes the alloy compositions, welding procedure, specimen geometry and manufacturing parameters. Also, a brief discussion of the irradiation at the High Flux Isotope Reactor (HFIR) is provided. Chapter 3 is devoted to the analysis of mechanical tests performed at the hot cell facility; tensile curves and mechanical properties are discussed in detail focusing on the irradiation temperature. Limited fractography results are also presented and analyzed. The discussion highlights the limitations of the testing within a hot cell. Chapter 4 underlines the advantages of in-situ testing and discusses the preliminary results obtained with newly developed miniature specimens. Specimens were moved to the Low Activation Materials Development and Analysis (LAMDA) laboratory and prepared for mechanical tests. Tensile tests were conducted at LAMDA using a modern digital image correlation approach allowing for strain distribution analysis. Plastic strain initiation and necking are discussed in detail; a concept of strain rate maps is also introduced and discussed. Follow-on SEM-EBSD and FIBTEM analysis is planned.« less

The Effect of Hole Quality on the Fatigue Life of 2024-T3 Aluminum Alloy Sheet

NASA Technical Reports Server (NTRS)

Everett, Richard A., Jr.

2004-01-01

This paper presents the results of a study whose main objective was to determine which type of fabrication process would least affect the fatigue life of an open-hole structural detail. Since the open-hole detail is often the fundamental building block for determining the stress concentration of built-up structural parts, it is important to understand any factor that can affect the fatigue life of an open hole. A test program of constant-amplitude fatigue tests was conducted on five different sets of test specimens each made using a different hole fabrication process. Three of the sets used different mechanical drilling procedures while a fourth and fifth set were mechanically drilled and then chemically polished. Two sets of specimens were also tested under spectrum loading to aid in understanding the effects of residual compressive stresses on fatigue life. Three conclusions were made from this study. One, the residual compressive stresses caused by the hole-drilling process increased the fatigue life by two to three times over specimens that were chemically polished after the holes were drilled. Second, the chemical polishing process does not appear to adversely affect the fatigue life. Third, the chemical polishing process will produce a stress-state adjacent to the hole that has insignificant machining residual stresses.

An ultra-high temperature testing instrument under oxidation environment up to 1800 °C.

PubMed

Cheng, Xiangmeng; Qu, Zhaoliang; He, Rujie; Ai, Shigang; Zhang, Rubing; Pei, Yongmao; Fang, Daining

2016-04-01

A new testing instrument was developed to measure the high-temperature constitutive relation and strength of materials under an oxidative environment up to 1800 °C. A high temperature electric resistance furnace was designed to provide a uniform temperature environment for the mechanical testing, and the temperature could vary from room temperature (RT) to 1800 °C. A set of semi-connected grips was designed to reduce the stress. The deformation of the specimen gauge section was measured by a high temperature extensometer. The measured results were acceptable compared with the results from the strain gauge method. Meanwhile, tensile testing of alumina was carried out at RT and 800 °C, and the specimens showed brittle fracture as expected. The obtained Young's modulus was in agreement with the reported value. In addition, tensile experiment of ZrB2-20%SiC ceramic was conducted at 1700 °C and the high-temperature tensile stress-strain curve was first obtained. Large plastic deformation up to 0.46% and the necking phenomenon were observed before the fracture of specimen. This instrument will provide a powerful research tool to study the high temperature mechanical property of materials under oxidation and is benefit for the engineering application of materials in aerospace field.

Mechanical characterization of natural building stones: observation of the fracture process zone by ESPI

NASA Astrophysics Data System (ADS)

Calvetti, Francesco; Cardani, Giuliana; Meda, Alberto

1999-09-01

The cultural heritage of many nations consist of a great variety of structures of high intrinsic value, which are often composed of natural building stones (NBS), as granite, limestone, marble and sandstone. The use of accurate inspection devices, such as laser interferometry, allows us to acquire information regarding the mechanical properties and damage (tensile cracks) of NBS, which represents the first step in the restoration process. In this paper, the potential application of an electronic speckle pattern interferometry (ESPI) is shown, with particular attention to the observed displacement field and the crack penetration during laboratory testing. In ESPI, by superimposing a reflected light to a reference digitized image, an interference phenomenon is produced. By comparing two recorded interference patterns (before and after loading), the corresponding deformation can be evaluated. The application of ESPI in several laboratory tests on NBS is presented in this paper. In particular, during bending tests performed on geometrically similar NBS specimens, it was observed that the size and shape of the localized damage zone do not depend on the specimen size. These results allow for an interpretation of the 'size- effect,' which consists of a reduction of nominal strength as the specimen size increases.

Flaw Tolerance in Lap Shear Brazed Joints. Part 1

NASA Technical Reports Server (NTRS)

Flom, Yury; Wang, Li-Qin

2003-01-01

Furnace brazing is a joining process used in the aerospace and other industries to produce strong permanent and hermetic structural joints. As in any joining process, brazed joints have various imperfections and defects. At the present time, our understanding of the influence of the internal defects on the strength of the brazed joints is not adequate. The goal of this 3-part investigation is to better understand the properties and failure mechanisms of the brazed joints containing defects. This study focuses on the behavior of the brazed lap shear joints because of their importance in manufacturing aerospace structures. In Part 1, an average shear strength capability and failure modes of the single lap joints are explored. Stainless steel specimens brazed with pure silver are tested in accordance with the AWS C3.2 standard. Comparison of the failure loads and the ultimate shear strength with the Finite Element Analysis (FEA) of the same specimens as a function of the overlap widths shows excellent correlation between the experimental and calculated values for the defect-free lap joints. A damage zone criterion is shown to work quite well in understanding the failure of the braze joints. In Part 2, the findings of the Part 1 will be verified on the larger test specimens. Also, various flaws will be introduced in the test specimens to simulate lack of braze coverage in the lap joints. Mechanical testing and FEA will be performed on these joints to verify that behavior of the flawed ductile lap joints is similar to joints with a reduced braze area. Finally, in Part 3, the results obtained in Parts 1 and 2 will be applied to the actual brazed structure to evaluate the load-carrying capability of a structural lap joint containing discontinuities. In addition, a simplified engineering procedure will be offered for the laboratory testing of the lap shear specimens.

Phase Transformation and Creep Behavior in Ti50Pd30Ni20 High Temperature Shape Memory Alloy in Compression

NASA Technical Reports Server (NTRS)

Kumar, Parikshith K.; Desai, Uri; Monroe, James; Lagoudas, Dimitris C.; Karaman, Ibrahim; Noebe, Ron; Bigelow, Glenn

2010-01-01

The creep behavior and the phase transformation of Ti50Pd30Ni20 High Temperature Shape Memory Alloy (HTSMA) is investigated by standard creep tests and thermomechanical tests. Ingots of the alloy are induction melted, extruded at high temperature, from which cylindrical specimens are cut and surface polished. A custom high temperature test setup is assembled to conduct the thermomechanical tests. Following preliminary monotonic tests, standard creep tests and thermally induced phase transformation tests are conducted on the specimen. The creep test results suggest that over the operating temperatures and stresses of this alloy, the microstructural mechanisms responsible for creep change. At lower stresses and temperatures, the primary creep mechanism is a mixture of dislocation glide and dislocation creep. As the stress and temperature increase, the mechanism shifts to predominantly dislocation creep. If the operational stress or temperature is raised even further, the mechanism shifts to diffusion creep. The thermally induced phase transformation tests show that actuator performance can be affected by rate independent irrecoverable strain (transformation induced plasticity + retained martensite) as well as creep. The rate of heating and cooling can adversely impact the actuators performance. While the rate independent irrecoverable strain is readily apparent early in the actuators life, viscoplastic strain continues to accumulate over the lifespan of the HTSMA. Thus, in order to get full actuation out of the HTSMA, the heating and cooling rates must be sufficiently high enough to avoid creep.

Cyclic creep and fatigue of TD-NiCr (thoria-dispersion-strengthened nickel-chromium), TD-Ni, and NiCr sheet at 1200 C

NASA Technical Reports Server (NTRS)

Hirschberg, M. H.; Spera, D. A.; Klima, S. J.

1972-01-01

The resistance of thin TD-NiCr sheet to cyclic deformation was compared with that of TD-Ni and a conventional nickel-chromium alloy. Strains were determined by a calibration technique which combines room-temperature strain gage and deflection measurements with high-temperature deflection measurements. Analyses of the cyclic tests using measured tensile and creep-rupture data indicated that the TD-NiCr and NiCr alloy specimens failed by a cyclic creep mechanism. The TD-Ni specimens, on the other hand, failed by a fatigue mechanism.

Mechanical behaviour of cerclage material consisting of silicon rubber.

PubMed

Hinrichsen, G; Eberhardt, A; Springer, H

1979-09-01

Silicon rubber specimens of circular or rectangular cross-section (cross-section area between ca. 2 and 7 mm2) are used as cerclage bands. A series of commercial cerclage elements was investigated for mechanical characteristics, such as stress-strain behaviour and modulus of elasticity, using a tensile-testing machine. Large differences in these properties exist among the various specimens. Moreover, time-dependent effects, such as stress-relaxation, retardation, and creep, were analysed by the present investigations. One has to take into consideration that the initial length and stress of the cerclage band vary significantly with time after the operation.

The effect of zoledronate-containing primer on dentin bonding of a universal adhesive.

PubMed

Zenobi, Walter; Feitosa, Victor Pinheiro; Moura, Maria Elisa Martins; D'arcangelo, Camillo; Rodrigues, Lidiany Karla de Azevedo; Sauro, Salvatore

2018-01-01

To evaluate the bonding ability and nanoleakage of a universal adhesive applied to dentin pre-treated using a zoledronate-containing primer (zol-primer) before and after mechanical load cycling. Flat dentin surfaces obtained from human molars were assigned to one of the following adhesion procedures (n=6): 1-Single Bond Universal (SBU) applied in etch-and-rinse mode; 2- SBU applied as etch-and-rinse after the application of zol-primer; 3- SBU applied in self-etch strategy; 4- SBU applied as self-etch after the use of zol-primer. Half of the specimens were processed for microtensile bond strength test after 24h, while the other half part was submitted to 200,000 mechanical cycles. Further specimens were silver-impregnated and assessed for interface nanoleakage by SEM. Data were analyzed with two-way ANOVA and Tukey's test (p<0.05). At 24h evaluation, the four groups presented similar bond strengths, whilst both groups bonded with etch-and-rinse technique showed significant bond strength reduction after mechanical load (p<0.05), with the highest drop in bond strength for the specimens pre-treated with the zol-primer. No negative effects were found for self-etch strategy (p>0.05) in microtensile test. Lower nanoleakage expression was observed for etch-and-rinse specimens treated with zol-primer. However, noteworthy reduction of adhesive layer thickness was observed when combining the zol-primer with the self-etch bonding approach. It can be concluded that zol-primer should not be used along with a universal adhesive in etch-and-rinse mode, but its application before self-etch application may provide less degradation of the resin-dentin interface. Copyright © 2017 Elsevier Ltd. All rights reserved.

Influence of Dissipated Forming Energy on Flow Curves of Austenitic Stainless Steel

NASA Astrophysics Data System (ADS)

Steinheimer, Rainer; Engel, Bernd

2011-08-01

Finite element (FE) simulations are widely used to design sheet metal forming processes. Flow curves and forming limit curves of the semi-finished goods are required for these computations. Mostly flow curves are obtained by conversions of stress-strain caracteristics from uniaxial tensile tests. In these calculations, uniform strain and stress within the gauge length is postulated until reaching elongation without necking. This precondition is true only if specimens remain homogenous during the test procedure. Effects from dissipated mechanical energy and heat flow on the results of uniaxial tensile tests were examined with specimen made of austenitic stainless steels with practical experiments and FE simulations.

Composite materials for space applications

NASA Technical Reports Server (NTRS)

Rawal, Suraj P.; Misra, Mohan S.; Wendt, Robert G.

1990-01-01

The objectives of the program were to: generate mechanical, thermal, and physical property test data for as-fabricated advanced materials; design and fabricate an accelerated thermal cycling chamber; and determine the effect of thermal cycling on thermomechanical properties and dimensional stability of composites. In the current program, extensive mechanical and thermophysical property tests of various organic matrix, metal matrix, glass matrix, and carbon-carbon composites were conducted, and a reliable database was constructed for spacecraft material selection. Material property results for the majority of the as-fabricated composites were consistent with the predicted values, providing a measure of consolidation integrity attained during fabrication. To determine the effect of thermal cycling on mechanical properties, microcracking, and thermal expansion behavior, approximately 500 composite specimens were exposed to 10,000 cycles between -150 and +150 F. These specimens were placed in a large (18 cu ft work space) thermal cycling chamber that was specially designed and fabricated to simulate one year low earth orbital (LEO) thermal cycling in 20 days. With this rate of thermal cycling, this is the largest thermal cycling unit in the country. Material property measurements of the thermal cycled organic matrix composite laminate specimens exhibited less than 24 percent decrease in strength, whereas, the remaining materials exhibited less than 8 percent decrease in strength. The thermal expansion response of each of the thermal cycled specimens revealed significant reduction in hysteresis and residual strain, and the average CTE values were close to the predicted values.

In situ monitored in-pile creep testing of zirconium alloys

NASA Astrophysics Data System (ADS)

Kozar, R. W.; Jaworski, A. W.; Webb, T. W.; Smith, R. W.

2014-01-01

The experiments described herein were designed to investigate the detailed irradiation creep behavior of zirconium based alloys in the HALDEN Reactor spectrum. The HALDEN Test Reactor has the unique capability to control both applied stress and temperature independently and externally for each specimen while the specimen is in-reactor and under fast neutron flux. The ability to monitor in situ the creep rates following a stress and temperature change made possible the characterization of creep behavior over a wide stress-strain-rate-temperature design space for two model experimental heats, Zircaloy-2 and Zircaloy-2 + 1 wt%Nb, with only 12 test specimens in a 100-day in-pile creep test program. Zircaloy-2 specimens with and without 1 wt% Nb additions were tested at irradiation temperatures of 561 K and 616 K and stresses ranging from 69 MPa to 455 MPa. Various steady state creep models were evaluated against the experimental results. The irradiation creep model proposed by Nichols that separates creep behavior into low, intermediate, and high stress regimes was the best model for predicting steady-state creep rates. Dislocation-based primary creep, rather than diffusion-based transient irradiation creep, was identified as the mechanism controlling deformation during the transitional period of evolving creep rate following a step change to different test conditions.

Experimental data on the properties of natural fiber particle reinforced polymer composite material.

PubMed

Chandramohan, D; Presin Kumar, A John

2017-08-01

This paper presents an experimental study on the development of polymer bio-composites. The powdered coconut shell, walnut shells and Rice husk are used as reinforcements with bio epoxy resin to form hybrid composite specimens. The fiber compositions in each specimen are 1:1 while the resin and hardener composition 10:1 respectively. The fabricated composites were tested as per ASTM standards to evaluate mechanical properties such as tensile strength, flexural strength, shear strength and impact strength are evaluated in both with moisture and without moisture. The result of test shows that hybrid composite has far better properties than single fibre glass reinforced composite under mechanical loads. However it is found that the incorporation of walnut shell and coconut shell fibre can improve the properties.

Fractography and mechanisms of environmentally enhanced fatigue crack propagation of a reactor pressure vessel steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Torronen, K.; Kemppainen, M.

1981-10-01

This paper describes the findings and interpretations of the fractographic survey conducted for the International Cyclic Crack Growth Rate (ICCGR) cooperative group round-robin specimens. Specimens of A533B pressure vessel steel were tested at several laboratories in the United States and elsewhere with the same nominal test parameters. A rather wide scatter of the results was found. A fractographic and metallographic survey was carried out in order to clarify the scatter and to evaluate the micromechanism of the crack growth. The fractographic findings are reported in detail and correlated to the crack growth behavior. A hydrogen-assisted crack propagation mechanism based onmore » the fractography is proposed and applied to the observed crack growth behavior.« less

Experimental Investigation on the Fatigue Mechanical Properties of Intermittently Jointed Rock Models Under Cyclic Uniaxial Compression with Different Loading Parameters

NASA Astrophysics Data System (ADS)

Liu, Yi; Dai, Feng; Dong, Lu; Xu, Nuwen; Feng, Peng

2018-01-01

Intermittently jointed rocks, widely existing in many mining and civil engineering structures, are quite susceptible to cyclic loading. Understanding the fatigue mechanism of jointed rocks is vital to the rational design and the long-term stability analysis of rock structures. In this study, the fatigue mechanical properties of synthetic jointed rock models under different cyclic conditions are systematically investigated in the laboratory, including four loading frequencies, four maximum stresses, and four amplitudes. Our experimental results reveal the influence of the three cyclic loading parameters on the mechanical properties of jointed rock models, regarding the fatigue deformation characteristics, the fatigue energy and damage evolution, and the fatigue failure and progressive failure behavior. Under lower loading frequency or higher maximum stress and amplitude, the jointed specimen is characterized by higher fatigue deformation moduli and higher dissipated hysteresis energy, resulting in higher cumulative damage and lower fatigue life. However, the fatigue failure modes of jointed specimens are independent of cyclic loading parameters; all tested jointed specimens exhibit a prominent tensile splitting failure mode. Three different crack coalescence patterns are classified between two adjacent joints. Furthermore, different from the progressive failure under static monotonic loading, the jointed rock specimens under cyclic compression fail more abruptly without evident preceding signs. The tensile cracks on the front surface of jointed specimens always initiate from the joint tips and then propagate at a certain angle with the joints toward the direction of maximum compression.

Formability and macroscopic shearing of a titanium alloy Ti-6Al-4V under channel die compression

NASA Astrophysics Data System (ADS)

Francillette, Henri; Garand, Christian

2017-10-01

The mechanical behavior of Ti-6Al-4V is analyzed using channel die compression tests at room temperature. Specimens were cut out from a starting sheet in order to consider samples with specific initial crystallographic textures. Three types of specimens are considered in the study using an angle θ defined with the initial directions LD0, TD0 and ND0 of the starting sheet. The following values of θ are considered : 0°, 45° and 90°. Plastic deformations up to 20% are considered. Several experimental techniques are used, namely optical microscopy, SEM and Xray diffraction for texture evolution. The true stress-strain curves are plotted and the shape change of the specimens is analyzed. A macroscopic shearing is observed for one the three types of initial textures considered, notably θ = 45°. To complete the study, the Taylor model is applied in order to compare the activation of the mechanisms of the α phase in the different specimens.

A novel specimen-specific methodology to optimise the alignment of long bones for experimental testing.

PubMed

Cheong, Vee San; Bull, Anthony M J

2015-12-16

The choice of coordinate system and alignment of bone will affect the quantification of mechanical properties obtained during in-vitro biomechanical testing. Where these are used in predictive models, such as finite element analysis, the fidelic description of these properties is paramount. Currently in bending and torsional tests, bones are aligned on a pre-defined fixed span based on the reference system marked out. However, large inter-specimen differences have been reported. This suggests a need for the development of a specimen-specific alignment system for use in experimental work. Eleven ovine tibiae were used in this study and three-dimensional surface meshes were constructed from micro-Computed Tomography scan images. A novel, semi-automated algorithm was developed and applied to the surface meshes to align the whole bone based on its calculated principal directions. Thereafter, the code isolates the optimised location and length of each bone for experimental testing. This resulted in a lowering of the second moment of area about the chosen bending axis in the central region. More importantly, the optimisation method decreases the irregularity of the shape of the cross-sectional slices as the unbiased estimate of the population coefficient of variation of the second moment of area decreased from a range of (0.210-0.435) to (0.145-0.317) in the longitudinal direction, indicating a minimisation of the product moment, which causes eccentric loading. Thus, this methodology serves as an important pre-step to align the bone for mechanical tests or simulation work, is optimised for each specimen, ensures repeatability, and is general enough to be applied to any long bone. Copyright © 2015 Elsevier Ltd. All rights reserved.

Mechanical fatigue resistance of an implantable branched lead system for a distributed set of longitudinal intrafascicular electrodes

NASA Astrophysics Data System (ADS)

Pena, A. E.; Kuntaegowdanahalli, S. S.; Abbas, J. J.; Patrick, J.; Horch, K. W.; Jung, R.

2017-12-01

Objective. A neural interface system has been developed that consists of an implantable stimulator/recorder can with a 15-electrode lead that trifurcates into three bundles of five individual wire longitudinal intrafascicular electrodes. This work evaluated the mechanical fatigue resistance of the branched lead and distributed electrode system under conditions designed to mimic anticipated strain profiles that would be observed after implantation in the human upper arm. Approach. Custom test setups and procedures were developed to apply linear or angular strain at four critical stress riser points on the lead and electrode system. Each test was performed to evaluate fatigue under a high repetition/low amplitude paradigm designed to test the effects of arm movement on the leads during activities such as walking, or under a low repetition/high amplitude paradigm designed to test the effects of more strenuous upper arm activities. The tests were performed on representative samples of the implantable lead system for human use. The specimens were fabricated using procedures equivalent to those that will be used during production of human-use implants. Electrical and visual inspections of all test specimens were performed before and after the testing procedures to assess lead integrity. Main results. Measurements obtained before and after applying repetitive strain indicated that all test specimens retained electrical continuity and that electrical impedance remained well below pre-specified thresholds for detection of breakage. Visual inspection under a microscope at 10×  magnification did not reveal any signs of damage to the wires or silicone sheathing at the stress riser points. Significance. These results demonstrate that the branched lead of this implantable neural interface system has sufficient mechanical fatigue resistance to withstand strain profiles anticipated when the system is implanted in an arm. The novel test setups and paradigms may be useful in testing other lead systems.

In vitro analysis of laser meniscectomy.

PubMed

Vangsness, C T; Akl, Y; Nelson, S J; Liaw, L H; Smith, C F; Marshall, G J

1995-01-01

Partial meniscectomies were performed on 32 fresh human meniscal autopsy specimens. The following laser systems were tested: carbon dioxide (CO2), neodymium:yttrium aluminum garnet (Nd:YAG), potassium titanyl phosphate (KTP), holmium:YAG (Ho:YAG), and excimer. Meniscectomies with these lasers were compared with scalpel, mechanical, and electrocautery meniscectomies. Lasers were applied to specimens in and out of normal saline. Routine hematoxylin and eosin and sirius red sections were prepared for each specimen, and the depths of thermal changes were analyzed. Scanning electron microscopy was used to visualize the meniscectomy interface. Among these specimens, the scalpel and mechanical meniscectomies showed the least extension of cellular changes (range, 10-15 nm). The excimer laser caused the least tissue changes of the lasers tested. Tissue changes were less extensive with the pulsed CO2 laser than with the holmium:YAG, neodymium:YAG, and KTP lasers. Scanning electron microscopy showed that use of the scalpel meniscectomy resulted in the smoothest meniscectomy edge, followed by use of the excimer, CO2, holmium:YAG, neodymium:YAG, and KTP lasers. The most surface disruption occurred with electrocautery. Meniscectomies under saline required more energy and took longer in each case, with the holmium:YAG, neodymium:YAG, and CO2 laser cutting the best. Saline meniscectomies showed less thermal change. The CO2 and KTP lasers cut best in air.

Numerical investigation of the mechanical properties of the additive manufactured bone scaffolds fabricated by FDM: The effect of layer penetration and post-heating.

PubMed

Naghieh, S; Karamooz Ravari, M R; Badrossamay, M; Foroozmehr, E; Kadkhodaei, M

2016-06-01

In recent years, thanks to additive manufacturing technology, researchers have gone towards the optimization of bone scaffolds for the bone reconstruction. Bone scaffolds should have appropriate biological as well as mechanical properties in order to play a decisive role in bone healing. Since the fabrication of scaffolds is time consuming and expensive, numerical methods are often utilized to simulate their mechanical properties in order to find a nearly optimum one. Finite element analysis is one of the most common numerical methods that is used in this regard. In this paper, a parametric finite element model is developed to assess the effects of layers penetration׳s effect on inter-layer adhesion, which is reflected on the mechanical properties of bone scaffolds. To be able to validate this model, some compression test specimens as well as bone scaffolds are fabricated with biocompatible and biodegradable poly lactic acid using fused deposition modeling. All these specimens are tested in compression and their elastic modulus is obtained. Using the material parameters of the compression test specimens, the finite element analysis of the bone scaffold is performed. The obtained elastic modulus is compared with experiment indicating a good agreement. Accordingly, the proposed finite element model is able to predict the mechanical behavior of fabricated bone scaffolds accurately. In addition, the effect of post-heating of bone scaffolds on their elastic modulus is investigated. The results demonstrate that the numerically predicted elastic modulus of scaffold is closer to experimental outcomes in comparison with as-built samples. Copyright © 2016 Elsevier Ltd. All rights reserved.

1000542

NASA Image and Video Library

2010-04-13

HORACE STORNG (AEROSPACE ENGINEER, ER31 PROPULSION TURBOMACHINERY DESIGN & DEVELOPMENT BRANCH) ADJUSTS A UNIQUE MECHANICAL TEST SETUP THAT MEASURES STRAIN ON A SINGLE SAMPLE, USING TWO DIFFERENT TECHNIQUES AT THE SAME TIME. THE TEST FIXTURE HOLDS A SPECIMEN THAT REPRESENTS A LIQUID OXYGEN (LOX) BEARING FROM THE J2-X ENGINE

High Pressure Compression-Molding of α-Cellulose and Effects of Operating Conditions.

PubMed

Pintiaux, Thibaud; Viet, David; Vandenbossche, Virginie; Rigal, Luc; Rouilly, Antoine

2013-05-30

Commercial α-cellulose was compression-molded to produce 1A dog-bone specimens under various operating conditions without any additive. The resulting agromaterials exhibited a smooth, plastic-like surface, and constituted a suitable target as replacement for plastic materials. Tensile and three-points bending tests were conducted according to ISO standards related to the evaluation of plastic materials. The specimens had strengths comparable to classical petroleum-based thermoplastics. They also exhibited high moduli, which is characteristic of brittle materials. A higher temperature and higher pressure rate produced specimens with higher mechanical properties while low moisture content produced weaker specimens. Generally, the strong specimen had higher specific gravity and lower moisture content. However, some parameters did not follow the general trend e.g., thinner specimen showed much higher Young's Modulus, although their specific gravity and moisture content remained similar to control, revealing a marked skin-effect which was confirmed by SEM observations.

High Pressure Compression-Molding of α-Cellulose and Effects of Operating Conditions

PubMed Central

Pintiaux, Thibaud; Viet, David; Vandenbossche, Virginie; Rigal, Luc; Rouilly, Antoine

2013-01-01

Commercial α-cellulose was compression-molded to produce 1A dog-bone specimens under various operating conditions without any additive. The resulting agromaterials exhibited a smooth, plastic-like surface, and constituted a suitable target as replacement for plastic materials. Tensile and three-points bending tests were conducted according to ISO standards related to the evaluation of plastic materials. The specimens had strengths comparable to classical petroleum-based thermoplastics. They also exhibited high moduli, which is characteristic of brittle materials. A higher temperature and higher pressure rate produced specimens with higher mechanical properties while low moisture content produced weaker specimens. Generally, the strong specimen had higher specific gravity and lower moisture content. However, some parameters did not follow the general trend e.g., thinner specimen showed much higher Young’s Modulus, although their specific gravity and moisture content remained similar to control, revealing a marked skin-effect which was confirmed by SEM observations. PMID:28809271

Characterization of Fatigue Damage for Bonded Composite Skin/Stringer Configurations

NASA Technical Reports Server (NTRS)

Paris, Isabelle; Cvitkovich, Michael; Krueger, Ronald

2008-01-01

The fatigue damage was characterized in specimens which consisted of a tapered composite flange bonded onto a composite skin. Quasi-static tension tests were performed first to determine the failure load. Subsequently, tension fatigue tests were performed at 40%, 50%, 60% and 70% of the failure load to evaluate the debonding mechanisms. For four specimens, the cycling loading was stopped at intervals. Photographs of the polished specimen edges were taken under a light microscope to document the damage. At two diagonally opposite corners of the flange, a delamination appeared to initiate at the flange tip from a matrix crack in the top 45deg skin ply and propagated at the top 45deg/-45deg skin ply interface. At the other two diagonally opposite corners, a delamination running in the bondline initiated from a matrix crack in the adhesive pocket. In addition, two specimens were cut longitudinally into several sections. Micrographs revealed a more complex pattern inside the specimen where the two delamination patterns observed at the edges are present simultaneously across most of the width of the specimen. The observations suggest that a more sophisticated nondestructive evaluation technique is required to capture the complex damage pattern of matrix cracking and multi-level delaminations.

Tribosupplementation with Lubricin in Prevention of Post-Traumatic Arthritis

DTIC Science & Technology

2013-10-01

was performed and synovial fluid was collected from the joint for use as a lubricant during mechanical testing. For the Arthroscopy specimens (n=4...arthroscopic irrigation was performed as follows: an arthrotomy was made in the superior capsule and an arthroscopy cannula was introduced. The joint...been cycled through the joint and saved for use as a lubricant during mechanical testing. For both Control and Arthroscopy knees, paired, full

3D FDM production and mechanical behavior of polymeric sandwich specimens embedding classical and honeycomb cores

NASA Astrophysics Data System (ADS)

Brischetto, Salvatore; Ferro, Carlo Giovanni; Torre, Roberto; Maggiore, Paolo

2018-04-01

Desktop 3D FDM (Fused Deposition Modelling) printers are usually employed for the production of nonstructural objects. In recent years, the present authors tried to use this technology also to produce structural elements employed in the construction of small UAVs (Unmanned Aerial Vehicles). Mechanical stresses are not excessive for small multirotor UAVs. Therefore, the FDM technique combined with polymers, such as the ABS (Acrylonitrile Butadiene Styrene) and the PLA(Poly Lactic Acid), can be successfully employed to produce structural components. The present new work is devoted to the production and preliminary structural analysis of sandwich configurations. These new lamination schemes could lead to an important weight reduction without significant decreases of mechanical properties. Therefore, it could be possible, for the designed application (e.g., a multifunctional small UAV produced via FDM), to have stiffener and lighter structures easy to be manufactured with a low-cost 3D printer. The new sandwich specimens here proposed are PLA sandwich specimens embedding a PLA honeycomb core produced by means of the same extruder, multilayered specimens with ABS external layers and an internal homogeneous PLA core using different extruders for the two materials, sandwich specimens with external ABS skins and an internal PLA honeycomb core using different extruders for the two materials, and sandwich specimens where two different extruders have been employed for PLA material used for skins and for the internal honeycomb core. For all the proposed configurations, a detailed description of the production activity is given.Moreover, several preliminary results about three-point bending tests, different mechanical behaviors and relative delamination problems for each sandwich configuration will be discussed in depth.

Microstructural effects on the room and elevated temperature low cycle fatigue behavior of Waspaloy. M.S. Thesis Final Report

NASA Technical Reports Server (NTRS)

Lerch, B. A.

1982-01-01

Longitudinal specimens of Waspaloy containing either coarse grains with small gamma or fine grains with large gamma were tested in air at a frequency of 0.33 Hz or 0.50 Hz. The coarse grained structures exhibited planar slip on (III) planes and precipitate shearing at all temperatures. Cracks initiated by a Stage 1 mechanism and propagated by a striation forming mechanism. At 700 C and 800 C, cleavage and intergranular cracking were observed. Testing at 500 C, 700 C, and 800 C caused precipitation of grain boundary carbides. At 700 C, carbides precipitated on slip bands. The fine grained structures exhibited planar slip on (111) planes. Dislocations looped the large gamma precipitates. This structure led to stress saturation and propagation was observed. Increasing temperatures resulted in increased specimen oxidation for both heat treatments. Slip band and grain boundary oxidation were observed. At 800 C, oxidized grain boundaries were cracked by intersecting slip bands which resulted in intergranular failure. The fine specimens had crack initiation later in the fatigue life, but with more rapid propagation crack propagation.

Plastic deformation in nanoscale gold single crystals and open-celled nanoporous gold

NASA Astrophysics Data System (ADS)

Lee, Dongyun; Wei, Xiaoding; Zhao, Manhong; Chen, Xi; Jun, Seong C.; Hone, James; Kysar, Jeffrey W.

2007-01-01

The results of two sets of experiments to measure the elastic-plastic behaviour of gold at the nanometre length scale are reported. One set of experiments was on free-standing nanoscale single crystals of gold, and the other was on free-standing nanoscale specimens of open-celled nanoporous gold. Both types of specimens were fabricated from commercially available leaf which was either pure Au or a Au/Ag alloy following by dealloying of the Ag. Mechanical testing specimens of a 'dog-bone' shape were fabricated from the leaf using standard lithographic procedures after the leaf had been glued onto a silicon wafer. The thickness of the gauge portion of the specimens was about 100 nm, the width between 250 nm and 300 nm and the length 7 µm. The specimens were mechanically loaded with a nanoindenter (MTS) at the approximate midpoint of the gauge length. The resulting force-displacement curve of the single crystal gold was serrated and it was evident that slip localization occurred on individual slip systems; however, the early stages of the plastic deformation occurred in a non-localized manner. The results of detailed finite element analyses of the specimen suggest that the critical resolved shear stress of the gold single crystal was as high as 135 MPa which would lead to a maximum uniaxial stress of about 500 MPa after several per cent strain. The behaviour of the nanoporous gold was substantially different. It exhibited an apparent elastic behaviour until the point where it failed in an apparently brittle manner, although it is assumed that plastic deformation occurred in the ligaments prior to failure. The average elastic stiffness of three specimens was measured to be Enp = 8.8 GPa and the stress at ultimate failure averaged 190 MPa for the three specimens tested. Scaling arguments suggest that the stress in the individual ligaments could approach the theoretical shear strength. Presented at the IUTAM Symposium on Plasticity at the Micron Scale, Technical University of Denmark, Copenhagen, Denmark.

Compression failure mechanisms of single-ply, unidirectional, carbon-fiber composites

NASA Technical Reports Server (NTRS)

Ha, Jong-Bae; Nairn, John A.

1992-01-01

A single-ply composite compression test was used to study compression failure mechanisms as a function of fiber type, matrix type, and interfacial strength. Composites made with low- and intermediate-modulus fibers (Hercules AS4 and IM7) in either an epoxy (Hercules 3501-6) or a thermoplastic (ULTEM and LARC-TPI) matrix failed by kink banding and out-of-plane slip. The failures proceeded by rapid and catastrophic damage propagation across the specimen width. Composites made with high-modulus fibers (Hercules HMS4/3501-6) had a much lower compression strength. Their failures were characterized by kink banding and longitudinal splitting. The damage propagated slowly across the specimen width. Composites made with fibers treated to give low interfacial strength had low compression strength. These composites typically failed near the specimen ends and had long kink bands.

Influence of High Temperature Treatment on Mechanical Behavior of a Coarse-grained Marble

NASA Astrophysics Data System (ADS)

Rong, G.; Peng, J.; Jiang, M.

2017-12-01

High temperature has a significant influence on the physical and mechanical behavior of rocks. With increasing geotechnical engineering structures concerning with high temperature problems such as boreholes for oil or gas production, underground caverns for storage of radioactive waste, and deep wells for injection of carbon dioxides, etc., it is important to study the influence of temperature on the physical and mechanical properties of rocks. This paper experimentally investigates the triaxial compressive properties of a coarse-grained marble after exposure to different high temperatures. The rock specimens were first heated to a predetermined temperature (200, 400, and 600 oC) and then cooled down to room temperature. Triaxial compression tests on these heat-treated specimens subjected to different confining pressures (i.e., 0, 5, 10, 15, 20, 25, 30, 35, and 40 MPa) were then conducted. Triaxial compression tests on rock specimens with no heat treatment were also conducted for comparison. The results show that the high temperature treatment has a significant influence on the microstructure, porosity, P-wave velocity, stress-strain relation, strength and deformation parameters, and failure mode of the tested rock. As the treatment temperature gradually increases, the porosity slightly increases and the P-wave velocity dramatically decreases. Microscopic observation on thin sections reveals that many micro-cracks will be generated inside the rock specimen after high temperature treatment. The rock strength and Young's modulus show a decreasing trend with increase of the treatment temperature. The ductility of the rock is generally enhanced as the treatment temperature increases. In general, the high temperature treatment weakens the performance of the tested rock. Finally, a degradation parameter is defined and a strength degradation model is proposed to characterize the strength behavior of heat-treated rocks. The results in this study provide useful data for evaluation of rock properties in high temperature condition.

Morphological and mechanical characterization of composite bone cement containing polymethylmethacrylate matrix functionalized with trimethoxysilyl and bioactive glass.

PubMed

Puska, Mervi; Moritz, Niko; Aho, Allan J; Vallittu, Pekka K

2016-06-01

Medical polymers of biostable nature (e.g. polymethylmetacrylate, PMMA) are widely used in various clinical applications. In this study, novel PMMA-based composite bone cement was prepared. Bioactive glass (BAG) particulate filler (30wt%) was added to enhance potentially the integration of bone to the cement. The polymer matrix was functionalized with trimethoxysilyl to achieve an interfacial bond between the matrix and the fillers of BAG. The amount of trimethoxysilyl in the monomer system varied from 0 to 75wt%. The effects of dry and wet (simulated body fluid, SBF at +37°C for 5 weeks) conditions were investigated. In total, 20 groups of specimens were prepared. The specimens were subjected to a destructive mechanical test in compression. Scanning electron microscopy (SEM) and micro-computed tomography (micro-CT) were used to study the surface and the three-dimensional morphology of the specimens. The results of the study indicated that the addition of trimethoxysilyl groups led to the formation of a hybrid polymer matrix which, in lower amounts (<10wt% of total weight), did not significantly affect the compression properties. However, when the specimens stored in dry and wet conditions were compared, the water sorption increased the compression strength (~5-10MPa per test group). At the same time, the water sorption also caused an evident porous structure formation for the specimens containing BAG and siloxane formation in the hybrid polymer matrix. Copyright © 2015 Elsevier Ltd. All rights reserved.

Magnetic and electric bulge-test instrument for the determination of coupling mechanical properties of functional free-standing films and flexible electronics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yu, Zejun; Li, Faxin; Pei, Yongmao, E-mail: peiym@pku.edu.cn, E-mail: fangdn@pku.edu.cn

2014-06-15

For the first time a novel multi-field bulge-test instrument which enables measurements of the biaxial mechanical properties and electro-magnetic-mechanical coupling effect of free-standing films in external magnetic/electric fields was proposed. The oil pressure was designed with two ranges, 0–1 MPa for elastic small deformation and 0–7 MPa for plastic/damage large deformation. A magnetic field that was horizontal and uniform in the film plane was supplied by a hollow cylindrical magnet. The magnitude could be changed from 0 to 10 000 Oe by adjusting the position of the testing film. Meanwhile, an electric field applied on the film was provided by amore » voltage source (Maximum voltage: 1000 V; Maximum current: 1 A). Various signals related to deformation, mechanical loading, magnetic field, and electric field could be measured simultaneously without mutual interference, which was confirmed by the coincidence of the measured P-H curves for titanium (Ti)/nickel (Ni) specimens with/without external fields. A hardening phenomenon under magnetic/electric fields was observed for Ni and lead zirconate titanate specimens. The multi-field bulge-test instrument will provide a powerful research tool to study the deformation mechanism of functional films and flexible electronics in the coupling field.« less

Environmental effects on aluminum fracture

NASA Technical Reports Server (NTRS)

Schwartzberg, F. R.; Shepic, J. A.

1976-01-01

The sustained load stress corrosion cracking (SCC) threshold for aluminum alloy 214 was determined using smooth (sigma sub TH) and precracked (K sub ISCC) specimens, and cyclic load growth behavior in 3.5% NaCl salt solution was studied. The relationship between K sub ISCC and sigma sub TH was also studied. The work showed that 2124-T851 aluminum alloy in plate gage has a moderately high resistance to stress corrosion attack. Experimental results showed that no SCC occurred in the longitudinal and long transverse directions in any of the tests. Some SCC was found by smooth tests in the short transverse direction, and the data were confirmed by two test methods-sigma sub TH = 275 MN/sq m (40 ksi). No SCC was found from compact specimen tests in any direction: surface flaw and center notch specimens evaluated in the short transverse direction exhibited SCC. The data indicate that stress corrosion behavior is defect, size, and stress dependent, but not entirely in accordance with a stress intensity controlled mechanism.

Bithermal fatigue: A simplified alternative to thermomechanical fatigue

NASA Technical Reports Server (NTRS)

Verrilli, Michael J.

1988-01-01

A bithermal fatigue test technique was proposed as a simplified alternative to the thermomechanical fatigue test. Both the thermomechanical cycle and the bithermal technique can be used to study nonisothermal fatigue behavior. The difference between the two cycles is that in a conventional thermomechanical fatigue cycle the temperature is continuously varied concurrently with the applied mechanical strains, but in the bithermal fatigue cycle the specimen is held at zero load during the temperature excursions and all the loads are applied at the two extreme temperatures of the cycle. Experimentally, the bithermal fatigue test technique offers advantages such as ease in synchronizing the temperature and mechanical strain waveforms, in minimizing temperature gradients in the specimen gauge length, and in reducing and interpreting thermal fatigue such as the influence of alternate high and low temperatures on the cyclic stress-strain response characteristics, the effects of thermal state, and the possibility of introducing high- and low-temperature deformation mechanisms within the same cycle. The bithermal technique was used to study nonisothermal fatigue behavior of alloys such as single-crystal PWA 1480, single-crystal Rene N4, cast B1900+Hf, and wrought Haynes 188.

A comparison of the fracture resistance of three machinable ceramics after thermal and mechanical fatigue.

PubMed

Yang, Rui; Arola, Dwayne; Han, Zhihui; Zhang, Xiuyin

2014-10-01

Mechanical and thermal fatigue may affect ceramic restorations in the oral environment. The purpose of this study was to determine the influence of thermal and mechanical cycling on the fracture load and fracture patterns of 3 machinable ceramics. Seventy-two human third molar teeth were prepared for bonding ceramic specimens of Sirona CEREC Blocs, IPS e.maxCAD, or inCoris ZI meso blocks. The 24 specimens of each ceramic were divided into 4 groups (n=6), which underwent no preloading (control), thermocycling (5°C-55°C, 2000 cycles), mechanical cycling (10(5) cycles, 100 N), and thermocycling (5°C-55°C, 2000 cycles) plus mechanical cycling (10(5) cycles, 100 N). The specimens were subsequently loaded to failure, and both stereomicroscopy and scanning electron microscopy were used to investigate the fracture patterns. The data were analyzed with 2-way ANOVA and the Fisher exact probability test (α=.05). Mechanical and thermal cycling had a significant influence on the critical load to failure of the 3 ceramics. No significant difference was found between mechanical cycling for 10(5) times and thermocycling for 2000 times within the same ceramic. The specimens of inCoris ZI experienced significantly higher fracture loads for all the groups. The fracture patterns of the 3 machinable ceramics showed that failure mainly occurred at the cement-dentin interface. The effects of combined thermal and mechanical cycling on the fracture load of ceramics were more significant than any individual mode of cyclic fatigue. Overall, the inCoris ZI resisted thermal and mechanical fatigue better than the Sirona CEREC and IPS e.maxCAD. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

1000538

NASA Image and Video Library

2010-04-13

AYMAN GIRGIS (EM10 MATERIALS TEST ENGINEER, JACOBS ESTS GROUP/JTI) ADJUSTS DUAL LENSES FOR A UNIQUE MECHANICAL TST SETUP THAT MEASURES STRAIN ON A SINGLE SAMPLE, USING TWO DIFFERENT TECHNIQUES AT THE SAME TIME. THE TEST FIXTURE HOLDS A SPECIMEN THAT REPRESENTS A LIQUID OXYGEN (LOX) BEARING FROM THE J2-X ENGINE

1000540

NASA Image and Video Library

2010-04-13

ERIC EARHART (AEROSPACE ENGINEER, ER41 PROPULSION STRUCTURAL & DYNAMICS ANALYSIS BRANCH) DISCUSSES DATA PRODUCED BY A UNIQUE MECHANICAL TEST SETUP THAT MEASURES STRAIN ON A SINGLE SAMPLE, USING TWO DIFFERENT TECHNIQUES AT THE SAME TIME. THE TEST FIXTURE HOLDS A SPECIMEN THAT REPRESENTS A LIQUID OXYGEN (LOX) BEARING FROM THE J2-X ENGINE

Atlas 5013 tank corrosion test

NASA Technical Reports Server (NTRS)

Sutherland, W. M.; Girton, L. D.; Treadway, D. G.

1978-01-01

The type and cause of corrosion in spot welded joints were determined by X-ray and chemical analysis. Fatigue and static tests showed the degree of degradation of mechanical properties. The corrosion inhibiting effectiveness of WD-40 compound and required renewal period by exposing typical joint specimens were examined.

Effects of heat treatments and UV exposures on mechanical properties of 3D printed acrylonitrile butadiene styrene specimens

NASA Astrophysics Data System (ADS)

Hughes, Shawn M.; Alamir, Mohammed; Neas, Brian; Alzahrani, Naif; Asmatulu, Ramazan

2017-04-01

Over the last few years, tremendous amount of research efforts has been conducted on 3D printing materials, methods and systems. Various 3D printer materials in different size, shape and geometry can be used for advanced designs, modeling, and manufacturing for different industrial applications. In the present study, dog bone shape specimen was designed via a CATIA CAD model, and then printed by a 3D printer using a polymeric filament (acrylonitrile butadiene styrene - ABS). Some of the prepared samples were heat treated at 40 °C, 60 °C, and 80 °C for 30 minutes, while the others were exposed to the UV light in a chamber for 0, 5, 10, 15 and 20 days. The surface and mechanical properties of the conditioned samples were determined using water contact angle and tensile test units, respectively. The test results indicated that the heat treatment process increased the mechanical properties; however, the UV exposure tests significantly reduced the water contact angle and properties of the samples. During these studies, undergraduate engineering students were involved in the tests, and gained a lot of hands-on research experiences.

Experimental investigation on the failure of T-joints at elevated temperature under unaxial loading

NASA Astrophysics Data System (ADS)

Bahri, N. F.; Afendi, M.; Razlan, Z. M.; Nor, A.; Baharuddin, S. A.

2017-09-01

In this study, the mechanical properties and maximum failure load of a bulk and T-joints subjected to tensile loading were investigated experimentally. A bulk and the T-joint specimens were fabricated and tested in order to investigate the effects of temperature conditions on the failure of the joints. The adherent and adhesive used for T-joint are 304 L stainless steel and Hysol E 214 HP with the adhesive thickness of 1.0 mm. The tensile test of the bulk specimen and adhesively T-joint were conducted by using a universal testing machine (UTM) at room temperature (RT), 55 °C, 75 °C, 100 °C and 120 °C, respectively. It was found that as the temperature increases, the failure force strength decreases for bulk and T-joint specimen. Data obtained from the tests at 120 °C showed the failure force of the bulk adhesive decreased by approximately 44 % compared to the specimen tested at RT. Next, the bulk of Hysol failure force result was compared with Araldite at RT and 100 °C. Araldite data was taken from the previous study [1]. It has also been found that the bulk for Hysol has higher failure force compared to Araldite at RT and 100 °C.

Effective Size Analysis of the Diametral Compression (Brazil) Test Specimen

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jadaan, Osama M.; Wereszczak, Andrew A

2009-04-01

This study considers the finite element analysis (FEA) simulation and Weibull effective size analysis for the diametral compression (DC) or Brazil specimen loaded with three different push-rod geometries. Those geometries are a flat push-rod, a push-rod whose radius of curvature is larger than that for the DC specimen, and a push-rod whose radius of curvature matches that of the DC specimen. Such established effective size analysis recognizes that the tensile strength of structural ceramics is typically one to two orders of magnitude less than its compressive strength. Therefore, because fracture is much more apt to result from a tensile stressmore » than a compressive one, this traditional analysis only considers the first principal tensile stress field in the mechanically loaded ceramic component for the effective size analysis. The effective areas and effective volumes were computed as function of Weibull modulus using the CARES/Life code. Particular attention was devoted to the effect of mesh sensitivity and localized stress concentration. The effect of specimen width on the stress state was also investigated. The effects of push-rod geometry, the use of steel versus WC push-rods, and considering a frictionless versus no-slip interface between push-rod and specimen on the maximum stresses, where those stresses are located, and the effective area and effective volume results are described. Of the three push-rod geometries, it is concluded that the push-rod (made from WC rather than steel) whose radius of curvature matches that of the DC specimen is the most apt to cause fracture initiation within the specimen's bulk rather than at the loading interface. Therefore, its geometry is the most likely to produce a valid diametral compression strength test. However, the DC specimen remains inefficient in terms of its area and volume efficiencies; namely, the tensile strength of only a few percent of the specimen's entire area or volume is sampled. Given the high probability that a valid (or invalid) test can be proven by ceramic fractographic practices suggests that this test method and specimen is questionable for use with relatively strong structural ceramics.« less

Influence of gaseous hydrogen on the mechanical properties of incoloy 903. [gas-metal interactions/iron alloys

NASA Technical Reports Server (NTRS)

1975-01-01

Solid specimens of the alloy Inconel 903 (iron based alloy) were exposed to four gaseous environments and high temperatures. Air, pure helium, pure hydrogen, and hydrogen and water vapor combined were the gaseous environments employed, and the temperature was 1400 F. Various mechanical property tests (low cycle fatigue, creep-rupture, tensile properties) were performed on the alloy. Results indicate that the hydrogen and water vapor environment cause a sharp reduction in the mechanical properties of the alloy. Photographs of the test equipment used and the microstructure of the tested alloy are included.

Strength of laser welded joints of polypropylene composites

NASA Astrophysics Data System (ADS)

Votrubec, V.; Hisem, P.; Vinšová, L.; Lukášová, V.

2017-11-01

This paper deals with experimental tests of laser welded polypropylene composites. Polymers, such as polypropylene, are often filled with fibres in order to increase their mechanical properties. The welding procedure can also influence material properties nearby weld joints. Therefore the strength of weld joints is lower than strength of primary materials. This effect is proved by realized shear tests. Polymer specimens were filled with 20 % and 40 % of glass fibres and all possible combinations of specimens were welded for experiments. There is also discussed influence of volume fraction of glass fibres in polypropylene on the strength of weld joint.

Residual stress analysis on tensile MMC specimens after loading/unloading tests in several conditions

NASA Astrophysics Data System (ADS)

Giuliani, Alessandra; Albertini, Gianni; Manescu, Adrian

2004-07-01

Residual stresses have been investigated in samples made of AA6061+22% Al2O3 in order to correlate microstructural characteristics with mechanical performances. In particular, the possible occurrence of a brittle fracture induced by an excessive load transfer from the matrix to the reinforcement was investigated. To this end, macrostresses and microstresses were analysed. A neutron diffraction test on 12 specimens submitted to several loading/unloading conditions at different temperatures was performed. These measurements aimed to establish the optimal temperature for the initial extruded billet in pre-heating stage, before forging the final wheel hub.

In situ observation of fracture processes in high-strength concretes and limestone using high-speed X-ray phase-contrast imaging

DOE Office of Scientific and Technical Information (OSTI.GOV)

Parab, Niranjan D.; Guo, Zherui; Hudspeth, Matthew

The mechanical properties and fracture mechanisms of geomaterials and construction materials such as concrete are reported to be dependent on the loading rates. However, the in situ cracking inside such specimens cannot be visualized using traditional optical imaging methods since the materials are opaque. In this study, the in situ sub-surface failure/damage mechanisms in Cor-Tuf (a reactive powder concrete), a high-strength concrete (HSC) and Indiana limestone under dynamic loading were investigated using high-speed synchrotron X-ray phase-contrast imaging. Dynamic compressive loading was applied using a modified Kolsky bar and fracture images were recorded using a synchronized high-speed synchrotron X-ray imaging set-up.more » Three-dimensional synchrotron X-ray tomography was also performed to record the microstructure of the specimens before dynamic loading. In the Cor-Tuf and HSC specimens, two different modes of cracking were observed: straight cracking or angular cracking with respect to the direction of loading. In limestone, cracks followed the grain boundaries and voids, ultimately fracturing the specimen. Cracks in HSC were more tortuous than the cracks in Cor-Tuf specimens. The effects of the microstructure on the observed cracking behaviour are discussed. This article is part of the themed issue ‘Experimental testing and modelling of brittle materials at high strain rates’.« less

Fatigue Behavior of Inconel 718 TIG Welds

NASA Astrophysics Data System (ADS)

Alexopoulos, Nikolaos D.; Argyriou, Nikolaos; Stergiou, Vasillis; Kourkoulis, Stavros K.

2014-08-01

Mechanical behavior of reference and TIG-welded Inconel 718 specimens was examined in the present work. Tensile, constant amplitude fatigue, and fracture toughness tests were performed in ambient temperature for both, reference and welded specimens. Microstructure revealed the presence of coarse and fine-grained heat-affected zones. It has been shown that without any post-weld heat treatment, welded specimens maintained their tensile strength properties while their ductility decreased by more than 40%. It was found that the welded specimens had lower fatigue life and this decrease was a function of the applied fatigue maximum stress. A 30% fatigue life decrease was noticed in the high cycle fatigue regime for the welded specimens while this decrease exceeded 50% in the low cycle fatigue regime. Cyclic stress-strain curves showed that Inconel 718 experiences a short period of hardening followed by softening for all fatigue lives. Cyclic fatigue response of welded specimens' exhibited cyclically stable behavior. Finally, a marginal decrease was noticed in the Mode I fracture toughness of the welded specimens.

Thermal-Fatigue Crack-Growth Characteristics and Mechanical Strain Cycling Behavior of A-286 Discaloy, and 16-25-6 Austenitic Steels

NASA Technical Reports Server (NTRS)

Smith, Robert W.; Smith, Gordon T.

1960-01-01

Thermal-fatigue crack-growth characteristics of notched- and unnotched-disk specimens of A-286, Discaloy, hot-cold worked 16-25-6, and overaged 16-25-6 were experimentally studied. Separately controlled variables were total strain range (0.0043 to 0.0079 in./in.), maximum cycle temperature (1300 and 1100 F), and hold time at maximum temperature (O and 5 min). A limited number of mechanical, push-pull, constant-strain cycle tests at room temperature were made using notched and un-notched bars of the same materials. In these tests the number of cycles to failure as well as the variation of load change with accumulated cycles was measured, and the effects of mean stress were observed. Constant-strain-range mechanical-fatigue tests at room temperature revealed notched-bar fatigue life to be strongly influenced by mean stress. For a specific strain range, the longest fatigue life was always found to be associated with the least-tensile (or most compressive) mean stress. By defining thermal-fatigue life as the number of cycles required to produce a crack area of 6000 square mils, the relative thermal-fatigue resistances of the test materials were established. Notched-disk specimens of A-286 and Discaloy steels exhibited longer fatigue lives than either hot-cold worked or overaged 16-25-6. On the other hand, unnotched-disk specimens of Discaloy and hot-cold worked 16-25-6 had longer lives than A-286 and overaged 16-25-6. Separation of the crack-growth data into microstage and macrostage periods revealed that the macrostage period accounted for the greatest part of the difference among materials when tested in the notched configuration, while the microstage was largely responsible for the differences encountered in unnotched disks.

Development of Cone Wedge Ring Expansion Test to Evaluate Mechanical Properties of Clad Tubing Structure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Jy-An John

To determine the hoop tensile properties of irradiated fuel cladding in a hot cell, a cone wedge ring expansion test method was developed. A four-piece wedge insert was designed with tapered angles matched to the cone shape of a loading piston. The ring specimen was expanded in the radial direction by the lateral expansion of the wedges under the downward movement of the piston. The advantages of the proposed method are that implementation of the test setup in a hot cell is simple and easy, and that it enables a direct strain measurement of the test specimen from the piston’smore » vertical displacement soon after the wedge-clad contact resistance is initiated.« less

Mechanisms of deformation and fracture in high temperature low cycle fatigue of Rene 80 and IN 100

NASA Technical Reports Server (NTRS)

Romanoski, G. R., Jr.

1982-01-01

Specimens tested for the AGARD strain range partitioning program were investigated. Rene 80 and IN 100 were tested in air and in vacuum; at 871 C, 925 C, and 1000 C; and in the coated and uncoated condition. The specimens exhibited a multiplicity of high-temperature low-cycle fatigue damage. Observations of the various forms of damage were consistent with material and testing conditions and were generally in agreement with previous studies. In every case observations support a contention that failure occurs at a particular combination of crack length and maximum stress. A failure criterion which is applicable in the regime of testing studied is presented. The predictive capabilities of this criterion are straight forward.

Charpy Impact Energy and Microindentation Hardness of 60-NITINOL

NASA Technical Reports Server (NTRS)

Stanford, Malcolm K.

2012-01-01

60-NITINOL (60 wt.% Ni 40 wt.% Ti) is being studied as a material for advanced aerospace components. The Charpy impact energy and microindentation hardness has been studied for this material, fabricated by vacuum induction skull melting (casting) and by hot isostatic pressing. Test specimens were prepared in various hardened and annealed heat treatment conditions. The average impact energy ranged from 0.33 to 0.49J for the hardened specimens while the annealed specimens had impact energies ranging from 0.89 to 1.18J. The average hardness values of the hardened specimens ranged from 590 to 676 HV while that of the annealed specimens ranged from 298 to 366 HV, suggesting an inverse relationship between impact energy and hardness. These results are expected to provide guidance in the selection of heat treatment processes for the design of mechanical components.

Dynamic Loading of Carrara Marble in a Heated State

NASA Astrophysics Data System (ADS)

Wong, Louis Ngai Yuen; Li, Zhihuan; Kang, Hyeong Min; Teh, Cee Ing

2017-06-01

Useable land is a finite space, and with a growing global population, countries have been exploring the use of underground space as a strategic resource to sustain the growth of their society and economy. However, the effects of impact loading on rocks that have been heated, and hence the integrity of the underground structure, are still not fully understood and has not been included in current design standards. Such scenarios include traffic accidents and explosions during an underground fire. This study aims to provide a better understanding of the dynamic load capacity of Carrara marble at elevated temperatures. Dynamic uniaxial compression tests are performed on Carrara marble held at various temperatures using a split-Hopkinson Pressure Bar (SHPB) setup with varying input force. A customized oven is included in the SHPB setup to allow for testing of the marble specimens in a heated state. After the loading test, a three-wave analysis is performed to obtain the dynamic stress-strain curve of the specimen under loading. The fragments of the failed specimens were also collected and dry-sieved to obtain the particle size distribution. The results reveal that the peak stress of specimens that have been heated is negatively correlated with the heating temperature. However, the energy absorbed by the specimens at peak stress at all temperatures is similar, indicating that a significant amount of energy is dissipated via plastic deformation. Generally, fragment size is also found to show a negative correlation with heating temperature and loading pressure. However, in some cases this relationship does not hold true, probably due to the occurrence of stress shadowing. Linear Elastic Fracture Mechanics has been found to be generally applicable to specimens tested at low temperatures; but at higher temperatures, Elastic-Plastic Fracture Mechanics will give a more accurate prediction. Another contribution of this study is to show that other than the peak stress of the rock failure type, the strain history experienced by the rock during impact and the post-impact fragment size distribution are also significant distinguishing features of damage caused by dynamic loading on heated rocks.

Development of a thermally-assisted piercing (TAP) process for introducing holes into thermoplastic composites

NASA Astrophysics Data System (ADS)

Brown, Nicholas W. A.

Composite parts can be manufactured to near-net shape with minimum wastage of material; however, there is almost always a need for further machining. The most common post-manufacture machining operations for composite materials are to create holes for assembly. This thesis presents and discusses a thermally-assisted piercing process that can be used as a technique for introducing holes into thermoplastic composites. The thermally-assisted piercing process heats up, and locally melts, thermoplastic composites to allow material to be displaced around a hole, rather than cutting them out from the structure. This investigation was concerned with how the variation of piercing process parameters (such as the size of the heated area, the temperature of the laminate prior to piercing and the geometry of the piercing spike) changed the material microstructure within carbon fibre/Polyetheretherketone (PEEK) laminates. The variation of process parameters was found to significantly affect the formation of resin rich regions, voids and the fibre volume fraction in the material surrounding the hole. Mechanical testing (using open-hole tension, open-hole compression, plain-pin bearing and bolted bearing tests) showed that the microstructural features created during piercing were having significant influence over the resulting mechanical performance of specimens. By optimising the process parameters strength improvements of up to 11% and 21% were found for pierced specimens when compared with drilled specimens for open-hole tension and compression loading, respectively. For plain-pin and bolted bearing tests, maximum strengths of 77% and 85%, respectively, were achieved when compared with drilled holes. Improvements in first failure force (by 10%) and the stress at 4% hole elongation (by 18%), however, were measured for the bolted bearing tests when compared to drilled specimens. The overall performance of pierced specimens in an industrially relevant application ultimately depends on the properties required for that specific scenario. The results within this thesis show that the piercing technique could be used as a direct replacement to drilling depending on this application.

Mechanical and microbiological properties and drug release modeling of an etch-and-rinse adhesive containing copper nanoparticles.

PubMed

Gutiérrez, M F; Malaquias, P; Matos, T P; Szesz, A; Souza, S; Bermudez, J; Reis, A; Loguercio, A D; Farago, P V

2017-03-01

To evaluate the effect of addition of copper nanoparticles (CN) at different concentrations into a two-step etch-and-rinse (2-ER) adhesive on antimicrobial activity (AMA), copper release (CR), ultimate tensile strength (UTS), degree of conversion (DC), water sorption (WS), solubility (SO), as well as the immediate (IM) and 1-year resin-dentin bond strength (μTBS) and nanoleakage (NL). Seven adhesives were formulated according to the addition of CN (0, 0.0075, 0.015, 0.06, 0.1, 0.5 and 1wt%) in adhesive. The AMA was evaluated against Streptococcus mutans using agar diffusion assay. For CR, WS and SO, specimens were constructed and tested for 28 days. For UTS, specimens were tested after 24h and 28 days. For DC, specimens were constructed and tested after 24h by FTIR. After enamel removal, the ER was applied to dentin. After composite resin build-ups, specimens were sectioned to obtain resin-dentin sticks. For μTBS and NL, specimens were tested after 24h and 1-year periods. All data were submitted to statistical analysis (α=0.05). The addition of CN provided AMA to the adhesives at all concentrations. Higher CR was observed in adhesives with higher concentration of CN. UTS, DC, WS and SO were not influenced. For μTBS an increase was observed in 0.1 and 0.5% copper group. For NL, a significant decrease was observed in all groups in comparison with control group. After 1-year, no significant reductions of μTBS and no significant increases of NL were observed for copper containing adhesives compared to the control group. The addition of CN in concentrations up to 1wt% in the 2-ER adhesive may be an alternative to provide AMA and preserve the bonding to dentin, without reducing adhesives' mechanical properties evaluated. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Why do nickel-titanium archwires fracture intraorally? Fractographic analysis and failure mechanism of in-vivo fractured wires.

PubMed

Zinelis, Spiros; Eliades, Theodore; Pandis, Nikolaos; Eliades, George; Bourauel, Christoph

2007-07-01

The aim of this study was to characterize intraorally fractured nickel-titanium (Ni-Ti) archwires, determine the type of fracture, assess changes in the alloy's hardness and structure, and propose a mechanism of failure. Eleven Ni-Ti SE 200 and 19 copper-Ni-Ti (both, Ormco, Glendora, Calif) intraorally fractured archwires were collected. The location of fracture (anterior or posterior), wire type, cross section, and period of service before fracture were recorded. The retrieved wires and brand-, type-, and size-matched specimens of unused wires were subjected to scanning electron microscopy to assess the fracture type and morphological variation of fracture site of retrieved specimens, and to Vickers hardness (HV200) testing to investigate the hardness of as-received and in-vivo fractured specimens. Fracture site distribution was statistically analyzed with the chi-square test (alpha = 0.05), whereas the results of the hardness testing were analyzed with 2-way ANOVA with state (control vs in-vivo fractured) and composition (Ni-Ti SE vs copper-Ni-Ti) serving as discriminating variables and the Student-Newman-Keuls test at the 95% confidence level. The fracture site distribution showed a preferential location at the midspan between the premolar and the molar, suggesting that masticatory forces and complex loading during engagement of the wire to the bracket slot and potential intraoral aging might account for fracture incidence. All retrieved wires had the distinct features of brittle fracture without plastic deformation or crack propagation, whereas no increase in hardness was observed for the retrieved specimens. Most fractures sites were in the posterior region of the arch, probably because of the high-magnitude masticatory forces. Brittle fracture without plastic deformation was observed in most Ni-Ti wires regardless of archwire composition. There was no increase in the hardness of the intraorally exposed specimens regardless of wire type. This contradicts previous in-vitro studies and rules out hydrogen embrittlement as the cause of fracture.

Creep Behavior and Durability of Cracked CMC

NASA Technical Reports Server (NTRS)

Bhatt, R. T.; Fox, Dennis; Smith, Craig

2015-01-01

To understand failure mechanisms and durability of cracked Ceramic matrix composites (CMCs), Melt Infiltration (MI) SiCSiC composites with Sylramic-iBN fibers and full Chemical vapour infiltration SiCSiC composites with Sylramic-ion bombarded BN (iBN) and Hi-Nicalon -S fibers were pre-cracked between 150 to 200 megapascal and then creep and Sustained Peak Low Cycle Fatigue (SPLCF) tested at 13150 C at stress levels from 35 to 103 megapascal for up to 200 hours under furnace and burner rig conditions. In addition creep testing was also conducted on pre-cracked full Chemical vapour infiltration SiCSiC composites at 14500 C between 35 and 103 megapascal for up to 200 hours under furnace conditions. If the specimens survived the 200 hour durability tests, then they were tensile tested at room temperature to determine their residual tensile properties. The failed specimens were examined by Scanning electron microscope (SEM) to determine the failure modes and mechanisms. The influence of crack healing matrix, fiber types, crack density, testing modes and interface oxidation on durability of cracked Ceramic matrix composites (CMCs) will be discussed.

Contribution of postpolymerization conditioning and storage environments to the mechanical properties of three interim restorative materials.

PubMed

Thompson, Geoffrey A; Luo, Qing

2014-09-01

Because polymer-based interim restorative materials are weak, even well-made restorations sometimes fail before the definitive restoration is ready for insertion. Therefore, knowing which fabrication procedures and service conditions affect mechanical properties is important, particularly over an extended period. The purpose of this study was to evaluate the effect of thermal treatment, surface sealing, thermocycling, storage media, storage temperature, and age on autopolymerizing poly(methylmethacrylate) and bis-acryl interim restorative materials. Outcome measures were flexural strength, Vickers surface microhardness, and impact strength. Flexural strength and microhardness of poly(methylmethacrylate) (Jet Acrylic) and 2 bis-acryl-composite resin (Protemp 3 Garant and Integrity) interim restorative materials were evaluated as affected by storage media, storage temperature, storage time, thermocycling, postpolymerization thermal treatment, or application of a surface sealer. In total, 2880 beam specimens (25×2×2 mm) were fabricated. Mechanical property analyses were made at 10 days, 30 days, 6 months, and 1 year after specimen preparation. Flexural strength was determined by using a 3-point bending test in a universal testing machine with a 1 kN load cell at a crosshead speed of 5.0 mm min(-1). Fracture specimens were recovered and used for determining Vickers microhardness. Measurements were made with a 0.1 N load and 15 second dwell time. Three microhardness measurements were made for each specimen, and the mean was used for reporting Vickers microhardness. Notched impact specimens (64×12.7×6.35 mm) were fabricated from Jet, Protemp 3 Garant, and Integrity interim restorative materials, yielding 288 impact specimens. Impact strengths were assessed at 10 days, 30 days, 6 months, and 1 year with a 2 J pendulum. The effects of the various experimental treatments were determined and rank ordered with analysis of variance, F ratios, and least square means differences Student t tests (α=.05). All experimental treatments investigated had significant effects on flexural strength, with material (P<.001) and thermocycling (P<.001) being dominant. Moreover, all experimental treatments investigated had a significant overall impact on Vickers microhardness with material (P<.001) and Palaseal glaze (P<.001) showing large effects. Material (P<.001) and age (P=.010) had a significant effect on impact strength. Mechanical properties of some interim polymeric materials can be improved by postpolymerization heat treatments or surface glazing. This procedure may extend the useful lifetime of some bis-acryl interim restorations. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Mechanical properties and ultrastructural characteristics of a glass fiber-reinforced composite.

PubMed

García Barbero, Alvaro Enrique; Vera González, Vicente; García Barbero, Ernesto; Aliaga Vera, Ignacio

2015-06-01

To examine the ultrastructural characteristics of a fiber-reinforced composite (FRC) and its behavior in vitro as a framework for fixed partial dentures (FPDs). A total of 40 specimens were prepared using extracted teeth fixed in methacrylate blocks as supports for the FPD, then the specimens were divided into four groups depending on whether a retaining box was used to fix the FPD to the support teeth, and on whether a composite pontic was assembled on top of the fibers. Fracture testing was performed in a universal testing machine (1 mm/minute). Fracture strength values and failure types were statistically compared for each group. Using retaining boxes did not improve the mechanical behavior of the restorative system. The weakest element of the system was the composite tooth constructed on top of the FRC.

Mechanical Properties Optimization of Poly-Ether-Ether-Ketone via Fused Deposition Modeling.

PubMed

Deng, Xiaohu; Zeng, Zhi; Peng, Bei; Yan, Shuo; Ke, Wenchao

2018-01-30

Compared to the common selective laser sintering (SLS) manufacturing method, fused deposition modeling (FDM) seems to be an economical and efficient three-dimensional (3D) printing method for high temperature polymer materials in medical applications. In this work, a customized FDM system was developed for polyether-ether-ketone (PEEK) materials printing. The effects of printing speed, layer thickness, printing temperature and filling ratio on tensile properties were analyzed by the orthogonal test of four factors and three levels. Optimal tensile properties of the PEEK specimens were observed at a printing speed of 60 mm/s, layer thickness of 0.2 mm, temperature of 370 °C and filling ratio of 40%. Furthermore, the impact and bending tests were conducted under optimized conditions and the results demonstrated that the printed PEEK specimens have appropriate mechanical properties.

Energy absorption in composite materials for crashworthy structures

NASA Technical Reports Server (NTRS)

Farley, Gary L.

1987-01-01

Crash energy-absorption processes in composite materials have been studied as part of a research program aimed at the development of energy absorbing subfloor beams for crashworthy military helicopters. Based on extensive tests on glass/epoxy, graphite/epoxy, and Kevlar/epoxy composites, it is shown that the energy-absorption characteristics and crushing modes of composite beams are similar to those exhibited by tubular specimens of similar material and architecture. The crushing mechanisms have been determined and related to the mechanical properties of the constituent materials and specimen architecture. A simple and accurate method for predicting the energy-absorption capability of composite beams has been developed.

Physical and Mechanical Properties of W-Ni-Fe-Co Metal Foam Modified by Titanium Tungsten Carbide Alloying

NASA Astrophysics Data System (ADS)

Ishchenko, A. N.; Tabachenko, A. N.; Afanas'eva, S. A.; Belov, N. N.; Biryukov, Yu. A.; Burkin, V. V.; D'yachkovskii, A. S.; Rogaev, K. S.; Skosyrskii, A. B.; Yugov, N. T.

2018-02-01

The paper studies physical and mechanical properties of tungsten-nickel-iron-cobalt metal foam alloyed with titanium tungsten carbide. Test specimens are obtained by the liquid phase sintering of powder materials, including those containing tungsten nanopowders. High porosity metal foams are prepared through varying the porosity of powder specimens and the content of filling material. The penetration capability of cylinder projectiles made of new alloys is explored in this paper. It is shown that their penetration depth exceeds that of the prototype with relevant weight and size, made of tungsten-nickel-iron alloy, other factors being equal.

The effect of different fibre volume fraction on mechanical properties of banana/pineapple leaf (PaLF)/glass hybrid composite

NASA Astrophysics Data System (ADS)

Hanafee, Z. M.; Khalina, A.; Norkhairunnisa, M.; Syams, Z. Edi; Liew, K. E.

2017-09-01

This paper investigates the effect of fibre volume fraction on mechanical properties of banana-pineapple leaf (PaLF)-glass reinforced epoxy resin under tensile loading. Uniaxial tensile tests were carried out on specimens with different fibre contents (30%, 40%, 50% in weight). The composite specimens consists of 13 different combinations. The effect of hybridisation between synthetic and natural fibre onto tensile properties was determined and the optimum fibre volume fraction was obtained at 50% for both banana and PaLF composites. Additional 1 layer of woven glass fibre increased the tensile strength of banana-PaLF composite up to 85%.

A study of graphite-epoxy laminate failures due to high transverse shear strains using the multi-span-beam shear test procedure

NASA Technical Reports Server (NTRS)

Jegley, Dawn C.

1989-01-01

The multi-span-beam shear test procedure is used to study failure mechanisms in graphite-epoxy laminates due to high transverse shear strains induced by severe local bending deformations in test specimens. Results of a series of tests on specimens with a variety of stacking sequences, including some with adhesive interleaving, are presented. These results indicate that laminates with stacking sequences with several + or - 45 and 90 deg plies next to each other are more susceptible to failures due to high transverse shear strains than laminates with + or - 45 and 0 deg plies next to each other or with + or - 45 deg plies next to layers of adhesive interleaving. Results of these tests are compared with analytical results based on finite elements.

An Effective Modal Approach to the Dynamic Evaluation of Fracture Toughness of Quasi-Brittle Materials

NASA Astrophysics Data System (ADS)

Ferreira, L. E. T.; Vareda, L. V.; Hanai, J. B.; Sousa, J. L. A. O.; Silva, A. I.

2017-05-01

A modal dynamic analysis is used as the tool to evaluate the fracture toughness of concrete from the results of notched-through beam tests. The dimensionless functions describing the relation between the frequencies and specimen geometry used for identifying the variation in the natural frequency as a function of crack depth is first determined for a 150 × 150 × 500-mm notched-through specimen. The frequency decrease resulting from the propagating crack is modeled through a modal/fracture mechanics approach, leading to determination of an effective crack length. This length, obtained numerically, is used to evaluate the fracture toughness of concrete, the critical crack mouth opening displacements, and the brittleness index proposed. The methodology is applied to tests performed on high-strength concrete specimens. The frequency response for each specimen is evaluated before and after each crack propagation step. The methodology is then validated by comparison with results from the application of other methodologies described in the literature and suggested by RILEM.

Failure modes of single and multi-bolted joint in the pultruded fiber reinforced polymer composite members

NASA Astrophysics Data System (ADS)

Kim, S. Y.; Yoo, J. H.; Kim, H. K.; Shin, K. Y.; Yoon, S. J.

2018-06-01

In this paper, we discussed the structural behavior of bolted lap-joint connections in pultruded FRP structural members. Especially, bolted connections in pultruded FRP members are investigated for their failure modes and strength. Specimens with single and multiple bolt-holes are tested in tension under bolt-loading conditions. All of the specimens are instrumented with strain gages and the load-strain responses are monitored. The failed specimens are examined for the cracks and failure patterns. The purpose of this paper is to predict the failure strength by using the ratio of the results obtained by the experiment and the finite element analysis. In the study, several tests are conducted to determine the mechanical properties of pultruded FRP materials before the main experiment. The results are used in the finite element analysis for single and multiple bolted lap-joint specimens. The results obtained by the experiment are compared with the results obtained by the finite element analysis.

Shear transfer capacity of reinforced concrete exposed to fire

NASA Astrophysics Data System (ADS)

Ahmad, Subhan; Bhargava, Pradeep; Chourasia, Ajay

2018-04-01

Shear transfer capacity of reinforced concrete elements is a function of concrete compressive strength and reinforcement yield strength. Exposure of concrete and steel to elevated temperature reduces their mechanical properties resulting in reduced shear transfer capacity of RC elements. The objective of present study is to find the effect of elevated temperature on shear transfer capacity of reinforced concrete. For this purpose pushoff specimens were casted using normal strength concrete. After curing, specimens were heated to 250°C and 500°C in an electric furnace. Cooled specimens were tested for shear transfer capacity in a universal testing machine. It was found that shear transfer capacity and stiffness (slope of load-slip curve) were reduced when the specimens were heated to 250°C and 500°C. Load level for the initiation of crack slip was found to be decreased as the temperature was increased. A simple analytical approach is also proposed to predict the shear transfer capacity of reinforced concrete after elevated temperature.

High-strain rate tensile characterization of graphite platelet reinforced vinyl ester based nanocomposites using split-Hopkinson pressure bar

NASA Astrophysics Data System (ADS)

Pramanik, Brahmananda

The dynamic response of exfoliated graphite nanoplatelet (xGnP) reinforced and carboxyl terminated butadiene nitrile (CTBN) toughened vinyl ester based nanocomposites are characterized under both dynamic tensile and compressive loading. Dynamic direct tensile tests are performed applying the reverse impact Split Hopkinson Pressure Bar (SHPB) technique. The specimen geometry for tensile test is parametrically optimized by Finite Element Analysis (FEA) using ANSYS Mechanical APDLRTM. Uniform stress distribution within the specimen gage length has been verified using high-speed digital photography. The on-specimen strain gage installation is substituted by a non-contact Laser Occlusion Expansion Gage (LOEG) technique for infinitesimal dynamic tensile strain measurements. Due to very low transmitted pulse signal, an alternative approach based on incident pulse is applied for obtaining the stress-time history. Indirect tensile tests are also performed combining the conventional SHPB technique with Brazilian disk test method for evaluating cylindrical disk specimens. The cylindrical disk specimen is held snugly in between two concave end fixtures attached to the incident and transmission bars. Indirect tensile stress is estimated from the SHPB pulses, and diametrical transverse tensile strain is measured using LOEG. Failure diagnosis using high-speed digital photography validates the viability of utilizing this indirect test method for characterizing the tensile properties of the candidate vinyl ester based nanocomposite system. Also, quasi-static indirect tensile response agrees with previous investigations conducted using the traditional dog-bone specimen in quasi-static direct tensile tests. Investigation of both quasi-static and dynamic indirect tensile test responses show the strain rate effect on the tensile strength and energy absorbing capacity of the candidate materials. Finally, the conventional compressive SHPB tests are performed. It is observed that both strength and energy absorbing capacity of these candidate material systems are distinctively less under dynamic tension than under compressive loading. Nano-reinforcement appears to marginally improve these properties for pure vinyl ester under dynamic tension, although it is found to be detrimental under dynamic compression.

1000539

NASA Image and Video Library

2010-04-13

AYMAN GIRGIS (EM10 MATERIALS TEST ENGINEER, JACOBS ESTS GROUP/JTI) AND ERIC EARHART (AEROSPACE ENGINEER, ER41 PROPULSION STRUCTURAL & DYNAMICS ANALYSIS BRANCH) DISCUSS DATA PRODUCED BY A UNIQUE MECHANICAL TEST SETUP THAT MEASURES STRAIN ON A SINGLE SAMPLE, USING TWO DIFFERENT TECHNIQUES AT THE SAME TIME. THE TEST FIXTURE HOLDS A SPECIMEN THAT REPRESENTS A LIQUID OXYGEN (LOX) BEARING FROM THE J2-X ENGINE.

46 CFR 164.120-7 - Acceptance criteria.

Code of Federal Regulations, 2013 CFR

2013-10-01

... Mechanical & Physical Properties of Glass Cloth Base Plastic Laminate (Lengthwise direction of test specimens is parallel to the warp direction of glass fabric.) (1) Tested Under Standard Conditions: (i... ASTM D 695 241 MPa (35,000 ln/in2). (v) Fire retardant MSC Circ. 1006 Pass. (vi) Water absorption, 24...

46 CFR 164.120-7 - Acceptance criteria.

Code of Federal Regulations, 2014 CFR

2014-10-01

... Mechanical & Physical Properties of Glass Cloth Base Plastic Laminate (Lengthwise direction of test specimens is parallel to the warp direction of glass fabric.) (1) Tested Under Standard Conditions: (i... ASTM D 695 241 MPa (35,000 ln/in2). (v) Fire retardant MSC Circ. 1006 Pass. (vi) Water absorption, 24...

46 CFR 164.120-7 - Acceptance criteria.

Code of Federal Regulations, 2012 CFR

2012-10-01

... Mechanical & Physical Properties of Glass Cloth Base Plastic Laminate (Lengthwise direction of test specimens is parallel to the warp direction of glass fabric.) (1) Tested Under Standard Conditions: (i... ASTM D 695 241 MPa (35,000 ln/in2). (v) Fire retardant MSC Circ. 1006 Pass. (vi) Water absorption, 24...

Is the Dresden technique a mechanical design of choice suitable for the repair of middle third Achilles tendon ruptures? A biomechanical study.

PubMed

de la Fuente, C; Carreño-Zillmann, G; Marambio, H; Henríquez, H

2016-01-01

To compare the mechanical failure of the Dresden technique for Achilles tendon repair with the double modified Kessler technique controlled repair technique. The maximum resistance of the two repair techniques are also compared. A total of 30 Achilles tendon ruptures in bovine specimens were repaired with an Ethibond(®) suture to 4.5cm from the calcaneal insertion. Each rupture was randomly distributed into one of two surgical groups. After repair, each specimen was subjected to a maximum traction test. The mechanical failure (tendon, suture, or knot) rates (proportions) were compared using the exact Fisher test (α=.05), and the maximum resistances using the Student t test (α=.05). There was a difference in the proportions of mechanical failures, with the most frequent being a tendon tear in the Dresden technique, and a rupture of the suture in the Kessler technique. The repair using the Dresden technique performed in the open mode, compared to the Kessler technique, has a more suitable mechanical design for the repair of middle third Achilles tendon ruptures on developing a higher tensile resistance in 58.7%. However, its most common mechanical failure was a tendon tear, which due to inappropriate loads could lead to lengthening of the Achilles tendon. Copyright © 2016 SECOT. Publicado por Elsevier España, S.L.U. All rights reserved.

A high temperature testing system for ceramic composites

NASA Technical Reports Server (NTRS)

Hemann, John

1994-01-01

Ceramic composites are presently being developed for high temperature use in heat engine and space power system applications. The operating temperature range is expected to be 1090 to 1650 C (2000 F to 3000 F). Very little material data is available at these temperatures and, therefore, it is desirable to thoroughly characterize the basic unidirectional fiber reinforced ceramic composite. This includes testing mainly for mechanical material properties at high temperatures. The proper conduct of such characterization tests requires the development of a tensile testing system includes unique gripping, heating, and strain measuring devices which require special considerations. The system also requires an optimized specimen shape. The purpose of this paper is to review various techniques for measuring displacements or strains, preferably at elevated temperatures. Due to current equipment limitations it is assumed that the specimen is to be tested at a temperature of 1430 C (2600F) in an oxidizing atmosphere. For the most part, previous high temperature material characterization tests, such as flexure and tensile tests, have been performed in inert atmospheres. Due to the harsh environment in which the ceramic specimen is to be tested, many conventional strain measuring techniques can not be applied. Initially a brief description of the more commonly used mechanical strain measuring techniques is given. Major advantages and disadvantages with their application to high temperature tensile testing of ceramic composites are discussed. Next, a general overview is given for various optical techniques. Advantages and disadvantages which are common to these techniques are noted. The optical methods for measuring strain or displacement are categorized into two sections. These include real-time techniques. Finally, an optical technique which offers optimum performance with the high temperature tensile testing of ceramic composites is recommended.

Ageing under mechanical stress: first experiments for a silver based multilayer mirror

NASA Astrophysics Data System (ADS)

Lalo, Arnaud; Ravel, Guillaume; Ignat, Michel; Cousin, Bernard; Swain, Michael V.

2017-11-01

Improving materials and devices reliability is a major concern to the spatial industry. Results are reported for satellite mirrors-like specimens consisting in oxide-protected metal systems. Optical coatings were deposited by electron beam evaporation. Mechanical stress fields in multi-layered materials play an important role. The stress state can have far-reaching implications both in kinetics and thermodynamics. Therefore an integrated apparatus with four-point bending equipment was designed. The technique allowed us to exert stress into a film or a system of films on a substrate concurrently with thermal treatment. In order to achieve the first tests performed with the help of the apparatus, various preliminary characterizations were required. The article reports the preliminary micro-mechanical testing of the materials (ultra micro-indentation to evaluate the elastic modulus of the samples materials and wafer curvature technique to determine the specimen residual stress) and the first ageing experiment. Experimental evidence of accelerated ageing under stress is successfully reported.

Influence of Structure and Composition on Dynamic Viscoelastic Property of Cartilaginous Tissue: Criteria for Classification between Hyaline Cartilage and Fibrocartilage Based on Mechanical Function

NASA Astrophysics Data System (ADS)

Miyata, Shogo; Tateishi, Tetsuya; Furukawa, Katsuko; Ushida, Takashi

Recently, many types of methodologies have been developed to regenerate articular cartilage. It is important to assess whether the reconstructed cartilaginous tissue has the appropriate mechanical functions to qualify as hyaline (articular) cartilage. In some cases, the reconstructed tissue may become fibrocartilage and not hyaline cartilage. In this study, we determined the dynamic viscoelastic properties of these two types of cartilage by using compression and shear tests, respectively. Hyaline cartilage specimens were harvested from the articular surface of bovine knee joints and fibrocartilage specimens were harvested from the meniscus tissue of the same. The results of this study revealed that the compressive energy dissipation of hyaline cartilage showed a strong dependence on testing frequency at low frequencies, while that of fibrocartilage did not. Therefore, the compressive energy dissipation that is indicated by the loss tangent could become the criterion for the in vitro assessment of the mechanical function of regenerated cartilage.

Mechanical Behavior of a Hi-Nicalon(tm)/SiC Composite Having a Polycarbosilane Derived Matrix

NASA Technical Reports Server (NTRS)

Hurwitz, Frances I.; Calomino, Anthony M.; McCue, Terry R.

1999-01-01

Polymer infiltration of a rigidized preform, followed by pyrolysis to convert the polymer to a ceramic, potentially offers a lower cost alternative to CVD. It also offers more moderate temperature requirements than melt infiltration approaches, which should minimize potential fiber damage during processing. However, polymer infiltration and pyrolysis results in a more microcracked matrix. Preliminary mechanical property characterization, including elevated temperature (1204 C) tensile, 500 h stress rupture behavior and low cycle fatigue, was conducted on Hi-Nicalon (TM)/Si-C-(O) composites having a dual layer BN/SiC interface and a matrix derived by impregnation and pyrolysis of allylhydridopolycarbosilane (AHPCS). Microstructural evaluation of failure surfaces and of polished transverse and longitudinal cross sections of the failed specimens was used to identify predominant failure mechanisms. In stress rupture testing at 1093 C, the failure was interface dominated, while at 1204 C in both stress rupture and two hour hold/fatigue tests failure was matrix dominated, resulting in specimen delamination.

Effect of molding conditions on fracture mechanisms and stiffness of a composite of grid structure

NASA Astrophysics Data System (ADS)

Nikolaev, V. P.; Pichugin, V. S.; Korobeinikov, A. G.

1999-01-01

Methods of determining a complex of stiffness and deformability characteristics of a composite with rhomb-type grid structure were elaborated. Rhomb-type specimens were used for testing the ribs of the structure in tension, compression, and bending and the nodal points in shear in the plane of the ribs. The effect of additional tensioning of the ribs preceding the curing of the binder was investigated (ten tensioning levels ranging from 8 to 70 N/bundle with a linear density of 390 tex were applied). In testing epoxy-carbon specimens (UKN-5000+EHD-MK) in compression and tension, the failure mode changed depending on the tensioning level, i.e., the presence or absence of delamination and the appearance of "dry" fibers were detected. Dependences of the mechanical properties on tensioning were of a markedly pronounced extreme nature. The methods elaborated allow us to investigate the effect of other molding parameters, as well as the conditions and nature of loading, on the mechanical characteristics of composites.

High-Temperature Adhesive Strain Gage Developed

NASA Technical Reports Server (NTRS)

Pereira, J. Michael; Roberts, Gary D.

1997-01-01

Researchers at the NASA Lewis Research Center have developed a unique strain gage and adhesive system for measuring the mechanical properties of polymers and polymer composites at elevated temperatures. This system overcomes some of the problems encountered in using commercial strain gages and adhesives. For example, typical commercial strain gage adhesives require a postcure at temperatures substantially higher than the maximum test temperature. The exposure of the specimen to this temperature may affect subsequent results, and in some cases may be higher than the glass-transition temperature of the polymer. In addition, although typical commercial strain gages can be used for short times at temperatures up to 370 C, their long-term use is limited to 230 C. This precludes their use for testing some high-temperature polyimides near their maximum temperature capability. Lewis' strain gage and adhesive system consists of a nonencapsulated, unbacked gage grid that is bonded directly to the polymer after the specimen has been cured but prior to the normal postcure cycle. The gage is applied with an adhesive specially formulated to cure under the specimen postcure conditions. Special handling, mounting, and electrical connection procedures were developed, and a fixture was designed to calibrate each strain gage after it was applied to a specimen. A variety of tests was conducted to determine the performance characteristics of the gages at elevated temperatures on PMR-15 neat resin and titanium specimens. For these tests, which included static tension, thermal exposure, and creep tests, the gage and adhesive system performed within normal strain gage specifications at 315 C. An example of the performance characteristics of the gage can be seen in the figure, which compares the strain gage measurement on a polyimide specimen at 315 C with an extensometer measurement.

Subcritical crack growth of selected aerospace pressure vessel materials

NASA Technical Reports Server (NTRS)

Hall, L. R.; Bixler, W. D.

1972-01-01

This experimental program was undertaken to determine the effects of combined cyclic/sustained loads, stress level, and crack shape on the fatigue crack growth rate behavior of cracks subjected to plane strain conditions. Material/environment combinations tested included: 2219-T87 aluminum plate in gaseous helium, room air, and 3.5% NaCl solution at room temperature, liquid nitrogen, and liquid hydrogen; 5Al-2.5 Sn (ELI) titanium plate in liquid nitrogen and liquid hydrogen and 6AL-4V (ELI) STA titanium plate in gaseous helium and methanol at room temperature. Most testing was accomplished using surface flawed specimens instrumented with a clip gage to continuously monitor crack opening displacements at the specimen surface. Tapered double cantilever beam specimens were also tested. Static fracture and ten hour sustained load tests were conducted to determine fracture toughness and apparent threshold stress intensity values. Cyclic tests were performed using sinusoidal loading profiles at 333 MHz (20 cpm) and trapezoidal loading profiles at both 8.3 MHz (0.5 cpm) and 3.3 MHz (0.2 cpm). Data were evaluated using modified linear elastic fracture mechanics parameters.

Strain rate sensitivity of autoclaved aerated concrete from quasi-static regime to shock loading

NASA Astrophysics Data System (ADS)

Mespoulet, Jérôme; Plassard, Fabien; Hereil, Pierre Louis

2015-09-01

The quasi-static mechanical behavior of autoclaved aerated concrete is well-known and can be expressed as a function of its density. There are however not much studies dealing with its dynamic behavior and its damping ability when subjected to a mechanical shock or a blast. This study presents experimental results obtained at the Shock Physics Laboratory of THIOT INGENIERIE company. The test specimens are made of YTONG(TM ) cellular concrete with porosity in the range of 75 to 80%. Experimental tests cover a large strain rate amplitude (higher than 104 s-1) for specimens up to 250 mm. They were carried out with a small compression press and with two facilities dedicated to dynamic material characterization: JUPITER dynamic large press (2 MN, 3 ms rising time) and TITAN multi-caliber single-stage gas gun. Results in un-confined conditions show an increase of the compressive strength when strain rate increases (45% increase at 5.102 s-1) but dynamic tests induce damage early in the experiment. This competition between dynamic strength raise and specimen fracture makes the complete compaction curve determination not to be done in unconfined dynamic condition. A 25% increase of the compressive strength has been observed between unconfined and confined condition in Q.S. regime.

Comprehensive Understanding of Ductility Loss Mechanisms in Various Steels with External and Internal Hydrogen

NASA Astrophysics Data System (ADS)

Takakuwa, Osamu; Yamabe, Junichiro; Matsunaga, Hisao; Furuya, Yoshiyuki; Matsuoka, Saburo

2017-11-01

Hydrogen-induced ductility loss and related fracture morphologies are comprehensively discussed in consideration of the hydrogen distribution in a specimen with external and internal hydrogen by using 300-series austenitic stainless steels (Types 304, 316, 316L), high-strength austenitic stainless steels (HP160, XM-19), precipitation-hardened iron-based super alloy (A286), low-alloy Cr-Mo steel (JIS-SCM435), and low-carbon steel (JIS-SM490B). External hydrogen is realized by a non-charged specimen tested in high-pressure gaseous hydrogen, and internal hydrogen is realized by a hydrogen-charged specimen tested in air or inert gas. Fracture morphologies obtained by slow-strain-rate tensile tests (SSRT) of the materials with external or internal hydrogen could be comprehensively categorized into five types: hydrogen-induced successive crack growth, ordinary void formation, small-sized void formation related to the void sheet, large-sized void formation, and facet formation. The mechanisms of hydrogen embrittlement are broadly classified into hydrogen-enhanced decohesion (HEDE) and hydrogen-enhanced localized plasticity (HELP). In the HEDE model, hydrogen weakens interatomic bonds, whereas in the HELP model, hydrogen enhances localized slip deformations. Although various fracture morphologies are produced by external or internal hydrogen, these morphologies can be explained by the HELP model rather than by the HEDE model.

Observations of Fabric Development in Polycrystalline Ice at Basal Pressures: Methods and Initial Results

NASA Astrophysics Data System (ADS)

Breton, D. J.; Baker, I.; Cole, D. M.

2012-12-01

Understanding and predicting the flow of polycrystalline ice is crucial to ice sheet modeling and paleoclimate reconstruction from ice cores. Ice flow rates depend strongly on the fabric (i.e. the distribution of grain sizes and crystallographic orientations) which evolves over time and enhances the flow rate in the direction of applied stress. The mechanisms for fabric evolution in ice have been extensively studied at atmospheric pressures, but little work has been done to observe these processes at the high pressures experienced deep within ice sheets where long-term changes in ice rheology are expected to have significance. We conducted compressive creep tests on a 917 kg m-3 polycrystalline ice specimen at 20 MPa hydrostatic pressure, thus simulating ~2,000 m depth. Initial specimen grain orientations were random, typical grain diameters were 1.2 mm, and the applied creep stress was 0.3 MPa. Subsequent microstructural analyses on the deformed specimen and a similarly prepared, undeformed specimen allowed characterization of crystal fabric evolution under pressure. Our microstructural analysis technique simultaneously collected grain shape and size data from Scanning Electron Microscope (SEM) micrographs and obtained crystallographic orientation data via Electron BackScatter Diffraction (EBSD). Combining these measurements allows rapid analysis of the ice fabric over large numbers of grains, yielding statistically useful numbers of grain size and full c- and a-axis grain orientation data. The combined creep and microstructural data demonstrate pressure-dependent effects on the mechanical and microstructural evolution of polycrystalline ice. We discuss possible mechanisms for the observed phenomena, and future directions for hydrostatic creep testing.

Mechanical and interfacial characterization of laser welded Co-Cr alloy with different joint configurations

PubMed Central

Kokolis, John; Chakmakchi, Makdad; Theocharopoulos, Antonios; Prombonas, Anthony

2015-01-01

PURPOSE The mechanical and interfacial characterization of laser welded Co-Cr alloy with two different joint designs. MATERIALS AND METHODS Dumbbell cast specimens (n=30) were divided into 3 groups (R, I, K, n=10). Group R consisted of intact specimens, group I of specimens sectioned with a straight cut, and group K of specimens with a 45° bevel made at the one welding edge. The microstructure and the elemental distributions of alloy and welding regions were examined by an SEM/EDX analysis and then specimens were loaded in tension up to fracture. The tensile strength (TS) and elongation (ε) were determined and statistically compared among groups employing 1-way ANOVA, SNK multiple comparison test (α=.05) and Weibull analysis where Weibull modulus m and characteristic strength σο were identified. Fractured surfaces were imaged by a SEM. RESULTS SEM/EDX analysis showed that cast alloy consists of two phases with differences in mean atomic number contrast, while no mean atomic number was identified for welded regions. EDX analysis revealed an increased Cr and Mo content at the alloy-joint interface. All mechanical properties of group I (TS, ε, m and σο) were found inferior to R while group K showed intermediated values without significant differences to R and I, apart from elongation with group R. The fractured surfaces of all groups showed extensive dendritic pattern although with a finer structure in the case of welded groups. CONCLUSION The K shape joint configuration should be preferred over the I, as it demonstrates improved mechanical strength and survival probability. PMID:25722836

Evaluation of fracture toughness of human dentin using elastic-plastic fracture mechanics.

PubMed

Yan, Jiahau; Taskonak, Burak; Platt, Jeffrey A; Mecholsky, John J

2008-01-01

Dentin, the mineralized tissue forming the bulk of the tooth, lies between the enamel and the pulp chamber. It is a rich source of inspiration for designing novel synthetic materials due to its unique microstructure. Most of the previous studies investigating the fracture toughness of dentin have used linear-elastic fracture mechanics (LEFM) that ignores plastic deformation and could underestimate the toughness of dentin. With the presence of collagen (approximately 30% by volume) aiding the toughening mechanisms in dentin, we hypothesize that there is a significant difference between the fracture toughness estimated using LEFM (Kc) and elastic-plastic fracture mechanics (EPFM) (KJc). Single-edge notched beam specimens with in-plane (n=10) and anti-plane (n=10) parallel fractures were prepared following ASTM standard E1820 and tested in three-point flexure. KJc of the in-plane parallel and anti-plane parallel specimens were found to be 3.1 and 3.4 MPa m 1/2 and Kc were 2.4 and 2.5 MPa m 1/2, respectively. The fracture toughness estimated based on KJc is significantly greater than that estimated based on Kc (32.5% on average; p<0.001). In addition, KJc of anti-plane parallel specimens is significantly greater than that of in-plane parallel specimens. We suggest that, in order to critically evaluate the fracture toughness of human dentin, EPFM should be employed.

Rheological Characteristics of Cement Grout and its Effect on Mechanical Properties of a Rock Fracture

NASA Astrophysics Data System (ADS)

Liu, Quansheng; Lei, Guangfeng; Peng, Xingxin; Lu, Chaobo; Wei, Lai

2018-02-01

Grouting reinforcement, which has an obvious strengthening effect on fractured rock mass, has been widely used in various fields in geotechnical engineering. The rheological properties of grout will greatly affect its diffusion radius in rock fractures, and the water-cement ratio is an important factor in determining the grouting flow patterns. The relationship between shear stress and shear rate which could reflect the grout rheological properties, the effects of water-cement ratio, and temperature on the rheological properties of grouting was studied in the laboratory. Besides, a new method for producing fractured rock specimens was proposed and solved the problem of producing natural fractured rock specimens. To investigate the influences of grouting on mechanical properties of a rock fracture, the fractured rock specimens made using the new method were reinforced by grouting on the independent designed grouting platform, and then normal and tangential mechanical tests were carried out on fractured rock specimens. The results showed that the mechanical properties of fractured rock mass are significantly improved by grouting, the peak shear strength and residual strength of rock fractures are greatly improved, and the resistance to deformation is enhanced after grouting. Normal forces affect the tangential behavior of the rock fracture, and the tangential stress strength increases with normal forces. The strength and stability of fractured rock mass are increased by grouting reinforcement.

Pre-aging time dependence of microstructure and mechanical properties in nanostructured Al-2wt%Cu alloy

NASA Astrophysics Data System (ADS)

Azad, Bahram; Borhani, Ehsan

2016-03-01

This work is focused on the effect of pre-aging time on the properties of Al-2wt%Cu alloy processed by accumulative roll bonding (ARB) process. Following aged at 190 °C for 10 or 30 min, the samples were deformed up to a strain of 4.8 by the ARB process. The microstructure evolution was investigated by transmission electron microscope and electron backscattering diffraction analyzes. The results showed that the Al2Cu precipitates were formed with different sizes due to the different pre-aging times and the finer precipitates were more effective on the formation of high angle grain boundaries during the ARB process. The grain size of Aged-10 min and Aged-30 min specimens decreased to 400 nm and 420 nm, respectively, after 6 cycles of the ARB process. Also, the final texture after 6 cycles of the ARB process, shown in the {111} pole figure, were different depending on the starting microstructures. The mechanical properties of specimens were investigated by the Vickers microhardness measurements and the tensile tests. The results showed that the mechanical properties are affected by the starting microstructure. The mechanical properties of Aged-10 min specimen were different compared to Aged-30 min specimen due to the different size of the pre-existing precipitates. Although by continuing process, the precipitates were probably dissolved due to the heavy deformation.

Effect of gloss and heat on the mechanical behaviour of a glass carbomer cement.

PubMed

Menne-Happ, Ulrike; Ilie, Nicoleta

2013-03-01

The effect of gloss and heat on the mechanical behaviour of a recently launched glass carbomer cement (GCP, GCP dental) was evaluated and compared with resin-modified glass ionomer cements (Fuji II LC, GC and Photac Fil Quick Aplicap, 3M ESPE). 120bar-shaped specimens (n=20) were produced, maintained in distilled water at 37°C and tested after one week. The GCP specimens were cured with and without heat application and with and without gloss. The flexural strength and modulus of elasticity in flexural test as well as the micro-mechanical properties (Vickers Hardness, indentation modulus, creep) of the top and bottom surface were evaluated. The amount and size of the fillers, voids and cracks were compared using a light and a scanning electron microscope. In the flexural test, the resin-modified glass ionomer cements performed significantly better than GCP. Fuji II LC and Photac Fil (Weibull parameter: 17.7 and 14.3) proved superior reliability in the flexural test compared to GCP (1.4-2.6). The highest Vickers Hardness and lowest creep were achieved by GCP, whereas Fuji II LC reached the highest indentation modulus. The results of this study proved that relationships exist between the compositions, microstructures and mechanical properties of the cements. Heat treatment and gloss application did not influence the mechanical properties of GCP. The mechanical properties were basically influenced by the type of cement and its microstructure. Considering the measured mechanical properties, there is no need of using gloss or heat when restoring teeth with GCP. Copyright © 2012 Elsevier Ltd. All rights reserved.

Biomechanical Analysis of All-Inside, Arthroscopic Suture Repair Versus Extensor Retinaculum Capsulorrhaphy for Triangular Fibrocartilage Complex Tears With Instability.

PubMed

Patel, Amar A; Alhandi, Ali A; Milne, Edward; Dy, Christopher J; Latta, Loren L; Ouellette, E Anne

2016-03-01

To assess ulnocarpal joint stability after treatment of a peripheral triangular fibrocartilage complex (TFCC) injury with all-inside arthroscopic suture repair (SR), extensor retinaculum capsulorrhaphy with the Herbert sling (HS), and a combination of both (SR+HS). Twelve fresh-frozen, age-matched, upper-extremity specimens intact from the distal humerus were prepared. Nondestructive mechanical testing was performed to assess native ulnocarpal joint stability and load-displacement curves were recorded. A peripheral, ulnar-sided TFCC injury was created with arthroscopic assistance, and mechanical testing was performed. Each specimen was treated with SR or HS and testing was repeated. The 6 specimens treated with SR were then treated with HS (SR+HS), and testing was repeated. We used paired Student t tests for statistical analysis within cohorts. For all cohorts, there was an average increase in ulnar translation after the creation of a peripheral TFCC injury and an average decrease after repair. Herbert sling decreased translation by 21%, SR decreased translation by 12%, and SR+HS decreased translation by 26%. Suture repair plus HS and HS reduce ulnar translation the most after a peripheral TFCC injury, followed by SR alone. Ulnocarpal joint stability should be assessed clinically in patients with peripheral TFCC injury, and consideration should be made for using extensor capsulorrhaphy in isolation or as an adjunct to SR as a treatment option. Copyright © 2016 American Society for Surgery of the Hand. Published by Elsevier Inc. All rights reserved.

Modelling the graphite fracture mechanisms

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jacquemoud, C.; Marie, S.; Nedelec, M.

2012-07-01

In order to define a design criterion for graphite components, it is important to identify the physical phenomena responsible for the graphite fracture, to include them in a more effective modelling. In a first step, a large panel of experiments have been realised in order to build up an important database; results of tensile tests, 3 and 4 point bending tests on smooth and notched specimens have been analysed and have demonstrated an important geometry related effects on the behavior up to fracture. Then, first simulations with an elastic or an elastoplastic bilinear constitutive law have not made it possiblemore » to simulate the experimental fracture stress variations with the specimen geometry, the fracture mechanisms of the graphite being at the microstructural scale. That is the reason why a specific F.E. model of the graphite structure has been developed in which every graphite grain has been meshed independently, the crack initiation along the basal plane of the particles as well as the crack propagation and coalescence have been modelled too. This specific model has been used to test two different approaches for fracture initiation: a critical stress criterion and two criteria of fracture mechanic type. They are all based on crystallographic considerations as a global critical stress criterion gave unsatisfactory results. The criteria of fracture mechanic type being extremely unstable and unable to represent the graphite global behaviour up to the final collapse, the critical stress criterion has been preferred to predict the results of the large range of available experiments, on both smooth and notched specimens. In so doing, the experimental observations have been correctly simulated: the geometry related effects on the experimental fracture stress dispersion, the specimen volume effects on the macroscopic fracture stress and the crack propagation at a constant stress intensity factor. In addition, the parameters of the criterion have been related to experimental observations: the local crack initiation stress of 8 MPa corresponds to the non-linearity apparition on the global behavior observed experimentally and the the maximal critical stress defined for the particle of 30 MPa is equivalent to the fracture stress of notched specimens. This innovative combination of crack modelling and a local crystallographic critical stress criterion made it possible to understand that cleavage initiation and propagation in the graphite microstructure was driven by a mean critical stress criterion. (authors)« less

Interface morphology and mechanical properties of Al-Cu-Al laminated composites fabricated by explosive welding and subsequent rolling process

NASA Astrophysics Data System (ADS)

Hoseini-Athar, M. M.; Tolaminejad, B.

2016-07-01

Explosive welding is a well-known solid state method for joining similar and dissimilar materials. In the present study, tri-layered Al-Cu-Al laminated composites with different interface morphologies were fabricated by explosive welding and subsequent rolling. Effects of explosive ratio and rolling thickness reduction on the morphology of interface and mechanical properties were evaluated through optical/scanning electron microscopy, micro-hardness, tensile and tensile-shear tests. Results showed that by increasing the thickness reduction, bonding strength of specimens including straight and wavy interfaces increases. However, bonding strength of the specimens with melted layer interface decreases up to a threshold thickness reduction, then rapidly increases by raising the reduction. Hardness Values of welded specimens were higher than those of original material especially near the interface and a more uniform hardness profile was obtained after rolling process.

Degradation of Nylon 6,6 Fire-Suppression Casing from Plutonium Glove Boxes Under Alpha and Neutron Irradiation

DOE PAGES

Millsap, Donald W.; Cournoyer, Michael E.; Landsberger, Sheldon; ...

2015-04-23

Nylon 6,6 tensile specimens, conforming to the casing for self-contained fire extinguisher systems, have been irradiated using both an accelerator He ++ ion beam and a 5-Ci PuBe neutron source to model the radiation damage these systems would likely incur over a lifetime of operation within glove boxes. Following irradiation, these samples were mechanically tested using standard practices as described in ASTM D638. The results of the He ++ study indicate that the tensile strength of the nylon specimens undergoes some slight (<10%) degradation while other properties of the samples, such as elongation and tangent modulus, appear to fluctuate withmore » increasing dose levels. The He ++-irradiated specimens also have a noticeable level of discoloration corresponding to increasing levels of dose. The neutron-irradiated samples show a higher degree of mechanical degradation than the He ++-irradiated samples.« less

Interlaboratory study for nickel alloy 625 made by laser powder bed fusion to quantify mechanical property variability.

PubMed

Brown, Christopher U; Jacob, Gregor; Stoudt, Mark; Moylan, Shawn; Slotwinski, John; Donmez, Alkan

2016-08-01

Six different organizations participated in this interlaboratory study to quantify the variability in the tensile properties of Inconel 625 specimens manufactured using laser-powder-bed-fusion additive manufacturing machines. The tensile specimens were heat treated and tensile tests conducted until failure. The properties measured were yield strength, ultimate tensile strength, elastic modulus, and elongation. Statistical analysis revealed that between-participant variability for yield strength, ultimate tensile strength, and elastic modulus values were significantly higher (up to 4 times) than typical within-participant variations. Only between-participant and within-participant variability were both similar for elongation. A scanning electron microscope was used to examine one tensile specimen for fractography. The fracture surface does not have many secondary cracks or other features that would reduce the mechanical properties. In fact, the features largely consist of microvoid coalescence and are entirely consistent with ductile failure.

Interlaboratory study for nickel alloy 625 made by laser powder bed fusion to quantify mechanical property variability

PubMed Central

Brown, Christopher U.; Jacob, Gregor; Stoudt, Mark; Moylan, Shawn; Slotwinski, John; Donmez, Alkan

2017-01-01

Six different organizations participated in this interlaboratory study to quantify the variability in the tensile properties of Inconel 625 specimens manufactured using laser-powder-bed-fusion additive manufacturing machines. The tensile specimens were heat treated and tensile tests conducted until failure. The properties measured were yield strength, ultimate tensile strength, elastic modulus, and elongation. Statistical analysis revealed that between-participant variability for yield strength, ultimate tensile strength, and elastic modulus values were significantly higher (up to 4 times) than typical within-participant variations. Only between-participant and within-participant variability were both similar for elongation. A scanning electron microscope was used to examine one tensile specimen for fractography. The fracture surface does not have many secondary cracks or other features that would reduce the mechanical properties. In fact, the features largely consist of microvoid coalescence and are entirely consistent with ductile failure. PMID:28243032

Interlaboratory Study for Nickel Alloy 625 Made by Laser Powder Bed Fusion to Quantify Mechanical Property Variability

NASA Astrophysics Data System (ADS)

Brown, Christopher U.; Jacob, Gregor; Stoudt, Mark; Moylan, Shawn; Slotwinski, John; Donmez, Alkan

2016-08-01

Six different organizations participated in this interlaboratory study to quantify the variability in the tensile properties of Inconel 625 specimens manufactured using laser powder bed fusion-additive manufacturing machines. The tensile specimens were heat treated and tensile tests were conducted until failure. The properties measured were yield strength, ultimate tensile strength, elastic modulus, and elongation. Statistical analysis revealed that between-participant variability for yield strength, ultimate tensile strength, and elastic modulus values were significantly higher (up to four times) than typical within-participant variations. Only between-participant and within-participant variability were both similar for elongation. A scanning electron microscope was used to examine one tensile specimen for fractography. The fracture surface does not have many secondary cracks or other features that would reduce the mechanical properties. In fact, the features largely consist of microvoid coalescence and are entirely consistent with ductile failure.

Comparative evaluation of the amount of the residual monomer in conventional and deep-frozen heat cure polymethylmethacrylate acrylic resin: An in vitro study.

PubMed

Jadhav, Sonali S; Mahajan, Neerja; Sethuraman, Rajesh

2018-01-01

Heat cure acrylic resin material with reduced monomer content is generally recommended for clinical usage as it leads to improved mechanical, physical, and biocompatibility properties. The purpose of the present study was to evaluate and compare the amount of the residual monomer in the conventional and three different groups of deep-frozen heat cure polymethylmethacrylate (PMMA) acrylic resin. Totally 40 Specimens of heat cure PMMA acrylic resin (DPI India) (10 conventional heat cure and 30 deep frozen) were made using two disc-shaped stainless steel molds and invested into type II dental stone using compression molding technique. Each group contained 10 specimens ( n = 10). Group 1: Control group of conventional polished PMMA specimen stored in water for 24 h at +37°C (10 specimens), Group 2: Deep frozen unpolished PMMA (10 specimens), Group 3: Deep frozen polished PMMA (10 specimens), and Group 4: Deep frozen polished PMMA specimen stored in water for 24 h at +37°C (10 specimens). Amount of the residual monomer content in all the specimens was measured using high-performance liquid chromatography. Data were analyzed using One-Way Analysis of Variance and multiple comparison Tukey's post hoc test (α = 0.05). Least residual monomer content was found in Group 4 (0.12 wt%) followed by Group 3 (0.19 wt%), Group 2 (0.23 wt%), and Group 1 (0.26 wt%). Statistically significant difference ( P < 0.05) was found in residual monomer content for all the four groups tested. Post hoc test for intergroup comparison also showed a significant difference between groups. The amount of the residual monomer was found to be least in deep-frozen polished PMMA specimen stored in water for 24 h at +37°C (Group 4). Thus, it can be concluded that deep freezing, polishing, and storing in water can reduce the residual monomer content.

An Elaborate Data Set Characterizing the Mechanical Response of the Foot

PubMed Central

Erdemir, Ahmet; Sirimamilla, Pavana A.; Halloran, Jason P.; van den Bogert, Antonie J.

2010-01-01

Background Mechanical properties of the foot are responsible for its normal function and play a role in various clinical problems. Specifically, we are interested in quantification of foot mechanical properties to assist the development of computational models for movement analysis and detailed simulations of tissue deformation. Current available data are specific to a foot region and the loading scenarios are limited to a single direction. A data set that incorporates regional response, to quantify individual function of foot components, as well as overall response, to illustrate their combined operation, does not exist. Furthermore, combined three-dimensional loading scenarios while measuring the complete three-dimensional deformation response are lacking. When combined with an anatomical image data set, development of anatomically realistic and mechanically validated models becomes possible. Therefore, the goal of this study was to record and disseminate the mechanical response of a foot specimen, supported by imaging data. Method of Approach Robotic testing was conducted at the rear foot, forefoot, metatarsal heads, and the foot as a whole. Complex foot deformations were induced by single mode loading, e.g. compression, and combined loading, e.g. compression and shear. Small and large indenters were used for heel and metatarsal head loading; an elevated platform was utilized to isolate the rear foot and forefoot; and a full platform compressed the whole foot. Three-dimensional tool movements and reaction loads were recorded simultaneously. Computed tomography scans of the same specimen were collected for anatomical reconstruction a-priori. Results Three-dimensional mechanical response of the specimen was nonlinear and viscoelastic. A low stiffness region was observed starting with contact between the tool and foot regions, increasing with loading. Loading and unloading response portrayed hysteresis. Loading range ensured capturing the toe and linear regions of the load deformation curves for the dominant loading direction, with the rates approximating those of walking. Conclusion A large data set was successfully obtained to characterize the overall as well as regional mechanical response of an intact foot specimen under single and combined loads. Medical imaging complemented the mechanical testing data to establish the potential relationship between the anatomical architecture and mechanical response, and for further development of foot models that are mechanically realistic and anatomically consistent. This combined data set has been documented and disseminated in the public domain to promote future development in foot biomechanics. PMID:19725699

High Temperature Degradation Mechanisms in Polymer Matrix Composites

NASA Technical Reports Server (NTRS)

Cunningham, Ronan A.

1996-01-01

Polymer matrix composites are increasingly used in demanding structural applications in which they may be exposed to harsh environments. The durability of such materials is a major concern, potentially limiting both the integrity of the structures and their useful lifetimes. The goal of the current investigation is to develop a mechanism-based model of the chemical degradation which occurs, such that given the external chemical environment and temperatures throughout the laminate, laminate geometry, and ply and/or constituent material properties, we can calculate the concentration of diffusing substances and extent of chemical degradation as functions of time and position throughout the laminate. This objective is met through the development and use of analytical models, coupled to an analysis-driven experimental program which offers both quantitative and qualitative information on the degradation mechanism. Preliminary analyses using a coupled diffusion/reaction model are used to gain insight into the physics of the degradation mechanisms and to identify crucial material parameters. An experimental program is defined based on the results of the preliminary analysis which allows the determination of the necessary material coefficients. Thermogravimetric analyses are carried out in nitrogen, air, and oxygen to provide quantitative information on thermal and oxidative reactions. Powdered samples are used to eliminate diffusion effects. Tests in both inert and oxidative environments allow the separation of thermal and oxidative contributions to specimen mass loss. The concentration dependency of the oxidative reactions is determined from the tests in pure oxygen. Short term isothermal tests at different temperatures are carried out on neat resin and unidirectional macroscopic specimens to identify diffusion effects. Mass loss, specimen shrinkage, the formation of degraded surface layers and surface cracking are recorded as functions of exposure time. Geometry effects in the neat resin, and anisotropic diffusion effects in the composites, are identified through the use of specimens with different aspect ratios. The data is used with the model to determine reaction coefficients and effective diffusion coefficients. The empirical and analytical correlations confirm the preliminary model results which suggest that mass loss at lower temperatures is dominated by oxidative reactions and that these reaction are limited by diffusion of oxygen from the surface. The mechanism-based model is able to successfully capture the basic physics of the degradation phenomena under a wide range of test conditions. The analysis-based test design is successful in separating out oxidative, thermal, and diffusion effects to allow the determination of material coefficients. This success confirms the basic picture of the process; however, a more complete understanding of some aspects of the physics are required before truly predictive capability can be achieved.

Summary and Evaluation of NRC-Sponsored Stellite 6 Aging and Friction Tests

DOE Office of Scientific and Technical Information (OSTI.GOV)

J. C. Watkins; K. G. DeWall; D. Bramwell

1999-04-01

This report describes four sets of tests sponsored by the U.S. Nuclear Regulatory Commission and conducted by the Idaho National Engineering and Environmental Laboratory. The tests support research addressing the need to provide assurance that motor-operated valves are able to perform their intended safety function, usually to open or close against specified (design basis) flow and pressure loads. One of the parameters that affects a gate valve's operability is the friction between the disc seats and the valve body seats. In most gate valves, these surfaces are hardfaced with Stellite 6, a cobalt-based alloy. The tests described in this reportmore » investigate the changes that occur in the friction as the Stellite 6 surfaces develop an oxide film as they age. Stellite 6 specimens were aged in a corrosion autoclave, the oxide films were examined and characterized, and the specimens were subjected to friction testing in a friction autoclave. A very thin oxide film formed after only a fe w days of natural aging. Even a very thin oxide film caused an increase in friction. The surface structure of the oxide film was dominated by a hard crystalline structure, such that the friction response was analogous to rubbing two pieces of sandpaper together. In the limited data provided by naturally aged specimens (78 days maximum exposure, very thin oxide films), the friction increased with greater aging time, approaching an as-yet-undetermined plateau. Although the thickness of the oxide film increased with greater aging time, the mechanical properties of the oxide film (larger granules with greater aging time) appeared to play a greater role in the friction response. Friction testing of specimens subjected to simulated in-service testing strokes at intervals during the aging process showed only a slight decrease in friction, compared to other specimens. Results from specimens subjected to accelerated aging were inconclusive, because of differences in the structure and comp osition of the oxide films, compared to naturally aged specimens. For the naturally aged specimens, the highest friction occurred on the first stroke. The first stroke smeared the oxide film and dislodged some of the granules, so that subsequent strokes saw lower friction values and less variation in the friction. This result underscores the importance of planning in-plant tests so that data are collected from the first stroke following a period of inactivity.« less

Apparatus for Testing Flat Specimens of Thermal Insulation

NASA Technical Reports Server (NTRS)

Fesmire, James E.; Augustynowicz, Stanislaw D.

2005-01-01

An apparatus has been developed to implement an improved method of testing flat-plate specimens of thermal-insulation materials for cryogenic application. The method includes testing under realistic use conditions that could include vacuum and mechanical loading at a pressure up to 70 psi (=0.48 MPa). The apparatus can accommodate a rigid or flexible specimen having thickness up to 1.25 in. (=3.2 cm) and diameters between 6 and 10 in. (about 15.2 and 25.4 cm, respectively). Typical test conditions include boundary temperatures between 77 K and 373 K and vacuum/interstitial gas filling at a pressure between 10(exp -6) torr (=1.3 x 10(exp -4) Pa) and 760 torr (atmospheric pressure =0.1 MPa). The interstitial gas could be N2, He, CO2, or any other suitable gas to which the insulation is expected to be exposed in use. Relative to prior apparatuses and testing methods, this apparatus and the testing method that it implements offer advantages of relative simplicity and ease of use. The basic principle of operation of the apparatus is that of boil-off calorimetry, using liquid nitrogen or any other suitable liquid that boils at a desired temperature below ambient temperature. Comparative rates of flow of heat through the thicknesses of the specimens (heat-leak rates) and apparent-thermal-conductivity values are obtained from tests of specimens. Absolute values of heat-leak rates and apparent thermal conductivities are computed from a combination of (1) the aforementioned comparative values and (2) calibration factors obtained by testing reference specimens of materials that have known thermal-insulation properties. The apparatus includes a full complement of temperature sensors, a vacuum pump and chamber, a monitoring and control system, and tools and fixtures that enable rapid and reliable installation and removal of specimens. A specimen is installed at the bottom of the vacuum chamber, and a cold-mass assembly that includes a tank is lowered into position above and around the specimen (see figure). A spring-based compensating fixture helps to ensure adequate thermal contact with possibly irregular specimen surfaces. For a high-compression test, the springs can be replaced with spacers. A flat circular load cell at the bottom of the chamber measures the compressive load on the specimen. Once the desired compressive-load, temperature, and vacuum/gas-filling conditions are established, testing begins. During a test, all measurements are recorded by use of a portable data-acquisition system and a computer. The total heat-leak rate is measured and calculated as the boil-off flow rate multiplied by the latent heat of vaporization. The parasitic heat leak (to the side of the specimen and to the top and side of the cold-mass tank) is reduced to a small fraction of the total heat leak by use of a combination of multilayer-insulation (MLI) shield rings, reflective film, a fiberglass/epoxy centering ring, and a bulk fill of aerogel beads. This combination eliminates the need for a cryogenic guard chamber used in a typical prior apparatus to reduce the parasitic heat leak.

Influence of Residual Stresses on Fretting Fatigue Life Prediction in Ti-6Al-4V

DTIC Science & Technology

2008-01-01

DATES COVERED (From - To) January 2008 Journal Article Preprint 01 January 2008 – 01 January 2008 4 . TITLE AND SUBTITLE INFLUENCE OF RESIDFUAL...62102F 6 . AUTHOR(S) Patrick J. Golden (AFRL/RXLMN) Dennis Buchanan (Dayton Research Institute) Sam Naboulsi (The University of Texas) 5d...tests that included coated specimens and specimens treated with LSP or 3 LPB [ 4 ]. The conclusion of this work was that mechanics based predictions were

Fatigue Characteristics of 3D Printed Acrylonitrile Butadiene Styrene (ABS)

NASA Astrophysics Data System (ADS)

Padzi, M. M.; Bazin, M. M.; Muhamad, W. M. W.

2017-11-01

Recently, the use of 3D printer technology has become significant to industries, especially when involving the new product development. 3D printing is a technology, which produces the 3D product or prototype using a layer-by-layer technique. However, there becomes less research on the mechanical performance of the 3D printed component. In the present work, fatigue characteristics of 3D printed specimen have been studied. Acrylonitrile butadiene styrene (ABS) has been chosen as a material research due to its wide applications. Two types of specimen used, which is the 3D printing and moulding specimens. Fused deposition modelling (FDM) technique was used to produce the specimens. The dog bone shape part was produced based on ASTM D638 standard and the tensile test has been carried out to get the mechanical properties. Fatigue test was carried out at 40%, 60% and 80% of the tensile strength. The moulded part shows higher fatigue cycles compared to 3D printed part for all loading percentages. Fatigue lives for 40%, 60% and 80%, were 911, 2645 and 26948 cycles, respectively. The results indicated that 3D printed part has a lower fatigue life, which may not suitable for industrial applications. However, the 3D printed part could be improved by using various parameters and may be introduced in low strength application.

Effect of Time and Temperature on Transformation Toughened Zirconias.

DTIC Science & Technology

1987-06-01

room temperature. High temperature mechanical tests performed vere stress rupture and stepped temperature stress rupture. The results of the tests...tetragonal precipitates will spontaneously transform to the monoclinic phae due to the lattice mismatch stress if they become larger than about 0.2 on, with...specimens, including fast fracture and fracture toughness testing. High temper- ture testing consisting of stress rupture and stepped temperature stress

Effect of etching with distinct hydrofluoric acid concentrations on the flexural strength of a lithium disilicate-based glass ceramic.

PubMed

Prochnow, Catina; Venturini, Andressa B; Grasel, Rafaella; Bottino, Marco C; Valandro, Luiz Felipe

2017-05-01

This study examined the effects of distinct hydrofluoric acid concentrations on the mechanical behavior of a lithium disilicate-based glass ceramic. Bar-shaped specimens were produced from ceramic blocks (e.max CAD, Ivoclar Vivadent). The specimens were polished, chamfered, and sonically cleaned in distilled water. The specimens were randomly divided into five groups (n = 23). The HF1, HF3, HF5, and HF10 specimens were etched for 20 s with acid concentrations of 1%, 3%, 5%, and 10%, respectively, while the SC (control) sample was untreated. The etched surfaces were evaluated using a scanning electron microscope and an atomic force microscope. Finally, the roughness was measured, and 3-point bending flexural tests were performed. The data were analyzed using one-way analysis of variance (ANOVA) and Tukey's test (α = 0.05). The Weibull modulus and characteristic strength were also determined. No statistical difference in the roughness and flexural strength was determined among the groups. The structural reliabilities (Weilbull moduli) were similar for the tested groups; however, the characteristic strength of the HF1 specimen was greater than that of the HF10 specimen. Compared with the untreated ceramic, the surface roughness and flexural strength of the ceramic were unaffected upon etching, regardless of the acid concentration. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 885-891, 2017. © 2016 Wiley Periodicals, Inc.

In situ high-energy X-ray diffraction study of tensile deformation of neutron-irradiated polycrystalline Fe-9%Cr alloy

DOE PAGES

Zhang, Xuan; Li, Meimei; Park, Jun -Sang; ...

2016-12-30

The effect of neutron irradiation on tensile deformation of a Fe-9wt.%Cr alloy was investigated using in situ high-energy synchrotron X-ray diffraction during room-temperature uniaxial tensile tests. New insights into the deformation mechanisms were obtained through the measurements of lattice strain evolution and the analysis of diffraction peak broadening using the modified Williamson-Hall method. Two neutron-irradiated specimens, one irradiated at 300 °C to 0.01 dpa and the other at 450 °C to 0.01dpa, were tested along with an unirradiated specimen. The macroscopic stress–strain curves of the irradiated specimens showed increased strength, reduced ductility and work-hardening exponent compared to the unirradiated specimen.more » The evolutions of the lattice strain, the dislocation density and the coherent scattering domain size in the deformation process revealed different roles of the submicroscopic defects in the 300°C/0.01 dpa specimen and the TEM-visible nanometer-sized dislocation loops in the 450°C/0.01 dpa specimen: submicroscopic defects extended the linear work hardening stage (stage II) to a higher strain, while irradiation-induced dislocation loops were more effective in dislocation pinning. Lastly, while the work hardening rate of stage II was unaffected by irradiation, significant dynamic recovery in stage III in the irradiated specimens led to the early onset of necking without stage IV as observed in the unirradiated specimen.« less

Analysis of Subcritical Crack Growth in Dental Ceramics Using Fracture Mechanics and Fractography

PubMed Central

Taskonak, Burak; Griggs, Jason A.; Mecholsky, John J.; Yan, Jia-Hau

2008-01-01

Objectives The aim of this study was to test the hypothesis that the flexural strengths and critical flaw sizes of dental ceramic specimens will be affected by the testing environment and stressing rate even though their fracture toughness values will remain the same. Methods Ceramic specimens were prepared from an aluminous porcelain (Vitadur Alpha; VITA Zahnfabrik, Bad Säckingen, Germany) and an alumina-zirconia-glass composite (In-Ceram® Zirconia; VITA Zahnfabrik). Three hundred uniaxial flexure specimens (150 of each material) were fabricated to dimensions of 25 mm × 4 mm × 1.2 mm according to the ISO 6872 standard. Each group of 30 specimens was fractured in water using one of four different target stressing rates ranging on a logarithmic scale from 0.1 to 100 MPa/s for Vitadur Alpha and from 0.01 to 10 MPa/s for In-Ceram® Zirconia. The fifth group was tested in inert environment (oil) with a target stressing rate of 100 MPa/s for Vitadur Alpha and 1000 MPa/s for In-Ceram® Zirconia. The effects of stressing rate and environment on flexural strength, critical flaw size, and fracture toughness were analyzed statistically by Kruskal-Wallis one-way ANOVA on ranks followed by post-hoc comparisons using Dunn’s test (α=0.05). In addition, 20 Vitadur Alpha specimens were fabricated with controlled flaws to simplify fractography. Half of these specimens were fracture tested in water and half in oil at a target stressing rate of 100 MPa/s, and the results were compared using Mann-Whitney rank sum tests (α=0.05). A logarithmic regression model was used to determine the fatigue parameters for each material. Results For each ceramic composition, specimens tested in oil had significantly higher strength (P≤0.05) and smaller critical flaw size (significant for Vitadur Alpha, P≤0.05) than those tested in water but did not have significantly different fracture toughness (P>0.05). Specimens tested at faster stressing rates had significantly higher strength (P≤0.05) but did not have significantly different fracture toughness (P>0.05). Regarding critical flaw size, stressing rate had a significant effect for In-Ceram® Zirconia specimens (P≤0.05) but not for Vitadur Alpha specimens (P>0.05). Fatigue parameters, n and ln B, were 38.4 and −12.7 for Vitadur Alpha and were 13.1 and 10.4 for In-Ceram® Zirconia. Significance Moisture assisted subcritical crack growth had a more deleterious effect on In-Ceram® Zirconia core ceramic than on Vitadur Alpha porcelain. Fracture surface analysis identified fracture surface features that can potentially mislead investigators into misidentifying the critical flaw. PMID:17845817

Analysis of subcritical crack growth in dental ceramics using fracture mechanics and fractography.

PubMed

Taskonak, Burak; Griggs, Jason A; Mecholsky, John J; Yan, Jia-Hau

2008-05-01

The aim of this study was to test the hypothesis that the flexural strengths and critical flaw sizes of dental ceramic specimens will be affected by the testing environment and stressing rate even though their fracture toughness values will remain the same. Ceramic specimens were prepared from an aluminous porcelain (Vitadur Alpha; VITA Zahnfabrik, Bad Säckingen, Germany) and an alumina-zirconia-glass composite (In-Ceram Zirconia; VITA Zahnfabrik). Three hundred uniaxial flexure specimens (150 of each material) were fabricated to dimensions of 25 mmx4 mmx1.2 mm according to the ISO 6872 standard. Each group of 30 specimens was fractured in water using one of four different target stressing rates ranging on a logarithmic scale from 0.1 to 100 MPa/s for Vitadur Alpha and from 0.01 to 10 MPa/s for In-Ceram Zirconia. The fifth group was tested in inert environment (oil) with a target stressing rate of 100 MPa/s for Vitadur Alpha and 1000 MPa/s for In-Ceram Zirconia. The effects of stressing rate and environment on flexural strength, critical flaw size, and fracture toughness were analyzed statistically by Kruskal-Wallis one-way ANOVA on ranks followed by post hoc comparisons using Dunn's test (alpha=0.05). In addition, 20 Vitadur Alpha specimens were fabricated with controlled flaws to simplify fractography. Half of these specimens were fracture tested in water and half in oil at a target stressing rate of 100 MPa/s, and the results were compared using Mann-Whitney rank sum tests (alpha=0.05). A logarithmic regression model was used to determine the fatigue parameters for each material. For each ceramic composition, specimens tested in oil had significantly higher strength (P0.05). Specimens tested at faster stressing rates had significantly higher strength (P0.05). Regarding critical flaw size, stressing rate had a significant effect for In-Ceram Zirconia specimens (P0.05). Fatigue parameters, n and lnB, were 38.4 and -12.7 for Vitadur Alpha and were 13.1 and 10.4 for In-Ceram Zirconia. Moisture assisted subcritical crack growth had a more deleterious effect on In-Ceram Zirconia core ceramic than on Vitadur Alpha porcelain. Fracture surface analysis identified fracture surface features that can potentially mislead investigators into misidentifying the critical flaw.

A Quantitative Study of the Relationship between the Distribution of Different Types of Collagen and the Mechanical Behavior of Rabbit Medial Collateral Ligaments

PubMed Central

Wan, Chao; Hao, Zhixiu; Wen, Shizhu; Leng, Huijie

2014-01-01

The mechanical properties of ligaments are key contributors to the stability and function of musculoskeletal joints. Ligaments are generally composed of ground substance, collagen (mainly type I and III collagen), and minimal elastin fibers. However, no consensus has been reached about whether the distribution of different types of collagen correlates with the mechanical behaviors of ligaments. The main objective of this study was to determine whether the collagen type distribution is correlated with the mechanical properties of ligaments. Using axial tensile tests and picrosirius red staining-polarization observations, the mechanical behaviors and the ratios of the various types of collagen were investigated for twenty-four rabbit medial collateral ligaments from twenty-four rabbits of different ages, respectively. One-way analysis of variance was used in the comparison of the Young's modulus in the linear region of the stress-strain curves and the ratios of type I and III collagen for the specimens (the mid-substance specimens of the ligaments) with different ages. A multiple linear regression was performed using the collagen contents (the ratios of type I and III collagen) and the Young's modulus of the specimens. During the maturation of the ligaments, the type I collagen content increased, and the type III collagen content decreased. A significant and strong correlation () was identified by multiple linear regression between the collagen contents (i.e., the ratios of type I and type III collagen) and the mechanical properties of the specimens. The collagen content of ligaments might provide a new perspective for evaluating the linear modulus of global stress-strain curves for ligaments and open a new door for studying the mechanical behaviors and functions of connective tissues. PMID:25062068

A quantitative study of the relationship between the distribution of different types of collagen and the mechanical behavior of rabbit medial collateral ligaments.

PubMed

Wan, Chao; Hao, Zhixiu; Wen, Shizhu; Leng, Huijie

2014-01-01

The mechanical properties of ligaments are key contributors to the stability and function of musculoskeletal joints. Ligaments are generally composed of ground substance, collagen (mainly type I and III collagen), and minimal elastin fibers. However, no consensus has been reached about whether the distribution of different types of collagen correlates with the mechanical behaviors of ligaments. The main objective of this study was to determine whether the collagen type distribution is correlated with the mechanical properties of ligaments. Using axial tensile tests and picrosirius red staining-polarization observations, the mechanical behaviors and the ratios of the various types of collagen were investigated for twenty-four rabbit medial collateral ligaments from twenty-four rabbits of different ages, respectively. One-way analysis of variance was used in the comparison of the Young's modulus in the linear region of the stress-strain curves and the ratios of type I and III collagen for the specimens (the mid-substance specimens of the ligaments) with different ages. A multiple linear regression was performed using the collagen contents (the ratios of type I and III collagen) and the Young's modulus of the specimens. During the maturation of the ligaments, the type I collagen content increased, and the type III collagen content decreased. A significant and strong correlation (R2 = 0.839, P < 0.05) was identified by multiple linear regression between the collagen contents (i.e., the ratios of type I and type III collagen) and the mechanical properties of the specimens. The collagen content of ligaments might provide a new perspective for evaluating the linear modulus of global stress-strain curves for ligaments and open a new door for studying the mechanical behaviors and functions of connective tissues.

Hygrothermal damage mechanisms in graphite-epoxy composites

NASA Technical Reports Server (NTRS)

Crossman, F. W.; Mauri, R. E.; Warren, W. J.

1979-01-01

T300/5209 and T300/5208 graphite epoxy laminates were studied experimentally and analytically in order to: (1) determine the coupling between applied stress, internal residual stress, and moisture sorption kinetics; (2) examine the microscopic damage mechanisms due to hygrothermal cycling; (3) evaluate the effect of absorbed moisture and hygrothermal cycling on inplane shear response; (4) determine the permanent loss of interfacial bond strength after moisture absorption and drying; and (5) evaluate the three dimensional stress state in laminates under a combination of hygroscopic, thermal, and mechanical loads. Specimens were conditioned to equilibrium moisture content under steady exposure to 55% or 95% RH at 70 C or 93 C. Some specimens were tested subsequent to moisture conditioning and 100 cycles between -54 C and either 70 C or 93 C.

Investigation of specimen size effects by in-situ microcompression of equal channel angular pressed copper

DOE Office of Scientific and Technical Information (OSTI.GOV)

Howard, C.; Frazer, D.; Lupinacci, A.

Here, micropillar compression testing was implemented on Equal Channel Angular Pressed copper samples ranging from 200 nm to 10 µm in side length in order to measure the mechanical properties yield strength, first load drop during plastic deformation at which there was a subsequent stress decrease with increasing strain, work hardening, and strain hardening exponent. Several micropillars containing multiple grains were investigated in a 200 nm grain sample. The effective pillar diameter to grain size ratios, D/d, were measured to be between 1.9 and 27.2. Specimens having D/d ratios between 0.2 and 5 were investigated in a second sample thatmore » was annealed at 200 °C for 2 h with an average grain size of 1.3 µm. No yield strength or elastic modulus size effects were observed in specimens in the 200 nm grain size sample. However work hardening increases with a decrease in critical ratios and first stress drops occur at much lower stresses for specimens with D/d ratios less than 5. For comparison, bulk tensile testing of both samples was performed, and the yield strength values of all micropillar compression tests for the 200 nm grained sample are in good agreement with the yield strength values of the tensile tests.« less

Investigation of specimen size effects by in-situ microcompression of equal channel angular pressed copper

DOE PAGES

Howard, C.; Frazer, D.; Lupinacci, A.; ...

2015-09-30

Here, micropillar compression testing was implemented on Equal Channel Angular Pressed copper samples ranging from 200 nm to 10 µm in side length in order to measure the mechanical properties yield strength, first load drop during plastic deformation at which there was a subsequent stress decrease with increasing strain, work hardening, and strain hardening exponent. Several micropillars containing multiple grains were investigated in a 200 nm grain sample. The effective pillar diameter to grain size ratios, D/d, were measured to be between 1.9 and 27.2. Specimens having D/d ratios between 0.2 and 5 were investigated in a second sample thatmore » was annealed at 200 °C for 2 h with an average grain size of 1.3 µm. No yield strength or elastic modulus size effects were observed in specimens in the 200 nm grain size sample. However work hardening increases with a decrease in critical ratios and first stress drops occur at much lower stresses for specimens with D/d ratios less than 5. For comparison, bulk tensile testing of both samples was performed, and the yield strength values of all micropillar compression tests for the 200 nm grained sample are in good agreement with the yield strength values of the tensile tests.« less

Electric reaction arising in bone subjected to mechanical loadings

NASA Astrophysics Data System (ADS)

Murasawa, Go; Cho, Hideo; Ogawa, Kazuma

2006-03-01

The aim of present study is the investigation of the electric reaction arising in bone subjected to mechanical loadings. Firstly, specimen was fabricated from femur of cow, and ultrasonic propagation in bone was measured by ultrasonic technique. Secondary, 4-point bending test was conducted up to fracture, and electric reaction arising in bone was measured during loading. Thirdly, cyclic 4-point bending test was conducted to investigate the effect of applied displacement speed on electric reaction.

TEST SYSTEM FOR EVALUATING SPENT NUCLEAR FUEL BENDING STIFFNESS AND VIBRATION INTEGRITY

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Jy-An John; Wang, Hong; Bevard, Bruce Balkcom

2013-01-01

Transportation packages for spent nuclear fuel (SNF) must meet safety requirements specified by federal regulations. For normal conditions of transport, vibration loads incident to transport must be considered. This is particularly relevant for high-burnup fuel (>45 GWd/MTU). As the burnup of the fuel increases, a number of changes occur that may affect the performance of the fuel and cladding in storage and during transportation. The mechanical properties of high-burnup de-fueled cladding have been previously studied by subjecting defueled cladding tubes to longitudinal (axial) tensile tests, ring-stretch tests, ring-compression tests, and biaxial tube burst tests. The objective of this study ismore » to investigate the mechanical properties and behavior of both the cladding and the fuel in it under vibration/cyclic loads similar to the sustained vibration loads experienced during normal transport. The vibration loads to SNF rods during transportation can be characterized by dynamic, cyclic, bending loads. The transient vibration signals in a specified transport environment can be analyzed, and frequency, amplitude and phase components can be identified. The methodology being implemented is a novel approach to study the vibration integrity of actual SNF rod segments through testing and evaluating the fatigue performance of SNF rods at defined frequencies. Oak Ridge National Laboratory (ORNL) has developed a bending fatigue system to evaluate the response of the SNF rods to vibration loads. A three-point deflection measurement technique using linear variable differential transformers is used to characterize the bending rod curvature, and electromagnetic force linear motors are used as the driving system for mechanical loading. ORNL plans to use the test system in a hot cell for SNF vibration testing on high burnup, irradiated fuel to evaluate the pellet-clad interaction and bonding on the effective lifetime of fuel-clad structure bending fatigue performance. Technical challenges include pure bending implementation, remote installation and detachment of the SNF test specimen, test specimen deformation measurement, and identification of a driving system suitable for use in a hot cell. Surrogate test specimens have been used to calibrate the test setup and conduct systematic cyclic tests. The calibration and systematic cyclic tests have been used to identify test protocol issues prior to implementation in the hot cell. In addition, cyclic hardening in unidirectional bending and softening in reverse bending were observed in the surrogate test specimens. The interface bonding between the surrogate clad and pellets was found to impact the bending response of the surrogate rods; confirming this behavior in the actual spent fuel segments will be an important aspect of the hot cell test implementation,« less

A Comprehensive Specimen-Specific Multiscale Data Set for Anatomical and Mechanical Characterization of the Tibiofemoral Joint

PubMed Central

Chokhandre, Snehal; Colbrunn, Robb; Bennetts, Craig; Erdemir, Ahmet

2015-01-01

Understanding of tibiofemoral joint mechanics at multiple spatial scales is essential for developing effective preventive measures and treatments for both pathology and injury management. Currently, there is a distinct lack of specimen-specific biomechanical data at multiple spatial scales, e.g., joint, tissue, and cell scales. Comprehensive multiscale data may improve the understanding of the relationship between biomechanical and anatomical markers across various scales. Furthermore, specimen-specific multiscale data for the tibiofemoral joint may assist development and validation of specimen-specific computational models that may be useful for more thorough analyses of the biomechanical behavior of the joint. This study describes an aggregation of procedures for acquisition of multiscale anatomical and biomechanical data for the tibiofemoral joint. Magnetic resonance imaging was used to acquire anatomical morphology at the joint scale. A robotic testing system was used to quantify joint level biomechanical response under various loading scenarios. Tissue level material properties were obtained from the same specimen for the femoral and tibial articular cartilage, medial and lateral menisci, anterior and posterior cruciate ligaments, and medial and lateral collateral ligaments. Histology data were also obtained for all tissue types to measure specimen-specific cell scale information, e.g., cellular distribution. This study is the first of its kind to establish a comprehensive multiscale data set for a musculoskeletal joint and the presented data collection approach can be used as a general template to guide acquisition of specimen-specific comprehensive multiscale data for musculoskeletal joints. PMID:26381404

DACS II - A distributed thermal/mechanical loads data acquisition and control system

NASA Technical Reports Server (NTRS)

Zamanzadeh, Behzad; Trover, William F.; Anderson, Karl F.

1987-01-01

A distributed data acquisition and control system has been developed for the NASA Flight Loads Research Facility. The DACS II system is composed of seven computer systems and four array processors configured as a main computer system, three satellite computer systems, and 13 analog input/output systems interconnected through three independent data networks. Up to three independent heating and loading tests can be run concurrently on different test articles or the entire system can be used on a single large test such as a full scale hypersonic aircraft. Thermal tests can include up to 512 independent adaptive closed loop control channels. The control system can apply up to 20 MW of heating to a test specimen while simultaneously applying independent mechanical loads. Each thermal control loop is capable of heating a structure at rates of up to 150 F per second over a temperature range of -300 to +2500 F. Up to 64 independent mechanical load profiles can be commanded along with thermal control. Up to 1280 analog inputs monitor temperature, load, displacement and strain on the test specimens with real time data displayed on up to 15 terminals as color plots and tabular data displays. System setup and operation is accomplished with interactive menu-driver displays with extensive facilities to assist the users in all phases of system operation.

Structural Integrity of an Electron Beam Melted Titanium Alloy.

PubMed

Lancaster, Robert; Davies, Gareth; Illsley, Henry; Jeffs, Spencer; Baxter, Gavin

2016-06-14

Advanced manufacturing encompasses the wide range of processes that consist of "3D printing" of metallic materials. One such method is Electron Beam Melting (EBM), a modern build technology that offers significant potential for lean manufacture and a capability to produce fully dense near-net shaped components. However, the manufacture of intricate geometries will result in variable thermal cycles and thus a transient microstructure throughout, leading to a highly textured structure. As such, successful implementation of these technologies requires a comprehensive assessment of the relationships of the key process variables, geometries, resultant microstructures and mechanical properties. The nature of this process suggests that it is often difficult to produce representative test specimens necessary to achieve a full mechanical property characterisation. Therefore, the use of small scale test techniques may be exploited, specifically the small punch (SP) test. The SP test offers a capability for sampling miniaturised test specimens from various discrete locations in a thin-walled component, allowing a full characterisation across a complex geometry. This paper provides support in working towards development and validation strategies in order for advanced manufactured components to be safely implemented into future gas turbine applications. This has been achieved by applying the SP test to a series of Ti-6Al-4V variants that have been manufactured through a variety of processing routes including EBM and investigating the structural integrity of each material and how this controls the mechanical response.

Composite Behavior of a Novel Insulated Concrete Sandwich Wall Panel Reinforced with GFRP Shear Grids: Effects of Insulation Types.

PubMed

Kim, JunHee; You, Young-Chan

2015-03-03

A full-scale experimental program was used in this study to investigate the structural behavior of novel insulated concrete sandwich wall panels (SWPs) reinforced with grid-type glass-fiber-reinforced polymer (GFRP) shear connectors. Two kinds of insulation-expanded polystyrene (EPS) and extruded polystyrene (XPS) with 100 mm thickness were incased between the two concrete wythes to meet the increasing demand for the insulation performance of building envelope. One to four GFRP shear grids were used to examine the degree of composite action of the two concrete wythes. Ten specimens of SWPs were tested under displacement control subjected to four-point concentrated loads. The test results showed that the SWPs reinforced with GFRP grids as shear connectors developed a high degree of composite action resulting in high flexural strength. The specimens with EPS foam exhibited an enhanced load-displacement behavior compared with the specimens with XPS because of the relatively stronger bond between insulation and concrete. In addition, the ultimate strength of the test results was compared to the analytical prediction with the mechanical properties of only GRFP grids. The specimens with EPS insulation presented higher strength-based composite action than the ones with XPS insulation.

Shape memory characteristics and mechanical properties of powder metallurgy processed Ti50Ni40Cu10 alloy.

PubMed

Kim, Yeon-Wook

2014-10-01

Ti-Ni-Cu alloy powders were prepared by gas atomization and porous bulk specimens were fabricated by spark plasma sintering (SPS). The microstructure of as-solidified powders exhibited a cellular structure and they contained a high density of nano-sized porosities which were located in the intercellular regions. XRD analysis showed that one-step martensitic transformation of B2-B19 occurred in all alloy powders and SPS specimens. When the martensitic transformation start temperature (M(s)) and austenite transformation finish temperature (A(f)) were determined in order to analyze the dependence of powder size on transformation temperatures, the M(s) increased slightly from -17.5 degrees C to - 14.6 degrees C as increasing the powder size ranging from between 25 and 50 μm to ranging between 100 and 150 μm. However, the M(s) and A(f) of the as-atomized powders is much smaller than those of SPS specimens and the M(s) of porous specimen was about 10.9 degrees C. Loading-unloading compressive tests were carried out to investigate the mechanical properties of porous Ti-Ni-Cu specimen. The specimen was compressed to the strain of 6% at a temperature higher than A,. After unloading, the residual strain was 2.1%. After the compressed specimen was heated to 60 degrees C and held for 30 minutes and then cooled to room temperature, the changes in the length of the specimens were measured. Then it was found that the recovered strain ascribed to shape memory effect was 1.5%.

Electronics reliability fracture mechanics. Volume 2: Fracture mechanics

NASA Astrophysics Data System (ADS)

Kallis, J.; Duncan, L.; Buechler, D.; Backes, P.; Sandkulla, D.

1992-05-01

This is the second of two volumes. The other volume (WL-TR-92-3015) is 'Causes of Failures of Shop Replaceable Units and Hybrid Microcircuits.' The objective of the Electronics Reliability Fracture Mechanics (ERFM) program was to develop and demonstrate a life prediction technique for electronic assemblies, when subjected to environmental stresses of vibration and thermal cycling, based upon the mechanical properties of the materials and packaging configurations which make up an electronic system. The application of fracture mechanics to microscale phenomena in electronic assemblies was a pioneering research effort. The small scale made the experiments very difficult; for example, the 1-mil-diameter bond wires in microelectronic devices are 1/3 the diameter of a human hair. A number of issues had to be resolved to determine whether a fracture mechanics modelling approach is correct for the selected failures; specifically, the following two issues had to be resolved: What fraction of the lifetime is spent in crack initiation? Are macro fracture mechanics techniques, used in large structures such as bridges, applicable to the tiny structures in electronic equipment? The following structural failure mechanisms were selected for modelling: bondwire fracture from mechanical cycling; bondwire fracture from thermal (power) cycling; plated through hole (PTH) fracture from thermal cycling. The bondwire fracture test specimens were A1-1 percent Si wires, representative of wires used in the parts in the modules selected for detailed investigation in this program (see Vol. 1 of this report); 1-mil-diameter wires were tested in this program. The PTH test specimens were sections of 14-layer printed wiring boards of the type used.

Study on the Factors Affecting the Mechanical Behavior of Electron Beam Melted Ti6Al4V

NASA Astrophysics Data System (ADS)

Pirozzi, Carmine; Franchitti, Stefania; Borrelli, Rosario; Caiazzo, Fabrizia; Alfieri, Vittorio; Argenio, Paolo

2017-09-01

In this study, a mechanical characterization has been performed on EBM built Ti-6Al-4V tensile samples. The results of tensile tests have shown a different behavior between two sets of specimens: as built and machined ones. Supporting investigations have been carried out in order to physically explain the statistical difference of mechanical performances. Cylindrical samples which represent the tensile specimens geometry have been EBM manufactured and then investigated in their as built conditions from macrostructural and microstructural point of view. In order to make robust this study, cylindrical samples have been EBM manufactured with different size and at different height from build plate. The reason of this choice was arisen from the need of understanding if other factors as the massivity and specific location could affect the microstructure and defects generations consequently influencing the mechanical behavior of the EBMed components. The results of this study have proved that the irregularity of external circular surfaces of examined cylinders, reducing significantly the true cross section withstanding the applied load, has given a comprehensive physical explanation of the different tensile behavior of the two sets of tensile specimens.

Delamination Fracture Related to Tempering in a High-Strength Low-Alloy Steel

NASA Astrophysics Data System (ADS)

Yan, Wei; Sha, Wei; Zhu, Lin; Wang, Wei; Shan, Yi-Yin; Yang, Ke

2010-01-01

The delamination or splitting of mechanical test specimens of rolled steel plate is a phenomenon that has been studied for many years. In the present study, splitting during fracture of tensile and Charpy V-notch (CVN) test specimens is examined in a high-strength low-alloy plate steel. It is shown that delamination did not occur in test specimens from plate in the as-rolled condition, but was severe in material tempered in the temperature range 500 °C to 650 °C. Minor splitting was seen after heating to 200 °C, 400 °C, and 700 °C. Samples that had been triple quenched and tempered to produce a fine equiaxed grain size also did not exhibit splitting. Microstructural and preferred orientation studies are presented and are discussed as they relate to the splitting phenomenon. It is concluded that the elongated as-rolled grains and grain boundary embrittlement resulting from precipitates (carbides and nitrides) formed during reheating were responsible for the delamination.

Pseudo-dynamic tests on masonry residential buildings seismically retrofitted by precast steel reinforced concrete walls

NASA Astrophysics Data System (ADS)

Li, Wenfeng; Wang, Tao; Chen, Xi; Zhong, Xiang; Pan, Peng

2017-07-01

A retrofitting technology using precast steel reinforced concrete (PSRC) panels is developed to improve the seismic performance of old masonry buildings. The PSRC panels are built up as an external PSRC wall system surrounding the existing masonry building. The PSRC walls are well connected to the existing masonry building, which provides enough confinement to effectively improve the ductility, strength, and stiffenss of old masonry structures. The PSRC panels are prefabricated in a factory, significantly reducing the situ work and associated construction time. To demonstrate the feasibility and mechanical effectivenss of the proposed retrofitting system, a full-scale five-story specimen was constructed. The retrofitting process was completed within five weeks with very limited indoor operation. The specimen was then tested in the lateral direction, which could potentially suffer sigifnicant damage in a large earthquake. The technical feasibility, construction workability, and seismic performance were thoroughly demonstrated by a full-scale specimen construction and pseudo-dynamic tests.

Gaseous hydrogen embrittlement of PH 13-8 Mo steel

NASA Astrophysics Data System (ADS)

Ding, Y. S.; Tsay, L. W.; Chiang, M. F.; Chen, C.

2009-04-01

In this study, notched tensile and fatigue crack growth tests in gaseous hydrogen were performed on PH 13-8 Mo stainless steel specimens at room temperature. These specimens were susceptible to hydrogen embrittlement (HE), but at different degrees, depending on the aging conditions or the microstructures of the alloys. In hydrogen, the accelerated fatigue crack growth rate (FCGR) usually accompanied a reduced notched tensile strength (NTS) of the specimens, i.e., the faster the FCGR the lower the NTS. It was proposed that the same fracture mechanism could be applied to these two different types of specimens, regardless of the loading conditions. Rapid fatigue crack growth and high NTS loss were found in the H800 (426 °C under-aged) and H900 (482 °C peak-aged) specimens. The HE susceptibility of the steel was reduced by increasing the aging temperature above 593 °C, which was attributed to the increased amount of austenite in the structure. Extensive quasi-cleavage fracture was observed for the specimens that were deteriorated severely by HE.

[Ex Vivo Testing of Mechanical Properties of Canine Metacarpal/Metatarsal Bones after Simulated Implant Removal].

PubMed

Srnec, R; Fedorová, P; Pěnčík, J; Vojtová, L; Sedlinská, M; Nečas, A

2016-01-01

PURPOSE OF THE STUDY In a long-term perspective, it is better to remove implants after fracture healing. However, subsequent full or excessive loading of an extremity may result in refracture, and the bone with holes after screw removal may present a site with predilection for this. The aim of the study was to find ways of how to decrease risk factors for refracture in such a case. This involved support to the mechanical properties of a bone during its remodelling until defects following implant removal are repaired, using a material tolerated by bone tissue and easy to apply. It also included an assessment of the mechanical properties of a bone after filling the holes in it with a newly developed biodegradable polymer-composite gel ("bone paste"). The composite also has a prospect of being used to repair bony defects produced by pathological processes. MATERIAL AND METHODS Experiments were carried out on intact weight-bearing small bones in dogs. A total of 27 specimens of metacarpal/metatarsal bones were used for ex vivo testing. They were divided into three groups: K1 (n = 9) control undamaged bones; K2 (n = 9) control bones with iatrogenic damage simulating holes left after cortical screw removal; EXP (n = 9) experimental specimens in which simulated holes in bone were filled with the biodegradable self-hardening composite. The bone specimens were subjected to three-point bending in the caudocranial direction by a force acting parallel to the direction of drilling in their middiaphyses. The value of maximum load achieved (N) and the corresponding value of a vertical displacement (mm) were recorded in each specimen, then compared and statistically evaluated. RESULTS On application of a maximum load (N), all bone specimens broke in the mid-part of their diaphyses. In group K1 the average maximum force of 595.6 ± 79.5 N was needed to break the bone; in group K2 it was 347.6 ± 58.6 N; and in group EXP it was 458.3 ± 102.7 N. The groups with damaged bones, K2 and EXP, were compared and the difference was found to be statistically significant (p ≤ 0.05). CONCLUSIONS The recently developed biodegradable polymer-composite gel is easy and quick to apply to any defect, regardless of its shape, in bone tissue. The ex vivo mechanical tests on canine short bones showed that the composite applied to defects, which simulated holes left after screw removal, provided sufficient mechanical support to the bone architecture. The results of measuring maximum loading forces were statistically significant. However, before the composite could be recommended for use in veterinary or human medical practice, thorough pre-clinical studies will be required. fracture fixation, mechanical testing, bone plate, cortical screw, refracture.

Corrosion Analysis of TiCN Coated Al-7075 Alloy for Marine Applications: A Case Study

NASA Astrophysics Data System (ADS)

Srinath, M. K.; Ganesha Prasad, M. S.

2018-05-01

Corrosion is one of the most important marine difficulties that cause long term problems, occurring in ships and submarines surrounded by a corrosive environment when coupled with chemical, temperature and stress related conditions. Corrosion of marine parts could lead to severe disasters. Coatings and heat treatment in a very effective way could be used to protect the aluminium parts against corrosion. The present case study focuses on the corrosion and microstructural properties of TiCN coatings fabricated on Al-7075 aluminium alloy substrate by using Physical Vapour Deposition technique. Corrosion properties of specimen's heat treated at 500 °C at durations of 1, 4, 8 and 12 h were tested through salt spray test. According to D-1193, ASTM standard, corrosion resistance of coated and heat treated Al-7075 samples were investigated in solution kept at 95 °F with a pH of 6.5-7.2, with 5 sections of NaCl to 95 sections of type IV water. The specimen's heat treated for 1 h showed positive corrosion resistance, while the specimens treated for longer durations had the opposite effect. The microstructures of the salt spray tested coatings were investigated by scanning electron microscope. X-ray diffraction tests were conducted on specimens to determine the atomic and molecular structure of the surface crystals and the unit cell dimensions. The corrosion mechanisms of the coated specimens under the heat treated conditions have been explored.

Mechanical-physical experimental tests on lime mortars and bricks reinforced with hemp

NASA Astrophysics Data System (ADS)

Formisano, Antonio; Dessı, Enzo; Landolfo, Raffaele

2017-11-01

Hemp is an agricultural product used for various applications. In the Civil Engineering field, only a limited use of this natural material, called the "green pig" since exploitation of all its constituent parts is allowed, has been done. For this reason, in the paper an experimental activity on lime mortars and bricks reinforced with hemp components has been performed. Compression and bending tests have been carried out on specimens manufactured with hemp shives and fibres, respectively. The achieved results have shown that hemp products change the failure modes from brittle to ductile, leaving basically unaltered the strength capacity of reinforced specimens with respect to unreinforced ones.

Automated Tow Placement Processing and Characterization of Composites

NASA Technical Reports Server (NTRS)

Prabhakaran, R.

2004-01-01

The project had one of the initial objectives as automated tow placement (ATP), in which a robot was used to place a collimated band of pre-impregnated ribbons or a wide preconsolidated tape onto a tool surface. It was proposed to utilize the Automated Tow Placement machine that was already available and to fabricate carbon fiber reinforced PEEK (polyether-ether-ketone) matrix composites. After initial experiments with the fabrication of flat plates, composite cylinders were to be fabricated. Specimens from the fabricated parts were to be tested for mechanical characterization. A second objective was to conduct various types of tests for characterizing composite specimens cured by different fabrication processes.

Comparison between Different Methods for Biomechanical Assessment of Ex Vivo Fracture Callus Stiffness in Small Animal Bone Healing Studies

PubMed Central

Steiner, Malte; Volkheimer, David; Meyers, Nicholaus; Wehner, Tim; Wilke, Hans-Joachim; Claes, Lutz; Ignatius, Anita

2015-01-01

For ex vivo measurements of fracture callus stiffness in small animals, different test methods, such as torsion or bending tests, are established. Each method provides advantages and disadvantages, and it is still debated which of those is most sensitive to experimental conditions (i.e. specimen alignment, directional dependency, asymmetric behavior). The aim of this study was to experimentally compare six different testing methods regarding their robustness against experimental errors. Therefore, standardized specimens were created by selective laser sintering (SLS), mimicking size, directional behavior, and embedding variations of respective rat long bone specimens. For the latter, five different geometries were created which show shifted or tilted specimen alignments. The mechanical tests included three-point bending, four-point bending, cantilever bending, axial compression, constrained torsion, and unconstrained torsion. All three different bending tests showed the same principal behavior. They were highly dependent on the rotational direction of the maximum fracture callus expansion relative to the loading direction (creating experimental errors of more than 60%), however small angular deviations (<15°) were negligible. Differences in the experimental results between the bending tests originate in their respective location of maximal bending moment induction. Compared to four-point bending, three-point bending is easier to apply on small rat and mouse bones under realistic testing conditions and yields robust measurements, provided low variation of the callus shape among the tested specimens. Axial compressive testing was highly sensitive to embedding variations, and therefore cannot be recommended. Although it is experimentally difficult to realize, unconstrained torsion testing was found to be the most robust method, since it was independent of both rotational alignment and embedding uncertainties. Constrained torsional testing showed small errors (up to 16.8%, compared to corresponding alignment under unconstrained torsion) due to a parallel offset between the specimens’ axis of gravity and the torsional axis of rotation. PMID:25781027

Effect of ceramic infrastructure on the failure behavior and stress distribution of fixed partial dentures.

PubMed

Borba, Márcia; Duan, Yuanyuan; Griggs, Jason A; Cesar, Paulo F; Della Bona, Álvaro

2015-04-01

The effect of the ceramic infrastructure (IS) on the failure behavior and stress distribution of fixed partial dentures (FPDs) was evaluated. Twenty FPDs with a connector cross-section of 16 mm(2) were produced for each IS and veneered with porcelain: (YZ) Vita In-Ceram YZ/Vita VM9 porcelain; (IZ) Vita In-Ceram Zirconia/Vita VM7 porcelain; (AL) Vita In-Ceram AL/Vita VM7 porcelain. Two experimental conditions were evaluated (n = 10). For control specimens, load was applied in the center of the pontic at 0.5 mm/min until failure, using a universal testing machine, in 37°C deionized water. For mechanical cycling (MC) specimens, FPDs were subjected to MC (2 Hz, 140 N, 10(6) cycles) and subsequently tested as described for the control group. For YZ, an extra group of 10 FPDs were built with a connector cross-section of 9 mm(2) and tested until failure. Fractography and FEA were performed. Data were analyzed by ANOVA and Tukey's test (α = 0.05). YZ16 showed the greatest fracture load mean value, followed by YZ16-MC. Specimens from groups YZ9, IZ16, IZ16-MC, AL16 and AL16-MC showed no significant difference for the fracture load. The failure behavior and stress distribution of FPDs was influenced by the type of IS. AL and IZ FPDs showed similar fracture load values but different failure modes and stress distribution. YZ showed the best mechanical behavior and may be considered the material of choice to produce posterior FPDs as it was possible to obtain a good mechanical performance even with a smaller connector dimension (9 mm(2)). Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

How tough is bone? Application of elastic-plastic fracture mechanics to bone.

PubMed

Yan, Jiahau; Mecholsky, John J; Clifton, Kari B

2007-02-01

Bone, with a hierarchical structure that spans from the nano-scale to the macro-scale and a composite design composed of nano-sized mineral crystals embedded in an organic matrix, has been shown to have several toughening mechanisms that increases its toughness. These mechanisms can stop, slow, or deflect crack propagation and cause bone to have a moderate amount of apparent plastic deformation before fracture. In addition, bone contains a high volumetric percentage of organics and water that makes it behave nonlinearly before fracture. Many researchers used strength or critical stress intensity factor (fracture toughness) to characterize the mechanical property of bone. However, these parameters do not account for the energy spent in plastic deformation before bone fracture. To accurately describe the mechanical characteristics of bone, we applied elastic-plastic fracture mechanics to study bone's fracture toughness. The J integral, a parameter that estimates both the energies consumed in the elastic and plastic deformations, was used to quantify the total energy spent before bone fracture. Twenty cortical bone specimens were cut from the mid-diaphysis of bovine femurs. Ten of them were prepared to undergo transverse fracture and the other 10 were prepared to undergo longitudinal fracture. The specimens were prepared following the apparatus suggested in ASTM E1820 and tested in distilled water at 37 degrees C. The average J integral of the transverse-fractured specimens was found to be 6.6 kPa m, which is 187% greater than that of longitudinal-fractured specimens (2.3 kPa m). The energy spent in the plastic deformation of the longitudinal-fractured and transverse-fractured bovine specimens was found to be 3.6-4.1 times the energy spent in the elastic deformation. This study shows that the toughness of bone estimated using the J integral is much greater than the toughness measured using the critical stress intensity factor. We suggest that the J integral method is a better technique in estimating the toughness of bone.

Effect of alkaline treatment on mechanical properties of kenaf fiber reinforced polyester composites

NASA Astrophysics Data System (ADS)

Reddy, Bijjam Ramgopal; Dhoria, Sneha H.

2018-04-01

This paper focuses on the study of the effect of chemical treatment on mechanical properties such as tensile, flexural and impact properties of kenaf fiber reinforced polyester composites. Adhesion between the fiber and polymer is one of factors affecting the mechanical properties of composites. In order to increase the adhesion, the fibers are chemically treated with 5% of sodium hydroxide (NaOH) solution. The composite specimens are prepared in both untreated and treated forms of kenaf fibers with five levels of fiber volume fractions. The specimens are prepared according to ASTM standards. Mechanical tests such as tensile, flexural and impact are conducted to determine ultimate tensile strength, bending strength and impact strength of composites. The effect of change in volume fraction on the mechanical properties of the composites is studied for both untreated (raw) and chemically treated kenaf fibers. It has been found that the composites made of chemically treated fibers have good mechanical properties compared to untreated fibers.

Mechanical properties of new dental pulp-capping materials.

PubMed

Nielsen, Matthew J; Casey, Jeffery A; VanderWeele, Richard A; Vandewalle, Kraig S

2016-01-01

The mechanical properties of pulp-capping materials may affect their resistance to fracture during placement of a final restorative material or while supporting an overlying restoration over time. The purpose of this study was to compare the compressive strength, flexural strength, and flexural modulus of 2 new pulp-capping materials (TheraCal LC and Biodentine), mineral trioxide aggregate (MTA), and calcium hydroxide over time. Specimens were created in molds and tested to failure in a universal testing machine after 15 minutes, 3 hours, and 24 hours. The MTA specimens did not set at 15 minutes. At all time periods, TheraCal LC had the greatest compressive and flexural strengths. After 3 and 24 hours, Biodentine had the greatest flexural modulus. TheraCal LC had greater early strength to potentially resist fracture during immediate placement of a final restorative material. Biodentine had greater stiffness after 3 hours to potentially provide better support of an overlying restoration under function over time.

Mechanical behavior of a ceramic matrix composite material. M.S. Thesis Final Report

NASA Technical Reports Server (NTRS)

Grosskopf, Paul P.; Duke, John C., Jr.

1991-01-01

Monolithic ceramic materials have been used in industry for hundreds of years. These materials have proven their usefulness in many applications, yet, their potential for critical structural applications is limited. The existence of an imperfection in a monolithic ceramic on the order of several microns in size may be critical, resulting in catastrophic failure. To overcome this extreme sensitivity to small material imperfections, reinforced ceramic materials were developed. A ceramic matrix which has been reinforced with continuous fibers is not only less sensitive to microscopic flaws, but is also able to sustain significant damage without suffering catastrophic failure. A borosilicate glass reinforced with several layers of plain weave silicon carbide cloth (Nicalon) was studied. The mechanical testing which was performed included both flexural and tensile loading configurations. This testing was done not only to determine the material properties, but also to initiate a controlled amount of damage within each specimen. Several nondestructive testing techniques, including acousto-ultrasonics (AU), were performed on the specimens periodically during testing. The AU signals were monitored through the use of an IBM compatible personal computer with a high speed data acquisition board. Software was written which manipulates the AU signals in both the time and frequency domains, resulting in quantitative measures of the mechanical response of the material. The measured AU parameters are compared to both the mechanical test results and data from other nondestructive methods including ultrasonic C-scans and penetrant enhanced x ray radiography.

High Temperature Mechanical Characterization of Ceramic Matrix Composites

NASA Technical Reports Server (NTRS)

Gyekenyesi, John Z.

1998-01-01

A high temperature mechanical characterization laboratory has been assembled at NASA Lewis Research Center. One contribution of this work is to test ceramic matrix composite specimens in tension in environmental extremes. Two high temperature tensile testing systems were assembled. The systems were assembled based on the performance and experience of other laboratories and meeting projected service conditions for the materials in question. The systems use frames with an electric actuator and a center screw. A PC based data acquisition and analysis system is used to collect and analyze the data. Mechanical extensometers are used to measure specimen strain. Thermocouples, placed near the specimen, are used to measure the specimen gage section temperature. The system for testing in air has a resistance element furnace with molybdenum disilicide elements and pneumatic grips with water cooling attached to hydraulic alignment devices. The system for testing in an inert gas has a graphite resistance element furnace in a chamber with rigidly mounted, water cooled, hydraulically actuated grips. Unidirectional SiC fiber reinforced reaction bonded Si3N4 and triaxially woven, two dimensional, SiC fiber reinforced enhanced SiC composites were tested in unidirectional tension. Theories for predicting the Young's modulus, modulus near the ultimate strength, first matrix cracking stress, and ultimate strength were applied and evaluated for suitability in predicting the mechanical behavior of SiC/RBSN and enhanced SiC/SiC composites. The SiC/RBSN composite exhibited pseudo tough behavior (increased area under the stress/strain curve) from 22 C to 1500 C. The rule of mixtures provides a good estimate of the Young's modulus of the SiC/RBSN composite using the constituent properties from room temperature to 1440 C for short term static tensile tests in air or nitrogen. The rule of mixtures significantly overestimates the secondary modulus near the ultimate strength. The ACK theory provides the best approximation of the first matrix cracking stress when residual stresses are ignored. The theory of Cao and Thouless, based on Weibull statistics, gave the best prediction for the composite ultimate strength. The enhanced SiC/SiC composite exhibited nonlinear stress/strain behavior from 24 C to 1370 C in air with increased ultimate strain when compared to monolithic SiC. The theory of Yang and Chou with the assumption of a frictional fiber/matrix interface provided the best estimate of the Young's modulus. The theory of Cao and Thouless gave the best estimate for the ultimate strength.

Fused silicon-rich coatings for superalloys

NASA Technical Reports Server (NTRS)

Smialek, J. L.

1974-01-01

Various compositions of nickel-silicon and aluminum-silicon slurries were sprayed on IN 100 specimens and fusion-sintered to form fully dense coatings. Cyclic furnace oxidation tests in 1 atm air at 1100 C showed all the coatings to be protective for at least 600 hours, and one slurry, Al-60Si, was protective for 1000 hours. This coating also protected NASA TAZ 8A and NASA-TRW VIA for 1000 hours in the same furnace test. Alloys B 1900, TD-NiCr, and Mar-M200 were protected for lesser times, while NX 188 and NASA WAZ 20 were scarcely protected at all. Limited stress-rupture testing on 0.64-cm-diam IN 100 specimens detected no degradation of mechanical properties due to silicon diffusion.

Testing system for ferromagnetic shape memory microactuators.

PubMed

Ganor, Y; Shilo, D; Messier, J; Shield, T W; James, R D

2007-07-01

Ferromagnetic shape memory alloys are a class of smart materials that exhibit a unique combination of large strains and fast response when exposed to magnetic field. Accordingly, these materials have significant potential in motion generation applications such as microactuators and sensors. This article presents a novel experimental system that measures the dynamic magnetomechanical behavior of microscale ferromagnetic shape memory specimens. The system is comprised of an alternating magnetic field generator (AMFG) and a mechanical loading and sensing system. The AMFG generates a dynamic magnetic field that periodically alternates between two orthogonal directions to facilitate martensitic variant switching and to remotely achieve a full magnetic actuation cycle, without the need of mechanical resetting mechanisms. Moreover, the AMFG is designed to produce a magnetic field that inhibits 180 degrees magnetization domain switching, which causes energy loss without strain generation. The mechanical loading and sensing system maintains a constant mechanical load on the measured specimen by means of a cantilever beam, while the displacement is optically monitored with a resolution of approximately 0.1 microm. Preliminary measurements using Ni(2)MnGa single crystal specimens, with a cross section of 100x100 microm(2), verified their large actuation strains and established their potential to become a material of great importance in microactuation technology.

Effects of Simulated Functional Loading Conditions on Dentin, Composite, and Laminate Structures

PubMed Central

Walker, Mary P.; Teitelbaum, Heather K.; Eick, J. David; Williams, Karen B.

2008-01-01

Use of composite restorations continues to increase, tempered by more potential problems when placed in posterior dentition. Thus, it is essential to understand how these materials function under stress-bearing clinical conditions. Since mastication is difficult to replicate in the laboratory, cyclic loading is frequently used within in vitro evaluations but often employs traditional fatigue testing, which typically does not simulate occlusal loading because higher stresses and loading frequencies are used, so failure mechanisms may be different. The present investigation utilized relevant parameters (specimen size; loading frequency) to assess the effects of cyclic loading on flexural mechanical properties and fracture morphology of (coronal) dentin, composite, and dentin-adhesive-composite “laminate” structures. Incremental monitoring of flexural modulus on individual beams over 60,000 loading cycles revealed a gradual increase across materials; post-hoc comparisons indicated statistical significance only for 1 versus 60k cycles. Paired specimens were tested (one exposed to 60k loading cycles, one to static loading only), and comparisons of flexural modulus and strength showed statistically significantly higher values for cyclically-loaded specimens across materials, with no observable differences in fracture morphology. Localized reorganization of dentin collagen and polymer chains could have increased flexural modulus and strength during cyclic loading, which may have implications toward the life and failure mechanisms of clinical restorations and underlying tooth structure. PMID:18823019

Assessment of osteoinduction using a porous hydroxyapatite coating prepared by micro-arc oxidation on a new titanium alloy.

PubMed

Jing, Wensen; Zhang, Minghua; Jin, Lei; Zhao, Jian; Gao, Qing; Ren, Min; Fan, Qingyu

2015-12-01

Surface modification and material improvement is now an important way to improve the osseointegration between bone and uncemented prothesis. The purpose of this study was to investigate the bone ingrowth potential of porous hydroxyapatite (HA) coatings prepared by micro-arc oxidation (MAO) on Ti-3Zr-2Sn-3Mo-25Nb, a new titanium alloy. HA-coated specimens were implanted in the left proximal femoral medullary canal of beagles for 4, 12, and 24 weeks, and uncoated specimens were implanted in the right as a control. The surface morphology and phase composition were investigated with environmental scanning electron microscopy and X-ray diffractometry. The bone ingrowth was assessed by histomorphometry. A pull-out test was performed to assess the mechanical performance of the bone-implant interface. A porous coating was well prepared on the new titanium alloy by using the MAO method. The bone-to-implant contact was significantly higher for the HA-coated group compared to that in the uncoated group. Mechanical tests showed that the HA-coated group had significantly higher maximum force at the bone-implant interface compared to the uncoated specimens. MAO is a suitable coating approach for this new titanium alloy. The HA coating prepared by this approach can significantly promote bone ingrowth and the mechanical performance of the bone-implant interface. Copyright © 2015. Published by Elsevier Ltd.

Evaluation of Test Methods for Triaxially Braided Composites using a Meso-Scale Finite Element Model

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Chao

The characterization of triaxially braided composite is complicate due to the nonuniformity of deformation within the unit cell as well as the possibility of the freeedge effect related to the large size of the unit cell. Extensive experimental investigation has been conducted to develop more accurate test approaches in characterizing the actual mechanical properties of the material we are studying. In this work, a meso-scale finite element model is utilized to simulate two complex specimens: notched tensile specimen and tube tensile specimen, which are designed to avoid the free-edge effect and free-edge effect induced premature edge damage. The full fieldmore » strain data is predicted numerically and compared with experimental data obtained by Digit Image Correlation. The numerically predicted tensile strength values are compared with experimentally measured results. The discrepancy between numerically predicted and experimentally measured data, the capability of different test approaches are analyzed and discussed. The presented numerical model could serve as assistance to the evaluation of different test methods, and is especially useful in identifying potential local damage events.« less

Water sensitivity of the seismic properties of polycrystalline olivine

NASA Astrophysics Data System (ADS)

Cline, C. J., II; Jackson, I.; Faul, U.; Berry, A.

2016-12-01

Fully synthetic solgel-derived Fo90 olivine specimens have been fabricated with varying concentrations of hydroxyl, chemically bound as doubly protonated Si vacancies associated with nearby Ti/Mg substitution (the `Ti-clinohumite' defect). The `water' contents of three such specimens hot-pressed within welded Pt capsules are controlled by the amount of added TiO2-dopant and ranged between 176 and 802 ppm Ti/Si, providing concentrations of bound hydrogen ranging between 330 and 1150 ppm H/Si respectively. These sol-gel derived specimens, along with another natural Ti-bearing specimen hot-pressed from powder produced by grinding hand-picked single crystals of San Carlos olivine, were then each subsequently wrapped in Pt and interrogated under water-undersaturated conditions via forced torsional oscillation. Testing was conducted at seismic periods of 1 - 1000 s and 200 MPa confining pressure during slow staged cooling from 1200 to 25 °C. All Ti-doped hydrous specimens tested, including the San Carlos olivine specimen, show high temperature background behavior, involving monotonically increasing levels of dissipation and decreasing values of shear modulus with increasing oscillation period and increasing temperature. Comparison of the mechanical behavior observed in these water-undersaturated specimens to that for a similarly fabricated dry Ti-bearing olivine specimen shows a striking contrast, with much more dissipation and lower modulus observed in the hydrous specimens, but with limited sensitivity of seismic properties to the total water content among the hydrous specimens in the series. Further experiments in progress on Pt-sleeved, dry, undoped Fo90 are designed to clarify further the sensitivity of the seismic properties to water content and possibly oxygen fugacity.

Femtosecond laser machining for characterization of local mechanical properties of biomaterials: a case study on wood

PubMed Central

Jakob, Severin; Pfeifenberger, Manuel J.; Hohenwarter, Anton; Pippan, Reinhard

2017-01-01

Abstract The standard preparation technique for micro-sized samples is focused ion beam milling, most frequently using Ga+ ions. The main drawbacks are the required processing time and the possibility and risks of ion implantation. In contrast, ultrashort pulsed laser ablation can process any type of material with ideally negligible damage to the surrounding volume and provides 4 to 6 orders of magnitude higher ablation rates than the ion beam technique. In this work, a femtosecond laser was used to prepare wood samples from spruce for mechanical testing at the micrometre level. After optimization of the different laser parameters, tensile and compressive specimens were produced from microtomed radial-tangential and longitudinal-tangential sections. Additionally, laser-processed samples were exposed to an electron beam prior to testing to study possible beam damage. The specimens originating from these different preparation conditions were mechanically tested. Advantages and limitations of the femtosecond laser preparation technique and the deformation and fracture behaviour of the samples are discussed. The results prove that femtosecond laser processing is a fast and precise preparation technique, which enables the fabrication of pristine biological samples with dimensions at the microscale. PMID:28970867

Femtosecond laser machining for characterization of local mechanical properties of biomaterials: a case study on wood

NASA Astrophysics Data System (ADS)

Jakob, Severin; Pfeifenberger, Manuel J.; Hohenwarter, Anton; Pippan, Reinhard

2017-12-01

The standard preparation technique for micro-sized samples is focused ion beam milling, most frequently using Ga+ ions. The main drawbacks are the required processing time and the possibility and risks of ion implantation. In contrast, ultrashort pulsed laser ablation can process any type of material with ideally negligible damage to the surrounding volume and provides 4 to 6 orders of magnitude higher ablation rates than the ion beam technique. In this work, a femtosecond laser was used to prepare wood samples from spruce for mechanical testing at the micrometre level. After optimization of the different laser parameters, tensile and compressive specimens were produced from microtomed radial-tangential and longitudinal-tangential sections. Additionally, laser-processed samples were exposed to an electron beam prior to testing to study possible beam damage. The specimens originating from these different preparation conditions were mechanically tested. Advantages and limitations of the femtosecond laser preparation technique and the deformation and fracture behaviour of the samples are discussed. The results prove that femtosecond laser processing is a fast and precise preparation technique, which enables the fabrication of pristine biological samples with dimensions at the microscale.

A mechanical property and stress corrosion evaluation of VIM-ESR-VAR work strengthened and direct double aged Inconel 718 bar material

NASA Technical Reports Server (NTRS)

Montano, J. W.

1986-01-01

Presented are the mechanical properties and the stress corrosion resistance of triple melted vacuum induction melted (VIM), electro-slag remelted (ESR), and vacuum arc remelted (VAR), solution treated, work strengthened and direct double aged Inconel 718 alloy bars 4.00 in. (10.16) and 5.75 in. (14.60 cm) diameter. Tensile, charpy v-notched impact, and compact tension specimens were tested at ambient temperature in both the longitudinal and transverse directions. Longitudinal tensile and yield strengths in excess of 220 ksi (1516.85 MPa) and 200 ksi (1378.00 MPa) respectively, were realized at ambient temperature. Additional charpy impact and compact tension tests were performed at -100 F (-73 C). Longitudinal charpy impact strength equalled or exceeded 12.0 ft-lbs (16.3 Joules) at ambient and at -100 F(-73 C) while longitudinal compact (LC) tension fracture toughness strength remained above 79 ksi (86.80 MPa) at ambient and at -100 F(-73 C) temperatures. No failures occurred in the longitudinal or transverse tensile specimens stressed to 75 and 100 percent of their respective yield strengths and exposed to a salt fog environment for 180 days. Tensile tests performed after the stress corrosion test indicated no mechanical property degradation.

Role of the Middle Lumbar Fascia on Spinal Mechanics: A Human Biomechanical Assessment.

PubMed

Ranger, Tom A; Newell, Nicolas; Grant, Caroline A; Barker, Priscilla J; Pearcy, Mark J

2017-04-15

Biomechanical experiment. The aims of the present study were to test the effect of fascial tension on lumbar segmental axial rotation and lateral flexion and the effect of the angle of fascial attachment. Tension in the middle layer of lumbar fascia has been demonstrated to affect mechanical properties of lumbar segmental flexion and extension in the neutral zone. The effect of tension on segmental axial rotation and lateral flexion has, however, not been investigated. Seven unembalmed lumbar spines were divided into segments and mounted for testing. A 6 degree-of-freedom robotic testing facility was used to displace the segments in each anatomical plane (flexion-extension, lateral bending, and axial rotation) with force and moment data recorded by a load cell positioned beneath the test specimen. Tests were performed with and without a 20 N fascia load and the subsequent forces and moments were compared. In addition, forces and moments were compared when the specimens were held in a set position and the fascia loading angle was varied. A fascial tension of 20 N had no measurable effect on the forces or moments measured when the specimens were displaced in any plane of motion (P > 0.05). When 20 N of fascial load were applied to motion segments in a set position small segmental forces and moments were measured. Changing the angle of the fascial load did not significantly alter these measurements. Application of a 20 N fascial load did not produce a measureable effect on the mechanics of a motion segment, even though it did produce small measurable forces and moments on the segments when in a fixed position. Results from the present study are inconsistent with previous studies, suggesting that further investigation using multiple testing protocols and different loading conditions is required to determine the effects of fascial loading on spinal segment behavior. N/A.

Wideband MRE and static mechanical indentation of human liver specimen: sensitivity of viscoelastic constants to the alteration of tissue structure in hepatic fibrosis.

PubMed

Reiter, Rolf; Freise, Christian; Jöhrens, Korinna; Kamphues, Carsten; Seehofer, Daniel; Stockmann, Martin; Somasundaram, Rajan; Asbach, Patrick; Braun, Jürgen; Samani, Abbas; Sack, Ingolf

2014-05-07

Despite the success of elastography in grading hepatic fibrosis by stiffness related noninvasive markers the relationship between viscoelastic constants in the liver and tissue structure remains unclear. We therefore studied the mechanical properties of 16 human liver specimens with different degrees of fibrosis, inflammation and steatosis by wideband magnetic resonance elastography (MRE) and static indentation experiments providing the specimens׳ static Young׳s modulus (E), dynamic storage modulus (G') and dynamic loss modulus (G″). A frequency-independent shear modulus μ and a powerlaw exponent α were obtained by fitting G' and G″ using the two-parameter sprinpot model. The mechanical parameters were compared to the specimens׳ histology derived parameters such as degree of Fibrosis (F), inflammation score and fat score, amount of hydroxyproline (HYP) used for quantification of collagen, blood markers and presurgery in vivo function tests. The frequency averaged parameters G', G″ and μ were significantly correlated with F (G': R=0.762, G″: R=0.830; μ: R=0.744; all P<0.01) and HYP (G': R=0.712; G″: R=0.720; μ: R=0.731; all P<0.01). The powerlaw exponent α displayed an inverse correlation with F (R=-0.590, P=0.034) and a trend of inverse correlation with HYP (R=-0.470, P=0.089). The static Young׳s modulus E was less correlated with F (R=0.587, P=0.022) and not sensitive to HYP. Although inflammation was highly correlated with F (R=0.773, P<0.001), no interaction was discernable between inflammation and mechanical parameters measured in this study. Other histological and blood markers as well as liver function test were correlated with neither F nor the measured mechanical parameters. In conclusion, viscoelastic constants measured by wideband MRE are highly sensitive to histologically proven fibrosis. Our results suggest that, in addition to the amount of connective tissue, subtle structural changes of the viscoelastic matrix determine the sensitivity of mechanical tissue properties to hepatic fibrosis. Copyright © 2014 Elsevier Ltd. All rights reserved.

Surface characteristics and biocompatibility of cranioplasty titanium implants following different surface treatments.

PubMed

Hatamleh, Muhanad M; Wu, Xiaohong; Alnazzawi, Ahmad; Watson, Jason; Watts, David

2018-04-01

Surface and mechanical properties of titanium alloys are integral for their use in restoring bone defects of skull and face regions. These properties are affected by the method of constructing and surface treatment of the titanium implant. This study aimed to investigate the effects of titanium finishing protocols on the surface morphology, hardness and biocompatibility of TiAl6V4. Square shaped TiAl6V4 specimens (ASTM F68) (10×10×0.5mm) were divided into seven groups of different surface treatments (n=10). The treatments included mechanical polishing, sandblasting with AL 2 O 3 (50μm), immersion in different acids, and/or electro-chemical anodization. Weight loss %; 3D micro-roughness; Knoop micro-hardness, and osteoblast cell attachment and proliferation (after 3 days) were determined for each specimen. Data was analysed using one way ANOVA and Dunett T3 post-hoc tests, and t-test (p<0.05). Weight loss % was in the range of 1.70-5.60 as mechanical polishing produced the highest weight loss, followed by sandblasting, and combined protocol of mechanical polishing and acid treatment (p<0.05). Micro-roughness values (μm) were in the range of 2.81-16.68. It was the highest for control specimens (p<0.05), and smoothest surfaces after combined mechanical polishing and acid treatment; or after electro-chemical treatment (p<0.05). Micro-hardness values (MPa) ranged 170.90-442.15 as sandblasting with/without acid treatment caused statically significantly the highest values (p<0.05) while control and mechanically polished specimens had the lowest values (p<0.05). All treatments produced equally biocompatible surfaces (p>0.05) after 1h or 3 days. Furthermore, osteoblast cell proliferation statistically significantly increased after 3days among each surface treatment (p<0.05). Different finishing treatments have variable effect on cranioplasty titanium surface loss, micro-roughness and micro-hardness but constant improved biocompatibility effect. Electro-chemical treatment caused less material loss and produced biocompatible smoothest surface of comparable hardness; hence it can be suitable for cranioplasty titanium surface finishing. Copyright © 2018 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Thermo-Mechanical Fatigue of a Fiber Reinforced Titanium Aluminide Composite

DTIC Science & Technology

1991-03-01

Puiitr]on Air Foic. Base, Oiio 91 10 25 038 DTIC 4E L L E C :i<. THERMO- MECHAN I CAL FAT I GUE OF A FIBER REINFORCED TITANIUM ALUMINIDE COMPOSITE Thesis...reinforced titanium aluminide composite was investigated. Three test specimens were subjected to in-phase thermo- mechanical cycling and four to out-of...Unclassified UL ............................... AFIT/GAE/ENY/91S-1 THERMO- MECHANICAL FATIGUE OF A FIBER REINFORCED TITANIUM ALUMINIDE COMPOSITE THESIS

Using Hysteretic Energy to Evaluate Damping Characteristics of Hard Coating on Titanium

DTIC Science & Technology

2013-03-21

Ivancic, Frank T. The Effect of a Hard Coating on the Damping and Fatigue Life of Titanium. Air Force Institute of Technology (AU), Wright-Patterson AFB... aluminum specimens to determine the effects of losses for different grip mechanisms, a suspected problem in previous work with this method. Peak...done in a vacuum, and the nature of the free-decay test also confines strain to relatively low values for coated specimens (< 1000 µε) (Reed 2007

Effect of Stress Ratio on Fatigue Crack Growth Rate at Notched Hole in 7075-T6 Aluminum Alloy Under Biaxial Fatigue

DTIC Science & Technology

2016-08-18

Taylor and Lee studied the effect of in-plane stress biaxility on the fatigue life [22]. Research in this subject is going on but no research done to...closer picture to the hole, notch, pre -crack and the crack in one of the specimens in Abaqus program...which is the scope of this research , using fracture mechanics approach. 6 To achieve the purpose of this study , the specimen has to be test

Effects of age and loading rate on equine cortical bone failure.

PubMed

Kulin, Robb M; Jiang, Fengchun; Vecchio, Kenneth S

2011-01-01

Although clinical bone fractures occur predominantly under impact loading (as occurs during sporting accidents, falls, high-speed impacts or other catastrophic events), experimentally validated studies on the dynamic fracture behavior of bone, at the loading rates associated with such events, remain limited. In this study, a series of tests were performed on femoral specimens obtained post-mortem from equine donors ranging in age from 6 months to 28 years. Fracture toughness and compressive tests were performed under both quasi-static and dynamic loading conditions in order to determine the effects of loading rate and age on the mechanical behavior of the cortical bone. Fracture toughness experiments were performed using a four-point bending geometry on single and double-notch specimens in order to measure fracture toughness, as well as observe differences in crack initiation between dynamic and quasi-static experiments. Compressive properties were measured on bone loaded parallel and transverse to the osteonal growth direction. Fracture propagation was then analyzed using scanning electron and scanning confocal microscopy to observe the effects of microstructural toughening mechanisms at different strain rates. Specimens from each horse were also analyzed for dry, wet and mineral densities, as well as weight percent mineral, in order to investigate possible influences of composition on mechanical behavior. Results indicate that bone has a higher compressive strength, but lower fracture toughness when tested dynamically as compared to quasi-static experiments. Fracture toughness also tends to decrease with age when measured quasi-statically, but shows little change with age under dynamic loading conditions, where brittle "cleavage-like" fracture behavior dominates. Copyright © 2010 Elsevier Ltd. All rights reserved.

1000537

NASA Image and Video Library

2010-04-13

NATHAN HORACE STRONG (AEROSPACE ENGINEER, ER31 PROPULSION TURBOMACHINERY DESIGN & DEVELOPMENT BRANCH) AND NATHAN COFFEE (EM10 MATERIALS TEST ENGINEER, JACOBS ESTS GROUP/JTI) ADJUST A UNIQUE MECHANICAL TEST SETUP THAT MEASURES STRAIN ON A SINGLE SAMPLE, USING TWO DIFFERENT TECHNIQUES AT THE SAME TIME. THE TEST FIXTURE HOLDS A SPECIMEN THAT REPRESENTS A LIQUID OXYGEN (LOX) BEARING FROM THE J2-X ENGINE. COFFEY, AT RIGHT, WORK IN A LAB IN BUILDING 4612 ON A BEARING TEST

Mechanical Behavior of Brittle Rock-Like Specimens with Pre-existing Fissures Under Uniaxial Loading: Experimental Studies and Particle Mechanics Approach

NASA Astrophysics Data System (ADS)

Cao, Ri-hong; Cao, Ping; Lin, Hang; Pu, Cheng-zhi; Ou, Ke

2016-03-01

Joints and fissures with similar orientation or characteristics are common in natural rocks; the inclination and density of the fissures affect the mechanical properties and failure mechanism of the rock mass. However, the strength, crack coalescence pattern, and failure mode of rock specimens containing multi-fissures have not been studied comprehensively. In this paper, combining similar material testing and discrete element numerical method (PFC2D), the peak strength and failure characteristics of rock-like materials with multi-fissures are explored. Rock-like specimens were made of cement and sand and pre-existing fissures created by inserting steel shims into cement mortar paste and removing them during curing. The peak strength of multi-fissure specimens depends on the fissure angle α (which is measured counterclockwise from horizontal) and fissure number ( N f). Under uniaxial compressional loading, the peak strength increased with increasing α. The material strength was lowest for α = 25°, and highest for α = 90°. The influence of N f on the peak strength depended on α. For α = 25° and 45°, N f had a strong effect on the peak strength, while for higher α values, especially for the 90° sample, there were no obvious changes in peak strength with different N f. Under uniaxial compression, the coalescence modes between the fissures can be classified into three categories: S-mode, T-mode, and M-mode. Moreover, the failure mode can be classified into four categories: mixed failure, shear failure, stepped path failure, and intact failure. The failure mode of the specimen depends on α and N f. The peak strength and failure modes in the numerically simulated and experimental results are in good agreement.

Evaluation of fracture toughness and mechanical properties of ternary thiol-ene-methacrylate systems as resin matrix for dental restorative composites.

PubMed

Beigi, Saeed; Yeganeh, Hamid; Atai, Mohammad

2013-07-01

Study and evaluation of fracture toughness, flexural and dynamic mechanical properties, and crosslink density of ternary thiol-ene-methacrylate systems and comparison with corresponding conventional methacrylate system were considered in the present study. Urethane tetra allyl ether monomer (UTAE) was synthesized as ene monomer. Different formulations were prepared based on combination of UTAE, BisGMA/TEGDMA and a tetrathiol monomer (PETMP). The photocuring reaction was conducted under visible light using BD/CQ combination as photoinitiator system. Mechanical properties were evaluated via measuring flexural strength, flexural modulus and fracture toughness. Scanning electron microscopy (SEM) was utilized to study the morphology of the fractured specimen's cross section. Viscoelastic properties of the samples were also determined by dynamic mechanical thermal analysis (DMTA). The same study was performed on a conventional methacrylate system. The data were analyzed and compared by ANOVA and Tukey HSD tests (significance level=0.05). The results showed improvement in fracture toughness of the specimens containing thiol-ene moieties. DMTA revealed a lower glass transition temperature and more homogenous structure for thiol-ene containing specimens in comparison to the system containing merely methacrylate monomer. The flexural modulus and flexural strength of the specimens with higher thiol-ene content were lower than the neat methacrylate system. The SEM micrographs of the fractured surface of specimens with higher methacrylate content were smooth and mirror-like (shiny) which represent brittle fracture. The thiol-ene-methacrylate system can be used as resin matrix of dental composites with enhanced fracture toughness in comparison to the methacrylate analogous. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Status of Initial Assessment of Physical and Mechanical Properties of Graphite Grades for NGNP Appkications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Strizak, Joe P; Burchell, Timothy D; Windes, Will

2011-12-01

Current candidate graphite grades for the core structures of NGNP include grades NBG-17, NBG-18, PCEA and IG-430. Both NBG-17 and NBG-18 are manufactured using pitch coke, and are vibrationally molded. These medium grain products are produced by SGL Carbon SAS (France). Tayo Tanso (Japan) produces IG-430 which is a petroleum coke, isostatically molded, nuclear grade graphite. And PCEA is a medium grain, extruded graphite produced by UCAR Carbon Co. (USA) from petroleum coke. An experimental program has been initiated to develop physical and mechanical properties data for these current candidate graphites. The results will be judged against the requirements formore » nuclear grade graphites set forth in ASTM standard D 7219-05 "Standard Specification for Isotropic and Near-isotropic Nuclear Graphites". Physical properties data including thermal conductivity and coefficient of thermal expansion, and mechanical properties data including tensile, compressive and flexural strengths will be obtained using the established test methods covered in D-7219 and ASTM C 781-02 "Standard Practice for Testing Graphite and Boronated Graphite Components for High-Temperature Gas-Cooled Nuclear Reactors". Various factors known to effect the properties of graphites will be investigated. These include specimen size, spatial location within a graphite billet, specimen orientation (ag and wg) within a billet, and billet-to-billet variations. The current status of the materials characterization program is reported herein. To date billets of the four graphite grades have been procured, and detailed cut up plans for obtaining the various specimens have been prepared. Particular attention has been given to the traceability of each specimen to its spatial location and orientation within a billet.« less

Glaucoma-related Changes in the Mechanical Properties and Collagen Micro-architecture of the Human Sclera

PubMed Central

Coudrillier, Baptiste; Pijanka, Jacek K.; Jefferys, Joan L.; Goel, Adhiraj; Quigley, Harry A.; Boote, Craig; Nguyen, Thao D.

2015-01-01

Objective The biomechanical behavior of the sclera determines the level of mechanical insult from intraocular pressure to the axons and tissues of the optic nerve head, as is of interest in glaucoma. In this study, we measure the collagen fiber structure and the strain response, and estimate the material properties of glaucomatous and normal human donor scleras. Methods Twenty-two posterior scleras from normal and diagnosed glaucoma donors were obtained from an eyebank. Optic nerve cross-sections were graded to determine the presence of axon loss. The specimens were subjected to pressure-controlled inflation testing. Full-field displacement maps were measured by digital image correlation (DIC) and spatially differentiated to compute surface strains. Maps of the collagen fiber structure across the posterior sclera of each inflated specimen were obtained using synchrotron wide-angle X-ray scattering (WAXS). Finite element (FE) models of the posterior scleras, incorporating a specimen-specific representation of the collagen structure, were constructed from the DIC-measured geometry. An inverse finite element analysis was developed to estimate the stiffness of the collagen fiber and inter-fiber matrix. Results The differences between glaucoma and non-glaucoma eyes were small in magnitude. Sectorial variations of degree of fiber alignment and peripapillary scleral strain significantly differed between normal and diagnosed glaucoma specimens. Meridional strains were on average larger in diagnosed glaucoma eyes compared with normal specimens. Non-glaucoma specimens had on average the lowest matrix and fiber stiffness, followed by undamaged glaucoma eyes, and damaged glaucoma eyes but the differences in stiffness were not significant. Conclusion The observed biomechanical and microstructural changes could be the result of tissue remodeling occuring in glaucoma and are likely to alter the mechanical environment of the optic nerve head and contribute to axonal damage. PMID:26161963

Microgravity

NASA Image and Video Library

1998-01-01

On STS-89, three Mechanics of Granular Materials (MGM) test cells were subjected to five cycles of compression and relief (left) and three were subjected to shorter displacement cycles that simulate motion during an earthquake (right). In the compression/relief tests, the sand particles rearranged themselves and slightly re-expanded the column during relief. In the short displacement tests, the specimen's resistance to compression decreases, even though the displacement remains the same. The specimens were cycled up to 100 times or until the resistive force was less than 1% that of the previous cycle. Sand and soil grains have faces that can cause friction as they roll and slide against each other, or even cause sticking and form small voids between grains. This complex behavior can cause soil to behave like a liquid under certain conditions such as earthquakes or when powders are handled in industrial processes. Mechanics of Granular Materials (MGM) experiments aboard the Space Shuttle use the microgravity of space to simulate this behavior under conditons that carnot be achieved in laboratory tests on Earth. MGM is shedding light on the behavior of fine-grain materials under low effective stresses. Applications include earthquake engineering, granular flow technologies (such as powder feed systems for pharmaceuticals and fertilizers), and terrestrial and planetary geology. Nine MGM specimens have flown on two Space Shuttle flights. Another three are scheduled to fly on STS-107. The principal investigator is Stein Sture of the University of Colorado at Boulder. Credit: NASA/Marshall Space Flight Center (MSFC)

Design and fabrication of titanium multi-wall Thermal Protection System (TPS) test panels

NASA Technical Reports Server (NTRS)

Blair, W.; Meaney, J. E., Jr.; Rosenthal, H. A.

1980-01-01

A titanium multiwall thermal protection system panel was designed. The panel is a nine sheet sandwich structure consisting of an upper and lower face sheet; four dimpled sheets, three septum sheets, and clips for attachment to a vehicle structure. An acceptable fabrication process was developed, and the panel design was verified through mechanical and thermal testing of component specimens. A design was completed which takes into consideration fabrication techniques, thermal properties, mechanical properties, and materials availability.

Ultrasonic NDE and mechanical testing of fiber placement composites

NASA Astrophysics Data System (ADS)

Liu, Zhanjie; Fei, Dong; Hsu, David K.; Dayal, Vinay; Hale, Richard D.

2002-05-01

A fiber placed composite, especially with fiber steering, has considerably more complex internal structure than a laminate laid up from unidirectional prepreg tapes. In this work, we performed ultrasonic imaging of ply interfaces of fiber placed composite laminates, with an eye toward developing a tool for evaluating their quality. Mechanical short-beam shear tests were also conducted on both nonsteered and steered specimens to examine their failure behavior and its relationship to the structural defects indicated by ultrasonic imaging.

Revealing Slip Bands In A Metal-Matrix/Fiber Composite

NASA Technical Reports Server (NTRS)

Lerch, Bradley A.

1995-01-01

Experimental procedure includes heat treatments and metallographic techniques developed to facilitate studies of deformation of metal-matrix/fiber composite under stress. Reveals slip bands, indicative of plastic flow occurring in matrix during mechanical tests of specimens of composite.

A study of creep crack growth in 2219-T851

NASA Astrophysics Data System (ADS)

Bensussan, Philippe L.; Jablonski, David A.; Pelloux, Regis M.

1984-01-01

Creep crack growth rates were measured in high strength 2219-T851 aluminum alloy with a computerized fully automated test procedure. Crack growth tests were performed on CT specimens with side grooves. The experimental set-up is described. During a test, the specimen is cyclically loaded on a servohydraulic testing machine under computer control, maintained at maximum load for a given hold time at each cycle, unloaded, and then reloaded. Crack lengths are obtained from compliance measurements recorded during each unloading. It is shown that the measured crack growth rates per cycle do represent creep crack growth rates per unit time for hold times longer than 10 seconds. The validity of LEFM concepts for side-grooved specimens is reviewed, and compliance and stress intensity factor calibrations for such specimens are reported. For the range of testing conditions of this study, 2219-T851 is shown to be creep brittle in terms of concepts of fracture mechanics of creeping solids. It is found that, under these testing conditions, a correlation exists between the creep crack growth rates under plane strain conditions and the stress intensity factor ( da/dt = A K 3.8 at 175 °C) for simple K histories in a regime of steady or quasi-steady state crack growth. The micromechanisms of fracture are determined to be of complex nature. The fracture mode is observed to be mixed inter- and transgranular, the relative amount of intergranular fracture decreasing as K and da/dt increase.

Fatigue Behavior and Deformation Mechanisms in Inconel 718 Superalloy Investigated

NASA Technical Reports Server (NTRS)

2005-01-01

The nickel-base superalloy Inconel 718 (IN 718) is used as a structural material for a variety of components in the space shuttle main engine (SSME) and accounts for more than half of the total weight of this engine. IN 718 is the bill-of-material for the pressure vessels of nickel-hydrogen batteries for the space station. In the case of the space shuttle main engine, structural components are typically subjected to startup and shutdown load transients and occasional overloads in addition to high-frequency vibratory loads from routine operation. The nickel-hydrogen battery cells are prooftested before service and are subjected to fluctuating pressure loads during operation. In both of these applications, the structural material is subjected to a monotonic load initially, which is subsequently followed by fatigue. To assess the life of these structural components, it is necessary to determine the influence of a prior monotonic load on the subsequent fatigue life of the superalloy. An insight into the underlying deformation and damage mechanisms is also required to properly account for the interaction between the prior monotonic load and the subsequent fatigue loading. An experimental investigation was conducted to establish the effect of prior monotonic straining on the subsequent fatigue behavior of wrought, double-aged, IN 718 at room temperature. First, monotonic strain tests and fully-reversed, strain-controlled fatigue tests were conducted on uniform-gage-section IN 718 specimens. Next, fully reversed fatigue tests were conducted under strain control on specimens that were monotonically strained in tension. Results from this investigation indicated that prior monotonic straining reduced the fatigue resistance of the superalloy particularly at the lowest strain range. Some of the tested specimens were sectioned and examined by transmission electron microscopy to reveal typical microstructures as well as the active deformation and damage mechanisms under each of the loading conditions. In monotonically strained specimens, deformation during the subsequent fatigue loading was mainly confined to the deformation bands initiated during the prior monotonic straining. This can cause dislocations to move more readily along the previously activated deformation bands and to pile up near grain boundaries, eventually making the grain boundaries susceptible to fatigue crack initiation. The mechanisms inferred from the microstructural investigation were extremely valuable in interpreting the influence of prior monotonic straining on the subsequent fatigue life of Inconel 718 superalloy.

Experimental measurement of lattice strain pole figures using synchrotron x rays

DOE Office of Scientific and Technical Information (OSTI.GOV)

Miller, M.P.; Bernier, J.V.; Park, J.-S.

This article describes a system for mechanically loading test specimens in situ for the determination of lattice strain pole figures and their evolution in multiphase alloys via powder diffraction. The data from these experiments provide insight into the three-dimensional mechanical response of a polycrystalline aggregate and represent an extremely powerful material model validation tool. Relatively thin (0.5 mm) iron/copper specimens were axially strained using a mechanical loading frame beyond the macroscopic yield strength of the material. The loading was halted at multiple points during the deformation to conduct a diffraction experiment using a 0.5x0.5 mm{sup 2} monochromatic (50 keV) xmore » ray beam. Entire Debye rings of data were collected for multiple lattice planes ({l_brace}hkl{r_brace}'s) in both copper and iron using an online image plate detector. Strain pole figures were constructed by rotating the loading frame about the specimen transverse direction. Ideal powder patterns were superimposed on each image for the purpose of geometric correction. The chosen reference material was cerium (IV) oxide powder, which was spread in a thin layer on the downstream face of the specimen using petroleum jelly to prevent any mechanical coupling. Implementation of the system at the A2 experimental station at the Cornell High Energy Synchrotron Source (CHESS) is described. The diffraction moduli measured at CHESS were shown to compare favorably to in situ data from neutron-diffraction experiments conducted on the same alloys.« less

Fracture-induced mechanophore activation and solvent healing in poly(methyl methacrylate)

NASA Astrophysics Data System (ADS)

Celestine, Asha-Dee N.

Damage detection is a highly desirable functionality in engineering materials. The potential of using mechanophores, stress-sensitive molecules, as material stress sensors has been established through tensile, compressive and shear tests. Spiropyran (SP) has been the chosen mechanophore and this molecule undergoes a ring opening reaction (activation) upon the application of mechanical stress. This activation is accompanied by a change in color and fluorescence as the colorless SP is converted to the highly colored merocyanine (MC) form. One requirement for SP activation in bulk polymers is large scale plastic deformation. In order to induce this plastic deformation during fracture testing of SP-linked brittle polymers such as poly(methyl methacrylate) (PMMA), rubber nanoparticles can be incorporated into the matrix material. These nanoparticles facilitate the increased shear yielding necessary for SP activation during mechanical testing. Cross-linked SP-PMMA, containing 7.3 wt% rubber nanoparticles is synthesized via a free radical polymerization. Specimens of this material are fabricated for Single Edge Notch Tension (SENT) testing. The rubber toughened SP-PMMA specimens are first prestretched to approximately 35% axial strain to align the spiropyran molecules in the direction of applied force and thus increase the likelihood of fracture-induced activation. After prestretching the specimens are pre-notched and irradiated with 532 nm wavelength light to revert the colored merocyanine to the colorless spiropyran form. Specimens are then fracture tested to failure using the SENT test. The evolution of mechanophore activation is monitored via in situ fluorescence imaging and inspection of the specimens after testing. Activation of the SP is observed ahead of the crack tip and along the propagated crack. Also, the degree of activation is found to increase with crack growth and the size of the activation zone is linearly correlated to the size of the plastic zone ahead of the crack tip. Control specimens in which the mechanophore is absent or tethered in positions in which no mechanochemical activation is expected are also tested and exhibit no change in color or fluorescence intensity with crack propagation. The relationship between fracture-induced mechanophore activation in rubber toughened SP-PMMA and the strain and stress ahead of the propagating crack is also studied. SP activation is again detected and quantified by in situ fluorescence imaging. Digital Image Correlation (DIC) is used to measure the strain ahead of the crack tip. The corresponding stress is generated through the use of the Hutchinson-Rice-Rosengren (HRR) singularity field equations. Mechanophore activation ahead of the crack tip is shown to follow a power law distribution that is closely aligned with strain. The potential of SP as a damage sensor is explored further by incorporating the spiropyran into the core of rubber nanoparticles. SP-linked rubber nanoparticles are synthesized using a seeded emulsion polymerization process and incorporated into cross-linked PMMA at a concentration of 5 wt%. Cylindrical specimens are torsion tested and the activation of the SP within the nanoparticles is monitored via full field fluorescence imaging. SP activation within the core is shown to increase with shear strain. Autonomous damage repair in PMMA is also investigated. The first demonstration of fully autonomous self-healing in PMMA is achieved through the use of solvent microcapsules. Solvent microcapsules with a PMMA-anisole liquid core are prepared and embedded within a linear PMMA matrix. Specimens of the microcapsule-loaded material are then fabricated for Double Cleavage Drilled Compression (DCDC) fracture testing. The DCDC specimens, containing increasing concentrations of solvent microcapsules, are tested and then allowed to heal for a fixed period of time before a second DCDC test. The healing efficiency of each material system is evaluated based on the recovery of fracture toughness and is shown to be dependent on healing time and microcapsule concentration. (Abstract shortened by UMI.).

Softening due to disordered grain boundaries in nanocrystalline Co.

PubMed

Yuasa, Motohiro; Hakamada, Masataka; Nakano, Hiromi; Mabuchi, Mamoru; Chino, Yasumasa

2013-08-28

Nanocrystalline Co consisting of fcc and hcp phases was processed by electrodeposition, and its mechanical properties were investigated by hardness tests. In addition, high-resolution transmission electron microscopy observations and molecular dynamics (MD) simulations were performed to investigate the grain boundary structure and dislocation nucleation from the grain boundaries. A large amount of disorders existed at the grain boundaries and stacking faults were formed from the grain boundaries in the as-deposited Co specimen. The as-deposited specimen showed a lower hardness than did the annealed specimen, although the grain size of the former was smaller than that of the latter. The activation volume of the as-deposited specimen (=1.5b(3)) was lower than that of the annealed specimen (=50b(3)), thus indicating that nucleation of dislocations from grain boundaries is more active in the as-deposited specimen than in the annealed specimens. The MD simulations showed that dislocation nucleation was closely related to a change in the defect structures at the boundary. Therefore, it is suggested that a significant amount of defects enhance changes in the defect structures at the boundary, resulting in softening of the as-deposited specimen.

Softening due to disordered grain boundaries in nanocrystalline Co

NASA Astrophysics Data System (ADS)

Yuasa, Motohiro; Hakamada, Masataka; Nakano, Hiromi; Mabuchi, Mamoru; Chino, Yasumasa

2013-08-01

Nanocrystalline Co consisting of fcc and hcp phases was processed by electrodeposition, and its mechanical properties were investigated by hardness tests. In addition, high-resolution transmission electron microscopy observations and molecular dynamics (MD) simulations were performed to investigate the grain boundary structure and dislocation nucleation from the grain boundaries. A large amount of disorders existed at the grain boundaries and stacking faults were formed from the grain boundaries in the as-deposited Co specimen. The as-deposited specimen showed a lower hardness than did the annealed specimen, although the grain size of the former was smaller than that of the latter. The activation volume of the as-deposited specimen (=1.5b3) was lower than that of the annealed specimen (=50b3), thus indicating that nucleation of dislocations from grain boundaries is more active in the as-deposited specimen than in the annealed specimens. The MD simulations showed that dislocation nucleation was closely related to a change in the defect structures at the boundary. Therefore, it is suggested that a significant amount of defects enhance changes in the defect structures at the boundary, resulting in softening of the as-deposited specimen.

Laboratory Characterization of SAM-35 Concrete

DTIC Science & Technology

2006-09-01

procedures given in American Society for Testing and Materials (ASTM) D 2216 (ASTM 2002e). Based on the appropriate values of posttest water content, wet...composition properties of the material. All of the mechanical property tests were conducted quasi -statically with axial strain rates on the order...nondestructive pulse-velocity measurements were performed on each specimen. The TXC tests exhibited a continuous increase in principal stress

In situ X-ray monitoring of damage accumulation in SiC/RBSN tensile specimens

NASA Technical Reports Server (NTRS)

Baaklini, George Y.; Bhatt, Ramkrishna T.

1991-01-01

The room-temperature tensile testing of silicon carbide fiber reinforced reaction-bonded silicon nitride (SiC/RBSN) composite specimens was monitored by using in-situ X-ray film radiography. Radiographic evaluation before, during, and after loading provided data on the effect of preexisting volume flaws (high density impurities, and local density variations) on the fracture behavior of composites. Results from (O)1, (O)3, (O)5, and (O)8 composite specimens showed that X-ray film radiography can monitor damage accumulations during tensile loading. Matrix cracking, fiber-matrix debonding, and fiber pullout were imaged throughout the tensile loading history of the specimens. Further, in-situ film radiography was found to be a helpful and practical technique for estimating interfacial shear strength between the SiC fiber and the RBSN matrix by the matrix crack spacing method. It is concluded that pretest, in-situ, and post-test radiography can provide for a greater understanding of ceramic matrix composite mechanical behavior, a verification of related experimental procedures, and a validation and development of related analytical models.

In-situ x-ray monitoring of damage accumulation in SiC/RBSN tensile specimens

NASA Technical Reports Server (NTRS)

Baaklini, George Y.; Bhatt, Ramakrishna T.

1991-01-01

The room-temperature tensile testing of silicon carbide fiber reinforced reaction-bonded silicon nitride (SiC/RBSN) composite specimens was monitored by using in-situ x ray film radiography. Radiographic evaluation before, during, and after loading provided data on the effect of preexisting volume flaws (high density impurities, and local density variations) on the fracture behavior of composites. Results from (0)1, (0)3, (0)5, and (0)8 composite specimens, showed that x ray film radiography can monitor damage accumulations during tensile loading. Matrix cracking, fiber-matrix debonding, and fiber pullout were imaged throughout the tensile loading history of the specimens. Further, in-situ film radiography was found to be a helpful and practical technique for estimating interfacial shear strength between the SiC fiber and the RBSN matrix by the matrix crack spacing method. It is concluded that pretest, in-situ, and post-test radiography can provide for a greater understanding of ceramic matrix composite mechanical behavior, a verification of related experimental procedures, and a validation and development of related analytical models.

Fracture behaviour of the 14Cr ODS steel exposed to helium and liquid lead

NASA Astrophysics Data System (ADS)

Hojna, Anna; Di Gabriele, Fosca; Hadraba, Hynek; Husak, Roman; Kubena, Ivo; Rozumova, Lucia; Bublikova, Petra; Kalivodova, Jana; Matejicek, Jiri

2017-07-01

This work describes the fracture behaviour of the 14Cr ODS steel produced by mechanical alloying process, after high temperature exposures. Small specimens were exposed to helium gas in a furnace at 720 °C for 500 h. Another set of specimens was exposed to flowing liquid lead in the COLONRI II loop at 650 °C for 1000 h. All specimens were tested for the impact and tensile behaviour. The impact test results are compared to other sets of specimens in the as received state and after isothermal annealing at 650 °C for 1000 h. The impact curves of the exposed materials showed positive shifts on the transition temperature. While the upper shelf value did not change in the Pb exposed ODS steel, it significantly increased in the He exposed one. The differences are discussed in terms of surface and subsurface microscopy observation. The embrittlement can be explained as the effect of a slight change in the grain boundary and size distribution combined with the depletion of sub-surface region from alloying elements forming oxide scale on the surface.

Fatigue life prediction of bonded primary joints

NASA Technical Reports Server (NTRS)

Knauss, J. F.

1979-01-01

The validation of a proposed fatigue life prediction methodology was sought through the use of aluminum butt and scarf joint and graphite/epoxy butt joint specimens in a constant amplitude fatigue environment. The structural properties of the HYSOL 9313 adhesive system were obtained by mechanical test of molded heat adhesive specimens. Aluminum contoured double cantilever beam specimens were used to generate crack velocity versus stress intensity factor data. The specific objectives were: (1) to ascertain the feasibility of predicting fatigue failure of an adhesive in a primary bonded composite structure by incorporating linear elastic crack growth behavior; and (2) to ascertain if acoustic emission and/or compliance measurement techniques can be used to detect flaws.

Development and Testing of a Single Frequency Terahertz Imaging System for Breast Cancer Detection

PubMed Central

St. Peter, Benjamin; Yngvesson, Sigfrid; Siqueira, Paul; Kelly, Patrick; Khan, Ashraf; Glick, Stephen; Karellas, Andrew

2013-01-01

The ability to discern malignant from benign tissue in excised human breast specimens in Breast Conservation Surgery (BCS) was evaluated using single frequency terahertz radiation. Terahertz (THz) images of the specimens in reflection mode were obtained by employing a gas laser source and mechanical scanning. The images were correlated with optical histological micrographs of the same specimens, and a mean discrimination of 73% was found for five out of six samples using Receiver Operating Characteristic (ROC) analysis. The system design and characterization is discussed in detail. The initial results are encouraging but further development of the technology and clinical evaluation is needed to evaluate its feasibility in the clinical environment. PMID:25055306

Structure and mechanical properties of parts obtained by selective laser melting of metal powder based on intermetallic compounds Ni3Al

NASA Astrophysics Data System (ADS)

Smelov, V. G.; Sotov, A. V.; Agapovichev, A. V.; Nosova, E. A.

2018-03-01

The structure and mechanical properties of samples are obtained from metal powder based on intermetallic compound by selective laser melting. The chemical analysis of the raw material and static tensile test of specimens were made. Change in the samples’ structure and mechanical properties after homogenization during four and twenty-four hours were investigated. A small-sized combustion chamber of a gas turbine engine was performed by the selective laser melting method. The print combustion chamber was subjected to the gas-dynamic test in a certain temperature and time range.

Tactual discrimination of softness.

PubMed

Srinivasan, M A; LaMotte, R H

1995-01-01

1. We investigated the ability of humans to tactually discriminate the softness of objects, using novel elastic objects with deformable and rigid surfaces. For objects with deformable surfaces, we cast transparent rubber specimens with variable compliances. For objects with rigid surfaces ("spring cells") we fabricated telescoping hollow cylinders with the inner cylinder supported by several springs. To measure the human discriminability and to isolate the associated information-processing mechanisms, we performed psychophysical experiments under three conditions: 1) active touch with the normal finger, where both tactile and kinesthetic information was available to the subject: 2) active touch with local cutaneous anesthesia, so that only kinesthetic information was available; and 3) passive touch, where a computer-controlled mechanical stimulator brought down the compliant specimens onto the passive fingerpad of the subject, who therefore had only tactile information. 2. We first characterized the mechanical behavior of the human fingerpad and the test objects by determining the relationship between the depth and force of indentation during constant-velocity indentations by a rigid probe. The fingerpad exhibited a pronounced nonlinear behavior in the indentation depth versus force trace such that compliance, as indicated by the local slope of the trace, decreased with increases in indentation depth. The traces for all the rubber specimens were approximately linear, indicating a constant but distinct value of compliance for each specimen. The fingerpad was more compliant than each of the rubber specimens. 3. All the human subjects showed excellent softness discriminability in ranking the rubber specimens by active touch, and the subjective perception of softness correlated one-to-one with the objectively measured compliance. The ability of subjects to discriminate the compliance of spring cells was consistently poorer compared with that of the rubber specimens. 4. For pairwise discrimination of a selected set of rubber specimens, kinesthetic information alone was insufficient. However, tactile information alone was sufficient, even when the velocities and forces of specimen application were randomized. In contrast, for discriminating pairs of spring cells, tactile information alone was insufficient, and both tactile and kinesthetic information were found to be necessary. 5. The differences in the sufficiency of tactile information for the discrimination of the two types of objects can be explained by the mechanics of contact of the fingerpad and its effect on tactile information. For objects with deformable surfaces, the spatial pressure distribution within the contact region depends on both the force applied and the specimen compliance.(ABSTRACT TRUNCATED AT 250 WORDS)

Study of Effects on Mechanical Properties of PLA Filament which is blended with Recycled PLA Materials

NASA Astrophysics Data System (ADS)

Babagowda; Kadadevara Math, R. S.; Goutham, R.; Srinivas Prasad, K. R.

2018-02-01

Fused deposition modeling is a rapidly growing additive manufacturing technology due to its ability to build functional parts having complex geometry. The mechanical properties of the build part is depends on several process parameters and build material of the printed specimen. The aim of this study is to characterize and optimize the parameters such as layer thickness and PLA build material which is mixed with recycled PLA material. Tensile and flexural or bending test are carried out to determine the mechanical response characteristics of the printed specimen. Taguchi method is used for number of experiments and Taguchi S/N ratio is used to identify the set of parameters which give good results for respective response characteristics, effectiveness of each parameters is investigated by using analysis of variance (ANOVA).

Method of fission heat flux determination from experimental data

DOEpatents

Paxton, Frank A.

1999-01-01

A method is provided for determining the fission heat flux of a prime specimen inserted into a specimen of a test reactor. A pair of thermocouple test specimens are positioned at the same level in the holder and a determination is made of various experimental data including the temperature of the thermocouple test specimens, the temperature of bulk water channels located in the test holder, the gamma scan count ratios for the thermocouple test specimens and the prime specimen, and the thicknesses of the outer clads, the fuel fillers, and the backclad of the thermocouple test specimen. Using this experimental data, the absolute value of the fission heat flux for the thermocouple test specimens and prime specimen can be calculated.

Changed morphology and mechanical properties of cancellous bone in the mandibular condyles of edentate people.

PubMed

Giesen, E B W; Ding, M; Dalstra, M; van Eijden, T M G J

2004-03-01

Since edentate subjects have a reduced masticatory function, it can be expected that the morphology of the cancellous bone of their mandibular condyles has changed according to the altered mechanical environment. In the present study, the morphology of cylindrical cancellous bone specimens of the mandibular condyles of edentate subjects (n = 25) was compared with that of dentate subjects (n = 24) by means of micro-computed tomography and by the application of Archimedes' principle. Stiffness and strength were determined by destructive mechanical testing. Compared with dentate subjects, it appeared that, in edentate subjects, the bone was less dense and the trabecular structure was less plate-like. The regression models of stiffness and strength built from bone volume fraction and the trabecular orientation relative to the axis of the specimen were similar for both dentate and edentate subjects. This indicates that, under reduced mechanical load, the fundamental relationship between bone morphology and mechanical properties does not change.

Effects of silicon additions on oxidation and mechanical behavior of the nickel-base superalloy B-1900

NASA Technical Reports Server (NTRS)

Miner, R. V., Jr.; Lowell, C. E.

1975-01-01

Test specimens with nominal additions of Si were tested in oxidation, thermal fatigue, sulfidation, tension, and stress rupture, and were also extensively studied metallographically. Alloy B-1900 modified with 0.6- or 1.2-wt% Si exhibited oxidation resistance equivalent to that of aluminide-coated B-1900 during cyclic, high-gas-velocity oxidation tests. Resistances to thermal fatigue and sulfidation were improved by the Si additions, but were not superior to aluminide-coated B-1900. Stress-rupture tests at 1000 C of specimens given the standard heat treatment to simulate an aluminide coating cycle showed Si to be detrimental. However, application of another heat treatment increased the rupture life of the alloy with 0.6-wt% Si to that of the unmodified B-1900 given the standard heat treatment.

Studies of biaxial mechanical properties and nonlinear finite element modeling of skin.

PubMed

Shang, Xituan; Yen, Michael R T; Gaber, M Waleed

2010-06-01

The objective of this research is to conduct mechanical property studies of skin from two individual but potentially connected aspects. One is to determine the mechanical properties of the skin experimentally by biaxial tests, and the other is to use the finite element method to model the skin properties. Dynamic biaxial tests were performed on 16 pieces of abdominal skin specimen from rats. Typical biaxial stress-strain responses show that skin possesses anisotropy, nonlinearity and hysteresis. To describe the stress-strain relationship in forms of strain energy function, the material constants of each specimen were obtained and the results show a high correlation between theory and experiments. Based on the experimental results, a finite element model of skin was built to model the skin's special properties including anisotropy and nonlinearity. This model was based on Arruda and Boyce's eight-chain model and Bischoff et al.'s finite element model of skin. The simulation results show that the isotropic, nonlinear eight-chain model could predict the skin's anisotropic and nonlinear responses to biaxial loading by the presence of an anisotropic prestress state.

UHPC for Blast and Ballistic Protection, Explosion Testing and Composition Optimization

NASA Astrophysics Data System (ADS)

Bibora, P.; Drdlová, M.; Prachař, V.; Sviták, O.

2017-10-01

The realization of high performance concrete resistant to detonation is the aim and expected outcome of the presented project, which is oriented to development of construction materials for larger objects as protective walls and bunkers. Use of high-strength concrete (HSC / HPC - “high strength / performance concrete”) and high-fiber reinforced concrete (UHPC / UHPFC -“Ultra High Performance Fiber Reinforced Concrete”) seems to be optimal for this purpose of research. The paper describes the research phase of the project, in which we focused on the selection of specific raw materials and chemical additives, including determining the most suitable type and amount of distributed fiber reinforcement. Composition of UHPC was optimized during laboratory manufacture of test specimens to obtain the best desired physical- mechanical properties of developed high performance concretes. In connection with laboratory testing, explosion field tests of UHPC specimens were performed and explosion resistance of laboratory produced UHPC testing boards was investigated.

Experimental study on lateral strength of wall-slab joint subjected to lateral cyclic load

NASA Astrophysics Data System (ADS)

Masrom, Mohd Asha'ari; Mohamad, Mohd Elfie; Hamid, Nor Hayati Abdul; Yusuff, Amer

2017-10-01

Tunnel form building has been utilised in building construction since 1960 in Malaysia. This method of construction has been applied extensively in the construction of high rise residential house (multistory building) such as condominium and apartment. Most of the tunnel form buildings have been designed according to British standard (BS) whereby there is no provision for seismic loading. The high-rise tunnel form buildings are vulnerable to seismic loading. The connections between slab and shear walls in the tunnel-form building constitute an essential link in the lateral load resisting mechanism. Malaysia is undergoing a shifting process from BS code to Eurocode (EC) for building construction since the country has realised the safety threats of earthquake. Hence, this study is intended to compare the performance of the interior wall slab joint for a tunnel form structure designed based on Euro and British codes. The experiment included a full scale test of the wall slab joint sub-assemblages under reversible lateral cyclic loading. Two sub-assemblage specimens of the wall slab joint were designed and constructed based on both codes. Each specimen was tested using lateral displacement control (drift control). The specimen designed by using Eurocode was found could survive up to 3.0% drift while BS specimen could last to 1.5% drift. The analysis results indicated that the BS specimen was governed by brittle failure modes with Ductility Class Low (DCL) while the EC specimen behaved in a ductile manner with Ductility Class Medium (DCM). The low ductility recorded in BS specimen was resulted from insufficient reinforcement provided in the BS code specimen. Consequently, the BS specimen could not absorb energy efficiently (low energy dissipation) and further sustain under inelastic deformation.

Evaluation of Flexural Strength of Polymethyl Methacrylate modified with Silver Colloidal Nanoparticles subjected to Two Different Curing Cycles: An in vitro Study.

PubMed

Munikamaiah, Ranganath L; Jain, Saket K; Pal, Kapil S; Gaikwad, Ajay

2018-03-01

Silver colloidal nanoparticles have been incorporated into acrylic resins to induce antimicrobial properties. However, as additives, they can influence the mechanical properties of the final product. Mechanical properties are also dependent on different curing cycles. The aim of this study was to evaluate flexural strength of a denture base resin incorporated with different concentrations of silver colloidal nanoparticles subjected to two different curing cycles. Lucitone 199 denture base resin was used into which silver colloidal nanoparticles were incorporated at 0.5 and 5% by polymer mass. Specimens devoid of nanoparticles were used as controls. A total of 60 specimens were fabricated and divided into two groups. Each group was divided into three subgroups consisting of 10 specimens each. The specimens were fabricated according to American Dental Association (ADA) specification No. 12 and tested for flexural strength using universal testing machine. Silver colloidal nanoparticle incorporation at 0.5% concentration increased the mean flexural strength in both curing cycles by 7.5 and 4.4%, respectively, when compared with the control group. The study suggested that the mean flexural strength value of 0.5% silver colloidal nanoparticles in denture base resin was above the value of the control group both in short and long curing cycles, which makes it clinically suitable as a denture base material. However, at 5% concentration, the statistically significant amount of decrease in flexural strength compared with the value of control group both in short and long curing cycles gives it a questionable prognosis. The specimens incorporated with the antimicrobial agent 0.5% silver colloidal nanoparticles and processed by long curing cycles showed significant increase in its flexural strength compared with the control group, which makes it clinically suitable as a denture base material.

Fracture Toughness Determination of Cracked Chevron Notched Brazilian Disc Rock Specimen via Griffith Energy Criterion Incorporating Realistic Fracture Profiles

NASA Astrophysics Data System (ADS)

Xu, Yuan; Dai, Feng; Zhao, Tao; Xu, Nu-wen; Liu, Yi

2016-08-01

The cracked chevron notched Brazilian disc (CCNBD) specimen has been suggested by the International Society for Rock Mechanics to measure the mode I fracture toughness of rocks, and has been widely adopted in laboratory tests. Nevertheless, a certain discrepancy has been observed in results when compared with those derived from methods using straight through cracked specimens, which might be due to the fact that the fracture profiles of rock specimens cannot match the straight through crack front as assumed in the measuring principle. In this study, the progressive fracturing of the CCNBD specimen is numerically investigated using the discrete element method (DEM), aiming to evaluate the impact of the realistic cracking profiles on the mode I fracture toughness measurements. The obtained results validate the curved fracture fronts throughout the fracture process, as reported in the literature. The fracture toughness is subsequently determined via the proposed G-method originated from Griffith's energy theory, in which the evolution of the realistic fracture profile as well as the accumulated fracture energy is quantified by DEM simulation. A comparison between the numerical tests and the experimental results derived from both the CCNBD and the semi-circular bend (SCB) specimens verifies that the G-method incorporating realistic fracture profiles can contribute to narrowing down the gap between the fracture toughness values measured via the CCNBD and the SCB method.

Intact Imaging of Human Heart Structure Using X-ray Phase-Contrast Tomography.

PubMed

Kaneko, Yukihiro; Shinohara, Gen; Hoshino, Masato; Morishita, Hiroyuki; Morita, Kiyozo; Oshima, Yoshihiro; Takahashi, Masashi; Yagi, Naoto; Okita, Yutaka; Tsukube, Takuro

2017-02-01

Structural examination of human heart specimens at the microscopic level is a prerequisite for understanding congenital heart diseases. It is desirable not to destroy or alter the properties of such specimens because of their scarcity. However, many of the currently available imaging techniques either destroy the specimen through sectioning or alter the chemical and mechanical properties of the specimen through staining and contrast agent injection. As a result, subsequent studies may not be possible. X-ray phase-contrast tomography is an imaging modality for biological soft tissues that does not destroy or alter the properties of the specimen. The feasibility of X-ray phase-contrast tomography for the structural examination of heart specimens was tested using infantile and fetal heart specimens without congenital diseases. X-ray phase-contrast tomography was carried out at the SPring-8 synchrotron radiation facility using the Talbot grating interferometer at the bending magnet beamline BL20B2 to visualize the structure of five non-pretreated whole heart specimens obtained by autopsy. High-resolution, three-dimensional images were obtained for all specimens. The images clearly showed the myocardial structure, coronary vessels, and conduction bundle. X-ray phase-contrast tomography allows high-resolution, three-dimensional imaging of human heart specimens. Intact imaging using X-ray phase-contrast tomography can contribute to further structural investigation of heart specimens with congenital heart diseases.

Mechanical properties of thin films of laser-welded titanium and their associated welding defects.

PubMed

Wu, Yulu; Xin, Haitao; Zhang, Chunbao; Tang, Zhongbin; Zhang, Zhiyuan; Wang, Weifeng

2014-11-01

The aim of this study was to evaluate the mechanical properties of thin films of laser-welded cast titanium using an interference strain/displacement gauge (ISDG) and to analyze factors that affect laser welding. Dog-bone-shaped small specimens of cast titanium were prepared by wire cutting after they were laser-welded. The specimens were divided into three groups according to the gap distance of the laser weld; the control was non-welded titanium. Small specimens without cast defects detected by X-ray screening were measured by a tensile test machine using ISDG, and stress-strain curves were drawn. Finally, the fracture texture was analyzed. The ultimate tensile strengths (UTSs) of specimens with a gap distance of 0.00, 0.25, and 0.50 mm were 492.16 ± 33.19, 488.09 ± 43.18, and 558.45 ± 10.80 MPa, respectively. There were no significant differences in UTS between the test groups and the control group (p > 0.05). However, the plastic deformation and the percent elongation increased as the gap distance increased. Incomplete penetration defects appeared in groups that had small gap distances, which may have affected the properties of the laser-welded titanium. However, the welding material was still pure titanium. These results suggest that an appropriate gap distance should be maintained to improve the application of dental laser welding.

Hydromechanics in dentine: role of dentinal tubules and hydrostatic pressure on mechanical stress-strain distribution.

PubMed

Kishen, A; Vedantam, S

2007-10-01

This investigation is to understand the role of free water in the dentinal tubules on the mechanical integrity of bulk dentine. Three different experiments were conducted in this study. In experiment 1, three-dimensional models of dentine with gradient elastic modulus, homogenous elastic modulus, and with and without hydrostatic pressure were simulated using the finite element method. Static compressive loads of 15, 50 and 100 N were applied and the distribution of the principal stresses, von Mises stresses, and strains in loading direction were determined. In experiment 2, experimental compression testing of fully hydrated and partially dehydrated dentine (21 degrees C for 72 h) was conducted using a Universal testing machine. In experiment 3, Fourier transform infrared spectroscopic analysis of hydrated and partially dehydrated dentine was carried out. The finite element analysis revealed that the dentine model with simulated hydrostatic pressure displayed residual tensile stresses and strains in the inner region adjacent to the root canal. When external compressive loads were applied to the model, the residual stresses and strains counteracted the applied loads. Similarly the hydrated specimens subjected to experimental compression loads showed greater toughness when compared to the partially dehydrated specimens. The stress at fracture was significantly higher in partially dehydrated specimens (p=0.014), while the strain at fracture was significantly higher in hydrated dentine specimens (p=0.037). These experiments highlighted the distinct role of free water in the dentinal tubules and hydrostatic pressure on the stress-strain distribution within the bulk dentine.

Design, fabrication, and implementation of thermally driven outdoor testing devices for building joint sealants.

PubMed

White, C C; Tan, K T; O'Brien, E P; Hunston, D L; Chin, J W; Williams, R S

2011-02-01

The paper describes the development, implementation, and testing of two thermally driven outdoor exposure instruments. These devices are unique in their ability to impose field generated thermally induced strain on sealant specimens while monitoring their resulting load and displacement. The instruments combine a fixed wood and steel supporting frame with a moving polyvinyl chloride frame, and employ differences in the coefficients of thermal expansion between the supporting frame and moving frame to induce strain on the sealant specimens. Two different kinds of instruments have been fabricated, "winter/tension" and "winter/compression" designs. In the winter/tension design, the thermally induced dimensional change is directly transferred to the specimens; while in the winter/compression design, the samples are loaded in an opposite direction with the dimensional change. Both designs are instrumented to monitor load and displacement and are built so that the strain on the specimen does not exceed ±25% over the range of temperatures expected in Gaithersburg, MD. Additionally, a weather station is colocated with the device to record environmental conditions in 1 min intervals. This combination of weather information with mechanical property data enables a direct link between environmental conditions and the corresponding sealant response. The reliability and effectiveness of these instruments are demonstrated with a typical sealant material. The results show that the instruments work according to the design criteria and provide a meaningful quantitative platform to monitor the mechanical response of sealant exposed to outdoor weathering.

The Influence of Phase Change Materials on the Properties of Self-Compacting Concrete.

PubMed

Fenollera, María; Míguez, José Luis; Goicoechea, Itziar; Lorenzo, Jaime; Ángel Álvarez, Miguel

2013-08-15

The aim of this paper is to research new thermally-efficient concrete walls, analyzing the mechanical behavior of a self-compacting concrete to manufacture an uncoated solid structural panel, with the incorporation of a micro-encapsulated phase change material as additive. Different dosages are tested and mechanical properties of the product obtained from the molding of concrete specimens are evaluated, testing mechanical compressive strength, slump flow, and density. The results reveal the optimum percentage of additive in the mixture that enables compliance with the technical specifications required by the product to be manufactured. A test is also performed for measuring the thermal conductivity for the optimal sample obtained and it evidences the reduction thereof.

Measurement of fracture toughness of metallic materials produced by additive manufacturing

NASA Astrophysics Data System (ADS)

Quénard, O.; Dorival, O.; Guy, Ph.; Votié, A.; Brethome, K.

2018-04-01

This study focuses on the microstructure and mechanical properties of metallic materials produced by additive layer manufacturing (ALM), especially the laser beam melting process. The influence of the specimen orientation during the ALM process and that of two post-build thermal treatments were investigated. The identified metal powder is Ti-6Al-4V (titanium base). Metallographic analysis shows their effects on the microstructure of the metals. Mechanical experiments involving tensile tests as well as toughness tests were performed according to ASTM (American Society for Testing and Materials) norms. The results show that the main influence is that of the thermal treatments; however the manufacturing stacking direction may lead to some anisotropy in the mechanical properties.