Polysilicic acid gel method derived V2O5/SiO2 composite materials: Synthesis and characterization

NASA Astrophysics Data System (ADS)

Wang, Dawei; Zhou, Linzong; Feng, Xiaofei; Zhao, Ning; Yang, Bin

2017-01-01

The V2O5/SiO2 composite was prepared by a sol-gel method followed a sintering procedure. The low-cost Na2SiO3•9H2O was used as silicon source, while NH4VO3 was used as vanadium source. By adding NH4VO3 to Na2SiO3 solution and adjusting the mixture's pH with saturated (NH4)2SO4 solution the polysilicic acid gel was formed to give a homogeneous gel composite with VO3-well-distributed in it. The gel composite was dried at 100 °C to give the xerogel, then the xerogel was calcined in air to obtain the V2O5/SiO2 composite. The V2O5/SiO2 composites were characterized by SEM analysis, FT-IR spectroscopy and powder X-ray diffractions.

Cesium and strontium ion exchange on the framework titanium silicate M2Ti2O3SiO4.nH2O (M = H, Na).

PubMed

Solbrå, S; Allison, N; Waite, S; Mikhalovsky, S V; Bortun, A I; Bortun, L N; Clearfield, A

2001-02-01

The ion exchange properties of the titanium silicate, M2Ti2O3SiO4.nH2O (M = H, Na), toward stable and radioactive 137Cs+ and 89Sr2+, have been examined. By studying the cesium and strontium uptake in the presence of NaNO3, CaCl2, NaOH, and HNO3 (in the range of 0.01-6 M) the sodium titanium silicate was found to be an efficient Cs+ ion exchanger in acid, neutral, and alkaline media and an efficient Sr2+ ion exchanger in neutral and alkaline media, which makes it promising for treatment of contaminated environmental media and biological systems.

Structural Evaluation of 5,5'-Bis(naphth-2-yl)-2,2'-bithiophene in Organic Field-Effect Transistors with n-Octadecyltrichlorosilane Coated SiO2 Gate Dielectric.

PubMed

Lauritzen, Andreas E; Torkkeli, Mika; Bikondoa, Oier; Linnet, Jes; Tavares, Luciana; Kjelstrup-Hansen, Jakob; Knaapila, Matti

2018-05-25

We report on the structure and morphology of 5,5'-bis(naphth-2-yl)-2,2'-bithiophene (NaT2) films in bottom-contact organic field-effect transistors (OFETs) with octadecyltrichlorosilane (OTS) coated SiO 2 gate dielectric, characterized by atomic force microscopy (AFM), grazing-incidence X-ray diffraction (GIXRD), and electrical transport measurements. Three types of devices were investigated with the NaT2 thin-film deposited either on (1) pristine SiO 2 (corresponding to higher surface energy, 47 mJ/m 2 ) or on OTS deposited on SiO 2 under (2) anhydrous or (3) humid conditions (corresponding to lower surface energies, 20-25 mJ/m 2 ). NaT2 films grown on pristine SiO 2 form nearly featureless three-dimensional islands. NaT2 films grown on OTS/SiO 2 deposited under anhydrous conditions form staggered pyramid islands where the interlayer spacing corresponds to the size of the NaT2 unit cell. At the same time, the grain size measured by AFM increases from hundreds of nanometers to micrometers and the crystal size measured by GIXRD from 30 nm to more than 100 nm. NaT2 on OTS/SiO 2 deposited under humid conditions also promotes staggered pyramids but with smaller crystals 30-80 nm. The NaT2 unit cell parameters in OFETs differ 1-2% from those in bulk. Carrier mobilities tend to be higher for NaT2 layers on SiO 2 (2-3 × 10 -4 cm 2 /(V s)) compared to NaT2 on OTS (2 × 10 -5 -1 × 10 -4 cm 2 /(V s)). An applied voltage does not influence the unit cell parameters when probed by GIXRD in operando.

Optical temperature sensing of NaYbF4: Tm3+@SiO2 core-shell micro-particles induced by infrared excitation.

PubMed

Wang, Xiangfu; Zheng, Jin; Xuan, Yan; Yan, Xiaohong

2013-09-09

NaYbF(4):Tm3+@SiO(2) core-shell micro-particles were synthesized by a hydrothermal method and subsequent ultrasonic coating process. Optical temperature sensing has been observed in NaYbF4: Tm(3+)@SiO(2)core-shell micro-particles with a 980 nm infrared laser as excitation source.The fluorescence intensity ratios, optical temperature sensitivity, and temperature dependent population re-distribution ability from the thermally coupled (1)D(2)/(1)G(4) and (3)F(2) /(3)H(4) levels of the Tm(3+) ion have been analyzed as a function of temperature in the range of 100~700 K in order to check its availability as a optical temperature sensor. A better behavior as a lowtemperature sensor has been obtained with a minimum sensitivity of 5.4 × 10(-4) K(-1) at 430 K. It exhibits temperature induced population re-distribution from (1)D(2) /(1)G(4) thermally coupled levels at higher temperature range.

Investigating the influence of Na+ and Sr2+ on the structure and solubility of SiO2-TiO2-CaO-Na2O/SrO bioactive glass.

PubMed

Li, Y; Placek, L M; Coughlan, A; Laffir, F R; Pradhan, D; Mellott, N P; Wren, A W

2015-02-01

This study was conducted to determine the influence that network modifiers, sodium (Na+) and strontium (Sr2+), have on the solubility of a SiO2-TiO2-CaO-Na2O/SrO bioactive glass. Glass characterization determined each composition had a similar structure, i.e. bridging to non-bridging oxygen ratio determined by X-ray photoelectron spectroscopy. Magic angle spinning nuclear magnetic resonance (MAS-NMR) confirmed structural similarities as each glass presented spectral shifts between -84 and -85 ppm. Differential thermal analysis and hardness testing revealed higher glass transition temperatures (Tg 591-760 °C) and hardness values (2.4-6.1 GPa) for the Sr2+ containing glasses. Additionally the Sr2+ (~250 mg/L) containing glasses displayed much lower ion release rates than the Na+ (~1,200 mg/L) containing glass analogues. With the reduction in ion release there was an associated reduction in solution pH. Cytotoxicity and cell adhesion studies were conducted using MC3T3 Osteoblasts. Each glass did not significantly reduce cell numbers and osteoblasts were found to adhere to each glass surface.

Reduction Mechanisms of Cu2+-Doped Na2O-Al2O3-SiO2 Glasses during Heating in H2 Gas.

PubMed

Nogami, Masayuki; Quang, Vu Xuan; Ohki, Shinobu; Deguchi, Kenzo; Shimizu, Tadashi

2018-01-25

Controlling valence state of metal ions that are doped in materials has been widely applied for turning optical properties. Even though hydrogen has been proven effective to reduce metal ions because of its strong reducing capability, few comprehensive studies focus on practical applications because of the low diffusion rate of hydrogen in solids and the limited reaction near sample surfaces. Here, we investigated the reactions of hydrogen with Cu 2+ -doped Na 2 O-Al 2 O 3 -SiO 2 glass and found that a completely different reduction from results reported so far occurs, which is dominated by the Al/Na concentration ratio. For Al/Na < 1, Cu 2+ ions were reduced via hydrogen to metallic Cu, distributing in glass body. For Al/Na > 1, on the other hand, the reduction of Cu 2+ ions occurred simultaneously with the formation of OH bonds, whereas the reduced Cu metal moved outward and formed a metallic film on glass surface. The NMR and Fourier transform infrared results indicated that the Cu 2+ ions were surrounded by Al 3+ ions that formed AlO 4 , distorted AlO 4 , and AlO 5 units. The diffused H 2 gas reacted with the Al-O - ···Cu + units, forming Al-OH and metallic Cu, the latter of which moved freely toward glass surface and in return enhanced H 2 diffusion.

Gels and gel-derived glasses in the system Na2O-B2O3-SiO2

NASA Technical Reports Server (NTRS)

Mukherjee, S. P.

1983-01-01

The containerless melting of high-purity multicomponent homogeneous gels and gel monoliths offers a unique approach to making ultrapure multicomponent optical glasses in the reduced gravity environment of space. Procedures for preparing and characterizing gels and gel-derived glasses in the system Na2O-B2O3-SiO2 are described. Preparation is based on the polymerization reactions of alkoxysilane with trimethyl borate or boric acid and a suitable sodium compound. The chemistry of the gelling process is discussed in terms of process parameters and the gel compositions. The physicochemical nature of gels prepared by three different procedures was found to be significantly different. Infrared absorption spectra indicate finite differences in the molecular structures of the different gels. The melting of the gel powders and the transformation of porous gel monoliths to transparent 'glass' without melting are described.

Synthesis of Nanoscale CaO-Al2O3-SiO2-H2O and Na2O-Al2O3-SiO2-H2O Using the Hydrothermal Method and Their Characterization

PubMed Central

Yang, Jingbin; Li, Dongxu; Fang, Yuan

2017-01-01

C-A-S-H (CaO-Al2O3-SiO2-H2O) and N-A-S-H (Na2O-Al2O3-SiO2-H2O) have a wide range of chemical compositions and structures and are difficult to separate from alkali-activated materials. Therefore, it is difficult to analyze their microscopic properties directly. This paper reports research on the synthesis of C-A-S-H and N-A-S-H particles with an average particle size smaller than 300 nm by applying the hydrothermal method. The composition and microstructure of the products with different CaO(Na2O)/SiO2 ratios and curing conditions were characterized using XRD, the RIR method, FTIR, SEM, TEM, and laser particle size analysis. The results showed that the C-A-S-H system products with a low CaO/SiO2 ratio were mainly amorphous C-A-S-H gels. With an increase in the CaO/SiO2 ratio, an excess of Ca(OH)2 was observed at room temperature, while in a high-temperature reaction system, katoite, C4AcH11, and other crystallized products were observed. The katoite content was related to the curing temperature and the content of Ca(OH)2 and it tended to form at a high-temperature and high-calcium environment, and an increase in the temperature renders the C-A-S-H gels more compact. The main products of the N-A-S-H system at room temperature were amorphous N-A-S-H gels and a small amount of sodalite. An increase in the curing temperature promoted the formation of the crystalline products faujasite and zeolite-P. The crystallization products consisted of only zeolite-P in the high-temperature N-A-S-H system and its content were stable above 70%. An increase in the Na2O/SiO2 ratio resulted in more non-bridging oxygen and the TO4 was more isolated in the N-A-S-H structure. The composition and microstructure of the C-A-S-H and N-A-S-H system products synthesized by the hydrothermal method were closely related to the ratio of the raw materials and the curing conditions. The results of this study increase our understanding of the hydration products of alkali-activated materials. PMID

Structural study of Na2O-B2O3-SiO2 glasses from molecular simulations using a polarizable force field.

PubMed

Pacaud, Fabien; Delaye, Jean-Marc; Charpentier, Thibault; Cormier, Laurent; Salanne, Mathieu

2017-10-28

Sodium borosilicate glasses Na 2 O-B 2 O 3 -SiO 2 (NBS) are complex systems from a structural point of view. Three main building units are present: tetrahedral SiO 4 and BO 4 (B IV ) and triangular BO 3 (B III ). One of the salient features of these compounds is the change of the B III /B IV ratio with the alkali concentration, which is very difficult to capture in force fields-based molecular dynamics simulations. In this work, we develop a polarizable force field that is able to reproduce the boron coordination and more generally the structure of several NBS systems in the glass and in the melt. The parameters of the potential are fitted from density functional theory calculations only, in contrast with the existing empirical potentials for NBS systems. This ensures a strong improvement on the transferability of the parameters from one composition to another. Using this new force field, the structure of NBS systems is validated against neutron diffraction and nuclear magnetic resonance experiments. A special focus is given to the distribution of B III /B IV with respect to the composition and the temperature.

Compositional dependence of bioactivity of glasses in the system Na2O-K2O-MgO-CaO-B2O3-P2O5-SiO2.

PubMed

Brink, M; Turunen, T; Happonen, R P; Yli-Urpo, A

1997-10-01

The bioactivity, i.e., bone-bonding ability, of 26 glasses in the system Na2O-K2O-MgO-CaO-B2O3-P2O5-SiO2 was studied in vivo. This investigation of bioactivity was performed to establish the compositional dependence of bioactivity, and enabled a model to be developed that describes the relation between reactions in vivo and glass composition. Reactions in vivo were investigated by inserting glass implants into rabbit tibia for 8 weeks. The glasses and the surrounding tissue were examined using scanning electron microscopy (SEM), light microscopy, and energy-dispersive X-ray analysis (EDXA). For most of the glasses containing < 59 mol % SiO2, SEM and EDXA showed two distinct layers at the glass surface after implantation, one silica-rich and another containing calcium phosphate. The build-up of these layers in vivo was taken as a sign of bioactivity. The in vivo experiments showed that glasses in the investigated system are bioactive when they contain 14-30 mol % alkali oxides, 14-30 mol % alkaline earth oxides, and < 59 mol % SiO2. Glasses containing potassium and magnesium bonded to bone in a similar way as bioactive glasses developed so far.

Experimental and thermodynamic study of heterogeneous and homogeneous equilibria in the system NaAlSiO4-SiO2

NASA Astrophysics Data System (ADS)

Waterwiese, Tanja; Chatterjee, Niranjan D.; Dierdorf, Ivana; Göttlicher, Jörg; Kroll, Herbert

1995-08-01

Internally consistent thermodynamic datasets available at present call for a further improvement of the data for nepheline (Holland and Powell 1988; Berman 1991). Because nepheline is a common rock-forming mineral, an attempt has been made to improve on the present state of knowledge of its thermodynamic properties. To achieve that goal, two heterogeneous reactions involving nepheline, albite, jadeite and a-quartz in the system NaAlSiO4-SiO2 have been reversed by long duration runs in the range 460 ≤ T(°C) ≤ 960 and 10 ≤ P(kbar) ≤ 22. Given sufficiently long run times, the albite run products approach internal equilibrium with respect to their Al,Si order-disorder states. Using appropriate thermochemical, thermophysical, and volumetric data, Landau expansion for albite, and the relevant reaction reversals, a refined thermodynamic dataset (ΔfH{i/0} and S{i/0}) has been derived for nepheline, jadeite, a-quartz, albite, and monalbite. Our refined data agree very well with their calorimetric counterparts, but have smaller uncertainties. The refined dataset for ΔfH{i/0} and S{i/0}, including their uncertainties and correlation, help generate the NaAlSiO4-SiO2 phase diagram including 2a confidence interval for each P-T curve (Fig. 5).

Kinetics of Valeric Acid Ketonization and Ketenization in Catalytic Pyrolysis on Nanosized SiO2 , γ-Al2 O3 , CeO2 /SiO2 , Al2 O3 /SiO2 and TiO2 /SiO2.

PubMed

Kulyk, Kostiantyn; Palianytsia, Borys; Alexander, John D; Azizova, Liana; Borysenko, Mykola; Kartel, Mykola; Larsson, Mats; Kulik, Tetiana

2017-07-19

Valeric acid is an important renewable platform chemical that can be produced efficiently from lignocellulosic biomass. Upgrading of valeric acid by catalytic pyrolysis has the potential to produce value added biofuels and chemicals on an industrial scale. Understanding the different mechanisms involved in the thermal transformations of valeric acid on the surface of nanometer-sized oxides is important for the development of efficient heterogeneously catalyzed pyrolytic conversion techniques. In this work, the thermal decomposition of valeric acid on the surface of nanoscale SiO 2 , γ-Al 2 O 3 , CeO 2 /SiO 2 , Al 2 O 3 /SiO 2 and TiO 2 /SiO 2 has been investigated by temperature-programmed desorption mass spectrometry (TPD MS). Fourier transform infrared spectroscopy (FTIR) has also been used to investigate the structure of valeric acid complexes on the oxide surfaces. Two main products of pyrolytic conversion were observed to be formed depending on the nano-catalyst used-dibutylketone and propylketene. Mechanisms of ketene and ketone formation from chemisorbed fragments of valeric acid are proposed and the kinetic parameters of the corresponding reactions were calculated. It was found that the activation energy of ketenization decreases in the order SiO 2 >γ-Al 2 O 3 >TiO 2 /SiO 2 >Al 2 O 3 /SiO 2 , and the activation energy of ketonization decreases in the order γ-Al 2 O 3 >CeO 2 /SiO 2 . Nano-oxide CeO 2 /SiO 2 was found to selectively catalyze the ketonization reaction. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Synthesis of Radioisotope Mn-56@SiO2, Sm-153@SiO2, and Dy-165@SiO2 Hybrid Nanoparticles for Use as Radiotracer.

PubMed

Seo, Sang-Ei; Kang, Yun Ok; Jung, Sung-Hee; Choi, Seong-Ho

2015-09-01

Radioisotope hybrid nanoparticles (NPs) of Mn-56@SiO2, Sm-153@SiO2, and Dy-165@SiO2 were synthesized by neutron irradiation of Mn-55@SiO2, Sm-150@SiO2, and Dy-163@SiO2 NPs respectively using the HANARO research reactor. The Mn-55@SiO2, Sm-150@SiO2, and Dy-163@SiO2 NPs were synthesized by calcination in air flow at 500 degrees C for 8 h of the hybrid NPs that has been prepared by the sol-gel reaction of tetraethyl silicate in the presence of the complex precursors. Mn-55, Sm-150, and Dy-163 were selected for use as radiotracers were selected because these elements can be easily gamma-activated by neutrons (activation limits: 1 picogram (Dy), 1-10 picogram (Mn), 10-100 picogram (Sm)). The successful synthesis of the radioisotope hybrid NPs was confirmed by Transmission Electron Microscopy (TEM), Energy Dispersive X-ray Spectrometry (EDS), Scanning Electron Microscopy (SEM), and Gamma Spectroscopy analysis. The synthesized the radioisotope hybrid NPs could be used as radiotracers in the scientific, environmental, engineering, and industrial fields.

Nanocomposite dielectrics in PbO-BaO-Na2O-Nb2O5-SiO2 system with high breakdown strength for high voltage capacitor applications.

PubMed

Zhang, Qingmeng; Luo, Jun; Tang, Qun; Han, Dongfang; Zhou, Yi; Du, Jun

2012-11-01

Nanocomposite dielectrics in 6PbO-4BaO-20Na2O-40Nb2O5-30SiO2 system were prepared via melt-quenching followed by controlled crystallization. X-ray diffraction studies reveal that Pb2Nb2O7, Ba,NaNb5O15, NaNbO3 and PbNb2O6 phases are formed from the as-quenched glass annealed in temperature range from 700 degrees C to 850 degrees C. Ba2NaNb5O15, Pb2Nb2O7 crystallizes at 700 degrees C and then Pb2Nb2O7 disappears at 850 degrees C, while PbNb2O6 and NaNbO3 are formed at 850 degrees C. Microstructural observation shows that the crystallized particles are nanometer-sized and randomly distributed with glass matrix being often found at grain boundaries. The dielectric constant of the nanocomposites formed at different crystallization temperatures shows good frequency and electric field stability. The breakdown strength is slightly decreased when the glass-ceramics thickness is varied from 1 mm to 4 mm. The corresponding energy density could reach 2.96 J/cm3 with a breakdown strength of 58 kV/mm for thickness of 1 mm.

The first Fe-based Na+-ion cathode with two distinct types of polyanions: Fe 3P 5SiO 19

DOE PAGES

Kan, W. H.; Huq, A.; Manthiram, A.

2015-05-15

We report the synthesis, structure, and electrochemistry of the first Na +-ion cathode with two distinct types of polyanions: Fe 3P 5SiO 19. The Fe-based cathode has a reversible capacity of ca. 70 mAh g -1; ca. 1.7 Na + ions per formula can be inserted/extracted at an average voltage of 2.5 V versus Na +/Na.

Comparative study of three magnetic nano-particles (FeSO4, FeSO4/SiO2, FeSO4/SiO2/TiO2) in plasmid DNA extraction.

PubMed

Rahnama, H; Sattarzadeh, A; Kazemi, F; Ahmadi, N; Sanjarian, F; Zand, Z

2016-11-15

Recent updates on Magnetic Nano-Particles (MNPs) based separation of nucleic acids have received more attention due to their easy manipulation, simplicity, ease of automation and cost-effectiveness. It has been indicated that DNA molecules absorb on solid surfaces via hydrogen-bonding, and hydrophobic and electrostatic interactions. These properties highly depend on the surface condition of the solid support. Therefore, surface modification of MNPs may enhance their functionality and specification. In the present study, we functionalized Fe3O4 nano-particle surface utilizing SiO2 and TiO2 layer as Fe3O4/SiO2 and Fe3O4/SiO2/TiO2 and then compare their functionality in the adsorption of plasmid DNA molecules with the naked Fe3O4 nano-particles. The result obtained showed that the purity and amount of DNA extracted by Fe3O4 coated by SiO2 or SiO2/TiO2 were higher than the naked Fe3O4 nano-particles. Furthermore, we obtained pH 8 and 1.5 M NaCl as an optimal condition for desorption of DNA from MNPs. The result further showed that, 0.2 mg nano-particle and 10 min at 55 °C are the optimal conditions for DNA desorption from nano-particles. In conclusion, we recommended Fe3O4/SiO2/TiO2 as a new MNP for separation of DNA molecules from biological sources. Copyright © 2016 Elsevier Inc. All rights reserved.

Adsorption of proteins on γ-Fe2O3 and γ-Fe2O3/SiO2 magnetic materials

NASA Astrophysics Data System (ADS)

Khokhlova, T. D.

2017-10-01

γ-Fe2O3-SiO2 composites are synthesized via the coprecipitation of a γ-Fe2O3 magnetic carrier (with specific surface S = 17 m2/g and pore volume V = 0.51 cm3/g) and silicon dioxide from an aqueous glass (sodium silicate) solution. The effect coagulation agent NaCl has on the coprecipitation process and structural characteristics of the composite is discussed. Adding NaCl to the aqueous glass solution prevents the formation of SiO2 macrogel making it possible to obtain highly porous composites with high adsorption capacity for proteins cytochrome C and hemoglobin. It is established that a composite that is 50% SiO2 and produced with the addition of 5% NaCl ( S = 150 m2/g and V = 0.87 cm3/g) has a sixfold and twofold higher capacity (280 and 175 mg/g) for cytochrome C and hemoglobin, respectively, than the initial ferric oxide (45 and 82 mg/g). The capacity for cytochrome C and hemoglobin of a composite synthesized without NaCl ( S = 50 m2/g and V = 0.45 cm3/g) is 19 and 20 mg/g, respectively, which is twofold and fourfold lower than those of the initial γ-Fe2O3. The dependence of protein adsorption on pH and the ionic strength of a solution is studied, and the conditions for the maximum adsorption and complete desorption of proteins are established. It is concluded that composites synthesized with additions of NaCl can be used as magnetocontrollable sorbents for the purification, concentration, and immobilization of proteins, and for the preparation of biocatalysts based on immobilized enzymes.

A study on electrical conductivity of chemosynthetic Al 2O 3-2SiO 2 geoploymer materials

NASA Astrophysics Data System (ADS)

Cui, Xue-Min; Zheng, Guang-Jian; Han, Yao-Cong; Su, Feng; Zhou, Ji

Al 2O 3-2SiO 2 amorphous powders are synthesized by sol-gel method with tetraethoxysilane (TEOS) and aluminum nitrate (ANN) as the starting materials. The microstructure and phase structure of the powders are investigated by SEM and XRD analysis. Geopolymer materials samples are prepared by mechanically mixing stoichiometric amounts of calcined Al 2O 3-2SiO 2 powders and sodium silicate solutions to allow a mass ratio of Na 2O/Al 2O 3 = 0.4, 0.375, 0.35, 0.325, 0.288, 0.26, 0.23 or 0.2 separately, and finally to form a homogenous slurry at a fixed H 2O/Na 2O mole ratio = 11.7. The results show that the synthetic Al 2O 3-2SiO 2 powders have polycondensed property and their compressive strengthes are similar to that of nature metakaolin geopolymer materials. The results also show that the water consumption is not the main influencing factor on electrical conductivity of harden geopolymer materials but it can intensively affect the microstructure of geopolymer materials. In addition, the electrical conductivity of harden geopolymer sample is investigated, and the results show that the geopolymer materials have a high ionic electrical conductivity of about 1.5 × 10 -6 S cm -1 in air at room temperature.

Shock-induced transformations in the system NaAlSiO4-SiO2 - A new interpretation

NASA Technical Reports Server (NTRS)

Sekine, Toshimori; Ahrens, Thomas J.

1992-01-01

New internally consistent interpretations of the phases represented by the high pressure phase shock wave data for an albite-rich rock, jadeite, and nepheline in the system NaAlSiO4-SiO2, are obtained using the results of static high pressure investigations, and the recent discovery of the hollandite phase in a shocked meteorite. We conclude that nepheline transforms directly to the calcium ferrite structure, whereas albite transforms possibly to the hollandite structure. Shock Hugoniots for the other plagioclase and alkali feldspars also indicate that these transform to hollandite structures. The pressure-volume data at high pressure could alternatively represent the compression of an amorphous phase. Moreover, the shock Hugoniot data are expected to reflect the properties of the melt above shock stresses of 60-80 GPa. The third order Birch-Murnaghan equation of state parameters are given for the calcium ferrite type NaAlSiO4 and for albite-rich, orthoclase-rich, and anorthite-rich hollandites.

Phase Equilibria Study in the TeO2-Na2O-SiO2 System in Air Between 723 K (500 °C) and 1473 K (1200 °C)

NASA Astrophysics Data System (ADS)

Santoso, Imam; Taskinen, Pekka

2016-08-01

Knowledge of phase equilibria in the TeO2-Na2O-SiO2 system at elevated temperatures is important for ceramic and glass industries and for improving the operation of the smelting process of tellurium-containing materials. A review of previous investigations has indicated, however, that there are omissions in the available datasets on the liquidus temperatures of the molten TeO2-Na2O-SiO2 mixtures. The employed experimental method included equilibration of mixtures made from high purity oxides, rapid quenching of the equilibrated samples in water and followed by compositional analysis of the phases using an electron probe X-ray microanalyzer. The liquidus and phase equilibria in the TeO2-SiO2, TeO2-Na2O, and SiO2-TeO2-Na2O systems have been studied for a wide range of compositions between 723 K (500 °C) and 1473 K (1200 °C) at TeO2, SiO2, and Na2SiO3 saturations. New data have been generated in the SiO2-TeO2-Na2O system at SiO2 saturation. The liquidus compositions in the TeO2-Na2O system at TeO2 saturation have been compared with the previous data and an assessed phase diagram.

Gels and gel-derived glasses in the Na2O-B2O3-SiO2 system. [containerless melting in space

NASA Technical Reports Server (NTRS)

Mukherjee, S. P.

1982-01-01

The containerless melting of high-purity multicomponent homogeneous gels and gel-monoliths offers a unique approach to making ultrapure multicomponent optical glasses in the reduced gravity environment of space. Procedures for preparing and characterizing gels and gel-derived glasses in the Na2O-B2O3-SiO2 system are described. Preparation is based on the polymerization reactions of alkoxysilane with trimethyl borate or boric acid and a suitable sodium compound. The chemistry of the gelling process is discussed in terms of process parameters and the gel compositions. The physicochemical nature of gels prepared by three different procedures were found to be significantly different. IR absorption spectra indicate finite differences in the molecular structures of the different gels. The melting of the gel powders and the transformation of porous gel-monoliths to transparent 'glass' without melting are described.

Synthesis of magnetically recyclable MnFe2O4@SiO2@Ag nanocatalyst: Its high catalytic performances for azo dyes and nitro compounds reduction

NASA Astrophysics Data System (ADS)

Kurtan, U.; Amir, Md.; Yıldız, A.; Baykal, A.

2016-07-01

In this study, magnetically recycable MnFe2O4@SiO2@Ag nanocatalyst (MnFe2O4@SiO2@Ag MRCs) has been synthesized through co-precipition and chemical reduction method. XRD analysis confirmed the synthesis of single phase nanoproduct with crystallite size of 10 nm. VSM measurements showed the superparamagnetic property of the product. Catalytic studies showed that MnFe2O4@SiO2@Ag MRC could catalyze the reduction of the various azo compounds like methyl orange (MO), methylene blue (MB), eosin Y (EY), and rhodamine B (RhB) and also aromatic nitro compounds such as 4-nitrophenol (4-NP), 4-nitroaniline (4-NA) and 2-nitroaniline (2-NA). Moreover, the magnetic nanocatalyst showed an excellent reusability properties that remained unchanged after several cycles. Therefore, MnFe2O4@SiO2@Ag is the potential candidate for the application of organic pollutants for wastewater treatment.

Uptake, transport, distribution and Bio-effects of SiO2 nanoparticles in Bt-transgenic cotton.

PubMed

Le, Van Nhan; Rui, Yukui; Gui, Xin; Li, Xuguang; Liu, Shutong; Han, Yaning

2014-12-05

SiO2 nanoparticle is one of the most popular nanomaterial which has been used in various fields, such as wastewater treatment, environmental remediation, food processing, industrial and household applications, biomedicine, disease labeling, and biosensor, etc. In agriculture, the use of SiO2 nanoparticles as insecticide, carriers in drug delivery, or in uptake and translocation of nutrient elements, etc., has been given attention. However, the effects of nanoparticles on plants have been seldom studied. In this work, the toxicity of SiO2 nanoparticles and their uptake, transport, distribution and bio-effects have been investigated in Bt-transgenic cotton. The phytotoxic effects of SiO2 nanoparticles were exhibited in Bt-transgenic cotton with different SiO2 concentrations of 0, 10, 100, 500 and 2000 mg.L(-1) for 3 weeks through dry biomasses, nutrient elements, xylem sap, enzymes activities, and hormone concentrations. The uptake and distribution of nanoparticles by the plants were confirmed using transmission electron microscopy (TEM). The SiO2 nanoparticles decreased significantly the plant height, shoot and root biomasses; the SiO2 nanoparticles also affected the contents of Cu, Mg in shoots and Na in roots of transgenic cotton; and SOD activity and IAA concentration were significantly influenced by SiO2 nanoparticles. In addition, SiO2 nanoparticles were present in the xylem sap and roots as examined by TEM showing that the SiO2 nanoparticles were transported from roots to shoots via xylem sap. This is the first report of the transportation of SiO2 nanoparticles via xylem sap within Bt-transgenic cotton. This study provides direct evidence for the bioaccumulation of SiO2 nanoparticles in plants, which shows the potential risks of SiO2 nanoparticles impact on food crops and human health.

Sol-gel preparation of self-cleaning SiO2-TiO2/SiO2-TiO2 double-layer antireflective coating for solar glass

NASA Astrophysics Data System (ADS)

Lin, Wensheng; Zheng, Jiaxian; Yan, Lianghong; Zhang, Xinxiang

2018-03-01

Self-cleaning SiO2-TiO2/SiO2-TiO2 double-layer antireflective (AR) coating is prepared by sol-gel process. SiO2 sol is prepared by using tetraethyl orthosilicate (TEOS) as precursor and ammonia as catalyst, while TiO2 sol was prepared by using tetrabutyl orthotitanate (TBOT) as precursor and hydrochloric acid as catalyst. The effect of TiO2 content on refractive index, abrasion-resistance and photo-catalytic activity of SiO2-TiO2 hybrid thin films or powders is systematically investigated. It is found that the refractive index of SiO2-TiO2 hybrid thin films increases gradually from 1.18 to 1.53 as the weight ratio of TiO2 to SiO2 increased from 0 to 1.0. The SiO2-TiO2 hybrid thin film and powder possesses good abrasion-resistance and photo-catalytic activity, respectively, as the weight ratio of TiO2 to SiO2 is 0.4. The degradation degree of Rhodamine B by SiO2-TiO2 hybrid powder is 88.3%. Finally, SiO2-TiO2/SiO2-TiO2 double-layer AR coating with high transmittance, abrasion-resistance and self-cleaning property is realized.

Preparation and Characterization of PbO-SrO-Na2O-Nb2O5-SiO2 Glass Ceramics Thin Film for High-Energy Storage Application

NASA Astrophysics Data System (ADS)

Tan, Feihu; Zhang, Qingmeng; Zhao, Hongbin; Wei, Feng; Du, Jun

2018-03-01

PbO-SrO-Na2O-Nb2O5-SiO2 (PSNNS) glass ceramic thin films were prepared by pulsed laser deposition technology on heavily doped silicon substrates. The influence of annealing temperatures on microstructures, dielectric properties and energy storage performances of the as-prepared films were investigated in detail. X-ray diffraction studies indicate that Pb2Nb2O7 crystallizes at 800°C and disappears at 900°C, while NaNbO3 and PbNb2O6 are formed at the higher temperature of 900°C. The dielectric properties of the glass ceramics thin films have a strong dependence on the phase assemblages that are developed during heat treatment. The maximum dielectric constant value of 171 was obtained for the film annealed at 800°C, owing to the high electric breakdown field strength, The energy storage densities of the PSNNS films annealed at 800°C were as large as 36.9 J/cm3, These results suggest that PSNNS thin films are promising for energy storage applications.

A Structural Molar Volume Model for Oxide Melts Part I: Li2O-Na2O-K2O-MgO-CaO-MnO-PbO-Al2O3-SiO2 Melts—Binary Systems

NASA Astrophysics Data System (ADS)

Thibodeau, Eric; Gheribi, Aimen E.; Jung, In-Ho

2016-04-01

A structural molar volume model was developed to accurately reproduce the molar volume of molten oxides. As the non-linearity of molar volume is related to the change in structure of molten oxides, the silicate tetrahedral Q-species, calculated from the modified quasichemical model with an optimized thermodynamic database, were used as basic structural units in the present model. Experimental molar volume data for unary and binary melts in the Li2O-Na2O-K2O-MgO-CaO-MnO-PbO-Al2O3-SiO2 system were critically evaluated. The molar volumes of unary oxide components and binary Q-species, which are model parameters of the present structural model, were determined to accurately reproduce the experimental data across the entire binary composition in a wide range of temperatures. The non-linear behavior of molar volume and thermal expansivity of binary melt depending on SiO2 content are well reproduced by the present model.

Effect of neutron-irradiation on optical properties of SiO2-Na2O-MgO-Al2O3 glasses

NASA Astrophysics Data System (ADS)

Sandhu, Amanpreet Kaur; Singh, Surinder; Pandey, Om Prakash

2009-07-01

Silica based glasses are used as nuclear shielding materials. The effect of radiation on these glasses varies as per the constituents used in these glasses. Glasses of different composition of SiO2-Na2OMgO-Al2O3 were made by melt casting techniques. These glasses were irradiated with neutrons of different fluences. Optical absorption measurements of neutron-irradiated silica based glasses were performed at room temperature (RT) to detect and characterize the induced radiation damage in these materials. The absorption band found for neutron-irradiated glasses are induced by hole type color centers related to non-bridging oxygen ions (NBO) located in different surroundings of glass matrix. Decrease in the transmittance indicates the formation of color-center defects. Values for band gap energy and the width of the energy tail above the mobility gap have been measured before and after irradiation. The band gap energy has been found to decrease with increasing fluence while the Urbach energy shows an increase. The effects of the composition of the glasses on these parameters have been discussed in detail in this paper.

Bioactivity of gel-glass powders in the CaO-SiO2 system: a comparison with ternary (CaO-P2O5-SiO2) and quaternary glasses (SiO2-CaO-P2O5-Na2O).

PubMed

Saravanapavan, Priya; Jones, Julian R; Pryce, Russell S; Hench, Larry L

2003-07-01

Bioactive glasses react chemically with body fluids in a manner that is compatible with the repair processes of the tissues. This results in the formation of an interfacial bond between the glasses and living tissue. Bioactive glasses also stimulate bone-cell proliferation. This behavior is dependent on the chemical composition as well as the surface texture of the glasses. It has been recently reported that gel-derived monolith specimens in the binary SiO2 - CaO are bioactive over a similar molar range of SiO2 content as the previously studied ternary CaO-P2O5-SiO2 system. In this report, the preparation and bioactivity of the binary gel-glass powder with 70 mol % SiO2 is discussed and its bioactivity is compared with the melt-derived 45S5 (quaternary) Bioglass and sol-gel-derived 58S (ternary) bioactive gel-glass compositions. Dissolution kinetic parameters K(1) and K(2) were also computed based on the silicon release for all glass powders. It was shown that the simple two-component SiO2-CaO gel-glass powder is bioactive with comparable dissolution rates as the clinically used melt-derived 45S5 Bioglass powder and extensively studied sol-gel-derived 58S gel-glass powder. Copyright 2003 Wiley Periodicals, Inc.

Synthesis of Copper-Based Nanostructured Catalysts on SiO2-Al2O3, SiO2-TiO2, and SiO2-ZrO2 Supports for NO Reduction.

PubMed

Namkhang, Pornpan; Kongkachuichay, Paisan

2015-07-01

The selective catalytic reduction of NO over a series of Cu-based catalysts supported on modified silica including SiO2-Al2O3, SiO2-TiO2, and SiO2-ZrO2 prepared via a sol-gel process and a flame spray pyrolysis (FSP) was studied. The prepared catalysts were characterized by means of TEM, XRD, XRF, TPR, and nitrogen physisorption measurement techniques, to determine particle diameter, morphology, crystallinity, phase composition, copper reducibility, surface area, and pore size of catalysts. The particles obtained from sol-gel method were almost spherical while the particles obtained from the FSP were clearly spherical and non-porous nanosized particles. The effects of Si:Al, Si:Ti, and Si:Zr molar ratio of precursor were identified as the domain for different crystalline phase of materials. It was clearly seen that a high SiO2 content inhibited the crystallization of materials. The BET surface area of catalysts obtained from sol-gel method was higher than that from the FSP and it shows that surface area increased with increasing SiO2 molar ratio due to high surface area from SiO2. The catalyst performances were tested for the selective catalytic reduction of NO with H2. It was found that the catalyst prepared over 7 wt% Cu on Si02-Al2O3 support was the most active compared with the others which converted NO as more than 70%. Moreover, the excess copper decreased the performance of NO reduction, due to the formation of CuO agglomeration covered on the porous silica as well as the alumina surface, preventing the direct contact of CO2 and AL2O3.

Bioactivity of Y2O3 and CeO2 doped SiO2-SrO-Na2O glass-ceramics.

PubMed

Placek, L M; Keenan, T J; Wren, A W

2016-08-01

The bioactivity of yttrium and cerium are investigated when substituted for Sodium (Na) in a 0.52SiO2-0.24SrO-0.24-xNa2O-xMO glass-ceramics (where x = 0.08 and MO = Y2O3 or CeO2). Bioactivity is monitored through pH and inductively coupled plasma-optical emission spectrometry where pH of simulated body fluid ranged from 7.5 to 7.6 and increased between 8.2 and 10.0 after 14-day incubation with the glass-ceramic disks. Calcium (Ca) and phosphorus (P) levels in simulated body fluid after incubation with yttrium and cerium containing disks show a continual decline over the 14-day period. In contrast, Con disks (not containing yttrium or cerium) caused the elimination of Ca in solution after 1 day and throughout the incubation period, and initially showed a decline in P levels followed by an increase at 14 days. Scanning electron microscopy and energy dispersive spectroscopy confirmed the presence of Ca and P on the surface of the simulated body fluid-incubated disks and showed precipitates on Con and HCe (8 mol% cerium) samples. Cell viability of MC3T3 osteoblasts was not significantly affected at a 9% extract concentration. Optical microscopy after 24 h cell incubation with disks showed that Con samples do not support osteoblast or Schwann cell growth, while all yttrium and cerium containing disks have direct contact with osteoblasts spread across the wells. Schwann cells attached in all wells, but only showed spreading with the HY-S (8 mol% yttrium, heated to sintering temperature) and YCe (4 mol% yttrium and cerium) disks. Scanning electron microscopy of the compatible disks shows osteoblast and sNF96.2 Schwann cells attachment and spreading directly on the disk surfaces. © The Author(s) 2016.

Pressure-induced Ge coordination change in SiO2-GeO2 glasses

NASA Astrophysics Data System (ADS)

Majérus, O.; Cormier, L.; Itié, J.-P.; Calas, G.

2003-04-01

Among the parameters controlling igneous processes in Earth, the density and transport properties of silicate melts are playing a major role. These properties are strongly dependent upon pressure, in a way that can significantly differ from the crystalline phases. The study of the pressure-induced structural changes can give a further understanding of the peculiar microscopic origins of these properties in molten phases. As in silicate minerals, the coordination change IVSi towards VISi is expected to be the major transformation occurring in melts at mantle conditions, yielding amorphous phases with properties distinct to those corresponding to a tetrahedral framework. This change is predicted by molecular dynamics simulations, but experimental evidences are scarce because of difficult technical constraints. The binary SiO_2-GeO_2 system allows a further insight into the compression mechanism of a tetrahedral framework glass structure. The Ge coordination change and its composition dependence can be assessed by using XAS spectroscopy at Ge K-edge with a diamond anvil cell. In this study, we report an in situ investigation carried out on well characterized glasses of the SiO_2-GeO_2 system. Experiments were preformed on the D11 beamline which is a unique dispersive experimental setup developed at the Laboratoire pour l’Utilisation du Rayonnement Magnétique (LURE, Orsay, France). Pressures up to 25 GPa have been obtained. With increasing SiO_2 content, both Ge-O distances extracted from EXAFS data and XANES features indicate the regular increase of the pressure threshold for the Ge coordination change (from 4 in pure GeO_2 to 12 Gpa in 80 mol% SiO_2-bearing glass), which corresponds to the end of the elastic compression regime, and the achievement of the transformation on a broader pressure range as predicted in pure SiO_2. These data are compared to results on slightly depolymerised glasses of Na_2O-GeO_2 composition, where a greater variety of compression

B2O3/SiO2 substitution effect on structure and properties of Na2O-CaO-SrO-P2O5-SiO2 bioactive glasses from molecular dynamics simulations.

PubMed

Ren, Mengguo; Lu, Xiaonan; Deng, Lu; Kuo, Po-Hsuen; Du, Jincheng

2018-05-23

The effect of B2O3/SiO2 substitution in SrO-containing 55S4.3 bioactive glasses on glass structure and properties, such as ionic diffusion and glass transition temperature, was investigated by combining experiments and molecular dynamics simulations with newly developed potentials. Both short-range (such as bond length and bond angle) and medium-range (such as polyhedral connection and ring size distribution) structures were determined as a function of glass composition. The simulation results were used to explain the experimental results for glass properties such as glass transition temperature and bioactivity. The fraction of bridging oxygen increased linearly with increasing B2O3 content, resulting in an increase in overall glass network connectivity. Ion diffusion behavior was found to be sensitive to changes in glass composition and the trend of the change with the level of substitution is also temperature dependent. The differential scanning calorimetry (DSC) results show a decrease in glass transition temperature (Tg) with increasing B2O3 content. This is explained by the increase in ion diffusion coefficient and decrease in ion diffusion energy barrier in glass melts, as suggested by high-temperature range (above Tg) ion diffusion calculations as B2O3/SiO2 substitution increases. In the low-temperature range (below Tg), the Ea for modifier ions increased with B2O3/SiO2 substitution, which can be explained by the increase in glass network connectivity. Vibrational density of states (VDOS) were calculated and show spectral feature changes as a result of the substitution. The change in bioactivity with B2O3/SiO2 substitution is discussed with the change in pH value and release of boric acid into the solution.

Heat treatment of Na2O-CaO-P2O5-SiO2 bioactive glasses: densification processes and postsintering bioactivity.

PubMed

Sola, A; Bellucci, D; Raucci, M G; Zeppetelli, S; Ambrosio, L; Cannillo, V

2012-02-01

Because of their excellent bioactivity, bioactive glasses are increasingly diffused to produce biomedical devices for bone prostheses, to face the dysfunctions that may be caused by traumatic events, diseases, or even natural aging. However, several processing routes, such as the production of scaffolds or the deposition of coatings, include a thermal treatment to apply or sinter the glass. The exposure to high temperature may induce a devetrification phenomenon, altering the properties and, in particular, the bioactivity of the glass. The present contribution offers an overview of the thermal behavior and properties of two glasses belonging to the Na2O-CaO-P2O5-SiO2 system, to be compared to the standard 45S5 Bioglass(®). The basic goal is to understand the effect of both the original composition and the thermal treatment on the performance of the sintered glasses. The new glasses, the one (BG_Na) with a high content of Na2O, the other (BG_Ca) with a high content of CaO, were fully characterized and sintering tests were performed to define the most interesting firing cycles. The sintered samples, treated at 880°C and 800°C respectively, were investigated from a microstructural point of view and their mechanical properties were compared to those of the bulk (not sintered) glass counterparts. The effect of sintering was especially striking on the BG_Ca material, whose Vickers hardness increased from 598.9 ± 46.7 HV to 1053.4 ± 35.0 HV. The in vitro tests confirmed the ability of the glasses, both in bulk and sintered form, of generating a hydroxyapatite surface layer when immersed in a simulated body fluid. More accurate biological tests performed on the sintered glasses proved the high bioactivity of the CaO-rich composition even after a heat treatment. Copyright © 2011 Wiley Periodicals, Inc.

A study of low threshold and high gain Nd3+ ions doped SiO2-B2O3-Na2CO3-NaF-CaF2 glasses for NIR laser applications

NASA Astrophysics Data System (ADS)

Megala, Rajesh; Gowthami, T.; John Sushma, N.; Kamala, S.; Deva Prasad Raju, B.

2018-05-01

Fluoroborosilicate glasses of composition 35SiO2-25B2O3-10Na2CO3-15NaF-15CaF2-xNd2O3 (where x = 0.1, 0.5. 1.0, 2.0 mol%) were prepared by melt quenching technique and various physical properties have been calculated. From the absorption spectra J-O Intensity parameters Ωλ (λ = 2, 4, 6) and radiative properties are evaluated by using J-O theory. The high values of Ω2 = 4.213 × 10-20 cm2, Ω4 = 5.345 × 10-20 cm2, Ω6 = 5.526 × 10-20 cm2 suggest that among the prepared glasses 0.5 mol% Nd glass is more asymmetric, more covalent and rigid in nature. The emission spectra were recorded with 808 nm laser as excitation source. The strong NIR emissions were observed at 876 nm, 1056 nm, 1328 nm corresponding to the transitions 4F3/2 → 4I9/2, 4F3/2 → 4I11/2, 4F3/2 → 4I13/2 respectively. Stimulated emission cross -section (σemi) and Gain bandwidth (σemi × Δλeff) were calculated. For 0.5 mol% Nd these values are found to be 3.30 × 10-20 cm2, 11 × 10-26 cm2. From the decay curve analysis the lifetime values for 4F3/2 level have been determined and these values are decreased with increase in Nd3+ ions concentration. These results may suggest that the prepared SBNCNd05 (Nd = 0.5 mol%) glass could be useful for 1056 nm laser applications.

Post-pyrite transition in SiO2

NASA Astrophysics Data System (ADS)

Ho, K.; Wu, S.; Umemoto, K.; Wentzcovitch, R. M.; Ji, M.; Wang, C.

2010-12-01

Here we propose a new phase of SiO2 beyond the pyrite-type phase. SiO2 is one of the most important minerals in Earth and planetary sciences. So far, the pyrite-type phase has been identified experimentally as the highest-pressure form of SiO2. In solar giants and extrasolar planets whose interior pressures are considerably higher than that on Earth, a post-pyrite transition in SiO2 may occur at ~ 1 TPa as a result of the dissociation of MgSiO3 post-perovskite into MgO and SiO2 [Umemtoto et al., Science 311, 983 (2006)]. Several dioxides considered to be low-pressure analogs of SiO2 have a phase with cotunnite-type (PbCl2-type) structure as the post-pyrite phase. However, a first-principles structural search using a genetic algorithm shows that SiO2 should undergo a post-pyrite transition to a hexagonal phase, not to the cotunnite phase. The hexagonal phase is energetically very competitive with the cotunnite-type one. This work was supported by the U.S. Department of Energy, Office of Basic Energy Science, Division of Materials Sciences and Engineering and NSF under ATM-0428774 (VLab), EAR-0757903, and EAR-1019853. Ames Laboratory is operated for the U.S. Department of Energy by Iowa State University under Contract No. DE-AC02-07CH11358. The computations were performed at the National Energy Research Supercomputing Centre (NERSC) and the Minnesota Supercomputing Institute (MSI).

Do SiO 2 and carbon-doped SiO 2 nanoparticles melt? Insights from QM/MD simulations and ramifications regarding carbon nanotube growth

NASA Astrophysics Data System (ADS)

Page, Alister J.; Chandrakumar, K. R. S.; Irle, Stephan; Morokuma, Keiji

2011-05-01

Quantum chemical molecular dynamics (QM/MD) simulations of pristine and carbon-doped SiO 2 nanoparticles have been performed between 1000 and 3000 K. At temperatures above 1600 K, pristine nanoparticle SiO 2 decomposes rapidly, primarily forming SiO. Similarly, carbon-doped nanoparticle SiO 2 decomposes at temperatures above 2000 K, primarily forming SiO and CO. Analysis of the physical states of these pristine and carbon-doped SiO 2 nanoparticles indicate that they remain in the solid phase throughout decomposition. This process is therefore one of sublimation, as the liquid phase is never entered. Ramifications of these observations with respect to presently debated mechanisms of carbon nanotube growth on SiO 2 nanoparticles will be discussed.

Optical properties of Ag nanoclusters formed by irradiation and annealing of SiO2/SiO2:Ag thin films

NASA Astrophysics Data System (ADS)

Güner, S.; Budak, S.; Gibson, B.; Ila, D.

2014-08-01

We have deposited five periodic SiO2/SiO2 + Ag multi-nano-layered films on fused silica substrates using physical vapor deposition technique. The co-deposited SiO2:Ag layers were 2.7-5 nm and SiO2 buffer layers were 1-15 nm thick. Total thickness was between 30 and 105 nm. Different concentrations of Ag, ranging from 1.5 to 50 molecular% with respect to SiO2 were deposited to determine relevant rates of nanocluster formation and occurrence of interaction between nanoclusters. Using interferometry as well as in situ thickness monitoring, we measured the thickness of the layers. The concentration of Ag in SiO2 was measured with Rutherford Backscattering Spectrometry (RBS). To nucleate Ag nanoclusters, 5 MeV cross plane Si ion bombardments were performed with fluence varying between 5 × 1014 and 1 × 1016 ions/cm2 values. Optical absorption spectra were recorded in the range of 200-900 nm in order to monitor the Ag nanocluster formation in the thin films. Thermal annealing treatment at different temperatures was applied as second method to form varying size of nanoclusters. The physical properties of formed super lattice were criticized for thermoelectric applications.

Preparation and Characterization of Fluorescent SiO2 Microspheres

NASA Astrophysics Data System (ADS)

Xu, Cui; Zhang, Hao; Guan, Ruifang

2018-01-01

Fluorescent compound without typical fluorophores was synthesized with citric acid (CA) and aminopropyltriethoxysilane (APTS) firstly, and then it was grafted to the surface of the prepared SiO2 microspheres by chemical reaction. The fluorescent SiO2 microspheres with good fluorescent properties were obtained by optimizing the reaction conditions. And the morphology and structure of the fluorescent SiO2 microspheres have been characterized by scanning electron microscopy (SEM) and fourier transform infrared (FTIR) spectroscopy. The results showed that the preparation of fluorescent SiO2 microspheres have good monodispersity and narrow particle size distribution. Moreover, the fluorescent SiO2 microspheres can be applied to detect Fe3+ in aqueous solution, prepare fluorescent SiO2 rubber, and have potential to be applied in the fluorescent labeling and fingerprint appearing technique fields.

Photoluminescence analysis of Ce3+:Zn2SiO4 & Li++ Ce3+:Zn2SiO4: phosphors by a sol-gel method

NASA Astrophysics Data System (ADS)

Babu, B. Chandra; Vandana, C. Sai; Guravamma, J.; Rudramadevi, B. Hemalatha; Buddhudu, S.

2015-06-01

Here, we report on the development and photoluminescence analysis of Zn2SiO4, Ce3+:Zn2SiO4 & Li+ + Ce3+: Zn2SiO4 novel powder phosphors prepared by a sol-gel technique. The total amount of Ce3+ ions was kept constant in this experiment at 0.05 mol% total doping. The excitation and emission spectra of undoped (Zn2SiO4) and Ce3+ doped Zn2SiO4 and 0.05 mol% Li+ co-doped samples have been investigated. Cerium doped Zn2SiO4 powder phosphors had broad blue emission corresponding to the 2D3/2→2FJ transition at 443nm. Stable green-yellow-red emission has been observed from Zn2SiO4 host matrix and also we have been observed the enhanced luminescence of Li+ co-doped Zn2SiO4:Ce3+. Excitation and emission spectra of these blue luminescent phosphors have been analyzed in evaluating their potential as luminescent screen coating phosphors.

Bonding Transition in SiO2 Glass at High Pressures: Applications to SiO2 Liquid in Earth's Interior

NASA Astrophysics Data System (ADS)

Yoo, C.; Lin, J.; Fukui, H.; Prendergast, D.; Okuchi, T.; Cai, Y.; Hiraoka, N.; Trave, A.; Eng, P.; Hu, M. Y.; Chow, P.

2006-12-01

SiO2 and MgSiO3 liquids are two major components in the magma deep inside the Earth. Knowledge of their electronic bonding characters at high pressures is essential to understanding the complex properties of the materials in the melts. The nature of pressure-induced bonding change in amorphous SiO2 has been an intriguing and long-standing problem that remains to be further understood. For example, previous infrared and X-ray diffraction studies suggested that a continuous transformation from the four- to six-fold coordinated silicon occurred in amorphous SiO2 at high pressures, whereas separate optical Raman studies attributed to a pressure-induced shift in the local ring statistics and a breakdown in the intermediate-range order. Here we have studied the oxygen near K-edge spectra of SiO2 glass to 51 GPa obtained using X-ray Raman scattering in a diamond-anvil cell, which directly probes the electronic bonding character of the sample. Our results provide conclusive evidence for a pressure-induced electronic bonding transition in SiO2 glass at high pressures. Although a progressive decrease in the mean Si-O-Si angle in the SiO4 tetrahedra is believed to be responsible for the irreversible densification in SiO2 glass at high pressures, our observed transition is reversible upon decompression. A similar transformation is also expected to occur in silicate glasses and melts, which will most definitely alter their physical, mechanical and transport properties in the magma chamber deep in the Earth's interior. This work was performed under the auspices of the U.S. DOE by UC/LLNL under Contract W-7405-Eng-48.

Method of Preparing Monoclinic BaO.Al2O3.2SiO2

DTIC Science & Technology

Monoclinic celsian (BaO.Al2O3.2SiO2) is produced by heating a stoichiometric, powder mixture of BaCO3 (or BaC2O4), Al2O3, and SiO2 (preferably SiO2 gel) with monoclinic celsian seeds at from 1250 deg C to 1500 deg C.

Optical properties of the Al2O3/SiO2 and Al2O3/HfO2/SiO2 antireflective coatings

NASA Astrophysics Data System (ADS)

Marszałek, Konstanty; Winkowski, Paweł; Jaglarz, Janusz

2014-01-01

Investigations of bilayer and trilayer Al2O3/SiO2 and Al2O3/HfO2/SiO2 antireflective coatings are presented in this paper. The oxide films were deposited on a heated quartz glass by e-gun evaporation in a vacuum of 5 × 10-3 [Pa] in the presence of oxygen. Depositions were performed at three different temperatures of the substrates: 100 °C, 200 °C and 300 °C. The coatings were deposited onto optical quartz glass (Corning HPFS). The thickness and deposition rate were controlled with Inficon XTC/2 thickness measuring system. Deposition rate was equal to 0.6 nm/s for Al2O3, 0.6 nm - 0.8 nm/s for HfO2 and 0.6 nm/s for SiO2. Simulations leading to optimization of the thin film thickness and the experimental results of optical measurements, which were carried out during and after the deposition process, have been presented. The optical thickness values, obtained from the measurements performed during the deposition process were as follows: 78 nm/78 nm for Al2O3/SiO2 and 78 nm/156 nm/78 nm for Al2O3/HfO2/SiO2. The results were then checked by ellipsometric technique. Reflectance of the films depended on the substrate temperature during the deposition process. Starting from 240 nm to the beginning of visible region, the average reflectance of the trilayer system was below 1 % and for the bilayer, minima of the reflectance were equal to 1.6 %, 1.15 % and 0.8 % for deposition temperatures of 100 °C, 200 °C and 300 °C, respectively.

Potential energy landscape of an interstitial O2 molecule in a SiO2 film near the SiO2/Si(001) interface

NASA Astrophysics Data System (ADS)

Ohta, Hiromichi; Watanabe, Takanobu; Ohdomari, Iwao

2008-10-01

Potential energy distribution of interstitial O2 molecule in the vicinity of SiO2/Si(001) interface is investigated by means of classical molecular simulation. A 4-nm-thick SiO2 film model is built by oxidizing a Si(001) substrate, and the potential energy of an O2 molecule is calculated at Cartesian grid points with an interval of 0.05 nm in the SiO2 film region. The result shows that the potential energy of the interstitial site gradually rises with approaching the interface. The potential gradient is localized in the region within about 1 nm from the interface, which coincides with the experimental thickness of the interfacial strained layer. The potential energy is increased by about 0.62 eV at the SiO2/Si interface. The result agrees with a recently proposed kinetic model for dry oxidation of silicon [Phys. Rev. Lett. 96, 196102 (2006)], which argues that the oxidation rate is fully limited by the oxidant diffusion.

Photosensitized electron transfer processes in SiO2 colloids and sodium lauryl sulfate micellar systems: Correlation of quantum yields with interfacial surface potentials

PubMed Central

Laane, Colja; Willner, Itamar; Otvos, John W.; Calvin, Melvin

1981-01-01

The effectiveness of negatively charged colloidal SiO2 particles in controlling photosensitized electron transfer reactions has been studied and compared with that of the negatively charged sodium lauryl sulfate (NaLauSO4) micellar system. In particular, the photosensitized reduction of the zwitterionic electron acceptor propylviologen sulfonate (PVS0) with tris(2,2′-bipyridinium)ruthenium(II) [Ru(bipy)32+] as the sensitizer and triethanolamine as the electron donor is found to have a quantum yield of 0.033 for formation of the radical anion (PVS[unk]) in the SiO2 colloid compared with 0.005 in the homogeneous system and 0.0086 in a NaLauSO4 micellar solution. The higher quantum yields obtained with the SiO2 colloidal system are attributed to substantial stabilization against back reaction of the intermediate photoproducts—i.e., Ru(bipy)33+ and PVS[unk]—by electrostatic repulsion of the reduced electron acceptor from the negatively charged particle surface. The binding properties of the SiO2 particles and NaLauSO4 micelles were investigated by flow dialysis. The results show that the sensitizer binds to both interfaces and that the SiO2 interface is characterized by a much higher surface potential than the micellar interface (≈-170 mV vs. -85 mV). The effect of ionic strength on the surface potential was estimated from the Gouy-Chapman theory, and the measured quantum yields of photosensitized electron transfer were correlated with surface potential at different ionic strengths. This correlation shows that the quantum yield is not affected by surface potentials smaller than ≈-40 mV. At larger potentials, the quantum yield increases rapidly. The quantum yield obtained in the micellar system at different strengths fits nicely on the correlation curve for the colloid SiO2 system. These results indicate that the surface potential is the dominant factor in the quantum yield improvement for PVS0 reduction. PMID:16593095

The principal Hugoniot of Mg2SiO4 to 950 GPa

NASA Astrophysics Data System (ADS)

Townsend, J. P.; Root, S.; Shulenburger, L.; Lemke, R. W.; Kraus, R. G.; Jacobsen, S. B.; Spaulding, D.; Davies, E.; Stewart, S. T.

2017-12-01

We present new measurements and ab-initio calculations of the principal Hugoniot states of forsterite Mg2SiO4 in the liquid regime between 200-950 GPa.Forsterite samples were shock compressed along the principal Hugoniot using plate-impact shock compression experiments on the Sandia National Laboratories Z machine facility.In order to gain insight into the physical state of the liquid, we performed quantum molecular dynamics calculations of the Hugoniot and compare the results to experiment.We show that the principal Hugoniot is consistent with that of a single molecular fluid phase of Mg2SiO4, and compare our results to previous dynamic compression experiments and QMD calculations.Finally, we discuss how the results inform planetary accretion and impact models.Sandia National Laboratories is a multimission laboratory managed and operated by National Technology and Engineering Solutions of Sandia, LLC., a wholly owned subsidiary of Honeywell International, Inc., for the U.S. Department of Energy's National Nuclear Security Administration under contract DE-NA0003525.

SiO2 Solubility in Rutile at High Pressure and Temperature

NASA Astrophysics Data System (ADS)

Ren, Y.; Fei, Y.; Yang, J.; Bai, W. J.; Xu, Z. Q.

2005-12-01

Silicon-bearing rutile has been found in nature. The extent of SiO2 solubility in rutile and the nature of its origin are still not clear. At high pressure, SiO2 takes rutile structure with 6-coordinated Si. The high-pressure phase of SiO2 may enhance its solubility in rutile because possible isovalent exchange in octahedral site. In this study, we report new experimental results on SiO2 solubility in rutile up to 23 GPa and 2273 K. Starting materials are mixtures of powdered TiO2 and SiO2, with compositions of (Ti0.5Si0.5)O2, (Ti0.93Si0.07)O2, and (Ti0.75Si0.25)O2. The mixtures were loaded into either a platinum capsules (for a 10/5 assembly) or a rhenium capsules (for an 8/3 assembly). The experiments were carried out using multi-anvil high-pressure apparatus with rhenium resistance heater. Sample temperatures were measured with a type-C thermocouple. The quenched samples were recovered and prepared for electron microprobe analyses. TiO2-rich and SiO2-rich phases are produced in all the quenched samples. The analyses showed that the solubility of SiO2 in rutile increases with increasing pressure, from 1.5 wt% SiO2 at 10 GPa to 3.8 wt% SiO2 at 23 GPa for a given temperature of 2073 K. The solubility also increases with increasing temperature, from 0.5 wt% SiO2 at 1773 K to 4.5 wt% SiO2 at 2273 K for a given pressure of 18 GPa. On the other hand, the solubility of TiO2 in coesite or stishovite is very limited, with an average of 0.6 wt% TiO2 over the experimental P-T ranges. Lower oxygen fugacity decreases the solubility of SiO2 in rutile, whereas water has little effect on the solubility of SiO2 in rutile. Our experimental data are extreme useful for determine the depth of origin for the SiO2-bearing rutile in nature.

Highly Luminescent Hybrid SiO2-Coated CdTe Quantum Dots Retained Initial Photoluminescence Efficiency in Sol-Gel SiO2 Film.

PubMed

Sun, Hongsheng; Xing, Yugui; Wu, Qinan; Yang, Ping

2015-02-01

A highly luminescent silica film was fabricated using tetraethyl orthosilicate (TEOS) and 3-aminopropyltrimethoxysilane (APS) through a controlled sol-gel reaction. The pre-hydrolysis of TEOS and APS which resulted in the mixture of TEOS and APS in a molecular level is a key for the formation of homogenous films. The aminopropyl groups in APS play an important role for obtaining homogeneous film with high photoluminescence (PL). Red-emitting hybrid SiO2-coated CdTe nano-crystals (NCs) were fabricated by a two-step synthesis including a thin SiO2 coating via a sol-gel process and a subsequent refluxing using green-emitting CdTe NCs. The hybrid SiO2-coated CdTe NCs were embedded in a functional SiO2 film via a two-step process including adding the NCs in SiO2 sol with a high viscosity and almost without ethanol and a subsequent spinning coating. The hybrid SiO2-coated CdTe NCs retained their initial PL efficiency (54%) in the film. Being encapsulated with the hybrid NCs in the film, no change on the absorption and PL spectra of red-emitting CdTe NCs (632 nm) was observed. This indicates the hybrid NCs is stable enough during preparation. This phenomenon is ascribed to the controlled sol-gel process and a hybrid SiO2 shell on CdTe NCs. Because these films exhibited high PL efficiency and stability, they will be utilizable for potential applications in many fields.

Crystallization kinetics of bioactive glasses in the ZnO-Na2O-CaO-SiO2 system.

PubMed

Malavasi, Gianluca; Lusvardi, Gigliola; Pedone, Alfonso; Menziani, Maria Cristina; Dappiaggi, Monica; Gualtieri, Alessandro; Menabue, Ledi

2007-08-30

The crystallization kinetics of Na(2)O.CaO.2SiO(2) (x = 0) and 0.68ZnO.Na(2)O.CaO.2SiO(2) (x = 0.68, where x is the ZnO stoichiometric coefficient in the glass formula) bioactive glasses have been studied using both nonisothermal and isothermal methods. The results obtained from isothermal XRPD analyses have showed that the first glass crystallizes into the isochemical Na(2)CaSi(2)O(6) phase, whereas the Na(2)ZnSiO(4) crystalline phase is obtained from the Zn-rich glass, in addition to Na(2)CaSi(2)O(6). The activation energy (Ea) for the crystallization of the Na(2)O.CaO.2SiO(2) glass is 193 +/- 10 and 203 +/- 5 kJ/mol from the isothermal in situ XRPD and nonisothermal DSC experiments, respectively. The Avrami exponent n determined from the isothermal method is 1 at low temperature (530 degrees C), and its value increases linearly with temperature increase up to 2 at 607 degrees C. For the crystallization of Na(2)CaSi(2)O(6) from the Zn-containing glass, higher values of both the crystallization temperature (667 and 661 degrees C) and Ea (223 +/- 10 and 211 +/- 5 kJ/mol) have been found from the isothermal and nonisothermal methods, respectively. The Na(2)ZnSiO(4) crystalline phase crystallizes at lower temperature with respect to Na(2)CaSi(2)O(6), and the Ea value is 266 +/- 20 and 245 +/- 15 kJ/mol from the isothermal and nonisothermal methods, respectively. The results of this work show that the addition of Zn favors the crystallization from the glass at lower temperature with respect to the Zn-free glass. In fact, it causes an increase of Ea for the Na diffusion process, determined using MD simulations, and consequently an overall increase of Ea for the crystallization process of Na(2)CaSi(2)O(6). Our results show good agreement between the Ea and n values obtained with the two different methods and confirm the reliability of the nonisothermal method applied to kinetic crystallization of glassy systems. This study allows the determination of the temperature

Thermodynamic properties of Na2O-SiO2-CaO melts at 1000 to 1100 °C

NASA Astrophysics Data System (ADS)

Neudorf, D. A.; Elliott, J. F.

1980-12-01

The thermodynamic properties of Na2O-SiO2 and Na2O-SiO2-CaO melts have been measured using the galvanic cellbegin{array}{*{20}c} {O_2 (g), (Na_2 O), Pt} \\ {Na_2 O - WO_3 liq} \\ left| begin{gathered} Na^ + \\ β - alumina \\ right| begin{array}{*{20}c} {Pt,(Na_2 O), O_2 (g)} \\ {Na_2 O - SiO_2 - CaO liq} \\ Activities of Na2O were calculated from the reversible emf of the cell. This is possible because the activity of Na2O in the Na2O-WO3 liquid is known from previous work. Data for the binary Na2O-SiO2 system were obtained between 1000 and 1100 °C and for compositions ranging from 25 wt pct to 40 wt pct Na2O. At 1050 °C, Loga_{Na_2 O} varied from approximately 10.2 at 25 wt pct Na2O to approximately -8.3 at 40 wt pct Na2O, the dependence with respect to composition being nearly linear. The Gibbs-Duhem equation was used to calculate the activities of SiO2(s), and the integral mixing properties, G M, HM, and S M, were derived. At the di-silicate composition, G M = -83 kJ/mol, H M = -41 kJ mol and S M = 33 J/mol K at 1000 °C. (Standard states are pure, liquid Na2O and pure, solid tridymite.) The activity data are interpreted in terms of the polymeric nature of silicate melts. Activities of Na2O in the Na2O-CaO-SiO2 system were measured for the 25, 30 and 35 wt pct Na2O binary compositions with up to 10 wt pct CaO added. The addition of CaO caused an increase in the activity of Na2O at constantN_{Na_2 O} /N_{SiO_2 } . The experimental data agree well with the behavior predicted by Richardson’s ternary mixing model.

Effect of Commercial SiO2 and SiO2 from rice husk ash loading on biodegradation of Poly (lactic acid) and crosslinked Poly (lactic acid)

NASA Astrophysics Data System (ADS)

Prapruddivongs, C.; Apichartsitporn, M.; Wongpreedee, T.

2017-09-01

In this work, biodegradation behavior of poly (lactic acid) (PLA) and crosslinked PLA filled with two types of SiO2, precipitated SiO2 (commercial SiO2) and SiO2 from rice husk ash, were studied. Rice husks were first treated with 2 molar hydrochloric acid (HCl) to produce high purity SiO2, before burnt in a furnace at 800°C for 6 hours. All components were melted bending by an internal mixer then hot pressed using compression molder to form tested specimens. FTIR spectra of SiO2 and PLA samples were investigated. The results showed the lack of silanol group (Si-OH) of rice husk ash after steric acid surface modification, while the addition of particles can affect the crosslinking of the PLA. For biodegradation test by evaluating total amount of carbon dioxide (CO2) evolved during 60 days incubation at a controlled temperature of 58±2°C, the results showed that the biodegradation of crosslinked PLA occurred slower than the neat PLA. However, SiO2 incorporation enhanced the degree of biodegradation In particular, introducing commercial SiO2 in PLA and crosslinked PLA tended to clearly increase the degree of biodegradation as a consequence of the more accelerated hydrolysis degradation.

Synthesis of zeolites Na-A and Na-X from tablet compressed and calcinated coal fly ash

NASA Astrophysics Data System (ADS)

Hu, Tao; Gao, Wenyan; Liu, Xin; Zhang, Yifu; Meng, Changgong

2017-10-01

Zeolites Na-A and Na-X are important synthetic zeolites widely used for separation and adsorption in industry. It is of great significance to develop energy-efficient routines that can synthesize zeolites Na-A and Na-X from low-cost raw materials. Coal fly ash (CFA) is the major residue from the combustion of coal and biomass containing more than 85% SiO2 and Al2O3, which can readily replace the conventionally used sodium silicate and aluminate for zeolite synthesis. We used Na2CO3 to replace the expensive NaOH used for the calcination of CFA and showed that tablet compression can enhance the contact with Na2CO3 for the activation of CFA through calcination for the synthesis of zeolites Na-A and Na-X under mild conditions. We optimized the control variables for zeolite synthesis and showed that phase-pure zeolite Na-A can be synthesized with CFA at reactant molar ratio, hydrothermal reaction temperature and reaction time of 1.3Na2O: 0.6Al2O3: 1SiO2: 38H2O at 80°C for 6 h, respectively, while phase-pure zeolite Na-X can be synthesized at 2.2Na2O: 0.2Al2O3: 1SiO2: 88H2O at 100°C for 8 h, respectively. The composition, morphology, specific surface area, vibration spectrum and thermogravimetry of synthesized Na-A and Na-X were further characterized.

Upconversion induced enhancement of dye sensitized solar cells based on core-shell structured β-NaYF4:Er3+, Yb3+@SiO2 nanoparticles

NASA Astrophysics Data System (ADS)

Zhou, Ziyao; Wang, Jiahong; Nan, Fan; Bu, Chenghao; Yu, Zhenhua; Liu, Wei; Guo, Shishang; Hu, Hao; Zhao, Xing-Zhong

2014-01-01

Upconversion materials have been employed as energy relay materials in dye sensitized solar cells (DSCs) to broaden the range of light absorption. However, the origin of the enhancements can be induced by both upconversion and size-dependent light scattering effects. To clarify the role of the upconversion material in the photoelectrode of DSCs, an upconversion induced device was realized here, which has the size-dependent light scattering effect eliminated via the application of NaYF4:Er3+, Yb3+@SiO2 upconversion nanoparticles (β-NYEY@SiO2 UCNPs). An enhancement of 6% in efficiency was observed for the device. This demonstration provided an insight into the possible further employment of upconversion in DSCs.Upconversion materials have been employed as energy relay materials in dye sensitized solar cells (DSCs) to broaden the range of light absorption. However, the origin of the enhancements can be induced by both upconversion and size-dependent light scattering effects. To clarify the role of the upconversion material in the photoelectrode of DSCs, an upconversion induced device was realized here, which has the size-dependent light scattering effect eliminated via the application of NaYF4:Er3+, Yb3+@SiO2 upconversion nanoparticles (β-NYEY@SiO2 UCNPs). An enhancement of 6% in efficiency was observed for the device. This demonstration provided an insight into the possible further employment of upconversion in DSCs. Electronic supplementary information (ESI) available: Details of preparations and characterizations; the TEM images, EDX measurements, XRD measurements and upconversion emission spectrum of bared β-NYEY nanocrystals; SEM and AFM images of the photoelectrode with different concentrations of β-NYEY nanocrystals; J-V characteristics, EIS measurements and fitted EIS parameters of the DSCs based on five different photoelectrodes. See DOI: 10.1039/c3nr04315k

Efficient drug delivery using SiO2-layered double hydroxide nanocomposites.

PubMed

Li, Li; Gu, Zi; Gu, Wenyi; Liu, Jian; Xu, Zhi Ping

2016-05-15

MgAl-layered double hydroxide (MgAl-LDH) nanoparticles have great potentials in drug and siRNA delivery. In this work, we used a nanodot-coating strategy to prepare SiO2 dot-coated layered double hydroxide (SiO2@MgAl-LDH) nanocomposites with good dispersibility and controllable size for drug delivery. The optimal SiO2@MgAl-LDH nanocomposite was obtained by adjusting synthetic parameters including the mass ratio of MgAl-LDH to SiO2, the mixing temperature and time. The optimal SiO2@MgAl-LDH nanocomposite was shown to have SiO2 nanodots (10-15nm in diameter) evenly deposited on the surface of MgAl-LDHs (110nm in diameter) with the plate-like morphology and the average hydrodynamic diameter of 170nm. We further employed SiO2@MgAl-LDH nanocomposite as a nanocarrier to deliver methotrexate (MTX), a chemotherapy drug, to the human osteosarcoma cell (U2OS) and found that MTX delivered by SiO2@MgAl-LDH nanocomposite apparently inhibited the U2OS cell growth. Copyright © 2016 Elsevier Inc. All rights reserved.

SiO2 and TiO2 nanoparticles synergistically trigger macrophage inflammatory responses.

PubMed

Tsugita, Misato; Morimoto, Nobuyuki; Nakayama, Masafumi

2017-04-11

Silicon dioxide (SiO 2 ) nanoparticles (NPs) and titanium dioxide (TiO 2 ) NPs are the most widely used inorganic nanomaterials. Although the individual toxicities of SiO 2 and TiO 2 NPs have been extensively studied, the combined toxicity of these NPs is much less understood. In this study, we observed unexpected and drastic activation of the caspase-1 inflammasome and production of IL-1β in mouse bone marrow-derived macrophages stimulated simultaneously with SiO 2 and TiO 2 NPs at concentrations at which these NPs individually do not cause macrophage activation. Consistent with this, marked lung inflammation was observed in mice treated intratracheally with both SiO 2 and TiO 2 NPs. In macrophages, SiO 2 NPs localized in lysosomes and TiO 2 NPs did not; while only TiO 2 NPs produced ROS, suggesting that these NPs induce distinct cellular damage leading to caspase-1 inflammasome activation. Intriguingly, dynamic light scattering measurements revealed that, although individual SiO 2 and TiO 2 NPs immediately aggregated to be micrometer size, the mixture of these NPs formed a stable and relatively monodisperse complex with a size of ~250 nm in the presence of divalent cations. Taken together, these results suggest that SiO 2 and TiO 2 NPs synergistically induce macrophage inflammatory responses and subsequent lung inflammation. Thus, we propose that it is important to assess the synergistic toxicity of various combinations of nanomaterials.

Nrf2 protects against oxidative stress induced by SiO2 nanoparticles.

PubMed

Liu, Wei; Hu, Tao; Zhou, Li; Wu, Desheng; Huang, Xinfeng; Ren, Xiaohu; Lv, Yuan; Hong, Wenxu; Huang, Guanqin; Lin, Zequn; Liu, Jianjun

2017-10-01

The aim of our study was to explore the role of nuclear factor erythroid 2 (NF-E2)-related factor 2 (Nrf2) on the exposure of SiO 2 nanoparticles (NPs) and its influence. To understand the mechanism of NP-induced oxidative stress, the involvement of oxidative-stress-responding transcription factors and the Nrf2/antioxidant reactive element (ARE) signaling pathway in the toxicity of SiO 2 NPs' exposure was investigated via in vivo and in vitro models. A549 cells showed a significant cytotoxic effect while A549-shNrf2 cells showed decreased cell viability after nm-SiO 2 exposure. SiO 2 NPs' exposure activated the Nrf2/ARE signaling pathway. Nrf2 -/- exposed mice showed increased reactive oxygen species, 8-hydroxyl deoxyguanosine level and decreased total antioxidant capacity. Nrf2/ARE signaling pathway activation disrupted, leading inhibition of heme oxygenase-1 and upregulation of PKR-like endoplasmic-reticulum-regulated kinase. Our findings suggested that Nrf2 could protect against oxidative stress induced by SiO 2 NPs, and the Nrf2/ARE pathway might be involved in mild-to-moderate SiO 2 NP-induced oxidative stress that was evident from dampened activity of Nrf2.

Synthesis of a conducting SiO2-carbon composite from commercial silicone grease and its conversion to paramagnetic SiO2 particles.

PubMed

Pol, V G; Pol, S V; George, P P; Markovsky, B; Gedanken, A

2006-07-13

The thermal decomposition of commercial silicone grease was carried out in a closed reactor (Swagelok) that was heated at 800 degrees C for 3 h, yielding a SiO2-carbon composite with a BET surface area of 369 m2/g. The bulk conductivity (5.72 x 10(-6) S x cm(-2)) of the SiO2-carbon composite was determined by impedance measurements. The as-prepared SiO2-carbon composite was further annealed at 500 degrees C in air for 2 h, which led to the formation of white paramagnetic silica particles (confirmed by ESR), possessing a surface area of 111 m2/g. The present synthetic technique requires unsophisticated equipment and a low-cost commercial precursor, and the reaction is carried out without a solvent, surfactant, or catalyst. The mechanism for the formation of a porous SiO2-carbon composite from the silicone grease is also presented.

Core-exsolved SiO2 Dispersal in the Earth's Mantle

NASA Astrophysics Data System (ADS)

Helffrich, G. R.; Ballmer, M.; Hirose, K.

2017-12-01

SiO2 may have been expelled from the core following its formation in the early stages of Earth's accretion and onwards through the present day. On account of SiO2's low density with respect to both the core and the lowermost mantle, we examine the process of SiO2 accumulation at the core-mantle boundary (CMB) and its incorporation into the mantle by buoyant rise. Today, the if SiO2 is 100-10000 times more viscous than lower mantle material, the dimensions of SiO2 diapirs formed by the viscous Rayleigh-Taylor instability at the CMB would cause them to be swept into the mantle as inclusions of 100 m - 10 km diameter. Under early Earth conditions of rapid heat loss after core formation, SiO2 diapirs of 5-80 km diameter could have risen independently of mantle flow to their level of neutral buoyancy in the mantle, trapping them there due to a combination of high viscosity and neutral buoyancy. We examine the SiO2 yield by assuming Si+O saturation at the conditions found at the base of a magma ocean and find that for a range of conditions, dispersed bodies could reach as high as 2 volume percent in shallow parts of the lower mantle, with their abundance decreasing with depth. At such low concentrations, their effect on aggregate seismic wavespeeds would be within the uncertainty of the radial Earth model PREM. However, their presence would be revealed by small-scale scattering in the lower mantle due to the bodies' large velocity contrast. We conclude that the shallow lower mantle (700-1500 km depth) could harbor SiO2 released in early Earth times.

A novel fabrication of a high performance SiO(2)-graphene oxide (GO) nanohybrids: Characterization of thermal properties of epoxy nanocomposites filled with SiO(2)-GO nanohybrids.

PubMed

Haeri, S Z; Ramezanzadeh, B; Asghari, M

2017-05-01

In this study it has been aimed to enhance the thermal resistance of epoxy coating through incorporation of SiO 2 -GO nanohybrids. SiO 2 -GO nanohybrids were synthesized through one-step sol-gel route using a mixture of Tetraethylorthosilane (TEOS) and 3-Aminopropyl triethoxysilane (APTES) silanes. The SiO 2 -GO nanohybrids were prepared at various hydrolysis times of 24, 48 and 72h. Then 0.2wt.% of GO and SiO 2 -GO nanohybrids were separately incorporated into the epoxy coating. Results revealed that amino functionalized SiO 2 nanoparticles with particle size around 20-30nm successfully synthesized on the basal plane of GO. Results showed significant improvement of dispersion and interfacial interactions between nanohybrids and epoxy composite arising from covalent bonding between the SiO 2 -GO and the epoxy matrix. It was found that the thermal resistance of SiO 2 -GO nanohybrids and SiO 2 -GO/Epoxy nanocomposite was noticeably higher than GO and epoxy matrix, respectively. Copyright © 2017 Elsevier Inc. All rights reserved.

In vitro evaluation of bioactivity of SiO2-CaO-P2O5-Na2O-CaF2-ZnO glass-ceramics

NASA Astrophysics Data System (ADS)

Riaz, Madeeha; Zia, Rehana; Saleemi, Farhat; Bashir, Farooq; Hossain, Tousif; Kayani, Zohra

2014-09-01

Zinc is an essential trace element that stimulates bone formation but it is also known as an inhibitor of apatite crystal growth. In this work addition of ZnO to SiO2-CaO-P2O5-Na2O-CaF2 glass-ceramic system was made by conventional melt-quenching technique. DSC curves showed that the addition of ZnO moved the endothermic and exothermic peaks to lower temperatures. X-ray diffraction analysis did not reveal any additional phase caused by ZnO addition and showed the presence of wollastonite and hydroxyapatite crystalline phases only in all the glass-ceramic samples. As bio-implant apatite forming ability is an essential condition, the surface reactivity of the prepared glass-ceramic specimens was studied in vitro in Kokubo's simulated body fluid (SBF) [1] with ion concentration nearly equal to human blood plasma for 30 days at 37 °C under static condition. Atomic absorption spectroscopy (AAS) was used to study the changes in element concentrations in soaking solutions and XRD, FT-IR and SEM were used to elucidate surface properties of prepared glass-ceramics, which confirmed the formation of HCAp on the surface of all glass-ceramics. It was found that the addition of ZnO had a positive effect on bioactivity of glass-ceramics and made it a potential candidate for restoration of damaged bones.

Shock and Release Data on Forsterite (Mg2SiO4) Single Crystals

NASA Astrophysics Data System (ADS)

Root, S.; Townsend, J. P.; Shulenburger, L.; Davies, E.; Kraus, R. G.; Spaulding, D.; Stewart, S. T.; Jacobsen, S. B.; Mattsson, T. R.

2016-12-01

The Kepler mission has discovered numerous extra-solar rocky planets with sizes ranging from Earth-size to the super-Earths with masses 40 times larger than Earth. The solid solution series of (Mg, Fe)2SiO4 (olivine) is a major component in the mantle of Earth and likely these extra-solar rocky planets. However, understanding how the (Mg, Fe)2SiO4 system behaves at Earth like and super-Earth like pressures is still unknown. Using Sandia's Z machine facility, we shock compress single crystal forsterite, the Mg end-member of the olivine series. Solid aluminum flyers are accelerated up to 28 km/s to generate steady shock states up to 950 GPa. Release states from the Hugoniot are determined as well. In addition to experiments, we perform density functional theory (DFT) calculations to examine the potential phases along the Mg2SiO4 Hugoniot. We compare our results to other recent shock experiments on forsterite. Sandia National Laboratories is a multiprogram laboratory managed and operated by Sandia Corporation, a wholly owned subsidiary of Lockheed Martin Corporation, for the U.S. Department of Energy's National Nuclear Security Administration under Contract No. DE-AC04-94AL85000. This work was performed under the auspices of the U.S. Department of Energy by Lawrence Livermore National Laboratory under Contract DE-AC52-07NA27344.

Assessment of role of iron ions on the physical and spectroscopic properties of multi-component Na2O-PbO-Bi2O3-SiO2 glass ceramics

NASA Astrophysics Data System (ADS)

Rao, M. V. Sambasiva; Kumar, A. Suneel; Ram, G. Chinna; Tirupataiah, Ch.; Rao, D. Krishna

2018-01-01

Multi-component glass ceramics composition Na2O-PbO-Bi2O3-SiO2 doped with different concentrations of Fe2O3 as nucleating agent were characterised by XRD, SEM (scanning electron microscope) and DTA (differential thermal analysis) techniques. Optical absorption, EPR, FTIR and Raman studies are also carried out on these glass ceramics. Absorption bands observed at about 457, 489, 678 and 820 nm are the characteristics of Fe3+ ions whereas the band observed at about 964 nm is due to Fe2+ ions. EPR studies suggested that Fe3+ ions entered in the lattice as tetragonally distorted octahedral symmetry or rhombic sites at low concentration of Fe2O3, whereas at higher concentration of Fe2O3 (beyond 1 mol%), the super exchange type of interactions between multivalency iron ions begin to dominate. FTIR and Raman spectra have revealed the behaviour of various structural units in the glass ceramic matrix. The analysis of these spectroscopic studies indicates that iron ions do exist in Fe3+ and Fe2+ state.

Core-Exsolved SiO2 Dispersal in the Earth's Mantle

NASA Astrophysics Data System (ADS)

Helffrich, George; Ballmer, Maxim D.; Hirose, Kei

2018-01-01

SiO2 may have been expelled from the core directly following core formation in the early stages of Earth's accretion and onward through the present day. On account of SiO2's low density with respect to both the core and the lowermost mantle, we examine the process of SiO2 accumulation at the core-mantle boundary (CMB) and its incorporation into the mantle by buoyant rise. Today, if SiO2 is 100-10,000 times more viscous than lower mantle material, the dimensions of SiO2 diapirs formed by the viscous Rayleigh-Taylor instability at the CMB would cause them to be swept into the mantle as inclusions of 100 m-10 km diameter. Under early Earth conditions of rapid heat loss after core formation, SiO2 diapirs of ˜1 km diameter could have risen independently of mantle flow to their level of neutral buoyancy in the mantle, trapping them there due to a combination of intrinsically high viscosity and neutral buoyancy. We examine the SiO2 yield by assuming Si + O saturation at the conditions found at the base of a magma ocean and find that for a range of conditions, dispersed bodies could reach as high as 8.5 vol % in parts of the lower mantle. At such low concentration, their effect on aggregate seismic wave speeds is within observational seismology uncertainty. However, their presence can account for small-scale scattering in the lower mantle due to the bodies' large-velocity contrast. We conclude that the shallow lower mantle (700-1,500 km depth) could harbor SiO2 released in early Earth times.

A highly efficient g-C3N4/SiO2 heterojunction: the role of SiO2 in the enhancement of visible light photocatalytic activity.

PubMed

Hao, Qiang; Niu, Xiuxiu; Nie, Changshun; Hao, Simeng; Zou, Wei; Ge, Jiangman; Chen, Daimei; Yao, Wenqing

2016-11-23

SiO 2 , an insulator, hardly has any photocatalytic acitivity due to its intrinsic property, and it is generally used as a hard template to increase the surface area of catalysts. However, in this work, we found that the surface state of the insulator SiO 2 can promote the migration of photogenerated charge carriers, leading to the enhancement of the photooxidation ability of graphitic carbon nitride (g-C 3 N 4 ). A one-pot calcination method was employed to prepare g-C 3 N 4 /SiO 2 composites using melamine and SiO 2 as precursors. The composites present considerably high photocatalytic degradation activities for 2,4-dichlorophenol (2,4-DCP) and rhodamine B (RhB) under visible light (λ > 420 nm) irradiation, which are about 1.53 and 4.18 times as high as those of bulk g-C 3 N 4 , respectively. The enhancement of the photocatalytic activity is due to the fact that the introduction of the insulator SiO 2 in g-C 3 N 4 /SiO 2 composites can greatly improve the specific surface area of the composites; more importantly, the impurity energy level of SiO 2 can help accelerate the separation and transfer of electron-hole pairs of g-C 3 N 4 . Electron paramagnetic resonance (EPR) spectroscopy and trapping experiments with different radical scavengers show that the main active species of g-C 3 N 4 are superoxide radicals, while holes also play a role in photodegradation. For g-C 3 N 4 /SiO 2 -5, besides superoxide radicals and holes, the effect of hydroxyl radicals was greatly improved. Finally, a possible mechanism for the photogenerated charge carrier migration of the g-C 3 N 4 /SiO 2 photocatalyst was proposed.

Field emission properties of SiO2-wrapped CNT field emitter.

PubMed

Lim, Yu Dian; Hu, Liangxing; Xia, Xin; Ali, Zishan; Wang, Shaomeng; Tay, Beng Kang; Aditya, Sheel; Miao, Jianmin

2018-01-05

Carbon nanotubes (CNTs) exhibit unstable field emission (FE) behavior with low reliability due to uneven heights of as-grown CNTs. It has been reported that a mechanically polished SiO 2 -wrapped CNT field emitter gives consistent FE performance due to its uniform CNT heights. However, there are still a lack of studies on the comparison between the FE properties of freestanding and SiO 2 -wrapped CNTs. In this study, we have performed a comparative study on the FE properties of freestanding and SiO 2 -wrapped CNT field emitters. From the FE measurements, freestanding CNT field emitter requires lower applied voltage of 5.5 V μm -1 to achieve FE current density of 22 mA cm -2 ; whereas SiO 2 -wrapped field emitter requires 8.5 V μm -1 to achieve the same current density. This can be attributed to the lower CNT tip electric field of CNTs embedded in SiO 2 , as obtained from the electric field simulation. Nevertheless, SiO 2 -wrapped CNTs show higher consistency in FE current than freestanding CNTs. Under repeated FE measurement, SiO 2 -wrapped CNT field emitter achieves consistent FE behavior from the 1st voltage sweep, whereas freestanding field emitter only achieved consistent FE performance after 3rd voltage sweep. At the same time, SiO 2 -wrapped CNTs exhibit better emission stability than freestanding CNTs over 4000 s continuous emission.

Field emission properties of SiO2-wrapped CNT field emitter

NASA Astrophysics Data System (ADS)

Lim, Yu Dian; Hu, Liangxing; Xia, Xin; Ali, Zishan; Wang, Shaomeng; Tay, Beng Kang; Aditya, Sheel; Miao, Jianmin

2018-01-01

Carbon nanotubes (CNTs) exhibit unstable field emission (FE) behavior with low reliability due to uneven heights of as-grown CNTs. It has been reported that a mechanically polished SiO2-wrapped CNT field emitter gives consistent FE performance due to its uniform CNT heights. However, there are still a lack of studies on the comparison between the FE properties of freestanding and SiO2-wrapped CNTs. In this study, we have performed a comparative study on the FE properties of freestanding and SiO2-wrapped CNT field emitters. From the FE measurements, freestanding CNT field emitter requires lower applied voltage of 5.5 V μm-1 to achieve FE current density of 22 mA cm-2 whereas SiO2-wrapped field emitter requires 8.5 V μm-1 to achieve the same current density. This can be attributed to the lower CNT tip electric field of CNTs embedded in SiO2, as obtained from the electric field simulation. Nevertheless, SiO2-wrapped CNTs show higher consistency in FE current than freestanding CNTs. Under repeated FE measurement, SiO2-wrapped CNT field emitter achieves consistent FE behavior from the 1st voltage sweep, whereas freestanding field emitter only achieved consistent FE performance after 3rd voltage sweep. At the same time, SiO2-wrapped CNTs exhibit better emission stability than freestanding CNTs over 4000 s continuous emission.

Comparisons between TiO2- and SiO2-flux assisted TIG welding processes.

PubMed

Tseng, Kuang-Hung; Chen, Kuan-Lung

2012-08-01

This study investigates the effects of flux compounds on the weld shape, ferrite content, and hardness profile in the tungsten inert gas (TIG) welding of 6 mm-thick austenitic 316 L stainless steel plates, using TiO2 and SiO2 powders as the activated fluxes. The metallurgical characterizations of weld metal produced with the oxide powders were evaluated using ferritoscope, optical microscopy, and Vickers microhardness test. Under the same welding parameters, the penetration capability of TIG welding with TiO2 and SiO2 fluxes was approximately 240% and 292%, respectively. A plasma column made with SiO2 flux exhibited greater constriction than that made with TiO2 flux. In addition, an anode root made with SiO2 flux exhibited more condensation than that made with TiO2 flux. Results indicate that energy density of SiO2-flux assisted TIG welding is higher than that of TiO2-flux assisted TIG welding.

Surface spins disorder in uncoated and SiO2 coated maghemite nanoparticles

NASA Astrophysics Data System (ADS)

Zeb, F.; Nadeem, K.; Shah, S. Kamran Ali; Kamran, M.; Gul, I. Hussain; Ali, L.

2017-05-01

We studied the surface spins disorder in uncoated and silica (SiO2) coated maghemite (γ-Fe2O3) nanoparticles using temperature and time dependent magnetization. The average crystallite size for SiO2 coated and uncoated nanoparticles was about 12 and 29 nm, respectively. Scanning electron microscopy (SEM) showed that the nanoparticles are spherical in shape and well separated. Temperature scans of zero field cooled (ZFC)/field cooled (FC) magnetization measurements showed lower average blocking temperature (TB) for SiO2 coated maghemite nanoparticles as compared to uncoated nanoparticles. The saturation magnetization (Ms) of SiO2 coated maghemite nanoparticles was also lower than the uncoated nanoparticles and is attributed to smaller average crystallite size of SiO2 coated nanoparticles. For saturation magnetization vs. temperature data, Bloch's law (M(T)= M(0).(1- BTb)) was fitted well for both uncoated and SiO2 coated nanoparticles and yields: B =3×10-7 K-b, b=2.22 and B=0.0127 K-b, b=0.57 for uncoated and SiO2 coated nanoparticles, respectively. Higher value of B for SiO2 coated nanoparticles depicts decrease in exchange coupling due to enhanced surface spins disorder (broken surface bonds) as compared to uncoated nanoparticles. The Bloch's exponent b was decreased for SiO2 coated nanoparticles which is due to their smaller average crystallite size or finite size effects. Furthermore, a sharp increase of coercivity at low temperatures (<25 K) was observed for SiO2 coated nanoparticles which is also due to contribution of increased surface anisotropy or frozen surface spins in these smaller nanoparticles. The FC magnetic relaxation data was fitted to stretched exponential law which revealed slower magnetic relaxation for SiO2 coated nanoparticles. All these measurements revealed smaller average crystallite size and enhanced surface spins disorder in SiO2 coated nanoparticles than in uncoated γ-Fe2O3 nanoparticles.

Quasi-solid state rechargeable Na-CO2 batteries with reduced graphene oxide Na anodes.

PubMed

Hu, Xiaofei; Li, Zifan; Zhao, Yaran; Sun, Jianchao; Zhao, Qing; Wang, Jianbin; Tao, Zhanliang; Chen, Jun

2017-02-01

Na-CO 2 batteries using earth-abundant Na and greenhouse gas CO 2 are promising tools for mobile and stationary energy storage, but they still pose safety risks from leakage of liquid electrolyte and instability of the Na metal anode. These issues result in extremely harsh operating conditions of Na-CO 2 batteries and increase the difficulty of scaling up this technology. We report the development of quasi-solid state Na-CO 2 batteries with high safety using composite polymer electrolyte (CPE) and reduced graphene oxide (rGO) Na anodes. The CPE of PVDF-HFP [poly(vinylidene fluoride- co -hexafluoropropylene)]-4% SiO 2 /NaClO 4 -TEGDME (tetraethylene glycol dimethyl ether) has high ion conductivity (1.0 mS cm -1 ), robust toughness, a nonflammable matrix, and strong electrolyte-locking ability. In addition, the rGO-Na anode presents fast and nondendritic Na + plating/stripping (5.7 to 16.5 mA cm -2 ). The improved kinetics and safety enable the constructed rGO-Na/CPE/CO 2 batteries to successfully cycle in wide CO 2 partial pressure window (5 to 100%, simulated car exhaust) and especially to run for 400 cycles at 500 mA g -1 with a fixed capacity of 1000 mA·hour g -1 in pure CO 2 . Furthermore, we scaled up the reversible capacity to 1.1 A·hour in pouch-type batteries (20 × 20 cm, 10 g, 232 Wh kg -1 ). This study makes quasi-solid state Na-CO 2 batteries an attractive prospect.

Quasi–solid state rechargeable Na-CO2 batteries with reduced graphene oxide Na anodes

PubMed Central

Hu, Xiaofei; Li, Zifan; Zhao, Yaran; Sun, Jianchao; Zhao, Qing; Wang, Jianbin; Tao, Zhanliang; Chen, Jun

2017-01-01

Na-CO2 batteries using earth-abundant Na and greenhouse gas CO2 are promising tools for mobile and stationary energy storage, but they still pose safety risks from leakage of liquid electrolyte and instability of the Na metal anode. These issues result in extremely harsh operating conditions of Na-CO2 batteries and increase the difficulty of scaling up this technology. We report the development of quasi–solid state Na-CO2 batteries with high safety using composite polymer electrolyte (CPE) and reduced graphene oxide (rGO) Na anodes. The CPE of PVDF-HFP [poly(vinylidene fluoride-co-hexafluoropropylene)]–4% SiO2/NaClO4–TEGDME (tetraethylene glycol dimethyl ether) has high ion conductivity (1.0 mS cm−1), robust toughness, a nonflammable matrix, and strong electrolyte-locking ability. In addition, the rGO-Na anode presents fast and nondendritic Na+ plating/stripping (5.7 to 16.5 mA cm−2). The improved kinetics and safety enable the constructed rGO-Na/CPE/CO2 batteries to successfully cycle in wide CO2 partial pressure window (5 to 100%, simulated car exhaust) and especially to run for 400 cycles at 500 mA g−1 with a fixed capacity of 1000 mA·hour g−1 in pure CO2. Furthermore, we scaled up the reversible capacity to 1.1 A·hour in pouch-type batteries (20 × 20 cm, 10 g, 232 Wh kg−1). This study makes quasi–solid state Na-CO2 batteries an attractive prospect. PMID:28164158

Diffusion reaction of oxygen in HfO2/SiO2/Si stacks.

PubMed

Ferrari, S; Fanciulli, M

2006-08-03

We study the oxidation mechanism of silicon in the presence of a thin HfO2 layer. We performed a set of annealing in 18O2 atmosphere on HfO2/SiO2/Si stacks observing the 18O distribution in the SiO2 layer with time-of-flight secondary ion mass spectrometry (ToF-SIMS). The 18O distribution in HfO2/SiO2/Si stacks upon 18O2 annealing suggests that what is responsible for SiO2 growth is the molecular O2, whereas no contribution is found of the atomic oxygen to the oxidation. By studying the dependence of the oxidation velocity from oxygen partial pressure and annealing temperature, we demonstrate that the rate-determining step of the oxidation is the oxygen exchange at the HfO2/SiO2 interface. When moisture is chemisorbed in HfO2 films, the oxidation of the underlying silicon substrate becomes extremely fast and its kinetics can be described as a wet silicon oxidation process. The silicon oxidation during O2 annealing of the atomic layer deposited HfO2/Si is fast in its early stage due to chemisorbed moisture and becomes slow after the first 10 s.

High Temperature Aerogels in the Al2O3-SiO2 System

NASA Technical Reports Server (NTRS)

Hurwitz, Frances I.; Aranda, Denisse V.; Gallagher, Meghan E.

2008-01-01

Al2O3-SiO2 aerogels are of interest as constituents of thermal insulation systems for use at high temperatures. Al2O3 and mullite aerogels are expected to crystallize at higher temperatures than their SiO2 counterparts, hence avoiding the shrinkages that accompany the formation of lower temperature SiO2 phases and preserving pore structures into higher temperature regimes. The objective of this work is to determine the influence of processing parameters on shrinkage, gel structure (including surface area, pore size and distribution) and pyrolysis behavior.

Effect of alkali earth oxides on hydroxy-carbonated apatite nano layer formation for SiO2-BaO-CaO-Na2O-P2O5 glass system

NASA Astrophysics Data System (ADS)

Kiran, P.; Ramakrishna, V.; Shashikala, H. D.; Udayashankar, N. K.

2017-11-01

Barium soda lime phosphosilicate [(58SiO2-(32 - x)BaO- xCao-6Na2O-4P2O5 (where x = 15, 20, 25 and 30 mol%)] samples were synthesised using conventional sol-gel method at 700 °C sintering temperature. Thermal, structural properties were studied using thermo gravimetric analysis and differential thermal analysis, X-ray diffraction, scanning electron microscopy, fourier transform infrared and Raman spectroscopy. Using Raman spectra non-bridging oxygen concentrations were estimated. The hydroxy-carbonated apatite (HCA) layer formation on samples was analysed for 7 days using simulated body fluid (SBF) soaked samples. The growth of HCA layers self-assembled on the sample surface was discussed as a function of NBO/BO ratio. Results indicated that the number of Ca2+ ions released into SBF solution in dissolution process and weight loss of SB-treated samples vary with NBO/BO ratio. The changes in NBO/BO ratios were observed to be proportional to HCA forming ability of barium soda lime phosphosilicate glasses.

Mineral-solution equilibria—III. The system Na 2OAl 2O 3SiO 2H 2OHCl

NASA Astrophysics Data System (ADS)

Popp, Robert K.; Frantz, John D.

1980-07-01

Chemical equilibrium between sodium-aluminum silicate minerals and chloride bearing fluid has been experimentally determined in the range 500-700°C at 1 kbar, using rapid-quench hydrothermal methods and two modifications of the Ag + AgCl acid buffer technique. The temperature dependence of the thermodynamic equilibrium constant ( K) for the reaction NaAlSi 3O 8 + HCl o = NaCl o + 1/2Al 2SiO 5, + 5/2SiO 2 + 1/2H 2O Albite Andalusite Qtz. K = (a NaCl o) /(a H 2O ) 1/2/(a HCl o) can be described by the following equation: log k = -4.437 + 5205.6/ T( K) The data from this study are consistent with experimental results reported by MONTOYA and HEMLEY (1975) for lower temperature equilibria defined by the assemblages albite + paragonite + quartz + fluid and paragonite + andalusite + quartz + fluid. Values of the equilibrium constants for the above reactions were used to estimate the difference in Gibbs free energy of formation between NaCl o and HCl o in the range 400-700°C and 1-2 kbar. Similar calculations using data from phase equilibrium studies reported in the literature were made to determine the difference in Gibbs free energy of formation between KCl o and HCl o. These data permit modelling of the chemical interaction between muscovite + kspar + paragonite + albite + quartz assemblages and chloride-bearing hydrothermal fluids.

SiO2/TiO2/Ag multilayered microspheres: Preparation, characterization, and enhanced infrared radiation property

NASA Astrophysics Data System (ADS)

Ye, Xiaoyun; Cai, Shuguang; Zheng, Chan; Xiao, Xueqing; Hua, Nengbin; Huang, Yanyi

2015-08-01

SiO2/TiO2/Ag core-shell multilayered microspheres were successfully synthesized by the combination of anatase of TiO2 modification on the surfaces of SiO2 spheres and subsequent Ag nanoparticles deposition and Ag shell growth with face-centered cubic (fcc) Ag. The composites were characterized by TEM, FT-IR, UV-vis, Raman spectroscopy and XRD, respectively. The infrared emissivity values during 8-14 μm wavelengths of the composites were measured. The results revealed that TiO2 thin layers with the thickness of ∼10 nm were coated onto the SiO2 spheres of ∼220 nm in diameter. The thickness of the TiO2 layers was controlled by varying the amount of TBOT precursor. Homogeneous Ag nanoparticles of ∼20 nm in size were successfully deposited by ultrasound on the surfaces of SiO2/TiO2 composites, followed by complete covering of Ag shell. The infrared emissivity value of the SiO2/TiO2 composites was decreased than that of pure SiO2. Moreover, the introduction of the Ag brought the remarkably lower infrared emissivity value of the SiO2/TiO2/Ag multilayered microspheres with the lowest value down to 0.424. Strong chemical effects in the interface of SiO2/TiO2 core-shell composites and high reflection performance of the metal Ag are two decisive factors for the improved infrared radiation performance of the SiO2/TiO2/Ag multilayered microspheres.

Preparation of SiO2@Ag Composite Nanoparticles and Their Antimicrobial Activity.

PubMed

Qin, Rui; Li, Guian; Pan, Liping; Han, Qingyan; Sun, Yan; He, Qiao

2017-04-01

At normal atmospheric temperature, the modified sol–gel method was employed to synthesize SiO2 nanospheres (SiO2 NSs) whose average size was about 352 nm. Silver nanoparticles (Ag NPs) were uniformly distributed on the surface of SiO2 nanospheres (SiO2 NSs) by applying chemical reduction method at 95 °C and the size of silver nanoparticles (Ag NPs) could be controlled by simply tuning the reaction time and the concentration of sodium citrate. Besides, the size, morphology, structure and optical absorption properties of SiO2@Ag composite nanoparticles were measured and characterized by laser particle size analyzer (LPSA), transmission electron microscope (TEM), scanning electron microscope (SEM), X-ray diffraction (XRD) and ultraviolet visible absorption spectrometer (UV-Vis), respectively. Furthermore, antimicrobial effect experiments that against gram-negative bacteria (E. coli) and gram-positive bacteria (S. aureus) were carried out to characterize the antibacterial activity of synthesized SiO2@Ag composite nanoparticles. The results show that the prepared SiO2@Ag composite nanoparticles have strong antimicrobial activity, which is associated with the size of silver nanoparticles.

SiO2 Glass Density to Lower-Mantle Pressures

NASA Astrophysics Data System (ADS)

Petitgirard, Sylvain; Malfait, Wim J.; Journaux, Baptiste; Collings, Ines E.; Jennings, Eleanor S.; Blanchard, Ingrid; Kantor, Innokenty; Kurnosov, Alexander; Cotte, Marine; Dane, Thomas; Burghammer, Manfred; Rubie, David C.

2017-11-01

The convection or settling of matter in the deep Earth's interior is mostly constrained by density variations between the different reservoirs. Knowledge of the density contrast between solid and molten silicates is thus of prime importance to understand and model the dynamic behavior of the past and present Earth. SiO2 is the main constituent of Earth's mantle and is the reference model system for the behavior of silicate melts at high pressure. Here, we apply our recently developed x-ray absorption technique to the density of SiO2 glass up to 110 GPa, doubling the pressure range for such measurements. Our density data validate recent molecular dynamics simulations and are in good agreement with previous experimental studies conducted at lower pressure. Silica glass rapidly densifies up to 40 GPa, but the density trend then flattens to become asymptotic to the density of SiO2 minerals above 60 GPa. The density data present two discontinuities at ˜17 and ˜60 GPa that can be related to a silicon coordination increase from 4 to a mixed 5 /6 coordination and from 5 /6 to sixfold, respectively. SiO2 glass becomes denser than MgSiO3 glass at ˜40 GPa , and its density becomes identical to that of MgSiO3 glass above 80 GPa. Our results on SiO2 glass may suggest that a variation of SiO2 content in a basaltic or pyrolitic melt with pressure has at most a minor effect on the final melt density, and iron partitioning between the melts and residual solids is the predominant factor that controls melt buoyancy in the lowermost mantle.

Magnetic studies of SiO2 coated CoFe2O4 nanoparticles

NASA Astrophysics Data System (ADS)

Limaye, Mukta V.; Singh, Shashi B.; Das, Raja; Poddar, Pankaj; Abyaneh, Majid K.; Kulkarni, Sulabha K.

2017-11-01

Oleic acid capped CoFe2O4 nanoparticles which exhibit a high coercivity of ∼9.47 kOe at room temperature were coated with a robust coating of SiO2. We have used chemical synthesis method to obtain SiO2 coated CoFe2O4 nanoparticles with different weight percentages of CoFe2O4 in SiO2 (1.5, 3.1 and 4.8 wt.%). The morphological investigation of the coated nanoparticles by transmission electron microscopy shows that the particles are spherical with average size ∼160 nm. Infrared spectroscopy reveals that oleic acid capping on the surface of CoFe2O4 nanoparticles is retained after silica coating process. The complete coating of SiO2 on CoFe2O4 nanoparticles is confirmed by X-ray photoelectron spectroscopy as there is no signature of cobalt or iron ions on the surface. Magnetic measurements show that coercivity of SiO2 coated CoFe2O4 particles remains more or less unaffected as in CoFe2O4 nanoparticles at room temperature. In addition, the temperature dependent magnetic measurements show that at 5 K the CoFe2O4 and SiO2 coated 1.5 wt.% CoFe2O4 samples exhibit a very high value of coercivity (∼20 kOe) which is more than twice as compared to room temperature coercivity value (∼9.47 kOe). We conclude that silica coating in our study does not significantly affect the coercivity of CoFe2O4 nanoparticles.

Physical and Electrical Properties of SiO2 Layer Synthesized by Eco-Friendly Method

NASA Astrophysics Data System (ADS)

Jong-Woong Kim,; Young-Seok Kim,; Sung-Jei Hong,; Tae-Hwan Hong,; Jeong-In Han,

2010-05-01

SiO2 thin film has a wide range of applications, including insulation layers in microelectronic devices, such as semiconductors and flat panel displays, due to its advantageous characteristics. Herein, we developed a new eco-friendly method for manufacturing SiO2 nanoparticles and, thereby, SiO2 paste to be used in the digital printing process for the fabrication of SiO2 film. By excluding harmful Cl- and NO3- elements from the SiO2 nanoparticle synthetic process, we were able to lower the heat treatment temperature for the SiO2 precursor from 600 to 300 °C and the diameter of the final SiO2 nanoparticles to about 14 nm. The synthesized SiO2 nanoparticles were dispersed in an organic solvent with additives to make a SiO2 paste for feasibility testing. The SiO2 paste was printed onto a glass substrate to test the feasibility of using it for digital printing. The insulation resistance of the printed film was high enough for it to be used as an insulation layer for passivation.

Understanding the magnetic behavior of heat treated CaO-P2O5-Na2O-Fe2O3-SiO2 bioactive glass using electron paramagnetic resonance studies

NASA Astrophysics Data System (ADS)

Shankhwar, Nisha; Kothiyal, G. P.; Srinivasan, A.

2014-09-01

Bioactive glass of composition 41CaO-44SiO2-4P2O5-8Fe2O3-3Na2O has been heat treated in the temperature (TA) range of 750-1150 °C for time periods (tA) ranging from 1 h to 3 h to yield magnetic bioactive glass ceramics (MBCs). X-ray diffraction studies indicate the presence of bone mineral (hydroxyapatite and wollastonite) and magnetic (magnetite and α-hematite) phases in nanocrystalline form in the MBCs. Electron paramagnetic resonance (EPR) study was carried out to understand the variation in saturation magnetization and coercivity of the MBCs with TA and tA. These studies reveal the nature and amount of iron ions present in the MBCs and their interaction in the glassy oxide matrix as a function of annealing parameters. The deterioration in the magnetic properties of the glass heat treated above 1050 °C is attributed to the crystallization of the non-magnetic α-hematite phase. These results are expected to be useful in the application of these MBCs as thermoseeds in hyperthermia treatment of cancer.

SiO_{2} Glass Density to Lower-Mantle Pressures.

PubMed

Petitgirard, Sylvain; Malfait, Wim J; Journaux, Baptiste; Collings, Ines E; Jennings, Eleanor S; Blanchard, Ingrid; Kantor, Innokenty; Kurnosov, Alexander; Cotte, Marine; Dane, Thomas; Burghammer, Manfred; Rubie, David C

2017-11-24

The convection or settling of matter in the deep Earth's interior is mostly constrained by density variations between the different reservoirs. Knowledge of the density contrast between solid and molten silicates is thus of prime importance to understand and model the dynamic behavior of the past and present Earth. SiO_{2} is the main constituent of Earth's mantle and is the reference model system for the behavior of silicate melts at high pressure. Here, we apply our recently developed x-ray absorption technique to the density of SiO_{2} glass up to 110 GPa, doubling the pressure range for such measurements. Our density data validate recent molecular dynamics simulations and are in good agreement with previous experimental studies conducted at lower pressure. Silica glass rapidly densifies up to 40 GPa, but the density trend then flattens to become asymptotic to the density of SiO_{2} minerals above 60 GPa. The density data present two discontinuities at ∼17 and ∼60  GPa that can be related to a silicon coordination increase from 4 to a mixed 5/6 coordination and from 5/6 to sixfold, respectively. SiO_{2} glass becomes denser than MgSiO_{3} glass at ∼40  GPa, and its density becomes identical to that of MgSiO_{3} glass above 80 GPa. Our results on SiO_{2} glass may suggest that a variation of SiO_{2} content in a basaltic or pyrolitic melt with pressure has at most a minor effect on the final melt density, and iron partitioning between the melts and residual solids is the predominant factor that controls melt buoyancy in the lowermost mantle.

On the existence of a high-temperature polymorph of Na2Ca6Si4O15—implications for the phase equilibria in the system Na2O-CaO-SiO2

NASA Astrophysics Data System (ADS)

Kahlenberg, Volker; Maier, Matthias

2016-12-01

Singe crystals of a new high-temperature polymorph of Na2Ca6Si4O15 have been obtained from solid state reactions performed at 1300 °C. The basic crystallographic data of this so-called β-phase at ambient conditions are as follows: space group P1 c1, a = 9.0112(5) Å, b = 7.3171(5) Å, c = 10.9723(6) Å, β = 107.720(14)°, V = 689.14(7) Å3, Z = 2. The crystals showed twinning by reticular merohedry (mimicking an orthorhombic C-centred unit cell) which was accounted for during data processing and structure solution. Structure determination was accomplished by direct methods. Least-squares refinements resulted in a residual of R(|F|) = 0.043 for 5811 observed reflections with I > 2σ(I). From a structural point of view β-Na2Ca6Si4O15 can be attributed to the group of mixed-anion silicates containing [Si2O7]-dimers as well as isolated [SiO4]-tetrahedra in the ratio 1:2, i.e. more precisely the formula can be written as Na2Ca6[SiO4]2[Si2O7]. The tetrahedral groups are arranged in layers parallel to (100). Sodium and calcium cations are located between the silicate anions for charge compensation and are coordinated by six to eight nearest oxygen ligands. Alternatively, the structure can be described as a mixed tetrahedral-octahedral framework based on kröhnkite-type [Ca(SiO4)2O2]-chains in which the CaO6-octahedra are corner-linked to bridging SiO4-tetrahedra. The infinite chains are running parallel to [001] and are concentrated in layers parallel to (010). Adjacent layers are shifted relative to each other by an amount of +δ or -δ along a*. Consequently, a …ABABAB… stacking sequence is created. A detailed comparison with related structures such as α-Na2Ca6Si4O15 and other A2B6Si4O15 representatives including topological as well as group theoretical aspects is presented. There are strong indications that monoclinic Na2Ca3Si2O8 mentioned in earlier studies is actually misinterpreted β-Na2Ca6Si4O15. In addition to the detailed crystallographic analysis of

Effect of the SiO2 Support on the Catalytic Performance of Ag/ZrO2/SiO2 Catalysts for the Single-Bed Production of Butadiene from Ethanol

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dagle, Vanessa; Flake, Matthew D.; Lemmon, Teresa

2018-05-18

A ternary Ag/ZrO2/SiO2 catalyst system was studied for the single-step conversion of ethanol to butadiene by varying the catalyst composition (Ag, Ir, or Pt metal component, Ag/ZrO2 loading, and choice of SiO2 support) and operating conditions (space velocity and feed gas composition). Exceptional catalytic performance was achieved over a 1%Ag/4%ZrO2/SiO2-SBA-16 catalyst leading to 99% conversion and 71% butadiene selectivity while operating under mild conditions (325ºC, 1 atm, 0.23 hr-1). Several classes of silica (i.e., silica gels, fumed silicas, meoporous silicas) were evaluated as support, and SBA-16 was found to be the most promising. The nature of the SiO2 support wasmore » found to have a strong influence on both conversion and selectivity. Higher SiO2 catalyst surface areas lead to greater conversion due to increased Ag dispersion thus accelerating the initial ethanol dehydrogenation reaction. By independently varying Ag and ZrO2 loading, Ag was found to be the main component affecting ethanol conversion. Butadiene selectivity varied depending on the concentration of ZrO2 and acidic characteristics of the SiO2 support. A direct relationship between butadiene selectivity and concentration of Lewis acid sites was evidenced. Also, adding H2 to the feed had little effect on conversion while improving catalytic stability, however, selectivity to butadiene was decreased. Finally, catalyst regenerability was successfully demonstrated for several cycles.« less

Effect of the SiO 2 support on the catalytic performance of Ag/ZrO 2 /SiO 2 catalysts for the single-bed production of butadiene from ethanol

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dagle, Vanessa Lebarbier; Flake, Matthew D.; Lemmon, Teresa L.

A ternary Ag/ZrO2/SiO2 catalyst system was studied for the single-step conversion of ethanol to butadiene by varying the catalyst composition (Ag, Ir, or Pt metal component, Ag/ZrO2 loading, and choice of SiO2 support) and operating conditions (space velocity and feed gas composition). Exceptional catalytic performance was achieved over a 1%Ag/4%ZrO2/SiO2-SBA-16 catalyst leading to 99% conversion and 71% butadiene selectivity while operating under mild conditions (325ºC, 1 atm, 0.23 hr-1). Several classes of silica (i.e., silica gels, fumed silicas, meoporous silicas) were evaluated as support, and SBA-16 was found to be the most promising. The nature of the SiO2 support wasmore » found to have a strong influence on both conversion and selectivity. Higher SiO2 catalyst surface areas lead to greater conversion due to increased Ag dispersion thus accelerating the initial ethanol dehydrogenation reaction. By independently varying Ag and ZrO2 loading, Ag was found to be the main component affecting ethanol conversion. Butadiene selectivity varied depending on the concentration of ZrO2 and acidic characteristics of the SiO2 support. A direct relationship between butadiene selectivity and concentration of Lewis acid sites was evidenced. Also, adding H2 to the feed had little effect on conversion while improving catalytic stability, however, selectivity to butadiene was decreased. Finally, catalyst regenerability was successfully demonstrated for several cycles.« less

Magnetism from Fe2O3 nanoparticles embedded in amorphous SiO2 matrix

NASA Astrophysics Data System (ADS)

Sendil Kumar, A.; Bhatnagar, Anil K.

2018-02-01

Fe2O3 nanoparticles are embedded in amorphous SiO2 matrix by coprecipitation method with varying concentrations. Conditions are optimized to get almost monodispersed Fe2O3 nanoparticles with high chemical stability. Microstructure of synthesized nanoparticles is well characterized and found that Fe2O3 is in nanocrystalline form and embedded uniformly in amorphous SiO2 matrix. Enhanced surface reactivity is found for nanoparticles which influences physical properties of the SiO2 supported Fe2O3 system due to adsorption. In oxide nanoparticles, significant number of defect sites at the surface is expected but when supported medium such as SiO2 it reduces this defect concentration. Field- and temperature-dependent magnetisation studies on these samples show superparamagnetic behaviour. Superparamagnetic behaviour is seen in all the concentration systems but the coercivity observed in the lower concentration systems is found to be anomalous compared to that of higher concentrations. The observed magnetic behaviour comes from either unsaturated bond existing due to the absence of anions at the surface of nanoparticles or reconstruction of atomic orbitals taking place at interface of Fe2O3-SiO2 system.

Investigating the solubility and cytocompatibility of CaO-Na2 O-SiO2 /TiO2 bioactive glasses.

PubMed

Wren, Anthony W; Coughlan, Aisling; Smith, Courtney M; Hudson, Sarah P; Laffir, Fathima R; Towler, Mark R

2015-02-01

This study aims to investigate the solubility of a series of titanium (TiO2 )-containing bioactive glasses and their subsequent effect on cell viability. Five glasses were synthesized in the composition range SiO2 -Na2 O-CaO with 5 mol % of increments TiO2 substituted for SiO2 . Glass solubility was investigated with respect to (1) exposed surface area, (2) particle size, (3) incubation time, and (4) compositional effects. Ion release profiles showed that sodium (Na(+) ) presented high release rates after 1 day and were unchanged between 7 and 14 days. Calcium (Ca(2+) ) release presented a significant change at each time period and was also composition dependent, where a reduction in Ca(2+) release is observed with an increase in TiO2 concentration. Silica (Si(4+) ) release did not present any clear trends while no titanium (Ti(4+) ) was released. Cell numbers were found to increase up to 44%, compared to the growing control population, with a reduction in particle size and with the inclusion of TiO2 in the glass composition. © 2014 Wiley Periodicals, Inc.

Nd2O3-SiO2 nanocomposites: A simple sonochemical preparation, characterization and photocatalytic activity.

PubMed

Zinatloo-Ajabshir, Sahar; Mortazavi-Derazkola, Sobhan; Salavati-Niasari, Masoud

2018-04-01

Nd 2 O 3 -SiO 2 nanocomposites with enhanced photocatalytic activity have been obtained through simple and rapid sonochemical route in presence of putrescine as a new basic agent, for the first time. The influence of the mole ratio of Si:Nd, basic agent and ultrasonic power have been optimized to obtain the best Nd 2 O 3 -SiO 2 nanocomposites on shape, size and photocatalytic activity. The produced Nd 2 O 3 -SiO 2 nanocomposites have been characterized utilizing XRD, EDX, TEM, FT-IR, DRS and FESEM. Application of the as-formed Nd 2 O 3 -SiO 2 nano and bulk structures as photocatalyst with photodegradation of methyl violet contaminant under ultraviolet illumination was compared. Results demonstrated that SiO 2 has remarkable effect on catalytic performance of Nd 2 O 3 photocatalyst for decomposition. By introducing of SiO 2 to Nd 2 O 3 , decomposition efficiency of Nd 2 O 3 toward methyl violet contaminant under ultraviolet illumination was increased. Copyright © 2017 Elsevier B.V. All rights reserved.

Olivine-modified spinel-spinel transitions in the system Mg2SiO4-Fe2SiO4: Calorimetric measurements, thermochemical calculation, and geophysical application

NASA Astrophysics Data System (ADS)

Akaogi, Masaki; Ito, Eiji; Navrotsky, Alexandra

1989-11-01

The olivine(α)-modified spinel(β)-spinel (γ) transitions in the system Mg2SiO4-Fe2SiO4 were studied by high-temperature solution calorimetry. Enthalpies of the β-γ and a α-γ transitions in Mg2SiO4 at 975 K and of the α-γ transition in Fe2SiO4 at 298 K were measured. The γ solid solution showed a positive enthalpy of mixing. Phase relations at high pressures and high temperatures were calculated from these thermochemical data including correction for the effect of nonideality of α, β, and γ solid solutions. The calculated phase diagrams agree well with those determined experimentally by Katsura and Ito very recently. The α - (Mg0.89, Fe0.11)2SiO4 transforms to β through a region of α+β without passing through the α+γ phase field at around 400 km depth in the mantle with an interval of about 18(±5) km. Temperatures at 390 and 650 km depths are estimated to be about 1673 and 1873 K, respectively, assuming an adiabatic geotherm.

Electrical characteristics of SiO2/ZrO2 hybrid tunnel barrier for charge trap flash memory

NASA Astrophysics Data System (ADS)

Choi, Jaeho; Bae, Juhyun; Ahn, Jaeyoung; Hwang, Kihyun; Chung, Ilsub

2017-08-01

In this paper, we investigate the electrical characteristics of SiO2/ZrO2 hybrid tunnel oxide in metal-Al2O3-SiO2-Si3N4-SiO2-silicon (MAONOS) structure in an effort to improve program and erase speed as well as retention characteristics. Inserting ZrO2 into the conventional MAONOS structure increased the programmed V th variation to 6.8 V, and increased the erased V th variation to -3.7 V at 17 MV/cm. The results can be understood in terms of reducing the Fowler-Nordheim (F/N) tunneling barrier due to high-k ZrO2 in the tunneling oxide. In addition, Zr diffusion in SiO2 caused the formation of Zr x Si1- x O2 at the interface region, which reduced the energy band gap of SiO2. The retention property of the hybrid tunnel oxide varied depending on the thickness of SiO2. For thin SiO2 less than 30 Å, the retention properties of the tunneling oxides were poor compared with those of the SiO2 only tunneling oxides. However, the hybrid tunneling oxides with SiO2 thickness thicker than 40 Å yielded improved retention behavior compared with those of the SiO2-only tunneling oxides. The detailed analysis in charge density of ZrO2 was carried out by ISPP test. The obtained charge density was quite small compared to that of the total charge density, which indicates that the inserted ZrO2 layer serves as a tunneling material rather than charge storage dielectric.

Preparation of SiO2-Protecting Metallic Fe Nanoparticle/SiO2 Composite Spheres for Biomedical Application

PubMed Central

Hsieh, Pin-Wei; Tseng, Ching-Li; Kuo, Dong-Hau

2015-01-01

Functionalized Fe nanoparticles (NPs) have played an important role in biomedical applications. In this study, metallic Fe NPs were deposited on SiO2 spheres to form a Fe/SiO2 composite. To protect the Fe from oxidation, a thin SiO2 layer was coated on the Fe/SiO2 spheres thereafter. The size and morphology of the SiO2@Fe/SiO2 composite spheres were examined by transmission electron microscopy (TEM). The iron form and its content and magnetic properties were examined by X-ray diffraction (XRD), inductively-coupled plasma mass spectrometry (ICP-MS) and a superconducting quantum interference device (SQUID). The biocompatibility of the SiO2@Fe/SiO2 composite spheres was examined by Cell Counting Kit-8 (CCK-8) and lactate dehydrogenase (LDH) tests. The intracellular distribution of the SiO2@Fe/SiO2 composite spheres was observed using TEM. XRD analysis revealed the formation of metallic iron on the surface of the SiO2 spheres. According to the ICP-MS and SQUID results, using 0.375 M FeCl3·6H2O for Fe NPs synthesis resulted in the highest iron content and magnetization of the SiO2@Fe/SiO2 spheres. Using a dye loading experiment, a slow release of a fluorescence dye from SiO2@Fe/SiO2 composite spheres was confirmed. The SiO2@Fe/SiO2 composite spheres co-cultured with L929 cells exhibit biocompatibility at concentrations <16.25 µg/mL. The TEM images show that the SiO2@Fe/SiO2 composite spheres were uptaken into the cytoplasm and retained in the endosome. The above results demonstrate that the SiO2@Fe/SiO2 composite spheres could be used as a multi-functional agent, such as a magnetic resonance imaging (MRI) contrast agent or drug carriers in biomedical applications.

Direct fabrication of hybrid nanofibres composed of SiO2-PMMA nanospheres via electrospinning.

PubMed

Zhang, Ran; Shang, Tinghua; Yang, Guang; Jia, Xiaolong; Cai, Qing; Yang, Xiaoping

2016-08-01

The direct fabrication of hybrid nanofibres composed of poly(methyl methacrylate)-grafted SiO2 (SiO2-PMMA) nanospheres via electrospinning was investigated in detail. SiO2-PMMA nanospheres were successfully prepared, with the SiO2 nanospheres synthesized via the Stober method, followed by in situ surface-initiated atom transfer radical polymerization of methyl methacrylate (MMA). Electrospinning was carried out with N,N-dimethylformamide (DMF) as the solvent to disperse SiO2-PMMA nanospheres. The size of the SiO2 core, the molecular weight of the PMMA shell and the concentration of the SiO2-PMMA/DMF solution all had substantial effects on the morphology and structure of electrospun nanofibres composed of SiO2-PMMA nanospheres. When these determining factors were well-tailored, it was found that one-dimensional necklace-like nanofibres were obtained, with SiO2-PMMA nanospheres aligned one by one along the fibre. The successful fabrication of nanofibres by directly electrospinning the SiO2-PMMA/DMF solution verified that polymer-grafted particles possess polymer-like characteristics, which endowed them with the ability to be processed into desirable shapes and structures. Copyright © 2016 Elsevier B.V. All rights reserved.

Electronic sputtering of vitreous SiO2: Experimental and modeling results

NASA Astrophysics Data System (ADS)

Toulemonde, M.; Assmann, W.; Trautmann, C.

2016-07-01

The irradiation of solids with swift heavy ions leads to pronounced surface and bulk effects controlled by the electronic energy loss of the projectiles. In contrast to the formation of ion tracks in bulk materials, the concomitant emission of atoms from the surface is much less investigated. Sputtering experiments with different ions (58Ni, 127I and 197Au) at energies around 1.2 MeV/u were performed on vitreous SiO2 (a-SiO2) in order to quantify the emission rates and compare them with data for crystalline SiO2 quartz. Stoichiometry of the sputtering process was verified by monitoring the thickness decreases of a thin SiO2 film deposited on a Si substrate. Angular distributions of the emitted atoms were measured by collecting sputtered atoms on arc-shaped Cu catcher foils. Subsequent analysis of the number of Si atoms deposited on the catcher foils was quantified by elastic recoil detection analysis providing differential as well as total sputtering yields. Compared to existing data for crystalline SiO2, the total sputtering yields for vitreous SiO2 are by a factor of about five larger. Differences in the sputtering rate and track formation characteristics between amorphous and crystalline SiO2 are discussed within the frame of the inelastic thermal spike model.

Facile preparation of polyethylenimine-tannins coated SiO2 hybrid materials for Cu2+ removal

NASA Astrophysics Data System (ADS)

Huang, Qiang; Liu, Meiying; Zhao, Jiao; Chen, Junyu; Zeng, Guangjian; Huang, Hongye; Tian, Jianwen; Wen, Yuanqing; Zhang, Xiaoyong; Wei, Yen

2018-01-01

Polyethylenimine-tannins coated SiO2 (SiO2@PEI-TA) hybrid materials have been prepared via a single-step multifunctional coating with polyethylenimine (PEI) and tannins (TA), and characterized by transmission electron microscope (TEM), Fourier transform infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA), and X-ray photoelectron spectroscopy (XPS). The as-prepared SiO2@PEI-TA composites were examined as adsorbents to remove the Cu2+ from aqueous solution. The effects of contact time, initial Cu2+ concentration, solution pH and temperature, on Cu2+ adsorption have been investigated. The results show that the adsorption of Cu2+ onto SiO2@PEI-TA is dependent on the contact time, Cu2+ concentration, pH and temperature. The SiO2@PEI-TA composites show a 2.4-fold increase in adsorption capacity, implying that the introduction of PEI-TA coating is in favor of the Cu2+ adsorption. Based on the analysis of kinetic data, the kinetics of Cu2+ adsorption is more accurately described by the pseudo-second-order model. The equilibrium data are analyzed by Langmuir and Freundlich isotherms. Results of isotherms show that the better agreement is Freundlich isotherm model with correlation coefficient of 0.9914, which suggests that the adsorption of Cu2+ onto SiO2@PEI-TA is mainly a heterogeneous adsorption process. Thermodynamic analyses show that the adsorption interaction is actually a spontaneous and endothermic chemical process, which might involve the chemical chelation between Cu2+ and functional groups (amine and carboxyl groups) on the surface of SiO2@PEI-TA. In addition, the Cu2+ ions could desorb from SiO2@PEI-TA by using acid solution and the adsorption efficiency remains at high level after five adsorption-desorption recycles. These results provide potential applications of these novel adsorbents for the removal of heavy metal Cu2+ from aqueous solution and also provide strong evidence to support the adsorption mechanism proposed in the study.

SiO2 and CaF2 Behavior During Shielded Metal Arc Welding and Their Effect on Slag Detachability of the CaO-CaF2-SiO2 Type ENiCrFe-7-Covered Electrode

NASA Astrophysics Data System (ADS)

Wang, Huang; Qin, Renyao; He, Guo

2016-09-01

The metallurgical behavior during shielded metal arc welding (SMAW) and the slag detachability of the CaO-CaF2-SiO2 type ENiCrFe-7-covered electrodes was investigated. The results indicated that the slag detachability could be improved as the SiO2 in the flux coatings decreased. When the SiO2 in the flux coating was 10.9 pct, about 28.3 pct CaF2 resulted in the best slag detachability. The CaF2 and SiO2 in the flux coating interacted during SMAW to form gaseous SiF4 to be evacuated. In the reactions, one SiO2 consumed two CaF2, leading to the reduction of the ratio of CaF2/SiO2. After comparing the slag compositions, the best slag detachability was obtained at CaO:CaF2:SiO2 = 1.7:1.8:1, but the worst slag detachability appeared at CaO:CaF2:SiO2 = 1.3:0.9:1. The XRD analysis revealed that the oxides and fluorides in the slags preferred to gather together to form cuspidine and other complex phases. If the CaF2 was dominant in the slags, they intended to form homogenous porous microstructures that were relatively strong and would most likely detach from the weld metal in blocks, exhibiting good slag detachability. If the cuspidine phase was dominant, the slags exhibited a `rock strata'-like microstructure in the intergranular area. Such microstructure was very fragile and could be broken into fine powders that were easily embedded in the weld ripples, leading to slag adhesions. This work provides the researcher with a wealth of information and data, which will also be beneficial to the welding material producers and users.

Effect of the SiO 2 support on the catalytic performance of Ag/ZrO 2/SiO 2 catalysts for the single-bed production of butadiene from ethanol

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dagle, Vanessa Lebarbier; Flake, Matthew D.; Lemmon, Teresa L.

A ternary Ag/ZrO 2/SiO 2 catalyst system was studied for single-step conversion of ethanol to butadiene by varying the catalyst composition (Ag, Ir, or Pt metal component, Ag/ZrO 2 loading, and choice of SiO 2 support) and operating conditions (space velocity and feed gas composition). Exceptional catalytic performance was achieved over a 1%Ag/4%ZrO 2/SiO 2-SBA-16 catalyst leading to 99% conversion and 71% butadiene selectivity while operating under mild conditions (325°C, 1 atm, and 0.23 h –1). Several classes of silica—silica gels, fumed silicas, mesoporous silicas)—were evaluated as catalyst supports, and SBA-16 was found to be the most promising choice. Themore » SiO 2 support was found to significantly influence both conversion and selectivity. A higher SiO 2 catalyst surface area facilitates increased Ag dispersion which leads to greater conversion due to the accelerated initial ethanol dehydrogenation reaction step. By independently varying Ag and ZrO 2 loading, Ag was found to be the main component that affects ethanol conversion. ZrO 2 loading and thus Lewis acid sites concentration was found to have little impact on the ethanol conversion. Butadiene selectivity depends on the concentration of Lewis acid site, which in turn differs depending on the choice of SiO 2 support material. We observed a direct relationship between butadiene selectivity and concentration of Lewis acid sites. Butadiene selectivity decreases as the concentration of Lewis acid sites increases, which corresponds to an increase in ethanol dehydration to ethylene and diethyl ether. Additionally, adding H 2 to the feed had little effect on conversion while improving catalytic stability; however, selectivity to butadiene decreased. Lastly, catalyst regenerability was successfully demonstrated for several cycles.« less

Effect of the SiO 2 support on the catalytic performance of Ag/ZrO 2/SiO 2 catalysts for the single-bed production of butadiene from ethanol

DOE PAGES

Dagle, Vanessa Lebarbier; Flake, Matthew D.; Lemmon, Teresa L.; ...

2018-05-19

A ternary Ag/ZrO 2/SiO 2 catalyst system was studied for single-step conversion of ethanol to butadiene by varying the catalyst composition (Ag, Ir, or Pt metal component, Ag/ZrO 2 loading, and choice of SiO 2 support) and operating conditions (space velocity and feed gas composition). Exceptional catalytic performance was achieved over a 1%Ag/4%ZrO 2/SiO 2-SBA-16 catalyst leading to 99% conversion and 71% butadiene selectivity while operating under mild conditions (325°C, 1 atm, and 0.23 h –1). Several classes of silica—silica gels, fumed silicas, mesoporous silicas)—were evaluated as catalyst supports, and SBA-16 was found to be the most promising choice. Themore » SiO 2 support was found to significantly influence both conversion and selectivity. A higher SiO 2 catalyst surface area facilitates increased Ag dispersion which leads to greater conversion due to the accelerated initial ethanol dehydrogenation reaction step. By independently varying Ag and ZrO 2 loading, Ag was found to be the main component that affects ethanol conversion. ZrO 2 loading and thus Lewis acid sites concentration was found to have little impact on the ethanol conversion. Butadiene selectivity depends on the concentration of Lewis acid site, which in turn differs depending on the choice of SiO 2 support material. We observed a direct relationship between butadiene selectivity and concentration of Lewis acid sites. Butadiene selectivity decreases as the concentration of Lewis acid sites increases, which corresponds to an increase in ethanol dehydration to ethylene and diethyl ether. Additionally, adding H 2 to the feed had little effect on conversion while improving catalytic stability; however, selectivity to butadiene decreased. Lastly, catalyst regenerability was successfully demonstrated for several cycles.« less

Fabrication of SiO2@ZrO2@Y2O3:Eu3+ core-multi-shell structured phosphor.

PubMed

Gao, Xuan; He, Diping; Jiao, Huan; Chen, Juan; Meng, Xin

2011-08-01

ZrO2 interface was designed to block the reaction between SiO2 and Y2O3 in SiO2@Y2O3:Eu coreshell structure phosphor. SiO2@ZrO2@Y2O3:Eu core-multi-shell phosphors were successfully synthesized by combing an LBL method with a Sol-gel process. Based on electron microscopy, X-ray diffraction, and spectroscopy experiments, compelling evidence for the formation of the Y2O3:Eu outer shell on ZrO2 were presented. The presence of ZrO2 layer on SiO2 core can block the reaction of SiO2 core and Y2O3 shell effectively. By this kind of structure, the reaction temperature of the SiO2 core and Y2O3 shell in the SiO2@Y2O3:Eu core-shell structure phosphor can be increased about 200-300 degrees C and the luminescent intensity of this structure phosphor can be improved obviously. Under the excitation of ultraviolet (254 nm), the Eu3+ ion mainly shows its characteristic red (611 nm, 5D0-7F2) emissions in the core-multi-shell particles from Y2O3:Eu3+ shells. The emission intensity of Eu3+ ions can be tuned by the annealing temperatures, the number of coating times, and the thickness of ZrO2 interface, respectively.

Studies on influence of aluminium ions on the bioactivity of B2O3-SiO2-P2O5-Na2O-CaO glass system by means of spectroscopic studies

NASA Astrophysics Data System (ADS)

Mohini, G. Jagan; Krishnamacharyulu, N.; Sahaya Baskaran, G.; Rao, P. Venkateswara; Veeraiah, N.

2013-12-01

Bioactive multi component glasses of the composition of 27.4 B2O3-6.4 SiO2-2.5 P2O5-25.5 Na2O-(38.2 - x) CaO: x Al2O3 (x between 0 and 3.2) were synthesized, by melt quenching technique and their bioactivity was investigated as a function of Al2O3 concentration. Initially, optical absorption and infrared spectra were recorded and analyzed in order to have some pre-understanding over structural aspects of the glasses. For understanding the bioactivity, the samples were immersed in simulated body fluid (SBF) solution for prolonged times (∼30 days) and the weight loss measurements were carried out. The spectroscopic studies were repeated on the post immersed samples. From the comparison of the analysis of the spectroscopic data of both pre-immersed and post-immersed samples together with the information on variation of pH value of residual solution as a function of immersion time, it is concluded that the participation of aluminium ions in tetrahedral positions is hindrance for the formation of HA layer and for the bioactivity of the samples.

Synthesis of Hollow Nanotubes of Zn2SiO4 or SiO2: Mechanistic Understanding and Uranium Adsorption Behavior.

PubMed

Tripathi, Shalini; Bose, Roopa; Roy, Ahin; Nair, Sajitha; Ravishankar, N

2015-12-09

We report a facile synthesis of Zn2SiO4 nanotubes using a two-step process consisting of a wet-chemical synthesis of core-shell ZnO@SiO2 nanorods followed by thermal annealing. While annealing in air leads to the formation of hollow Zn2SiO4, annealing under reducing atmosphere leads to the formation of SiO2 nanotubes. We rationalize the formation of the silicate phase at temperatures much lower than the temperatures reported in the literature based on the porous nature of the silica shell on the ZnO nanorods. We present results from in situ transmission electron microscopy experiments to clearly show void nucleation at the interface between ZnO and the silica shell and the growth of the silicate phase by the Kirkendall effect. The porous nature of the silica shell is also responsible for the etching of the ZnO leading to the formation of silica nanotubes under reducing conditions. Both the hollow silica and silicate nanotubes exhibit good uranium sorption at different ranges of pH making them possible candidates for nuclear waste management.

Shear strength of metal - SiO2 contacts

NASA Technical Reports Server (NTRS)

Pepper, S. V.

1978-01-01

The strength of the bond between metals and SiO2 is studied by measuring the static coefficient of friction of metals contacting alpha-quartz in ultrahigh vacuum. It was found that copper with either chemisorbed oxygen, nitrogen or sulphur exhibited higher contact strength on stoichiometric SiO2 than did clean copper. Since the surface density of states induced by these species on copper is similar, it appears that the strength of the interfacial bond can be related to the density of states on the metal surface.

Shear strength of metal - SiO2 contacts

NASA Technical Reports Server (NTRS)

Pepper, S. V.

1978-01-01

The strength of the bond between metals and SiO2 was studied by measuring the static coefficient of friction of metals contacting alpha-quartz in ultrahigh vacuum. It was found that copper with either chemisorbed oxygen, nitrogen, or sulphur exhibited higher contact strength on stoichiometric SiO2 than did clean copper. Since the surface density of states induced by these species on copper is similar, it appears that the strength of the interfacial bond can be related to the density of states on the metal surface.

Role of SiO2 coating in multiferroic CoCr2O4 nanoparticles

NASA Astrophysics Data System (ADS)

Kamran, M.; Ullah, Asmat; Mehmood, Y.; Nadeem, K.; Krenn, H.

2017-02-01

Effect of silica (SiO2) coating concentration on structural and magnetic properties of multiferroic cobalt chromite (CoCr2O4) nanoparticles have been studied. The nanoparticles with average crystallite size in the range 19 to 28 nm were synthesised by sol-gel method. X-ray diffraction (XRD) analysis has verified the composition of single-phase cubic normal spinel structure of CoCr2O4 nanoparticles. The average crystallite size and cell parameter decreased with increasing SiO2 concentration. TEM image revealed that the shape of nanoparticles was non-spherical. Zero field cooled/field cooled (ZFC/FC) curves revealed that nanoparticles underwent a transition from paramagnetic (PM) state to collinear short-range ferrimagnetic (FiM) state, and this PM-FiM transition temperature decreased from 101 to 95 K with increasing SiO2 concentration or decreasing crystallite size. A conical spin state at Ts = 27 K was also observed for all the samples which decreased with decreasing average crystallite size. Low temperature lock-in transition was also observed in these nanoparticles at 12 K for uncoated nanoparticles which slightly shifted towards low temperature with decreasing average crystallite size. Saturation magnetization (Ms) showed decreasing trend with increasing SiO2 concentration, which was due to decrease in average crystallite size of nanoparticles and enhanced surface disorder in smaller nanoparticles. The temperature dependent AC-susceptibility also showed the decrease in the transition temperature (Tc), broadening of the Tc peak and decrease in magnetization with increasing SiO2 concentration or decreasing average crystallite size. In summary, the concentration of SiO2 has significantly affected the structural and magnetic properties of CoCr2O4 nanoparticles.

Crystallization kinetics of BaO-Al2O3-SiO2 glasses

NASA Technical Reports Server (NTRS)

Bansal, Narottam P.; Hyatt, Mark J.

1989-01-01

Barium aluminosilicate glasses are being investigated as matrix materials in high-temperature ceramic composites for structural applications. Kinetics of crystallization of two refractory glass compositions in the barium aluminosilicate system were studied by differential thermal analysis (DTA), X-ray diffraction (XRD), and scanning electron microscopy (SEM). From variable heating rate DTA, the crystallization activation energies for glass compositions (wt percent) 10BaO-38Al2O3-51SiO2-1MoO3 (glass A) and 39BaO-25Al2O3-35SiO2-1MoO3 (glass B) were determined to be 553 and 558 kJ/mol, respectively. On thermal treatment, the crystalline phases in glasses A and B were identified as mullite (3Al2O3-2SiO2) and hexacelsian (BaO-Al2O3-2SiO2), respectively. Hexacelsian is a high-temperature polymorph which is metastable below 1590 C. It undergoes structural transformation into the orthorhombic form at approximately 300 C accompanied by a large volume change which is undesirable for structural applications. A process needs to be developed where stable monoclinic celsian, rather than hexacelsian, precipitates out as the crystal phase in glass B.

Crystallization kinetics of BaO-Al2O3-SiO2 glasses

NASA Technical Reports Server (NTRS)

Bansal, Narottam P.; Hyatt, Mark J.

1988-01-01

Barium aluminosilicate glasses are being investigated as matrix materials in high-temperature ceramic composites for structural applications. Kinetics of crystallization of two refractory glass compositions in the barium aluminosilicate system were studied by differential thermal analysis (DTA), X-ray diffraction (XRD), and scanning electron microscopy (SEM). From variable heating rate DTA, the crystallization activation energies for glass compositions (wt percent) 10BaO-38Al2O3-51SiO2-1MoO3 (glass A) and 39BaO-25Al2O3-35SiO2-1MoO3 (glass B) were determined to be 553 and 558 kJ/mol, respectively. On thermal treatment, the crystalline phases in glasses A and B were identified as mullite (3Al2O3-2SiO2) and hexacelsian (BaO-Al2O3-2SiO2), respectively. Hexacelsian is a high-temperature polymorph which is metastable below 1590 C. It undergoes structural transformation into the orthorhombic form at approximately 300 C accompanied by a large volume change which is undesirable for structural applications. A process needs to be developed where stable monoclinic celsian, rather than hexacelsian, precipitates out as the crystal phase in glass B.

Diffusive charge transport in graphene on SiO 2

NASA Astrophysics Data System (ADS)

Chen, J.-H.; Jang, C.; Ishigami, M.; Xiao, S.; Cullen, W. G.; Williams, E. D.; Fuhrer, M. S.

2009-07-01

We review our recent work on the physical mechanisms limiting the mobility of graphene on SiO 2. We have used intentional addition of charged scattering impurities and systematic variation of the dielectric environment to differentiate the effects of charged impurities and short-range scatterers. The results show that charged impurities indeed lead to a conductivity linear in density ( σ(n)∝n) in graphene, with a scattering magnitude that agrees quantitatively with theoretical estimates; increased dielectric screening reduces the scattering from charged impurities, but increases the scattering from short-range scatterers. We evaluate the effects of the corrugations (ripples) of graphene on SiO 2 on transport by measuring the height-height correlation function. The results show that the corrugations cannot mimic long-range (charged impurity) scattering effects, and have too small an amplitude-to-wavelength ratio to significantly affect the observed mobility via short-range scattering. Temperature-dependent measurements show that longitudinal acoustic phonons in graphene produce a resistivity that is linear in temperature and independent of carrier density; at higher temperatures, polar optical phonons of the SiO 2 substrate give rise to an activated, carrier density-dependent resistivity. Together the results paint a complete picture of charge carrier transport in graphene on SiO 2 in the diffusive regime.

Self-cleaning cotton functionalized with TiO2/SiO2: focus on the role of silica.

PubMed

Pakdel, Esfandiar; Daoud, Walid A

2013-07-01

This manuscript aims to investigate the functionalization of cotton fabrics with TiO2/SiO2. In this study, the sol-gel method was employed to prepare titania and silica sols and the functionalization was carried out using the dip-pad-dry-cure process. Titanium tetra isopropoxide (TTIP) and tetra ethyl orthosilicate (TEOS) were utilized as precursors of TiO2 and SiO2, respectively. TiO2/SiO2 composite sols were prepared in three different Ti:Si molar ratios of 1:0.43, 1:1, and 1:2.33. The self-cleaning property of cotton samples functionalized with TiO2/SiO2 was assessed based on the coffee stain removal capability and the decomposition rate of methylene blue under UV irradiation. FTIR study of the TiO2/SiO2 photocatalyst confirmed the existence of Si-O-Si and Ti-O-Si bonds. Scanning electron microscopy was employed to investigate the morphology of the functionalized cotton samples. The samples coated with TiO2/SiO2 showed greater ability of coffee stain removal and methylene blue degradation compared with samples functionalized with TiO2 demonstrating improved self-cleaning properties. The role of SiO2 in improving these properties is also discussed. Copyright © 2013 Elsevier Inc. All rights reserved.

Dewetting process of Au films on SiO2 nanowires: Activation energy evaluation

NASA Astrophysics Data System (ADS)

Ruffino, F.; Grimaldi, M. G.

2015-05-01

SiO2 nanowires gain scientific and technological interest in application fields ranging from nano-electronics, optics and photonics to bio-sensing. Furthermore, the SiO2 nanowires chemical and physical properties, and so their performances in devices, can be enhanced if decorated by metal nanoparticles (such Au) due to local plasmonic effects. In the present paper, we propose a simple, low-cost and high-throughput three-steps methodology for the mass-production of Au nanoparticles coated SiO2 nanowires. It is based on (1) production of the SiO2 nanowires on Si surface by solid state reaction of an Au film with the Si substrate at high temperature; (2) sputtering deposition of Au on the SiO2 nanowires to obtain the nanowires coated by an Au film; and (3) furnace annealing processes to induce the Au film dewetting on the SiO2 nanowires surface. Using scanning electron microscopy analyses, we followed the change of the Au nanoparticles mean versus the annealing time extracting values for the characteristic activation energy of the dewetting process of the Au film on the SiO2 nanowires surface. Such a study can allow the tuning of the nanowires/nanoparticles sizes for desired technological applications.

Selective adsorption of thiophenic compounds from fuel over TiO2/SiO2 under UV-irradiation.

PubMed

Miao, Guang; Ye, Feiyan; Wu, Luoming; Ren, Xiaoling; Xiao, Jing; Li, Zhong; Wang, Haihui

2015-12-30

This study investigates selective adsorption of thiophenic compounds from fuel over TiO2/SiO2 under UV-irradiation. The TiO2/SiO2 adsorbents were prepared and then characterized by N2 adsorption, X-ray diffraction and X-ray photoelectron spectroscopy. Adsorption isotherms, selectivity and kinetics of TiO2/SiO2 were measured in a UV built-in batch reactor. It was concluded that (a) with the employment of UV-irradiation, high organosulfur uptake of 5.12 mg/g was achieved on the optimized 0.3TiO2/0.7SiO2 adsorbent at low sulfur concentration of 15 ppmw-S, and its adsorption selectivity over naphthalene was up to 325.5; (b) highly dispersed TiO2 served as the photocatalytic sites for DBT oxidation, while SiO2 acted as the selective adsorption sites for the corresponding oxidized DBT using TiO2 as a promoter, the two types of active sites worked cooperatively to achieve the high adsorption selectivity of TiO2/SiO2; (c) The kinetic rate-determining step for the UV photocatalysis-assisted adsorptive desulfurization (PADS) over TiO2/SiO2 was DBT oxidation; (d) consecutive adsorption-regeneration cycles suggested that the 0.3TiO2/0.7SiO2 adsorbent can be regenerated by acetonitrile washing followed with oxidative air treatment. This work demonstrated an effective PADS approach to greatly enhance adsorption capacity and selectivity of thiophenic compounds at low concentrations for deep desulfurization under ambient conditions. Copyright © 2015 Elsevier B.V. All rights reserved.

Nanocomposite Phosphor Consisting of CaI2:Eu2+ Single Nanocrystals Embedded in Crystalline SiO2.

PubMed

Daicho, Hisayoshi; Iwasaki, Takeshi; Shinomiya, Yu; Nakano, Akitoshi; Sawa, Hiroshi; Yamada, Wataru; Matsuishi, Satoru; Hosono, Hideo

2017-11-29

High luminescence efficiency is obtained in halide- and chalcogenide-based phosphors, but they are impractical because of their poor chemical durability. Here we report a halide-based nanocomposite phosphor with excellent luminescence efficiency and sufficient durability for practical use. Our approach was to disperse luminescent single nanocrystals of CaI 2 :Eu 2+ in a chemically stable, translucent crystalline SiO 2 matrix. Using this approach, we successfully prepared a nanocomposite phosphor by means of self-organization through a simple solid-state reaction. Single nanocrystals of 6H polytype (thr notation) CaI 2 :Eu 2+ with diameters of about 50 nm could be generated not only in a SiO 2 amorphous powder but also in a SiO 2 glass plate. The nanocomposite phosphor formed upon solidification of molten CaI 2 left behind in the crystalline SiO 2 that formed from the amorphous SiO 2 under the influence of a CaI 2 flux effect. The resulting nanocomposite phosphor emitted brilliant blue luminescence with an internal quantum efficiency up to 98% upon 407 nm violet excitation. We used cathodoluminescence microscopy, scanning transmission electron microscopy, and Rietveld refinement of the X-ray diffraction patterns to confirm that the blue luminescence was generated only by the CaI 2 :Eu 2+ single nanocrystals. The phosphor was chemically durable because the luminescence sites were embedded in the crystalline SiO 2 matrix. The phosphor is suitable for use in near-ultraviolet light-emitting diodes. The concept for this nanocomposite phosphor can be expected to be effective for improvements in the practicality of poorly durable materials such as halides and chalcogenides.

Enhanced luminous transmittance of thermochromic VO2 thin film patterned by SiO2 nanospheres

NASA Astrophysics Data System (ADS)

Zhou, Liwei; Liang, Jiran; Hu, Ming; Li, Peng; Song, Xiaolong; Zhao, Yirui; Qiang, Xiaoyong

2017-05-01

In this study, an ordered SiO2 nanosphere array coated with vanadium dioxide (VO2) has been fabricated to enhance transmittance with the potential application as an energy-efficient coating in the field of smart windows. SiO2 arrays were formed using the methods of self-assembly, and VO2 thin films were prepared by rapid thermal annealing (RTA) of sputtered vanadium films. VO2@SiO2 arrays were characterized by scanning electron microscopy, X-ray diffraction, a four-point probe, and UV-vis-NIR spectrophotometry. Compared with the planar films, the films deposited on 300 nm diameter SiO2 nanospheres can offer approximately 18% enhancement of luminous transmission (Tlum) because the diameter is smaller than the given wavelength and the protuberance of the surface array behaves as a gradation of refractive index producing antireflection. The solar regulation efficiency was not much deteriorated.

Hydroxyapatite-TiO2-SiO2-Coated 316L Stainless Steel for Biomedical Application

NASA Astrophysics Data System (ADS)

Sidane, Djahida; Khireddine, Hafit; Bir, Fatima; Yala, Sabeha; Montagne, Alex; Chicot, Didier

2017-07-01

This study investigated the effectiveness of titania (TiO2) as a reinforcing phase in the hydroxyapatite (HAP) coating and silica (SiO2) single layer as a bond coat between the TiO2-reinforced hydroxyapatite (TiO2/HAP) top layer and 316L stainless steel (316L SS) substrate on the corrosion resistance and mechanical properties of the underlying 316L SS metallic implant. Single layer of SiO2 film was first deposited on 316L SS substrate and studied separately. Water contact angle measurements, X-ray photoelectron spectroscopy, and Fourier transform infrared spectrophotometer analysis were used to evaluate the hydroxyl group reactivity at the SiO2 outer surface. The microstructural and morphological results showed that the reinforcement of HAP coating with TiO2 and SiO2 reduced the crystallite size and the roughness surface. Indeed, the deposition of 50 vol pct TiO2-reinforced hydroxyapatite layer enhanced the hardness and the elastic modulus of the HAP coating, and the introduction of SiO2 inner layer on the surface of the 316L SS allowed the improvement of the bonding strength and the corrosion resistance as confirmed by scratch studies, nanoindentation, and cyclic voltammetry tests.

Luminescence properties of Ca2 Ga2 SiO7 :RE phosphors for UV white-light-emitting diodes.

PubMed

Jiao, Mengmeng; Lv, Wenzhen; Lü, Wei; Zhao, Qi; Shao, Baiqi; You, Hongpeng

2015-03-16

A series of Eu(2+) -, Ce(3+) -, and Tb(3+) -doped Ca2 Ga2 SiO7 phosphors is synthesized by using a high-temperature solid-state reaction. The powder X-ray diffraction and structure refinement data indicate that our prepared phosphors are single phased and the phosphor crystalizes in a tetrahedral system with the ${P\\bar 42m}$ (113) space group. The Eu(2+) - and Ce(3+) -doped phosphors both have broad excitation bands, which match well with the UV light-emitting diodes chips. Under irradiation of λ=350 nm, Ca2 Ga2 SiO7 :Eu(2+) and Ca2 Ga2 SiO7 :Ce(3+) , Li(+) have green and blue emissions, respectively. Luminescence of Ca2 Ga2 SiO7 :Tb(3+) , Li(+) phosphor varies with the different Tb(3+) contents. The thermal stability and energy-migration mechanism of Ca2 Ga2 SiO7 :Eu(2+) are also studied. The investigation results indicate that the prepared Ca2 Ga2 SiO7 :Eu(2+) and Ca2 Ga2 SiO7 :Ce(3+) , Li(+) samples show potential as green and blue phosphors, respectively, for UV-excited white-light-emitting diodes. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Processing of SiO2 protective layer using HMDS precursor by combustion CVD.

PubMed

Park, Kyoung-Soo; Kim, Youngman

2011-08-01

Hexamethyldisilazane (HMDS, [(CH3)3Si]2NH) was used as a precursor to form SiO2 protective coatings on IN738LC alloys by combustion chemical vapor deposition (CCVD). SEM and XPS showed that the processed coatings were composed mainly of SiO2. The amount of HMDS had the largest effect on the size of the SiO2 agglomerates and the thickness of the deposited coatings. The specimens coated with SiO2 using the 0.05 mol/l HMDS solution showed a significantly higher temperature oxidation resistance than those deposited under other conditions.

Study on spectroscopic properties and effects of tungsten ions in 2Bi2O3-3GeO2/SiO2 glasses.

PubMed

Yu, Pingsheng; Su, Liangbi; Cheng, Junhua; Zhang, Xia; Xu, Jun

2017-04-01

The 2Bi 2 O 3 -3GeO 2 /SiO 2 glass samples have been prepared by the conventional melt quenching technique. XRD patterns, absorption spectra, excitation-emission spectra and Raman measurements were utilized to characterize the synthesized glasses. When substitute SiO 2 for GeO 2 , the 0.4Bi 2 O 3 -(0.4-0.1)GeO 2 -(0.2-0.5)SiO 2 glasses exhibit strong emission centered at about 475nm (under 300nm excitation), and the decay constants are within the scope of 20-40ns. W doping into 2Bi 2 O 3 -3SiO 2 glass could increase the emission intensity of 470nm, and the W-doped 2Bi 2 O 3 -3SiO 2 glass has shown another emission at about 433nm with much shorter decay time (near 10ns). The 2Bi 2 O 3 -3GeO 2 /SiO 2 glass system could be the possible candidate for scintillator in high energy physics applications. Copyright © 2017 Elsevier Ltd. All rights reserved.

Critical Evaluations and Thermodynamic Optimizations of the MnO-Mn2O3-SiO2 and FeO-Fe2O3-MnO-Mn2O3-SiO2 Systems

NASA Astrophysics Data System (ADS)

Kang, Youn-Bae; Jung, In-Ho

2017-06-01

A critical evaluation and thermodynamic modeling for thermodynamic properties of all oxide phases and phase diagrams in the Fe-Mn-Si-O system (MnO-Mn2O3-SiO2 and FeO-Fe2O3-MnO-Mn2O3-SiO2 systems) are presented. Optimized Gibbs energy parameters for the thermodynamic models of the oxide phases were obtained which reproduce all available and reliable experimental data within error limits from 298 K (25°C) to above the liquidus temperatures at all compositions covering from known oxide phases, and oxygen partial pressure from metal saturation to 0.21 bar. The optimized thermodynamic properties and phase diagrams are believed to be the best estimates presently available. Slag (molten oxide) was modeled using the modified quasichemical model in the pair approximation. Olivine (Fe2SiO4-Mn2SiO4) was modeled using two-sublattice model in the framework of the compound energy formalism (CEF), while rhodonite (MnSiO3-FeSiO3) and braunite (Mn7SiO_{12} with excess Mn2O3) were modeled as simple Henrian solutions. It is shown that the already developed models and databases of two spinel phases (cubic- and tetragonal-(Fe, Mn)3O4) using CEF [Kang and Jung, J. Phys. Chem. Solids (2016), vol. 98, pp. 237-246] can successfully be integrated into a larger thermodynamic database to be used in practically important higher order system such as silicate. The database of the model parameters can be used along with a software for Gibbs energy minimization in order to calculate any type of phase diagram section and thermodynamic properties.

Cd2SiO4/Graphene nanocomposite: Ultrasonic assisted synthesis, characterization and electrochemical hydrogen storage application.

PubMed

Masjedi-Arani, Maryam; Salavati-Niasari, Masoud

2018-05-01

For the first time, a simple and rapid sonochemical technique for preparing of pure Cd 2 SiO 4 nanostructures has been developed in presence of various surfactants of SDS, CTAB and PVP. Uniform and fine Cd 2 SiO 4 nanoparticle was synthesized using of polymeric PVP surfactant and ultrasonic irradiation. The optimized cadmium silicate nanostructures added to graphene sheets and Cd 2 SiO 4 /Graphene nanocomposite synthesized through pre-graphenization. Hydrogen storage capacity performances of Cd 2 SiO 4 nanoparticle and Cd 2 SiO 4 /Graphene nanocomposite were compared. Obtained results represent that Cd 2 SiO 4 /Graphene nanocomposites have higher hydrogen storage capacity than Cd 2 SiO 4 nanoparticles. Cd 2 SiO 4 /Graphene nanocomposites and Cd 2 SiO 4 nanoparticles show hydrogen storage capacity of 3300 and 1300 mAh/g, respectively. Copyright © 2018 Elsevier B.V. All rights reserved.

Analysis of SiO2 nanoparticles binding proteins in rat blood and brain homogenate.

PubMed

Shim, Kyu Hwan; Hulme, John; Maeng, Eun Ho; Kim, Meyoung-Kon; An, Seong Soo A

2014-01-01

A multitude of nanoparticles, such as titanium oxide (TiO2), zinc oxide, aluminum oxide, gold oxide, silver oxide, iron oxide, and silica oxide, are found in many chemical, cosmetic, pharmaceutical, and electronic products. Recently, SiO2 nanoparticles were shown to have an inert toxicity profile and no association with an irreversible toxicological change in animal models. Hence, exposure to SiO2 nanoparticles is on the increase. SiO2 nanoparticles are routinely used in numerous materials, from strengthening filler for concrete and other construction composites, to nontoxic platforms for biomedical application, such as drug delivery and theragnostics. On the other hand, recent in vitro experiments indicated that SiO2 nanoparticles were cytotoxic. Therefore, we investigated these nanoparticles to identify potentially toxic pathways by analyzing the adsorbed protein corona on the surface of SiO2 nanoparticles in the blood and brain of the rat. Four types of SiO2 nanoparticles were chosen for investigation, and the protein corona of each type was analyzed using liquid chromatography-tandem mass spectrometry technology. In total, 115 and 48 plasma proteins from the rat were identified as being bound to negatively charged 20 nm and 100 nm SiO2 nanoparticles, respectively, and 50 and 36 proteins were found for 20 nm and 100 nm arginine-coated SiO2 nanoparticles, respectively. Higher numbers of proteins were adsorbed onto the 20 nm sized SiO2 nanoparticles than onto the 100 nm sized nanoparticles regardless of charge. When proteins were compared between the two charges, higher numbers of proteins were found for arginine-coated positively charged SiO2 nanoparticles than for the negatively charged nanoparticles. The proteins identified as bound in the corona from SiO2 nanoparticles were further analyzed with ClueGO, a Cytoscape plugin used in protein ontology and for identifying biological interaction pathways. Proteins bound on the surface of nanoparticles may affect

Dry etched SiO2 Mask for HgCdTe Etching Process

NASA Astrophysics Data System (ADS)

Chen, Y. Y.; Ye, Z. H.; Sun, C. H.; Deng, L. G.; Zhang, S.; Xing, W.; Hu, X. N.; Ding, R. J.; He, L.

2016-09-01

A highly anisotropic etching process with low etch-induced damage is indispensable for advanced HgCdTe (MCT) infrared focal plane array (IRFPA) detectors. The inductively coupled plasma (ICP) enhanced reactive ion etching technique has been widely adopted in manufacturing HgCdTe IRFPA devices. An accurately patterned mask with sharp edges is decisive to accomplish pattern duplication. It has been reported by our group that the SiO2 mask functions well in etching HgCdTe with high selectivity. However, the wet process in defining the SiO2 mask is limited by ambiguous edges and nonuniform patterns. In this report, we patterned SiO2 with a mature ICP etching technique, prior to which a thin ZnS film was deposited by thermal evaporation. The SiO2 film etching can be terminated at the auto-stopping point of the ZnS layer thanks to the high selectivity of SiO2/ZnS in SF6 based etchant. Consequently, MCT etching was directly performed without any other treatment. This mask showed acceptable profile due to the maturity of the SiO2 etching process. The well-defined SiO2 pattern and the etched smooth surfaces were investigated with scanning electron microscopy and atomic force microscope. This new mask process could transfer the patterns exactly with very small etch-bias. A cavity with aspect-ratio (AR) of 1.2 and root mean square roughness of 1.77 nm was achieved first, slightly higher AR of 1.67 was also get with better mask profile. This masking process ensures good uniformity and surely benefits the delineation of shrinking pixels with its high resolution.

Enhanced the hydrophobic surface and the photo-activity of TiO2-SiO2 composites

NASA Astrophysics Data System (ADS)

Wahyuni, S.; Prasetya, A. T.

2017-02-01

The aim of this research is to develop nanomaterials for coating applications. This research studied the effect of various TiO2-SiO2 composites in acrylic paint to enhance the hydrophobic properties of the substrate. Titanium dioxide containing silica in the range 20-35 mol% has been synthesized using sol-gel route. The XRD’s spectra show that increasing SiO2 content in the composite, decreasing its crystalline properties but increasing the surface area. TiO2-SiO2 composite was dispersed in acrylic paint in 2% composition by weight. The largest contact angle was 70, which produced by the substrate coated with TS-35-modified acrylic paint. This study also investigated the enhanced photo-activity of TiO2-SiO2 modified with poly-aniline. The XRD spectra show that the treatment does not change the crystal structure of TiO2. The photo-activity of the composite was evaluated by degradation of Rhodamine-B with visible light. The best performance of the degradation process was handled by the composite treated with 0.1mL anilines per gram of TiO2-SiO2 composite (TSP-A). On the other side, the contact angle 70 has not shown an excellent hydrophobic activity. However, the AFM spectra showed that nanoroughness has started to form on the surface of acrylic paint modified with TiO2-SiO2 than acrylic alone.

SiO2-induced release of sVEGFRs from pulmonary macrophages.

PubMed

Chao, Jie; Lv, Yan; Chen, Jin; Wang, Jing; Yao, Honghong

2018-01-01

The inhalation of silicon dioxide (SiO 2 ) particles causes silicosis, a stubborn pulmonary disease that is characterized by alveolar inflammation during the early stage. Soluble cytokine receptors (SCRs) play important roles in regulating inflammation by either attenuating or promoting cytokine signaling. However, the role of SCRs in silicosis remains unknown. Luminex assays revealed increased soluble vascular endothelial growth factor receptor (sVEGFR) family levels in the plasma of silicosis patients. In an enzyme-linked immunosorbent assay (ELISA), cells from the differentiated human monocytic cell line U937 released sVEGFR family proteins after exposure to SiO 2 (50μg/cm 2 ). Further Western blot experiments revealed that VEGFR expression was also elevated in U937 cells. In contrast, levels of sVEGFR family members did not change in the supernatants of human umbilical vein endothelial cells (HUVECs) after exposure to SiO 2 (50μg/cm 2 ). Interestingly, VEGFR expression in HUVECs decreased after SiO 2 treatment. In a scratch assay, HUVECs exhibited cell migration ability, indicating the acquisition of mesenchymal properties. Our findings highlight the important role of sVEGFRs in both inflammation and fibrosis induced by SiO 2 , suggesting a possible mechanism for the fibrogenic effects observed in pulmonary diseases associated with fibrosis. Copyright © 2017 Elsevier B.V. All rights reserved.

Enhancement of red emission intensity of Ca2Al2SiO7:Eu3+ phosphor by MoO3 doping or excess SiO2 addition for application to white LEDs

NASA Astrophysics Data System (ADS)

Jiao, H. Y.; LiMao, C. R.; Chen, Q.; Wang, P. Y.; Cai, R. C.

2018-01-01

Ca1.86Al2(Si1-xMox)O7:0.14Eu3+ and Ca1.86Al2Si1+yO7+2y:0.14 Eu3+ were synthesized by solid-state reaction. X-ray powder diffraction, excitation and emission spectra were used to investigate their structures and photoluminescence properties. The results shows that the phosphor Ca1.86Al2SiO7:0.14Eu3+ cannot be excited efficiently by light of 393 nm. The introduced Mo ion does not change the position of the excitation peak, but increases both the absorption at 400nm and the emission intensity of Eu3+. The intense red emitting phosphor Ca1.86Al2(Si0.95Mo0.05)O7:0.14Eu3+ was obtained, which has 67% enhanced luminous intensity compared to that of the undoped sample Ca1.86Al2SiO7:0.14Eu3+. Otherwise, SiO2 excess of non-stoichiometric phosphors Ca1.86Al2Si1+yO7+2y:0.14Eu3+ showed the characteristic pattern of a tetragonal structure with a small SiO2 concentration. The optimal phosphor of Ca1.86Al2Si1.1O7.2:0.14Eu3+ has a luminous intensity about two times higher than that of the original stoichiometric phosphor Ca1.86Al2SiO7:0.14Eu3+. We confirmed that the photoluminescence intensity of the obtained phosphors is fairly enhanced by excessive SiO2. The mechanism of this photoluminescence enhancement is discussed in this paper.

Preparation of Nano-TiO2-Coated SiO2 Microsphere Composite Material and Evaluation of Its Self-Cleaning Property

PubMed Central

Sun, Sijia; Deng, Tongrong; Ding, Hao; Chen, Ying; Chen, Wanting

2017-01-01

In order to improve the dispersion of nano-TiO2 particles and enhance its self-cleaning properties, including photocatalytic degradation of pollutants and surface hydrophilicity, we prepared nano-TiO2-coated SiO2 microsphere composite self-cleaning materials (SiO2–TiO2) by co-grinding SiO2 microspheres and TiO2 soliquid and calcining the ground product. The structure, morphology, and self-cleaning properties of the SiO2–TiO2 were characterized. The characterization results showed that the degradation efficiency of methyl orange by SiO2–TiO2 was 97%, which was significantly higher than that obtained by pure nano-TiO2. The minimum water contact angle of SiO2–TiO2 was 8°, indicating strong hydrophilicity and the good self-cleaning effect. The as-prepared SiO2–TiO2 was characterized by the nano-TiO2 particles uniformly coated on the SiO2 microspheres and distributed in the gap among the microspheres. The nano-TiO2 particles were in an anatase phase with the particle size of 15–20 nm. The nano-TiO2 particles were combined with SiO2 microspheres via the dehydroxylation of hydroxyl groups on their surfaces. PMID:29099774

The effect of Cr2O3 doping on structures and dielectric constants of SiO2-Bi2O3-B2O3-Na2CO3 glass based on silica gel of natural sand

NASA Astrophysics Data System (ADS)

Diantoro, M.; Zaini, M. B.; Muniroh, Z.; Nasikhudin; Hidayat, A.

2017-05-01

One of the abundant natural resources along the coastal lines of Indonesia is silica sand. One of the beaches which has a lot of silica content is Bancar-Tuban beach. Silica can be used as a raw material of glass that has multiple properties in optic, dielectric, and other physical properties by introducing specific dopants. Some oxides have been used as dopant e.g. Al2O3, Fe3O4, and NiO. However, there has not been any comprehensive study discussing the multiple properties of natural silica-sand-based glass with Cr2O3 dopant so far. A series of samples have been prepared, which mean two solid steps to state melting technique. Cr2O3 was selected as a dopant due to its potential to control its color and to increase the dielectric constant of the glass. The synthesis of silica (SiO2) sand from BancarTuban beach was conducted through the sol-gel process. The composition varied as the addition of Cr2O3on 50SiO2-25B2O3-(6.5-x) Bi2O3-18.5Na2CO3-xCr2O3 (x = 0, 0.02, 0.04, 0.06 and 0.08mol), later called SBBN glass. The samples’ characterizations of the structure and morphology were conducted through the use of XRD, and SEM-EDX. The measurements were done by using a DC capacitance meter in order to investigate the dielectric properties of the sample, under the influence of light. It is shown that addition of Cr2O3 did not alter the crystal structure but changed the structure of the functional bond formation. It is also revealed that the dielectric constant increased along with the increasing of Cr2O3. An interesting result was that the dielectric constant of the glass was quantized decreasingly as the increase of light.

Effect of SiO2 addition and gamma irradiation on the lithium borate glasses

NASA Astrophysics Data System (ADS)

Raut, A. P.; Deshpande, V. K.

2018-01-01

The physical properties like density, glass transition temperature (Tg), and ionic conductivity of lithium borate (LB) glasses with SiO2 addition were measured before and after gamma irradiation. Remarkable changes in properties have been obtained in the physical properties of LB glasses with SiO2 addition and after gamma irradiation. The increase in density and glass transition temperature of LB glasses with SiO2 addition has been explained with the help of increase in density of cross linking due to SiO4 tetrahedra formation. The increase in ionic conductivity with SiO2 addition was explained with the help of ‘mixed glass former effect’. The increase in density and Tg of LB glasses with SiO2 addition after gamma irradiation has been attributed to fragmentation of bigger ring structure into smaller rings, which increases the density of cross linking and hence compaction. The exposure of gamma irradiation has lead to decrease in ionic conductivity of LB glasses with SiO2 addition. The atomic displacement caused by gamma irradiation resulted in filling of interstices and decrease in trapping sites. This explains the obtained decrease in ionic conductivity after gamma irradiation of glasses. The obtained results of effect of SiO2 addition and gamma irradiation on the density, Tg and ionic conductivity has been supported by FTIR results.

Fabrication of silicon-on-diamond substrate with an ultrathin SiO2 bonding layer

NASA Astrophysics Data System (ADS)

Nagata, Masahiro; Shirahama, Ryouya; Duangchan, Sethavut; Baba, Akiyoshi

2018-06-01

We proposed and demonstrated a sputter etching method to prepare both a flat surface (root-mean-square surface roughness of approximately 0.2–0.3 nm) and an ultrathin SiO2 bonding layer at an accuracy of approximately 5 nm in thickness to fabricate a silicon-on-diamond substrate (SOD). We also investigated a plasma activation method on a SiO2 surface using various gases. We found that O2 plasma activation is more suitable for the bonding between SiO2 and Si than N2 or Ar plasma activation. We speculate that the concentration of hydroxyl groups on the SiO2 surface was increased by O2 plasma activation. We fabricated the SOD substrate with an ultrathin (15 nm in thickness) SiO2 bonding layer using the sputter etching and O2 plasma activation methods.

Driving the photoluminescent and structural properties of X2-Y2SiO5 by varying the dopant Dy3+ concentration towards cool WLED applications

NASA Astrophysics Data System (ADS)

Ramakrishna, G.; Nagabhushana, H.; Hareesh, K.; Sunitha, D. V.

2017-07-01

Dy3+ doped Y2SiO5 nanophosphors were synthesized by solution combustion technique using Calotropis gigantean milk latex and NaCl as fuel and flux respectively. Powder X-ray diffraction (PXRD) confirmed the formation of monoclinic X2-phase Y2SiO5 belonging to the phase group C2/c. Fourier transform infrared spectroscopy (FTIR) shows characteristic metal-oxygen (Y-O) vibration band at 721 cm-1. Transmission electron microscopic (TEM) and Scanning electron microscopic (SEM) morphological feature exhibits non-uniform almost spherical shaped nanosized particles. The photoluminescence (PL) emission peaks, recorded at 388 nm, showed radiative emissions at 483, 575 and 636 nm respectively. Judd-Ofelt (JO) analysis was carried out to estimate the radiative (AR) properties, radiative life time (τR), branching ratio (βR) and stimulated emission crossection (σλp). The CIE and CCT was estimated using McCamy empirical formula. In the beginning, the CIE co-ordinate values were lying in the light blue region. However, with increase in Dy3+ concentration the values shifted towards white region. CCT value was found to be ∼6984 K. Therefore, Y2SiO5:Dy3+ (9 mol%) can be used for cool day light and WLED applications.

Characterization of remote O2-plasma-enhanced CVD SiO2/GaN(0001) structure using photoemission measurements

NASA Astrophysics Data System (ADS)

Truyen, Nguyen Xuan; Ohta, Akio; Makihara, Katsunori; Ikeda, Mitsuhisa; Miyazaki, Seiichi

2018-01-01

The control of chemical composition and bonding features at a SiO2/GaN interface is a key to realizing high-performance GaN power devices. In this study, an ∼5.2-nm-thick SiO2 film has been deposited on an epitaxial GaN(0001) surface by remote O2-plasma-enhanced chemical vapor deposition (O2-RPCVD) using SiH4 and Ar/O2 mixture gases at a substrate temperature of 500 °C. The depth profile of chemical structures and electronic defects of the O2-RPCVD SiO2/GaN structures has been evaluated from a combination of SiO2 thinning examined by X-ray photoelectron spectroscopy (XPS) and the total photoelectron yield spectroscopy (PYS) measurements. As a highlight, we found that O2-RPCVD is effective for fabricating an abrupt SiO2/GaN interface.

Thermally tunable VO2-SiO2 nanocomposite thin-film capacitors

NASA Astrophysics Data System (ADS)

Sun, Yifei; Narayanachari, K. V. L. V.; Wan, Chenghao; Sun, Xing; Wang, Haiyan; Cooley, Kayla A.; Mohney, Suzanne E.; White, Doug; Duwel, Amy; Kats, Mikhail A.; Ramanathan, Shriram

2018-03-01

We present a study of co-sputtered VO2-SiO2 nanocomposite dielectric thin-film media possessing continuous temperature tunability of the dielectric constant. The smooth thermal tunability is a result of the insulator-metal transition in the VO2 inclusions dispersed within an insulating matrix. We present a detailed comparison of the dielectric characteristics of this nanocomposite with those of a VO2 control layer and of VO2/SiO2 laminate multilayers of comparable overall thickness. We demonstrated a nanocomposite capacitor that has a thermal capacitance tunability of ˜60% between 25 °C and 100 °C at 1 MHz, with low leakage current. Such thermally tunable capacitors could find potential use in applications such as sensing, thermal cloaks, and phase-change energy storage devices.

Tribological Properties of TiO2/SiO2 Double Layer Coatings Deposited on CP-Ti

NASA Astrophysics Data System (ADS)

Çomakli, O.; Yazici, M.; Yetim, T.; Yetim, A. F.; Çelik, A.

In the present paper, the influences of different double layer on wear and scratch performances of commercially pure Titanium (CP-Ti) were investigated. TiO2/SiO2 and SiO2/TiO2 double layer coatings were deposited on CP-Ti by sol-gel dip coating process and calcined at 750∘C. The phase structure, cross-sectional morphology, composition, wear track morphologies, adhesion properties, hardness and roughness of uncoated and coated samples were characterized with X-ray diffraction, scanning electron microscopy (SEM), nano-indentation technique, scratch tester and 3D profilometer. Also, the tribological performances of all samples were investigated by a pin-on-disc tribo-tester against Al2O3 ball. Results showed that hardness, elastic modulus and adhesion resistance of double layer coated samples were higher than untreated CP-Ti. It was found that these properties of TiO2/SiO2 double layer coatings have higher than SiO2/TiO2 double layer coating. Additionally, the lowest friction coefficient and wear rates were obtained from TiO2/SiO2 double layer coatings. Therefore, it was seen that phase structure, hardness and film adhesion are important factors on the tribological properties of double layer coatings.

Effect of interfacial SiO2- y layer and defect in HfO2- x film on flat-band voltage of HfO2- x /SiO2- y stacks for backside-illuminated CMOS image sensors

NASA Astrophysics Data System (ADS)

Na, Heedo; Lee, Jimin; Jeong, Juyoung; Kim, Taeho; Sohn, Hyunchul

2018-03-01

In this study, the effect of oxygen gas fraction during deposition of a hafnium oxide (HfO2- x ) film and the influence of the quality of the SiO2- y interlayer on the nature of flat-band voltage ( V fb) in TiN/HfO/SiO2- y /p-Si structures were investigated. X-ray photoemission spectroscopy analysis showed that the non-lattice oxygen peak, indicating an existing oxygen vacancy, increased as the oxygen gas fraction decreased during sputtering. From C- V and J- E analyses, the V fb behavior was significantly affected by the characteristics of the SiO2- y interlayer and the non-lattice oxygen fraction in the HfO2- x films. The HfO2- x /native SiO2- y stack presented a V fb of - 1.01 V for HfO2- x films with an oxygen gas fraction of 5% during sputtering. Additionally, the V fb of the HfO2- x /native SiO2- y stack could be controlled from - 1.01 to - 0.56 V by changing the deposition conditions of the HfO2- x film with the native SiO2- y interlayer. The findings of this study can be useful to fabricate charge-accumulating layers for backside-illuminated image sensor devices.

The relation between residual stress, interfacial structure and the joint property in the SiO2f/SiO2-Nb joints.

PubMed

Ma, Qiang; Li, Zhuo Ran; Yang, Lai Shan; Lin, Jing Huang; Ba, Jin; Wang, Ze Yu; Qi, Jun Lei; Feng, Ji Cai

2017-06-23

In order to achieve a high-quality joint between SiO 2f /SiO 2 and metals, it is necessary to address the poor wettability of SiO 2f /SiO 2 and the high residual stress in SiO 2f /SiO 2 -Nb joint. Here, we simultaneously realize good wettability and low residual stress in SiO 2f /SiO 2 -Nb joint by combined method of HF etching treatment and Finite Element Analysis (FEA). After etching treatment, the wettability of E-SiO 2f /SiO 2 was improved, and the residual stress in the joint was decreased. In order to better control the quality of joints, efforts were made to understand the relationship between surface structure of E-SiO 2f /SiO 2 and residual stress in joint using FEA. Based on the direction of FEA results, a relationship between residual stress, surface structure and joint property in the brazed joints were investigated by experiments. As well the FEA and the brazing test results both realized the high-quality joint of E-SiO 2f /SiO 2 -Nb and the shear strength of the joint reached 61.9 MPa.

Melting and subsolidus reactions in the system K2O-CaO-Al2O3-SiO2-H2O

NASA Astrophysics Data System (ADS)

Johannes, Wilhelm

1980-09-01

Beginning of melting and subsolidus relationships in the system K2O-CaO-Al2O3-SiO2-H2O have been experimentally investigated at pressures up to 20 kbars. The equilibria discussed involve the phases anorthite, sanidine, zoisite, muscovite, quartz, kyanite, gas, and melt and two invariant points: Point [Ky] with the phases An, Or, Zo, Ms, Qz, Vapor, and Melt; point [Or] with An, Zo, Ms, Ky, Qz, Vapor, and Melt. The invariant point [Ky] at 675° C and 8.7 kbars marks the lowest solidus temperature of the system investigated. At pressures above this point the hydrated phases zoisite and muscovite are liquidus phases and the solidus temperatures increase with increasing pressure. At 20 kbars beginning of melting occurs at 740 °C. The solidus temperatures of the quinary system K2O-CaO-Al2O3-SiO2-H2O are almost 60° C (at 20 kbars) and 170° C (at 2kbars) below those of the limiting quaternary system CaO-Al2O3-SiO2-H2O. The maximum water pressure at which anorthite is stable is lowered from 14 to 8.7 kbars in the presence of sanidine. The stability limits of anorthite+ vapor and anorthite+sanidine+vapor at temperatures below 700° C are almost parallel and do not intersect. In the wide temperature — pressure range at pressures above the reaction An+Or+Vapor = Zo+Ms+Qz and temperatures below the melting curve of Zo+Ms+Ky+Qz+Vapor, the feldspar assemblage anorthite+sanidine is replaced by the hydrated phases zoisite and muscovite plus quartz. CaO-Al2O3-SiO2-H2O. Knowledge of the melting relationships involving the minerals zoisite and muscovite contributes to our understanding of the melting processes occuring in the deeper parts of the crust. Beginning of melting in granites and granodiorites depends on the composition of plagioclase. The solidus temperatures of all granites and granodiorites containing plagioclases of intermediate composition are higher than those of the Ca-free alkali feldspar granite system and below those of the Na-free system discussed in this

Low-temperature heat capacities of CaAl2SiO6 glass and pyroxene and thermal expansion of CaAl2SiO6 pyroxene.

USGS Publications Warehouse

Haselton, H.T.; Hemingway, B.S.; Robie, R.A.

1984-01-01

Low-T heat capacities (5-380 K) have been measured by adiabatic calorimetry for synthetic CaAl2SiO6 glass and pyroxene. High-T unit cell parameters were measured for CaAl2SiO6 pyroxene by means of a Nonius Guinier-Lenne powder camera in order to determine the mean coefficient of thermal expansion in the T range 25-1200oC. -J.A.Z.

Effect of NiO and Light Intensity on Dielectric Constant of SiO2-B2O3-Bi2O3-Na2CO3 Glass Based on Silica Gel of Natural Sands

NASA Astrophysics Data System (ADS)

Diantoro, M.; Muniroh, Z.; Zaini, B.; Mustikasari, A. A.; Nasikhudin; Hidayat, A.; Taufiq, A.; Sunaryono; Mufti, N.

2017-05-01

The use of silica in various fields is significantly increasing. One common application is silica based functional glass which has naturally show specific dielectric, optical, and magnetic properties. Many studies have been performing to explore the influence of dopant, composition, and other processing parameters as well as employing various characterization. In the previous work, we report the use of silica from silica sands. To reduce the melting temperature, we used silica sol-gel beside the utilization of some oxides such as B2O3, Na2CO3, and Bi3O3. We also used NiO as dopant explore the glass properties. We have prepared a series of sample with the composition of 50SiO2-25B2O3-(6.5-x) Bi3O3-18.5 Na2CO3-xNiO (x = 0, 1, 2, 3 and 4 wt%). After weighting process, the composition was blended, then heated to 450 °C for 120 minutes and then raised at 950 °C for 60 minutes in the crucible. Then samples of glass separated from the crucible and in the characterization of the structure using the DTA, XRD, SEM-EDAX and FTIR and measuring dielectric constant using a capacitance meter. The increase of NiO dopant resulted in increasing the dielectric constant of glass. On the other hand, the dielectric constant gradually decreases with the increase of light intensity. One can be noted that the applied intensity give rise to the step-like decrease of the dielectric constant. Whereas, the increasing magnetic field indicate the increase of dielectric constant.

Effect of SiO2 coating layer morphology on TiH2 gas release characteristic.

PubMed

Yang, Zhimao; Fang, Jixiang; Ding, Bingjun

2005-10-15

In this study, a uniform and compact SiO2 film-coating layer was prepared on the surface of TiH2 particles by sol-gel method using inexpensive raw materials. The preparation process of SiO2-coated TiH2 particles and the effect of the coating layer morphology on the gas release characteristic were investigated in detail. When the pH value of TiH2 suspending solution is about 4.0 and the concentration of silicic acid is more than 0.5 mol/L, the coating layer shows a SiO2 particle-coating morphology. While a homogeneous and dense film-coating layer can be obtained when the solution pH value and concentration of silicic acid are about 4.0 and 0.5 mol/L. The results of gas release at 700 degrees C show that TiH2 particles coated with silicon dioxide layers can efficiently delay the starting time of gas release of TiH2 powders to 60-100 s. Comparing the particle-coating layer, the SiO2 film-coating layer has a better delaying effect on gas release of TiH2 particles.

Fe3O4/SiO2-g-PSStNa polymer nanocomposite microspheres (PNCMs) from a surface-initiated atom transfer radical polymerization (SI-ATRP) approach for pectinase immobilization.

PubMed

Lei, Zhongli; Ren, Na; Li, Yanli; Li, Na; Mu, Bo

2009-02-25

Polymer nanocomposite microspheres (PNCMs) as solid supports can improve the efficiency of immobilized enzymes by reducing diffusional limitation as well as by increasing the surface area per mass unit. In this work, pectinase was immobilized on Fe(3)O(4)/SiO2-g-poly(PSStNa) nanocomposite microspheres by covalent attachment. Biochemical studies showed an improved storage stability of the immobilized pectinase as well as enhanced performance at higher temperatures and over a wider pH range. The immobilized enzyme retained >50% of its initial activity over 30 days, and the optimum temperature and pH also increased to the ranges of 50-60 degrees C and 3.0-4.7, respectively. The kinetics of a model reaction catalyzed by the immobilized pectinase was finally investigated by the Michaelis-Menten equation. The PSStNa support presents a very simple, mild, and time-saving process for enzyme immobilization, and this strategy of immobilizing pectinase also makes use of expensive enzymes economically viable, strengthening repeated use of them as catalysts following their rapid and easy separation with a magnet.

Shock states of solid Mg2SiO4

NASA Astrophysics Data System (ADS)

Townsend, Joshua; Shulenburger, Luke

2017-06-01

To date there have been thousands of planets discovered outside our solar system. Forsterite, the magnesium end-member of olivine, ((Mg , Fe) 2SiO4) is abundant in the Earth's mantle, and is likely a common planetary building block throughout the galaxy. Despite extensive investigation under terrestrial pressure and temperature regimes, the behavior of the Mg2SiO4 system at higher pressures and temperatures (P>100 GPa, T>4000 K) remains poorly understood. To better understand the behavior of planetary impact processes and the structure of massive planets we investigated the high pressure and high temperature properties of Mg2SiO4 using combined shock compression experiments on the Z-machine at Sandia National Laboratories, and ab-initio molecular dynamics simulations. We compare our results to other recent experiments on shocked forsterite. Sandia National Laboratories is a multi-program laboratory managed and operated by Sandia Corporation, a wholly owned subsidiary of Lockheed Martin Corporation, for the U.S. Department of Energy's National Nuclear Security Administration under Contract No. DE-AC04-94AL85000. SAND2017-1987 C.

Screen-Printed Photochromic Textiles through New Inks Based on SiO2@naphthopyran Nanoparticles.

PubMed

Pinto, Tânia V; Costa, Paula; Sousa, Céu M; Sousa, Carlos A D; Pereira, Clara; Silva, Carla J S M; Pereira, Manuel Fernando R; Coelho, Paulo J; Freire, Cristina

2016-10-26

Photochromic silica nanoparticles (SiO 2 @NPT), fabricated through the covalent immobilization of silylated naphthopyrans (NPTs) based on 2H-naphtho[1,2-b]pyran (S1, S2) and 3H-naphtho[2,1-b]pyran (S3, S4) or through the direct adsorption of the parent naphthopyrans (1, 3) onto silica nanoparticles (SiO 2 NPs), were successfully incorporated onto cotton fabrics by a screen-printing process. Two aqueous acrylic- (AC-) and polyurethane- (PU-) based inks were used as dispersing media. All textiles exhibited reversible photochromism under UV and solar irradiation, developing fast responses and intense coloration. The fabrics coated with SiO 2 @S1 and SiO 2 @S2 showed rapid color changes and high contrasts (ΔE* ab = 39-52), despite presenting slower bleaching kinetics (2-3 h to fade to the original color), whereas the textiles coated with SiO 2 @S3 and SiO 2 @S4 exhibited excellent engagement between coloration and decoloration rates (coloration and fading times of 1 and 2 min, respectively; ΔE* ab = 27-53). The PU-based fabrics showed excellent results during the washing fastness tests, whereas the AC-based textiles evidenced good results only when a protective transfer film was applied over the printed design.

Ion assisted deposition of SiO2 film from silicon

NASA Astrophysics Data System (ADS)

Pham, Tuan. H.; Dang, Cu. X.

2005-09-01

Silicon dioxide, SiO2, is one of the preferred low index materials for optical thin film technology. It is often deposited by electron beam evaporation source with less porosity and scattering, relatively durable and can have a good laser damage threshold. Beside these advantages the deposition of critical optical thin film stacks with silicon dioxide from an E-gun was severely limited by the stability of the evaporation pattern or angular distribution of the material. The even surface of SiO2 granules in crucible will tend to develop into groove and become deeper with the evaporation process. As the results, angular distribution of the evaporation vapor changes in non-predicted manner. This report presents our experiments to apply Ion Assisted Deposition process to evaporate silicon in a molten liquid form. By choosing appropriate process parameters we can get SiO2 film with good and stable property.

Emission analysis of Tb3+ -and Sm3+ -ion-doped (Li2 O/Na2 O/K2 O) and (Li2 O + Na2 O/Li2 O + K2 O/K2 O + Na2 O)-modified borosilicate glasses.

PubMed

Naveen Kumar Reddy, B; Sailaja, S; Thyagarajan, K; Jho, Young Dahl; Sudhakar Reddy, B

2018-05-01

Four series of borosilicate glasses modified by alkali oxides and doped with Tb 3+ and Sm 3+ ions were prepared using the conventional melt quenching technique, with the chemical composition 74.5B 2 O 3 + 10SiO 2 + 5MgO + R + 0.5(Tb 2 O 3 /Sm 2 O 3 ) [where R = 10(Li 2 O /Na 2 O/K 2 O) for series A and C, and R = 5(Li 2 O + Na 2 O/Li 2 O + K 2 O/K 2 O + Na 2 O) for series B and D]. The X-ray diffraction (XRD) patterns of all the prepared glasses indicate their amorphous nature. The spectroscopic properties of the prepared glasses were studied by optical absorption analysis, photoluminescence excitation (PLE) and photoluminescence (PL) analysis. A green emission corresponding to the 5 D 4 → 7 F 5 (543 nm) transition of the Tb 3+ ions was registered under excitation at 379 nm for series A and B glasses. The emission spectra of the Sm 3+ ions with the series C and D glasses showed strong reddish-orange emission at 600 nm ( 4 G 5/2 → 6 H 7/2 ) with an excitation wavelength λ exci = 404 nm ( 6 H 5/2 → 4 F 7/2 ). Furthermore, the change in the luminescence intensity with the addition of an alkali oxide and combinations of these alkali oxides to borosilicate glasses doped with Tb 3+ and Sm 3+ ions was studied to optimize the potential alkali-oxide-modified borosilicate glass. Copyright © 2017 John Wiley & Sons, Ltd.

Surface modification of SiO2 coated ZnO nanoparticles for multifunctional cotton fabrics.

PubMed

El-Naggar, Mehrez E; Hassabo, Ahmed G; Mohamed, Amina L; Shaheen, Tharwat I

2017-07-15

A simple chemical synthetic route was designed to prepare zinc oxide nanoparticles (ZnO-NPs) by using sodium alginate as anti-agglomeration agent in the presence of sodium hydroxide as alkali. Next, surface modification of ZnO-NPs with SiO 2 nanoparticles was achieved as per to sol-gel process. Further enhancing of the multifunctional properties of SiO 2 @ZnO-NPs was conducted successfully thanks to (aminopropyl)triethoxysilan (APTES) and vinyltriethoxysilan (VTES) which, in turns, increase the affinity of the SiO 2 @ZnO-NPs nanocomposite towards glycosidic chains of cotton fabrics. Thorough characterizations of synthesized ZnO-NPs, SiO 2 @ZnO-NPs, SiO 2 @ZnO-NPs/APTES and SiO 2 @ZnO-NPs/VTES were conducted by the making use of well advanced techniques such as FT-IR, XRD, TEM, DLS and SEM-EDX. The data obtained clarified the formation of an interfacial chemical bond between ZnO and SiO 2 as affirmed by FT-IR and XRD analysis. In addition, the results revealed by TEM, zeta sizer and SEM-EDX techniques, declared that the amorphous layers of SiO 2 , APTES or VTES evenly coated the surface of ZnO-NPs. For these nanocomposites, the work was extended to render cotton fabrics multifunctional properties such as antibacterial and UV protection with high durability even after 20 washing cycles using pad dry cure method. Taking the advantages of the silane compounds terminated by active groups such as OH, NH 2 , etc., open the door for further functionalization of the cotton fabrics' surfaces by durable multifunctional agents applied in various applications. Copyright © 2017 Elsevier Inc. All rights reserved.

Crack-resistant Al2O3-SiO2 glasses.

PubMed

Rosales-Sosa, Gustavo A; Masuno, Atsunobu; Higo, Yuji; Inoue, Hiroyuki

2016-04-07

Obtaining "hard" and "crack-resistant" glasses have always been of great important in glass science and glass technology. However, in most commercial glasses both properties are not compatible. In this work, colorless and transparent xAl2O3-(100-x)SiO2 glasses (30 ≤ x ≤ 60) were fabricated by the aerodynamic levitation technique. The elastic moduli and Vickers hardness monotonically increased with an increase in the atomic packing density as the Al2O3 content increased. Although a higher atomic packing density generally enhances crack formation in conventional oxide glasses, the indentation cracking resistance increased by approximately seven times with an increase in atomic packing density in binary Al2O3-SiO2 glasses. In particular, the composition of 60Al2O3 • 40SiO2 glass, which is identical to that of mullite, has extraordinary high cracking resistance with high elastic moduli and Vickers hardness. The results indicate that there exist aluminosilicate compositions that can produce hard and damage-tolerant glasses.

Crack-resistant Al2O3-SiO2 glasses

NASA Astrophysics Data System (ADS)

Rosales-Sosa, Gustavo A.; Masuno, Atsunobu; Higo, Yuji; Inoue, Hiroyuki

2016-04-01

Obtaining “hard” and “crack-resistant” glasses have always been of great important in glass science and glass technology. However, in most commercial glasses both properties are not compatible. In this work, colorless and transparent xAl2O3-(100-x)SiO2 glasses (30 ≤ x ≤ 60) were fabricated by the aerodynamic levitation technique. The elastic moduli and Vickers hardness monotonically increased with an increase in the atomic packing density as the Al2O3 content increased. Although a higher atomic packing density generally enhances crack formation in conventional oxide glasses, the indentation cracking resistance increased by approximately seven times with an increase in atomic packing density in binary Al2O3-SiO2 glasses. In particular, the composition of 60Al2O3•40SiO2 glass, which is identical to that of mullite, has extraordinary high cracking resistance with high elastic moduli and Vickers hardness. The results indicate that there exist aluminosilicate compositions that can produce hard and damage-tolerant glasses.

Microwave electromagnetic and absorption properties of SiO2/C core/shell composites plated with metal cobalt

NASA Astrophysics Data System (ADS)

Shen, Guozhu; Fang, Xumin; Wu, Hongyan; Wei, Hongyu; Li, Jingfa; Li, Kaipeng; Mei, Buqing; Xu, Yewen

2017-04-01

A facile method has been developed to fabricate magnetic core/shell SiO2/C/Co sub-microspheres via the pyrolysis of SiO2/PANI (polyaniline) and electroless plating method. The electromagnetic parameters of these SiO2/C and SiO2/C/Co composites were measured and the microwave reflection loss properties were evaluated in the frequency range of 2-18 GHz. The results show that the dielectric loss of SiO2/C composite increases with the increase of carbonization temperature and the magnetic loss enhances due to the deposition of cobalt on the SiO2/C sub-microspheres. The reflection loss results exhibit that the microwave absorption properties of the SiO2/C/Co composites are more excellent than those of SiO2/C composites for each thickness. The maximum effective absorption bandwidth (reflection loss ≤ -10 dB) arrives at 5.0 GHz (13.0-18 GHz) for SiO2/C/Co composite with 1.5 mm of thickness and the minimum reflection loss value is -24.0 dB at 5.0 GHz with 4.0 mm of thickness. The microwave loss mechanism of the SiO2/C/Co composites was also discussed in this paper.

Enhanced antioxidation and microwave absorbing properties of SiO2-coated flaky carbonyl iron particles

NASA Astrophysics Data System (ADS)

Zhou, Yingying; Xie, Hui; Zhou, Wancheng; Ren, Zhaowen

2018-01-01

SiO2 was successfully coated on the surface of flaky carbonyl iron particles using a chemical bath deposition method in the presence of 3-aminopropyl triethoxysilane (APTES). The morphologies, composition, valence states of elements, as well as antioxidation and electromagnetic properties of the samples were characterized by scanning electron microscope (SEM), energy dispersive spectrometer (EDS), X-ray photoelectron spectroscopy (XPS), thermogravimetric (TG) and microwave network analyzer. TG curve shows the obvious weight gain of carbonyl iron was deferred to 360 °C after SiO2-coated, which can be ascribed to the exits of SiO2 overlayer. Compared with the raw carbonyl iron, SiO2-coated sample shows good wave absorption performance due to its impedance matching. The electromagnetic properties of raw and SiO2-coated carbonyl iron particles were characterized in X band before and after heat treatment at 250 °C for 10 h. It was established that SiO2-coated carbonyl iron demonstrate good thermal stability, indicating SiO2-coating is useful in the usage of microwave absorbers operating at temperature up to 250 °C.

New structure of high-pressure body-centered orthorhombic Fe 2SiO 4

DOE PAGES

Yamanaka, Takamitsu; Kyono, Atsushi; Nakamoto, Yuki; ...

2015-08-01

Here, a structural change in Fe 2SiO 4 spinel and the structure of a new high pressure phase are determined by Rietveld 26 profile fitting of x-ray diffraction data up to 64 GPa at ambient temperature. The compression curve of the spinel is discontinuous at approximately 20 GPa. Fe Kβ x-ray emission measurements at high pressure show that the transition from a high spin (HS) to an intermediate spin (IS) state begins at 17 GPa in the spinel phase. The IS electronic state is gradually enhanced with pressure, which results in an isostructural phase transition. A transition from the cubic spinel structure to a body centered orthorhombic phase (I-Fe 2SiO 4) with space group Imma and Z=4 was observed at approximately 34 GPa. The structure of I-Fe 2SiO 4 has two crystallographically distinct FeO 6 octahedra, which are arranged in layers parallel to (101) and (011) and are very similar to the layers of FeO 6 octahedra that constitute the spinel structure. Silicon also exists in six-fold coordination in I-Fe 2SiO 4. The transformation to the new high-pressure phase is reversible under decompression at ambient temperature. A Martensitic transformation of each slab of the spinel structure with translation vector [more » $$\\vec{1/8}$$ $$\\vec{1/8}$$ $$\\vec{1/8}$$] generates the I-Fe 2SiO 4 structure. Laser heating of I-Fe 2SiO 4 at 1500 K results in a decomposition of the material to rhombohedral FeO and SiO 2 stishovite.« less

Surface properties of SiO2 with and without H2O2 treatment as gate dielectrics for pentacene thin-film transistor applications

NASA Astrophysics Data System (ADS)

Hung, Cheng-Chun; Lin, Yow-Jon

2018-01-01

The effect of H2O2 treatment on the surface properties of SiO2 is studied. H2O2 treatment leads to the formation of Si(sbnd OH)x at the SiO2 surface that serves to reduce the number of trap states, inducing the shift of the Fermi level toward the conduction band minimum. H2O2 treatment also leads to a noticeable reduction in the value of the SiO2 capacitance per unit area. The effect of SiO2 layers with H2O2 treatment on the behavior of carrier transports for the pentacene/SiO2-based organic thin-film transistor (OTFT) is also studied. Experimental identification confirms that the shift of the threshold voltage towards negative gate-source voltages is due to the reduced number of trap states in SiO2 near the pentacene/SiO2 interface. The existence of a hydrogenated layer between pentacene and SiO2 leads to a change in the pentacene-SiO2 interaction, increasing the value of the carrier mobility.

Influence of SiO2 Addition on Properties of PTFE/TiO2 Microwave Composites

NASA Astrophysics Data System (ADS)

Yuan, Ying; Wang, Jie; Yao, Minghao; Tang, Bin; Li, Enzhu; Zhang, Shuren

2018-01-01

Composite substrates for microwave circuit applications have been fabricated by filling polytetrafluoroethylene (PTFE) polymer matrix with ceramic powder consisting of rutile TiO2 ( D 50 ≈ 5 μm) partially substituted with fused amorphous SiO2 ( D 50 ≈ 8 μm) with composition x vol.% SiO2 + (50 - x) vol.% TiO2 ( x = 0, 3, 6, 9, 12), and the effects of SiO2 addition on characteristics such as the density, moisture absorption, microwave dielectric properties, and thermal properties systematically investigated. The results show that the filler was well distributed throughout the matrix. High dielectric constant ( ɛ r > 7.19) and extremely low moisture absorption (<0.02%) were obtained, resulting from the relatively high density of the composites. The ceramic particles served as barriers and improved the thermal stability of the PTFE polymer, retarding its decomposition. The temperature coefficient of dielectric constant ( τ ɛ ) of the composites shifted toward the positive direction (from - 309 ppm/°C to - 179 ppm/°C) as the SiO2 content was increased, while the coefficient of thermal expansion remained almost unchanged (˜ 35 ppm/°C).

Design of flexible PANI-coated CuO-TiO2-SiO2 heterostructure nanofibers with high ammonia sensing response values

NASA Astrophysics Data System (ADS)

Pang, Zengyuan; Nie, Qingxin; Lv, Pengfei; Yu, Jian; Huang, Fenglin; Wei, Qufu

2017-06-01

We report a room-temperature ammonia sensor with extra high response values and ideal flexibility, including polyaniline (PANI)-coated titanium dioxide-silicon dioxide (TiO2-SiO2) or copper oxide-titanium dioxide-silicon dioxide (CuO-TiO2-SiO2) composite nanofibers. Such flexible inorganic TiO2-SiO2 and CuO-TiO2-SiO2 composite nanofibers were prepared by electrospinning, followed by calcination. Then, in situ polymerization of aniline monomers was carried out with inorganic TiO2-SiO2 and CuO-TiO2-SiO2 composite nanofibers as templates. Gas sensing tests at room temperature indicated that the obtained CuO-TiO2-SiO2/PANI composite nanofibers had much higher response values to ammonia gas (ca. 45.67-100 ppm) than most of those reported before as well as the prepared TiO2-SiO2/PANI composite nanofibers here. These excellent sensing properties may be due to the P-N, P-P heterojunctions and a structure similar to field-effect transistors formed on the interfaces between PANI, TiO2, and CuO, which is p-type, n-type, and p-type semiconductor, respectively. In addition, the prepared free-standing CuO-TiO2-SiO2/PANI composite nanofiber membrane was easy to handle and possessed ideal flexibility, which is promising for potential applications in wearable sensors in the future.

Design of flexible PANI-coated CuO-TiO2-SiO2 heterostructure nanofibers with high ammonia sensing response values.

PubMed

Pang, Zengyuan; Nie, Qingxin; Lv, Pengfei; Yu, Jian; Huang, Fenglin; Wei, Qufu

2017-06-02

We report a room-temperature ammonia sensor with extra high response values and ideal flexibility, including polyaniline (PANI)-coated titanium dioxide-silicon dioxide (TiO 2 -SiO 2 ) or copper oxide-titanium dioxide-silicon dioxide (CuO-TiO 2 -SiO 2 ) composite nanofibers. Such flexible inorganic TiO 2 -SiO 2 and CuO-TiO 2 -SiO 2 composite nanofibers were prepared by electrospinning, followed by calcination. Then, in situ polymerization of aniline monomers was carried out with inorganic TiO 2 -SiO 2 and CuO-TiO 2 -SiO 2 composite nanofibers as templates. Gas sensing tests at room temperature indicated that the obtained CuO-TiO 2 -SiO 2 /PANI composite nanofibers had much higher response values to ammonia gas (ca. 45.67-100 ppm) than most of those reported before as well as the prepared TiO 2 -SiO 2 /PANI composite nanofibers here. These excellent sensing properties may be due to the P-N, P-P heterojunctions and a structure similar to field-effect transistors formed on the interfaces between PANI, TiO 2 , and CuO, which is p-type, n-type, and p-type semiconductor, respectively. In addition, the prepared free-standing CuO-TiO 2 -SiO 2 /PANI composite nanofiber membrane was easy to handle and possessed ideal flexibility, which is promising for potential applications in wearable sensors in the future.

Morphology and crystalline phase study of electrospun TiO2 SiO2 nanofibres

NASA Astrophysics Data System (ADS)

Ding, Bin; Kim, Hakyong; Kim, Chulki; Khil, Myungseob; Park, Soojin

2003-05-01

Nanofibres of TiO2-SiO2 (Ti:Si = 50: 50 mol%) with diameters of 50-400 nm were prepared by calcining electrospun nanofibres of polyvinyl acetate (PVac)/titania-silica composite as precursor. These PVac/titania-silica hybrid nanofibres were obtained from a homogenous solution of PVac with a sol-gel of titanium isopropoxide (TiP) and tetraethoxysilane by using the electrospinning technique. The nanofibres were characterized by scanning electron microscopy (SEM), wide-angle x-ray diffraction (WAXD), Fourier transform infrared (FTIR) spectroscopy and Brunauer-Emmett-Teller (BET) surface area. SEM, WAXD and FTIR results indicated that the morphology and crystalline phase of TiO2-SiO2 nanofibres were strongly influenced by the calcination temperature and the content of titania and silica in the nanofibres. Additionally, the BET results showed that the surface area of TiO2-SiO2 nanofibres was decreased with increasing calcination temperature and the content of titania and silica in nanofibres.

Evaporation kinetics of Mg2SiO4 crystals and melts from molecular dynamics simulations

NASA Technical Reports Server (NTRS)

Kubicki, J. D.; Stolper, E. M.

1993-01-01

Computer simulations based on the molecular dynamics (MD) technique were used to study the mechanisms and kinetics of free evaporation from crystalline and molten forsterite (i.e., Mg2SiO4) on an atomic level. The interatomic potential employed for these simulations reproduces the energetics of bonding in forsterite and in gas-phase MgO and SiO2 reasonably accurately. Results of the simulation include predicted evaporation rates, diffusion rates, and reaction mechanisms for Mg2SiO4(s or l) yields 2Mg(g) + 20(g) + SiO2(g).

Optical properties of ion-beam-synthesized Au nanoparticles in SiO2 matrix

NASA Astrophysics Data System (ADS)

Hsieh, Chang-Lin; Oyoshi, Keiji; Chao, Der-Sheng; Tsai, Hsu-Sheng; Hong, Wei-Lun; Takeda, Yoshihiko; Liang, Jenq-Horng

2016-05-01

In recent years, gold (Au) nanoparticles have been synthesized via various methods and used in optical and biomedical detection. Au nanoparticles contain some remarkable dimension-dependent optical properties due to surface plasmon resonance (SPR) in Au nanoparticles which causes high absorption in visible light regions. Since SPR in well-crystallized Au nanoparticles can enhance the local electromagnetic field, it is thus expected that greater efficiency in the photoluminescence (PL) originating from oxygen deficiency centers (ODC) can be achieved in Au-implanted SiO2 matrix. In order to demonstrate the enhancement of PL, Au nanoparticles were formed in SiO2 film using ion beam synthesis and their optical and microstructural properties were also investigated in this study. The results revealed that a clear absorption peak at approximately 530 nm was identified in the UV-Vis spectra and was attributed to SPR induced by Au nanoparticles in SiO2. The SPR of Au nanoparticles is also dependent on thermal treatment conditions, such as post-annealing temperature and ambient. The Au nanoparticle-containing SiO2 film also displayed several distinctive peaks at approximately 320, 360, 460, and 600 nm in the PL spectra and were found to be associated with ODC-related defects and non-bridging oxygen hole centers (NBOHC) in SiO2. In addition, the PL peak intensities increased as post-annealing temperature increased, a finding contradictory to the defect recovery but highly consistent with the SPR tendency. A maximum PL emission was achieved when the Au-implanted SiO2 film was annealed at 1100 °C for 1 h under N2. Therefore, the existence of Au nanoparticles in SiO2 film can induce SPR effects as well as enhance PL emission resulting from defect-related luminescence centers.

Excellent Brightness with Shortening Lifetime of Textured Zn2SiO4:Mn2+ Phosphor Films on Quartz Glass

NASA Astrophysics Data System (ADS)

Park, Jehong; Park, Kwangwon; Lee, Jaebum; Kim, Jongsu; Kim, Seongsin Margaret; Kung, Patrick

2010-04-01

Green-emissive textured Zn2SiO4:Mn2+ phosphor films were fabricated by the thermal diffusion of ZnO:Mn on quartz glass. The Zn2SiO4:Mn2+ phosphor films became textured along several hexagonal directions and their chemical composition was continuously graded at the interface. The decay time of Mn2+ was as short as 4.4 ms, and the optical transition probability of the films defined as the inverse of decay time showed a strong correlation with film texture degree as a function of annealing temperature. The brightest Zn2SiO4:Mn2+ film showed a photoluminescent brightness as high as 65% compared with a commercial Zn2SiO4:Mn2+ phosphor powder screen and a maximum absolute transparency of 70%. These excellent optical properties are explained by the combination of the unique textured structure and continuous grading of the Zn2SiO4:Mn2+ chemical composition at the interface.

Reflectance modulation using SiO2/TiO2 multilayer structures prepared by sol-gel spin coating process for optical applications

NASA Astrophysics Data System (ADS)

Dubey, R. S.; Ganesan, V.

2017-11-01

Passive devices made of SiO2/TiO2 bilayers have been demanded for the molding of electromagnetic waves in optical waveguides, microcavities, solar cells, sensors and so on. Here, we present the fabrication and characterization of SiO2/TiO2 multilayer structures as reflectors. The refractive indices were found to be 1.43 & 2.0 with thicknesses 230 & 70 nm corresponding to the SiO2 and TiO2 films respectively. AFM surface topography study showed little bit large surface roughness of the TiO2 as compared to SiO2 film due to its large grain size. The corresponding reflectance enhancement was noticed with the increased number of bilayers of SiO2/TiO2 films. Furthermore, six alternate layers of SiO2/TiO2 demonstrated the as much as 78% reflectance in the near-infrared wavelength range.

Structure and crystallization of SiO2 and B2O3 doped lithium disilicate glasses from theory and experiment.

PubMed

Erlebach, Andreas; Thieme, Katrin; Sierka, Marek; Rüssel, Christian

2017-09-27

Solid solutions of SiO 2 and B 2 O 3 in Li 2 O·2SiO 2 are synthesized and characterized for the first time. Their structure and crystallization mechanisms are investigated employing a combination of simulations at the density functional theory level and experiments on the crystallization of SiO 2 and B 2 O 3 doped lithium disilicate glasses. The remarkable agreement of calculated and experimentally determined cell parameters reveals the preferential, kinetically controlled incorporation of [SiO 4 ] and [BO 4 ] at the Li + lattice sites of the Li 2 O·2SiO 2 crystal structure. While the addition of SiO 2 increases the glass viscosity resulting in lower crystal growth velocities, glasses containing B 2 O 3 show a reduction of both viscosities and crystal growth velocities. These observations could be rationalized by a change of the chemical composition of the glass matrix surrounding the precipitated crystal phase during the course of crystallization, which leads to a deceleration of the attachment of building units required for further crystal growth at the liquid-crystal interface.

Beyond sixfold coordinated Si in SiO2 glass at ultrahigh pressures.

PubMed

Prescher, Clemens; Prakapenka, Vitali B; Stefanski, Johannes; Jahn, Sandro; Skinner, Lawrie B; Wang, Yanbin

2017-09-19

We investigated the structure of SiO 2 glass up to 172 GPa using high-energy X-ray diffraction. The combination of a multichannel collimator with diamond anvil cells enabled the measurement of structural changes in silica glass with total X-ray diffraction to previously unachievable pressures. We show that SiO 2 first undergoes a change in Si-O coordination number from fourfold to sixfold between 15 and 50 GPa, in agreement with previous investigations. Above 50 GPa, the estimated coordination number continuously increases from 6 to 6.8 at 172 GPa. Si-O bond length shows first an increase due to the fourfold to sixfold coordination change and then a smaller linear decrease up to 172 GPa. We reconcile the changes in relation to the oxygen-packing fraction, showing that oxygen packing decreases at ultrahigh pressures to accommodate the higher than sixfold Si-O coordination. These results give experimental insight into the structural changes of silicate glasses as analogue materials for silicate melts at ultrahigh pressures.

Solution-derived SiO2 gate insulator formed by CO2 laser annealing for polycrystalline silicon thin-film transistors

NASA Astrophysics Data System (ADS)

Hishitani, Daisuke; Horita, Masahiro; Ishikawa, Yasuaki; Ikenoue, Hiroshi; Uraoka, Yukiharu

2017-05-01

The formation of perhydropolysilazane (PHPS)-based SiO2 films by CO2 laser annealing is proposed. Irradiation with a CO2 laser with optimum fluence transformed a prebaked PHPS film into a SiO2 film with uniform composition in the thickness direction. Polycrystalline silicon thin-film transistors (poly-Si TFTs) with a SiO2 film as the gate insulator were fabricated. When the SiO2 film was formed by CO2 laser annealing (CO2LA) at the optimum fluence of 20 mJ/cm2, the film had fewer OH groups which was one-twentieth that of the furnace annealed PHPS film and one-hundredth that of the SiO2 film deposited by plasma-enhanced chemical vapor deposition (PECVD) using tetraethyl orthosilicate (TEOS). The resulting TFTs using PHPS showed a clear transistor operation with a field-effect mobility of 37.9 ± 1.2 cm2 V-1 s-1, a threshold voltage of 9.8 ± 0.2 V, and a subthreshold swing of 0.76 ± 0.02 V/decade. The characteristics of such TFTs were as good as those of a poly-Si TFT with a SiO2 gate insulator prepared by PECVD using TEOS.

The preparation and photocatalytic activity of CdS/(Cal-Ta2O5-SiO2) composite photocatalyst under visible light

NASA Astrophysics Data System (ADS)

Li, Juxia

2018-02-01

CdS/(Cal-Ta2O5-SiO2) composite photocatalyst has been successfully fabricated via wet chemistry method. Ta2O5-SiO2 with multi-step Ta2O5 deposition on SiO2 has more Ta2O5 on SiO2 to ensure the active sites. Trough multi-step calcination, Ta2O5 can load on SiO2 with uniform and stable, which make it have high photocatalytic activity. The obtained samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), diffuse reflectance ultraviolet-visible spectroscopy (UV-vis) and photoluminescence spectroscopy (PL). Without any co-catalysts, the as-prepared CdS/(Cal-Ta2O5-SiO2) exhibited remarkable photocatalytic activity and recyclability both in the degradation of rhodamine B and in the hydrogen production from water splitting under visible light.

Size-tunable synthesis of SiO(2) nanotubes via a simple in situ templatelike process.

PubMed

Shen, Guozhen; Bando, Yoshio; Golberg, Dmitri

2006-11-23

SiO(2) nanotubes with tunable diameters and lengths have been successfully synthesized via a simple in situ templatelike process by thermal evaporation of SiO, ZnS, and GaN in a vertical induction furnace. The structure and morphologies were systematically investigated using X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and energy-dispersive X-ray spectrometry. Studies found that both the diameters and lengths of the SiO(2) nanotubes can be effectively tuned by simply changing the reaction temperatures. The range of changes was from 30 nm (diameter) and several hundred micrometers (length) at 1450 degrees C to 100 nm (diameter) and 2-10 micrometers (length) at 1300 degrees C. Varying some other experimental parameters results in the formation of additional SiO(2)-based nanostructures, such as core-shell ZnS-SiO(2) nanocables, ZnS nanoparticle filled SiO(2) nanotubes, and fluffy SiO(2) spheres. Based on the observations, an in situ templatelike process was proposed to explain the possible growth mechanism.

Preparation, chromatographic evaluation and application of adenosine 5'-monophosphate modified ZrO2/SiO2 stationary phase in hydrophilic interaction chromatography.

PubMed

Wang, Qing; Luo, Zhi-Yuan; Ye, Mao; Wang, Yu-Zhuo; Xu, Li; Shi, Zhi-Guo; Xu, Lanying

2015-02-27

The zirconia-coated silica (ZrO2/SiO2) material was obtained by coupling layer-by-layer (LbL) self-assembly method and sol-gel technology, to take dual advantages of the suitable porous structure of SiO2 and basic resistance of ZrO2. Adenosine 5'-monophosphate (5'-AMP) was then self-assembled onto ZrO2/SiO2 via Lewis acid-base interaction, generating 5'-AMP-ZrO2/SiO2. The chromatographic properties of 5'-AMP-ZrO2/SiO2 were systemically studied by evaluating the effect of acetonitrile content, pH and buffer concentration in the mobile phase. The results demonstrated that the 5'-AMP-ZrO2/SiO2 possessed hydrophilic interaction chromatographic (HILIC) property comprising hydrophilic, hydrogen-bonding, electrostatic and ion-exchange interactions. For basic analytes, the column efficiency of ZrO2/SiO2 and 5'-AMP-ZrO2/SiO2 was superior to the bare ZrO2, and different selectivity was obtained after the introduction of 5'-AMP. For acidic analytes, good resolution was obtained on 5'-AMP-ZrO2/SiO2 while the analysis failed on the bare ZrO2 column owing to strong adsorption. Hence, the proposed 5'-AMP-ZrO2/SiO2 had great potential in analyzing acidic compounds in HILIC mode. It was an extended application of ZrO2 based SP. Copyright © 2015 Elsevier B.V. All rights reserved.

Preparation of polystyrene/SiO2 microsphere via Pickering emulsion polymerization: Synergistic effect of SiO2 concentrations and initiator sorts

NASA Astrophysics Data System (ADS)

Zhou, Haiou; Shi, Tiejun; Zhou, Xun

2013-02-01

In this paper, polystyrene (PS)/SiO2 microspheres were successfully prepared via Pickering emulsion polymerization stabilized solely by ethacryloxypropyltrimethoxysilane (MPTMS) modified SiO2 nanoparticles. The formation mechanisms of PS/SiO2 microspheres with different morphology were investigated under various Pickering emulsion polymerization conditions. The results showed that SiO2 concentrations and initiator sorts would synergistically impact on the morphology of products corresponding to distinct formation mechanisms. When SiO2 concentrations was low and water-solute initiator potassium persulfate (KPS) was used, aqueous nucleation was dominant, which was deduced to the formation of dispersive microspheres sparsely anchored by SiO2 particles. When SiO2 concentrations was increased and oil-solute initiator azobisisobutyronitrile (AIBN) was applied, nucleation in oil phase prevailed which lead to the formation of microspheres densely packed by SiO2 particles.

Growth and luminescent properties of Lu2SiO5 and Lu2SiO5:Ce single crystalline films

NASA Astrophysics Data System (ADS)

Zorenko, Yu; Nikl, M.; Gorbenko, V.; Mares, J. A.; Savchyn, V.; Voznyak, T.; Solsky, I.; Grynyov, B.; Sidletskiy, O.; Kurtsev, D.; Beitlerova, A.; Kucerkova, R.

2010-11-01

Single crystalline films (SCF) of Lu2SiO5 (LSO) and Lu2SiO5:Ce (LSO:Ce) silicates with thickness of 2.5-21 μm were crystallised by liquid phase epitaxy method onto undoped LSO substrates from melt-solution based on PbO-B2O3 flux. The luminescence and scintillation properties of LSO and LSO:Ce SCFs were compared with the properties of a reference LSO:Ce and LYSO:Ce crystals. The light yield (LY) of LSO and LSO:Ce SCF reaches up 30 % and 145 %, respectively, of that of a reference LSO:Ce crystal under excitation by α-particles of 241Am source (5.5 MeV). We found that the luminescence spectrum of LSO:Ce SCF is red-shifted with respect to the spectrum of a reference LSO:Ce crystal. Differences in luminescence properties of LSO:Ce SCF and single crystal are explained by the different distribution of Ce3+ over the Lu1 and Lu2 positions of LSO host and are also due to Pb2+ contamination in the former.

Ca2 Al2 SiO7 :Ce3+ phosphors for mechanoluminescence dosimetry.

PubMed

Tiwari, Geetanjali; Brahme, Nameeta; Sharma, Ravi; Bisen, D P; Sao, Sanjay Kumar; Sahu, Ishwar Prasad

2016-12-01

A series of Ce 3+ ion single-doped Ca 2 Al 2 SiO 7 phosphors was synthesized by a combustion-assisted method at an initiating temperature of 600 °C. The samples were annealed at 1100 °C for 3 h and their X-ray diffraction patterns confirmed a tetragonal structure. The phase structure, particle size, surface morphology and elemental analysis were analyzed using X-ray diffraction (XRD), transmission electron microscope (TEM), scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) spectroscopy techniques. Thermoluminescence (TL) intensity increased with increase in ultraviolet (UV) light exposure time up to 15 min. With further increase in the UV irradiation time the TL intensity decreases. The increase in TL intensity indicates that trap concentration increased with UV exposure time. A broad peak at 121 °C suggested the existence of a trapping level. The peak of mechanoluminescence (ML) intensity versus time curve increased linearly with increasing impact velocity of the moving piston. Mechanoluminescence intensity increased with increase in UV irradiation time up to 15 min. Under UV-irradiation excitation, the TL and ML emission spectra of Ca 2 Al 2 SiO 7 :Ce 3+ phosphor showed the characteristic emission of Ce 3+ peaking at 400 nm (UV-violet) and originating from the Ce 3+ transitions of 5d-4f ( 2 F 5/2 and 2 F 7/2 ). The photoluminescence (PL) emission spectra for Ca 2 Al 2 SiO 7 :Ce 3+ were similar to the ML/TL emission spectra. The mechanism of ML excitation and the suitability of the Ca 2 Al 2 SiO 7 :Ce 3+ phosphor for radiation dosimetry are discussed. Copyright © 2016 John Wiley & Sons, Ltd. Copyright © 2016 John Wiley & Sons, Ltd.

Facile synthesis of microporous SiO2/triangular Ag composite nanostructures for photocatalysis

NASA Astrophysics Data System (ADS)

Sirohi, Sidhharth; Singh, Anandpreet; Dagar, Chakit; Saini, Gajender; Pani, Balaram; Nain, Ratyakshi

2017-11-01

In this article, we present a novel fabrication of microporous SiO2/triangular Ag nanoparticles for dye (methylene blue) adsorption and plasmon-mediated degradation. Microporous SiO2 nanoparticles with pore size <2 nm were synthesized using cetyltrimethylammonium bromide as a structure-directing agent and functionalized with APTMS ((3-aminopropyl) trimethoxysilane) to introduce amine groups. Amine-functionalized microporous silica was used for adsorption of triangular silver (Ag) nanoparticles. The synthesized microporous SiO2 nanostructures were investigated for adsorption of different dyes including methylene blue, congo red, direct green 26 and curcumin crystalline. Amine-functionalized microporous SiO2/triangular Ag nanostructures were used for plasmon-mediated photocatalysis of methylene blue. The experimental results revealed that the large surface area of microporous silica facilitated adsorption of dye. Triangular Ag nanoparticles, due to their better charge carrier generation and enhanced surface plasmon resonance, further enhanced the photocatalysis performance.

ZrO2 film interfaces with Si and SiO2

NASA Astrophysics Data System (ADS)

Lopez, C. M.; Suvorova, N. A.; Irene, E. A.; Suvorova, A. A.; Saunders, M.

2005-08-01

The interface formed by the thermal oxidation of sputter-deposited Zr metal onto Si(100)- and SiO2-coated Si(100) wafers was studied in situ and in real time using spectroscopic ellipsometry (SE) in the 1.5-4.5 photon energy range and mass spectrometry of recoiled ions (MSRI). SE yielded optical properties for the film and interface and MSRI yielded film and interface composition. An optical model was developed and verified using transmission electron microscopy. Interfacial reaction of the ZrO2 was observed for both substrates, with more interaction for Si substrates. Equivalent oxide thicknesses and interface trap levels were determined on capacitors with lower trap levels found on samples with a thicker SiO2 underlayer. In addition to the optical properties for the intermixed interface layer, the optical properties for Zr metal and unreacted ZrO2 are also reported.

Efficiency improvement of InGaN light emitting diodes with embedded self-assembled SiO2 nanosphere arrays

NASA Astrophysics Data System (ADS)

Zhang, Yonghui; Wei, Tongbo; Wang, Junxi; Fan, Chao; Chen, Yu; Hu, Qiang; Li, Jinmin

2014-05-01

In this study, the periodic SiO2 nanosphere nanopatterned sapphire substrate (SiO2-NPSS) was made using self-assembled SiO2 nanosphere monolayer template and inductively coupled plasma (ICP) etching. And the self-assembled SiO2 nanosphere monolayer was directly embedded into the GaN/sapphire interface by nanoscale epitaxial lateral overgrowth (NELOG). For comparison, a common nanopatterned sapphire substrate (C-NPSS) was also made through dry etching with the SiO2 nanospheres used as the mask. Compared with LEDs grown on C-NPSS and flat sapphire substrate (FSS), the external quantum efficiency of LEDs with SiO2 nanopheres (SiO2-NPSS) was increased by 30.7% and 81.9% under a driving current 350 mA. The SiO2-NPSS not only improved the crystalline quality of GaN but also enhanced the light extraction efficiency (LEE) of LED. And the SiO2-NPSS LED also showed more light in vertical direction and more uniform light distribution. By finite-difference time-domain (FDTD) simulation, we confirmed that more light could be reflected from the GaN/SiO2 interface than the GaN/sapphire interface because the refractive index of SiO2 was lower than that of sapphire. Therefore, LED grown on the SiO2-NPSS showed superior light extraction efficiency compared to that on C-NPSS.

Effect of concentration variation on 2.0 µm emission of Ho3+-doped SiO2-Al2O3-Na2CO3-SrF2-CaF2 oxyfluorosilicate glasses

NASA Astrophysics Data System (ADS)

Gelija, Devarajulu; Borelli, Deva Prasad Raju

2018-02-01

The concentration variation of Ho3+ ion-doped SiO2-Al2O3-Na2CO3-SrF2-CaF2 glasses has been prepared by conventional melt quenching method. The thermal stability of 1 mol % of Ho3+-doped oxyfluorosilicate glass has been calculated using the differential thermal analysis (DTA) spectra. The phenomenological Judd-Ofelt intensity parameters Ωλ ( λ = 2, 4 and 6) were calculated for all concentrations of Ho3+ ions. The luminescence spectra in visible region of Ho3+ ion-doped glasses were recorded under the excitation wavelength of 452 nm. The spectra consists of several intense emission bands (5F4, 5S2) → 5I8 (547 nm), 5F3 → 5I8 (647 nm), 5F5 → 5I7 (660 nm) and (5F4, 5S2) → 5I7 (750 nm) in the range 500-780 nm. The fluorescence emission at ˜2.0 µm (5I7 → 5I8) was observed under the excitation of 488 nm Ar-ion laser. The stimulated emission cross section for 5I7 → 5I8 transition (˜2.0 µm) varies from 8.46 to 9.52 × 10-21 cm2, as calculated by the Fuchtbauer-Ladenburg (FL) theory. However, Mc-Cumber theory was used to calculate emission cross section values about 4.24-5.75 × 10-21 cm2 for the 5I7 → 5I8 transition in all concentrations of Ho3+-doped oxyfluorosilicate glasses. Therefore, these results reveal that the 0.5 mol % of Ho3+-doped oxyfluorosilicate glasses, exhibiting higher emission cross section, has potentially been used for laser applications at ˜ 2.0 µm.

Filtering effect of SiO2 optical waveguide ring resonator applied to optoelectronic oscillator.

PubMed

Chen, Jiamin; Zheng, Yongqiu; Xue, Chenyang; Zhang, Chengfei; Chen, Yi

2018-05-14

Single-mode oscillation is crucial to the practicality of optoelectronic oscillator (OEO). Due to the limited by bandwidth and precision of radio frequency (RF) filters, it is difficult to be achieved for the OEO based on the long fiber-optic delay line. So instead of the long fiber-optic delay line, SiO 2 optical waveguide ring resonator (OWRR) with high-Q and mode selection is first presented to be applied to OEO. The OEOs based on the minimum loop and SiO 2 OWRR are constructed. The oscillation characteristics of the minimum loop OEO and the transmission characteristics of the SiO 2 OWRR are simulated by MATLAB, respectively. The filtering effect of the SiO 2 OWRR applied to the OEO is verified theoretically by comparing these simulation results. Subsequently, the contrastive experiments of the above two OEOs on oscillation modes are carried out. The oscillation mode spacing of 40.32 MHz and 2.137 GHz are obtained. These results show that the SiO 2 OWRR can function as an excellent 'filter' in the minimum loop of the OEO. Moreover, the side mode suppression ratio and the phase noise of the OEO have been improved. Our experimental results demonstrate that the OEO adopting SiO 2 OWRR is feasible to achieve the single-mode oscillation and obtain better performance microwave signals.

New structure of high-pressure body-centered orthorhombic Fe 2 SiO 4

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yamanaka, Takamitsu; Kyono, Atsushi; Nakamoto, Yuki

2015-08-01

A structural change in Fe2SiO4 spinel (ringwoodite) has been found by synchrotron powder diffraction study and the structure of a new high-pressure phase was determined by Monte-Carlo simulation method and Rietveld profile fitting of X-ray diffraction data up to 64 GPa at ambient temperature. A transition from the cubic spinel structure to a body centered orthorhombic phase (I-Fe2SiO4) with space group Imma and Z = 4 was observed at approximately 34 GPa. The structure of I-Fe2SiO4 has two crystallographically independent FeO6 octahedra. Iron resides in two different sites of sixfold coordination: Fe1 and Fe2, which are arranged in layers parallelmore » to (101) and (011) and are very similar to the layers of FeO6 octahedra in the spinel structure. Silicon is located in the sixfold coordination in I-Fe2SiO4. The transformation to the new high-pressure phase is reversible under decompression at ambient temperature. A martensitic transformation of each slab of the spinel structure with translation vector Embedded Image generates the I-Fe2SiO4 structure. Laser heating of I-Fe2SiO4 at 1500 K results in a decomposition of the material to rhombohedral FeO and SiO2 stishovite. FeKβ X-ray emission measurements at high pressure up to 65 GPa show that the transition from a high spin (HS) to an intermediate spin (IS) state begins at 17 GPa in the spinel phase. The IS electron spin state is gradually enhanced with pressure. The Fe2+ ion at the octahedral site changes the ion radius under compression at the low spin, which results in the changes of the lattice parameter and the deformation of the octahedra of the spinel structure. The compression curve of the lattice parameter of the spinel is discontinuous at ~20 GPa. The spin transition induces an isostructural change.« less

Radiation-induced amorphization of Ce-doped Mg2Y8(SiO4)6O2 silicate apatite

NASA Astrophysics Data System (ADS)

Zhou, Jianren; Yao, Tiankai; Lian, Jie; Shen, Yiqiang; Dong, Zhili; Lu, Fengyuan

2016-07-01

Ce-doped Mg2Y8(SiO4)6O2 silicate apatite (Ce = 0.05 and 0.5) were irradiated with 1 MeV Kr2+ ion beam irradiation at different temperatures and their radiation response and the cation composition dependence of the radiation-induced amorphization were studied by in situ TEM. The two Ce-doped Mg2Y8(SiO4)6O2 silicate apatites are sensitive to ion beam induced amorphization with a low critical dose (0.096 dpa) at room temperature, and exhibits significantly different radiation tolerance at elevated temperatures. Ce concentration at the apatite AI site plays a critical role in determining the radiation response of this silicate apatite, in which the Ce3+ rich Mg2Y7.5Ce0.5(SiO4)6O2 displays lower amorphization susceptibility than Mg2Y7.95Ce0.05(SiO4)6O2 with a lower Ce3+ occupancy at the AI sites. The critical temperature (Tc) and activation energy (Ea) change from 667.5 ± 33 K and 0.162 eV of Mg2Y7.5Ce0.5(SiO4)6O2 to 963.6 ± 64 K and 0.206 eV of Mg2Y7.95Ce0.05(SiO4)6O2. We demonstrate that the radiation tolerance can be controlled by varying the chemical composition, and enhanced radiation tolerance is achieved by increasing the Ce concentration at the AI site.

Fourier transform infrared spectroscopic study of gamma irradiated SiO2 nanoparticles

NASA Astrophysics Data System (ADS)

Huseynov, Elchin; Garibov, Adil; Mehdiyeva, Ravan; Huseynova, Efsane

2018-03-01

In the present work, nano SiO2 particles are investigated before and after gamma irradiation (25, 50, 75, 100 and 200 kGy) using Fourier transform infrared (FTIR) spectroscopy method for the wavenumber between 400-4000 cm-1. It is found that as a result of spectroscopic analysis, five new peaks have appeared after gamma radiation. Two of new obtained peaks (which are located at 687 cm-1 and 2357 cm-1 of wavenumber) were formed as a result of gamma radiation interaction with Si-O bonds. Another three new peaks (peaks appropriate to 941, 2052 and 2357 cm-1 values of wavenumber) appear as a result of interaction of water with nano SiO2 particles after gamma irradiation. It has been defined as asymmetrical bending vibration, symmetrical bending vibration, symmetrical stretching vibration and asymmetrical stretching vibration of Si-O bonds appropriate to peaks.

NaF-assisted combustion synthesis of MoSi2 nanoparticles and their densification behavior

NASA Astrophysics Data System (ADS)

Nersisyan, Hayk H.; Lee, Tae Hyuk; Ri, Vladislav; Lee, Jong Hyeon; Suh, Hoyoung; Kim, Jin-Gyu; Son, Hyeon Taek; Kim, Yong-Ho

2017-03-01

The exothermic reduction of oxides mixture (MoO3+2SiO2) by magnesium in NaF melt enables the synthesis of nanocrystalline MoSi2 powders in near-quantitative yields. The combustion wave with temperature of about 1000-1200 °C was recorded in highly diluted by NaF starting mixtures. The by-products of combustion reaction (NaF and MgO) were subsequently removed by leaching with acid and washing with water. The as-prepared MoSi2 nanopowder composed of spherical and dendritic shape particles was consolidated using the spark plasma sintering method at 1200-1500 °C and 50 MPa for 10 min. The result was dense compacts (98.6% theoretical density) possessing submicron grains and exhibiting hardness of 8.74-12.92 GPa.

Design and fabrication of a large area freestanding compressive stress SiO2 optical window

NASA Astrophysics Data System (ADS)

Van Toan, Nguyen; Sangu, Suguru; Ono, Takahito

2016-07-01

This paper reports the design and fabrication of a 7.2 mm  ×  9.6 mm freestanding compressive stress SiO2 optical window without buckling. An application of the SiO2 optical window with and without liquid penetration has been demonstrated for an optical modulator and its optical characteristic is evaluated by using an image sensor. Two methods for SiO2 optical window fabrication have been presented. The first method is a combination of silicon etching and a thermal oxidation process. Silicon capillaries fabricated by deep reactive ion etching (deep RIE) are completely oxidized to form the SiO2 capillaries. The large compressive stress of the oxide causes buckling of the optical window, which is reduced by optimizing the design of the device structure. A magnetron-type RIE, which is investigated for deep SiO2 etching, is the second method. This method achieves deep SiO2 etching together with smooth surfaces, vertical shapes and a high aspect ratio. Additionally, in order to avoid a wrinkling optical window, the idea of a Peano curve structure has been proposed to achieve a freestanding compressive stress SiO2 optical window. A 7.2 mm  ×  9.6 mm optical window area without buckling integrated with an image sensor for an optical modulator has been successfully fabricated. The qualitative and quantitative evaluations have been performed in cases with and without liquid penetration.

Positronium formation in SiO2 films grown on Si substrates studied by monoenergetic positron beams

NASA Astrophysics Data System (ADS)

Uedono, A.; Wei, L.; Tanigawa, S.; Suzuki, R.; Ohgaki, H.; Mikado, T.; Kawano, T.; Ohji, Y.

1994-04-01

The annihilation characteristics of positrons in SiO2 films grown on Si substrates were studied by using monoenergetic positron beams. Doppler broadening profiles of the annihilation radiation and lifetime spectra of positrons were measured as a function of incident positron energy for SiO2 (166 nm)/Si specimens fabricated by thermal oxidation. From the measurements, it was found that about 90% of positrons implanted into the SiO2 film annihilate from positronium (Ps) states. This fact was due to the trapping of positrons by open-space defects and a resultant enhanced formation of Ps in such regions. For the SiO2 film grown at 650 °C, the lifetime of ortho-Ps was found to be shorter than that in the film grown at 1000 °C. This result suggests that the volume of open-space defects in the SiO2 film decreased with decreasing the growth rate of the SiO2 film.

Positron annihilation in SiO 2-Si studied by a pulsed slow positron beam

NASA Astrophysics Data System (ADS)

Suzuki, R.; Ohdaira, T.; Uedono, A.; Kobayashi, Y.

2002-06-01

Positron and positronium (Ps) behavior in SiO 2-Si have been studied by means of positron annihilation lifetime spectroscopy (PALS) and age-momentum correlation (AMOC) spectroscopy with a pulsed slow positron beam. The PALS study of SiO 2-Si samples, which were prepared by a dry-oxygen thermal process, revealed that the positrons implanted in the Si substrate and diffused back to the interface do not contribute to the ortho-Ps long-lived component, and the lifetime spectrum of the interface has at least two components. From the AMOC study, the momentum distribution of the ortho-Ps pick-off annihilation in SiO 2, which shows broader momentum distribution than that of crystalline Si, was found to be almost the same as that of free positron annihilation in SiO 2. A varied interface model was proposed to interpret the results of the metal-oxide-semiconductor (MOS) experiments. The narrow momentum distribution found in the n-type MOS with a negative gate bias voltage could be attributed to Ps formation and rapid spin exchange in the SiO 2-Si interface. We have developed a two-dimensional positron lifetime technique, which measures annihilation time and pulse height of the scintillation gamma-ray detector for each event. Using this technique, the positronium behavior in a porous SiO 2 film, grown by a sputtering method, has been studied.

SiO2 nanofluid planar jet impingement cooling on a convex heated plate

NASA Astrophysics Data System (ADS)

Asghari Lafmajani, Neda; Ebrahimi Bidhendi, Mahsa; Ashjaee, Mehdi

2016-12-01

The main objective of this paper is to investigate the heat transfer coefficient of a planar jet of SiO2 nanofluid that impinges vertically on the middle of a convex heated plate for cooling purposes. The planar jet issues from a rectangular slot nozzle. The convex aluminum plate has a thickness, width and length of 0.2, 40 and 130 mm, respectively, and is bent with a radius of 200 mm. A constant heat-flux condition is employed. 7 nm SiO2 particles are added to water to prepare the nanofluid with 0.1, 1 and 2 % (ml SiO2/ml H2O) concentrations. The tests are also performed at different Reynolds numbers from 1803 to 2782. Results indicate that adding the SiO2 nanoparticles can effectively increase both local and average heat transfer coefficients up to 39.37 and 32.78 %, respectively. These positive effects often are more pronounced with increasing Reynolds numbers. This enhancement increases with ascending the concentration of nanofluid, especially from 0.1 to 1 %.

High-pressure Phase Relation In The MgAl2O4-Mg2SiO4 System

NASA Astrophysics Data System (ADS)

Kojitani, H.; Hisatomi, R.; Akaogi, M.

2005-12-01

High-pressure and high-temperature experiments indicate that high-pressure phases of oceanic basalts contain Al-rich phases. MgAl2O4 with calcium ferrite-type crystal structure is considered as a main component of such the Al-rich phases. Since the calcium ferrite-type MgAl2O4 can be synthesized at only the maximum pressure of a Kawai-type high-pressure apparatus with tungsten carbide (WC) anvils, the amount of a synthesized sample is very limited. Therefore, the crystal structure of the calcium ferrite-type MgAl2O4 has been hardly known in detail due to these difficulties in sample synthesis. In our high-pressure experiments in the MgO-Al2O3-SiO2 system, it was shown that Mg2SiO4 component could be dissolved in the MgAl2O4 calcium ferrite. In this study, we tried to synthesize a single phase MgAl2O4 calcium ferrite sample and to make the Rietveld refinement of the XRD pattern of the sample. The high-pressure phase relations in the MgAl2O4-Mg2SiO4 system were studied to know the stability field of the MgAl2O4-Mg2SiO4 calcium ferrite solid solutions. Lattice parameters-composition relation of the MgAl2O4-Mg2SiO4 calcium ferrite solid solutions was also determined. High-pressure and high-temperature experiments were performed by using a Kawai-type high-pressure apparatus at Gakushuin University. WC anvils with truncated edge length of 1.5 mm were used. Heating was made by a Re heater. Temperature was measured by a Pt/Pt-13%Rh thermocouple. Starting materials for the phase relation experiments were the mixture of MgO, Al2O3 and SiO2 with bulk compositions of MgAl2O4:Mg2SiO4 = 90:10, 78:22, 70:30 and 50:50. The starting materials were held at 21-27 GPa and 1600 °C for 3 hours and then were recovered by the quenching method. The MgAl2O4 calcium ferrite sample for the Rietveld analysis was prepared by heating MgAl2O4 spinel at 27 GPa and about 2200 °C for one hour. Powder X-ray diffraction (XRD) profiles of obtained samples were measured by using a X-ray diffractometer

Vaporization of SiO2 and MgSiO3

NASA Astrophysics Data System (ADS)

Stixrude, L. P.; Xiao, B.

2016-12-01

Vaporization of SiO2 and MgSiO3B Xiaoa and L Stixrude*a, a Department of Earth Sciences, University College London, WC1E 6BT London, UK *presenting author, email: l.stixrude@ucl.ac.uk Vaporization is an important process in Earth's earliest evolution during which giant impacts are thought to have produced a transient silicate atmosphere. As experimental data are very limited, little is known of the near-critical vaporization of Earth's major oxide components: MgO and SiO2. We have performed novel ab initio molecular dynamics simulations of vapor-liquid coexistence in the SiO2 and MgSiO3 systems. The simulations, based on density functional theory using the VASP code, begin with a suitably prepared liquid slab embedded in a vacuum. During the dynamical trajectory in the canonical ensemble, we see spontaneous vaporization, leading eventually to a steady-state chemical equilibrium between the two coexisting phases. We locate the liquid-vapor critical point at 6600 K and 0.40 g/cm3 for MgSiO3 and 5300 K and 0.43 g/cm3 for SiO2. By carefully examining the trajectories, we determine the composition and speciation of the vapor. For MgSiO3, We find that the vapor is significantly richer in Mg, O, and atomic (non-molecular) species than extrapolation of low-temperature experimental data has suggested. These results will have important implications for our understanding of the initial chemistry of the Earth and Moon and the initial thermal state of Earth.

Structure-Dependent Spectroscopic Properties of Yb3+-Doped Phosphosilicate Glasses Modified by SiO2

PubMed Central

Wang, Ling; Zeng, Huidan; Yang, Bin; Ye, Feng; Chen, Jianding; Chen, Guorong; Smith, Andew T.; Sun, Luyi

2017-01-01

Yb3+-doped phosphate glasses containing different amounts of SiO2 were successfully synthesized by the conventional melt-quenching method. The influence mechanism of SiO2 on the structural and spectroscopic properties was investigated systematically using the micro-Raman technique. It was worth noting that the glass with 26.7 mol % SiO2 possessed the longest fluorescence lifetime (1.51 ms), the highest gain coefficient (1.10 ms·pm2), the maximum Stark splitting manifold of 2F7/2 level (781 cm−1), and the largest scalar crystal-field NJ and Yb3+ asymmetry degree. Micro-Raman spectra revealed that introducing SiO2 promoted the formation of P=O linkages, but broke the P=O linkages when the SiO2 content was greater than 26.7 mol %. Based on the previous 29Si MAS NMR experimental results, these findings further demonstrated that the formation of [SiO6] may significantly affect the formation of P=O linkages, and thus influences the spectroscopic properties of the glass. These results indicate that phosphosilicate glasses may have potential applications as a Yb3+-doped gain medium for solid-state lasers and optical fiber amplifiers. PMID:28772601

Mechanical properties and in vitro bioactivity of Ca5(PO4)2SiO4 bioceramic.

PubMed

Lu, Wenhao; Duan, Wei; Guo, Yaping; Ning, Congqin

2012-02-01

Pure Ca(5)(PO(4))(2)SiO(4) bioceramic was first prepared by a sol-gel method using triethyl phosphate, tetraethoxysilane, and calcium nitrate tetrahydrate as original materials. Simulated body fluid (SBF) immersion tests revealed that Ca(5)(PO(4))(2)SiO(4) samples had a greater in vitro apatite-forming ability than hydroxyapatite (HA). After soaking Ca(5)(PO(4))(2)SiO(4) samples in the SBF for 1 day, bone-like apatite precipitated on the surfaces and the apatite layer became thicker with increasing the soaking time. However, few bone-like apatites precipitated on the HA samples even after soaking in the SBF for 7 days. The good in vitro bioactivity of Ca(5)(PO(4))(2)SiO(4) samples was attributed to the silanol (Si-OH) groups and greater solubility of Ca(5)(PO(4))(2)SiO(4). In addition, hot-pressed Ca(5)(PO(4))(2)SiO(4) ceramic exhibited lower bending strength and elastic modulus than hot-pressed HA, since the former had a lower relative density than the latter. The results have shown that Ca(5)(PO(4))(2)SiO(4) is a potential candidate material for bone repair. © The Author(s), 2010.

Interaction of cesium adatoms with free-standing graphene and graphene-veiled SiO 2 surfaces

DOE Office of Scientific and Technical Information (OSTI.GOV)

Weck, Philippe F.; Kim, Eunja; Biedermann, Grant W.

2015-04-21

In this study, the interaction of Cs adatoms with mono- or bi-layered graphene (MLG and BLG), either free-standing or on a SiO 2 substrate, was investigated using density functional theory. The most stable adsorption sites for Cs are found to be hollow sites on both graphene sheets and graphene-veiled SiO 2(0001). In addition, larger dipole moments are created when a MLG-veiled SiO 2(0001) substrate is used for adsorption of Cs atoms compared to the adsorption on free-standing MLG, due to charge transfer occurring between the MLG and the SiO 2 substrate. For the adsorption of Cs on BLG-veiled SiO 2(0001)more » substrate, these differences are smoothed out and the binding energies corresponding to different sites are nearly degenerate; smaller dipole moments created by the Cs adatoms on BLG compared to MLG are also predicted.« less

Super-bright and short-lived photoluminescence of textured Zn2SiO4:Mn2+ phosphor film on quartz glass

NASA Astrophysics Data System (ADS)

Park, Jehong; Park, Kwangwon; Lee, Jaebum; Kim, Jongsu; Seo, Kwangil; Kwon, Kevin; Kung, Patrick; Kim, Seongsin M.

2010-02-01

Green-emissive textured Zn2SiO4:Mn2+ phosphor film was fabricated by a thermal diffusion of ZnO:Mn on quartz glass. The characterization has been performed in terms of Mn2+ ions concentration (Mn/Zn=1~9 mol %). As an increase of Mn2+ ions concentration in the Zn2SiO4:Mn2+ phosphor film, the emission peak was red shifted from 519 nm to 526 nm, and the decay time to 10% of the maximum intensity was shorter from 20 ms to 0.5 ms. All annealed Zn2SiO4:Mn2+ phosphor films became textured along some hexagonal directions on the amorphous quartz glass. The brightest Zn2SiO4:Mn2+ film at optimal Mn2+ concentration of 5 % showed the photoluminescence brightness of 65 % and the shortened decay time of 4.4 ms in comparison with a commercially Zn2SiO4: Mn2+ powder phosphor screen. The excellencies can be attributed to a unique textured structure.

In-situ synthesis of SiO2@MOF composites for high-efficiency removal of aniline from aqueous solution

NASA Astrophysics Data System (ADS)

Han, Tongtong; Li, Caifeng; Guo, Xiangyu; Huang, Hongliang; Liu, Dahuan; Zhong, Chongli

2016-12-01

A series of SiO2@aluminum-MOF(MIL-68) composites with different SiO2 loadings have been synthesized by a simple and mild compositing strategy for high-efficiency removal of aniline. As evidenced from SEM and TEM images as well as the particle size distribution, the incorporation of SiO2 can improve the dispersity of MIL-68(Al) in composites, and result in the smaller particle size than that of pristine MIL-68(Al). Besides, the adsorption of aniline over SiO2, MIL-68(Al), the physical mixture of these two materials, and SiO2@MIL-68(Al) composites was investigated comparatively, demonstrating a relatively high adsorption capacity (531.9 mg g-1) of 7% SiO2@MIL-68(Al) towards aniline. Combining the ultrafast adsorption dynamics (reaching equilibrium within 40 s) and great reusability, 7% SiO2@MIL-68(Al) shows excellent adsorption performance. This indicates that the SiO2@MIL-68(Al) composites possess great potential applications as a kind of fascinating adsorbent in water pollution protection.

Fabrication and Luminescence Characterization of a Silica Nanomatrix Embedded with NaYF4:Yb:Er:Tm@NaGdF4/Fe3O4 Nanoparticles

NASA Astrophysics Data System (ADS)

Thangaraju, Dheivasigamani; Santhana, Vedi; Matsuda, Satoshi; Hayakawa, Yasuhiro

2018-05-01

Hexagonal NaYF4:Yb:Er:Tm@NaGdF4 core-shell nanocrystals were synthesized using a seed mediated hot injection method, and monodispersed Fe3O4 (4 nm) nanoparticles were prepared from iron(II) actylacetonate by a precursor thermal decomposition method. Structural and morphology verified NaYF4:Yb:Er:Tm@NaGdF4 and Fe3O4 nanoparticles were utilized for the preparation of NaYF4:Yb:Er:Tm@NaGdF4/Fe3O4@SiO2 nanocomposite using a micro-emulsion method. Existence of Fe3O4 in NaYF4:Yb:Er:Tm@NaGdF4 in SiO2 nano-spheres were confirmed with transmission electron microscopy. Luminescence measurement revealed that NaYF4:Yb:Er:Tm@NaGdF4 exhibited strong emissions at green and red regions, in addition to a weak blue emission also observed under 980 nm excitation. Up-conversion emission of the nanoparticle-embedded silica nanocomposite showed that the up-conversion emission was not affected by Fe3O4 nanoparticles.

Heat capacity and entropy of Ni2SiO4-olivine from 5 to 1000 K and heat capacity of Co2SiO4 from 360 to 1000 K.

USGS Publications Warehouse

Robie, R.A.; Hemingway, B.S.; Ito, J.; Krupka, K.M.

1984-01-01

The heat capacity of Ni2SiO4-olivine has been measured between 5 and 387 K by cryogenic adiabatic-shield calorimetry and between 360 and 1000 K by differential scanning calorimetry. The heat capacity of Co2SiO4-olivine was measured between 360 and 1000 K by differential scanning calorimetry.-J.A.Z.

Comparison of Multilayer Dielectric Thin Films for Future Metal-Insulator-Metal Capacitors: Al2O3/HfO2/Al2O3 versus SiO2/HfO2/SiO2

NASA Astrophysics Data System (ADS)

Park, Sang-Uk; Kwon, Hyuk-Min; Han, In-Shik; Jung, Yi-Jung; Kwak, Ho-Young; Choi, Woon-Il; Ha, Man-Lyun; Lee, Ju-Il; Kang, Chang-Yong; Lee, Byoung-Hun; Jammy, Raj; Lee, Hi-Deok

2011-10-01

In this paper, two kinds of multilayered metal-insulator-metal (MIM) capacitors using Al2O3/HfO2/Al2O3 (AHA) and SiO2/HfO2/SiO2 (SHS) were fabricated and characterized for radio frequency (RF) and analog mixed signal (AMS) applications. The experimental results indicate that the AHA MIM capacitor (8.0 fF/µm2) is able to provide a higher capacitance density than the SHS MIM capacitor (5.1 fF/µm2), while maintaining a low leakage current of about 50 nA/cm2 at 1 V. The quadratic voltage coefficient of capacitance, α gradually decreases as a function of stress time under constant voltage stress (CVS). The parameter variation of SHS MIM capacitors is smaller than that of AHA MIM capacitors. The effects of CVS on voltage linearity and time-dependent dielectric breakdown (TDDB) characteristics were also investigated.

Stepwise mechanism and H2O-assisted hydrolysis in atomic layer deposition of SiO2 without a catalyst.

PubMed

Fang, Guo-Yong; Xu, Li-Na; Wang, Lai-Guo; Cao, Yan-Qiang; Wu, Di; Li, Ai-Dong

2015-01-01

Atomic layer deposition (ALD) is a powerful deposition technique for constructing uniform, conformal, and ultrathin films in microelectronics, photovoltaics, catalysis, energy storage, and conversion. The possible pathways for silicon dioxide (SiO2) ALD using silicon tetrachloride (SiCl4) and water (H2O) without a catalyst have been investigated by means of density functional theory calculations. The results show that the SiCl4 half-reaction is a rate-determining step of SiO2 ALD. It may proceed through a stepwise pathway, first forming a Si-O bond and then breaking Si-Cl/O-H bonds and forming a H-Cl bond. The H2O half-reaction may undergo hydrolysis and condensation processes, which are similar to conventional SiO2 chemical vapor deposition (CVD). In the H2O half-reaction, there are massive H2O molecules adsorbed on the surface, which can result in H2O-assisted hydrolysis of the Cl-terminated surface and accelerate the H2O half-reaction. These findings may be used to improve methods for the preparation of SiO2 ALD and H2O-based ALD of other oxides, such as Al2O3, TiO2, ZrO2, and HfO2.

Stepwise mechanism and H2O-assisted hydrolysis in atomic layer deposition of SiO2 without a catalyst

NASA Astrophysics Data System (ADS)

Fang, Guo-Yong; Xu, Li-Na; Wang, Lai-Guo; Cao, Yan-Qiang; Wu, Di; Li, Ai-Dong

2015-02-01

Atomic layer deposition (ALD) is a powerful deposition technique for constructing uniform, conformal, and ultrathin films in microelectronics, photovoltaics, catalysis, energy storage, and conversion. The possible pathways for silicon dioxide (SiO2) ALD using silicon tetrachloride (SiCl4) and water (H2O) without a catalyst have been investigated by means of density functional theory calculations. The results show that the SiCl4 half-reaction is a rate-determining step of SiO2 ALD. It may proceed through a stepwise pathway, first forming a Si-O bond and then breaking Si-Cl/O-H bonds and forming a H-Cl bond. The H2O half-reaction may undergo hydrolysis and condensation processes, which are similar to conventional SiO2 chemical vapor deposition (CVD). In the H2O half-reaction, there are massive H2O molecules adsorbed on the surface, which can result in H2O-assisted hydrolysis of the Cl-terminated surface and accelerate the H2O half-reaction. These findings may be used to improve methods for the preparation of SiO2 ALD and H2O-based ALD of other oxides, such as Al2O3, TiO2, ZrO2, and HfO2.

Role of bulk and Nanosized SiO2 to overcome salt stress during Fenugreek germination (Trigonella foenum- graceum L.).

PubMed

Ivani, Reihane; Sanaei Nejad, Seyed Hossein; Ghahraman, Bijan; Astaraei, Ali Reza; Feizi, Hassan

2018-04-05

The effects of bulk and Nanosized SiO 2 on seed germination and seedling growth indices of fenugreek under salinity stress were studied in the College of Agriculture, Ferdowsi University of Mashhad, Iran, in 2013. The experimental treatments included 4 levels of salinity stress (0, 50, 100 and 150 mM), 2 concentrations of bulk (50 and 100 ppm), 2 concentrations of nanosized SiO 2 (50 and 100 ppm), and control (without any SiO 2 types). Seedling growth attributes significantly improved when bulk and nanosized SiO 2 concentrations applied singly or with different levels of salt stress. However, they significantly declined with salt application. The adverse effects of salt on shoot, root and seedling lengths were alleviated by application of 50 ppm nanosized SiO 2 treatment. Under salt stress condition, addition of 50 and 100 ppm nanosized SiO 2 to fenugreek seeds increased shoot, root and seedling dry weights as compared to bulk SiO 2 concentrations and control treatments, though 50 ppm nanosized SiO 2 was more effective than 100 ppm nanosized SiO 2 application. It was concluded that nanosized SiO 2 improves growth attributes of fenugreek and mitigate adverse effects of salt stress.

Space electric field concentrated effect for Zr:SiO2 RRAM devices using porous SiO2 buffer layer

PubMed Central

2013-01-01

To improve the operation current lowing of the Zr:SiO2 RRAM devices, a space electric field concentrated effect established by the porous SiO2 buffer layer was investigated and found in this study. The resistive switching properties of the low-resistance state (LRS) and high-resistance state (HRS) in resistive random access memory (RRAM) devices for the single-layer Zr:SiO2 and bilayer Zr:SiO2/porous SiO2 thin films were analyzed and discussed. In addition, the original space charge limited current (SCLC) conduction mechanism in LRS and HRS of the RRAM devices using bilayer Zr:SiO2/porous SiO2 thin films was found. Finally, a space electric field concentrated effect in the bilayer Zr:SiO2/porous SiO2 RRAM devices was also explained and verified by the COMSOL Multiphysics simulation model. PMID:24330524

Quenching from highly-excited SiO rotational levels due to H2 collision

NASA Astrophysics Data System (ADS)

Stancil, Phillip C.; Belayneh, Michael; Wan, Yier; Yang, Benhui H.

2018-06-01

Using a full quantum-mechanical close-coupling approach on a 4D rigid-rotor potential energy surface (PES), we performed scattering calculations for highly-excited rotational levels (j=6-10) of SiO for interactions with H2 for the first time. Emission lines from highly excited SiO rotational levels are observed in a variety of environments including outflows from AGB stars. However, explicit collisional data are lacking for H2 colliders, except for recent work from our group for j=1-5. Here we extend that work using a hybrid OpenMP/MPI scattering code and a PES computed at the CCSD(T)-F12b level of theory. The H2 and SiO bond lengths are fixed at their equilibrium values. The current results will allow for non-local thermodynamic models of SiO rotational emission from AGB stars. This work was funded by NASA grant NNX16AF09G.

Highly Enhanced H2 Sensing Performance of Few-Layer MoS2/SiO2/Si Heterojunctions by Surface Decoration of Pd Nanoparticles.

PubMed

Hao, Lanzhong; Liu, Yunjie; Du, Yongjun; Chen, Zhaoyang; Han, Zhide; Xu, Zhijie; Zhu, Jun

2017-10-17

A novel few-layer MoS 2 /SiO 2 /Si heterojunction is fabricated via DC magnetron sputtering technique, and Pd nanoparticles are further synthesized on the device surface. The results demonstrate that the fabricated sensor exhibits highly enhanced responses to H 2 at room temperature due to the decoration of Pd nanoparticles. For example, the Pd-decorated MoS 2 /SiO 2 /Si heterojunction shows an excellent response of 9.2 × 10 3 % to H 2 , which is much higher than the values for the Pd/SiO 2 /Si and MoS 2 /SiO 2 /Si heterojunctions. In addition, the H 2 sensing properties of the fabricated heterojunction are dependent largely on the thickness of the Pd-nanoparticle layer and there is an optimized Pd thickness for the device to achieve the best sensing characteristics. Based on the microstructure characterization and electrical measurements, the sensing mechanisms of the Pd-decorated MoS 2 /SiO 2 /Si heterojunction are proposed. These results indicate that the Pd decoration of few-layer MoS 2 /SiO 2 /Si heterojunctions presents an effective strategy for the scalable fabrication of high-performance H 2 sensors.

Improved performance of Bis-GMA/TEGDMA dental composites by net-like structures formed from SiO2 nanofiber fillers.

PubMed

Wang, Xiaoyan; Cai, Qing; Zhang, Xuehui; Wei, Yan; Xu, Mingming; Yang, Xiaoping; Ma, Qi; Cheng, Yali; Deng, Xuliang

2016-02-01

The major objective of this study was to explore the effects of silicon dioxide (SiO2) nanofibers on the performance of 2, 2-bis-[4-(methacryloxypropoxy)-phenyl]-propane (Bis-GMA)/tri-(ethyleneglycol) dimethacrylate (TEGDMA) dental composites. At first, the mechanical properties of Bis-GMA/TEGDMA (50/50, w/w) resins containing different contents of SiO2 nanofibers were evaluated to identify the appropriate composition to achieve the significant reinforcing effect. Secondly, optimized contents (5 or 10wt.%) of SiO2 nanofibers were mixed into resins together with SiO2 microparticles, which was 60wt.% of the resin. Controls for comparison were Bis-GMA/TEGDMA resins containing only SiO2 microparticles (60wt.%) or with additional SiO2 nanoparticles (5 or 10wt.%). Properties including abrasion, polymerization shrinkage and mechanical properties were evaluated to determine the contribution of SiO2 nanofibers. In comparison with SiO2 nanoparticles, SiO2 nanofibers improved the overall performance of Bis-GMA/TEGDMA composite resins, especially in improving abrasion resistance and decreasing polymerization shrinkage. The explanations were that one-dimensional SiO2 nanofibers were able to shield particular fillers from being abraded off, and able to form a kind of overlapped fibrous network to resist polymerization shrinkage. With these approaches, SiO2 nanofiber-containing Bis-GMA composite resins were envisioned a promising choice to achieve long-term durable restorations in clinical therapies. Copyright © 2015. Published by Elsevier B.V.

UV Light-Driven Photodegradation of Methylene Blue by Using Mn0.5Zn0.5Fe2O4/SiO2 Nanocomposites

NASA Astrophysics Data System (ADS)

Indrayana, I. P. T.; Julian, T.; Suharyadi, E.

2018-04-01

The photodegradation activity of nanocomposites for 20 ppm methylene blue solution has been investigated in this work. Nanocomposites Mn0.5Zn0.5Fe2O4/SiO2 have been synthesized using coprecipitation method. The X-ray diffraction (XRD) pattern confirmed the formation of three phases in sample Mn0.5Zn0.5Fe2O4/SiO2 i.e., Mn0.5Zn0.5Fe2O4, Zn(OH)2, and SiO2. The appearance of SiO2 phase showed that the encapsulation process has been carried out. The calculated particles size of Mn0.5Zn0.5Fe2O4/SiO2 is greater than Mn0.5Zn0.5Fe2O4. Bonding analysis via vibrational spectra for Mn0.5Zn0.5Fe2O4/SiO2 confirmed the formation of bonds Me-O-Si stretching (2854.65 cm-1) and Si-O-Si asymmetric stretching (1026.13 cm-1). The optical gap energy of Mn0.5Zn0.5Fe2O4/SiO2 was smaller (2.70 eV) than Mn0.5Zn0.5Fe2O4 (3.04 eV) due to smaller lattice dislocation and microstrain that affect their electronic structure. The Mn0.5Zn0.5Fe2O4/SiO2 showed high photodegradation ability due to smaller optical gap energy and the appearance of SiO2 ligand that can easily attract dye molecules. The Mn0.5Zn0.5Fe2O4/SiO2 also showed high degradation activity even without UV light radiation. The result showed that photodegradation reaction doesn’t follow pseudo-first order kinetics.

First-principles study on leakage current caused by oxygen vacancies at HfO2/SiO2/Si interface

NASA Astrophysics Data System (ADS)

Takagi, Kensuke; Ono, Tomoya

2018-06-01

The relationship between the position of oxygen vacancies in HfO2/SiO2/Si gate stacks and the leakage current is studied by first-principles electronic-structure and electron-conduction calculations. We find that the increase in the leakage current due to the creation of oxygen vacancies in the HfO2 layer is much larger than that in the SiO2 interlayer. According to previous first-principles total energy calculations, the formation energy of oxygen vacancies is smaller in the SiO2 interlayer than that in the HfO2 layer under the same conditions. Therefore, oxygen vacancies will be attracted from the SiO2 interlayer to minimize the energy, thermodynamically justifying the scavenging technique. Thus, the scavenging process efficiently improves the dielectric constant of HfO2-based gate stacks without increasing the number of oxygen vacancies, which cause the dielectric breakdown.

Bulk properties and near-critical behaviour of SiO2 fluid

NASA Astrophysics Data System (ADS)

Green, Eleanor C. R.; Artacho, Emilio; Connolly, James A. D.

2018-06-01

Rocky planets and satellites form through impact and accretion processes that often involve silicate fluids at extreme temperatures. First-principles molecular dynamics (FPMD) simulations have been used to investigate the bulk thermodynamic properties of SiO2 fluid at high temperatures (4000-6000 K) and low densities (500-2240 kg m-3), conditions which are relevant to protoplanetary disc condensation. Liquid SiO2 is highly networked at the upper end of this density range, but depolymerises with increasing temperature and volume, in a process characterised by the formation of oxygen-oxygen (Odbnd O) pairs. The onset of vaporisation is closely associated with the depolymerisation process, and is likely to be non-stoichiometric at high temperature, initiated via the exsolution of O2 molecules to leave a Si-enriched fluid. By 6000 K the simulated fluid is supercritical. A large anomaly in the constant-volume heat capacity occurs near the critical temperature. We present tabulated thermodynamic properties for silica fluid that reconcile observations from FPMD simulations with current knowledge of the SiO2 melting curve and experimental Hugoniot curves.

Proton trapping in SiO 2 layers thermally grown on Si and SiC

NASA Astrophysics Data System (ADS)

Afanas'ev, V. V.; Ciobanu, F.; Pensl, G.; Stesmans, A.

2002-11-01

Positive charging of thermal SiO 2 layers on (1 0 0)Si and (0 0 0 1)6H-, 4H-SiC related to trapping of protons is studied using low-energy proton implantation into the oxide, and compared to the trapping of holes generated by 10-eV photons. Proton trapping has an initial probability close to 100% and shows little sensitivity to the annealing-induced oxygen deficiency of SiO 2. In contrast to protons, hole trapping in as-grown SiO 2 shows a much lower efficiency which increases upon oxide annealing, in qualitative correlation with the higher density of O 3Si• defects (E' centers) detected by electron spin resonance after hole injection. Despite these differences, the neutralization of positive charges induced by holes and protons has the same cross-section, and in both cases is accompanied by liberation of atomic H suggesting that protons account for positive charge in both cases. The rupture of Si-O bonds in the oxide observed upon proton injection suggests, as a first basic step, the bonding of a proton to a bridging oxygen atom in SiO 2 network.

Improved electrochemical and thermal properties of nickel rich LiNi0.6Co0.2Mn0.2O2 cathode materials by SiO2 coating

NASA Astrophysics Data System (ADS)

Cho, Woosuk; Kim, Sang-Min; Song, Jun Ho; Yim, Taeeun; Woo, Sang-Gil; Lee, Ko-Woon; Kim, Jeom-Soo; Kim, Young-Jun

2015-05-01

A surface coating of SiO2 is applied to a Ni rich LiNi0.6Co0.2Mn0.2O2 cathode material in a bid to improve its electrochemical and thermal properties. A uniform coating is achieved through a wet process using nano-sized SiO2 powder, and though the coated electrode is found to exhibit a reduced rate capability, its cycle performance at a high temperature of 60 °C is greatly enhanced. The effect of this SiO2 coating is further investigated by electrochemical impedance spectroscopy, which confirms that it suppresses the growth of interfacial impedance during progressive cycles. The SiO2 coating also demonstrates good HF scavenging ability, producing a subsequent reduction in the degradation of the active core material. The thermal properties of LiNi0.6Co0.2Mn0.2O2 are also improved by the SiO2 coating due to a reduction in the direct contact between the electrode and electrolyte. On the basis of these results, SiO2 coating is considered a viable surface modification method for improving the electrochemical and thermal properties of LiNi0.6Co0.2Mn0.2O2.

Sixfold-coordinated amorphous polymorph of SiO2 under high pressure.

PubMed

Sato, Tomoko; Funamori, Nobumasa

2008-12-19

We have developed synchrotron x-ray absorption and diffraction techniques for measuring the density and structure of noncrystalline materials at high pressures and have applied them to studying the behavior of SiO2 glass. The density, coordination number, and Si-O bond length at a pressure of 50 GPa were measured to be 4.63 g/cm;{3}, 6.3, and 1.71 A, respectively. Based on the density data measured in this study and the sound velocity data available in the literature, the bulk modulus at 50 GPa was estimated to be 390 GPa, which is consistent with the pressure dependence of the density in the vicinity of 50 GPa. These results, together with the knowledge from our exploratory study, suggest that SiO2 glass behaves as a single amorphous polymorph having a sixfold-coordinated structure at pressures above 40-45 GPa up to at least 100 GPa.

Efficient VEGF targeting delivery of DOX using Bevacizumab conjugated SiO2@LDH for anti-neuroblastoma therapy.

PubMed

Zhu, Rongrong; Wang, Zhaoqi; Liang, Peng; He, Xiaolie; Zhuang, Xizhen; Huang, Ruiqi; Wang, Mei; Wang, Qigang; Qian, Yechang; Wang, Shilong

2017-11-01

Vascular endothelial growth factor (VEGF) plays an important role in angiogenesis and is highly expressed in carcinoma, which make it an important target for tumor targeting therapy. Neuroblastoma is the main cause for cancer-related death in children. Like most solid tumors, it is also accompanied with the overexpression of VEGF. Doxorubicin Hydrochloride (DOX), a typical chemotherapeutic agent, exhibits efficient anticancer activities for various cancers. However, DOX, without targeting ability, usually causes severe damage to normal tissues. To overcome the shortages, we designed a novel nano-composite, which is Bevacizumab (Bev) modified SiO 2 @LDH nanoparticles (SiO 2 @LDH-Bev), loading with DOX to achieve targeting ability and curative efficiency. SiO 2 @LDH-DOX and SiO 2 @LDH-Bev-DOX nanoparticles were synthesized and the physicochemical properties were characterized by TEM detection, Zeta potential analysis, FTIR, Raman and XPS analysis. Then in vitro and in vivo anti-neuroblastoma efficiency, targeting ability and mechanisms of anti-carcinoma and anti-angiogenesis of SiO 2 @LDH-Bev-DOX were explored. Our results indicated that we obtained the core-shell structure SiO 2 @LDH-Bev with an average diameter of 253±10nm and the amount of conjugated Bev was 4.59±0.38μg/mg SiO 2 @LDH-Bev. SiO 2 @LDH-Bev-DOX could improve the cellular uptake and the targeting effect of DOX to brain and tumor, enhance the anti-neuroblastoma and anti-angiogenesis efficiency both in vitro and in vivo, and alleviate side effects of DOX sharply, especially hepatic injury. In addition, we also demonstrated that angiogenesis inhibitory effect was mediated by DOX and VEGF triggered signal pathways, including PI3K/Akt, Raf/MEK/ERK, and adhesion related pathways. In summary, SiO 2 @LDH-Bev could be a potential VEGF targeting nanocarrier applied in VEGF positive cancer therapy. This paper explored that a novel core-shell structure nanomaterial SiO 2 @LDH and modified SiO 2 @LDH with

First principle study of electronic structures and optical properties of Ce-doped SiO2

NASA Astrophysics Data System (ADS)

Cong, Wei-Yan; Lu, Ying-Bo; Zhang, Peng; Guan, Cheng-Bo

2018-05-01

Electronic structures and optical properties of Silicon dioxide (SiO2) systems with and without cerium(Ce) dopant were calculated using the density functional theory. We find that after the Ce incorporation, a new localized impurity band appears between the valance band maximum (VBM) and the conduction band minimum (CBM) of SiO2 system, which is induced mainly by the Ce-4f orbitals. The localized impurity band constructs a bridge between the valence band and the conduction band, making the electronic transition much easier. The calculated optical properties show that in contrast from the pure SiO2 sample, absorption in the visible-light region is found in Ce-doped SiO2 system, which originates from the transition between the valence band and Ce-4f dominated impurity band, as well as the electronic transition from Ce-4f states to Ce-5d states. All calculated results indicate that Ce doping is an effective strategy to improve the optical performance of SiO2 sample, which is in agreement with the experimental results.

Organic-Free, ZnO-Assisted Synthesis of Zeolite FAU with Tunable SiO2 /Al2 O3 Molar Ratio.

PubMed

Guo, Ya; Sun, Tianjun; Gu, Yiming; Liu, Xiaowei; Ke, Quanli; Wang, Shudong

2018-05-04

Zeolite FAU with tunable SiO 2 /Al 2 O 3 molar ratio has been successfully synthesized in the absence of organic structure-directing agents (OSDA). Specifically, the addition of zinc species contributes to the feasible and effective adjustment of the framework SiO 2 /Al 2 O 3 molar ratio between about 4 and 6 depending on the amount of zinc species added in the batch composition. In contrast, a typical OSDA such as tetramethylammonium hydroxide (TMAOH) has a limited effect on the SiO 2 /Al 2 O 3 molar ratio of the zeolite. The role of zinc species is essential for the crystallization of zeolite FAU with a higher SiO 2 /Al 2 O 3 molar ratio under the particular synthesis conditions. It is speculated that zinc species may suppress the incorporation of aluminum into the aluminosilicate framework, which is due to the Coulombic repulsive interaction. A higher SiO 2 /Al 2 O 3 molar ratio is also found to be accompanied by a lower CO 2 adsorption heat for CO 2 /CH 4 separation. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

SiO2-Ag-SiO2 core/shell structure with a high density of Ag nanoparticles for CO oxidation catalysis.

PubMed

Feng, Xiaoqian; Li, Hongmo; Zhang, Qing; Zhang, Peng; Song, Xuefeng; Liu, Jing; Zhao, Liping; Gao, Lian

2016-11-11

SiO 2 -Ag-SiO 2 , a sandwiched core/shell structure with a layer of Ag nanoparticles (∼4 nm) encapsulated between a shallow SiO 2 surface layer and a SiO 2 submicrosphere substrate (∼200 nm), has been synthesized from [Formula: see text] and SiO 2 spheres by a facile one-pot hydrothermal method. The composite is proposed to result from the dynamic balance between the [Formula: see text] reduction and the dissolution-redeposition of SiO 2 in mild basic media. The synthetic mechanism and the roles of the reaction time, temperature, and the amount of ammonia in the formation of this unique structure are investigated and discussed. The composite structure shows superior catalytic performance in CO oxidation to the control Ag/SiO 2 structure prepared by impregnation. Pre-treatment by O 2 at 600 °C significantly improves the catalytic performance of the composite structure and preserves the nanocomposite structure well.

Simple sonochemical synthesis of Ho2O3-SiO2 nanocomposites as an effective photocatalyst for degradation and removal of organic contaminant.

PubMed

Zinatloo-Ajabshir, Sahar; Mortazavi-Derazkola, Sobhan; Salavati-Niasari, Masoud

2017-11-01

In this work, highly photocatalytically active Ho 2 O 3 -SiO 2 nanocomposites have been designed and applied for decomposition of methylene blue pollutant. Ho 2 O 3 -SiO 2 nanocomposites have been produced by new, quick and facile sonochemical process with the aid of tetramethylethylenediamine as a novel basic agent for the first time. The effect of the kind of basic agent, ultrasonic time and dosage of Ho source on the grain size, photocatalytic behavior and shape of the Ho 2 O 3 -SiO 2 nanocomposites have been evaluated for optimization the production condition. FESEM, EDX, FT-IR, DRS, XRD and TEM have been applied to characterize the as-produced Ho 2 O 3 -SiO 2 nanocomposites. Use of the as-produced Ho 2 O 3 -SiO 2 nanocomposites as photocatalyst via destruction of methylene blue pollutant under UV illumination has been compared. It was observed that SiO 2 has notable impact on catalytic activity of holmium oxide photocatalyst for destruction. Introducing of SiO 2 to holmium oxide can enhance destruction efficiency of holmium oxide to methylene blue pollutant under ultraviolet light. Copyright © 2017 Elsevier B.V. All rights reserved.

Natural Occurrence of Fe2SiO4 - in Shocked Umbarger l6 Chondrite

NASA Astrophysics Data System (ADS)

Xie, Z.; Sharp, T. G.

2001-12-01

Fe2SiO4 with the spinel structure was synthesized by Ringwood [1] and inferred to be important in Earth's upper mantle [1,2], but it has not previously been found in nature. Umbarger is an L6 chondrite, which contains a series of high-pressure phases: ring-woodite, akimotoite, augite and hollandite-structured plagioclase [3-6]. Transmission electron microscopy also revealed a Fe2SiO4-spinel and stishovite assem-blage in a Fe-rich zone of a melt pocket. Phyllosili-cates and glass are also associated with the Fe2SiO4-spinel, indicating post-shock aqueous glass alteration. The Fe2SiO4-spinel grains are equant to irregular, with sizes from 100 to 400 nm. Diffraction patterns can only be indexed as a spinel structure, but the unit cell is a little large (a= 8.46 Å) relative to synthetic Fe2SiO4-spinel (a=8.234 Å [1]). EDS analyses show that the spinel has a fayalite compositon with Fe/(Fe+Mg) ratio ranging from 62% to 97%. Stishovite occurs as elongated prismatic crystals up to 1 mm long and up to 100 mm wide. The alteration products in Umbarger are phyllosilicates rich in Fe and Si, with a basal layer spacing of about 9.7 Å. Crystallization of melt veins began with akimotoite and ringwoodite at pressures up to 25 GPa and ended with augite at pressure less than 18 GPa [3, 4]. Mg2SiO4-spinel and stishovite are stable in the pres-sure range from 15 GPa to 25 GPa in the enstatite-forsterite system [7], while Fe2SiO4-spinel and stishovite is stable at lower pressure. Fe2SiO4-spinel and stishovite assemblage, like that of Akimotoite plus ringwoodite, is a sub-solidus assemblage, indicating crystallization of a supercooled liquid during rapid cooling and decompression associated with shock pres-sure release. Reference: [1] Ringwood A.E. (1958) GCA,15, 18-29. [2] Irifune T. (1993) The Island Arc, 2, 55-71. [3] Xie Z. and Sharp T. G. (2000a) LPS XXXI, 2065.pdf. [4] Xie Z. and Sharp T. G. (2000b) MAPS, 35 A172. [5] Xie Z. et al.(2001) LPS XXXII, 1805.pdf. [6] Sharp T.G. (2001

Preparation and photocatalytic properties of nanometer-sized magnetic TiO2/SiO2/CoFe2O4 composites.

PubMed

Li, Hansheng; Zhang, Yaping; Wu, Qin; Wang, Xitao; Liu, Changhao

2011-11-01

Magnetic TiO2/SiO2/CoFe2O4 nanoparticles (TiO2/SCFs) were prepared by a sol-gel process in a reverse microemulsion combined with solvent-thermal technique. TiO2/SCFs were characterized by Fourier transform infrared spectrometry, thermogravimetric analysis-differential scanning calorimetry, X-ray diffraction, Raman spectrometry, TEM, BET specific surface area measurement, and magnetic analysis. Structure analyses indicated that TiO2/SCFs presented a core-shell structure with TiO2 uniformly coating on SiO2/CoFe2O4 nanomagnets (SCFs) and typical ferromagnetic hysteresis. TiO2/SCFs showed larger specific surface area and better photocatalytic activities than TiO2 and TiO2/CoFe2O4 photocatalysts prepared by the same method. The doping interaction between TiO2 and CoFe2O4 reduced thanks to the inert SiO2 mesosphere.

The improvement of SiO2 nanotubes electrochemical behavior by hydrogen atmosphere thermal treatment

NASA Astrophysics Data System (ADS)

Spataru, Nicolae; Anastasescu, Crina; Radu, Mihai Marian; Balint, Ioan; Negrila, Catalin; Spataru, Tanta; Fujishima, Akira

2018-06-01

Highly defected SiO2 nanotubes (SiO2-NT) were obtained by a simple sol-gel procedure followed by calcination. Boron-doped diamond (BDD) polycrystalline films coated with SiO2-NT were used as working electrodes and, unexpectedly, cyclic voltammetric experiments have shown that the concentration of both positive and negative defects at the surface is high enough to enable redox processes involving positively charged Ru(bpy)32+/3+ to occur. Conversely, no electrochemical activity was put into evidence for Fe(CN)63-/4- species, most likely as a result of the strong electrostatic repulsion exerted by the negatively charged SiO2 surface. The concentration of surface defects was further increased by a subsequent thermal treatment in a hydrogen atmosphere which, as EIS measurements have shown, significantly promotes Ru(bpy)32+ anodic oxidation. Digital simulation of the voltammetric responses demonstrated that this treatment does not lead to a similar increase of the number of electron-donor sites. It was also found that methanol anodic oxidation at hydrogenated SiO2-NT-supported platinum results in Tafel slopes of 116-220 mV decade-1, comparable to those reported for both conventional PtRu and Pt-oxide catalysts.

Thickness and composition of ultrathin SiO2 layers on Si

NASA Astrophysics Data System (ADS)

van der Marel, C.; Verheijen, M. A.; Tamminga, Y.; Pijnenburg, R. H. W.; Tombros, N.; Cubaynes, F.

2004-07-01

Ultrathin SiO2 layers are of importance for the semiconductor industry. One of the techniques that can be used to determine the chemical composition and thickness of this type of layers is x-ray photoelectron spectroscopy (XPS). As shown by Seah and Spencer [Surf. Interface Anal. 33, 640 (2002)], it is not trivial to characterize this type of layer by means of XPS in a reliable way. We have investigated a series of ultrathin layers of SiO2 on Si (in the range from 0.3 to 3 nm) using XPS. The samples were also analyzed by means of transmission electron microscopy (TEM), Rutherford backscattering (RBS), and ellipsometry. The thickness of the SiO2 layers (d) was determined from the XPS results using three different approaches: the ``standard'' equation (Seah and Spencer) for d, an overlayer-substrate model calculation, and the QUASES-Tougaard [Surf. Interface Anal. 26, 249 (1998), QUASES-Tougaard: Software package for Quantitative Analysis of Surfaces by Electron Spectroscopy, version 4.4 (2000); http://www.quases.com] method. Good agreement was obtained between the results of XPS analyses using the ``standard'' equation, the overlayer-substrate model calculation, and RBS results. The QUASES-Tougaard results were approximately 62% above the other XPS results. The optical values for the thickness were always slightly higher than the thickness according to XPS or RBS. Using the model calculation, these (relatively small) deviations from the optical results could be explained as being a consequence of surface contaminations with hydrocarbons. For a thickness above 2.5 nm, the TEM results were in good agreement with the results obtained from the other techniques (apart from QUASES-Tougaard). Below 2.5 nm, significant deviations were found between RBS, XPS, and optical data on the one hand and TEM results on the other hand; the deviations became larger as the thickness of the SiO2 decreased. This effect may be related to interface states of oxygen, which have been

An Investigation on the Tribological Performances of the SiO2/MoS2 Hybrid Nanofluids for Magnesium Alloy-Steel Contacts

NASA Astrophysics Data System (ADS)

Xie, Hongmei; Jiang, Bin; Liu, Bo; Wang, Qinghang; Xu, Junyao; Pan, Fusheng

2016-07-01

Hybrid nano-materials offer potential scope for an increasing numerous novel applications when engineered to deliver availably functional properties. In the present study, the SiO2/MoS2 hybrid nanoparticles with different mass ratios were employed as lubricant additives in the base oil, and their tribological properties were evaluated using a reciprocating ball-on-plate tribometer for magnesium alloy-steel contacts. The results demonstrate that the SiO2/MoS2 hybrid nanoparticles exhibit superior lubrication performances than individual nano-SiO2 or nano-MoS2 even in high load and diverse velocity cases. The optimal SiO2/MoS2 mixing ratio and the concentration of SiO2/MoS2 hybrid nanoparticles in the base oil are 0.25:0.75 and 1.00-1.25 wt%, respectively. The excellent lubrication properties of the SiO2/MoS2 hybrid nanoparticles are attributed to the physical synergistic lubricating actions of nano-SiO2 and nano-MoS2 during the rubbing process.

An Investigation on the Tribological Performances of the SiO2/MoS2 Hybrid Nanofluids for Magnesium Alloy-Steel Contacts.

PubMed

Xie, Hongmei; Jiang, Bin; Liu, Bo; Wang, Qinghang; Xu, Junyao; Pan, Fusheng

2016-12-01

Hybrid nano-materials offer potential scope for an increasing numerous novel applications when engineered to deliver availably functional properties. In the present study, the SiO2/MoS2 hybrid nanoparticles with different mass ratios were employed as lubricant additives in the base oil, and their tribological properties were evaluated using a reciprocating ball-on-plate tribometer for magnesium alloy-steel contacts. The results demonstrate that the SiO2/MoS2 hybrid nanoparticles exhibit superior lubrication performances than individual nano-SiO2 or nano-MoS2 even in high load and diverse velocity cases. The optimal SiO2/MoS2 mixing ratio and the concentration of SiO2/MoS2 hybrid nanoparticles in the base oil are 0.25:0.75 and 1.00-1.25 wt%, respectively. The excellent lubrication properties of the SiO2/MoS2 hybrid nanoparticles are attributed to the physical synergistic lubricating actions of nano-SiO2 and nano-MoS2 during the rubbing process.

Analysis of thermal stresses in HfO2/SiO2 high reflective optical coatings for high power laser applications

NASA Astrophysics Data System (ADS)

Gao, Chunxue; Zhao, Zhiwei; Zhu, Zhuoya; Li, Shuang; Mi, Changwen

2015-02-01

HfO2/SiO2 high reflective optical coatings are widely used in high power laser applications because of their high laser damage resistance and appropriate spectral performance. The residual stresses strongly influence the performance and longevity of the optical coatings. Thermal stresses are the primary components of the residual stresses. In the present work, the distribution of thermal stresses in HfO2/SiO2 high reflective optical coatings was investigated using two different computational methods: finite element method (FEM) and an analytical method based on force and moment balances and classical beam bending theory. The results by these two methods were compared and found to be in agreement with each other, demonstrating that these two methods are effective and accurate ways to predict the thermal stresses in HfO2/SiO2 optical coatings. In addition, these two methods were also used to obtain the thermal stresses in HfO2/SiO2 optical coatings with different layer number to investigate the effect of the layer number on the thermal stresses of the HfO2/SiO2 optical coatings. The results show that with the increase of the layer number, the stresses in the substrate increase, while the stresses in the respective SiO2 and HfO2 layers decrease. Besides, it was also found that the radius of curvature of the coating system decreases as the layer number increases, leading to larger bending curvature in the system.

Design and Synthesis of Hierarchical SiO2@C/TiO2 Hollow Spheres for High-Performance Supercapacitors.

PubMed

Zhang, Ying; Zhao, Yan; Cao, Shunsheng; Yin, Zhengliang; Cheng, Li; Wu, Limin

2017-09-06

TiO 2 has been widely investigated as an electrode material because of its long cycle life and good durability, but the relatively low theoretical capacity restricts its practical application. Herein, we design and synthesize novel hierarchical SiO 2 @C/TiO 2 (HSCT) hollow spheres via a template-directed method. These unique HSCT hollow spheres combine advantages from both TiO 2 such as cycle stability and SiO 2 with a high accessible area and ionic transport. In particular, the existence of a C layer is able to enhance the electrical conductivity. The SiO 2 layer with a porous structure can increase the ion diffusion channels and accelerate the ion transfer from the outer to the inner layers. The electrochemical measurements demonstrate that the HSCT-hollow-sphere-based electrode manifests a high specific capacitance of 1018 F g -1 at 1 A g -1 which is higher than those for hollow TiO 2 (113 F g -1 ) and SiO 2 /TiO 2 (252 F g -1 ) electrodes, and substantially higher than those of all the previously reported TiO 2 -based electrodes.

Novel nanofluidic chemical cells based on self-assembled solid-state SiO2 nanotubes.

PubMed

Zhu, Hao; Li, Haitao; Robertson, Joseph W F; Balijepalli, Arvind; Krylyuk, Sergiy; Davydov, Albert V; Kasianowicz, John J; Suehle, John S; Li, Qiliang

2017-10-27

Novel nanofluidic chemical cells based on self-assembled solid-state SiO 2 nanotubes on silicon-on-insulator (SOI) substrate have been successfully fabricated and characterized. The vertical SiO 2 nanotubes with a smooth cavity are built from Si nanowires which were epitaxially grown on the SOI substrate. The nanotubes have rigid, dry-oxidized SiO 2 walls with precisely controlled nanotube inner diameter, which is very attractive for chemical-/bio-sensing applications. No dispersion/aligning procedures were involved in the nanotube fabrication and integration by using this technology, enabling a clean and smooth chemical cell. Such a robust and well-controlled nanotube is an excellent case of developing functional nanomaterials by leveraging the strength of top-down lithography and the unique advantage of bottom-up growth. These solid, smooth, clean SiO 2 nanotubes and nanofluidic devices are very encouraging and attractive in future bio-medical applications, such as single molecule sensing and DNA sequencing.

Novel nanofluidic chemical cells based on self-assembled solid-state SiO2 nanotubes

NASA Astrophysics Data System (ADS)

Zhu, Hao; Li, Haitao; Robertson, Joseph W. F.; Balijepalli, Arvind; Krylyuk, Sergiy; Davydov, Albert V.; Kasianowicz, John J.; Suehle, John S.; Li, Qiliang

2017-10-01

Novel nanofluidic chemical cells based on self-assembled solid-state SiO2 nanotubes on silicon-on-insulator (SOI) substrate have been successfully fabricated and characterized. The vertical SiO2 nanotubes with a smooth cavity are built from Si nanowires which were epitaxially grown on the SOI substrate. The nanotubes have rigid, dry-oxidized SiO2 walls with precisely controlled nanotube inner diameter, which is very attractive for chemical-/bio-sensing applications. No dispersion/aligning procedures were involved in the nanotube fabrication and integration by using this technology, enabling a clean and smooth chemical cell. Such a robust and well-controlled nanotube is an excellent case of developing functional nanomaterials by leveraging the strength of top-down lithography and the unique advantage of bottom-up growth. These solid, smooth, clean SiO2 nanotubes and nanofluidic devices are very encouraging and attractive in future bio-medical applications, such as single molecule sensing and DNA sequencing.

Effect of source frequency and pulsing on the SiO2 etching characteristics of dual-frequency capacitive coupled plasma

NASA Astrophysics Data System (ADS)

Kim, Hoe Jun; Jeon, Min Hwan; Mishra, Anurag Kumar; Kim, In Jun; Sin, Tae Ho; Yeom, Geun Young

2015-01-01

A SiO2 layer masked with an amorphous carbon layer (ACL) has been etched in an Ar/C4F8 gas mixture with dual frequency capacitively coupled plasmas under variable frequency (13.56-60 MHz)/pulsed rf source power and 2 MHz continuous wave (CW) rf bias power, the effects of the frequency and pulsing of the source rf power on the SiO2 etch characteristics were investigated. By pulsing the rf power, an increased SiO2 etch selectivity was observed with decreasing SiO2 etch rate. However, when the rf power frequency was increased, not only a higher SiO2 etch rate but also higher SiO2 etch selectivity was observed for both CW and pulse modes. A higher CF2/F ratio and lower electron temperature were observed for both a higher source frequency mode and a pulsed plasma mode. Therefore, when the C 1s binding states of the etched SiO2 surfaces were investigated using X-ray photoelectron spectroscopy (XPS), the increase of C-Fx bonding on the SiO2 surface was observed for a higher source frequency operation similar to a pulsed plasma condition indicating the increase of SiO2 etch selectivity over the ACL. The increase of the SiO2 etch rate with increasing etch selectivity for the higher source frequency operation appears to be related to the increase of the total plasma density with increasing CF2/F ratio in the plasma. The SiO2 etch profile was also improved not only by using the pulsed plasma but also by increasing the source frequency.

Multifunctional, angle dependent antireflection, and hydrophilic properties of SiO2 inspired by nano-scale structures of cicada wings

NASA Astrophysics Data System (ADS)

Zada, Imran; Zhang, Wang; Sun, Peng; Imtiaz, Muhammad; Abbas, Waseem; Zhang, Di

2017-10-01

Inspired by the multifunctional properties of cicada wings, we have precisely replicated biomorphic SiO2 with antireflective structures (ARSs) using a simple, inexpensive, and highly effective sol-gel ultrasonic method. The biomorphic replica of SiO2 was directly achieved from a cicada template at high calcination. The biomorphic SiO2 not only inherited the ARS effectively but also exhibited the excellent angle dependent antireflective properties over a wide range of incident angles (10°-60°). The change in reflectance spectra (visible wavelength) of biomorphic SiO2 was observed from 0.3% to 3.3% with the increasing incident angles. The smooth surface of the SiO2 crystal without nanostructures showed a high reflection of 9.2% compared to the biomorphic SiO2 with ARS. These excellent antireflective properties of biomorphic SiO2 can be attributed to the nanoscale structures which introduce a gradient in the refractive index between air and the material surface via ARS. In the meantime, biomorphic SiO2 demonstrates high hydrophilic properties due to the existence of nanostructures on its surface. These multifunctional properties of biomorphic SiO2, angle dependent antireflective properties, and hydrophilicity with high thermal stability may have potential applications in solar cells and antifogging optical materials.

Positron annihilation on the surfaces of SiO 2 films thermally grown on single crystal of Cz-Si

NASA Astrophysics Data System (ADS)

Deng, Wen; Yue, Li; Zhang, Wei; Cheng, Xu-xin; Zhu, Yan-yan; Huang, Yu-yang

2009-09-01

Two-detector coincidence system and mono-energetic slow positron beam has been applied to measure the Doppler broadening spectra for single crystals of SiO2, SiO2 films with different thickness thermally grown on single crystal of Cz-Si, and single crystal of Si without oxide film. Oxygen is recognized as a peak at about 11.85 × 10-3m0c on the ratio curves. The S parameters decrease with the increase of positron implantation energy for the single crystal of SiO2 and Si without oxide film. However, for the thermally grown SiO2-Si sample, the S parameters in near surface of the sample increase with positron implantation energy. It is due to the formation of silicon oxide at the surface, which lead to lower S value. S and W parameters vary with positron implantation depth indicate that the SiO2-Si system consist of a surface layer, a SiO2 layer, a SiO2-Si interface layer and a semi-infinite Si substrate.

Adsorption of transgenic insecticidal Cry1Ab protein to SiO2. 2. Patch-controlled electrostatic attraction.

PubMed

Madliger, Michael; Sander, Michael; Schwarzenbach, René P

2010-12-01

Adsorption governs the fate of Cry proteins from genetically modified Bt crops in soils. The effect of ionic strength (I) on the adsorption of Cry1Ab (isoelectric point IEP(Cry1Ab) ≈ 6) to negatively charged quartz (SiO(2)) and positively charged poly-L-lysine (PLL) was investigated at pH 5 to 8, using quartz crystal microbalance with dissipation monitoring and optical waveguide lightmode spectroscopy. Cry1Ab adsorbed via positively and negatively charged surface patches to SiO(2) and PLL, respectively. This patch controlled electrostatic attraction (PCEA) explains the observed increase in Cry1Ab adsorption to sorbents that carried the same net charge as the protein (SiO(2) at pH > IEP(Cry1Ab) and PLL at pH < IEP(Cry1Ab)) with decreasing I. In contrast, the adsorption of two reference proteins, BSA and HEWL, with different adsorption mechanism, were little affected by similar changes of I. Consistent with PCEA, Cry1Ab desorption from SiO(2) at pH > IEP(Cry1Ab) increased with increasing I and pH. Weak Cry1Ab-SiO(2) PCEA above pH 7 resulted in reversible, concentration dependent adsorption. Solution depletion experiments showed that PCEA also governed Cry1Ab adsorption to SiO(2) particles at environmentally relevant concentrations (a few ng mL(-1)). These results imply that models describing Cry1Ab adsorption to charged surfaces in soils need to account for the nonuniform surface charge distribution of the protein.

Synergistic Effect of MoS2 and SiO2 Nanoparticles as Lubricant Additives for Magnesium Alloy–Steel Contacts

PubMed Central

Xie, Hongmei; Jiang, Bin; Hu, Xingyu; Peng, Cheng; Guo, Hongli; Pan, Fusheng

2017-01-01

The tribological performances of the SiO2/MoS2 hybrids as lubricant additives were explored by a reciprocating ball-on-flat tribometer for AZ31 magnesium alloy/AISI 52100 bearing steel pairs. The results demonstrated that the introduction of SiO2/MoS2 hybrids into the base oil exhibited a significant reduction in the friction coefficient and wear volume as well as an increase in load bearing capacity, which was better than the testing results of the SiO2 or MoS2 nanolubricants. Specifically, the addition of 0.1 wt % nano-SiO2 mixed with 1.0 wt % nano-MoS2 into the base oil reduced the friction coefficient by 21.8% and the wear volume by 8.6% compared to the 1.0 wt % MoS2 nanolubricants. The excellent lubrication behaviors of the SiO2/MoS2 hybrid nanolubricants can be explained by the micro-cooperation of different nanoparticles with disparate morphology and lubrication mechanisms. PMID:28644394

Preparation and Characterization of ZnO Nanoparticles Supported on Amorphous SiO2

PubMed Central

Chen, Ying; Ding, Hao; Sun, Sijia

2017-01-01

In order to reduce the primary particle size of zinc oxide (ZnO) and eliminate the agglomeration phenomenon to form a monodisperse state, Zn2+ was loaded on the surface of amorphous silica (SiO2) by the hydrogen bond association between hydroxyl groups in the hydrothermal process. After calcining the precursors, dehydration condensation among hydroxyl groups occurred and ZnO nanoparticles supported on amorphous SiO2 (ZnO–SiO2) were prepared. Furthermore, the SEM and TEM observations showed that ZnO nanoparticles with a particle size of 3–8 nm were uniformly and dispersedly loaded on the surface of amorphous SiO2. Compared with pure ZnO, ZnO–SiO2 showed a much better antibacterial performance in the minimum inhibitory concentration (MIC) test and the antibacterial properties of the paint adding ZnO–SiO2 composite. PMID:28796157

Magnetic behaviour of synthetic Co(2)SiO(4).

PubMed

Sazonov, Andrew; Meven, Martin; Hutanu, Vladimir; Heger, Gernot; Hansen, Thomas; Gukasov, Arsen

2009-12-01

Synthetic Co(2)SiO(4) crystallizes in the olivine structure (space group Pnma) with two crystallographically non-equivalent Co positions and shows antiferromagnetic ordering below 50 K. We have investigated the temperature variation of the Co(2)SiO(4) magnetic structure by means of non-polarized and polarized neutron diffraction for single crystals. Measurements with non-polarized neutrons were made at 2.5 K (below T(N)), whereas polarized neutron diffraction experiments were carried out at 70 and 150 K (above T(N)) in an external magnetic field of 7 T parallel to the b axis. Additional accurate non-polarized powder diffraction studies were performed in a broad temperature range from 5 to 500 K with small temperature increments. Detailed symmetry analysis of the Co(2)SiO(4) magnetic structure shows that it corresponds to the magnetic (Shubnikov) group Pnma, which allows the antiferromagnetic configuration (G(x), C(y), A(z)) for the 4a site with inversion symmetry 1 (Co1 position) and (0,C(y),0) for the 4c site with mirror symmetry m (Co2 position). The temperature dependence of the Co1 and Co2 magnetic moments obtained from neutron diffraction experiments was fitted in a modified molecular-field model. The polarized neutron study of the magnetization induced by an applied field shows a non-negligible amount of magnetic moment on the oxygen positions, indicating a delocalization of the magnetic moment from Co towards neighbouring O owing to superexchange coupling. The relative strength of the exchange interactions is discussed based on the non-polarized and polarized neutron data.

Enhanced Visible Transmittance of Thermochromic VO2 Thin Films by SiO2 Passivation Layer and Their Optical Characterization

PubMed Central

Yu, Jung-Hoon; Nam, Sang-Hun; Lee, Ji Won; Boo, Jin-Hyo

2016-01-01

This paper presents the preparation of high-quality vanadium dioxide (VO2) thermochromic thin films with enhanced visible transmittance (Tvis) via radio frequency (RF) sputtering and plasma enhanced chemical vapor deposition (PECVD). VO2 thin films with high Tvis and excellent optical switching efficiency (Eos) were successfully prepared by employing SiO2 as a passivation layer. After SiO2 deposition, the roughness of the films was decreased 2-fold and a denser structure was formed. These morphological changes corresponded to the results of optical characterization including the haze, reflectance and absorption spectra. In spite of SiO2 coating, the phase transition temperature (Tc) of the prepared films was not affected. Compared with pristine VO2, the total layer thickness after SiO2 coating was 160 nm, which is an increase of 80 nm. Despite the thickness change, the VO2 thin films showed a higher Tvis value (λ 650 nm, 58%) compared with the pristine samples (λ 650 nm, 43%). This enhancement of Tvis while maintaining high Eos is meaningful for VO2-based smart window applications. PMID:28773679

The effect of X-ray exposure on Ba2SiO4:Eu3+

NASA Astrophysics Data System (ADS)

Volhard, Max-Fabian; Jüstel, Thomas

2018-03-01

The ortho-silicates Ba2SiO4:Eu3+ and Ba2SiO4:Eu2+ are well-established materials for fluorescent light sources, e.g., phosphor converted LEDs. Samples containing Eu2+or Eu3+were synthesised by the solid-state-method, and the phase purity was determined by X-ray powder diffractometry. The photoluminescence of both phosphors was examined as a function of the pre-treatment. Upon irradiation of Ba2SiO4:Eu3+ with X-rays (tungsten target source), the reduction of Eu3+ towards Eu2+ was observed. This reduction behaviour was thoroughly recorded, and the linearity of the process was determined. Furthermore, the relationship between the acceleration voltage and the reduction process is discussed.

Enhancement of activity and sulfur resistance of CeO2 supported on TiO2-SiO2 for the selective catalytic reduction of NO by NH3.

PubMed

Liu, Caixia; Chen, Liang; Li, Junhua; Ma, Lei; Arandiyan, Hamidreza; Du, Yu; Xu, Jiayu; Hao, Jiming

2012-06-05

A series of novel metal-oxide-supported CeO(2) catalysts were prepared via the wet impregnation method, and their NH(3)-SCR activities were investigated. The Ce/TiO(2)-SiO(2) catalyst with a Ti/Si mass ratio of 3/1 exhibited superior NH(3)-SCR activity and high N(2) selectivity in the temperature range of 250-450 °C. The characterization results revealed that the activity enhancement was correlated with the properties of the support material. Cerium was highly dispersed on the TiO(2)-SiO(2) binary metal oxide support, and the interaction of Ti and Si resulted in greater conversion of Ce(4+) to Ce(3+) on the surface of the catalyst compared to that on the single metal oxide supports. As a result of in the increased number of acid sites on Ce/TiO(2)-SiO(2) that resulted from the addition of SiO(2), the NH(3) adsorption capacity was significantly improved. All of these factors played significant roles in the high SCR activity. More importantly, Ce/TiO(2)-SiO(2) exhibited strong resistance to SO(2) and H(2)O poisoning. After the addition of SiO(2), the number of Lewis-acid sites was not decreased, but the number of Brønsted-acid sites on the TiO(2)-SiO(2) carrier was increased. The introduction of SiO(2) further weakened the alkalinity over the surface of the Ce/TiO(2)-SiO(2) catalyst, which resulted in sulfate not easily accumulating on the surface of the Ce/TiO(2)-SiO(2) catalyst in comparison with Ce/TiO(2).

Fabrication of graphene oxide decorated with Fe3O4@SiO2 for immobilization of cellulase

NASA Astrophysics Data System (ADS)

Li, Yue; Wang, Xiang-Yu; Jiang, Xiao-Ping; Ye, Jing-Jing; Zhang, Ye-Wang; Zhang, Xiao-Yun

2015-01-01

Fe3O4@SiO2-graphene oxide (GO) composites were successfully fabricated by chemical binding of functional Fe3O4@SiO2 and GO and applied to immobilization of cellulase via covalent attachment. The prepared composites were further characterized by transmission electron microscopy and Fourier transform infrared spectroscopy. Fe3O4 nanoparticles (NPs) were monodisperse spheres with a mean diameter of 17 ± 0.2 nm. The thickness of SiO2 layer was calculated as being 6.5 ± 0.2 nm. The size of Fe3O4@SiO2 NPs was 24 ± 0.3 nm, similar to that of Fe3O4@SiO2-NH2. Fe3O4@SiO2-GO composites were synthesized by linking of Fe3O4@SiO2-NH2 NPs to GO with the catalysis of EDC and NHS. The prepared composites were used for immobilization of cellulase. A high immobilization yield and efficiency of above 90 % were obtained after the optimization. The half-life of immobilized cellulase (722 min) was 3.34-fold higher than that of free enzyme (216 min) at 50 °C. Compared with the free cellulase, the optimal temperature of the immobilized enzyme was not changed; but the optimal pH was shifted from 5.0 to 4.0, and the thermal stability was enhanced. The immobilized cellulase could be easily separated and reused under magnetic field. These results strongly indicate that the cellulase immobilized onto the Fe3O4@SiO2-GO composite has potential applications in the production of bioethanol.

Surface Phenomena During Plasma-Assisted Atomic Layer Etching of SiO2.

PubMed

Gasvoda, Ryan J; van de Steeg, Alex W; Bhowmick, Ranadeep; Hudson, Eric A; Agarwal, Sumit

2017-09-13

Surface phenomena during atomic layer etching (ALE) of SiO 2 were studied during sequential half-cycles of plasma-assisted fluorocarbon (CF x ) film deposition and Ar plasma activation of the CF x film using in situ surface infrared spectroscopy and ellipsometry. Infrared spectra of the surface after the CF x deposition half-cycle from a C 4 F 8 /Ar plasma show that an atomically thin mixing layer is formed between the deposited CF x layer and the underlying SiO 2 film. Etching during the Ar plasma cycle is activated by Ar + bombardment of the CF x layer, which results in the simultaneous removal of surface CF x and the underlying SiO 2 film. The interfacial mixing layer in ALE is atomically thin due to the low ion energy during CF x deposition, which combined with an ultrathin CF x layer ensures an etch rate of a few monolayers per cycle. In situ ellipsometry shows that for a ∼4 Å thick CF x film, ∼3-4 Å of SiO 2 was etched per cycle. However, during the Ar plasma half-cycle, etching proceeds beyond complete removal of the surface CF x layer as F-containing radicals are slowly released into the plasma from the reactor walls. Buildup of CF x on reactor walls leads to a gradual increase in the etch per cycle.

Preparation and characterization of silane-modified SiO2 particles reinforced resin composites with fluorinated acrylate polymer.

PubMed

Liu, Xue; Wang, Zengyao; Zhao, Chengji; Bu, Wenhuan; Na, Hui

2018-04-01

A series of fluorinated dental resin composites were prepared with two kinds of SiO 2 particles. Bis-GMA (bisphenol A-glycerolate dimethacrylate)/4-TF-PQEA (fluorinated acrylate monomer)/TEGDMA (triethylene glycol dimethacrylate) (40/30/30, wt/wt/wt) was introduced as resin matrix. SiO 2 nanopartices (30nm) and SiO 2 microparticles (0.3µm) were silanized with 3-methacryloxypropyl trimethoxysilane (γ-MPS) and used as fillers. After mixing the resin matrix with 0%, 10%, 20%, 30% SiO 2 nanopartices and 0%, 10%, 20%, 30%, 40%, 50% SiO 2 microparticles, respectively, the fluorinated resin composites were obtained. Properties including double bond conversion (DC), polymerization shrinkage (PS), water sorption (W p ), water solubility (W y ), mechanical properties and cytotoxicity were investigated in comparison with those of neat resin system. The results showed that, filler particles could improve the overall performance of resin composites, particularly in improving mechanical properties and reducing PS of composites along with the addition of filler loading. Compared to resin composites containing SiO 2 microparticles, SiO 2 nanoparticles resin composites had higher DC, higher mechanical properties, lower PS and lower W p under the same filler content. Especially, 50% SiO 2 microparticles reinforced resins exhibited the best flexural strength (104.04 ± 7.40MPa), flexural modulus (5.62 ± 0.16GPa), vickers microhardness (37.34 ± 1.13 HV), compressive strength (301.54 ± 5.66MPa) and the lowest polymerization (3.42 ± 0.22%). Copyright © 2018 Elsevier Ltd. All rights reserved.

Preparation of SiO2 Passivation Thin Film for Improved the Organic Light-Emitting Device Life Time

NASA Astrophysics Data System (ADS)

Hong, Jeong Soo; Kim, Sang Mo; Kim, Kyung-Hwan

2011-08-01

To improve the organic light-emitting diode (OLED) lifetime, we prepared a SiO2 thin film for OLED passivation using a facing target sputtering (FTS) system as a function of oxygen gas flow rate and working pressure. The properties of the SiO2 thin film were examined by Fourier transform infrared (FT-IR), photoluminescence (PL) intensity measurement, field emission scanning electron microscopy (FE-SEM), and ultraviolet-visible (UV-vis) spectrometry that As a result, we found that a SiO2 thin film is formed at a 2 sccm oxygen gas flow rate and results the minimum damage to the organic layer is observed at a 1 mTorr working pressure. Also, from the water vapor transmission rate (WVTR), we observed that all of the as-deposited SiO2 thin films showed the ability of blocking moisture. After the properties were evaluated, an optimized SiO2 thin film was applied to OLED passivation. As a result, the property of the OLED fabricated by SiO2 passivation is similar to the OLED fabricated by glass passivation. However, the performance of OLED was degraded by enhancing of SiO2 passivation. This is the organic layer of the device is exposed to plasma for a prolonged period. Therefore, a method of minimizing damage to the organic layer and optimum conditions for what are important.

Mass spectrometric studies of SiO2 deposition in an indirect plasma enhanced LPCVD system

NASA Technical Reports Server (NTRS)

Iyer, R.; Lile, D. L.; Mcconica, C. M.

1993-01-01

Reaction pathways for the low temperature deposition of SiO2 from silane and indirect plasma-excited oxygen-nitrogen mixtures are proposed based on experimental evidence gained from mass spectrometry in an indirect plasma enhanced chemical vapor deposition chamber. It was observed that about 80-85 percent of the silane was oxidized to byproduct hydrogen and only about 15-20 percent to water. Such conversion levels have led us to interpret that silanol (SiH3OH) could be the precursor for SiO2 film deposition, rather than siloxane /(SiH3)2O/ which has generally been cited in the literature. From mass spectrometry, we have also shown the effects of the plasma, and of mixing small amounts of N2 with the oxygen flow, in increasing the deposition rate of SiO2. Free radical reaction of nitric oxide, synthesized from the reaction of oxygen and nitrogen in the plasma chamber, and an *ncrease in atomic oxygen concentration, are believed to be the reasons for these SiO2 deposition rate increases. Through mass spectrometry we have, in addition, been able to identify products, presumably originating from terminating reactions, among a sequence of chemical reactions proposed for the deposition of SiO2.

Silicate liquid immiscibility in magmas and in the system K2O-FeO-AI2O3-SiO2: an example of serendipity

USGS Publications Warehouse

Roedder, E.

1978-01-01

The concept of silicate liquid immiscibility was invoked early in the history of petrology to explain certain pairs of compositionally divergent rocks, but. as a result of papers by Greig (Am. J. Sci. 13, 1-44, 133-154) and Bowen (The Evolution of the Igneous Rocks), it fell into disfavor for many years. The discovery of immiscibility in geologically reasonable temperature ranges and compositions in experimental work on the system K2O-FeO-Al2O3-SiO2, and of evidence for immiscibility in a variety of lunar and terrestrial rocks, has reinstated the process. Phase equilibria in the high-silica corner of the tetrahedron representing the system K2O- FeO-Al2O3-SiO2 are presented, in the form of constant FeO sections through the tetrahedron, at 10% increments. Those sections, showing the tentative relationships of the primary phase volumes, are based on 5631 quenching runs on 519 compositions, made in metallic iron containers in pure nitrogen. Thirteen crystalline compounds are involved, of which at least six show two or more crystal modifica-tions. Two separate phase volumes, in each of which two immiscible liquids, one iron-rich and the other iron-poor, are present at the liquidus. One of these volumes is entirely within the quaternary system, astride the 1:1 K2O:Al2O3 plane. No quaternary compounds as such have been found, but evidence does point toward at least partial quaternary solid solution, with rapidly lowering liquidus temperatures, from K2O??Al2O3?? 2SiO2 ('potash nepheline', kalsilite. kaliophilite) to the isostructural compound K2O??FeO??3SiO2, and from K2O??Al2O3??4SiO2 (leucite) to the isostructural compound K2O??FeO??5SiO2, Both of these series apparently involve substitution, in tetrahedral coordination. of a ferrous iron and a silicon ion for two aluminum ions. Some of the 'impurities' found in analyses of the natural phases may reflect these substitutions. As a result of the geometry of the immiscibility volume located entirely within the quaternary

Facile preparation of magnetic mesoporous MnFe2O4@SiO2-CTAB composites for Cr(VI) adsorption and reduction.

PubMed

Li, Na; Fu, Fenglian; Lu, Jianwei; Ding, Zecong; Tang, Bing; Pang, Jiabin

2017-01-01

Chromium-contaminated water is regarded as one of the biggest threats to human health. In this study, a novel magnetic mesoporous MnFe 2 O 4 @SiO 2 -CTAB composite was prepared by a facile one-step modification method and applied to remove Cr(VI). X-ray diffraction, scanning electron microscopy, transmission electron microscopy, specific surface area, and vibrating sample magnetometer were used to characterize MnFe 2 O 4 @SiO 2 -CTAB composites. The morphology analysis showed that the composites displayed a core-shell structure. The outer shell was mesoporous silica with CTAB and the core was MnFe 2 O 4 nanoparticles, which ensured the easy separation by an external magnetic field. The performance of MnFe 2 O 4 @SiO 2 -CTAB composites in Cr(VI) removal was far better than that of bare MnFe 2 O 4 nanoparticles. There were two reasons for the effective removal of Cr(VI) by MnFe 2 O 4 @SiO 2 -CTAB composites: (1) mesoporous silica shell with abundant CTA + significantly enhanced the Cr(VI) adsorption capacity of the composites; (2) a portion of Cr(VI) was reduced to less toxic Cr(III) by MnFe 2 O 4 , followed by Cr(III) immobilized on MnFe 2 O 4 @SiO 2 -CTAB composites, which had been demonstrated by X-ray photoelectron spectroscopy results. The adsorption of Cr(VI) onto MnFe 2 O 4 @SiO 2 -CTAB followed the Freundlich isotherm model and pseudo-second-order model. Tests on the regeneration and reuse of the composites were performed. The removal efficiency of Cr(VI) still retained 92.4% in the sixth cycle. MnFe 2 O 4 @SiO 2 -CTAB composites exhibited a great potential for the removal of Cr(VI) from water. Copyright © 2016 Elsevier Ltd. All rights reserved.

Matrix solid-phase dispersion extraction of organophosphorus pesticide using SiO2-poly(N-vinylimidazole)

NASA Astrophysics Data System (ADS)

Gutiérrez-Solís, M. C.; Muñoz-Rodríguez, D.; Medina-Peralta, S.; Carrera-Figueiras, C.; Ávila-Ortega, A.

2013-06-01

A sorbent material based on silica particles modified with poly(N-vinylimidazole) (SiO2-PVI) has been evaluated for the treatment of samples by matrix solid-phase dispersion (MSPD). The extraction of four organophosphorus pesticides was done from a spiked tomato and the extracts were analyzed by gas chromatography coupled to mass spectrometry. Six elution solvents were evaluated and acetone was selected due to better recovery of the four pesticides and low background signal in the chromatograms. A factorial design 24 was used for selection of extraction conditions. The factors were contact time, acetone volume, treatment (with or without freeze-drying) and adsorbent (SiO2 or SiO2-PVI). The best recoveries were obtained using 15 minutes of contact, 2 mL of solvent and sorbent without freeze-drying. The recoveries were between 60 and 83% for SiO2-PVI in spiked tomato with 0.2 and 0.8μg/g.

Viscosity of SiO2-"FeO"-Al2O3 System in Equilibrium with Metallic Fe

NASA Astrophysics Data System (ADS)

Chen, Mao; Raghunath, Sreekanth; Zhao, Baojun

2013-08-01

The present study delivered the measurements of viscosities in SiO2-"FeO"-Al2O3 system in equilibrium with metallic Fe. The rotational spindle technique was used in the measurements at the temperature range of 1473 K to 1773 K (1200 °C to 1500 °C). Molybdenum crucibles and spindles were employed in all measurements. The Fe saturation condition was maintained by an iron plate placed at the bottom of the crucible. The equilibrium compositions of the slags were measured by EPMA after the viscosity measurements. The effect of up to 20 mol. pct Al2O3 on the viscosity of the SiO2-"FeO" slag was investigated. The "charge compensation effect" of the Al2O3 and FeO association has been discussed. The modified quasi-chemical viscosity model has been optimized in the SiO2-"FeO"-Al2O3 system in equilibrium with metallic Fe to describe the viscosity measurements of the present study.

Nanoscale charge transfer and diffusion at the MoS2/SiO2 interface by atomic force microscopy: contact injection versus triboelectrification.

PubMed

Xu, Rui; Ye, Shili; Xu, Kunqi; Lei, Le; Hussain, Sabir; Zheng, Zhiyue; Pang, Fei; Xing, Shuya; Liu, Xinmeng; Ji, Wei; Cheng, Zhihai

2018-08-31

Understanding the process of charge generation, transfer, and diffusion between two-dimensional (2D) materials and their supporting substrates is very important for potential applications of 2D materials. Compared with the systematic studies of triboelectric charging in a bulk sample, a fundamental understanding of the triboelectrification of the 2D material/insulator system is rather limited. Here, the charge transfer and diffusion of both the SiO 2 surface and MoS 2 /SiO 2 interface through contact electrification and frictional electrification are investigated systematically in situ by scanning Kelvin probe microscopy and dual-harmonic electrostatic force microscopy. Different from the simple static charge transfer between SiO 2 and the PtSi alloy atomic force microscope (AFM) tip, the charge transfer between the tip and the MoS 2 /SiO 2 system is complicated. Triboelectric charges, generated by contact or frictional electrification with the AFM tip, are trapped at the MoS 2 /SiO 2 interface and act as floating gates. The local charge discharge processes can be obtained by monitoring the surface potential. The charge decay time (τ) of the MoS 2 /SiO 2 interface is one (or two) orders of magnitude larger than the decay time τ of the SiO 2 surface. This work facilitates an understanding of the triboelectric and de-electrification of the interface between 2D materials and substrates. In addition to the charge transfer and diffusion, we demonstrate the nanopatterns of surface and interfacial charges, which have great potential for the application of self-assembly of charged nanostructures.

Infrared, Raman and Magnetic Resonance Spectroscopic Study of SiO2:C Nanopowders.

PubMed

Savchenko, Dariya; Vorliček, Vladimir; Kalabukhova, Ekaterina; Sitnikov, Aleksandr; Vasin, Andrii; Kysil, Dmytro; Sevostianov, Stanislav; Tertykh, Valentyn; Nazarov, Alexei

2017-12-01

Optical and magnetic properties of SiO 2 :C nanopowders obtained by chemical and thermal modification of fumed silica were studied by Fourier transform infrared spectroscopy, Raman, continuous wave (CW) electron paramagnetic resonance (EPR), echo-detected EPR and pulsed electron nuclear double resonance (ENDOR) spectroscopy. Two overlapping signals of Lorentzian lineshape were detected in CW EPR spectra of the initial SiO 2 :C. The EPR signal at g = 2.0055(3) is due to the silicon dangling bonds, which vanishes after thermal annealing, and the second EPR signal at g = 2.0033(3) was attributed to the carbon-related defect (CRD). The annealing of the SiO 2 :C samples gives rise to the increase of the CRD spin density and shift to the higher g-values due to the appearance of the oxygen in the vicinity of the CRD. Based on the temperature-dependent behavior of the CRD EPR signal intensity, linewidth and resonance field position we have attributed it to the spin system with non-localized electrons hopping between neighboring carbon dangling bonds, which undergo a strong exchange interaction with a localized spin system of carbon nanodots. The observed motional narrowing of the CRD EPR signal in the temperature interval from 4 to 20 K indicates that electrons are mobile at 4 K which can be explained by a quantum character of the conductivity in the vicinity of the carbon layer. The electrons trapped in quantum wells move from one carbon nanodot to another by hopping process through the energy barrier. The fact that echo-detected EPR signal at g = 2.0035(3) was observed in SiO 2 :C sample annealed at T ann  ≥ 700 °C serves as evidence that non-localized electrons coexist with localized electrons that have the superhyperfine interaction with surrounding 13 C and 29 Si nuclei located at the SiO 2 :C interface. The presence of the superhyperfine interaction of CRD with 1 H nuclei indicates the existence of hydrogenated regions in SiO 2 :C sample.

Bacterial cellulose composites loaded with SiO2 nanoparticles: Dynamic-mechanical and thermal properties.

PubMed

Sheykhnazari, Somayeh; Tabarsa, Taghi; Ashori, Alireza; Ghanbari, Abbas

2016-12-01

The aim of this paper was to prepare composites of bacterial cellulose (BC) filled with silica (SiO 2 ) nanoparticles to evaluate the influence of the SiO 2 contents (3, 5 and 7wt%) on the thermo-mechanical properties of the composites. BC hydro-gel was immersed in an aqueous solution of silanol derived from tetraethoxysilane (TEOS), the silanol was then converted into SiO 2 in the BC matrix by pressing at 120°C and 2MPa. The BC/SiO 2 translucent sheets were examined by dynamic-mechanical analysis (DMA), thermo gravimetric analysis (TGA), and scanning electron microscopy (SEM). The temperature dependence of the storage modulus, loss modulus and tan delta was determined by DMA. In general, the results revealed that the increment of storage modulus and thermal stability increased concomitantly with the augmentation of SiO 2 content. Therefore, it could be concluded that the mechanical properties of the composites were improved by using high amounts of nano silica. This would be a high aspect ratio of BC capable of connecting the BC matrix and SiO 2 , thereby enhancing a large contact surface and resulting in excellent coherence. A decrease of the storage modulus was consistent with increasing temperature, resulting from softening of the composites. The storage modulus of the composites increased in the order: BC/S7>BC/S5>BC/S3, while the loss modulus and tan delta decreased. On the other hand, the thermal stabilities of all BC/SiO 2 composites were remarkably enhanced as compared to the pristine BC. TGA curves showed that the temperature of decomposition of the pure BC gradually shifted from about 260°C to about 370°C as silica content increased. SEM observations illustrated that the nano-scale SiO 2 was embedded between the voids and nano-fibrils of the BC matrix. Overall, the results indicated that the successful synthesis and superior properties of BC/SiO 2 advocate its effectiveness for various applications. Copyright © 2016 Elsevier B.V. All rights reserved.

Behavior of Al2O3 and SiO2 with heating in a Cl2 + CO stream

NASA Technical Reports Server (NTRS)

Shchetinin, L. K.

1984-01-01

Differential thermal analysis (DTA) and Thermogravimetric analysis (TGA) were used to study the chlorination of alpha-Al2O3, gamma-Al2O3 and amorphous SiO2 in a Cl + CO stream, for the preparation of AlCl3 and SiCl4. The chlorination starting temperatures were 235 deg for Al2O3 and 680 deg for SiO2. The chlorination of alpha- and gamma-Al2O3 takes place via the formation of AlOCl as an intermediate product, and its subsequent dissociation at 480 to 560 deg, according to 3AlOCl yields AlCl3 + Al2O3. The chlorination activation energies are given for the three oxides.

Preparation of Fe3O4/SiO2-guanidine organobase catalyst for 1,5-diphenylpenta-2,4-dien-1-one synthesis

NASA Astrophysics Data System (ADS)

Cahyana, A. H.; Fitria, D.; Ardiansah, B.; Rahayu, D. U. C.

2017-04-01

A novel heterogeneous organobase catalyst of Fe3O4/SiO2-guanidine was prepared in three stages. First, Fe3O4 nanoparticle was obtained by co-precipitation method using seaweed Sargassum Sp. as natural reductant. Fe3O4 was then coated by SiO2 using TEOS as silica source, resulting Fe3O4/SiO2. Finally, Fe3O4/SiO2-Guanidine was obtained by modifying Fe3O4/SiO2 with guanidine in the suitable reaction condition. This organobase catalyst was characterized by Scanning Electron Microscope (SEM), Energy Dispersive X-ray Spectroscopy (EDS), and Particle Size Analyzer (PSA). The material was then used as a highly active catalyst in aldol condensation reaction between acetophenone and cinnamaldehyde to produce 1,5-diphenylpenta-2,4-dien-1-one. The structure elucidation of the organic product was confirmed by UV-Vis, FTIR, and LC-MS.

Highly transparent and efficient counter electrode using SiO2/PEDOT-PSS composite for bifacial dye-sensitized solar cells.

PubMed

Song, Dandan; Li, Meicheng; Li, Yingfeng; Zhao, Xing; Jiang, Bing; Jiang, Yongjian

2014-05-28

A highly transparent and efficient counter electrode was facilely fabricated using SiO2/poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT-PSS) inorganic/organic composite and used in bifacial dye-sensitized solar cells (DSCs). The optical properties of SiO2/PEDOT-PSS electrode can be tailored by the blending amount of SiO2 and film thickness, and the incorporation of SiO2 in PEDOT-PSS provides better transmission in the long wavelength range. Meanwhile, the SiO2/PEDOT-PSS counter electrode shows a better electrochemical catalytic activity than PEDOT-PSS electrode for triiodide reduction, and the role of SiO2 in the catalytic process is investigated. The bifacial DSC with SiO2/PEDOT-PSS counter electrode achieves a high power conversion efficiency (PCE) of 4.61% under rear-side irradiation, which is about 83% of that obtained under front-side irradiation. Furthermore, the PCE of bifacial DSC can be significantly increased by adding a reflector to achieve bifacial irradiation, which is 39% higher than that under conventional front-side irradiation.

Radiation Hardened Silicon-on-Insulator Structures with N+ Ion Modified Buried SiO2 Layer

NASA Astrophysics Data System (ADS)

Tyschenko, I. E.; Popov, V. P.

2009-12-01

Radiation-resistant silicon-on-insulator structures were produced by N+ ion implantation into thermally grown SiO2 film and subsequent hydrogen transfer of the Si layer to the nitrogen-implanted substrate under conditions of vacuum wafer bonding. Accumulation of the carriers in the buried SiO2 was investigated as a function of fluence of nitrogen ions in the range (1-6)×1015 cm2 and as a function of total radiation dose ranging from 104 to 107 rad (Si). It was found that the charge generated near the nitrided bonding interface was reduced by a factor of four compared to the thermal SiO2/Si interface.

Effects of (NH4)2S x treatment on the surface properties of SiO2 as a gate dielectric for pentacene thin-film transistor applications

NASA Astrophysics Data System (ADS)

Hung, Cheng-Chun; Lin, Yow-Jon

2018-01-01

The effect of (NH4)2S x treatment on the surface properties of SiO2 is studied. (NH4)2S x treatment leads to the formation of S-Si bonds on the SiO2 surface that serves to reduce the number of donor-like trap states, inducing the shift of the Fermi level toward the conduction band minimum. A finding in this case is the noticeably reduced value of the SiO2 capacitance as the sulfurated layer is formed at the SiO2 surface. The effect of SiO2 layers with (NH4)2S x treatment on the carrier transport behaviors for the pentacene/SiO2-based organic thin-film transistor (OTFT) is also studied. The pentacene/as-cleaned SiO2-based OTFT shows depletion-mode behavior, whereas the pentacene/(NH4)2S x -treated SiO2-based OTFT exhibits enhancement-mode behavior. Experimental identification confirms that the depletion-/enhancement-mode conversion is due to the dominance competition between donor-like trap states in SiO2 near the pentacene/SiO2 interface and acceptor-like trap states in the pentacene channel. A sulfurated layer between pentacene and SiO2 is expected to give significant contributions to carrier transport for pentacene/SiO2-based OTFTs.

Magnetic zeolite NaA: synthesis, characterization based on metakaolin and its application for the removal of Cu2+, Pb2+.

PubMed

Liu, Haibo; Peng, Shuchuan; Shu, Lin; Chen, Tianhu; Bao, Teng; Frost, Ray L

2013-06-01

The optimum parameters for synthesis of zeolite NaA based on metakaolin were investigated according to results of cation exchange capacity and static water adsorption of all synthesis products and selected X-ray diffraction (XRD). Magnetic zeolite NaA was synthesized by adding Fe3O4 in the precursor of zeolite. Zeolite NaA and magnetic zeolite NaA were characterized with scanning electron microscopy (SEM) and XRD. Magnetic zeolite NaA with different Fe3O4 loadings was prepared and used for removal of heavy metals (Cu(2+), Pb(2+)). The results show the optimum parameters for synthesis zeolite NaA are SiO2/Al2O3=2.3, Na2O/SiO2=1.4, H2O/Na2O=50, crystallization time 8h, crystallization temperature 95 °C. The addition of Fe3O4 makes the NaA zeolite with good magnetic susceptibility and good magnetic stability regardless of the Fe3O4 loading, confirming the considerable separation efficiency. Additionally, Fe3O4 loading had a little effect on removal of heavy metal by magnetic zeolite, however, the adsorption capacity still reaches 2.3 mmol g(-1) for Cu(2+), Pb(2+) with a removal efficiency of over 95% in spite of 4.7% Fe3O4 loading. This indicates magnetic zeolite can be used to remove metal heavy at least Cu(2+), Pb(2+) from water with metallic contaminants and can be separated easily after a magnetic process. Copyright © 2013 Elsevier Ltd. All rights reserved.

Synthesis, luminescence, and energy-transfer properties of β-Na2Ca4(PO4)2(SiO4):A (A = Eu(2+), Dy(3+), Ce(3+)/Tb(3+)) phosphors.

PubMed