Electrodeposition synthesis of MnO{sub 2}/TiO{sub 2} nanotube arrays nanocomposites and their visible light photocatalytic activity

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xu, Xuyao; Zhou, Xiaosong, E-mail: zxs801213@163.com; Li, Xiaoyu, E-mail: lixiaoyu@iga.ac.cn

2014-11-15

Highlights: • MnO{sub 2}/TiO{sub 2} nanotube arrays nanocomposites are prepared by electrodeposition. • MnO{sub 2}/TiO{sub 2} exhibits high visible light photocatalytic activity. • The results of XRD show the depositions are attributed to α-MnO{sub 2}. • A photocatalytic mechanism is discussed under visible light irradiation. - Abstract: MnO{sub 2}/TiO{sub 2} nanotube arrays nanocomposite photocatalysts have been synthesized through an electrodeposition method. X-ray powder diffraction analysis and X-ray photoelectron spectroscopy measurements reveal that the products of electrodeposition method are MnO{sub 2}. Scanning electron microscopy measurements suggest that the depositions are deposited on the surface or internal of the nanotube. UV–vis lightmore » absorbance spectra demonstrate the excellent adsorption properties of MnO{sub 2}/TiO{sub 2} over the whole region of visible light, which enables this novel photocatalytic material to possess remarkable activity in the photocatalytic degradation of acid Orange II under visible light radiation. Moreover, a possible photocatalytic mechanism is discussed.« less

Fabrication and photoelectrochemical properties of ZnS/Au/TiO2 nanotube array films.

PubMed

Zhu, Yan-Feng; Zhang, Juan; Xu, Lu; Guo, Ya; Wang, Xiao-Ping; Du, Rong-Gui; Lin, Chang-Jian

2013-03-21

A highly ordered TiO(2) nanotube array film was fabricated by an anodic oxidation method. The film was modified by Au nanoparticles (NPs) formed by a deposition-precipitation technique and was covered with a thin ZnS shell prepared by a successive ionic layer adsorption and reaction (SILAR) method. The photoelectrochemical properties of the prepared ZnS/Au/TiO(2) composite film were evaluated by incident photon-to-current conversion efficiency (IPCE), and photopotential and electrochemical impedance spectroscopy (EIS) measurements under white light illumination. The results indicated that the Au NPs could expand the light sensitivity range of the film and suppress the electron-hole recombination, and the ZnS shell could inhibit the leakage of photogenerated electrons from the surface of Au NPs to the ZnS/electrolyte interface. When the 403 stainless steel in a 0.5 M NaCl solution was coupled to the ZnS/Au/TiO(2) nanotube film photoanode under illumination, its potential decreased by 400 mV, showing that the composite film had a better photocathodic protection effect on the steel than that of a pure TiO(2) nanotube film.

Synthesis of molecular imprinted polymer modified TiO{sub 2} nanotube array electrode and their photoelectrocatalytic activity

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lu Na; Chen Shuo; Wang Hongtao

2008-10-15

A tetracycline hydrochloride (TC) molecularly imprinted polymer (MIP) modified TiO{sub 2} nanotube array electrode was prepared via surface molecular imprinting. Its surface was structured with surface voids and the nanotubes were open at top end with an average diameter of approximately 50 nm. The MIP-modified TiO{sub 2} nanotube array with anatase phase was identified by XRD and a distinguishable red shift in the absorption spectrum was observed. The MIP-modified electrode also exhibited a high adsorption capacity for TC due to its high surface area providing imprinted sites. Photocurrent was generated on the MIP-modified photoanode using the simulated solar spectrum andmore » increased with the increase of positive bias potential. Under simulated solar light irradiation, the MIP-modified TiO{sub 2} nanotube array electrode exhibited enhanced photoelectrocatalytic (PEC) activity with the apparent first-order rate constant being 1.2-fold of that with TiO{sub 2} nanotube array electrode. The effect of the thickness of the MIP layer on the PEC activity was also evaluated. - Graphical abstract: A tetracycline hydrochloride molecularly imprinted polymer modified TiO{sub 2} nanotube array electrode was prepared via surface molecular imprinting. It showed improved response to simulated solar light and higher adsorption capability for tetracycline hydrochloride, thereby exhibiting increased PEC activity under simulated solar light irradiation. The apparent first-order rate constant was 1.2-fold of that on TiO{sub 2} nanotube array electrode.« less

Structure and dye-sensitized solar cell application of TiO2 nanotube arrays fabricated by the anodic oxidation method

NASA Astrophysics Data System (ADS)

Ok, Seon-Yeong; Cho, Kwon-Koo; Kim, Ki-Won; Ryu, Kwang-Sun

2010-05-01

Well-ordered TiO2 nanotube arrays were fabricated by the potentiostatic anodic oxidation method using pure Ti foil as a working electrode and ethylene glycol solution as an electrolyte with the small addition of NH4F and H2O. The influence of anodization temperature and time on the morphology and formation of TiO2 nanotube arrays was examined. The TiO2 nanotube arrays were applied as a photoelectrode to dye-sensitized solar cells. Regardless of anodizing temperature and time, the average diameter and wall thickness of TiO2 nanotube arrays show a similar value, whereas the length increases with decreasing reaction temperature. The conversion efficiency is very low, which is due to a morphology breaking of the TiO2 nanotube arrays in the manufacturing process of a photoelectrode.

Transparent anodic TiO2 nanotube arrays on plastic substrates for disposable biosensors and flexible electronics.

PubMed

Farsinezhad, Samira; Mohammadpour, Arash; Dalrymple, Ashley N; Geisinger, Jared; Kar, Piyush; Brett, Michael J; Shankar, Karthik

2013-04-01

Exploitation of anodically formed self-organized TiO2 nanotube arrays in mass-manufactured, disposable biosensors, rollable electrochromic displays and flexible large-area solar cells would greatly benefit from integration with transparent and flexible polymeric substrates. Such integration requires the vacuum deposition of a thin film of titanium on the desired substrate, which is then anodized in suitable media to generate TiO2 nanotube arrays. However the challenges associated with control of Ti film morphology, nanotube array synthesis conditions, and film adhesion and transparency, have necessitated the use of substrate heating during deposition to temperatures of at least 300 degrees C and as high as 500 degrees C to generate highly ordered open-pore nanotube arrays, thus preventing the use of polymeric substrates. We report on a film growth technique that exploits atomic peening to achieve high quality transparent TiO2 nanotube arrays with lengths up to 5.1 microm at room temperature on polyimide substrates without the need for substrate heating or substrate biasing or a Kauffman ion source. The superior optical quality and uniformity of the nanotube arrays was evidenced by the high specular reflectivity and the smooth pattern of periodic interferometric fringes in the transmission spectra of the nanotube arrays, from which the wavelength-dependent effective refractive index was extracted for the air-TiO2 composite medium. A fluorescent immunoassay biosensor constructed using 5.1 microm-long transparent titania nanotube arrays (TTNAs) grown on Kapton substrates detected human cardiac troponin I at a concentration of 0.1 microg ml(-1).

A Facile Method for Loading CeO2 Nanoparticles on Anodic TiO2 Nanotube Arrays.

PubMed

Liao, Yulong; Yuan, Botao; Zhang, Dainan; Wang, Xiaoyi; Li, Yuanxun; Wen, Qiye; Zhang, Huaiwu; Zhong, Zhiyong

2018-04-03

In this paper, a facile method was proposed to load CeO 2 nanoparticles (NPs) on anodic TiO 2 nanotube (NT) arrays, which leads to a formation of CeO 2 /TiO 2 heterojunctions. Highly ordered anatase phase TiO 2 NT arrays were fabricated by using anodic oxidation method, then these individual TiO 2 NTs were used as tiny "nano-containers" to load a small amount of Ce(NO 3 ) 3 solutions. The loaded anodic TiO 2 NTs were baked and heated to a high temperature of 450 °C, under which the Ce(NO 3 ) 3 would be thermally decomposed inside those nano-containers. After the thermal decomposition of Ce(NO 3 ) 3 , cubic crystal CeO 2 NPs were obtained and successfully loaded into the anodic TiO 2 NT arrays. The prepared CeO 2 /TiO 2 heterojunction structures were characterized by a variety of analytical technologies, including XRD, SEM, and Raman spectra. This study provides a facile approach to prepare CeO 2 /TiO 2 films, which could be very useful for environmental and energy-related areas.

Synthesis and magnetotransport studies of CrO2 films grown on TiO2 nanotube arrays by chemical vapor deposition

NASA Astrophysics Data System (ADS)

Wang, Xiaoling; Zhang, Caiping; Wang, Lu; Lin, Tao; Wen, Gehui

2018-04-01

The CrO2 films have been prepared on the TiO2 nanotube array template via atmospheric pressure chemical vapor deposition method. And the growth procedure was studied. In the beginning of the deposition process, the CrO2 grows on the cross section of the TiO2 nanotubes wall, forms a nanonet-like layer. And the grain size of CrO2 is very small. With the increase of the deposition time, the grain size of CrO2 also increases, and the nanonet-like layer changes into porous film. With the further increase of the deposition time, all the nanotubes are covered by CrO2 grains and the surface structure becomes polycrystalline film. The average grain size on the surface of the CrO2 films deposited for 1 h, 2 h and 5 h is about 190 nm, 300 nm and 470 nm. The X-ray diffraction pattern reveals that the rutile CrO2 film has been synthesized on the TiO2 nanotube array template. The CrO2 films show large magnetoresistance (MR) at low temperature, which should originate from spin-dependent tunneling through grain boundaries between CrO2 grains. And the tunneling mechanism of the CrO2 films can be well described by the fluctuation-induced tunneling (FIT) model. The CrO2 film deposited for 2 h shows insulator behavior from 5 k to 300 K, but the CrO2 film deposited for 5 h shows insulator-metal transition around 140 K. The reason is briefly discussed.

Fast diffusion of silver in TiO2 nanotube arrays

PubMed Central

Zhang, Wanggang; Liu, Yiming; Zhou, Diaoyu; Wang, Hui

2016-01-01

Summary Using magnetron sputtering and heat treatment, Ag@TiO2 nanotubes are prepared. The effects of heat-treatment temperature and heating time on the evolution of Ag nanofilms on the surface of TiO2 nanotubes and microstructure of Ag nanofilms are investigated by X-ray diffraction, field emission scanning electron microscopy, and transmission electron microscopy. Ag atoms migrate mainly on the outmost surface of the TiO2 nanotubes, and fast diffusion of Ag atoms is observed. The diffusivity for the diffusion of Ag atoms on the outmost surface of the TiO2 nanotubes at 400 °C is 6.87 × 10−18 m2/s, which is three orders of magnitude larger than the diffusivities for the diffusion of Ag through amorphous TiO2 films. The activation energy for the diffusion of Ag atoms on the outmost surface of the TiO2 nanotubes in the temperature range of 300 to 500 °C is 157 kJ/mol, which is less than that for the lattice diffusion of Ag and larger than that for the grain boundary diffusion. The diffusion of Ag atoms leads to the formation of Ag nanocrystals on the outmost surface of TiO2 nanotubes. Probably there are hardly any Ag nanocrystals formed inside the TiO2 nanotubes through the migration of Ag. PMID:27547630

Fast fabrication of long TiO2 nanotube array with high photoelectrochemical property on flexible stainless steel.

PubMed

Tao, Jie; Wu, Tao; Gao, Peng

2012-03-01

Oriented highly ordered long TiO2 nanotube array films with nanopore structure and high photoelectrochemical property were fabricated on flexible stainless steel substrate (50 microm) by anodization treatment of titanium thin films in a short time. The samples were characterized by means of field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD) and photoelectrochemical methods, respectively. The results showed that Ti films deposited at the condition of 0.7 Pa Ar pressure and 96 W sputtering power at room temperature was uniform and dense with good homogeneity and high crystallinity. The voltage and the anodization time both played significant roles in the formation of TiO2 nanopore-nanotube array film. The optimal voltage was 60 V and the anodization time is less than 30 min by anodizing Ti films in ethylene glycerol containing 0.5% (w) NH4F and 3% (w) H2O. The growth rate of TiO2 nanotube array was as high as 340 nm/min. Moreover, the photocurrent-potential curves, photocurrent response curves and electrochemical impedance spectra results indicated that the TiO2 nanotube array film with the nanoporous structure exhibited a better photo-response ability and photoelectrochemical performance than the ordinary TiO2 nanotube array film. The reason is that the nanoporous structure on the surface of the nanotube array can separate the photo electron-hole pairs more efficiently and completely than the tubular structure.

Conical islands of TiO2 nanotube arrays in the photoelectrode of dye-sensitized solar cells.

PubMed

Kim, Woong-Rae; Park, Hun; Choi, Won-Youl

2015-01-01

Ti conical island structures were fabricated using photolithography and the reactive ion etching method. The resulting conical island structures were anodized in ethylene glycol solution containing 0.25 wt% NH4F and 2 vol% H2O, and conical islands composed of TiO2 nanotubes were successfully formed on the Ti foils. The conical islands composed of TiO2 nanotubes were employed in photoelectrodes for dye-sensitized solar cells (DSCs). DSC photoelectrodes based on planar Ti structures covered with TiO2 nanotubes were also fabricated as a reference. The short-circuit current (J sc) and efficiency of DSCs based on the conical island structures were higher than those of the reference samples. The efficiency of DSCs based on the conical island structures reached up to 1.866%. From electrochemical impedance spectroscopy and open-circuit voltage (V oc) decay measurements, DSCs based on the conical island structures exhibited a lower charge transfer resistance at the counter cathode and a longer electron lifetime at the interface of the photoelectrode and electrolyte compared to the reference samples. The conical island structure was very effective at improving performances of DSCs based on TiO2 nanotubes. Graphical AbstractConical islands of TiO2 nanotube arrays are fabricated by an anodizing process with Ti protruding dots which have a conical shape. The conical islands are applied for use in DSC photoelectrodes. DSCs based on the conical islands of TiO2 nanotube arrays have the potential to achieve higher efficiency levels compared to DSCs based on normal TiO2 nanotubes and TiO2 nanoparticles because the conical islands of TiO2 nanotube arrays enlarge the surface area for dye adsorption.

Cr(VI) removal on visible light active TiO2 nanotube arrays

NASA Astrophysics Data System (ADS)

Bashirom, Nurulhuda; Zulkifli, Muhammad Afiq; Subagja, Subagja; Kian, Tan Wai; Matsuda, Atsunori; Lockman, Zainovia

2018-05-01

Self-organized TiO2 nanotube (TNT) arrays were fabricated by anodic oxidation of titanium foil in three different fluoride electrolytes: ethylene glycol (EG), glycerol, and sodium sulfate (Na2SO4) at different voltage and anodization time. In these electrolytes, the TNTs were produced in ˜ 2 µm long, but at the different diameter. The size of inner diameter can be arranged from the largest to the smallest value in the order of glycerol > EG > Na2SO4. Crystallization of the TNTs by annealing was led to the formation of anatase-TiO2. The sample can be activated under natural sunlight for reduction of hexavalent chromium, Cr(VI) into trivalent chromium, Cr(III). The reduction was thought to occur via synergistic reactions between adsorption and photoreduction. The result demonstrates 100 % of Cr(VI) removal efficiency over the TNTs grown in EG after 120 min. Whereas, only 48 % and 45 % of Cr(VI) can be removed over the TNTs fabricated in glycerol and Na2SO4, respectively. High photocatalytic activity of the TNTs-EG can be attributed to high crystallinity of anatase phase, enhanced Cr(VI) adsorption, and less electron-hole recombination due to smoother tube walls.

N- and C-Modified TiO2 Nanotube Arrays: Enhanced Photoelectrochemical Properties and Effect of Nanotubes Length on Photoconversion Efficiency

PubMed Central

Mohamed, Ahmed El Ruby; Barghi, Shahzad

2018-01-01

In this investigation, a new, facile, low cost and environmental-friendly method was introduced to fabricate N- and C-modified TiO2 nanotube arrays by immersing the as-anodized TiO2 nanotube arrays (TNTAs) in a urea aqueous solution with mechanical agitation for a short time and keeping the TNTAs immersed in the solution for 6 h at room temperature. Then, the TNTAs were annealed at different temperatures. The produced N-, C-modified TNTAs were characterized using FESEM, EDX, XRD, XPS, UV-Vis diffuse reflectance spectra. Modified optical properties with narrow band gap energy, Eg, of 2.65 eV was obtained after annealing the modified TNTAs at 550 °C. Modified TNTAs showed enhanced photoelectochemical performance. Photoconversion efficiency (PCE) was increased from 4.35% for pristine (unmodified) TNTAs to 5.18% for modified TNTAs, an increase of 19%. Effect of nanotubes length of modified TNTAs on photoelectrochemical performance was also studied. Photocurrent density and PCE were increased by increasing nanotube length with a maximum PCE of 6.38% for nanotube length of 55 µm. This high PCE value was attributed to: band gap reduction due to C- and N-modification of TNTAs surface, increased surface area of long TNTAs compared with short TNTAs, investigated in previous studies. PMID:29597248

Preparation and UV-Vis photodegradation of gaseous benzene by TiO2 nanotube arrays supporting V2O5 nanoparticles

NASA Astrophysics Data System (ADS)

Zhao, Chunxia; Song, Yanbao; Yang, Yunxia; Chen, Wen; Li, Xiaoyu; Wang, Zongsheng

2015-07-01

TiO2-based catalysts effective in visible radiation for eliminating organic pollutants have attracted intense research activity as a future generation photocatalytic material. However, recombination of electron-hole pairs through trapping/de-trapping as well as the disadvantages of recycling and separation/filtration of powders lead to the limitation of powder TiO2 materials. TiO2 nanotube array films supporting vanadium pentoxide nanoparticles (VTNTs) were synthesized by electrophoresis deposition method with the prepared TiO2 nanotube arrays as the cathode and V2O5 sol as the electrolyte. The results indicate that the formation of Ti-O-V bonds and intimate interaction between host-guest interfaces help to enhance the hybrids’ photodegradation activity of gaseous benzene. Importantly, hybrid film catalysts prepared with 0.05 mol/L V2O5 sol for 10 min electrophoresis deposition perform a 98% conversion rate of benzene and 1028.8 mg/m3CO2 production in 80 min under UV-Vis irradiation.

Reconstruction of TiO2/MnO2-C nanotube/nanoflake core/shell arrays as high-performance supercapacitor electrodes

NASA Astrophysics Data System (ADS)

Xiong, Qinqin; Zheng, Cun; Chi, Hongzhong; Zhang, Jun; Ji, Zhenguo

2017-02-01

Construction of electrodes with fast reaction kinetics is of great importance for achieving advanced supercapacitors. Herein we report a facile combined synthetic strategy with atomic layer deposition (ALD) and electrodeposition to rationally fabricate nanotube/nanoflake core/shell arrays. ALD-TiO2 nanotubes are used as the skeleton core for assembly of electrodeposited MnO2-C nanoflake shells forming a core/shell structure. Highly porous architecture and good electrical conductivity are combined in this unique core/shell structure, resulting in fast ion/electron transfer. In tests of electrochemical performance, the TiO2/MnO2-C core/shell arrays are characterized as cathode for asymmetric supecapacitors and exhibit high specific capacitance (880 F g-1 at 2.5 A g-1), excellent rate properties (735 F g-1 at 30 A g-1) and good long-term cycling stability (94.3% capacitance retention after 20 000 cycles). The proposed electrode construction strategy is favorable for fabrication of other advanced supercapacitor electrodes.

Reconstruction of TiO2/MnO2-C nanotube/nanoflake core/shell arrays as high-performance supercapacitor electrodes.

PubMed

Xiong, Qinqin; Zheng, Cun; Chi, Hongzhong; Zhang, Jun; Ji, Zhenguo

2017-02-03

Construction of electrodes with fast reaction kinetics is of great importance for achieving advanced supercapacitors. Herein we report a facile combined synthetic strategy with atomic layer deposition (ALD) and electrodeposition to rationally fabricate nanotube/nanoflake core/shell arrays. ALD-TiO 2 nanotubes are used as the skeleton core for assembly of electrodeposited MnO 2 -C nanoflake shells forming a core/shell structure. Highly porous architecture and good electrical conductivity are combined in this unique core/shell structure, resulting in fast ion/electron transfer. In tests of electrochemical performance, the TiO 2 /MnO 2 -C core/shell arrays are characterized as cathode for asymmetric supecapacitors and exhibit high specific capacitance (880 F g -1 at 2.5 A g -1 ), excellent rate properties (735 F g -1 at 30 A g -1 ) and good long-term cycling stability (94.3% capacitance retention after 20 000 cycles). The proposed electrode construction strategy is favorable for fabrication of other advanced supercapacitor electrodes.

The TAED/H2O2/NaHCO3 system as an approach to low-temperature and near-neutral pH bleaching of cotton.

PubMed

Long, Xiaoxia; Xu, Changhai; Du, Jinmei; Fu, Shaohai

2013-06-05

A low-temperature and near-neutral pH bleaching system was conceived for cotton by incorporating TAED, H2O2 and NaHCO3. The TAED/H2O2/NaHCO3 system was investigated and optimized for bleaching of cotton using a central composite design (CCD) combined with response surface methodology (RSM). CCD experimental data were fitted to create a response surface quadratic model (RSQM) describing the degree of whiteness of bleached cotton fabric. Analysis of variance for the RSQM revealed that temperature was the most significant variable, followed by [TAED] and time, while [NaHCO3] was insignificant. An effective system was conducted by adding 5.75 g L(-1) TAED together with H2O2 and NaHCO3 at a molar ratio of 1:2.4:2.8 and applied to bleaching of cotton at 70 °C for 40 min. Compared to a commercial bleaching method, the TAED/H2O2/NaHCO3 system provided cotton with comparable degree of whiteness, slightly inferior water absorbency and acceptable dyeability, but had competitive advantage in protecting cotton from severe chemical damage in bleaching. Copyright © 2013 Elsevier Ltd. All rights reserved.

Enhancement in photo-electrochemical efficiency by reducing recombination rate in branched TiO2 nanotube array on functionalizing with ZnO micro crystals

NASA Astrophysics Data System (ADS)

Boda, Muzaffar Ahmad; Ashraf Shah, Mohammad

2018-06-01

In this study, branched TiO2 nanotube array were fabricated through electrochemical anodization process at constant voltage using third generation electrolyte. On account of morphological advantage, these nanotubes shows significant enhancement in photo-electrochemical property than compact or conventional titania nanotube array. However, their photo-electrochemical efficiency intensifies on coating with ZnO micro-crystals. ZnO coated branched TiO2 nanotube array shows a photocurrent density of 27.8 mA cm‑2 which is 1.55 times the photocurrent density (17.2 mA cm‑2) shown by bare branched titania nanotubes. The significant enhancement in photocurrent density shown by the resulting ZnO/TiO2 hybrid structure is attributed to suppression in electron–hole recombination phenomenon by offering smooth pathway to photo generated excitons on account of staggered band edge positions in individual semiconductors.

Ag2S/CdS/TiO2 Nanotube Array Films with High Photocurrent Density by Spotting Sample Method.

PubMed

Sun, Hong; Zhao, Peini; Zhang, Fanjun; Liu, Yuliang; Hao, Jingcheng

2015-12-01

Ag2S/CdS/TiO2 hybrid nanotube array films (Ag2S/CdS/TNTs) were prepared by selectively depositing a narrow-gap semiconductor-Ag2S (0.9 eV) quantum dots (QDs)-in the local domain of the CdS/TiO2 nanotube array films by spotting sample method (SSM). The improvement of sunlight absorption ability and photocurrent density of titanium dioxide (TiO2) nanotube array films (TNTs) which were obtained by anodic oxidation method was realized because of modifying semiconductor QDs. The CdS/TNTs, Ag2S/TNTs, and Ag2S/CdS/TNTs fabricated by uniformly depositing the QDs into the TNTs via the successive ionic layer adsorption and reaction (SILAR) method were synthesized, respectively. The X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray photoelectron spectrum (XPS) results demonstrated that the Ag2S/CdS/TNTs prepared by SSM and other films were successfully prepared. In comparison with the four films of TNTs, CdS/TNTs, Ag2S/TNTs, and Ag2S/CdS/TNTs by SILAR, the Ag2S/CdS/TNTs prepared by SSM showed much better absorption capability and the highest photocurrent density in UV-vis range (320~800 nm). The cycles of local deposition have great influence on their photoelectric properties. The photocurrent density of Ag2S/CdS/TNTs by SSM with optimum deposition cycles of 6 was about 37 times that of TNTs without modification, demonstrating their great prospective applications in solar energy utilization fields.

(Na{sub x}k{sub 1−x}){sub 2}Ta{sub 4}O{sub 11}(x≈0.93) piezoelectric phase from the transformation of Ta{sub 2}O{sub 5} thin films of monoclinic structure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Le Gallic, M., E-mail: Marie.Le-Gallic@grenoble-inp.fr; Roussel, H.

2013-04-15

A phase of trigonal structure has been reported in previous articles to be piezoelectric with a very high longitudinal d{sub 33} coefficient of several thousand pm/V (J. Solid State Chem. 184 (2011) 2023, 2033). It was observed in Ta{sub 2}O{sub 5} thin films and assumed to be the result of a reversible monoclinic–trigonal phase transition. However, new investigations are reported because the cell parameters of this phase are actually very close to those of the natrotantite mineral Na{sub 2}Ta{sub 4}O{sub 11}. From analyses by X-ray energy dispersive spectroscopy (XEDS), the chemical composition of this trigonal phase corresponds to (Na{sub x}K{submore » 1−x}){sub 2}Ta{sub 4}O{sub 11} with x≈0.93. The origin of sodium, potassium, iron and oxygen atoms is found to be due to a pollution coming from alumina crucibles used for thermal treatments. Knowing both atomic structures Ta{sub 2}O{sub 5} and Na{sub 2}Ta{sub 4}O{sub 11} and their structural relationships, observed by high resolution transmission electron microscopy (HRTEM), the mechanism of the reaction of transformation is re-examined and discussed. This mechanism implies that Ta{sup 5+} vacancies likely exist in monoclinic structures of tantalum oxide and that electrical neutrality could be due to incorporated proton H{sup +} instead of O{sup 2−} vacancies or Ta{sup 5+} interstitials. - Graphical abstract: (a, b) TEM images of interfaces between Ta{sub 2}O{sub 5} monoclinic and (Na{sub 0.93}K{sub 0.07}){sub 2}Ta{sub 4}O{sub 11} trigonal phases where it appears that the ratio of periods for the transformation monoclinic-to-trigonal is 3/2 (c, d) corresponding schema of the reaction of transformation, (a, c) viewed along the zone axes [010]{sub o}∥[1{sup ¯}21{sup ¯}]{sub R} and (b, d) along the zone axes [100]{sub o}∥[101{sup ¯}]{sub R}. Highlights: ► The formation of a piezoelectric phase in Ta{sub 2}O{sub 5} thin films, reported in previous articles, is re-examined. ► Its composition is

Cobalt-Doped Black TiO2 Nanotube Array as a Stable Anode for Oxygen Evolution and Electrochemical Wastewater Treatment.

PubMed

Yang, Yang; Kao, Li Cheng; Liu, Yuanyue; Sun, Ke; Yu, Hongtao; Guo, Jinghua; Liou, Sofia Ya Hsuan; Hoffmann, Michael R

2018-05-04

TiO 2 has long been recognized as a stable and reusable photocatalyst for water splitting and pollution control. However, it is an inefficient anode material in the absence of photoactivation due to its low electron conductivity. To overcome this limitation, a series of conductive TiO 2 nanotube array electrodes have been developed. Even though nanotube arrays are effective for electrochemical oxidation initially, deactivation is often observed within a few hours. To overcome the problem of deactivation, we have synthesized cobalt-doped Black-TiO 2 nanotube array (Co-Black NTA) electrodes that are stable for more than 200 h of continuous operation in a NaClO 4 electrolyte at 10 mA cm -2 . Using X-ray photoelectron spectroscopy, X-ray absorption spectroscopy, electron paramagnetic resonance spectroscopy, and DFT simulations, we are able to show that bulk oxygen vacancies (O v ) are the primary source of the enhanced conductivity of Co-Black. Cobalt doping both creates and stabilizes surficial oxygen vacancies, O v , and thus prevents surface passivation. The Co-Black electrodes outperform dimensionally stable IrO 2 anodes (DSA) in the electrolytic oxidation of organic-rich wastewater. Increasing the loading of Co leads to the formation of a CoO x film on top of Co-Black electrode. The CoO x /Co-Black composite electrode was found to have a lower OER overpotential (352 mV) in comparison to a DSA IrO 2 (434 mV) electrode and a stability that is greater than 200 h in a 1.0 M KOH electrolyte at a current density of 10 mA cm -2 .

Polyoxometalate-modified TiO2 nanotube arrays photoanode materials for enhanced dye-sensitized solar cells

NASA Astrophysics Data System (ADS)

Liu, Ran; Sun, Zhixia; Zhang, Yuzhuo; Xu, Lin; Li, Na

2017-10-01

In this work, we prepared for the first time the TiO2 nanotube arrays (TNAs) photoanode with polyoxometalate(POMs)-modified TiO2 electron-transport layer for improving the performance of zinc phthalocyanine(ZnPc)-sensitized solar cells. The as-prepared POMs/TNAs/ZnPc composite photoanode exhibited higher photovoltaic performances than the TNAs/ZnPc photoanode, so that the power conversion efficiency of the solar cell device based on the POMs/TNAs/ZnPc photoanode displayed a notable improvement of 45%. These results indicated that the POMs play a key role in reducing charge recombination in phthalocyanine-sensitized solar cells, together with TiO2 nanotube arrays being helpful for electron transport. The mechanism of the performance improvement was demonstrated by the measurements of electrochemical impedance spectra and open-circuit voltage decay curves. Although the resulting performance is still below that of the state-of-the-art dye-sensitized solar cells, this study presents a new insight into improving the power conversion efficiency of phthalocyanine-sensitized solar cells via polyoxometalate-modified TiO2 nanotube arrays photoanode.

Highly efficient and completely flexible fiber-shaped dye-sensitized solar cell based on TiO2 nanotube array

NASA Astrophysics Data System (ADS)

Lv, Zhibin; Yu, Jiefeng; Wu, Hongwei; Shang, Jian; Wang, Dan; Hou, Shaocong; Fu, Yongping; Wu, Kai; Zou, Dechun

2012-02-01

A type of highly efficient completely flexible fiber-shaped solar cell based on TiO2 nanotube array is successfully prepared. Under air mass 1.5G (100 mW cm-2) illumination conditions, the photoelectric conversion efficiency of the solar cell approaches 7%, the highest among all fiber-shaped cells based on TiO2 nanotube arrays and the first completely flexible fiber-shaped DSSC. The fiber-shaped solar cell demonstrates good flexibility, which makes it suitable for modularization using weaving technologies.A type of highly efficient completely flexible fiber-shaped solar cell based on TiO2 nanotube array is successfully prepared. Under air mass 1.5G (100 mW cm-2) illumination conditions, the photoelectric conversion efficiency of the solar cell approaches 7%, the highest among all fiber-shaped cells based on TiO2 nanotube arrays and the first completely flexible fiber-shaped DSSC. The fiber-shaped solar cell demonstrates good flexibility, which makes it suitable for modularization using weaving technologies. Electronic supplementary information (ESI) available. See DOI: 10.1039/c2nr11532h

Transparent TiO 2 nanotube array photoelectrodes prepared via two-step anodization

DOE PAGES

Kim, Jin Young; Zhu, Kai; Neale, Nathan R.; ...

2014-04-04

Two-step anodization of transparent TiO 2 nanotube arrays has been demonstrated with aid of a Nb-doped TiO 2 buffer layer deposited between the Ti layer and TCO substrate. Enhanced physical adhesion and electrochemical stability provided by the buffer layer has been found to be important for successful implementation of the two-step anodization process. As a result, with the proposed approach, the morphology and thickness of NT arrays could be controlled very precisely, which in turn, influenced their optical and photoelectrochemical properties.

Cobalt-Doped Black TiO2 Nanotube Array as a Stable Anode for Oxygen Evolution and Electrochemical Wastewater Treatment

PubMed Central

2018-01-01

TiO2 has long been recognized as a stable and reusable photocatalyst for water splitting and pollution control. However, it is an inefficient anode material in the absence of photoactivation due to its low electron conductivity. To overcome this limitation, a series of conductive TiO2 nanotube array electrodes have been developed. Even though nanotube arrays are effective for electrochemical oxidation initially, deactivation is often observed within a few hours. To overcome the problem of deactivation, we have synthesized cobalt-doped Black-TiO2 nanotube array (Co-Black NTA) electrodes that are stable for more than 200 h of continuous operation in a NaClO4 electrolyte at 10 mA cm–2. Using X-ray photoelectron spectroscopy, X-ray absorption spectroscopy, electron paramagnetic resonance spectroscopy, and DFT simulations, we are able to show that bulk oxygen vacancies (Ov) are the primary source of the enhanced conductivity of Co-Black. Cobalt doping both creates and stabilizes surficial oxygen vacancies, Ov, and thus prevents surface passivation. The Co-Black electrodes outperform dimensionally stable IrO2 anodes (DSA) in the electrolytic oxidation of organic-rich wastewater. Increasing the loading of Co leads to the formation of a CoOx film on top of Co-Black electrode. The CoOx/Co-Black composite electrode was found to have a lower OER overpotential (352 mV) in comparison to a DSA IrO2 (434 mV) electrode and a stability that is greater than 200 h in a 1.0 M KOH electrolyte at a current density of 10 mA cm–2. PMID:29755829

Visible-light-driven photoelectrochemical and photocatalytic performances of Cr-doped SrTiO3/TiO2 heterostructured nanotube arrays.

PubMed

Jiao, Zhengbo; Chen, Tao; Xiong, Jinyan; Wang, Teng; Lu, Gongxuan; Ye, Jinhua; Bi, Yingpu

2013-01-01

Well-aligned TiO2 nanotube arrays have become of increasing significance because of their unique highly ordered array structure, high specific surface area, unidirectional charge transfer and transportation features. However, their poor visible light utilization as well as the high recombination rate of photoexcited electron-hole pairs greatly limited their practical applications. Herein, we demonstrate the fabrication of visible-light-responsive heterostructured Cr-doped SrTiO3/TiO2 nanotube arrays by a simple hydrothermal method, which facilitate efficient charge separation and thus improve the photoelectrochemical as well as photocatalytic performances.

Na2O-Al2O3 system: Activity of Na2O in (α + β)- and (β + β)-alumina

NASA Astrophysics Data System (ADS)

Kale, G. M.

1992-12-01

The activity of Na2O in a biphasic mixture of (α + β)-alumina has been measured in the temperature range of 700 to 1100 K using the solid-state galvanic cell: 11663_2007_Article_BF02656462_TeX2GIFE1.gif _{(1:1)}^{Pt,CO_2 + O_2 /Na_2 CO_3 /(α + β ) - alumin a//(Y_2 O_3 )ZrO_2 //In + In_2 O_3 ,Ta,Pt} Similarly, the activity of Na2O in a (β + β’’)-alumina two-phase mixture has been measured between 700 and 1100 K employing the galvanic cell: 11663_2007_Article_BF02656462_TeX2GIFE2.gif _{(1:1)}^{Pt,CO_2 + O_2 /Na_2 CO_3 /(β + β ) - alumin a//(Y_2 O_3 )ZrO_2 //In + In_2 O_3 ,Ta,Pt} The reversible electromotive force (emf ) of both the cells was found to vary linearly with temperature over the entire temperature range of measurement. From the measured reversible emf and auxiliary thermodynamic data for In2O2, Na2O, CO2 and Na2CO3 reported in the literature, the temperature dependence of the logarithm of activity of Na2O in (α + β)-alumina is obtained: 11663_2007_Article_BF02656462_TeX2GIFE3.gif log α _{Na_2 O} (α + β ) = 1.85 - 14,750/T(K)( ± 0.015)(700 ≤slant T ≤slant 1100) For (β + β'’)-alumina, 11663_2007_Article_BF02656462_TeX2GIFE4.gif log α _{Na_2 O} (β + β ) = 3.9 - 13,000/T(K)( ± 0.015)(700 ≤slant T ≤slant 1100)

Chemical modification of TiO2 nanotube arrays for label-free optical biosensing applications

NASA Astrophysics Data System (ADS)

Terracciano, Monica; Galstyan, Vardan; Rea, Ilaria; Casalino, Maurizio; De Stefano, Luca; Sbervegleri, Giorgio

2017-10-01

In this study, we have fabricated TiO2 nanotube arrays by the potentiostatic anodic oxidation of Ti foils in fluoride-containing electrolyte and explored them as versatile devices for biosensing applications. TiO2 nanotubes have been chemically modified in order to bind Protein A as a specific target analyte for the optical biosensing. The obtained structures have been characterized by scanning electron microscopy, Fourier transform infrared spectroscopy, water contact angle, fluorescence microscopy, spectroscopic reflectometry and photoluminescence. Investigations show that the prepared TiO2 nanotubes, 2.5 μm long and 75 nm thick, can be easily and efficiently bio-modified, and the obtained structures are strongly photoluminescent, thus suitable for the label-free biosensing applications in the range of μM, due to their peculiar optical properties.

Fully Depleted Ti-Nb-Ta-Zr-O Nanotubes: Interfacial Charge Dynamics and Solar Hydrogen Production.

PubMed

Chiu, Yi-Hsuan; Lai, Ting-Hsuan; Chen, Chun-Yi; Hsieh, Ping-Yen; Ozasa, Kazunari; Niinomi, Mitsuo; Okada, Kiyoshi; Chang, Tso-Fu Mark; Matsushita, Nobuhiro; Sone, Masato; Hsu, Yung-Jung

2018-05-01

Poor kinetics of hole transportation at the electrode/electrolyte interface is regarded as a primary cause for the mediocre performance of n-type TiO 2 photoelectrodes. By adopting nanotubes as the electrode backbone, light absorption and carrier collection can be spatially decoupled, allowing n-type TiO 2 , with its short hole diffusion length, to maximize the use of the available photoexcited charge carriers during operation in photoelectrochemical (PEC) water splitting. Here, we presented a delicate electrochemical anodization process for the preparation of quaternary Ti-Nb-Ta-Zr-O mixed-oxide (denoted as TNTZO) nanotube arrays and demonstrated their utility in PEC water splitting. The charge-transfer dynamics for the electrodes was investigated using time-resolved photoluminescence, electrochemical impedance spectroscopy, and the decay of open-circuit voltage analysis. Data reveal that the superior photoactivity of TNTZO over pristine TiO 2 originated from the introduction of Nd, Ta, and Zr elements, which enhanced the amount of accessible charge carriers, modified the electronic structure, and improved the hole injection kinetics for expediting water splitting. By modulating the water content of the electrolyte employed in the anodization process, the wall thickness of the grown TNTZO nanotubes can be reduced to a size smaller than that of the depletion layer thickness, realizing a fully depleted state for charge carriers to further advance the PEC performance. Hydrogen evolution tests demonstrate the practical efficacy of TNTZO for realizing solar hydrogen production. Furthermore, with the composition complexity and fully depleted band structure, the present TNTZO nanotube arrays may offer a feasible and universal platform for the loading of other semiconductors to construct a sophisticated heterostructure photoelectrode paradigm, in which the photoexcited charge carriers can be entirely utilized for efficient solar-to-fuel conversion.

Structure and physical properties of EuTa{sub 2}O{sub 6} tungsten bronze polymorph

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kolodiazhnyi, T., E-mail: kolodiazhnyi.taras@nims.go.jp; Sakurai, H.; Vasylkiv, O.

A tetragonal tungsten bronze (TTB) polymorph of EuTa{sub 2}O{sub 6} was prepared and analyzed. EuTa{sub 2}O{sub 6} crystallizes in the centrosymmetric Pnam space group (with unit cell: a = 12.3693, b = 12.4254, and c = 7.7228 Å) isomorphous with orthorhombic β-SrTa{sub 2}O{sub 6}. In contrast to early reports, we see no evidence of deviation from paramagnetic Curie-Weiss behavior among the Eu{sup 2+} 4f{sup 7}spins in EuTa{sub 2}O{sub 6} down to 2 K. Dielectric constant shows a broad peak at ca. 50 K with dielectric dispersion resembling diffuse phase transition. The relaxation time, however, follows a simple (non-freezing) thermally activated process with an activation energy of 92 meV and anmore » attempt frequency of f{sub 0} = 5.79 × 10{sup 12 }Hz. A thermal conductivity of EuTa{sub 2}O{sub 6} shows a low-temperature (T ≈ 30 K) “plateau” region reminiscent of a glass-like behaviour in Nb-based TTB compounds. This behaviour can be attributed to the loosely bound Eu{sup 2+} ions occupying large tricapped trigonal prismatic sites in the EuTa{sub 2}O{sub 6} structure.« less

Efficient Visible-Light-Driven Z-Scheme Overall Water Splitting Using a MgTa2O(6-x)N(y)/TaON Heterostructure Photocatalyst for H2 Evolution.

PubMed

Chen, Shanshan; Qi, Yu; Hisatomi, Takashi; Ding, Qian; Asai, Tomohiro; Li, Zheng; Ma, Su Su Khine; Zhang, Fuxiang; Domen, Kazunari; Li, Can

2015-07-13

An (oxy)nitride-based heterostructure for powdered Z-scheme overall water splitting is presented. Compared with the single MgTa2O(6-x)N(y) or TaON photocatalyst, a MgTa2O(6-x)N(y)/TaON heterostructure fabricated by a simple one-pot nitridation route was demonstrated to effectively suppress the recombination of carriers by efficient spatial charge separation and decreased defect density. By employing Pt-loaded MgTa2O(6-x)N(y)/TaON as a H2-evolving photocatalyst, a Z-scheme overall water splitting system with an apparent quantum efficiency (AQE) of 6.8% at 420 nm was constructed (PtO(x)-WO3 and IO3(-)/I(-) pairs were used as an O2-evolving photocatalyst and a redox mediator, respectively), the activity of which is circa 7 or 360 times of that using Pt-TaON or Pt-MgTa2O(6-x)N)y) as a H2-evolving photocatalyst, respectively. To the best of our knowledge, this is the highest AQE among the powdered Z-scheme overall water splitting systems ever reported. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Hydrogenated TiO2 nanotube arrays for supercapacitors.

PubMed

Lu, Xihong; Wang, Gongming; Zhai, Teng; Yu, Minghao; Gan, Jiayong; Tong, Yexiang; Li, Yat

2012-03-14

We report a new and general strategy for improving the capacitive properties of TiO(2) materials for supercapacitors, involving the synthesis of hydrogenated TiO(2) nanotube arrays (NTAs). The hydrogenated TiO(2) (denoted as H-TiO(2)) were obtained by calcination of anodized TiO(2) NTAs in hydrogen atmosphere in a range of temperatures between 300 to 600 °C. The H-TiO(2) NTAs prepared at 400 °C yields the largest specific capacitance of 3.24 mF cm(-2) at a scan rate of 100 mV s(-1), which is 40 times higher than the capacitance obtained from air-annealed TiO(2) NTAs at the same conditions. Importantly, H-TiO(2) NTAs also show remarkable rate capability with 68% areal capacitance retained when the scan rate increase from 10 to 1000 mV s(-1), as well as outstanding long-term cycling stability with only 3.1% reduction of initial specific capacitance after 10,000 cycles. The prominent electrochemical capacitive properties of H-TiO(2) are attributed to the enhanced carrier density and increased density of hydroxyl group on TiO(2) surface, as a result of hydrogenation. Furthermore, we demonstrate that H-TiO(2) NTAs is a good scaffold to support MnO(2) nanoparticles. The capacitor electrodes made by electrochemical deposition of MnO(2) nanoparticles on H-TiO(2) NTAs achieve a remarkable specific capacitance of 912 F g(-1) at a scan rate of 10 mV s(-1) (based on the mass of MnO(2)). The ability to improve the capacitive properties of TiO(2) electrode materials should open up new opportunities for high-performance supercapacitors. © 2012 American Chemical Society

Controllable Synthesis of TiO2@Fe2O3 Core-Shell Nanotube Arrays with Double-Wall Coating as Superb Lithium-Ion Battery Anodes

PubMed Central

Zhong, Yan; Ma, Yifan; Guo, Qiubo; Liu, Jiaqi; Wang, Yadong; Yang, Mei; Xia, Hui

2017-01-01

Highlighted by the safe operation and stable performances, titanium oxides (TiO2) are deemed as promising candidates for next generation lithium-ion batteries (LIBs). However, the pervasively low capacity is casting shadow on desirable electrochemical behaviors and obscuring their practical applications. In this work, we reported a unique template-assisted and two-step atomic layer deposition (ALD) method to achieve TiO2@Fe2O3 core-shell nanotube arrays with hollow interior and double-wall coating. The as-prepared architecture combines both merits of the high specific capacity of Fe2O3 and structural stability of TiO2 backbone. Owing to the nanotubular structural advantages integrating facile strain relaxation as well as rapid ion and electron transport, the TiO2@Fe2O3 nanotube arrays with a high mass loading of Fe2O3 attained desirable capacity of ~520 mA h g−1, exhibiting both good rate capability under uprated current density of 10 A g−1 and especially enhanced cycle stability (~450 mA h g−1 after 600 cycles), outclassing most reported TiO2@metal oxide composites. The results not only provide a new avenue for hybrid core-shell nanotube formation, but also offer an insight for rational design of advanced electrode materials for LIBs. PMID:28098237

3D Ta/TaO x /TiO2/Ti synaptic array and linearity tuning of weight update for hardware neural network applications

NASA Astrophysics Data System (ADS)

Wang, I.-Ting; Chang, Chih-Cheng; Chiu, Li-Wen; Chou, Teyuh; Hou, Tuo-Hung

2016-09-01

The implementation of highly anticipated hardware neural networks (HNNs) hinges largely on the successful development of a low-power, high-density, and reliable analog electronic synaptic array. In this study, we demonstrate a two-layer Ta/TaO x /TiO2/Ti cross-point synaptic array that emulates the high-density three-dimensional network architecture of human brains. Excellent uniformity and reproducibility among intralayer and interlayer cells were realized. Moreover, at least 50 analog synaptic weight states could be precisely controlled with minimal drifting during a cycling endurance test of 5000 training pulses at an operating voltage of 3 V. We also propose a new state-independent bipolar-pulse-training scheme to improve the linearity of weight updates. The improved linearity considerably enhances the fault tolerance of HNNs, thus improving the training accuracy.

Formation of TiO2 nanotube arrays in KOH added fluoride-ethylene glycol (EG) electrolyte and its photoelectrochemical response

NASA Astrophysics Data System (ADS)

Nyein, Nyein; Lockman, Zainovia; Matsuda, Astunori; Kawamura, Go; Tan, Wai Kian; Oo, Than Zaw

2016-07-01

In this study, highly ordered TiO2 nanotube arrays were prepared by anodic oxidation of titanium foil in fluoride -EG electrolyte containing a small amount of potassium hydroxide, KOH at 60 V for 30 min. This electrolyte resulted in the formation of long nanotubes with an average length of 10 µm and diameter of 170 nm. For comparison, TiO2 nanotubes anodized in H2O added EG electrolyte which produces short nanotubes with an average tube length of 5 µm and diameter of 170 nm. It appears that the addition of KOH into the fluoride EG electrolyte accelerated the formation of the TiO2 nanotubes as it is believed that the chemical dissolution at the tips of the nanotubes is suppressed. Highly ordered TiO2 nanotubes anodized in KOH added EG electrolyte exhibited the photocurrent density of 2 mA/cm2, which is significantly higher than H2O added sample (1.5 mA/cm2).

Photo-reduced Cu/CuO nanoclusters on TiO2 nanotube arrays as highly efficient and reusable catalyst

NASA Astrophysics Data System (ADS)

Jin, Zhao; Liu, Chang; Qi, Kun; Cui, Xiaoqiang

2017-01-01

Non-noble metal nanoparticles are becoming more and more important in catalysis recently. Cu/CuO nanoclusters on highly ordered TiO2 nanotube arrays are successfully developed by a surfactant-free photoreduction method. This non-noble metal Cu/CuO-TiO2 catalyst exhibits excellent catalytic activity and stability for the reduction of 4-nitrophenol (4-NP) to 4-aminophenol (4-AP) with the presence of sodium borohydride (NaBH4). The rate constant of this low-cost Cu/CuO based catalyst is even higher than that of the noble metal nanoparticles decorated on the same TiO2 substrate. The conversion efficiency remains almost unchanged after 7 cycles of recycling. The recycle process of this Cu/CuO-TiO2 catalyst supported by Ti foil is very simple and convenient compared with that of the common powder catalysts. This catalyst also exhibited great catalytic activity to other organic dyes, such as methylene blue (MB), rhodamine B (RhB) and methyl orange (MO). This highly efficient, low-cost and easily reusable Cu/CuO-TiO2 catalyst is expected to be of great potential in catalysis in the future.

Highly efficient and completely flexible fiber-shaped dye-sensitized solar cell based on TiO2 nanotube array.

PubMed

Lv, Zhibin; Yu, Jiefeng; Wu, Hongwei; Shang, Jian; Wang, Dan; Hou, Shaocong; Fu, Yongping; Wu, Kai; Zou, Dechun

2012-02-21

A type of highly efficient completely flexible fiber-shaped solar cell based on TiO(2) nanotube array is successfully prepared. Under air mass 1.5G (100 mW cm(-2)) illumination conditions, the photoelectric conversion efficiency of the solar cell approaches 7%, the highest among all fiber-shaped cells based on TiO(2) nanotube arrays and the first completely flexible fiber-shaped DSSC. The fiber-shaped solar cell demonstrates good flexibility, which makes it suitable for modularization using weaving technologies. This journal is © The Royal Society of Chemistry 2012

Substitution and Redox Chemistry of [Bu(4)N](2)[Ta(6)Cl(12)(OSO(2)CF(3))(6)].

PubMed

Prokopuk, Nicholas; Kennedy, Vance O.; Stern, Charlotte L.; Shriver, Duward F.

1998-09-21

Two sequential electrochemical reductions occur for the cluster anion [Ta(6)Cl(12)(OSO(2)CF(3))(6)](2)(-) at 0.89 and 0.29 V vs Ag/AgCl, with the generation [Ta(6)Cl(12)(OSO(2)CF(3))(6)](3)(-) and [Ta(6)Cl(12)(OSO(2)CF(3))(6)](4)(-). Chemical reduction of [Ta(6)Cl(12)(OSO(2)CF(3))(6)](2)(-) by ferrocene produces [Ta(6)Cl(12)(OSO(2)CF(3))(6)](3)(-) with the concomitant shift of the nu(SO(2)) stretch from 1002 to 1018 cm(-)(1). Reaction of [Bu(4)N](2)[Ta(6)Cl(12)(OSO(2)CF(3))(6)] (1) with [Bu(4)N]X (X = Cl, Br, I, NCS) occurs by reduction and substitution, yielding [Bu(4)N](3)[Ta(6)Cl(12)X(6)], where the clusters with X = Br, I, and NCS are new. Spectroscopic (IR and UV-vis) evidence indicates that the reduced cluster core {Ta(6)Cl(12)}(2+) is produced in reaction mixtures of 1 with the halide and pseudohalide ions. Concomitant substitution of the triflate ligands of 1 by X(-) occurs and the rates for the overall reduction and substitution increase in the order X(-) = Cl(-) < Br(-) < NCS(-) < I(-) < CN(-). Reduction of 1 with ferrocene followed by addition of [Bu(4)N]O(2)CCH(3) produces the new cluster [Ta(6)Cl(12)(O(2)CCH(3))(6)](3)(-) isolated as the tetrabutylammonium salt. Cyclic voltammetry and UV-vis spectroscopy on the new clusters [Bu(4)N](3)[Ta(6)Cl(12)X(6)] (X = Br, I, NCS, and O(2)CCH(3)) are reported. Crystal data for [Bu(4)N](3)[Ta(6)Cl(12)(NCS)(6)].CH(2)Cl(2): monoclinic, space group, P2(1)/c (No. 14); a = 25.855(6) Å, b = 21.843(6) Å, c = 16.423(3) Å; beta = 100.03(2) degrees; V = 9133(3) Å(3); Z = 4.

A study of nitrogen behavior in the formation of Ta/TaN and Ti/TaN alloyed metal electrodes on SiO2 and HfO2 dielectrics

NASA Astrophysics Data System (ADS)

Gassilloud, R.; Maunoury, C.; Leroux, C.; Piallat, F.; Saidi, B.; Martin, F.; Maitrejean, S.

2014-04-01

We studied Ta, TaN, and sub-stoichiometric TaNx electrodes (obtained by nitrogen redistribution in Ta/TaN or Ti/TaN bilayers) deposited on thermal SiO2 and HfO2/IL (0.8 nm SiO2 IL, i.e., interlayer) stacks. Effective work-functions (WF) were extracted on MOS capacitor structures on SiO2 bevelled insulator of 4.2 eV for pure Ta, 4.6 eV for TaN, and 4.3 eV for sub-stoichiometric TaNx. This intermediate WF value is explained by TaN nitrogen redistribution with reactive Ta or Ti elements shifting the gate work-function toward the Si conduction band. The same electrodes deposited on an HfO2/IL dielectric showed different behavior: First, the Ta/HfO2/IL stack shows a +200 meV WF increase (towards the Si valence band) compared to the SiO2 dielectric stack. This increase is explained by the well-known HfO2/IL dipole formation. Second, in contrast to electrodes deposited on SiO2, sub-stoichiometric TaNx/HfO2 is found to have a lower WF (4.3 eV), than pure Ta on HfO2 (4.4 eV). This inversion in work-function behavior measured on SiO2 vs. HfO2 is explained by the nitrogen redistribution in Ta/TaN bilayer together with diffusion of nitrogen through the HfO2 layer, leading to Si-N formation which prevents dipole formation at the HfO2/IL interface.

Heterostructured ZnFe2O4/Fe2TiO5/TiO2 Composite Nanotube Arrays with an Improved Photocatalysis Degradation Efficiency Under Simulated Sunlight Irradiation

NASA Astrophysics Data System (ADS)

Xiong, Kun; Wang, Kunzhou; Chen, Lin; Wang, Xinqing; Fan, Qingbo; Courtois, Jérémie; Liu, Yuliang; Tuo, Xianguo; Yan, Minhao

2018-03-01

To improve the visible light absorption and photocatalytic activity of titanium dioxide nanotube arrays (TONTAs), ZnFe2O4 (ZFO) nanocrystals were perfused into pristine TONTA pipelines using a novel bias voltage-assisted perfusion method. ZFO nanocrystals were well anchored on the inner walls of the pristine TONTAs when the ZFO suspensions (0.025 mg mL-1) were kept under a 60 V bias voltage for 1 h. After annealing at 750 °C for 2 h, the heterostructured ZFO/Fe2TiO5 (FTO)/TiO2 composite nanotube arrays were successfully obtained. Furthermore, Fe3+ was reduced to Fe2+ when solid solution reactions occurred at the interface of ZFO and the pristine TONTAs. Introducing ZFO significantly enhanced the visible light absorption of the ZFO/FTO/TONTAs relative to that of the annealed TONTAs. The coexistence of type I and staggered type II band alignment in the ZFO/FTO/TONTAs facilitated the separation of photogenerated electrons and holes, thereby improving the efficiency of the ZFO/FTO/TONTAs for photocatalytic degradation of methylene blue when irradiated with simulated sunlight. [Figure not available: see fulltext.

Augmented Photoelectrochemical Efficiency of ZnO/TiO2 Nanotube Heterostructures

NASA Astrophysics Data System (ADS)

Boda, Muzaffar Ahmad; Shah, Mohammad Ashraf

2017-11-01

ZnO/TiO2 nanotube heterostructures have been fabricated by electrodeposition of ZnO microcrystals over electrochemically anodized TiO2 nanotube arrays. The resulting ZnO/TiO2 nanotube heterostructures showed enhanced photocurrent density of 5.72 mA cm-2, about 1.5 times the value of 3.68 mA cm-2 shown by bare compact TiO2 nanotubes. This enhanced photocurrent density of the ZnO/TiO2 nanotube heterostructures is due to high electron mobility in the ZnO crystals, thereby decreasing the electron-hole recombination process, good interfacial quality between the ZnO and TiO2 structures, and a proposed smooth charge-transfer mechanism due to band bending at the interface. The morphological features of the as-prepared heterostructures were determined by field-emission scanning electron microscopy (FESEM). The crystallinity and phase purity of the samples were confirmed by x-ray diffraction (XRD) analysis. The light absorption properties of the prepared samples were investigated by ultraviolet-visible diffuse reflectance spectroscopy (UV-Vis DRS). The photoelectrochemical efficiency of bare and ZnO-modified TiO2 nanotube heterostructures was determined by electrochemical analyzer.

Enhanced photo-assistant electrocatalysis of anodization TiO2 nanotubes via surrounded surface decoration with MoS2 for hydrogen evolution reaction

NASA Astrophysics Data System (ADS)

Tian, Yuanyuan; Song, Ye; Dou, Meiling; Ji, Jing; Wang, Feng

2018-03-01

A highly ordered TiO2 nanotube array covered with MoS2 is fabricated through a facile anodization of a metallic Ti followed by electrochemical deposition approach. The morphologies characterization of v-TiO2@MoS2 indicate that a whole scale of 1D TiO2nanotube uniformly covered with the MoS2 layer inside and outside, and the pathway inside the TiO2nanotube is kept flow-through. The as-synthesized v-TiO2@MoS2 hybrid exhibits higher efficient and stable visible light activities than that of either pure TiO2 nanotubes or nv-TiO2@MoS2 nanostructures. By electrochemical measurements such as linear sweep voltammetry(LSV) and electrochemical impedance spectroscope (EIS) under light illumination or in dark, we find that the v-TiO2@MoS2hybrid shows markedly enhanced photoelectrochemical performance. Furthermore, we compare the electrocatalytic behavior of v-TiO2@MoS2under illumination in H2SO4/Lactic acid within Na2S/NaSO3 solution. The results show that the photo-assistant electrocatalytic activity in acidic environment is much better than in alkaline environment. The highly directional and orthogonal separation of charge carriers between TiO2 nanotubes and MoS2 layer, together with maximally exposed MoS2 edges, light harvesting and junctions formed between TiO2 and MoS2 is supposed to be mainly responsible for the enhanced photo-assistant electrocatalytic activity of v-TiO2@MoS2.

Exploring doxorubicin localization in eluting TiO2 nanotube arrays through fluorescence correlation spectroscopy analysis.

PubMed

De Santo, Ilaria; Sanguigno, Luigi; Causa, Filippo; Monetta, Tullio; Netti, Paolo A

2012-11-07

Drug elution properties of TiO(2) nanotube arrays have been largely investigated by means of solely macroscopic observations. Controversial elution performances have been reported so far and a clear comprehension of these phenomena is still missing as a consequence of a lack of molecular investigation methods. Here we propose a way to discern drug elution properties of nanotubes through the evaluation of drug localization by Fluorescence Correlation Spectroscopy (FCS) analysis. We verified this method upon doxorubicin elution from differently loaded TiO(2) nanotubes. Diverse elution profiles were obtained from nanotubes filled by soaking and wet vacuum impregnation methods. Impregnated nanotubes controlled drug diffusion up to thirty days, while soaked samples completed elution in seven days. FCS analysis of doxorubicin motion in loaded nanotubes clarified that more than 90% of drugs dwell preferentially in inter-nanotube spaces in soaked samples due to decorrelation in a 2D fashion, while a 97% fraction of molecules showed 1D mobility ascribable to displacements along the nanotube vertical axis of wet vacuum impregnated nanotubes. The diverse drug localizations inferred from FCS measurements, together with distinct drug-surface interaction strengths resulting from diverse drug filling techniques, could explain the variability in elution kinetics.

Synthesis of highly ordered TiO2 nanotube in malonic acid solution by anodization.

PubMed

Ryu, Won Hee; Park, Chan Jin; Kwon, Hyuk Sang

2008-10-01

We synthesized TiO2 nanotube array by anodizing in a solution of malonic acid (HOOCCH2COOH) and NH4F, and analyzed the morphology of the nanotube using scanning electron microscopy (SEM). The morphology of TiO2 nanotube was largely affected by anodizing time, anodizing voltage, and malonic acid concentration. With increasing the anodizing voltage from 5 V to 20 V, the diameter of TiO2 nanotube was increased from about 20 nm to 110 nm and its length from about 10 nm to 700 nm. In addition, the length of TiO2 nanotube was increased with increasing anodizing time up to 6 h at 20 V. We obtained the longest and the most highly ordered nanotube structure when anodizing Ti in a solution of 0.5 wt% NH4F and 1 M malonic acid at 20 V for 6 h.

Effect of Size-Dependent Thermal Instability on Synthesis of Zn2 SiO4-SiOx Core–Shell Nanotube Arrays and Their Cathodoluminescence Properties

PubMed Central

2010-01-01

Vertically aligned Zn2SiO4-SiOx(x < 2) core–shell nanotube arrays consisting of Zn2SiO4-nanoparticle chains encapsulated into SiOx nanotubes and SiOx-coated Zn2SiO4 coaxial nanotubes were synthesized via one-step thermal annealing process using ZnO nanowire (ZNW) arrays as templates. The appearance of different nanotube morphologies was due to size-dependent thermal instability and specific melting of ZNWs. With an increase in ZNW diameter, the formation mechanism changed from decomposition of “etching” to Rayleigh instability and then to Kirkendall effect, consequently resulting in polycrystalline Zn2SiO4-SiOx coaxial nanotubes, single-crystalline Zn2SiO4-nanoparticle-chain-embedded SiOx nanotubes, and single-crystalline Zn2SiO4-SiOx coaxial nanotubes. The difference in spatially resolved optical properties related to a particular morphology was efficiently documented by means of cathodoluminescence (CL) spectroscopy using a middle-ultraviolet emission at 310 nm from the Zn2SiO4 phase. PMID:20672064

From GaN to ZnGa(2)O(4) through a low-temperature process: nanotube and heterostructure arrays.

PubMed

Lu, Ming-Yen; Zhou, Xiang; Chiu, Cheng-Yao; Crawford, Samuel; Gradečak, Silvija

2014-01-22

We demonstrate a method to synthesize GaN-ZnGa2O4 core-shell nanowire and ZnGa2O4 nanotube arrays by a low-temperature hydrothermal process using GaN nanowires as templates. Transmission electron microscopy and X-ray photoelectron spectroscopy results show that a ZnGa2O4 shell forms on the surface of GaN nanowires and that the shell thickness is controlled by the time of the hydrothermal process and thus the concentration of Zn ions in the solution. Furthermore, ZnGa2O4 nanotube arrays were obtained by depleting the GaN core from GaN-ZnGa2O4 core-shell nanowire arrays during the reaction and subsequent etching with HCl. The GaN-ZnGa2O4 core-shell nanowires exhibit photoluminescence peaks centered at 2.60 and 2.90 eV attributed to the ZnGa2O4 shell, as well as peaks centered at 3.35 and 3.50 eV corresponding to the GaN core. We also demonstrate the synthesis of GaN-ZnGa2O4 heterojunction nanowires by a selective formation process as a simple route toward development of heterojunction nanodevices for optoelectronic applications.

Visible light-harvesting of TiO2 nanotubes array by pulsed laser deposited CdS

NASA Astrophysics Data System (ADS)

Bjelajac, Andjelika; Djokic, Veljko; Petrovic, Rada; Socol, Gabiel; Mihailescu, Ion N.; Florea, Ileana; Ersen, Ovidiu; Janackovic, Djordje

2014-08-01

Titanium dioxide (TiO2) nanotubes arrays, obtained by anodization technique and annealing, were decorated with CdS using pulsed laser deposition method. Their structural, morphological and chemical characterization was carried out by electron microscopy in scanning (SEM) and transmission (TEM) modes, combined with energy dispersive spectroscopy (EDS) and electron energy loss spectroscopy (EELS). It was demonstrated that the quantity of deposited CdS can be controlled by varying the number of laser pulses. The chemical mapping of the elements of interest was performed using the energy filtered mode of the electron microscope. The results showed that pulse laser deposition is an adequate technique for deposition of CdS inside and between 100 nm wide TiO2 nanotubes. The diffuse reflectance spectroscopy investigation of selected samples proved that the absorption edge of the prepared CdS/TiO2 nanocomposites is significantly extended to the visible range. The corresponding band gaps were determinated from the Tauc plot of transformed Kubelka-Munk function. The band gap reduction of TiO2 nanotubes by pulsed laser deposition of CdS was put in evidence.

Morphology modulation of SrTiO3/TiO2 heterostructures for enhanced photoelectrochemical performance.

PubMed

Jiao, Zhengbo; Chen, Tao; Yu, Hongchao; Wang, Teng; Lu, Gongxuan; Bi, Yingpu

2014-04-01

Design and fabrication of nanoscale semiconductors with regulatable morphology or structure has attracted tremendous interest due to the dependency relationship between properties and architectures. Two types of SrTiO3/TiO2 nanocomposites with different morphologies and structures have been fabricated by controlling the kinetics of hydrothermal reactions. One is TiO2 nanotube arrays densely wrapped by SrTiO3 film and the other is SrTiO3 nanospheres distributed on the top region of TiO2 nanotube arrays, which has been firstly fabricated. It has been found that the photoelectrochemical performances of these heterostructures are crucially dominated by their architectures. Heterostructured SrTiO3/TiO2 nanotube arrays were fabricated by traditional method in the absence of NaOH and they exhibited higher photoelectrochemical performance than pure TiO2 nanotube arrays. However, the compact SrTiO3 coating film on the sidewalls of TiO2 nanotube arrays could inevitably destroy the tubular structures of TiO2 and thus go against the vectorial transport of electrons. Interestingly, when excess NaOH was added into the growth solution, SrTiO3 nanospheres would be rationally grafted on the top of TiO2 nanotube arrays, which could preserve the tubular structures of TiO2, and thus further improve the photoelectrochemical performance. Copyright © 2013 Elsevier Inc. All rights reserved.

Morphological evolution of TiO2 nanotube arrays with lotus-root-shaped nanostructure

NASA Astrophysics Data System (ADS)

Yu, Dongliang; Song, Ye; Zhu, Xufei; Yang, Ruiquan; Han, Aijun

2013-07-01

TiO2 nanotube arrays (TNAs) with lotus-root-shaped nanostructure have been fabricated by a modified two-step electrochemical anodization method. In the present work, different morphologies formed under different anodizing voltages are investigated in detail by field-emission scanning electron microscope. The results show that the concaves left by the first-step anodization can guide the uniform growth of TNAs in some degree as the second-step anodizing voltage is the same with that in the first step, however, when lower voltages are adopted in the second-step anodization, no guidance can be achieved, and different morphological TNAs with lotus-root-shaped nanostructure are fabricated. And we find that the nanotube diameters are directly proportional to the applied voltage in the second-step anodization. Furthermore, a possible mechanism for the growth of the TiO2 nanotubes with the special morphology is proposed for the first time, which depends on both the oxygen bubble mold and the viscous flow of the barrier oxide from the pore base to the pore wall.

Confined NaAlH4 nanoparticles inside CeO2 hollow nanotubes towards enhanced hydrogen storage.

PubMed

Gao, Qili; Xia, Guanglin; Yu, Xuebin

2017-10-05

NaAlH 4 has been widely regarded as a potential hydrogen storage material due to its favorable thermodynamics and high energy density. The high activation energy barrier and high dehydrogenation temperature, however, significantly hinder its practical application. In this paper, CeO 2 hollow nanotubes (HNTs) prepared by a simple electrospinning technique are adopted as functional scaffolds to support NaAlH 4 nanoparticles (NPs) towards advanced hydrogen storage performance. The nanoconfined NaAlH 4 inside CeO 2 HNTs, synthesized via the infiltration of molten NaAlH 4 into the CeO 2 HNTs under high hydrogen pressure, exhibited significantly improved dehydrogenation properties compared with both bulk and ball-milled CeO 2 HNTs-catalyzed NaAlH 4 . The onset dehydrogenation temperature of the NaAlH 4 @CeO 2 composite was reduced to below 100 °C, with only one main dehydrogenation peak appearing at 130 °C, which is 120 °C and 50 °C lower than for its bulk counterpart and for the ball-milled CeO 2 HNTs-catalyzed NaAlH 4 , respectively. Moreover, ∼5.09 wt% hydrogen could be released within 30 min at 180 °C, while only 1.6 wt% hydrogen was desorbed from the ball-milled NaAlH 4 under the same conditions. This significant improvement is mainly attributed to the synergistic effects contributed by the CeO 2 HNTs, which could act as not only a structural scaffold to fabricate and confine the NaAlH 4 NPs, but also as an effective catalyst to enhance the hydrogen storage performance of NaAlH 4 .

Pd-MnO2 nanoparticles/TiO2 nanotube arrays (NTAs) photo-electrodes photo-catalytic properties and their ability of degrading Rhodamine B under visible light.

PubMed

Thabit, Mohamed; Liu, Huiling; Zhang, Jian; Wang, Bing

2017-10-01

Pd-MnO 2 /TiO 2 nanotube arrays (NTAs) photo-electrodes were successfully fabricated via anodization and electro deposition subsequently; the obtained Pd-MnO 2 /TiO 2 NTAs photo electrodes were analyzed by scanning electron microscopy (SEM), X-ray diffraction (XRD) and characterized accordingly. Moreover, the light harvesting and absorption properties were investigated via ultraviolet-visible diffuse reflectance spectrum (DRS); photo degradation efficiency was investigated via analyzing the photo catalytic degradation of Rhodamine B under visible illumination (xenon light). The performed analyses illustrated that Pd-MnO 2 codoped particles were successfully deposited onto the surface of the TiO 2 nanotube arrays; DRS results showed significant improvement in visible light absorption which was between 400 and 700nm. Finally, the photo catalytic degradation efficiency results of the designated organic pollutant (Rhodamine B) illustrated a superior photocatalytic (PC) efficiency of approximately 95% compared to the bare TiO 2 NTAs, which only exhibited a photo catalytic degradation efficiency of approximately 61%, thus it indicated the significant enhancement of the light absorption properties of fabricated photo electrodes and their yield of OH radicals. Copyright © 2017. Published by Elsevier B.V.

TiO2 Nanotube Arrays: Fabricated by Soft-Hard Template and the Grain Size Dependence of Field Emission Performance

NASA Astrophysics Data System (ADS)

Yang, Xuxin; Ma, Pei; Qi, Hui; Zhao, Jingxin; Wu, Qiang; You, Jichun; Li, Yongjin

2017-11-01

Highly ordered TiO2 nanotube (TNT) arrays were successfully synthesized by the combination of soft and hard templates. In the fabrication of them, anodic aluminum oxide membranes act as the hard template while the self-assembly of polystyrene-block-poly(ethylene oxide) (PS-b-PEO) complexed with titanium-tetraisopropoxide (TTIP, the precursor of TiO2) provides the soft template to control the grain size of TiO2 nanotubes. Our results indicate that the field emission (FE) performance depends crucially on the grain size of the calcinated TiO2 which is dominated by the PS-b-PEO and its blending ratio with TTIP. The optimized sample (with the TTIP/PEO ratio of 3.87) exhibits excellent FE performances involving both a low turn-on field of 3.3 V/um and a high current density of 7.6 mA/cm2 at 12.7 V/μm. The enhanced FE properties can be attributed to the low effective work function (1.2 eV) resulted from the smaller grain size of TiO2.

Photoelectrochemical CdSe/TiO2 nanotube array microsensor for high-resolution in-situ detection of dopamine.

PubMed

Qin, Caidie; Bai, Xue; Zhang, Yue; Gao, Kai

2018-05-03

A photoelectrochemical wire microelectrode was constructed based on the use of a TiO 2 nanotube array with electrochemically deposited CdSe semiconductor. A strongly amplified photocurrent is generated on the sensor surface. The microsensor has a response in the 0.05-20 μM dopamine (DA) concentration range and a 16.7 μM detection limit at a signal-to-noise ratio of 3. Sensitivity, recovery and reproducibility of the sensor were validated by detecting DA in spiked human urine, and satisfactory results were obtained. Graphical abstract Schematic of a sensitive photoelectrochemical microsensor based on CdSe modified TiO 2 nanotube array. The photoelectrochemical microsensor was successfully applied to the determination of dopamine in urine samples.

YCrWO 6 : Polar and Magnetic Oxide with CaTa 2O 6 -Related Structure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Sun Woo; Emge, Thomas J.; Deng, Zheng

Here, a new polar and magnetic oxide, YCrWO 6, was successfully synthesized and characterized. YCrWO 6 crystallizes in polar orthorhombic space group Pna21 (no. 33) of edge-sharing dimers of CrO 6 and WO 6 octahedra, which are connected by corner-sharing to form a three-dimensional framework structure with Y 3+ cations located in the channels. The structure of YCrWO 6 is related to that of CaTa2O 6; however, the ordering of Cr 3+ and W 6+ in the octahedral sites breaks the inversion symmetry of the parent CaTa 2O 6 structure. X-ray absorption near edge spectroscopy of YCrWO 6 confirmed themore » oxidation state of Cr 3+ and W 6+. Temperature-dependent optical second harmonic generation measurements on YCrWO 6 confirmed the noncentrosymmetric character and evidenced a noncentrosymmetric-to-centrosymmetric phase transition above 800 °C. Piezoresponse force microscopy measurements on YCrWO 6 at room temperature show strong piezoelectric domains. Magnetic measurements of YCrWO 6 indicate antiferromagnetic order at T N of ~22 K with Weiss temperature of -34.66 K.« less

YCrWO 6 : Polar and Magnetic Oxide with CaTa 2O 6 -Related Structure

DOE PAGES

Kim, Sun Woo; Emge, Thomas J.; Deng, Zheng; ...

2018-01-05

Here, a new polar and magnetic oxide, YCrWO 6, was successfully synthesized and characterized. YCrWO 6 crystallizes in polar orthorhombic space group Pna21 (no. 33) of edge-sharing dimers of CrO 6 and WO 6 octahedra, which are connected by corner-sharing to form a three-dimensional framework structure with Y 3+ cations located in the channels. The structure of YCrWO 6 is related to that of CaTa2O 6; however, the ordering of Cr 3+ and W 6+ in the octahedral sites breaks the inversion symmetry of the parent CaTa 2O 6 structure. X-ray absorption near edge spectroscopy of YCrWO 6 confirmed themore » oxidation state of Cr 3+ and W 6+. Temperature-dependent optical second harmonic generation measurements on YCrWO 6 confirmed the noncentrosymmetric character and evidenced a noncentrosymmetric-to-centrosymmetric phase transition above 800 °C. Piezoresponse force microscopy measurements on YCrWO 6 at room temperature show strong piezoelectric domains. Magnetic measurements of YCrWO 6 indicate antiferromagnetic order at T N of ~22 K with Weiss temperature of -34.66 K.« less

One-Step Formation of WO3-Loaded TiO2 Nanotubes Composite Film for High Photocatalytic Performance

PubMed Central

Lee, Wai Hong; Lai, Chin Wei; Abd Hamid, Sharifah Bee

2015-01-01

High aspect ratio of WO3-loaded TiO2 nanotube arrays have been successfully synthesized using the electrochemical anodization method in an ethylene glycol electrolyte containing 0.5 wt% ammonium fluoride in a range of applied voltage of 10–40 V for 30 min. The novelty of this research works in the one-step formation of WO3-loaded TiO2 nanotube arrays composite film by using tungsten as the cathode material instead of the conventionally used platinum electrode. As compared with platinum, tungsten metal has lower stability, forming dissolved ions (W6+) in the electrolyte. The W6+ ions then move towards the titanium foil and form a coherent deposit on titanium foil. By controlling the oxidation rate and chemical dissolution rate of TiO2 during the electrochemical anodization, the nanotubular structure of TiO2 film could be achieved. In the present study, nanotube arrays were characterized using FESEM, EDAX, XRD, as well as Raman spectroscopy. Based on the results obtained, nanotube arrays with average pore diameter of up to 74 nm and length of 1.6 µm were produced. EDAX confirmed the presence of tungsten element within the nanotube arrays which varied in content from 1.06 at% to 3.29 at%. The photocatalytic activity of the nanotube arrays was then investigated using methyl orange degradation under TUV 96W UV-B Germicidal light irradiation. The nanotube with the highest aspect ratio, geometric surface area factor and at% of tungsten exhibited the highest photocatalytic activity due to more photo-induced electron-hole pairs generated by the larger surface area and because WO3 improves charge separation, reduces charge carrier recombination and increases charge carrier lifetime via accumulation of electrons and holes in the two different metal oxide semiconductor components.

An innovative approach to synthesize highly-ordered TiO2 nanotubes.

PubMed

Isimjan, Tayirjan T; Yang, D Q; Rohani, Sohrab; Ray, Ajay K

2011-02-01

An innovative route to prepare highly-ordered and dimensionally controlled TiO2 nanotubes has been proposed using a mild sonication method. The nanotube arrays were prepared by the anodization of titanium in an electrolyte containing 3% NH4F and 5% H2O in glycerol. It is demonstrated that the TiO2 nanostructures has two layers: the top layer is TiO2 nanowire and underneath is well-ordered TiO2 nanotubes. The top layer can easily fall off and form nanowires bundles by implementing a mild sonication after a short annealing time. We found that the dimensions of the TiO2 nanotubes were only dependent on the anodizing condition. The proposed technique may be extended to fabricate reproducible well-ordered TiO2 nanotubes with large area on other metals.

Development of Amperometric Glucose Biosensor Based on Prussian Blue Functionlized TiO2 Nanotube Arrays

PubMed Central

Gao, Zhi-Da; Qu, Yongfang; Li, Tongtong; Shrestha, Nabeen K.; Song, Yan-Yan

2014-01-01

Amperometric biosensors consisting of oxidase and peroxidase have attracted great attention because of their wide application. The current work demonstrates a novel approach to construct an enzymatic biosensor based on TiO2 nanotube arrays (TiNTs) as a supporting electrode on which Prussian Blue (PB)-an “artificial enzyme peroxidase” and enzyme glucose oxidase (GOx) have been immobilized. For this, PB nanocrystals are deposited onto the nanotube wall photocatalytically using the intrinsic photocatalytical property of TiO2, and the GOx/AuNPs nanobiocomposites are subsequently immobilized into the nanotubes via the electrodeposition of polymer. The resulting electrode exhibits a fast response, wide linear range, and good stability for glucose sensing. The sensitivity of the sensor is as high as 248 mA M−1 cm−2, and the detection limit is about 3.2 μM. These findings demonstrate a promising strategy to integrate enzymes and TiNTs, which could provide an analytical access to a large group of enzymes for bioelectrochemical applications including biosensors and biofuel cells. PMID:25367086

Partial nitrogen loss in SrTaO2N and LaTiO2N oxynitride perovskites

NASA Astrophysics Data System (ADS)

Chen, Daixi; Habu, Daiki; Masubuchi, Yuji; Torii, Shuki; Kamiyama, Takashi; Kikkawa, Shinichi

2016-04-01

SrTaO2N heated in a helium atmosphere began to release nitrogen of approximately 30 at% at 950 °C while maintaining the perovskite structure and its color changed from orange to dark green. Then it decomposed above 1200 °C to a black mixture of Sr1.4Ta0.6O2.73, Ta2N, and Sr5Ta4O15. The second decomposition was not clearly observed when SrTaO2N was heated in a nitrogen atmosphere below 1550 °C. After heating at 1500 °C for 3 h under a 0.2 MPa nitrogen atmosphere, the perovskite product became dark green and conductive. Structure refinement results suggested that the product was a mixture of tetragonal and cubic perovskites with a decreased ordering of N3-/O2-. The sintered body was changed to an n-type semiconductor after a partial loss of nitrogen to be reduced from the originally insulating SrTaO2N perovskite lattice. LaTiO2N was confirmed to have a similar cis-configuration of the TiO4N2 octahedron as that of TaO4N2 in SrTaO2N. It also released some of its nitrogen at 800 °C changing its color from brown to black and then decomposed to a mixture of LaTiO3, La2O3, and TiN at 1100 °C. These temperatures are lower than those in SrTaO2N.

Evolution of resistive switching mechanism through H2O2 sensing by using TaOx-based material in W/Al2O3/TaOx/TiN structure

NASA Astrophysics Data System (ADS)

Chakrabarti, Somsubhra; Panja, Rajeswar; Roy, Sourav; Roy, Anisha; Samanta, Subhranu; Dutta, Mrinmoy; Ginnaram, Sreekanth; Maikap, Siddheswar; Cheng, Hsin-Ming; Tsai, Ling-Na; Chang, Ya-Ling; Mahapatra, Rajat; Jana, Debanjan; Qiu, Jian-Tai; Yang, Jer-Ren

2018-03-01

Understanding of resistive switching mechanism through H2O2 sensing and improvement of switching characteristics by using TaOx-based material in W/Al2O3/TaOx/TiN structure have been reported for the first time. Existence of amorphous Al2O3/TaOx layer in the RRAM devices has been confirmed by transmission electron microscopy. By analyzing the oxidation states of Ta2+/Ta5+ for TaOx switching material and W0/W6+ for WOx layer at the W/TaOx interface through X-ray photoelectron spectroscopy and H2O2 sensing, the reduction-oxidation mechanism under Set/Reset occurs only in the TaOx layer for the W/Al2O3/TaOx/TiN structures. This leads to higher Schottky barrier height at the W/Al2O3 interface (0.54 eV vs. 0.46 eV), higher resistance ratio, and long program/erase endurance of >108 cycles with 100 ns pulse width at a low operation current of 30 μA. Stable retention of more than 104 s at 85 °C is also obtained. Using conduction mechanism and reduction-oxidation reaction, current-voltage characteristic has been simulated. Both TaOx and WOx membranes have high pH sensitivity values of 47.65 mV/pH and 49.25 mV/pH, respectively. Those membranes can also sense H2O2 with a low concentration of 1 nM in an electrolyte-insulator-semiconductor structure because of catalytic activity, while the Al2O3 membrane does not show sensing. The TaOx material in W/Al2O3/TaOx/TiN structure does not show only a path towards high dense, small size memory application with understanding of switching mechanism but also can be used for H2O2 sensors.

Non-metal doped TiO2 nanotube arrays for high efficiency photocatalytic decomposition of organic species in water

NASA Astrophysics Data System (ADS)

Szkoda, Mariusz; Siuzdak, Katarzyna; Lisowska-Oleksiak, Anna

2016-10-01

Titanium dioxide is a well-known photoactive semiconductor with a variety of possible applications. The procedure of pollutant degradation is mainly performed using TiO2 powder suspension. It can also be exploited an immobilized catalyst on a solid support. Morphology and chemical doping have a great influence on TiO2 activity under illumination. Here we compare photoactivity of titania nanotube arrays doped with non-metal atoms: nitrogen, iodine and boron applied for photodegradation of organic dye - methylene blue and terephtalic acid. The doped samples act as a much better photocatalyst in the degradation process of methylene blue and lead to the formation of much higher amount of hydroxyl radicals (•OH) than undoped TiO2 nanotube arrays. The use of a catalyst active under solar light illumination in the form of thin films on a stable substrate can be scaled up for an industrial application.

Magnetic properties of tapiolite (FeTa2O6); a quasi two-dimensional (2D) antiferromagnet

NASA Astrophysics Data System (ADS)

Chung, E. M. L.; Lees, M. R.; McIntyre, G. J.; Wilkinson, C.; Balakrishnan, G.; Hague, J. P.; Visser, D.; McK Paul, D.

2004-11-01

The possibilities of two-dimensional (2D) short-range magnetic correlations and frustration effects in the mineral tapiolite are investigated using bulk-property measurements and neutron Laue diffraction. In this study of the magnetic properties of synthetic single-crystals of tapiolite, we find that single crystals of FeTa2O6 order antiferromagnetically at TN = 7.95 ± 0.05 K, with extensive two-dimensional correlations existing up to at least 40 K. Although we find no evidence that FeTa2O6 is magnetically frustrated, hallmarks of two-dimensional magnetism observed in our single-crystal data include: (i) broadening of the susceptibility maximum due to short-range correlations, (ii) a spin-flop transition and (iii) lambda anomalies in the heat capacity and d(χT)/dT. Complementary neutron Laue diffraction measurements reveal 1D magnetic diffuse scattering extending along the c* direction perpendicular to the magnetic planes. This magnetic diffuse scattering, observed for the first time using the neutron Laue technique by VIVALDI, arises directly as a result of 2D short-range spin correlations.

Amorphization of Ta2O5 under swift heavy ion irradiation

NASA Astrophysics Data System (ADS)

Cusick, Alex B.; Lang, Maik; Zhang, Fuxiang; Sun, Kai; Li, Weixing; Kluth, Patrick; Trautmann, Christina; Ewing, Rodney C.

2017-09-01

Crystalline Ta2O5 powder is shown to amorphize under 2.2 GeV 197Au ion irradiation. Synchrotron X-ray diffraction (XRD), Raman spectroscopy, small-angle X-ray scattering (SAXS), and transmission electron microscopy (TEM) were used to characterize the structural transition from crystalline to fully-amorphous. Based on Rietveld refinement of XRD data, the initial structure is orthorhombic (P2mm) with a very large unit cell (a = 6.20, b = 40.29, c = 3.89 Å; V = 971.7 Å3), ideally containing 22 Ta and 55 O atoms. At a fluence of approximately 3 × 1011 ions/cm2, a diffuse amorphous background becomes evident, increasing in intensity relative to diffraction maxima until full amorphization is achieved at approximately 3 × 1012 ions/cm2. An anisotropic distortion of the orthorhombic structure occurred during the amorphization process, with an approximately constant unit cell volume. The amorphous phase fraction as a function of fluence was determined, yielding a trend that is consistent with a direct-impact model for amorphization. SAXS and TEM data indicate that ion tracks exhibit a core-shell morphology. Raman data show that the amorphous phase is comprised of TaO6 and TaO5 coordination-polyhedra in contrast to the TaO6 and TaO7 units that exist in crystalline Ta2O5. Analysis of Raman data shows that oxygen-deficiency increases with fluence, indicating a loss of oxygen that leads to an estimated final stoichiometry of Ta2O4.2 at a fluence of 1 × 1013 ions/cm2.

Ta2O5-memristor synaptic array with winner-take-all method for neuromorphic pattern matching

NASA Astrophysics Data System (ADS)

Truong, Son Ngoc; Van Pham, Khoa; Yang, Wonsun; Min, Kyeong-Sik; Abbas, Yawar; Kang, Chi Jung; Shin, Sangho; Pedrotti, Ken

2016-08-01

Pattern matching or pattern recognition is one of the elemental components that constitute the very complicated recalling and remembering process in human's brain. To realize this neuromorphic pattern matching, we fabricated and tested a 3 × 3 memristor synaptic array with the winner-take-all method in this research. In the measurement, first, the 3 × 3 Ta2O5 memristor array is programmed to store [LLL], [LHH], and [HLH], where L is a low-resistance state and H is a high-resistance state, at the 1st, 2nd, and 3rd columns, respectively. After the programming, three input patterns, [111], [100], and [010], are applied to the memristor synaptic array. From the measurement results, we confirm that all three input patterns can be recognized well by using a twin memristor crossbar with synaptic arrays. This measurement can be thought of as the first real verification of the twin memristor crossbar with memristive synaptic arrays for neuromorphic pattern recognition.

Synthesis and photoluminescence properties of Dy{sup 3+} doped white light emitting CdTa{sub 2}O{sub 6} phosphors

DOE Office of Scientific and Technical Information (OSTI.GOV)

İlhan, Mustafa, E-mail: mustafa.ilhan@marmara.edu.tr; Ekmekçi, Mete Kaan

2015-03-15

The undoped and CdTa{sub 2}O{sub 6}:Dy{sup 3+} (0.2≤x≤2.0 mol%) phosphors were synthesized at 1100 °C for 12 h by the conventional solid state reaction method. The synthesized CdTa{sub 2}O{sub 6}:Dy{sup 3+} phosphors were characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), Energy dispersive spectroscopy (EDS) and Photoluminescence (PL) analyses. The PL spectra showed the presence of excitation peaks between 310 and 440 nm due to the 4f–4f transitions of Dy{sup 3+}. The emission of Dy{sup 3+} ions at 353.0 nm excitation was observed at 487.1 nm (blue) and 577.8 nm (yellow) due to the {sup 4}F{sub 9/2}→{sup 6}H{sub 15/2}more » transitions and {sup 4}F{sub 9/2}→{sup 6}H{sub 13/2} transitions, respectively. The PL analysis results also showed that the emissions increase with the increasing Dy{sup 3+} ion content. The emissions increased with the doping concentration of up to 1 mol%, and above this level decreased due to concentration quenching effect. The CIE chromaticity color coordinates (x,y) of the CdTa{sub 2}O{sub 6}:Dy{sup 3+} phosphors were found to be in the white light region of the chromaticity diagram. - Graphical abstract: Emission spectra at λ{sub ex}=353.0 nm and CIE chromaticity coordinate diagram of CdTa{sub 2}O{sub 6}:Dy{sup 3+} phosphors. - Highlights: • Pure and CdTa{sub 2}O{sub 6}:Dy{sup 3+} was produced by solid state reaction method. • CdTa{sub 2}O{sub 6}:Dy{sup 3+} phosphor exhibited blue and yellow emissions due to the {sup 4}F{sub 9/2}→{sup 6}H{sub 15/2} and {sup 4}F{sub 9/2}→{sup 6}H{sub 13/2} transitions. • The CCT value for 1.0 mol% CdTa{sub 2}O{sub 6}:Dy{sup 3+} was 5133 K which was located in the cool white daylight region. • Dy{sup 3+} doped CdTa{sub 2}O{sub 6} phosphor has potential in the production of white LEDs.« less

H-TiO2/C/MnO2 nanocomposite materials for high-performance supercapacitors

NASA Astrophysics Data System (ADS)

Di, Jing; Fu, Xincui; Zheng, Huajun; Jia, Yi

2015-06-01

Functionalized TiO2 nanotube arrays with decoration of MnO2 nanoparticles (denoted as H-TiO2/C/MnO2) have been synthesized in the application of electrochemical capacitors. To improve both areal and gravimetric capacitance, hydrogen treatment and carbon coating process were conducted on TiO2 nanotube arrays. By scanning electron microscopy and X-ray photoelectron spectroscopy, it is confirmed that the nanostructure is formed by the uniform incorporation of MnO2 nanoparticles growing round the surface of the TiO2 nanotube arrays. Impedance analysis proves that the enhanced capacitive is due to the decrease of charge transfer resistance and diffusion resistance. Electrochemical measurements performed on this H-TiO2/C/MnO2 nanocomposite when used as an electrode material for an electrochemical pseudocapacitor presents quasi-rectangular shaped cyclic voltammetry curves up to 100 mV/s, with a large specific capacitance (SC) of 299.8 F g-1 at the current density of 0.5 A g-1 in 1 M Na2SO4 electrolyte. More importantly, the electrode also exhibits long-term cycling stability, only 13 % of SC loss after 2000 continuous charge-discharge cycles. Based on the concept of integrating active materials on highly ordered nanostructure framework, this method can be widely applied to the synthesis of high-performance electrode materials for energy storage.

Structure, photoluminescence and thermoluminescence study of a composite ZnTa2O6/ZnGa2O4 compound doped with Pr3+

NASA Astrophysics Data System (ADS)

Noto, L. L.; Shaat, S. K. K.; Poelman, D.; Dhlamini, M. S.; Mothudi, B. M.; Swart, H. C.

2016-05-01

The study of persistent luminescence is interesting for applications related to biological imaging, self-lit roads and security signs. Composite Pr-doped samples were prepared in one pot by solid chemical reaction at 1200 °C for 4 h. The X-ray diffraction patterns of the samples showed mixed phases which correspond to ZnGa2O4 and ZnTa2O6 phases. Interestingly, the secondary electron microscopy images showed that the surface morphology is composed of particles with different shapes: irregular, rhombus and rod shapes. The X-ray maps obtained using field emission scanning electron microscopy, confirmed that the irregular particles correspond to ZnTa2O6, and the rods correspond to ZnGa2O4. Red emission was observed from 1D2 → 3H4, 3P0 → 3H6, 3P0 → 3F2 and 1D2 → 3H5 transitions of Pr3+. The lifetime of the persistent luminescence was measured, and the corresponding trapping centres were investigated using thermoluminescence spectroscopy.

Enhanced photocatalytic activity of hydrogenated and vanadium doped TiO2 nanotube arrays grown by anodization of sputtered Ti layers

NASA Astrophysics Data System (ADS)

Motola, Martin; Satrapinskyy, Leonid; Čaplovicová, Mária; Roch, Tomáš; Gregor, Maroš; Grančič, Branislav; Greguš, Ján; Čaplovič, Ľubomír; Plesch, Gustav

2018-03-01

TiO2 nanotube (TiNT) arrays were grown on silicon substrate via electrochemical anodization of titanium films sputtered by magnetron. To improve the photocatalytic activity of arrays annealed in air (o-TiNT), doping of o-TiNT with vanadium was performed (o-V/TiNT). These non-doped and doped TiNT arrays were also hydrogenated in H2/Ar atmosphere to r-TiNT and r-V/TiNT samples, respectively. Investigation of composition and morphology by X-ray diffraction (XRD), electron microscopy (SEM and TEM) and X-ray photoelectron spectroscopy (XPS) showed the presence of well-ordered arrays of anatase nanotubes with average diameter and length of 100 nm and 1.3 μm, respectively. In both oxidized and reduced V-doped samples, vanadium is partly dissolved in the structure of anatase and partly deposited in form of oxide on the nanotube surface. Vanadium-doped and reduced samples exhibited higher rates in the photodegradation of organic dyes (compared to non-modified o-TiNT sample) and this is caused by limitation of electron-hole recombination rates and by shift of the energy gap into visible region. The photocatalytic activity was measured under UV, sunlight and visible irradiation, and the corresponding efficiency increased in the order (o-TiNT) < (r-TiNT) < (o-V/TiNT) < (r-V/TiNT). Under visible light, only r-TiNT and r-V/TiNT showed significant photocatalytic activity.

Laser stimulated third harmonic generation studies in ZnO-Ta2O5-B2O3 glass ceramics entrenched with Zn3Ta2O8 crystal phases

NASA Astrophysics Data System (ADS)

Siva Sesha Reddy, A.; Jedryka, J.; Ozga, K.; Ravi Kumar, V.; Purnachand, N.; Kityk, I. V.; Veeraiah, N.

2018-02-01

In this study zinc borate glasses doped with different concentrations Ta2O5 were synthesized and were crystallized by heat treatment for prolonged times. The samples were characterized by XRD, SEM, IR and Raman spectroscopy techniques. The SEM images of the crystallized samples have indicated that the samples contain randomly distributed crystal grains with size ∼1 μm entrenched in the residual amorphous phase. XRD studies have exhibited diffraction peaks identified as being due to the reflections from (1 1 1) planes of monoclinic Zn3Ta2O8 crystal phase that contains intertwined tetrahedral zinc and octahedral tantalate structural units. The concentration of such crystal phases in the bulk samples is observed to increase with increase of Ta2O5 up to 3.0 mol%. The IR and Raman spectroscopy studies have confirmed the presence of ZnO4 and TaO6 structural units in the glass network in addition to the conventional borate structural units. For measuring third harmonic generation (THG) in the samples, the samples were irradiated with 532 nm laser beam and the intensity of THG of probing beam (Nd:YAG λ = 1064 nm 20 ns pulsed laser (ω)) is measured as a function of fundamental beam power varying up to 200 J/m2. The intensity of THG is found to be increasing with increase of fundamental beam power and found to be the maximal for the glass crystallized with 3.0 mol% of Ta2O5. The intensity of THG of the ceramicized samples is found to be nearly 5 times higher with respect to that of pre-crystallized samples. The generation of 3ω is attributed to the perturbation/interaction between Zn3Ta2O8 anisotropic crystal grains and the incident probing beam.

X-ray photoelectron spectroscopy as detection tool for coordinated or uncoordinated fluorine atoms demonstrated on fluoride systems NaF, K2TaF7, K3TaF8, K2ZrF6, Na7Zr6F31 and K3ZrF7

NASA Astrophysics Data System (ADS)

Boča, Miroslav; Barborík, Peter; Mičušík, Matej; Omastová, Mária

2012-07-01

While systems K3TaF8 and K3ZrF7 were prepared by modified molten salt method modified wet pathway was used for reproducible preparation of Na7Zr6F31. Its congruently melting character was demonstrated on simultaneous TG/DSC measurements and XRD patterns. X-ray photoelectron spectroscopy was applied for identification of differently bonded fluorine atoms in series of compounds NaF, K2TaF7, K3TaF8, K2ZrF6, Na7Zr6F31 and K3ZrF7. Three different types of fluorine atoms were described qualitatively and quantitatively. Uncoordinated fluorine atoms (F-) provide signals at lowest binding energies, followed by signals from terminally coordinated fluorine atoms (M-F) and then bridging fluorine atoms (M-F-M) at highest energy. Based on XPS F 1s signals assigned to fluorine atoms in compounds with correctly determined structure it was suggested that fluorine atoms in K3ZrF7 have partially bridging character.

Hierarchical Oriented Anatase TiO2 Nanostructure arrays on Flexible Substrate for Efficient Dye-sensitized Solar Cells

PubMed Central

Wu, Wu-Qiang; Rao, Hua-Shang; Xu, Yang-Fan; Wang, Yu-Fen; Su, Cheng-Yong; Kuang, Dai-Bin

2013-01-01

The vertically oriented anatase single crystalline TiO2 nanostructure arrays (TNAs) consisting of TiO2 truncated octahedrons with exposed {001} facets or hierarchical TiO2 nanotubes (HNTs) consisting of numerous nanocrystals on Ti-foil substrate were synthesized via a two-step hydrothermal growth process. The first step hydrothermal reaction of Ti foil and NaOH leads to the formation of H-titanate nanowire arrays, which is further performed the second step hydrothermal reaction to obtain the oriented anatase single crystalline TiO2 nanostructures such as TiO2 nanoarrays assembly with truncated octahedral TiO2 nanocrystals in the presence of NH4F aqueous or hierarchical TiO2 nanotubes with walls made of nanocrystals in the presence of pure water. Subsequently, these TiO2 nanostructures were utilized to produce dye-sensitized solar cells in a backside illumination pattern, yielding a significant high power conversion efficiency (PCE) of 4.66% (TNAs, JSC = 7.46 mA cm−2, VOC = 839 mV, FF = 0.75) and 5.84% (HNTs, JSC = 10.02 mA cm−2, VOC = 817 mV, FF = 0.72), respectively. PMID:23715529

Giant strain with low cycling degradation in Ta-doped [Bi{sub 1/2}(Na{sub 0.8}K{sub 0.2}){sub 1/2}]TiO{sub 3} lead-free ceramics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Xiaoming; Tan, Xiaoli, E-mail: xtan@iastate.edu

2016-07-21

Non-textured polycrystalline [Bi{sub 1/2}(Na{sub 0.8}K{sub 0.2}){sub 1/2}](Ti{sub 1−x}Ta{sub x})O{sub 3} ceramics are fabricated and their microstructures and electrical properties are characterized. Transmission electron microscopy reveals the coexistence of the rhombohedral R3c and tetragonal P4bm phases in the form of nanometer-sized domains in [Bi{sub 1/2}(Na{sub 0.8}K{sub 0.2}){sub 1/2}]TiO{sub 3} with low Ta concentration. When the composition is x = 0.015, the electrostrain is found to be highly asymmetric under bipolar fields of ±50 kV/cm. A very large value of 0.62% is observed in this ceramic, corresponding to a large-signal piezoelectric coefficient d{sub 33}* of 1240 pm/V (1120 pm/V under unipolar loading). These values are greater thanmore » most previously reported lead-free polycrystalline ceramics and can even be compared with some lead-free piezoelectric single crystals. Additionally, this ceramic displays low cycling degradation; its electrostrain remains above 0.55% even after undergoing 10 000 cycles of ±50 kV/cm bipolar fields at 2 Hz. Therefore, Ta-doped [Bi{sub 1/2}(Na{sub 0.8}K{sub 0.2}){sub 1/2}]TiO{sub 3} ceramics show great potential for large displacement devices.« less

Betavoltaic Enhancement Using Defect-Engineered TiO2 Nanotube Arrays through Electrochemical Reduction in Organic Electrolytes.

PubMed

Ma, Yang; Wang, Na; Chen, Jiang; Chen, Changsong; San, Haisheng; Chen, Jige; Cheng, Zhengdong

2018-06-19

Utilizing high-energy beta particles emitted from radioisotopes for long-lifetime betavoltaic cells is a great challenge due to low energy conversion efficiency. Here, we report a betavoltaic cell fabricated using TiO 2 nanotube arrays (TNTAs) electrochemically reduced in ethylene glycol electrolyte (EGECR-TNTAs) for the enhancement of the betavoltaic effect. The electrochemical reduction of TNTAs using high cathodic bias in organic electrolytes is indeed a facile and effective strategy to induce in situ self-doping of oxygen vacancy (OV) and Ti 3+ defects. The black EGECR-TNTAs are highly stable with a significantly narrower band gap and higher electrical conductivity as well as UV-vis-NIR light absorption. A 20 mCi of 63 Ni betavoltaic cell based on the reduced TNTAs exhibits a maximum ECE of 3.79% with open-circuit voltage of 1.04 V, short-circuit current density of 117.5 nA cm -2 , and a maximum power density of 39.2 nW cm -2 . The betavoltaic enhancement can be attributed to the enhanced charge carrier transport and separation as well as multiple exciton generation of electron-hole pairs due the generation of OV and Ti 3+ interstitial bands below the conductive band of TiO 2.

Electrochemical synthesis of self-organized TiO2 crystalline nanotubes without annealing

NASA Astrophysics Data System (ADS)

Giorgi, Leonardo; Dikonimos, Theodoros; Giorgi, Rossella; Buonocore, Francesco; Faggio, Giuliana; Messina, Giacomo; Lisi, Nicola

2018-03-01

This work demonstrates that upon anodic polarization in an aqueous fluoride-containing electrolyte, TiO2 nanotube array films can be formed with a well-defined crystalline phase, rather than an amorphous one. The crystalline phase was obtained avoiding any high temperature annealing. We studied the formation of nanotubes in an HF/H2O medium and the development of crystalline grains on the nanotube wall, and we found a facile way to achieve crystalline TiO2 nanotube arrays through a one-step anodization. The crystallinity of the film was influenced by the synthesis parameters, and the optimization of the electrolyte composition and anodization conditions (applied voltage and time) were carried out. For comparison purposes, crystalline anatase TiO2 nanotubes were also prepared by thermal treatment of amorphous nanotubes grown in an organic bath (ethylene glycol/NH4F/H2O). The morphology and the crystallinity of the nanotubes were studied by field emission gun-scanning electron microscopy (FEG-SEM) and Raman spectroscopy, whereas the electrochemical and semiconducting properties were analyzed by means of linear sweep voltammetry, impedance spectroscopy, and Mott-Schottky plots. X-ray photoelectron spectroscopy (XPS) and ultraviolet photoelectron spectroscopy (UPS) allowed us to determine the surface composition and the electronic structure of the samples and to correlate them with the electrochemical data. The optimal conditions to achieve a crystalline phase with high donor concentration are defined.

Visible Light Assisted Photocatalytic Hydrogen Generation by Ta 2O 5/Bi 2O 3, TaON/Bi 2O 3, and Ta 3N 5/Bi 2O 3 Composites

DOE PAGES

Adhikari, Shiba; Hood, Zachary D.; More, Karren Leslie; ...

2015-06-15

Composites comprised of two semiconducting materials with suitable band gaps and band positions have been reported to be effective at enhancing photocatalytic activity in the visible light region of the electromagnetic spectrum. Here, we report the synthesis, complete structural and physical characterizations, and photocatalytic performance of a series of semiconducting oxide composites. UV light active tantalum oxide (Ta2O5) and visible light active tantalum oxynitride (TaON) and tantalum nitride (Ta 3N 5) were synthesized, and their composites with Bi 2O 3 were prepared in situ using benzyl alcohol as solvent. The composite prepared using equimolar amounts of Bi 2O 3 andmore » Ta 2O 5 leads to the formation of the ternary oxide, bismuth tantalate (BiTaO 4) upon calcination at 1000 °C. The composites and single phase bismuth tantalate formed were characterized by powder X-ray diffraction (PXRD), thermogravimetric analysis (TGA), Brunauer–Emmett–Teller (BET) surface area measurement, scanning electron microscopy (SEM), transmission electron microscopy (TEM), UV–Vis diffuse reflectance spectroscopy, and photoluminescence. The photocatalytic activities of the catalysts were evaluated for generation of hydrogen using aqueous methanol solution under visible light irradiation (λ ≥ 420 nm). The results show that as-prepared composite photocatalysts extend the light absorption range and restrict photogenerated charge-carrier recombination, resulting in enhanced photocatalytic activity compared to individual phases. The mechanism for the enhanced photocatalytic activity for the heterostructured composites is elucidated based on observed activity, band positions calculations, and photoluminescence data.« less

Thermodynamic properties of Na2O-SiO2-CaO melts at 1000 to 1100 °C

NASA Astrophysics Data System (ADS)

Neudorf, D. A.; Elliott, J. F.

1980-12-01

The thermodynamic properties of Na2O-SiO2 and Na2O-SiO2-CaO melts have been measured using the galvanic cellbegin{array}{*{20}c} {O_2 (g), (Na_2 O), Pt} \\ {Na_2 O - WO_3 liq} \\ left| begin{gathered} Na^ + \\ β - alumina \\ right| begin{array}{*{20}c} {Pt,(Na_2 O), O_2 (g)} \\ {Na_2 O - SiO_2 - CaO liq} \\ Activities of Na2O were calculated from the reversible emf of the cell. This is possible because the activity of Na2O in the Na2O-WO3 liquid is known from previous work. Data for the binary Na2O-SiO2 system were obtained between 1000 and 1100 °C and for compositions ranging from 25 wt pct to 40 wt pct Na2O. At 1050 °C, Loga_{Na_2 O} varied from approximately 10.2 at 25 wt pct Na2O to approximately -8.3 at 40 wt pct Na2O, the dependence with respect to composition being nearly linear. The Gibbs-Duhem equation was used to calculate the activities of SiO2(s), and the integral mixing properties, G M, HM, and S M, were derived. At the di-silicate composition, G M = -83 kJ/mol, H M = -41 kJ mol and S M = 33 J/mol K at 1000 °C. (Standard states are pure, liquid Na2O and pure, solid tridymite.) The activity data are interpreted in terms of the polymeric nature of silicate melts. Activities of Na2O in the Na2O-CaO-SiO2 system were measured for the 25, 30 and 35 wt pct Na2O binary compositions with up to 10 wt pct CaO added. The addition of CaO caused an increase in the activity of Na2O at constantN_{Na_2 O} /N_{SiO_2 } . The experimental data agree well with the behavior predicted by Richardson’s ternary mixing model.

Enhanced visible light photocatalytic water reduction from a g-C 3N 4/SrTa 2O 6 heterojunction

DOE PAGES

Adhikari, Shiba P.; Hood, Zachary D.; Wang, Hui; ...

2017-06-02

In this paper, a new g-C 3N 4/SrTa 2O 6 heterojunction photocatalyst was designed and prepared by chimie douce (soft chemistry) method where carbon nitride (g-C 3N 4) was deposited over the metastable perovskite phase of SrTa 2O 6. The morphological study of the heterojunction using SEM and STEM revealed that g-C 3N 4 nanofibers are dispersed uniformly on the surface of SrTa 2O 6 plates leading to the intimate contact between them. The heterojunction could achieve a high and stable visible light photocatalytic H 2 generation of 137 mmol/h/mole of g-C 3N 4, which is much larger than themore » amount of hydrogen generated by one mole of pristine g-C 3N 4. Finally, a plausible mechanism for the observed enhanced photocatalytic activity for the heterojunction is proposed on the basis of effective charge separation of photogenerated electron-hole pairs, supported by band position calculations and photo-physical properties of g-C 3N 4 and SrTa 2O 6.« less

Enhanced visible light photocatalytic water reduction from a g-C 3N 4/SrTa 2O 6 heterojunction

DOE Office of Scientific and Technical Information (OSTI.GOV)

Adhikari, Shiba P.; Hood, Zachary D.; Wang, Hui

In this paper, a new g-C 3N 4/SrTa 2O 6 heterojunction photocatalyst was designed and prepared by chimie douce (soft chemistry) method where carbon nitride (g-C 3N 4) was deposited over the metastable perovskite phase of SrTa 2O 6. The morphological study of the heterojunction using SEM and STEM revealed that g-C 3N 4 nanofibers are dispersed uniformly on the surface of SrTa 2O 6 plates leading to the intimate contact between them. The heterojunction could achieve a high and stable visible light photocatalytic H 2 generation of 137 mmol/h/mole of g-C 3N 4, which is much larger than themore » amount of hydrogen generated by one mole of pristine g-C 3N 4. Finally, a plausible mechanism for the observed enhanced photocatalytic activity for the heterojunction is proposed on the basis of effective charge separation of photogenerated electron-hole pairs, supported by band position calculations and photo-physical properties of g-C 3N 4 and SrTa 2O 6.« less

Flexible symmetric supercapacitors based on vertical TiO2 and carbon nanotubes

NASA Astrophysics Data System (ADS)

Chien, C. J.; Chang, Pai-Chun; Lu, Jia G.

2010-03-01

Highly conducting and porous carbon nanotubes are widely used as electrodes in double-layer-effect supercapacitors. In this presentation, vertical TiO2 nanotube array is fabricated by anodization process and used as supercapacitor electrode utilizing its compact density, high surface area and porous structure. By spin coating carbon nanotube networks on vertical TiO2 nanotube array as electrodes with 1M H2SO4 electrolyte in between, the specific capacitance can be enhanced by 30% compared to using pure carbon nanotube network alone because of the combination of double layer effect and redox reaction from metal oxide materials. Based on cyclic voltammetry and galvanostatic charge-discharge measurements, this type of hybrid electrode has proven to be suitable for high performance supercapacitor application and maintain desirable cycling stability. The electrochemical impedance spectroscopy technique shows that the electrode has good electrical conductivity. Furthermore, we will discuss the prospect of extending this energy storage approach in flexible electronics.

Disorder engineering of undoped TiO2 nanotube arrays for highly efficient solar-driven oxygen evolution.

PubMed

Salari, M; Aboutalebi, S H; Aghassi, A; Wagner, P; Mozer, A J; Wallace, G G

2015-02-28

The trade-off between performance and complexity of the device manufacturing process should be balanced to enable the economic harvest of solar energy. Here, we demonstrate a conceptual, yet practical and well-regulated strategy to achieve efficient solar photocatalytic activity in TiO2 through controlled phase transformation and disorder engineering in the surface layers of TiO2 nanotubes. This approach enabled us to fine-tune the bandgap structure of undoped TiO2 according to our needs while simultaneously obtaining robust separation of photo-excited charge carriers. Introduction of specific surface defects also assisted in utilization of the visible part of sunlight to split water molecules for the production of oxygen. The strategy proposed here can serve as a guideline to overcome the practical limitation in the realization of efficient, non-toxic, chemically stable photoelectrochemical systems with high catalytic activity at neutral pH under visible illumination conditions. We also successfully incorporated TiO2 nanotube arrays (TNTAs) with free-based porphyrin affording a pathway with an overall 140% enhanced efficiency, an oxygen evolution rate of 436 μL h(-1) and faradic efficiencies over 100%.

Self-organized TiO2 nanotube arrays in the photocatalytic degradation of methylene blue under UV light irradiation

NASA Astrophysics Data System (ADS)

Chung, Eun Hyuk; Baek, Seong Rim; Yu, Seong Mi; Kim, Jong Pil; Hong, Tae Eun; Kim, Hyun Gyu; Bae, Jong-Seong; Jeong, Euh Duck; Khan, F. Nawaz; Jung, Ok-sang

2015-04-01

Nanostructured titanium dioxide (NTiO2) is known to possess efficient photocatalytic activity and to have diverse applications in many fields due to its chemical stability, high surface area/volume ratio, high transmittance, and high refractive index in the visible and the near-ultraviolet regions. These facts prompted us to develop TiO2 nanotube (TiO2 NT) arrays through electrochemical anodic oxidation involving different electrolytes comprised of phosphoric acid — hydrofluoric acid aqueous systems by varying the voltage and the time. The annealing temperature of the nanotubes, TiO2 NTs, were varied to modify the surface morphology and were characterized by using X-ray diffraction and scanning electron microscopy. Scanning electron microscopy and X-ray diffraction results showed that the samples had uniform morphologies and good crystalline structures of the anatase phase at lower annealing temperatures and of the rutile phase at higher annealing temperatures. A secondary-ion mass-spectrometry analysis was used to investigate the surface atoms and to conduct a depth profile analysis of the TiO2 NTs. The efficiency of the photocatalytic activity of the TiO2 NT arrays in degrading methylene blue (MB) was investigated under UV-Vis light irradiation. The maximum photocatalytic activity was achieved for the samples with lower annealing temperatures due to their being in the anatase phase and having a higher surface area and a smaller crystal size, which play important roles in the degradation of organic pollutants.

Thermal degradation of TiO2 nanotubes on titanium

NASA Astrophysics Data System (ADS)

Shivaram, Anish; Bose, Susmita; Bandyopadhyay, Amit

2014-10-01

The objective of this research was to study thermal degradation behavior of TiO2 nanotubes on titanium (Ti). TiO2 nanotubes were grown via anodization method on commercially pure Ti (Cp-Ti) discs using two different electrolytes, 1 vol. % HF in deionized (DI) water and 1 vol. % HF + 0.5 wt. % NH4F + 10 vol. % DI water in ethylene glycol, to obtain nanotubes with two different lengths, 300 nm and 950 nm keeping the nanotube diameter constant at 100 ± 20 nm. As grown TiO2 nanotubes were subjected to heat treatment to understand thermal degradation as a function of both temperature and hold time. The signs of degradation were observed mainly when amorphous nanotubes started to crystallize, however the crystallization temperature varied based on TiO2 nanotubes length and anodizing condition. Overall, 300 nm nanotubes were thermally stable at least up to 400 °C for 12 h, while the 950 nm long nanotubes show signs of degradation from 400 °C for 6 h only. Clearly, length of nanotubes, heat treatment temperature as well as hold times show influence toward degradation kinetics of TiO2 nanotubes on titanium.

Fabrication of uniformly dispersed Ag nanoparticles loaded TiO{sub 2} nanotube arrays for enhancing photoelectrochemical and photocatalytic performances under visible light irradiation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yi, Junhui; Zhang, Shengsen; Wang, Hongjuan

2014-12-15

Graphical abstract: Uniformly dispersed Ag nanoparticles (NPs) were successfully loaded on both the outer and inner surface of the TiO{sub 2} nanotube arrays (NTs) through a simple polyol method, which exhibited the enhanced photoelectrochemical and photocatalytic performances under visible-light irradiation due to the more effective separation of photo-generated electron–hole pairs and faster interfacial charge transfer. - Highlights: • Highly dispersed Ag nanoparticles (NPs) are successfully prepared by polyol method. • Ag NPs are uniformly loaded on the surface of the TiO{sub 2} nanotube arrays (NTs). • Ag/TiO{sub 2}-NTs exhibit the enhanced photocatalytic activity under visible-light. • The enhanced photocurrent ismore » explained by electrochemical impedance spectroscopy. - Abstract: Uniformly dispersed Ag nanoparticles (NPs) were successfully loaded on both the outer and inner surface of the TiO{sub 2} nanotube arrays (NTs) through a simple polyol method. The as-prepared Ag/TiO{sub 2}-NTs were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy and UV–vis diffusion reflectance spectroscopy. Photoelectrochemical behaviors were investigated via photocurrent response and electrochemical impedance spectroscopy (EIS). Photocatalytic activity of Ag/TiO{sub 2}-NTs was evaluated by degradation of acid orange II under visible light irradiation. The results showed that photocatalytic efficiency of Ag/TiO{sub 2}-NTs is more than 5 times higher than that of pure TiO{sub 2} NTs. Comparing with the electrochemical deposition method, the photocatalytic activity of Ag/TiO{sub 2}-NTs prepared by polyol method has been obviously increased.« less

Hydrothermal preparation of copper doped NaTaO3 nanoparticles and study on the photocatalytic mechanism.

PubMed

Liu, Yulu; Su, Yiguo; Han, Hui; Wang, Xiaojing

2013-02-01

Effects of copper cations doping into wide band gap semiconductor photocatalysts of tantalate on morphology, visible light response, and photocatalytic performance were studied. A series of Cu-doped NaTaO3 catalysts were prepared by hydrothermal method. XRD and XPS results suggested that copper were successfully doped into the NaTaO3 nanocrystal in the Cu2+ state. TEM studies showed the formation of the cube shape nanoparticles of NaTaO3 as well as Cu-doped NaTaO3. UV-Vis diffuse reflectance spectra clearly indicated the red-shift in the series of copper doped NaTaO3 catalysts, resulting in a decrease in the band gap of NaTaO3. The trend of red shift was increased with an increase of copper doping concentration, whereas the photo-degradation methylene blue (MB) is not improved by the doping of copper ions. The simulation of energy band structure by density functional theory unfolded that the substitution of Ta5+ ions by Cu2+ ions results in forming an intermediate band (IB) upper the top of the valence band (VB), which is mainly attributed to the state of Cu 3d. The intermediate band is responsible for the red-shift caused by the doping of Cu ions. Meanwhile Cu species can become the recombination centers of photoinduced electrons and holes. Thus, the quickly recombination of e(-)h(+) pairs is one of the most significant factors which deteriorate the photoactivity of Cu-doped NaTaO3.

Dye-sensitized solar cells employing doubly or singly open-ended TiO2 nanotube arrays: structural geometry and charge transport.

PubMed

Choi, Jongmin; Song, Seulki; Kang, Gyeongho; Park, Taiho

2014-09-10

We systematically investigated the charge transport properties of doubly or singly open-ended TiO2 nanotube arrays (DNT and SNT, respectively) for their utility as electrodes in dye-sensitized solar cells (DSCs). The SNT or DNT arrays were transferred in a bottom-up (B-up) or top-up (T-up) configuration onto a fluorine-doped tin oxide (FTO) substrate onto which had been deposited a 2 μm thick TiO2 nanoparticle (NP) interlayer. This process yielded four types of DSCs prepared with SNTs (B-up or T-up) or DNT (B-up or T-up). The photovoltaic performances of these DSCs were analyzed by measuring the dependence of the charge transport on the DSC geometry. High resolution scanning electron microscopy techniques were used to characterize the electrode cross sections, and electrochemical impedance spectroscopy was used to characterize the electrical connection at the interface between the NT array and the TiO2 NP interlayer. We examined the effects of decorating the DNT or SNT arrays with small NPs (sNP@DNT and sNP@SNT, respectively) in an effort to increase the extent of dye loading. The DNT arrays decorated with small NPs performed better than the decorated SNT arrays, most likely because the Ti(OH)4 precursor solution flowed freely into the array through the open ends of the NTs in the DNT case but not in the SNT case. The sNP@DNT-based DSC exhibited a better PCE (10%) compared to the sNP@SNT-based DSCs (6.8%) because the electrolyte solution flow was not restricted, direct electron transport though the NT arrays was possible, the electrical connection at the interface between the NT array and the TiO2 NP interlayer was good, and the array provided efficient light harvesting.

Corrosion and wear behaviours of a reactive-sputter-deposited Ta2O5 nanoceramic coating

NASA Astrophysics Data System (ADS)

Hu, Wei; Xu, Jiang; Lu, Xiaolin; Hu, Dongsheng; Tao, Hongliang; Munroe, Paul; Xie, Zong-Han

2016-04-01

In order to improve the wear and corrosion resistance of Ti-6Al-4V, a novel β-Ta2O5 nanoceramic coating was synthesised using reactive sputter deposition enabled by double glow discharge plasma technique. The surface topography, chemical composition, and microstructure of the newly developed coating were characterised by a variety of surface analytical techniques. The coating microstructure was found to exhibit a compact striated pattern extending in a direction perpendicular to coating surface, which is composed of equiaxed β-Ta2O5 grains with an average grain size of ∼20 nm, well adhered to the Ti-6A1-4V substrate. The hardness and the Young's modulus of the as-deposited coating were obtained by nanoindentation, and the adhesion strength between the coating and substrate was determined by a scratch tester. The dry sliding wear behaviours of the coating were investigated at room temperature against Si3N4 ceramic balls at room temperature under applied loads ranging from 2.3 N to 5.3 N using a ball-on-disc tribometer. The specific wear rates of the coating exhibited only a slight increase with applied normal load, and were shown to be two orders of magnitude lower than that for Ti-6Al-4V under the same loading condition. Furthermore, the electrochemical behaviour of the coating immersed in 3.5 wt.% NaCl solution was systematically examined by using a range of complementary electrochemical techniques including potentiodynamic polarisation, electrochemical impedance spectroscopy (EIS), Mott-Schottky analysis as well as potential of zero charge (PZC). The results showed that the corrosion resistance of the β-Ta2O5 nanoceramic coating was better than that of Ti-6Al-4V alloy in 3.5 wt.% NaCl solution. Hence, by possessing higher mechanical properties and good wear and corrosion resistance, the β-Ta2O5 nanoceramic coating is considered to be a promising candidate for protection of engineering components operating under harsh conditions.

Frustration by competing interactions in the highly-distorted double perovskites La2NaRuO6 and La2NaOsO6

NASA Astrophysics Data System (ADS)

Aczel, A. A.; Bugaris, D. E.; Li, L.; Yan, J.-Q.; de La Cruz, C.; Zur Loye, H.-C.; Nagler, S. E.

2013-03-01

The usual classical behavior of S = 3/2, B-site ordered double perovskites results in simple, commensurate magnetic ground states. In contrast, heat capacity and neutron powder diffraction measurements for the S = 3/2 systems La2NaB'O6 (B' = Ru, Os) reveal an incommensurate magnetic ground state for La2NaRuO6 and a drastically suppressed ordered moment for La2NaOsO6. This behavior is attributed to the large monoclinic structural distortions of these double perovskites. The distortions have the effect of weakening the nearest neighbor superexchange interactions, presumably to an energy scale that is comparable to the next nearest neighbor superexchange. The exotic ground states in these materials can then arise from a competition between these two types of antiferromagnetic interactions, providing a novel mechanism for achieving frustration in the double perovskite family. Work at ORNL is supported by the Division of Scientific User Facilities and the Materials Science and Engineering Division, DOE Basic Energy Sciences. Work at the University of South Carolina is supported by the Heterogeneous Functional Materials Research Center, funded by DOE under award number de-sc0001061.

A photoelectrochemical immunosensor for tris(2,3-dibromopropyl) isocyanurate detection with a multiple hybrid CdTe/Au-TiO2 nanotube arrays.

PubMed

Feng, Hui; Zhou, Liping; Li, Jiezhen; Tran T, ThanhThuy; Wang, Niya; Yuan, Lijuan; Yan, Zhihong; Cai, Qingyun

2013-10-07

In this paper, tris(2,3-dibromopropyl) isocyanurate (TBC) is for the first time as far as we know determined by ultrasensitive photoelectrochemical (PEC) immunoassay using an antibody-modified ternary hybrid CdTe/Au-TiO2 nanotube arrays (NTAs) photoelectrode, developed by the pulse electrodeposition technique. The as-prepared hybrid shows enhanced photon absorption and photocurrent response, which subsequently increased the photoelectrical conversion efficiency in the visible region. TBC-antibody (Ab) was developed in rabbits as a result of immunization with the BSA-TBC conjugate and covalently cross-linked onto the CdTe/Au-TiO2 NTAs. Since the photocurrent is highly dependent on the TiO2 surface properties, the specific interaction between TBC and the antibody results in a sensitive change in the photocurrent, which displayed a linear range of 5.0 × 10(-11) to 5.0 × 10(-5) M and a low detection limit of 5.0 × 10(-11) M for TBC determination. This proposed strategy highlights the application of TiO2 nanotube in visible-light-activated photoelectrochemical biosensing, which could largely reduce the destructive effect of UV light on biomolecules.

Low-temperature crystallization of anodized TiO2 nanotubes at the solid-gas interface and their photoelectrochemical properties

NASA Astrophysics Data System (ADS)

Liu, Jing; Liu, Zhaoyue; Zhang, Tierui; Zhai, Jin; Jiang, Lei

2013-06-01

TiO2 nanotubular arrays formed by electrochemical anodization have attracted significant attention for photoelectrochemical applications that utilize solar energy. However, the as-anodized TiO2 nanotubes are amorphous, and need to be crystallized by high-temperature thermal annealing. Herein, we describe a low-temperature hydrothermal solid-gas route to crystallize TiO2 nanotubes. In this process, the as-anodized TiO2 hydroxo nanotubes are dehydrated to yield anatase phase via solid-gas interface reaction in an autoclave at a temperature of less than 180 °C. The solid-gas interface reaction alleviates the collapse of as-anodized TiO2 nanotubes during hydrothermal process efficiently. Compared with the common thermal annealing at the same temperature but at atmospheric pressure, the hydrothermal route improves the photocurrent density of TiO2 nanotubes by ~10 times in KOH electrolyte. The duration of the hydrothermal reaction has a substantial effect on the photoelectrochemical properties of TiO2 nanotubes, which is ascribed to the synergetic effect between the crystallization and structural evolution. Electron donors can further suppress the charge recombination in the low-temperature crystallized TiO2 nanotubes and boost the photocurrent density by ~120%.TiO2 nanotubular arrays formed by electrochemical anodization have attracted significant attention for photoelectrochemical applications that utilize solar energy. However, the as-anodized TiO2 nanotubes are amorphous, and need to be crystallized by high-temperature thermal annealing. Herein, we describe a low-temperature hydrothermal solid-gas route to crystallize TiO2 nanotubes. In this process, the as-anodized TiO2 hydroxo nanotubes are dehydrated to yield anatase phase via solid-gas interface reaction in an autoclave at a temperature of less than 180 °C. The solid-gas interface reaction alleviates the collapse of as-anodized TiO2 nanotubes during hydrothermal process efficiently. Compared with the common

Sunlight activated anodic freestanding ZrO2 nanotube arrays for Cr(VI) photoreduction.

PubMed

Bashirom, Nurulhuda; Tan, Wai Kian; Go, Kawamura; Matsuda, Atsunori; Abdul Razak, Khairunisak; Lockman, Zainovia

2018-06-14

Visible-light-active freestanding zirconia (ZrO2) nanotube (FSZNT) arrays were fabricated by a facile electrochemical anodization method in fluoride containing ethylene glycol electrolyte added to it 1 vol.% of potassium carbonate (K2CO3) at 60 V for 1 h. Poor adhesion at metal|oxide interface was induced by K2CO3 leading to formation of the FSZNT flakes. The effect of crystal structures of FSZNTs e.g., amorphous, amorphous/tetragonal, and tetragonal/monoclinic was investigated towards the photocatalytic reduction of 10 ppm hexavalent chromium, Cr(VI) at pH 2 under sunlight. The results demonstrate the amorphous FSZNTs exhibited the highest Cr(VI) removal efficiency than the crystalline FSZNTs (95 % versus 33 % after 5 h). The high photocatalytic activity of the amorphous FSZNTs can be attributed to enhanced Cr(VI) adsorption, high visible light absorption, and better charge carriers separation. The low photocatalytic activity of the crystalline FSZNTs annealed at 500 °C was mainly attributed to poor Cr(VI) adsorption, low visible light absorption, and less photoactive monoclinic-ZrO2. © 2018 IOP Publishing Ltd.

Fabrication and deformation behaviour of multilayer Al2O3/Ti/TiO2 nanotube arrays.

PubMed

Baradaran, S; Basirun, W J; Zalnezhad, E; Hamdi, M; Sarhan, Ahmed A D; Alias, Y

2013-04-01

In this study, titanium thin films were deposited on alumina substrates by radio frequency (RF) magnetron sputtering. The mechanical properties of the Ti coatings were evaluated in terms of adhesion strength at various RF powers, temperatures, and substrate bias voltages. The coating conditions of 400W of RF power, 250°C, and a 75V substrate bias voltage produced the strongest coating adhesion, as obtained by the Taguchi optimisation method. TiO2 nanotube arrays were grown as a second layer on the Ti substrates using electrochemical anodisation at a constant potential of 20V and anodisation times of 15min, 45min, and 75min in a NH4F electrolyte solution (75 ethylene glycol: 25 water). The anodised titanium was annealed at 450°C and 650°C in a N2 gas furnace to obtain different phases of titania, anatase and rutile, respectively. The mechanical properties of the anodised layer were investigated by nanoindentation. The results indicate that Young's modulus and hardness increased with annealing temperature to 650°C. Copyright © 2013 Elsevier Ltd. All rights reserved.

Emission analysis of Tb3+ -and Sm3+ -ion-doped (Li2 O/Na2 O/K2 O) and (Li2 O + Na2 O/Li2 O + K2 O/K2 O + Na2 O)-modified borosilicate glasses.

PubMed

Naveen Kumar Reddy, B; Sailaja, S; Thyagarajan, K; Jho, Young Dahl; Sudhakar Reddy, B

2018-05-01

Four series of borosilicate glasses modified by alkali oxides and doped with Tb 3+ and Sm 3+ ions were prepared using the conventional melt quenching technique, with the chemical composition 74.5B 2 O 3 + 10SiO 2 + 5MgO + R + 0.5(Tb 2 O 3 /Sm 2 O 3 ) [where R = 10(Li 2 O /Na 2 O/K 2 O) for series A and C, and R = 5(Li 2 O + Na 2 O/Li 2 O + K 2 O/K 2 O + Na 2 O) for series B and D]. The X-ray diffraction (XRD) patterns of all the prepared glasses indicate their amorphous nature. The spectroscopic properties of the prepared glasses were studied by optical absorption analysis, photoluminescence excitation (PLE) and photoluminescence (PL) analysis. A green emission corresponding to the 5 D 4 → 7 F 5 (543 nm) transition of the Tb 3+ ions was registered under excitation at 379 nm for series A and B glasses. The emission spectra of the Sm 3+ ions with the series C and D glasses showed strong reddish-orange emission at 600 nm ( 4 G 5/2 → 6 H 7/2 ) with an excitation wavelength λ exci = 404 nm ( 6 H 5/2 → 4 F 7/2 ). Furthermore, the change in the luminescence intensity with the addition of an alkali oxide and combinations of these alkali oxides to borosilicate glasses doped with Tb 3+ and Sm 3+ ions was studied to optimize the potential alkali-oxide-modified borosilicate glass. Copyright © 2017 John Wiley & Sons, Ltd.

Engineering of highly ordered TiO2 nanopore arrays by anodization

NASA Astrophysics Data System (ADS)

Wang, Huijie; Huang, Zhennan; Zhang, Li; Ding, Jie; Ma, Zhaoxia; Liu, Yong; Kou, Shengzhong; Yang, Hangsheng

2016-07-01

Finite element analysis was used to simulate the current density distributions in the TiO2 barrier layer formed at the initial stage of Ti anodization. The morphology modification of the barrier layer was found to induce current density distribution change. By starting the anodization with proper TiO2 barrier layer morphology, the current density distribution can be adjusted to favor the formation of either nanotube arrays or nanopore arrays of anodic TiO2. We also found that the addition of sodium acetate into the electrolyte suppressed both the field-assisted chemical dissolution of TiO2 and the TiF62- hydrolysis induced TiO2 deposition during anodization, and thus further favored the nanopore formation. Accordingly, highly ordered anodic TiO2 nanopore arrays, similar to anodic aluminum oxide nanopore arrays, were successfully prepared.

Na2Ti6O13@TiO2 core-shell nanorods with controllable mesoporous shells and their enhanced photocatalytic performance

NASA Astrophysics Data System (ADS)

Zhou, Xuefan; Zhong, Donglin; Luo, Hang; Pan, Jun; Zhang, Dou

2018-01-01

In this study, dispersive and free-standing Na2Ti6O13 nanorods with diameter of about 500 nm and length of about 10 μm were synthesized by the molten salt method. The Na2Ti6O13@TiO2 (denoted as TTO) core-shell nanorods were fabricated by a versatile kinetics controlled coating method. The TiO2 shells were uniform and mesoporous with exposed {101} facets. The thickness of TiO2 shells can be well controlled by the content of Ti(OC4H9)4, ranging from 0 nm, 15 nm, 60 nm to 70 nm corresponding to Na2Ti6O13, 0.25-TTO, 0.50-TTO and 0.75-TTO nanorods respectively. The crystalline phases, microstructure, porosity, photoabsorption and photocatalytic performance of all the samples were investigated systematically. The nanoscale heterojunction structure between Na2Ti6O13 and TiO2, reductive TiO2 {101} facets and high aspect ratio Na2Ti6O13 nanorods resulted in the enhanced photocatalytic performance of TTO nanorods. The optimized thickness of TiO2 shells were about 60 nm for 0.50-TTO nanorods, which possessed superior BET surface area, optical absorption and photocatalytic performance.

Formation and evolution of anodic TiO2 nanotube embryos

NASA Astrophysics Data System (ADS)

Jin, Rong; Liao, Maoying; Lin, Tong; Zhang, Shaoyu; Shen, Xiaoping; Song, Ye; Zhu, Xufei

2017-06-01

Anodic TiO2 nanotubes (ATNTs) have been widely investigated for decades due to their interesting nanostructures and various applications. However, the formation mechanism of ATNTs still remains unclear. To date, most of researches focus on the tubular structure but neglect the formation process of initial nanotube embryos. Herein, polyethylene glycol (PEG) is added into the traditional electrolyte to moderate the transformation process from compact layer to porous layer. Based on ‘oxygen bubble mould’ and ‘plastic flow model’ theory, the formation and evolution process of nanotube embryo is clarified firstly. Results validate the effect of ‘oxygen bubble mould’ on the formation of nanotube embryo, which has a great effect on regulating the morphology of ATNT arrays. Besides, nanotubes prepared in electrolytes with PEG show shorter tube length with larger diameter than that prepared in traditional electrolytes. The addition of PEG can also effectively avoid the breakdown phenomenon. Highlights Transformation from compact layer into porous layer is observed in PEG electrolyte. The effect of oxygen bubble mould is first demonstrated and observed. The formation process of TiO2 nanotube embryo is described systematically. TiO2 nanotubes prepared in PEG electrolyte show short length and large diameter.

Ag-bridged Ag2O nanowire network/TiO2 nanotube array p-n heterojunction as a highly efficient and stable visible light photocatalyst.

PubMed

Liu, Chengbin; Cao, Chenghao; Luo, Xubiao; Luo, Shenglian

2015-03-21

A unique Ag-bridged Ag2O nanowire network/TiO2 nanotube array p-n heterojunction (Ag-Ag2O/TiO2 NT) was fabricated by simple electrochemical method. Ag nanoparticles were firstly electrochemically deposited onto the surface of TiO2 NT and then were partly oxidized to Ag2O nanowires while the rest of Ag mother nanoparticles were located at the junctions of Ag2O nanowire network. The Ag-Ag2O/TiO2 NT heterostructure exhibited strong visible-light response, effective separation of photogenerated carriers, and high adsorption capacity. The integration of Ag-Ag2O self-stability structure and p-n heterojunction permitted high and stable photocatalytic activity of Ag-Ag2O/TiO2 NT heterostructure photocatalyst. Under 140-min visible light irradiation, the photocatalytic removal efficiency of both dye acid orange 7 (AO7) and industrial chemical p-nitrophenol (PNP) over Ag-Ag2O/TiO2 NT reached nearly 100% much higher than 17% for AO7 or 13% for PNP over bare TiO2 NT. After 5 successive cycles under 600-min simulated solar light irradiation, Ag-Ag2O/TiO2 NT remained highly stable photocatalytic activity. Copyright © 2014 Elsevier B.V. All rights reserved.

Efficient removal of herbicide 2,4-dichlorophenoxyacetic acid from water using Ag/reduced graphene oxide co-decorated TiO2 nanotube arrays.

PubMed

Tang, Yanhong; Luo, Shenglian; Teng, Yarong; Liu, Chengbin; Xu, Xiangli; Zhang, Xilin; Chen, Liang

2012-11-30

A new photocatalyst, Ag nanoparticles (NPs) and reduced graphene oxide (RGO) co-decorated TiO(2) nanotube arrays (NTs) (Ag/RGO-TiO(2) NTs), was designed and facilely produced by combining electrodeposition and photoreduction processes. The structures and properties of the photocatalysts were characterized. The ternary catalyst exhibited almost 100% photocatalytic removal efficiency of typical herbicide 2,4-dichlorophenoxyacetic acid (2,4-D) from water under simulated solar light irradiation. The photodegradation rate toward 2,4-D over Ag/RGO-TiO(2) NTs is 11.3 times that over bare TiO(2) NTs. After 10 successive cycles with 1600 min of irradiation, Ag/RGO-TiO(2) NTs maintained as high 2,4-D removal efficiency as 97.3% with excellent stability and easy recovery, which justifies the photocatalytic system a promising application for herbicide removal from water. Copyright © 2012 Elsevier B.V. All rights reserved.

Fast growth with crystal splitting of morphology-controllable Bi2S3 flowers on TiO2 nanotube arrays

NASA Astrophysics Data System (ADS)

Yang, L. X.; Ding, Y. B.; Luo, S. L.; Luo, Y.; Deng, F.; Li, Y.

2013-03-01

Bi2S3 crystals with flower-like morphologies are deposited on TiO2 nanotube arrays (NTs) by applying the cathodic pulse electrodeposition (PED) technique at 120 °C in 20 s. The highly oriented TiO2 NTs/Ti serving as substrate has high surface energy which is favorable for Gibbs free energy decreasing in nucleation process. Numerous boundaries between NTs are nucleation sites for atomic clusters, resulting in a fast nucleation velocity. Effective and fast heterogeneous nucleation initiates a thermodynamic control growth model and finally leads to the fast formation of highly crystallized Bi2S3 with a typical splitting property. Ethylene glycol (EG) was introduced into the electrolytes to inhibit the typical growth along the c axis ([0 0 1] plane) and facilitate the growth along the ab plane, producing Bi2S3 crystals with variable morphologies from sheaves to flowers by increasing EG contents.

Impact of total ionizing dose irradiation on Pt/SrBi2Ta2O9/HfTaO/Si memory capacitors

NASA Astrophysics Data System (ADS)

Yan, S. A.; Zhao, W.; Guo, H. X.; Xiong, Y.; Tang, M. H.; Li, Z.; Xiao, Y. G.; Zhang, W. L.; Ding, H.; Chen, J. W.; Zhou, Y. C.

2015-01-01

In this work, metal-ferroelectric-insulator-semiconductor (MFIS) structure capacitors with SrBi2Ta2O9 (300 nm) as ferroelectric thin film and HfTaO (6 nm, 8 nm, 10 nm, and 12 nm) as insulating buffer layer were proposed and investigated. The prepared capacitors were fabricated and characterized before radiation and then subjected to 60Co gamma irradiation in steps of two dose levels. Significant irradiation-induced degradation of the electrical characteristics was observed. The radiation experimental results indicated that stability and reliability of as-fabricated MFIS capacitors for nonvolatile memory applications could become uncontrollable under strong irradiation dose and/or long irradiation time.

On the existence of a high-temperature polymorph of Na2Ca6Si4O15—implications for the phase equilibria in the system Na2O-CaO-SiO2

NASA Astrophysics Data System (ADS)

Kahlenberg, Volker; Maier, Matthias

2016-12-01

Singe crystals of a new high-temperature polymorph of Na2Ca6Si4O15 have been obtained from solid state reactions performed at 1300 °C. The basic crystallographic data of this so-called β-phase at ambient conditions are as follows: space group P1 c1, a = 9.0112(5) Å, b = 7.3171(5) Å, c = 10.9723(6) Å, β = 107.720(14)°, V = 689.14(7) Å3, Z = 2. The crystals showed twinning by reticular merohedry (mimicking an orthorhombic C-centred unit cell) which was accounted for during data processing and structure solution. Structure determination was accomplished by direct methods. Least-squares refinements resulted in a residual of R(|F|) = 0.043 for 5811 observed reflections with I > 2σ(I). From a structural point of view β-Na2Ca6Si4O15 can be attributed to the group of mixed-anion silicates containing [Si2O7]-dimers as well as isolated [SiO4]-tetrahedra in the ratio 1:2, i.e. more precisely the formula can be written as Na2Ca6[SiO4]2[Si2O7]. The tetrahedral groups are arranged in layers parallel to (100). Sodium and calcium cations are located between the silicate anions for charge compensation and are coordinated by six to eight nearest oxygen ligands. Alternatively, the structure can be described as a mixed tetrahedral-octahedral framework based on kröhnkite-type [Ca(SiO4)2O2]-chains in which the CaO6-octahedra are corner-linked to bridging SiO4-tetrahedra. The infinite chains are running parallel to [001] and are concentrated in layers parallel to (010). Adjacent layers are shifted relative to each other by an amount of +δ or -δ along a*. Consequently, a …ABABAB… stacking sequence is created. A detailed comparison with related structures such as α-Na2Ca6Si4O15 and other A2B6Si4O15 representatives including topological as well as group theoretical aspects is presented. There are strong indications that monoclinic Na2Ca3Si2O8 mentioned in earlier studies is actually misinterpreted β-Na2Ca6Si4O15. In addition to the detailed crystallographic analysis of

Understanding the magnetic behavior of heat treated CaO-P2O5-Na2O-Fe2O3-SiO2 bioactive glass using electron paramagnetic resonance studies

NASA Astrophysics Data System (ADS)

Shankhwar, Nisha; Kothiyal, G. P.; Srinivasan, A.

2014-09-01

Bioactive glass of composition 41CaO-44SiO2-4P2O5-8Fe2O3-3Na2O has been heat treated in the temperature (TA) range of 750-1150 °C for time periods (tA) ranging from 1 h to 3 h to yield magnetic bioactive glass ceramics (MBCs). X-ray diffraction studies indicate the presence of bone mineral (hydroxyapatite and wollastonite) and magnetic (magnetite and α-hematite) phases in nanocrystalline form in the MBCs. Electron paramagnetic resonance (EPR) study was carried out to understand the variation in saturation magnetization and coercivity of the MBCs with TA and tA. These studies reveal the nature and amount of iron ions present in the MBCs and their interaction in the glassy oxide matrix as a function of annealing parameters. The deterioration in the magnetic properties of the glass heat treated above 1050 °C is attributed to the crystallization of the non-magnetic α-hematite phase. These results are expected to be useful in the application of these MBCs as thermoseeds in hyperthermia treatment of cancer.

TiO2 micro-flowers composed of nanotubes and their application to dye-sensitized solar cells.

PubMed

Kim, Woong-Rae; Park, Hun; Choi, Won-Youl

2014-02-24

TiO2 micro-flowers were made to bloom on Ti foil by the anodic oxidation of Ti-protruding dots with a cylindrical shape. Arrays of the Ti-protruding dots were prepared by photolithography, which consisted of coating the photoresists, attaching a patterned mask, illuminating with UV light, etching the Ti surface by reactive ion etching (RIE), and stripping the photoresist on the Ti foil. The procedure for the blooming of the TiO2 micro-flowers was analyzed by field emission scanning electron microscopy (FESEM) as the anodizing time was increased. Photoelectrodes of dye-sensitized solar cells (DSCs) were fabricated using TiO2 micro-flowers. Bare TiO2 nanotube arrays were used for reference samples. The short-circuit current (Jsc) and the power conversion efficiency of the DSCs based on the TiO2 micro-flowers were 4.340 mA/cm2 and 1.517%, respectively. These values of DSCs based on TiO2 micro-flowers were higher than those of bare samples. The TiO2 micro-flowers had a larger surface area for dye adsorption compared to bare TiO2 nanotube arrays, resulting in improved Jsc characteristics. The structure of the TiO2 micro-flowers allowed it to adsorb dyes very effectively, also demonstrating the potential to achieve higher power conversion efficiency levels for DSCs compared to a bare TiO2 nanotube array structure and the conventional TiO2 nanoparticle structure.

TiO2 micro-flowers composed of nanotubes and their application to dye-sensitized solar cells

PubMed Central

2014-01-01

TiO2 micro-flowers were made to bloom on Ti foil by the anodic oxidation of Ti-protruding dots with a cylindrical shape. Arrays of the Ti-protruding dots were prepared by photolithography, which consisted of coating the photoresists, attaching a patterned mask, illuminating with UV light, etching the Ti surface by reactive ion etching (RIE), and stripping the photoresist on the Ti foil. The procedure for the blooming of the TiO2 micro-flowers was analyzed by field emission scanning electron microscopy (FESEM) as the anodizing time was increased. Photoelectrodes of dye-sensitized solar cells (DSCs) were fabricated using TiO2 micro-flowers. Bare TiO2 nanotube arrays were used for reference samples. The short-circuit current (Jsc) and the power conversion efficiency of the DSCs based on the TiO2 micro-flowers were 4.340 mA/cm2 and 1.517%, respectively. These values of DSCs based on TiO2 micro-flowers were higher than those of bare samples. The TiO2 micro-flowers had a larger surface area for dye adsorption compared to bare TiO2 nanotube arrays, resulting in improved Jsc characteristics. The structure of the TiO2 micro-flowers allowed it to adsorb dyes very effectively, also demonstrating the potential to achieve higher power conversion efficiency levels for DSCs compared to a bare TiO2 nanotube array structure and the conventional TiO2 nanoparticle structure. PMID:24565201

TiO2 micro-flowers composed of nanotubes and their application to dye-sensitized solar cells

NASA Astrophysics Data System (ADS)

Kim, Woong-Rae; Park, Hun; Choi, Won-Youl

2014-02-01

TiO2 micro-flowers were made to bloom on Ti foil by the anodic oxidation of Ti-protruding dots with a cylindrical shape. Arrays of the Ti-protruding dots were prepared by photolithography, which consisted of coating the photoresists, attaching a patterned mask, illuminating with UV light, etching the Ti surface by reactive ion etching (RIE), and stripping the photoresist on the Ti foil. The procedure for the blooming of the TiO2 micro-flowers was analyzed by field emission scanning electron microscopy (FESEM) as the anodizing time was increased. Photoelectrodes of dye-sensitized solar cells (DSCs) were fabricated using TiO2 micro-flowers. Bare TiO2 nanotube arrays were used for reference samples. The short-circuit current ( J sc) and the power conversion efficiency of the DSCs based on the TiO2 micro-flowers were 4.340 mA/cm2 and 1.517%, respectively. These values of DSCs based on TiO2 micro-flowers were higher than those of bare samples. The TiO2 micro-flowers had a larger surface area for dye adsorption compared to bare TiO2 nanotube arrays, resulting in improved J sc characteristics. The structure of the TiO2 micro-flowers allowed it to adsorb dyes very effectively, also demonstrating the potential to achieve higher power conversion efficiency levels for DSCs compared to a bare TiO2 nanotube array structure and the conventional TiO2 nanoparticle structure.

Structural Stability and Electronic Properties of Na2C6O6 for a Rechargeable Sodium-ion Battery

NASA Astrophysics Data System (ADS)

Yamashita, Tomoki; Fujii, Akihiro; Momida, Hiroyoshi; Oguchi, Tamio

2014-03-01

Sodium-ion batteries have been explored as a promising alternative to lithium-ion batteries owing to a significant advantage of a natural abundance of sodium. Recently, it has been reported that disodium rhodizonate, Na2C6O6, exhibit good electrochemical properties and cycle performance as a minor-metal free organic cathode for sodium-ion batteries. However, its crystal structures during discharge/charge cycle still remain unclear. In this work, we theoretically propose feasible crystal structures of Na2+xC6O6 using first principles calculations. A structural phase transition has been found: Na4C6O6 has a different C6O6 packing arrangement from Na2C6O6. Electronic structures of Na2+xC6O6 during discharge/charge cycle are also discussed. Our predictions could be the key to understanding the discharge/charge process of Na2C6O6. Supported by MEXT program ``Elements Strategy Initiative to Form Core Rersearch Center'' (since 2012), MEXT; Ministry of Education Culture, Sports, Science and Technology, Japan.

Formation and characterization of Ta2O5/TaOx films formed by O ion implantation

NASA Astrophysics Data System (ADS)

Ruffell, S.; Kurunczi, P.; England, J.; Erokhin, Y.; Hautala, J.; Elliman, R. G.

2013-07-01

Ta2O5/TaOx (oxide/suboxide) heterostructures are fabricated by high fluence O ion-implantation into deposited Ta films. The resultant films are characterized by depth profiling X-ray photoelectron spectroscopy (XPS), cross-sectional transmission electron microscopy (XTEM), four-point probe, and current-voltage and capacitance-voltage measurements. The measurements show that Ta2O5/TaOx oxide/suboxide heterostructures can be fabricated with the relative thicknesses of the layers controlled by implantation energy and fluence. Electrical measurements show that this approach has promise for high volume manufacturing of resistive switching memory devices based on oxide/suboxide heterostructures.

Synthesis and characterization of Ag-doped TiO2 nanotubes on Ti-6Al-4V and Ti-6Al-7Nb alloy

NASA Astrophysics Data System (ADS)

Ulfah, Ika Maria; Bachtiar, Boy M.; Murnandityas, Arnita Rut; Slamet

2018-05-01

The present paper is focused on comparative behavior of nanotubes growth on Ti-6Al-4V and Ti-6Al-7Nb alloy using electrochemical anodization method. These alloys were anodized in electrolytes solution containing glycerol, water and 0.5wt.% of NH4F. Silver-doped TiO2 nanotubes were synthesized using photo-assisted deposition (PAD) at various Ag loading concentration in 0.05 M, 0.10 M, and 0.15 M. The phase composition and morphological characteristics were investigated by XRD and FESEM/EDX, respectively. The surface wettability was measured by contact angle meter. The results showed that TiO2 nanotubes can be grown on these surface alloys. XRD profiles revealed crystal formation of anatase, rutile and Ag on these surface alloys. According to FESEM images, the average nanotube diameter of Ti-6Al-4V alloy and Ti-6Al-7Nb alloy are 134 nm and 120 nm, respectively. EDX-Mapping analysis showed that Ag desposited over surface of TiO2 nanotubes. The surface wettability indicated hydrophilicity properties on Ti-4Al-4V alloy and Ti-6Al-7Nb alloy surface. This study may contribute to the development of silver-doped TiO2 nanotubes on Ti-6Al-4V alloy and Ti-6Al-7Nb alloy can be considered in various photocatalytic applications such as biomedical devicesdue to photocatalytic mechanism and antibacterial ability.

Laser Backscatter and Propagation in Low-Density Ta2O5 and SiO2 Foams

NASA Astrophysics Data System (ADS)

Mariscal, Derek; Patankar, Siddarth; Goyon, Clement; Baker, Kevin; MacLaren, Stephan; Hammer, Jim; Baumann, Ted; Amendt, Peter; Menapace, Joseph; Berger, Robert; Afeyan, Bedros; Tabak, Max; Kim, Sung Ho; Dixit, Sham; Moody, John; Jones, Ogden; LLNL Team; Polymath Research Inc. Collaboration

2016-10-01

Recent experiments at the Jupiter Laser Facility at LLNL have investigated the propagation and backscatter of a laser in low-density foams (2-30 mg/cc) comprised of Ta2O5 and SiO2. The foams fill the volume of thin polyimide tubes (2 mm diameter, 0.5-2 mm length), while the laser is directed down the axis of the tubes. Time-resolved Stimulated Brillouin Scattering (SBS) spectrum, time-integrated Stimulated Raman Scattering (SRS) spectrum and power were measured in the focusing cone. In addition Near Backscatter Imaging (NBI) assessed SBS outside the focusing cone while X-ray diagnostics were used to assess laser propagation through the foams. While this experiment uses a 2-omega laser drive, the pulse shape, irradiance, and the ratio ne/nc are scaled to be similar to future tests using Ta2O5 foams at the NIF. Experimental results are directly compared to calculations of laser propagation and backscattered spectra. This work was performed under the auspices of the U.S. Department of Energy by the Lawrence Livermore National Laboratory under Contract DE-AC52-07NA27344, with funding support from the Laboratory Directed Research and Development Program 15-ERD-073.

Investigation of anodic TiO2 nanotube composition with high spatial resolution AES and ToF SIMS

NASA Astrophysics Data System (ADS)

Dronov, Alexey; Gavrilin, Ilya; Kirilenko, Elena; Dronova, Daria; Gavrilov, Sergey

2018-03-01

High resolution Scanning Auger Electron Spectroscopy (AES) and Time-of-Flight Secondary Ion Mass-Spectrometry (ToF SIMS) were used to investigate structure and elemental composition variation of both across an array of TiO2 nanotubes (NTs) and single tube of an array. The TiO2 NT array was grown by anodic oxidation of Ti foil in fluorine-containing ethylene glycol electrolyte. It was found that the studied anodic TiO2 nanotubes have a layered structure with rather sharp interfaces. The differences in AES depth profiling results of a single tube with the focused primary electron beam (point analysis) and over an area of 75 μm in diameter of a nanotube array with the defocused primary electron beam are discussed. Depth profiling by ToF SIMS was carried out over approximately the same size of a nanotube array to determine possible ionic fragments in the structure. The analysis results show that the combination of both mentioned methods is useful for a detailed analysis of nanostructures with complex morphology and multi-layered nature.

Enhanced photoelectrocatalytic performance of heterostructured TiO2-based nanoparticles decorated nanotubes

NASA Astrophysics Data System (ADS)

Wu, Liangpeng; Yang, Xu; Huang, Yanqin; Li, Xinjun

2017-06-01

Titanium oxide nanotubes were prepared by hydrothermal treatment of TiO2 powder in NaOH aqueous solution and subsequently calcined. Titanium oxide nanotubes were further decorated by TiO2 nanoparticles through in situ hydrolysis of titanium isopropoxide containing alcohol and ammonia in an aqueous medium to form the composite catalyst (TNP/TiO2NTs). The morphology and structure of TNP/TiO2NTs were characterized by scanning and transmission electron microscopy, X-ray diffraction, UV-Vis, and Raman spectra. The separation efficiency of photo-excited carriers was investigated by photoluminescence technique and photoelectrochemical behavior. The photocatalytic activity was evaluated by the photocatalytic degradation of methyl orange. Due to the synergy effect caused by the interaction of titanium oxide nanotubes and TiO2 nanoparticles, the TNP/TiO2NTs composite shows efficient photogenerated carriers' separation and the increased light absorption. The photocatalytic activity was enhanced.

Facile fabrication of Si-doped TiO2 nanotubes photoanode for enhanced photoelectrochemical hydrogen generation

NASA Astrophysics Data System (ADS)

Dong, Zhenbiao; Ding, Dongyan; Li, Ting; Ning, Congqin

2018-04-01

Photoelectrochemical (PEC) water splitting based doping modified one dimensional (1D) titanium dioxide (TiO2) nanostructures provide an efficient method for hydrogen generation. Here we first successfully fabricated 1D Si-doped TiO2 (Ti-Si-O) nanotube arrays through anodizing Ti-Si alloys with different Si amount, and reported the PEC properties for water splitting. The Ti-Si-O nanotube arrays fabricated on Ti-5 wt.% Si alloy and annealed at 600 °C possess higher PEC activity, yielding a higher photocurrent density of 0.83 mA/cm2 at 0 V vs. Ag/AgCl. The maximum photoconversion efficiency was 0.54%, which was 2.7 times the photoconversion efficiency of undoped TiO2.

Band gap engineering of NaTaO3 using density functional theory: a charge compensated codoping strategy.

PubMed

Modak, Brindaban; Srinivasu, K; Ghosh, Swapan K

2014-08-28

In this theoretical study, we employ a codoping strategy to reduce the band gap of NaTaO3 aimed at improving the photocatalytic activity under visible light. The systematic study includes the effects of metal (W) and nonmetal (N) codoping on the electronic structure of NaTaO3 in comparison to the effect of individual dopants. The feasibility of the introduction of N into the NaTaO3 crystal structure is found to be enhanced in the presence of W, as indicated by the calculated formation energy. This codoping leads to formation of a charge compensated system, beneficial for the minimization of vacancy related defect formation. The electronic structure calculations have been carried out using a hybrid density functional for an accurate description of the proposed system. The introduction of W in place of Ta leads to the appearance of donor states below the conduction band, while N doping in place of oxygen introduces isolated acceptor states above the valence band. The codoping of N and W also passivates undesirable discrete midgap states. This feature is not observed in the case of (Cr, N) codoped NaTaO3 in spite of its charge compensated nature. We have also studied charge non-compensated codoping using several dopant pairs, including anion-anion and cation-anion pairs. However, this non-compensated codoping introduces localized states in between the valence band and the conduction band, and hence may not be effective in enhancing the photocatalytic properties of NaTaO3. The optical spectrum shows that the absorption curve for the (W, N)-codoped NaTaO3 is extended to the visible region due to narrowing of the band gap to 2.67 eV. Moreover, its activity for the photo decomposition of water to produce both H2 and O2 remains intact. Hence, based on the present investigation we can propose (W, N) codoped NaTaO3 as a promising photocatalyst for visible light driven water splitting.

Structurally Engineered Nanoporous Ta2O5-x Selector-Less Memristor for High Uniformity and Low Power Consumption.

PubMed

Kwon, Soonbang; Kim, Tae-Wook; Jang, Seonghoon; Lee, Jae-Hwang; Kim, Nam Dong; Ji, Yongsung; Lee, Chul-Ho; Tour, James M; Wang, Gunuk

2017-10-04

A memristor architecture based on metal-oxide materials would have great promise in achieving exceptional energy efficiency and higher scalability in next-generation electronic memory systems. Here, we propose a facile method for fabricating selector-less memristor arrays using an engineered nanoporous Ta 2 O 5-x architecture. The device was fabricated in the form of crossbar arrays, and it functions as a switchable rectifier with a self-embedded nonlinear switching behavior and ultralow power consumption (∼2.7 × 10 -6 W), which results in effective suppression of crosstalk interference. In addition, we determined that the essential switching elements, such as the programming power, the sneak current, the nonlinearity value, and the device-to-device uniformity, could be enhanced by in-depth structural engineering of the pores in the Ta 2 O 5-x layer. Our results, on the basis of the structural engineering of metal-oxide materials, could provide an attractive approach for fabricating simple and cost-efficient memristor arrays with acceptable device uniformity and low power consumption without the need for additional addressing selectors.

Oriented TiO2 nanotubes as a lithium metal storage medium

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Jae-Hun; Kang, Hee-Kook; Woo, Sang-Gil

2014-07-01

A new strategy for suppressing dendritic lithium growth in rechargeable lithium metal batteries is introduced, in which TiO2 nanotube (NT) array electrodes prepared by anodization are used as a metallic lithium storage medium. During the first charge process, lithium ions are inserted into the crystal structure of the TiO2 NT arrays, and then, lithium metal is deposited on the surfaces of the NT arrays, i.e., in the NT pores and between NT walls. From the second cycle onward, the TiO2 material is used as lithium ion pathways, which results in the effective current distribution for lithium deposition and prevents disintegrationmore » of the deposited metallic lithium. Compared to a Li(Cu foil)-LiCoO2 cell, the Li(TiO2 NT)-LiCoO2 cell exhibits enhanced cycling efficiency. This new concept will enable other 3D structured negative active materials to be used as lithium metal storage media for lithium metal batteries.« less

Hydrothermal solid-gas route to TiO2 nanoparticles/nanotube arrays for high-performance supercapacitors

NASA Astrophysics Data System (ADS)

Fan, Haowen; Zhang, He; Luo, Xiaolei; Liao, Maoying; Zhu, Xufei; Ma, Jing; Song, Ye

2017-07-01

Although TiO2 nanotube arrays (TNTAs) have shown great promise as supercapacitor materials, their specific capacitances are still not comparable with some typical materials. Here, TiO2 nanoparticles (NPs)/TNTAs hybrid structure has been derived from the anodized TNTAs by a facile hydrothermal solid-gas method (HSGM), which can avoid cracking or curling of the TNTAs from Ti substrate. The obtained NPs/TNTAs hybrid structure can exhibit a ∼4.90 times increase in surface area and a ∼5.49 times increase in areal specific capacitance compared to the TNTAs without HSGM treatment. Besides, the argon-atmosphere annealing can offer improved areal capacitance and cycling stability relative to the air-atmosphere annealing. The hydrothermal vapor pressure is a key factor for controlling microscopic morphologies of TNTAs, the morphology transformations of TNTAs during the HSGM treatment can be accelerated under enhanced vapor pressures. The highest areal capacitance of HSGM-treated TNTAs is up to 76.12 mF cm-2 at 0.5 mA cm-2, well above that of any TiO2 materials reported to date.

Structural and dielectric properties of Sr3(MgTa2)O9 and Sr3(ZnTa2)O9

NASA Astrophysics Data System (ADS)

Hoque, Md. M.; Dutta, Alo; Kumar, S.; Sinha, T. P.

2015-07-01

Herein, we report the crystal structures and morphological properties of Sr3(MgTa2)O9 (SMT) and Sr3(ZnTa2)O9 (SZT) synthesized by solid state ceramic method along with the results of alternating current impedance spectroscopic (ACIS) study in a frequency range from 50 Hz to 1 MHz at selective temperatures between 393 and 573 K. The crystal structures of SMT and SZT have been determined by Rietveld refinement of powder X-ray diffraction pattern using an initial structural model developed on the basis of literature survey. The results indicate that both the samples possess hexagonal structure of trigonal P 3 bar m 1 space group. The lattice parameters of SMT are a=b=5.65162 Å, c=6.94440 Å, α=β=90° and γ=120° and those of SZT are a=b=5.65832 Å, c=6.95911 Å and α=β=90° and γ=120°. SMT and SZT are isostructural and they exhibit 2:1 B site ordering with the staking sequence of {-Ta-Ta-Mg (Zn)-} (Mg for SMT and Zn for SZT) layer repeat on (111) plane of the pseudocells. The characteristic vibrational bands due to Ta-O, Mg-O and Zn-O bonds have been observed in the FTIR spectra of the samples. The FESEM micrographs of the samples show that the grains size ranges between 0.40 and 3.65 μm and 0.9 to 4.2 μm for SMT and SZT, respectively. To account for the polydispersive nature of the dielectric relaxation mechanism along with the effects of dc conductivity and localized space charges the variation of real (ε‧) and imaginary (ε″) parts of dielectric constant with frequency has been analytically interpreted in the framework of modified Cole-Cole model. SMT and SZT having the activation energies of 0.35 eV and 0.33 eV, respectively (obtained from the Arrhenius plot of dc conductivity), are semiconducting in nature. The electrical current conduction in the samples occurs by polaron hopping process. Further, we have shown that chemical property of A site cations has significant role in determining the dielectric properties of A3B‧B″2O9 type perovskites

Enhanced photocatalytic hydrogen production from water-ethanol solution by Ruthenium doped La-NaTaO3

NASA Astrophysics Data System (ADS)

Husin, H.; Alam, P. N.; Zaki, M.; Sofyana; Jakfar; Husaini; Hasfita, F.

2018-04-01

The photocatalytic hydrogen production from ethanol aqueous solution, with the use ruthenium doped La-NaTaO3 has been investigated. Ruthenium doped La-NaTaO3 catalysts are prepared by impregnation method. The catalysts are by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The Ru co-catalyst demonstrated from the TEM image shows a good dispersion on the surface of La-C-NaTaO3 with an average particle size between 4-5 nm. The photocatalytic reaction is carried out in a closed reactor with a gas circulation system. The catalytic activity of La-NaTaO3 improved markedly (6.6 times from pure water) when Ru is loaded onto its surface. The hydrogen production is notably enhanced in the presence of ethanol as electron donors. This result is much higher when compared with the rate of hydrogen production in the sample without co- catalysts about 9.4 times higher after Ru deposition from ethanol aqueous solution. Increasing the production of hydrogen on the Ru/La-NaTaO3 closely related to the decrease in recombination between electron-hole pairs.

Highly ordered Fe3+/TiO2 nanotube arrays for efficient photocataltyic degradation of nitrobenzene

NASA Astrophysics Data System (ADS)

Zhang, Yiyang; Gu, Di; Zhu, Lingyue; Wang, Baohui

2017-10-01

Highly ordered TiO2 nanotube arrays (TiO2 NTs) were prepared through a facile two-step electrochemical anodization, subsequently, active iron ions were introduced into the TiO2 NTs via a direct impregnation method. The XPS results showed that the iron elements existed in TiO2 NTs in the form of Fe3+ ions. Compared with the undoped TiO2 NTs, the absorption edge of Fe3+/TiO2 NTs showed an overt red shift and the photocurrent improved obviously, which indicated that Fe3+/TiO2 had a much higher photocatalytic activity. The optimal doping content was tested to be 0.1 mol/L which could make the photocatalytic activity of TiO2 NTs obviously improves under both visible and ultraviolent light. The prepared samples were adopted as photocatalyst to degrade nitrobenzene (NB). The reaction rate constants ks under UV light were in the order kone-stepTiO2NTs = 0.00338 O NTs = 0.00455 O NTs = 0.00736 which showed the superior photocatalysis activity of Fe3+/TiO2 NTs. The final degradation products were probed to be CO2 and H2O, which demonstrated that NB could be completely mineralized to harmless inorganic substance. The mechanism of NB degradation with Fe3+/TiO2 was also discussed and the quenching experiments further confirm that rad OH, h+ and rad O2- are active intermediates in the process of photocatalytic degradation.

Phase and Physicochemical Properties Diagrams of Quaternary System Li2B4O7 + Na2B4O7 + Mg2B6O11 + H2O

NASA Astrophysics Data System (ADS)

Wang, Shi-qiang; Du, Xue-min; Jing, Yan; Guo, Ya-fei; Deng, Tian-long

2017-12-01

The phase and physicochemical properties diagrams of the quaternary system (Li2B4O7 + Na2B4O7 + Mg2B6O11) at 288.15 K and 0.1 MPa were constructed using the solubilities, densities, and refractive indices measured. In the phase diagrams of the system there are one invariant point, three univariant isothermic dissolution curves, and three crystallization regions corresponding to Li2B4O7 · 3H2O, Na2B4O7 · 10H2O, and Mg2B6O11 · 15H2O, respectively. The solution density, refractive index of the quaternary system changes regularly with the increasing of Li2B4O7 concentration. The calculated values of density and refractive index using empirical equations of the quaternary system are in good agreement with the experimental values.

Electrochemically conductive treatment of TiO2 nanotube arrays in AlCl3 aqueous solution for supercapacitors

NASA Astrophysics Data System (ADS)

Zhong, Wenjie; Sang, Shangbin; Liu, Yingying; Wu, Qiumei; Liu, Kaiyu; Liu, Hongtao

2015-10-01

Highly ordered TiO2 nanotube arrays (NTAs) with excellent stability and large specific surface area make them competitive using as supercapacitor materials. Improving the conductivity of TiO2 is of great concern for the construction of high-performance supercapacitors. In this work, we developed a novel approach to improve the performance of TiO2 materials, involving the fabrication of Al-doped TiO2 NTAs by a simple electrochemical cathodic polarization treatment in AlCl3 aqueous solution. The prepared Al-doped TiO2 NTAs exhibited excellent electrochemical performances, attributing to the remarkably improved electrical conductivity (i.e., from approx. 10 kΩ to 20 Ω). Further analysis showed that Al3+ ions rather than H+ protons doped into TiO2 lattice cause this high conductivity. A MnO2/Al-TiO2 composite was evaluated by cyclic voltammetry, and achieved the specific capacitance of 544 F g-1, and the Ragone plot of the sample showed a high power density but less reduction of energy density. These results indicate that the MnO2/Al-TiO2 NTAs sample could be served as a promising electrode material for high -performance supercapacitors.

Evaluation to the effect of B2O3-La2O3-SrO-Na2O-Al2O3 bonding agent on Ti6Al4V-porcelain bonding.

PubMed

Zhao, C Q; Wu, S Q; Lu, Y J; Gan, Y L; Guo, S; Lin, J J; Huang, T T; Lin, J X

2016-10-01

Low-fusing bonding agents have been widely applied in Ti-ceramics restorations. As an important category, borate bonding agents have great potentials in increasing Ti-porcelain bonding. The purpose of this study is to evaluate the effect of borate bonding agent with addition of Na2O and Al2O3 on Ti6Al4V-porcelain bonding. The thermal properties of borate bonding agent, such as glass transition temperature (Tg) and crystallization peak temperature (Tp), were investigated to establish the sintering process. And the coefficient of thermal expansion (CTE) was to evaluate the matching effect of porcelain to Ti6Al4V. The bond strength was analyzed by the three point bending test. The microscopic morphology of the borate bonding agent surface after sintering, the interface of Ti-borate bonding agent-porcelain, and the fracture mode after porcelains fracture, were studied to assess the influence of borate bonding agent on Ti6Al4V-ceramics. With the addition of Na2O and Al2O3, the porcelain residues were observed increased indication on the Ti6Al4V surface after porcelain fracture and the bond strength was acquired the maximum (49.45MPa) in the bonding agent composition of 75.70B2O3-5.92La2O3-11.84SrO-4.67Na2O-1.87Al2O3. Those results suggest that borate bonding agent is an effective way to improve the Ti6Al4V-ceramics bond strength. And the addition of Na2O and Al2O3 strengthen this effect. Copyright © 2016 Elsevier Ltd. All rights reserved.

Microstructure and pseudocapacitive properties of electrodes constructed of oriented NiO-TiO2 nanotube arrays.

PubMed

Kim, Jae-Hun; Zhu, Kai; Yan, Yanfa; Perkins, Craig L; Frank, Arthur J

2010-10-13

We report on the synthesis and electrochemical properties of oriented NiO-TiO(2) nanotube (NT) arrays as electrodes for supercapacitors. The morphology of the films prepared by electrochemically anodizing Ni-Ti alloy foils was characterized by scanning and transmission electron microscopies, X-ray diffraction, and photoelectron spectroscopies. The morphology, crystal structure, and composition of the NT films were found to depend on the preparation conditions (anodization voltage and postgrowth annealing temperature). Annealing the as-grown NT arrays to a temperature of 600 °C transformed them from an amorphous phase to a mixture of crystalline rock salt NiO and rutile TiO(2). Changes in the morphology and crystal structure strongly influenced the electrochemical properties of the NT electrodes. Electrodes composed of NT films annealed at 600 °C displayed pseudocapacitor (redox-capacitor) behavior, including rapid charge/discharge kinetics and stable long-term cycling performance. At similar film thicknesses and surface areas, the NT-based electrodes showed a higher rate capability than the randomly packed nanoparticle-based electrodes. Even at the highest scan rate (500 mV/s), the capacitance of the NT electrodes was not much smaller (within 12%) than the capacitance measured at the slowest scan rate (5 mV/s). The faster charge/discharge kinetics of NT electrodes at high scan rates is attributed to the more ordered NT film architecture, which is expected to facilitate electron and ion transport during the charge-discharge reactions.

The development of Ti6Al4V based anti bacterial dental implant modified with TiO2 nanotube arrays doped silver metal (Ag)

NASA Astrophysics Data System (ADS)

Slamet, Bachtiar, B. M.; Wulan, P. P. D. K.; Setiadi, Sari, D. P.

2017-05-01

The development of Ti6Al4V based anti bacterial dental implant, modified with dopanted silver metal (Ag) TiO2 nanotube arrays (TiNTAs), is studied in this research. The condition inside the mouth is less foton energy, the dental implant material need to be modified with silver metal (Ag) dopanted TiNTAs. Modified TiNTAs used silver metal dopanted with Photo Assisted Deposition (PAD) method can be used as an electron trapper and produced hydroxyl radical, therefore it has antibacterial properties. The verification of antibacterial properties developed with biofilm static test using Streptococcus mutans bacteria model within 3 and 16 hours incubation, was characterized with XRD and SEM-EDX. Properties test result that resisting the biofilm growth effectively is TiNTAs/Ag/0,15, with 97,62 % disinfection bacteria sampel.

Pt nanoparticle on La0.02Na0.98TaO3 catalyst for hydrogen evolution from glycerol aqueous solution

NASA Astrophysics Data System (ADS)

Husin, Husni; Adisalamun, Sy, Yuliana; Asnawi, Teku Muhammad; Hasfita, Fikri

2017-01-01

Pt nanoparticles on La-doped sodium tantalum oxide (La0.02Na0.98TaO3), which acts as an active co-catalyst for H2 evolution under UV light irradiation was successfully synthesized by photo-deposition method. The La0.02Na0.98TaO3 photocatalyst was obtained by the reaction of La(NO3)2.3H2O, TaCl5, and NaOH at ambient temperature. The catalyst produced was characterized by a scanning electron microscope (SEM) and a high-resolution transmission electron microscope (HRTEM). SEM images of the La0.02Na0.98TaO3 sample showing that its particles size is ranging between 50-150 nm. The Pt particles are detected from HRTEM images is around 2-4 nm. The Pt/La0.02Na0.98TaO3 samples prepared were applied for photocatalytic H2 production at 30°C. The photocatalyst performance was evaluated for hydrogen production from water combining with glycerol as an electron donor (sacrificial reagent). The reactions were carried out in a closed reactor with a gas circulation system, illuminated with mercury (Hg) lamp. The experimental results show that the presence of glycerol in the systems can not only improve the efficiency of photocatalytic hydrogen generation but can also be decomposed to hydrogen efficiently. The photocatalytic activity of La0.02Na0.98TaO3 is significantly enhanced when Pt was loaded onto its crystalline surface.

Chemical vapor deposition of Ta{sub 2}O{sub 5} corrosion resistant coatings

DOE Office of Scientific and Technical Information (OSTI.GOV)

Graham, D.W.; Stinton, D.P.

1992-12-31

Silicon carbide and silicon nitride heat engine components are susceptible to hot corrosion by molten Na{sub 2}SO{sub 4} which forms from impurities present in fuel and the environment. Chemically vapor deposited Ta{sub 2}O{sub 5} coatings are being developed as a means to protect components from reaction with these salts and preserve their structural properties. Investigations to optimize the structure of the coating have revealed that the deposition conditions dramatically affect the coating morphology. Coatings deposited at high temperatures are typically columnar in structure; high concentrations of the reactant gases produce oxide powders on the substrate surface. Ta{sub 2}O{sub 5} depositedmore » at low temperatures consists of grains that are finer and have significantly less porosity than that formed at high temperatures. Samples of coatings which have been produced by CVD have successfully completed preliminary testing for resistance to corrosion by Na{sub 2}SO{sub 4}.« less

First-principles study on ferromagnetism in double perovskite Sr2AlTaO6 doped with Cu or Zn at B sites

NASA Astrophysics Data System (ADS)

Li, Y. D.; Wang, C. C.; Guo, Y. M.; Yu, Y.; Lu, Q. L.; Huang, S. G.; Li, Q. J.; Wang, H.; Cheng, R. L.; Liu, C. S.

2018-05-01

The possibilities of ferromagnetism induced by nonmagnetic dopants (Cu, Zn) in double perovskite Sr2AlTaO6 at B sites are investigated by density functional theory. Calculations reveal that substitutions at Ta-site tend to form high spin electronic configurations and could induce ferromagnetism which can be attributed to the hole-mediated p- d hybridization between Cu (or Zn) eg states and the neighboring O 2p states. The dopants preferably substitute at Al-site and adopt low spin electronic structures. Due to the smaller hole concentration and weaker covalent intensity, Sr2AlTaO6 with dopants at Al-site exhibits p-type metallic semiconductors without spin polarization.

Hierarchical NiCo2 S4 Nanotube@NiCo2 S4 Nanosheet Arrays on Ni Foam for High-Performance Supercapacitors.

PubMed

Chen, Haichao; Chen, Si; Shao, Hongyan; Li, Chao; Fan, Meiqiang; Chen, Da; Tian, Guanglei; Shu, Kangying

2016-01-01

Hierarchical NiCo2 S4 nanotube@NiCo2 S4 nanosheet arrays on Ni foam have been successfully synthesized. Owing to the unique hierarchical structure, enhanced capacitive performance can be attained. A specific capacitance up to 4.38 F cm(-2) is attained at 5 mA cm(-2) , which is much higher than the specific capacitance values of NiCo2 O4 nanosheet arrays, NiCo2 S4 nanosheet arrays and NiCo2 S4 nanotube arrays on Ni foam. The hierarchical NiCo2 S4 nanostructure shows superior cycling stability; after 5000 cycles, the specific capacitance still maintains 3.5 F cm(-2) . In addition, through the morphology and crystal structure measurement after cycling stability test, it is found that the NiCo2 S4 electroactive materials are gradually corroded; however, the NiCo2 S4 phase can still be well-maintained. Our results show that hierarchical NiCo2 S4 nanostructures are suitable electroactive materials for high performance supercapacitors. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Facile electrochemical synthesis of antimicrobial TiO2 nanotube arrays

PubMed Central

Zhao, Yu; Xing, Qi; Janjanam, Jagadeesh; He, Kun; Long, Fei; Low, Ke-Bin; Tiwari, Ashutosh; Zhao, Feng; Shahbazian-Yassar, Reza; Friedrich, Craig; Shokuhfar, Tolou

2014-01-01

Infection-related complications have been a critical issue for the application of titanium orthopedic implants. The use of Ag nanoparticles offers a potential approach to incorporate antimicrobial properties into the titanium implants. In this work, a novel and simple method was developed for synthesis of Ag (II) oxide deposited TiO2 nanotubes (TiNTs) using electrochemical anodization followed by Ag electroplating processes in the same electrolyte. The quantities of AgO nanoparticles deposited in TiNT were controlled by selecting different electroplating times and voltages. It was shown that AgO nanoparticles were crystalline and distributed throughout the length of the nanotubes. Inductively coupled plasma mass spectrometry tests showed that the quantities of released Ag were less than 7 mg/L after 30 days at 37°C. Antimicrobial assay results show that the AgO-deposited TiNTs can effectively kill the Escherichia coli bacteria. Although the AgO-deposited TiNTs showed some cytotoxicity, it should be controllable by optimization of the electroplating parameters and incorporation of cell growth factor. The results of this study indicated that antimicrobial properties could be added to nanotextured medical implants through a simple and cost effective method. PMID:25429214

Possibility of Flat-Band Ferromagnetism in Hole-Doped Pyrochlore Oxides Sn2 Nb2 O7 and Sn2 Ta2 O7

NASA Astrophysics Data System (ADS)

Hase, I.; Yanagisawa, T.; Aiura, Y.; Kawashima, K.

2018-05-01

Quantum mechanics tells us that the hopping integral between local orbitals makes the energy band dispersive. In a lattice with geometric frustration, however, dispersionless flat bands may appear due to quantum interference. Several models possessing flat bands have been proposed theoretically, and many attracting magnetic and electronic properties are predicted. However, despite many attempts to realize these models experimentally, compounds that are appropriately described by this model have not been found so far. Here we show that pyrochlore oxides Sn2 Nb2 O7 and Sn2Ta2O7 are such examples, by performing first-principles band calculation and several tight-binding analyses. Moreover, spin-polarized band calculation shows that the hole-doped systems Sn2 Nb2 O6 N and Sn2 Ta2 O6 N have complete spin polarization, and their magnetic moments are mostly carried by Sn-s and N-p orbitals, which are usually nonmagnetic. These compounds are not only candidates for ferromagnets without a magnetic element, but also will provide an experimental platform for a flat-band model which shows a wide range of physical properties.

Application of NaClO-treated multiwalled carbon nanotubes as solid phase extraction sorbents for preconcentration of trace 2,4-dichlorophenoxyacetic acid in aqueous samples.

PubMed

Lu, Ping; Deng, Dayi; Ni, Xiaodan

2012-09-01

Multiwalled carbon nanotubes functionalized by oxidation of original multiwalled carbon nanotubes with NaClO were prepared and their application as solid phase extraction sorbent for 2,4-dichlorophenoxyacetic acid (2,4-D) was investigated systemically, and a new method was developed for the determination of trace 2,4-D in water samples based on extraction and preconcentration of 2,4-D with solid phase extraction columns packed with NaClO-treated multiwalled carbon nanotubes prior to its determination by HPLC. The optimum experimental parameters for preconcentration of 2,4-D, including the column activating conditions, the amount of the sorbent, pH of the sample, elution composition, and elution volume, were investigated. The results indicated 2,4-D could be quantitatively retained by 100 mg NaClO-treated multiwalled carbon nanotubes at pH 5, and then eluted completely with 10 mL 3:1 (v/v) methanol-ammonium acetate solution (0.3 mol/L). The detection limit of this method for 2,4-D was 0.15 μg/L, and the relative standard deviation was 2.3% for fortified tap water samples and 2.5% for fortified riverine water sample at the 10 μg/L level. The method was validated using fortified tap water and riverine water samples with known amount of 2,4-D at the 0.4, 10, and 30 μg/L levels, respectively. © 2012 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Single step synthesis of rutile TiO{sub 2} nanoflower array film by chemical bath deposition method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dhandayuthapani, T.; Sivakumar, R.; Ilangovan, R., E-mail: rilangovan@yahoo.com

2016-05-06

Titanium oxide (TiO{sub 2}) nanostructures such as nanorod arrays, nanotube arrays and nanoflower arrays have been extensively investigated by the researchers. Among them nanoflower arrays has shown superior performance than other nanostructures in Dye sensitized solar cell, photocatalysis and energy storage applications. Herein, a single step synthesis for rutile TiO{sub 2} nanoflower array films suitable for device applications has been reported. Rutile TiO{sub 2} nanoflower thin film was synthesized by chemical bath deposition method using NaCl as an additive. Bath temperature induced evolution of nanoflower thin film arrays was observed from the morphological study. X-ray diffraction study confirmed the presencemore » of rutile phase polycrystalline TiO{sub 2}. Micro-Raman study revealed the presence of surface phonon mode at 105 cm{sup −1} due to the phonon confinement effect (finite size effect), in addition with the rutile Raman active modes of B{sub 1}g (143 cm{sup −1}), Eg (442 cm{sup −1}) and A{sub 1}g (607 cm{sup −1}). Further, the FTIR spectrum confirmed the presence of Ti-O-Ti bonding vibration. The Tauc plot showed the direct energy band gap nature of the film with the value of 2.9 eV.« less

Tunable TiO2 Nanotube Arrays for Flexible Bio-Sensitized Solar Cells

DTIC Science & Technology

2012-08-01

microid extender followed by a colloidal silica /wetted imperial cloth. The foil was then cut into 1- × 2-cm samples. Then, the substrates were...17. Lei, B.; Liao, J.; Wang, R. J.; Su, C.; Kuang, D. Ordered Crystalline Ti02 Nanotube Arrays on Transparent FTO Glass for Efficient Dye...combined with a transparent , Indium Tin Dioxide coated PET film are attractive candidates for efficient, flexible DSSC’s. Flexible solar cells offer

First investigations on the quaternary system Na2O-K2O-CaO-SiO2: synthesis and crystal structure of the mixed alkali calcium silicate K1.08Na0.92Ca6Si4O15

NASA Astrophysics Data System (ADS)

Kahlenberg, Volker; Mayerl, Michael Jean-Philippe; Schmidmair, Daniela; Krüger, Hannes; Tribus, Martina

2018-04-01

In the course of an exploratory study on the quaternary system Na2O-K2O-CaO-SiO2 single crystals of the first anhydrous sodium potassium calcium silicate have been obtained from slow cooling of a melt in the range between 1250 and 1050 °C. Electron probe micro analysis suggested the following idealized molar ratios of the oxides for the novel compound: K2O:Na2O:CaO:SiO2 = 1:1:12:8 (or KNaCa6Si4O15). Single-crystal diffraction measurements on a crystal with chemical composition K1.08Na0.92Ca6Si4O15 resulted in the following basic crystallographic data: monoclinic symmetry, space group P 21/ c, a = 8.9618(9) Å, b = 7.3594(6) Å, c = 11.2453(11) Å, β= 107.54(1)°, V = 707.2(1) Å3, Z = 2. Structure solution was performed using direct methods. The final least-squares refinement converged at a residual of R(|F|) = 0.0346 for 1288 independent reflections and 125 parameters. From a structural point of view, K1.08Na0.92Ca6Si4O15 belongs to the group of mixed-anion silicates containing [Si2O7]- and [SiO4]-units in the ratio 1:2. The mono- and divalent cations occupy a total of four crystallographically independent positions located in voids between the tetrahedra. Three of these sites are exclusively occupied by calcium. The fourth site is occupied by 54(1)% K and 46%(1) Na, respectively. Alternatively, the structure can be described as a heteropolyhedral framework based on corner-sharing silicate tetrahedra and [CaO6]-octahedra. The network can build up from kröhnkite-like [Ca(SiO4)2O2]-chains running along [001]. A detailed comparison with other A2B6Si4O15-compounds including topological and group-theoretical aspects is presented.

The preparation and photocatalytic activity of CdS/(Cal-Ta2O5-SiO2) composite photocatalyst under visible light

NASA Astrophysics Data System (ADS)

Li, Juxia

2018-02-01

CdS/(Cal-Ta2O5-SiO2) composite photocatalyst has been successfully fabricated via wet chemistry method. Ta2O5-SiO2 with multi-step Ta2O5 deposition on SiO2 has more Ta2O5 on SiO2 to ensure the active sites. Trough multi-step calcination, Ta2O5 can load on SiO2 with uniform and stable, which make it have high photocatalytic activity. The obtained samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), diffuse reflectance ultraviolet-visible spectroscopy (UV-vis) and photoluminescence spectroscopy (PL). Without any co-catalysts, the as-prepared CdS/(Cal-Ta2O5-SiO2) exhibited remarkable photocatalytic activity and recyclability both in the degradation of rhodamine B and in the hydrogen production from water splitting under visible light.

Influence of Ta doping in resistive switching behavior of TiO2

NASA Astrophysics Data System (ADS)

Barman, Arabinda; Saini, Chetan P.; Deshmukh, Sujit; Dhar, Sankar; Kanjilal, Aloke

An approach has been made to understand the resistive switching behavior in Ta-doped TiO2 films on Pt substrates. Prior to thin film deposition, Ta-doped TiO2 powder has been synthesized chemically using Ta and Ti precursor solutions. However, the Ta doping has seriously been affected by increasing Ta concentration above 1 at% due to the segregation of Ta2O5 phase. The Ta-doped TiO2 targets have been prepared for pulsed laser deposition of the films on Pt substrates using an excitation wavelength of 248 nm. The structural and chemical properties of the Ta-doped TiO2 films have been investigated in details with the help of XRD, SIMS, XAS and XPS. The stoichiometry of the Ta-doped TiO2 films with increasing depth has been verified initially by SIMS. The electrical study of the corresponding device structures further suggests that the optimized resistive switching effect can be accomplished up to a threshold Ta-doping of 1 at%. Nevertheless, a highly conducting behavior has been shown when the TiO2 films are doped with 2 at% Ta. These results will be discussed in details in the light of defect induced resistive switching phenomenon.

Field Emission Study of Carbon Nanotubes: High Current Density from Nanotube Bundle Arrays

NASA Technical Reports Server (NTRS)

Bronikowski, Micheal J.; Manohara, Harish M.; Siegel, Peter H.; Hunt, Brian D.

2004-01-01

We have investigated the field emission behavior of lithographically patterned bundles of multiwalled carbon nanotubes arranged in a variety of array geometries. Such arrays of nanotube bundles are found to perform significantly better in field emission than arrays of isolated nanotubes or dense, continuous mats of nanotubes, with the field emission performance depending on the bundle diameter and inter-bundle spacing. Arrays of 2-micrometers diameter nanotube bundles spaced 5 micrometers apart (edge-to-edge spacing) produced the largest emission densities, routinely giving 1.5 to 1.8 A/cm(sup 2) at approximately 4 V/micrometer electric field, and greater than 6 A/cm(sup 2) at 20 V/micrometers.

Scanning electron microscopy of heat treated TiO2 nanotubes arrays obtained by anodic oxidation

NASA Astrophysics Data System (ADS)

Naranjo, D. I.; García-Vergara, S. J.; Blanco, S.

2017-12-01

Scanning electron microscopy was used to investigate the anatase-rutile transformation of self-organized TiO2 nanotubes obtained on titanium foil by anodizing and subsequent heat treatment. The anodizing was carried out at 20V in an 1% v/v HF acid and ethylene glycol:water (50:50) electrolyte at room temperature. The anodized samples were initially pre-heat treated at 450°C for 4 hours to modify the amorphous structure of TiO2 nanotubes into anatase structure. Then, the samples were heated between 600 to 800°C for different times, in order to promote the transformation to rutile structure. The formation of TiO2 nanotubes is evident by SEM images. Notably, when the samples are treated at high temperature, the formation of rutile crystals starts to become evident at the nanotubes located on the originally grain boundaries of the titanium. Thus, the anatase - rutile transformation has a close relationship with the microstructure of the titanium, more exactly with grain boundaries.

TiO2 Nanotubes: Recent Advances in Synthesis and Gas Sensing Properties

PubMed Central

Galstyan, Vardan; Comini, Elisabetta; Faglia, Guido; Sberveglieri, Giorgio

2013-01-01

Synthesis—particularly by electrochemical anodization-, growth mechanism and chemical sensing properties of pure, doped and mixed titania tubular arrays are reviewed. The first part deals on how anodization parameters affect the size, shape and morphology of titania nanotubes. In the second part fabrication of sensing devices based on titania nanotubes is presented, together with their most notable gas sensing performances. Doping largely improves conductivity and enhances gas sensing performances of TiO2 nanotubes. PMID:24184919

Thermodynamic modeling of melts in the system Na 2O-NaAlO 2-SiO 2-F 2O -1

NASA Astrophysics Data System (ADS)

Dolejš, David; Baker, Don R.

2005-12-01

Fluorine is a common volatile element in magmatic-hydrothermal systems, but its solution mechanisms and thermodynamic description in highly polymerized silicate melts are poorly known. We have developed a thermodynamic model for fluorosilicate liquids that links experimentally determined phase equilibria and spectroscopic information on melt structure. The model is applicable to crystallization of fluoride minerals, fluoride-silicate immiscibility in natural felsic melts, and metallurgical processes. Configurational properties of fluorosilicate melts are described by mixing on three site levels (sublattices): (1) alkali fluoride, polyhedral aluminofluoride and silicofluoride species and nonbridging terminations of the aluminosilicate network, (2) alkali-aluminate and silicate tetrahedra within the network and (3) bridging oxygen, nonbridging oxygen and terminal fluorine atoms on tetrahedral apices of the network. Abundances of individual chemical species are described by a homogeneous equilibrium representing melt depolymerization: F - (free) + O 0 (bridging) = F 0 (terminal) + O - (nonbridging) which corresponds to a replacement of an oxygen bridging two tetrahedra by a pair of terminations, one with F and the other with an O and a charge-balancing Na. In cryolite-bearing systems two additional interaction mechanisms occur: (1) the self-dissociation of octahedral aluminofluoride complexes: [AlF 6] = [AlF 4] + 2 [F], and (2) the short-range order between (O,F)-corners and (Si,NaAl)-centers of tetrahedra: Si-O-Si + 2 [NaAl]-F = [NaAl]-O-[NaAl] + 2 Si-F. Portrayal of these equilibria in ternary Thompson reaction space allows for the decrease in the number of interaction mechanisms by linearly combining melt depolymerization with tetrahedral short-range order. In this formulation, the nonideal thermodynamic properties are represented by reaction energies of homogeneous equilibria, thus defining directly individual chemical species concentrations and configurational

Three-dimensional hot electron photovoltaic device with vertically aligned TiO2 nanotubes.

PubMed

Goddeti, Kalyan C; Lee, Changhwan; Lee, Young Keun; Park, Jeong Young

2018-05-09

Titanium dioxide (TiO 2 ) nanotubes with vertically aligned array structures show substantial advantages in solar cells as an electron transport material that offers a large surface area where charges travel linearly along the nanotubes. Integrating this one-dimensional semiconductor material with plasmonic metals to create a three-dimensional plasmonic nanodiode can influence solar energy conversion by utilizing the generated hot electrons. Here, we devised plasmonic Au/TiO 2 and Ag/TiO 2 nanodiode architectures composed of TiO 2 nanotube arrays for enhanced photon absorption, and for the subsequent generation and capture of hot carriers. The photocurrents and incident photon to current conversion efficiencies (IPCE) were obtained as a function of photon energy for hot electron detection. We observed enhanced photocurrents and IPCE using the Ag/TiO 2 nanodiode. The strong plasmonic peaks of the Au and Ag from the IPCE clearly indicate an enhancement of the hot electron flux resulting from the presence of surface plasmons. The calculated electric fields and the corresponding absorbances of the nanodiode using finite-difference time-domain simulation methods are also in good agreement with the experimental results. These results show a unique strategy of combining a hot electron photovoltaic device with a three-dimensional architecture, which has the clear advantages of maximizing light absorption and a metal-semiconductor interface area.

Highly Durable Na2V6O16·1.63H2O Nanowire Cathode for Aqueous Zinc-Ion Battery.

PubMed

Hu, Ping; Zhu, Ting; Wang, Xuanpeng; Wei, Xiujuan; Yan, Mengyu; Li, Jiantao; Luo, Wen; Yang, Wei; Zhang, Wencui; Zhou, Liang; Zhou, Zhiqiang; Mai, Liqiang

2018-03-14

Rechargeable aqueous zinc-ion batteries are highly desirable for grid-scale applications due to their low cost and high safety; however, the poor cycling stability hinders their widespread application. Herein, a highly durable zinc-ion battery system with a Na 2 V 6 O 16 ·1.63H 2 O nanowire cathode and an aqueous Zn(CF 3 SO 3 ) 2 electrolyte has been developed. The Na 2 V 6 O 16 ·1.63H 2 O nanowires deliver a high specific capacity of 352 mAh g -1 at 50 mA g -1 and exhibit a capacity retention of 90% over 6000 cycles at 5000 mA g -1 , which represents the best cycling performance compared with all previous reports. In contrast, the NaV 3 O 8 nanowires maintain only 17% of the initial capacity after 4000 cycles at 5000 mA g -1 . A single-nanowire-based zinc-ion battery is assembled, which reveals the intrinsic Zn 2+ storage mechanism at nanoscale. The remarkable electrochemical performance especially the long-term cycling stability makes Na 2 V 6 O 16 ·1.63H 2 O a promising cathode for a low-cost and safe aqueous zinc-ion battery.

Ag nanoparticle-filled TiO2 nanotube arrays prepared by anodization and electrophoretic deposition for dye-sensitized solar cells

NASA Astrophysics Data System (ADS)

Wei, Xing; Sugri Nbelayim, Pascal; Kawamura, Go; Muto, Hiroyuki; Matsuda, Atsunori

2017-03-01

A layer of TiO2 nanotube (TNT) arrays with a thickness of 13 μm is synthesized by a two-step anodic oxidation from Ti metal foil. Surface charged Ag nanoparticles (NPs) are prepared by chemical reduction. After a pretreatment of the TNT arrays by acetone vapor, Ag NP filled TNT arrays can be achieved by electrophoretic deposition (EPD). Effects of the applied voltage during EPD such as DC-AC difference, frequency and waveform are investigated by quantitative analysis using atomic absorption spectroscopy. The results show that the best EPD condition is using DC 2 V + AC 4 V and a square wave of 1 Hz as the applied voltage. Back illuminated dye-sensitized solar cells are fabricated from TNT arrays with and without Ag NPs. The efficiency increased from 3.70% to 5.01% by the deposition of Ag NPs.

Co(OH)2/RGO/NiO sandwich-structured nanotube arrays with special surface and synergistic effects as high-performance positive electrodes for asymmetric supercapacitors

NASA Astrophysics Data System (ADS)

Xu, Han; Zhang, Chi; Zhou, Wen; Li, Gao-Ren

2015-10-01

High power density, high energy density and excellent cycling stability are the main requirements for high-performance supercapacitors (SCs) that will be widely used for portable consumer electronics and hybrid electric vehicles. Here we investigate novel types of hybrid Co(OH)2/reduced graphene oxide (RGO)/NiO sandwich-structured nanotube arrays (SNTAs) as positive electrodes for asymmetric supercapacitors (ASCs). The synthesized Co(OH)2/RGO/NiO SNTAs exhibit a significantly improved specific capacity (~1470 F g-1 at 5 mV s-1) and excellent cycling stability with ~98% Csp retention after 10 000 cycles because of the fast transport and short diffusion paths for electroactive species, the high utilization rate of electrode materials, and special synergistic effects among Co(OH)2, RGO, and NiO. The high-performance ASCs are assembled using Co(OH)2/RGO/NiO SNTAs as positive electrodes and active carbon (AC) as negative electrodes, and they exhibit a high energy density (115 Wh kg-1), a high power density (27.5 kW kg-1) and an excellent cycling stability (less 5% Csp loss after 10 000 cycles). This study shows an important breakthrough in the design and fabrication of multi-walled hybrid nanotube arrays as positive electrodes for ASCs.High power density, high energy density and excellent cycling stability are the main requirements for high-performance supercapacitors (SCs) that will be widely used for portable consumer electronics and hybrid electric vehicles. Here we investigate novel types of hybrid Co(OH)2/reduced graphene oxide (RGO)/NiO sandwich-structured nanotube arrays (SNTAs) as positive electrodes for asymmetric supercapacitors (ASCs). The synthesized Co(OH)2/RGO/NiO SNTAs exhibit a significantly improved specific capacity (~1470 F g-1 at 5 mV s-1) and excellent cycling stability with ~98% Csp retention after 10 000 cycles because of the fast transport and short diffusion paths for electroactive species, the high utilization rate of electrode materials, and

Hollow waveguides with low intrinsic photoluminescence fabricated with Ta2O5 and SiO2 films

NASA Astrophysics Data System (ADS)

Zhao, Y.; Jenkins, M.; Measor, P.; Leake, K.; Liu, S.; Schmidt, H.; Hawkins, A. R.

2011-02-01

A type of integrated hollow core waveguide with low intrinsic photoluminescence fabricated with Ta2O5 and SiO2 films is demonstrated. Hollow core waveguides made with a combination of plasma-enhanced chemical vapor deposition SiO2 and sputtered Ta2O5 provide a nearly optimal structure for optofluidic biofluorescence measurements with low optical loss, high fabrication yield, and low background photoluminescence. Compared to earlier structures made using Si3N4, the photoluminescence background of Ta2O5 based hollow core waveguides is decreased by a factor of 10 and the signal-to-noise ratio for fluorescent nanobead detection is improved by a factor of 12.

Preparation of TiO2/boron-doped diamond/Ta multilayer films and use as electrode materials for supercapacitors

NASA Astrophysics Data System (ADS)

Shi, Chao; Li, Hongji; Li, Cuiping; Li, Mingji; Qu, Changqing; Yang, Baohe

2015-12-01

We report nanostructured TiO2/boron-doped diamond (BDD)/Ta multilayer films and their electrochemical performances as supercapacitor electrodes. The BDD films were grown on Ta substrates using electron-assisted hot filament chemical vapor deposition. Ti metal layers were deposited on the BDD surfaces by radio frequency magnetron sputtering, and nanostructured TiO2/BDD/Ta thin films were prepared by electrochemical etching and thermal annealing. The successful formation of TiO2 and Ta layered nanostructures was demonstrated using scanning electron and transmission electron microscopies. The electrochemical responses of these electrodes were evaluated by examining their use as electrical double-layer capacitors, using cyclic voltammetry, and galvanostatic charge/discharge and impedance measurements. When the TiO2/BDD/Ta film was used as the working electrode with 0.1 M Na2SO4 as the electrolyte, the capacitor had a specific capacitance of 5.23 mF cm-2 at a scan rate of 5 mV s-1 for a B/C ratio of 0.1% w/w. Furthermore, the TiO2/BDD/Ta film had improved electrochemical stability, with a retention of 89.3% after 500 cycles. This electrochemical behavior is attributed to the quality of the BDD, the surface roughness and electrocatalytic activities of the TiO2 layer and Ta nanoporous structures, and the synergies between them. These results show that TiO2/BDD/Ta films are promising as capacitor electrodes for special applications.

Flux-mediated syntheses, structural characterization and low-temperature polymorphism of the p-type semiconductor Cu2Ta4O11

NASA Astrophysics Data System (ADS)

King, Nacole; Sullivan, Ian; Watkins-Curry, Pilanda; Chan, Julia Y.; Maggard, Paul A.

2016-04-01

A new low-temperature polymorph of the copper(I)-tantalate, α-Cu2Ta4O11, has been synthesized in a molten CuCl-flux reaction at 665 °C for 1 h and characterized by powder X-ray diffraction Rietveld refinements (space group Cc (#9), a=10.734(1) Å, b = 6.2506(3) Å, c=12.887(1) Å, β = 106.070(4)°). The α-Cu2Ta4O11 phase is a lower-symmetry monoclinic polymorph of the rhombohedral Cu2Ta4O11 structure (i.e., β-Cu2Ta4O11 space group R 3 ̅ c (#167), a = 6.2190(2) Å, c=37.107(1) Å), and related crystallographically by ahex=amono/√3, bhex=bmono, and chex=3cmonosinβmono. Its structure is similar to the rhombohedral β-Cu2Ta4O11 and is composed of single layers of highly-distorted and edge-shared TaO7 and TaO6 polyhedra alternating with layers of nearly linearly-coordinated Cu(I) cations and isolated TaO6 octahedra. Temperature dependent powder X-ray diffraction data show the α-Cu2Ta4O11 phase is relatively stable under vacuum at 223 K and 298 K, but reversibly transforms to β-Cu2Ta4O11 by at least 523 K and higher temperatures. The symmetry-lowering distortions from β-Cu2Ta4O11 to α-Cu2Ta4O11 arise from the out-of-center displacements of the Ta 5d0 cations in the TaO7 pentagonal bipyramids. The UV-vis diffuse reflectance spectrum of the monoclinic α-Cu2Ta4O11 shows an indirect bandgap transition of ∼2.6 eV, with the higher-energy direct transitions starting at ∼2.7 eV. Photoelectrochemical measurements on polycrystalline films of α-Cu2Ta4O11 show strong cathodic photocurrents of ∼1.5 mA/cm2 under AM 1.5 G solar irradiation.

Solubility of SC2O3 in NA3ALF6-K3ALF6-ALF3 Melts

NASA Astrophysics Data System (ADS)

Tian, Zhongliang; Hu, Xun; Lai, Yanqing; Yang, Shu; Ye, Shaolong; Li, Jie

The electrolyte with high solubility for Sc2O3 is very important to realize the preparation of Al-Sc master alloy by the molten salt electrolysis. The solubility of Sc2O3 in K3AlF6-Na3AlF6-AlF3 melts is determined with an isothermal saturation method. The effects of KR (ratio of K3AlF6 to K3AlF6+Na3AlF6), the concentration of Al2O3 and the temperature on the solubility of Sc2O3 are also investigated. The results indicate that the solubility of Sc2O3 in K3AlF6-Na3AlF6-AlF3 melts increases and then decreases with KR increasing. The solubility of Sc2O3 is 8.698 wt.% in (K3AlF6-Na3AlF6)(KR25%)-18 wt.%AlF3 melts at 940°C. The effect of temperature on the solubility is little, and the values are 8.575 wt.% and 8.762 wt.% respectively when the temperatures are 930°C and 960°C. The solubility decreases from 8.809 wt.% to 7.058 wt.% as the concentration of Al2O3 increases from 1.5 wt.% to 5.0 wt.% at 950°C.

Magnetic ground state of the layered honeycomb compound Na2Co2TeO6

NASA Astrophysics Data System (ADS)

Bera, A. K.; Yusuf, S. M.

2018-04-01

The magnetic correlations in the 2D layered honeycomb compound Na2Co2TeO6 has been investigated. The temperature dependent susceptibility curve reveals a transition to the magnetically ordered state at TN ˜ 25 K. The temperature dependent neutron diffraction study confirms an antiferromagnetic ordering below TN. The magnetic ground state is determined to be a zigzag antiferromagnet that appears due to competing exchange interactions beyond nearest neighbors. The moments align along the crystallographic b axis with reduced ordered magnetic moment values of 2.72(2) μB/Co2+ and 2.52(3) μB/Co2+ for two Co sites, respectively. In comparison to the theoretical phase diagram the determined zigzag antiferromagnetic ground state suggests that the compound Na2Co2TeO6 is situated in the proximity to the quantum spin liquid state in the phase diagram.

MnO2 nanorods/SiO2 sphere coated on single-wall carbon nanotubes as supercapacitor electrode for high energy storage applications

NASA Astrophysics Data System (ADS)

Iro, Zaharaddeen S.; Subramani, C.; Kesavan, T.; Dash, S. S.; Sasidharan, M.; Sundramoorthy, Ashok K.

2017-12-01

A composite of MnO2/SiO2 sphere was coated on single-wall carbon nanotubes (MnO2/SiO2/SWCNT) using one-pot hydrothermal synthesis method. KMnO4 was used as an oxidizing agent for mild functionalization of single-wall carbon nanotubes (SWCNT), and also as a precursor of MnO2. A comparative study in the presence of SiO2 and SWCNT was carried out using bare MnO2 as a reference. After addition of SiO2, the composite obtained showed an increase in both the specific capacitance and cycle life which can be associated with spherical shape of SiO2 which offered reduction sites for MnO2. With the addition of SWCNT less than 5%, the composite further showed an increase in capacitance and cycle life, this is because of the good conductive nature, excellent mechanical property and chemical stability of SWCNT. The electrochemical behaviour was studied using cyclic voltammetry and galvanostatic charge/discharge method in 1 M Na2SO4 electrolyte. The specific capacitance of MnO2, MnO2/SiO2 and MnO2/SiO2/SWCNT composite is 73.6 F g-1, 108.7 F g-1 and 136 F g-1 at a current density of 1 A g-1, respectively. The MnO2/SiO2/SWCNT energy density was 68 Wh kg-1 with power density of 444.4 W kg-1. The MnO2/SiO2/SWCNT composite retained 88% of its specific capacitance after 500 cycles. We envisage that this hybrid material could be applied for preparation of supercapacitor electrode.

Crystallization kinetics of bioactive glasses in the ZnO-Na2O-CaO-SiO2 system.

PubMed

Malavasi, Gianluca; Lusvardi, Gigliola; Pedone, Alfonso; Menziani, Maria Cristina; Dappiaggi, Monica; Gualtieri, Alessandro; Menabue, Ledi

2007-08-30

The crystallization kinetics of Na(2)O.CaO.2SiO(2) (x = 0) and 0.68ZnO.Na(2)O.CaO.2SiO(2) (x = 0.68, where x is the ZnO stoichiometric coefficient in the glass formula) bioactive glasses have been studied using both nonisothermal and isothermal methods. The results obtained from isothermal XRPD analyses have showed that the first glass crystallizes into the isochemical Na(2)CaSi(2)O(6) phase, whereas the Na(2)ZnSiO(4) crystalline phase is obtained from the Zn-rich glass, in addition to Na(2)CaSi(2)O(6). The activation energy (Ea) for the crystallization of the Na(2)O.CaO.2SiO(2) glass is 193 +/- 10 and 203 +/- 5 kJ/mol from the isothermal in situ XRPD and nonisothermal DSC experiments, respectively. The Avrami exponent n determined from the isothermal method is 1 at low temperature (530 degrees C), and its value increases linearly with temperature increase up to 2 at 607 degrees C. For the crystallization of Na(2)CaSi(2)O(6) from the Zn-containing glass, higher values of both the crystallization temperature (667 and 661 degrees C) and Ea (223 +/- 10 and 211 +/- 5 kJ/mol) have been found from the isothermal and nonisothermal methods, respectively. The Na(2)ZnSiO(4) crystalline phase crystallizes at lower temperature with respect to Na(2)CaSi(2)O(6), and the Ea value is 266 +/- 20 and 245 +/- 15 kJ/mol from the isothermal and nonisothermal methods, respectively. The results of this work show that the addition of Zn favors the crystallization from the glass at lower temperature with respect to the Zn-free glass. In fact, it causes an increase of Ea for the Na diffusion process, determined using MD simulations, and consequently an overall increase of Ea for the crystallization process of Na(2)CaSi(2)O(6). Our results show good agreement between the Ea and n values obtained with the two different methods and confirm the reliability of the nonisothermal method applied to kinetic crystallization of glassy systems. This study allows the determination of the temperature

SnO2, IrO2, Ta2O5, Bi2O3, and TiO2 nanoparticle anodes: electrochemical oxidation coupled with the cathodic reduction of water to yield molecular H2

NASA Astrophysics Data System (ADS)

Choi, Jina; Qu, Yan; Hoffmann, Michael R.

2012-08-01

In recent years, the search for environmentally friendly alternative energy sources with reduced carbon footprints has increased. The coupling of photovoltaic power sources with advanced electrolysis systems for hydrogen production via water splitting using organic contaminants as sacrificial electron donors has been considered to a be viable alternative. In this report, we demonstrated the feasibility of a scaled-up rooftop prototype of the proposed hybrid photovoltaic-electrolysis system, which utilizes semiconductor nanoparticles coated on to metal substrates as electrodes for the generation of hydrogen coupled with the oxidation of wastewater. Application of an anodic bias of >2.0 V to bismuth-doped TiO2 (BiO x -TiO2) on Ti metal anodes with a sequential under-coatings of nanoparticulate SnO2, IrO2, Ta2O5, and Bi2O3 results in the electrochemical degradation of a variety of organic chemical contaminants in water (i.e., rhodamine B (Rh.B), methylene blue (MB), salicylic acid, triclosan, and phenol) and actual wastewater from a chemical manufacturing plant, while at the same time, molecular hydrogen is produced at stainless steel (SS) cathodes. The kinetics of the anodic substrates oxidation is investigated as a function of the cell current ( I cell), substrate concentration, and background electrolyte composition (e.g., NaCl, Na2SO4, or seawater). Average current efficiencies were found to be in the range of 4-22 %, while the cathodic current and energy efficiencies for hydrogen production were found to be in the range of 50-70 % and 20-40 %, respectively.

Wettability, structural and optical properties investigation of TiO{sub 2} nanotubular arrays

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zalnezhad, E., E-mail: erfan@hanyang.ac.kr; Maleki, E.; Banihashemian, S.M.

2016-06-15

Graphical abstract: FESEM images of the TiO 2 nanotube layers formed at 0.5 wt% NH4F/ glycerol. - Highlights: • Structural property investigation of TiO{sub 2} nanotube. • Evaluation of wettability of TiO{sub 2} nanotube. • Study on optical properties of TiO{sub 2} nanotube. • The effect of anatase phase on optical and wettability properties of TiO{sub 2.} - Abstract: In this study, the effect of microstructural evolution of TiO{sub 2} nanotubular arrays on wettability and optical properties was investigated. Pure titanium was deposited on silica glass by PVD magnetron sputtering technique. The Ti coated substrates were anodized in an electrolytemore » containing NH{sub 4}F/glycerol. The structures of the ordered anodic TiO{sub 2} nanotubes (ATNs) as long as 175 nm were studied using field emission scanning electron microscopy (FESEM) and X-ray diffraction (XRD). The result shows a sharp peak in the optical absorbance spectra around the band gap energy, 3.49–3.42 eV for annealed and non-annealed respectively. The thermal process induced growth of the grain size, which influence on the density of particles and the index of refraction. Furthermore, the wettability tests' result displays that the contact angle of intact substrate (θ = 74.7°) was decreased to 31.4° and 17.4° after anodization for amorphous and heat treated (450 °C) ANTs coated substrate, respectively.« less

Co-Precipitation Synthesis and Characterization of SrBi2Ta2O9 Ceramic

NASA Astrophysics Data System (ADS)

Afqir, Mohamed; Tachafine, Amina; Fasquelle, Didier; Elaatmani, Mohamed; Carru, Jean-Claude; Zegzouti, Abdelouahad; Daoud, Mohamed

2018-04-01

Strontium bismuth tantalate (SrBi2Ta2O9) was synthesized by a co-precipitation method. The sample was characterized by x-ray powder diffraction patterns (XRD), Fourier-transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). The results of the dielectric properties are reported at room temperature. No secondary phases were found while heating the powder at 850°C and the pure SrBi2Ta2O9 phase was formed, as revealed by XRD. The characteristic bands for SrBi2Ta2O9 were observed by FTIR at approximately 619 cm-1 and 810 cm-1. SEM micrographs for the sample displayed thin plate-like grains. The grain size was less than 1 μm and the crystallite size of about 24 nm. Dielectric response at room temperature shows that the SrBi2Ta2O9 ceramic has low loss values, and the flattening of the dielectric constant at higher frequencies. The observed Curie temperature is comparable with those reported in the literature.

Enhanced field emission properties of tilted graphene nanoribbons on aggregated TiO{sub 2} nanotube arrays

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hung, Shang-Chao, E-mail: schung99@gmail.com; Chen, Yu-Jyun

2016-07-15

Highlights: • Graphene nanoribbons (GNBs) slanted on aggregate TiO{sub 2} nanotube (A-TNTs) as field-emitters. • Turn-on electric field and field enhancement factor β are dependent on the substrate morphology. • Various quantities of GNRs are deposited on top of A-TNTs (GNRs/A-TNTs) with different morphologies. • With an increase of GNBs compositions, the specimens' turn-on electric field is reduced to 2.8 V/μm. • The field enhancement factor increased rapidly to about 1964 with the addition of GNRs. - Abstract: Graphene nanoribbons (GNRs) slanted on aggregate TiO{sub 2} nanotube arrays (A-TNTs) with various compositions as field-emitters are reported. The morphology, crystalline structure,more » and composition of the as-obtained specimens were characterized by field-emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD) and Raman spectrometry. The dependence of the turn-on electric field and the field enhancement factor β on substrate morphology was studied. An increase of GNRs reduces the specimens’ turn-on electric field to 2.8 V/μm and the field enhancement factor increased rapidly to about 1964 with the addition of GNRs. Results show a strong dependence of the field emission on GNR composition aligned with the gradient on the top of the A-TNT substrate. Enhanced FE properties of the modified TNTs can be mainly attributed to their improved electrical properties and rougher surface morphology.« less

Thin layer of ordered boron-doped TiO2 nanotubes fabricated in a novel type of electrolyte and characterized by remarkably improved photoactivity

NASA Astrophysics Data System (ADS)

Siuzdak, Katarzyna; Szkoda, Mariusz; Lisowska-Oleksiak, Anna; Grochowska, Katarzyna; Karczewski, Jakub; Ryl, Jacek

2015-12-01

This paper reports a novel method of boron doped titania nanotube arrays preparation by electrochemical anodization in electrolyte containing boron precursor - boron trifluoride diethyl etherate (BF3 C4H10O), simultaneously acting as an anodizing agent. A pure, ordered TiO2 nanotubes array, as a reference sample, was also prepared in solution containing a standard etching compound: ammonium fluoride. The doped and pure titania were characterized by scanning electron microscopy, UV-vis spectroscopy, Raman spectroscopy, X-ray photoelectron spectroscopy, photoluminescence emission spectroscopy and by means of electrochemical methods. The B-doping decidedly shifts the absorption edge of TiO2 nanotubes towards the visible light region and significantly inhibits the radiative recombination processes. Despite the fact that the doped sample is characterized by 4.6 lower real surface area when compared to pure titania, it leads to the decomposition of methylene blue in 93%, that is over 2.3 times higher than the degradation efficiency exhibited by the undoped material. The formation rate of hydroxyl radicals (rad OH) upon illumination significantly favours boron doped titania as a photocatalytic material. Moreover, the simple doping of TiO2 nanotubes array results in the enhancement of generated photocurrent from 120 μA/cm2 to 350 μA/cm2 registered for undoped and doped electrode, respectively.

A facile one-step synthesis of Mn{sub 3}O{sub 4} nanoparticles-decorated TiO{sub 2} nanotube arrays as high performance electrode for supercapacitors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Jianfang; Wang, Yan; Key Laboratory of Advance Functional Materials and Devices of Anhui Province, Hefei 230009

Via a facile one-step chemical bath deposition route, homogeneously dispersed Mn{sub 3}O{sub 4} nanoparticles have been successfully deposited onto the inner surface of TiO{sub 2} nanotube arrays (TNAs). The content and size of Mn{sub 3}O{sub 4} can be controlled by changing the deposition time. Field emission scanning electron microscopy and transmission electron microscopy analysis reveal the morphologies structures of Mn{sub 3}O{sub 4}/TNAs composites. The crystal-line structures are characterized by the X-ray diffraction patterns and Raman spectra. X-ray photoelectron spectroscopy further confirms the valence states of the sample elements. The electrochemical properties of Mn{sub 3}O{sub 4}/TNAs electrodes are systematically investigated bymore » the combine use of cyclic voltammetry, galvanostatic charge-discharge and electrochemical impedance spectroscopy. The resulting Mn{sub 3}O{sub 4}/TNAs electrode prepared by deposition time of 3 h shows the highest specific capacitance of 570 F g{sup −1} at a current density of 1 A g{sup −1}. And it also shows an excellent long-term cycling stability at a current density of 5 A g{sup −1}, which remaining 91.8% of the initial capacitance after 2000 cycles. Thus this kind of Mn{sub 3}O{sub 4} nanoparticles decorated TNAs may be considered as an alternative promising candidate for high performance supercapacitor electrodes. - Graphical abstract: Mn{sub 3}O{sub 4} nanoparticles have been uniformly deposited onto the inner surfaces of TiO{sub 2} nanotube arrays through a facile one-step chemical bath deposition method. As electrodes for supercapacitors, they exhibit a relatively high specific capacity and excellent cycling stability. - Highlights: • Mn{sub 3}O{sub 4} nanoparticles have been deposited onto TiO{sub 2} nanotube arrays by chemical bath deposition. • The Mn{sub 3}O{sub 4}/TNAs exhibits a highest specific capacitance of 570 F g{sup –1} at a current density of 1 A g{sup –1}. • The Mn{sub 3}O{sub 4

Wire-shaped perovskite solar cell based on TiO2 nanotubes

NASA Astrophysics Data System (ADS)

Wang, Xiaoyan; Kulkarni, Sneha A.; Li, Zhen; Xu, Wenjing; Batabyal, Sudip K.; Zhang, Sam; Cao, Anyuan; Wong, Lydia Helena

2016-05-01

In this work, a wire-shaped perovskite solar cell based on TiO2 nanotube (TNT) arrays is demonstrated for the first time by integrating a perovskite absorber on TNT-coated Ti wire. Anodization was adopted for the conformal growth of TNTs on Ti wire, together with the simultaneous formation of a compact TiO2 layer. A sequential step dipping process is employed to produce a uniform and compact perovskite layer on top of TNTs with conformal coverage as the efficient light absorber. Transparent carbon nanotube film is wrapped around Ti wire as the hole collector and counter electrode. The integrated perovskite solar cell wire by facile fabrication approaches shows a promising future in portable and wearable textile electronics.

Electrical Conductivity of Cancrinite-Type Na8 - 2 x Ca x [Al6Si6O24][CO3] · 2H2O ( x ≤ 0.03) Crystals

NASA Astrophysics Data System (ADS)

Sorokin, N. I.

2018-05-01

The electrical conductivity of crystals of artificial cancrinite Na8 - 2 x Ca x [Al6Si6O24][CO3] · 2H2O ( x ≤ 0.03) has been studied in the temperature range of 498-604 K. These crystals were grown by hydrothermal synthesis on a seed in the Na2O-Al2O3-SiO2-H2O system ( t = 380-420°C, P = 3 × 107-9 × 107 Pa). The ionic conductivity of a single-crystal sample (sp. gr. P63), measured along the crystallographic axis c, is low: σ = 8 × 10-7 S/cm at 300°C. The electric transport activation energy is E a = 0.81 ± 0.05 eV. The relationship between the ionic conductivity and specific features of the atomic structure of cancrinites is discussed.

High pressure synthesis of amorphous TiO2 nanotubes

NASA Astrophysics Data System (ADS)

Li, Quanjun; Liu, Ran; Wang, Tianyi; Xu, Ke; Dong, Qing; Liu, Bo; Liu, Jing; Liu, Bingbing

2015-09-01

Amorphous TiO2 nanotubes with diameters of 8-10 nm and length of several nanometers were synthesized by high pressure treatment of anatase TiO2 nanotubes. The structural phase transitions of anatase TiO2 nanotubes were investigated by using in-situ high-pressure synchrotron X-ray diffraction (XRD) method. The starting anatase structure is stable up to ˜20GPa, and transforms into a high-density amorphous (HDA) form at higher pressure. Pressure-modified high- to low-density transition was observed in the amorphous form upon decompression. The pressure-induced amorphization and polyamorphism are in good agreement with the previous results in ultrafine TiO2 nanoparticles and nanoribbons. The relationship between the LDA form and α-PbO2 phase was revealed by high-resolution transmission electron microscopy (HRTEM) study. In addition, the bulk modulus (B0 = 158 GPa) of the anatase TiO2 nanotubes is smaller than those of the corresponding bulks and nanoparticles (180-240 GPa). We suggest that the unique open-ended nanotube morphology and nanosize play important roles in the high pressure phase transition of TiO2 nanotubes.

Xanthine oxidase functionalized Ta2O5 nanostructures as a novel scaffold for highly sensitive SPR based fiber optic xanthine sensor.

PubMed

Kant, Ravi; Tabassum, Rana; Gupta, Banshi D

2018-01-15

Fabrication and characterization of a surface plasmon resonance based fiber optic xanthine sensor using entrapment of xanthine oxidase (XO) enzyme in several nanostructures of tantalum (v) oxide (Ta 2 O 5 ) have been reported. Chemical route was adopted for synthesizing Ta 2 O 5 nanoparticles, nanorods, nanotubes and nanowires while Ta 2 O 5 nanofibers were prepared by electrospinning technique. The synthesized Ta 2 O 5 nanostructures were characterized by photoluminescence, scanning electron microscopy, UV-Visible spectra and X-ray diffraction pattern. The probes were fabricated by coating an unclad core of the fiber with silver layer followed by the deposition of XO entrapped Ta 2 O 5 nanostructures. The crux of sensing mechanism relies on the modification of dielectric function of sensing layer upon exposure to xanthine solution of diverse concentrations, reflected in terms of shift in resonance wavelength. The sensing probe coated with XO entrapped Ta 2 O 5 nanofibers has been turned out to possess maximum sensitivity amongst the synthesized nanostructures. The probe was optimized in terms of pH of the sample and the concentration of XO entrapped in Ta 2 O 5 nanofibers. The optimized sensing probe possesses a remarkably good sensitivity of 26.2nm/µM in addition to linear range from 0 to 3µM with an invincible LOD value of 0.0127µM together with a response time of 1min. Furthermore, probe selectivity with real sample analysis ensure the usage of the sensor for practical scenario. The results reported open a novel perspective towards a sensitive, rapid, reliable and selective detection of xanthine. Copyright © 2017 Elsevier B.V. All rights reserved.

Enhanced photoelectrochemical degradation of Ibuprofen and generation of hydrogen via BiOI-deposited TiO2 nanotube arrays.

PubMed

Chen, Hanlin; Peng, Yen-Ping; Chen, Ting-Yu; Chen, Ku-Fan; Chang, Ken-Lin; Dang, Zhi; Lu, Gui-Ning; He, Hongping

2018-08-15

This study employed BiOI-deposited TiO 2 nanotube arrays (BiOI-TNTAs) electrode in a photoelectrochemical (PEC) system to oxidize Ibuprofen and generate hydrogen in the anodic and cathodic chamber, respectively. FESEM results revealed the diameter of TiO 2 nanotubes was 90-110nm. According to the XRD analysis, the BiOI-TNTAs were dominated by the anatase phase and tetragonal structure of BiOI. XPS results confirmed the coexistence of BiOI in the BiOI-TNTAs associated with Bi (33.76%) and I (8.81%). UV-vis absorption spectra illustrated BiOI-TNTAs exhibit strong absorptions in the visible light region. The PEC method showed the best degradation efficiency for Ibuprofen is a rate constant of 3.21×10 -2 min -1 . The results of the Nyquist plot revealed the recombination of photogenerated electron-hole pairs was inhibited as the bias potential was applied. Furthermore, the Bode plot demonstrated the lifetime (τ el ) of photoexcited electrons of BiOI-TNTAs was 1.8 and 4.1 times longer than that of BiOI-Ti and TNTAs, respectively. In the cathodic chamber, the amount of hydrogen generation reached 219.94μM/cm 2 after 3h of reaction time. Copyright © 2018 Elsevier B.V. All rights reserved.

Interfacial Engineered Polyaniline/Sulfur-Doped TiO2 Nanotube Arrays for Ultralong Cycle Lifetime Fiber-Shaped, Solid-State Supercapacitors.

PubMed

Li, Chun; Wang, Zhuanpei; Li, Shengwen; Cheng, Jianli; Zhang, Yanning; Zhou, Jingwen; Yang, Dan; Tong, Dong-Ge; Wang, Bin

2018-05-30

Fiber-shaped supercapacitors (FSCs) have great promises in wearable electronics applications. However, the limited specific surface area and inadequate structural stability caused by the weak interfacial interactions of the electrodes result in relatively low specific capacitance and unsatisfactory cycle lifetime. Herein, solid-state FSCs with high energy density and ultralong cycle lifetime based on polyaniline (PANI)/sulfur-doped TiO 2 nanotube arrays (PANI/S-TiO 2 ) are fabricated by interfacial engineering. The experimental results and ab initio calculations reveal that S doping can effectively promote the conductivity of titania nanotubes and increase the binding energy of PANI anchored on the electrode surface, leading to a much stronger binding of PANI on the surface of the electrode and excellent electrode structure stability. As a result, the FSCs using the PANI/S-TiO 2 electrodes deliver a high specific capacitance of 91.9 mF cm -2 , a capacitance retention of 93.78% after 12 000 charge-discharge cycles, and an areal energy density of 3.2 μW h cm -2 . Meanwhile, the all-solid-state FSC device retains its excellent flexibility and stable electrochemical capacitance even after bending 150 cycles. The enhanced performances of FSCs could be attributed to the large surface area, reduced ion diffusion path, improved electrical conductivity, and engineered interfacial interaction of the rationally designed electrodes.

Structural studies on a high-pressure polymorph of NaYSi 2O 6

NASA Astrophysics Data System (ADS)

Kahlenberg, Volker; Konzett, Jürgen; Kaindl, Reinhard

2007-06-01

High-pressure synthesis experiments in the system Na 2O-Y 2O 3-SiO 2 revealed the existence of a previously unknown polymorph of NaYSi 2O 6 or Na 3Y 3[Si 3O 9] 2 which was quenched from 3.0 GPa and 1000 °C. Structural investigations on this modification have been performed using single-crystal X-ray diffraction data collected at ambient conditions. Furthermore, unpolarized micro-Raman spectra have been obtained from single-crystal material. The high-P modification of NaYSi 2O 6 crystallizes in the centrosymmetric space group C2/ c with 12 formula units per cell ( a=8.2131(9) Å, b=10.3983(14) Å, c=17.6542(21) Å, β=100.804(9)°, V=1481.0(3) Å 3, R(| F|)=0.033 for 1142 independent observed reflections) and belongs to the group of cyclo-silicates. Basic building units are isolated three-membered [Si 3O 9] rings located in layers parallel to (010). Within a single layer the rings are concentrated in strings parallel to [100]. The sequence of directedness of up ( U) or down ( D) pointing tetrahedra of a single ring is UUU or DDD, respectively. Stacking of the layers parallel to b results in the formation of a three-dimensional structure in which yttrium and sodium cations are incorporated for charge compensation. In more detail, four non-tetrahedral cation positions can be differentiated which are coordinated by 6 and 8 oxygen ligands. Refinements of the site occupancies did not reveal any indication for mixed Na-Y populations on these positions. Finally, several geometrical parameters of rings occurring in cyclo-trisilicate structures have been compiled and are discussed.

Suppression of Leakage Current of Metal-Insulator-Semiconductor Ta2O5 Capacitors with Al2O3/SiON Buffer Layer

NASA Astrophysics Data System (ADS)

Tonomura, Osamu; Miki, Hiroshi; Takeda, Ken-ichi

2011-10-01

An Al2O3/SiO buffer layer was incorporated in a metal-insulator-semiconductor (MIS) Ta2O5 capacitor for dynamic random access memory (DRAM) application. Al2O3 was chosen for the buffer layer owing to its high band offset against silicon and oxidation resistance against increase in effective oxide thickness (EOT). It was clarified that post-deposition annealing in nitrogen at 800 °C for 600 s increased the band offset between Al2O3 and the lower electrode and decreased leakage current by two orders of magnitude at 1 V. Furthermore, we predicted and experimentally confirmed that there was an optimized value of y in (Si3N4)y(SiO2)(1-y), which is 0.58, for minimizing the leakage current and EOT of SiON. To clarify the oxidation resistance and appropriate thickness of Al2O3, a TiN/Ta2O5/Al2O3/SiON/polycrystalline-silicon capacitor was fabricated. It was confirmed that the lower electrode was not oxidized during the crystallization annealing of Ta2O5. By setting the Al2O3 thickness to 3.4 nm, the leakage current is lowered below the required value with an EOT of 3.6 nm.

A study on the resistance switching of Ag2Se and Ta2O5 heterojunctions using structural engineering

NASA Astrophysics Data System (ADS)

Lee, Tae Sung; Lee, Nam Joo; Abbas, Haider; Hu, Quanli; Yoon, Tae-Sik; Lee, Hyun Ho; Le Shim, Ee; Kang, Chi Jung

2018-01-01

The resistive random access memory (RRAM) devices with heterostuctures have been investigated due to cycling stability, nonlinear switching, complementary resistive switching and self-compliance. The heterostructured devices can modulate the resistive switching (RS) behavior appropriately by bilayer structure with a variety of materials. In this study, the bipolar resistive switching characteristics of the bilayer structures composed of Ta2O5 and Ag2Se, which are transition-metal oxide (TMO) and silver chalcogenide, were investigated. The bilayer devices of Ta2O5 deposited on Ag2Se (Ta2O5/Ag2Se) and Ag2Se deposited on Ta2O5 (Ag2Se/Ta2O5) were fabricated for investigation of the RS characteristics by stacking sequence of Ta2O5 and Ag2Se. All operating voltages were applied to the Ag top electrode with the Pt bottom electrode grounded. The Ta2O5/Ag2Se device showed that a negative voltage sweep switched the device from high resistance state (HRS) to low resistance state (LRS) and a positive voltage sweep switched the device from LRS to HRS. On the contrary, for the Ag2Se/Ta2O5 device a positive voltage sweep switched the device from HRS to LRS, and a negative voltage sweep switched it from LRS to HRS. The polarity dependence of RS was attributed to the stacking sequence of Ta2O5 and Ag2Se. In addition, the combined heterostructured device of both bilayer stacks, Ta2O5/Ag2Se and Ag2Se/Ta2O5, exhibited the complementary switching characteristics. By using threshold switching devices, sneak path leakage can be reduced without additional selectors. The bilayer heterostructures of Ta2O5 and Ag2Se have various advantages such as self-compliance, reproducibility and forming-free stable RS. It confirms the possible applications of TMO and silver chalcogenide heterostructures in RRAM.

Effect of Al gate on the electrical behaviour of Al-doped Ta2O5 stacks

NASA Astrophysics Data System (ADS)

Skeparovski, A.; Novkovski, N.; Atanassova, E.; Paskaleva, A.; Lazarov, V. K.

2011-06-01

The electrical behaviour of Al-doped Ta2O5 films on nitrided silicon and implemented in Al-gated MIS capacitors has been studied. The dopant was introduced into the Ta2O5 through its surface by deposing a thin Al layer on the top of Ta2O5 followed by an annealing process. The HRTEM images reveal that the initial double-layer structure of the stacks composed of doped Ta2O5 and interfacial SiON layer undergoes changes during the formation of the Al gate and transforms into a three-layer structure with an additional layer between the Al electrode and the doped Ta2O5. This layer, being a result of reaction between the Al gate and the Al-doped Ta2O5, affects the overall electrical properties of the stacks. Strong charge trapping/detrapping processes have been established in the vicinity of the doped Ta2O5/SiON interface resulting in a large C-V hysteresis effect. The charge trapping also influences the current conduction in the layers keeping the current density level rather low even at high electric fields (J < 10-6 A cm-2 at 7 MV cm-1). By employing a three-layer model of the stack, the permittivity of both, the Al-doped Ta2O5 and the additional layer, has been estimated and the corresponding conduction mechanisms identified.

Na2Ti6O13: a potential anode for grid-storage sodium-ion batteries.

PubMed

Rudola, Ashish; Saravanan, Kuppan; Devaraj, Sappani; Gong, Hao; Balaya, Palani

2013-08-28

The ultra-fast (30C or 2 min) rate capability and impressive long cycle life (>5000 cycles) of Na2Ti6O13 are reported. A stable 2.5 V sodium-ion battery full cell is demonstrated. In addition, the sodium storage mechanism and thermal stability of Na2Ti6O13 are discussed.

Self-Organized Formation of Short TiO2 Nanotube Arrays By Complete Anodization of Ti Thin Films

NASA Astrophysics Data System (ADS)

Okada, Masahisa; Tajima, Kazuki; Yamada, Yasusei; Yoshimura, Kazuki

We investigate the self-organized growth of short TiO2 nanotubes by complete anodization of Ti thin films deposited on Si substrates in ethylene glycol electrolytes with small addition of NH4F. During the anodization process, real-time inspection of the current transient is performed to anodize the Ti films completely. X-ray photoelectron spectroscopy and scanning electron microscopy are employed to characterize the resulting samples. We find that the length of the formed TiO2 nanotubes is governed by the thickness of Ti thin films independently of the tube diameter. Short TiO2 nanotubes are also found to be stable up to 550 °C in air atmosphere even after crystallization to rutile.

O-GlcNAc-mediated interaction between VER2 and TaGRP2 elicits TaVRN1 mRNA accumulation during vernalization in winter wheat

PubMed Central

Xiao, Jun; Xu, Shujuan; Li, Chunhua; Xu, Yunyuan; Xing, Lijing; Niu, Yuda; Huan, Qing; Tang, Yimiao; Zhao, Changping; Wagner, Doris; Gao, Caixia; Chong, Kang

2014-01-01

Vernalization, sensing of prolonged cold, is important for seasonal flowering in eudicots and monocots. While vernalization silences a repressor (FLC, MADS-box transcription factor) in eudicots, it induces an activator (TaVRN1, an AP1 clade MADS-box transcription factor) in monocots. The mechanism for TaVRN1 induction during vernalization is not well understood. Here we reveal a novel mechanism for controlling TaVRN1 mRNA accumulation in response to prolonged cold sensing in wheat. The carbohydrate-binding protein VER2, a jacalin lectin, promotes TaVRN1 upregulation by physically interacting with the RNA-binding protein TaGRP2. TaGRP2 binds to TaVRN1 pre-mRNA and inhibits TaVRN1 mRNA accumulation. The physical interaction between VER2 and TaGRP2 is controlled by TaGRP2 O-GlcNAc modification, which gradually increases during vernalization. The interaction between VER2 and O-GlcNAc-TaGRP2 reduces TaGRP2 protein accumulation in the nucleus and/or promotes TaGRP2 dissociation from TaVRN1, leading to TaVRN1 mRNA accumulation. Our data reveal a new mechanism for sensing prolonged cold in temperate cereals. PMID:25091017

Making Carbon-Nanotube Arrays Using Block Copolymers: Part 2

NASA Technical Reports Server (NTRS)

Bronikowski, Michael

2004-01-01

Some changes have been incorporated into a proposed method of manufacturing regular arrays of precisely sized, shaped, positioned, and oriented carbon nanotubes. Such arrays could be useful as mechanical resonators for signal filters and oscillators, and as electrophoretic filters for use in biochemical assays. A prior version of the method was described in Block Copolymers as Templates for Arrays of Carbon Nanotubes, (NPO-30240), NASA Tech Briefs, Vol. 27, No. 4 (April 2003), page 56. To recapitulate from that article: As in other previously reported methods, carbon nanotubes would be formed by decomposition of carbon-containing gases over nanometer-sized catalytic metal particles that had been deposited on suitable substrates. Unlike in other previously reported methods, the catalytic metal particles would not be so randomly and densely distributed as to give rise to thick, irregular mats of nanotubes with a variety of lengths, diameters, and orientations. Instead, in order to obtain regular arrays of spaced-apart carbon nanotubes as nearly identical as possible, the catalytic metal particles would be formed in predetermined regular patterns with precise spacings. The regularity of the arrays would be ensured by the use of nanostructured templates made of block copolymers.

Co(OH)2/RGO/NiO sandwich-structured nanotube arrays with special surface and synergistic effects as high-performance positive electrodes for asymmetric supercapacitors.

PubMed

Xu, Han; Zhang, Chi; Zhou, Wen; Li, Gao-Ren

2015-10-28

High power density, high energy density and excellent cycling stability are the main requirements for high-performance supercapacitors (SCs) that will be widely used for portable consumer electronics and hybrid electric vehicles. Here we investigate novel types of hybrid Co(OH)2/reduced graphene oxide (RGO)/NiO sandwich-structured nanotube arrays (SNTAs) as positive electrodes for asymmetric supercapacitors (ASCs). The synthesized Co(OH)2/RGO/NiO SNTAs exhibit a significantly improved specific capacity (∼1470 F g(-1) at 5 mV s(-1)) and excellent cycling stability with ∼98% Csp retention after 10 000 cycles because of the fast transport and short diffusion paths for electroactive species, the high utilization rate of electrode materials, and special synergistic effects among Co(OH)2, RGO, and NiO. The high-performance ASCs are assembled using Co(OH)2/RGO/NiO SNTAs as positive electrodes and active carbon (AC) as negative electrodes, and they exhibit a high energy density (115 Wh kg(-1)), a high power density (27.5 kW kg(-1)) and an excellent cycling stability (less 5% Csp loss after 10 000 cycles). This study shows an important breakthrough in the design and fabrication of multi-walled hybrid nanotube arrays as positive electrodes for ASCs.

Studies on solid solutions based on layered honeycomb-ordered phases P2-Na{sub 2}M{sub 2}TeO{sub 6} (M=Co, Ni, Zn)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Berthelot, Romain; Schmidt, Whitney; Sleight, A.W.

2012-12-15

Three complete solid solutions between the layered phases P2-Na{sub 2}M{sub 2}TeO{sub 6} (M=Co, Ni, Zn) have been prepared by conventional solid state method and investigated through X-ray diffraction, magnetism and optical measurements. All compositions are characterized by a M{sup 2+}/X{sup 6+} honeycomb ordering within the slabs and crystallize in a hexagonal unit cell. However, a structural transition based on a different stacking is observed as nickel (space group P6{sub 3}/mcm) is substituted by zinc or cobalt (space group P6{sub 3}22). All compositions exhibit a paramagnetic Curie-Weiss behavior at high temperatures; and the magnetic moment values confirm the presence of Ni{supmore » 2+} and/or Co{sup 2+} cations. The low-temperature antiferromagnetic order of Na{sub 2}Ni{sub 2}TeO{sub 6} and Na{sub 2}Co{sub 2}TeO{sub 6} is suppressed by zinc substitution. The color of the obtained compositions varies from pink, to light green and white when M=Co, Ni, Zn, respectively. - Graphical abstract: The comparison between the structure of Na{sub 2}Ni{sub 2}TeO{sub 6} (left) and Na{sub 2}M{sub 2}TeO{sub 6} (M=Co, Zn) (right) evidences the stacking difference with distinct atom sequences along the hexagonal c-axis. Highlights: Black-Right-Pointing-Pointer Solid solutions between lamellar phases Na{sub 2}M{sub 2}TeO{sub 6} (M=Co, Ni, Zn) are investigated. Black-Right-Pointing-Pointer A M{sup 2+}/X{sup 6+} honeycomb ordering characterized all the compositions. Black-Right-Pointing-Pointer A structural transition is shown when Ni is replaced by Co or Zn. Black-Right-Pointing-Pointer The low-temperature AFM ordering of Na{sub 2}Ni{sub 2}TeO{sub 6} and Na{sub 2}Co{sub 2}TeO{sub 6} is suppressed by zinc substitution. Black-Right-Pointing-Pointer Color changes from pink to light green and white when M=Co, Ni, Zn, respectively.« less

Hybrid MnO2/carbon nanotube-VN/carbon nanotube supercapacitors

NASA Astrophysics Data System (ADS)

Su, Y.; Zhitomirsky, I.

2014-12-01

Composite materials, containing fibrous VN nanoparticles and multiwalled carbon nanotubes (MWCNT) are prepared by a chemical method for application in electrochemical supercapacitors. We demonstrate for the first time that VN-MWCNT electrodes exhibit good capacitive behavior in 0.5 M Na2SO4 electrolyte in a negative voltage window of 0.9 V. Quartz crystal microbalance studies provide an insight into the mechanism of charge storage. Composite VN-MWCNT materials show significant improvement in capacitance, compared to individual VN and MWCNT materials. Testing results indicate that VN-MWCNT electrodes exhibit high specific capacitance at high mass loadings in the range of 10-30 mg cm-2, good capacitance retention at scan rates in the range of 2-200 mV s-1 and good cycling stability. The highest specific capacitance of 160 F g-1 is achieved at a scan rate of 2 mV s-1. The new findings open a new and promising strategy in the fabrication of hybrid devices based on VN. The proof-of-principle is demonstrated by the fabrication of hybrid supercapacitor devices based on VN-MWCNT negative electrodes and MnO2 -MWCNT positive electrodes with voltage window of 1.8 V in aqueous 0.5 M Na2SO4 electrolyte. The hybrid VN-MWCNT/MnO2-MWCNT supercapacitor cells show promising capacitive and power-energy characteristics.

Anchorage of γ-Al 2O 3 nanoparticles on nitrogen-doped multiwalled carbon nanotubes

DOE PAGES

Rodríguez-Pulido, A.; Martínez-Gutiérrez, H.; Calderon-Polania, G. A.; ...

2016-06-07

Nitrogen-doped multiwalled carbon nanotubes (CNx-MWNTs) have been decorated with γ-Al 2O 3 nanoparticles by a novel method. This process involved a wet chemical approach in conjunction with thermal treatment. During the particle anchoring process, individual CNx-MWNT nanotubes agglomerated into bundles, resulting in arrays of aligned CNx-MWNT coated with γ-Al 2O 3. Extensive characterization of the resulting γ-Al 2O 3/CNx-MWNT bundles was performed using a range of electron microscopy imaging and microanalytical techniques. In conclusion, a possible mechanism explaining the nanobundle alignment is described, and possible applications of these materials for the fabrication of ceramic composites using CNx-MWNTs are briefly discussed.

New Defective Brannerite-Type Vanadates. I. Synthesis and Study of Mn 1- x- yφ xNa yV 2-2 x-yMo 2 x+yO 6 Solid Solutions

NASA Astrophysics Data System (ADS)

Masłowska, Bogna; Ziółkowski, Jacek

1994-05-01

MnV 2O 6 of the brannerite-type structure (below 540°C) doped with MoO 3 and Na 2O forms isomorphous solid solutions MnNaφ = Mn 1- x-yφ xNa yV 2-2 x-yMo 2 x+ yO 6 (φ cation vacancy in the original Mn position), belonging to the pseudoternary MnV 2O 6-NaVMoO 6-MoO 3 system. Particular cases are MnNa = Mn 1- yNa y V 2- yMo yO 6 ( x = 0), Mnφ = Mn 1- xφ xV 2-2 xMo 2 xO 6 ( y = 0), and Naφ = Na 1- xφ xV 1- xMo 1+ xO 6 ( x + y = 1). MnV 2O 6 and NaVMoO 6 show miscibility in the entire composition range (MnNa). The opposite boundary of MnNaφ passes through the (100 x, 100 y) points (45, 0), (33, 30), and (30, 70). The phase diagram of the pseudobinary MnV 2O 6-NaVMoO 6 system (determined with DTA) shows (i) a narrow double-lens-type solidus-liquidus gap at high values of y , (ii) two peritectic meltings at lower y (yielding the high temperature β-MnNa and Mn 2V 2O 7), and (iii) little area of β-MnNa. Lattice parameters of MnNa (determined with X-ray diffraction) reveal small deviations from Vegard's law. As the ionic radii of both dopants (Na + and Mo 6+) are, respectively, larger than those of mother ions (Mn 2+ and V 5+), the unit cell increases in all directions with rising y along the MnNa series of solid solutions. However, due to the anisotropy of the structure, parameter c is strongly sensitive to Na/Mn substitution, b is ruled by Mo/V, and a is weakly influenced by Mo/V. Close analogy to the behavior of the previously studied MnV 2O 6-LiVMoO 6-MoO 6 system is discussed.

Fabrication of transparent TiO2 nanotube-based photoanodes for CdS/CdTe quantum co-sensitized solar cells

NASA Astrophysics Data System (ADS)

Gualdrón-Reyes, A. F.; Cárdenas-Arenas, A.; Martínez, C. A.; Kouznetsov, V. V.; Meléndez, A. M.

2017-01-01

In order to fabricate a solar cell, ordered TiO2 nanotube (TNT) arrays were prepared by double anodization. TNT arrays with variable lengths were obtained by changing the duration of the anodizing process of up to 3h. TNT membranes were transferred to indium tin oxide substrates and attached with a B-TiO2 sol. TNT photoanode with the best photoelectrochemical performance was sensitized with CdS by SILAR method. On other hand, CdTe quantum dots prepared via colloidal synthesis were deposited on TNT photoanodes for 2h, 4h and 6h. In addition, TNT/CdS was loaded with CdTe quantum dots for 4 h. Morphology and chemical modification of TiO2 were characterized by FESEM and XPS, while their photoelectrochemical performance was measured by open-circuit photopotential and photovoltammetry under visible light. TiO2 nanotubes grown during 2.5h showed the highest photocurrent due to presence of Ti3+ donor states by N and F co-doping, increasing the number of photogenerated electrons transported to back collector. TNT/CdS/CdTe photoanode reach the highest conversion efficiency under AM 1.5G simulated solar illumination.

Optical phonon characteristics of an orthorhombic-transformed polymorph of CaTa2O6 single crystal fibre

NASA Astrophysics Data System (ADS)

Almeida, R. M.; Andreeta, M. R. B.; Hernandes, A. C.; Dias, A.; Moreira, R. L.

2014-03-01

Infrared-reflectivity spectroscopy and micro-Raman scattering were used to determine the optical phonon features of orthorhombic calcium tantalite (CaTa2O6) single crystal fibres. The fibres, obtained by the Laser-Heated Pedestal Growth method, grew into an ordered cubic structure \\left( Pm\\bar{3} \\right). Long-time annealing was used to induce a polymorphic transformation to an aeschynite orthorhombic structure (Pnma space group). The phase transformation led to the appearance of structural domains and micro-cracks, responsible for diffuse scattering and depolarization of the scattered light in the visible range, but not in the infrared region. Thus, polarized infrared spectroscopy could be performed within oriented single domains, with an appropriate microscope, allowing us to determine all relevant polar phonons of the orthorhombic CaTa2O6. The obtained phononic dielectric response, {{\\epsilon }_{r}} = 22.4 and = 86 × 103 GHz, shows the appropriateness of the material for microwave applications. Totally symmetric Raman modes could be resolved by polarization, after re-polishing the cracked sample surface.

Scaling of anomalous Hall effect in Ta/CoFeB/MgAl2O4/Ta multilayers

NASA Astrophysics Data System (ADS)

Wu, Yong; Zhang, Qimeng; Meng, Kangkang; Chen, Jikun; Xu, Xiaoguang; Miao, Jun; Jiang, Yong

2017-06-01

The anomalous Hall effect (AHE) is studied in Ta/CoFeB/MgAl2O4/Ta multilayers with different thicknesses of MgAl2O4 (t), which causes in-plane magnetic anisotropy (IMA) for t = 1.0 nm and perpendicular magnetic anisotropy (PMA) for t ≥ 1.2 nm. Conventional scaling was demonstrated to be not inadequate in our case. The origin of the AHE in Ta/CoFeB/MgAl2O4/Ta multilayers is mainly an extrinsic mechanism. The contribution of skew scattering (SS) is unneglectable, and both the SS and side jump are enhanced when the magnetic anisotropy changes from IMA to PMA, indicating that the oxidation at the interface of CoFeB/MgAl2O4 has a dominant influence on the AHE.

Generic Synthesis of Carbon Nanotube Branches on Metal Oxide Arrays Exhibiting Stable High-Rate and Long-Cycle Sodium-Ion Storage.

PubMed

Xia, Xinhui; Chao, Dongliang; Zhang, Yongqi; Zhan, Jiye; Zhong, Yu; Wang, Xiuli; Wang, Yadong; Shen, Ze Xiang; Tu, Jiangping; Fan, Hong Jin

2016-06-01

A new and generic strategy to construct interwoven carbon nanotube (CNT) branches on various metal oxide nanostructure arrays (exemplified by V2 O3 nanoflakes, Co3 O4 nanowires, Co3 O4 -CoTiO3 composite nanotubes, and ZnO microrods), in order to enhance their electrochemical performance, is demonstrated for the first time. In the second part, the V2 O3 /CNTs core/branch composite arrays as the host for Na(+) storage are investigated in detail. This V2 O3 /CNTs hybrid electrode achieves a reversible charge storage capacity of 612 mAh g(-1) at 0.1 A g(-1) and outstanding high-rate cycling stability (a capacity retention of 100% after 6000 cycles at 2 A g(-1) , and 70% after 10 000 cycles at 10 A g(-1) ). Kinetics analysis reveals that the Na(+) storage is a pseudocapacitive dominating process and the CNTs improve the levels of pseudocapacitive energy by providing a conductive network. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Synthesis of self-organized TiO{sub 2} nanotube arrays: Microstructural, stereoscopic, and topographic studies

DOE Office of Scientific and Technical Information (OSTI.GOV)

Quiroz, Heiddy P., E-mail: hpquirozg@unal.edu.co; Dussan, A., E-mail: adussanc@unal.edu.co

2016-08-07

In this work, titanium dioxide nanotubes were prepared by using titanium foils via electrochemical anodization in ethylene glycol solutions containing different amounts of water and fluoride in the ranges of 1%–3% and 0.15%–0.5%, respectively, to determine their effects on morphology, optical, and crystalline structure properties. Annealing processes were performed on all samples in the range between 273 and 723 K. Morphology and structure properties of the samples were studied by scanning electron microscopy, X-ray diffraction (XRD), and transmission electron microscopy. Titanium dioxide (TiO{sub 2}) nanotubes, through anodization method, are strongly influenced by conditions, like fluoride concentration and applied voltages. Tube lengthsmore » between 2 and 7 μm were obtained, exhibiting different diameters and wall thicknesses. When alternating voltage was applied, the outer surface of the nanotubes exhibited evenly spaced ring-shaped regions, while smooth tubes were observed when constant voltage was applied. Reflection peaks, corresponding to Brookite, Anatase, and Rutile, of TiO{sub 2} phases, were observed from the XRD pattern. These phases were corroborated via μXRD measurements, and the Ti{sub 3}O{sub 5} phase was also observed in detail. Absorption coefficient (α), optical band gap (Eg), and extinction coefficient (ε) of TiO{sub 2} nanotubes were calculated by transmittance spectra in the UV–Vis range. Strong absorption was noted in the UV region from reflectance and absorbance measurements. A correlation between synthesis parameters and physical properties is presented.« less

Exploring hierarchical FeS2/C composite nanotubes arrays as advanced cathode for lithium ion batteries

NASA Astrophysics Data System (ADS)

Pan, G. X.; Cao, F.; Xia, X. H.; Zhang, Y. J.

2016-11-01

Rational construction of advanced FeS2 cathode is one of research hotspots, and of great importance for developing high-performance lithium ion batteries (LIBs). Herein we report a facile hydrolysis-sulfurization method for fabrication of FeS2/C nanotubes arrays with the help of sacrificial Co2(OH)2CO3 nanowires template and glucose carbonization. Self-supported FeS2/C nanotubes consist of interconnected nanoburrs of 5-20 nm, and show hierarchical porous structure. The FeS2/C nanotubes arrays are demonstrated with enhanced cycling life and noticeable high-rate capability with capacities ranging from 735 mAh g-1 at 0.25 C to 482 mAh g-1 at 1.5 C, superior to those FeS2 counterparts in the literature. The composite nanotubes arrays architecture plays positive roles in the electrochemical enhancement due to combined advantages of large electrode-electrolyte contact area, good strain accommodation, improved electrical conductivity, and enhanced structural stability.

Label-free detection of biomolecules with Ta2O5-based field effect devices

NASA Astrophysics Data System (ADS)

Branquinho, Rita Maria Mourao Salazar

Field-effect-based devices (FEDs) are becoming a basic structural element in a new generation of micro biosensors. Their numerous advantages such as small size, labelfree response and versatility, together with the possibility of on-chip integration of biosensor arrays with a future prospect of low-cost mass production, make their development highly desirable. The present thesis focuses on the study and optimization of tantalum pentoxide (Ta2O5) deposited by rf magnetron sputtering at room temperature, and their application as sensitive layer in biosensors based on field effect devices (BioFEDs). As such, the influence of several deposition parameters and post-processing annealing temperature and surface plasma treatment on the film¡¦s properties was investigated. Electrolyte-insulator-semiconductor (EIS) field-effect-based sensors comprising the optimized Ta2O5 sensitive layer were applied to the development of BioFEDs. Enzyme functionalized sensors (EnFEDs) were produced for penicillin detection. These sensors were also applied to the label free detection of DNA and the monitoring of its amplification via polymerase chain reaction (PCR), real time PCR (RT-PCR) and loop mediated isothermal amplification (LAMP). Ion sensitive field effect transistors (ISFETs) based on semiconductor oxides comprising the optimized Ta2O5 sensitive layer were also fabricated. EIS sensors comprising Ta2O5 films produced with optimized conditions demonstrated near Nernstian pH sensitivity, 58+/-0.3 mV/pH. These sensors were successfully applied to the label-free detection of penicillin and DNA. Penicillinase functionalized sensors showed a 29+/-7 mV/mM sensitivity towards penicillin detection up to 4 mM penicillin concentration. DNA detection was achieved with 30 mV/mugM sensitivity and DNA amplification monitoring with these sensors showed comparable results to those obtained with standard fluorescence based methods. Semiconductor oxides-based ISFETs with Ta2O5 sensitive layer were

RNA adducts with Na 2SeO 4 and Na 2SeO 3 - Stability and structural features

NASA Astrophysics Data System (ADS)

Nafisi, Shohreh; Manouchehri, Firouzeh; Montazeri, Maryam

2011-12-01

Selenium compounds are widely available in dietary supplements and have been extensively studied for their antioxidant and anticancer properties. Low blood Se levels were found to be associated with an increased incidence and mortality from various types of cancers. Although many in vivo and clinical trials have been conducted using these compounds, their biochemical and chemical mechanisms of efficacy are the focus of much current research. This study was designed to examine the interaction of Na 2SeO 4 and Na 2SeO 3 with RNA in aqueous solution at physiological conditions, using a constant RNA concentration (6.25 mM) and various sodium selenate and sodium selenite/polynucleotide (phosphate) ratios of 1/80, 1/40, 1/20, 1/10, 1/5, 1/2 and 1/1. Fourier transform infrared, UV-Visible spectroscopic methods were used to determine the drug binding modes, the binding constants, and the stability of Na 2SeO 4 and Na 2SeO 3-RNA complexes in aqueous solution. Spectroscopic evidence showed that Na 2SeO 4 and Na 2SeO 3 bind to the major and minor grooves of RNA ( via G, A and U bases) with some degree of the Se-phosphate (PO 2) interaction for both compounds with overall binding constants of K(Na 2SeO 4-RNA) = 8.34 × 10 3 and K(Na 2SeO 3-RNA) = 4.57 × 10 3 M -1. The order of selenium salts-biopolymer stability was Na 2SeO 4-RNA > Na 2SeO 3-RNA. RNA aggregations occurred at higher selenium concentrations. No biopolymer conformational changes were observed upon Na 2SeO 4 and Na 2SeO 3 interactions, while RNA remains in the A-family structure.

MnO2 nanotubes assembled on conductive graphene/polyester composite fabric as a three-dimensional porous textile electrode for flexible electrochemical capacitors.

PubMed

Jin, Chun; Jin, Li-Na; Guo, Mei-Xia; Liu, Ping; Zhang, Jia-Nan; Bian, Shao-Wei

2017-12-15

A three-dimensional (3D) electrode material was successfully synthesized through a facile ZnO-assisted hydrothermal process in which vertical MnO 2 nanotube arrays were in situ grown on the conductive graphene/polyester composite fabric. The morphology and structure of MnO 2 nanotubes/graphene/polyester textile electrode were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The 3D electrode structure facilitates to achieve the maximum number of active sites for the pesudocapacitance redox reaction, fast electrolyte ion transportation and short ion diffusion path. The electrochemical measurements showed that the electrode possesses good capacitance capacity which reached 498F/g at a scan rate of 2mV/s in Na 2 SO 4 electrolyte solution. The electrode also showed stable electrochemical performances under the conditions of long-term cycling, and mechanical bending and twisting. Copyright © 2017 Elsevier Inc. All rights reserved.

Carbon Nanotube Nanoelectrode Array for Ultrasensitive DNA Detection

NASA Technical Reports Server (NTRS)

Li, Jun; Koehne, Jessica; Chen, Hua; Cassell, Alan; Ng, Hou Tee; Fan, Wendy; Ye, Qi; Han, Jie; Meyyappan, M.

2003-01-01

A reliable nanoelectrode array based on vertically aligned multi-walled carbon nanotubes (MWNTs) embedded in SiO2 is used for ultrasensitive DNA detection. Characteristic nanoelectrode behavior is observed using low-density MWNT arrays for measuring both bulk and surface immobilized redox species such as K4Fe(CN)6. The open-end of MWNTs present similar properties as graphite edge-plane electrodes with wide potential window, flexible chemical functionalities, and good biocompatibility. Oligonucleotide probes are selectively functionalized at the open ends cf the nanotube array and specifically hybridized with oligonucleotide targets. The guanine groups are employed as the signal moieties in the electrochemical measurements. Ru(bpy)3(2+) mediator is used to further amplify the guanine oxidation signal. The hybridization of subattomoles of PCR amplified DNA targets is detected electrochemically by combining the MWNT nanoelectrode array with the Ru(bpy)32' amplification mechanism. This system provides a general platform of molecular diagnostics for applications requiring ultrahigh sensitivity, high-degree of miniaturization, and simple sample preparations.

Study of TiO{sub 2} nanotubes as an implant application

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hazan, Roshasnorlyza, E-mail: roshasnorlyza@nm.gov.my; Sreekantan, Srimala; Mydin, Rabiatul Basria S. M. N.

Vertically aligned TiO{sub 2} nanotubes have become the primary candidates for implant materials that can provide direct control of cell behaviors. In this work, 65 nm inner diameters of TiO{sub 2} nanotubes were successfully prepared by anodization method. The interaction of bone marrow stromal cells (BMSC) in term of cell adhesion and cell morphology on bare titanium and TiO{sub 2} nanotubes is reported. Field emission scanning electron microscopy (FESEM) analysis proved interaction of BMSC on TiO{sub 2} nanotubes structure was better than flat titanium (Ti) surface. Also, significant cell adhesion on TiO{sub 2} nanotubes surface during in vitro study revealed thatmore » BMSC prone to attach on TiO{sub 2} nanotubes. From the result, it can be conclude that TiO{sub 2} nanotubes are biocompatible to biological environment and become a new generation for advanced implant materials.« less

Interface structure in Cu/Ta2O5/Pt resistance switch: a first-principles study.

PubMed

Xiao, Bo; Watanabe, Satoshi

2015-01-14

The interface structures of a Cu/Ta2O5/Pt resistance switch under various oxidation conditions have been examined from first-principles. The O-rich Cu/Ta2O5 interface is found to be stable within a wide range of O chemical potentials. In this interface structure, a considerable number of interface Cu atoms tend to migrate to the amorphous Ta2O5 (a-Ta2O5) layer, which causes the formation of the Cu2O layer. The interface Cu atoms become more ionized with an increase in the interface O concentration and/or temperature. These ionized Cu(+) ions could function as one of the main sources for the formation of conduction filaments in the Cu/a-Ta2O5/Pt resistance switch. In contrast, the ionization of the interface Cu atoms is not observed in the Cu/crystal-Ta2O5 interface primarily due to the much lower Cu ionic conductivity in crystal-Ta2O5 than that in amorphous state. In addition, the Pt electrode could not be ionized, irrespective of the interface O concentration and temperature. The formation of interface O vacancies in Pt/Ta2O5 is always energetically more stable than that in Cu/Ta2O5, which may be partly responsible for the cone shape of conduction filament formed in the Cu/a-Ta2O5/Pt resistance switch, where the base of the cone lies on the Pt/Ta2O5 interface.

Highly efficient visible-light driven photocatalytic hydrogen production from a novel Z-scheme Er3+:YAlO3/Ta2O5-V5+||Fe3+-TiO2/Au coated composite

NASA Astrophysics Data System (ADS)

Wang, Guowei; Ma, Xue; Wei, Shengnan; Li, Siyi; Qiao, Jing; Wang, Jun; Song, Youtao

2018-01-01

In this work, the preparation of a novel Z-scheme photocatalyst, Er3+:YAlO3/Ta2O5-V5+||Fe3+-TiO2/Au coated composite, for visible-light photocatalytic hydrogen production is reported for the first time. In this photocatalyst, Au nanoparticles as conduction band co-catalyst provide more active sites to enrich electrons. Ta2O5-V5+||Fe3+-TiO2 as composite redox cycle system thoroughly separates the photo-generated electrons and holes. In addition, Er3+:YAlO3 as up-conversion luminescence agent (from visible-light to ultraviolet-light) provides enough ultraviolet-light for satisfying the energy demand of wide band-gap semiconductors (TiO2 and Ta2O5). The photocatalytic hydrogen production can be achieved from methanol as sacrificial agent (electron donor) under visible-light irradiation. The main influence factors such as initial solution pH and molar ratio of TiO2 and Ta2O5 on visible-light photocatalytic hydrogen production activity of Er3+:YAlO3/Ta2O5-V5+||Fe3+-TiO2/Au coated composite are discussed in detail. The results show that the Er3+:YAlO3/Ta2O5-V5+||Fe3+-TiO2/Au coated composite with 1.0:0.5 M ratio of TiO2 and Ta2O5 in methanol aqueous solution at pH = 6.50 displays the highest photocatalytic hydrogen production activity. Furthermore, a high level of photocatalytic activity can be still maintained within three cycles under the same conditions. It implies that the prepared Z-scheme Er3+:YAlO3/Ta2O5-V5+||Fe3+-TiO2/Au coated composite may be a promising photocatalyst utilizing solar energy for hydrogen production.

Vertically aligned ZnO nanorod core-polypyrrole conducting polymer sheath and nanotube arrays for electrochemical supercapacitor energy storage

PubMed Central

2014-01-01

Nanocomposite electrodes having three-dimensional (3-D) nanoscale architecture comprising of vertically aligned ZnO nanorod array core-polypyrrole (PPy) conducting polymer sheath and the vertical PPy nanotube arrays have been investigated for supercapacitor energy storage. The electrodes in the ZnO nanorod core-PPy sheath structure are formed by preferential nucleation and deposition of PPy layer over hydrothermally synthesized vertical ZnO nanorod array by controlled pulsed current electropolymerization of pyrrole monomer under surfactant action. The vertical PPy nanotube arrays of different tube diameter are created by selective etching of the ZnO nanorod core in ammonia solution for different periods. Cyclic voltammetry studies show high areal-specific capacitance approximately 240 mF.cm-2 for open pore and approximately 180 mF.cm-2 for narrow 30-to-36-nm diameter PPy nanotube arrays attributed to intensive faradic processes arising from enhanced access of electrolyte ions through nanotube interior and exterior. Impedance spectroscopy studies show that capacitive response extends over larger frequency domain in electrodes with PPy nanotube structure. Simulation of Nyquist plots by electrical equivalent circuit modeling establishes that 3-D nanostructure is better represented by constant phase element which accounts for the inhomogeneous electrochemical redox processes. Charge-discharge studies at different current densities establish that kinetics of the redox process in PPy nanotube electrode is due to the limitation on electron transport rather than the diffusive process of electrolyte ions. The PPy nanotube electrodes show deep discharge capability with high coulomb efficiency and long-term charge-discharge cyclic studies show nondegrading performance of the specific areal capacitance tested for 5,000 cycles. PMID:25246867

Incorporation of TiO2 nanotubes in a polycrystalline zirconia: Synthesis of nanotubes, surface characterization, and bond strength.

PubMed

Dos Santos, Angélica Feltrin; Sandes de Lucena, Fernanda; Sanches Borges, Ana Flávia; Lisboa-Filho, Paulo Noronha; Furuse, Adilson Yoshio

2018-04-05

Despite numerous advantages such as high strength, the bond of yttria-stabilized zirconia polycrystal (Y-TZP) to tooth structure requires improvement. The purpose of this in vitro study was to evaluate the incorporation of TiO 2 nanotubes into zirconia surfaces and the bond strength of resin cement to the modified ceramic. TiO 2 nanotubes were produced by alkaline synthesis, mixed with isopropyl alcohol (50 wt%) and applied on presintered zirconia disks. The ceramics were sintered, and the surfaces were characterized by confocal laser microscopy, scanning electron microscopy (SEM), and energy-dispersive x-ray spectroscopy (EDS) analysis. For bond strength, the following 6 groups (n=16) were evaluated: without TiO 2 and Single Bond Universal; with TiO 2 nanotubes and Single Bond Universal; without TiO 2 nanotubes and Z-prime; with TiO 2 nanotubes and Z-prime; without TiO 2 and Signum Zirconia Bond; with TiO 2 and Signum Zirconia Bond. After sintering, resin cement cylinders, diameter of 1.40 mm and 1 mm in height, were prepared and polymerized for 20 seconds. Specimens were stored in water at 37°C for 30 days and submitted to a shear test. Data were analyzed by 2-way ANOVA and Tukey honest significant difference (α=.05) tests. EDS analysis confirmed that nanoagglomerates were composed of TiO 2 . The shear bond strength showed statistically significant differences among bonding agents (P<.001). No significant differences were found with the application of nanotubes, regardless of the group analyzed (P=.682). The interaction among the bonding agent factors and addition of nanotubes was significant (P=.025). Nanotubes can be incorporated into zirconia surfaces. However, this incorporation did not improve bond strength. Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Phase transition in lithium garnet oxide ionic conductors Li7La3Zr2O12: The role of Ta substitution and H2O/CO2 exposure

NASA Astrophysics Data System (ADS)

Wang, Yuxing; Lai, Wei

2015-02-01

High Li-content lithium garnet oxides are promising solid electrolyte materials for lithium batteries. Being the highest Li-content lithium garnet oxides, Li7La3Zr2O12 has been reported to crystallize in either the tetragonal or cubic phase with no consensus on the exact conditions under which these two phases are formed, which may be due to unintentional Al contamination and air exposure. In this work, the effects of Ta substitution and H2O/CO2 exposure have been studied under Al-contamination free conditions with minimal air exposure. We showed that 1) the Ta-substitution induced phase transition occurred through a two-phase mechanism and a minimum 0.6 mol of Ta substitution to Zr is needed to stabilize the cubic phase; 2) H2O and CO2 can individually induce the tetragonal-cubic phase transition in Li7La3Zr2O12 through proton exchange and Li extraction, respectively, which can have great influence on the transport properties of Li7La3Zr2O12.

Synthesis and characterization of nanotubes from misfit compounds (LnS)1+yTaS2 (Ln= Pr, Sm, Gd, Yb).

PubMed

Tenne, Reshef; Serra, Marco; Stolovas, Dalit; Houben, Lothar; Popovitz-Biro, Ronit; Pinkas, Iddo; Kampmann, Felix; Maultzsch, Janina; Joselevich, Ernesto

2018-06-06

The synthesis and characterization of nanotubes from the misfit layered compounds (MLC) (LnS)1+yTaS2 (shortly denoted as LnS-TaS2) (Ln= Pr, Sm, Gd and Yb), not reported before, are described (the bulk compound YbS-LaS2 was not documented before). Transmission electron microscopy (TEM) and selected area electron diffraction (SAED) show that the interlayer spacing along the c-axis decrease with increasing atomic number of the lanthanide atom, suggesting tighter interaction between the LnS layer and the TaS2 for the late lanthanides. The Raman spectra of the tubules were studied and compared to the bulk MLC compounds. Like bulk MLC, the Raman spectra can be divided into the low frequency modes (110-150 cm-1) of the LnS lattice and the high frequency (250-400 cm-1) of the TaS2 lattice. The Raman spectra indicate that the vibrational lattice modes of the strained layers in the tubes are stiffer than those in the bulk compounds. Furthermore, the modes of the late lanthanides are higher in energy compared with the earlier lanthanides, suggesting larger charge transfer between the LnS and the TaS2 layers for the late lanthanides. Polarized Raman measurements showed the expected binodal intensity profile (antenna effect). The intensity ratio of the Raman signal showed that the E2g mode of TaS2 is more sensitive to the light polarization effect than its A1g mode. These nanotubes are expected to reveal interesting low temperature quasi-1D transport behavior. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Incorporating TiO2 nanotubes with a peptide of D-amino K122-4 (D) for enhanced mechanical and photocatalytic properties

NASA Astrophysics Data System (ADS)

Guo, L. Q.; Hu, Y. W.; Yu, B.; Davis, E.; Irvin, R.; Yan, X. G.; Li, D. Y.

2016-02-01

Titanium dioxide (TiO2) nanotubes are promising for a wide variety of potential applications in energy, biomedical and environmental sectors. However, their low mechanical strength and wide band gap limit their widespread technological use. This article reports our recent efforts to increase the mechanical strength of TiO2 nanotubes with lowered band gap by immobilizing a peptide of D-amino K122-4 (D) onto the nanotubes. Topographies and chemical compositions of the peptide-coated and uncoated TiO2 nanotubular arrays were characterized by scanning electron microscopy and X-ray photoelectron spectroscopy (XPS). Properties of the peptide-coated and uncoated TiO2 nanotubular arrays, including hardness, elastic modulus, electron work function and photocurrent, were evaluated using micromechanical probe, Kelvin Probe and electrochemical system. Effect of the peptide on surface conductivity was also investigated through current mapping and I-V curve analysis with conductive atomic force microscopy. It is demonstrated that the peptide coating simultaneously enhances the mechanical strength, photocatalytic and electrical properties of TiO2 nanotubes.

Influence of Li3BO3 additives on the Li+ conductivity and stability of Ca/Ta-substituted Li6.55(La2.95Ca0.05)(Zr1.5Ta0.5)O12 electrolytes

NASA Astrophysics Data System (ADS)

Zhang, L. C.; Yang, J. F.; Gao, Y. X.; Wang, X. P.; Fang, Q. F.; Chen, C. H.

2017-07-01

The cubic Ca/Ta-substituted Li6.55(La2.95Ca0.05)(Zr1.5Ta0.5)O12 (LLCZTO) electrolytes were synthesized at 800 °C with Li3BO3 as additives. The optimal amount of Li3BO3 and its influences on the microstructure, crystal structures, Li+ conductivity and the stability of the Li6.55(La2.95Ca0.05)(Zr1.5Ta0.5)O12 were studied by SEM, XRD and EIS. Among all the samples, when the molar ratio of Li3BO3 to the Li6.55(La2.95Ca0.05)(Zr1.5Ta0.5)O12 is 4:5, the highest Li+ conductivity of 1.33 × 10-4 S cm-1 at 30 °C is obtained. When the LLCZTO samples are exposed in air, the Li+ conductivity is deteriorated possibly owing to the side reactions between the LLCZTO and the H2O or CO2 in the air. The Li3BO3 addition can alleviate such deterioration of the Li+ conductivity.

From Ba{sub 3}Ta{sub 5}O{sub 14}N to LaBa{sub 2}Ta{sub 5}O{sub 13}N{sub 2}: Decreasing the optical band gap of a photocatalyst

DOE Office of Scientific and Technical Information (OSTI.GOV)

Anke, B.; Bredow, T.; Pilarski, M.

Yellow LaBa{sub 2}Ta{sub 5}O{sub 13}N{sub 2} was successfully synthesized as phase-pure material crystallizing isostructurally to previously reported Ba{sub 3}Ta{sub 5}O{sub 14}N and mixed-valence Ba{sub 3}Ta{sup V}{sub 4}Ta{sup IV}O{sub 15}. The electronic structure of LaBa{sub 2}Ta{sub 5}O{sub 13}N{sub 2} was studied theoretically with the range-separated hybrid method HSE06. The most stable structure was obtained when lanthanum was placed on 2a and nitrogen on 4h sites confirming Pauling's second rule. By incorporating nitrogen, the measured band gap decreases from ∼3.8 eV for the oxide via 2.74 eV for Ba{sub 3}Ta{sub 5}O{sub 14}N to 2.63 eV for the new oxide nitride, giving risemore » to an absorption band well in the visible-light region. Calculated fundamental band gaps confirm the experimental trend. The atom-projected density of states has large contributions from N2p orbitals close to the valence band edge. These are responsible for the observed band gap reduction. Photocatalytic hydrogen formation was investigated and compared with that of Ba{sub 3}Ta{sub 5}O{sub 14}N revealing significantly higher activity for LaBa{sub 2}Ta{sub 5}O{sub 13}N{sub 2} under UV-light. - Graphical abstract: X-ray powder diffraction pattern of LaBa{sub 2}Ta{sub 5}O{sub 13}N{sub 2} with the results of the Rietveld refinements. Inset: Unit cell of LaBa{sub 2}Ta{sub 5}O{sub 13}N{sub 2} and polyhedral representation of the crystal structure. - Highlights: • Synthesis of a new oxide nitride LaBa{sub 2}Ta{sub 5}O{sub 13}N{sub 2}. • Refinement of the crystal structure. • Quantum chemical calculations provided band gap close to the measured value. • New phase shows a higher photocatalytic H{sub 2} evolution rate compared to prior tested Ba{sub 3}Ta{sub 5}O{sub 14}N.« less

Enhanced photoelectrochemical water splitting performance of anodic TiO(2) nanotube arrays by surface passivation.

PubMed

Gui, Qunfang; Xu, Zhen; Zhang, Haifeng; Cheng, Chuanwei; Zhu, Xufei; Yin, Min; Song, Ye; Lu, Linfeng; Chen, Xiaoyuan; Li, Dongdong

2014-10-08

One-dimensional anodic titanium oxide nanotube (TONT) arrays provide a direct pathway for charge transport, and thus hold great potential as working electrodes for electrochemical energy conversion and storage devices. However, the prominent surface recombination due to the large amount surface defects hinders the performance improvement. In this work, the surface states of TONTs were passivated by conformal coating of high-quality Al2O3 onto the tubular structures using atomic layer deposition (ALD). The modified TONT films were subsequently employed as anodes for photoelectrochemical (PEC) water splitting. The photocurrent (0.5 V vs Ag/AgCl) recorded under air mass 1.5 global illumination presented 0.8 times enhancement on the electrode with passivation coating. The reduction of surface recombination rate is responsible for the substantially improved performance, which is proposed to have originated from a decreased interface defect density in combination with a field-effect passivation induced by a negative fixed charge in the Al2O3 shells. These results not only provide a physical insight into the passivation effect, but also can be utilized as a guideline to design other energy conversion devices.

Anti-biofouling function of amorphous nano-Ta2O5 coating for VO2-based intelligent windows.

PubMed

Li, Jinhua; Guo, Geyong; Wang, Jiaxing; Zhou, Huaijuan; Shen, Hao; Yeung, Kelvin W K

2017-04-28

From environmental and health perspectives, the acquisition of a surface anti-biofouling property holds important significance for the usability of VO 2 intelligent windows. Herein, we firstly deposited amorphous Ta 2 O 5 nanoparticles on VO 2 film by the magnetron sputtering method. It was found that the amorphous nano-Ta 2 O 5 coating possessed a favorable anti-biofouling capability against Pseudomonas aeruginosa as an environmental microorganism model, behind which lay the mechanism that the amorphous nano-Ta 2 O 5 could interrupt the microbial membrane electron transport chain and significantly elevate the intracellular reactive oxygen species (ROS) level. A plausible relationship was established between the anti-biofouling activity and physicochemical nature of amorphous Ta 2 O 5 nanoparticles from the perspective of defect chemistry. ROS-induced oxidative damage gave rise to microbial viability loss. In addition, the amorphous nano-Ta 2 O 5 coating can endow VO 2 with favorable cytocompatibility with human skin fibroblasts. This study may provide new insights into understanding the anti-biofouling and antimicrobial actions of amorphous transition metal oxide nanoparticles, which is conducive to expanding their potential applications in environmental fields.

Anti-biofouling function of amorphous nano-Ta2O5 coating for VO2-based intelligent windows

NASA Astrophysics Data System (ADS)

Li, Jinhua; Guo, Geyong; Wang, Jiaxing; Zhou, Huaijuan; Shen, Hao; Yeung, Kelvin W. K.

2017-04-01

From environmental and health perspectives, the acquisition of a surface anti-biofouling property holds important significance for the usability of VO2 intelligent windows. Herein, we firstly deposited amorphous Ta2O5 nanoparticles on VO2 film by the magnetron sputtering method. It was found that the amorphous nano-Ta2O5 coating possessed a favorable anti-biofouling capability against Pseudomonas aeruginosa as an environmental microorganism model, behind which lay the mechanism that the amorphous nano-Ta2O5 could interrupt the microbial membrane electron transport chain and significantly elevate the intracellular reactive oxygen species (ROS) level. A plausible relationship was established between the anti-biofouling activity and physicochemical nature of amorphous Ta2O5 nanoparticles from the perspective of defect chemistry. ROS-induced oxidative damage gave rise to microbial viability loss. In addition, the amorphous nano-Ta2O5 coating can endow VO2 with favorable cytocompatibility with human skin fibroblasts. This study may provide new insights into understanding the anti-biofouling and antimicrobial actions of amorphous transition metal oxide nanoparticles, which is conducive to expanding their potential applications in environmental fields.

Influences of the residual argon gas and thermal annealing on Ta2O5 and SiO2 thin film filters

NASA Astrophysics Data System (ADS)

Liu, Wen-Jen; Chen, Chih-Min; Lai, Yin-Chieh

2005-04-01

Ion beam assisted deposition (IBAD) technique had widely used for improving stacking density and atomic mobility of thin films in many applications, especially adopted in optical film industries. Tantalum pentaoxide (Ta2O5) and silicon oxides (SiO2) optical thin films were deposited on the quartz glass substrate by using argon ion beam assisted deposition, and the influences of the residual argon gas and thermal annealing processes on the optical property, stress, compositional and microstructure evolution of the thin films were investigated in this study. Ta2O5 thin films were analyzed by XPS indicated that the ratio value of oxygen to tantalum was insufficient, at the same time, the residual argon gas in the thin films might result in film and device instabilities. Adopting oxygen-thermal annealing treatment at the temperature of 425°C, the thin films not only decreased the residual argon gas and the surface roughness, but also provided the sufficient stoichiometric ratio. Simultaneously, microstructure examination indicated few nano-crystallized structures and voids existed in Ta2O5 thin films, and possessed reasonable refractive index and lower extinction coefficient. By the way, we also suggested the IBAD system using the film compositional gas ion beam to replace the argon ion beam for assisting deposited optical films. The designed (HL)6H6LH(LH)6 multi-layers indicated higher insertion loss than the designed (HL)68H(LH)6 multi-layers. Therefore, using the high refractive index as spacer material represented lower insertion loss.

Improved speed and data retention characteristics in flash memory using a stacked HfO2/Ta2O5 charge-trapping layer

NASA Astrophysics Data System (ADS)

Zheng, Zhiwei; Huo, Zongliang; Zhang, Manhong; Zhu, Chenxin; Liu, Jing; Liu, Ming

2011-10-01

This paper reports the simultaneous improvements in erase speed and data retention characteristics in flash memory using a stacked HfO2/Ta2O5 charge-trapping layer. In comparison to a memory capacitor with a single HfO2 trapping layer, the erase speed of a memory capacitor with a stacked HfO2/Ta2O5 charge-trapping layer is 100 times faster and its memory window is enlarged from 2.7 to 4.8 V for the same ±16 V sweeping voltage range. With the same initial window of ΔVFB = 4 V, the device with a stacked HfO2/Ta2O5 charge-trapping layer has a 3.5 V extrapolated 10-year retention window, while the control device with a single HfO2 trapping layer has only 2.5 V for the extrapolated 10-year window. The present results demonstrate that the device with the stacked HfO2/Ta2O5 charge-trapping layer has a strong potential for future high-performance nonvolatile memory application.

Laser damage comparisons of broad-bandwidth, high-reflection optical coatings containing TiO 2, Nb 2O 5, or Ta 2O 5 high-index layers

DOE PAGES

Field, Ella Suzanne; Bellum, John Curtis; Kletecka, Damon E.

2016-09-21

Broad bandwidth coatings allow angle of incidence flexibility and accommodate spectral shifts due to aging and water absorption. Higher refractive index materials in optical coatings, such as TiO 2, Nb 2O 5, and Ta 2O 5, can be used to achieve broader bandwidths compared to coatings that contain HfO 2 high index layers. We have identified the deposition settings that lead to the highest index, lowest absorption layers of TiO 2, Nb 2O 5, and Ta 2O 5, via e-beam evaporation using ion-assisted deposition. We paired these high index materials with SiO 2 as the low index material to createmore » broad bandwidth high reflection coatings centered at 1054 nm for 45 deg angle of incidence and P polarization. Furthermore, high reflection bandwidths as large as 231 nm were realized. Laser damage tests of these coatings using the ISO 11254 and NIF-MEL protocols are presented, which revealed that the Ta 2O 5/SiO 2 coating exhibits the highest resistance to laser damage, at the expense of lower bandwidth compared to the TiO 2/SiO 2 and Nb 2O 5/SiO 2 coatings.« less