Effect of Fe-Mn addition on microstructure and magnetic properties of NdFeB magnetic powders

NASA Astrophysics Data System (ADS)

Kurniawan, C.; Purba, A. S.; Setiadi, E. A.; Simbolon, S.; Warman, A.; Sebayang, P.

2018-03-01

In this paper, the effect of Fe-Mn alloy addition on microstructures and magnetic properties of NdFeB magnetic powders was investigated. Varied Fe-Mn compositions of 1, 5, and 10 wt% were mixed with commercial NdFeB type MQA powders for 15 minutes using shaker mill. The characterizations were performed by powder density, PSA, XRD, SEM, and VSM. The Fe-Mn addition increased the powder density of NdFeB/Fe-Mn powders. On the other side, particle size distribution slightly decreased as the Fe-Mn composition increases. Magnetic properties of NdFeB/Fe-Mn powders changed with the increasing of Fe-Mn content. SEM analysis showed the particle size of NdFeB/Fe-Mn powder was smaller as the Fe-Mn composition increases. It showed that NdFeB/Fe-Mn particles have different size and shape for NdFeB and Fe-Mn particles separately. The optimum magnetic properties of NdFeB/Fe-Mn powder was achieved on the 5 wt% Fe-Mn composition with remanence M r = 49.45 emu/g, coercivity H c = 2.201 kOe, and energy product, BH max = 2.15 MGOe.

Nd-Fe-B/Sm-M/Nd-M (M = Fe, Co, Ti, Cu, Zr) hybrid magnets with improved thermal stability

NASA Astrophysics Data System (ADS)

Grigoras, M.; Lostun, M.; Urse, M.; Borza, F.; Chiriac, H.; Lupu, N.

2018-02-01

Hybrid magnets of Nd12Fe82B6(2:14:1-phase)/Nd9.4Fe59Co25.3Ti6.3(3:29-phase) and Nd12Fe82B6/Sm11.1Co65.8Fe8.9Cu10.7Zr3.5(2:17-phase) with different weight ratio have been prepared by spark plasma sintering pressing technique from ball-milled powders obtained from melt-spun ribbons. Influence of the ratio between the two phases on the magnetic properties and thermal stability of the hybrid magnets was studied. It has been found that the ratio has a remarkable influence, especially on the thermal stability of the bulk magnets. However, the magnetic properties of such type of hybrid magnets result not only from the type and ratio of components but also from the interaction between them. It was found that in NdFeB/3:29 hybrid magnets with 15% content of 3:29-phase, the temperature coefficients of remanence (α) and of coercivity (β) are improved from -0.095 to -0.082 (%/°C) and from -0.57 to -0.47 (%/°C), respectively, as compared to the Nd2Fe14B single-phase counterpart. While for the NdFeB/2:17 hybrid magnets the content of 2:17-phase is not significantly influencing the temperature coefficient of induction (α), the temperature coefficient of °C (β) increases up to -0.41 (%/°C) for 10% content of 2:17-phase. The increase in the reversible temperature coefficients of hybrid magnets indicate a remarkable improvement of their thermal stability.

Thermal aging of melt-spun NdFeB magnetic powder in hydrogen

NASA Astrophysics Data System (ADS)

Pinkerton, Frederick E.; Balogh, Michael P.; Ellison, Nicole; Foto, Aldo; Sechan, Martin; Tessema, Misle M.; Thompson, Margarita P.

2016-11-01

High energy product neodymium-iron-boron (NdFeB) magnets are the premier candidate for demanding electrified vehicle traction motor applications. Injection molded (IM) or compression molded (CM) magnets made using NdFeB powders are promising routes to improve motor efficiency, cost, and manufacturability. However, IM and CM NdFeB magnets are susceptible to substantial thermal aging losses at motor operating temperatures when exposed to the automatic transmission fluid (ATF) used as a lubricant and cooling medium. The intrinsic coercivity Hci of NdFeB IM and CM magnets degrades by as much as 18% when aged for 1000 h in ATF at 150 °C, compared to a 3% loss when aged in air. Here we report aging studies of rapidly quenched NdFeB powder in air, ATF, and H2 gas. Expansion of the NdFeB crystal lattice in both ATF and H2 identified hydrogen dissociated from the ATF during aging and diffused into the primary NdFeB phase as the probable cause of the coercivity loss of IM and CM magnets.

The Impact Induced Demagnetization Mechanism in NdFeB Permanent Magnets

NASA Astrophysics Data System (ADS)

Li, Yan-Feng; Zhu, Ming-Gang; Li, Wei; Zhou, Dong; Lu, Feng; Chen, Lang; Wu, Jun-Ying; Qi, Yan; Du, An

2013-09-01

Compression of unmagnetized Nd2Fe14B permanent magnets is executed by using shock waves with different pressures in a one-stage light gas gun system. The microstructure, crystal structure, and magnetic properties of the magnets are examined with scanning electronic microscopy, x-ray diffraction, hysteresis loop instruments, and a vibrating sample magnetometer, respectively. The NdFeB magnets display a demagnetization phenomenon after shock wave compression. The coercivity dropped from about 21.4 kOe to 3.2 kOe. The critical pressure of irreversible demagnetization of NdFeB magnets should be less than 4.92 GPa. The coercivity of the NdFeB magnets compressed by shock waves could be recovered after annealing at 900°C and 520°C for 2 h, sequentially. The chaotic orientation of Nd2Fe14B grains in the compressed magnets is the source of demagnetization.

Coercivity enhancement in hot deformed Nd2Fe14B-type magnets by doping low-melting RCu alloys (R = Nd, Dy, Nd + Dy)

NASA Astrophysics Data System (ADS)

Lee, Y. I.; Huang, G. Y.; Shih, C. W.; Chang, W. C.; Chang, H. W.; You, J. S.

2017-10-01

Magnetic properties of the anisotropic NdFeB magnets prepared by hot pressing followed by die-upsetting NdFeB MQU-F powders doped with low-melting RCu alloy powders were explored, where RCu stands for Nd70Cu30, Dy70Cu30 and (Nd0.5Dy0.5)70Cu30, respectively. In addition, the post-annealing at 600 °C was employed to modify the microstructures and the magnetic properties of the hot deformed magnets. It is found that doping RCu alloy powders is effective in enhancing the coercivity of the hot deformed NdFeB magnets from 15.1 kOe to 16.3-19.5 kOe. For Nd70Cu30-doped magnets, the increment of coercivity is only 1.2 kOe. Meanwhile, Dy70Cu30-doped and (Nd0.5Dy0.5)70Cu30-doped magnets show an almost identical enhancement of coercivity of about 4.4 kOe. Importantly, the latter magnet shows a beneficial effect of reducing the usage of Dy from 1.6 wt% to 0.8 wt%. TEM analysis shows that nonmagnetic Nd, Dy and Cu appear at grain boundary and isolate the magnetic grains, leading to an enhancement of coercivity. Doping lower melting point Dy-lean (Nd0.5Dy0.5)70Cu30 powders into commercial MQU-F powders for making high coercivity hot deformed NdFeB magnets might be a potential and economic way for mass production.

Substitution of Nd with other rare earth elements in melt spun Nd{sub 2}Fe{sub 14}B magnets

DOE Office of Scientific and Technical Information (OSTI.GOV)

Brown, D. N.; Lau, D.; Chen, Z.

2016-05-15

This is a contemporary study of rapidly quenched Nd{sub 1.6}X{sub 0.4}Fe{sub 14}B magnetic materials (where X= Nd, Y, Ce, La, Pr, Gd and Ho). A 20% substitution of the Nd component from Nd{sub 2}Fe{sub 14}B can bring about some commercial advantage. However, there will be some compromise to the magnetic performance. Light rare earth elements are definitely more abundant (Y, Ce, La) than the heavier rare earth elements, but when they are included in RE{sub 2}Fe{sub 14}B magnets they tend to lower magnetic performance and thermal stability. Substituting heavy rare earth elements (Gd, Ho) for Nd in Nd{sub 2}Fe{sub 14}Bmore » improves the thermal stability of magnets but causes a loss in magnet remanence.« less

Local profile dependence of coercivity in (MM0.3Nd0.7)-Fe-B sintered magnets

NASA Astrophysics Data System (ADS)

Yu, Xiaoqiang; Zhu, Minggang; Liu, Weiqiang; Li, Wei; Sun, Yachao; Shi, Xiaoning; Yue, Ming

2018-03-01

Two magnets with the same nominal composition of (MM0.3Nd0.7)-Fe-B (Marked as A) and [(La0.27Ce0.53Pr0.03Nd0.17)0.3Nd0.7]-Fe-B (Marked as B) were prepared using traditional powder metallurgical process, respectively. In order to point out the difference between two magnets, the magnetic properties, microstructure and magnetic domain of both magnets were investigated. Both magnets have the same elements, but different raw materials of misch-metal (MM) and La/Ce/Pr/Nd pure metal, which induces different magnetic properties. The magnet A with Br of 13.1 kGs, Hcj of 7.6 kOe, (BH)max of 37.8 MGOe and magnet B with Br of 13.4 kGs, Hcj of 5.8 kOe, (BH)max of 34.5 MGOe are obtained. Although both magnets have the similar Br, magnet A has higher coercivity than that of magnet B. According to refined results of characteristic X-ray diffraction peaks, there is a hard magnetic main phase with higher magnetic anisotropy field (HA) in magnet A and opposite case happens on magnet B. SEM images demonstrate that magnet A has more continuous RE-rich phase and smaller grain size compared to that of magnet B, which contributes to enhancing the coercivity. In addition, two main phases of [Nd0.82(La, Ce)0.18]-Fe-B and [Nd0.75(La, Ce)0.25]-Fe-B were detected by the EDX calculation, and the two main phases in both magnets were observed by magnetic domains again. Compared to magnet B, 2:14:1 main phases in magnet A contain more [Nd0.82(La, Ce)0.18]-Fe-B main phases and less [Nd0.75(La, Ce)0.25]-Fe-B main phases, which also leads to higher coercivity due to the different HA among Nd2Fe14B, La2Fe14B and Ce2Fe14B phases. Therefore, it is concluded that MM substitution could exhibit better magnetic properties than (La0.27Ce0.53Pr0.03Nd0.17)-metal substitution. Furthermore, applications of MM are beneficial to fabricate (MM, Nd)-Fe-B permanent magnets with lower cost.

Magnetic performance change of multi-main-phase Nd-Ce-Fe-B magnets by diffusing (Nd, Pr)H x

NASA Astrophysics Data System (ADS)

Ma, Tianyu; Zhang, Wenying; Peng, Baixing; Liu, Yongsheng; Chen, Yongjie; Wang, Xinhua; Yan, Mi

2018-02-01

The grain boundary diffusion process (GBDP) is effective to enhance coercivity of the single-main-phase (SMP) RE2Fe14B (rare earth (RE)) magnets through forming magnetic hardening shells surrounding the hard grain cores. Here, the GBDP was applied to the multi-main-phase (MMP) (Nd, Pr)22.3Ce8.24FebalM1.0B1.0 (wt.%) magnets prepared by sintering the mixture of Ce-free and Ce-containing 2:14:1 powders, which have shown superior magnetic properties, especially coercivity, to the SMP ones at the same average composition. The remanence of the (Nd, Pr)H x diffused magnets increases gradually with the increase of diffusion temperature from 480 to 880 °C, the coercivity, however, slightly decreases. The highest (BH)max of 350.1 kJ m-3 is achieved when diffusing at 680 °C, which is 9.2% higher than 320.7 kJ m-3 for the as-prepared magnet. The remanence increment is due to the diffusion of Nd/Pr into the 2:14:1 phase grains, enlarging the intrinsic saturation magnetic polarization. The slight coercivity reduction is due to the gradual homogenization of RE distribution within the 2:14:1 grains of the undiffused parts, i.e. approaching the ‘close to equilibrium (or SMP)’ state, which offsets the positive contributions from the enrichment of Nd/Pr in the Ce-rich 2:14:1 phase and the formation of continuous RE-rich intergranular phase. These findings suggest that the GBDP effect on coercivity of the MMP Nd-Ce-Fe-B magnets is distinctly different from the SMP ones, and that the chemical heterogeneity should be carefully controlled to improve the magnetic properties of such high cost-performance permanent magnets.

Towards understanding of magnetization reversal in Nd-Fe-B nanocomposites: analysis by high-throughput micromagnetic simulations

NASA Astrophysics Data System (ADS)

Erokhin, Sergey; Berkov, Dmitry; Ito, Masaaki; Kato, Akira; Yano, Masao; Michels, Andreas

2018-03-01

We demonstrate how micromagnetic simulations can be employed in order to characterize and analyze the magnetic microstructure of nanocomposites. For the example of nanocrystalline Nd-Fe-B, which is a potential material for future permanent-magnet applications, we have compared three different models for the micromagnetic analysis of this material class: (i) a description of the nanocomposite microstructure in terms of Stoner-Wohlfarth particles with and without the magnetodipolar interaction; (ii) a model based on the core-shell representation of the nanograins; (iii) the latter model including a contribution of superparamagnetic clusters. The relevant parameter spaces have been systematically scanned with the aim to establish which micromagnetic approach can most adequately describe experimental data for this material. According to our results, only the last, most sophisticated model is able to provide an excellent agreement with the measured hysteresis loop. The presented methodology is generally applicable to multiphase magnetic nanocomposites and it highligths the complex interrelationship between the microstructure, magnetic interactions, and the macroscopic magnetic properties.

3-D laser confocal microscopy study of the oxidation of NdFeB magnets in atmospheric conditions

NASA Astrophysics Data System (ADS)

Meakin, J. P.; Speight, J. D.; Sheridan, R. S.; Bradshaw, A.; Harris, I. R.; Williams, A. J.; Walton, A.

2016-08-01

Neodymium iron boron (NdFeB) magnets are used in a number of important applications, such as generators in gearless wind turbines, motors in electric vehicles and electronic goods (e.g.- computer hard disk drives, HDD). Hydrogen can be used as a processing gas to separate and recycle scrap sintered Nd-Fe-B magnets from end-of-life products to form a powder suitable for recycling. However, the magnets are likely to have been exposed to atmospheric conditions prior to processing, and any oxidation could lead to activation problems for the hydrogen decrepitation reaction. Many previous studies on the oxidation of NdFeB magnets have been performed at elevated temperatures; however, few studies have been formed under atmospheric conditions. In this paper a combination of 3-D laser confocal microscopy and Raman spectroscopy have been used to assess the composition, morphology and rate of oxidation/corrosion on scrap sintered NdFeB magnets. Confocal microscopy has been employed to measure the growth of surface reaction products at room temperature, immediately after exposure to air. The results showed that there was a significant height increase at the triple junctions of the Nd-rich grain boundaries. Using Raman spectroscopy, the product was shown to consist of Nd2O3 and formed only on the Nd-rich triple junctions. The diffusion coefficient of the triple junction reaction product growth at 20 °C was determined to be approximately 4 × 10-13 cm2/sec. This value is several orders of magnitude larger than values derived from the diffusion controlled oxide growth observations at elevated temperatures in the literature. This indicates that the growth of the room temperature oxidation products are likely defect enhanced processes at the NdFeB triple junctions.

Energy barrier analysis of Nd-Fe-B thin films

NASA Astrophysics Data System (ADS)

Goto, R.; Okamoto, S.; Kikuchi, N.; Kitakami, O.

2015-05-01

The magnetization reversal mechanism of a permanent magnet has long been a controversial issue, which is closely related to the so-called coercivity problem. It is well known that the energy barrier for magnetization reversal contains essential information on reversal process. In this study, we propose a method to analyze the energy barrier function for the magnetization reversal. Preferentially (001) oriented Nd-Fe-B films with and without a Nd overlayer are used as model magnets. By combining the magnetic viscosity and time dependent coercivity measurements, the barrier function has been successfully evaluated. As a result, although the Nd-Fe-B films with and without Nd overlayer exhibit different magnetic behaviors, the power indices for their energy barrier are almost the same, suggesting that the magnetization reversal proceeds in a similar mode.

Dynamic fracture of sintered Nd-Fe-B magnet under uniaxial compression

NASA Astrophysics Data System (ADS)

Wang, Huanran; Wan, Yin; Chen, Danian; Lei, Guohua; Ren, Chunying

2018-06-01

The dynamic fracture of the Nd-Fe-B magnets under uniaxial compression is investigated using a split Hopkinson pressure bar (SHPB). The surface deformation and fracture processes of the Nd-Fe-B specimens are recorded adopting a high-speed photography (HSP) with digital image correlation (DIC). The load and work applied to the specimens in the SHPB tests are determined with the strain signals of the transmitted and reflected waves. The surface strain distributions of the Nd-Fe-B specimen during the SHPB testing are revealed with DIC. It is shown by the HSP with DIC that when the load is near the maximum, the cracks at some positions on the surface of the expanding Nd-Fe-B specimen are formed and ran along certain directions. The work applied to the specimen per unit volume which corresponds to the maximal load is used to characterize the impact stability of the Nd-Fe-B specimen. The localized fracture strains at some positions on the surface of the expanding specimens at some characteristic times are determined with DIC, which are the projections of the strains onto the DIC plane.

Double coating protection of Nd-Fe-B magnets: Intergranular phosphating treatment and copper plating

NASA Astrophysics Data System (ADS)

Zheng, Jingwu; Chen, Haibo; Qiao, Liang; Lin, Min; Jiang, Liqiang; Che, Shenglei; Hu, Yangwu

2014-12-01

In this work, a double coating protection technique of phosphating treatment and copper plating was made to improve the corrosion resistance of sintered Nd-Fe-B magnets. In other words, the intergranular region of sintered Nd-Fe-B is allowed to generate passive phosphate conversion coating through phosphating treatment, followed by the copper coating on the surface of sintered Nd-Fe-B. The morphology and corrosion resistance of the phosphated sintered Nd-Fe-B were observed using SEM and electrochemical method respectively. The phosphate conversion coating was formed more preferably on the intergranular region of sintered Nd-Fe-B than on the main crystal region; just after a short time of phosphating treatment, the intergranular region of sintered Nd-Fe-B has been covered by the phosphate conversion coating and the corrosion resistance is significantly improved. With the synergistic protection of the intergranular phosphorization and the followed copper electrodeposition, the corrosion resistance of the sintered Nd-Fe-B is significantly better than that with a single phosphate film or single plating protection.

Direct-write 3D printing of NdFeB bonded magnets

DOE PAGES

Compton, Brett Gibson; Kemp, James William; Novikov, Timofei V.; ...

2016-08-17

We report a method to fabricate Nd-Fe-B bonded magnets of complex shape via extrusion-based additive manufacturing (AM), also known as 3D-printing. We have successfully formulated a 3D-printable epoxy-based ink for direct-write AM with anisotropic MQA NdFeB magnet particles that can be deposited at room temperature. The new feedstocks contain up to 40 vol.% MQA anisotropic Nd-Fe-B magnet particles, and they are shown to remain uniformly dispersed in the thermoset matrix throughout the deposition process. Ring, bar, and horseshoe-type 3D magnet structures were printed and cured in air at 100°C without degrading the magnetic properties. Lastly, this study provides a newmore » pathway for fabricating Nd-Fe-B bonded magnets with complex geometry at low temperature, and presents new opportunities for fabricating multifunctional hybrid structures and devices.« less

Direct-write 3D printing of NdFeB bonded magnets

DOE Office of Scientific and Technical Information (OSTI.GOV)

Compton, Brett Gibson; Kemp, James William; Novikov, Timofei V.

We report a method to fabricate Nd-Fe-B bonded magnets of complex shape via extrusion-based additive manufacturing (AM), also known as 3D-printing. We have successfully formulated a 3D-printable epoxy-based ink for direct-write AM with anisotropic MQA NdFeB magnet particles that can be deposited at room temperature. The new feedstocks contain up to 40 vol.% MQA anisotropic Nd-Fe-B magnet particles, and they are shown to remain uniformly dispersed in the thermoset matrix throughout the deposition process. Ring, bar, and horseshoe-type 3D magnet structures were printed and cured in air at 100°C without degrading the magnetic properties. Lastly, this study provides a newmore » pathway for fabricating Nd-Fe-B bonded magnets with complex geometry at low temperature, and presents new opportunities for fabricating multifunctional hybrid structures and devices.« less

Study on corrosion behaviors of sintered Nd-Fe-B magnets in different environmental conditions

NASA Astrophysics Data System (ADS)

Li, J. J.; Li, A. H.; Zhu, M. G.; Pan, W.; Li, W.

2011-04-01

Nd-Fe-B magnets have outstanding magnetic properties, but their corrosion resistance is poor because the rare-earth-rich phases in them are easily oxidized. In this article, we report an investigation of the corrosion behaviors of sintered Nd-Fe-B magnets with varied compositions in different corrosion conditions. The weight losses of the magnets after corrosion testing were measured after brushing off the corrosion products. The magnetic flux losses of the magnets were measured using a fluxmeter. A scanning electron microscope equipped with an energy dispersive x-ray analysis system was employed to observe the corrosion morphology. It was found that the humid-heat resistance of the magnets was obviously improved by partially substituting Dy for Nd and adding minor Co. The corrosion products and morphologies of Nd-Fe-B magnets for the autoclave test were different from those for the constant humid-heat test. The corrosion rates of the magnets for the former were much slower than for the latter; this is probably because the high-pressure steam led to an oxygen-deficient atmosphere, and the liquid film on the surface of the magnet specimens hindered the diffusion of oxygen into the bulk for the autoclave test.

The origin of coercivity decrease in fine grained Nd-Fe-B sintered magnets

NASA Astrophysics Data System (ADS)

Li, W. F.; Ohkubo, T.; Hono, K.; Sagawa, M.

2009-04-01

Microstructures of fine grained Nd-Fe-B sintered magnets that were produced by the pressless process were investigated to understand the origin of the sudden coercivity decrease below a certain grain size. The intrinsic coercivity is inversely proportional to ln D2 with the highest coercivity of 17 kOe at D˜4.5 μm, below which the coercivity drops as the grain size decreases. We found that the degradation of the coercivity of the magnet with a grain size of 3 μm was mainly caused by the inhomogeneous distribution of fcc-Nd oxide whose volume fraction increased with respect to the dhcp Nd-rich phase.

Impulse Magnetization of Nd-Fe-B Sintered Magnets for Sensors

PubMed Central

Przybylski, Marek; Kapelski, Dariusz; Ślusarek, Barbara; Wiak, Sławomir

2016-01-01

Magnetization of large Nd-Fe-B sintered permanent magnets is still challenging. This type of permanent magnet is electrically conductive, so impulse magnetization causes a flow of eddy currents which prevent magnetization of the whole volume of the magnet. The paper deals with the impulse magnetization of sintered Nd-Fe-B permanent magnets and shows a method for the determination of suitable parameters for the supply system. The necessary magnetic field strength for magnetization of the magnet to saturation was determined. The optimal magnetizing fixture supply voltage for magnetization to saturation was determined from simulations in PSpice software, finite element analyses in Maxwell 15 and measurements. Measurements of magnetic induction on the surface of the Nd-Fe-B magnet are also presented to ensure that a magnet with 70 mm diameter and 20 mm in height is fully saturated. PMID:27110783

Impulse Magnetization of Nd-Fe-B Sintered Magnets for Sensors.

PubMed

Przybylski, Marek; Kapelski, Dariusz; Ślusarek, Barbara; Wiak, Sławomir

2016-04-21

Magnetization of large Nd-Fe-B sintered permanent magnets is still challenging. This type of permanent magnet is electrically conductive, so impulse magnetization causes a flow of eddy currents which prevent magnetization of the whole volume of the magnet. The paper deals with the impulse magnetization of sintered Nd-Fe-B permanent magnets and shows a method for the determination of suitable parameters for the supply system. The necessary magnetic field strength for magnetization of the magnet to saturation was determined. The optimal magnetizing fixture supply voltage for magnetization to saturation was determined from simulations in PSpice software, finite element analyses in Maxwell 15 and measurements. Measurements of magnetic induction on the surface of the Nd-Fe-B magnet are also presented to ensure that a magnet with 70 mm diameter and 20 mm in height is fully saturated.

Enhancement of exchange coupling interaction of NdFeB/MnBi hybrid magnets

NASA Astrophysics Data System (ADS)

Nguyen, Truong Xuan; Nguyen, Khanh Van; Nguyen, Vuong Van

2018-03-01

MnBi ribbons were fabricated by melt - spinning with subsequent annealing. The MnBi ribbons were ground and mixed with NdFeB commercial Magnequench powders (MQA). The hybrid powder mixtures were subjected thrice to the annealing and ball-milling route. The hybrid magnets (100 - x)NdFeB/xMnBi, x=0, 30, 40, 50 and 100 wt% were in-mold aligned in an 18 kOe magnetic field and warm compacted at 290 °C by 2000 psi uniaxial pressure for 10 min. An enhancement of the exchange coupling of NdFeB/MnBi hybrid magnets was obtained by optimizing the magnets' microstructures via annealing and ball-milling processes. The magnetic properties of prepared NdFeB/MnBi hybrid magnets were studied and discussed in details.

Improved thermal stability of TbF3-coated sintered Nd-Fe-B magnets by electrophoretic deposition

NASA Astrophysics Data System (ADS)

Cao, X. J.; Chen, L.; Guo, S.; Di, J. H.; Ding, G. F.; Chen, R. J.; Yan, A. R.; Chen, K. Z.

2018-05-01

Using electrophoretic deposition (EPD) method, the impact of TbF3 diffusion on the coercivity, microstructure and thermal stability of sintered Nd-Fe-B magnets with different rare earth (RE) content was investigated. In the diffused magnets with the RE content of 34 wt.%, the maximum coercivity about 28.12 kOe with less than 1.44 wt.% Tb was achieved, the coercivity temperature coefficient (β) was improved to -0.50 %/°C from -0.58 %/°C within the temperature interval 25-160 °C, and the maximum operating temperature further increased to about 160 °C. It suggested that TbF3 diffused magnets had much superior thermal stability than the annealed samples. This was attributed to the formation of the Tb-rich (Nd, Tb)2Fe14B phase in the outer region of the matrix grains and the improved Nd-rich grain boundary phase after TbF3 diffusion.

Structure and magnetic properties of the Nd9.5Fe84.5B6 alloy subjected to severe plastic deformation and annealing

NASA Astrophysics Data System (ADS)

Menushenkov, V. P.; Shchetinin, I. V.; Chernykh, S. V.; Savchenko, A. G.; Gorshenkov, M. V.; Zhukov, D. G.

2017-10-01

The effect of severe plastic deformation (SPD) by torsion and subsequent annealing on the structure and magnetic properties of the cast Nd9.5Fe84.5B6 alloy is studied. SPD by torsion is shown to lead to partial amorphization of the Nd2Fe14B phase and the precipitation of α-Fe; subsequent annealing results in the crystallization of the amorphous phase and the formation of a nanocomposite Nd2Fe14B/α-Fe structure. After SPD by torsion at 20 revolutions and annealing at 873 K, the (101) texture is formed; in this case, the coercive force is H c = 360 kA/m and the maximum energy product is ( BH) max = 166 kJ/m3. The residual magnetization and the squareness ratio of the hysteretic loop of the textured alloy decrease as the ambient temperature decreases.

Electrochemical corrosion behavior, microstructure and magnetic properties of sintered Nd-Fe-B permanent magnet doped by CuZn5 powders

NASA Astrophysics Data System (ADS)

Liu, W. Q.; Wang, Z.; Sun, C.; Yue, M.; Liu, Y. Q.; Zhang, D. T.; Zhang, J. X.

2014-05-01

Nd-Fe-B permanent magnets with a small amount of CuZn5 powders doping were prepared by conventional sintered method. The effects of CuZn5 contents on magnetic properties and microstructure, electrochemical corrosion resistance of sintered Nd-Fe-B magnets were systematically studied. The results show that the magnetic properties of magnets do not have a significant variation by CuZn5 powders doping; the coercivity of magnets rises gradually, while the remanence of the magnets decreases a little with increasing of the CuZn5 amount. The CuZn5 doped magnets have more positive corrosion potential, Ecorr, and much lower corrosion current density, icorr, than the magnets without CuZn5 doping, indicating CuZn5 doping could improve the corrosion resistance. Both Zn and Cu enrich mainly into the Nd-rich phase, fully improve the wettability between the Nd-rich phase and the Nd2Fe14B phase, and repair the defects of the main phase, so the coercivity of magnets doped with CuZn5 powders rises. Such microstructure modification effectively restrains the aggressive inter-granular corrosion. As a result, the CuZn5 doped magnet possesses excellent corrosion resistance in NaCl electrolyte.

Structure and magnetic properties of Nd2Fe14B fine particles produced by spark erosion

NASA Astrophysics Data System (ADS)

Wan, H.; Berkowitz, A. E.

1994-11-01

At present Nd2Fe14B is the best permanent magnet because of its extremely high coercivity and energy product. Optimum properties of Nd2Fe14B magnets can be attained by producing single domain particles, and then aligning and compacting them. Due to the reactivity of the Nd constitutent, it is challenging to produce and handle a large amount of fine particles of this material. We have prepared fine particles of Nd2Fe14B by spark erosion with various dielectric media. Yield, size, size distribution, structure, and magnetic properties are discussed. The Nd2Fe14B particles were made by the sharker pot spark erosion method. Relaxation oscillators or a pulse generator were used to power the park erosion. Commercial Neomax 35 was employed as the primary material. The dielectric media were liquid Ar, Ar gas, and hydrocarbons, which provided an oxygen free environment. Structure and size were studied by transmission electron microscopy (TEM), scanning electron microscopy (SEM), and x-ray diffraction. Magnetic properties were measured by vibrating sample magnetometer (VSM) with temperatures in range of 4.2-1200 K. The particles produced in these three different dielectric media had different microstructures and crystal structures. The particles made in Ar gas were pure Nd2Fe14B phase. The particles made in liquid Ar were a mixture of amorphous and crystalline Nd2Fe14B, because the liquid Ar provided a much higher quench rate than Ar gas, which produced some amorphous Nd2Fe14B. Upon annealing, the amorphous particles became crystalline. The fine particles produced in hydrocarbons, such as pentane and dodecane, had more complex mixed phases, since the rare earth reacted with the hydrocarbons during the sparking process. The phases were NdC2, alpha-Fe, and amorphous and crystalline Nd2Fe14B. The effects of power parameters, such as voltage and capacitance, on particle size were investigated. Particle sizes from 20 nm to 50 microns were obtained. Nd2Fe14B

Preparation of Nd-Fe-B/α-Fe nano-composite thick-film magnets on various substrates using PLD with high laser energy density above 10 J/cm2

NASA Astrophysics Data System (ADS)

Nakano, M.; Kondo, H.; Yamashita, A.; Yanai, T.; Itakura, M.; Fukunaga, H.

2018-05-01

PLD (Pulsed Laser Deposition) method with high laser energy density (LED) above 10 J/cm2 followed by a flash annealing enabled us to obtain isotropic nano-composite thick-film magnets with (BH)max ≧ 80 kJ/m3 on polycrystalline Ta substrates. We also have demonstrated that a dispersed structure composed of α-Fe together with Nd2Fe14B phases with the average grain diameter of approximately 20 nm could be formed on the Ta substrates. In this study, we tried to enhance the (BH)max value by controlling the microstructure due to the usage of different metal based substrates with each high melting point such as Ti, Nb, and W. Although it was difficult to vary the microstructure and to improve the magnetic properties of the films deposited on the substrates, we confirmed that isotropic thick-film magnets with (BH)max ≧ 80 kJ/m3 based on the nano-dispersed α-Fe and Nd2Fe14B phases could be obtained on various metal substrates with totally different polycrystalline structure. On the other hand, the use of a glass substrate lead to the deterioration of magnetic properties of a film prepared using the same preparation process.

The microstructure and magnetic properties of melt-spun Fe 76Nd 16B 8 magnetic materials

NASA Astrophysics Data System (ADS)

Hadjipanayis, G. C.; Dickenson, R. C.; Lawless, K. R.

1986-02-01

The origin of magnetic hardening has been examined in melt-spun Fe 76Nd 16B 8 samples heat-treated at around 700°C. Microstructure studies show the same phases as in sintered magnets consisting of Fe 14Nd 2B, Fe 4NdB 4 and two high-Nd content phases. These phases exist in both equiaxed and faceted crystallites of submicron size. Lorentz microscopy shows domain walls which end at grain boundaries indicating that they are pinned there.

Electromagnetic machines with Nd-Fe-B magnets

NASA Astrophysics Data System (ADS)

Hanitsch, Rolf

1989-08-01

Permanent magnet motors are now becoming more accepted for general use in industrial fixed and variable speed drives. With the application of high-energy permanent magnets, such as Nd-Fe-B, the new motors offer higher efficiency and reduced size and weight compared with wound field energy converters of the same rating.

Single-crystal and textured polycrystalline Nd2Fe14B flakes with a submicron or nanosize thickness

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cui, BZ; Zheng, LY; Li, WF

2012-02-01

This paper reports on the fabrication, structure and magnetic property optimization of Nd2Fe14B single-crystal and [0 0 1] textured poly-nanocrystalline flakes prepared by surfactant-assisted high-energy ball milling (HEBM). Single-crystal Nd2Fe14B flakes first with micron and then with submicron thicknesses were formed via continuous basal cleavage along the (1 1 0) planes of the irregularly shaped single-crystal microparticles during the early stage of HEBM. With further milling, [0 0 1] textured polycrystalline submicron Nd2Fe14B flakes were formed. Finally, crystallographically anisotropic polycrystalline Nd2Fe14B nanoflakes were formed after milling for 5-6 h. Anisotropic magnetic behavior was found in all of the flake samples.more » Nd2Fe14B flakes prepared with either oleic acid (OA) or oleylamine (OY) as the surfactant exhibited similar morphology, structure and magnetic properties. Both the addition of some low-melting-point eutectic Nd70Cu30 alloy and an appropriate post-annealing can increase the coercivity of the Nd2Fe14B flakes. The coercivity of Nd2Fe14B nanoflakes with an addition of 16.7 wt.% Nd70Cu30 by milling for 5 h in heptane with 20 wt.% OY increased from 3.7 to 6.8 kOe after annealing at 450 degrees C for 0.5 h. The mechanism for formation and coercivity enhancement of Nd2Fe14B single-crystal and textured poly-nanocrystalline flakes with a submicron or nanosize thickness was discussed. (C) 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.« less

Magnetic properties of (misch metal, Nd)-Fe-B melt-spun magnets

NASA Astrophysics Data System (ADS)

Li, R.; Shang, R. X.; Xiong, J. F.; Liu, D.; Kuang, H.; Zuo, W. L.; Zhao, T. Y.; Sun, J. R.; Shen, B. G.

2017-05-01

The effect of replacing Nd with misch metal (MM) on magnetic properties and thermal stability has been investigated on melt-spun (Nd1-xMMx)13.5Fe79.5B7 ribbons by varying x from 0 to 1. All of the alloys studied crystallize in the tetragonal 2:14:1 structure with single hard magnetic phase. Curie temperature (Tc), coercivity (Hcj), remanence magnetization (Br) and maximum energy product ((BH)max) all decrease with MM content. The melt-spun MM13.5Fe79.5B ribbons with high ratio of La and Ce exhibit high magnetic properties of Hcj = 8.2 kOe and (BH)max= 10.3 MGOe at room temperature. MM substitution also significantly strengthens the temperature stability of coercivity. The coercivities of the samples with x = 0.2 and even 0.4 exhibit large values close to that of Nd13.5Fe79.5B7 ribbons above 400 K.

Investigation on demagnetization of Nd2Fe14B permanent magnets induced by irradiation

NASA Astrophysics Data System (ADS)

Li, Zhefu; Jia, Yanyan; Liu, Renduo; Xu, Yuhai; Wang, Guanghong; Xia, Xiaobin

2017-12-01

Nd2Fe14B is an important component of insertion devices, which are used in synchrotron radiation sources, and could be demagnetized by irradiation. In the present study, the Monte Carlo code FLUKA was used to analyze the irradiation field of Nd2Fe14B, and it was confirmed that the main demagnetization particle was neutron. Nd2Fe14B permanent magnet samples were irradiated by Ar ions at different doses to simulate neutron irradiation damage. The hysteresis loops were measured using a vibrating sample magnetometer, and the microstructure evolutions were characterized by transmission electron microscopy. Moreover, the relationship between them was discussed. The results indicate that the decrease in saturated magnetization is caused by the changes in microstructure. The evolution of single crystals into an amorphous structure is the reason for the demagnetization phenomenon of Nd2Fe14B permanent magnets when considering its microscopic structure.

Strategic coating of NdFeB magnets with Dy to improve the coercivity of permanent magnets

DOE PAGES

Ucar, Huseyin; Parker, David S.; Nlebedim, I. C.; ...

2015-12-25

Here, we present a method, supported by theoretical analysis, for optimizing the usage of the critical rare earth element dysprosium in Nd 2Fe 14B (NdFeB)-based permanent magnets. In this method, we use Dy selectively in locations such as magnet edges and faces, where demagnetization factors are most significant, rather than uniformly throughout the bulk sample. A 200 nm thick Dy film was sputtered onto commercial N-38, NdFeB magnets with a thickness of 3 mm and post-annealed at temperatures from 600 - 700 C. Magnets displayed enhanced coercivities after post-annealing. Furthermore, our experimental results indicate as large as a 5 percentmore » increase in the energy product of NdFeB magnets, achieved for a total Dy weight percentage of 0.06 percent, much less than that used in commercial grade Dy-NdFeB magnets. Finally, by assuming all Dy diffused into NdFeB magnets, the improvement in energy product corresponds to a saving of over 1% Dy (critical element). Magnets manufactured using this technique will therefore be higher performing and significantly less expensive than those made presently.« less

One pot synthesis of exchange coupled Nd2Fe14B/alpha-Fe by pechini type sol-gel method.

PubMed

Hussain, Abid; Jadhav, Abhijit P; Baek, Yeon Kyung; Choi, Hul Jin; Lee, Jaeho; Kang, Young Soo

2013-11-01

In this work, a combination of nanoparticles of Nd2Fe14B hard magnetic phase and alpha-Fe soft magnetic phase were synthesized by one pot chemical synthesis technique using sol-gel method. A gel of Nd-Fe-B was prepared using NdCl3 x 6H2O, FeCl3 x 6H2O, H3BO3, citric acid, and ethylene glycol by pechini type sol-gel method. The gel was subsequently calcined and annealed to obtain the mixed oxide powders. The produced metal oxide particles were identified with XRD, SEM, TEM to obtain the crystal structure, shape and domain structure of them. The nanoparticles of mixed phase of Nd2Fe14B/alpha-Fe were obtained from these oxides by a process of reduction-diffusion in vacuum by employing CaH2 as reducing agent. During this process it was optimized by controlling temperature, reaction time and concentration of the reducing agent (CaH2). The phase formation of Nd2Fe14B was resulted by the direct diffusion of NdH2, Fe and B. The magnetic property of produced hard and soft phases was successfully identified with vibrating sample magnetometer (VSM). The mixed domains of the hard and soft phases were identified with selected area electron diffraction method (SAED) patterns.

Binder Jetting: A Novel NdFeB Bonded Magnet Fabrication Process

DOE Office of Scientific and Technical Information (OSTI.GOV)

Paranthaman, M. Parans; Shafer, Christopher S.; Elliott, Amy M.

2016-04-05

Our goal of this research is to fabricate near-net-shape isotropic (Nd) 2Fe 14B-based (NdFeB) bonded magnets using a three dimensional printing process to compete with conventional injection molding techniques used for bonded magnets. Additive manufacturing minimizes the waste of critical materials and allows for the creation of complex shapes and sizes. The binder jetting process works similarly to an inkjet printer. A print-head passes over a bed of NdFeB powder and deposits a polymer binding agent to bind the layer of particles together. The bound powder is then coated with another layer of powder, building the desired shape in successivemore » layers of bonded powder. Upon completion, the green part and surrounding powders are placed in an oven at temperatures between 100°C and 150°C for 4–6 h to cure the binder. After curing, the excess powder can be brushed away to reveal the completed “green” part. Green magnet parts were then infiltrated with a clear urethane resin to achieve the measured density of the magnet of 3.47 g/cm 3 close to 46% relative to the NdFeB single crystal density of 7.6 g/cm 3. Magnetic measurements indicate that there is no degradation in the magnetic properties. In conclusion, this study provides a new pathway for preparing near-net-shape bonded magnets for various magnetic applications.« less

Effect of sintering process on the magnetic and mechanical properties of sintered Nd-Fe-B magnets

NASA Astrophysics Data System (ADS)

Hu, Z. H.; Qu, H. J.; Zhao, J. Q.; Yan, C. J.; Liu, X. M.

2014-11-01

The magnetic and mechanical properties of sintered Nd-Fe-B magnets prepared by different sintering processes were investigated. The results showed that the intrinsic coercivity and fracture toughness of sintered Nd-Fe-B magnets first increased, and then declined with increasing annealing temperature. The optimum magnetic properties and fracture toughness of sintered Nd-Fe-B magnets were obtained at the annealing temperature of 540 °C. Sintering temperature increasing from 1047 °C to 1071 °C had hardly effect on the magnetic properties of sintered Nd-Fe-B magnets. The variation of Vickers hardness and fracture toughness was not the same with increasing sintering temperature, and the effect of sintering temperature on the mechanical properties was complex and irregular. The reasons for the variation on magnetic and mechanical properties were analyzed, and we presumed that the effect of microstructure on the mechanical properties was more sensitive than the magnetic properties through analyzing the microstructure of sintered Nd-Fe-B magnets.

Feasibility study of electrophoresis deposition of DyF3 on Nd-Fe-B particles for coercivity enhancement

NASA Astrophysics Data System (ADS)

Kim, K. M.; Kang, M. S.; Kwon, H. W.; Lee, J. G.; Yu, J. H.

2018-05-01

Feasibility of the electrophoresis deposition (EPD) technique for homogeneous and adhesive deposition of DyF3 particles on the Nd-Fe-B-type particles was studied, and coercivity enhancement in the diffusion-treated Nd-Fe-B-type particles deposited with DyF3 by EPD was investigated. HDDR-treated Nd12.5Fe80.6B6.4Ga0.3Nb0.2 particles were deposited with DyF3 particles by EPD. More homogeneous and adhesive deposition of DyF3 particles on the surface of Nd-Fe-B particles was made by the EPD with respect to conventional dip-coating, and this led to more active and homogeneous diffusion of Dy. More profound coercivity enhancement was achieved in the diffusion-treated Nd-Fe-B-type particles deposited with DyF3 by EPD compared to dip-coated particles.

Low temperature diffusion process using rare earth-Cu eutectic alloys for hot-deformed Nd-Fe-B bulk magnets

DOE Office of Scientific and Technical Information (OSTI.GOV)

Akiya, T., E-mail: akiya.takahiro@nims.go.jp; Sepehri-Amin, H.; Ohkubo, T.

2014-05-07

The low temperature grain boundary diffusion process using RE{sub 70}Cu{sub 30} (RE = Pr, Nd) eutectic alloy powders was applied to sintered and hot-deformed Nd-Fe-B bulk magnets. Although only marginal coercivity increase was observed in sintered magnets, a substantial enhancement in coercivity was observed when the process was applied to hot-deformed anisotropic bulk magnets. Using Pr{sub 70}Cu{sub 30} eutectic alloy as a diffusion source, the coercivity was enhanced from 1.65 T to 2.56 T. The hot-deformed sample expanded along c-axis direction only after the diffusion process as RE rich intergranular layers parallel to the broad surface of the Nd{sub 2}Fe{sub 14}B are thickened inmore » the c-axis direction.« less

Effects of trace elements on the crystal field parameters of Nd ions at the surface of Nd{sub 2}Fe{sub 14}B grains

DOE Office of Scientific and Technical Information (OSTI.GOV)

Toga, Yuta; Suzuki, Tsuneaki; Sakuma, Akimasa, E-mail: sakuma@solid.apph.tohoku.ac.jp

2015-06-14

Using first-principles calculations, we investigate the positional dependence of trace elements such as O and Cu on the crystal field parameter A{sub 2}{sup 0}, proportional to the magnetic anisotropy constant K{sub u} of Nd ions placed at the surface of Nd{sub 2}Fe{sub 14}B grains. The results suggest the possibility that the A{sub 2}{sup 0} parameter of Nd ions at the (001) surface of Nd{sub 2}Fe{sub 14}B grains exhibits a negative value when the O or Cu atom is located near the surface, closer than its equilibrium position. At the (110) surface, however, O atoms located at the equilibrium position providemore » a negative A{sub 2}{sup 0}, while for Cu additions A{sub 2}{sup 0} remains positive regardless of Cu's position. Thus, Cu atoms are expected to maintain a positive local K{sub u} of surface Nd ions more frequently than O atoms when they approach the grain surfaces in the Nd-Fe-B grains.« less

Multiple magnetic scattering in small-angle neutron scattering of Nd-Fe-B nanocrystalline magnet.

PubMed

Ueno, Tetsuro; Saito, Kotaro; Yano, Masao; Ito, Masaaki; Shoji, Tetsuya; Sakuma, Noritsugu; Kato, Akira; Manabe, Akira; Hashimoto, Ai; Gilbert, Elliot P; Keiderling, Uwe; Ono, Kanta

2016-06-20

We have investigated the influence of multiple scattering on the magnetic small-angle neutron scattering (SANS) from a Nd-Fe-B nanocrystalline magnet. We performed sample-thickness- and neutron-wavelength-dependent SANS measurements, and observed the scattering vector dependence of the multiple magnetic scattering. It is revealed that significant multiple scattering exists in the magnetic scattering rather than the nuclear scattering of Nd-Fe-B nanocrystalline magnet. It is considered that the mean free path of the neutrons for magnetic scattering is rather short in Nd-Fe-B magnets. We analysed the SANS data by the phenomenological magnetic correlation model considering the magnetic microstructures and obtained the microstructural parameters.

Electronic structure of the (Nd{sub 1−x}Dy{sub x}){sub 2}Fe{sub 14}B (0 ≤ x ≤ 1) system studied by X-ray photoelectron spectroscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Jing; Liang, Le; Yang, Bin

2015-09-15

Systematic characterization of electronic structures in the (Nd{sub 1−x}Dy{sub x}){sub 2}Fe{sub 14}B system, especially the 4f behavior, provides an insight to the physical nature of the evolution of magnetic properties. A series of X-ray photoelectron spectroscopy (XPS) core-level and valence-band spectra were used to study the electronic structures. It was found that substitution of Dy for Nd in Nd{sub 2}Fe{sub 14}B results in a nonlinear variation in the evolution of electronic structures. Only the finite coupling between the Nd 4f states and the Fe 3d states is found at both the Nd-rich regime and the Dy-rich regime. When the Dymore » concentration and the Nd concentration approach to be equal, a strong coupling between the Nd 4f states and the Fe 3d states is found, which results in a bonding state between them. Additionally, the 4f components in the (Nd{sub 1−x}Dy{sub x}){sub 2}Fe{sub 14}B system are ascribed to three parts: 1) the individual contribution of the Dy 4f states, which emerges just after the Dy-substitution; 2) the contribution of the coupling between the Nd 4f states and the Dy 4f states, which arises only when 0.4 ≤ x ≤ 0.6; 3) the associated contributions of the Nd 4f states and the Dy 4f states, where the contribution of the Nd 4f states and that of the Dy 4f states are prominent in the Nd-rich regime and Dy-rich regime, respectively.« less

Effect of oxygen content of Nd-Fe-B sintered magnet on grain boundary diffusion process of DyH2 dip-coating

NASA Astrophysics Data System (ADS)

Bae, Kyoung-Hoon; Lee, Seong-Rae; Kim, Hyo-Jun; Lee, Min-Woo; Jang, Tae-Suk

2015-11-01

We investigated the effect of oxygen content on the microstructural and magnetic properties of a DyH2 dip-coated Nd-Fe-B sintered magnet. When the magnet had a low oxygen content (1500 ppm), the volume and size of the rare-earth-rich oxide (Nd-Dy-O) phase was reduced, and a uniform and continuous thin Nd-rich grain boundary phase (GBP) was well developed. The grain boundary diffusion depth of Dy increased from 200 to 350 μm with decreasing oxygen content from ˜3000 to 1500 ppm. The coercivity of the low-oxygen magnet increased from 19.98 to 23.59 kOe after grain boundary diffusion process (GBDP) while the remanence reduction was minimized. The formation of an fcc-NdOx Nd-rich phase in the high-oxygen magnet hindered the formation of a Nd-rich triple-junction phase and GBP. In contrast, a metallic dhcp-Nd phase, which was closely related to coercivity enhancement after GBDP, was formed in the low-oxygen magnet.

Selective Extraction and Recovery of Nd and Dy from Nd-Fe-B Magnet Scrap by Utilizing Molten MgCl2

NASA Astrophysics Data System (ADS)

Shirayama, Sakae; Okabe, Toru H.

2018-06-01

Fundamental experiments are conducted with the aim of developing an efficient recycling process for rare earth elements (REEs) from neodymium-iron-boron (Nd-Fe-B) permanent magnet scrap. Molten magnesium dichloride (MgCl2) was chosen as an extraction medium, which can selectively chlorinate and extract REEs in magnet alloys. Dysprosium-containing Nd-Fe-B magnet alloy was immersed in molten MgCl2 at 1273 K (1000 °C) for 3 to 12 hours. The results of the experiments clearly show that the REEs in the magnetic alloy were successfully extracted into the molten salt, while the Fe-B alloy remained in a solid form. The extraction ratios of Nd and Dy were at most 87 and 78 mass pct, respectively. After the extraction experiment, excess MgCl2 and Mg were removed by vacuum distillation and the rare earth chlorides were recovered. Thus, the feasibility of this method for efficient recovery of rare earths using molten MgCl2 is demonstrated.

Selective Extraction and Recovery of Nd and Dy from Nd-Fe-B Magnet Scrap by Utilizing Molten MgCl2

NASA Astrophysics Data System (ADS)

Shirayama, Sakae; Okabe, Toru H.

2018-02-01

Fundamental experiments are conducted with the aim of developing an efficient recycling process for rare earth elements (REEs) from neodymium-iron-boron (Nd-Fe-B) permanent magnet scrap. Molten magnesium dichloride (MgCl2) was chosen as an extraction medium, which can selectively chlorinate and extract REEs in magnet alloys. Dysprosium-containing Nd-Fe-B magnet alloy was immersed in molten MgCl2 at 1273 K (1000 °C) for 3 to 12 hours. The results of the experiments clearly show that the REEs in the magnetic alloy were successfully extracted into the molten salt, while the Fe-B alloy remained in a solid form. The extraction ratios of Nd and Dy were at most 87 and 78 mass pct, respectively. After the extraction experiment, excess MgCl2 and Mg were removed by vacuum distillation and the rare earth chlorides were recovered. Thus, the feasibility of this method for efficient recovery of rare earths using molten MgCl2 is demonstrated.

Soapnut extract mediated synthesis of nanoscale cobalt substituted NdFeB ferromagnetic materials and their characterization

NASA Astrophysics Data System (ADS)

Rao, G. V. S. Jayapala; Prasad, T. N. V. K. V.; Shameer, Syed; Rao, M. Purnachandra

2018-04-01

Neodymium iron boron (NdFeB) permanent magnets have high energy product with suitable magnetic and physical properties for an array of applications including power generation and motors. However, synthetic routes of NdFeB permanent magnets involve critical procedures with high energy and needs scientific skills. Herein, we report on soapnut extract mediated synthesis of nanoscale cobalt substituted NdFeB (Co-NdFeB) permanent magnetic powders (Nd: 15%, Fe: 77.5%, B: 7.5% and Co with molar ratios: 0.5, 1, 1.5 and 2). A 10 ml of 10% soapnut extract was added to 90 ml of respective chemical composition and heated to 60 °C for 30 min and aged for 24 h. The dried powder was sintered at 500 °C for 1 h. The characterization of the prepared nanoscale Co-NdFeB magnetic powders was done using the techniques such as Dynamic Light Scattering (DLS for size and zeta potential measurements), X-ray diffraction (XRD) for structural determination, Scanning electron microscopy (SEM) with energy dispersion spectroscopy (EDS) for surface morphological and elemental analysis, Fourier transform infrared spectroscopy (FT-IR) for the identification of functional groups associated and hysteresis loop studies to quantify the magnetization. The results revealed that particles were in irregular and tubular shaped and highly stable (Zeta potential: -44.4 mV) with measured size <100 nm. XRD micrographs revealed a tetragonal crystal structure and FTIR showed predominant N-H and O-H stretching indicates the involvement of these functional groups in the reduction and stabilization process of Co-NdFeB magnetic powders. Hysteresis studies signify the effect of an increase in Co concentration.

Demagnetization of Nd 2Fe 14B, Pr 2Fe 14B, and Sm 2Co 17 Permanent Magnets in Spallation Irradiation Fields

DOE PAGES

Simos, Nikolaos; Ozaki, S.; Mokhov, N.; ...

2018-02-27

Prompted by the need for radiation-resistant permanent magnets for insertion devices (IDs) of high-brilliance next-generation synchrotrons such as the National Synchrotron Light Source II, the demagnetization of Nd 2Fe 14B and Pr 2Fe 14B was studied after exposure to a mixed irradiating field. Degradation and damage of the permanent magnetic material by components of electromagnetic showers induced in magnets by intense high-energy electron beams will alter the magnetic field structure of the IDs. Plate-like Nd 2Fe 14B magnets were irradiated to 1.8 Grad dose and were evaluated against Pr 2Fe 14B magnets irradiated to a lower dose of 20 Mrad.more » In addition, annular Sm 2Co 17 and Nd 2Fe 14B magnets integrated within a ferrofluidic feedthrough (FFFT) rotary seal were also irradiated to dose levels of 2 Grad for Sm 2Co 17 and 20 Mrad for Nd 2Fe 14B. Post-irradiation measurements of the magnetic intensity revealed that severe demagnetization exceeding 85% occurs in Nd 2Fe 14B magnets after only 50 Mrad dose and over 87% for Pr 2Fe 14B after 10 Mrad dose. The annular-shaped Sm 2Co 17 magnets of the FFFTs were almost insensitive to irradiation up to a dose of 2 Grad. Annular-shaped Nd 2Fe 14B magnets also showed resistance to demagnetization, a direct consequence of the annular shape which is characterized by the removal of the stronger demagnetizing field present at the center of a disk-like magnet. As a result, the sensitivity of boron-based permanent magnets to neutron energy (thermal versus fast) was also assessed via specifically designed experiments and discussed.« less

Demagnetization of Nd 2Fe 14B, Pr 2Fe 14B, and Sm 2Co 17 Permanent Magnets in Spallation Irradiation Fields

DOE Office of Scientific and Technical Information (OSTI.GOV)

Simos, Nikolaos; Ozaki, S.; Mokhov, N.

Prompted by the need for radiation-resistant permanent magnets for insertion devices (IDs) of high-brilliance next-generation synchrotrons such as the National Synchrotron Light Source II, the demagnetization of Nd 2Fe 14B and Pr 2Fe 14B was studied after exposure to a mixed irradiating field. Degradation and damage of the permanent magnetic material by components of electromagnetic showers induced in magnets by intense high-energy electron beams will alter the magnetic field structure of the IDs. Plate-like Nd 2Fe 14B magnets were irradiated to 1.8 Grad dose and were evaluated against Pr 2Fe 14B magnets irradiated to a lower dose of 20 Mrad.more » In addition, annular Sm 2Co 17 and Nd 2Fe 14B magnets integrated within a ferrofluidic feedthrough (FFFT) rotary seal were also irradiated to dose levels of 2 Grad for Sm 2Co 17 and 20 Mrad for Nd 2Fe 14B. Post-irradiation measurements of the magnetic intensity revealed that severe demagnetization exceeding 85% occurs in Nd 2Fe 14B magnets after only 50 Mrad dose and over 87% for Pr 2Fe 14B after 10 Mrad dose. The annular-shaped Sm 2Co 17 magnets of the FFFTs were almost insensitive to irradiation up to a dose of 2 Grad. Annular-shaped Nd 2Fe 14B magnets also showed resistance to demagnetization, a direct consequence of the annular shape which is characterized by the removal of the stronger demagnetizing field present at the center of a disk-like magnet. As a result, the sensitivity of boron-based permanent magnets to neutron energy (thermal versus fast) was also assessed via specifically designed experiments and discussed.« less

2Flux growth and characterization of Ce-substituted Nd 2 Fe 14 B single crystals

DOE PAGES

Susner, Michael A.; Conner, Benjamin S.; Saparov, Bayrammurad I.; ...

2016-10-27

Single crystals of (Nd 1-xCe x) 2Fe 14B are grown out of Fe-(Nd,Ce) flux. Chemical and structural analysis of the crystals indicate that (Nd 1-xCe x) 2Fe 14B forms a solid solution until at least x = 0.38 with a Vegard-like variation of the lattice constants with x. Refinements of single crystal neutron diffraction data indicate that Ce has a slight site preference (7:3) for the 4g rare earth site over the 4f site. Magnetization measurements at 300 K show only small decreases with increasing Ce content in saturation magnetization (M s) and anisotropy field (H A), and Curie temperaturemore » (T C). First principles calculations are carried out to understand the effect of Ce substitution on the electronic and magnetic properties. For a multitude of applications, it is expected that the advantage of incorporating lower-cost and more abundant Ce will outweigh the small adverse effects on magnetic properties. In conclusion, Ce-substituted Nd 2Fe 14B is therefore a potential high-performance permanent magnet material with substantially reduced Nd content.« less

The effect of CuAl addition on the magnetic property, thermal stability and corrosion resistance of the sintered NdFeB magnets

NASA Astrophysics Data System (ADS)

Liu, Y. L.; Liang, J.; He, Y. Ch.; Li, Y. F.; Wang, G. F.; Ma, Q.; Liu, F.; Zhang, Y.; Zhang, X. F.

2018-05-01

To improve the coercivity of the Nd-Fe-B sintered magnets, the Cu29.8Al70.2 (at.%) powders with low melting point were introduced into the Nd-Fe-B magnets. The magnetic properties, microstructure, thermal stability and corrosion behavior of the sintered magnets with different amount of Cu29.8Al70.2 (0,0.25,0.50,0.75,1.0 wt.%) were investigated. When the amount of doped Cu29.8Al70.2 was less than 0.75 wt.%, the coercivity was improved, especially that of the magnets with 0.25 wt.% Cu29.8Al70.2, markedly increased to 13.97 kOe from 12.67 kOe (without CuAl). The improvement of magnetic properties could be attributed to enhanced wettability between Nd2Fe14B phase and Nd-rich phase and decreased exchange coupling between grains, which depended on the optimization of grain boundary microstructure and their distribution by codoping Cu and Al. With the addition of 0-1.0 wt.% Cu29.8Al70.2 powders, the reversible temperature coefficients of remanence and coercivity of the magnets could be also improved. The corrosion resistances was also found to be improved through small addition of Cu29.8Al70.2 powder in 3.5 wt.% NaCl solution by electrochemical and immersion tests, which could be due to the enhancement of the Nd-rich intergranular phase by addition Cu29.8Al70.2.

Temperature and field direction dependences of first-order reversal curve (FORC) diagrams of hot-deformed Nd-Fe-B magnets

NASA Astrophysics Data System (ADS)

Yomogita, Takahiro; Okamoto, Satoshi; Kikuchi, Nobuaki; Kitakami, Osamu; Sepehri-Amin, Hossein; Ohkubo, Tadakatsu; Hono, Kazuhiro; Akiya, Takahiro; Hioki, Keiko; Hattori, Atsushi

2018-02-01

First-order reversal curve (FORC) diagram has been previously adopted for the analyses of magnetization reversal process and/or quantitative evaluation of coercivity and interaction field dispersions in various magnetic samples. Although these kinds of information are valuable for permanent magnets, previously reported FORC diagrams of sintered Nd-Fe-B magnets exhibit very complicated patterns. In this paper, we have studied the FORC diagrams of hot-deformed Nd-Fe-B magnets under various conditions. Contrary to the previous reports on sintered Nd-Fe-B magnets, the FORC diagram of the hot-deformed Nd-Fe-B magnet exhibits a very simple pattern consisting of a strong spot and a weak line. From this FORC diagram pattern, it is revealed that the coercivity dispersion of the hot-deformed Nd-Fe-B magnets is surprisingly small. Moreover, this feature of the FORC diagram pattern is very robust and unaffected by changes in various conditions such as grain boundary diffusion process, temperature, and field direction, whereas these conditions significantly change the coercivity and the shape of magnetization curve. This fact indicates that the magnetization reversal process of the hot-deformed Nd-Fe-B magnets is almost unchanged against these conditions.

Modelling of the material flow of Nd-Fe-B magnets under high temperature deformation via finite element simulation method

PubMed Central

Chen, Yen-Ju; Lee, Yen-I; Chang, Wen-Cheng; Hsiao, Po-Jen; You, Jr-Shian; Wang, Chun-Chieh; Wei, Chia-Min

2017-01-01

Abstract Hot deformation of Nd-Fe-B magnets has been studied for more than three decades. With a good combination of forming processing parameters, the remanence and (BH)max values of Nd-Fe-B magnets could be greatly increased due to the formation of anisotropic microstructures during hot deformation. In this work, a methodology is proposed for visualizing the material flow in hot-deformed Nd-Fe-B magnets via finite element simulation. Material flow in hot-deformed Nd-Fe-B magnets could be predicted by simulation, which fitted with experimental results. By utilizing this methodology, the correlation between strain distribution and magnetic properties enhancement could be better understood. PMID:28970869

Improved magnetic properties and thermal stabilities of Pr-Nd-Fe-B sintered magnets by Hf addition

NASA Astrophysics Data System (ADS)

Jiang, Qingzheng; Lei, Weikai; Zeng, Qingwen; Quan, Qichen; Zhang, Lili; Liu, Renhui; Hu, Xianjun; He, Lunke; Qi, Zhiqi; Ju, Zhihua; Zhong, Minglong; Ma, Shengcan; Zhong, Zhenchen

2018-05-01

Nd2Fe14B-type permanent magnets have been widely applied in various fields such as wind power, voice coil motors, and medical instruments. The large temperature dependence of coercivity, however, limits their further applications. We have systematically investigated the magnetic properties, thermal stabilities and coercivity mechanisms of the (Pr0.2Nd0.8)13Fe81-xB6Hfx (x=0, 0.5) nanocrystalline magnets fabricated by a spark plasma sintering (SPS) technique. The results indicate that the influence of Hf addition is significant on magnetic properties and thermal stabilities of the (PrNd)2Fe14B-type sintered magnets. It is shown that the sample with x = 0.5 at 300 K has much higher coercivity and remanent magnetization than those counterparts without Hf. The temperature coefficients of remanence (α) and coercivity (β) of the (Pr0.2Nd0.8)13Fe81-xB6Hfx magnets are improved significantly from -0.23 %/K, -0.57 %/K for the sample at x = 0 to -0.17 %/K, -0.49 %/K for the sample at x = 0.5 in the temperature range of 300-400 K. Furthermore, it is found out that the domain wall pinning mechanism is more likely responsible for enhancing the coercivity of the (Pr0.2Nd0.8)13Fe81-xB6Hfx magnets.

Magnetic properties and magnetization reversal mechanism of Nd-Fe-B nanoparticles synthesized by a sol-gel method

NASA Astrophysics Data System (ADS)

Rahimi, Hamed; Ghasemi, Ali; Mozaffarinia, Reza; Tavoosi, Majid

2017-12-01

Nd-Fe-B oxide powders with various pH were prepared using chloride and nitrate precursors including NdCl3·6H2O, FeCl3·6H2O, H3BO3, Nd2O3, Fe(NO3)3·9H2O, HNO3, citric acid (CA), ethylene glycol (EG) by Pechini type sol-gel method. The pH of chloride and nitrate base sols were 0 and 2.2, respectively. Mixed oxide powders were obtained by calcination and annealing the gels. These oxides by using a reduction-diffusion process under high vacuum and employing CaH2 as reducing agent at 800 °C were hated to prepare Nd2Fe14B nanoparticles. The role of pH on phase, morphologies, microstructure, and magnetic properties of the powders were investigated. The results show that with a decrease in pH, the average particle size and coercivity of Nd-Fe-B oxide powders were decreased and increased, respectively. Nd2Fe14B nanoparticles were formed successfully after reduction process. The average particle size of reduction treated products were 30 and 65 nm for powders which made of chloride and nitrate base metal salts, respectively. Final powders which made of chloride and nitrate base metal salts had a saturation magnetization of 127.7 emu/g and 122.8 emu/g while the coercivity of samples were 3.32 kOe and 1.82 kOe, respectively. The experimental results in the angular dependence of coercivity indicated that the normalized coercivity of the permanent magnets Hc(θ)/Hc(0) obeys the 1/cosθ law and intermediate between the 1/cosθ law and Stoner-Wohlfarth formula for different Nd2Fe14B magnets which made of nitrate and chloride base metal salts, respectively. Also, the results show that different Nd2Fe14B magnets which made of nitrate and chloride base metal salts had the maximum energy product of 5 and 16 MGOe, respectively. The Henkel plot showed that magnetic phases in synthesized NdFeB magnets which made of chloride and nitrate base metal salts were coupled by exchange and dipolar interactions, respectively. Different average particle size, morphology and microstructure were

Efficient reuse of the waste sintered NdFeB magnet with Dy2O3 addition

NASA Astrophysics Data System (ADS)

Li, Chencheng; Sun, Aizhi; Tian, Zhenya; Zhang, Xun; Ma, Bin

2018-09-01

In this paper, the efficient recycling method of sintered NdFeB waste was studied. The production process can be greatly simplified by crushing the recovered waste magnet into hundreds of micron-sized magnetic powder and preparing the magnet directly with orientating, molding and sintering. The magnetic properties of the magnet prepared by commercial N45 recovered waste can reach Br = 1.09 T, (BH)max = 196 kJ/m3 and Hcj = 601 kA/m. Adding a small amount of Dy2O3 can significantly improve the Br of the above magnet. The maximum Hcj can reach 1310 kA/m and (BH)max can reach 204 kJ/m3. The microstructure analysis shows that Dy2O3 diffused along the grain boundaries mainly and forms Dy-rich shell around the Nd2Fe14B grains which increase the difficulty of forming anti-magnetization.

Angular dependence of coercivity in isotropically aligned Nd-Fe-B sintered magnets

NASA Astrophysics Data System (ADS)

Matsuura, Yutaka; Nakamura, Tetsuya; Sumitani, Kazushi; Kajiwara, Kentaro; Tamura, Ryuji; Osamura, Kozo

2018-05-01

In order to understand the coercivity mechanism in Nd-Fe-B sintered magnets, the angular dependence of the coercivity of an isotropically aligned Nd15Co1.0B6Febal. sintered magnet was investigated through magnetization measurements using a vibrating sample magnetometer. These results are compared with the angular dependence calculated under the assumption that the magnetization reversal of each grain follows the Kondorskii law or, in other words, the 1/cos θ law for isotropic alignment distributions. The calculated angular dependence of the coercivity agrees very well with the experiment for magnetic fields applied between angles of 0 and 60°, and it is expected that the magnetization reversal occurs in each grain individually followed the 1/cos θ law. In contrast, this agreement between calculation and experiment is not found for anisotropic Nd-Fe-B samples. This implies that the coercivity of the aligned magnets depends upon the de-pinning of the domain walls from pinning sites. When the de-pinning occurs, it is expected that the domain walls are displaced through several grains at once.

Re-exchange of Fe and Cu at the interface in sintered Nd-Fe-B magnets: A method to eliminate Fe precipitation at grain boundaries

NASA Astrophysics Data System (ADS)

Yang, YuQi; Si, HengGang; Yang, Hao; Zhang, Lan; Huang, DongFang; Chen, BaiYi; Xu, Fang; Hu, YongMei; Han, BaoJun

2018-01-01

According to the decoupling hypothesis for magnetic grains, the coercivity in sintered Nd-Fe-B magnets is increased after Cu doping, which is due to the formation of non-magnetic grain boundaries. However, this method partially fails, and ferromagnetic Fe-segregation occurs at the grain boundary. We discovered both experimentally and through calculation that the Fe content at the grain boundaries can be tuned across a wide range by introducing another element of Ag. Segregated Fe at high temperature at the grain boundary re-dissolves into Nd2Fe14B grains during annealing at low temperature. Both configurable and magnetic entropies contribute a large driving force for the formation of nonmagnetic grain boundaries. Almost zero Fe content could be achieved at the grain boundaries of sintered Nd-Fe-B magnet.

Material flow analysis of NdFeB magnets for Denmark: a comprehensive waste flow sampling and analysis approach.

PubMed

Habib, Komal; Schibye, Peter Klausen; Vestbø, Andreas Peter; Dall, Ole; Wenzel, Henrik

2014-10-21

Neodymium-iron-boron (NdFeB) magnets have become highly desirable for modern hi-tech applications. These magnets, in general, contain two key rare earth elements (REEs), i.e., neodymium (Nd) and dysprosium (Dy), which are responsible for the very high strength of these magnets, allowing for considerable size and weight reduction in modern applications. This study aims to explore the current and future potential of a secondary supply of neodymium and dysprosium from recycling of NdFeB magnets. For this purpose, material flow analysis (MFA) has been carried out to perform the detailed mapping of stocks and flows of NdFeB magnets in Denmark. A novel element of this study is the value added to the traditionally practiced MFAs at national and/or global levels by complementing them with a comprehensive sampling and elemental analysis of NdFeB magnets, taken out from a sample of 157 different products representing 18 various product types. The results show that the current amount of neodymium and dysprosium in NdFeB magnets present in the Danish waste stream is only 3 and 0.2 Mg, respectively. However, this number is estimated to increase to 175 Mg of neodymium and 11.4 Mg of dysprosium by 2035. Nevertheless, efficient recovery of these elements from a very diverse electronic waste stream remains a logistic and economic challenge.

Micro-patterning of resin-bonded NdFeB magnet for a fully integrated electromagnetic actuator

NASA Astrophysics Data System (ADS)

Tao, Kai; Wu, Jin; Kottapalli, Ajay Giri Prakash; Chen, Di; Yang, Zhuoqing; Ding, Guifu; Lye, Sun Woh; Miao, Jianmin

2017-12-01

This paper reports a fully-integrated, batch-fabricated electromagnetic actuator which features micro-patterned NdFeB magnets. The entire actuator is fabricated through MEMS-compatible laminated surface micromachining technology, eliminating the requirement for further component assembly processes. The fabrication strategy allowed the entire volume of the actuator to be reduced to a small size of 2.5 × 2.5 × 2 mm3, which is one of the smallest NdFeB-based electromagnetic actuators demonstrated to date. The magnetic properties of NdFeB thin films are further investigated and optimized using different types of lithographically-defined micromolds. By altering the direction of the input current, actuating displacements of approximately ±10 μm are achieved during both the attraction and the repulsion operations. This work demonstrates the viability and compatibility of using polymer-bonded magnets for magnetic MEMS applications.

Effect of Nb doping on the microstructure and magnetic properties of Nd-Ce-Fe-B alloy

NASA Astrophysics Data System (ADS)

Quan, Qichen; Zhang, Lili; Jiang, Qingzheng; Lei, Weikai; Zeng, Qingwen; Hu, Xianjun; Wang, Lei; Yu, Xi; Du, Junfeng; Fu, Gang; Liu, Renhui; Zhong, Minglong; Zhong, Zhenchen

2017-11-01

With the intention to reduce the Nd content in Nd2Fe14B-type alloys, 20 at.% Ce and 0.5 at.% Nb substituting Nd and Fe in the Nd13Fe82B5 alloys were previously employed to improve successfully the coercivity and the thermal stability without the energy product reduction. In this study, a light increase of the remnant polarization Jr was observed in (Nd0.8Ce0.2)13Fe82-xNbxB5 alloy at x = 0.5 and x = 1.0, resulting from the increasing amount of α-Fe phase. The optimum magnetic properties obtained with 0.5 at.% Nb doping are Hcj = 13.1 kOe, Jr = 0.79 T, (BH)max = 13.3 MGOe, respectively. Besides, the coercivity Hcj and maximum energy product (BH)max for the melt-spun ribbons with 0.5 at.% Nb addition are higher than those of the Nb-free ribbons in the temperature range of 300-450 K. Both the variations of Curie temperature Tc and a increase of lattice constants a and c of the hard magnetic phase with Nb addition imply that some of Nb atoms may directly enter into the hard magnetic phase, occupying the Fe sites. With the analysis on the demagnetization curve, Henkel curve and the observation of transmission electron microscope (TEM), the results indicate that a small amount of Nb can enhance the coercivity and exchange coupling though improving the microstructure of alloys.

XMCD and TEM studies of as-cast and rapidly quenched Fe50Nd50 alloys

NASA Astrophysics Data System (ADS)

Menushenkov, V. P.; Menushenkov, A. P.; Shchetinin, I. V.; Wilhelm, F.; Ivanov, A. A.; Rudnev, I. A.; Ivanov, V. G.; Rogalev, A.; Savchenko, A. G.; Zhukov, D. G.; Rafalskiy, A. V.; Ketov, S. V.

2017-12-01

We present the XMCD analysis of as-cast and melt spun Fe50Nd50 samples performed at L2,3 -Nd and K-Fe absorption edges at 5 and 50 K in comparison with macroscopic data of XRD, TEM and magnetic properties measurements. In addition, we have measured the magnetic field dependence of XMCD signal for both types of the samples in magnetic fields up/down to 17 T. The obtained results pointed to the strong difference between structure and magnetic properties of the as-cast and melt spun Fe50Nd50 alloys for both macroscopic and local measurements. The element selective XMCD loops for melt spun alloy show almost identical value of the coercive force Hci for L 2-Nd and K-Fe edges and practically do not depend on temperature. XMCD loop at K-Fe edge is a sum of contributions of the Fe-based phases. The main Fe-rich phase has high Hci ≈ 2,4 T as a highly anisotropic phase. The absence of the K-Fe XMCD loop saturation in the field up to 17 T points to presence of the second Nd-rich Nd-Fe phase which is ferromagnetic at temperature lower than 50 K. In accordance to the TEM results these both phases may coexist as the mixture of nanocrystals which was formed as a result of decomposition of the amorphous-like matrix phase. The XMCD loop at L2 -Nd edge with Hci ≈ 1,9 T is the sum of contributions from two Nd-based phases: hard Fe-rich phase (Hci ≈ 2,4 T) and Nd-Fe matrix phase of medium hardness with Hci ≈ 1,3 T. The macroscopic loop showed the higher Hci compared to XMCD loops. Such discrepancy may be caused by the fact that XMCD signal is collected from a 5-10 mcm thick surface layer, which contains many defects that reduce anisotropy and coercivity.

Nd2O3-SiO2 nanocomposites: A simple sonochemical preparation, characterization and photocatalytic activity.

PubMed

Zinatloo-Ajabshir, Sahar; Mortazavi-Derazkola, Sobhan; Salavati-Niasari, Masoud

2018-04-01

Nd 2 O 3 -SiO 2 nanocomposites with enhanced photocatalytic activity have been obtained through simple and rapid sonochemical route in presence of putrescine as a new basic agent, for the first time. The influence of the mole ratio of Si:Nd, basic agent and ultrasonic power have been optimized to obtain the best Nd 2 O 3 -SiO 2 nanocomposites on shape, size and photocatalytic activity. The produced Nd 2 O 3 -SiO 2 nanocomposites have been characterized utilizing XRD, EDX, TEM, FT-IR, DRS and FESEM. Application of the as-formed Nd 2 O 3 -SiO 2 nano and bulk structures as photocatalyst with photodegradation of methyl violet contaminant under ultraviolet illumination was compared. Results demonstrated that SiO 2 has remarkable effect on catalytic performance of Nd 2 O 3 photocatalyst for decomposition. By introducing of SiO 2 to Nd 2 O 3 , decomposition efficiency of Nd 2 O 3 toward methyl violet contaminant under ultraviolet illumination was increased. Copyright © 2017 Elsevier B.V. All rights reserved.

Assessment of corrosion resistance of Nd-Fe-B magnets by silanization for orthodontic applications

NASA Astrophysics Data System (ADS)

Fabiano, F.; Celegato, F.; Giordano, A.; Borsellino, C.; Bonaccorsi, L.; Calabrese, L.; Tiberto, P.; Cordasco, G.; Matarese, G.; Fabiano, V.; Azzerboni, B.

2014-02-01

Nd-Fe-B permanent magnets are characterised by excellent magnetic properties. However, being extremely vulnerable to the attack of both climate and corrosive environments, their applications are limited. This paper describes how, at different thicknesses of N-propyl-trimetoxy-silane, the coating affects the magnetic force of nickel plated magnets. We also investigate if the corrosion resistance of silanized Nd-Fe-B magnets increases in mildly corrosive environments by immersing them in a synthetic saliva solution. It was found that the silanization treatment does not affect the strength of the magnetic force and provide an enhancement of the corrosion resistance of the substrate.

Coercivity enhancement of Dy-coated Nd-Fe-B flakes by crystallization

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fukunaga, H.; Sugimoto, Y.; Nakano, M.

2011-04-01

The coercivity of isotropic Dy-coated Nd-Fe-B flakes was enhanced by crystallization and simultaneous diffusion of Dy from their surfaces. Amorphous Dy-coated Nd-Fe-B flakes were crystallized by heating them to 923 K 2over a 2 min period followed by rapid cooling. During crystallization, the Dy on the surface diffused into the flakes. This low-temperature rapid annealing produced flakes with fine grains and the Dy diffusion enhanced their coercivity. The coercivity after crystallization increased with increasing Dy layer thickness, although the remanence decreased when the layer thickness exceeded 3 {mu}m. Thick coatings of over 6 {mu}m resulted in the formation of DyFe{submore » 2}, which degraded the magnetic properties of the crystallized flakes. Flakes with a 3-{mu}m-thick coating exhibited excellent magnetic properties after annealing: They had a coercivity of 1880 kA/m and a remanence of 78 emu/g. This coercivity is approximately 500 kA/m higher than that of uncoated flakes, whereas the remanence is comparable to that of uncoated flakes.« less

High coercivity, anisotropic, heavy rare earth-free Nd-Fe-B by Flash Spark Plasma Sintering.

PubMed

Castle, Elinor; Sheridan, Richard; Zhou, Wei; Grasso, Salvatore; Walton, Allan; Reece, Michael J

2017-09-11

In the drive to reduce the critical Heavy Rare Earth (HRE) content of magnets for green technologies, HRE-free Nd-Fe-B has become an attractive option. HRE is added to Nd-Fe-B to enhance the high temperature performance of the magnets. To produce similar high temperature properties without HRE, a crystallographically textured nanoscale grain structure is ideal; and this conventionally requires expensive "die upset" processing routes. Here, a Flash Spark Plasma Sintering (FSPS) process has been applied to a Dy-free Nd 30.0 Fe 61.8 Co 5.8 Ga 0.6 Al 0.1 B 0.9 melt spun powder (MQU-F, neo Magnequench). Rapid sinter-forging of a green compact to near theoretical density was achieved during the 10 s process, and therefore represents a quick and efficient means of producing die-upset Nd-Fe-B material. The microstructure of the FSPS samples was investigated by SEM and TEM imaging, and the observations were used to guide the optimisation of the process. The most optimal sample is compared directly to commercially die-upset forged (MQIII-F) material made from the same MQU-F powder. It is shown that the grain size of the FSPS material is halved in comparison to the MQIII-F material, leading to a 14% increase in coercivity (1438 kA m -1 ) and matched remanence (1.16 T) giving a BH max of 230 kJ m -3 .

CRADA/NFE-15-05761 Report: Additive Manufacturing of Isotropic NdFeB Bonded Permanent Magnets

DOE Office of Scientific and Technical Information (OSTI.GOV)

Paranthaman, M. Parans

2016-07-18

The technical objective of this technical collaboration phase I proposal is to fabricate net shape isotropic NdFeB bonded magnets utilizing additive manufacturing technologies at the ORNL MDF. The goal is to form complex shapes of thermoplastic and/or thermoset bonded magnets without expensive tooling and with minimal wasted material. Two additive manufacturing methods; the binder jet process; and big area additive manufacturing (BAAM) were used. Binder jetting produced magnets with the measured density of the magnet of 3.47 g/cm 3, close to 46% relative to the NdFeB single crystal density of 7.6 g/cm 3 were demonstrated. Magnetic measurements indicate that theremore » is no degradation in the magnetic properties. In addition, BAAM was used to fabricate isotropic near-net-shape NdFeB bonded magnets with magnetic and mechanical properties comparable or better than those of traditional injection molded magnets. The starting polymer magnet composite pellets consist of 65 vol% isotropic NdFeB powder and 35 vol% polyamide (Nylon-12). The density of the final BAAM magnet product reached 4.8 g/cm 3, and the room temperature magnetic properties are: Intrinsic coercivity Hci = 8.65 kOe, Remanence Br = 5.07 kG, and energy product (BH) max = 5.47 MGOe (43.50 kJ/m 3). This study provides a new pathway for preparing near-net shape bonded magnets for various magnetic applications.« less

Magnetic properties of the surface layer and its magnetic interaction with the interior of Nd-Fe-B sintered magnets

NASA Astrophysics Data System (ADS)

Kobayashi, Kurima; Nakamura, Michi-hide; Urushibata, Kimiko

2015-05-01

The magnetization and demagnetization mechanisms in the mechanically polished surface layers (SL) of the c-plane and a-b plane of Nd-Fe-B sintered magnets were investigated. The magnetic interaction between the SL and the interior of the magnet was clarified by using vibrating sample magnetometer measurements of a whole sample and magneto-force microscopy observations of the domain structure of the SL layer. The polishing eliminated the Nd-rich grain boundary phases, which was only about 2 nm thick, from the SL crystal grains in the sintered magnets. The a-b plane polishing caused the independent magnetic reversal of the a-b plane SL, which was about 5.5 μm thick, as in the platy samples. The coercivities (μ0Hc) of the SL were less than 0.3 T. In contrast, the c-plane polishing did not produce independent magnetic reversal of the SL, although the coercivity of bulk samples was clearly decreased by the formation of the c-plane SL. The grains in the SL should form clusters that alter the demagnetizing factors, depending on the shape of cluster as a magnetic unit. The magnetic interaction among the SL crystal grains is expected to play an important role in the coercivity mechanism of Nd-Fe-B sintered magnets.

Influence of annealing temperature on the Dy diffusion process in NdFeB magnets

NASA Astrophysics Data System (ADS)

Hu, Sheng-qing; Peng, Kun; Chen, Hong

2017-03-01

Sintered NdFeB magnets were coated with a layer of Dy metal using electron beam evaporation method and then annealed at various temperatures to investigate the temperature dependence of Dy diffusion process in NdFeB magnets. A Dy-rich phase was observed along the grain boundaries after the grain boundary diffusion process, the diffusion coefficients of various temperatures were obtained, the diffusion coefficients of Dy along the grain boundaries at 800 °C and 900 °C were determined to be 9.8×10-8 cm2 s-1 and 2.4×10-7 cm2 s-1, respectively. The diffusion length depended on the annealing temperature and the maximum diffusion length of approximately 1.8 mm and 3.0 mm can be obtained after annealing at 800 °C and 900 °C for 8 h. Higher diffusion temperature results in the diffusion not only along the grain boundaries but also into grains and then decrease in magnetic properties. The optimum annealing conditions can be determined as 900 °C for 8 h. The coercivity was improved from 1040 kA/m to 1450 kA/m and its magnetization has no significant reduction after the grain boundary diffusion process at the optimum annealing conditions.

Magnetic Force Microscopy Investigation of Magnetic Domains in Nd2Fe14B

NASA Astrophysics Data System (ADS)

Talari, Mahesh Kumar; Markandeyulu, G.; Rao, K. Prasad

2010-07-01

Remenance and coercivity in Nd2Fe14B materials are strongly dependent on the microstructural aspects like phases morphology and grain size. The coercivity (Hc) of a magnetic material varies inversely with the grain size (D) and there is a critical size below which Hc∝D6. Domain wall pinning by grain boundaries and foreign phases is the important mechanism in explaining the improvement in coercivity and remenance. Nd2Fe14B intermetallic compound with stochiometric composition was prepared from pure elements (Nd -99.5%, Fe—99.95%, B -99.99%) by arc melting in argon atmosphere. Magnetic Force Microscope (MFM) gives high-resolution magnetic domain structural information of ferromagnetic samples. DI-3100 Scanning Probe Microscope with MESP probes was used For MFM characterization of the samples. Magnetic domains observed in cast ingots were very long (up to 40 μm were observed) and approximately 1-5 μm wide due to high anisotropy of the compounds. Magnetic domains have displayed different image contrast and morphologies at different locations of the samples. The domain morphologies and image contrast obtained in this analysis were explained in this paper.

Feasibility of low-cost magnetic rail designs by integrating ferrite magnets and NdFeB magnets for HTS Maglev systems

NASA Astrophysics Data System (ADS)

Sun, R. X.; Deng, Z. G.; Gou, Y. F.; Li, Y. J.; Zheng, J.; Wang, S. Y.; Wang, J. S.

2015-09-01

Permanent magnet guideway (PMG) is an indispensable part of high temperature superconducting (HTS) Maglev systems. Present PMGs are made of NdFeB magnets with excellent performance and cost much. As another permanent magnet material, the ferrite magnet is weak at magnetic energy product and coercive force, but inexpensive. So, it is a possible way to integrate the ferrite and NdFeB magnets for cutting down the cost of present PMGs. In the paper, the equivalent on magnetic field intensity between ferrite magnets and NdFeB magnets was evaluated by finite element simulation. According to the calculation results, the magnetic field of the PMG integrating ferrite magnets and NdFeB magnets can be increased remarkably comparing with the pure ferrite PMG. It indicates that low-cost PMG designs by integrating the two permanent magnet materials are feasible for the practical HTS Maglev system.

Effects of B and Mo on the magnetic properties of NdFeTi-nitrides with ThMn[sub 12]-type structure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Y.B.; Kim, H.T.; Kim, C.S.

1993-11-01

The alloys having nearly single phase of ThMn[sub 12]-type structure (1-12 phase) have been successfully synthesized in NdFe[sub 10.7]Ti[sub 1.3[minus]y]M[sub y] (M = B/Mo) alloy systems by substituting B or Mo up to 23% of Ti (y=0.3). After nitrification, the unit cell volume of 1--12 phase has increased by about 2--3% and a-Fe phase of 5--15 wt.% has been formed depending on the substitutional elements. The nitrides, NdFe[sub 10.7]TiB[sub 0.3]N[sub x] and Nd Fe[sub 10.7]TiMo[sub 0.3]N[sub x], were confirmed to have uniaxial anisotropy by X-ray diffractometry. The results of magnetic measurements for the nitrides have shown that B is verymore » effective for the increase of both Curie temperature and magnetization. On the other band, Mo is effective for the increase of anisotropy field, but it decreases the magnetization. The Curie temperature and magnetization of NdFe[sub 10.7]TiB[sub 0.3]N[sub x] are 560 C and 148 Am[sup 2] /kg, respectively, by about 20% and 15% higher than those of NdFe[sub 10.7]Ti[sub 1.3]N[sub x]. The anisotropy field of NdFe[sub 10.7]TiMo[sub 0.3]N[sub x] is about 7960 kA/m (100 kOe) which is about 25% higher than that of NdFe[sub 10.7]Ti[sub 1.3]N[sub x].« less

Magnetic properties and magnetocrystalline anisotropy of Nd 2Fe 17, Nd 2Fe 17X 3, and related compounds

DOE PAGES

Pandey, Tribhuwan; Parker, David S.

2018-02-26

The electronic and magnetic properties of Nd 2Fe 17 and Nd 2Fe 17X 3 (X = C or N) compounds have been calculated using the first-principles density functional calculations. Among these, the nitrogen and carbon interstitial compounds exhibit all of the required properties such as a saturation moment of 1.6 T, Curie temperature of 700–750 K, however easy magnetic axis lies in the planar direction making them less attractive for permanent magnet applications. The calculated magnetocrystalline anisotropy energy is found to be -2.7 MJ/m 3 for Nd 2Fe 17C 3 and -4.7 MJ/m 3 for Nd 2Fe 17N 3. Finally,more » we further explored the possibility of changing the easy axis direction through La/Ce alloying at Nd site. Although the MAE is found to be smaller in magnitude for all the La/Ce alloys it still maintains planar direction.« less

Abnormal variation of magnetic properties with Ce content in (PrNdCe)2Fe14B sintered magnets prepared by dual alloy method

NASA Astrophysics Data System (ADS)

Xue-Feng, Zhang; Jian-Ting, Lan; Zhu-Bai, Li; Yan-Li, Liu; Le-Le, Zhang; Yong-Feng, Li; Qian, Zhao

2016-05-01

Resource-saving (PrNdCe)2Fe14B sintered magnets with nominal composition (PrNd)15-x Ce x Fe77B8 (x = 0-10) were prepared using a dual alloy method by mixing (PrNd)5Ce10Fe77B8 with (PrNd)15Fe77B8 powders. For Ce atomic percent of 1% and 2%, coercivity decreases dramatically. With further increase of Ce atomic percent, the coercivity increases, peaks at 6.38 kOe in (PrNd)11Ce4Fe77B8, and then declines gradually. The abnormal dependence of coercivity is likely related to the inhomogeneity of rare earth chemical composition in the intergranular phase, where PrNd concentration is strongly dependent on the additive amount of (PrNd)5Ce10Fe77B8 powders. In addition, for Ce atomic percent of 8%, 7%, and 6% the coercivity is higher than that of magnets prepared by the conventional method, which shows the advantage of the dual alloy method in preparing high abundant rare earth magnets. Project supported by the National Natural Science Foundation of China (Grant Nos. 51461033, 51571126, 51541105, and 11547032), the Natural Science Foundation of Inner Mongolia, China (Grant No. 2013MS0110), and the Inner Mongolia University of Science and Technology Innovation Fund, China.

Effect of washing process on the magnetic properties of Nd-Fe-B nanoparticles prepared by reduction-diffusion method

NASA Astrophysics Data System (ADS)

Wang, Y.; Ahn, J.; Kim, D.; Ren, W. J.; Liu, W.; Zhang, Z. D.; Choi, C. J.

2017-10-01

Nd-Fe-B nanoparticles with a particle size below 50 nm and excellent magnetic properties were obtained via a novel route which makes use of both spray drying and reduction-diffusion processes. Uniform Nd-Fe-B particles were formed by the optimization of Ca amount as a reducing agent and additional washing by milling in ethanol media. Especially, we implemented a two-step washing process which contributed to the excellent magnetic properties with high remanence and coercivity. After the removal of CaO by novel washing process, the maximum energy product (BH)max of the particles showed 22.1 MGOe. This value is superior to those reported in reduction-diffusion process. We used Henkel plot to assume the mechanism of magnetic interactions of the Nd-Fe-B nanoparticles.

Thermodynamic Studies on NdFeO 3(s)

NASA Astrophysics Data System (ADS)

Parida, S. C.; Dash, Smruti; Singh, Ziley; Prasad, R.; Jacob, K. T.; Venugopal, V.

2002-02-01

The enthalpy increments and the standard molar Gibbs energy of formation of NdFeO3(s) have been measured using a high-temperature Calvet microcalorimeter and a solid oxide galvanic cell, respectively. A λ-type transition, related to magnetic order-disorder transformation (antiferromagnetic to paramagnetic), is apparent from the heat capacity data at ∼687 K. Enthalpy increments, except in the vicinity of transition, can be represented by a polynomial expression: {H°m(T)-H°m(298.15 K)}/J·mol-1 (±0.7%)=-53625.6+146.0(T/K) +1.150×10-4(T/K)2 +3.007×106(T/K)-1; (298.15≤T/K ≤1000). The heat capacity, the first differential of {H°m(T)-H°m(298.15 K)} with respect to temperature, is given by Cop, m/J·K-1·mol-1=146.0+2.30×10-4(T/K)-3.007×106(T/K)-2. The reversible emf's of the cell, (-) Pt/{NdFeO3(s) +Nd2O3(s)+Fe(s)}//YDT/CSZ//{Fe(s)'FeO'(s)}/Pt(+), were measured in the temperature range from 1004 to 1208 K. It can be represented within experimental error by a linear equation: E/V:(0.1418±0.0003)-(3.890±0.023)×10-5(T/K). The Gibbs energy of formation of solid NdFeO3 calculated by the least-squares regression analysis of the data obtained in the present study, and data for Fe0.95O and Nd2O3 from the literature, is given by ΔfG°m(NdFeO3, s)/kJ·mol-1(±2.0)=-1345.9+0.2542(T/K); (1000≤T/K ≤1650). The error in ΔfG°m(NdFeO3, s, T) includes the standard deviation in emf and the uncertainty in the data taken from the literature. Values of ΔfH°m(NdFeO3, s, 298.15 K) and S°m(NdFeO3, s, 298.15 K) calculated by the second law method are -1362.5 (±6) kJ·mol-1 and 123.9 (±2.5) J·K-1·mol-1, respectively. Based on the thermodynamic information, an oxygen potential diagram for the system Nd-Fe-O was developed at 1350 K.

Deduction of the chemical state and the electronic structure of Nd{sub 2}Fe{sub 14}B compound from X-ray photoelectron spectroscopy core-level and valence-band spectra

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Jing; Liang, Le; Zhang, Lanting, E-mail: lantingzh@sjtu.edu.cn, E-mail: lmsun@sjtu.edu.cn

2014-10-28

Characterization of chemical state and electronic structure of the technologically important Nd{sub 2}Fe{sub 14}B compound is attractive for understanding the physical nature of its excellent magnetic properties. X-ray photoelectron spectroscopy (XPS) study of such rare-earth compound is important and also challenging due to the easy oxidation of surface and small photoelectron cross-sections of rare-earth 4f electrons and B 2p electrons, etc. Here, we reported an investigation based on XPS spectra of Nd{sub 2}Fe{sub 14}B compound as a function of Ar ion sputtering time. The chemical state of Fe and that of B in Nd{sub 2}Fe{sub 14}B compound can be clearlymore » determined to be 0 and −3, respectively. The Nd in Nd{sub 2}Fe{sub 14}B compound is found to have the chemical state of close to +3 instead of +3 as compared with the Nd in Nd{sub 2}O{sub 3}. In addition, by comparing the valence-band spectrum of Nd{sub 2}Fe{sub 14}B compound to that of the pure Fe, the contributions from Nd, Fe, and B to the valence-band structure of Nd{sub 2}Fe{sub 14}B compound is made more clear. The B 2p states and B 2s states are identified to be at ∼11.2 eV and ∼24.6 eV, respectively, which is reported for the first time. The contribution from Nd 4f states can be identified both in XPS core-level spectrum and XPS valence-band spectrum. Although Nd 4f states partially hybridize with Fe 3d states, Nd 4f states are mainly localized in Nd{sub 2}Fe{sub 14}B compound.« less

Corrosion and protection of NdFeB type magnets

NASA Astrophysics Data System (ADS)

Cavalloti, P.; Bozzini, B.; Cecchini, R.; Bava, G. F.; Davies, H. A.; Hoggarth, C.

1992-02-01

A general mechanism for the corrosion behaviour of NdFeB magnets is presented, related to the magnet heterogeneity with the presence of different phases. Cathodic control is outlined. An electrochemical method to assess the corrosion resistance of magnets, with and without coatings, is proposed; it is based on the study of the transient voltage at the magnet surface after a second cathodic current pulse in a suitable aggressive solution and its dependence on the amount of cathodic current circulating. Suitable pretreatments have been tried and interesting results obtained with passivation pretreatments, giving phosphorous Nd at grain boundaries. Coatings if sintered and plastic magnets have been tried using several methods. Good results are obtained with Zn-Co layers on sintered magnets and a sol-gel glass on powders for plastic magnets. Improved ACS (Autocatalytic Chemical Deposition) Ni=P coatings have been realized, with an alkaline brass flash plating to start ACD deposition.

Permanent magnetic properties of NdFe12Nx sputtered films epitaxially grown on V buffer layer

NASA Astrophysics Data System (ADS)

Sato, T.; Ohsuna, T.; Yano, M.; Kato, A.; Kaneko, Y.

2017-08-01

To clarify the magnetic properties of the NdFe12Nx compound, which shows promise as a high-performance permanent magnet material, NdFe12Nx epitaxial films fabricated by using a V underlayer on MgO (100) single-crystalline substrates were investigated. Nd-Fe films deposited on a V underlayer consist of NdFe12 grains, which have a c-axis orientation perpendicular to the film plane, as well as α-Fe and Nd2Fe17 phases. In the Nd-Fe-N film obtained by subsequent nitridation of the Nd-Fe film, NdFe12Nx grains grew as the dominant phase, and the volume fractions of α-Fe phases dropped below 5%. A Nd-Fe-N film with a thickness of 50 nm exhibits a saturation magnetization (Ms) of 1.7 T, an anisotropy field (HA) of ˜60 kOe, a magnetocrystalline anisotropy energy (K1) of ˜4.1 MJ/m3, and a coercivity (Hc) of 1.7 kOe. The Hc of a Nd-Fe-N film with a thickness of 25 nm is 4.3 kOe. These results indicate that NdFe12Nx compounds have a superior Ms compared to Nd-Fe-B magnets, while the enhancement in Hc is indispensable.

Coercivity enhancement mechanism in Dy-substituted Nd-Fe-B nanoparticles synthesized by sol-gel base method followed by a reduction-diffusion process

NASA Astrophysics Data System (ADS)

Rahimi, Hamed; Ghasemi, Ali; Mozaffarinia, Reza; Tavoosi, Majid

2017-05-01

In current work, Nd15-xDyxFe77.5B7.5 (at%) nanoparticles with different Dy-content (x=0.0, 0.5, 1.0, 1.5, 2.0, 2.5, 3.0) were synthesized by sol-gel method followed by a reduction-diffusion process. The effects of Dy on the magnetic properties and the relations between the microstructure and the coercivity of Dy-substituted Nd-Fe-B nanoparticles have been studied. The coercivity of Nd-Fe-B nanoparticles with the addition of Dy first increase, reaches a maximum, and then starts to decrease. The coercivity of Dy-substituted Nd-Fe-B nanoparticle synthesized by sol-gel method increased from 938.9 to 1663.9 kA/m while the remanence decreased slightly from 1.16 to 1.06 T. The results show that with an increase in Dy content the variation of maximum energy product ((BH)max), lowest-order uniaxial magnetocrystalline anisotropy constant (Ku1), and Curie temperature (Tc) had a trend as same as the coercivity. The Henkel plot showed that the existence of exchange coupling interaction between grains, and the exchange coupling interactions increased with increasing x from 0.0 to 2.0 and then decrease with further increasing x≥2.5. The optimum magnetic properties of Nd-Fe-B nanoparticles with (BH)max =40.38 MGOe, Hc=1663.9 kA/m, Br=1.08 T were obtained by substituted 2.0 at% Dy. The effects of increasing temperature on magnetic properties of Dy-substituted Nd-Fe-B nanoparticle magnets with 2.0 at% Dy was investigated. The reduced spin-reorientation temperature was obtained for Dy-substituted Nd-Fe-B nanoparticles with 2.0 at% Dy. Below 100 K a spin-reorientation transition was takes place. The temperature coefficient of coercivity (β) was -0.36, -0.46, -0.41, -0.34, -0.29, -0.24, -0.25%/°C at different temperature 50, 100, 150, 200, 250, 300, 350 °C, respectively. Mössbauer spectroscopy was applied to study the composition and properties of Dy-substituted Nd-Fe-B magnet. Microstructure analysis showed a homogeneous distribution of Dy in produced samples. The possible

Magnetic and structural properties of rapidly quenched Nd-Fe-Co-Ge-B alloys

NASA Astrophysics Data System (ADS)

Beitollahi, A.; Gholamipour, R.; Marghusian, V. K.; Andreev, S. V.; Bogatkin, A. N.; Duragin, S. S.; Kozlov, A. N.; Kudrevatykh, N. V.; Bogdanov, S. G.; Pirogov, A. N.

2006-12-01

We have studied the structure and magnetic properties of some rapidly quenched and subsequently annealed alloys prepared by centrifugal method with a composition (in wt %) Nd(29.5), Co(6), B(1.1), Ge (x), Fe(balance) with x=0.0, 0.2, 0.4, 0.6, 0.8, 1.0 (wt %) for Ge. Based on X-ray diffraction (XRD), elastic neutron diffraction, and small-angle neutron scattering (SANS), the formation of partially crystallized main hard magnetic 2:14:1 (Φ) phase in the amorphous matrix was detected for all as-spun samples. The size of the clusters formed for the sample with 1 wt % Ge determined based on SANS profiles was about 10 nm. It was shown that the addition of Ge shifts the maximum crystallization peak of the main 2:14:1 phase to higher temperatures. The variation of the magnitudes of different magnetic parameters such as i H c and M s versus Ge concentration for as-spun samples can be possibly related to the different rate of crystallization of the 2:14:1 phase formed. Further, for the samples doped with 0.8 and 1.0 wt % Ge and annealed at 760°C for 5 min the formation of some extra phases such as Nd5Ge3, NdFe2, NdB4, as well as α-Fe was detected by XRD. The magnetic measurements carried out using a vibrating-sample magnetometer (VSM) for these samples also supported the XRD data obtained. While the highest values of coercivity i H c = 772 kA/m were obtained for the annealed samples without Ge, the highest value of σr = 69 emu/g was also obtained for the samples substituted with 0.8 wt % Ge without an appreciable reduction in i H c.

A novel method combining additive manufacturing and alloy infiltration for NdFeB bonded magnet fabrication

DOE PAGES

Li, Ling; Tirado, Angelica; Conner, Benjamin S.; ...

2017-04-27

In this paper, binder jetting additive manufacturing technique is employed to fabricate NdFeB isotropic bonded magnets, followed by an infiltration process with low-melting point eutectic alloys [i.e., Nd 3Cu 0.25Co 0.75 (NdCuCo) and Pr 3Cu 0.25Co 0.75 (PrCuCo)]. Densification and mechanical strength improvement are achieved for the as-printed porous part. Meanwhile, the intrinsic coercivity H ci is enhanced from 732 to 1345 kA/m and 1233 kA/m after diffusion of NdCuCo and PrCuCo, respectively. This study presents a novel method for fabricating complex-shaped bonded magnets with promising mechanical and magnetic properties.

A novel method combining additive manufacturing and alloy infiltration for NdFeB bonded magnet fabrication

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Ling; Tirado, Angelica; Conner, Benjamin S.

In this paper, binder jetting additive manufacturing technique is employed to fabricate NdFeB isotropic bonded magnets, followed by an infiltration process with low-melting point eutectic alloys [i.e., Nd 3Cu 0.25Co 0.75 (NdCuCo) and Pr 3Cu 0.25Co 0.75 (PrCuCo)]. Densification and mechanical strength improvement are achieved for the as-printed porous part. Meanwhile, the intrinsic coercivity H ci is enhanced from 732 to 1345 kA/m and 1233 kA/m after diffusion of NdCuCo and PrCuCo, respectively. This study presents a novel method for fabricating complex-shaped bonded magnets with promising mechanical and magnetic properties.

New magnetic rails with double-layer Halbach structure by employing NdFeB and ferrite magnets for HTS maglev

NASA Astrophysics Data System (ADS)

Sun, Ruixue; Zheng, Jun; Zheng, Botian; Qian, Nan; Li, Jipeng; Deng, Zigang

2018-01-01

In the high temperature superconducting (HTS) maglev system, the magnetic rail as an essential infrastructure is needed all along the route to carry passengers and goods to the destinations. Thus, large amount of rare earth magnetic materials are required in the magnetic rail construction. In order to decrease the dependence of magnetic rails on rare earth elements, the ferrite magnet is employed to replace part of the NdFeB magnets containing rare earth elements. Consequently, a new type rail with double-layer Halbach structure is presented, which is consisted of NdFeB and ferrite magnets. In this paper, we designed and fabricated the proposed rail, and further measured its magnetic flux density distribution and electromagnetic force interacting with HTS bulks. Experimental results indicate that, this new type rail, in double-layer Halbach structure, can achieve an equivalent distribution of magnetic flux density and levitation performance as the pure NdFeB Halbach rail, while a 10% reduction in NdFeB magnet consumption can be realized at the same time. In addition this work explores another magnetic material selection for HTS maglev applications. The dependence on rare earth element and the cost of magnetic rails can be further reduced, as the coercive force of ferrite magnets improved.

Nd2Fe14C-based magnet with better permanent magnetic properties prepared by a simple mechanochemical method

NASA Astrophysics Data System (ADS)

Geng, Hongmin; Ji, Yuan; Zhang, Jingjing; Gao, Yuchao; Yan, Yu; Wang, Wenquan; Su, Feng; Du, Xiaobo

2017-11-01

Nd2Fe14C-based magnet is prepared by a mechanochemical method, namely high-energy ball-milling Nd2Fe11Bx (x = 0-0.15) alloy in heptane (C7H16), followed by annealing to 850 °C in vacuum. Under the action of high-energy ball-milling, Nd2Fe11Bx react with heptane to form NdH2+δ, Fe-(CB), C, etc. H2 is released and Nd2Fe17, Nd2Fe17Cx (x = 0-3), Nd2Fe14C, Nd carbides and α-Fe are formed in the subsequent annealing. C amount depends on ball-milling time t. Long time ball milling or high C content suppresses the formation of 2:17 phase and favors the formation of 2:14:1 phase in the final products. Excessive ball-milling results in the quick increase of α-Fe. The maximum of magnetically hard Nd2Fe14C is obtained at t = 4 h. For Nd2Fe11 samples, there exists considerable quantity of Nd carbides and α-Fe phase appears earlier and increases rapidly with extending the ball-milling time t. The addition of B element shortens the ball-milling time of the formation of maximum Nd2Fe14C and prominently suppresses the formation of Nd carbide and α-Fe. The optimum magnetic properties, coercivity iHc of 1193.7 kA/m, remanence Mr of 580.9 kA/m, maximum magnetic energy product (BH)max of 91.7 kJ/m3 is approaching to its theoretic value of 99.2 kJ/m3 for isotropic Nd2Fe14C magnet, are obtained in Nd2Fe11B0.06 alloy ball milled for 3.5 h.

Hydrogen absorption and its effect on magnetic properties of Nd2Fe14B

NASA Astrophysics Data System (ADS)

Bezdushnyi, R.; Damianova, R.; Tereshina, I. S.; Pankratov, N. Yu.; Nikitin, S. A.

2018-05-01

Magnetic properties of hydrides of the intermetallic compound Nd2Fe14BHx are investigated in the temperature range covering the Curie temperatures (TC) of the compounds (up to 670 K). The temperature dependencies of magnetization are measured under continuous control of hydrogen content in the investigated samples. The dependencies of Curie and spin-reorientation transition (TSR) temperatures on the hydrogen concentration are studied in detail. The dependence of hydrogen concentration on pressure at a constant temperature (near TC) and on the temperature at various pressures are obtained. We attempted to estimate the contributions of the unit cell volume increase upon hydrogenation and the electronic structure change in the variation of TC of the hydrogenated Nd2Fe14 B .

Effect of grain alignment distribution on magnetic properties in (MM, Nd)-Fe-B sintered magnets

NASA Astrophysics Data System (ADS)

Yu, Xiaoqiang; Yue, Ming; Zhu, Minggang; Liu, Weiqiang; Li, Yuqing; Xi, Longlong; Li, Jiajie; Zhang, Jiuxing; Li, Wei

2018-03-01

H cj of (MM x Nd1-x )-Fe-B sintered magnets decreases distinctly with x increasing when misch metal (MM) content (x) ranges from 0.3 to 1. Practical application is taken into consideration so that the (MM0.6Nd0.4)-Fe-B components are chosen to analyze the changes in behavior of the magnetic properties. Both Magnet II and Magnet III belong to (MM0.6Nd0.4)-Fe-B sintered magnets, however, it should be noted that Magnet II is prepared by the single alloying method (SAM) and Magnet III is prepared by the double main phase alloy method (DMPAM). Core-shell structures of the magnets prepared by DMPAM can result in the higher H cj and lower knee-point coercivity (H k) compared with that by SAM. Furthermore, for Magnet II, the abnormal grain growth contributes to a better grain alignment and smaller distribution coefficient (σ) defined as the degree of grain alignment, which will enforce a higher tendency of the H cj decreasing and H k increasing. The expression of their normalized coercivity h(σ) is deduced by combining Gao’s starting field model with Kronmüller’s nucleation mechanism. Based on the overall h(σ) ~ σ curve, the best desirable h(σ) value is calculated when σ  =  0.09. Theoretically, for Magnet III, the resultant larger σ should be attributed to the more uniform grain alignment. In addition, the deviations of grain size distributions on the c-plane become more remarkable with more MM concentrates, which can be presented by SEM images. Meanwhile, by means of the pole figures, it is also verified that the grain alignment distribution becomes much more diverse with x increasing. Therefore, it can be predicted whether the grain alignment distribution is significant for H k and H cj of (MM x Nd1-x )-Fe-B sintered magnets (x  ≠  0.6) prepared by SAM/DMPAM or not.

The effect of Nb additions on the thermal stability of melt-spun Nd2Fe14B

NASA Astrophysics Data System (ADS)

Lewis, L. H.; Gallagher, K.; Panchanathan, V.

1999-04-01

Elevated-temperature superconducting quantum interference device (SQUID) magnetometry was performed on two samples of melt-spun and optimally annealed Nd2Fe14B; one sample contained 2.3 wt % Nb and one was Nb-free. Continuous full hysteresis loops were measured with a SQUID magnetometer at T=630 K, above the Curie temperature of the 2-14-1 phase, as a function of field (1 T⩽H⩽-1 T) and time on powdered samples sealed in quartz tubes at a vacuum of 10-6 Torr. The measured hysteresis signals were deconstructed into a high-field linear paramagnetic portion and a low-field ferromagnetic signal of unclear origin. While the saturation magnetization of the ferromagnetic signal from both samples grows with time, the signal from the Nb-containing sample is always smaller. The coercivity data are consistent with a constant impurity particle size in the Nb-containing sample and an increasing impurity particle size in the Nb-free sample. The paramagnetic susceptibility signal from the Nd2Fe14B-type phase in the Nb-free sample increases with time, while that from the Nb-containing sample remains constant. It is suggested that the presence of Nb actively suppresses the thermally induced formation of poorly crystallized Fe-rich regions that apparently exist in samples of both compositions.

Liquid coated melt-spun Nd-Fe-B powders for bonded magnets

NASA Astrophysics Data System (ADS)

Li, D.; Gaiffi, S.; Kirk, D.; Young, K.; Herchenroeder, J.; Berwald, T.

1999-04-01

The liquid coating (LC) has been employed to apply epoxy and lubricant over the surface of rapidly solidified Nd-Fe-B powder particles. The LC led to an improvement of physical and magnetic properties for the powders and magnets compared to the dry blending and the encapsulation methods. The LC powders have excellent flowability and can be used for bonded magnets requiring very close tolerances; further bonded magnets made using this powder posses higher strength.

The corrosion mechanism of the sintered (Ce, Nd)-Fe-B magnets prepared by double main phase and single main phase approaches

NASA Astrophysics Data System (ADS)

Shi, Xiaoning; Zhu, Minggang; Zhou, Dong; Song, Liwei; Guo, Zhaohui; Li, Jia; Li, Wei

2018-05-01

The sintered (Ce, Nd)-Fe-B magnets were produced widely by Double Main Phase (DMP) method in China as the magnetic properties of the DMP magnets are superior to those of single main phase (SMP) magnets with the same nominal composition. In this work, the microstructure and corrosion mechanism of the sintered (Ce0.2Nd0.8)30FebalB (wt.%) magnets prepared by DMP and SMP method were studied in detail. Compared to SMP magnets, the DMP magnets have more positive corrosion potential, lower corrosion current density, larger electron transfer resistance, and lower mass loss of the free corrosion experiment in 0.5mol/l Na2SO4 aqueous solution. All of the results show that the DMP magnets have better corrosion resistance than SMP magnets. The back scattered electron images show that the crystalline grains of the DMP magnets are sphericity with a smooth surface while the SMP ones have plenty of edges and corners. Besides, the distribution of Ce/Nd is much more uneven in both magnetic phase and rare earth (Re)-rich phase of the DMP magnets than those of SMP magnets. After corrosion, DMP magnets show eroded magnetic phase and intact Re-rich phase, which indicate that galvanic corrosion of the Re-rich phase acting as the cathode appears.

Influence of Nb addition on vacancy defects and magnetic properties of the nanocrystalline Nd-Fe-B permanent magnets

NASA Astrophysics Data System (ADS)

Szwaja, Małgorzata; Gębara, Piotr; Filipecki, Jacek; Pawlik, Katarzyna; Przybył, Anna; Pawlik, Piotr; Wysłocki, Jerzy J.; Filipecka, Katarzyna

2015-05-01

In present work, influence of Nb addition on vacancy defects and magnetic properties of nanocrystalline Nd-Fe-B permanent magnets, was investigated. Samples with composition (Nd,Fe,B)100-xNbx (where x=6,7,8) were studied in as-cast state and after annealing. Samples were prepared by arc-melting with high purity of constituent elements under Ar atmosphere. Ribbons were obtained by melt-spinning technique under low pressure of Ar. Ribbon samples in as-cast state had amorphous structure and soft magnetic properties. Positron annihilation lifetime spectroscopy PALS has been applied to detection of positron - trapping voids (vacancy defects). With increase of Nb in alloy increasing of vacancy defects concentration was observed. Heat treatment of the samples was carried out at various temperatures (from 923 K to 1023 K) for 5 min, in order to obtain nanocrystalline structure. The aim of present work was to determine the influence of Nb addition and annealing conditions on the vacancy defects and magnetic properties of the Nd-Fe-B- type alloys in as-cast state and after heat treatment.

Electrodeposition of amorphous Ni P coatings onto Nd Fe B permanent magnet substrates

NASA Astrophysics Data System (ADS)

Ma, C. B.; Cao, F. H.; Zhang, Z.; Zhang, J. Q.

2006-12-01

Decorative and protective Ni-P amorphous coatings were electroplated onto NdFeB permanent magnet from an ortho-phosphorous acid contained bath. The influences of the main electroplating technological parameters including current density, bath pH, bath temperature and H3PO3 on the structure and chemical composition of Ni-P coatings were investigated by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) techniques in conjunction with X-ray diffraction (XRD), scanning transmission electron microscopy (SEM) and X-ray energy-dispersive spectrometry (EDX). The optimized amorphous Ni-P coated NdFeB can stand for ca. 180 h against neutral 3.0 wt.% NaCl salt spray without any pitting corrosion. Meanwhile, the results also showed that large phosphorous content is the precondition for Ni-P coatings to possess the amorphous structure, but too much high phosphorous content can damage the amorphous structure due to the separation of superfluous P from Ni2P/Ni3P and the resultant formation of multi-phase coatings (such as Ni2P-P).

Electromagnetic and Microwave-Absorbing Properties of Plate-Like Nd-Ce-Fe Powder

NASA Astrophysics Data System (ADS)

Qiao, Ziqiang; Pan, Shunkang; Xiong, Jilei; Cheng, Lichun; Lin, Peihao; Luo, Jialiang

2017-01-01

Plate-like Ce x Nd2- x Fe17 ( x = 0.0, 0.1, 0.2, 0.3, 0.4) powders have been synthesized by an arc melting and high-energy ball milling method. The structure of the Nd-Ce-Fe powders was investigated by x-ray diffraction analysis. Their morphology and particle size distribution were evaluated by scanning electron microscopy and laser particle analysis. The saturation magnetization and electromagnetic parameters of the powders were characterized using vibrating-sample magnetometry and vector network analysis, respectively. The results reveal that the Ce x Nd2- x Fe17 ( x = 0.0, 0.1, 0.2, 0.3, 0.4) powders consisted of Nd2Fe17 single phase with different Ce contents. The particle size and saturation magnetization decreased with increasing Ce content. The resonant frequencies of ɛ″ and μ″ moved towards lower frequency with increasing Ce concentration. The minimum reflection loss value decreased as the Ce content was increased. The minimum reflection loss and absorption peak frequency of Ce0.2Nd1.8Fe17 with coating thickness of 1.8 mm were -22.5 dB and 7 GHz, respectively. Increasing the values of the complex permittivity and permeability could result in materials with good microwave absorption properties.

Magnetic properties of bulk, and rapidly solidified nanostructured (Nd 1-xCe x) 2Fe 14-yCo yB ribbons

DOE PAGES

Pathak, Arjun K.; Khan, M.; Gschneidner, Jr., K. A.; ...

2015-11-06

Magnetic properties of Ce and Co co-doped (Nd 1-xCe x) 2Fe 14-yCo yB compounds have been investigated both in bulk polycrystalline and rapidly solidified nanostructured ribbon forms. For certain Ce concentrations the materials exhibit spin re-orientation transitions below 140 K. The Curie temperatures, saturation magnetizations, and other magnetic properties relevant for applications as permanent magnets are controlled by Ce and Co substitutions for Nd and Fe, respectively. Most importantly, the results show that Ce, Co co-doped compounds are excellent replacements for several Dy-based high performance permanent magnets (dysprosium is one of the critical elements and is, therefore, in short supply).more » As a result, the high temperature (>375 K) magnetic properties for Nd–Ce–Fe–Co–B based alloys show promise not only as a replacement for Dy-doped Nd 2Fe 14B permanent magnets, but the new alloys also require significantly lower amounts of Nd, which too is the critical element that can be replaced by a more abundant Ce.« less

Enhanced Magnetic Properties of Nd15Fe77B8 Alloy Powders Produced by Melt-Spinning Technique

NASA Astrophysics Data System (ADS)

Öztürk, Sultan; İcin, Kürşat; Öztürk, Bülent; Topal, Uğur; Odabaşı, Hülya Kaftelen; Göbülük, Metin; Cora, Ömer Necati

2017-10-01

Rapidly solidified Nd15Fe77B8 alloy powders were produced by means of melt-spinning method in high-vacuum atmosphere to achieve improved magnetic and thermal properties. To this goal, a vacuum milling apparatus was designed and constructed to ball-mill the melt-spun powders in a surfactant active atmosphere. Various milling times were experimented to reveal the effect of the milling time on the mean particle size and other size-dependent properties such as magnetism and Curie temperature. Grain structure, cooling rate, and phase structure of the produced powders were also investigated. The Curie points shifted to higher temperatures from the ingot condition to surfactant active ball-milling and the values for Nd15Fe77B8 ingot alloy, melt-spun powders, and surfactant active ball-milled powders were 552 K, 595 K, and 604 K (279 °C, 322 °C, and 331 °C), respectively. It was noted that the surfactant active ball-milling process improved the magnetic and thermal properties of melt-spun Nd15Fe77B8 alloy powders. Compared to relevant literature, the coercivity of powders increased significantly with increasing milling time and decreasing in powder size. The coercivity value as high as 3427 kA m-1 was obtained.

Big area additive manufacturing of high performance bonded NdFeB magnets

DOE PAGES

Li, Ling; Tirado, Angelica; Nlebedim, I. C.; ...

2016-10-31

Additive manufacturing allows for the production of complex parts with minimum material waste, offering an effective technique for fabricating permanent magnets which frequently involve critical rare earth elements. In this report, we demonstrate a novel method - Big Area Additive Manufacturing (BAAM) - to fabricate isotropic near-net-shape NdFeB bonded magnets with magnetic and mechanical properties comparable or better than those of traditional injection molded magnets. The starting polymer magnet composite pellets consist of 65 vol% isotropic NdFeB powder and 35 vol% polyamide (Nylon-12). The density of the final BAAM magnet product reached 4.8 g/cm3, and the room temperature magnetic propertiesmore » are: intrinsic coercivity Hci = 688.4 kA/m, remanence B r = 0.51 T, and energy product (BH) max = 43.49 kJ/m 3 (5.47 MGOe). In addition, tensile tests performed on four dog-bone shaped specimens yielded an average ultimate tensile strength of 6.60 MPa and an average failure strain of 4.18%. Scanning electron microscopy images of the fracture surfaces indicate that the failure is primarily related to the debonding of the magnetic particles from the polymer binder. As a result, the present method significantly simplifies manufacturing of near-net-shape bonded magnets, enables efficient use of rare earth elements thus contributing towards enriching the supply of critical materials.« less

Big area additive manufacturing of high performance bonded NdFeB magnets

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Ling; Tirado, Angelica; Nlebedim, I. C.

Additive manufacturing allows for the production of complex parts with minimum material waste, offering an effective technique for fabricating permanent magnets which frequently involve critical rare earth elements. In this report, we demonstrate a novel method - Big Area Additive Manufacturing (BAAM) - to fabricate isotropic near-net-shape NdFeB bonded magnets with magnetic and mechanical properties comparable or better than those of traditional injection molded magnets. The starting polymer magnet composite pellets consist of 65 vol% isotropic NdFeB powder and 35 vol% polyamide (Nylon-12). The density of the final BAAM magnet product reached 4.8 g/cm3, and the room temperature magnetic propertiesmore » are: intrinsic coercivity Hci = 688.4 kA/m, remanence B r = 0.51 T, and energy product (BH) max = 43.49 kJ/m 3 (5.47 MGOe). In addition, tensile tests performed on four dog-bone shaped specimens yielded an average ultimate tensile strength of 6.60 MPa and an average failure strain of 4.18%. Scanning electron microscopy images of the fracture surfaces indicate that the failure is primarily related to the debonding of the magnetic particles from the polymer binder. As a result, the present method significantly simplifies manufacturing of near-net-shape bonded magnets, enables efficient use of rare earth elements thus contributing towards enriching the supply of critical materials.« less

The impact of processing parameters on the properties of Zn-bonded Nd-Fe-B magnets

NASA Astrophysics Data System (ADS)

Kelhar, Luka; Zavašnik, Janez; McGuiness, Paul; Kobe, Spomenka

2016-12-01

We report on the effect of loading factor and pressure on the density and the magnetic properties of Zn-bonded Nd-Fe-B magnets produced by pulsed-electric-current sintering (PECS). The idea behind this study is to fabricate bonded magnets with a metallic binder in order for the bonded magnet to operate at temperatures higher than 180 °C: the current upper-limit for polymer-bonded magnets. These composites are made of hard-magnetic powder in the form of melt-spun ribbons bonded with the low-melting-point metal Zn. The binder additions were varied from 10 to 30 wt%, and pressures of 50 and 500 MPa were applied. The high-pressure mode with 20 wt% Zn resulted in a 24% increase of Jr, compared to the low-pressure mode. The magnetic measurements revealed a maximum remanence of 0.64 T for 10 wt% Zn, while the coercivity is largely unaffected by the processing conditions. The density of the composites was up to 7.0 g/cm3, corresponding to 94% of the theoretical density. Compared to commercial polymer-bonded magnets, the Zn-bonded counterparts exhibit a slightly lower Jr, but the coercivity is retained. We show that there is a minor diffusion of Zn into the Nd-Fe-B, forming a 1 μm thin transition layer, but it does not harm the magnetic properties. These metal-bonded Nd-Fe-B magnets are ideal for use in high-temperature automotive applications like under-the-hood sensors and other magnet-based devices that are close to the engine.

First report on soapnut extract-mediated synthesis of sulphur-substituted nanoscale NdFeB permanent magnets and their characterization

NASA Astrophysics Data System (ADS)

Jayapala Rao, G. V. S.; Prasad, T. N. V. K. V.; Shameer, Syed; Arun, T.; Purnachandra Rao, M.

2017-10-01

Biosynthesis of nanoscale materials has its own advantages over other physical and chemical methods. Using soapnut extract as reducing and stabilizing agent for the synthesis of inorganic nanoscale materials is novel and has not been exploited to its potential so far. Herein, we report for the first time on the effects of sulphur substitution on soapnut extract-mediated synthesis of nanoscale NdFeB (S-NdFeB) permanent magnetic powders (Nd 15%, Fe 77.5%, B 7.5% and S with molar ratios: 0.1, 0.2, 0.3, 0.4, and 0.5). To synthesize, a 10 ml of 10% soapnut extract was added to 90 ml of respective chemical composition and heated to 60 °C for 30 min and aged for 24 h. The dried powder was sintered at 500 °C for 1 h. The characterization of the as-prepared nanoscale S-NdFeB magnetic materials was done using the techniques such as X-ray diffraction (XRD), scanning electron microscopy (SEM) with energy dispersion spectroscopy (EDS), Fourier transform infrared spectroscopy (FT-IR), dynamic light scattering (DLS for size and zeta potential measurements) and vibrating sample magnetometer (VSM)-hysteresis loop studies. The results revealed that particles were highly stable (with a negative zeta potential of 25.7 mV) with irregular and spherical shape (with measured hydrodynamic diameter 6.7 and 63.5 nm). The tetragonal structures of the formed powders were revealed by XRD micrographs. Hysteresis loop studies clearly indicate the effect of S concentration on the enhanced magnetization of the materials.

High electrical resistivity Nd-Fe-B die-upset magnet doped with eutectic DyF3-LiF salt mixture

NASA Astrophysics Data System (ADS)

Kim, K. M.; Kim, J. Y.; Kwon, H. W.; Kim, D. H.; Lee, J. G.; Yu, J. H.

2017-05-01

Nd-Fe-B-type die-upset magnet with high electrical resistivity was prepared by doping of eutectic DyF3-LiF salt mixture. Mixture of melt-spun Nd-Fe-B flakes (MQU-F: Nd13.6Fe73.6Co6.6Ga0.6B5.6) and eutectic binary (DyF3-LiF) salt (25 mol% DyF3 - 75 mol% LiF) was hot-pressed and then die-upset. By adding the eutectic salt mixture (> 4 wt%), electrical resistivity of the die-upset magnet was enhanced to over 400 μ Ω .cm compared to 190 μ Ω .cm of the un-doped magnet. Remarkable enhancement of the electrical resistivity was attributed to homogeneous and continuous coverage of the interface between flakes by the easily melted eutectic salt dielectric mixture. It was revealed that active substitution of the Nd atoms in neighboring flakes by the Dy atoms from the added (DyF3-LiF) salt mixture had occurred during such a quick thermal processing of hot-pressing and die-upsetting. This Dy substitution led to coercivity enhancement in the die-upset magnet doped with the eutectic (DyF3-LiF) salt mixture. Coercivity and remanence of the die-upset magnet doped with (DyF3-LiF) salt mixture was as good as those of the DyF3-doped magnet.

Heat capacity, resistivity, and angular dependent magnetization studies of single crystal Nd 1 + ϵ Fe 4 B 4 for ϵ ≈ 1 7

DOE Office of Scientific and Technical Information (OSTI.GOV)

Conner, Benjamin S.; Susner, Michael A.; UES Inc., Beavercreek, OH

Advances in crystal growth have allowed for synthesis of large single crystals of Nd 1+ϵFe 4B 4, a well-known phase with a modulated structure. As a result we are able to report heat capacity and resistivity measurements on a single crystal Nd 1+ϵFe 4B 4 sample with a distribution of ϵ that skews towards the solubility limit of Nd near ϵ ≈ 17. Heat capacity measurements show evidence of crystal field splitting at temperatures higher than the long-range ferromagnetic Curie temperature. Heat capacity, resistivity, and magnetization measurements all confirm a Curie temperature of 7 K which is lower than previouslymore » reported values in the Nd 1+ϵFe 4B 4 system. Here, we also perform measurements of the angular dependence of the magnetization and discover behavior associated with the magnetic anisotropy that is inconsistent with the simple description previously proposed.« less

Heat capacity, resistivity, and angular dependent magnetization studies of single crystal Nd 1 + ϵ Fe 4 B 4 for ϵ ≈ 1 7

DOE PAGES

Conner, Benjamin S.; Susner, Michael A.; UES Inc., Beavercreek, OH; ...

2017-04-04

Advances in crystal growth have allowed for synthesis of large single crystals of Nd 1+ϵFe 4B 4, a well-known phase with a modulated structure. As a result we are able to report heat capacity and resistivity measurements on a single crystal Nd 1+ϵFe 4B 4 sample with a distribution of ϵ that skews towards the solubility limit of Nd near ϵ ≈ 17. Heat capacity measurements show evidence of crystal field splitting at temperatures higher than the long-range ferromagnetic Curie temperature. Heat capacity, resistivity, and magnetization measurements all confirm a Curie temperature of 7 K which is lower than previouslymore » reported values in the Nd 1+ϵFe 4B 4 system. Here, we also perform measurements of the angular dependence of the magnetization and discover behavior associated with the magnetic anisotropy that is inconsistent with the simple description previously proposed.« less

Effects of Mg nanopowders intergranular addition on the magnetic properties and corrosion resistance of sintered Nd-Fe-B

NASA Astrophysics Data System (ADS)

Li, Zhi-jie; Wang, Xiao-er; Li, Jia-yang; Li, Jia; Wang, Hong-zhi

2017-11-01

In order to improve the magnetic properties and corrosion resistance of sintered Nd-Fe-B magnets, the (PrNd)29.9Dy0.1B1Co1Cu0.15Febal (wt%) powders were mixed with Mg nanopowders, as grain boundary modifiers. For Nd-Fe-B magnets with 0.1-0.4 wt% Mg addition, the result showed that addition amount of 0.1 wt% Mg, Hcj reaches the maximum value of 999.1 kA/m, Br reaches 1.436T, (BH)max reaches 396.9 kJ/m3 and magnet density is 7.42 g/cm3, which are related to the microstructural modification of grain boundaries and the magnet density. Effects of Mg addition on corrosion behavior in sulphuric acid and sodium chloride solution were researched by electrochemical workstation. With increase of Mg addition level, the magnet turns to have a higher corrosion potential and lower corrosion current density, the corrosion poverty is improved. However, temperature coefficient remained nearly unchanged with Mg addition.

Fabrication of highly dense isotropic Nd-Fe-B nylon bonded magnets via extrusion-based additive manufacturing [Fabrication of highly dense isotropic Nd-Fe-B bonded magnets via extrusion-based additive manufacturing

DOE PAGES

Li, Ling; Jones, Kodey E.; Sales, Brian C.; ...

2018-04-03

Magnetically isotropic bonded magnets with a high loading fraction of 70 vol.% Nd-Fe-B are fabricated via an extrusion-based additive manufacturing, or 3D printing system that enables rapid production of large parts. The density of the printed magnet is ~5.2 g/cm 3. The room temperature magnetic properties are: intrinsic coercivity Hci = 8.9 kOe (708.2 kA/m), remanence Br = 5.8 kG (0.58 T), and energy product (BH)max = 7.3 MGOe (58.1 kJ/m 3). The as-printed magnets are then coated with two types of polymers, both of which improve the thermal stability as revealed by flux aging loss measurements. Tensile tests performedmore » at 25 °C and 100 °C show that the ultimate tensile stress (UTS) increases with increasing loading fraction of the magnet powder, and decreases with increasing temperature. AC magnetic susceptibility and resistivity measurements show that the 3D printed Nd-Fe-B bonded magnets exhibit extremely low eddy current loss and high resistivity. Lastly, we demonstrate the performance of the 3D printed magnets in a DC motor configuration via back electromotive force measurements.« less

Fabrication of highly dense isotropic Nd-Fe-B nylon bonded magnets via extrusion-based additive manufacturing [Fabrication of highly dense isotropic Nd-Fe-B bonded magnets via extrusion-based additive manufacturing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Ling; Jones, Kodey E.; Sales, Brian C.

Magnetically isotropic bonded magnets with a high loading fraction of 70 vol.% Nd-Fe-B are fabricated via an extrusion-based additive manufacturing, or 3D printing system that enables rapid production of large parts. The density of the printed magnet is ~5.2 g/cm 3. The room temperature magnetic properties are: intrinsic coercivity Hci = 8.9 kOe (708.2 kA/m), remanence Br = 5.8 kG (0.58 T), and energy product (BH)max = 7.3 MGOe (58.1 kJ/m 3). The as-printed magnets are then coated with two types of polymers, both of which improve the thermal stability as revealed by flux aging loss measurements. Tensile tests performedmore » at 25 °C and 100 °C show that the ultimate tensile stress (UTS) increases with increasing loading fraction of the magnet powder, and decreases with increasing temperature. AC magnetic susceptibility and resistivity measurements show that the 3D printed Nd-Fe-B bonded magnets exhibit extremely low eddy current loss and high resistivity. Lastly, we demonstrate the performance of the 3D printed magnets in a DC motor configuration via back electromotive force measurements.« less

Plasma sprayed Fe(76)Nd(16)B(8) permanent magnets

NASA Technical Reports Server (NTRS)

Overfelt, R. A.; Anderson, C. D.; Flanagan, W. F.

1986-01-01

Thin coatings (0.16 mm) and thick coatings (0.50 mm) of Fe(76)Nd(16)B(8) were deposited on stainless-steel substrates by low pressure plasma spraying. Microscopic examination of the coatings in a light microscope revealed excessive porosity, but good bonding to the substrate. Fracture cross sections examined in a scanning electron microscope showed the grains to be equiaxed and approximately 1 micron or less in diameter in the as-sprayed condition. The intrinsic coercivities of the as-sprayed coatings varied from 5.8 to 10.9 kOe. The effects of postspray heat treatments on the intrinsic coercivity are also given.

Big Area Additive Manufacturing of High Performance Bonded NdFeB Magnets.

PubMed

Li, Ling; Tirado, Angelica; Nlebedim, I C; Rios, Orlando; Post, Brian; Kunc, Vlastimil; Lowden, R R; Lara-Curzio, Edgar; Fredette, Robert; Ormerod, John; Lograsso, Thomas A; Paranthaman, M Parans

2016-10-31

Additive manufacturing allows for the production of complex parts with minimum material waste, offering an effective technique for fabricating permanent magnets which frequently involve critical rare earth elements. In this report, we demonstrate a novel method - Big Area Additive Manufacturing (BAAM) - to fabricate isotropic near-net-shape NdFeB bonded magnets with magnetic and mechanical properties comparable or better than those of traditional injection molded magnets. The starting polymer magnet composite pellets consist of 65 vol% isotropic NdFeB powder and 35 vol% polyamide (Nylon-12). The density of the final BAAM magnet product reached 4.8 g/cm 3 , and the room temperature magnetic properties are: intrinsic coercivity H ci  = 688.4 kA/m, remanence B r  = 0.51 T, and energy product (BH) max  = 43.49 kJ/m 3 (5.47 MGOe). In addition, tensile tests performed on four dog-bone shaped specimens yielded an average ultimate tensile strength of 6.60 MPa and an average failure strain of 4.18%. Scanning electron microscopy images of the fracture surfaces indicate that the failure is primarily related to the debonding of the magnetic particles from the polymer binder. The present method significantly simplifies manufacturing of near-net-shape bonded magnets, enables efficient use of rare earth elements thus contributing towards enriching the supply of critical materials.

Big Area Additive Manufacturing of High Performance Bonded NdFeB Magnets

NASA Astrophysics Data System (ADS)

Li, Ling; Tirado, Angelica; Nlebedim, I. C.; Rios, Orlando; Post, Brian; Kunc, Vlastimil; Lowden, R. R.; Lara-Curzio, Edgar; Fredette, Robert; Ormerod, John; Lograsso, Thomas A.; Paranthaman, M. Parans

2016-10-01

Additive manufacturing allows for the production of complex parts with minimum material waste, offering an effective technique for fabricating permanent magnets which frequently involve critical rare earth elements. In this report, we demonstrate a novel method - Big Area Additive Manufacturing (BAAM) - to fabricate isotropic near-net-shape NdFeB bonded magnets with magnetic and mechanical properties comparable or better than those of traditional injection molded magnets. The starting polymer magnet composite pellets consist of 65 vol% isotropic NdFeB powder and 35 vol% polyamide (Nylon-12). The density of the final BAAM magnet product reached 4.8 g/cm3, and the room temperature magnetic properties are: intrinsic coercivity Hci = 688.4 kA/m, remanence Br = 0.51 T, and energy product (BH)max = 43.49 kJ/m3 (5.47 MGOe). In addition, tensile tests performed on four dog-bone shaped specimens yielded an average ultimate tensile strength of 6.60 MPa and an average failure strain of 4.18%. Scanning electron microscopy images of the fracture surfaces indicate that the failure is primarily related to the debonding of the magnetic particles from the polymer binder. The present method significantly simplifies manufacturing of near-net-shape bonded magnets, enables efficient use of rare earth elements thus contributing towards enriching the supply of critical materials.

Rare Earth Extraction from NdFeB Magnet Using a Closed-Loop Acid Process.

PubMed

Kitagawa, Jiro; Uemura, Ryohei

2017-08-14

There is considerable interest in extraction of rare earth elements from NdFeB magnets to enable recycling of these elements. In practical extraction methods using wet processes, the acid waste solution discharge is a problem that must be resolved to reduce the environmental impact of the process. Here, we present an encouraging demonstration of rare earth element extraction from a NdFeB magnet using a closed-loop hydrochloric acid (HCl)-based process. The extraction method is based on corrosion of the magnet in a pretreatment stage and a subsequent ionic liquid technique for Fe extraction from the HCl solution. The rare earth elements are then precipitated using oxalic acid. Triple extraction has been conducted and the recovery ratio of the rare earth elements from the solution is approximately 50% for each extraction process, as compared to almost 100% recovery when using a one-shot extraction process without the ionic liquid but with sufficient oxalic acid. Despite its reduced extraction efficiency, the proposed method with its small number of procedures at almost room temperature is still highly advantageous in terms of both cost and environmental friendliness. This study represents an initial step towards realization of a closed-loop acid process for recycling of rare earth elements.

Evaluation of the effects of aging in synthetic saliva solution of both commercial and silanized Nd-Fe-B magnets for dental application

NASA Astrophysics Data System (ADS)

Fabiano, F.; Puliafito, V.; Calabrese, L.; Borsellino, C.; Bonaccorsi, L. M.; Giordano, A.; Fabiano, V.; Cordasco, G.

2016-04-01

Neodymium-iron-boron magnets are able to ensure a magnetic flux with high maximum energy product also at miniaturized size. In the past, due to their marked corrosion in saliva they were unsuccessfully implemented in orthodontic systems. Thereby, we propose a multi-layered organic-inorganic coating able to supply anticorrosion resistance, wear resistance and durability to the whole assembly. We evaluated the influence on the magnetic force of commercial nickel plated and silanized Nd-Fe-B during aging time in synthetic Fusayama saliva. Two magnets based-micromagnetic simulations were performed in order to analyze the magnetic field generated which is linked to the magnetic force. Our key results underline that the proposed hybrid coating does not affect the magnetic force of Nd-Fe-B magnets, moreover, preventing corrosion degradation in aggressive solution. Thus the limiting aspects avoiding the use of Nd-Fe-B magnets for orthodontic and prosthodontic applications can be overcome by using silane agents as surface coating.

Imaging the magnetic nanodomains in Nd 2 Fe 14 B

DOE PAGES

Huang, Lunan; Taufour, Valentin; Lamichhane, T. N.; ...

2016-03-08

Here, we study magnetic domains in Nd 2Fe 14B single crystals using high resolution magnetic force microscopy (MFM). Previous MFM studies and small angle neutron scattering experiments suggested the presence of nanoscale domains in addition to optically detected micrometer-scale ones. We find, in addition to the elongated, wavy nanodomains reported by a previous MFM study, that the micrometer-sized, star-shaped fractal pattern is constructed of an elongated network of nanodomains ~20 nm in width, with resolution-limited domain walls thinner than 2 nm. While the microscopic domains exhibit significant resilience to an external magnetic field, some of the nanodomains are sensitive tomore » the magnetic field of the MFM tip.« less

Study on magnetic properties of (Nd0.8Ce0.2)2-xFe12Co2B (x = 0-0.6) alloys

NASA Astrophysics Data System (ADS)

Tan, G. S.; Xu, H.; Yu, L. Y.; Tan, X. H.; Zhang, Q.; Gu, Y.; Hou, X. L.

2017-09-01

In the present work, (Nd0.8Ce0.2)2-xFe12Co2B (x = 0-0.6) permanent alloys are prepared by melt-spinning method. The hard magnetic properties of (Nd0.8Ce0.2)2-xFe12Co2B (x = 0-0.6) alloys annealed at optimum temperatures have been investigated systematically. Depending on the Nd, Ce concentration, the maximum energy product ((BH)max) and remanence (Br) increase gradually with x in the range of 0 ≤ x ≤ 0.4, whereas decrease gradually in the alloys with 0.4 < x ≤ 0.6. It is found that the optimum magnetic properties are obtained at x = 0.4: Hci = 4.9 kOe, Br = 10.1 kG, (BH)max = 13.7 MGOe. Specifically, magnetic field heat treatment below the Curie temperature is applied for (Nd0.8Ce0.2)1.6Fe12Co2B (x = 0.4) annealed ribbons. The magnetic properties Br, (BH)max and squareness are all enhanced after the magnetic field heat treatment. The (BH)max shows a substantial increase from 13.7 MGOe to 16.0 MGOe after the heat treatment at 623 K with a magnetic field of 1 T, which gets 17% improvement compared with that of the sample without a magnetic field heat treatment. We demonstrate that the magnetic field heat treatment plays a certain role in the magnetization reversal behavior and can improve the microstructure of (Nd0.8Ce0.2)1.6Fe12Co2B alloy.

Angular dependence of coercivity derived from alignment dependence of coercivity in Nd-Fe-B sintered magnets

NASA Astrophysics Data System (ADS)

Matsuura, Yutaka; Nakamura, Tetsuya; Sumitani, Kazushi; Kajiwara, Kentaro; Tamura, Ryuji; Osamura, Kozo

2018-01-01

Experimental results of the alignment dependence of the coercivity in Nd-Fe-B sintered magnets showed that the angle of magnetization reversal for anisotropically aligned magnets was bigger than that obtained from the theoretical results calculated using the postulation that every grain independently reverses its magnetization direction following the 1/cos θ law. The angles of reversed magnetization (θ1) for Nd13.48Co0.55B5.76Febal. with alignment α=0.95 and for Nd12.75Dy0.84B5.81Co0.55Febal. with α=0.96 were 30° and 36°, respectively, which were very similar to that of an ideal magnet with a Gaussian distribution (σ=31° and 44°, respectively) of the grain alignment. In this model, we postulated that every grain independently reversed according to the 1/cos θ law. The calculation results for the angular dependence of the coercivity using the values θ1=ω1(0°)=30°, σ=31° and θ1=ω1(0°)=36°, σ=44° could qualitatively and convincingly explain the observed angular dependence of the coercivity of Nd14.2B6.2Co1.0Febal. and Nd14.2Dy0.3B6.2Co1.0Febal.. It is speculated that the magnetic domain wall is pinned at grains tilted away from the easy magnetization direction, and when the magnetic domain wall de-pins from the tilted grains, the magnetic domain wall jumps through several grains. We suggest that the coercive force of the aligned magnet behaves like a low-aligned magnet owing to the magnetization reversal of the crust of the grains induced by the pinning and subsequent jumping of the magnetic domain wall.

Self-vibration cancellation of a novel bi-directional magnetized NdFeB/magnetostrictive/piezoelectric laminate

NASA Astrophysics Data System (ADS)

Leung, Chung Ming; Wang, Feifei; Wang, Ya

2016-06-01

A novel magnetoelectric (ME) laminated composite structure is proposed in this work, aiming to provide a good self-vibration cancellation performance under the magnetic field detection environment. The proposed structure consists of two Terfenol-D magnetostrictive alloy plates which are revised and length-magnetized by two NdFeB magnets bonded on the top surface of a thickness-polarized Pb(Zr, Ti)O3 (PZT) ceramic plate with separate electrodes. Experiments have shown that great vibration suppression up to 44 dB under harmonic disturbance was observed. The ME coefficient of the proposed structure also reaches up to ˜29 mV/Oe at non-resonance frequency and 758 mV/Oe at resonance frequency of 79 kHz which is ˜2 times larger than the traditional L-T Terfenol-D/PZT bilayer configuration of the same scale. Such performance improvement is achieved based on the bi-directional magnetic field bias (HBias) of two NdFeB magnets in magnetostrictive layer, internal in-series electrical wire connection in piezoelectric layer. The proposed design has great potential to be used for industrial applications associated with heavy environmental vibration noise.

Big Area Additive Manufacturing of High Performance Bonded NdFeB Magnets

PubMed Central

Li, Ling; Tirado, Angelica; Nlebedim, I. C.; Rios, Orlando; Post, Brian; Kunc, Vlastimil; Lowden, R. R.; Lara-Curzio, Edgar; Fredette, Robert; Ormerod, John; Lograsso, Thomas A.; Paranthaman, M. Parans

2016-01-01

Additive manufacturing allows for the production of complex parts with minimum material waste, offering an effective technique for fabricating permanent magnets which frequently involve critical rare earth elements. In this report, we demonstrate a novel method - Big Area Additive Manufacturing (BAAM) - to fabricate isotropic near-net-shape NdFeB bonded magnets with magnetic and mechanical properties comparable or better than those of traditional injection molded magnets. The starting polymer magnet composite pellets consist of 65 vol% isotropic NdFeB powder and 35 vol% polyamide (Nylon-12). The density of the final BAAM magnet product reached 4.8 g/cm3, and the room temperature magnetic properties are: intrinsic coercivity Hci = 688.4 kA/m, remanence Br = 0.51 T, and energy product (BH)max = 43.49 kJ/m3 (5.47 MGOe). In addition, tensile tests performed on four dog-bone shaped specimens yielded an average ultimate tensile strength of 6.60 MPa and an average failure strain of 4.18%. Scanning electron microscopy images of the fracture surfaces indicate that the failure is primarily related to the debonding of the magnetic particles from the polymer binder. The present method significantly simplifies manufacturing of near-net-shape bonded magnets, enables efficient use of rare earth elements thus contributing towards enriching the supply of critical materials. PMID:27796339

Microstructures, magnetic properties and coercivity mechanisms of Nd-Ce-Fe-B based alloys by Zr substitution

NASA Astrophysics Data System (ADS)

Wang, Lei; Quan, Qichen; Zhang, Lili; Hu, Xianjun; Ur Rehman, Sajjad; Jiang, Qingzheng; Du, Junfeng; Zhong, Zhenchen

2018-03-01

In this paper, the effects of Zr addition on microstructures, magnetic properties, exchange coupling, and coercivity mechanisms of Nd-Ce-Fe-B alloys fabricated by melt-spinning technique are investigated. It is found that the coercivity Hcj is enhanced significantly by Zr substitution in the (Nd0.8Ce0.2)13Fe82-xZrxB5 alloys, while the remanence Jr is reduced slightly. The Hcj increases from 12.2 to 13.7 kOe by adding Zr up to 1.5 at. %, whereas Hcj is decreased with a further increase in Zr content. The larger lattice constants and unit cell volumes of the matrix phase indicate that Zr atoms enter into the hard magnetic phase by substituting Fe sites. The reduction of Tc implies the attenuation of the exchange interaction in the 2:14:1 phase with Zr occupying the Fe sites. The weakened intergranular exchange coupling of the Zr added alloy may be attributed to the formation of a non-magnetic intergranular phase. It is worth noting that the coercivity is dominated by the pinning of domain walls at defect positions even though the nucleation of reversal domains still exists. The synergistic function between the pinning effect and the exchange coupling leads to improved magnetic properties.

Magnetic studies of melt spun NdFeAl-C alloys

NASA Astrophysics Data System (ADS)

Rodríguez Torres, C. E.; Cabrera, A. F.; Sánchez, F. H.; Billoni, O. V.; Urreta, S. E.; Fabietti, L. M.

2004-12-01

Alloys with compositions Nd 60-xC xFe 30Al 10 ( x=0, 1, 5 and 10) were processed by melt spinning at a tangential speed of 5 m/s. The as-cast ribbons were characterized by X-ray diffraction, Mössbauer Effect spectroscopy and their room temperature hysteresis loops. The substitution of Nd by C is found to affect the phase selection, from mainly DHCP-Nd for x=0 to DHCP-Nd /FCC-Nd for the other ones. Mössbauer spectra of all the as-cast samples indicate that Fe is present in crystalline magnetic phases as well as in a paramagnetic one. The major crystalline phase was identified as a μ-type (or A1) metastable phase, which is reported to have a large anisotropy field and a relatively high saturation polarization. Interstitial C stabilizes the μ-type phase and improves its average hyperfine field. The magnetic measurements display an increase of coercivity and remanence with the C concentration.

Effect of Partial Substitution of Neodymium with Praseodymium on the Magnetic and Process Properties of Sintered Magnets of Type NdFeB

NASA Astrophysics Data System (ADS)

Dormidontov, N. A.; Dormidontov, A. G.; Lileev, A. S.; Kamynin, A. V.; Lukin, A. A.

2017-01-01

The effect of substitution of neodymium with praseodymium in sintered magnets of type NdFeB on their magnetic and process properties in the concentration range of [Pr] = 0 - 13 wt.% is studied. The special features of milling of the alloys, sintering processes and heat treatments in the production of magnets containing praseodymium are discussed. Hysteresis characteristics of B r ≥ 1.2 T, H cJ ≥ 1200 kA/m, H cb ≥ 880 kA/m, H k ≥ 960 kA/m, and BH max ≥ 280 kJ/m3 are obtained for magnets with composition (in wt.%) 33 Nd, 10 Pr, 1.5 (Ti + Al + Cu), 1.3 B, the remainder Fe.

Magnetic structure of the mixed antiferromagnet NdMn0.8Fe0.2O3

NASA Astrophysics Data System (ADS)

Mihalik, Matúš; Mihalik, Marián; Hoser, Andreas; Pajerowski, Daniel M.; Kriegner, Dominik; Legut, Dominik; Lebecki, Kristof M.; Vavra, Martin; Fitta, Magdalena; Meisel, Mark W.

2017-10-01

The magnetic structure of the mixed antiferromagnet NdMn0.8Fe0.2O3 was resolved. Neutron powder diffraction data definitively resolve the Mn sublattice with a magnetic propagation vector k =(000 ) and with the magnetic structure (Ax,Fy,Gz ) for 1.6 K Nd sublattice has a (0 ,fy,0 ) contribution in the same temperature interval. The Mn sublattice undergoes a spin-reorientation transition at T1≈13 K while the Nd magnetic moment abruptly increases at this temperature. Powder x-ray diffraction shows a strong magnetoelastic effect at TN but no additional structural phase transitions from 3 to 300 K. Density functional theory calculations confirm the magnetic structure of the undoped NdMnO3 as part of our analysis. Taken together, these results show that the magnetic structure of the Mn sublattice in NdMn0.8Fe0.2O3 is a combination of the Mn and Fe parent compounds, but the magnetic ordering of the Nd sublattice spans a broader temperature interval than in the case of NdMnO3 and NdFeO3. This result is a consequence of the fact that the Nd ions do not order independently, but via polarization from the Mn/Fe sublattice.

Novel hydrogen decrepitation behaviors of (La, Ce)-Fe-B strips

NASA Astrophysics Data System (ADS)

Jin, Jiaying; Bai, Guohua; Zhang, Yujing; Peng, Baixing; Liu, Yongsheng; Ma, Tianyu; Yan, Mi

2018-05-01

La and Ce substitution for Nd in the 2:14:1-type sintered magnet is of commercial interest to reduce the material cost and to balance the utilization of rare earth (RE) sources. As hydrogen decrepitation (HD) is widely utilized to prepare the magnetic powders during magnets fabrication, incorporating La and Ce into the Nd-Fe-B permanent magnets, however, may exert complex influences on the decrepitation behavior. In the present work, through a comparative study of the HD behaviors between the (La, Ce)-Fe-B strips and the conventional Nd-Fe-B ones, we find that similar to the Nd-Fe-B system, increasing hydrogen pressures from 2.5 to 5.5 MPa do not break the 2:14:1 tetragonal structure of (La, Ce)-Fe-B strips. The enhanced hydrogen absorption behaviors are observed with increasing pressure, which are still inferior to that of the Nd-Fe-B strips. This should be ascribed to the higher oxygen affinity of La and Ce than that of Nd, leading to the decreased amount of active RE-rich phase and limited hydrogen diffusion channel. As a result, the hydrogen absorption of 2:14:1 matrix phase is significantly suppressed, dramatically weakening the exothermic effect. This finding suggests that La and Ce with stable 2:14:1 tetragonal structure upon HD process are promising alternatives for Nd, despite that more precise oxygen control is necessary for the microstructure modification and magnetic performance enhancement of (La, Ce)-Fe-B sintered magnets.

Improvement of the magnetic moment of NiZn ferrites induced by substitution of Nd3+ ions for Fe3+ ions

NASA Astrophysics Data System (ADS)

Wu, Xuehang; Chen, Wen; Wu, Wenwei; Wu, Juan; Wang, Qing

2018-05-01

Four types of Ni-Zn based ferrites materials having the general formula Ni0.5Zn0.5NdxFe2-xO4 (0.0 ≤ x ≤ 0.12) have been successfully synthesized by calcining oxalates in air and the influence of Nd content on the structure and magnetic properties of Ni0.5Zn0.5NdxFe2-xO4 is studied. X-ray diffraction examination confirms that a high-crystallized Ni0.5Zn0.5NdxFe2-xO4 with cubic spinel structure is obtained when the precursor is calcined at 1000 °C in air for 2 h. The substitutions of Nd3+ ions for partial Fe3+ ions do not change the spinel crystalline structure of MFe2O4. The incorporation of Nd3+ ions in place of Fe3+ ions in Ni-Zn ferrites increases the average crystallite size. Specific saturation magnetization decreases with increase in Nd content. This is because Nd3+ ions with smaller magnetic moment preferentially fill the octahedral sites. In addition, antiferromagnetic FeNdO3 increases with increase in Nd content. In this study, Ni0.5Zn0.5Nd0.08Fe1.92O4, calcined at 1000 °C, exhibits the highest magnetic moment (4.2954 μB) and the lowest coercivity (28.82 Oe).

Characterization of α-Fe-Free Heteroepitaxial NdFe12- x Ti x Thin-Film Materials with a Novel Cubic Laves Fe2Ti Phase

NASA Astrophysics Data System (ADS)

Hadorn, Jason Paul; Hirayama, Yusuke; Ohkubo, Tadakatsu

2018-01-01

Thin films with compositions of NdFe12 and NdFe11Ti1 were fabricated on W-buffered MgO(001) substrates of varying roughness. In this study, X-ray diffraction (XRD) and transmission electron microscopy (TEM) were used to characterize the films microstructurally, chemically, and crystallographically. This study revealed successful heteroepitaxial synthesis of the tetragonal NdFe12 and NdFe12- x Ti x phases in the Ti-free and Ti-containing films, respectively, both with surface-normal c-axis orientation. It also revealed the presence of other phases within the magnetic layer. The NdFe12 films contained many α-Fe particles, which preferentially precipitated at locally rough regions of the W-buffer interface. The NdFe11Ti1 film showed the ubiquitous presence of an Fe2Ti phase, which covered most of the buffer thereby preventing the formation of α-Fe. This phase was determined to have a novel Cu2Mg-type cubic Laves ( C15) crystal structure with fourfold interfacial symmetry, good coherency, and a low mismatch with the W-buffer, thus rendering itself as being an ideal interface for the heteroepitaxial synthesis of NdFe12- x Ti x crystals. It is proposed that successful application of a cubic Fe2Ti underlayer on W can contribute to the development of a fabrication strategy for NdFe12 thin films without the presence of soft magnetic α-Fe.

Hydrogen Decrepitation Press-Less Process recycling of NdFeB sintered magnets

NASA Astrophysics Data System (ADS)

Xia, Manlong; Abrahamsen, Asger B.; Bahl, Christian R. H.; Veluri, Badrinath; Søegaard, Allan I.; Bøjsøe, Poul

2017-11-01

A Hydrogen Decrepitation Press-Less Process (HD-PLP) recycling method for recycling of anisotropic NdFeB magnets is demonstrated. The method combines hydrogen decrepitation (HD) disintegration of the initial magnet, powder sieving and the Press-Less Process (PLP), where hydride powder is sintered in a graphite mold. Coercivities up to 534 kA/m were obtained in porous samples based on powder size d < 100 μm. Adding a ball milling step resulted in full density isotropic magnets for d > 100 μm. The coercivity reached Hci = 957 kA/m being 86% of the original N48M material without addition of rare earth elements.

Unsupervised data mining in nanoscale x-ray spectro-microscopic study of NdFeB magnet

DOE Office of Scientific and Technical Information (OSTI.GOV)

Duan, Xiaoyue; Yang, Feifei; Antono, Erin

Novel developments in X-ray based spectro-microscopic characterization techniques have increased the rate of acquisition of spatially resolved spectroscopic data by several orders of magnitude over what was possible a few years ago. This accelerated data acquisition, with high spatial resolution at nanoscale and sensitivity to subtle differences in chemistry and atomic structure, provides a unique opportunity to investigate hierarchically complex and structurally heterogeneous systems found in functional devices and materials systems. However, handling and analyzing the large volume data generated poses significant challenges. Here we apply an unsupervised data-mining algorithm known as DBSCAN to study a rare-earth element based permanentmore » magnet material, Nd 2Fe 14B. We are able to reduce a large spectro-microscopic dataset of over 300,000 spectra to 3, preserving much of the underlying information. Scientists can easily and quickly analyze in detail three characteristic spectra. Our approach can rapidly provide a concise representation of a large and complex dataset to materials scientists and chemists. For instance, it shows that the surface of common Nd 2Fe 14B magnet is chemically and structurally very different from the bulk, suggesting a possible surface alteration effect possibly due to the corrosion, which could affect the material’s overall properties.« less

Unsupervised data mining in nanoscale x-ray spectro-microscopic study of NdFeB magnet

DOE PAGES

Duan, Xiaoyue; Yang, Feifei; Antono, Erin; ...

2016-09-29

Novel developments in X-ray based spectro-microscopic characterization techniques have increased the rate of acquisition of spatially resolved spectroscopic data by several orders of magnitude over what was possible a few years ago. This accelerated data acquisition, with high spatial resolution at nanoscale and sensitivity to subtle differences in chemistry and atomic structure, provides a unique opportunity to investigate hierarchically complex and structurally heterogeneous systems found in functional devices and materials systems. However, handling and analyzing the large volume data generated poses significant challenges. Here we apply an unsupervised data-mining algorithm known as DBSCAN to study a rare-earth element based permanentmore » magnet material, Nd 2Fe 14B. We are able to reduce a large spectro-microscopic dataset of over 300,000 spectra to 3, preserving much of the underlying information. Scientists can easily and quickly analyze in detail three characteristic spectra. Our approach can rapidly provide a concise representation of a large and complex dataset to materials scientists and chemists. For instance, it shows that the surface of common Nd 2Fe 14B magnet is chemically and structurally very different from the bulk, suggesting a possible surface alteration effect possibly due to the corrosion, which could affect the material’s overall properties.« less

Treatment of reverse osmosis (RO) concentrate by the combined Fe/Cu/air and Fenton process (1stFe/Cu/air-Fenton-2ndFe/Cu/air).

PubMed

Ren, Yi; Yuan, Yue; Lai, Bo; Zhou, Yuexi; Wang, Juling

2016-01-25

To decompose or transform the toxic and refractory reverse osmosis (RO) concentrate and improve the biodegradability, 1stFe/Cu/air-Fenton-2ndFe/Cu/air were developed to treat RO concentrate obtained from an amino acid production plant in northern China. First, their operating conditions were optimized thoroughly. Furthermore, 5 control experiments were setup to confirm the superiority of 1stFe/Cu/air-Fenton-2ndFe/Cu/air and synergistic reaction between Fe/Cu/air and Fenton. The results suggest that the developed method could obtain high COD removal (65.1%) and BOD5/COD ratio (0.26) due to the synergistic reaction between Fe/Cu/air and Fenton. Under the optimal conditions, the influent and effluent of 1stFe/Cu/air-Fenton-2ndFe/Cu/air and 5 control experiments were analyzed by using UV, FTIR, EEM and LC, which confirm the superiority of 1stFe/Cu/air-Fenton-2ndFe/Cu/air. Therefore, the developed method in this study is a promising process for treatment of RO concentrate. Copyright © 2015 Elsevier B.V. All rights reserved.

Magnetic structure of the mixed antiferromagnet NdMn 0.8 Fe 0.2 O 3

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mihalik, Matus; Mihalik, Marian; Hoser, Andreas

The magnetic structure of the mixed antiferromagnet NdMn 0.8Fe 0.2O 3 was resolved. Neutron powder diffraction data definitively resolve the Mn sublattice with a magnetic propagation vector k=(000) and with the magnetic structure (A x, F y, G z) for 1.6 K N(≈ 59 K). The Nd sublattice has a (0, f y, 0) contribution in the same temperature interval. The Mn sublattice undergoes a spin-reorientation transition at T 1 ≈ 13 K while the Nd magnetic moment abruptly increases at this temperature. Powder x-ray diffraction shows a strong magnetoelastic effect at T N but no additional structural phase transitionsmore » from 3 to 300 K. Density functional theory calculations confirm the magnetic structure of the undoped NdMnO 3 as part of our analysis. Taken together, these results show that the magnetic structure of the Mn sublattice in NdMn 0.8Fe 0.2O 3 is a combination of the Mn and Fe parent compounds, but the magnetic ordering of the Nd sublattice spans a broader temperature interval than in the case of NdMnO 3 and NdFeO 3. Lastly, this result is a consequence of the fact that the Nd ions do not order independently, but via polarization from the Mn/Fe sublattice.« less

Magnetic structure of the mixed antiferromagnet NdMn 0.8 Fe 0.2 O 3

DOE PAGES

Mihalik, Matus; Mihalik, Marian; Hoser, Andreas; ...

2017-10-27

The magnetic structure of the mixed antiferromagnet NdMn 0.8Fe 0.2O 3 was resolved. Neutron powder diffraction data definitively resolve the Mn sublattice with a magnetic propagation vector k=(000) and with the magnetic structure (A x, F y, G z) for 1.6 K N(≈ 59 K). The Nd sublattice has a (0, f y, 0) contribution in the same temperature interval. The Mn sublattice undergoes a spin-reorientation transition at T 1 ≈ 13 K while the Nd magnetic moment abruptly increases at this temperature. Powder x-ray diffraction shows a strong magnetoelastic effect at T N but no additional structural phase transitionsmore » from 3 to 300 K. Density functional theory calculations confirm the magnetic structure of the undoped NdMnO 3 as part of our analysis. Taken together, these results show that the magnetic structure of the Mn sublattice in NdMn 0.8Fe 0.2O 3 is a combination of the Mn and Fe parent compounds, but the magnetic ordering of the Nd sublattice spans a broader temperature interval than in the case of NdMnO 3 and NdFeO 3. Lastly, this result is a consequence of the fact that the Nd ions do not order independently, but via polarization from the Mn/Fe sublattice.« less

Site-preference and valency for rare-earth sites in (R-Ce)2Fe14B [R =La,Nd] magnets

NASA Astrophysics Data System (ADS)

Alam, Aftab; Khan, Mahmud; McCallum, R. W.; Johnson, D. D.

2013-03-01

Rare-earth (R) permanent magnets of R2Fe14B have technological importance due to their high energy products, and they have two symmetry distinct R-sites (Wyckoff 4f and 4g) that affect chemistry and valence. Designing magnetic behavior and stability via alloying is technologically relevant to reduce critical (expensive) R-content while retaining key properties; cerium, an abundant (cheap) R-element, offers this potential. We calculate magnetic properties and Ce site preference in (R1-xCex)Fe14B [R=La,Nd] using density functional theory (DFT) methods. The Fe moments compare well with neutron scattering data - remain weakly affected by Hubbard U, but improved with spin-orbit coupling. In (La,Ce)2Fe14B, Ce alloys for 0 < x < 1 with a preference for smaller R(4f) sites, as observed, a trend we find unaffected by valence. Whereas in (Nd,Ce)2Fe14B, Ce is predicted to have limited alloying (x < 0.3) with a preference for larger R(4g) sites, resulting in weak partial ordering and segregation. Curie temperatures versus x were predicted for a typical sample processing and verified experimentally. We shall also present some initial results on the critical mixed valency of Ce in related compounds. Work at Ames Laboratory was supported by the U.S. Department of Energy, ARPA-E under the REACT program (0472-1526)

Ceramics-bonded Nd-Fe-B-type magnet with high electrical resistivity

NASA Astrophysics Data System (ADS)

Kang, M. S.; Kwon, H. W.; Kim, D. H.; Lee, J. G.; Yu, J. H.

2018-05-01

Ceramics-bonded magnet with remarkably high electrical resistivity was fabricated by hot-pressing the mixture of Nd13.6Fe73.6Co6.6Ga0.6B5.6 alloy melt-spun flakes and dielectric Bi2O3-SiO2-B2O3 ceramics powder with low melting point. Coercivity of the ceramics-bonded magnet decreased with increasing the addition of ceramics binder, and this was attributed to the increased demagnetizing factor. Thin oxidized layer on the flake surface formed by reaction between the flake and oxide binder also contributed to reducing coercivity in the ceramics-bonded magnet. Highly resistive ceramics-bonded magnet containing 30 vol% ceramics binder still had good magnetic performance and high mechanical strength at 175 oC: iHc = 5 kOe, Mr = 4.8 kG, (BH)max = 4.3 MGOe, and over 900 MPa.

Effect of annealing conditions on the microstructure and magnetic properties of sintered Nd-Fe-B magnets as seen by magnetic small-angle neutron scattering

NASA Astrophysics Data System (ADS)

Périgo, Élio A.; Titov, Ivan; Weber, Raoul; Mettus, Denis; Peral, Inma; Vallcorba, Oriol; Honecker, Dirk; Feoktystov, Artem; Michels, Andreas

2018-03-01

We have investigated the effect of the annealing conditions (heating rate and temperature) on the magnetic microstructure of sintered Nd-Fe-B magnets by means of magnetometry, scanning electron microscopy, high-energy synchrotron x-ray diffraction, and small-angle neutron scattering (SANS). While the temperature treatment has a strong effect on the coercivity (reduction by about 50% on annealing), the associated changes in the microstructure do surprisingly not show up (or at best only very weakly) in the neutron-scattering signal, which probes a mesoscopic real-space length scale ranging between about 1–300 nm. On the other hand, the x-ray data reveal microstructural changes in the Nd-rich phases, presumably due to modifications in grain-boundary regions. Moreover, we observe an unusual diamond-shaped angular anisotropy in the SANS cross section, which strongly points towards the existence of texture in the nuclear microstructure.

Highly oriented NdFeCoB nanocrystalline magnets from partially disproportionated compacts by reactive deformation under low pressure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zheng, Qing; Li, Jun; Liu, Ying, E-mail: liuying5536@163.com

2014-05-07

In the present investigation, we take advantage of the ultrafine grain size of NdFeCoB partially hydrogen-disproportionated phases, and prepare anisotropic nanocrystalline magnets with full density and homogenous microstructure and texture by reactive deformation under low pressure. Our results suggest that the pressure could properly promote an occurrence of desorption-recombination reaction due to a shorter-range rearrangement of the atoms, and the newly recombined Nd{sub 2}Fe{sub 14}B grains with fine grain size could undergo deformation immediately after the phase transformation, and then an obvious anisotropy and uniform alignment would be obtained. The maximum magnetic properties, (BH){sub max} = 25.8 MGOe, Br = 11.8 kG, H{sub cj} = 5.5more » kOe, were obtained after being treated for 5 min at 820 °C in vacuum. The present study highlights the feasibility to prepare anisotropic nanocrystalline magnets with homogeneous microstructure and a strong (00l) texture of uniform grain size under low pressure.« less

Structure and performance of anisotropic nanocrystalline Nd-Fe-B magnets fabricated by high-velocity compaction followed by deformation

NASA Astrophysics Data System (ADS)

Zhao, L. Z.; Deng, X. X.; Yu, H. Y.; Guan, H. J.; Li, X. Q.; Xiao, Z. Y.; Liu, Z. W.; Greneche, J. M.

2017-12-01

High-velocity compaction (HVC) has been proposed as an effective approach for the fabrication of nanocrystalline Nd-Fe-B magnets. In this work, the effect of powder size on the density of HVCed magnets has been studied and the anisotropic nanocrystalline Nd-Fe-B magnets were prepared by HVC followed by hot deformation (HD). It is found that a proper particle size range is beneficial to high density. The investigations on the microstructure, magnetic domain structure, and hyperfine structure, indicate that the deformed grain structure and the magnetic domain structure with uniform paramagnetic grain boundary phase give good magnetic properties of HVC + HDed magnets. These magnets also have good mechanical and anti-corrosion properties. The results indicate that HVC is not only a near-net-shape, room temperature and binder-free process but is also able to maintain uniform nanostructure and to achieve good magnetic properties in both isotropic and anisotropic magnets. As a result, HVC can be employed as an ideal alternative process for bonding or hot pressing for the conventional MQI, MQII and MQIII magnets.

Magnetization reversal mechanisms in hybrid resin-bonded Nd Fe B magnets

NASA Astrophysics Data System (ADS)

Plusa, D.; Dospial, M.; Slusarek, B.; Kotlarczyk, U.

2006-11-01

The magnetic properties of isotropic epoxy resin-bonded magnets prepared by mixing a hard magnetic powder made from melt quenched Nd-Fe-Co-B ribbons and a soft magnetic iron powder have been examined. The magnetization reversal processes and the magnetic parameters have been studied by the measurement of the virgin magnetization curves, the major and minor hysteresis loops and sets of recoil curves. From these recoil curves the field dependence of the reversible and irreversible magnetization components during the magnetization and demagnetization processes has been derived. The remanence relationship was used to study the nature of magnetic interaction between the grains. A study of interaction domains was conducted using optical microscopy. Groups of domains, each over several grains, were observed. It was found that the reversal process in the samples investigated involves the rotation of magnetization vectors in the iron powder grains and pinning of domain walls at the MQP-B grain boundaries.

The thermal expansion of hard magnetic materials of the Nd-Fe-B system

NASA Astrophysics Data System (ADS)

Savchenko, Igor; Kozlovskii, Yurii; Samoshkin, Dmitriy; Yatsuk, Oleg

2017-10-01

The results of dilatometric measurement of the thermal expansion of hard magnetic materials brands N35M, N35H and N35SH containing as a main component the crystalline phase of Nd2Fe14B type are presented. The temperature range from 200 to 750 K has been investigated by the method of dilatometry with an error of 1.5-2×10-7 K-1. The approximation dependences of the linear thermal expansion coefficient have been obtained. The character of changes of the thermal coefficient of linear expansion in the region of the Curie point has been specified, its critical indices and critical amplitudes have been defined.

Rapid sintering of anisotropic, nanograined Nd-Fe-B by flash-spark plasma sintering

NASA Astrophysics Data System (ADS)

Castle, Elinor; Sheridan, Richard; Grasso, Salvatore; Walton, Allan; Reece, Mike

2016-11-01

A Spark Plasma Sintering (SPS) furnace was used to Flash-Sinter (FS) Nd-Fe-Dy-Co-B-Ga melt spun permanent magnetic material. During the 10 s "Flash" process (heating rate 2660 K min-1), sample sintering (to theoretical density) and deformation (54% height reduction) occurred. This produced texturing and significant magnetic anisotropy, comparable to conventional die-upset magnets; yet with much greater coercivities (>1600 kA m-1) due to the nanoscale characteristics of the plate-like sintered grains. These preliminary results suggest that Flash-SPS could provide a new processing route for the mass production of highly anisotropic, nanocrystalline magnetic materials with high coercivity.

Magnetic interactions in anisotropic Nd-Dy-Fe-Co-B/α-Fe multilayer magnets

NASA Astrophysics Data System (ADS)

Dai, Z. M.; Liu, W.; Zhao, X. T.; Han, Z.; Kim, D.; Choi, C. J.; Zhang, Z. D.

2016-10-01

The magnetic properties and the possible interaction mechanisms of anisotropic soft- and hard-magnetic multilayers have been investigated by altering the thickness of different kinds of spacer layers. The metal Ta and the insulating oxides MgO, Cr2O3 have been chosen as spacer layers to investigate the characteristics of the interactions between soft- and hard-magnetic layers in the anisotropic Nd-Dy-Fe-Co-B/α-Fe multilayer system. The dipolar and exchange interaction between hard and soft phases are evaluated with the help of the first order reversal curve method. The onset of the nucleation field and the magnetization reversal by domain wall movement are also evident from the first-order-reversal-curve measurements. Reversible/irreversible distributions reveal the natures of the soft- and hard-magnetic components. Incoherent switching fields are observed and the calculations show the semiquantitative contributions of hard and soft components to the system. An antiferromagnetic spacer layer will weaken the interaction between ferromagnetic layers and the effective interaction length decreases. As a consequence, the dipolar magnetostatic interaction may play an important role in the long-range interaction in anisotropic multilayer magnets.

Study of structural and magnetic properties of melt spun Nd2Fe13.6Zr0.4B ingot and ribbon

NASA Astrophysics Data System (ADS)

Amin, Muhammad; Siddiqi, Saadat A.; Ashfaq, Ahmad; Saleem, Murtaza; Ramay, Shahid M.; Mahmood, Asif; Al-Zaghayer, Yousef S.

2015-12-01

Nd2Fe13.6Zr0.4B hard magnetic material were prepared using arc-melting technique on a water-cooled copper hearth kept under argon gas atmosphere. The prepared samples, Nd2Fe13.6Zr0.4B ingot and ribbon are characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM) for crystal structure determination and morphological studies, respectively. The magnetic properties of the samples have been explored using vibrating sample magnetometer (VSM). The lattice constants slightly increased due to the difference in the ionic radii of Fe and that of Zr. The bulk density decreased due to smaller molar weight and low density of Zr as compared to that of Fe. Ingot sample shows almost single crystalline phase with larger crystallite sizes whereas ribbon sample shows a mixture of amorphous and crystalline phases with smaller crystallite sizes. The crystallinity of the material was highly affected with high thermal treatments. Magnetic measurements show noticeable variation in magnetic behavior with the change in crystallite size. The sample prepared in ingot type shows soft while ribbon shows hard magnetic behavior.

Corrosion Protection of Nd-Fe Magnets via Phophatization, Silanization and Electrostatic Spraying with Organic Resin Composite Coatings

NASA Astrophysics Data System (ADS)

Ding, Xia; Li, Jingjie; Li, Musen; Ge, Shengsong; Wang, Xiuchun; Ding, Kaihong; Cui, Shengli; Sun, Yongcong

2014-09-01

Nd-Fe-B permanent magnets possess excellent properties. However, they are highly sensitive to the attack of corrosive environment. The aim of this work is to improve the corrosion resistance of the magnets by phosphatization, silanization, and electrostatic spraying with organic resin composite coatings. Field emission scanning electron microscope (FE-SEM) and energy dispersive spectrometer (EDS) tests showed that uniform phosphate conversion coatings and spray layers were formed on the surface of the Nd-Fe-B magnets. Neutral salt spray tests exhibited that, after treated by either phosphating, silanization or electrostatic spraying, the protectiveness of Nd-Fe-B alloys was apparently increased. And corrosion performance of magnets treated with silane only was slightly inferior to those of phosphatized ones. However, significant improvement in corrosion protection was achieved after two-step treatments, i.e. by top-coating spray layer with phosphate or silane films underneath. Grid test indicated that the phosphate and silane coating were strongly attached to the substrate while silane film was slightly weaker than the phosphate-treated ones. Magnetic property analysis revealed phosphatization, silanization, and electrostatic spraying caused decrease in magnetism, but silanization had the relatively smaller effect.

Observation of magnetization and exchange bias reversals in NdFe0.5Cr0.5O3

NASA Astrophysics Data System (ADS)

Sharannia, M. P.; De, Santanu; Singh, Ripandeep; Das, A.; Nirmala, R.; Santhosh, P. N.

2017-05-01

Polycrystalline NdFe0.5Cr0.5O3 has orthorhombic structure with Pnma space group and is magnetically ordered at room temperature as confirmed by neutron diffraction. The magnetic structure involves CxGyFz type ordering of Fe3+/Cr3+ ions. NdFe0.5Cr0.5O3 shows magnetization reversal and sign reversal of exchange bias at 16 K. Nd3+ moments that get induced by the internal field of |Fe+Cr| sublattice couple antiferromagnetically with the ferromagnetic component of |Fe+Cr| sublattice. Nd3+ moments overcome the |Fe+Cr| moments at 16 K below which the material shows negative magnetization and positive exchange bias.

Nd-doped Bi2O3 nanocomposites: simple synthesis and improved photocatalytic activity for hydrogen production under visible light

NASA Astrophysics Data System (ADS)

Al-Namshah, Khadijah S.; Mohamed, Reda M.

2018-04-01

Bi2O3 has 2.4 eV band gap energy, which means it absorb in visible region. Though the photocatalytic activity of Bi2O3 is extremely little due to rapid rate of photogenerated electron-hole recombination. To face the economical and practical needs, the photocatalytic efficiency of Bi2O3 should be upgraded. In this paper, this was achieved by addition of neodymium to Bi2O3 nanosheets and Nd/Bi2O3 nanocomposites were prepared by a easy process at room temperature using a surfactant of Pluronic F127. The Bi2O3 nanosheets and Nd/Bi2O3 nanocomposites were investigated by many tools. The photocatalytic activity of Nd/Bi2O3 samples is better than Bi2O3 due to reduced band gap and reduced electron-hole recombination of Bi2O3 with addition of neodymium. In addition, Nd/Bi2O3 nanocomposites exhibit photocatalytic stability for hydrogen production which enables it to be reused on other occasions also.

Increased Efficiency of a Permanent Magnet Synchronous Generator through Optimization of NdFeB Magnet Arrays

NASA Astrophysics Data System (ADS)

Khazdozian, Helena; Hadimani, Ravi; Jiles, David

2014-03-01

The United States is currently dependent on fossil fuels for the majority of its energy needs, which has many negative consequences such as climate change. Wind turbines present a viable alternative, with the highest energy return on investment among even fossil fuel generation. Traditional commercial wind turbines use an induction generator for energy conversion. However, induction generators require a gearbox to increase the rotational speed of the drive shaft. These gearboxes increase the overall cost of the wind turbine and account for about 35 percent of reported wind turbine failures. Direct drive permanent magnet synchronous generators (PMSGs) offer an alternative to induction generators which eliminate the need for a gearbox. Yet, PMSGs can be more expensive than induction generators at large power output due to their size and weight. To increase the efficiency of PMSGs, the geometry and configuration of NdFeB permanent magnets were investigated using finite element techniques. The optimized design of the PMSG increases flux density and minimizes cogging torque with NdFeB permanent magnets of a reduced volume. These factors serve to increase the efficiency and reduce the overall cost of the PMSG. This work is supported by a National Science Foundation IGERT fellowship and the Barbara and James Palmer Endowment at the Department of Electrical and Computer Engineering of Iowa State University.

Large enhancement of magnetic moment in L1(0) ordered FePt thin films by Nd substitutional doping

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xu, D. B.; Sun, C J; Chen, J. S.

2015-07-01

We studied L1(0) ordered Fe50Pt50-xNdx alloy films, which showed a large enhancement (similar to 18.4% at room temperature and similar to 11.7% at 10 K) of magnetic moment with 6 atomic % of Nd. Analysis of the x-ray magnetic circular dichroism spectra at the Fe L-3,L-2 edges and Nd M-5,M-4 edges in Fe50Pt44Nd6 films indicated a significant contribution of the Nd orbital moment. The origin of the large enhancement of magnetic moment was attributed to the effect of ferromagnetic coupling of the total magnetic moments between Fe and Nd. Density functional theory based first principles calculations supported the experimental observationsmore » of increasing moment due to Nd substitution of Pt.« less

Coercivity degradation caused by inhomogeneous grain boundaries in sintered Nd-Fe-B permanent magnets

NASA Astrophysics Data System (ADS)

Chen, Hansheng; Yun, Fan; Qu, Jiangtao; Li, Yingfei; Cheng, Zhenxiang; Fang, Ruhao; Ye, Zhixiao; Ringer, Simon P.; Zheng, Rongkun

2018-05-01

Quantitative correlation between intrinsic coercivity and grain boundaries in three dimensions is critical to further improve the performance of sintered Nd-Fe-B permanent magnets. Here, we quantitatively reveal the local composition variation across and especially along grain boundaries using the powerful atomic-scale analysis technique known as atom probe tomography. We also estimate the saturation magnetization, magnetocrystalline anisotropy constant, and exchange stiffness of the grain boundaries on the basis of the experimentally determined structure and composition. Finally, using micromagnetic simulations, we quantify the intrinsic coercivity degradation caused by inhomogeneous grain boundaries. This approach can be applied to other magnetic materials for the analysis and optimization of magnetic properties.

Magnetic and microstructural investigation of high-coercivity net-shape Nd-Fe-B-type magnets produced from spark-plasma-sintered melt-spun ribbons blended with DyF3

NASA Astrophysics Data System (ADS)

Žagar, Kristina; Kocjan, Andraž; Kobe, Spomenka

2016-04-01

Nanostructured Nd-Fe-B-type materials produced by melt-spinning (MS) are used in a variety of applications in the electronics, automotive, and sensor industries. The very rapid MS process leads to flake-like powders with metastable, nanoscale, Nd2Fe14B grains. These powders are then formed into net-shaped, isotropic, polymer-bonded magnets, or they are hot formed into fully dense, metallic magnets that are isotropic and anisotropic. These fully dense magnets are usually produced with a conventional hot press without the inclusion of additives prior to the hot pressing. As a result, their properties, particularly the coercivity (Hci), are insufficient at automotive-relevant temperatures of 100-150 °C since the material Hci has a large temperature coefficient. In this study, we instead add a thin layer of DyF3 to the melt-spun ribbons prior to their hot consolidation in order to enhance the coercivity through a diffusion-based, partial substitution of the Nd by Dy. This is accomplished by applying extremely rapid, spark-plasma sintering to minimize any growth of the nanoscale Nd2Fe14B grains during consolidation. The result is a very high-coercivity magnet with drastically reduced amounts of heavy rare earths that is suitable for high-temperature applications. This work clearly demonstrates how rapidly formed, metastable states can provide us with properties that are unobtainable with conventional techniques.

FIELD DEPENDENCE OF THE SPIN REORIENTATION TEMPERATURE IN MICRO AND NANOCRYSTALLINE FORMS OF Nd{sub 2}Fe{sub 14}B.

DOE Office of Scientific and Technical Information (OSTI.GOV)

LEWIS,L.H.; HARLAND,C.L.

2002-08-18

Insight into the anisotropy behavior of Nd{sub 2}Fe{sub 14}B may be obtained by measurements of the spin reorientation temperature T{sub S} where the overall magnetocrystalline anisotropy changes to allow the magnetic moment to relax from an easy axis to an easy cone configuration. DC magnetization measurements made at various applied fields on sintered and nanocrystalline forms of Nd{sub 2}Fe{sub 14}B indicate a T{sub S} that remains constant for the sintered sample but is strongly field-dependent for the nanocrystalline forms of the material. Specifically, T{sub S} decreases with decreasing applied fields of strengths 5 T, 1 T and 0.01 T. Amore » simple model that minimizes the total energy of the system leads to the conclusion that the spin reorientation temperature is insensitive to applied field. Therefore it is concluded that the apparent decrease in the system's spin reorientation temperatures with decrease in measuring field can be attributed to the nanoscale structure of the system and a difference in the anisotropy constants compared to their bulk values.« less

The influence of Nd dopants on spin and orbital moments in Nd-doped permalloy thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Luo, Chen, E-mail: ronanluochen@gmail.com; Zhang, Wen, E-mail: xiaotur@gmail.com, E-mail: yazhai@seu.edu.cn; Zhai, Ya, E-mail: xiaotur@gmail.com, E-mail: yazhai@seu.edu.cn

2014-08-25

Magnetic properties of Nd{sub X}-Ni{sub 80}Fe{sub 20(1−X)} thin films have been investigated using x-ray absorption spectroscopy and x-ray magnetic circular dichroism (XMCD) at room temperature. With the Nd concentration increasing, the ratio of orbital-to-spin moment of Ni and Fe increases significantly, indicating that the spin-orbit coupling in permalloy thin films is enhanced due to the Nd impurities. The spin and orbital moments have been obtained by the sum rules analysis, which shows that the Nd impurities lead to a strong dispersion of spin moments of Fe and Ni while have no effect on orbital moments in Nd-doped permalloy thin films.more » Element-specific XMCD hysteresis loops suggest an antiferromagnetic coupling between the magnetic moments of Nd and permalloy at room temperature. The static magnetic properties have been studied by vibrating sample magnetometer for comparison, which shows a nice agreement with the XMCD results.« less

Recovery of rare earths from spent NdFeB magnets of wind turbine: Leaching and kinetic aspects.

PubMed

Kumari, Aarti; Sinha, Manish Kumar; Pramanik, Swati; Sahu, Sushanta Kumar

2018-05-01

Increasing demands of rare earth (RE) metals for advanced technological applications coupled with the scarcity of primary resources have led to the development of processes to treat secondary resources like scraps or end of life products that are often rich in such metals. Spent NdFeB magnet may serve as a potential source of rare earths containing around ∼30% of neodymium and other rare earths. In the present investigation, a pyro-hydrometallurgical process has been developed to recover rare earth elements (Nd, Pr and Dy) from the spent wind turbine magnet. The spent magnet is demagnetized and roasted at 1123 K to convert rare earths and iron to their respective oxides. Roasting of the magnet not only provides selectivity, but enhances the leaching efficiency also. The leaching of the roasted sample with 0.5 M hydrochloric acid at 368 K, 100 g/L pulp density and 500 rpm for 300 min selectively recovers the rare earth elements almost quantitatively leaving iron oxide in the residue. Leaching of rare earth elements with hydrochloric acid follows the mixed controlled kinetic model with activation energy (E a ) of 30.1 kJ/mol in the temperature range 348-368 K. The leaching mechanism is further established by characterizing the leach residues obtained at different time intervals by scanning electron microscopy- energy dispersive X-ray spectroscopy (SEM-EDS) and X-ray diffraction (XRD). Individual rare earth elements from the leach solution containing 16.8 g/L of Nd, 3.8 g/L Pr, 0.28 g/L of Dy and other minor impurity elements could be separated by solvent extraction. However, mixed rare earth oxide of 99% purity was produced by oxalate precipitation followed by roasting. The leach residue comprising of pure hematite has a potential to be used as pigment or can find other applications. Copyright © 2018 Elsevier Ltd. All rights reserved.

Effect of deformation ratios on grain alignment and magnetic properties of hot pressing/hot deformation Nd-Fe-B magnets

NASA Astrophysics Data System (ADS)

Guo, Zhaohui; Li, Mengyu; Wang, Junming; Jing, Zheng; Yue, Ming; Zhu, Minggang; Li, Wei

2018-05-01

The magnetic properties, microstructure and orientation degrees of hot pressing magnet and hot deformation Nd-Fe-B magnets with different deformation ratios have been investigated in this paper. The remanence (Br) and maximum magnetic energy product ((BH)max) were enhanced gradually with the deformation ratio increasing from 0% to 70%, whereas the coercivity (HCj) decreased. The scanning electron microscopy (SEM) images of fractured surfaces parallel to the pressure direction during hot deformation show that the grains tend to extend perpendicularly to the c-axes of Nd2Fe14B grains under the pressure, and the aspect ratios of the grains increase with the increase of deformation ratio. Besides, the compression stress induces the long axis of grains to rotate and the angle (θ) between c-axis and pressure direction decreases. The X-ray diffraction (XRD) patterns reveal that orientation degree improves with the increase of deformation ratio, agreeing well with the SEM results. The hot deformation magnet with a deformation ratio of 70% has the best Br and (BH)max, and the magnetic properties are as followed: Br=1.40 T, HCj=10.73 kOe, (BH)max=42.30 MGOe.

The effect of surface grain reversal on the AC losses of sintered Nd-Fe-B permanent magnets

NASA Astrophysics Data System (ADS)

Moore, Martina; Roth, Stefan; Gebert, Annett; Schultz, Ludwig; Gutfleisch, Oliver

2015-02-01

Sintered Nd-Fe-B magnets are exposed to AC magnetic fields in many applications, e.g. in permanent magnet electric motors. We have measured the AC losses of sintered Nd-Fe-B magnets in a closed circuit arrangement using AC fields with root mean square-values up to 80 mT (peak amplitude 113 mT) over the frequency range 50 to 1000 Hz. Two magnet grades with different dysprosium content were investigated. Around the remanence point the low grade material (1.7 wt% Dy) showed significant hysteresis losses; whereas the losses in the high grade material (8.9 wt% Dy) were dominated by classical eddy currents. Kerr microscopy images revealed that the hysteresis losses measured for the low grade magnet can be mainly ascribed to grains at the sample surface with multiple domains. This was further confirmed when the high grade material was subsequently exposed to DC and AC magnetic fields. Here a larger number of surface grains with multiple domains are also present once the step in the demagnetization curve attributed to the surface grain reversal is reached and a rise in the measured hysteresis losses is evident. If in the low grade material the operating point is slightly offset from the remanence point, such that zero field is not bypassed, its AC losses can also be fairly well described with classical eddy current theory.

Enhanced method of magnetic powder alignment for production of PLP Nd-Fe-B magnets

NASA Astrophysics Data System (ADS)

Popov, A. G.; Golovnia, O. A.; Protasov, A. V.

2017-04-01

It is demonstrated how the high degree of powder alignment in PLP magnets can be achieved by loading the powder into a container placed in a magnetic field of moderate strength. The strip-cast alloy with a composition of 30.00 Nd, 1.95 Dy, 66.42 Fe, 0.99 B, 0.54 Co, 0.1 Ga (wt%) was subjected to hydrogen decrepitation and then milled in a vibratory mill in toluene to an average particle size of 2.9 μm determined by the FSSS method. The powder was compacted in the magnetic field of 0.2 - 1.2 T to the filling density 2.6 - 3.2×103 kg/m3. It is shown that loading the powder into a container placed in a magnetic field enhances the degree of powder alignment in sintered Nd-Fe-B magnets produced from non-pressed powder. At the filling density less than 3.2×103 kg/m3, the density of magnets is high but insufficient, because of the formation of magnetostatic chains of particles, which impedes the powder compaction. The simulation by the discrete-element method qualitatively proves that the magnetostatic interaction of the chains of particles that are formed in the course of loading in the magnetic field stimulates a decrease in the density of the sintered magnets and its non-uniform distribution over the sample. As a result of the optimization of the parameters of the alignment and compaction of the powder loaded in a magnetic field, PLP magnets with Br ≥1.34 T, Hc ≥950 kA/m, (BH)max ≥340 kJ/m3, and the degree of alignment exceeding 96% were produced.

Magnetic properties and magnetostriction of PrxNd1-xFe1.9 (0 <= x <= 1.0) alloys at low temperature

NASA Astrophysics Data System (ADS)

Wang, Yong; Tang, Shao-Long; Li, Yu-Long; Xie, Ren; Du, You-Wei

2013-03-01

The crystal structure, magnetic and magnetostrictive properties of high-pressure synthesized PrxNd1-xFe1.9 (0 <= x <= 1.0) alloys were studied. The alloys exhibit single cubic Laves phase with MgCu2-type structure. The initial magnetization curve reveals that Pr0.2Nd0.8Fe1.9 has a minimum magnetocrystalline anisotropy at 5 K. The magnetostriction curve at 5 K shows that Pr0.2Nd0.8Fe1.9 has a very good low-field magnetostrictive property, and the magnetostriction of the PrxNd1-xFe1.9 alloy in high magnetic field is attributable mainly to Pr. The temperature dependence of the magnetostriction (λ‖) at the field of 5 kOe shows that the substitution of Nd reduces the K1 remarkably, and the values of λ‖ of Pr0.2Nd0.8Fe1.9 and Pr0.8Nd0.2Fe1.9 alloys are nearly five times larger than that of the PrFe1.9 alloy below 50 K; the λ‖ of Pr0.8Nd0.2Fe1.9 reaches up to 1082 ppm at 100 K, which makes it a potential candidate for application in this temperature range.

A combined experimental and finite element analysis method for the estimation of eddy-current loss in NdFeB magnets.

PubMed

Fratila, Radu; Benabou, Abdelkader; Tounzi, Abdelmounaïm; Mipo, Jean-Claude

2014-05-14

NdFeB permanent magnets (PMs) are widely used in high performance electrical machines, but their relatively high conductivity subjects them to eddy current losses that can lead to magnetization loss. The Finite Element (FE) method is generally used to quantify the eddy current loss of PMs, but it remains quite difficult to validate the accuracy of the results with complex devices. In this paper, an experimental test device is used in order to extract the eddy current losses that are then compared with those of a 3D FE model.

Interfacial magnetic coupling in hetero-structure of Fe/double-perovskite NdBaMn2O6 single crystal

NASA Astrophysics Data System (ADS)

Lin, W. C.; Tsai, C. L.; Ogawa, K.; Yamada, S.; Gandhi, Ashish C.; Lin, J. G.

2018-04-01

The interfacial magnetic coupling between metallic Fe and the double-perovskite NdBaMn2O6 single crystal was investigated in the heterostructure of 4-nm Pd/10-nm Fe/NdBaMn2O6. A considerable magnetic coupling effect was observed in the temperature range coincident with the magnetic phase transition of NdBaMn2O6. When the temperature was elevated above 270 K, NdBaMn2O6 transformed from a state of antiferromagnetic fluctuating domains to a superparamagnetism-like (ferromagnetic fluctuation) state with high magnetic susceptibility. Concurrently, the interfacial magnetic coupling between the Fe layer and the NdBaMn2O6 crystal was observed, as indicated by the considerable squareness reduction and coercivity enhancement in the Fe layer. Moreover, the presence of the Fe layer changed the magnetic structure of NdBaMn2O6 from conventional 4-fold symmetry to 2-fold symmetry. These observations offer applicable insights into the mutual magnetic interaction in the heterostructures of metallic ferromagnetism/perovskite materials.

Oxygen trapped by rare earth tetrahedral clusters in Nd4FeOS6: Crystal structure, electronic structure, and magnetic properties

NASA Astrophysics Data System (ADS)

Lin, Qisheng; Taufour, Valentin; Zhang, Yuemei; Wood, Max; Drtina, Thomas; Bud'ko, Sergey L.; Canfield, Paul C.; Miller, Gordon J.

2015-09-01

Single crystals of Nd4FeOS6 were grown from an Fe-S eutectic solution. Single crystal X-ray diffraction analysis revealed a Nd4MnOSe6-type structure (P63mc, a=9.2693(1) Å, c=6.6650(1)Å, V=495.94(1) Å3, Z=2), featuring parallel chains of face-sharing [FeS6×1/2]4- trigonal antiprisms and interlinked [Nd4OS3]4+ cubane-like clusters. Oxygen atoms were found to be trapped by Nd4 clusters in the [Nd4OS3]4+ chains. Structural differences among Nd4MnOSe6-type Nd4FeOS6 and the related La3CuSiS7- and Pr8CoGa3-type structures have been described. Magnetic susceptibility measurements on Nd4FeOS6 suggested the dominance of antiferromagnetic interactions at low temperature, but no magnetic ordering down to 2 K was observed. Spin-polarized electronic structure calculations revealed magnetic frustration with dominant antiferromagnetic interactions.

Coercivity enhancement of sintered Nd-Fe-B magnets by chemical bath deposition of TbCl{sub 3}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Guo, Shuai, E-mail: gshuai@nimte.ac.cn; Zhang, Xiaofeng; Ding, Guangfei

2014-05-07

The chemical bath deposition (CBD) and the grain boundary diffusion method were combined to diffuse the heavy rare earth for obtain the thick magnets with high coercivity and low heavy rare earth. The jet mill powders were soaked into the alcohol solution of 0.2 wt. % TbCl{sub 3}. A thin layer of TbCl{sub 3} was wrapped to the surface of (PrNd){sub 2}Fe{sub 14}B powder particles. The coercivity of magnet is increased from 11.89 kOe to 14.72 kOe without significant reduction of remanence after grain boundary diffusion in the sintering and the annealing processes. The temperature coefficients of the remanence and themore » coercivity are improved by the substitution of PrNd by Tb in the surface of grains. The highly accelerated temperature/humidity stress test (HAST) results indicate that the CBD magnet has poor corrosion resistance, attributing to the present of Cl atoms in the grain boundaries.« less

Investigation of the magnetic properties of Nd-Fe-B based hard magnetic materials

NASA Astrophysics Data System (ADS)

Grössinger, R.; Hilscher, G.; Kirchmayr, H.; Sassik, H.; Strnat, R.; Wiesinger, G.

1985-05-01

Nd-Fe-B type magnets were prepared by a melt spinning technique. The resulting ribbons were used as starting material for plastic bonded aligned powder magnets. The hard magnetic properties were studied in static fields up to 50 kG as well as in pulsed fields up to 150 kG. The coercivity measured on ribbons ( 1H' c) was found for high values to be larger than that obtained from the plastic bonded magnets ( 1Hc), which we attribute to the influence of the grinding procedure. The anisotropy field HA determined by applying the SPD (Singular Point Detection) technique, was found (for υ < 13 m/s) to depend strongly on the wheel velocity υ, however for velocities exceeding this value, HA remained essentially constant (∼ 75 kG). Mössbauer spectra were recorded at room as well as at liquid helium temperature. The different shape of the respective spectra reflects the change of the easy axis with temperature. A phase analysis performed by computer fitting the spectra showed that the amount of Fe-precipitates influences the formation of the coercivity.

Magneto-crystalline anisotropy of NdFe0.9Mn0.1O3 single crystal

NASA Astrophysics Data System (ADS)

Mihalik, Marián; Mihalik, Matúš; Zentková, Mária; Uhlířová, Klára; Kratochvílová, Marie; Roupcová, Pavla

2018-05-01

Our present study on oriented single crystal revealed huge magneto-crystalline anisotropy with respect to principal crystallographic axes, even several magnetic transitions were observed below TN = 748 K (c-axis) at 700 K (a-axis) as well 657 K (b-axis). The spin reorientation of magnetic moment takes place in very narrow temperature range between 135 K and 125 K and is attributed to vanishing of ferromagnetic component aligned along b-axis. Measurements of magnetic isotherms trace the development of ferromagnetic component and revealed the intermediate temperature range between 120 K and 20 K which is characterised by zero ferromagnetic components in any principal crystal direction. The ferromagnetic component develops consecutive at low temperature below 20 K along a-axis. Our study indicates completely different magnetic structure of NdFe0.9Mn0.1O3 below 135 K in comparison with NdFeO3.

Preparation and properties of isotropic Nd-Fe-B bonded magnets with sodium silicate binder

NASA Astrophysics Data System (ADS)

Liu, W. Q.; Hu, R. J.; Yue, M.; Yin, Y. X.; Zhang, D. T.

2017-08-01

In present study, sodium silicate, a kind of heat-resistant binder, was used to prepare bonded Nd-Fe-B magnets with improved thermal stability and mechanical strength. Effect of curing temperature and curing time of the new binder to the magnetic properties, microstructure, and mechanical strength of the magnets was systematically investigated. Fracture surface morphology observation show that sodium silicate in bonded magnets could completely be cured at 175 °C for 40 min, and the magnets prepared under this condition exhibit optimal properties. They exhibit usable magnetic properties of Br of 4.66 kGs, Hcj of 4.84 kOe, and (BH)max of 4.06 MGOe at 200 °C. Moreover, the magnets possess high compressive strength of 63 MPa.

Structure Evolution and Multiferroic Properties in Cobalt Doped Bi4NdTi3Fe1-xCoxO15-Bi3NdTi2Fe1-xCoxO12-δ Intergrowth Aurivillius Compounds

PubMed Central

Zhang, D. L.; Huang, W. C.; Chen, Z. W.; Zhao, W. B.; Feng, L.; Li, M.; Yin, Y. W.; Dong, S. N.; Li, X. G.

2017-01-01

Here, we report the structure evolution, magnetic and ferroelectric properties in Co-doped 4- and 3-layered intergrowth Aurivillius compounds Bi4NdTi3Fe1-xCoxO15-Bi3NdTi2Fe1-xCoxO12-δ. The compounds suffer a structure evolution from the parent 4-layered phase (Bi4NdTi3FeO15) to 3-layered phase (Bi3NdTi2CoO12-δ) with increasing cobalt doping level from 0 to 1. Meanwhile the remanent magnetization and polarization show opposite variation tendencies against the doping level, and the sample with x = 0.3 has the largest remanent magnetization and the smallest polarization. It is believed that the Co concentration dependent magnetic properties are related to the population of the Fe3+ -O-Co3+ bonds, while the suppressed ferroelectric polarization is due to the enhanced leakage current caused by the increasing Co concentration. Furthermore, the samples (x = 0.1–0.7) with ferromagnetism show magnetoelectric coupling effects at room temperature. The results indicate that it is an effective method to create new multiferroic materials through modifying natural superlattices. PMID:28272495

Coercivity enhancement of sintered Nd-Fe-B magnets by chemical bath deposition

NASA Astrophysics Data System (ADS)

Zhang, Qiushuang; Guo, Shuai; Yang, Xiao; Zeng, Jiling; Cao, Xuejing; Chen, Renjie; Yan, Aru

2018-05-01

The chemical bath deposition (CBD) method is used to diffuse the heavy rare earth element in order to obtain the high coercivity magnets with low heavy rare earth element. The jet mill powders are soaked in the alcohol suspension of Dy(CH3CHOHCH3)3 (Dy-ipa) so that Nd2Fe14B powder particles are surrounded by Dy-ipa homogeneously. By adding 1.0 wt. % Dy, the coercivity of magnet is increased from 14.47 kOe to 17.55 kOe with slight reduction of remanence after grain boundary diffusion (GBD) in the sintering and annealing processes. The temperature coefficient of coercivity optimizes from -0.629 %/°C to -0.605 %/°C as well as that of remanence improves from -0.108 %/°C to -0.100 %/°C. The CBD method is helpful for thermal stability and alignment either. The relation between the microstructure and the coercivity has been studied systematically.

Magnetic properties of Fe-Nd silica glass ceramics

NASA Astrophysics Data System (ADS)

Nayak, Manjunath T.; Desa, J. A. Erwin; Babu, P. D.

2018-04-01

Soda lime silica glass ceramics containing iron and neodymium have been synthesized. The XRD pattern revealed that the glass samples devitrified into multiple phases. Fe2O3 as an initial component converted into Fe3O4 in the sample during the synthesis, and was the main contributor to the magnetic property of the sample. The inclusion of Nd was found to enhance the magnetization of the sample at 5K. The coercivity of the sample increased with decrease in temperature from room to 5K.

LAND-deFeND - An innovative database structure for landslides and floods and their consequences.

PubMed

Napolitano, Elisabetta; Marchesini, Ivan; Salvati, Paola; Donnini, Marco; Bianchi, Cinzia; Guzzetti, Fausto

2018-02-01

Information on historical landslides and floods - collectively called "geo-hydrological hazards - is key to understand the complex dynamics of the events, to estimate the temporal and spatial frequency of damaging events, and to quantify their impact. A number of databases on geo-hydrological hazards and their consequences have been developed worldwide at different geographical and temporal scales. Of the few available database structures that can handle information on both landslides and floods some are outdated and others were not designed to store, organize, and manage information on single phenomena or on the type and monetary value of the damages and the remediation actions. Here, we present the LANDslides and Floods National Database (LAND-deFeND), a new database structure able to store, organize, and manage in a single digital structure spatial information collected from various sources with different accuracy. In designing LAND-deFeND, we defined four groups of entities, namely: nature-related, human-related, geospatial-related, and information-source-related entities that collectively can describe fully the geo-hydrological hazards and their consequences. In LAND-deFeND, the main entities are the nature-related entities, encompassing: (i) the "phenomenon", a single landslide or local inundation, (ii) the "event", which represent the ensemble of the inundations and/or landslides occurred in a conventional geographical area in a limited period, and (iii) the "trigger", which is the meteo-climatic or seismic cause (trigger) of the geo-hydrological hazards. LAND-deFeND maintains the relations between the nature-related entities and the human-related entities even where the information is missing partially. The physical model of the LAND-deFeND contains 32 tables, including nine input tables, 21 dictionary tables, and two association tables, and ten views, including specific views that make the database structure compliant with the EC INSPIRE and the Floods

Magnetic and morphological characterization of Nd2Fe14B magnets with different quality grades at low temperature 5-300 K

NASA Astrophysics Data System (ADS)

Diez-Jimenez, E.; Perez-Diaz, J. L.; Ferdeghini, C.; Canepa, F.; Bernini, C.; Cristache, C.; Sanchez-Garcia-Casarrubios, J.; Valiente-Blanco, I.; Ruiz-Navas, E. M.; Martínez-Rojas, J. A.

2018-04-01

An increasing number of cryogenic devices may benefit from the use of Nd2Fe14B permanent magnets. However, it is necessary to precisely know their behavior because magnetization varies significantly due to Spin Reorientation Transition. In this work, magnetic and morphological characterization of Nd2Fe14B commercial polycrystalline magnets with different quality grades from 5 to 300 K is provided. A set of magnets ranging from N35 to N52 quality have been analyzed. Mean grain dimension as well as material composition elements are provided. Higher quality magnets show smaller mean grain dimensions. Regarding cryogenic temperatures, the well know spin transition effect appears in all the magnets as expected, however, the transition temperature occurs at different temperatures in a range from 112 to 120 K which is lower than those obtained for single crystal samples. Moreover, the relative variation of the remanence from 300 to 5 K is lower than 4% while the maximum expected variation is in average 11%. As extra information, the same analyzes are provided for additional quality grades N40M, N40S, N40SH and N40UH.

Micromagnetic simulation of anisotropic grain boundary diffusion for sintered Nd-Fe-B magnets

NASA Astrophysics Data System (ADS)

Li, W.; Zhou, Q.; Zhao, L. Z.; Wang, Q. X.; Zhong, X. C.; Liu, Z. W.

2018-04-01

A systematic investigation on the anisotropic grain boundary diffusion in sintered Nd-Fe-B magnets is carried out by micromagnetic simulation. The results indicate that the critical reason for the anisotropic diffusion effect is not the difference in the amount of Dy diffused along different directions but the macroscopic demagnetizing field. The diffusion parallel to the easy axis from both pole surfaces of the magnet can increase the nucleation fields in the two major regions with large macroscopic demagnetizing fields, where the reverse domains can nucleate easily. As a consequence, the grain boundary diffusion along the directions parallel to the easy axis from two pole surfaces is more effective to improve the coercivity of the magnets than that along other directions. It is also found that, to enhance the coercivity, only a limited diffusion depth is required. The present result is in good agreement with the recent experimental findings.

Characterisation of the aqueous corrosion process in NdFeB melt spun ribbon and MQI bonded magnets

NASA Astrophysics Data System (ADS)

McCain, Stephen

A major factor limiting the use and longevity of rare earth based magnetic materials is their susceptibility to aqueous corrosion and associated detrimental effects upon the magnetic properties of the material. This process was investigated through a combination of exposure to simulated environmental conditions and hydrogen absorption/desorption studies (HADS) in conjunction with magnetic characterisation. This study utilises NdFeB MQP-B melt-spun ribbon manufactured by Magnequench, in the form of MQI bonded magnets and also in its unbonded state as MQ powder. Specifically, it was concerned with how effective a variety of bonding media (epoxy resin,PTFE, zinc) and surface coatings (PTFE, Qsil, zinc LPPS, Dex-Cool) were at limiting the impact of aqueous corrosion in MQI bonded magnets. To characterise the effect of hydrogen absorption upon the magnetic properties of the MQP-B, hydrogen uptake was induced followed by a series of outgassing heat treatments with subsequent magnetic characterisation accompanied by HADS techniques performed after each outgas. This allowed comparisons to be made between the effects of aqueous corrosion process and hydrogen absorption upon the magnetic properties of the alloy.. This study has clearly demonstrated the link between the abundance of environmental moisture and rate of Hci losses in MQI bonded magnets. In addition to this the key mechanism responsible for the degradation of magnetic properties has been identified. These losses have been attributed to the absorption of hydrogen generated by the dissociation of water in the presence of NdFeB during the aqueous corrosion process. It has been shown that the use of a bonding media that is impermeable to water can limit the effects of aqueous corrosion by limiting water access to the Magnequench particles (MQP) and also the positive effects of the use of suitable surface coatings has been shown to be effective for the same reason..

EFFECT OF PRE-ALLOYING CONDITION ON THE BULK AMORPHOUS ALLOY ND(60)FE(30)AL(10).

DOE Office of Scientific and Technical Information (OSTI.GOV)

OCONNOR,A.S.; LEWIS,L.H.; MCCALLUM,R.W.

Bulk metallic glasses are materials that require only modest cooling rates to obtain amorphous solids directly from the melt. Nd{sub 60}Fe{sub 30}Al{sub 10} has been reported to be a ferromagnetic bulk metallic glass that exhibits high coercivity, a combination unlike conventional Nd-based amorphous magnetic alloys. To clarify the relationship between short-range order and high coercivity in glassy Nd{sub 60}Fe{sub 30}Al{sub 10}, experiments were performed to verify the existence of a homogeneous liquid state prior to rapid solidification. Alloys were prepared by various pre-alloying routes and then melt-spun. Arc-melted alloys were prepared for melt spinning using three different protocols involving: (1)more » alloying all three elements at once, (2) forming a Nd-Fe alloy which was subsequently alloyed with Al, and (3) forming a Fe-Al alloy for subsequent alloying with Nd. XRD, DTA, and magnetic measurement data from the resultant ribbons indicate significant differences in both the glassy fraction and the crystalline phase present in the as-spun material. These observed differences are attributed to the presence of highly stable nanoscopic aluminide-and/or silicide-phases, or motes, present in the melt prior to solidification. These motes would affect the short-range order and coercivity of the resultant glassy state and are anticipated to provide heterogeneous nucleation sites for crystallization.« less

Ab initio calculation of electronic structure and magnetic properties of R2Fe14BNx (R = Pr,Nd)

NASA Astrophysics Data System (ADS)

Tian, Guang; Zha, Liang; Yang, Wenyun; Qiao, Guanyi; Wang, Changsheng; Yang, Yingchang; Yang, Jinbo

2018-05-01

The site preference of N atom for R2Fe14BNx (R= Pr, Nd) and the interstitial nitrogen effect on the magnetic properties have been studied by the first-principles method. It was found that the nitrogen is more likely to occupy the 4e site for Pr2Fe14BNx compound, while 4f site for Nd2Fe14BNx. When N atoms entering some specific crystal sites (such as 2a and 4f), the total magnetic moments of these compounds are not reduced, but slightly increased. Although the doping of N may reduce the total magnetic moments of some R2Fe14B compounds in the cases of optimal occupancy, the volumetric effect caused by N doping can still change the electron density distributions of Fe near the Fermi level, improving the magnetic ordering temperature of such compounds.

Effect of low-melting point phases on the microstructure and properties of spark plasma sintered and hot deformed Nd-Fe-B alloys

NASA Astrophysics Data System (ADS)

Zhang, Li; Wang, Meiyu; Yan, Xueliang; Lin, Ye; Shield, Jeffrey

2018-04-01

The effect of adding a low melting point Pr-Cu-Al alloy during spark plasma sintering of melt-spun Nd-Fe-B ribbons is investigated. Regions of coarse grains were reduced and overall grain refinement was observed after the addition of Pr68Cu25Al7, leading to an enhancement of coercivity from 12.7 kOe to 20.4 kOe. Hot deformation of the samples in the spark plasma sintering system resulted in the formation of platelet-like grains, producing crystallographic alignment and magnetic anisotropy. The hot deformation process improved the remanence and energy product but reduced the coercivity. The decrease of coercivity resulted from grain growth and aggregation of Pr and Nd elements at triple-junction phases.

Investigation of magnetization dynamics damping in Ni80Fe20/Nd-Cu bilayer at room temperature

NASA Astrophysics Data System (ADS)

Fan, Wei; Fu, Qiang; Qian, Qian; Chen, Qian; Liu, Wanling; Zhou, Xiaochao; Yuan, Honglei; Yue, Jinjin; Huang, Zhaocong; Jiang, Sheng; Kou, Zhaoxia; Zhai, Ya

2018-05-01

Focusing on the Ni80Fe20 (Py)/Nd-Cu bilayers, the magnetization dynamic damping from spin pumping effect is investigated systematically by doping itinerant Cu in rear earth metal Nd. Various Ta/Py/Nd1-xCux/Ta/Si films with x = 0%, 16%, 38%, 46% and 58% are prepared by magnetron sputtering. For every content of Cu, the thickness of Nd-Cu layer is changed from 1 nm to 32 nm. The damping coefficient increases with increasing the thickness of Nd-Cu layer, which shows the trend of the spin pumping behavior. Also, with increasing Cu concentration in the Nd-Cu layer, the damping coefficient decreases, implying that the spin-orbit coupling in Nd-Cu layer is indeed cut down by high itinerant of Cu dopants. It is interesting that the spin diffusion length (λSD) in the Nd-Cu layer for different Cu dopants is not found to increase monotonously.

Compaction and sintering behaviors of a Nd-Fe-B permanent magnet alloy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chin, T.; Hung, M.; Tsai, D.

1988-11-15

Extensive x-ray diffraction (XRD) and magnetic measurements were done on Nd/sub 15/ Fe/sub 77/ B/sub 8/ magnet alloy green compacts after cold isostatic pressing following a pulsed 2-T field (CIP) and die-pressing under a static 1.2-T perpendicular field (DP1) or parallel field (DP2), and on those after sintering. An alignment factor F, through the calculation of the integrated diffraction intensity ratio of the XRD patterns, was adopted as the effectiveness of magnetic alignment. At the green compact state, DP1 has the best alignment while CIP the worst. However, after sintering the alignment factor was such that CIP>DPI>DP2, the same ordermore » as the magnetic properties. Three mechanisms were proposed for the evolution of the alignment factor at different stages of sintering, i.e., that both the appearance of a liquid phase at low temperatures and preferred grain growth at high temperatures enhance F, while recrystallization at intermediate temperatures deteriorates F. CIP results in less-defect green compact, hence less recrystallization, leading to better resultant alignment« less

Studies on in situ magnetic alignment of bonded anisotropic Nd-Fe-B alloy powders

NASA Astrophysics Data System (ADS)

Nlebedim, I. C.; Ucar, Huseyin; Hatter, Christine B.; McCallum, R. W.; McCall, Scott K.; Kramer, M. J.; Paranthaman, M. Parans

2017-01-01

Considerations for achieving high degree of alignment in polymer bonded permanent magnets are presented via the results of a study on in situ magnetic alignment of anisotropic Nd-Fe-B magnet powders. Contributions from effect of the alignment temperature, alignment magnetic field and the properties of the polymer on the hard magnetic properties of the bonded magnet were considered. The thermo-rheological properties of the polymer and the response of the magnet powders to the applied magnetic field indicate that hard magnetic properties were optimized at an alignment temperature just above the melting temperature of the EVA co-polymer. This agrees with an observed correlation between the change in magnetization due to improved magnetic alignment of the anisotropic powders and the change in viscosity of the binder. Manufacturing cost can be minimized by identifying optimum alignment temperatures and magnetic field strengths.

Hyperfine fields of Fe in Nd2Fe14BandSm2Fe17N3

NASA Astrophysics Data System (ADS)

Akai, Hisazumi; Ogura, Masako

2015-03-01

High saturation magnetization of rare-earth magnets originates from Fe and the strong magnetic anisotropy stems from f-states of rare-earth elements such as Nd and Sm. Therefore the hyperfine fields of both Fe and rare-earth provide us with important pieces of information: Fe NMR enable us to detect site dependence of the local magnetic moment and magnetic anisotropy (Fe sites also contribute to the magnetic anisotropy) while rare-earth NQR directly give the information of electric field gradients (EFG) that are related to the shape of the f-electron cloud as well as the EFG produced by ligands. In this study we focus on the hyperfine fields of materials used as permanent magnets, Nd2Fe14BandSm2Fe17N3 from theoretical points of view. The detailed electronic structure together with the hyperfine interactions are discussed on the basis of the first-principles calculation. In particular, the relations between the observed hyperfine fields and the magnetic properties are studies in detail. The effects of doping of those materials by other elements such as Dy and the effects of N adding in Sm2Fe17N3 will be discussed. This work was supported by Elements Strategy Initiative Center for Magnetic Materials Project, the Ministry of Education, Culture, Sports, Science and Technology, Japan.

Charge Transport and Thermoelectric Properties of (Nd1- z Yb z ) y Fe4- x Co x Sb12 Skutterudites

NASA Astrophysics Data System (ADS)

Shin, Dong-Kil; Jang, Kyung-Wook; Choi, Soon-Mok; Lee, Soonil; Seo, Won-Seon; Kim, Il-Ho

2018-06-01

Partially double-filled (Nd1- z Yb z ) y Fe4- x Co x Sb12 ( z = 0.25, 0.75, y = 0.8, and x = 0, 0.5, 1.0) skutterudites were prepared by encapsulated melting, annealing, and hot pressing, and the effects of Nd/Yb partial double filling and Co charge compensation on the microstructure, charge transport, and thermoelectric properties were investigated. All the specimens were transformed to the skutterudite phase together with a few secondary phases such as FeSb2, but FeSb2 formation was suppressed on increasing Co content. Nd and Yb were successfully double-filled in the voids of the skutterudite lattice and Co was well substituted at Fe sites, as indicated by changes in the lattice constant with Nd/Yb filling and Fe/Co substitution. All the specimens showed p-type conduction and exhibited degenerate semiconductor characteristics at temperatures from 323 K to 823 K, and the charge transport properties depended on the filling ratio of Nd and Yb because of the difference between the valencies of Nd and Yb. The electrical conductivity decreased and the Seebeck coefficient increased owing to a decrease in the carrier concentration with increasing Co content. The lattice thermal conductivity decreased because phonon scattering was enhanced by Nd and Yb partial double filling, but partially double-filled specimens did not exhibit a further significant reduction in the lattice thermal conductivity compared with the completely double-filled specimens. A maximum ZT of 0.83 was obtained for (Nd0.75Yb0.25)0.8Fe3CoSb12 at 723 K.

Perspective for using Nd-Fe-B magnets as a tool for the improvement of the production and transportation of Vietnamese crude oil with high paraffin content

NASA Astrophysics Data System (ADS)

Tung, N. P.; Vinh, N. Q.; Phong, N. T. P.; Long, B. Q. K.; Hung, P. V.

2003-04-01

Controlling the paraffin deposition is one of the most serious and costly problems for high-paraffin crude-oil production and transportation. This holds especially for offshore, deep-water wells and pipelines, like in Vietnam. For finding solutions for these problems, a series of experiments has been performed in order to study the effects of a magnetic field on the rheology of two often produced crude oil samples, using the high and variable magnetic-flux density of a Nd-Fe-B magnet. The resulting changes in the essential characteristics of the magnetically treated (MT) crude oils, like form and size of the paraffin clusters as well as the rheology parameters, have definitely proved the possibility to use a Nd-Fe-B magnetic tool as an environmentally friendly and effective method to control the paraffin deposition in crude oils of Vietnam that have a high paraffin content.

{sup 75}As NMR study of the oriented pnictide superconducting compound NdFeAsO{sub 0.83}F{sub 0.17}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pahari, Bholanath

Magnetization and {sup 75}As nuclear magnetic resonance (NMR) measurements in the superconductor NdFeAsO{sub 0.83}F{sub 0.17} (T{sub C}~46 K) are performed in order to investigate the effect of the Nd 4f electrons in the superconducting property. The magnetization curve displays a Nd 4f moments generated Curie-Weiss signal in the field of 7 T. {sup 75}As NMR spectra in the oriented sample (H{sub 0}‖ab) are recorded at 7 T in the temperature range 10–300 K and temperature dependent {sup 75}As NMR shift, K{sub ab} has been obtained. The K{sub ab} curve shows a Curie-Weiss type contribution. The magnitude of hyperfine field, H{submore » hf} (4.4 kOe/μ{sub B}) estimated from the K{sub ab} vs χ plot indicates a non-negligible RKKY-type interaction between localized Nd 4f moments mediated by itinerant Fe 3d electrons.« less

Studies on in situ magnetic alignment of bonded anisotropic Nd-Fe-B alloy powders

DOE PAGES

Nlebedim, I. C.; Ucar, Huseyin; Hatter, Christine B.; ...

2016-08-30

We presented some considerations for achieving high degree of alignment in polymer bonded permanent magnets via the results of a study on in situ magnetic alignment of anisotropic Nd-Fe-B magnet powders. Contributions from effect of the alignment temperature, alignment magnetic field and the properties of the polymer on the hard magnetic properties of the bonded magnet were considered. Moreover, the thermo-rheological properties of the polymer and the response of the magnet powders to the applied magnetic field indicate that hard magnetic properties were optimized at an alignment temperature just above the melting temperature of the EVA co-polymer. This agrees withmore » an observed correlation between the change in magnetization due to improved magnetic alignment of the anisotropic powders and the change in viscosity of the binder. Finally, manufacturing cost can be minimized by identifying optimum alignment temperatures and magnetic field strengths.« less

Nanocrystalline NiNd0.01Fe1.99O4 as a gas sensor

NASA Astrophysics Data System (ADS)

Shinde, Tukaram J.; Gadkari, Ashok B.; Jadhav, Sarjerao R.; Kumar, Surender; Dalawai, Sanjeev P.; Vasambekar, Pramod N.

2015-06-01

Nanocrystalline NiNd0.01Fe1.99O4 has been synthesized by oxalate co-precipitation method and was characterized by X-ray diffraction technique. X-ray diffraction analysis confirms the formation of single phase cubic spinel structure. Crystallite size of the ferrite lies in the nano-particle range. The gas sensing properties of nanocrystalline ferrite were studied for gases like Cl2, LPG and C2H5OH. It was observed that NiNd0.01Fe1.99O4 is more sensitive towards chlorine followed by LPG at an operating temperature 277 °C compared to ethanol.

Chemical separation of Nd from geological samples for chronological studies using (146)Sm-(142)Nd and (147)Sm-(143)Nd systematics.

PubMed

Kagami, Saya; Yokoyama, Tetsuya

2016-09-21

Sm-Nd dating, which involves long-lived (147)Sm-(143)Nd and short-lived (146)Sm-(142)Nd systematics, has been widely used in the field of geosciences. To obtain precise and accurate ages of geological samples, the determination of highly precise Nd isotope ratios with nearly complete removal of Ce and Sm is indispensable to avoid mass spectral interference. In this study, we developed a three-step column chemistry procedure for separating Nd from geological samples that includes cation exchange chromatography for separating major elements from rare earth elements (REEs), oxidative extraction chromatography using Ln Resin coupled with HNO3 + KBrO3 for separating tetravalent Ce from the remaining REEs, and final purification of Nd using Ln Resin. This method enables high recovery of Nd (>91%) with effective separation of Nd from Ce and Sm (Ce/Nd < 1.2 × 10(-5) and Sm/Nd < 5.2 × 10(-6)). In addition, we devised a new method for determining Sm/Nd ratios with the isotope dilution inductively coupled plasma mass spectrometry method using (145)Nd- and (149)Sm-enriched spikes coupled with a group separation of REEs using TRU Resin. Applying the techniques developed in this study, we determined the Sm-Nd whole-rock isochron age of basaltic eucrites, yielding 4577 - 88(+ 55) Ma and 4558 ± 300 Ma for (146)Sm-(142)Nd and (147)Sm-(143)Nd systematics, respectively. Copyright © 2016 Elsevier B.V. All rights reserved.

Polydimethylsiloxane films doped with NdFeB powder: magnetic characterization and potential applications in biomedical engineering and microrobotics.

PubMed

Iacovacci, V; Lucarini, G; Innocenti, C; Comisso, N; Dario, P; Ricotti, L; Menciassi, A

2015-12-01

This work reports the fabrication, magnetic characterization and controlled navigation of film-shaped microrobots consisting of a polydimethylsiloxane-NdFeB powder composite material. The fabrication process relies on spin-coating deposition, powder orientation and permanent magnetization. Films with different powder concentrations (10 %, 30 %, 50 % and 70 % w/w) were fabricated and characterized in terms of magnetic properties and magnetic navigation performances (by exploiting an electromagnet-based platform). Standardized data are provided, thus enabling the exploitation of these composite materials in a wide range of applications, from MEMS/microrobot development to biomedical systems. Finally, the possibility to microfabricate free-standing polymeric structures and the biocompatibility of the proposed composite materials is demonstrated.

Effects of Molar Ratios and Sintering Times on Crystal Structures and Surface Morphology of Nd1+xFeO3 Oxide Alloy Prepared by using Solid Reaction Method

NASA Astrophysics Data System (ADS)

Sujiono, E. H.; Agus, J.; Samnur, S.; Triyana, K.

2018-05-01

The effects of molar ratios and sintering times on crystal structures and surface morphology on NdFeO3 oxide alloy have been studied. NdFeO3 oxide alloy formed by chemical preparation with solid reaction method using raw oxide Fe2O3 (99.9 %) and Nd2O3 (99.9 %) powders. In this article we reported the effects of molar ratios x = (–0.1, –0.2 and –0.3) and sintering times for 15 h and 20 h on crystal structures and surface morphology of Nd1+xFeO3 synthesized by solid-state reaction method. The results indicate that variation of molar ratio and sintering time has influenced the FWHM, crystalline size and grain size. The Nd1+xFeO3 have a major phase is NdFeO3, and other minor phases are Fe2O3, Nd2O3 and Nd(OH)3. The dominant intensity of hkl (121) with a value in FWHM, crystallite size, and grain size an indication the results will be applied as a gas sensor material as the focus of the further study.

Relevance of 4f-3d exchange to finite-temperature magnetism of rare-earth permanent magnets: An ab-initio-based spin model approach for NdFe{sub 12}N

DOE Office of Scientific and Technical Information (OSTI.GOV)

Matsumoto, Munehisa; Akai, Hisazumi; Doi, Shotaro

2016-06-07

A classical spin model derived ab initio for rare-earth-based permanent magnet compounds is presented. Our target compound, NdFe{sub 12}N, is a material that goes beyond today's champion magnet compound Nd{sub 2}Fe{sub 14}B in its intrinsic magnetic properties with a simpler crystal structure. Calculated temperature dependence of the magnetization and the anisotropy field agrees with the latest experimental results in the leading order. Having put the realistic observables under our numerical control, we propose that engineering 5d-electron-mediated indirect exchange coupling between 4f-electrons in Nd and 3d-electrons from Fe would most critically help enhance the material's utility over the operation-temperature range.

Electron doping effect on structural and magnetic phase transitions in Sr{sub 2-x}Nd{sub x}FeMoO{sub 6} double perovskites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Azad, A.K.; Eriksson, S.-G.; Khan, Abdullah

2006-05-15

Polycrystalline Sr{sub 2-x}Nd{sub x}FeMoO{sub 6} (x=0.0, 0.1, 0.2, 0.4) materials have been synthesized by a citrate co-precipitation method and studied by neutron powder diffraction (NPD) and magnetization measurements. Rietveld analysis of the temperature-dependent NPD data shows that the compounds (x=0.0, 0.1, 0.2) crystallize in the tetragonal symmetry in the range 10-400K and converts to cubic symmetry above 450K. The unit cell volume increases with increasing Nd{sup 3+} concentration, which is an electronic effect in order to change the valence state of the B-site cations. Antisite defects at the Fe-Mo sublattice increases with the Nd{sup 3+} doping. The Curie temperature wasmore » increased from 430K for x=0 to 443K for x=0.4. The magnetic moment of the Fe-site decreases while the Mo-site moment increases with electron doping. The antiferromagnetic arrangement causes the system to show a net ferrimagnetic moment.« less

Long-term product consistency test of simulated 90-19/Nd HLW glass

NASA Astrophysics Data System (ADS)

Gan, X. Y.; Zhang, Z. T.; Yuan, W. Y.; Wang, L.; Bai, Y.; Ma, H.

2011-01-01

Chemical durability of 90-19/Nd glass, a simulated high-level waste (HLW) glass in contact with the groundwater was investigated with a long-term product consistency test (PCT). Generally, it is difficult to observe the long term property of HLW glass due to the slow corrosion rate in a mild condition. In order to overcome this problem, increased contacting surface ( S/ V = 6000 m -1) and elevated temperature (150 °C) were employed to accelerate the glass corrosion evolution. The micro-morphological characteristics of the glass surface and the secondary minerals formed after the glass alteration were analyzed by SEM-EDS and XRD, and concentrations of elements in the leaching solution were determined by ICP-AES. In our experiments, two types of minerals, which have great impact on glass dissolution, were found to form on 90-19/Nd HLW glass surface when it was subjected to a long-term leaching in the groundwater. One is Mg-Fe-rich phyllosilicates with honeycomb structure; the other is aluminosilicates (zeolites). Mg and Fe in the leaching solution participated in the formation of phyllosilicates. The main components of phyllosilicates in alteration products of 90-19/Nd HLW glass are nontronite (Na 0.3Fe 2Si 4O 10(OH) 2·4H 2O) and montmorillonite (Ca 0.2(Al,Mg) 2Si 4O 10(OH) 2·4H 2O), and those of aluminosilicates are mordenite ((Na 2,K 2,Ca)Al 2Si 10O 24·7H 2O)) and clinoptilolite ((Na,K,Ca) 5Al 6Si 30O 72·18H 2O). Minerals like Ca(Mg)SO 4 and CaCO 3 with low solubility limits are prone to form precipitant on the glass surface. Appearance of the phyllosilicates and aluminosilicates result in the dissolution rate of 90-19/Nd HLW glass resumed, which is increased by several times over the stable rate. As further dissolution of the glass, both B and Na in the glass were found to leach out in borax form.

Reconstruction of the Nd isotope composition of seawater on epicontinental seas: Testing the potential of Fe-Mn oxyhydroxide coatings on foraminifera tests for deep-time investigations

NASA Astrophysics Data System (ADS)

Charbonnier, Guillaume; Pucéat, Emmanuelle; Bayon, Germain; Desmares, Delphine; Dera, Guillaume; Durlet, Christophe; Deconinck, Jean-François; Amédro, Francis; Gourlan, Alexandra T.; Pellenard, Pierre; Bomou, Brahimsamba

2012-12-01

The Fe-Mn oxide fraction leached from deep-sea sediments has been increasingly used to reconstruct the Nd isotope composition of deep water masses, that can be used to track changes in oceanic circulation with a high temporal resolution. Application of this archive to reconstruct the Nd isotope composition of bottom seawater in shallow shelf environments remained however to be tested. Yet as the Nd isotope composition of seawater on continental margins is particularly sensitive to changes in erosional inputs, establishment of neritic seawater Nd isotope evolution around areas of deep water formation would be useful to discriminate the influence of changes in oceanic circulation and in isotopic composition of erosional inputs on the Nd isotope record of deep waters. The purpose of this study is to test the potential of Fe-Mn coatings leached from foraminifera tests to reconstruct the Nd isotope composition of seawater in shelf environments for deep-time intervals. Albian to Turonian samples from two different outcrops have been recovered, from the Paris Basin (Wissant section, northern France) and from the Western Interior Seaway (Hot Spring, South Dakota, USA), that were deposited in epicontinental seas. Rare Earth Element (REE) spectra enriched in middle REEs in the foraminifera leach at Wissant highlight the presence of Fe-Mn oxides. The similarity of the Nd isotopic signal of the Fe-Mn oxide fraction leached from foraminifera tests with that of fish teeth suggests that Fe-Mn oxides coating foraminifera can be good archives of shelf bottom seawater Nd isotopic composition. Inferred bottom shelf water Nd isotope compositions at Wissant range from -8.5 to -9.7 ɛ-units, about 1.5-2 ɛ-units higher than that of the contemporaneous local detrital fraction. At Hot Spring, linear REE spectra characterizing foraminifera leach may point to an absence of authigenic marine Fe-Mn oxide formation in this area during the Late Cenomanian-Early Turonian, consistent with dysoxic

Delayed demagnetization jumps in (NdDy)(FeCo)B magnets in a steady-state magnetic field

NASA Astrophysics Data System (ADS)

L'vova, G. L.; Kirman, M. V.; Koplak, O. V.; Kucheryaev, V. V.; Valeev, R. A.; Piskorskii, V. P.; Morgunov, R. B.

2017-11-01

Spontaneous demagnetization jumps are observed in sintered magnets (Nd0.6Dy0.4)16(Fe0.77Co0.23)78B6 in a constant magnetic field after a sharp decrease in an external magnetic field from the value corresponding to the saturation to a value close to the coercive force. It is shown that the number of the magnetization jumps is proportional to their amplitudes. A low value of the autocorrelation coefficient between the jump amplitude and the time of its appearance ( R < 0.1) demonstrate the stochasticity of the jumps. It is found that the spectral jump density is independent of the frequency, i.e., a white magnetic noise is observed. The distribution of the magnetic field gradient has been obtained near the sample surface that makes it possible to distinguish domains and the grain magnetization in the dependence on the direction of the texturing of the sintered magnet.

Magnetic Properties of NdFe10Mo2-N Bonded Magnet

NASA Astrophysics Data System (ADS)

Zhang, Hong-Wei; Hu, Bo-Ping; Han, Zhong-Fan; Jin, Han-Min; Fu, Quan

1997-06-01

The dependence of remanence and coercivity on the magnetizing field is studied for isotropic and anisotropic epoxy resin bonded magnets. It was found that the coercivity of the NdFe10Mo2-N bonded magnet is mainly controlled by nucleation of reversed magnetic domains. Variation of iHc with Zn content and heat treatment conditions is studied. The value of 0 iHc obtained in the best Zn-bonded condition is about 0.15 T higher than before bonding. The variation of the amount of α-Fe with processing conditions is demonstrated for anisotropic Zn-bonded magnets.

The Sm-Nd history of KREEP. [in lunar rocks

NASA Technical Reports Server (NTRS)

Lugmair, G. W.; Carlson, R. W.

1978-01-01

Sm-Nd whole rock measurements on a variety of KREEP-rich samples from different landing sites are reported. Despite a variation of Nd and Sm concentrations of almost a factor of 3, the Sm-Nd ratios, as well as the Nd-143/Nd-144 values, show an extremely close grouping. No systematic differences between samples from different landing sites are resolved. These results are taken to be indicative of a moon-wide process having been responsible for the generation of the KREEP source reservoir, 4.36 plus or minus 0.06 AE ago, as estimated from model age calculation.

Nanocrystalline NiNd{sub 0.01}Fe{sub 1.99}O{sub 4} as a gas sensor

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shinde, Tukaram J., E-mail: pshindetj@yahoo.co.in; Gadkari, Ashok B.; Jadhav, Sarjerao R.

2015-06-24

Nanocrystalline NiNd{sub 0.01}Fe{sub 1.99}O{sub 4} has been synthesized by oxalate co-precipitation method and was characterized by X-ray diffraction technique. X-ray diffraction analysis confirms the formation of single phase cubic spinel structure. Crystallite size of the ferrite lies in the nano-particle range. The gas sensing properties of nanocrystalline ferrite were studied for gases like Cl{sub 2}, LPG and C{sub 2}H{sub 5}OH. It was observed that NiNd{sub 0.01}Fe{sub 1.99}O{sub 4} is more sensitive towards chlorine followed by LPG at an operating temperature 277 °C compared to ethanol.

Spectroscopic Properties of B2O3-PbO-Nd2O3 Glasses

NASA Astrophysics Data System (ADS)

Simon, V.; Ardelean, I.; Milea, I.; Peteanu, M.; Simon, S.

Samples belonging to xNd2O3(100-x) [2B2O3·PbO] glass system, with 0≤ x≤ 40 mol%, are investigated by IR and UV-VIS spectroscopies in order to obtain evidence for the influence of Nd2O3 on the local order from 2B2O3·PbO glass matrix. Besides the IR absorption bands characteristic to lead and boron arrangements, typical absorption lines of Nd3+ ions around 4000 cm-1 and 6000 cm-1 are recorded. The 6000 cm-1 band appears only for the samples with x≥25 mol% Nd2O3. The split of some UV-VIS absorption bands arising from transitions of neodymium ions in doublet lines as well as the shift of the absorption bands as the Nd2O3 content increases denote the influence of the lead-borate matrix on the radiative transitions of the lanthanide ion.

Effects of annealing process on magnetic properties and structures of Nd-Pr-Ce-Fe-B melt-spun powders

NASA Astrophysics Data System (ADS)

Pei, Kun; Lin, Min; Yan, Aru; Zhang, Xing

2016-05-01

The effects of annealing process on magnetic properties and structures of Nd-Pr-Ce-Fe-B melt-spun powders have been investigated. The magnetic properties improve a lot when the annealing temperature is 590-650 °C and the annealing time exceeds 1 min. The magnetic properties is stable when the annealing time is 590-650 °C. The powders contains obvious grains when the annealing time is only 1 min, while the grains grow up obviously, leading to the decrease of Br and (BH)max, when the annealing time is more than 9 min. The Hcj changes little for different annealing time. The cooling rate also affects the magnetic properties of powders with different Ce-content. Faster cooling rate is favorable to improve magnetic properties with low Ce-content powders, while high Ce-content powders need slower cooling rate.

Thermopower of CexR1-xB6 (R=La, Pr and Nd)

NASA Astrophysics Data System (ADS)

Kim, Moo‑Sung; Nakai, Yuki; Tou, Hideki; Sera, Masafumi; Iga, Fumitoshi; Takabatake, Toshiro; Kunii, Satoru

2006-06-01

The thermopower, S, of CexR1-xB6 (R=La, Pr, Nd) was investigated. S with a positive sign shows a typical behavior observed in the Ce Kondo system, an increase with decreasing temperature at high temperatures and a maximum at low temperatures. The S values of all the systems at high temperatures are roughly linearly dependent on the Ce concentration, indicating the conservation of the single-impurity character of the Kondo effect in a wide x range. However, the maximum value of S, Smax, and the temperature, Tmax, at which Smax is observed exhibit different x dependences between CexLa1-xB6 and CexR1-xB6 (R=Pr, Nd). In CexLa1-xB6, Tmax, which is ˜8 K in CeB6, decreases with decreasing x and converges to ˜1 K in a very dilute alloy and Smax shows an increase below x ˜ 0.1 after decreasing with decreasing x. In CexR1-xB6 (R=Pr, Nd), Tmax shows a weak x dependence but Smax shows a roughly linear decrease in x. These results are discussed from the standpoint of the chemical pressure effect and the Ce-Ce interaction. S in the long-range ordered phase shows very different behaviors between CexPr1-xB6 and CexNd1-xB6.

Preparation and characterization of polystyrene/neodymium hydroxide (PS/Nd(OH)3) nano-composites

NASA Astrophysics Data System (ADS)

Alsewailem, Fares D.; Bagabas, Abdulaziz A.; Binkhodor, Yazeed A.

2018-03-01

Composites of polystyrene and Neodymium hydroxide nanrods (PS/Nd(OH)3) were formulated and characterized in this study. Cetyl (1-hexadccyl) trimethyl ammonium bromide (CTAB) was used as dispersion agent for the Nd(OH)3 rods in the PS matrix. PS/Nd(OH)3 composites were prepared by solution and melt compounding. Morphological, thermal, and mechanical properties of the prepared composites were investigated. CTAB was found to be more effective as dispersion agent in composites prepared by solution compounding in comparison with those prepared by melt compounding, and that was due to the mild conditions used in solution compounding. Nonetheless, impact strength of the composite at 0.5 wt% Nd(OH)3 was drastically reduced in the absence of CTAB. Both tensile and impact strengths were found to greatly decreased at higher loading of Nd(OH)3, e.g. 5 wt%, even with the use of CTAB. Thermal stability of the PS/Nd(OH)3 composites was noticeably increased at relatively low loading of Nd(OH)3, e.g. 0.5 wt%.

Recycling and Mantle Stirring Determined by 142Nd/144Nd Isotopic Ratios

NASA Astrophysics Data System (ADS)

Jacobsen, S. B.; Ranen, M. C.

2004-12-01

It is now well established that 146Sm was live in the early solar system with an initial uniform 146Sm/144Sm ratio of ~0.008. Harper and Jacobsen (1992) discovered that a sample from Isua (~3.8 Ga old) had a positive 142Nd/144Nd anomaly of 33 ppm when compared to normal terrestrial and chondritic Nd. Furthermore, Jacobsen and Harper (1996) reported results from other Isua as well as Acasta (~4 Ga old) samples. Three other Isua samples had a possible small range (about -15 to +15), while two Acasta samples had no anomalies (normal to within 5 ppm). The presence of 142Nd anomalies at Isua has recently been confirmed by two other groups (Boyet et al. 2003; Caro et al. 2003). The available data demonstrate both the existence of early depleted mantle and that the early mantle was isotopically heterogeneous. As discussed by Jacobsen and Harper (1996), the recycling rate can be determined by tracing the decay of the average 142Nd/144Nd value of the depleted mantle. In addition, by using the 142Nd/144Nd heterogeneity in the depleted mantle through time we can determine the stirring rate of the mantle (Kellogg, Jacobsen and O'Connell, 2002) as a function of time. For this project our goal is to obtain a resolution in 142Nd/144Nd measurements of ~1 ppm. We have thus compared results obtained for the Nd isotope composition and 142Nd enriched standards for three different TIMS instruments: The Finnigan MAT 262 at Harvard, the Isoprobe-T and Finnigan TRITON mass spectrometers in GV Instrument's and Thermo Electron's demo laboratories in Manchester and Bremen, respectively. The Finnigan TRITON was designed in response to a request from the senior author for such an instrument. The results obtained so far demonstrate that all three instruments yield the same 142Nd/144Nd, 143Nd/144Nd and 145Nd/144Nd isotopic ratios to within a few ppm, while 148Nd/144Nd and 150Nd/144Nd ratios agree to within 10-20 ppm, when all ratios are normalized to 146Nd/144Nd using the exponential law. Due to

High Precision 142Nd/144Nd and 143Nd/144Nd Isotope Ratio Measurements in Rock Samples

NASA Astrophysics Data System (ADS)

Ali, A.; Srinivasan, G.

2009-05-01

The long-lived 147Sm-143Nd system with a half-life (T1/2) of 106 Gyr is generally used for geochronology. The short-lived 146Sm-142Nd system (T1/2= 103 Myr) is used as a geological tracer to track early (˜500 Ma) silicate differentiation [1] events in different planetary bodies. The isotope composition measurements by thermal ionization mass spectrometry (TIMS) require purification of Nd using chemical separation methods. This is important as an impure sample will give both a very poor ion yield and cause beam instability in the mass spectrometer, potentially resulting in a poor analysis [2]. The separation of Nd for 143Nd isotope measurement is, fairly straightforward because there is no isobaric interference of any other REE. While 142Nd isotope analysis needs chemically separated Nd fraction to be ˜100% Ce-free as latter is composed of a substantial amount of 142Ce isotope. A 4-steps technique, modified from Caro et al., [3], for the separation of Nd is established at the Cosmochemistry Laboratory of University of Toronto, Canada and applied to the measurement of Nd isotope ratios in geological reference sample BCR-2 (USGS, Columbia River basalt) using TIMS. Results of the isotopic ratios obtained for BCR-2 are in good agreement with published values [e.g., 4]. Analytical work on the samples discovered as the oldest rocks on Earth [5] from Nuvvuagittuq greenstone belt in Québec, Canada and various meteorites is in progress. An account of the procedures involved is briefly described here. All working solutions and acids were prepared using >18.2 MΩ.cm-1 H2O from a Milli-Q water system. Experiments were performed under Class 100 clean work bench with acid-cleaned apparatus and plastic-ware. The whole rock powders were weighed (20-30 mg) and dissolved in a mixture of HF and HNO3 using PFA vials and heated at 110°C. Further decomposition was done in Teflon bomb in the oven at 205°C. Later on contents of the Teflon bomb were transferred to vials and fluorides

Synthesis, structures and magnetic properties of Pr-lean Pr2Fe14B/Fe3B nanocomposite alloys

NASA Astrophysics Data System (ADS)

Mingxiang, Pan; Pengyue, Zhang; Hongliang, Ge; Hangfu, Yang; Qiong, Wu

2012-09-01

The lean rare-earth Pr4.5Fe77-xTixB18.5 (x=0, 1, 4, 5) nanocomposite alloys were prepared by melt spinning method and subsequent thermal annealing. The effect of Ti content and annealing temperature on the magnetic properties and the microstructure of these magnets were investigated. The enhancing coercivity Hc from 211.4 to 338.2 kA/m has been observed at the optimal annealing temperature of 700 °C by the addition of 5 at% Ti in Pr2Fe14B/Fe3B alloys. It was also found that increasing Ti content leads to marked grain refinement in the annealed alloys, resulting in strong exchange-coupling interaction between the hard and the soft phases in these ribbons. In addition, the magnetization reversal behaviors of Pr2Fe14B/Fe3B nanocomposites were discussed in detail.

Structural and Magnetic Properties Evolution of Co-Nd Substituted M-type Hexagonal Strontium Ferrites Synthesized by Ball-Milling-Assisted Ceramic Process

NASA Astrophysics Data System (ADS)

Chen, Wen; Wu, Wenwei; Zhou, Chong; Zhou, Shifang; Li, Miaoyu; Ning, Yu

2018-03-01

M-type hexagonal Sr1- x Co x Nd x Fe12- x O19 ( x = 0, 0.08, 0.16, and 0.24) has been synthesized by ball milling, followed by calcination in air. The calcined products have been characterized by x-ray powder diffraction (XRD), scanning electron microscopy (SEM), Fourier transform infrared spectra, and vibrating sample magnetometry. XRD and SEM analyses confirm the formation of M-type Sr hexaferrite with platelet-like morphology when Sr1- x Co x Nd x Fe12- x O19 ( x = 0, 0.08, 0.16, and 0.24) precursors are calcined at 950°C in air for 2.5 h. Lattice parameters " a" and " c" values of Sr1- x Co x Nd x Fe12- x O19 reflect a very small variation after doping of Nd3+ and Co2+ ions. Average crystallite size of Sr1- x Co x Nd x Fe12- x O19 sample, calcined at 1150°C, decreased obviously after doping of Co2+ and Nd3+ ions. This is because the bond energy of Nd3+-O2- is much larger than that of Sr2+-O2-. Magnetic characterization indicates that all the samples exhibit good magnetic properties. Substitution of Sr2+ and Fe3+ ions by Nd3+ and Co2+ ions can improve the specific saturation magnetizations and remanence of Sr1- x Co x Nd x Fe12- x O19. Sr0.84Co0.16Nd0.16Fe11.84O19, calcined at 1050°C, has the highest specific saturation magnetization value (74.75 ± 0.60 emu/g), remanence (45.15 ± 0.32 emu/g), and magnetic moment (14.34 ± 0.11 μ B); SrFe12O19, calcined at 1150°C, has the highest coercivity value (4037.01 ± 42.39 Oe). These magnetic parameters make this material a promising candidate for applications such as high-density magnetic recording and microwave absorbing materials.

The Effect of Molar Ratio on Crystal Structure and Morphology of Nd1+XFeO3 (X=0.1, 0.2, and 0.3) Oxide Alloy Material Synthesized by Solid State Reaction Method

NASA Astrophysics Data System (ADS)

Zharvan, V.; Kamaruddin, Y. N. I.; Samnur, S.; Sujiono, E. H.

2017-05-01

Perovskite is an oxide alloy which has a structure of ABO3 (A = La, Nd, Sm, Gd; B = Fe, CO, Ni) and has an excellent catalytic activity and gas-sensitive properties. NdFeO3 and its derivatives are important candidates for gas sensors. In this study, the effect of molar ratio (x=0.1, 0.2 and 0.3) on crystal structure and morphology of Nd1+xFeO3 synthesized by solid state reaction method has been studied. Nd1+xFeO3 samples were prepared using Nd2O3 (99.99 %) and Fe2O3 (99.99 %) as precursors. All of the samples were characterized using XRD to identify the phase and using SEM to identify the morphology. The synthesized Nd1+xFeO3 samples showed that molar ratio strongly influences the intensity, FWHM, and crystalline size. The samples of Nd1+xFeO3 have homogenous morphology and have three major phases, i.e. NdFeO3, Nd(OH)3 and Nd2O3 with crystalline sizes of NdFeO3 of 137.0±0.1 nm, 152.2±0.1 nm and 137.0±0.1 nm for Nd1.1FeO3, Nd1.2FeO3, and Nd1.3FeO3, respectively. These results indicated that the sample of Nd1.2FeO3 was a good candidate for a gas sensor material.

Modeling of magnetic hystereses in soft MREs filled with NdFeB particles

NASA Astrophysics Data System (ADS)

Kalina, K. A.; Brummund, J.; Metsch, P.; Kästner, M.; Borin, D. Yu; Linke, J. M.; Odenbach, S.

2017-10-01

Herein, we investigate the structure-property relationships of soft magnetorheological elastomers (MREs) filled with remanently magnetizable particles. The study is motivated from experimental results which indicate a large difference between the magnetization loops of soft MREs filled with NdFeB particles and the loops of such particles embedded in a comparatively stiff matrix, e.g. an epoxy resin. We present a microscale model for MREs based on a general continuum formulation of the magnetomechanical boundary value problem which is valid for finite strains. In particular, we develop an energetically consistent constitutive model for the hysteretic magnetization behavior of the magnetically hard particles. The microstructure is discretized and the problem is solved numerically in terms of a coupled nonlinear finite element approach. Since the local magnetic and mechanical fields are resolved explicitly inside the heterogeneous microstructure of the MRE, our model also accounts for interactions of particles close to each other. In order to connect the microscopic fields to effective macroscopic quantities of the MRE, a suitable computational homogenization scheme is used. Based on this modeling approach, it is demonstrated that the observable macroscopic behavior of the considered MREs results from the rotation of the embedded particles. Furthermore, the performed numerical simulations indicate that the reversion of the sample’s magnetization occurs due to a combination of particle rotations and internal domain conversion processes. All of our simulation results obtained for such materials are in a good qualitative agreement with the experiments.

Large magnetic response in (Bi4Nd)Ti3(Fe0.5Co0.5)O15 ceramic at room-temperature

NASA Astrophysics Data System (ADS)

Yang, F. J.; Su, P.; Wei, C.; Chen, X. Q.; Yang, C. P.; Cao, W. Q.

2011-12-01

Ceramics of Nd/Co co-substituted Bi5Ti3FeO15, i.e., (Bi4Nd)Ti3(Fe0.5Co0.5)O15 were prepared by the conventional solid-state reaction method. The X-ray diffraction pattern demonstrates that the sample of the layered perovskite phase was successfully obtained, even if little Bi-deficient pyrochlore Bi2Ti2O7 also existed. The ferroelectric and magnetic Curie temperatures were determined to be 1077 K and 497 K, respectively. The multiferroic property of the sample at room temperature was demonstrated by ferroelectric and magnetic measurements. Remarkably, by Nd/Co co-substituting, the sample exhibited large magnetic response with 2Mr = 330 memu/g and 2Hc = 562 Oe at applied magnetic field of 8 kOe at room temperature. The present work suggests the possibility of doped Bi5Ti3FeO15 as a potential multiferroic.

Single-vortex pinning and penetration depth in superconducting NdFeAsO 1-xF x

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Jessie T.; Kim, Jeehoon; Huefner, Magdalena

2015-10-12

We use a magnetic force microscope (MFM) to investigate single vortex pinning and penetration depth in NdFeAsO 1-xF x, one of the highest-T c iron-based superconductors. In fields up to 20 Gauss, we observe a disordered vortex arrangement, implying that the pinning forces are stronger than the vortex-vortex interactions. We measure the typical force to depin a single vortex, F depin ≃ 4.5 pN, corresponding to a critical current up to J c ≃ 7×10 5 A/cm 2. As a result, our MFM measurements allow the first local and absolute determination of the superconducting in-plane penetration depth in NdFeAsO 1-xFmore » x, λ ab = 320 ± 60 nm, which is larger than previous bulk measurements.« less

Phase Equilibria, Crystal Structure and Hydriding/Dehydriding Mechanism of Nd4Mg80Ni8 Compound

PubMed Central

Luo, Qun; Gu, Qin-Fen; Zhang, Jie-Yu; Chen, Shuang-Lin; Chou, Kuo-Chih; Li, Qian

2015-01-01

In order to find out the optimal composition of novel Nd-Mg-Ni alloys for hydrogen storage, the isothermal section of Nd-Mg-Ni system at 400 °C is established by examining the equilibrated alloys. A new ternary compound Nd4Mg80Ni8 is discovered in the Mg-rich corner. It has the crystal structure of space group I41/amd with lattice parameters of a = b = 11.2743(1) Å and c = 15.9170(2) Å, characterized by the synchrotron powder X-ray diffraction (SR-PXRD). High-resolution transmission electron microscopy (HR-TEM) is used to investigate the microstructure of Nd4Mg80Ni8 and its hydrogen-induced microstructure evolution. The hydrogenation leads to Nd4Mg80Ni8 decomposing into NdH2.61-MgH2-Mg2NiH0.3 nanocomposites, where the high density phase boundaries provide a great deal of hydrogen atoms diffusion channels and nucleation sites of hydrides, which greatly enhances the hydriding/dehydriding (H/D) properties. The Nd4Mg80Ni8 exhibits a good cycle ability. The kinetic mechanisms of H/D reactions are studied by Real Physical Picture (RPP) model. The rate controlling steps are diffusion for hydriding reaction in the temperature range of 100 ~ 350 °C and surface penetration for dehydriding reaction at 291 ~ 347 °C. In-situ SR-PXRD results reveal the phase transformations of Mg to MgH2 and Mg2Ni to Mg2NiH4 as functions of hydrogen pressure and hydriding time. PMID:26471964

Submicron R2Fe14B particles

NASA Astrophysics Data System (ADS)

Koylu-Alkan, O.; Barandiaran, J. M.; Salazar, D.; Hadjipanayis, G. C.

2016-05-01

Mechanochemical synthesis of submicron R2Fe14B particles with R = Dy, Nd, Pr has been performed successfully via high energy ball milling of rare-earth oxides, iron oxide and boron oxide in the presence of a reducing agent (Ca) and a dispersant material (CaO), followed by annealing at 800 - 900 °C. In the R = Nd system, we were able to fabricate particles embedded in a CaO matrix with coercivity (Hc) of 10.3 kOe after annealing at 900 °C for 5 min. After washing off the dispersant, the Hc was decreased to below 1 kOe because of hydrogen absorption that leads to the formation of the hydrated R2Fe14BHx phase that has a lower anisotropy. Upon removal of the hydrogen the coercivity was increased to 3.3 kOe. The average size of the Nd2Fe14B particles increases from 100 nm in a sample synthesized at 800 °C to 158 nm at 900 °C. The isotropic Dy2Fe14B particles showed a higher coercivity of 21 kOe in washed samples after annealing at 900 °C for 5 min. An average size of 71 nm is measured in samples synthesized at 800 °C and 107 nm at 900 °C. Fitting the high field M(H) measurements in Nd2Fe14B to the law of approach to saturation gave values for the magnetocrystalline anisotropy for the washed sample 2.23 × 107 erg/cm3 and for the vacuum annealed sample 4.15 × 107 erg/cm3, both of which are lower than the bulk values. This would explain the lower values of Hc observed in the particles.

Exogenous attention enhances 2nd-order contrast sensitivity

PubMed Central

Barbot, Antoine; Landy, Michael S.; Carrasco, Marisa

2011-01-01

Natural scenes contain a rich variety of contours that the visual system extracts to segregrate the retinal image into perceptually coherent regions. Covert spatial attention helps extract contours by enhancing contrast sensitivity for 1st-order, luminance-defined patterns at attended locations, while reducing sensitivity at unattended locations, relative to neutral attention allocation. However, humans are also sensitive to 2nd-order patterns such as spatial variations of texture, which are predominant in natural scenes and cannot be detected by linear mechanisms. We assess whether and how exogenous attention—the involuntary and transient capture of spatial attention—affects the contrast sensitivity of channels sensitive to 2nd-order, texture-defined patterns. Using 2nd-order, texture-defined stimuli, we demonstrate that exogenous attention increases 2nd-order contrast sensitivity at the attended location, while decreasing it at unattended locations, relative to a neutral condition. By manipulating both 1st- and 2nd-order spatial frequency, we find that the effects of attention depend both on 2nd-order spatial frequency of the stimulus and the observer’s 2nd-order spatial resolution at the target location. At parafoveal locations, attention enhances 2nd-order contrast sensitivity to high, but not to low 2nd-order spatial frequencies; at peripheral locations attention also enhances sensitivity to low 2nd-order spatial frequencies. Control experiments rule out the possibility that these effects might be due to an increase in contrast sensitivity at the 1st-order stage of visual processing. Thus, exogenous attention affects 2nd-order contrast sensitivity at both attended and unattended locations. PMID:21356228

Achievement of high coercivity in sintered R-Fe-B magnets based on misch-metal by dual alloy method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Niu, E, E-mail: niue@aphy.iphy.ac.cn; Wang, Zhen-Xi; Beijing Zhong Ke San Huan Research, No.10 Chuangxin Road, Changping District, Beijing 102200

2014-03-21

The R-Fe-B (R, rare earth) sintered magnets prepared with different ratio of alloys of MM-Fe-B (MM, misch-metal) and Nd-Fe-B by dual alloy method were investigated. As expected, the high ratio of MM-Fe-B alloy degrades the hard magnetic properties heavily with intrinsic coercivity lower than 5 kOe. When the atomic ratio MM/R ≤ 21.5% the magnetic properties can reach a practical level of B{sub r} ≥ 12.1 kGs, H{sub cj} ≥ 10.7 kOe, and (BH){sub max} ≥ 34.0 MGOe. And the effect of H{sub cj} enhancement by the grain boundary diffusion process is obvious when MM/R ≤ 21.5%. It is revealed that the decrement of intrinsic magnetic properties of R{sub 2}Fe{submore » 14}B matrix phase is not the main reason of the degradation of the magnets with high MM ratio. The change of deteriorated microstructure together with phase component plays fundamental roles in low H{sub cj}. In high MM ratio magnets, (a) after annealing, Ce atoms inside main phase are inclined to be segregated in the outer layer of the main phase grains; (b) there is no thin layer of Ce-rich phase as an analogue of Nd-rich phase to separate main phase grains; (c) excessive Ce tends to form CeFe{sub 2} grains.« less

Genetic diversities of MT-ND1 and MT-ND2 genes are associated with high-altitude adaptation in yak.

PubMed

Shi, Yu; Hu, Yongsong; Wang, Jie; Elzo, Mauricio A; Yang, Xue; Lai, Songjia

2018-04-01

Tibetan yak (Bos grunniens) inhabiting the Qinghai-Tibet Plateau (QTP) where the average altitude is 4000 m, is specially adapted to live at these altitudes. Conversely, cattle (B. taurus) has been found to suffer from high-altitude hypertension or heart failure when exposed to these high altitudes. Two mitochondrial genes, MT-ND1 and MT-ND2, encode two subunits of NADH dehydrogenase play an essential role in the electron transport chain of oxidative phosphorylation (OXPHOS). We sequenced these two mitochondrial genes in two bovine groups (70 Tibetan yaks and 70 Xuanhan cattle) and downloaded 300 sequences of B. taurus (cattle), 93 sequences of B. grunniens (domestic yak), and 2 sequences of B. mutus (wild yak) from NCBI to increase our understanding of the mechanisms of adaptability to hypoxia at high altitudes in yaks compared to cattle. MT-ND1 SNP m.3907 C > T, present in all Tibetan yaks, was positively associated with high-altitude adaptation (p < .0006). Specially, mutation m.3638 A > G present in all cattle, resulting in the termination of transcription, was negatively associated with high-altitude adaptation (p < .0006). Additionally, MT-ND2 SNPs m.4351 G > A and m.5218 C > T also showed positive associations with high-altitude adaptation (p < .0004). MT-ND1 haplotypes H2, H3, H4, H6, and H7 showed positive associations but haplotype H20 had a negative association with high-altitude adaptation (p < .0008). Similarly, MT-ND2 haplotypes Ha1 Ha8, Ha10, and Ha11 were positively associated whereas haplotype Ha2 was negatively associated with adaptability to high-altitudes (p < .0008). Thus, MT-ND1 and MT-ND2 can be considered as candidate genes associated with adaptation to high-altitude environments.

Clean to dirty limit and T c suppression in NdFeAsO0.7F0.3 studied by H c2 analysis

NASA Astrophysics Data System (ADS)

Pallecchi, I.; Tarantini, C.; Shen, Y.; Singh, R. K.; Newman, N.; Cheng, P.; Jia, Y.; Wen, H.-H.; Putti, M.

2018-07-01

In this work, we investigate the temperature dependence of the upper critical field, dH c2/dT, in an increasingly disordered NdFeAsO0.7F0.3 (NdFeAs(O,F)) single crystal that has been progressively irradiated up to a 5.25 × 1016 cm- 2 total α-particle dose. For the H∣∣ab-plane, dH c2/dT does not vary remarkably with irradiation, while for the H∣∣c-axis it increases sharply after the first irradiation of 3.60 × 1015 cm-2 and then more gradually with further irradiation doses. Focusing on the H∣∣c-axis, we develop a phenomenological analysis of the H c2 slope which allows us to inspect the crossover from the clean to the dirty regime. From the H c2 slope normalized to the critical temperature and to its clean limit value, we extract the ratio of the coherence length ξ BCS to the mean free path {\\ell } and we find that when T c is reduced by a factor of four from its pristine value, ξ BCS/{\\ell } becomes as large as ˜7 and {\\ell } reaches values of ˜1.8 nm, indicating that NdFeAs(O,F) is well into the dirty regime. Our analysis of the H c2 slope also allows us to compare the pair-breaking effectiveness of scattering in different superconductors, showing similarity between unconventional NdFeAs(O,F) and moderate-T c phonon-mediated devices, such as MgB2 and A15 compounds, but much a stronger difference with YBa2Cu3O7-δ . This work thus shows that dH c2/dT is a reliable parameter, providing an alternative to residual resistivity, for investigating the pair-breaking mechanism induced by impurity scattering in superconductors.

Influence of Segmentation of Ring-Shaped NdFeB Magnets with Parallel Magnetization on Cylindrical Actuators

PubMed Central

Eckert, Paulo Roberto; Goltz, Evandro Claiton; Filho, Aly Ferreira Flores

2014-01-01

This work analyses the effects of segmentation followed by parallel magnetization of ring-shaped NdFeB permanent magnets used in slotless cylindrical linear actuators. The main purpose of the work is to evaluate the effects of that segmentation on the performance of the actuator and to present a general overview of the influence of parallel magnetization by varying the number of segments and comparing the results with ideal radially magnetized rings. The analysis is first performed by modelling mathematically the radial and circumferential components of magnetization for both radial and parallel magnetizations, followed by an analysis carried out by means of the 3D finite element method. Results obtained from the models are validated by measuring radial and tangential components of magnetic flux distribution in the air gap on a prototype which employs magnet rings with eight segments each with parallel magnetization. The axial force produced by the actuator was also measured and compared with the results obtained from numerical models. Although this analysis focused on a specific topology of cylindrical actuator, the observed effects on the topology could be extended to others in which surface-mounted permanent magnets are employed, including rotating electrical machines. PMID:25051032

Influence of segmentation of ring-shaped NdFeB magnets with parallel magnetization on cylindrical actuators.

PubMed

Eckert, Paulo Roberto; Goltz, Evandro Claiton; Flores Filho, Aly Ferreira

2014-07-21

This work analyses the effects of segmentation followed by parallel magnetization of ring-shaped NdFeB permanent magnets used in slotless cylindrical linear actuators. The main purpose of the work is to evaluate the effects of that segmentation on the performance of the actuator and to present a general overview of the influence of parallel magnetization by varying the number of segments and comparing the results with ideal radially magnetized rings. The analysis is first performed by modelling mathematically the radial and circumferential components of magnetization for both radial and parallel magnetizations, followed by an analysis carried out by means of the 3D finite element method. Results obtained from the models are validated by measuring radial and tangential components of magnetic flux distribution in the air gap on a prototype which employs magnet rings with eight segments each with parallel magnetization. The axial force produced by the actuator was also measured and compared with the results obtained from numerical models. Although this analysis focused on a specific topology of cylindrical actuator, the observed effects on the topology could be extended to others in which surface-mounted permanent magnets are employed, including rotating electrical machines.

Enhanced ferromagnetic properties in Nd and Gd co-doped BiFeO3 ceramics

NASA Astrophysics Data System (ADS)

Jena, A. K.; Chelvane, J. Arout; Mohanty, J.

2018-05-01

Structural, optical and magnetic properties of Nd3+ and Gd3+ doped BiFeO3 were studied. X-ray diffraction studies confirmed that all the co-doped Bi1-x-yNdxGdyFeO3 samples are polycrystalline in nature crystallizing in rhombohedral type structure (Space group: R3c). In addition to this presence of residual phases like Bi2Fe4O9, Bi25FeO40 were also observed. Raman spectra confirms the structural distortion in co-doped ceramics. Band gap of samples decrease from 2.08eV to 1.95eV with increase in Gd concentration. Room temperature magnetization measurement indicated enhancement of magnetic properties with increase in Gd concentration.

Spin-lattice coupling mediated multiferroicity in (ND 4) 2FeCl 5 • D 2O

DOE PAGES

Tian, Wei; Cao, Huibo; Wang, Jincheng; ...

2016-12-07

In this paper, we report a neutron diffraction study of the multiferroic mechanism in (ND 4) 2FeCl 5 • D 2O, a molecular compound that exhibits magnetically induced ferroelectricity. This material exhibits two successive magnetic transitions on cooling: a long-range order transition to an incommensurate (IC) collinear sinusoidal spin state at T N = 7.3 K, followed by a second transition to an IC cycloidal spin state at T FE = 6.8 K, the latter of which is accompanied by spontaneous ferroelectric polarization. The cycloid structure is strongly distorted by spin-lattice coupling, as evidenced by the observations of both oddmore » and even higher-order harmonics associated with the cycloid wave vector, and a weak commensurate phase that coexists with the IC phase. The second-order harmonic appears at T FE, thereby providing unambiguous evidence that the onset of the electric polarization is accompanied by a lattice modulation due to spin-lattice interaction. The neutron results, in conjunction with the negative thermal expansion and large magnetostriction observed, indicate that spin-lattice coupling plays a critical role in the ferroelectric mechanism of (ND 4) 2FeCl 5 • D 2O.« less

Solid-solution stability and preferential site-occupancy in (R-R′){sub 2}Fe{sub 14}B compounds

DOE Office of Scientific and Technical Information (OSTI.GOV)

Colin, C. V.; Dempsey, N. M.; Univ. Grenoble Alpes, Inst NEEL, F-38000 Grenoble

The rare-earth (R) uniaxial anisotropy of R{sub 2}Fe{sub 14}B compounds with magnetic R atoms (e.g., Nd or Pr) is at the origin of the exceptional hard magnetic properties achieved in magnets based on these compounds. The uniaxial anisotropy found in Ce{sub 2}Fe{sub 14}B is attributed mainly to the magnetism of Fe. Ce is the most abundant R element and there has been much recent effort to fabricate magnets in which Ce is partially substituted for Nd. In the present neutron study of (R{sub 1−x}Ce{sub x}){sub 2}Fe{sub 14}B (R = La or Nd), Ce is found to enter the R{sub 2}Fe{submore » 14}B phase over the entire composition range. The crystallographic parameters decrease with increasing Ce content and the Ce atoms preferentially occupy the smaller 4f sites. It is concluded that Ce in these (RR′){sub 2}Fe{sub 14}B compounds essentially maintains the intermediate valence character found in Ce{sub 2}Fe{sub 14}B. It is proposed that, in this intermediate valence state, Ce weakly contributes to uniaxial anisotropy, thus making a link with the fact that significant coercivity is preserved in Ce-substituted NdFeB magnets.« less

2nd Gen FeCrAl ODS Alloy Development For Accident-Tolerant Fuel Cladding

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dryepondt, Sebastien N.; Massey, Caleb P.; Edmondson, Philip D.

Extensive research at ORNL aims at developing advanced low-Cr high strength FeCrAl alloys for accident tolerant fuel cladding. One task focuses on the fabrication of new low Cr oxide dispersion strengthened (ODS) FeCrAl alloys. The first Fe-12Cr-5Al+Y 2O 3 (+ ZrO 2 or TiO 2) ODS alloys exhibited excellent tensile strength up to 800 C and good oxidation resistance in steam up to 1400 C, but very limited plastic deformation at temperature ranging from room to 800 C. To improve alloy ductility, several fabrication parameters were considered. New Fe-10-12Cr-6Al gas-atomized powders containing 0.15 to 0.5wt% Zr were procured and ballmore » milled for 10h, 20h or 40h with Y2O3. The resulting powder was then extruded at temperature ranging from 900 to 1050 C. Decreasing the ball milling time or increasing the extrusion temperature changed the alloy grain size leading to lower strength but enhanced ductility. Small variations of the Cr, Zr, O and N content did not seem to significantly impact the alloy tensile properties, and, overall, the 2nd gen ODS FeCrAl alloys showed significantly better ductility than the 1st gen alloys. Tube fabrication needed for fuel cladding will require cold or warm working associated with softening heat treatments, work was therefore initiated to assess the effect of these fabrications steps on the alloy microstructure and properties. This report has been submitted as fulfillment of milestone M3FT 16OR020202091 titled, Report on 2nd Gen FeCrAl ODS Alloy Development for the Department of Energy Office of Nuclear Energy, Advanced Fuel Campaign of the Fuel Cycle R&D program.« less

Structural, magnetic and Mössbauer studies of Nd-doped Mg-Mn ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Somnath; Sharma, Indu; Kotnala, R. K.; Singh, M.; Kumar, Arun; Dhiman, Pooja; Singh, Virender Pratap; Verma, Kartikey; Kumar, Gagan

2017-12-01

The present work is focused on the replacement of Fe3+ ions by rare-earth Nd3+ ions and their influence on the cations distribution, structural, magnetic and Mössbauer properties of Mg-Mn nanoferrites. Nanosized Nd-doped Mg-Mn nanoferrites, Mg0.9Mn0.1NdxFe2-xO4, where x = 0.1, 0.2 & 0.3, were successfully synthesized for the first time through solution combustion technique. X-ray diffraction studies confirmed the formation of single phase nature of the synthesized nanoferrites. Williamsons-Hall plots were used to obtain the particle size and strain while the lattice parameter was obtained from Nelson-Riley plots. The particle size was observed to decrease (19.2-13.5 nm) while lattice parameter was observed to increase (8.373-8.391 Å) with the incorporation of Nd3+ ions. Cation distribution between the tetrahedral (A-site) and octahedral (B-site) was estimated by using the X-ray diffraction method & magnetization technique. The estimated cation distribution was used to investigate the detailed structural parameters. Room temperature M-H study revealed a decrease of saturation magnetization (10.15-1.83 emu/g) and an increase in coercivity (22.86-27.19 Oe) with the increasing substitution of Nd3+ ions. Magnetic results obtained in the present study indicated that the synthesized nanoferrites can be a useful candidate for electromagnet applications.

147Sm-143Nd systematics of Earth are inconsistent with a superchondritic Sm/Nd ratio

PubMed Central

Huang, Shichun; Jacobsen, Stein B.; Mukhopadhyay, Sujoy

2013-01-01

The relationship between the compositions of the Earth and chondritic meteorites is at the center of many important debates. A basic assumption in most models for the Earth’s composition is that the refractory elements are present in chondritic proportions relative to each other. This assumption is now challenged by recent 142Nd/144Nd ratio studies suggesting that the bulk silicate Earth (BSE) might have an Sm/Nd ratio 6% higher than chondrites (i.e., the BSE is superchondritic). This has led to the proposal that the present-day 143Nd/144Nd ratio of BSE is similar to that of some deep mantle plumes rather than chondrites. Our reexamination of the long-lived 147Sm-143Nd isotope systematics of the depleted mantle and the continental crust shows that the BSE, reconstructed using the depleted mantle and continental crust, has 143Nd/144Nd and Sm/Nd ratios close to chondritic values. The small difference in the ratio of 142Nd/144Nd between ordinary chondrites and the Earth must be due to a process different from mantle-crust differentiation, such as incomplete mixing of distinct nucleosynthetic components in the solar nebula. PMID:23479630

Longitudinal spin Seebeck effect in Nd{sub 2}BiFe{sub 5−x}Ga{sub x}O{sub 12} prepared on gadolinium gallium garnet (001) by metal organic decomposition method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Asada, H., E-mail: asada@yamaguchi-u.ac.jp; Kuwahara, A.; Sakata, N.

2015-05-07

Nd{sub 2}BiFe{sub 5−x}Ga{sub x}O{sub 12} thin films with the Ga composition x = 0, 0.5, and 1.0 are prepared on (001) oriented gadolinium gallium garnet substrates by a metal organic decomposition method. Only (001) peaks are observed in x-ray diffraction patterns for all the films, suggesting that the highly oriented Nd{sub 2}BiFe{sub 5−x}Ga{sub x}O{sub 12} thin films were formed. Increasing Ga composition, the saturation magnetization decreases, and the perpendicular easy axis is enhanced due to the decrease of the shape anisotropy. Longitudinal spin Seebeck effects (LSSEs) in Nd{sub 2}BiFe{sub 5−x}Ga{sub x}O{sub 12} thin films with a Pt layer of 10 nm in thicknessmore » were investigated. Magnetic field dependence of the thermoelectric voltage caused by the LSSE in Nd{sub 2}BiFe{sub 5−x}Ga{sub x}O{sub 12} films indicates the hysteresis loop with the small coercivity reflecting the magnetization curve. The decrease of LSSE voltage in Nd{sub 2}BiFe{sub 5−x}Ga{sub x}O{sub 12} is clearly observed with the decrease of Fe composition.« less

The Sm-Nd systematics of silicate inclusions in iron meteorites: Results from Caddo (IAB)

NASA Technical Reports Server (NTRS)

Stewart, Brian W.; Papanastassiou, D. A.; Wasserburg, G. J.

1993-01-01

The timing of events leading to the formation of silicate-rich and metal-rich regions in planetesimals remains an important problem in the study of planetary formation and differentiation in the early solar system. The IAB irons are especially important as they are considered to represent a magmatic differentiation series. Iron meteorites present a particular challenge for chronological studies, due to the relative paucity of phases serving as hosts for radioactive parent-daughter nuclides. Recent work using the Re-Os system, following on the pioneering work by Herr et al. and Luck and Allegre, appears promising, but investigators up to now have concentrated on whole rock isochrons. Silicate clasts enclosed within iron meteorites can provide information about the chronology and thermal history of irons. Extensive work on Rb-Sr, K-Ar, and I-Xe has been reported on silicate inclusions in iron meteorites. We report the initial results from our Sm-Nd study of an inclusion with the Caddo IAB iron, the first Sm-Nd isotopic study of a silicate clast embedded within an iron meteorite. Our results include measurements of the standard long-lived Sm-147/Nd-143 (tau = 152 AE) system, as well as the shorter-lived SM-146/Nd-142 (tau = 0.149 AE) system, which has been shown to be very useful in deciphering the history of the early solar system. The Caddo silicate clast was described by Palme et al., who kindly provided us with a major part of the inclusion. The inclusion is coarse-grained consisting predominantly of olivine, clinopyroxene, and plagioclase, with lesser amounts of orthopyroxene, Fe-Ni metal, sulfide, and phosphate. The relatively large grain size (up to 3 mm) and 120 degree grain boundaries suggest extensive metamorphism at high temperatures. Based on study of a thin section, there is evidence for metal invading along grain boundaries in some regions of the inclusion, suggesting that the Fe-Ni metal was molten when the silicate clast was incorporated. Metamorphic

Synthesis and characterisation of the n = 2 Ruddlesden–Popper phases Ln{sub 2}Sr(Ba)Fe{sub 2}O{sub 7} (Ln = La, Nd, Eu)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gurusinghe, Nicola N.M.; Figuera, Juand de la; Marco, José F.

2013-09-01

Graphical abstract: - Highlights: • Some Ruddlesden–Popper phases have been characterised. • Substitution on the A site influences cationic order. • The magnetic moment redirects with temperature - Abstract: A series of n = 2 Ruddlesden–Popper phases A{sub 2}B{sub 2}O{sub 7} of composition Ln{sub 2}Sr(Ba)Fe{sub 2}O{sub 7} (Ln = La, Nd, Eu) have been prepared. La{sub 2}SrFe{sub 2}O{sub 7} and La{sub 2}BaFe{sub 2}O{sub 7} crystallise in the tetragonal space group I4/mmm. The structures of Eu{sub 2}SrFe{sub 2}O{sub 7} and Nd{sub 2}SrFe{sub 2}O{sub 7} are best described in space group P4{sub 2}/mnm. Substitution on the A site with smaller lanthanide- andmore » larger alkaline metal- ions leads to enhanced cationic order in these phases and reflects increasing differences in cationic radii. All the compounds are antiferromagnetically ordered between 298 and 2 K. In La{sub 2}SrFe{sub 2}O{sub 7} the magnetic moment lies along [1 1 0] at all temperatures between 298 and 2 K whereas in La{sub 2}BaFe{sub 2}O{sub 7} the magnetic moment at 298 K lies along the crystallographic x-axis but redirects from the [1 0 0] to the [1 1 0] direction between 210 and 190 K and is retained in this direction until 2 K. In Nd{sub 2}SrFe{sub 2}O{sub 7} the magnetic moment at 298 K lies along [1 1 0] but rotates from [1 1 0] to [0 0 1] between 17 and 9 K. A series of {sup 57}Fe Mössbauer spectra recorded from La{sub 2}SrFe{sub 2}O{sub 7} between 290 and 600 K indicate a magnetic ordering temperature of T{sub N} ≥ 535 K.« less

Preparation of poly (arylene ether nitrile)/NzdFeB composite film with excellent thermal properties and tensile strength

NASA Astrophysics Data System (ADS)

Pan, Hai; Xu, Mingzhen; Liu, Xiaobo

2017-12-01

PEN/NdFeB composite films were prepared by the solution casting method. The thermal properties, fracture morphology and tensile strength of the composite films were tested by DSC, TGA, SEM and electromechanical universal testing machine, respectively. The results reveal that the composite film has good thermal properties and tensile strength. Glass-transition temperature and decomposition temperatures at weight loss of 5% ot the composite films retain at 166±1 C and 462±4 C, respectively. The composite film with 5 wt.% NdFeB has the best tensile strength value for 100.5 MPa. In addition, it was found that the NdFeB filler was well dispersed in PEN matrix by SEM analysis.

Significant reduction of saturation magnetization and microwave-reflection loss in barium-natural ferrite via Nd3+ substitution

NASA Astrophysics Data System (ADS)

Widanarto, W.; Ardenti, E.; Ghoshal, S. K.; Kurniawan, C.; Effendi, M.; Cahyanto, W. T.

2018-06-01

To minimize the signal degradation, many electronic devices require efficient microwave absorbers with very low reflection-losses within the X-band. We prepared a series of trivalent neodymium-ion (Nd3+) substituted barium-natural ferrite using a modified solid-state reaction method. The effect of the Nd3+-ion content on the structure, surface morphology, magnetic properties, and microwave reflection loss was studied. The composites were characterized using X-ray diffraction, a vibrating sample magnetometer, scanning electron microscopy, and a vector network analyzer. The XRD patterns of the sample without Nd3+ reveal the presence of BaFe12O19 (hexagonal) and BaFe2O4 (rhombohedral) phases. Furthermore, a new hexagonal crystal phase of Ba6Nd2Fe4O15 appeared after substituting Nd3+. The average size of the prepared barium-natural ferrite particles was estimated to be between 0.4 and 0.8 μm. Both saturation magnetization and microwave reflection losses of these barium-ferrites were significantly reduced by increasing the Nd3+ content.

Characterization of the magnetic properties of NdFeB thick films exposed to elevated temperatures

NASA Astrophysics Data System (ADS)

Fujiwara, Ryogen; Devillers, Thibaut; Givord, Dominique; Dempsey, Nora M.

2018-05-01

Hard magnetic films used in magnetic micro-systems may be exposed to elevated temperatures during film and system fabrication and also during use of the micro-system. In this work, we studied the influence of temperature on the magnetic properties of 10 μm thick out-of-plane textured NdFeB films fabricated by high rate triode sputtering. Out-of-plane hysteresis loops were measured in the range 300K - 650K to establish the temperature dependence of coercivity, magnetization at 7 T and remanent magnetization. Thermal demagnetization was measured and magnetization losses were recorded from 350K in films heated under zero or low (-0.1 T) external field and from 325 K for films heated under an external field of -0.5 T. The effect of thermal cycling under zero field on the remanent magnetization was also studied and it was found that cycling between room temperature and 323 K did not lead to any significant loss in remanence at room temperature, while a 4% drop is recorded when the sample is cycled between RT and 343K. Measurement of hysteresis loops at room temperature following exposure to elevated temperatures reveals that while remanent magnetisation is practically recovered in all cases, irreversible losses in coercivity occur (6.7 % following heating to 650K, and 1.3 % following heating to 343K). The relevance of these results is discussed in terms of system fabrication and use.

Prediction of the new efficient permanent magnet SmCoNiFe3

NASA Astrophysics Data System (ADS)

Söderlind, P.; Landa, A.; Locht, I. L. M.; Åberg, D.; Kvashnin, Y.; Pereiro, M.; Däne, M.; Turchi, P. E. A.; Antropov, V. P.; Eriksson, O.

2017-09-01

We propose a new efficient permanent magnet, SmCoNiFe3, which is a development of the well-known SmCo5 prototype. More modern neodymium magnets of the Nd-Fe-B type have an advantage over SmCo5 because of their greater maximum energy products due to their iron-rich stoichiometry. Our new magnet, however, removes most of this disadvantage of SmCo5 while preserving its superior high-temperature efficiency over the neodymium magnets. We show by means of first-principles electronic-structure calculations that SmCoNiFe3 has very favorable magnetic properties and could therefore potentially replace SmCo5 or Nd-Fe-B types in various applications.

Prediction of the new efficient permanent magnet SmCoNiFe 3

DOE PAGES

Soderlind, P.; Landa, A.; Locht, I. L. M.; ...

2017-09-14

Here, we propose a new efficient permanent magnet, SmCoNiFe 3, which is a development of the well-known SmCo 5 prototype. More modern neodymium magnets of the Nd-Fe-B type have an advantage over SmCo 5 because of their greater maximum energy products due to their iron-rich stoichiometry. Our new magnet, however, removes most of this disadvantage of SmCo 5 while preserving its superior high-temperature efficiency over the neodymium magnets. We show by means of first-principles electronic-structure calculations that SmCoNiFe 3 has very favorable magnetic properties and could therefore potentially replace SmCo 5 or Nd-Fe-B types in various applications.

Magnetization reversal mechanism and coercivity enhancement in three-dimensional granular Nd-Fe-B magnets studied by micromagnetic simulations

NASA Astrophysics Data System (ADS)

Lee, Jae-Hyeok; Choe, Jinhyeok; Hwang, Shinwon; Kim, Sang-Koog

2017-08-01

We studied the mechanism of magnetization reversals and coercivity enhancements in three-dimensional (3D) granular Nd-Fe-B permanent magnets using finite-element micromagnetic simulations. The magnetization reversals in the hard magnets consisting of hard-phase grains separated by relatively soft-phase grain boundaries were analyzed with reference to the simulation results for the magnetic field-dependent distributions of the local magnetizations. The saturation magnetization of the grain-boundary phase plays a crucial role in the transition between nucleation- and domain-wall-propagation-controlled reversal processes. The smaller the saturation magnetization of the grain-boundary phase is, the more preferable is the nucleation-controlled process, which results in a larger coercivity. The exchange stiffness of the grain-boundary phase determines the preferred paths of domain-wall propagations, whether inward into grains or along the grain boundaries for relatively small and large exchange stiffness, respectively. However, the exchange stiffness of the grain-boundary phase alone does not significantly contribute to coercivity enhancement in cases where the size of hard-phase grains is much greater than the exchange length. This work paves the way for the design of high-performance hard magnets of large coercivity and maximum-energy-product values.

Thermodynamic Modeling of the Ge-Nd Binary System

NASA Astrophysics Data System (ADS)

Liu, Miao; Li, Changrong; Du, Zhenmin; Guo, Cuiping; Niu, Chunju

The Ge-Nd has been critically assessed by means of the CALculation of PHAse Diagram (CALPHAD) technique. For the liquid phase, the associate model was used with the constituent species Ge, Nd, Ge3Nd5 and Ge1.6Nd in the Ge-Nd system. The terminal solid solution diamond-(Ge), dhcp-(Nd) and bcc_A2-(Nd) in the Ge-Nd system were described using the substitutional model, in which the excess Gibbs energy was formulated with the Redlich-Kister equation. The compounds with homogeneity ranges, α(Ge1.6Nd), β(Ge1.6Nd), (GeNd), (Ge4Nd5) and (Ge3Nd5) were modeled using two sublattices as α(Ge,Nd)1.6Nd, β(Ge,Nd)1.6Nd, (Ge,Nd)Nd, (Ge,Nd)4Nd5 and (Ge,Nd)3Nd5, respectively. A set of self-consistent thermodynamic parameters for each of the Ge-Nd binary systems was obtained. The calculation results agree well with the available experimental data from literatures.

Submicron R{sub 2}Fe{sub 14}B particles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Koylu-Alkan, O., E-mail: ozlem@udel.edu, E-mail: hadji@udel.edu; Hadjipanayis, G. C., E-mail: ozlem@udel.edu, E-mail: hadji@udel.edu; Barandiaran, J. M.

Mechanochemical synthesis of submicron R{sub 2}Fe{sub 14}B particles with R = Dy, Nd, Pr has been performed successfully via high energy ball milling of rare-earth oxides, iron oxide and boron oxide in the presence of a reducing agent (Ca) and a dispersant material (CaO), followed by annealing at 800 - 900 °C. In the R = Nd system, we were able to fabricate particles embedded in a CaO matrix with coercivity (H{sub c}) of 10.3 kOe after annealing at 900 °C for 5 min. After washing off the dispersant, the H{sub c} was decreased to below 1 kOe because of hydrogen absorptionmore » that leads to the formation of the hydrated R{sub 2}Fe{sub 14}BH{sub x} phase that has a lower anisotropy. Upon removal of the hydrogen the coercivity was increased to 3.3 kOe. The average size of the Nd{sub 2}Fe{sub 14}B particles increases from 100 nm in a sample synthesized at 800 °C to 158 nm at 900 °C. The isotropic Dy{sub 2}Fe{sub 14}B particles showed a higher coercivity of 21 kOe in washed samples after annealing at 900 °C for 5 min. An average size of 71 nm is measured in samples synthesized at 800 °C and 107 nm at 900 °C. Fitting the high field M(H) measurements in Nd{sub 2}Fe{sub 14}B to the law of approach to saturation gave values for the magnetocrystalline anisotropy for the washed sample 2.23 × 10{sup 7} erg/cm{sup 3} and for the vacuum annealed sample 4.15 × 10{sup 7} erg/cm{sup 3}, both of which are lower than the bulk values. This would explain the lower values of H{sub c} observed in the particles.« less

Magnetic Phase Transitions in NdCoAsO

DOE Office of Scientific and Technical Information (OSTI.GOV)

McGuire, Michael A; Gout, Delphine J; Garlea, Vasile O

2010-01-01

NdCoAsO undergoes three magnetic phase transitions below room temperature. Here we report the results of our experimental investigation of this compound, including determination of the crystal and magnetic structures using powder neutron diffraction, as well as measurements of electrical resistivity, thermal conductivity, Seebeck coefficient, magnetization, and heat capacity. These results show that upon cooling a ferromagnetic state emerges near 69 K with a small saturation moment of -0.2{micro}{sub B}, likely on Co atoms. At 14 K the material enters an antiferromagnetic state with propagation vector (0 0 1/2) and small ordered moments (-0.4{micro}{sub B}) on Co and Nd. Near 3.5more » K a third transition is observed, and corresponds to the antiferromagnetic ordering of larger moments on Nd, with the same propagation vector. The ordered moment on Nd reaches 1.39(5){micro}{sub B} at 300 mK. Anomalies in the magnetization, electrical resistivity, and heat capacity are observed at all three magnetic phase transitions.« less

Lunar initial Nd-143/Nd-144 - Differential evolution of the lunar crust and mantle

NASA Technical Reports Server (NTRS)

Lugmair, G. W.; Marti, K.

1978-01-01

The Sm-Nd evolution of Apollo 15 green glass is discussed. The ICE age (intercept with chondritic evolution) of 3.8 + or - 0.4 eons overlaps the range of reported (Ar-39)-(Ar-40) ages and implies a distinct source region for green glass, characterized by very low and unfractionated REE abundances. Evidence is presented that LINd (lunar initial Nd) is compatible with a 'chondritic'-type Nd isotopic evolution as observed in the Juvinas meteorite. This normalization is used to study the Sm-Nd system of various lunar rock types. The results obtained from a limited number of rocks clearly indicate differential Sm-Nd evolution for the lunar crust and mantle. High-Ti basalts returned by the Apollo 11 and 17 missions were derived from distinct source regions. The Nd-143 evolution in KREEP requires a source region which is clearly distinct from any mantle reservoir.

Nonlinear optical properties of Nd3+-Li+ co-doped ZnS-PVP thin films

NASA Astrophysics Data System (ADS)

Talwatkar, S. S.; Sunatkari, A. L.; Tamgadge, Y. S.; Muley, G. G.

2018-04-01

The nonlinear optical properties of Nd3+-Li+ co-doped ZnS-PVP nanocomposite were studied using a continuous wave (CW) He-Ne laser (λ = 632.8 nm)by z-scan technique. The nonlinear refractive index (n2), absorption coefficient (β) and third order nonlinear susceptibility (χ(3)) of PVP thin films embedded with Nd3+-Li+ co-doped ZnS NPs was found in the order of 10-7 cm2/W, 10-6 cm/W and 10-7 esu respectively. The nonlinearity found increasing with Nd3+-Li+ co-dopant concentration. Based on the results, it is proposed that this material is a new class of luminescent material suitable in optoelectronics devices application, especially in light-emitting devices, electroluminescent devices, display devices, etc.

The End of Monterey Submarine Canyon Incision and Potential River Source Areas-Os, Nd, and Pb Isotope Constraints from Hydrogenetic Fe-Mn Crusts

NASA Astrophysics Data System (ADS)

Conrad, T. A.; Nielsen, S.; Ehrenbrink, B. P. E.; Blusztajn, J.; Hein, J. R.; Paytan, A.

2015-12-01

The Monterey Canyon off central California is the largest submarine canyon off North America and is comparable in scale to the Grand Canyon. The age and history of the Monterey Canyon are poorly constrained due to thick sediment cover and sediment disruption from turbidity currents. To address this deficit we analyzed isotopic proxies (Os, Pb, Nd) from hydrogenetic ferromanganese (Fe-Mn) crusts, which grow over millions of years on elevated rock surfaces by precipitation of metals from seawater. Fe-Mn crusts were studied from Davidson Seamount near the base of the Monterey submarine fan, the Taney Seamount Chain, and from Hoss Seamount, which serves as a regional control (Fig.). Fe-Mn crusts were dated using Os isotope ratios compared to those that define the Cenozoic Os isotope seawater curve. Four Fe-Mn crust samples from Davidson and Taney Seamounts deviate from the Os isotopic seawater curve towards radiogenic values after 4.5±1 Ma. Osmium is well mixed in the global ocean and is not subject to significant diffusive reequilibration in Fe-Mn crusts. We therefore attribute deviations from the Os isotope seawater curve to large-scale terrestrial input that ended about 4.5±1 Ma. The two Davidson samples also show more radiogenic Nd isotope values from about 4.5±1 Ma. Lead isotopes in one Davidson Seamount crust, measured by LA-ICPMS, deviate from regional values after 4.5±1 Ma for about 500 ka towards terrestrial sources. The Taney Seamount Fe-Mn crust does not deviate from regional Nd nor Pb isotope values due to its greater distance from Monterey Canyon and the shorter marine residence times of Nd and Pb. Isotope plots of our crust data and compiled data for potential source rocks indicate that the river that carved Monterey Canyon carried sediment with values closer to the Sierra Nevada than to a Colorado Plateau source, with cessation of major riverine input occurring approximately 4.5±1 Ma, an age that we interpret as the end of the Monterey Canyon

Chemically Inhomogeneous RE-Fe-B Permanent Magnets with High Figure of Merit: Solution to Global Rare Earth Criticality

PubMed Central

Jin, Jiaying; Ma, Tianyu; Zhang, Yujing; Bai, Guohua; Yan, Mi

2016-01-01

The global rare earth (RE) criticality, especially for those closely-relied Nd/Pr/Dy/Tb in the 2:14:1-typed permanent magnets (PMs), has triggered tremendous attempts to develop new alternatives. Prospective candidates La/Ce with high abundance, however, cannot provide an equivalent performance due to inferior magnetic properties of (La/Ce)2Fe14B to Nd2Fe14B. Here we report high figure-of-merit La/Ce-rich RE-Fe-B PMs, where La/Ce are inhomogeneously distributed among the 2:14:1 phase. The resultant exchange coupling within an individual grain and magnetostatic interactions across grains ensure much superior performance to the La/Ce homogeneously distributed magnet. Maximum energy product (BH)max of 42.2 MGOe is achieved even with 36 wt. % La-Ce incorporation. The cost performance, (BH)max/cost, has been raised by 27.1% compared to a 48.9 MGOe La/Ce-free commercial magnet. The construction of chemical heterogeneity offers recipes to develop commercial-grade PMs using the less risky La/Ce, and also provides a promising solution to the REs availability constraints. PMID:27553789

Influence of Fe-substitution on structural, magnetic and magnetocaloric properties of Nd2Fe17-xCox solid solutions

NASA Astrophysics Data System (ADS)

Bouchaala, N.; Jemmali, M.; Bartoli, T.; Nouri, K.; Hentech, I.; Walha, S.; Bessais, L.; Salah, A. Ben

2018-02-01

Nd2Fe17-xCox (x = 0 , 1 , 2 , 3 , 4) intermetallic compounds, obtained under arc-melting conditions, have been investigated by means of X-ray diffraction analysis (XRD), Mössbauer spectrometry and magnetic measurements. The Rietveld refinement revealed that the sample is a pure compound with rhombohedral Th2Zn17-type structure (R 3 bar m space group) with the following lattice parameters: a = 8.5792 (2) Å, c = 12.4615 (2) Å. Using Mössbauer spectrometry analysis coupled with structural consideration we have unambiguously determined the cobalt atoms preferred inequivalent crystallographic site. Nd2Fe17 show an increase of 3.5 T in their weighted average hyperfine fields upon cobalt substitution. Whatever the cobalt content, the hyperfine field of these compounds follow this sequence Hhf { 6 c } >Hhf { 9 d } >Hhf { 18 f } >Hhf { 18 h }. The magnetic measurements showed that the Curie temperature increases with the Co content. The magnetic entropy change (ΔSM) was estimated from isothermal magnetization curves and it increases from 3.35 J/Kg K for x = 0 to 5.83 J/Kg K for x = 2 at μ0 H = 1.6 T . The relative cooling power (RCP) is in the range of 11.6 J/kg (x = 0) and 16 J/kg (x = 2).

Testing Models for the Origin of the Earth-Moon System with 142Nd/144Nd Measurements

NASA Astrophysics Data System (ADS)

Hyung, E.; Jacobsen, S. B.; Zeng, L.

2015-12-01

The Sm-Nd system is widely used for tracking the differentiation and evolution of planetary silicate reservoirs, due to the well understood, strong Sm-Nd fractionation between melt and mantle minerals. The short-lived 146Sm-142Nd system with a half-life of 103 Ma or 68 Ma has been used to constrain early planetary differentiation events based on early Archean terrestrial rocks, lunar rocks and meteorites. Early Archean terrestrial rocks show significant variations in 142Nd/144Nd of about 30 ppm, demonstrating very early differentiation of the Earth's mantle and crust. In contrast, present day 142Nd/144Nd ratios of mantle-derived ocean island basalts and MORBs show almost no variation at the reported analytical precision level (2σ = ± 6 ppm), suggesting that such early variations have been erased with time due to crustal recycling and mantle mixing. The 142Nd/144Nd ratio of the lunar mantle has been reported to be offset from terrestrial standards by about -5 ppm, barely resolvable with the reported analytical uncertainties. Differences in the 142Nd/144Nd ratios between the bulk Earth and Moon may suggest early large scale silicate differentiation events on the Earth that predate the Giant Moon forming impact. To address this problem, we carry out new 142Nd/144Nd measurements of terrestrial rocks, and lunar rocks and meteorites with a TIMS (Isoprobe T) equipped with new Xact Faraday amplifiers provided by Isotopx. We find that the Xact amplifiers provide lower noise than the earlier generation preamplifiers and operate close to the theoretical thermodynamic noise limit calculated from the Johnson equation. So far we have been able to improve multidynamic measurements to be reproducible to within ± 2 ppm at the 2σ level, and with this precision we find no variations in a few young terrestrial rocks. Our next step is measurements of lunar rocks and E-chondrites. If these turn out to be identical to the modern Earth, then the Nd isotope system may tell the same

Diode-pumped quasi-three-level Nd:GdV O4-Nd:YAG sum-frequency laser at 464 nm

NASA Astrophysics Data System (ADS)

Lu, Jie

2014-04-01

We report a laser architecture to obtain continuous-wave (cw) blue radiation at 464 nm. A 808 nm diode pumped a Nd:GdV O4 crystal emitting at 912 nm. A part of the pump power was then absorbed by the Nd:GdV O4 crystal. The remainder was used to pump a Nd:YAG crystal emitting at 946 nm. Intracavity sum-frequency mixing at 912 and 946 nm was then realized in a LiB3O5 (LBO) crystal to produce blue radiation. We obtained a cw output power of 1.52 W at 464 nm with a pump laser diode emitting 18.4 W at 808 nm.

Thermal analysis and experimental study of end-pumped Nd: YLF laser at 1053 nm

NASA Astrophysics Data System (ADS)

El-Agmy, R. M.; Al-Hosiny, N.

2017-12-01

We have numerically analyzed the thermal effects in Nd: YLF laser rod. The calculations of temperature and stress distributions in the Nd: YLF laser rod was performed with finite element (FE) simulations. The calculations showed that the laser rod could be pumped up to a power of 40 W without fracture caused by thermal stress. The calculated thermal lens power of thermally induced lens in Nd: YLF ( σ-polarization) laser rod was analyzed and validated experimentally with two independent techniques. A Shack-Hartmann wavefront sensor and a Mach-Zehnder interferometer were used for direct measurements of focal thermal lens at different pump powers. The obtained measurements were coinciding with the FE simulations.

Defining Simple nD Operations Based on Prosmatic nD Objects

NASA Astrophysics Data System (ADS)

Arroyo Ohori, K.; Ledoux, H.; Stoter, J.

2016-10-01

An alternative to the traditional approaches to model separately 2D/3D space, time, scale and other parametrisable characteristics in GIS lies in the higher-dimensional modelling of geographic information, in which a chosen set of non-spatial characteristics, e.g. time and scale, are modelled as extra geometric dimensions perpendicular to the spatial ones, thus creating a higher-dimensional model. While higher-dimensional models are undoubtedly powerful, they are also hard to create and manipulate due to our lack of an intuitive understanding in dimensions higher than three. As a solution to this problem, this paper proposes a methodology that makes nD object generation easier by splitting the creation and manipulation process into three steps: (i) constructing simple nD objects based on nD prismatic polytopes - analogous to prisms in 3D -, (ii) defining simple modification operations at the vertex level, and (iii) simple postprocessing to fix errors introduced in the model. As a use case, we show how two sets of operations can be defined and implemented in a dimension-independent manner using this methodology: the most common transformations (i.e. translation, scaling and rotation) and the collapse of objects. The nD objects generated in this manner can then be used as a basis for an nD GIS.

Altering the cooling rate dependence of phase formation during rapid solidification in the Nd 2Fe 14B system

NASA Astrophysics Data System (ADS)

Branagan, D. J.; McCallum, R. W.

In order to evaluate the effects of additions on the solidification behavior of Nd 2Fe 14B, a stoichiometric alloy was modified with elemental additions of Ti or C and a compound addition of Ti with C. For each alloy, a series of wheel speed runs was undertaken, from which the optimum wheel speeds and optimum energy products were determined. On the BHmax versus wheel speed plots, regions were identified in order to analyze the changes with cooling rates leading to phase formation brought about by the alloy modifications. The compilation of the regional data of the modified alloys showed their effects on altering the cooling rate dependence of phase formation. It was found that the regions of properitectic iron formation, glass formation, and the optimum cooling rate can be changed by more than a factor of two through appropriate alloying additions. The effects of the alloy modifications can be visualized in a convenient fashion through the use of a model continuous cooling transformation (CCT) diagram which represents phase formation during the solidification process under continuous cooling conditions for a wide range of cooling rates from rapid solidification to equilibrium cooling.

Magnetic Properties Improvement of Die-upset Nd-Fe-B Magnets by Dy-Cu Press Injection and Subsequent Heat Treatment

NASA Astrophysics Data System (ADS)

Wang, Zexuan; Ju, Jinyun; Wang, Jinzhi; Yin, Wenzong; Chen, Renjie; Li, Ming; Jin, Chaoxiang; Tang, Xu; Lee, Don; Yan, Aru

2016-12-01

Ultrafine-grained die-upset Nd-Fe-B magnets are of importance because they provide a wide researching space to redesign the textured structures. Here is presented a route to obtain a new die-upset magnet with substantially improved magnetic properties. After experiencing the optimized heat treatment, both the coercivity and remanent magnetization of the Dy-Cu press injected magnets increased substantially in comparison with those of the annealed reference magnets, which is distinct from the reported experimental results on heavy rare-earth diffusion. To study the mechanism, we analyzed the texture evolution in high-temperature annealed die-upset magnets, which had significant impact on the improvement of remanent magnetization. On basis of the results, we find that the new structures are strongly interlinked with the initial structures. With injecting Dy-Cu eutectic alloy, an optimized initial microstructure was achieved in the near-surface diffused regions, which made preparations for the subsequent texture improvement. Besides, the Dy gradient distribution of near-surface regions of the Dy-Cu press injected magnets was also investigated. By controlling the initial microstructure and subsequent diffusion process, a higher performance magnet is expected to be obtained.

Magnetic Properties Improvement of Die-upset Nd-Fe-B Magnets by Dy-Cu Press Injection and Subsequent Heat Treatment

PubMed Central

Wang, Zexuan; Ju, Jinyun; Wang, Jinzhi; Yin, Wenzong; Chen, Renjie; Li, Ming; Jin, Chaoxiang; Tang, Xu; Lee, Don; Yan, Aru

2016-01-01

Ultrafine-grained die-upset Nd-Fe-B magnets are of importance because they provide a wide researching space to redesign the textured structures. Here is presented a route to obtain a new die-upset magnet with substantially improved magnetic properties. After experiencing the optimized heat treatment, both the coercivity and remanent magnetization of the Dy-Cu press injected magnets increased substantially in comparison with those of the annealed reference magnets, which is distinct from the reported experimental results on heavy rare-earth diffusion. To study the mechanism, we analyzed the texture evolution in high-temperature annealed die-upset magnets, which had significant impact on the improvement of remanent magnetization. On basis of the results, we find that the new structures are strongly interlinked with the initial structures. With injecting Dy-Cu eutectic alloy, an optimized initial microstructure was achieved in the near-surface diffused regions, which made preparations for the subsequent texture improvement. Besides, the Dy gradient distribution of near-surface regions of the Dy-Cu press injected magnets was also investigated. By controlling the initial microstructure and subsequent diffusion process, a higher performance magnet is expected to be obtained. PMID:27922060

Filled Nd(z)Fe(x)Co(4-x)Sb(12-y)Ge(y) Skutterudites: Processing and Thermoelectric Properties

NASA Technical Reports Server (NTRS)

Mackey, Jon; Sehirlioglu, Alp; Dynys, Fred

2016-01-01

Skutterudites have proven to be a useful thermoelectric system as a result of their enhanced figure of merit (ZT1), cheap material cost, favorable mechanical properties, and good thermal stability. The majority of skutterudite interest in recent years has been focused on binary skutterudites like CoSb3. Binary skutterudites are often double and triple filled, with a range of elements from the lanthanide series, in order to reduce the lattice component of thermal conductivity. Ternary and quaternary skutterudites, such as Co4Ge6Se6 or Ni4Sb8Sn4, provide additional paths to tune the electronic structure. The thermal conductivity can further be improved in these complex skutterudites by the introduction of fillers. The Nd(z)Fe(x)Co(4-x)Sb(12-y)Ge(y) system has been investigated as a p-type thermoelectric material, and is stable up to 600 C. The influence of Fe and Ge content, along with filler Nd, was investigated on thermoelectric transport properties. In addition to the chemical influence on properties, some processing details of the system will also be addressed.

Causes of 142Nd Variation in Earth

NASA Astrophysics Data System (ADS)

Boyet, M.; Bouvier, A.; Gannoun, A.; Carlson, R.

2015-12-01

Variability of the 142Nd/144Nd ratio can reflect Sm/Nd fractionation during the lifetime of 146Sm, i.e. the first 500 Ma of Solar System history1 and nucleosynthetic heterogeneity inherited from the solar nebula. Deciphering the message carried by 142Nd variability requires a detailed examination of the data for Earth and meteorites. The elevated 142Nd/144Nd in terrestrial samples relative to average chondrites suggests that all terrestrial rocks sampled by volcanism over the Earth's history come from a geochemical reservoir characterized by a superchondritic Sm/Nd ratio. The chemical compliment to this reservoir, however, has never been seen, so it either was lost during Earth's accretion2,3, or is preserved in a deep hidden reservoir 1,4. These models are based on a comparison of Earth rocks and O-chondrites because they do not show any variation in stable Sm and Nd isotopic composition compared to Earth6-8. The first analyzed E-chondrites with terrestrial 142Nd/144Nd showed 144Sm excesses that reflect an excess p-process contribution. Although 142Nd is mainly produced by s-process, there is a direct p-process component estimated to be lower than 4 %. We will present new Sm and Nd isotopic data on meteoritic materials. CAIs show deficits in both r- and p-process isotopes that would lead to elevated 142Nd, yet the bulk C-chondrites in which they are contained show excesses in r-process isotopes and hence 142Nd/144Nd lower than terrestrial. The new E-chondrites data do not confirm the 142Nd-144Sm correlation observed in bulk chondrites In light of these results and using 146Sm-142Nd isochrons for constraining the bulk 142Nd/144Nd ratio of planetary bodies, we will discuss the 142Nd signature of terrestrial samples (from Hadean to present). 1Boyet & Carlson, Science 2005; 2O'Neill & Palme, Phil. Trans. R. Soc 2008; 3Caro et al. Nature 2008; 4Andreasen et al. EPSL 2008; 6Andreasen & Sharma, Science 2006; 7Carlson et al., Science 2007; 8Gannoun et al. PNAS 2011.

Pressure effect on ferroelectricity of multiferroic Ho0.5Nd0.5Fe3(BO3)4

NASA Astrophysics Data System (ADS)

Poudel, Narayan; Gooch, Melissa; Lorenz, Bernd; Bezmaternykh, L. N.; Temerov, V. L.; Chu, C. W.

Ho0.5Nd0.5Fe3(BO3)4 becomes multiferroic below 33 K where it enters into the AFM1 phase and gives rise to a ferroelectric polarization along the a-axis. At 9.5 K, the polarization drops sharply and remains finite value of 40 μC/m2. This is due to the spin rotation from the a-b plane into the c-axis and gives rise to the AFM2 phase. The application of pressure suppresses the AFM2 phase and moves the spin rotation transition from 9.5 K to 4.8 K up to pressure of 18.8 kbar which is observed in both dielectric and pyroelectric measurements. The change in magnetic anisotropy of rare-earth moments and Fe ions under pressure drives the spin rotation transition of rare-earth at lower temperature. DOE, the AFOSR, the T.L.L Temple Foundation, the J.J. and R. Moores Endowment, and the State of Texas (TCSUH).

Magnetic and electrical properties of Nd7Pt3 studied on single crystals

NASA Astrophysics Data System (ADS)

Tsutaoka, Takanori; Ueda, Koyo; Matsushita, Takuya

2018-07-01

Magnetic and electrical properties of Nd7Pt3 with the Th7Fe3 type hexagonal structure have been studied on single crystals by measuring magnetization, magnetic susceptibility and electrical resistivity. Nd7Pt3 possesses a ferromagnetic state below TC = 38 K; a canted antiferromagnetic state takes place at Tt2 = 34 K. Another magnetic phase transition has also been observed at Tt1 = 25 K. The magnetization curve along the a- and b-axes at 2 K shows anomalous first-order irreversible behavior. The direction of the magnetic moment in the canted state can be tilted from the c-plane. Electrical resistivity measurement results show metallic property; three anomalies were observed at Tt1, Tt2 and TC, respectively.

Nd-ordering-driven Mn spin reorientation and magnetization reversal in the magnetostructurally coupled compound NdMn O3

NASA Astrophysics Data System (ADS)

Kumar, A.; Yusuf, S. M.; Ritter, C.

2017-07-01

A detailed neutron diffraction study on NdMn O3 infers that the low temperature transition at 15 K is due to the ordering of Nd sublattice moment with a (0 ,-Fy,0 ) type spin arrangement. Interestingly, the ordering of the Nd sublattice drives a reorientation (by 180∘) of the net ferromagnetic moment of the Mn sublattice along the b axis. Such a Mn spin reorientation from (Ax,Fy,0 ) (with an antiferromagnetic ordering temperature of 73 K) to (Ax,-Fy,0 ) at 15 K, explains the magnetization reversal phenomenon present in this perovskite compound at 15 K. Moreover at 15 K, significant crystallographic structural distortions in terms of temperature variations of lattice parameters and bond angles are found. A sign change in the temperature variation of magnetic entropy is also found at 15 K. The present study signifies the role of rare-earth (Nd) moment ordering in tuning various physical properties, such as magnetocaloric and magnetoelastic of the larger size (>0.912 Å ) R ion based R Mn O3 compounds.

Multiferroic properties in NdFeO3-PbTiO3 solid solutions

NASA Astrophysics Data System (ADS)

Kumar, Sunil; Pal, Jaswinder; Kaur, Shubhpreet; Agrawal, P.; Singh, Mandeep; Singh, Anupinder

2018-05-01

The x(NdFeO3) - 1-x(PbTiO3) where x = 0.2 solid solution was prepared using solid state reaction route. The X-ray diffraction (XRD) data reveals the single phase formation. The microstructure shows grain growth with lesser porosity. The energy dispersive analysis confirms the presence of elements in stochiometric proportion. The polarization vs. Electric field loop estabilished a ferroelectric type behavior but lossy in nature. This lossy nature may be due to the presence of large leakage current in solid solution. The Magnetization vs. Magnetic field plot exhibits a unsaturated hysteriss loop indicates that the sample is not purely ferromagnetic.

Thin films sputtered from Ba{sub 2}NdFeNb{sub 4}O{sub 15} multiferroic targets on BaFe{sub 12}O{sub 19} coated substrates

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bodeux, Romain; Univ. Bordeaux, ICMCB, UPR 9048, F-33600 Pessac; Michau, Dominique, E-mail: dominique.michau@icmcb.cnrs.fr

2016-09-15

Highlights: • Synthesis of Ba{sub 2}NdFeNb{sub 4}O{sub 15}/BaFe{sub 12}O{sub 19} (BaM) heterostructures by RF magnetron sputtering. • Growth of TTB layer were retained regardless of the underlayer (Pt bottom electrode or BaM). • Dielectric and magnetic properties were obtained from the Pt/TTB/BaM/Pt stacks. - Abstract: Ba{sub 2}NdFeNb{sub 4}O{sub 15} tetragonal tungsten bronze (TTB)/BaFe{sub 12}O{sub 19} (BaM) hexaferrite bilayers have been grown by RF magnetron sputtering on Pt/TiO{sub 2}/SiO{sub 2}/Si (PtS) substrates. The BaM layer is textured along (0 0 1) while the TTB layer is multioriented regardless of the PtS or BaM/PtS substrate. Dielectric properties of TTB films are similarmore » to those of bulk, i.e., ε ∼ 150 and a magnetic hysteresis loop is obtained from TTB/BaM bilayers, thanks to the BaM component. This demonstrates the possibility of transferring to 2 dimensional structures the composite multiferroic system TTB/BaM previously identified in 3 dimensional bulk ceramics.« less

Lanthanite-(Nd), Nd2(CO3)3·8H2O

PubMed Central

Morrison, Shaunna M.; Andrade, Marcelo B.; Wenz, Michelle D.; Domanik, Kenneth J.; Downs, Robert T.

2013-01-01

Lanthanite-(Nd), ideally Nd2(CO3)3·8H2O [dineodymium(III) tricarbonate octa­hydrate], is a member of the lanthanite mineral group characterized by the general formula REE 2(CO3)3·8H2O, where REE is a 10-coordinated rare earth element. Based on single-crystal X-ray diffraction of a natural sample from Mitsukoshi, Hizen-cho, Karatsu City, Saga Prefecture, Japan, this study presents the first structure determination of lanthanite-(Nd). Its structure is very similar to that of other members of the lanthanite group. It is composed of infinite sheets made up of corner- and edge-sharing of two NdO10-polyhedra (both with site symmetry ..2) and two carbonate triangles (site symmetries ..2 and 1) parallel to the ab plane, and stacked perpendicular to c. These layers are linked to one another only through hydrogen bonding involving the water mol­ecules. PMID:23476479

Crystalline and magnetooptical characteristics of (Tb,Bi)3(Fe,Ga)5O12 deposited on (Y,Nd)3Al5O12

NASA Astrophysics Data System (ADS)

Morimoto, Ryohei; Goto, Taichi; Nakamura, Yuichi; Boey Lim, Pang; Uchida, Hironaga; Inoue, Mitsuteru

2018-06-01

We prepared Bi- and Ga-substituted Tb3Fe5O12 (BiGa:TIG) films on a Nd-substituted Y3Al5O12 (Nd:YAG) single crystal substrate by pulsed laser deposition, and investigated their magnetic, optical, and magnetooptical properties. A BiGa:TIG film deposited with a substrate temperature of 700 °C shows the easy axis of magnetization along the out-of-plane direction of the film and the Faraday rotation angle of 900°/cm at a wavelength of 1064 nm. The epitaxial growth of the film is confirmed by X-ray diffraction analysis.

Reconstructing the evolution of the submarine Monterey Canyon System from Os, Nd, and Pb isotopes in hydrogenetic Fe-Mn crusts

USGS Publications Warehouse

Conrad, T.A.; Nielsen, S.G.; Peucker-Ehrenbrink, Bernhard; Blusztajn, J.; Winslow, D.; Hein, James; Paytan, A.

2017-01-01

The sources of terrestrial material delivered to the California margin over the past 7 Myr were assessed using 187Os/188Os, Nd, and Pb isotopes in hydrogenetic ferromanganese crusts from three seamounts along the central and southern California margin. From 6.8 to 4.5 (± 0.5) Ma, all three isotope systems show more radiogenic values at Davidson Seamount, located near the base of the Monterey Canyon System, than in Fe-Mn crusts from the more remote Taney and Hoss seamounts. At the Taney seamounts, approximately 225 km farther offshore from Davidson Seamount, 187Os/188Os values, but not Pb and Nd isotope ratios, also deviate from the Cenozoic seawater curve towards more radiogenic values from 6.8 to 4.5 (± 0.5) Ma. However, none of the isotope systems in Fe-Mn crusts deviate from seawater at Hoss Seamount located approximately 450 km to the south. The regional gradients in isotope ratios indicate that substantial input of dissolved and particulate terrestrial material into the Monterey Canyon System is responsible for the local deviations in the seawater Nd, Pb, and Os isotope compositions from 6.8 to 4.5 (± 0.5) Ma. The isotope ratios recorded in Fe-Mn crusts are consistent with a southern Sierra Nevada or western Basin and Range provenance of the terrestrial material which was delivered by rivers to the canyon. The exhumation of the modern Monterey Canyon must have begun between 10 and 6.8 ± 0.5 Ma, as indicated by our data, the age of incised strata, and paleo-location of the Monterey Canyon relative to the paleo-coastline.

Reconstructing the Evolution of the Submarine Monterey Canyon System From Os, Nd, and Pb Isotopes in Hydrogenetic Fe-Mn Crusts

NASA Astrophysics Data System (ADS)

Conrad, T. A.; Nielsen, S. G.; Peucker-Ehrenbrink, B.; Blusztajn, J.; Winslow, D.; Hein, J. R.; Paytan, A.

2017-11-01

The sources of terrestrial material delivered to the California margin over the past 7 Myr were assessed using 187Os/188Os, Nd, and Pb isotopes in hydrogenetic ferromanganese crusts from three seamounts along the central and southern California margin. From 6.8 to 4.5 (±0.5) Ma, all three isotope systems show more radiogenic values at Davidson Seamount, located near the base of the Monterey Canyon System, than in Fe-Mn crusts from the more remote Taney and Hoss Seamounts. At the Taney Seamounts, approximately 225 km farther offshore from Davidson Seamount, 187Os/188Os values, but not Pb and Nd isotope ratios, also deviate from the Cenozoic seawater curve toward more radiogenic values from 6.8 to 4.5 (±0.5) Ma. However, none of the isotope systems in Fe-Mn crusts deviate from seawater at Hoss Seamount located approximately 450 km to the south. The regional gradients in isotope ratios indicate that substantial input of dissolved and particulate terrestrial material into the Monterey Canyon System is responsible for the local deviations in the seawater Nd, Pb, and Os isotope compositions from 6.8 to 4.5 (±0.5) Ma. The isotope ratios recorded in Fe-Mn crusts are consistent with a southern Sierra Nevada or western Basin and Range provenance of the terrestrial material which was delivered by rivers to the canyon. The exhumation of the modern Monterey Canyon must have begun between 10 and 6.8 ± 0.5 Ma, as indicated by our data, the age of incised strata, and paleo-location of the Monterey Canyon relative to the paleo-coastline.

Site-preference and valency for rare-earth sites in (R-Ce)2Fe14B magnets

DOE Office of Scientific and Technical Information (OSTI.GOV)

Alam, Aftab; Khan, Mahmud; McCallum, R. W.

2013-01-28

Rare-earth (R) permanent magnets of R2Fe14B have technological importance due to their high energy products, and they have two R-sites (Wyckoff 4f and 4g, with four-fold multiplicity) that affect chemistry and valence. Designing magnetic behavior and stability via alloying is technologically relevant to reduce critical (expensive) R-content while retaining key properties; cerium, an abundant (cheap) R-element, offers this potential. We calculate magnetic properties and Ce site preference in (R1-xCex)2Fe14B [R=La,Nd] using density functional theory (DFT) methods—including a DFT+U scheme to treat localized 4f-electrons. Fe moments compare well with neutron data—almost unaffected by Hubbard U, and weakly affected by spin-orbit coupling.more » In La2Fe14B, Ce alloys for 0 ≤ x ≤ 1 and prefers smaller R(4f) sites, as observed, a trend we find unaffected by valence. Whereas, in Nd2Fe14B, Ce is predicted to have limited alloying (x ≤ 0.3) with a preference for larger R(4g) sites, resulting in weak partial ordering and segregation. The Curie temperatures versus x for (Nd,Ce) were predicted for a typical sample processing and verified experimentally.« less

Ultra-high precision 142Nd/144Nd measurements of the Proterozoic and implications for mixing in the Earth's mantle through time

NASA Astrophysics Data System (ADS)

Hyung, E.; Jacobsen, S. B.

2017-12-01

The decay of 146Sm to 142Nd is an excellent a tracer for early silicate differentiation events in the terrestrial planets, as the Sm/Nd ratio is usually fractionated during mantle partial melting and magma ocean crystallization. The short half-life (103 or 68 Ma) renders the system extinct within the first 500 Ma of Solar System formation. Samples with 142Nd/144Nd ratios that are substantially different from the bulk silicate Earth value of 142Nd/144Nd provide clear evidence for mantle differentiation in the Hadean. Published data for the 3.4 to 3.8 Ga old Isua supracrustal rocks and dykes have demonstrated both positive and negative 142Nd/144Nd anomalies (30 ppm range) providing clear evidence for Hadean enriched and depleted mantle reservoirs. In contrast, no 142Nd/144Nd anomalies have been found in modern day terrestrial samples with data that have 2σ uncertainties of about 5 ppm or more. Last year we reported improvements in 142Nd/144Nd measurements, using our IsotopX thermal ionization mass spectrometer, and obtained reproducibility of 142Nd/144Nd ratios to better than 2 ppm at the 2σ level. With this external reproducibility we found that all except one modern mantle-derived basalt had within error identical 142Nd/144Nd ratios. One sample is about 3.4 ppm lower than the rest of the modern basalt samples, providing evidence for some limited Hadean mantle differentiation signatures preserved up to present. We have also measured 142Nd/144Nd ratios for Proterozoic and Phanerozoic samples, whose ages range from 300 Ma to 2 Ga, to better than 2 ppm external reproducibility (2σ). Most of these samples also have 142Nd/144Nd ratios that cluster around the modern day value, but there are some samples that are either marginally high by 2 ppm or low by 2 ppm. Thus, while a 20 to 30 ppm range in 142Nd/144Nd is well resolved in the Archean, such large variability is not present in the Proterozoic and Phanerozoic. The relatively rapid changeover at the end of the Archean

Hadean silicate differentiation preserved by anomalous 142Nd/144Nd ratios in the Réunion hotspot source

NASA Astrophysics Data System (ADS)

Peters, Bradley J.; Carlson, Richard W.; Day, James M. D.; Horan, Mary F.

2018-03-01

Active volcanic hotspots can tap into domains in Earth’s deep interior that were formed more than two billion years ago. High-precision data on variability in tungsten isotopes have shown that some of these domains resulted from differentiation events that occurred within the first fifty million years of Earth history. However, it has not proved easy to resolve analogous variability in neodymium isotope compositions that would track regions of Earth’s interior whose composition was established by events occurring within roughly the first five hundred million years of Earth history. Here we report 142Nd/144Nd ratios for Réunion Island igneous rocks, some of which are resolvably either higher or lower than the ratios in modern upper-mantle domains. We also find that Réunion 142Nd/144Nd ratios correlate with helium-isotope ratios (3He/4He), suggesting parallel behaviour of these isotopic systems during very early silicate differentiation, perhaps as early as 4.39 billion years ago. The range of 142Nd/144Nd ratios in Réunion basalts is inconsistent with a single-stage differentiation process, and instead requires mixing of a conjugate melt and residue formed in at least one melting event during the Hadean eon, 4.56 billion to 4 billion years ago. Efficient post-Hadean mixing nearly erased the ancient, anomalous 142Nd/144Nd signatures, and produced the relatively homogeneous 143Nd/144Nd composition that is characteristic of Réunion basalts. Our results show that Réunion magmas tap into a particularly ancient, primitive source compared with other volcanic hotspots, offering insight into the formation and preservation of ancient heterogeneities in Earth’s interior.

An animal model for Norrie disease (ND): gene targeting of the mouse ND gene.

PubMed

Berger, W; van de Pol, D; Bächner, D; Oerlemans, F; Winkens, H; Hameister, H; Wieringa, B; Hendriks, W; Ropers, H H

1996-01-01

In order to elucidate the cellular and molecular processes which are involved in Norrie disease (ND), we have used gene targeting technology to generate ND mutant mice. The murine homologue of the ND gene was cloned and shown to encode a polypeptide that shares 94% of the amino acid sequence with its human counterpart. RNA in situ hybridization revealed expression in retina, brain and the olfactory bulb and epithelium of 2 week old mice. Hemizygous mice carrying a replacement mutation in exon 2 of the ND gene developed retrolental structures in the vitreous body and showed an overall disorganization of the retinal ganglion cell layer. The outer plexiform layer disappears occasionally, resulting in a juxtaposed inner and outer nuclear layer. At the same regions, the outer segments of the photoreceptor cell layer are no longer present. These ocular findings are consistent with observations in ND patients and the generated mouse line provides a faithful model for study of early pathogenic events in this severe X-linked recessive neurological disorder.

Anomalous magnetoelastic behaviour near morphotropic phase boundary in ferromagnetic Tb 1-xNd xCo 2 system

DOE PAGES

Murtaza, Adil; Yang, Sen; Zhou, Chao; ...

2016-08-04

In this study, we report a morphotropic phase boundary (MPB) involved ferromagnetic system Tb 1-xNd xCo 2 and reveal the corresponding structural and magnetoelastic properties of this system. With high resolution synchrotron X-ray diffractometry, the crystal structure of the TbCo 2-rich side is detected to be rhombohedral and that of NdCo 2-rich side is tetragonal below their respective Curie temperatures TC. The MPB composition Tb 0.35Nd 0.65Co 2 corresponds to the coexistence of the rhombohedral phase (R-phase) and tetragonal phase ( T-phase). Contrary to previously reported MPB involved ferromagnetic systems, the MPB composition of Tb 0.35Nd 0.65Co 2 shows minimummore » magnetization which can be understood as compensation of sublattice moments between the R-phase and the T-phase. Furthermore, magnetostriction of Tb 1-xNd xCo 2 decreases with increasing Nd concentration until x = 0.8 and then increases in the negative direction with further increasing Nd concentration; the optimum point for magnetoelastic properties lies towards the rhombohedral phase. Finally, our work not only shows an anomalous type of ferromagnetic MPB but also provides an effective way to design functional materials.« less

Corrosion Protection Properties of PPy-ND Composite Coating: Sonoelectrochemical Synthesis and Design of Experiment

NASA Astrophysics Data System (ADS)

Ashassi-Sorkhabi, H.; Bagheri, R.; Rezaei-Moghadam, B.

2016-02-01

In this research, the nanocomposite coatings comprising the polypyrrole-nanodiamond, PPy-ND, on St-12 steel electrodes were electro-synthesized using in situ polymerization process under ultrasonic irradiation. The corrosion protection performance and morphology characterization of prepared coatings were investigated by electrochemical methods and scanning electron microscopy, SEM, respectively. Also, the experimental design was employed to determine the best values considering the effective parameters such as the concentration of nanoparticles, the applied current density and synthesis time to achieve the most protective films. A response surface methodology, RSM, involving a central composite design, CCD, was applied to the modeling and optimization of the PPy-ND nanocomposite deposition. Pareto graphic analysis of the parameters indicated that the applied current density and some of the interactions were effective on the response. The electrochemical results proved that the embedment of diamond nanoparticle, DNP, improves the corrosion resistance of PPy coatings significantly. Therefore, desirable correlation exists between predicted data and experimental results.

Changes in Holocene to LGM water mass stratification near Southern Africa inferred from Nd isotopes

NASA Astrophysics Data System (ADS)

Jones, K. M.; Goldstein, S. L.; Hemming, S. R.; Hall, I. R.; Zahn, R.

2009-12-01

Global thermohaline circulation (THC) is an important component of the climate system that initiates or amplifies abrupt climate change. A major driver of THC is the formation of North Atlantic Deep Water (NADW), which is sandwiched by northward flowing Southern Ocean water masses as it is advected southward. An important exit route of NADW out of the South Atlantic is through flow around the southern tip of Africa, which makes the South African Margin an excellent location to investigate changes in THC and water mass stratification through time. We measured the Nd isotopes of modern seawater from three depth profiles collected along the South African Margin, which were collected on RSS Charles Darwin Cruise 154. All seawater profiles show a similar pattern with higher ɛNd values at intermediate depths (ɛNd ~ -9.5 at 600-1200m), lower values for the core of NADW (ɛNd ~ -11.5 at 2000-3500m), and higher values in the deepest waters sampled (ɛNd -9.8 at 4150m). This pattern is consistent with conservative mixing of major North Atlantic and Southern Ocean end-member water masses and is not consistent with inputs from, or exchange with margin sediments, for most depths. We also measured the Nd isotopes of multiple sedimentary archives in proximal Holocene coretop sediments collected from depths spanning intermediate to deep/bottom waters. The Nd isotopes of a fish tooth, several foram coating leachates, and multiple bulk sediment Fe-Mn leachates display the same pattern as the local seawater. We had no seawater for comparison with our deepest core (VM19-224; depth ~ 4600m), but the eNd value from it (ɛNd = -8.4) is consistent with Antarctic Bottom Water (ɛNd ~ -8.5). These results suggest: (1) that Nd isotopes of seawater in the region behave conservatively; (2) that the local margin sediments faithfully record the Nd isotope composition of the waters they are bathed in and (3) this “ground-truthing” implies that it is valid to use Nd isotopes as a circulation

Nonexponential London Penetration Depth of FeAs-Based Superconducting RFeAsO[subscript 0.9]F[subscript 0.1] (R=La, Nd) Single Crystals

DOE Office of Scientific and Technical Information (OSTI.GOV)

Martin, C.; Tillman, M.E.; Kim, H.

2009-07-31

The superconducting penetration depth {lambda}(T) has been measured in RFeAsO{sub 0.9}F{sub 0.1} (R=La, Nd) single crystals (R-1111). In Nd-1111, we find an upturn in {lambda}(T) upon cooling and attribute it to the paramagnetism of the Nd ions, similar to the case of the electron-doped cuprate Nd-Ce-Cu-O. After the correction for paramagnetism, the London penetration depth variation is found to follow a power-law behavior, {Delta}{lambda}L(T) {proportional_to} T{sup 2} at low temperatures. The same T{sup 2} variation of {lambda}(T) was found in nonmagnetic La-1111 crystals. Analysis of the superfluid density and of penetration depth anisotropy over the full temperature range is consistentmore » with two-gap superconductivity. Based on this and on our previous work, we conclude that both the RFeAsO (1111) and BaFe{sub 2}As{sub 2} (122) families of pnictide superconductors exhibit unconventional two-gap superconductivity.« less

Repetitively Q-switched Nd:BeL lasers

NASA Technical Reports Server (NTRS)

Degnan, J.; Birnbaum, M.; Deshazer, L. G.

1979-01-01

The thermal and mechanical characteristics which will ultimately limit the performance of Nd:BeL at high average power levels were investigated. The output beam characteristics (pulse width, peak power, beam dimensions and collimation) were determined at high repetition rates for both Nd:BeL and Nd:YAG. The output of Nd:BeL was shown to exceed that of Nd:YAG by a factor of 2.7 at low Q-switched repetition rates (1 Hz). This result follows from the smaller stimulated emission cross section of x-axis Nb:BeL compared to that of NdYAG by the same factor. At high repetition rates (10 Hz) the output of Nd:Bel falls to a level of three-fifths of its low repetition rate value while under similar tests the output of Nd:YAG remains essentially constant. A comparison of the measured values of the elasto-optic coefficients, the dn/dT values and the linear expansion coefficients for BeL and YAG failed to provide an explanation for the performance of BeL; however, thermal lensing was observed in Nd:BeL. Results imply that the output of a high repetition rate Q-switched Nd:BeL laser (high thermal loading) could be dramatically increased by utilization of a resonator design to compensate for the thermal lensing effects.

Hybrid organic-inorganic connectivity of NdIII(pyrazine-N,N'-dioxide)[CoIII(CN)6]3- coordination chains for creating near-infrared emissive Nd(iii) showing field-induced slow magnetic relaxation.

PubMed

Chorazy, Szymon; Charytanowicz, Tomasz; Wang, Junhao; Ohkoshi, Shin-Ichi; Sieklucka, Barbara

2018-05-29

A near-infrared emissive and magnetically anisotropic Nd(iii) complex is formed within a hybrid organic-inorganic {[NdIII(pzdo)(H2O)4][CoIII(CN)6]}·0.5(pzdo)·4H2O (1) (pzdo = pyrazine-N,N'-dioxide) ladder chain built of coexisting Nd-pzdo-Nd and Nd-NC-Co molecular bridges. 1 reveals two NdIII-centered properties, a field-induced slow magnetic relaxation of a single-ion origin with a thermal energy barrier of ΔE/kB = 51(2) K at Hdc = 1 kOe, and a near-infrared fluorescence sensitized by organic and inorganic linkers.

a Dual Proxy of Oceanic Weathering Inputs: Rare Earth Element Patterns and nd Isotopes from Metalliferous Sediment Cores

NASA Astrophysics Data System (ADS)

Sherrell, R. M.; Wright, J. D.; Hamelin, B.; Michard, A.

2002-12-01

Recent interest in reconstructing Nd isotopic distributions in the past ocean using Fe-Mn crusts, oxide coatings on sediment particles, foraminifera shells and fish teeth has raised questions about relative influence of water mass mixing vs. variations in weathering input. We have explored the utility of hydrothermal metalliferous sediments for generating high-resolution records of both Nd isotopes and rare earth element (REE) patterns in deepwater. We present a 135kyr record of high precision REE data, preliminary Nd isotope ratios, and δ18O from a 2.3 m core collected at 3180m at 11S on the East Pacific Rise (EPR). REEs are dominated (\\>96%) by seawater REEs adsorbed to Fe particles in these metalliferous carbonates; the hydrothermal REE source itself is negligible. Downcore variations in Nd/Er (proxy for light/heavy pattern fractionation) are not large (10%) but are easily quantified by our ICP-MS method (precision 1%), and reproducibly correspond to δ18O shifts. The largest Nd/Er excusions occur during deglaciations, e.g. Nd/Er=5.1 to 4.4 mol/mol between glacial MIS 6 and interglacial MIS 5e. If these variations reflect composition of ambient deepwater, then the results are opposite those expected by reduced influence of Atlantic component water (high Nd/Er) during glacials. Prelimininary ɛNd values for samples taken at Nd/Er extrema in MIS 1, 2, 5e and 6 are nearly invarient at -3.5+/-0.4, in excellent agreement with modern water column ɛNd for Pacific deepwater at this depth. Thus, while paleo-ɛNd shows virtually no change over 135kyr, REE pattern does carry information, but not, we believe, about water mass mixing changes. We suggest instead that Nd/Er reflects climatically-influenced weathering inputs to the Pacific REE pool. We propose a sea-level-driven mechanism: glacial low sea-stand reduces the extent of estuarine environments in which the light-REE-depleted seawater pattern is imparted, causing 1) more direct input of unfractionated crustal REE

Ultra-small Nd3+-doped nanoparticles as near-infrared luminescent biolabels of hemin in bacteria

NASA Astrophysics Data System (ADS)

Xi, Yonglan; Chang, Zhizhou; Ye, Xiaomei; Huang, Hongying; Huang, Yanan; Xiao, Qingbo; Lin, Hongzhen

2016-01-01

Near-infrared (NIR) luminescent Nd3+-doped nanoparticles (NPs) have attracted considerable attention in bioimaging and biodetection. Here, we demonstrate sub-6 nm NaGdF4:Nd3+,Fe3+ NPs as luminescent biolabels of hemin molecules that act as the exogenous electron carriers in microbial communities. Contrary to the severe quenching of the visible luminescence for either upconverting or downconverting NPs, the Nd3+-doped NPs show superior properties in avoiding the optical absorption of hemin within the UV and visible spectral regions. A detailed examination showed that the Nd3+-doped NPs exhibit no obvious toxic effects on the microbial communities and show scarce influence on the characteristics of labeled hemin molecules in enhancing the reducing power of the fermentation system. More importantly, by monitoring the NIR luminescence of Nd3+-doped NPs, the selective accumulation of exogenous electron carriers in bacteria that are lacking reducing power has been revealed for the first time. The application of Nd3+-doped NPs as biolabels in bacteria would provide new opportunities for further unravelling the role of exogenous electron carriers in anaerobic digestion.Near-infrared (NIR) luminescent Nd3+-doped nanoparticles (NPs) have attracted considerable attention in bioimaging and biodetection. Here, we demonstrate sub-6 nm NaGdF4:Nd3+,Fe3+ NPs as luminescent biolabels of hemin molecules that act as the exogenous electron carriers in microbial communities. Contrary to the severe quenching of the visible luminescence for either upconverting or downconverting NPs, the Nd3+-doped NPs show superior properties in avoiding the optical absorption of hemin within the UV and visible spectral regions. A detailed examination showed that the Nd3+-doped NPs exhibit no obvious toxic effects on the microbial communities and show scarce influence on the characteristics of labeled hemin molecules in enhancing the reducing power of the fermentation system. More importantly, by

Sm-Nd in marine carbonates and phosphates - Implications for Nd isotopes in seawater and crustal ages

NASA Technical Reports Server (NTRS)

Shaw, H. F.; Wasserburg, G. J.

1985-01-01

The possibility of establishing a record of variations in the isotopic composition of Nd in seawater over geologic time is explored. To construct such a record, a phase must be identified which incorporated Nd with the same isotopic composition as seawater at the time of its formation, preserves that composition, and which is relatively common in sediments. To evaluate the suitability of carbonates and phosphates, the Rb, Sr, Sm, and Nd concentrations and the Nd and Sr isotopic composition of a variety of modern and ancient marine calcite, aragonite, and apatite samples have been measured and the results are presented and discussed.

Early Earth evolution: new insight from Sm and Nd isotopes in meteoritic inclusions

NASA Astrophysics Data System (ADS)

Bouvier, A.; Boyet, M.

2014-12-01

The interpretation of Sm-Nd systematics for the early Earth relies on knowing the composition of the silicate Earth and the 146Sm decay constant. We have measured both 146Sm-142Nd and 147Sm-143Nd internal systematics of four individual Calcium, Aluminum-rich Inclusions (CAIs), the first solids formed in the Solar System [1], from 3 different carbonaceous chondrites from the CV3 group: Allende, Northwest Africa (NWA) 2364 and NWA 6991. Results obtained on NWA 6991 plot on a well-defined mineral and bulk isochron with a Solar System initial 146Sm/144Sm ratio of 0.0070 ±0.0024. This ratio is more consistent with the ratio defined from internal isochrons of differentiated meteorites using the half-life of 103 Ma for 146Sm [2], instead of the value obtained considering the half-life of 68 Ma [3]. On the basis of nucleosynthethic anomalies in Sm and Nd isotopes [4], the ordinary (O) and enstatite (E) chondrites remain potential candidates for the Earth's building blocks. OC have an average deficit of -18±3 ppm relative to modern terrestrial 142Nd/144Nd, whereas EC range from the OC to the terrestrial values [4-6]. Sm stable isotope compositions of the analyzed CAIs indicate that galactic cosmic rays did not affect the 142Nd/144Nd compositions, but deficits are found in the pure p-process 144Sm nuclide (-240 to -290 ppm/ standard). These deficits may translate to 142Nd deficits of a few ppm. NWA 6991 CAI 146Sm-142Nd internal isochron passes through a 142Nd/144Nd ratio of -6 ±6 ppm relative to the terrestrial standard at a chondritic 147Sm/144Nd of 0.1960. We note that this value is identical to the enstatite chondrite average and the 142Nd/144Nd ratio of the lunar mantle, as defined recently by [7] using a chondritic Sm/Nd and Lu/Hf for the bulk Moon. While the determination of the Sm-Nd reference parameters for the bulk Earth is still contentious, the difference in 142Nd/144Nd between modern terrestrial rocks and meteorites analyzed so far is <10ppm. [1] Bouvier and

A Mercury-like component of early Earth yields uranium in the core and high mantle (142)Nd.

PubMed

Wohlers, Anke; Wood, Bernard J

2015-04-16

Recent (142)Nd isotope data indicate that the silicate Earth (its crust plus the mantle) has a samarium to neodymium elemental ratio (Sm/Nd) that is greater than that of the supposed chondritic building blocks of the planet. This elevated Sm/Nd has been ascribed either to a 'hidden' reservoir in the Earth or to loss of an early-formed terrestrial crust by impact ablation. Since removal of crust by ablation would also remove the heat-producing elements--potassium, uranium and thorium--such removal would make it extremely difficult to balance terrestrial heat production with the observed heat flow. In the 'hidden' reservoir alternative, a complementary low-Sm/Nd layer is usually considered to reside unobserved in the silicate lower mantle. We have previously shown, however, that the core is a likely reservoir for some lithophile elements such as niobium. We therefore address the question of whether core formation could have fractionated Nd from Sm and also acted as a sink for heat-producing elements. We show here that addition of a reduced Mercury-like body (or, alternatively, an enstatite-chondrite-like body) rich in sulfur to the early Earth would generate a superchondritic Sm/Nd in the mantle and an (142)Nd/(144)Nd anomaly of approximately +14 parts per million relative to chondrite. In addition, the sulfur-rich core would partition uranium strongly and thorium slightly, supplying a substantial part of the 'missing' heat source for the geodynamo.

A Mercury-like component of early Earth yields uranium in the core and high mantle 142Nd

NASA Astrophysics Data System (ADS)

Wohlers, Anke; Wood, Bernard J.

2015-04-01

Recent 142Nd isotope data indicate that the silicate Earth (its crust plus the mantle) has a samarium to neodymium elemental ratio (Sm/Nd) that is greater than that of the supposed chondritic building blocks of the planet. This elevated Sm/Nd has been ascribed either to a `hidden' reservoir in the Earth or to loss of an early-formed terrestrial crust by impact ablation. Since removal of crust by ablation would also remove the heat-producing elements--potassium, uranium and thorium--such removal would make it extremely difficult to balance terrestrial heat production with the observed heat flow. In the `hidden' reservoir alternative, a complementary low-Sm/Nd layer is usually considered to reside unobserved in the silicate lower mantle. We have previously shown, however, that the core is a likely reservoir for some lithophile elements such as niobium. We therefore address the question of whether core formation could have fractionated Nd from Sm and also acted as a sink for heat-producing elements. We show here that addition of a reduced Mercury-like body (or, alternatively, an enstatite-chondrite-like body) rich in sulfur to the early Earth would generate a superchondritic Sm/Nd in the mantle and an 142Nd/144Nd anomaly of approximately +14 parts per million relative to chondrite. In addition, the sulfur-rich core would partition uranium strongly and thorium slightly, supplying a substantial part of the `missing' heat source for the geodynamo.

Influence of Zr substitution on the stabilization of ThMn{sub 12}-type (Nd{sub 1−α}Zr{sub α})(Fe{sub 0.75}Co{sub 0.25}){sub 11.25}Ti{sub 0.75}N{sub 1.2−1.4} (α = 0–0.3) compounds

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sakuma, N.; Yano, M.; Kato, A.

2016-05-15

The influence of Zr substitution in ThMn{sub 12} compounds was investigated using strip casting alloys. It was found that Zr substitution stabilized (Nd{sub 1−α}Zr{sub α})(Fe{sub 0.75}Co{sub 0.25}){sub 11.25}Ti{sub 0.75}N{sub 1.2−1.4} (α = 0–0.3) compounds. Specifically, a reduction in the lattice constant along the a-axis was observed. Energy-dispersive X-ray spectroscopy mapping combined with Cs-corrected scanning transmission electron microscopy indicated that Zr atoms preferentially occupied Nd 2a sites. Both the magnetic anisotropy field and saturation polarization were maximum at Zr substitution ratio α = 0.1. The (Nd{sub 1−α}Zr{sub α})(Fe{sub 0.75}Co{sub 0.25}){sub 11.25}Ti{sub 0.75}N{sub 1.2−1.4} (α = 0–0.3) compounds displayed higher saturation polarizationmore » than Nd{sub 2}Fe{sub 14}B at high temperatures.« less

Site-preference and valency for rare-earth sites in (R-Ce)(2)Fe14B magnets

DOE Office of Scientific and Technical Information (OSTI.GOV)

Alam, A; Khan, M; McCallum, RW

2013-01-28

Rare-earth (R) permanent magnets of R2Fe14B have technological importance due to their high energy products, and they have two R-sites (Wyckoff 4f and 4g, with four-fold multiplicity) that affect chemistry and valence. Designing magnetic behavior and stability via alloying is technologically relevant to reduce critical (expensive) R-content while retaining key properties; cerium, an abundant (cheap) R-element, offers this potential. We calculate magnetic properties and Ce site preference in (R1-xCex)(2)Fe14B [R = La, Nd] using density functional theory (DFT) methods-including a DFT+U scheme to treat localized 4f-electrons. Fe moments compare well with neutron data-almost unaffected by Hubbard U, and weakly affectedmore » by spin-orbit coupling. In La2Fe14B, Ce alloys for 0 <= x <= 1 and prefers smaller R(4f) sites, as observed, a trend we find unaffected by valence. Whereas, in Nd2Fe14B, Ce is predicted to have limited alloying (x <= 0.3) with a preference for larger R(4g) sites, resulting in weak partial ordering and segregation. The Curie temperatures versus x for (Nd, Ce) were predicted for a typical sample processing and verified experimentally. (C) 2013 American Institute of Physics. [http://dx.doi.org/10.1063/1.4789527]« less

Draft Genome Sequence of Pseudoalteromonas sp. Strain ND6B, an Oil-Degrading Isolate from Eastern Mediterranean Sea Water Collected at a Depth of 1,210 Meters

DOE PAGES

Harris, Austin P.; Techtmann, Stephen M.; Stelling, Savannah C.; ...

2014-11-26

We report the draft genome of Pseudoalteromonas sp. strain ND6B, which is able to grow with crude oil as a carbon source. Strain ND6B was isolated from eastern Mediterranean Sea deep water at a depth of 1,210 m. The genome of strain ND6B provides insight into the oil-degrading ability of the Pseudoalteromonas species.

Magneto-optical spectra and electron structure of Nd0.5Gd0.5Fe3(BO3)4 single crystal

NASA Astrophysics Data System (ADS)

Malakhovskii, A. V.; Gnatchenko, S. L.; Kachur, I. S.; Piryatinskaya, V. G.; Sukhachev, A. L.; Temerov, V. L.

2016-03-01

Polarized absorption spectra and magnetic circular dichroism (MCD) spectra of Nd0.5Gd0.5Fe3(BO3)4 single crystal were measured in the range of 10000-21000 cm-1 and at temperatures 2-300 K. On the basis of these data, in the paramagnetic state of the crystal, the 4f states of the Nd3+ ion were identified in terms of the irreducible representations and in terms of | J , ±MJ 〉 wave functions of the free atom. The changes of the Landé factor during f-f transitions were found theoretically in the | J , ±MJ 〉 wave functions approximation and were determined experimentally with the help of the measured MCD spectra. In the majority of cases the experimentally found values are close to the theoretically predicted ones.

A New Dual Proxy of Oceanic Weathering Inputs: Rare Earth Element Patterns and Nd Isotopes From Metalliferous Sediment Cores

NASA Astrophysics Data System (ADS)

Sherrell, R.; Wright, J.; Michard, A.; Hamelin, B.

Recent interest in reconstructing Nd isotopic distributions in the past ocean using Fe- Mn crusts, oxide coatings on sediment particles, foraminifera shells and fish teeth has raised questions about relative influence of water mass mixing vs. variations in weath- ering input. We have explored the utility of hydrothermal metalliferous sediments for generating high-resolution records of both Nd isotopes and rare earth element (REE) patterns in deepwater. We present a 135kyr record of high precision REE data, pre- liminary Nd isotope ratios, and 18O from a 2.3 m core collected at 3180m at 11S on the East Pacific Rise (EPR). REEs are dominated ( 96%) by seawater REEs adsorbed to Fe particles in these metalliferous carbonates; the hydrothermal REE source itself is negligible. Downcore variations in Nd/Er (proxy for light/heavy pattern fractiona- tion) are not large (10%) but are easily quantified by our ICP-MS method (precision 1%), and reproducibly correspond to 18O shifts. The largest Nd/Er excusions occur during deglaciations, e.g. Nd/Er=5.1 to 4.4 mol/mol between glacial MIS 6 and inter- glacial MIS 5e. If these variations reflect composition of ambient deepwater, then the results are opposite those expected by reduced influence of Atlantic component water (high Nd/Er) during glacials. Prelimininary Nd values for samples taken at Nd/Er ex- trema in MIS 1, 2, 5e and 6 are nearly invarient at -3.5+/-0.4, in excellent agreement with modern water column Nd for Pacific deepwater at this depth. Thus, while paleo- Nd shows virtually no change over 135kyr, REE pattern does carry information, but not, we believe, about water mass mixing changes. We suggest instead that Nd/Er re- flects climatically-influenced weathering inputs to the Pacific REE pool. We propose a sea-level-driven mechanism: glacial low sea-stand reduces the extent of estuarine environments in which the light-REE-depleted seawater pattern is imparted, causing 1) more direct input of unfractionated crustal

Magnetic order of Nd5Pb3 single crystals

NASA Astrophysics Data System (ADS)

Yan, J.-Q.; Ochi, M.; Cao, H. B.; Saparov, B.; Cheng, J.-G.; Uwatoko, Y.; Arita, R.; Sales, B. C.; Mandrus, D. G.

2018-04-01

We report millimeter-sized Nd5Pb3 single crystals grown out of a Nd-Co flux. We experimentally study the magnetic order of Nd5Pb3 single crystals by measuring the anisotropic magnetic properties, electrical resistivity under high pressure up to 8 GPa, specific heat, and neutron single crystal diffraction. Two successive magnetic orders are observed at T N1  =  44 K and T N2  =  8 K. The magnetic cells can be described with a propagation vector k=(0.5, 0, 0) . Cooling below T N1, Nd1 and Nd3 order forming ferromagnetic stripes along the b-axis, and the ferromagnetic stripes are coupled antiferromagnetically along the a-axis for the k=(0.5, 0, 0) magnetic domain. Cooling below T N2, Nd2 orders antiferromagnetically to nearby Nd3 ions. All ordered moments align along the crystallographic c-axis. The magnetic order at T N1 is accompanied by a quick drop of electrical resistivity upon cooling and a lambda-type anomaly in the temperature dependence of specific heat. At T N2, no anomaly was observed in electrical resistivity but there is a weak feature in specific heat. The resistivity measurements under hydrostatic pressures up to 8 GPa suggest a possible phase transition around 6 GPa. Our first-principles band structure calculations show that Nd5Pb3 has the same electronic structure as does Y5Si3 which has been reported to be a one-dimensional electride with anionic electrons that do not belong to any atom. Our study suggests that R 5Pb3 (R  =  rare earth) can be a materials playground for the study of magnetic electrides. This deserves further study after experimental confirmation of the presence of anionic electrons.

Magnetic order of Nd5Pb3 single crystals.

PubMed

Yan, J-Q; Ochi, M; Cao, H B; Saparov, B; Cheng, J-G; Uwatoko, Y; Arita, R; Sales, B C; Mandrus, D G

2018-04-04

We report millimeter-sized Nd 5 Pb 3 single crystals grown out of a Nd-Co flux. We experimentally study the magnetic order of Nd 5 Pb 3 single crystals by measuring the anisotropic magnetic properties, electrical resistivity under high pressure up to 8 GPa, specific heat, and neutron single crystal diffraction. Two successive magnetic orders are observed at T N1   =  44 K and T N2   =  8 K. The magnetic cells can be described with a propagation vector [Formula: see text]. Cooling below T N1 , Nd1 and Nd3 order forming ferromagnetic stripes along the b-axis, and the ferromagnetic stripes are coupled antiferromagnetically along the a-axis for the [Formula: see text] magnetic domain. Cooling below T N2 , Nd2 orders antiferromagnetically to nearby Nd3 ions. All ordered moments align along the crystallographic c-axis. The magnetic order at T N1 is accompanied by a quick drop of electrical resistivity upon cooling and a lambda-type anomaly in the temperature dependence of specific heat. At T N2 , no anomaly was observed in electrical resistivity but there is a weak feature in specific heat. The resistivity measurements under hydrostatic pressures up to 8 GPa suggest a possible phase transition around 6 GPa. Our first-principles band structure calculations show that Nd 5 Pb 3 has the same electronic structure as does Y 5 Si 3 which has been reported to be a one-dimensional electride with anionic electrons that do not belong to any atom. Our study suggests that R 5 Pb 3 (R  =  rare earth) can be a materials playground for the study of magnetic electrides. This deserves further study after experimental confirmation of the presence of anionic electrons.

Redetermination of the Sm-Nd Age and Initial (Epsilon)Nd of Lunar Troctolite 76535: Implications for Lunar Crustal Development

NASA Technical Reports Server (NTRS)

Nyquist, Laurence E.; Shih, C.-Y.; Reese, Y. D.

2012-01-01

Lunar troctolite 76535 is an old lunar rock predating the era of the lunar cataclysmic bombardment, but its radiometrially determined ages have been discordant [1-3]. The most recent multi-chronometer study [4] gave preferred ages of 4226+/-35 Ma and 4236+/-15 Ma from a Pb-207/Pb-206 isochron and an U-Pb upper concordia intercept, resp. We derive an age of 4323+/-64 Ma from Sm-Nd data reported by [4] for the bulk rock and three mineral separates. They derived an age of approx.4.38 Ga from combined Rb-Sr data [3,4] by omitting data for olivine separates. Ar-39-Ar-40 ages of approx.4.2 Ga are summarized by [5]. New Sm-147-Nd-143 data presented here give an age of 4335+/-71 Ma in agreement with the Sm-Nd age from [4], whereas Sm-146-Nd-142 data give a model age T(sub LEW) = 4439+/-22 Ma. Further, initial (Epsilon)Nd-143 for 76535 conforms to the Nd-143 evolution expected in an urKREEP [6] reservoir, consistent with inheritance of urKREEP Sm-Nd systematics via assimilation. We show that urKREEP Sm-Nd systematics require the lunar initial (Epsilon)Nd-143 to exceed the Chondritic Uniform Reservoir (CHUR) value [7], but are consistent with evolution from initial (Epsilon)Nd-143 like that of the HED meteorite parent body as defined by a 4557+/-20 Ma internal isochron for the cumulate eucrites Y-980433 and Y- 980318 [8].

Magnetic texturing due to the partial ordering of Fe+3 and Cu+2 in NdBaCuFeO5

NASA Astrophysics Data System (ADS)

Pissas, M.

2017-06-01

The crystal and magnetic structure of the oxygen deficient double perovskite NdBaCuFeO5 was studied, using neutron powder diffraction data. The structure was refined from neutron powder diffraction data using the space groups P 4 / mmm and P 4 mm . For 2K ⩽ T ⩽TN2 = 260K three families of magnetic Bragg peaks exist. These peaks can be indexed with commensurate propagation vectors k1 =[1/2 1/2 1/2], k2 =[1/2 1/2 0] and the incommensurate k3 =[1/2 1/2 0.4]. Above TN2 only magnetic Bragg peaks originated from k1 and k2 propagation, were observed. The incommensurate magnetic structure can be attributed to a circular inclined spiral ordering as in YBaCuFeO5 compound.

Reproduced multi-domain regions during demagnetization in Nd2Fe14B sintered magnets with different average grain sizes

NASA Astrophysics Data System (ADS)

Kobayashi, Kurima; Nimura, You-ta; Urushibata, Kimiko; Hayakawa, Kazuo

2018-04-01

We prepared five Nd2Fe14B sintered magnets with similar saturation polarizations (Js) of 1.38-1.43 T and anisotropy fields (Ha) of 6.76-8.52 T, but different grain sizes (DAV) of 3.1-8.4 μm in diameter and obviously different coercivities (μ0Hc) of 0.8-1.6 T. The observed difference in coercivity could not be explained by the Kronmüller equation, because of the similar Ha values and similar chemical compositions and microstructures resulting from similar preparation method except DAV. The Hc values themselves, however, are inversely proportional to DAV. During demagnetization after magnetization in a 5 T pulse field, domain wall motion (DWM) was observed except in the sample with μ0Hc = 1.6 T by using our step method. The DWM was also confirmed by susceptibility measurements using a custom-built vibrating sample magnetometer, and DWM was generated in the reproduced multi-domain regions (RMDR) during demagnetization. The magnitude of DWM as a polarization change in the RMDR was inversely proportional to the coercivities of the samples. Therefore, it should be considered that the propagation of the nucleated region through the grain boundary, which corresponds to the expansion process in previous studies, was different caused by, first, the difference in DAV, and, second, in grain boundary state which was varied by difference in final annealing temperature.

The assessment of REE patterns and 143Nd/ 144Nd ratios in fish remains

NASA Astrophysics Data System (ADS)

Grandjean, Patricia; Cappetta, Henri; Michard, Annie; Albarède, Francis

1987-07-01

The REE content and isotopic composition of Sr and Nd have been determined in fish teeth ranging in age from the Trias to the present and from various localities mostly around the Atlantic. These measurements have been carried out on Selachian and Teleost remains from the same locality in Togo and show no appreciable difference, which suggests, with the help of a mass balance calculation of the Ce anomaly, that diagenetic effects are not responsible for the REE enrichment of biogenic phosphates. One group of fossil teeth has about 3 times the REE abundances of shale and a shale-normalized pattern with a minimum at Sm: it is thought to reflect deposition in the open-sea environment. A second group has REE concentration about 10 times higher than the first group with either a regular light REE enrichment or, more frequently, a maximum in the middle REE, both being probably indicative of deposition in estuarine or near-shore conditions. The shape of the REE spectra and the size of the Ce anomaly can be used semi-quantitatively to determine the depth of deposition. The results presented here on Late Cretaceous/Eocene fish teeth samples from Morocco reflect an increasing influx of deep waters with a lowLa/Yb ratio and strong negative Ce anomaly, which agrees well with the evolution of sediment chemistry and microfauna associations. In contrast, ɛ Nd is typical of the water mass in which the fish debris decayed. Examples of nearly isolated basins identified with Nd isotopes include the South Atlantic prior to the Lutetian (ɛ Nd ≈ -13.5), the Miocene Persian Gulf (ɛ Nd = -3.1), and Bolivia during the Late Cretaceous (ɛ Nd = -12.8). Togo and Guinea-Bissau results suggest that, in the South Atlantic, the meridional oceanic circulation had not started before 45 Ma ago. Combination of REE andɛ Nd data suggests that the assignment of Jurassic-Cretaceous samples measured so far to open-sea water masses is still ambiguous.

Structural, electrical and magnetic study of Nd-Ni substituted W-type Hexaferrite

NASA Astrophysics Data System (ADS)

Khan, Imran; Sadiq, Imran; Ali, Irshad; Rana, Mazhar-Ud-Din; Najam-Ul-Haq, Muhammad; Shah, Afzal; Shakir, Imran; Naeem Ashiq, Muhammad

2016-01-01

A series of Nd-Ni substituted W-type hexaferrites with composition Sr1-xNdxCo2NiyFe16-yO27 (where x=0.0, 0.025, 0.050, 0.075, 0.1 and y=0.0, 0.25, 0.50, 0.75, 1) has been prepared by the chemical co-precipitation method. The effect of rare earth Nd substitution at strontium site while Ni at iron site on microstructure, electrical and magnetic properties has been investigated. All the XRD patterns of the synthesized materials show single W-type hexagonal phase without any other intermediate phases. SEM images show that the particles are homogeneous and hexagonal platelet-like shape. DC electrical resistivity measurements were carried out in temperature range of 298-673 K showing metal-to-semiconductor transition when doped with Nd-Ni. The magnetic properties such as saturation magnetization, remanence, squareness ratio and coercivity were calculated from hysteresis loops and were observed to increase with the increase in Nd-Ni concentration up to a certain substitution level which is beneficial for high density recording media.

146Sm-142Nd systematics measured in enstatite chondrites reveals a heterogeneous distribution of 142Nd in the solar nebula.

PubMed

Gannoun, Abdelmouhcine; Boyet, Maud; Rizo, Hanika; El Goresy, Ahmed

2011-05-10

The short-lived (146)Sm-(142)Nd chronometer (T(1/2) = 103 Ma) is used to constrain the early silicate evolution of planetary bodies. The composition of bulk terrestrial planets is then considered to be similar to that of primitive chondrites that represent the building blocks of rocky planets. However for many elements chondrites preserve small isotope differences. In this case it is not always clear to what extent these variations reflect the isotope heterogeneity of the protosolar nebula rather than being produced by the decay of parent isotopes. Here we present Sm-Nd isotopes data measured in a comprehensive suite of enstatite chondrites (EC). The EC preserve (142)Nd/(144)Nd ratios that range from those of ordinary chondrites to values similar to terrestrial samples. The EC having terrestrial (142)Nd/(144)Nd ratios are also characterized by small (144)Sm excesses, which is a pure p-process nuclide. The correlation between (144)Sm and (142)Nd for chondrites may indicate a heterogeneous distribution in the solar nebula of p-process matter synthesized in supernovae. However to explain the difference in (142)Nd/(144)Nd ratios, 20% of the p-process contribution to (142)Nd is required, at odds with the value of 4% currently proposed in stellar models. This study highlights the necessity of obtaining high-precision (144)Sm measurements to interpret properly measured (142)Nd signatures. Another explanation could be that the chondrites sample material formed in different pulses of the lifetime of asymptotic giant branch stars. Then the isotope signature measured in SiC presolar would not represent the unique s-process signature of the material present in the solar nebula during accretion.

Collaborative study for the establishment of the 2(nd) International Standard for Bleomycin Complex A2/B2.

PubMed

Jorajuria, S; Raphalen, C; Dujardin, V; Daas, A

2015-01-01

Organization (WHO) International Standard (IS) for bleomycin complex A2/B2. Eight laboratories from different countries participated. Potencies of the candidate material were estimated by microbiological assays with sensitive micro-organisms. To ensure continuity between consecutive batches, the 1(st) IS for bleomycin complex A2/B2 was used as a reference. Based on the results of the study, the 2(nd) IS for bleomycin complex A2/B2 was adopted at the meeting of the WHO Expert Committee for Biological Standardization (ECBS) in 2014 with an assigned potency of 12 500 International Units (IU) per vial. The 2(nd) IS for bleomycin complex A2/B2 is available from the European Directorate for the Quality of Medicines & HealthCare (EDQM).

Structural chemistry and magnetic properties of Nd{sub 18}Li{sub 8}Fe{sub 4}M′O{sub 39} (M′=Al, Ga) and La{sub 18}Li{sub 8}Fe{sub 4.5}In{sub 0.5}O{sub 39}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Thammajak, Nirawat; Battle, Peter D., E-mail: peter.battle@chem.ox.ac.uk; Brown, Catherine

Polycrystalline samples of Nd{sub 18}Li{sub 8}Fe{sub 4}M′O{sub 39} (M′=Al, Ga) and La{sub 18}Li{sub 8}Fe{sub 4.5}In{sub 0.5}O{sub 39} have been prepared by the ceramic method and characterised by neutron diffraction and magnetometry. All three compounds adopt a cubic structure (space group Pm3{sup ¯}n, a ∼12 Å) based on intersecting 〈1 1 1〉 chains of cation sites with alternating octahedral and prismatic coordination geometry. These sites are occupied by Li, Fe and M′ or In; Nd or La cations occupy sites between the chains. The cation distribution over the octahedral and prismatic sites within the chains is disordered in all three compounds.more » The Nd-containing compositions show spin-glass behaviour below ∼4.5 K whereas small, weakly-ferrimagnetic domains form in La{sub 18}Li{sub 8}Fe{sub 4.5}In{sub 0.5}O{sub 39} below 7.60 K. The dependence of the magnetic properties on the nature of the lanthanide cation is discussed. - Graphical abstract: At low temperatures Nd{sub 18}Li{sub 8}Fe{sub 4}M′O{sub 39} (M’=Al, Ga) behave as spin glasses whereas small ferrimagnetic domains form in La{sub 18}Li{sub 8}Fe{sub 4.5}In{sub 0.5}O{sub 39}. Display Omitted - Highlights: • p-Block cations can be accommodated in the La{sub 18}Li{sub 8}Rh{sub 5}O{sub 39} structure. • Small ferrimagnetic domains in La{sub 18}Li{sub 8}Fe{sub 4.5}In{sub 0.5}O{sub 39}. • Magnetic behaviour controlled by the lanthanide cation.« less

Sm-Nd Isotopic Systematics of Troctolite 76335

NASA Technical Reports Server (NTRS)

Edmunson, J.; Nyquist, L. E.; Borg, L. E.

2007-01-01

A study of the Sm-Nd isotopic systematics of lunar Mg-suite troctolite 76335 was undertaken to further establish the early chronology of lunar magmatism. Because the Rb-Sr isotopic systematics of similar sample 76535 yielded an age of 4570 +/- 70 Ma [2, lambda = 1.402 x 10(exp -11)], 76335 was expected to yield an old age. In contrast, the Sm-Nd and K-Ar ages of 76535 indicate that the sample is approximately 4260 Ma old, one of the youngest ages obtained for a Mg-suite rock. This study establishes the age of 76335 and discusses the constraints placed on its petrogenesis by its Sm-Nd isotope systematics. The Sm-Nd isotopic system of lunar Mg-suite troctolite 76335 indicates an age of 4278 +/- 60 Ma with an initial epsilon (sup 143)(sub Nd) value of 0.06 +/- 0.39. These values are consistent with the Sm-Nd isotopic systematics of similar sample 76535. Thus, it appears that a robust Sm-Nd age can be determined from a highly brecciated lunar sample. The Sm-Nd isotopic systematics of troctolites 76335 and 76535 appear to be different from those dominating the Mg-suite norites and KREEP basalts. Further analysis of the Mg-suite must be completed to reveal the isotopic relationships of these early lunar rocks.

Synergy of the Developed 6D BIM Framework and Conception of the nD BIM Framework and nD BIM Process Ontology

ERIC Educational Resources Information Center

O'Keeffe, Shawn Edward

2013-01-01

The author developed a unified nD framework and process ontology for Building Information Modeling (BIM). The research includes a framework developed for 6D BIM, nD BIM, and nD ontology that defines the domain and sub-domain constructs for future nD BIM dimensions. The nD ontology defines the relationships of kinds within any new proposed…

Blackbody absorption efficiencies for six lamp pumped Nd laser materials

NASA Technical Reports Server (NTRS)

Cross, Patricia L.; Barnes, Norman P.; Skolaut, Milton W., Jr.; Storm, Mark E.

1990-01-01

Utilizing high resolution spectra, the absorption efficiencies for six Nd laser materials were calculated as functions of the effective blackbody temperature of the lamp and laser crystal size. The six materials were Nd:YAG, Nd:YLF, Nd:Q-98 Glass, Nd:YVO4, Nd:BEL, and Nd:Cr:GSGG. Under the guidelines of this study, Nd:Cr:GSGG's absorption efficiency is twice the absorption efficiency of any of the other laser materials.

Nd-YAG Laser Treatment for Tracheobronchial Obstruction

PubMed Central

Lee, Yu-Chin; Chiang, Kuo-Hwa

1996-01-01

The Nd-YAG laser has good tissue penetration and coagulation effects thus has become an important weapon for photoresection of tracheobronchial obstructive lesions since 1980. Treatment of benign lesions including benign tumors and scar tissues using the Nd-YAG laser has good results. In the treatment of malignant tumors however, it has a lower effectivity rate when compared to benign lesions. From July 1984 to September 1995, a total of 65 patients were treated with Nd-YAG laser for tracheobronchial obstruction. There were 32 (49%) malignant tumors and 33 (51%) benign lesions. 116 resections were performed in 48 patients using the non-contact Nd-YAG laser (MBB, Medilas 2) before 1992. Thereafter, another 41 resections were performed in 17 cases using contact Nd-YAG laser (SLT, CL-X). The overall effectivity rate was 60%. The effectivity rate for benign lesions was 81.3% and 39.4% for malignant tumor. The effectivity rate between non-contact and contact Nd-YAG laser was not significantly different. PMID:18493424

Nd-YAG Laser Treatment for Tracheobronchial Obstruction.

PubMed

Perng, R P; Lee, Y C; Chiang, K H

1996-01-01

The Nd-YAG laser has good tissue penetration and coagulation effects thus has become an important weapon for photoresection of tracheobronchial obstructive lesions since 1980.Treatment of benign lesions including benign tumors and scar tissues using the Nd-YAG laser has good results. In the treatment of malignant tumors however, it has a lower effectivity rate when compared to benign lesions. From July 1984 to September 1995, a total of 65 patients were treated with Nd-YAG laser for tracheobronchial obstruction. There were 32 (49%) malignant tumors and 33 (51%) benign lesions. 116 resections were performed in 48 patients using the non-contact Nd-YAG laser (MBB, Medilas 2) before 1992. Thereafter, another 41 resections were performed in 17 cases using contact Nd-YAG laser (SLT, CL-X). The overall effectivity rate was 60%. The effectivity rate for benign lesions was 81.3% and 39.4% for malignant tumor. The effectivity rate between non-contact and contact Nd-YAG laser was not significantly different.

146Sm–142Nd systematics measured in enstatite chondrites reveals a heterogeneous distribution of 142Nd in the solar nebula

PubMed Central

Gannoun, Abdelmouhcine; Boyet, Maud; Rizo, Hanika; El Goresy, Ahmed

2011-01-01

The short-lived 146Sm–142Nd chronometer (T1/2 = 103 Ma) is used to constrain the early silicate evolution of planetary bodies. The composition of bulk terrestrial planets is then considered to be similar to that of primitive chondrites that represent the building blocks of rocky planets. However for many elements chondrites preserve small isotope differences. In this case it is not always clear to what extent these variations reflect the isotope heterogeneity of the protosolar nebula rather than being produced by the decay of parent isotopes. Here we present Sm–Nd isotopes data measured in a comprehensive suite of enstatite chondrites (EC). The EC preserve 142Nd/144Nd ratios that range from those of ordinary chondrites to values similar to terrestrial samples. The EC having terrestrial 142Nd/144Nd ratios are also characterized by small 144Sm excesses, which is a pure p-process nuclide. The correlation between 144Sm and 142Nd for chondrites may indicate a heterogeneous distribution in the solar nebula of p-process matter synthesized in supernovae. However to explain the difference in 142Nd/144Nd ratios, 20% of the p-process contribution to 142Nd is required, at odds with the value of 4% currently proposed in stellar models. This study highlights the necessity of obtaining high-precision 144Sm measurements to interpret properly measured 142Nd signatures. Another explanation could be that the chondrites sample material formed in different pulses of the lifetime of asymptotic giant branch stars. Then the isotope signature measured in SiC presolar would not represent the unique s-process signature of the material present in the solar nebula during accretion. PMID:21515828

Synthesis and characterization of iron based superconductor Nd-1111

NASA Astrophysics Data System (ADS)

Alborzi, Z.; Daadmehr, V.

2018-06-01

Polycrystalline sample of NdFeAsO0.8F0.2 was prepared by one-step solid-state reaction method. The structural and electrical properties of sample were characterized through XRD pattern and the 4-probe method. The critical temperature was obtained at 56 K. The crystal structure was tetragonal with P4/nmm:2 symmetry group.

Synthesis of Bi0.9Nd0.1FeO3 multiferroic nanoceramic by sol-gel method and its structural, surface morphology and dielectric analysis

NASA Astrophysics Data System (ADS)

Das, S.; Bera, K. P.; Nath, T. K.

2017-05-01

Synthesis of Nd-doped BFO multiferroic nanoceramic by the conventional sol-gel method has been carried out. HRXRD and FESEM have been used for the structural analysis to confirm the triclinic structure and to obtain the surface morphology showing agglomeration and to find out the size of the nanoparticles. A high precision LCR meter has been used to record the dielectric constants at various temperatures. Several anomalies are observed whose physical explanations have been given. Space charge polarization effect and magnetoelectric coupling have been confirmed in the synthesized Bi0.9Nd0.1FeO3 nanoceramic sample.

Low temperature magnetic properties of Nd2Ru2O7

NASA Astrophysics Data System (ADS)

Ku, S. T.; Kumar, D.; Lees, M. R.; Lee, W.-T.; Aldus, R.; Studer, A.; Imperia, P.; Asai, S.; Masuda, T.; Chen, S. W.; Chen, J. M.; Chang, L. J.

2018-04-01

We present magnetic susceptibility, heat capacity, and neutron diffraction measurements of polycrystalline Nd2Ru2O7 down to 0.4 K. Three anomalies in the magnetic susceptibility measurements at 146, 21 and 1.8 K are associated with an antiferromagnetic ordering of the Ru4+ moments, a weak ferromagnetic signal attributed to a canting of the Ru4+ and Nd3+ moments, and a long-range-ordering of the Nd3+ moments, respectively. The long-range order of the Nd3+ moments was observed in all the measurements, indicating that the ground state of the compound is not a spin glass. The magnetic entropy of Rln2 accumulated up to 5 K, suggests the Nd3+ has a doublet ground state. Lattice distortions accompany the transitions, as revealed by neutron diffraction measurements, and in agreement with earlier synchrotron x-ray studies. The magnetic moment of the Nd3+ ion at 0.4 K is estimated to be 1.54(2)µ B and the magnetic structure is all-in all-out as determined by our neutron diffraction measurements.

Magnetic structure of the ferromagnetic new ternary silicide Nd5CoSi2.

PubMed

Mayer, C; Gaudin, E; Gorsse, S; Porcher, F; André, G; Chevalier, B

2012-04-04

Nd(5)CoSi(2) was obtained from the elements by arc-melting followed by annealing at 883 K. Its investigation by single-crystal x-ray and neutron powder diffraction shows that this ternary silicide crystallizes as Nd(5)Si(3) in a tetragonal structure deriving from the Cr(5)B(3)-type (I4/mcm space group; a = 7.7472(2) and c = 13.5981(5) Å as unit cell parameters). The structural refinements confirm the mixed occupancy on the 8h site between Si and Co atoms, as already observed for Gd(5)CoSi(2). Magnetization and specific heat measurements reveal a ferromagnetic behavior below T(C) = 55 K for Nd(5)CoSi(2). This magnetic ordering is further evidenced by neutron powder diffraction investigation revealing between 1.8 K and T(C) a canted ferromagnetic structure in the direction of the c-axis described by a propagation vector k = (0 0 0). At 1.8 K, the two Nd(3+) ions carry ordered magnetic moments equal respectively to 1.67(7) and 2.37(7) μ(B) for Nd1 and Nd2; these two moments exhibit a canting angle of θ = 4.3(6)°. This magnetic structure presents some similarities with that reported for Nd(5)Si(3). © 2012 IOP Publishing Ltd

Crystal growth and scintillation properties of Nd-doped Lu 3Al 5O 12 single crystals with different Nd concentrations

NASA Astrophysics Data System (ADS)

Sugiyama, Makoto; Fujimoto, Yutaka; Yanagida, Takayuki; Yokota, Yuui; Pejchal, Jan; Furuya, Yuki; Tanaka, Hidehiko; Yoshikawa, Akira

2011-04-01

Nd 0.1%, 0.5%, 1% and 3% doped Lu 3Al 5O 12 (Nd:LuAG) single crystals were grown in the nitrogen atmosphere by the micro-pulling down (μ-PD) method. The grown crystals had a single-phase confirmed by powder XRD analysis. In absorption spectra, some weak absorption lines due to Nd 3+ 4f-4f transitions were observed and their intensity increased with the increase of Nd concentration. When excited by 241Am α-ray, a broad emission peak due to defects in the host lattice at 320 nm and some sharp lines due to Nd 3+ 4f-4f transitions at wavelength longer than 400 nm were observed. The decay time profiles of Nd:LuAG under γ-ray excitation were well approximated by two exponential function of 340-760 ns and 3-5 μs for each sample. By pulse height measurement using 137Cs, Nd 0.5%:LuAG showed the highest light yield of 7600 ± 760 photons/MeV.

Magnetic order of Nd 5 Pb 3 single crystals

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yan, Jiaqiang; Ochi, Masayuki; Cao, Huibo B.

We report millimeter-sized Nd 5Pb 3 single crystals grown out of a Nd–Co flux. We experimentally study the magnetic order of Nd 5Pb 3 single crystals by measuring the anisotropic magnetic properties, electrical resistivity under high pressure up to 8 GPa, specific heat, and neutron single crystal diffraction. Two successive magnetic orders are observed at T N1 = 44 K and T N2 = 8 K. The magnetic cells can be described with a propagation vector $k=(0.5, 0, 0)$ . Cooling below T N1, Nd1 and Nd3 order forming ferromagnetic stripes along the b-axis, and the ferromagnetic stripes are coupledmore » antiferromagnetically along the a-axis for the $k=(0.5, 0, 0)$ magnetic domain. Cooling below T N2, Nd2 orders antiferromagnetically to nearby Nd3 ions. All ordered moments align along the crystallographic c-axis. The magnetic order at T N1 is accompanied by a quick drop of electrical resistivity upon cooling and a lambda-type anomaly in the temperature dependence of specific heat. At T N2, no anomaly was observed in electrical resistivity but there is a weak feature in specific heat. The resistivity measurements under hydrostatic pressures up to 8 GPa suggest a possible phase transition around 6 GPa. Our first-principles band structure calculations show that Nd 5Pb 3 has the same electronic structure as does Y 5Si 3 which has been reported to be a one-dimensional electride with anionic electrons that do not belong to any atom. Our study suggests that R 5Pb 3 (R = rare earth) can be a materials playground for the study of magnetic electrides. To conclude, this deserves further study after experimental confirmation of the presence of anionic electrons.« less

Magnetic order of Nd 5 Pb 3 single crystals

DOE PAGES

Yan, Jiaqiang; Ochi, Masayuki; Cao, Huibo B.; ...

2018-03-02

We report millimeter-sized Nd 5Pb 3 single crystals grown out of a Nd–Co flux. We experimentally study the magnetic order of Nd 5Pb 3 single crystals by measuring the anisotropic magnetic properties, electrical resistivity under high pressure up to 8 GPa, specific heat, and neutron single crystal diffraction. Two successive magnetic orders are observed at T N1 = 44 K and T N2 = 8 K. The magnetic cells can be described with a propagation vector $k=(0.5, 0, 0)$ . Cooling below T N1, Nd1 and Nd3 order forming ferromagnetic stripes along the b-axis, and the ferromagnetic stripes are coupledmore » antiferromagnetically along the a-axis for the $k=(0.5, 0, 0)$ magnetic domain. Cooling below T N2, Nd2 orders antiferromagnetically to nearby Nd3 ions. All ordered moments align along the crystallographic c-axis. The magnetic order at T N1 is accompanied by a quick drop of electrical resistivity upon cooling and a lambda-type anomaly in the temperature dependence of specific heat. At T N2, no anomaly was observed in electrical resistivity but there is a weak feature in specific heat. The resistivity measurements under hydrostatic pressures up to 8 GPa suggest a possible phase transition around 6 GPa. Our first-principles band structure calculations show that Nd 5Pb 3 has the same electronic structure as does Y 5Si 3 which has been reported to be a one-dimensional electride with anionic electrons that do not belong to any atom. Our study suggests that R 5Pb 3 (R = rare earth) can be a materials playground for the study of magnetic electrides. To conclude, this deserves further study after experimental confirmation of the presence of anionic electrons.« less

Small polaronic hole hopping mechanism and Maxwell-Wagner relaxation in NdFeO3

NASA Astrophysics Data System (ADS)

Ahmad, I.; Akhtar, M. J.; Younas, M.; Siddique, M.; Hasan, M. M.

2012-10-01

In the modern micro-electronics, transition metal oxides due to their colossal values of dielectric permittivity possess huge potential for the development of capacitive energy storage devices. In the present work, the dielectric permittivity and the effects of temperature and frequency on the electrical transport properties of polycrystalline NdFeO3, prepared by solid state reaction method, are discussed. Room temperature Mossbauer spectrum confirms the phase purity, octahedral environment for Fe ion, and high spin state of Fe3+ ion. From the impedance spectroscopic measurements, three relaxation processes are observed, which are related to grains, grain boundaries (gbs), and electrode-semiconductor contact in the measured temperature and frequency ranges. Decrease in resistances and relaxation times of the grains and grain boundaries with temperature confirms the involvement of thermally activated conduction mechanisms. Same type of charge carriers (i.e., small polaron hole hopping) have been found responsible for conduction and relaxation processes through the grain and grain boundaries. The huge value of the dielectric constant (˜8 × 103) at high temperature and low frequency is correlated to the Maxwell-Wagner relaxation due to electrode-sample contact.

An efficient continuous-wave 591 nm light source based on sum-frequency mixing of a diode pumped Nd:GdVO4-Nd:CNGG laser

NASA Astrophysics Data System (ADS)

Zhao, Y. D.; Liu, J. H.

2013-08-01

We report a laser architecture to obtain continuous-wave (CW) yellow-orange light sources at the 591 nm wavelength. An 808 nm diode pumped a Nd:GdVO4 crystal emitting at 1063 nm. A part of the pump power was then absorbed by the Nd:CNGG crystal. The remaining pump power was used to pump a Nd:CNGG crystal emitting at 1329 nm. Intracavity sum-frequency mixing at 1063 and 1329 nm was then realized in a LiB3O5 (LBO) crystal to reach the yellow-orange radiation. We obtained a CW output power of 494 mW at 591 nm with a pump laser diode emitting 17.8 W at 808 nm.

Authigenic Nd isotope record of North Pacific Intermediate Water formation and boundary exchange on the Bering Slope

NASA Astrophysics Data System (ADS)

Jang, Kwangchul; Huh, Youngsook; Han, Yeongcheol

2017-01-01

The Bering Sea is a potential location for the formation of the North Pacific Intermediate Water (NPIW), which drives the global ocean circulation as a counterpart to the North Atlantic Deep Water (NADW). To evaluate the NPIW-NADW seesaw hypothesis, we reconstructed the long-term variation of the bottom water Nd isotopic composition at site U1345 on the Bering Slope by extracting authigenic Fe-Mn oxyhydroxide from bulk sediments. We examined six different extractions in order to ensure that authentic seawater composition is recovered. For Bering Slope sediments whose typical carbonate content is less than 5% (average 2%), the most reliable results are obtained if the decarbonation step is omitted and a low reagent-to-sediment ratio is adopted. The reconstructed authigenic εNd record for the last 520 kyr exhibits large temporal variations depending on whether the NPIW formation or the boundary exchange process is dominant. Periods of radiogenic εNd can be attributed to NPIW formation triggered by brine rejection, as evidenced by the difference in δ18O of benthic foraminifera between sites (Δδ18Obf), high % sea-ice related diatoms, and low abundance of Bulimina aff. Exilis (low-oxygen deep fauna). Diminished supply of unradiogenic Nd from boundary exchange seems to intensify these radiogenic peaks. On the other hand, the unradiogenic εNd intervals can be attributed to stagnant bottom water conditions, as can be deduced from the Δδ18Obf values, low % sea-ice related diatoms, abundant B. aff. Exilis, and laminations. When there is no NPIW formation, the continental margin sediments are exposed to boundary exchange for a longer period of time, leading to release of unradiogenic Nd. The mid-MIS 6 and mid-MIS 5 are exceptions in that NPIW formation occurred yet the εNd compositions are unradiogenic. NPIW formation and cold climate (closed Bering Strait) are not always correlated. Comparison against εNd records of the South Atlantic suggests only an ambiguous

Determination of Debye temperatures and Lamb-Mössbauer factors for LnFeO3 orthoferrite perovskites (Ln  =  La, Nd, Sm, Eu, Gd)

NASA Astrophysics Data System (ADS)

Scrimshire, A.; Lobera, A.; Bell, A. M. T.; Jones, A. H.; Sterianou, I.; Forder, S. D.; Bingham, P. A.

2018-03-01

Lanthanide orthoferrites have wide-ranging industrial uses including solar, catalytic and electronic applications. Here a series of lanthanide orthoferrite perovskites, LnFeO3 (Ln  =  La Nd; Sm; Eu; Gd), prepared through a standard stoichiometric wet ball milling route using oxide precursors, has been studied. Characterisation through x-ray diffraction and x-ray fluorescence confirmed the synthesis of phase-pure or near-pure LnFeO3 compounds. 57Fe Mössbauer spectroscopy was performed over a temperature range of 10 K-293 K to observe hyperfine structure and to enable calculation of the recoil-free fraction and Debye temperature (θ D) of each orthoferrite. Debye temperatures (Ln  =  La 474 K Nd 459 K Sm 457 K Eu 452 K Gd 473 K) and recoil-free fractions (Ln  =  La 0.827; Nd 0.817; Sm 0.816; Eu 0.812; Gd 0.826) were approximated through minimising the difference in the temperature dependent experimental centre shift and theoretical isomer shift, by allowing the Debye temperature and isomer shift values to vary. This method of minimising the difference between theoretical and actual values yields Debye temperatures consistent with results from other studies determined through thermal analysis methods. This displays the ability of variable-temperature Mössbauer spectroscopy to approximate Debye temperatures and recoil-free fractions, whilst observing temperature induced transitions over the temperature range observed. X-ray diffraction and Rietveld refinement show an inverse relationship between FeO6 octahedral volume and approximated Debye temperatures. Raman spectroscopy show an increase in the band positions attributed to soft modes of Ag symmetry, Ag(3) and Ag(5) from La to GdFeO3 corresponding to octahedral rotations and tilts in the [0 1 0] and [1 0 1] planes respectively.

Determining the Sensitivity of the Hf-Nd Proxy to Glacial Weathering

NASA Astrophysics Data System (ADS)

Namsinh, A.; Scher, H.; Piotrowski, A. M.

2017-12-01

The history of polar ice sheets through the Cenozoic is incompletely known. Estimates of the onset of northern hemisphere glaciation range from the Pliocene to mid-Eocene and precursor Antarctic glaciations are believed to have commenced in the middle Eocene. Uncertainty surrounding the history of ice sheets has resulted in debates about the sensitivity of ice sheets to changes in atmospheric CO2 through the Cenozoic. Geochemical proxies for continental weathering — particularly those that are sensitive to mechanical breakdown of the upper continental crust by ice sheets — could improve the fidelity of paleoclimate reconstructions of ice sheet history. Coupled hafnium (Hf) and neodymium (Nd) isotopes in seawater and authigenic sediment phases show a strong correlation with mechanical weathering rates, however the proxy has not been systematically tested on Pleistocene time scales. We measured the Hf and Nd isotope ratios of authigenic and detrital phases of sediment cores from 1150 m to 4045 m depth on the Rockall Plateau in the NE Atlantic Ocean. Our study is limited to the LGM, deglaciation and Holocene intervals. The authigenic fraction was extracted from bulk sediments by leaching with dilute hydroxylamine hydrochloride and EDTA to prevent readsorption of Hf. A stronger leach solution was then used to isolate the terrigenous detrital fraction. The fidelity of the seawater signal obtained by leaching is assessed by comparison of leachate eNd values to previously published eNd values from uncleaned forams from the same depth intervals. Initial tests with Holocene and deglacial samples verify that leachate eNd values are statistically indistinguishable from uncleaned forams. Shale-normalized REE patterns for leachates reveal negative Ce anomalies and a MREE enrichment typical of Fe-Mn oxydydroxide phases. Coupled Hf-Nd isotopes from authigenic leachates from our initial tests fall along the Seawater Array when plotted on a Hf-Nd isotope diagram, confirming

Determination of the optimum phase-matching directions for the self-frequency conversion of Nd:GdCOB and Nd:YCOB crystals

NASA Astrophysics Data System (ADS)

Chen, Xueyuan; Huang, Miaoliang; Luo, Zundu; Huang, Yidong

2001-09-01

We report on the nonlinear optical properties of Nd:Ca 4GdO(BO 3) 3 (Nd:GdCOB) and Nd:Ca 4YO(BO 3) 3 (Nd:YCOB) biaxial crystals by theoretical calculation. The phase-matching curves for the self-frequency conversion generation of both crystals are presented. The dependence of the effective nonlinear coefficients and walk-off angles on different phase-matching directions are discussed. The results show that the optimum type-I phase-matching directions for the self-frequency doubling and self-sum-frequency mixing lasers are not in the principal planes but are located respectively in the directions ( θ=67.1°, ϕ=132.35°) and ( θ=68.75°, ϕ=118.1°) for Nd:GdCOB, and ( θ=66.5°, ϕ=143.4°) and ( θ=65.9°, ϕ=134.1°) for Nd:YCOB.

Evidence from coupled (Sm-147)-(Nd-143) and (Sm-146)-(Nd-142) systematics for very early (4.5-Gyr) differentiation of the earth's mantle

NASA Technical Reports Server (NTRS)

Harper, Charles L., Jr.; Jacobsen, Stein B.

1992-01-01

Evidence for early differentiation of the earth's mantle is presented based on measurements of Nd-143/Nd-144 and Nd-142/Nd-144 ratios in an approximately 3.8 Gyr-old supracrustal rock from Isua, West Greenland. Coupled (Sm-146,147)-(Nd-142,143) systematics suggest that the fractionation of Sm/Nd took place 4.44-4.54 Gyr ago, due to extraction of a light rare earth element-enriched primordial crust.

Commercial-scale recycling of NdFeB-type magnets with grain boundary modification yields products with 'designer properties' that exceed those of starting materials.

PubMed

Zakotnik, M; Tudor, C O

2015-10-01

NdFeB-type magnets dominate the market for high performance magnetic materials, yet production of 'virgin' magnets via mining is environmentally, financially and energetically costly. Hence, interest is growing in 'magnet to magnet' recycling schemes that offer the potential for cheaper, more environmentally-friendly solutions to the world's growing appetite for rare-earth based magnetic materials. Unfortunately, previously described recycling processes only partially capitalise on this potential, because the methods described to date are limited to 'laboratory scale' or operate only under ideal conditions and result in products that fail to recapture the coercivity of the starting, scrap materials. Herein, we report a commercial scale process (120 kg batches) that completely recovers the properties of the starting scrap magnets. Indeed, 'grain boundary modification', via careful addition of a proprietary mix of blended elements, produces magnets with 'designer properties' that can exceed those of the starting materials and can be closely tailored to meet a wide variety of end-user applications, including high-coercivity (>2000 kA/m), sintered magnets suitable for motor applications. Copyright © 2015 Elsevier Ltd. All rights reserved.

Fluorescence properties of Nd3+-doped tellurite glasses.

PubMed

Kumar, K Upendra; Prathyusha, V A; Babu, P; Jayasankar, C K; Joshi, A S; Speghini, A; Bettinelli, M

2007-07-01

The compositional and concentration dependence of luminescence of the (4)F(3/2)-->(4)I(J) (J=13/2, 11/2 and 9/2) transitions in four Nd(3+)-doped tellurite based glasses has been studied. The free-ion energy levels obtained for 60TeO(2)+39ZnO(2)+1.0Nd(2)O(3) (TZN10) glass have been analysed using the free-ion Hamiltonian model and compared with similar results obtained for Nd(3+):glass systems. The absorption spectrum of TZN10 glass has been analysed using the Judd-Ofelt theory. Relatively longer decay rates have been obtained for Nd(3+)-doped phosphotellurite glasses. The emission characteristics of the (4)F(3/2)-->(4)I(11/2) transition, of the Nd(3+):TZN10 glass, are found to be comparable to those obtained for Nd(3+):phosphate laser glasses. The non-exponential shape of the emission decay curves for the (4)F(3/2)-->(4)I(11/2) transition is attributed to the presence of energy transfer processes between the Nd(3+) ions.

Cathodoluminescence response of natural and synthetic lanthanide-rich phosphates (Ln3+: Ce, Nd)

NASA Astrophysics Data System (ADS)

Barrera-Villatoro, A.; Boronat, C.; Rivera-Montalvo, T.; Correcher, V.; Garcia-Guinea, J.; Zarate-Medina, J.

2017-12-01

This paper reports on the cathodoluminescence (CL) emission of both natural and synthetic lanthanide-rich phosphates (Ln3+: Ce, Nd) previously characterized by X-ray Diffraction (XRD), Environmental Scanning Electronic Microscopy (ESEM) and Energy Dispersive Spectroscopy. The thermal treatment at 700 °C performed on the synthetic sample obtained by chemical precipitation, promotes increasing of the crystallinity degree giving rise to a phase transition from the hexagonal (comprising monazite and rabdophane) into the monoclinic (cerianite and monazite) structures detected by XRD. Despite the size and the morphology of the grains are similar under ESEM, it could be appreciated significant differences among CL signals attending to the shape (with well-defined peaks for the annealed sample) and intensity (with lower emission for the non-thermally pretreated synthetic phosphate). The main wavebands centered at (i) 360, 380 and 490 nm are associated respectively with 5D3/2 → 2F5/2 and 5D3/2 → 2F7/2 transitions as well as a redox reaction assigned to the presence of Ce3+, (ii) 276, 424, 516 and 531 nm are linked respectively to 2G9/2→4I9/2, 2P1/2→4I9/2, 4G9/2→4I9/2 and 4G7/2→4I9/2 Nd3+ transitions and (iii) 400-490 nm is due to non-bridging oxygen hole centers related to the tetrahedral PO43- groups or structural defects for the heated synthetic samples. The natural sample from Madagascar, with a very complex CL spectrum, displays a characteristic band emission in the green-yellow and red regions corresponding to [UO2]2+ groups and Sm3+ respectively.

Influence of the Amazon River on the Nd isotope composition of deep water in the western equatorial Atlantic during the Oligocene-Miocene transition

NASA Astrophysics Data System (ADS)

Stewart, Joseph A.; Gutjahr, Marcus; James, Rachael H.; Anand, Pallavi; Wilson, Paul A.

2016-11-01

Dissolved and particulate neodymium (Nd) are mainly supplied to the oceans via rivers, dust, and release from marine sediments along continental margins. This process, together with the short oceanic residence time of Nd, gives rise to pronounced spatial gradients in oceanic 143Nd/144Nd ratios (εNd). However, we do not yet have a good understanding of the extent to which the influence of riverine point-source Nd supply can be distinguished from changes in mixing between different water masses in the marine geological record. This gap in knowledge is important to fill because there is growing awareness that major global climate transitions may be associated not only with changes in large-scale ocean water mass mixing, but also with important changes in continental hydroclimate and weathering. Here we present εNd data for fossilised fish teeth, planktonic foraminifera, and the Fe-Mn oxyhydroxide and detrital fractions of sediments recovered from Ocean Drilling Project (ODP) Site 926 on Ceara Rise, situated approximately 800 km from the mouth of the River Amazon. Our records span the Mi-1 glaciation event during the Oligocene-Miocene transition (OMT; ∼23 Ma). We compare our εNd records with data for ambient deep Atlantic northern and southern component waters to assess the influence of particulate input from the Amazon River on Nd in ancient deep waters at this site. εNd values for all of our fish teeth, foraminifera, and Fe-Mn oxyhydroxide samples are extremely unradiogenic (εNd ≈ - 15); much lower than the εNd for deep waters of modern or Oligocene-Miocene age from the North Atlantic (εNd ≈ - 10) and South Atlantic (εNd ≈ - 8). This finding suggests that partial dissolution of detrital particulate material from the Amazon (εNd ≈ - 18) strongly influences the εNd values of deep waters at Ceara Rise across the OMT. We conclude that terrestrially derived inputs of Nd can affect εNd values of deep water many hundreds of kilometres from source. Our

Deep circulation changes in the South Atlantic since the Last Glacial Maximum from Nd isotope and multi-proxy records

NASA Astrophysics Data System (ADS)

Wei, R.; Abouchami, W.; Zahn, R.; Masque, P.

2016-01-01

We report down-core sedimentary Nd isotope (εNd) records from two South Atlantic sediment cores, MD02-2594 and GeoB3603-2, located on the western South African continental margin. The core sites are positioned downstream of the present-day flow path of North Atlantic Deep Water (NADW) and close to the Southern Ocean, which makes them suitable for reconstructing past variability in NADW circulation over the last glacial cycle. The Fe-Mn leachates εNd records show a coherent decreasing trend from glacial radiogenic values towards less radiogenic values during the Holocene. This trend is confirmed by εNd in fish debris and mixed planktonic foraminifera, albeit with an offset during the Holocene to lower values relative to the leachates, matching the present-day composition of NADW in the Cape Basin. We interpret the εNd changes as reflecting the glacial shoaling of Southern Ocean waters to shallower depths combined with the admixing of southward flowing Northern Component Water (NCW). A compilation of Atlantic εNd records reveals increasing radiogenic isotope signatures towards the south and with increasing depth. This signal is most prominent during the Last Glacial Maximum (LGM) and of similar amplitude across the Atlantic basin, suggesting continuous deep water production in the North Atlantic and export to the South Atlantic and the Southern Ocean. The amplitude of the εNd change from the LGM to Holocene is largest in the southernmost cores, implying a greater sensitivity to the deglacial strengthening of NADW at these sites. This signal impacted most prominently the South Atlantic deep and bottom water layers that were particularly deprived of NCW during the LGM. The εNd variations correlate with changes in 231Pa/230Th ratios and benthic δ13C across the deglacial transition. Together with the contrasting 231Pa/230Th: εNd pattern of the North and South Atlantic, this indicates a progressive reorganization of the AMOC to full strength during the Holocene.

Effect of α-particle irradiation on a NdFeAs(O,F) thin film

NASA Astrophysics Data System (ADS)

Tarantini, C.; Iida, K.; Sumiya, N.; Chihara, M.; Hatano, T.; Ikuta, H.; Singh, R. K.; Newman, N.; Larbalestier, D. C.

2018-07-01

The effect of α-particle irradiation on a NdFeAs(O,F) thin film has been investigated to determine how the introduction of defects affects basic superconducting properties, including the critical temperature T c and the upper critical field H c2, and properties more of interest for applications, like the critical current density J c and the related pinning landscape. The irradiation-induced suppression of the film T c is significantly smaller than on a similarly damaged single crystal. Moreover H c2 behaves differently, depending on the field orientation: for H//c the H c2 slope monotonically increases with increasing disorder, whereas for H//ab it remains constant at low dose and it increases only when the sample is highly disordered. This suggests that a much higher damage level is necessary to drive the NdFeAs(O,F) thin film into the dirty limit. Despite the increase in the low temperature H c2, the effects on the J c(H//c) performances are moderate in the measured temperature and field ranges, with a shifting of the pinning force maximum from 4.5 to 6 T after an irradiation of 2 × 1015 cm-2. On the contrary, J c(H//ab) is always suppressed. The analysis demonstrates that irradiation does introduce point defects (PD) acting as pinning centres proportionally to the irradiation fluence but also suppresses the effectiveness of c-axis correlated pinning present in the pristine sample. We estimate that significant performance improvements may be possible at high field or at temperatures below 10 K. The suppression of the J c(H//ab) performance is not related to a decrease of the J c anisotropy as found in other superconductors. Instead it is due to the presence of PD that decrease the efficiency of the ab-plane intrinsic pinning typical of materials with a layered structure.

Anomalous magnetoelastic behaviour near morphotropic phase boundary in ferromagnetic Tb{sub 1-x}Nd{sub x}Co{sub 2} system

DOE Office of Scientific and Technical Information (OSTI.GOV)

Murtaza, Adil; Yang, Sen, E-mail: yang.sen@mail.xjtu.edu.cn; Zhou, Chao

2016-08-01

In this work, we report a morphotropic phase boundary (MPB) involved ferromagnetic system Tb{sub 1-x}Nd{sub x}Co{sub 2} and reveal the corresponding structural and magnetoelastic properties of this system. With high resolution synchrotron X-ray diffractometry, the crystal structure of the TbCo{sub 2}-rich side is detected to be rhombohedral and that of NdCo{sub 2}-rich side is tetragonal below their respective Curie temperatures T{sub C}. The MPB composition Tb{sub 0.35}Nd{sub 0.65}Co{sub 2} corresponds to the coexistence of the rhombohedral phase (R-phase) and tetragonal phase (T-phase). Contrary to previously reported MPB involved ferromagnetic systems, the MPB composition of Tb{sub 0.35}Nd{sub 0.65}Co{sub 2} shows minimummore » magnetization which can be understood as compensation of sublattice moments between the R-phase and the T-phase. Furthermore, magnetostriction of Tb{sub 1-x}Nd{sub x}Co{sub 2} decreases with increasing Nd concentration until x = 0.8 and then increases in the negative direction with further increasing Nd concentration; the optimum point for magnetoelastic properties lies towards the rhombohedral phase. Our work not only shows an anomalous type of ferromagnetic MPB but also provides an effective way to design functional materials.« less

Healing of rat mouth mucosa after irradiation with CO2, Nd:YAG, and CO2-Nd:YAG combination lasers.

PubMed

Luomanen, M; Rauhamaa-Mäkinen, R; Meurman, J H; Kosloff, T; Tiitta, O

1994-08-01

The healing process of wounds made by a combination laser was studied in 90 rats. The laser system enabled both separate and combined use of CO2 and Nd:YAG laser irradiations. The laser wounds and the control excision wounds made by alligator forceps appeared on both sides of the tongue. Specimens from the wound sites were taken immediately, 6 h, and 1, 2, 4, 7, 11, 21, 28, and 42 days after surgery. The wound-healing process was studied by macroscopic evaluation before preparing the specimens for light microscopy. Some differences were noted in the wound-healing process among the three groups into which the experimental animals were divided. Tissue coagulation damage was most extensive in the Nd:YAG laser sites, where it was observed in its full extent 4 days after surgery. Epithelial cells were seen to begin to proliferate in all the wounds 6 h after surgery. Re-epithelialization was completed by between 7 (CO2) and 21 days (Nd:YAG) at all the wound sites. The inflammatory cell infiltration was more prominent in the Nd:YAG and the CO2-Nd:YAG combination laser wounds than in the CO2 and excision wounds during healing. Tissue regeneration occurred faster with less contraction in the combination CO2-Nd:YAG wounds than in Nd:YAG wounds. The best macroscopic healing result was seen in the CO2 wound sites. The combination laser was effective both at cutting and at coagulating tissue. Combining the CO2 and Nd:YAG laser irradiation into one beam resulted in a greater incision depth than what could have been expected from using the two lasers separately.

The Effect of High Concentration and Small Size of Nanodiamonds on the Strength of Interface and Fracture Properties in Epoxy Nanocomposite

PubMed Central

Haleem, Yasir A.; Song, Pin; Liu, Daobin; Wang, Changda; Gan, Wei; Saleem, Muhammad Farooq; Song, Li

2016-01-01

The concentration and small size of nanodiamonds (NDs) plays a crucial role in the mechanical performance of epoxy-based nanocomposites by modifying the interface strength. Herein, we systemically analyzed the relation between the high concentration and small size of ND and the fracture properties of its epoxy-based nanocomposites. It was observed that there is a two-fold increase in fracture toughness and a three-fold increase in fracture energy. Rationally, functionalized-NDs (F-NDs) showed a much better performance for the nanocomposite than pristine NDs (P-NDs) because of additional functional groups on its surface. The F-ND/epoxy nanocomposites exhibited rougher surface in contrast with the P-ND/epoxy, indicating the presence of a strong interface. We found that the interfaces in F-ND/epoxy nanocomposites at high concentrations of NDs overlap by making a web, which can efficiently hinder further crack propagation. In addition, the de-bonding in P-ND/epoxy nanocomposites occurred at the interface with the appearance of plastic voids or semi-naked particles, whereas the de-bonding for F-ND/epoxy nanocomposites happened within the epoxy molecular network instead of the interface. Because of the strong interface in F-ND/epoxy nanocomposites, at high concentrations the de-bonding within the epoxy molecular network may lead to subsequent cracks, parallel to the parent crack, via crack splitting which results in a fiber-like structure on the fracture surface. The plastic void growth, crack deflection and subsequent crack growth were correlated to higher values of fracture toughness and fracture energy in F-ND/epoxy nanocomposites. PMID:28773628

The Effect of High Concentration and Small Size of Nanodiamonds on the Strength of Interface and Fracture Properties in Epoxy Nanocomposite.

PubMed

Haleem, Yasir A; Song, Pin; Liu, Daobin; Wang, Changda; Gan, Wei; Saleem, Muhammad Farooq; Song, Li

2016-06-23

The concentration and small size of nanodiamonds (NDs) plays a crucial role in the mechanical performance of epoxy-based nanocomposites by modifying the interface strength. Herein, we systemically analyzed the relation between the high concentration and small size of ND and the fracture properties of its epoxy-based nanocomposites. It was observed that there is a two-fold increase in fracture toughness and a three-fold increase in fracture energy. Rationally, functionalized-NDs (F-NDs) showed a much better performance for the nanocomposite than pristine NDs (P-NDs) because of additional functional groups on its surface. The F-ND/epoxy nanocomposites exhibited rougher surface in contrast with the P-ND/epoxy, indicating the presence of a strong interface. We found that the interfaces in F-ND/epoxy nanocomposites at high concentrations of NDs overlap by making a web, which can efficiently hinder further crack propagation. In addition, the de-bonding in P-ND/epoxy nanocomposites occurred at the interface with the appearance of plastic voids or semi-naked particles, whereas the de-bonding for F-ND/epoxy nanocomposites happened within the epoxy molecular network instead of the interface. Because of the strong interface in F-ND/epoxy nanocomposites, at high concentrations the de-bonding within the epoxy molecular network may lead to subsequent cracks, parallel to the parent crack, via crack splitting which results in a fiber-like structure on the fracture surface. The plastic void growth, crack deflection and subsequent crack growth were correlated to higher values of fracture toughness and fracture energy in F-ND/epoxy nanocomposites.

Flame-ion chemistry of the lanthanide metals Ce, Pr and Nd

NASA Astrophysics Data System (ADS)

Patterson, Patricia M.; Goodings, John M.

1996-01-01

A pair of premixed, H2---O2---Ar flames of fuel-rich (FR) and fuel-lean (FL) composition, both at atmospheric pressure and 2425 K, were doped with about 10-6 mol fraction of the lanthanide metals La, Ce, Pr and Nd; from a previous study, La was used as a benchmark. The metals produce solid particles in the flames and gaseous metallic species. The latter include metallic atoms A near the flame reaction zone, but only the monoxide AO, the oxide hydroxide OAOH and, in some cases, the dioxide AO2 further downstream at equilibrium. Metallic ions (< 1% of the total metal) were observed by sampling the flames through a nozzle into a mass spectrometer. All of the observed ions can be represented by four hydrate series: (a) major signals of AO+·nH2O (n = 0-3) for La, Ce, Pr and Nd; (b) small signals of AO2H+·nH2O (n = 0-2) for Ce, Pr and Nd; (c) still smaller signals of AO2+·nH2O (n = 0, 1) for Ce, Pr and Nd in the FL flame only; and (d) tiny signals of AOH+·nH2O (n = 0, 1) for Pr and Nd in the FR flame only. The actual structures of some of these ions may not correspond to simple hydrates: e.g. AO+·H2O = A(OH)2+ = protonated OAOH; AO2H+·H2O = A(OH)3+, etc. Since hydrogen flames contain essentially no natural ionization, a major objective was to consider probable ionization mechanisms for the metals. The primary reactions include both chemi-ionization, and thermal (collisional) ionization of AO whose ionization energy is low (about 5 eV). Some of the ions are formed by secondary ion/molecule reactions including three-body hydration, proton transfer, electron (charge) transfer, H atom abstraction by radicals and oxidation. In addition, the chemical ionization of the metallic species by H3O+ was investigated. The flame-ion chemistry of these metals is discussed in detail.

Magnetic correlations in the intermetallic antiferromagnet Nd3Co4Sn13

NASA Astrophysics Data System (ADS)

Wang, C. W.; Lin, J. W.; Lue, C. S.; Liu, H. F.; Kuo, C. N.; Mole, R. A.; Gardner, J. S.

2017-11-01

Specific heat, magnetic susceptibility, and neutron scattering have been used to investigate the nature of the spin system in the antiferromagnet Nd3Co4Sn13. At room temperature Nd3Co4Sn13 has a cubic, Pm-3n structure similar to Yb3Rh4Sn13. Antiferromagnetic interactions between, Nd3+ ions dominate the magnetic character of this sample and at 2.4 K the Nd spins enter a long range order state with a magnetic propagation vector q  =  (0 0 0) with an ordered moment of 1.78(2) µ B at 1.5 K. The magnetic Bragg intensity grows very slowly below 1 K, reaching ~2.4 µ B at 350 mK. The average magnetic Nd3+ configuration corresponds to the 3D irreducible representation Γ7. This magnetic structure can be viewed as three sublattices of antiferromagnetic spin chains coupled with each other in the 120°-configuration. A well-defined magnetic excitation was measured around the 1 1 1 zone centre and the resulting dispersion curve is appropriate for an antiferromagnet with a gap of 0.20(1) meV.

Highly efficient solar-pumped Nd:YAG laser.

PubMed

Liang, Dawei; Almeida, Joana

2011-12-19

The recent progress in solar-pumped laser with Fresnel lens and Cr:Nd:YAG ceramic medium has revitalized solar laser researches, revealing a promising future for renewable reduction of magnesium from magnesium oxide. Here we show a big advance in solar laser collection efficiency by utilizing an economical Fresnel lens and a most widely used Nd:YAG single-crystal rod. The incoming solar radiation from the sun is focused by a 0.9 m diameter Fresnel lens. A dielectric totally internally reflecting secondary concentrator is employed to couple the concentrated solar radiation from the focal zone to a 4 mm diameter Nd:YAG rod within a conical pumping cavity. 12.3 W cw laser power is produced, corresponding to 19.3 W/m(2) collection efficiency, which is 2.9 times larger than the previous results with Nd:YAG single-crystal medium. Record-high slope efficiency of 3.9% is also registered. Laser beam quality is considerably improved by pumping a 3 mm diameter Nd:YAG rod.

Isotopic Equilibrium in Mature Oceanic Lithosphere: Insights From Sm-Nd Isotopes on the Corsica (France) Ophiolites

NASA Astrophysics Data System (ADS)

Rampone, E.; Hofmann, A. W.; Raczek, I.; Romairone, A.

2003-12-01

In mature oceanic lithosphere, formed at mid-ocean ridges, residual mantle peridotites and associated magmatic crust are, in principle, linked by a cogenetic relationship, because the times of asthenospheric mantle melting and magmatic crust production are assumed to be roughly coheval. This implies that oceanic peridotites and associated magmatic rocks should have similar isotopic compositions. Few isotope studies have been devoted to test this assumption. At mid-ocean ridges, similar Nd isotopic compositions in basalts and abyssal peridotites have been found by Snow et al. (1994), thus indicating that oceanic peridotites are indeed residues of MORB melting. By contrast, Salters and Dick (2002) have documented Nd isotope differences between abyssal peridotites and associated basalts, with peridotites showing higher 143Nd/144Nd values, and they concluded that an enriched pyroxenitic source component is required to explain the low end of the 143Nd/144Nd variation of the basalts. Here we present Sm/Nd isotope data on ophiolitic mantle peridotites and intruded gabbroic rocks from Mt.Maggiore (Corsica, France), interpreted as lithosphere remnants of the Jurassic Ligurian Tethys ocean. The peridotites are residual after low-degree (<10%) fractional melting. In places, spinel peridotites grade to plagioclase-rich impregnated peridotites. Clinopyroxene separates from both spinel- and plagioclase- peridotites display high 147Sm/144Nd (0.49-0.59) and 143Nd/144Nd (0.513367-0.513551) ratios, consistent with their depleted signature. The associated gabbros have Nd isotopic compositions typical of MORB (143Nd/144Nd = 0.51312-0.51314). Sm/Nd data on plag, whole rock and cpx from an olivine gabbro define an internal isochron with an age of 162 +/- 10 Ma, and an initial epsilon Nd value (9.0) indicating a MORB-type source. In the Sm-Nd isochron diagram, the peridotite data also conform to the above linear array, their initial (160 Ma) epsilon Nd values varying in the range 7

Magnetic field dependence of Sommerfeld coefficient and penetration depth in NdFeAsO1-XFX single crystal

NASA Astrophysics Data System (ADS)

Purohit, Geetanjali; Pattanaik, Anup; Nayak, Pratibindhya

2018-05-01

Anisotropic properties of Sommerfeld coefficient and penetration depth for single crystal NdFeAsO1-xFx has been studied by using modified phenomenological Ginzburg-Landau (GL) theory. In the above two-band superconducting system, the calculated value of Sommerfeld coefficient shows very close proximity with the experimental result as reported by Welp. Further, anisotropic ratio of penetration depth also calculated and reported for this system. The results of anisotropic properties of the above superconducting system implied that modified GL-theory in the form presented here can be applicable to the above superconducting system.

Tunable SERS signals of Rhodamine B molecules on Fe3O4@Au nanocomposite substrates controlled by magnetic field

NASA Astrophysics Data System (ADS)

Song, Hao; Fang, Rui Yang; Li, Ling

2018-02-01

In this work, we experimentally synthesized the Fe3O4@Au nanocomposites and used them as surface-enhanced Raman scattering (SERS) substrates. The Fe3O4@Au nanocomposites retained the metallic plasmon resonant effect and possessed the magnetic field controllable characteristics. The Raman spectra of Rhodamine B (RhB) probe molecules were studied under different external magnetic field. The magnitude of external magnetic field varied from 0 Gs to 700 Gs (1 Gs = 10-4 T) with intervals of 100 Gs. When the magnetic field magnitude increased, the Raman intensity of RhB probe molecules at 1356 cm-1 increased linearly. The slope of the linear fitting curves for the Raman intensity and area were 0.118/Gs and 3.700/Gs. The Raman enhancement could raise up to 7 times for RhB probe molecules when the magnetic field magnitude increased to 700 Gs. After removing the external magnetic field, the Raman peaks returned to its original intensity in several minutes. Under the external magnetic field, the Fe3O4@Au nanocomposites were concentrated, leading to the increase number of SERS "hot spots" and the surface Au density. The results show that the magnetic field controlled Fe3O4@Au nanocomposites can realize the enhanced and controllable SERS effect, which can be used in the reversible optical sensing and bio-medical applications.

Nd and Sr isotopic variations in acidic rocks from Japan: significance of upper-mantle heterogeneity

NASA Astrophysics Data System (ADS)

Terakado, Yasutaka; Nakamura, Noboru

1984-10-01

Initial Nd and Sr isotopic ratios have been measured for Cretaceous acidic and related intermediate rocks (24 volcanic and two plutonic rocks) from the Inner Zone of Southwest Japan (IZSWJ) to investigate the genesis of acidic magmas. The initial Nd and Sr isotopic ratios for these rocks show three interesting features: (1) ɛ Nd values for acidic rocks (+2 to -9) are negatively correlated with ɛ Sr values (+10 to +90) together with those for intermediate rocks ( ɛ Nd=+3 to -8; ɛ Sr=0 to +65). (2) The ɛ Nd values for silica rich rocks (>60% SiO2) correlate with the longitude of the sample locality, decreasing from west to east in a stepwise fashion: Four areas characterized by uniform ɛ Nd values are discriminated. (3) Low silica rocks (<60% SiO2) in a certain area have distinctly different ɛ Nd values from those of the high silica rocks in the same area. These results as well as those deduced from the additional samples collected, for comparison, from other provinces in Japan suggest that the acidic rocks can be formed neither by fractional crystallization processes from more basic magmas nor by crustal assimilation processes. The isotopic variations of the acidic rocks may reflect regional isotopic heterogeneity in the lower crust, and this heterogeneity may ultimately be attributed to the regional heterogeneity of the uppermost-mantle beneath the Japanese Islands.

Stabilization of Phase IV in CexLa1-xB6 (x=0.4, 0.5) by Pr and Nd Ion Dopings

NASA Astrophysics Data System (ADS)

Kondo, Akihiro; Taniguchi, Toshihiro; Tanida, Hiroshi; Matsumura, Takeshi; Sera, Masafumi; Iga, Fumitoshi; Tou, Hideki; Sakakibara, Toshiro; Kunii, Satoru

2009-09-01

We have studied the effect of magnetic rare-earth ion (Pr, Nd) doping on phase IV in CexLa1-xB6 (x=0.4, 0.5) systems. An unexpected large increase in the IV-I transition temperature TIV--I by Pr and Nd dopings was observed, while no such increase was observed for x≥ 0.6. Although we do not know the reason why the doping effect markedly differs between x≤ 0.5 and x≥ 0.6 at present, the order parameter in phase IV for x≤ 0.5 is coupled with the magnetic dipole moment of Pr and Nd ions and phase IV is stabilized.

75 FR 10462 - 92nd Meeting

Federal Register 2010, 2011, 2012, 2013, 2014

2010-03-08

... ARCTIC RESEARCH COMMISSION [USARC 10-018] 92nd Meeting February 16, 2010. Notice is hereby given that the U.S. Arctic Research Commission will hold its 92nd meeting in Miami, FL, on March 15, 2010...) Commissioners and staff reports. (4) Discussion and presentations concerning Arctic research activities. The...

X-ray absorption studies of gamma irradiated Nd doped phosphate glass

NASA Astrophysics Data System (ADS)

Rai, V. N.; Rajput, Parasmani; Jha, S. N.; Bhattacharyya, D.

2015-06-01

This paper presents the X-ray absorption near edge structure (XANES) studies of Nd doped phosphate glasses before and after gamma irradiation. The intensity and location of LIII edge white line peak of Nd changes depending on its concentration as well as on the ratio of O/Nd in the glass matrix. The decrease in the peak intensity of white line after gamma irradiation indicates towards reduction of Nd3+ to Nd2+ in the glass matrix, which increases with an increase in the doses of gamma irradiation. Similarity in the XANES spectra of Nd doped phosphate glasses and Nd2O3 suggests that coordination geometry around Nd3+ in glass samples may be identical to that of Nd2O3.

Highly efficient continuous-wave laser operation of LD-pumped Nd,Gd:CaF2 and Nd,Y:CaF2 crystals

NASA Astrophysics Data System (ADS)

Pang, Siyuan; Ma, Fengkai; Yu, Hao; Qian, Xiaobo; Jiang, Dapeng; Wu, Yongjing; Zhang, Feng; Liu, Jie; Xu, Jiayue; Su, Liangbi

2018-05-01

Spectroscopic properties of Nd:CaF2 crystals are investigated. The photoluminescence intensity in the near infrared region is drastically enhanced by co-doping Gd3+ ions and Y3+ in Nd:CaF2 crystals. Preliminary laser experiments are carried out with 0.3%Nd,5%Gd:CaF2 and 0.3%Nd,5%Y:CaF2 crystals under laser diode pumping; true continuous wave laser operation is achieved with slope efficiencies of 42% and 39%, respectively, and the maximum output power reaches 1.188 W.

Effect of TiC addition on microstructure and magnetic properties for MRE{sub 2}(Fe,Co){sub 14}B melt-spun ribbons (MRE=Nd+Y+Dy)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tang, W.; Wu, Y. Q.; Dennis, K. W.

2006-04-15

Effects of a TiC addition on microstructure and magnetic properties in [MRE{sub 2.2}Fe{sub 14}B]{sub (100-2x)/17.2}+Ti{sub x}C{sub x}(MRE=Nd+Y+Dy,x=1-5) ribbons, melt spun at a wheel speed of 16 m/s, were systematically studied. X-ray diffraction and differential thermal analysis data revealed that the addition of TiC improves the glass formability in the mixed rare earth alloys without Co, resulting in partially amorphous alloys. TEM observations showed that the average grain size in the as spun samples decreases from 200 to 20 nm with increasing x from 1 to 5, confirming that the addition of TiC can significantly improve microstructure. For an optimized [MRE{submore » 2}(Fe,Co){sub 14}B]{sub (100-2x)/17.2}+Ti{sub x}C{sub x} sample with x=2, spun at 25 m/s and annealed at 750 deg. C for 15 min, the room-temperature magnetic properties of H{sub cj}=11.8 kOe, M{sub r}=7.2 kGs, and (BH){sub max}=11.3 MGOe were obtained. Temperature coefficients for M{sub r} and H{sub cj} of -0.06 and -0.37%/ deg. C, respectively, also were measured in the temperature range of 27-100 deg. C. The new magnet alloy exhibits more uniform magnetic properties and a usable energy product to nearly 300 deg. C.« less

Lu-Hf and Sm-Nd evolution in lunar mare basalts

DOE Office of Scientific and Technical Information (OSTI.GOV)

Unruh, D.M.; Stille, P.; Patchett, P.J.

1984-02-15

Lu-Hf and Sm-Nd data for mare basalts combined with Rb-Sr and total REE data taken from the literature suggest that the mare basalts were derived by small (< or =10%) degrees of partial melting of cumulate sources, but that the magma ocean from which these sources formed was light REE and Hf-enriched. Calculated source compositions range fromm lherzolite to olivine websterite. Nonmodal melting of small amounts of ilmenite (< or =3%) in the sources seems to be required by the Lu/Hf data. A comparison of the Hf and Nd isotopic characteristics between the mare basalts and terrestrial oceanic basalts revealsmore » that the epsilonHf/epsilonNd ratios of low-Ti mare basalts are much higher than in terrestrial oceanic basalts. The results are qualitatively consistent with the hypothesis that terrestrial basalt sources are partial melt residues whereas mare basalt sources are cumulates. Alternatively, the results may imply that the terrestrial mantle has evolved in two (or more) stages of evolution, and that the net effect was depletion of the mantle during the first approx.1-3 b.y. followed by enrichment during the last 1-2 b.y.; or simply that there is a difference in Lu-Hf crystal-liquid partitioning (relative to Sm-Nd) between the lunar and terrestrial mantles.« less

Efficient dual-wavelength laser at 946 and 1064 nm with compactly combined Nd:YAG and Nd:YVO4 crystals

NASA Astrophysics Data System (ADS)

Cho, C. Y.; Chang, C. C.; Chen, Y. F.

2013-04-01

We originally employ a compact combination of a Nd:YAG crystal and a Nd:YVO4 crystal to develop an efficient dual-wavelength laser operating at 946 and 1064 nm. We exploit a short Nd:YAG crystal to generate 946 nm laser by reducing the reabsorption loss and a follow-up Nd:YVO4 crystal to generate a 1064 nm laser by absorbing the residual pump light. The output power ratio between the 946 and 1064 nm emissions can be flexibly adjusted from 0.3 to 0.9 by varying the separation between the two output couplers. At an incident pump power of 17 W, the total output power is generally higher than 5.2 W, with an overall optical-to-optical efficiency greater than 30%.

Optical properties of Nd3+ doped bismuth zinc borate glasses.

PubMed

Shanmugavelu, B; Venkatramu, V; Ravi Kanth Kumar, V V

2014-03-25

Glasses with compositions of (100-x) (Bi2ZnOB2O6) -x Nd2O3 (where x=0.1, 0.3, 0.5, 1 and 2 mol%) were prepared by melt quenching method and characterized through optical absorption, emission and decay curve measurements. Optical absorption spectra have been analyzed using Judd-Ofelt theory. The emission spectra exhibit three peaks at 919, 1063 and 1337 nm corresponding to (4)F3/2 to (4)I9/2, (4)I11/2 and (4)I13/2 transitions in the near infrared region. The emission intensity of the (4)F3/2 to (4)I11/2 transition increases with increase of Nd(3+) concentration up to 1 mol% and then concentration quenching is observed for 2 mol% of Nd(3+) concentration. The lifetimes for the (4)F3/2 level are found to decrease with increase in Nd2O3 concentration in the glasses. The decay curves of the glass up to 0.3 mol% of Nd(3+) exhibit single exponential nature and thereafter the curves become nonexponential nature (0.5, 1 and 2 mol%). The nonexponential curve has been fitted to the Inokuti-Hirayama model to understand the nature of energy transfer process. Copyright © 2013 Elsevier B.V. All rights reserved.

Crystal Structure and Magnetic Properties of New Cubic Quaternary Compounds RT2Sn2Zn18 (R = La, Ce, Pr, and Nd, and T = Co and Fe)

NASA Astrophysics Data System (ADS)

Isikawa, Yosikazu; Mizushima, Toshio; Ejiri, Jun-ichi; Kitayama, Shiori; Kumagai, Keigou; Kuwai, Tomohiko; Bordet, Pierre; Lejay, Pascal

2015-07-01

The new cubic quaternary intermetallic compounds RT2Sn2Zn18 (R = La, Ce, Pr, and Nd, and T = Co and Fe) were synthesized by the mixture-metal flux method using Zn and Sn. The crystal structure was investigated by powder X-ray diffraction and with a four-circle X-ray diffractometer using single crystals. The space group of the compounds is Fdbar{3}m (No. 227). The rare-earth atom is at the cubic site which is the center of a cage composed of Zn and Sn atoms. The crystal structure is the same as the CeCr2Al20-type crystal structure except the atoms at the 16c site, i.e., the Zn atoms at the 16c site are completely replaced by Sn atoms, indicating that the compounds are crystallographically new ordered quaternary compounds. The lattice parameter a and the physical properties of the magnetic susceptibility χ, the magnetization M, and the specific heat C of these cubic caged compounds were investigated. LaCo2Sn2Zn18 and LaFe2Sn2Zn18 are enhanced Pauli paramagnets that originate from the Co and Fe itinerant 3d electrons. CeCo2Sn2Zn18 and CeFe2Sn2Zn18 are also enhanced Pauli paramagnets that originate from both the 3d electrons and Ce 4f electrons. PrCo2Sn2Zn18 and PrFe2Sn2Zn18 are nonmagnetic materials with huge values of C divided by temperature, which indicates that the ground state of Pr ions is a non-Kramers' doublet. NdCo2Sn2Zn18 and NdFe2Sn2Zn18 are magnetic materials with the Néel temperatures of 1.0 and 3.8 K, respectively. All eight compounds have large magnetic moments of Co/Fe in the paramagnetic temperature region, and thus their magnetic moments are inferred to be magnetically frustrating owing to the pyrochlore lattice in the low-temperature region.

Sr, Nd, and Pb isotopes of ultramafic xenoliths in volcanic rocks of Eastern China: enriched components EMI and EMII in subcontinental lithosphere

USGS Publications Warehouse

Tatsumoto, M.; Basu, A.R.; Wankang, H.; Junwen, W.; Guanghong, X.

1992-01-01

The UThPb, SmNd, and RbSr isotopic systematics of mafic and ultramafic xenolithic rocks and associated megacrystic inclusions of aluminous augite and garnet, that occur in three alkalic volcanic suites: Kuandian in eastern Liaoning Province, Hanluoba in Hebei Province, and Minxi in western Fujian Province, China are described. In various isotopic data plots, the inclusion data invariably fall outside the isotopic ranges displayed by the host volcanic rocks, testifying to the true xenolithic nature of the inclusions. The major element partitioning data on Ca, Mg, Fe, and Al among the coexisting silicate minerals of the xenoliths establish their growth at ambient mantle temperatures of 1000-1100??C and possible depths of 70-80 km in the subcontinental lithosphere. Although the partitioning of these elements reflects equilibrium between coexisting minerals, equilibria of the Pb, Nd, and Sr isotopic systems among the minerals were not preserved. The disequilibria are most notable with respect to the 206Pb 204Pb ratios of the minerals. On a NdSr isotopic diagram, the inclusion data plot in a wider area than that for oceanic basalts from a distinctly more depleted component than MORB with higher 143Nd 144Nd and a much broader range of 87Sr 86Sr values, paralleling the theoretical trajectory of a sea-water altered lithosphere in NdSr space. The garnets consistently show lower ?? and ?? values than the pyroxenes and pyroxenites, whereas a phlogopite shows the highest ?? and ?? values among all the minerals and rocks studied. In a plot of ??207 and ??208, the host basalts for all three areas show lower ??207 and higher ??208 values than do the xenoliths, indicating derivation of basalts from Th-rich (relative to U) sources and xenoliths from U-rich sources. The xenolith data trends toward the enriched mantle components, EMI and EMII-like, characterized by high 87Sr 86Sr and ??207 values but with slightly higher 143Nd 144Nd. The EMI trend is shown more distinctly by the host

Synthesis of magnetic CoFe2O4/ordered mesoporous carbon nanocomposites and application in Fenton-like oxidation of rhodamine B.

PubMed

Deng, Jing; Chen, Yi-Jing; Lu, Yu-An; Ma, Xiao-Yan; Feng, Shan-Fang; Gao, Naiyun; Li, Jun

2017-06-01

CoFe 2 O 4 /ordered mesoporous carbon (OMC) nanocomposites were synthesized and tested as heterogeneous peroxymonosulfate (PMS) activator for the removal of rhodamine B. Characterization confirmed that CoFe 2 O 4 nanoparticles were tightly bonded to OMC, and the hybrid catalyst possessed high surface area, pore volume, and superparamagnetism. Oxidation experiments demonstrated that CoFe 2 O 4 /OMC nanocomposites displayed favorable catalytic activity in PMS solution and rhodamine B degradation could be well described by pseudo-first-order kinetic model. Sulfate radicals (SO 4 - ·) were verified as the primary reactive species which was responsible for the decomposition of rhodamine B. The optimum loading ratio of CoFe 2 O 4 and OMC was determined to be 5:1. Under optimum operational condition (catalyst dosage 0.05 g/L, PMS concentration 1.5 mM, pH 7.0, and 25 °C), CoFe 2 O 4 /OMC-activated peroxymonosulfate system could achieve almost complete decolorization of 100 mg/L rhodamine B within 60 min. The enhanced catalytic activity of CoFe 2 O 4 /OMC nanocomposites compared to that of CoFe 2 O 4 nanoparticles could be attributable to the increased adsorption capacity and accelerated redox cycles between Co(III)/Co(II) and Fe(III)/Fe(II).

Neodymium isotope heterogeneity of ordinary and carbonaceous chondrites and the origin of non-chondritic 142Nd compositions in the Earth

NASA Astrophysics Data System (ADS)

Fukai, Ryota; Yokoyama, Tetsuya

2017-09-01

We present high-precision Nd isotope compositions for ordinary and carbonaceous chondrites determined using thermal ionization mass spectrometry with dynamic and multistatic methods. The ordinary chondrites had uniform and non-terrestrial μ142 Nd , μ148 Nd , and μ150 Nd values, with data that plot along the mixing line between s-process and terrestrial components in μ150 Nd versus μ148 Nd and μ142 Nd versus μ148,150Nd diagrams. In contrast, the carbonaceous chondrites were characterized by larger anomalies in their μ142 Nd , μ148 Nd , and μ150 Nd values compared to ordinary chondrites. Importantly, the data for carbonaceous chondrites plot along the s-process and terrestrial mixing line in a μ150 Nd versus μ148 Nd diagram, whereas they have systematically lower μ142 Nd values than the s-process and terrestrial mixing line in μ142 Nd versus μ148,150Nd diagrams. This shift likely results from the incorporation of calcium- and aluminum-rich inclusions (CAIs), indicating that the Nd isotopic variability in the ordinary chondrites and CAI-free carbonaceous chondrites was caused solely by the heterogeneous distribution of s-process nuclides. The isotopic variation most likely results from nebular thermal processing that caused selective destruction of s-process-depleted (or r-process-enriched) dust grains in the inner Solar System where the parent bodies of ordinary chondrites formed, whereas such grains were preserved in the region of carbonaceous chondrite parent body formation. The Nd isotope dichotomy between ordinary and bulk aliquots of carbonaceous chondrites can be related to the presence of Jupiter, which may have separated two isotopically distinct reservoirs that were present in the solar nebula. After correcting for s-process anomalies and CAI contributions to the Nd isotopes observed in the chondrites, we obtained a μ142 Nd value (- 2.4 ± 4.8 ppm) that was indistinguishable from the terrestrial value. Our results corroborate the

Analysis of the strong coupling form factors of ΣbNB and ΣcND in QCD sum rules

NASA Astrophysics Data System (ADS)

Yu, Guo-Liang; Wang, Zhi-Gang; Li, Zhen-Yu

2017-08-01

In this article, we study the strong interaction of the vertices Σ b NB and Σ c ND using the three-point QCD sum rules under two different Dirac structures. Considering the contributions of the vacuum condensates up to dimension 5 in the operation product expansion, the form factors of these vertices are calculated. Then, we fit the form factors into analytical functions and extrapolate them into time-like regions, which gives the coupling constants. Our analysis indicates that the coupling constants for these two vertices are G ΣbNB = 0.43±0.01 GeV-1 and G ΣcND = 3.76±0.05 GeV-1. Supported by Fundamental Research Funds for the Central Universities (2016MS133)

A New ɛNd Record Covering Termination II

NASA Astrophysics Data System (ADS)

Deaney, E. L.; Thornalley, D. J.; van de Flierdt, T.; Kreissig, K.; Barker, S.

2014-12-01

The 143Nd/144Nd ratio (ɛNd) of seawater is used as a quasi-conservative tracer to examine past changes in water mass composition of the deep ocean. Records of ɛNd across the last deglaciation (Termination 1, T1) provide valuable information about water mass mixing that has improved our understanding of the ocean dynamics relevant to the process of deglaciation. However, questions remain concerning end-member source characteristics and regional hydrographic processes. Here we present a high resolution record of ɛNd derived from fish debris from ODP site 1063 across Termination 2. The different external and internal forcing (e.g. insolation versus freshwater) applicable to T2 make this a useful comparator for studies focused on T1. Accordingly we find large (up to 4 ɛNd units) fluctuations across T2 that can be related to high latitude climate changes as recorded by ice cores and other high resolution climate archives. We also identify periods of extremely negative values that require new explanations for changing end-member compositions. Our results have important implications for understanding North Atlantic deep water formation processes during critical climate transitions.

Ultra-high-precision Nd-isotope measurements of geological materials by MC-ICPMS

PubMed Central

Saji, Nikitha Susan; Wielandt, Daniel; Paton, Chad; Bizzarro, Martin

2016-01-01

We report novel techniques allowing the measurement of Nd-isotope ratios with unprecedented accuracy and precision by multi-collector inductively coupled plasma mass spectrometry. Using the new protocol, we have measured the Nd-isotopic composition of rock and synthetic Nd standards as well as that of the Allende carbonaceous chondrite. Analyses of BCR-2, BHVO-2 and GSP-2 rock standards yield mass-independent compositions identical to the JNdi-1 Nd-reference standard, with an external reproducibility of 2.4, 1.6, 1.6 and 3.5 ppm respectively, on μ142Nd, μ145Nd, μ146Nd and μ150Nd (μ representing the ppm-deviation of the ratios from JNdi-1) using 148Nd/144Nd for internal normalization. This represents an improvement in precision by a factor of 2, 7 and 9 respectively for μ142Nd, μ145Nd and μ150Nd. Near-quantitative recovery from purification chemistry and sample-standard bracketing allow for the determination of mass-dependent Nd-isotopic composition of samples. Synthetic standards, namely La Jolla and AMES, record mass-dependent variability of up to 1.2 ε per atomic mass unit and mass-independent compositions resolvable by up to 3 ppm for μ142Nd and 8 ppm for μ150Nd, relative to JNdi-1. The mass-independent compositions are consistent with equilibrium mass fractionation during purification. The terrestrial rock standards define a uniform stable ε145Nd of −0.24 ± 0.19 (2SD) relative to JNdi-1, indistinguishable from the mean Allende ε145Nd of −0.19 ± 0.09. We consider this value to represent the mass-dependent Nd-isotope composition of Bulk Silicate Earth (BSE). The modest mass-dependent fractionation of JNdi-1 relative to BSE results in potential effects on mass-independent composition that cannot be resolved within the reproducibility of our analyses when correcting for natural and instrumental mass fractionation by kinetic law, making it a suitable reference standard for analysis of unknowns. Analysis of Allende (CV3) carbonaceous chondrite

Nd:YAG development for spaceborne laser ranging system

NASA Technical Reports Server (NTRS)

Harper, L. L.; Logan, K. E.; Williams, R. H.; Stevens, D. A.

1979-01-01

The results of the development of a unique modelocked laser device to be utilized in future NASA space-based, ultraprecision laser ranger systems are summarized. The engineering breadboard constructed proved the feasibility of the pump-pulsed, actively modelocked, PTM Q-switched Nd:YAG laser concept for the generation of subnanosecond pulses suitable for ultra-precision ranging. The laser breadboard also included a double-pass Nd:YAG amplifier and provision for a Type II KD*P frequency doubler. The specific technical accomplishment was the generation of single 150 psec, 20-mJ pulses at 10 pps at a wavelength of 1.064 micrometers with 25 dB suppression of pre-and post-pulses.

VizieR Online Data Catalog: ND2 rotational spectrum (Melosso+,

NASA Astrophysics Data System (ADS)

Melosso, M.; Degli Esposti, C.; Dore, L.

2018-01-01

files used with the SPFIT/SPCAT program suite. There are 8 files of supplementary material, including a ReadMe, which was created by the AAS data editors. The text files are as follows: 1_Explan.txt = information on the content of the other files. 2ND2.fit = the output file of the fit of spectroscopic data used in the present study. 3ND2.lin = the corresponding line file. 4ND2.par = the corresponding parameter file. 5ND2.cat = the output file of the prediction made with the parameters determined in this study. 6ND2.var = the corresponding parameter file 7ND2.int = the corresponding intensity file (1 data file).

Variation in 142Nd/144Nd of Archean rocks from southwest Greenland : Implications for early Earth mantle dynamics

NASA Astrophysics Data System (ADS)

Rizo, H.; Boyet, M.; Blichert-Toft, J.; Rosing, M.; Paquette, J. L.

2012-04-01

The short-lived 146Sm-142Nd chronometer (half-life = 103 Ma) has proven successful in bringing constraints on the dynamics of the early Earth mantle. Since the parent isotope, 146Sm, was extant only during the first 300 Ma of the history of the Solar System, the positive 142Nd anomalies measured in southwest Greenland Archean rocks imply that their incompatible element-depleted mantle source formed during the Hadean. Interestingly, the magnitude of these anomalies seems to decrease over time. 3.7-3.8 Ga old rocks from the Amitsoq Complex have revealed +10 to +20 ppm 142Nd anomalies [1, 2, 3, 4, 5, 6, 7], whereas younger 3.0 Ga old samples from the Ivisaartoq greenstone belt yield smaller positive anomalies, ranging from +5.5 to +8.5 ppm [8]. Thus, the chemical heterogeneities detected in the southwest Greenland mantle were formed during the first 150 Ma of Earth's history, and seem to have resisted re-mixing by mantle convection until 3.0 Ga. In this study, we investigate the evolution of the southwest Greenland mantle during the time period of 3.3-3.4 Ga. The samples analyzed come from both the ~3.3 Ga amphibolite unit and the ~3.4 Ga Ameralik basic dyke swarm from the Amitsoq Complex. Coupled Sm-Nd and Lu-Hf bulk-rock ages obtained for seven amphibolites are in good agreement (3351 ± 210 Ma and 3302 ± 260 Ma, respectively) and consistent with the minimum age found by Nutman and Friend (2009) [9] for this formation. We further obtained coherent bulk-rock 147Sm-143Nd and zircon+baddeleyite 207Pb/206Pb ages for the Ameralik dykes (3428 ± 250 Ma and 3421 ± 34 Ma, respectively), in line with ages suggested by Nielsen at al., (2002) [10] and Nutman et al., (2004) [11]. We are currently in the process of analyzing these samples for 142Nd isotopic compositions and the results will be compared with the existing southwest Greenland data in order to shed new light on the evolution and destruction of heterogeneities in the early Earth mantle. [1] Rizo et al., (2011

Filled Nd(sub z) Fe(sub x) Co(sub 4-x) Sb(sub 12-y) Ge(sub y) Skutterudites: Processing and Thermoelectric Properties

NASA Technical Reports Server (NTRS)

Mackey, Jon; Sehirlioglu, Alp; Dynys, Fred

2016-01-01

Skutterudites have proven to be a useful thermoelectric system as a result of their enhanced figure of merit (ZT1), cheap material cost, favorable mechanical properties, and good thermal stability. The majority of skutterudite interest in recent years has been focused on binary skutterudites like CoSb3. Binary skutterudites are often double and triple filled, with a range of elements from the lanthanide series, in order to reduce the lattice component of thermal conductivity. Ternary and quaternary skutterudites, such as Co4Ge6Se6 or Ni4Sb8Sn4, provide additional paths to tune the electronic structure. The thermal conductivity can further be improved in these complex skutterudites by the introduction of fillers. The Nd (sub z) Fe (sub x) Co (sub 4-x) Sb (sub 12-y)Ge (sub y) system has been investigated as a p-type thermoelectric material, and is stable up to 600 degrees Centigrade. The influence of Fe and Ge content, along with filler Nd, was investigated on thermoelectric transport properties. In addition to the chemical influence on properties, some processing details of the system will also be addressed.

The Effects of Strain-Annealing on Tuning Permeability and Lowering Losses in Fe-Ni-Based Metal Amorphous Nanocomposites

DOE PAGES

Aronhime, Natan; DeGeorge, Vincent; Keylin, Vladimir; ...

2017-07-25

Here, Fe-Ni-based metal amorphous nanocomposites with a range of compositions (Fe 100–xNi x) 80Nb 4Si 2B 14 (30 ≤ x ≤ 70) are investigated for motor and transformer applications, where it is beneficial to have tunable permeability. It is shown that strain annealing offers an effective method for tuning permeability in these alloys. For an Fe-rich alloy, permeability increased from 4000 to 16,000 with a positive magnetostriction. In a Ni-rich alloy, permeability decreased from 290 to 40 with a negative magnetostriction. Significant elongations (above 60%) are observed during strain annealing at high stress. Crystallization products have been determined in allmore » alloys heated to 480°C. γ-FeNi is formed in all alloys, while (Fe 30Ni 70) 80Nb 4Si 2B 14 also undergoes secondary crystallization at temperatures of approximately 480°C to form a phase with the Cr 23C 6-type structure and a likely composition of Fe 21Nb 2B 6. Toroidal losses have been measured for (Fe 70Ni 30) 80Nb 4Si y B 16–y (0 ≤ y ≤ 3) at various annealing temperatures. At an induction of 1 T and frequency of 400 Hz and 1 kHz, the toroidal losses obtained are W 1.0T, 400 Hz = 0.9 W/kg and W 1.0T, 1 kHz = 2.3 W/kg, respectively. These losses are lower than losses recently reported for state of the art 3.0% and 6.5% silicon steels, a Metglas Fe-based amorphous alloy, and some Fe-based nanocomposites.« less

The Effects of Strain-Annealing on Tuning Permeability and Lowering Losses in Fe-Ni-Based Metal Amorphous Nanocomposites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aronhime, Natan; DeGeorge, Vincent; Keylin, Vladimir

Here, Fe-Ni-based metal amorphous nanocomposites with a range of compositions (Fe 100–xNi x) 80Nb 4Si 2B 14 (30 ≤ x ≤ 70) are investigated for motor and transformer applications, where it is beneficial to have tunable permeability. It is shown that strain annealing offers an effective method for tuning permeability in these alloys. For an Fe-rich alloy, permeability increased from 4000 to 16,000 with a positive magnetostriction. In a Ni-rich alloy, permeability decreased from 290 to 40 with a negative magnetostriction. Significant elongations (above 60%) are observed during strain annealing at high stress. Crystallization products have been determined in allmore » alloys heated to 480°C. γ-FeNi is formed in all alloys, while (Fe 30Ni 70) 80Nb 4Si 2B 14 also undergoes secondary crystallization at temperatures of approximately 480°C to form a phase with the Cr 23C 6-type structure and a likely composition of Fe 21Nb 2B 6. Toroidal losses have been measured for (Fe 70Ni 30) 80Nb 4Si y B 16–y (0 ≤ y ≤ 3) at various annealing temperatures. At an induction of 1 T and frequency of 400 Hz and 1 kHz, the toroidal losses obtained are W 1.0T, 400 Hz = 0.9 W/kg and W 1.0T, 1 kHz = 2.3 W/kg, respectively. These losses are lower than losses recently reported for state of the art 3.0% and 6.5% silicon steels, a Metglas Fe-based amorphous alloy, and some Fe-based nanocomposites.« less

The Effects of Strain-Annealing on Tuning Permeability and Lowering Losses in Fe-Ni-Based Metal Amorphous Nanocomposites

NASA Astrophysics Data System (ADS)

Aronhime, Natan; DeGeorge, Vincent; Keylin, Vladimir; Ohodnicki, Paul; McHenry, Michael E.

2017-11-01

Fe-Ni-based metal amorphous nanocomposites with a range of compositions (Fe100- x Ni x )80Nb4Si2B14 (30 ≤ x ≤ 70) are investigated for motor and transformer applications, where it is beneficial to have tunable permeability. It is shown that strain annealing offers an effective method for tuning permeability in these alloys. For an Fe-rich alloy, permeability increased from 4000 to 16,000 with a positive magnetostriction. In a Ni-rich alloy, permeability decreased from 290 to 40 with a negative magnetostriction. Significant elongations (above 60%) are observed during strain annealing at high stress. Crystallization products have been determined in all alloys heated to 480°C. γ-FeNi is formed in all alloys, while (Fe30Ni70)80Nb4Si2B14 also undergoes secondary crystallization at temperatures of approximately 480°C to form a phase with the Cr23C6-type structure and a likely composition of Fe21Nb2B6. Toroidal losses have been measured for (Fe70Ni30)80Nb4Si y B16- y (0 ≤ y ≤ 3) at various annealing temperatures. At an induction of 1 T and frequency of 400 Hz and 1 kHz, the toroidal losses obtained are W1.0T, 400 Hz = 0.9 W/kg and W1.0T, 1 kHz = 2.3 W/kg, respectively. These losses are lower than losses recently reported for state of the art 3.0% and 6.5% silicon steels, a Metglas Fe-based amorphous alloy, and some Fe-based nanocomposites.

Lu-Hf and Sm-Nd isotope systematics of Korean spinel peridotites: A case for metasomatically induced Nd-Hf decoupling

NASA Astrophysics Data System (ADS)

Choi, Sung Hi; Mukasa, Samuel B.

2012-12-01

We determined the Lu-Hf and Sm-Nd isotope compositions of spinel peridotite xenoliths in alkali basalts from Baengnyeong and Jeju islands, South Korea, to constrain the timing of melt-depletion events and stabilization of the lithospheric mantle beneath the region. Equilibration temperatures estimated by two-pyroxene thermometry range from 780 to 950 °C, and from 960 to 1010 °C for Baengnyeong and Jeju peridotites, respectively. The Baengnyeong peridotite clinopyroxenes are characterized by extremely radiogenic Hf in association with isotopically less extreme Nd, resulting in strong Nd-Hf decoupling referenced to the mantle array. This is in stark contrast to the well-correlated isotopic compositions of Hf and Nd in the Jeju peridotite clinopyroxenes, which plot along the Nd-Hf mantle array. The Hf abundances and isotopic compositions of the Baengnyeong clinopyroxenes were less affected by relatively recent secondary enrichments that overprinted the light rare earth element abundances and Nd isotopes, causing the decoupling of the Nd-Hf isotopes. The Nd-Hf isotopic compositions of the Jeju peridotites appear to have been re-equilibrated, probably as a result of efficient diffusion at the relatively higher temperatures of the Jeju peridotites. Lu-Hf tie lines for clinopyroxene and orthopyroxene from four of the Korean peridotites have negative slopes on a Lu-Hf isochron diagram, yielding negative ages. This is interpreted to indicate recent isotopic exchange in orthopyroxene by reaction with metasomatic agents having low 176Hf/177Hf components. Secondary overprinting in orthopyroxene was facilitated by the considerably lower Hf concentrations than in co-located clinopyroxene. Baengnyeong lherzolite clinopyroxenes yield a Lu-Hf errorchron age of 1.9 ± 0.1 Ga, which is independently supported by a model Os age (based on Re depletion or TRD) of 1.8 Ga on a refractory Baengnyeong peridotite. We interpret this age range to mark the time of stabilization of the mantle

Lu-Hf and Sm-Nd isotope systematics of Korean spinel peridotites: A case for metasomatically induced Nd-Hf decoupling

NASA Astrophysics Data System (ADS)

Choi, S.; Mukasa, S. B.

2012-12-01

We determined the Lu-Hf and Sm-Nd isotope compositions of spinel peridotite xenoliths in alkali basalts from Baengnyeong and Jeju islands, South Korea, to constrain the timing of melt-depletion events and stabilization of the lithospheric mantle beneath the region. Equilibration temperatures estimated by two-pyroxene thermometry range from 780 to 950°C, and from 960 to 1010°C for Baengnyeong and Jeju peridotites, respectively. The Baengnyeong peridotite clinopyroxenes are characterized by extremely radiogenic Hf in association with isotopically less extreme Nd, resulting in strong Nd-Hf decoupling referenced to the mantle array. This is in stark contrast to the well-correlated isotopic compositions of Hf and Nd in the Jeju peridotite clinopyroxenes, which plot along the Nd-Hf mantle array. The Hf abundances and isotopic compositions of the Baengnyeong clinopyroxenes were less affected by relatively recent secondary enrichments that overprinted the light rare earth element abundances and Nd isotopes, causing the decoupling of the Nd-Hf isotopes. The Nd-Hf isotopic compositions of the Jeju peridotites appear to have been re-equilibrated, probably as a result of efficient diffusion at the relatively higher temperatures of the Jeju peridotites. Lu-Hf tie lines for clinopyroxene and orthopyroxene from four of the Korean peridotites have negative slopes on a Lu-Hf isochron diagram, yielding negative ages. This is interpreted to indicate recent isotopic exchange in orthopyroxene by reaction with metasomatic agents having low 176Hf/177Hf components. Secondary overprinting in orthopyroxene was facilitated by the considerably lower Hf concentrations than in co-located clinopyroxene. Baengnyeong lherzolite clinopyroxenes yield a Lu-Hf errorchron age of 1.9 ± 0.1 Ga, which is independently supported by a model Os age (based on Re depletion or TRD) of 1.8 Ga on a refractory Baengnyeong peridotite. We interpret this age range to mark the time of stabilization of the mantle

The expression characteristics of mt-ND2 gene in chicken.

PubMed

Zhang, Wenwen; Hou, Lingling; Wang, Ting; Lu, Weiwei; Tao, Yafei; Chen, Wen; Du, Xiaohui; Huang, Yanqun

2016-09-01

Subunit 2 of NADH dehydrogenase (ND2) is encoded by the mt-ND2 gene and plays a critical role in controlling the production of the mitochondrial reactive oxygen species. Our study focused on exploring the mt-ND2 tissue expression patterns and the effects of energy restriction and dietary fat (linseed oil, corn oil, sesame oil or lard) level (2.5% and 5%) on its expression in chicken. The results showed that mt-ND2 gene was expressed in the 15 tissues of hybrid chickens with the highest level in heart and lowest level in pancreas tissue; 30% energy restriction did not significantly affect mt-ND2 mRNA level in chicken liver tissue. Both the mt-ND2 mRNA levels in chicken pectoralis (p < 0.05) and hepatic tissues (p < 0.05) at 42 d-old were affected by the type of dietary fats in 5% level, while not in abdominal fat tissues. The expression of mt-ND2 in hepatic tissues was down-regulated with chicken age (p < 0.01). The interactive effect of dietary fat types with chicken age (p < 0.05) was significant on mt-ND2 mRNA level. The study demonstrated that mt-ND2 gene was extensively expressed in tissues, and the expression was affected by dietary fat types and chicken age.

Neutron Diffraction Study of Parasitic Nd-Moment Order in the Checkerboard-Type Phase Nd 1.3Sr 0.7NiO 4

DOE PAGES

Kobayashi, Riki; Yoshizawa, Hideki; Matsuda, Masaaki; ...

2015-05-25

In this paper, the Nd-moment order in the layered nickelate Nd 2-xSr xNiO 4 (x = 0.7) has been investigated by performing a neutron diffraction experiment using a single crystal sample. First, the checkerboard (CB)-type charge order was confirmed by observing the temperature dependence of the nuclear superlattice peak at Q=(5,0,0) between 1.9 and 300 K, which indicates that the transition temperature of the CB-type charge order is above 300 K. Magnetic superlattice peaks with the propagation vector k=(1-ε,0,1) appear below 67 K, and the value of ε was determined to be 0.455 in good agreement with previous studies. Themore » intensity of the magnetic superlattice peaks appearing below 67 K shows a sharp increase below ≈20 K. This behavior indicates that the Nd moments freeze under the influence of the Ni ordering. The CB-type antiferromagnetic (AFM) Ni order in the NiO 2 layers is stacked antiferromagnetically in the c-axis direction, while the Nd moments in the Nd/SrO 2 layers are coupled antiferromagnetically with the Ni moments. Finally, the Nd moments are parallel to the c-axis, while the Ni moments are canted towards the c-axis direction from the basal ab-plane at low temperatures where the Nd moments are well ordered.« less

Diode-pumped quasi-three-level CW Nd:CLNGG and Nd:CNGG lasers.

PubMed

He, Kunna; Wei, Zhiyi; Li, Dehua; Zhang, Zhiguo; Zhang, Huaijin; Wang, Jiyang; Gao, Chunqing

2009-10-12

We have demonstrated what is to our knowledge the first quasi-three-level CW Nd:CLNGG laser with simple linear resonator. When the pump power was 18.2 W, a maximum output power of 1.63 W was obtained at the dual-wavelength of 935 nm and 928 nm. The optical-to-optical conversion efficiency was 9.0% and the slope efficiency was 11.5%. Lasing characteristics of a quasi-three-level CW Nd:CNGG laser were also investigated. A maximum output power of 1.87 W was obtained at the single-wavelength of 935 nm with 15.2 W pump power, corresponding to an optical-to-optical conversion efficiency of 12.3% and a slope efficiency of 15.6%.

A nucleosynthetic origin for the Earth's anomalous (142)Nd composition.

PubMed

Burkhardt, C; Borg, L E; Brennecka, G A; Shollenberger, Q R; Dauphas, N; Kleine, T

2016-09-15

A long-standing paradigm assumes that the chemical and isotopic compositions of many elements in the bulk silicate Earth are the same as in chondrites. However, the accessible Earth has a greater (142)Nd/(144)Nd ratio than do chondrites. Because (142)Nd is the decay product of the now-extinct (146)Sm (which has a half-life of 103 million years), this (142)Nd difference seems to require a higher-than-chondritic Sm/Nd ratio for the accessible Earth. This must have been acquired during global silicate differentiation within the first 30 million years of Solar System formation and implies the formation of a complementary (142)Nd-depleted reservoir that either is hidden in the deep Earth, or lost to space by impact erosion. Whether this complementary reservoir existed, and whether or not it has been lost from Earth, is a matter of debate, and has implications for determining the bulk composition of Earth, its heat content and structure, as well as for constraining the modes and timescales of its geodynamical evolution. Here we show that, compared with chondrites, Earth's precursor bodies were enriched in neodymium that was produced by the slow neutron capture process (s-process) of nucleosynthesis. This s-process excess leads to higher (142)Nd/(144)Nd ratios; after correction for this effect, the (142)Nd/(144)Nd ratios of chondrites and the accessible Earth are indistinguishable within five parts per million. The (142)Nd offset between the accessible silicate Earth and chondrites therefore reflects a higher proportion of s-process neodymium in the Earth, and not early differentiation processes. As such, our results obviate the need for hidden-reservoir or super-chondritic Earth models and imply a chondritic Sm/Nd ratio for the bulk Earth. Although chondrites formed at greater heliocentric distances and contain a different mix of presolar components than Earth, they nevertheless are suitable proxies for Earth's bulk chemical composition.

Effects of oxygen deficiency on the transport and dielectric properties of NdSrNbO

NASA Astrophysics Data System (ADS)

Hzez, W.; Benali, A.; Rahmouni, H.; Dhahri, E.; Khirouni, K.; Costa, B. F. O.

2018-06-01

In the present study, Nd0.7Sr0.3NbO3-y (y = 0.1, 0.15, 0.2) compounds were prepared via a solid-solid reaction route. The prepared samples were characterized by electrochemical impedance spectroscopy in order to establish the effects of temperature, frequency, and oxygen vacancies on both the transport and dielectric properties of NdSrNbO. We found that both the electrical and dielectric properties were highly sensitive to the concentration of oxygen vacancies. The conduction mechanism data were explained well according to the Mott model and adiabatic small polaronic hopping model. Electrochemical impedance spectroscopy analysis showed that one relaxation process was present in the Nd0.7Sr0.3NbO2.9 system whereas two relaxation processes were observed in the Nd0.7Sr0.3NbO2.85 and Nd0.7Sr0.3NbO2.8 systems, where the latter behavior indicated the presence of many active regions (due to the contributions of different microstructures). The temperature and frequency dependences of the dielectric constant confirmed the contributions of different polarization mechanisms. In particular, the high dielectric constant values at low frequencies and high temperatures were mainly related to the presence of different Schottky barriers, whereas the low dielectric constant values at high frequencies were essentially related to the intrinsic effect. The constant dielectric values obtained for the samples are greater than those in the NdSrFeO system, which makes them interesting materials for use in applications that require high dielectric constants.

Spectroscopic investigations of Nd3+ doped flouro- and chloro-borate glasses.

PubMed

Mohan, Shaweta; Thind, Kulwant Singh; Sharma, Gopi; Gerward, Leif

2008-10-01

Spectroscopic and physical properties of Nd3+ doped sodium lead flouro- and chloro-borate glasses of the type 20NaX-30PbO-49.5B2O3-0.5Nd2O3 (X=F and Cl) have been investigated. Optical absorption spectra have been used to determine the Slater Condon (F2, F4, and F6), spin orbit xi4f and Racah parameters (E1, E2, and E3). The oscillator strengths and the intensity parameters Omega2, Omega4 and Omega6 have been determined by the Judd-Ofelt theory, which in turn provide the radiative transition probability (A), total transition probability (A(T)), radiative lifetime (tauR) and branching ratio (beta) for the fluorescent level 4F3/2. The lasing efficiency of the prepared glasses has been characterized by the spectroscopic quality factor (Omega4/Omega6), the value of which is in the range of 0.2-1.5, typical for Nd3+ in different laser hosts. Nephelauxetic effect results in a red shift in the energy levels of Nd3+ for chloroborate glass. The radiative transition probability of the potential lasing transition 4F3/2-->4I11/2 of Nd3+ ions is found to be higher for flouroborate as compared to chloroborate glass.

Nd and Ru co-doped bismuth titanate polycrystalline thin films with improved ferroelectric properties

NASA Astrophysics Data System (ADS)

Sahoo, Kishor Kumar; Singh Rajput, Shailendra; Gupta, Rajeev; Roy, Amritendu; Garg, Ashish

2018-02-01

We report the ferroelectric properties of pulsed laser deposited thin films of Nd and Ru co-doped bismuth titanate (Bi4-x Nd x Ti3-y Ru y O12). Structural analysis of the as-grown films, using x-ray diffraction, showed a single-phase formation with a polycrystalline structure. In comparison to un-doped and Nd-doped films, ferroelectric measurements on co-doped films demonstrated improved properties with remnant polarization (P r) ~ 12.5 µC cm-2 and an enhanced electrical fatigue life for Bi3.25Nd0.75Ti2.8Ru0.20O12 films. The enhancement in remanent polarization is attributed to microscopic changes, such as local structural distortion and the modification of the dynamical/effective charges on constituent ions due to chemical strain upon simultaneous Bi- (A) and Ti- (B) site doping with Nd and Ru, which has a far stronger effect than only A-site doping with Nd. Piezoresponse force microscopy further confirmed the polar structure and domain switching at nanoscale. The films exhibit small yet finite magnetization at 10 K resulting from strain.

Designing a protonic ceramic fuel cell with novel electrochemically active oxygen electrodes based on doped Nd0.5Ba0.5FeO3-δ.

PubMed

Lyagaeva, Julia; Danilov, Nilolay; Tarutin, Arthem; Vdovin, Gennady; Medvedev, Dmitry; Demin, Anatoly; Tsiakaras, Panagiotis

2018-06-19

The Fe-based perovskite-structured Nd0.5Ba0.5FeO3-δ (NBF) system represents the basis for developing promising electrode materials for solid oxide fuel cells with proton-conducting electrolytes. This study aims at investigating the strategy of slight doping of neodymium-barium ferrite with some transition metals (M = Ni, Cu, Co) and examining the effect of this doping on the functional characteristics, such as phase structure, thermal expansion, total and ionic conductivity as well as electrochemical behavior, of Nd0.5Ba0.5Fe0.9M0.1O3-δ (NBFM) under testing in symmetrical cell (SC) and fuel cell (FC) modes of operation. Among the investigated dopants, cobalt (Co) is found to be the optimal dopant, resulting in an enhancement of transport properties and avoiding an undesirable increase in the thermal expansion coefficient. As a result, the electrode material made of NBFCo exhibits highest ionic conductivity and lowest polarization resistance in the SC mode of operation. Electrochemical characterization of the NBFCo cathode material in a protonic ceramic fuel cell (PCFC) followed by comparison of the obtained results with literature data demonstrates that NBFCo is an attractive cathode candidate for PCFC applications.

A nucleosynthetic origin for the Earth’s anomalous 142Nd composition

PubMed Central

Burkhardt, C.; Borg, L.E.; Brennecka, G.A.; Shollenberger, Q.R.; Dauphas, N.; Kleine, T.

2016-01-01

A long-standing paradigm assumes that the chemical and isotopic composition of many elements in the bulk silicate Earth are the same as in chondrites1–4. However, the accessible Earth has a greater 142Nd/144Nd than chondrites. Because 142Nd is the decay product of now-extinct 146Sm (t1/2= 103 million years5), this 142Nd difference seems to require a higher-than-chondritic Sm/Nd of the accessible Earth. This must have been acquired during global silicate differentiation within the first 30 million years of Solar System formation6 and implies the formation of a complementary 142Nd-depleted reservoir that either is hidden in the deep Earth6, or was lost to space by impact erosion3,7. Whether this complementary reservoir existed, and whether or not it has been lost from Earth is a matter of debate3,8,9, but has tremendous implications for determining the bulk composition of Earth, its heat content and structure, and for constraining the modes and timescales of its geodynamical evolution3,7,9,10. Here, we show that compared to chondrites, Earth’s precursor bodies were enriched in Nd produced by the slow neutron capture process (s-process) of nucleosynthesis. This s-process excess leads to higher 142Nd/144Nd, and, after correction for this effect, the 142Nd/144Nd of chondrites and the accessible Earth are indistinguishable within 5 parts per million. The 142Nd offset between the accessible silicate Earth and chondrites, therefore, reflects a higher proportion of s-process Nd in the Earth, and not early differentiation processes. As such, our results obviate the need for hidden reservoir or super-chondritic Earth models, and imply a chondritic Sm/Nd for bulk Earth. Thus, although chondrites formed at greater heliocentric distance and contain a different mix of presolar components than Earth, they nevertheless are suitable proxies for Earth’s bulk chemical composition. PMID:27629643

Neodymium Isotope Variability at the Grain Scale in the Sub-Continental Lithospheric Mantle: NdO+ Analyses of Individual Clinopyroxene Grains (<5 ng Nd aliquots) from a Kilbourne Hole Harzburgitic Xenolith.

NASA Astrophysics Data System (ADS)

Harvey, J.; Honn, D.; Baxter, E. F.; Warren, J. M.; Hammond, S.; Walshaw, R.

2014-12-01

It is evident that at scales of 102 to 10-2 m there is significant isotopic heterogeneity in the mantle that is not always reflected in primitive melts. The "Os isotopic gap"[1] is one such manifestation of this phenomenon but a similar offset exists between the Nd isotope composition of abyssal peridotites and the mid-ocean ridge basalts that they are inferred to have produced[2]. This study takes advantage of recent advances in the analysis of Nd isotopes as NdO+[3,4] which permit the precise analysis of single clinopyroxene grains (<1 mg mass; <5 ng Nd) from a continental harzburgitic xenolith from Kilbourne Hole, NM. Analyses of aggregates of clinopyroxenes from 5 Kilbourne Hole xenoliths reveal a wide range of 143Nd/144Nd (0.513011 ± 28 to 0.513615 ±19)[5]. This study demonstrates significant grain-to-grain isotopic heterogeneity at a scale of 10-2 m (143Nd/144Nd = 0.513089 ± 78 to 0.513364 ± 74) which (i) is equivalent to the range of values for Pacific MORB[6] and (ii) is more primitive than local basalts with an asthenospheric signature[7]. This suggests that small-scale refractory domains exist within the mantle which are either not sampled during partial melting or whose presence is obscured by the melting of higher volumes of more fusible material. Ref:[1]Alard et al. (2005) Nature 436, 1005-1008 [2]Warren et al. (2009) JGR 114, B12203, doi:10.1029/2008JB006186 [3]Harvey and Baxter (2009) Chem. Geol. 258, 251-257 [4]Honn et al. (2013) AGU Fall abstr. V33-2722 [5]Harvey et al. (2012) J. Petrol. 53, 1709-1742 [6]Hofmann (1997) Nature 385, 219-229 [7]Thompson et al. (2005) J. Petrol. 46, 1603-1643

Advances of naphthalene degradation in Pseudomonas putida ND6

NASA Astrophysics Data System (ADS)

Song, Fu; Shi, Yifei; Jia, Shiru; Tan, Zhilei; Zhao, Huabing

2018-03-01

Naphthalene is one of the most common and simple polycyclic aromatic hydrocarbons. Degradation of naphthalene has been greatly concerned due to its economic, free-pollution and its fine effect in Pseudomonas putida ND6. This review summarizes the development history of naphthalene degradation, the research progress of naphthalene degrading gene and naphthalene degradation pathway of Pseudomonas putida ND6, and the researching path of this strain. Although the study of naphthalene degradation is not consummate in Pseudomonas putida ND6, there is a potential capability for Pseudomonas putida ND6 to degrade the naphthalene in the further research.

Continental sedimentary processes decouple Nd and Hf isotopes

NASA Astrophysics Data System (ADS)

Garçon, Marion; Chauvel, Catherine; France-Lanord, Christian; Huyghe, Pascale; Lavé, Jérôme

2013-11-01

The neodymium and hafnium isotopic compositions of most crustal and mantle rocks correlate to form the "Terrestrial Array". However, it is now well established that whereas coarse detrital sediments follow this trend, fine-grained oceanic sediments have high Hf ratios relative to their Nd isotopic ratios. It remains uncertain whether this "decoupling" of the two isotopic systems only occurs in the oceanic environment or if it is induced by sedimentary processes in continental settings. In this study, the hafnium and neodymium isotopic compositions of sediments in large rivers is expressly used to constrain the behavior of the two isotopic systems during erosion and sediment transport from continent to ocean. We report major and trace element concentrations together with Nd and Hf isotopic compositions of bedloads, suspended loads and river banks from the Ganges River and its tributaries draining the Himalayan Range i.e. the Karnali, the Narayani, the Kosi and the Marsyandi Rivers. The sample set includes sediments sampled within the Himalayan Range in Nepal, at the Himalayan mountain front, and also downstream on the floodplain and at the outflow of the Ganges in Bangladesh. Results show that hydrodynamic sorting of minerals explains the entire Hf isotopic range, i.e. more than 10 εHf units, observed in the river sediments but does not affect the Nd isotopic composition. Bedloads and bank sediments have systematically lower εHf values than suspended loads sampled at the same location. Coarse-grained sediments lie below or on the Terrestrial Array in an εHf vs. εNd diagram. In contrast, fine-grained sediments, including most of the suspended loads, deviate from the Terrestrial Array toward higher εHf relative to their εNd, as is the case for oceanic terrigenous clays. The observed Nd-Hf decoupling is explained by mineralogical sorting processes that enrich bottom sediments in coarse and dense minerals, including unradiogenic zircons, while surface sediments

Stable Nd isotope variations in the inner Solar System: The effect of sulfide during differentiation?

NASA Astrophysics Data System (ADS)

McCoy-West, A.

2017-12-01

Radiogenic neodymium isotopes have been widely used in studies of planetary accretion to constrain the timescales of early planetary differention [1]. Whereas stable isotope varitaions potentially provide information on the the processes that occur during planet formation. Experimental work suggests that the Earth's core contains a significant proportion of sulfide [2], and recent experimental work shows that under reducing conditions sulfide can incorporate substantial quantities of refractory lithophile elements [including Nd; 3]. If planetary embroyos also contain sulfide-rich cores, Nd stable isotopes have the potential to trace this sulfide segregation event in highly reduced environments, because there is a significant contrast in bonding environment between sulfide and silicate, where heavy isotopes should be preferentially incorporated into high force-constant bonds involving REE3+ (i.e. the silicate mantle). Here we present 146Nd/144Nd data, obtained using a double spike TIMS technique, for a range of planetary bodies formed at variable oxidation states including samples from the Moon, Mars, the asteriod 4Vesta and the Angrite and Aubrite parent bodies. Analyses of chondritic meteorites and terrestrial igneous rocks indicate that the Earth has a Nd stable isotope composition that is indistinguishable from that of chondrites [4]. Eucrites and martian meteorites also have compositons within error of the chondritic average. Significantly more variabilty is observed in the low concentration lunar samples and diogienite meteorites with Δ146Nd = 0.16‰. Preliminary results suggest that the Nd stable isotope composition of oxidised planetary bodies are homogeneous and modifications are the result of subordinate magmatic processes. [1] Boyet & Carlson, Science 309, 576 (2005) [2] Labidi et al. Nature 501, 208 (2013); [3] Wohlers &Wood, Nature 520, 337 (2015); [4] McCoy-West et al. Goldschmidt Ab. 429 (2017).

Sm-Nd dating of the giant Sullivan Pb-Zn-Ag deposit, British Columbia

USGS Publications Warehouse

Jiang, Shao-Yong; Slack, John F.; Palmer, Martin R.

2000-01-01

We report here Sm and Nd isotope data for hydrothermal tourmalinites and sulfide ores from the giant Sullivan Pb-Zn-Ag deposit, which occurs in the lower part of the Mesoproterozoic Purcell (Belt) Supergroup. Whole-rock samples of quartz-tourmaline tourmalinite from the footwall alteration pipe yield a Sm-Nd isochron age of 1470 ± 59 Ma, recording synsedimentary B metasomatism of clastic sediments during early evolution of the Sullivan hydrothermal system. Data for variably altered (chloritized and/or albitized) tourmalinites from the hanging wall of the deposit, which are believed to have formed originally ca. 1470 Ma, define a younger 1076 ± 77 Ma isochron because of resetting of Sm and Nd isotopes during Grenvillian metamorphism. HCl leachates of bedded Pb-Zn ore yield a Sm-Nd isochron age of 1451 ± 46 Ma, which is consistent with syngenetic-exhalative mineralization ca. 1470 Ma; this age could also reflect a slightly younger, epigenetic hydrothermal event. Results obtained for the Sullivan deposit indicate that the Sm-Nd geochronometer has the potential to directly date mineralization and alteration in stratabound sulfide deposits that are not amenable to dating by other isotope methods.

Energy transfer efficiency from Cr(3+) to Nd(3+) in solar-pumped laser using transparent Nd/Cr:Y(3)Al(5)O(12) ceramics.

PubMed

Hasegawa, Kazuo; Ichikawa, Tadashi; Mizuno, Shintaro; Takeda, Yasuhiko; Ito, Hiroshi; Ikesue, Akio; Motohiro, Tomoyoshi; Yamaga, Mitsuo

2015-06-01

We report energy transfer efficiency from Cr³⁺ to Nd³⁺ in Nd (1.0 at.%)/Cr (0.4 at.%) co-doped Y₃Al₅O₁₂ (YAG) transparent ceramics in the laser oscillation states. The laser oscillation has performed using two pumping lasers operating at 808 nm and 561 nm; the former pumps Nd³⁺ directly to create the 1064 nm laser oscillation, whereas the latter assists the performance via Cr³⁺ absorption and sequential energy transfer to Nd³⁺. From the laser output power properties and laser mode analysis, the energy transfer efficiency was determined to be around 65%, which is close to that obtained from the spontaneous Nd³⁺ emission.

Grain boundary diffusion of Dy films prepared by magnetron sputtering for sintered Nd–Fe–B magnets

NASA Astrophysics Data System (ADS)

Chen, W.; Luo, J. M.; Guan, Y. W.; Huang, Y. L.; Chen, M.; Hou, Y. H.

2018-05-01

Dy films, deposited on the surface of sintered Nd–Fe–B magnets by magnetron sputtering, were employed for grain boundary diffusion source. High coercivity sintered Nd–Fe–B magnets were successfully prepared. Effects of sputtering power and grain boundary diffusion processes (GBDP) on the microstructure and magnetic properties were investigated in detail. The dense and uniform Dy films were beneficial to prepare high coercivity magnets by GBDP. The maximum coercivity value of 1189 kA m‑1 could be shown, which was an amplification of 22.3%, compared with that of as-prepared Nd–Fe–B magnet. Furthermore, the improved remanence and maximum energy product were also achieved through tuning grain boundary diffusion processes. Our results demonstrated that the formation of (Nd, Dy)2Fe14B shell surrounding Nd2Fe14B grains and fine, uniform and continuous intergranular RE-rich phases jointly contribute to the improved coercivity.

Nd- And Er-Doped Phosphate Glass For Fiber Laser.

NASA Astrophysics Data System (ADS)

Yamashita, Toshiharu T.

1990-02-01

Laser fibers prepared from Nd- and Er-doped phosphate glass possessing a large stimulated emission cross section have been investigated both in a single fiber and in a fiber bundle. In the single fiber, continuous wave oscillations were successfully obtained at 1.054 p.m and 1.366 µm on a high Nd-doped single-mode fiber of 10 mm in length and also at 1.535 pm in a Er-doped single-mode fiber, sensitized by Nd, Yb. Especially, a low threshold of 1 mw and a high slope-efficiency of 50% were achieved in 1.054 pm laser oscillation on a Nd-doped fiber, end-pumped with a laser diode. A fiber bundle of phosphate glass doped with 8 wt% Nd2O3 yielded an average output power of 100 W at 50 pps where the bundle was 4.6 mm in diameter and was side-pumped with flash lamps.

Bering Sea Nd isotope records of North Pacific Intermediate Water circulation

NASA Astrophysics Data System (ADS)

Rabbat, C.; Knudson, K. P.; Goldstein, S. L.

2017-12-01

North Pacific Intermediate Water (NPIW) is the primary water mass associated with Pacific meridional overturning circulation. While the relationship between Atlantic meridional overturning circulation and climate has been extensively studied, a lack of suitable sediment cores has limited past investigations of North Pacific climate and NPIW variability. Integrated Ocean Drilling Program Site U1342 (818 m water depth) on Bower's Ridge in the Bering Sea is located at a sensitive depth for detecting changes in NPIW, and it is the only available sub-arctic North Pacific site that offers long, continuous core recovery, relatively high sedimentation rates, excellent foraminifera preservation, and a well-constrained age model over multiple glacial-interglacial cycles. Previous work at Site U1342 from Knudson and Ravelo (2015), using non-quantitative circulation proxies, provides evidence for enhanced NPIW formation during extreme glacials associated with the closure of the Bering Strait and suggest that NPIW was formed locally within the Bering Sea. Our work builds on the potential importance of these results and applies more robust and potentially quantitative circulation proxies to constrain NPIW variability. Here, we present new records of NPIW circulation from Site U1342 based on Nd isotope analyses on fish debris and Fe-Mn encrusted foraminifera, which serve as semi-quantitative "water mass tracers." Weak Bering Sea NPIW formation and ventilation are reflected by relatively lower eNd values indicative of open subarctic North Pacific waters, which are presently predominant, whereas enhanced Bering Sea NPIW formation and ventilation are be reflected by relatively higher eNd values due to the input of Nd from regional volcanic rocks.

Effects of energy transfer on quantum efficiency of YAG:Nd

NASA Astrophysics Data System (ADS)

Lupei, V.; Lupei, A.; Georgescu, S.; Yen, W. M.

1989-10-01

Using the energy transfer parameters deduced from the study on nonexponential luminescence decay of the 4F3/2 level of Nd(3+) in YAG at room temperature, it is shown that up to 1.5 at. pct Nd, the relative quantum efficiency is reduced by an amount of 18.2C, C being the relative Nd concentration. It is pointed out that about 20 percent of this reduction is due to a very effective quenching mechanism inside the nearest-neighbor Nd-ion pairs.

Nonlinear refraction of Nd3+-Li+ co-doped CdS-PVP nanostructure

NASA Astrophysics Data System (ADS)

Talwatkar, S. S.; Sunatkari, A. L.; Tamgadge, Y. S.; Muley, G. G.

2018-05-01

Third-order optical nonlinearity of the co-doped CdS nanoparticles embedded in polymer thin films is studied with the Z-scan technique with 632.8 nm excitation using a cw laser. The results show that the co-doped CdS nanocomposite film exhibits enhanced negative nonlinear refractive index in the order of n2 ≈ 10-5 cm2/W, as compared to the undoped CdS nanoparticles. Nonlinear refractive index of co-doped CdS-PVP thin film are found maximum for the sample doped with 5 wt% of Nd3+-Li+ concentration. The underlying mechanism is discussed.

Comparative study of passively Q-switched c-cut Nd:YVO4/Nd:YAG lasers based on CVD graphene and controlled operation

NASA Astrophysics Data System (ADS)

Jia, Fuqiang; Liu, Pei; Li, Kang; Chen, Hao; Cheng, Yongjie; Cai, Zhiping; Copner, Nigel

2017-07-01

In this paper, a comparative study of passively Q-switched c-cut Nd:YVO4 and Nd:YAG lasers using four different layers CVD graphene as saturable absorber are demonstrated experimentally for the first time. Moreover, it is successful to accurately control the frequency of repetition rates of the CVD graphern passively Q-switched lasers by pulsed pump. The impacts of laser materials, layers of CVD graphene and cavity length on output parameters are investigated intensively as well, the result shows that the c-cut Nd:YVO4 is a promising laser media compared with Nd:YAG for passively Q-switched lasers based on CVD graphene, as it has better performances in pulse width, pulse energy and peak power. A useful and cost-effective way to generate stable pulsed lasers by CVD graphene or other novel saturable materials are demonstrated.

Next-Generation Magnetic Nanocomposites: Cytotoxic and Genotoxic Effects of Coated and Uncoated Ferric Cobalt Boron (FeCoB) Nanoparticles In Vitro.

PubMed

Netzer, Katharina; Jordakieva, Galateja; Girard, Angelika M; Budinsky, Alexandra C; Pilger, Alexander; Richter, Lukas; Kataeva, Nadezhda; Schotter, Joerg; Godnic-Cvar, Jasminka; Ertl, Peter

2018-03-01

Metal nanoparticles (NPs) have unique physicochemical properties and a widespread application scope depending on their composition and surface characteristics. Potential biomedical applications and the growing diversity of novel nanocomposites highlight the need for toxicological hazard assessment of next-generation magnetic nanomaterials. Our study aimed to evaluate the cytotoxic and genotoxic properties of coated and uncoated ferric cobalt boron (FeCoB) NPs (5-15 nm particle size) in cultured normal human dermal fibroblasts. Cell proliferation was assessed via ATP bioluminescence kit, and DNA breakage and chromosomal damage were measured by alkaline comet assay and micronucleus test. Polyacryl acid-coated FeCoB NPs [polyacrylic acid (PAA)-FeCoB NPs) and uncoated FeCoB NPs inhibited cell proliferation at 10 μg/ml. DNA strand breaks were significantly increased by PAA-coated FeCoB NPs, uncoated FeCoB NPs and l-cysteine-coated FeCoB NPs (Cys-FeCoB NPs), although high concentrations (10 μg/ml) of coated NPs (Cys- and PAA-FeCoB NPs) showed significantly more DNA breakage when compared to uncoated ones. Uncoated FeCoB NPs and coated NPs (PAA-FeCoB NPs) also induced the formation of micronuclei. Additionally, PAA-coated NPs and uncoated FeCoB NPs showed a negative correlation between cell proliferation and DNA strand breaks, suggesting a common pathomechanism, possibly by oxidation-induced DNA damage. We conclude that uncoated FeCoB NPs are cytotoxic and genotoxic at in vitro conditions. Surface coating of FeCoB NPs with Cys and PAA does not prevent but rather aggravates DNA damage. Further safety assessment and a well-considered choice of surface coating are needed prior to application of FeCoB nanocomposites in biomedicine. © 2017 Nordic Association for the Publication of BCPT (former Nordic Pharmacological Society).

Collisional depopulation of rubidium Rydberg states by ND/sub 3/

DOE Office of Scientific and Technical Information (OSTI.GOV)

Petitjean, L.; Gounand, F.; Fournier, P.R.

1986-02-01

This paper reports the measurement of the depopulation cross sections of the Rb(ns) and Rb(nd) states by ND/sub 3/ (23< or =n< or =50). The experimental data are discussed with reference to previous work done on collisions between Rb(ns) and Rb(nd) states and NH/sub 3/.

New magnetic phase and magnetic coherence in Nd/Sm(001) superlattices

NASA Astrophysics Data System (ADS)

Soriano, S.; Dufour, C.; Dumesnil, K.; Stunault, A.

2006-06-01

In order to investigate magnetic phenomena in Nd and Sm layers separately, resonant x-ray magnetic scattering experiments have been performed to study Nd/Sm(001) superlattices with different relative layers thickness. The samples were grown using molecular beam epitaxy, and optimized to yield dhcp Sm growth and thus a coherent dhcp stacking across the Nd/Sm superlattices. The magnetic phases in Sm layers are very close to the ones evidenced in dhcp thick films. In contrast, the magnetism in Nd layers shows strong differences with the bulk case. In superlattices with a large Sm thickness (>8 nm), no magnetic scattering usually associated with Nd magnetic structure was detected. In superlattices with smaller Sm thickness (<4 nm), new Nd magnetic phases have been observed. A detailed analysis of the propagation of the magnetic structures in the cubic and hexagonal sublattices of both Sm and Nd is presented. Both Sm hexagonal and cubic magnetic phases propagate coherently through 3.7 nm thick Nd layers but remain confined in Sm layers when the Nd layers are 7.1 nm thick. In contrast, the critical Sm thickness allowing a coherent propagation of Nd magnetic order is different for the hexagonal and cubic sublattices above 5 K. Finally, we show that: (i) a spin-density wave and a 4f magnetic order with perpendicular polarization are exclusive on a given crystallographic site (either hexagonal or cubic); (ii) a 4f magnetic order on a crystallographic site does not perturb the establishment of a spin-density wave with a perpendicular polarization on the other site.

A nucleosynthetic origin for the Earth’s anomalous 142Nd composition

DOE PAGES

Burkhardt, C.; Borg, L. E.; Brennecka, G. A.; ...

2016-09-14

A long-standing paradigm assumes that the chemical and isotopic compositions of many elements in the bulk silicate Earth are the same as in chondrites(1-4). But, the accessible Earth has a greater Nd-142/Nd-144 ratio than do chondrites. Because Nd-142 is the decay product of the now-extinct Sm-146 (which has a half-life of 103 million years(5)), this Nd-142 difference seems to require a higher-than-chondritic Sm/Nd ratio for the accessible Earth. This must have been acquired during global silicate differentiation within the first 30 million years of Solar System formation(6) and implies the formation of a complementary Nd-142-depleted reservoir that either is hiddenmore » in the deep Earth(6), or lost to space by impact erosion(3,7). Whether this complementary reservoir existed, and whether or not it has been lost from Earth, is a matter of debate(3,8,9), and has implications for determining the bulk composition of Earth, its heat content and structure, as well as for constraining the modes and timescales of its geodynamical evolution(3,7,9,10). We show that, compared with chondrites, Earth's precursor bodies were enriched in neodymium that was produced by the slow neutron capture process (s-process) of nucleosynthesis. This s-process excess leads to higher Nd-142/Nd-144 ratios; after correction for this effect, the Nd-142/Nd-144 ratios of chondrites and the accessible Earth are indistinguishable within five parts per million. The Nd-142 offset between the accessible silicate Earth and chondrites therefore reflects a higher proportion of s-process neodymium in the Earth, and not early differentiation processes. Our results obviate the need for hidden-reservoir or super-chondritic Earth models and imply a chondritic Sm/Nd ratio for the bulk Earth. Although chondrites formed at greater heliocentric distances and contain a different mix of presolar components than Earth, they nevertheless are suitable proxies for Earth's bulk chemical composition.« less

A nucleosynthetic origin for the Earth’s anomalous 142Nd composition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Burkhardt, C.; Borg, L. E.; Brennecka, G. A.

A long-standing paradigm assumes that the chemical and isotopic compositions of many elements in the bulk silicate Earth are the same as in chondrites(1-4). But, the accessible Earth has a greater Nd-142/Nd-144 ratio than do chondrites. Because Nd-142 is the decay product of the now-extinct Sm-146 (which has a half-life of 103 million years(5)), this Nd-142 difference seems to require a higher-than-chondritic Sm/Nd ratio for the accessible Earth. This must have been acquired during global silicate differentiation within the first 30 million years of Solar System formation(6) and implies the formation of a complementary Nd-142-depleted reservoir that either is hiddenmore » in the deep Earth(6), or lost to space by impact erosion(3,7). Whether this complementary reservoir existed, and whether or not it has been lost from Earth, is a matter of debate(3,8,9), and has implications for determining the bulk composition of Earth, its heat content and structure, as well as for constraining the modes and timescales of its geodynamical evolution(3,7,9,10). We show that, compared with chondrites, Earth's precursor bodies were enriched in neodymium that was produced by the slow neutron capture process (s-process) of nucleosynthesis. This s-process excess leads to higher Nd-142/Nd-144 ratios; after correction for this effect, the Nd-142/Nd-144 ratios of chondrites and the accessible Earth are indistinguishable within five parts per million. The Nd-142 offset between the accessible silicate Earth and chondrites therefore reflects a higher proportion of s-process neodymium in the Earth, and not early differentiation processes. Our results obviate the need for hidden-reservoir or super-chondritic Earth models and imply a chondritic Sm/Nd ratio for the bulk Earth. Although chondrites formed at greater heliocentric distances and contain a different mix of presolar components than Earth, they nevertheless are suitable proxies for Earth's bulk chemical composition.« less

Two Thai families with Norrie disease (ND): association of two novel missense mutations with severe ND phenotype, seizures, and a manifesting carrier.

PubMed

Yamada, K; Limprasert, P; Ratanasukon, M; Tengtrisorn, S; Yingchareonpukdee, J; Vasiknanonte, P; Kitaoka, T; Ghadami, M; Niikawa, N; Kishino, T

2001-04-15

We describe two Thai families with Norrie disease (ND) in three generations, including 10 affected males and one manifesting female. All affected males in each family had severely defective eye development with complete loss of vision. In addition, three male patients (one from family 1 and two from family 2) suffered from epilepsy, and one female carrier from one family manifested blindness with phthisis bulbi in her right eye. Mutation analysis of the ND gene (NDP) revealed two different novel missense mutations (L16P and S75P) that co-segregated with ND in each family, suggesting that the newly appearing proline at codon 16 or codon 75 alters the conformation of the ND protein and contributes to the severe phenotype of ND in each family. Other studies suggest that epileptic seizures or growth retardation that is associated with ND is the consequence of loss of contiguous genes, because most such patients had deletions extending beyond the Norrie locus. Our finding that the three affected males in the two families with the missense mutations had epilepsy does not support a contiguous gene effect, but favors the pleiotropism of NDP, at least as far as the epileptic manifestation is concerned. The unilateral blindness in the female carrier may have been due to non-random X-inactivation. Copyright 2001 Wiley-Liss, Inc.

Peering Through a Martian Veil: ALHA84001 Sm-Nd Age Revisited

NASA Technical Reports Server (NTRS)

Nyquist, Laurence E.; Shih, Chi-Yu

2013-01-01

The ancient Martian orthopyroxenite ALH84001experienced a complex history of impact and aqueous alteration events. Here we summarize Sm-147-Nd-143 and Sm-146-Nd-142 analyses performed at JSC. Further, using REE data, we model the REE abundance pattern of the basaltic magma parental to ALH84001 cumulus orthopyroxene. We find the Sm-146-Nd-142 isotopic data to be consistent with isotopic evolution in material having the modeled Sm/Nd ratio from a time very close to the planet's formation to igneous crystallization of ALH84001 as inferred from the Sm-Nd studies.

Tracing Tethyan Phosphogenesis From Temporal Variations of 44Ca/42Ca and 143Nd/144Nd Isotope Ratios in Francolites and P Accumulation