Method for synthesizing metal bis(borano) hypophosphite complexes

DOEpatents

Cordaro, Joseph G.

2013-06-18

The present invention describes the synthesis of a family of metal bis(borano) hypophosphite complexes. One procedure described in detail is the syntheses of complexes beginning from phosphorus trichloride and sodium borohydride. Temperature, solvent, concentration, and atmosphere are all critical to ensure product formation. In the case of sodium bis(borano) hypophosphite, hydrogen gas was evolved upon heating at temperatures above 150.degree. C. Included in this family of materials are the salts of the alkali metals Li, Na and K, and those of the alkaline earth metals Mg and Ca. Hydrogen storage materials are possible. In particular the lithium salt, Li[PH.sub.2(BH.sub.3).sub.2], theoretically would contain nearly 12 wt % hydrogen. Analytical data for product characterization and thermal properties are given.

Growth of Ionic Selectivity Prussian Blue Modified Celgard Separator for High Performance Lithium Sulfur Battery.

PubMed

Wu, Xian; Fan, Lishuang; Qiu, Yue; Wang, Maoxu; Cheng, Junhan; Guan, Bin; Guo, Zhikun; Zhang, Naiqing; Sun, Kening

2018-06-26

Lithium sulfur batteries have been restricted on their major technical problem of shuttling soluble polysulfides between electrodes, resulting in serious capacity fading. For purpose of develop a high-performance lithium-sulfur battery, we first time utilize a simple growth method to introduce a Prussian blue modified Celgard separator as an ion selective membrane in lithium sulfur batteries. The unique structure of Prussian blue could effectively suppress the shuttle of polysulfides but scarcely affect the transfer ability of lithium ions, which is beneficial to achieve high sulfur conversion efficiency and capacity retention. The lithium sulfur battery with Prussian blue modified Celgard separator reveals an average capacity decaying of only 0.03% per cycle at 1C after 1000 cycles. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Seventh Topical Report on The Reactions of Borohydrides and Aluminohydrides with Wolfram (VI) Halides and Eighth Topical Report on Preparation and Properties of Thorium Borohydride

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bragdon, Robert W.

1950-11-08

(1) A comprehensive investigation of methods for the preparation of hydrides of wolfram has been made. A wolfram (IV) hydride-aluminum hydride mixture has been prepared and its N{sub H} and thermal stability determined for its evaluation as a nuclear radiation shield material. Aluminum borohydride has been shown to reduce wolfram (VI) chloride to a subchloride. The alkali borohydrides also reduce hexavalent wolfram, but in no case has a wolfram borohydride been isolated. (2) An investigation of the chemical and physical properties of thorium borohydride, which pertain to its use as alow-temperature nuclear radiatin shield, is presented. Values are taken frommore » the literature when available and are supplemented where necessary by our experimental investigation.« less

A composite of borohydride and super absorbent polymer for hydrogen generation

NASA Astrophysics Data System (ADS)

Li, Z. P.; Liu, B. H.; Liu, F. F.; Xu, D.

To develop a hydrogen source for underwater applications, a composite of sodium borohydride and super absorbent polymer (SAP) is prepared by ball milling sodium borohydride powder with SAP powder, and by dehydrating an alkaline borohydride gel. When sodium polyacrylate (NaPAA) is used as the SAP, the resulting composite exhibits a high rate of borohydride hydrolysis for hydrogen generation. A mechanism of hydrogen evolution from the NaBH 4-NaPAA composite is suggested based on structure analysis by X-ray diffraction and scanning electron microscopy. The effects of water and NiCl 2 content in the precursor solution on the hydrogen evolution behavior are investigated and discussed.

Nanoconfinement in activated mesoporous carbon of calcium borohydride for improved reversible hydrogen storage.

PubMed

Comănescu, Cezar; Capurso, Giovanni; Maddalena, Amedeo

2012-09-28

Mesoporous carbon frameworks were synthesized using the soft-template method. Ca(BH(4))(2) was incorporated into activated mesoporous carbon by the incipient wetness method. The activation of mesoporous carbon was necessary to optimize the surface area and pore size. Thermal programmed absorption measurements showed that the confinement of this borohydride into carbon nanoscaffolds improved its reversible capacity (relative to the reactive portion) and performance of hydrogen storage compared to unsupported borohydride. Hydrogen release from the supported hydride started at a temperature as low as 100 °C and the dehydrogenation rate was fast compared to the bulk borohydride. In addition, the hydrogen pressure necessary to regenerate the borohydride from the dehydrogenation products was reduced.

On the purity assessment of solid sodium borohydride

NASA Astrophysics Data System (ADS)

Botasini, Santiago; Méndez, Eduardo

2012-01-01

Since sodium borohydride has become extensively used as chemical hydrogen storage material in fuel cells, many techniques have been proposed to assess the purity of this substance. However, all of them are developed in aqueous media, where the reagent is unstable. In addition, its hygroscopic nature was difficults in any attempt to make precise quantifications. The present work compares three different methods, namely, voltammetric, titrimetric, and Fourier transformed infrared spectroscopy (FTIR) in order to assess the purity of sodium borohydride, using an expired and a new sodium borohydride samples as references. Our results show that only the FTIR measurements provide a simple and semi-quantitative means to assess the purity of sodium borohydride due to the fact that it is the only one that measures the sample in the solid state. A comparison between the experimental data and theoretical calculation reveals the identification of the absorption bands at 1437 cm-1 of sodium metaborate and 2291 cm-1 of sodium borohydride which represent a good fingerprint for the qualitative assessment of the sample quality.

Enhanced activity of Au-Fe/C anodic electrocatalyst for direct borohydride-hydrogen peroxide fuel cell

NASA Astrophysics Data System (ADS)

Yi, Lanhua; Wei, Wei; Zhao, Caixian; Tian, Li; Liu, Jing; Wang, Xianyou

2015-07-01

Carbon supported Au-Fe bimetallic nanocatalysts (Au-Fe/C) are facilely prepared via a modified NaBH4 reduction method in aqueous solution at room temperature, and used as the anode electrocatalyst of direct borohydride-hydrogen peroxide fuel cell (DBHFC). The physical and electrochemical properties of the Au-Fe/C electrocatalysts are characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD), cyclic voltammetry (CV), rotating disc electrode (RDE) voltammetry, chronoamperometry (CA), chronopotentiometry (CP), and fuel cell test. The results show that Au-Fe/C catalysts display higher catalytic activity for the direct electrooxidation of BH4- than carbon supported pure Au nanocatalyst (Au/C), especially Au50Fe50/C catalyst presents the highest catalytic activity among all as-prepared catalysts. Besides, the single DBHFC with Au50Fe50/C anode and Au/C cathode obtains the maximum power density as high as 34.9 mW cm-2 at 25 °C.

The crystal chemistry of inorganic metal borohydrides and their relation to metal oxides.

PubMed

Černý, Radovan; Schouwink, Pascal

2015-12-01

The crystal structures of inorganic homoleptic metal borohydrides are analysed with respect to their structural prototypes found amongst metal oxides in the inorganic databases such as Pearson's Crystal Data [Villars & Cenzual (2015). Pearson's Crystal Data. Crystal Structure Database for Inorganic Compounds, Release 2014/2015, ASM International, Materials Park, Ohio, USA]. The coordination polyhedra around the cations and the borohydride anion are determined, and constitute the basis of the structural systematics underlying metal borohydride chemistry in various frameworks and variants of ionic packing, including complex anions and the packing of neutral molecules in the crystal. Underlying nets are determined by topology analysis using the program TOPOS [Blatov (2006). IUCr CompComm. Newsl. 7, 4-38]. It is found that the Pauling rules for ionic crystals apply to all non-molecular borohydride crystal structures, and that the latter can often be derived by simple deformation of the close-packed anionic lattices c.c.p. and h.c.p., by partially removing anions and filling tetrahedral or octahedral sites. The deviation from an ideal close packing is facilitated in metal borohydrides with respect to the oxide due to geometrical and electronic considerations of the BH4(-) anion (tetrahedral shape, polarizability). This review on crystal chemistry of borohydrides and their similarity to oxides is a contribution which should serve materials engineers as a roadmap to design new materials, synthetic chemists in their search for promising compounds to be prepared, and materials scientists in understanding the properties of novel materials.

Boron-Based Hydrogen Storage: Ternary Borides and Beyond

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vajo, John J.

DOE continues to seek reversible solid-state hydrogen materials with hydrogen densities of ≥11 wt% and ≥80 g/L that can deliver hydrogen and be recharged at moderate temperatures (≤100 °C) and pressures (≤100 bar) enabling incorporation into hydrogen storage systems suitable for transportation applications. Boron-based hydrogen storage materials have the potential to meet the density requirements given boron’s low atomic weight, high chemical valance, and versatile chemistry. However, the rates of hydrogen exchange in boron-based compounds are thus far much too slow for practical applications. Although contributing to the high hydrogen densities, the high valance of boron also leads to slowmore » rates of hydrogen exchange due to extensive boron-boron atom rearrangements during hydrogen cycling. This rearrangement often leads to multiple solid phases occurring over hydrogen release and recharge cycles. These phases must nucleate and react with each other across solid-solid phase boundaries leading to energy barriers that slow the rates of hydrogen exchange. This project sought to overcome the slow rates of hydrogen exchange in boron-based hydrogen storage materials by minimizing the number of solid phases and the boron atom rearrangement over a hydrogen release and recharge cycle. Two novel approaches were explored: 1) developing matched pairs of ternary borides and mixed-metal borohydrides that could exchange hydrogen with only one hydrogenated phase (the mixed-metal borohydride) and only one dehydrogenated phase (the ternary boride); and 2) developing boranes that could release hydrogen by being lithiated using lithium hydride with no boron-boron atom rearrangement.« less

Lithium modified zeolite synthesis for conversion of biodiesel-derived glycerol to polyglycerol

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ayoub, Muhammad, E-mail: muhammad.ayoub@petronas.com.my; Abdullah, Ahmad Zuhairi, E-mail: chzuhairi@usm.my; Inayat, Abrar, E-mail: abrar.inayat@petronas.com.my

Basic zeolite has received significant attention in the catalysis community. These zeolites modified with alkaline are the potential replacement for existing zeolite catalysts due to its unique features with added advantages. The present paper covers the preparation of lithium modified zeolite Y (Li-ZeY) and its activity for solvent free conversion of biodiesel-derived glycerol to polyglycerol via etherification process. The modified zeolite was well characterized by X-ray diffraction (XRD), Scanning Electron Microscope (SEM) and Nitrogen Adsorption. The SEM images showed that there was no change in morphology of modified zeolite structure after lithium modification. XRD patterns showed that the structure ofmore » zeolite was sustained after lithium modification. The surface properties of parent and modified zeolite was also observed N{sub 2} adsortion-desorption technique and found some changes in surface area and pore size. In addition, the basic strength of prepared materials was measured by Hammet indicators and found that basic strength of Li-ZeY was highly improved. This modified zeolite was found highly thermal stable and active heterogamous basic catalyst for conversion of solvent free glycerol to polyglycerol. This reaction was conducted at different temperatures and 260 °C was found most active temperature for this process for reaction time from 6 to 12 h over this basic catalyst in the absence of solvent.« less

Development and Optimization of Targeted Nanoscale Iron Delivery Methods for Treatment of NAPL Source Zones

DTIC Science & Technology

2011-04-01

27 III.1.2.3. Gum Arabic Emulsion ……………………………………………. 29 III.1.2.4. Reactivity Studies GA...GA Gum Arabic HLB Hydrophobic Lipophilic Balance IFT Interfacial Tension MISER Michigan Soil-Vapor Extraction Remediation model mRNIP Modified...trichloroethylene (TCE) (99.9%) were supplied by Fischer Scientific. Sodium borohydride (NaBH4) (98+%) and Gum Arabic were supplied by Acros Organics. Purified water

Synthesis and electrospinning carboxymethyl cellulose lithium (CMC-Li) modified 9,10-anthraquinone (AQ) high-rate lithium-ion battery.

PubMed

Qiu, Lei; Shao, Ziqiang; Liu, Minglong; Wang, Jianquan; Li, Pengfa; Zhao, Ming

2014-02-15

New cellulose derivative CMC-Li was synthesized, and nanometer CMC-Li fiber was applied to lithium-ion battery and coated with AQ by electrospinning. Under the protection of inert gas, modified AQ/carbon nanofibers (CNF)/Li nanometer composite material was obtained by carbonization in 280 °C as lithium battery anode materials for the first time. The morphologies and structures performance of materials were characterized by using IR, (1)H NMR, SEM, CV and EIS, respectively. Specific capacity was increased from 197 to 226.4 mAhg(-1) after modification for the first discharge at the rate of 2C. Irreversible reduction reaction peaks of modified material appeared between 1.5 and 1.7 V and the lowest oxidation reduction peak of the difference were 0.42 V, the polarization was weaker. Performance of cell with CMC-Li with the high degree of substitution (DS) was superior to that with low DS. Cellulose materials were applied to lithium battery to improve battery performance by electrospinning. Copyright © 2013 Elsevier Ltd. All rights reserved.

Process for synthesis of ammonia borane for bulk hydrogen storage

DOEpatents

Autrey, S Thomas [West Richland, WA; Heldebrant, David J [Richland, WA; Linehan, John C [Richland, WA; Karkamkar, Abhijeet J [Richland, WA; Zheng, Feng [Richland, WA

2011-03-01

The present invention discloses new methods for synthesizing ammonia borane (NH.sub.3BH.sub.3, or AB). Ammonium borohydride (NH.sub.4BH.sub.4) is formed from the reaction of borohydride salts and ammonium salts in liquid ammonia. Ammonium borohydride is decomposed in an ether-based solvent that yields AB at a near quantitative yield. The AB product shows promise as a chemical hydrogen storage material for fuel cell powered applications.

Chaotropic salts: novel modifiers for the capillary electrophoretic analysis of benzodiazepines.

PubMed

Su, Hsiu-Li; Lan, Min-Tsu; Lin, Kuan-Wen; Hsieh, You-Zung

2008-08-01

This paper describes a CE method for analyzing benzodiazepines using the chaotropic salts lithium trifluoromethanesulfonate (LiOTf), lithium hexafluorophosphate (LiPF(6)), and lithium bis(trifluoromethanesulfonyl)imide (LiNTf(2)) as modifiers in the running buffer. Although adequate resolution of seven benzodiazepine analytes occurred under the influence of each of the chaotropic anions, the separation efficiency was highest when bis(trifluoromethanesulfonyl)imide (Tf(2)N(-)) was the modifier. We applied affinity CE in conjunction with linear analysis to determine the association constants for the formation of complexes between the Tf(2)N(-) anion and the benzodiazepines. According to the estimated Gibbs free energies, the interactions between this chaotropic anion and the benzodiazepines were either ion-dipole or ion-induced dipole interactions. Adding chaotropic salts as modifiers into CE buffers is a simple and reproducible technique for separating benzodiazepines.

Self-Printing on Graphitic Nanosheets with Metal Borohydride Nanodots for Hydrogen Storage

NASA Astrophysics Data System (ADS)

Li, Yongtao; Ding, Xiaoli; Zhang, Qingan

2016-08-01

Although the synthesis of borohydride nanostructures is sufficiently established for advancement of hydrogen storage, obtaining ultrasmall (sub-10 nm) metal borohydride nanocrystals with excellent dispersibility is extremely challenging because of their high surface energy, exceedingly strong reducibility/hydrophilicity and complicated composition. Here, we demonstrate a mechanical-force-driven self-printing process that enables monodispersed (~6 nm) NaBH4 nanodots to uniformly anchor onto freshly-exfoliated graphitic nanosheets (GNs). Both mechanical-forces and borohydride interaction with GNs stimulate NaBH4 clusters intercalation/absorption into the graphite interlayers acting as a ‘pen’ for writing, which is accomplished by exfoliating GNs with the ‘printed’ borohydrides. These nano-NaBH4@GNs exhibit favorable thermodynamics (decrease in ΔH of ~45%), rapid kinetics (a greater than six-fold increase) and stable de-/re-hydrogenation that retains a high capacity (up to ~5 wt% for NaBH4) compared with those of micro-NaBH4. Our results are helpful in the scalable fabrication of zero-dimensional complex hydrides on two-dimensional supports with enhanced hydrogen storage for potential applications.

Self-Printing on Graphitic Nanosheets with Metal Borohydride Nanodots for Hydrogen Storage

PubMed Central

Li, Yongtao; Ding, Xiaoli; Zhang, Qingan

2016-01-01

Although the synthesis of borohydride nanostructures is sufficiently established for advancement of hydrogen storage, obtaining ultrasmall (sub-10 nm) metal borohydride nanocrystals with excellent dispersibility is extremely challenging because of their high surface energy, exceedingly strong reducibility/hydrophilicity and complicated composition. Here, we demonstrate a mechanical-force-driven self-printing process that enables monodispersed (~6 nm) NaBH4 nanodots to uniformly anchor onto freshly-exfoliated graphitic nanosheets (GNs). Both mechanical-forces and borohydride interaction with GNs stimulate NaBH4 clusters intercalation/absorption into the graphite interlayers acting as a ‘pen’ for writing, which is accomplished by exfoliating GNs with the ‘printed’ borohydrides. These nano-NaBH4@GNs exhibit favorable thermodynamics (decrease in ∆H of ~45%), rapid kinetics (a greater than six-fold increase) and stable de-/re-hydrogenation that retains a high capacity (up to ~5 wt% for NaBH4) compared with those of micro-NaBH4. Our results are helpful in the scalable fabrication of zero-dimensional complex hydrides on two-dimensional supports with enhanced hydrogen storage for potential applications. PMID:27484735

Modified secondary lithium metal batteries with the polyaniline-carbon nanotube composite buffer layer.

PubMed

Zhang, Ding; Yin, Yanli; Liu, Changhong; Fan, Shoushan

2015-01-07

A modified secondary lithium metal battery inserted with a polyaniline-carbon nanotube nanoporous composite buffer layer was fabricated. This unique and simple design of battery has the great potential to decrease the safety risk of the secondary Li metal battery in cycles of recharging processes and improve its cycle life in the future.

Responses of Lithium-Modified Bath to a Shift in Heat Input/Output Balance and Observation of Freeze-Lining Formation During the Heat Balance Shift

NASA Astrophysics Data System (ADS)

Liu, Jingjing; Taylor, Mark; Dorreen, Mark

2018-02-01

In the aluminum electrolysis process, new industrial aluminum/electricity power markets demand a new cell technology to extend the cell heat balance and amperage operating window of smelters by shifting the steady states. The current work investigates the responses of lithium-modified bath system when the input/output balance is shifted in a laboratory analogue to the industrial heat balance shift. Li2CO3 is added to the cryolite-AlF3-CaF2-Al2O3 system as a bath modifier. A freeze deposit is formed on a `cold finger' dipped into the bath and investigated by X-ray diffraction analysis and electron probe X-ray microanalysis. The macro- and micro-structure of the freeze lining varies with the bath superheat (bath temperature minus bath liquidus temperature) and an open crystalline layer with entrapped liquid dominates the freeze thickness. Compared with the cryolite-AlF3-CaF2-Al2O3 bath system, the lithium-modified bath freeze is more sensitive to the heat balance shift. This freeze investigation provides primary information to understand the variation of the side ledge in an industrial cell when the lithium-modified bath system is used.

Electrocatalysis of borohydride oxidation: a review of density functional theory approach combined with experimental validation.

PubMed

Escaño, Mary Clare Sison; Arevalo, Ryan Lacdao; Gyenge, Elod; Kasai, Hideaki

2014-09-03

The electrocatalysis of borohydride oxidation is a complex, up-to-eight-electron transfer process, which is essential for development of efficient direct borohydride fuel cells. Here we review the progress achieved by density functional theory (DFT) calculations in explaining the adsorption of BH4(-) on various catalyst surfaces, with implications for electrocatalyst screening and selection. Wherever possible, we correlate the theoretical predictions with experimental findings, in order to validate the proposed models and to identify potential directions for further advancements.

Electrocatalysis of borohydride oxidation: a review of density functional theory approach combined with experimental validation

NASA Astrophysics Data System (ADS)

Sison Escaño, Mary Clare; Lacdao Arevalo, Ryan; Gyenge, Elod; Kasai, Hideaki

2014-09-01

The electrocatalysis of borohydride oxidation is a complex, up-to-eight-electron transfer process, which is essential for development of efficient direct borohydride fuel cells. Here we review the progress achieved by density functional theory (DFT) calculations in explaining the adsorption of BH4- on various catalyst surfaces, with implications for electrocatalyst screening and selection. Wherever possible, we correlate the theoretical predictions with experimental findings, in order to validate the proposed models and to identify potential directions for further advancements.

A theoretical study of the structure and stability of borohydride on 3d transition metals

NASA Astrophysics Data System (ADS)

Arevalo, Ryan Lacdao; Escaño, Mary Clare Sison; Gyenge, Elod; Kasai, Hideaki

2012-12-01

The adsorption of borohydride on 3d transition metals (Cr, Mn, Fe, Co, Ni and Cu) was studied using first principles calculations within spin-polarized density functional theory. Magnetic effect on the stability of borohydride is noted. Molecular adsorption is favorable on Co, Ni and Cu, which is characterized by the strong s-dzz hybridization of the adsorbate-substrate states. Dissociated adsorption structure yielding one or two H adatom fragments on the surface is observed for Cr, Mn and Fe.

Modified Ion-Conducting Ceramics Based on Lanthanum Gallate: Synthesis, Structure, and Properties

NASA Astrophysics Data System (ADS)

Kaleva, G. M.; Politova, E. D.; Mosunov, A. V.; Sadovskaya, N. V.

2018-06-01

A review is presented of the synthesis and complex investigation of modified ion-conducting ceramics based on heterosubstituted lanthanum gallate as a promising electrolyte material for solid oxide fuel cells. The effect the composition of multicomponent complex oxides has on the structure, microstructure, and electrophysical properties of ceramics is examined. Samples of ceramics with new compositions are produced via solid-state synthesis and modified with lithium fluoride. A drop is observed in the sintering temperature of the ceramics, caused by the liquid phase mechanism of sintering as a result of the low-melting superstoichiometric quantities of the additive. The effect lithium fluoride has on the process of phase formation, microstructure, and conductivity of the ceramics is investigated. It is found that samples modified with lithium fluoride display high density, dense grain packing, and high values of electrical conductivity at high temperatures.

Functional interface of polymer modified graphite anode

NASA Astrophysics Data System (ADS)

Komaba, S.; Ozeki, T.; Okushi, K.

Graphite electrodes were modified by polyacrylic acid (PAA), polymethacrylic acid (PMA), and polyvinyl alcohol (PVA). Their electrochemical properties were examined in 1 mol dm -3 LiClO 4 ethylene carbonate:dimethyl carbonate (EC:DMC) and propylene carbonate (PC) solutions as an anode of lithium ion batteries. Generally, lithium ions hardly intercalate into graphite in the PC electrolyte due to a decomposition of the PC electrolyte at ca. 0.8 V vs. Li/Li +, and it results in the exfoliation of the graphene layers. However, the modified graphite electrodes with PAA, PMA, and PVA demonstrated the stable charge-discharge performance due to the reversible lithium intercalation not only in the EC:DMC but also in the PC electrolytes since the electrolyte decomposition and co-intercalation of solvent were successfully suppressed by the polymer modification. It is thought that these improvements were attributed to the interfacial function of the polymer layer on the graphite which interacted with the solvated lithium ions at the electrode interface.

Ex Vivo Oxidation in Tissue and Plasma Assays of Hydroxyoctadecadienoates: (Z,E/E,E)-Stereoisomer Ratios

PubMed Central

Liu, Wei; Yin, Huiyong; Akazawa, Yoko Ogawa; Yoshida, Yasukazu; Niki, Etsuo; Porter, Ned A.

2010-01-01

The primary products from peroxidation of linoleate in biological tissues and fluids are the hydroperoxy octadecadienoates and the products normally assayed, after reduction of the hydroperoxides, are the corresponding hydroxy octadecadienoates (HODEs). The HODEs are found in tissues and fluids as a mixture of Z,E and E,E stereoisomers. Two regioisomeric sets of Z,E and E,E stereoisomers are normally observed with substitution at the 9 and 13 position of the 18-carbon chain. The Z,E/E,E product ratio has proved to be a useful means for assessing the reducing capacity of the medium undergoing peroxidation. The HODE Z,E/E,E product ratios previously reported for tissues such as liver and brain vary from 0.5 to 2.0 and plasma ratios are somewhat higher, between 2.0 and 3.0. The reported literature protocols for HODE assay in tissues involve homogenization, reduction with sodium borohydride in the presence of BHT, and ester hydrolysis with KOH to give the free HODEs. This is followed by either reverse-phase HPLC of the free acid HODEs or by conversion to TMS derivatives and GC/MS. When sodium borohydride is replaced in the protocol by triphenylphosphine, a gentler reducing agent, HODE Z,E/E,E product ratios are much higher and lower total HODEs levels of are found. It is proposed that inclusion of sodium borohydride in the isolation procedures leads to ex vivo reactions that are avoided if triphenylphosphine is used as the reducing agent. Modified protocols for HODE analyses (Tissue and Plasma Methods #2) are described that should be used for assays of tissues and fluids. PMID:20423158

High performance Aurivillius phase sodium-potassium bismuth titanate lead-free piezoelectric ceramics with lithium and cerium modification

NASA Astrophysics Data System (ADS)

Wang, Chun-Ming; Wang, Jin-Feng

2006-11-01

The piezoelectric properties of the lithium and cerium modified A-site vacancies sodium-potassium bismuth titanate (NKBT) lead-free piezoceramics are investigated. The piezoelectric activity of NKBT ceramics is significantly improved by the modification of lithium and cerium. The Curie temperature TC, piezoelectric coefficient d33, and mechanical quality factor Qm for the NKBT ceramics modified with 0.10mol% (LiCe) are found to be 660°C, 25pC/N, and 3135, respectively. The Curie temperature gradually decreases from 675to650°C with the increase of (LiCe) modification. The dielectric spectroscopy shows that all the samples possess stable piezoelectric properties, demonstrating that the (LiCe) modified NKBT-based ceramics are the promising candidates for high temperature applications.

Improving Ionic Conductivity and Lithium-Ion Transference Number in Lithium-Ion Battery Separators.

PubMed

Zahn, Raphael; Lagadec, Marie Francine; Hess, Michael; Wood, Vanessa

2016-12-07

The microstructure of lithium-ion battery separators plays an important role in separator performance; however, here we show that a geometrical analysis falls short in predicting the lithium-ion transport in the electrolyte-filled pore space. By systematically modifying the surface chemistry of a commercial polyethylene separator while keeping its microstructure unchanged, we demonstrate that surface chemistry, which alters separator-electrolyte interactions, influences ionic conductivity and lithium-ion transference number. Changes in separator surface chemistry, particularly those that increase lithium-ion transference numbers can reduce voltage drops across the separator and improve C-rate capability.

Method of Manufacturing Micro-Disperse Particles of Sodium Borohydride

DOEpatents

Kravitz, Stanley H.; Hecht, Andrew M.; Sylwester. Alan P.; Bell, Nelson S.

2008-09-23

A compact solid source of hydrogen gas, where the gas is generated by contacting water with micro-disperse particles of sodium borohydride in the presence of a catalyst, such as cobalt or ruthenium. The micro-disperse particles can have a substantially uniform diameter of 1-10 microns, and preferably about 3-5 microns. Ruthenium or cobalt catalytic nanoparticles can be incorporated in the micro-disperse particles of sodium borohydride, which allows a rapid and complete reaction to occur without the problems associated with caking and scaling of the surface by the reactant product sodium metaborate. A closed loop water management system can be used to recycle wastewater from a PEM fuel cell to supply water for reacting with the micro-disperse particles of sodium borohydride in a compact hydrogen gas generator. Capillary forces can wick water from a water reservoir into a packed bed of micro-disperse fuel particles, eliminating the need for using an active pump.

Method of generating hydrogen gas from sodium borohydride

DOEpatents

Kravitz, Stanley H.; Hecht, Andrew M.; Sylwester, Alan P.; Bell, Nelson S.

2007-12-11

A compact solid source of hydrogen gas, where the gas is generated by contacting water with micro-disperse particles of sodium borohydride in the presence of a catalyst, such as cobalt or ruthenium. The micro-disperse particles can have a substantially uniform diameter of 1-10 microns, and preferably about 3-5 microns. Ruthenium or cobalt catalytic nanoparticles can be incorporated in the micro-disperse particles of sodium borohydride, which allows a rapid and complete reaction to occur without the problems associated with caking and scaling of the surface by the reactant product sodium metaborate. A closed loop water management system can be used to recycle wastewater from a PEM fuel cell to supply water for reacting with the micro-disperse particles of sodium borohydride in a compact hydrogen gas generator. Capillary forces can wick water from a water reservoir into a packed bed of micro-disperse fuel particles, eliminating the need for using an active pump.

Destabilized and catalyzed borohydride for reversible hydrogen storage

DOEpatents

Mohtadi, Rana F [Northville, MI; Zidan, Ragaiy [Aiken, SC; Gray, Joshua [Aiken, SC; Stowe, Ashley C [Knoxville, TN; Sivasubramanian, Premkumar [Aiken, SC

2012-02-28

A process of forming a hydrogen storage material, including the steps of: providing a borohydride material of the formula: M(BH.sub.4).sub.x where M is an alkali metal or an alkaline earth metal and 1.ltoreq.x.ltoreq.2; providing an alanate material of the formula: M.sub.1(AlH.sub.4).sub.x where M.sub.1 is an alkali metal or an alkaline earth metal and 1.ltoreq.x.ltoreq.2; providing a halide material of the formula: M.sub.2Hal.sub.x where M.sub.2 is an alkali metal, an alkaline earth metal or transition metal and Hal is a halide and 1.ltoreq.x.ltoreq.4; combining the borohydride, alanate and halide materials such that 5 to 50 molar percent from the borohydride material is present forming a reaction product material having a lower hydrogen release temperature than the alanate material.

Synthesis and thermal decomposition behaviors of magnesium borohydride ammoniates with controllable composition as hydrogen storage materials.

PubMed

Yang, Yanjing; Liu, Yongfeng; Li, You; Gao, Mingxia; Pan, Hongge

2013-02-01

An ammonia-redistribution strategy for synthesizing metal borohydride ammoniates with controllable coordination number of NH(3) was proposed, and a series of magnesium borohydride ammoniates were easily synthesized by a mechanochemical reaction between Mg(BH(4))(2) and its hexaammoniate. A strong dependence of the dehydrogenation temperature and purity of the released hydrogen upon heating on the coordination number of NH(3) was elaborated for Mg(BH(4))(2)·xNH(3) owing to the change in the molar ratio of H(δ+) and H(δ-), the charge distribution on H(δ+) and H(δ-), and the strength of the coordinate bond N:→Mg(2+). The monoammoniate of magnesium borohydride (Mg(BH(4))(2)·NH(3)) was obtained for the first time. It can release 6.5% pure hydrogen within 50 minutes at 180 °C. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Chemical modification of electrolytes for lithium batteries

NASA Astrophysics Data System (ADS)

Afanas'ev, Vladimir N.; Grechin, Aleksandr G.

2002-09-01

Modern approaches to modifying chemically electrolytes for lithium batteries are analysed with the aim of optimising the charge-transfer processes in liquid-phase and solid (polymeric) media. The main regularities of transport properties of lithium electrolyte solutions containing complex (encapsulated) ions in aprotic solvents and polymers are discussed. The prospects for the development of electrolytic solvosystems with the chain (ionotropic) mechanism of conduction with respect to lithium ions are outlined. The bibliography includes 126 references.

Electrochemical research in chemical hydrogen storage materials: Sodium borohydride and organotin hydrides

NASA Astrophysics Data System (ADS)

McLafferty, Jason

Chemical storage of hydrogen involves release of hydrogen in a controlled manner from materials in which the hydrogen is covalently bound. Sodium borohydride and aminoborane are two materials given consideration as chemical hydrogen storage materials by the US Department of Energy. A very significant barrier to adoption of these materials as hydrogen carriers is their regeneration from "spent fuel," i.e., the material remaining after discharge of hydrogen. In this thesis, some research directed at regeneration of sodium borohydride and aminoborane is described. For sodium borohydride, electrochemical reduction of boric acid and sodium metaborate (representing spent fuel) in alkaline, aqueous solution has been investigated. Similarly to literature reports (primarily patents), a variety of cathode materials were tried in these experiments. Additionally, approaches directed at overcoming electrostatic repulsion of borate anion from the cathode, not described in the previous literature for electrochemical reduction of spent fuels, have been attempted. A quantitative analytical method for measuring the concentration of sodium borohydride in alkaline aqueous solution has been developed as part of this work and is described herein. Finally, findings from stability tests for sodium borohydride in aqueous solutions of several different compositions are reported. For aminoborane, other research institutes have developed regeneration schemes involving tributyltin hydride. In this thesis, electrochemical reduction experiments attempting to regenerate tributyltin hydride from tributyltin chloride (a representative by-product of the regeneration scheme) are described. These experiments were performed in the non-aqueous solvents acetonitrile and 1,2-dimethoxyethane. A non-aqueous reference electrode for electrolysis experiments in acetonitrile was developed and is described.

Evaluation of zirconium as a permanent chemical modifier using synchrotron radiation and imaging techniques for lithium determination in sediment slurry samples by ET AAS.

PubMed

Flores, Araceli V; Pérez, Carlos A; Arruda, Marco A Z

2004-02-27

In the present paper, lithium was determined in river sediment using slurry sampling and electrothermal atomic absorption spectrometry (ET AAS) after L'vov platform coating with zirconium (as a permanent chemical modifier). The performance of this modifier and its distribution on the L'vov platform after different heating cycles were evaluated using synchrotron radiation X-ray fluorescence (SRXRF) and imaging scanning electron microscopy (SEM) techniques. The analytical conditions for lithium determination in river sediment slurries were also investigated and the best conditions were obtained employing 1300 and 2300 degrees C for pyrolysis and atomization temperatures, respectively. In addition, 100mg of sediment samples were prepared using 4.0moll(-1) HNO(3). The Zr-coating permitted lithium determination with good precision and accuracy after 480 heating cycles using the same platform for slurry samples. The sediment samples were collected from five different points of the Cachoeira river, São Paulo, Brazil. The detection and quantification limits were, respectively, 0.07 and 0.23mugl(-1).

Nano-TiO2 decorated carbon coating on the separator to physically and chemically suppress the shuttle effect for lithium-sulfur battery

NASA Astrophysics Data System (ADS)

Shao, Hongyuan; Wang, Weikun; Zhang, Hao; Wang, Anbang; Chen, Xiaonong; Huang, Yaqin

2018-02-01

Despite recent progress in designing modified separators for lithium-sulfur (Li-S) batteries, detail in optimizing the synergistic effect between chemical and physical immobilization for lithium polysulfides (LiPS) in modified separator hasn't been investigated totally. Here, a nano-TiO2 decorated carbon layer (T-DCL) has been successfully applied to modify separator for the Li-S battery. The results indicate that appropriate weight percentage of nano-TiO2 uniformly distributed in conductive carbon layer is effective to chemically and physically immobilize for LiPS, and promote the electron transfer during discharge/charge process. The performance of the modified Li-S battery with T-DCL separator are significantly enhanced, with a specific capacity of 883 mAh g-1 retained after 180 cycles at 0.1 C and 762 mAh g-1 retained after 200 cycles at 0.5C, which are much higher than that of separators only coated with TiO2 layer or conductive carbon layer. Besides, the separator coated with T-DCL also shows low electrochemical impedance and good lithium anode protection. These results indicate that separator with T-DCL is promising to balance the physical and chemical LiPS trapping effect, and optimize the electrochemical performance for Li-S battery.

Understanding and Mitigating the Effects of Stable Dodecahydro- closo -dodecaborate Intermediates on Hydrogen-Storage Reactions

DOE PAGES

White, James L.; Newhouse, Rebecca J.; Zhang, Jin Z.; ...

2016-10-25

Alkali metal borohydrides can reversibly store hydrogen; however, the materials display poor cyclability, often times linked to occurrence of stable closo-polyborate intermediate species. In an effort to understand the role of such intermediates on the hydrogen storage properties of metal borohydrides, several alkali metal dodecahydro-closo-dodecaborate salts were isolated in anhydrous form and characterized by diffraction and spectroscopic techniques. Mixtures of Li 2B 12H 12, Na 2B 12H 12, and K 2B 12H 12 with the corresponding alkali metal hydrides were subjected to hydrogenation conditions known to favor partial or full reversibility in metal borohydrides. The stoichiometric mixtures of MH andmore » M 2B 12H 12 salts form the corresponding metal borohydrides MBH 4 (M=Li, Na, K) in almost quantitative yield at 100 MPa H 2 and 500 °C. In addition, stoichiometric mixtures of Li 2B 12H 12 and MgH 2 were found to form MgB 2 at 500 °C and above upon desorption in vacuum. The two destabilization strategies outlined above suggest that metal polyhydro-closo-polyborate species can be converted into the corresponding metal borohydrides or borides, albeit under rather harsh conditions of hydrogen pressure and temperature.« less

Temperature-mediated phase transformation, pore geometry and pore hysteresis transformation of borohydride derived in-born porous zirconium hydroxide nanopowders

PubMed Central

Nayak, Nadiya B.; Nayak, Bibhuti B.

2016-01-01

Development of in-born porous nature of zirconium hydroxide nanopowders through a facile hydrogen (H2) gas-bubbles assisted borohydride synthesis route using sodium borohydride (NaBH4) and novel information on the temperature-mediated phase transformation, pore geometry as well as pore hysteresis transformation of in-born porous zirconium hydroxide nanopowders with the help of X-ray diffraction (XRD), Brunauer–Emmett–Teller (BET) isotherm and Transmission Electron Microscopy (TEM) images are the main theme of this research work. Without any surfactants or pore forming agents, the borohydride derived amorphous nature of porous powders was stable up to 500 °C and then the seed crystals start to develop within the loose amorphous matrix and trapping the inter-particulate voids, which led to develop the porous nature of tetragonal zirconium oxide at 600 °C and further sustain this porous nature as well as tetragonal phase of zirconium oxide up to 800 °C. The novel hydrogen (H2) gas-bubbles assisted borohydride synthesis route led to develop thermally stable porous zirconium hydroxide/oxide nanopowders with an adequate pore size, pore volume, and surface area and thus these porous materials are further suggested for promising use in different areas of applications. PMID:27198738

Grain boundary modification to suppress lithium penetration through garnet-type solid electrolyte

NASA Astrophysics Data System (ADS)

Hongahally Basappa, Rajendra; Ito, Tomoko; Morimura, Takao; Bekarevich, Raman; Mitsuishi, Kazutaka; Yamada, Hirotoshi

2017-09-01

Garnet-type solid electrolytes are one of key materials to enable practical usage of lithium metal anode for high-energy-density batteries. However, it suffers from lithium growth in pellets on charging, which causes short circuit. In this study, grain boundaries of Li6.5La3Zr1.5Ta0.5O12 (LLZT) pellets are modified with Li2CO3 and LiOH to investigate the influence of the microstructure of grain boundaries on lithium growth and to study the mechanism of the lithium growth. In spite of similar properties (relative density of ca. 96% and total ionic conductivity of 7 × 10-4 S cm-1 at 25 °C), the obtained pellets exhibit different tolerance on the short circuit. The LLZT pellets prepared from LiOH-modified LLZT powders exhibit rather high critical current density of 0.6 mA cm-2, at which short circuit occurs. On the other hand, the LLZT pellets without grain boundary modification short-circuited at 0.15 mA cm-2. Microstructural analyses by means of SEM, STEM and EIS suggest that lithium grows through interconnected open voids, and reveal that surface layers such as Li2CO3 and LiOH are not only plug voids but also facilitate the sintering of LLZT to suppress the lithium growth. The results indicate a strategy towards short-circuit-free lithium metal batteries.

Tetra-n-butylammonium borohydride semiclathrate: a hybrid material for hydrogen storage.

PubMed

Shin, Kyuchul; Kim, Yongkwan; Strobel, Timothy A; Prasad, P S R; Sugahara, Takeshi; Lee, Huen; Sloan, E Dendy; Sum, Amadeu K; Koh, Carolyn A

2009-06-11

In this study, we demonstrate that tetra-n-butylammonium borohydride [(n-C(4)H(9))(4)NBH(4)] can be used to form a hybrid hydrogen storage material. Powder X-ray diffraction measurements verify the formation of tetra-n-butylammonium borohydride semiclathrate, while Raman spectroscopic and direct gas release measurements confirm the storage of molecular hydrogen within the vacant cavities. Subsequent to clathrate decomposition and the release of physically bound H(2), additional hydrogen was produced from the hybrid system via a hydrolysis reaction between the water host molecules and the incorporated BH(4)(-) anions. The additional hydrogen produced from the hydrolysis reaction resulted in a 170% increase in the gravimetric hydrogen storage capacity, or 27% greater storage than fully occupied THF + H(2) hydrate. The decomposition temperature of tetra-n-butylammonium borohydride semiclathrate was measured at 5.7 degrees C, which is higher than that for pure THF hydrate (4.4 degrees C). The present results reveal that the BH(4)(-) anion is capable of stabilizing tetraalkylammonium hydrates.

Understanding oscillatory phenomena in molecular hydrogen generation via sodium borohydride hydrolysis.

PubMed

Budroni, M A; Biosa, E; Garroni, S; Mulas, G R C; Marchettini, N; Culeddu, N; Rustici, M

2013-11-14

The hydrolysis of borohydride salts represents one of the most promising processes for the generation of high purity molecular hydrogen under mild conditions. In this work we show that the sodium borohydride hydrolysis exhibits a fingerprinting periodic oscillatory transient in the hydrogen flow over a wide range of experimental conditions. We disproved the possibility that flow oscillations are driven by supersaturation phenomena of gaseous bubbles in the reactive mixture or by a nonlinear thermal feedback according to a thermokinetic model. Our experimental results indicate that the NaBH4 hydrolysis is a spontaneous inorganic oscillator, in which the hydrogen flow oscillations are coupled to an "oscillophor" in the reactive solution. The discovery of this original oscillator paves the way for a new class of chemical oscillators, with fundamental implications not only for testing the general theory on oscillations, but also with a view to chemical control of borohydride systems used as a source of hydrogen based green fuel.

Influence of the concentration of borohydride towards hydrogen production and escape for borohydride oxidation reaction on Pt and Au electrodes - experimental and modelling insights

NASA Astrophysics Data System (ADS)

Olu, Pierre-Yves; Bonnefont, Antoine; Braesch, Guillaume; Martin, Vincent; Savinova, Elena R.; Chatenet, Marian

2018-01-01

The Borohydride Oxidation Reaction (BOR), the anode reaction in a Direct borohydride fuel cell (DBFC), is complex and still poorly understood, which impedes the development and deployment of the DBFC technology. In particular, no practical electrocatalyst is capable to prevent gaseous hydrogen generation and escape from its anode upon operation, which lowers the fuel-efficiency of the DBFC and raises safety issues in operation. The nature of the anode electrocatalysts strongly influences the hydrogen escape characteristics of the DBFC, which demonstrates how important it is to isolate the BOR mechanism in conditions relevant to DBFC operation. In this paper, from a selected literature review and BOR experiments performed in differential electrochemical mass spectrometry (DEMS) in a wide range of NaBH4 concentration (5-500 mM), a microkinetic model of the BOR for both Pt and Au surfaces is proposed; this model takes into account the hydrogen generation and escape.

Electrolytic method for the production of lithium using a lithium-amalgam electrode

DOEpatents

Cooper, John F.; Krikorian, Oscar H.; Homsy, Robert V.

1979-01-01

A method for recovering lithium from its molten amalgam by electrolysis of the amalgam in an electrolytic cell containing as a molten electrolyte a fused-salt consisting essentially of a mixture of two or more alkali metal halides, preferably alkali metal halides selected from lithium iodide, lithium chloride, potassium iodide and potassium chloride. A particularly suitable molten electrolyte is a fused-salt consisting essentially of a mixture of at least three components obtained by modifying an eutectic mixture of LiI-KI by the addition of a minor amount of one or more alkali metal halides. The lithium-amalgam fused-salt cell may be used in an electrolytic system for recovering lithium from an aqueous solution of a lithium compound, wherein electrolysis of the aqueous solution in an aqueous cell in the presence of a mercury cathode produces a lithium amalgam. The present method is particularly useful for the regeneration of lithium from the aqueous reaction products of a lithium-water-air battery.

The Discovery-Oriented Approach to Organic Chemistry. 6. Selective Reduction in Organic Chemistry: Reduction of Aldehydes in the Presence of Esters Using Sodium Borohydride

ERIC Educational Resources Information Center

Baru, Ashvin R.; Mohan, Ram S.

2005-01-01

A discovery-oriented lab experiment is developed that illustrates the chemoselective nature of reductions using sodium borohydride. Products are of sufficient purity to allow analysis by spectroscopy without further purification.

Tailoring the properties of ammine metal borohydrides for solid-state hydrogen storage.

PubMed

Jepsen, Lars H; Ley, Morten B; Filinchuk, Yaroslav; Besenbacher, Flemming; Jensen, Torben R

2015-04-24

A series of halide-free ammine manganese borohydrides, Mn(BH4 )2 ⋅nNH3 , n=1, 2, 3, and 6, a new bimetallic compound Li2 Mn(BH4 )4 ⋅6NH3 , and the first ammine metal borohydride solid solution Mg1-x Mnx (BH4 )2 ⋅6NH3 are presented. Four new crystal structures have been determined by synchrotron radiation powder X-ray diffraction and the thermal decomposition is systematically investigated for all the new compounds. The solid-gas reaction between Mn(BH4 )2 and NH3 provides Mn(BH4 )2 ⋅6NH3 . The number of NH3 per Mn has been varied by mechanochemical treatment of Mn(BH4 )2 ⋅6NH3 -Mn(BH4 )2 mixtures giving rise to increased hydrogen purity for n/m≤1 for M(BH4 )m ⋅nNH3 . The structures of Mg(BH4 )2 ⋅3NH3 and Li2 Mg(BH4 )4 ⋅6NH3 have been revisited and new structural models are presented. Finally, we demonstrate that ammonia destabilizes metal borohydrides with low electronegativity of the metal (χp <∼1.6), while metal borohydrides with high electronegativity (χp >∼1.6) are generally stabilized. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Flexible Carbon Nanotube Modified Separator for High-Performance Lithium-Sulfur Batteries

PubMed Central

Liu, Bin; Wu, Xiaomeng; Wang, Shan; Tang, Zhen; Yang, Quanling; Hu, Guo-Hua; Xiong, Chuanxi

2017-01-01

Lithium-sulfur (Li-S) batteries have become promising candidates for electrical energy storage systems due to their high theoretical specific energy density, low cost and environmental friendliness. However, there are some technical obstacles of lithium-sulfur batteries to be addressed, such as the shuttle effect of polysulfides. Here, we introduced organically modified carbon nanotubes (CNTs) as a coating layer for the separator to optimize structure and enhance the performance of the Li-S battery. The results showed that the cell with a CNTs-coated separator exhibited an excellent cycling performance. Compared to the blank separator, the initial discharge capacity and the capacity after 100 cycles for the CNTs-coated separator was increased by 115% and 161%, respectively. Besides, according to the rate capability test cycling from 0.1C to 2C, the battery with a CNTs-coated separator still released a capacity amounting to 90.2% of the initial capacity, when the current density returned back to 0.1C. It is believed that the organically modified CNTs coating effectively suppresses the shuttle effect during the cycling. The employment of a CNTs-coated separator provides a promising approach for high-performance lithium-sulfur batteries. PMID:28933721

Hydrogen storage material and related processes

DOEpatents

Soloveichik, Grigorii Lev [Latham, NY; Andrus, Matthew John [Cape Canaveral, FL

2012-06-05

Disclosed herein is a composition comprising a complex hydride and a borohydride catalyst wherein the borohydride catalyst comprises a BH.sub.4 group, and a group IV metal, a group V metal, or a combination of a group IV and a group V metal. Also disclosed herein are methods of making the composition.

Hydrogen storage material and related processes

DOEpatents

Soloveichik; Grigorii Lev , Andrus; Matthew John

2010-07-13

Disclosed herein is a composition comprising a complex hydride and a borohydride catalyst wherein the borohydride catalyst comprises a BH.sub.4 group, and a group IV metal, a group V metal, or a combination of a group IV and a group V metal. Also disclosed herein are methods of making the composition.

A Simple Recipe for Whitening Old Newspaper Clippings.

ERIC Educational Resources Information Center

Carter, Henry A.

1995-01-01

Describes a method for experimenting with both whitening and deacidifying old newspaper clippings using sodium borohydride bleaching. Clippings are soaked in distilled water then immersed in sodium borohydride for 15-20 minutes. After rinsing with distilled water, the paper is washed with saturated Ca(OH)2 solution. Readers should not begin…

Borohydride Reduction of Estrone: Demonstration of Diastereoselectivity in the Undergraduate Organic Chemistry Laboratory

ERIC Educational Resources Information Center

Aditya, Animesh; Nichols, David E.; Loudon, G. Marc

2008-01-01

This experiment presents a guided-inquiry approach to the demonstration of diastereoselectivity in an undergraduate organic chemistry laboratory. Chiral hindered ketones such as estrone, undergo facile reduction with sodium borohydride in a highly diastereoselective manner. The diastereomeric estradiols produced in the reaction can be analyzed and…

A prospective comparative study of interaction between lithium and modified electroconvulsive therapy.

PubMed

Thirthalli, Jagadisha; Harish, Thippeswamy; Gangadhar, Bangalore N

2011-03-01

To compare patients on lithium and those not on lithium with regard to adverse effects while receiving ECT. Inpatients with schizophrenia, non-organic psychosis, mania and depression, who were prescribed ECTs either on (n=27) or not (n=28) on lithium were studied. Clinicians blind to lithium-status recorded seizure parameters, interaction with succinyl choline, cardiovascular response, recovery from ECT and immediate post-ECT complications. The lithium group showed no significant difference in terms of seizure variables, apnea time, and recovery from anaesthesia when compared to the non-lithium group. Average maximum heart rate, average maximum systolic blood pressure and average maximum rate pressure product were significantly lower in patients who had combined lithium and ECT. In lithium patients the average time to post-ECT recovery was directly correlated with serum lithium level. Though concurrent lithium is by and large safe during ECT, it benefits to maintain serum lithium level at lower end of therapeutic range. However, the findings can be applied to relatively young patients with no risk factors for ECT-complications.

Green coconut fiber: a novel carrier for the immobilization of commercial laccase by covalent attachment for textile dyes decolourization.

PubMed

Cristóvão, Raquel O; Silvério, Sara C; Tavares, Ana P M; Brígida, Ana Iraidy S; Loureiro, José M; Boaventura, Rui A R; Macedo, Eugénia A; Coelho, Maria Alice Z

2012-09-01

Commercial laccase formulation was immobilized on modified green coconut fiber silanized with 3-glycidoxypropyltrimethoxysilane, aiming to achieve a cheap and effective biocatalyst. Two different strategies were followed: one point (pH 7.0) and multipoint (pH 10.0) covalent attachment. The influence of immobilization time on enzymatic activity and the final reduction with sodium borohydride were evaluated. The highest activities were achieved after 2 h of contact time in all situations. Commercial laccase immobilized at pH 7.0 was found to have higher activity and higher affinity to the substrate. However, the immobilization by multipoint covalent attachment improved the biocatalyst thermal stability at 50 °C, when compared to soluble enzyme and to the immobilized enzyme at pH 7.0. The Schiff's bases reduction by sodium borohydride, in spite of causing a decrease in enzyme activity, showed to contribute to the increase of operational stability through bonds stabilization. Finally, these immobilized enzymes showed high efficiency in the continuous decolourization of reactive textile dyes. In the first cycle, the decolourization is mainly due to dyes adsorption on the support. However, when working in successive cycles, the adsorption capacity of the support decreases (saturation) and the enzymatic action increases, indicating the applicability of this biocatalyst for textile wastewater treatment.

Mangalith: a new lithium pacemaker battery

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gerbier, G.; Lehmann, G.

1980-01-01

An original lithium battery system is being developed for pacemaker application. The material used, lithium-manganese dioxide, industrially available at the present time for a variety of electronic applications, has been modified and adapted for pacemaker power requirements. The utilization of a different modification of manganese dioxide offers performance advantages. The cell technology is described and performance comparisons between this new cathode material and the industrial counterpart are reported. 7 refs.

Characterization of radiation damage to DNA by reaction with borohydride.

PubMed Central

Schellenberg, K A; Shaeffer, J; Nichols, R K; Gates, D

1981-01-01

Irradiation of aqueous solutions of native calf thymus DNA with x-rays produced functional groups that reacted with sodium borohydride. The DNA was labeled with tritium from NaB3H4 to the extent of 2.0 x 10(-10) atom/dalton/rad. The presence of cysteamine or other radical scavengers, or saturation of the solution with nitrogen during irradiation decreased the labeling. After mild acid hydrolysis, the major tritium-containing moiety was identical with 2,3-dihydroxy-2-methylpropanoic acid in all chromatographic systems tested. The suggested mechanism of labeling involved reduction by borohydride of the potential aldehyde at carbon 6 of thymine glycol residues present in the irradiated DNA. PMID:7279674

Deliberate modification of the solid electrolyte interphase (SEI) during lithiation of magnetite, Fe 3O 4: impact on electrochemistry

DOE PAGES

Bock, David C.; Marschilok, Amy C.; Takeuchi, Kenneth J.; ...

2017-11-20

Here, magnetite is a conversion anode material displaying multi-electron transfer during lithiation and delithiation. The solid electrolyte interphase (SEI) on magnetite, Fe 3O 4, electrodes for lithium ion batteries was deliberately modified through the use of fluoroethylene carbonate (FEC) electrolyte additive, improving both capacity retention and rate capability. Analysis showed reduction of FEC at higher voltage compared to non-fluorinated solvents with formation of a modified lithium flouride containing electrode surface.

First-principles investigations of ionic conduction in Li and Na borohydrides

NASA Astrophysics Data System (ADS)

Varley, Joel; Heo, Tae-Wook; Ray, Keith; Bonev, Stanimir; Wood, Brandon

Recent experimental studies have identified a family of alkali borohydride materials that exhibit superionic transition temperatures approaching room temperature and ionic conductivities exceeding 0.1 S/cm-1, making them highly promising solid electrolytes for next-generation batteries. Despite the rapid advances in improving the superionic conductivity in these materials, an understanding of the exact mechanisms driving the transport remains unknown. Here we use ab initio molecular dynamics calculations to address this issue by characterizing the diffusivity of the Li and Na species in a representative set of closoborane ionic conductors. We investigate both the Na and Li-containing borohydrides with icosahedral (B12H12) and double-capped square antiprism (B10H10) anion species and discuss the trends in ionic conductivity as a function of stoichiometry and the incorporation of various dopants. Our results support the borohydrides as a subset of a larger family of very promising solid electrolytes and identify strategies to improving the conductivity in these materials. This work performed under the auspices of the U.S. Department of Energy by Lawrence Livermore National Laboratory under Contract DE-AC52-07NA27344.

Polyethylene oxide film coating enhances lithium cycling efficiency of an anode-free lithium-metal battery.

PubMed

Assegie, Addisu Alemayehu; Cheng, Ju-Hsiang; Kuo, Li-Ming; Su, Wei-Nien; Hwang, Bing-Joe

2018-03-29

The practical implementation of an anode-free lithium-metal battery with promising high capacity is hampered by dendrite formation and low coulombic efficiency. Most notably, these challenges stem from non-uniform lithium plating and unstable SEI layer formation on the bare copper electrode. Herein, we revealed the homogeneous deposition of lithium and effective suppression of dendrite formation using a copper electrode coated with a polyethylene oxide (PEO) film in an electrolyte comprising 1 M LiTFSI, DME/DOL (1/1, v/v) and 2 wt% LiNO3. More importantly, the PEO film coating promoted the formation of a thin and robust SEI layer film by hosting lithium and regulating the inevitable reaction of lithium with the electrolyte. The modified electrode exhibited stable cycling of lithium with an average coulombic efficiency of ∼100% over 200 cycles and low voltage hysteresis (∼30 mV) at a current density of 0.5 mA cm-2. Moreover, we tested the anode-free battery experimentally by integrating it with an LiFePO4 cathode into a full-cell configuration (Cu@PEO/LiFePO4). The new cell demonstrated stable cycling with an average coulombic efficiency of 98.6% and capacity retention of 30% in the 200th cycle at a rate of 0.2C. These impressive enhancements in cycle life and capacity retention result from the synergy of the PEO film coating, high electrode-electrolyte interface compatibility, stable polar oligomer formation from the reduction of 1,3-dioxolane and the generation of SEI-stabilizing nitrite and nitride upon lithium nitrate reduction. Our result opens up a new route to realize anode-free batteries by modifying the copper anode with PEO to achieve ever more demanding yet safe interfacial chemistry and control of dendrite formation.

First-principles studies of phase stability and crystal structures in Li-Zn mixed-metal borohydrides

NASA Astrophysics Data System (ADS)

Wang, Yongli; Zhang, Yongsheng; Wolverton, C.

2013-07-01

We address the problem of finding mixed-metal borohydrides with favorable thermodynamics and illustrate the approach using the example of LiZn2(BH4)5. Using density functional theory (DFT), along with the grand-canonical linear programming method (GCLP), we examine the experimentally and computationally proposed crystal structures and the finite-temperature thermodynamics of dehydrogenation for the quaternary hydride LiZn2(BH4)5. We find the following: (i) For LiZn2(BH4)5, DFT calculations of the experimental crystal structures reveal that the structure from the neutron diffraction experiments of Ravnsbæk is more stable [by 24 kJ/(mol f.u.)] than that based on a previous x-ray study. (ii) Our DFT calculations show that when using the neutron-diffraction structure of LiZn2(BH4)5, the recently theoretically predicted LiZn(BH4)3 compound is unstable with respect to the decomposition into LiZn2(BH4)5+LiBH4. (iii) GCLP calculations show that even though LiZn2(BH4)5 is a combination of weakly [Zn(BH4)2] and strongly (LiBH4) bound borohydrides, its decomposition is not intermediate between the two individual borohydrides. Rather, we find that the decomposition of LiZn2(BH4)5 is divided into a weakly exothermic step [LiZn2(BH4)5→2Zn+(1)/(5)LiBH4+(2)/(5)Li2B12H12+(36)/(5)H2] and three strong endothermic steps (12LiBH4→10LiH+Li2B12H12+13H2; Zn+LiH→LiZn+(1)/(2)H2; 2Zn+Li2B12H12→2LiZn+12B+6H2). DFT-calculated ΔHZPET=0K values for the first three LiZn2(BH4)5 decomposition steps are -19, +37, +74 kJ/(mol H2), respectively. The behavior of LiZn2(BH4)5 shows that mixed-metal borohydrides formed by mixing borohydrides of high and low thermodynamics stabilities do not necessarily have an intermediate decomposition tendency. Our results suggest the correct strategy to find intermediate decomposition in mixed-metal borohydrides is to search for stable mixed-metal products such as ternary metal borides.

Modified Separator Performing Dual Physical/Chemical Roles to Inhibit Polysulfide Shuttle Resulting in Ultrastable Li-S Batteries.

PubMed

Abbas, Syed Ali; Ding, Jiang; Wu, Sheng Hui; Fang, Jason; Boopathi, Karunakara Moorthy; Mohapatra, Anisha; Lee, Li Wei; Wang, Pen-Cheng; Chang, Chien-Cheng; Chu, Chih Wei

2017-12-26

In this paper we describe a modified (AEG/CH) coated separator for Li-S batteries in which the shuttling phenomenon of the lithium polysulfides is restrained through two types of interactions: activated expanded graphite (AEG) flakes interacted physically with the lithium polysulfides, while chitosan (CH), used to bind the AEG flakes on the separator, interacted chemically through its abundance of amino and hydroxyl functional groups. Moreover, the AEG flakes facilitated ionic and electronic transfer during the redox reaction. Live H-cell discharging experiments revealed that the modified separator was effective at curbing polysulfide shuttling; moreover, X-ray photoelectron spectroscopy analysis of the cycled separator confirmed the presence of lithium polysulfides in the AEG/CH matrix. Using this dual functional interaction approach, the lifetime of the pure sulfur-based cathode was extended to 3000 cycles at 1C-rate (1C = 1670 mA/g), decreasing the decay rate to 0.021% per cycle, a value that is among the best reported to date. A flexible battery based on this modified separator exhibited stable performance and could turn on multiple light-emitting diodes. Such modified membranes with good mechanical strength, high electronic conductivity, and anti-self-discharging shield appear to be a scalable solution for future high-energy battery systems.

Volcano Plot for Bimetallic Catalysts in Hydrogen Generation by Hydrolysis of Sodium Borohydride

ERIC Educational Resources Information Center

Koska, Anais; Toshikj, Nikola; Hoett, Sandra; Bernaud, Laurent; Demirci, Umit B.

2017-01-01

In the field of "hydrogen energy", sodium borohydride (NaBH[subscript 4]) is a potential hydrogen carrier able to release H[subscript 2] by hydrolysis in the presence of a metal catalyst. Our laboratory experiment focuses on this. It is intended for thirdyear undergraduate students in order to have hands-on laboratory experience through…

Regenerative Fuel Cells for Space Power and Energy Conversion (NaBH4/H2O2 Fuel Cell Development)

NASA Technical Reports Server (NTRS)

Valdez, Thomas I.; Miley, George H.; Luo, Nie; Burton, Rodney; Mather, Joseph; Hawkins, Glenn; Byrd, Ethan; Gu, Lifeng; Shrestha, Prajakti Joshi

2006-01-01

A viewgraph presentation describing hydrogen peroxide and sodium borohydride development is shown. The topics include: 1) Motivation; 2) The Sodium Borohydride Fuel Cell; 3) Fuel Cell Comparisons; 4) MEA Optimization; 5) 500-Watt Stack Testing; 6) System Modeling: Fuel Cell Power Source for Lunar Rovers; and 7) Conclusions

A Guided-Inquiry Approach to the Sodium Borohydride Reduction and Grignard Reaction of Carbonyl Compounds

ERIC Educational Resources Information Center

Rosenberg, Robert E.

2007-01-01

The guided-inquiry approach is applied to the reactions of sodium borohydride and phenyl magnesium bromide with benzaldehyde, benzophenone, benzoic anhydride, and ethyl benzoate. Each team of four students receives four unknowns. Students identify the unknowns and their reaction products by using the physical state of the unknown, an…

Effective Trapping of Lithium Polysulfides Using a Functionalized Carbon Nanotube-Coated Separator for Lithium-Sulfur Cells with Enhanced Cycling Stability.

PubMed

Ponraj, Rubha; Kannan, Aravindaraj G; Ahn, Jun Hwan; Lee, Jae Hee; Kang, Joonhee; Han, Byungchan; Kim, Dong-Won

2017-11-08

The critical issues that hinder the practical applications of lithium-sulfur batteries, such as dissolution and migration of lithium polysulfides, poor electronic conductivity of sulfur and its discharge products, and low loading of sulfur, have been addressed by designing a functional separator modified using hydroxyl-functionalized carbon nanotubes (CNTOH). Density functional theory calculations and experimental results demonstrate that the hydroxyl groups in the CNTOH provoked strong interaction with lithium polysulfides and resulted in effective trapping of lithium polysulfides within the sulfur cathode side. The reduction in migration of lithium polysulfides to the lithium anode resulted in enhanced stability of the lithium electrode. The conductive nature of CNTOH also aided to efficiently reutilize the adsorbed reaction intermediates for subsequent cycling. As a result, the lithium-sulfur cell assembled with a functional separator exhibited a high initial discharge capacity of 1056 mAh g -1 (corresponding to an areal capacity of 3.2 mAh cm -2 ) with a capacity fading rate of 0.11% per cycle over 400 cycles at 0.5 C rate.

Alternate seal configuration for lithium primary cells

NASA Technical Reports Server (NTRS)

Kelley, J. A.

1982-01-01

The problem of glass degradation in the glass-to-metal seals in lithium/sulfur dioxide cells is discussed. The glass degradation mechanism is attributed to lithium reacting with glass which is a result of deposition of lithium at the glass/metal/electrolyte interface. The worst degradation was observed when cells were stored in the inverted position. Alternate sealing methods were examined and a modified Ziegler seal is considered to be one of the best possible methods. The seal consists of a crimp type soft seal using a plastic annulus and a metal tube. Results of degradation tests are presented.

Neuroprotective Effects of Psychotropic Drugs in Huntington’s Disease

PubMed Central

Lauterbach, Edward C.

2013-01-01

Psychotropics (antipsychotics, mood stabilizers, antidepressants, anxiolytics, etc.) are commonly prescribed to treat Huntington’s disease (HD). In HD preclinical models, while no psychotropic has convincingly affected huntingtin gene, HD modifying gene, or huntingtin protein expression, psychotropic neuroprotective effects include upregulated huntingtin autophagy (lithium), histone acetylation (lithium, valproate, lamotrigine), miR-222 (lithium-plus-valproate), mitochondrial protection (haloperidol, trifluoperazine, imipramine, desipramine, nortriptyline, maprotiline, trazodone, sertraline, venlafaxine, melatonin), neurogenesis (lithium, valproate, fluoxetine, sertraline), and BDNF (lithium, valproate, sertraline) and downregulated AP-1 DNA binding (lithium), p53 (lithium), huntingtin aggregation (antipsychotics, lithium), and apoptosis (trifluoperazine, loxapine, lithium, desipramine, nortriptyline, maprotiline, cyproheptadine, melatonin). In HD live mouse models, delayed disease onset (nortriptyline, melatonin), striatal preservation (haloperidol, tetrabenazine, lithium, sertraline), memory preservation (imipramine, trazodone, fluoxetine, sertraline, venlafaxine), motor improvement (tetrabenazine, lithium, valproate, imipramine, nortriptyline, trazodone, sertraline, venlafaxine), and extended survival (lithium, valproate, sertraline, melatonin) have been documented. Upregulated CREB binding protein (CBP; valproate, dextromethorphan) and downregulated histone deacetylase (HDAC; valproate) await demonstration in HD models. Most preclinical findings await replication and their limitations are reviewed. The most promising findings involve replicated striatal neuroprotection and phenotypic disease modification in transgenic mice for tetrabenazine and for sertraline. Clinical data consist of an uncontrolled lithium case series (n = 3) suggesting non-progression and a primarily negative double-blind, placebo-controlled clinical trial of lamotrigine. PMID:24248060

Lithium ameliorates open-field and elevated plus maze behaviors, and brain phospho-glycogen synthase kinase 3-beta expression in fragile X syndrome model mice.

PubMed

Chen, Xi; Sun, Weiwen; Pan, Ying; Yang, Quan; Cao, Kaiyi; Zhang, Jin; Zhang, Yizhi; Chen, Mincong; Chen, Feidi; Huang, Yueling; Dai, Lijun; Chen, Shengqiang

2013-10-01

To investigate whether lithium modifies open-field and elevated plus maze behavior, and brain phospho-glycogen synthase kinase 3 (P-GSK3beta) expression in Fmr1 knockout mice. One hundred and eighty FVB mice, including knockout and wild type, with an age of 30 days were used. An open-field and elevated plus maze was utilized to test behavior, while western blot was used to measure the P-GSK3beta expression. Six groups were formed: control (saline), lithium chloride 30, 60, 90, 120, and 200 mg/kg. The experiments were carried out in the Institute of Neuroscience, Second Affiliated Hospital of Guangzhou Medical University, Guangzhou, China between January and June 2012. Lithium significantly decreased total distance, crossing, central area time, and center entry in the open-field test (p<0.05), and significantly reduced open-arm tracking, open-arm entry, and open-arm time in the elevated plus maze (p<0.05) in knockout mice. In wild type mice, significant changes were observed in both behavior tests in some treatment groups. Lithium ameliorated P-GSK3beta expression in the hippocampus of all the treatment groups in knockout mice (p<0.05). However, lithium did not modify either GSK3beta expression in tissues of knockout mice, or P-GSK3beta or GSK3beta expression in tissues of wild type mice. Lithium ameliorated open-field and elevated plus maze behaviors of Fmr1 knockout mice. This effect may be related to its enhancement of P-GSK3beta expression. Our findings suggest that lithium might have a therapeutic effect in fragile X syndrome.

New chemical hydrogen storage materials exploiting the self-sustaining thermal decomposition of guanidinium borohydride.

PubMed

Groshens, Thomas J; Hollins, Richard A

2009-06-07

Guanidinium borohydride (GBH) was structurally characterized by single-crystal X-ray diffraction and found to release more than 10 wt% H(2) as a fairly pure stream during a self-sustaining thermal decomposition reaction both with and without additives that were identified to reduce the concentration of the main ammonia impurity and control the reaction sustainability.

A Microwave-Assisted Reduction of Cyclohexanone Using Solid-State-Supported Sodium Borohydride

ERIC Educational Resources Information Center

White, Lori L.; Kittredge, Kevin W.

2005-01-01

The reduction of carbonyl groups by sodium borohydride though is a well-known reaction in most organic lab texts, a difficulty for an instructor adopting this reaction in a student lab is that it is too long. Using a microwave assisted organic synthesis solves this difficulty and one such reaction, which is the microwave-assisted reduction of…

Solid Aluminum Borohydrides for Prospective Hydrogen Storage.

PubMed

Dovgaliuk, Iurii; Safin, Damir A; Tumanov, Nikolay A; Morelle, Fabrice; Moulai, Adel; Černý, Radovan; Łodziana, Zbigniew; Devillers, Michel; Filinchuk, Yaroslav

2017-12-08

Metal borohydrides are intensively researched as high-capacity hydrogen storage materials. Aluminum is a cheap, light, and abundant element and Al 3+ can serve as a template for reversible dehydrogenation. However, Al(BH 4 ) 3 , containing 16.9 wt % of hydrogen, has a low boiling point, is explosive on air and has poor storage stability. A new family of mixed-cation borohydrides M[Al(BH 4 ) 4 ], which are all solid under ambient conditions, show diverse thermal decomposition behaviors: Al(BH 4 ) 3 is released for M=Li + or Na + , whereas heavier derivatives evolve hydrogen and diborane. NH 4 [Al(BH 4 ) 4 ], containing both protic and hydridic hydrogen, has the lowest decomposition temperature of 35 °C and yields Al(BH 4 ) 3 ⋅NHBH and hydrogen. The decomposition temperatures, correlated with the cations' ionic potential, show that M[Al(BH 4 ) 4 ] species are in the most practical stability window. This family of solids, with convenient and versatile properties, puts aluminum borohydride chemistry in the mainstream of hydrogen storage research, for example, for the development of reactive hydride composites with increased hydrogen content. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Platinum- and membrane-free swiss-roll mixed-reactant alkaline fuel cell.

PubMed

Aziznia, Amin; Oloman, Colin W; Gyenge, Előd L

2013-05-01

Eliminating the expensive and failure-prone proton exchange membrane (PEM) together with the platinum-based anode and cathode catalysts would significantly reduce the high capital and operating costs of low-temperature (<373 K) fuel cells. We recently introduced the Swiss-roll mixed-reactant fuel cell (SR-MRFC) concept for borohydride-oxygen alkaline fuel cells. We now present advances in anode electrocatalysis for borohydride electrooxidation through the development of osmium nanoparticulate catalysts supported on porous monolithic carbon fiber materials (referred to as an osmium 3D anode). The borohydride-oxygen SR-MRFC operates at 323 K and near atmospheric pressure, generating a peak power density of 1880 W m(-2) in a single-cell configuration by using an osmium-based anode (with an osmium loading of 0.32 mg cm(-2)) and a manganese dioxide gas-diffusion cathode. To the best of our knowledge, 1880 W m(-2) is the highest power density ever reported for a mixed-reactant fuel cell operating under similar conditions. Furthermore, the performance matches the highest reported power densities for conventional dual chamber PEM direct borohydride fuel cells. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

New hydrogen-rich ammonium metal borohydrides, NH4[M(BH4)4], M = Y, Sc, Al, as potential H2 sources.

PubMed

Starobrat, A; Jaroń, T; Grochala, W

2018-03-26

Three metal-ammonium borohydrides, NH4[M(BH4)4] M = Y, Sc, Al, denoted 1, 2, 3, respectively, were prepared via a low temperature mechanochemical synthesis and characterized using PXRD, FTIR and TGA/DSC/MS. The compounds 1 and 2 adopt the P21/c space group while the compound 3 crystallizes in an orthorhombic unit cell (Fddd). The first decomposition step of all three derivatives of ammonium borohydride has the maximum rate at 48 °C, 53 °C and 35 °C for 1, 2 and 3, respectively, which are comparable to that for NH4BH4 (53 °C). The thermal decomposition of these metal-ammonium borohydrides is a multistep process, with predominantly exothermic low-temperature stages. The compound 1 decomposes via known Y(BH4)3, however, some of the solid decomposition products of the other two compounds have not been fully identified. In the system containing compound 2, a new, more dense polymorph of the previously reported LiSc(BH4)4 has been detected as the intermediate of slow decomposition at room temperature.

Simulating the synthesis and thermodynamic characteristics of the desolvation of lanthanide borohydride tris-Tetrahydrofuranates

NASA Astrophysics Data System (ADS)

Gafurov, B. A.; Mirsaidov, I. U.; Nasrulloeva, D. Kh.; Badalov, A.

2013-10-01

Lanthanide borohydride tris-tetrahydrofuranates (Ln(BH4) · 3THF, where THF is tetrahydrofuran and Ln is La, Nd, Sm, Gd, Er, Yb, and Lu) is synthesized via the exchange reaction of lanthanide(III) chloride and sodium borohydride in THF. It is found that synthesis proceeds according to a stepwise mechanism and the product of the reaction (lanthanide borohydride) initiates the process. The two-step character of the desolvation of Ln(BH4)3 · 3THF under steady-state conditions in the temperature range of 300 to 400 K is determined through X-ray phase and chemical analyses, tensiometry, and gas volumetry. It is established that one mole and then two moles of THF are removed from the initial sample at the first and second steps, respectively. Equations for barograms are obtained and the thermodynamic characteristics of desolvation of Ln(BH4)3 · 3THF under study are calculated. Gibbs energy values of the stages of process are determined semi-empirically. The law of its change for the entire series of Ln(BH4)3 · 3THF is determined with the emergence of the tetrad effect.

Carboxylate modified porous graphitic carbon: a new class of hydrophilic interaction liquid chromatography phases.

PubMed

Wahab, M Farooq; Ibrahim, Mohammed E A; Lucy, Charles A

2013-06-18

Stationary phases for hydrophilic interaction liquid chromatography (HILIC) are predominantly based on silica and polymer supports. We present porous graphitic carbon particles with covalently attached carboxylic acid groups (carboxylate-PGC) as a new HILIC stationary phase. PGC particles were modified by adsorbing the diazonium salt of 4-aminobenzoic acid onto the PGC, followed by reduction of the adsorbed salt with sodium borohydride. The newly developed carboxylate-PGC phase exhibits different selectivity than that of 35 HPLC columns, including bare silica, zwitterionic, amine, reversed, and unmodified PGC phases. Carboxylate-PGC is stable from pH 2.0 to 12.6, yielding reproducible retention even at pH 12.6. Characterization of the new phase is presented by X-ray photoelectron spectroscopy, thermogravimetry, zeta potentials, and elemental analysis. The chromatographic performance of carboxylate-PGC as a HILIC phase is illustrated by separations of carboxylic acids, nucleotides, phenols, and amino acids.

Investigation of catalytic activity towards oxygen reduction reaction of Pt dispersed on boron doped graphene in acid medium.

PubMed

Pullamsetty, Ashok; Sundara, Ramaprabhu

2016-10-01

Boron doped graphene was prepared by a facile method and platinum (Pt) decoration over boron doped graphene was done in various chemical reduction methods such as sodium borohydride (NaBH4), polyol and modified polyol. X-ray diffraction analysis indicates that the synthesized catalyst particles are present in a nanocrystalline structure and transmission and scanning electron microscopy were employed to investigate the morphology and particle distribution. The electrochemical properties were investigated with the help of the rotating disk electrode (RDE) technique and cyclic voltammetry. The results show that the oxygen reduction reaction (ORR) takes place by a four-electron process. The kinetics of the ORR was evaluated using K-L and Tafel plots. The electrocatalyst obtained in modified polyol reduction method has shown the better catalytic activity compared to other two electrocatalysts. Copyright © 2016 Elsevier Inc. All rights reserved.

Self-standing elastomeric composites based on lithium ferrites and their dielectric behavior

NASA Astrophysics Data System (ADS)

Soreto Teixeira, S.; Graça, M. P. F.; Dionisio, M.; Ilcíkova, M.; Mosnacek, J.; Spitalsky, Z.; Krupa, I.; Costa, L. C.

2014-12-01

Lithium ferrite (LiFe5O8) is an attractive material for technological applications due to its physical properties, which are significantly dependent on the preparation method and raw materials. In this work, LiFe5O8 crystallites were obtained by controlled heat-treatment process at 1100 °C, of a homogeneous mixture of Li2O-Fe2O3 powders, prepared by wet ball-milling and using lithium and iron nitrates as raw materials. The main goal was the preparation of a flexible and self-standing tick composite film by embedding lithium ferrite particles in a polymeric matrix, taking advantage of the good mechanical properties of the polymer and of the electrical and dielectric properties of the ferrite. The selected polymer matrix was styrene-b-isoprene-b-styrene copolymer. To prepare the composites, the lithium ferrite particles were chemically modified in order to functionalize their surface. To analyse the influence of the particles surface modification, different composites were made, with modified and unmodified particles. The structure of the obtained composites was studied by FTIR, XRD, TGA, and DSC techniques. The dielectric properties were analysed, in the frequency range between 10 Hz and 1 MHz and in function of temperature in the range between -73 °C and 127 °C. These properties were related with the structure and concentration of the particles in the matrix network. The composites with the modified particles present higher dielectric constant, maintaining values of loss tangent sufficiently low (<10-2) that can be considered interesting for technological applications.

Chloride-reinforced carbon nanofiber host as effective polysulfide traps in lithium-sulfur batteries

DOE PAGES

Fan, Lei; Zhuang, Houlong; Zhang, Kaihang; ...

2016-01-01

Lithium-sulfur (Li-S) battery is one of the most promising alternatives for the current state-of-art lithium-ion batteries (LIBs) due to its high theoretical energy density and lower production cost from the use of earth abundant element - sulfur. However, the commercialization of Li-S batteries has been so far limited to the cyclability and the retention of active sulfur materials. Using co-electrospinning and physical vapor deposition procedures, we created a class of chloride-carbon nanofiber composites, and studied their effectiveness on polysulfides sequestration. By trapping sulfur reduction products in the modified-cathode through both chemical and physical confinements in a conductive host, these chloride-coatedmore » cathodes are shown to remarkably suppress the polysulfide dissolution and shuttling between lithium and sulfur electrodes. We show that not only the binding energy but also the electronic conductivity of the host plays an important role on the reversibility of sulfur-based cathode upon repeated cycles. Electrochemical analysis of the chloride-modified cathodes over hundreds of cycles indicates that too strong binding of the sulfur species may lead to the decay of Coulombic efficiency. Cells containing indium chloride-modified carbon nanofiber outperform cells with other halogenated salt modifications, delivering an average specific capacity of above 1200mAh g-1 at 0.2C over 200 cycles. Once loaded with high S content, it shows stable capacity retention with only 0.019% decay per cycle from 5th to 650th cycle. It also shows stabilized cyclability and enhanced Coulombic efficiency in the absence of traditional anode stabilizer lithium nitrite.« less

Highly stable noble-metal nanoparticles in tetraalkylphosphonium ionic liquids for in situ catalysis.

PubMed

Banerjee, Abhinandan; Theron, Robin; Scott, Robert W J

2012-01-09

Gold and palladium nanoparticles were prepared by lithium borohydride reduction of the metal salt precursors in tetraalkylphosphonium halide ionic liquids in the absence of any organic solvents or external nanoparticle stabilizers. These colloidal suspensions remained stable and showed no nanoparticle agglomeration over many months. A combination of electrostatic interactions between the coordinatively unsaturated metal nanoparticle surface and the ionic-liquid anions, bolstered by steric protection offered by the bulky alkylated phosphonium cations, is likely to be the reason behind such stabilization. The halide anion strongly absorbs to the nanoparticle surface, leading to exceptional nanoparticle stability in halide ionic liquids; other tetraalkylphosphonium ionic liquids with non-coordinating anions, such as tosylate and hexafluorophosphate, show considerably lower affinities towards the stabilization of nanoparticles. Palladium nanoparticles stabilized in the tetraalkylphosphonium halide ionic liquid were stable, efficient, and recyclable catalysts for a variety of hydrogenation reactions at ambient pressures with sustained activity. Aerial oxidation of the metal nanoparticles occurred over time and was readily reversed by re-reduction of oxidized metal salts. Copyright © 2012 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Synthesis of 9,9,9-trideutero-1,4-dihydroxynonane mercapturic acid (d3-DHN-MA), a useful internal standard for DHN-MA urinalysis.

PubMed

Chantegrel, B; Deshayes, C; Doutheau, A; Steghens, J P

2002-10-01

Racemic 1,4-dihydroxynonane mercapturic acid (DHN-MA) and 9,9,9-trideutero-1,4-dihydroxynonane mercapturic acid (d3-DHN-MA) are synthesized on a 400-mg scale (overall yield approximately 40%) by a two-step sequence involving Michael addition of N-acetyl-L-cysteine to methyl 4-hydroxynon-2(E)-enoate or methyl 9,9,9-trideutero-4-hydroxynon-2 (E)-enoate, followed by reduction of the intermediate adducts with lithium borohydride. The requisite starting methyl esters are obtained, respectively, from heptanal or 7,7,7-trideuteroheptanal and methyl 4-chlorophenylsulfinylacetate via a sulfoxide piperidine and carbonyl reaction described in the literature. The 7,7,7-trideuteroheptanal is easily prepared by classical methods in four steps from 6-bromo-1-hexanol. 13C NMR data indicate that DHN-MA as well as d3-DHN-MA are obtained as mixtures of four diastereomers. Preliminary results show that d3-DHN-MA could be used as an internal standard for mass spectrometric quantification of DHN-MA in human urine.

Direct synthesis of calcium borohydride

DOEpatents

Ronnebro, Ewa Carin Ellinor [Dublin, CA; Majzoub, Eric H [Pleasanton, CA

2009-10-27

A method is disclosed for directly preparing an alkaline earth metal borohydride, i.e. Ca(BH.sub.4).sub.2, from the alkaline earth metal hydride and the alkaline earth metal boride. The borohydride thus prepared is doped with a small portion of a metal chloride catalyst compound, such as RuCl.sub.3, TiCl.sub.3, or a mixture of TiCl.sub.3 and palladium metal. The process provides for mechanically mixing the dry reagents under an inert atmosphere followed by charging the mixed materials with high pressure hydrogen at about 70 MPa while heating the mixture to about 400.degree. C. The method is relatively simple and inexpensive and provides reversible hydride compounds which are free of the usual contamination introduced by prior art wet chemical methods.

Effect of notch depth of modified current collector on internal-short-circuit mitigation for lithium-ion battery

NASA Astrophysics Data System (ADS)

Wang, Meng; Noelle, Daniel J.; Shi, Yang; Le, Anh V.; Qiao, Yu

2018-01-01

Formation of internal short circuit (ISC) may result in catastrophic thermal runaway of lithium-ion battery (LIB). Among LIB cell components, direct contact between cathode and anode current collectors is most critical to the ISC behavior, yet is still relatively uninvestigated. In the current study, we analyze the effect of heterogeneity of current collector on the temperature increase of LIB cells subjected to mechanical abuse. The cathode current collector is modified by surface notches, so that it becomes effectively brittle and the ISC site can be isolated. Results from impact tests on LIB cells with modified current collectors suggest that their temperature increase can be negligible. The critical parameters include the failure strain and the failure work of modified current collector, both of which are related to the notch depth.

Surface modified CF x cathode material for ultrafast discharge and high energy density

DOE PAGES

Dai, Yang; Zhu, Yimei; Cai, Sendan; ...

2014-11-10

Li/CF x primary possesses the highest energy density of 2180 W h kg⁻¹ among all primary lithium batteries. However, a key limitation for the utility of this type of battery is in its poor rate capability because the cathode material, CF x, is an intrinsically poor electronic conductor. Here, we report on our development of a controlled process of surface de-fluorination under mild hydrothermal conditions to modify the highly fluorinated CF x. The modified CF x, consisting of an in situ generated shell component of F-graphene layers, possesses good electronic conductivity and removes the transporting barrier for lithium ions, yieldingmore » a high-capacity performance and an excellent rate-capability. Indeed, a capacity of 500 mA h g⁻¹ and a maximum power density of 44 800 W kg⁻¹ can be realized at the ultrafast rate of 30 C (24 A g⁻¹), which is over one order of magnitude higher than that of the state-of-the-art primary lithium-ion batteries.« less

By-Product Carrying Humidified Hydrogen: An Underestimated Issue in the Hydrolysis of Sodium Borohydride.

PubMed

Petit, Eddy; Miele, Philippe; Demirci, Umit B

2016-07-21

Catalyzed hydrolysis of sodium borohydride generates up to four molecules of hydrogen, but contrary to what has been reported so far, the humidified evolved gas is not pure hydrogen. Elemental and spectroscopic analyses show, for the first time, that borate by-products pollute the stream as well as the vessel. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Solid-state rechargeable magnesium battery

DOEpatents

Shao, Yuyan; Liu, Jun; Liu, Tianbiao; Li, Guosheng

2016-09-06

Embodiments of a solid-state electrolyte comprising magnesium borohydride, polyethylene oxide, and optionally a Group IIA or transition metal oxide are disclosed. The solid-state electrolyte may be a thin film comprising a dispersion of magnesium borohydride and magnesium oxide nanoparticles in polyethylene oxide. Rechargeable magnesium batteries including the disclosed solid-state electrolyte may have a coulombic efficiency .gtoreq.95% and exhibit cycling stability for at least 50 cycles.

Enhanced lithium storage capability of Li3V2(PO4)3@C co-modified with graphene and Ce3+ doping as high-power cathode for lithium-ion batteries

NASA Astrophysics Data System (ADS)

Tong, Junjie; Fang, Yunhui

2017-12-01

As a high-voltage cathode material, monoclinic Li3V2(PO4)3 has been proposed as the next-generation commercial electrode for lithium-ion batteries. Nevertheless, it remains a practical challenge to improve the poor electronic conductivity of Li3V2(PO4)3. Herein, we first design and fabricate the Li3V2(PO4)3@C (LVP@C) nanocrystals further modified by graphene and doped with Ce3+-ion via a facile sol-gel method. The Ce3+ doping can form a continuous conductive pathway in the electrode and thus improve the intrinsic electronic conductivity of Li3V2(PO4)3 material. Meanwhile, the residual carbon layer and graphene can also construct a conductive network, which is helpful to enhance the apparent conductivity of Li3V2(PO4)3. Therefore, the graphene and Ce3+ doping co-decorated LVP@C (G-LVCeP@C) composite exhibits better lithium storage capability than the LVP@C and Ce3+-doped LVP@C (LVCeP@C) materials. This novel design provides an effective strategy for the preparation of other electrodes for lithium-ion batteries.

Synthesis, structure and properties of bimetallic sodium rare-earth (RE) borohydrides, NaRE(BH4)4, RE = Ce, Pr, Er or Gd.

PubMed

Payandeh GharibDoust, SeyedHosein; Ravnsbæk, Dorthe B; Černý, Radovan; Jensen, Torben R

2017-10-10

Formation, stability and properties of new metal borohydrides within RE(BH 4 ) 3 -NaBH 4 , RE = Ce, Pr, Er or Gd is investigated. Three new bimetallic sodium rare-earth borohydrides, NaCe(BH 4 ) 4 , NaPr(BH 4 ) 4 and NaEr(BH 4 ) 4 are formed based on an addition reaction between NaBH 4 and halide free rare-earth metal borohydrides RE(BH 4 ) 3 , RE = Ce, Pr, Er. All the new compounds crystallize in the orthorhombic crystal system. NaCe(BH 4 ) 4 has unit cell parameters of a = 6.8028(5), b = 17.5181(13), c = 7.2841(5) Å and space group Pbcn. NaPr(BH 4 ) 4 is isostructural to NaCe(BH 4 ) 4 with unit cell parameters of a = 6.7617(2), b = 17.4678(7), c = 7.2522(3) Å. NaEr(BH 4 ) 4 crystallizes in space group Cmcm with unit cell parameters of a = 8.5379(2), b = 12.1570(4), c = 9.1652(3) Å. The structural relationships, also to the known RE(BH 4 ) 3 , are discussed in detail and related to the stability and synthesis conditions. Heat treatment of NaBH 4 -Gd(BH 4 ) 3 mixture forms an unstable amorphous phase, which decomposes after one day at RT. NaCe(BH 4 ) 4 and NaPr(BH 4 ) 4 show reversible hydrogen storage capacity of 1.65 and 1.04 wt% in the fourth H 2 release, whereas that of NaEr(BH 4 ) 4 continuously decreases. This is mainly assigned to formation of metal hydrides and possibly slower formation of sodium borohydride. The dehydrogenated state clearly contains rare-earth metal borides, which stabilize boron in the dehydrogenated state.

Improvement of energy conversion efficiency and power generation in direct borohydride-hydrogen peroxide fuel cell: The effect of Ni-M core-shell nanoparticles (M = Pt, Pd, Ru)/Multiwalled Carbon Nanotubes on the cell performance

NASA Astrophysics Data System (ADS)

Hosseini, M. G.; Mahmoodi, R.

2017-12-01

In this study, core@shell nanoparticles with Ni as a core material and Pt, Pd and Ru as shell materials are synthesized on multiwalled carbon nanotube (MWCNT) as catalyst support using the sequence reduction method. The influence of Ni@Pt, Ni@Pd and Ni@Ru core@shell nanoparticles on MWCNT toward borohydride oxidation in alkaline solution is investigated by various three-electrode electrochemical techniques. Also, the impact of these anodic electrocatalysts on the performance of direct borohydride-hydrogen peroxide fuel cell (DBHPFC) is evaluated. The structural and morphological properties of electrocatalysts are studied by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), energy-dispersive X-ray spectroscopy (EDX), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HR-TEM) and X-ray photoelectron spectroscopy (XPS). The results of three electrode investigations show that Ni@Pd/MWCNT has excellent catalytic activity since borohydride oxidation current density on Ni@Pd/MWCNT (34773.27 A g-1) is 1.37 and 9.19 times higher than those of Ni@Pt/MWCNT (25347.27 A g-1) and Ni@Ru/MWCNT (3782.83 A g-1), respectively. Also, the energy conversion efficiency and power density of DBHPFC with Ni@Pd/MWCNT (246.82 mW cm-2) increase to 34.27% and 51.53% respect to Ni@Pt/MWCNT (162.24 mW cm-2) and Ni@Ru/MWCNT (119.62 mW cm-2), respectively. This study reveals that Ni@Pd/MWCNT has highest activity toward borohydride oxidation and stability in fuel cell.

Lithium Circuit Test Section Design and Fabrication

NASA Technical Reports Server (NTRS)

Godfroy, Thomas; Garber, Anne

2006-01-01

The Early Flight Fission - Test Facilities (EFF-TF) team has designed and built an actively pumped lithium flow circuit. Modifications were made to a circuit originally designed for NaK to enable the use of lithium that included application specific instrumentation and hardware. Component scale freeze/thaw tests were conducted to both gain experience with handling and behavior of lithium in solid and liquid form and to supply anchor data for a Generalized Fluid System Simulation Program (GFSSP) model that was modified to include the physics for freeze/thaw transitions. Void formation was investigated. The basic circuit components include: reactor segment, lithium to gas heat exchanger, electromagnetic (EM) liquid metal pump, load/drain reservoir, expansion reservoir, instrumentation, and trace heaters. This paper will discuss the overall system design and build and the component testing findings.

Lithium Circuit Test Section Design and Fabrication

NASA Astrophysics Data System (ADS)

Godfroy, Thomas; Garber, Anne; Martin, James

2006-01-01

The Early Flight Fission - Test Facilities (EFF-TF) team has designed and built an actively pumped lithium flow circuit. Modifications were made to a circuit originally designed for NaK to enable the use of lithium that included application specific instrumentation and hardware. Component scale freeze/thaw tests were conducted to both gain experience with handling and behavior of lithium in solid and liquid form and to supply anchor data for a Generalized Fluid System Simulation Program (GFSSP) model that was modified to include the physics for freeze/thaw transitions. Void formation was investigated. The basic circuit components include: reactor segment, lithium to gas heat exchanger, electromagnetic (EM) liquid metal pump, load/drain reservoir, expansion reservoir, instrumentation, and trace heaters. This paper discusses the overall system design and build and the component testing findings.

Alkaline sodium borohydride gel as a hydrogen source for PEMFC or an energy carrier for NaBH 4-air battery

NASA Astrophysics Data System (ADS)

Liu, B. H.; Li, Z. P.; Chen, L. L.

In this preliminary study, we tried to use sodium polyacrylate as the super absorbent polymer to form alkaline NaBH 4 gel and explored its possibilities for borohydride hydrolysis and borohydride electro-oxidation. It was found that the absorption capacity of sodium polyacrylate decreased with increasing NaBH 4 concentration. The formed gel was rather stable in the sealed vessel but tended to slowly decompose in open air. Hydrogen generation from the gel was carried out using CoCl 2 catalyst precursor solutions. Hydrogen generation rate from the alkaline NaBH 4 gel was found to be higher and impurities in hydrogen were less than that from the alkaline NaBH 4 solution. The NaBH 4 gel also successfully powered a NaBH 4-air battery.

Method of synthesizing enriched decaborane for use in generating boron neutron capture therapy pharmaceuticals

DOEpatents

Cowan, Robert L.; Ginosar, Daniel M.; Dunks, Gary B.

2000-01-01

A method is described for synthesizing decaborane wherein at least about 90% of the boron atoms in the decaborane are the .sup.10 B isotope, comprising the steps of: (a) reacting boric acid with a C.sub.1 to C.sub.10 alkanol to form a .sup.10 B-alkyl borate wherein at least about 90% of the boron atoms in the boric acid are the .sup.10 B isotope; (b) reducing the .sup.10 B-alkyl borate to form an alkali metal .sup.10 B-borohydride; (c) converting the alkali metal .sup.10 B-borohydride to a .sup.10 B-tetradecahydroundecaborate ion; and (d) converting the .sup.10 B-tetradecahydroundecaborate ion to .sup.10 B-decaborane. Methods of preparing tetradecahydroundecaborate ions and decaborane from alkali metal borohydrides are also described.

Evidence of ion intercalation mediated band structure modification and opto-ionic coupling in lithium niobite

NASA Astrophysics Data System (ADS)

Shank, Joshua C.; Tellekamp, M. Brooks; Doolittle, W. Alan

2015-01-01

The theoretically suggested band structure of the novel p-type semiconductor lithium niobite (LiNbO2), the direct coupling of photons to ion motion, and optically induced band structure modifications are investigated by temperature dependent photoluminescence. LiNbO2 has previously been used as a memristor material but is shown here to be useful as a sensor owing to the electrical, optical, and chemical ease of lithium removal and insertion. Despite the high concentration of vacancies present in lithium niobite due to the intentional removal of lithium atoms, strong photoluminescence spectra are observed even at room temperature that experimentally confirm the suggested band structure implying transitions from a flat conduction band to a degenerate valence band. Removal of small amounts of lithium significantly modifies the photoluminescence spectra including additional larger than stoichiometric-band gap features. Sufficient removal of lithium results in the elimination of the photoluminescence response supporting the predicted transition from a direct to indirect band gap semiconductor. In addition, non-thermal coupling between the incident laser and lithium ions is observed and results in modulation of the electrical impedance.

Effects of organic silicon compounds as additives on charge-discharge cycling efficiencies of lithium in nonaqueous electrolytes for rechargeable lithium cells

NASA Astrophysics Data System (ADS)

Yanagisawa, Ryota; Endo, Hisayuki; Unno, Masafumi; Morimoto, Hideyuki; Tobishima, Shin-ichi

2014-11-01

Influence of mixing organic silicon compounds into 1 M (M: mol L-1) LiPF6-ethylene carbonate (EC)/ethylmethyl carbonate (EMC) (mixing volume ratio = 3:7) mixed solvent electrolytes on charge-discharge cycling efficiencies of lithium metal negative electrodes is examined. As organic silicon compounds, polyether-modified siloxanes with polyethylene oxide chains, chlorotrimethylsilane, tetraethoxysilane, cis-tetra [isobutyl (dimethylsiloxy)] cyclotetrasiloxane and cage-type silsesquioxane are investigated. Charge-discharge cycling tests of lithium are galvanostatically carried out using stainless steel working electrodes. Charge-discharge cycling efficiencies of lithium tend to improve by mixing organic silicon compounds. A cage-type silsesquioxane, octaphenyloctasilsesquioxane (Ph8T8) exhibits the highest cycling efficiency of approximately 80% with small mixing amount of 0.02 M Ph8T8. Mechanism of enhancement of lithium cycling efficiencies by mixing organic silicon compounds is considered to be due to the suppression of excess reduction of LiPF6-EC/EMC by lithium and the growth of surface film on lithium.

Self-standing elastomeric composites based on lithium ferrites and their dielectric behavior

DOE Office of Scientific and Technical Information (OSTI.GOV)

Soreto Teixeira, S.; Graça, M. P. F.; Costa, L. C.

2014-12-14

Lithium ferrite (LiFe{sub 5}O{sub 8}) is an attractive material for technological applications due to its physical properties, which are significantly dependent on the preparation method and raw materials. In this work, LiFe{sub 5}O{sub 8} crystallites were obtained by controlled heat-treatment process at 1100 °C, of a homogeneous mixture of Li{sub 2}O-Fe{sub 2}O{sub 3} powders, prepared by wet ball-milling and using lithium and iron nitrates as raw materials. The main goal was the preparation of a flexible and self-standing tick composite film by embedding lithium ferrite particles in a polymeric matrix, taking advantage of the good mechanical properties of the polymer andmore » of the electrical and dielectric properties of the ferrite. The selected polymer matrix was styrene-b-isoprene-b-styrene copolymer. To prepare the composites, the lithium ferrite particles were chemically modified in order to functionalize their surface. To analyse the influence of the particles surface modification, different composites were made, with modified and unmodified particles. The structure of the obtained composites was studied by FTIR, XRD, TGA, and DSC techniques. The dielectric properties were analysed, in the frequency range between 10 Hz and 1 MHz and in function of temperature in the range between −73 °C and 127 °C. These properties were related with the structure and concentration of the particles in the matrix network. The composites with the modified particles present higher dielectric constant, maintaining values of loss tangent sufficiently low (<10{sup −2}) that can be considered interesting for technological applications.« less

Freeze-drying synthesis of three-dimensional porous LiFePO4 modified with well-dispersed nitrogen-doped carbon nanotubes for high-performance lithium-ion batteries

NASA Astrophysics Data System (ADS)

Tu, Xiaofeng; Zhou, Yingke; Song, Yijie

2017-04-01

The three-dimensional porous LiFePO4 modified with uniformly dispersed nitrogen-doped carbon nanotubes has been successfully prepared by a freeze-drying method. The morphology and structure of the porous composites are characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS), and the electrochemical performances are evaluated using the constant current charge/discharge tests, cyclic voltammetry and electrochemical impedance spectroscopy. The nitrogen-doped carbon nanotubes are uniformly dispersed inside the porous LiFePO4 to construct a superior three-dimensional conductive network, which remarkably increases the electronic conductivity and accelerates the diffusion of lithium ion. The porous composite displays high specific capacity, good rate capability and excellent cycling stability, rendering it a promising positive electrode material for high-performance lithium-ion batteries.

Evaluation of anode (electro)catalytic materials for the direct borohydride fuel cell: Methods and benchmarks

NASA Astrophysics Data System (ADS)

Olu, Pierre-Yves; Job, Nathalie; Chatenet, Marian

2016-09-01

In this paper, different methods are discussed for the evaluation of the potential of a given catalyst, in view of an application as a direct borohydride fuel cell DBFC anode material. Characterizations results in DBFC configuration are notably analyzed at the light of important experimental variables which influence the performances of the DBFC. However, in many practical DBFC-oriented studies, these various experimental variables prevent one to isolate the influence of the anode catalyst on the cell performances. Thus, the electrochemical three-electrode cell is a widely-employed and useful tool to isolate the DBFC anode catalyst and to investigate its electrocatalytic activity towards the borohydride oxidation reaction (BOR) in the absence of other limitations. This article reviews selected results for different types of catalysts in electrochemical cell containing a sodium borohydride alkaline electrolyte. In particular, propositions of common experimental conditions and benchmarks are given for practical evaluation of the electrocatalytic activity towards the BOR in three-electrode cell configuration. The major issue of gaseous hydrogen generation and escape upon DBFC operation is also addressed through a comprehensive review of various results depending on the anode composition. At last, preliminary concerns are raised about the stability of potential anode catalysts upon DBFC operation.

Spontaneous synthesis of gold nanoparticles on gum arabic-modified iron oxide nanoparticles as a magnetically recoverable nanocatalyst.

PubMed

Wu, Chien-Chen; Chen, Dong-Hwang

2012-06-19

A novel magnetically recoverable Au nanocatalyst was fabricated by spontaneous green synthesis of Au nanoparticles on the surface of gum arabic-modified Fe3O4 nanoparticles. A layer of Au nanoparticles with thickness of about 2 nm was deposited on the surface of gum arabic-modified Fe3O4 nanoparticles, because gum arabic acted as a reducing agent and a stabilizing agent simultaneously. The resultant magnetically recoverable Au nanocatalyst exhibited good catalytic activity for the reduction of 4-nitrophenol with sodium borohydride. The rate constants evaluated in terms of pseudo-first-order kinetic model increased with increase in the amount of Au nanocatalyst or decrease in the initial concentration of 4-nitrophenol. The kinetic data suggested that this catalytic reaction was diffusion-controlled, owing to the presence of gum arabic layer. In addition, this nanocatalyst exhibited good stability. Its activity had no significant decrease after five recycles. This work is useful for the development and application of magnetically recoverable Au nanocatalyst on the basis of green chemistry principles.

Spontaneous synthesis of gold nanoparticles on gum arabic-modified iron oxide nanoparticles as a magnetically recoverable nanocatalyst

PubMed Central

2012-01-01

A novel magnetically recoverable Au nanocatalyst was fabricated by spontaneous green synthesis of Au nanoparticles on the surface of gum arabic-modified Fe3O4 nanoparticles. A layer of Au nanoparticles with thickness of about 2 nm was deposited on the surface of gum arabic-modified Fe3O4 nanoparticles, because gum arabic acted as a reducing agent and a stabilizing agent simultaneously. The resultant magnetically recoverable Au nanocatalyst exhibited good catalytic activity for the reduction of 4-nitrophenol with sodium borohydride. The rate constants evaluated in terms of pseudo-first-order kinetic model increased with increase in the amount of Au nanocatalyst or decrease in the initial concentration of 4-nitrophenol. The kinetic data suggested that this catalytic reaction was diffusion-controlled, owing to the presence of gum arabic layer. In addition, this nanocatalyst exhibited good stability. Its activity had no significant decrease after five recycles. This work is useful for the development and application of magnetically recoverable Au nanocatalyst on the basis of green chemistry principles. PMID:22713480

Thermomechanical treatment of welded joints of aluminum-lithium alloys modified by scandium

NASA Astrophysics Data System (ADS)

Malikov, A. G.

2017-12-01

At present, the aeronautical equipment manufacture involves up-to-date high-strength aluminum alloys of decreased density resulting from the lithium admixture. Various technologies of fusible welding of these alloys are being developed. The paper presents experimental investigations of the optimization of the laser welding of aluminum alloys with the scandium-modified welded joint after thermomechanical treatment. The effect of scandium on the micro- and macrostructure is studied along with strength characteristics of the welded joint. It is found that thermomechanical treatment allows us to obtain the strength of the welded joint 0.89 for the Al-Mg-Li system and 0.99 for the Al-Cu-Li system with the welded joint modified by scandium in comparison with the base alloy after treatment.

Anode Improvement in Rechargeable Lithium-Sulfur Batteries.

PubMed

Tao, Tao; Lu, Shengguo; Fan, Ye; Lei, Weiwei; Huang, Shaoming; Chen, Ying

2017-12-01

Owing to their theoretical energy density of 2600 Wh kg -1 , lithium-sulfur batteries represent a promising future energy storage device to power electric vehicles. However, the practical applications of lithium-sulfur batteries suffer from poor cycle life and low Coulombic efficiency, which is attributed, in part, to the polysulfide shuttle and Li dendrite formation. Suppressing Li dendrite growth, blocking the unfavorable reaction between soluble polysulfides and Li, and improving the safety of Li-S batteries have become very important for the development of high-performance lithium sulfur batteries. A comprehensive review of various strategies is presented for enhancing the stability of the anode of lithium sulfur batteries, including inserting an interlayer, modifying the separator and electrolytes, employing artificial protection layers, and alternative anodes to replace the Li metal anode. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Density functional theory based screening of ternary alkali-transition metal borohydrides: A computational material design project

NASA Astrophysics Data System (ADS)

Hummelshøj, J. S.; Landis, D. D.; Voss, J.; Jiang, T.; Tekin, A.; Bork, N.; Dułak, M.; Mortensen, J. J.; Adamska, L.; Andersin, J.; Baran, J. D.; Barmparis, G. D.; Bell, F.; Bezanilla, A. L.; Bjork, J.; Björketun, M. E.; Bleken, F.; Buchter, F.; Bürkle, M.; Burton, P. D.; Buus, B. B.; Calborean, A.; Calle-Vallejo, F.; Casolo, S.; Chandler, B. D.; Chi, D. H.; Czekaj, I.; Datta, S.; Datye, A.; DeLaRiva, A.; Despoja, V.; Dobrin, S.; Engelund, M.; Ferrighi, L.; Frondelius, P.; Fu, Q.; Fuentes, A.; Fürst, J.; García-Fuente, A.; Gavnholt, J.; Goeke, R.; Gudmundsdottir, S.; Hammond, K. D.; Hansen, H. A.; Hibbitts, D.; Hobi, E.; Howalt, J. G.; Hruby, S. L.; Huth, A.; Isaeva, L.; Jelic, J.; Jensen, I. J. T.; Kacprzak, K. A.; Kelkkanen, A.; Kelsey, D.; Kesanakurthi, D. S.; Kleis, J.; Klüpfel, P. J.; Konstantinov, I.; Korytar, R.; Koskinen, P.; Krishna, C.; Kunkes, E.; Larsen, A. H.; Lastra, J. M. G.; Lin, H.; Lopez-Acevedo, O.; Mantega, M.; Martínez, J. I.; Mesa, I. N.; Mowbray, D. J.; Mýrdal, J. S. G.; Natanzon, Y.; Nistor, A.; Olsen, T.; Park, H.; Pedroza, L. S.; Petzold, V.; Plaisance, C.; Rasmussen, J. A.; Ren, H.; Rizzi, M.; Ronco, A. S.; Rostgaard, C.; Saadi, S.; Salguero, L. A.; Santos, E. J. G.; Schoenhalz, A. L.; Shen, J.; Smedemand, M.; Stausholm-Møller, O. J.; Stibius, M.; Strange, M.; Su, H. B.; Temel, B.; Toftelund, A.; Tripkovic, V.; Vanin, M.; Viswanathan, V.; Vojvodic, A.; Wang, S.; Wellendorff, J.; Thygesen, K. S.; Rossmeisl, J.; Bligaard, T.; Jacobsen, K. W.; Nørskov, J. K.; Vegge, T.

2009-07-01

We present a computational screening study of ternary metal borohydrides for reversible hydrogen storage based on density functional theory. We investigate the stability and decomposition of alloys containing 1 alkali metal atom, Li, Na, or K (M1); and 1 alkali, alkaline earth or 3d/4d transition metal atom (M2) plus two to five (BH4)- groups, i.e., M1M2(BH4)2-5, using a number of model structures with trigonal, tetrahedral, octahedral, and free coordination of the metal borohydride complexes. Of the over 700 investigated structures, about 20 were predicted to form potentially stable alloys with promising decomposition energies. The M1(Al/Mn/Fe)(BH4)4, (Li/Na)Zn(BH4)3, and (Na/K)(Ni/Co)(BH4)3 alloys are found to be the most promising, followed by selected M1(Nb/Rh)(BH4)4 alloys.

Compact solid source of hydrogen gas

DOEpatents

Kravitz, Stanley H.; Hecht, Andrew M.; Sylwester, Alan P.; Bell, Nelson S.

2004-06-08

A compact solid source of hydrogen gas, where the gas is generated by contacting water with micro-disperse particles of sodium borohydride in the presence of a catalyst, such as cobalt or ruthenium. The micro-disperse particles can have a substantially uniform diameter of 1-10 microns, and preferably about 3-5 microns. Ruthenium or cobalt catalytic nanoparticles can be incorporated in the micro-disperse particles of sodium borohydride, which allows a rapid and complete reaction to occur without the problems associated with caking and scaling of the surface by the reactant product sodium metaborate. A closed loop water management system can be used to recycle wastewater from a PEM fuel cell to supply water for reacting with the micro-disperse particles of sodium borohydride in a compact hydrogen gas generator. Capillary forces can wick water from a water reservoir into a packed bed of micro-disperse fuel particles, eliminating the need for using an active pump.

Effect of groove width of modified current collector on internal short circuit of abused lithium-ion battery

NASA Astrophysics Data System (ADS)

Wang, Meng; Shi, Yang; Noelle, Daniel J.; Le, Anh V.; Qiao, Yu

2017-10-01

In a lithium-ion battery (LIB), mechanical abuse often leads to internal short circuits (ISC) that trigger thermal runaway. We investigated a thermal-runaway mitigation (TRM) technique using a modified current collector. By generating surface grooves on the current collector, the area of electrodes directly involved in ISC could be largely reduced, which decreased the ISC current. The TRM mechanism took effect immediately after the LIB was damaged. The testing data indicate that the groove width is a critical factor. With optimized groove width, this technique may enable robust and multifunctional design of LIB cells for large-scale energy-storage units.

Free-standing sulfur host based on titanium-dioxide-modified porous-carbon nanofibers for lithium-sulfur batteries

NASA Astrophysics Data System (ADS)

Song, Xiong; Gao, Tuo; Wang, Suqing; Bao, Yue; Chen, Guoping; Ding, Liang-Xin; Wang, Haihui

2017-07-01

Lithium-sulfur (Li-S) batteries are regarded as a promising next-generation electrical-energy-storage technology due to their low cost and high theoretical energy density. Furthermore, flexible and wearable electronics urgently requires their power sources to be mechanically robust and flexible. However, the effective progress of high-performance, flexible Li-S batteries is still hindered by the poor conductivity of sulfur cathodes and the dissolution of lithium polysulfides as well as the weak mechanical properties of sulfur cathodes. Herein, a new type of flexible porous carbon nanofiber film modified with graphene and ultrafine polar TiO2 nanoparticles is designed as a sulfur host, in which the artful structure enabled the highly efficient dispersion of sulfur for a high capacity and a strong confinement capability of lithium polysulfides, resulting in prolonged cycle life. Thus, the cathode shows an extremely high initial specific discharge capacity of 1501 mA h g-1 at 0.1 C and an excellent rate capability of 668 mA h g-1 at 5 C as well as prolonged cycling stability. The artful design provides a facile method to fabricate high-performance, flexible sulfur cathodes for Li-S batteries.

Inhibiting polysulfides diffusion of lithium-sulfur batteries using an acetylene black-CoS2 modified separator: Mechanism research and performance improvement

NASA Astrophysics Data System (ADS)

Zeng, Pan; Huang, Liwu; Zhang, Xinling; Han, Yamiao; Chen, Yungui

2018-01-01

Lithium-sulfur (Li-S) batteries are considered as one of the most promising chemistries in secondary energy storage field owing to their high energy density. However, the poor electrochemical performance mainly associated with the polysulfides shuttle has greatly hampered their practical application. Herein, a simple acetylene black (AB)-CoS2 coated separator is first designed to suppress the migration of polysulfides. The AB-CoS2 modified separator can not only efficiently capture the polysulfides by forming strong chemical bonding but also guarantee the rapid lithium ions diffusion. Moreover, the AB-CoS2 coating could serve as an upper current collector to accelerate electron transport for reinforcing the utilization of sulfur and ensuring the reactivation of the trapped active material. Consequently, the Li-S cell using AB-CoS2 modified separator shows a long-term cycling stability with an extremely low decay rate (0.09% per cycle) up to 450 cycles at a high rate of 2 C (3350 mA g-1). It also exhibits excellent rate capabilities, which maintains a capacity of 475 mAh g-1 even at 4.0 C rate.

A green synthesis of a layered titanate, potassium lithium titanate; lower temperature solid-state reaction and improved materials performance

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ogawa, Makoto, E-mail: waseda.ogawa@gmail.com; Department of Earth Sciences, Waseda University, 1-6-1 Nishiwaseda, Shinjuku-ku, Tokyo 169-8050; Morita, Masashi, E-mail: m-masashi@y.akane.waseda.jp

2013-10-15

A layered titanate, potassium lithium titanate, with the size range from 0.1 to 30 µm was prepared to show the effects of the particle size on the materials performance. The potassium lithium titanate was prepared by solid-state reaction as reported previously, where the reaction temperature was varied. The reported temperature for the titanate preparation was higher than 800 °C, though 600 °C is good enough to obtain single-phase potassium lithium titanate. The lower temperature synthesis is cost effective and the product exhibit better performance as photocatalysts due to surface reactivity. - Graphical abstract: Finite particle of a layered titanate, potassiummore » lithium titanate, was prepared by solid-state reaction at lower temperature to show modified materials performance. Display Omitted - Highlights: • Potassium lithium titanate was prepared by solid-state reaction. • Lower temperature reaction resulted in smaller sized particles of titanate. • 600 °C was good enough to obtain single phased potassium lithium titanate. • The product exhibited better performance as photocatalyst.« less

Effect of halideions on the surface-enhanced Raman spectroscopy of methylene blue for borohydride-reduced silver colloid

NASA Astrophysics Data System (ADS)

Dong, Xiao; Gu, Huaimin; Liu, Fang

2011-01-01

The surface enhanced Raman scattering (SERS) spectrum of methylene blue (MB) was studied when adding a range of halideions to borohydride-reduced silver colloid. The halideions such as chloride, bromide and iodide were added as aggregating agents to study the effects of halideions on SERS spectroscopy of MB and observe which halideion gives the greatest enhancement for borohydride-reduced silver colloids. The SERS spectra of MB were also detected over a wide range of concentrations of halideions to find the optimum concentration of halideions for SERS enhancement. From the results of this study, the intensity of SERS signal of MB was enhanced significantly when adding halideions to the colloid. Among the three kinds of halideions, chloride gives the greatest enhancement on SERS signal. The enhancement factors for MB with optimal concentration of chloride, bromide and iodide are 3.44×104, 2.04×104, and 1.0×104, respectively. The differences of the SERS spectra of MB when adding different kinds and concentrations of halideions to the colloid may be attributed to the both effects of extent of aggregation of the colloid and the modification of silver surface chemistry. The purpose of this study is to further investigate the effect of halideions on borohydride-reduced silver colloid and to make the experimental conditions suitable for detecting some analytes in high efficiency on rational principles.

Metastable structure of Li13Si4

NASA Astrophysics Data System (ADS)

Gruber, Thomas; Bahmann, Silvia; Kortus, Jens

2016-04-01

The Li13Si4 phase is one out of several crystalline lithium silicide phases, which is a potential electrode material for lithium ion batteries and contains a high theoretical specific capacity. By means of ab initio methods like density functional theory (DFT) many properties such as heat capacity or heat of formation can be calculated. These properties are based on the calculation of phonon frequencies, which contain information about the thermodynamical stability. The current unit cell of "Li13Si4" given in the ICSD database is unstable with respect to DFT calculations. We propose a modified unit cell that is stable in the calculations. The evolutionary algorithm EVO found a structure very similar to the ICSD one with both of them containing metastable lithium positions. Molecular dynamic simulations show a phase transition between both structures where these metastable lithium atoms move. This phase transition is achieved by a very fast one-dimensional lithium diffusion and stabilizes this phase.

A new family of metal borohydride guanidinate complexes: Synthesis, structures and hydrogen-storage properties

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wu, Hui, E-mail: huiwu@nist.gov; Zhou, Xiuquan; Rodriguez, Efrain E.

We report on a new class of complex hydrides: borohydride guanidinate complexes (MBH{sub 4}·nCN{sub 3}H{sub 5}, M=Li, Mg, and Ca). They can be prepared via facile solid-state synthesis routes. Their crystal structures were successfully determined using a combination of X-ray diffraction, first-principles calculations and neutron vibrational spectroscopy. Among these compounds, Mg(BH{sub 4}){sub 2}·6CN{sub 3}H{sub 5} is composed of large complex Mg[CN{sub 3}H{sub 5}]{sub 6}{sup 2+} cations and surrounding BH{sub 4}{sup -} ions, while Ca(BH{sub 4}){sub 2}·2CN{sub 3}H{sub 5} possesses layers of corner-sharing Ca[BH{sub 4}]{sub 4}(CN{sub 3}H{sub 5}){sub 2} octahedra. Our dehydrogenation results show that ≈10 wt% hydrogen can be releasedmore » from MBH{sub 4}·nCN{sub 3}H{sub 5} (M=Li, Mg, and Ca) at moderate temperatures with minimal ammonia and diborane contamination thanks to the synergistic effect of C-N bonds from guanidine and hydridic H from borohydrides leading to a weakening of the N-H bonds, thus impeding ammonia gas liberation. Further tuning the dehydrogenation with different cation species indicates that Mg(BH{sub 4}){sub 2}·nCN{sub 3}H{sub 5} can exhibit the optimum properties with nearly thermally neutral dehydrogenation and very high purity hydrogen release. - Graphical abstract: A new family of complex hydrides: borohydride guanidinates, was developed with diverse crystal structures and remarkable hydrogen storage properties. - Highlights: • A new family of complex hydrides, borohydride guanidinate complexes, are synthesized. • Their diverse crystal structures are determined using combined characterizations. • These compounds can release ~10 wt% pure H{sub 2} at moderate temperatures. • Dehydrogenation thermodynamics and H{sub 2} purity can be tuned by varying cation species.« less

Sponge-like reduced graphene oxide/silicon/carbon nanotube composites for lithium ion batteries

NASA Astrophysics Data System (ADS)

Fang, Menglu; Wang, Zhao; Chen, Xiaojun; Guan, Shiyou

2018-04-01

Three-dimensional sponge-like reduced graphene oxide/silicon/carbon nanotube composites were synthesized by one-step hydrothermal self-assembly using silicon nanoparticles, graphene oxide and amino modified carbon nanotubes to develop high-performance anode materials of lithium ion batteries. Scanning electron microscopy and transmission electron microscopy images show the structure of composites that Silicon nanoparticles are coated with reduced graphene oxide while amino modified carbon nanotubes wrap around the reduced graphene oxide in the composites. When applied to lithium ion battery, these composites exhibit high initial specific capacity of 2552 mA h/g at a current density of 0.05 A/g. In addition, reduced graphene oxide/silicon/carbon nanotube composites also have better cycle stability than bare Silicon nanoparticles electrode with the specific capacity of 1215 mA h/g after 100 cycles. The three-dimension sponge-like structure not only ensures the electrical conductivity but also buffers the huge volume change, which has broad potential application in the field of battery.

Regenerable antioxidants-introduction of chalcogen substituents into tocopherols.

PubMed

Poon, Jia-Fei; Singh, Vijay P; Yan, Jiajie; Engman, Lars

2015-02-02

To improve the radical-trapping capacity of the natural antioxidants, alkylthio-, alkylseleno-, and alkyltelluro groups were introduced into all vacant aromatic positions in β-, γ- and δ-tocopherol. Reaction of the tocopherols with electrophilic chalcogen reagents generated by persulfate oxidation of dialkyl dichalcogenides provided convenient but low-yielding access to many sulfur and selenium derivatives, but failed in the case of tellurium. An approach based on lithiation of the appropriate bromo-tocopherol, insertion of chalcogen into the carbon-lithium bond, air-oxidation to a dichalcogenide, and final borohydride reduction/alkylation turned out to be generally applicable to the synthesis of all chalcogen derivatives. Whereas alkylthio- and alkylseleno analogues were generally poorer quenchers of lipid peroxyl radicals than the corresponding parents, all tellurium compounds showed a substantially improved radical-trapping activity. Introduction of alkyltelluro groups into the tocopherol scaffold also caused a dramatic increase in the regenerability of the antioxidant. In a two-phase lipid peroxidation system containing N-acetylcysteine as a water-soluble co-antioxidant the inhibition time was up to six-fold higher than that recorded for the natural antioxidants. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

An all-solid-state lithium/polyaniline rechargeable cell

NASA Astrophysics Data System (ADS)

Li, Changzhi; Peng, Xinsheng; Zhang, Borong; Wang, Baochen

1992-07-01

The performance of an all-solid-state cell having a lithium negative electrode, a modified polyethylene oxide (PEO)-epoxy resin (ER) electrolyte, and a polyaniline (PAn) positive electrode has been studied using cyclic voltammetry, charge/discharge cycling, and polarization curves at various temperatures. The redox reaction of the PAn electrode at the PAn/modified PEO-ER interface exhibits good reversibility. At 50-80 C, the Li/PEO-ER-LiClO4/PAn cell shows more than 40 charge/discharge cycles, 90 percent charge/discharge efficiency, and 54 W h kg discharge energy density (on PAn weight basis) at 50 micro-A between 2 and 4 V. The polarization performance of the battery improves steadily with increase in temperature.

Investigation of oxygen reduction and methanol oxidation reaction activity of PtAu nano-alloy on surface modified porous hybrid nanocarbon supports

NASA Astrophysics Data System (ADS)

Parambath Vinayan, Bhaghavathi; Nagar, Rupali; Ramaprabhu, Sundara

2016-09-01

We investigate the electrocatalytic activity of PtAu alloy nanoparticles supported on various chemically modified carbon morphologies towards oxygen reduction reaction (ORR) and methanol oxidation reaction (MOR). The surface-modification of graphene nanosheets (f-G), multi-walled carbon nanotubes (f-MWNTs) and (graphene nanosheets-carbon nanotubes) hybrid support (f-G-MWNTs) were carried out by soft functionalization method using a cationic polyelectrolyte poly-(diallyldimethyl ammonium chloride). The Pt and PtAu alloy nanoparticles were dispersed over chemically modified carbon supports by sodium-borohydride assisted modified polyol reduction method. The electrochemical performance of all electrocatalysts were studied by half- and full-cell proton exchange membrane fuel cell (PEMFC) measurements and PtAu/f-G-MWNTs catalyst comparatively yielded the best catalytic performance. PEMFC full cell measurements of PtAu/f-G-MWNTs cathode electrocatalyst yield a maximum power density of 319 mW cm-2 at 60 °C without any back pressure,which is 2.1 times higher than that of cathode electrocatalyst Pt on graphene support. The high ORR and MOR activity of PtAu/f-G-MWNTs electrocatalyst is due to the alloying effect and inherent beneficial properties of porous hybrid nanocarbon support.

Spectroscopic study of surface enhanced Raman scattering of caffeine on borohydride-reduced silver colloids

NASA Astrophysics Data System (ADS)

Chen, Xiaomin; Gu, Huaimin; Shen, Gaoshan; Dong, Xiao; Kang, Jian

2010-06-01

The surface enhanced Raman scattering (SERS) of caffeine on borohydride-reduced silver colloids system under different aqueous solution environment has been studied in this paper. The relative intensity of SERS of caffeine significantly varies with different concentrations of sodium chloride and silver particles. However, at too high or too low concentration of sodium chloride and silver particle, the enhancement of SERS spectra is not evident. The SERS spectra of caffeine suggest that the contribution of the charge transfer mechanism to SERS may be dominant. The chloride ions can significantly enhance the efficiency of SERS, while the enhancement is selective, as the efficiency in charge transfer enhancement is higher than in electromagnetic enhancement. Therefore, it can be concluded that the active site of chloride ion locates on the bond between the caffeine and the silver surface. In addition, the SERS spectra of caffeine on borohydride-reduced and citrate-reduced silver colloids are different, which may be due to different states caffeine adsorbed on silver surface under different silver colloids.

Lithium Ion Recognition with Nanofluidic Diodes through Host-Guest Complexation in Confined Geometries.

PubMed

Ali, Mubarak; Ahmed, Ishtiaq; Ramirez, Patricio; Nasir, Saima; Mafe, Salvador; Niemeyer, Christof M; Ensinger, Wolfgang

2018-05-15

The lithium ion recognition is receiving significant attention because of its application in pharmaceuticals, lubricants and, especially, in energy technology. We present a nanofluidic device for specific lithium ion recognition via host-guest complexation in a confined environment. A lithium-selective receptor molecule, the aminoethyl-benzo-12-crown-4 (BC12C4-NH 2 ), is designed and functionalized on single conical nanopores in polyethylene terephthalate (PET) membranes. The native carboxylic acid groups on the pore walls are covalently linked with the crown ether moieties and the process is monitored from the changes in the current-voltage ( I- V) curves. The B12-crown-4 moieties are known to specifically bind with lithium ions and when the modified pore is exposed to different alkali metal chloride solutions separately, significant changes in the ion current and rectification are only observed for lithium chloride. This fact suggests the generation of positively charged B12C4-Li + complexes on the pore surface. Furthermore, the nanofluidic diode is able to recognize the lithium ion even in the presence of high concentrations of potassium ions in the external electrolyte solution. Thus, this nanodevice suggests a strategy to miniaturize nanofluidic porous systems for efficient recognition, extraction, and separation of lithium from raw materials.

Protective effects of long-term lithium administration in a slowly progressive SMA mouse model.

PubMed

Biagioni, Francesca; Ferrucci, Michela; Ryskalin, Larisa; Fulceri, Federica; Lazzeri, Gloria; Calierno, Maria Teresa; Busceti, Carla L; Ruffoli, Riccardo; Fornai, Francesco

2017-12-01

In the present study we evaluated the long-term effects of lithium administration to a knock-out double transgenic mouse model (Smn-/-; SMN1A2G+/-; SMN2+/+) of Spinal Muscle Atrophy type III (SMA-III). This model is characterized by very low levels of the survival motor neuron protein, slow disease progression and motor neuron loss, which enables to detect disease-modifying effects at delayed time intervals. Lithium administration attenuates the decrease in motor activity and provides full protection from motor neuron loss occurring in SMA-III mice, throughout the disease course. In addition, lithium prevents motor neuron enlargement and motor neuron heterotopy and suppresses the occurrence of radial-like glial fibrillary acidic protein immunostaining in the ventral white matter of SMA-III mice. In SMA-III mice long-term lithium administration determines a dramatic increase of survival motor neuron protein levels in the spinal cord. These data demonstrate that long-term lithium administration during a long-lasting motor neuron disorder attenuates behavioural deficit and neuropathology. Since low level of survival motor neuron protein is bound to disease severity in SMA, the robust increase in protein level produced by lithium provides solid evidence which calls for further investigations considering lithium in the long-term treatment of spinal muscle atrophy.

Lithium, but not Valproate, Reduces Impulsive Choice in the Delay-Discounting Task in Mice

PubMed Central

Halcomb, Meredith E; Gould, Todd D; Grahame, Nicholas J

2013-01-01

Both lithium and valproate are well-established treatments for bipolar disorder. Studies have also found that lithium is effective at reducing suicidal behaviors in patients with mood disorders. Impulsivity is a validated endophenotype of both bipolar disorder and suicidal behavior. We assessed effects of treatment with lithium or valproate on cognitive impulsivity in selectively bred mice previously shown to manifest relatively high levels of cognitive impulsivity. Mice were trained in the delay-discounting paradigm, a measure of cognitive impulsivity reflecting a behavioral bias towards immediacy, and then treated with lithium, valproate, or control chow. After 3 weeks of drug treatment, mice were tested at various delays to a large, delayed reward. Drug treatment continued during this time. Lithium reduced impulsivity, whereas valproate had no effect on choice behavior. Both drugs increased the number of choice trials and reinforcer intake, but effects on choice behavior did not depend on these motivational changes. To our knowledge, this is the first study demonstrating lithium's effects to reduce cognitive impulsivity. Future studies may focus on the ability of putative pharmacotherapies for patients at risk for bipolar disorder or suicide to modify the impulsive choice dimension of this diseases. PMID:23584261

Dendrite-Suppressed Lithium Plating from a Liquid Electrolyte via Wetting of Li 3N

DOE Office of Scientific and Technical Information (OSTI.GOV)

Park, Kyusung; Goodenough, John B.

Lithium metal is an ultimate anode material to provide the highest energy density for a given cathode by providing a higher capacity and cell voltage. However, lithium is not used as the anode in commercial lithium-ion batteries because electrochemical dendrite formation and growth during charge can induce a cell short circuit that ignites the flammable liquid electrolyte. Plating of lithium through a bed of Li 3N particles is shown to transform dendrite growth into a 3D lithium network formed by wetting the particle surfaces; plating through a Li 3N particle is without dendrite nucleation. The Li 3N particles create amore » higher overpotential during Li deposition than that with dendrite growth in galvanostatic charge/discharge tests. The characteristic overpotential increase is correlated with the morphological changes and a more isotropic growth behavior. The Li 3N-modified Li electrode shows a stable cycling performance at 0.5 and 1.0 mA cm -2 for more than 100 cycles. In this paper, the origin of the bonding responsible for wetting of the Li 3N particles by lithium and for plating through a Li 3N particle is discussed.« less

Dendrite-Suppressed Lithium Plating from a Liquid Electrolyte via Wetting of Li 3N

DOE PAGES

Park, Kyusung; Goodenough, John B.

2017-07-10

Lithium metal is an ultimate anode material to provide the highest energy density for a given cathode by providing a higher capacity and cell voltage. However, lithium is not used as the anode in commercial lithium-ion batteries because electrochemical dendrite formation and growth during charge can induce a cell short circuit that ignites the flammable liquid electrolyte. Plating of lithium through a bed of Li 3N particles is shown to transform dendrite growth into a 3D lithium network formed by wetting the particle surfaces; plating through a Li 3N particle is without dendrite nucleation. The Li 3N particles create amore » higher overpotential during Li deposition than that with dendrite growth in galvanostatic charge/discharge tests. The characteristic overpotential increase is correlated with the morphological changes and a more isotropic growth behavior. The Li 3N-modified Li electrode shows a stable cycling performance at 0.5 and 1.0 mA cm -2 for more than 100 cycles. In this paper, the origin of the bonding responsible for wetting of the Li 3N particles by lithium and for plating through a Li 3N particle is discussed.« less

Chloride-Reinforced Carbon Nanofiber Host as Effective Polysulfide Traps in Lithium-Sulfur Batteries.

PubMed

Fan, Lei; Zhuang, Houlong L; Zhang, Kaihang; Cooper, Valentino R; Li, Qi; Lu, Yingying

2016-12-01

Lithium-sulfur (Li-S) battery is one of the most promising alternatives for the current state-of-the-art lithium-ion batteries due to its high theoretical energy density and low production cost from the use of sulfur. However, the commercialization of Li-S batteries has been so far limited to the cyclability and the retention of active sulfur materials. Using co-electrospinning and physical vapor deposition procedures, we created a class of chloride-carbon nanofiber composites, and studied their effectiveness on polysulfides sequestration. By trapping sulfur reduction products in the modified cathode through both chemical and physical confinements, these chloride-coated cathodes are shown to remarkably suppress the polysulfide dissolution and shuttling between lithium and sulfur electrodes. From adsorption experiments and theoretical calculations, it is shown that not only the sulfide-adsorption effect but also the diffusivity in the vicinity of these chlorides materials plays an important role on the reversibility of sulfur-based cathode upon repeated cycles. Balancing the adsorption and diffusion effects of these nonconductive materials could lead to the enhanced cycling performance of an Li-S cell. Electrochemical analyses over hundreds of cycles indicate that cells containing indium chloride-modified carbon nanofiber outperform cells with other halogenated salts, delivering an average specific capacity of above 1200 mAh g -1 at 0.2 C.

Vapor Pressure Measurements of LiBH4, NaBH 4 and Ca(BH4)2 using Knudsen Torsion Effusion Gravimetric Method

NASA Astrophysics Data System (ADS)

Danyan, Mohammad Masoumi

Hydrogen storage is one of the critical technologies needed on the path towards commercialization for mobile applications. In the past few years, a range of new light weight hydrogen containing material has been discovered with good storage properties. Among them, lithium borohydride (LiBH 4) sodium borohydride (NaBH4) and calcium borohydride (Ca(BH 4)2) have shown promising results to be used as solid state hydrogen storage material. In this work, we have determined equilibrium vapor pressures of LiBH 4 NaBH4 and Ca(BH4)2 obtained by Torsion effusion thermogravimetric method. Results for all the three hydrides exhibited that a small fraction of the materials showed congruency, and sublimed as gaseous compound, but the majority of the material showed incongruent vaporization. Two Knudsen cells of 0.3 and 0.6mm orifice size was employed to measure the total vapor pressures. A Whitman-Motzfeldt method is used to extrapolate the measured vapor pressures to zero orifice size to calculate the equilibrium vapor pressures. In the case of LiBH4 we found that 2% of the material evaporated congruently (LiBH4(s) → LiBH4(g)) according to the equation: logPLiBH4/P 0 =-3263.5 +/-309/T + (1.079 +/-0.69) and rest as incongruent vaporization to LiH, B, and hydrogen gas according to the equation logPeq/P0 =(-3263.5 +/-309)/T+ (2.458 +/-0.69) with DeltaH evap.= 62.47+/-5.9 kJ/mol of H2, DeltaSevap. = 47.05+/-13 J/mol of H2.K. The NaBH4 also had somewhat similar behavior, with 9% congruent evaporation and equilibrium vapor pressure equation of logPLiBH4=-7700+/-335/ T+ (6.7+/-1.5) and 91% incongruent decomposition to Na and Boron metal, and hydrogen gas. The enthalpy of vaporization; DeltaHevap. = 147.2+/-6.4kJ/molH2 and DeltaSevap.= 142 +/-28 kJ/molH2.K (550-650K). The Ca(BH4) 2 exhibited similar vaporization behavior with congruency of 3.2%. The decomposition products are CaH2 and Boron metal with evolution of hydrogen gas varying with the pressure equation as logPeq /P0 =(-1562.7 +/-177)/ T+ (2.57 +/-0.155). The enthalpy and entropy of vaporization, DeltaH evap.= 29.9+/-3.3kJ/molH2, DeltaSevap.=49.14 +/-2.9 J/molH2.K (400-650K) respectively. More details of the properties of the vaporization such partial pressures of effusing gases, Gibbs energies of vaporization, molecular weight of effusing gases, as well as decomposition products, evaporation reactions, thermodynamic modeling of the disproportionation of these three compounds are discussed in this dissertation.

Studies on the crystalline lens. XXI. Bidirectional carrier-mediated transport of lithium

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kinsey, V.E.; McLean, I.W.

1974-10-01

Movement of lithium both into and out of cultured rabbit lenses occurs by processes that obey Michaelis-Menten kinetics as well as by a nonsaturable process. The parameters describing the kinetics of transport are evaluated on the basis of a modified version of a pump-leak hypothesis that was shown previously to account for the fluxes of other alkali metal cations. Potassium is a potent competitive inhibitor of the carrier-mediated transport of lithium into the lens. Lithium weakly inhibits the influx of potassium by a noncompetitive process. The observation that lithium is a weak inhibitor of potassium transport (Ki = 70 mM)more » while having a moderate affinity for its carrier (Km = 4.0 mM) suggests that more than one site may be responsible for the transport of potassium and lithium into the lens. Active transport of lithium out of the lens does not appear to involve the sodium pump, since the rate of sodium efflux is unaffected by lithium. Both influx and efflux of lithium are inhibited by ouabain (10/sup -5/ M) but not by amiloride (10/sup -4/ M) or oxytocin (20 milliunits per milliliter). Lithium displaces proportionate amounts of sodium and potassium from intracellular fluid when lenses are cultured in the presence of this cation. The nonsaturable exchange of lithium is independent of observed differences in electric potential, indicating that lithium does not permeate the lenticular membranes by simple diffusion of lithium ions, but rather as a complex with either a free anion or a carrier within the membrane. The affinity of lithium for the carrier is essentially equal to that of cesium and much lower than that for rubidium, whereas the kd of both lithium and rubidium is much higher than that for cesium. These differences indicate that a common pathway cannot be responsible for the discrimination between cations by both the pump and the leak.« less

Molecular Toxicology of Chromatin: The Role of Poly (ADP-Ribose) in Gene Control

DTIC Science & Technology

1985-12-15

remaining aý minor camponent. There- fore, in order to minimize this minor product we include potassium phosphate (p1 6.6) in an amount equivalent to the... phosphate (pH 6.6) followed by 0.005 ml of a 0.10 M solution of sodium 3 H]-borohydride in 0.10 M potassium hydroxide. The resultant solution, which...AMP. Five hundred nmol of oxidized AMP was mixed with 5000 nmol of borohydride in 4.5 mM potassium phosphate , pH 9, in a final volume of 1100 Ul

Formation and accumulation of radiation-induced defects and radiolysis products in modified lithium orthosilicate pebbles with additions of titanium dioxide

NASA Astrophysics Data System (ADS)

Zarins, Arturs; Valtenbergs, Oskars; Kizane, Gunta; Supe, Arnis; Knitter, Regina; Kolb, Matthias H. H.; Leys, Oliver; Baumane, Larisa; Conka, Davis

2016-03-01

Lithium orthosilicate (Li4SiO4) pebbles with 2.5 wt.% excess of silicon dioxide (SiO2) are the European Union's designated reference tritium breeding ceramics for the Helium Cooled Pebble Bed (HCPB) Test Blanket Module (TBM). However, the latest irradiation experiments showed that the reference Li4SiO4 pebbles may crack and form fragments under operation conditions as expected in the HCPB TBM. Therefore, it has been suggested to change the chemical composition of the reference Li4SiO4 pebbles and to add titanium dioxide (TiO2), to obtain lithium metatitanate (Li2TiO3) as a second phase. The aim of this research was to investigate the formation and accumulation of radiation-induced defects (RD) and radiolysis products (RP) in the modified Li4SiO4 pebbles with different contents of TiO2 for the first time, in order to estimate and compare radiation stability. The reference and the modified Li4SiO4 pebbles were irradiated with accelerated electrons (E = 5 MeV) up to 5000 MGy absorbed dose at 300-990 K in a dry argon atmosphere. By using electron spin resonance (ESR) spectroscopy it was determined that in the modified Li4SiO4 pebbles, several paramagnetic RD and RP are formed and accumulated, like, E' centres (SiO33-/TiO33-), HC2 centres (SiO43-/TiO3-) etc. On the basis of the obtained results, it is concluded that the modified Li4SiO4 pebbles with TiO2 additions have comparable radiation stability with the reference pebbles.

Design and operation of a 1000 C lithium-cesium test system

NASA Technical Reports Server (NTRS)

Hays, L. G.; Haskins, G. M.; Oconnor, D. E.; Torola, J., Jr.

1973-01-01

A 100 kWt cesium-lithium test loop fabricated of niobium-1% zirconium for experiments on erosion and two-phase system operation at temperatures of 980 C and velocities of 150 m/s. Although operated at design temperature for 100 hours, flow instabilities in the two-phase separator interfered with the achievement of the desired mass flow rates. A modified separator was fabricated and installed in the loop to alleviate this problem.

Inelastic collisions of positrons with one-valence-electron targets

NASA Technical Reports Server (NTRS)

Abdel-Raouf, Mohamed Assad

1990-01-01

The total elastic and positronium formation cross sections of the inelastic collisions between positrons and various one-valence-electron atoms, (namely hydrogen, lithium, sodium, potassium and rubidium), and one-valence-electron ions, (namely hydrogen-like, lithium-like and alkaline-earth positive ions) are determined using an elaborate modified coupled-static approximation. Special attention is devoted to the behavior of the Ps cross sections at the energy regions lying above the Ps formation thresholds.

Modified carbon black materials for lithium-ion batteries

DOEpatents

Kostecki, Robert; Richardson, Thomas; Boesenberg, Ulrike; Pollak, Elad; Lux, Simon

2016-06-14

A lithium (Li) ion battery comprising a cathode, a separator, an organic electrolyte, an anode, and a carbon black conductive additive, wherein the carbon black has been heated treated in a CO.sub.2 gas environment at a temperature range of between 875-925 degrees Celsius for a time range of between 50 to 70 minutes to oxidize the carbon black and reduce an electrochemical reactivity of the carbon black towards the organic electrolyte.

Inhibition of GSK3 dependent tau phosphorylation by metals.

PubMed

Gómez-Ramos, Alberto; Domínguez, Jorge; Zafra, Delia; Corominola, Helena; Gomis, Ramon; Guinovart, Joan J; Avila, Jesús

2006-04-01

One of the main pathological characteristics of Alzheimer's disease is the presence in the brain of the patients of an aberrant structure, the paired helical filaments, composed of hyperphosphorylated tau. The level of tau phosphorylation has been correlated with the capacity for tau aggregation. Thus, the mechanism for tau phosphorylation could be important to clarify those pathological features in Alzheimer's disease. Tau protein could be modified by different kinases, being GSK3 the one that could modify more sites of that protein. GSK3 activity could be modulate by the presence of metals like magnesium that can be required for the proper function of the kinase, whereas, metals like manganesum or lithium inhibit the activity of the kinase. Many works have been done to study the inhibition of GSK3 by lithium, a specific inhibitor of that kinase. More recently, it has been indicated that sodium tungstate could also inhibit GSK3 through a different mechanism. In this review, we discuss the effect of these two metals, lithium and tungstate, on GSK3 (or tau I kinase) activity.

Chronic Microdose Lithium Treatment Prevented Memory Loss and Neurohistopathological Changes in a Transgenic Mouse Model of Alzheimer's Disease.

PubMed

Nunes, Marielza Andrade; Schöwe, Natalia Mendes; Monteiro-Silva, Karla Cristina; Baraldi-Tornisielo, Ticiana; Souza, Suzzanna Ingryd Gonçalves; Balthazar, Janaina; Albuquerque, Marilia Silva; Caetano, Ariadiny Lima; Viel, Tania Araujo; Buck, Hudson Sousa

2015-01-01

The use of lithium is well established in bipolar disorders and the benefits are being demonstrated in neurodegenerative disorders. Recently, our group showed that treatment with microdose lithium stabilized the cognitive deficits observed in Alzheimer's disease (AD) patients. In order to verify the lithium microdose potential in preventing the disease development, the aim of this work was to verify the effects of chronic treatment with microdose lithium given before and after the appearance of symptoms in a mouse model of a disease similar to AD. Transgenic mice (Cg-Tg(PDGFB-APPSwInd)20Lms/2J) and their non-transgenic litter mate genetic controls were treated with lithium carbonate (0.25mg/Kg/day in drinking water) for 16 or 8 months starting at two and ten months of age, respectively [corrected]. Similar groups were treated with water. At the end of treatments, both lithium treated transgenic groups and non-transgenic mice showed no memory disruption, different from what was observed in the water treated transgenic group. Transgenic mice treated with lithium since two months of age showed decreased number of senile plaques, no neuronal loss in cortex and hippocampus and increased BDNF density in cortex, when compared to non-treated transgenic mice. It is suitable to conclude that these data support the use of microdose lithium in the prevention and treatment of Alzheimer's disease, once the neurohistopathological characteristics of the disease were modified and the memory of transgenic animals was maintained.

Chronic Microdose Lithium Treatment Prevented Memory Loss and Neurohistopathological Changes in a Transgenic Mouse Model of Alzheimer's Disease

PubMed Central

Monteiro-Silva, Karla Cristina; Baraldi-Tornisielo, Ticiana; Souza, Suzzanna Ingryd Gonçalves; Balthazar, Janaina; Albuquerque, Marilia Silva; Caetano, Ariadiny Lima; Viel, Tania Araujo; Buck, Hudson Sousa

2015-01-01

The use of lithium is well established in bipolar disorders and the benefits are being demonstrated in neurodegenerative disorders. Recently, our group showed that treatment with microdose lithium stabilized the cognitive deficits observed in Alzheimer’s disease (AD) patients. In order to verify the lithium microdose potential in preventing the disease development, the aim of this work was to verify the effects of chronic treatment with microdose lithium given before and after the appearance of symptoms in a mouse model of a disease similar to AD. Transgenic mice (Cg-Tg(PDGFB-APPSwInd)20Lms/2J) and their non-transgenic litter mate genetic controls were treated with lithium carbonate (1.2 mg/Kg/day in drinking water) for 16 or 8 months starting at two and ten months of age, respectively. Similar groups were treated with water. At the end of treatments, both lithium treated transgenic groups and non-transgenic mice showed no memory disruption, different from what was observed in the water treated transgenic group. Transgenic mice treated with lithium since two months of age showed decreased number of senile plaques, no neuronal loss in cortex and hippocampus and increased BDNF density in cortex, when compared to non-treated transgenic mice. It is suitable to conclude that these data support the use of microdose lithium in the prevention and treatment of Alzheimer’s disease, once the neurohistopathological characteristics of the disease were modified and the memory of transgenic animals was maintained. PMID:26605788

Preparation method of Ni@Pt/C nanocatalyst affects the performance of direct borohydride-hydrogen peroxide fuel cell: Improved power density and increased catalytic oxidation of borohydride.

PubMed

Hosseini, Mir Ghasem; Mahmoodi, Raana

2017-08-15

The Ni@Pt/C electrocatalysts were synthesized using two different methods: with sodium dodecyl sulfate (SDS) and without SDS. The metal loading in synthesized nanocatalysts was 20wt% and the molar ratio of Ni: Pt was 1:1. The structural characterizations of Ni@Pt/C electrocatalysts were investigated by field emission scanning electron microscopy (FE-SEM), energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HR-TEM). The electrocatalytic activity of Ni@Pt/C electrocatalysts toward BH 4 - oxidation in alkaline medium was studied by means of cyclic voltammetry (CV), chronopotentiometry (CP), chronoamperometry (CA) and electrochemical impedance spectroscopy (EIS). The results showed that Ni@Pt/C electrocatalyst synthesized without SDS has superior catalytic activity toward borohydride oxidation (22016.92Ag Pt -1 ) in comparison with a catalyst prepared in the presence of SDS (17766.15Ag Pt -1 ) in NaBH 4 0.1M at 25°C. The Membrane Electrode Assembly (MEA) used in fuel cell set-up was fabricated with catalyst-coated membrane (CCM) technique. The effect of Ni@Pt/C catalysts prepared with two methods as anode catalyst on the performance of direct borohydride-hydrogen peroxide fuel cell was studied. The maximum power density was obtained using Ni@Pt/C catalyst synthesized without SDS at 60°C, 1M NaBH 4 and 2M H 2 O 2 (133.38mWcm -2 ). Copyright © 2017 Elsevier Inc. All rights reserved.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wei, Xiaoliang; Cosimbescu, Lelia; Xu, Wu

We will present a novel design lithium-organic non-aqueous redox flow battery based on a modified ferrocene catholyte. This RFB produced desired electrochemical performance exceeding most of the currently reported nonaqueous RFB systems.

A Chemical-Adsorption Strategy to Enhance the Reaction Kinetics of Lithium-Rich Layered Cathodes via Double-Shell Surface Modification.

PubMed

Guo, Lichao; Li, Jiajun; Cao, Tingting; Wang, Huayu; Zhao, Naiqin; He, Fang; Shi, Chunsheng; He, Chunnian; Liu, Enzuo

2016-09-21

Sluggish surface reaction kinetics hinders the power density of Li-ion battery. Thus, various surface modification techniques have been applied to enhance the electronic/ionic transfer kinetics. However, it is challenging to obtain a continuous and uniform surface modification layer on the prime particles with structure integration at the interface. Instead of classic physical-adsorption/deposition techniques, we propose a novel chemical-adsorption strategy to synthesize double-shell modified lithium-rich layered cathodes with enhanced mass transfer kinetics. On the basis of experimental measurement and first-principles calculation, MoO2S2 ions are proved to joint the layered phase via chemical bonding. Specifically, the Mo-O or Mo-S bonds can flexibly rotate to bond with the cations in the layered phase, leading to the good compatibility between the thiomolybdate adsorption layer and layered cathode. Followed by annealing treatment, the lithium-excess-spinel inner shell forms under the thiomolybdate adsorption layer and functions as favorable pathways for lithium and electron. Meanwhile, the nanothick MoO3-x(SO4)x outer shell protects the transition metal from dissolution and restrains electrolyte decomposition. The double-shell modified sample delivers an enhanced discharge capacity almost twice as much as that of the unmodified one at 1 A g(-1) after 100 cycles, demonstrating the superiority of the surface modification based on chemical adsorption.

Free-anchored Nb2O5@graphene networks for ultrafast-stable lithium storage.

PubMed

Deng, Qinglin; Li, Mengjiao; Wang, Junyong; Jiang, Kai; Hu, Zhigao; Chu, Junhao

2018-05-04

Orthorhombic Nb 2 O 5 (T-Nb 2 O 5 ) has structural merit but poor electrical conductivity, limiting their applications in energy storage. Although graphene is frequently adopted to effectively improve its electrochemical properties, the ordinary modified methods cannot meet the growing demands for high-performance. Here, we demonstrate that different graphene modified routes play a vital role in affecting the electrochemical performances of T-Nb 2 O 5 . By only manual shaking within one minute, Nb 2 O 5 nano-particles can be rapidly adsorbed onto graphene, then the free-anchored T-Nb 2 O 5 @graphene three-dimensional networks can be successfully prepared based on hydrogel method. As for the application in lithium-ion batteries, it performs outstanding rate character (129 mA h g -1 (25C rate), 110 mA h g -1 (50C rate) and 90 mA h g -1 (100C rate), correspond to 79%, 67% and 55% capacity of 0.5C rate, respectively) and excellent long-term cycling feature (∼70% capacity retention after 20000 cycles). Moreover, it still maintains similar ultrafast-stable lithium storage performances when Cu foil is substituted by Al foil as current collector. In addition, relevant kinetics mechanisms are also expounded. This work provides a versatile strategy for the preparation of graphene modified Nb 2 O 5 or other types of nanoparticles.

Free-anchored Nb2O5@graphene networks for ultrafast-stable lithium storage

NASA Astrophysics Data System (ADS)

Deng, Qinglin; Li, Mengjiao; Wang, Junyong; Jiang, Kai; Hu, Zhigao; Chu, Junhao

2018-05-01

Orthorhombic Nb2O5 (T-Nb2O5) has structural merit but poor electrical conductivity, limiting their applications in energy storage. Although graphene is frequently adopted to effectively improve its electrochemical properties, the ordinary modified methods cannot meet the growing demands for high-performance. Here, we demonstrate that different graphene modified routes play a vital role in affecting the electrochemical performances of T-Nb2O5. By only manual shaking within one minute, Nb2O5 nano-particles can be rapidly adsorbed onto graphene, then the free-anchored T-Nb2O5@graphene three-dimensional networks can be successfully prepared based on hydrogel method. As for the application in lithium-ion batteries, it performs outstanding rate character (129 mA h g-1 (25C rate), 110 mA h g-1 (50C rate) and 90 mA h g-1 (100C rate), correspond to 79%, 67% and 55% capacity of 0.5C rate, respectively) and excellent long-term cycling feature (˜70% capacity retention after 20000 cycles). Moreover, it still maintains similar ultrafast-stable lithium storage performances when Cu foil is substituted by Al foil as current collector. In addition, relevant kinetics mechanisms are also expounded. This work provides a versatile strategy for the preparation of graphene modified Nb2O5 or other types of nanoparticles.

Preparation of Advanced CuO Nanowires/Functionalized Graphene Composite Anode Material for Lithium Ion Batteries.

PubMed

Zhang, Jin; Wang, Beibei; Zhou, Jiachen; Xia, Ruoyu; Chu, Yingli; Huang, Jia

2017-01-17

The copper oxide (CuO) nanowires/functionalized graphene (f-graphene) composite material was successfully composed by a one-pot synthesis method. The f-graphene synthesized through the Birch reduction chemistry method was modified with functional group "-(CH₂)₅COOH", and the CuO nanowires (NWs) were well dispersed in the f-graphene sheets. When used as anode materials in lithium-ion batteries, the composite exhibited good cyclic stability and decent specific capacity of 677 mA·h·g -1 after 50 cycles. CuO NWs can enhance the lithium-ion storage of the composites while the f-graphene effectively resists the volume expansion of the CuO NWs during the galvanostatic charge/discharge cyclic process, and provide a conductive paths for charge transportation. The good electrochemical performance of the synthesized CuO/f-graphene composite suggests great potential of the composite materials for lithium-ion batteries anodes.

Chiral Compounds and Green Chemistry in Undergraduate Organic Laboratories: Reduction of a Ketone by Sodium Borohydride and Baker's Yeast

NASA Astrophysics Data System (ADS)

Pohl, Nicola; Clague, Allen; Schwarz, Kimberly

2002-06-01

We describe an integrated set of experiments for the undergraduate organic laboratory that allows students to compare and contrast biological and chemical means of introducing chirality into a molecule. The racemic reduction of ethyl acetoacetate with sodium borohydride and the same reduction in the presence of a tartaric acid ligand are described, and a capillary gas chromatography column packed with a chiral material for product analysis is introduced. The results of these two hydride reactions are compared with the results of a common undergraduate experiment, the baker's yeast reduction of ethyl acetoacetate.

Study on preparation of ultrafine amorphous particles by chemical reduction

NASA Astrophysics Data System (ADS)

Song, Xu; Yusheng, Xu; Huali, Jiang; Qing, Xue

1993-04-01

Ultrafine amorphous FeNiB powder was prepared by potassium borohydride reduction by mixing the aqueous solutions in a bath of supersonic oscillator. Different mixing ratios of potassium borohydride to metal salt were applied. Analysis of the composition of the sample and the Fe 2+ and Ni 2+ remaining in the filtrate after preparation shows that a quantity of KBH 4 about 1.5 times the stoichiometrical quantity is enough. Mössbauer measurements were performed at room temperature and it was found that excess KBH 4 makes no distinct difference in the spectra of the samples.

High cycle life secondary lithium battery

NASA Technical Reports Server (NTRS)

Yen, Shiao-Ping S. (Inventor); Shen, David H. (Inventor); Carter, Boyd J. (Inventor); Somoano, Robert B. (Inventor)

1985-01-01

A secondary battery (10) of high energy density and long cycle is achieved by coating the separator (18) with a film (21) of cationic polymer such as polyvinyl-imidazoline. The binder of the positive electrode (14) such as an ethylene-propylene elastomer binder (26) containing particles (28) of TiS.sub.2 chalcogenide can also be modified to contain sulfone functional groups by incorporating liquid or solid sulfone materials such as 0.1 to 5 percent by weight of sulfolane into the binder. The negative lithium electrode (14), separator (18) and positive electrode (16) are preferably spirally wound and disposed within a sealed casing (17) containing terminals (32, 34). The modified separator and positive electrode are more wettable by the electrolytes in which a salt is dissolved in a polar solvent such as sulfolane.

Recombination luminescence from electron-irradiated Li-diffused Si

NASA Technical Reports Server (NTRS)

Johnson, E. S.; Compton, W. D.; Noonan, J. R.; Streetman, B. G.

1973-01-01

Lithium doping has a dramatic effect on the low-temperature photoluminescence of electron-irradiated Si. In oxigen-lean Si with Li doping, a new irradiation-dependent luminescence band between 0.75 and 1.05 eV is observed, which is dominated by a zero-phonon peak at 1.045 eV. This band is believed to be due to radiative transitions involving a Li-modified divacancy. This band is present also in oxygen-rich, Li-diffused Si and is accompanied by bands previously related to the Si-G15(K) center and the divacancy. The intensities of the Li-modified divacancy and Si-G15(K) center bands are relatively weak in the oxygen-rich material, apparently due to the formation of lithium-oxygen complexes which reduce the concentration of unassociated interstitial Li and O.

Surface Modified Pinecone Shaped Hierarchical Structure Fluorinated Mesocarbon Microbeads for Ultrafast Discharge and Improved Electrochemical Performances

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dai, Yang; Fang, Yuan; Cai, Sendan

2016-12-01

Among all primary lithium batteries, Li/CF x primary battery possesses the highest energy density of 2180 Wh kg -1. However, a key limitation is its poor rate capability because the cathode material CF x is intrinsically a poor electronic conductor. Here, we developed a so-called “doing subtraction” method to modify the pinecone shaped fluorinated mesocarbon microbead (F-MCMB). The modified fluorinated mesocarbon microbead (MF-MCMB), manifests the advantage of open-framed structure, possesses good electronic conductivity and removes transport barrier for lithium ions. Thus, high capacity performance and excellent rate capability without compromising capacity can be obtained. A capacity of 343 mAhg -1more » and a maximum power density of 54600 W kg -1 are realized at an ultrafast rate of 40 C (28A g -1). Additionally, the MF-MCMB cathode does not show any voltage delay even at 5C during the discharge, which is a remarkable improvement over the state-of-the-art CF xmaterials.« less

High-rate lithium/manganese dioxide batteries; the double cell concept

NASA Astrophysics Data System (ADS)

Drews, Jürgen; Wolf, Rüdiger; Fehrmann, Gerd; Staub, Roland

An implantable defibrillator battery has to provide pulse-power capabilities as well as high energy density. Low self-discharge rates are mandatory and an ability to check the state of charge is required. To accomplish these requirements, a lithium/manganese dioxide battery with a modified active cathode mass has been developed. Usage of a double cell design increases significantly the battery performance within an implantable defibrillator. The design features of a high-rate, pulse-power, manganese dioxide double cell are described.

Surface modifications for carbon lithium intercalation anodes

DOEpatents

Tran, Tri D.; Kinoshita, Kimio

2000-01-01

A prefabricated carbon anode containing predetermined amounts of passivating film components is assembled into a lithium-ion rechargeable battery. The modified carbon anode enhances the reduction of the irreversible capacity loss during the first discharge of a cathode-loaded cell. The passivating film components, such as Li.sub.2 O and Li.sub.2 CO.sub.3, of a predetermined amount effective for optimal passivation of carbon, are incorporated into carbon anode materials to produce dry anodes that are essentially free of battery electrolyte prior to battery assembly.

Microdose lithium treatment stabilized cognitive impairment in patients with Alzheimer's disease.

PubMed

Nunes, Marielza Andrade; Viel, Tania Araujo; Buck, Hudson Sousa

2013-01-01

A lower incidence of dementia in bipolar patients treated with lithium has been described. This metal inhibits the phosphorylation of glycogen-synthase-kinase 3-α and β, which are related to amyloid precursor protein processing and tau hyperphosphorylation in pathological conditions, respectively. Following the same rationale, a group just found that lithium has disease-modifying properties in amnestic mild cognitive impairment with potential clinical implications for the prevention of Alzheimer's Disease (AD) when a dose ranging from 150 to 600 mg is used. As lithium is highly toxic in regular doses, our group evaluated the effect of a microdose of 300 μg, administered once daily on AD patients for 15 months. In the evaluation phase, the treated group showed no decreased performance in the mini-mental state examination test, in opposition to the lower scores observed for the control group during the treatment, with significant differences starting three months after the beginning of the treatment, and increasing progressively. This data suggests the efficacy of a microdose lithium treatment in preventing cognitive loss, reinforcing its therapeutic potential to treat AD using very low doses.

Directing the Lithium-Sulfur Reaction Pathway via Sparingly Solvating Electrolytes for High Energy Density Batteries.

PubMed

Lee, Chang-Wook; Pang, Quan; Ha, Seungbum; Cheng, Lei; Han, Sang-Don; Zavadil, Kevin R; Gallagher, Kevin G; Nazar, Linda F; Balasubramanian, Mahalingam

2017-06-28

The lithium-sulfur battery has long been seen as a potential next generation battery chemistry for electric vehicles owing to the high theoretical specific energy and low cost of sulfur. However, even state-of-the-art lithium-sulfur batteries suffer from short lifetimes due to the migration of highly soluble polysulfide intermediates and exhibit less than desired energy density due to the required excess electrolyte. The use of sparingly solvating electrolytes in lithium-sulfur batteries is a promising approach to decouple electrolyte quantity from reaction mechanism, thus creating a pathway toward high energy density that deviates from the current catholyte approach. Herein, we demonstrate that sparingly solvating electrolytes based on compact, polar molecules with a 2:1 ratio of a functional group to lithium salt can fundamentally redirect the lithium-sulfur reaction pathway by inhibiting the traditional mechanism that is based on fully solvated intermediates. In contrast to the standard catholyte sulfur electrochemistry, sparingly solvating electrolytes promote intermediate- and short-chain polysulfide formation during the first third of discharge, before disproportionation results in crystalline lithium sulfide and a restricted fraction of soluble polysulfides which are further reduced during the remaining discharge. Moreover, operation at intermediate temperatures ca. 50 °C allows for minimal overpotentials and high utilization of sulfur at practical rates. This discovery opens the door to a new wave of scientific inquiry based on modifying the electrolyte local structure to tune and control the reaction pathway of many precipitation-dissolution chemistries, lithium-sulfur and beyond.

Lithium attenuated the behavioral despair induced by acute neurogenic stress through blockade of opioid receptors in mice.

PubMed

Khaloo, Pegah; Sadeghi, Banafshe; Ostadhadi, Sattar; Norouzi-Javidan, Abbas; Haj-Mirzaian, Arya; Zolfagharie, Samira; Dehpour, Ahmad-Reza

2016-10-01

Major depressive disorder is disease with high rate of morbidity and mortality. Stressful events lead to depression and they can be used as a model of depression in rodents. In this study we aimed to investigate whether lithium modifies the stressed-induced depression through blockade of opioid receptors in mice. We used foot shock stress as stressor and forced swimming test (FST), tail suspension test (TST) and open field test (OFT) to evaluation the behavioral responses in mice. We also used naltrexone hydrochloride (as opioid receptor antagonist), and morphine (as opioid receptor agonist). Our results displayed that foot-shock stress significantly increased the immobility time in TST and FST but it could not change the locomotor behavior in OFT. When we combined the low concentrations of lithium and naltrexone a significant reduction in immobility time was seen in the FST and TST in comparison with control foot-shock stressed group administered saline only. Despite the fact that our data showed low concentrations of lithium, when administered independently did not significantly affect the immobility time. Also our data indicated that concurrent administration of lithium and naltrexone had no effect on open field test. Further we demonstrated that simultaneous administration of morphine and lithium reverses the antidepressant like effect of active doses of lithium. Our data acclaimed that we lithium can augment stressed-induced depression and opioid pathways are involved in this action. Copyright © 2016 Elsevier Masson SAS. All rights reserved.

Beneficial synergistic effects of microdose lithium with pyrroloquinoline quinone in an Alzheimer's disease mouse model.

PubMed

Zhao, Lei; Gong, Neng; Liu, Meng; Pan, Xiaoli; Sang, Shaoming; Sun, Xiaojing; Yu, Zhe; Fang, Qi; Zhao, Na; Fei, Guoqiang; Jin, Lirong; Zhong, Chunjiu; Xu, Tianle

2014-12-01

Alzheimer's disease (AD) is a complicated, neurodegenerative disorder involving multifactorial pathogeneses and still lacks effective clinical treatment. Recent studies show that lithium exerts disease-modifying effects against AD. However, the intolerant side effects at conventional effective dosage limit the clinical use of lithium in treating AD. To explore a novel AD treatment strategy with microdose lithium, we designed and synthesized a new chemical, tri-lithium pyrroloquinoline quinone (Li3PQQ), to study the synergistic effects of low-dose lithium and pyrroloquinoline quinone, a native compound with powerful antioxidation and mitochondrial amelioration. The results showed that Li3PQQ at a relative low dose (6 and 12 mg/kg) exhibited more powerful effects in restoring the impairment of learning and memory, facilitating hippocampal long-term potentiation, and reducing cerebral amyloid deposition and phosphorylated tau level in APP/PS1 transgenic mice than that of lithium chloride at both low and high dose (5 and 100 mg/kg). We further found that Li3PQQ inhibited the activity of glycogen synthase kinase-3 and increased the activity of β-amyloid-binding alcohol dehydrogenase, which might underlie the beneficial effects of Li3PQQ on APP/PS1 transgenic mice. Our study demonstrated the efficacy of a novel AD therapeutic strategy targeting at multiple disease-causing mechanisms through the synergistic effects of microdose lithium and pyrroloquinoline quinone. Copyright © 2014 Elsevier Inc. All rights reserved.

An ammonia-stabilized mixed-cation borohydride: synthesis, structure and thermal decomposition behavior.

PubMed

Yang, Yanjing; Liu, Yongfeng; Wu, Hui; Zhou, Wei; Gao, Mingxia; Pan, Hongge

2014-01-07

We demonstrate the synthesis, crystal structure and thermal decomposition behavior of a novel ammonia-stabilized mixed-cation borohydride where the NH3 groups enable the coexistence of Li and Mg cations as an "assistant". Li2Mg(BH4)4·6NH3, which is comprised of orderly arranged Mg[NH3]6(2+) ammine complexes and Li2[BH4]4(2-) complex anions, was synthesized by the mechanochemical reaction between Mg(BH4)2·6NH3 and LiBH4. This novel compound crystallizes in a tetragonal P4(3)2(1)2 (No. 96) structure with lattice parameters a = b = 10.7656(8) Å and c = 13.843(1) Å with very short dihydrogen bonds, which determine a very low onset temperature of 80 °C for hydrogen release and are also responsible for the nucleation of Li2Mg(BH4)4·3NH3 as a decomposition intermediate. Mechanistic investigations on the thermal decomposition showed that the H(δ+)-H(δ-) combination in the ammonia-stabilized mixed-cation borohydride was significantly enhanced due to the strengthened Mg-N bonds. Upon heating, 11.02 moles of H2 (equivalent to 11.1 wt%) and 3.07 moles of NH3 are evolved from one mole of Li2Mg(BH4)4·6NH3 with a three-step reaction. The insights into the formation mechanism of ammonia-stabilized mixed-cation borohydride and the role played by NH3 group are very useful as a guideline for the design and synthesis of novel B-N-based materials with high hydrogen content.

Synthesis of Ca(BH4)2 from Synthetic Colemanite Used in Hydrogen Storage by Mechanochemical Reaction

NASA Astrophysics Data System (ADS)

Karabulut, Ahmet F.; Guru, Metin; Boynueğri, Tuğba A.; Aydin, Mustafa Yasir

2016-08-01

In this study, synthesis of Ca(BH4)2 has been carried out with a solid phase reaction in which synthetic colemanite has been used as a raw material. Three dimensional high energy spex collider was selected for this mechanochemical reaction. Calcium borohydride is one of the most valuable metal borohydrides. In order to produce calcium borohydride economically, anhydrous colemanite mineral has been used as reactant. Calcium borohydride has been directly manufactured from anhydrous colemanite in spex-type ball milling without the need for any intermediate product. Thus, the advantages of this method over wet chemical procedure (such as having no intermediate product, no azeotropic limitations and no need of regaining product from solution after production by using evaporation, crystallization and drying processes) have made it possible to achieve the desired economical gains. Parametric experiments were conducted to determine the best conditions for the highest yield of solid phase reaction in the spex-type ball milling. Best results have been determined by using areas of related peaks in spectra of Fourier transform infrared spectroscopy (FT-IR). In order to use peaks area for determining Ca(BH4)2 concentration, a calibration graph of FT-IR absorbance peak areas has been created by using samples with known different concentrations of commercial Ca(BH4)2. Optimum amounts of calcium hydride and synthesis reaction time were found to be 2.1 times the stoichiometric ratio and 2500 min, respectively. As a result of these optimizations, the maximum yield of the solid phase reaction carried out by the spex-type ball milling has been determined as 93%.

The preliminary design of bearings for the control system of a high-temperature lithium-cooled nuclear reactor

NASA Technical Reports Server (NTRS)

Yacobucci, H. G.; Waldron, W. D.; Walowit, J. A.

1973-01-01

The design of bearings for the control system of a fast reactor concept is presented. The bearings are required to operate at temperatures up to 2200 F in one of two fluids, lithium or argon. Basic bearing types are the same regardless of the fluid. Crowned cylindrical journals were selected for radially loaded bearings and modified spherical bearings were selected for bearings under combined thrust and radial loads. Graphite and aluminum oxide are the materials selected for the argon atmosphere bearings while cermet compositions (carbides or nitrides bonded with refractory metals) were selected for the lithium lubricated bearings. Mounting of components is by shrink fit or by axial clamping utilizing differential thermal expansion.

Facile synthesis of SiO{sub 2} nanoparticles for biomedical applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Scano, A., E-mail: alescano80@tiscali.it; Pilloni, M., E-mail: alescano80@tiscali.it; Cabras, V., E-mail: alescano80@tiscali.it

Silica nanoparticles (SiO{sub 2} NPs) for biomedical applications have been prepared by using a facile modified Stöber-synthesis. Potassium borohydride (KBH{sub 4}) has been introduced in the synthesis procedure in order to control NP size. Several samples have been prepared varying tetraethylorthosilicate (TEOS) concentration, and using different process conditions (temperature, reaction time and atmosphere). In order to study the influence of the process conditions on the NP size, morphology and properties, several characterization techniques were used. Size and morphology of the as-prepared SiO{sub 2} NPs have been studied by using Transmission Electron Microscope (TEM) and Dynamic Light Scattering (DLS) techniques. Structuralmore » characterization was carried out by X-ray powder diffraction. To investigate the SiO{sub 2} NP fluorescence emission properties the fluorescence spectroscopy was also used.« less

Structure determination of the neutral exopolysaccharide produced by Lactobacillus delbrueckii subsp. bulgaricus OLL1073R-1.

PubMed

Van Calsteren, Marie-Rose; Gagnon, Fleur; Nishimura, Junko; Makino, Seiya

2015-09-02

The neutral exopolysaccharide (NPS) of Lactobacillus delbrueckii subsp. bulgaricus strain OLL1073R-1 was purified and characterized. The molecular mass was 5.0×10(6) g/mol. Sugar and absolute configuration analyses gave the following composition: d-Glc, 1; d-Gal, 1.5. The NPS was also submitted to periodate oxidation followed by borohydride reduction and Smith degradation. Sugar and methylation analyses, (1)H and (13)C nuclear magnetic resonance, and mass spectrometry of the NPS or of its specifically modified products allowed determining the repeating unit sequence: {2)Glc(α1-3)Glc(β1-3)[Gal(β1-4)]Gal(β1-4)Gal(α1-}n. The structure is compared to that of exopolysaccharides produced by other Lactobacillus bulgaricus strains. Copyright © 2015. Published by Elsevier Ltd.

Optical and physical properties of samarium doped lithium diborate glasses

NASA Astrophysics Data System (ADS)

Hanumantharaju, N.; Sardarpasha, K. R.; Gowda, V. C. Veeranna

2018-05-01

Sm3+ doped lithium di-borate glasses with composition 30Li2O-60B2O3-(10-x) PbO, (where 0 < x < 2 mole. %) were prepared by melt quenching method. The addition of modifier oxide to vitreous B2O3 modifies the glass network by converting three coordinated trigonal boron units (BO3) to weaker anionic four coordinated tetrahedral borons (BO4). The decrease in density and increase in molar volume with samarium ion content indicates the openness of the glass structure. The gradual increase in average separation of boron-boron atoms with VmB clearly indicates deterioration of borate glass network, which in turn leads to decrease in the oxygen packing density. The replacements of Sm2O3 for PbO depolymerise the chain structure and that would increase the concentration of non-bridging oxygens. The marginal increase of optical band gap energy after 1.0 mol.% of Sm2O3 is explained by considering the structural modification in lead-borate. The influence of Sm3+ ion on physical and optical properties in lithium-lead-borate glasses is investigated and the results were discussed in view of the structure of borate glass network.

Synthesis of Pt/rGO catalysts with two different reducing agents and their methanol electrooxidation activity

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vu, Thu Ha Thi, E-mail: ptntd2004@yahoo.fr; Tran, Thanh Thuy Thi, E-mail: tranthithanhthuygl@gmail.com; Le, Hong Ngan Thi

2016-01-15

Highlights: • Pt/rGO catalysts were successfully synthesized using either NaBH{sub 4} or ethylene glycol. • Synthesis using NaBH{sub 4} could improve electrocatalytic towards methanol oxidation of Pt/rGO catalyst. • 40%Pt/rGO synthesized using NaBH{sub 4} showed the best electrocatalytic performance. - Abstract: The synthesis processes of Platinum (Pt) on reduced graphene oxide (rGO) catalysts from graphene oxide (GO) using two reducing agents including sodium borohydride and ethylene glycol is reported. Structure and morphology of Pt/rGO catalysts are characterized by X-ray powder diffraction, transmission electron microscopy, Raman spectroscopy, and X-ray photoelectron spectroscopy. Electrocatalytic methanol oxidation properties of these catalysts are evaluated bymore » cyclic voltammetry and chronoamperometry. The results show that catalyst synthesized using sodium borohydride has a higher metallic Pt content and an improved catalytic performance in comparison to catalyst synthesized using ethylene glycol. Moreover, effect of Pt loading amount on electrocatalytic methanol oxidation performance of catalysts synthesized using sodium borohydride is systematically investigated. The optimal Pt loading amount on graphene is determined to be 40%.« less

Predicting new multicomponent materials for hydrogen storage using first-principles calculations

NASA Astrophysics Data System (ADS)

Aidhy, Dilpuneet; Wolverton, Chris

2010-03-01

Wide research has unraveled some very promising hydrogen storage materials such as metal borohydrides, amides and alanates. However, all of these materials are limited either thermodynamically or kinetically. The recent observation of mixing in these systems (e.g., borohydride-amide mixing in Li4(BH4)(NH2)3 [1] and metal mixing in NaZn2(BH4)3) [2] has demonstrated the possibility of forming new multicomponent ordered compounds that may have desirable hydrogen storage properties. However, these multicomponent systems are largely unexplored. Here, we use density functional theory (DFT) along with Monte Carlo-based crystal structure prediction methods to search for new multicomponent hydrides. We find evidence for stable compounds in the Mg(BH4)2/Mg(NH2)2 system, which have not yet been observed. In addition, we also study a wide range of mixed metal borohydride systems, and find evidence of ordered stable structures such as Li2Na(BH4)3. 1. F. E. Pinkerton, M. S. Meyer, G. P. Meisner and M. P. Balogh, J. Phys. Chem. B 110, 7967 (2006). 2. D. Ravnsbeak, Y. Filinchuk, Y. Cerenius, H. J. Jakobsen, F. Besenbacher, J. Skibsted and T. R. Jensen, Angew. Chem. 48, 6659 (2009).

Isotopic Exchange in Porous and Dense Magnesium Borohydride.

PubMed

Zavorotynska, Olena; Deledda, Stefano; Li, Guanqiao; Matsuo, Motoaki; Orimo, Shin-ichi; Hauback, Bjørn C

2015-09-01

Magnesium borohydride (Mg(BH4)2) is one of the most promising complex hydrides presently studied for energy-related applications. Many of its properties depend on the stability of the BH4(-) anion. The BH4(-) stability was investigated with respect to H→D exchange. In situ Raman measurements on high-surface-area porous Mg(BH4 )2 in 0.3 MPa D2 have shown that the isotopic exchange at appreciable rates occurs already at 373 K. This is the lowest exchange temperature observed in stable borohydrides. Gas-solid isotopic exchange follows the BH4(-) +D˙ →BH3D(-) +H˙ mechanism at least at the initial reaction steps. Ex situ deuteration of porous Mg(BH4)2 and its dense-phase polymorph indicates that the intrinsic porosity of the hydride is the key behind the high isotopic exchange rates. It implies that the solid-state H(D) diffusion is considerably slower than the gas-solid H→D exchange reaction at the surface and it is a rate-limiting steps for hydrogen desorption and absorption in Mg(BH4)2. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

The Removal of Cu (II) from Aqueous Solution using Sodium Borohydride as a Reducing Agent

NASA Astrophysics Data System (ADS)

Sithole, N. T.; Ntuli, F.; Mashifana, T.

2018-03-01

The removal and recovery of metals from wastewater has been a subject of significant importance due the negative impact these toxic metals have on human health and the environment as a result of water and soil pollution. Increased use of the metals and chemicals in the process industries has resulted in generation of large quantity of effluents that contains high level of toxic metals and other pollutants. The objective of this work was to recover of Cu in its elemental form as metallic powder from aqueous solution using NaBH4 as a reducing agent. Reductive precipitation was achieved in a batch reactor at 65°C using Cu powder as a seeding material. This study also investigated the effect of concentration of sodium borohydride (NaBH4) as a reducing agent. The amount of NaBH4 was varied based on mole ratios which are 1:1, 1:0.25 and 1:0.1 to recover Cu from synthetic wastewater. The results obtained showed that sodium borohydride is an effective reducing agent to recover Cu from wastewater. The optimum concentration of NaBH4 that gives the best results the 1:1 molar ratio with over 99% Cu removal.

Determination of methylmercury and inorganic mercury in water samples by slurry sampling cold vapor atomic absorption spectrometry in a flow injection system after preconcentration on silica C(18) modified.

PubMed

Segade, Susana Río; Tyson, Julian F

2007-03-15

A novel method for preconcentration of methylmercury and inorganic mercury from water samples was developed involving the determination of ngl(-1) levels of analytes retained on the silica C(18) solid sorbent, previous complexation with ammonium pyrrolidine dithiocarbamate (APDC), by slurry sampling cold vapor atomic absorption spectrometry (SS-CVAAS) in a flow injection (FI) system. Several variables were optimized affecting either the retention of both mercury species, such as APDC concentration, silica C(18) amount, agitation times, or their determination, including hydrochloric acid concentration in the suspension medium, peristaltic pump speed and argon flow-rate. A Plackett-Burman saturated factorial design permitted to differentiate the influential parameters on the preconcentration efficiency, which were after optimized by the sequential simplex method. The contact time between mercury containing solution and APDC, required to reach an efficient sorption, was decreased from 26 to 3min by the use of sonication stirring instead of magnetic stirring. The use of 1moldm(-3) hydrochloric acid suspension medium and 0.75% (m/v) sodium borohydride reducing agent permitted the selective determination of methylmercury. The combination of 5moldm(-3) hydrochloric acid and 10(-4)% (m/v) sodium borohydride was used for the selective determination of inorganic mercury. The detection limits achieved for methylmercury and inorganic mercury determination under optimum conditions were 0.96 and 0.25ngl(-1), respectively. The reliability of the proposed method for the determination of both mercury species in waters was checked by the analysis of samples spiked with known concentrations of methylmercury and inorganic mercury; quantitative recoveries were obtained.

Deuterium and lithium-6 MAS NMR studies of manganese oxide electrode materials

NASA Astrophysics Data System (ADS)

Paik, Younkee

Electrolytic manganese dioxide (EMD) is used world wide as the cathode materials in both lithium and alkaline primary (non-rechargeable) batteries. We have developed deuterium and lithium MAS NMR techniques to study EMD and related manganese oxides and hydroxides, where diffraction techniques are of limited value due to a highly defective nature of the structures. Deuterons in EMD, manganite, groutite, and deuterium-intercalated pyrolusite and ramsdellite were detected by NMR, for the first time, and their locations and motions in the structures were analyzed by applying variable temperature NMR techniques. Discharge mechanisms of EMD in alkaline (aqueous) electrolytes were studied, in conjunction with step potential electrochemical spectroscopic (SPECS) method, and five distinctive discharge processes were proposed. EMD is usually heat-treated at about 300--400°C to remove water to be used in lithium batteries. Details of the effects of heat-treatment, such as structural and compositional changes as a function of heat-treatment temperature, were studied by a combination of MAS NMR, XRD, and thermogravimetric analysis. Lithium local environments in heat-treated EMD (HEMD) that were discharged in lithium cells, were described in terms of related environments found in model compounds pyrolusite and ramsdellite where specific Li + sites were detected by MAS NMR and the hyperfine shift scale method of Grey et al. Acid-leaching of Li2MnO3 represents an approach for synthesizing new or modified manganese oxide electrode materials for lithium rechargeable batteries. Progressive removal of lithium from specific crystallographic sites, followed by a gradual change of the crystal structure, was monitored by a combination of NMR and XRD techniques.

Systematic Effect for an Ultralong Cycle Lithium-Sulfur Battery.

PubMed

Wu, Feng; Ye, Yusheng; Chen, Renjie; Qian, Ji; Zhao, Teng; Li, Li; Li, Wenhui

2015-11-11

Rechargeable lithium-sulfur (Li-S) batteries are attractive candidates for energy storage devices because they have five times the theoretical energy storage of state-of-the-art Li-ion batteries. The main problems plaguing Li-S batteries are poor cycle life and limited rate capability, caused by the insulating nature of S and the shuttle effect associated with the dissolution of intermediate lithium polysulfides. Here, we report the use of biocell-inspired polydopamine (PD) as a coating agent on both the cathode and separator to address these problems (the "systematic effects"). The PD-modified cathode and separator play key roles in facilitating ion diffusion and keeping the cathode structure stable, leading to uniform lithium deposition and a solid electrolyte interphase. As a result, an ultralong cycle performance of more than 3000 cycles, with a capacity fade of only 0.018% per cycle, was achieved at 2 C. It is believed that the systematic modification of the cathode and separator for Li-S batteries is a new strategy for practical applications.

Integrating a Photocatalyst into a Hybrid Lithium-Sulfur Battery for Direct Storage of Solar Energy.

PubMed

Li, Na; Wang, Yarong; Tang, Daiming; Zhou, Haoshen

2015-08-03

Direct capture and storage of abundant but intermittent solar energy in electrical energy-storage devices such as rechargeable lithium batteries is of great importance, and could provide a promising solution to the challenges of energy shortage and environment pollution. Here we report a new prototype of a solar-driven chargeable lithium-sulfur (Li-S) battery, in which the capture and storage of solar energy was realized by oxidizing S(2-) ions to polysulfide ions in aqueous solution with a Pt-modified CdS photocatalyst. The battery can deliver a specific capacity of 792 mAh g(-1) during 2 h photocharging process with a discharge potential of around 2.53 V versus Li(+)/Li. A specific capacity of 199 mAh g(-1), reaching the level of conventional lithium-ion batteries, can be achieved within 10 min photocharging. Moreover, the charging process of the battery can proceed under natural sunlight irradiation. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Preparation of Advanced CuO Nanowires/Functionalized Graphene Composite Anode Material for Lithium Ion Batteries

PubMed Central

Zhang, Jin; Wang, Beibei; Zhou, Jiachen; Xia, Ruoyu; Chu, Yingli; Huang, Jia

2017-01-01

The copper oxide (CuO) nanowires/functionalized graphene (f-graphene) composite material was successfully composed by a one-pot synthesis method. The f-graphene synthesized through the Birch reduction chemistry method was modified with functional group “–(CH2)5COOH”, and the CuO nanowires (NWs) were well dispersed in the f-graphene sheets. When used as anode materials in lithium-ion batteries, the composite exhibited good cyclic stability and decent specific capacity of 677 mA·h·g−1 after 50 cycles. CuO NWs can enhance the lithium-ion storage of the composites while the f-graphene effectively resists the volume expansion of the CuO NWs during the galvanostatic charge/discharge cyclic process, and provide a conductive paths for charge transportation. The good electrochemical performance of the synthesized CuO/f-graphene composite suggests great potential of the composite materials for lithium-ion batteries anodes. PMID:28772432

Structural studies of lead lithium borate glasses doped with silver oxide.

PubMed

Coelho, João; Freire, Cristina; Hussain, N Sooraj

2012-02-01

Silver oxide doped lead lithium borate (LLB) glasses have been prepared and characterized. Structural and composition characterization were accessed by XRD, FTIR, Raman, SEM and EDS. Results from FTIR and Raman spectra indicate that Ag(2)O acts as a network modifier even at small quantities by converting three coordinated to four coordinated boron atoms. Other physical properties, such as density, molar volume and optical basicity are also evaluated. Furthermore, they are also affected by the silver oxide composition. Copyright © 2011 Elsevier B.V. All rights reserved.

Effects of Electrospun Carbon Nanofibers' Interlayers on High-Performance Lithium-Sulfur Batteries.

PubMed

Gao, Tianji; Le, TrungHieu; Yang, Ying; Yu, Zhihao; Huang, Zhenghong; Kang, Feiyu

2017-03-31

Two different interlayers were introduced in lithium-sulfur batteries to improve the cycling stability with sulfur loading as high as 80% of total mass of cathode. Melamine was recommended as a nitrogen-rich (N-rich) amine component to synthesize a modified polyacrylic acid (MPAA). The electrospun MPAA was carbonized into N-rich carbon nanofibers, which were used as cathode interlayers, while carbon nanofibers from PAA without melamine was used as an anode interlayer. At the rate of 0.1 C, the initial discharge capacity with two interlayers was 983 mAh g -1 , and faded down to 651 mAh g -1 after 100 cycles with the coulombic efficiency of 95.4%. At the rate of 1 C, the discharge capacity was kept to 380 mAh g -1 after 600 cycles with a coulombic efficiency of 98.8%. It apparently demonstrated that the cathode interlayer is extremely effective at shutting down the migration of polysulfide ions. The anode interlayer induced the lithium ions to form uniform lithium metal deposits confined on the fiber surface and in the bulk to strengthen the cycling stability of the lithium metal anode.

Two-cation competition in ionic-liquid-modified electrolytes for lithium ion batteries.

PubMed

Lee, Sang-Young; Yong, Hyun Hang; Lee, Young Joo; Kim, Seok Koo; Ahn, Soonho

2005-07-21

It is a common observation that when ionic liquids are added to electrolytes the performances of lithium ion cells become poor, while the thermal safeties of the electrolytes might be improved. In this study, this behavior is investigated based on the kinetics of ionic diffusion. As a model ionic liquid, we chose butyldimethylimidazolium hexafluorophosphate (BDMIPF(6)). The common solvent was propylene carbonate (PC), and lithium hexafluorophosphate (LiPF(6)) was selected as the lithium conducting salt. Ionic diffusion coefficients are estimated by using a pulsed field gradient NMR technique. From a basic study on the model electrolytes (BDMIPF(6) in PC, LiPF(6) in PC, and BDMIPF(6) + LiPF(6) in PC), it was found that the BDMI(+) from BDMIPF(6) shows larger diffusion coefficients than the Li(+) from LiPF(6). However, the anionic (PF(6)(-)) diffusion coefficients present little difference between the model electrolytes. The higher diffusion coefficient of BDMI(+) than that of Li(+) suggests that the poor C-rate performance of lithium ion cells containing ionic liquids as an electrolyte component can be attributed to the two-cation competition between Li(+) and BDMI(+).

Tellurium speciation analysis using hydride generation in situ trapping electrothermal atomic absorption spectrometry and ruthenium or palladium modified graphite tubes.

PubMed

Yildirim, Emrah; Akay, Pınar; Arslan, Yasin; Bakirdere, Sezgin; Ataman, O Yavuz

2012-12-15

Speciation of tellurium can be achieved by making use of different kinetic behaviors of Te(IV) and Te(VI) upon their reaction with sodium borohydride using hydride generation. While Te(IV) can form H(2)Te, Te(VI) will not form any volatile species during the course of hydride formation and measurement by atomic absorption spectrometry. Quantitative reduction of Te(VI) was achieved through application of a microwave assisted prereduction of Te(VI) in 6.0 mol/L HCl solution. Enhanced sensitivity was achieved by in situ trapping of the generated H(2)Te species in a previously heated graphite furnace whose surface was modified using Pd or Ru. Overall efficiency for in situ trapping in pyrolytically coated graphite tube surface was found to be 15% when volatile analyte species are trapped for 60s at 300°C. LOD and LOQ values were calculated as 0.086 ng/mL and 0.29 ng/mL, respectively. Efficiency was increased to 46% and 36% when Pd and Ru surface modifiers were used, respectively. With Ru modified graphite tube 173-fold enhancement was obtained over 180 s trapping period with respect to ETAAS; the tubes could be used for 250 cycles. LOD values were 0.0064 and 0.0022 ng/mL for Pd and Ru treated ETAAS systems, respectively, for 180 s collection of 9.6 mL sample solution. Copyright © 2012 Elsevier B.V. All rights reserved.

Structure and Performance of Epoxy Resin Cladded Graphite Used as Anode

NASA Astrophysics Data System (ADS)

Zhou, Zhentao; Li, Haijun

This paper is concerning to prepare modified natural graphite which is low-cost and advanced materials used as lithium ion battery anode using the way of cladding natural graphite with epoxy resin. The results shows that the specific capacity and circular performance of the modified natural graphite, which is prepared in the range of 600°C and 1000°C, have been apparently improved compare with the not-modified natural graphite. The first reversible capacity of the modified natural graphite is 338mAh/g and maintain more than 330mAh/g after 20 charge/discharge circles.

Development of a solar powered residential air conditioner (General optimization)

NASA Technical Reports Server (NTRS)

Lowen, D. J.

1976-01-01

A commercially available 3-ton residential Lithium Bromide (LiBr) absorption air conditioner was modified for use with lower temperature solar heated water. The modification included removal of components such as the generator, concentration control chamber, liquid trap, and separator; and the addition of a Chrysler designed generator, an off-the-shelf LiBr-solution pump. The design goal of the modified unit was to operate with water as the heat-transfer fluid at a target temperature of 85 C (185 F), 29.4 C (85 F) cooling water inlet, producing 10.5 kW (3 tons) of cooling. Tests were performed on the system before and after modification to provide comparative data. At elevated temperatures (96 C, 205 F), the test results show that Lithium Bromide was carried into the condenser due to the extremely violent boiling and degraded the evaporator performance.

Fabricate heterojunction diode by using the modified spray pyrolysis method to deposit nickel-lithium oxide on indium tin oxide substrate.

PubMed

Wu, Chia-Ching; Yang, Cheng-Fu

2013-06-12

P-type lithium-doped nickel oxide (p-LNiO) thin films were deposited on an n-type indium tin oxide (ITO) glass substrate using the modified spray pyrolysis method (SPM), to fabricate a transparent p-n heterojunction diode. The structural, optical, and electrical properties of the p-LNiO and ITO thin films and the p-LNiO/n-ITO heterojunction diode were characterized by field emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), UV-visible spectroscopy, Hall effect measurement, and current-voltage (I-V) measurements. The nonlinear and rectifying I-V properties confirmed that a heterojunction diode characteristic was successfully formed in the p-LNiO/n-ITO (p-n) structure. The I-V characteristic was dominated by space-charge-limited current (SCLC), and the Anderson model demonstrated that band alignment existed in the p-LNiO/n-ITO heterojunction diode.

Final Technical Report for GO15056 Millennium Cell: Development of an Advanced Chemical Hydrogen Storage and Generation System

DOE Office of Scientific and Technical Information (OSTI.GOV)

Moreno, Oscar

The objectives of this project are to increase system storage capacity by improving hydrogen generation from concentrated sodium borohydride, with emphasis on reactor and system engineering; to complete a conceptual system design based on sodium borohydride that will include key technology improvements to enable a hydrogen fuel system that will meet the systembased storage capacity of 1.2 kWh/L (36 g H2/L) and 1.5 kWh/kg (45 g H2/kg), by the end of FY 2007; and to utilize engineering expertise to guide Center research in both off-board chemical hydride regeneration and on-board hydrogen generation systems.

Controlled Synthesis and Magnetic Properties of Uniform Hierarchical Polyhedral α-Fe2O3 Particles

NASA Astrophysics Data System (ADS)

Long, Nguyen Viet; Yang, Yong; Thi, Cao Minh; Phuc, Le Hong; Nogami, Masayuki

2017-06-01

The controlled synthesis of uniform hierarchical polyhedral iron (Fe) micro-/nanoscale oxide particles with the α-Fe2O3 structure is presented. The hierarchical polyhedral iron oxide particles were synthesized by modified polyol methods with sodium borohydride as a powerful and efficient reducing agent. A critical heat treatment process used during the synthesis allowed for the interesting formation of α-Fe2O3 hematite with a micro-/nanoscale structure. The structure and weak ferromagnetism of the α-Fe2O3 particles were investigated by x-ray diffraction with whole pattern fitting and Rietveld refinement, scanning electron microscopy, and by vibrating sample magnetometry. The as-prepared α-Fe2O3 particles and the three dimensional models presented have promising practical applications for energy storage and conversion in batteries, capacitors, and fuel cells, and related spintronic devices and technologies.

Fixing the Big Bang Theory's Lithium Problem

NASA Astrophysics Data System (ADS)

Kohler, Susanna

2017-02-01

How did our universe come into being? The Big Bang theory is a widely accepted and highly successful cosmological model of the universe, but it does introduce one puzzle: the cosmological lithium problem. Have scientists now found a solution?Too Much LithiumIn the Big Bang theory, the universe expanded rapidly from a very high-density and high-temperature state dominated by radiation. This theory has been validated again and again: the discovery of the cosmic microwave background radiation and observations of the large-scale structure of the universe both beautifully support the Big Bang theory, for instance. But one pesky trouble-spot remains: the abundance of lithium.The arrows show the primary reactions involved in Big Bang nucleosynthesis, and their flux ratios, as predicted by the authors model, are given on the right. Synthesizing primordial elements is complicated! [Hou et al. 2017]According to Big Bang nucleosynthesis theory, primordial nucleosynthesis ran wild during the first half hour of the universes existence. This produced most of the universes helium and small amounts of other light nuclides, including deuterium and lithium.But while predictions match the observed primordial deuterium and helium abundances, Big Bang nucleosynthesis theory overpredicts the abundance of primordial lithium by about a factor of three. This inconsistency is known as the cosmological lithium problem and attempts to resolve it using conventional astrophysics and nuclear physics over the past few decades have not been successful.In a recent publicationled by Suqing Hou (Institute of Modern Physics, Chinese Academy of Sciences) and advisorJianjun He (Institute of Modern Physics National Astronomical Observatories, Chinese Academy of Sciences), however, a team of scientists has proposed an elegant solution to this problem.Time and temperature evolution of the abundances of primordial light elements during the beginning of the universe. The authors model (dotted lines) successfully predicts a lower abundance of the beryllium isotope which eventually decays into lithium relative to the classical Maxwell-Boltzmann distribution (solid lines), without changing the predicted abundances of deuterium or helium. [Hou et al. 2017]Questioning StatisticsHou and collaborators questioned a key assumption in Big Bang nucleosynthesis theory: that the nuclei involved in the process are all in thermodynamic equilibrium, and their velocities which determine the thermonuclear reaction rates are described by the classical Maxwell-Boltzmann distribution.But do nuclei still obey this classical distribution in the extremely complex, fast-expanding Big Bang hot plasma? Hou and collaborators propose that the lithium nuclei dont, and that they must instead be described by a slightly modified version of the classical distribution, accounted for using whats known as non-extensive statistics.The authors show that using the modified velocity distributions described by these statistics, they can successfully predict the observed primordial abundances of deuterium, helium, and lithium simultaneously. If this solution to the cosmological lithium problem is correct, the Big Bang theory is now one step closer to fully describing the formation of our universe.CitationS. Q. Hou et al 2017 ApJ 834 165. doi:10.3847/1538-4357/834/2/165

A new family of metal borohydride guanidinate complexes: Synthesis, structures and hydrogen-storage properties

NASA Astrophysics Data System (ADS)

Wu, Hui; Zhou, Xiuquan; Rodriguez, Efrain E.; Zhou, Wei; Udovic, Terrence J.; Yildirim, Taner; Rush, John J.

2016-10-01

We report on a new class of complex hydrides: borohydride guanidinate complexes (MBH4·nCN3H5, M=Li, Mg, and Ca). They can be prepared via facile solid-state synthesis routes. Their crystal structures were successfully determined using a combination of X-ray diffraction, first-principles calculations and neutron vibrational spectroscopy. Among these compounds, Mg(BH4)2·6CN3H5 is composed of large complex Mg[CN3H5]62+ cations and surrounding BH4- ions, while Ca(BH4)2·2CN3H5 possesses layers of corner-sharing Ca[BH4]4(CN3H5)2 octahedra. Our dehydrogenation results show that ≈10 wt% hydrogen can be released from MBH4·nCN3H5 (M=Li, Mg, and Ca) at moderate temperatures with minimal ammonia and diborane contamination thanks to the synergistic effect of C-N bonds from guanidine and hydridic H from borohydrides leading to a weakening of the N-H bonds, thus impeding ammonia gas liberation. Further tuning the dehydrogenation with different cation species indicates that Mg(BH4)2·nCN3H5 can exhibit the optimum properties with nearly thermally neutral dehydrogenation and very high purity hydrogen release.

Boronic acid recognition of non-interacting carbohydrates for biomedical applications: increasing fluorescence signals of minimally interacting aldoses and sucralose.

PubMed

Resendez, Angel; Halim, Md Abdul; Singh, Jasmeet; Webb, Dominic-Luc; Singaram, Bakthan

2017-11-22

To address carbohydrates that are commonly used in biomedical applications with low binding affinities for boronic acid based detection systems, two chemical modification methods were utilized to increase sensitivity. Modified carbohydrates were analyzed using a two component fluorescent probe based on boronic acid-appended viologen-HPTS (4,4'-o-BBV). Carbohydrates normally giving poor signals (fucose, l-rhamnose, xylose) were subjected to sodium borohydride (NaBH 4 ) reduction in ambient conditions for 1 h yielding the corresponding sugar alcohols from fucose, l-rhamnose and xylose in essentially quantitative yields. Compared to original aldoses, apparent binding affinities were increased 4-25-fold. The chlorinated sweetener and colon permeability marker sucralose (Splenda), otherwise undetectable by boronic acids, was dechlorinated to a detectable derivative by reactive oxygen and hydroxide intermediates by the Fenton reaction or by H 2 O 2 and UV light. This method is specific to sucralose as other common sugars, such as sucrose, do not contain any carbon-chlorine bonds. Significant fluorescence response was obtained for chemically modified sucralose with the 4,4'-o-BBV-HPTS probe system. This proof of principle can be applied to biomedical applications, such as gut permeability, malabsorption, etc.

Electrochemical characterisation of a lithium-ion battery electrolyte based on mixtures of carbonates with a ferrocene-functionalised imidazolium electroactive ionic liquid.

PubMed

Forgie, John C; El Khakani, Soumia; MacNeil, Dean D; Rochefort, Dominic

2013-05-28

Electrolytic solutions of lithium-ion batteries can be modified with additives to improve their stability and safety. Electroactive molecules can be used as such additives to act as an electron (redox) shuttle between the two electrodes to prevent overcharging. The electroactive ionic liquid, 1-ferrocenylmethyl-3-methylimidazolium bis(trifluoromethanesulfonyl)amide (TFSI), was synthesised and its electrochemical properties were investigated when diluted with ethylene carbonate-diethyl carbonate solvent at various concentrations. Cyclic voltammetry data were gathered to determine the redox potential, diffusion coefficient and heterogeneous rate constants of the electroactive imidazolium TFSI ionic liquid in the carbonate solution. The properties of this molecule as an additive in lithium battery electrolytes were studied in standard coin cells with a metallic Li anode and a Li4Ti5O12 cathode.

Chemiluminescence: An Illuminating Experiment

ERIC Educational Resources Information Center

Gafney, Harry D.; Adamson, Arthur W.

1975-01-01

Describes an experiment in which luminescence is observed during a reaction between sodium borohydride and trisbipyridalruthenium (III). Includes a discussion of the theory of chemiluminescence. (MLH)

Cation-substituted spinel oxide and oxyfluoride cathodes for lithium ion batteries

DOEpatents

Manthiram, Arumugam; Choi, Wongchang

2014-05-13

The present invention includes compositions and methods of making cation-substituted and fluorine-substituted spinel cathode compositions by firing a LiMn.sub.2-y-zLi.sub.yM.sub.zO.sub.4 oxide with NH.sub.4HF.sub.2 at low temperatures of between about 300 and 700.degree. C. for 2 to 8 hours and a .eta. of more than 0 and less than about 0.50, mixed two-phase compositions consisting of a spinel cathode and a layered oxide cathode, and coupling them with unmodified or surface modified graphite anodes in lithium ion cells.

The structural studies of vanadium substituted lithium-bismuth-boro-tellurite glass

NASA Astrophysics Data System (ADS)

Madhu, A.; Eraiah, B.

2018-05-01

The structural studies of vanadium substituted lithium-bismuth-boro-tellurite glass is successfully prepared and certain analysis like XRD,FTIR,DTA/TGA with density, molar volume are done. The amorphous phase has been identified based on X-ray diffraction analysis. The vanadium oxide plays the role as a glass-modifier and influences on BO3 ↔ BO4 conversion. The observed nonlinear variation in Tg with vanadium oxide increase, it reflects structural changes. The nonlinear variation of density and molar volume can be attributed to vanadium oxide incorporation have increased the number of Non-bridging oxygen (NBO'S).

Interfacial strain effects on lithium diffusion pathways in the spinel solid electrolyte Li-doped MgAl2O4

NASA Astrophysics Data System (ADS)

O'Rourke, Conn; Morgan, Benjamin J.

2018-04-01

The (Li,Al)-codoped magnesium spinel (LixMg1 -2 xAl2 +xO4 ) is a solid lithium-ion electrolyte with potential use in all-solid-state lithium-ion batteries. The spinel structure means that interfaces with spinel electrodes, such as LiyMn2O4 and Li4 +3 zTi5O12 , may be lattice matched, with potentially low interfacial resistances. Small lattice parameter differences across a lattice-matched interface are unavoidable, causing residual epitaxial strain. This strain potentially modifies lithium diffusion near the electrolyte-electrode interface, contributing to interfacial resistance. Here, we report a density functional theory study of strain effects on lithium diffusion pathways for (Li,Al)-codoped magnesium spinel, for xLi=0.25 and xLi=0.5 . We have calculated diffusion profiles for the unstrained materials, and for isotropic and biaxial tensile strains of up to 6 % , corresponding to {100 } epitaxial interfaces with LiyMn2O4 and Li4 +3 zTi5O12 . We find that isotropic tensile strain reduces lithium diffusion barriers by as much as 0.32 eV , with typical barriers reduced by ˜0.1 eV. This effect is associated with increased volumes of transitional octahedral sites, and broadly follows qualitative changes in local electrostatic potentials. For biaxial (epitaxial) strain, which more closely approximates strain at a lattice-matched electrolyte-electrode interface, changes in octahedral site volumes and in lithium diffusion barriers are much smaller than under isotropic strain. Typical barriers are reduced by only ˜0.05 eV. Individual effects, however, depend on the pathway considered and the relative strain orientation. These results predict that isotropic strain strongly affects ionic conductivities in (Li,Al)-codoped magnesium spinel electrolytes, and that tensile strain is a potential route to enhanced lithium transport. For a lattice-matched interface with candidate spinel-structured electrodes, however, epitaxial strain has a small, but complex, effect on lithium diffusion barriers.

Direct synthesis of magnesium borohydride

DOEpatents

Ronnebro, Ewa Carin Ellinor [Kennewick, WA; Severa, Godwin [Honolulu, HI; Jensen, Craig M [Kailua, HI

2012-04-03

A method is disclosed for directly preparing an alkaline earth metal borohydride, i.e. Mg(BH.sub.4).sub.2, from the alkaline earth metal boride MgB.sub.2 by hydrogenating the MgB.sub.2 at an elevated temperature and pressure. The boride may also be doped with small amounts of a metal chloride catalyst such as TiCl.sub.3 and/or NiCl.sub.2. The process provides for charging MgB.sub.2 with high pressure hydrogen above at least 70 MPa while simultaneously heating the material to about 350.degree. C. to about 400.degree. C. The method is relatively simple and inexpensive and provides a reversible hydride compound having a hydrogen capacity of at least 11 wt %.

A novel approach to isoindolo[2,1-a]indol-6-ones.

PubMed

Duncanson, Philip; Cheong, Yuen-Ki; Motevalli, Majid; Griffiths, D Vaughan

2012-06-07

A convenient route to isoindolo[2,1-a]indol-6-ones has been developed starting from the appropriate 2-(N-phthaloyl)benzoic acids. Formation of the acid chlorides with thionyl chloride followed by heating with triethyl phosphite in a suitable solvent resulted in a multistep reaction giving tetracyclic β-ketophosphonates that on reduction with sodium borohydride gave the required indolones in good overall yields. Analogous β-ketophosphonates were also prepared starting with N,N-(1,8-naphthaloyl)-2-aminobenzoic acid and 2-(2,5-dioxo-2,5-dihydro-1H-pyrrol-1-yl)benzoic acids although of these only the naphthaloyl product could be reduced with sodium borohydride without cleaving the amide bond in the ring system.

Mesoporous carbon-coated LiFePO4 nanocrystals co-modified with graphene and Mg2+ doping as superior cathode materials for lithium ion batteries.

PubMed

Wang, Bo; Xu, Binghui; Liu, Tiefeng; Liu, Peng; Guo, Chenfeng; Wang, Shuo; Wang, Qiuming; Xiong, Zhigang; Wang, Dianlong; Zhao, X S

2014-01-21

In this work, mesoporous carbon-coated LiFePO4 nanocrystals further co-modified with graphene and Mg(2+) doping (G/LFMP) were synthesized by a modified rheological phase method to improve the speed of lithium storage as well as cycling stability. The mesoporous structure of LiFePO4 nanocrystals was designed and realized by introducing the bead milling technique, which assisted in forming sucrose-pyrolytic carbon nanoparticles as the template for generating mesopores. For comparison purposes, samples modified only with graphene (G/LFP) or Mg(2+) doping (LFMP) as well as pure LiFePO4 (LFP) were also prepared and investigated. Microscopic observation and nitrogen sorption analysis have revealed the mesoporous morphologies of the as-prepared composites. X-ray diffraction (XRD) and Rietveld refinement data demonstrated that the Mg-doped LiFePO4 is a single olivine-type phase and well crystallized with shortened Fe-O and P-O bonds and a lengthened Li-O bond, resulting in an enhanced Li(+) diffusion velocity. Electrochemical properties have also been investigated after assembling coin cells with the as-prepared composites as the cathode active materials. Remarkably, the G/LFMP composite has exhibited the best electrochemical properties, including fast lithium storage performance and excellent cycle stability. That is because the modification of graphene provided active sites for nuclei, restricted the in situ crystallite growth, increased the electronic conductivity and reduced the interface reaction current density, while, Mg(2+) doping improved the intrinsically electronic and ionic transfer properties of LFP crystals. Moreover, in the G/LFMP composite, the graphene component plays the role of "cushion" as it could quickly realize capacity response, buffering the impact to LFMP under the conditions of high-rate charging or discharging, which results in a pre-eminent rate capability and cycling stability.

Nanoprocess and nanoscale surface functionalization on cathode materials for advanced lithium-ion batteries.

PubMed

Alaboina, Pankaj Kumar; Uddin, Md-Jamal; Cho, Sung-Jin

2017-10-26

Nanotechnology-driven development of cathode materials is an essential part to revolutionize the evolution of the next generation lithium ion batteries. With the progress of nanoprocess and nanoscale surface modification investigations on cathode materials in recent years, the advanced battery technology future seems very promising - Thanks to nanotechnology. In this review, an overview of promising nanoscale surface deposition methods and their significance in surface functionalization on cathodes is extensively summarized. Surface modified cathodes are provided with a protective layer to overcome the electrochemical performance limitations related to side reactions with electrolytes, reduce self-discharge reactions, improve thermal and structural stability, and further enhance the overall battery performance. The review addresses the importance of nanoscale surface modification on battery cathodes and concludes with a comparison of the different nanoprocess techniques discussed to provide a direction in the race to build advanced lithium-ion batteries.

Benchmarking lithium amide versus amine bonding by charge density and energy decomposition analysis arguments.

PubMed

Engelhardt, Felix; Maaß, Christian; Andrada, Diego M; Herbst-Irmer, Regine; Stalke, Dietmar

2018-03-28

Lithium amides are versatile C-H metallation reagents with vast industrial demand because of their high basicity combined with their weak nucleophilicity, and they are applied in kilotons worldwide annually. The nuclearity of lithium amides, however, modifies and steers reactivity, region- and stereo-selectivity and product diversification in organic syntheses. In this regard, it is vital to understand Li-N bonding as it causes the aggregation of lithium amides to form cubes or ladders from the polar Li-N covalent metal amide bond along the ring stacking and laddering principle. Deaggregation, however, is more governed by the Li←N donor bond to form amine adducts. The geometry of the solid state structures already suggests that there is σ- and π-contribution to the covalent bond. To quantify the mutual influence, we investigated [{(Me 2 NCH 2 ) 2 (C 4 H 2 N)}Li] 2 ( 1 ) by means of experimental charge density calculations based on the quantum theory of atoms in molecules (QTAIM) and DFT calculations using energy decomposition analysis (EDA). This new approach allows for the grading of electrostatic Li + N - , covalent Li-N and donating Li←N bonding, and provides a way to modify traditional widely-used heuristic concepts such as the -I and +I inductive effects. The electron density ρ ( r ) and its second derivative, the Laplacian ∇ 2 ρ ( r ), mirror the various types of bonding. Most remarkably, from the topological descriptors, there is no clear separation of the lithium amide bonds from the lithium amine donor bonds. The computed natural partial charges for lithium are only +0.58, indicating an optimal density supply from the four nitrogen atoms, while the Wiberg bond orders of about 0.14 au suggest very weak bonding. The interaction energy between the two pincer molecules, (C 4 H 2 N) 2 2- , with the Li 2 2+ moiety is very strong ( ca. -628 kcal mol -1 ), followed by the bond dissociation energy (-420.9 kcal mol -1 ). Partitioning the interaction energy into the Pauli (Δ E Pauli ), dispersion (Δ E disp ), electrostatic (Δ E elstat ) and orbital (Δ E orb ) terms gives a 71-72% ionic and 25-26% covalent character of the Li-N bond, different to the old dichotomy of 95 to 5%. In this regard, there is much more potential to steer the reactivity with various substituents and donor solvents than has been anticipated so far.

High Substitution Rate in TiO 2 Anatase Nanoparticles with Cationic Vacancies for Fast Lithium Storage

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Wei; Corradini, Dario; Body, Monique

2015-06-24

Doping is generally used to tune and enhance the properties of metal oxides. However, their chemical composition cannot be readily modified beyond low dopant amounts without disrupting the crystalline atomic structure. In the case of anatase TiO 2, we introduce a new solution-based chemical route allowing the composition to be significantly modified, substituting the divalent O 2- anions by monovalent F- and OH- anions resulting in the formation of cationic Ti 4+ vacancies (square) whose concentration can be controlled by the reaction temperature. The resulting polyanionic anatase has the general composition Ti 1-x-y square x+yO 2-4(x+y)F 4x(OH) 4y, reaching vacancymore » concentrations of up to 22%, i.e., Ti 0.78 square 0.22O 1.12F 0.4(OH) 0.48. Solid-state F-19 NMR spectroscopy reveals that fluoride ions can accommodate up to three different environments, depending on Ti and vacancies (i.e. Ti 3-F, Ti- 2 square 1-F, and Ti- 1 square 2-F), with a preferential location close to vacancies. DFT calculations further confirm the fluoride/vacancy ordering. When its characteristics were evaluated as an electrode for reversible Li-ion storage, the material shows a modified lithium reaction mechanism, which has been rationalized by the occurrence of cationic vacancies acting as additional lithium hosting sites within the anatase framework. Finally, the material shows a fast discharging/charging behavior, compared to TiO 2, highlighting the benefits of the structural modifications and paving the way for the design of advanced electrode materials, based on a defect mediated mechanism.« less

Rotating disk electrode study of borohydride oxidation in a molten eutectic electrolyte and advancements in the intermediate temperature borohydride battery

NASA Astrophysics Data System (ADS)

Wang, Andrew; Gyenge, Előd L.

2017-08-01

The electrode kinetics of the NaBH4 oxidation reaction (BOR) in a molten NaOH-KOH eutectic mixture is investigated by rotating disk electrode (RDE) voltammetry on electrochemically oxidized Ni at temperatures between 458 K and 503 K. The BH4- diffusion coefficient in the molten alkali eutectic together with the BOR activation energy, exchange current density, transfer coefficient and number of electrons exchanged, are determined. Electrochemically oxidized Ni shows excellent BOR electrocatalytic activity with a maximum of seven electrons exchanged and a transfer coefficient up to one. X-ray photoelectron spectroscopy (XPS) reveals the formation of NiO as the catalytically active species. The high faradaic efficiency and BOR rate on oxidized Ni anode in the molten electrolyte compared to aqueous alkaline electrolytes is advantageous for power sources. A novel molten electrolyte battery design is investigated using dissolved NaBH4 at the anode and immobilized KIO4 at the cathode. This battery produces a stable open-circuit cell potential of 1.04 V, and a peak power density of 130 mW cm-2 corresponding to a superficial current density of 160 mA cm-2 at 458 K. With further improvements and scale-up borohydride molten electrolyte batteries and fuel cells could be integrated with thermal energy storage systems.

Synthesis of noble metal nanoparticles

NASA Astrophysics Data System (ADS)

Bahadory, Mozhgan

Improved methods were developed for the synthesis of noble metal nanoparticles. Laboratory experiments were designed for introducing of nanotechnology into the undergraduate curriculum. An optimal set of conditions for the synthesis of clear yellow colloidal silver was investigated. Silver nanoparticles were obtained by borohydride reduction of silver nitrate, a method which produces particles with average size of 12+/-2 nm, determined by Transmission Electron Microscopy (TEM). The plasmon absorbance is at 397 nm and the peak width at half maximum (PWHM) is 70-75 nm. The relationship between aggregation and optical properties was determined along with a method to protect the particles using polyvinylpyrrolidone (PVP). A laboratory experiment was designed in which students synthesize yellow colloidal silver, estimate particle size using visible spectroscopy, and study aggregation effects. The synthesis of the less stable copper nanoparticles is more difficult because copper nanopaticles are easily oxidized. Four methods were used for the synthesis of copper nanoparticles, including chemical reduction with sodium borohydride, sodium borohydride with potassium iodide, isopropyl alcohol with cetyltrimethylammonium bormide (CTAB) and reducing sugars. The latter method was also the basis for an undergraduate laboratory experiment. For each reaction, the dependence of stability of the copper nanoparticles on reagent concentrations, additives, relative amounts of reactants, and temperature is explored. Atomic force microscopy (AFM), TEM and UV-Visible Spectroscopy were used to characterize the copper nanoparticles. A laboratory experiment to produce copper nanoparticles from household chemicals was developed.

Experimental advances and preliminary mathematical modeling of the Swiss-roll mixed-reactant direct borohydride fuel cell

NASA Astrophysics Data System (ADS)

Aziznia, Amin; Oloman, Colin W.; Gyenge, Előd L.

2014-11-01

The Swiss-roll single-cell mixed reactant (SR-MRFC) borohydride - oxygen fuel cell equipped with Pt/carbon cloth 3D anode and either MnO2 or Ag gas-diffusion cathodes is investigated by a combination of experimental studies and preliminary mathematical modeling of the polarization curve. We investigate the effects of four variables: cathode side metallic mesh fluid distributor, separator type (Nafion 112® vs. Viledon®), cathode catalyst (MnO2 vs. Ag), and the hydrophilic pore volume fraction of the gas-diffusion cathode. Using a two-phase feed of alkaline borohydride solution (1 M NaBH4 - 2 M NaOH) and O2 gas in an SR-MRFC equipped with Pt/C 3D anode, MnO2 gas diffusion cathode, Viledon® porous diaphragm, expanded mesh cathode-side fluid distributor, the maximum superficial power density is 2230 W m-2 at 323 K and 105 kPa(abs). The latter superficial power density is almost 3.5 times higher than our previously reported superficial power density for the same catalyst combinations. Furthermore, with a Pt anode and Ag cathode catalyst combination, a superficial power density of 2500 W m-2 is achieved with superior performance durability compared to the MnO2 cathode. The fuel cell results are substantiated by impedance spectroscopy analysis and preliminary mathematical model predictions based on mixed potential theory.

Toward a lithium-"air" battery: the effect of CO2 on the chemistry of a lithium-oxygen cell.

PubMed

Lim, Hyung-Kyu; Lim, Hee-Dae; Park, Kyu-Young; Seo, Dong-Hwa; Gwon, Hyeokjo; Hong, Jihyun; Goddard, William A; Kim, Hyungjun; Kang, Kisuk

2013-07-03

Lithium-oxygen chemistry offers the highest energy density for a rechargeable system as a "lithium-air battery". Most studies of lithium-air batteries have focused on demonstrating battery operations in pure oxygen conditions; such a battery should technically be described as a "lithium-dioxygen battery". Consequently, the next step for the lithium-"air" battery is to understand how the reaction chemistry is affected by the constituents of ambient air. Among the components of air, CO2 is of particular interest because of its high solubility in organic solvents and it can react actively with O2(-•), which is the key intermediate species in Li-O2 battery reactions. In this work, we investigated the reaction mechanisms in the Li-O2/CO2 cell under various electrolyte conditions using quantum mechanical simulations combined with experimental verification. Our most important finding is that the subtle balance among various reaction pathways influencing the potential energy surfaces can be modified by the electrolyte solvation effect. Thus, a low dielectric electrolyte tends to primarily form Li2O2, while a high dielectric electrolyte is effective in electrochemically activating CO2, yielding only Li2CO3. Most surprisingly, we further discovered that a high dielectric medium such as DMSO can result in the reversible reaction of Li2CO3 over multiple cycles. We believe that the current mechanistic understanding of the chemistry of CO2 in a Li-air cell and the interplay of CO2 with electrolyte solvation will provide an important guideline for developing Li-air batteries. Furthermore, the possibility for a rechargeable Li-O2/CO2 battery based on Li2CO3 may have merits in enhancing cyclability by minimizing side reactions.

Intercalation of Lithium in Pitch-Based Graphitized Carbon Fibers Chemically Modified by Fluorine: Soft Carbon With or Without an Oxide Surface

NASA Technical Reports Server (NTRS)

Hung, Ching-Chen; Prisko, Aniko

1999-01-01

The effects of carbon structure and surface oxygen on the carbon's performance as the anode in lithium-ion battery were studied. Two carbon materials were used for the electrochemical tests: soft carbon made from defluorination of graphite fluoride, and the carbon precursor from which the graphite fluoride was made. In this research the precursor was graphitized carbon fiber P-100. It was first fluorinated to form CF(0.68), then defluorinated slowly at 350 to 450 C in bromoform, and finally heated in 1000 C nitrogen before exposed to room temperature air, producing disordered soft carbon having basic surface oxides. This process caused very little carbon loss. The electrochemical test involved cycles of lithium intercalation and deintercalation using C/saturated LiI-50/50 (vol %) EC and DMC/Li half cell. The cycling test had four major results. (1) The presence of a basic oxide surface may prevent solvent from entering the carbon structure and therefore prolong the carbon's cycle life for lithium intercalation-deintercalation. (2) The disordered soft carbon can store lithium through two different mechanisms. One of them is lithium intercalation. which gives the disordered carbon an electrochemical behavior similar to its more ordered graphitic precursor. The other is unknown in its chemistry, but is responsible for the high-N,oltage portion (less than 0.3V) of the charge-discharge curve. (3) Under certain conditions, the disordered carbon can store more lithium than its precursor. (4) These sample and its precursor can intercalate at 200 mA/g. and deintercalate at a rate of 2000 mA/g without significant capacity loss.

A transfer function type of simplified electrochemical model with modified boundary conditions and Padé approximation for Li-ion battery: Part 1. lithium concentration estimation

NASA Astrophysics Data System (ADS)

Yuan, Shifei; Jiang, Lei; Yin, Chengliang; Wu, Hongjie; Zhang, Xi

2017-06-01

To guarantee the safety, high efficiency and long lifetime for lithium-ion battery, an advanced battery management system requires a physics-meaningful yet computationally efficient battery model. The pseudo-two dimensional (P2D) electrochemical model can provide physical information about the lithium concentration and potential distributions across the cell dimension. However, the extensive computation burden caused by the temporal and spatial discretization limits its real-time application. In this research, we propose a new simplified electrochemical model (SEM) by modifying the boundary conditions for electrolyte diffusion equations, which significantly facilitates the analytical solving process. Then to obtain a reduced order transfer function, the Padé approximation method is adopted to simplify the derived transcendental impedance solution. The proposed model with the reduced order transfer function can be briefly computable and preserve physical meanings through the presence of parameters such as the solid/electrolyte diffusion coefficients (Ds&De) and particle radius. The simulation illustrates that the proposed simplified model maintains high accuracy for electrolyte phase concentration (Ce) predictions, saying 0.8% and 0.24% modeling error respectively, when compared to the rigorous model under 1C-rate pulse charge/discharge and urban dynamometer driving schedule (UDDS) profiles. Meanwhile, this simplified model yields significantly reduced computational burden, which benefits its real-time application.

Graphene-modified nanostructured vanadium pentoxide hybrids with extraordinary electrochemical performance for Li-ion batteries

DOE PAGES

Liu, Qi; Li, Zhe-Fei; Liu, Yadong; ...

2015-01-20

The long-standing issues of low intrinsic electronic conductivity, slow lithium-ion diffusion and irreversible phase transitions on deep discharge prevent the high specific capacity/energy (443 mAh g -1 and 1,550 Wh kg -1) vanadium pentoxide from being used as the cathode material in practical battery applications. Here we develop a method to incorporate graphene sheets into vanadium pentoxide nanoribbons via the sol–gel process. The resulting graphene-modified nanostructured vanadium pentoxide hybrids contain only 2 wt. % graphene, yet exhibits extraordinary electrochemical performance: a specific capacity of 438 mAh g -1, approaching the theoretical value (443 mAh g -1), a long cyclability andmore » significantly enhanced rate capability. Such performance is the result of the combined effects of the graphene on structural stability, electronic conduction, vanadium redox reaction and lithium-ion diffusion supported by various experimental studies. Finally, this method provides a new avenue to create nanostructured metal oxide/graphene materials for advanced battery applications.« less

Graphene nanosheets and polyacrylic acid grafted silicon composite anode for lithium ion batteries

NASA Astrophysics Data System (ADS)

Assresahegn, Birhanu Desalegn; Ossonon, Benjamin Diby; Bélanger, Daniel

2018-07-01

A silicon/graphene composite anode for lithium-ion batteries was fabricated with a high loading of Si by combining surface-modified silicon with graphene. The Si nanopowder was modified by a binder-like organic moeity (1-(bromoethyl) benzene and polyacrylic acid) grafted on the surface of hydrogenated silicon by diazonium chemistry and surface initiated atom transfer radical polymerization. The graphene was produced by electrochemical exfoliation of natural graphite. The optimum composite electrode prepared without a binder, with silicon loading as high as 85 wt% and a mass loading of 1.1 ± 0.1 mg cm-2 yielded a discharge capacity of 1020 mAh per gram of electrode mass (or 1200 mAh per gram of Si) after 586 charge/discharge cycles at a rate of 3.4 A g-1. It showed first cycle Coulombic efficiency of more than 90% in the absence of electrolyte additives at a current rate of 0.05 A g-1.

Nickel Hydroxide-Modified Sulfur/Carbon Composite as a High-Performance Cathode Material for Lithium Sulfur Battery.

PubMed

Niu, Xiao-Qing; Wang, Xiu-Li; Xie, Dong; Wang, Dong-Huang; Zhang, Yi-Di; Li, Yi; Yu, Ting; Tu, Jiang-Ping

2015-08-05

Tailored sulfur cathode is vital for the development of a high performance lithium-sulfur (Li-S) battery. A surface modification on the sulfur/carbon composite would be an efficient strategy to enhance the cycling stability. Herein, we report a nickel hydroxide-modified sulfur/conductive carbon black composite (Ni(OH)2@S/CCB) as the cathode material for the Li-S battery through the thermal treatment and chemical precipitation method. In this composite, the sublimed sulfur is stored in the CCB, followed by a surface modification of Ni(OH)2 nanoparticles with size of 1-2 nm. As a cathode for the Li-S battery, the as-prepared Ni(OH)2@S/CCB electrode exhibits better cycle stability and higher rate discharge capacity, compared with the bare S/CCB electrode. The improved performance is largely due to the introduction of Ni(OH)2 surface modification, which can effectively suppress the "shuttle effect" of polysulfides, resulting in enhanced cycling life and higher capacity.

Decomposition of ultrathin LiF cathode underlayer in organic-based devices evidenced by ToF-SIMS depth profiling

NASA Astrophysics Data System (ADS)

Pakhomov, Georgy L.; Drozdov, Mikhail N.; Travkin, Vlad V.; Bochkarev, Mikhail N.

2017-11-01

In this work we investigate the chemical composition of an archetypal thin-film organic device with the Ag/LiF cathode using the time-of-flight secondary ion mass spectrometry (ToF-SIMS) with depth profiling. The LiF cathode underlayer is partly decomposed because a significant amount of lithium is released into the bulk of the multilayer device. The released lithium diffuses all the way to the substrate, accumulating, as revealed by ToF-SIMS depth profiles, at the interfaces rather than uniformly doping the underlying layers. Particularly, the bottom anode becomes chemically modified.

Cation-substituted spinel oxide and oxyfluoride cathodes for lithium ion batteries

DOEpatents

Manthiram, Arumugam; Choi, Wonchang

2010-05-18

The present invention includes compositions and methods of making cation-substituted and fluorine-substituted spinel cathode compositions by firing a LiMn_2-y-zLi_yM_zO₄ oxide with NH₄HF₂ at low temperatures of between about 300 and 700.degree. C. for 2 to 8 hours and a .eta. of more than 0 and less than about 0.50, mixed two-phase compositions consisting of a spinel cathode and a layered oxide cathode, and coupling them with unmodified or surface modified graphite anodes in lithium ion cells.

Ca(BH 4) 2 as a simple tool for the preparation of thorium and uranium metallocene borohydride complexes: First synthesis and crystal structure of (C 5Me 5) 2Th(η 3-H 3BH) 2

DOE PAGES

Erickson, Karla A.; Scott, Brian Lindley; Kiplinger, Jaqueline Loetsch

2017-01-18

Here, calcium borohydride allows for the high-yielding synthesis of (C 5Me 5)2An(η 3-H 3BH) 2 (An = Th, U) by reaction with (C 5Me 5) 2AnCl 2 (An = Th, U). While a preparative synthesis of (C 5Me 5) 2U(η 3-H 3BH) 2 has been previously reported in the literature using K(C 5Me 5) and U(BH 4) 4, the use of Ca(BH 4) 2 is higher yielding and mild. Full characterization of the novel compound (C 5Me 5) 2Th(η 3-H 3BH) 2 is presented.

Ca(BH 4) 2 as a simple tool for the preparation of thorium and uranium metallocene borohydride complexes: First synthesis and crystal structure of (C 5Me 5) 2Th(η 3-H 3BH) 2

DOE Office of Scientific and Technical Information (OSTI.GOV)

Erickson, Karla A.; Scott, Brian Lindley; Kiplinger, Jaqueline Loetsch

Here, calcium borohydride allows for the high-yielding synthesis of (C 5Me 5)2An(η 3-H 3BH) 2 (An = Th, U) by reaction with (C 5Me 5) 2AnCl 2 (An = Th, U). While a preparative synthesis of (C 5Me 5) 2U(η 3-H 3BH) 2 has been previously reported in the literature using K(C 5Me 5) and U(BH 4) 4, the use of Ca(BH 4) 2 is higher yielding and mild. Full characterization of the novel compound (C 5Me 5) 2Th(η 3-H 3BH) 2 is presented.

Borohydride electro-oxidation in a molten alkali hydroxide eutectic mixture and a novel borohydride-periodate battery

NASA Astrophysics Data System (ADS)

Wang, Andrew; Gyenge, Előd L.

2015-05-01

The electrochemical oxidation of BH4- in a molten NaOH-KOH eutectic mixture (0.515:0.485 mole fractions), is investigated for the first time by cyclic voltammetry and electrochemical impedance spectroscopy. Anodically oxidized Ni is electrocatalytically more active than Pt for BH4- oxidation in the molten alkali electrolyte as shown by the more than three times higher exchange current density (i.e. 15.8 mA cm-2 vs. 4.6 mA cm-2 at 185 °C). Next the proof-of-concept for a novel BH4-/IO4- molten alkali electrolyte battery is presented. Using oxidized Ni mesh anode and Pt mesh cathode a maximum power density of 63 mW cm-2 is achieved at 185 °C.

Mechanical Deformation of a Lithium-Metal Anode Due to a Very Stiff Separator

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ferrese, A; Newman, J

2014-05-21

This work builds on the two-dimensional model presented by Ferrese et al. [J. Electrochem. Soc., 159, A1615 (2012)1, which captures the movement of lithium metal at the negative electrode during cycling in a Li-metal/LiCoO2 cell. In this paper, the separator is modeled as a dendrite-inhibiting polymer separator with an elastic modulus of 16 GPa. The separator resists the movement of lithium through the generation of stresses in the cell. These stresses affect the negative electrode through two mechanisms altering the thermodynamics of the negative electrode and deforming the negative electrode mechanically. From this analysis, we find that the dendrite-inhibiting separatormore » causes plastic and elastic deformation of the lithium at the negative electrode which flattens the electrode considerably when compared to the liquid-electrolyte case. This flattening of the negative electrode causes only very slight differences in the local state of charge in the positive electrode. When comparing the magnitude of the effects flattening the negative electrode, we find that the plastic deformation plays a much larger role than either the pressure-modified reaction kinetics or elastic deformation. This is due to the low yield strength of the lithium metal, which limits the stresses such that they have only a small effect on the reaction kinetics. (C) 2014 The Electrochemical Society. All rights reserved.« less

Direct Observation of Active Material Concentration Gradients and Crystallinity Breakdown in LiFePO4 Electrodes During Charge/Discharge Cycling of Lithium Batteries.

PubMed

Roberts, Matthew R; Madsen, Alex; Nicklin, Chris; Rawle, Jonathan; Palmer, Michael G; Owen, John R; Hector, Andrew L

2014-04-03

The phase changes that occur during discharge of an electrode comprised of LiFePO 4 , carbon, and PTFE binder have been studied in lithium half cells by using X-ray diffraction measurements in reflection geometry. Differences in the state of charge between the front and the back of LiFePO 4 electrodes have been visualized. By modifying the X-ray incident angle the depth of penetration of the X-ray beam into the electrode was altered, allowing for the examination of any concentration gradients that were present within the electrode. At high rates of discharge the electrode side facing the current collector underwent limited lithium insertion while the electrode as a whole underwent greater than 50% of discharge. This behavior is consistent with depletion at high rate of the lithium content of the electrolyte contained in the electrode pores. Increases in the diffraction peak widths indicated a breakdown of crystallinity within the active material during cycling even during the relatively short duration of these experiments, which can also be linked to cycling at high rate.

Direct Observation of Active Material Concentration Gradients and Crystallinity Breakdown in LiFePO4 Electrodes During Charge/Discharge Cycling of Lithium Batteries

PubMed Central

2014-01-01

The phase changes that occur during discharge of an electrode comprised of LiFePO4, carbon, and PTFE binder have been studied in lithium half cells by using X-ray diffraction measurements in reflection geometry. Differences in the state of charge between the front and the back of LiFePO4 electrodes have been visualized. By modifying the X-ray incident angle the depth of penetration of the X-ray beam into the electrode was altered, allowing for the examination of any concentration gradients that were present within the electrode. At high rates of discharge the electrode side facing the current collector underwent limited lithium insertion while the electrode as a whole underwent greater than 50% of discharge. This behavior is consistent with depletion at high rate of the lithium content of the electrolyte contained in the electrode pores. Increases in the diffraction peak widths indicated a breakdown of crystallinity within the active material during cycling even during the relatively short duration of these experiments, which can also be linked to cycling at high rate. PMID:24790684

Correlation between thermodynamical stabilities of metal borohydrides and cation electronegativites: First-principles calculations and experiments

NASA Astrophysics Data System (ADS)

Nakamori, Yuko; Miwa, Kazutoshi; Ninomiya, Akihito; Li, Haiwen; Ohba, Nobuko; Towata, Shin-Ichi; Züttel, Andreas; Orimo, Shin-Ichi

2006-07-01

The thermodynamical stabilities for the series of metal borohydrides M(BH4)n ( M=Li , Na, K, Cu, Mg, Zn, Sc, Zr, and Hf; n=1-4 ) have been systematically investigated by first-principles calculations. The results indicated that an ionic bonding between Mn+ cations and [BH4]- anions exists in M(BH4)n , and the charge transfer from Mn+ cations to [BH4]- anions is a key feature for the stability of M(BH4)n . A good correlation between the heat of formation ΔHboro of M(BH4)n and the Pauling electronegativity of the cation χP can be found, which is represented by the linear relation, ΔHboro=248.7χP-390.8 in the unit of kJ/mol BH4 . In order to confirm the predicted correlation experimentally, the hydrogen desorption reactions were studied for M(BH4)n ( M=Li , Na, K, Mg, Zn, Sc, Zr, and Hf), where the samples of the later five borohydrides were mechanochemically synthesized. The thermal desorption analyses indicate that LiBH4 , NaBH4 , and KBH4 desorb hydrogen to hydride phases. Mg(BH4)2 , Sc(BH4)3 , and Zr(BH4)4 show multistep desorption reactions through the intermediate phases of hydrides and/or borides. On the other hand, Zn(BH4)2 desorbs hydrogen and borane to elemental Zn due to instabilities of Zn hydride and boride. A correlation between the desorption temperature Td and the Pauling electronegativity χP is observed experimentally and so χP is an indicator to approximately estimate the stability of M(BH4)n . The enthalpy change for the desorption reaction, ΔHdes , is estimated using the predicted ΔHboro and the reported data for decomposed product, ΔHhyd/boride . The estimated ΔHdes show a good correlation with the observed Td , indicating that the predicted stability of borohydride is experimentally supported. These results are useful for exploring M(BH4)n with appropriate stability as hydrogen storage materials.

Improved Control of Charging Voltage for Li-Ion Battery

NASA Technical Reports Server (NTRS)

Timmerman, Paul; Bugga, Ratnakumar

2006-01-01

The protocol for charging a lithium-ion battery would be modified, according to a proposal, to compensate for the internal voltage drop (charging current internal resistance of the battery). The essence of the modification is to provide for measurement of the internal voltage drop and to increase the terminal-voltage setting by the amount of the internal voltage drop. Ordinarily, a lithium-ion battery is charged at constant current until its terminal voltage attains a set value equal to the nominal full-charge potential. The set value is chosen carefully so as not to exceed the lithium-plating potential, because plated lithium in metallic form constitutes a hazard. When the battery is charged at low temperature, the internal voltage drop is considerable because the electrical conductivity of the battery electrolyte is low at low temperature. Charging the battery at high current at any temperature also gives rise to a high internal voltage drop. In some cases, the internal voltage drop can be as high as 1 volt per cell. Because the voltage available for charging is less than the terminal voltage by the amount of the internal voltage drop, the battery is not fully charged (see figure), even when the terminal voltage reaches the set value. In the modified protocol, the charging current would be periodically interrupted so that the zero-current battery-terminal voltage indicative of the state of charge could be measured. The terminal voltage would also be measured at full charging current. The difference between the full-current and zero-current voltages would equal the internal voltage drop. The set value of terminal voltage would then be increased beyond the nominal full-charge potential by the amount of the internal voltage drop. This adjustment would be performed repeatedly, in real time, so that the voltage setting would track variations in the internal voltage drop to afford full charge without risk of lithium plating. If the charging current and voltage settings were controlled by a computer, then this method of charge control could readily be implemented in software.

Boronic acid recognition of non-interacting carbohydrates for biomedical applications: increasing fluorescence signals of minimally interacting aldoses and sucralose†

PubMed Central

Resendez, Angel; Halim, Md Abdul; Singh, Jasmeet; Webb, Dominic-Luc

2017-01-01

To address carbohydrates that are commonly used in biomedical applications with low binding affinities for boronic acid based detection systems, two chemical modification methods were utilized to increase sensitivity. Modified carbohydrates were analyzed using a two component fluorescent probe based on boronic acid-appended viologen–HPTS (4,4′-o-BBV). Carbohydrates normally giving poor signals (fucose, l-rhamnose, xylose) were subjected to sodium borohydride (NaBH4) reduction in ambient conditions for 1 h yielding the corresponding sugar alcohols from fucose, l-rhamnose and xylose in essentially quantitative yields. Compared to original aldoses, apparent binding affinities were increased 4–25-fold. The chlorinated sweetener and colon permeability marker sucralose (Splenda), otherwise undetectable by boronic acids, was dechlorinated to a detectable derivative by reactive oxygen and hydroxide intermediates by the Fenton reaction or by H2O2 and UV light. This method is specific to sucralose as other common sugars, such as sucrose, do not contain any carbon-chlorine bonds. Significant fluorescence response was obtained for chemically modified sucralose with the 4,4′-o-BBV–HPTS probe system. This proof of principle can be applied to biomedical applications, such as gut permeability, malabsorption, etc. PMID:29130464

Facile synthesis of hydroxy-modified MOF-5 for improving the adsorption capacity of hydrogen by lithium doping.

PubMed

Kubo, Masaru; Hagi, Hayato; Shimojima, Atsushi; Okubo, Tatsuya

2013-11-01

A facile synthesis of partially hydroxy-modified MOF-5 and its improved H2-adsorption capacity by lithium doping are reported. The reaction of Zn(NO3)2·6H2O with a mixture of terephthalic acid (H2BDC) and 2-hydroxyterephthalic acid (H2BDC-OH) in DMF gave hydroxy-modified MOF-5 (MOF-5-OH-x), in which the molar fraction (x) of BDC-OH(2-) was up to 0.54 of the whole ligand. The MOF-5-OH-x frameworks had high BET surface areas (about 3300 m(2) g(-1)), which were comparable to that of MOF-5. We suggest that the MOF-5-OH-x frameworks are formed by the secondary growth of BDC(2-)-rich MOF-5 seed crystals, which are nucleated during the early stage of the reaction. Subsequent Li doping into MOF-5-OH-x results in increased H2 uptake at 77 K and 0.1 MPa from 1.23 to 1.39 wt.% and an increased isosteric heat of H2 adsorption from 5.1-4.2 kJ mol(-1) to 5.5-4.4 kJ mol(-1). Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Microscale Interface Synthesis of Ni-B Amorphous Nanoparticles from NiSO4 by Sodium Borohydride Reduction in Microreactor

NASA Astrophysics Data System (ADS)

Xu, Lei; Peng, Jinhui; Meng, Binfang; Li, Wei; Liu, Bingguo; Luo, Huilong

2016-09-01

Amorphous nanoparticles have attracted a large amount of interest due to their superior catalytic activity and unique selectivity. The Ni-B amorphous nanoparticles were synthesized from aqueous reduction of NiSO4 by sodium borohydride in microscale interface at room temperature. The size, morphology, elemental compositions, and the chemical composition on the surface of Ni-B amorphous nanoparticles were characterized by transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). All the results showed that the synthesized particles are Ni-B amorphous nanoparticles with uniform in size distribution and having good dispersion. The mean particle diameter of Ni-B amorphous nanoparticles was around 9 nm. The present work provides an alternative synthesis route for the Ni-B amorphous nanoparticles.

A direct borohydride fuel cell with a polymer fiber membrane and non-noble metal catalysts.

PubMed

Yang, Xiaodong; Liu, Yongning; Li, Sai; Wei, Xiaozhu; Wang, Li; Chen, Yuanzhen

2012-01-01

Polymer electrolyte membranes (PEM) and Pt-based catalysts are two crucial components which determine the properties and price of fuel cells. Even though, PEM faces problem of fuel crossover in liquid fuel cells such as direct methanol fuel cell (DMFC) and direct borohydride fuel cell (DBFC), which lowers power output greatly. Here, we report a DBFC in which a polymer fiber membrane (PFM) was used, and metal oxides, such as LaNiO₃ and MnO₂, were used as cathode catalysts, meanwhile CoO was used as anode catalyst. Peak power density of 663 mW·cm⁻² has been achieved at 65°C, which increases by a factor of 1.7-3.7 compared with classic DBFCs. This fuel cell structure can also be extended to other liquid fuel cells, such as DMFC.

Optimizing Performance Parameters of Chemically-Derived Graphene/p-Si Heterojunction Solar Cell.

PubMed

Batra, Kamal; Nayak, Sasmita; Behura, Sanjay K; Jani, Omkar

2015-07-01

Chemically-derived graphene have been synthesized by modified Hummers method and reduced using sodium borohydride. To explore the potential for photovoltaic applications, graphene/p-silicon (Si) heterojunction devices were fabricated using a simple and cost effective technique called spin coating. The SEM analysis shows the formation of graphene oxide (GO) flakes which become smooth after reduction. The absence of oxygen containing functional groups, as observed in FT-IR spectra, reveals the reduction of GO, i.e., reduced graphene oxide (rGO). It was further confirmed by Raman analysis, which shows slight reduction in G-band intensity with respect to D-band. Hall effect measurement confirmed n-type nature of rGO. Therefore, an effort has been made to simu- late rGO/p-Si heterojunction device by using the one-dimensional solar cell capacitance software, considering the experimentally derived parameters. The detail analysis of the effects of Si thickness, graphene thickness and temperature on the performance of the device has been presented.

Synthesis of gold nanorods with a longitudinal surface plasmon resonance peak of around 1250 nm

NASA Astrophysics Data System (ADS)

Nguyen, Thi Nhat Hang; Le Trinh Nguyen, Thi; Thanh Tuyen Luong, Thi; Thang Nguyen, Canh Minh; Nguyen, Thi Phuong Phong

2016-03-01

We prepared gold nanorods and joined them to chemicals such as tetrachloauric (III) acid trihydrate, silver nitrate, hydroquinone, hexadecyltrimethylammonium bromide, sodium hydroxide and sodium borohydride using the seed-mediated method. The combination of hydroquinone, with or without salicylic acid, influences the size of the gold nanorods, and this is demonstrated by the results of TEM images, UV-vis spectra and the value of the longitudinal surface plasmon resonance peak with respect to the UV-vis spectra. By changing the Ag+ ion and hydroquinone concentration and the combination of hydroquinone and salicylic acid, the size of the gold nanorods can be controlled and this is manifested by longitudinal surface plasmon resonance peaks forming between 875 and 1278 nm. In particular, sample E2 achieved a longitudinal surface plasmon peak at 1273 nm and an aspect ratio of more than 10 by modifying the hydroquinone to 2.5 mM and salicylic acid to 0.5 mM concentration in the growth solution.

Magneto-plasmonic Au-Coated Co nanoparticles synthesized via hot-injection method

NASA Astrophysics Data System (ADS)

Souza, João B., Jr.; Varanda, Laudemir C.

2018-02-01

A synthetic procedure is described for the obtaining of superparamagnetic Co nanoparticles (NPs) via hot-injection method in the presence of sodium borohydride. The Co NPs obtained have an average diameter of 5.3 nm and saturation magnetization of 115 emu g-1. A modified Langevin equation is fitted to the magnetization curves using a log-normal distribution for the particle diameter and an effective field to account for dipolar interactions. The calculated magnetic diameter of the Co NPs is 0.6 nm smaller than TEM-derived values, implying a magnetic dead layer of 0.3 nm. The magnetic core is coated with Au to prevent oxidation, resulting in water-stable magneto-plasmonic Co/Au core/shell NPs with saturation of 71.6 emu g-1. The coating adds a localized surface plasmon resonance property with absorbance in the so-called ‘therapeutic window’ (690-900 nm), suitable for biomedical applications. It is suggested that these multifunctional NPs are distinguished as a potential platform for applied and fundamental research.

Real single ion solvation free energies with quantum mechanical simulation

DOE PAGES

Duignan, Timothy T.; Baer, Marcel D.; Schenter, Gregory K.; ...

2017-07-04

Single ion solvation free energies are one of the most important properties of electrolyte solutions and yet there is ongoing debate about what these values are. Only the values for neutral ion pairs are known. Here, we use DFT interaction potentials with molecular dynamics simulation (DFT-MD) combined with a modified version of the quasi-chemical theory (QCT) to calculate these energies for the lithium and fluoride ions. A method to correct for the error in the DFT functional is developed and very good agreement with the experimental value for the lithium fluoride pair is obtained. Moreover, this method partitions the energiesmore » into physically intuitive terms such as surface potential, cavity and charging energies which are amenable to descriptions with reduced models. Here, our research suggests that lithium's solvation free energy is dominated by the free energetics of a charged hard sphere, whereas fluoride exhibits significant quantum mechanical behavior that cannot be simply described with a reduced model.« less

Silicon oxycarbide glass-graphene composite paper electrode for long-cycle lithium-ion batteries.

PubMed

David, Lamuel; Bhandavat, Romil; Barrera, Uriel; Singh, Gurpreet

2016-03-30

Silicon and graphene are promising anode materials for lithium-ion batteries because of their high theoretical capacity; however, low volumetric energy density, poor efficiency and instability in high loading electrodes limit their practical application. Here we report a large area (approximately 15 cm × 2.5 cm) self-standing anode material consisting of molecular precursor-derived silicon oxycarbide glass particles embedded in a chemically-modified reduced graphene oxide matrix. The porous reduced graphene oxide matrix serves as an effective electron conductor and current collector with a stable mechanical structure, and the amorphous silicon oxycarbide particles cycle lithium-ions with high Coulombic efficiency. The paper electrode (mass loading of 2 mg cm(-2)) delivers a charge capacity of ∼588 mAh g(-1)electrode (∼393 mAh cm(-3)electrode) at 1,020th cycle and shows no evidence of mechanical failure. Elimination of inactive ingredients such as metal current collector and polymeric binder reduces the total electrode weight and may provide the means to produce efficient lightweight batteries.

Real single ion solvation free energies with quantum mechanical simulation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Duignan, Timothy T.; Baer, Marcel D.; Schenter, Gregory K.

Single ion solvation free energies are one of the most important properties of electrolyte solutions and yet there is ongoing debate about what these values are. Only the values for neutral ion pairs are known. Here, we use DFT interaction potentials with molecular dynamics simulation (DFT-MD) combined with a modified version of the quasi-chemical theory (QCT) to calculate these energies for the lithium and fluoride ions. A method to correct for the error in the DFT functional is developed and very good agreement with the experimental value for the lithium fluoride pair is obtained. Moreover, this method partitions the energiesmore » into physically intuitive terms such as surface potential, cavity and charging energies which are amenable to descriptions with reduced models. Here, our research suggests that lithium's solvation free energy is dominated by the free energetics of a charged hard sphere, whereas fluoride exhibits significant quantum mechanical behavior that cannot be simply described with a reduced model.« less

Porous cellulose diacetate-SiO2 composite coating on polyethylene separator for high-performance lithium-ion battery.

PubMed

Chen, Wenju; Shi, Liyi; Wang, Zhuyi; Zhu, Jiefang; Yang, Haijun; Mao, Xufeng; Chi, Mingming; Sun, Lining; Yuan, Shuai

2016-08-20

The developments of high-performance lithium ion battery are eager to the separators with high ionic conductivity and thermal stability. In this work, a new way to adjust the comprehensive properties of inorganic-organic composite separator was investigated. The cellulose diacetate (CDA)-SiO2 composite coating is beneficial for improving the electrolyte wettability and the thermal stability of separators. Interestingly, the pore structure of composite coating can be regulated by the weight ratio of SiO2 precursor tetraethoxysilane (TEOS) in the coating solution. The electronic performance of lithium ion batteries assembled with modified separators are improved compared with the pristine PE separator. When weight ratio of TEOS in the coating solution was 9.4%, the composite separator shows the best comprehensive performance. Compared with the pristine PE separator, its meltdown temperature and the break-elongation at elevated temperature increased. More importantly, the discharge capacity and the capacity retention improved significantly. Copyright © 2016 Elsevier Ltd. All rights reserved.

Study on novel functional materials carboxymethyl cellulose lithium (CMC-Li) improve high-performance lithium-ion battery.

PubMed

Qiu, Lei; Shao, Ziqiang; Xiang, Pan; Wang, Daxiong; Zhou, Zhenwen; Wang, Feijun; Wang, Wenjun; Wang, Jianquan

2014-09-22

Novel cellulose derivative CMC-Li was synthesized by cotton as raw material. The mechanism of the CMC-Li modified electrode materials by electrospinning was reported. CMC-Li/lithium iron phosphate (LiFePO4, LFP) composite fiber coated with LFP and CMC-Li nanofibers was successfully obtained by electrospinning. Then, CMC-Li/LFP nano-composite fiber was carbonized under nitrogen at a high temperature formed CNF/LFP/Li (CLL) composite nanofibers as cathode material. It can increase the contents of Li+, and improving the diffusion efficiency and specific capacity. The battery with CLL as cathode material retained close to 100% of initial reversible capacity after 200 cycles at 168 mAh g(-1), which was nearly the theoretical specific capacity of LFP. The cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), X-ray diffraction (XRD) and scanning electron microscope (SEM) were characterizing material performance. The batteries have good electrochemical property, outstanding pollution-free, excellent stability. Copyright © 2014 Elsevier Ltd. All rights reserved.

Effects of lithium doping on microstructure, electrical properties, and chemical bonds of sol-gel derived NKN thin films

NASA Astrophysics Data System (ADS)

Lin, Chun-Cheng; Chen, Chan-Ching; Weng, Chung-Ming; Chu, Sheng-Yuan; Hong, Cheng-Shong; Tsai, Cheng-Che

2015-02-01

Highly (100/110) oriented lead-free Lix(Na0.5K0.5)1-xNbO3 (LNKN, x = 0, 0.02, 0.04, and 0.06) thin films are fabricated on Pt/Ti/SiO2/Si substrates via a sol-gel processing method. The lithium (Li) dopants modify the microstructure and chemical bonds of the LNKN films, and therefore improve their electrical properties. The optimal values of the remnant polarization (Pr = 14.3 μC/cm2), piezoelectric coefficient (d33 = 48.1 pm/V), and leakage current (<10-5 A/cm2) are obtained for a lithium addition of x = 0.04 (i.e., 4 at. %). The observation results suggest that the superior electrical properties are the result of an improved crystallization, a larger grain size, and a smoother surface morphology. It is shown that the ion transport mechanism is dominated by an Ohmic behavior under low electric fields and the Poole-Frenkel emission effect under high electric fields.

In-situ grown CNTs modified SiO2/C composites as anode with improved cycling stability and rate capability for lithium storage

NASA Astrophysics Data System (ADS)

Wang, Siqi; Zhao, Naiqin; Shi, Chunsheng; Liu, Enzuo; He, Chunnian; He, Fang; Ma, Liying

2018-03-01

Silica (SiO2) is regarded as one of the most promising anode materials for lithium ion batteries owing to its high theoretical specific capacity, relatively low operation potentials, abundance, environmental benignity and low cost. However, the low intrinsic electrical conductivity and large volume change of SiO2 during the discharge/charge cycles usually results in poor electrochemical performance. In this work, carbon nanotubes (CNTs) modified SiO2/C composites have been fabricated through an in-situ chemical vapor deposition method. The results show that the electrical conductivity of the SiO2/C/CNTs is visibly enhanced through a robust connection between the CNTs and SiO2/C particles. Compared with the pristine SiO2 and SiO2/C composites, the SiO2/C/CNTs composites display a high initial capacity of 1267.2 mA h g-1. Besides, an excellent cycling stability with the capacity of 315.7 mA h g-1 is achieved after 1000th cycles at a rate of 1 A g-1. The significantly improved electrochemical properties of the SiO2/C/CNTs composites are mainly attributed to the formation of three dimensional CNT networks in the SiO2/C substrate, which can not only shorten the Li-ion diffusion path but also relieve the volume change during the lithium-ion insertion/extraction processes.

Precipitation of free fatty acids generated by Malassezia - a possible explanation for the positive effects of lithium succinate in seborrhoeic dermatitis.

PubMed

Mayser, P; Schulz, S

2016-08-01

Lithium succinate and gluconate are effective alternative options licensed for the topical treatment of seborrhoeic dermatitis (SD). Their mode of action is not fully elucidated. Minimal inhibitory concentrations against Malassezia (M.) yeasts, which play an important role in SD, are very high. An assay based on the hydrolysis of ethyl octanoate enables us to test the hydrolytic activity of reference strains of the species M. globosa, M. sympodialis and M. furfur solely without interference by fungal growth as the free octanoic acid generated has antifungal activity. In this assay the presence of alkali salts (lithium, sodium and potassium succinate resp.) in concentrations of 2%, 4% and 8% does not influence hydrolytic activity but the availability of the generated free fatty acid in a dose-dependent manner which was analysed by means of high-performance thin layer chromatography and densitometry. This was best effected with the lithium, followed by the sodium and only to a low degree by the potassium salt. As shown by attenuated total reflection Fourier transform infrared spectroscopy the free fatty acid reacted to the respective alkali soap and precipitate from solution. The alkali soaps could not be utilized by the M. spp. as shown in a modified Tween auxanogram and in lack of fungal growth by ethyl oleate in the presence of 8% lithium succinate. The effect of lithium succinate on growth of M. yeasts and presumably in SD can be explained by a precipitation of free fatty acids as alkali soaps limiting their availability for the growth of these lipid-dependent yeasts. © 2016 European Academy of Dermatology and Venereology.

A systematic review of lumped-parameter equivalent circuit models for real-time estimation of lithium-ion battery states

NASA Astrophysics Data System (ADS)

Nejad, S.; Gladwin, D. T.; Stone, D. A.

2016-06-01

This paper presents a systematic review for the most commonly used lumped-parameter equivalent circuit model structures in lithium-ion battery energy storage applications. These models include the Combined model, Rint model, two hysteresis models, Randles' model, a modified Randles' model and two resistor-capacitor (RC) network models with and without hysteresis included. Two variations of the lithium-ion cell chemistry, namely the lithium-ion iron phosphate (LiFePO4) and lithium nickel-manganese-cobalt oxide (LiNMC) are used for testing purposes. The model parameters and states are recursively estimated using a nonlinear system identification technique based on the dual Extended Kalman Filter (dual-EKF) algorithm. The dynamic performance of the model structures are verified using the results obtained from a self-designed pulsed-current test and an electric vehicle (EV) drive cycle based on the New European Drive Cycle (NEDC) profile over a range of operating temperatures. Analysis on the ten model structures are conducted with respect to state-of-charge (SOC) and state-of-power (SOP) estimation with erroneous initial conditions. Comparatively, both RC model structures provide the best dynamic performance, with an outstanding SOC estimation accuracy. For those cell chemistries with large inherent hysteresis levels (e.g. LiFePO4), the RC model with only one time constant is combined with a dynamic hysteresis model to further enhance the performance of the SOC estimator.

Lithium Sensitivity of Store Operated Ca2+ Entry and Survival of Fibroblasts Isolated from Chorea-Acanthocytosis Patients.

PubMed

Pelzl, Lisann; Elsir, Bhaeldin; Sahu, Itishri; Bissinger, Rosi; Singh, Yogesh; Sukkar, Basma; Honisch, Sabina; Schoels, Ludger; Jemaà, Mohamed; Lang, Elisabeth; Storch, Alexander; Hermann, Andreas; Stournaras, Christos; Lang, Florian

2017-01-01

The widely expressed protein chorein fosters activation of the phosphoinositide 3 kinase (PI3K) pathway thus supporting cell survival. Loss of function mutations of the chorein encoding gene VPS13A (vacuolar protein sorting-associated protein 13A) causes chorea-acanthocytosis (ChAc), a neurodegenerative disorder paralleled by deformations of erythrocytes. In mice, genetic knockout of chorein leads to enhanced neuronal apoptosis. PI3K dependent signalling upregulates Orai1, a pore forming channel protein accomplishing store operated Ca2+ entry (SOCE). Increased Orai1 expression and SOCE have been shown to confer survival of tumor cells. SOCE could be up-regulated by lithium. The present study explored, whether SOCE and/or apoptosis are altered in ChAc fibroblasts and could be modified by lithium treatment. Fibroblasts were isolated from ChAc patients and age-matched healthy volunteers. Cytosolic Ca2+ activity ([Ca2+]i) was estimated from Fura-2-fluorescence, SOCE from increase of [Ca2+]i following Ca2+ re-addition after Ca2+-store depletion with sarcoendoplasmatic Ca2+-ATPase (SERCA) inhibitor thapsigargin (1 µM), and apoptosis from annexin-V/propidium iodide staining quantified in flow cytometry. SOCE was significantly smaller in ChAc fibroblasts than in control fibroblasts. Lithium (2 mM, 24 hours) significantly increased and Orai1 blocker 2-Aminoethoxydiphenyl Borate (2-APB, 50 µM, 24 hours) significantly decreased SOCE. Annexin-V-binding and propidium iodide staining were significantly higher in ChAc fibroblasts than in control fibroblasts. In ChAc fibroblasts annexin-V-binding and propidium iodide staining were significantly decreased by lithium treatment, significantly increased by 2-APB and virtually lithium insensitive in the presence of 2-APB. In ChAc fibroblasts, downregulation of SOCE contributes to enhanced susceptibility to apoptosis. Both, decreased SOCE and enhanced apoptosis of ChAc fibroblasts can be reversed by lithium treatment. © 2017 The Author(s). Published by S. Karger AG, Basel.

Open-label treatment trial of lithium to target the underlying defect in fragile X syndrome.

PubMed

Berry-Kravis, Elizabeth; Sumis, Allison; Hervey, Crystal; Nelson, Michael; Porges, Stephen W; Weng, Ning; Weiler, Ivan Jeanne; Greenough, William T

2008-08-01

In fragile X syndrome (FXS), it is hypothesized that absence of the fragile X mental retardation protein (FMRP) disrupts regulation of group 1 metabotropic glutamate receptor (mGluR and mGluR5)-dependent translation in dendrites. Lithium reduces mGluR-activated translation and reverses phenotypes in the dfxr mutant fly and fmr1 knockout mouse. This pilot add-on trial was conducted to evaluate safety and efficacy of lithium in humans with FXS. Fifteen individuals with FXS, ages 6-23, received lithium titrated to levels of 0.8-1.2 mEq/L. The primary outcome measure, the Aberrant Behavior Checklist --Community Edition (ABC-C) Irritability Subscale, secondary outcome measures (other ABC-C subscales, clinical global improvement scale (CGI), visual analog scale for behavior (VAS), Vineland Adaptive Behavior Scale (VABS)), exploratory cognitive and psychophysiological measures and an extracellular signal-regulated kinase (ERK) activation assay were administered at baseline and 2 months of treatment. Side effects were quantified with a standardized checklist and lithium level, complete blood count (CBC), thyroid stimulating hormone (TSH), and chemistry screen were done at baseline, 2 weeks, 4 weeks and 2 months. The only significant treatment-related side effects were polyuria/polydipsia (n = 7) and elevated TSH (n = 4). Although the ABC-C Irritability Subscale showed only a trend toward improvement, there was significant improvement in the Total ABC-C score (p = 0.005), VAS (p = 0.003), CGI (p = 0.002), VABS Maladaptive Behavior Subscale (p = 0.007), and RBANS List Learning (p = 0.03) and an enhanced ERK activation rate (p = 0.007). Several exploratory tasks proved too difficult for lower-functioning FXS subjects. Results from this study are consistent with results in mouse and fly models of FXS, and suggest that lithium is well-tolerated and provides functional benefits in FXS, possibly by modifying the underlying neural defect. A placebo-controlled trial of lithium in FXS is warranted.

Nitridation-driven conductive Li4Ti5O12 for lithium ion batteries.

PubMed

Park, Kyu-Sung; Benayad, Anass; Kang, Dae-Joon; Doo, Seok-Gwang

2008-11-12

To modify oxide structure and introduce a thin conductive film on Li4Ti5O12, thermal nitridation was adopted for the first time. NH3 decomposes surface Li4Ti5O12 to conductive TiN at high temperature, and surprisingly, it also modifies the surface structure in a way to accommodate the single phase Li insertion and extraction. The electrochemically induced Li4+deltaTi5O12 with a TiN coating layer shows great electrochemical properties at high current densities.

Simplified preparation of coniferyl and sinapyl alcohols.

PubMed

Kim, Hoon; Ralph, John

2005-05-04

Coniferyl and sinapyl alcohols were prepared from commercially available coniferaldehyde and sinapaldehyde using borohydride exchange resin in methanol. This reduction is highly regioselective and exceptionally simple, making these valuable monolignols readily available to researchers lacking synthetic chemistry expertise.

Complex metal borohydrides: multifunctional materials for energy storage and conversion

NASA Astrophysics Data System (ADS)

Mohtadi, Rana; Remhof, Arndt; Jena, Puru

2016-09-01

With the limited supply of fossil fuels and their adverse effect on the climate and the environment, it has become a global priority to seek alternate sources of energy that are clean, abundant, and sustainable. While sources such as solar, wind, and hydrogen can meet the world’s energy demand, considerable challenges remain to find materials that can store and/or convert energy efficiently. This topical review focuses on one such class of materials, namely, multi-functional complex metal borohydrides that not only have the ability to store sufficient amount of hydrogen to meet the needs of the transportation industry, but also can be used for a new generation of metal ion batteries and solar cells. We discuss the material challenges in all these areas and review the progress that has been made to address them, the issues that still need to be resolved and the outlook for the future.

Complex metal borohydrides: multifunctional materials for energy storage and conversion.

PubMed

Mohtadi, Rana; Remhof, Arndt; Jena, Puru

2016-09-07

With the limited supply of fossil fuels and their adverse effect on the climate and the environment, it has become a global priority to seek alternate sources of energy that are clean, abundant, and sustainable. While sources such as solar, wind, and hydrogen can meet the world's energy demand, considerable challenges remain to find materials that can store and/or convert energy efficiently. This topical review focuses on one such class of materials, namely, multi-functional complex metal borohydrides that not only have the ability to store sufficient amount of hydrogen to meet the needs of the transportation industry, but also can be used for a new generation of metal ion batteries and solar cells. We discuss the material challenges in all these areas and review the progress that has been made to address them, the issues that still need to be resolved and the outlook for the future.

A direct borohydride fuel cell with a polymer fiber membrane and non-noble metal catalysts

PubMed Central

Yang, Xiaodong; Liu, Yongning; Li, Sai; Wei, Xiaozhu; Wang, Li; Chen, Yuanzhen

2012-01-01

Polymer electrolyte membranes (PEM) and Pt-based catalysts are two crucial components which determine the properties and price of fuel cells. Even though, PEM faces problem of fuel crossover in liquid fuel cells such as direct methanol fuel cell (DMFC) and direct borohydride fuel cell (DBFC), which lowers power output greatly. Here, we report a DBFC in which a polymer fiber membrane (PFM) was used, and metal oxides, such as LaNiO3 and MnO2, were used as cathode catalysts, meanwhile CoO was used as anode catalyst. Peak power density of 663 mW·cm−2 has been achieved at 65°C, which increases by a factor of 1.7–3.7 compared with classic DBFCs. This fuel cell structure can also be extended to other liquid fuel cells, such as DMFC. PMID:22880160

Development of Hydrogen Storage Tank Systems Based on Complex Metal Hydrides

PubMed Central

Ley, Morten B.; Meggouh, Mariem; Moury, Romain; Peinecke, Kateryna; Felderhoff, Michael

2015-01-01

This review describes recent research in the development of tank systems based on complex metal hydrides for thermolysis and hydrolysis. Commercial applications using complex metal hydrides are limited, especially for thermolysis-based systems where so far only demonstration projects have been performed. Hydrolysis-based systems find their way in space, naval, military and defense applications due to their compatibility with proton exchange membrane (PEM) fuel cells. Tank design, modeling, and development for thermolysis and hydrolysis systems as well as commercial applications of hydrolysis systems are described in more detail in this review. For thermolysis, mostly sodium aluminum hydride containing tanks were developed, and only a few examples with nitrides, ammonia borane and alane. For hydrolysis, sodium borohydride was the preferred material whereas ammonia borane found less popularity. Recycling of the sodium borohydride spent fuel remains an important part for their commercial viability. PMID:28793541

Freeze-Dried Sulfur-Graphene Oxide-Carbon Nanotube Nanocomposite for High Sulfur-Loading Lithium/Sulfur Cells.

PubMed

Hwa, Yoon; Seo, Hyeon Kook; Yuk, Jong-Min; Cairns, Elton J

2017-11-08

The ambient-temperature rechargeable lithium/sulfur (Li/S) cell is a strong candidate for the beyond lithium ion cell since significant progress on developing advanced sulfur electrodes with high sulfur loading has been made. Here we report on a new sulfur electrode active material consisting of a cetyltrimethylammonium bromide-modified sulfur-graphene oxide-carbon nanotube (S-GO-CTA-CNT) nanocomposite prepared by freeze-drying. We show the real-time formation of nanocrystalline lithium sulfide (Li 2 S) at the interface between the S-GO-CTA-CNT nanocomposite and the liquid electrolyte by in situ TEM observation of the reaction. The combination of GO and CNT helps to maintain the structural integrity of the S-GO-CTA-CNT nanocomposite during lithiation/delithiation. A high S loading (11.1 mgS/cm 2 , 75% S) S-GO-CTA-CNT electrode was successfully prepared using a three-dimensional structured Al foam as a substrate and showed good S utilization (1128 mAh/g S corresponding to 12.5 mAh/cm 2 ), even with a very low electrolyte to sulfur weight ratio of 4. Moreover, it was demonstrated that the ionic liquid in the electrolyte improves the Coulombic efficiency and stabilizes the morphology of the Li metal anode.

Ionic Liquid-Enhanced Solid State Electrolyte Interface (SEI) for Lithium Sulfur Batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zheng, Jianming; Gu, Meng; Chen, Honghao

2013-05-16

Li-S battery is a complicated system with many challenges existing before its final market penetration. While most of the reported work for Li-S batteries is focused on the cathode design, we demonstrate in this work that the anode consumption accelerated by corrosive polysulfide solution also critically determines the Li-S cell performance. To validate this hypothesis, ionic liquid (IL) N-methyl-N-butylpyrrolidinium bis(trifluoromethylsulfonyl)imide (Py14TFSI) has been employed to modify the properties of SEI layer formed on Li metal surface in Li-S batteries. It is found that the IL-enhanced passivation film on the lithium anode surface exhibits much different morphology and chemical compositions, effectivelymore » protecting lithium metal from continuous attack by soluble polysulfides. Therefore, both cell impedance and the irreversible consumption of polysulfides on lithium metal are reduced. As a result, the Coulombic efficiency and the cycling stability of Li-S batteries have been greatly improved. After 120 cycles, Li-S battery cycled in the electrolyte containing IL demonstrates a high capacity retention of 94.3% at 0.1 C rate. These results unveil another important failure mechanism for Li-S batteries and shin the light on the new approaches to improve Li-S battery performances.« less

Rational Design of Porous Covalent Triazine-Based Framework Composites as Advanced Organic Lithium-Ion Battery Cathodes.

PubMed

Yuan, Ruoxin; Kang, Wenbin; Zhang, Chuhong

2018-06-02

In an effort to explore the use of organic high-performance lithium ion battery cathodes as an alternative to resolve the current bottleneck hampering the development of their inorganic counterparts, a rational strategy focusing on the optimal composition of covalent triazine-based frameworks (CTFs) with carbon-based materials of varied dimensionalities is delineated. Two-dimensional reduced graphene oxide (rGO) with a compatible structural conformation with the layered CTF is the most suitable scaffold for the tailored mesopores in the polymeric framework, providing outstanding energy storage ability. Through facile ionothermal synthesis and structure engineering, the obtained CTF-rGO composite possesses a high specific surface area of 1357.27 m²/g, and when used as a lithium ion battery cathode it delivers a large capacity of 235 mAh/g in 80 cycles at 0.1 A/g along with a stable capacity of 127 mAh/g over 2500 cycles at 5 A/g. The composite with modified pore structure shows drastically improved performance compared to a pristine CTF, especially at large discharge currents. The CTF-rGO composite with excellent capacity, stability, and rate performance shows great promise as an emerging high-performance cathode that could revolutionize the conventional lithium-ion battery industry.

Application of Lithium Attachment Mass Spectrometry for Knudsen Evaporation and Chemical Ionisation Mass Spectrometry (KEMS, CIMS)

NASA Astrophysics Data System (ADS)

Bannan, T.; Booth, M.; Benyezzar, M.; Bacak, A.; Alfarra, M. R. R.; Topping, D. O.; Percival, C.

2015-12-01

Lithium ion attachment mass spectrometry provides a non-specific, non-fragmenting and sensitive method for detection of volatile species in the gas phase. The design, manufacture, and results from lithium ion attachment ionisation sources for two mass spectrometry systems are presented. Trace gas analysis is investigated using a modified Chemical Ionization Mass Spectrometer (CIMS) and vapour pressure (VP) measurements using a modified Knudsen Effusion Mass Spectrometer (KEMS) are presented. The Li+ modified CIMS provided limits of detection of 4 ppt for acetone, 0.2 ppt for formic acid, 15 ppt for nitric acid and 120 ppt from ammonia. Despite improvements, the problem of burnout remained persistent. The Li+ CIMS would unlikely be suitable for field or aircraft work, but could be appropriate for certain lab applications. The KEMS currently utilizes an electron impact (EI) ionisation source which provides a highly sensitive source, with the drawback of fragmentation of ionized molecules (Booth et al., 2009). Using Li+ KEMS the VP of samples can be measured without fragmentation and can therefore be used to identify VPs of individual components in mixtures. The validity of using Li+ for determining the VP of mixtures was tested by making single component VP measurements, which showed good agreement with EI measurements of Poly ethylene glycol (PEG) 3 and PEG 4, both when individually measured and when mixed. The Li+ KEMS was then used to investigate a system of atmospheric relevance, α-pinene secondary organic aerosol, generated in a reaction chamber (Alfarra et al., 2012). The VPs of the individual components from this generated sample are within the range we expect for compounds capable of partitioning between the particle and gas phase of an aerosol (0.1-10-5 Pa). Li+ source has a calculated sensitivity approximately 75 times less than that of EI, but the lack of fragmentation using the Li+ source is a significant advantage.

Application of Lithium Attachment Mass Spectrometry for Knudsen Evaporation and Chemical Ionisation Mass Spectrometry (KEMS, CIMS)

NASA Astrophysics Data System (ADS)

Bannan, Thomas; Booth, A. Murray; Alfarra, Rami; Bacak, Asan; Pericval, Carl

2016-04-01

Lithium ion attachment mass spectrometry provides a non-specific, non-fragmenting and sensitive method for detection of volatile species in the gas phase. The design, manufacture, and results from lithium ion attachment ionisation sources for two mass spectrometry systems are presented. Trace gas analysis is investigated using a modified Chemical Ionization Mass Spectrometer (CIMS) and vapour pressure (VP) measurements using a modified Knudsen Effusion Mass Spectrometer (KEMS) are presented. The Li+ modified CIMS provided limits of detection of 4 ppt for acetone, 0.2 ppt for formic acid, 15 ppt for nitric acid and 120 ppt from ammonia. Despite improvements, the problem of burnout remained persistent. The Li+ CIMS would unlikely be suitable for field or aircraft work, but could be appropriate for certain lab applications. The KEMS currently utilizes an electron impact (EI) ionisation source which provides a highly sensitive source, with the drawback of fragmentation of ionized molecules (Booth et al., 2009). Using Li+ KEMS the VP of samples can be measured without fragmentation and can therefore be used to identify VPs of individual components in mixtures. The validity of using Li+ for determining the VP of mixtures was tested by making single component VP measurements, which showed good agreement with EI measurements of Poly ethylene glycol (PEG) 3 and PEG 4, both when individually measured and when mixed. The Li+ KEMS was then used to investigate a system of atmospheric relevance, α-pinene secondary organic aerosol, generated in a reaction chamber (Alfarra et al., 2012). The VPs of the individual components from this generated sample are within the range we expect for compounds capable of partitioning between the particle and gas phase of an aerosol (0.1-10-5 Pa). Li+ source has a calculated sensitivity approximately 75 times less than that of EI, but the lack of fragmentation using the Li+ source is a significant advantage.

Core--strategy leading to high reversible hydrogen storage capacity for NaBH4.

PubMed

Christian, Meganne L; Aguey-Zinsou, Kondo-François

2012-09-25

Owing to its high storage capacity (10.8 mass %), sodium borohydride (NaBH(4)) is a promising hydrogen storage material. However, the temperature for hydrogen release is high (>500 °C), and reversibility of the release is unachievable under reasonable conditions. Herein, we demonstrate the potential of a novel strategy leading to high and stable hydrogen absorption/desorption cycling for NaBH(4) under mild pressure conditions (4 MPa). By an antisolvent precipitation method, the size of NaBH(4) particles was restricted to a few nanometers (<30 nm), resulting in a decrease of the melting point and an initial release of hydrogen at 400 °C. Further encapsulation of these nanoparticles upon reaction of nickel chloride at their surface allowed the synthesis of a core--shell nanostructure, NaBH(4)@Ni, and this provided a route for (a) the effective nanoconfinement of the melted NaBH(4) core and its dehydrogenation products, and (b) reversibility and fast kinetics owing to short diffusion lengths, the unstable nature of nickel borohydride, and possible modification of reaction paths. Hence at 350 °C, a reversible and steady hydrogen capacity of 5 mass % was achieved for NaBH(4)@Ni; 80% of the hydrogen could be desorbed or absorbed in less than 60 min, and full capacity was reached within 5 h. To the best of our knowledge, this is the first time that such performances have been achieved with NaBH(4). This demonstrates the potential of the strategy in leading to major advancements in the design of effective hydrogen storage materials from pristine borohydrides.

Synthesis and Characterization of Methylammonium Borohydride

DOE Office of Scientific and Technical Information (OSTI.GOV)

Graham, Kathryn R.; Bowden, Mark E.; Kemmitt, Tim

2011-01-06

A new borohydride, [CH3NH3]+[BH4]-, has been synthesised by the metathesis of CH3NH3X and MBH4 in methylamine in order to determine its behaviour in comparison to ammonium borohydride [NH4]+[BH4]-. The introduction of methyl groups is expected to disrupt the hydrogen bonding network of [NH4]+[BH4]- and in turn alter the hydrogen release properties. Room temperature X-ray diffraction studies have shown that [CH3NH3]+[BH4]- adopts a tetragonal unit cell with lattice parameters of a = 4.9486 Å and b = 8.9083 Å. The room temperature structure shows considerable hydrogen mobility similar to that observed in NH3BH3. The kinetics and thermodynamics of these reactions havemore » been investigated and show hydrogen release follows a similar pathway to that of [NH4]+[BH4]-. Both compounds decompose slowly at room temperature and rapidly at ca. 40 °C to form the diammoniate of diborane or the methylated analogue [BH2(CH3NH2)2]+BH4-. The first stage of decomposition has been further investigated by means on in-situ X-ray diffraction and solid state 11B NMR spectroscopy, and appears to occur in the absence of any detectable intermediates to form crystalline [BH2(CH3NH2)2]+BH4-. [(CH3)2NH2]+[BH4]- and [BH2{(CH3)2NH}2]+BH4- have also been synthesised by analogous routes, indicating a more general applicability of the synthetic method.« less

An all-solid-state lithium/polyaniline rechargeable cell

NASA Astrophysics Data System (ADS)

Changzhi, Li; Xinsheng, Peng; Borong, Zhang; Baochen, Wang

The performance of an all-solid-state cell having a lithium negative electrode, a modified polyethylene oxide (PEO)—epoxy resin (ER) electrolyte, and a polyaniline (PAn) positive electrode has been studied using cyclic voltammetry, charge/discharge cycling, and polarization curves at various temperatures. The redox reaction of the PAn electrode at the PAn/modifed PEOER interface exhibits good reversibility. At 50-80 °C, the Li/PEOERLiClO 4/PAn cell shows more than 40 charge/discharge cycles, 90% charge/discharge efficiency, and 54 W h kg -1 discharge energy density (on PAn weight basis) at 50 μA between 2 and 4 V. The polarization performance of the battery improves steadily with increase in temperature.

A preliminary study on the short-term efficacy of chairside computer-aided design/computer-assisted manufacturing- generated posterior lithium disilicate crowns.

PubMed

Reich, Sven; Fischer, Sören; Sobotta, Bernhard; Klapper, Horst-Uwe; Gozdowski, Stephan

2010-01-01

The purpose of this preliminary study was to evaluate the clinical performance of chairside-generated crowns over a preliminary time period of 24 months. Forty-one posterior crowns made of a machinable lithium disilicate ceramic for full-contour crowns were inserted in 34 patients using a chairside computer-aided design/computer-assisted manufacturing technique. The crowns were evaluated at baseline and after 6, 12, and 24 months according to modified United States Public Health Service criteria. After 2 years, all reexamined crowns (n = 39) were in situ; one abutment exhibited secondary caries and two abutments received root canal treatment. Within the limited observation period, the crowns revealed clinically satisfying results.

Targeted partial surface modification with nano-SiO2@Li2CoPO4F as high-voltage cathode material for LIBs

NASA Astrophysics Data System (ADS)

Chang, Caiyun; Huang, Zhipeng; Tian, Runsai; Jiang, Xinyu; Li, Chunsheng; Feng, Jijun

2017-10-01

Tuning whole/partial surface modification on cathode material with oxide material is a sought-after method to enhance the electrochemical performance in power storage field. Herein, nano-SiO2 targeted partial surface modified high voltage cathode material Li2CoPO4F has been successfully fabricated via a facile self-assembly process in silica dispersion at ambient temperature. With the aid of polar -OH groups attracted on the surface of SiO2 micelles, the nano-SiO2 preferentially nestle up along the borders and boundaries of Li2CoPO4F particles, where protection should be deployed with emphasis against the undesirable interactions between materials and electrolytes. Compared with pristine Li2CoPO4F, the SiO2 selectively modified Li2CoPO4F cathode materials, especially LCPF-3S, exhibit desirable electrochemical performances with higher discharge capacity, more outstanding cycle stability and favorable rate capability without any additional carbon involved. The greatly enhanced electrochemical properties can be attributed to the improved lithium-ion diffusion kinetics and structure tolerance during repeated lithiation/delithiation process. Such findings reveal a great potential of nano-SiO2 modified Li2CoPO4F as high energy cathode material for lithium ion batteries.

Solid-state sodium cells - An alternative to lithium cells?

NASA Astrophysics Data System (ADS)

West, K.; Zachau-Christiansen, B.; Jacobsen, T.; Skaarup, S.

1989-05-01

The cycling properties of laboratory cells based on the insertion of sodium into vanadium oxides using polymer electrolyte at 80 C are reported. In the best system: Na/PEO, NaClO4/V2O5 (modified), C, high reversibility, and an energy density comparable with the Li/TiS2 system have been obtained.

Variation of photoluminescence features in Pr{sup 3+} doped lithium-fluoro-borate glass by changing different modifier oxides (MgO, CaO, CdO and PbO)-Judd-Ofelt theory application

DOE Office of Scientific and Technical Information (OSTI.GOV)

Balakrishna, A.; Rajesh, D.; Babu, S.

2015-06-24

Pr{sup 3+} (1.0 mol%) doped different modifier oxide based six lithium-fluoro-borate glasses with chemical composition of 49Li{sub 2}B{sub 4}O{sub 7}-20BaF{sub 2}-10NaF-20MO (where M= Mg, Ca, Cd and Pb), 49Li{sub 2}B{sub 4}O{sub 7}-20BaF{sub 2}-10NaF-10MgO-10CaO and 49Li{sub 2}B{sub 4}O{sub 7}-20BaF{sub 2}-10NaF-10CdO-10PbO were prepared by conventional melt quenching technique. Judd-Ofelt theory has been applied for evaluating the Judd-Ofelt intensity parameters for Pr{sup 3+} ion in these glass compositions and are in turn to used to predict radiative properties such as radiative transition probabilities (A{sub T}), branching ratios (β) and stimulated emission cross-section (σ{sub P}). Stimulated emission cross-section (σ{sub p}) of prominent emission transitions,more » {sup 3}P{sub 0}→{sup 3}H{sub 4} and {sup 1}D{sub 2}→{sup 3}H{sub 4} of Pr{sup 3+} ion in all lithium-fluoro-borate glasses were calculated. Among all the emission transitions, {sup 3}P{sub 0}→{sup 3}H{sub 4} posseses higher branching ratio and stimulated emission cross-section in Mg-Ca glass, which leads to the best laser excitation at 487 nm wavelength.« less

Present understanding of the stability of Li-stuffed garnets with moisture, carbon dioxide, and metallic lithium

NASA Astrophysics Data System (ADS)

Hofstetter, Kyle; Samson, Alfred Junio; Narayanan, Sumaletha; Thangadurai, Venkataraman

2018-06-01

Fast lithium-ion conducting garnet-type metal oxides are promising membranes for next-generation all-solid-state Li batteries and beyond Li-ion batteries, including Li-air and Li-S batteries, due to their high total Li-ion conductivity and excellent chemical stability against reaction with elemental Li. Several studies have been reported on structure-chemical composition-ionic conductivity property in Li-stuffed garnet-type metal oxides. Here, an overview of the chemical and electrochemical stability of lithium-based garnets against moisture/humidity, aqueous solutions, carbon dioxide, sulfur, and metallic lithium are analyzed. Moisture and aqueous stability studies focus on understanding the crystal structure stability, the proton exchange capacity as a function of Li content in Li-stuffed garnets, and how the protonated species affect the crystal structure and mass transport properties. H+/Li+ exchange was found to be in the range of 2-100%. Stability concerning Li-ion conductivity and morphology under carbon dioxide are discussed. Interfacial chemical stability with lithium metal characterized by electrochemical stability window, Li dendrite formation and area specific resistance (ASR) for the reaction Li ⇌ Li+ +e- are presented. Recent attempts to suppress dendrite formation and to reduce ASR via surface modification are also highlighted. Li and Li-stuffed garnet interface ASR values are shown to be as high as >2000 Ω cm2 and as low as 1 Ω cm2 at room temperature for surface modified Li-stuffed samples. Furthermore, recent studies on Li-S battery utilizing chemically stable Li - garnet electrolyte are also discussed.

Soft tissue adhesion of polished versus glazed lithium disilicate ceramic for dental applications.

PubMed

Brunot-Gohin, C; Duval, J-L; Azogui, E-E; Jannetta, R; Pezron, I; Laurent-Maquin, D; Gangloff, S C; Egles, C

2013-09-01

Ceramics are widely used materials for prosthesis, especially in dental fields. Despite multiple biomedical applications, little is known about ceramic surface modifications and the resulting cell behavior at its contact. The aim of this study is to evaluate the biological response of polished versus glazed surface treatments on lithium disilicate dental ceramic. We studied a lithium disilicate ceramic (IPS e.max(®) Press, Ivoclar Vivadent) with 3 different surface treatments: raw surface treatment, hand polished surface treatment, and glazed surface treatment (control samples are Thermanox(®), Nunc). In order to evaluate the possible modulation of cell response at the surface of ceramic, we compared polished versus glazed ceramics using an organotypic culture model of chicken epithelium. Our results show that the surface roughness is not modified as demonstrated by equivalent Ra measurements. On the contrary, the contact angle θ in water is very different between polished (84°) and glazed (33°) samples. The culture of epithelial tissues allowed a very precise assessment of histocompatibility of these interfaces and showed that polished samples increased cell adhesion and proliferation as compared to glazed samples. Lithium disilicate polished ceramic provided better adhesion and proliferation than lithium disilicate glazed ceramic. Taken together, our results demonstrate for the first time, how it is possible to use simple surface modifications to finely modulate the adhesion of tissues. Our results will help dental surgeons to choose the most appropriate surface treatment for a specific clinical application, in particular for the ceramic implant collar. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Acetaldehyde-induced structural and conformational alterations in human immunoglobulin G: A physicochemical and multi-spectroscopic study.

PubMed

Waris, Sana; Habib, Safia; Tantry, Irfan Qadir; Khan, Rizwan Hasan; Mahmood, Riaz; Ali, Asif

2018-07-01

Acetaldehyde is a reactive aldehyde produced as an intermediate of alcohol metabolism and tobacco pyrolysis. It has the potential to interact with different biomolecules in various tissues which results in the formation of stable, unstable and covalent adducts. This causes structural and functional modifications that may lead to severe complications such as cancer. This study has probed the structural modifications in human immunoglobulin G (IgG) as a function of different concentrations of acetaldehyde in the presence of reducing agent, sodium borohydride. Acetaldehyde mediated modifications in IgG have been characterised by various physicochemical techniques. UV-spectrophotometry showed that acetaldehyde modified IgG exhibited marked increase in hyperchromicity. Fluorescence studies revealed a significant quenching of tryptophan fluorescence which resulted in loss of β-sheet secondary structure that was confirmed by circular dichroic analysis. Gross structural changes in the morphology of IgG were confirmed by increase in mass and hydrodynamic radius of this glycoprotein along with the appearance of fibrillar structures in modified IgG, when compared to the granular structure of the native form of IgG observed by scanning electron microscope. The results indicate that acetaldehyde causes alterations in the secondary and tertiary structure of the protein leading to diminution of normal function of IgG molecule. Copyright © 2018 Elsevier B.V. All rights reserved.

Stereoselective reduction of the bioactive 19-nor-clerodane trans-dehydrocrotonin by using sodium borohydride and cerium (III) chloride as a catalyst

NASA Astrophysics Data System (ADS)

Soares, Breno Almeida; Firme, Caio Lima; Castro, Rosane Nora; Bortoluzzi, Adailton João; Maciel, Maria Aparecida Medeiros

2018-02-01

The bioactive 19-nor-clerodane trans-dehydrocrotonin (t-DCTN) is herein used as starting material to afford an epimeric derivative mixture so called t-DCTN-α and β-OL, which is a diastereoisomeric pair. The stereoselective reduction of t-DCTN was performed in methanol medium by using NaBH4 and CeCl3·7H2O which react reducing the C2 carbonyl group on the t-DCTN decalin ring moiety. The t-DCTN-diastereoisomeric compounds were characterized by chromatographic HPLC analyses and by NMR data. The crystal structure of t-DCTN-α-OL was confirmed employing X-ray diffraction. Additionally, an experimental and theoretical NMR chemical shifts study applied to the t-DCTN diastereoisomeric derivatives lead favorable coefficients of correlation (R > 0.98) by using B3LYP combined with 6-311++G(d,p) basis set. Furthermore, a modified Gemal and Luche's mechanism in stepwise fashion is proposed. Agreement between theoretical and experimental higher reactivity of NaBH4/Ce3+ towards NaBH4 was found and the theoretical results explicit the participation of the reaction solvent (methanol) on transition state by using NaBH4 unlike that involving NaBH4/Ce3+. It was found that the proposed modified mechanism only occurs in 0.8 eq. of Ce3+ salt.

Response of mouse epidermal cells to single doses of heavy-particles

NASA Technical Reports Server (NTRS)

Leith, J. T.; Schilling, W. A.; Welch, G. P.

1972-01-01

The survival of mouse epidermal cells to heavy-particles has been studied In Vivo by the Withers clone technique. Experiments with accelerated helium, lithium and carbon ions were performed. The survival curve for the helium ion irradiations used a modified Bragg curve method with a maximum tissue penetration of 465 microns, and indicated that the dose needed to reduce the original cell number to 1 surviving cell/square centimeters was 1525 rads with a D sub o of 95 rads. The LET at the basal cell layer was 28.6 keV per micron. Preliminary experiments with lithium and carbon used treatment doses of 1250 rads with LET's at the surface of the skin of 56 and 193 keV per micron respectively. Penetration depths in skin were 350 and 530 microns for the carbon and lithium ions whose Bragg curves were unmodified. Results indicate a maximum RBE for skin of about 2 using the skin cloning technique. An attempt has been made to relate the epidermal cell survival curve to mortality of the whole animal for helium ions.

Silicon oxycarbide glass-graphene composite paper electrode for long-cycle lithium-ion batteries

PubMed Central

David, Lamuel; Bhandavat, Romil; Barrera, Uriel; Singh, Gurpreet

2016-01-01

Silicon and graphene are promising anode materials for lithium-ion batteries because of their high theoretical capacity; however, low volumetric energy density, poor efficiency and instability in high loading electrodes limit their practical application. Here we report a large area (approximately 15 cm × 2.5 cm) self-standing anode material consisting of molecular precursor-derived silicon oxycarbide glass particles embedded in a chemically-modified reduced graphene oxide matrix. The porous reduced graphene oxide matrix serves as an effective electron conductor and current collector with a stable mechanical structure, and the amorphous silicon oxycarbide particles cycle lithium-ions with high Coulombic efficiency. The paper electrode (mass loading of 2 mg cm−2) delivers a charge capacity of ∼588 mAh g−1electrode (∼393 mAh cm−3electrode) at 1,020th cycle and shows no evidence of mechanical failure. Elimination of inactive ingredients such as metal current collector and polymeric binder reduces the total electrode weight and may provide the means to produce efficient lightweight batteries. PMID:27025781

Porous PVDF/PANI ion-exchange membrane (IEM) modified by polyvinylpyrrolidone (PVP) and lithium chloride in the application of membrane capacitive deionisation (MCDI).

PubMed

Zhang, Yiming; Zhang, Wei; Cházaro-Ruiz, Luis F

2018-05-01

In this work, polyvinylidene fluoride (PVDF)/polyaniline (PANI) heterogeneous anion-exchange membranes filled with pore-forming agents polyvinylpyrrolidone (PVP) and lithium chloride were prepared by the solution-casting technique using the solvent 1-methyl-2-pyrrolidone (NMP) and a two-step phase inversion procedure. Key properties of the as-prepared membranes, such as hydrophilicity, water content, ion exchange capacity, fixed ion concentration, conductivity and transport number were examined and compared between membranes in different conditions. The pore-forming hydrophilic additives PVP and lithium chloride to the casting solution appeared to improve the ion-exchange membranes (IEMs) by increasing the conductivity, transport number and hydrophilicity. The effects of increasing membrane drying time on the porosity of the as-prepared membranes were found to lower membrane porosity by reducing membrane water content. However, pore-forming agents were found to be able to stabilise membrane transport number with different drying times. As-prepared PVDF/PANI anion-exchange membrane with pore-forming agent is demonstrated to be a more efficient candidate for water purification (e.g. desalination) and other industrial applications.

A Comparison of the Predictive Capabilities of the Embedded-Atom Method and Modified Embedded-Atom Method Potentials for Lithium

DOE PAGES

Vella, Joseph R.; Stillinger, Frank H.; Panagiotopoulos, Athanassios Z.; ...

2015-07-23

Here, we compare six lithium potentials by examining their ability to predict coexistence properties and liquid structure using molecular dynamics. All potentials are of the embedded-atom-method (EAM) type. The coexistence properties we focus on are the melting curve, vapor pressure, saturated liquid density, and vapor-liquid surface tension. For each property studied, the simulation results are compared to available experimental data in order to properly assess the accuracy of each potential. We find that the Cui 2NN MEAM is the most robust potential, giving adequate agreement with most of the properties examined. For example, the zero-pressure melting point of this potentialmore » is shown to be around 443 K, while experimentally is it about 454 K. This potential also gives excellent agreement with saturated liquid densities, even though no liquid properties were used in the fitting procedure. Our study allows us to conclude that the Cui 2NN MEAM should be used for further simulations of lithiums.« less

Soluble Graphene Nanosheets from Recycled Graphite of Spent Lithium Ion Batteries

NASA Astrophysics Data System (ADS)

Zhao, Liangliang; Liu, Xiya; Wan, Chuanyun; Ye, Xiangrong; Wu, Fanhong

2018-02-01

Soluble graphene nanosheets are fabricated from recycled graphite of spent lithium ion batteries through a modified Hammers process followed by deoxygenation with NaOH-KOH eutectic. Ultrasonic exfoliation in N-methyl-pyrrolidone indicates the loosened graphene layers in recycled graphite are prone to exfoliation. Reduction of the exfoliated graphene oxide sheets was conducted in molten NaOH-KOH eutectic at different temperatures. The results show that molten NaOH-KOH effectively eliminates the unsaturated oxygen-containing moieties from the exfoliated graphene oxide sheets while creating more hydroxyl functional groups. Higher temperature treatment is more prone to remove hydroxyls while producing the shrinkage on the surface of graphene sheets. Graphene sheet with a good solubility is produced when the graphene oxide is heat-treated at 220 °C for 10 h. After reduction, the graphene oxide sheets exhibit excellent dispersibility or solubility in water, ethanol and other polar solvents, therefore being highly desirable for solution processing of graphene materials. Such study not only identifies a high-quality stockpile to prepare soluble graphene but also paves a feasible alternative of graphite recycling from spent lithium batteries.

Performance Enhancement of a Sulfur/Carbon Cathode by Polydopamine as an Efficient Shell for High-Performance Lithium-Sulfur Batteries.

PubMed

Zhang, Xuqing; Xie, Dong; Zhong, Yu; Wang, Donghuang; Wu, Jianbo; Wang, Xiuli; Xia, Xinhui; Gu, Changdong; Tu, Jiangping

2017-08-04

Lithium-sulfur batteries (LSBs) are considered to be among the most promising next-generation high-energy batteries. It is a consensus that improving the conductivity of sulfur cathodes and impeding the dissolution of lithium polysulfides are two key accesses to high-performance LSBs. Herein we report a sulfur/carbon black (S/C) cathode modified by self-polymerized polydopamine (pDA) with the assistance of polymerization treatment. The pDA acts as a novel and effective shell on the S/C cathode to stop the shuttle effect of polysulfides. By the synergistic effect of enhanced conductivity and multiple blocking effect for polysulfides, the S/C@pDA electrode exhibits improved electrochemical performances including large specific capacity (1135 mAh g -1 at 0.2 C), high rate capability (533 mAh g -1 at 5 C) and long cyclic life (965 mAh g -1 after 200 cycles). Our smart design strategy may promote the development of high-performance LSBs. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Bayesian modelling of the emission spectrum of the Joint European Torus Lithium Beam Emission Spectroscopy system.

PubMed

Kwak, Sehyun; Svensson, J; Brix, M; Ghim, Y-C

2016-02-01

A Bayesian model of the emission spectrum of the JET lithium beam has been developed to infer the intensity of the Li I (2p-2s) line radiation and associated uncertainties. The detected spectrum for each channel of the lithium beam emission spectroscopy system is here modelled by a single Li line modified by an instrumental function, Bremsstrahlung background, instrumental offset, and interference filter curve. Both the instrumental function and the interference filter curve are modelled with non-parametric Gaussian processes. All free parameters of the model, the intensities of the Li line, Bremsstrahlung background, and instrumental offset, are inferred using Bayesian probability theory with a Gaussian likelihood for photon statistics and electronic background noise. The prior distributions of the free parameters are chosen as Gaussians. Given these assumptions, the intensity of the Li line and corresponding uncertainties are analytically available using a Bayesian linear inversion technique. The proposed approach makes it possible to extract the intensity of Li line without doing a separate background subtraction through modulation of the Li beam.

Quantitative bioluminescent detection of bacteria

NASA Technical Reports Server (NTRS)

Chappelle, E. W.; Picciolo, G. L.

1976-01-01

Phosphoflavins in sample are measured using photobacterial luciferase assay technique for flavin mononucleotide (FMN). Boiling perchloric acid is used to rupture cells to free bound flavin and to hydrolyze flavin adenine dinucleotide to FMN. Base-stabilized water solution of sodium borohydride is used as reactant.

Electrospun-sodiumtetrafluoroborate-polyethylene oxide membranes for solvent-free sodium ion transport in solid state sodium ion batteries

NASA Astrophysics Data System (ADS)

Freitag, K. M.; Walke, P.; Nilges, T.; Kirchhain, H.; Spranger, R. J.; van Wüllen, L.

2018-02-01

Electrospinning is used to fabricate sodium ion conducting fiber membranes composed of polyethylene oxide (PEO), sodium tetrafluoroborate (NaBF4), and succinonitrile (SN) as plasticizer. As compared to conventionally prepared lithium electrolyte membranes with identical composition (PEO:SN:LiBF4), those membranes exhibit conductivities up to 10-4 S cm-1 at 328 K (activation energy ∼36 kJ mol-1, 36:8:1 membrane), which favors such systems as a solid-state electrolyte alternative for batteries. The conduction mechanism is evaluated and the ion mobility are examined. We identified the segment mobility of the polyethylene oxide as the main driving force for the enhanced ion mobility in the membranes. The introduction of SN has only a minor influence on the conductivity and segment mobility at room temperature, but extents the anion and cation mobility to temperatures below ambient. For the 36:8:1 (PEO:SN:NaBF4) membrane we found the highest ion mobility of all membranes under investigation. A comparison of the present sodium membranes with lithium systems of the same composition shows that the overall performance of the sodium systems is comparable. Taking plasticizer-free sodium membranes into account they perform even better than the lithium containing counterparts, and plasticizer-modified membranes show only half an order of magnitude lower conductivities than comparable lithium ones.

Desired crystal oriented LiFePO4 nanoplatelets in situ anchored on a graphene cross-linked conductive network for fast lithium storage.

PubMed

Wang, Bo; Liu, Anmin; Abdulla, Wael Al; Wang, Dianlong; Zhao, X S

2015-05-21

Electron transfer and lithium ion diffusion rates are the key factors limiting the lithium ion storage in anisotropic LiFePO4 electrodes. In this work, we employed a facile solvothermal method to synthesize a "platelet-on-sheet" LiFePO4/graphene composite (LFP@GNs), which is LiFePO4 nanoplatelets in situ grown on graphene sheets with highly oriented (010) facets of LiFePO4 crystals. Such a two-phase contact mode with graphene sheets cross-linked to form a three-dimensional porous network is favourable for both fast lithium ion and electron transports. As a result, the designed LFP@GNs displayed a high rate capability (∼56 mA h g(-1) at 60 C) and long life cycling stability (∼87% capacity retention over 1000 cycles at 10 C). For comparison purposes, samples ex situ modified with graphene (LFP/GNs) as well as pure LiFePO4 platelets (LFP) were also prepared and investigated. More importantly, the obtained LFP@GNs can be used as a basic unit for constructing more complex structures to further improve electrochemical performance, such as coating the exposed LFP surface with a thin layer of carbon to build a C@LFP@GN composite to further enhance its cycling stability (∼98% capacity retention over 1000 cycles at 10 C).

Lithium-ion battery cell-level control using constrained model predictive control and equivalent circuit models

NASA Astrophysics Data System (ADS)

Xavier, Marcelo A.; Trimboli, M. Scott

2015-07-01

This paper introduces a novel application of model predictive control (MPC) to cell-level charging of a lithium-ion battery utilizing an equivalent circuit model of battery dynamics. The approach employs a modified form of the MPC algorithm that caters for direct feed-though signals in order to model near-instantaneous battery ohmic resistance. The implementation utilizes a 2nd-order equivalent circuit discrete-time state-space model based on actual cell parameters; the control methodology is used to compute a fast charging profile that respects input, output, and state constraints. Results show that MPC is well-suited to the dynamics of the battery control problem and further suggest significant performance improvements might be achieved by extending the result to electrochemical models.

In situ engineering of the electrode-electrolyte interface for stabilized overlithiated cathodes

DOE PAGES

Evans, Tyler; Piper, Daniela Molina; Sun, Huaxing; ...

2017-01-05

Here, the first-ever demonstration of stabilized Si/lithium-manganese-rich full cells, capable of retaining >90% energy over early cycling and >90% capacity over more than 750 cycles at the 1C rate (100% depth-of-discharge), is made through the utilization of a modified ionic liquid electrolyte capable of forming a favorable cathode-electrolyte interface.

A comparison of sodium borohydride as a fuel for proton exchange membrane fuel cells and for direct borohydride fuel cells

NASA Astrophysics Data System (ADS)

Wee, Jung-Ho

Two types of fuel cell systems using NaBH 4 aqueous solution as a fuel are possible: the hydrogen/air proton exchange membrane fuel cell (PEMFC) which uses onsite H 2 generated via the NaBH 4 hydrolysis reaction (B-PEMFC) at the anode and the direct borohydride fuel cell (DBFC) system which directly uses NaBH 4 aqueous solution at the anode and air at the cathode. Recently, research on these two types of fuel cells has begun to attract interest due to the various benefits of this liquid fuel for fuel cell systems for portable applications. It might therefore be relevant at this stage to evaluate the relative competitiveness of the two fuel cells. Considering their current technologies and the high price of NaBH 4, this paper evaluated and analyzed the factors influencing the relative favorability of each type of fuel cell. Their relative competitiveness was strongly dependent on the extent of the NaBH 4 crossover. When considering the crossover in DBFC systems, the total costs of the B-PEMFC system were the most competitive among the fuel cell systems. On the other hand, if the crossover problem were to be completely overcome, the total cost of the DBFC system generating six electrons (6e-DBFC) would be very similar to that of the B-PEMFC system. The DBFC system generating eight electrons (8e-DBFC) became even more competitive if the problem of crossover can be overcome. However, in this case, the volume of NaBH 4 aqueous solution consumed by the DBFC was larger than that consumed by the B-PEMFC.

Fracture load of ceramic restorations after fatigue loading.

PubMed

Baladhandayutham, Balasudha; Lawson, Nathaniel C; Burgess, John O

2015-08-01

A clinician must decide what ceramic coping and veneer material to prescribe based on the amount of tooth reduction possible and the desired esthetic outcome of the restoration. The purpose of this in vitro study was to compare the fracture strength of monolithic and bilayered lithium disilicate (IPS e.max) and zirconia (LAVA) crowns at clinically relevant thicknesses after load cycling. Crowns (n=8) were fabricated from 6 groups: 1.2-mm monolithic lithium disilicate, 1.5-mm monolithic lithium disilicate, 1.5-mm bilayered lithium disilicate with hand-layered veneer, 0.6 mm monolithic zirconia, 1.2-mm bilayered zirconia with hand-layered veneer, and 1.2-mm bilayered zirconia with milled veneer (dimension represents thickness at the occlusal pit). Crowns were cemented to identical milled resin dies with resin-modified glass ionomer cement. Cemented crowns were stored at 37°C for 24 hours and load cycled for 200,000 cycles at 25 N at a rate of 40 cycles/minute. The ultimate fracture load for each specimen was measured in a universal testing machine. Data were analyzed with a 1-way ANOVA and Tukey honest significant difference post hoc analysis (α=.05). Mean ±SD fracture load values were 1465 ±330 N for monolithic lithium disilicate (1.2-mm thickness) and 2027 ±365 N (1.5-mm thickness) and 1732 ±315 N for bilayered hand-veneered lithium disilicate (1.5-mm thickness). Fracture loads were 1669 ±311 N for monolithic zirconia crowns (0.6mm thickness), 2625 ±300 N for zirconia milled-veneered (1.2-mm thickness), and 2655 ±590N for zirconia hand-veneered crowns (1.2mm thickness). One-way ANOVA showed a statistically significant difference among the groups (P<.01). Veneered zirconia crowns showed the highest fracture strength, 1.2-mm hand veneered zirconia was similar to that of 1.5-mm monolithic zirconia, and all other groups were not statistically different. Crowns of 1.2-mm bilayered zirconia had higher fracture loads than 0.6-mm zirconia or 1.2-mm lithium disilicate monolithic crowns. Copyright © 2015 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Oral choline decreases brain purine levels in lithium-treated subjects with rapid-cycling bipolar disorder: a double-blind trial using proton and lithium magnetic resonance spectroscopy.

PubMed

Lyoo, In Kyoon; Demopulos, Christina M; Hirashima, Fuyuki; Ahn, Kyung Heup; Renshaw, Perry F

2003-08-01

Oral choline administration has been reported to increase brain phosphatidylcholine levels. As phospholipid synthesis for maintaining membrane integrity in mammalian brain cells consumes approximately 10-15% of the total adenosine triphosphate (ATP) pool, an increased availability of brain choline may lead to an increase in ATP consumption. Given reports of genetic studies, which suggest mitochondrial dysfunction, and phosphorus (31P) magnetic resonance spectroscopy (MRS) studies, which report dysfunction in high-energy phosphate metabolism in patients with bipolar disorder, the current study is designed to evaluate the role of oral choline supplementation in modifying high-energy phosphate metabolism in subjects with bipolar disorder. Eight lithium-treated patients with DSM-IV bipolar disorder, rapid cycling type were randomly assigned to 50 mg/kg/day of choline bitartrate or placebo for 12 weeks. Brain purine, choline and lithium levels were assessed using 1H- and 7Li-MRS. Patients received four to six MRS scans, at baseline and weeks 2, 3, 5, 8, 10 and 12 of treatment (n = 40 scans). Patients were assessed using the Clinical Global Impression Scale (CGIS), the Young Mania Rating Scale (YRMS) and the Hamilton Depression Rating Scale (HDRS) at each MRS scan. There were no significant differences in change-from-baseline measures of CGIS, YMRS, and HDRS, brain choline/creatine ratios, and brain lithium levels over a 12-week assessment period between the choline and placebo groups or within each group. However, the choline treatment group showed a significant decrease in purine metabolite ratios from baseline (purine/n-acetyl aspartate: coef = -0.08, z = -2.17, df = 22, p = 0.030; purine/choline: coef = -0.12, z = -1.97, df = 22, p = 0.049) compared to the placebo group, controlling for brain lithium level changes. Brain lithium level change was not a significant predictor of purine ratios. The current study reports that oral choline supplementation resulted in a significant decrease in brain purine levels over a 12-week treatment period in lithium-treated patients with DSM-IV bipolar disorder, rapid-cycling type, which may be related to the anti-manic effects of adjuvant choline. This result is consistent with mitochondrial dysfunction in bipolar disorder inadequately meeting the demand for increased ATP production as exogenous oral choline administration increases membrane phospholipid synthesis.

Immobilization of Candida antarctica lipase B by covalent attachment to green coconut fiber.

PubMed

Brígida, Ana I S; Pinheiro, Alvaro D T; Ferreira, Andrea L O; Pinto, Gustavo A S; Gonçalves, Luciana R B

2007-04-01

The objective of this study was to covalently immobilize Candida antarctica type B lipase (CALB) onto silanized green coconut fibers. Variables known to control the number of bonds between enzyme and support were evaluated including contact time, pH, and final reduction with sodium borohydride. Optimal conditions for lipase immobilization were found to be 2 h incubation at both pH 7.0 and 10.0. Thermal stability studies at 60 degrees C showed that the immobilized lipase prepared at pH 10.0 (CALB-10) was 363-fold more stable than the soluble enzyme and 5.4-fold more stable than the biocatalyst prepared at pH 7.0 (CALB-7). CALB-7 was found to have higher specific activity and better stability when stored at 5 degrees C. When sodium borohydride was used as reducing agent on CALB-10 there were no improvement in storage stability and at 60 degrees C stability was reduced for both CALB-7 and CALB-10.

Immobilization of Candida antarctica Lipase B by Covalent Attachment to Green Coconut Fiber

NASA Astrophysics Data System (ADS)

Brígida, Ana I. S.; Pinheiro, Álvaro D. T.; Ferreira, Andrea L. O.; Pinto, Gustavo A. S.; Gonçalves, Luciana R. B.

The objective of this study was to covalently immobilize Candida antarctica type B lipase (CALB) onto silanized green coconut fibers. Variables known to control the number of bonds between enzyme and support were evaluated including contact time, pH, and final reduction with sodium borohydride. Optimal conditions for lipase immobilization were found to be 2h incubation at both pH 7.0 and 10.0. Thermal stability studies at 60°C showed that the immobilized lipase prepared at pH 10.0 (CALB-10) was 363-fold more stable than the soluble enzyme and 5.4-fold more stable than the biocatalyst prepared at pH 7.0 (CALB-7). CALB-7 was found to have higher specific activity and better stability when stored at 5°C. When sodium borohydride was used as reducing agent on CALB-10 there were no improvement in storage stability and at 60°C stability was reduced for both CALB-7 and CALB-10.

Effects of the surface modification of silver nanoparticles on the surface-enhanced Raman spectroscopy of methylene blue for borohydride-reduced silver colloid

NASA Astrophysics Data System (ADS)

Dong, Xiao; Gu, Huaimin; Kang, Jian; Yuan, Xiaojuan; Wu, Jiwei

2010-12-01

The paper further investigated the relationship between the modification of the surface chemistry and the enhancement mechanisms of borohydride-reduced silver particles (BRSC). The bands of residual ions die down while the anomalous bands increase gradually with the increasing of the concentration of Cl - and Br -. It means the residual ions are displaced gradually by the added Cl - or Br - and the two halides can lead to the aggregation of the BRSC to a certain extent. However, the most strongly binding anions - I -, cannot cause any aggregation of silver particles. From the detection of methylene blue (MB), the relationship between the modification of silver surface chemistry and the enhancement mechanisms was discussed. Chloride gives the greatest enhancement while the iodide gives the lowest enhancement among the different kinds of anions. There are also some anomalous bands in the SERS spectra of MB, and these anomalous bands were given rational explanation in this paper.

Ultrahigh figure-of-merit for hydrogen generation from sodium borohydride using ternary metal catalysts

NASA Astrophysics Data System (ADS)

Hu, Lunghao; Ceccato, R.; Raj, R.

We report further increase in the figure-of-merit (FOM) for hydrogen generation from NaBH 4 than reported in an earlier paper [1], where a sub-nanometer layer of metal catalysts are deposited on carbon nanotube paper (CNT paper) that has been functionalized with polymer-derived silicon carbonitride (SiCN) ceramic film. Ternary, Ru-Pd-Pt, instead of the binary Pd-Pt catalyst used earlier, together with a thinner CNT paper is shown to increase the figure-of-merit by up to a factor of six, putting is above any other known catalyst for hydrogen generation from NaBH 4. The catalysts are prepared by first impregnating the functionalized CNT-paper with solutions of the metal salts, followed by reduction in a sodium borohydride solution. The reaction mechanism and the catalyst efficiency are described in terms of an electric charge transfer, whereby the negative charge on the BH 4 - ion is exchanged with hydrogen via the electronically conducting SiCN/CNT substrate [1].

Hydrolysis and regeneration of sodium borohydride (NaBH4) - A combination of hydrogen production and storage

NASA Astrophysics Data System (ADS)

Chen, W.; Ouyang, L. Z.; Liu, J. W.; Yao, X. D.; Wang, H.; Liu, Z. W.; Zhu, M.

2017-08-01

Sodium borohydride (NaBH4) hydrolysis is a promising approach for hydrogen generation, but it is limited by high costs, low efficiency of recycling the by-product, and a lack of effective gravimetric storage methods. Here we demonstrate the regeneration of NaBH4 by ball milling the by-product, NaBO2·2H2O or NaBO2·4H2O, with MgH2 at room temperature and atmospheric pressure without any further post-treatment. Record yields of NaBH4 at 90.0% for NaBO2·2H2O and 88.3% for NaBO2·4H2O are achieved. This process also produces hydrogen from the splitting of coordinate water in hydrated sodium metaborate. This compensates the need for extra hydrogen for generating MgH2. Accordingly, we conclude that our unique approach realizes an efficient and cost-effective closed loop system for hydrogen production and storage.

Colloidal Au and Au-alloy catalysts for direct borohydride fuel cells: Electrocatalysis and fuel cell performance

NASA Astrophysics Data System (ADS)

Atwan, Mohammed H.; Macdonald, Charles L. B.; Northwood, Derek O.; Gyenge, Elod L.

Supported colloidal Au and Au-alloys (Au-Pt and Au-Pd, 1:1 atomic ratio) on Vulcan XC-72 (with 20 wt% metal load) were prepared by the Bönneman method. The electrocatalytic activity of the colloidal metals with respect to borohydride electro-oxidation for fuel cell applications was investigated by voltammetry on static and rotating electrodes, chronoamperometry, chronopotentiometry and fuel cell experiments. The fundamental electrochemical techniques showed that alloying Au, a metal that leads to the maximum eight-electron oxidation of BH 4 -, with Pd or Pt, well-known catalysts of dehydrogenation reactions, improved the electrode kinetics of BH 4 - oxidation. Fuel cell experiments corroborated the kinetic studies. Using 5 mg cm -2 colloidal metal load on the anode, it was found that Au-Pt was the most active catalyst giving a cell voltage of 0.47 V at 100 mA cm -2 and 333 K, while under identical conditions the cell voltage using colloidal Au was 0.17 V.

A novel magnetic Fe@Au core-shell nanoparticles anchored graphene oxide recyclable nanocatalyst for the reduction of nitrophenol compounds.

PubMed

Gupta, Vinod Kumar; Atar, Necip; Yola, Mehmet Lütfi; Üstündağ, Zafer; Uzun, Lokman

2014-01-01

In this study, a novel catalyst based on Fe@Au bimetallic nanoparticles involved graphene oxide was prepared and characterized by transmission electron microscope (TEM), and x-ray photoelectron spectroscopy (XPS). The nanomaterial was used in catalytic reductions of 4-nitrophenol and 2-nitrophenol in the presence of sodium borohydride. The experimental parameters such as temperature, the dosage of catalyst and the concentration of sodium borohydride were studied. The rates of catalytic reduction of the nitrophenol compounds have been found as the sequence: 4-nitrophenol>2-nitrophenol. The kinetic and thermodynamic parameters of nitrophenol compounds were determined. Activation energies were found as 2.33 kcal mol(-1) and 3.16 kcal mol(-1) for 4-nitrophenol and 2-nitrophenol, respectively. The nanomaterial was separated from the product by using a magnet and recycled after the reduction of nitrophenol compounds. The recyclable of the nanocatalyst is economically significant in industry. Copyright © 2013 Elsevier Ltd. All rights reserved.

Tailoring Thermodynamics and Kinetics for Hydrogen Storage in Complex Hydrides towards Applications.

PubMed

Liu, Yongfeng; Yang, Yaxiong; Gao, Mingxia; Pan, Hongge

2016-02-01

Solid-state hydrogen storage using various materials is expected to provide the ultimate solution for safe and efficient on-board storage. Complex hydrides have attracted increasing attention over the past two decades due to their high gravimetric and volumetric hydrogen densities. In this account, we review studies from our lab on tailoring the thermodynamics and kinetics for hydrogen storage in complex hydrides, including metal alanates, borohydrides and amides. By changing the material composition and structure, developing feasible preparation methods, doping high-performance catalysts, optimizing multifunctional additives, creating nanostructures and understanding the interaction mechanisms with hydrogen, the operating temperatures for hydrogen storage in metal amides, alanates and borohydrides are remarkably reduced. This temperature reduction is associated with enhanced reaction kinetics and improved reversibility. The examples discussed in this review are expected to provide new inspiration for the development of complex hydrides with high hydrogen capacity and appropriate thermodynamics and kinetics for hydrogen storage. © 2015 The Chemical Society of Japan & Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Color reduction of sulfonated eucalyptus kraft lignin.

PubMed

Zhang, Hui; Bai, Youcan; Zhou, Wanpeng; Chen, Fangeng

2017-04-01

Several eucalyptus lignins named as HSL, SML and BSL were prepared by high temperature sulfonation, sulfomethylation, butane sultone sulfonation respectively. The color properties of samples were investigated. Under optimized conditions the sulfonic group (SO 3 H) content of HSL, SML and BSL reached 1.52, 1.60 and 1.58mmol/g, respectively. Samples were characterized by UV-vis spectroscopy, FTIR spectroscopy, 1 H NMR spectroscopy, GPC and brightness test, respectively. The results revealed that BSL performed a higher molecular weight and lighter color due to the phenolic hydroxyl blocking by 1,4-butane sultone (1,4-BS). The color reduction of sodium borohydride treated BSL (labeled as SBSL) was further enhanced and the brightness value was improved by 76.1% compared with the darkest HSL. SBSL process was much better than HSL and SML process. Hydroxyl blocking effect of 1,4-BS and reducibility of sodium borohydride played important roles in the color reduction of sulfonated eucalyptus kraft lignin. Copyright © 2017 Elsevier B.V. All rights reserved.

Further evidence for a potassium-like action of lithium ions on sodium efflux in frog skeletal muscle

PubMed Central

Beaugé, L. A.; Ortiz, Olga

1972-01-01

1. The efflux of labelled sodium as well as net sodium and lithium changes were studied in aged high sodium sartorius muscles of the South American frog Leptodactilus ocelatus. 2. In the presence of 2·5 mM potassium in the media, the replacement of external sodium with lithium or magnesium resulted in an increase in sodium efflux. The magnitude of such increase was always larger in lithium. 3. With the absence of potassium in the media, the response of sodium efflux to replacement of external sodium varied with the cation used as a substitute. In lithium Ringer there was always a noticeable increase, whereas in magnesium there was always a marked reduction. The same results were observed when calcium was substituted for magnesium. 4. The replacement of 60 mM external sodium with sucrose did not prevent the stimulating effect of 5 mM potassium on sodium efflux, nor the inhibitory action of 10-4 M ouabain. This indicates that neither sucrose by itself, nor the lowering of the ionic strength, modified to an appreciable extent the function of the sodium pump. 5. Net sodium extrusion took place against an electrochemical gradient in potassium-free — 50 mM sodium — mM lithium Ringer. About 75% of this efflux was ouabain sensitive. 6. Muscles made both sodium and lithium rich and incubated in potassium-free — 60 mM sodium — 50 mM lithium Ringer also showed net sodium extrusion against an electrochemical gradient, which was 85% ouabain sensitive. This extrusion took place even under conditions where the changes in free energy favouring lithium entry were always lower than the changes in free energy opposing sodium going out. This indicates that a sodium-lithium exchange by a counter-transport process is unlikely. 7. External potassium reduced the ouabain sensitive lithium influx in muscles incubated in lithium Ringer. The values found were 5·90 ± 0·39 μ-mole/g.hr and 2·66 ± 0·43 μmole/g.hr in potassium-free and 15 mM potassium respectively. At the same time potassium had no effect on the ouabain-insensitive lithium uptake. 8. Muscles incubated in potassium-free-magnesium Ringer had a residual sodium efflux which could not be accounted for by passive movement. About 40% of it was abolished by 10-4 M ouabain. This ouabain-sensitive part could be a consequence of some stimulation of the sodium pump by potassium leaking out of the cells. If this is correct it should be inhibited by external sodium and should not contribute to the total sodium efflux in potassium-free sodium media. 9. Magnesium was used as the reference cation to study the sodium-stimulated sodium efflux under potassium-free conditions. The total sodium efflux amounted to 0·668 hr-1 (rate constant) and was 71% ouabain sensitive. 10. The present experiments demonstrated that lithium ions have a direct stimulating effect on sodium efflux in high sodium skeletal muscle, and strongly support the notion that this effect is produced by an activation of the sodium pump through a potassium-like action. PMID:4637626

Formation of Nanosized Defective Lithium Peroxides through Si-Coated Carbon Nanotube Cathodes for High Energy Efficiency Li-O2 Batteries.

PubMed

Lin, Qi; Cui, Zhonghui; Sun, Jiyang; Huo, Hanyu; Chen, Cheng; Guo, Xiangxin

2018-06-06

The formation and decomposition of lithium peroxides (Li 2 O 2 ) during cycling is the key process for the reversible operation of lithium-oxygen batteries. The manipulation of such products from the large toroidal particles about hundreds of nanometers to the ones in the scale of tens of nanometers can improve the energy efficiency and the cycle life of the batteries. In this work, we carry out an in situ morphology tuning of Li 2 O 2 by virtue of the surface properties of the n-type Si-modified aligned carbon nanotube (CNT) cathodes. With the introduction of an n-type Si coating layer on the CNT surface, the morphology of Li 2 O 2 formed by discharge changes from large toroidal particles (∼300 nm) deposited on the pristine CNT cathodes to nanoparticles (10-20 nm) with poor crystallinity and plenty of lithium vacancies. Beneficial from such changes, the charge overpotential dramatically decreases to 0.55 V, with the charge plateau lying at 3.5 V even in the case of a high discharge capacity (3450 mA h g -1 ) being delivered, resulting in the high electrical energy efficiency approaching 80%. Such an improvement is attributed to the fact that the introduction of the n-type Si coating layer changes the surface properties of CNTs and guides the formation of nanosized amorphous-like lithium peroxides with plenty of defects. These results demonstrate that the cathode surface properties play an important role in the formation of products formed during the cycle, providing inspiration to design superior cathodes for the Li-O 2 cells.

The Pulsed Fission-Fusion (PUFF) Concept for Deep Space Exploration and Terrestrial Power Generation

NASA Technical Reports Server (NTRS)

Adams, Robert; Cassibry, Jason; Schillo, Kevin

2017-01-01

This team is exploring a modified Z-pinch geometry as a propulsion system, imploding a liner of liquid lithium onto a pellet containing both fission and fusion fuel. The plasma resulting from the fission and fusion burn expands against a magnetic nozzle, for propulsion, or a magnetic confinement system, for terrestrial power generation. There is considerable synergy in the concept; the lithium acts as a temporary virtual cathode, and adds reaction mass for propulsion. Further, the lithium acts as a radiation shield against generated neutrons and gamma rays. Finally, the density profile of the column can be tailored using the lithium sheath. Recent theoretical and experimental developments (e.g. tailored density profile in the fuel injection, shear stabilization, and magnetic shear stabilization) have had great success in mitigating instabilities that have plagued previous fusion efforts. This paper will review the work in evaluating the pellet sizes and z-pinch conditions for optimal PuFF propulsion. Trades of pellet size and composition with z-pinch power levels and conditions for the tamper and lithium implosion are evaluated. Current models, both theoretical and computational, show that a z-pinch can ignite a small (1 cm radius) fission-fusion target with significant yield. Comparison is made between pure fission and boosted fission targets. Performance is shown for crewed spacecraft for high speed Mars round trip missions and near interstellar robotic missions. The PuFF concept also offers a solution for terrestrial power production. PuFF can, with recycling of the effluent, achieve near 100% burnup of fission fuel, providing a very attractive power source with minimal waste. The small size of PuFF relative to today's plants enables a more distributed power network and less exposure to natural or man-made disruptions.

Studies on Ionic Conductivity and Electrochemical Stability of Plasticized Photopolymerized Polymer Electrolyte Membranes for Solid State Lithium Ion Batteries

NASA Astrophysics Data System (ADS)

He, Ruixuan

In pursuit of safer and more flexible solid-state lithium ion batteries, solid polymer electrolytes have emerged as a promising candidate. The present dissertation entails exploration of solid plasticized, photopolymerized (i.e. ultraviolent-cured) polymer electrolyte membranes (PEM) for fulfilling the critical requirements of electrolytes, such as high ionic conductivity and good thermal and electrochemical stability, among others. Electrochemical performance of PEMs containing lithium ion half-cells was also investigated at different two temperatures. Phase diagram approach was adopted to guide the fabrication of two types of plasticized PEMs. Prepolymer poly (ethylene glycol) diacrylate (PEGDA) was used as a matrix for building an ionic conductive and mechanically sturdy network. Lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) was incorporated as a source of lithium ions, while a solid plasticizer succinonitrile (SCN) and a liquid plasticizer tetraethylene glycol dimethyl ether (TEGDME) were incorporated in the respective systems. The important role of plasticizer on the enhancement of ionic conductivity (sigma) to the superionic conductive level (10-3 S/cm) was revealed in both systems. It is worth noting that photopolymerization induced crystallization (PIC) occurred during UV-curing in the SCN-rich region of the ternary PEGDA/LiTFSI/SCN ternary mixtures. The PEM thus formed contained a plastic crystal phase, which showed lower σ relative to their amorphous PEGDA/LiTFSI/TEGDME counterpart. Comparisons on other thermal and electrochemical properties of the two types of PEMs are presented in Chapter IV. For the PEGDA/LiTFSI/SCN PEMs, fundamental study was carried out to clarify the relationship between σ and glass transition temperature (T g). In lithium salt/polymer binary PEMs, increase in Tg and reduction in σ were observed; these may be attributed to ion-dipole complexation between dissociated lithium cations and ether oxygen upon salt addition. Notably, above the threshold salt concentration of 7 mol %, dual loss tangent peaks were observed in dynamic mechanical studies. These might be ascribed to segmental relaxations of ion-dipole complexed networks and that of polymer chains surrounding the undissociated lithium salt acting like "fillers". Upon SCN incorporation, these two peaks merged into one that was further suppressed below the Tg of the pure network, whereas σ improved to the superionic conductor level. The role of SCN on the σ enhancement as both plasticizer for the polymer network and ionizer for the salt is discussed in Chapter V. In order to improve the mechanical toughness of the highly conductive PEGDA/LiTFSI/SCN PEM, effects of prepolymer molecular weight on mechanical and electrochemical properties of PEMs were further investigated. By increasing molecular weight of PEGDA from 700 to 6000 g/mol, toughness and elongation at break were enhanced as expected. Interestingly, improved ionic conductivity was achieved simultaneously. The dual improvement may be attributed to the less chemical crosslinked points and the more flexible chain motion in the looser network of PEGDA6000-PEM relative to its PEGDA700 counterpart. Subsequently, high thermal stability and electrochemical stability of both types of PEMs, as well as the satisfactory room temperature charge/discharge cycling performance of PEM containing lithium ion half-cells were observed. The pertinent information is documented in Chapter VI. Finally, the investigation of the charge/discharge cycling performance of solid-state LiFePO4 half-cells at an elevated temperature of 60°C is discussed in Chapter VII. In the half-cells, particularly, SCN plasticized PEMs with and without electrolyte modifier lithium bis(oxalato)borate (LiBOB) were respectively employed. Rapid decline of capacity and increase of cell resistance were found in the unmodified PEM containing cell; however, these deteriorations were greatly suppressed upon LiBOB modification. Electrochemical and thermal compatibility of PEMs towards different electrodes were examined in several symmetric cells and half-cells. Detailed characterization on LiFePO 4 electrodes and PEMs retrieved from these cells implied that the observed battery failure might be triggered by an amide-forming side reaction that took place at the interface of a SCN plasticized PEM and a lithium electrode at high temperature. Of particular importance is the fact that this detrimental side reaction was effectively suppressed upon LiBOB electrolyte modifier addition. Plausible mechanisms are discussed.

2'-O-methyl-5-formylcytidine (f5Cm), a new modified nucleotide at the 'wobble' of two cytoplasmic tRNAs Leu (NAA) from bovine liver.

PubMed Central

Païs de Barros, J P; Keith, G; El Adlouni, C; Glasser, A L; Mack, G; Dirheimer, G; Desgrès, J

1996-01-01

The nucleotide analysis of a cytoplasmic tRNA(Leu) isolated from bovine liver revealed the presence of an unknown modified nucleotide N. The corresponding N nucleoside was isolated by different enzymatic and chromatographic protocols from a partially purified preparation of this tRNA(Leu). Its chemical characterization was determined from its chromatographic properties, UV-absorption spectroscopy and mass spectrometric measurements, as well as from those of the borohydride reduced N nucleoside and its etheno-trimethylsilyl derivative. The structure of N was established as 2'-O-methyl-5-formylcytidine (f5CM), and its reduced derivative as 2'-O-methyl-5-hydroxy-methylcytidine (om5Cm). By sequencing the bovine liver tRNA(Leu), the structure of the anticodon was determined as f5CmAA. In addition, the nucleotide sequence showed two primary structures differing only by the nucleotide 47c which is either uridine or adenosine. The two slightly differing bovine liver tRNAs-Leu(f5CmAA) are the only tRNAs so far sequenced which contain f5Cm. The role of such a modified cytidine at the first position of the anticodon is discussed in terms of decoding properties for the UUG and UUA leucine codons. Recently, precise evidence was obtained for the presence of f5Cm at the same position in tRNAs(Leu)(NAA) isolated from rabbit and lamb liver. Therefore, the 2'-O-methyl-5-formyl modification of cytidine at position 34 could be a general feature of cytoplasmic tRNAs(Leu)(NAA) in mammals. PMID:8628682

Improved Butanol-Methanol (BUME) Method by Replacing Acetic Acid for Lipid Extraction of Biological Samples.

PubMed

Cruz, Mutya; Wang, Miao; Frisch-Daiello, Jessica; Han, Xianlin

2016-07-01

Extraction of lipids from biological samples is a critical step in lipidomics, especially for shotgun lipidomics where lipid extracts are directly infused into a mass spectrometer. The butanol-methanol (BUME) extraction method was originally developed to extract lipids from plasma samples with 1 % acetic acid. Considering some lipids are sensitive to acidic environments, we modified this protocol by replacing acetic acid with lithium chloride solution and extended the modified extraction to tissue samples. Although no significant reduction of plasmalogen levels in the acidic BUME extracts of rat heart samples was found, the modified method was established to extract various tissue samples, including rat liver, heart, and plasma. Essentially identical profiles of the majority of lipid classes were obtained from the extracts of the modified BUME and traditional Bligh-Dyer methods. However, it was found that neither the original, nor the modified BUME method was suitable for 4-hydroxyalkenal species measurement in biological samples.

Improved Butanol-Methanol (BUME) Method by Replacing Acetic Acid for Lipid Extraction of Biological Samples

PubMed Central

Cruz, Mutya; Wang, Miao; Frisch-Daiello, Jessica; Han, Xianlin

2016-01-01

Extraction of lipids from biological samples is a critical step in lipidomics, especially for shotgun lipidomics where lipid extracts are directly infused into a mass spectrometer. The butanol-methanol (BUME) extraction method was originally developed to extract lipids from plasma samples with 1% acetic acid. Considering some lipids are sensitive to acidic environments, we modified this protocol by replacing acetic acid with lithium chloride solution and extended the modified extraction to tissue samples. Although no significant reduction of plasmalogen levels in the acidic BUME extracts of rat heart samples was found, the modified method was established to extract various tissue samples, including rat liver, heart, and plasma. Essentially identical profiles of the majority of lipid classes were obtained from the extracts of the modified BUME and traditional Bligh-Dyer methods. However, it was found that neither the original, nor the modified BUME method was suitable for 4-hydroxyalkenal species measurement in biological samples. PMID:27245345

Radiation grafting of methyl methacrylate onto polyethylene separators for lithium secondary batteries

NASA Astrophysics Data System (ADS)

Gwon, Sung-Jin; Choi, Jae-Hak; Sohn, Joon-Yong; An, Sung-Jun; Ihm, Young-Eon; Nho, Young-Chang

2008-08-01

Micro-porous polyethylene separator was modified by radiation grafting of methyl methacrylate in order to improve its affinity with a liquid electrolyte. The degree of grafting (DOG) increased with the monomer concentration and grafting time. The morphological change of the modified separator was investigated by scanning electron microscopy. The degree of crystallinity upon grafting was reduced due to the formation of an amorphous PMMA layer. The electrolyte uptake and the ionic conductivity of the separator increased with an increase in the DOG. The ionic conductivity reached 2.0 mS/cm for the grafted polyethylene separator with 127 wt% DOG.

Synthesis and Electrochemical Property of LiMn2O4 Porous Hollow Nanofiber as Cathode for Lithium-Ion Batteries.

PubMed

Duan, Lianfeng; Zhang, Xueyu; Yue, Kaiqiang; Wu, Yue; Zhuang, Jian; Lü, Wei

2017-12-01

The LiMn 2 O 4 hollow nanofibers with a porous structure have been synthesized by modified electrospinning techniques and subsequent thermal treatment. The precursors were electrospun directly onto the fluorine-doped tin oxide (FTO) glass. The heating rate and FTO as substrate play key roles on preparing porous hollow nanofiber. As cathode materials for lithium-ion batteries (LIBs), LiMn 2 O 4 hollow nanofibers showed the high specific capacity of 125.9 mAh/g at 0.1 C and a stable cycling performance, 105.2 mAh/g after 400 cycles. This unique structure could relieve the structure expansion effectively and provide more reaction sites as well as shorten the diffusion path for Li + for improving electrochemical performance for LIBs.

Lithium-ion battery cell-level control using constrained model predictive control and equivalent circuit models

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xavier, MA; Trimboli, MS

This paper introduces a novel application of model predictive control (MPC) to cell-level charging of a lithium-ion battery utilizing an equivalent circuit model of battery dynamics. The approach employs a modified form of the MPC algorithm that caters for direct feed-though signals in order to model near-instantaneous battery ohmic resistance. The implementation utilizes a 2nd-order equivalent circuit discrete-time state-space model based on actual cell parameters; the control methodology is used to compute a fast charging profile that respects input, output, and state constraints. Results show that MPC is well-suited to the dynamics of the battery control problem and further suggestmore » significant performance improvements might be achieved by extending the result to electrochemical models. (C) 2015 Elsevier B.V. All rights reserved.« less

Molecular structure of the lithium enolate of acetaldehyde

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lynch, T.J.; Newcomb, M.; Bergbreiter, D.E.

1980-11-21

Calculations of the structures of isomers of the lithium enolate of acetaldehyde done at the restricted Hartree-Fock level with the HONDO program on the CDC 7600 are reported. Using the standard 4-31 G basis set, these calculations produce excessively large bond angles, and this favors the most open of the three isomeric structures. Including the polarization functions on the carbons and oxygen and using the recent Dunning and Hayes (3s2p/2s) contraction indicates that the chirol enolates are the lowest energy structure. However, the differences of the various enolate structures are small and could be modified by solvent effects. These resultsmore » are proported to suggest that the enolates containing internal ligands may be prepared such that a new chirol center would exist by virtue of the counterion position. (BLM)« less

Effects of Electrospun Carbon Nanofibers’ Interlayers on High-Performance Lithium–Sulfur Batteries

PubMed Central

Gao, Tianji; Le, TrungHieu; Yang, Ying; Yu, Zhihao; Huang, Zhenghong; Kang, Feiyu

2017-01-01

Two different interlayers were introduced in lithium–sulfur batteries to improve the cycling stability with sulfur loading as high as 80% of total mass of cathode. Melamine was recommended as a nitrogen-rich (N-rich) amine component to synthesize a modified polyacrylic acid (MPAA). The electrospun MPAA was carbonized into N-rich carbon nanofibers, which were used as cathode interlayers, while carbon nanofibers from PAA without melamine was used as an anode interlayer. At the rate of 0.1 C, the initial discharge capacity with two interlayers was 983 mAh g−1, and faded down to 651 mAh g−1 after 100 cycles with the coulombic efficiency of 95.4%. At the rate of 1 C, the discharge capacity was kept to 380 mAh g−1 after 600 cycles with a coulombic efficiency of 98.8%. It apparently demonstrated that the cathode interlayer is extremely effective at shutting down the migration of polysulfide ions. The anode interlayer induced the lithium ions to form uniform lithium metal deposits confined on the fiber surface and in the bulk to strengthen the cycling stability of the lithium metal anode. PMID:28772731

Modified High-Nickel Cathodes with Stable Surface Chemistry Against Ambient Air for Lithium-Ion Batteries.

PubMed

You, Ya; Celio, Hugo; Li, Jianyu; Dolocan, Andrei; Manthiram, Arumugam

2018-03-30

High-Ni layered oxides are promising next-generation cathodes for lithium-ion batteries owing to their high capacity and lower cost. However, as the Ni content increases over 70 %, they have a high dynamic affinity towards moisture and CO 2 in ambient air, primarily reacting to form LiOH, Li 2 CO 3 , and LiHCO 3 on the surface, which is commonly termed "residual lithium". Air exposure occurs after synthesis as it is common practice to handle and store them under ambient conditions. The air exposure leads to significant performance losses, and hampers the electrode fabrication, impeding their practical viability. Herein, we show that substituting a small amount of Al for Ni in the crystal lattice notably improves the chemical stability against air by limiting the formation of LiOH, Li 2 CO 3 , LiHCO 3 , and NiO in the near-surface region. The Al-doped high-Ni oxides display a high capacity retention with excellent rate capability and cycling stability after being exposed to air for 30 days. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Kinetic approach to the study of froth flotation applied to a lepidolite ore

NASA Astrophysics Data System (ADS)

Vieceli, Nathália; Durão, Fernando O.; Guimarães, Carlos; Nogueira, Carlos A.; Pereira, Manuel F. C.; Margarido, Fernanda

2016-07-01

The number of published studies related to the optimization of lithium extraction from low-grade ores has increased as the demand for lithium has grown. However, no study related to the kinetics of the concentration stage of lithium-containing minerals by froth flotation has yet been reported. To establish a factorial design of batch flotation experiments, we conducted a set of kinetic tests to determine the most selective alternative collector, define a range of pulp pH values, and estimate a near-optimum flotation time. Both collectors (Aeromine 3000C and Armeen 12D) provided the required flotation selectivity, although this selectivity was lost in the case of pulp pH values outside the range between 2 and 4. Cumulative mineral recovery curves were used to adjust a classical kinetic model that was modified with a non-negative parameter representing a delay time. The computation of the near-optimum flotation time as the maximizer of a separation efficiency (SE) function must be performed with caution. We instead propose to define the near-optimum flotation time as the time interval required to achieve 95%-99% of the maximum value of the SE function.

In Situ Raman Spectroscopic Studies on Concentration of Electrolyte Salt in Lithium-Ion Batteries by Using Ultrafine Multifiber Probes.

PubMed

Yamanaka, Toshiro; Nakagawa, Hiroe; Tsubouchi, Shigetaka; Domi, Yasuhiro; Doi, Takayuki; Abe, Takeshi; Ogumi, Zempachi

2017-03-09

Lithium-ion batteries have attracted considerable attention due to their high power density. The change in concentration of salt in the electrolyte solution in lithium-ion batteries during operation causes serious degradation of battery performance. Herein, a new method of in situ Raman spectroscopy with ultrafine multifiber probes was developed to simultaneously study the concentrations of ions at several different positions in the electrolyte solution in deep narrow spaces between the electrodes in batteries. The total amount of ions in the electrolyte solution clearly changed during operation due to the low permeability of the solid-electrolyte interphase (SEI) at the anode for Li + permeation. The permeability, which is a key factor to achieve high battery performance, was improved (enhanced) by adding film-forming additives to the electrolyte solution to modify the properties of the SEI. The results provide important information for understanding and predicting phenomena occurring in a battery and for designing a superior battery. The present method is useful for analysis in deep narrow spaces in other electrochemical devices, such as capacitors. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

The conversion of a room temperature NaK loop to a high temperature MHD facility for Li/V blanket testing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Reed, C.B.; Haglund, R.C.; Miller, M.E.

1996-12-31

The Vanadium/Lithium system has been the recent focus of ANL`s Blanket Technology Pro-ram, and for the last several years, ANL`s Liquid Metal Blanket activities have been carried out in direct support of the ITER (International Thermonuclear Experimental Reactor) breeding blanket task area. A key feasibility issue for the ITER Vanadium/Lithium breeding blanket is the Near the development of insulator coatings. Design calculations, Hua and Gohar, show that an electrically insulating layer is necessary to maintain an acceptably low magneto-hydrodynamic (MHD) pressure drop in the current ITER design. Consequently, the decision was made to convert Argonne`s Liquid Metal EXperiment (ALEX) frommore » a 200{degrees}C NaK facility to a 350{degrees}C lithium facility. The upgraded facility was designed to produce MHD pressure drop data, test section voltage distributions, and heat transfer data for mid-scale test sections and blanket mockups at Hartmann numbers (M) and interaction parameters (N) in the range of 10{sup 3} to 10{sup 5} in lithium at 350{degrees}C. Following completion of the upgrade work, a short performance test was conducted, followed by two longer multiple-hour, MHD tests, all at 230{degrees}C. The modified ALEX facility performed up to expectations in the testing. MHD pressure drop and test section voltage distributions were collected at Hartmann numbers of 1000.« less

Conversion of a room temperature NaK loop to a high temperature MHD facility for Li/V blanket testing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Reed, C.B.; Haglund, R.C.; Miller, M.E.

1996-12-31

The Vanadium/Lithium system has been the recent focus of ANL`s Blanket Technology Program, and for the last several years, ANL`s Liquid Metal Blanket activities have been carried out in direct support of the ITER (International Thermonuclear Experimental Reactor) breeding blanket task area. A key feasibility issue for the ITER Vanadium/Lithium breeding blanket is the development of insulator coatings. Design calculations, Hua and Gohar, show that an electrically insulating layer is necessary to maintain an acceptably low magnetohydrodynamic (MHD) pressure drop in the current ITER design. Consequently, the decision was made to convert Argonne`s Liquid Metal EXperiment (ALEX) from a 200{degree}Cmore » NaK facility to a 350{degree}C lithium facility. The upgraded facility was designed to produce MHD pressure drop data, test section voltage distributions, and heat transfer data for mid-scale test sections and blanket mockups at Hartmann numbers (M) and interaction parameters (N) in the range of 10{sup 3} to 10{sup 5} in lithium at 350{degree}C. Following completion of the upgrade work, a short performance test was conducted, followed by two longer, multiple-hour, MHD tests, all at 230{degree}C. The modified ALEX facility performed up to expectations in the testing. MHD pressure drop and test section voltage distributions were collected at Hartmann numbers of 1000. 4 refs., 2 figs.« less

High Temperature Thermosetting Polyimide Nanocomposites Prepared with Reduced Charge Organoclay

NASA Technical Reports Server (NTRS)

Campbell, Sandi; Liang, Margaret I.

2005-01-01

The naturally occurring sodium and calcium cations found in bentonite clay galleries were exchanged with lithium cations. Following the cation exchange, a series of reduced charge clays were prepared by heat treatment of the lithium bentonite at 130 C, 150 C, or 170 C. Inductively coupled plasma (ICP) analysis showed that heating the lithium clay at elevated temperatures reduced its cation exchange capacity. Ion exchange of heat-treated clays with either a protonated alkyl amine or a protonated aromatic diamine resulted in decreasing amounts of the organic modifier incorporated into the lithium clay. The level of silicate dispersion in a thermosetting polyimide matrix was dependent upon the temperature of Li-clay heat treatment as well as the organic modification. In general, clays treated at 150 C or 170 C, and exchanged with protonated octadcylamine or protonated 2,2'-dimethlybenzidine (DMBZ) showed a higher degree of dispersion than clays treated at 130 C, or exchanged with protonated dodecylamine. Dynamic mechanical analysis showed little change in the storage modulus or T(sub g) of the nanocomposites compared to the base resin. However, long term isothermal aging of the samples showed a significant decrease in the resin oxidative weight loss. Nanocomposite samples aged in air for 1000 hours at 288 C showed of to a decrease in weight loss compared to that of the base resin. This again was dependent on the temperature at which the Li-clay was heated and the choice of organic modification.

An overview of preparation and applications of stabilized zero-valent iron nanoparticles for soil and groundwater remediation.

PubMed

Zhao, Xiao; Liu, Wen; Cai, Zhengqing; Han, Bing; Qian, Tianwei; Zhao, Dongye

2016-09-01

Nano-scale zero-valent iron (nZVI) is one of the most intensively studied materials for environmental cleanup uses over the past 20 years or so. Freshly prepared nZVI is highly reactive due to its high specific surface area and strong reducing power. Over years, the classic borohydride reduction method for preparing nZVI has been modified by use of various stabilizers or surface modifiers to acquire more stable and soil deliverable nZVI for treatment of different organic and inorganic contaminants in water and soil. While most studies have been focused on testing nZVI for water treatment, the greater potential or advantage of nZVI appears to be for in situ remediation of contaminated soil and groundwater by directly delivering stabilized nZVI into the contaminated subsurface as it was proposed from the beginning. Compared to conventional remediation practices, the in situ remediation technique using stabilized nZVI offers some unique advantages. This work provides an update on the latest development of stabilized nZVI for various environmental cleanup uses, and overviews the evolution and environmental applications of stabilized nZVI. Commonly used stabilizers are compared and the stabilizing mechanisms are discussed. The effectiveness and constraints of the nZVI-based in situ remediation technology are summarized. This review also reveals some critical knowledge gaps and research needs, such as interactions between delivered nZVI and the local biogeochemical conditions. Copyright © 2016 Elsevier Ltd. All rights reserved.

Modified lithium vanadium oxide electrode materials products and methods

DOEpatents

Thackeray, Michael M.; Kahaian, Arthur J.; Visser, Donald R.; Dees, Dennis W.; Benedek, Roy

1999-12-21

A method of improving certain vanadium oxide formulations is presented. The method concerns fluorine doping formulations having a nominal formula of LiV.sub.3 O.sub.8. Preferred average formulations are provided wherein the average oxidation state of the vanadium is at least 4.6. Herein preferred fluorine doped vanadium oxide materials, electrodes using such materials, and batteries including at least one electrode therein comprising such materials are provided.

Optical and vibrational spectroscopy of Ba0.85Ca0.15Zr0.1Ti0.9O3 modified lithium borate glass ceramics

NASA Astrophysics Data System (ADS)

Viswanath, Pamarti; Prashanth, Sadhu Sai Pavan; Molli, Muralikrishna; Wicram, Jaschin Prem; Sai Muthukumar, V.

2018-04-01

Glass ceramics are excellent replacement for single crystalline materials which are expensive and difficult to fabricate. In this context, we have attempted to fabricate glass nanocomposites comprising of Lithium Borate glass matrix embedded with lead free ferroelectric Ba0.85Ca0.15Zr0.1Ti0.9O3 (BCZT). Both of these functional materials are known to exhibit excellent ferroelectric behavior and are currently explored for various device applications. We have prepared these novel glass nanocomposite using melt-quenching techniquein various chemical composition involving different molar ratio. x(Ba0.85Ca0.15Zr0.1Ti0.9O3)-(1-x)(Li2O.2B2O3) where (x=0.1,0.2,0.3,0.4). The as-quenched samples exhibited amorphous nature as revealed by X-ray Diffraction studies. With the increase in BCZT content we have observed significant alteration in optical bandgap and Urbach energy. The tailoring of optical properties by tuning the structure was probed by Raman vibrational spectroscopy which confirmed the dominant role played by BCZT as a network modifier in these borate glasses. Concomitantly, these glass nanocomposites were found to be excellent UV absorbers.

Enhanced photocatalytic activity of wool fibers having titanium dioxide nanoparticles formed inside their cortex

NASA Astrophysics Data System (ADS)

Zhang, Hui; Sun, Runjun; Wu, Hailiang; Mao, Ningtao

2018-07-01

A wool-TiO2 nanoparticle composite material having TiO2 nanoparticles both infiltrated in the matrix between macrofibrils inside cortical cells of wool fibers and grafted on the fiber surface is obtained in this study, and the wool-nanoparticle composite material is found to have highly photocatalytic activities with an extremely narrow band gap of 2.8 eV. The wool fibers are obtained using three successive technical steps: wool fibers are swollen by using lithium bromide, then saturated with tetrabutyl titanate ethanol solution and subsequently treated in boiling water. It was demonstrated that the chemical bonds formed between the as-synthesized TiO2 nanoparticles and the wool fibers swollen by lithium bromide include C‑Ti4+(Ti3+), N‑Ti4+(Ti3+), O‑Ti3+, and S‑Ti4+(Ti3+) bonds. The modified wool fibers have shown markedly improved photocatalytic efficiency due to their enhanced visible light absorption capability, which is much better than the (N-doped) TiO2 coated wool fibers. In contrast, TiO2 modified wool fibers swollen by using formic acid have poorer photoactivity, this might be due to the elimination of trivalent titanium between TiO2 nanoparticles and the wool fibers.

Effect of synthesizing method on the properties of LiFePO4/C composite for rechargeable lithium-ion batteries

NASA Astrophysics Data System (ADS)

Yoon, Man-Soon; Islam, Mobinul; Park, Young Min; Ur, Soon-Chul

2013-03-01

Olivine-type LiFePO4/C cathode materials are fabricated with FePO4 powders that are pre-synthesized by two different processes from iron chloride solution. Process I is a modified precipitation method which is implemented by the pH control of a solution using NH4OH to form FePO4 precipitates at room temperature. Process II is a conventional precipitation method, of which H3PO4 (85%) solution is gradually added to a FeCl3 solution during the process to maintain a designated mole ratio. The solution is subsequently aged at 90°C in a water bath until FePO4 precipitates appear. In order to synthesize LiFePO4/C composites, each batch of FePO4 powders is then mixed with pre-milled lithium carbonate and glucose (8 wt. %) as a carbon source in a ball-mill. The structural characteristics of both LiFePO4/C composites fabricated using iron phospates from two different routes have been examined employing XRD and SEM. The modified precipitation process is considered to be a relatively simple and effective process for the preparation of LiFePO4/C composites owing to their excellent electrochemical properties and rate capabilities.

Improvement of electrochemical performance of nickel rich LiNi0.6Co0.2Mn0.2O2 cathode active material by ultrathin TiO2 coating.

PubMed

Qin, CanCan; Cao, JiaLi; Chen, Jun; Dai, GaoLe; Wu, TongFu; Chen, Yanbin; Tang, YueFeng; Li, AiDong; Chen, Yanfeng

2016-06-21

LiNi0.6Co0.2Mn0.2O2 cathode material has been surface-modified by coating with ultrathin TiO2via atomic layer deposition (ALD) technology to improve the electrochemical performance of LiNi0.6Co0.2Mn0.2O2 cathodes for lithium ion batteries. Within the cut-off voltage of 2.5-4.3 V, the coated sample delivers an initial discharge capacity of 187.7 mA h g(-1) at 0.1 C and with a capacity retention about 85.9% after 100 cycles at 1 C, which provides a significant improvement in terms of discharge capacity and cyclability, as compared with those of the bare one. Such enhanced electrochemical performance of the coated sample is ascribed to its high-quality ultrathin coating of amorphous TiO2, which can protect the active material from HF attack, withstand the dissolution of metal ions in the electrode and favor the lithium diffusion of oxide as proved by electrochemical impedance spectroscopy (EIS) tests. TiO2 coating via the ALD process provides a potential approach for battery factories to surface-modify Ni-rich electrode materials so as to realize improvements in electrochemical performance.

Enhanced photocatalytic activity of wool fibers having titanium dioxide nanoparticles formed inside their cortex.

PubMed

Zhang, Hui; Sun, Runjun; Wu, Hailiang; Mao, Ningtao

2018-05-01

A wool-TiO2 nanoparticle composite material having TiO2 nanoparticles both infiltrated in the matrix between macrofibrils inside cortical cells of wool fibers and grafted on the fiber surface is obtained in this study, and the wool-nanoparticle composite material is found to have highly photocatalytic activities with an extremely narrow band gap of 2.8 eV. The wool fibers are obtained using three successive technical steps: wool fibers are swollen by using lithium bromide, then saturated with tetrabutyl titanate ethanol solution and subsequently treated in boiling water. It was demonstrated that the chemical bonds formed between the as-synthesized TiO2 nanoparticles and the wool fibers swollen by lithium bromide include C-Ti4+(Ti3+), N-Ti4+(Ti3+), O-Ti3+, and S-Ti4+(Ti3+) bonds. The modified wool fibers have shown markedly improved photocatalytic efficiency due to their enhanced visible light absorption capability, which is much better than the (N-doped) TiO2 coated wool fibers. In contrast, TiO2 modified wool fibers swollen by using formic acid have poorer photoactivity, this might be due to the elimination of trivalent titanium between TiO2 nanoparticles and the wool fibers. © 2018 IOP Publishing Ltd.

Association of Lithium in Drinking Water With the Incidence of Dementia.

PubMed

Kessing, Lars Vedel; Gerds, Thomas Alexander; Knudsen, Nikoline Nygård; Jørgensen, Lisbeth Flindt; Kristiansen, Søren Munch; Voutchkova, Denitza; Ernstsen, Vibeke; Schullehner, Jörg; Hansen, Birgitte; Andersen, Per Kragh; Ersbøll, Annette Kjær

2017-10-01

Results from animal and human studies suggest that lithium in therapeutic doses may improve learning and memory and modify the risk of developing dementia. Additional preliminary studies suggest that subtherapeutic levels, including microlevels of lithium, may influence human cognition. To investigate whether the incidence of dementia in the general population covaries with long-term exposure to microlevels of lithium in drinking water. This Danish nationwide, population-based, nested case-control study examined longitudinal, individual geographic data on municipality of residence and data from drinking water measurements combined with time-specific data from all patients aged 50 to 90 years with a hospital contact with a diagnosis of dementia from January 1, 1970, through December 31, 2013, and 10 age- and sex-matched control individuals from the Danish population. The mean lithium exposure in drinking water since 1986 was estimated for all study individuals. Data analysis was performed from January 1, 1995, through December 31, 2013. A diagnosis of dementia in a hospital inpatient or outpatient contact. Diagnoses of Alzheimer disease and vascular dementia were secondary outcome measures. In primary analyses, distribution of lithium exposure was compared between patients with dementia and controls. A total of 73 731 patients with dementia and 733 653 controls (median age, 80.3 years; interquartile range, 74.9-84.6 years; 44 760 female [60.7%] and 28 971 male [39.3%]) were included in the study. Lithium exposure was statistically significantly different between patients with a diagnosis of dementia (median, 11.5 µg/L; interquartile range, 6.5-14.9 µg/L) and controls (median, 12.2 µg/L; interquartile range, 7.3-16.0 µg/L; P < .001). A nonlinear association was observed. Compared with individuals exposed to 2.0 to 5.0 µg/L, the incidence rate ratio (IRR) of dementia was decreased in those exposed to more than 15.0 µg/L (IRR, 0.83; 95% CI, 0.81-0.85; P < .001) and 10.1 to 15.0 µg/L (IRR, 0.98; 95% CI, 0.96-1.01; P = .17) and increased with 5.1 to 10.0 µg/L (IRR, 1.22; 95% CI, 1.19-1.25; P < .001). Similar patterns were found with Alzheimer disease and vascular dementia as outcomes. Long-term increased lithium exposure in drinking water may be associated with a lower incidence of dementia in a nonlinear way; however, confounding from other factors associated with municipality of residence cannot be excluded.

Nickel-Hydrogen and Lithium Ion Space Batteries

NASA Technical Reports Server (NTRS)

Reid, Robert O., II

2004-01-01

The tasks of the Electrochemistry Branch of NASA Glenn Research Center are to improve and develop high energy density and rechargeable, life-long batteries. It is with these batteries that people across the globe are able to power their cell phones, laptop computers, and cameras. Here, at NASA Glenn Research Center, the engineers and scientists of the Electrochemistry branch are leading the way in the development of more powerful, long life batteries that can be used to power space shuttles and satellites. As of now, the cutting edge research and development is being done on nickel-hydrogen batteries and lithium ion batteries. Presently, nickel-hydrogen batteries are common types of batteries that are used to power satellites, space stations, and space shuttles, while lithium batteries are mainly used to power smaller appliances such as portable computers and phones. However, the Electrochemistry Branch at NASA Glenn Research Center is focusing more on the development of lithium ion batteries for deep space use. Because of the limitless possibilities, lithium ion batteries can revolutionize the space industry for the better. When compared to nickel-hydrogen batteries, lithium ion batteries possess more advantages than its counterpart. Lithium ion batteries are much smaller than nickel-hydrogen batteries and also put out more power. They are more energy efficient and operate with much more power at a reduced weight than its counterpart. Lithium ion cells are also cheaper to make, possess flexibility that allow for different design modifications. With those statistics in hand, the Electrochemistry Branch of NASA Glenn has decided to shut down its Nickel-Hydrogen testing for lithium ion battery development. Also, the blackout in the summer of 2003 eliminated vital test data, which played a part in shutting down the program. from the nickel-hydrogen batteries and compare it to past data. My other responsibilities include superheating the electrolyte that is used in the nickel-hydrogen cell in a calorimeter to test its performance under various conditions. 1 used a program called Arbin to study my data. The Arbin allows me to look at different parameters such as pressure and time and how they affect the changing temperature of the electrolyte that is being tested. In addition, I had the responsibility of taking apart and modifying battery coolers that would be used. My mentors told me that the batteries kept shutting down, so it was my responsibility to remove excess fan grilles, rotate the fans, and then switch the aluminum standoffs with nylon ones so that the coolers could operate without problems. My last task is to collect all the battery test data and organize them into charts using Microsoft Excel, before the Branch is able to conduct its research on lithium ion batteries. Therefore, during my tenure, it is my responsibility to take down final test data

The Reduction of a Nitrile (CN) Group by Sodium Borohydride. The Preparation of Phosphine--Amine and Phosphine--Iimidate Complesex of Tungsten Carbonyl.

ERIC Educational Resources Information Center

Faust, Kristen E.; Storhoff, Bruce N.

1989-01-01

Describes an experiment for advanced-level undergraduate students for extending student experiences involving recording and interpreting infrared (IR) and nuclear magnetic resonance (NMR) spectra from reactions of organometallic compounds. Experimental procedures, analyses and structural assignments, and suggestions for extension and modification…

FT–Raman investigation of bleaching of spruce thermomechanical pulp

Treesearch

U.P. Agarwal; L.L. Landucci

2004-01-01

Spruce thermomechanical pulp was bleached initially by alkaline hydrogen peroxide and then by sodium dithionite and sodium borohydride. Near-infrared Fourier-transform–Raman spectroscopy revealed that spectral differences were due primarily to coniferaldehyde and p-quinone structures in lignin, new direct evidence that bleaching removes p-quinone structures. In...

Photoinduced Formation and Characterization of Metallic Silver and Gold Particles in VYCOR (trademark) Glass

DTIC Science & Technology

2004-12-01

agent such as citric acid or sodium borohydride. Other systems have been studied in which polymers such as poly vinyl alcohol/poly acrylic acid or...Wu, M. H., Henderson, D. O., Malone, K., Mills, G., Meldrum , A., Proceedings of the Electrochemical Society, 1999, 98-11, 439.

Impregnated metal-polymeric functional beads

NASA Technical Reports Server (NTRS)

Rembaum, Alan (Inventor); Volksen, Willi (Inventor)

1980-01-01

Amine containing polymeric microspheres such as polyvinyl pyridine are complexed with metal salts or acids containing metals such as gold, platinum or iron. After reduction with sodium borohydride, the salt is reduced to finely divided free metal or metal oxides, useful as catalysts. Microspheres containing covalent bonding sites can be used for labeling or separating proteins.

Impregnated metal-polymeric functional beads

NASA Technical Reports Server (NTRS)

Rembaum, Alan (Inventor); Volksen, Willi (Inventor)

1978-01-01

Amine containing polymeric microspheres such as polyvinyl pyridine are complexed with metal salts or acids containing metals such as gold, platinum or iron. After reduction with sodium borohydride, the salt is reduced to finely divided free metal or metal oxides, useful as catalysts. Microspheres containing covalent bonding sites can be used for labeling or separating proteins.

NMR Studies of Structure-Reactivity Relationships in Carbonyl Reduction: A Collaborative Advanced Laboratory Experiment

ERIC Educational Resources Information Center

Marincean, Simona; Smith, Sheila R.; Fritz, Michael; Lee, Byung Joo; Rizk, Zeinab

2012-01-01

An upper-division laboratory project has been developed as a collaborative investigation of a reaction routinely taught in organic chemistry courses: the reduction of carbonyl compounds by borohydride reagents. Determination of several trends regarding structure-activity relationship was possible because each student contributed his or her results…

Process for production of a borohydride compound

DOEpatents

Allen, Nathan Tait; Butterick, III, Robert; Chin, Arthur Achhing; Millar, Dean Michael; Molzahn, David Craig

2014-08-19

A process for production of a borohydride compound M(BH.sub.4).sub.y. The process has three steps. The first step combines a compound of formula (R.sup.1O).sub.yM with aluminum, hydrogen and a metallic catalyst containing at least one metal selected from the group consisting of titanium, zirconium, hafnium, niobium, vanadium, tantalum and iron to produce a compound of formula M(AlH.sub.3OR.sup.1).sub.y, wherein R.sup.1 is phenyl or phenyl substituted by at least one alkyl or alkoxy group; M is an alkali metal, Be or Mg; and y is one or two; wherein the catalyst is present at a level of at least 200 ppm based on weight of aluminum. The second step combines the compound of formula M(AlH.sub.3OR.sup.1).sub.y with a borate, boroxine or borazine compound to produce M(BH.sub.4).sub.y and a byproduct mixture containing alkali metal and aluminum aryloxides. The third step separates M(BH.sub.4).sub.y from the byproduct mixture.

High performance polymer chemical hydrogel-based electrode binder materials for direct borohydride fuel cells

NASA Astrophysics Data System (ADS)

Choudhury, Nurul A.; Ma, Jia; Sahai, Yogeshwar; Buchheit, Rudolph G.

Novel, cost-effective, high-performance, and environment-friendly electrode binders, comprising polyvinyl alcohol chemical hydrogel (PCH) and chitosan chemical hydrogel (CCH), are reported for direct borohydride fuel cells (DBFCs). PCH and CCH binders-based electrodes have been fabricated using a novel, simple, cost-effective, time-effective, and environmentally benign technique. Morphologies and electrochemical performance in DBFCs of the chemical hydrogel binder-based electrodes have been compared with those of Nafion ® binder-based electrodes. Relationships between the performance of binders in DBFCs with structural features of the polymers and the polymer-based chemical hydrogels are discussed. The CCH binder exhibited better performance than a Nafion ® binder whereas the PCH binder exhibited comparable performance to Nafion ® in DBFCs operating at elevated cell temperatures. The better performance of CCH binder at higher operating cell temperatures has been ascribed to the hydrophilic nature and water retention characteristics of chitosan. DBFCs employing CCH binder-based electrodes and a Nafion ®-117 membrane as an electrolyte exhibited a maximum peak power density of about 589 mW cm -2 at 70 °C.

Silver nanoparticles-containing dual-function hydrogels based on a guar gum-sodium borohydride system

PubMed Central

Dai, Lei; Nadeau, Ben; An, Xingye; Cheng, Dong; Long, Zhu; Ni, Yonghao

2016-01-01

Dual-function hydrogels, possessing both stimuli-responsive and self-healing properties, have recently attracted attention of both chemists and materials scientists. Here we report a new paradigm using natural polymer (guar gum, GG) and sodium borohydride (NaBH4), for the preparation of silver nanoparticles (AgNPs)-containing smart hydrogels in a simple, fast and economical way. NaBH4 performs as a reducing agent for AgNPs synthesis using silver nitrate (AgNO3) as the precursor. Meanwhile, sodium metaborate (NaBO2) (from NaBH4) behaves as a cross-linking agent between GG molecular chains. The AgNPs/GG hydrogels with excellent viscoelastic properties can be obtained within 3 min at room temperature without the addition of other cross-linkers. The resultant AgNPs/GG hydrogels are flowable and injectable, and they possess excellent pH/thermal responsive properties. Additionally, they exhibit rapid self-healing capacity. This work introduces a facile and scale-up way to prepare a class of hydrogels that can have great potential to biomedical and other industrial applications. PMID:27819289

Flagellar filament bio-templated inorganic oxide materials - towards an efficient lithium battery anode.

PubMed

Beznosov, Sergei N; Veluri, Pavan S; Pyatibratov, Mikhail G; Chatterjee, Abhijit; MacFarlane, Douglas R; Fedorov, Oleg V; Mitra, Sagar

2015-01-13

Designing a new generation of energy-intensive and sustainable electrode materials for batteries to power a variety of applications is an imperative task. The use of biomaterials as a nanosized structural template for these materials has the potential to produce hitherto unachievable structures. In this report, we have used genetically modified flagellar filaments of the extremely halophilic archaea species Halobacterium salinarum to synthesize nanostructured iron oxide composites for use as a lithium-ion battery anode. The electrode demonstrated a superior electrochemical performance compared to existing literature results, with good capacity retention of 1032 mAh g(-1) after 50 cycles and with high rate capability, delivering 770 mAh g(-1) at 5 A g(-1) (~5 C) discharge rate. This unique flagellar filament based template has the potential to provide access to other highly structured advanced energy materials in the future.

Internal-short-mitigating current collector for lithium-ion battery

NASA Astrophysics Data System (ADS)

Wang, Meng; Le, Anh V.; Noelle, Daniel J.; Shi, Yang; Meng, Y. Shirley; Qiao, Yu

2017-05-01

Mechanical abuse often causes thermal runaway of lithium-ion battery (LIB). When a LIB cell is impacted, radial cracks can be formed in the current collector, separating the electrode into petals. As separator ruptures, the petals on positive and negative electrodes may contact each other, forming internal short circuit (ISC). In this study, we conducted an experimental investigation on LIB coin cells with current collectors modified by surface notches. Our testing results showed that as the current collector contained appropriate surface notches, the cracking mode of electrode in a damaged LIB cell could be adjusted. Particularly, if a complete circumferential crack was generated, the petals would be cut off, which drastically reduced the area of electrode involved in ISC and the associated heat generation rate. A parameterized study was performed to analysis various surface-notch configurations. We identified an efficient surface-notch design that consistently led to trivial temperature increase of ISC.

Flagellar filament bio-templated inorganic oxide materials – towards an efficient lithium battery anode

PubMed Central

Beznosov, Sergei N.; Veluri, Pavan S.; Pyatibratov, Mikhail G.; Chatterjee, Abhijit; MacFarlane, Douglas R.; Fedorov, Oleg V.; Mitra, Sagar

2015-01-01

Designing a new generation of energy-intensive and sustainable electrode materials for batteries to power a variety of applications is an imperative task. The use of biomaterials as a nanosized structural template for these materials has the potential to produce hitherto unachievable structures. In this report, we have used genetically modified flagellar filaments of the extremely halophilic archaea species Halobacterium salinarum to synthesize nanostructured iron oxide composites for use as a lithium-ion battery anode. The electrode demonstrated a superior electrochemical performance compared to existing literature results, with good capacity retention of 1032 mAh g−1 after 50 cycles and with high rate capability, delivering 770 mAh g−1 at 5 A g−1 (~5 C) discharge rate. This unique flagellar filament based template has the potential to provide access to other highly structured advanced energy materials in the future. PMID:25583370

Influence of scandium on the microstructure and strength properties of the welded joint at the laser welding of aluminum-lithium alloys

NASA Astrophysics Data System (ADS)

Malikov, A. G.; Golyshev, A. A.; Ivanova, M. Yu.

2017-10-01

Today, aeronautical equipment manufacture involves up-to-date high-strength aluminum alloys of decreased density resulting from lithium admixture. Various technologies of fusible welding of these alloys are being developed. Serious demands are imposed to the welded joints of aluminum alloys in respect to their strength characteristics. The paper presents experimental investigations of the optimization of the laser welding of aluminum alloys with the scandium-modified welded joint. The effect of scandium on the micro-and macro-structure has been studied as well as the strength characteristics of the welded joint. It has been found that scandium under in the laser welding process increases the welded joint elasticity for the system Al-Mg-Li, aluminum alloy 1420 by 20 %, and almost doubles the same for the system Al-Cu-Li, aluminum alloy 1441.

Micro- and nanodomain imaging in uniaxial ferroelectrics: Joint application of optical, confocal Raman, and piezoelectric force microscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shur, V. Ya., E-mail: vladimir.shur@urfu.ru; Zelenovskiy, P. S.

2014-08-14

The application of the most effective methods of the domain visualization in model uniaxial ferroelectrics of lithium niobate (LN) and lithium tantalate (LT) family, and relaxor strontium-barium niobate (SBN) have been reviewed in this paper. We have demonstrated the synergetic effect of joint usage of optical, confocal Raman, and piezoelectric force microscopies which provide extracting of the unique information about formation of the micro- and nanodomain structures. The methods have been applied for investigation of various types of domain structures with increasing complexity: (1) periodical domain structure in LN and LT, (2) nanodomain structures in LN, LT, and SBN, (3)more » nanodomain structures in LN with modified surface layer, (4) dendrite domain structure in LN. The self-assembled appearance of quasi-regular nanodomain structures in highly non-equilibrium switching conditions has been considered.« less

Flagellar filament bio-templated inorganic oxide materials - towards an efficient lithium battery anode

NASA Astrophysics Data System (ADS)

Beznosov, Sergei N.; Veluri, Pavan S.; Pyatibratov, Mikhail G.; Chatterjee, Abhijit; Macfarlane, Douglas R.; Fedorov, Oleg V.; Mitra, Sagar

2015-01-01

Designing a new generation of energy-intensive and sustainable electrode materials for batteries to power a variety of applications is an imperative task. The use of biomaterials as a nanosized structural template for these materials has the potential to produce hitherto unachievable structures. In this report, we have used genetically modified flagellar filaments of the extremely halophilic archaea species Halobacterium salinarum to synthesize nanostructured iron oxide composites for use as a lithium-ion battery anode. The electrode demonstrated a superior electrochemical performance compared to existing literature results, with good capacity retention of 1032 mAh g-1 after 50 cycles and with high rate capability, delivering 770 mAh g-1 at 5 A g-1 (~5 C) discharge rate. This unique flagellar filament based template has the potential to provide access to other highly structured advanced energy materials in the future.

Ion transport restriction in mechanically strained separator membranes

NASA Astrophysics Data System (ADS)

Cannarella, John; Arnold, Craig B.

2013-03-01

We use AC impedance methods to investigate the effect of mechanical deformation on ion transport in commercial separator membranes and lithium-ion cells as a whole. A Bruggeman type power law relationship is found to provide an accurate correlation between porosity and tortuosity of deformed separators, which allows the impedance of a separator membrane to be predicted as a function of deformation. By using mechanical compression to vary the porosity of the separator membranes during impedance measurements it is possible to determine both the α and γ parameters from the modified Bruggeman relation for individual separator membranes. From impedance testing of compressed pouch cells it is found that separator deformation accounts for the majority of the transport restrictions arising from compressive stress in a lithium-ion cell. Finally, a charge state dependent increase in the impedance associated with charge transfer is observed with increasing cell compression.

Extracorporeal Treatment for Lithium Poisoning: Systematic Review and Recommendations from the EXTRIP Workgroup

PubMed Central

Decker, Brian S.; Goldfarb, David S.; Dargan, Paul I.; Friesen, Marjorie; Gosselin, Sophie; Hoffman, Robert S.; Lavergne, Valéry; Nolin, Thomas D.

2015-01-01

The Extracorporeal Treatments in Poisoning Workgroup was created to provide evidence-based recommendations on the use of extracorporeal treatments in poisoning. Here, the EXTRIP workgroup presents its recommendations for lithium poisoning. After a systematic literature search, clinical and toxicokinetic data were extracted and summarized following a predetermined format. The entire workgroup voted through a two-round modified Delphi method to reach a consensus on voting statements. A RAND/UCLA Appropriateness Method was used to quantify disagreement, and anonymous votes were compiled and discussed in person. A second vote was conducted to determine the final workgroup recommendations. In total, 166 articles met inclusion criteria, which were mostly case reports, yielding a very low quality of evidence for all recommendations. A total of 418 patients were reviewed, 228 of which allowed extraction of patient-level data. The workgroup concluded that lithium is dialyzable (Level of evidence=A) and made the following recommendations: Extracorporeal treatment is recommended in severe lithium poisoning (1D). Extracorporeal treatment is recommended if kidney function is impaired and the [Li+] is >4.0 mEq/L, or in the presence of a decreased level of consciousness, seizures, or life-threatening dysrhythmias irrespective of the [Li+] (1D). Extracorporeal treatment is suggested if the [Li+] is >5.0 mEq/L, significant confusion is present, or the expected time to reduce the [Li+] to <1.0 mEq/L is >36 hours (2D). Extracorporeal treatment should be continued until clinical improvement is apparent or [Li+] is <1.0 mEq/L (1D). Extracorporeal treatments should be continued for a minimum of 6 hours if the [Li+] is not readily measurable (1D). Hemodialysis is the preferred extracorporeal treatment (1D), but continuous RRT is an acceptable alternative (1D). The workgroup supported the use of extracorporeal treatment in severe lithium poisoning. Clinical decisions on when to use extracorporeal treatment should take into account the [Li+], kidney function, pattern of lithium toxicity, patient’s clinical status, and availability of extracorporeal treatments. PMID:25583292

Novel Slurry Electrolyte Containing Lithium Metasilicate for High Electrochemical Performance of a 5 V Cathode.

PubMed

Ren, Yonghuan; Mu, Daobin; Wu, Feng; Wu, Borong

2015-10-21

We report a novel slurry electrolyte with ultrahigh concentration of insoluble inorganic lithium metasilicate (Li2SiO3) that is exploited for lithium ion batteries to combine the merits of solid and liquid electrolytes. The safety, conductivity, and anodic and storage stabilities of the eletrolyte are examined, which are all enhanced compared to a base carbonate electrolyte. The compatibility of the elecrolyte with a LiNi0.5Mn1.5O4 cathode is evaluated under high voltage. A discharge capacity of 173.8 mAh g(-1) is still maintained after 120 cycles, whereas it is only 74.9 mAh g(-1) in the base electrolyte. Additionally, the rate capability of the LiNi0.5Mn1.5O4 cathode is also improved with reduced electrode polarization. TEM measurements indicate that the electrode interface is modified by Li2SiO3 with a thinner solid electrolyte interphase film. Density functional theory computations demonstrate that LiPF6 is stabilized against its decomposition by Li2SiO3. A possible path for the reaction between PF5 and Li2SiO3 is also proposed by deducing the transition states involved in the process using the DFT method.

Advanced carbon materials/olivine LiFePO4 composites cathode for lithium ion batteries

NASA Astrophysics Data System (ADS)

Gong, Chunli; Xue, Zhigang; Wen, Sheng; Ye, Yunsheng; Xie, Xiaolin

2016-06-01

In the past two decades, LiFePO4 has undoubtly become a competitive candidate for the cathode material of the next-generation LIBs due to its abundant resources, low toxicity and excellent thermal stability, etc. However, the poor electronic conductivity as well as low lithium ion diffusion rate are the two major drawbacks for the commercial applications of LiFePO4 especially in the power energy field. The introduction of highly graphitized advanced carbon materials, which also possess high electronic conductivity, superior specific surface area and excellent structural stability, into LiFePO4 offers a better way to resolve the issue of limited rate performance caused by the two obstacles when compared with traditional carbon materials. In this review, we focus on advanced carbon materials such as one-dimensional (1D) carbon (carbon nanotubes and carbon fibers), two-dimensional (2D) carbon (graphene, graphene oxide and reduced graphene oxide) and three-dimensional (3D) carbon (carbon nanotubes array and 3D graphene skeleton), modified LiFePO4 for high power lithium ion batteries. The preparation strategies, structure, and electrochemical performance of advanced carbon/LiFePO4 composite are summarized and discussed in detail. The problems encountered in its application and the future development of this composite are also discussed.

Electrochemical lithium intercalation into Bi2Sr2CaCu2O8+δ

NASA Astrophysics Data System (ADS)

Shimono, Takahiro; Kobayashi, Wataru; Nitani, Hiroaki; Kumai, Reiji; Moritomo, Yutaka

2013-04-01

We have prepared Li-intercalated LixBi2Sr2CaCu2O8+δ (x =0-2.0) samples by using electrochemical method, and performed synchrotron x-ray diffraction, Cu K-edge x-ray absorption fine structure (XAFS), and magnetic susceptibility measurements. With increasing x, a- and c-lattice parameters monotonically increase, which shows lithium intercalation into Bi2Sr2CaCu2O8+δ. Accompanied by the lithium insertion, the valence of Cu ion changes from Cu2+/Cu3+ to Cu1+/Cu2+ to realize charge neutrality. This change of the valence was detected by Cu K-edge XAFS measurement. A clear increase of spectral weight that corresponds to 1s→ 4pπ(3d10L) was observed at around 8982 eV with x. The superconducting (SC) transition temperature TC significantly changes from 74 K for x = 0 to 90 K for x = 0.8, which is attributed to modified density of states by the decrease of hole concentration. A volume fraction of the superconducting phase was 1-2 % for x >= 0.6 implying phase separation where Li-rich non SC phase and Li-poor SC phase coexist. Such a phase separation is universally seen in electrode active materials.

Lithiation Mechanism of Tunnel-Structured MnO 2 Electrode Investigated by In Situ Transmission Electron Microscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lee, Seung-Yong; Wu, Lijun; Poyraz, Altug S.

Manganese oxide (α-MnO 2) has been considered as a promising energy material, including as a lithium-based battery electrode candidate, due to its environmental friendliness. Thanks to its unique 1D [2 × 2] tunnel structure, α-MnO 2 can be applied to a cathode by insertion reaction and to an anode by conversion reaction in corresponding voltage ranges, in a lithium-based battery. Numerous reports have attributed its remarkable performance to its unique tunnel structure; however, the precise electrochemical reaction mechanism remains unknown. In this study, finding of the lithiation mechanism of α-MnO 2 nanowire by in situ transmission electron microscopy (TEM) ismore » reported. By elaborately modifying the existing in situ TEM experimental technique, rapid lithium-ion diffusion through the tunnels is verified. Furthermore, by tracing the full lithiation procedure, the evolution of the MnO intermediate phase and the development of the MnO and Li 2O phases with preferred orientations is demonstrated, which explains how the conversion reaction occurs in α-MnO 2 material. This study provides a comprehensive understanding of the electrochemical lithiation process and mechanism of α-MnO 2 material, in addition to the introduction of an improved in situ TEM biasing technique.« less

Lithiation Mechanism of Tunnel-Structured MnO 2 Electrode Investigated by In Situ Transmission Electron Microscopy

DOE PAGES

Lee, Seung-Yong; Wu, Lijun; Poyraz, Altug S.; ...

2017-10-06

Manganese oxide (α-MnO 2) has been considered as a promising energy material, including as a lithium-based battery electrode candidate, due to its environmental friendliness. Thanks to its unique 1D [2 × 2] tunnel structure, α-MnO 2 can be applied to a cathode by insertion reaction and to an anode by conversion reaction in corresponding voltage ranges, in a lithium-based battery. Numerous reports have attributed its remarkable performance to its unique tunnel structure; however, the precise electrochemical reaction mechanism remains unknown. In this study, finding of the lithiation mechanism of α-MnO 2 nanowire by in situ transmission electron microscopy (TEM) ismore » reported. By elaborately modifying the existing in situ TEM experimental technique, rapid lithium-ion diffusion through the tunnels is verified. Furthermore, by tracing the full lithiation procedure, the evolution of the MnO intermediate phase and the development of the MnO and Li 2O phases with preferred orientations is demonstrated, which explains how the conversion reaction occurs in α-MnO 2 material. This study provides a comprehensive understanding of the electrochemical lithiation process and mechanism of α-MnO 2 material, in addition to the introduction of an improved in situ TEM biasing technique.« less

Gravitino dark matter and the lithium primordial abundance within a pre-BBN modified expansion

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bailly, Sean, E-mail: sean.bailly@lapp.in2p3.fr

2011-03-01

We present supersymmetric scenarios with gravitino LSP and stau NLSP in the case of a non-standard model of cosmology with the addition of a dark component in the pre-BBN era. In the context of the standard model of cosmology, gravitino LSP has drawn quite some attention as it is a good candidate for dark matter. It is produced in scattering processes during reheating after inflation and from the decay of the stau. With a long lifetime, the stau decays during Big Bang Nucleosynthesis. It is strongly constrained by the abundance of light elements but can however address the known ''BBNmore » lithium problem''. It requires fairly massive staus m{sub τ-tilde}∼> 1TeV and puts an upper bound on the reheating temperature T{sub R} ≅ 10{sup 7} GeV which does not satisfy the requirements for thermal leptogenesis. For the non-standard cosmological scenario, the reheating temperature bound can be strongly relaxed T{sub R} >> 10{sup 9}GeV and the lithium-7 problem solved with a stau typical mass of m{sub τ-tilde} ∼ 600–700 GeV and down to ∼ 400GeV with a very important dark component that could enable possible production and detection at the LHC.« less

Synthesis and characterization of self-bridged silver vanadium oxide/CNTs composite and its enhanced lithium storage performance.

PubMed

Liang, Liying; Liu, Haimei; Yang, Wensheng

2013-02-07

The improvement of the electrochemical properties of electrode materials with large capacity and good capacity retention is becoming an important task in the field of lithium ion batteries (LIBs). We designed a function-oriented hybrid material consisting of silver vanadium oxide (β-AgVO(3)) nanowires modified with uniform Ag nanoparticles and multi-walled carbon nanotubes (CNTs) as a high-performance cathode material for LIBs. The Ag nanoparticles which precipitated automatically in the synthetic process act as a bridge between the β-AgVO(3) nanowires and CNTs, creating a self-bridged network structure. The Ag particles at the junction of the nanowires and CNTs facilitate electron transport from the CNTs to the nanowires, and thereby improve the electrical conductivity of the β-AgVO(3) nanowires and the composite. Moreover, the self-bridged network is hierarchically porous with a high surface area. When used as a cathode material, this composite electrode reveals high discharge capacities, excellent rate capability, and good cycling stability. The improved performance of the composite arises from its unique nanosized β-AgVO(3) nanowires with short diffusion pathway for lithium ions, efficient electron collection and transfer in the presence of Ag nanoparticles, together with excellent electrical conductivity of CNTs.

Flower-like hydrogenated TiO2(B) nanostructures as anode materials for high-performance lithium ion batteries

NASA Astrophysics Data System (ADS)

Zhang, Zhonghua; Zhou, Zhenfang; Nie, Sen; Wang, Honghu; Peng, Hongrui; Li, Guicun; Chen, Kezheng

2014-12-01

Flower-like hydrogenated TiO2(B) nanostructures have been synthesized via a facile solvothermal approach combined with hydrogenation treatment. The obtained TiO2(B) nanostructures show uniform and hierarchical flower-like morphology with a diameter of 124 ± 5 nm, which are further constructed by primary nanosheets with a thickness of 10 ± 1.2 nm. The Ti3+ species and/or oxygen vacancies are well introduced into the structures of TiO2(B) after hydrogen reduction, resulting in an enhancement in the electronic conductivity (up to 2.79 × 10-3 S cm-1) and the modified surface electrochemical activity. When evaluated for lithium storage capacity, the hydrogenated TiO2(B) nanostructures exhibit enhanced electrochemical energy storage performances compared to the pristine TiO2(B) nanostructures, including high capacity (292.3 mA h g-1 at 0.5C), excellent rate capability (179.6 mA h g-1 at 10C), and good cyclic stability (98.4% capacity retention after 200 cycles at 10C). The reasons for these improvements are explored in terms of the increased electronic conductivity and the facilitation of lithium ion transport arising from the introduction of oxygen vacancies and the unique flower-like morphologies.

Synthesis of nano-sized silicon from natural halloysite clay and its high performance as anode for lithium-ion batteries

NASA Astrophysics Data System (ADS)

Zhou, Xiangyang; Wu, Lili; Yang, Juan; Tang, Jingjing; Xi, Lihua; Wang, Biao

2016-08-01

Recently, nanostructured Si has been intensively studied as a promising anode candidate for lithium ion batteries due to its ultrahigh capacity. However, the downsizing of Si to nanoscale dimension is often impeded by complicated and expensive methods. In this work, natural halloysite clay was utilized for the production of Si nanoparticles through selective acid etching and modified magnesiothermic reduction processes. The physical and chemical changes of these samples during the various processes have been analyzed. The as-prepared Hsbnd Si from halloysite clay is composed of many interconnected Si nanoparticles with an average diameter of 20-50 nm. Owing to the small size and porous nature, the Hsbnd Si nanoparticles exhibit a satisfactory performance as an anode for lithium ion batteries. Without further modification, a stable capacity over 2200 mAh g-1 at a rate of 0.2 C after 100 cycles and a reversible capacity above 800 mAh g-1 at a rate of 1 C after 1000 cycles can be obtained. As a result, this synthetic route is cost-effective and can be scaled up for mass production of Si nanoparticles, which may facilitate valuable utilization of halloysite clay and further commercial application of Si-based anode materials.

PROFILING GLYCOL-SPLIT HEPARINS BY HPLC/MS ANALYSIS OF THEIR HEPARINASE-GENERATED OLIGOSACCHARIDES1

PubMed Central

Alekseeva, Anna; Casu, Benito; Torri, Giangiacomo; Pierro, Sabrina; Naggi, Annamaria

2012-01-01

Glycol-split (gs) heparins, obtained by periodate oxidation / borohydride reduction of heparin currently used as anticoagulant and antithrombotic drug, are arousing increasing interest in anti-cancer and anti-inflammation therapies. These new medical uses are favored by the loss of anticoagulant activity associated with glycol-splitting-induced inactivation of the antithrombin III (AT) binding site. The structure of gs-heparins has not been studied yet in detail. In this work, an ion-pair reversed-phase chromatography (IPRP-HPLC) coupled with electrospray ionization mass spectrometry (ESI-MS) widely used for unmodified heparin has been adapted to the analysis of oligosaccharides generated by digestion with heparinases of gs-heparins usually prepared from porcine mucosal heparin. The method has been also found very effective in analyzing glycol-split derivatives obtained from heparins of different animal and tissue origin. Besides the major 2-O-sulfated disaccharides, heparinase digests of gs-heparins mainly contain tetra- and hexasaccharides incorporating one or two gs residues, with distribution patterns typical for individual gs-heparins. A heptasulfated, mono-N-acetylated hexasaccharide with two gs residues has been shown to be a marker of the gs-modified AT binding site within heparin chains. PMID:23201389

Preparation of Ag/SiO2 nanocomposite and assessment of its antifungal effect on soybean plant (a Vietnamese species DT-26)

NASA Astrophysics Data System (ADS)

Chau Nguyen, Hoai; Thuy Nguyen, Thi; Hien Dao, Trong; Buu Ngo, Quoc; Pham, Hoang Long; Nguyen, Thi Bich Ngoc

2016-12-01

Soybean crop losses due to fungal diseases are considerable and directly depend on the severity of the disease. The objective of this study was to assess antifungal activity of silver/silica (Ag/SiO2) nanocomposite against crop pathogenic fungi (Fusarium oxysporium and Rhizoctonia solani) in soybean farming. Firstly, silica particles with a size ranging from 20 to 30 nm were modified with 3-aminopropyl triethoxysilane (APTES) for 2 h. Then these amino acid - functionalized silica particles were exposed to silver ion solution followed by reduction of silver ions with sodium borohydride to form Ag/SiO2 nanocomposite. The formation of the linkage between APTES and silica particles was confirmed by Fourier transform infrared (FTIR) spectroscopy. The surface plasmon absorption maximum at 400 nm confirmed the nano essence of the silver particles on silica particles. For the seed coating, bentonite from Lam Dong deposit, Vietnam, was used as an encapsulation substance, while carboxymethyl cellulose (CMC) was used as a binding agent. The assessment of fungicidal activity of the Ag/SiO2 nanocomposite produced showed that this product is effective in inhibition of the pathogenic fungi in soybean plant.

Growth of fluorescence gold clusters using photo-chemically activated ligands

NASA Astrophysics Data System (ADS)

Mishra, Dinesh; Aldeek, Fadi; Michael, Serge; Palui, Goutam; Mattoussi, Hedi

2016-03-01

Ligands made of lipoic acid (LA) appended with a polyethylene glycol (PEG) chain have been used in the aqueous phase growth of luminescent gold clusters with distinct emission from yellow to near-IR, using two different routes. In the first route, the gold-ligand complex was chemically reduced using sodium borohydride in alkaline medium, which gave near- IR luminescent gold clusters with maximum emission around 745 nm. In the second method, LA-PEG ligand was photochemically modified to a mixture of thiols, oligomers and oxygenated species under UV-irradiation, which was then used as both reducing agent and stabilizing ligand. By adjusting the pH, temperature, and time of the reaction, we were able to obtain clusters with two distinct emission properties. Refluxing the gold-ligand complex in alkaline medium in the presence of excess ligand gave yellow emission within the first two hours and the emission shifted to red after overnight reaction. Mass spectrometry and chemical assay were used to understand the photo-chemical transformation of Lipoic Acid (LA). Mass spectroscopic studies showed the photo-irradiated product contains thiols, oligomers (dimers, trimers and tetramers) as well as oxygenated species. The amount of thiol formed under different conditions of irradiation was estimated using Ellman's assay.

Synthesis of FeCoB amorphous nanoparticles and application in ferrofluids

NASA Astrophysics Data System (ADS)

Zhao, Shuchun; Bian, Xiufang; Yang, Chuncheng; Yu, Mengchun; Wang, Tianqi

2018-03-01

Magnetic FeCoB amorphous nanoparticles were successfully synthesized by borohydride reduction in water/n-hexane (W/He) microemulsions. The as-prepared FeCoB alloys are amorphous and spherical nanoparticles with an average particle size about 10.7 nm, compared to FeCoB alloys with an average particle size about 304.2 nm which were synthesized by a conventional aqua-solution method. Furthermore, three kinds of FeCoB ferrofluids (FFs) were prepared by dispersing FeCoB particles into W/He microemulsion, water and silicone oil respectively. Results show that the W/He-based FeCoB FFs are superparamagnetic with saturation magnetization (Ms) reaching to 12.4 emu/g. Besides, compared to water-based and silicone oil-based FFs, W/He-based FeCoB FFs exhibit high stability, with magnetic weights decreasing slightly even under the magnetic field intensity of H = 210 mT. In the W/He-based FeCoB FFs, interfacial tensions of water phase and oil phase are supposed to prevent the agglomeration and sedimentation of FeCoB nanoparticles dispersed in different water droplets of the microemulsion, compared to the current stabilizing method of directly modifying the surface of particles.

The Enhanced Catalytic Activities of Asymmetric Au-Ni Nanoparticle Decorated Halloysite-Based Nanocomposite for the Degradation of Organic Dyes

NASA Astrophysics Data System (ADS)

Jia, Lei; Zhou, Tao; Xu, Jun; Li, Xiaohui; Dong, Kun; Huang, Jiancui; Xu, Zhouqing

2016-02-01

Janus particles (JPs) are unique among the nano-/microobjects because they provide asymmetry and can thus impart drastically different chemical or physical properties. In this work, we have fabricated the magnetic halloysite nanotube (HNT)-based HNTs@Fe3O4 nanocomposite (NCs) and then anchored the Janus Au-Ni or isotropic Au nanoparticles (NPs) to the surface of external wall of sulfydryl modified magnetic nanotubes. The characterization by physical methods authenticates the successful fabrication of two different magnetic HNTs@Fe3O4@Au and HNTs@Fe3O4@Au-Ni NCs. The catalytic activity and recyclability of the two NCs have been evaluated considering the degradation of Congo red (CR) and 4-nitrophenol (4-NP) using sodium borohydride as a model reaction. The results reveal that the symmetric Au NPs participated NCs display low activity in the degradation of the above organic dyes. However, a detailed kinetic study demonstrates that the employ of bimetallic Janus Au-Ni NPs in the NCs indicates enhanced catalytic activity, owing to the structurally specific nature. Furthermore, the magnetic functional NCs reported here can be used as recyclable catalyst which can be recovered simply by magnet.

Hydrides and Borohydrides of Light Elements

DTIC Science & Technology

1947-12-04

Troy, Attn: Inst. of Naval Science (30) Solar Aircraft Cu,, San Diego, Attn: Dr. M. A. Williamson " (31) INSMAT. N. J. for Itandard Oil Co., Esso Lab...with the other# iLD F.Re p. 8 ilt -ms" #61ggSotod that.. ir addition to thc impurity in the t~y..thr, an impurkty, prosumably aluminum hydride, in

Green Synthesis of Ag and Pd Nanospheres, Nanowires, and Nanorods Using Vitamin B2: Catalytic Polymerisation of Aniline and Pyrrole

EPA Science Inventory

For the first time, we report green chemistry approach using vitamin B2 in the synthesis of silver (Ag) and palladium (Pd), nanospheres, nanowires and nanorods at room temperature without using any harmful reducing agents, such as sodium borohydride (NaBH4) or hydroxylamine hydro...

Evaluation of the gamma radiation shielding parameters of bismuth modified quaternary glass system

NASA Astrophysics Data System (ADS)

Kaur, Parminder; Singh, K. J.; Thakur, Sonika

2018-05-01

Glasses modified with heavy metal oxides (HMO) are an interesting area of research in the field of gamma-ray shielding. Bismuth modified lithium-zinc-borate glasses have been studied whereby bismuth oxide is added from 0 to 50 mol%. The gamma ray shielding properties of the glasses were evaluated at photon energy 662 keV with the help of XMuDat computer program by using the Hubbell and Seltzer database. Various gamma ray shielding parameters such as attenuation coefficient, shield thickness in terms of half and tenth value layer, effective atomic number have been studied in this work. A useful comparison of this glass system has been made with standard radiation shielding concretes viz. ordinary, barite and iron concrete. The glass samples containing 20 to 50 mol% bismuth oxide have shown better gamma ray shielding properties and hence have the potential to become good radiation absorbers.

High-Quality TiS2 For Li/TiS2 Cells

NASA Technical Reports Server (NTRS)

Huang, Chen-Kuo; Surampudi, Subbarao; Shen, David H.; Delgiannis, Fotios; Halpert, Gerald

1992-01-01

Modified process for synthesis of battery-grade titanium sulfide (TiS2) yields substantially improved material for Li/TiS2 electrochemical cells. Includes all-vapor-phase reaction between sulfur and titanium. Product less dense and more homogeneous, consists of smaller particles of higher crystalline quality, and purer. Cells have high cathode utilization and long cycle life performance. Expected to find applications in rechargeable lithium batteries for spacecraft, military equipment, telecommunication systems, automobiles, and consumer products.

Liquid-like ionic conduction in solid lithium and sodium monocarba- closo-decaborates near or at room temperature

DOE PAGES

Tang, Wan Si; Matsuo, Motoaki; Wu, Hui; ...

2016-02-05

Both LiCB 9H 10 and NaCB 9H 10 exhibit liquid-like cationic conductivities (≥0.03 S cm –1) in their disordered hexagonal phases near or at room temperature. Furthermore, these unprecedented conductivities and favorable stabilities enabled by the large pseudoaromatic polyhedral anions render these materials in their pristine or further modified forms as promising solid electrolytes in next-generation, power devices.

Carbon felt interlayer derived from rice paper and its synergistic encapsulation of polysulfides for lithium-sulfur batteries

NASA Astrophysics Data System (ADS)

Yang, Kai; Zhong, Lei; Guan, Ruiteng; Xiao, Min; Han, Dongmei; Wang, Shuanjin; Meng, Yuezhong

2018-05-01

Lithium-sulfur (Li-S) batteries have remarkably high theoretical specific capacity as promising candidates for next-generation energy storage. However, the "polysulfides shuttle" effect hampers its commercial application. Here, we use a kind of rice paper as a raw material to get inorganic oxides doping carbon felt by the facile carbonization method, and then modified by a simple coating process using poly (fluorenyl ether ketone) and Super P slurry. The special structure of the carbon felt derived from rice paper and its modified layer endow the final electronic conductive interlayer with inherent polysulfides absorbents and ion Coulombic repulsion functions, respectively, which show synergistic effect for trapping polysulfides. As an interlayer of Li-S batteries, the obtained carbon felt/poly (fluorenyl ether ketone)& Super P (CFSS) interlayer shows excellent electrochemical performance in improving specific capacity and decreasing polarization. The batteries with CFSS interlayer exhibit a high capacity of 837 mA h g-1 at 2.0 C and a high initial capacity of 1073.4 mA h g-1 and good capacity retention of 824.5 mA h g-1 after 500 cycles at 0.5 C. CFSS interlayer also shows excellent anti-self-discharge performance. Therefore, the simple and economical CFSS interlayer can be considered as a promising component for high performance Li-S batteries.

Phase transition in lithium ammonium sulphate doped with cesium metal ions

NASA Astrophysics Data System (ADS)

Gaafar, M.; Kassem, M. E.; Kandil, S. H.

2000-07-01

Effects of doped cesium (C s+) metal ions (with different molar ratios n) on the phase transition of lithium ammonium sulphate LiNH 4SO 4 system have been studied by measuring the specific heat Cp( T) of the doped systems in the temperature range from 400 to 480 K. The study shows a peculiar phase transition of the pure system ( n=0) characterized by double distinct peaks, changed to a single sharp and narrow one as a result of the doping process. The measurements exhibit different effects of enhanced molar ratios of dopants on the phase transition behaviour of this system. At low dopant content ( n≤3%), the excess specific heat (Δ Cp) max at the transition temperature T1 decreases till a minimum value at n=0.8%, then it increases gradually. In this case, Δ Cp( T) behaviour is varied quantitatively and not modified. Enhanced dopant content ( n>3%) has a pronounced effect on the critical behaviour, which is significantly changed and considerably modified relative to the pure system. In addition, broadening of the critical temperature region, and decrease of (Δ Cp) max associated with changes of the Landau expansion coefficients are obtained and discussed. The study deals with the contribution of the thermally excited dipoles to the specific heat in the ferroelectric region and shows that their energy depends on doping.

Co3O4 nanocrystals with exposed low-surface-energy planes anchored on chemically integrated graphitic carbon nitride-modified nitrogen-doped graphene: A high-performance anode material for lithium-ion batteries

NASA Astrophysics Data System (ADS)

Zhang, Wenyao; Fu, Yongsheng; Wang, Xin

2018-05-01

A facile strategy to synthesize a composite composed of cubic Co3O4 nanocrystals anchored on chemically integrated g-C3N4-modified N-graphene (CN-NG) as an advanced anode material for high-performance lithium-ion batteries is reported. It is found that the morphology of the Co3O4 nanocrystals contains blunt-edge nanocubes with well-demarcated boundaries and numerous exposed low-index (1 1 1) crystallographic facets. These planes can be directly involved in the electrochemical reactions, providing rapid Li-ion transport channels for charging and discharging and thus enhancing the round-trip diffusion efficiency. On the other hand, the CN-NG support displays unusual textural features, such as superior structural stability, accessible active sites, and good electrical conductivity. The experimental results reveal that the chemical and electronic coupling of graphitic carbon nitride and nitrogen-doped graphene synergistically facilitate the anchoring of Co3O4 nanocrystals and prevents their migration. The resulting Co3O4/CN-NG composite exhibits a high specific reversible capacity of up to 1096 mAh g-1 with excellent cycling stability and rate capability. We believe that such a hybrid carbon support could open a new path for applications in electrocatalysis, sensors, supercapacitors, etc., in the near future.

Dual-protection of a graphene-sulfur composite by a compact graphene skin and an atomic layer deposited oxide coating for a lithium-sulfur battery.

PubMed

Yu, Mingpeng; Wang, Aiji; Tian, Fuyang; Song, Hongquan; Wang, Yinshu; Li, Chun; Hong, Jong-Dal; Shi, Gaoquan

2015-03-12

A reduced graphene oxide (rGO)-sulfur composite aerogel with a compact self-assembled rGO skin was further modified by an atomic layer deposition (ALD) of ZnO or MgO layer, and used as a free-standing electrode material of a lithium-sulfur (Li-S) battery. The rGO skin and ALD-oxide coating worked as natural and artificial barriers to constrain the polysulfides within the cathode region. As a result, the Li-S battery based on this electrode material exhibited superior cycling stability, good rate capability and high coulombic efficiency. Furthermore, ALD-ZnO coating was tested for performance improvement and found to be more effective than ALD-MgO coating. The ZnO modified G-S electrode with 55 wt% sulfur loading delivered a maximum discharge capacity of 998 mA h g(-1) at a current density of 0.2 C. A high capacity of 846 mA h g(-1) was achieved after charging/discharging for 100 cycles with a coulombic efficiency of over 92%. In the case of using LiNO3 as a shuttle inhibitor, this electrode showed an initial discharge capacity of 796 mA h g(-1) and a capacity retention of 81% after 250 cycles at a current density of 1 C with an average coulombic efficiency higher than 99.7%.

Developing New Electrolytes for Advanced Li-ion Batteries

NASA Astrophysics Data System (ADS)

McOwen, Dennis Wayne

The use of renewable energy sources is on the rise, as new energy generating technologies continue to become more efficient and economical. Furthermore, the advantages of an energy infrastructure which relies more on sustainable and renewable energy sources are becoming increasingly apparent. The most readily available of these renewable energy sources, wind and solar energy in particular, are naturally intermittent. Thus, to enable the continued expansion and widespread adoption of renewable energy generating technology, a cost-effective energy storage system is essential. Additionally, the market for electric/hybrid electric vehicles, which both require efficient energy storage, continues to grow as more consumers seek to reduce their consumption of gasoline. These vehicles, however, remain quite expensive, due primarily to costs associated with storing the electrical energy. High-voltage and thermally stable Li-ion battery technology is a promising solution for both grid-level and electric vehicle energy storage. Current limitations in materials, however, limit the energy density and safe operating temperature window of the battery. Specifically, the state-of-the-art electrolyte used in Li-ion batteries is not compatible with recently developed high-voltage positive electrodes, which are one of the most effectual ways of increasing the energy density. The electrolyte is also thermally unstable above 50 °C, and prone to thermal runaway reaction if exposed to prolonged heating. The lithium salt used in such electrolytes, LiPF6, is a primary contributor to both of these issues. Unfortunately, an improved lithium salt which meets the myriad property requirements for Li-ion battery electrolytes has eluded researchers for decades. In this study, a renewed effort to find such a lithium salt was begun, using a recently developed methodology to rapidly screen for desirable properties. Four new lithium salts and one relatively new but uncharacterized lithium salt were synthesized for this investigation: dilithium 1,2,5-thiadiazolidine-3,4-dione-1,1-dioxide (Li2TDD), lithium ethyl N-trifluoroacetylcarbamate (LiETAC), lithium hexafluoroisopropoxide (LiHFI), lithium pentafluorophenolate (LiPFPO), and lithium 2-trifluoromethyl-4,5-dicyanoimidazolide (LiTDI). Using crystalline solvate structure analysis and electrolyte solvation numbers, each of these lithium salts were compared to more well-characterized lithium salts, such as LiPF6 and LiBF4. From this study, links between anion structural characteristics and the anion...Li+ cation interactions (i.e., ionic association strength) were made. From the screening of the five lithium salts that were synthesized, LiTDI was determined to be a promising candidate for Li-ion battery electrolytes. Further characterization of carbonate- and mixed carbonate-LiTDI electrolytes (e.g., ionic conductivity) confirmed this to be the case. Coin cells containing LiTDI or LiPF6 electrolytes showed that cells with either electrolyte could deliver nearly identical power density at 25 °C. Additionally, thermogravimetric analysis (TGA) and NMR suggested that the LiTDI salt and carbonate-LiTDI electrolytes are thermally stable up to at least 60 °C. Further supporting this finding, coin cells cycled at 60 °C with LiPF6 lost significantly more capacity than those with LiTDI. Therefore, LiTDI is a prime candidate for the complete replacement of LiPF6 to significantly increase Li-ion battery tolerance to heat, improving the safety characteristics. In addition to searching for new lithium salts, the effect of lithium salt concentration on electrolyte physicochemical properties was investigated. This radically different approach to modifying electrolyte properties determined that amorphous, highly concentrated carbonate-lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) electrolytes have drastically different behavior than more dilute electrolytes. For example, the thermal stability and anodic stability vs. a Pt electrode of the concentrated electrolytes are significantly higher. Most striking, however, was the suppression of Al corrosion by the concentrated carbonate-LiTFSI electrolytes, despite the fact that Al corrosion of more dilute carbonate-LiTFSI electrolytes has consistently been attributed to the TFSI- anion in the literature. These results, explained by crystalline solvate analysis, Raman spectroscopy, and molecular dynamics simulations, could change the way Li-ion battery electrolytes are designed.

Aniline-modified porous graphitic carbon for hydrophilic interaction and attenuated reverse phase liquid chromatography.

PubMed

Iverson, Chad D; Lucy, Charles A

2014-12-19

Most stationary phases for hydrophilic interaction liquid chromatography (HILIC) and reversed phase liquid chromatography (RPLC) are based on silica. Porous graphitic carbon (PGC) is an attractive alternative to silica-based phases due to its chemical and thermal stability, and unique selectivity. However, native PGC is strongly hydrophobic and in some instances excessively retentive. PGC particles with covalently attached aniline groups (Dimethylaniline-PGC and Aniline-PGC) were synthesized to alter the surface polarity of PGC. First, the diazonium salt of N,N-dimethyl-p-phenylenediamine or 4-nitroaniline was adsorbed onto the PGC surface. The adsorbed salt was reduced with sodium borohydride and (Aniline-PGC only) the nitro group was further reduced with iron powder to the aniline. X-ray photoelectron spectroscopy confirmed the surface functionalities and that these moieties were introduced to the surface at concentrations of 0.9 and 2.1molecules/nm(2), respectively. These modified PGC phases (especially Aniline-PGC) were evaluated as HILIC and reversed phases. The Dimethylaniline-PGC phase displayed only weak HILIC retention of phenolic solutes. In contrast, the Aniline-PGC phase displayed up to nearly a 7-fold increase in HILIC retention vs. an aniline-silica phase and selectivity that differed from 10 other HILIC phases. Introduction of aniline groups to the PGC surface reduced the RPLC retentivity of PGC up to more than 5-fold and improved the separation efficiency up to 6-fold. The chromatographic performance of Aniline-PGC is demonstrated by separations of nucleotides, nucleosides, carboxylic acids, basic pharmaceuticals, and other compounds. Copyright © 2014 Elsevier B.V. All rights reserved.

Forty-photon-per-pulse spectral phase retrieval by shaper-assisted modified interferometric field autocorrelation.

PubMed

Hsu, Chen-Shao; Chiang, Hsin-Chien; Chuang, Hsiu-Po; Huang, Chen-Bin; Yang, Shang-Da

2011-07-15

We retrieve the spectral phase of 400 fs pulses at 1560 nm with 5.2 aJ coupled pulse energy (40 photons) by the modified interferometric field autocorrelation method, using a pulse shaper and a 5 cm long periodically poled lithium niobate waveguide. The carrier-envelope phase control of the shaper can reduce the fringe density of the interferometric trace and permits longer lock-in time constants, achieving a sensitivity of 2.7×10(-9) mW(2) (40 times better than the previous record for self-referenced nonlinear pulse measurement). The high stability of the pulse shaper allows for accurate and reproducible measurements of complicated spectral phases. © 2011 Optical Society of America

Probing the Reactivity of Cyclic "N,O"-Acetals versus Cyclic "O,O"-Acetals with NaBH[subscript 4] and CH[subscript 3]MgI

ERIC Educational Resources Information Center

Ciaccio, James A.; Saba, Shahrokh; Bruno, Samantha M.; Bruppacher, John H.; McKnight, Alexa G.

2018-01-01

An operationally straightforward, project-like laboratory experiment has been developed in which students directly compare the reactivity of two heterocycles, a cyclic "O,O"-acetal (standard C-O protecting group) and a cyclic "N,O"-acetal (oxazolidine), toward sodium borohydride and methylmagnesium iodide. Students synthesize a…

Chemical bonding analysis on amphoteric hydrogen - alkaline earth ammine borohydrides

NASA Astrophysics Data System (ADS)

Kiruthika, S.; Ravindran, P.

2018-04-01

Usually the ions in solid are in the positive oxidation states or in the negative oxidation state depending upon the chemical environment. It is highly unusual for an ion having both positive as well as negative oxidation state in a particular compound. Structural analysis suggest that the alkaline earth ammine borohydrides (AABH) with the chemical formula M (BH4)2(NH3)2 (M = Mg, Ca, or Sr) where hydrogen is present in +1 and -1 oxidation states. In order to understand the oxidation states of hydrogen and also the character of chemical bond present in AABH we have made charge density, electron localization function, Born effective charge, Bader effective charge, and density of states analyses using result from the density functional calculations. Our detailed analyses show that hydrogen is in amphoteric behavior with hydrogen closer to boron is in negative oxidation state and that closer to nitrogen is in the positive oxidation state. Due to the presence of finite covalent bonding between the consitutents in AABH the oxidation state of hydrogen is non-interger value. The confirmation of the presence of amphtoric behavior of hydrogen in AABH has implication in hydrogen storage applications.

Flow injection method for the determination of silver concentration in drinking water for spacecrafts.

PubMed

Bruzzoniti, Maria Concetta; Kobylinska, Dorota Korte; Franko, Mladen; Sarzanini, Corrado

2010-04-14

A flow injection method has been developed for determination of silver. The method is based on a reduction reaction with sodium borohydride which leads to the formation of a colloidal species which is monitored at a wavelength of 390 nm. The reaction variables flow rate, sodium borohydride concentration and pH, which affect sensitivity, were investigated and their effects were established using a two-levels, three-factor experimental design. Further optimization of manifold variables (reaction coil and injection volume) allowed us to determine silver in the range 0.050-5.0 mg L(-1) with a minimum detectable concentration of 0.050 mg L(-1). Silver is added, as biocide, to drinking water for spacecrafts. The chemical species of silver, present in this kind of sample, were characterized by a procedure based on the selective retention of Ag(+) onto a 2.2.2. cryptand based substrate followed by determination of the non-bound and bound (after elution) Ag(+) by the FIA method. The method optimized was applied to a drinking water sample provided for the launch with the Automated Transfer Vehicle (ATV) module Jule Verne to the International Space Station (March 9, 2008). Copyright 2010 Elsevier B.V. All rights reserved.

Optical properties of humic substances and CDOM: effects of borohydride reduction.

PubMed

Ma, Jiahai; Del Vecchio, Rossana; Golanoski, Kelli S; Boyle, Erin S; Blough, Neil V

2010-07-15

Treatment of Suwanee River humic (SRHA) and fulvic (SRFA) acids, a commercial lignin (LAC), and a series of solid phase extracts (C18) from the Middle Atlantic Bight (MAB extracts) with sodium borohydride (NaBH(4)), a selective reductant of carbonyl-containing compounds including quinones and aromatic ketones, produces a preferential loss of visible absorption (> or = 50% for SRFA) and substantially enhanced, blue-shifted fluorescence emission (2- to 3-fold increase). Comparison of the results with those obtained from a series of model quinones and hydroquinones demonstrates that these spectral changes cannot be assigned directly to the absorption and emission of visible light by quinones/hydroquinones. Instead, these results are consistent with a charge transfer model in which the visible absorption is due primarily to charge transfer transitions arising among hydroxy- (methoxy-) aromatic donors and carbonyl-containing acceptors. Unlike most of the model hydroquinones, the changes in optical properties of the natural samples following NaBH(4) reduction were largely irreversible in the presence of air and following addition of a Cu(2+) catalyst, providing tentative evidence that aromatic ketones (or other similar carbonyl-containing structures) may play a more important role than quinones in the optical properties of these materials.

Does 8-methacryloxyoctyl trimethoxy silane (8-MOTS) improve initial bond strength on lithium disilicate glass ceramic?

PubMed

Maruo, Yukinori; Nishigawa, Goro; Yoshihara, Kumiko; Minagi, Shogo; Matsumoto, Takuya; Irie, Masao

2017-03-01

Dental ceramic surfaces are modified with silane coupling agents, such as γ-methacryloxypropyl trimethoxy silane (γ-MPTS), to improve bond strength. For bonding between lithium disilicate glass ceramic and resin cement, the objective was to investigate if 8-methacryloxyoctyl trimethoxy silane (8-MOTS) could yield a similar performance as the widely used γ-MPTS. One hundred and ten lithium disilicate glass ceramic specimens were randomly divided into 11 groups (n=10) according to pretreatment regime. All specimens were pretreated with a different solution composed of one or a combination of these agents: 10 or 20wt% silane coupling agent of γ-MPTS or 8-MOTS, followed by a hydrolysis solution of acetic acid or 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP). Each pretreated surface was luted to a stainless steel rod of 3.6mm diameter and 2.0mm height with resin cement. Shear bond strength between ceramic and cement was measured after 24-h storage in 37°C distilled water. 8-MOTS produced the same bonding performance as γ-MPTS. Both silane coupling agents significantly increased the bond strength of resin cement, depending on their concentration. When activated by 10-MDP hydrolysis solution, 20wt% concentration produced the highest values (γ-MPTS: 24.9±5.1MPa; 8-MOTS: 24.6±7.4MPa). Hydrolysis with acetic acid produced lower bond strengths than with 10-MDP. Silane coupling pretreatment with 8-MOTS increased the initial bond strength between lithium disilicate glass ceramic and resin cement, rendering the same bonding effect as the conventional γ-MPTS. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Carbon and oxygen X-ray line emission from the interstellar medium

NASA Technical Reports Server (NTRS)

Schnopper, H. W.; Delvaille, J. P.; Rocchia, R.; Blondel, C.; Cheron, C.; Christy, J. C.; Ducros, R.; Koch, L.; Rothenflug, R.

1982-01-01

A soft X-ray, 0.3-1.0 keV spectrum from a 1 sr region which includes a portion of the North Polar Spur, obtained by three rocketborne lithium-drifted silicon detectors, shows the C V, C VI, O VII and O VIII emission lines. The spectrum is well fitted by a two-component, modified Kato (1976) model, where the coronal emission is in collisional equilibrium, with interstellar medium and North Polar Spur temperatures of 1.1 and 3.8 million K, respectively.

Thickness, humidity, and polarization dependent ferroelectric switching and conductivity in Mg doped lithium niobate

DOE Office of Scientific and Technical Information (OSTI.GOV)

Neumayer, Sabine M.; Rodriguez, Brian J., E-mail: brian.rodriguez@ucd.ie; Conway Institute of Biomolecular and Biomedical Research, University College Dublin, Belfield, Dublin 4

2015-12-28

Mg doped lithium niobate (Mg:LN) exhibits several advantages over undoped LN such as resistance to photorefraction, lower coercive fields, and p-type conductivity that is particularly pronounced at domain walls and opens up a range of applications, e.g., in domain wall electronics. Engineering of precise domain patterns necessitates well founded knowledge of switching kinetics, which can differ significantly from that of undoped LN. In this work, the role of humidity and sample composition in polarization reversal has been investigated under application of the same voltage waveform. Control over domain sizes has been achieved by varying the sample thickness and initial polarizationmore » as well as atmospheric conditions. In addition, local introduction of proton exchanged phases allows for inhibition of domain nucleation or destabilization, which can be utilized to modify domain patterns. Polarization dependent current flow, attributed to charged domain walls and band bending, demonstrates the rectifying ability of Mg:LN in combination with suitable metal electrodes that allow for further tailoring of conductivity.« less

Supercritical Carbon Dioxide-Assisted Process for Well-Dispersed Silicon/Graphene Composite as a Li ion Battery Anode.

PubMed

Lee, Sang Ha; Park, Sengyoen; Kim, Min; Yoon, Dohyeon; Chanthad, Chalathorn; Cho, Misuk; Kim, Jaehoon; Park, Jong Hyeok; Lee, Youngkwan

2016-08-18

The silicon (Si)/graphene composite has been touted as one of the most promising anode materials for lithium ion batteries. However, the optimal fabrication method for this composite remains a challenge. Here, we developed a novel method using supercritical carbon dioxide (scCO2) to intercalate Si nanoparticles into graphene nanosheets. Silicon was modified with a thin layer of polyaniline, which assisted the dispersion of graphene sheets by introducing π-π interaction. Using scCO2, well-dispersed Si/graphene composite was successfully obtained in a short time under mild temperature. The composite showed high cycle performance (1,789 mAh/g after 250 cycles) and rate capability (1,690 mAh/g at a current density of 4,000 mA/g). This study provides a new approach for cost-effective and scalable preparation of a Si/graphene composite using scCO2 for a highly stable lithium battery anode material.

Supercritical Carbon Dioxide-Assisted Process for Well-Dispersed Silicon/Graphene Composite as a Li ion Battery Anode

PubMed Central

Lee, Sang Ha; Park, Sengyoen; Kim, Min; Yoon, Dohyeon; Chanthad, Chalathorn; Cho, Misuk; Kim, Jaehoon; Park, Jong Hyeok; Lee, Youngkwan

2016-01-01

The silicon (Si)/graphene composite has been touted as one of the most promising anode materials for lithium ion batteries. However, the optimal fabrication method for this composite remains a challenge. Here, we developed a novel method using supercritical carbon dioxide (scCO2) to intercalate Si nanoparticles into graphene nanosheets. Silicon was modified with a thin layer of polyaniline, which assisted the dispersion of graphene sheets by introducing π-π interaction. Using scCO2, well-dispersed Si/graphene composite was successfully obtained in a short time under mild temperature. The composite showed high cycle performance (1,789 mAh/g after 250 cycles) and rate capability (1,690 mAh/g at a current density of 4,000 mA/g). This study provides a new approach for cost-effective and scalable preparation of a Si/graphene composite using scCO2 for a highly stable lithium battery anode material. PMID:27535108

Sub-2 nm Thick Fluoroalkylsilane Self-Assembled Monolayer-Coated High Voltage Spinel Crystals as Promising Cathode Materials for Lithium Ion Batteries

PubMed Central

Zettsu, Nobuyuki; Kida, Satoru; Uchida, Shuhei; Teshima, Katsuya

2016-01-01

We demonstrate herein that an ultra-thin fluoroalkylsilane self-assembled monolayer coating can be used as a modifying agent at LiNi0.5Mn1.5O4−δcathode/electrolyte interfaces in 5V-class lithium-ion batteries. Bare LiNi0.5Mn1.5O4−δ cathode showed substantial capacity fading, with capacity dropping to 79% of the original capacity after 100 cycles at a rate of 1C, which was entirely due to dissolution of Mn3+ from the spinel lattice via oxidative decomposition of the organic electrolyte. Capacity retention was improved to 97% on coating ultra-thin FAS17-SAM onto the LiNi0.5Mn1.5O4 cathode surface. Such surface protection with highly ordered fluoroalkyl chains insulated the cathode from direct contact with the organic electrolyte and led to increased tolerance to HF. PMID:27553901

Shape Modification and Size Classification of Microcrystalline Graphite Powder as Anode Material for Lithium-Ion Batteries

NASA Astrophysics Data System (ADS)

Wang, Cong; Gai, Guosheng; Yang, Yufen

2018-03-01

Natural microcrystalline graphite (MCG) composed of many crystallites is a promising new anode material for lithium-ion batteries (LiBs) and has received considerable attention from researchers. MCG with narrow particle size distribution and high sphericity exhibits excellent electrochemical performance. A nonaddition process to prepare natural MCG as a high-performance LiB anode material is described. First, raw MCG was broken into smaller particles using a pulverization system. Then, the particles were modified into near-spherical shape using a particle shape modification system. Finally, the particle size distribution was narrowed using a centrifugal rotor classification system. The products with uniform hemispherical shape and narrow size distribution had mean particle size of approximately 9 μm, 10 μm, 15 μm, and 20 μm. Additionally, the innovative pilot experimental process increased the product yield of the raw material. Finally, the electrochemical performance of the prepared MCG was tested, revealing high reversible capacity and good cyclability.

Mechanisms Underlying Ionic Mobilities in Nanocomposite Polymer Electrolytes

NASA Astrophysics Data System (ADS)

Ganesan, Venkat; Hanson, Benjamin; Pryamitsyn, Victor

2014-03-01

Recently, a number of experiments have demonstrated that addition of ceramics with nanoscale dimensions can lead to substantial improvements in the low temperature conductivity of the polymeric materials. However, the origin of such behaviors, and more generally, the manner by which nanoscale fillers impact the ion mobilities remain unresolved. In this communication, we report the results of atomistic molecular dynamics simulations which used multibody polarizable force-fields to study lithium ion diffusivities in an amorphous poly(ethylene-oxide) (PEO) melt containing well-dispersed TiO2 nanoparticles. We observed that the lithium ion diffusivities decrease with increased particle loading. Our analysis suggests that the ion mobilities are correlated to the nanoparticle-induced changes in the polymer segmental dynamics. Interestingly, the changes in polymer segmental dynamics were seen to be related to the nanoparticle's influence on the polymer conformational features. Overall, our results indicate that addition of nanoparticle fillers modify polymer conformations and the polymer segmental dynamics, and thereby influence the ion mobilities of polymer electrolytes.

A chemically activated graphene-encapsulated LiFePO4 composite for high-performance lithium ion batteries.

PubMed

Ha, Jeonghyun; Park, Seung-Keun; Yu, Seung-Ho; Jin, Aihua; Jang, Byungchul; Bong, Sungyool; Kim, In; Sung, Yung-Eun; Piao, Yuanzhe

2013-09-21

A composite of modified graphene and LiFePO4 has been developed to improve the speed of charging-discharging and the cycling stability of lithium ion batteries using LiFePO4 as a cathode material. Chemically activated graphene (CA-graphene) has been successfully synthesized via activation by KOH. The as-prepared CA-graphene was mixed with LiFePO4 to prepare the composite. Microscopic observation and nitrogen sorption analysis have revealed the surface morphologies of CA-graphene and the CA-graphene/LiFePO4 composite. Electrochemical properties have also been investigated after assembling coin cells with the CA-graphene/LiFePO4 composite as a cathode active material. Interestingly, the CA-graphene/LiFePO4 composite has exhibited better electrochemical properties than the conventional graphene/LiFePO4 composite as well as bare LiFePO4, including exceptional speed of charging-discharging and excellent cycle stability. That is because the CA-graphene in the composite provides abundant porous channels for the diffusion of lithium ions. Moreover, it acts as a conducting network for easy charge transfer and as a divider, preventing the aggregation of LiFePO4 particles. Owing to these properties of CA-graphene, LiFePO4 could demonstrate enhanced and stably long-lasting electrochemical performance.

Mesoscopic modeling and parameter estimation of a lithium-ion battery based on LiFePO4/graphite

NASA Astrophysics Data System (ADS)

Jokar, Ali; Désilets, Martin; Lacroix, Marcel; Zaghib, Karim

2018-03-01

A novel numerical model for simulating the behavior of lithium-ion batteries based on LiFePO4(LFP)/graphite is presented. The model is based on the modified Single Particle Model (SPM) coupled to a mesoscopic approach for the LFP electrode. The model comprises one representative spherical particle as the graphite electrode, and N LFP units as the positive electrode. All the SPM equations are retained to model the negative electrode performance. The mesoscopic model rests on non-equilibrium thermodynamic conditions and uses a non-monotonic open circuit potential for each unit. A parameter estimation study is also carried out to identify all the parameters needed for the model. The unknown parameters are the solid diffusion coefficient of the negative electrode (Ds,n), reaction-rate constant of the negative electrode (Kn), negative and positive electrode porosity (εn&εn), initial State-Of-Charge of the negative electrode (SOCn,0), initial partial composition of the LFP units (yk,0), minimum and maximum resistance of the LFP units (Rmin&Rmax), and solution resistance (Rcell). The results show that the mesoscopic model can simulate successfully the electrochemical behavior of lithium-ion batteries at low and high charge/discharge rates. The model also describes adequately the lithiation/delithiation of the LFP particles, however, it is computationally expensive compared to macro-based models.

Hydrogen, lithium, and lithium hydride production

DOEpatents

Brown, Sam W.; Spencer, Larry S.; Phillips, Michael R.; Powell, G. Louis; Campbell, Peggy J.

2017-06-20

A method is provided for extracting hydrogen from lithium hydride. The method includes (a) heating lithium hydride to form liquid-phase lithium hydride; (b) extracting hydrogen from the liquid-phase lithium hydride, leaving residual liquid-phase lithium metal; (c) hydriding the residual liquid-phase lithium metal to form refined lithium hydride; and repeating steps (a) and (b) on the refined lithium hydride.

Hydrogen, lithium, and lithium hydride production

DOEpatents

Brown, Sam W; Spencer, Larry S; Phillips, Michael R; Powell, G. Louis; Campbell, Peggy J

2014-03-25

A method of producing high purity lithium metal is provided, where gaseous-phase lithium metal is extracted from lithium hydride and condensed to form solid high purity lithium metal. The high purity lithium metal may be hydrided to provide high purity lithium hydride.

Cross-Course Collaboration in the Undergraduate Chemistry Curriculum: Isotopic Labeling with Sodium Borodeuteride in the Introductory Organic Chemistry Laboratory

ERIC Educational Resources Information Center

Kjonaas, Richard A.; Fitch, Richard W.; Noll, Robert J.

2017-01-01

A microscale isotopic labeling experiment is described for the introductory organic chemistry laboratory course wherein half of the students use sodium borohydride (NaBH[subscript 4]) and the other half use sodium borodeuteride (NaBD[subscript 4]) to reduce acetophenone to 1-phenylethanol and then compare spectral data. The cost is reasonable, and…

Piperidine Synthesis.

DTIC Science & Technology

1992-09-01

ORGANIZATION NAME(S) AND ADORESS(ES) B . PERFORMING ORGANIZATION CDR, CRDEC, ATTN: SMCCR-RSC-O, APG, MD REPORT NUMBER 21010-5423 CRDEC-TR-409 9. SPONSORING...hydroxypyridine with iodomethane or benzyl chloride followed by sodium borohydride reduction and HBr cleavage of the enol ether is yet another effective...Piperidine, Elsevier, New York, 1991. ( b ) Armardgo, W.L.F., "Stereochemistry of Heterocyclic Compounds, Part 1," John Wiley & Sons, New York, 1977. (c

The removal of uranium onto carbon-supported nanoscale zero-valent iron particles

NASA Astrophysics Data System (ADS)

Crane, Richard A.; Scott, Thomas

2014-12-01

In the current work carbon-supported nanoscale zero-valent iron particles (CS nZVI), synthesised by the vacuum heat treatment of ferric citrate trihydrate absorbed onto carbon black, have been tested for the removal of uranium (U) from natural and synthetic waters. Two types of CS nZVI were tested, one vacuum annealed at 600 °C for 4 h and the other vacuum annealed at 700 °C for 4 h, with their U removal behaviour compared to nZVI synthesised via the reduction of ferrous iron using sodium borohydride. The batch systems were analysed over a 28-day reaction period during which the liquid and nanoparticulate solids were periodically analysed to determine chemical evolution of the solutions and particulates. Results demonstrate a well-defined difference between the two types of CS nZVI, with greater U removal exhibited by the nanomaterial synthesised at 700 °C. The mechanism has been attributed to the CS nZVI synthesised at 700 °C exhibiting (i) a greater proportion of surface oxide Fe2+ to Fe3+ (0.34 compared to 0.28); (ii) a greater conversion of ferric citrate trihydrate [2Fe(C6H5O7)·H2O] to Fe0; and (iii) a larger surface area (108.67 compared to 88.61 m2 g-1). Lower maximum U uptake was recorded for both types of CS nZVI in comparison with the borohydride-reduced nZVI. A lower decrease in solution Eh and DO was also recorded, indicating that less chemical reduction of U was achieved by the CS nZVI. Despite this, lower U desorption in the latter stages of the experiment (>7 days) was recorded for the CS nZVI synthesised at 700 °C, indicating that carbon black in the CS nZVI is likely to have contributed towards U sorption and retention. Overall, it can be stated that the borohydride-reduced nZVI were significantly more effective than CS nZVI for U removal over relatively short timescales (e.g. <48 h), however, they were more susceptible to U desorption over extended time periods.

Trends in Syntheses, Structures, and Properties for Three Series of Ammine Rare-Earth Metal Borohydrides, M(BH4)3·nNH3 (M = Y, Gd, and Dy).

PubMed

Jepsen, Lars H; Ley, Morten B; Černý, Radovan; Lee, Young-Su; Cho, Young Whan; Ravnsbæk, Dorthe; Besenbacher, Flemming; Skibsted, Jørgen; Jensen, Torben R

2015-08-03

Fourteen solvent- and halide-free ammine rare-earth metal borohydrides M(BH4)3·nNH3, M = Y, Gd, Dy, n = 7, 6, 5, 4, 2, and 1, have been synthesized by a new approach, and their structures as well as chemical and physical properties are characterized. Extensive series of coordination complexes with systematic variation in the number of ligands are presented, as prepared by combined mechanochemistry, solvent-based methods, solid-gas reactions, and thermal treatment. This new synthesis approach may have a significant impact within inorganic coordination chemistry. Halide-free metal borohydrides have been synthesized by solvent-based metathesis reactions of LiBH4 and MCl3 (3:1), followed by reactions of M(BH4)3 with an excess of NH3 gas, yielding M(BH4)3·7NH3 (M = Y, Gd, and Dy). Crystal structure models for M(BH4)3·nNH3 are derived from a combination of powder X-ray diffraction (PXD), (11)B magic-angle spinning NMR, and density functional theory (DFT) calculations. The structures vary from two-dimensional layers (n = 1), one-dimensional chains (n = 2), molecular compounds (n = 4 and 5), to contain complex ions (n = 6 and 7). NH3 coordinates to the metal in all compounds, while BH4(-) has a flexible coordination, i.e., either as a terminal or bridging ligand or as a counterion. M(BH4)3·7NH3 releases ammonia stepwise by thermal treatment producing M(BH4)3·nNH3 (6, 5, and 4), whereas hydrogen is released for n ≤ 4. Detailed analysis of the dihydrogen bonds reveals new insight about the hydrogen elimination mechanism, which contradicts current hypotheses. Overall, the present work provides new general knowledge toward rational materials design and preparation along with limitations of PXD and DFT for analysis of structures with a significant degree of dynamics in the structures.

Materials Compositions for Lithium Ion Batteries with Extended Thermal Stability

NASA Astrophysics Data System (ADS)

Kalaga, Kaushik

Advancements in portable electronics have generated a pronounced demand for rechargeable energy storage devices with superior capacity and reliability. Lithium ion batteries (LIBs) have evolved as the primary choice of portable power for several such applications. While multiple variations have been developed, safety concerns of commercial technologies limit them to atmospheric temperature operability. With several niche markets such as aerospace, defense and oil & gas demanding energy storage at elevated temperatures, there is a renewed interest in developing rechargeable batteries that could survive temperatures beyond 100°C. Instability of critical battery components towards extreme thermal and electrochemical conditions limit their usability at high temperatures. This study deals with developing material configurations for LIB components to stabilize them at such temperatures. Flammable organic solvent based electrolytes and low melting polymer based separators have been identified as the primary bottleneck for LIBs to survive increasing temperature. Furthermore, thermally activated degradation processes in oxide based electrodes have been identified as the reason for their limited lifetime. A quasi-solid composite comprising of room temperature ionic liquids (RTILs) and Clay was developed as an electrolyte/separator hybrid and tested to be stable up to 120°C. These composites facilitate complete reversible Li intercalation in lithium titanate (LTO) with a stable capacity of 120 mAh g-1 for several cycles of charge and discharge while simultaneously resisting severe thermal conditions. Modified phosphate based electrodes were introduced as a reliable alternative for operability at high temperatures in this study. These systems were shown to deliver stable reversible capacity for numerous charge/discharge cycles at elevated temperatures. Higher lithium intercalation potential of the developed cathode materials makes them interesting candidates for high voltage lithium batteries, which may be dubbed as the next generation devices. Architectural engineering of battery components to amplify the device performance is also discussed. 3D electrode structures developed using CVD and electrodeposition techniques demonstrated significant enhancement in performance when compared to their 2D analogues. The study has established the prospects of LIBs at high temperatures through material tuning and engineering approaches and envisage a scope for viable devices.

77 FR 21714 - Hazardous Materials: Transportation of Lithium Batteries

Federal Register 2010, 2011, 2012, 2013, 2014

2012-04-11

... and configurations of lithium batteries: 1. Lithium ion batteries (PI 965). 2. Lithium ion batteries packed with equipment (PI 966). 3. Lithium ion batteries contained in equipment (PI 967). 4. Lithium... requirements including package weight limits (10 kg for lithium ion cells and batteries and 2.5 kg for lithium...

A facile route to modify ferrous phosphate and its use as an iron-containing resource for LiFePO4 via a polyol process.

PubMed

Li, Shaomin; Liu, Xichuan; Mi, Rui; Liu, Hao; Li, Yinchuan; Lau, Woon-min; Mei, Jun

2014-06-25

This study introduces an economical and environmentally friendly way of synthesizing LiFePO4/C to be used as cathode material in lithium ion batteries via two processes: (1) the synthesis of LiFePO4/C cathode material using a low cost divalent precursor ferrous phosphate, Fe3 (PO4)2·8H2O, as iron source in a polyol process and (2) the modification of the morphology of this precursor by varying the reaction time in a coprecipitation process. The study examines the effects of different structures and morphologies of the precursor on the structure and electrochemical performance of the as-synthesized LiFePO4/C. The LiFePO4/C shows an excellent rate capability and cycle performance, with initial discharge capacities of 153, 128, and 106 mA h g(-1) at 1 C, 5 C, and 10 C. The capacity retention is respectively 98.7%, 98.2%, and 98.7%, after 10 cycles at the corresponding rates. The capacity retention remains at 97% even after 300 cycles at the rate of 10 C. The outstanding electrochemical performance can be attributed to the improved rate of Li(+) diffusion and the excellent crystallinity of synthesized LiFePO4/C powders through the modified precursor. Therefore, this is an economical and environmentally friendly way of synthesizing LiFePO4/C to be used as cathode material in lithium ion batteries.

Insights in the electronic structure and redox reaction energy in LiFePO{sub 4} battery material from an accurate Tran-Blaha modified Becke Johnson potential

DOE Office of Scientific and Technical Information (OSTI.GOV)

Araujo, Rafael B., E-mail: rafael.barros@physics.uu.se; Almeida, J. de S; Instituto de Física, Universidade Federal da Bahia, Salvador, Bahia

The main goals of this paper are to investigate the accuracy of the Tran-Blaha modified Becke Johnson (TB-mBJ) potential to predict the electronic structure of lithium iron phosphate and the related redox reaction energy with the lithium deintercalation process. The computed electronic structures show that the TB-mBJ method is able to partially localize Fe-3d electrons in LiFePO{sub 4} and FePO{sub 4} which usually is a problem for the generalized gradient approximation (GGA) due to the self interaction error. The energy band gap is also improved by the TB-mBJ calculations in comparison with the GGA results. It turned out, however, thatmore » the redox reaction energy evaluated by the TB-mBJ technique is not in good agreement with the measured one. It is speculated that this disagreement in the computed redox energy and the experimental value is due to the lack of a formal expression to evaluate the exchange and correlation energy. Therefore, the TB-mBJ is an efficient method to improve the prediction of the electronic structures coming form the standard GGA functional in LiFePO{sub 4} and FePO{sub 4}. However, it does not appear to have the same efficiency for evaluating the redox reaction energies for the investigated system.« less

Vaccum Gas Tungsten Arc Welding, phase 1

NASA Astrophysics Data System (ADS)

Weeks, J. L.; Krotz, P. D.; Todd, D. T.; Liaw, Y. K.

1995-03-01

This two year program will investigate Vacuum Gas Tungsten Arc Welding (VGTAW) as a method to modify or improve the weldability of normally difficult-to-weld materials. VGTAW appears to offer a significant improvement in weldability because of the clean environment and lower heat input needed. The overall objective of the program is to develop the VGTAW technology and implement it into a manufacturing environment that will result in lower cost, better quality and higher reliability aerospace components for the space shuttle and other NASA space systems. Phase 1 of this program was aimed at demonstrating the process's ability to weld normally difficult-to-weld materials. Phase 2 will focus on further evaluation, a hardware demonstration and a plan to implement VGTAW technology into a manufacturing environment. During Phase 1, the following tasks were performed: (1) Task 11000 Facility Modification - an existing vacuum chamber was modified and adapted to a GTAW power supply; (2) Task 12000 Materials Selection - four difficult-to-weld materials typically used in the construction of aerospace hardware were chosen for study; (3) Task 13000 VGTAW Experiments - welding experiments were conducted under vacuum using the hollow tungsten electrode and evaluation. As a result of this effort, two materials, NARloy Z and Incoloy 903, were downselected for further characterization in Phase 2; and (4) Task 13100 Aluminum-Lithium Weld Studies - this task was added to the original work statement to investigate the effects of vacuum welding and weld pool vibration on aluminum-lithium alloys.

Vaccum Gas Tungsten Arc Welding, phase 1

NASA Technical Reports Server (NTRS)

Weeks, J. L.; Krotz, P. D.; Todd, D. T.; Liaw, Y. K.

1995-01-01

This two year program will investigate Vacuum Gas Tungsten Arc Welding (VGTAW) as a method to modify or improve the weldability of normally difficult-to-weld materials. VGTAW appears to offer a significant improvement in weldability because of the clean environment and lower heat input needed. The overall objective of the program is to develop the VGTAW technology and implement it into a manufacturing environment that will result in lower cost, better quality and higher reliability aerospace components for the space shuttle and other NASA space systems. Phase 1 of this program was aimed at demonstrating the process's ability to weld normally difficult-to-weld materials. Phase 2 will focus on further evaluation, a hardware demonstration and a plan to implement VGTAW technology into a manufacturing environment. During Phase 1, the following tasks were performed: (1) Task 11000 Facility Modification - an existing vacuum chamber was modified and adapted to a GTAW power supply; (2) Task 12000 Materials Selection - four difficult-to-weld materials typically used in the construction of aerospace hardware were chosen for study; (3) Task 13000 VGTAW Experiments - welding experiments were conducted under vacuum using the hollow tungsten electrode and evaluation. As a result of this effort, two materials, NARloy Z and Incoloy 903, were downselected for further characterization in Phase 2; and (4) Task 13100 Aluminum-Lithium Weld Studies - this task was added to the original work statement to investigate the effects of vacuum welding and weld pool vibration on aluminum-lithium alloys.

Protective lithium ion conducting ceramic coating for lithium metal anodes and associate method

DOEpatents

Bates, John B.

1994-01-01

A battery structure including a cathode, a lithium metal anode and an electrolyte disposed between the lithium anode and the cathode utilizes a thin-film layer of lithium phosphorus oxynitride overlying so as to coat the lithium anode and thereby separate the lithium anode from the electrolyte. If desired, a preliminary layer of lithium nitride may be coated upon the lithium anode before the lithium phosphorous oxynitride is, in turn, coated upon the lithium anode so that the separation of the anode and the electrolyte is further enhanced. By coating the lithium anode with this material lay-up, the life of the battery is lengthened and the performance of the battery is enhanced.

Application of ionic liquids in electrochemical sensing systems.

PubMed

Shiddiky, Muhammad J A; Torriero, Angel A J

2011-01-15

Since 1992, when the room temperature ionic liquids (ILs) based on the 1-alkyl-3-methylimidazolium cation were reported to provide an attractive combination of an electrochemical solvent and electrolyte, ILs have been widely used in electrodeposition, electrosynthesis, electrocatalysis, electrochemical capacitor, and lithium batteries. However, it has only been in the last few years that electrochemical biosensors based on carbon ionic liquid electrodes (CILEs) and IL-modified macrodisk electrodes have been reported. However, there are still a lot of challenges in achieving IL-based sensitive, selective, and reproducible biosensors for high speed analysis of biological and environmental compounds of interest. This review discusses the principles of operation of electrochemical biosensors based on CILEs and IL/composite-modified macrodisk electrodes. Subsequently, recent developments and major strategies for enhancing sensing performance are discussed. Key challenges and opportunities of IL-based biosensors to further development and use are considered. Emphasis is given to direct electron-transfer reaction and electrocatalysis of hemeproteins and enzyme-modified composite electrodes. Copyright © 2010 Elsevier B.V. All rights reserved.

Electrochemical performance of La2O3/Li2O/TiO2 nano-particle coated cathode material LiFePO4.

PubMed

Wang, Hong; Yang, Chi; Liu, Shu-Xin

2014-09-01

Cathode material, LiFePO4 was modified by coating with a thin layer of La2O3/Li2O/TiO2 nano-particles for improving its performance for lithium ion batteries. The morphology and structure of the modified cathode material were characterized by powder X-ray diffraction, scanning electron microcopy and AES. The performance of the battery with the modified cathode material, including cycling stability, C-rate discharge was examined. The results show that the battery composed of the coated cathode materials can discharge at a large current density and show stable cycling performance in the range from 2.5 to 4.0 V. The rate of Li ion diffusion increases in the battery with the La2O3/Li2O/TiO2-coated LiFePO4 as a cathode and the coating layer may acts as a faster ion conductor (La(2/3-x)Li(3x)TiO3).

Disease-modifying and symptomatic treatment of amyotrophic lateral sclerosis

PubMed Central

Dorst, Johannes; Ludolph, Albert C.; Huebers, Annemarie

2017-01-01

In this review, we summarize the most important recent developments in the treatment of amyotrophic lateral sclerosis (ALS). In terms of disease-modifying treatment options, several drugs such as dexpramipexole, pioglitazone, lithium, and many others have been tested in large multicenter trials, albeit with disappointing results. Therefore, riluzole remains the only directly disease-modifying drug. In addition, we discuss antisense oligonucleotides (ASOs) as a new and potentially causal treatment option. Progress in symptomatic treatments has been more important. Nutrition and ventilation are now an important focus of ALS therapy. Several studies have firmly established that noninvasive ventilation improves patients’ quality of life and prolongs survival. On the other hand, there is still no consensus regarding best nutritional management, but big multicenter trials addressing this issue are currently ongoing. Evidence regarding secondary symptoms like spasticity, muscle cramps or sialorrhea remains generally scarce, but some new insights will also be discussed. Growing evidence suggests that multidisciplinary care in specialized clinics improves survival. PMID:29399045

A stable organic-inorganic hybrid layer protected lithium metal anode for long-cycle lithium-oxygen batteries

NASA Astrophysics Data System (ADS)

Zhu, Jinhui; Yang, Jun; Zhou, Jingjing; Zhang, Tao; Li, Lei; Wang, Jiulin; Nuli, Yanna

2017-10-01

A stable organic-inorganic hybrid layer (OIHL) is direct fabricated on lithium metal surface by the interfacial reaction of lithium metal foil with 1-chlorodecane and oxygen/carbon dioxide mixed gas. This favorable OIHL is approximately 30 μm thick and consists of lithium alkyl carbonate and lithium chloride. The lithium-oxygen batteries with OIHL protected lithium metal anode exhibit longer cycle life (340 cycles) than those with bare lithium metal anode (50 cycles). This desirable performance can be ascribed to the robust OIHL which prevents the growth of lithium dendrites and the corrosion of lithium metal.

Evaluation of Pd Nanoparticle-Decorated CeO2-MWCNT Nanocomposite as an Electrocatalyst for Formic Acid Fuel Cells

NASA Astrophysics Data System (ADS)

Saleem, Junaid; Safdar Hossain, SK.; Al-Ahmed, Amir; Rahman, Ateequr; McKay, Gordon; Hossain, Mohammed M.

2018-04-01

In this work, CeO2-modified Pd/CeO2-carbon nanotube (CNT) electrocatalyst for the electro-oxidation of formic acid has been investigated. The support CNT was first modified with different amounts (5-30 wt.%) of CeO2 using a precipitation-deposition method. The electrocatalysts were developed by dispersing Pd on the CeO2-CNT supports using the borohydride reduction method. The synthesized electrocatalysts were analyzed for composition, morphology and electronic structure using x-ray diffraction (XRD), scanning electron microscopy with energy-dispersive x-ray spectroscopy (SEM/EDX), transmission electron microscopy (TEM), x-ray photoelectron spectroscopy (XPS), and thermogravimetric analysis (TGA) techniques. The formation of Pd nanoparticles on the CeO2-CNT support was confirmed using TEM. The activity of Pd/CeO2-CNT and of Pd-CNT samples upon oxidation of formic acid was evaluated by using carbon monoxide stripping voltammetry, cyclic voltammetry, and chronoamperometry. The addition of moderate amounts of cerium oxide (up to 10 wt.%) significantly improved the activity of Pd/CeO2-CNT compared to the unmodified Pd-CNT. Pd/10 wt.% CeO2-CNT showed a current density of 2 A mg-1, which is ten times higher than that of the unmodified Pd-CNT (0.2 A mg-1). Similarly, the power density obtained for Pd/10 wt.% CeO2-CNT in an air-breathing formic acid fuel cell was 6.8 mW/cm2 which is two times higher than Pd-CNT (3.2 mW/cm2), thus exhibiting the promotional effects of CeO2 to Pd/CeO2-CNT. A plausible justification for the improved catalytic performance and stability is provided in the light of the physical characterization results.

Ductile all-cellulose nanocomposite films fabricated from core-shell structured cellulose nanofibrils.

PubMed

Larsson, Per A; Berglund, Lars A; Wågberg, Lars

2014-06-09

Cellulosic materials have many desirable properties such as high mechanical strength and low oxygen permeability and will be an important component in a sustainable biomaterial-based society, but unfortunately they often lack the ductility and formability offered by petroleum-based materials. This paper describes the fabrication and characterization of nanocomposite films made of core-shell modified cellulose nanofibrils (CNFs) surrounded by a shell of ductile dialcohol cellulose, created by heterogeneous periodate oxidation followed by borohydride reduction of the native cellulose in the external parts of the individual fibrils. The oxidation with periodate selectively produces dialdehyde cellulose, and the process does not increase the charge density of the material. Yet the modified cellulose fibers could easily be homogenized to CNFs. Prior to film fabrication, the CNF was shown by atomic force microscopy to be 0.5-2 μm long and 4-10 nm wide. The films were fabricated by filtration, and besides uniaxial tensile testing at different relative humidities, they were characterized by scanning electron microscopy and oxygen permeability. The strength-at-break at 23 °C and 50% RH was 175 MPa, and the films could, before rupture, be strained, mainly by plastic deformation, to about 15% and 37% at 50% RH and 90% RH, respectively. This moisture plasticization was further utilized to form a demonstrator consisting of a double-curved structure with a nominal strain of 24% over the curvature. At a relative humidity of 80%, the films still acted as a good oxygen barrier, having an oxygen permeability of 5.5 mL·μL/(m(2)·24 h·kPa). These properties indicate that this new material has a potential for use as a barrier in complex-shaped structures and hence ultimately reduce the need for petroleum-based plastics.

Prospects for Remediation of 1,2,3-Trichloropropane by Natural and Engineered Abiotic Degradation Reactions

DTIC Science & Technology

2010-06-01

represent predicted values calculated from QSARs described in (8). Blue symbols represent experimental data from (10...C) and FeBH (theor/C) refer to values estimated from QSARs for granular mm sized nano-iron (8) and borohydride reduced nano-iron (14), respectively...Both papers report QSARs for reduction of chlorinated aliphatics using energies of the lowest unoccupied molecular orbital (ELUMO) as the

Rapid determination of nanogram amounts of tellurium in silicate rocks

USGS Publications Warehouse

Greenland, L.P.; Campbell, E.Y.

1976-01-01

A hydride-generation flameless atomic-absorption technique is used to determine as little as 5 ng g-1 tellurium in 0.25 g of silicate rock. After acid decomposition of the sample, tellurium hydride is generated with sodium borohydride and the vapor passed directly to a resistance-heated quartz cell mounted in an atomic-absorption spectrophotometer. Analyses of 11 U.S. Geological Survey standard rocks are presented. ?? 1976.

Prediction of thermodynamically reversible hydrogen storage reactions utilizing Ca-M(M = Li, Na, K)-B-H systems: a first-principles study.

PubMed

Guo, Yajuan; Ren, Ying; Wu, Haishun; Jia, Jianfeng

2013-12-01

Calcium borohydride is a potential candidate for onboard hydrogen storage because it has a high gravimetric capacity (11.5 wt.%) and a high volumetric hydrogen content (∼130 kg m(-3)). Unfortunately, calcium borohydride suffers from the drawback of having very strongly bound hydrogen. In this study, Ca(BH₄)₂ was predicted to form a destabilized system when it was mixed with LiBH₄, NaBH₄, or KBH₄. The release of hydrogen from Ca(BH₄)₂ was predicted to proceed via two competing reaction pathways (leading to CaB₆ and CaH₂ or CaB₁₂H₁₂ and CaH₂) that were found to have almost equal free energies. Using a set of recently developed theoretical methods derived from first principles, we predicted five new hydrogen storage reactions that are among the most attractive of those presently known. These combine high gravimetric densities (>6.0 wt.% H₂) with have low enthalpies [approximately 35 kJ/(mol(-1) H₂)] and are thermodynamically reversible at low pressure within the target window for onboard storage that is actively being considered for hydrogen storage applications. Thus, the first-principles theoretical design of new materials for energy storage in future research appears to be possible.

Mucinous (colloid) adenocarcinomas secrete distinct O-acylated forms of sialomucins: a histochemical study of gastric, colorectal and breast adenocarcinomas.

PubMed

Sáez, C; Japón, M A; Poveda, M A; Segura, D I

2001-12-01

Mucinous (colloid) adenocarcinomas represent a distinct group of tumours defined by the presence of large amounts of extracellular mucins. By using histochemical methods, we analysed mucins secreted by mucinous versus non-mucinous adenocarcinomas and looked for differential secretion profiles. Sixty-four adenocarcinomas were studied (23 colorectal, 17 gastric, and 24 breast tumours). Thirty-two tumours were of the colloid type. The following methods were applied to paraffin tissue sections: (i) Alcian blue (pH 2.5) and periodic acid-Schiff (PAS); (ii) high iron diamine and Alcian blue (pH 2.5); (iii) periodic acid borohydride, potassium hydroxide, and PAS; (iv) periodic acid-thionine Schiff, potassium hydroxide, and PAS; and (v) periodic acid-borohydride and PAS. Most adenocarcinomas secreted acidic mucins, with sialomucins predominating over sulfomucins, except for non-mucinous adenocarcinomas of the breast which showed predominant neutral mucins. All mucinous adenocarcinomas contained C9-O-acyl sialic acid as mono, di(C8,C9)-, or tri(C7,C8,C9)-O-acyl forms. Acidic mucins secreted by the majority of non-colloid adenocarcinomas consisted of non-O-acylated sialomucins. C9-O-acylation of sialic acid is a characteristic feature of mucinous adenocarcinomas and can be readily detected by histochemical methods.

The configuration of 2,6-diamino-3-hydroxypimelic acid in microbial cell walls

PubMed Central

Perkins, H. R.

1969-01-01

β-Hydroxydiaminopimelic acid, together with some diaminopimelic acid, occurs in the cell-wall mucopeptide of certain Actinomycetales. These components were converted into their di-DNP derivatives and separated by chromatography. Hence the relative proportions present in the cell walls of a number of species were measured. The problem of acid-induced inversion of configuration was studied. Of the diaminohydroxypimelic acids isomer B (see Scheme 2; amino groups meso, hydroxy group threo to its neighbouring amino group) always predominated but a small proportion of isomer D (amino groups l, hydroxy group erythro) also occurred. The configuration of the diaminohydroxypimelic acids was determined by periodate oxidation to glutamic γ-semialdehyde, which underwent spontaneous ring-closure. Reduction with sodium borohydride produced optically active proline, the configuration of which was determined by direct measurement of the optical rotation of DNP-proline. Un-cross-linked diaminohydroxypimelic acid in the cell wall was oxidized with periodate in the presence of ammonia. Since the remaining amino group was bound in peptide linkage, ring-closure was prevented and borohydride reduction of the aldehyde–ammonia presumed to be present resulted in the formation of ornithine. The quantity of ornithine was used as a measure of the degree of cross-linking. PMID:4311441

Investigation of the characteristics of a stacked direct borohydride fuel cell for portable applications

NASA Astrophysics Data System (ADS)

Kim, Cheolhwan; Kim, Kyu-Jung; Ha, Man Yeong

To investigate the possibility of the portable application of a direct borohydride fuel cell (DBFC), weight reduction of the stack and high stacking of the cells are investigated for practical running conditions. For weight reduction, carbon graphite is adopted as the bipolar plate material even though it has disadvantages in tight stacking, which results in stacking loss from insufficient material strength. For high stacking, it is essential to have a uniform fuel distribution among cells and channels to maintain equal electric load on each cell. In particular, the design of the anode channel is important because active hydrogen generation causes non-uniformity in the fuel flow-field of the cells and channels. To reduce the disadvantages of stacking force margin and fuel maldistribution, an O-ring type-sealing system with an internal manifold and a parallel anode channel design is adopted, and the characteristics of a single and a five-cell fuel cell stack are analyzed. By adopting carbon graphite, the stack weight can be reduced by 4.2 times with 12% of performance degradation from the insufficient stacking force. When cells are stacked, the performance exceeds the single-cell performance because of the stack temperature increase from the reduction of the radiation area from the narrow stacking of cells.

Electroless growth of silver nanoparticles into mesostructured silica block copolymer films.

PubMed

Bois, Laurence; Chassagneux, Fernand; Desroches, Cédric; Battie, Yann; Destouches, Nathalie; Gilon, Nicole; Parola, Stéphane; Stéphan, Olivier

2010-06-01

Silver nanoparticles and silver nanowires have been grown inside mesostructured silica films obtained from block copolymers using two successive reduction steps: the first one involves a sodium borohydride reduction or a photoreduction of silver nitrate contained in the film, and the second one consists of a silver deposit on the primary nanoparticles, carried out by silver ion solution reduction with hydroxylamine chloride. We have demonstrated that the F127 block copolymer ((PEO)(106)(PPO)(70)(PEO)(106)), "F type", mesostructured silica film is a suitable "soft" template for the fabrication of spherical silver nanoparticles arrays. Silver spheres grow from 7 to 11 nm upon the second reduction step. As a consequence, a red shift of the surface plasmon resonance associated with metallic silver has been observed and attributed to plasmonic coupling between particles. Using a P123 block copolymer ((PEO)(20)(PPO)(70)(PEO)(20)), "P type", mesostructured silica film, we have obtained silver nanowires with typical dimension of 10 nm x 100 nm. The corresponding surface plasmon resonance is blue-shifted. The hydroxylamine chloride treatment appears to be efficient only when a previous chemical reduction is performed, assuming that the first sodium borohydride reduction induces a high concentration of silver nuclei in the first layer of the porous silica (film/air interface), which explains their reactivity for further growth.

Hydrolysis of Mg(BH4)2 and its coordination compounds as a way to obtain hydrogen

NASA Astrophysics Data System (ADS)

Solovev, Mikhail V.; Chashchikhin, Oleg V.; Dorovatovskii, Pavel V.; Khrustalev, Victor N.; Zyubin, A. S.; Zyubina, T. S.; Kravchenko, O. V.; Zaytsev, Alexey A.; Dobrovolsky, Yu. A.

2018-02-01

Three ligand-stabilized Mg(BH4)2-based complexes have been synthesized and evaluated as potential hydrogen storage media for portable fuel cell applications. The new borohydrides: Mg(BH4)2 × 0.5Et2O and Mg(BH4)2 × diglyme (diglyme - CH3O(CH2)2O(CH2)2OCH3) have been synthesized and examined by X-ray single crystal diffraction method. Hydrolysis reactions of the compounds liberate hydrogen in quantities ranging from 46 to 96% of the theoretical yield. The hydrolysis of Mg(BH4)2 and other borohydrides is also accompanied by the diborane formation. The amount of liberated diborane depends on the Mg-coordination environment. To explain this fact quantum-chemical calculations have been performed. It is shown that formation of Mg-O-Mg-bridges enables the side process of diborane generation. It means that the size and denticity of the ligand directly affects the amount of released diborane. In general, the larger the ligand and the higher its denticity, the smaller is amount of diborane produced. The new compound Mg(BH4)2 × diglyme decomposes without diborane formation that allows one to be considered as a new promising chemical hydrogen storage compound for the practical usage.

Investigation of platinum and palladium as potential anodic catalysts for direct borohydride and ammonia borane fuel cells

NASA Astrophysics Data System (ADS)

Olu, Pierre-Yves; Deschamps, Fabien; Caldarella, Giuseppe; Chatenet, Marian; Job, Nathalie

2015-11-01

Platinum and palladium are investigated as anodic catalysts for direct borohydride and direct ammonia borane fuel cells (DBFC and DABFC). Half-cell characterizations performed at 25 °C using NH3BH3 or NaBH4 alkaline electrolytes demonstrate the lowest open-circuit potential and highest electrocatalytic activity for the NH3BH3 alkaline electrolyte for Pd and Pt rotating disk electrodes, respectively. Voltammograms performed in fuel cell configuration at 25 °C confirm this trend: the highest open circuit voltage (1.05 V) and peak power density (181 mW·cm-2) are monitored for DABFC using Pd/C and Pt/C anodes, respectively. Increasing the temperature heightens the peak power density (that reaches 420 mW·cm-2 at 60 °C for DBFC using Pt/C anodes), but strongly generates gas from the fuel hydrolysis, hindering the overall fuel cells performances. The anode texture strongly influences the fuel cell performances, highlighting: (i) that an open anode texture is required to efficiently circulate the anolyte and (ii) the difficulty to compare potential anodic catalysts characterized using different fuel cell setups within the literature. Furthermore, TEM imaging of Pt/C and Pd/C catalysts prior/post DBFC and DABFC operation shows fast degradation of the carbon-supported nanoparticles.

Co3O4 nanowires as efficient catalyst precursor for hydrogen generation from sodium borohydride hydrolysis

NASA Astrophysics Data System (ADS)

Wei, Lei; Cao, Xurong; Ma, Maixia; Lu, Yanhong; Wang, Dongsheng; Zhang, Suling; Wang, Qian

Hydrogen generation from the catalytic hydrolysis of sodium borohydride has many advantages, and therefore, significant research has been undertaken on the development of highly efficient catalysts for this purpose. In our present work, Co3O4 nanowires were successfully synthesized as catalyst precursor by employing SBA-15 as a hard template. For material characterization, high-resolution transmission electron microscopy (HRTEM), powder X-ray diffraction (XRD), fourier-transform infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA), inductively coupled plasma-atomic emission spectroscopy (ICP-AES) and N2 adsorption isotherms were employed, respectively. To measure the catalyst activity, typical water-displacement method was carried out. Using a reaction solution comprising 10wt.% NaBH4 and 2wt.% NaOH, the hydrogen generation rate (HGR) was observed to be as high as 7.74L min-1 g-1 at 25∘C in the presence of Co3O4 nanowires, which is significantly higher than that of CoB nanoparticles and commercial Co3O4 powder. Apparent activation energy was calculated to be 50.9kJ mol-1. After recycling the Co3O4 nanowires six times, HGR was decreased to be 72.6% of the initial level.

Fuel cell system with sodium borohydride as hydrogen source for unmanned aerial vehicles

NASA Astrophysics Data System (ADS)

Kim, Kyunghwan; Kim, Taegyu; Lee, Kiseong; Kwon, Sejin

In this study, we design and fabricate a fuel cell system for application as a power source in unmanned aerial vehicles (UAVs). The fuel cell system consists of a fuel cell stack, hydrogen generator, and hybrid power management system. PEMFC stack with an output power of 100 W is prepared and tested to decide the efficient operating conditions; the stack must be operated in the dead-end mode with purge in order to ensure prolonged stack performance. A hydrogen generator is fabricated to supply gaseous hydrogen to the stack. Sodium borohydride (NaBH 4) is used as the hydrogen source in the present study. Co/Al 2O 3 catalyst is prepared for the hydrolysis of the alkaline NaBH 4 solution at room temperature. The fabricated Co catalyst is comparable to the Ru catalyst. The UAV consumes more power in the takeoff mode than in the cruising mode. A hybrid power management system using an auxiliary battery is developed and evaluated for efficient energy management. Hybrid power from both the fuel cell and battery powers takeoff and turning flight operations, while the fuel cell supplies steady power during the cruising flight. The capabilities of the fuel-cell UAVs for long endurance flights are validated by successful flight tests.

Toxicity of silver nanoparticles towards tumoral human cell lines U-937 and HL-60.

PubMed

Barbasz, Anna; Oćwieja, Magdalena; Roman, Maciej

2017-08-01

The toxicity of three types of silver nanoparticles towards histiocytic lymphoma (U-937) and human promyelocytic cells (HL-60) was studied. The nanoparticles were synthesized in a chemical reduction method using sodium borohydride. Trisodium citrate and cysteamine hydrochloride were used to generate a negative and positive nanoparticle surface charge. The evaluation of cell viability, membrane integrity, antioxidant activity and the induction of inflammation were used to evaluate the difference in cellular response to the nanoparticle treatment. The results revealed that the cysteamine-stabilized (positively charged) nanoparticles (SBATE) were the least toxic although they exhibited a similar ion release profile as the unmodified (negatively charged) nanoparticles obtained using sodium borohydride (SBNM). Citrate-stabilized nanoparticles (SBTC) induced superoxide dismutase (SOD) activity in the HL-60 cells and total antioxidant activity in the U-937 cells despite their resistance to oxidative dissolution. The toxicity of SBNM nanoparticles was manifested in the disruption of membrane integrity, decrease in the mitochondrial functions of cells and the induction of inflammation. These findings allowed to conclude that mechanism of silver nanoparticle cytotoxicity is the combination of effects coming from the surface charge of nanoparticles, released silver ions and biological activity of stabilizing agent molecules. Copyright © 2017 Elsevier B.V. All rights reserved.

Advanced Micro/Nanostructures for Lithium Metal Anodes

PubMed Central

Zhang, Rui; Li, Nian‐Wu; Cheng, Xin‐Bing; Yin, Ya‐Xia

2017-01-01

Owning to their very high theoretical capacity, lithium metal anodes are expected to fuel the extensive practical applications in portable electronics and electric vehicles. However, unstable solid electrolyte interphase and lithium dendrite growth during lithium plating/stripping induce poor safety, low Coulombic efficiency, and short span life of lithium metal batteries. Lately, varies of micro/nanostructured lithium metal anodes are proposed to address these issues in lithium metal batteries. With the unique surface, pore, and connecting structures of different nanomaterials, lithium plating/stripping processes have been regulated. Thus the electrochemical properties and lithium morphologies have been significantly improved. These micro/nanostructured lithium metal anodes shed new light on the future applications for lithium metal batteries. PMID:28331792

76 FR 53056 - Outbound International Mailings of Lithium Batteries

Federal Register 2010, 2011, 2012, 2013, 2014

2011-08-25

... or lithium-ion batteries in accordance with Packing Instruction 967, Section II, or Packing... Secondary Lithium-ion (Rechargeable) Cells and Batteries. Small consumer-type lithium-ion cells and... shipment may contain a maximum of four lithium-ion cells or two lithium-ion batteries. c. The lithium...

The effect of the carbon nanotube buffer layer on the performance of a Li metal battery

NASA Astrophysics Data System (ADS)

Zhang, Ding; Zhou, Yi; Liu, Changhong; Fan, Shoushan

2016-05-01

Lithium (Li) metal is one of the most promising candidates as an anode for the next-generation energy storage systems because of its high specific capacity and lowest negative electrochemical potential. But the growth of Li dendrites limits the application of the Li metal battery. In this work, a type of modified Li metal battery with a carbon nanotube (CNT) buffer layer inserted between the separator and the Li metal electrode was reported. The electrochemical results show that the modified batteries have a much better rate capability and cycling performance than the conventional Li metal batteries. The mechanism study by electrochemical impedance spectroscopy reveals that the modified battery has a smaller charge transfer resistance and larger Li ion diffusion coefficient during the deposition process on the Li electrode than the conventional Li metal batteries. Symmetric battery tests show that the interfacial behavior of the Li metal electrode with the buffer layer is more stable than the naked Li metal electrode. The morphological characterization of the CNT buffer layer and Li metal lamina reveals that the CNT buffer layer has restrained the growth of Li dendrites. The CNT buffer layer has great potential to solve the safety problem of the Li metal battery.Lithium (Li) metal is one of the most promising candidates as an anode for the next-generation energy storage systems because of its high specific capacity and lowest negative electrochemical potential. But the growth of Li dendrites limits the application of the Li metal battery. In this work, a type of modified Li metal battery with a carbon nanotube (CNT) buffer layer inserted between the separator and the Li metal electrode was reported. The electrochemical results show that the modified batteries have a much better rate capability and cycling performance than the conventional Li metal batteries. The mechanism study by electrochemical impedance spectroscopy reveals that the modified battery has a smaller charge transfer resistance and larger Li ion diffusion coefficient during the deposition process on the Li electrode than the conventional Li metal batteries. Symmetric battery tests show that the interfacial behavior of the Li metal electrode with the buffer layer is more stable than the naked Li metal electrode. The morphological characterization of the CNT buffer layer and Li metal lamina reveals that the CNT buffer layer has restrained the growth of Li dendrites. The CNT buffer layer has great potential to solve the safety problem of the Li metal battery. Electronic supplementary information (ESI) available. See DOI: 10.1039/c6nr00465b

Research, Development and Fabrication of Lithium Solar Cells, Part 2

NASA Technical Reports Server (NTRS)

Iles, P. A.

1972-01-01

The development and fabrication of lithium solar cells are discussed. Several single-step, lithium diffusion schedules using lower temperatures and times are described. A comparison was made using evaporated lithium metal as the lithium source, and greatly improved consistency in lithium concentrations was obtained. It was possible to combine all processing steps to obtain lithium doped cells of high output which also contained adequate lithium to ensure good recoverability.

21 CFR 862.3560 - Lithium test system.

Code of Federal Regulations, 2012 CFR

2012-04-01

... 21 Food and Drugs 8 2012-04-01 2012-04-01 false Lithium test system. 862.3560 Section 862.3560....3560 Lithium test system. (a) Identification. A lithium test system is a device intended to measure lithium (from the drug lithium carbonate) in serum or plasma. Measurements of lithium are used to assure...

21 CFR 862.3560 - Lithium test system.

Code of Federal Regulations, 2013 CFR

2013-04-01

... 21 Food and Drugs 8 2013-04-01 2013-04-01 false Lithium test system. 862.3560 Section 862.3560....3560 Lithium test system. (a) Identification. A lithium test system is a device intended to measure lithium (from the drug lithium carbonate) in serum or plasma. Measurements of lithium are used to assure...

21 CFR 862.3560 - Lithium test system.

Code of Federal Regulations, 2010 CFR

2010-04-01

... 21 Food and Drugs 8 2010-04-01 2010-04-01 false Lithium test system. 862.3560 Section 862.3560....3560 Lithium test system. (a) Identification. A lithium test system is a device intended to measure lithium (from the drug lithium carbonate) in serum or plasma. Measurements of lithium are used to assure...

21 CFR 862.3560 - Lithium test system.

Code of Federal Regulations, 2014 CFR

2014-04-01

... 21 Food and Drugs 8 2014-04-01 2014-04-01 false Lithium test system. 862.3560 Section 862.3560....3560 Lithium test system. (a) Identification. A lithium test system is a device intended to measure lithium (from the drug lithium carbonate) in serum or plasma. Measurements of lithium are used to assure...

21 CFR 862.3560 - Lithium test system.

Code of Federal Regulations, 2011 CFR

2011-04-01

... 21 Food and Drugs 8 2011-04-01 2011-04-01 false Lithium test system. 862.3560 Section 862.3560....3560 Lithium test system. (a) Identification. A lithium test system is a device intended to measure lithium (from the drug lithium carbonate) in serum or plasma. Measurements of lithium are used to assure...

Stabilized Lithium-Metal Surface in a Polysulfide-Rich Environment of Lithium-Sulfur Batteries.

PubMed

Zu, Chenxi; Manthiram, Arumugam

2014-08-07

Lithium-metal anode degradation is one of the major challenges of lithium-sulfur (Li-S) batteries, hindering their practical utility as next-generation rechargeable battery chemistry. The polysulfide migration and shuttling associated with Li-S batteries can induce heterogeneities of the lithium-metal surface because it causes passivation by bulk insulating Li2S particles/electrolyte decomposition products on a lithium-metal surface. This promotes lithium dendrite formation and leads to poor lithium cycling efficiency with complicated lithium surface chemistry. Here, we show copper acetate as a surface stabilizer for lithium metal in a polysulfide-rich environment of Li-S batteries. The lithium surface is protected from parasitic reactions with the organic electrolyte and the migrating polysulfides by an in situ chemical formation of a passivation film consisting of mainly Li2S/Li2S2/CuS/Cu2S and electrolyte decomposition products. This passivation film also suppresses lithium dendrite formation by controlling the lithium deposition sites, leading to a stabilized lithium surface characterized by a dendrite-free morphology and improved surface chemistry.

Dual-protection of a graphene-sulfur composite by a compact graphene skin and an atomic layer deposited oxide coating for a lithium-sulfur battery

NASA Astrophysics Data System (ADS)

Yu, Mingpeng; Wang, Aiji; Tian, Fuyang; Song, Hongquan; Wang, Yinshu; Li, Chun; Hong, Jong-Dal; Shi, Gaoquan

2015-03-01

A reduced graphene oxide (rGO)-sulfur composite aerogel with a compact self-assembled rGO skin was further modified by an atomic layer deposition (ALD) of ZnO or MgO layer, and used as a free-standing electrode material of a lithium-sulfur (Li-S) battery. The rGO skin and ALD-oxide coating worked as natural and artificial barriers to constrain the polysulfides within the cathode region. As a result, the Li-S battery based on this electrode material exhibited superior cycling stability, good rate capability and high coulombic efficiency. Furthermore, ALD-ZnO coating was tested for performance improvement and found to be more effective than ALD-MgO coating. The ZnO modified G-S electrode with 55 wt% sulfur loading delivered a maximum discharge capacity of 998 mA h g-1 at a current density of 0.2 C. A high capacity of 846 mA h g-1 was achieved after charging/discharging for 100 cycles with a coulombic efficiency of over 92%. In the case of using LiNO3 as a shuttle inhibitor, this electrode showed an initial discharge capacity of 796 mA h g-1 and a capacity retention of 81% after 250 cycles at a current density of 1 C with an average coulombic efficiency higher than 99.7%.A reduced graphene oxide (rGO)-sulfur composite aerogel with a compact self-assembled rGO skin was further modified by an atomic layer deposition (ALD) of ZnO or MgO layer, and used as a free-standing electrode material of a lithium-sulfur (Li-S) battery. The rGO skin and ALD-oxide coating worked as natural and artificial barriers to constrain the polysulfides within the cathode region. As a result, the Li-S battery based on this electrode material exhibited superior cycling stability, good rate capability and high coulombic efficiency. Furthermore, ALD-ZnO coating was tested for performance improvement and found to be more effective than ALD-MgO coating. The ZnO modified G-S electrode with 55 wt% sulfur loading delivered a maximum discharge capacity of 998 mA h g-1 at a current density of 0.2 C. A high capacity of 846 mA h g-1 was achieved after charging/discharging for 100 cycles with a coulombic efficiency of over 92%. In the case of using LiNO3 as a shuttle inhibitor, this electrode showed an initial discharge capacity of 796 mA h g-1 and a capacity retention of 81% after 250 cycles at a current density of 1 C with an average coulombic efficiency higher than 99.7%. Electronic supplementary information (ESI) available: Procedures of ALD operation, supplementary figures and details of theoretical simulations. See DOI: 10.1039/c5nr00166h

Lithium in 2012

USGS Publications Warehouse

Jaskula, B.W.

2013-01-01

In 2012, estimated world lithium consumption was about 28 kt (31,000 st) of lithium contained in minerals and compounds, an 8 percent increase from that of 2011. Estimated U.S. consumption was about 2 kt (2,200 st) of contained lithium, the same as that of 2011. The United States was thought to rank fourth in consumption of lithium and remained the leading importer of lithium carbonate and the leading producer of value-added lithium materials. One company, Rockwood Lithium Inc., produced lithium compounds from domestic brine resources near Silver Peak, NV.

Lanthanum Nitrate As Electrolyte Additive To Stabilize the Surface Morphology of Lithium Anode for Lithium-Sulfur Battery.

PubMed

Liu, Sheng; Li, Guo-Ran; Gao, Xue-Ping

2016-03-01

Lithium-sulfur (Li-S) battery is regarded as one of the most promising candidates beyond conventional lithium ion batteries. However, the instability of the metallic lithium anode during lithium electrochemical dissolution/deposition is still a major barrier for the practical application of Li-S battery. In this work, lanthanum nitrate, as electrolyte additive, is introduced into Li-S battery to stabilize the surface of lithium anode. By introducing lanthanum nitrate into electrolyte, a composite passivation film of lanthanum/lithium sulfides can be formed on metallic lithium anode, which is beneficial to decrease the reducibility of metallic lithium and slow down the electrochemical dissolution/deposition reaction on lithium anode for stabilizing the surface morphology of metallic Li anode in lithium-sulfur battery. Meanwhile, the cycle stability of the fabricated Li-S cell is improved by introducing lanthanum nitrate into electrolyte. Apparently, lanthanum nitrate is an effective additive for the protection of lithium anode and the cycling stability of Li-S battery.

Surface-protected LiCoO2 with ultrathin solid oxide electrolyte film for high-voltage lithium ion batteries and lithium polymer batteries

NASA Astrophysics Data System (ADS)

Yang, Qi; Huang, Jie; Li, Yejing; Wang, Yi; Qiu, Jiliang; Zhang, Jienan; Yu, Huigen; Yu, Xiqian; Li, Hong; Chen, Liquan

2018-06-01

Surface modification of LiCoO2 with the ultrathin film of solid state electrolyte of Li1.4Al0.4Ti1.6(PO4)3 (LATP) has been realized by a new and facile solution-based method. The coated LiCoO2 reveals enhanced structural and electrochemical stability at high voltage (4.5 V vs Li+/Li) in half-cell with liquid electrolyte. Transmission electron microscopy (TEM) images show that a dense LATP coating layer is covered on the surface of LiCoO2 uniformly with thickness of less than 20 nm. The LATP coating layer is proven to be able to prevent the direct contact between the cathode and the electrolyte effectively and thus to suppress the side reactions of liquid electrolyte with LiCoO2 surface at high charging voltage. As a result, dissolution of Co3+ has been largely suppressed over prolonged cycling as indicated by the X-ray photoelectron spectroscopy (XPS) measurements. Due to this surface passivating feature, the electrochemical performance of 0.5 wt% LATP modified LiCoO2 has also been evaluated in an all solid lithium battery with poly(ethylene oxide)-based polymer electrolyte. The cell exhibits 93% discharge capacity retention of the initial discharge capacity after 50 cycles at the charging cut-off voltage of 4.2 V, suggesting that the LATP coating layer is effective to suppress the oxidation of PEO at high voltage.

Stabilization of cubic Li7La3Hf2O12 by Al-doping

NASA Astrophysics Data System (ADS)

Baklanova, Yana V.; Tyutyunnik, Alexander P.; Tarakina, Nadezda V.; Fortes, A. Dominic; Maksimova, Lidiya G.; Korona, Daniil V.; Denisova, Tatyana A.

2018-07-01

In this paper we report on the stabilization of cubic Li7La3Hf2O12 by Al3+ doping and present a detailed crystal structure study and lithium ion conductivity measurements of the obtained compound. Polycrystalline Al-doped Li7La3Hf2O12 was prepared by a modified solid state method. The compound consists of micrometer size grains encapsulated by a glassy phase, which helps preventing the volatilization of lithium during annealing. Al-doped Li7La3Hf2O12 crystallizes in the garnet-related structure with a cubic unit cell (sp. gr. Ia 3 bar d (230)). A structural refinement using X-ray and neutron powder diffraction data showed that the Al3+ ions occupy only tetrahedral Li+ sites in the structure. The presence of overextended leading edges of the peaks on the XRD and NPD data is described by the introduction of an additional phase with rhombohedral distortion that occurs through a stretching of the cubic phase along the body diagonal. The activation energy as well as the total conductivity at room temperature are close to values obtained for un-doped cubic Li7La3Zr2O12 and Li7La3Hf2O12 garnets, which make Al-doped Li7La3Hf2O12 a potential candidate for the application as solid electrolyte in solid-state rechargeable lithium-ion batteries.

Development of lithium powder based anode with conductive carbon materials for lithium batteries

NASA Astrophysics Data System (ADS)

Park, Man Su

Current lithium ion battery with a graphite anode shows stable cycle performance and safety. However, the lithium ion battery still has the limitation of having a low energy density caused by the application of lithium intercalated cathode and anode with low energy density. The combination of high capacity non-lithiated cathode such as sulfur and carbon and lithium metal anode has been researched for a long time to maximize battery's energy density. However, this cell design also has a lot of technical challenges to be solved. Among the challenges, lithium anode's problem related to lithium dendrite growth causing internal short and low cycling efficiency is very serious. Thus, extensive research on lithium metal anode has been performed to solve the lithium dendrite problem and a major part of the research has been focused on the control of the interface between lithium and electrolyte. However, research on lithium anode design itself has not been much conducted. In this research, innovative lithium anode design for less dendrite growth and higher cycling efficiency was suggested. Literature review for the lithium dendrite growth mechanism was conducted in Chapter 2 to develop electrode design concept and the importance of the current density on lithium dendrite growth was also found in the literatures. The preliminary test was conducted to verify the developed electrode concept by using lithium powder based anode (LIP) with conductive carbon materials and the results showed that lithium dendrite growth could be suppressed in this electrode design due to its increased electrochemical surface area and lithium deposition sites during lithium deposition. The electrode design suggested in Chapter 2 was extensively studied in Chapter 3 in terms of lithium dendrite growth morphology, lithium cycling efficiency and full cell cycling performance. This electrode concept was further developed to maximize the electrode's performance and safety in Chapter 4. In this new electrode design, electrically isolated super-p carbon agglomerates in the electrode were effectively reduced by adding conductive fillers such as graphite and further improvement in cycling performance and safety was also verified. The lithium powder based anode with conductive carbon materials is very useful concept as an alternative anode design instead of pure lithium metal anode for high energy density lithium batteries such as lithium-sulfur and lithium-air. As shown in Chapter 5, this electrode concept can be further developed and optimized through the application of new carbon materials and structure.

Investigation of lithium PFC surface characteristics and low recycling at LTX/LTX-Beta

NASA Astrophysics Data System (ADS)

Maan, Anurag; Kaita, Robert; Elliott, Drew; Boyle, Dennis; Majeski, Richard; Donovan, David; Buzi, Luxherta; Koel, Bruce E.; Biewer, Theodore M.

2017-10-01

Lithium coatings on high-Z PFCs at LTX have led to improved plasma performance. The initial hypothesis was that lithium retains hydrogen by forming lithium hydride and thereby enabling low recycling in LTX. However, recent in-vacuo measurements indicate the presence of lithium oxide in deposited lithium coatings. Improved plasma performance continued to be observed in the presence of lithium oxide. These observations raise questions like what is the nature of the lithium oxide surface, whether the PFC is an amorphous mixture of lithium and lithium oxide or something more ordered like a lithium oxide layer growing on top of lithium, and whether lithium oxide is responsible for any retention of hydrogen from the plasma. To investigate the mechanism by which the LTX PFC might be responsible for low recycling, we discuss the results of deuterium retention measurements using NRA/RBS and sample characterization using high resolution XPS (HR-XPS) in bulk lithium samples. Baseline HR-XPS scans indicate the presence of Lithium Oxide on sputtered lithium samples. Status of related planned experiments at LTX- β will also be discussed. This work was supported by the US. D.O.E. contract DE-AC05-00OR22725 and DE-AC02-09CH11466. BEK acknowledges support of this work by the U.S. DOE, Office of Science/FES under Award Number DE-SC0012890.

Lithium

USGS Publications Warehouse

Jaskula, B.W.

2011-01-01

In 2010, lithium consumption in the United States was estimated to have been about 1 kt (1,100 st) of contained lithium, a 23-percent decrease from 2009. The United States was estimated to be the fourth largest consumer of lithium. It remained the leading importer of lithium carbonate and the leading producer of value-added lithium materials. Only one company, Chemetall Foote Corp. (a subsidiary of Chemetall GmbH of Germany), produced lithium compounds from domestic resources. In 2010, world lithium consumption was estimated to have been about 21 kt (22,000 st) of lithium contained in minerals and compounds, a 12-percent increase from 2009.

Lithium

USGS Publications Warehouse

Jaskula, B.W.

2010-01-01

In 2009, lithium consumption in the United States was estimated to have been about 1.2 kt (1,300 st) of contained lithium, a 40-percent decrease from 2008. The United States was estimated to be the fourth largest consumer of lithium, and remained the leading importer of lithium carbonate and the leading producer of value-added lithium materials. Only one company, Chemetall Foote Corp. (a subsidiary of Chemetall GmbH of Germany), produced lithium compounds from domestic resources. In 2009, world lithium consumption was estimated to have been about 18.7 kt (20,600 st) of lithium contained in minerals and compounds.

Electrochemical Energy Storage Materials

DTIC Science & Technology

2012-07-01

of porous polypropylene membrane (Celgrad® 2400) separators soaked in a liquid electrolyte solution containing 1.0 M lithium hexafluorophosphate ... Lithium Li-ion Lithium ion LiO2 Lithium Dioxide LiOx Lithium Oxide (non stoichiometric) LiPF6 lithium hexafluorophosphate LT-ALD Low Temperature...Nanostructured Battery Architectures, Nanostructured Lithium Ion Batteries 16. SECURITY CLASSIFICATION OF: 17. LIMITATION OF ABSTRACT: SAR 18. NUMBER OF

APPARATUS FOR THE PRODUCTION OF LITHIUM METAL

DOEpatents

Baker, P.S.; Duncan, F.R.; Greene, H.B.

1961-08-22

Methods and apparatus for the production of high-purity lithium from lithium halides are described. The apparatus is provided for continuously contacting a molten lithium halide with molten barium, thereby forming lithium metal and a barium halide, establishing separate layers of these reaction products and unreacted barium and lithium halide, and continuously withdrawing lithium and barium halide from the reaction zone. (AEC)

49 CFR 173.185 - Lithium cells and batteries.

Code of Federal Regulations, 2014 CFR

2014-10-01

... 20 Wh for a lithium ion cell or 100 Wh for a lithium ion battery. After December 31, 2015, each lithium ion battery subject to this provision must be marked with the Watt-hour rating on the outside case... cell and 25 g for a lithium metal battery and 60 Wh for a lithium ion cell or 300 Wh for a lithium ion...

On the reasons for low sulphur utilization in the lithium-sulphur batteries

NASA Astrophysics Data System (ADS)

Kolosnitsyn, V. S.; Kuzmina, E. V.; Karaseva, E. V.

2015-01-01

This work is to study the reasons for the relatively low efficiency of sulphur reduction (about 75%) in lithium-sulphur batteries. The two main reasons for that are suggested to be: the relatively low electrochemical activity of low order lithium polysulphides and blocking of the carbon framework of the sulphur electrode by insoluble products of electrochemical reactions - sulphur and lithium sulphide. The electrochemical activity of lithium polysulphides with different composition (Li2Sn, n = 2-6) has been studied in 1 M solutions of CF3SO3Li in sulfolane. It is shown that lithium polysulphides including lithium disulphide are able to electrochemically reduce with efficiency close to 100%. The electrochemical activity of lithium polysulphides decreases with the order. The order of lithium polysulphides affects the value of voltage of discharge plateaus but not the efficiency of sulphur reducing in the lithium polysulphides species. The relatively low efficiency of sulphur reduction in the lithium-sulphur batteries is more likely caused by blocking of carbon particles in the sulphur electrode by insoluble products of electrochemical reactions (sulphur and lithium sulphide). This prevents the electrochemical reduction of low order lithium polysulphides and especially lithium disulphide.

High conducting oxide--sulfide composite lithium superionic conductor

DOEpatents

Liang, Chengdu; Rangasamy, Ezhiylmurugan; Dudney, Nancy J.; Keum, Jong Kahk; Rondinone, Adam Justin

2017-01-17

A solid electrolyte for a lithium-sulfur battery includes particles of a lithium ion conducting oxide composition embedded within a lithium ion conducting sulfide composition. The lithium ion conducting oxide composition can be Li.sub.7La.sub.3Zr.sub.2O.sub.12 (LLZO). The lithium ion conducting sulfide composition can be .beta.-Li.sub.3PS.sub.4 (LPS). A lithium ion battery and a method of making a solid electrolyte for a lithium ion battery are also disclosed.

Spreading of lithium on a stainless steel surface at room temperature

DOE Office of Scientific and Technical Information (OSTI.GOV)

Skinner, C. H.; Capece, A. M.; Roszell, J. P.

Lithium conditioned plasma facing surfaces have lowered recycling and enhanced plasma performance on many fusion devices and liquid lithium plasma facing components are under consideration for future machines. A key factor in the performance of liquid lithium components is the wetting by lithium of its container. We have observed the surface spreading of lithium from a mm-scale particle to adjacent stainless steel surfaces using a scanning Auger microprobe that has elemental discrimination. Here, the spreading of lithium occurred at room temperature (when lithium is a solid) from one location at a speed of 0.62 μm/day under ultrahigh vacuum conditions. Separatemore » experiments using temperature programmed desorption (TPD) investigated bonding energetics between monolayer-scale films of lithium and stainless steel. While multilayer lithium desorption from stainless steel begins to occur just above 500 K (E des = 1.54 eV), sub-monolayer Li desorption occurred in a TPD peak at 942 K (E des = 2.52 eV) indicating more energetically favorable lithium-stainless steel bonding (in the absence of an oxidation layer) than lithium lithium bonding.« less

Spreading of lithium on a stainless steel surface at room temperature

DOE PAGES

Skinner, C. H.; Capece, A. M.; Roszell, J. P.; ...

2015-11-10

Lithium conditioned plasma facing surfaces have lowered recycling and enhanced plasma performance on many fusion devices and liquid lithium plasma facing components are under consideration for future machines. A key factor in the performance of liquid lithium components is the wetting by lithium of its container. We have observed the surface spreading of lithium from a mm-scale particle to adjacent stainless steel surfaces using a scanning Auger microprobe that has elemental discrimination. Here, the spreading of lithium occurred at room temperature (when lithium is a solid) from one location at a speed of 0.62 μm/day under ultrahigh vacuum conditions. Separatemore » experiments using temperature programmed desorption (TPD) investigated bonding energetics between monolayer-scale films of lithium and stainless steel. While multilayer lithium desorption from stainless steel begins to occur just above 500 K (E des = 1.54 eV), sub-monolayer Li desorption occurred in a TPD peak at 942 K (E des = 2.52 eV) indicating more energetically favorable lithium-stainless steel bonding (in the absence of an oxidation layer) than lithium lithium bonding.« less

Spreading of lithium on a stainless steel surface at room temperature

NASA Astrophysics Data System (ADS)

Skinner, C. H.; Capece, A. M.; Roszell, J. P.; Koel, B. E.

2016-01-01

Lithium conditioned plasma facing surfaces have lowered recycling and enhanced plasma performance on many fusion devices and liquid lithium plasma facing components are under consideration for future machines. A key factor in the performance of liquid lithium components is the wetting by lithium of its container. We have observed the surface spreading of lithium from a mm-scale particle to adjacent stainless steel surfaces using a scanning Auger microprobe that has elemental discrimination. The spreading of lithium occurred at room temperature (when lithium is a solid) from one location at a speed of 0.62 μm/day under ultrahigh vacuum conditions. Separate experiments using temperature programmed desorption (TPD) investigated bonding energetics between monolayer-scale films of lithium and stainless steel. While multilayer lithium desorption from stainless steel begins to occur just above 500 K (Edes = 1.54 eV), sub-monolayer Li desorption occurred in a TPD peak at 942 K (Edes = 2.52 eV) indicating more energetically favorable lithium-stainless steel bonding (in the absence of an oxidation layer) than lithium-lithium bonding.

Effect of Copper Oxide, Titanium Dioxide, and Lithium Fluoride on the Thermal Behavior and Decomposition Kinetics of Ammonium Nitrate

NASA Astrophysics Data System (ADS)

Vargeese, Anuj A.; Mija, S. J.; Muralidharan, Krishnamurthi

2014-07-01

Ammonium nitrate (AN) is crystallized along with copper oxide, titanium dioxide, and lithium fluoride. Thermal kinetic constants for the decomposition reaction of the samples were calculated by model-free (Friedman's differential and Vyzovkins nonlinear integral) and model-fitting (Coats-Redfern) methods. To determine the decomposition mechanisms, 12 solid-state mechanisms were tested using the Coats-Redfern method. The results of the Coats-Redfern method show that the decomposition mechanism for all samples is the contracting cylinder mechanism. The phase behavior of the obtained samples was evaluated by differential scanning calorimetry (DSC), and structural properties were determined by X-ray powder diffraction (XRPD). The results indicate that copper oxide modifies the phase transition behavior and can catalyze AN decomposition, whereas LiF inhibits AN decomposition, and TiO2 shows no influence on the rate of decomposition. Possible explanations for these results are discussed. Supplementary materials are available for this article. Go to the publisher's online edition of the Journal of Energetic Materials to view the free supplemental file.

Thickness, humidity, and polarization dependent ferroelectric switching and conductivity in Mg doped lithium niobate

DOE PAGES

Neumayer, Sabine M.; Strelcov, Evgheni; Manzo, Michele; ...

2015-12-28

Mg doped lithium niobate (Mg:LN) exhibits several advantages over undoped LN such as resistance to photorefraction, lower coercive fields, and p-type conductivity that is particularly pronounced at domain walls and opens up a range of applications, e.g., in domain wall electronics. Engineering of precise domain patterns necessitates well founded knowledge of switching kinetics, which can differ significantly from that of undoped LN. In this work, the role of humidity and sample composition in polarization reversal has been investigated under application of the same voltage waveform. Control over domain sizes has been achieved by varying the sample thickness and initial polarizationmore » as well as atmospheric conditions. Additionally, local introduction of proton exchanged phases allows for inhibition of domain nucleation or destabilization, which can be utilized to modify domain patterns. In polarization dependent current flow, attributed to charged domain walls and band bending, it the rectifying ability of Mg: LN in combination with suitable metal electrodes that allow for further tailoring of conductivity is demonstrated.« less

Appearance of small polaron hopping conduction in iron modified cobalt lithium bismuth borate glasses

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dahiya, M. S.; Khasa, S., E-mail: skhasa@yahoo.com; Yadav, Arti

2016-05-23

Lithium bismuth borate glasses containing different amounts of cobalt and iron oxides having chemical composition xFe{sub 2}O{sub 3}•(20-x)CoO•30Li{sub 2}O•10Bi{sub 2}O{sub 3}•40B{sub 2}O{sub 3} (x = 0, 5, 10, 15 and 20 mol% abbreviated as CFLBB1-5 respectively) prepared via melt quench technique have been investigated for their dc electrical conductivity. The amorphous nature of prepared glasses has been confirmed through X-ray diffraction measurements. The dc electrical conductivity has been analyzed by applying Mott’s small polaron hopping model. Activation energies corresponding to lower and higher temperature region have been evaluated. The iron ion concentration (N), mean spacing between iron ions (R) and polaronmore » radius (R{sub p}) has been evaluated using the values of phonon radius (R{sub ph}) and Debye temperature (θ{sub D}). The glass sample without iron (CFLBB1) shows ionic conductivity but the incorporation of iron in the glass matrix results in the appearance of electronic conductivity.« less

Electrospun montmorillonite modified poly(vinylidene fluoride) nanocomposite separators for lithium-ion batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fang, Changjiang; Yang, Shuli; Zhao, Xinfei

2016-07-15

Highlights: • Composite separators of PVDF and MMT for lithium-ion batteries were electrospun. • Thermal dimensional stability and tensile property of composite separators get improved. • Presence of montmorillonite promotes electrical properties of PVDF fibrous separators. • Batteries consisting of PVDF/MMT-5% separator achieve the best performance. - Abstract: Composite separators of poly(vinylidene fluoride) (PVDF) with different contents of montmorillonite (MMT) for Li-ion batteries have been fabricated by electrospinning. The morphology, function group, crystallinity, and mechanical properties of membranes were investigated by scanning electron microscope (SEM), Fourier Transform infrared spectra (FT-IR), differential scanning calorimetry (DSC), and tensile test, respectively. Interlayer spacingmore » of MMT in polymer was characterized by X-ray diffraction (XRD). In addition, the results of electrochemical measurements suggest that PVDF/MMT-5% composite membrane has maximum ionic conductivity of 4.2 mS cm{sup −1}, minimum interfacial resistance of 97 Ω, and excellent electrochemical stability. The cell comprising PVDF/MMT-5% composite membrane shows higher capacity and more stable cycle performance than the one using commercial Celgard PP membrane.« less

Formation of self-organized domain structures with charged domain walls in lithium niobate with surface layer modified by proton exchange

NASA Astrophysics Data System (ADS)

Shur, V. Ya.; Akhmatkhanov, A. R.; Chuvakova, M. A.; Dolbilov, M. A.; Zelenovskiy, P. S.; Lobov, A. I.

2017-03-01

We have studied the self-organized dendrite domain structures appeared as a result of polarization reversal in the uniform field in lithium niobate single crystals with the artificial surface layer created by proton exchange. We have revealed the self-organized sub-micron scale dendrite domain patterns consisting of domain stripes oriented along the X crystallographic directions separated by arrays of dashed residual domains at the surface by scanning probe microscopy. Raman confocal microscopy allowed visualizing the quasi-regular dendrite domain structures with similar geometry in the vicinity of both polar surfaces. The depth of the structure was about 20 μm for Z+ polar surface and 70 μm for Z- one. According to the proposed mechanism, the dendrite structure formation at the surface was related to the ineffective screening of the residual depolarization field. The computer simulation of the structure formation based on the cellular automata model with probabilistic switching rule proved the eligibility of the proposed scheme, the simulated dendrite domain patterns at various depths being similar to the experimental ones.

Conjugated polymer energy level shifts in lithium-ion battery electrolytes.

PubMed

Song, Charles Kiseok; Eckstein, Brian J; Tam, Teck Lip Dexter; Trahey, Lynn; Marks, Tobin J

2014-11-12

The ionization potentials (IPs) and electron affinities (EAs) of widely used conjugated polymers are evaluated by cyclic voltammetry (CV) in conventional electrochemical and lithium-ion battery media, and also by ultraviolet photoelectron spectroscopy (UPS) in vacuo. By comparing the data obtained in the different systems, it is found that the IPs of the conjugated polymer films determined by conventional CV (IPC) can be correlated with UPS-measured HOMO energy levels (EH,UPS) by the relationship EH,UPS = (1.14 ± 0.23) × qIPC + (4.62 ± 0.10) eV, where q is the electron charge. It is also found that the EAs of the conjugated polymer films measured via CV in conventional (EAC) and Li(+) battery (EAB) media can be linearly correlated by the relationship EAB = (1.07 ± 0.13) × EAC + (2.84 ± 0.22) V. The slopes and intercepts of these equations can be correlated with the dielectric constants of the polymer film environments and the redox potentials of the reference electrodes, as modified by the surrounding electrolyte, respectively.

Influence of annealing on the photodeposition of silver on periodically poled lithium niobate

DOE PAGES

Carville, N. Craig; Neumayer, Sabine M.; Manzo, Michele; ...

2016-02-03

Here, the preferential deposition of metal nanoparticles onto periodically poled lithium niobate surfaces, whereby photogenerated electrons accumulate in accordance with local electric fields and reduce metal ions from solution, is known to depend on the intensity and wavelength of the illumination and the concentration of the solution used. Here, it is shown that for identical deposition conditions (wavelength, intensity, concentration), post-poling annealing for 10 h at 200 °C modifies the surface reactivity through the reorientation of internal defect fields. Whereas silver nanoparticles deposit preferentially on the +z domains on unannealed crystals, the deposition occurs preferentially along 180 degrees domain wallsmore » for annealed crystals. In neither case is the deposition selective; limited deposition occurs also on the unannealed -z domain surface and on both annealed domain surfaces. The observed behavior is attributed to a relaxation of the poling-induced defect frustration mediated by Li + ion mobility during annealing, which affects the accumulation of electrons, thereby changing the surface reactivity. The evolution of the defect field with temperature is corroborated using Raman spectroscopy.« less

Suppression of dendritic lithium growth in lithium metal-based batteries.

PubMed

Li, Linlin; Li, Siyuan; Lu, Yingying

2018-06-19

Lithium metal-based batteries offer promising prospects as alternatives to today's lithium-ion batteries, due to their ultra-high energy density. Unfortunately, the application of lithium metal is full of challenges and has puzzled researchers for more than 40 years. In this feature article, we describe the history of the development of lithium metal batteries and their existing key challenges, which include non-uniform electrodeposition, volume expansion, high reactivity of the lithium metal/unstable solid electrolyte interphase (SEI), and the shuttling of active cathode materials. Then, we focus on the growth mechanisms of uneven lithium electrodeposition and extend the discussion to the approaches to inhibit lithium dendrites. Finally, we discuss future directions that are expected to drive progress in the development of lithium metal batteries.

Polyethylene-glycol-doped polypyrrole increases the rate performance of the cathode in lithium-sulfur batteries.

PubMed

Wu, Feng; Chen, Junzheng; Li, Li; Zhao, Teng; Liu, Zhen; Chen, Renjie

2013-08-01

Polypyrrole-polyethylene glycol (PPy/PEG)-modified sulfur/aligned carbon nanotubes (PPy/PEG-S/A-CNTs) were synthesized by using an in situ polymerization method. The ratio of PPy to PEG equaled 31.7:1 after polymerization, and the PEG served as a cation dopant in the polymerization and electrochemical reactions. Elemental analysis, FTIR, Raman spectroscopy, XRD, and electrochemical methods were performed to measure the physicochemical properties of the composite. Elemental analysis demonstrated that the sulfur, PPy, PEG, A-CNT, and chloride content in the synthesized material was 64.6%, 22.1%, 0.7%, 12.1%, and 0.5%, respectively. The thickness of the polymer shell was about 15-25 nm, and FTIR confirmed the successful PPy/PEG synthesis. The cathode exhibited a high initial specific capacity of 1355 mAh g(-1) , and a sulfur usage of 81.1%. The reversible capacity of 924 mAh g(-1) was obtained after 100 cycles, showing a remarkably improved cyclability compared to equivalent systems without PEG doping and without any coatings. PPy/PEG provided an effective electronically conductive network and a stable interface structure for the cathode. Rate performance of the PPy/PEG- S/A-CNT composite was more than double that of the unmodified S/A-CNTs. Remarkably, the battery could work at a very high current density of 8 A g(-1) and reached an initial capacity of 542 mAh g(-1) ; it also retained a capacity of 480 mAh g(-1) after 100 cycles. The addition of PEG as a dopant in the PPy shell contributed to this prominent rate improvement. Lithium ions and electrons were available everywhere on the surfaces of the particles, and thus could greatly improve the electrochemical reaction; PEG is a well-known solvent for lithium salts and a very good lithium-ion catcher. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Preparation of Proton Exchange Membranes and Lithium Batteries from Melamine-containing Ormosils

NASA Technical Reports Server (NTRS)

Tigelaar, Dean M.; Kinder, James D.; Meador, Mary Ann; Waldecker, James; Bennett, William R.

2004-01-01

Our laboratory has recently reported a series of rodcoil polymers for lithium batteries that display dimensionally stable films with good ionic conductivity. The rod segments consist of rigid linear and branched polyimides and the coil segments are polyethylene oxides (PEO). It has been proposed that good mechanical and transport properties are due to phase separation between the rod and coil segments. It was also observed that increased branching and molecular weight lead to increased conductivity. The following study was undertaken to assess the effects of phase separation in polyalkylene oxides connected by melamine linkages. Melamine was chosen as the linking unit because it provides a branching site, cation binding sites to help ionic transport between polymer chains, and the opportunity for self assembly through hydrogen bonding. Polymers were made by the reaction of cyanuric chloride with a series of amine-terminated alkylene oxides. A linear polymer was first made, followed by reaction of the third site on cyanuric chloride with varying ratios of monofunctional Jeffamine and (3-aminopropyl)triethoxysilane. The lithium trifluoromethane sulfonamide-doped polymers are then crosslinked through a sol-gel process to form free-standing films. Initial results have shown mechanically strong films with lithium conductivities on the order of 2 x 10(exp -5) S/cm at ambient temperature. In a separate study, organically modified silanes (Ormosils) that contain sulfonic acid derivatized melamines have been incorporated into proton exchange membranes. The membranes are made by reaction of the primary amine groups of various ratios of melamine derivative and difunctional Jeffamine (MW = 2000) with the epoxide group of (3-Glycidyloxypropyl)trimethoxysilane. The films were then cross-linked through a sol-gel process. Resulting sulfuric acid doped films are strong, flexible, and have proton conductivities on the order of 2 x l0(exp -2) S/cm (120 C, 25% relative humidity). Our best results have been observed when films contain 60% PEO and 40% sulfonated melamine.

Substitution of Li for Cu in Cu2ZnSnS4: Toward Wide Band Gap Absorbers with Low Cation Disorder for Thin Film Solar Cells.

PubMed

Lafond, A; Guillot-Deudon, C; Vidal, J; Paris, M; La, C; Jobic, S

2017-03-06

The substitution of lithium for copper in Cu 2 ZnSnS 4 (CZTS) has been experimentally and theoretically investigated. Formally, the (Cu 1-x Li x )ZnSnS 4 system exhibits two well-defined solid solutions. Indeed, single crystal structural analyses demonstrate that the low (x < 0.4) and high (x > 0.6) lithium-content compounds adopt the kesterite structure and the wurtz-kesterite structure, respectively. For x between 0.4 and 0.6, the two aforementioned structure types coexist. Moreover, 119 Sn NMR analyses carried out on a (Cu 0.7 Li 0.3 ) 2 ZnSnS 4 sample clearly indicate that lithium replaces copper preferentially on two of the three available 2-fold crystallographic sites commonly occupied by Cu and Zn in disordered kesterite. Furthermore, the observed individual lines in the NMR spectrum suggest that the propensity of Cu and Zn atoms to be randomly distributed over the 2c and 2d crystallographic sites is lowered when lithium is partially substituted for copper. Additionally, the first-principles calculations provide insights into the arrangement of Li atoms as a function of the Cu/Zn disorder and its effect on the structural (lattice parameters) and optical properties of CZTS (band gap evolution). Those calculations agree with the experimental observations and account for the evolutions of the unit cell parameters as well as for the increase of band gap when the Li-content increases. The calculation of the formation enthalpy of point defect unambiguously indicates that Li modifies the Cu/Zn disorder in a manner similar to the change of Cu/Zn disorder induced by Ag alloying. Overall, it was found that Li alloying is a versatile way of tuning the optoelectronic properties of CZTS making it a good candidate as wide band gap materials for the top cells of tandem solar cells.

Laboratory Studies of Hydrogen Gas Generation Using the Cobalt Chloride Catalyzed Sodium Borohydride-Water Reaction

DTIC Science & Technology

2015-07-01

already use hydrogen for weather balloons . Besides cost, hydrogen has other advantages over helium. Hydrogen has more lift than helium, so larger...of water vapor entering the gas stream, and avoid damaging the balloon /aerostat (aerostats typically have an operational temperature range of -50 to...Aerostats: “Gepard” Tethered Aerostats with Mobile Mooring Systems. Available at http://rosaerosystems.com/aero/obj7. Accessed June 4, 2015. 11

CERDEC Fuel Cell Team: Military Transitions for Soldier Fuel Cells

DTIC Science & Technology

2008-10-27

Fuel Cell (DMFC) (PEO Soldier) Samsung: 20W DMFC (CRADA) General Atomics & Jadoo: 50W Ammonia Borane Fueled PEMFC Current Fuel Cell Team Efforts...Continued Ardica: 20W Wearable PEMFC operating on Chemical Hydrides Spectrum Brands w/ Rayovac: Hydrogen Generators and Alkaline Fuel Cells for AA...100W Ammonia Borane fueled PEMFC Ultralife: 150W sodium borohydride fueled PEMFC Protonex: 250W RMFC and Power Manager (ARO) NanoDynamics: 250W SOFC

Mathematical Modeling and Optimization Studies on Development of Fuel Cells for Multifarious Applications

DTIC Science & Technology

2010-05-12

multicomponent steady-state model for liquid -feed solid polymer electrolyte DBFCs. These fuel cells use sodium borohydride (NaBH4) in alkaline media...layers, diffusion layers and the polymer electrolyte membrane for a liquid feed DBFC. Diffusion of reactants within and between the pores is accounted...projected for futuristic portable applications. In this project we developed a three- dimensional, multicomponent steady-state model for liquid -feed solid

75 FR 9147 - Hazardous Materials: Transportation of Lithium Batteries

Federal Register 2010, 2011, 2012, 2013, 2014

2010-03-01

... for lithium metal batteries and lithium ion batteries were adopted into the UN Recommendations. The... regulations were revised to reflect this change. Adopt shipping descriptions for lithium ion batteries including lithium ion polymer batteries (UN3480), lithium ion batteries packed with equipment including...

77 FR 28259 - Mailings of Lithium Batteries

Federal Register 2010, 2011, 2012, 2013, 2014

2012-05-14

... containing lithium metal or lithium-ion cells or batteries and applies regardless of quantity, size, watt... ``lithium content'' for secondary lithium-ion batteries when describing maximum quantity limits. In addition...-ion (Rechargeable) Cells and Batteries [Revise 10.20.6 as follows:] Small consumer-type lithium-ion...

Clinical assessment of pacemaker power sources

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bilitch, M.; Parsonnet, V.; Furman, S.

1980-01-01

The development of power sources for cardiac pacemakers has progressed from a 15-year usage of mercury-zinc batteries to widely used and accepted lithium cells. At present, there are about 6 different types of lithium cells incorporated into commercially distributed pacemakers. The authors reviewed experience over a 5-year period with 1711 mercury-zinc, 130 nuclear (P238) and 1912 lithium powered pacemakers. The lithium units have included 698 lithium-iodide, 270 lithium-silver chromate, 135 lithium-thionyl chloride, 31 lithium-lead and 353 lithium-cupric sulfide batteries. 57 of the lithium units have failed (91.2% component failure and 5.3% battery failure). 459 mercury-zinc units failed (25% component failuremore » and 68% battery depletion). The data show that lithium powered pacemaker failures are primarily component, while mercury-zinc failures are primarily battery related. It is concluded that mercury-zinc powered pulse generators are obsolete and that lithium and nuclear (P238) power sources are highly reliable over the 5 years for which data are available. 3 refs.« less

High performance discharges in the Lithium Tokamak eXperiment with liquid lithium walls

DOE PAGES

Schmitt, J. C.; Bell, R. E.; Boyle, D. P.; ...

2015-05-15

The first-ever successful operation of a tokamak with a large area (40% of the total plasma surface area) liquid lithium wall has been achieved in the Lithium Tokamak eXperiment (LTX). These results were obtained with a new, electron beam-based lithium evaporation system, which can deposit a lithium coating on the limiting wall of LTX in a five-minute period. Preliminary analyses of diamagnetic and other data for discharges operated with a liquid lithium wall indicate that confinement times increased by 10 x compared to discharges with helium-dispersed solid lithium coatings. Ohmic energy confinement times with fresh lithium walls, solid and liquid,more » exceed several relevant empirical scaling expressions. Spectroscopic analysis of the discharges indicates that oxygen levels in the discharges limited on liquid lithium walls were significantly reduced compared to discharges limited on solid lithium walls. Finally, Tokamak operations with a full liquid lithium wall (85% of the total plasma surface area) have recently started.« less

Grain Boundary Engineering of Lithium-Ion-Conducting Lithium Lanthanum Titanate for Lithium-Air Batteries

DTIC Science & Technology

2016-01-01

release; distribution is unlimited. 1 1. Introduction Lithium (Li)- ion batteries are currently one of the leading energy storage device technologies...ARL-TR-7584 ● JAN 2016 US Army Research Laboratory Grain Boundary Engineering of Lithium - Ion - Conducting Lithium Lanthanum...Titanate for Lithium -Air Batteries by Victoria L Blair, Claire V Weiss Brennan, and Joseph M Marsico Approved for public

Lithium use in batteries

USGS Publications Warehouse

Goonan, Thomas G.

2012-01-01

Lithium has a number of uses but one of the most valuable is as a component of high energy-density rechargeable lithium-ion batteries. Because of concerns over carbon dioxide footprint and increasing hydrocarbon fuel cost (reduced supply), lithium may become even more important in large batteries for powering all-electric and hybrid vehicles. It would take 1.4 to 3.0 kilograms of lithium equivalent (7.5 to 16.0 kilograms of lithium carbonate) to support a 40-mile trip in an electric vehicle before requiring recharge. This could create a large demand for lithium. Estimates of future lithium demand vary, based on numerous variables. Some of those variables include the potential for recycling, widespread public acceptance of electric vehicles, or the possibility of incentives for converting to lithium-ion-powered engines. Increased electric usage could cause electricity prices to increase. Because of reduced demand, hydrocarbon fuel prices would likely decrease, making hydrocarbon fuel more desirable. In 2009, 13 percent of worldwide lithium reserves, expressed in terms of contained lithium, were reported to be within hard rock mineral deposits, and 87 percent, within brine deposits. Most of the lithium recovered from brine came from Chile, with smaller amounts from China, Argentina, and the United States. Chile also has lithium mineral reserves, as does Australia. Another source of lithium is from recycled batteries. When lithium-ion batteries begin to power vehicles, it is expected that battery recycling rates will increase because vehicle battery recycling systems can be used to produce new lithium-ion batteries.

Reversible Lithium Neurotoxicity: Review of the Literature

PubMed Central

Netto, Ivan

2012-01-01

Objective: Lithium neurotoxicity may be reversible or irreversible. Reversible lithium neurotoxicity has been defined as cases of lithium neurotoxicity in which patients recovered without any permanent neurologic sequelae, even after 2 months of an episode of lithium toxicity. Cases of reversible lithium neurotoxicity differ in clinical presentation from those of irreversible lithium neurotoxicity and have important implications in clinical practice. This review aims to study the clinical presentation of cases of reversible lithium neurotoxicity. Data Sources: A comprehensive electronic search was conducted in the following databases: MEDLINE (PubMed), 1950 to November 2010; PsycINFO, 1967 to November 2010; and SCOPUS (EMBASE), 1950 to November 2010. MEDLINE and PsycINFO were searched by using the OvidSP interface. Study Selection: A combination of the following search terms was used: lithium AND adverse effects AND central nervous system OR neurologic manifestation. Publications cited include articles concerned with reversible lithium neurotoxicity. Data Extraction: The age, sex, clinical features, diagnostic categories, lithium doses, serum lithium levels, precipitating factors, and preventive measures of 52 cases of reversible lithium neurotoxicity were extracted. Data Synthesis: Among the 52 cases of reversible lithium neurotoxicity, patients ranged in age from 10 to 80 years and a greater number were female (P = .008). Most patients had affective disorders, schizoaffective disorders, and/or depression (P < .001) and presented mainly with acute organic brain syndrome. In most cases, the therapeutic serum lithium levels were less than or equal to 1.5 mEq/L (P < .001), and dosage regimens were less than 2,000 mg/day. Specific drug combinations with lithium, underlying brain pathology, abnormal tissue levels, specific diagnostic categories, and elderly populations were some of the precipitating factors reported for reversible lithium neurotoxicity. The preventive measures were also described. Conclusions: Reversible lithium neurotoxicity presents with a certain clinical profile and precipitating factors for which there are appropriate preventive measures. This recognition will help in early diagnosis and prompt treatment of lithium neurotoxicity. PMID:22690368

Towards a Unified Understanding of Lithium Action in Basic Biology and its Significance for Applied Biology.

PubMed

Jakobsson, Eric; Argüello-Miranda, Orlando; Chiu, See-Wing; Fazal, Zeeshan; Kruczek, James; Nunez-Corrales, Santiago; Pandit, Sagar; Pritchet, Laura

2017-12-01

Lithium has literally been everywhere forever, since it is one of the three elements created in the Big Bang. Lithium concentration in rocks, soil, and fresh water is highly variable from place to place, and has varied widely in specific regions over evolutionary and geologic time. The biological effects of lithium are many and varied. Based on experiments in which animals are deprived of lithium, lithium is an essential nutrient. At the other extreme, at lithium ingestion sufficient to raise blood concentration significantly over 1 mM/, lithium is acutely toxic. There is no consensus regarding optimum levels of lithium intake for populations or individuals-with the single exception that lithium is a generally accepted first-line therapy for bipolar disorder, and specific dosage guidelines for sufferers of that condition are generally agreed on. Epidemiological evidence correlating various markers of social dysfunction and disease vs. lithium level in drinking water suggest benefits of moderately elevated lithium compared to average levels of lithium intake. In contrast to other biologically significant ions, lithium is unusual in not having its concentration in fluids of multicellular animals closely regulated. For hydrogen ions, sodium ions, potassium ions, calcium ions, chloride ions, and magnesium ions, blood and extracellular fluid concentrations are closely and necessarily regulated by systems of highly selective channels, and primary and secondary active transporters. Lithium, while having strong biological activity, is tolerated over body fluid concentrations ranging over many orders of magnitude. The lack of biological regulation of lithium appears due to lack of lithium-specific binding sites and selectivity filters. Rather lithium exerts its myriad physiological and biochemical effects by competing for macromolecular sites that are relatively specific for other cations, most especially for sodium and magnesium. This review will consider what is known about the nature of this competition and suggest using and extending this knowledge towards the goal of a unified understanding of lithium in biology and the application of that understanding in medicine and nutrition.

ASSESSMENT OF LITHIUM USING THE IEHR EVALUATIVE PROCESS FOR ASSESSING HUMAN DEVELOPMENTAL AND REPRODUCTIVE TOXICITY OF AGENTS

EPA Science Inventory

This document presents an evaluation of the reproductive and developmental effects of lithium and reviews toxicologic information on several specific lithium salts: ithium carbonate, lithium chloride, lithium citrate, and lithium hypochlorite. ithium (Li), an alkali metal, is a n...

77 FR 68069 - Outbound International Mailings of Lithium Batteries

Federal Register 2010, 2011, 2012, 2013, 2014

2012-11-15

... (Rechargeable) Cells and Batteries Small consumer-type lithium-ion cells and batteries like those used to power... of only four lithium-ion cells or two lithium-ion batteries. c. The lithium content must not exceed... POSTAL SERVICE 39 CFR Part 20 Outbound International Mailings of Lithium Batteries AGENCY: Postal...

77 FR 28488 - Outbound International Mailings of Lithium Batteries and Other Dangerous Goods

Federal Register 2010, 2011, 2012, 2013, 2014

2012-05-15

... Instructions. Lithium-ion cells and lithium metal batteries are listed in the Technical Instructions as Class 9... metal or lithium alloy (non-rechargeable) cells and batteries, or secondary lithium-ion cells and... POSTAL SERVICE 39 CFR Part 20 Outbound International Mailings of Lithium Batteries and Other...

Lithium Down-regulates Histone Deacetylase 1 (HDAC1) and Induces Degradation of Mutant Huntingtin*

PubMed Central

Wu, Shuai; Zheng, Shui-Di; Huang, Hong-Ling; Yan, Li-Chong; Yin, Xiao-Fei; Xu, Hai-Neng; Zhang, Kang-Jian; Gui, Jing-Hua; Chu, Liang; Liu, Xin-Yuan

2013-01-01

Lithium is an effective mood stabilizer that has been clinically used to treat bipolar disorder for several decades. Recent studies have suggested that lithium possesses robust neuroprotective and anti-tumor properties. Thus far, a large number of lithium targets have been discovered. Here, we report for the first time that HDAC1 is a target of lithium. Lithium significantly down-regulated HDAC1 at the translational level by targeting HDAC1 mRNA. We also showed that depletion of HDAC1 is essential for the neuroprotective effects of lithium and for the lithium-mediated degradation of mutant huntingtin through the autophagic pathway. Our studies explain the multiple functions of lithium and reveal a novel mechanism for the function of lithium in neurodegeneration. PMID:24165128

Where is the lithium? Quantitative determination of the lithium distribution in lithium ion battery cells: Investigations on the influence of the temperature, the C-rate and the cell type

NASA Astrophysics Data System (ADS)

Vortmann-Westhoven, Britta; Winter, Martin; Nowak, Sascha

2017-04-01

With lithium being the capacity determining species in lithium-ion battery (LIB) cells, the local quantification is of enormous importance for understanding of the cell performance. The investigation of the lithium distribution in LIB full cells is performed with two different cell types, T-cells of the Swagelok® type and pouch bag cells with lithium nickel cobalt manganese oxide and mesocarbon microbead graphite as the active materials as well as a lithium hexafluorophosphate based organic carbonate solvent electrolyte. The lithium content of/at the individual components of the cells is analyzed for different states of charge (SOCs) by inductively coupled plasma-optical emission spectrometry (ICP-OES) and the lithium distribution as well as the loss of active lithium within the cells is calculated after cycling. With increasing the SOC, the lithium contents decrease in the cathodes and simultaneously increase in the anodes. The temperature increase shows a clear shift of the lithium content in the direction of the anode for the T-cells. The comparison of the C-rate influence shows that the lower the C-rate, the more the lithium content on the electrodes is shifted into the direction of the anode.

Documentation of Stainless Steel Lithium Circuit Test Section Design. Suppl

NASA Technical Reports Server (NTRS)

Godfroy, Thomas J. (Compiler); Martin, James J.

2010-01-01

The Early Flight Fission-Test Facilities (EFF-TF) team was tasked by Naval Reactors Prime Contract Team (NRPCT) to design, fabricate, and test an actively pumped lithium (Li) flow circuit. This Li circuit takes advantage of work in progress at the EFF TF on a stainless steel sodium/potassium (NaK) circuit. The effort involved modifying the original stainless steel NaK circuit such that it could be operated with Li in place of NaK. This new design considered freeze/thaw issues and required the addition of an expansion tank and expansion/extrusion volumes in the circuit plumbing. Instrumentation has been specified for Li and circuit heaters have been placed throughout the design to ensure adequate operational temperatures and no uncontrolled freezing of the Li. All major components have been designed and fabricated prior to circuit redesign for Li and were not modified. Basic circuit components include: reactor segment, Li to gas heat exchanger, electromagnetic liquid metal pump, load/drain reservoir, expansion reservoir, instrumentation, and trace heaters. The reactor segment, based on a Los Alamos National Laboratory 100-kW design study with 120 fuel pins, is the only prototypic component in the circuit. However, due to earlier funding constraints, a 37-pin partial-array of the core, including the central three rings of fuel pins (pin and flow path dimensions are the same as those in the full design), was selected for fabrication and test. This Technical Publication summarizes the design and integration of the pumped liquid metal Li flow circuit as of May 1, 2005. This supplement contains drawings, analysis, and calculations

Documentation of Stainless Steel Lithium Circuit Test Section Design

NASA Technical Reports Server (NTRS)

Godfroy, T. J.; Martin, J. J.; Stewart, E. T.; Rhys, N. O.

2010-01-01

The Early Flight Fission-Test Facilities (EFF-TF) team was tasked by Naval Reactors Prime Contract Team (NRPCT) to design, fabricate, and test an actively pumped lithium (Li) flow circuit. This Li circuit takes advantage of work in progress at the EFF TF on a stainless steel sodium/potassium (NaK) circuit. The effort involved modifying the original stainless steel NaK circuit such that it could be operated with Li in place of NaK. This new design considered freeze/thaw issues and required the addition of an expansion tank and expansion/extrusion volumes in the circuit plumbing. Instrumentation has been specified for Li and circuit heaters have been placed throughout the design to ensure adequate operational temperatures and no uncontrolled freezing of the Li. All major components have been designed and fabricated prior to circuit redesign for Li and were not modified. Basic circuit components include: reactor segment, Li to gas heat exchanger, electromagnetic liquid metal pump, load/drain reservoir, expansion reservoir, instrumentation, and trace heaters. The reactor segment, based on a Los Alamos National Laboratory 100-kW design study with 120 fuel pins, is the only prototypic component in the circuit. However, due to earlier funding constraints, a 37-pin partial-array of the core, including the central three rings of fuel pins (pin and flow path dimensions are the same as those in the full design), was selected for fabrication and test. This Technical Publication summarizes the design and integration of the pumped liquid metal Li flow circuit as of May 1, 2005.

Antidepressant-like Responses to Lithium in Genetically Diverse Mouse Strains

PubMed Central

Can, Adem; Blackwell, Robert A.; Piantadosi, Sean C.; Dao, David T.; O’Donnell, Kelley C.; Gould, Todd D.

2011-01-01

A mood stabilizing and antidepressant response to lithium is only found in a subgroup of bipolar disorder and depression patients. Identifying strains of mice that are responsive and non-responsive to lithium may elucidate genomic and other biological factors that play a role in lithium responsiveness. Mouse strains were tested in the forced swim, tail suspension, and open field tests after acute and chronic systemic, and intracerebroventricular and chronic lithium treatments. Serum and brain lithium levels were measured. Three (129S6/SvEvTac, C3H/HeNHsd, C57BL/6J) of the eight inbred strains tested, and one (CD-1) of the three outbred strains, showed an antidepressant-like response in the forced swim test following acute systemic administration of lithium. The three responsive inbred strains, as well as the DBA/2J strain, were also responsive in the forced swim test after chronic administration of lithium. However, in the tail suspension test, acute lithium resulted in an antidepressant-like effect only in C3H/HeNHsd mice. Only C57BL/6J and DBA/2J were responsive in the tail suspension test after chronic administration of lithium. Intracerebroventricular lithium administration resulted in a similar response profile in BALB/cJ (non-responsive) and C57BL/6J (responsive) strains. Serum and brain lithium concentrations demonstrated that behavioral results were not due to differential pharmacokinetics of lithium in individual strains, suggesting that genetic factors likely regulate responsiveness to lithium. Our results indicate that responsiveness to lithium in tests of antidepressant efficacy varies among genetically diverse mouse strains. These results will assist in identifying genomic factors associated with lithium responsiveness and the mechanisms of lithium action. PMID:21306560

Lithium enrichment in intracontinental rhyolite magmas leads to Li deposits in caldera basins.

PubMed

Benson, Thomas R; Coble, Matthew A; Rytuba, James J; Mahood, Gail A

2017-08-16

The omnipresence of lithium-ion batteries in mobile electronics, and hybrid and electric vehicles necessitates discovery of new lithium resources to meet rising demand and to diversify the global lithium supply chain. Here we demonstrate that lake sediments preserved within intracontinental rhyolitic calderas formed on eruption and weathering of lithium-enriched magmas have the potential to host large lithium clay deposits. We compare lithium concentrations of magmas formed in a variety of tectonic settings using in situ trace-element measurements of quartz-hosted melt inclusions to demonstrate that moderate to extreme lithium enrichment occurs in magmas that incorporate felsic continental crust. Cenozoic calderas in western North America and in other intracontinental settings that generated such magmas are promising new targets for lithium exploration because lithium leached from the eruptive products by meteoric and hydrothermal fluids becomes concentrated in clays within caldera lake sediments to potentially economically extractable levels.Lithium is increasingly being utilized for modern technology in the form of lithium-ion batteries. Here, using in situ measurements of quartz-hosted melt inclusions, the authors demonstrate that preserved lake sediments within rhyolitic calderas have the potential to host large lithium-rich clay deposits.

Electrochemical hydrogen Storage Systems

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dr. Digby Macdonald

2010-08-09

As the global need for energy increases, scientists and engineers have found a possible solution by using hydrogen to power our world. Although hydrogen can be combusted as a fuel, it is considered an energy carrier for use in fuel cells wherein it is consumed (oxidized) without the production of greenhouse gases and produces electrical energy with high efficiency. Chemical storage of hydrogen involves release of hydrogen in a controlled manner from materials in which the hydrogen is covalently bound. Sodium borohydride and aminoborane are two materials given consideration as chemical hydrogen storage materials by the US Department of Energy.more » A very significant barrier to adoption of these materials as hydrogen carriers is their regeneration from 'spent fuel,' i.e., the material remaining after discharge of hydrogen. The U.S. Department of Energy (DOE) formed a Center of Excellence for Chemical Hydrogen Storage, and this work stems from that project. The DOE has identified boron hydrides as being the main compounds of interest as hydrogen storage materials. The various boron hydrides are then oxidized to release their hydrogen, thereby forming a 'spent fuel' in the form of a lower boron hydride or even a boron oxide. The ultimate goal of this project is to take the oxidized boron hydrides as the spent fuel and hydrogenate them back to their original form so they can be used again as a fuel. Thus this research is essentially a boron hydride recycling project. In this report, research directed at regeneration of sodium borohydride and aminoborane is described. For sodium borohydride, electrochemical reduction of boric acid and sodium metaborate (representing spent fuel) in alkaline, aqueous solution has been investigated. Similarly to literature reports (primarily patents), a variety of cathode materials were tried in these experiments. Additionally, approaches directed at overcoming electrostatic repulsion of borate anion from the cathode, not described in the previous literature for electrochemical reduction of spent fuels, have been attempted. A quantitative analytical method for measuring the concentration of sodium borohydride in alkaline aqueous solution has been developed as part of this work and is described herein. Finally, findings from stability tests for sodium borohydride in aqueous solutions of several different compositions are reported. For aminoborane, other research institutes have developed regeneration schemes involving tributyltin hydride. In this report, electrochemical reduction experiments attempting to regenerate tributyltin hydride from tributyltin chloride (a representative by-product of the regeneration scheme) are described. These experiments were performed in the non-aqueous solvents acetonitrile and 1,2-dimethoxyethane. A non-aqueous reference electrode for electrolysis experiments in acetonitrile was developed and is described. One class of boron hydrides, called polyhedral boranes, became of interest to the DOE due to their ability to contain a sufficient amount of hydrogen to meet program goals and because of their physical and chemical safety attributes. Unfortunately, the research performed here has shown that polyhedral boranes do not react in such a way as to allow enough hydrogen to be released, nor do they appear to undergo hydrogenation from the spent fuel form back to the original hydride. After the polyhedral boranes were investigated, the project goals remained the same but the hydrogen storage material was switched by the DOE to ammonia borane. Ammonia borane was found to undergo an irreversible hydrogen release process, so a direct hydrogenation was not able to occur. To achieve the hydrogenation of the spent ammonia borane fuel, an indirect hydrogenation reaction is possible by using compounds called organotin hydrides. In this process, the organotin hydrides will hydrogenate the spent ammonia borane fuel at the cost of their own oxidation, which forms organotin halides. To enable a closed-loop cycle, our task was then to be able to hydrogenate the organotin halides back to their hydride form. In addition to this experimental work, a parallel project was carried out to develop a new model of electrochemical impedance spectroscopy (EIS) that could be used to define the mechanisms of the electrochemical hydrogenation reactions. The EIS technique is capable of probing complex chemical and electrochemical reactions, and our model was written into a computer code that allowed the input of experimental EIS data and the extraction of kinetic parameters based on a best-fit analysis of theoretical reaction schemes. Finally, electrochemical methods for hydrogenating organic and metallo-organic materials have been explored.« less

Reasons for lithium discontinuation in men and women with bipolar disorder: a retrospective cohort study.

PubMed

Öhlund, Louise; Ott, Michael; Oja, Sofia; Bergqvist, Malin; Lundqvist, Robert; Sandlund, Mikael; Salander Renberg, Ellinor; Werneke, Ursula

2018-02-07

Lithium remains first choice as maintenance treatment for bipolar affective disorder. Yet, about half of all individuals may stop their treatment at some point, despite lithium's proven benefits concerning the prevention of severe affective episodes and suicide. Retrospective cohort study in the Swedish region of Norrbotten into the causes of lithium discontinuation. The study was set up to (1) test whether patients with bipolar affective disorder or schizoaffective disorder, treated with lithium maintenance therapy, were more likely to discontinue lithium because of adverse effects than lack of therapeutic effectiveness, (2) explore gender differences, (3) understand the role of diagnosis and (4) identify who, patient or doctor, took the initiative to stop lithium. Review of medical records for all episodes of lithium discontinuation that had occurred between 1997 and 2013 with the intent to stop lithium for good. Of 873 patients treated with lithium, 54% discontinued lithium, corresponding to 561 episodes of lithium discontinuation. In 62% of episodes, lithium was discontinued due to adverse effects, in 44% due to psychiatric reasons, and in 12% due to physical reasons interfering with lithium treatment. The five single most common adverse effects leading to lithium discontinuation were diarrhoea (13%), tremor (11%), polyuria/polydipsia/diabetes insipidus (9%), creatinine increase (9%) and weight gain (7%). Women were as likely as men to take the initiative to stop lithium, but twice as likely to consult a doctor before taking action (p < 0.01). Patients with type 1 BPAD or SZD were more likely to discontinue lithium than patients with type 2 or unspecified BPAD (p < 0.01). Patients with type 1 BPAD or SZD were more likely to refuse medication (p < 0.01). Conversely, patients with type 2 or unspecified BPAD were three times as likely to discontinue lithium for lack or perceived lack of effectiveness (p < 0.001). Stopping lithium treatment is common and occurs mostly due to adverse effects. It is important to discuss potential adverse effects with patients before initiation and continuously during lithium treatment, to reduce the frequency of potentially unnecessary discontinuations.

Multi-layered, chemically bonded lithium-ion and lithium/air batteries

DOEpatents

Narula, Chaitanya Kumar; Nanda, Jagjit; Bischoff, Brian L; Bhave, Ramesh R

2014-05-13

Disclosed are multilayer, porous, thin-layered lithium-ion batteries that include an inorganic separator as a thin layer that is chemically bonded to surfaces of positive and negative electrode layers. Thus, in such disclosed lithium-ion batteries, the electrodes and separator are made to form non-discrete (i.e., integral) thin layers. Also disclosed are methods of fabricating integrally connected, thin, multilayer lithium batteries including lithium-ion and lithium/air batteries.

Population Pharmacokinetic Analyses of Lithium: A Systematic Review.

PubMed

Methaneethorn, Janthima

2018-02-01

Even though lithium has been used for the treatment of bipolar disorder for several decades, its toxicities are still being reported. The major limitation in the use of lithium is its narrow therapeutic window. Several methods have been proposed to predict lithium doses essential to attain therapeutic levels. One of the methods used to guide lithium therapy is population pharmacokinetic approach which accounts for inter- and intra-individual variability in predicting lithium doses. Several population pharmacokinetic studies of lithium have been conducted. The objective of this review is to provide information on population pharmacokinetics of lithium focusing on nonlinear mixed effect modeling approach and to summarize significant factors affecting lithium pharmacokinetics. A literature search was conducted from PubMed database from inception to December, 2016. Studies conducted in humans, using lithium as a study drug, providing population pharmacokinetic analyses of lithium by means of nonlinear mixed effect modeling, were included in this review. Twenty-four articles were identified from the database. Seventeen articles were excluded based on the inclusion and exclusion criteria. A total of seven articles were included in this review. Of these, only one study reported a combined population pharmacokinetic-pharmacodynamic model of lithium. Lithium pharmacokinetics were explained using both one- and two-compartment models. The significant predictors of lithium clearance identified in most studies were renal function and body size. One study reported a significant effect of age on lithium clearance. The typical values of lithium clearance ranged from 0.41 to 9.39 L/h. The magnitude of inter-individual variability on lithium clearance ranged from 12.7 to 25.1%. Only two studies evaluated the models using external data sets. Model methodologies in each study are summarized and discussed in this review. For future perspective, a population pharmacokinetic-pharmacodynamic study of lithium is recommended. Moreover, external validation of previously published models should be performed.

Lithium Dinitramide as an Additive in Lithium Power Cells

NASA Technical Reports Server (NTRS)

Gorkovenko, Alexander A.

2007-01-01

Lithium dinitramide, LiN(NO2)2 has shown promise as an additive to nonaqueous electrolytes in rechargeable and non-rechargeable lithium-ion-based electrochemical power cells. Such non-aqueous electrolytes consist of lithium salts dissolved in mixtures of organic ethers, esters, carbonates, or acetals. The benefits of adding lithium dinitramide (which is also a lithium salt) include lower irreversible loss of capacity on the first charge/discharge cycle, higher cycle life, lower self-discharge, greater flexibility in selection of electrolyte solvents, and greater charge capacity. The need for a suitable electrolyte additive arises as follows: The metallic lithium in the anode of a lithium-ion-based power cell is so highly reactive that in addition to the desired main electrochemical reaction, it engages in side reactions that cause formation of resistive films and dendrites, which degrade performance as quantified in terms of charge capacity, cycle life, shelf life, first-cycle irreversible capacity loss, specific power, and specific energy. The incidence of side reactions can be reduced through the formation of a solid-electrolyte interface (SEI) a thin film that prevents direct contact between the lithium anode material and the electrolyte. Ideally, an SEI should chemically protect the anode and the electrolyte from each other while exhibiting high conductivity for lithium ions and little or no conductivity for electrons. A suitable additive can act as an SEI promoter. Heretofore, most SEI promotion was thought to derive from organic molecules in electrolyte solutions. In contrast, lithium dinitramide is inorganic. Dinitramide compounds are known as oxidizers in rocket-fuel chemistry and until now, were not known as SEI promoters in battery chemistry. Although the exact reason for the improvement afforded by the addition of lithium dinitramide is not clear, it has been hypothesized that lithium dinitramide competes with other electrolyte constituents to react with lithium on the surface of the anode to form a beneficial SEI. Apparently, nitrides and oxides that result from reduction of lithium dinitramide on the anode produce a thin, robust SEI different from the SEIs formed from organic SEI promoters. The SEI formed from lithium dinitramide is more electronically insulating than is the film formed in the presence of an otherwise identical electrolyte that does not include lithium dinitramide. SEI promotion with lithium dinitramide is useful in batteries with metallic lithium and lithium alloy anodes.

A low-temperature electrolyte for lithium and lithium-ion batteries

NASA Astrophysics Data System (ADS)

Plichta, E. J.; Behl, W. K.

An electrolyte consisting of 1 M solution of lithium hexafluorophosphate in 1:1:1 ethylene carbonate(EC)-dimethyl carbonate(DMC)-ethyl methyl carbonate(EMC) is proposed for low temperature applications of lithium and lithium-ion cells. The new electrolyte has good conductivity and electrochemical stability. Lithium and lithium-ion cells using the new electrolyte were found to be operable at temperatures down to -40°C. The paper also reports on the electrochemical stability of aluminum metal, which is used as a substrate for the positive electrodes in lithium-ion cells, in the new electrolyte.

Lithium

USGS Publications Warehouse

Jaskula, B.W.

2012-01-01

In 2011, world lithium consumption was estimated to have been about 25 kt (25,000 st) of lithium contained in minerals and compounds, a 10-percent increase from 2010. U.S. consumption was estimated to have been about 2 kt (2,200 st) of contained lithium, a 100-percent increase from 2010. The United States was estimated to be the fourth-ranked consumer of lithium and remained the leading importer of lithium carbonate and the leading producer of value-added lithium materials. One company, Chemetall Foote Corp. (a subsidiary of Chemetall GmbH of Germany), produced lithium compounds from domestic brine resources near Silver Peak, NV.

Lithium-associated hyperthyroidism.

PubMed

Siyam, Fadi F; Deshmukh, Sanaa; Garcia-Touza, Mariana

2013-08-01

Goiters and hypothyroidism are well-known patient complications of the use of lithium for treatment of bipolar disease. However, the occurrence of lithium-induced hyperthyroidism is a more rare event. Many times, the condition can be confused with a flare of mania. Monitoring through serial biochemical measurement of thyroid function is critical in patients taking lithium. Hyperthyroidism induced by lithium is a condition that generally can be controlled medically without the patient having to discontinue lithium therapy, although in some circumstances, discontinuation of lithium therapy may be indicated. We report on a patient case of lithium-associated hyperthyroidism that resolved after discontinuation of the medication.

Tracking Lithium Ions via Widefield Fluorescence Microscopy for Battery Diagnostics.

PubMed

Padilla, Nicolas A; Rea, Morgan T; Foy, Michael; Upadhyay, Sunil P; Desrochers, Kyle A; Derus, Tyler; Knapper, Kassandra A; Hunter, Nathanael H; Wood, Sharla; Hinton, Daniel A; Cavell, Andrew C; Masias, Alvaro G; Goldsmith, Randall H

2017-07-28

Direct tracking of lithium ions with time and spatial resolution can provide an important diagnostic tool for understanding mechanisms in lithium ion batteries. A fluorescent indicator of lithium ions, 2-(2-hydroxyphenyl)naphthoxazole, was synthesized and used for real-time tracking of lithium ions via widefield fluorescence microscopy. The fluorophore can be excited with visible light and was shown to enable quantitative determination of the lithium ion diffusion constant in a microfluidic model system for a plasticized polymer electrolyte lithium battery. The use of widefield fluorescence microscopy for in situ tracking of lithium ions in batteries is discussed.

Organic hydrogen peroxide-driven low charge potentials for high-performance lithium-oxygen batteries with carbon cathodes

PubMed Central

Wu, Shichao; Qiao, Yu; Yang, Sixie; Ishida, Masayoshi; He, Ping; Zhou, Haoshen

2017-01-01

Reducing the high charge potential is a crucial concern in advancing the performance of lithium-oxygen batteries. Here, for water-containing lithium-oxygen batteries with lithium hydroxide products, we find that a hydrogen peroxide aqueous solution added in the electrolyte can effectively promote the decomposition of lithium hydroxide compounds at the ultralow charge potential on a catalyst-free Ketjen Black-based cathode. Furthermore, for non-aqueous lithium-oxygen batteries with lithium peroxide products, we introduce a urea hydrogen peroxide, chelating hydrogen peroxide without any water in the organic, as an electrolyte additive in lithium-oxygen batteries with a lithium metal anode and succeed in the realization of the low charge potential of ∼3.26 V, which is among the best levels reported. In addition, the undesired water generally accompanying hydrogen peroxide solutions is circumvented to protect the lithium metal anode and ensure good battery cycling stability. Our results should provide illuminating insights into approaches to enhancing lithium-oxygen batteries. PMID:28585527

Ultrafast fluxional exchange dynamics in electrolyte solvation sheath of lithium ion battery

PubMed Central

Lee, Kyung-Koo; Park, Kwanghee; Lee, Hochan; Noh, Yohan; Kossowska, Dorota; Kwak, Kyungwon; Cho, Minhaeng

2017-01-01

Lithium cation is the charge carrier in lithium-ion battery. Electrolyte solution in lithium-ion battery is usually based on mixed solvents consisting of polar carbonates with different aliphatic chains. Despite various experimental evidences indicating that lithium ion forms a rigid and stable solvation sheath through electrostatic interactions with polar carbonates, both the lithium solvation structure and more importantly fluctuation dynamics and functional role of carbonate solvent molecules have not been fully elucidated yet with femtosecond vibrational spectroscopic methods. Here we investigate the ultrafast carbonate solvent exchange dynamics around lithium ions in electrolyte solutions with coherent two-dimensional infrared spectroscopy and find that the time constants of the formation and dissociation of lithium-ion···carbonate complex in solvation sheaths are on a picosecond timescale. We anticipate that such ultrafast microscopic fluxional processes in lithium-solvent complexes could provide an important clue to understanding macroscopic mobility of lithium cation in lithium-ion battery on a molecular level. PMID:28272396

Oriented TiO2 nanotubes as a lithium metal storage medium

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Jae-Hun; Kang, Hee-Kook; Woo, Sang-Gil

2014-07-01

A new strategy for suppressing dendritic lithium growth in rechargeable lithium metal batteries is introduced, in which TiO2 nanotube (NT) array electrodes prepared by anodization are used as a metallic lithium storage medium. During the first charge process, lithium ions are inserted into the crystal structure of the TiO2 NT arrays, and then, lithium metal is deposited on the surfaces of the NT arrays, i.e., in the NT pores and between NT walls. From the second cycle onward, the TiO2 material is used as lithium ion pathways, which results in the effective current distribution for lithium deposition and prevents disintegrationmore » of the deposited metallic lithium. Compared to a Li(Cu foil)-LiCoO2 cell, the Li(TiO2 NT)-LiCoO2 cell exhibits enhanced cycling efficiency. This new concept will enable other 3D structured negative active materials to be used as lithium metal storage media for lithium metal batteries.« less

Ultrafast fluxional exchange dynamics in electrolyte solvation sheath of lithium ion battery

NASA Astrophysics Data System (ADS)

Lee, Kyung-Koo; Park, Kwanghee; Lee, Hochan; Noh, Yohan; Kossowska, Dorota; Kwak, Kyungwon; Cho, Minhaeng

2017-03-01

Lithium cation is the charge carrier in lithium-ion battery. Electrolyte solution in lithium-ion battery is usually based on mixed solvents consisting of polar carbonates with different aliphatic chains. Despite various experimental evidences indicating that lithium ion forms a rigid and stable solvation sheath through electrostatic interactions with polar carbonates, both the lithium solvation structure and more importantly fluctuation dynamics and functional role of carbonate solvent molecules have not been fully elucidated yet with femtosecond vibrational spectroscopic methods. Here we investigate the ultrafast carbonate solvent exchange dynamics around lithium ions in electrolyte solutions with coherent two-dimensional infrared spectroscopy and find that the time constants of the formation and dissociation of lithium-ion...carbonate complex in solvation sheaths are on a picosecond timescale. We anticipate that such ultrafast microscopic fluxional processes in lithium-solvent complexes could provide an important clue to understanding macroscopic mobility of lithium cation in lithium-ion battery on a molecular level.

Organic hydrogen peroxide-driven low charge potentials for high-performance lithium-oxygen batteries with carbon cathodes

NASA Astrophysics Data System (ADS)

Wu, Shichao; Qiao, Yu; Yang, Sixie; Ishida, Masayoshi; He, Ping; Zhou, Haoshen

2017-06-01

Reducing the high charge potential is a crucial concern in advancing the performance of lithium-oxygen batteries. Here, for water-containing lithium-oxygen batteries with lithium hydroxide products, we find that a hydrogen peroxide aqueous solution added in the electrolyte can effectively promote the decomposition of lithium hydroxide compounds at the ultralow charge potential on a catalyst-free Ketjen Black-based cathode. Furthermore, for non-aqueous lithium-oxygen batteries with lithium peroxide products, we introduce a urea hydrogen peroxide, chelating hydrogen peroxide without any water in the organic, as an electrolyte additive in lithium-oxygen batteries with a lithium metal anode and succeed in the realization of the low charge potential of ~3.26 V, which is among the best levels reported. In addition, the undesired water generally accompanying hydrogen peroxide solutions is circumvented to protect the lithium metal anode and ensure good battery cycling stability. Our results should provide illuminating insights into approaches to enhancing lithium-oxygen batteries.

Ultrafast fluxional exchange dynamics in electrolyte solvation sheath of lithium ion battery.

PubMed

Lee, Kyung-Koo; Park, Kwanghee; Lee, Hochan; Noh, Yohan; Kossowska, Dorota; Kwak, Kyungwon; Cho, Minhaeng

2017-03-08

Lithium cation is the charge carrier in lithium-ion battery. Electrolyte solution in lithium-ion battery is usually based on mixed solvents consisting of polar carbonates with different aliphatic chains. Despite various experimental evidences indicating that lithium ion forms a rigid and stable solvation sheath through electrostatic interactions with polar carbonates, both the lithium solvation structure and more importantly fluctuation dynamics and functional role of carbonate solvent molecules have not been fully elucidated yet with femtosecond vibrational spectroscopic methods. Here we investigate the ultrafast carbonate solvent exchange dynamics around lithium ions in electrolyte solutions with coherent two-dimensional infrared spectroscopy and find that the time constants of the formation and dissociation of lithium-ion···carbonate complex in solvation sheaths are on a picosecond timescale. We anticipate that such ultrafast microscopic fluxional processes in lithium-solvent complexes could provide an important clue to understanding macroscopic mobility of lithium cation in lithium-ion battery on a molecular level.

Solid-state lithium battery

DOEpatents

Ihlefeld, Jon; Clem, Paul G; Edney, Cynthia; Ingersoll, David; Nagasubramanian, Ganesan; Fenton, Kyle Ross

2014-11-04

The present invention is directed to a higher power, thin film lithium-ion electrolyte on a metallic substrate, enabling mass-produced solid-state lithium batteries. High-temperature thermodynamic equilibrium processing enables co-firing of oxides and base metals, providing a means to integrate the crystalline, lithium-stable, fast lithium-ion conductor lanthanum lithium tantalate (La.sub.1/3-xLi.sub.3xTaO.sub.3) directly with a thin metal foil current collector appropriate for a lithium-free solid-state battery.

Lithium vanadium oxides (Li1+xV3O8) as cathode materials in lithium-ion batteries for soldier portable power systems

NASA Astrophysics Data System (ADS)

Wang, Gaojun; Chen, Linfeng; Mathur, Gyanesh N.; Varadan, Vijay K.

2011-04-01

Improving soldier portable power systems is very important for saving soldiers' lives and having a strategic advantage in a war. This paper reports our work on synthesizing lithium vanadium oxides (Li1+xV3O8) and developing their applications as the cathode (positive) materials in lithium-ion batteries for soldier portable power systems. Two synthesizing methods, solid-state reaction method and sol-gel method, are used in synthesizing lithium vanadium oxides, and the chemical reaction conditions are determined mainly based on thermogravimetric and differential thermogravimetric (TG-DTG) analysis. The synthesized lithium vanadium oxides are used as the active positive materials in the cathodes of prototype lithium-ion batteries. By using the new solid-state reaction technique proposed in this paper, lithium vanadium oxides can be synthesized at a lower temperature and in a shorter time, and the synthesized lithium vanadium oxide powders exhibit good crystal structures and good electrochemical properties. In the sol-gel method, different lithium source materials are used, and it is found that lithium nitrate (LiNO3) is better than lithium carbonate (Li2CO3) and lithium hydroxide (LiOH). The lithium vanadium oxides synthesized in this work have high specific charge and discharge capacities, which are helpful for reducing the sizes and weights, or increasing the power capacities, of soldier portable power systems.

What we need to know about the effect of lithium on the kidney.

PubMed

Gong, Rujun; Wang, Pei; Dworkin, Lance

2016-12-01

Lithium has been a valuable treatment for bipolar affective disorders for decades. Clinical use of lithium, however, has been problematic due to its narrow therapeutic index and concerns for its toxicity in various organ systems. Renal side effects associated with lithium include polyuria, nephrogenic diabetes insipidus, proteinuria, distal renal tubular acidosis, and reduction in glomerular filtration rate. Histologically, chronic lithium nephrotoxicity is characterized by interstitial nephritis with microcyst formation and occasional focal segmental glomerulosclerosis. Nevertheless, this type of toxicity is uncommon, with the strongest risk factors being high serum levels of lithium and longer time on lithium therapy. In contrast, in experimental models of acute kidney injury and glomerular disease, lithium has antiproteinuric, kidney protective, and reparative effects. This paradox may be partially explained by lower lithium doses and short duration of therapy. While long-term exposure to higher psychiatric doses of lithium may be nephrotoxic, short-term low dose of lithium may be beneficial and ameliorate kidney and podocyte injury. Mechanistically, lithium targets glycogen synthase kinase-3β, a ubiquitously expressed serine/threonine protein kinase implicated in the processes of tissue injury, repair, and regeneration in multiple organ systems, including the kidney. Future studies are warranted to discover the exact "kidney-protective dose" of lithium and test the effects of low-dose lithium on acute and chronic kidney disease in humans. Copyright © 2016 the American Physiological Society.

What we need to know about the effect of lithium on the kidney

PubMed Central

Gong, Rujun; Wang, Pei

2016-01-01

Lithium has been a valuable treatment for bipolar affective disorders for decades. Clinical use of lithium, however, has been problematic due to its narrow therapeutic index and concerns for its toxicity in various organ systems. Renal side effects associated with lithium include polyuria, nephrogenic diabetes insipidus, proteinuria, distal renal tubular acidosis, and reduction in glomerular filtration rate. Histologically, chronic lithium nephrotoxicity is characterized by interstitial nephritis with microcyst formation and occasional focal segmental glomerulosclerosis. Nevertheless, this type of toxicity is uncommon, with the strongest risk factors being high serum levels of lithium and longer time on lithium therapy. In contrast, in experimental models of acute kidney injury and glomerular disease, lithium has antiproteinuric, kidney protective, and reparative effects. This paradox may be partially explained by lower lithium doses and short duration of therapy. While long-term exposure to higher psychiatric doses of lithium may be nephrotoxic, short-term low dose of lithium may be beneficial and ameliorate kidney and podocyte injury. Mechanistically, lithium targets glycogen synthase kinase-3β, a ubiquitously expressed serine/threonine protein kinase implicated in the processes of tissue injury, repair, and regeneration in multiple organ systems, including the kidney. Future studies are warranted to discover the exact “kidney-protective dose” of lithium and test the effects of low-dose lithium on acute and chronic kidney disease in humans. PMID:27122541

49 CFR 173.185 - Lithium cells and batteries.

Code of Federal Regulations, 2012 CFR

2012-10-01

... Class 7 § 173.185 Lithium cells and batteries. (a) Cells and batteries. A lithium cell or battery, including a lithium polymer cell or battery and a lithium-ion cell or battery, must conform to all of the... 49 Transportation 2 2012-10-01 2012-10-01 false Lithium cells and batteries. 173.185 Section 173...

49 CFR 173.185 - Lithium cells and batteries.

Code of Federal Regulations, 2013 CFR

2013-10-01

... Class 7 § 173.185 Lithium cells and batteries. (a) Cells and batteries. A lithium cell or battery, including a lithium polymer cell or battery and a lithium-ion cell or battery, must conform to all of the... 49 Transportation 2 2013-10-01 2013-10-01 false Lithium cells and batteries. 173.185 Section 173...

49 CFR 173.185 - Lithium cells and batteries.

Code of Federal Regulations, 2011 CFR

2011-10-01

... Class 7 § 173.185 Lithium cells and batteries. (a) Cells and batteries. A lithium cell or battery, including a lithium polymer cell or battery and a lithium-ion cell or battery, must conform to all of the... 49 Transportation 2 2011-10-01 2011-10-01 false Lithium cells and batteries. 173.185 Section 173...

49 CFR 173.185 - Lithium cells and batteries.

Code of Federal Regulations, 2010 CFR

2010-10-01

... Class 7 § 173.185 Lithium cells and batteries. (a) Cells and batteries. A lithium cell or battery, including a lithium polymer cell or battery and a lithium-ion cell or battery, must conform to all of the... 49 Transportation 2 2010-10-01 2010-10-01 false Lithium cells and batteries. 173.185 Section 173...

Lithium toxicity in a neonate owing to false elevation of blood lithium levels caused by contamination in a lithium heparin container: case report and review of the literature.

PubMed

Arslan, Zainab; Athiraman, Naveen K; Clark, Simon J

2016-08-01

Lithium toxicity in a neonate can occur owing to antenatal exposure as a result of maternal treatment for psychiatric illnesses. False elevation of lithium levels has been reported in the paediatric population when the sample was mistakenly collected in a lithium heparin container. A term, male infant was born to a mother who was on lithium treatment for a psychiatric illness. On day 1, the infant was jittery, had a poor suck with difficulties in establishing feeds. Blood taken from the infant approximately 8 hours after birth demonstrated a lithium level of 4.9 mmol/L (adult toxic level w1.5 mmol/L). However, the sample for lithium levels was sent in a lithium heparin container and the probability of false elevation was considered. He was closely monitored in the neonatal intensive care unit and his hydration was optimised with intravenous fluids. Clinically, he remained well and commenced feeding, and his jitteriness had decreased the following day. A repeat blood lithium level, collected in a gel container, was only 0.4 mmol/L. The initially raised lithium level was owing to contamination from the lithium heparin container.

Effect of lithium in the DIII-D SOL and plasma-facing surfaces

NASA Astrophysics Data System (ADS)

Jackson, G. L.; Chrobak, C. P.; McLean, A. G.; Maingi, R.; Mansfield, D. K.; Roquemore, A. L.; Diwakar, P.; Hassanein, A.; Lietz, A.; Rudakov, D. L.; Sizyuk, T.; Tripathi, J.

2015-08-01

Lithium has been introduced into the DIII-D tokamak, and migration and retention in graphite have been characterized since no lithium was present in DIII-D initially. A new regime with an enhanced edge electron pedestal and H98y2 ⩽ 2 has been obtained with lithium. Lithium deposition was not uniform, but rather preferentially deposited near the strike points, consistent with previous 13C experiments. Edge visible lithium light (LiI) remained well above the previous background during the entire DIII-D campaign, decaying with a 2600 plasma-second e-fold, but plasma performance was only affected on the discharge with lithium injection. Lithium injection demonstrated the capability of reducing hydrogenic recycling, density, and ELM frequency. Graphite and silicon samples were exposed to a lithium-injected discharge, using the DiMES system and then removed for ex-situ analysis. The deposited lithium layer remained detectable to a depth up to 1 μm.

Light-assisted delithiation of lithium iron phosphate nanocrystals towards photo-rechargeable lithium ion batteries

PubMed Central

Paolella, Andrea; Faure, Cyril; Bertoni, Giovanni; Marras, Sergio; Guerfi, Abdelbast; Darwiche, Ali; Hovington, Pierre; Commarieu, Basile; Wang, Zhuoran; Prato, Mirko; Colombo, Massimo; Monaco, Simone; Zhu, Wen; Feng, Zimin; Vijh, Ashok; George, Chandramohan; Demopoulos, George P.; Armand, Michel; Zaghib, Karim

2017-01-01

Recently, intensive efforts are dedicated to convert and store the solar energy in a single device. Herein, dye-synthesized solar cell technology is combined with lithium-ion materials to investigate light-assisted battery charging. In particular we report the direct photo-oxidation of lithium iron phosphate nanocrystals in the presence of a dye as a hybrid photo-cathode in a two-electrode system, with lithium metal as anode and lithium hexafluorophosphate in carbonate-based electrolyte; a configuration corresponding to lithium ion battery charging. Dye-sensitization generates electron–hole pairs with the holes aiding the delithiation of lithium iron phosphate at the cathode and electrons utilized in the formation of a solid electrolyte interface at the anode via oxygen reduction. Lithium iron phosphate acts effectively as a reversible redox agent for the regeneration of the dye. Our findings provide possibilities in advancing the design principles for photo-rechargeable lithium ion batteries. PMID:28393912

Light-assisted delithiation of lithium iron phosphate nanocrystals towards photo-rechargeable lithium ion batteries

NASA Astrophysics Data System (ADS)

Paolella, Andrea; Faure, Cyril; Bertoni, Giovanni; Marras, Sergio; Guerfi, Abdelbast; Darwiche, Ali; Hovington, Pierre; Commarieu, Basile; Wang, Zhuoran; Prato, Mirko; Colombo, Massimo; Monaco, Simone; Zhu, Wen; Feng, Zimin; Vijh, Ashok; George, Chandramohan; Demopoulos, George P.; Armand, Michel; Zaghib, Karim

2017-04-01

Recently, intensive efforts are dedicated to convert and store the solar energy in a single device. Herein, dye-synthesized solar cell technology is combined with lithium-ion materials to investigate light-assisted battery charging. In particular we report the direct photo-oxidation of lithium iron phosphate nanocrystals in the presence of a dye as a hybrid photo-cathode in a two-electrode system, with lithium metal as anode and lithium hexafluorophosphate in carbonate-based electrolyte; a configuration corresponding to lithium ion battery charging. Dye-sensitization generates electron-hole pairs with the holes aiding the delithiation of lithium iron phosphate at the cathode and electrons utilized in the formation of a solid electrolyte interface at the anode via oxygen reduction. Lithium iron phosphate acts effectively as a reversible redox agent for the regeneration of the dye. Our findings provide possibilities in advancing the design principles for photo-rechargeable lithium ion batteries.

Light-assisted delithiation of lithium iron phosphate nanocrystals towards photo-rechargeable lithium ion batteries.

PubMed

Paolella, Andrea; Faure, Cyril; Bertoni, Giovanni; Marras, Sergio; Guerfi, Abdelbast; Darwiche, Ali; Hovington, Pierre; Commarieu, Basile; Wang, Zhuoran; Prato, Mirko; Colombo, Massimo; Monaco, Simone; Zhu, Wen; Feng, Zimin; Vijh, Ashok; George, Chandramohan; Demopoulos, George P; Armand, Michel; Zaghib, Karim

2017-04-10

Recently, intensive efforts are dedicated to convert and store the solar energy in a single device. Herein, dye-synthesized solar cell technology is combined with lithium-ion materials to investigate light-assisted battery charging. In particular we report the direct photo-oxidation of lithium iron phosphate nanocrystals in the presence of a dye as a hybrid photo-cathode in a two-electrode system, with lithium metal as anode and lithium hexafluorophosphate in carbonate-based electrolyte; a configuration corresponding to lithium ion battery charging. Dye-sensitization generates electron-hole pairs with the holes aiding the delithiation of lithium iron phosphate at the cathode and electrons utilized in the formation of a solid electrolyte interface at the anode via oxygen reduction. Lithium iron phosphate acts effectively as a reversible redox agent for the regeneration of the dye. Our findings provide possibilities in advancing the design principles for photo-rechargeable lithium ion batteries.

Lithium-Based High Energy Density Flow Batteries

NASA Technical Reports Server (NTRS)

Bugga, Ratnakumar V. (Inventor); West, William C. (Inventor); Kindler, Andrew (Inventor); Smart, Marshall C. (Inventor)

2014-01-01

Systems and methods in accordance with embodiments of the invention implement a lithium-based high energy density flow battery. In one embodiment, a lithium-based high energy density flow battery includes a first anodic conductive solution that includes a lithium polyaromatic hydrocarbon complex dissolved in a solvent, a second cathodic conductive solution that includes a cathodic complex dissolved in a solvent, a solid lithium ion conductor disposed so as to separate the first solution from the second solution, such that the first conductive solution, the second conductive solution, and the solid lithium ionic conductor define a circuit, where when the circuit is closed, lithium from the lithium polyaromatic hydrocarbon complex in the first conductive solution dissociates from the lithium polyaromatic hydrocarbon complex, migrates through the solid lithium ionic conductor, and associates with the cathodic complex of the second conductive solution, and a current is generated.

Enantioselective Effect of Flurbiprofen on Lithium Disposition in Rats.

PubMed

Uwai, Yuichi; Matsumoto, Masashi; Kawasaki, Tatsuya; Nabekura, Tomohiro

2017-01-01

Lithium is administered for treating bipolar disorders and is mainly excreted into urine. Nonsteroidal anti-inflammatory drugs inhibit this process. In this study, we examined the enantioselective effect of flurbiprofen on the disposition of lithium in rats. Pharmacokinetic experiments with lithium were performed. Until 60 min after the intravenous administration of lithium chloride at 30 mg/kg as a bolus, 17.8% of lithium injected was recovered into the urine. Its renal clearance was calculated to be 1.62 mL/min/kg. Neither creatinine clearance (Ccr) nor pharmacokinetics of lithium was affected by the simultaneous injection of (R)-flurbiprofen at 20 mg/kg. (S)-flurbiprofen impaired the renal function and interfered with the urinary excretion of lithium. The ratio of renal clearance of lithium to Ccr was decreased by the (S)-enantiomer. This study clarified that the (S)-flurbiprofen but not (R)-flurbiprofen inhibited the renal excretion of lithium in rats. © 2017 S. Karger AG, Basel.

Dendrite preventing separator for secondary lithium batteries

NASA Technical Reports Server (NTRS)

Shen, David H. (Inventor); Surampudi, Subbarao (Inventor); Huang, Chen-Kuo (Inventor); Halpert, Gerald (Inventor)

1993-01-01

Dendrites are prevented from shorting a secondary lithium battery by use of a first porous separator, such as porous polypropylene, adjacent to the lithium anode that is unreactive with lithium and a second porous fluoropolymer separator between the cathode and the first separator, such as polytetrafluoroethylene, that is reactive with lithium. As the tip of a lithium dendrite contacts the second separator, an exothermic reaction occurs locally between the lithium dendrite and the fluoropolymer separator. This results in the prevention of the dendrite propagation to the cathode.

Dendrite preventing separator for secondary lithium batteries

NASA Technical Reports Server (NTRS)

Shen, David H. (Inventor); Surampudi, Subbarao (Inventor); Huang, Chen-Kuo (Inventor); Halpert, Gerald (Inventor)

1995-01-01

Dendrites are prevented from shorting a secondary lithium battery by use of a first porous separator such as porous polypropylene adjacent the lithium anode that is unreactive with lithium and a second porous fluoropolymer separator between the cathode and the first separator such as polytetrafluoroethylene that is reactive with lithium. As the tip of a lithium dendrite contacts the second separator, an exothermic reaction occurs locally between the lithium dendrite and the fluoropolymer separator. This results in the prevention of the dendrite propagation to the cathode.

A Survey of Low-Temperature Operational Boundaries of Navy and Marine Corps Lithium and Lithium-Ion Batteries

DTIC Science & Technology

2016-09-29

Lithium and Lithium - Ion Batteries September 29, 2016 Approved for public release; distribution is unlimited. Joseph F. parker JeFFrey W. Long Surface...Boundaries of Navy and Marine Corps Lithium and Lithium - Ion Batteries Joseph F. Parker, Jeffrey W. Long, Olga A. Baturina, and Corey T. Love Naval...U.S. Marine Corps have identified a strategic interest to operate lithium - ion batteries in cold climate regions as well as undersea and in high

Lithium compensation for full cell operation

DOEpatents

Xiao, Jie; Zheng, Jianming; Chen, Xilin; Lu, Dongping; Liu, Jun; Jiguang, Jiguang

2016-05-17

Disclosed herein are embodiments of a lithium-ion battery system comprising an anode, an anode current collector, and a layer of lithium metal in contact with the current collector, but not in contact with the anode. The lithium compensation layer dissolves into the electrolyte to compensate for the loss of lithium ions during usage of the full cell. The specific placement of the lithium compensation layer, such that there is no direct physical contact between the lithium compensation layer and the anode, provides certain advantages.

Procedures for the synthesis of ethylenediamine bisborane and ammonia borane

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ramachandran, Padi Veeraraghavan; Gagare, Pravin D.; Mistry, Hitesh

A method for synthesizing ammonia borane includes (a) preparing a reaction mixture in one or more solvents, the reaction mixture containing sodium borohydride, at least one ammonium salt, and ammonia; and (b) incubating the reaction mixture at temperatures between about 0.degree. C. to about room temperature in an ambient air environment under conditions sufficient to form ammonia borane. Methods for synthesizing ethylenediamine bisborane, and methods for dehydrogenation of ethylenediamine bisborane are also described.

Research in Biological and Medical Sciences Including Biochemistry, Communicable Disease and Immunology, Internal Medicine, Physiology, Psychiatry, Surgery, and Veterinary Medicine. Volume 1

DTIC Science & Technology

1979-09-01

and R.P. MacDermott. Antibody-dependent cell-mediated antibacterial activity of human mononuclear cells. I. K-lymphocytes and monocytes are effective...malaria research. During the reporting period, research activities have included analyses of: 1) a hemagglutination inhibition test for early detection of...radioiodination or sodium borohydride reduction. Evaluate the potential roles of activity for each protein isolated. Compare the composition of isolated

Measurement of the Isotopic Ratio of [to the tenth power]B/[to the eleventh power]B in NaBH[subscript 4] by [to the first power]H NMR

ERIC Educational Resources Information Center

Zanger, Murray; Moyna, Guillermo

2005-01-01

A study uses nuclear magnetic resonance (NMR) spectroscopy in a novel way to determine the isotopic ration between [to the tenth power]B and [to the eleventh power]B in sodium borohydride (NaBH4). The experiment provides an unusual and relatively simple means for undergraduate chemistry students to accurately measure the distribution of the two…

Proceedings of the Tri-Service Gun Tube Wear and Erosion Symposium, ARRADCOM, Dover, NJ, 29-31 March 1977

DTIC Science & Technology

1977-03-01

failure was due to the material property or plating defects . In view of the electrolyte being of a proprietary nature and inconsistencies were...rifling action along the entire length of each barrel with no major pitting or other defects . Metallographic examination of the cross-section of the...Ethylenediamine, 98% _ - 52 Sodium borohydride, 98% I _ - 1 Dimethylamine borane ( DMAE ) - - 4 Sodium hypophosphite (H120) 22.5 15 - - Lead acetate (31120

A Critical Examination of the Reaction of Pyridoxal 5-Phosphate with Human Hemoglobin Ao

DTIC Science & Technology

1989-01-01

sodium borohydride gives unacceptable levels of methemoglobin (i.e., > 10%). Excessive foaming and methemoglobin formation can be partially avoided using...a biochemical level . By using new advances in HPLC column technology, we could better determine hetero- geneity in the product mixture due solely to... diphosphoglycerate (2,3-DPG). 6 SFH, which had been stripped of 2,3-DPG, was deoxygenated with nitrogen and treated with a solution of PLP in Tris

Aqueous sodium borohydride induced thermally stable porous zirconium oxide for quick removal of lead ions

PubMed Central

Nayak, Nadiya B.; Nayak, Bibhuti B.

2016-01-01

Aqueous sodium borohydride (NaBH4) is well known for its reducing property and well-established for the development of metal nanoparticles through reduction method. In contrary, this research paper discloses the importance of aqueous NaBH4 as a precipitating agent towards development of porous zirconium oxide. The boron species present in aqueous NaBH4 play an active role during gelation as well as phase separated out in the form of boron complex during precipitation, which helps to form boron free zirconium hydroxide [Zr(OH)4] in the as-synthesized condition. Evolved in-situ hydrogen (H2) gas-bubbles also play an important role to develop as-synthesized loose zirconium hydroxide and the presence of intra-particle voids in the loose zirconium hydroxide help to develop porous zirconium oxide during calcination process. Without any surface modification, this porous zirconium oxide quickly adsorbs almost hundred percentages of toxic lead ions from water solution within 15 minutes at normal pH condition. Adsorption kinetic models suggest that the adsorption process was surface reaction controlled chemisorption. Quick adsorption was governed by surface diffusion process and the adsorption kinetic was limited by pore diffusion. Five cycles of adsorption-desorption result suggests that the porous zirconium oxide can be reused efficiently for removal of Pb (II) ions from aqueous solution. PMID:26980545

Tailorable thiolated trimethyl chitosans for covalently stabilized nanoparticles.

PubMed

Verheul, Rolf J; van der Wal, Steffen; Hennink, Wim E

2010-08-09

A novel four-step method is presented to synthesize partially thiolated trimethylated chitosan (TMC) with a tailorable degree of quaternization and thiolation. First, chitosan was partially N-carboxylated with glyoxylic acid and sodium borohydride. Next, the remaining amines were quantitatively dimethylated with formaldehyde and sodium borohydride and then quaternized with iodomethane in NMP. Subsequently, these partially carboxylated TMCs dissolved in water were reacted with cystamine at pH 5.5 using EDC as coupling agent. After addition of DTT and dialysis, thiolated TMCs were obtained, varying in degree of quaternization (25-54%) and degree of thiolation (5-7%), as determined with (1)H NMR and Ellman's assay. Gel permeation chromatography with light scattering detection indicated limited intermolecular cross-linking. All thiolated TMCs showed rapid oxidation to yield disulfide cross-linked TMC at pH 7.4, while the thiolated polymers were rather stable at pH 4.0. When Calu-3 cells were used, XTT and LDH cell viability tests showed a slight reduction in cytotoxicity for thiolated TMCs as compared to the nonthiolated polymers with similar DQs. Positively charged nanoparticles loaded with fluorescently labeled ovalbumin were made from thiolated TMCs and thiolated hyaluronic acid. The stability of these particles was confirmed in 0.8 M NaCl, in contrast to particles made from nonthiolated polymers that dissociated under these conditions, demonstrating that the particles were held together by intermolecular disulfide bonds.

Room temperature micro-hydrogen-generator

NASA Astrophysics Data System (ADS)

Gervasio, Don; Tasic, Sonja; Zenhausern, Frederic

A new compact and cost-effective hydrogen-gas generator has been made that is well suited for supplying hydrogen to a fuel-cell for providing base electrical power to hand-carried appliances. This hydrogen-generator operates at room temperature, ambient pressure and is orientation-independent. The hydrogen-gas is generated by the heterogeneous catalytic hydrolysis of aqueous alkaline borohydride solution as it flows into a micro-reactor. This reactor has a membrane as one wall. Using the membrane keeps the liquid in the reactor, but allows the hydrogen-gas to pass out of the reactor to a fuel-cell anode. Aqueous alkaline 30 wt% borohydride solution is safe and promotes long application life, because this solution is non-toxic, non-flammable, and is a high energy-density (≥2200 W-h per liter or per kilogram) hydrogen-storage solution. The hydrogen is released from this storage-solution only when it passes over the solid catalyst surface in the reactor, so controlling the flow of the solution over the catalyst controls the rate of hydrogen-gas generation. This allows hydrogen generation to be matched to hydrogen consumption in the fuel-cell, so there is virtually no free hydrogen-gas during power generation. A hydrogen-generator scaled for a system to provide about 10 W electrical power is described here. However, the technology is expected to be scalable for systems providing power spanning from 1 W to kW levels.